Gold/silver core-shell 20 nm nanoparticles extracted from citrate solution examined by XPS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Engelhard, Mark H.; Smith, Jordan N.; Baer, Donald R.

Silver nanoparticles of many types are widely used in consumer and medical products. The surface chemistry of particles and the coatings that form during synthesis or use in many types of media can significantly impact the behaviors of particles including dissolution, transformation and biological or environmental impact. Consequently it is useful to be able to extract information about the thickness of surface coatings and other attributes of nanoparticles produced in a variety of ways. It has been demonstrated that X-ray Photoelectron Spectroscopy (XPS) can be reliably used to determine the thickness of organic and other nanoparticles coatings and shells. However,more » care is required to produce reliable and consistent information. Here we report the XPS spectra from gold/silver core-shell nanoparticles of nominal size 20 nm removed from a citrate saturated solution after one and two washing cycles. The Simulation of Electron Spectra for Surface Analysis (SESSA) program had been used to model peak amplitudes to obtain information on citrate coatings that remain after washing and demonstrate the presence of the gold core. This data is provided so that others can compare use of SESSA or other modeling approaches to quantify the nature of coatings to those already published and to explore the impacts particle non-uniformities on XPS signals from core-shell nanoparticles.« less

Calculation of density of states of transition metals: From bulk sample to nanocluster

NASA Astrophysics Data System (ADS)

Krasavin, Andrey V.; Borisyuk, Petr V.; Vasiliev, Oleg S.; Zhumagulov, Yaroslav V.; Kashurnikov, Vladimir A.; Kurelchuk, Uliana N.; Lebedinskii, Yuriy Yu.

2018-03-01

A technique is presented of restoring the electronic density of states of the valence band from data of X-ray photoelectron spectroscopy (XPS). The originality of the technique consists in using a stochastic procedure to solve an integral equation relating the density of states and the experimental X-ray photoelectron spectra via the broadening function. To obtain the broadening function, only the XPS spectra of the core levels are needed. The results are presented for bulk sample of gold and tungsten and nanoclusters of tantalum; the possibility of using the results to determine the density of states of low-dimensional structures, including ensembles of metal nanoclusters, is demonstrated.

Electronic structure evolution of fullerene on CH 3NH 3PbI 3

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Chenggong; Wang, Congcong; Liu, Xiaoliang

2015-03-19

The thickness dependence of fullerene on CH 3NH 3PbI 3 perovskitefilm surface has been investigated by using ultraviolet photoemission spectroscopy (UPS), X-ray photoemission spectroscopy(XPS), and inverse photoemission spectroscopy (IPES). The lowest unoccupied molecular orbital and highest occupied molecular orbital (HOMO) can be observed directly with IPES and UPS. It is observed that the HOMO level in fullerene shifts to lower binding energy. The XPS results show a strong initial shift of core levels to lower binding energy in the perovskite, which indicates that electrons transfer from the perovskitefilm to fullerene molecules. Further deposition of fullerene forms C 60 solid, accompaniedmore » by the reduction of the electron transfer. As a result, the strongest electron transfer happened at 1/4 monolayer of fullerene.« less

Electronic structure evolution of fullerene on CH{sub 3}NH{sub 3}PbI{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Chenggong; Wang, Congcong; Kauppi, John

2015-03-16

The thickness dependence of fullerene on CH{sub 3}NH{sub 3}PbI{sub 3} perovskite film surface has been investigated by using ultraviolet photoemission spectroscopy (UPS), X-ray photoemission spectroscopy (XPS), and inverse photoemission spectroscopy (IPES). The lowest unoccupied molecular orbital and highest occupied molecular orbital (HOMO) can be observed directly with IPES and UPS. It is observed that the HOMO level in fullerene shifts to lower binding energy. The XPS results show a strong initial shift of core levels to lower binding energy in the perovskite, which indicates that electrons transfer from the perovskite film to fullerene molecules. Further deposition of fullerene forms C{submore » 60} solid, accompanied by the reduction of the electron transfer. The strongest electron transfer happened at 1/4 monolayer of fullerene.« less

Deduction of the chemical state and the electronic structure of Nd{sub 2}Fe{sub 14}B compound from X-ray photoelectron spectroscopy core-level and valence-band spectra

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jing; Liang, Le; Zhang, Lanting, E-mail: lantingzh@sjtu.edu.cn, E-mail: lmsun@sjtu.edu.cn

2014-10-28

Characterization of chemical state and electronic structure of the technologically important Nd{sub 2}Fe{sub 14}B compound is attractive for understanding the physical nature of its excellent magnetic properties. X-ray photoelectron spectroscopy (XPS) study of such rare-earth compound is important and also challenging due to the easy oxidation of surface and small photoelectron cross-sections of rare-earth 4f electrons and B 2p electrons, etc. Here, we reported an investigation based on XPS spectra of Nd{sub 2}Fe{sub 14}B compound as a function of Ar ion sputtering time. The chemical state of Fe and that of B in Nd{sub 2}Fe{sub 14}B compound can be clearlymore » determined to be 0 and −3, respectively. The Nd in Nd{sub 2}Fe{sub 14}B compound is found to have the chemical state of close to +3 instead of +3 as compared with the Nd in Nd{sub 2}O{sub 3}. In addition, by comparing the valence-band spectrum of Nd{sub 2}Fe{sub 14}B compound to that of the pure Fe, the contributions from Nd, Fe, and B to the valence-band structure of Nd{sub 2}Fe{sub 14}B compound is made more clear. The B 2p states and B 2s states are identified to be at ∼11.2 eV and ∼24.6 eV, respectively, which is reported for the first time. The contribution from Nd 4f states can be identified both in XPS core-level spectrum and XPS valence-band spectrum. Although Nd 4f states partially hybridize with Fe 3d states, Nd 4f states are mainly localized in Nd{sub 2}Fe{sub 14}B compound.« less

Towards a Predictive Thermodynamic Model of Oxidation States of Uranium Incorporated in Fe (hydr) oxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bagus, Paul S.

The theoretical research in this project has been directed toward the interpretation of core-level spectroscopies for systems relevant to the project. For the initial efforts, the focus of our theoretical simulations has been the interpretation of laboratory and synchrotron X-Ray Photoemission Spectra, XPS. In more recent efforts, an increasing emphasis has been placed on developing transparent understandings of X-Ray Adsorption Spectra, XAS . For the XAS, the principal concern is for the near-edge features, either just below or just above, an ionization limit or edge, which are described as Near-Edge X-Ray Adsorption Fine Structure, NEXAFS. In particular, a priority hasmore » involved the analysis and interpretation of XPS and NEXAFS spectra, especially of Fe and U systems, as measured by our PNNL collaborators. The overall objective of our theoretical studies is to establish connections between features of the spectra and their origin in the electronic structure of the materials. The efforts for the analysis of XPS have been reviewed in a paper by the PI, C. J. Nelin, and E. S. Ilton from PNNL on “The interpretation of XPS spectra: Insights into materials properties”, Surf. Sci. Reports, 68, 273 (2013). Two materials properties of special interest have been the degree of ionicity and the character of the covalent bonding in a range of oxides formed with transition metal, lanthanide, and actinide cations. Since the systems treated have electrons in open shells, it has been necessary to determine the energetics and the character of the angular momentum coupling of the open shell electrons. In particular, we have established methods for the treatment of the “intermediate coupling” which arises when the system is between the limit of Russell-Saunders multiplets, and the limit of j-j coupling where the spin-orbit splittings of single electrons dominate. A recent paper by the PI, and M. J. Sassi, and K. M. Rosso, (both at PNNL) “Intermediate Coupling For Core-Level Excited States: Consequences For X-Ray Absorption Spectroscopy”, J. Elec. Spectros. and Related Phenom., 200, 174 (2015) describes our first application of these methods. As well as applications to problems and materials of direct interest for our PNNL colleagues, we have pursued applications of fundamental theoretical significance for the analysis and interpretation of XPS and XAS spectra. These studies are important for the development of the fields of core-level spectroscopies as well as to advance our capabilities for applications of interest to our PNNL colleagues. An excellent example is our study of the surface core-level shifts, SCLS, for the surface and bulk atoms of an oxide that provides a new approach to understanding how the surface electronic of oxides differs from that in the bulk of the material. This work has the potential to lead to a new key to understanding the reactivity of oxide surfaces. Our theoretical studies use cluster models with finite numbers of atoms to describe the properties of condensed phases and crystals. This approach has allowed us to focus on the local atomistic, chemical interactions. For these clusters, we obtain orbitals and spinors through the solution of the Hartree-Fock, HF, and the fully relativistic Dirac HF equations. These orbitals are used to form configuration mixing wavefunctions which treat the many-body effects responsible for the open shell angular momentum coupling and for the satellites of the core-level spectra. Our efforts have been in two complementary directions. As well as the applications described above, we have placed major emphasis on the enhancement and extension of our theoretical and computational capabilities so that we can treat complex systems with a greater range of many-body effects. Noteworthy accomplishments in terms of method development and enhancement have included: (1) An improvement in our treatment of the large matrices that must be handled when many-body effects are treated. (2) Improvements and extensions of our capabilities for the calculation of the intensities of XPS and XAS transitions. And (3) ongoing development of flexible programs for the visualization of the theoretical spectra so that they can be compared with experiment. Our efforts on applications and methodology for these and related topics will continue under a sub-contract to PNNL.« less

New insights into micro/nanoscale combined probes (nanoAuger, μXPS) to characterize Ag/Au@SiO2 core-shell assemblies.

PubMed

Ledeuil, J B; Uhart, A; Soulé, S; Allouche, J; Dupin, J C; Martinez, H

2014-10-07

This work has examined the elemental distribution and local morphology at the nanoscale of core@shell Ag/Au@SiO2 particles. The characterization of such complex metal/insulator materials becomes more efficient when using an initial cross-section method of preparation of the core@shell nanoparticles (ion milling cross polisher). The originality of this route of preparation allows one to obtain undamaged, well-defined and planar layers of cross-cut nano-objects. Once combined with high-resolution techniques of characterization (XPS, Auger and SEM), the process appears as a powerful way to minimize charging effects and enhance the outcoming electron signal (potentially affected by the topography of the material) during analysis. SEM experiments have unambiguously revealed the hollow-morphology of the metal core, while Auger spectroscopy observations showed chemical heterogeneity within the particles (as silver and gold are randomly found in the core ring). To our knowledge, this is the first time that Auger nano probe spectroscopy has been used and successfully optimized for the study of some complex metal/inorganic interfaces at such a high degree of resolution (≈12 nm). Complementarily, XPS Au 4f and Ag 3d peaks were finally detected attesting the possibility of access to the whole chemistry of such nanostructured assemblies.

Extended Fenske-Hall LCAO MO calculations of core-level shifts in solid P compounds

NASA Astrophysics Data System (ADS)

Franke, R.; Chassé, T.; Reinhold, J.; Streubel, P.; Szargan, R.

1997-08-01

Extended Fenske-Hall LCAO-MO ΔSCF calculations on solids modelled as H-pseudoatom saturated clusters are reported. The computational results verify the experimentally obtained initial-state (effective atomic charges, Madelung potential) and relaxation-energy contributions to the XPS phosphorus core-level binding energy shifts measured in Na 3PO 3S, Na 3PO 4, Na 2PO 3F and NH 4PF 6 in reference to red phosphorus. It is shown that the different initial-state contributions observed in the studied phosphates are determined by local and nonlocal terms while the relaxation-energy contributions are mainly dependent on the nature of the nearest neighbors of the phosphorus atom.

An Electrochemical, Microtopographical and Ambient Pressure X-Ray Photoelectron Spectroscopic Investigation of Si/TiO 2/Ni/Electrolyte Interfaces

DOE PAGES

Lichterman, Michael F.; Richter, Matthias H.; Hu, Shu; ...

2015-12-05

The electrical and spectroscopic properties of the TiO 2/Ni protection layer system, which enables stabilization of otherwise corroding photoanodes, have been investigated in contact with electrolyte solutions by scanning-probe microscopy, electrochemistry and in-situ ambient pressure X-ray photoelectron spectroscopy (AP-XPS). Specifically, the energy-band relations of the p +-Si/ALD-TiO 2/Ni interface have been determined for a selected range of Ni thicknesses. AP-XPS measurements using tender X-rays were performed in a three-electrode electrochemical arrangement under potentiostatic control to obtain information from the semiconductor near-surface region, the electrochemical double layer (ECDL) and the electrolyte beyond the ECDL. The degree of conductivity depended on themore » chemical state of the Ni on the TiO 2 surface. At low loadings of Ni, the Ni was present primarily as an oxide layer and the samples were not conductive, although the TiO 2 XPS core levels nonetheless displayed behavior indicative of a metal-electrolyte junction. In contrast, as the Ni thickness increased, the Ni phase was primarily metallic and the electrochemical behavior became highly conductive, with the AP-XPS data indicative of a metal-electrolyte junction. Electrochemical and microtopographical methods have been employed to better define the nature of the TiO 2/Ni electrodes and to contextualize the AP-XPS results.« less

Polyphenylsilole multilayers--an insight from X-ray electron spectroscopy and density functional theory.

PubMed

Diller, Katharina; Ma, Yong; Luo, Yi; Allegretti, Francesco; Liu, Jianzhao; Tang, Ben Zhong; Lin, Nian; Barth, Johannes V; Klappenberger, Florian

2015-12-14

We present a combined investigation by means of X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine-structure (NEXAFS) spectroscopy of condensed multilayers of two polyphenylsiloles, namely hexaphenylsilole (HPS) and tetraphenylsilole (TPS). Both compounds exhibit very similar spectroscopic signatures, whose interpretation is aided by density functional theory (DFT) calculations. High-resolution XPS spectra of the Si 2p and C 1s core levels of these multilayers indicate a positively charged silicon ion flanked by two negatively charged adjacent carbon atoms in the silole core of both molecules. This result is corroborated quantitatively by DFT calculations on isolated HPS (TPS) molecules, which show a natural bond orbital partial charge of +1.67 e (+1.58 e) on the silicon and -0.34 e (-0.58 e) on the two neighbouring carbon atoms in the silole ring. These charges are conserved in direct contact with a Cu(111) substrate for films of submonolayer coverage, as evidenced by the Si 2p XPS data. The C K-edge NEXAFS spectra of HPS and TPS multilayers exhibit distinct and differing features. Their main characteristics reappear in the simulated spectra and are assigned to the different inequivalent carbon species in the molecule. The angle-dependent measurements hardly reveal any dichroism, i.e., the molecular π-systems are not uniformly oriented parallel or perpendicular with respect to the surface. Changes in the growth conditions of TPS, i.e., a reduction of the substrate temperature from 240 K to 80 K during deposition, lead to a broadening of both XPS and NEXAFS signatures, as well as an upward shift of the Si 2p and C 1s binding energies, indicative of a less ordered growth mode at low temperature.

New insights into micro/nanoscale combined probes (nanoAuger, μXPS) to characterize Ag/Au@SiO2 core-shell assemblies

NASA Astrophysics Data System (ADS)

Ledeuil, J. B.; Uhart, A.; Soulé, S.; Allouche, J.; Dupin, J. C.; Martinez, H.

2014-09-01

This work has examined the elemental distribution and local morphology at the nanoscale of core@shell Ag/Au@SiO2 particles. The characterization of such complex metal/insulator materials becomes more efficient when using an initial cross-section method of preparation of the core@shell nanoparticles (ion milling cross polisher). The originality of this route of preparation allows one to obtain undamaged, well-defined and planar layers of cross-cut nano-objects. Once combined with high-resolution techniques of characterization (XPS, Auger and SEM), the process appears as a powerful way to minimize charging effects and enhance the outcoming electron signal (potentially affected by the topography of the material) during analysis. SEM experiments have unambiguously revealed the hollow-morphology of the metal core, while Auger spectroscopy observations showed chemical heterogeneity within the particles (as silver and gold are randomly found in the core ring). To our knowledge, this is the first time that Auger nano probe spectroscopy has been used and successfully optimized for the study of some complex metal/inorganic interfaces at such a high degree of resolution (~12 nm). Complementarily, XPS Au 4f and Ag 3d peaks were finally detected attesting the possibility of access to the whole chemistry of such nanostructured assemblies.This work has examined the elemental distribution and local morphology at the nanoscale of core@shell Ag/Au@SiO2 particles. The characterization of such complex metal/insulator materials becomes more efficient when using an initial cross-section method of preparation of the core@shell nanoparticles (ion milling cross polisher). The originality of this route of preparation allows one to obtain undamaged, well-defined and planar layers of cross-cut nano-objects. Once combined with high-resolution techniques of characterization (XPS, Auger and SEM), the process appears as a powerful way to minimize charging effects and enhance the outcoming electron signal (potentially affected by the topography of the material) during analysis. SEM experiments have unambiguously revealed the hollow-morphology of the metal core, while Auger spectroscopy observations showed chemical heterogeneity within the particles (as silver and gold are randomly found in the core ring). To our knowledge, this is the first time that Auger nano probe spectroscopy has been used and successfully optimized for the study of some complex metal/inorganic interfaces at such a high degree of resolution (~12 nm). Complementarily, XPS Au 4f and Ag 3d peaks were finally detected attesting the possibility of access to the whole chemistry of such nanostructured assemblies. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr03211j

Electronic structure of α-SrB4O7: experiment and theory

NASA Astrophysics Data System (ADS)

Atuchin, V. V.; Kesler, V. G.; Zaitsev, A. I.; Molokeev, M. S.; Aleksandrovsky, A. S.; Kuzubov, A. A.; Ignatova, N. Y.

2013-02-01

The investigation of valence band structure and electronic parameters of constituent element core levels of α-SrB4O7 has been carried out with x-ray photoemission spectroscopy. Optical-quality crystal α-SrB4O7 has been grown by the Czochralski method. Detailed photoemission spectra of the element core levels have been recorded from the powder sample under excitation by nonmonochromatic Al Kα radiation (1486.6 eV). The band structure of α-SrB4O7 has been calculated by ab initio methods and compared to XPS measurements. It has been found that the band structure of α-SrB4O7 is weakly dependent on the Sr-related states.

InP/ZnS nanocrystals: coupling NMR and XPS for fine surface and interface description.

PubMed

Virieux, Héloïse; Le Troedec, Marianne; Cros-Gagneux, Arnaud; Ojo, Wilfried-Solo; Delpech, Fabien; Nayral, Céline; Martinez, Hervé; Chaudret, Bruno

2012-12-05

Advanced (1)H, (13)C, and (31)P solution- and solid-state NMR studies combined with XPS were used to probe, at the molecular scale, the composition (of the core, the shell, and the interface) and the surface chemistry of InP/ZnS core/shell quantum dots prepared via a non-coordinating solvent strategy. The interface between the mismatched InP and ZnS phases is composed of an amorphous mixed oxide phase incorporating InPO(x) (with x = 3 and predominantly 4), In(2)O(3), and InO(y)(OH)(3-2y) (y = 0, 1). Thanks to the analysis of the underlying reaction mechanisms, we demonstrate that the oxidation of the upper part of the InP core is the consequence of oxidative conditions brought by decarboxylative coupling reactions (ketonization). These reactions occur during both the core preparation and the coating process, but according to different mechanisms.

Perspective: Chemical reactions in ionic liquids monitored through the gas (vacuum)/liquid interface.

PubMed

Maier, F; Niedermaier, I; Steinrück, H-P

2017-05-07

This perspective analyzes the potential of X-ray photoelectron spectroscopy under ultrahigh vacuum (UHV) conditions to follow chemical reactions in ionic liquids in situ. Traditionally, only reactions occurring on solid surfaces were investigated by X-ray photoelectron spectroscopy (XPS) in situ. This was due to the high vapor pressures of common liquids or solvents, which are not compatible with the required UHV conditions. It was only recently realized that the situation is very different when studying reactions in Ionic Liquids (ILs), which have an inherently low vapor pressure, and first studies have been performed within the last years. Compared to classical spectroscopy techniques used to monitor chemical reactions, the advantage of XPS is that through the analysis of their core levels all relevant elements can be quantified and their chemical state can be analyzed under well-defined (ultraclean) conditions. In this perspective, we cover six very different reactions which occur in the IL, with the IL, or at an IL/support interface, demonstrating the outstanding potential of in situ XPS to gain insights into liquid phase reactions in the near-surface region.

Lattice and Valence Electronic Structures of Crystalline Octahedral Molybdenum Halide Clusters-Based Compounds, Cs2[Mo6X14] (X = Cl, Br, I), Studied by Density Functional Theory Calculations.

PubMed

Saito, Norio; Cordier, Stéphane; Lemoine, Pierric; Ohsawa, Takeo; Wada, Yoshiki; Grasset, Fabien; Cross, Jeffrey S; Ohashi, Naoki

2017-06-05

The electronic and crystal structures of Cs 2 [Mo 6 X 14 ] (X = Cl, Br, I) cluster-based compounds were investigated by density functional theory (DFT) simulations and experimental methods such as powder X-ray diffraction, ultraviolet-visible spectroscopy, and X-ray photoemission spectroscopy (XPS). The experimentally determined lattice parameters were in good agreement with theoretically optimized ones, indicating the usefulness of DFT calculations for the structural investigation of these clusters. The calculated band gaps of these compounds reproduced those experimentally determined by UV-vis reflectance within an error of a few tenths of an eV. Core-level XPS and effective charge analyses indicated bonding states of the halogens changed according to their sites. The XPS valence spectra were fairly well reproduced by simulations based on the projected electron density of states weighted with cross sections of Al K α , suggesting that DFT calculations can predict the electronic properties of metal-cluster-based crystals with good accuracy.

Relativistic many-body XMCD theory including core degenerate effects

NASA Astrophysics Data System (ADS)

Fujikawa, Takashi

2009-11-01

A many-body relativistic theory to analyze X-ray Magnetic Circular Dichroism (XMCD) spectra has been developed on the basis of relativistic quantum electrodynamic (QED) Keldysh Green's function approach. This theoretical framework enables us to handle relativistic many-body effects in terms of correlated nonrelativistic Green's function and relativistic correction operator Q, which naturally incorporates radiation field screening and other optical field effects in addition to electron-electron interactions. The former can describe the intensity ratio of L2/L3 which deviates from the statistical weight (branching ratio) 1/2. In addition to these effects, we consider the degenerate or nearly degenerate effects of core levels from which photoelectrons are excited. In XPS spectra, for example in Rh 3d sub level excitations, their peak shapes are quite different: This interesting behavior is explained by core-hole moving after the core excitation. We discuss similar problems in X-ray absorption spectra in particular excitation from deep 2p sub levels which are degenerate in each sub levels and nearly degenerate to each other in light elements: The hole left behind is not frozen there. We derive practical multiple scattering formulas which incorporate all those effects.

New quaternary thallium indium germanium selenide TlInGe2Se6: Crystal and electronic structure

NASA Astrophysics Data System (ADS)

Khyzhun, O. Y.; Parasyuk, O. V.; Tsisar, O. V.; Piskach, L. V.; Myronchuk, G. L.; Levytskyy, V. O.; Babizhetskyy, V. S.

2017-10-01

Crystal structure of a novel quaternary thallium indium germanium selenide TlInGe2Se6 was investigated by means of powder X-ray diffraction method. It was determined that the compound crystallizes in the trigonal space group R3 with the unit cell parameters a = 10.1798(2) Å, c = 9.2872(3) Å. The relationship with similar structures was discussed. The as-synthesized TlInGe2Se6 ingot was tested with X-ray photoelectron spectroscopy (XPS) and X-ray emission spectroscopy (XES). In particular, the XPS valence-band and core-level spectra were recorded for initial and Ar+ ion-bombarded surfaces of the sample under consideration. The XPS data allow for statement that the TlInGe2Se6 surface is rigid with respect to Ar+ ion-bombardment. Particularly, Ar+ ion-bombardment (3.0 keV, 5 min duration, ion current density fixed at 14 μA/cm2) did not cause substantial modifications of stoichiometry in topmost surface layers. Furthermore, comparison on a common energy scale of the XES Se Kβ2 and Ge Kβ2 bands and the XPS valence-band spectrum reveals that the principal contributions of the Se 4p and Ge 4p states occur in the upper and central portions of the valence band of TlInGe2Se6, respectively, with also their substantial contributions in other portions of the band. The bandgap energy of TlInGe2Se6 at the level of αg=103 cm-1 is equal to 2.38 eV at room temperature.

XPS analysis of activated carbon supported ionic liquids: Enhanced purity and reduced charging

NASA Astrophysics Data System (ADS)

Foelske-Schmitz, A.; Weingarth, D.; Kötz, R.

2011-12-01

Herein we report on XPS measurements on five different [EMIM] based ionic liquids (IL) prepared on activated carbon and aluminium supports. The anions were [TFSI], [BF4], [FAP], [B(CN)4] and [EtOSO3]. The results show that impurities such as O, Si or hydrocarbons were significantly reduced or no longer detected when preparation was performed on the high surface area carbon support. All core level spectra were fitted and for [EMIM][FAP], [EMIM][B(CN)4] and [EMIM][EtOSO3] de-convolution procedures of the C 1s lines are suggested. Comparison of the determined binding energies with published data strongly suggests that sample charging is irrelevant when preparation is performed on the activated carbon support. This observation is supposed to refer to the high capacitance of the high surface area carbon.

Core-level spectra and molecular deformation in adsorption: V-shaped pentacene on Al(001)

PubMed Central

Lin, He; Brivio, Gian Paolo; Floreano, Luca; Fratesi, Guido

2015-01-01

Summary By first-principle simulations we study the effects of molecular deformation on the electronic and spectroscopic properties as it occurs for pentacene adsorbed on the most stable site of Al(001). The rationale for the particular V-shaped deformed structure is discussed and understood. The molecule–surface bond is made evident by mapping the charge redistribution. Upon X-ray photoelectron spectroscopy (XPS) from the molecule, the bond with the surface is destabilized by the electron density rearrangement to screen the core hole. This destabilization depends on the ionized carbon atom, inducing a narrowing of the XPS spectrum with respect to the molecules adsorbed hypothetically undistorted, in full agreement to experiments. When looking instead at the near-edge X-ray absorption fine structure (NEXAFS) spectra, individual contributions from the non-equivalent C atoms provide evidence of the molecular orbital filling, hybridization, and interchange induced by distortion. The alteration of the C–C bond lengths due to the V-shaped bending decreases by a factor of two the azimuthal dichroism of NEXAFS spectra, i.e., the energy splitting of the sigma resonances measured along the two in-plane molecular axes. PMID:26734516

Electronic Structure of TlBa2CaCu2O(7-Delta)

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Novikov, D. L.; Freeman, A. J.; Siegal, M. P.

1997-01-01

The core levels of TlBa2CaCu2O(7-delta) (Tl-1212) epitaxial films have been measured with X-ray photoelectron spectroscopy (XPS). The valence electronic structure has been determined using the full-potential linear muffin-tin-orbital band-structure method and measured with XPS. The calculations show that a van Hove singularity (VHS) lies above the Fermi level (E(sub F)) for the stoichiometric compound (delta = 0.5), while for 50% oxygen vacancies in the Tl-O layer (delta = 0.5) E(sub F) is in close proximity to the VHS. Samples annealed in nitrogen (to reduce the hole overdoping by the removal of oxygen) exhibit higher core-level binding energies and a higher T(sub c), consistent with a shift of E(sub F) closer to the VHS. Comparisons are made to the core levels and valence bands of Tl2Ba2CaCu2O(8 + delta)(Tl-2212) and HgBa2CaCu2O)6 + delta) (Hg- 1212). The similarity of the Cu 2p(sub 3/2) spectra for Tl-1212 and Tl-2212 indicates that the number of Tl-O layers has little effect on the Cu-O bonding. However, the Tl-1212 and Hg-1212 Cu 2p(sub 3/2) signals exhibit differences which suggest that the replacement of T(sup 3+) with Hg(sup 2+) results in a decrease in the O 2p right arrow Cu 3d charge-transfer energy and differences in the probabilities of planar vs apical oxygen charge transfer and/or Zhang-Rice singlet-state formation. Differences between the Tl-1212 and the Tl-2212 and Hg-1212 measured valence bands are consistent with the calculated Cu 3d and (Tl,Hg) 6s/5d partial densities of states.

Observing Graphene Grow: Catalyst–Graphene Interactions during Scalable Graphene Growth on Polycrystalline Copper

PubMed Central

2013-01-01

Complementary in situ X-ray photoelectron spectroscopy (XPS), X-ray diffractometry, and environmental scanning electron microscopy are used to fingerprint the entire graphene chemical vapor deposition process on technologically important polycrystalline Cu catalysts to address the current lack of understanding of the underlying fundamental growth mechanisms and catalyst interactions. Graphene forms directly on metallic Cu during the high-temperature hydrocarbon exposure, whereby an upshift in the binding energies of the corresponding C1s XPS core level signatures is indicative of coupling between the Cu catalyst and the growing graphene. Minor carbon uptake into Cu can under certain conditions manifest itself as carbon precipitation upon cooling. Postgrowth, ambient air exposure even at room temperature decouples the graphene from Cu by (reversible) oxygen intercalation. The importance of these dynamic interactions is discussed for graphene growth, processing, and device integration. PMID:24041311

Effects of M=Si, Ga and Al for Co substitution on the electronic properties of RCo4M as probed by XPS

NASA Astrophysics Data System (ADS)

Laslo, A.; Dudric, R.; Neumann, M.; Isnard, O.; Coldea, M.; Pop, V.

2014-12-01

The electronic properties of RCo5-xMx (R=Er, Sm, Tm; M=Si, Ga, Al; x=0 and 1) compounds were investigated by X-ray photoelectron spectroscopy (XPS). The study was focused on the Co 3s exchange splitting, the valence bands and chemical shifts of the elements from the analyzed compounds. The Co 2p3/2 core-level chemical shifts were described by means of the Auger parameters and Wagner plot. The hybridization between the R 5d6s and M 3sp and 4sp states and Co 3d states leads to a partial filling of the Co 3d band and to a decrease of the Co magnetic moments in comparison with the value in pure Co metal, in good agreement with the magnetic measurements.

X-Ray Photoelectron Spectroscopic Characterization of Iron Oxide Nanoparticles

NASA Astrophysics Data System (ADS)

Radu, T.; Iacovita, C.; Benea, D.; Turcu, R.

2017-05-01

We report X-ray photoelectron spectroscopy (XPS) results on iron oxide magnetic nanoparticle (Fe3O4) synthesized using solvothermal reduction in the presence of polyethylene glycol. The magnetite obtained was employed as precursor for the synthesis of γ-Fe2O3 (by oxygen dissociation) which in turn was transformed into α-Fe2O3. We confirmed the magnetite, maghemite and hematite structure by Fourier Transformed Spectroscopy (FTIR) and X-ray diffraction (XRD). The analysis of the XPS core level and valence band (VB) photoemission spectra for all investigated samples is discussed in terms of the degree of iron oxidation. This is of fundamental importance to better understand the electronic structure of the obtained iron oxide nanoparticles in order to control and improve their quality for specific biomedical applications. Moreover, theoretical band structure calculations are performed for magnetite and the separate contributions of Fe in tetragonal and octahedral environment are shown.

Chemical and structural order in silicon oxynitrides by methods of surface physics

NASA Astrophysics Data System (ADS)

Finster, J.; Heeg, J.; Klinkenberg, E.-D.

A large number of thin amorphous layers of SiO xN y and several (crystalline) reference compounds (SiO 2, Si 3N 4, Si 2N 2O) are studied. Although XANES and SEXAFS are well sulted to derive structural and chemical order, for these compounds many problems remain to be solved. We show how core level spectra (XPS, AES) can be used to gain such information (e.g. random bonding structure, N coordination, oxidation behaviour).

X-ray photoemission spectroscopy of nonmetallic materials: Electronic structures of boron and BxOy

NASA Astrophysics Data System (ADS)

Ong, C. W.; Huang, H.; Zheng, B.; Kwok, R. W. M.; Hui, Y. Y.; Lau, W. M.

2004-04-01

Although an increasing volume of x-ray photoemission spectroscopic (XPS) data has been accumulated on boron and boron-rich compounds because of their unusual properties, including a unique three-center, two-electron bonding configuration, their common nonmetallic nature has been overlooked. Typically, the measured energy-state data are not clarified by surface Fermi level positions of these nonmetallic samples, which compromises the scientific contents of the data. In the present study, we revisited the XPS studies of sputter-cleaned β-rhombohedral boron (βr-B), the oxidized surface of βr-B, B6O pellet, and polished B2O3, to illustrate the impact and resolution of this scientific issue. These samples were chosen because βr-B is the most thermodynamically stable polytype of pure boron, B2O3 is its fully oxidized form, and B6O is the best known superhard family member of boron-rich compounds. From our XPS measurements, including those from a sputter-cleaned gold as a metal reference, we deduced that our βr-B had a surface Fermi level located at 0.7±0.1 eV from its valence-band maximum (VBM) (referred as EFL) and a binding energy for its B 1s core level at 187.2 eV from VBM (Eb,VBM). The latter attribute, unlike typical XPS binding energy data that are referenced to a sample-dependent Fermi level (Eb,FL), is immune from any uncertainties and variations arising from sample doping and surface charging. For bulk B2O3, we found an Eb,VBM for its B 1s core level at 190.5 eV and an Eb,FL at 193.6 eV. For our βr-B subjected to a surface oxidation treatment, an overlayer structure of ˜1.2 nm B2O3/˜2 nm B2O/B was found. By comparing the data from this sample and those from βr-B and bulk B2O3, we infer that the oxide overlayer carried some negative fixed charge and this induced on the semiconducting βr-B sample an upward surface band bending of ˜0.6 eV. As for our B6O sample, we found an EFL of ˜1.7 eV and two different chemical states having Eb,VBM of 185.4 and 187.2 eV, with the former belonging to boron with no oxygen neighbor and the latter to boron with an oxygen neighbor. The methodology in this work is universally applicable to all nonmetallic samples.

Substrate effect on the growth of Sn thin films

NASA Astrophysics Data System (ADS)

Chakraborty, Suvankar; Menon, Krishnakumar S. R.

2018-05-01

Growth of tin (Sn) on Ag(001), Ag(111) and W(110) substrate has been studied at elevated temperatures (473 K) using x-ray photoemission spectroscopy (XPS) and low energy electron diffraction (LEED). For Sn growth on silver substrates, it is noticed that both Sn 3d and Ag 3d core-level spectra shift in the higher binding energy direction due to the formation of surface alloy with the substrate. In both cases, surface alloy finally transforms into bulk alloy finally reaching bulk Sn value. For Sn growth on W(110) only Sn 3d core-level spectra shift in the higher binding energy direction due to surface core-level effect whereas no shift for tungsten core-level was noticed confirming no alloy formation. Sn is incorporated into the surface of substrate silver layer by removing every alternate or every third silver atoms to relieve the surface tensile stress as confirmed by LEED. On the other hand, tungsten being hard, Sn forms an overlayer structure by sitting in different energetically available positions rather than forming an alloy as energetically also it is not possible. Sn forms alloy with soft substrate silver and form overlayer films with tungsten. These studies are important in understanding the growth mechanism of Sn films on metal substrates.

Gram-level synthesis of core-shell structured catalysts for the oxygen reduction reaction in proton exchange membrane fuel cells

NASA Astrophysics Data System (ADS)

Luo, Mingchuan; Wei, Lingli; Wang, Fanghui; Han, Kefei; Zhu, Hong

2014-12-01

Over the past decade, Pt based core-shell structured alloys have been studied extensively as oxygen reduction reaction (ORR) catalysts for proton exchange membrane fuel cells (PEMFCs) because of their distinctive electrochemical performance and low Pt loading. In this paper, a facile route based on microwave-assisted polyol method and chemical dealloying process is proposed to synthesize carbon supported core-shell structured nanoparticles (NPs) in gram-level for ORR electrocatalysis in PEMFCs. The obtained samples are characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX), inductively coupled plasma atomic emission spectroscopy (ICP-AES), and X-ray photoelectron spectroscopy (XPS). These physical characterization indicate that the final synthesized NPs are highly dispersed on the carbon support, and in a core-shell structure with CuPt alloy as the core and Pt as the shell. Electrochemical measurements, conducted by cyclic voltammetry (CV) and rotating disk electrode (RDE) tests, show the core-shell structured catalyst exhibit a 3× increase in mass activity and a 2× increase in specific activity over the commercial Pt/C catalyst, respectively. These results demonstrate that this route can be a reliable way to synthesize low-Pt catalyst in large-scale for PEMFCs.

Size effects in electronic and catalytic properties of unsupported palladium nanoparticles in electrooxidation of formic acid.

PubMed

Zhou, Wei Ping; Lewera, Adam; Larsen, Robert; Masel, Rich I; Bagus, Paul S; Wieckowski, Andrzej

2006-07-13

We report a combined X-ray photoelectron spectroscopy (XPS), cyclic voltammetry (CV), and chronoamperometry (CA) study of formic acid electrooxidation on unsupported palladium nanoparticle catalysts in the particle size range from 9 to 40 nm. The CV and CA measurements show that the most active catalyst is made of the smallest (9 and 11 nm) Pd nanoparticles. Besides the high reactivity, XPS data show that such nanoparticles display the highest core-level binding energy (BE) shift and the highest valence band (VB) center downshift with respect to the Fermi level. We believe therefore that we found a correlation between formic acid oxidation current and BE and VB center shifts, which, in turn, can directly be related to the electronic structure of palladium nanoparticles of different particle sizes. Clearly, such a trend using unsupported catalysts has never been reported. According to the density functional theory of heterogeneous catalysis, and mechanistic considerations, the observed shifts are caused by a weakening of the bond strength of the COOH intermediate adsorption on the catalyst surface. This, in turn, results in the increase in the formic acid oxidation rate to CO2 (and in the associated oxidation current). Overall, our measurements demonstrate the particle size effect on the electronic properties of palladium that yields different catalytic activity in the HCOOH oxidation reaction. Our work highlights the significance of the core-level binding energy and center of the d-band shifts in electrocatalysis and underlines the value of the theory that connects the center of the d-band shifts to catalytic reactivity.

Reduction and structural modification of zirconolite on He+ ion irradiation

NASA Astrophysics Data System (ADS)

Gupta, Merry; Kulriya, P. K.; Shukla, Rishabh; Dhaka, R. S.; Kumar, Raj; Ghumman, S. S.

2016-07-01

The immobilization of minor actinides and alkaline-earth metal is a major concern in nuclear industry due to their long-term radioactive contribution to the high level waste (HLW). Materials having zirconolite, pyrochlore, and perovskite structure are promising candidates for immobilization of HLW. The zirconolite which exhibits high radiation stability and corrosion resistance behavior is investigated for its radiation stability against alpha particles in the present study. CaZrTi2O7 pellets prepared using solid state reaction techniques, were irradiated with 30 keV He+ ions for the ion fluence varying from 1 × 1017 to 1 × 1021 ions/m2. Scanning electron microscopy (SEM) images of the un-irradiated sample exhibited well separated grains with average size of about 6.8 μm. On the ion irradiation, value of the average grains size was about 7.1 μm, and change in the microstructure was insignificant. The X-ray photoelectron spectroscopy (XPS) studies showed a shift in the core level peak position (of Ca 2p, Ti 2p and Zr 3d) towards lower binding energy with respect to pristine sample as well as loss of oxygen was also observed for sample irradiated with the ion fluence of 1 × 1020 ions/m2. These indicate a decrease in co-ordination number and the ionic character of Msbnd O bond. Moreover, core level XPS signal was not detected for sample irradiated with ion fluence of 1 × 1021 ions/m2, suggesting surface damage of the sample at this ion fluence. However, X-ray diffraction (XRD) studies showed that zirconolite was not amorphized even on irradiation up to a fluence order of 1 × 1021 ion/m2. But, significant decrease in peak intensity due to creation of defects and a marginal positive peak shift due to tensile strain induced by irradiation, were observed. Thus, XRD along with XPS investigation suggests that reduction, decrease in co-ordination number, and increase in covalency are responsible for the radiation damage in zirconolite.

S2p core level spectroscopy of short chain oligothiophenes

NASA Astrophysics Data System (ADS)

Baseggio, O.; Toffoli, D.; Stener, M.; Fronzoni, G.; de Simone, M.; Grazioli, C.; Coreno, M.; Guarnaccio, A.; Santagata, A.; D'Auria, M.

2017-12-01

The Near-Edge X-ray-Absorption Fine-Structure (NEXAFS) and X-ray Photoemission Spectroscopy (XPS) of short-chain oligothiophenes (thiophene, 2,2'-bithiophene, and 2,2':5',2″-terthiophene) in the gas phase have been measured in the sulfur L2,3-edge region. The assignment of the spectral features is based on the relativistic two-component zeroth-order regular approximation time dependent density functional theory approach. The calculations allow us to estimate both the contribution of the spin-orbit splitting and of the molecular-field splitting to the sulfur binding energies and give results in good agreement with the experimental measurements. The deconvolution of the calculated S2p NEXAFS spectra into the two manifolds of excited states converging to the LIII and LII edges facilitates the attribution of the spectral structures. The main S2p NEXAFS features are preserved along the series both as concerns the energy positions and the nature of the transitions. This behaviour suggests that the electronic and geometrical environment of the sulfur atom in the three oligomers is relatively unaffected by the increasing chain length. This trend is also observed in the XPS spectra. The relatively simple structure of S2p NEXAFS spectra along the series reflects the localized nature of the virtual states involved in the core excitation process.

Exploring the core level shift origin of sulfur and thiolates on Pd(111) surfaces.

PubMed

Salvarezza, Roberto Carlos; Carro, Pilar

2015-10-07

Thiol molecules on planar metal surfaces are widely used for building sensing and electronic devices and also as capping agents to protect and to control the size and shape of nanoparticles. In the case of Pd the thiol molecules exhibit a complex behavior because C-S bond scission is possible, resulting in a significant amount of co-adsorbed S. Therefore identification of these species on Pd is a key point for many applications, a task that is usually achieved by XPS. Here we show, from DFT calculations, that the core level shift (CLS) of the S 2p binding energy (BE) of thiol and sulfur on different thiol-Pd(111) surface models strongly depends on the adsorbed or subsurface state of sulfur atoms. Our results reflect the complexity of S 2p BE behavior and contribute to understanding and reanalyzing the experimental data of thiolated Pd surfaces.

X-ray photoelectron spectrometry and binding energies of Be 1s and O 1s core levels in clinobarylite, BaBe{sub 2}Si{sub 2}O{sub 7}, from Khibiny massif, Kola peninsula

DOE Office of Scientific and Technical Information (OSTI.GOV)

Atuchin, V.V.; Kesler, V.G.; Sapozhnikov, V.K.

2008-09-15

The electronic structure of BaBe{sub 2}Si{sub 2}O{sub 7}, clinobarylite, has been investigated by means of X-ray photoelectron spectroscopy (XPS). The valence band of the crystal is mainly formed by Ba 5p, Ba 3s and O 2s states. At higher binding energies the emission lines related to the Si 2p, Be 1s, Si 2s, O 1s and numerous Ba-related states were analyzed in the photoemission spectrum. The Si KLL Auger line has been measured under excitation by the bremsstrahlung X-rays from the Al anode. Chemical bonding effects for Be 1s core level have been considered by comparison with electronic parameters measuredmore » for other beryllium containing oxides.« less

Chemical state analysis of heavily phosphorus-doped epitaxial silicon films grown on Si (1 0 0) by X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Lee, Minhyeong; Kim, Sungtae; Ko, Dae-Hong

2018-06-01

In this work, we investigated the chemical bonding states in highly P-doped Si thin films epitaxially grown on Si (0 0 1) substrates using high-resolution X-ray photoelectron spectroscopy (HR-XPS). HR-XPS P 2p core-level spectra clearly show spin-orbital splitting between P 2p1/2 and P 2p3/2 peaks in Si films doped with a high concentration of P. Moreover, the intensities of P 2p1/2 and P 2p3/2 peaks for P-doped Si films increase with P concentrations, while their binding energies remained almost identical. These results indicate that more P atoms are incorporated into the substitutional sites of the Si lattice with the increase of P concentrations. In order to identify the chemical states of P-doped Si films shown in XPS Si 2p spectra, the spectra of bulk Si were subtracted from those of Si:P samples, which enables us to clearly identify the new chemical state related to Sisbnd P bonds. We observed that the presence of the two well-resolved new peaks only for the Si:P samples at the binding energy higher than those of a Sisbnd Si bond, which is due to the strong electronegativity of P than that of Si. Experimental findings in this study using XPS open up new doors for evaluating the chemical states of P-doped Si materials in fundamental researches as well as in industrial applications.

Development of core-shell coaxially electrospun composite PCL/chitosan scaffolds.

PubMed

Surucu, Seda; Turkoglu Sasmazel, Hilal

2016-11-01

This study was related to combining of synthetic Poly (ε-caprolactone) (PCL) and natural chitosan polymers to develop three dimensional (3D) PCL/chitosan core-shell scaffolds for tissue engineering applications. The scaffolds were fabricated with coaxial electrospinning technique and the characterizations of the samples were done by thickness and contact angle (CA) measurements, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-Ray Photoelectron Spectroscopy (XPS) analyses, mechanical and PBS absorption and shrinkage tests. The average inter-fiber diameter values were calculated for PCL (0.717±0.001μm), chitosan (0.660±0.007μm) and PCL/chitosan core-shell scaffolds (0.412±0.003μm), also the average inter-fiber pore size values exhibited decreases of 66.91% and 61.90% for the PCL and chitosan scaffolds respectively, compared to PCL/chitosan core-shell ones. XPS analysis of the PCL/chitosan core-shell structures exhibited the characteristic peaks of PCL and chitosan polymers. The cell culture studies (MTT assay, Confocal Laser Scanning Microscope (CLSM) and SEM analyses) carried out with L929 ATCC CCL-1 mouse fibroblast cell line proved that the biocompatibility performance of the scaffolds. The obtained results showed that the created micro/nano fibrous structure of the PCL/chitosan core-shell scaffolds in this study increased the cell viability and proliferation on/within scaffolds. Copyright © 2016 Elsevier B.V. All rights reserved.

Electronic structure and fundamental absorption edges of KPb2Br5, K0.5Rb0.5Pb2Br5, and RbPb2Br5 single crystals

NASA Astrophysics Data System (ADS)

Tarasova, A. Yu.; Isaenko, L. I.; Kesler, V. G.; Pashkov, V. M.; Yelisseyev, A. P.; Denysyuk, N. M.; Khyzhun, O. Yu.

2012-05-01

X-ray photoelectron core-level and valence-band spectra for pristine and Ar+-ion irradiated (001) surfaces of KPb2Br5, K0.5Rb0.5Pb2Br5, and RbPb2Br5 single crystals grown by the Bridgman method have been measured and fundamental absorption edges of the ternary bromides have been recorded in the polarized light at 300 K and 80 K. The present X-ray photoelectron spectroscopy (XPS) results reveal high chemical stability of (001) surfaces of KxRb1-xPb2Br5 (x=0, 0.5, and 1.0) single crystals. Substitution of potassium for rubidium in KxRb1-xPb2Br5 does not cause any changes of binding energy values and shapes of the XPS constituent element core-level spectra. Measurements of the fundamental absorption edges indicate that band gap energy, Eg, increases by about 0.14 and 0.19 eV when temperature decreases from 300 K to 80 K in KPb2Br5 and RbPb2Br5, respectively. Furthermore, there is no dependence of the Eg value for KPb2Br5 upon the light polarization, whilst the band gap energy value for RbPb2Br5 is bigger by 0.03-0.05 eV in the case of E‖c compared to those in the cases of E‖a and E‖b.

Hidden relationship between the electrical conductivity and the Mn 2p core-level photoemission spectra in La{sub 1-x}Sr{sub x}MnO{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hishida, T.; Ohbayashi, K.; Saitoh, T.

2013-01-28

Core-level electronic structure of La{sub 1-x}Sr{sub x}MnO{sub 3} has been studied by x-ray photoemission spectroscopy (XPS). We first report, by the conventional XPS, the well-screened shoulder structure in Mn 2p{sub 3/2} peak, which had been observed only by hard x-ray photoemission spectroscopy so far. Multiple-peak analysis revealed that the Mn{sup 4+} spectral weight was not proportional to the nominal hole concentration x, indicating that a simple Mn{sup 3+}/Mn{sup 4+} intensity ratio analysis may result in a wrong quantitative elemental analysis. Considerable weight of the shoulder at x = 0.0 and the fact that the shoulder weight was even slightly goingmore » down from x = 0.2 to 0.4 were not compatible with the idea that this weight simply represents the metallic behavior. Further analysis found that the whole Mn 2p{sub 3/2} peak can be decomposed into four portions, the Mn{sup 4+}, the (nominal) Mn{sup 3+}, the shoulder, and the other spectral weight located almost at the Mn{sup 3+} location. We concluded that this weight represents the well-screened final state at Mn{sup 4+} sites, whereas the shoulder is known as that of the Mn{sup 3+} states. We found that the sum of these two spectral weight has an empirical relationship to the conductivity evolution with x.« less

Annealing effects on the chemical deposited CdS films and the electrical properties of CdS/CdTe solar cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Han, Junfeng; Institute of Materials Science, Darmstadt University of Technology, Petersenstr. 23, 64287 Darmstadt; Liao, Cheng, E-mail: Cliao@pku.edu.cn

2011-02-15

Graphical abstract: From XPS core level spectras, compared with as-depositing CdS (sample A), the Fermi level is shifting closer to the conduction band after annealing treatment in the oxygen (sample B) while it is shifting closer to the valence band after annealing treatment in the argon-hydrogen (sample C). That might be the main reason of the different performance of the final devices. The open circuit voltage of the CdS/CdTe solar cell increases when the CBD CdS is annealed with oxygen, while the performance of the solar cell decreases when the CBD CdS is annealed with argon-hydrogen. Research highlights: {yields} Twomore » different methods (oxidation and reduction) were used to anneal CdS films for CdTe solar cells. {yields} Electrical properties were analyzed by XPS (Fermi levels of CdS films). {yields} Annealing treatment in oxidation atmosphere could shift Fermi level of CdS film to higher position and consequently improve the CdS/CdTe junction and performance of solar cells. -- Abstract: CdS layers grown by chemical bath deposition (CBD) are annealed in the oxygen and argon-hydrogen atmosphere respectively. It has been found that the open circuit voltage of the CdS/CdTe solar cell increases when the CBD CdS is annealed with oxygen before the deposition of CdTe by close spaced sublimation (CSS), while the performance of the solar cell decreases when the CBD CdS is annealed with argon-hydrogen. Electronic properties of the CdS films are investigated using X-ray photo-electron spectroscopy (XPS), which indicates that the Fermi level is shifting closer to the conduction band after annealing in the oxygen and consequently a higher open circuit voltage of the solar cell can be obtained.« less

Boron difluoride dibenzoylmethane derivatives: Electronic structure and luminescence

NASA Astrophysics Data System (ADS)

Tikhonov, Sergey A.; Vovna, Vitaliy I.; Osmushko, Ivan S.; Fedorenko, Elena V.; Mirochnik, Anatoliy G.

2018-01-01

Electronic structure and optical properties of boron difluoride dibenzoylmethanate and four of its derivatives have been studied by X-ray photoelectron spectroscopy, absorption and luminescence spectroscopy and quantum chemistry (DFT, TDDFT). The relative quantum luminescence yields have been revealed to correlate with charge transfers of HOMO-LUMO transitions, energy barriers of aromatic substituents rotation and the lifetime of excited states in the investigated complexes. The bathochromic shift of intensive bands in the optical spectra has been observed to occur when the functional groups are introduced into p-positions of phenyl cycles due to destabilizing HOMO levels. Calculated energy intervals between electronic levels correlate well with XPS spectra structure of valence and core electrons.

Carbon monoxide reaction with UO2(111) single crystal surfaces: A theoretical and experimental study

NASA Astrophysics Data System (ADS)

Senanayake, S. D.; Soon, A.; Kohlmeyer, A.; Söhnel, T.; Idriss, H.

2005-07-01

The reaction of CO has been investigated on the surfaces of UO2(111) single crystal. Over the stoichiometric surface CO does not adsorb at 300 K and no further reaction is noticed. Over UO2-x (prepared by Ar+ bombardment), CO molecules adsorb and in presence of traces of H2 they couple to form acetylene molecules that desorb in two temperature domains during temperature programmed desorption (TPD). In the presence of excess H2 the coupling product is found to be ethylene. X-ray photoelectron spectroscopy (XPS) of the core level shows the presence of an U 4f line at 377 eV on the UO2-x surface, attributed to U metal. This line disappears upon CO adsorption (5 L and above) at 300 K indicating oxidation of U metal atoms by O from dissociatively adsorbed CO. XPS C 1s shows that the only C containing species formed is carbide. Computation of a α-U metal 2d-periodic slab was also conducted using plane-wave pseudopotential in the density functional theoretical framework. Two modes of CO adsorption were considered: molecular and dissociative. The dissociative adsorption was found more energetically favoured by 0.46 eV. From TPD, XPS and computation results it is strongly suggested that CO is dissociatively adsorbed on UO2-x and that a stable U-C species is formed at 300 K.

Effects of rare earth doping on multi-core iron oxide nanoparticles properties

NASA Astrophysics Data System (ADS)

Petran, Anca; Radu, Teodora; Borodi, Gheorghe; Nan, Alexandrina; Suciu, Maria; Turcu, Rodica

2018-01-01

New multi-core iron oxide magnetic nanoparticles doped with rare earth metals (Gd, Eu) were obtained by a one step synthesis procedure using a solvothermal method for potential biomedical applications. The obtained clusters were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray microanalysis (EDX), X-ray photoelectron spectroscopy (XPS) and magnetization measurements. They possess high colloidal stability, a saturation magnetization of up to 52 emu/g, and nearly spherical shape. The presence of rare earth ions in the obtained samples was confirmed by EDX and XPS. XRD analysis proved the homogeneous distribution of the trivalent rare earth ions in the inverse-spinel structure of magnetite and the increase of crystal strain upon doping the samples. XPS study reveals the valence state and the cation distribution on the octahedral and tetrahedral sites of the analysed samples. The observed shift of the XPS valence band spectra maximum in the direction of higher binding energies after rare earth doping, as well as theoretical valence band calculations prove the presence of Gd and Eu ions in octahedral sites. The blood protein adsorption ability of the obtained samples surface, the most important factor of the interaction between biomaterials and body fluids, was assessed by interaction with bovine serum albumin (BSA). The rare earth doped clusters surface show higher afinity for binding BSA. In vitro cytotoxicity test results for the studied samples showed no cytotoxicity in low and medium doses, establishing a potential perspective for rare earth doped MNC to facilitate multiple therapies in a single formulation for cancer theranostics.

Upgrade of beamline BL08B at Taiwan Light Source from a photon-BPM to a double-grating SGM beamline.

PubMed

Yuh, Jih Young; Lin, Shan Wei; Huang, Liang Jen; Fung, Hok Sum; Lee, Long Life; Chen, Yu Joung; Cheng, Chiu Ping; Chin, Yi Ying; Lin, Hong Ji

2015-09-01

During the last 20 years, beamline BL08B has been upgraded step by step from a photon beam-position monitor (BPM) to a testing beamline and a single-grating beamline that enables experiments to record X-ray photo-emission spectra (XPS) and X-ray absorption spectra (XAS) for research in solar physics, organic semiconductor materials and spinel oxides, with soft X-ray photon energies in the range 300-1000 eV. Demands for photon energy to extend to the extreme ultraviolet region for applications in nano-fabrication and topological thin films are increasing. The basic spherical-grating monochromator beamline was again upgraded by adding a second grating that delivers photons of energy from 80 to 420 eV. Four end-stations were designed for experiments with XPS, XAS, interstellar photoprocess systems (IPS) and extreme-ultraviolet lithography (EUVL) in the scheduled beam time. The data from these experiments show a large count rate in core levels probed and excellent statistics on background normalization in the L-edge adsorption spectrum.

Surface damage in cystine, an amino acid dimer, induced by keV ions.

PubMed

Salles, R C M; Coutinho, L H; da Veiga, A G; Sant'Anna, M M; de Souza, G G B

2018-01-28

We have studied the interaction of an ion beam (17.6 keV F - ) with cystine, a dimer formed by the binding of two cysteine residues. Cystine can be considered as an ideal prototype for the study of the relevance of the disulfide (-S-S-) chemical bond in biomolecules. For the sake of comparison, the amino acid cysteine has also been subjected to the same experimental conditions. Characterization of the samples by XPS and NEXAFS shows that both pristine cystine and pristine cysteine are found as a dipolar ion (zwitterion). Following irradiation, the dimer and the amino acid show a tendency to change from the dipole ion form to the normal uncharged form. The largest spectral modification was observed in the high resolution XPS spectra obtained at around the N 1s core level for the two biomolecules. The 2p sulfur edge spectra of cysteine and cystine were much less sensitive to radiation effects. We suggest that the disulfide bond (-S-S-) remains stable before and after irradiation, contributing to the larger radiation stability of cystine as compared to the amino acid cysteine.

Effect of Ni Core Structure on the Electrocatalytic Activity of Pt-Ni/C in Methanol Oxidation

PubMed Central

Kang, Jian; Wang, Rongfang; Wang, Hui; Liao, Shijun; Key, Julian; Linkov, Vladimir; Ji, Shan

2013-01-01

Methanol oxidation catalysts comprising an outer Pt-shell with an inner Ni-core supported on carbon, (Pt-Ni/C), were prepared with either crystalline or amorphous Ni core structures. Structural comparisons of the two forms of catalyst were made using transmission electron microscopy (TEM), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS), and methanol oxidation activity compared using CV and chronoamperometry (CA). While both the amorphous Ni core and crystalline Ni core structures were covered by similar Pt shell thickness and structure, the Pt-Ni(amorphous)/C catalyst had higher methanol oxidation activity. The amorphous Ni core thus offers improved Pt usage efficiency in direct methanol fuel cells. PMID:28811402

Adsorption study of copper phthalocyanine on Si(111)(√3 × √3)R30°Ag surface

NASA Astrophysics Data System (ADS)

Menzli, S.; Ben Hamada, B.; Arbi, I.; Souissi, A.; Laribi, A.; Akremi, A.; Chefi, C.

2016-04-01

The adsorption of copper phthalocyanine (CuPc) molecules on Si(111)(√3 × √3)R30°Ag surface is studied at room temperature under ultra high vacuum. Crystallographic, chemical and electronic properties of the interface are investigated by low energy electron diffraction (LEED), ultraviolet and X-ray photoemission spectroscopies (UPS, XPS) and X-ray photoemission diffraction (XPD). LEED and XPD results indicate that after one monolayer deposition the molecular layer is highly ordered with a flat lying adsorption configuration. The corresponding pattern reveals the coexistence of three symmetrically equivalent orientations of molecules with respect to the substrate. XPS core level spectra of the substrate reveal that there is no discernible chemical interaction between molecules and substrate; however there is evidence of Fermi level movement. During the growth, the work function was found to decrease from 4.90 eV for the clean substrate to 4.35 eV for the highest coverage (60 monolayers). Within a thickness of two monolayer deposition an interface dipole of 0.35 eV and a band bending of 0.2 eV have been found. UPS spectra indicate the existence of a band bending of the highest occupied molecular orbital (HOMO) of 0.55 eV. The changes in the work function, in the Fermi level position and in the HOMO state have been used to determine the energy level alignment at the interface.

First-principle calculation of core level binding energies of Li{sub x}PO{sub y}N{sub z} solid electrolyte

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guille, Émilie; Vallverdu, Germain, E-mail: germain.vallverdu@univ-pau.fr; Baraille, Isabelle

2014-12-28

We present first-principle calculations of core-level binding energies for the study of insulating, bulk phase, compounds, based on the Slater-Janak transition state model. Those calculations were performed in order to find a reliable model of the amorphous Li{sub x}PO{sub y}N{sub z} solid electrolyte which is able to reproduce its electronic properties gathered from X-ray photoemission spectroscopy (XPS) experiments. As a starting point, Li{sub 2}PO{sub 2}N models were investigated. These models, proposed by Du et al. on the basis of thermodynamics and vibrational properties, were the first structural models of Li{sub x}PO{sub y}N{sub z}. Thanks to chemical and structural modifications appliedmore » to Li{sub 2}PO{sub 2}N structures, which allow to demonstrate the relevance of our computational approach, we raise an issue concerning the possibility of encountering a non-bridging kind of nitrogen atoms (=N{sup −}) in Li{sub x}PO{sub y}N{sub z} compounds.« less

Probing molecular orientations in thin films by x-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Li, Y.; Li, P.; Lu, Z.-H.

2018-03-01

A great number of functional organic molecules in active thin-film layers of optoelectronic devices have highly asymmetric structures, such as plate-like, rod-like, etc. This makes molecular orientation an important aspect in thin-films as it can significantly affect both the optical and electrical performance of optoelectronic devices. With a combination of in-situ ultra violet photoelectron spectroscopy (UPS) and x-ray photoelectron spectroscopy (XPS) investigations for organic molecules having a broad range of structural properties, we discovered a rigid connection of core levels and frontier highest occupied molecular orbital levels at organic interfaces. This finding opens up opportunities of using X-ray photoemission spectroscopy as an alternative tool to UPS for providing an easy and unambiguous data interpretation in probing molecular orientations.

Direct work function measurement by gas phase photoelectron spectroscopy and its application on PbS nanoparticles.

PubMed

Axnanda, Stephanus; Scheele, Marcus; Crumlin, Ethan; Mao, Baohua; Chang, Rui; Rani, Sana; Faiz, Mohamed; Wang, Suidong; Alivisatos, A Paul; Liu, Zhi

2013-01-01

Work function is a fundamental property of a material's surface. It is playing an ever more important role in engineering new energy materials and efficient energy devices, especially in the field of photovoltaic devices, catalysis, semiconductor heterojunctions, nanotechnology, and electrochemistry. Using ambient pressure X-ray photoelectron spectroscopy (APXPS), we have measured the binding energies of core level photoelectrons of Ar gas in the vicinity of several reference materials with known work functions (Au(111), Pt(111), graphite) and PbS nanoparticles. We demonstrate an unambiguously negative correlation between the work functions of reference samples and the binding energies of Ar 2p core level photoelectrons detected from the Ar gas near the sample surface region. Using this experimentally determined linear relationship between the surface work function and Ar gas core level photoelectron binding energy, we can measure the surface work function of different materials under different gas environments. To demonstrate the potential applications of this ambient pressure XPS technique in nanotechnology and solar energy research, we investigate the work functions of PbS nanoparticles with various capping ligands: methoxide, mercaptopropionic acid, and ethanedithiol. Significant Fermi level position changes are observed for PbS nanoparticles when the nanoparticle size and capping ligands are varied. The corresponding changes in the valence band maximum illustrate that an efficient quantum dot solar cell design has to take into account the electrochemical effect of the capping ligand as well.

Accurate quasiparticle calculation of x-ray photoelectron spectra of solids

NASA Astrophysics Data System (ADS)

Aoki, Tsubasa; Ohno, Kaoru

2018-05-01

It has been highly desired to provide an accurate and reliable method to calculate core electron binding energies (CEBEs) of crystals and to understand the final state screening effect on a core hole in high resolution x-ray photoelectron spectroscopy (XPS), because the ΔSCF method cannot be simply used for bulk systems. We propose to use the quasiparticle calculation based on many-body perturbation theory for this problem. In this study, CEBEs of band-gapped crystals, silicon, diamond, β-SiC, BN, and AlP, are investigated by means of the GW approximation (GWA) using the full ω integration and compared with the preexisting XPS data. The screening effect on a deep core hole is also investigated in detail by evaluating the relaxation energy (RE) from the core and valence contributions separately. Calculated results show that not only the valence electrons but also the core electrons have an important contribution to the RE, and the GWA have a tendency to underestimate CEBEs due to the excess RE. This underestimation can be improved by introducing the self-screening correction to the GWA. The resulting C1s, B1s, N1s, Si2p, and Al2p CEBEs are in excellent agreement with the experiments within 1 eV absolute error range. The present self-screening corrected GW approach has the capability to achieve the highly accurate prediction of CEBEs without any empirical parameter for band-gapped crystals, and provide a more reliable theoretical approach than the conventional ΔSCF-DFT method.

Accurate quasiparticle calculation of x-ray photoelectron spectra of solids.

PubMed

Aoki, Tsubasa; Ohno, Kaoru

2018-05-31

It has been highly desired to provide an accurate and reliable method to calculate core electron binding energies (CEBEs) of crystals and to understand the final state screening effect on a core hole in high resolution x-ray photoelectron spectroscopy (XPS), because the ΔSCF method cannot be simply used for bulk systems. We propose to use the quasiparticle calculation based on many-body perturbation theory for this problem. In this study, CEBEs of band-gapped crystals, silicon, diamond, β-SiC, BN, and AlP, are investigated by means of the GW approximation (GWA) using the full ω integration and compared with the preexisting XPS data. The screening effect on a deep core hole is also investigated in detail by evaluating the relaxation energy (RE) from the core and valence contributions separately. Calculated results show that not only the valence electrons but also the core electrons have an important contribution to the RE, and the GWA have a tendency to underestimate CEBEs due to the excess RE. This underestimation can be improved by introducing the self-screening correction to the GWA. The resulting C1s, B1s, N1s, Si2p, and Al2p CEBEs are in excellent agreement with the experiments within 1 eV absolute error range. The present self-screening corrected GW approach has the capability to achieve the highly accurate prediction of CEBEs without any empirical parameter for band-gapped crystals, and provide a more reliable theoretical approach than the conventional ΔSCF-DFT method.

Toward a comprehensive understanding of solid-state core-level XPS linewidths: Experimental and theoretical studies on the Si2p and O1s linewidths in silicates

NASA Astrophysics Data System (ADS)

Bancroft, G. M.; Nesbitt, H. W.; Ho, R.; Shaw, D. M.; Tse, J. S.; Biesinger, M. C.

2009-08-01

High resolution X-ray Photoelectron Spectroscopy (XPS) core-level Si2p and O1s spectra of the nonconductors α-SiO2 (quartz) at 120 and 300 K and vitreous SiO2 at 300 K were obtained with a Kratos Axis Ultra XPS instrument (instrumental resolution of <0.4eV ) which incorporates a unique charge compensation system that minimizes differential charge broadening on nonconductors. The Si2p and O1s linewidths at 300 K ( ˜1.1 and ˜1.2eV , respectively) are similar for all silicates (and similar to previous thin film SiO2 spectra obtained previously), showing that differential charging does not contribute significantly to our spectra. At 120 K, there is a small decrease (0.04 eV) in the Si2p linewidth of α-SiO2 , but no measurable decrease in O1s linewidth. The O1s lines are generally and distinctly asymmetric. We consider all possible sources of line broadening and show that final state vibrational broadening (FSVB) and phonon broadening are the major causes of the broad and asymmetric lines. Previous high resolution gas phase XPS studies have identified large FSVB contributions to the Si2p spectra of SiCl4 , SiF4 , and Si(OCH3)4 molecules, and this vibrational structure leads total Si2p3/2 linewidths of up to ˜0.5eV , even with individual peak linewidths of <0.1eV . The Si atom of Si(OCH3)4 is an excellent analog for Si in crystalline SiO2 because the Si-O bond lengths and symmetric stretch frequencies are similar in both compounds. Similar vibrational contributions to the Si2p and O1s spectra of solid silicates are anticipated if the Si2p and O1s core-hole states produce similar changes to the Si-O bond length in both phases. To investigate the possibility, Car-Parrinello molecular dynamics calculations were performed and show that changes to Si-O bond lengths between ion and ground states (Δr) for both Si2p and O1s hole states are similar for both crystalline SiO2 and gaseous Si(OCH3)4 . Δr are -0.04Å for Si2p and ˜+0.05Å for O1s in both compounds. Indeed, the vibrational envelope from the Si2p spectrum of Si(OCH3)4 , broadened to our instrumental linewidth of 0.4 eV, accounts for the majority (˜0.8eV) of the Si2p3/2 linewidth for crystalline SiO2 (˜1.1eV) with phonon broadening accounting for the remainder. The results provide excellent support for the tenet that final state vibrational splitting, as seen in the gas phase molecules, similarly affects the solid-state spectra. The calculations also indicate that the O1s linewidths should be larger than the Si2p linewidths, as observed in our spectra. FSVB should also lead to small peak asymmetries, as seen in the O1s spectra. The contribution of phonon broadening to the linewidth is also evaluated and shown to be comparable to the FSVB contribution at 120 and 300 K but considerably smaller at very low temperatures.

Formation and stability of dense arrays of Au nanoclusters on hexagonal boron nitride/Rh(111)

NASA Astrophysics Data System (ADS)

Patterson, Matthew C.; Habenicht, Bradley F.; Kurtz, Richard L.; Liu, Li; Xu, Ye; Sprunger, Phillip T.

2014-05-01

We have studied the nucleation and growth of Au clusters at submonolayer and greater coverages on the h-BN nanomesh grown on Rh(111) by means of scanning tunneling microscopy (STM), x-ray photoelectron spectroscopy (XPS), and density functional theory (DFT). STM reveals that submonolayer Au deposited at 115 K nucleates within the nanomesh pores and remains confined to the pores even after warming to room temperature. Whereas there is a propensity of monoatomic high islands at low temperature, upon annealing, bi- and multilayer Au clusters emerge. Deposition of higher coverages of Au similarly results in Au clusters primarily confined to the nanomesh pores at room temperature. XPS analysis of core-level electronic states in the deposited Au shows strong final-state effects induced by restricted particle size dominating for low Au coverage, with indications that larger Au clusters are negatively charged by interaction through the h-BN monolayer. DFT calculations suggest that the structure of the Au clusters transitions from monolayer to bilayer at a size between 30 and 37 atoms per cluster, in line with our experiment. Bader charge analysis supports the negative charge state of deposited Au.

Incommensurate growth of Co thin film on close-packed Ag(111) surface

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barman, Sukanta, E-mail: sukanta.ac@gmail.com; Menon, Krishna Kumar S. R., E-mail: krishna.menon@saha.ac.in

2016-05-06

Growth of ultrathin Co layers on close-packed Ag(111)were investigated by means of Low Energy Electron Diffraction (LEED), X-ray Photoelectron Spectroscopy (XPS) and Angle-resolved Photoemission Spectroscopy(ARPES) techniques. The close-packed hexagonal face of Co(0001), exhibits a lattice misfit about 13% with Ag(111) surface which manipulates the growth to be incommensurate up to a certain thickness. The strain field causes aperiodic height undulation in the sub-angstrom regime of the film which was confirmed by p(1 × 1) LEED pattern along with a 6-fold moiré reconstruction pattern in the lower film thickness (up to ∼2ML). The evolution of the LEED pattern was studied withmore » increasing film coverage. Lattice strain was measured with respect to the relative positions of these double spots as a functionof film thickness. Almost a constant strain (∼13%) in the full range of film thickness explains the moiré pattern formation in order to stabilize the incommensurate growth. For higher film coverages, an epitaxial well-ordered commensurate growth was observed. Core level and valance band electronic structures of these films were studied by XPS and ARPES techniques.« less

Crystal growth of Bi{sub 2}Te{sub 3} and noble cleaved (0001) surface properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Atuchin, V.V., E-mail: atuchin@thermo.isp.nsc.ru; Functional Electronics Laboratory, Tomsk State University, Tomsk 634050; Golyashov, V.A.

2016-04-15

A high quality Bi{sub 2}Te{sub 3} crystal has been grown by Bridgman method with the use of rotating heat field. The phase purity and bulk structural quality of the crystal have been verified by XRD analysis and rocking curve observation. The atomically smooth Bi{sub 2}Te{sub 3}(0001) surface with an excellent crystallographic quality is formed by cleavage in the air. The chemical and microstructural properties of the surface have been evaluated with RHEED, AFM, STM, SE and XPS. The Bi{sub 2}Te{sub 3}(0001) cleaved surface is formed by atomically smooth terraces with the height of the elemental step of ~1.04±0.1 nm, asmore » estimated by AFM. There is no surface oxidation process detected over a month keeping in the air at normal conditions, as shown by comparative core level photoelectron spectroscopy. - Graphical abstract: A high quality Bi{sub 2}Te{sub 3} crystal has been grown by Bridgman method with the use of rotating heat field and the Bi{sub 2}Te{sub 3}(0001) cleaved surface has been evaluated with RHEED, AFM, STM, SE and XPS. - Highlights: • High-quality Bi{sub 2}Te{sub 3} crystal of 10 mm in diameter and 50 mm long have been grown. • The high-purity cleaved Bi{sub 2}Te{sub 3}(0001) surface has been evaluated by RHEED, AFM, STM and XPS methods. • The Bi{sub 2}Te{sub 3} surface covered by atomically smooth (0001) terraces is chemically stable for a long time.« less

Preparation of paclitaxel/chitosan co-assembled core-shell nanofibers for drug-eluting stent

NASA Astrophysics Data System (ADS)

Tang, Jing; Liu, Yongjia; Zhu, Bangshang; Su, Yue; Zhu, Xinyuan

2017-01-01

The paclitaxel/chitosan (PTX/CS) core-shell nanofibers (NFs) are easily prepared by co-assembly of PTX and CS and used in drug-eluting stent. The mixture solution of PTX (dissolved in ethanol) and CS (dissolved in 1% acetic acid water solution) under sonication will make the formation of NFs, in which small molecule PTX co-assembles with biomacromolecular CS through non-covalent interactions. The obtained NFs are tens to hundreds nanometers in diameter and millimeter level in length. Furthermore, the structure of PTX/CS NFs was characterized by confocal laser scanning microscopy (CLSM), zeta potential, X-ray photoelectron spectroscopy (XPS) and nanoscale infra-red (nanoIR), which provided evidences demonstrated that PTX/CS NFs are core-shell structures. The 'shell' of CS wrapped outside of the NFs, while PTX is located in the core. Thus it resulted in high drug loading content (>40 wt.%). The well-controlled drug release, low cytotoxicity and good haemocompatibility were also found in drug carrier system of PTX/CS NFs. In addition, the hydrophilic and flexible properties of NFs make them easily coating and filming on stent to prepare drug-eluting stent (DES). Therefore, this study provides a convenient method to prepare high PTX loaded NFs, which is a promising nano-drug carrier used for DES and other biomedical applications. The possible molecular mechanism of PTX and CS co-assembly and core-shell nanofiber formation is also explored.

Electronic Interactions of Size-Selected Oxide Clusters on Metallic and Thin Film Oxide Supports

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xue, Meng; Nakayama, Miki; Liu, Ping

The interfacial electronic structure of various size-selected metal oxide nanoclusters (M 3O x; M = Mo, Nb, Ti) on Cu(111) and a thin film of Cu 2O supports were investigated in this paper by a combination of experimental methods and density functional theory (DFT). These systems explore electron transfer at the metal–metal oxide interface which can modify surface structure, metal oxidation states, and catalytic activity. Electron transfer was probed by measurements of surface dipoles derived from coverage dependent work function measurements using two-photon photoemission (2PPE) and metal core level binding energy spectra from X-ray photoelectron spectroscopy (XPS). The measured surfacemore » dipoles are negative for all clusters on Cu(111) and Cu 2O/Cu(111), but those on the Cu 2O surface are much larger in magnitude. In addition, sub-stoichiometric or “reduced” clusters exhibit smaller surface dipoles on both the Cu(111) and Cu 2O surfaces. Negative surface dipoles for clusters on Cu(111) suggest Cu → cluster electron transfer, which is generally supported by DFT-calculated Bader charge distributions. For Cu 2O/Cu(111), calculations of the surface electrostatic potentials show that the charge distributions associated with cluster adsorption structures or distortions at the cluster–Cu 2O–Cu(111) interface are largely responsible for the observed negative surface dipoles. Changes observed in the XPS spectra for the Mo 3d, Nb 3d, and Ti 2p core levels of the clusters on Cu(111) and Cu 2O/Cu(111) are interpreted with help from the calculated Bader charges and cluster adsorption structures, the latter providing information about the presence of inequivalent cation sites. Finally, the results presented in this work illustrate how the combined use of different experimental probes along with theoretical calculations can result in a more realistic picture of cluster–support interactions and bonding.« less

Electronic Interactions of Size-Selected Oxide Clusters on Metallic and Thin Film Oxide Supports

DOE PAGES

Xue, Meng; Nakayama, Miki; Liu, Ping; ...

2017-09-13

The interfacial electronic structure of various size-selected metal oxide nanoclusters (M 3O x; M = Mo, Nb, Ti) on Cu(111) and a thin film of Cu 2O supports were investigated in this paper by a combination of experimental methods and density functional theory (DFT). These systems explore electron transfer at the metal–metal oxide interface which can modify surface structure, metal oxidation states, and catalytic activity. Electron transfer was probed by measurements of surface dipoles derived from coverage dependent work function measurements using two-photon photoemission (2PPE) and metal core level binding energy spectra from X-ray photoelectron spectroscopy (XPS). The measured surfacemore » dipoles are negative for all clusters on Cu(111) and Cu 2O/Cu(111), but those on the Cu 2O surface are much larger in magnitude. In addition, sub-stoichiometric or “reduced” clusters exhibit smaller surface dipoles on both the Cu(111) and Cu 2O surfaces. Negative surface dipoles for clusters on Cu(111) suggest Cu → cluster electron transfer, which is generally supported by DFT-calculated Bader charge distributions. For Cu 2O/Cu(111), calculations of the surface electrostatic potentials show that the charge distributions associated with cluster adsorption structures or distortions at the cluster–Cu 2O–Cu(111) interface are largely responsible for the observed negative surface dipoles. Changes observed in the XPS spectra for the Mo 3d, Nb 3d, and Ti 2p core levels of the clusters on Cu(111) and Cu 2O/Cu(111) are interpreted with help from the calculated Bader charges and cluster adsorption structures, the latter providing information about the presence of inequivalent cation sites. Finally, the results presented in this work illustrate how the combined use of different experimental probes along with theoretical calculations can result in a more realistic picture of cluster–support interactions and bonding.« less

Electronic structure of layered titanate Nd 2Ti 2O 7

NASA Astrophysics Data System (ADS)

Atuchin, V. V.; Gavrilova, T. A.; Grivel, J.-C.; Kesler, V. G.

2008-10-01

The electronic structure of the binary titanate Nd 2Ti 2O 7 has been studied by X-ray photoelectron spectroscopy (XPS). Spectral features of the valence band and all constituent element core levels have been considered. The Auger parameters of titanium and oxygen in Nd 2Ti 2O 7 are determined as αTi = 873.5 and αO = 1042.2 eV. Chemical bonding effects have been discussed with the binding energies differences ΔTi = (BE O 1s - BE Ti 2p 3/2) = 71.5 eV and ΔNd = (BE Nd 3d 5/2 - BE O 1s) = 452.5 eV as key parameters in comparison with those in other titanium- and neodymium-bearing oxides.

Structural, morphological and electronic properties of pulsed laser grown Eu2O3 thin films

NASA Astrophysics Data System (ADS)

Kumar, Sandeep; Prakash, Ram; Choudhary, R. J.; Phase, D. M.

2018-05-01

Herein, we report the growth, structural, morphological and electronic properties of Europium sesquioxide (Eu2O3) thin films on Si [1 0 0] substrate using pulsed laser deposition technique. The films were deposited at ˜750 °C substrate temperature while the oxygen partial pressure (OPP) was varied (vacuum,˜1 mTorr, ˜10 mTorr and ˜300 mTorr). X-ray diffraction results confirm the single phase cubic structure of the film grown at ˜300 mTorr. The XRD results are also supported by the Raman's spectroscopy results. Eu-3d XPS core level spectra confirms the dominant contributions from the "3+" states of Eu in the film.

Toward a computational and experimental model of a poly-epoxy surface

NASA Astrophysics Data System (ADS)

Duguet, Thomas; Bessaguet, Camille; Aufray, Maëlenn; Esvan, Jérôme; Charvillat, Cédric; Vahlas, Constantin; Lacaze-Dufaure, Corinne

2015-01-01

A model poly-epoxy surface formed by the reaction of DGEBA and EDA is studied by the combination of experiments and DFT calculations. A special synthesis protocol is presented leading to the formation of a surface that is smooth (Sa < 1 nm), chemically homogeneous, and that presents a low-defect density (0.21 μm-2), as shown by AFM characterizations. Then, XPS is used for the determination of the elemental and functional groups' surface composition. DFT allows the identification and assignment of individual bonds contributions to the experimental 1s core-level peaks. Overall, we demonstrate that such a model sample is perfectly suitable for a use as a template for the study of poly-epoxy surface functionalization.

Automated Creation of Labeled Pointcloud Datasets in Support of Machine-Learning Based Perception

DTIC Science & Technology

2017-12-01

computationally intensive 3D vector math and took more than ten seconds to segment a single LIDAR frame from the HDL-32e with the Dell XPS15 9650’s Intel...Core i7 CPU. Depth Clustering avoids the computationally intensive 3D vector math of Euclidean Clustering-based DON segmentation and, instead

Destruction behavior of hexabromocyclododecanes during incineration of solid waste containing expanded and extruded polystyrene insulation foams.

PubMed

Takigami, Hidetaka; Watanabe, Mafumi; Kajiwara, Natsuko

2014-12-01

Hexabromocyclododecanes (HBCDs) have been used for flame retardation mainly in expanded polystyrene (EPS) and extruded polystyrene (XPS) insulation foams. Controlled incineration experiments with solid wastes containing each of EPS and XPS were conducted using a pilot-scale incinerator to investigate the destruction behavior of HBCDs and their influence on the formation of polybrominated dibenzo-p-dioxins and dibenzofurans (PBDD/DFs). EPS and XPS materials were respectively blended with refuse derived fuel (RDF) as input wastes for incineration. Concentrations of HBCDs contained in the EPS- and XPS-added RDFs, were 140 and 1100 mg kg(-1), respectively. In which γ-HBCD was dominant (68% of the total HBCD content) in EPS-added RDF and α-HBCD accounted for 73% of the total HBCDs in XPS-added RDF. During the incineration experiments with EPS and XPS, primary and secondary combustion zones were maintained at temperatures of 840 °C and 900 °C. The residence times of waste in the primary combustion zone and flue gas in the secondary combustion zone was 30 min and three seconds, respectively. HBCDs were steadily degraded in the combustion chambers and α-, β-, and γ-HBCD behaved similarly. Concentration levels of the total HBCDs in the bag filter exit gas for the two experiments with EPS and XPS were 0.7 and 0.6ngmN(-3), respectively. HBCDs were also not detected (<0.2 ng g(-1)) in the bottom and fly ash samples. From the obtained results, it was calculated that HBCDs were sufficiently destroyed in the whole incineration process with destruction efficiencies of more than 99.9999 for both of EPS and XPS cases. For PBDD/DFs, the levels detected in the bottom and fly ash samples were very low (0.028 ng g(-1) at maximum). In the case of XPS-added experiment, 2,3,7,8-TeBDD and 2,3,7,8-TeBDF were determined in the flue gas at levels (0.05-0.07 ng mN(-3)) slightly over the detection limits in the environmental emission gas samples, suggesting HBCDs in XPS are possibly a precursor of detected PBDD/DFs. Operational care should be taken when the ratio of HBCD-containing polystyrene is increased in the input wastes just to make sure of formation prevention and emission control of PBDD/DFs. The concentrations and congener patterns of PCDD/DFs and dl-PCBs in the samples during the three experiments were not affected by an addition of HBCDs. Copyright © 2014 Elsevier Ltd. All rights reserved.

XPS and NRA investigations during the fabrication of gold nanostructured functionalized screen-printed sensors for the detection of metallic pollutants

NASA Astrophysics Data System (ADS)

Jasmin, Jean-Philippe; Miserque, Frédéric; Dumas, Eddy; Vickridge, Ian; Ganem, Jean-Jacques; Cannizzo, Caroline; Chaussé, Annie

2017-03-01

An all covalent nanostructured lead sensor was built by the successive grafting of gold nanoparticles and carboxylic ligands at the surface of self-adhesive carbon screen-printed electrodes (SPEs). Surface analysis techniques were used in each step in order to investigate the structuration of this sensor. The self-adhesive surfaces were made from the electrochemical grafting of p-phenylenediamine at the surface of the SPEs via diazonium salts chemistry. The quantity of grafted aniline functions, estimated by Nuclear Reaction Analysis (NRA) performed with p-phenylenediamine labelled with 15N isotope, is in agreement with an almost complete coverage of the electrode surface. The subsequent diazotization of the aniline functions at the surface of the SPEs was performed; X-ray Photoelectron Spectroscopy (XPS) allowed us to consider a quantitative conversion of the aniline functions into diazonium moieties. The spontaneous grafting of gold nanoparticles on the as-obtained reactive surfaces ensures the nanostructuration of the material, and XPS studies showed that the covalent bonding of the gold nanoparticles at the surface of the SPEs induces a change both in the Au-4f (gold nanoparticles) and Cl-2p (carbon ink) core level signals. These unusual observations are explained by an interaction between the carbon ink constituting the substrate and the gold nanoparticles. Heavy and toxic metals are considered of major environmental concern because of their non-biodegradability. In a final step, the grafting of the carboxylic ligands at the surface of the SPEs and an accumulation step in the presence of lead(II) cations allowed us to evidence the interest of nanostructured materials as metallic pollutants sensors.

Crystal structure and X-ray photoemission spectroscopic study of A{sub 2}LaMO{sub 6} [A=Ba, Ca; M=Nb, Ta

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dutta, Alo, E-mail: alo_dutta@yahoo.com; Saha, Sujoy; Kumari, Premlata

2015-09-15

The X-ray photoemission spectroscopic (XPS) study of the double perovskite oxides A{sub 2}LaMO{sub 6} [A=Ba, Ca; M=Nb, Ta] synthesized by the solid-state reaction technique has been carried out to investigate the nature of the chemical state of the constituent ions and the bonding between them. The Rietveld refinement of the X-ray diffraction patterns suggests the monoclinic crystal structure of all the materials at room temperature. The negative and positive chemical shifts of the core level XPS spectrum of O-1s and Nb-3d{sub 3/2}/Ta-4f{sub 5/2} respectively suggest the covalent bonding between Nb/Ta cations and O ion. The change of the bonding strengthmore » between the anion and the cations from one material to another has been analyzed. The vibrational property of the materials is investigated using the room temperature Raman spectra. A large covalency of Ta-based compound than Nb compound is confirmed from the relative shifting of the Raman modes of the materials. - Graphical abstract: Crystal structure of two perovskite oxides CLN and CLT is investigated. XPS study confirms the two different co-ordination environments of Ca and covalent bonding between B-site cations and O-ion. - Highlights: • Ordered perovskite structure obtained by Rietveld refinement of XRD patterns. • Study of nature of chemical bonding by X-ray photoemission spectroscopy. • Opposite chemical shift of d-states of Nb/Ta with respect to O. • Covalent bonding between d-states of Nb/Ta and O. • Relative Raman shifts of CLN and CLT substantiate the more covalent character of Ta than Nb.« less

Effects of oxide replacement with fluoride at the CoFeB interface on interface magnetic anisotropy and its voltage control

NASA Astrophysics Data System (ADS)

Pankieiev, Mykhailo; Kita, Koji

2018-05-01

In this paper we report results of improving Co60Fe20B20 interface perpendicular magnetic anisotropy (PMA) by replacing neighbor oxide layer with fluoride one. We expected that fluorine as element with higher than oxide electronegativity could more effectively attract electrons from out-of-plane d orbitals of ferromagnetic, increasing role of in-plane orbitals. By this we wanted to increase PMA and its response to applied voltage bias. Polar magneto-optic Kerr effect measurement show decreasing of out-of-plane magnetic field needed to change magnetization to perpendicular in stacks with oxygen replaced by fluorine as well as increasing of coefficient of response to applied voltage α from < 10 fJ/Vm for CoFeB/Al2O3 interface to 20 fJ/Vm for CoFeB/AlF3/Al2O3 and 22 fJ/Vm for CoFeB/MgF2 stacks. Direct chemical interaction of Co with F was confirmed by x-ray photoelectron spectroscopy (XPS) measurement of Co2p core level region. Moreover angular-resolved XPS showed that F tends to stay at CoFeB interface rather than diffuse out of it.

Internal structure of InP/ZnS nanocrystals unraveled by high-resolution soft X-ray photoelectron spectroscopy.

PubMed

Huang, Kai; Demadrille, Renaud; Silly, Mathieu G; Sirotti, Fausto; Reiss, Peter; Renault, Olivier

2010-08-24

High-energy resolution photoelectron spectroscopy (DeltaE < 200 meV) is used to investigate the internal structure of semiconductor quantum dots containing low Z-contrast elements. In InP/ZnS core/shell nanocrystals synthesized using a single-step procedure (core and shell precursors added at the same time), a homogeneously alloyed InPZnS core structure is evidenced by quantitative analysis of their In3d(5/2) spectra recorded at variable excitation energy. When using a two-step method (core InP nanocrystal synthesis followed by subsequent ZnS shell growth), XPS analysis reveals a graded core/shell interface. We demonstrate the existence of In-S and S(x)-In-P(1-x) bonding states in both types of InP/ZnS nanocrystals, which allows a refined view on the underlying reaction mechanisms.

Ultrasonic approach to the synthesis of HMX@TATB core-shell microparticles with improved mechanical sensitivity.

PubMed

Huang, Bing; Hao, Xiaofei; Zhang, Haobin; Yang, Zhijian; Ma, Zhigang; Li, Hongzhen; Nie, Fude; Huang, Hui

2014-07-01

To improve the safety of sensitive explosive HMX while maintaining explosion performance, a moderately powerful but insensitive explosive TATB was used to coat HMX microparticles via a facile ultrasonic method. By using Estane as surface modifier and nano-sized TATB as the shell layer, the HMX@TATB core-shell microparticles with a monodisperse size and compact shell structure were successfully constructed. Both scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) results confirmed the formation of perfect core-shell structured composites. Based on a systematic and comparative study of the effect of experimental conditions, a possible formation mechanism of core-shell structure was proposed in detail. Moreover, the perfect core-shell HMX@TATB microparticles exhibited a unique thermal behavior and significantly improved mechanical sensitivity compared with that of the physical mixture. Copyright © 2014 Elsevier B.V. All rights reserved.

Acetate- and thiol-capped monodisperse ruthenium nanoparticles: XPS, XAS, and HRTEM studies.

PubMed

Chakroune, Nassira; Viau, Guillaume; Ammar, Souad; Poul, Laurence; Veautier, Delphine; Chehimi, Mohamed M; Mangeney, Claire; Villain, Françoise; Fiévet, Fernand

2005-07-19

Monodisperse ruthenium nanoparticles were prepared by reduction of RuCl3 in 1,2-propanediol. The mean particle size was controlled by appropriate choice of the reduction temperature and the acetate ion concentration. Colloidal solutions in toluene were obtained by coating the metal particles with dodecanethiol. High-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), and X-ray absorption spectroscopy (XANES and EXAFS for the Ru K-absorption edge) were performed on particles of two different diameters, 2 and 4 nm, and in different environments, polyol/acetate or thiol. For particles stored in polyol/acetate XPS studies revealed superficial oxidation limited to one monolayer and a surface coating containing mostly acetate ions. Analysis of the EXAFS spectra showed both oxygen and ruthenium atoms around the ruthenium atoms with a Ru-Ru coordination number N smaller than the bulk value, as expected for fine particles. In the case of 2 nm acetate-capped particles N is consistent with particles made up of a metallic core and an oxidized monolayer. For 2 nm thiol-coated particles, a Ru-S bond was evidenced by XPS and XAS. For the 4 nm particles XANES and XPS studies showed that most of the ruthenium atoms are in the zerovalent state. Nevertheless, in both cases, when capped with thiol, the Ru-Ru coordination number inferred from EXAFS is much smaller than for particles of the same size stored in polyol. This is attributed to a structural disorganization of the particles by thiol chemisorption. HRTEM studies confirm the marked dependence of the structural properties of the ruthenium particles on their chemical environment; they show the acetate-coated particles to be single crystals, whereas the thiol-coated particles appear to be polycrystalline.

New Generation Materials and Structures for Nanophotonics and Nanoelectronics

DTIC Science & Technology

2006-04-30

been investigated using thermogravimetric analysis and FTIR spectroscopy. The nanoparticles appear to have excess surfactants on their surface, but...processes. We continued analysis of the vibrational modes of the InP/II- VI core-shell nanoparticles determined by IR and Raman studies, and initiated...photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), BET surface area analysis , transmission electron microscopy (TEM), and SQUID magnetometry. In

Synthesis and gas sensing properties of α-Fe(2)O(3)@ZnO core-shell nanospindles.

PubMed

Zhang, Jun; Liu, Xianghong; Wang, Liwei; Yang, Taili; Guo, Xianzhi; Wu, Shihua; Wang, Shurong; Zhang, Shoumin

2011-05-06

α-Fe(2)O(3)@ZnO core-shell nanospindles were synthesized via a two-step hydrothermal approach, and characterized by means of SEM/TEM/XRD/XPS. The ZnO shell coated on the nanospindles has a thickness of 10-15 nm. Considering that both α-Fe(2)O(3) and ZnO are good sensing materials, we have investigated the gas sensing performances of the core-shell nanocomposite using ethanol as the main probe gas. It is interesting to find that the gas sensor properties of the core-shell nanospindles are significantly enhanced compared with pristine α-Fe(2)O(3). The enhanced sensor properties are attributed to the unique core-shell nanostructure. The detailed sensing mechanism is discussed with respect to the energy band structure and the electron depletion theory. The core-shell nanostructure reported in this work provides a new path to fabricate highly sensitive materials for gas sensing applications.

Multiplet Splitting Effects on Core-Level Photoemission and Inverse-Photoemission Spectra of Uranium Intermetallic Compounds

NASA Astrophysics Data System (ADS)

Okada, Kozo

1999-03-01

The present paper discusses the role of U 5f-5f exchange interaction (J) in the inverse photoemission spectrum (IPES) and the U 4f x-ray photoemission spectrum (XPS) of uranium intermetallic compounds. The origin of the broad main peak in the IPES of UPd3 and UPd2Al3, for instance, is ascribed to the exchange coupling effects of 5f electrons. In other words, whether the ground state is of high-spin or of low-spin is directly reflected in the width of the IPES. On the other hand, the interpretation for the U 4f photoemission spectrum is not so greatly influenced by J. The full-multiplet calculations are also performed for an U4+ ion for comparison.

Photoelectron spectroscopic studies of ultra-thin CuPc layers on a Si(111)-(√3 × √3)R30°-B surface

NASA Astrophysics Data System (ADS)

Menzli, S.; Laribi, A.; Mrezguia, H.; Arbi, I.; Akremi, A.; Chefi, C.; Chérioux, F.; Palmino, F.

2016-12-01

The adsorption of copper phthalocyanine (CuPc) molecules on Si(111)-(√3 × √3)R30°-B surface is investigated at room temperature under ultra-high vacuum. Crystallographic, chemical and electronic properties of the interface are investigated by low energy electron diffraction (LEED), ultraviolet and X-ray photoemission spectroscopies (UPS, XPS) and X-ray photoemission diffraction (XPD). LEED and XPD results shed light on the growth mechanism of CuPc on this substrate. At one monolayer coverage the growth mode was characterized by the formation of crystalline 3D nanoislands. The molecular packing deduced from this study appears very close to the one of the bulk CuPc α phase. The 3D islands are formed by molecules aligned in a standing manner. XPS core level spectra of the substrate reveal that there is no discernible chemical interaction between molecules and substrate. However there is charge transfer from molecules to the substrate. During the growth, the work function (WF) was found to decrease from 4.50 eV for the clean substrate to 3.70 eV for the highest coverage (30 monolayers). Within a thickness of two monolayers deposition, an interface dipole of 0.50 eV was found. A substrate band bending of 0.25 eV was deduced over all the range of exposure. UPS spectra indicate the existence of a band bending of the highest occupied molecular orbital (HOMO) of 0.30 eV. The changes in the work function, in the Fermi level position and in the onset of the molecular HOMO state have been used to determine the energy level alignment at the interface.

Novel highly ordered core–shell nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dey, Sonal; Hossain, Mohammad D.; Mayanovic, Robert A.

2016-10-26

Core–shell nanoparticles have potential for a wide range of applications due to the tunability of their magnetic, catalytic, electronic, optical, and other physicochemical properties. A frequent drawback in the design of core–shell nanoparticles and nanocrystals is the lack of control over an extensive, disordered, and compositionally distinct interface that occurs due to the dissimilarity of structural and compositional phases of the core and shell. In this work, we demonstrate a new hydrothermal nanophase epitaxy (HNE) technique to synthesize highly structurally ordered α-Cr 2O 3@α-Co 0.38Cr 1.62O 2.92 inverted core–shell nanoparticles (CSNs) with evidence for the nanoscale growth of corundum structuremore » beginning from the core and extending completely into the shell of the CSNs with minimal defects at the interface. The high-resolution TEM results show a sharp interface exhibiting epitaxial atomic registry of shell atoms over highly ordered core atoms. The XPS and Co K-edge XANES analyses indicate the +2 oxidation state of cobalt is incorporated in the shell of the CSNs. Our XPS and EXAFS results are consistent with oxygen vacancy formation in order to maintain charge neutrality upon substitution of the Co 2+ ion for the Cr 3+ ion in the α-Co 0.38Cr 1.62O 2.92 shell. Furthermore, the CSNs exhibit the magnetic exchange bias effect, which is attributed to the exchange anisotropy at the interface made possible by the nanophase epitaxial growth of the α-Co 0.38Cr 1.62O 2.92 shell on the α-Cr 2O 3 core of the nanoparticles. The combination of a well-structured, sharp interface and novel nanophase characteristics is highly desirable for nanostructures having enhanced magnetic properties.« less

Synergistic effect in carbon coated LiFePO4 for high yield spontaneous grafting of diazonium salt. Structural examination at the grain agglomerate scale.

PubMed

Madec, Lénaïc; Robert, Donatien; Moreau, Philippe; Bayle-Guillemaud, Pascale; Guyomard, Dominique; Gaubicher, Joël

2013-08-07

Molecular grafting of p-nitrobenzene diazonium salt at the surface of (Li)FePO4-based materials was thoroughly investigated. The grafting yields obtained by FTIR, XPS, and elemental analysis for core shell LiFePO4-C are found to be much higher than the sum of those associated with either the LiFePO4 core or the carbon shell alone, thereby revealing a synergistic effect. Electrochemical, XRD, and EELS experiments demonstrate that this effect stems from the strong participation of the LiFePO4 core that delivers large amounts of electrons to the carbon substrate at a constant energy, above the Fermi level of the diazonium salt. Correspondingly large multilayer anisotropic structures that are associated with outstanding grafting yields could be observed from TEM experiments. Results therefore constitute strong evidence of a grafting mechanism where homolytic cleavage of the N2(+) species occurs together with the formation and grafting of radical nitro-aryl intermediates. Although the oxidation and concomitant Li deintercalation of LiFePO4 grains constitute the main driving force of the functionalization reaction, EFTEM EELS mapping shows a striking lack of spatial correlation between grafted grains and oxidized ones.

Room-temperature ferromagnetic Cr-doped Ge/GeOx core-shell nanowires.

PubMed

Katkar, Amar S; Gupta, Shobhnath P; Seikh, Md Motin; Chen, Lih-Juann; Walke, Pravin S

2018-06-08

The Cr-doped tunable thickness core-shell Ge/GeO x nanowires (NWs) were synthesized and characterized using x-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy, energy-dispersive x-ray spectroscopy, x-ray photoelectron spectroscopy and magnetization studies. The shell thickness increases with the increase in synthesis temperature. The presence of metallic Cr and Cr 3+ in core-shell structure was confirmed from XPS study. The magnetic property is highly sensitive to the core-shell thickness and intriguing room temperature ferromagnetism is realized only in core-shell NWs. The magnetization decreases with an increase in shell thickness and practically ceases to exist when there is no core. These NWs show remarkably high Curie temperature (T C  > 300 K) with the dominating values of its magnetic remanence (M R ) and coercivity (H C ) compared to germanium dilute magnetic semiconductor nanomaterials. We believe that our finding on these Cr-doped Ge/GeO X core-shell NWs has the potential to be used as a hard magnet for future spintronic devices, owing to their higher characteristic values of ferromagnetic ordering.

Self-assembly and graft polymerization route to Monodispersed Fe3O4@SiO2--polyaniline core-shell composite nanoparticles: physical properties.

PubMed

Reddy, Kakarla Raghava; Lee, Kwang-Pill; Kim, Ju Young; Lee, Youngil

2008-11-01

This study describes the synthesis of monodispersed core-shell composites of silica-modified magnetic nanoparticles and conducting polyaniline by self-assembly and graft polymerization. Magnetic ferrite nanoparticles (Fe3O4) were prepared by coprecipitation of Fe+2 and Fe+3 ions in alkaline solution, and then silananized. The silanation of magnetic particles (Fe3O4@SiO2) was carried out using 3-bromopropyltrichlorosilane (BPTS) as the coupling agent. FT-IR spectra indicated the presence of Fe--O--Si chemical bonds in Fe3O4@SiO2. Core-shell type nanocomposites (Fe3O4@SiO2/PANI) were prepared by grafting polyaniline (PANI) on the surface of silanized magnetic particles through surface initiated in-situ chemical oxidative graft polymerization. The nanocomposites were characterized by high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectra (XPS), Fourier transform infrared (FTIR) spectra, UV-visible spectroscopy, photoluminescence (PL) spectra, electrical conductivity and magnetic characteristics. HRTEM images of the nanocomposites revealed that the silica-modified magnetic particles made up the core while PANI made up the shell. The XPS spectrum revealed the presence of silica in the composites, and the XRD results showed that the composites were more crystalline than pure PANI. PL spectra show that composites exhibit photoluminescent property. Conductivity of the composites (6.2 to 9.4 x 10(-2) S/cm) was higher than that of pristine PANI (3.7 x 10(-3) S/cm). The nanocomposites exhibited superparamagnetism. Formation mechanism of the core-shell structured nanocomposites and the effect of modified magnetic nanoparticles on the electro-magnetic properties of the Fe3O4@SiO2/PANI nanocomposites are also investigated. This method provides a new strategy for the generation of multi-functional nanocomposites that composed of other conducting polymers and metal nanoparticles.

Fermi Level shifting, Charge Transfer and Induced Magnetic Coupling at La0.7Ca0.3MnO3/LaNiO3 Interface

PubMed Central

Ning, Xingkun; Wang, Zhanjie; Zhang, Zhidong

2015-01-01

A large magnetic coupling has been observed at the La0.7Ca0.3MnO3/LaNiO3 (LCMO/LNO) interface. The x-ray photoelectron spectroscopy (XPS) study results show that Fermi level continuously shifted across the LCMO/LNO interface in the interface region. In addition, the charge transfer between Mn and Ni ions of the type Mn3+ − Ni3+ → Mn4+ − Ni2+ with the oxygen vacancies are observed in the interface region. The intrinsic interfacial charge transfer can give rise to itinerant electrons, which results in a “shoulder feature” observed at the low binding energy in the Mn 2p core level spectra. Meanwhile, the orbital reconstruction can be mapped according to the Fermi level position and the charge transfer mode. It can be considered that the ferromagnetic interaction between Ni2+ and Mn4+ gives rise to magnetic regions that pin the ferromagnetic LCMO and cause magnetic coupling at the LCMO/LNO interface. PMID:25676088

Mesoporous coaxial titanium nitride-vanadium nitride fibers of core-shell structures for high-performance supercapacitors.

PubMed

Zhou, Xinhong; Shang, Chaoqun; Gu, Lin; Dong, Shanmu; Chen, Xiao; Han, Pengxian; Li, Lanfeng; Yao, Jianhua; Liu, Zhihong; Xu, Hongxia; Zhu, Yuwei; Cui, Guanglei

2011-08-01

In this study, titanium nitride-vanadium nitride fibers of core-shell structures were prepared by the coaxial electrospinning, and subsequently annealed in the ammonia for supercapacitor applications. These core-shell (TiN-VN) fibers incorporated mesoporous structure into high electronic conducting transition nitride hybrids, which combined higher specific capacitance of VN and better rate capability of TiN. These hybrids exhibited higher specific capacitance (2 mV s(-1), 247.5 F g(-1)) and better rate capability (50 mV s(-1), 160.8 F g(-1)), which promise a good candidate for high-performance supercapacitors. It was also revealed by electrochemical impedance spectroscopy (EIS) and X-ray photoelectron spectroscopy (XPS) characterization that the minor capacitance fade originated from the surface oxidation of VN and TiN.

Effects of the carrier concentration on polarity determination in Ga-doped ZnO films by hard x-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Song, Huaping; Makino, Hisao; Kobata, Masaaki; Nomoto, Junichi; Kobayashi, Keisuke; Yamamoto, Tetsuya

2018-03-01

Core level (CL) and valence band (VB) spectra of heavily Ga-doped ZnO (GZO) films with carrier concentrations (Ne) ranging from 1.8 × 1020 to 1.0 × 1021 cm-3 were measured by high-resolution Al Kα (hν = 1486.6 eV) x-ray photoelectron spectroscopy (XPS) and Cr Kα (hν = 5414.7 eV) hard x-ray photoelectron spectroscopy (HAXPES). The CL spectra of the GZO films measured by XPS had little dependence on Ne. In contrast, clear differences in asymmetric broadening were observed in the HAXPES spectra owing to the large probing depth. The asymmetry in the Zn 2p3/2 and O 1s HAXPES spectra is mainly attributed to the energy loss of the conduction electron plasmon caused by the high Ne of the GZO films. Similar asymmetry was also observed in the VB spectra of these GZO films. It was found that such asymmetry plays a crucial role in the determination of crystal polarity. With increasing Ne, the intensity of the sub-peak at a binding energy Eb of about 5 eV in the VB spectrum decreased and the sub-peak became indistinguishable. We clarified the limitation of the criterion using the sub-peak and proposed an alternative method for polarity determination.

Single Silver Adatoms on Nanostructured Manganese Oxide Surfaces: Boosting Oxygen Activation for Benzene Abatement.

PubMed

Chen, Yaxin; Huang, Zhiwei; Zhou, Meijuan; Ma, Zhen; Chen, Jianmin; Tang, Xingfu

2017-02-21

The involvement of a great amount of active oxygen species is a crucial requirement for catalytic oxidation of benzene, because complete mineralization of one benzene molecule needs 15 oxygen atoms. Here, we disperse single silver adatoms on nanostructured hollandite manganese oxide (HMO) surfaces by using a thermal diffusion method. The single-atom silver catalyst (Ag 1 /HMO) shows high catalytic activity in benzene oxidation, and 100% conversion is achieved at 220 °C at a high space velocity of 23 000 h -1 . The Mars-van Krevelen mechanism is valid in our case as the reaction orders for both benzene and O 2 approach one, according to reaction kinetics data. Data from H 2 temperature-programmed reduction and O core-level X-ray photoelectron spectra (XPS) reveal that Ag 1 /HMO possesses a great amount of active surface lattice oxygen available for benzene oxidation. Valence-band XPS and density functional theoretical calculations demonstrate that the single Ag adatoms have the upshifted 4d orbitals, thus facilitating the activation of gaseous oxygen. Therefore, the excellent activation abilities of Ag 1 /HMO toward both surface lattice oxygen and gaseous oxygen account for its high catalytic activity in benzene oxidation. This work may assist with the rational design of efficient metal-oxide catalysts for the abatement of volatile organic compounds such as benzene.

Formation of graphitic carbon nitride and boron carbon nitride film on sapphire substrate

NASA Astrophysics Data System (ADS)

Kosaka, Maito; Urakami, Noriyuki; Hashimoto, Yoshio

2018-02-01

As a novel production method of boron carbon nitride (BCN) films, in this paper, we present the incorporation of B into graphitic carbon nitride (g-C3N4). First, we investigated the formation of g-C3N4 films via chemical vapor deposition (CVD) using melamine powder as the precursor. The formation of g-C3N4 films on a c-plane sapphire substrate was confirmed by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and Raman spectroscopy measurements. The deposition temperature of g-C3N4 films was found to be suitable between 550 and 600 °C since the degradation and desorption of hexagonal C-N bonds should be suppressed. As for BCN films, we prepared BCN films via two-zone extended CVD using ammonia borane as the B precursor. Several XPS signals from B, C, and N core levels were detected from B-incorporated g-C3N4 films. While the N composition was almost constant, the marked tendencies for increasing B composition and decreasing C composition were achieved with the increase in the B incorporation, indicating the incorporation of B atoms by the substitution for C atoms. Optical absorptions were shifted to the high-energy side by B incorporation, which indicates the successful formation of BCN films using melamine and ammonia borane powders as precursors.

The interaction of atomic oxygen with copper: An XPS, AES, XRD, optical transmission, and stylus profilometry study

NASA Technical Reports Server (NTRS)

Raikar, Ganesh N.; Gregory, John C.; Christl, Ligia C.; Peters, Palmer N.

1993-01-01

The University of Alabama in Huntsville (UAH) experiment A-0114 was designed to study the reaction of material surfaces with low earth orbits (LEO) atmospheric oxygen. The experiment contained 128 one-inch circular samples; metals, polymers, carbons, and semiconductors. Half of these samples were exposed on the front of the Long Duration Exposure Facility (LDEF) and remaining on the rear. Among metal samples, copper has shown some interesting new results. There were two forms of copper samples: a thin film sputter-coated on fused silica and a solid piece of OFHC copper. They were characterized by x-ray and Auger electron spectroscopies, x-ray diffraction, and high resolution profilometry. Cu 2p core level spectra were used to demonstrate the presence of Cu2O and CuO and to determine the oxidation states.

Room Temperature Ferromagnetic, Anisotropic, Germanium Rich FeGe(001) Alloys.

PubMed

Lungu, George A; Apostol, Nicoleta G; Stoflea, Laura E; Costescu, Ruxandra M; Popescu, Dana G; Teodorescu, Cristian M

2013-02-21

Ferromagnetic Fe x Ge 1- x with x = 2%-9% are obtained by Fe deposition onto Ge(001) at high temperatures (500 °C). Low energy electron diffraction (LEED) investigation evidenced the preservation of the (1 × 1) surface structure of Ge(001) with Fe deposition. X-ray photoelectron spectroscopy (XPS) at Ge 3d and Fe 2p core levels evidenced strong Fe diffusion into the Ge substrate and formation of Ge-rich compounds, from FeGe₃ to approximately FeGe₂, depending on the amount of Fe deposited. Room temperature magneto-optical Kerr effect (MOKE) evidenced ferromagnetic ordering at room temperature, with about 0.1 Bohr magnetons per Fe atom, and also a clear uniaxial magnetic anisotropy with the in-plane easy magnetization axis. This compound is a good candidate for promising applications in the field of semiconductor spintronics.

Pulse plating of Pt on n-GaAs ( 1 0 0 ) wafer surfaces: Synchrotron induced photoelectron spectroscopy and XPS of wet fabrication processes

NASA Astrophysics Data System (ADS)

Ensling, D.; Hunger, R.; Kraft, D.; Mayer, Th.; Jaegermann, W.; Rodriguez-Girones, M.; Ichizli, V.; Hartnagel, H. L.

2003-01-01

Preparation steps of Pt/n-GaAs Schottky contacts as applied in the fabrication process of varactor diode arrays for THz applications are analysed by photoelectron spectroscopy. Pulsed cathodic deposition of Pt onto GaAs (1 0 0) wafer surfaces from acidic solution has been studied by core level photoelectron spectroscopy using different excitation energies. A laboratory AlKα source as well as synchrotron radiation of hν=130 and 645 eV at BESSY was used. Chemical analyses and semiquantitative estimates of layer thickness are given for the natural oxide of an untreated wafer surface, a surface conditioning NH 3 etching step, and stepwise pulse plating of Pt. The structural arrangement of the detected species and interface potentials are considered.

Trace hydrogen sulfide gas sensor based on tungsten sulfide membrane-coated thin-core fiber modal interferometer

NASA Astrophysics Data System (ADS)

Deng, Dashen; Feng, Wenlin; Wei, Jianwei; Qin, Xiang; Chen, Rong

2017-11-01

A novel fiber-optic hydrogen sulfide sensor based on a thin-core Mach-Zehnder fiber modal interferometer (TMZFI) is demonstrated and fabricated. This in-line interferometer is composed of a short section of thin-core fiber sandwiched between two standard single mode fibers, and the fast response to hydrogen sulfide is achieved via the construction of tungsten sulfide film on the outside surface of the TMZFI using the dip-coating and calcination technique. The fabricated sensing nanofilm is characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS) spectrometer, Fourier transform infrared (FTIR) and spectroscopic analysis technology, etc. Experimental results showed that the WS2 sensing film has a hexagonal structure with a compact and porous morphology. The XPS and FTIR indicate that the existence of two elements (W and S) is demonstrated. With the increasing concentration of hydrogen sulfide, the interference spectra appear blue shift. In addition, a high sensitivity of 18.37 pm/ppm and a good linear relationship are obtained within a measurement range from 0 to 80 ppm. In addition, there is an excellent selectivity for H2S, which has also been proved by the surface adsorption energy results of tungsten sulfide with four gases (H2S, N2, O2 and CO2) by using the density functional theory calculations. This interferometer has the advantages of simple structure, high sensitivity and easy manufacture, and could be used in the safety monitoring field of hydrogen sulfide gas.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kaspar, Tiffany C.; Sushko, Peter V.; Bowden, Mark E.

Epitaxial thin films of Cr2-xTixO3 were deposited by oxygen-plasma-assisted molecular beam epitaxy (OPA-MBE) for 0.04 ≤ x ≤ 0.26. Ti speciation is verified by both x-ray photoelectron spectroscopy (XPS) and Ti K-edge x-ray absorption near-edge spectroscopy (XANES) to be Ti4+. Substitution of Ti for Cr in the corundum lattice is confirmed by modeling of the Ti K-edge extended x-ray absorption fine structure (EXAFS). Room temperature electrical transport measurements confirm the highly insulating nature of Ti-doped Cr2O3, despite the presence of aliovalent Ti4+. The resistivity of highly pure, undoped Cr2O3 was measured to be three orders of magnitude higher than formore » Ti-doped Cr2O3. Although the formation of Cr vacancies in Ti-doped Cr2O3 is found by density functional theory (DFT) calculations to be the energetically preferable defect compensation mechanism to maintain charge neutrality, an analysis of the XPS and EXAFS data reveal the presence of both Cr vacancies and oxygen interstitials at intermediate and high Ti concentrations, with a weak trend towards Cr vacancies as the Ti concentration increases. At low Ti concentrations, a strong dependence of the XPS Ti 2p core level peak width on concentration is observed. This dependence is attributed to the presence of widely spaced Ti dopants, which renders compensation of two or three Ti by a single oxygen interstitial or Cr vacancy, respectively, less probable. Instead, defect clusters of unknown type occur, although they may involve Cr vacancies. The defect compensation model developed here provides insight into previous, conflicting reports of n-type versus p-type conductivity in Ti-doped Cr2O3 at high temperature, and will inform future studies to exploit the wide variety of electronic and magnetic properties of corundum-structure oxides.« less

Giant crystal-electric-field effect and complex magnetic behavior in single-crystalline CeRh3Si2

NASA Astrophysics Data System (ADS)

Pikul, A. P.; Kaczorowski, D.; Gajek, Z.; Stȩpień-Damm, J.; Ślebarski, A.; Werwiński, M.; Szajek, A.

2010-05-01

Single-crystalline CeRh3Si2 was investigated by means of x-ray diffraction, magnetic susceptibility, magnetization, electrical resistivity, and specific-heat measurements carried out in wide temperature and magnetic field ranges. Moreover, the electronic structure of the compound was studied at room temperature by cerium core-level x-ray photoemission spectroscopy (XPS). The physical properties were analyzed in terms of crystalline electric field and compared with results of ab initio band-structure calculations performed within the density-functional theory approach. The compound was found to crystallize in the orthorhombic unit cell of the ErRh3Si2 type (space group Imma No.74, Pearson symbol: oI24 ) with the lattice parameters a=7.1330(14)Å , b=9.7340(19)Å , and c=5.6040(11)Å . Analysis of the magnetic and XPS data revealed the presence of well-localized magnetic moments of trivalent cerium ions. All the physical properties were found to be highly anisotropic over the whole temperature range studied and influenced by exceptionally strong crystalline electric field with the overall splitting of the 4f1 ground multiplet exceeding 5700 K. Antiferromagnetic order of the cerium magnetic moments at TN=4.70(1)K and their subsequent spin rearrangement at Tt=4.48(1)K manifest themselves as distinct anomalies in the temperature characteristic of all the physical properties investigated and exhibit complex evolution in an external magnetic field. A tentative magnetic B-T phase diagram, constructed for B parallel to the b axis being the easy magnetization direction, shows very complex magnetic behavior of CeRh3Si2 , similar to that recently reported for an isostructural compound CeIr3Si2 . The electronic band-structure calculations corroborated the antiferromagnetic ordering of the cerium magnetic moments and well-reproduced the experimental XPS valence-band spectrum.

X-ray photoemission spectroscopy investigation of CaTiO{sub 3}:Eu for luminescence property: effect of Eu{sup 3+} ion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Kaichen; Zhao, Baijun; Gao, Lu, E-mail: gaolu@jlu.edu.cn

2016-06-15

Graphical abstract: The influence on the photoluminescent performance due to the electronic structure change in Eu-doped CaTiO{sub 3} of the specific core-level and valence band spectrum via X-ray photoemission spectroscopy were characterized. - Highlights: • Single phase CaTiO{sub 3} and CaTiO{sub 3}: Eu crystals were prepared under mild hydrothermal method. • Crystal structure, doping level and the relations to their luminescent property were discussed. • Charge compensation mechanism was discussed via valance band spectrum by XPS. - Abstract: Charge compensation of on-site Eu 4f–5d transition that determines the luminescent performance was confirmed with valance band spectrum. Influence of photoelectrons frommore » CaTiO{sub 3}: Eu to the corresponding luminescent performance was discussed based on the crystal structure, doping level and the relations to their luminescent property. This paper is important to further optimize the luminescent performance for improving the efficiency and reducing the cost in light emitting diode industry.« less

Study of fission-product segregation in used CANDU fuel by X-ray photoelectron spectroscopy (XPS) II

NASA Astrophysics Data System (ADS)

Hocking, William H.; Duclos, A. Michael; Johnson, Lawrence H.

1994-03-01

A thorough investigation of the grain-boundary chemistry of used CANDU fuel from one intact element has been conducted by X-ray photoelectron spectroscopy (XPS). Selected findings from more extensive XPS measurements on other used CANDU fuels exposed to storage conditions are included for comparison. Cesium, rubidium, tellurium and barium have been commonly observed, often reaching high degrees of surface enrichment, although their relative abundances can vary widely with a complex dependence on the fuel irradiation history. Lower concentrations of cadmium, molybdenum, strontium and iodine have also been occasionally detected. Except for iodine, chemical-shift data are indicative of oxidized species, possibly uranates. Segregation at monolayer-level coverages has been demonstrated by sequential XPS analysis and argon-ion sputtering. Calculations based on an idealized thin-film model are consistent with the depth profiles. The interpretation of these results is discussed in the context of previous studies, especially on LWR fuels.

Photoluminescent silicon nanocrystal-based multifunctional carrier for pH-regulated drug delivery.

PubMed

Xu, Zhigang; Wang, Dongdong; Guan, Min; Liu, Xiaoyan; Yang, Yanjie; Wei, Dongfeng; Zhao, Chunyan; Zhang, Haixia

2012-07-25

A core-shell structured multifunctional carrier with nanocrystalline silicon (ncSi) as the core and a water-soluble block copolymer as the shell based on a poly(methacrylic acid) (PMAA) inner shell and polyethylene glycol (MPEG) outer shell (ncSi-MPM) was synthesized for drug delivery. The morphology, composition, and properties of the resulting ncSi-MPM were determined by comprehensive multianalytical characterization, including (1)H NMR spectroscopy, FTIR spectroscopy, XPS spectroscopy, TEM, DLS, and fluorescence spectroscopy analyses. The size of the resulting ncSi-MPM nanocarriers ranged from 40 to 110 nm under a simulated physiological environment. The loading efficiency of model drug doxorubicin (DOX) was approximately 6.1-7.4 wt % for ncSi-MPM and the drug release was pH controlled. Cytotoxicity studies demonstrated that DOX-loaded ncSi-MPM showed high anticancer activity against Hela cells. Hemolysis percentages (<2%) of ncSi-MPM were within the scope of safe values. Fluorescent imaging studies showed that the nanocarriers could be used as a tracker at the cellular level. Integration of the above functional components may result in ncSi-MPM becoming a promising multifunctional carrier for drug delivery and biomedical applications.

Surface studies of novel oxide-free biocompatible coatings on metals

NASA Astrophysics Data System (ADS)

GAO, FENG

The valence band and core-level X-ray Photoelectron Spectroscopy (XPS) was used to probe biocompatible films formed on the surface of metals. The key to the successful adhesion of these biocompatible films is shown to be the initial formation of a thin, oxide free, etidronate film on the metal. It was not found possible to prepare the biocompatible films directly on the metal surfaces. These films formed on metals may find application in medical implants. The biocompatible films were exposed to air, water and sodium chloride for corrosion studies. The thin hydroxyapatite and etidronate film on the metal show differential charging effects that caused a doubling of the peaks in some core level spectra. This shows the coating has some electric properties such as dielectric or piezoelectric characters. This coating may have application in the insulating materials of electronic circuits or dielectric/ piezoelectric layer in bio-sensors. Experiment and calculation method of X-ray Photoelectron Spectroscopy is one powerful technology in surface and interface analysis. The valence band spectra proved especially valuable in the identification of the surface chemistry of the films, and these spectra were interpreted by comparing the experimental spectra with spectra calculated using band structure calculations which showed good agreement with experiment. The calculated spectrum could also be used to compare with the difference of experiment spectra for the investigation of the interface layers.

Fabrication of Cu-Ag core-shell bimetallic superfine powders by eco-friendly reagents and structures characterization

NASA Astrophysics Data System (ADS)

Zhao, Jun; Zhang, Dongming; Zhao, Jie

2011-09-01

Superfine bimetallic Cu-Ag core-shell powders were synthesized by reduction of copper sulfate pentahydrate and silver nitrate with eco-friendly ascorbic acid as a reducing agent and cyclodextrins as a protective agent in an aqueous system. The influence of Ag/Cu ratio on coatings was investigated. Ag was homogeneously distributed on the surface of Cu particles at a mole ratio of Ag/Cu=1. FE-SEM showed an uniformity of Ag coatings on Cu particles. Antioxidation of Cu particles was improved by increasing Ag/Cu ratio. TEM-EDX and UV-vis spectra also revealed that Cu cores were covered by Ag nanoshells on the whole. The surface composition analysis by XPS indicated that only small parts of Cu atoms in the surface were oxidized. It was noted that the hindrance of cyclodextrins chemisorbed on particles plays an important role in forming high quality and good dispersity Cu-Ag (Cu@Ag) core-shell powders.

Effect of Zinc Incorporation on the Performance of Red Light Emitting InP Core Nanocrystals.

PubMed

Xi, Lifei; Cho, Deok-Yong; Besmehn, Astrid; Duchamp, Martial; Grützmacher, Detlev; Lam, Yeng Ming; Kardynał, Beata E

2016-09-06

This report presents a systematic study on the effect of zinc (Zn) carboxylate precursor on the structural and optical properties of red light emitting InP nanocrystals (NCs). NC cores were assessed using X-ray photoelectron spectroscopy (XPS), X-ray absorption spectroscopy (XAS), energy-dispersive X-ray spectroscopy (EDX), and high-resolution transmission electron microscopy (HRTEM). When moderate Zn:In ratios in the reaction pot were used, the incorporation of Zn in InP was insufficient to change the crystal structure or band gap of the NCs, but photoluminescence quantum yield (PLQY) increased dramatically compared with pure InP NCs. Zn was found to incorporate mostly in the phosphate layer on the NCs. PL, PLQY, and time-resolved PL (TRPL) show that Zn carboxylates added to the precursors during NC cores facilitate the synthesis of high-quality InP NCs by suppressing nonradiative and sub-band-gap recombination, and the effect is visible also after a ZnS shell is grown on the cores.

A preliminary view on adsorption of organics on ice at temperatures close to melting point

NASA Astrophysics Data System (ADS)

Kong, Xiangrui; Waldner, Astrid; Orlando, Fabrizio; Artiglia, Luca; Ammann, Markus; Bartels-Rausch, Thorsten

2016-04-01

Ice and snow play active roles in the water cycle, the energy budget of the Earth, and environmental chemistry in the atmosphere and cryosphere. The uptake of trace gases from the atmosphere may induce changes in the structure of the surface layer of ice crystals and has important consequences for atmospheric chemistry and the climate system. However, a molecular-level understanding of trace gas adsorption on ice is still missing, and also little is known about the impurity-induced ice-surface disorder in the context of environmental relevance. It is a general challenge to apply highly sensitive experimental approaches to ambient air conditions, e.g. studies of volatile surfaces, because of the strict requirements of vacuum experimental conditions. In this study, we employed synchrotron-based X-ray Photoelectron Spectroscopy (XPS) and partial electron yield Near Edge X-ray Absorption Fine Structure (NEXAFS) in a state-of-the-art Near-Ambient Pressure Photoelectron (NAPP) spectroscopy end station. The NAPP enables to utilize the surface sensitive experimental methods, XPS and NEXAFS with electron detection, on volatile surfaces, i.e. ice at temperatures approaching zero degree Celsius. XPS and NEXAFS provide unique information of hydrogen bonding network, surface concentration of organic adsorbates, depth profile of dopants in the ice, and acid-base dissociation on the surfaces. For instance, a few carboxylic acids, e.g. acetic acid and formic acid, have been recently studied by XPS and NEXAFS in NAPP. Amines are a group of nitrogen-containing basic organics with atmospheric relevance. Only few studies have been focused on amines, and atmospheric models rarely take account of them due to the limitation of knowledge. Several amines have been found to play active roles in the processes of aerosol formation, e.g. dimethylamine (DMA), trimethylamine (TMA) and 1-propanamine. In this study, we will focus on one of these three amines after pre-tests, and perform core-level spectroscopies to reveal the behaviour of adsorption and dissociation on ice. Additionally, pure ice and amine doped ice will be compared for their surface structure change at different temperatures, which will indicate the differences of surface disordering caused by different factors. For instance, we will have a chance to know better if impurities will cause local disordering, i.e. forming hydration shell, which challenges the traditional picture of a homogenous disordered doped ice surface. The findings of this study could not only improve our understanding of how acidic organics adsorb to ice, and of their chemical properties on ice, but also have potentials to know better the behaviour of pure ice at temperatures approaching to the melting point.

Electronic structure of layered ferroelectric high-k titanate Pr2Ti2O7

NASA Astrophysics Data System (ADS)

Atuchin, V. V.; Gavrilova, T. A.; Grivel, J.-C.; Kesler, V. G.; Troitskaia, I. B.

2012-11-01

The spectroscopic parameters and electronic structure of binary titanate Pr2Ti2O7 have been studied by IR-, Raman and X-ray photoelectron spectroscopy (XPS) for the powder sample prepared by solid state synthesis. The spectral features of valence band and all constituent element core levels have been considered. The Auger parameters of titanium and oxygen in Pr2Ti2O7 have been determined as αTi=872.8 and αO=1042.3 eV. Variations of cation-anion bond ionicity have been discussed using binding energy differences ΔTi=(BE O 1s-BE Ti 2p3/2)=71.6 eV and ΔPr=BE(Pr 3d5/2)-BE(O 1s)=403.8 eV as key parameters in comparison with those of other titanium- and praseodymium-bearing oxides.

Room Temperature Ferromagnetic, Anisotropic, Germanium Rich FeGe(001) Alloys

PubMed Central

Lungu, George A.; Apostol, Nicoleta G.; Stoflea, Laura E.; Costescu, Ruxandra M.; Popescu, Dana G.; Teodorescu, Cristian M.

2013-01-01

Ferromagnetic FexGe1−x with x = 2%–9% are obtained by Fe deposition onto Ge(001) at high temperatures (500 °C). Low energy electron diffraction (LEED) investigation evidenced the preservation of the (1 × 1) surface structure of Ge(001) with Fe deposition. X-ray photoelectron spectroscopy (XPS) at Ge 3d and Fe 2p core levels evidenced strong Fe diffusion into the Ge substrate and formation of Ge-rich compounds, from FeGe3 to approximately FeGe2, depending on the amount of Fe deposited. Room temperature magneto-optical Kerr effect (MOKE) evidenced ferromagnetic ordering at room temperature, with about 0.1 Bohr magnetons per Fe atom, and also a clear uniaxial magnetic anisotropy with the in-plane [110] easy magnetization axis. This compound is a good candidate for promising applications in the field of semiconductor spintronics. PMID:28809330

Low-cost and eco-friendly nebulizer spray coated CuInAlS2 counter electrode for dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Dhas, C. Ravi; Christy, A. Jennifer; Venkatesh, R.; Esther Santhoshi Monica, S.; Panda, Subhendu K.; Subramanian, B.; Ravichandran, K.; Sudhagar, P.; Raj, A. Moses Ezhil

2018-05-01

CuInAlS2 thin films for different substrate temperatures were deposited by a novel nebulizer spray technique. The polycrystalline CIAS thin film exhibited tetragonal structure with the preferential orientation of (1 1 2) plane. Nanoflakes were observed from the surface morphology of CIAS film. The peak position of core level spectra confirms the presence of CuInAlS2 from XPS analysis. The absorbance spectra and optical band gap were observed from the optical property. The activation energy, carrier concentration, hole mobility and resistivity were determined by linear four probe and Hall effect measurements. The CIAS film was used as a counter electrode (CE) in dye-sensitized solar cells (DSSCs) and is characterized by cyclic voltammetry, electrochemical impedance spectroscopy and Tafel measurements. DSSC fabricated with the CIAS CE achieved the photo conversion efficiency of about 2.55%.

Polydopamine and MnO2 core-shell composites for high-performance supercapacitors

NASA Astrophysics Data System (ADS)

Hou, Ding; Tao, Haisheng; Zhu, Xuezhen; Li, Maoguo

2017-10-01

Polydopamine and MnO2 core-shell composites (PDA@MnO2) for high-performance supercapacitors had been successfully synthesized by a facile and fast method. The morphology, crystalline phase and chemical composition of PDA@MnO2 composites are characterized using SEM, TEM, XRD, EDS and XPS. The performance of PDA@MnO2 composites are further investigated by cyclic voltammetry, galvanostatic charge-discharge and electrochemical impedance spectroscopy in 1 M Na2SO4 electrolyte. The PDA@MnO2 core-shell nanostructure composites exhibit a high capacitance of 193 F g-1 at the current density of 1A g-1 and retained over 81.2% of its initial capacitance after 2500 cycles of charge-discharge at 2 A g-1. The results manifest that the PDA@MnO2 composites can be potentially applied in supercapacitors.

Electronic, magnetic, transport, and thermal properties of single-crystalline UF e2A l10

NASA Astrophysics Data System (ADS)

Troć, R.; Samsel-Czekała, M.; Talik, E.; Wawryk, R.; Gajek, Z.; Pasturel, M.

2015-09-01

The valence and core-level x-ray photoemission spectra (XPS), performed on an UF e2A l10 single crystal, were measured using the Al Kα radiation. The results of valence XPS show practically two separate regions of spectral intensity, one just at the Fermi level (EF) and the other one being a wide content with its maximum at about 0.8 eV below EF. These give rise to two electronic configurations of the 5 f states in the studied aluminide, itinerant and localized ones, i.e., their dual character. In such a situation the corresponding valence spectra, calculated within the local density approximation (LDA), well explain the former configuration, being responsible for a metallic behavior of the studied compound. Moreover, this behavior is confirmed clearly also by our results of magnetotransport measurements. On the other hand, the obtained magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power data support very well the local character of the 5 f2 -electron configuration of the U4 + ion in UF e2A l10 having the orthorhombic and cage-type crystal structure. Based on that configuration, the magnetic and thermal characteristics of the compound were modeled by the effective crystal field (CF) potential in the intermediate coupling scheme using initial parameters obtained by the angular overlap model (AOM). The obtained final CF parameters yielded the CF level scheme, composed of only singlets, proper for orthorhombic symmetry. Such a set of singlets reproduces in a satisfactory way both the strongly anisotropic temperature variations of the magnetic susceptibility, measured along the three main crystallographic directions, as well as the Schottky anomaly, evaluated using specific heat results of isomorphic ThF e2A l10 as a phonon reference. Also, the strongly anisotropic behavior of the Seebeck coefficient and its low temperature maxima observed for the compound studied here have been explained roughly by the CF effect.

Applications of XPS in the characterization of Battery materials

DOE PAGES

Shutthanandan, Vaithiyalingam; Nandasiri, Manjula; Zheng, Jianming; ...

2018-05-26

In this study, technological development requires reliable power sources where energy storage devices are emerging as a critical component. Wide range of energy storage devices, Redox-flow batteries (RFB), Lithium ion based batteries (LIB), and Lithium-sulfur (LSB) batteries are being developed for various applications ranging from grid-scale level storage to mobile electronics. Material complexities associated with these energy storage devices with unique electrochemistry are formidable challenge which needs to be address for transformative progress in this field. X-ray photoelectron spectroscopy (XPS) - a powerful surface analysis tool - has been widely used to study these energy storage materials because of itsmore » ability to identify, quantify and image the chemical distribution of redox active species. However, accessing the deeply buried solid-electrolyte interfaces (which dictates the performance of energy storage devices) has been a challenge in XPS usage. Herein we report our recent efforts to utilize the XPS to gain deep insight about these interfaces under realistic conditions with varying electrochemistry involving RFB, LIB and LSB.« less

Applications of XPS in the characterization of Battery materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shutthanandan, Vaithiyalingam; Nandasiri, Manjula; Zheng, Jianming

In this study, technological development requires reliable power sources where energy storage devices are emerging as a critical component. Wide range of energy storage devices, Redox-flow batteries (RFB), Lithium ion based batteries (LIB), and Lithium-sulfur (LSB) batteries are being developed for various applications ranging from grid-scale level storage to mobile electronics. Material complexities associated with these energy storage devices with unique electrochemistry are formidable challenge which needs to be address for transformative progress in this field. X-ray photoelectron spectroscopy (XPS) - a powerful surface analysis tool - has been widely used to study these energy storage materials because of itsmore » ability to identify, quantify and image the chemical distribution of redox active species. However, accessing the deeply buried solid-electrolyte interfaces (which dictates the performance of energy storage devices) has been a challenge in XPS usage. Herein we report our recent efforts to utilize the XPS to gain deep insight about these interfaces under realistic conditions with varying electrochemistry involving RFB, LIB and LSB.« less

Multispectroscopic (FTIR, XPS, and TOFMS-TPD) Investigation of the Core-Shell Bonding in Sonochemically-Prepared Aluminum Nanoparticles Capped with Oleic Acid (Preprint)

DTIC Science & Technology

2010-04-01

dimethylethylamine and a titanium (IV) isopropoxide catalyst were added to the solution. The concentrations of the alane complex and titanium catalyst in...public release 3.0 METHODS, ASSUMPTIONS, AND PROCEDURES 3.1 Materials Alane N,N-dimethylethylamine in a 0.4 M toluene solution, titanium (IV... isopropoxide (98%), oleic acid (99%), dodecane (99% and anhydrous), and oleyl alcohol (99%) were all obtained from Aldrich and used as received

Multispectroscopic (FTIR, XPS, and TOFMS-TPD) Investigation of the Core-Shell Bonding in Sonochemically Prepared Aluminum Nanoparticles Capped with Oleic Acid (Postprint)

DTIC Science & Technology

2010-03-04

Alane N,N-dimethylethylamine in a 0.4 M toluene solution, titanium (IV) isopropoxide (98%), oleic acid (99%), dodecane (99% and anhydrous), and oleyl...inside a dry nitrogen glovebox, where alane N,N-dimethylethylamine and a titanium (IV) isopropoxide catalyst were added to the solution. The...concentrations of the alane complex and titanium catalyst in this solution were 50 and 0.55 mM, respectively. This solution was then transferred into a sonication

In-situ growth of HfO2 on clean 2H-MoS2 surface: Growth mode, interface reactions and energy band alignment

NASA Astrophysics Data System (ADS)

Chen, Chang Pang; Ong, Bin Leong; Ong, Sheau Wei; Ong, Weijie; Tan, Hui Ru; Chai, Jian Wei; Zhang, Zheng; Wang, Shi Jie; Pan, Ji Sheng; Harrison, Leslie John; Kang, Hway Chuan; Tok, Eng Soon

2017-10-01

Room temperature growth of HfO2 thin film on clean 2H-MoS2 via plasma-sputtering of Hf-metal target in an argon/oxygen environment was studied in-situ using x-ray photoelectron spectroscopy (XPS). The deposited film was observed to grow akin to a layer-by-layer growth mode. At the onset of growth, a mixture of sulfate- and sulfite-like species (SOx2- where x = 3, 4), and molybdenum trioxide (MoO3), are formed at the HfO2/MoS2 interface. An initial decrease in binding energies for both Mo 3d and S 2p core-levels of the MoS2 substrate by 0.4 eV was also observed. Their binding energies, however, did not change further with increasing HfO2 thickness. There was no observable change in the Hf4f core-level binding energy throughout the deposition process. With increasing HfO2 deposition, MoO3 becomes buried at the interface while SOx2- was observed to be present in the film. The shift of 0.4 eV for both Mo 3d and S 2p core-levels of the MoS2 substrate can be attributed to a charge transfer from the substrate to the MoO3/SOx2--like interface layer. Consequently, the Type I heterojunction valence band offset (conduction band offset) becomes 1.7 eV (2.9 eV) instead of 1.3 eV (3.3 eV) expected from considering the bulk HfO2 and MoS2 valence band offset (conduction band offset). The formation of these states and its influence on band offsets will need to be considered in their device applications.

Electronic structure evolution in doping of fullerene (C{sub 60}) by ultra-thin layer molybdenum trioxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Chenggong; Wang, Congcong; Kauppi, John

2015-08-28

Ultra-thin layer molybdenum oxide doping of fullerene has been investigated using ultraviolet photoemission spectroscopy (UPS) and X-ray photoemission spectroscopy (XPS). The highest occupied molecular orbital (HOMO) can be observed directly with UPS. It is observed that the Fermi level position in fullerene is modified by ultra-thin-layer molybdenum oxide doping, and the HOMO onset is shifted to less than 1.3 eV below the Fermi level. The XPS results indicate that charge transfer was observed from the C{sub 60} to MoO{sub x} and Mo{sup 6+} oxides is the basis as hole dopants.

Preparation and recognition of surface molecularly imprinted core-shell microbeads for protein in aqueous solutions

NASA Astrophysics Data System (ADS)

Lu, Yan; Yan, Chang-Ling; Gao, Shu-Yan

2009-04-01

In this paper, a surface molecular imprinting technique was reported for preparing core-shell microbeads of protein imprinting, and bovine hemoglobin or bovine serum albumin were used as model proteins for studying the imprinted core-shell microbeads. 3-Aminophenylboronic acid (APBA) was polymerized onto the surface of polystyrene microbead in the presence of the protein templates to create protein-imprinted core-shell microbeads. The various samples were characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and Brunauer-Emmett-Teller (BET) methods. The effect of pH on rebinding of the template hemoglobin, the specific binding and selective recognition were studied for the imprinted microbeads. The results show that the bovine hemoglobin-imprinted core-shell microbeads were successfully created. The shell was a sort of imprinted thin films with porous structure and larger surface areas. The imprinted microbeads have good selectivity for templates and high stability. Due to the recognition sites locating at or closing to the surface, these imprinted microbeads have good property of mass-transport. Unfortunately, the imprint technology was not successfully applied to imprinting bovine serum albumin (BSA).

Fluorescence properties of alloyed ZnSeS quantum dots overcoated with ZnTe and ZnTe/ZnS shells

NASA Astrophysics Data System (ADS)

Adegoke, Oluwasesan; Mashazi, Philani; Nyokong, Tebello; Forbes, Patricia B. C.

2016-04-01

Fluorescent alloyed ternary ZnSeS quantum dots (QDs) have been synthesized via the pyrolysis of organometallic precursors. The effects of passivation of ZnTe and ZnTe/ZnS shells on the optical properties of the ternary alloyed ZnSeS core have been studied. A ligand exchange reaction using L-cysteine as a capping ligand was used to obtain water-soluble nanocrystals. The nanocrystals were each characterized by UV/vis absorption and fluorescence spectroscopy, transmission electron microscopy, X-ray diffractometry (XRD) and X-ray photoelectron spectroscopy (XPS). The photoluminescence (PL) quantum yield (QY) of alloyed ZnSeS QDs was 14% and this value increased to 27% when ZnTe was overcoated around the surface but further coating with a ZnS shell decreased the PL QY slightly to 24%. This implies that ZnTe shell suppressed non-radiative recombination exciton states in the alloyed core while further layering with a ZnS shell offered no further improvement in suppressing the defect states. XPS analysis confirmed the presence of the first shell layering but showed a weakened intensity signal of S (2p) and Se (3d) for the ZnSeS/ZnTe/ZnS QDs. Our work demonstrates for the first time that shell passivation of alloyed Zn-based QDs can offer improved optical properties. We hope the optical information presented in this work will be useful in the selection of alloyed Zn-based QDs appropriate for the intended application.

Structural Studies of the Initial Stages of Fluoride Epitaxy on Silicon and GERMANIUM(111)

NASA Astrophysics Data System (ADS)

Denlinger, Jonathan David

The epitaxial growth of ionic insulators on semiconductor substrates is of interest due to fundamental issues of interface bonding and structure as well as to potential technological applications. The initial stages of Group IIa fluoride insulator growth on (111) Si and Ge substrates by molecular beam epitaxy are studied with the in situ combination of X-ray Photoelectron Spectroscopy (XPS) and Diffraction (XPD). While XPS probes the electronic structure, XPD reveals atomic structure. In addition, low energy electron diffraction (LEED) is used to probe surface order and a separate study using X-ray standing wave (XSW) fluorescence reveals interface cation bonding sites. Following the formation of a chemically-reacted interface layer in CaF_2 epitaxy on Si(111), the morphology of the subsequent bulk layers is found to be dependent on substrate temperature and incident flux rate. At temperatures >=600 ^circC a transition from three -dimensional island formation at low flux to laminar growth at higher flux is observed with bulk- and interface-resolved XPD. At lower substrate temperatures, laminar growth is observed at all fluxes, but with different bulk nucleation behavior due to changes in the stoichiometry of the interface layer. This new observation of kinetic effects on the initial nucleation in CaF_2 epitaxy has important ramifications for the formation of thicker heterostructures for scientific or device applications. XPS and XPD are also used to identify for the first time, surface core-level species of Ca and F, and a secondary interface-shifted F Auger component arising from a second-layer site directly above interface-layer Ca atoms. The effects of lattice mismatch (from -3% to 8%) are investigated with various growths of Ca_{rm x}Sr _{rm 1-x}F_2 on Si and Ge (111) substrates. Triangulation of (111) and (220) XSW indicates a predominance of 3-fold hollow Sr bonding sites coexisting with 4-fold top sites for monolayers of SrF_2 on Si. XSW and LEED reveal a lateral discommensuration of the overlayer for lattice mismatches of >5% relative to the substrate. XPD also reveals a transition from single - to mixed-domains of overlayer crystallographic orientation for mismatches >=3.5%.

Core-shell rhodium sulfide catalyst for hydrogen evolution reaction / hydrogen oxidation reaction in hydrogen-bromine reversible fuel cell

NASA Astrophysics Data System (ADS)

Li, Yuanchao; Nguyen, Trung Van

2018-04-01

Synthesis and characterization of high electrochemical active surface area (ECSA) core-shell RhxSy catalysts for hydrogen evolution oxidation (HER)/hydrogen oxidation reaction (HOR) in H2-Br2 fuel cell are discussed. Catalysts with RhxSy as shell and different percentages (5%, 10%, and 20%) of platinum on carbon as core materials are synthesized. Cyclic voltammetry is used to evaluate the Pt-equivalent mass specific ECSA and durability of these catalysts. Transmission electron microscopy (TEM), X-ray Photoelectron spectroscopy (XPS) and Energy-dispersive X-ray spectroscopy (EDX) techniques are utilized to characterize the bulk and surface compositions and to confirm the core-shell structure of the catalysts, respectively. Cycling test and polarization curve measurements in the H2-Br2 fuel cell are used to assess the catalyst stability and performance in a fuel cell. The results show that the catalysts with core-shell structure have higher mass specific ECSA (50 m2 gm-Rh-1) compared to a commercial catalyst (RhxSy/C catalyst from BASF, 6.9 m2 gm-Rh-1). It also shows better HOR/HER performance in the fuel cell. Compared to the platinum catalyst, the core-shell catalysts show more stable performance in the fuel cell cycling test.

High ink absorption performance of inkjet printing based on SiO2@Al13 core-shell composites

NASA Astrophysics Data System (ADS)

Chen, YiFan; Jiang, Bo; Liu, Li; Du, Yunzhe; Zhang, Tong; Zhao, LiWei; Huang, YuDong

2018-04-01

The increasing growth of the inkjet market makes the inkjet printing more necessary. A composite material based on core-shell structure has been developed and applied to prepare inkjet printing layer. In this contribution, the ink printing record layers based on SiO2@Al13 core-shell composite was elaborated. The prepared core-shell composite materials were characterized by X-ray photoelectron spectroscopy (XPS), zeta potential, X-ray diffraction (XRD), scanning electron microscopy (SEM). The results proved the presence of electrostatic adsorption between SiO2 molecules and Al13 molecules with the formation of the well-dispersed system. In addition, based on the adsorption and the liquid permeability analysis, SiO2@Al13 ink printing record layer achieved a relatively high ink uptake (2.5 gmm-1) and permeability (87%), respectively. The smoothness and glossiness of SiO2@Al13 record layers were higher than SiO2 record layers. The core-shell structure facilitated the dispersion of the silica, thereby improved its ink absorption performance and made the clear printed image. Thus, the proposed procedure based on SiO2@Al13 core-shell structure of dye particles could be applied as a promising strategy for inkjet printing.

Phosphorus doped graphene by inductively coupled plasma and triphenylphosphine treatments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shin, Dong-Wook, E-mail: shindong37@skku.edu; Kim, Tae Sung; Yoo, Ji-Beom, E-mail: jbyoo@skku.edu

Highlights: • Substitution doping is a promising method for opening the energy band gap of graphene. • Substitution doping with phosphorus in the graphene lattice has numerous advantage such as high band gap, low formation energy, and high net charge density compared to nitrogen. • V{sub dirac} of Inductively coupled plasma (ICP) and triphenylphosphine (TPP) treated graphene was −57 V, which provided clear evidence of n-type doping. • Substitutional doping of graphene with phosphorus is verified by the XPS spectra of P 2p core level and EELS mapping of phosphorus. • The chemical bonding between P and graphene is verymore » stable for a long time in air (2 months). - Abstract: Graphene is considered a host material for various applications in next-generation electronic devices. However, despite its excellent properties, one of the most important issues to be solved as an electronic material is the creation of an energy band gap. Substitution doping is a promising method for opening the energy band gap of graphene. Herein, we demonstrate the substitutional doping of graphene with phosphorus using inductively coupled plasma (ICP) and triphenylphosphine (TPP) treatments. The electrical transfer characteristics of the phosphorus doped graphene field effect transistor (GFET) have a V{sub dirac} of ∼ − 54 V. The chemical bonding between P and C was clearly observed in XPS spectra, and uniform distribution of phosphorus within graphene domains was confirmed by EELS mapping. The capability for substitutional doping of graphene with phosphorus can significantly promote the development of graphene based electronic devices.« less

Final-state effect on x-ray photoelectron spectrum of nominally d1 and n -doped d0 transition-metal oxides

NASA Astrophysics Data System (ADS)

Lin, Chungwei; Posadas, Agham; Hadamek, Tobias; Demkov, Alexander A.

2015-07-01

We investigate the x-ray photoelectron spectroscopy (XPS) of nominally d1 and n -doped d0 transition-metal oxides including NbO2,SrVO3, and LaTiO3 (nominally d1), as well as n -doped SrTiO3 (nominally d0). In the case of single phase d1 oxides, we find that the XPS spectra (specifically photoelectrons from Nb 3 d , V 2 p , Ti 2 p core levels) all display at least two, and sometimes three distinct components, which can be consistently identified as d0,d1, and d2 oxidation states (with decreasing order in binding energy). Electron doping increases the d2 component but decreases the d0 component, whereas hole doping reverses this trend; a single d1 peak is never observed, and the d0 peak is always present even in phase-pure samples. In the case of n -doped SrTiO3, the d1 component appears as a weak shoulder with respect to the main d0 peak. We argue that these multiple peaks should be understood as being due to the final-state effect and are intrinsic to the materials. Their presence does not necessarily imply the existence of spatially localized ions of different oxidation states nor of separate phases. A simple model is provided to illustrate this interpretation, and several experiments are discussed accordingly. The key parameter to determine the relative importance between the initial-state and final-state effects is also pointed out.

Combining Theory and Experiment for Multitechnique Characterization of Activated CO 2 on Transition Metal Carbide (001) Surfaces

DOE PAGES

Kunkel, Christian; Viñes, Francesc; Ramírez, Pedro J.; ...

2018-01-15

Early transition metal carbides (TMC; TM = Ti, Zr, Hf, V, Nb, Ta, Mo) with face-centered cubic crystallographic structure have emerged as promising materials for CO 2 capture and activation. Density functional theory (DFT) calculations using the Perdew–Burke–Ernzerhof exchange–correlation functional evidence charge transfer from the TMC surface to CO 2 on the two possible adsorption sites, namely, MMC and TopC, and the electronic structure and binding strength differences are discussed. Further, the suitability of multiple experimental techniques with respect to (1) adsorbed CO2 recognition and (2) MMC/TopC adsorption distinction is assessed from extensive DFT simulations. Results show that ultraviolet photoemissionmore » spectroscopies (UPS), work function changes, core level X-ray photoemission spectroscopy (XPS), and changes in linear optical properties could well allow for adsorbed CO2 detection. Only infrared (IR) spectra and scanning tunnelling microscopy (STM) seem to additionally allow for MMC/TopC adsorption site distinction. These findings are confirmed with experimental XPS measurements, demonstrating CO 2 binding on single crystal (001) surfaces of TiC, ZrC, and VC. The experiments also help resolving ambiguities for VC, where CO 2 activation was unexpected due to low adsorption energy, but could be related to kinetic trapping involving a desorption barrier. With a wealth of data reported and direct experimental evidence provided, this study aims to motivate further basic surface science experiments on an interesting case of CO 2 activating materials, allowing also for a benchmark of employed theoretical models.« less

An X-ray photoelectron spectroscopy study of BF3 adsorption on positively and negatively poled LiNbO3 (0001)

NASA Astrophysics Data System (ADS)

Herdiech, M. W.; Mönig, H.; Altman, E. I.

2014-08-01

Adsorption of the strong Lewis acid BF3 was investigated to probe the sensitivity of the Lewis basicity of surface oxygens on LiNbO3 (0001) to the ferroelectric polarization direction. Adsorption and desorption were characterized by using X-ray photoelectron spectroscopy (XPS) to monitor the intensity and binding energy of the F 1s core level as a function of BF3 exposure and temperature. The results indicate that both BF3 uptake and desorption are very similar on the positively and negatively poled surfaces. In particular, BF3 only weakly adsorbs with the majority of the adsorbed BF3 desorbing below 200 K. Despite the similarities in the uptake and desorption behavior, the binding energy of the F 1s peak relative to the substrate Nb 3d5/2 peak was sensitive to the polarization direction, with the F 1s peak occurring at a binding energy up to 0.3 eV lower on positively poled than negatively poled LiNbO3 for equivalent BF3 exposures. Rather than reflecting a difference in bonding to the surface, however, this shift could be associated with oppositely oriented dipoles at the positively and negatively poled surfaces creating opposite band offsets between the adsorbate and the substrate. A similar effect was observed with lead zirconate titanate thin films where the Pb 4f XPS peak position changes as a function of temperature as a result of the pyroelectric effect which changes the magnitude of the surface and interface dipoles.

Electronic structure, charge transfer, and intrinsic luminescence of gadolinium oxide nanoparticles: Experiment and theory

NASA Astrophysics Data System (ADS)

Zatsepin, D. A.; Boukhvalov, D. W.; Zatsepin, A. F.; Kuznetsova, Yu. A.; Mashkovtsev, M. A.; Rychkov, V. N.; Shur, V. Ya.; Esin, A. A.; Kurmaev, E. Z.

2018-04-01

The cubic (c) and monoclinic (m) polymorphs of Gd2O3 were studied using the combined analysis of several materials science techniques - X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and photoluminescence (PL) spectroscopy. Density functional theory (DFT) based calculations for the samples under study were performed as well. The cubic phase of gadolinium oxide (c-Gd2O3) synthesized using a precipitation method exhibits spheroidal-like nanoclusters with well-defined edges assembled from primary nanoparticles with an average size of 50 nm, whereas the monoclinic phase of gadolinium oxide (m-Gd2O3) deposited using explosive pyrolysis has a denser structure compared with natural gadolinia. This phase also has a structure composed of three-dimensional complex agglomerates without clear-edged boundaries that are ∼21 nm in size plus a cubic phase admixture of only 2 at.% composed of primary edge-boundary nanoparticles ∼15 nm in size. These atomic features appear in the electronic structure as different defects ([Gd…Osbnd OH] and [Gd…Osbnd O]) and have dissimilar contributions to the charge-transfer processes among the appropriate electronic states with ambiguous contributions in the Gd 5р - O 2s core-like levels in the valence band structures. The origin of [Gd…Osbnd OH] defects found by XPS was well-supported by PL analysis. The electronic and atomic structures of the synthesized gadolinias calculated using DFT were compared and discussed on the basis of the well-known joint OKT-van der Laan model, and good agreement was established.

Combining Theory and Experiment for Multitechnique Characterization of Activated CO 2 on Transition Metal Carbide (001) Surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kunkel, Christian; Viñes, Francesc; Ramírez, Pedro J.

Early transition metal carbides (TMC; TM = Ti, Zr, Hf, V, Nb, Ta, Mo) with face-centered cubic crystallographic structure have emerged as promising materials for CO 2 capture and activation. Density functional theory (DFT) calculations using the Perdew–Burke–Ernzerhof exchange–correlation functional evidence charge transfer from the TMC surface to CO 2 on the two possible adsorption sites, namely, MMC and TopC, and the electronic structure and binding strength differences are discussed. Further, the suitability of multiple experimental techniques with respect to (1) adsorbed CO2 recognition and (2) MMC/TopC adsorption distinction is assessed from extensive DFT simulations. Results show that ultraviolet photoemissionmore » spectroscopies (UPS), work function changes, core level X-ray photoemission spectroscopy (XPS), and changes in linear optical properties could well allow for adsorbed CO2 detection. Only infrared (IR) spectra and scanning tunnelling microscopy (STM) seem to additionally allow for MMC/TopC adsorption site distinction. These findings are confirmed with experimental XPS measurements, demonstrating CO 2 binding on single crystal (001) surfaces of TiC, ZrC, and VC. The experiments also help resolving ambiguities for VC, where CO 2 activation was unexpected due to low adsorption energy, but could be related to kinetic trapping involving a desorption barrier. With a wealth of data reported and direct experimental evidence provided, this study aims to motivate further basic surface science experiments on an interesting case of CO 2 activating materials, allowing also for a benchmark of employed theoretical models.« less

Improved Lubricating Performance by Combining Oil-Soluble Hairy Silica Nanoparticles and an Ionic Liquid as an Additive for a Synthetic Base Oil

DOE PAGES

Seymour, Bryan T.; Fu, Wenxin; Wright, Roger A. E.; ...

2018-04-05

This article reports on improved lubricating performance by combining oil-soluble poly(lauryl methacrylate) brush-grafted silica nanoparticles (hairy NPs or HNP) and an oil-miscible phosphonium-phosphate ionic liquid (IL) as a friction-reducing additive for a polyalphaolefin (PAO) oil. The HNP was synthesized by surface-initiated reversible addition–fragmentation chain transfer polymerization. At a total concentration of 2% and sufficiently high individual concentrations for HNP and IL in PAO, high-contact stress, ball-on-flat reciprocating tribological tests showed that the friction decreased by up to 23% compared with 2% HNP alone in PAO and by up to 35% compared to the PAO mixed with 2% IL. Scanning electronmore » microscopy, energy-dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy (XPS) analysis revealed that the tribofilm formed from the PAO containing 1% HNP + 1% IL was enriched with both Si and P, indicating that both hairy NPs and IL were involved in the tribochemical reactions. In addition, the O 1s and Si 2p peaks in the core-level XPS spectra exhibited significant shifts for the mixture of 1% HNP + 1% IL compared to those for 2% HNP, suggesting the possible formation of new covalent bonds. These results indicated that HNP and IL reacted with each other and also with the metal substrate during the rubbing process, which likely strengthened the tribofilm and its bonding with the substrate and thus further improved the lubrication.« less

Improved Lubricating Performance by Combining Oil-Soluble Hairy Silica Nanoparticles and an Ionic Liquid as an Additive for a Synthetic Base Oil

DOE Office of Scientific and Technical Information (OSTI.GOV)

Seymour, Bryan T.; Fu, Wenxin; Wright, Roger A. E.

This article reports on improved lubricating performance by combining oil-soluble poly(lauryl methacrylate) brush-grafted silica nanoparticles (hairy NPs or HNP) and an oil-miscible phosphonium-phosphate ionic liquid (IL) as a friction-reducing additive for a polyalphaolefin (PAO) oil. The HNP was synthesized by surface-initiated reversible addition–fragmentation chain transfer polymerization. At a total concentration of 2% and sufficiently high individual concentrations for HNP and IL in PAO, high-contact stress, ball-on-flat reciprocating tribological tests showed that the friction decreased by up to 23% compared with 2% HNP alone in PAO and by up to 35% compared to the PAO mixed with 2% IL. Scanning electronmore » microscopy, energy-dispersive X-ray spectroscopy, and X-ray photoelectron spectroscopy (XPS) analysis revealed that the tribofilm formed from the PAO containing 1% HNP + 1% IL was enriched with both Si and P, indicating that both hairy NPs and IL were involved in the tribochemical reactions. In addition, the O 1s and Si 2p peaks in the core-level XPS spectra exhibited significant shifts for the mixture of 1% HNP + 1% IL compared to those for 2% HNP, suggesting the possible formation of new covalent bonds. These results indicated that HNP and IL reacted with each other and also with the metal substrate during the rubbing process, which likely strengthened the tribofilm and its bonding with the substrate and thus further improved the lubrication.« less

Preparation of gallium nitride surfaces for atomic layer deposition of aluminum oxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kerr, A. J.; Department of Chemistry and Biochemistry, University of California, San Diego, La Jolla, California 92093; Chagarov, E.

2014-09-14

A combined wet and dry cleaning process for GaN(0001) has been investigated with XPS and DFT-MD modeling to determine the molecular-level mechanisms for cleaning and the subsequent nucleation of gate oxide atomic layer deposition (ALD). In situ XPS studies show that for the wet sulfur treatment on GaN(0001), sulfur desorbs at room temperature in vacuum prior to gate oxide deposition. Angle resolved depth profiling XPS post-ALD deposition shows that the a-Al{sub 2}O{sub 3} gate oxide bonds directly to the GaN substrate leaving both the gallium surface atoms and the oxide interfacial atoms with XPS chemical shifts consistent with bulk-like charge.more » These results are in agreement with DFT calculations that predict the oxide/GaN(0001) interface will have bulk-like charges and a low density of band gap states. This passivation is consistent with the oxide restoring the surface gallium atoms to tetrahedral bonding by eliminating the gallium empty dangling bonds on bulk terminated GaN(0001)« less

Location of Varying Hydrophobicity Zinc(II) Phthalocyanine-Type Photosensitizers in Methoxy Poly(ethylene oxide) and Poly(l-lactide) Block Copolymer Micelles Using 1H NMR and XPS Techniques.

PubMed

Lamch, Łukasz; Tylus, Włodzimierz; Jewgiński, Michał; Latajka, Rafał; Wilk, Kazimiera A

2016-12-15

Hydrophobic zinc(II) phthalocyanine-type derivatives, solubilized in polymeric micelles (PMs), provide a befitting group of so-called nanophotosensitizers, suitable for a variety of photodynamic therapy (PDT) protocols. The factors that influence the success of such products in PDT are the location of the active cargo in the PMs and the nanocarrier-enhanced ability to safely interact with biological systems and fulfill their therapeutic functions. Therefore, the aim of this work was to determine the solubilization loci of three phthalocyanines of varying hydrophobicity, i.e., zinc(II) phthalocyanine (ZnPc), along with its tetrasulfonic acid (ZnPc-sulfo 4 ) and perfluorinated (ZnPcF 16 ) derivatives, loaded in polymeric micelles of methoxy poly(ethylene oxide)-b-poly(l-lactide) (mPEG-b-PLLA), by means of 1 H nuclear magnetic resonance (NMR) and X-ray photoelectron spectroscopy (XPS) combined with ion sputtering. Furthermore, the microenvironment influence upon the chemical and physical status of the solubilized cargo in PMs, expressed by photobleaching and reactive oxygen species (ROS) generation comparing to the same properties of native cargoes in solution, was also evaluated and discussed in regards to the probing location data. The studied phthalocyanine-loaded PMs exhibited good physical stability, high drug-loading efficiency, and a size of less than ca. 150 nm with low polydispersity indices. The formation of polymeric micelles and the solubilization locus were investigated by 1 H NMR and XPS. ZnPc localized within the PM core, whereas both ZnPcF 16 and ZnPc-sulfo 4 - in the corona of PMs. We proved that the cargo locus is crucial for the photochemical properties of the studied phthalocyanines; the increase in photostability and ability to generate ROS in micellar solution compared to free photosensitizer was most significant for the photosensitizer in the PM core. Our results indicate the role of the cargo location in the PM microenvironment and demonstrate that such attempts are fundamental for improving the properties of photosensitizers and their assumed efficiency as nanophotosensitizers in PDT.

Fabrication of hierarchical core-shell polydopamine@MgAl-LDHs composites for the efficient enrichment of radionuclides

NASA Astrophysics Data System (ADS)

Zhu, Kairuo; Lu, Songhua; Gao, Yang; Zhang, Rui; Tan, Xiaoli; Chen, Changlun

2017-02-01

Novel hierarchical core/shell structured polydopamine@MgAl-layered double hydroxides (PDA@MgAl-LDHs) composites involving MgAl-layered double hydroxide shells and PDA cores were fabricated thought one-pot coprecipitation assembly and methodically characterized by X-ray diffraction, Fourier transformed infrared spectroscopy, scanning/transmission electron microscopy, selected area electron diffraction, elemental mapping, thermogravimetric analysis and X-ray photoelectron spectroscopy technologies. U(VI) and Eu(III) sorption experiments showed that the PDA@MgAl-LDHs exhibited higher sorption ability with a maximum sorption capacity of 142.86 and 76.02 mg/g at 298 K and pH 4.5, respectively. More importantly, according to XPS analyses, U(VI) and Eu(III) were sorbed on PDA@MgAl-LDHs via oxygen-containing functional groups, and the chemical affinity of U(VI) by oxygen-containing functional groups is higher than that of Eu(III). These observations show great expectations in the enrichment of radionuclides from aquatic environments by PDA@MgAl-LDHs.

Jingle-bell-shaped ferrite hollow sphere with a noble metal core: Simple synthesis and their magnetic and antibacterial properties

NASA Astrophysics Data System (ADS)

Li, Siheng; Wang, Enbo; Tian, Chungui; Mao, Baodong; Kang, Zhenhui; Li, Qiuyu; Sun, Guoying

2008-07-01

In this paper, a simple strategy is developed for rational fabrication of a class of jingle-bell-shaped hollow structured nanomaterials marked as Ag@ MFe 2O 4 ( M=Ni, Co, Mg, Zn), consisting of ferrite hollow shells and metal nanoparticle cores, using highly uniform colloidal Ag@C microspheres as template. The final composites were obtained by direct adsorption of metal cations Fe 3+ and M 2+ on the surface of the Ag@C spheres followed by calcination process to remove the middle carbon shell and transform the metal ions into pure phase ferrites. The as-prepared composites were characterized by X-ray photoelectron spectroscopy (XPS), energy-dispersive X-ray analysis (EDX), X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV-vis spectroscopy and SQUID magnetometer. The results showed that the composites possess the magnetic property of the ferrite shell and the optical together with antibacterial property of the Ag core.

Enhance the photoluminescence and radioluminescence of La2Zr2O7:Eu3+ core nanoparticles by coating with a thin Y2O3 shell

NASA Astrophysics Data System (ADS)

Pokhrel, Madhab; Burger, Arnold; Groza, Michael; Mao, Yuanbing

2017-06-01

We report the generation of La2Zr2O7:5%Eu3+@Y2O3 (LZO5E@YO) core@shell crystalline inorganic-inorganic heterogeneous nanoparticles (NPs). The Y2O3 (YO) shell coating process based on a chemical sol-gel method led to the growth of a thin YO shell on the ordered pyrochlore La2Zr2O7:5%Eu3+ (LZO5E) core NPs. Photoluminescence (PL) analyses demonstrated a blue shift of 15 nm on charge transfer (CT) excitation band of the core@shell NPs from that of the core NPs. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) along x-ray diffraction (XRD), Fourier-transform Infrared spectroscopy (FTIR) and x-ray photoelectron spectroscopy (XPS) studies confirmed the formation of the thin YO layer over the LZO5E core NPs. The PL intensity of the LZO5E@YO core@shell NPs was enhanced by three fold compared to that of the LZO5E core NPs, and higher quantum yield (QY) was observed for the former compared to the original NPs by more than 70%. Higher radioluminescence (RL) emission was also observed for the core@shell NPs compared to the core NPs. Our ability of obtaining near-perfect core@shell heterostructure with enhanced luminescence performance opens the door for the development of efficient La2Zr2O7:5%Eu3+@Y2O3 NPs for both optical and x-ray scintillation applications.

Structural and optical properties of ZnSe:Eu/ZnS quantum dots depending on interfacial residual europium

NASA Astrophysics Data System (ADS)

Park, Ji Young; Lee, Chan Gi; Seo, Han Wook; Jeong, Da-Woon; Kim, Min Young; Kim, Woo-Byoung; Kim, Bum Sung

2018-01-01

A multimodal emitter comprising of ZnSe:Eu/ZnS (core/shell) quantum dots (QDs) by adding a ZnS precursor in situ during synthesis. ZnSe/Eu2+/Eu3+/ZnS actives both core and core/shell. QDs prepared with the ZnS precursor displayed a luminescence intensity three times that of ZnSe QDs due to the passivation effect of the Shell. While the core QDs display the 450-550 nm emission of Eu2+ (4F65D1 → 4F7), the core/shell system showed no Eu2+ emission but only the sharp peaks in the red at 579, 592, 615, 651, and 700 nm due to the electronic transitions of 5D0 → 7Fn (n = 0-4) depending on leisurely decreased with increased reaction time. These results are in agreement with Eu 3d spectra of XPS analysis results. Microscopic analyses show that the core and core/shell QDs both have a zinc blende structure, and their respective sizes were about 3.19 and 3.44 nm. The lattice constant in the central portion of the core/shell QDs are around d111 = 3.13 Å, which is between the outside and inside ring patterns (d111 = 3.27 and 3.07 Å, respectively). This shows the effective over-capping of shell onto the core QDs. The core/shell structure may contain Eu2O3 bonding the over-coated ZnS surface on the Eu3+-doped ZnSe core.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yoshimoto, Shinya, E-mail: yosshi@issp.u-tokyo.ac.jp; Shiozawa, Yuichiro; Koitaya, Takanori

Electronic states and electrical conductivity of the native oxide Si(111) surface adsorbed with an electron donor tetrakis(dimethylamino)ethylene (TDAE) were investigated using ultraviolet photoelectron spectroscopy, X-ray photoelectron spectroscopy (XPS), and independently driven four-probe conductivity measurements. The formation of positively charged TDAE species is confirmed by the downward shift of the vacuum level by 1.45 eV, the absence of HOMO level in the valence band, and observation of the positively charged state in the N 1s XPS spectra. Si 2p XPS spectra and four-probe conductivity measurements revealed that TDAE adsorption induces an increase in downward band bending and a reduction in electrical resistancemore » of the surface, respectively. The sheet conductivity and the electron density of the surface are 1.1 μS/◻ and 4.6 × 10{sup 9} cm{sup −2}, respectively, after TDAE adsorption, and they are as high as 350% of the original surface. These results demonstrate that the electron density of the semiconductor surface is successfully controlled by the electron donor molecule TDAE.« less

Chemistry Characterization of Jet Aircraft Engine Particulate by XPS: Results from APEX III

NASA Technical Reports Server (NTRS)

Vander Wal, Randy L.; Bryg, Victoria M.

2014-01-01

This paper reports XPS analysis of jet exhaust particulate from a B737, Lear, ERJ, and A300 aircraft during the APEX III NASA led field campaign. Carbon hybridization and bonding chemistry are identified by high-resolution scans about the C1s core-shell region. Significant organic content as gauged by the sp3/sp2 ratio is found across engines and platforms. Polar oxygen functional groups include carboxylic, carbonyl and phenol with combined content of 20 percent or more. By lower resolution survey scans various elements including transition metals are identified along with lighter elements such as S, N, and O in the form of oxides. Burning additives within lubricants are probable sources of Na, Ba, Ca, Zn, P and possibly Sn. Elements present and their percentages varied significantly across all engines, not revealing any trend or identifiable cause for the differences, though the origin is likely the same for the same element when observed. This finding suggests that their presence can be used as a tracer for identifying soots from aircraft engines as well as diagnostic for monitoring engine performance and wear.

A new method of nanocrystalline nickel powder formation by magnetron sputtering on the water-soluble substrates

NASA Astrophysics Data System (ADS)

Tučkutė, S.; Urbonavičius, M.; Lelis, M.; Maiorov, M.; Díaz Ordaz, J. R.; Milčius, D.

2018-01-01

Due to the accurate and relatively easy control magnetron sputtering is an attractive technique for the synthesis of metallic particles. This work describes a new method of nickel powder production by depositing nickel on the surface of sodium chloride particles which were used as the template and are soluble in water. Ni powder with flake-like structure was obtained after washing Ni coated salt particles in ultrasonic cleaner. Salt particles and nickel powder were characterized using scanning electron microscope (SEM), energy-dispersive x-ray spectrometer, XRD and X-ray photoelectron spectroscopy (XPS) techniques. SEM images showed that thickness of the received Ni particles varied in the nanoscale and depended on the magnetron deposition time but did not depend on the size of salt particles. On the other hand initial size of the salt particles was successfully employed a measure to control lateral dimensions of Ni powder. XRD and XPS analysis results revealed that Ni particles had metallic core and oxidized shell which was a cause of the slightly deteriorated magnetic properties.

Tunable anomalous hall effect induced by interfacial catalyst in perpendicular multilayers

NASA Astrophysics Data System (ADS)

Zhang, J. Y.; Peng, W. L.; Sun, Q. Y.; Liu, Y. W.; Dong, B. W.; Zheng, X. Q.; Yu, G. H.; Wang, C.; Zhao, Y. C.; Wang, S. G.

2018-04-01

The interfacial structures, playing a critical role on the transport properties and the perpendicular magnetic anisotropy in thin films and multilayers, can be modified by inserting an ultrathin functional layer at the various interfaces. The anomalous Hall effect (AHE) in the multilayers with core structure of Ta/CoFeB/X/MgO/Ta (X: Hf or Pt) is tuned by interfacial catalytic engineering. The saturation anomalous Hall resistance (RAH) is increased by 16.5% with 0.1 nm Hf insertion compared with the reference sample without insertion. However, the RAH value is decreased by 9.0% with 0.1 nm Pt insertion. The interfacial states were characterized by the X-ray photoelectron spectroscopy (XPS). The XPS results indicate that a strong bonding between Hf and O for Hf insertion, but no bonding between Pt and O for Pt insertion. The bonding between metal and oxygen leads to various oxygen migration behavior at the interfaces. Therefore, the opposite behavior about the RAH originates from the different oxygen behavior due to various interfacial insertion. This work provides a new approach to manipulate spin transport property for the potential applications.

Characterization of tetraethylene glycol passivated iron nanoparticles

NASA Astrophysics Data System (ADS)

Nunes, Eloiza da Silva; Viali, Wesley Renato; da Silva, Sebastião William; Coaquira, José Antonio Huamaní; Garg, Vijayendra Kumar; de Oliveira, Aderbal Carlos; Morais, Paulo César; Jafelicci Júnior, Miguel

2014-10-01

The present study describes the synthesis and characterization of iron@iron oxide nanoparticles produced by passivation of metallic iron in tetraethylene glycol media. Structural and chemical characterizations were performed using transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Mössbauer spectroscopy. Pomegranate-like core@shell nanoparticulate material in the size range of 90-120 nm was obtained. According to quantitative phase analysis using Rietveld structure refinement the synthesized iron oxide was identified as magnetite (Fe3O4) whereas the iron to magnetite mass fractions was found to be 47:53. These findings are in good agreement with the data obtained from Mössbauer and thermal gravimetric analysis (TGA). The XPS data revealed the presence of a surface organic layer with higher hydrocarbon content, possibly due to the tetraethylene glycol thermal degradation correlated with iron oxidation. The room-temperature (300 K) saturation magnetization measured for the as-synthesized iron and for the iron-iron oxide were 145 emu g-1 and 131 emu g-1, respectively. The measured saturation magnetizations are in good agreement with data obtained from TEM, XRD and Mössbauer spectroscopy.

Study of the electronic structure of electron accepting cyano-films: TCNQversusTCNE.

PubMed

Capitán, Maria J; Álvarez, Jesús; Navio, Cristina

2018-04-18

In this article, we perform systematic research on the electronic structure of two closely related organic electron acceptor molecules (TCNQ and TCNE), which are of technological interest due to their outstanding electronic properties. These studies have been performed from the experimental point of view by the use electron spectroscopies (XPS and UPS) and supported theoretically by the use of ab-initio DFT calculations. The cross-check between both molecules allows us to identify the characteristic electronic features of each part of the molecules and their contribution to the final electronic structure. We can describe the nature of the band gap of these materials, and we relate this with the appearance of the shake-up features in the core level spectra. A band bending and energy gap reduction of the aforementioned electronic structure in contact with a metal surface are seen in the experimental results as well in the theoretical calculations. This behavior implies that the TCNQ thin film accepts electrons from the metal substrate becoming a Schottky n-junction.

Initial stages of Lutetium growth on Si (111)-7 × 7 probed by STM and core-level photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Smykalla, Lars; Shukrynau, Pavel; Hietschold, Michael

2017-09-01

The interaction of small amounts of Lutetium with the Si (111)-7 × 7 reconstructed surface was investigated in detail using a combination of Scanning Tunneling Microscopy (STM) and Photoelectron Spectroscopy (XPS and UPS). Various immobile and also fastly moving atoms and nanocluster were found in the initial growth of the Lu/Si interface. Density functional theory calculations and photoelectron spectroscopy results suggest that the most attractive adsorption sites for the Lu atoms are basins around Si rest-atoms and there is no strong interaction between Lu and Si at the initial steps of film growth. However Lu nanocluster could also be found on other adsorption sites which results in a different voltage dependence in STM. Coverage-dependent STM images reveal the growth of a closed Lu metal overlayer by joining of the clusters. The existence of a stoichiometric Lu silicide compound was not detected on the surface in the initial growth for deposition at room temperature.

Interface electronic structure and morphology of 2,7-dioctyl[1]benzothieno[3,2-b]benzothiophene (C8-BTBT) on Au film

NASA Astrophysics Data System (ADS)

Wang, Shitan; Niu, Dongmei; Lyu, Lu; Huang, Yingbao; Wei, Xuhui; Wang, Can; Xie, Haipeng; Gao, Yongli

2017-09-01

The interfacial electronic structure and morphology of 2,7-dioctyl[1]benzothieno[3,2-b]benzothiophene(C8-BTBT) on polycrystalline Au film was investigated with photoemission spectroscopy (PES), atomic force microscopy (AFM) and grazing incidence X-ray diffraction (GIXRD). The transport barriers of holes and electrons at the interface are 1.72 eV and 2.12 eV, respectively, from the UPS measurement. There is no chemical reaction of C8-BTBT with Au from the XPS investigation of core levels Au 4f, C 1s and S 2p. The upmost molecules adopt a standing up configuration deduced from the diffraction peaks in GIXRD and the step height in AFM. Increasing order of the upright orientation of C8-BTBT molecules with film growth result in decreasing work function of the C8-BTBT thin film by forming an outward pointing dipole layer with the ordered end Csbnd H bonds.

Energy level alignment at the methylammonium lead iodide/copper phthalocyanine interface

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Shi; Goh, Teck Wee; Sum, Tze Chien, E-mail: Alfred@ntu.edu.sg, E-mail: Tzechien@ntu.edu.sg

2014-08-01

The energy level alignment at the CH{sub 3}NH{sub 3}PbI{sub 3}/copper phthalocyanine (CuPc) interface is investigated by X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS). XPS reveal a 0.3 eV downward band bending in the CuPc film. UPS validate this finding and further reveal negligible interfacial dipole formation – verifying the viability of vacuum level alignment. The highest occupied molecular orbital of CuPc is found to be closer to the Fermi level than the valance band maximum of CH{sub 3}NH{sub 3}PbI{sub 3}, facilitating hole transfer from CH{sub 3}NH{sub 3}PbI{sub 3} to CuPc. However, subsequent hole extraction from CuPc may bemore » impeded by the downward band bending in the CuPc layer.« less

Bioconjugated iron oxide nanocubes: synthesis, functionalization, and vectorization.

PubMed

Wortmann, Laura; Ilyas, Shaista; Niznansky, Daniel; Valldor, Martin; Arroub, Karim; Berger, Nadja; Rahme, Kamil; Holmes, Justin; Mathur, Sanjay

2014-10-08

A facile bottom-up approach for the synthesis of inorganic/organic bioconjugated nanoprobes based on iron oxide nanocubes as the core with a nanometric silica shell is demonstrated. Surface coating and functionalization protocols developed in this work offered good control over the shell thickness (8-40 nm) and enabled biovectorization of SiO2@Fe3O4 core-shell structures by covalent attachment of folic acid (FA) as a targeting unit for cellular uptake. The successful immobilization of folic acid was investigated both quantitatively (TGA, EA, XPS) and qualitatively (AT-IR, UV-vis, ζ-potential). Additionally, the magnetic behavior of the nanocomposites was monitored after each functionalization step. Cell viability studies confirmed low cytotoxicity of FA@SiO2@Fe3O4 conjugates, which makes them promising nanoprobes for targeted internalization by cells and their imaging.

In situ fabrication of ZnO@N-doped nanoporous carbon core-shell heterostructures with high photocatalytic and adsorption capacity by a calcination of ZnO@MOF strategy

NASA Astrophysics Data System (ADS)

Qi, Qi; Liu, Sujuan; Li, Xing; Kong, Chunlong; Guo, Zhiyong; Chen, Liang

2017-11-01

This report describes the controllable encapsulation of ZnO nanoparticles with N-doped nanoporous carbon (N-NpC) via a simple fabrication and calcination of ZnO@ZIF-8 (zeolitic imidazolate framework). In the fabrication of ZnO@ZIF-8, ZnO was used both as the support and Zn source for the formation of ZIF-8. After calcination under N2 atmosphere, the ZnO@N-NpC core-shell heterostructures were formed and characterized by IR, UV-vis, XRD, XPS, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). As expected, the well-defined ZnO@N-NpC core-shell nanospheres demonstrated distinct photocatalytic activity and adsorption capacity in response to the dye methylene blue (MB) in aqueous solution, and the degradation efficiency of MB is up to 99% under UV irradiation for 20 min after catalysts were reused for 5 cycles and stored for two months. Therefore, it is reasonable to believe that the ZnO@N-NpC core-shell heterostructures are new-type nanomaterials for photodegradation of the organic pollutants from wastewater.

Identification of a BrOOO- intermediate species in the ozonolysis of bromide at the liquid/vapor interface from liquid jet XPS

NASA Astrophysics Data System (ADS)

Chen, Shuzhen; Artiglia, Luca; Orlando, Fabrizio; Corral-Arroyo, Pablo; Edebeli, Jacinta; Ammann, Markus

2017-04-01

Oxidation of bromide by gas phase ozone (O3) in the absence of photochemistry is believed to be one of the important dark reactions to produce HOBr as the starting point of the multiphase cycling reaction mechanisms that release bromide out of sea water, sea spray or marine aerosols from aqueous solution that later drive O3 depleting chemistry in the troposphere [1]. The reaction of bromide with O3 occurs through an acid catalyzed mechanism involving a BrOOO- complex as an intermediate [2]. Slow oxidation of bromide by O3 in the bulk aqueous phase is of limited relevance; previous kinetic experiments have suspected the reaction to be enhanced at the surface of aqueous solutions. Thus, identifying BrOOO- at the interface would be a major step to understanding the multiphase oxidation of bromide with O3. Here, we provide a direct experimental evidence for the formation of a BrOOO- reaction intermediate at the surface by investigating the reaction of aqueous solutions NaBr with gas phase O3 after millisecond time scale exposure using the surface sensitive in situ liquid jet X-ray photoelectron spectroscopy (XPS) at the Swiss Light Source (SLS). We acquired Br 3d core level spectra of 0.125 M NaBr solution in presence and absence of ozone in the gas phase. We found a new feature with a peak position shifted towards higher binding energy (by ˜0.7 eV) compared to Br-, which was clearly different from the Br 3d core levels spectra of hypobromite and bromate measured with reference solutions. Our results suggest the appearance of the formation of the BrOOO- reaction intermediate as a new component, in agreement with theoretical calculations of the Br- ozonolysis mechanism [3]. Additionally, by varying the photoelectron kinetic energy and thus probe depth via variation of the probing photon energy, the new feature appears to be present near the liquid/vapor interface. Besides, kinetic experiments for the reaction of O3 with bromide are ongoing to investigate the dependence on the temperature, ozone concentration, which may give further information such as the relative oxidation rate at the liquid/vapor interface versus that in the bulk phase. [1] S. Wang, et al., Proceedings of the National Academy of Sciences, 2015, 112, 9281-9286. [2] Q. Liu, et al., Inorganic Chemistry, 2001, 40, 4436-4442. [3] I. Gladich, et al., The Journal of Physical Chemistry A, 2015, 119, 4482-4488.

Facile synthesis of mercaptosuccinic acid-capped CdTe/CdS/ZnS core/double shell quantum dots with improved cell viability on different cancer cells and normal cells

NASA Astrophysics Data System (ADS)

Parani, Sundararajan; Bupesh, Giridharan; Manikandan, Elayaperumal; Pandian, Kannaiyan; Oluwafemi, Oluwatobi Samuel

2016-11-01

Water-soluble, mercaptosuccinic acid (MSA)-capped CdTe/CdS/ZnS core/double shell quantum dots (QDs) were prepared by successive growth of CdS and ZnS shells on the as-synthesized CdTe/CdSthin core/shell quantum dots. The formation of core/double shell structured QDs was investigated by ultraviolet-visible (UV-Vis) absorption and photoluminescence (PL) spectroscopy, PL decay studies, X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). The core/double shell QDs exhibited good photoluminescence quantum yield (PLQY) which is 70% higher than that of the parent core/shell QDs, and they are stable for months. The average particle size of the core/double shell QDs was ˜3 nm as calculated from the transmission electron microscope (TEM) images. The cytotoxicity of the QDs was evaluated on a variety of cancer cells such as HeLa, MCF-7, A549, and normal Vero cells by 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (MTT) cell viability assay. The results showed that core/double shell QDs were less toxic to the cells when compared to the parent core/shell QDs. MCF-7 cells showed proliferation on incubation with QDs, and this is attributed to the metalloestrogenic activity of cadmium ions released from QDs. The core/double shell CdTe/CdS/ZnS (CSS) QDs were conjugated with transferrin and successfully employed for the biolabeling and fluorescent imaging of HeLa cells. These core/double shell QDs are highly promising fluorescent probe for cancer cell labeling and imaging applications.

Band alignment of atomic layer deposited MgO/Zn0.8Al0.2O heterointerface determined by charge corrected X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Yan, Baojun; Liu, Shulin; Yang, Yuzhen; Heng, Yuekun

2016-05-01

Pure magnesium (MgO) and zinc oxide doped with aluminum oxide (Zn0.8Al0.2O) were prepared via atomic layer deposition. We have studied the structure and band gap of bulk Zn0.8Al0.2O material by X-ray diffractometer (XRD) and Tauc method, and the band offsets and alignment of atomic layer deposited MgO/Zn0.8Al0.2O heterointerface were investigated systematically using X-ray photoelectron spectroscopy (XPS) in this study. Different methodologies, such as neutralizing electron gun, the use of C 1s peak recalibration and zero charging method, were applied to recover the actual position of the core levels in insulator materials which were easily influenced by differential charging phenomena. Schematic band alignment diagram, valence band offset (ΔEV) and conduction band offset (ΔEC) for the interface of the MgO/Zn0.8Al0.2O heterostructure have been constructed. An accurate value of ΔEV = 0.72 ± 0.11 eV was obtained from various combinations of core levels of heterojunction with varied MgO thickness. Given the experimental band gaps of 7.83 eV for MgO and 5.29 eV for Zn0.8Al0.2O, a type-II heterojunction with a ΔEC of 3.26 ± 0.11 eV was found. Band offsets and alignment studies of these heterojunctions are important for gaining deep consideration to the design of various optoelectronic devices based on such heterointerface.

Effects of hydrogen treatment on ohmic contacts to p-type GaN films

NASA Astrophysics Data System (ADS)

Huang, Bohr-Ran; Chou, Chia-Hui; Ke, Wen-Cheng; Chou, Yi-Lun; Tsai, Chia-Lung; Wu, Meng-chyi

2011-06-01

This study investigated the effects of hydrogen (H 2) treatment on metal contacts to Mg-doped p-GaN films by Hall-effect measurement, current-voltage ( I- V) analyzer and X-ray photoemission spectra (XPS). The interfacial oxide layer on the p-GaN surface was found to be the main reason for causing the nonlinear I- V behavior of the untreated p-GaN films. The increased nitrogen vacancy (V N) density due to increased GaN decomposition rate at high-temperature hydrogen treatment is believed to form high density surface states on the surface of p-GaN films. Compared to untreated p-GaN films, the surface Fermi level determined by the Ga 2p core-level peak on 1000 °C H 2-treated p-GaN films lies about ˜2.1 eV closer to the conduction band edge (i.e., the surface inverted to n-type behavior). The reduction in barrier height due to the high surface state density pinned the surface Fermi level close to the conduction band edge, and allowed the electrons to easily flow over the barrier from the metal into the p-GaN films. Thus, a good ohmic contact was achieved on the p-GaN films by the surface inversion method.

Ultrafast Carrier dynamics of InxGa1-xN nanostructures grown directly on Si(111)

NASA Astrophysics Data System (ADS)

Kumar, Praveen; Devi, Pooja; Rodriguez⁠, P. E. D. S.; Kumar, Manish; Shivling, V. D.; Noetzel, Richard; Sharma, Chhavi; Sinha, R. K.; Kumar, Mahesh

2018-05-01

We show a flux dependence changes in structural, optical and electronic properties of InxGa1-xN nanostructures (NSs) namely nanocolumns (NCs), nanoflakes (NFs) and nanowall network (NWN) grown directly on Si(111) surface. Field emission scanning electron microscopy (FESEM) images were recorded to see morphological changes from NFs to NCs and NWNc etc, while high-resolution X-ray diffraction (HRXRD) ω-2θ scans were used to determine In incorporation. The maximum In incorporation was observed to be 20, 33 and 38% for the sharp transition from NFs to NCs and NWNs, respectively. The charge carrier dynamics of these grown NSs were probed using Ultrafast Femtosecond Transient Absorption Spectroscopy (UFTAS) with excitation at 350 nm pump wavelength. The UFTAS studies show the comparative charge carriers dynamics of the NWS, NCs and NFs. The charge carrier studies show a higher lifetime in NWNs as compare to NCs and NFs. Further, to examine electronic structure and level of degeneracy of these NSs, core-level and valence band spectra were analyzed by X-ray photoelectron spectroscopy (XPS), which manifest the upward band bending ranging from 0.2 eV to 0.4 eV.

Enhanced room temperature ferromagnetism in Ni doped SnO2 nanoparticles: A comprehensive study

NASA Astrophysics Data System (ADS)

Ahmed, Ateeq; Ali, T.; Naseem Siddique, M.; Ahmad, Abid; Tripathi, P.

2017-08-01

We emphasized on a detailed investigation of the structural, optical, and magnetic properties of pure and Ni-doped SnO2 nanoparticles (NPs) synthesized by a sol-gel process. An extensive structural study has been carried out using various characterization techniques. The X-ray Diffraction (XRD) spectra show the formation of the single phase tetragonal structure of pure and Ni-doped SnO2 NPs without any noticeable impurity phase such as NiO. XRD results indicate that the crystallite size of SnO2 is found to be decreased with Ni doping, which has also been confirmed by the Field Emission Scanning Electron Microscopy study. X-ray Photoelectron Spectroscopy (XPS) measurements displayed a clear sign for Ni2+ ions occupying the lattice sites of Sn4+ in the SnO2 host which also gives clear evidence for the formation of single phase Sn1-xNixO2 NPs. The optical analysis shows a significant decrease in the energy gap of SnO2, i.e., (from 3.71 eV to 3.28 eV) as Ni concentration increases which may be correlated with the core level valence band XPS analysis. Photoluminescence studies show that Ni doping creates oxygen vacancies due to dissimilar ionic radii of Ni2+ and Sn4+. Superconducting quantum interference device measurements revealed that the Ni doped SnO2 NPs exhibit strong ferromagnetic behavior at room temperature and this analysis has been well fitted with a simple relationship to find out magnetic parameters proposed by Stearns and Cheng et al. Hence, our results demonstrate that Ni-doping has strong impact on the structural, optical, and magnetic properties.

Dendrimer encapsulated Silver nanoparticles as novel catalysts for reduction of aromatic nitro compounds

NASA Astrophysics Data System (ADS)

Asharani, I. V.; Thirumalai, D.; Sivakumar, A.

2017-11-01

Polyethylene glycol (PEG) core dendrimer encapsulated silver nanoparticles (AgNPs) were synthesized through normal chemical reduction method, where dendrimer acts as reducing and stabilizing agent. The encapsulated AgNPs were well characterized using TEM, DLS and XPS techniques. The synthesized AgNPs showed excellent catalytic activity towards the reduction of aromatic nitro compounds with sodium borohydride as reducing agent and the results substantiate that dendrimer encapsulated AgNPs can be an effective catalyst for the substituted nitro aromatic reduction reactions. Also the kinetics of different nitro compounds reductions was studied and presented.

Electronic structure of CdSe-ZnS 2D nanoplatelets

NASA Astrophysics Data System (ADS)

Cruguel, Hervé; Livache, Clément; Martinez, Bertille; Pedetti, Silvia; Pierucci, Debora; Izquierdo, Eva; Dufour, Marion; Ithurria, Sandrine; Aubin, Hervé; Ouerghi, Abdelkarim; Lacaze, Emmanuelle; Silly, Mathieu G.; Dubertret, Benoit; Lhuillier, Emmanuel

2017-04-01

Among colloidal nanocrystals, 2D nanoplatelets (NPLs) made of cadmium chalcogenides have led to especially well controlled optical features. However, the growth of core shell heterostructures has so far been mostly focused on CdS shells, while more confined materials will be more promising to decouple the emitting quantum states of the core from their external environment. Using k.p simulation, we demonstrate that a ZnS shell reduces by a factor 10 the leakage of the wavefunction into the surrounding medium. Using X-ray photoemission (XPS), we confirm that the CdSe active layer is indeed unoxidized. Finally, we build an effective electronic spectrum for these CdSe/ZnS NPLs on an absolute energy scale which is a critical set of parameters for the future integration of this material into optoelectronic devices. We determine the work function (WF) to be 4.47 eV while the material is behaving as an n-type semiconductor.

Synthesis of Pd₃Co₁@Pt/C core-shell catalysts for methanol-tolerant cathodes of direct methanol fuel cells.

PubMed

Aricò, Antonino S; Stassi, Alessandro; D'Urso, Claudia; Sebastián, David; Baglio, Vincenzo

2014-08-18

A composite Pd-based electrocatalyst consisting of a surface layer of Pt (5 wt.%) supported on a core Pd3Co1 alloy (95 wt.%) and dispersed as nanoparticles on a carbon black support (50 wt.% metal content) was prepared by using a sulphite-complex route. The structure, composition, morphology, and surface properties of the catalyst were investigated by XRD, XRF, TEM, XPS and low-energy ion scattering spectroscopy (LE-ISS). The catalyst showed an enrichment of Pt on the surface and a smaller content of Co in the outermost layers. These characteristics allow a decrease the Pt content in direct methanol fuel cell cathode electrodes (from 1 to 0.06 mg cm(-2)) without significant decay in performance, due also to a better tolerance to methanol permeated through the polymer electrolyte membrane. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Synthesis and characterization of cationic lipid coated magnetic nanoparticles using multiple emulsions as microreactors

NASA Astrophysics Data System (ADS)

Akbaba, Hasan; Karagöz, Uğur; Selamet, Yusuf; Kantarcı, A. Gülten

2017-03-01

The aim of this study was to develop a novel iron oxide nanoparticle synthesis method with in-situ surface coating. For this purpose multiple emulsions were used as microreactors for the first time and magnetic iron oxide particles synthesized in the core of cationic solid lipid nanoparticles. DLS, SEM, TEM, VSM, Raman Spectrometer, XRD, and XPS techniques were performed for characterization of the magnetic nanoparticles. Obtained magnetic nanoparticles are superparamagnetic and no additional process was needed for surface adjustments. They are positively charged as a result of cationic lipid coating and has appropriate particle size (<30 nm) for drug or nucleic acid delivery. Structure analysis showed that magnetic core material is in the form of magnetite. Saturation magnetization value was measured as 15-17 emu g-1 for lipid coated magnetic nanoparticles obtained by multiple emulsion method which is reasonably sufficient for magnetic targeting.

Molecular-level removal of proteinaceous contamination from model surfaces and biomedical device materials by air plasma treatment.

PubMed

Banerjee, K K; Kumar, S; Bremmell, K E; Griesser, H J

2010-11-01

Established methods for cleaning and sterilising biomedical devices may achieve removal of bioburden only at the macroscopic level while leaving behind molecular levels of contamination (mainly proteinaceous). This is of particular concern if the residue might contain prions. We investigated at the molecular level the removal of model and real-life proteinaceous contamination from model and practical surfaces by air plasma (ionised air) treatment. The surface-sensitive technique of X-ray photoelectron spectroscopy (XPS) was used to assess the removal of proteinaceous contamination, with the nitrogen (N1s) photoelectron signal as its marker. Model proteinaceous contamination (bovine serum albumin) adsorbed on to a model surface (silicon wafer) and the residual proteinaceous contamination resulting from incubating surgical stainless steel (a practical biomaterial) in whole human blood exhibited strong N1s signals [16.8 and 18.5 atomic percent (at.%), respectively] after thorough washing. After 5min air plasma treatment, XPS detected no nitrogen on the sample surfaces, indicating complete removal of proteinaceous contamination, down to the estimated XPS detection limit 10ng/cm(2). Applying the same plasma treatment, the 7.7at.% nitrogen observed on a clinically cleaned dental bur was reduced to a level reflective of new, as-received burs. Contact angle measurements and atomic force microscopy also indicated complete molecular-level removal of the proteinaceous contamination upon air plasma treatment. This study demonstrates the effectiveness of air plasma treatment for removing proteinaceous contamination from both model and practical surfaces and offers a method for ensuring that no molecular residual contamination such as prions is transferred upon re-use of surgical and dental instruments. Crown Copyright © 2010. Published by Elsevier Ltd. All rights reserved.

Combined soft and hard X-ray ambient pressure photoelectron spectroscopy studies of semiconductor/electrolyte interfaces

DOE PAGES

Starr, David E.; Favaro, Marco; Abdi, Fatwa F.; ...

2017-05-18

The development of solar fuel generating materials would greatly benefit from a molecular level understanding of the semiconductor/electrolyte interface and changes in the interface induced by an applied potential and illumination by solar light. Ambient pressure photoelectron spectroscopy techniques with both soft and hard X-rays, AP-XPS and AP-HAXPES respectively, have the potential to markedly contribute to this understanding. In this paper we initially provide two examples of current challenges in solar fuels material development that AP-XPS and AP-HAXPES can directly a ddress. This will be followed by a brief description of the distinguishing and complementary characteristics of soft and hardmore » X-ray AP-XPS and AP-HAXPES and best approaches to achieving monolayer sensitivity in solid/aqueous electrolyte studies. In particular we focus on the detection of surface adsorbed hydroxyl groups in the presence of aqueous hydroxide anions in the electrolyte, a common situation when investigating photoanodes for solar fuel generating applications. Finally, the article concludes by providing an example of a combined AP-XPS and AP-HAXPES study of a semiconductor/aqueous electrolyte interface currently used in water splitting devices specifically the BiVO 4/aqueous potassium phosphate electrolyte interface.« less

Auger Electrons as Probes for Composite Micro- and Nano- structured Materials: Application to Solid Electrolyte Interphases in Graphite and Silicon-Graphite Electrodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kalaga, Kaushik; Shkrob, Ilya A.; Haasch, Richard T.

In this study, Auger electron spectroscopy (AES) combined with ion sputtering profilometry, Xray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) have been used in a complementary fashion to examine chemical and microstructural changes in graphite (Gr) and silicon/graphite (Si/Gr) blends contained in the negative electrodes of lithium-ion cells. We demonstrate how AES can be used to characterize morphology of the solid-electrolyte interphase (SEI) deposits in such heterogeneous media, complementing well-established methods, such as XPS and SEM. In this way we demonstrate that the SEI does not consist of uniformly thick layers on the graphite and silicon; the thickness ofmore » the SEI layers in cycle-life aged electrodes follows an exponential distribution with a mean of ca. 13 nm for the graphite and ca. 20-25 nm for the silicon nanoparticles (with a crystalline core of 50-70 nm in diameter). Furthermore, a “sticky-sphere” model, in which Si nanoparticles are covered with a layer of polymer binder (that is replaced by the SEI during cycling) of variable thickness is introduced to account for the features observed.« less

X-Ray Photoelectron Spectroscopy and Tribology Studies of Annealed Fullerene-like WS2 Nanoparticles

NASA Astrophysics Data System (ADS)

Kopnov, F.; Tenne, R.; Späth, B.; Jägermann, W.; Cohen, H.; Feldman, Y.; Zak, A.; Moshkovich, A.; Rapoport, L.

The temporal chemical changes occurring at the surface of fullerene-like (IF) nanoparticles of WS2 were investigated using X-ray photo-electron spectroscopy (XPS) and compared to those of bulk powder (2H) of the same material. It is possible to follow the long term (surface oxidation and carbonization) occurring at defects on the outermost surface (0001) layer of the fullerene-like nanoparticles. Similar but perhaps more distinctive changes are observed on the prismatic (hk0) surfaces of the 2H powder. Vacuum annealing is shown to remove most of these changes and bring the surface close to its stoichiometric composition. In accordance with previous measurements, further evidence is obtained for the existence of water molecules which are entrapped in the hollow core and interstitial defects of the fullerene-like nanoparticles during the synthesis. They are also shown to be removed by the vacuum annealing process. Chemically resolved electrical measurements (CREM) in the XPS show that the vacuum annealed IF samples become more intrinsic. Finally, tribological measurements show that the vacuum annealed IF samples perform better as an additive to oil than the non-annealed IF samples and the bulk (2H) platelets powder.

Auger Electrons as Probes for Composite Micro- and Nano- structured Materials: Application to Solid Electrolyte Interphases in Graphite and Silicon-Graphite Electrodes

DOE PAGES

Kalaga, Kaushik; Shkrob, Ilya A.; Haasch, Richard T.; ...

2017-10-05

In this study, Auger electron spectroscopy (AES) combined with ion sputtering profilometry, Xray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) have been used in a complementary fashion to examine chemical and microstructural changes in graphite (Gr) and silicon/graphite (Si/Gr) blends contained in the negative electrodes of lithium-ion cells. We demonstrate how AES can be used to characterize morphology of the solid-electrolyte interphase (SEI) deposits in such heterogeneous media, complementing well-established methods, such as XPS and SEM. In this way we demonstrate that the SEI does not consist of uniformly thick layers on the graphite and silicon; the thickness ofmore » the SEI layers in cycle-life aged electrodes follows an exponential distribution with a mean of ca. 13 nm for the graphite and ca. 20-25 nm for the silicon nanoparticles (with a crystalline core of 50-70 nm in diameter). Furthermore, a “sticky-sphere” model, in which Si nanoparticles are covered with a layer of polymer binder (that is replaced by the SEI during cycling) of variable thickness is introduced to account for the features observed.« less

Full membrane spanning self-assembled monolayers as model systems for UHV-based studies of cell-penetrating peptides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Franz, Johannes; Graham, Daniel J.; Schmüser, Lars

2015-03-01

Biophysical studies of the interaction of peptides with model membranes provide a simple yet effective approach to understand the transport of peptides and peptide based drug carriers across the cell membrane. Therein, the authors discuss the use of self-assembled monolayers fabricated from the full membrane-spanning thiol (FMST) 3-((14-((4'-((5-methyl-1-phenyl-35-(phytanyl)oxy-6,9,12,15,18,21,24,27,30,33,37-undecaoxa-2,3-dithiahenpentacontan-51-yl)oxy)-[1,1'-biphenyl]-4-yl)oxy)tetradecyl)oxy)-2-(phytanyl)oxy glycerol for ultrahigh vacuum (UHV) based experiments. UHV-based methods such as electron spectroscopy and mass spectrometry can provide important information about how peptides bind and interact with membranes, especially with the hydrophobic core of a lipid bilayer. Moreover, near-edge x-ray absorption fine structure spectra and x-ray photoelectron spectroscopy (XPS) data showed thatmore » FMST forms UHV-stable and ordered films on gold. XPS and time of flight secondary ion mass spectrometry depth profiles indicated that a proline-rich amphipathic cell-penetrating peptide, known as sweet arrow peptide is located at the outer perimeter of the model membrane.« less

Catalyst-free fabrication of novel ZnO/CuO core-Shell nanowires heterojunction: Controlled growth, structural and optoelectronic properties

NASA Astrophysics Data System (ADS)

Khan, Muhammad Arif; Wahab, Yussof; Muhammad, Rosnita; Tahir, Muhammad; Sakrani, Samsudi

2018-03-01

Development of controlled growth and vertically aligned ZnO/CuO core-shell heterojunction nanowires (NWs) with large area by a catalyst free vapor deposition and oxidation approach has been investigated. Structural characterization reveals successful fabrication of a core ZnO nanowire having single crystalline hexagonal wurtzite structure along [002] direction and CuO nanostructure shell with thickness (8-10 nm) having polycrystalline monoclinic structure. The optical property analysis suggests that the reflectance spectrum of ZnO/CuO heterostructure nanowires is decreased by 18% in the visible range, which correspondingly shows high absorption in this region as compared to pristine ZnO nanowires. The current-voltage (I-V) characteristics of core-shell heterojunction nanowires measured by conductive atomic force microscopy (C-AFM) shows excellent rectifying behavior, which indicates the characteristics of a good p-n junction. The high-resolution transmission electron microscopy (HRTEM) has confirmed the sharp junction interface between the core-shell heterojunction nanowire arrays. The valence band offset and conduction band offset at ZnO/CuO heterointerfaces are measured to be 2.4 ± 0.05 and 0.23 ± 0.005 eV respectively, using X-ray photoelectron spectroscopy (XPS) and a type-II band alignment structure is found. The results of this study contribute to the development of new advanced device heterostructures for solar energy conversion and optoelectronics applications.

Mechanism of in situ surface polymerization of gallic acid in an environmental-inspired preparation of carboxylated core-shell magnetite nanoparticles.

PubMed

Tóth, Ildikó Y; Szekeres, Márta; Turcu, Rodica; Sáringer, Szilárd; Illés, Erzsébet; Nesztor, Dániel; Tombácz, Etelka

2014-12-30

Magnetite nanoparticles (MNPs) with biocompatible coatings are good candidates for MRI (magnetic resonance imaging) contrasting, magnetic hyperthermia treatments, and drug delivery systems. The spontaneous surface induced polymerization of dissolved organic matter on environmental mineral particles inspired us to prepare carboxylated core-shell MNPs by using a ubiquitous polyphenolic precursor. Through the adsorption and in situ surface polymerization of gallic acid (GA), a polygallate (PGA) coating is formed on the nanoparticles (PGA@MNP) with possible antioxidant capacity. The present work explores the mechanism of polymerization with the help of potentiometric acid-base titration, dynamic light scattering (for particle size and zeta potential determination), UV-vis (UV-visible light spectroscopy), FTIR-ATR (Fourier-transformed infrared spectroscopy by attenuated total reflection), and XPS (X-ray photoelectron spectroscopy) techniques. We observed the formation of ester and ether linkages between gallate monomers both in solution and in the adsorbed state. Higher polymers were formed in the course of several weeks both on the surface of nanoparticles and in the dispersion medium. The ratio of the absorbances of PGA supernatants at 400 and 600 nm (i.e., the E4/E6 ratio commonly used to characterize the degree of polymerization of humic materials) was determined to be 4.3, similar to that of humic acids. Combined XPS, dynamic light scattering, and FTIR-ATR results revealed that, prior to polymerization, the GA monomers became oxidized to poly(carboxylic acid)s due to ring opening while Fe(3+) ions reduced to Fe(2+). Our published results on the colloidal and chemical stability of PGA@MNPs are referenced thoroughly in the present work. Detailed studies on biocompatibility, antioxidant property, and biomedical applicability of the particles will be published.

Liquid-phase pulsed laser ablation synthesis of graphitized carbon-encapsulated palladium core-shell nanospheres for catalytic reduction of nitrobenzene to aniline

NASA Astrophysics Data System (ADS)

Kim, Yu-jin; Ma, Rory; Reddy, D. Amaranatha; Kim, Tae Kyu

2015-12-01

Graphitized carbon-encapsulated palladium (Pd) core-shell nanospheres were produced via pulsed laser ablation of a solid Pd foil target submerged in acetonitrile. The microstructural features and optical properties of these nanospheres were characterized via high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and UV-visible spectroscopy. Microstructural analysis indicated that the core-shell nanostructures consisted of single-crystalline cubic metallic Pd spheres that serve as the core material, over which graphitized carbon was anchored as a heterogeneous shell. The absorbance spectrum of the synthesized nanostructures exhibited a broad (absorption) band at ∼264 nm; this band corresponded to the typical inter-band transition of a metallic system and resulted possibly from the absorbance of the ionic Pd2+. The catalytic properties of the Pd and Pd@C core-shell nanostructures were investigated using the reduction of nitrobenzene to aniline by an excess amount of NaBH4 in an aqueous solution at room temperature, as a model reaction. Owing to the graphitized carbon-layered structure and the high specific surface area, the resulting Pd@C nanostructures exhibited higher conversion efficiencies than their bare Pd counterparts. In fact, the layered structure provided access to the surface of the Pd nanostructures for the hydrogenation reaction, owing to the synergistic effect between graphitized carbon and the nanostructures. Their unique structure and excellent catalytic performance render Pd@C core-shell nanostructures highly promising candidates for catalysis applications.

Photoreactive, core-shell cross-linked/hollow microspheres prepared by delayed addition of cross-linker in dispersion polymerization for antifouling and immobilization of protein.

PubMed

Wang, Shengliu; Yue, Kai; Liu, Lianying; Yang, Wantai

2013-01-01

When dispersion polymerization of styrene (St) had run for 3h, after particle rapidly growing stage, 4,4'-dimethacryloyloxybenzophenone (DMABP) cross-linker was added to reaction system and photoreactive, core(PSt)-shell(Poly(St-co-DMABP)) particles with rich benzophenone (BP) groups on surface were prepared. Polymerization of DMABP could occurred mainly on the preformed core of PSt because its diffusion could be impeded by (1) compactness of particles formed at the moment of cross-linker addition (more than 80% of monomer had been consumed, particles were no longer fully swollen by monomer), (2) reduced polarity of continuous phase, and (3) immediate occurrence of cross-linking. Subsequently, photoreactive, cross-linked hollow particles were yielded by removal of uncross-linked core in THF. SEM and TEM observation demonstrated the formation of core-shell structure and improvement of shell thickness when DMABP content increased. UV-vis spectra analysis on polymer dissolved in THF indicated that there is no polymer of DMABP in core. FTIR spectra analysis and XPS measurement further revealed that BP component on particle surface was enriched when amount of DMABP increased. Finally, an anti-fouling polymer (poly (ethylene glycol), PEG) and protein of mouse IgG was immobilized on particle surface under UV irradiation, as confirmed by FTIR spectra analysis, SEM observation and TMB color reaction. Crown Copyright © 2012. Published by Elsevier Inc. All rights reserved.

X-ray photoelectron spectroscopic and morphologic studies of Ru nanoparticles deposited onto highly oriented pyrolytic graphite

NASA Astrophysics Data System (ADS)

Bavand, R.; Yelon, A.; Sacher, E.

2015-11-01

Ruthenium nanoparticles (Ru NPs) function as effective catalysts in specific reactions, such as methanation and Fischer-Tropsch syntheses. It is our purpose to physicochemically characterize their surfaces, at which catalysis occurs, by surface-sensitive X-ray photoelectron spectroscopy (XPS), using the symmetric peak component anaylsis technique developed in our laboratory to reveal previously hidden components. Ru NPs were deposited by evaporation (0.25-1.5 nm nominal deposition range) onto highly oriented pyrolytic graphite (HOPG). In addition to their surfaces being characterized by XPS, an indication of morphology was obtained from transmission electron microscopy (TEM). Our use of symmetric peak component XPS analysis has revealed detailed information on a previously unidentified surface oxide initially formed, as well as on the valence electronic structure and its variation with NP size, information that is of potential importance in the use of these NPs in catalysis. Each of the several Ru core XPS spectra characterized (3d, 3p and 3s) was found to be composed of three symmetric components. Together with two metal oxide O1s components, these give evidence of a rather complex, previously unidentified oxide that is initially formed. The Ru valence band (4d and 5s) spectra clearly demonstrate a loss of metallicity, a simultaneous increase of the Kubo gap, and an abrupt transfer in valence electron density from the 4d to the 5s orbitals (known as electron spill-over), as the NP size decreases below 0.5 nm. TEM photomicrographs, as a function of deposition rate, show that, at a rate that gives insufficient time for the NP condensation energy to dissipate, the initially well-separated NPs are capable of diffusing laterally and aggregating. This indicates weak NP bonding to the HOPG substrate. Carbide is formed, at both high and low deposition rates, at Ru deposition thicknesses greater than 0.25 nm, its formation explained by Ru NPs reacting with residual hydrocarbon vapor, under the influence of the heat of condensation released on Ru deposition, and not by Ru reacting with the HOPG substrate.

Elemental content of enamel and dentin after bleaching of teeth (a comparative study between laser-induced breakdown spectroscopy and x-ray photoelectron spectroscopy)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Imam, H.; Ahmed, Doaa; Eldakrouri, Ashraf

2013-06-21

The elemental content of the superficial and inner enamel as well as that of dentin was analyzed using laser-induced breakdown spectroscopy (LIBS) and x-ray photoelectron spectroscopy (XPS) of bleached and unbleached tooth specimens. It is thus clear from the spectral analysis using both the LIBS and XPS technique that elemental changes (though insignificant within the scopes of this study) of variable intensities do occur on the surface of the enamel and extend deeper to reach dentin. The results of the LIBS revealed a slight reduction in the calcium levels in the bleached compared to the control specimens in all themore » different bleaching groups and in both enamel and dentin. The good correlation found between the LIBS and XPS results demonstrates the possibility of LIBS technique for detection of minor loss in calcium and phosphorus in enamel and dentin.« less

Stabilizing subnanometer Ag(0) nanoclusters by thiolate and diphosphine ligands and their crystal structures

NASA Astrophysics Data System (ADS)

Yang, Huayan; Wang, Yu; Zheng, Nanfeng

2013-03-01

The combined use of thiolate and diphosphine as surface ligands helps to stabilize subnanometer Ag(0) nanoclusters, resulting in the successful crystallization of two Ag(0)-containing nanoclusters (Ag16 and Ag32) for X-ray single crystal analysis. Both clusters have core-shell structures with Ag86+ and Ag2212+ as their cores, which are not simply either fragments of face-centered cubic metals or their five-fold twinned counterparts. The clusters display UV-Vis absorption spectra consisting of molecule-like optical transitions.The combined use of thiolate and diphosphine as surface ligands helps to stabilize subnanometer Ag(0) nanoclusters, resulting in the successful crystallization of two Ag(0)-containing nanoclusters (Ag16 and Ag32) for X-ray single crystal analysis. Both clusters have core-shell structures with Ag86+ and Ag2212+ as their cores, which are not simply either fragments of face-centered cubic metals or their five-fold twinned counterparts. The clusters display UV-Vis absorption spectra consisting of molecule-like optical transitions. Electronic supplementary information (ESI) available: Experimental details, more pictures of the structure and XPS spectra of the clusters. CCDC 916463 and 916464. For ESI and crystallographic data in CIF or other electronic format see DOI: 10.1039/c3nr34328f

Auger electron diffraction study of the growth of Fe(001) films on ZnSe(001)

NASA Astrophysics Data System (ADS)

Jonker, B. T.; Prinz, G. A.

1991-03-01

The growth of Fe films on ZnSe(001) epilayers and bulk GaAs(001) substrates has been studied to determine the mode of film growth, the formation of the interface, and the structure of the overlayer at the 1-10 monolayer level. Auger electron diffraction (AED), x-ray photoelectron spectroscopy (XPS), and reflection high-energy electron diffraction data are obtained for incremental deposition of the Fe(001) overlayer. The coverage dependence of the AED forward scattering peaks reveals a predominantly layer-by-layer mode of film growth at 175 °C on ZnSe, while a more three-dimensional growth mode occurs on the oxide-desorbed GaAs(001) substrate. XPS studies of the semiconductor 3d levels indicate that the Fe/ZnSe interface is less reactive than the Fe/GaAs interface.

Optical and transport properties of LaTi{sub 1−x}M{sub x}(O,N){sub 3±δ} (x=0; 0.1, M=Nb{sup 5+}, W{sup 6+}) thin films prepared by plasma ammonolysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maegli, Alexandra E.; Sagarna, Leyre; Populoh, Sascha

2014-03-15

Oxynitride thin films of composition LaTi{sub 1−x}M{sub x}(O,N){sub 3±δ} with x=0; 0.1 and M=Nb{sup 5+}, W{sup 6+} were prepared by nitridation via microwave-induced plasma (MIP) ammonolysis, which allowed keeping the nitridation time short (16 min). The higher possible oxidation states of the B-site substituents (Nb{sup 5+}, W{sup 6+}) with respect to Ti{sup 4+} caused higher N content for LaTi{sub 0.9}Nb{sub 0.1}(O,N){sub 3±δ} and LaTi{sub 0.9}W{sub 0.1}(O,N){sub 3±δ} compared to LaTiO{sub 2}N due to charge-compensation. XPS O 1s and N 1s core level and valence band spectra evidenced for increasing N content in the order LaTiO{sub 2}N

Interaction of atomic oxygen with thin film and bulk copper: An XPS, AES, XRD, and profilometer study

NASA Technical Reports Server (NTRS)

Raikar, Genesh N.; Gregory, John C.; Christl, Ligia C.; Peters, Palmer N.

1992-01-01

The University of Alabama in Huntsville (UAH) experiment A-0114 was designed primarily to study degradation of material surfaces due to low earth orbital (LEO) atmospheric oxygen. The experiment contained 128 one inch circular samples: metals, polymers, carbons, and semiconductors. Among metal samples, copper has shown some interesting new results. Two types of copper samples, a film sputter coated on fused silica and a bulk piece of OFHC copper, were characterized employing a variety of techniques such as X-ray and Auger electron spectroscopies, X-ray diffraction, and high resolution profilometry. Cu 2p core level spectra were used to characterize the presence of Cu2O and CuO in addition to Cu Auger LMM lines. These results are supported by our recent X-ray diffraction studies which clearly establish the presence of Cu oxides which we were unable to prove in our earlier work. Profilometry showed an increase in thickness of the film sample where exposed to 106.7 +/- 0.5 nm from an initial thickness of 74.2 +/- 1.1 nm. Further studies with SEM and ellipsometry are underway.

The surface of 1-euro coins studied by X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Gou, F.; Gleeson, M. A.; Villette, J.; Kleyn, S. E. F.; Kleyn, A. W.

2004-03-01

The two alloy surfaces (pill and ring) that are present on 1-euro coins have been studied by X-ray photoelectron spectroscopy (XPS). Comparison is made between coins from general circulation and coin surfaces that have been subjected to a variety of cleaning and oxidation treatments. The concentrations and possible oxidation states of the metals (nickel, copper and zinc) at the surface were derived from analysis of the 2p 3/2 core levels. The surface atomic ratios measured for the pill and the ring parts of the euro coins were compared to the official bulk ratios. This study shows a clear nickel enrichment of both pill and ring surfaces. Nickel at surface seems to be present mainly in hydroxide form although the chloride form cannot be excluded. A small concentration of zinc was present on the surface of the pill, even though it is not present in the bulk alloy. Evidence of both nickel and zinc surface enrichment is observed for the ring. No surface enrichment is observed for the atomically clean or oxidized alloy surfaces over a 60-h time scale.

Hierarchical Mesoporous NiO/MnO2@PANI Core-Shell Microspheres, Highly Efficient and Stable Bifunctional Electrocatalysts for Oxygen Evolution and Reduction Reactions.

PubMed

He, Junkai; Wang, Mingchao; Wang, Wenbo; Miao, Ran; Zhong, Wei; Chen, Sheng-Yu; Poges, Shannon; Jafari, Tahereh; Song, Wenqiao; Liu, Jiachen; Suib, Steven L

2017-12-13

We report on the new facile synthesis of mesoporous NiO/MnO 2 in one step by modifying inverse micelle templated UCT (University of Connecticut) methods. The catalyst shows excellent electrocatalytic activity and stability for both the oxygen evolution reaction (OER) and the oxygen reduction reaction (ORR) in alkaline media after further coating with polyaniline (PANI). For electrochemical performance, the optimized catalyst exhibits a potential gap, ΔE, of 0.75 V to achieve a current of 10 mA cm -2 for the OER and -3 mA cm -2 for the ORR in 0.1 M KOH solution. Extensive characterization methods were applied to investigate the structure-property of the catalyst for correlations with activity (e.g., XRD, BET, SEM, HRTEM, FIB-TEM, XPS, TGA, and Raman). The high electrocatalytic activity of the catalyst closely relates to the good electrical conductivity of PANI, accessible mesoporous structure, high surface area, as well as the synergistic effect of the specific core-shell structure. This work opens a new avenue for the rational design of core-shell structure catalysts for energy conversion and storage applications.

Ultrasound-induced capping of polystyrene on TiO2 nanoparticles by precipitation with compressed CO2 as antisolvent.

PubMed

Zhang, Jianling; Liu, Zhimin; Han, Buxing; Li, Junchun; Li, Zhonghao; Yang, Guanying

2005-06-01

In this work, a route for the synthesis of inorganic/polymer core/shell composite nanoparticles was proposed, which can be called the antisolvent-ultrasound method. Compressed CO2 was used as antisolvent to precipitate the polymer from its solution dispersed with inorganic nanoparticles, during which ultrasonic irradiation was used to induce the coating of precipitated polymers on the surfaces of the inorganic nanoparticles. TiO2/polystyrene (PS) core/shell nanocomposites have been successfully prepared using this method. The transmission electronic micrographs (TEM) of the obtained nanocomposites show that the TiO2 nanoparticles are coated by the PS shells, of which the thickness can be tuned by the pressure of CO2. The phase structure, absorption properties, and thermal stability of the composite were characterized by X-ray diffraction (XRD), UV-vis spectra, and thermogravimetry, respectively. The results of X-ray photoelectron spectra (XPS) indicate the formation of a strong interaction between PS and TiO2 nanoparticles in the resultant products. This method has some potential advantages for applications and may be easily applied to the preparation of a range of inorganic/polymer core/shell composite nanoparticles.

Human nitric oxide biomarker as potential NO donor in conjunction with superparamagnetic iron oxide @ gold core shell nanoparticles for cancer therapeutics.

PubMed

Singh, Nimisha; Patel, Khushbu; Sahoo, Suban K; Kumar, Rajender

2018-03-01

Nitric oxide releasing superparamagnetic (Fe 3 O 4 -Au@NTHP) nanoparticles were synthesized by conjugation of human biomarker of nitric oxide, N-nitrosothioproline with iron oxide-gold (Fe 3 O 4 -Au) core shell nanoparticles. The structure and morphology of the prepared nanoparticles were confirmed by ATR-FTIR, HR-TEM, EDAX, XPS, DLS and VSM measurements. N-nitrosothioproline is a natural molecule and nontoxic to humans. Thus, the core shell nanoparticles prepared were highly biocompatible. The prepared Fe 3 O 4 -Au@NTHP nanoparticles also provided an excellent release of nitric oxide in dark and upon light irradiation for cancer treatment. The amount of NO release was controllable with the wavelength of light and time of irradiation. The developed nanoparticles provided efficient cellular uptake and good cytotoxicity in picomolar range when tested on HeLa cancerous cells. These nanoparticles on account of their controllable NO release can also be used to release small amount of NO for killing cancerous cells without any toxic effect. Furthermore, the magnetic and photochemical properties of these nanoparticles provides dual platform for magneto therapy and phototherapy for cancer treatment. Copyright © 2017 Elsevier B.V. All rights reserved.

Band alignments of different buffer layers (CdS, Zn(O,S), and In{sub 2}S{sub 3}) on Cu{sub 2}ZnSnS{sub 4}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yan, Chang; Liu, Fangyang; Song, Ning

2014-04-28

The heterojunctions of different n-type buffers, i.e., CdS, Zn(O,S), and In{sub 2}S{sub 3} on p-type Cu{sub 2}ZnSnS{sub 4} (CZTS) were investigated using X-ray Photoelectron Spectroscopy (XPS) and Near Edge X-ray Absorption Fine Structure (NEXAFS) Measurements. The band alignment of the heterojunctions formed between CZTS and the buffer materials was carefully measured. The XPS data were used to determine the Valence Band Offsets (VBO) of different buffer/CZTS heterojunctions. The Conduction Band Offset (CBO) was calculated indirectly by XPS data and directly measured by NEXAFS characterization. The CBO of the CdS/CZTS heterojunction was found to be cliff-like with CBO{sub XPS} = −0.24 ± 0.10 eV and CBO{submore » NEXAFS} = −0.18 ± 0.10 eV, whereas those of Zn(O,S) and In{sub 2}S{sub 3} were found to be spike-like with CBO{sub XPS} = 0.92 ± 0.10 eV and CBO{sub NEXAFS} = 0.87 ± 0.10 eV for Zn(O,S)/CZTS and CBO{sub XPS} = 0.41 ± 0.10 eV for In{sub 2}S{sub 3}/CZTS, respectively. The CZTS photovoltaic device using the spike-like In{sub 2}S{sub 3} buffer was found to yield a higher open circuit voltage (Voc) than that using the cliff-like CdS buffer. However, the CBO of In{sub 2}S{sub 3}/CZTS is slightly higher than the optimum level and thus acts to block the flow of light-generated electrons, significantly reducing the short circuit current (Jsc) and Fill Factor (FF) and thereby limiting the efficiency. Instead, the use of a hybrid buffer for optimization of band alignment is proposed.« less

Co-electrospinning fabrication and photocatalytic performance of TiO{sub 2}/SiO{sub 2} core/sheath nanofibers with tunable sheath thickness

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cao, Houbao, E-mail: caohoubao66@163.com; Du, Pingfan; Song, Lixin

2013-11-15

Graphical abstract: - Highlights: • The core–sheath TiO{sub 2}/SiO{sub 2} nanofibers were fabricated by co-electrospinning technique. • The catalytic property of nanofibers with different sheath thickness was studied. • The potential methods of improving catalytic efficiency are suggested. - Abstract: In this paper, core/sheath TiO{sub 2}/SiO{sub 2} nanofibers with tunable sheath thickness were directly fabricated via a facile co-electrospinning technique with subsequent calcination at 500 °C. The morphologies and structures of core/sheath TiO{sub 2}/SiO{sub 2} nanofibers were characterized by TGA, FESEM, TEM, FTIR, XPS and BET. It was found that the 1D core/sheath nanofibers are made up of anatase–rutile TiO{submore » 2} core and amorphous SiO{sub 2} sheath. The influences of SiO{sub 2} sheath and its thickness on the photoreactivity were evaluated by observing photo-degradation of methylene blue aqueous solution under the irradiation of UV light. Compared with pure TiO{sub 2} nanofibers, the core/sheath TiO{sub 2}/SiO{sub 2} nanofibers performed a better catalytic performance. That was attributed to not only efficient separation of hole–electron pairs resulting from the formation of heterojunction but also larger surface area and surface silanol group which will be useful to provide higher capacity for oxygen adsorption to generate more hydroxyl radicals. And the optimized core/sheath TiO{sub 2}/SiO{sub 2} nanofibers with a sheath thickness of 37 nm exhibited the best photocatalytic performance.« less

Incorporation of low energy activated nitrogen onto HOPG surface: Chemical states and thermal stability studies by in-situ XPS and Raman spectroscopy

NASA Astrophysics Data System (ADS)

Chandran, Maneesh; Shasha, Michal; Michaelson, Shaul; Hoffman, Alon

2016-09-01

In this paper we report the chemical states analysis of activated nitrogen incorporated highly oriented pyrolytic graphite (HOPG) surface under well-controlled conditions. Nitrogen incorporation is carried out by two different processes: an indirect RF nitrogen plasma and low energy (1 keV) N2+ implantation. Bonding configuration, concentration and thermal stability of the incorporated nitrogen species by aforesaid processes are systematically compared by in-situ X-ray photoelectron spectroscopy (XPS). Relatively large concentration of nitrogen is incorporated onto RF nitride HOPG surface (16.2 at.%), compared to N2+ implanted HOPG surface (7.7 at.%). The evolution of N 1s components (N1, N2, N3) with annealing temperature is comprehensively discussed, which indicates that the formation and reorganization of local chemical bonding states are determined by the process of nitridation and not by the prior chemical conditioning (i.e., amorphization or hydrogenation) of the HOPG surface. A combined XPS and Raman spectroscopy studies revealed that N2+ implantation process resulted in a high level of defects to the HOPG surface, which cannot be annealed-out by heat treatment up to 1000 °C. On the other hand, the RF nitrogen plasma process did not produce a high level of surface defects, while incorporating nearly the same amount of stable nitrogen species.

Synthesis and Luminescence Properties of Core/Shell ZnS:Mn/ZnO Nanoparticles.

PubMed

Jiang, Daixun; Cao, Lixin; Liu, Wei; Su, Ge; Qu, Hua; Sun, Yuanguang; Dong, Bohua

2009-01-01

In this paper the influence of ZnO shell thickness on the luminescence properties of Mn-doped ZnS nanoparticles is studied. Transmission electron microscopy (TEM) images showed that the average diameter of ZnS:Mn nanoparticles is around 14 nm. The formation of ZnO shells on the surface of ZnS:Mn nanoparticles was confirmed by X-ray diffraction (XRD) patterns, high-resolution TEM (HRTEM) images, and X-ray photoelectron spectroscopy (XPS) measurements. A strong increase followed by a gradual decline was observed in the room temperature photoluminescence (PL) spectra with the thickening of the ZnO shell. The photoluminescence excitation (PLE) spectra exhibited a blue shift in ZnO-coated ZnS:Mn nanoparticles compared with the uncoated ones. It is shown that the PL enhancement and the blue shift of optimum excitation wavelength are led by the ZnO-induced surface passivation and compressive stress on the ZnS:Mn cores.

Functionalization of nanocrystalline diamond films with phthalocyanines

NASA Astrophysics Data System (ADS)

Petkov, Christo; Reintanz, Philipp M.; Kulisch, Wilhelm; Degenhardt, Anna Katharina; Weidner, Tobias; Baio, Joe E.; Merz, Rolf; Kopnarski, Michael; Siemeling, Ulrich; Reithmaier, Johann Peter; Popov, Cyril

2016-08-01

Phthalocyanine (Pc) derivatives containing different central metal atoms (Mn, Cu, Ti) and different peripheral chains were synthesized and comprehensively characterized. Their interaction with nanocrystalline diamond (NCD) films, as-grown by hot-filament chemical vapor deposition or after their modification with oxygen plasma to exchange the hydrogen termination with oxygen-containing groups, was studied by X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine structure (NEXAFS) spectroscopy. The elemental composition as determined by XPS showed that the Pc were grafted on both as-grown and O-terminated NCD. Mn, Cu and Ti were detected together with N stemming from the Pc ring and S in case of the Ti-Pc from the peripheral ligands. The results for the elemental surface composition and the detailed study of the N 1s, S 2p and O 1s core spectra revealed that Ti-Pc grafted better on as-grown NCD but Cu-Pc and Mn-Pc on O-terminated films. Samples of Mn-Pc on as-grown and O-terminated NCD were further investigated by NEXAFS spectroscopy. The results showed ordering of the grafted molecules, laying flat on the H-terminated NCD surface while only the macrocycles were oriented parallel to the O-terminated surface with the peripheral chains perpendicular to it.

Enhanced UV-visible response of bismuth subcarbonate nanowires for degradation of xanthate and photocatalytic reaction mechanism.

PubMed

Cui, Kuixin; He, Yuehui; Jin, Shengming

2016-04-01

(BiO)2CO3 nanowires were prepared by simple hydrothermal treatment of commercial Bi2O3 powders and characterized by X-ray diffractometry, scanning electron microscopy, transmission electron microscopy (TEM), high-resolution TEM, and X-ray photoelectron spectroscopy (XPS). The photocatalytic activity of (BiO)2CO3 nanowires was studied through degradation of sodium isopropyl xanthate. Photocatalytic experimental results indicated that the as-prepared (BiO)2CO3 nanowires show high photocatalytic efficiency. Photocatalytic activity increased after two cycles. Time-dependent UV-vis spectra demonstrated that the final degradation products included isopropyl alcohol and carbon disulfide. UV-vis diffuse reflection spectra showed that the band gap of the as-prepared (BiO)2CO3 nanowires and recycled (BiO)2CO3 nanowires were 2.75 eV and 1.15 eV, respectively. XPS results indicated that formation of Bi2S3@(BiO)2CO3 core-shell nanowires occurred after recycled photodegradation of isopropyl xanthate owing to existence of two types of Bi configurations in the recycled (BiO)2CO3 nanowires. A probable degradation mechanism of isopropyl xanthate was also proposed. Copyright © 2016 Elsevier Ltd. All rights reserved.

XPS Protocol for the Characterization of Pristine and Functionalized Single Wall Carbon Nanotubes

NASA Technical Reports Server (NTRS)

Sosa, E. D.; Allada, R.; Huffman, C. B.; Arepalli, S.

2009-01-01

Recent interest in developing new applications for carbon nanotubes (CNT) has fueled the need to use accurate macroscopic and nanoscopic techniques to characterize and understand their chemistry. X-ray photoelectron spectroscopy (XPS) has proved to be a useful analytical tool for nanoscale surface characterization of materials including carbon nanotubes. Recent nanotechnology research at NASA Johnson Space Center (NASA-JSC) helped to establish a characterization protocol for quality assessment for single wall carbon nanotubes (SWCNTs). Here, a review of some of the major factors of the XPS technique that can influence the quality of analytical data, suggestions for methods to maximize the quality of data obtained by XPS, and the development of a protocol for XPS characterization as a complementary technique for analyzing the purity and surface characteristics of SWCNTs is presented. The XPS protocol is then applied to a number of experiments including impurity analysis and the study of chemical modifications for SWCNTs.

Designed synthesis of multi-functional PEGylated Yb2O3:Gd@SiO2@CeO2 islands core@shell nanostructure.

PubMed

Li, Junqi; Yao, Shuang; Song, Shuyan; Wang, Xiao; Wang, Yinghui; Ding, Xing; Wang, Fan; Zhang, Hongjie

2016-07-28

Nanomaterials that can restrain or reduce the production of excessive reactive oxygen species such as H2O2 to defend and treat against Alzheimer's disease (AD) have attracted much attention. In this paper, we adopt the strategy of layer-by-layer deposition; namely, first synthesizing available gadolinium-doped ytterbia nanoparticles (Yb2O3:Gd NPs) as cores, and then coating them with silica via the classical Stöber method to prevent leakage and act as a carrier for subsequent ceria deposition and PEGylation, and finally obtain the expected core@shell-structured nanocomposite of PEGylated Yb2O3:Gd@SiO2@CeO2 islands. The nanomaterial has proved not only to be a high-performance dual-modal contrast agent for use in MRI and CT, but also to exhibit excellent catalase mimetic activity, which may help the prognosis, diagnosis and treatment of AD in the future. In addition, scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared (FTIR) spectroscopy characterization have revealed the successful design and synthesis of the cores with remarkable size uniformity, with well-distributed CeO2 islands decorated on the surface of SiO2 shells, and tightly immobilized PEG.

Empirical optimization of DFT  +  U and HSE for the band structure of ZnO.

PubMed

Bashyal, Keshab; Pyles, Christopher K; Afroosheh, Sajjad; Lamichhane, Aneer; Zayak, Alexey T

2018-02-14

ZnO is a well-known wide band gap semiconductor with promising potential for applications in optoelectronics, transparent electronics, and spintronics. Computational simulations based on the density functional theory (DFT) play an important role in the research of ZnO, but the standard functionals, like Perdew-Burke-Erzenhof, result in largely underestimated values of the band gap and the binding energies of the Zn 3d electrons. Methods like DFT  +  U and hybrid functionals are meant to remedy the weaknesses of plain DFT. However, both methods are not parameter-free. Direct comparison with experimental data is the best way to optimize the computational parameters. X-ray photoemission spectroscopy (XPS) is commonly considered as a benchmark for the computed electronic densities of states. In this work, both DFT  +  U and HSE methods were parametrized to fit almost exactly the binding energies of electrons in ZnO obtained by XPS. The optimized parameterizations of DFT  +  U and HSE lead to significantly worse results in reproducing the ion-clamped static dielectric tensor, compared to standard high-level calculations, including GW, which in turn yield a perfect match for the dielectric tensor. The failure of our XPS-based optimization reveals the fact that XPS does not report the ground state electronic structure for ZnO and should not be used for benchmarking ground state electronic structure calculations.

Empirical optimization of DFT  +  U and HSE for the band structure of ZnO

NASA Astrophysics Data System (ADS)

Bashyal, Keshab; Pyles, Christopher K.; Afroosheh, Sajjad; Lamichhane, Aneer; Zayak, Alexey T.

2018-02-01

ZnO is a well-known wide band gap semiconductor with promising potential for applications in optoelectronics, transparent electronics, and spintronics. Computational simulations based on the density functional theory (DFT) play an important role in the research of ZnO, but the standard functionals, like Perdew-Burke-Erzenhof, result in largely underestimated values of the band gap and the binding energies of the Zn3d electrons. Methods like DFT  +  U and hybrid functionals are meant to remedy the weaknesses of plain DFT. However, both methods are not parameter-free. Direct comparison with experimental data is the best way to optimize the computational parameters. X-ray photoemission spectroscopy (XPS) is commonly considered as a benchmark for the computed electronic densities of states. In this work, both DFT  +  U and HSE methods were parametrized to fit almost exactly the binding energies of electrons in ZnO obtained by XPS. The optimized parameterizations of DFT  +  U and HSE lead to significantly worse results in reproducing the ion-clamped static dielectric tensor, compared to standard high-level calculations, including GW, which in turn yield a perfect match for the dielectric tensor. The failure of our XPS-based optimization reveals the fact that XPS does not report the ground state electronic structure for ZnO and should not be used for benchmarking ground state electronic structure calculations.

Electronic structure of rare-earth chromium antimonides RECrSb{sub 3} (RE=La-Nd, Sm, Gd-Dy, Yb) by X-ray photoelectron spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Crerar, Shane J.; Mar, Arthur, E-mail: arthur.mar@ualberta.ca; Grosvenor, Andrew P.

The electronic structure of the ternary rare-earth chromium antimonides RECrSb{sub 3} (RE=La-Nd, Sm, Gd-Dy, Yb) has been examined by high-resolution X-ray photoelectron spectroscopy (XPS) for the first time. The RE 3d or 4d core-line spectra are substantially complicated by the presence of satellite peaks but their general resemblance to those of RE{sub 2}O{sub 3} tends to support the presence of trivalent RE atoms in RECrSb{sub 3}. However, the Yb 4d spectrum of YbCrSb{sub 3} also shows peaks that are characteristic of divalent ytterbium. The Cr 2p core-line spectra exhibit asymmetric lineshapes and little change in binding energy (BE) relative tomore » Cr metal, providing strong evidence for electronic delocalization. The Sb 3d core-line spectra reveal slightly negative BE shifts relative to elemental antimony, supporting the presence of anionic Sb species in RECrSb{sub 3}. The experimental valence band spectrum of LaCrSb{sub 3} matches well with the calculated density of states, and it can be fitted to component peaks belonging to individual atoms to yield an average formulation that agrees well with expectations ('La{sup 3+}Cr{sup 3+}(Sb{sup 2-}){sub 3}'). On progressing from LaCrSb{sub 3} to NdCrSb{sub 3}, the 4f-band in the valence band spectra grows in intensity and shifts to higher BE. The valence band spectrum for YbCrSb{sub 3} also supports the presence of divalent ytterbium. - Graphical Abstract: In their valence band spectra, the 4f-band intensifies and shifts to higher BE on progressing from LaCrSb{sub 3} to NdCrSb{sub 3}. Highlights: Black-Right-Pointing-Pointer High-resolution core-line and valence band XPS spectra were measured for RECrSb{sub 3}. Black-Right-Pointing-Pointer Divalent Yb is present in YbCrSb{sub 3}, in contrast to trivalent RE in other members. Black-Right-Pointing-Pointer Asymmetric Cr 2p spectral lineshape confirms delocalization of Cr valence electrons. Black-Right-Pointing-Pointer Small negative Sb 3d BE shifts support assignment of anionic Sb atoms. Black-Right-Pointing-Pointer Fitted valence band spectra show shifts in the 4f band as RE is changed.« less

Preparation and characterization of silica-coated ZnSe nanowires with thermal stability and photoluminescence.

PubMed

Xiong, Shenglin; Xi, Baojuan; Wang, Weizhi; Zhou, Hongyang; Zhang, Shuyuan; Qian, Yitai

2007-12-01

Silica-coated ZnSe nanowires with well-controlled the thickness of sheath in the range of 10-60 nm have been synthesized through a simple sol-gel process. The thickness of silica coating could be controlled through altering reaction parameters such as volume ratio of TEOS and ammonia. XRD, high-resolution TEM, X-ray photoelectron spectroscopy (XPS), Raman spectra, thermogravimetric analysis (TGA), and photoluminescence (PL) spectra were used to characterize the core/sheath nanostructures. Room-temperature PL measurements indicate these silica-coated ZnSe nanowires remarkably improve the PL intensity. Meanwhile, the thermal stability has been enhanced greatly, which is useful for their potential applications in advanced semiconductor devices.

An investigation into the surface heterogeneity of nitric acid oxidized carbon fiber

NASA Astrophysics Data System (ADS)

Woodhead, Andrea L.; de Souza, Mandy L.; Church, Jeffrey S.

2017-04-01

The carbon fiber surface plays a critical role in the performance of carbon fiber composite materials and, thus it is important to have a thorough understanding of the fiber surface. A series of nitric acid treated intermediate modulus carbon fibers with increasing treatment level was prepared and characterized using a range of surface sensitive techniques including Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), X-ray Photoelectron Spectroscopy (XPS) and Raman spectroscopy. The results, which were found to be consistent with increasing treatment levels, were compared to the literature. Raman spectral mapping has been used to investigate the heterogeneity of the carbon fiber surface after nitric acid oxidation. The mapping enabled the effects of surface treatment on carbon fiber to be investigated at a spatial resolution unattainable by XPS and provided chemical structure information not provided by SEM or AFM. The highest level of treatment resulted in the most heterogeneous surface. Raman mapping, while time consuming, can provide valuable information which can lead to an enhanced understanding of the heterogeneity of the carbon fiber surface.

X-ray photoelectron spectroscopy study of chemically-etched Nd-Ce-Cu-O surfaces

NASA Technical Reports Server (NTRS)

Vasquez, R. P.; Gupta, A.; Kussmaul, A.

1991-01-01

Acetic acid, Br2, and HCl solutions are investigated for removing insulating species from Nd(1.85)Ce(0.15)CuO(4-delta) (NCCO) thin film surfaces. X-ray photoelectron spectroscopy (XPS) shows that the HCl etch is most effective, yielding O 1s spectra comparable to those obtained from samples cleaned in vacuum and a clear Fermi edge in the valence band region. Reduction and oxidation reversibly induces and eliminates, respectively, Fermi level states for undoped samples, but has no clearly observable effect on the XPS spectra for doped samples. Reactivity to air is much less for NCCO compared to hole superconductors, which is attributed to the lack of reactive alkaline earth elements in NCCO.

Application of surface analysis to solve problems of wear

NASA Technical Reports Server (NTRS)

Buckley, D. H.

1981-01-01

Results are presented for the use of surface analytical tools including field ion microscopy, Auger emission spectroscopy analysis (AES), cylindrical mirror Auger analysis and X-ray photoelectron spectroscopy (XPS). Data from the field ion microscope reveal adhesive transfer (wear) at the atomic level with the formation of surface compounds not found in the bulk, and AES reveals that this transfer will occur even in the presence of surface oxides. Both AES and XPS reveal that in abrasive wear with silicon carbide and diamond contacting the transition metals, the surface and the abrasive undergo a chemical or structural change which effects wear. With silicon carbide, silicon volatilizes leaving behind a pseudo-graphitic surface and the surface of diamond is observed to graphitize.

Etude Spectroscopique des Surfaces des Couches Minces de Silicium Amorphe Hydrogene

NASA Astrophysics Data System (ADS)

Bekkay, Touhami

In this work, we have studied the surface of hydrogenated a-Si and phosphorous doped a-Si:H,P. Due to the presence of unstable dangling bonds, these films are oxidized in the air after their preparation. XPS and UPS have been used to study these oxidized surfaces before and after plasma sputtering and wet chemical cleaning. We used deconvolution technique for the analysis of the spectra. First, the composition of a-Si:H films, prepared by plasma deposition at various power levels, has been determined by XPS. It has been found that films deposited using 5 W power contain SiH_4 molecules. This is confirmed by IR measurements. These molecules have not been seen in films prepared with a plasma power above 5 W. The XPS spectra of the surface oxide, before and after 3 keV sputtering by argon show that is impossible to completely remove these surface oxide ions. During sputtering, some oxygen atoms are forward scattered into the silicon substrat and form new oxidation states. UPS has been used to study the valence bands of the oxidized surfaces before and after HF cleaning. Prior to a chemical etch, the valence band analysis of the native SiO_2 indicates the presence of three O(2p) orbitals, in agreement with theory. Two are non-bonding orbitals and the third is associated with weak bonding to Si(3p). Two other orbitals have been identified at 10 eV and 11.8 eV. They correspond to O(2p)-Si(3p) and O(2p)-Si(3s) bonds respectively. A residual film containing -SiH, -SiO, SiOH and non-bonding orbitals has been found, after HF cleaning. A series of a-Si:H films have been doped with phosphine (PH_3). Their corresponding XPS spectra around 130 eV are dominated by the surface and bulk plasmon peaks. Numerical filtering has been used to distinguish between the phosphorous P(2p) peak located at 129.5 eV and the phosphorous oxide peak located at 134 eV. The increase in the intensity of these peaks as the (PH_3) increases indicates that a certain proportion of phosphorous is incorporated into the Si matrix and that the rest is oxidized. The shifts of the bulk Fermi level, E_{rm F}, and the surface Fermi level, E _{rm FS}, vary linearly with (PH_3). The difference between these two straight lines give the potential responsible for the bulk band bending. Close to the surface, the band bending is deduced by varying the detection angle in XPS measurements; a maximum value of 0.2 eV has been found in a depth range of 38 A to 105 A.

A novel fabrication of Cu{sub 2}O@Cu{sub 7}S{sub 4} core-shell micro/nanocrystals from Cu{sub 2}O temples and enhanced photocatalytic activities

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Junqi, E-mail: sfmlab@163.com; Sun, Long; Yan, Ying

2016-08-15

Highlights: • The Cu{sub 2}O@Cu{sub 7}S{sub 4} core-shell crystals maintained the same morphology with template. • The crystals exhibit enhanced photocatalytic activity than the pure Cu{sub 2}O crystals. • The photocatalytic activity of different R crystals is diverse from each other. • A possible formation mechanism has been proposed. - Abstract: Uniform and monodispersed Cu{sub 2}O@Cu{sub 7}S{sub 4} core-shell micro/nanocrystals have been synthesized successfully at room temperature via a simple chemical etching reaction, using Cu{sub 2}O as sacrificial template. The structure and properties of the crystals were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscopy (TEM),more » X-ray photoelectron spectra (XPS). The photocatalytic activity of the Cu{sub 2}O@Cu{sub 7}S{sub 4} crystals was evaluated by photocatalytic decolorization of MeO (methyl orange) aqueous solution at ambient temperature under visible-light irradiation. The results show that the as-prepared Cu{sub 2}O@Cu{sub 7}S{sub 4} crystals revealed core-shell structure, which maintained the same morphology with corresponding template and were composed of cuboctahedron Cu{sub 7}S{sub 4} shell and active Cu{sub 2}O core. Due to the unique Cu{sub 2}O@Cu{sub 7}S{sub 4} core-shell structure, the crystals exhibit enhanced photocatalytic activity than that of the pure Cu{sub 2}O crystals, and the photocatalytic activity of different R crystals is diverse from each other. A possible formation mechanism has been proposed.« less

Passivation of InGaAs(001)-(2 × 4) by Self-Limiting Chemical Vapor Deposition of a Silicon Hydride Control Layer.

PubMed

Edmonds, Mary; Kent, Tyler; Chagarov, Evgueni; Sardashti, Kasra; Droopad, Ravi; Chang, Mei; Kachian, Jessica; Park, Jun Hong; Kummel, Andrew

2015-07-08

A saturated Si-Hx seed layer for gate oxide or contact conductor ALD has been deposited via two separate self-limiting and saturating CVD processes on InGaAs(001)-(2 × 4) at substrate temperatures of 250 and 350 °C. For the first self-limiting process, a single silicon precursor, Si3H8, was dosed at a substrate temperature of 250 °C, and XPS results show the deposited silicon hydride layer saturated at about 4 monolayers of silicon coverage with hydrogen termination. STS results show the surface Fermi level remains unpinned following the deposition of the saturated silicon hydride layer, indicating the InGaAs surface dangling bonds are electrically passivated by Si-Hx. For the second self-limiting process, Si2Cl6 was dosed at a substrate temperature of 350 °C, and XPS results show the deposited silicon chloride layer saturated at about 2.5 monolayers of silicon coverage with chlorine termination. Atomic hydrogen produced by a thermal gas cracker was subsequently dosed at 350 °C to remove the Si-Cl termination by replacing with Si-H termination as confirmed by XPS, and STS results confirm the saturated Si-Hx bilayer leaves the InGaAs(001)-(2 × 4) surface Fermi level unpinned. Density function theory modeling of silicon hydride surface passivation shows an Si-Hx monolayer can remove all the dangling bonds and leave a charge balanced surface on InGaAs.

Electrochemical and solid-state NMR studies on LiCoO 2 coated with Al 2O 3 derived from carboxylate-alumoxane

NASA Astrophysics Data System (ADS)

Fey, George T. K.; Kao, H. M.; Muralidharan, P.; Kumar, T. P.; Cho, Y. D.

The surface of LiCoO 2 cathodes was coated with various wt.% of Al 2O 3 derived from methoxyethoxy acetate-alumoxane (MEA-alumoxane) by a mechano-thermal coating procedure, followed by calcination at 723 K in air for 10 h. The structure and morphology of the surface modified LiCoO 2 samples have been characterized with XRD, SEM, EDS, TEM, BET, XPS/ESCA and solid-state 27Al magic angle spinning (MAS) NMR techniques. The Al 2O 3 coating forms a thin layer on the surface of the core material with an average thickness of 20 nm. The corresponding 27Al MAS NMR spectrum basically exhibited the same characteristics as the spectrum for pristine Al 2O 3 derived from MEA-alumoxane, indicating that the local environment of aluminum atoms was not significantly changed at coating levels below 1 wt.%. This provides direct evidence that Al 2O 3 was on the surface of the core materials. The LiCoO 2 coated with 1 wt.% Al 2O 3 sustained continuous cycle stability 13 times longer than pristine LiCoO 2. A comparison of the electrochemical impedance behavior of the pristine and coated materials revealed that the failure of pristine cathode performance is associated with an increase in the particle-particle resistance upon continuous cycling. Coating improved the cathode performance by suppressing the characteristic structural phase transitions (hexagonal to monoclinic to hexagonal) that occur in pristine LiCoO 2 during the charge-discharge processes.

The interaction of small metal particles with refractory oxide supports

NASA Technical Reports Server (NTRS)

Park, C.; Heinemann, K.

1985-01-01

Islands and continuous layers of Pd were grown in UHV on Mo and MoO subtrates. As-deposited Pd islands and layers exhibited bulk Pd adsorption properties for CO when the Pd had been deposited at RT and at thicknesses exceeding 3 ML. However, CO adsorption was drastically reduced upon annealing. This deactivation was interpreted in terms of substrate/support interaction involving the diffusion of substrate species toward the Pd surface, using AES, TPD, and work function measurement techniques. A study of the growth and annealing behavior of Pd on Mo(110) was made for thicknesses up to 12 monolayers and substrate temperatures up to 1300K, using AES, XPS, LEED, and work function measurements. At low tempertures Pd formed a monolayer without alloying. In thick layers (12 ML) annealed about 700 K, Mo diffusion into the Pd layer and alloying were noted. Such layers remained continuous up to 1100 K. Thinner Pd layers were less stable and started coalescing upon annealing to as little as 550 K. Significant changes in Pd Auger peak shape, as well as shifts of Pd core levels, were observed during layer growth and annealing.

The 2√{3}×2√{3}R30 surface reconstruction of alkali/Si(1 1 1):B semiconducting surfaces

NASA Astrophysics Data System (ADS)

Tournier-Colletta, C.; Chaput, L.; Tejeda, A.; Cardenas, L. A.; Kierren, B.; Malterre, D.; Fagot-Revurat, Y.; Fèvre, P. Le; Bertran, F.; Taleb-Ibrahimi, A.

2013-02-01

The surface structure of alkali doped Si(1 1 1):B ultra-thin films has been studied by low-energy electron diffraction (LEED), X-ray photoemission spectroscopy (XPS) and scanning tunneling microscopy (STM). A comparative study of K/Si(1 1 1)-3 × 1 and K/Si(1 1 1):B-2√{3}×2√{3}R30 interfaces allowed us to determine the saturation coverage to be 0.5 monolayer in the later case. The 2√{3}-surface reconstruction is shown to be a common property of pure K, Rb, Cs materials and K0.4Rb0.6 alloys but progressively disappears if Rb is replaced by Ca. Taking into account the existence of two distinct boron sites in the ratio 1/3 as seen from B-1s core levels spectra, LAPW-DFT calculations have been carried out in order to optimize the atomic structure. As a result, alkali adatoms are shown to form trimers leading to a large modulation of the Sisbnd B bonds accompanied by an inhomogeneous doping of the dangling bonds in agreement with voltage dependent STM images.

U-Zr alloy: XPS and TEM study of surface passivation

NASA Astrophysics Data System (ADS)

Paukov, M.; Tkach, I.; Huber, F.; Gouder, T.; Cieslar, M.; Drozdenko, D.; Minarik, P.; Havela, L.

2018-05-01

Surface reactivity of Uranium metal is an important factor limiting its practical applications. Bcc alloys of U with various transition metals are much less reactive than pure Uranium. So as to specify the mechanism of surface protection, we have been studying the U-20 at.% Zr alloy by photoelectron spectroscopy and transmission electron microscopy. The surface was studied in as-obtained state, in various stages of surface cleaning, and during an isochronal annealing cycle. The analysis based on U-4f, Zr-3p, and O-1 s spectra shows that a Zr-rich phase segregates at the surface at temperatures exceeding 550 K, which provides a self-assembled coating. The comparison of oxygen exposure of the stoichiometric and coated surfaces shows that the coating is efficiently preventing the oxidation of uranium even at elevated temperatures. The coating can be associated with the UZr2+x phase. TEM study indicated that the coating is about 20 nm thick. For the clean state, the U-4f core-level lines of the bcc alloy are practically identical to those of α-U, revealing similar delocalization of the 5f electronic states.

Laser induced Bi diffusion in As40S60 thin films and the optical properties change probed by FTIR and XPS

NASA Astrophysics Data System (ADS)

Naik, Ramakanta; Sahoo, Pragyan Paramita; Sripan, C.; Ganesan, R.

2016-12-01

Amorphous chalcogenide semiconducting materials are playing a pivotal role in modern technology. Such type of materials are very sensitive to electromagnetic radiations which is useful for infrared optics. In the present report, Bi doped in As40S60 thin films (As40S60, Bi06As40S54) of 800 nm thickness were prepared by thermal evaporation method. The Bi06As40S54 thin film is subjected to laser irradiation for photo induced study. The X-ray diffraction study reveals no structural change due to laser irradiation. The optical parameters are affected by both Bi addition and laser irradiation which brings a change in the transmitivity and absorption coefficient. The indirect optical band gap is found to be increased by 0.08 eV with laser irradiation with the decrease in disorderness. The Tauc parameter and Urbach energy which measures the degree of disorderness changes with Bi doping and irradiation. The refractive index is modified by the illumination process which is useful for optical applications. The optical property change is well supported by the X-ray photoelectron core level spectra.

Laser induced Te diffusion in amorphous As50Se50 thin films probed by FTIR and XPS

NASA Astrophysics Data System (ADS)

Behera, Mukta; Panda, Rozalin; Naik, Ramakanta

2017-05-01

In the present report, we have demonstrated the combine effect of deposition and photo diffusion of Te into As50Se50 chalcogenide thin films. The influence of Te deposition onto As50Se50 layer has modified the optical parameters. The thermally evaporated Te/As50Se50 bilayer film is irradiated with near bandgap laser light. The optical and structural property of Te/As50Se50 bilayer film under the influence of laser irradiation has been investigated by X-ray photo electron spectroscopy and Fourier transform infrared spectroscopy. The As3d, Se3d and Te4d core level peaks of the photo diffused film show significant changes in shape and position in comparisons with those obtained for non irradiated films. The extensive analysis by deconvoluting the spectra shows the Te diffusion into As50Se50 matrix by forming Te-As-Se layer. The optical band gap of the diffused region is found to be decreased with the increase of density of states in the band edge. The change in transmissivity and absorption coefficient modified the optical constants which is discussed in the light of the present result.

Acquisition and evolution of plant pathogenesis-associated gene clusters and candidate determinants of tissue-specificity in xanthomonas.

PubMed

Lu, Hong; Patil, Prabhu; Van Sluys, Marie-Anne; White, Frank F; Ryan, Robert P; Dow, J Maxwell; Rabinowicz, Pablo; Salzberg, Steven L; Leach, Jan E; Sonti, Ramesh; Brendel, Volker; Bogdanove, Adam J

2008-01-01

Xanthomonas is a large genus of plant-associated and plant-pathogenic bacteria. Collectively, members cause diseases on over 392 plant species. Individually, they exhibit marked host- and tissue-specificity. The determinants of this specificity are unknown. To assess potential contributions to host- and tissue-specificity, pathogenesis-associated gene clusters were compared across genomes of eight Xanthomonas strains representing vascular or non-vascular pathogens of rice, brassicas, pepper and tomato, and citrus. The gum cluster for extracellular polysaccharide is conserved except for gumN and sequences downstream. The xcs and xps clusters for type II secretion are conserved, except in the rice pathogens, in which xcs is missing. In the otherwise conserved hrp cluster, sequences flanking the core genes for type III secretion vary with respect to insertion sequence element and putative effector gene content. Variation at the rpf (regulation of pathogenicity factors) cluster is more pronounced, though genes with established functional relevance are conserved. A cluster for synthesis of lipopolysaccharide varies highly, suggesting multiple horizontal gene transfers and reassortments, but this variation does not correlate with host- or tissue-specificity. Phylogenetic trees based on amino acid alignments of gum, xps, xcs, hrp, and rpf cluster products generally reflect strain phylogeny. However, amino acid residues at four positions correlate with tissue specificity, revealing hpaA and xpsD as candidate determinants. Examination of genome sequences of xanthomonads Xylella fastidiosa and Stenotrophomonas maltophilia revealed that the hrp, gum, and xcs clusters are recent acquisitions in the Xanthomonas lineage. Our results provide insight into the ancestral Xanthomonas genome and indicate that differentiation with respect to host- and tissue-specificity involved not major modifications or wholesale exchange of clusters, but subtle changes in a small number of genes or in non-coding sequences, and/or differences outside the clusters, potentially among regulatory targets or secretory substrates.

A Multicenter Randomized Noninferiority Trial Comparing GreenLight-XPS Laser Vaporization of the Prostate and Transurethral Resection of the Prostate for the Treatment of Benign Prostatic Obstruction: Two-yr Outcomes of the GOLIATH Study.

PubMed

Thomas, James A; Tubaro, Andrea; Barber, Neil; d'Ancona, Frank; Muir, Gordon; Witzsch, Ulrich; Grimm, Marc-Oliver; Benejam, Joan; Stolzenburg, Jens-Uwe; Riddick, Antony; Pahernik, Sascha; Roelink, Herman; Ameye, Filip; Saussine, Christian; Bruyère, Franck; Loidl, Wolfgang; Larner, Tim; Gogoi, Nirjan-Kumar; Hindley, Richard; Muschter, Rolf; Thorpe, Andrew; Shrotri, Nitin; Graham, Stuart; Hamann, Moritz; Miller, Kurt; Schostak, Martin; Capitán, Carlos; Knispel, Helmut; Bachmann, Alexander

2016-01-01

The GOLIATH study is a 2-yr trial comparing transurethral resection of prostate (TURP) to photoselective vaporization with the GreenLight XPS Laser System (GL-XPS) for the treatment of benign prostatic obstruction (BPO). Noninferiority of GL-XPS to TURP was demonstrated based on a 6-mo follow-up from the study. To determine whether treatment effects observed at 6 mo between GL-XPS and TURP was maintained at the 2-yr follow-up. Prospective randomized controlled trial at 29 centers in nine European countries involving 281 patients with BPO. Photoselective vaporization using the 180-W GreenLight GL-XPS or conventional (monopolar or bipolar) TURP. The primary outcome was the International Prostate Symptom Score for which a margin of three was used to evaluate the noninferiority of GL-XPS. Secondary outcomes included Qmax, prostate volume, prostate specific antigen, Overactive Bladder Questionnaire Short Form, International Consultation on Incontinence Questionnaire Short Form, occurrence of surgical retreatment, and freedom from complications. One hundred and thirty-six patients were treated using GL-XPS and 133 using TURP. Noninferiority of GL-XPS on International Prostate Symptom Score, Qmax, and freedom from complications was demonstrated at 6-mo and was sustained at 2-yr. The proportion of patients complication-free through 24-mo was 83.6% GL-XPS versus 78.9% TURP. Reductions in prostate volume and prostate specific antigen were similar in both arms and sustained over the course of the trial. Compared with the 1(st) yr of the study, very few adverse events or retreatments were reported in either arm. Treatment differences in the Overactive Bladder Questionnaire Short Form observed at 12-mo were not statistically significant at 24-mo. A limitation was that patients and treating physicians were not blinded to the therapy. Twenty-four-mo follow-up data demonstrated that GL-XPS provides a durable surgical option for the treatment of BPO that exhibits efficacy and safety outcomes similar to TURP. The long-term effectiveness and safety of GLP-XLS was similar to conventional TURP for the treatment of prostate enlargement. Copyright © 2015 European Association of Urology. Published by Elsevier B.V. All rights reserved.

Location and Electronic Nature of Phosphorus in the Si Nanocrystal − SiO2 System

PubMed Central

König, Dirk; Gutsch, Sebastian; Gnaser, Hubert; Wahl, Michael; Kopnarski, Michael; Göttlicher, Jörg; Steininger, Ralph; Zacharias, Margit; Hiller, Daniel

2015-01-01

Up to now, no consensus exists about the electronic nature of phosphorus (P) as donor for SiO2-embedded silicon nanocrystals (SiNCs). Here, we report on hybrid density functional theory (h-DFT) calculations of P in the SiNC/SiO2 system matching our experimental findings. Relevant P configurations within SiNCs, at SiNC surfaces, within the sub-oxide interface shell and in the SiO2 matrix were evaluated. Atom probe tomography (APT) and its statistical evaluation provide detailed spatial P distributions. For the first time, we obtain ionisation states of P atoms in the SiNC/SiO2 system at room temperature using X-ray absorption near edge structure (XANES) spectroscopy, eliminating structural artefacts due to sputtering as occurring in XPS. K energies of P in SiO2 and SiNC/SiO2 superlattices (SLs) were calibrated with non-degenerate P-doped Si wafers. results confirm measured core level energies, connecting and explaining XANES spectra with h-DFT electronic structures. While P can diffuse into SiNCs and predominantly resides on interstitial sites, its ionization probability is extremely low, rendering P unsuitable for introducing electrons into SiNCs embedded in SiO2. Increased sample conductivity and photoluminescence (PL) quenching previously assigned to ionized P donors originate from deep defect levels due to P. PMID:25997696

Study of concentration-dependent cobalt ion doping of TiO2 and TiO(2-x)Nx at the nanoscale.

PubMed

Gole, James L; Prokes, Sharka M; Glembocki, O J; Wang, Junwei; Qiu, Xiaofeng; Burda, Clemens

2010-07-01

Experiments with a porous sol-gel generated TiO(2) nanocolloid and its corresponding oxynitride TiO(2-x)N(x) are carried out to evaluate those transformations which accompany additional doping with transition metals. In this study, doping with cobalt (Co(ii)) ions is evaluated using a combination of core level and VB-photoelectron and optical spectroscopy, complementing data obtained from Raman spectroscopy. Raman spectroscopy suggests that cobalt doping of porous sol-gel generated anatase TiO(2) and nitridated TiO(2-x)N(x) introduces a spinel-like structure into the TiO(2) and TiO(2-x)N(x) lattices. TEM and XPS data complemented by valence band-photoelectron spectra demonstrate that metallic cobalt clusters are not formed even at high doping levels. As evidenced by Raman spectroscopy, the creation of a spinel-like structure is commensurate with the room temperature conversion of the oxide and its oxynitride from the anatase to the rutile form. The onset of this kinetically driven process correlates with the formation of spinel sites within the TiO(2) and TiO(2-x)N(x) particles. Despite their visible light absorption, the photocatalytic activity of these cobalt seeded systems is diminished relative to the oxynitride TiO(2-x)N(x).

Design of WO3-SnO2 core-shell nanofibers and their enhanced gas sensing performance based on different work function

NASA Astrophysics Data System (ADS)

Li, Feng; Gao, Xing; Wang, Rui; Zhang, Tong

2018-06-01

In this work, core-shell WO3-SnO2 (CS-WS) nanofibers (NFs) have been successfully synthesized via a coaxial electrospinning approach. The structure and morphology characteristics of the resultant products were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectra (XPS). To investigate the sensing mechanism of the CS-WS NFs, sensors based on SnO2 NFs, WO3 NFs, and SnO2-WO3 composite NFs were fabricated respectively, and their gas sensing properties were investigated by using CO, ethanol, toluene, acetone, and ammonia as the test gas. The results indicated that the CS-WS NFs exhibited a good response to ethanol (5.09 at 10 ppm) and short response/recovery time (18.5 s and 282 s) compared with the other test gases. The enhanced ethanol sensing properties of CS-WS NFs compared with those of SnO2 NFs were closely associated with the CS structure and its derivative effect due to the different work function of SnO2 and WO3. The approach proposed in this study may contribute to the realization of more sensitive metal oxide semiconductor (MOS) core-shell heterostructure sensors.

Novel synthesis of core-shell Au-Pt dendritic nanoparticles supported on carbon black for enhanced methanol electro-oxidation

NASA Astrophysics Data System (ADS)

Cao, Ribing; Xia, Tiantian; Zhu, Ruizhi; Liu, Zhihua; Guo, Jinming; Chang, Gang; Zhang, Zaoli; Liu, Xiong; He, Yunbin

2018-03-01

Core-shell Au-Pt dendritic nanoparticles (Au-Pt NPs) has been synthesized via a facile seed-mediated growth method, in which dendritic Pt nanoparticles as shell grow on the surface of gold nanocores by using ascorbic acid (AA) as "green" reducing reagents. The morphologies and compositions of the as-prepared nanocomposites with core-shell structure are characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). Electrochemical experiments, including cyclic voltammetry (CV) and chronoamperometry (CA) are performed to investigate the electrocatalytic properties of the Au-Pt NPs loaded carbon black composites (Au-Pt NPs/V) towards methanol oxidation in an alkaline solution. It is found that the reduction time of AA could regulate the thickness and amount of Pt on the Au nanocores, which significantly affect catalytic activity of the Au-Pt NPs/V toward methanol oxidation. Au-Pt NPs/V with optimum reduction time 4 h exhibit 2.3-times higher electrocatalytic activity than that of a commercial catalyst (Pt/carbon black) and an excellent CO tolerance toward methanol oxidation. This behavior is attributed to large active electrochemical area of the bimetallic nanocomposites and the change in the electronic structure of Pt when Au surface modified with fewer Pt nanoparticles.

Organic nitrogen chemistry during low-grade metamorphism

USGS Publications Warehouse

Boudou, J.-P.; Schimmelmann, A.; Ader, M.; Mastalerz, Maria; Sebilo, M.; Gengembre, L.

2008-01-01

Most of the organic nitrogen (Norg) on Earth is disseminated in crustal sediments and rocks in the form of fossil nitrogen-containing organic matter. The chemical speciation of fossil Norg within the overall molecular structure of organic matter changes with time and heating during burial. Progressive thermal evolution of organic matter involves phases of enhanced elimination of Norg and ultimately produces graphite containing only traces of nitrogen. Long-term chemical and thermal instability makes the chemical speciation of Norg a valuable tracer to constrain the history of sub-surface metamorphism and to shed light on the subsurface biogeochemical nitrogen cycle and its participating organic and inorganic nitrogen pools. This study documents the evolutionary path of Norg speciation, transformation and elimination before and during metamorphism and advocates the use of X-ray photoelectron spectroscopy (XPS) to monitor changes in Norg speciation as a diagnostic tool for organic metamorphism. Our multidisciplinary evidence from XPS, stable isotopes, traditional quantitative coal analyses, and other analytical approaches shows that at the metamorphic onset Norg is dominantly present as pyrrolic and pyridinic nitrogen. The relative abundance of nitrogen substituting for carbon in condensed, partially aromatic systems (where N is covalently bonded to three C atoms) increases exponentially with increasing metamorphic grade, at the expense of pyridinic and pyrrolic nitrogen. At the same time, much Norg is eliminated without significant nitrogen isotope fractionation. The apparent absence of Rayleigh-type nitrogen isotopic fractionation suggests that direct thermal loss of nitrogen from an organic matrix does not serve as a major pathway for Norg elimination. Instead, we propose that hot H, O-containing fluids or some of their components gradually penetrate into the carbonaceous matrix and eliminate Norg along a progressing reaction front, without causing nitrogen isotope fractionation in the residual Norg in the unreacted core of the carbonaceous matrix. Before the reaction front can reach the core, an increasing part of core Norg chemically stabilizes in the form of nitrogen atoms substituting for carbon in condensed, partially aromatic systems forming graphite-like structural domains with delocalized ??-electron systems (nitrogen atoms substituting for "graphitic" carbon in natural metamorphic organic matter). Thus, this nitrogen species with a conservative isotopic composition is the dominant form of residual nitrogen at higher metamorphic grade. ?? 2007 Elsevier Ltd. All rights reserved.

Electronic structure and optical properties of defect chalcopyrite HgGa2Se4

NASA Astrophysics Data System (ADS)

Gabrelian, B. V.; Lavrentyev, A. A.; Vu, Tuan V.; Parasyuk, O. V.; Khyzhun, O. Y.

2018-01-01

We report on studies from an experimental and theoretical viewpoint of the electronic structure of mercury digallium selenide, HgGa2Se4, a very promising optoelectronic material. In particular, the method of X-ray photoelectron spectroscopy (XPS) was used to evaluate binding energies of the constituent element core electrons and the shape of the valence band for pristine and Ar+-ion bombarded surfaces of HgGa2Se4 single crystal. First principles band-structure calculations were performed in the present work using the augmented plane wave + local orbitals (APW+lo). These calculations indicate that the Se 4p states are the main contributors at the top and in the upper portion of the valence band with slightly smaller contributions of the Ga 4p states in the upper portion of the band as well. Further, the central portion of the valence band is determined mainly by contributions of the Ga 4s states, and the Hg 5d states are the principal contributors to the bottom of the valence band. These theoretical data are in fair agreement when matching on a common energy scale of the X-ray emission bands giving information on the energy distribution of the Se 4p and Ga 4p states and the XPS valence-band spectrum of the HgGa2Se4 crystal. The principal optical constants are elucidated from the DFT calculations.

X-Ray photoelectron Spectroscopy Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Engelhard, Mark H.; Droubay, Timothy C.; Du, Yingge

2017-01-03

With capability for obtaining quantitative elemental composition, chemical and electronic state, and overlayer thickness information from the top ~10 nm of a sample surface, X-ray Photoelectron Spectroscopy (XPS) or Electron Spectroscopy for Chemical Analysis (ESCA) is a versatile and widely used technique for analyzing surfaces. The technique is applied to a host of materials, from insulators to conductors in virtually every scientific field and sub-discipline. More recently, XPS has been extended under in-situ and operando conditions. Following a brief introduction to XPS principles and instrument components, this article exemplifies widely ranging XPS applications in material and life sciences.

Highly-branched anisotropic hybrid nanoparticles at surfaces.

NASA Astrophysics Data System (ADS)

Tsukruk, Vladimir

2009-03-01

We present a brief overview of our recent studies on combined hybrid anisotropic structures composed of inorganic nanoparticles and highly branched molecules such as modified silsesquioxanes polyhedra cores (POSS) with mixed hydrophobic-hydrophilic tails and silver nanowires with functionalized star block copolymer with embedded gold nanoparticles (nanocobs). We demonstrate two-stage melting of that branched POSS and their ability to form monolayer and multilayered LB structures. On the other hand, we observed that silver-BCP-gold nanocobs display extremely bright Raman scattering caused by surface enhanced Raman effect with very different longitudinal and transversal optical properties as revealed by high-resolution confocal Raman microscopy. To study these hybrid nanostructures we applied combined AFM, SEM, TEM, XPS, SERS, UV-vis, and XR techniques.

Structural and mechanical properties of hydroxyapatite coatings formed by ion-beam assisted deposition

NASA Astrophysics Data System (ADS)

Zykova, A.; Safonov, V.; Dudin, S.; Yakovin, S.; Donkov, N.; Ghaemi, M. H.; Szkodo, M.; Antoszkiewicz, M.; Szyfelbain, M.; Czaban, A.

2018-03-01

The ion-beam assisted deposition (IBAD) is an advanced method capable of producing crystalline coatings at low temperatures. We determined the characteristics of hydroxyapatite Ca10(PO4)6(OH)2 target and coatings formed by IBAD using X-ray photoemission spectroscopy (XPS), X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and energy dispersive X-ray (EDX). The composition of the coatings’ cross-section and surface was close to those of the target. The XPS spectra showed that the binding energy values of Ca (2p1/2, 2p3/2), P (2p3/2), and O 1s levels are related to the hydroxyapatite phase. The coatings demonstrate an optimal H/E ratio, and a good resistance to scratch tests.

Gold core@silver semishell Janus nanoparticles prepared by interfacial etching

NASA Astrophysics Data System (ADS)

Chen, Limei; Deming, Christopher P.; Peng, Yi; Hu, Peiguang; Stofan, Jake; Chen, Shaowei

2016-07-01

Gold core@silver semishell Janus nanoparticles were prepared by chemical etching of Au@Ag core-shell nanoparticles at the air/water interface. Au@Ag core-shell nanoparticles were synthesized by chemical deposition of a silver shell onto gold seed colloids followed by the self-assembly of 1-dodecanethiol onto the nanoparticle surface. The nanoparticles then formed a monolayer on the water surface of a Langmuir-Blodgett trough, and part of the silver shell was selectively etched away by the mixture of hydrogen peroxide and ammonia in the water subphase, where the etching was limited to the side of the nanoparticles that was in direct contact with water. The resulting Janus nanoparticles exhibited an asymmetrical distribution of silver on the surface of the gold cores, as manifested in transmission electron microscopy, UV-vis absorption, and X-ray photoelectron spectroscopy measurements. Interestingly, the Au@Ag semishell Janus nanoparticles exhibited enhanced electrocatalytic activity in oxygen reduction reactions, as compared to their Au@Ag and Ag@Au core-shell counterparts, likely due to a synergistic effect between the gold cores and silver semishells that optimized oxygen binding to the nanoparticle surface.Gold core@silver semishell Janus nanoparticles were prepared by chemical etching of Au@Ag core-shell nanoparticles at the air/water interface. Au@Ag core-shell nanoparticles were synthesized by chemical deposition of a silver shell onto gold seed colloids followed by the self-assembly of 1-dodecanethiol onto the nanoparticle surface. The nanoparticles then formed a monolayer on the water surface of a Langmuir-Blodgett trough, and part of the silver shell was selectively etched away by the mixture of hydrogen peroxide and ammonia in the water subphase, where the etching was limited to the side of the nanoparticles that was in direct contact with water. The resulting Janus nanoparticles exhibited an asymmetrical distribution of silver on the surface of the gold cores, as manifested in transmission electron microscopy, UV-vis absorption, and X-ray photoelectron spectroscopy measurements. Interestingly, the Au@Ag semishell Janus nanoparticles exhibited enhanced electrocatalytic activity in oxygen reduction reactions, as compared to their Au@Ag and Ag@Au core-shell counterparts, likely due to a synergistic effect between the gold cores and silver semishells that optimized oxygen binding to the nanoparticle surface. Electronic supplementary information (ESI) available: Additional TEM, UV-vis, XPS, and electrochemical data. See DOI: 10.1039/c6nr03368g

Versatile technique for assessing thickness of 2D layered materials by XPS

NASA Astrophysics Data System (ADS)

Zemlyanov, Dmitry Y.; Jespersen, Michael; Zakharov, Dmitry N.; Hu, Jianjun; Paul, Rajib; Kumar, Anurag; Pacley, Shanee; Glavin, Nicholas; Saenz, David; Smith, Kyle C.; Fisher, Timothy S.; Voevodin, Andrey A.

2018-03-01

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) and the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Therefore, after XPS analysis, exactly the same sample can undergo further processing or utilization.

Versatile technique for assessing thickness of 2D layered materials by XPS

DOE PAGES

Zemlyanov, Dmitry Y.; Jespersen, Michael; Zakharov, Dmitry N.; ...

2018-02-07

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS 2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) andmore » the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Furthermore, after XPS analysis, exactly the same sample can undergo further processing or utilization.« less

Versatile technique for assessing thickness of 2D layered materials by XPS.

PubMed

Zemlyanov, Dmitry Y; Jespersen, Michael; Zakharov, Dmitry N; Hu, Jianjun; Paul, Rajib; Kumar, Anurag; Pacley, Shanee; Glavin, Nicholas; Saenz, David; Smith, Kyle C; Fisher, Timothy S; Voevodin, Andrey A

2018-03-16

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS 2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) and the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Therefore, after XPS analysis, exactly the same sample can undergo further processing or utilization.

Versatile technique for assessing thickness of 2D layered materials by XPS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zemlyanov, Dmitry Y.; Jespersen, Michael; Zakharov, Dmitry N.

X-ray photoelectron spectroscopy (XPS) has been utilized as a versatile method for thickness characterization of various two-dimensional (2D) films. Accurate thickness can be measured simultaneously while acquiring XPS data for chemical characterization of 2D films having thickness up to approximately 10 nm. For validating the developed technique, thicknesses of few-layer graphene (FLG), MoS 2 and amorphous boron nitride (a-BN) layer, produced by microwave plasma chemical vapor deposition (MPCVD), plasma enhanced chemical vapor deposition (PECVD), and pulsed laser deposition (PLD) respectively, were accurately measured. The intensity ratio between photoemission peaks recorded for the films (C 1s, Mo 3d, B 1s) andmore » the substrates (Cu 2p, Al 2p, Si 2p) is the primary input parameter for thickness calculation, in addition to the atomic densities of the substrate and the film, and the corresponding electron attenuation length (EAL). The XPS data was used with a proposed model for thickness calculations, which was verified by cross-sectional transmission electron microscope (TEM) measurement of thickness for all the films. The XPS method determines thickness values averaged over an analysis area which is orders of magnitude larger than the typical area in cross-sectional TEM imaging, hence provides an advanced approach for thickness measurement over large areas of 2D materials. The study confirms that the versatile XPS method allows rapid and reliable assessment of the 2D material thickness and this method can facilitate in tailoring growth conditions for producing very thin 2D materials effectively over a large area. Furthermore, the XPS measurement for a typical 2D material is non-destructive and does not require special sample preparation. Furthermore, after XPS analysis, exactly the same sample can undergo further processing or utilization.« less

X-ray photoelectron spectroscopy for characterization of wood surfaces in adhesion studies

Treesearch

James F. Beecher; Charles R. Frihart

2005-01-01

X-ray photoelectron spectroscopy (XPS) is one of a set of tools that have been used to characterize wood surfaces. Among the advantages of XPS are surface sensitivity, identification of nearly all elements, and frequently, discrimination of bonding states. For these reasons, XPS seemed to be an appropriate tool to help explain the differences in bond strength under wet...

Interfaces in heterogeneous catalytic reactions: Ambient pressure XPS as a tool to unravel surface chemistry

DOE PAGES

Palomino, Robert M.; Hamlyn, Rebecca; Liu, Zongyuan; ...

2017-04-27

In this paper we provide a summary of the recent development of ambient pressure X-ray photoelectron spectroscopy (AP-XPS) and its application to catalytic surface chemistry. The methodology as well as significant advantages and challenges associated with this novel technique are described. Details about specific examples of using AP-XPS to probe surface chemistry under working reaction conditions for a number of reactions are explained: CO oxidation, water-gas shift (WGS), CO 2 hydrogenation, dry reforming of methane (DRM) and ethanol steam reforming (ESR). In conclusion, we discuss insights into the future development of the AP-XPS technique and its applications.

Interfaces in heterogeneous catalytic reactions: Ambient pressure XPS as a tool to unravel surface chemistry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Palomino, Robert M.; Hamlyn, Rebecca; Liu, Zongyuan

In this paper we provide a summary of the recent development of ambient pressure X-ray photoelectron spectroscopy (AP-XPS) and its application to catalytic surface chemistry. The methodology as well as significant advantages and challenges associated with this novel technique are described. Details about specific examples of using AP-XPS to probe surface chemistry under working reaction conditions for a number of reactions are explained: CO oxidation, water-gas shift (WGS), CO 2 hydrogenation, dry reforming of methane (DRM) and ethanol steam reforming (ESR). In conclusion, we discuss insights into the future development of the AP-XPS technique and its applications.

Electronic structure study of wide band gap magnetic semiconductor (La0.6Pr0.4)0.65Ca0.35MnO3 nanocrystals in paramagnetic and ferromagnetic phases

NASA Astrophysics Data System (ADS)

Dwivedi, G. D.; Joshi, Amish G.; Kumar, Shiv; Chou, H.; Yang, K. S.; Jhong, D. J.; Chan, W. L.; Ghosh, A. K.; Chatterjee, Sandip

2016-04-01

X-ray circular magnetic dichroism (XMCD), X-ray photoemission spectroscopy (XPS), and ultraviolet photoemission spectroscopy (UPS) techniques were used to study the electronic structure of nanocrystalline (La0.6Pr0.4)0.65Ca0.35MnO3 near Fermi-level. XMCD results indicate that Mn3+ and Mn4+ spins are aligned parallel to each other at 20 K. The low M-H hysteresis curve measured at 5 K confirms ferromagnetic ordering in the (La0.6Pr0.4)0.65Ca0.35MnO3 system. The low temperature valence band XPS indicates that coupling between Mn3d and O2p is enhanced and the electronic states near Fermi-level have been suppressed below TC. The valence band UPS also confirms the suppression of electronic states near Fermi-level below Curie temperature. UPS near Fermi-edge shows that the electronic states are almost absent below 0.5 eV (at 300 K) and 1 eV (at 115 K). This absence clearly demonstrates the existence of a wide band-gap in the system since, for hole-doped semiconductors, the Fermi-level resides just above the valence band maximum.

Room-temperature fabrication of core-shell nano-ZnO/pollen grain biocomposite for adsorptive removal of organic dye from water

NASA Astrophysics Data System (ADS)

Tzvetkov, George; Kaneva, Nina; Spassov, Tony

2017-04-01

A new core-shell nano-ZnO/pollen grain (n-ZnO/PG) biocomposite has been successfully synthesized via simple and low-temperature two-step liquid precipitation method. The synthetic strategy consists of grafting the surface of pine pollen grains (PG) with Zn2+-organic complexes followed by a treatment in Zn(CH3COO)2/NaOH solution, thus producing a closed n-ZnO shell around the organic core, with a thickness of ∼450 nm. Scanning electron microscopy, X-ray diffraction, FTIR, XPS and UV-vis spectroscopy measurements along with N2 adsorption/desorption were used to characterize the resulting n-ZnO/PG biocomposite. The as-prepared core-shell microparticles are meso-/macro-porous with BET surface area of 25 m2 g-1 and total pore volume of 0.26 cm3 g-1. The adsorption properties of n-ZnO/PG were evaluated through adsorption of Malachite Green (MG) from aqueous medium at room temperature (25 °C). For the sake of comparison, the physico-chemical and adsorptive properties of the raw PG and pure n-ZnO were also examined. Results indicate that n-ZnO/PG is the most favorable for the adsorption of MG under the conditions used in this study. The adsorption kinetic data for PG, n-ZnO and n-ZnO/PG follow the pseudo-second order equation and the maximum adsorption capacity follows an order of n-ZnO/PG > n-ZnO > PG. For n-ZnO/PG an adsorption uptake up to 145.9 mg g-1 is observed. The as-prepared core-shell biocomposite material is a promising cost-effective and environmentally friendly adsorbent due to its textural properties, surface chemistry, adsorption capacity and recyclability.

Zero-valent iron treatment of dark brown colored coffee effluent: Contributions of a core-shell structure to pollutant removals.

PubMed

Tomizawa, Mayuka; Kurosu, Shunji; Kobayashi, Maki; Kawase, Yoshinori

2016-12-01

The decolorization and total organic carbon (TOC) removal of dark brown colored coffee effluent by zero-valent iron (ZVI) have been systematically examined with solution pH of 3.0, 4.0, 6.0 and 8.0 under oxic and anoxic conditions. The optimal decolorization and TOC removal were obtained at pH 8.0 with oxic condition. The maximum efficiencies of decolorization and TOC removal were 92.6 and 60.2%, respectively. ZVI presented potential properties for pollutant removal at nearly neutral pH because of its core-shell structure in which shell or iron oxide/hydroxide layer on ZVI surface dominated the decolorization and TOC removal of coffee effluent. To elucidate the contribution of the core-shell structure to removals of color and TOC at the optimal condition, the characterization of ZVI surface by scanning electron microscopy (SEM) with an energy dispersive X-ray spectroscope (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) was conducted. It was confirmed that the core-shell structure was formed and the shell on ZVI particulate surface and the precipitates formed during the course of ZVI treatment consisted of iron oxides and hydroxides. They were significantly responsible for decolorization and TOC removal of coffee effluent via adsorption to shell on ZVI surface and inclusion into the precipitates rather than the oxidative degradation by OH radicals and the reduction by emitted electrons. The presence of dissolved oxygen (DO) enhanced the formation of the core-shell structure and as a result improved the efficiency of ZVI treatment for the removal of colored components in coffee effluents. ZVI was found to be an efficient material toward the treatment of coffee effluents. Copyright © 2016 Elsevier Ltd. All rights reserved.

Tunable Stoichiometry of BCxNy Thin Films Through Multitarget Pulsed Laser Deposition Monitored via In Situ Ellipsometry (Postprint)

DTIC Science & Technology

2014-02-05

X - ray photoelectron spectroscopy (XPS), Raman spectroscopy , and atomic ...calculate thickness, n and k. X - ray photoelectron spectroscopy (XPS), Raman spectroscopy , and atomic force microscopy (AFM) were all performed on each of the... X - ray photoelectron spectroscopy (XPS) and Raman spectroscopy were used to measure and compare the composition of the films.6 In this paper,

Electron-spectroscopy and -diffraction study of the conductivity of CVD diamond ( 0 0 1 )2×1 surface

NASA Astrophysics Data System (ADS)

Kono, S.; Takano, T.; Shimomura, M.; Goto, T.; Sato, K.; Abukawa, T.; Tachiki, M.; Kawarada, H.

2003-04-01

A chemical vapor deposition as-grown diamond (0 0 1) single-domain 2 × 1 surface was studied by electron-spectroscopy and electron-diffraction in ultrahigh vacuum (UHV). In order to change the surface conductivity (SC) of the diamond in UHV, three annealing stages were used; without annealing, annealing at 300 °C and annealing at 550 °C. From low energy electron diffraction and X-ray photoelectron spectroscopic (XPS) studies, an existence of SC was suggested for the first two stages of annealing and an absence of SC was suggested for the last stage of annealing. Changes in C KVV Auger electron spectroscopic spectra, C KVV Auger electron diffraction (AED) patterns and C 1s XPS peak positions were noticed between the annealing stages at 300 and 550 °C. These changes are interpreted as such that the state of hydrogen involvement in a subsurface of diamond (0 0 1)2 × 1 changes as SC changes. In particular, the presence of local disorder in diamond configuration in SC subsurface is pointed out from C KVV AED. From C 1s XPS peak shifts, a lower bound for the Fermi-level for SC layers from the valence band top is presented to be ˜0.5 eV.

XPS characterization of silver exchanged ETS-10 and mordenite molecular sieves.

PubMed

Anson, A; Maham, Y; Lin, C C H; Kuznicki, T M; Kuznicki, S M

2009-05-01

Silver exchanged molecular sieves ETS-10 (Ag-ETS-10) and mordenite (Ag-mordenite) were dehydrated under vacuum at temperatures between 100 degrees C-350 degrees C. Changes in the state of the silver were studied using X-ray photoelectron spectroscopy (XPS). Silver cations in titanosilicate Ag-ETS-10 are fully reduced to Ag(0) at temperatures as low as 150 degrees C. The characteristic features of the XPS spectrum of silver in this Ag-ETS-10 species correspond to only metallic silver. The signal for metallic silver is not observed in the XPS spectrum of aluminosilicate Ag-mordenite, indicating that silver cations are not reduced, even after heating to 350 degrees C.

Surface zwitterionicalization of poly(vinylidene fluoride) membranes from the entrapped reactive core-shell silica nanoparticles.

PubMed

Zhu, Li-Jing; Zhu, Li-Ping; Zhang, Pei-Bin; Zhu, Bao-Ku; Xu, You-Yi

2016-04-15

We demonstrate the preparation and properties of poly(vinylidene fluoride) (PVDF) filtration membranes modified via surface zwitterionicalization mediated by reactive core-shell silica nanoparticles (SiO2 NPs). The organic/inorganic hybrid SiO2 NPs grafted with poly(methyl meth acrylate)-block-poly(2-dimethylaminoethyl methacrylate) copolymer (PMMA-b-PDMAEMA) shell were prepared by surface-initiated reversible addition fragmentation chain transfer (SI-RAFT) polymerization and then used as a membrane-making additive of PVDF membranes. The PDMAEMA exposed on membrane surface and pore walls were quaternized into zwitterionic poly(sulfobetaine methacrylate) (PSBMA) using 1,3-propane sultone (1,3-PS) as the quaternization agent. The membrane surface chemistry and morphology were analyzed by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), respectively. The hydrophilicity, permeability and antifouling ability of the investigated membranes were evaluated in detail. It was found that the PSBMA chains brought highly-hydrophilic and strong fouling resistant characteristics to PVDF membranes due to the powerful hydration of zwitterionic surface. The SiO2 cores and PMMA chains in the hybrid NPs play a role of anchors for the linking of PSBMA chains to membrane surface. Compared to the traditional strategies for membrane hydrophilic modification, the developed method in this work combined the advantages of both blending and surface reaction. Copyright © 2016 Elsevier Inc. All rights reserved.

A novel IrNi@PdIr/C core-shell electrocatalyst with enhanced activity and durability for the hydrogen oxidation reaction in alkaline anion exchange membrane fuel cells.

PubMed

Qin, Bowen; Yu, Hongmei; Jia, Jia; Jun, Chi; Gao, Xueqiang; Yao, Dewei; Sun, Xinye; Song, Wei; Yi, Baolian; Shao, Zhigang

2018-03-08

Herein, a novel non-platinum core-shell catalyst, namely, IrNi@PdIr/C was prepared via a galvanic replacement reaction; it exhibits enhanced hydrogen oxidation activity and excellent stability under alkaline conditions. Electrochemical experiments demonstrated that the mass and specific activities at 50 mV of IrNi@PdIr/C are 2.1 and 2.2 times that of commercial Pt/C in 0.1 M KOH at 298 K, respectively. Moreover, accelerated degradation tests have shown that the electrochemically active surface area (ECSA) of IrNi@PdIr/C reduces by only 5.1%, which is almost 4 times less than that of commercial Pt/C and the mass activity at 50 mV of IrNi@PdIr/C after 2000 potential cycles is still 1.8 times higher than that of aged Pt/C. XRD and XPS analysis suggest that the enhanced HOR activity is attributed to the weakening of the hydrogen binding to the PdIr overlayers induced by the IrNi core. The better stability to potential cycling can be associated with the PdIr shell, which inhibits oxide formation. These results suggest that IrNi@PdIr/C is a promising non-platinum anode catalyst for alkaline anion exchange membrane fuel cells.

Multicenter study on costs associated with two surgical procedures: GreenLight XPS 180 W versus the gold standard transurethral resection of the prostate.

PubMed

Benejam-Gual, J M; Sanz-Granda, A; Budía, A; Extramiana, J; Capitán, C

2014-01-01

To analyze the costs associated with two surgical procedures for lower urinary tract symptoms secondary to benign prostatic hyperplasia: GreenLight XPS 180¦W versus the gold standard transurethral resection of the prostate. A multicenter, retrospective cost study was carried out from the National Health Service perspective, over a 3-month time period. Costs were broken down into pre-surgical, surgical and post-surgical phases. Data were extracted from records of patients operated sequentially, with IPSS=15, Qmax=15 mL/seg and a prostate volume of 40-80mL, adding only direct healthcare costs (€, 2013) associated with the procedure and management of complications. A total of 79 patients sequentially underwent GL XPS (n: 39) or TURP (n: 40) between July and October, 2013. Clinical outcomes were similar (94.9% and 92.5%, GL XPS and TURP, respectively) without significant differences (P=.67). The average direct cost per patient was reduced by €114 in GL XPS versus TURP patients; the cost was higher in the surgical phase with GL XPS (difference: €1,209; P<.001) but was lower in the post-surgical phase (difference: €-1,351; P<.001). The GreenLight XPS 180-W laser system is associated with a reduction in costs with respect to transurethral resection of prostate in the surgical treatment of LUTS secondary to PBH. This reduction is due to a shorter inpatient length of stay that offsets the cost of the new technology. Copyright © 2013 AEU. Published by Elsevier Espana. All rights reserved.

Nanoscale zero-valent iron (nZVI): aspects of the core-shell structure and reactions with inorganic species in water.

PubMed

Yan, Weile; Herzing, Andrew A; Kiely, Christopher J; Zhang, Wei-Xian

2010-11-25

Aspects of the core-shell model of nanoscale zero-valent iron (nZVI) and their environmental implications were examined in this work. The structure and elemental distribution of nZVI were characterized by X-ray energy-dispersive spectroscopy (XEDS) with nanometer-scale spatial resolution in an aberration-corrected scanning transmission electron microscope (STEM). The analysis provides unequivocal evidence of a layered structure of nZVI consisting of a metallic iron core encapsulated by a thin amorphous oxide shell. Three aqueous environmental contaminants, namely Hg(II), Zn(II) and hydrogen sulfide, were studied to probe the reactive properties and the surface chemistry of nZVI. High-resolution X-ray photoelectron spectroscopy (HR-XPS) analysis of the reacted particles indicated that Hg(II) was sequestrated via chemical reduction to elemental mercury. On the other hand, Zn(II) removal was achieved via sorption to the iron oxide shell followed by zinc hydroxide precipitation. Hydrogen sulfide was immobilized on the nZVI surface as disulfide (S(2)(2-)) and monosulfide (S(2-)) species. Their relative abundance in the final products suggests that the retention of hydrogen sulfide occurs via reactions with the oxide shell to form iron sulfide (FeS) and subsequent conversion to iron disulfide (FeS(2)). The results presented herein highlight the multiple reactive pathways permissible with nZVI owing to its two functional constituents. The core-shell structure imparts nZVI with manifold functional properties previously unexamined and grants the material with potentially new applications. Copyright © 2010 Elsevier B.V. All rights reserved.

A New Observation of the Quiet Sun Soft X-ray (0.5-5 keV) Spectrum

NASA Astrophysics Data System (ADS)

Caspi, A.; Woods, T. N.; Stone, J.

2012-12-01

The solar corona is the brightest source of X-rays in the solar system, and the X-ray emission is highly variable with solar activity. While this is particularly true during solar flares, when emission can be enhanced by many orders of magnitude up to gamma-ray energies, even the so-called "quiet Sun" is bright in soft X-rays (SXRs), as the ~1-2 MK ambient plasma of the corona emits significant thermal bremsstrahlung up to ~5 keV. However, the actual solar SXR (0.5-5 keV) spectrum is not well known, particularly during quiet periods, as, with few exceptions, this energy range has not been systematically studied in many years. Previous observations include ultra-high-resolution but very narrow-band spectra from crystral spectrometers (e.g. Yohkoh/BCS), or integrated broadband irradiances from photometers (e.g. GOES/XRS, TIMED/XPS, etc.) that lack detailed spectral information. In recent years, broadband measurements with fair energy resolution (~0.5-0.7 keV FWHM) were made by SphinX on CORONAS-Photon and XRS on MESSENGER, although they did not extend below ~1 keV. We present observations of the quiet Sun SXR emission obtained using a new SXR spectrometer flown on the third SDO/EVE underflight calibration rocket (NASA 36.286). The commercial off-the-shelf Amptek X123 silicon drift detector, with an 8-micron Be window and custom aperture, measured the solar SXR emission from ~0.5 to >10 keV with ~0.15 keV FWHM resolution (though, due to hardware limitations, with only ~0.12 keV binning) and 2-sec cadence over ~5 minutes on 23 June 2012. Despite the rising solar cycle, activity on 23 June 2012 was abnormally low, with no visible active regions and GOES XRS emission near 2010 levels; we measured no solar counts above ~4 keV during the observation period. We compare our X123 measurements with spectra and broadband irradiances from other instruments, including the SphinX observations during the deep solar minimum of 2009, and with upper limits of >3 keV quiet Sun emission determined from RHESSI. We discuss the possible implications for X-ray-producing physical processes in the quiescent, active-region-free corona. The X123 spectrum could potentially serve as a reference for ~0.5-4 keV quiet Sun emission, to help improve solar spectral models such as CHIANTI and XPS Level 4. Our comparisons indicate that XPS Level 4 likely requires significant revisions in the SXR range, which may have downstream implications for the Earth ionosphere models that have used XPS Level 4 as their solar input.

A New Observation of the Quiet Sun Soft X-ray (0.5-5 keV) Spectrum

NASA Astrophysics Data System (ADS)

Caspi, Amir; Woods, Thomas N.; Stone, Jordan

2013-03-01

The solar corona is the brightest source of X-rays in the solar system, and the X-ray emission is highly variable with solar activity. While this is particularly true during solar flares, when emission can be enhanced by many orders of magnitude up to gamma-ray energies, even the so-called "quiet Sun" is bright in soft X-rays (SXRs), as the 1-2 MK ambient plasma of the corona emits significant thermal bremsstrahlung up to 5 keV. However, the actual solar SXR (0.5-5 keV) spectrum is not well known, particularly during quiet periods, as, with few exceptions, this energy range has not been systematically studied in many years. Previous observations include ultra-high-resolution but very narrow-band spectra from crystral spectrometers (e.g. Yohkoh/BCS), or integrated broadband irradiances from photometers (e.g. GOES/XRS, TIMED/XPS, etc.) that lack detailed spectral information. In recent years, broadband measurements with fair energy resolution ( 0.5-0.7 keV FWHM) were made by SphinX on CORONAS-Photon and XRS on MESSENGER, although they did not extend below 1 keV. We present observations of the quiet Sun SXR emission obtained using a new SXR spectrometer flown on the third SDO/EVE underflight calibration rocket (NASA 36.286). The commercial off-the-shelf Amptek X123 silicon drift detector, with an 8-micron Be window and custom aperture, measured the solar SXR emission from 0.5 to >10 keV with 0.15 keV FWHM resolution (though, due to hardware limitations, with only 0.12 keV binning) and 2-sec cadence over 5 minutes on 23 June 2012. Despite the rising solar cycle, activity on 23 June 2012 was abnormally low, with no visible active regions and GOES XRS emission near 2010 levels; we measured no solar counts above 4 keV during the observation period. We compare our X123 measurements with spectra and broadband irradiances from other instruments, including the SphinX observations during the deep solar minimum of 2009, and with upper limits of >3 keV quiet Sun emission determined from RHESSI. We discuss the possible implications for X-ray-producing physical processes in the quiescent, active-region-free corona. The X123 spectrum could potentially serve as a reference for 0.5-4 keV quiet Sun emission, to help improve solar spectral models such as CHIANTI and XPS Level 4. Our comparisons indicate that XPS Level 4 likely requires significant revisions in the SXR range, which may have downstream implications for the Earth ionosphere models that have used XPS Level 4 as their solar input.

Efficient solar light-driven degradation of Congo red with novel Cu-loaded Fe3O4@TiO2 nanoparticles.

PubMed

Arora, Priya; Fermah, Alisha; Rajput, Jaspreet Kaur; Singh, Harminder; Badhan, Jigyasa

2017-08-01

In this work, Cu-loaded Fe 3 O 4 @TiO 2 core shell nanoparticles were prepared in a single pot by coating of TiO 2 on Fe 3 O 4 nanoparticles followed by Cu loading. X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM), thermogravimetric analysis (TGA), Brunauer-Emmett- Teller (BET), vibrating sample magnetometry (VSM), X-ray photoelectron spectroscopy (XPS), and valence band X-ray photoelectron spectroscopy (VB XPS) techniques were used for characterization of as prepared nanoparticles. Synergism between copper and titania was evaluated by studying the solar light-driven photodegradation of Congo red dye solution in the presence of Fe 3 O 4 @TiO 2 nanoparticles on one side and Cu-loaded Fe 3 O 4 @TiO 2 nanoparticles on the other side. The latter performed better than the former catalyst, indicating the enhanced activity of copper-loaded catalyst. Further photodegradation was studied by three means, i.e., under ultraviolet (UV), refluxing, and solar radiations. Cu-loaded Fe 3 O 4 @TiO 2 enhanced the degradation efficiency of Congo red dye. Thus, Cu act possibly by reducing the band gap of TiO 2 and widening the optical response of semiconductor, as a result of which solar light could be used to carry out photocatalysis. Graphical abstract Photodegradation of congo red over Cu-loaded Fe 3 O 4 @TiO 2 nanoparticles.

Rapid Aluminum Nanoparticle Production by Milling in NH₃ and CH₃NH₂ Atmospheres: An Experimental and Theoretical Study.

PubMed

McMahon, Brandon W; Yu, Jiang; Boatz, Jerry A; Anderson, Scott L

2015-07-29

Ball milling of aluminum in gaseous atmospheres of ammonia and monomethylamine (MMA) was found to produce particles in the 100 nm size range with high efficiency. A combination of mass spectrometry, X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis with mass spectrometric product analysis (TGA-MS), scanning electron microscopy (SEM), infrared spectroscopy, and dynamic light scattering (DLS) was used to study the particles and the chemical interactions responsible for particle production. To help understand the nature of the surface chemistry, high level quantum chemical calculations were performed to predict the structures and energetics for binding and reactions of NH3 and MMA on aluminum surfaces. Both NH3 and MMA react with aluminum under milling conditions, producing H2 and other gaseous products, and leaving the surfaces functionalized. The surface functionalization enhances size reduction by reducing the surface free energy and the tendency toward mechanochemical welding. For both NH3 and MMA, the particle cores are metallic aluminum, but the surface chemical properties are quite different. The ammonia-milled particles are capped by an AlNxOyHz layer ∼10 nm thick, which passivates the particles. The MMA-milled particles are capped with a thinner passivating layer, such that they are pyrophoric in air and react with N2 at elevated temperatures.

Surface Modification of Polyimide for Improving Adhesion Strength by Inductively Coupled Plasma

NASA Astrophysics Data System (ADS)

Byun, Tae Joon; Kim, Sung Il; Kim, Youn Joon; Choi, Yoon Suk; Choi, In Sik; Setsuhara, Yuichi; Geon Han, Jeon

2009-08-01

This study examined the effect of an inductively coupled plasma (ICP) treatment using an argon and helium gas mixture on the adhesion between polyimide and a copper film. Optical emission spectroscopy (OES) of the ICP revealed the emission intensity of helium and argon at various intensities with the helium mixing ratio. The treated polyimide surface was analyzed using a contact angle analyzer, Atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). The contact angle and RMS roughness ranged from 66 to 31° and 2.3 to 4.1 nm, respectively. XPS showed an increase in C-O bonding. The highest peel strength was 0.43 kgf/cm at a 40% of helium mixing ratio, which contained the highest level of activate species. Overall, an ICP treatment of a polyimide surface with a 40% helium gas mixture improves the adhesion strength between copper and polyimide significantly.

Naval Arctic Research Laboratory (NARL) Subsurface Containment Berm Investigation

DTIC Science & Technology

2015-10-01

Southwest UTM Universal Transverse Mercator XPS Extruded Polystyrene WGS World Geodetic System ERDC/CRREL TR-15-15 1 1 Introduction In 1996, under...layers of extruded polystyrene (XPS) board insula- tion at approximately 1.0 m below the ground surface for the length of the berm. The XPS was...ply- wood installed during the trench construction. We attempted probing in Dew Line Road and in the area adjacent to the Navy Hangar and Treat- ment

XPS and bioactivity study of the bisphosphonate pamidronate adsorbed onto plasma sprayed hydroxyapatite coatings

NASA Astrophysics Data System (ADS)

McLeod, Kate; Kumar, Sunil; Smart, Roger St. C.; Dutta, Naba; Voelcker, Nicolas H.; Anderson, Gail I.; Sekel, Ron

2006-12-01

This paper reports the use of X-ray photoelectron spectroscopy (XPS) to investigate bisphosphonate (BP) adsorption onto plasma sprayed hydroxyapatite (HA) coatings commonly used for orthopaedic implants. BPs exhibit high binding affinity for the calcium present in HA and hence can be adsorbed onto HA-coated implants to exploit their beneficial properties for improved bone growth at the implant interface. A rigorous XPS analysis of pamidronate, a commonly used nitrogenous BP, adsorbed onto plasma sprayed HA-coated cobalt-chromium substrates has been carried out, aimed at: (a) confirming the adsorption of this BP onto HA; (b) studying the BP diffusion profile in the HA coating by employing the technique of XPS depth profiling; (c) confirming the bioactivity of the adsorbed BP. XPS spectra of plasma sprayed HA-coated discs exposed to a 10 mM aqueous BP solution (pamidronate) for periods of 1, 2 and 24 h showed nitrogen and phosphorous photoelectron signals corresponding to the BP, confirming its adsorption onto the HA substrate. XPS depth profiling of the 2 h BP-exposed HA discs showed penetration of the BP into the HA matrix to depths of at least 260 nm. The bioactivity of the adsorbed BP was confirmed by the observed inhibition of osteoclast (bone resorbing) cell activity. In comparison to the HA sample, the HA sample with adsorbed BP exhibited a 25-fold decrease in primary osteoclast cells.

The Gaussian-Lorentzian Sum, Product, and Convolution (Voigt) functions in the context of peak fitting X-ray photoelectron spectroscopy (XPS) narrow scans

NASA Astrophysics Data System (ADS)

Jain, Varun; Biesinger, Mark C.; Linford, Matthew R.

2018-07-01

X-ray photoelectron spectroscopy (XPS) is arguably the most important vacuum technique for surface chemical analysis, and peak fitting is an indispensable part of XPS data analysis. Functions that have been widely explored and used in XPS peak fitting include the Gaussian, Lorentzian, Gaussian-Lorentzian sum (GLS), Gaussian-Lorentzian product (GLP), and Voigt functions, where the Voigt function is a convolution of a Gaussian and a Lorentzian function. In this article we discuss these functions from a graphical perspective. Arguments based on convolution and the Central Limit Theorem are made to justify the use of functions that are intermediate between pure Gaussians and pure Lorentzians in XPS peak fitting. Mathematical forms for the GLS and GLP functions are presented with a mixing parameter m. Plots are shown for GLS and GLP functions with mixing parameters ranging from 0 to 1. There are fundamental differences between the GLS and GLP functions. The GLS function better follows the 'wings' of the Lorentzian, while these 'wings' are suppressed in the GLP. That is, these two functions are not interchangeable. The GLS and GLP functions are compared to the Voigt function, where the GLS is shown to be a decent approximation of it. Practically, both the GLS and the GLP functions can be useful for XPS peak fitting. Examples of the uses of these functions are provided herein.

XUV Photometer System (XPS): New Dark-Count Corrections Model and Improved Data Products

NASA Astrophysics Data System (ADS)

Elliott, J. P.; Vanier, B.; Woods, T. N.

2017-12-01

We present newly updated dark-count calibrations for the SORCE XUV Photometer System (XPS) and the resultant improved data products released in March of 2017. The SORCE mission has provided a 14-year solar spectral irradiance record, and the XPS contributes to this record in the 0.1 nm to 40 nm range. The SORCE spacecraft has been operating in what is known as Day-Only Operations (DO-Op) mode since February of 2014. In this mode it is not possible to collect data, including dark-counts, when the spacecraft is in eclipse as we did prior to DO-Op. Instead, we take advantage of the position of the XPS filter-wheel, and collect these data when the wheel position is in a "dark" position. Further, in this mode dark data are not always available for all observations, requiring an extrapolation in order to calibrate data at these times. To extrapolate, we model this with a piece-wise 2D nonlinear least squares surface fit in the time and temperature dimensions. Our model allows us to calibrate XPS data into the DO-Op phase of the mission by extrapolating along this surface. The XPS version 11 data product release benefits from this new calibration. We present comparisons of the previous and current calibration methods in addition to planned future upgrades of our data products.

XPS and EELS characterization of Mn2SiO4, MnSiO3 and MnAl2O4

NASA Astrophysics Data System (ADS)

Grosvenor, A. P.; Bellhouse, E. M.; Korinek, A.; Bugnet, M.; McDermid, J. R.

2016-08-01

X-ray Photoelectron Spectroscopy (XPS) and Electron Energy Loss Spectroscopy (EELS) are strong candidate techniques for characterizing steel surfaces and substrate-coating interfaces when investigating the selective oxidation and reactive wetting of advanced high strength steels (AHSS) during the continuous galvanizing process. However, unambiguous identification of ternary oxides such as Mn2SiO4, MnSiO3, and MnAl2O4 by XPS or EELS, which can play a significant role in substrate reactive wetting, is difficult due to the lack of fully characterized standards in the literature. To resolve this issue, samples of Mn2SiO4, MnSiO3 and MnAl2O4 were synthesized and characterized by XPS and EELS. The unique features of the XPS and EELS spectra for the Mn2SiO4, MnSiO3 and MnAl2O4 standards were successfully derived, thereby allowing investigators to fully differentiate and identify these oxides at the surface and subsurface of Mn, Si and Al alloyed AHSS using these techniques.

Layer uniformity in glucose oxidase immobilization on SiO 2 surfaces

NASA Astrophysics Data System (ADS)

Libertino, Sebania; Scandurra, Antonino; Aiello, Venera; Giannazzo, Filippo; Sinatra, Fulvia; Renis, Marcella; Fichera, Manuela

2007-09-01

The goal of this work was the characterization, step by step, of the enzyme glucose oxidase (GOx) immobilization on silicon oxide surfaces, mainly by means of X-Ray photoelectron spectroscopy (XPS). The immobilization protocol consists of four steps: oxide activation, silanization, linker molecule deposition and GOx immobilization. The linker molecule, glutaraldehyde (GA) in this study, must be able to form a uniform layer on the sample surface in order to maximize the sites available for enzyme bonding and achieve the best enzyme deposition. Using a thin SiO 2 layer grown on Si wafers and following the XPS Si2p signal of the Si substrate during the immobilization steps, we demonstrated both the glutaraldehyde layer uniformity and the possibility to use XPS to monitor thin layer uniformity. In fact, the XPS substrate signal, not shielded by the oxide, is suppressed only when a uniform layer is deposited. The enzyme correct immobilization was monitored using the XPS C1s and N1s signals. Atomic force microscopy (AFM) measurements carried out on the same samples confirmed the results.

Transcription analysis of pilS and xpsEL genes from Xylella fastidiosa.

PubMed

Coltri, Patricia P; Rosato, Yoko B

2005-04-01

Xylella fastidiosa is a xylem-limited phytopathogen responsible for diseases in several plants such as citrus and coffee. Analysis of the bacterial genome revealed some putative pathogenicity-related genes that could help to elucidate the molecular mechanisms of plant-pathogen interactions. In the present work, the transcription of three genes of the bacterium, grown in defined and rich media and also in media containing host plant extracts (sweet orange, 'ponkan' and coffee) was analyzed by RT-PCR. The pilS gene, which encodes a sensor histidine kinase responsible for the biosynthesis of fimbriae, was transcribed when the bacterium was grown in more complex media such as PW and in medium containing plant extracts. The xps genes (xpsL and xpsE) which are related to the type II secretion system were also detected when the bacterium was grown in rich media and media with 'ponkan' and coffee extracts. It was thus observed that pilS and xpsEL genes of X. fastidiosa can be modulated by environmental factors and their expression is dependent on the nutritional status of the growth medium.

Surface Analysis of 4-Aminothiophenol Adsorption at Polycrystalline Platinum Electrodes

NASA Technical Reports Server (NTRS)

Rosario-Castro, Belinda I.; Fachini, Estevao R.; Contes, Enid J.; Perez-Davis, Marla E.; Cabrera, Carlos R.

2008-01-01

Formation of self-assembled monolayer (SAM) of 4-aminothiophenol (4-ATP) on polycrystalline platinum electrodes has been studied by surface analysis and electrochemistry techniques. The 4-ATP monolayer was characterized by cyclic voltammetry (CV), Raman spectroscopy, reflection absorption infrared (RAIR) spectroscopy, and X-ray photoelectron spectroscopy (XPS). Cyclic voltammetry (CV) experiments give an idea about the packing quality of the monolayer. RAIR and Raman spectra for 4-ATP modified platinum electrodes showed the characteristic adsorption bands for neat 4-ATP indicating the adsorption of 4-ATP molecules on platinum surface. The adsorption on platinum was also evidenced by the presence of sulfur and nitrogen peaks by XPS survey spectra of the modified platinum electrodes. High resolution XPS studies and RAIR spectrum for platinum electrodes modified with 4-ATP indicate that molecules are sulfur-bonded to the platinum surface. The formation of S-Pt bond suggests that ATP adsorption gives up an amino terminated SAM. Thickness of the monolayer was evaluated via angle-resolved XPS (AR-XPS) analyses. Derivatization of 4-ATP SAM was performed using 16-Br hexadecanoic acid.

Gas Sensors Based on Tin Oxide Nanoparticles Synthesized from a Mini-Arc Plasma Source

DOE PAGES

Lu, Ganhua; Huebner, Kyle L.; Ocola, Leonidas E.; ...

2006-01-01

Minimore » aturized gas sensors or electronic noses to rapidly detect and differentiate trace amount of chemical agents are extremely attractive. In this paper, we report on the fabrication and characterization of a functional tin oxide nanoparticle gas sensor. Tin oxide nanoparticles are first synthesized using a convenient and low-cost mini-arc plasma source. The nanoparticle size distribution is measured online using a scanning electrical mobility spectrometer (SEMS). The product nanoparticles are analyzed ex-situ by high resolution transmission electron microscopy (HRTEM) for morphology and defects, energy dispersive X-ray (EDX) spectroscopy for elemental composition, electron diffraction for crystal structure, and X-ray photoelectron spectroscopy (XPS) for surface composition. Nonagglomerated rutile tin oxide ( SnO 2 ) nanoparticles as small as a few nm have been produced. Larger particles bear a core-shell structure with a metallic core and an oxide shell. The nanoparticles are then assembled onto an e-beam lithographically patterned interdigitated electrode using electrostatic force to fabricate the gas sensor. The nanoparticle sensor exhibits a fast response and a good sensitivity when exposed to 100 ppm ethanol vapor in air.« less

Hierarchical paramecium-like hollow and solid Au/Pt bimetallic nanostructures constructed using goethite as template

NASA Astrophysics Data System (ADS)

Liu, Wei; Repo, Eveliina; Heikkilä, Mikko; Leskelä, Markku; Sillanpää, Mika

2010-10-01

Novel hollow and solid paramecium-like hierarchical Au/Pt bimetallic nanostructures were constructed using goethite as template via a seed-mediated growth method. Transmission electron microscopy (TEM), ξ-potential measurement, UV-vis spectroscopy, energy dispersive x-ray spectroscopy (EDS), ICP-AES measurement, x-ray powder diffraction (XRD) and x-ray photoelectron spectroscopy (XPS) were utilized to systematically characterize the bimetallic nanostructures. It is found that the core structure of the paramecium-like bimetallic nanomaterial is closely related to reducing agent. When ascorbic acid is used as reducing agent, goethite serves as in situ sacrificed template and hollow paramecium-like bimetallic structure is obtained. When NH2OH·HCl is used, solid nanostructure with preserved goethite core is produced. Heating the reaction solution is necessary to obtain the paramecium-like morphology with rough interconnected Pt cilia shell. The thickness of Pt cilia layer can be controlled by adjusting the molar ratio of H2PtCl6 to Au nanoseeds. The overgrowth of the rough Pt cilia is proposed to be via an autocatalytic and three-dimensional heterogeneous nucleation process first through flower-like morphology. Both the hollow and solid hierarchical paramecium-like Au/Pt bimetallic nanostructures show good catalytic activities.

Hierarchical paramecium-like hollow and solid Au/Pt bimetallic nanostructures constructed using goethite as template.

PubMed

Liu, Wei; Repo, Eveliina; Heikkilä, Mikko; Leskelä, Markku; Sillanpää, Mika

2010-10-01

Novel hollow and solid paramecium-like hierarchical Au/Pt bimetallic nanostructures were constructed using goethite as template via a seed-mediated growth method. Transmission electron microscopy (TEM), xi-potential measurement, UV-vis spectroscopy, energy dispersive x-ray spectroscopy (EDS), ICP-AES measurement, x-ray powder diffraction (XRD) and x-ray photoelectron spectroscopy (XPS) were utilized to systematically characterize the bimetallic nanostructures. It is found that the core structure of the paramecium-like bimetallic nanomaterial is closely related to reducing agent. When ascorbic acid is used as reducing agent, goethite serves as in situ sacrificed template and hollow paramecium-like bimetallic structure is obtained. When NH(2)OH.HCl is used, solid nanostructure with preserved goethite core is produced. Heating the reaction solution is necessary to obtain the paramecium-like morphology with rough interconnected Pt cilia shell. The thickness of Pt cilia layer can be controlled by adjusting the molar ratio of H(2)PtCl(6) to Au nanoseeds. The overgrowth of the rough Pt cilia is proposed to be via an autocatalytic and three-dimensional heterogeneous nucleation process first through flower-like morphology. Both the hollow and solid hierarchical paramecium-like Au/Pt bimetallic nanostructures show good catalytic activities.

Hydrogen peroxide sensing using ultrathin platinum-coated gold nanoparticles with core@shell structure.

PubMed

Li, Yongxin; Lu, Qiufang; Wu, Shengnan; Wang, Lun; Shi, Xianming

2013-03-15

Ultrathin platinum-coated gold (Pt@Au) nanoparticles with core@shell structure have been developed by under-potential deposition (UPD) redox replacement technique. A single UPD Cu replacement with Pt(2+) produced a uniform Pt monolayer on the surface of gold nanoparticles, which are immobilized on glassy carbon electrode (GCE) surface based on electrostatic interaction. The ultrathin Pt@Au nanoparticles were confirmed by cyclic voltammetry and X-ray photoelectron spectroscopy (XPS). Voltammetry and amperometric methodologies were used to evaluate the electrocatalytic activity of the Pt@Au nanoparticles modified electrode towards the reduction of hydrogen peroxide under the physiological condition. The present results show that ultrathin Pt coating greatly enhances the electrocatalytic activity towards the reduction of hydrogen peroxide, which can be utilized to fabricate the hydrogen peroxide sensor. Chronoamperometric experiments showed that at an applied potential of 0.08 V (vs. Ag/AgCl), the current reduction of hydrogen peroxide was linear to its concentration in the range of 1-450 μΜ, and the detection limit was found to be 0.18 μM (signal-to-noise ratio, S/N=3). Copyright © 2012 Elsevier B.V. All rights reserved.

Recovery Act. Advanced Building Insulation by the CO 2 Foaming Process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Arthur

In this project, ISTN proposed to develop a new "3rd" generation of insulation technology. The focus was a cost-effective foaming process that could be used to manufacture XPS and other extruded polymer foams using environmentally clean blowing agents, and ultimately achieve higher R-values than existing products while maintaining the same level of cost-efficiency. In the U.S., state-of-the-art products are primarily manufactured by two companies: Dow and Owens Corning. These products (i.e., STYROFOAM and FOAMULAR) have a starting thermal resistance of R-5.0/inch, which declines over the life of the product as the HFC blowing agents essential to high R-value exchange withmore » air in the environment. In the existing technologies, the substitution of CO2 for HFCs as the primary foaming agent results in a much lower starting R-value, as evidenced in CO2-foamed varieties of XPS in Europe with R-4.2/inch insulation value. The major overarching achievement from this project was ISTN's development of a new process that uses CO2 as a clean blowing agent to achieve up to R-5.2/inch at the manufacturing scale, with a production cost on a per unit basis that is less than the cost of Dow and Owens Corning XPS products.« less

Quantitative analysis of Ni2+/Ni3+ in Li[NixMnyCoz]O2 cathode materials: Non-linear least-squares fitting of XPS spectra

NASA Astrophysics Data System (ADS)

Fu, Zewei; Hu, Juntao; Hu, Wenlong; Yang, Shiyu; Luo, Yunfeng

2018-05-01

Quantitative analysis of Ni2+/Ni3+ using X-ray photoelectron spectroscopy (XPS) is important for evaluating the crystal structure and electrochemical performance of Lithium-nickel-cobalt-manganese oxide (Li[NixMnyCoz]O2, NMC). However, quantitative analysis based on Gaussian/Lorentzian (G/L) peak fitting suffers from the challenges of reproducibility and effectiveness. In this study, the Ni2+ and Ni3+ standard samples and a series of NMC samples with different Ni doping levels were synthesized. The Ni2+/Ni3+ ratios in NMC were quantitatively analyzed by non-linear least-squares fitting (NLLSF). Two Ni 2p overall spectra of synthesized Li [Ni0.33Mn0.33Co0.33]O2(NMC111) and bulk LiNiO2 were used as the Ni2+ and Ni3+ reference standards. Compared to G/L peak fitting, the fitting parameters required no adjustment, meaning that the spectral fitting process was free from operator dependence and the reproducibility was improved. Comparison of residual standard deviation (STD) showed that the fitting quality of NLLSF was superior to that of G/L peaks fitting. Overall, these findings confirmed the reproducibility and effectiveness of the NLLSF method in XPS quantitative analysis of Ni2+/Ni3+ ratio in Li[NixMnyCoz]O2 cathode materials.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ding, Laura; Harvey, Stephen P.; Teeter, Glenn

We demonstrate the potential of X-ray photoelectron spectroscopy (XPS) to characterize new carrier-selective contacts (CSC) for solar cell application. We show that XPS not only provides information about the surface chemical properties of the CSC material, but that operando XPS, i.e. under light bias condition, can also directly measure the photovoltage that develops at the CSC/absorber interface, revealing device relevant information without the need of assembling a full solar cell. We present the application of the technique to molybdenum oxide hole-selective contact films on a crystalline silicon absorber.

Combined PIXE and XPS analysis on republican and imperial Roman coins

NASA Astrophysics Data System (ADS)

Daccà, A.; Prati, P.; Zucchiatti, A.; Lucarelli, F.; Mandò, P. A.; Gemme, G.; Parodi, R.; Pera, R.

2000-03-01

A combined PIXE and XPS analysis has been performed on a few Roman coins of the republican and imperial age. The purpose was to investigate via XPS the nature and extent of patina in order to be capable of extracting PIXE data relative to the coins bulk. The inclusion of elements from the surface layer, altered by oxidation and inclusion, is a known source of uncertainty in PIXE analyses of coins, performed to assess the composition and the provenance.

Composition of RF-sputtered refractory compounds determined by X-ray photoelectron spectroscopy

NASA Technical Reports Server (NTRS)

Wheeler, D. R.; Brainard, W. A.

1978-01-01

RF-sputtered coatings of CrB2, MoSi2, Mo2C, TiC, and MoS2 were examined by X-ray photoelectron spectroscopy (XPS). Data on stoichiometry, impurity content, and chemical bonding were obtained. The influences of sputtering target history, deposition time, RF power level, and substrate bias were studied. Significant deviations from stoichiometry and high oxide levels were related to target outgassing. The effect of substrate bias depended on the particular coating material studied.

Upgrade of the Surface Spectrometer at NEPOMUC for PAES, XPS and STM Investigations

NASA Astrophysics Data System (ADS)

Zimnik, S.; Lippert, F.; Hugenschmidt, C.

2014-04-01

The characterization of the elemental composition of surfaces is of great importance for the understanding of many surface processes, such as surface segregation or oxidation. Positron-annihilation-induced Auger Electron Spectroscopy (PAES) is a powerful technique for gathering information about the elemental composition of only the topmost atomic layer of a sample. The upgraded surface spectrometer at NEPOMUC (NEtron induced POsitron source MUniCh) enables a comprehensive surface analysis with the complementary techniques STM, XPS and PAES. A new X-ray source for X-ray induced photoelectron spectroscopy (XPS) was installed to gather additional information on oxidation states. A new scanning tunneling microscope (STM) is used as a complementary method to investigate with atomic resolution the surface electron density. The combination of PAES, XPS and STM allows the characterization of both the elemental composition, and the surface topology.

Progress in the synthesis and characterization of magnetite nanoparticles with amino groups on the surface

NASA Astrophysics Data System (ADS)

Durdureanu-Angheluta, A.; Dascalu, A.; Fifere, A.; Coroaba, A.; Pricop, L.; Chiriac, H.; Tura, V.; Pinteala, M.; Simionescu, B. C.

2012-05-01

This manuscript deals with the synthesis of new hydrophilic magnetite particles by employing a two-step method: in the first step magnetite particles with hydrophobic shell formed in presence of oleic acid-oleylamine complex through a synthesis in mass, without solvent, in a mortar with pestle were obtained; while in the second step the hydrophobic shell was interchanged with an aminosilane monomer. The influence of the Fe2+/Fe3+ molar ratio on the dimension of the particles of high importance for their potential applications was carefully investigated. This paper, also presents an alternative method of synthesis of new core-shell magnetite particles and the complete study of their structure and morphology by FT-IR, XPS, TGA, ESEM and TEM techniques. The rheological properties and magnetization analysis of high importance for magnetic particles were also investigated.

Investigation of structural, morphological, luminescent and thermal properties of combusted aluminium-based iron oxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shinde, S.S.; Rajpure, K.Y., E-mail: rajpure@yahoo.co

Nanocomposites of aluminium integrated hematite {alpha}-Fe{sub 2}O{sub 3} are synthesized by combustion route using aqueous solutions of AR grade ferric trichloride and aluminium nitrate as precursors. The influence of aluminium incorporation on to the morphology, XPS, photoluminescence and thermal properties has been investigated. The FESEM and AFM micrographs depict that the samples are compact and have homogeneously distributed grains of varying sizes ({approx}20-60 nm). Chemical composition and valence states of constituent elements in hematite are analyzed by XPS. In room temperature photoluminescence (PL) study, we observed strong violet emission around 436 nm without any deep-level emission and a small PLmore » FWHM indicating that the concentrations of defects are responsible for deep-level emissions. The specific heat and thermal conductivity study shows the phonon conduction behavior is dominant. We studied interparticle interactions using complex impedance spectroscopy. We report a new potential candidate for its possible applications in optoelectronics and magnetic devices. -- Graphical abstract: Frequency and temperature dependent interparticle interactions like grains, grain boundary effects using complex impedance spectroscopy of pure and 10 at% Al:Fe{sub 2}O{sub 3} have been studied. Display Omitted« less

The shift of optical band gap in W-doped ZnO with oxygen pressure and doping level

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chu, J.; Chongqing Institute of Green and Intelligent Technology, Chinese Academy of Science, Chongqing 400714; Peng, X.Y.

2014-06-01

Highlights: • CVD–PLD co-deposition technique was used. • Better crystalline of the ZnO samples causes the redshift of the optical band gap. • Higher W concentration induces blueshift of the optical band gap. - Abstract: Tungsten-doped (W-doped) zinc oxide (ZnO) nanostructures were synthesized on quartz substrates by pulsed laser and hot filament chemical vapor co-deposition technique under different oxygen pressures and doping levels. We studied in detail the morphological, structural and optical properties of W-doped ZnO by SEM, XPS, Raman scattering, and optical transmission spectra. A close correlation among the oxygen pressure, morphology, W concentrations and the variation of bandmore » gaps were investigated. XPS and Raman measurements show that the sample grown under the oxygen pressure of 2.7 Pa has the maximum tungsten concentration and best crystalline structure, which induces the redshift of the optical band gap. The effect of W concentration on the change of morphology and shift of optical band gap was also studied for the samples grown under the fixed oxygen pressure of 2.7 Pa.« less

Syntheses and applications of manganese-doped II-VI semiconductor nanocrystals

NASA Astrophysics Data System (ADS)

Yang, Heesun

Syntheses, characterizations, and applications of two different Mn-doped semiconductor nanocrystals, ZnS:Mn and CdS:Mn/ZnS core/shell, were investigated. ZnS:Mn nanocrystals with sizes between 3 and 4 nm were synthesized via a competitive reaction chemistry. A direct current (dc) electroluminescent (EL) device having a hybrid organic/inorganic multilayer structure of an indium tin oxide (ITO) transparent conducting electrode, a (poly(3,4-ethylenedioxythiophene)/poly(styrenesulfonate) (PEDOT-PSS) and a poly(N-vinylcarbazole) (PVK) bilayer hole transport film, a ZnS:Mn nanocrystal layer, and Al dot contacts was demonstrated to emit blue (˜445 and ˜495 nm) from PVK and yellow (˜600 nm) light from Mn activator in ZnS. The EL emission spectrum was dependent upon both the voltage and Mn concentration, showing a decreasing nanocrystal to PVK emission ratio from 10 at 20 V to 4 at 28 V, and an increasing ratio from 1.3 at 0.40 mol % to 4.3 at 2.14 mol %. Mn-doped CdS core nanocrystals were produced ranging from 1.5 to 2.3 nm in diameter with a ZnS shell via a reverse micelle process. In contrast to CdS:Mn nanocrystals passivated by n-dodecanethiol, ZnS-passivated CdS:Mn (CdS:Mn/ZnS core/shell) nanocrystals were efficient and photostable. CdS:Mn/ZnS core/shell nanocrystals exhibited a quantum yield of ˜18%, and the photoluminescence (PL) intensity increased by 40% after 400 nm UV irradiation in air. X-ray photoelectron spectroscopy (XPS) data showed that UV irradiation of CdS:Mn/ZnS nanocrystals induces the photooxidation of the ZnS shell surface to ZnSO4. This photooxidation product is presumably responsible for the increased PL emission by serving as a passivating surface layer. Luminescent lifetime data from the core/shell nanocrystals could be fit with two exponential functions, with a time constant of ˜170 nsec for the defect-related centers and of ˜1 msec for the Mn centers. The CdS:Mn/ZnS nanocrystals with a core crystal diameter of 2.3 nm and a 0.4 nm thick ZnS shell were used as an electroluminescent material. EL devices were tested having a hybrid organic/inorganic multilayer structure of ITO//PEDOT-PSS//conjugated polymer//CdS:Mn/ZnS nanocrystal//Al. Orange from PVK device and green EL emission from poly(p-phenylene vinylene) (PPV) device were observed, respectively. These observations are shown to be consistent with the energy level diagrams of the EL devices. The CdS:Mn/ZnS core/shell quantum dots are not water-soluble because of their hydrophobicity. Silica-overcoated CdS:Mn/ZnS quantum dots were synthesized to create water-soluble quantum dots. The amorphous and porous silica layer did not significantly modify the optical and photophysical properties of CdS:Mn/ZnS quantum dots.

Surface analysis characterisation of gum binders used in modern watercolour paints

NASA Astrophysics Data System (ADS)

Sano, Naoko; Cumpson, Peter J.

2016-02-01

Conducting this study has demonstrated that not only SEM-EDX but also XPS can be an efficient tool for characterising watercolour paint surfaces. We find that surface effects are mediated by water. Once the powdered components in the watercolour come into contact with water they dramatically transform their chemical structures at the surface and show the presence of pigment components with a random dispersion within the gum layer. Hence the topmost surface of the paint is confirmed as being composed of the gum binder components. This result is difficult to confirm using just one analytical technique (either XPS or SEM-EDX). In addition, peak fitting of C1s XPS spectra suggests that the gum binder in the commercial watercolour paints is probably gum arabic (by comparison with the reference materials). This identification is not conclusive, but the combination techniques of XPS and SEM shows the surface structure with material distribution of the gum binder and the other ingredients of the watercolour paints. Therefore as a unique technique, XPS combined with SEM-EDX may prove a useful method in the study of surface structure for not only watercolour objects but also other art objects; which may in future help in the conservation for art.

13C NMR and XPS characterization of anion adsorbent with quaternary ammonium groups prepared from rice straw, corn stalk and sugarcane bagasse

NASA Astrophysics Data System (ADS)

Cao, Wei; Wang, Zhenqian; Zeng, Qingling; Shen, Chunhua

2016-12-01

Despite amino groups modified crop straw has been intensively studied as new and low-cost adsorbent for removal of anionic species from water, there is still a lack of clear characterization for amino groups, especially quaternary ammonium groups in the surface of crop straw. In this study, we used 13C NMR and XPS technologies to characterize adsorbents with quaternary ammonium groups prepared from rice straw, corn stalk and sugarcane bagasse. 13C NMR spectra clearly showed the presence of quaternary ammonium groups in lignocelluloses structure of modified crop straw. The increase of nitrogen observed in XPS survey spectra also indicated the existence of quaternary ammonium group in the surface of the adsorbents. The curve fitting of high-resolution XPS N1s and C1s spectra were conducted to probe the composition of nitrogen and carbon contained groups, respectively. The results showed the proportion of quaternary ammonium group significantly increased in the prepared adsorbent's surface that was dominated by methyl/methylene, hydroxyl, quaternary ammonium, ether and carbonyl groups. This study proved that 13C NMR and XPS could be successfully utilized for characterization of quaternary ammonium modified crop straw adsorbents.

Preparation, characterization, and infrared emissivity property of optically active polyurethane/TiO{sub 2}/SiO{sub 2} multilayered microspheres

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang Yong; Zhou Yuming, E-mail: ymzhou@seu.edu.cn; Ge Jianhua

Optically active polyurethane/titania/silica (LPU/TiO{sub 2}/SiO{sub 2}) multilayered core-shell composite microspheres were prepared by the combination of titania deposition on the surface of silica spheres and subsequent polymer grafting. LPU/TiO{sub 2}/SiO{sub 2} was characterized by FT-IR, UV-vis spectroscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), thermogravimetric analysis (TGA), SEM and TEM, and the infrared emissivity value (8-14 {mu}m) was investigated in addition. The results indicated that titania and polyurethane had been successfully coated onto the surfaces of silica microspheres. LPU/TiO{sub 2}/SiO{sub 2} exhibited clearly multilayered core-shell construction. The infrared emissivity values reduced along with the increase of covering layers thus provedmore » that the interfacial interactions had direct influence on the infrared emissivity. Besides, LPU/TiO{sub 2}/SiO{sub 2} multilayered microspheres based on the optically active polyurethane took advantages of the orderly secondary structure and strengthened interfacial synergistic actions. Consequently, it possessed the lowest infrared emissivity value. - Graphical Abstract: Optically active polyurethane/titania/silica (LPU/TiO{sub 2}/SiO{sub 2}) multilayered core-shell composite microspheres were prepared by the combination of titania deposition on the surface of silica spheres and subsequent polymer grafting. Highlights: > Optically active polyurethane based on tyrosine was used for the modification of nanoparticles. > LPU/TiO{sub 2}/SiO{sub 2} multilayered core-shell microspheres were prepared and characterized. > Interfacial interactions and secondary structure affected the infrared emissivity of composite.« less

Improvement of energy conversion efficiency and power generation in direct borohydride-hydrogen peroxide fuel cell: The effect of Ni-M core-shell nanoparticles (M = Pt, Pd, Ru)/Multiwalled Carbon Nanotubes on the cell performance

NASA Astrophysics Data System (ADS)

Hosseini, M. G.; Mahmoodi, R.

2017-12-01

In this study, core@shell nanoparticles with Ni as a core material and Pt, Pd and Ru as shell materials are synthesized on multiwalled carbon nanotube (MWCNT) as catalyst support using the sequence reduction method. The influence of Ni@Pt, Ni@Pd and Ni@Ru core@shell nanoparticles on MWCNT toward borohydride oxidation in alkaline solution is investigated by various three-electrode electrochemical techniques. Also, the impact of these anodic electrocatalysts on the performance of direct borohydride-hydrogen peroxide fuel cell (DBHPFC) is evaluated. The structural and morphological properties of electrocatalysts are studied by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy-dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM) and X-ray photoelectron spectroscopy (XPS). The results of three electrode investigations show that Ni@Pd/MWCNT has excellent catalytic activity since borohydride oxidation current density on Ni@Pd/MWCNT (34773.27 A g-1) is 1.37 and 9.19 times higher than those of Ni@Pt/MWCNT (25347.27 A g-1) and Ni@Ru/MWCNT (3782.83 A g-1), respectively. Also, the energy conversion efficiency and power density of DBHPFC with Ni@Pd/MWCNT (246.82 mW cm-2) increase to 34.27% and 51.53% respect to Ni@Pt/MWCNT (162.24 mW cm-2) and Ni@Ru/MWCNT (119.62 mW cm-2), respectively. This study reveals that Ni@Pd/MWCNT has highest activity toward borohydride oxidation and stability in fuel cell.

Free-standing and flexible graphene papers as disposable non-enzymatic electrochemical sensors.

PubMed

Zhang, Minwei; Halder, Arnab; Hou, Chengyi; Ulstrup, Jens; Chi, Qijin

2016-06-01

We have explored AuNPs (13 nm) both as a catalyst and as a core for synthesizing water-dispersible and highly stable core-shell structural gold@Prussian blue (Au@PB) nanoparticles (NPs). Systematic characterization by transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) disclosed AuNPs coated uniformly by a 5 nm thick PB layer. Au@PB NPs were attached to single-layer graphene oxide (GO) to form Au@PB decorated GO sheets. The resulting hybrid material was filtered layer-by-layer into flexible and free-standing GO paper, which was further converted into conductive reduced GO (RGO)/Au@PB paper via hydrazine vapour reduction. High-resolution TEM images suggested that RGO papers are multiply sandwich-like structures functionalized with core-shell NPs. Resulting sandwich functionalized graphene papers have high conductivity, sufficient flexibility, and robust mechanical strength, which can be cut into free-standing electrodes. Such electrodes, used as non-enzymatic electrochemical sensors, were tested systematically for electrocatalytic sensing of hydrogen peroxide. The high performance was indicated by some of the key parameters, for example the linear H2O2 concentration response range (1-30 μM), the detection limit (100 nM), and the high amperometric sensitivity (5 A cm(-2) M(-1)). With the advantages of low cost and scalable production capacity, such graphene supported functional papers are of particular interest in the use as flexible disposable sensors. Copyright © 2016 Elsevier B.V. All rights reserved.

Mo-doped V2O5 hierarchical nanorod/nanoparticle core/shell porous microspheres with improved performance for cathode of lithium-ion battery

NASA Astrophysics Data System (ADS)

Yu, Haolin; Zeng, Jianyun; Hao, Wen; Zhou, Peng; Wen, Xiaogang

2018-05-01

Mo-doped V2O5 hierarchical nanorod/nanoparticle core/shell porous microspheres (MVHPMs) were prepared via a simple hydrothermal approach using ammonium metavanadate and ammonium molybdate as precursors followed by a thermal annealing process. The samples were characterized by XRD, SEM, TEM, EDS, and XPS carefully; it confirmed that porous microspheres with uniform Mo doping in the V2O5 matrix were obtained, and it contains an inner core self-assembled with 1D nanorods and outer shell consisting of nanoparticles. A plausible growth mechanism of Mo-doped V2O5 (Mo-V2O5) porous microspheres is suggested. The unique microstructure made the Mo-V2O5 hierarchical microspheres a good cathode material for Li-ion battery. The results indicate the synthesized Mo-V2O5 hierarchical microspheres exhibit well-improved electrochemical performance compared to the undoped samples. It delivers a high initial reversible capacity of 282 mAh g-1 at 0.2 C, 208 mAh g-1 at 2 C, and 111 mAh g-1 at 10 C, and it also exhibits good cycling stabilities; a capacity of 144 mAh g-1 is obtained after 200 cycles at 6 C with a capacity retention of > 82%, which is much high than that of pure V2O5 (95 mAh g-1 with a capacity retention of 72%). [Figure not available: see fulltext.

X-ray Photoelectron Spectroscopy study of CaV1-xMoxO3-δ

NASA Astrophysics Data System (ADS)

Belyakov, S. A.; Kuznetsov, M. V.; Shkerin, S. N.

2018-06-01

An investigation was carried out on perovskite-based derivatives of CaV1-xMoxO3-δ using X-ray Photoelectron Spectroscopy (XPS). According to the XRD pattern, the area of homogeneity covers the region from x = 0 to x = 0.6. Wide XPS-peaks of Ca, V, Mo and O are observed, signalling that elements are presented in multiple states. A model for explaining the large chemical shifts of XPS peaks due to different charging effects on different parts of the sample surface is proposed.

Analysis of XPS spectra of Fe 2+ and Fe 3+ ions in oxide materials

NASA Astrophysics Data System (ADS)

Yamashita, Toru; Hayes, Peter

2008-02-01

Samples of the iron oxides Fe 0.94O, Fe 3O 4, Fe 2O 3, and Fe 2SiO 4 were prepared by high temperature equilibration in controlled gas atmospheres. The samples were fractured in vacuum and high resolution XPS spectra of the fractured surfaces were measured. The peak positions and peak shape parameters of Fe 3p for Fe 2+ and Fe 3+ were derived from the Fe 3p XPS spectra of the standard samples of 2FeO·SiO 2 and Fe 2O 3, respectively. Using these parameters, the Fe 3p peaks of Fe 3O 4 and Fe 1- yO are analysed. The results indicate that high resolution XPS techniques can be used to determine the Fe 2+/Fe 3+ ratios in metal oxides. The technique has the potential for application to other transition metal oxide systems.

The Synthesis of a Core-Shell Photocatalyst Material YF3:Ho3+@TiO2 and Investigation of Its Photocatalytic Properties

PubMed Central

Xu, Xuan; Zhou, Shiyu; Long, Jun; Wu, Tianhu; Fan, Zihong

2017-01-01

In this paper, YF3:Ho3+@TiO2 core-shell nanomaterials were prepared by hydrolysis of tetra-n-butyl titanate (TBOT) using polyvinylpyrrolidone K-30 (PVP) as the coupling agent. Characterization methods including X-ray diffraction (XRD), transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDS) under TEM, X-ray photoelectron spectroscopy (XPS), fluorescence spectrometry, ultraviolet-visible diffuse reflectance spectroscopy, and electron spin resonance (ESR) were used to characterize the properties and working mechanism of the prepared photocatalyst material. They indicated that the core phase YF3 nanoparticles were successfully coated with a TiO2 shell and the length of the composite was roughly 100 nm. The Ho3+ single-doped YF3:Ho3+@TiO2 displayed strong visible absorption peaks with wavelengths of 450, 537, and 644 nm, respectively. By selecting these three peaks as excitation wavelengths, we could observe 288 nm (5D4→5I8) ultraviolet emission, which confirmed that there was indeed an energy transfer from YF3:Ho3+ to anatase TiO2. In addition, this paper investigated the influences of different TBOT dosages on photocatalysis performance of the as-prepared photocatalyst material. Results showed that the YF3:Ho3+@TiO2 core-shell nanomaterial was an advanced visible-light-driven catalyst, which decomposed approximately 67% of rhodamine b (RhB) and 34.6% of phenol after 10 h of photocatalysis reaction. Compared with the blank experiment, the photocatalysis efficiency was significantly improved. Finally, the visible-light-responsive photocatalytic mechanism of YF3:Ho3+@TiO2 core-shell materials and the influencing factors of photocatalytic degradation were investigated to study the apparent kinetics, which provides a theoretical basis for improving the structural design and functions of this new type of catalytic material. PMID:28772662

Electronic structure study of wide band gap magnetic semiconductor (La{sub 0.6}Pr{sub 0.4}){sub 0.65}Ca{sub 0.35}MnO{sub 3} nanocrystals in paramagnetic and ferromagnetic phases

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dwivedi, G. D.; Chou, H.; Yang, K. S.

2016-04-25

X-ray circular magnetic dichroism (XMCD), X-ray photoemission spectroscopy (XPS), and ultraviolet photoemission spectroscopy (UPS) techniques were used to study the electronic structure of nanocrystalline (La{sub 0.6}Pr{sub 0.4}){sub 0.65}Ca{sub 0.35}MnO{sub 3} near Fermi-level. XMCD results indicate that Mn{sup 3+} and Mn{sup 4+} spins are aligned parallel to each other at 20 K. The low M-H hysteresis curve measured at 5 K confirms ferromagnetic ordering in the (La{sub 0.6}Pr{sub 0.4}){sub 0.65}Ca{sub 0.35}MnO{sub 3} system. The low temperature valence band XPS indicates that coupling between Mn3d and O2p is enhanced and the electronic states near Fermi-level have been suppressed below T{sub C}. The valence bandmore » UPS also confirms the suppression of electronic states near Fermi-level below Curie temperature. UPS near Fermi-edge shows that the electronic states are almost absent below 0.5 eV (at 300 K) and 1 eV (at 115 K). This absence clearly demonstrates the existence of a wide band-gap in the system since, for hole-doped semiconductors, the Fermi-level resides just above the valence band maximum.« less

Toward an Improved Understanding of the Role of Soil Organic Matter in NOy Cycling through Investigation of Heterogeneous Reactions with NO2+

NASA Astrophysics Data System (ADS)

Engelhard, M.; Hansen, R. F.; Raff, J. D.

2017-12-01

Molecular level investigation of compositional changes due to heterogeneous reactions of nitrogen oxides (NOx, NOy) with soil organic matter (SOM) is important to develop a fundamental scientific understanding of the soil/atmosphere interface. In addition, interactions between NOx reservoir species and SOM play a more important role in NOx and NOy recycling than previously realized. Despite the importance of soil to the global terrestrial-atmospheric cycling of nitrogen, interactions of N2O5 with SOM are not well understood. Uncertainty in these processes is problematic because it means that NOy is not properly represented in the Earth-systems models used for prediction and regulation. The ultimate objective of this study is to investigate the production of NOy from the reaction of N2O5 with SOM and elucidate the mechanisms that return NOy back to the atmosphere, where NOy can contribute to aerosol and O3 formation. In the initial phase of this study, we reacted SOM standards with NO2+ (produced from concentrated HNO3), which is an intermediate in the heterogeneous reaction of N2O5 with SOM. We then characterized these reaction products using X-ray photoelectron spectroscopy (XPS). XPS was used to measure the nitrogen chemistry before and after reaction of SOM with NO2+. These results will be discussed along with the pros and cons using XPS to characterize SOM chemistry.

Towards nanometric resolution in multilayer depth profiling: a comparative study of RBS, SIMS, XPS and GDOES.

PubMed

Escobar Galindo, Ramón; Gago, Raul; Duday, David; Palacio, Carlos

2010-04-01

An increasing amount of effort is currently being directed towards the development of new functionalized nanostructured materials (i.e., multilayers and nanocomposites). Using an appropriate combination of composition and microstructure, it is possible to optimize and tailor the final properties of the material to its final application. The analytical characterization of these new complex nanostructures requires high-resolution analytical techniques that are able to provide information about surface and depth composition at the nanometric level. In this work, we comparatively review the state of the art in four different depth-profiling characterization techniques: Rutherford backscattering spectroscopy (RBS), secondary ion mass spectrometry (SIMS), X-ray photoelectron spectroscopy (XPS) and glow discharge optical emission spectroscopy (GDOES). In addition, we predict future trends in these techniques regarding improvements in their depth resolutions. Subnanometric resolution can now be achieved in RBS using magnetic spectrometry systems. In SIMS, the use of rotating sample holders and oxygen flooding during analysis as well as the optimization of floating low-energy ion guns to lower the impact energy of the primary ions improves the depth resolution of the technique. Angle-resolved XPS provides a very powerful and nondestructive technique for obtaining depth profiling and chemical information within the range of a few monolayers. Finally, the application of mathematical tools (deconvolution algorithms and a depth-profiling model), pulsed sources and surface plasma cleaning procedures is expected to greatly improve GDOES depth resolution.

Electronic structure and phase separation of superconducting and nonsuperconducting KxFe2-ySe2 revealed by x-ray photoemission spectroscopy

NASA Astrophysics Data System (ADS)

Oiwake, M.; Ootsuki, D.; Noji, T.; Hatakeda, T.; Koike, Y.; Horio, M.; Fujimori, A.; Saini, N. L.; Mizokawa, T.

2013-12-01

We have investigated the electronic structure of superconducting (SC) and nonsuperconducting (non-SC) KxFe2-ySe2 using x-ray photoemission spectroscopy (XPS). The spectral shape of the Fe 2p XPS is found to depend on the amount of Fe vacancies. The Fe 2p3/2 peak of the SC and non-SC Fe-rich samples is accompanied by a shoulder structure on the lower binding energy side, which can be attributed to the metallic phase embedded in the Fe2+ insulating phase. The absence of the shoulder structure in the non-SC Fe-poor sample allows us to analyze the Fe 2p spectra using a FeSe4 cluster model. The Fe 3d-Se 4p charge-transfer energy of the Fe2+ insulating phase is found to be ˜2.3 eV which is smaller than the Fe 3d-Fe 3d Coulomb interaction of ˜3.5 eV. This indicates that the Fe2+ insulating state is the charge-transfer type in the Zaanen-Sawatzky-Allen scheme. We also find a substantial change in the valence-band XPS as a function of Fe content and temperature. The metallic state at the Fermi level is seen in the SC and non-SC Fe-rich samples and tends to be enhanced with cooling in the SC sample.

Thickness measurement of a thin hetero-oxide film with an interfacial oxide layer by X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Kim, Kyung Joong; Lee, Seung Mi; Jang, Jong Shik; Moret, Mona

2012-02-01

The general equation Tove = L cos θ ln(Rexp/R0 + 1) for the thickness measurement of thin oxide films by X-ray photoelectron spectroscopy (XPS) was applied to a HfO2/SiO2/Si(1 0 0) as a thin hetero-oxide film system with an interfacial oxide layer. The contribution of the thick interfacial SiO2 layer to the thickness of the HfO2 overlayer was counterbalanced by multiplying the ratio between the intensity of Si4+ from a thick SiO2 film and that of Si0 from a Si(1 0 0) substrate to the intensity of Si4+ from the HfO2/SiO2/Si(1 0 0) film. With this approximation, the thickness levels of the HfO2 overlayers showed a small standard deviation of 0.03 nm in a series of HfO2 (2 nm)/SiO2 (2-6 nm)/Si(1 0 0) films. Mutual calibration with XPS and transmission electron microscopy (TEM) was used to verify the thickness of HfO2 overlayers in a series of HfO2 (1-4 nm)/SiO2 (3 nm)/Si(1 0 0) films. From the linear relation between the thickness values derived from XPS and TEM, the effective attenuation length of the photoelectrons and the thickness of the HfO2 overlayer could be determined.

X-ray Photoelectron Spectroscopy Study of Argon-Plasma-Treated Fluoropolymers

NASA Technical Reports Server (NTRS)

Golub, Morton A.; Lopata, Eugene S.; Finney, Lorie S.

1994-01-01

Films of poly(tetrafluoroethylene) (PTFE) and of a tetrafluoroethylene-perfluoroalkyl vinyl ether (approximately 49:1) copolymer (PFA) were exposed to a radio-frequency argon plasma and then examined by X-ray photoelectron spectroscopy (XPS). The use of fluoropolymer films nearly free of surface hydrocarbon contamination as well as the use of a monochromatized X-ray source for XPS removed two factors contributing to conflicting reports on the effect of exposure time on the fluorine-to-carbon (F/C) and oxygen-to-carbon (O/C) ratios for several Ar-plasma-treated fluoropolymers. Contrary to literature indications, a common pattern was found for PTFE and PFA: a moderate decrease in F/C ratio (from 1.99 to 1.40, and from 1.97 to 1.57, respectively), together with a moderate increase in O/C ratio (from negligible to about 0.10, and from 0.012 to about O.10, respectively) at very short exposures, after which the F/C ratios remained essentially constant on prolonged exposures, while the O/C ratios for PTFE and PFA leveled off at 0.11 and 0.15, respectively. The XPS C(sub 1s), spectra for these polymers exposed to the Ar plasma for 20 min were similar and presented, besides a prominent peak at 292.0 eV (CF2,) and a minor peak at 294.0 or 294.1 eV (CF3), a composite band of four curve-resolved peaks (approximately 285-290 eV) representing various CH, CC, CO, CN, and CF functionalities.

Characterization of fossil remains using XRF, XPS and XAFS spectroscopies

NASA Astrophysics Data System (ADS)

Zougrou, I. M.; Katsikini, M.; Pinakidou, F.; Brzhezinskaya, M.; Papadopoulou, L.; Vlachos, E.; Tsoukala, E.; Paloura, E. C.

2016-05-01

Synchrotron radiation micro-X-Ray Fluorescence (μ-XRF), X-ray photoelectron (XPS) and X-ray Absorption Fine Structure (XAFS) spectroscopies are applied for the study of paleontological findings. More specifically the costal plate of a gigantic terrestrial turtle Titanochelon bacharidisi and a fossilized coprolite of the cave spotted hyena Crocuta crocuta spelaea are studied. Ca L 2,3-edge NEXAFS and Ca 2p XPS are applied for the identification and quantification of apatite and Ca containing minerals. XRF mapping and XAFS are employed for the study of the spatial distribution and speciation of the minerals related to the deposition environment.

Quantitative depth profiling of Ce(3+) in Pt/CeO2 by in situ high-energy XPS in a hydrogen atmosphere.

PubMed

Kato, Shunsuke; Ammann, Markus; Huthwelker, Thomas; Paun, Cristina; Lampimäki, Markus; Lee, Ming-Tao; Rothensteiner, Matthäus; van Bokhoven, Jeroen A

2015-02-21

The redox property of ceria is a key factor in the catalytic activity of ceria-based catalysts. The oxidation state of well-defined ceria nanocubes in gas environments was analysed in situ by a novel combination of near-ambient pressure X-ray Photoelectron Spectroscopy (XPS) and high-energy XPS at a synchrotron X-ray source. In situ high-energy XPS is a promising new tool to determine the electronic structure of matter under defined conditions. The aim was to quantitatively determine the degree of cerium reduction in a nano-structured ceria-supported platinum catalyst as a function of the gas environment. To obtain a non-destructive depth profile at near-ambient pressure, in situ high-energy XPS analysis was performed by varying the kinetic energy of photoelectrons from 1 to 5 keV, and, thus, the probing depth. In ceria nanocubes doped with platinum, oxygen vacancies formed only in the uppermost layers of ceria in an atmosphere of 1 mbar hydrogen and 403 K. For pristine ceria nanocubes, no change in the cerium oxidation state in various hydrogen or oxygen atmospheres was observed as a function of probing depth. In the absence of platinum, hydrogen does not dissociate and, thus, does not lead to reduction of ceria.

An in situ XPS study of L-cysteine co-adsorbed with water on polycrystalline copper and gold

NASA Astrophysics Data System (ADS)

Jürgensen, Astrid; Raschke, Hannes; Esser, Norbert; Hergenröder, Roland

2018-03-01

The interactions of biomolecules with metal surfaces are important because an adsorbed layer of such molecules introduces complex reactive functionality to the substrate. However, studying these interactions is challenging: they usually take place in an aqueous environment, and the structure of the first few monolayers on the surface is of particular interest, as these layers determine most interfacial properties. Ideally, this requires surface sensitive analysis methods that are operated under ambient conditions, for example ambient pressure x-ray photoelectron spectroscopy (AP-XPS). This paper focuses on an AP-XPS study of the interaction of water vapour and l-Cysteine on polycrystalline copper and gold surfaces. Thin films of l-Cysteine were characterized with XPS in UHV and in a water vapour atmosphere (P ≤ 1 mbar): the structure of the adsorbed l-Cysteine layer depended on substrate material and deposition method, and exposure of the surface to water vapour led to the formation of hydrogen bonds between H2O molecules and the COO- and NH2 groups of adsorbed l-Cysteine zwitterions and neutral molecules, respectively. This study also proved that it is possible to investigate monolayers of biomolecules in a gas atmosphere with AP-XPS using a conventional laboratory Al-Kα x-ray source.

The effects of surface pretreatment and nitrogen tetroxide purification on the corrosion rate of Type 304L stainless steel

NASA Technical Reports Server (NTRS)

Blue, G. D.; Moran, C. M.

1985-01-01

Corrosion rates of 304L stainless steel coupons in MON-1 oxidizer have been measured as a function of cleaning procedures employed, surface layer positions, propellant impurity levels, and short-term exposure durations (14 to 90 days). Of special interest was propellant contamination by buildup of soluble iron, which may cause flow decay. Surface treatments employed were combinations of cleaning, pickling, and passivation procedures. Propellants used were MIL-SPEC MON-1 and several types of purified NTO (i.e., low water, low chloride) which may, at a later time, be specified as spacecraft grade. Pretest coupon surface analysis by X-ray photoelectron spectroscopy (XPS-ESCA) has revealed important differences, for the different cleaning procedures, in the make-up of the surface layer, both in composition and state of chemical combination of the elements involved. Comparisons will be made of XPS/ESCA data, for different cleaning procedures, for specimens before and after propellant exposure.

Ferromagnetic mechanism of (Co, Cu)-codoped ZnO films with different Co concentrations investigated by X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Yuan, Huan; Du, Xiaosong; Xu, Ming

2016-05-01

Cobalt/copper-codoped ZnO nanoparticles, synthesized with different Co concentrations by a sol-gel method using ethanol as solvent, were studied via XPS. Hexagonal wurtzite structure was found in all samples, with no evidence of any secondary phase. The average crystallite size of the samples was around 20-30 nm, altered significantly with increasing Co concentration. Copper ions and Cobalt ions are indeed substituted into the ZnO lattice at the Zn2+ site, as shown by XRD and XPS. Further studies showed dramatic changes of Cu valence from +2 to +1 as the Co concentration level exceeds 1%, accompanied by a blue-shift of the optical bandgap from 3.01 to 3.13 eV. Ferromagnetism of the Co-doped Zn0.95Cu0.05O thin films was observed and found to be tunable - a phenomenon associated with the valence state of the Cu ions and the existence of some defects like oxygen vacancies in the films.

High performance SONOS flash memory with in-situ silicon nanocrystals embedded in silicon nitride charge trapping layer

NASA Astrophysics Data System (ADS)

Lim, Jae-Gab; Yang, Seung-Dong; Yun, Ho-Jin; Jung, Jun-Kyo; Park, Jung-Hyun; Lim, Chan; Cho, Gyu-seok; Park, Seong-gye; Huh, Chul; Lee, Hi-Deok; Lee, Ga-Won

2018-02-01

In this paper, SONOS-type flash memory device with highly improved charge-trapping efficiency is suggested by using silicon nanocrystals (Si-NCs) embedded in silicon nitride (SiNX) charge trapping layer. The Si-NCs were in-situ grown by PECVD without additional post annealing process. The fabricated device shows high program/erase speed and retention property which is suitable for multi-level cell (MLC) application. Excellent performance and reliability for MLC are demonstrated with large memory window of ∼8.5 V and superior retention characteristics of 7% charge loss for 10 years. High resolution transmission electron microscopy image confirms the Si-NC formation and the size is around 1-2 nm which can be verified again in X-ray photoelectron spectroscopy (XPS) where pure Si bonds increase. Besides, XPS analysis implies that more nitrogen atoms make stable bonds at the regular lattice point. Photoluminescence spectra results also illustrate that Si-NCs formation in SiNx is an effective method to form deep trap states.

Liquid phase deposition synthesis of hexagonal molybdenum trioxide thin films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Deki, Shigehito; Beleke, Alexis Bienvenu; Kotani, Yuki

2009-09-15

Hexagonal molybdenum trioxide thin films with good crystallinity and high purity have been fabricated by the liquid phase deposition (LPD) technique using molybdic acid (H{sub 2}MoO{sub 4}) dissolved in 2.82% hydrofluoric acid (HF) and H{sub 3}BO{sub 3} as precursors. The crystal was found to belong to a hexagonal hydrate system MoO{sub 3}.nH{sub 2}O (napprox0.56). The unit cell lattice parameters are a=10.651 A, c=3.725 A and V=365.997 A{sup 3}. Scanning electron microscope (SEM) images of the as-deposited samples showed well-shaped hexagonal rods nuclei that grew and where the amount increased with increase in reaction time. X-ray photon electron spectroscopy (XPS) spectramore » showed a Gaussian shape of the doublet of Mo 3d core level, indicating the presence of Mo{sup 6+} oxidation state in the deposited films. The deposited films exhibited an electrochromic behavior by lithium intercalation and deintercalation, which resulted in coloration and bleaching of the film. Upon dehydration at about 450 deg. C, the hexagonal MoO{sub 3}.nH{sub 2}O was transformed into the thermodynamically stable orthorhombic phase. - Abstract: SEM photograph of typical h-MoO{sub 3}.nH{sub 2}O thin film nuclei obtained after 36 h at 40 deg. C by the LPD method. Display Omitted« less

Correlation between theoretical descriptor and catalytic oxygen reduction activity of graphene supported palladium and palladium alloy electrocatalysts

NASA Astrophysics Data System (ADS)

Seo, Min Ho; Choi, Sung Mook; Lee, Dong Un; Kim, Won Bae; Chen, Zhongwei

2015-12-01

The oxygen reduction reaction, ORR, performances of graphene-supported palladium (Pd) and palladium alloys (Pd3X: X = Ag, Co and Fe) catalysts with highly dispersed catalyst particles are investigated in acidic and alkaline conditions using a rotating disk electrode, RDE. Graphene nanosheet, GNS, supported Pd based catalysts are fabricated without surfactant through the impregnation of Pd and 2nd metal precursors on GNS, leading to small and uniformly dispersed nanoparticles, even when high metal loading of up to 60 wt.% are deposited on supports. The ab-initio density functional theory, DFT, calculations, which are based on the d-band center theory, have been applied to correlate with the results of the ORR performances obtained by half-cell tests. Additionally, the cohesive energy, Ecoh, and dissolution potential, Um, for the Pd nanoparticles have been calculated to understand thermodynamic stability. To elucidate the d-band center shift, the Pd 3d5/2 core-level binding energies for Pd/GNS, Pd3Ag/GNS, Pd3Fe/GNS and Pd3Co/GNS have been investigated by X-ray photoelectron spectroscopy, XPS. The GNS-supported Pd, or Pd-based alloy-nanoparticle catalyst shows good ORR activity under acidic and alkaline conditions, suggesting it may offer potential replacement for Pt for use in cathode electrodes of anion-exchange membrane fuel cell, AEMFC, and acid based polymer electrolyte fuel cell, PEMFC.

Surface characterization of ZnO/ZnMn2O4 and Cu/Mn3O4 powders obtained by thermal degradation of heterobimetallic complexes

NASA Astrophysics Data System (ADS)

Barrault, Joël; Makhankova, Valeriya G.; Khavryuchenko, Oleksiy V.; Kokozay, Vladimir N.; Ayrault, Philippe

2012-03-01

From the selective transformation of the heterometallic (Zn-Mn or Cu-Mn) carboxylate complexes with 2,2'-bipyridyl by thermal degradation at relatively low (350 °C) temperature, it was possible to get either well defined spinel ZnMn2O4 over zinc oxide or well dispersed copper particles surrounded by a manganese oxide (Mn3O4) in a core-shell like structure. Morphology of the powder surface was examined by scanning electron microscopy with energy dispersive X-ray microanalysis (SEM/EDX). Surface composition was determined by X-ray photoelectron spectroscopy (XPS). Specific surface of the powders by nitrogen adsorption was found to be 33±0.2 and 9±0.06 m2 g-1 for Zn-Mn and Cu-Mn samples, respectively, which is comparable to those of commercial products.

Controlled doping by self-assembled dendrimer-like macromolecules

NASA Astrophysics Data System (ADS)

Wu, Haigang; Guan, Bin; Sun, Yingri; Zhu, Yiping; Dan, Yaping

2017-02-01

Doping via self-assembled macromolecules might offer a solution for developing single atom electronics by precisely placing individual dopants at arbitrary location to meet the requirement for circuit design. Here we synthesize dendrimer-like polyglycerol macromolecules with each carrying one phosphorus atom in the core. The macromolecules are immobilized by the coupling reagent onto silicon surfaces that are pre-modified with a monolayer of undecylenic acid. Nuclear magnetic resonance (NMR) and X-ray photoelectron spectroscopy (XPS) are employed to characterize the synthesized macromolecules and the modified silicon surfaces, respectively. After rapid thermal annealing, the phosphorus atoms carried by the macromolecules diffuse into the silicon substrate, forming dopants at a concentration of 1017 cm-3. Low-temperature Hall effect measurements reveal that the ionization process is rather complicated. Unlike the widely reported simple ionization of phosphorus dopants, nitrogen and carbon are also involved in the electronic activities in the monolayer doped silicon.

Bimetallic magnetic PtPd-nanoparticles as efficient catalyst for PAH removal from liquid media

NASA Astrophysics Data System (ADS)

Zanato, A. F. S.; Silva, V. C.; Lima, D. A.; Jacinto, M. J.

2017-11-01

Monometallic Pd- and bimetallic PtPd-nanoparticles supported on a mesoporous magnetic magnetite@silica matrix resembling a core-shell structure (Fe3O4@mSiO2) have been fabricated. The material was characterized by transmission electron microscope (TEM), high-angle annular dark field-scanning transmission electron microscopy (HAADF-STEM), X-ray photoelectron spectra (XPS), energy dispersive spectroscopy (EDS) and inductively coupled plasma mass spectrometry (ICP-MS). The catalysts were applied in the removal of anthracene from liquid phase via catalytic hydrogenation. It was found that anthracene as a model compound could be completely converted into the partially hydrogenated species by the monometallic and bimetallic solids. However, during the recycling study the bimetallic material (Fe3O4@mSiO2PtPd-) showed an enhanced activity towards anthracene removal compared with the monometallic materials. A single portion of the PtPd-based catalyst can be used up to 11 times in the hydrogenation of anthracene under mild conditions (6 atm of H2, 75 °C, 20 min). Thanks to the presence of a dense magnetic core, the catalysts were capable of responding to an applied external magnetic field and once the reaction was completed, catalyst/product separation was straightforward.

Synthesis and in vitro cellular interactions of superparamagnetic iron nanoparticles with a crystalline gold shell

NASA Astrophysics Data System (ADS)

Bandyopadhyay, Sulalit; Singh, Gurvinder; Sandvig, Ioanna; Sandvig, Axel; Mathieu, Roland; Anil Kumar, P.; Glomm, Wilhelm Robert

2014-10-01

Fe@Au core-shell nanoparticles (NPs) exhibit multiple functionalities enabling their effective use in applications such as medical imaging and drug delivery. In this work, a novel synthetic method was developed and optimized for the synthesis of highly stable, monodisperse Fe@Au NPs of average diameter ∼24 nm exhibiting magneto-plasmonic characteristics. Fe@Au NPs were characterized by a wide range of experimental techniques, including scanning (transmission) electron microscopy (S(T)EM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDX), dynamic light scattering (DLS) and UV-vis spectroscopy. The formed particles comprise an amorphous iron core with a crystalline Au shell of tunable thickness, and retain the superparamagnetic properties at room temperature after formation of a crystalline Au shell. After surface modification, PEGylated Fe@Au NPs were used for in vitro studies on olfactory ensheathing cells (OECs) and human neural stem cells (hNSCs). No adverse effects of the Fe@Au particles were observed post-labeling, both cell types retaining normal morphology, viability, proliferation, and motility. It can be concluded that no appreciable toxic effects on both cell types, coupled with multifunctionality and chemical stability make them ideal candidates for therapeutic as well as diagnostic applications.

Dynamic XPS measurements of ultrathin polyelectrolyte films containing antibacterial Ag–Cu nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taner-Camcı, Merve; Suzer, Sefik, E-mail: suzer@fen.bilkent.edu.tr

Ultrathin films consisting of polyelectrolyte layers prepared by layer-by-layer deposition technique and containing also Ag and Cu nanoparticles exhibit superior antibacterial activity toward Escherichia coli. These films have been investigated with XPS measurements under square wave excitation at two different frequencies, in order to further our understanding about the chemical/physical nature of the nanoparticles. Dubbed as dynamical XPS, such measurements bring out similarities and differences among the surface structures by correlating the binding energy shifts of the corresponding XPS peaks. Accordingly, it is observed that the Cu2p, Ag3d of the metal nanoparticles, and S2p of cysteine, the stabilizer and themore » capping agent, exhibit similar shifts. On the other hand, the C1s, N1s, and S2p peaks of the polyelectrolyte layers shift differently. This finding leads us the claim that the Ag and Cu atoms are in a nanoalloy structure, capped with cystein, as opposed to phase separated entities.« less

Lab-based ambient pressure X-ray photoelectron spectroscopy from past to present

NASA Astrophysics Data System (ADS)

Arble, Chris; Jia, Meng; Newberg, John T.

2018-05-01

Chemical interactions which occur at a heterogeneous interface between a gas and substrate are critical in many technological and natural processes. Ambient pressure X-ray photoelectron spectroscopy (AP-XPS) is a powerful spectroscopy tool that is inherently surface sensitive, elemental and chemical specific, with the ability to probe sample surfaces in the presence of a gas phase. In this review, we discuss the evolution of lab-based AP-XPS instruments, from the first development by Siegbahn and coworkers up through modern day systems. A comprehensive overview is given of heterogeneous experiments investigated to date via lab-based AP-XPS along with the different instrumental metrics that affect the quality of sample probing. We conclude with a discussion of future directions for lab-based AP-XPS, highlighting the efficacy for this in-demand instrument to continue to expand in its ability to significantly advance our understanding of surface chemical processes under in situ conditions in a technologically multidisciplinary setting.

Structural, XPS and magnetic studies of pulsed laser deposited Fe doped Eu{sub 2}O{sub 3} thin film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Sandeep; Prakash, Ram, E-mail: rpgiuc@gmail.com; Choudhary, R.J.

2015-10-15

Highlights: • Growth of Fe doped Eu{sub 2}O{sub 3} thin films by PLD. • XRD and Raman’s spectroscopy used for structure confirmation. • The electronic states of Eu and Fe are confirmed by XPS. • Magnetic properties reveals room temperature magnetic ordering in deposited film. - Abstract: Fe (4 at.%) doped europium (III) oxide thin film was deposited on silicon (1 0 0) substrate by pulsed laser deposition technique. Structural, spectral and magnetic properties were studied by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and magnetization measurements. XRD and Raman spectroscopy reveal that the grown film is singlemore » phased and belongs to the cubic structure of Eu{sub 2}O{sub 3}. XPS study of the Eu{sub 1.92}Fe{sub 0.08}O{sub 3} film shows that Fe exists in Fe{sup 3+} ionic state in the film. The film exhibits magnetic ordering at room temperature.« less

Hydrolysis condensation reactions of titanium alkoxides in thin films: A study of the steric hindrance effect by X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Barlier, Vincent; Bounor-Legaré, Véronique; Boiteux, Gisèle; Davenas, Joël; Léonard, Didier

2008-06-01

An original approach based on X-ray photoelectron spectroscopy (XPS) is proposed to study the influence of the surrounding humidity on the hydrolysis-condensation reactions of five titanium alkoxides in thin films. More precisely, the influence of the nature of the ligands (propoxide, butoxide, isopropoxide, phenoxide, and 9H-carbazole-9-yl-ethyl-oxy) on the reaction rate was evidenced. The reaction advancement was evaluated by comparing XPS chemical compositions to theoretical compositions calculated for all the possible rates. XPS chemical environment information allowed validating the reliability of this approach through the evaluation of the condensation state. In both approaches, the influence of the steric hindrance on the reactivity of titanium alkoxides was highlighted to be similar to what has been previously observed in solution. Theses results corroborate the validity of our XPS approach to determine titanium alkoxide hydrolysis-condensation reactions in the specific application of thin films.

Schottky Barrier Height of Pd/MoS2 Contact by Large Area Photoemission Spectroscopy.

PubMed

Dong, Hong; Gong, Cheng; Addou, Rafik; McDonnell, Stephen; Azcatl, Angelica; Qin, Xiaoye; Wang, Weichao; Wang, Weihua; Hinkle, Christopher L; Wallace, Robert M

2017-11-08

MoS 2 , as a model transition metal dichalcogenide, is viewed as a potential channel material in future nanoelectronic and optoelectronic devices. Minimizing the contact resistance of the metal/MoS 2 junction is critical to realizing the potential of MoS 2 -based devices. In this work, the Schottky barrier height (SBH) and the band structure of high work function Pd metal on MoS 2 have been studied by in situ X-ray photoelectron spectroscopy (XPS). The analytical spot diameter of the XPS spectrometer is about 400 μm, and the XPS signal is proportional to the detection area, so the influence of defect-mediated parallel conduction paths on the SBH does not affect the measurement. The charge redistribution by Pd on MoS 2 is detected by XPS characterization, which gives insight into metal contact physics to MoS 2 and suggests that interface engineering is necessary to lower the contact resistance for the future generation electronic applications.

Quantitative analysis of Si1-xGex alloy films by SIMS and XPS depth profiling using a reference material

NASA Astrophysics Data System (ADS)

Oh, Won Jin; Jang, Jong Shik; Lee, Youn Seoung; Kim, Ansoon; Kim, Kyung Joong

2018-02-01

Quantitative analysis methods of multi-element alloy films were compared. The atomic fractions of Si1-xGex alloy films were measured by depth profiling analysis with secondary ion mass spectrometry (SIMS) and X-ray Photoelectron Spectroscopy (XPS). Intensity-to-composition conversion factor (ICF) was used as a mean to convert the intensities to compositions instead of the relative sensitivity factors. The ICFs were determined from a reference Si1-xGex alloy film by the conventional method, average intensity (AI) method and total number counting (TNC) method. In the case of SIMS, although the atomic fractions measured by oxygen ion beams were not quantitative due to severe matrix effect, the results by cesium ion beam were very quantitative. The quantitative analysis results by SIMS using MCs2+ ions are comparable to the results by XPS. In the case of XPS, the measurement uncertainty was highly improved by the AI method and TNC method.

The adsorption of methyl iodide on uranium and uranium dioxide: Surface characterization using X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES)

NASA Astrophysics Data System (ADS)

Dillard, J. G.; Moers, H.; Klewe-Nebenius, H.; Kirch, G.; Pfennig, G.; Ache, H. J.

1984-09-01

The adsorption of methyl iodide on uranium and on uranium dioxide has been studied at 25 °C. Surfaces of the substrates were characterized before and after adsorption by X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES). The XPS binding energy results indicate that CH 3I adsorption on uranium yields a carbide-type carbon, UC, and uranium iodide, UI 3. On uranium dioxide the carbon electron binding energy measurements are consistent with the formation of a hydrocarbon, —CH 3-type moiety. The interpretation of XPS and AES spectral features for CH 3I adsorption on uranium suggest that a complex dissociative adsorption reaction takes place. Adsorption of CH 3I on UO 2 occurs via a dissociative process. Saturation coverage occurs on uranium at approximately two langmuir (1 L = 10 -6 Torr s) exposure whereas saturation coverage on uranium dioxide is found at about five langmuir.

Electro-optic investigation of the n-alkanethiol GaAs(001) interface: Surface phenomena and applications to photoluminescence-based biosensing

NASA Astrophysics Data System (ADS)

Marshall, Gregory M.

Semiconductor surfaces coupled to molecular structures derived from organic chemistry form the basis of an emerging class of field-effect devices. In addition to molecular electronics research, these interfaces are developed for a variety of sensor applications in the electronic and optical domains. Of practical interest are self-assembled monolayers (SAMs) comprised of n-alkanethiols [HS(CH2)n], which couple to the GaAs(001) surface through S-GaAs covalent bond formation. These SAMs offer potential functionality in terms of the requisite sensor chemistry and the passivation effect such coupling is known to afford. In this thesis, the SAM-GaAs interface is investigated in the context of a photonic biosensor based on photoluminescence (PL) variation. The scope of the work is categorized into three parts: i) the structural and compositional analysis of the surface using X-ray photoelectron spectroscopy (XPS), ii) the investigation of electronic properties at the interface under equilibrium conditions using infrared (IR) spectroscopy, the Kelvin probe method, and XPS, and iii) the analysis of the electro-optic response under steady-state photonic excitation, specifically, the surface photovoltage (SPV) and PL intensity. Using a partial overlayer model of angle-resolved XPS spectra in which the component assignments are shown to be quantitatively valid, the coverage fraction of methyl-terminated SAMs is shown to exceed 90%. Notable among the findings are a low-oxide, Ga-rich surface with elemental As present in sub-monolayer quantities consistent with theoretical surface morphologies. Modal analysis of transmission IR spectra show that the SAM molecular order is sufficient to support a Beer-Lambert determination of the IR optical constants, which yields the observation of a SAM-specific absorbance enhancement. By correlation of the IR absorbance with the SAM dipole layer potential, the enhancement mechanism is attributed to the vibrational moments added by the electronic polarizability in the static field of the SAM. Lastly, the surface Fermi level position is determined by XPS and is used to interpret SPV results in terms of a thiol-induced reduction of the surface cross-section for minority carrier-capture. Numerical analysis confirms this result based on the carrier transport theory of PL intensity by means of a reduction of the surface recombination velocity. Keywords: photonics, biosensor, GaAs, self-assembled monolayers, X-ray photoelectron spectroscopy, IR spectroscopy, photoluminescence, surface Fermi level, surface photovoltage.

Chemisorbed monolayers of corannulene penta-thioethers on gold.

PubMed

Angelova, Polina; Solel, Ephrath; Parvari, Galit; Turchanin, Andrey; Botoshansky, Mark; Gölzhäuser, Armin; Keinan, Ehud

2013-02-19

Penta(tert-butylthio)corannulene and penta(4-dimethylaminophenylthio)corannulene form highly stable monolayers on gold surfaces, as indicated by X-ray photoelectron spectroscopy (XPS). Formation of these homogeneous monolayers involves multivalent coordination of the five sulfur atoms to gold with the peripheral alkyl or aryl substituents pointing away from the surface. No dissociation of C-S bonds upon binding could be observed at room temperature. Yet, the XPS experiments reveal strong chemical bonding between the thioether groups and gold. Temperature-dependent XPS study shows that the thermal stability of the monolayers is higher than the typical stability of self-assembled monolayers (SAMs) of thiolates on gold.

XPS studies of Mg doped GDC (Ce0.8Gd0.2O2-δ) for IT-SOFC

NASA Astrophysics Data System (ADS)

Tyagi, Deepak; Rao, P. Koteswara; Wani, B. N.

2018-04-01

Fuel Cells have gained much attention as efficient and environment friendly device for both stationary as well as mobile applications. For intermediate temperature SOFC (IT-SOFC), ceria based electrolytes are the most promising one, due to their higher ionic conductivity at relatively lower temperatures. Gd doped ceria is reported to be having the highest ionic conductivity. In the present work, Mg is codoped along with Gd and the electronic structure of the constituents is studied by XPS. XPS confirm that the Cerium is present in +4 oxidation state only which indicates that electronic conduction can be completely avoided.

Surface Characterization of Polymer Blends by XPS and ToF-SIMS

PubMed Central

Chan, Chi Ming; Weng, Lu-Tao

2016-01-01

The surface properties of polymer blends are important for many industrial applications. The physical and chemical properties at the surface of polymer blends can be drastically different from those in the bulk due to the surface segregation of the low surface energy component. X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary mass spectrometry (ToF-SIMS) have been widely used to characterize surface and bulk properties. This review provides a brief introduction to the principles of XPS and ToF-SIMS and their application to the study of the surface physical and chemical properties of polymer blends. PMID:28773777

Thickness and composition of ultrathin SiO2 layers on Si

NASA Astrophysics Data System (ADS)

van der Marel, C.; Verheijen, M. A.; Tamminga, Y.; Pijnenburg, R. H. W.; Tombros, N.; Cubaynes, F.

2004-07-01

Ultrathin SiO2 layers are of importance for the semiconductor industry. One of the techniques that can be used to determine the chemical composition and thickness of this type of layers is x-ray photoelectron spectroscopy (XPS). As shown by Seah and Spencer [Surf. Interface Anal. 33, 640 (2002)], it is not trivial to characterize this type of layer by means of XPS in a reliable way. We have investigated a series of ultrathin layers of SiO2 on Si (in the range from 0.3 to 3 nm) using XPS. The samples were also analyzed by means of transmission electron microscopy (TEM), Rutherford backscattering (RBS), and ellipsometry. The thickness of the SiO2 layers (d) was determined from the XPS results using three different approaches: the ``standard'' equation (Seah and Spencer) for d, an overlayer-substrate model calculation, and the QUASES-Tougaard [Surf. Interface Anal. 26, 249 (1998), QUASES-Tougaard: Software package for Quantitative Analysis of Surfaces by Electron Spectroscopy, version 4.4 (2000); http://www.quases.com] method. Good agreement was obtained between the results of XPS analyses using the ``standard'' equation, the overlayer-substrate model calculation, and RBS results. The QUASES-Tougaard results were approximately 62% above the other XPS results. The optical values for the thickness were always slightly higher than the thickness according to XPS or RBS. Using the model calculation, these (relatively small) deviations from the optical results could be explained as being a consequence of surface contaminations with hydrocarbons. For a thickness above 2.5 nm, the TEM results were in good agreement with the results obtained from the other techniques (apart from QUASES-Tougaard). Below 2.5 nm, significant deviations were found between RBS, XPS, and optical data on the one hand and TEM results on the other hand; the deviations became larger as the thickness of the SiO2 decreased. This effect may be related to interface states of oxygen, which have been investigated [D. A. Muller, T. Sorsch, S. Moccio, F. H. Baumann, K. Evans-Lutterodt, and G. Timp, Nature (London) 399, 758 (1999); D. A. Muller and J. B. Neaton, Structure and Energetics of the Interface Between Si and Amorphous SiO2 in Fundamental Aspects of Silicon Oxidation, edited by Y. J. Chabal (Springer, Berlin, 2001), pp. 219-246.] by means of high-resolution electron energy loss spectroscopy measurements of the O K edge in ultrathin gate oxides of SiO2. .

XNBR-grafted halloysite nanotube core-shell as a potential compatibilizer for immiscible polymer systems

NASA Astrophysics Data System (ADS)

Paran, S. M. R.; Naderi, G.; Ghoreishy, M. H. R.

2016-09-01

Halloysite nanotubes (HNTs) grafted with carboxylated nitrile byutadiene rubber (XNBR) were synthesized via a sol-gel method. The HNTs as an inorganic cores were pre-treated with 3-Glycidoxypropyl trimethoxysilane, then successfully coated with the XNBR as an organic shell. The properties of XNBR-grafted HNTs were characterized by transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The results suggested that the XNBR grafted to the surfaces of HNTs successfully. Then the TPE nanocomposites based on polyamide-6 (PA6) and nitrile butadiene rubber (NBR) containing various XNBR-grafted and pristine HNTs were prepared via a direct melt mixing method. The morphology, mechanical, dynamic mechanical and rheological properties of the prepared TPE nanocomposites were investigated. The results show that the XNBR-grafted HNTs can effectively improve the morphology and mechanical properties of the PA6/NBR TPEs. The morphology study of the prepared nanocomposites show that the effect of XNBR-grafted HNTs on the size reduction of NBR phase is markedly more effective than the pristine HNTs and rose by 50% in the same concentrations. Mechanical measurements show that the Young's modulus of the TPE nanocomposites rose by 60% in just 7 wt% of XNBR-grafted HNT loading. The results indicate that the introduction of HNT/XNBR core-shells into the PA6/NBR TPEs can enhances the interfacial interactions and provides a more fine rubber phase morphology and controlled mechanical properties in comparison with the accordingly TPE nanocomposites containing pristine HNTs.

Preparation of PPy-Coated MnO2 Hybrid Micromaterials and Their Improved Cyclic Performance as Anode for Lithium-Ion Batteries

NASA Astrophysics Data System (ADS)

Feng, Lili; Zhang, Yinyin; Wang, Rui; Zhang, Yanli; Bai, Wei; Ji, Siping; Xuan, Zhewen; Yang, Jianhua; Zheng, Ziguang; Guan, Hongjin

2017-09-01

MnO2@PPy core-shell micromaterials are prepared by chemical polymerization of pyrrole on the MnO2 surface. The polypyrrole (PPy) is formed as a homogeneous organic shell on the MnO2 surface. The thickness of PPy shell can be adjusted by the usage of pyrrole. The analysis of SEM, FT-IR, X-ray photoelectron spectroscopy (XPS), thermo-gravimetric analysis (TGA), and XRD are used to confirm the formation of PPy shell. Galvanostatic cell cycling and electrochemical impedance spectroscopy (EIS) are used to evaluate the electrochemical performance as anode for lithium-ion batteries. The results show that after formation of MnO2@PPy core-shell micromaterials, the cyclic performance as anode for lithium-ion batteries is improved. Fifty microliters of PPy-coated caddice-clew-like MnO2 has the best cyclic performances as has 620 mAh g-1 discharge specific capacities after 300 cycles. As a comparison, the discharge specific capacity of bare MnO2 materials falls to below 200 mAh g-1 after 10 cycles. The improved lithium-storage cyclic stability of the MnO2@PPy samples attributes to the core-shell hybrid structure which can buffer the structural expansion and contraction of MnO2 caused by the repeated embedding and disengagement of Li ions and can prevent the pulverization of MnO2. This experiment provides an effective way to mitigate the problem of capacity fading of the transition metal oxide materials as anode materials for (lithium-ion batteries) LIBs.

Preparation of PPy-Coated MnO2 Hybrid Micromaterials and Their Improved Cyclic Performance as Anode for Lithium-Ion Batteries.

PubMed

Feng, Lili; Zhang, Yinyin; Wang, Rui; Zhang, Yanli; Bai, Wei; Ji, Siping; Xuan, Zhewen; Yang, Jianhua; Zheng, Ziguang; Guan, Hongjin

2017-09-02

MnO 2 @PPy core-shell micromaterials are prepared by chemical polymerization of pyrrole on the MnO 2 surface. The polypyrrole (PPy) is formed as a homogeneous organic shell on the MnO 2 surface. The thickness of PPy shell can be adjusted by the usage of pyrrole. The analysis of SEM, FT-IR, X-ray photoelectron spectroscopy (XPS), thermo-gravimetric analysis (TGA), and XRD are used to confirm the formation of PPy shell. Galvanostatic cell cycling and electrochemical impedance spectroscopy (EIS) are used to evaluate the electrochemical performance as anode for lithium-ion batteries. The results show that after formation of MnO 2 @PPy core-shell micromaterials, the cyclic performance as anode for lithium-ion batteries is improved. Fifty microliters of PPy-coated caddice-clew-like MnO 2 has the best cyclic performances as has 620 mAh g -1 discharge specific capacities after 300 cycles. As a comparison, the discharge specific capacity of bare MnO 2 materials falls to below 200 mAh g -1 after 10 cycles. The improved lithium-storage cyclic stability of the MnO 2 @PPy samples attributes to the core-shell hybrid structure which can buffer the structural expansion and contraction of MnO 2 caused by the repeated embedding and disengagement of Li ions and can prevent the pulverization of MnO 2 . This experiment provides an effective way to mitigate the problem of capacity fading of the transition metal oxide materials as anode materials for (lithium-ion batteries) LIBs.

Surface characterization of ZnO/ZnMn{sub 2}O{sub 4} and Cu/Mn{sub 3}O{sub 4} powders obtained by thermal degradation of heterobimetallic complexes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barrault, Joeel, E-mail: joel.barrault@univ-poitiers.fr; Makhankova, Valeriya G., E-mail: leram@univ.kiev.ua; Khavryuchenko, Oleksiy V.

2012-03-15

From the selective transformation of the heterometallic (Zn-Mn or Cu-Mn) carboxylate complexes with 2,2 Prime -bipyridyl by thermal degradation at relatively low (350 Degree-Sign C) temperature, it was possible to get either well defined spinel ZnMn{sub 2}O{sub 4} over zinc oxide or well dispersed copper particles surrounded by a manganese oxide (Mn{sub 3}O{sub 4}) in a core-shell like structure. Morphology of the powder surface was examined by scanning electron microscopy with energy dispersive X-ray microanalysis (SEM/EDX). Surface composition was determined by X-ray photoelectron spectroscopy (XPS). Specific surface of the powders by nitrogen adsorption was found to be 33{+-}0.2 and 9{+-}0.06more » m{sup 2} g{sup -1} for Zn-Mn and Cu-Mn samples, respectively, which is comparable to those of commercial products. - Graphical abstract: From the selective transformation of heterometallic (Zn-Mn or Cu-Mn) carboxylate complexes, it was possible to get either well defined spinel ZnMn{sub 2}O{sub 4} over zinc oxide or well dispersed copper particles surrounded by a manganese oxide (Mn{sub 3}O{sub 4}) in a core-shell like structure. Highlights: Black-Right-Pointing-Pointer Thermal degradation of heterometallic complexes results in fine disperse particles. Black-Right-Pointing-Pointer Core-shell Cu/Mn{sub 3}O{sub 4} particles are obtained. Black-Right-Pointing-Pointer ZnMn{sub 2}O{sub 4} spinel layer covers ZnO particles.« less

Insights into electrochemical reactions from ambient pressure photoelectron spectroscopy.

PubMed

Stoerzinger, Kelsey A; Hong, Wesley T; Crumlin, Ethan J; Bluhm, Hendrik; Shao-Horn, Yang

2015-11-17

The understanding of fundamental processes in the bulk and at the interfaces of electrochemical devices is a prerequisite for the development of new technologies with higher efficiency and improved performance. One energy storage scheme of great interest is splitting water to form hydrogen and oxygen gas and converting back to electrical energy by their subsequent recombination with only water as a byproduct. However, kinetic limitations to the rate of oxygen-based electrochemical reactions hamper the efficiency in technologies such as solar fuels, fuel cells, and electrolyzers. For these reactions, the use of metal oxides as electrocatalysts is prevalent due to their stability, low cost, and ability to store oxygen within the lattice. However, due to the inherently convoluted nature of electrochemical and chemical processes in electrochemical systems, it is difficult to isolate and study individual electrochemical processes in a complex system. Therefore, in situ characterization tools are required for observing related physical and chemical processes directly at the places where and while they occur and can help elucidate the mechanisms of charge separation and charge transfer at electrochemical interfaces. X-ray photoelectron spectroscopy (XPS), also known as ESCA (electron spectroscopy for chemical analysis), has been used as a quantitative spectroscopic technique that measures the elemental composition, as well as chemical and electronic state of a material. Building from extensive ex situ characterization of electrochemical systems, initial in situ studies were conducted at or near ultrahigh vacuum (UHV) conditions (≤10(-6) Torr) to probe solid-state electrochemical systems. However, through the integration of differential-pumping stages, XPS can now operate at pressures in the torr range, comprising a technique called ambient pressure XPS (AP-XPS). In this Account, we briefly review the working principles and current status of AP-XPS. We use several recent in situ studies on model electrochemical components as well as operando studies performed by our groups at the Advanced Light Source (ALS) at Lawrence Berkeley National Laboratory to illustrate that AP-XPS is both a chemically and an electrically specific tool since photoelectrons carry information on both the local chemistry and electrical potentials. The applications of AP-XPS to oxygen electrocatalysis shown in this Account span well-defined studies of (1) the oxide/oxygen gas interface, (2) the oxide/water vapor interface, and (3) operando measurements of half and full electrochemical cells. Using specially designed model devices, we can expose and isolate the electrode or interface of interest to the incident X-ray beam and AP-XPS analyzer to relate the electrical potentials to the composition/chemical state of the key components and interfaces. We conclude with an outlook on new developments of AP-XPS end stations, which may provide significant improvement in the observation of dynamics over a wide range of time scales, higher spatial resolution, and improved characterization of boundary or interface layers (solid/solid and liquid/solid).

Hydrogeochemical and mineralogical investigations of arsenic- and humic substance-enriched aquifers

NASA Astrophysics Data System (ADS)

Liu, Chen-Wuing; Lai, Chih-Chieh; Chen, Yen-Yu; Lu, Kuang-Liang

2013-08-01

This study investigated the hydrogeochemical and mineralogical characteristics of arsenic-contaminated and humic-substance-enriched aquifers in the Chianan Plain, Taiwan, which is an endemic area for blackfoot disease (BFD). Factorial analysis (FA) was used to evaluate the hydrochemical characteristics of 83 groundwater samples in the Chianan Plain, and 462 geological core samples obtained from 9 drilling wells were collected to analyze their arsenic and iron contents. The major mineral phases and chemical components were determined using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy and energy dispersive spectrometry (SEM-EDS). Partition of arsenic among various hosting solids in sediments was determined by sequential extraction. The results of FA showed that the hydrochemical characteristics of the groundwater samples could be grouped by 4 factors: salinization, arsenic, sulfide, and iron. Arsenic was positively correlated with alkalinity, dissolved organic/inorganic carbon, and fluorescence intensity [humic acids, (HAs)]. As(V) has a higher chelating affinity with HAs than does As(III), resulting in higher As(V) concentrations distributed throughout the reducing environment. High levels and correlations of As and HAs may cause BFD in the Chianan Plain. No correlation was found between the measured and calculated redox potentials of the various redox couples. The As(III)/As(V) was under a chemical non-equilibrium condition. The vertical distribution of the sedimentary As (solid phase) typically increased with depth, but the aqueous As concentrations were higher in the second aquifer (depth of 80-120 m). Arsenic content (solid phase) was higher in the clay/silt sediments and marine formations. The major minerals identified by XPS and SEM-EDS were goethite, hematite, magnetite, pyrite, and siderite, agreeing with the SI values calculated by PHREEQC. Arsenic content was strongly correlated with sulfur (weight%; R2 = 0.76, p < 0.05), but was weakly correlated with iron (weight%). However, a moderate correlation (R2 = 0.44-0.75; p < 0.001) between As(s) and Fe(s) in the sediments was found in the transitions in the marine and non-marine formations, especially in the fine grains. The chelation of humic complex, competition for sorption sites of organic carbon, reduction dissolution of Fe oxides are mainly responsible for the groundwater As mobility in the Chianan Plain, especially for the marine sequence.

X-ray Photoelectron Spectroscopy (XPS), Rutherford Back Scattering (RBS) studies

NASA Technical Reports Server (NTRS)

Neely, W. C.; Bozak, M. J.; Williams, J. R.

1993-01-01

X-ray photoelectron spectroscopy (XPS), Rutherford Back Scattering (RBS) studies of each of sample received were completed. Since low angle X-ray could not be performed because of instrumentation problems, Auger spectrometry was employed instead. The results of these measurements for each of the samples is discussed in turn.

1300929

NASA Image and Video Library

2013-08-15

ARTHUR BROWN (AST, AEROSPACE METALLIC MATERIALS) LOADS A CERAMIC COATED SILICON WAFER INTO A KRATOS (ELECTRON SPECTROSCOPY FOR CHEMICAL ANALYSIS) TO PERFORM X-RAY PHOTOELECTRON SPECTROSCOPY (XPS). XPS IS A TECHNIQUE THAT ANALYZES THE SURFACE CHEMISTRY OF A SAMPLE BY IRRADIATING IT WITH X-RAYS AND MEASURING THE NUMBER AND KINETIC ENERGY OF ELECTRON THAT ESCAPE.

Ultra-fine structures of Pd-Ag-HAp nanoparticle deposition on protruded TiO2 barrier layer for dental implant

NASA Astrophysics Data System (ADS)

Jang, Jae-Myung; Kim, Seung-Dai; Park, Tae-Eon; Choe, Han-Cheol

2018-02-01

The biocompatibility structure of an implant surface is of great importance to the formation of new bone tissue around the dental implant and also has a significant chemical reaction in the osseointegration process. Thus, ultra-fine Pd-Ag-HAp nanoparticles have been electrodeposited on protruded TiO2 barrier layer in mixed electrolyte solutions. Unusual protrusions patterns, which are assigned to Pd-Ag-HAp nanoparticles, can be clearly differentiated from a TiO2 nanotube oxide layer formed by an anodizing process. In the chemical bonding state, the surface characteristics of Pd/Ag/HAp compounds have been investigated by FE-SEM, EDS mapping analysis, and XPS analysis. The mapping dots of the elements including Ti, Ca, Pd, Ag, and P showed a homogeneous distribution throughout the entire surface when deposited onto the protruded TiO2 barrier layer. The XPS spectra of Ti-2p, O-1S, Pd-3d, and Ag-3d have been investigated, with the major XPS peak indicating Pd-3d. The Ag-3d level was clearly observed with further scanning of the Ca-2p region. Based on the results of the chemical states, the structural properties of the protrusion patterns were also examined after being deposited onto the barrier oxide film, resulting in the representative protrusion patterns being mainly composed of Pd-Ag-HAp compounds. The results of the soaking evaluation showed that the protrusion patterns and the protruded TiO2 barrier layer were all effective in regards to biocompatibility.

A ToF-SIMS and XPS study of protein adsorption and cell attachment across PEG-like plasma polymer films with lateral compositional gradients

NASA Astrophysics Data System (ADS)

Menzies, Donna J.; Jasieniak, Marek; Griesser, Hans J.; Forsythe, John S.; Johnson, Graham; McFarland, Gail A.; Muir, Benjamin W.

2012-12-01

In this work we report a detailed X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) study of poly(ethylene glycol) PEG-like chemical gradients deposited via plasma enhanced chemical vapour deposition (PECVD) at two different load powers using diethylene glycol dimethyl ether (DG) as a monomer. Principal component analysis (PCA) was applied to the ToF-SIMS data both before and after protein adsorption on the plasma polymer thin films. Results of the PCA loadings indicated a higher content of hydrocarbon fragments across the higher load power gradient, which adsorbed higher amounts of proteins. Gradients deposited at a lower load power retained a higher degree of monomer like functionality as did the central region directly underneath the knife edge electrode. Analysis of the adsorption of serum proteins (human serum albumin and fetal bovine serum) was monitored across the gradient films and increased with decreasing ether (PEG-like) film chemistries. The effect of protein incubation time on the levels adsorbed fetal bovine serum on the plasma polymer films was critical, with significantly more protein adsorbing after 24 hour incubation times on both gradient films. The attachment of HeLa cells on the gradients appeared to be dictated not only by the surface chemistry, but also by the adsorption of serum proteins. XPS analysis revealed that at surface ether concentrations of less than 70% in the gradient films, significant increases in protein and cell attachment were observed.

Reaction chemistry and ligand exchange at cadmium selenide nanocrystal surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Owen, Jonathan; Park, Jungwon; Trudeau, Paul-Emile

Chemical modification of nanocrystal surfaces is fundamentally important to their assembly, their implementation in biology and medicine, and greatly impacts their electrical and optical properties. However, it remains a major challenge owing to a lack of analytical tools to directly determine nanoparticle surface structure. Early nuclear magnetic resonance (NMR) and X-ray photoelectron spectroscopy (XPS) studies of CdSe nanocrystals prepared in tri-n-octylphosphine oxide (1) and tri-n-octylphosphine (2), suggested these coordinating solvents are datively bound to the particle surface. However, assigning the broad NMR resonances of surface-bound ligands is complicated by significant concentrations of phosphorus-containing impurities in commercial sources of 1, andmore » XPS provides only limited information about the nature of the phosphorus containing molecules in the sample. More recent reports have shown the surface ligands of CdSe nanocrystals prepared in technical grade 1, and in the presence of alkylphosphonic acids, include phosphonic and phosphinic acids. These studies do not, however, distinguish whether these ligands are bound datively, as neutral, L-type ligands, or by X-type interaction of an anionic phosphonate/phosphinate moiety with a surface Cd{sup 2+} ion. Answering this question would help clarify why ligand exchange with such particles does not proceed generally as expected based on a L-type ligand model. By using reagents with reactive silicon-chalcogen and silicon-chlorine bonds to cleave the ligands from the nanocrystal surface, we show that our CdSe and CdSe/ZnS core-shell nanocrystal surfaces are likely terminated by X-type binding of alkylphosphonate ligands to a layer of Cd{sup 2+}/Zn{sup 2+} ions, rather than by dative interactions. Further, we provide spectroscopic evidence that 1 and 2 are not coordinated to our purified nanocrystals.« less

Investigating the complex mechanism of B migration in a magnetic-tunnel-junction trilayer structure—a combined study using XPS and TOF-SIMS

NASA Astrophysics Data System (ADS)

Ying, Ji-Feng; Ji, Rong; Ter Lim, Sze; Tran, Michael N.; Wang, Chen Chen; Ernult, Franck

2016-02-01

The magnetic-tunnel-junction (MTJ) structure is the core of many important devices, such as magnetic recording head and STT-RAM. CoFeB/MgO/CoFeB tri-layer thin-film stack is a widely researched MTJ structure. In this tri-layer, the functional property of the MTJ, i.e. its TMR ratio, is critically dependent on the crystal orientation of the CoFe grains. In order for the desired (1 0 0) out of plane texture to develop in the CoFeB layers, B needs to be engineered to be expelled out of these CoFeB layers, and diffuse or migrate into the adjacent layers. Ta is usually used as a seed layer adjacent to the MTJ structure. In this work, we investigated the important B-migration mechanisms within this MTJ structure through a combined XPS/TOF-SIMS study. Specifically, we tried to elucidate the possible physical/chemical interactions between the B and Ta that could happen with different film stack designs. Previous works have shown that there might be two possible B-migration mechanisms. One mechanism is direct B diffusion into the adjacent Ta layer during annealing. The other B-migration mechanism is through the formation of TaBOx species, in which B could be carried out by the Ta diffusion. In particular, through studying a series of film stacks, we discussed the circumstances under which one of these B-migration mechanisms becomes dominant. Furthermore, we discussed how these B-migration mechanisms facilitated the B expulsion in a common MTJ structure.

Arsenic(V) removal from groundwater using nano scale zero-valent iron as a colloidal reactive barrier material.

PubMed

Kanel, Sushil Raj; Greneche, Jean-Mark; Choi, Heechul

2006-03-15

The removal of As(V), one of the most poisonous groundwater pollutants, by synthetic nanoscale zero-valent iron (NZVI) was studied. Batch experiments were performed to investigate the influence of pH, adsorption kinetics, sorption mechanism, and anionic effects. Field emission scanning electron microscopy (FE-SEM), high-resolution transmission electron microscopy (HR-TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Mossbauer spectroscopy were used to characterize the particle size, surface morphology, and corrosion layer formation on pristine NZVI and As(V)-treated NZVI. The HR-TEM study of pristine NZVI showed a core-shell-like structure, where more than 90% of the nanoparticles were under 30 nm in diameter. Mössbauer spectroscopy further confirmed its structure in which 19% were in zero-valent state with a coat of 81% iron oxides. The XRD results showed that As(V)-treated NZVI was gradually converted into magnetite/maghemite corrosion products over 90 days. The XPS study confirmed that 25% As(V) was reduced to As(III) by NZVI after 90 days. As(V) adsorption kinetics were rapid and occurred within minutes following a pseudo-first-order rate expression with observed reaction rate constants (Kobs) of 0.02-0.71 min(-1) at various NZVI concentrations. Laser light scattering analysis confirmed that NZVI-As(V) forms an inner-sphere surface complexation. The effects of competing anions revealed that HCO3-, H4SiO4(0), and H2PO4(2-) are potential interfering agents in the As(V) adsorption reaction. Our results suggest that NZVI is a suitable candidate for As(V) remediation.

Investigating early stages of biocorrosion with XPS: AISI 304 stainless steel exposed to Burkholderia species

NASA Astrophysics Data System (ADS)

Johansson, Leena-Sisko; Saastamoinen, Tuomas

1999-04-01

We have investigated the interactions of an exopolymer-producing bacteria, Burkholderia sp. with polished AISI 304 stainless steel substrates using X-ray photoelectron spectroscopy (XPS). Steel coupons were exposed to the pure bacteria culture in a specially designed flowcell for 6 h during which the experiment was monitored in situ with an optical microscope. XPS results verified the formation of biofilm containing extracellular polymer on all the samples exposed to bacteria. Sputter results indicated that some ions needed for metabolic processes were trapped within the biofilm. Changes in the relative Fe concentration and Fe 2p peak shape indicated that also iron had accumulated into the biofilm.

Samarium electrodeposited acetate and oxide thin films on stainless steel substrate characterized by XPS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Myhre, Kristian; Burns, Jonathan; Meyer, Harry

Characterization of a samarium thin film deposited on a stainless steel substrate using molecular electrodeposition was carried out using a Thermo Scientific K-Alpha X-ray photoelectron spectrometer. We studied two types of samarium electrodeposition samples, one as-deposited and one heated to 700 °C in an air flow. Survey scans include peaks coming from the stainless steel substrate, such as Fe and Cr. An X-ray photoelectron spectroscopy (XPS) survey spectrum, Sm 3d, C 1s, and O 1s narrow scans are shown. It was determined that the heating process decomposed the deposited Sm acetate to Sm 2O 3 using XPS.

Samarium electrodeposited acetate and oxide thin films on stainless steel substrate characterized by XPS

DOE PAGES

Myhre, Kristian; Burns, Jonathan; Meyer, Harry; ...

2016-06-01

Characterization of a samarium thin film deposited on a stainless steel substrate using molecular electrodeposition was carried out using a Thermo Scientific K-Alpha X-ray photoelectron spectrometer. We studied two types of samarium electrodeposition samples, one as-deposited and one heated to 700 °C in an air flow. Survey scans include peaks coming from the stainless steel substrate, such as Fe and Cr. An X-ray photoelectron spectroscopy (XPS) survey spectrum, Sm 3d, C 1s, and O 1s narrow scans are shown. It was determined that the heating process decomposed the deposited Sm acetate to Sm 2O 3 using XPS.

XPS Study of Oxide/GaAs and SiO2/Si Interfaces

NASA Technical Reports Server (NTRS)

Grunthaner, F. J.; Grunthaner, P. J.; Vasquez, R. P.; Lewis, B. F.; Maserjian, J.; Madhukar, A.

1982-01-01

Concepts developed in study of SiO2/Si interface applied to analysis of native oxide/GaAs interface. High-resolution X-ray photoelectron spectroscopy (XPS) has been combined with precise chemical-profiling technique and resolution-enhancement methods to study stoichiometry of transitional layer. Results are presented in report now available.

Use of XPS to clarify the Hall coefficient sign variation in thin niobium layers buried in silicon

NASA Astrophysics Data System (ADS)

Demchenko, Iraida N.; Lisowski, Wojciech; Syryanyy, Yevgen; Melikhov, Yevgen; Zaytseva, Iryna; Konstantynov, Pavlo; Chernyshova, Maryna; Cieplak, Marta Z.

2017-03-01

Si/Nb/Si trilayers formed with 9.5 and 1.3 nm thick niobium layer buried in amorphous silicon were prepared by magnetron sputtering and studied using XPS depth-profile techniques in order to investigate the change of Hall coefficient sign with thickness. The analysis of high-resolution (HR) XPS spectra revealed that the thicker layer sample has sharp top interface and metallic phase of niobium, thus holes dominate the transport. In contrast, the analysis indicates that the thinner layer sample has a Nb-rich mixed alloy formation at the top interface. The authors suggest that the main effect leading to a change of sign of the Hall coefficient for the thinner layer sample (which is negative contrary to the positive sign for the thicker layer sample) may be related to strong boundary scattering enhanced by the presence of silicon ions in the layer close to the interface/s. The depth-profile reconstruction was performed by SESSA software tool confirming that it can be reliably used for quantitative analysis/interpretation of experimental XPS data.

Surface chemical reactions induced on pyrite by ion bombardment

NASA Astrophysics Data System (ADS)

Ruano, Gustavo; Pomiro, Fernando; Ferrón, Julio

2018-01-01

Through X-ray photoemission spectroscopy (XPS), we studied the chemical changes induced in a natural crystal of pyrite (FeS2) upon exposure to 4.5 keV He+ beam. We found an important reducing effect induced by ion bombardment leading to the production of iron embedded in the pyrite matrix. Through a combination of the usual Doniach-Sunjic treatment and Factor Analysis of XPS yields, we were able of analyzing the full Fe 2p XPS signal. We could in this way distinguish Fe compounds with the same binding energy for the Fe 2p3/2 yield. Our results show that He+ bombardment disrupts the ionic environment producing S2-2 and S0, Fe2+ and Fe3+ ions, and the reduction to metallic iron. The remaining pyrite matrix does not passivate the embedded iron structures, which are readily oxidized under air exposure. The oxide formed resembled that of magnetite from the XPS point of view. Further He+ bombardment proved to be efficient to reduce the iron oxide back to iron again.

XPS and 31P NMR inquiry of Eu3+-induced structural modification in SnO-containing phosphate glass

NASA Astrophysics Data System (ADS)

Jiménez, José A.; Fachini, Esteban Rosim; Zhao, Chunqing

2018-07-01

The influence of Eu3+ doping on the structural properties of SnO-containing phosphate glass has been investigated by X-ray photoelectron spectroscopy (XPS) and 31P nuclear magnetic resonance (NMR) spectroscopy. Oxygen 1s XPS data indicates that the Eu3+ doping results in a higher concentration of non-bridging oxygens in the glass matrix, whereas 31P NMR shows an increase in the terminal phosphate chain tetrahedral units, i.e. the amount of Q1 sites with only one bridging oxygen. Accordingly, both techniques agree with a depolymerization effect induced by the Eu3+ ions. Further, XPS reveals that together with the Eu3+ doping, the presence of Sn4+ is supported while the presence of Eu2+ is also indicated. The structural changes are then indicated to be a consequence of redox chemistry between Sn2+ and Eu3+ promoting a transition of tin from Sn2+ with a role as network former to Sn4+ acting as network modifier in the glass system.

X-ray photoelectron spectroscopy on 1-peso and 2-pesos of the Argentine Republic

NASA Astrophysics Data System (ADS)

Gard, Faramarz S.; Duffo, Gustavo; Bergamasco, Pablo; Forlerer, Elena

2018-04-01

Relative concentrations of nickel and copper at the surface of the ring and centre parts of 1-peso and 2-pesos Argentine coins have been studied by means of X-ray photoemission spectroscopy (XPS). It has been observed Ni-enrichment at the surface of the ring (silvery) part of a 1-peso, minted in 1994, whereas the XPS data reveals lack of nickel at the surface of the centre (silvery) part of a 2-pesos, minted in 2016. This discrepancy is explained by analyzing the XPS peaks of oxygen and carbon, and is suggested to be related to the contamination layer on the surface of the coins. The XPS analysis of the golden parts of the coins, namely the centre part of the 1-peso and the ring part of the 2-pesos coins were inconclusive, due to the small amount of the Ni (nominally %2) used in those parts. The possible oxidations states of the metals at the surface of the untreated and treated coins with the artificial human sweat were also identified.

Surfactant Mediated Growth of Co on MgO(111)

NASA Astrophysics Data System (ADS)

Johnson-Steigelman, H. Trevor; Parihar, Somendra S.; Lyman, Paul F.

2010-03-01

Monolayer films of Co were deposited using an electrostatic electron-beam evaporator on single-crystal MgO(111)- √3 x√3 R 30^o substrates held at room temperature, with subsequent annealing of temperatures 400 C to 800 C. These films were characterized using low-energy electron diffraction (LEED), x-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and x-ray diffraction (XRD). After short anneals of 400 C, AFM, LEED, and XPS suggest that islanding has occurred at the surface. XPS and XRD indicate the presence of elemental Co. 1-2 ML films of Ag were examined as a potential surfactant to aid in the growth of smooth Co films. Despite the fact that Ag itself formed islands, it was found that the presence of Ag did have a surfactant effect upon the thin-film growth of Co on Ag/MgO(111)- √3 x√3 R 30^o. Co islands were still present, but much more smooth than islands formed without Ag. XPS and AFM suggest strongly that Ag floated to the top of these samples at temperatures above 400 ^oC.

Comparative study of the native oxide on 316L stainless steel by XPS and ToF-SIMS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tardio, Sabrina, E-mail: s.tardio@surrey.ac.uk; Abel, Marie-Laure; Castle, James E.

2015-09-15

The very thin native oxide film on stainless steel, of the order of 2 nm, is known to be readily modified by immersion in aqueous media. In this paper, X-ray photoelectron spectroscopy (XPS) and time of flight secondary ions mass spectrometry are employed to investigate the nature of the air-formed film and modification after water emersion. The film is described in terms of oxide, hydroxide, and water content. The preferential dissolution of iron is shown to occur on immersion. It is shown that a water absorbed layer and a hydroxide layer are present above the oxide-like passive film. The concentrations ofmore » water and hydroxide appear to be higher in the case of exposure to water. A secure method for the peak fitting of Fe2p and Cr2p XPS spectra of such films on their metallic substrates is described. The importance of XPS survey spectra is underlined and the feasibility of C{sub 60}{sup +} SIMS depth profiling of a thin oxide layer is shown.« less

Surface functionalization of thin-film diamond for highly stable and selective biological interfaces

PubMed Central

Stavis, Courtney; Clare, Tami Lasseter; Butler, James E.; Radadia, Adarsh D.; Carr, Rogan; Zeng, Hongjun; King, William P.; Carlisle, John A.; Aksimentiev, Aleksei; Bashir, Rashid; Hamers, Robert J.

2011-01-01

Carbon is an extremely versatile family of materials with a wide range of mechanical, optical, and mechanical properties, but many similarities in surface chemistry. As one of the most chemically stable materials known, carbon provides an outstanding platform for the development of highly tunable molecular and biomolecular interfaces. Photochemical grafting of alkenes has emerged as an attractive method for functionalizing surfaces of diamond, but many aspects of the surface chemistry and impact on biological recognition processes remain unexplored. Here we report investigations of the interaction of functionalized diamond surfaces with proteins and biological cells using X-ray photoelectron spectroscopy (XPS), atomic force microscopy, and fluorescence methods. XPS data show that functionalization of diamond with short ethylene glycol oligomers reduces the nonspecific binding of fibrinogen below the detection limit of XPS, estimated as > 97% reduction over H-terminated diamond. Measurements of different forms of diamond with different roughness are used to explore the influence of roughness on nonspecific binding onto H-terminated and ethylene glycol (EG)-terminated surfaces. Finally, we use XPS to characterize the chemical stability of Escherichia coli K12 antibodies on the surfaces of diamond and amine-functionalized glass. Our results show that antibody-modified diamond surfaces exhibit increased stability in XPS and that this is accompanied by retention of biological activity in cell-capture measurements. Our results demonstrate that surface chemistry on diamond and other carbon-based materials provides an excellent platform for biomolecular interfaces with high stability and high selectivity. PMID:20884854

Versailles Project on Advanced Materials and Standards Interlaboratory Study on Measuring the Thickness and Chemistry of Nanoparticle Coatings Using XPS and LEIS.

PubMed

Belsey, Natalie A; Cant, David J H; Minelli, Caterina; Araujo, Joyce R; Bock, Bernd; Brüner, Philipp; Castner, David G; Ceccone, Giacomo; Counsell, Jonathan D P; Dietrich, Paul M; Engelhard, Mark H; Fearn, Sarah; Galhardo, Carlos E; Kalbe, Henryk; Won Kim, Jeong; Lartundo-Rojas, Luis; Luftman, Henry S; Nunney, Tim S; Pseiner, Johannes; Smith, Emily F; Spampinato, Valentina; Sturm, Jacobus M; Thomas, Andrew G; Treacy, Jon P W; Veith, Lothar; Wagstaffe, Michael; Wang, Hai; Wang, Meiling; Wang, Yung-Chen; Werner, Wolfgang; Yang, Li; Shard, Alexander G

2016-10-27

We report the results of a VAMAS (Versailles Project on Advanced Materials and Standards) inter-laboratory study on the measurement of the shell thickness and chemistry of nanoparticle coatings. Peptide-coated gold particles were supplied to laboratories in two forms: a colloidal suspension in pure water and; particles dried onto a silicon wafer. Participants prepared and analyzed these samples using either X-ray photoelectron spectroscopy (XPS) or low energy ion scattering (LEIS). Careful data analysis revealed some significant sources of discrepancy, particularly for XPS. Degradation during transportation, storage or sample preparation resulted in a variability in thickness of 53 %. The calculation method chosen by XPS participants contributed a variability of 67 %. However, variability of 12 % was achieved for the samples deposited using a single method and by choosing photoelectron peaks that were not adversely affected by instrumental transmission effects. The study identified a need for more consistency in instrumental transmission functions and relative sensitivity factors, since this contributed a variability of 33 %. The results from the LEIS participants were more consistent, with variability of less than 10 % in thickness and this is mostly due to a common method of data analysis. The calculation was performed using a model developed for uniform, flat films and some participants employed a correction factor to account for the sample geometry, which appears warranted based upon a simulation of LEIS data from one of the participants and comparison to the XPS results.

AFM AND XPS Characterization of Zinc-Aluminum Alloy Coatings with Attention to Surface Dross and Flow Lines

NASA Astrophysics Data System (ADS)

Harding, Felipe A.; Alarcon, Nelson A.; Toledo, Pedro G.

Surfaces of various zinc-aluminum alloy (Zn-Al) coated steel samples are studied with attention to foreign surface dross by atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS/ESCA). AFM topographic maps of zinc-aluminum alloy surfaces free of dross reveal the perfect nanoscale details of two kinds of dendrites: branched and globular. In all magnifications the dendrites appear smooth and, in general, very clean. XPS analysis of the extreme surface of a Zn-Al sample reveals Al, Zn, Si and O as the main components. The XPS results show no segregation or separation of phases other than those indicated by the ternary Al-Zn-Si diagram. For surfaces of Zn-Al plagued with impurities, high resolution AFM topographic maps reveal three situations: (1) areas with well-defined dendrites, relatively free of dross; (2) areas with small, millimeter-sized black spots known as dross; and (3) areas with large black stains, known as flow lines. Dendrite deformation and dross accumulation increase notably in the neighborhood, apparently clean to the naked eye, of dross or flow lines. XPS results of areas with dross and flow lines indicate unacceptable high concentration of Si and important Si phase separation. These results, in the light of AFM work, reveal that dross and flow lines are a consequence of a high local concentration of Si from high melting point silica and silicate impurities in the Zn-Al alloy source.

Comparing XPS on bare and capped ZrN films grown by plasma enhanced ALD: Effect of ambient oxidation

NASA Astrophysics Data System (ADS)

Muneshwar, Triratna; Cadien, Ken

2018-03-01

In this article we compare x-ray photoelectron spectroscopy (XPS) measurements on bare- and capped- zirconium nitride (ZrN) films to investigate the effect of ambient sample oxidation on the detected bound O in the form of oxide ZrO2 and/or oxynitride ZrOxNy. ZrN films in both bare- and Al2O3/AlN capped- XPS samples were grown by plasma-enhanced atomic layer deposition (PEALD) technique using tetrakis dimethylamino zirconium (TDMAZr) precursor, forming gas (5% H2, rest N2) inductively coupled plasma (ICP), and as received research grade process gases under identical process conditions. Capped samples were prepared by depositing 1 nm thick PEALD AlN on ZrN, followed by additional deposition of 1 nm thick ALD Al2O3, without venting of ALD reactor. On bare ZrN sample at room temperature, spectroscopic ellipsometry (SE) measurements with increasing ambient exposure times (texp) showed a self-limiting surface oxidation with the oxide thickness (dox) approaching 3.7 ± 0.02 nm for texp > 120 min. In XPS data measured prior to sample sputtering (tsput = 0), ZrO2 and ZrOxNy were detected in bare- samples, whereas only ZrN and Al2O3/AlN from capping layer were detected in capped- samples. For bare-ZrN samples, appearance of ZrO2 and ZrOxNy up to sputter depth (dsput) of 15 nm in depth-profile XPS data is in contradiction with measured dox = 3.7 nm, but explained from sputtering induced atomic inter-diffusion within analyzed sample. Appearance of artifacts in the XPS spectra from moderately sputtered (dsput = 0.2 nm and 0.4 nm) capped-ZrN sample, provides an evidence to ion-bombardment induced modifications within analyzed sample.

Cohort study comparing prostate photovaporisation with XPS 180W and HPS 120W laser.

PubMed

López, B; Capitán, C; Hernández, V; de la Peña, E; Jiménez-Valladolid, I; Guijarro, A; Pérez-Fernández, E; Llorente, C

2016-01-01

Prostate photovaporisation with Greenlight laser for the surgical treatment of benign prostate hyperplasia has rapidly evolve to the new XPS 180W. We have previously demonstrated the safety and efficacy of the HPS 120W. The aim of this study was to assess the functional and safety results, with a year of follow-up, of photovaporisation using the XPS 180W laser compared with its predecessor. A cohort study was conducted with a series of 191 consecutive patients who underwent photovaporisation between 1/2008 and 5/2013. The inclusion criteria were an international prostate symptom score (IPSS) >15 after medical failure, a prostate volume <80 cm(3) and a maximum flow <15 mL/s. We assessed preoperative and intraoperative variables (energy used, laser time and total surgical time), complications, catheter hours, length of stay and functional results (maximum flow, IPSS, prostate-specific antigen and prostate volume) at 3, 6 and 12 months. We analysed the homogeneity in preoperative characteristics of the 2 groups through univariate analysis techniques. The postoperative functional results were assessed through an analysis of variance of repeated measures with mixed models. A total of 109 (57.1%) procedures were performed using HPS 120W, and 82 (42.9%) were performed using XPS. There were no differences between the preoperative characteristics. We observed significant differences both in the surgical time and effective laser time in favour of the XPS system. This advantage was 11% (48 ± 15.7 vs. 53.8 ± 16.2, p<.05) and 9% (32.8 ± 11.7 vs. 36 ± 11.6, p<.05), respectively. There were no statistically significant differences in the rest of the analysed parameters. The technical improvements in the XPS 180W system help reduce surgical time, maintaining the safety and efficacy profile offered by the HPS 120W system, with completely superimposable results at 1 year of follow-up. Copyright © 2015 AEU. Publicado por Elsevier España, S.L.U. All rights reserved.

A smart core-sheath nanofiber that captures and releases red blood cells from the blood

NASA Astrophysics Data System (ADS)

Shi, Q.; Hou, J.; Zhao, C.; Xin, Z.; Jin, J.; Li, C.; Wong, S.-C.; Yin, J.

2016-01-01

A smart core-sheath nanofiber for non-adherent cell capture and release is demonstrated. The nanofibers are fabricated by single-spinneret electrospinning of poly(N-isopropylacrylamide) (PNIPAAm), polycaprolactone (PCL) and nattokinase (NK) solution blends. The self-assembly of PNIPAAm and PCL blends during the electrospinning generates the core-sheath PCL/PNIPAAm nanofibers with PNIPAAm as the sheath. The PNIPAAm-based core-sheath nanofibers are switchable between hydrophobicity and hydrophilicity with temperature change and enhance stability in the blood. When the nanofibers come in contact with blood, the NK is released from the nanofibers to resist platelet adhesion on the nanofiber surface, facilitating the direct capture and isolation of red blood cells (RBCs) from the blood above phase-transition temperature of PNIPAAm. Meanwhile, the captured RBCs are readily released from the nanofibers with temperature stimuli in an undamaged manner. The release efficiency of up to 100% is obtained while maintaining cellular integrity and function. This work presents promising nanofibers to effectively capture non-adherent cells and release for subsequent molecular analysis and diagnosis of single cells.A smart core-sheath nanofiber for non-adherent cell capture and release is demonstrated. The nanofibers are fabricated by single-spinneret electrospinning of poly(N-isopropylacrylamide) (PNIPAAm), polycaprolactone (PCL) and nattokinase (NK) solution blends. The self-assembly of PNIPAAm and PCL blends during the electrospinning generates the core-sheath PCL/PNIPAAm nanofibers with PNIPAAm as the sheath. The PNIPAAm-based core-sheath nanofibers are switchable between hydrophobicity and hydrophilicity with temperature change and enhance stability in the blood. When the nanofibers come in contact with blood, the NK is released from the nanofibers to resist platelet adhesion on the nanofiber surface, facilitating the direct capture and isolation of red blood cells (RBCs) from the blood above phase-transition temperature of PNIPAAm. Meanwhile, the captured RBCs are readily released from the nanofibers with temperature stimuli in an undamaged manner. The release efficiency of up to 100% is obtained while maintaining cellular integrity and function. This work presents promising nanofibers to effectively capture non-adherent cells and release for subsequent molecular analysis and diagnosis of single cells. Electronic supplementary information (ESI) available: Electrospinning of polymer nanofibers; FTIR spectra and XPS spectra of PCL, PNIPAAm and PCL/PNIPAAm nanofibers; SEM images of PCL/PNIPAAm nanofibers with varied composition; PNIPAAm content on the sheath of nanofibers; stability of core-sheath PCL/PNIPAAm nanofibers. Platelet adhesion on the PCL/PNIPAAm nanofibers in the presence of NK; Protein adsorption on nanofibers. See DOI: 10.1039/c5nr07070h

Ab initio calculations of the electronic structure and specific optical features of β-LiNH4SO4 single crystals

NASA Astrophysics Data System (ADS)

Rudysh, M. Ya.; Brik, M. G.; Stadnyk, V. Yo.; Brezvin, R. S.; Shchepanskyi, P. A.; Fedorchuk, A.; Khyzhun, O. Y.; Kityk, I. V.; Piasecki, M.

2018-01-01

In the present work complex experimental and theoretical studies of electronic and optical properties for β-lithium-ammonium sulfate crystals of good optical quality are performed using the X-ray photoelectron spectroscopy (XPS) and X-ray emission spectroscopy (XES). Standard immersion and spectroscopic techniques accompanied by the theoretical quantum-chemical calculations in the density functional theory (DFT) framework were applied. Calculations of band structure and related properties were carried out within a framework of local density and generalized gradient approximations as well as hybrid B3LYP functionals. The energy levels features and their origin are established from the DFT calculations and they were ferified by XPS and XES measurements. Theoretical and experimental refractive indices dispersions along the principal crystallographic directions (nx, ny and nz) as well as birefringence dispersion (Δnx, Δny and Δnz) in the visible spectral range are obtained. It was found a closeness of nx and ny curves for the titled crystals. More precise birefringence examining predicts their intersection at λ ≈ 190 nm.

The crystallization behavior of amorphous Ge2Sb2Te5 films induced by a multi-pulsed nanosecond laser

NASA Astrophysics Data System (ADS)

Fan, T.; Liu, F. R.; Li, W. Q.; Guo, J. C.; Wang, Y. H.; Sun, N. X.; Liu, F.

2017-09-01

In this paper, accumulated crystallization of amorphous Ge2Sb2Te5 (a-GST) films induced by a multi-pulsed nanosecond (ns) excimer laser was investigated by x-ray diffraction (XRD), atomic force microscopy, field-emission scanning electron microscopy, x-ray photoelectron spectroscopy (XPS) and a spectrophotometer. XRD analyses revealed that detectable crystallization was firstly observed in the preferred orientation (200), followed by the orientations (220) and (111) after two pulses. Optical contrast, determined by crystallinity as well as surface roughness, was found to retain a linear relation within the first three pulses. A layered growth mechanism from the top surface to the interior of a-GST films was used to explain the crystallization behavior induced by the multi-pulse ns laser. XPS analyses for bond rearrangement and electronic structure further suggested that the crystallization process was performed by generating new bonds of Ge-Te and Sb-Te after laser irradiations. This paper presents the potential of multi-level devices and tunable thermal emitters based on controllable crystallization of phase-change materials.

Enhancing the photocatalytic degradation of Fe-Ti over SiO2 nanocomposite material for paraquat removal

NASA Astrophysics Data System (ADS)

Kruanetr, Senee; Wanchanthuek, Ratchaneekorn

2018-05-01

The effect of Fe and Ti loaded over SiO2 (called FeTi/SiO2) in paraquat degradation was studied for both the catalytic activity and the catalyst surface properties. Sufficient characterization techniques were used to obtain the physical and chemical properties of the FeTi/SiO2 system, such as the adsorption-desorption isotherm, surface area and porous structure, XRD diffraction, FTIR spectroscopy, UV–vis diffuse reflection spectrometry and XPS spectroscopy. The catalytic activity in paraquat degradation studies showed that the bimetallic Fe-Ti over SiO2 had higher activity than the monometallic of either Fe or Ti over SiO2 and also the order of the Fe and Ti loading was the significant parameter affecting the activity. The XPS showed that the level of Fe3+ over the catalyst was related to the obtained activity. Moreover, the optimum Fe:Ti ratio in the FeTi/SiO2 system was 1:1 (by weight). Finally, the effect of the support pretreatment (SiO2 pretreatment) was studied and showed a negative effect on the expressed activity.

Hot filament CVD of boron nitride films

DOEpatents

Rye, Robert R.

1992-01-01

Using a hot filament (.apprxeq.1400.degree. C.) to activate borazine (B.sub.3 N.sub.3 H.sub.6) molecules for subsequent reaction with a direct line-of-sight substrate, transparent boron ntiride films as thick as 25,000 angstroms are grown for a substrate temperature as low as 100.degree. C. The minimum temperature is determined by radiative heating from the adjacent hot filament. The low temperature BN films show no indication of crystallinity with X-ray diffraction (XRD). X-ray photoelectron spectra (XPS) show the films to have a B:N ratio of 0.97:1 with no other XPS detectable impurities above the 0.5% level. Both Raman and infrared (IR) spectroscopy are characteristic of h-BN with small amounts of hydrogen detected as N-H and B-H bands in the IR spectrum. An important feature of this method is the separation and localization of the thermal activation step at the hot filament from the surface reaction and film growth steps at the substrate surface. This allows both higher temperature thermal activation and lower temperature film growth.

Surface Defect Passivation and Reaction of c-Si in H2S.

PubMed

Liu, Hsiang-Yu; Das, Ujjwal K; Birkmire, Robert W

2017-12-26

A unique passivation process of Si surface dangling bonds through reaction with hydrogen sulfide (H 2 S) is demonstrated in this paper. A high-level passivation quality with an effective minority carrier lifetime (τ eff ) of >2000 μs corresponding to a surface recombination velocity of <3 cm/s is achieved at a temperature range of 550-650 °C. X-ray photoelectron spectroscopy (XPS) confirmed the bonding states of Si and S and provides insights into the reaction pathway of Si with H 2 S and other impurity elements both during and after the reaction. Quantitative analysis of XPS spectra showed that the τ eff increases with an increase in the surface S content up to ∼3.5% and stabilizes thereafter, indicative of surface passivation by monolayer coverage of S on the Si surface. However, S passivation of the Si surface is highly unstable because of thermodynamically favorable reaction with atmospheric H 2 O and O 2 . This instability can be eliminated by capping the S-passivated Si surface with a protective thin film such as low-temperature-deposited amorphous silicon nitride.

Does core mobility of lumbar total disc arthroplasty influence sagittal and frontal intervertebral displacement? Radiologic comparison with fixed-core prosthesis

PubMed Central

Delécrin, Joël; Allain, Jérôme; Beaurain, Jacques; Steib, Jean-Paul; Chataigner, Hervé; Aubourg, Lucie; Huppert, Jean; Ameil, Marc; Nguyen, Jean-Michel

2009-01-01

Background An artificial disc prosthesis is thought to restore segmental motion in the lumbar spine. However, it is reported that disc prosthesis can increase the intervertebral translation (VT). The concept of the mobile-core prosthesis is to mimic the kinematic effects of the migration of the natural nucleus and therefore core mobility should minimize the VT. This study explored the hypothesis that core translation should influence VT and that a mobile core prosthesis may facilitate physiological motion. Methods Vertebral translation (measured with a new method presented here), core translation, range of motion (ROM), and distribution of flexion-extension were measured on flexion-extension, neutral standing, and lateral bending films in 89 patients (63 mobile-core [M]; 33 fixed-core [F]). Results At L4-5 levels the VT with M was lower than with F and similar to the VT of untreated levels. At L5-S1 levels the VT with M was lower than with F but was significantly different compared to untreated levels. At M levels a strong correlation was found between VT and core translation; the VT decreases as the core translation increases. At F levels the VT increases as the ROM increases. No significant difference was found between the ROM of untreated levels and levels implanted with either M or F. Regarding the mobility distribution with M and F we observed a deficit in extension at L5-S1 levels and a similar distribution at L4-5 levels compared to untreated levels. Conclusion The intervertebral mobility was different between M and F. The M at L4-5 levels succeeded to replicate mobility similar to L4-5 untreated levels. The M at L5-S1 succeeded in ROM, but failed regarding VT and mobility distribution. Nevertheless M minimized VT at L5-S1 levels. The F increased VT at both L4-5 and L5-S1. Clinical Relevance This study validates the concept that the core translation of an artificial lumbar disc prosthesis minimizes the VT. PMID:25802632

Hybrid biocomposites based on titania nanotubes and a hydroxyapatite coating deposited by RF-magnetron sputtering: Surface topography, structure, and mechanical properties

NASA Astrophysics Data System (ADS)

Chernozem, Roman V.; Surmeneva, Maria A.; Krause, Bärbel; Baumbach, Tilo; Ignatov, Viktor P.; Tyurin, Alexander I.; Loza, Kateryna; Epple, Matthias; Surmenev, Roman A.

2017-12-01

In this study, biocomposites based on porous titanium oxide structures and a calcium phosphate (CaP) or hydroxyapatite (HA) coating are described and prepared. Nanotubes (NTs) with different pore dimensions were processed using anodic oxidation of Ti substrates in a NH4F-containing electrolyte solution at anodization voltages of 30 and 60 V with a DC power supply. The external diameters of the nanotubes prepared at 30 V and 60 V were 53 ± 10 and 98 ± 16 nm, respectively. RF-magnetron sputtering of the HA target in a single deposition run was performed to prepare a coating on the surface of TiO2 NTs prepared at 30 and 60 V. The thickness of the CaP coating deposited on the mirror-polished Si substrate in the same deposition run with TiO2 NTs was determined by optical ellipsometry (SE) 95 ± 5 nm. Uncoated and CaP-coated NTs were annealed at 500 °C in air. Afterwards, the presence of TiO2 (anatase) was observed. The scanning electron microscopy (SEM), X-ray diffraction (XRD), photoelectron spectroscopy (XPS) and nanoindentation results revealed the influence that the NT dimensions had on the CaP coating deposition process. The tubular surfaces of the NTs were completely coated with the HA coating when prepared at 30 V, and no homogeneous CaP coating was observed when prepared at 60 V. The XRD patterns show peaks assigned to crystalline HA only for the coated TiO2 NTs prepared at 30 V. High-resolution XPS spectra show binding energies (BE) of Ca 2p, P 2p and O 1s core-levels corresponding to HA and amorphous calcium phosphate on TiO2 NTs prepared at 30 V and 60 V, respectively. Fabrication of TiO2 NTs results in a significant decrease to the elastic modulus and nanohardness compared to the Ti substrate. The porous structure of the NTs causes an increase in the elastic strain to failure of the coating (H/E) and the parameter used to describe the resistance of the material to plastic deformation (H3/E2) at the nanoscale level compared to the Ti substrate. Furthermore, only the HA coating on the NTs exhibits a significantly increased H/E ratio and H3/E2 factor compared to the NTs and Ti substrate. Increases in resistance to penetration for the indenter were also observed for HA-coated TiO2 NTs prepared at 30 V compared to uncoated and CaP-coated NTs prepared at 60 V.

A Safer Formulation Concept for Flame-Generated Engineered Nanomaterials

PubMed Central

Gass, Samuel; Cohen, Joel M.; Pyrgiotakis, Georgios; Sotiriou, Georgios A.; Pratsinis, Sotiris E.; Demokritou, Philip

2013-01-01

The likely success or failure of the nanotechnology industry depends on the environmental health and safety of engineered nanomaterials (ENMs). While efforts toward engineering safer ENMs are sparse, such efforts are considered crucial to the sustainability of the nanotech industry. A promising approach in this regard is to coat potentially toxic nanomaterials with a biologically inert layer of amorphous SiO2. Core-shell particles exhibit the surface properties of their amorphous SiO2 shell while maintaining specific functional properties of their core material. A major challenge in the development of functional core-shell particles is the design of scalable high-yield processes that can meet large-scale industrial demand. Here, we present a safer formulation concept for flame-generated ENMs based on a one-step, in flight SiO2 encapsulation process, which was recently introduced by the authors as a means for a scalable manufacturing of SiO2 coated ENMs. Firstly, the versatility of the SiO2-coating process is demonstrated by applying it to four ENMs (CeO2, ZnO, Fe2O3, Ag) marked by their prevalence in consumer products as well as their range in toxicity. The ENM-dependent coating fundamentals are assessed and process parameters are optimized for each ENM investigated. The effects of the SiO2-coating on core material structure, composition and morphology, as well as the coating efficiency on each nanostructured material, are evaluated using state-of-the-art analytical methods (XRD, N2 adsorption, TEM, XPS, isopropanol chemisorption). Finally, the biological interactions of SiO2-coated vs. uncoated ENMs are evaluated using cellular bioassays, providing valuable evidence for reduced toxicity for the SiO2-coated ENMs. Results indicate that the proposed ‘safer by design’ concept bears great promise for scaled-up application in industry in order to reduce the toxicological profile of ENMs for certain applications. PMID:23961338

Structure of oxides prepared by decomposition of layered double Mg–Al and Ni–Al hydroxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cherepanova, Svetlana V.; Novosibirsk State University, Novosibirsk; Leont’eva, Natalya N., E-mail: n_n_leonteva@list.ru

2015-05-15

Abstracts: Thermal decomposition of Mg–Al and Ni–Al layered double hydroxides LDH at temperatures lower than 800 °C leads to the formation of oxides with different structures. Mg–Al oxide has a very defective structure and consists of octahedral layers as in periclase MgO and mixed octahedral–tetrahedral layers as in spinel MgAl{sub 2}O{sub 4}. Mixed Ni–Al oxide has a sandwich-like structure, consisting of a core with Al-doped NiO-like structure and some surface layers with spinel NiAl{sub 2}O{sub 4} structure epitaxial connected with the core. Suggested models were verified by simulation of X-ray diffraction patterns using DIFFaX code, as well as HRTEM, IR-,more » UV-spectroscopies, and XPS. - Graphical abstract: In the Mg–Al layered double hydroxide Al{sup 3+} ions migrate into interlayers during decomposition. The Mg–Al oxide represents sequence of octahedral and octahedral–tetrahedral spinel layers with vacancies. The Ni–Al oxide has a sandwich-like structure with NiO-like core and surface spinel layers as a result of migration of Al{sup 3+} ions on the surface. The models explain the presence and absence of “memory effect” for the Mg–Al and Ni–Al oxides, respectively. - Highlights: • We study products of Mg(Ni)–Al LDH decomposition by calcination at 500(400)–800 °C. • In Mg–Al/Ni–Al LDH Al ions migrate into interlayers/on the surface during decomposition. • Mg–Al oxide represents sequence of periclase- and spinel-like layers with vacancies. • Ni–Al oxide has a sandwich-like structure with NiO-like core and surface spinel layers. • The models explain the presence/absence of “memory effect” for Mg–Al/Ni–Al oxides.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Moonsoo; Kim, Jongmin; Cho, Jaehee

Graphical abstract: The presence of Chlorine in the outer surface resulted in a highly electro-negative surface states and an increase in the vacuum energy level. - Highlights: • We investigated the influence of chlorine surface treatment on ITO properties. • Chlorination induced the change of the electro-static potential in the outer surface. • Chlorine electro-chemical treatment of ITO is a simple, fast and effective technique. - Abstract: In this work, we investigate the influence of a chlorine-based electro-chemical surface treatment on the characteristics of indium tin oxide (ITO) including the work function, chemical composition, and phase transition. The treated ITOsmore » were characterized using X-ray photoelectron spectroscopy (XPS), ultra-violet photoelectron spectroscopy (UPS), 4-point probe measurements, and grazing incidence X-ray diffraction (GI-XRD). We confirmed a change of the chemical composition in the near-surface region of the ITO and the formation of indium-chlorine (In-Cl) bonds and surface dipoles (via XPS). In particular, the change of the electro-static potential in the outer surface was caused by chlorination. Due to the vacuum-level shift after the electro-chemical treatment in a dilute hydrochloric acid, the ITO work function was increased by ∼0.43 eV (via UPS); furthermore, the electro-negativity of the chlorine anions attracted electrons to emit them from the hole transport layer (HTL) to the ITO anodes, resulting in an increase of the hole-injection efficiency.« less

Corrosion investigation of fire-gilded bronze involving high surface resolution spectroscopic imaging

NASA Astrophysics Data System (ADS)

Masi, G.; Chiavari, C.; Avila, J.; Esvan, J.; Raffo, S.; Bignozzi, M. C.; Asensio, M. C.; Robbiola, L.; Martini, C.

2016-03-01

Gilded bronzes are often affected by severe corrosion, due to defects in the Au layer and Au/Cu alloy galvanic coupling, stimulated by large cathodic area of the gilded layer. Galvanic corrosion, triggered by gilding defects, leads to products growth at the Au/bronze interface, inducing blistering or break-up of the Au layer. In this context, fire-gilded bronze replicas prepared by ancient methods (use of spreadable Au-Hg paste) was specifically characterised by compiling complementary spectroscopic and imaging information before/after accelerated ageing with synthetic rain. Fire-gilded bronze samples were chemically imaged in cross-section at nano-metric scale (<200 nm) using high energy and lateral resolution synchrotron radiation photoemission (HR-SRPES) of core levels and valence band after conventional characterisation of the samples by Glow Discharge optical Emission Spectroscopy (GD-OES) and conventional X-ray photoelectron spectroscopy (XPS). We have found a net surface enrichment in Zn and Sn after fire-gilding and presence of metallic Hg, Pb and Cu within the Au layer. Moreover, the composition distribution of the elements together with their oxidation has been determined. It was also revealed that metallic phases including Hg and Pb remain in the gilding after corrosion. Moreover, selective dissolution of Zn and Cu occurs in the crater due to galvanic coupling, which locally induces relative Sn species enrichment (decuprification). The feasibility advantages and disadvantages of chemical imaging using HR-SRPES to study artworks have been investigated on representative replicas.

Evidence of room temperature ferromagnetism in argon/oxygen annealed TiO2 thin films deposited by electron beam evaporation technique

NASA Astrophysics Data System (ADS)

Mohanty, P.; Kabiraj, D.; Mandal, R. K.; Kulriya, P. K.; Sinha, A. S. K.; Rath, Chandana

2014-04-01

TiO2 thin films deposited by electron beam evaporation technique annealed in either O2 or Ar atmosphere showed ferromagnetism at room temperature. The pristine amorphous film demonstrates anatase phase after annealing under Ar/O2 atmosphere. While the pristine film shows a super-paramagnetic behavior, both O2 and Ar annealed films display hysteresis at 300 K. X-ray photo emission spectroscopy (XPS), Raman spectroscopy, Rutherford's backscattering spectroscopy (RBS), cross-sectional transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS) were used to refute the possible role of impurities/contaminants in magnetic properties of the films. The saturation magnetization of the O2 annealed film is found to be higher than the Ar annealed one. It is revealed from shifting of O 1s and Ti 2p core level spectra as well as from the enhancement of high binding energy component of O 1s spectra that the higher magnetic moment is associated with higher oxygen vacancies. In addition, O2 annealed film demonstrates better crystallinity, uniform deposition and smoother surface than that of the Ar annealed one from glancing angle X-ray diffraction (GAXRD) and atomic force microscopy (AFM). We conclude that although ferromagnetism is due to oxygen vacancies, the higher magnetization in O2 annealed film could be due to crystallinity, which has been observed earlier in Co doped TiO2 film deposited by pulsed laser deposition (Mohanty et al., 2012 [10]).

Band alignment of SiO2/(AlxGa1-x)2O3 (0 ≤ x ≤ 0.49) determined by X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Feng, Zhaoqing; Feng, Qian; Zhang, Jincheng; Li, Xiang; Li, Fuguo; Huang, Lu; Chen, Hong-Yan; Lu, Hong-Liang; Hao, Yue

2018-03-01

In this work, we report the investigation of the band alignment of SiO2/(AlxGa1-x)2O3 (0 ≤ x ≤ 0.49) utilizing the high resolution X-ray photoelectron spectroscopy (XPS) measurements. The single crystallinity and orientation of β-(AlxGa1-x)2O3 films grown on sapphire by pulsed laser deposition were studied with the high resolution X-ray diffraction. The Ga 2p3/2 and Si 2p core-level spectra as well as valence band spectra were used in the analysis of band alignment. As the mole fraction x of Al increases from 0 to 0.49, the bandgap and conduction band offset values of SiO2/(AlxGa1-x)2O3 increases from 4.9 to 5.6 eV and from 1.5 to 2.1 eV, respectively, while that of valence band offset decreases from 2.2 to 0.9 eV. From the results obtained, the energy band diagram of the studied SiO2/(AlxGa1-x)2O3 (0 ≤ x ≤ 0.49) interfaces is found to be of type I. Energy band lineups of SiO2/(AlxGa1-x)2O3 were thus determined which can be used as for Ga2O3 based power device technology.

PVP-Assisted Synthesis of Uniform Carbon Coated Li2S/CB for High-Performance Lithium-Sulfur Batteries.

PubMed

Chen, Lin; Liu, Yuzi; Zhang, Fan; Liu, Caihong; Shaw, Leon L

2015-11-25

The lithium-sulfur (Li-S) battery is a great alternative to the state-of-the-art lithium ion batteries due to its high energy density. However, low utilization of active materials, the insulating nature of sulfur or lithium sulfide (Li2S), and polysulfide dissolution in organic liquid electrolyte lead to low initial capacity and fast performance degradation. Herein, we propose a facile and viable approach to address these issues. This new approach entails synthesis of Li2S/carbon black (Li2S/CB) cores encapsulated by a nitrogen-doped carbon shell with polyvinylpyrrolidone (PVP) assistance. Combining energy-filtered transmission electron microscopy (EFTEM) elemental mappings, XPS and FTIR measurements, it is confirmed that the as-synthesized material has a structure of a Li2S/CB core with a nitrogen-doped carbon shell (denoted as Li2S/CB@NC). The Li2S/CB@NC cathode yields an exceptionally high initial capacity of 1020 mAh/g based on Li2S mass at 0.1 C with stable Coulombic efficiency of 99.7% over 200 cycles. Also, cycling performance shows the capacity decay per cycle as small as 0.17%. Most importantly, to further understand the materials for battery applications, field emission transmission electron microscopy (FETEM) and elemental mapping tests without exposure to air for Li2S samples in cycled cells are reported. Along with the first ever FETEM and field emission scanning electron microscopy (FESEM) investigations of cycled batteries, Li2S/CB@NC cathode demonstrates the capability of robust core-shell nanostructures for different rates and improved capacity retention, revealing Li2S/CB@NC designed here as an outstanding system for high-performance lithium-sulfur batteries.

X-PEEM, XPS and ToF-SIMS characterisation of xanthate induced chalcopyrite flotation: Effect of pulp potential

NASA Astrophysics Data System (ADS)

Kalegowda, Yogesh; Chan, Yuet-Loy; Wei, Der-Hsin; Harmer, Sarah L.

2015-05-01

Synchrotron-based X-ray photoemission electron microscopy (X-PEEM), X-ray photo-electron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS) and ultraviolet visible spectroscopy were used to characterize the flotation behaviour of chalcopyrite with xanthate at different processing conditions. The flotation recovery of chalcopyrite decreased from 97% under oxidative conditions (Eh ~ 385 mV SHE, pH 4) to 41% at a reductive potential of - 100 mV SHE (at pH 9). X-PEEM images constructed from the metal L3 absorption edges were used to produce near-edge X-ray absorption fine structure (NEXAFS) spectra from regions of interest, allowing the variability in mineral surface chemistry of each mineral particle to be analysed, and the effect of pulp potential (Eh) on the flotation of chalcopyrite to be determined. XPS, ToF-SIMS and NEXAFS analyses of chalcopyrite particles at oxidative conditions show that the surface was mildly oxidised and covered with adsorbed molecular CuEX. The Cu 2p XPS and Cu L2,3 NEXAFS spectra were dominated by CuI species attributed to bulk chalcopyrite and adsorbed CuEX. At a reductive potential of - 100 mV SHE, an increase in concentration of CuI and FeIII oxides and hydroxides was observed. X-PEEM analysis was able to show the presence of a low percentage of CuII oxides (CuO or Cu(OH)2) with predominantly CuI oxide (Cu2O) which is not evident in Cu 2p XPS spectra.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Olivieri, Giorgia; Brown, Matthew A., E-mail: matthew.brown@mat.ethz.ch; Parry, Krista M.

Over the past decade, energy-dependent ambient pressure X-ray photoelectron spectroscopy (XPS) has emerged as a powerful analytical probe of the ion spatial distributions at the vapor (vacuum)-aqueous electrolyte interface. These experiments are often paired with complementary molecular dynamics (MD) simulations in an attempt to provide a complete description of the liquid interface. There is, however, no systematic protocol that permits a straightforward comparison of the two sets of results. XPS is an integrated technique that averages signals from multiple layers in a solution even at the lowest photoelectron kinetic energies routinely employed, whereas MD simulations provide a microscopic layer-by-layer descriptionmore » of the solution composition near the interface. Here, we use the National Institute of Standards and Technology database for the Simulation of Electron Spectra for Surface Analysis (SESSA) to quantitatively interpret atom-density profiles from MD simulations for XPS signal intensities using sodium and potassium iodide solutions as examples. We show that electron inelastic mean free paths calculated from a semi-empirical formula depend strongly on solution composition, varying by up to 30% between pure water and concentrated NaI. The XPS signal thus arises from different information depths in different solutions for a fixed photoelectron kinetic energy. XPS signal intensities are calculated using SESSA as a function of photoelectron kinetic energy (probe depth) and compared with a widely employed ad hoc method. SESSA simulations illustrate the importance of accounting for elastic-scattering events at low photoelectron kinetic energies (<300 eV) where the ad hoc method systematically underestimates the preferential enhancement of anions over cations. Finally, some technical aspects of applying SESSA to liquid interfaces are discussed.« less

Versailles Project on Advanced Materials and Standards Interlaboratory Study on Measuring the Thickness and Chemistry of Nanoparticle Coatings Using XPS and LEIS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Belsey, Natalie A.; Cant, David J. H.; Minelli, Caterina

We report the results of a VAMAS (Versailles Project on Advanced Materials and Standards) inter-laboratory study on the measurement of the shell thickness and chemistry of nanoparticle coatings. Peptide-coated gold particles were supplied to laboratories in two forms: a colloidal suspension in pure water and; particles dried onto a silicon wafer. Participants prepared and analyzed these samples using either X-ray photoelectron spectroscopy (XPS) or low energy ion scattering (LEIS). Careful data analysis revealed some significant sources of discrepancy, particularly for XPS. Degradation during transportation, storage or sample preparation resulted in a variability in thickness of 53 %. The calculation methodmore » chosen by XPS participants contributed a variability of 67 %. However, variability of 12 % was achieved for the samples deposited using a single method and by choosing photoelectron peaks that were not adversely affected by instrumental transmission effects. The study identified a need for more consistency in instrumental transmission functions and relative sensitivity factors, since this contributed a variability of 33 %. The results from the LEIS participants were more consistent, with variability of less than 10 % in thickness and this is mostly due to a common method of data analysis. The calculation was performed using a model developed for uniform, flat films and some participants employed a correction factor to account for the sample geometry, which appears warranted based upon a simulation of LEIS data from one of the participants and comparison to the XPS results.« less

Determination of trace metals in TSP and PM2.5 materials collected in the Metropolitan Area of Monterrey, Mexico: A characterization study by XPS, ICP-AES and SEM-EDS

NASA Astrophysics Data System (ADS)

González, Lucy T.; Longoria Rodríguez, F. E.; Sánchez-Domínguez, M.; Cavazos, Aleyda; Leyva-Porras, C.; Silva-Vidaurri, L. G.; Askar, Karim Acuña; Kharissov, B. I.; Villarreal Chiu, J. F.; Alfaro Barbosa, J. M.

2017-11-01

The concentration levels of trace metals of toxicological importance were evaluated in the total suspended particles (TSP) and particulate matter smaller than 2.5 μm (PM2.5) collected in the Metropolitan Area of Monterrey (MAM) in Mexico. Samples were characterized by inductively coupled plasma atomic emission spectroscopy (ICP-AES), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy with an energy-dispersive spectroscopy system (SEM-EDS). In addition, the data were statistically treated by the methodology of Pearson Correlation (PC) and Principal Components Analysis (PCA) to identify the possible emitting sources. Surface analysis of the particulate matter (PM) by XPS revealed that the most abundant elements were Ca, Al, Na, Zn, Cu and Mg. The deconvolution of the Ca2p, Zn2p and Cu2p signals showed that the main contributors were CaCO3, ZnO and Cu/Cu2O, respectively. The bulk analysis of the PM by ICP-AES showed Fe, Cu and Zn as the most abundant elements. Fe-rich particles presented two different morphologies: the prismatic particles were associated with a natural origin, while the spherical particles with anthropogenic sources. The Zn and Cu were predominantly observed in the sampling stations with high vehicular traffic, and the emitting sources were associated with the burning of fuels from automobiles and the wear of the tires and brakes. The highest concentration of Pb was detected in the sampling station located near the industrial zones, and its cause was associated with the ceramic and glass industries, the burning of fuel oil in power plants and the production of lead-based batteries for automobiles.

Colour changes by laser irradiation of reddish building limestones

NASA Astrophysics Data System (ADS)

Grossi, C. M.; Benavente, D.

2016-10-01

We have used X-ray photoelectron spectroscopy (XPS) as a novel method to investigate the causes of colour changes in a reddish limestone under irradiation by a Q-switched Nd:YAG 1064 nm laser. We irradiated clean dry and wet surfaces of Pidramuelle Roja, a building stone frequently used in the Asturian heritage, at fluences ranging from 0.12 to 1.47 J cm-2. We measured the colour coordinates and undertook XPS analysis of the state of oxidation of iron both before and after irradiation. Visible colour changes and potential aesthetic damage occurred on dry surfaces from a fluence of 0.31 J cm-2, with the stone showing a greening effect and very intense darkening. The colour change on dry surfaces was considerably higher than on wet surfaces, which at the highest fluence (1.47 J cm-2) was also above the human visual detection threshold. The use of XPS demonstrated that the change in colour (chroma and hue) is associated with a reduction in the iron oxidation state on dry surfaces during laser irradiation. This points out to a potential routinary use of XPS to analyse causes of colour changes during laser cleaning in other types of coloured building stones.

Effects of the low Earth orbit space environment on the surface chemistry of Kapton polyimide film: An XPS study

NASA Technical Reports Server (NTRS)

Lee, Myung; Rooney, William; Whiteside, James

1992-01-01

Kapton H (DuPont Trademark) polyimide specimens exposed to the low earth (LEO) space environment suffered significant weathering with surface erosions of approximately 8.0 microns. Despite these effects, no significant changes in bulk chemistry were observed. X-ray photoelectron spectroscopy (XPS) was used to determine local changes induced from approximately 25 percent in 1980 vintage ground control specimens to nearly 53 percent in space exposed specimens. The greatest increase was observed for the divalent oxygen moieties, although a slight increase in carbonyl oxygen was also measured. Furthermore, the chemical shifts of all XPS peaks of space-exposed Kapton are shifted to higher energy. This is consistent with a higher oxidation state of the space exposed surface. Finally, space exposed specimens had distinct silicon peaks (2p 100 eV and 2s 149 eV) in their XPS spectra in agreement with widespread reports of silicon contamination throughout the LDEF satellite. These results are discussed in terms of surface reactivity of the polyimide exposed to the LEO environment and the chemical nature of contaminants deposited on flight surfaces due to satellite outgassing.

Study of mesoporous CdS-quantum-dot-sensitized TiO2 films by using X-ray photoelectron spectroscopy and AFM

PubMed Central

Wojcieszak, Robert; Raj, Gijo

2014-01-01

Summary CdS quantum dots were grown on mesoporous TiO2 films by successive ionic layer adsorption and reaction processes in order to obtain CdS particles of various sizes. AFM analysis shows that the growth of the CdS particles is a two-step process. The first step is the formation of new crystallites at each deposition cycle. In the next step the pre-deposited crystallites grow to form larger aggregates. Special attention is paid to the estimation of the CdS particle size by X-ray photoelectron spectroscopy (XPS). Among the classical methods of characterization the XPS model is described in detail. In order to make an attempt to validate the XPS model, the results are compared to those obtained from AFM analysis and to the evolution of the band gap energy of the CdS nanoparticles as obtained by UV–vis spectroscopy. The results showed that XPS technique is a powerful tool in the estimation of the CdS particle size. In conjunction with these results, a very good correlation has been found between the number of deposition cycles and the particle size. PMID:24605274

Confirmation of Incorporation of Cu and Se Ions in Applied p- and n-Type-Doped Sb2S3 by Photoemission Spectroscopy

NASA Astrophysics Data System (ADS)

Validžić, Ivana Lj; Popović, Maja; Lojpur, Vesna; Bundaleski, Nenad; Rakočević, Zlatko

2018-04-01

The effect of incorporating copper (Cu) and selenium (Se) ions into stibnite (Sb2S3) lattice was investigated using x-ray photoelectron spectroscopy (XPS). The incorporation of Cu and Se ions was verified by comparing the XPS spectra of the undoped (amorphous Sb2S3), doped ( p and n-doped) and pure Se and Cu-acetate powders. The main photoelectron Cu 2p1/2 (951.8 eV) and Cu 2p3/2 (932.1 eV) lines derived from the Cu-doped and Cu-acetate powder samples were clearly observed, whereas in the undoped sample, none of the characteristic lines of Cu were detected. The Se Auger line (138.6 eV), the only line of Se which does not coincide with the lines of Sb and S, was successfully detected in an Se-doped XPS sample and the spectrum of pure Se, while Se in the undoped sample was not found. Further, the XPS measurements revealed the relative amounts of Cu and Se in antimony sulfide, as well as the oxidation state of copper incorporated into the matrix.

NEXAFS and XPS characterization of molecular oxygen adsorbed on Ni(100) at 80 K

NASA Astrophysics Data System (ADS)

Kim, C. M.; Jeong, H. S.; Kim, E. H.

2000-07-01

X-ray photoelectron spectroscopy (XPS), thermal desorption spectroscopy (TDS) and near edge extended X-ray absorption fine structure (NEXAFS) have been combined to investigate the adsorption of oxygen on Ni(100) at 80 K. Three O(1s) XPS features were observed at 530.0, 531.1 and 534.7 eV when the Ni(100) surface was exposed to 600 L of oxygen at 80 K. They are assigned as O 2-, O 1- and molecular oxygen species, respectively. The presence of molecular oxygen has been confirmed by TDS and NEXAFS. Molecular O 2 on Ni(100) is oriented perpendicular to the surface, and the OO bond length is estimated to be 1.24 Å, based on the NEXAFS σ ∗ resonance energy.

New Pt/Alumina model catalysts for STM and in situ XPS studies

NASA Astrophysics Data System (ADS)

Nartova, Anna V.; Gharachorlou, Amir; Bukhtiyarov, Andrey V.; Kvon, Ren I.; Bukhtiyarov, Valerii I.

2017-04-01

The new Pt/alumina model catalysts for STM and in situ XPS studies based on thin alumina film formed over the conductive substrate are proposed. Procedure of platinum deposition developed for porous alumina was adapted for the model alumina support. The set of Pt/AlOx-film samples with the different mean platinum particle size was prepared. Capabilities of in situ XPS investigations of the proposed catalysts were demonstrated in study of NO decomposition on platinum nanoparticles. It is shown that proposed model catalysts behave similarly to Pt/γ-Al2O3 and provide the new opportunities for the instrumental studies of platinum catalysts due to resolving several issues (charging, heating, screening) that are typical for the investigation of the porous oxide supported catalysts.

Laser techniques for spectroscopy of core-excited atomic levels

NASA Technical Reports Server (NTRS)

Harris, S. E.; Young, J. F.; Falcone, R. W.; Rothenberg, J. E.; Willison, J. R.

1982-01-01

We discuss three techniques which allow the use of tunable lasers for high resolution and picosecond time scale spectroscopy of core-excited atomic levels. These are: anti-Stokes absorption spectroscopy, laser induced emission from metastable levels, and laser designation of selected core-excited levels.

Comparison of predicted engine core noise with current and proposed aircraft noise certification requirements

NASA Technical Reports Server (NTRS)

Vonglahn, U. H.; Groesbeck, D. E.

1981-01-01

Predicted engine core noise levels are compared with measured total aircraft noise levels and with current and proposed federal noise certification requirements. Comparisons are made at the FAR-36 measuring stations and include consideration of both full- and cutback-power operation at takeoff. In general, core noise provides a barrier to achieving proposed EPA stage 5 noise levels for all types of aircraft. More specifically, core noise levels will limit further reductions in aircraft noise levels for current widebody commercial aircraft.

Direct evaluation of electrical dipole moment and oxygen density ratio at high-k dielectrics/SiO2 interface by X-ray photoelectron spectroscopy analysis

NASA Astrophysics Data System (ADS)

Fujimura, Nobuyuki; Ohta, Akio; Ikeda, Mitsuhisa; Makihara, Katsunori; Miyazaki, Seiichi

2018-04-01

The electrical dipole moment at an ultrathin high-k (HfO2, Al2O3, TiO2, Y2O3, and SrO)/SiO2 interface and its correlation with the oxygen density ratio at the interface have been directly evaluated by X-ray photoelectron spectroscopy (XPS) under monochromatized Al Kα radiation. The electrical dipole moment at the high-k/SiO2 interface has been measured from the change in the cut-off energy of secondary photoelectrons. Moreover, the oxygen density ratio at the interface between high-k and SiO2 has been estimated from cation core-line signals, such as Hf 4f, Al 2p, Y 3d, Ti 2p, Sr 3d, and Si 2p. We have experimentally clarified the relationship between the measured electrical dipole moment and the oxygen density ratio at the high-k/SiO2 interface.

Role of excess ligand and effect of thermal treatment in hybrid inorganic-organic EUV resists

NASA Astrophysics Data System (ADS)

Mattson, Eric C.; Rupich, Sara M.; Cabrera, Yasiel; Chabal, Yves J.

2018-03-01

The chemical structure and thermal reactivity of recently discovered inorganic-organic hybrid resist materials are characterized using a combination of in situ and ex situ infrared (IR) spectroscopy and x-ray photoemission spectroscopy (XPS). The materials are comprised of a small HfOx core capped with methacrylic acid ligands that form a combined hybrid cluster, HfMAA. The observed IR modes are consistent with the calculated modes predicted from the previously determined x-ray crystal structure of the HfMAA-12 cluster, but also contain extrinsic hydroxyl groups. We find that the water content of the films is dependent on the concentration of excess ligand added to the solution. The effect of environment used during post-application baking (PAB) is studied and correlated to changes in solubility of the films. In doing so, we find that hydroxylation of the clusters results in formation of additional Hf-O-Hf linkages upon heating, which in turn impacts the solubility of the films.

A novel methanol sensor based on gas-penetration through a porous polypyrrole-coated polyacrylonitrile nanofiber mat.

PubMed

Jun, Tae-Sun; Ho, Thi Anh; Rashid, Muhammad; Kim, Yong Shin

2013-09-01

In this work, we propose a novel chemoresistive gas sensor operated under a vertical analyte flow passing through a permeable sensing membrane. Such a configuration is different from the use of a planar sensor implemented under a conventional horizontal flow. A highly porous core-shell polyacrylonitrile-polypyrrole (PAN@PPy) nanofiber mat was prepared as the sensing element via electrospinning and two-step vapor-phase polymerization (VPP). Various analysis methods such as SEM, TEM, FT-IR and XPS measurements were employed in order to characterize structural features of the porous sensing mat. These analyses confirmed that very thin (ca. 10 nm) conductive PPy sheath layers were deposited by VPP on electrospun PAN nanofibers with an average diameter of 258 nm. Preliminary results revealed that the gas penetration-type PAN@PPy sensor had a higher sensor response and shorter detection and recovery times upon exposure to methanol analyte when compared with a conventional horizontal flow sensor due to efficient and fast analyte transfer into the sensing layer.

A novel magnetic Fe@Au core-shell nanoparticles anchored graphene oxide recyclable nanocatalyst for the reduction of nitrophenol compounds.

PubMed

Gupta, Vinod Kumar; Atar, Necip; Yola, Mehmet Lütfi; Üstündağ, Zafer; Uzun, Lokman

2014-01-01

In this study, a novel catalyst based on Fe@Au bimetallic nanoparticles involved graphene oxide was prepared and characterized by transmission electron microscope (TEM), and x-ray photoelectron spectroscopy (XPS). The nanomaterial was used in catalytic reductions of 4-nitrophenol and 2-nitrophenol in the presence of sodium borohydride. The experimental parameters such as temperature, the dosage of catalyst and the concentration of sodium borohydride were studied. The rates of catalytic reduction of the nitrophenol compounds have been found as the sequence: 4-nitrophenol>2-nitrophenol. The kinetic and thermodynamic parameters of nitrophenol compounds were determined. Activation energies were found as 2.33 kcal mol(-1) and 3.16 kcal mol(-1) for 4-nitrophenol and 2-nitrophenol, respectively. The nanomaterial was separated from the product by using a magnet and recycled after the reduction of nitrophenol compounds. The recyclable of the nanocatalyst is economically significant in industry. Copyright © 2013 Elsevier Ltd. All rights reserved.

Preparation and characterization of biocompatible magnetic carbon nanotubes

NASA Astrophysics Data System (ADS)

Shan, Yan; Chen, Kezheng; Yu, Xuegang; Gao, Lian

2010-11-01

Magnetic carbon nanotubes consisting of multi-wall carbon nanotubes (MWNTs) core and Fe3O4 shell were successfully prepared by in situ thermal decomposition of Fe(acac)3 or FeCl3 or Fe(CO)5 in 2-pyrrolidone containing acid treated MWNTs at 240 °C with the protection of nitrogen gas. The samples were characterized by TEM, XRD, SEAD, XPS and superconducting quantum interference device. Also, their biocompatibility was compared with naked carbon nanotubes. The results showed that after coated with Fe3O4 nanoparticles, the obtained magnetic carbon nanotubes show superparamagnetic characteristic at room temperature, and their blocking temperature is about 80 K. The magnetic properties of the nanotubes are relevant to the content of magnetic particles, increasing content of magnetic nanoparticles leads to higher blocking temperature and saturation magnetization. The results of antimicrobial activities to bacterial cells (Escherichia coli) showed that the MWNTs have antimicrobial activity, while the magnetic nanotubes are biocompatible even with a higher concentration than that of MWNTs.

New technique for the direct measurement of core noise from aircraft engines

NASA Technical Reports Server (NTRS)

Krejsa, E. A.

1981-01-01

A new technique is presented for directly measuring the core noise levels from gas turbine aircraft engines. The technique requires that fluctuating pressures be measured in the far-field and at two locations within the engine core. The cross-spectra of these measurements are used to determine the levels of the far-field noise that propagated from the engine core. The technique makes it possible to measure core noise levels even when other noise sources dominate. The technique was applied to signals measured from an AVCO Lycoming YF102 turbofan engine. Core noise levels as a function of frequency and radiation angle were measured and are presented over a range of power settings.

X-ray photoelectron spectroscopy study of radiofrequency sputtered chromium bromide, molybdenum disilicide, and molybdenum disulfide coatings and their friction properties

NASA Technical Reports Server (NTRS)

Wheeler, D. R.; Brainard, W. A.

1977-01-01

Radiofrequency sputtered coatings of CRB2, MOSI2, and MOS2 were examined by X-ray photoelectron spectroscopy. The effects of sputtering target history, deposition time, RF power level, and substrate bias on film composition were studied. Friction tests were run on RF sputtered surfaces of 440-C steel to correlate XPS data with lubricating properties. Significant deviations from stoichiometry and high oxide levels for all three compounds were related to target outgassing. The effect of biasing on these two factors depended on the compound. Improved stoichiometry correlated well with good friction and wear properties.

Fracture surface analysis in composite and titanium bonding: Part 1: Titanium bonding

NASA Technical Reports Server (NTRS)

Sanderson, K. A.; Wightman, J. P.

1985-01-01

Fractured lap shear Ti 6-4 adherends bonded with polyphenyquinoxaline (PPQ) and polysulfone were analyzed. The effects of adherend pretreatment, stress level, thermal aging, anodizing voltage, and modified adhesive of Ti 6-4 adherend bonded with PPQ on lap shear strength were studied. The effect of adherend pretreatment on lap shear strength was investigated for PS samples. Results of scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) used to study the surface topography and surface composition are also discussed.

A Cul-3-BTB ubiquitylation pathway regulates junctional levels and asymmetry of core planar polarity proteins

PubMed Central

Strutt, Helen; Searle, Elizabeth; Thomas-MacArthur, Victoria; Brookfield, Rosalind; Strutt, David

2013-01-01

The asymmetric localisation of core planar polarity proteins at apicolateral junctions is required to specify cell polarity in the plane of epithelia. This asymmetric distribution of the core proteins is proposed to require amplification of an initial asymmetry by feedback loops. In addition, generation of asymmetry appears to require the regulation of core protein levels, but the importance of such regulation and the underlying mechanisms is unknown. Here we show that ubiquitylation acts through more than one mechanism to control core protein levels in Drosophila, and that without this regulation cellular asymmetry is compromised. Levels of Dishevelled at junctions are regulated by a Cullin-3-Diablo/Kelch ubiquitin ligase complex, the activity of which is most likely controlled by neddylation. Furthermore, activity of the deubiquitylating enzyme Fat facets is required to maintain Flamingo levels at junctions. Notably, ubiquitylation does not alter the total cellular levels of Dishevelled or Flamingo, but only that of the junctional population. When junctional core protein levels are either increased or decreased by disruption of the ubiquitylation machinery, their asymmetric localisation is reduced and this leads to disruption of planar polarity at the tissue level. Loss of asymmetry by altered core protein levels can be explained by reference to feedback models for amplification of asymmetry. PMID:23487316

A poly-epoxy surface explored by Hartree-Fock ΔSCF simulations of C1s XPS spectra

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gavrielides, A.; Duguet, T., E-mail: thomas.duguet@ensiacet.fr, E-mail: Paul.Bagus@unt.edu; Esvan, J.

Whereas poly-epoxy polymers represent a class of materials with a wide range of applications, the structural disorder makes them difficult to model. In the present work, we use good experimental model samples in the sense that they are pure, fully polymerized, flat and smooth, defect-free, and suitable for ultrahigh vacuum x-ray photoelectron spectroscopy, XPS, experiments. In parallel, we perform Hartree-Fock, HF, calculations of the binding energies, BEs, of the C1s electrons in a model molecule composed of the two constituents of the poly-epoxy sample. These C1s BEs were determined using the HF ΔSCF method, which is known to yield accuratemore » values, especially for the shifts of the BEs, ΔBEs. We demonstrate the benefits of combining rigorous theory with careful XPS measurements in order to obtain correct assignments of the C1s XPS spectra of the polymer sample. Both the relative binding energies—by the ΔSCF method—and relative intensities—in the sudden approximation, SA, are calculated. It results in an excellent match with the experimental spectra. We are able to identify 9 different chemical environments under the C1s peak, where an exclusively experimental work would have found only 3 contributions. In addition, we observe that some contributions are localized at discrete binding energies, whereas others allow a much wider range because of the variation of their second neighbor bound polarization. Therefore, HF-ΔSCF simulations significantly increase the spectral resolution of XPS and thus offer a new avenue for the exploration of the surface of polymers.« less

Morphology and Chemical Composition of soot particles emitted by Wood-burning Cook-Stoves: a HRTEM, XPS and Elastic backscattering Studies.

NASA Astrophysics Data System (ADS)

Carabali-Sandoval, G. A., Sr.; Castro, T.; Peralta, O.; De la Cruz, W.; Días, J.; Amelines, O.; Rivera-Hernández, M.; Varela, A.; Muñoz-Muñoz, F.; Policroniades, R.; Murillo, G.; Moreno, E.

2014-12-01

The morphology, microstructure and the chemical composition on surface of soot particles were studied by using high resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS) and elastic backscattering spectrometry. In order to obtain freshly soot particles emitted by home-made wood-burning cook stoves, copper grids for Transmission Electron Microscope (TEM) were placed on the last two of an 8-stages MOUDI cascade impactor. The analysis of HRTEM micrographs revealed the nanostructure and the particle size of soot particles. The XPS survey spectra show a large carbon peak around 285 eV and the oxygen signal at 533 eV. Some differences observed in the carbon/oxygen (C/O) ratio of the particles probably depend on the combustion process efficiency of each cook-stove analyzed. The C-1s XPS spectra show an asymmetric broad peak and other with low intensity that corresponds to sp2 and sp3hybridization, which were fitted with a convolution using Gaussian functions. Elastic backscattering technique allows a chemical elemental analysis of samples and confirms the presence of C, O and Si observed by XPS. Additionally, the morphological properties of soot aggregates were analyzed calculating the border-based fractal dimension (Df). Particles exhibit complex shapes with high values of Df. Also, real-time absorption (σabs) and scattering (σsct) coefficients of fine (with aerodynamic diameter < 2.5 µm) soot particles were measured. The trend in σabs and σsct indicate that the cooking process has two important combustion stages which varied in its flaming strength, being vigorous in the first stage and soft in the second one.

Quantitative interpretation of molecular dynamics simulations for X-ray photoelectron spectroscopy of aqueous solutions

NASA Astrophysics Data System (ADS)

Olivieri, Giorgia; Parry, Krista M.; Powell, Cedric J.; Tobias, Douglas J.; Brown, Matthew A.

2016-04-01

Over the past decade, energy-dependent ambient pressure X-ray photoelectron spectroscopy (XPS) has emerged as a powerful analytical probe of the ion spatial distributions at the vapor (vacuum)-aqueous electrolyte interface. These experiments are often paired with complementary molecular dynamics (MD) simulations in an attempt to provide a complete description of the liquid interface. There is, however, no systematic protocol that permits a straightforward comparison of the two sets of results. XPS is an integrated technique that averages signals from multiple layers in a solution even at the lowest photoelectron kinetic energies routinely employed, whereas MD simulations provide a microscopic layer-by-layer description of the solution composition near the interface. Here, we use the National Institute of Standards and Technology database for the Simulation of Electron Spectra for Surface Analysis (SESSA) to quantitatively interpret atom-density profiles from MD simulations for XPS signal intensities using sodium and potassium iodide solutions as examples. We show that electron inelastic mean free paths calculated from a semi-empirical formula depend strongly on solution composition, varying by up to 30% between pure water and concentrated NaI. The XPS signal thus arises from different information depths in different solutions for a fixed photoelectron kinetic energy. XPS signal intensities are calculated using SESSA as a function of photoelectron kinetic energy (probe depth) and compared with a widely employed ad hoc method. SESSA simulations illustrate the importance of accounting for elastic-scattering events at low photoelectron kinetic energies (<300 eV) where the ad hoc method systematically underestimates the preferential enhancement of anions over cations. Finally, some technical aspects of applying SESSA to liquid interfaces are discussed.

Demonstration of an ultrasensitive refractive-index plasmonic sensor by enabling its quadrupole resonance in phase interrogation.

PubMed

Lee, Hsin-Cheng; Li, Chung-Tien; Chen, How-Foo; Yen, Ta-Jen

2015-11-15

We present an ultrasensitive plasmonic sensing system by introducing a nanostructured X-shaped plasmonic sensor (XPS) and measuring its localized optical properties in phase interrogation. Our tailored XPS exhibits two major resonant modes of a low-order dipole and a high-order quadrupole, between which the quadrupole resonance allows an ultrahigh sensitivity, due to its higher quality factor. Furthermore, we design an in-house common-path phase-interrogation system, in contrast to conventional wavelength-interrogation methods, to achieve greater sensing capability. The experimental measurement shows that the sensing resolution of the XPS reaches 1.15×10(-6) RIU, not only two orders of magnitude greater than the result of the controlled extinction measurement (i.e., 9.90×10(-5) RIU), but also superior than current reported plasmonic sensors.

RECENT XPS STUDIES OF THE EFFECT OF PROCESSING ON NB SRF SURFACES

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hui Tian; Binping Xiao; Michael Kelley

XPS studies have consistently shown that Nb surfaces for SRF chiefly comprise of a few nm of Nb2O5 on top of Nb metal, with minor amounts of Nb sub-oxides. Nb samples after BCP/EP treatment with post-baking at the various conditions have been examined by using synchrotron based XPS. Despite the confounding influence of surface roughness, certain outcomes are clear. Lower-valence Nb species are always and only associated with the metal/oxide interface, but evidence for an explicit layer structure or discrete phases is lacking. Post-baking without air exposure shows decreased oxide layer thickness and increased contribution from lower valence species, butmore » spectra obtained after subsequent air exposure cannot be distinguished from those obtained prior to baking, though the SRF performance improvement remains.« less

Efficient red luminescence from organic-soluble Au25 clusters by ligand structure modification

NASA Astrophysics Data System (ADS)

Mathew, Ammu; Varghese, Elizabeth; Choudhury, Susobhan; Pal, Samir Kumar; Pradeep, T.

2015-08-01

An efficient method to enhance visible luminescence in a visibly non-luminescent organic-soluble 4-(tert butyl)benzyl mercaptan (SBB)-stabilized Au25 cluster has been developed. This method relies mainly on enhancing the surface charge density on the cluster by creating an additional shell of thiolate on the cluster surface, which enhances visible luminescence. The viability of this method has been demonstrated by imparting red luminescence to various ligand-protected quantum clusters (QCs), observable to the naked eye. The bright red luminescent material derived from Au25SBB18 clusters was characterized using UV-vis and luminescence spectroscopy, TEM, SEM/EDS, XPS, TG, ESI and MALDI mass spectrometry, which collectively proposed an uncommon molecular formula of Au29SBB24S, suggested to be due to different stapler motifs protecting the Au25 core. The critical role of temperature on the emergence of luminescence in QCs has been studied. The restoration of the surface ligand shell on the Au25 cluster and subsequent physicochemical modification to the cluster were probed by various mass spectral and spectroscopic techniques. Our results provide fundamental insights into the ligand characteristics determining luminescence in QCs.An efficient method to enhance visible luminescence in a visibly non-luminescent organic-soluble 4-(tert butyl)benzyl mercaptan (SBB)-stabilized Au25 cluster has been developed. This method relies mainly on enhancing the surface charge density on the cluster by creating an additional shell of thiolate on the cluster surface, which enhances visible luminescence. The viability of this method has been demonstrated by imparting red luminescence to various ligand-protected quantum clusters (QCs), observable to the naked eye. The bright red luminescent material derived from Au25SBB18 clusters was characterized using UV-vis and luminescence spectroscopy, TEM, SEM/EDS, XPS, TG, ESI and MALDI mass spectrometry, which collectively proposed an uncommon molecular formula of Au29SBB24S, suggested to be due to different stapler motifs protecting the Au25 core. The critical role of temperature on the emergence of luminescence in QCs has been studied. The restoration of the surface ligand shell on the Au25 cluster and subsequent physicochemical modification to the cluster were probed by various mass spectral and spectroscopic techniques. Our results provide fundamental insights into the ligand characteristics determining luminescence in QCs. Electronic supplementary information (ESI) available: Additional data on characterization of red luminescent Au29 QC and comparison with parent Au25SBB18 are given. See DOI: 10.1039/c5nr03457d

Multicharged Ion Promoted Desorption (MIPD) of Reaction Co-Products

DTIC Science & Technology

2015-02-13

measurements of surface modifications using mass spectrometry, Raman spectroscopy and XPS were made to 1. REPORT DATE (DD-MM-YYYY) 4. TITLE AND...desorption and ex-situ measurements of surface modifications using mass spectrometry, Raman spectroscopy and XPS were made to determine ion-induced...irradiations were made with the samples at normal incidence to the incoming beams and post-analysis of these samples was achieved using Raman spectroscopy. It

Surface modification of EPDM rubber by plasma treatment.

PubMed

Grythe, Kai Frode; Hansen, Finn Knut

2006-07-04

The effect of argon, oxygen, and nitrogen plasma treatment of solvent cast EPDM rubber films has been investigated by means of atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), and surface energy measurements. Plasma treatment leads to changes in the surface energy from 25 to 70 mN/m. Treatment conditions influenced both the changes in surface energy and the stability, and it became more difficult to obtain good contact angle measurements after longer (> ca. 4 min) treatment times, probably because of an increasingly uneven surface structure. XPS analyses revealed that up to 20 at. % oxygen can be easily incorporated and that variations of approximately 5% can be controlled by the plasma conditions. Oxygen was mainly found in hydroxyl groups, but also as carbonyl and carboxyl. XPS analyses showed more stable surfaces than expected from contact angles, probably because XPS analysis is less surface sensitive than contact angle measurements. AFM measurements revealed different surface structures with the three gases. The surface roughness increased generally with treatment time, and dramatic changes could be observed at longer times. At short times, surface energy changes were much faster than the changes in surface structure, showing that plasma treatment conditions can be utilized to tailor both surface energies and surface structure of EPDM rubber.

Surface analysis of 316 stainless steel treated with cold atmospheric plasma

NASA Astrophysics Data System (ADS)

Williams, David F.; Kellar, Ewen J. C.; Jesson, David A.; Watts, John F.

2017-05-01

The surface of 316 stainless steel has been modified using cold atmospheric plasma (CAP) to increase the surface free energy (by cleaning the and chemically activating the surface)IN preparation for subsequent processes such as painting, coating or adhesive bonding. The analyses carried out, on CAP treated 316 stainless steel surfaces, includes X-ray photoelectron spectroscopy (XPS), imaging XPS (iXPS), and surface free energy (SFE) analysis using contact angle measurements. The CAP treatment is shown to increase the SFE of as-received 316 stainless steel from ∼39 mJ m-1 to >72 mJ m-1 after a short exposure to the plasma torch. This was found to correlate to a reduction in adventitious carbon, as determined by XPS analysis of the surface. The reduction from ∼90 at% to ∼30% and ∼39 at%, after being plasma treated for 5 min and 15 s respectively, shows that the process is relatively quick at changing the surface. It is suggested that the mechanism that causes the increase in surface free energy is chain scission of the hydrocarbon contamination triggered by free electrons in the plasma plume followed by chemical functionalisation of the metal oxide surface and some of the remaining carbon contamination layer.

Morphological, chemical and structural characterisation of deciduous enamel: SEM, EDS, XRD, FTIR and XPS analysis.

PubMed

Zamudio-Ortega, C M; Contreras-Bulnes, R; Scougall-Vilchis, R J; Morales-Luckie, R A; Olea-Mejía, O F; Rodríguez-Vilchis, L E

2014-09-01

The purpose of this study was to characterise the enamel surface of sound deciduous teeth in terms of morphology, chemical composition, structure and crystalline phases. The enamel of 30 human deciduous teeth was examined by: Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Spectroscopy (EDS), X-ray Powder Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), and X-ray Photoelectron Spectroscopy (XPS). Chemical differences between incisors and canines were statistically evaluated using the Mann-Whitney U test (p ≤ 0.05). Three enamel patterns were observed by SEM: 'mostly smooth with some groves', 'abundant microporosities' and 'exposed prisms'. The average Ca/P molar ratios were 1.37 and 1.03 by EDS and XPS, respectively. The crystallite size determined by XRD was 210.82 ± 16.78 Å. The mean ratio between Ca bonded to phosphate and Ca bonded to hydroxyl was approximately 10:1. The enamel of sound deciduous teeth showed two main patterns: 'mostly smooth with some groves' and 'abundant microporosities'. 'Exposed prisms' was a secondary pattern. There were slight variations among the Ca/P molar ratios found by EDS and XPS, suggesting differences in the mineral content from the enamel surface to the interior. The crystalline phases found in enamel were hydroxyapatite and carbonate apatite, with major type B than type A carbonate incorporation.

Oxidation of palladium on Au(111) and ZnO(0001) supports

DOE PAGES

Lallo, J.; Tenney, S. A.; Kramer, A.; ...

2014-10-21

The oxidation of supported Pd-deposits on Au(111) and ZnO(0001) single crystals has been studied by x- ray photoemission spectroscopy (XPS). Oxidation has been carried out ex-situ in a high-pressure cell with subsequent vacuum-transfer and characterization by XPS in ultrahigh vacuum (UHV), as well as using in-situ characterization by synchrotron based near-ambient pressure XPS. On Au(111) alloying of Pd with the substrate competes with oxidation and only sufficiently thick Pd films have been found to oxidize. For Pd on ZnO the oxidation conditions depend on the amount of deposited Pd. Thicker Pd deposits behave similar to bulk Pd, while thinner filmsmore » oxidize already at lower temperatures. Interestingly, for very small amounts of Pd, in-situ XPS shows full oxidation at room temperature and at less than 0.6 mbar O₂ pressure. This indicates a lowering of the kinetic barriers for oxidation of very small supported Pd-clusters. The formed oxide is, however, not stable in UHV and a slow reduction is observed. The instability of this oxide indicates that the Pd-oxide formed at the interface to ZnO may have different chemical properties compared to bulk PdO or surface oxides on Pd.« less

Composite targets in HiPIMS plasmas: Correlation of in-vacuum XPS characterization and optical plasma diagnostics

NASA Astrophysics Data System (ADS)

Layes, Vincent; Monje, Sascha; Corbella, Carles; Schulz-von der Gathen, Volker; von Keudell, Achim; de los Arcos, Teresa

2017-05-01

In-vacuum characterization of magnetron targets after High Power Impulse Magnetron Sputtering (HiPIMS) has been performed by X-ray photoelectron spectroscopy (XPS). Al-Cr composite targets (circular, 50 mm diameter) mounted in two different geometries were investigated: an Al target with a small Cr disk embedded at the racetrack position and a Cr target with a small Al disk embedded at the racetrack position. The HiPIMS discharge and the target surface composition were characterized in parallel for low, intermediate, and high power conditions, thus covering both the Ar-dominated and the metal-dominated HiPIMS regimes. The HiPIMS plasma was investigated using optical emission spectroscopy and fast imaging using a CCD camera; the spatially resolved XPS surface characterization was performed after in-vacuum transfer of the magnetron target to the XPS chamber. This parallel evaluation showed that (i) target redeposition of sputtered species was markedly more effective for Cr atoms than for Al atoms; (ii) oxidation at the target racetrack was observed even though the discharge ran in pure Ar gas without O2 admixture, the oxidation depended on the discharge power and target composition; and (iii) a bright emission spot fixed on top of the inserted Cr disk appeared for high power conditions.

A quantitative model and the experimental evaluation of the liquid fuel layer for the downward flame spread of XPS foam.

PubMed

Luo, Shengfeng; Xie, Qiyuan; Tang, Xinyi; Qiu, Rong; Yang, Yun

2017-05-05

The objective of this work is to investigate the distinctive mechanisms of downward flame spread for XPS foam. It was physically considered as a moving down of narrow pool fire instead of downward surface flame spread for normal solids. A method was developed to quantitatively analyze the accumulated liquid fuel based on the experimental measurement of locations of flame tips and burning rates. The results surprisingly showed that about 80% of the generated hot liquid fuel remained in the pool fire during a certain period. Most of the consumed solid XPS foam didn't really burn away but transformed as the liquid fuel in the downward moving pool fire, which might be an important promotion for the fast fire development. The results also indicated that the dripping propensity of the hot liquid fuel depends on the total amount of the hot liquid accumulated in the pool fire. The leading point of the flame front curve might be the breach of the accumulated hot liquid fuel if it is enough for dripping. Finally, it is suggested that horizontal noncombustible barriers for preventing the accumulation and dripping of liquid fuel are helpful for vertical confining of XPS fire. Copyright © 2017 Elsevier B.V. All rights reserved.

Band bending at the heterointerface of GaAs/InAs core/shell nanowires monitored by synchrotron X-ray photoelectron spectroscopy

NASA Astrophysics Data System (ADS)

Khanbabaee, B.; Bussone, G.; Knutsson, J. V.; Geijselaers, I.; Pryor, C. E.; Rieger, T.; Demarina, N.; Grützmacher, D.; Lepsa, M. I.; Timm, R.; Pietsch, U.

2016-10-01

Unique electronic properties of semiconductor heterostructured nanowires make them useful for future nano-electronic devices. Here, we present a study of the band bending effect at the heterointerface of GaAs/InAs core/shell nanowires by means of synchrotron based X-ray photoelectron spectroscopy. Different Ga, In, and As core-levels of the nanowire constituents have been monitored prior to and after cleaning from native oxides. The cleaning process mainly affected the As-oxides and was accompanied by an energy shift of the core-level spectra towards lower binding energy, suggesting that the As-oxides turn the nanowire surfaces to n-type. After cleaning, both As and Ga core-levels revealed an energy shift of about -0.3 eV for core/shell compared to core reference nanowires. With respect to depth dependence and in agreement with calculated strain distribution and electron quantum confinement, the observed energy shift is interpreted by band bending of core-levels at the heterointerface between the GaAs nanowire core and the InAs shell.

Homogeneous crystalline FeSi2 films of c (4 × 8) phase grown on Si (111) by reactive deposition epitaxy.

PubMed

Zou, Zhi-Qiang; Sun, Li-Min; Shi, Gao-Ming; Liu, Xiao-Yong; Li, Xu

2013-12-05

The growth of iron silicides on Si (111) using reactive deposition epitaxy method was studied by scanning tunneling microscopy and X-ray photoelectron spectroscopy (XPS). Instead of the mixture of different silicide phases, a homogeneous crystalline film of c (4 × 8) phase was formed on the Si (111) surface at approximately 750°C. Scanning tunneling spectra show that the film exhibits a semiconducting character with a band gap of approximately 0.85 eV. Compared with elemental Fe, the Fe 2p peaks of the film exhibit a lower spin-orbit splitting (-0.3 eV) and the Fe 2p3/2 level has a smaller full-width at half maximum (-0.6 eV) and a higher binding energy (+0.3 eV). Quantitative XPS analysis shows that the c (4 × 8) phase is in the FeSi2 stoichiometry regime. The c (4 × 8) pattern could result from the ordered arrangement of defects of Fe vacancies in the buried Fe layers.

Low-temperature thermal reduction of graphene oxide: In situ correlative structural, thermal desorption, and electrical transport measurements

NASA Astrophysics Data System (ADS)

Lipatov, Alexey; Guinel, Maxime J.-F.; Muratov, Dmitry S.; Vanyushin, Vladislav O.; Wilson, Peter M.; Kolmakov, Andrei; Sinitskii, Alexander

2018-01-01

Elucidation of the structural transformations in graphene oxide (GO) upon reduction remains an active and important area of research. We report the results of in situ heating experiments, during which electrical, mass spectrometry, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and transmission electron microscopy (TEM) measurements were carried out correlatively. The simultaneous electrical and temperature programmed desorption measurements allowed us to correlate the onset of the increase in the electrical conductivity of GO by five orders of magnitude at about 150 °C with the maxima of the rates of desorption of H2O, CO, and CO2. Interestingly, this large conductivity change happens at an intermediate level of the reduction of GO, which likely corresponds to the point when the graphitic domains become large enough to enable percolative electronic transport. We demonstrate that the gas desorption is intimately related to (i) the changes in the chemical structure of GO detected by XPS and Raman spectroscopy and (ii) the formation of nanoscopic holes in GO sheets revealed by TEM. These in situ observations provide a better understanding of the mechanism of the GO thermal reduction.

(001) 3C SiC/Ni contact interface: In situ XPS observation of annealing induced Ni2Si formation and the resulting barrier height changes

NASA Astrophysics Data System (ADS)

Tengeler, Sven; Kaiser, Bernhard; Chaussende, Didier; Jaegermann, Wolfram

2017-04-01

The electronic states of the (001) 3C SiC/Ni interface prior and post annealing are investigated via an in situ XPS interface experiment, allowing direct observation of the induced band bending and the transformation from Schottky to ohmic behaviour for the first time. A single domain (001) 3C SiC sample was prepared via wet chemical etching. Nickel was deposited on the sample in multiple in situ deposition steps via RF sputtering, allowing observation of the 3C SiC/Ni interface formation. Over the course of the experiments, an upward band bending of 0.35 eV was observed, along with defect induced Fermi level pinning. This indicates a Schottky type contact behaviour with a barrier height of 0.41 eV. The subsequent annealing at 850 °C for 5 min resulted in the formation of a Ni2Si layer and a reversal of the band bending to 0.06 eV downward. Thus explaining the ohmic contact behaviour frequently reported for annealed n-type 3C SiC/Ni contacts.

Synthesis of nitrosobenzene via photocatalytic oxidation of aniline over MgO/TiO2 under visible light irradiation

NASA Astrophysics Data System (ADS)

Chen, Jinsong; Xiong, Jinhua; Song, Yujie; Yu, Yan; Wu, Ling

2018-05-01

MgO/TiO2 (Degussa P25 TiO2) composites were prepared and were used as visible-light-driven photocatalysts for the oxidation of aniline to nitrosobenzene under oxygen atmosphere. The typical sample with 5 wt% MgO loaded P25 (MP5) shows comparable photocatalytic activity with 2 wt% Pt/P25. The analyzed results of XPS indicate that the lattice oxygen in the MP5 possess higher electron density than those in P25. The electron-rich lattice oxygen, formed as a result of MgO loaded, would facilitate the deprontonation of aniline. A new peak at 3310 cm-1 was observed in in-situ FTIR spectrum for aniline adsorbed on the sample MP5, suggesting that anilino species were formed. These species may be produced via the deprontonation of aniline and result in the formation of the surface complexes. Further XPS studies for aniline adsorbed on the catalysts also indicate the existence of the surface complexes. Under visible light irradiation, the electrons may excite from the surface complexes and initiate the oxidation processes. Finally, speculated photocatalytic processes for the oxidation of aniline to nitrosobenzene were proposed at molecular level.

Plasma surface cleaning in a microwave plasma source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsai, C.C.; Nelson, W.D.; Haselton, H.H.

1994-03-01

A microwave electron cyclotron resonance (ECR) plasma source has been operated to produce reactive plasmas of oxygen and its mixture with argon. Aluminum samples (0.95 cm by 1.9 cm) were coated with thin films (<20 {mu}m in thickness) of Shell Vitrea oil and cleaned by using such reactive plasmas. The plasma cleaning was done in discharge conditions of microwave power up to 1300 W, radio frequency power up to 200 W, biased potential up to 400 V, gas pressures up to 5 mtorr, and operating time up to 35 min. The surface texture of the postcleaned samples has been examinedmore » visually. Mass loss of the samples after plasma cleaning was measured to estimate cleaning rates. Measured clean rates of low-pressure (0.5-mtorr) argon/oxygen plasmas were as high as 2.7 {mu}m/min. X-ray photoelectron spectroscopy (XPS) was used to determine cleanliness of the sample surfaces after plasma cleaning. The XPS study on polished samples confirmed the effectiveness of plasma cleaning in achieving atomic level of surface cleanliness. In this technical memorandum plasma properties, cleaning phenomena, and significant results are reported and discussed.« less

Homogeneous crystalline FeSi2 films of c (4 × 8) phase grown on Si (111) by reactive deposition epitaxy

PubMed Central

2013-01-01

The growth of iron silicides on Si (111) using reactive deposition epitaxy method was studied by scanning tunneling microscopy and X-ray photoelectron spectroscopy (XPS). Instead of the mixture of different silicide phases, a homogeneous crystalline film of c (4 × 8) phase was formed on the Si (111) surface at approximately 750°C. Scanning tunneling spectra show that the film exhibits a semiconducting character with a band gap of approximately 0.85 eV. Compared with elemental Fe, the Fe 2p peaks of the film exhibit a lower spin-orbit splitting (−0.3 eV) and the Fe 2p3/2 level has a smaller full-width at half maximum (−0.6 eV) and a higher binding energy (+0.3 eV). Quantitative XPS analysis shows that the c (4 × 8) phase is in the FeSi2 stoichiometry regime. The c (4 × 8) pattern could result from the ordered arrangement of defects of Fe vacancies in the buried Fe layers. PMID:24305438

20 CFR 641.740 - How will the Department determine whether a grantee fails, meets, or exceeds the expected levels...

Code of Federal Regulations, 2010 CFR

2010-04-01

... grantee fails, meets, or exceeds the expected levels of performance for the core indicators and what will... determine whether a grantee fails, meets, or exceeds the expected levels of performance for the core... such levels) by aggregating the grantee's core indicators. The aggregate is calculated by combining the...

Cesium power: low Cs+ levels impart stability to perovskite solar cells.

PubMed

Deepa, Melepurath; Salado, Manuel; Calio, Laura; Kazim, Samrana; Shivaprasad, S M; Ahmad, Shahzada

2017-02-01

Towards increasing the stability of perovskite solar cells, the addition of Cs + is found to be a rational approach. Recently triple cation based perovskite solar cells were found to be more effective in terms of stability and efficiency. Heretofore they were unexplored, so we probed the Cs/MA/FA (cesium/methyl ammonium/formamidinium) cation based perovskites by X-ray photoelectron spectroscopy (XPS) and correlated their compositional features with their solar cell performances. The Cs + content was found to be optimum at 5%, when incorporated in the (MA 0.15 FA 0.85 )Pb(I 0.85 Br 0.15 ) 3 lattice, because the corresponding device yielded the highest fill factor compared to the perovskite without Cs + and with 10% Cs + . XPS studies distinctly reveal how Cs + aids in maintaining the expected stoichiometric ratios of I : Pb 2+ , I : N and Br : Pb 2+ in the perovskites, and how the valence band (VB) edge is dependent on the Cs + proportion, which in turn governs the open circuit voltage. Even at a low content of 5%, Cs + resides deep within the absorber layer, and ensures minimum distortion of the VB level (compared to 0% and 10% Cs + perovskites) upon Ar + sputtering, thus allowing the formation of a stable robust material that delivers excellent solar cell response. This study which brings out the role of Cs + is anticipated to be of paramount significance to further engineer the composition and improve device performances.

Surface analysis of glass fibres using XPS and AFM: case study of glass fibres recovered from the glass fibre reinforced polymer using chemical recycling

NASA Astrophysics Data System (ADS)

Nzioka, A. M.; Kim, Y. J.

2018-01-01

In this study, we present the results of an experimental study of the use of the X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) to characterise the coatings of the recovered E - glass fibres. The recovered E - glass fibres were obtained using chemical recycling process coupled with ultrasound cavitation. The objective of this study was to analyse the impact of chemical recycling and the ultrasound cavitation process on the sizing properties of the recovered fibres. We obtained the recovered fibres and sized using 1 wt% 3 - aminopropyltriethoxysilane (APS). Part of the sized fibres was washed with acetone and analysed all the sample fibres using AFM and XPS. Results showed the different composition of sizing after extraction using acetone. We compared the results of this study with that of virgin clean glass fibres.

Surface and electronic structure of Bi-Ca-Sr-Cu-O superconductors studied by LEED, UPS and XPS

NASA Astrophysics Data System (ADS)

Shen, Z.-X.; Lindberg, P. A. P.; Wells, B. O.; Lindau, I.; Spicer, W. E.; Mitzi, D. B.; Eom, C. B.; Kapitulnik, A.; Geballe, T. H.; Soukiassian, P.

1989-02-01

Single crystal and polycrystalline samples of Bi2CaSr2Cu2O8 have been studied by various surface sensitive techniques, including low energy electron diffraction (LEED), ultraviolet photoemission spectroscopy (UPS) and x-ray photoemission spectroscopy (XPS). The surface structure of the single crystals was characterized by LEED to be consistent with that of the bulk structure. Our data suggest that Bi2CaSr2Cu2O8 single crystals are very stable in the ultrahigh vacuu. No change of XPS spectra with temperature was observed. We have also studied the electronic structure of Bi2Sr2CuO6, which has a lower superconducting transition temperature Tc. Comparing the electronic structure of the two Bi-Ca-Sr-Cu-O superconductors, an important difference in the density of states near EF was observed which seems to be related to the difference in Tc.

Platinized tin oxide catalysts for CO2 lasers: Effects of pretreatment

NASA Technical Reports Server (NTRS)

Gardner, Steven D.; Hoflund, Gar B.; Schryer, David R.; Upchurch, Billy T.

1990-01-01

Platinized tin oxide surfaces used for low-temperature CO oxidation in CO2 lasers have been characterized before and after reduction in CO at 125 and 250 C using ion scattering spectroscopy (ISS) and X ray photoelectron spectroscopy (XPS). XPS indicates that the Pt is present initially as PtO2. Reduction at 125 C converts the PtO2 to Pt(OH)2 while reduction at 250 C converts the PtO2 to metallic Pt. ISS shows that the Pt in the outermost atomic layer of the catalyst is mostly covered by substrate species during the 250 C reduction. Both the ISS and XPS results are consistent with Pt/Sn alloy formation. The surface dehydration and migration of substrate species over surface Pt and Sn appear to explain why a CO pretreatment at 250 C produces inferior CO oxidation activities compared to a 125 C pretreatment.

Platinized tin oxide catalysts for CO2 lasers - Effects of pretreatment

NASA Technical Reports Server (NTRS)

Gardner, Steven D.; Hoflund, Gar B.; Schryer, David R.; Upchurch, Billy T.

1989-01-01

Platinized tin oxide surfaces used for low-temperature CO oxidation in CO2 lasers have been characterized before and after reduction in CO at 125 and 250 C using ion scattering spectroscopy (ISS) and X-ray photoelectron spectroscopy (XPS). XPS indicates that the Pt is present initially as Pto2. Reduction at 125 C converts the PtO2 to Pt(OH)2 while reduction at 250 C converts the PtO2 to metallic Pt. ISS shows that the Pt in the outermost atomic layer of the catalyst is mostly covered by substrate species during the 250 C reduction. Both the ISS and XPS results are consistent with Pt/Sn alloy formation. The surface dehydration and migration of substrate species over surface Pt and Sn appear to explain why a CO pretreatment at 250 C produces inferior CO oxidation activities compared to a 125 C pretreatment.

Morphological and XPS study of ball milled Fe1-xAlx (0.3≤x≤0.6) alloys

NASA Astrophysics Data System (ADS)

Rajan, Sandeep; Kumar, Anil; Vyas, Anupam; Brajpuriya, Ranjeet

2018-05-01

The paper presents mechanical and XPS study of ball milled Fe1-xAlx (0.3≤x≤0.6) alloys. The author prepared the solid solution of Fe(Al) with different composition of Al by using mechanical alloying (MA) technique. The MA process induces a progressive dissolution of Al into Fe, resulted in the formation of an extended Fe(Al) solid solution with the bcc structure after 5 hr of milling. The SEM Images shows that the initial shape of particles disappeared completely, and their structure became a mixture of small and large angular-shaped crystallites with different sizes. The TEM micrograph also confirms the reduction in crystallite size and alloy formation. XPS study shows the shift in the binding energy position of both Fe and Al Peaks provide strong evidence of Fe(Al) phase formation after milling.

XPS studies of nitrogen doping niobium used for accelerator applications

NASA Astrophysics Data System (ADS)

Yang, Ziqin; Lu, Xiangyang; Tan, Weiwei; Zhao, Jifei; Yang, Deyu; Yang, Yujia; He, Yuan; Zhou, Kui

2018-05-01

Nitrogen doping study on niobium (Nb) samples used for the fabrication of superconducting radio frequency (SRF) cavities was carried out. The samples' surface treatment was attempted to replicate that of the Nb SRF cavities, which includes heavy electropolishing (EP), nitrogen doping and the subsequent EP with different amounts of material removal. The surface chemical composition of Nb samples with different post treatments has been studied by XPS. The chemical composition of Nb, O, C and N was presented before and after Gas Cluster Ion Beam (GCIB) etching. No signals of poorly superconducting nitrides NbNx was found on the surface of any doped Nb sample with the 2/6 recipe before GCIB etching. However, in the depth range greater than 30 nm, the content of N element is below the XPS detection precision scope even for the Nb sample directly after nitrogen doping treatment with the 2/6 recipe.

Conduction band offset at GeO{sub 2}/Ge interface determined by internal photoemission and charge-corrected x-ray photoelectron spectroscopies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, W. F.; Nishimula, T.; Nagashio, K.

2013-03-11

We report a consistent conduction band offset (CBO) at a GeO{sub 2}/Ge interface determined by internal photoemission spectroscopy (IPE) and charge-corrected X-ray photoelectron spectroscopy (XPS). IPE results showed that the CBO value was larger than 1.5 eV irrespective of metal electrode and substrate type variance, while an accurate determination of valence band offset (VBO) by XPS requires a careful correction of differential charging phenomena. The VBO value was determined to be 3.60 {+-} 0.2 eV by XPS after charge correction, thus yielding a CBO (1.60 {+-} 0.2 eV) in excellent agreement with the IPE results. Such a large CBO (>1.5more » eV) confirmed here is promising in terms of using GeO{sub 2} as a potential passivation layer for future Ge-based scaled CMOS devices.« less

Identification of the silver state in the framework of Ag-containing zeolite by XRD, FTIR, photoluminescence, 109Ag NMR, EPR, DR UV-vis, TEM and XPS investigations.

PubMed

Popovych, Nataliia; Kyriienko, Pavlo; Soloviev, Sergiy; Baran, Rafal; Millot, Yannick; Dzwigaj, Stanislaw

2016-10-26

Silver has been identified in the framework of Ag x SiBEA zeolites (where x = 3-6 Ag wt%) by the combined use of XRD, 109 Ag MAS NMR, FTIR, diffuse reflectance UV-visible, EPR and XPS spectroscopy. The incorporation of Ag ions into the framework of SiBEA zeolite has been evidenced by XRD. The consumption of OH groups as a result of their reaction with the silver precursor has been monitored by FTIR and photoluminescence spectroscopy. The changes in the silver state as a function of Ag content and thermal and hydrogen treatment at 573 K have been identified by 109 Ag MAS NMR, EPR, DR UV-visible, TEM and XPS investigations. The acidity of AgSiBEA has been investigated by FTIR spectroscopy of adsorbed CO and pyridine used as probe molecules.

XPS and ToF-SIMS analysis of natural rubies and sapphires heat-treated in a reducing (5 mol% H 2/Ar) atmosphere

NASA Astrophysics Data System (ADS)

Achiwawanich, S.; James, B. D.; Liesegang, J.

2008-12-01

Surface effects on Mong Hsu rubies and Kanchanaburi sapphires after heat treatment in a controlled reducing atmosphere (5 mol% H 2/Ar) have been investigated using advanced surface science techniques including X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS). Visual appearance of the gemstones is clearly affected by the heat treatment in a reducing atmosphere. Kanchanaburi sapphires, in particular, exhibit Fe-containing precipitates after the heat treatment which have not been observed in previous studies under an inert atmosphere. Significant correlation between changes in visual appearance of the gemstones and variations in surface concentration of trace elements, especially Ti and Fe are observed. The XPS and ToF-SIMS results suggest that; (1) a reducing atmosphere affects the oxidation state of Fe; (2) dissociation of Fe-Ti interaction may occur during heat treatment.

XPS and UPS studies on electronic structure of Li 2O

NASA Astrophysics Data System (ADS)

Tanaka, Satoru; Taniguchi, Masaki; Tanigawa, Hisashi

2000-12-01

The adsorption behavior of H 2O on Li 2O was studied by X-ray photo electron spectroscopy (XPS) and ultraviolet photo electron spectroscopy (UPS). XPS and UPS spectra of Li 2O single crystals which were exposed to different pressure of H 2O vapor were observed. In O(1s) region, two peaks were observed and they were assigned to O(1s) in precipitated LiOH on the surface and O(1s) in Li 2O. After H 2O exposure, a peak broadening and an appearance of a new peak were observed at the higher binding energy region than O(1s) in Li 2O. They were attributed to surface -OH and H 2O molecule adsorbed on the surface. The adsorption behavior of H 2O was discussed from the observation of electronic structure in Li 2O surface.

Toward a better determination of dairy powders surface composition through XPS matrices development.

PubMed

Nikolova, Y; Petit, J; Sanders, C; Gianfrancesco, A; Scher, J; Gaiani, C

2015-01-01

The surface composition of dairy powders prepared by mixing various amounts of micellar casein (MC), whey proteins isolate (WPI), lactose, and anhydrous milk fat (AMF) was investigated by XPS measurements. The use of matrices are generally accepted to transform surface atomic composition (i.e., C, O, N contents) into surface component composition (i.e., lactose, proteins, lipids). These atomic-based matrices were revisited and two new matrices based on the surface bond composition were developed. Surface compositions obtained from atomic and bond-based matrices were compared. A successful matrix allowing good correlations between XPS predicted and theoretical surface composition for powders free from fat was identified. Nevertheless, samples containing milk fat were found to present a possible segregation of components owing to the AMF overrepresentation on the surface. Supplementary analyses (FTIR, SEM) were carried out in order to investigate the homogeneity of the mixtures. Copyright © 2014 Elsevier B.V. All rights reserved.

On the genesis of molybdenum carbide phases during reduction-carburization reactions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guil-Lopez, R., E-mail: rut.guil@icp.csic.es; Nieto, E.; Departamento de Tecnologia Quimica y Energetica, ESCET, Universidad Rey Juan Carlos, C/Tulipan s/n, 28933-Mostoles

2012-06-15

Molybdenum carbide has been prepared according to the carbothermal reduction method. Carbon black substrate was used as C-source whereas a H{sub 2}-flow was the reducing agent. Two different H{sub 2} consumption steps were identified during the carburization treatment. The low temperature step is related to the reduction of Mo{sup 6+}-to-Mo{sup 4+}, the higher temperature process accounts for the deep reduction of Mo{sup 4+}-to-metal Mo{sup 0} and its subsequent reaction with C to form the Mo-carbide. The influences of the maximum carburization temperature, carburization time, gas hourly space velocity regarding Mo-loading, heating rate and temperature of Ar pre-treatment were analyzed. Allmore » these conditions are interrelated to each other. Thus, the carburization process ends at 700 Degree-Sign C when Mo-loading is 10 wt%, however Mo-loading higher than 10 wt% requires higher temperatures. Carburization temperatures up to 800 Degree-Sign C are needed to fulfill Mo-carbide formation with samples containing 50 wt% Mo. Nevertheless, Ar pre-treatment at 550 Degree-Sign C and slow heating rates favor the carburization, thus requiring lower carburization temperatures to reach the same carburization level. - Graphical Abstract: H{sub 2}-consumption profile (TPR) during the molybdenum carburization process, XRD patterns of the reduced Mo-samples after carburization and TEM-micrographs with two different enlargement of the samples with 5, 20 and 50 wt% Mo. Highlights: Black-Right-Pointing-Pointer Control of carburization variables: tailor the reduced/carbide Mo-phases (single/mixture). Black-Right-Pointing-Pointer Mo carburization in two stages: (1) Mo{sup 6+}-Mo{sup 4+}; (2) Mo{sup 4+}-Mo{sup 0} and, at once, MoC. Black-Right-Pointing-Pointer The carburization process is faster than Mo{sup 4+} reduction. Black-Right-Pointing-Pointer XPS probed: reduced Mo particles show core-shell structure. Black-Right-Pointing-Pointer Core: reduced Mo (Mo{sub 2}C, MoO{sub 2} and/or Mo{sup 0}); Shell: 2-3 nm of MoO{sub 3}.« less

Beneficial effects of water in the colloidal synthesis of InP/ZnS core-shell quantum dots for optoelectronic applications.

PubMed

Ramasamy, Parthiban; Kim, Bumjin; Lee, Min-Sang; Lee, Jong-Soo

2016-10-21

We demonstrate that the presence of a small amount of water as an impurity during the hot-injection synthesis can significantly decrease the emission lines full width at half-maximum (FWHM) and improve the quantum yield (QY) of InP/ZnS quantum dots (QDs). By utilizing the water present in the indium precursor and solvent, we obtained InP/ZnS QDs emitting around 530 nm with a FWHM as narrow as 46 nm and a QY up to 45%. Without water, the synthesized QDs have emission around 625 nm with a FWHM of 66 nm and a QY of about 33%. Absorption spectra, XRD and XPS analyses revealed that when water is present, an amorphous phosphate layer is formed over the InP QDs and inhibits the QD growth. This amorphous layer favors the formation of a very thick ZnS shell by decreasing the lattice mismatch between the InP core and the ZnS shell. We further show the possibility to tune the emission wavelengths of InP/ZnS QDs by simply adjusting the amount of water present in the system while keeping all the other reaction parameters (i.e., precursor concentration, reaction temperature and time) constant. As an example of their application in light-emitting diodes (LEDs), the green and red InP/ZnS QDs are combined with a blue LED chip to produce white light.

Application of surface analytical methods in thin film analysis

NASA Astrophysics Data System (ADS)

Wen, Xingu

Self-assembly and the sol-gel process are two promising methods for the preparation of novel materials and thin films. In this research, these two methods were utilized to prepare two types of thin films: self-assembled monolayers of peptides on gold and SiO2 sol-gel thin films modified with Ru(II) complexes. The properties of the resulting thin films were investigated by several analytical techniques in order to explore their potential applications in biomaterials, chemical sensors, nonlinear optics and catalysis. Among the analytical techniques employed in the study, surface analytical techniques, such as X-ray photoelectron spectroscopy (XPS) and grazing angle reflection absorption Fourier transform infrared spectroscopy (RA-FTIR), are particularly useful in providing information regarding the compositions and structures of the thin films. In the preparation of peptide thin films, monodisperse peptides were self-assembled on gold substrate via the N-terminus-coupled lipoic acid. The film compositions were investigated by XPS and agreed well with the theoretical values. XPS results also revealed that the surface coverage of the self-assembled films was significantly larger than that of the physisorbed films and that the chemisorption between the peptides and gold surface was stable in solvent. Studies by angle dependent XPS (ADXPS) and grazing angle RA-FTIR indicated that the peptides were on average oriented at a small angle from the surface normal. By using a model of orientation distribution function, both the peptide tilt angle and film thickness can be well calculated. Ru(II) complex doped SiO2 sol-gel thin films were prepared by low temperature sol-gel process. The ability of XPS coupled with Ar + ion sputtering to provide both chemical and compositional depth profile information of these sol-gel films was evaluated. This technique, together with UV-VIS and electrochemical measurements, was used to investigate the stability of Ru complexes in the composite films. The stability of Ru complexes with respect to dopant leaching was dependent on the film microstructures. Three methods aiming to improve the dopant stability were also explored. In addition, the ion exchange properties of the composite films, upon exposure to various ions in aqueous solutions, were investigated by XPS, and the ion exchange mechanism was elucidated.

Polyethylene Glycol-Mediated Synthesis of Cubic Iron Oxide Nanoparticles with High Heating Power

NASA Astrophysics Data System (ADS)

Iacovita, Cristian; Stiufiuc, Rares; Radu, Teodora; Florea, Adrian; Stiufiuc, Gabriela; Dutu, Alina; Mican, Sever; Tetean, Romulus; Lucaciu, Constantin M.

2015-10-01

Iron oxide magnetic nanoparticles (IOMNPs) have been successfully synthesized by means of solvothermal reduction method employing polyethylene glycol (PEG200) as a solvent. The as-synthesized IOMNPs are poly-dispersed, highly crystalline, and exhibit a cubic shape. The size of IOMNPs is strongly dependent on the reaction time and the ration between the amount of magnetic precursor and PEG200 used in the synthesis method. At low magnetic precursor/PEG200 ratio, the cubic IOMNPs coexist with polyhedral IOMNPs. The structure and morphology of the IOMNPs were thoroughly investigated by using a wide range of techniques: TEM, XRD, XPS, FTIR, and RAMAN. XPS analysis showed that the IOMNPs comprise a crystalline magnetite core bearing on the outer surface functional groups from PEG200 and acetate. The presence of physisorbed PEG200 on the IOMNP surface is faintly detected through FT-IR spectroscopy. The surface of IOMNPs undergoes oxidation into maghemite as proven by RAMAN spectroscopy and the occurrence of satellite peaks in the Fe2p XP spectra. The magnetic studies performed on powder show that the blocking temperature (TB) of IOMNPs is around 300 K displaying a coercive field in between 160 and 170 Oe. Below the TB, the field-cooled (FC) curves turn concave and describe a plateau indicating that strong magnetic dipole-dipole interactions are manifested in between IOMNPs. The specific absorption rate (SAR) values increase with decreasing nanoparticle concentrations for the IOMNPs dispersed in water. The SAR dependence on the applied magnetic field, studied up to magnetic field amplitude of 60 kA/m, presents a sigmoid shape with saturation values up to 1700 W/g. By dispersing the IOMNPs in PEG600 (liquid) and PEG1000 (solid), it was found that the SAR values decrease by 50 or 75 %, indicating that the Brownian friction within the solvent was the main contributor to the heating power of IOMNPs.

Geometry-dependent DNA-TiO2 immobilization mechanism: A spectroscopic approach

NASA Astrophysics Data System (ADS)

Silva-Moraes, M. O.; Garcia-Basabe, Y.; de Souza, R. F. B.; Mota, A. J.; Passos, R. R.; Galante, D.; Fonseca Filho, H. D.; Romaguera-Barcelay, Y.; Rocco, M. L. M.; Brito, W. R.

2018-06-01

DNA nucleotides are used as a molecular recognition system on electrodes modified to be applied in the detection of various diseases, but immobilization mechanisms, as well as, charge transfers are not satisfactorily described in the literature. An electrochemical and spectroscopic study was carried out to characterize the molecular groups involved in the direct immobilization of DNA structures on the surface of nanostructured TiO2 with the aim of evaluating the influence of the geometrical aspects. X-ray photoelectron spectroscopy at O1s and P2p core levels indicate that immobilization of DNA samples occurs through covalent (Psbnd Osbnd Ti) bonds. X-ray absorption spectra at the Ti2p edge reinforce this conclusion. A new species at 138.5 eV was reported from P2p XPS spectra analysis which plays an important role in DNA-TiO2 immobilization. The Psbnd Osbnd Ti/Osbnd Ti ratio showed that quantitatively the DNA immobilization mechanism is dependent on their geometry, becoming more efficient for plasmid ds-DNA structures than for PCR ds-DNA structures. The analysis of photoabsorption spectra at C1s edge revealed that the molecular groups that participate in the C1s → LUMO electronic transitions have different pathways in the charge transfer processes at the DNA-TiO2 interface. Our results may contribute to additional studies of immobilization mechanisms understanding the influence of the geometry of different DNA molecules on nanostructured semiconductor and possible impact to the charge transfer processes with application in biosensors or aptamers.

Using “Tender” x-ray ambient pressure x-Ray photoelectron spectroscopy as a direct probe of solid-liquid interface

DOE PAGES

Axnanda, Stephanus; Crumlin, Ethan J.; Mao, Baohua; ...

2015-05-07

We report a new method to probe the solid-liquid interface through the use of a thin liquid layer on a solid surface. An ambient pressure XPS (AP-XPS) endstation that is capable of detecting high kinetic energy photoelectrons (7 keV) at a pressure up to 110 Torr has been constructed and commissioned. Additionally, we have deployed a “dip & pull” method to create a stable nanometers-thick aqueous electrolyte on platinum working electrode surface. Combining the newly constructed AP-XPS system, “dip & pull” approach, with a “tender” X-ray synchrotron source (2 keV–7 keV), we are able to access the interface between liquidmore » and solid dense phases with photoelectrons and directly probe important phenomena occurring at the narrow solid-liquid interface region in an electrochemical system. Using this approach, we have performed electrochemical oxidation of the Pt electrode at an oxygen evolution reaction (OER) potential. Under this potential, we observe the formation of both Pt²⁺ and Pt⁴⁺ interfacial species on the Pt working electrode in situ. We believe this thin-film approach and the use of “tender” AP-XPS highlighted in this study is an innovative new approach to probe this key solid-liquid interface region of electrochemistry.« less

Using “Tender” x-ray ambient pressure x-Ray photoelectron spectroscopy as a direct probe of solid-liquid interface

DOE Office of Scientific and Technical Information (OSTI.GOV)

Axnanda, Stephanus; Crumlin, Ethan J.; Mao, Baohua

We report a new method to probe the solid-liquid interface through the use of a thin liquid layer on a solid surface. An ambient pressure XPS (AP-XPS) endstation that is capable of detecting high kinetic energy photoelectrons (7 keV) at a pressure up to 110 Torr has been constructed and commissioned. Additionally, we have deployed a “dip & pull” method to create a stable nanometers-thick aqueous electrolyte on platinum working electrode surface. Combining the newly constructed AP-XPS system, “dip & pull” approach, with a “tender” X-ray synchrotron source (2 keV–7 keV), we are able to access the interface between liquidmore » and solid dense phases with photoelectrons and directly probe important phenomena occurring at the narrow solid-liquid interface region in an electrochemical system. Using this approach, we have performed electrochemical oxidation of the Pt electrode at an oxygen evolution reaction (OER) potential. Under this potential, we observe the formation of both Pt²⁺ and Pt⁴⁺ interfacial species on the Pt working electrode in situ. We believe this thin-film approach and the use of “tender” AP-XPS highlighted in this study is an innovative new approach to probe this key solid-liquid interface region of electrochemistry.« less

The Effect of Thermal and Mechanical Treatments on Kaolinite: Characterization by XPS and IEP Measurements.

PubMed

Torres Sánchez RM; Basaldella; Marco

1999-07-15

The surface transformations induced on kaolinite by different thermal and mechanical treatments have been investigated by means of X-ray photoelectron spectroscopy (XPS), Bremsstrahlung induced Auger spectroscopy, and isoelectric point (IEP) measurements. Heating the kaolinite at temperatures between 500 and 750 degrees C results in the change of a substantial fraction of surface Al from octahedral to tetrahedral coordination, which we associate with the dehydroxylation of kaolinite. Heating at 900 and 980 degrees C brings about the development of an octahedral Al fraction which is associated with the formation of gamma-Al(2)O(3). The development of an Al tetrahedral component in the Al KLL spectra of the mechanically treated (ground) samples has been also observed. The Si/Al atomic ratio obtained by XPS in the thermally treated samples is the same as that shown by the original kaolinite. However, the XPS data show a clear reduction of the Si/Al atomic ratio in the mechanically treated samples, which suggests that the mechanical treatment has induced an Al enrichment of the kaolinite surface. The IEP values indicated a thermal transformation to metakaolinite and mullite with the increase of temperature (750 to 980 degrees C). The IEP change for the milled samples can be only explained by assuming a 30% kaolinite coating by the Al oxide neoformed by grinding. Copyright 1999 Academic Press.

Metal ion interaction with phosphorylated tyrosine analogue monolayers on gold.

PubMed

Petoral, Rodrigo M; Björefors, Fredrik; Uvdal, Kajsa

2006-11-23

Phosphorylated tyrosine analogue molecules (pTyr-PT) were assembled onto gold substrates, and the resulting monolayers were used for metal ion interaction studies. The monolayers were characterized by X-ray photoelectron spectroscopy (XPS), infrared reflection-absorption spectroscopy (IRAS), cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS), both prior to and after exposure to metal ions. XPS verified the elemental composition of the molecular adsorbate and the presence of metal ions coordinated to the phosphate groups. Both the angle-dependent XPS and IRAS results were consistent with the change in the structural orientation of the pTyr-PT monolayer upon exposure to metal ions. The differential capacitance of the monolayers upon coordination of the metal ions was evaluated using EIS. These metal ions were found to significantly change the capacitance of the pTyr-PT monolayers in contrast to the nonphosphorylated tyrosine analogue (TPT). CV results showed reduced electrochemical blocking capabilities of the phosphorylated analogue monolayer when exposed to metal ions, supporting the change in the structure of the monolayer observed by XPS and IRAS. The largest change in the structure and interfacial capacitance was observed for aluminum ions, compared to calcium, magnesium, and chromium ions. This type of monolayer shows an excellent capability to coordinate metal ions and has a high potential for use as sensing layers in biochip applications to monitor the presence of metal ions.

Alkaline Earth Core Level Photoemission Spectroscopy of High-Temperature Superconductors

NASA Technical Reports Server (NTRS)

Vasquez, R.

1993-01-01

This paper examines photoemission measurements of the alkaline Earth core levels of high-temperature superconductors and related materials, models that seek to explain the large negative shifts observed relative to the corresponding alkaline Earth metals, and the effect of lattice site disorder on the core level spectra and the presence or absence of intrinsic surface peaks.

20 CFR 641.720 - How will the Department and grantees initially determine and then adjust expected levels of...

Code of Federal Regulations, 2011 CFR

2011-04-01

... initially determine and then adjust expected levels of performance for the core performance measures? 641... the core performance measures? (a) Initial agreement. Before the beginning of each Program Year, the Department and each grantee will undertake to agree upon expected levels of performance for each core...

The College Level Teaching Core: An Orientation and Training System for New Faculty.

ERIC Educational Resources Information Center

Graber, Jared S.; Kinser, Paul

The College Level Teaching Core offered at Valencia Community College (Florida) has been developed as a planned orientation and training program for college faculty. Offered twice per academic year during the early part of both the fall and spring semesters, the majority of College Level Teaching Core participants are members of the college's…

20 CFR 641.720 - How will the Department and grantees initially determine and then adjust expected levels of...

Code of Federal Regulations, 2010 CFR

2010-04-01

... initially determine and then adjust expected levels of performance for the core performance measures? 641... the core performance measures? (a) Initial agreement. Before the beginning of each Program Year, the Department and each grantee will undertake to agree upon expected levels of performance for each core...

A perspective on two chemometrics tools: PCA and MCR, and introduction of a new one: Pattern recognition entropy (PRE), as applied to XPS and ToF-SIMS depth profiles of organic and inorganic materials

NASA Astrophysics Data System (ADS)

Chatterjee, Shiladitya; Singh, Bhupinder; Diwan, Anubhav; Lee, Zheng Rong; Engelhard, Mark H.; Terry, Jeff; Tolley, H. Dennis; Gallagher, Neal B.; Linford, Matthew R.

2018-03-01

X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) are much used analytical techniques that provide information about the outermost atomic and molecular layers of materials. In this work, we discuss the application of multivariate spectral techniques, including principal component analysis (PCA) and multivariate curve resolution (MCR), to the analysis of XPS and ToF-SIMS depth profiles. Multivariate analyses often provide insight into data sets that is not easily obtained in a univariate fashion. Pattern recognition entropy (PRE), which has its roots in Shannon's information theory, is also introduced. This approach is not the same as the mutual information/entropy approaches sometimes used in data processing. A discussion of the theory of each technique is presented. PCA, MCR, and PRE are applied to four different data sets obtained from: a ToF-SIMS depth profile through ca. 100 nm of plasma polymerized C3F6 on Si, a ToF-SIMS depth profile through ca. 100 nm of plasma polymerized PNIPAM (poly (N-isopropylacrylamide)) on Si, an XPS depth profile through a film of SiO2 on Si, and an XPS depth profile through a film of Ta2O5 on Ta. PCA, MCR, and PRE reveal the presence of interfaces in the films, and often indicate that the first few scans in the depth profiles are different from those that follow. PRE and backward difference PRE provide this information in a straightforward fashion. Rises in the PRE signals at interfaces suggest greater complexity to the corresponding spectra. Results from PCA, especially for the higher principal components, were sometimes difficult to understand. MCR analyses were generally more interpretable.

Surfactant-mediated growth of cobalt on magnesium oxide(111)

NASA Astrophysics Data System (ADS)

Johnson-Steigelman, Harry Trevor

Monolayer films of Co have been deposited using an electrostatic electron-beam evaporator on single-crystal MgO(111)-( 3x3 ) R 30° and MgO(111)-(1x1) substrates held at room temperature (RT), with subsequent annealing of temperatures 400°C to 800°C. These films have been characterized using low-energy electron diffraction (LEED), x-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM). Upon RT deposition of Co, the LEED pattern of the substrate disappears and the XPS signal of MgO features reduce in intensity. After short anneals of 400°C, the LEED pattern returns and the MgO features increase in intensity. AFM images suggest that islanding has occurred at the surface. This conclusion is supported by the behavior of thicker films of Co on MgO(111), which showed pronounced changes in the MgO related XPS features. The behavior of the Mg 2p and O 1s features were analyzed and compared to previously reported reconstructions of the MgO(111)-(1x1) and MgO(111)-( 3x3 ) R 30° surfaces. Ag was examined as a potential surfactant to aid in the growth of smooth Co films. Ag was deposited onto MgO(111)-( 3x3 ) R 30° substrates and investigated using XPS, LEED, and AFM. It was found that Ag formed islands upon annealing. Despite the fact that Ag formed islands, it was found that the presence of Ag did have a surfactant effect upon the thin-film growth of Co on Ag/MgO(111)-( 3x3 ) R 30° substrates with 1-2 ML of Ag. Co islands were still present, but much more smooth than islands formed without the Ag surfactant. XPS peak intensity changes and AFM suggest strongly that Ag floated to the top of these samples at temperatures above 400°C. The Co growth mode appears to be Volmer-Weber island growth, as seen in AFM.

Nitrogen-doped carbon dots originating from unripe peach for fluorescent bioimaging and electrocatalytic oxygen reduction reaction.

PubMed

Atchudan, Raji; Edison, Thomas Nesakumar Jebakumar Immanuel; Lee, Yong Rok

2016-11-15

This paper reports the robust hydrothermal synthesis of nitrogen doped carbon dots (N-CDs) using the unripe fruit of Prunus persica (peach) as the carbon precursor and aqueous ammonia as the nitrogen source. The optical properties of synthesized N-CDs were characterized by ultraviolet visible (UV-Vis) and fluorescence spectroscopy techniques. The synthesized N-CDs were emitted blue light when excitated with a portable UV lamp. The materials with the optical properties were characterized further by high resolution transmission electron microscope (HRTEM), X-ray diffraction (XRD), Raman, Fourier transform infrared (FT-IR) and X-ray photoelectron spectroscopy (XPS). The mean size of the N-CDs was approximately 8nm, as calculated from the HRTEM image. The d-spacing of N-CDs, calculated using Bragg law, was approximately 0.21nm, which was consistent with the interlayer distance calculated from the HRTEM image. FT-IR spectroscopy and XPS revealed the presence of the phytoconstituents functionalities of peach fruit over the N-CDs surface and a high level of nitrogen doping on carbon dots (CDs) was confirmed by XPS studies. These results suggest that the unripe fruit extract of peach is an ideal candidate for the preparation of N-CDs. The resulting N-CDs showed excellent optical properties in water. The synthesized N-CDs exhibited a high fluorescence quantum yield and low cytotoxicity, and can be used as fluorescence imaging probes. In addition, the N-CDs were catalytically activite towards the oxygen reduction reaction (ORR). The N-CDs exhibited good catalytic activity in an alkaline medium (0.1M KOH) with a remarkable ORR of approximately 0.72V vs reversible hydrogen electrode (RHE), and O2 reduction follows mainly a 2 electron pathway by being reduced to hydrogen peroxide. The 2-electron reduction pathway is used in industry for H2O2 production. Copyright © 2016 Elsevier Inc. All rights reserved.

Distinguishing solid bitumens formed by thermochemical sulfate reduction and thermal chemical alteration

USGS Publications Warehouse

Kelemen, S.R.; Walters, C.C.; Kwiatek, P.J.; Afeworki, M.; Sansone, M.; Freund, H.; Pottorf, R.J.; Machel, H.G.; Zhang, T.; Ellis, G.S.; Tang, Y.; Peters, K.E.

2008-01-01

Insoluble solid bitumens are organic residues that can form by the thermal chemical alteration (TCA) or thermochemical sulfate reduction (TSR) of migrated petroleum. TCA may actually encompass several low temperature processes, such as biodegradation and asphaltene precipitation, followed by thermal alteration. TSR is an abiotic redox reaction where petroleum is oxidized by sulfate. It is difficult to distinguish solid bitumens associated with TCA of petroleum from those associated with TSR when both processes occur at relatively high temperature. The focus of the present work was to characterize solid bitumen samples associated with TCA or TSR using X-ray photoelectron spectroscopy (XPS). XPS is a surface analysis conducted on either isolated or in situ (>25 ??m diameter) solid bitumen that can provide the relative abundance and chemical speciation of carbon, organic and inorganic heteroatoms (NSO). In this study, naturally occurring solid bitumens from three locations, Nisku Fm. Brazeau River area (TSR-related), LaBarge Field Madison Fm. (TSR-related), and the Alaskan Brooks range (TCA-related), are compared to organic solids generated during laboratory simulation of the TSR and TCA processes. The abundance and chemical nature of organic nitrogen and sulfur in solid bitumens can be understood in terms of the nature of (1) petroleum precursor molecules, (2) the concentration of nitrogen by way of thermal stress and (3) the mode of sulfur incorporation. TCA solid bitumens originate from polar materials that are initially rich in sulfur and nitrogen. Aromaticity and nitrogen increase as thermal stress cleaves aliphatic moieties and condensation reactions take place. Organic sulfur in TCA organic solids remains fairly constant with increasing maturation (3.5 to ???17 sulfur per 100 carbons) into aromatic structures and to the low levels of nitrogen in their hydrocarbon precursors. Hence, XPS results provide organic chemical composition information that helps to distinguish whether solid bitumen, either in situ or removed and concentrated from the rock matrix, was formed via the TCA or TRS process. ?? 2008 Elsevier Ltd.

Interaction of acidic trace gases with ice from a surface science perspective

NASA Astrophysics Data System (ADS)

Waldner, A.; Kong, X.; Ammann, M.; Orlando, F.; Birrer, M.; Artiglia, L.; Bartels-Rausch, T.

2016-12-01

Acidic trace gases, such as HCOOH, HCl and HONO, play important roles in atmospheric chemistry. The presence of ice is known to have the capability to modify this chemistry (Neu et al. 2012). The molecular level processes of the interaction of acidic trace gases with ice are still a matter of debate and a quantification of the uptake is difficult (Dash et al. 2006, Bartels-Rausch et al. 2014, Huthwelker et al. 2006). This hampers a proper inclusion of ice as a substrate in models of various scales as for example in global chemistry climate models that would among others allow predicting large-scale effects of ice clouds. So far, direct observations of the ice surface and of the interaction with trace gases at temperatures and concentrations relevant to the environment are very limited. In this study, we take advantage of the surface and analytical sensitivity as well as the chemical selectivity of photoemission and absorption spectroscopy performed at ambient pressure using the near ambient pressure photoemission endstation (NAPP) at Swiss Light Source to overcome this limitation in environmental science (Orlando et al. 2016). Specifically, ambient pressure X-ray Photoelectron Spectroscopy (XPS) allows us to get information about chemical state and concentration depth profiles of dopants. The combination of XPS with auger electron yield Near-Edge X-ray Absorption Fine Structure (NEXAFS) enables us to locate the dopant and analyse wheather the interaction leads to enhanced surface disorder and to what extent different disorders influences the uptake of the trace gas. For the first time, this study looks directly at the interaction of HCOOH, the strongest organic acid, with ice at 2 different temperatures (233 and 253 K) relevant for environmental science by means of electron spectroscopy. XPS depth profiles indicate that the HCOOH basically remains within the topmost ice layers and O K-edge NEXAFS analysis show that the interaction ice-HCOOH does not lead to enhanced surface disorder at environmentally relevant conditions.

Ferrocene functionalized nanoscale mixed-oxides as a potent phosphate adsorbent from the synthetic and real (Persian Gulf) waters.

PubMed

Arshadi, M; Zandi, H; Akbari, J; Shameli, A

2015-07-15

The application of covalently attached ferrocene groups to the aluminum-silicate nanoparticles (ASNPs) for phosphate (P) removal from the synthetic and real waters has been studied and the prepared nanomaterials were analyzed by XPS, EDS, BET, TEM, chemical analysis (CHN), FTIR, and ICP-AES. The immobilization of the ferrocene on the surface of the inorganic support (mixed oxides) can lead to reduce the drawback of the pristine ferrocene molecules which may have strong tendency to agglomerate into larger particles, resulting in the negative effect on both available active sites and catalyst performance. XPS of Fe ions evidenced that most of the active sites of the nano-adsorbent is in the form of Fe(III) ions at the surface. The heterogeneous Fe(III) ions were effective toward removal of phosphate. The contact time to obtain equilibrium for maximum adsorption of phosphate (100%) was found to be 120 min. The adsorption kinetics of P has been evaluated in terms of pseudo-first- and -second-order kinetics, and the Freundlich and Langmuir isotherm models have also been tested to the equilibrium adsorption results. The adsorption process was spontaneous and endothermic in nature and followed pseudo-second-order kinetic model. FTIR, EDS and XPS results confirmed the formation of Fe-O-P bond on the Si/Al@Fe surface after adsorption of P from aqueous media. The Si/Al@Fe displayed high reusability due to its high removal capacity after 10th adsorption-desorption runs. The proposed adsorbent could also be utilized to adsorb the P ions from the real sample (Persian Gulf water). The high removal capacity of P ions from the real water and the high levels of reusability confirmed the versatility of the heterogenized ferrocene groups on the ASNPs. Copyright © 2015 Elsevier Inc. All rights reserved.

DOE ZERH Case Study: BrightLeaf Homes, McCormick Avenue, Brookfield, IL

DOE Office of Scientific and Technical Information (OSTI.GOV)

none,

2015-09-01

Case study of a DOE 2015 Housing Innovation Award winning production home in the cold climate that got a HERS 38 without PV, with staggered 2x4 studs every 8”on a 2x6 plate with dense-packed R-25 cellulose, basement with 3” XPS exterior and 2: XPS under slab; a vented attic with spray foam top plates and R-60 blown cellulose; 96% AFUE furnace, 14 SEER AC, plus fresh air intake.

Growth and Electronic Structure of Heusler Compounds for Use in Electron Spin Based Devices

DTIC Science & Technology

2015-06-01

either Co– or MnSi– initiated films on c(4x4) GaAs. Studies using x - ray photoemission spectroscopy (XPS), STM/STS, and transmission electron microscopy...Co– or MnSi– initiated films on c(4x4) GaAs. Studies using x - ray photoemission spectroscopy (XPS), STM/STS, and transmission electron microscopy (TEM...diagram of the Palmstrøm lab in-situ growth and char- acterization setup, with 6 MBE growth chambers, 3 scanning probe microscopes, an x - ray

Tgif1 Counterbalances the Activity of Core Pluripotency Factors in Mouse Embryonic Stem Cells.

PubMed

Lee, Bum-Kyu; Shen, Wenwen; Lee, Jiwoon; Rhee, Catherine; Chung, Haewon; Kim, Kun-Yong; Park, In-Hyun; Kim, Jonghwan

2015-10-06

Core pluripotency factors, such as Oct4, Sox2, and Nanog, play important roles in maintaining embryonic stem cell (ESC) identity by autoregulatory feedforward loops. Nevertheless, the mechanism that provides precise control of the levels of the ESC core factors without indefinite amplification has remained elusive. Here, we report the direct repression of core pluripotency factors by Tgif1, a previously known terminal repressor of TGFβ/activin/nodal signaling. Overexpression of Tgif1 reduces the levels of ESC core factors, whereas its depletion leads to the induction of the pluripotency factors. We confirm the existence of physical associations between Tgif1 and Oct4, Nanog, and HDAC1/2 and further show the level of Tgif1 is not significantly altered by treatment with an activator/inhibitor of the TGFβ/activin/nodal signaling. Collectively, our findings establish Tgif1 as an integral member of the core regulatory circuitry of mouse ESCs that counterbalances the levels of the core pluripotency factors in a TGFβ/activin/nodal-independent manner. Copyright © 2015 The Authors. Published by Elsevier Inc. All rights reserved.

Core-level photoemission investigation of atomic-fluorine adsorption on GaAs(110)

NASA Astrophysics Data System (ADS)

McLean, A. B.; Terminello, L. J.; McFeely, F. R.

1989-12-01

The adsorption of atomic F on the cleaved GaAs(110) surface has been studied with use of high-resolution core-level photoelectron spectroscopy by exposing the GaAs(110) surfaces to XeF2, which adsorbs dissociatively, leaving atomic F behind. This surface reaction produces two chemically shifted components in the Ga 3d core-level emission which are attributed to an interfacial monofluoride and a stable trifluoride reaction product, respectively. The As 3d core level develops only one chemically shifted component and from its exposure-dependent behavior it is attributed to an interfacial monofluoride. Least-squares analysis of the core-level line shapes revealed that (i) the F bonds to both the anion and the cation , (ii) the GaF3 component (characteristic of strong interfacial reaction) and the surface core-level shifted component (characteristic of a well ordered, atomically clean surface) are present together over a relatively large range of XeF2 exposures, and (iii) it is the initial disruption of the GaAs(110) surface that is the rate-limiting step in this surface reaction. These results are compared with similar studies of Cl and O adsorption on GaAs(110).

Self-perceived competency of infection control nurses based on Benner's framework: a nationwide survey in Korea.

PubMed

Kim, Kyung Mi; Choi, Jeong Sil

2015-05-01

The aim of this study was to evaluate the competency level of Korean infection control nurses (ICNs) by comparing the self-perceived competency level based on Benner's framework and the core competency proposed by the Certification Board of Infection Control. Study subjects included 90 ICNs working in Korean hospitals with more than 300 beds. A questionnaire was used to measure self-perceived competency level and core competency level. Using descriptive analysis, the core competency level of ICNs was found to differ significantly according to self-perceived competency level, and core competency level showed a significant increase with the increase of self-perceived competency level. Self-perceived competency level could be useful in classifying the competency level of nursing specialties. These results illustrate the competency levels of Korean ICNs and could serve as a reference to evaluate and expand the application of competency measurement not only for ICNs but also other groups of nurse specialists. Copyright © 2014 Elsevier Inc. All rights reserved.

Deposition of GdVO4:Eu3+ nanoparticles on silica nanospheres by a simple sol gel method

NASA Astrophysics Data System (ADS)

Liu, Guixia; Hong, Guangyan; Wang, Jinxian; Dong, Xiangting

2006-07-01

The deposition and coating of GdVO4:Eu3+ nanoparticles on spherical silica was carried out using a simple sol-gel method at low temperature. The GdVO4:Eu3+-coated silica composites obtained were characterized by differential thermal analysis (DTA), thermogravimetric (TG) analysis, x-ray diffraction (XRD), Fourier-transform IR spectroscopy (FT-IR), transmission electron microscopy (TEM), x-ray photoelectron spectroscopy (XPS), photoluminescence spectra, and kinetic decay. It is found that the ~5 nm GdVO4:Eu3+ nanoparticles coating the silica spheres are crystal in the as-prepared samples and the crystallinity increases with increasing annealing temperature. The composites obtained are spherical in shape with an average size of 100 nm. The GdVO4:Eu3+ nanoparticles are linked with silica cores by a chemical bond. The photoluminescence spectra of the obtained GdVO4:Eu3+-coated silica composites are similar to those of the bulk GdVO4:Eu3+ phosphors. The strongest peak is near 617 nm, which indicates that Eu3+ is located in the low symmetry site with non-inversion centre.

Preparation of Cd/Pb Chalcogenide Heterostructured Janus Particles via Controllable Cation Exchange

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Jianbing; Chernomordik, Boris D.; Crisp, Ryan W.

2015-07-28

We developed a strategy for producing quasi-spherical nanocrystals of anisotropic heterostructures of Cd/Pb chalcogenides. The nanostructures are fabricated via a controlled cation exchange reaction where the Cd2+ cation is exchanged for the Pb2+ cation. The cation exchange reaction is thermally activated and can be controlled by adjusting the reaction temperature or time. We characterized the particles using TEM, XPS, PL, and absorption spectroscopy. With complete exchange, high quality Pb-chalcogenide quantum dots are produced. In addition to Cd2+, we also find suitable conditions for the exchange of Zn2+ cations for Pb2+ cations. The cation exchange is anisotropic starting at one edgemore » of the nanocrystals and proceeds along the <111> direction producing a sharp interface at a (111) crystallographic plane. Instead of spherical core/shell structures, we produced and studied quasi-spherical CdS/PbS and CdSe/PbSe Janus-type heterostructures. Nontrivial PL behavior was observed from the CdS(e)/PbS(e) heterostructures as the Pb:Cd ratio is increased.« less

Synthesis and property of novel MnO2@polypyrrole coaxial nanotubes as electrode material for supercapacitors

NASA Astrophysics Data System (ADS)

Yao, Wei; Zhou, Hui; Lu, Yun

2013-11-01

Novel MnO2@polypyrrole (PPy) coaxial nanotubes have been prepared via a simple and green approach without any surfactant and additional oxidant. Under the acidic condition, MnO2 nanotubes act as both template and oxidant to initiate the polymerization of pyrrole monomers on its fresh-activated surface. Fourier transform infrared spectra (FT-IR), X-ray diffraction patterns (XRD), thermo-gravimetric analysis data (TG) and X-ray photoelectron spectra (XPS) suggest the formation of composite structure of MnO2@PPy. Also, FESEM and TEM images intuitively confirm that the PPy shell is coated uniformly on the surface of MnO2 nanotubes. Adjusting the concentrations of sulfuric acid or adding oxidant can modulate the morphology of the products accordingly. Due to the synergic effect between MnO2 core and PPy shell, the MnO2@PPy coaxial nanotubes possess better rate capability, larger specific capacitance of 380 F g-1, doubling the specific capacitance of MnO2 nanotubes, and good capacitance retention of 90% for its initial capacitance after 1000 cycles.

DMSO-Li2O2 Interface in the Rechargeable Li-O2 Battery Cathode: Theoretical and Experimental Perspectives on Stability.

PubMed

Schroeder, Marshall A; Kumar, Nitin; Pearse, Alexander J; Liu, Chanyuan; Lee, Sang Bok; Rubloff, Gary W; Leung, Kevin; Noked, Malachi

2015-06-03

One of the greatest obstacles for the realization of the nonaqueous Li-O2 battery is finding a solvent that is chemically and electrochemically stable under cell operating conditions. Dimethyl sulfoxide (DMSO) is an attractive candidate for rechargeable Li-O2 battery studies; however, there is still significant controversy regarding its stability on the Li-O2 cathode surface. We performed multiple experiments (in situ XPS, FTIR, Raman, and XRD) which assess the stability of the DMSO-Li2O2 interface and report perspectives on previously published studies. Our electrochemical experiments show long-term stable cycling of a DMSO-based operating Li-O2 cell with a platinum@carbon nanotube core-shell cathode fabricated via atomic layer deposition, specifically with >45 cycles of 40 h of discharge per cycle. This work is complemented by density functional theory calculations of DMSO degradation pathways on Li2O2. Both experimental and theoretical evidence strongly suggests that DMSO is chemically and electrochemically stable on the surface of Li2O2 under the reported operating conditions.

Preparation of Cd/Pb Chalcogenide Heterostructured Janus Particles via Controllable Cation Exchange.

PubMed

Zhang, Jianbing; Chernomordik, Boris D; Crisp, Ryan W; Kroupa, Daniel M; Luther, Joseph M; Miller, Elisa M; Gao, Jianbo; Beard, Matthew C

2015-07-28

We developed a strategy for producing quasi-spherical nanocrystals of anisotropic heterostructures of Cd/Pb chalcogenides. The nanostructures are fabricated via a controlled cation exchange reaction where the Cd(2+) cation is exchanged for the Pb(2+) cation. The cation exchange reaction is thermally activated and can be controlled by adjusting the reaction temperature or time. We characterized the particles using TEM, XPS, PL, and absorption spectroscopy. With complete exchange, high quality Pb-chalcogenide quantum dots are produced. In addition to Cd(2+), we also find suitable conditions for the exchange of Zn(2+) cations for Pb(2+) cations. The cation exchange is anisotropic starting at one edge of the nanocrystals and proceeds along the ⟨111⟩ direction producing a sharp interface at a (111) crystallographic plane. Instead of spherical core/shell structures, we produced and studied quasi-spherical CdS/PbS and CdSe/PbSe Janus-type heterostructures. Nontrivial PL behavior was observed from the CdS(e)/PbS(e) heterostructures as the Pb:Cd ratio is increased.

Comparison of iridium- and ruthenium-based, Pt-surface-enriched, nanosize catalysts for the oxygen-reduction reaction

NASA Astrophysics Data System (ADS)

Kaplan, D.; Goor, M.; Alon, M.; Tsizin, S.; Burstein, L.; Rosenberg, Y.; Popov, I.; Peled, E.

2016-02-01

Pt-surface-enriched nanosize catalysts (Pt-SENS catalysts) with ruthenium and iridium cores, supported on XC72, were synthesized and characterized. The structure and composition of the catalysts are determined by Energy-Dispersive X-ray Spectroscopy (EDS), X-ray Photoelectron Spectroscopy (XPS), Scanning Transmission Electron Microscopy (STEM) and X-Ray Diffraction (XRD). Electrochemical characterization tests, including oxygen-reduction-catalysis activity and durability studies of catalysts are performed with the use of cyclic-voltammetry and rotating-disk-electrode (RDE) techniques at room temperature. The ORR activity of the homemade catalysts is also compared to ORR activity of commercial 50%Pt/C catalyst. It is determined that the Ir-based catalyst (Pt/Ir/XC72) shows higher ORR activity in terms of A g-1 of Pt (at 0.85 V vs. RHE) than the Ru-based catalyst (Pt/Ru/XC72) and the commercial 50%Pt/C. The Ru-based catalyst shows similar ORR activity in terms of A g-1 of Pt, to that of the commercial 50%Pt/C, but with much lower durability.

Na2.5Fe1.75(SO4)3/Ketjen/rGO: An advanced cathode composite for sodium ion batteries

NASA Astrophysics Data System (ADS)

Goñi, A.; Iturrondobeitia, A.; Gil de Muro, I.; Lezama, L.; Rojo, T.

2017-11-01

An advanced cathode composite Na2.5Fe1.75(SO4)3/Ketjen/rGO for sodium ion batteries has been prepared, joining together the excellent electrochemical properties of the three components: off stoichiometric iron sulfate alluaudite, Ketjen Black carbon and reduced graphene oxide (rGO). This electrode material has been exhaustively characterized by XRD, thermogravimetric analysis, Raman spectroscopy and SEM and TEM microscopy. The study has demonstrated that a high quality electrode material has been designed containing a porous sulfate core properly coated by interweaved rGO fibers and Ketjen Black nanoparticles. The electrochemical study has revealed an excellent performance providing specific capacities close to the theoretical one at 1C. Additionally, this composite has shown a very good rate capability and a great cycling stability for at least 200 cycles maintaining a coulombic efficiency of 96%. The post mortem analysis, which includes EPR and XPS measurements, has demonstrated that the carbonaceous coating on the composite generates a stable and protective SEI layer over the active material guaranteeing a successful performance during a long cycle life.

Room-temperature ferromagnetic Cr-doped Ge/GeOx core–shell nanowires

NASA Astrophysics Data System (ADS)

Katkar, Amar S.; Gupta, Shobhnath P.; Motin Seikh, Md; Chen, Lih-Juann; Walke, Pravin S.

2018-06-01

The Cr-doped tunable thickness core–shell Ge/GeOx nanowires (NWs) were synthesized and characterized using x-ray diffraction, field-emission scanning electron microscopy, transmission electron microscopy, energy-dispersive x-ray spectroscopy, x-ray photoelectron spectroscopy and magnetization studies. The shell thickness increases with the increase in synthesis temperature. The presence of metallic Cr and Cr3+ in core–shell structure was confirmed from XPS study. The magnetic property is highly sensitive to the core–shell thickness and intriguing room temperature ferromagnetism is realized only in core–shell NWs. The magnetization decreases with an increase in shell thickness and practically ceases to exist when there is no core. These NWs show remarkably high Curie temperature (TC > 300 K) with the dominating values of its magnetic remanence (MR) and coercivity (HC) compared to germanium dilute magnetic semiconductor nanomaterials. We believe that our finding on these Cr-doped Ge/GeOX core–shell NWs has the potential to be used as a hard magnet for future spintronic devices, owing to their higher characteristic values of ferromagnetic ordering.

Development and characterization of coaxially electrospun gelatin coated poly (3-hydroxybutyric acid) thin films as potential scaffolds for skin regeneration.

PubMed

Nagiah, Naveen; Madhavi, Lakshmi; Anitha, R; Anandan, C; Srinivasan, Natarajan Tirupattur; Sivagnanam, Uma Tirichurapalli

2013-10-01

The morphology of fibers synthesized through electrospinning has been found to mimic extracellular matrix. Coaxially electrospun fibers of gelatin (sheath) coated poly (3-hydroxybutyric acid) (PHB) (core) was developed using 2,2,2 trifluoroethanol(TFE) and 1,1,1,3,3,3 hexafluoro-2-propanol(HFIP) as solvents respectively. The coaxial structure and coating of gelatin with PHB fibers was confirmed through transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Thermal stability of the coaxially electrospun fibers was analyzed using thermogravimetric analysis(TGA), differential scanning calorimetry(DSC) and differential thermogravimetric analysis(DTA). Complete evaporation of solvent and gelatin grafting over PHB fibers was confirmed through attenuated total reflection-Fourier transformed infrared spectroscopy (ATR-FTIR). The coaxially electrospun fibers exhibited competent tensile properties for skin regeneration with high surface area and porosity. In vitro degradation studies proved the stability of fibers and its potential applications in tissue engineering. The fibers supported the growth of human dermal fibroblasts and keratinocytes with normal morphology indicating its potential as a scaffold for skin regeneration. © 2013.

Formation of Ag nanoframes with facilitation of dithiols.

PubMed

Cheng, Fong-Yu; Hu, Kuo-Wei; Yeh, Chen-Sheng

2012-03-01

Two-dimensional Ag nanoprisms readily formed Ag triangular nanoframes upon electron beam irradiation. Following meso-2, 3-dimercaptosuccinicacid (DMSA) ripening behavior, continuous electron beam exposure transformed a solid nanoplate into a core/void/shell morphology, which then evolved into a hollow nanoframe structure. TEM was used to observe the ripening and etching processes of Ag nanoprisms as a function of DMSA concentration and electron irradiation time. X-ray diffraction (XRD) and FT-IR analysis were conducted to characterize the Ag nanoprism structure and surface before and after treatment with DMSA. X-ray photoelectron spectroscopy (XPS) was used to determine surface chemical compositions and indicated DMSA was adsorbed on the Ag nanoprisms in the form of Ag(+)-S(-). Raman measurements provided evidence of a disulfide group on Ag nanoprisms. Similar organosulfur structures such as mercaptosuccinic acid and 2-mercaptoacetic acid were also studied with results suggesting that the two S-H groups of dithiol DMSA played the crucial role in nanoframe fabrication. Using the same strategy with DMSA, the nano-architecture can be extended to 2D nanodiscs yielding nanorings.

XPS study of ruthenium tris-bipyridine electrografted from diazonium salt derivative on microcrystalline boron doped diamond.

PubMed

Agnès, Charles; Arnault, Jean-Charles; Omnès, Franck; Jousselme, Bruno; Billon, Martial; Bidan, Gérard; Mailley, Pascal

2009-12-28

Boron doped diamond (BDD) functionalization has received an increasing interest during the last few years. Such an infatuation comes from the original properties of BDD, including chemical stability or an electrochemical window, that opens the way for the design of (bio)sensors or smart interfaces. In such a context, diazonium salts appear to be well suited for BDD functionalization as they enable covalent immobilization of functional entities such as enzymes or DNA. In this study we report microcrystalline BDD functionalization with a metallic complex, ruthenium tris(bipyridine), using the p-(tris(bipyridine)Ru(2+))phenyl diazonium salt. Electrografting using cyclic voltammetry (CV) allowed the formation of a ruthenium complex film that was finely characterized using electrochemistry and X-ray photoelectron spectroscopy (XPS). Moreover, we showed that chronopotentiometry (CP) is a convenient tool to monitor Ru complex film deposition through the control of the electrochemical pulse parameters (i.e. current density and pulse duration). Finally, such a control was demonstrated through the correlation between electrochemical and XPS characterizations.

Structural and magnetic characterization of copper sulfonated phthalocyanine grafted onto treated polyethylene

NASA Astrophysics Data System (ADS)

Reznickova, A.; Kolska, Z.; Orendac, M.; Cizmar, E.; Sajdl, P.; Svorcik, V.

2016-08-01

This study focuses on high density polyethylene (HDPE) activated by Ar plasma treatment, subsequently grafted with copper sulfonated phthalocyanine (CuPc) especially pointing out to the surface and magnetic properties of those composites. Properties of pristine PE and their plasma treated counterparts were studied by different experimental techniques: X-ray photoelectron spectroscopy (XPS), UV-vis spectroscopy, zeta potential and by electron spin resonance (ESR). XPS analysis confirmed the successful grafting of phthalocyanine. The highest absorption was found for the sample grafted with bCuPc for 1 h. Electrokinetic analysis also confirmed the plasma treatment and also subsequent CuPc grafting influence significantly the surface chemistry and charge. These results correspond well with XPS determination. ESR studies confirmed the presence of CuPc grafted on HDPE. It was found, that grafting is mediated by magnetically inactive functional groups, rather than radicals. Magnetic properties of CuPc do not seem to change significantly after grafting CuPc on polyethylene surface.

The (001) 3C SiC surface termination and band structure after common wet chemical etching procedures, stated by XPS, LEED, and HREELS

NASA Astrophysics Data System (ADS)

Tengeler, Sven; Kaiser, Bernhard; Ferro, Gabriel; Chaussende, Didier; Jaegermann, Wolfram

2018-01-01

The (001) surface of cubic silicon carbide (3C SiC) after cleaning, Ar sputtering and three different wet chemical etching procedures was thoroughly investigated via (angle resolved) XPS, HREELS, and LEED. While Ar sputtering was found to be unsuitable for surface preparation, all three employed wet chemical etching procedures (piranha/NH4F, piranha/HF, and RCA) provide a clean surface. HF as oxide removal agent tends to result in fluorine traces on the sample surface, despite thorough rinsing. All procedures yield a 1 × 1 Si-OH/C-H terminated surface. However, the XPS spectra reveal some differences in the resulting surface states. NH4F for oxide removal produces a flat band situation, whereas the other two procedures result in a slight downward (HF) or upward (RCA) band bending. Because the band bending is small, it can be concluded that the number of unsaturated surface defects is low.

In situ formation of the active sites in Pd-Au bimetallic nanocatalysts for CO oxidation: NAP (near ambient pressure) XPS and MS study.

PubMed

Bukhtiyarov, A V; Prosvirin, I P; Saraev, A A; Klyushin, A Yu; Knop-Gericke, A; Bukhtiyarov, V I

2018-06-07

Model bimetallic Pd-Au/HOPG catalysts have been investigated in the CO oxidation reaction using a combination of NAP XPS and MS techniques. The samples have shown catalytic activity at temperatures above 150 °C. The redistribution of Au and Pd on the surface depending on the reaction conditions has been demonstrated using NAP XPS. The Pd enrichment of the bimetallic particles' surface under reaction gas mixture has been shown. Apparently, CO adsorption induces Pd segregation on the surface. Heating the sample under reaction conditions above 150 °C decomposes the Pd-CO state due to CO desorption and reaction and simultaneous Pd-Au alloy formation on the surface takes place. Cooling back down to RT results in reversible Pd segregation due to Pd-CO formation and the sample becomes inactive. It has been shown that in situ studies are necessary for investigation of the active sites in Pd-Au bimetallic systems.

X-ray photoelectron and mass spectroscopic study of electron irradiation and thermal stability of polytetrafluoroethylene

NASA Technical Reports Server (NTRS)

Wheeler, Donald R.; Pepper, Stephen V.

1990-01-01

Polytetrafluoroethylene (PTFE) was subjected to 3 keV electron bombardment and then heated in vacuum to 300 C. The behavior of the material as a function of radiation dose and temperature was studied by X-ray photoelectron spectroscopy (XPS) of the surface and mass spectroscopy of the species evolved. A quantitative comparison of the radiation dose rate with that in other reported studies showed that, for a given total dose, the damage observed by XPS is greater for higher dose rates. Lightly damaged material heated to 300 C evolved saturated fluorocarbon species, whereas unsaturated fluorocarbon species evolved from heavily damaged material. After heating the heavily damaged material, those features in the XPS that were associated with damage diminished, giving the appearance that the radiation damage annealed. The apparent annealing of the radiation damage was found to be due to the covering of the network by saturated fragments that easily diffused through the decomposed material to the surface region upon heating.

Adsorption differences between low coverage enantiomers of alanine on the chiral Cu{421}R surface.

PubMed

Gladys, Michael J; Han, Jeong Woo; Pedersen, Therese S; Tadich, Anton; O'Donnell, Kane M; Thomsen, Lars

2017-05-31

Chiral separation using heterogeneous methods has long been sought after. Chiral metal surfaces have the potential to make it possible to model these systems using small amino acids, the building blocks for proteins. A comparison of submonolayer concentrations of alanine enantiomers adsorbed onto Cu{421} R has revealed a large geometrical differences between the two molecules as compared to the saturated coverage. Large differences were observed in HR-XPS and NEXAFS and complemented by theoretical DFT calculations. At approximately one third of a monolayer a comparison of the C1s XPS signal showed a shift in the methyl group of more than 300 meV indicating that the two enantiomers are in different chemical environments. NEXAFS spectroscopy confirmed the XPS variations and showed large differences in the orientation of the adsorbed molecules. Our DFT results show that the l-enantiomer is energetically the most stable in the {311} microfacet configuration. In contrast to the full monolayer coverage, these lower coverages showed enhanced selectivity.

Structural model of homogeneous As–S glasses derived from Raman spectroscopy and high-resolution XPS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Golovchak, R.; Shpotyuk, O.; Mccloy, J. S.

2010-11-28

The structure of homogeneous bulk As x S 100- x (25 ≤ x ≤ 42) glasses, prepared by the conventional rocking–melting–quenching method, was investigated using high-resolution X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. It is shown that the main building blocks of their glass networks are regular AsS 3/2 pyramids and sulfur chains. In the S-rich domain, the existence of quasi-tetrahedral (QT) S = As(S 1/2) 3 units is deduced from XPS data, but with a concentration not exceeding ~3–5% of total atomic sites. Therefore, QT units do not appear as primary building blocks of the glass backbone in thesemore » materials, and an optimally-constrained network may not be an appropriate description for glasses when x < 40. Finally, it is shown that, in contrast to Se-based glasses, the ‘chain-crossing’ model is only partially applicable to sulfide glasses.« less

Initial stages of oxide formation on the Zr surface at low oxygen pressure: An in situ FIM and XPS study

PubMed Central

Bespalov, I.; Datler, M.; Buhr, S.; Drachsel, W.; Rupprechter, G.; Suchorski, Y.

2015-01-01

An improved methodology of the Zr specimen preparation was developed which allows fabrication of stable Zr nanotips suitable for FIM and AP applications. Initial oxidation of the Zr surface was studied on a Zr nanotip by FIM and on a polycrystalline Zr foil by XPS, both at low oxygen pressure (10−8–10−7 mbar). The XPS data reveal that in a first, fast stage of oxidation, a Zr suboxide interlayer is formed which contains three suboxide components (Zr+1, Zr+2 and Zr+3) and is located between the Zr surface and a stoichiometric ZrO2 overlayer that grows in a second, slow oxidation stage. The sole suboxide layer has been observed for the first time at very early states of the oxidation (oxygen exposure ≤4 L). The Ne+ FIM observations are in accord with a two stage process of Zr oxide formation. PMID:25766998

Antioxidation performance of poly(vinyl alcohol) modified poly(vinylidene fluoride) membranes

NASA Astrophysics Data System (ADS)

Wang, Daohui; Li, Xianfeng; Li, Qing; Liu, Zhen; Li, Nana; Huang, Qinglin; Zhang, Yufeng; Xiao, Changfa

2018-03-01

Commercial poly(vinylidene fluoride) (PVDF) membranes were modified by dip-coating and crosslinking hydrophilic poly(vinyl alcohol) (PVA) on the membrane surface. The antioxidation performance of the modified PVDF membranes was evaluated via exposing the modified membranes to sodium hypochlorite and potassium permanganate solutions for 5-30 days, respectively. The evaluation was based on the influences of the two oxidants on the permeability, rejection, and hydrophility of the modified membranes, which were characterized by water flux, ink rejection, water contact angle, x-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy, and x-ray diffraction (XRD) measurements. The XPS and water contact angle results show that the hydrophilicity of PVDF membranes was significantly improved when PVA was crosslinked on the surface of PVDF membranes. When the modified membranes had been treated with sodium hypochlorite or potassium permanganate for 30 days, the permeability and hydrophilicity were basically maintained and the rejection was slightly decreased. XPS and XRD indicated that some of PVAs coated on the membrane surface could be oxidized and peeled.

Production of sp3 hybridization by swift heavy ion irradiation of HOPG

NASA Astrophysics Data System (ADS)

Zeng, J.; Zhai, P. F.; Liu, J.; Yao, H. J.; Duan, J. L.; Hou, M. D.; Sun, Y. M.; Li, G. P.

2013-07-01

Highly oriented pyrolytic graphite (HOPG) samples were irradiated by swift heavy ions (86Kr, 209Bi and 238U) with the fluence of 1011-1013 ions/cm2 at room temperature. The production of sp3 hybridization by the irradiation process has been confirmed directly by X-ray photoelectron spectroscopy (XPS). In this work, both irradiated and pristine HOPG samples were investigated by XPS and Raman spectroscopy. The existence of sp3 component is confirmed on the surface of the irradiated HOPG samples. XPS result shows that the acreage ratio Isp3/Isp2 increases with the ion fluence and saturates at a higher value of irradiation. It is found that the amount of hybridization (Isp3/Isp2) strongly depends on the electronic energy loss in the sample. Raman spectra of the irradiated samples show the increasing of acreage ratio ID/IG with the ion fluence, which indicates the change of the atomic structure and the phase transition from sp2 to sp3.

Overview of xeroderma pigmentosum proteins architecture, mutations and post-translational modifications.

PubMed

Feltes, Bruno César; Bonatto, Diego

2015-01-01

The xeroderma pigmentosum complementation group proteins (XPs), which include XPA through XPG, play a critical role in coordinating and promoting global genome and transcription-coupled nucleotide excision repair (GG-NER and TC-NER, respectively) pathways in eukaryotic cells. GG-NER and TC-NER are both required for the repair of bulky DNA lesions, such as those induced by UV radiation. Mutations in genes that encode XPs lead to the clinical condition xeroderma pigmentosum (XP). Although the roles of XPs in the GG-NER/TC-NER subpathways have been extensively studied, complete knowledge of their three-dimensional structure is only beginning to emerge. Hence, this review aims to summarize the current knowledge of mapped mutations and other structural information on XP proteins that influence their function and protein-protein interactions. We also review the possible post-translational modifications for each protein and the impact of these modifications on XP protein functions. Copyright © 2014 Elsevier B.V. All rights reserved.

Graphene Membranes for Atmospheric Pressure Photoelectron Spectroscopy.

PubMed

Weatherup, Robert S; Eren, Baran; Hao, Yibo; Bluhm, Hendrik; Salmeron, Miquel B

2016-05-05

Atmospheric pressure X-ray photoelectron spectroscopy (XPS) is demonstrated using single-layer graphene membranes as photoelectron-transparent barriers that sustain pressure differences in excess of 6 orders of magnitude. The graphene serves as a support for catalyst nanoparticles under atmospheric pressure reaction conditions (up to 1.5 bar), where XPS allows the oxidation state of Cu nanoparticles and gas phase species to be simultaneously probed. We thereby observe that the Cu(2+) oxidation state is stable in O2 (1 bar) but is spontaneously reduced under vacuum. We further demonstrate the detection of various gas-phase species (Ar, CO, CO2, N2, O2) in the pressure range 10-1500 mbar including species with low photoionization cross sections (He, H2). Pressure-dependent changes in the apparent binding energies of gas-phase species are observed, attributable to changes in work function of the metal-coated grids supporting the graphene. We expect atmospheric pressure XPS based on this graphene membrane approach to be a valuable tool for studying nanoparticle catalysis.

Depth resolved compositional analysis of aluminium oxide thin film using non-destructive soft x-ray reflectivity technique

NASA Astrophysics Data System (ADS)

Sinha, Mangalika; Modi, Mohammed H.

2017-10-01

In-depth compositional analysis of 240 Å thick aluminium oxide thin film has been carried out using soft x-ray reflectivity (SXR) and x-ray photoelectron spectroscopy technique (XPS). The compositional details of the film is estimated by modelling the optical index profile obtained from the SXR measurements over 60-200 Å wavelength region. The SXR measurements are carried out at Indus-1 reflectivity beamline. The method suggests that the principal film region is comprised of Al2O3 and AlOx (x = 1.6) phases whereas the interface region comprised of SiO2 and AlOx (x = 1.6) mixture. The soft x-ray reflectivity technique combined with XPS measurements explains the compositional details of principal layer. Since the interface region cannot be analyzed with the XPS technique in a non-destructive manner in such a case the SXR technique is a powerful tool for nondestructive compositional analysis of interface region.

Polarity determination of polar and semipolar (112¯2) InN and GaN layers by valence band photoemission spectroscopy

NASA Astrophysics Data System (ADS)

Skuridina, D.; Dinh, D. V.; Lacroix, B.; Ruterana, P.; Hoffmann, M.; Sitar, Z.; Pristovsek, M.; Kneissl, M.; Vogt, P.

2013-11-01

We demonstrate that the polarity of polar (0001), (0001¯) and semipolar (112¯2) InN and GaN thin layers can be determined by valence band X-ray photoemission spectroscopy (XPS). The polarity of the layers has been confirmed by wet etching and convergent beam electron diffraction. Unlike these two techniques, XPS is a non-destructive method and unaffected by surface oxidation or roughness. Different intensities of the valence band states in spectra recorded by using AlKα X-ray radiation are observed for N-polar and group-III-polar layers. The highest intensity of the valence band state at ≈3.5 eV for InN and ≈5.2 eV for GaN correlates with the group-III polarity, while the highest intensity at ≈6.7 eV for InN and ≈9.5 eV for GaN correlates with the N-polarity. The difference between the peaks for the group-III- and N-polar orientations was found to be statistically significant at the 0.05 significance level. The polarity of semipolar (112¯2) InN and GaN layers can be determined by recording valence band photoelectrons emitted along the [000 ± 1] direction.

High sensitivity flat SiO2 fibres for medical dosimetry

NASA Astrophysics Data System (ADS)

Abdul Sani, Siti. F.; Alalawi, Amani I.; Azhar, Hairul A. R.; Amouzad Mahdiraji, Ghafour; Tamchek, Nizam; Nisbet, A.; Maah, M. J.; Bradley, D. A.

2014-11-01

We describe investigation of a novel undoped flat fibre fabricated for medical radiation dosimetry. Using high energy X-ray beams generated at a potential of 6 MV, comparison has been made of the TL yield of silica flat fibres, TLD-100 chips and Ge-doped silica fibres. The flat fibres provide competitive TL yield to that of TLD-100 chips, being some 100 times that of the Ge-doped fibres. Pt-coated flat fibres have then been used to increase photoelectron production and hence local dose deposition, obtaining significant increase in dose sensitivity over that of undoped flat fibres. Using 250 kVp X-ray beams, the TL yield reveals a progressive linear increase in dose for Pt thicknesses from 20 nm up to 80 nm. The dose enhancement factor (DEF) of (0.0150±0.0003) nm-1 Pt is comparable to that obtained using gold, agreeing at the 1% level with the value expected on the basis of photoelectron generation. Finally, X-ray photoelectron spectroscopy (XPS) has been employed to characterize the surface oxidation state of the fibre medium. The charge state of Si2p was found to lie on 103.86 eV of binding energy and the atomic percentage obtained from the XPS analysis is 22.41%.

Towards the preparation of realistic model Ziegler-Natta catalysts: XPS study of the MgCl 2/TiCl 4 interaction with flat SiO 2/Si(1 0 0)

NASA Astrophysics Data System (ADS)

Siokou, Angeliki; Ntais, Spyridon

2003-08-01

Despite of the wide use of supported Ti based Ziegler-Natta catalysts in the olefin polymerization industry, questions concerning the role of each one of the catalyst components in the polymerization process, have not found a satisfactory answer yet. This is mainly because of the high sensitivity of these systems to oxygen and atmospheric moisture that makes their study in an atomic level rather complicated. Realistic surface science models of the pre-activated SiO 2 supported MgCl 2/TiCl 4 and TiCl 4 Ziegler-Natta catalysts were prepared by spin coating on flat conductive SiO 2/Si(1 0 0) supports under inert atmosphere. This preparation technique resembles the wet chemical impregnation which is the industrial method of the catalyst preparation. XPS analysis showed that the catalyst precursor anchors on the silica surface through bonding of the Ti atoms with surface silanes or siloxanes, while Mg is attached to the Ti through chlorine bridges. Thermal treatment of the catalysts at 723 K leads to total Cl desorption when MgCl 2 is not present while a significant amount of the Ti atoms is reduced to the Ti 3+ state.

Synergistic effects of Mo and F doping on the quality factor of ZnO thin films prepared by a fully automated home-made nebulizer spray technique

NASA Astrophysics Data System (ADS)

Ravichandran, K.; Dineshbabu, N.; Arun, T.; Manivasaham, A.; Sindhuja, E.

2017-01-01

Transparent conducting oxide films of undoped, Mo doped, Mo + F co-doped ZnO were deposited using a facile homemade nebulizer spray pyrolysis technique. The effects of Mo and F doping on the structural, optical, electrical and surface morphological properties were investigated using XRD, UV-vis-NIR spectroscopy, I-V and Hall probe techniques, FESEM and AFM, and XPS, respectively. The XRD analysis confirms that all the films are well crystallized with hexagonal wurtzite structure. All the synthesized samples exhibit high transmittance (above 85%) in the visible region. The current-voltage (I-V) characteristics show the ohmic conduction nature of the films. The Hall probe measurements show that the synergistic effects of Mo and F doping cause desirable improvements in the quality factor of the ZnO films. A minimum resistivity of 5.12 × 10-3 Ω cm with remarkably higher values of mobility and carrier concentration is achieved for Mo (2 at.%) + F (15 at.%) co-doped ZnO films. A considerable variation in the intensity of deep level emission caused by Mo and F doping is observed in the photoluminescence (PL) studies. The presence of the constituent elements in the samples is confirmed by XPS analysis.

Semiconductor-to-metal transition in rutile TiO 2 induced by tensile strain

DOE PAGES

Benson, Eric E.; Miller, Elisa M.; Nanayakkara, Sanjini U.; ...

2017-02-10

Here, we report the first observation of a reversible, degenerate doping of titanium dioxide with strain, which is referred to as a semiconductor-to-metal transition. Application of tensile strain to a ~50 nm film of rutile TiO 2 thermally grown on a superelastic nitinol (NiTi intermetallic) substrate causes reversible degenerate doping as evidenced by electrochemistry, X-ray photoelectron spectroscopy (XPS), and conducting atomic force microscopy (CAFM). Cyclic voltammetry and impedance measurements show behavior characteristic of a highly doped n-type semiconductor for unstrained TiO 2 transitioning to metallic behavior under tensile strain. The transition reverses when strain is removed. Valence band XPS spectramore » show that samples strained to 5% exhibit metallic-like intensity near the Fermi level. Strain also induces a distinct transition in CAFM current-voltage curves from rectifying (typical of an n-type semiconductor) to ohmic (metal-like) behavior. We propose that strain raises the energy distribution of oxygen vacancies ( n-type dopants) near the conduction band and causes an increase in carrier concentration. As the carrier concentration is increased, the width of the depletion region is reduced, which then permits electron tunneling through the space charge barrier resulting in the observed metallic behavior.« less

X-ray photoelectron spectroscopy for identification of morphological defects and disorders in graphene devices

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aydogan, Pinar; Suzer, Sefik, E-mail: suzer@fen.bilkent.edu.tr; Polat, Emre O.

The progress in the development of graphene devices is promising, and they are now considered as an option for the current Si-based electronics. However, the structural defects in graphene may strongly influence the local electronic and mechanical characteristics. Although there are well-established analytical characterization methods to analyze the chemical and physical parameters of this material, they remain incapable of fully understanding of the morphological disorders. In this study, x-ray photoelectron spectroscopy (XPS) with an external voltage bias across the sample is used for the characterization of morphological defects in large area of a few layers graphene in a chemically specificmore » fashion. For the XPS measurements, an external +6 V bias applied between the two electrodes and areal analysis for three different elements, C1s, O1s, and Au4f, were performed. By monitoring the variations of the binding energy, the authors extract the voltage variations in the graphene layer which reveal information about the structural defects, cracks, impurities, and oxidation levels in graphene layer which are created purposely or not. Raman spectroscopy was also utilized to confirm some of the findings. This methodology the authors offer is simple but provides promising chemically specific electrical and morphological information.« less

Locating the Binding Sites of Pb(II) Ion with Human and Bovine Serum Albumins

PubMed Central

Belatik, Ahmed; Hotchandani, Surat; Carpentier, Robert; Tajmir-Riahi, Heidar-Ali

2012-01-01

Lead is a potent environmental toxin that has accumulated above its natural level as a result of human activity. Pb cation shows major affinity towards protein complexation and it has been used as modulator of protein-membrane interactions. We located the binding sites of Pb(II) with human serum (HSA) and bovine serum albumins (BSA) at physiological conditions, using constant protein concentration and various Pb contents. FTIR, UV-visible, CD, fluorescence and X-ray photoelectron spectroscopic (XPS) methods were used to analyse Pb binding sites, the binding constant and the effect of metal ion complexation on HSA and BSA stability and conformations. Structural analysis showed that Pb binds strongly to HSA and BSA via hydrophilic contacts with overall binding constants of KPb-HSA = 8.2 (±0.8)×104 M−1 and KPb-BSA = 7.5 (±0.7)×104 M−1. The number of bound Pb cation per protein is 0.7 per HSA and BSA complexes. XPS located the binding sites of Pb cation with protein N and O atoms. Pb complexation alters protein conformation by a major reduction of α-helix from 57% (free HSA) to 48% (metal-complex) and 63% (free BSA) to 52% (metal-complex) inducing a partial protein destabilization. PMID:22574219

Electrodeposition of germanium from supercritical fluids.

PubMed

Ke, Jie; Bartlett, Philip N; Cook, David; Easun, Timothy L; George, Michael W; Levason, William; Reid, Gillian; Smith, David; Su, Wenta; Zhang, Wenjian

2012-01-28

Several Ge(II) and Ge(IV) compounds were investigated as possible reagents for the electrodeposition of Ge from liquid CH(3)CN and CH(2)F(2) and supercritical CO(2) containing as a co-solvent CH(3)CN (scCO(2)) and supercritical CH(2)F(2) (scCH(2)F(2)). For Ge(II) reagents the most promising results were obtained using [NBu(n)(4)][GeCl(3)]. However the reproducibility was poor and the reduction currents were significantly less than the estimated mass transport limited values. Deposition of Ge containing films was possible at high cathodic potential from [NBu(n)(4)][GeCl(3)] in liquid CH(3)CN and supercritical CO(2) containing CH(3)CN but in all cases they were heavily contaminated by C, O, F and Cl. Much more promising results were obtained using GeCl(4) in liquid CH(2)F(2) and supercritical CH(2)F(2). In this case the reduction currents were consistent with mass transport limited reduction and bulk electrodeposition produced amorphous films of Ge. Characterisation by XPS showed the presence of low levels of O, F and C, XPS confirmed the presence of Ge together with germanium oxides, and Raman spectroscopy showed that the as deposited amorphous Ge could be crystallised by the laser used in obtaining the Raman measurements.

The corrosivity and passivity of sputtered Mg-Ti alloys

DOE PAGES

Song, Guang -Ling; Unocic, Kinga A.; Meyer, III, Harry M.; ...

2015-11-30

Our study explored the possibility of forming a “stainless” Mg–Ti alloy. The electrochemical behavior of magnetron-sputtered Mg–Ti alloys was measured in a NaCl solution, and the surface films on the alloys were examined by XPS, SEM and TEM. Increased corrosion resistance was observed with increased Ti content in the sputtered Mg–Ti alloys, but passive-like behavior was not reached until the Ti level (atomic %) was higher than the Mg level. Moreover, the surface film that formed on sputtered Mg–Ti based alloys in NaCl solution was thick, discontinuous and non-protective, whereas a thin, continuous and protective Mg and Ti oxide filmmore » was formed on a sputtered Ti–Mg based alloy.« less

Discrimination between biologically relevant calcium phosphate phases by surface-analytical techniques

NASA Astrophysics Data System (ADS)

Kleine-Boymann, Matthias; Rohnke, Marcus; Henss, Anja; Peppler, Klaus; Sann, Joachim; Janek, Juergen

2014-08-01

The spatially resolved phase identification of biologically relevant calcium phosphate phases (CPPs) in bone tissue is essential for the elucidation of bone remodeling mechanisms and for the diagnosis of bone diseases. Analytical methods with high spatial resolution for the discrimination between chemically quite close phases are rare. Therefore the applicability of state-of-the-art ToF-SIMS, XPS and EDX as chemically specific techniques was investigated. The eight CPPs hydroxyapatite (HAP), β-tricalcium phosphate (β-TCP), α-tricalcium phosphate (α-TCP), octacalcium phosphate (OCP), dicalcium phosphate dihydrate (DCPD), dicalcium phosphate (DCP), monocalcium phosphate (MCP) and amorphous calcium phosphate (ACP) were either commercial materials in high purity or synthesized by ourselves. The phase purity was proven by XRD analysis. All of the eight CPPs show different mass spectra and the phases can be discriminated by applying the principal component analysis method to the mass spectrometric data. The Ca/P ratios of all phosphates were determined by XPS and EDX. With both methods some CPPs can be distinguished, but the obtained Ca/P ratios deviate systematically from their theoretical values. It is necessary in any case to determine a calibration curve, respectively the ZAF values, from appropriate standards. In XPS also the O(1s)-satellite signals are correlated to the CPPs composition. Angle resolved and long-term XPS measurements of HAP clearly prove that there is no phosphate excess at the surface. Decomposition due to X-ray irradiation has not been observed.

Cyclic fatigue resistance of XP-endo Shaper compared with different nickel-titanium alloy instruments.

PubMed

Elnaghy, Amr; Elsaka, Shaymaa

2018-04-01

The aims of this study were to assess and compare the resistance to cyclic fatigue of XP-endo Shaper (XPS; FKG Dentaire, La Chaux-de-Fonds, Switzerland) instruments with TRUShape (TRS; Dentsply Tulsa Dental Specialties, Tulsa, OK, USA), HyFlex CM (HCM; Coltene, Cuyahoga Falls, OH, USA), Vortex Blue (VB; Dentsply Tulsa Dental Specialties), and iRace (iR; FKG Dentaire) nickel-titanium rotary instruments at body temperature. Size 30, 0.01 taper of XPS, size 30, 0.04 taper of HCM, VB, iR, and size 30, 0.06 taper of TRS instruments were immersed in saline at 37 ± 1 °C during cyclic fatigue testing. The instruments were tested with 60° angle of curvature and a 3-mm radius of curvature. The number of cycles to failure (NCF) was calculated and the length of the fractured segment was measured. Fractographic examination of the fractured surface was performed using a scanning electron microscope. The data were analyzed statistically using Kruskal-Wallis H test and Mann-Whitney U tests. Statistical significance was set at P < 0.05. XPS had a significantly greater NCF compared with the other instruments (P < 0.001). The topographic appearance of the fracture surfaces of tested instruments revealed ductile fracture of cyclic fatigue failure. XPS instruments exhibited greater cyclic fatigue resistance compared with the other tested instruments. XP-endo Shaper instruments could be used more safely in curved canals due to their higher fatigue resistance.

Valence-band offsets of CoTiSb/In0.53Ga0.47As and CoTiSb/In0.52Al0.48As heterojunctions

NASA Astrophysics Data System (ADS)

Harrington, S. D.; Sharan, A.; Rice, A. D.; Logan, J. A.; McFadden, A. P.; Pendharkar, M.; Pennachio, D. J.; Wilson, N. S.; Gui, Z.; Janotti, A.; Palmstrøm, C. J.

2017-08-01

The valence-band offsets, ΔEv, between semiconducting half-Heusler compound CoTiSb and lattice-matched III-V In0.53Ga0.47As and In0.52Al0.48As heterojunction interfaces have been measured using X-ray photoemission spectroscopy (XPS). These interfaces were formed using molecular beam epitaxy and transferred in situ for XPS measurements. Valence-band offsets of 0.30 eV and 0.58 eV were measured for CoTiSb/In0.53Ga0.47As and CoTiSb/In0.52Al0.48As, respectively. By combining these measurements with previously reported XPS ΔEv (In0.53Ga0.47As/In0.52Al0.48As) data, the results suggest that band offset transitivity is satisfied. In addition, the film growth order of the interface between CoTiSb and In0.53Ga0.47As is explored and does not seem to affect the band offsets. Finally, the band alignments of CoTiSb with GaAs, AlAs, and InAs are calculated using the density function theory with the HSE06 hybrid functional and applied to predict the band alignment of CoTiSb with In0.53Ga0.47As and In0.52Al0.48As. Good agreement is found between the calculated valence-band offsets and those determined from XPS.

Effects of Mn Ion Implantation on XPS Spectroscopy of GaN Thin Films

NASA Astrophysics Data System (ADS)

Majid, Abdul; Ahmad, Naeem; Rizwan, Muhammad; Khan, Salah Ud-Din; Ali, Fekri Abdulraqeb Ahmed; Zhu, Jianjun

2018-02-01

Gallium nitride (GaN) thin film was deposited onto a sapphire substrate and then implanted with 250 keV Mn ions at two different doses of 2 × 1016 ions/cm2 and 5 × 1016 ions/cm2. The as-grown and post-implantation-thermally-annealed samples were studied in detail using x-ray photoelectron spectroscopy (XPS). The XPS peaks of Ga 3 d, Ga 2 p, N 1 s, Mn 2 p and C 1 s were recorded in addition to a full survey of the samples. The doublet peaks of Ga 2 p for pure GaN were observed blue-shifted when compared with elemental Ga, and appeared further shifted to higher energies for the implanted samples. These observations point to changes in the bonds and the chemical environment of the host as a result of ion implantation. The results revealed broadening of the N 1 s peak after implantation, which is interpreted in terms of the presence of N-Mn bonds in addition to N-Ga bonds. The XPS spectra of Mn 2 p recorded for ion-implanted samples indicated splitting of Mn 2 p 1/2 and Mn 2 p 3/2 peaks higher than that for metallic Mn, which helps rule out the possibility of clustering and points to substitutional doping of Mn. These observations provide a framework that sheds light on the local environment of the material for understanding the mechanism of magnetic exchange interactions in Mn:GaN based diluted magnetic semiconductors.

Electron spectroscopy analysis

NASA Technical Reports Server (NTRS)

Gregory, John C.

1992-01-01

The Surface Science Laboratories at the University of Alabama in Huntsville (UAH) are equipped with x-ray photoelectron spectroscopy (XPS or ESCA) and Auger electron spectroscopy (AES) facilities. These techniques provide information from the uppermost atomic layers of a sample, and are thus truly surface sensitive. XPS provides both elemental and chemical state information without restriction on the type of material that can be analyzed. The sample is placed into an ultra high vacuum (UHV) chamber and irradiated with x-rays which cause the ejection of photoelectrons from the sample surface. Since x-rays do not normally cause charging problems or beam damage, XPS is applicable to a wide range of samples including metals, polymers, catalysts, and fibers. AES uses a beam of high energy electrons as a surface probe. Following electronic rearrangements within excited atoms by this probe, Auger electrons characteristic of each element present are emitted from the sample. The main advantage of electron induced AES is that the electron beam can be focused down to a small diameter and localized analysis can be carried out. On the rastering of this beam synchronously with a video display using established scanning electron microscopy techniques, physical images and chemical distribution maps of the surface can be produced. Thus very small features, such as electronic circuit elements or corrosion pits in metals, can be investigated. Facilities are available on both XPS and AES instruments for depth-profiling of materials, using a beam of argon ions to sputter away consecutive layers of material to reveal sub-surface (and even semi-bulk) analyses.

Synthesis of Fe-based core@ZnO shell nanopowders by laser pyrolysis for biomedical applications

NASA Astrophysics Data System (ADS)

Gavrila-Florescu, Lavinia; Dumitrache, Florian; Balas, Mihaela; Fleaca, Claudiu Teodor; Scarisoreanu, Monica; Morjan, Iuliana P.; Dutu, Elena; Ilie, Alina; Banici, Ana-Maria; Locovei, Claudiu; Prodan, Gabriel

2017-12-01

Nano-sized Fe-based (metallic, carbidic and/or oxidic) core@ZnO shell particles have been successfully synthesized in one step by the laser-induced pyrolysis method in an oxygen-deficient environment. The specific precursors were separately introduced through a three concentric nozzles injector: Fe(CO)5 vapors carried by C2H4 sensitizer (central flow), Zn(C2H5)2 vapors carried and diluted with Ar (middle annular coflow) and Ar containing low amount of O2 (external flow). Keeping constant the ethylene-carried Fe(CO)5 and O2 flows, while diminishing the Zn(C2H5)2 flow, we observed an increase of the Fe/Zn ratio in the resulted nanopowders. Also, using the same metal precursor flows, a nonlinear correlation between O2 external flow and nanocomposite atomic oxygen content is evidenced, indicating a possible interference of supplementary oxidation after air exposure. However, the lowest oxygen content along with metallic zinc was found in the sample synthesized in the most oxygen-deficient environment. Transmission electron microscopy (TEM), high-resolution electron microscopy (HRTEM), selected area electron diffraction (SAED), X-ray diffraction (XRD), energy-dispersive X-ray analysis (EDS), X-ray photoelectron spectroscopy (XPS) and magnetic analyses were performed for a comprehensive characterization. The aqueous Fe-based@ZnO nanoparticles (NPs) suspensions were prepared using L-Dopa ( l-3,4-dihydroxy-phenylalanine) as stabilizing agent in physiologic media. Also, a biocompatibility in vitro study was performed for PBS (phosphate buffered saline)-dispersed L-Dopa-stabilized Fe-based@ZnO nanoparticles with the best core-shell structural features on both human normal lung fibroblasts and tumoral colorectal cells. Our results proved the ability of these newly synthesized nanostructures to target cancer cells in order to induce cytotoxicity and to exhibit biocompatibility on normal cells for maintaining the proper function of healthy tissue.

Nanoparticles of lipid monolayer shell and biodegradable polymer core for controlled release of paclitaxel: effects of surfactants on particles size, characteristics and in vitro performance.

PubMed

Liu, Yutao; Pan, Jie; Feng, Si-Shen

2010-08-16

This work developed a system of nanoparticles of lipid monolayer shell and biodegradable polymer core for controlled release of anticancer drugs with paclitaxel as a model drug, in which the emphasis was given to the effects of the surfactant type and the optimization of the emulsifier amount used in the single emulsion solvent evaporation/extraction process for the nanoparticle preparation on the particle size, characters and in vitro performance. The drug loaded nanoparticles were characterized by laser light scattering (LLS) for size and size distribution, field-emission scanning electron microscopy (FESEM) for surface morphology, X-ray photoelectron spectroscopy (XPS) for surface chemistry, zetasizer for surface charge, and high performance liquid chromatography (HPLC) for drug encapsulation efficiency and in vitro drug release kinetics. MCF-7 breast cancer cells were employed to evaluate the cellular uptake and cytotoxicity. It was found that phospholipids of short chains such as 1,2-dilauroylphosphatidylocholine (DLPC) have great advantages over the traditional emulsifier poly(vinyl alcohol) (PVA), which is used most often in the literature, in preparation of nanoparticles of biodegradable polymers such as poly(D,L-lactide-co-glycolide) (PLGA) for desired particle size, character and in vitro cellular uptake and cytotoxicity. After incubation with MCF-7 cells at 0.250 mg/ml NP concentration, the coumarin-6 loaded PLGA NPs of DLPC shell showed more effective cellular uptake versus those of PVA shell. The analysis of IC(50), i.e. the drug concentration at which 50% of the cells are killed, demonstrated that our DLPC shell PLGA core NP formulation of paclitaxel could be 5.88-, 5.72-, 7.27-fold effective than the commercial formulation Taxol after 24, 48, 72h treatment, respectively. Copyright (c) 2010 Elsevier B.V. All rights reserved.

Theoretical surface core-level shifts for Be(0001)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Feibelman, P.J.

1994-05-15

Core-ionization potentials (CIP's) are computed for Be(0001). Three core features are observed in corresponding photoelectron spectra, with CIP's shifted relative to the bulk core level by [minus]0.825, [minus]0.570, and [minus]0.265 eV. The computed CIP shifts for the outer and subsurface layers, [minus]0.60 and [minus]0.29 eV, respectively, agree with the latter two of these. It is surmised that the [minus]0.825-eV shift is associated with a surface defect. The negative signs of the Be(0001) surface core-level shifts do not fit into the thermochemical picture widely used to explain CIP shifts. The reason is that a core-ionized Be atom is too small tomore » bond effectively to the remainder of the unrelaxed Be lattice.« less

The formation and structure of mechano-synthesized nanocrystalline Sr{sub 3}Fe{sub 2}O{sub 6.4}: XRD Rietveld, Mössabuer and XPS analyses

DOE Office of Scientific and Technical Information (OSTI.GOV)

Al-Rawas, A.D., E-mail: arawas@squ.edu.om; Widatallah, H.M.; Al-Harthi, S.H.

2015-05-15

Highlights: • The formation of mechano-synthesized nanocrystalline Sr{sub 3}Fe{sub 2}O{sub 7−δ} is investigated. • Pre-milling the reactants substantially lowers the formation temperature. • The core and surface structures were studied. • XRD and {sup 57}Fe Mössbauer spectroscopic analyses indicate the δ-value to be 0.60. • XPS shows a complex surface structure for the mechanosynthesized Sr{sub 3}Fe{sub 2}O{sub 7−δ} nanoparticles. - Abstract: The influence of ball milling and subsequent sintering of a 3:1 molar mixture of SrCO{sub 3} and α-Fe{sub 2}O{sub 3} on the formation of Sr{sub 3}Fe{sub 2}O{sub 7−δ} double perovskite is investigated with different analytical techniques. Milling the mixturemore » for 110 h leads to the formation of SrCO{sub 3}-α-Fe{sub 2}O{sub 3} nanocomposites and the structural deformation of α-Fe{sub 2}O{sub 3} via the incorporation of Sr{sup 2+} ions. Subsequent sintering of the pre-milled reactants’ mixture has led to the partial formation of an SrFeO{sub 3} perovskite-related phase in the temperature range 400–600 °C. This was followed by the progressive development of an Sr{sub 3}Fe{sub 2}O{sub 7−δ} phase that continued to increase with increasing sintering temperature until a single-phased nanocrystalline Sr{sub 3}Fe{sub 2}O{sub 7−δ} phase was attained at 950 °C (12 h). This temperature is ∼350 °C lower than the temperature at which the material is prepared conventionally using the ceramic method. The evolution of different structural phases during the reaction process is discussed. Rietveld refinement of the X-ray diffraction data shows a value of 0.60 for the oxygen deficiency δ, in consistency with the Fe{sup 3+}/Fe{sup 4+} ratio derived from the {sup 57}Fe Mössbauer data recorded at both 300 K and 78 K. The Mössbauer data suggests that the Sr{sub 3}Fe{sub 2}O{sub 6.4} nanoparticles are superparamagnetic with blocking temperatures below 78 K. The surfaces of the Sr{sub 3}Fe{sub 2}O{sub 6.4} nanoparticles were shown to have a complex structure and composition relative to those of their cores with traces of SrCO{sub 3}, SrO and SrFeO{sub 3−δ} being detected.« less

Surface characterization of LDEF carbon fiber/polymer matrix composites

NASA Technical Reports Server (NTRS)

Grammer, Holly L.; Wightman, James P.; Young, Philip R.; Slemp, Wayne S.

1995-01-01

XPS (x-ray photoelectron spectroscopy) and SEM (scanning electron microscopy) analysis of both carbon fiber/epoxy matrix and carbon fiber/polysulfone matrix composites revealed significant changes in the surface composition as a result of exposure to low-earth orbit. The carbon 1s curve fit XPS analysis in conjunction with the SEM photomicrographs revealed significant erosion of the polymer matrix resins by atomic oxygen to expose the carbon fibers of the composite samples. This erosion effect on the composites was seen after 10 months in orbit and was even more obvious after 69 months.

A comprehensive study of catalytic, morphological and electronic properties of ligand-protected gold nanoclusters using XPS, STM, XAFS, and TPD techniques

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Qiyuan; Cen, Jiajie; Zhao, Yue

Ultra-small gold nanoclusters were synthesized via a ligand exchange method and deposited onto different TiO2 supports to study their properties. STM imaging revealed that the as-synthesized gold nanoclusters had 2-D morphology consisting of monolayers of gold atoms. In conclusion, subsequent XPS, XAFS, and CO oxidation TPD results indicated that heat treatments of gold clusters at different temperatures significantly altered their electronic and catalytic properties due to ligand deprotection and cluster agglomeration.

XPS and Raman studies of Pt catalysts supported on activated carbon

NASA Astrophysics Data System (ADS)

Tyagi, Deepak; Varma, Salil; Bharadwaj, S. R.

2018-04-01

Activated carbon is a widely used support for dispersing noble metals in addition to its many applications. We have prepared platinum catalyst supported on activated carbon for HI decomposition reaction of I-S thermochemical process of hydrogen generation. These catalysts were characterized by XPS and Raman before and after using for the reaction. It was observed that platinum is present in zero oxidation state, while carbon is present is both sp2 and sp3 hybridized forms along with some amount of it bonded to oxygen.

A critical study of the role of the surface oxide layer in titanium bonding

NASA Technical Reports Server (NTRS)

Dias, S.; Wightman, J. P.

1983-01-01

Scanning electron microscope/X-ray photoelectron spectroscopy (SEM/XPS) analysis of fractured adhesively bonded Ti 6-4 samples is discussed. The text adhesives incuded NR 056X polyimide, polypheylquinoxaline (PPQ), and LARC-13 polyimide. Differentiation between cohesive and interfacial failure was based on the absence of presence of a Ti 2p XPS photopeak. In addition, the surface oxide layer on Ti-(6A1-4V) adherends is characterized and bond strength and durability are addressed. Bond durability in various environmental conditions is discussed.

GaAs Surface Passivation for Device Applications.

DTIC Science & Technology

1981-12-01

Ga203.’" . QI. a) / b) x 2.5 •• 24 21 18 As3d a) b) x 2. / 0 II 2 46 43 40 BINDING ENERGY (eV) Fig. 3 XPS spectra from a Ga2O3 covered GaAs surface of Ga...wU 24 21 Gas 18 SAs3d As2O3 ) .. 46 43 40 BINDING ENERGY (e) Fig. 4 XPS spectra from a AsJ03- Ga2O3 covered GaAs surface of Ga 3d (upper panel) and As

A comprehensive study of catalytic, morphological and electronic properties of ligand-protected gold nanoclusters using XPS, STM, XAFS, and TPD techniques

DOE PAGES

Wu, Qiyuan; Cen, Jiajie; Zhao, Yue; ...

2017-12-08

Ultra-small gold nanoclusters were synthesized via a ligand exchange method and deposited onto different TiO2 supports to study their properties. STM imaging revealed that the as-synthesized gold nanoclusters had 2-D morphology consisting of monolayers of gold atoms. In conclusion, subsequent XPS, XAFS, and CO oxidation TPD results indicated that heat treatments of gold clusters at different temperatures significantly altered their electronic and catalytic properties due to ligand deprotection and cluster agglomeration.

Interfacial chemical reactions between MoS2 lubricants and bearing materials

NASA Technical Reports Server (NTRS)

Zabinski, J. S.; Tatarchuk, B. J.

1989-01-01

XPS and conversion-electron Moessbauer spectroscopy (CEMS) were used to examine iron that was deposited on the basal plane of MoS2 single crystals and subjected to vacuum annealing, oxidizing, and reducing environments. Iron either intercalated into the MoS2 structure or formed oriented iron sulfides, depending on the level of excess S in the MoS2 structure. CEMS data demonstrated that iron sulfide crystal structures preferentially aligned with respect to the MoS2 basal plane, and that alignment (and potentially adhesion) could be varied by appropriate high-temperature annealing procedures.

Mechanical ball-milling preparation of fullerene/cobalt core/shell nanocomposites with high electrochemical hydrogen storage ability.

PubMed

Bao, Di; Gao, Peng; Shen, Xiande; Chang, Cheng; Wang, Longqiang; Wang, Ying; Chen, Yujin; Zhou, Xiaoming; Sun, Shuchao; Li, Guobao; Yang, Piaoping

2014-02-26

The design and synthesis of new hydrogen storage nanomaterials with high capacity at low cost is extremely desirable but remains challenging for today's development of hydrogen economy. Because of the special honeycomb structures and excellent physical and chemical characters, fullerenes have been extensively considered as ideal materials for hydrogen storage materials. To take the most advantage of its distinctive symmetrical carbon cage structure, we have uniformly coated C60's surface with metal cobalt in nanoscale to form a core/shell structure through a simple ball-milling process in this work. The X-ray diffraction (XRD), scanning electron microscope (SEM), Raman spectra, high-solution transmission electron microscopy (HRTEM), energy-dispersive X-ray spectrometry (EDX) elemental mappings, and X-ray photoelectron spectroscopy (XPS) measurements have been conducted to evaluate the size and the composition of the composites. In addition, the blue shift of C60 pentagonal pinch mode demonstrates the formation of Co-C chemical bond, and which enhances the stability of the as-obtained nanocomposites. And their electrochemical experimental results demonstrate that the as-obtained C60/Co composites have excellent electrochemical hydrogen storage cycle reversibility and considerably high hydrogen storage capacities of 907 mAh/g (3.32 wt % hydrogen) under room temperature and ambient pressure, which is very close to the theoretical hydrogen storage capacities of individual metal Co (3.33 wt % hydrogen). Furthermore, their hydrogen storage processes and the mechanism have also been investigated, in which the quasi-reversible C60/Co↔C60/Co-Hx reaction is the dominant cycle process.

Erythrocyte membrane cholesterol and lipid core growth in a rabbit model of atherosclerosis: modulatory effects of rosuvastatin.

PubMed

Tziakas, Dimitrios; Chalikias, Georgios; Kapelouzou, Alkistis; Tentes, Ioannis; Schäfer, Katrin; Karayannakos, Panagiotis; Kostakis, Alkiviadis; Boudoulas, Harissios; Konstantinides, Stavros

2013-12-10

Lipid core expansion is partly responsible for the conversion of a stable atherosclerotic lesion to a rupture-prone plaque. Intraplaque hemorrhage contributes to the accumulation of cholesterol within unstable plaques. In the present study, we investigated, using a rabbit model of atherosclerosis, the extent to which diet-induced increases in cholesterol content of erythrocyte membranes (CEM) contribute to lipid core expansion and the modulatory effect of rosuvastatin use. Rabbits fed with atherogenic diet (0.75% cholesterol) for 5 months exhibited advanced atherosclerotic lesions (mean plaque area, 0.39 ± 0.03 mm(2)), and lipid core size was associated with the concentration-time integral (CTI) of CEM levels (r=0.567, P=0.004) independent of other established predictors of lipid core size. Further experiments were performed by feeding rabbits atherogenic diet (1% cholesterol) for 3 months, followed by either normal diet or normal diet plus rosuvastatin for the next 3 months. Although no differences were observed in total plaque area between both groups, administration of rosuvastatin was associated with significantly smaller lipid cores, fewer macrophages within the lipid core, less microvessels as well as with lower CTI of CEM levels compared to normal diet alone. Moreover, intraplaque erythrocyte membranes covered a smaller lipid core area in rabbits under rosuvastatin plus normal diet as opposed to rabbits under diet alone. Increased CEM levels, induced by high-cholesterol diet, are associated with lipid core growth. Ingestion of a potent HMG-CoA reductase inhibitor (rosuvastatin) may decrease CEM levels, and this effect may contribute to regression of the lipid core. © 2013.

InP/ZnS-graphene oxide and reduced graphene oxide nanocomposites as fascinating materials for potential optoelectronic applications

NASA Astrophysics Data System (ADS)

Samal, Monica; Mohapatra, Priyaranjan; Subbiah, Ramesh; Lee, Chang-Lyoul; Anass, Benayad; Kim, Jang Ah; Kim, Taesung; Yi, Dong Kee

2013-09-01

Our recent studies on metal-organic nanohybrids based on alkylated graphene oxide (GO), reduced alkylated graphene oxide (RGO) and InP/ZnS core/shell quantum dots (QDs) are presented. The GO alkylated by octadecylamine (ODA) and the QD bearing a dodecane thiol (DDT) ligand are soluble in toluene. The nanocomposite alkylated-GO-QD (GOQD) is readily formed from the solution mixture. Treatment of the GOQD composite with hydrazine affords a reduced-alkylated-GO-QD (RGOQD) composite. The structure, morphology, photophysical and electrical properties of GOQDs and RGOQDs are studied. The micro-FTIR and Raman studies demonstrate evidence of the QD interaction with GO and RGO through facile intercalation of the alkyl chains. The field emission scanning electron microscopy (FESEM) and high resolution transmission electron microscopy (HRTEM) images of the GOQD composite show heaps of large QD aggregates piled underneath the GO sheet. Upon reduction to RGOQDs, the QDs become evenly distributed on the graphene bed and the size of the clusters significantly decreases. This also facilitates closer proximity of the QDs to the graphene domains by altering the optoelectronic properties of the RGOQDs. The X-ray photoelectron spectroscopy (XPS) results confirm QDs being retained in the composites, though a small elemental composition change takes place. The XPS and the fluorescence spectra show the presence of an In(Zn)P alloy while the X-ray diffraction (XRD) results show characteristics of the tetragonal indium. The photoluminescence (PL) quenching of QDs in GOQD and RGOQD films determined by the time correlated single photon counting (TCSPC) experiment demonstrates almost complete fluorescence quenching in RGOQDs. The conductance studies demonstrate the differences between GOQDs and RGOQDs. Investigation on the metal-oxide-semiconductor field-effect transistor (nMOSFET) characteristics shows the composite to exhibit p-type channel material properties. The RGOQD exhibits much superior electrical conductance as a channel material compared to the GOQD due to the close proximity of the QDs in the RGOQD to the graphene surface. The transfer characteristics, memory properties, and on/off ratios of the devices are determined. A mechanism has been proposed with reference to the Fermi energies of the composites estimated from the ultraviolet photoelectron spectroscopy (UPS) studies.Our recent studies on metal-organic nanohybrids based on alkylated graphene oxide (GO), reduced alkylated graphene oxide (RGO) and InP/ZnS core/shell quantum dots (QDs) are presented. The GO alkylated by octadecylamine (ODA) and the QD bearing a dodecane thiol (DDT) ligand are soluble in toluene. The nanocomposite alkylated-GO-QD (GOQD) is readily formed from the solution mixture. Treatment of the GOQD composite with hydrazine affords a reduced-alkylated-GO-QD (RGOQD) composite. The structure, morphology, photophysical and electrical properties of GOQDs and RGOQDs are studied. The micro-FTIR and Raman studies demonstrate evidence of the QD interaction with GO and RGO through facile intercalation of the alkyl chains. The field emission scanning electron microscopy (FESEM) and high resolution transmission electron microscopy (HRTEM) images of the GOQD composite show heaps of large QD aggregates piled underneath the GO sheet. Upon reduction to RGOQDs, the QDs become evenly distributed on the graphene bed and the size of the clusters significantly decreases. This also facilitates closer proximity of the QDs to the graphene domains by altering the optoelectronic properties of the RGOQDs. The X-ray photoelectron spectroscopy (XPS) results confirm QDs being retained in the composites, though a small elemental composition change takes place. The XPS and the fluorescence spectra show the presence of an In(Zn)P alloy while the X-ray diffraction (XRD) results show characteristics of the tetragonal indium. The photoluminescence (PL) quenching of QDs in GOQD and RGOQD films determined by the time correlated single photon counting (TCSPC) experiment demonstrates almost complete fluorescence quenching in RGOQDs. The conductance studies demonstrate the differences between GOQDs and RGOQDs. Investigation on the metal-oxide-semiconductor field-effect transistor (nMOSFET) characteristics shows the composite to exhibit p-type channel material properties. The RGOQD exhibits much superior electrical conductance as a channel material compared to the GOQD due to the close proximity of the QDs in the RGOQD to the graphene surface. The transfer characteristics, memory properties, and on/off ratios of the devices are determined. A mechanism has been proposed with reference to the Fermi energies of the composites estimated from the ultraviolet photoelectron spectroscopy (UPS) studies. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr02333h

Grafting titanium nitride surfaces with sodium styrene sulfonate thin films

PubMed Central

Zorn, Gilad; Migonney, Véronique; Castner, David G.

2014-01-01

The importance of titanium nitride lies in its high hardness and its remarkable resistance to wear and corrosion, which has led to its use as a coating for the heads of hip prostheses, dental implants and dental surgery tools. However, the usefulness of titanium nitride coatings for biomedical applications could be significantly enhanced by modifying their surface with a bioactive polymer film. The main focus of the present work was to graft a bioactive poly(sodium styrene sulfonate) (pNaSS) thin film from titanium nitride surfaces via a two-step procedure: first modifying the surface with 3-methacryloxypropyltrimethoxysilane (MPS) and then grafting the pNaSS film from the MPS modified titanium through free radical polymerization. X-ray photoelectron spectroscopy (XPS) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) were used after each step to characterize success and completeness of each reaction. The surface region of the titanium nitride prior to MPS functionalization and NaSS grafting contained a mixture of titanium nitride, oxy-nitride, oxide species as well as adventitious surface contaminants. After MPS functionalization, Si was detected by XPS, and characteristic MPS fragments were detected by ToF-SIMS. After NaSS grafting, Na and S were detected by XPS and characteristic NaSS fragments were detected by ToF-SIMS. The XPS determined thicknesses of the MPS and NaSS overlayers were ∼1.5 and ∼1.7 nm, respectively. The pNaSS film density was estimated by the toluidine blue colorimetric assay to be 260 ± 70 ng/cm2. PMID:25280842

[Quantitative surface analysis of Pt-Co, Cu-Au and Cu-Ag alloy films by XPS and AES].

PubMed

Li, Lian-Zhong; Zhuo, Shang-Jun; Shen, Ru-Xiang; Qian, Rong; Gao, Jie

2013-11-01

In order to improve the quantitative analysis accuracy of AES, We associated XPS with AES and studied the method to reduce the error of AES quantitative analysis, selected Pt-Co, Cu-Au and Cu-Ag binary alloy thin-films as the samples, used XPS to correct AES quantitative analysis results by changing the auger sensitivity factors to make their quantitative analysis results more similar. Then we verified the accuracy of the quantitative analysis of AES when using the revised sensitivity factors by other samples with different composition ratio, and the results showed that the corrected relative sensitivity factors can reduce the error in quantitative analysis of AES to less than 10%. Peak defining is difficult in the form of the integral spectrum of AES analysis since choosing the starting point and ending point when determining the characteristic auger peak intensity area with great uncertainty, and to make analysis easier, we also processed data in the form of the differential spectrum, made quantitative analysis on the basis of peak to peak height instead of peak area, corrected the relative sensitivity factors, and verified the accuracy of quantitative analysis by the other samples with different composition ratio. The result showed that the analytical error in quantitative analysis of AES reduced to less than 9%. It showed that the accuracy of AES quantitative analysis can be highly improved by the way of associating XPS with AES to correct the auger sensitivity factors since the matrix effects are taken into account. Good consistency was presented, proving the feasibility of this method.

Valence-band offsets of CoTiSb/In 0.53Ga 0.47As and CoTiSb/In 0.52Al 0.48As heterojunctions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Harrington, S. D.; Sharan, A.; Rice, A. D.

2017-08-11

The valence-band offsets, ΔE v, between semiconducting half-Heusler compound CoTiSb and lattice-matched III-V In 0.53Ga 0.47As and In 0.52Al 0.48As heterojunction interfaces have been measured using X-ray photoemission spectroscopy (XPS). These interfaces were formed using molecular beam epitaxy and transferred in situ for XPS measurements. Valence-band offsets of 0.30 eV and 0.58 eV were measured for CoTiSb/In 0.53Ga 0.47As and CoTiSb/In 0.52Al 0.48As, respectively. By combining these measurements with previously reported XPS ΔE v (In 0.53Ga 0.47As/In 0.52Al 0.48As) data, the results suggest that band offset transitivity is satisfied. In addition, the film growth order of the interface between CoTiSbmore » and In 0.53Ga 0.47As is explored and does not seem to affect the band offsets. Finally, the band alignments of CoTiSb with GaAs, AlAs, and InAs are calculated using the density function theory with the HSE06 hybrid functional and applied to predict the band alignment of CoTiSb with In 0.53Ga 0.47As and In 0.52Al 0.48As. As a result, good agreement is found between the calculated valence-band offsets and those determined from XPS.« less

Electronic structure and optical properties of noncentrosymmetric LiGaGe2Se6, a promising nonlinear optical material

NASA Astrophysics Data System (ADS)

Lavrentyev, A. A.; Gabrelian, B. V.; Vu, V. T.; Ananchenko, L. N.; Isaenko, L. I.; Yelisseyev, A.; Krinitsin, P. G.; Khyzhun, O. Y.

2016-11-01

X-ray photoelectron core-level and valence-band spectra are measured for pristine and Ar+ ion-bombarded surfaces of LiGaGe2Se6 single crystal grown by Bridgman-Stockbarger technique. Further, electronic structure of LiGaGe2Se6 is elucidated from both theoretical and experimental viewpoints. Density functional theory (DFT) calculations are made using the augmented plane wave +local orbitals (APW+lo) method to study total and partial densities of states in the LiGaGe2Se6 compound. The present calculations indicate that the principal contributors to the valence band are the Se 4p states: they contribute mainly at the top and in the central portion of the valence band of LiGaGe2Se6, with also their significant contributions in its lower portion. The Ge 4s and Ge 4p states are among other significant contributors to the valence band of LiGaGe2Se6, contributing mainly at the bottom and in the central portion, respectively. In addition, the calculations indicate that the bottom of the conduction band is composed mainly from the unoccupied Ge s and Se p states. The present DFT calculations are supported experimentally by comparison on a common energy scale of the X-ray emission bands representing the energy distribution of the 4p states associated with Ga, Ge and Se and the XPS valence-band spectrum of the LiGaGe2Se6 single crystal. The main optical characteristics of the LiGaGe2Se6 compound are elucidated by the first-principles calculations.

Electronic structure of the (Nd{sub 1−x}Dy{sub x}){sub 2}Fe{sub 14}B (0 ≤ x ≤ 1) system studied by X-ray photoelectron spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jing; Liang, Le; Yang, Bin

2015-09-15

Systematic characterization of electronic structures in the (Nd{sub 1−x}Dy{sub x}){sub 2}Fe{sub 14}B system, especially the 4f behavior, provides an insight to the physical nature of the evolution of magnetic properties. A series of X-ray photoelectron spectroscopy (XPS) core-level and valence-band spectra were used to study the electronic structures. It was found that substitution of Dy for Nd in Nd{sub 2}Fe{sub 14}B results in a nonlinear variation in the evolution of electronic structures. Only the finite coupling between the Nd 4f states and the Fe 3d states is found at both the Nd-rich regime and the Dy-rich regime. When the Dymore » concentration and the Nd concentration approach to be equal, a strong coupling between the Nd 4f states and the Fe 3d states is found, which results in a bonding state between them. Additionally, the 4f components in the (Nd{sub 1−x}Dy{sub x}){sub 2}Fe{sub 14}B system are ascribed to three parts: 1) the individual contribution of the Dy 4f states, which emerges just after the Dy-substitution; 2) the contribution of the coupling between the Nd 4f states and the Dy 4f states, which arises only when 0.4 ≤ x ≤ 0.6; 3) the associated contributions of the Nd 4f states and the Dy 4f states, where the contribution of the Nd 4f states and that of the Dy 4f states are prominent in the Nd-rich regime and Dy-rich regime, respectively.« less

Microscopic origin of lattice contraction and expansion in undoped rutile TiO2 nanostructures

NASA Astrophysics Data System (ADS)

Santara, Batakrushna; Giri, P. K.; Imakita, Kenji; Fujii, Minoru

2014-05-01

We have investigated the microscopic origin of lattice expansion and contraction in undoped rutile TiO2 nanostructures by employing several structural and optical spectroscopic tools. Rutile TiO2 nanostructures with morphologies such as nanorods, nanopillars and nanoflowers, depending upon the growth conditions, are synthesized by an acid-hydrothermal process. Depending on the growth conditions and post-growth annealing, lattice contraction and expansion are observed in the nanostructures and it is found to correlate with the nature and density of intrinsic defects in rutile TiO2. The change in lattice volume correlates well with the optical bandgap energy. Irrespective of growth conditions, theTiO2 nanostructures exhibit strong near infrared (NIR) photoluminescence (PL) at 1.43 eV and a weak visible PL, which are attributed to the Ti interstitials and O vacancies, respectively, in rutile TiO2 nanostructures. Further, ESR study reveals the presence of singly ionized oxygen vacancy defects. It is observed that lattice distortion depends systematically on the relative concentration and type of defects such as oxygen vacancies and Ti interstitials. XPS analyses revealed a downshift in energy for both Ti 2p and O 1s core level spectra for various growth conditions, which is believed to arise from the lattice distortions. It is proposed that the Ti4+ interstitial and F+ oxygen vacancy defects are primarily responsible for lattice expansion, whereas the electrostatic attraction between Ti4+ interstitial and O2- interstitial defects causes the lattice contraction in the undoped TiO2 nanostructures. The control of lattice parameters through the intrinsic defects may provide new routes to achieving novel functionalities in advanced materials that can be tailored for future technological applications.

Composition dependent structural and optical properties of PbF₂-TeO₂-B₂O₃-Eu₂O₃ glasses.

PubMed

Wagh, Akshatha; Raviprakash, Y; Upadhyaya, Vyasa; Kamath, Sudha D

2015-12-05

Boric oxide based quaternary glasses in the system PbF2-TeO2-B2O3-Eu2O3 have been prepared by melt quenching technique. Density, molar volume, FTIR, UV-Vis techniques were used to probe the structural modifications with incorporation of europium ions in the glass network. An increase in glass density & decrease in molar volume (Vm) values proved the structural changes occurring in coordination of boron atom [conversion of BO3 units to BO4]. This resulted in the increase of the compaction of the prepared glasses with increase in Eu2O3 contents. The amorphous natures of the samples were ascertained by XRD and metallization criterion (M) studies. XPS study showed the values of core-level binding energy [O1s, Eu3d, Eu4d, Te3d, Te4d, Pd4f, Pb5d, O1s, and F1s] of (PbF2-TeO2-B2O3-Eu2O3) the glass matrix. The frequency and temperature dependence of dielectric properties of present glasses were investigated in the frequency range of 1 Hz-10 MHz and temperature range of 313-773K. The study of dielectric measurements proved good insulating and thermal stability of the prepared glasses. At room temperature, dielectric loss [tanδ] values were negligibly small for prepared glasses and increased with increase in temperature. FTIR spectroscopy results were in good agreement with optical band energy gap, density, molar volume and hardness values revealing network modifications caused by europium ions in the glass structure. Copyright © 2015 Elsevier B.V. All rights reserved.

The reversal of the spontaneous exchange bias effect and zero-field-cooling magnetization in La1.5Sr0.5Co1-xFexMnO6: the effect of Fe doping.

PubMed

Zhang, H G; Xie, L; Liu, X C; Xiong, M X; Cao, L L; Li, Y T

2017-09-20

The crystal structure, electronic structure and magnetic properties were systematically studied in a series of Fe-doped La 1.5 Sr 0.5 CoMnO 6 double perovskites. The X-ray diffraction patterns of the samples are all refined with a rhombohedral (R3[combining macron]c) structure. The parameters a and c continuously increase with increasing Fe doping concentration x. X-ray photoelectron spectroscopy (XPS) spectra of the Mn, Co, and Fe 2p core levels, consistent with the soft X-ray absorption spectroscopy (XAS) spectra of Mn, Co, and Fe L 2,3 edges, indicate that their valence states are Mn 3+ and Mn 4+ , Co 2+ and Co 3+ , and Fe 3+ , respectively. However, relative to samples with x ≤ 0.1, there is an abrupt change of photon energy in the Co- and Fe-2p XAS spectra for x ≥ 0.2, implying the spin state transition is from high to low. In addition, this is further confirmed by a comparison between the calculated effective spin moment from the paramagnetic data and the theoretical value. Interestingly, we demonstrate the reversal of both zero-field-cooling magnetization and the sign switching of the spontaneous exchange bias (SEB) with the doping concentration from magnetic measurements. The magnetization reverses from positive to negative with the temperature decreasing across the compensation temperature at the critical concentration x = 0.2. Meanwhile, the exchange bias field of the SEB reverses from large negative values to positive ones. Our findings allow us to propose that the spin state transition caused by inhomogeneity is considered to play an important role in the reversal of the magnetization and the SEB effect.

Orthorhombic MoO3 nanobelts based NO2 gas sensor

NASA Astrophysics Data System (ADS)

Mane, A. A.; Moholkar, A. V.

2017-05-01

Molybdenum trioxide (MoO3) nanobelts have been deposited onto the glass substrates using chemical spray pyrolysis (CSP) deposition method. The XRD patterns reveal that films are polycrystalline having an orthorhombic crystal structure. Raman spectra confirm that the films are orthorhombic in phase. The XPS study shows the presence of two well resolved spectral lines of Mo-3d core levels appearing at the binding energy values of 232.82 eV and 235.95 eV corresponding to Mo-3d5/2 and Mo-3d3/2, respectively. These binding energy values are assigned to Mo6+ oxidation state of fully oxidized MoO3. The FE-SEM micrographs show the formation of nanobelts-like morphology. The AFM micrographs reveal that the RMS surface roughness increases from 16.5 nm to 17.5 nm with increase in film thickness from 470 nm to 612 nm and then decreases to 16 nm for 633 nm film thickness. The band gap energy is found to be decreased from 3.40 eV to 3.38 eV. To understand the electronic transport phenomenon in MoO3 thin films, dielectric properties are studied. For 612 nm film thickness, the highest NO2 gas response of 68% is obtained at an operating temperature of 200 °C for 100 ppm concentration with response and recovery times of 15 s and 150 s, respectively. The lower detection limit is found to be 10 ppm which is half of the immediately dangerous to life or health (IDLH) value of 20 ppm. Finally, NO2 gas sensing mechanism in an orthorhombic MoO3 crystal structure is discussed in detail.

Electronic structure and optical properties of Cs2HgI4: Experimental study and band-structure DFT calculations

NASA Astrophysics Data System (ADS)

Lavrentyev, A. A.; Gabrelian, B. V.; Vu, V. T.; Shkumat, P. N.; Myronchuk, G. L.; Khvyshchun, M.; Fedorchuk, A. O.; Parasyuk, O. V.; Khyzhun, O. Y.

2015-04-01

High-quality single crystal of cesium mercury tetraiodide, Cs2HgI4, has been synthesized by the vertical Bridgman-Stockbarger method and its crystal structure has been refined. In addition, electronic structure and optical properties of Cs2HgI4 have been studied. For the crystal under study, X-ray photoelectron core-level and valence-band spectra for pristine and Ar+-ion irradiated surfaces have been measured. The present X-ray photoelectron spectroscopy (XPS) results indicate that the Cs2HgI4 single crystal surface is very sensitive with respect to Ar+ ion-irradiation. In particular, Ar+ bombardment of the single crystal surface alters the elemental stoichiometry of the Cs2HgI4 surface. To elucidate peculiarities of the energy distribution of the electronic states within the valence-band and conduction-band regions of the Cs2HgI4 compound, we have performed first-principles band-structure calculations based on density functional theory (DFT) as incorporated in the WIEN2k package. Total and partial densities of states for Cs2HgI4 have been calculated. The DFT calculations reveal that the I p states make the major contributions in the upper portion of the valence band, while the Hg d, Cs p and I s states are the dominant contributors in its lower portion. Temperature dependence of the light absorption coefficient and specific electrical conductivity has been explored for Cs2HgI4 in the temperature range of 77-300 K. Main optical characteristics of the Cs2HgI4 compound have been elucidated by the first-principles calculations.

20 CFR 666.120 - What are the procedures for negotiating annual levels of performance?

Code of Federal Regulations, 2010 CFR

2010-04-01

... performance for each core indicator and the customer satisfaction indicators. In negotiating these levels, the... customer satisfaction; (3) The extent to which the levels of performance promote continuous improvement and... Governor must reach agreement on levels of performance for each core indicator and the customer...

Polyethylene imine modified hydrochar adsorption for chromium (VI) and nickel (II) removal from aqueous solution.

PubMed

Shi, Yuanji; Zhang, Tao; Ren, Hongqiang; Kruse, Andrea; Cui, Ruofan

2018-01-01

An adsorbent hydrochar was synthesized from corn cobs and modified with polyethylene imine (PEI). The hydrochars before and after modification were characterized by scanning electron microscopy, Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis. FTIR and XPS revealed that the PEI was grafted onto the hydrochar via ether and imine bonds formed with glutaraldehyde. The maximum adsorption capacities for Cr(VI) (33.663mg/g) and Ni(II) (29.059mg/g) on the modified hydrochars were 365% and 43.7% higher, respectively, than those on the unmodified hydrochar. A pseudo-second-order model described the adsorption of Ni(II) and Cr(VI) on all the adsorbents. The adsorption of Cr(VI) was endothermic, spontaneous, increased disorder, and obeyed the Langmuir model. By contrast, the adsorption of Ni(II) was exothermic, spontaneous, decreased disorder, and obeyed the Freundlich model. XPS confirmed that the adsorption sites and mechanisms for Ni(II) and Cr(VI) on the modified hydrochars were different. Copyright © 2017 Elsevier Ltd. All rights reserved.

Potassium-doped n-type bilayer graphene

NASA Astrophysics Data System (ADS)

Yamada, Takatoshi; Okigawa, Yuki; Hasegawa, Masataka

2018-01-01

Potassium-doped n-type bilayer graphene was obtained. Chemical vapor deposited bilayer and single layer graphene on copper (Cu) foils were used. After etching of Cu foils, graphene was dipped in potassium hydroxide aqueous solutions to dope potassium. Graphene on silicon oxide was characterized by X-ray photoelectron spectroscopy (XPS), energy dispersive X-ray spectroscopy (EDX), and Raman spectroscopy. Both XPS and EDX spectra indicated potassium incorporation into the bilayer graphene via intercalation between the graphene sheets. The downward shift of the 2D peak position of bilayer graphene after the potassium hydroxide (KOH) treatment was confirmed in Raman spectra, indicating that the KOH-treated bilayer graphene was doped with electrons. Electrical properties were measured using Hall bar structures. The Dirac points of bilayer graphene were shifted from positive to negative by the KOH treatment, indicating that the KOH-treated bilayer graphene was n-type conduction. For single layer graphene after the KOH treatment, although electron doping was confirmed from Raman spectra, the peak of potassium in the X-ray photoelectron spectroscopy (XPS) spectrum was not detected. The Dirac points of single layer graphene with and without the KOH treatment showed positive.

Surface characterization in composite and titanium bonding: Carbon fiber surface treatments for improved adhesion to thermoplastic polymers

NASA Technical Reports Server (NTRS)

Devilbiss, T. A.; Wightman, J. P.

1987-01-01

The effect of anodization in NaOH, H2SO4, and amine salts on the surface chemistry of carbon fibers was examined by X-ray photoelectron spectroscopy (XPS). The surfaces of carbon fibers after anodization in NaOH and H2SO4 were examined by scanning transmission electron microscopy (STEM), angular dependent XPS, UV absorption spectroscopy of the anodization bath, secondary ion mass spectrometry, and polar/dispersive surface energy analysis. Hercules AS-4, Dexter Hysol XAS, and Union Carbide T-300 fibers were examined by STEM, angular dependent XPS, and breaking strength measurement before and after commercial surface treatment. Oxygen and nitrogen were added to the fiber surfaces by anodization in amine salts. Analysis of the plasmon peak in the carbon 1s signal indicated that H2SO4 anodization affected the morphological structure of the carbon fiber surface. The work of adhesion of carbon fibers to thermoplastic resins was calculated using the geometric mean relationship. A correlation was observed between the dispersive component of the work of adhesion and the interfacial adhesion.

Evaluation of the surface properties of PTFE foam coating filter media using XPS and contact angle measurements

NASA Astrophysics Data System (ADS)

Park, Byung Hyun; Lee, Myong-Hwa; Kim, Sang Bum; Jo, Young Min

2011-02-01

A newly developed PTFE foam coating filter was developed which can be used for hot gas cleaning at temperatures up to 250 °C. The emulsion-type PTFE was coated onto a woven glass fiber using a foam coating method. The filter surface was closely examined using X-ray photoelectron spectroscopy (XPS) and contact angle measurements. The XPS results were used to determine the binding force between the carbon and fluorine of PTFE, which imparts coating stability to the filter medium. More than 95% of the bonds of the PTFE foam coating filter were between carbon and fluorine, and this filter demonstrated excellent hydrophobic and good oleophobic properties at the same time. The contact angles of liquid droplets on the filter surface were used to predict the potential wetability of the filter against water or oil. In addition, the very low surface free energy of the filter medium, which was evaluated using the Owens-Wendt method, demonstrates a very stable surface and a high de-dusting quality.

Deposition and characterization of stoichiometric films of V2O5 on Pd(111)

NASA Astrophysics Data System (ADS)

Feng, Xu; Abdel-Rahman, Mohammed K.; Kruppe, Christopher M.; Trenary, Michael

2017-10-01

A simple and efficient method has been used to grow V2O5 thin films on Pd(111) at a substrate temperature of 300 K through physical vapor deposition by heating a fine powder of V2O5 in a non-oxidative, UHV environment. X-ray photoelectron spectroscopy (XPS), reflection absorption infrared spectroscopy (RAIRS) and low energy electron diffraction (LEED) were used to characterize the thin films. When the as-grown films exceed a minimum thickness, characteristic features of V2O5 were revealed by XPS and RAIRS, which confirms the presence of stoichiometric V2O5. LEED indicates no long range order of the as-grown films at 300 K. Annealing to temperatures between 600 and 700 K causes a reduction of V2O5 to VO2 as identified by XPS and the formation of ordered structures as determined by LEED, and VO2 is predominant after annealing to 800 K. After further annealing to 1000 K, only an ordered form of V2O3 is present on Pd(111).

Long-term lithium-ion battery performance improvement via ultraviolet light treatment of the graphite anode

DOE PAGES

An, Seong Jin; Li, Jianlin; Sheng, Yangping; ...

2016-01-01

Effects of ultraviolet (UV) light on dried graphite anodes were investigated in terms of the cycle life of lithium ion batteries. The time variations for the UV treatment were 0 (no treatment), 20, 40, and 60 minutes. UV-light-treated graphite anodes were assembled for cycle life tests in pouch cells with pristine Li 1.02Ni 0.50Mn 0.29Co 0.19O 2 (NMC 532) cathodes. UV treatment for 40 minutes resulted in the highest capacity retention and the lowest resistance after the cycle life testing. X-ray photoelectron spectroscopy (XPS) and contact angle measurements on the graphite anodes showed changes in surface chemistry and wetting aftermore » the UV treatment. XPS also showed increases in solvent products and decreases in salt products on the SEI surface when UV-treated anodes were used. In conclusion, the thickness of the surface films and their compositions on the anodes and cathodes were also estimated using survey scans and snapshots from XPS depth profiles.« less

Epitaxial corundum-VTiO 3 thin films grown on c-cut sapphire

DOE PAGES

Kramer, Alan; Sutter, Eli; Su, Dong; ...

2017-04-12

Corundum structured VTiO 3 has been grown as epitaxial films on c-cut sapphire by laser molecular beam epitaxy. The properties of the film were characterized by reflection high energy electron diffraction, x-ray diffraction, transmission electron microscopy, and photoemission spectroscopy. All the structural probes clearly indicate the corundum structure of the film. X-ray photoemission spectroscopy (XPS) indicates that V is in a 3+ charge state implying that Ti also needs to adopt a 3+ charge state in order for the corundum structure to form. However, the Ti-2p XPS, while clearly broadened to the lower binding energy side compared to TiO 2,more » also exhibits a pronounced Ti 4+ component. This is tentatively assigned to a final state effect in XPS measurements and not as the true cation state. In conclusion, the valence band spectra show occupation of 3d metal states that resemble more closely those of Ti 2O 3 than for V 2O 3, suggesting that only the a1g molecular states are occupied.« less

Quantification of Efficiency of Beneficiation of Lunar Regolith

NASA Technical Reports Server (NTRS)

Trigwell, Steve; Lane, John; Captain, James; Weis, Kyle; Quinn, Jacqueline; Watanabe, Fumiya

2011-01-01

Electrostatic beneficiation of lunar regolith is being researched at Kennedy Space Center to enhance the ilmenite concentration of the regolith for the production of oxygen in in-situ resource utilization on the lunar surface. Ilmenite enrichment of up to 200% was achieved using lunar simulants. For the most accurate quantification of the regolith particles, standard petrographic methods are typically followed, but in order to optimize the process, many hundreds of samples were generated in this study that made the standard analysis methods time prohibitive. In the current studies, X-ray photoelectron spectroscopy (XPS) and Secondary Electron microscopy/Energy Dispersive Spectroscopy (SEM/EDS) were used that could automatically, and quickly, analyze many separated fractions of lunar simulant. In order to test the accuracy of the quantification, test mixture samples of known quantities of ilmenite (2, 5, 10, and 20 wt%) in silica (pure quartz powder), were analyzed by XPS and EDS. The results showed that quantification for low concentrations of ilmenite in silica could be accurately achieved by both XPS and EDS, knowing the limitations of the techniques. 1

Characterization of Colloidal Quantum Dot Ligand Exchange by X-ray Photoelectron Spectroscopy

NASA Astrophysics Data System (ADS)

Atewologun, Ayomide; Ge, Wangyao; Stiff-Roberts, Adrienne D.

2013-05-01

Colloidal quantum dots (CQDs) are chemically synthesized semiconductor nanoparticles with size-dependent wavelength tunability. Chemical synthesis of CQDs involves the attachment of long organic surface ligands to prevent aggregation; however, these ligands also impede charge transport. Therefore, it is beneficial to exchange longer surface ligands for shorter ones for optoelectronic devices. Typical characterization techniques used to analyze surface ligand exchange include Fourier-transform infrared spectroscopy, x-ray diffraction, transmission electron microscopy, and nuclear magnetic resonance spectroscopy, yet these techniques do not provide a simultaneously direct, quantitative, and sensitive method for evaluating surface ligands on CQDs. In contrast, x-ray photoelectron spectroscopy (XPS) can provide nanoscale sensitivity for quantitative analysis of CQD surface ligand exchange. A unique aspect of this work is that a fingerprint is identified for shorter surface ligands by resolving the regional XPS spectrum corresponding to different types of carbon bonds. In addition, a deposition technique known as resonant infrared matrix-assisted pulsed laser evaporation is used to improve the CQD film uniformity such that stronger XPS signals are obtained, enabling more accurate analysis of the ligand exchange process.

Charge transfer induced by MoO3 at boron subphthalocyanine chloride/α-sexithiophene heterojunction interface

NASA Astrophysics Data System (ADS)

Foggiatto, Alexandre L.; Sakurai, Takeaki

2018-03-01

The energy-level alignment of boron subphthalocyanine chloride (SubPc)/α-sexithiophene (6T) grown on MoO3 was investigated using ultraviolet and X-ray photoelectron spectroscopy (UPS and XPS). We demonstrated that the p-doping effect generated by the MoO3 layer can induce charge transfer at the organic-organic heterojunction interface. After the deposition of 6T on MoO3, the fermi level becomes pinned close to the 6T highest occupied molecular orbital (HOMO) level and when SubPc is deposited, owing to its tail states, charge transfer occurs in order to achieve thermodynamic equilibrium. We also demonstrated that the charge transfer can be reduced by annealing the film. We suggested that the reduction of the misalignment on the film induces a reduction in the density of gap states, which controls the charge transfer.

Angular dependent XPS study of surface band bending on Ga-polar n-GaN

NASA Astrophysics Data System (ADS)

Huang, Rong; Liu, Tong; Zhao, Yanfei; Zhu, Yafeng; Huang, Zengli; Li, Fangsen; Liu, Jianping; Zhang, Liqun; Zhang, Shuming; Dingsun, An; Yang, Hui

2018-05-01

Surface band bending and composition of Ga-polar n-GaN with different surface treatments were characterized by using angular dependent X-ray photoelectron spectroscopy. Upward surface band bending of varying degree was observed distinctly upon to the treatment methods. Besides the nitrogen vacancies, we found that surface states of oxygen-containing absorbates (O-H component) also contribute to the surface band bending, which lead the Fermi level pined at a level further closer to the conduction band edge on n-GaN surface. The n-GaN surface with lower surface band bending exhibits better linear electrical properties for Ti/GaN Ohmic contacts. Moreover, the density of positively charged surface states could be derived from the values of surface band bending.

RELAP5 Analyses of OECD/NEA ROSA-2 Project Experiments on Intermediate-Break LOCAs at Hot Leg or Cold Leg

NASA Astrophysics Data System (ADS)

Takeda, Takeshi; Maruyama, Yu; Watanabe, Tadashi; Nakamura, Hideo

Experiments simulating PWR intermediate-break loss-of-coolant accidents (IBLOCAs) with 17% break at hot leg or cold leg were conducted in OECD/NEA ROSA-2 Project using the Large Scale Test Facility (LSTF). In the hot leg IBLOCA test, core uncovery started simultaneously with liquid level drop in crossover leg downflow-side before loop seal clearing (LSC) induced by steam condensation on accumulator coolant injected into cold leg. Water remained on upper core plate in upper plenum due to counter-current flow limiting (CCFL) because of significant upward steam flow from the core. In the cold leg IBLOCA test, core dryout took place due to rapid liquid level drop in the core before LSC. Liquid was accumulated in upper plenum, steam generator (SG) U-tube upflow-side and SG inlet plenum before the LSC due to CCFL by high velocity vapor flow, causing enhanced decrease in the core liquid level. The RELAP5/MOD3.2.1.2 post-test analyses of the two LSTF experiments were performed employing critical flow model in the code with a discharge coefficient of 1.0. In the hot leg IBLOCA case, cladding surface temperature of simulated fuel rods was underpredicted due to overprediction of core liquid level after the core uncovery. In the cold leg IBLOCA case, the cladding surface temperature was underpredicted too due to later core uncovery than in the experiment. These may suggest that the code has remaining problems in proper prediction of primary coolant distribution.

Interfacial functionalization and engineering of nanoparticles

NASA Astrophysics Data System (ADS)

Song, Yang

The intense research interest in nanoscience and nanotechnology is largely fueled by the unique properties of nanoscale materials. In this dissertation, the research efforts are focused on surface functionalization and interfacial engineering of functional nanoparticles in the preparation of patchy nanoparticles (e.g., Janus nanoparticles and Neapolitan nanoparticles) such that the nanoparticle structures and properties may be manipulated to an unprecedented level of sophistication. Experimentally, Janus nanoparticles were prepared by an interfacial engineering method where one hemisphere of the originally hydrophobic nanoparticles was replaced with hydrophilic ligands at the air|liquid or solid|liquid interface. The amphiphilic surface characters of the Janus nanoparticles were verified by contact angle measurements, as compared to those of the bulk-exchange counterparts where the two types of ligands were distributed rather homogeneously on the nanoparticle surface. In a further study, a mercapto derivative of diacetylene was used as the hydrophilic ligands to prepare Janus nanoparticles by using hydrophobic hexanethiolate-protected gold nanoparticles as the starting materials. Exposure to UV irradiation led to effective covalent cross-linking between the diacetylene moieties of neighboring ligands and hence marked enhancement of the structural integrity of the Janus nanoparticles, which was attributable to the impeded surface diffusion of the thiol ligands on the nanoparticle surface, as manifested in fluorescence measurements of aged nanoparticles. More complicated bimetallic AgAu Janus nanoparticles were prepared by interfacial galvanic exchange reactions of a Langmuir-Blodgett monolayer of 1-hexanethiolate-passivated silver nanoparticles on a glass slide with gold(I)-mercaptopropanediol complex in a water/ethanol solution. The resulting nanoparticles exhibited an asymmetrical distribution not only of the organic capping ligands on the nanoparticle surface but also of the metal elements in the nanoparticle cores, in contrast to the bulk-exchange counterparts where these distributions were homogeneous within the nanoparticles, as manifested in contact angle, UV--vis, XPS, and TEM measurements. More interestingly, the electrocatalytic performance of the Janus nanoparticles was markedly better than the bulk-exchange ones, suggesting that the segregated distribution of the polar ligands from the apolar ones might further facilitate charge transfer from Ag to Au in the nanoparticle cores, leading to additional improvement of the adsorption and reduction of oxygen. This interfacial protocol was then adopted to prepare trimetallic Ag AuPt Neapolitan nanoparticles by two sequential galvanic exchange reactions of 1-hexanethiolate-capped silver nanoparticles with gold(I)-thiomalic acid and platinum(II)-hexanethiolate complexes. As both reactions were confined to an interface, the Au and Pt elements were situated on two opposite poles of the original Ag nanoparticles, which was clearly manifested in elemental mapping of the nanoparticles, and consistent with the damping and red-shift of the nanoparticle surface plasmon resonance. As nanoscale analogs to conventional amphiphilic molecules, the resulting Janus nanoparticles were found to form oil-in-water micelle-like or water-in-oil reverse micelle-like superparticulate structures depending on the solvent media. These unique characteristics were exploited for the effective transfer of diverse guest nanoparticles between organic and water phase. The transfer of hydrophobic nanoparticles from organic to water media or water-soluble nanoparticles to the organic phase was evidenced by TEM, DLS, UV-Vis, and PL measurements. In particular, line scans based on EDS analysis showed that the vesicle-like structures consisted of multiple layers of the Janus nanoparticles, which encapsulated the guest nanoparticles in the cores. The results highlight the unique effectiveness of using Janus nanoparticles in the formation of functional nanocomposites. Part of the dissertation research was also devoted to graphene quantum dots (GQDs)-supported platinum (Pt/G) nanoparticles and their electrocatalytic activity in oxygen reduction reaction. These Pt/G nanocomposites were prepared by a hydrothermal procedure at controlled temperatures. Spectroscopic measurements based on FTIR, Raman and XPS confirmed the formation of various oxygenated structural defects on GQDs and the variation of their concentrations with the hydrothermal conditions. Interestingly, electrocatalytic activity of GQD/Pt composites exhibited a volcano-shaped variation with the GQD structural defects, with the best identified as the samples prepared at 160 °C for 6 h where the mass activity was found to meet the DOE target for 2015. This remarkable performance was accounted for by the deliberate manipulation of the adsorption of oxygen and reaction intermediates on platinum by the GQD structural defects through partial charge transfer. The strategy presented herein may offer a new paradigm in the design and engineering of nanoparticle catalysts for fuel cell electrochemistry. In addition, studies were also carried out to study intervalence charge transfer between ferrocenyl moieties bonded on carbon nanoparticle surfaces by diazonium reaction. Electrochemical studies exhibited two pairs of voltammetric waves with a difference of their formal potentials at about 78 mV, suggesting nanoparticle-mediated intraparticle charge delocalization at mixed valence as a result of the strong core-ligand covalent bonds and the conductive sp 2 carbon matrix of the graphitic cores. Consistent behaviors were observed in near-infrared measurements, indicating that the particles behaved analogously to a Class I/II mixed-valence compound.

Sediment and water chemistry of the San Juan River and Escalante River deltas of Lake Powell, Utah, 2010-2011

USGS Publications Warehouse

Hornewer, Nancy J.

2014-01-01

Recent studies have documented the presence of trace elements, organic compounds including polycyclic aromatic hydrocarbons, and radionuclides in sediment from the Colorado River delta and from sediment in some side canyons in Lake Powell, Utah and Arizona. The fate of many of these contaminants is of significant concern to the resource managers of the National Park Service Glen Canyon National Recreation Area because of potential health impacts to humans and aquatic and terrestrial species. In 2010, the U.S. Geological Survey began a sediment-core sampling and analysis program in the San Juan River and Escalante River deltas in Lake Powell, Utah, to help the National Park Service further document the presence or absence of contaminants in deltaic sediment. Three sediment cores were collected from the San Juan River delta in August 2010 and three sediment cores and an additional replicate core were collected from the Escalante River delta in September 2011. Sediment from the cores was subsampled and composited for analysis of major and trace elements. Fifty-five major and trace elements were analyzed in 116 subsamples and 7 composited samples for the San Juan River delta cores, and in 75 subsamples and 9 composited samples for the Escalante River delta cores. Six composited sediment samples from the San Juan River delta cores and eight from the Escalante River delta cores also were analyzed for 55 low-level organochlorine pesticides and polychlorinated biphenyls, 61 polycyclic aromatic hydrocarbon compounds, gross alpha and gross beta radionuclides, and sediment-particle size. Additionally, water samples were collected from the sediment-water interface overlying each of the three cores collected from the San Juan River and Escalante River deltas. Each water sample was analyzed for 57 major and trace elements. Most of the major and trace elements analyzed were detected at concentrations greater than reporting levels for the sediment-core subsamples and composited samples. Low-level organochlorine pesticides and polychlorinated biphenyls were not detected in any of the samples. Only one polycyclic aromatic hydrocarbon compound was detected at a concentration greater than the reporting level for one San Juan composited sample. Gross alpha and gross beta radionuclides were detected at concentrations greater than reporting levels for all samples. Most of the major and trace elements analyzed were detected at concentrations greater than reporting levels for water samples.