Elasto-plastic bending of cracked plates, including the effects of crack closure. Ph.D. Thesis

NASA Technical Reports Server (NTRS)

Jones, D. P.

1972-01-01

A capability for solving elasto-plastic plate bending problems is developed using assumptions consistent with Kirchhoff plate theory. Both bending and extensional modes of deformation are admitted with the two modes becoming coupled as yielding proceeds. Equilibrium solutions are obtained numerically by determination of the stationary point of a functional which is analogous to the potential strain energy. The stationary value of the functional for each load increment is efficiently obtained through use of the conjugate gradient. This technique is applied to the problem of a large centrally through cracked plate subject to remote circular bending. Comparison is drawn between two cases of the bending problem. The first neglects the possibility of crack face interference with bending, and the second includes a kinematic prohibition against the crack face from passing through the symmetry plane. Results are reported which isolate the effects of elastoplastic flow and crack closure.

77 FR 55773 - Airworthiness Directives; The Boeing Company Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2012-09-11

...) inspections for cracking of the left and right rib hinge bearing lugs of the aft face of the center section of... bearing lugs of the aft face of the center section of the horizontal stabilizer; measuring crack length...). Recognition That Reporting of Findings Is Not Required American Airlines stated it recognizes that reporting...

Cracked rocks with positive and negative Poisson's ratio: real-crack properties extracted from pressure dependence of elastic-wave velocities

NASA Astrophysics Data System (ADS)

Zaitsev, Vladimir Y.; Radostin, Andrey V.; Dyskin, Arcady V.; Pasternak, Elena

2017-04-01

We report results of analysis of literature data on P- and S-wave velocities of rocks subjected to variable hydrostatic pressure. Out of about 90 examined samples, in more than 40% of the samples the reconstructed Poisson's ratios are negative for lowest confining pressure with gradual transition to the conventional positive values at higher pressure. The portion of rocks exhibiting negative Poisson's ratio appeared to be unexpectedly high. To understand the mechanism of negative Poisson's ratio, pressure dependences of P- and S-wave velocities were analyzed using the effective medium model in which the reduction in the elastic moduli due to cracks is described in terms of compliances with respect to shear and normal loading that are imparted to the rock by the presence of cracks. This is in contrast to widely used descriptions of effective cracked medium based on a specific crack model (e.g., penny-shape crack) in which the ratio between normal and shear compliances of such a crack is strictly predetermined. The analysis of pressure-dependences of the elastic wave velocities makes it possible to reveal the ratio between pure normal and shear compliances (called q-ratio below) for real defects and quantify their integral content in the rock. The examination performed demonstrates that a significant portion (over 50%) of cracks exhibit q-ratio several times higher than that assumed for the conventional penny-shape cracks. This leads to faster reduction of the Poisson's ratio with increasing the crack concentration. Samples with negative Poisson's ratio are characterized by elevated q-ratio and simultaneously crack concentration. Our results clearly indicate that the traditional crack model is not adequate for a significant portion of rocks and that the interaction between the opposite crack faces leading to domination of the normal compliance and reduced shear displacement discontinuity can play an important role in the mechanical behavior of rocks.

Universal Shapes formed by Interacting Cracks

NASA Astrophysics Data System (ADS)

Fender, Melissa; Lechenault, Frederic; Daniels, Karen

2011-03-01

Brittle failure through multiple cracks occurs in a wide variety of contexts, from microscopic failures in dental enamel and cleaved silicon to geological faults and planetary ice crusts. In each of these situations, with complicated curvature and stress geometries, pairwise interactions between approaching cracks nonetheless produce characteristically curved fracture paths known in the geologic literature as en passant cracks. While the fragmentation of solids via many interacting cracks has seen wide investigation, less attention has been paid to the details of individual crack-crack interactions. We investigate the origins of this widely observed crack pattern using a rectangular elastic plate which is notched on each long side and then subjected to quasistatic uniaxial strain from the short side. The two cracks propagate along approximately straight paths until the pass each other, after which they curve and release a lenticular fragment. We find that, for materials with diverse mechanical properties, the shape of this fragment has an aspect ratio of 2:1, with the length scale set by the initial cracks offset s and the time scale set by the ratio of s to the pulling velocity. The cracks have a universal square root shape, which we understand by using a simple geometric model and the crack-crack interaction.

Mitigation of Crack Damage in Metallic Materials

NASA Technical Reports Server (NTRS)

Leser, Patrick E.; Newman, John A.; Smith, Stephen W.; Leser, William P.; Wincheski, Russell A.; Wallace, Terryl A.; Glaessgen, Edward H.; Piascik, Robert S.

2014-01-01

A system designed to mitigate or heal crack damage in metallic materials has been developed where the protected material or component is coated with a low-melting temperature film. After a crack is formed, the material is heated, melting the film which then infiltrates the crack opening through capillary action. Upon solidification, the healing material inhibits further crack damage in two ways. While the crack healing material is intact, it acts like an adhesive that bonds or bridges the crack faces together. After fatigue loading damages, the healing material in the crack mouth inhibits further crack growth by creating artificially-high crack closure levels. Mechanical test data show that this method sucessfully arrests or retards crack growth in laboratory specimens.

The stress intensity factors for a periodic array of interacting coplanar penny-shaped cracks

PubMed Central

Lekesiz, Huseyin; Katsube, Noriko; Rokhlin, Stanislav I.; Seghi, Robert R.

2013-01-01

The effect of crack interactions on stress intensity factors is examined for a periodic array of coplanar penny-shaped cracks. Kachanov’s approximate method for crack interactions (Int. J. Solid. Struct. 1987; 23(1):23–43) is employed to analyze both hexagonal and square crack configurations. In approximating crack interactions, the solution converges when the total truncation number of the cracks is 109. As expected, due to high density packing crack interaction in the hexagonal configuration is stronger than that in the square configuration. Based on the numerical results, convenient fitting equations for quick evaluation of the mode I stress intensity factors are obtained as a function of crack density and angle around the crack edge for both crack configurations. Numerical results for the mode II and III stress intensity factors are presented in the form of contour lines for the case of Poisson’s ratio ν =0.3. Possible errors for these problems due to Kachanov’s approximate method are estimated. Good agreement is observed with the limited number of results available in the literature and obtained by different methods. PMID:27175035

Impact initiation of explosives and propellants via statistical crack mechanics

NASA Astrophysics Data System (ADS)

Dienes, J. K.; Zuo, Q. H.; Kershner, J. D.

2006-06-01

A statistical approach has been developed for modeling the dynamic response of brittle materials by superimposing the effects of a myriad of microcracks, including opening, shear, growth and coalescence, taking as a starting point the well-established theory of penny-shaped cracks. This paper discusses the general approach, but in particular an application to the sensitivity of explosives and propellants, which often contain brittle constituents. We examine the hypothesis that the intense heating by frictional sliding between the faces of a closed crack during unstable growth can form a hot spot, causing localized melting, ignition, and fast burn of the reactive material adjacent to the crack. Opening and growth of a closed crack due to the pressure of burned gases inside the crack and interactions of adjacent cracks can lead to violent reaction, with detonation as a possible consequence. This approach was used to model a multiple-shock experiment by Mulford et al. [1993. Initiation of preshocked high explosives PBX-9404, PBX-9502, PBX-9501, monitored with in-material magnetic gauging. In: Proceedings of the 10th International Detonation Symposium, pp. 459-467] involving initiation and subsequent quenching of chemical reactions in a slab of PBX 9501 impacted by a two-material flyer plate. We examine the effects of crack orientation and temperature dependence of viscosity of the melt on the response. Numerical results confirm our theoretical finding [Zuo, Q.H., Dienes, J.K., 2005. On the stability of penny-shaped cracks with friction: the five types of brittle behavior. Int. J. Solids Struct. 42, 1309-1326] that crack orientation has a significant effect on brittle behavior, especially under compressive loading where interfacial friction plays an important role. With a reasonable choice of crack orientation and a temperature-dependent viscosity obtained from molecular dynamics calculations, the calculated particle velocities compare well with those measured using embedded velocity gauges.

How Do Cracks Initiate and Grow in a Thin Glass Plate? A Peridynamic Analysis

DTIC Science & Technology

2014-06-17

evolution of these cracks, and confirm these results with fractography experiments of post-mortem samples. The results provide evidence of the predictive...face Questions to be answered  Can we understand how and why each type of crack system forms?  Crack surface fractography can give indication of...Symmetrical cracks form on the lower-right quarter of the plate. Jared Wright (ARL) fractography results Conclusions • The simplest peridynamic model

49 CFR 215.123 - Defective couplers.

Code of Federal Regulations, 2010 CFR

2010-10-01

... automatically with the adjacent car; (b) The car has a coupler that has a crack in the highly stressed junction... knuckle that is broken or cracked on the inside pulling face of the knuckle. (d) The car has a knuckle pin...) Missing; (ii) Inoperative; (iii) Bent; (iv) Cracked; or (v) Broken. ...

49 CFR 215.123 - Defective couplers.

Code of Federal Regulations, 2011 CFR

2011-10-01

... automatically with the adjacent car; (b) The car has a coupler that has a crack in the highly stressed junction... knuckle that is broken or cracked on the inside pulling face of the knuckle. (d) The car has a knuckle pin...) Missing; (ii) Inoperative; (iii) Bent; (iv) Cracked; or (v) Broken. ...

Effective spring stiffness for a periodic array of interacting coplanar penny-shaped cracks at an interface between two dissimilar isotropic materials

PubMed Central

Lekesiz, Huseyin; Katsube, Noriko; Rokhlin, Stanislav I.; Seghi, Robert R.

2013-01-01

An effective spring stiffness approximation is proposed for a hexagonal array of coplanar penny shaped cracks located at the interface between two dissimilar solids. The approximation is based on the factorization of the solution on the material dissimilarity factor, the crack interaction factor and the effective spring stiffness solution for non-interacting cracks in a homogeneous material. Such factorization is exact and was validated for 2D collinear cracks between two dissimilar solids. The crack interaction factor is obtained using a recently developed model for stress intensity factors for an array of coplanar penny shaped cracks in a homogeneous material; also the material dissimilarity function recently obtained for non-interacting penny shaped crack at the interface between two dissimilar materials is employed. The obtained solution is useful for an assessment by ultrasonic measurements of the interface stiffness in bonded structures for monitoring the interfacial microdamage growth due to mechanical loading and environmental factors. PMID:27175036

Effective spring stiffness for a periodic array of interacting coplanar penny-shaped cracks at an interface between two dissimilar isotropic materials.

PubMed

Lekesiz, Huseyin; Katsube, Noriko; Rokhlin, Stanislav I; Seghi, Robert R

2013-08-15

An effective spring stiffness approximation is proposed for a hexagonal array of coplanar penny shaped cracks located at the interface between two dissimilar solids. The approximation is based on the factorization of the solution on the material dissimilarity factor, the crack interaction factor and the effective spring stiffness solution for non-interacting cracks in a homogeneous material. Such factorization is exact and was validated for 2D collinear cracks between two dissimilar solids. The crack interaction factor is obtained using a recently developed model for stress intensity factors for an array of coplanar penny shaped cracks in a homogeneous material; also the material dissimilarity function recently obtained for non-interacting penny shaped crack at the interface between two dissimilar materials is employed. The obtained solution is useful for an assessment by ultrasonic measurements of the interface stiffness in bonded structures for monitoring the interfacial microdamage growth due to mechanical loading and environmental factors.

77 FR 36127 - Airworthiness Directives; BAE SYSTEMS (Operations) Limited Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2012-06-18

... by reports of cracking found in the wing rear spar. This AD requires a one-time detailed inspection for cracks, corrosion, and other defects of the rear face of the wing rear spar, and repair if...] AD requires a one- time [detailed] inspection [for cracks, corrosion, and other defects] of the rear...

Diffraction-based study of fatigue crack initiation and propagation in aerospace aluminum alloys

NASA Astrophysics Data System (ADS)

Gupta, Vipul K.

The crack initiation sites and microstructure-sensitive growth of small fatigue cracks are experimentally characterized in two precipitation-hardened aluminum alloys, 7075-T651 and 7050-T7451, stressed in ambient temperature moist-air (warm-humid) and -50°C dry N2 (cold-dry) environmental conditions. Backscattered electron imaging (BSE) and energy dispersive spectroscopy (EDS) of the fracture surfaces showed that Fe-Cu rich constituent particle clusters are the most common initiation sites within both alloys stressed in either environment. The crack growth within each alloy, on average, was observed to be slowed in the cold-dry environment than in the warm-humid environment, but only at longer crack lengths. Although no overwhelming effects of grain boundaries and grain orientations on small-crack growth were observed, crack growth data showed local fluctuations within individual grains. These observations are understood as crack propagation through the underlying substructure at the crack surface and frequent interaction with low/high-angle grain and subgrain boundaries, during cyclic loading, and, are further attributed to periodic changes in crack propagation path and multiple occurrences of crack-branching observed in the current study. SEM-based stereology in combination with electron backscattered diffraction (EBSD) established fatigue crack surface crystallography within the region from ˜1 to 50 mum of crack initiating particle clusters. Fatigue crack facets were parallel to a wide variety of crystallographic planes, with pole orientations distributed broadly across the irreducible stereographic triangle between the {001} and {101}-poles within both warm-humid and cold-dry environments. The results indicate environmentally affected fatigue cracking in both cases, given the similarity between the observed morphology and crystallography with that of a variety of aerospace aluminum alloys cracked in the presence of moist-air. There was no evidence of crystallographic {111} slip-plane cracking typical of the Stage I crack growth mode observed in single crystals and high purity polycrystals of face centered cubic metals, and which has presently been assumed for the present materials within fatigue crack initiation models. Rather, the facets tend to have near-Mode I spatial orientation, which is another indicator of the importance of environmentally affected fatigue damage. The results provide a physical basis to develop microstructurally-based next generation multi-stage fatigue (MSF) models that should include a new crack decohesion criteria based upon environmental fatigue cracking mechanisms. EBSD study of small-cracks in alloy 7050-T7451, stressed in warm-humid environment, showed that crack-path orientation changes and crack-branching occurred at both low/high-angle grain and subgrain boundaries. Single surface trace analysis suggests that the crack-path differs substantially from crystallographic slip-planes. EBSD-based observations of small-crack propagation through subgrain structure, either formed by cyclic plastic strain accumulation or pre-existing (typical of unrecrystallized grain structure in the present materials), suggest that subgrain structure plays a crucial role in small fatigue crack propagation. As mentioned earlier, local fluctuations in small-crack growth rates appear to be caused by frequent interaction with subgrain boundaries, and multiple occurrences of crack-branching and crack-path orientation changes at low/high-angle grain and subgrain boundaries. The aforementioned deviation from low-index {001}/{101}-planes and the occurrence of high-index cracking planes observed by EBSD/Stereology, in this study and others, are interpreted as trans-subgranular decohesion or inter-subgranular cracking, due to trapped hydrogen. In summary, the results provide a firmer experimental foundation for, and clearer understanding of, the mechanisms of environmental fatigue cracking of aluminum alloys, especially the role of inter-subgranular cracking, which had previously been advanced based upon fracture surface observations alone.

Nanoscale origins of the damage tolerance of the high-entropy alloy CrMnFeCoNi

DOE PAGES

Zhang, ZiJiao; Mao, M. M.; Wang, Jiangwei; ...

2015-12-09

Damage tolerance can be an elusive characteristic of structural materials requiring both high strength and ductility, properties that are often mutually exclusive. High-entropy alloys are of interest in this regard. Specifically, the single-phase CrMnFeCoNi alloy displays tensile strength levels of ~1 GPa, excellent ductility (~60–70%) and exceptional fracture toughness (KJIc>200M Pa√m). Here through the use of in situ straining in an aberration-corrected transmission electron microscope, we report on the salient atomistic to micro-scale mechanisms underlying the origin of these properties. We identify a synergy of multiple deformation mechanisms, rarely achieved in metallic alloys, which generates high strength, work hardening andmore » ductility, including the easy motion of Shockley partials, their interactions to form stacking-fault parallelepipeds, and arrest at planar slip bands of undissociated dislocations. In conclusion, we further show that crack propagation is impeded by twinned, nanoscale bridges that form between the near-tip crack faces and delay fracture by shielding the crack tip.« less

Nanoscale origins of the damage tolerance of the high-entropy alloy CrMnFeCoNi

PubMed Central

Zhang, ZiJiao; Mao, M. M.; Wang, Jiangwei; Gludovatz, Bernd; Zhang, Ze; Mao, Scott X.; George, Easo P.; Yu, Qian; Ritchie, Robert O.

2015-01-01

Damage tolerance can be an elusive characteristic of structural materials requiring both high strength and ductility, properties that are often mutually exclusive. High-entropy alloys are of interest in this regard. Specifically, the single-phase CrMnFeCoNi alloy displays tensile strength levels of ∼1 GPa, excellent ductility (∼60–70%) and exceptional fracture toughness (KJIc>200 MPa√m). Here through the use of in situ straining in an aberration-corrected transmission electron microscope, we report on the salient atomistic to micro-scale mechanisms underlying the origin of these properties. We identify a synergy of multiple deformation mechanisms, rarely achieved in metallic alloys, which generates high strength, work hardening and ductility, including the easy motion of Shockley partials, their interactions to form stacking-fault parallelepipeds, and arrest at planar slip bands of undissociated dislocations. We further show that crack propagation is impeded by twinned, nanoscale bridges that form between the near-tip crack faces and delay fracture by shielding the crack tip. PMID:26647978

Simplified computational methods for elastic and elastic-plastic fracture problems

NASA Technical Reports Server (NTRS)

Atluri, Satya N.

1992-01-01

An overview is given of some of the recent (1984-1991) developments in computational/analytical methods in the mechanics of fractures. Topics covered include analytical solutions for elliptical or circular cracks embedded in isotropic or transversely isotropic solids, with crack faces being subjected to arbitrary tractions; finite element or boundary element alternating methods for two or three dimensional crack problems; a 'direct stiffness' method for stiffened panels with flexible fasteners and with multiple cracks; multiple site damage near a row of fastener holes; an analysis of cracks with bonded repair patches; methods for the generation of weight functions for two and three dimensional crack problems; and domain-integral methods for elastic-plastic or inelastic crack mechanics.

Space Shuttle Main Engine High Pressure Fuel Turbopump Turbine Blade Cracking

NASA Technical Reports Server (NTRS)

Lee, Henry

1988-01-01

The analytical results from two-dimensional (2D) and three-dimensional (3D) finite element model investigations into the cracking of Space Shuttle Main Engine (SSME) High Pressure Fuel Turbopump (HPFTP) first- and second-stage turbine blades are presented. Specifically, the initiation causes for transverse cracks on the pressure side of the firststage blade fir tree lobes and face/corner cracks on the downstream fir tree face of the second-state blade are evaluated. Because the blade material, MAR-M-246 Hf (DS), is highly susceptible to hydrogen embrittlement in the -100 F to 400 F thermal environment, a steady-state condition (full power level = 109 percent) rather than a start-up or shut-down transient was considered to be the most likely candidate for generating a high-strain state in the fir tree areas. Results of the analyses yielded strain levels on both first- and second-stage blade fir tree regions that are of a magnitude to cause hydrogen assisted low cycle fatigue cracking. Also evident from the analysis is that a positive margin against fir tree cracking exists for the planned design modifications, which include shot peening for both first- and second-stage blade fir tree areas.

Simulating Matrix Crack and Delamination Interaction in a Clamped Tapered Beam

NASA Technical Reports Server (NTRS)

De Carvalho, N. V.; Seshadri, B. R.; Ratcliffe, J. G.; Mabson, G. E.; Deobald, L. R.

2017-01-01

Blind predictions were conducted to validate a discrete crack methodology based on the Floating Node Method to simulate matrix-crack/delamination interaction. The main novel aspects of the approach are: (1) the implementation of the floating node method via an 'extended interface element' to represent delaminations, matrix-cracks and their interaction, (2) application of directional cohesive elements to infer overall delamination direction, and (3) use of delamination direction and stress state at the delamination front to determine migration onset. Overall, good agreement was obtained between simulations and experiments. However, the validation exercise revealed the strong dependence of the simulation of matrix-crack/delamination interaction on the strength data (in this case transverse interlaminar strength, YT) used within the cohesive zone approach applied in this work. This strength value, YT, is itself dependent on the test geometry from which the strength measurement is taken. Thus, choosing an appropriate strength value becomes an ad-hoc step. As a consequence, further work is needed to adequately characterize and assess the accuracy and adequacy of cohesive zone approaches to model small crack growth and crack onset. Additionally, often when simulating damage progression with cohesive zone elements, the strength is lowered while keeping the fracture toughness constant to enable the use of coarser meshes. Results from the present study suggest that this approach is not recommended for any problem involving crack initiation, small crack growth or multiple crack interaction.

Interaction of Lamb Waves with Fatigue Cracks in Aluminum

DTIC Science & Technology

2011-09-01

Interaction of Lamb Waves with Fatigue Cracks in Aluminum E. D. SWENSON, C. T. OWENS and C. ALLEN ABSTRACT Elastic waves can travel across...the interaction of Lamb waves with both open and closed low-cycle fatigue cracks in aluminum plates using a three-dimensional laser Doppler vibrometer...and antisymmetric Lamb wave modes differ upon encountering fatigue cracks. INTRODUCTION The use of guided elastic waves (Lamb waves) has shown

Numerical simulation of stress amplification induced by crack interaction in human femur bone

NASA Astrophysics Data System (ADS)

Alia, Noor; Daud, Ruslizam; Ramli, Mohammad Fadzli; Azman, Wan Zuki; Faizal, Ahmad; Aisyah, Siti

2015-05-01

This research is about numerical simulation using a computational method which study on stress amplification induced by crack interaction in human femur bone. Cracks in human femur bone usually occur because of large load or stress applied on it. Usually, the fracture takes longer time to heal itself. At present, the crack interaction is still not well understood due to bone complexity. Thus, brittle fracture behavior of bone may be underestimated and inaccurate. This study aims to investigate the geometrical effect of double co-planar edge cracks on stress intensity factor (K) in femur bone. This research focuses to analyze the amplification effect on the fracture behavior of double co-planar edge cracks, where numerical model is developed using computational method. The concept of fracture mechanics and finite element method (FEM) are used to solve the interacting cracks problems using linear elastic fracture mechanics (LEFM) theory. As a result, this study has shown the identification of the crack interaction limit (CIL) and crack unification limit (CUL) exist in the human femur bone model developed. In future research, several improvements will be made such as varying the load, applying thickness on the model and also use different theory or method in calculating the stress intensity factor (K).

Crack propagation and the material removal mechanism of glass-ceramics by the scratch test.

PubMed

Qiu, Zhongjun; Liu, Congcong; Wang, Haorong; Yang, Xue; Fang, Fengzhou; Tang, Junjie

2016-12-01

To eliminate the negative effects of surface flaws and subsurface damage of glass-ceramics on clinical effectiveness, crack propagation and the material removal mechanism of glass-ceramics were studied by single and double scratch experiments conducted using an ultra-precision machine. A self-manufactured pyramid shaped single-grit tool with a small tip radius was used as the scratch tool. The surface and subsurface crack propagations and interactions, surface morphology and material removal mechanism were investigated. The experimental results showed that the propagation of lateral cracks to the surface and the interaction between the lateral cracks and radial cracks are the two main types of material peeling, and the increase of the scratch depth increases the propagation angle of the radial cracks and the interaction between the cracks. In the case of a double scratch, the propagation of lateral cracks and radial cracks between paired scratches results in material peeling. The interaction between adjacent scratches depends on the scratch depth and separation distance. There is a critical separation distance where the normalized material removal volume reaches its peak. These findings can help reduce surface flaws and subsurface damage induced by the grinding process and improve the clinical effectiveness of glass-ceramics used as biological substitute and repair materials. Copyright © 2016 Elsevier Ltd. All rights reserved.

Creep, Fatigue and Environmental Interactions and Their Effect on Crack Growth in Superalloys

NASA Technical Reports Server (NTRS)

Telesman, J.; Gabb, T. P.; Ghosn, L. J.; Smith, T.

2017-01-01

Complex interactions of creep/fatigue/environment control dwell fatigue crack growth (DFCG) in superalloys. Crack tip stress relaxation during dwells significantly changes the crack driving force and influence DFCG. Linear Elastic Fracture Mechanics, Kmax, parameter unsuitable for correlating DFCG behavior due to extensive visco-plastic deformation. Magnitude of remaining crack tip axial stresses controls DFCG resistance due to the brittle-intergranular nature of the crack growth process. Proposed a new empirical parameter, Ksrf, which incorporates visco-plastic evolution of the magnitude of remaining crack tip stresses. Previous work performed at 704C, extend the work to 760C.

Interaction of a penny-shaped crack and an external circular crack in a transversely isotropic composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsai, Y.M.

1998-12-31

The interaction of a penny-shaped crack and an external circular crack in a transversely isotropic composite is investigated using the techniques of Hankel transform and multiplying factors. The boundary conditions of the problem have three different parts. The stress intensity factors at the inner and the outer crack tips are obtained in exact expressions as the products of a dimensional quantity and nondimensional functions. The presence of a penny-shaped crack is shown to have a strong effect on the magnitude of the stress intensity of the external circular crack. The crack surface displacement is also obtained and evaluated numerically formore » different values of the ratio of the inner crack radius to the external crack radius.« less

Interaction of part-through cracks in a flat plate

NASA Technical Reports Server (NTRS)

Aksel, B.; Erdogan, F.

1985-01-01

The accuracy of the line spring model is determined. The effect of interaction between two and three cracks is investigated, and extensive numerical results which may be useful in applications are provided. Line spring model with Reissner's plate theory is formulated to be used for any number and configurations of cracks provided that there is symmetry. This model is used to find stress intensity factors for elliptic internal cracks, elliptic edge cracks and two opposite elliptic edge cracks. Despite the simplicity of the line spring model, the results are found to be close.

Strip Yield Model Numerical Application to Different Geometries and Loading Conditions

NASA Technical Reports Server (NTRS)

Hatamleh, Omar; Forman, Royce; Shivakumar, Venkataraman; Lyons, Jed

2006-01-01

A new numerical method based on the strip-yield analysis approach was developed for calculating the Crack Tip Opening Displacement (CTOD). This approach can be applied for different crack configurations having infinite and finite geometries, and arbitrary applied loading conditions. The new technique adapts the boundary element / dislocation density method to obtain crack-face opening displacements at any point on a crack, and succeeds by obtaining requisite values as a series of definite integrals, the functional parts of each being evaluated exactly in a closed form.

Harmonic oscillations of a longitudinal shear infinite hollow cylinder arbitrary cross-section with a tunnel crack

NASA Astrophysics Data System (ADS)

Kyrylova, O. I.; Popov, V. G.

2018-04-01

An effective analytical-numerical method for determining the dynamic stresses in a hollow cylindrical body of arbitrary cross-section with a tunnel crack under antiplane strain conditions is proposed. The method allows separately solving the integral equations on the crack faces and satisfying the boundary conditions on the body boundaries. It provides a convenient numerical scheme. Approximate formulas for calculating the dynamic stress intensity factors in a neighborhood of the crack are obtained and the influence of the crack geometry and wave number on these quantities is investigated, especially from the point of view of the resonance existence.

Hot-crack test for aluminium alloys welds using TIG process

NASA Astrophysics Data System (ADS)

Niel, A.; Deschaux-Beaume, F.; Bordreuil, C.; Fras, G.

2010-06-01

Hot cracking is a critical defect frequently observed during welding of aluminium alloys. In order to better understand the interaction between cracking phenomenon, process parameters, mechanical factors and microstructures resulting from solidification after welding, an original hot-cracking test during welding is developed. According to in-situ observations and post mortem analyses, hot cracking mechanisms are investigated, taking into account the interaction between microstructural parameters, depending on the thermal cycles, and mechanical parameters, depending on geometry and clamping conditions of the samples and on the thermal field on the sample. Finally, a process map indicating the limit between cracking and non-cracking zones according to welding parameters is presented.

A cylindrical shell with a stress-free end which contains an axial part-through or through crack

NASA Technical Reports Server (NTRS)

Erdogan, F.; Yahsi, O. S.

1985-01-01

The interaction problem of a through or a part through crack with a stress free boundary in a semi-infinite cylindrical shell is considered. It is assumed that the crack lies in a meridional plane which is a plane of symmetry with respect to the external loads as well as the geometry. The circular boundary of the semi-infinite cylinder is assumed to be stress free. By using a transverse shear theory the problem is formulated in terms of a system of singular integral equations. The line spring model is used to treat the part through crack problem. In the case of a through crack the interaction between the perturbed stress fields due to the crack and the free boundary is quite strong and there is a considerable increase in the stress intensity factors caused by the interaction. On the other hand in the problem of a surface crack the interaction appears to be much weaker and consequently the magnification in the stress intensity factors is much less significant.

A cylindrical shell with a stress-free end which contains an axial part-through or through crack

NASA Technical Reports Server (NTRS)

Erdogan, F.; Yahsi, O. S.

1983-01-01

The interaction problem of a through or a part through crack with a stress free boundary in a semi-infinite cylindrical shell is considered. It is assumed that the crack lies in a meridional plane which is a plane of symmetry with respect to the external loads as well as the geometry. The circular boundary of the semi-infinite cylinder is assumed to be stress free. By using a transverse shear theory the problem is formulated in terms of a system of singular integral equations. The line spring model is used to treat the part through crack problem. In the case of a through crack the interaction between the perturbed stress fields due to the crack and the free boundary is quite strong and there is a considerable increase in the stress intensity factors caused by the interaction. On the other hand in the problem of a surface crack the interaction appears to be much weaker and consequently the magnification in the stress intensity factors is much less significant.

Real-time direct and diffraction X-ray imaging of irregular silicon wafer breakage.

PubMed

Rack, Alexander; Scheel, Mario; Danilewsky, Andreas N

2016-03-01

Fracture and breakage of single crystals, particularly of silicon wafers, are multi-scale problems: the crack tip starts propagating on an atomic scale with the breaking of chemical bonds, forms crack fronts through the crystal on the micrometre scale and ends macroscopically in catastrophic wafer shattering. Total wafer breakage is a severe problem for the semiconductor industry, not only during handling but also during temperature treatments, leading to million-dollar costs per annum in a device production line. Knowledge of the relevant dynamics governing perfect cleavage along the {111} or {110} faces, and of the deflection into higher indexed {hkl} faces of higher energy, is scarce due to the high velocity of the process. Imaging techniques are commonly limited to depicting only the state of a wafer before the crack and in the final state. This paper presents, for the first time, in situ high-speed crack propagation under thermal stress, imaged simultaneously in direct transmission and diffraction X-ray imaging. It shows how the propagating crack tip and the related strain field can be tracked in the phase-contrast and diffracted images, respectively. Movies with a time resolution of microseconds per frame reveal that the strain and crack tip do not propagate continuously or at a constant speed. Jumps in the crack tip position indicate pinning of the crack tip for about 1-2 ms followed by jumps faster than 2-6 m s(-1), leading to a macroscopically observed average velocity of 0.028-0.055 m s(-1). The presented results also give a proof of concept that the described X-ray technique is compatible with studying ultra-fast cracks up to the speed of sound.

Analysis of crack propagation in roller bearings using the boundary integral equation method - A mixed-mode loading problem

NASA Technical Reports Server (NTRS)

Ghosn, L. J.

1988-01-01

Crack propagation in a rotating inner raceway of a high-speed roller bearing is analyzed using the boundary integral method. The model consists of an edge plate under plane strain condition upon which varying Hertzian stress fields are superimposed. A multidomain boundary integral equation using quadratic elements was written to determine the stress intensity factors KI and KII at the crack tip for various roller positions. The multidomain formulation allows the two faces of the crack to be modeled in two different subregions, making it possible to analyze crack closure when the roller is positioned on or close to the crack line. KI and KII stress intensity factors along any direction were computed. These calculations permit determination of crack growth direction along which the average KI times the alternating KI is maximum.

Theoretical Studies in Nondestructive Evaluation (NDE)

DTIC Science & Technology

1985-04-01

estimated radii of various flaws in a titanium alloy (Ti-6Al-4V) and in a ceramic material ( Si3 N4). The first column defines the flaw, the second coli...quantities, i.e., they wT &wirm ’.^M-.-rwr.- rrv" *r~Tirv* W^TT-J trnr t VR^ U» ■ ^■rs^Br^.TTP:rw? iwru" n^; are the strength of the inhomogeneities...with interacting crack faces.may be a poor reflector, and thus difficult 6 IM^ ni :’¥T MI’TWTM "mi%t^ir\\<i!.TR.^ci:i to detect and characterize. In

Roof Weakening of Hydraulic Fracturing for Control of Hanging Roof in the Face End of High Gassy Coal Longwall Mining: A Case Study

NASA Astrophysics Data System (ADS)

Huang, Bingxiang; Wang, Youzhuang

2016-09-01

The occurence of hanging roof commonly arises in the face end of longwall coal mining under hard roof conditions. The sudden break and subsequent caving of a hanging roof could result in the extrusion of gas in the gob to the face, causing gas concentrations to rise sharply and to increase to over a safety-limited value. A series of linear fracturing-holes of 32 mm diameter were drilled into the roof of the entries with an anchor rig. According to the theory that the gob should be fully filled with the fragmentized falling roof rock, the drilling depth is determined as being 3 5 times the mining height if the broken expansion coefficient takes an empirical value. Considering the general extension range of cracks and the supporting form of the entryway, the spacing distance between two drilling holes is determined as being 1 2 times the crack's range of extension. Using a mounting pipe, a high pressure resistant sealing device of a small diameter-size was sent to the designated location for the high-pressure hydraulic fracturing of the roof rock. The hydraulic fracturing created the main hydro-fracturing crack and airfoil branch cracks in the interior of the roof-rock, transforming the roof structure and weakening the strength of the roof to form a weak plane which accelerated roof caving, and eventually induced the full caving in of the roof in time with the help of ground pressure. For holes deeper than 4 m, retreating hydraulic fracturing could ensure the uniformity of crack extension. Tested and applied at several mines in Shengdong Mining District, the highest ruptured water pressure was found to be 55 MPa, and the hanging roof at the face end was reduced in length from 12 m to less than 1 2 m. This technology has eliminated the risk of the extrusion of gas which has accumulated in the gob.

A probabilistic method for determining the volume fraction of pre-embedded capsules in self-healing materials

NASA Astrophysics Data System (ADS)

Lv, Zhong; Chen, Huisu

2014-10-01

Autonomous healing of cracks using pre-embedded capsules containing healing agent is becoming a promising approach to restore the strength of damaged structures. In addition to the material properties, the size and volume fraction of capsules influence crack healing in the matrix. Understanding the crack and capsule interaction is critical in the development and design of structures made of self-healing materials. Assuming that the pre-embedded capsules are randomly dispersed we theoretically model flat ellipsoidal crack interaction with capsules and determine the probability of a crack intersecting the pre-embedded capsules i.e. the self-healing probability. We also develop a probabilistic model of a crack simultaneously meeting with capsules and catalyst carriers in two-component self-healing system matrix. Using a risk-based healing approach, we determine the volume fraction and size of the pre-embedded capsules that are required to achieve a certain self-healing probability. To understand the effect of the shape of the capsules on self-healing we theoretically modeled crack interaction with spherical and cylindrical capsules. We compared the results of our theoretical model with Monte-Carlo simulations of crack interaction with capsules. The formulae presented in this paper will provide guidelines for engineers working with self-healing structures in material selection and sustenance.

Crack Detection Using Combinations of Acoustic Emission and Guided Wave Signals from Bonded Piezoelectric Transducers

DTIC Science & Technology

2011-09-01

and bond integrity. Lastly, the PZT transducers are also utilized to track the lower frequency mechanical strains created during fatigue loading...face of the coupon and on either side of the gage section. Each coupon undergoes cyclic tensile loading to initiate and grow fatigue cracks. At...various intervals, the fatigue cycling is paused and the coupon is visually inspected for crack initiation and growth. While the cycling is paused

77 FR 13228 - Airworthiness Directives; BAE SYSTEMS (Operations) Limited Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2012-03-06

... wing rear spar. This proposed AD would require a one-time detailed inspection for cracks, corrosion, and other defects of the rear face of the wing rear spar, and repair if necessary. We are proposing... above, this [EASA] AD requires a one- time [detailed] inspection [for cracks, corrosion, and other...

Effects of weld residual stresses on crack-opening area analysis of pipes for LBB applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dong, P.; Rahman, S.; Wilkowski, G.

1997-04-01

This paper summarizes four different studies undertaken to evaluate the effects of weld residual stresses on the crack-opening behavior of a circumferential through-wall crack in the center of a girth weld. The effect of weld residual stress on the crack-opening-area and leak-rate analyses of a pipe is not well understood. There are no simple analyses to account for these effects, and, therefore, they are frequently neglected. The four studies involved the following efforts: (1) Full-field thermoplastic finite element residual stress analyses of a crack in the center of a girth weld, (2) A comparison of the crack-opening displacements from amore » full-field thermoplastic residual stress analysis with a crack-face pressure elastic stress analysis to determine the residual stress effects on the crack-opening displacement, (3) The effects of hydrostatic testing on the residual stresses and the resulting crack-opening displacement, and (4) The effect of residual stresses on crack-opening displacement with different normal operating stresses.« less

Mechanical Aspects of Interfaces and Surfaces in Ceramic Containing Systems.

DTIC Science & Technology

1984-12-14

of a computer model to simulate the crack damage. The model is based on the fracture mechanics of cracks engulfed by the short stress pulse generated...by drop impact. Inertial effects of the crack faces are a particularly important aspect of the model. The computer scheme thereby allows the stress...W. R. Beaumont, "On the Toughness of Particulate Filled Polymers." Water Drop Impact X. E. D. Case and A. G. Evans, "A Computer -Generated Simulation

Effect of initial contact surface condition on the friction and wear properties of bearing steel in cyclic reciprocating sliding contact

NASA Astrophysics Data System (ADS)

Tanaka, Y.; Endo, M.; Moriyama, S.

2017-05-01

Delamination failure is one of the most important engineering problems. This failure can frequently be detrimental to rolling contact machine elements such as bearings, gear wheels, etc. This phenomenon, called rolling contact fatigue, has a close relationship not only with opening-mode but also with shear-mode fatigue crack growth. The crack face interference is known to significantly affect the shear-mode fatigue crack propagation and its threshold behavior. Quantitative investigation on friction and wear at fatigue crack faces in the material is essentially impossible. Previously, thus, a novel ring-on-ring test by making use of fatigue testing machine was proposed to simulate a cyclic reciprocating sliding contact of crack surfaces. However, this test procedure had some problems. For instance, in order to achieve the uniform contact at the start of test, the rubbing of specimens must be conducted in advance. By this treatment, the specimen surfaces were already damaged before the test. In this study, an improvement of experimental method was made to perform the test using the damage-free specimens. The friction and wear properties for heat-treated high carbon-chromium bearing steel were investigated with this new method and the results were compared to the results obtained by using the initially damaged specimens.

An equivalent domain integral method for three-dimensional mixed-mode fracture problems

NASA Technical Reports Server (NTRS)

Shivakumar, K. N.; Raju, I. S.

1991-01-01

A general formulation of the equivalent domain integral (EDI) method for mixed mode fracture problems in cracked solids is presented. The method is discussed in the context of a 3-D finite element analysis. The J integral consists of two parts: the volume integral of the crack front potential over a torus enclosing the crack front and the crack surface integral due to the crack front potential plus the crack face loading. In mixed mode crack problems the total J integral is split into J sub I, J sub II, and J sub III representing the severity of the crack front in three modes of deformations. The direct and decomposition methods are used to separate the modes. These two methods were applied to several mixed mode fracture problems, were analyzed, and results were found to agree well with those available in the literature. The method lends itself to be used as a post-processing subroutine in a general purpose finite element program.

An equivalent domain integral method for three-dimensional mixed-mode fracture problems

NASA Technical Reports Server (NTRS)

Shivakumar, K. N.; Raju, I. S.

1992-01-01

A general formulation of the equivalent domain integral (EDI) method for mixed mode fracture problems in cracked solids is presented. The method is discussed in the context of a 3-D finite element analysis. The J integral consists of two parts: the volume integral of the crack front potential over a torus enclosing the crack front and the crack surface integral due to the crack front potential plus the crack face loading. In mixed mode crack problems the total J integral is split into J sub I, J sub II, and J sub III representing the severity of the crack front in three modes of deformations. The direct and decomposition methods are used to separate the modes. These two methods were applied to several mixed mode fracture problems, were analyzed, and results were found to agree well with those available in the literature. The method lends itself to be used as a post-processing subroutine in a general purpose finite element program.

Effects of Crack on Heat Flux in Hypersonic Shock/Boundary-Layer Interaction

NASA Astrophysics Data System (ADS)

Ozawa, Hiroshi; Hanai, Katsuhisa; Kitamura, Keiichi; Mori, Koichi; Nakamura, Yoshiaki

A small crack on body surface led to a tragic accident in 2003, which is the Columbia accident. During the shuttle's re-entry, high temperature gas penetrated crack on leading-edge of the left wing and melted the aluminum structure, finally the Columbia blew up. Since early times, there are many fundamental studies about simple cavity-flow formed on body surface in hypersonic speeds. However, an investigation of Shock/Boundary-Layer Interaction (SBLI) on crack has not been researched. For multistage space transportation vehicle such as TSTO, SBLI is an inevitable problem, and then SBLI on crack becomes a critical issue for TSTO development. In this study, the effects of crack, where SBLI occurs, were investigated for TSTO hypersonic speed (M∞ = 8.1). A square crack locates at SBLI point on the TSTO booster. Results show that a crack and its depth strongly effect on peak heat flux and aerodynamic interaction flow-field. In the cases of shallow crack (d/C ≤ 0.10), there exist two high heat flux regions on crack floor, which locates at a flow reattachment region and a back end wall of crack. In this case, a peak heat flux at flow reattachment region becomes about 2 times as large as the stagnation point heat flux, which value becomes larger compared with a peak heat flux in the case of No-Crack TSTO. While in the case of deep crack (d/C = 0.20), overall heat flux on crack floor decreases to below the stagnation point heat flux. These results provide useful data for a development of TSTO thermal protection system (TPS) such as thermal protection tile.

Stress interactions among arrays of tensile cracks in 3D: Implications for the nucleation of shear failure and the orientations of faults.

NASA Astrophysics Data System (ADS)

Healy, D.; Davis, T.

2017-12-01

In low porosity rocks it is widely believed that planes of shear failure nucleate through the interaction of arrays of smaller tensile microcracks. This model has been confirmed through laboratory rock deformation experiments and detailed microstructural analyses. In this contribution we use the Boundary Element Method (BEM) to model the interactions of arrays of tensile cracks, discretised as ellipsoidal voids in three dimensions (3D). We calculate the elastic stresses in the solid matrix surrounding the cracks resulting from an applied load and include the interaction effects of each crack upon all the others. We explore the role of variations in crack shape, size, position and orientation upon the total and locally perturbed stress fields. We calculate the average crack normal stress (CNS) acting over the area of each tensile crack, and then find the locus of the maximum value of this stress throughout the modelled volume. Following Reches & Lockner (1994) and Healy et al. (2006a, 2006b), we assert that planes of shear failure will most likely nucleate on surfaces parallel to the locus of maximum average CNS. These shear planes are oblique to all three principal stresses in the far field.

Interaction of wave with a body submerged below an ice sheet with multiple arbitrarily spaced cracks

NASA Astrophysics Data System (ADS)

Li, Z. F.; Wu, G. X.; Ji, C. Y.

2018-05-01

The problem of wave interaction with a body submerged below an ice sheet with multiple arbitrarily spaced cracks is considered, based on the linearized velocity potential theory together with the boundary element method. The ice sheet is modeled as a thin elastic plate with uniform properties, and zero bending moment and shear force conditions are enforced at the cracks. The Green function satisfying all the boundary conditions including those at cracks, apart from that on the body surface, is derived and is expressed in an explicit integral form. The boundary integral equation for the velocity potential is constructed with an unknown source distribution over the body surface only. The wave/crack interaction problem without the body is first solved directly without the need for source. The convergence and comparison studies are undertaken to show the accuracy and reliability of the solution procedure. Detailed numerical results through the hydrodynamic coefficients and wave exciting forces are provided for a body submerged below double cracks and an array of cracks. Some unique features are observed, and their mechanisms are analyzed.

Implementation of equivalent domain integral method in the two-dimensional analysis of mixed mode problems

NASA Technical Reports Server (NTRS)

Raju, I. S.; Shivakumar, K. N.

1989-01-01

An equivalent domain integral (EDI) method for calculating J-intergrals for two-dimensional cracked elastic bodies is presented. The details of the method and its implementation are presented for isoparametric elements. The total and product integrals consist of the sum of an area of domain integral and line integrals on the crack faces. The line integrals vanish only when the crack faces are traction free and the loading is either pure mode 1 or pure mode 2 or a combination of both with only the square-root singular term in the stress field. The EDI method gave accurate values of the J-integrals for two mode I and two mixed mode problems. Numerical studies showed that domains consisting of one layer of elements are sufficient to obtain accurate J-integral values. Two procedures for separating the individual modes from the domain integrals are presented. The procedure that uses the symmetric and antisymmetric components of the stress and displacement fields to calculate the individual modes gave accurate values of the integrals for all problems analyzed. The EDI method when applied to a problem of an interface crack in two different materials showed that the mode 1 and mode 2 components are domain dependent while the total integral is not. This behavior is caused by the presence of the oscillatory part of the singularity in bimaterial crack problems. The EDI method, thus, shows behavior similar to the virtual crack closure method for bimaterial problems.

Self-healing of cracks formed in Silicon-Aluminum anodes electrochemically cycled at high lithiation rates

NASA Astrophysics Data System (ADS)

Bhattacharya, Sandeep; Alpas, Ahmet T.

2016-10-01

Lithiation-induced volume changes in Si result in fracture and fragmentation of Si anodes in Li-ion batteries. This paper reports the self-healing behaviour of cracks observed in micron-sized Si particles dispersed in a ductile Al matrix of a Si-Al electrode electrochemically cycled vs. Li/Li+ using a high lithiation rate of 15.6 C. Cross-sectional high-resolution transmission electron microscopy and Raman spectroscopy revealed that an amorphous layer with a depth up to ∼100 nm was formed at the surface of Si particles. In-situ optical microscopy performed during electrochemical experiments revealed development of cracks in Si particles as the voltage decreased to 0.02 V during lithiation. Self-healing of cracks in Si particles occurred in two steps: i) arresting of the crack growth at the Si/Al interface as the surrounding Al matrix had a higher fracture toughness and thus acted as a barrier to crack propagation, and ii) closure of cracks due to compressive stresses applied to the crack faces by the amorphous zones formed on each side of the crack paths.

The crack-inclusion interaction problem

NASA Technical Reports Server (NTRS)

Liu, X.-H.; Erdogan, F.

1986-01-01

The general plane elastostatic problem of interaction between a crack and an inclusion is considered. The Green's functions for a pair of dislocations and a pair of concentrated body forces are used to generate the crack and the inclusion. Integral equations are obtained for a line crack and an elastic line inclusion having an arbitrary relative orientation and size. The nature of stress singularity around the end points of rigid and elastic inclusions is described and three special cases of this intersection problem are studied. The problem is solved for an arbitrary uniform stress state away from the crack-inclusion region. The nonintersecting crack-inclusion problem is considered for various relative size, orientation, and stiffness parameters, and the stress intensity factors at the ends of the inclusion and the crack are calculated. For the crack-inclusion intersection case, special stress intensity factors are defined and are calculated for various values of the parameters defining the relative size and orientation of the crack and the inclusion and the stiffness of the inclusion.

The crack-inclusion interaction problem

NASA Technical Reports Server (NTRS)

Xue-Hui, L.; Erdogan, F.

1984-01-01

The general plane elastostatic problem of interaction between a crack and an inclusion is considered. The Green's functions for a pair of dislocations and a pair of concentrated body forces are used to generate the crack and the inclusion. Integral equations are obtained for a line crack and an elastic line inclusion having an arbitrary relative orientation and size. The nature of stress singularity around the end points of rigid and elastic inclusions is described and three special cases of this intersection problem are studied. The problem is solved for an arbitrary uniform stress state away from the crack-inclusion region. The nonintersecting crack-inclusion problem is considered for various relative size, orientation, and stiffness parameters, and the stress intensity factors at the ends of the inclusion and the crack are calculated. For the crack-inclusion intersection case, special stress intensity factors are defined and are calculated for various values of the parameters defining the relative size and orientation of the crack and the inclusion and the stiffness of the inclusion.

The bending strength of tablets with a breaking line--Comparison of the results of an elastic and a "brittle cracking" finite element model with experimental findings.

PubMed

Podczeck, Fridrun; Newton, J Michael; Fromme, Paul

2015-11-10

The aim of this work was to ascertain the influence of the position of the breaking line of bevel-edged tablets in a three-point bending test. Two different brands of commercially available, flat-round, bevel-edged tablets with a single central breaking line were studied. Breaking line positions tested, relative to the upper loading roll, were 0°, 22.5°, 45°, 67.5° and 90°. The breaking line faced either up- or downwards during the test. The practical results were compared with FEM results simulating similar test configurations. Tablets failed mainly across the failure plane, resulting in two tablet halves. An exception to this was found for tablets where the breaking line faced down and was positioned at an angle of 22.5° relative to the loading plane. Here the crack followed the breaking line in the centre of the tablets and only diverged towards the loading plane position at the edges of the tablets. The breaking line facing upwards resulted in a significantly higher tensile strength of the tablets compared to it facing downwards. However, with one exception, the orientation of the breaking line relative to the loading plane appeared not to affect the tensile strength values. A fully elastic FEM model indicated that both the position of the breaking line relative to the loading plane and as to whether the breaking line faced up- or downwards during the bending test would result in considerably different failure loads during practical experiments. The results also suggested that regardless of the breaking line position, when it is facing down crack propagation should start at the outer edges propagating towards the midpoint of the discs until failure occurs. Failure should hence always result in equal tablet halves, whereby the failure plane should coincide with the loading plane. Neither predictions fully reflected the practical behaviour of the tablets. Using a brittle cracking FEM model significantly larger tensile stresses for tablets with the breaking line positioned downwards at 0° or 22.5° relative to the loading plane were still predicted, but the differences between model and experimental values was greatly reduced. The remaining differences are more likely due to the inadequacy of the equation available to calculate the experimental tensile strength values. This equation cannot account for the presence of a breaking line and overestimates the thickness of the loading plane by the depth of the breaking line when in 0° or 22.5° position. If the depth of the breaking line is taken into account, the model predictions and the experimental findings are comparable. Also, in the brittle cracking FEM simulations the predicted crack propagation patterns were similar to those found in the experiments, and the model stress distributions across the lower surfaces were much more homogeneous and streamlined parallel to the loading plane. The brittle cracking model hence reflected the practicalities of the bending test more closely. The findings suggested that with the breaking line facing down fracture should always start in the centre of a tablet at its lower surface, initiated by the breaking line. Due to simultaneous development of larger stresses along the y-axis the tablet should still break into two equal halves along the loading plane, unless the position of the breaking line relative to the loading plane was 22.5°. In this case the tablet would fail by a mixed process, whereby failure would occur mainly along the breaking line, but due to simultaneous crack formation at the lower surface close to the bevel edge parallel to the loading plane the final breaking pattern would deviate from the breaking line about half-way from its centre, as seen in the practical experiments. Copyright © 2015 Elsevier B.V. All rights reserved.

Laplace-SGBEM analysis of the dynamic stress intensity factors and the dynamic T-stress for the interaction between a crack and auxetic inclusions

NASA Astrophysics Data System (ADS)

Kwon, Kibum

A dynamic analysis of the interaction between a crack and an auxetic (negative Poisson ratio)/non-auxetic inclusion is presented. The two most important fracture parameters, namely the stress intensity factors and the T-stress are analyzed by using the symmetric Galerkin boundary element method in the Laplace domain for three different models of crack-inclusion interaction. To investigate the effects of auxetic inclusions on the fracture behavior of composites reinforced by this new type of material, comparisons of the dynamic stress intensity factors and the dynamic T-stress are made between the use of auxetic inclusions as opposed to the use of traditional inclusions. Furthermore, the technique presented in this research can be employed to analyze for the interaction between a crack and a cluster of auxetic/non-auxetic inclusions. Results from the latter models can be employed in crack growth analysis in auxetic-fiber-reinforced composites.

Combustion: Structural interaction in a viscoelastic material

NASA Technical Reports Server (NTRS)

Chang, T. Y.; Chang, J. P.; Kumar, M.; Kuo, K. K.

1980-01-01

The effect of interaction between combustion processes and structural deformation of solid propellant was considered. The combustion analysis was performed on the basis of deformed crack geometry, which was determined from the structural analysis. On the other hand, input data for the structural analysis, such as pressure distribution along the crack boundary and ablation velocity of the crack, were determined from the combustion analysis. The interaction analysis was conducted by combining two computer codes, a combustion analysis code and a general purpose finite element structural analysis code.

Fracture mechanics by three-dimensional crack-tip synchrotron X-ray microscopy

PubMed Central

Withers, P. J.

2015-01-01

To better understand the relationship between the nucleation and growth of defects and the local stresses and phase changes that cause them, we need both imaging and stress mapping. Here, we explore how this can be achieved by bringing together synchrotron X-ray diffraction and tomographic imaging. Conventionally, these are undertaken on separate synchrotron beamlines; however, instruments capable of both imaging and diffraction are beginning to emerge, such as ID15 at the European Synchrotron Radiation Facility and JEEP at the Diamond Light Source. This review explores the concept of three-dimensional crack-tip X-ray microscopy, bringing them together to probe the crack-tip behaviour under realistic environmental and loading conditions and to extract quantitative fracture mechanics information about the local crack-tip environment. X-ray diffraction provides information about the crack-tip stress field, phase transformations, plastic zone and crack-face tractions and forces. Time-lapse CT, besides providing information about the three-dimensional nature of the crack and its local growth rate, can also provide information as to the activation of extrinsic toughening mechanisms such as crack deflection, crack-tip zone shielding, crack bridging and crack closure. It is shown how crack-tip microscopy allows a quantitative measure of the crack-tip driving force via the stress intensity factor or the crack-tip opening displacement. Finally, further opportunities for synchrotron X-ray microscopy are explored. PMID:25624521

Unusual properties of high-compliance porosity extracted from measurements of pressure-dependent wave velocities in rocks

NASA Astrophysics Data System (ADS)

Zaitsev, Vladimir Y.; Radostin, Andrey V.; Pasternak, Elena; Dyskin, Arcady

2016-04-01

Conventionally the interpretation of wave velocities and their variations under load is conducted assuming that closable cracks have simple planar shapes, like the popular model of penny-shape cracks. For such cracks, the proportion between complementary variations in different elastic parameters of rocks (such as S- and P-wave velocities) is strictly pre-determined, in particular, it is independent of the crack aspect ratio and rather weakly dependent on the Poisson's ratio of the intact rock. Real rocks, however, contain multitude of cracks of different geometry. Faces of such cracks can exhibit complex modes of interaction when closed by external load, which may result in very different ratios between normal- and shear compliances of such defects. In order to describe the reduction of different elastic moduli, we propose a model in which the compliances of crack-like defects are explicitly decoupled and are not predetermined, so that the ratio q between total normal- and shear- compliances imparted to the rock mass (as well as individual values of these compliances) can be estimated from experimental data on reduction of different elastic moduli (e.g., pressure dependences of P- and S-wave velocities). Physically, the so-extracted ratio q can be interpreted as intrinsic property of individual crack-like defects similar to each other, or as a characteristic of proportion between concentrations of pure normal cracks with very large q and pure shear cracks with q→0. The latter case can correspond, e.g., to saturated cracks in which weakly-compressible liquid prevents crack closing under normal loading. It can be shown that for conventional dry planar cracks, the compliance ratio is q ˜2. The developed model applied to the data on wave-velocity variations with external pressure indicates that elastic properties of the real crack-like defects in rocks can differ considerably from the usually assumed ones. Comparison with experimental data on variations P- and S-wave velocities with hydrostatic compression of different dry and saturated rocks (sandstones, Westerly granite and Webatuck dolomite, etc.) shows that our model is accurate in a wide range of pressures with constant (i.e., pressure-independent) values of parameter q. Furthermore, the determined values of the latter are considerably different from those of conventional cracks. In particular, although all saturated samples have values q <1, the simplified approximation q=0 (i.e., the absence of normal compressibility that is often assumed for wet cracks) leads to large errors in the prediction of complementary variations in the shear- and bulk elastic moduli. Among dry sandstones, the majority have q >2 and many sandstones exhibit unusually high q»1 suggesting quite rough and tortoise nature of real cracks in those rocks. We demonstrate that in such cases, the use of the conventional assumption q ˜2 typical of penny-shape cracks leads to striking inconsistency between the predicted and experimentally observed crack-induced complementary variations in different elastic moduli. Furthermore, among samples with q»1, we revealed numerous examples that demonstrate negative Poisson's ratio at low pressures. VYZ and AVR acknowledge the financial support by RFBR grant No 15-05-05143.

Theoretical investigation of crack formation in tungsten after heat loads

NASA Astrophysics Data System (ADS)

Arakcheev, A. S.; Huber, A.; Wirtz, M.; Sergienko, G.; Steudel, I.; Burdakov, A. V.; Coenen, J. W.; Kreter, A.; Linke, J.; Mertens, Ph.; Shoshin, A. A.; Unterberg, B.; Vasilyev, A. A.

2015-08-01

Transient events such as ELMs in large plasma devices lead to significant heat load on plasma-facing components (PFCs). ELMs cause mechanical damage of PFCs (e.g. cracks). The cracks appear due to stresses caused by thermal extension. Analytical calculations of the stresses are carried out for tungsten. The model only takes into account the basic features of solid body mechanics without material modifications (e.g. fatigue or recrystallization). The numerical results of the model demonstrate good agreement with experimental data obtained at the JUDITH-1, PSI-2 and GOL-3 facilities.

A shape memory polymer concrete crack closure system activated by electrical current

NASA Astrophysics Data System (ADS)

Teall, Oliver; Pilegis, Martins; Davies, Robert; Sweeney, John; Jefferson, Tony; Lark, Robert; Gardner, Diane

2018-07-01

The presence of cracks has a negative impact on the durability of concrete by providing paths for corrosive materials to the embedded steel reinforcement. Cracks in concrete can be closed using shape memory polymers (SMP) which produce a compressive stress across the crack faces. This stress has been previously found to enhance the load recovery associated with autogenous self-healing. This paper details the experiments undertaken to incorporate SMP tendons containing polyethylene terephthalate (PET) filaments into reinforced and unreinforced 500 × 100 × 100 mm structural concrete beam samples. These tendons are activated via an electrical supply using a nickel-chrome resistance wire heating system. The set-up, methodology and results of restrained shrinkage stress and crack closure experiments are explained. Crack closure of up to 85% in unreinforced beams and 26%–39% in reinforced beams is measured using crack-mouth opening displacement, microscope and digital image correlation equipment. Conclusions are made as to the effectiveness of the system and its potential for application within industry.

Influence of load interactions on crack growth as related to state of stress and crack closure

NASA Technical Reports Server (NTRS)

Telesman, J.

1985-01-01

Fatigue crack propagation (FCP) after an application of a low-high loading sequence was investigated as a function of specimen thickness and crack closure. No load interaction effects were detected for specimens in a predominant plane strain state. However, for the plane stress specimens, initially high FCP rates after transition to a higher stress intensity range were observed. The difference in observed behavior was explained by examining the effect of the resulting closure stress intensity values on the effective stress intensity range.

Floating Node Method and Virtual Crack Closure Technique for Modeling Matrix Cracking-Delamination Interaction

NASA Technical Reports Server (NTRS)

DeCarvalho, N. V.; Chen, B. Y.; Pinho, S. T.; Baiz, P. M.; Ratcliffe, J. G.; Tay, T. E.

2013-01-01

A novel approach is proposed for high-fidelity modeling of progressive damage and failure in composite materials that combines the Floating Node Method (FNM) and the Virtual Crack Closure Technique (VCCT) to represent multiple interacting failure mechanisms in a mesh-independent fashion. In this study, the approach is applied to the modeling of delamination migration in cross-ply tape laminates. Delamination, matrix cracking, and migration are all modeled using fracture mechanics based failure and migration criteria. The methodology proposed shows very good qualitative and quantitative agreement with experiments.

Path (un)predictability of two interacting cracks in polycarbonate sheets using Digital Image Correlation.

PubMed

Koivisto, J; Dalbe, M-J; Alava, M J; Santucci, S

2016-08-31

Crack propagation is tracked here with Digital Image Correlation analysis in the test case of two cracks propagating in opposite directions in polycarbonate, a material with high ductility and a large Fracture Process Zone (FPZ). Depending on the initial distances between the two crack tips, one may observe different complex crack paths with in particular a regime where the two cracks repel each other prior to being attracted. We show by strain field analysis how this can be understood according to the principle of local symmetry: the propagation is to the direction where the local shear - mode KII in fracture mechanics language - is zero. Thus the interactions exhibited by the cracks arise from symmetry, from the initial geometry, and from the material properties which induce the FPZ. This complexity makes any long-range prediction of the path(s) impossible.

Plastic zone size and crack tip opening displacement of a Dugdale crack interacting with a coated circular inclusion

NASA Astrophysics Data System (ADS)

Hoh, H. J.; Xiao, Z. M.; Luo, J.

2010-09-01

An analytical investigation on the plastic zone size of a crack near a coated circular inclusion under three different loading conditions of uniaxial tension, uniform tension and pure shear was carried out. Both the crack and coated circular inclusion are embedded in an infinite matrix, with the crack oriented along the radial direction of the inclusion. In the solution procedure, the crack is simulated as a continuous distribution of edge dislocations. With the Dugdale model of small-scale yielding [J. Mech. Phys. Solids 8 (1960) p. 100], two thin strips of yielded plastic zones are introduced at both crack tips. Using the solution for a coated circular inclusion interacting with a single dislocation as the Green's function, the physical problem is formulated into a set of singular integral equations. Using the method of Erdogan and Gupta [Q. J. Appl. Math. 29 (1972) p. 525] and iterative numerical procedures, the singular integral equations are solved numerically for the plastic zone sizes and crack tip opening displacement.

Influence of fatigue crack wake length and state of stress on crack closure

NASA Technical Reports Server (NTRS)

Telesman, J.; Fisher, D. M.

1986-01-01

The location of crack closure with respect to crack wake and specimen thickness under different loading conditions was determined. The rate of increase of K sub CL in the crack wake was found to be significantly higher for plasticity induced closure in comparison to roughness induced closure. Roughness induced closure was uniform throughout the thickness of the specimen while plasticity induced closure levels were 50 percent higher in the near surface region than in the midthickness. The influence of state of stress on low-high load interaction effects was also examined. Load interaction effects differed depending upon the state of stress and were explained in terms of delta K sub eff.

Influence of fatigue crack wake length and state of stress on crack closure

NASA Technical Reports Server (NTRS)

Telesman, Jack; Fisher, Douglas M.

1988-01-01

The location of crack closure with respect to crack wake and specimen thickness under different loading conditions was determined. The rate of increase of K sub CL in the crack wake was found to be significantly higher for plasticity induced closure in comparison to roughness induced closure. Roughness induced closure was uniform throughout the thickness of the specimen while plasticity induced closure levels were 50 percent higher in the near surface region than in the midthickness. The influence of state of stress on low-high load interaction effects was also examined. Load interaction effects differed depending upon the state of stress and were explained in terms of delta K sub eff.

3D characterization of trans- and inter-lamellar fatigue crack in (α + β) Ti alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Babout, Laurent, E-mail: Laurent.babout@p.lodz.pl; Jopek, Łukasz; Preuss, Michael

2014-12-15

This paper presents a three dimensional image processing strategy that has been developed to quantitatively analyze and correlate the path of a fatigue crack with the lamellar microstructure found in Ti-6246. The analysis is carried out on X-ray microtomography images acquired in situ during uniaxial fatigue testing. The crack, the primary β-grain boundaries and the α lamellae have been segmented separately and merged for the first time to allow a better characterization and understanding of their mutual interaction. This has particularly emphasized the role of translamellar crack growth at a very high propagation angle with regard to the lamellar orientation,more » supporting the central role of colonies favorably oriented for basal 〈a〉 slip to guide the crack in the fully lamellar microstructure of Ti alloy. - Highlights: • 3D tomography images reveal strong short fatigue crack interaction with α lamellae. • Proposed 3D image processing methodology makes their segmentation possible. • Crack-lamellae orientation maps show prevalence of translamellar cracking. • Angle study comforts the influence of basal/prismatic slip on crack path.« less

Macro-mesoscopic Fracture and Strength Character of Pre-cracked Granite Under Stress Relaxation Condition

NASA Astrophysics Data System (ADS)

Liu, Junfeng; Yang, Haiqing; Xiao, Yang; Zhou, Xiaoping

2018-05-01

The fracture characters are important index to study the strength and deformation behavior of rock mass in rock engineering. In order to investigate the influencing mechanism of loading conditions on the strength and macro-mesoscopic fracture character of rock material, pre-cracked granite specimens are prepared to conduct a series of uniaxial compression experiments. For parts of the experiments, stress relaxation tests of different durations are also conducted during the uniaxial loading process. Furthermore, the stereomicroscope is adopted to observe the microstructure of the crack surfaces of the specimens. The experimental results indicate that the crack surfaces show several typical fracture characters in accordance with loading conditions. In detail, some cleavage fracture can be observed under conventional uniaxial compression and the fractured surface is relatively rough, whereas as stress relaxation tests are attached, relative slip trace appears between the crack faces and some shear fracture starts to come into being. Besides, the crack faces tend to become smoother and typical terrace structures can be observed in local areas. Combining the macroscopic failure pattern of the specimens, it can be deduced that the duration time for the stress relaxation test contributes to the improvement of the elastic-plastic strain range as well as the axial peak strength for the studied material. Moreover, the derived conclusion is also consistent with the experimental and analytical solution for the pre-peak stage of the rock material. The present work may provide some primary understanding about the strength character and fracture mechanism of hard rock under different engineering environments.

Analytical and Experimental Study of Near-Threshold Interactions Between Crack Closure Mechanisms

NASA Technical Reports Server (NTRS)

Newman, John A.; Riddell, William T.; Piascik, Robert S.

2003-01-01

The results of an analytical closure model that considers contributions and interactions between plasticity-, roughness-, and oxide-induced crack closure mechanisms are presented and compared with experimental data. The analytical model is shown to provide a good description of the combined influences of crack roughness, oxide debris, and plasticity in the near-threshold regime. Furthermore, analytical results indicate that closure mechanisms interact in a non-linear manner such that the total amount of closure is not the sum of closure contributions for each mechanism.

The application of an atomistic J-integral to a ductile crack.

PubMed

Zimmerman, Jonathan A; Jones, Reese E

2013-04-17

In this work we apply a Lagrangian kernel-based estimator of continuum fields to atomic data to estimate the J-integral for the emission dislocations from a crack tip. Face-centered cubic (fcc) gold and body-centered cubic (bcc) iron modeled with embedded atom method (EAM) potentials are used as example systems. The results of a single crack with a K-loading compare well to an analytical solution from anisotropic linear elastic fracture mechanics. We also discovered that in the post-emission of dislocations from the crack tip there is a loop size-dependent contribution to the J-integral. For a system with a finite width crack loaded in simple tension, the finite size effects for the systems that were feasible to compute prevented precise agreement with theory. However, our results indicate that there is a trend towards convergence.

The Severely-Distressed African American Family in the Crack Era: Empowerment is not Enough

PubMed Central

Dunlap, Eloise; Golub, Andrew; Johnson, Bruce D.

2008-01-01

Numerous African American families have struggled for generations with persistent poverty, especially in the inner city. These conditions were further strained during the 1980s and 1990s by the widespread use of crack cocaine. For many, crack use became an obsession, dominated their lives, and superseded family responsibilities. This behavior placed additional pressure on already stressed kin support networks. This paper explores the processes prevailing in two households during this period. In the 2000s, children born to members of the Crack Generation are avoiding use of crack but face major deficits from their difficult childhoods. This presents both challenges and opportunities. The discussion considers initiatives from both a social problems and a strengths perspective that could help these families and help these families help themselves to advance their economic circumstances. PMID:18852841

Investigation into Cherenkov light scattering and refraction on aerogel surface

NASA Astrophysics Data System (ADS)

Barnyakov, A. Yu.; Barnyakov, M. Yu.; Bobrovnikov, V. S.; Buzykaev, A. R.; Danilyuk, A. F.; Katcin, A. A.; Kirilenko, P. S.; Kononov, S. A.; Korda, D. V.; Kravchenko, E. A.; Kudryavtsev, V. N.; Kuyanov, I. A.; Onuchin, A. P.; Ovtin, I. V.; Podgornov, N. A.; Predein, A. Yu.; Prisekin, V. G.; Protsenko, R. S.; Shekhtman, L. I.

2017-12-01

The work concerns the development of aerogel radiators for RICH detectors. Aerogel tiles with a refractive index of 1.05 were tested with a RICH prototype on the electron beam on the VEPP-4M collider. It has been shown that polishing with silk tissue yields good surface quality, the amount of light loss at this surface being about 5-7%. The Cherenkov angle resolution was measured for a tile in two conditions: with a clean exit face and with a polished exit face. The number of photons detected was 13.3 and 12.7 for the clean and polished surfaces, respectively. The Cherenkov angle resolution for the polished surface is 55% worse, which can be explained with the forward scattering on the polished surface. A tile with a crack inside was also tested. The experimental data show that the Cherenkov angle resolution is the same for tracks crossing the crack area and in a crack-free area.

PRELIMINARY PROGRESS IN THE DEVELOPMENT OF DUCTILE-PHASE TOUGHENED TUNGSTEN FOR PLASMA-FACING MATERIALS: DUAL-PHASE FINITE ELEMENT DAMAGE MODELS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Henager, Charles H.; Nguyen, Ba Nghiep; Kurtz, Richard J.

The objective of this study is to develop a finite element continuum damage model suitable for modeling deformation, cracking, and crack bridging for W-Cu, W-Ni-Fe, and other ductile phase toughened W-composites, or more generally, any multi-phase composite structure where two or more phases undergo cooperative deformation in a composite system.

Interaction between a crack and a soft inclusion

NASA Technical Reports Server (NTRS)

Xue-Hui, L.; Erdogan, F.

1985-01-01

With the application to weld defects in mind, the interaction problem between a planar-crack and a flat inclusion in an elastic solid is considered. The elastic inclusion is assumed to be sufficiently thin so that the thickness distribution of the stresses in the inclusion may be neglected. The problem is reduced to a system of four integral equations having Cauchy-type dominant kernels. The stress intensity factors are calculated and tabulated for various crack-inclusion geometries and the inclusion to matrix modulus ratios, and for general homogeneous loadiong conditions away from the crack-inclusion region.

Penetration of Face Hardened Bullet Proof Steel by Yawed .50 cal. AP (armor Piercing) Bullets at O deg. Obliquity

DTIC Science & Technology

1943-07-09

for sevarad platos a o"’l i~u.Li * DAVID I. 157"iCYI, Copy, tos 81*,AI’C Doa ’* (dir*et) B3uiad Deec !’Alb (diroot) Lt, Gseauque 10 tJt. Jolmson- E...2233 10 CP N1 1/21’ Hole. 42 2265 55 PP NH 2" Pin S. 43 2260 53 PP NH 3" x 4" Crack. 44 2240 25 PP RJ HB No Crack. 45 2252 27 PP RJ RB No Cracks, 46

Progressive failure of sheeted rock slopes: the 2009–2010 Rhombus Wall rock falls in Yosemite Valley, California, USA

USGS Publications Warehouse

Stock, Greg M.; Martel, Stephen J.; Collins, Brian D.; Harp, Edwin L.

2012-01-01

Progressive rock-fall failures in natural rock slopes are common in many environments, but often elude detailed quantitative documentation and analysis. Here we present high-resolution photography, video, and laser scanning data that document spatial and temporal patterns of a 15-month-long sequence of at least 14 rock falls from the Rhombus Wall, a sheeted granitic cliff in Yosemite Valley, California. The rock-fall sequence began on 26 August 2009 with a small failure at the tip of an overhanging rock slab. Several hours later, a series of five rock falls totaling 736 m3progressed upward along a sheeting joint behind the overhanging slab. Over the next 3 weeks, audible cracking occurred on the Rhombus Wall, suggesting crack propagation, while visual monitoring revealed opening of a sheeting joint adjacent to the previous failure surface. On 14 September 2009 a 110 m3 slab detached along this sheeting joint. Additional rock falls between 30 August and 20 November 2010, totaling 187 m3, radiated outward from the initial failure area along cliff (sub)parallel sheeting joints. We suggest that these progressive failures might have been related to stress redistributions accompanying propagation of sheeting joints behind the cliff face. Mechanical analyses indicate that tensile stresses should occur perpendicular to the cliff face and open sheeting joints, and that sheeting joints should propagate parallel to a cliff face from areas of stress concentrations. The analyses also account for how sheeting joints can propagate to lengths many times greater than their depths behind cliff faces. We posit that as a region of failure spreads across a cliff face, stress concentrations along its margin will spread with it, promoting further crack propagation and rock falls.

Analysis and prediction of Multiple-Site Damage (MSD) fatigue crack growth

NASA Technical Reports Server (NTRS)

Dawicke, D. S.; Newman, J. C., Jr.

1992-01-01

A technique was developed to calculate the stress intensity factor for multiple interacting cracks. The analysis was verified through comparison with accepted methods of calculating stress intensity factors. The technique was incorporated into a fatigue crack growth prediction model and used to predict the fatigue crack growth life for multiple-site damage (MSD). The analysis was verified through comparison with experiments conducted on uniaxially loaded flat panels with multiple cracks. Configuration with nearly equal and unequal crack distribution were examined. The fatigue crack growth predictions agreed within 20 percent of the experimental lives for all crack configurations considered.

Strain Profiling of Fatigue Crack Overload Effects Using Energy Dispersive X-Ray Diffraction

DOE Office of Scientific and Technical Information (OSTI.GOV)

Croft,M.; Zhong, Z.; Jisrawi, N.

In this paper, an assessment of commonly used assumptions associated with {Delta}K{sub eff} and their implications on FCG predictions in light of existing experimental and numerical data is presented. In particular, the following assumptions are examined: (1). {Delta}K{sub eff} fully describes cyclic stresses and strains at the crack-tip vicinity. (2). K{sub op} can be determined experimentally or numerically with certain accuracy. (3). Overload alters K{sub op} but not K{sub max} and associated s{sub max} at the crack-tip 'process zone'. (4). Contact of crack faces curtails the crack driving force in terms of {Delta}K{sub eff}. The analysis indicates that there ismore » insufficient support to justify the above assumptions. In contrary, the analysis demonstrates that a two-parameter fatigue crack driving force in terms of {Delta}K and K{sub max}, which accounts for both applied and the internal stresses should be used in FCG analyses and predictions.« less

Interaction between a circular inclusion and an arbitrarily oriented crack

NASA Technical Reports Server (NTRS)

Erdogan, F.; Gupta, G. D.; Ratwani, M.

1975-01-01

The plane interaction problem for a circular elastic inclusion embedded in an elastic matrix which contains an arbitrarily oriented crack is considered. Using the existing solutions for the edge dislocations as Green's functions, first the general problem of a through crack in the form of an arbitrary smooth arc located in the matrix in the vicinity of the inclusion is formulated. The integral equations for the line crack are then obtained as a system of singular integral equations with simple Cauchy kernels. The singular behavior of the stresses around the crack tips is examined and the expressions for the stress-intensity factors representing the strength of the stress singularities are obtained in terms of the asymptotic values of the density functions of the integral equations. The problem is solved for various typical crack orientations and the corresponding stress-intensity factors are given.

Fatigue-Crack-Growth Structural Analysis

NASA Technical Reports Server (NTRS)

Newman, J. C., Jr.

1986-01-01

Elastic and plastic deformations calculated under variety of loading conditions. Prediction of fatigue-crack-growth lives made with FatigueCrack-Growth Structural Analysis (FASTRAN) computer program. As cyclic loads are applied to initial crack configuration, FASTRAN predicts crack length and other parameters until complete break occurs. Loads are tensile or compressive and of variable or constant amplitude. FASTRAN incorporates linear-elastic fracture mechanics with modifications of load-interaction effects caused by crack closure. FASTRAN considered research tool, because of lengthy calculation times. FASTRAN written in FORTRAN IV for batch execution.

Gaseous hydrogen-induced cracking of Ti-5Al-2.5Sn.

NASA Technical Reports Server (NTRS)

Williams, D. P.; Nelson, H. G.

1972-01-01

Study of the kinetics of hydrogen-induced cracking in the Ti-5Al-2.5Sn titanium alloy, which has a structure of acicular alpha platelets in a beta matrix. The crack-growth rate at low stress-intensity levels was found to be exponentially dependent on stress intensity but essentially independent of temperature. The crack-growth rate at intermediate stress-intensity levels was found to be independent of stress intensity but dependent on temperature in such a way that crack-growth rate was controlled by a thermally activated mechanism having an activation energy of 5500 cal/mole and varied as the square root of the hydrogen pressure. The crack-growth rate at stress-intensity levels very near the fracture toughness is presumed to be independent of environment. The results are interpreted to suggest that crack growth at high stress intensities is controlled by normal, bulk failure mechanisms such as void coalescence and the like. At intermediate stress-intensity levels the transport of hydrogen to some interaction site along the alpha-beta boundary is the rate-controlling mechanism. The crack-growth behavior at low stress intensities suggests that the hydrogen interacts at this site to produce a strain-induced hydride which, in turn, induces crack growth by restricting plastic flow at the crack tip.

RECENT PROGRESS IN THE FABRICATION AND CHARACTERIZATION OF DUCTILE-PHASE-TOUGHENED TUNGSTEN LAMINATES FOR PLASMA-FACING MATERIALS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cunningham, Kevin; Odette, G Robert; Fields, Kirk A.

2015-09-23

A promising approach to increasing the fracture toughness of W-alloys is ductile-phase toughening (DPT). A ductile phase reinforcement in a brittle matrix increases toughness primarily by crack bridging. A W-Cu laminate was fabricated and the properties of the constituent metals were characterized along with those for the composite. Development of a design model for large-scale crack bridging continued.

Crack-Inclusion Interaction: A Review

DTIC Science & Technology

2014-03-01

research on the problem. fracture mechanics, inclusion, crack, dislocation, Erdogan , Dundurs, integral equation, Green’s function 58 Christopher S. Meyer...14 Figure 9. Geometry for the crack-inclusion problem, adapted from Erdogan and Wei (21) . . . 23 Figure 10. The...crack-inclusion problem geometry, adapted from Erdogan and Wei (21): figure 9 is repeated here in the text for convenience

Surface crack problems in plates

NASA Technical Reports Server (NTRS)

Joseph, P. F.; Erdogan, F.

1989-01-01

The mode I crack problem in plates under membrane loading and bending is reconsidered. The purpose is to examine certain analytical features of the problem further and to provide some new results. The formulation and the results given by the classical and the Reissner plate theories for through and part-through cracks are compared. For surface cracks the three-dimensional finite element solution is used as the basis of comparison. The solution is obtained and results are given for the crack/contact problem in a plate with a through crack under pure bending and for the crack interaction problem. Also, a procedure is developed to treat the problem of subcritical crack growth and to trace the evolution of the propagating crack.

Line spring model and its applications to part-through crack problems in plates and shells

NASA Technical Reports Server (NTRS)

Erdogan, Fazil; Aksel, Bulent

1988-01-01

The line spring model is described and extended to cover the problem of interaction of multiple internal and surface cracks in plates and shells. The shape functions for various related crack geometries obtained from the plane strain solution and the results of some multiple crack problems are presented. The problems considered include coplanar surface cracks on the same or opposite sides of a plate, nonsymmetrically located coplanar internal elliptic cracks, and in a very limited way the surface and corner cracks in a plate of finite width and a surface crack in a cylindrical shell with fixed end.

Line Spring Model and Its Applications to Part-Through Crack Problems in Plates and Shells

NASA Technical Reports Server (NTRS)

Erdogan, F.; Aksel, B.

1986-01-01

The line spring model is described and extended to cover the problem of interaction of multiple internal and surface cracks in plates and shells. The shape functions for various related crack geometries obtained from the plane strain solution and the results of some multiple crack problems are presented. The problems considered include coplanar surface cracks on the same or opposite sides of a plate, nonsymmetrically located coplanar internal elliptic cracks, and in a very limited way the surface and corner cracks in a plate of finite width and a surface crack in a cylindrical shell with fixed end.

Controlled crack shapes for indentation fracture of soda-lime glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Smith, S.M.; Scattergood, R.O.

1992-01-01

Radial cracks for indented soda-lime glass aged in distilled water were highly elliptical because of truncation by lateral cracks. Indentation in silicone oil minimized radial/lateral crack interaction but still produced cracks having nominally constant ellipticity during bend testing. Analysis of applied stress/indentation crack length data using stress intensity factors based on half-penny crack shape resulted in apparent R-curve behavior and/or overestimation of the fracture toughness. Incorporation of elliptical shape factors eliminated the R-curve behavior and reduced measured toughness to near the accepted value for soda-lime glass.

The operational styles of crack houses in Detroit.

PubMed

Mieczkowski, T

1990-01-01

This chapter identified three methods by which crack cocaine is distributed at the retail level: the street-corner or walk-up sales system, the runners and beepermen system, and the crack house. The chapter devoted primary attention to the crack house, because it appears as the most popular method for distribution. In examining the crack house, it is noted that there are identifiable styles of crack-house operations. If the quality and quantity of social interaction, as well as the situation in which sellers posture themselves, are taken as indices, then a typology can be created characterizing crack-house operations. One end of the scale is an austere method in which social interaction between buyer and seller is severely restricted; on the other, crack houses operate as tavern-style exchange locations, which include socialization above and beyond that required for the exchange of money for crack. The nature of these exchanges are themselves important, since they involve social behaviors that are of concern. One concern is the degree and nature of violence as it is associated with drug abuse. The data in this chapter describe some ways in which violence appears within the crack subculture. This violence comes from multiple sources, but some prominent ones appear to be the businesslike operations of crack distribution, the personal disorganization that surrounds and characterizes the crack-consuming environment, and the distortions of character that crack users describe as often accompanying significant binges of crack consumption. Distributors use violence to control situations. Violence is most prominently used for security at the point of retail sale, to periodically resolve conflicts with rivals, and to discipline employees when necessary. Insofar as it is described by this group of informants, crack as a social phenomenon is tied to violent and abusive behavior. This chapter reports on behaviors that, although not traditionally violent, are of concern and bear upon public health and safety. Tavern-style crack houses may encourage and make possible hypersexuality among participants and thus increase STD and HIV risks. The use of barter as a supplement to a cash economy in the crack trade represents further complications in creating social policies in reaction to this behavior. A range of other illegal and problematic behaviors was also described, illustrating the complexity of interactions that constitute the life of street-level crack users. The social policies that may be called for in response to these social events are not simple and are most certainly not defined by these particular data.(ABSTRACT TRUNCATED AT 400 WORDS)

A Crack Growth Evaluation Method for Interacting Multiple Cracks

NASA Astrophysics Data System (ADS)

Kamaya, Masayuki

When stress corrosion cracking or corrosion fatigue occurs, multiple cracks are frequently initiated in the same area. According to section XI of the ASME Boiler and Pressure Vessel Code, multiple cracks are considered as a single combined crack in crack growth analysis, if the specified conditions are satisfied. In crack growth processes, however, no prescription for the interference between multiple cracks is given in this code. The JSME Post-Construction Code, issued in May 2000, prescribes the conditions of crack coalescence in the crack growth process. This study aimed to extend this prescription to more general cases. A simulation model was applied, to simulate the crack growth process, taking into account the interference between two cracks. This model made it possible to analyze multiple crack growth behaviors for many cases (e. g. different relative position and length) that could not be studied by experiment only. Based on these analyses, a new crack growth analysis method was suggested for taking into account the interference between multiple cracks.

From Face-to-Face to Paired Oral Proficiency Interviews: The Nut Is yet to Be Cracked

ERIC Educational Resources Information Center

Birjandi, Parviz; Bagherkazemi, Marzieh

2011-01-01

The pressing need for English oral communication skills in multifarious contexts today is compelling impetus behind the large number of studies done on oral proficiency interviewing. Moreover, given the recently articulated concerns with the fairness and social dimension of such interviews, parallel concerns have been raised as to how most fairly…

Thermoregulatory value of cracking-clay soil shelters for small vertebrates during extreme desert conditions.

PubMed

Waudby, Helen P; Petit, Sophie

2017-05-01

Deserts exhibit extreme climatic conditions. Small desert-dwelling vertebrates have physiological and behavioral adaptations to cope with these conditions, including the ability to seek shelter. We investigated the temperature (T) and relative humidity (RH) regulating properties of the soil cracks that characterize the extensive cracking-clay landscapes of arid Australia, and the extent of their use by 2 small marsupial species: fat-tailed and stripe-faced dunnarts (Sminthopsis crassicaudata and Sminthopsis macroura). We measured hourly (over 24-h periods) the T and RH of randomly-selected soil cracks compared to outside conditions, during 2 summers and 2 winters. We tracked 17 dunnarts (8 Sminthopsis crassicaudata and 9 Sminthopsis macroura) to quantify their use of cracks. Cracks consistently moderated microclimate, providing more stable conditions than available from non-crack points, which often displayed comparatively dramatic fluctuations in T and RH. Both dunnart species used crack shelters extensively. Cracks constitute important shelter for small animals during extreme conditions by providing a stable microclimate, which is typically cooler than outside conditions in summer and warmer in winter. Cracks likely play a fundamental sheltering role by sustaining the physiological needs of small mammal populations. Globally, cracking-clay areas are dominated by agricultural land uses, including livestock grazing. Management of these systems should focus not only on vegetation condition, but also on soil integrity, to maintain shelter resources for ground-dwelling fauna. © 2016 International Society of Zoological Sciences, Institute of Zoology/Chinese Academy of Sciences and John Wiley & Sons Australia, Ltd.

Elastic interactions of a fatigue crack with a micro-defect by the mixed boundary integral equation method

NASA Technical Reports Server (NTRS)

Lua, Yuan J.; Liu, Wing K.; Belytschko, Ted

1993-01-01

In this paper, the mixed boundary integral equation method is developed to study the elastic interactions of a fatigue crack and a micro-defect such as a void, a rigid inclusion or a transformation inclusion. The method of pseudo-tractions is employed to study the effect of a transformation inclusion. An enriched element which incorporates the mixed-mode stress intensity factors is applied to characterize the singularity at a moving crack tip. In order to evaluate the accuracy of the numerical procedure, the analysis of a crack emanating from a circular hole in a finite plate is performed and the results are compared with the available numerical solution. The effects of various micro-defects on the crack path and fatigue life are investigated. The results agree with the experimental observations.

The interaction of pulsed eddy current with metal surface crack for various coils

NASA Astrophysics Data System (ADS)

Yang, Hung-Chi; Tai, Cheng-Chi

2002-05-01

We study the interaction of pulsed eddy current (PEC) with metal surface cracks using various coils that have different geometric sizes. In the previous work, we have showed that the PEC technique can be used to inspect electrical-discharge-machined (EDM) notches with depth from 0.5 mm to 9 mm. The results showed that the relationship between PEC signals and crack depth is obvious. In this work, we further try a series of coils with different radii, heights, turns and shapes. We will discuss the effects of these coil parameters on the PEC signal. Some other critical problems of PEC measurements such as signal drift that caused by heating effect of coil currents will be studied. We also show more experiments on fatigue cracks to demonstrate the capability of PEC technique for cracks inspection.

Dynamic response of a cracked atomic force microscope cantilever used for nanomachining

PubMed Central

2012-01-01

The vibration behavior of an atomic force microscope [AFM] cantilever with a crack during the nanomachining process is studied. The cantilever is divided into two segments by the crack, and a rotational spring is used to simulate the crack. The two individual governing equations of transverse vibration for the cracked cantilever can be expressed. However, the corresponding boundary conditions are coupled because of the crack interaction. Analytical expressions for the vibration displacement and natural frequency of the cracked cantilever are obtained. In addition, the effects of crack flexibility, crack location, and tip length on the vibration displacement of the cantilever are analyzed. Results show that the crack occurs in the AFM cantilever that can significantly affect its vibration response. PACS: 07.79.Lh; 62.20.mt; 62.25.Jk PMID:22335820

The Effect of Crack Orientation on the Nonlinear Interaction of a P-wave with an S-wave

DOE PAGES

TenCate, J. A.; Malcolm, A. E.; Feng, X.; ...

2016-06-06

Cracks, joints, fluids, and other pore-scale structures have long been hypothesized to be the cause of the large elastic nonlinearity observed in rocks. It is difficult to definitively say which pore-scale features are most important, however, because of the difficulty in isolating the source of the nonlinear interaction. In this work, we focus on the influence of cracks on the recorded nonlinear signal and in particular on how the orientation of microcracks changes the strength of the nonlinear interaction. We do this by studying the effect of orientation on the measurements in a rock with anisotropy correlated with the presencemore » and alignment of microcracks. We measure the nonlinear response via the traveltime delay induced in a low-amplitude P wave probe by a high-amplitude S wave pump. We find evidence that crack orientation has a significant effect on the nonlinear signal.« less

Probability of brittle failure

NASA Technical Reports Server (NTRS)

Kim, A.; Bosnyak, C. P.; Chudnovsky, A.

1991-01-01

A methodology was developed for collecting statistically representative data for crack initiation and arrest from small number of test specimens. An epoxy (based on bisphenol A diglycidyl ether and polyglycol extended diglycyl ether and cured with diethylene triamine) is selected as a model material. A compact tension specimen with displacement controlled loading is used to observe multiple crack initiation and arrests. The energy release rate at crack initiation is significantly higher than that at a crack arrest, as has been observed elsewhere. The difference between these energy release rates is found to depend on specimen size (scale effect), and is quantitatively related to the fracture surface morphology. The scale effect, similar to that in statistical strength theory, is usually attributed to the statistics of defects which control the fracture process. Triangular shaped ripples (deltoids) are formed on the fracture surface during the slow subcritical crack growth, prior to the smooth mirror-like surface characteristic of fast cracks. The deltoids are complementary on the two crack faces which excludes any inelastic deformation from consideration. Presence of defects is also suggested by the observed scale effect. However, there are no defects at the deltoid apexes detectable down to the 0.1 micron level.

Periodic cracks and temperature-dependent stress in Mo/Si multilayers on Si substrates

NASA Astrophysics Data System (ADS)

Kravchenko, Grygoriy; Tran, Hai T.; Volinsky, Alex A.

2018-07-01

This work examines formation of the peculiar periodic crack patterns observed in the thermally loaded Mo/Si multilayers. Using the substrate curvature measurements, the macroscopic film stress evolution during thermal cycling was investigated. Then high-speed microscopic observation of crack propagation in the annealed Mo/Si multilayers was presented providing experimental evidence of the mechanism underlying formation of the periodic crack patterns. The origin of the peculiar periodic crack patterns was determined. They were observed to form by the slow crack propagation under quasi-static conditions as a result of the interaction between the channelling crack propagation and the advance of the delamination front.

Stress-intensity factor calculations using the boundary force method

NASA Technical Reports Server (NTRS)

Tan, P. W.; Raju, I. S.; Newman, J. C., Jr.

1987-01-01

The Boundary Force Method (BFM) was formulated for the three fundamental problems of elasticity: the stress boundary value problem, the displacement boundary value problem, and the mixed boundary value problem. Because the BFM is a form of an indirect boundary element method, only the boundaries of the region of interest are modeled. The elasticity solution for the stress distribution due to concentrated forces and a moment applied at an arbitrary point in a cracked infinite plate is used as the fundamental solution. Thus, unlike other boundary element methods, here the crack face need not be modeled as part of the boundary. The formulation of the BFM is described and the accuracy of the method is established by analyzing a center-cracked specimen subjected to mixed boundary conditions and a three-hole cracked configuration subjected to traction boundary conditions. The results obtained are in good agreement with accepted numerical solutions. The method is then used to generate stress-intensity solutions for two common cracked configurations: an edge crack emanating from a semi-elliptical notch, and an edge crack emanating from a V-notch. The BFM is a versatile technique that can be used to obtain very accurate stress intensity factors for complex crack configurations subjected to stress, displacement, or mixed boundary conditions. The method requires a minimal amount of modeling effort.

Development of a relationship between external measurements and reinforcement stress

NASA Astrophysics Data System (ADS)

Brault, Andre; Hoult, Neil A.; Lees, Janet M.

2015-03-01

As many countries around the world face an aging infrastructure crisis, there is an increasing need to develop more accurate monitoring and assessment techniques for reinforced concrete structures. One of the challenges associated with assessing existing infrastructure is correlating externally measured parameters such as crack widths and surface strains with reinforcement stresses as this is dependent on a number of variables. The current research investigates how the use of distributed fiber optic sensors to measure reinforcement strain can be correlated with digital image correlation measurements of crack widths to relate external crack width measurements to reinforcement stresses. An initial set of experiments was undertaken involving a series of small-scale beam specimens tested in three-point bending with variable reinforcement properties. Relationships between crack widths and internal reinforcement strains were observed including that both the diameter and number of bars affected the measured maximum strain and crack width. A model that uses measured crack width to estimate reinforcement strain was presented and compared to the experimental results. The model was found to provide accurate estimates of load carrying capacity for a given crack width, however, the model was potentially less accurate when crack widths were used to estimate the experimental reinforcement strains. The need for more experimental data to validate the conclusions of this research was also highlighted.

Refinement of determination of critical thresholds of stress-strain behaviour by using AE data: potential for evaluation of durability of natural stone

NASA Astrophysics Data System (ADS)

Prikryl, Richard; Lokajíček, Tomáš

2017-04-01

According to previous studies, evaluation of stress-strain behaviour (in uniaxial compression) of various rocks appears to be effective tool allowing for prediction of resistance of natural stone to some physical weathering processes. Precise determination of critical thresholds, specifically of 'crack initiation' and 'crack damage' is fundamental issue in this approach. In contrast to 'crack damage stress/strain threshold', which can be easily read from deflection point on volumetric curve, detection of 'crack initiation' is much more difficult. Besides previously proposed mathematical processing of axial stress-strain curve, recording of acoustic emission (AE) data and their processing provide direct measure of various stress/strain thresholds, specifically of 'crack initiation'. This specific parameter is required during successive computation of energetic parameters (mechanical work), that can be stored by a material without formation of new defects (microcracks) due to acting stress. Based on our experimental data, this mechanical work seems to be proportional to the resistance of a material to formation of mode I (tensile) cracks that are responsible for destruction of subsurface below exposed faces of natural stone.

Analysis of Multiple Cracks in an Infinite Functionally Graded Plate

NASA Technical Reports Server (NTRS)

Shbeeb, N. I.; Binienda, W. K.; Kreider, K. L.

1999-01-01

A general methodology was constructed to develop the fundamental solution for a crack embedded in an infinite non-homogeneous material in which the shear modulus varies exponentially with the y coordinate. The fundamental solution was used to generate a solution to fully interactive multiple crack problems for stress intensity factors and strain energy release rates. Parametric studies were conducted for two crack configurations. The model displayed sensitivity to crack distance, relative angular orientation, and to the coefficient of nonhomogeneity.

The effect of an East Pacific Rise offset on the formation of secondary cracks ahead of the Cocos-Nazca Rift at the Galapagos Triple Junction

NASA Astrophysics Data System (ADS)

Smith, D. K.; Montesi, L. G.; Schouten, H.; Zhu, W.

2011-12-01

A succession of short-lived, E-W trending cracks at the Galapagos Triple Junction north and south of the Cocos-Nazca (C-N) Rift, has been explained by a simple crack interaction model. The locations of where the cracks initiate are controlled by tensile stresses generated at the East Pacific Rise (EPR) by two interacting cracks: One representing the north-south trending EPR, and the other the large, westward propagating C-N Rift, whose tip is separated from the EPR by a distance D. The model predicts symmetric cracking at the EPR north and south of the C-N Rift tip. Symmetry in the distribution of cracks north and south of the C-N Rift is observed and especially remarkable between 2.5 and 1.5 Ma when the rapid jumping of cracks toward the C-N Rift appears synchronous. The rapid jumping can be explained by decreasing D, which means that the tip of the C-N Rift was moving closer to the EPR. Symmetry of cracking breaks down at 1.5 Ma, however, with the establishment of the Dietz Deep Rift, the southern boundary of the Galapagos microplate. Symmetry of cracking also breaks down on older crust to the east between about 100 35'W and 100 45'W (about 2.6 Ma) where a rapid jumping of cracks toward the C-N Rift is observed in the south cracking region. There is no evidence of similar rapid jumping in the north cracking region. It could be simply that the response to changing the value of D is not always as predicted. It could also be that the shape of the EPR has not always been symmetric about the C-N Rift, as assumed in the model. Currently, an overlapping spreading center with a 15 km east-west offset between the limbs of the EPR has formed at 1 50'N. We assess the importance of the geometry of the EPR on the crack interaction model. The model has been modified to include a ridge offset similar to what is observed today. We find that the region of stress enhancement at the EPR (where cracks initiate) is subdued south of the C-N Rift tip because of the EPR offset. It is possible, therefore, that the asymmetry in cracking observed since about 1.5 Ma may be explained in part by the presence of a ridge offset south of the C-N Rift tip.

Assessments of Fracture Toughness of Monolithic Ceramics-SEPB Versus SEVNB Methods

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Gyekenyesi, John P.

2006-01-01

Fracture toughness of a total of 13 advanced monolithic ceramics including silicon nitrides, silicon carbide, aluminas, and glass ceramic was determined at ambient temperature by using both single edge precracked beam (SEPB) and single edge v-notched beam (SEVNB) methods. Relatively good agreement in fracture toughness between the two methods was observed for advanced ceramics with flat R-curves; whereas, poor agreement in fracture toughness was seen for materials with rising R-curves. The discrepancy in fracture toughness between the two methods was due to stable crack growth with crack closure forces acting in the wake region of cracks even in SEVNB test specimens. The effect of discrepancy in fracture toughness was analyzed in terms of microstructural feature (grain size and shape), toughening exponent in R-curve, and stable crack growth determined using back-face strain gaging.

Experimental simulation of frost wedging-induced crack propagation in alpine rockwall

NASA Astrophysics Data System (ADS)

Jia, Hailiang; Leith, Kerry; Krautblatter, Michael

2016-04-01

Frost wedging is widely presumed to be the principal mechanism responsible for shattering jointed low-porosity rocks in high alpine rockwalls. The interaction of ice and rock physics regulates the efficacy of frost wedging. In order to better understand temporal aspects of this interaction, we present results of a series of laboratory experiments monitoring crack widening as a result of ice formation in an artificial crack (4mm wide, 80mm deep) cut 20 mm from the end of a rectangular granite block. Our results indicate that i) freezing direction plays a key role in determining the magnitude of crack widening; in short-term (1 day) experiments, maximum crack widening during top-down freezing (associated with 'autumn' conditions) was around 0.11mm, while inside-out freezing (resulting from 'spring' conditions) produced only 0.02 mm of deformation; ii) neither ice, nor water pressure (direct tension and hydraulic fracturing respectively) caused measurable irreversible crack widening during short-term tests, as the calculated maximum stress intensity at the crack tip was less than the fracture toughness of our granite sample; iii) development of ice pressure is closely related to the mechanical properties of the fracture in which it forms, and as such, the interaction of ice and rock is intrinsically dynamic; iv) irreversible crack widening (about 0.03mm) was only observed following a long-term (53 day) experiment representing a simplified transition from autumn to winter conditions. We suggest this is the result of stress corrosion aided by strong opening during freezing, and to a lesser degree by ice segregation up to one week after the initial freezing period, and downward migration of liquid water during the remainder of the test. Our results suggest the fundamental assumption of frost wedging, that rapid freezing from open ends of cracks can seal water inside the crack and thus cause damage through excessive stresses induced by volumetric expansion seems questionable.

Embrittlement of MISSE 5 Polymers After 13 Months of Space Exposure

NASA Technical Reports Server (NTRS)

Guo, Aobo; Yi, Grace T.; Ashmead, Claire C.; Mitchell, Gianna G.; deGroh, Kim K.

2012-01-01

Understanding space environment induced degradation of spacecraft materials is essential when designing durable and stable spacecraft components. As a result of space radiation, debris impacts, atomic oxygen interaction, and thermal cycling, the outer surfaces of space materials degrade when exposed to low Earth orbit (LEO). The objective of this study was to measure the embrittlement of 37 thin film polymers after LEO space exposure. The polymers were flown aboard the International Space Station and exposed to the LEO space environment as part of the Materials International Space Station Experiment 5 (MISSE 5). The samples were flown in a nadir-facing position for 13 months and were exposed to thermal cycling along with low doses of atomic oxygen, direct solar radiation and omnidirectional charged particle radiation. The samples were analyzed for space-induced embrittlement using a bend-test procedure in which the strain necessary to induce surface cracking was determined. Bend-testing was conducted using successively smaller mandrels to apply a surface strain to samples placed on a semi-suspended pliable platform. A pristine sample was also tested for each flight sample. Eighteen of the 37 flight samples experienced some degree of surface cracking during bend-testing, while none of the pristine samples experienced any degree of cracking. The results indicate that 49 percent of the MISSE 5 thin film polymers became embrittled in the space environment even though they were exposed to low doses (approx.2.75 krad (Si) dose through 127 mm Kapton) of ionizing radiation.

Some remarks on elastic crack-tip stress fields.

NASA Technical Reports Server (NTRS)

Rice, J. R.

1972-01-01

It is shown that if the displacement field and stress intensity factor are known as functions of crack length for any symmetrical load system acting on a linear elastic body in plane strain, then the stress intensity factor for any other symmetrical load system whatsoever on the same body may be directly determined. The result is closely related to Bueckner's (1970) weight function, through which the stress intensity factor is expressed as a sum of work-like products between applied forces and values of the weight function at their points of application. An example of the method is given wherein the solution for a crack in a remotely uniform stress field is used to generate the expression for the stress intensity factor due to an arbitrary traction distribution on the faces of a crack. A corresponding theory is developed in an appendix for three-dimensional crack problems, although this appears to be directly useful chiefly for problems in which there is axial symmetry.

A review of Brazilian scientific output on crack--contributions to the political agenda.

PubMed

Moreira, Marcelo Rasga; Fernandes, Fernando Manuel Bessa; Ribeiro, José Mendes; Franco Neto, Thereza de Lamare

2015-04-01

scientific literature about crack abuse published in Brazilian journals indexed in SCIELO. systematic review of literature treating findings as a framework for agenda-setting orienting policy decision makers. SCIELO online journals research since 02/06/2013 on tag crack as "key word searched" and in indexes as "research amplitude". An amount of 199 references were identified and their abstracts were analyzed getting to a final group of 59 articles specifically studying crack issues in Brazil. institutional criteria (journal, subject area, and publishing time) and analytical categories created by the authors: "Social Risk", "Treatment", "Use/Abuse", "Profile", "Social Relations", and "Study". crack use impact Brazilian journals since 2011; health field is prominent; articles about "Associated Risk" and "Treatment" prevail; SUS cannot face demand;investment improvement in CAP and harm reduction; therapeutic communities need to match with SUS standards; youngers, black people and poor express users profile; rave style use; repressive policies were not well succeeded; and multidisciplinary approach are necessary.

Mapping and load response of overload strain fields: Synchrotron X-ray measurements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shukla, V; Jisrawi, N M; Sadangi, R K

High energy synchrotron X-ray diffraction measurements have been performed to provide quantitative microscopic guidance for modeling of fatigue crack growth. Specifically we report local strain mapping, along with in situ loading strain response, results on 4140 steel fatigue specimens exhibiting the crack growth retardation 'overload effect'. Detailed, 2D, {epsilon}{gamma}{gamma}-strain field mapping shows that a single overload (OL) cycle creates a compressive strain field extending millimeters above and below the crack plane. The OL strain field structures are shown to persist after the crack tip has grown well beyond the OL position. The specimen exhibiting the maximal crack growth rate retardationmore » following overload exhibits a tensile residual strain region at the crack tip. Strain field results, on in situ tensile loaded specimens, show a striking critical threshold load, F{sub c}, phenomenon in their strain response. At loads below F{sub c} the strain response is dominated by a rapid suppression of the compressive OL feature with modest response at the crack tip. At loads above F{sub c} the strain response at the OL position terminates and the response at the crack tip becomes large. This threshold load response behavior is shown to exhibit lower F{sub c} values, and dramatically enhanced rates of strain change with load as the crack tip propagates farther beyond the OL position. The OL strain feature behind the crack tip also is shown to be suppressed by removing the opposing crack faces via an electron discharge cut passing through the crack tip. Finally unique 2D strain field mapping (imaging) results, through the depth of the specimen, of the fatigue crack front and the OL feature in the wake are also presented.« less

Shapes formed by interacting cracks

NASA Astrophysics Data System (ADS)

Daniels, Karen

2012-02-01

Brittle failure through multiple cracks occurs in a wide variety of contexts, from microscopic failures in dental enamel and cleaved silicon to geological faults and planetary ice crusts. In each of these situations, with complicated stress geometries and different microscopic mechanisms, pairwise interactions between approaching cracks nonetheless produce characteristically curved fracture paths. We investigate the origins of this widely observed ``en passant'' crack pattern by fracturing a rectangular slab which is notched on each long side and subjected to quasi-static uniaxial strain from the short side. The two cracks propagate along approximately straight paths until they pass each other, after which they curve and release a lens-shaped fragment. We find that, for materials with diverse mechanical properties, each curve has an approximately square-root shape, and that the length of each fragment is twice its width. We are able to explain the origins of this universal shape with a simple geometrical model.

Characterization of Pore Defects and Fatigue Cracks in Die Cast AM60 Using 3D X-ray Computed Tomography

NASA Astrophysics Data System (ADS)

Yang, Zhuofei; Kang, Jidong; Wilkinson, David S.

2015-08-01

AM60 high pressure die castings have been used in automobile applications to reduce the weight of vehicles. However, the pore defects that are inherent in die casting may negatively affect mechanical properties, especially the fatigue properties. Here we have studied damage ( e.g., pore defects, fatigue cracks) during strained-controlled fatigue using 3-dimensional X-ray computed tomography (XCT). The fatigue test was interrupted every 2000 cycles and the specimen was removed to be scanned using a desktop micro-CT system. XCT reveals pore defects, cracks, and fracture surfaces. The results show that pores can be accurately measured and modeled in 3D. Defect bands are found to be made of pores under 50 µm (based on volume-equivalent sphere diameter). Larger pores are randomly distributed in the region between the defect bands. Observation of fatigue cracks by XCT is performed in three ways such that the 3D model gives the best illustration of crack-porosity interaction while the other two methods, with the cracks being viewed on transverse or longitudinal cross sections, have better detectability on crack initiation and crack tip observation. XCT is also of value in failure analysis on fracture surfaces. By assessing XCT data during fatigue testing and observing fracture surfaces on a 3D model, a better understanding on the crack initiation, crack-porosity interaction, and the morphology of fracture surface is achieved.

An internal crack parallel to the boundary of a nonhomogeneous half plane under thermal loading

NASA Astrophysics Data System (ADS)

Jin, Zhi-He; Noda, Naotake

1993-05-01

This paper considers the crack problem for a semi-infinite nonhomogeneous thermoelastic solid subjected to steady heat flux over the boundary. The crack faces are assumed to be insulated. The research is aimed at understanding the effect of nonhomogeneities of materials on stress intensity factors. By using the Fourier transform, the problem is reduced to a system of singular integral equations which are solved numerically. Results are presented illustrating the influence of the nonhomogeneity of the material on the stress intensity factors. Zero Mode I stress intensity factors are found for some groups of the material constants, which may be interesting for the understanding of compositions of advanced Functionally Gradient Materials.

Improved concretes for corrosion resistance

DOT National Transportation Integrated Search

1997-07-01

The deterioration of various reinforced concrete bridge components containing conventional black steel reinforcement is the most important problem facing U.S. highway agencies. A major cause of this concrete deterioration (cracking, delamination, and...

Method for hot press forming articles

DOEpatents

Baker, Robert R.; Hartsock, Dale L.

1982-01-01

This disclosure relates to an improved method for achieving the best bond strength and for minimizing distortion and cracking of hot pressed articles. In particular, in a method for hot press forming both an outer facing circumferential surface of and an inner portion of a hub, and of bonding that so-formed outer facing circumferential surface to an inner facing circumferential surface of a pre-formed ring thereby to form an article, the following improvement is made. Normally, in this method, the outside ring is restrained by a restraining sleeve of ring-shaped cross-section having an inside diameter. A die member, used to hot press form the hub, is so-formed as to have an outside diameter sized to engage the inside diameter of the restraining sleeve in a manner permitting relative movement therebetween. The improved method is one in which several pairs of matched restraining sleeve and die member are formed with each matched pair having a predetermined diameter. The predetermined diameter of each matched pair is different from another matched pair by stepped increments. The largest inside diameter of a restraining sleeve is equal to the diameter of the outer facing circumferential surface of the hub. Each pair of the matched restraining sleeve and die member is used to form an article in which an inside hub is bonded to an outside ring. The several samples so-formed are evaluated to determine which sample has the best bond formed between the hub and the ring with the least or no cracking or distortion in the ring portion of the article. Thereafter, the matched restraining sleeve and die member which form the article having the best bonding characteristics and least distortion cracking is then used for repeated formations of articles.

Surface cracks in a plate of finite width under tension or bending

NASA Technical Reports Server (NTRS)

Erdogan, F.; Boduroglu, H.

1984-01-01

The problem of a finite plate containing collinear surface cracks is considered and solved by using the line spring model with plane elasticity and Reissner's plate theory. The main focus is on the effect of interaction between two cracks or between cracks and stress-free plate boundaries on the stress intensity factors in an effort to provide extensive numerical results which may be useful in applications. Some sample results are obtained and are compared with the existing finite element results. Then the problem is solved for a single (internal) crack, two collinear cracks, and two corner cracks for wide range of relative dimensions. Particularly in corner cracks, the agreement with the finite element solution is surprisingly very good. The results are obtained for semi-elliptic and rectangular crack profiles which may, in practice, correspond to two limiting cases of the actual profile of a subcritically growing surface crack.

Surface cracks in a plate of finite width under extension or bending

NASA Technical Reports Server (NTRS)

Erdogan, F.; Boduroglu, H.

1984-01-01

In this paper the problem of a finite plate containing collinear surface cracks is considered. The problem is solved by using the line spring model with plane elasticity and Reissner's plate theory. The main purpose of the study is to investigate the effect of interaction between two cracks or between cracks and stress-free plate boundaries on the stress intensity factors and to provide extensive numerical results which may be useful in applications. First, some sample results are obtained and are compared with the existing finite element results. Then the problem is solved for a single (internal) crack, two collinear cracks and two corner cracks for wide range of relative dimensions. Particularly in corner cracks the agreement with the finite element solution is surprisingly very good. The results are obtained for semielliptic and rectangular crack profiles which may, in practice, correspond to two limiting cases of the actual profile of a subcritically growing surface crack.

Corrosion fatigue crack propagation in metals

NASA Technical Reports Server (NTRS)

Gangloff, Richard P.

1990-01-01

This review assesses fracture mechanics data and mechanistic models for corrosion fatigue crack propagation in structural alloys exposed to ambient temperature gases and electrolytes. Extensive stress intensity-crack growth rate data exist for ferrous, aluminum and nickel based alloys in a variety of environments. Interactive variables (viz., stress intensity range, mean stress, alloy composition and microstructure, loading frequency, temperature, gas pressure and electrode potential) strongly affect crack growth kinetics and complicate fatigue control. Mechanistic models to predict crack growth rates were formulated by coupling crack tip mechanics with occluded crack chemistry, and from both the hydrogen embrittlement and anodic dissolution/film rupture perspectives. Research is required to better define: (1) environmental effects near threshold and on crack closure; (2) damage tolerant life prediction codes and the validity of similitude; (3) the behavior of microcrack; (4) probes and improved models of crack tip damage; and (5) the cracking performance of advanced alloys and composites.

Brittle Materials Design, High Temperature Gas Turbine

DTIC Science & Technology

1977-08-01

hubs were inspected radiographi - cally and by fluoresent dye penetrant. The dye penetrant revealed tight cracks on the inner axial faces of hub A... radiography of green parts has proved effective in detecting major flaws. Slip cast Si3N4 test bars having a density of 2.7 gm/cc show four point MOR...this run. Post inspection showed all ceramic parts to be crack free. The rotor failed during a subsequent run at 50,000 rpm and 2300°F T.I.T. (10

Dynamic J sub I-R Curve Testing of HY-130 Steel.

DTIC Science & Technology

1981-10-01

Society for Testing and Materials 0C Degrees Celsius COD Crack-opening displacement CT Compact tension CVN Charpy V-notch dia Diameter in-lb/in 2 Inch...inches per second. A key curve for HY-130 plate was developed under dynamic loading conditions using subsized compact specimens and was applied to...face grooves were machined along the crack line to a total section reduction of 20% with a standard Charpy V-notch (CVN) cutter (450 included angle

On the interaction of ultrasound with cracks: Applications to fatigue crack growth

NASA Technical Reports Server (NTRS)

Buck, O.; Thompson, R. B.; Rehbein, D. K.

1986-01-01

Partial contact of two rough fatigue crack surfaces leads to transmission and diffraction of an acoustic signal at those contacts. Recent experimental and theoretical efforts to understand and quantify such contact in greater detail are discussed. The objective is to develop an understanding of the closure phenomenon and its application to the interpretation of fatigue data, in particular the R-ratio, spike overload/underload and threshold effects on crack propagation.

Assessment of Reinforced Concrete Surface Breaking Crack Using Rayleigh Wave Measurement.

PubMed

Lee, Foo Wei; Chai, Hwa Kian; Lim, Kok Sing

2016-03-05

An improved single sided Rayleigh wave (R-wave) measurement was suggested to characterize surface breaking crack in steel reinforced concrete structures. Numerical simulations were performed to clarify the behavior of R-waves interacting with surface breaking crack with different depths and degrees of inclinations. Through analysis of simulation results, correlations between R-wave parameters of interest and crack characteristics (depth and degree of inclination) were obtained, which were then validated by experimental measurement of concrete specimens instigated with vertical and inclined artificial cracks of different depths. Wave parameters including velocity and amplitude attenuation for each case were studied. The correlations allowed us to estimate the depth and inclination of cracks measured experimentally with acceptable discrepancies, particularly for cracks which are relatively shallow and when the crack depth is smaller than the wavelength.

A boundary element alternating method for two-dimensional mixed-mode fracture problems

NASA Technical Reports Server (NTRS)

Raju, I. S.; Krishnamurthy, T.

1992-01-01

A boundary element alternating method, denoted herein as BEAM, is presented for two dimensional fracture problems. This is an iterative method which alternates between two solutions. An analytical solution for arbitrary polynomial normal and tangential pressure distributions applied to the crack faces of an embedded crack in an infinite plate is used as the fundamental solution in the alternating method. A boundary element method for an uncracked finite plate is the second solution. For problems of edge cracks a technique of utilizing finite elements with BEAM is presented to overcome the inherent singularity in boundary element stress calculation near the boundaries. Several computational aspects that make the algorithm efficient are presented. Finally, the BEAM is applied to a variety of two dimensional crack problems with different configurations and loadings to assess the validity of the method. The method gives accurate stress intensity factors with minimal computing effort.

Fracture of an isotropic medium strengthened with a regular system of stringers

NASA Astrophysics Data System (ADS)

Mir-Salim-zadeh, M. V.

2007-01-01

An isotropic medium containing a system of foreign transverse rectilinear inclusions is considered. Such a medium can be interpreted as an infinite plate strengthened with a regular system of ribs (stringers) whose cross section is a very narrow rectangle. The medium is weakened by a periodic system of rectilinear cracks. The action of the stringers is re placed by unknown equivalent concentrated forces at the points of their connection with the medium. The boundary-value problem on equilibrium of the periodic system of cracks under the action of external tensile forces is reduced to a singular integral equation, from the solution of which the stress in tensity factors are found. The condition of limiting state of equilibrium of the cracks is formulated based on a criterion of brittle fracture. The stress state in the case where crack faces come into a partial contact is also considered.

Acquisition of Inertia by a Moving Crack

NASA Astrophysics Data System (ADS)

Goldman, Tamar; Livne, Ariel; Fineberg, Jay

2010-03-01

We experimentally investigate the dynamics of “simple” tensile cracks. Within an effectively infinite medium, a crack’s dynamics perfectly correspond to inertialess behavior predicted by linear elastic fracture mechanics. Once a crack interacts with waves that it generated at earlier times, this description breaks down. Cracks then acquire inertia and sluggishly accelerate. Crack inertia increases with crack speed v and diverges as v approaches its limiting value. We show that these dynamics are in excellent accord with an equation of motion derived in the limit of an infinite strip [M. Marder, Phys. Rev. Lett. 66, 2484 (1991)PRLTAO0031-900710.1103/PhysRevLett.66.2484].

Rayleigh wave acoustic emission during crack propagation in steel

NASA Astrophysics Data System (ADS)

Horne, Michael R.

2003-07-01

An investigation was conducted of the existence of seismic surface pulses (SSP) on crack faces in near-failure fatigue. An SSP has components of various modes of wave propagation. The component with the largest amplitude is a Rayleigh surface wave pulse. The possibility that these surface modes have much higher amplitudes than bulk modes of acoustic emission (AE) was illustrated by an idealized thought experiment relating an SSP on a half-space to the response of crack faces to crack extension. A number of aspects of AE monitoring in finite objects were investigated. Attributes of surface wave propagation on the edge of a specimen were found to be easier to monitor than other modes of wave propagation. Wavelet analysis was used to compare the characteristics of brittle AE with other sources. A new testing paradigm was developed to reduce interference from secondary sources of AE and enhance the investigation of AE from critical crack behavior. Unique specimen design features were developed, data acquisition features sought and validated, a dead weight load frame was modified, and data analysis procedures were developed. Criteria based on velocity, frequency content, amplitude and shape were devised to determine if an AE event is an SSP. The tests were designed to mimic load conditions on structures such as bridges and hence investigate the difference between AE generated in field conditions and that of typical laboratory conditions. Varieties of steel, from very ductile to very brittle, were tested. It was concluded that plastic zone formation, considered a secondary source of AE, was found not to interfere with the SSP activity. The SSP was found experimentally to have 2-3 times the amplitude of the bulk wave AE. The lack of sufficient AE did not allow for determination of conclusive changes in the AE as the specimens approached failure. However, it was found that brittle crack extension in fatigue and ductile failure can produce wave propagation resembling the SSP.

Rayleigh wave acoustic emission during crack propagation in steel

NASA Astrophysics Data System (ADS)

Horne, Michael R.

An investigation was conducted of the existence of seismic surface pulses (SSP) on crack faces in near-failure fatigue. An SSP has components of various modes of wave propagation. The component with the largest amplitude is a Rayleigh surface wave pulse. The possibility that these surface modes have much higher amplitudes than bulk modes of acoustic emission (AE) was illustrated by an idealized thought experiment relating an SSP on a half-space to the response of crack faces to crack extension. A number of aspects of AE monitoring in finite objects were investigated. Attributes of surface wave propagation on the edge of a specimen were found to be easier to monitor than other modes of wave propagation. Wavelet analysis was used to compare the characteristics of brittle AE with other sources. A new testing paradigm was developed to reduce interference from secondary sources of AE and enhance the investigation of AE from critical crack behavior. Unique specimen design features were developed, data acquisition features sought and validated, a dead weight load frame was modified, and data analysis procedures were developed. Criteria based on velocity, frequency content, amplitude and shape were devised to determine if an AE event is an SSP. The tests were designed to mimic load conditions on structures such as bridges and hence investigate the difference between AE generated in field conditions and that of typical laboratory conditions. Varieties of steel, from very ductile to very brittle, were tested. It was concluded that plastic zone formation, considered a secondary source of AE, was found not to interfere with the SSP activity. The SSP was found experimentally to have 2-3 times the amplitude of the bulk wave AE. The lack of sufficient AE did not allow for determination of conclusive changes in the AE as the specimens approached failure. However, it was found that brittle crack extension in fatigue and ductile failure can produce wave propagation resembling the SSP.

Electrostatic measures for a piezoelectric thin film with an embedded crack in the substrate: II. Mode II

NASA Astrophysics Data System (ADS)

Ali, Rizwaan; Mahapatra, D. Roy; Gopalakrishnan, S.

2008-04-01

This paper is a successor to the previous paper by Ali et al (2008 Smart Mater. Struct. 17 025037); it presents the analysis for sensing an embedded mode-II crack in a substrate. The displacement field kinematics for the film-substrate system is extended to the problem of applied surface shear stress. This extension requires modifying the model presented in the previous paper to include the differences due to changes in boundary and excitation conditions. The film response in terms of voltage pattern over the film area—peculiar to the presence of a mode-II crack in the substrate—is illustrated here through the results of numerical simulations. Our analysis shows that the proposed electrostatic measures of the voltage and its gradients are useful in identifying the axial and depth-wise location, as well as the crack-face area of a planar mode-II crack. There is a marked difference in the pattern of results presented in this paper with the results in part I of this work for a mode-I crack. This distinction is of utmost importance, for it singularly suffices to identify the mode of crack in a substrate for a given set of boundary conditions.

Hydrogen enhanced crack growth in 18 Ni maraging steels

NASA Technical Reports Server (NTRS)

Hudak, S. J., Jr.; Wei, R. P.

1976-01-01

The kinetics of sustained-load subcritical crack growth for 18 Ni maraging steels in high-purity hydrogen are examined using the crack-tip stress intensity factor K as a measure of crack driving force. Crack growth rate as a function of stress intensity exhibited a clearly defined K-independent stage (Stage II). Crack growth rates in an 18 Ni (grade 250) maraging steel are examined for temperatures from -6 to +100 C. A critical temperature was observed above which crack growth rates became diminishingly small. At lower temperatures the activation energy for Stage II crack growth was found to be 16.7 plus or minus 3.3 kJ/mole. Temperature and hydrogen partial pressure are shown to interact in a complex manner to determine the apparent Kth (stress intensity level below which no observable crack growth occurs) and the crack growth behavior. Comparison of results on '250' and '300' grades of 18 Ni maraging steel indicate a significant influence of alloy composition and/or strength level on the crack growth behavior.

Theoretical predicting of permeability evolution in damaged rock under compressive stress

NASA Astrophysics Data System (ADS)

Vu, M. N.; Nguyen, S. T.; To, Q. D.; Dao, N. H.

2017-05-01

This paper outlines an analytical model of crack growth induced permeability changes. A theoretical solution of effective permeability of cracked porous media is derived. The fluid flow obeys Poisseuille's law along the crack and Darcy's law in the porous matrix. This solution exhibits a percolation threshold for any type of crack distribution apart from a parallel crack distribution. The physical behaviour of fluid flow through a cracked porous material is well reproduced by the proposed model. The presence of this effective permeability coupling to analytical expression of crack growth under compression enables the modelling of the permeability variation due to stress-induced cracking in a porous rock. This incorporation allows the prediction of the permeability change of a porous rock embedding an anisotropic crack distribution from any initial crack density, that is, lower, around or upper to percolation threshold. The interaction between cracks is not explicitly taken into account. The model is well applicable both to micro- and macrocracks.

Modeling Transverse Cracking in Laminates With a Single Layer of Elements Per Ply

NASA Technical Reports Server (NTRS)

Van Der Meer, Frans P.; Davila, Carlos G.

2012-01-01

The objective of the present paper is to investigate the ability of mesolevel X-FEM models with a single layer of elements per ply to capture accurately all aspects of matrix cracking. In particular, we examine whether the model can predict the insitu ply thickness effect on crack initiation and propagation, the crack density as a function of strain, the strain for crack saturation, and the interaction between delamination and transverse cracks. Results reveal that the simplified model does not capture correctly the shear-lag relaxation of the stress field on either side of a crack, which leads to an overprediction of the crack density. It is also shown, however, that after onset of delamination many of the inserted matrix cracks close again, and that the density of open cracks becomes similar to the density predicted by the detailed model. The degree to which the spurious cracks affect the global response is quantified and the reliability of the mesolevel approach with a single layer of elements per ply is discussed.

Elaboration of the Charge Constructions of Explosives for the Structure of Facing Stone

NASA Astrophysics Data System (ADS)

Khomeriki, Sergo; Mataradze, Edgar; Chikhradze, Nikoloz; Losaberidze, Marine; Khomeriki, Davit; Shatberashvili, Grigol

2017-12-01

Increased demand for high-strength facing material caused the enhancement of the volume of explosives use in modern technologies of blocks production. The volume of broken rocks and crushing quality depends on the rock characteristics and on the properties of the explosive, in particular on its brisance and serviceability. Therefore, the correct selection of the explosive for the specific massif is of a considerable practical importance. For efficient mining of facing materials by explosion method the solving of such problems as determination of the method of blasthole drilling as well as of the regime and charge values, selection of the explosive, blastholes distribution in the face and their order is necessary. This paper focuses on technical solutions for conservation of rock natural structure in the blocks of facing material, mined by the use of the explosives. It has been established that the efficient solving of mentioned problem is attained by reducing of shock pulse duration. In such conditions the rigidity of crystalline lattice increases in high pressure area. As a result, the hazard if crack formation in structural unites and the increases of natural cracks are excluded. Short-time action of explosion pulse is possible only by linear charges of the explosives, characterized by high detonation velocity which detonate by the velocity of 7-7.5 km/sec and are characterized by very small critical diameter.

Influence of High Cycle Thermal Loads on Thermal Fatigue Behavior of Thick Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Miller, Robert A.

1997-01-01

Thick thermal barrier coating systems in a diesel engine experience severe thermal Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF) during engine operation. In the present study, the mechanisms of fatigue crack initiation and propagation, as well as of coating failure, under thermal loads which simulate engine conditions, are investigated using a high power CO2 laser. In general, surface vertical cracks initiate early and grow continuously under LCF and HCF cyclic stresses. It is found that in the absence of interfacial oxidation, the failure associated with LCF is closely related to coating sintering and creep at high temperatures, which induce tensile stresses in the coating after cooling. Experiments show that the HCF cycles are very damaging to the coating systems. The combined LCF and HCF tests produced more severe coating surface cracking, microspallation and accelerated crack growth, as compared to the pure LCF test. It is suggested that the HCF component cannot only accelerate the surface crack initiation, but also interact with the LCF by contributing to the crack growth at high temperatures. The increased LCF stress intensity at the crack tip due to the HCF component enhances the subsequent LCF crack growth. Conversely, since a faster HCF crack growth rate will be expected with lower effective compressive stresses in the coating, the LCF cycles also facilitate the HCF crack growth at high temperatures by stress relaxation process. A surface wedging model has been proposed to account for the HCF crack growth in the coating system. This mechanism predicts that HCF damage effect increases with increasing temperature swing, the thermal expansion coefficient and the elastic modulus of the ceramic coating, as well as the HCF interacting depth. A good agreement has been found between the analysis and experimental evidence.

Ultrasound excited thermography: an efficient tool for the characterization of vertical cracks

NASA Astrophysics Data System (ADS)

Mendioroz, A.; Celorrio, R.; Salazar, A.

2017-11-01

Ultrasound excited thermography has gained a renewed interest in the last two decades as a nondestructive testing technique aimed at detecting and characterizing surface breaking and shallow subsurface discontinuities. It is based on measurement of the IR radiation emitted by the specimen surface to detect temperature rises produced by the heating of defects under high amplitude ultrasound excitation and is primarily addressed to flaws with contacting faces, such as kissing cracks or tight delaminations. The simplicity of application and the ability to detect small cracks in challenging media makes it an attractive emerging technology, which is still in a development stage. However, it has proven to provide an opportunity for the quantitative characterization of defects, mainly of vertical cracks. In this review, we present the principles of the technique and the different experimental implementations, we put it in context with other nondestructive tests and we summarize the work done in order to improve defect detectability and test reliability, with the final goal of determining the probability of detection. Then we review the contributions aimed at characterizing vertical cracks, i.e. retrieving the geometry and location of the crack from surface temperature data, generated by ultrasonic excitation.

Results of the second Round Robin on opening-load measurement conducted by ASTM Task Group E24.04.04 on crack closure measurement and analysis

NASA Technical Reports Server (NTRS)

Phillips, E. P.

1993-01-01

A second experimental Round Robin on the measurement of the crack opening load in fatigue crack growth tests has been completed by the ASTM Task Group E24.04.04 on Crack Closure Measurement and Analysis. Fourteen laboratories participated in the testing of aluminum alloy compact tension specimens. Opening-load measurements were made at three crack lengths during constant Delta K, constant stress ratio tests by most of the participants. Four participants made opening-load measurements during threshold tests. All opening-load measurements were based on the analysis of specimens compliance behavior, where the displacement/strain was measured either at the crack mouth or the mid-height back face location. The Round Robin data were analyzed for opening load using two non-subjective analysis methods: the compliance offset and the correlation coefficient methods. The scatter in the opening load results was significantly reduced when some of the results were excluded from the analysis population based on an accept/reject criterion for raw data quality. The compliance offset and correlation coefficient opening load analysis methods produced similar results for data populations that had been screened to eliminate poor quality data.

Ultrasonic inspection of studs (bolts) using dynamic predictive deconvolution and wave shaping.

PubMed

Suh, D M; Kim, W W; Chung, J G

1999-01-01

Bolt degradation has become a major issue in the nuclear industry since the 1980's. If small cracks in stud bolts are not detected early enough, they grow rapidly and cause catastrophic disasters. Their detection, despite its importance, is known to be a very difficult problem due to the complicated structures of the stud bolts. This paper presents a method of detecting and sizing a small crack in the root between two adjacent crests in threads. The key idea is from the fact that the mode-converted Rayleigh wave travels slowly down the face of the crack and turns from the intersection of the crack and the root of thread to the transducer. Thus, when a crack exists, a small delayed pulse due to the Rayleigh wave is detected between large regularly spaced pulses from the thread. The delay time is the same as the propagation delay time of the slow Rayleigh wave and is proportional to the site of the crack. To efficiently detect the slow Rayleigh wave, three methods based on digital signal processing are proposed: wave shaping, dynamic predictive deconvolution, and dynamic predictive deconvolution combined with wave shaping.

Damage in gamma titanium aluminides due to small particle impacts

NASA Astrophysics Data System (ADS)

Stief, P. S.; Rubal, M. P.; Gray, G. T., III; Pereiras, J. M.

1998-10-01

Initiation of cracking due to small particle impacts on low ductility intermetallics is investigated experimentally and theoretically. The gamma titanium aluminide alloys of interest which are being considered for elevated temperature structural applications in aircraft engines exhibit tensile ductilities on the order of 1-2%. Cracking due to any source, including small particle impacts, is of concern given the rapid growth of cracks in fatigue. This investigation focuses on a model geometry which reproduces the rear face cracking that is induced by a small particle impinging on an air foil leading edge. Small steel spheres are projected onto thin plates at velocities ranging from 76 to 305 ms ; cracking is thereby induced on the rear surface of the plates. Through finite element analyses of the dynamic impact event and some analytical estimates, we examine the hypothesis that crack initiation due to small particle impacts can be correlated with material ductility and with the severity and spatial extent of the straining during the impact event. In addition, with the use of static indentation tests in which similar strain distributions are present, some insight is gained into the difference in ductility between high and low strain rates. 1998 Elsevier Science Ltd.

Amplitude-independent flaw length determination using differential eddy current

NASA Astrophysics Data System (ADS)

Shell, E.

2013-01-01

Military engine component manufacturers typically specify the eddy current (EC) inspection requirements as a crack length or depth with the assumption that the cracks in both the test specimens and inspected component are of a similar fixed aspect ratio. However, differential EC response amplitude is dependent on the area of the crack face, not the length or depth. Additionally, due to complex stresses, in-service cracks do not always grow in the assumed manner. It would be advantageous to use more of the information contained in the EC data to better determine the full profile of cracks independent of the fixed aspect ratio amplitude response curve. A specimen with narrow width notches is used to mimic cracks of varying aspect ratios in a controllable manner. The specimen notches have aspect ratios that vary from 1:1 to 10:1. Analysis routines have been developed using the shape of the EC response signals that can determine the length of a surface flaw of common orientations without use of the amplitude of the signal or any supporting traditional probability of detection basis. Combined with the relationship between signal amplitude and area, the depth of the flaw can also be calculated.

Discrete Element Model for Simulations of Early-Life Thermal Fracturing Behaviors in Ceramic Nuclear Fuel Pellets

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hai Huang; Ben Spencer; Jason Hales

2014-10-01

A discrete element Model (DEM) representation of coupled solid mechanics/fracturing and heat conduction processes has been developed and applied to explicitly simulate the random initiations and subsequent propagations of interacting thermal cracks in a ceramic nuclear fuel pellet during initial rise to power and during power cycles. The DEM model clearly predicts realistic early-life crack patterns including both radial cracks and circumferential cracks. Simulation results clearly demonstrate the formation of radial cracks during the initial power rise, and formation of circumferential cracks as the power is ramped down. In these simulations, additional early-life power cycles do not lead to themore » formation of new thermal cracks. They do, however clearly indicate changes in the apertures of thermal cracks during later power cycles due to thermal expansion and shrinkage. The number of radial cracks increases with increasing power, which is consistent with the experimental observations.« less

Recent advances in the modelling of crack growth under fatigue loading conditions

NASA Technical Reports Server (NTRS)

Dekoning, A. U.; Tenhoeve, H. J.; Henriksen, T. K.

1994-01-01

Fatigue crack growth associated with cyclic (secondary) plastic flow near a crack front is modelled using an incremental formulation. A new description of threshold behaviour under small load cycles is included. Quasi-static crack extension under high load excursions is described using an incremental formulation of the R-(crack growth resistance)- curve concept. The integration of the equations is discussed. For constant amplitude load cycles the results will be compared with existing crack growth laws. It will be shown that the model also properly describes interaction effects of fatigue crack growth and quasi-static crack extension. To evaluate the more general applicability the model is included in the NASGRO computer code for damage tolerance analysis. For this purpose the NASGRO program was provided with the CORPUS and the STRIP-YIELD models for computation of the crack opening load levels. The implementation is discussed and recent results of the verification are presented.

Buckling delamination of the circular sandwich plate with piezoelectric face and elastic core layers under rotationally symmetric external pressure

NASA Astrophysics Data System (ADS)

Akbarov, Surkay D.; Cafarova, Fazile I.; Yahnioglu, Nazmiye

2017-02-01

The axisymmetric buckling delamination of the piezoelectric circular sandwich plate with piezoelectric face and elastic (metal) core layers around the interface penny-shaped cracks is investigated. The case is considered where short-circuit conditions with respect to the electrical potential on the upper and lower and also lateral surfaces of face layers are satisfied. It is assumed that the edge surfaces of the cracks have an infinitesimal rotationally symmetric initial imperfection and the development of this imperfection with rotationally symmetric compressive forces acting on the lateral surface of the plate is studied by employing the exact geometrically non-linear field equations and relations of electro-elasticity for piezoelectric materials. Solution to the considered nonlinear problem is reduced to solution of the series boundary value problems derived by applying the linearization procedure with respect to small imperfection of the sought values. Numerical results reveal the effect of piezoelectricity as well as geometrical and material parameters on the critical values are determined numerically by employing finite element method (FEM).

Fatigue crack propagation of nickel-base superalloys at 650 deg C

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Miner, R. V.

1988-01-01

The 650 C fatigue crack propagation behavior of two nickel-base superalloys, Rene 95 and Waspaloy, is studied with particular emphasis placed on understanding the roles of creep, environment, and two key grain boundary alloying additions, boron and zirconium. Comparison of air and vacuum data shows the air environment to be detrimental over a wide range of frequencies for both alloys. More in-depth analysis on Rene 95 shows at lower frequencies, such as 0.02 Hz, failure in air occurs by intergranular, environmentally-assisted creep crack growth, while at higher frequencies, up to 5.0 Hz, environmental interaction are still evident but creep effects are minimized. The effect of B and Zr in Waspaloy is found to be important where environmental and/or creep interactions are presented. In those instances, removal of B and Zr dramatically increases crack growth and it is therefore plausible that effective dilution of these elements may explain a previously observed trend in which crack growth rates increase with decreasing grain size.

Fatigue crack propagation of nickel-base superalloys at 650 deg C

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Miner, R. V.

1985-01-01

The 650 C fatigue crack propagation behavior of two nickel-base superalloys, Rene 95 and Waspaloy, is studied with particular emphasis placed on understanding the roles of creep, environment, and two key grain boundary alloying additions, boron and zirconium. Comparison of air and vacuum data shows the air environment to be detrimental over a wide range of frequencies for both alloys. More in-depth analysis on Rene 95 shows at lower frequencies, such as 0.02 Hz, failure in air occurs by intergranular, environmentally-assisted creep crack growth, while at higher frequencies, up to 5.0 Hz, environmental interactions are still evident but creep effects are minimized. The effect of B and Zr in Waspaloy is found to be important where environmental and/or creep interactions are presented. In those instances, removal of B and Zr dramatically increases crack growth and it is therefore plausible that effective dilution of these elements may explain a previously observed trend in which crack growth rates increase with decreasing grain size.

An autonomous surface discontinuity detection and quantification method by digital image correlation and phase congruency

NASA Astrophysics Data System (ADS)

Cinar, A. F.; Barhli, S. M.; Hollis, D.; Flansbjer, M.; Tomlinson, R. A.; Marrow, T. J.; Mostafavi, M.

2017-09-01

Digital image correlation has been routinely used to measure full-field displacements in many areas of solid mechanics, including fracture mechanics. Accurate segmentation of the crack path is needed to study its interaction with the microstructure and stress fields, and studies of crack behaviour, such as the effect of closure or residual stress in fatigue, require data on its opening displacement. Such information can be obtained from any digital image correlation analysis of cracked components, but it collection by manual methods is quite onerous, particularly for massive amounts of data. We introduce the novel application of Phase Congruency to detect and quantify cracks and their opening. Unlike other crack detection techniques, Phase Congruency does not rely on adjustable threshold values that require user interaction, and so allows large datasets to be treated autonomously. The accuracy of the Phase Congruency based algorithm in detecting cracks is evaluated and compared with conventional methods such as Heaviside function fitting. As Phase Congruency is a displacement-based method, it does not suffer from the noise intensification to which gradient-based methods (e.g. strain thresholding) are susceptible. Its application is demonstrated to experimental data for cracks in quasi-brittle (Granitic rock) and ductile (Aluminium alloy) materials.

Creep and cracking of concrete hinges: insight from centric and eccentric compression experiments.

PubMed

Schlappal, Thomas; Schweigler, Michael; Gmainer, Susanne; Peyerl, Martin; Pichler, Bernhard

2017-01-01

Existing design guidelines for concrete hinges consider bending-induced tensile cracking, but the structural behavior is oversimplified to be time-independent. This is the motivation to study creep and bending-induced tensile cracking of initially monolithic concrete hinges systematically. Material tests on plain concrete specimens and structural tests on marginally reinforced concrete hinges are performed. The experiments characterize material and structural creep under centric compression as well as bending-induced tensile cracking and the interaction between creep and cracking of concrete hinges. As for the latter two aims, three nominally identical concrete hinges are subjected to short-term and to longer-term eccentric compression tests. Obtained material and structural creep functions referring to centric compression are found to be very similar. The structural creep activity under eccentric compression is significantly larger because of the interaction between creep and cracking, i.e. bending-induced cracks progressively open and propagate under sustained eccentric loading. As for concrete hinges in frame-like integral bridge construction, it is concluded (i) that realistic simulation of variable loads requires consideration of the here-studied time-dependent behavior and (ii) that permanent compressive normal forces shall be limited by 45% of the ultimate load carrying capacity, in order to avoid damage of concrete hinges under sustained loading.

Crack problems for a rectangular plate and an infinite strip

NASA Technical Reports Server (NTRS)

Civelek, M. B.; Erdogan, F.

1980-01-01

The general plane problem for an infinite strip containing multiple cracks perpendicular to its boundaries is considered. The problem is reduced to a system of singular integral equations. Two specific problems of practical interest are then studied in detail. The first problem explores the interaction effect of multiple edge cracks in a plate or beam under tension or bending. The second problem is that of a rectangular plate containing an arbitrarily oriented crack in the plane of symmetry. Particular emphasis is placed on the problem of a plate containing an edge crack and subjected to concentrated forces.

Feasibility of fatigue crack detection and tracking with a multi-sensor in-situ monitoring system

NASA Astrophysics Data System (ADS)

Zhao, Xiaoliang; Qi, Kevin; Qian, Tao; Mei, Gang

2014-02-01

Fatigue crack is a common problem for steel bridges. A cost effective and reliable method for detecting and verifying growth of a crack is desired. In this work, feasibilities of fatigue crack monitoring with acoustic emission sensors and strain gauges were studied on an A36 steel compact-tension coupon under cyclic tensile loading. By examining the ultrasonic signal time-of-arrival and frequency spectrum, acoustic emissions from a crack growth can be distinguished from other structural borne noises such as those from the interaction of loading bolts with the bolt holes on the plate. Strain sensor and clip gauge sensor data were also correlated well with the growth of the crack.

Occlusal overload investigations by noninvasive technology: fluorescence microscopy and en-face optical coherence tomography

NASA Astrophysics Data System (ADS)

Marcauteanu, Corina; Negrutiu, Meda; Sinescu, Cosmin; Demjan, Enikö; Hughes, Michael; Bradu, Adrian; Dobre, George; Podoleanu, Adrian G.

2009-07-01

The aim of this study is the early detection and monitoring of occlusal overload in bruxing patients. En-Face Optical coherence tomography (eF-OCT) and fluorescence microscopy (FM) were used for the imaging of several anterior teeth extracted from patients with light active bruxism. We found a characteristic pattern of enamel cracks, that reached the tooth surface. We concluded that the combination of the en-Face OCT and FM is a promising non-invasive alternative technique for reliable monitoring of occlusal overload.

Fracture mechanics and surface chemistry investigations of environment-assisted crack growth

NASA Technical Reports Server (NTRS)

Wei, R. P.; Klier, K.; Simmons, G. W.; Chou, Y. T.

1984-01-01

It is pointed out that environment-assisted subcritical crack growth in high-strength steels and other high-strength alloys (particularly in hydrogen and in hydrogenous environments) is an important technological problem of long standing. This problem is directly related to issues of structural integrity, durability, and reliability. The terms 'hydrogen embrittlement' and 'stress corrosion cracking' have been employed to describe the considered phenomenon. This paper provides a summary of contributions made during the past ten years toward the understanding of environmentally assisted crack growth. The processes involved in crack growth are examined, and details regarding crack growth and chemical reactions are discussed, taking into account crack growth in steels exposed to water/water vapor, the effect of hydrogen, reactions involving hydrogen sulfide, and aspects of fracture surface morphology and composition. Attention is also given to the modeling of crack growth response, crack growth in gas mixtures, and the interaction of solute atoms with the crack-tip stress field.

Crack propagation of brittle rock under high geostress

NASA Astrophysics Data System (ADS)

Liu, Ning; Chu, Weijiang; Chen, Pingzhi

2018-03-01

Based on fracture mechanics and numerical methods, the characteristics and failure criterions of wall rock cracks including initiation, propagation, and coalescence are analyzed systematically under different conditions. In order to consider the interaction among cracks, adopt the sliding model of multi-cracks to simulate the splitting failure of rock in axial compress. The reinforcement of bolts and shotcrete supporting to rock mass can control the cracks propagation well. Adopt both theory analysis and simulation method to study the mechanism of controlling the propagation. The best fixed angle of bolts is calculated. Then use ansys to simulate the crack arrest function of bolt to crack. Analyze the influence of different factors on stress intensity factor. The method offer more scientific and rational criterion to evaluate the splitting failure of underground engineering under high geostress.

Inclusion models of tensile fracture in fiber-reinforced brittle-matrix composites. Ph.D. Thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tsai, W.

1993-12-31

Inclusion models of tensile fracture in fiber-reinforced brittle-matrix composites are proposed in this study. Three stages of matrix cracking including initiation of microcracks, propagation of a bridged crack and multiplication of periodic cracks are modeled using the unique approach - Eshelby`s equivalent inclusion method. Moreover, the interfacial debonding may occur during matrix cracking and is taken into account by the present analysis. After interfacial debonding initiates, the fiber slides against the friction which is assumed to be constant in chapter 2 and chapter 3. However, the fiber-matrix interfaces are assumed to be Coulomb`s friction controlled in chapter 4. Energy releasemore » rate and crack resistance are obtained analytically. From the fracture criterion, the equivalence of energy release rate and crack resistance, the critical applied stress is also obtained. On the critical applied stress the effects of material parameters such as interfacial frictional stress, interfacial surface energy, volume fraction of fibers, misfit strain are evaluated. These evaluations are important for the purpose of material design. Finally, it is attempted in chapter 5 to solve the crack-inhomogeneity interaction problem inhomogeneities. First, the formulation of two inhomogeneities without overlapping is derived in detail. When one of the inhomogeneities is the penny-shape crack and the other one is the ellipsoidal inhomogeneity, the interaction energy between the crack and the applied stress and the energy release rate of the crack are evaluated. Based on the framework of this chapter, one can deal with the real configuration including many inhomogeneities in the similar way. Also, the misfit strains due to thermal mismatch, phase transformation et al. can be included in the present analysis with no difficulty.« less

Fracture Capabilities in Grizzly with the extended Finite Element Method (X-FEM)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dolbow, John; Zhang, Ziyu; Spencer, Benjamin

Efforts are underway to develop fracture mechanics capabilities in the Grizzly code to enable it to be used to perform deterministic fracture assessments of degraded reactor pressure vessels (RPVs). A capability was previously developed to calculate three-dimensional interaction- integrals to extract mixed-mode stress-intensity factors. This capability requires the use of a finite element mesh that conforms to the crack geometry. The eXtended Finite Element Method (X-FEM) provides a means to represent a crack geometry without explicitly fitting the finite element mesh to it. This is effected by enhancing the element kinematics to represent jump discontinuities at arbitrary locations inside ofmore » the element, as well as the incorporation of asymptotic near-tip fields to better capture crack singularities. In this work, use of only the discontinuous enrichment functions was examined to see how accurate stress intensity factors could still be calculated. This report documents the following work to enhance Grizzly’s engineering fracture capabilities by introducing arbitrary jump discontinuities for prescribed crack geometries; X-FEM Mesh Cutting in 3D: to enhance the kinematics of elements that are intersected by arbitrary crack geometries, a mesh cutting algorithm was implemented in Grizzly. The algorithm introduces new virtual nodes and creates partial elements, and then creates a new mesh connectivity; Interaction Integral Modifications: the existing code for evaluating the interaction integral in Grizzly was based on the assumption of a mesh that was fitted to the crack geometry. Modifications were made to allow for the possibility of a crack front that passes arbitrarily through the mesh; and Benchmarking for 3D Fracture: the new capabilities were benchmarked against mixed-mode three-dimensional fracture problems with known analytical solutions.« less

An Artificial Neural Network-Based Algorithm for Evaluation of Fatigue Crack Propagation Considering Nonlinear Damage Accumulation

PubMed Central

Zhang, Wei; Bao, Zhangmin; Jiang, Shan; He, Jingjing

2016-01-01

In the aerospace and aviation sectors, the damage tolerance concept has been applied widely so that the modeling analysis of fatigue crack growth has become more and more significant. Since the process of crack propagation is highly nonlinear and determined by many factors, such as applied stress, plastic zone in the crack tip, length of the crack, etc., it is difficult to build up a general and flexible explicit function to accurately quantify this complicated relationship. Fortunately, the artificial neural network (ANN) is considered a powerful tool for establishing the nonlinear multivariate projection which shows potential in handling the fatigue crack problem. In this paper, a novel fatigue crack calculation algorithm based on a radial basis function (RBF)-ANN is proposed to study this relationship from the experimental data. In addition, a parameter called the equivalent stress intensity factor is also employed as training data to account for loading interaction effects. The testing data is then placed under constant amplitude loading with different stress ratios or overloads used for model validation. Moreover, the Forman and Wheeler equations are also adopted to compare with our proposed algorithm. The current investigation shows that the ANN-based approach can deliver a better agreement with the experimental data than the other two models, which supports that the RBF-ANN has nontrivial advantages in handling the fatigue crack growth problem. Furthermore, it implies that the proposed algorithm is possibly a sophisticated and promising method to compute fatigue crack growth in terms of loading interaction effects. PMID:28773606

An Artificial Neural Network-Based Algorithm for Evaluation of Fatigue Crack Propagation Considering Nonlinear Damage Accumulation.

PubMed

Zhang, Wei; Bao, Zhangmin; Jiang, Shan; He, Jingjing

2016-06-17

In the aerospace and aviation sectors, the damage tolerance concept has been applied widely so that the modeling analysis of fatigue crack growth has become more and more significant. Since the process of crack propagation is highly nonlinear and determined by many factors, such as applied stress, plastic zone in the crack tip, length of the crack, etc. , it is difficult to build up a general and flexible explicit function to accurately quantify this complicated relationship. Fortunately, the artificial neural network (ANN) is considered a powerful tool for establishing the nonlinear multivariate projection which shows potential in handling the fatigue crack problem. In this paper, a novel fatigue crack calculation algorithm based on a radial basis function (RBF)-ANN is proposed to study this relationship from the experimental data. In addition, a parameter called the equivalent stress intensity factor is also employed as training data to account for loading interaction effects. The testing data is then placed under constant amplitude loading with different stress ratios or overloads used for model validation. Moreover, the Forman and Wheeler equations are also adopted to compare with our proposed algorithm. The current investigation shows that the ANN-based approach can deliver a better agreement with the experimental data than the other two models, which supports that the RBF-ANN has nontrivial advantages in handling the fatigue crack growth problem. Furthermore, it implies that the proposed algorithm is possibly a sophisticated and promising method to compute fatigue crack growth in terms of loading interaction effects.

Effect of Mechanical Heterogeneity on the Crack Driving Force of a Reactor Pressure Vessel Outlet Nozzle DMW Joint

NASA Astrophysics Data System (ADS)

Lingyan, Zhao; Yinghao, Cui; He, Xue

2017-12-01

The welding mechanical heterogeneity, load complexity, material and geometrical structure makes it very difficult to assess the structural integrity of dissimilar metal weld (DMW) joints. Based on a numerical simulated approach of the continuous change of material mechanical property in the buttering layer, a reactor pressure vessel (RPV) outlet nozzle DMW joint with service loads is studied, effect of mechanical heterogeneity on the stress-strain field and stress triaxiality at the semi-elliptical surface crack front are discussed. The analyses show that once the crack extends into the high hardness zone of Alloy 182 buttering, the strain decreases sharply, the strain gradient increases and the crack propagation slows down. The influence of strength mismatch on the stress triaxiality at the shallow crack front is greater than that at the deep crack front. The interaction between strength mismatch and crack depth directly affects the crack growth direction.

Causes of Early-Age Thermal Cracking of Concrete Foundation Slabs and their Reinforcement to Control the Cracking

NASA Astrophysics Data System (ADS)

Bilčík, Juraj; Sonnenschein, Róbert; Gažovičová, Natália

2017-09-01

This paper focuses on the causes and consequences of early-age cracking of mass concrete foundation slabs due to restrained volume changes. Considering the importance of water leaking through cracks in terms of the serviceability, durability and environmental impact of watertight concrete structures, emphasis is placed on the effect of temperature loads on foundation slabs. Foundation slabs are usually restrained to some degree externally or internally. To evaluate the effect of external restraints on foundation slabs, friction and interaction models are introduced. The reinforcement of concrete cannot prevent the initiation of cracking, but when cracking has occurred, it may act to reduce the spacing and width of cracks. According to EN 1992-1-1, results of calculating crack widths with local variations included in National Annexes (NAs) vary considerably. A comparison of the required reinforcement areas according to different NAs is presented.

Ice damage to concrete

DOT National Transportation Integrated Search

1998-04-01

Concrete is a porous material. When saturated with water and then cooled to below 00C, it cracks internally. Upon repeated freezing and thawing, the cracks grow, interact, and lead eventually to macroscopic degradation, termed ice damage. This report...

Periodic nonlinear waves resulting from the contact interaction of a crack

NASA Astrophysics Data System (ADS)

Lee, Sang Eon; Jin, Suyeong; Hong, Jung-Wuk

2017-09-01

When two different inputs of distinct low and high frequencies are applied to a medium, the linear responses are composed of waves of two dominant frequencies. However, microcracks such as fatigue cracks generate nonlinear waves by modulating the characteristics of the incident waves. Although this phenomenon has been observed and used to detect microcracks, the underlying principles have not been thoroughly elucidated. The hysteresis properties were introduced to describe the nonlinear relationship between the stress and strain to explain these phenomena [Van Den Abeele et al., Res. Nondestruct. Eval. 12, 17 (2000) and Nazarov et al., Acoust. Phys. 49, 344 (2003)]. The generation of harmonics was explained by superimposing stress-strain relations that vary with crack width and excitation magnitude. As the crack depth increases, the ratio of magnitudes of the second harmonic to the first harmonic increases, but the increment becomes smaller [Kawashima et al., Ultrasonics 40, 611 (2002)]. Here, we show that the waves affected by the contact motion of the crack surfaces cultivate the nonlinearity in waveforms, resulting in high frequency off-band signals. With the hypothesis that the clapping of cracks might generate nonlinear components close to the high excitation frequency, we prove that the generation of the high frequency off-band peaks is directly affected by the clapping contact interaction of the crack surfaces. The amount of energy transmitted is closely related to the size of the crack width and the magnitudes of low and high frequency excitations.

Effective properties of a poroelastic medium containing a distribution of aligned cracks

NASA Astrophysics Data System (ADS)

Galvin, R. J.; Gurevich, B.

2009-07-01

We simulate the effect of fractures by considering them to be thin circular cracks in a poroelastic background. Using the solution of the scattering problem for a single-crack and multiple-scattering theory, we estimate the attenuation and dispersion of elastic waves in a porous medium containing a sparse distribution of cracks. When comparing with a similar model, in which multiple-scattering effects are neglected, we find that there is agreement at high frequencies and discrepancies at low frequencies. We conclude that the interaction between cracks should not be neglected at low frequencies, even in the limit of weak crack density. Since the models only agree with each other at high frequencies, when the time available for fluid diffusion is small, we conclude that the interaction between cracks, which is a result of fluid diffusion, is negligible at high frequencies. We also compare our results with a model for spherical inclusions and find that the attenuation for spherical inclusions has exactly the same dependence upon frequency but a difference in magnitude, which depends upon frequency. Since the attenuation curves are very close at low frequencies, we conclude that the effective medium properties are not sensitive to the shape of an inclusion at wavelengths that are large compared with the inclusion size. However, at frequencies such that the wavelength is comparable to or smaller than the inclusion size, the effective properties are sensitive to the greater compliance of the flat cracks, and more attenuation occurs at a given frequency as a result.

High-temperature low cycle fatigue behavior of a gray cast iron

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fan, K.L., E-mail: 12klfan@tongji.edu.cn; He, G.Q.; She, M.

The strain controlled low cycle fatigue properties of the studied gray cast iron for engine cylinder blocks were investigated. At the same total strain amplitude, the low cycle fatigue life of the studied material at 523 K was higher than that at 423 K. The fatigue behavior of the studied material was characterized as cyclic softening at any given total strain amplitude (0.12%–0.24%), which was attributed to fatigue crack initiation and propagation. Moreover, this material exhibited asymmetric hysteresis loops due to the presence of the graphite lamellas. Transmission electron microscopy analysis suggested that cyclic softening was also caused by themore » interactions of dislocations at 423 K, such as cell structure in ferrite, whereas cyclic softening was related to subgrain boundaries and dislocation climbing at 523 K. Micro-analysis of specimen fracture appearance was conducted in order to obtain the fracture characteristics and crack paths for different strain amplitudes. It showed that the higher the temperature, the rougher the crack face of the examined gray cast iron at the same total strain amplitude. Additionally, the microcracks were readily blunted during growth inside the pearlite matrix at 423 K, whereas the microcracks could easily pass through pearlite matrix along with deflection at 523 K. The results of fatigue experiments consistently showed that fatigue damage for the studied material at 423 K was lower than that at 523 K under any given total strain amplitude. - Highlights: • The low cycle fatigue behavior of the HT250 for engine cylinder blocks was investigated. • TEM investigations were conducted to explain the cyclic deformation response. • The low cycle fatigue cracks of HT250 GCI were studied by SEM. • The fatigue life of the examined material at 523 K is higher than that at 423 K.« less

Centerline (longitudinal) joint adhesive performance : two to three-year review.

DOT National Transportation Integrated Search

2009-11-01

This report discusses preliminary evaluations of adhesive use along longitudinal paving : joints on hot mix asphalt pavements to help prevent longitudinal cracking. Seven : pavements where adhesive was applied to the vertical or sloped face of the fi...

75 FR 4482 - Airworthiness Directives; Eurocopter France Model SE3160, SA315B, SA316B, SA316C, and SA319B...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-01-28

... spar by using calipers held against the face of the No. 1 spar in alignment with the through pins. [cir... using calipers held against the face of the No. 1 spar in alignment with the through pins as depicted in..., either a crack, an elongated through pinhole, movement of a through pin, or a through pin that is not...

Mean-field crack networks on desiccated films and their applications: Girl with a Pearl Earring.

PubMed

Flores, J C

2017-02-15

Usual requirements for bulk and fissure energies are considered in obtaining the interdependence among external stress, thickness and area of crack polygons in desiccated films. The average area of crack polygons increases with thickness as a power-law of 4/3. The sequential fragmentation process is characterized by a topological factor related to a scaling finite procedure. Non-sequential overly tensioned (prompt) fragmentation is briefly discussed. Vermeer's painting, Girl with a Pearl Earring, is considered explicitly by using computational image tools and simple experiments and applying the proposed theoretical analysis. In particular, concerning the source of lightened effects on the girl's face, the left/right thickness layer ratio (≈1.34) and the stress ratio (≈1.102) are evaluated. Other master paintings are briefly considered.

Predictions of Poisson's ratio in cross-ply laminates containing matrix cracks and delaminations

NASA Technical Reports Server (NTRS)

Harris, Charles E.; Allen, David H.; Nottorf, Eric W.

1989-01-01

A damage-dependent constitutive model for laminated composites has been developed for the combined damage modes of matrix cracks and delaminations. The model is based on the concept of continuum damage mechanics and uses second-order tensor valued internal state variables to represent each mode of damage. The internal state variables are defined as the local volume average of the relative crack face displacements. Since the local volume for delaminations is specified at the laminate level, the constitutive model takes the form of laminate analysis equations modified by the internal state variables. Model implementation is demonstrated for the laminate engineering modulus E(x) and Poisson's ratio nu(xy) of quasi-isotropic and cross-ply laminates. The model predictions are in close agreement to experimental results obtained for graphite/epoxy laminates.

Analytical and numerical solutions for heat transfer and effective thermal conductivity of cracked media

NASA Astrophysics Data System (ADS)

Tran, A. B.; Vu, M. N.; Nguyen, S. T.; Dong, T. Q.; Le-Nguyen, K.

2018-02-01

This paper presents analytical solutions to heat transfer problems around a crack and derive an adaptive model for effective thermal conductivity of cracked materials based on singular integral equation approach. Potential solution of heat diffusion through two-dimensional cracked media, where crack filled by air behaves as insulator to heat flow, is obtained in a singular integral equation form. It is demonstrated that the temperature field can be described as a function of temperature and rate of heat flow on the boundary and the temperature jump across the cracks. Numerical resolution of this boundary integral equation allows determining heat conduction and effective thermal conductivity of cracked media. Moreover, writing this boundary integral equation for an infinite medium embedding a single crack under a far-field condition allows deriving the closed-form solution of temperature discontinuity on the crack and particularly the closed-form solution of temperature field around the crack. These formulas are then used to establish analytical effective medium estimates. Finally, the comparison between the developed numerical and analytical solutions allows developing an adaptive model for effective thermal conductivity of cracked media. This model takes into account both the interaction between cracks and the percolation threshold.

Stone orientation affects the mechanism of failure in artificial kidney stones subject to shock waves

NASA Astrophysics Data System (ADS)

van Cauwelaert, Javier; Cleveland, Robin O.

2003-10-01

Micro computed tomography (CT) imaging was used to follow the progressive development of cracks in artificial kidney stones. The artificial stones were made from U30 cement with a cylindrical shape (6.5 mm diameter and 8.5 mm long). The stones were held within a polypropylene vial in one of three orientations: vertical, horizontal, and angled at 45 deg. The stones were treated with an electromagnetic lithotripter and the initiation and growth of cracks was observed using microCT. The images show that the orientation of the stones with respect to the shock changes the dominant mechanism for fragmentation. Vertical stones developed a spall-like crack near the distal surface, which propagated from the surface to the interior of the stone. Initiation of a secondary spall-like crack was observed proximal to the first crack. Little surface damage was observed. Horizontal stones presented pitting in the proximal surface and erosion in lateral faces, indicating the action of cavitation. Angled stones presented both spall-like fracture in either the leading or the distal corners and surface damage (pitting) in the proximal surface. Experiments are being performed to follow the development of cracks in human kidney stones. [Work supported by the Whitaker Foundation.

Phase field modeling of crack propagations in fluid-saturated porous media with anisotropic surface energy

NASA Astrophysics Data System (ADS)

Na, S.; Sun, W.; Yoon, H.; Choo, J.

2016-12-01

Directional mechanical properties of layered geomaterials such as shale are important on evaluating the onset and growth of fracture for engineering applications such as hydraulic fracturing, geologic carbon storage, and geothermal recovery. In this study, a continuum phase field modeling is conducted to demonstrate the initiation and pattern of cracks in fluid-saturated porous media. The discontinuity of sharp cracks is formulated using diffusive crack phase field modeling and the anisotropic surface energy is incorporated to account for the directional fracture toughness. In particular, the orientation of bedding in geomaterials with respect to the loading direction is represented by the directional critical energy release rate. Interactions between solid skeleton and fluid are also included to analyze the mechanical behavior of fluid-saturated geologic materials through the coupled hydro-mechanical model. Based on the linear elastic phase field modeling, we also addressed how the plasticity in crack phase field influences the crack patterns by adopting the elasto-plastic model with Drucker-Prager yield criterion. Numerical examples exhibit the features of anisotropic surface energy, the interactions between solid and fluid and the effects of plasticity on crack propagations.Sandia National Laboratories is a multi-program laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under contract DE-AC04-94AL85000.

Concurrent atomistic and continuum simulation of bi-crystal strontium titanate with tilt grain boundary

PubMed Central

Yang, Shengfeng; Chen, Youping

2015-01-01

In this paper, we present the development of a concurrent atomistic–continuum (CAC) methodology for simulation of the grain boundary (GB) structures and their interaction with other defects in ionic materials. Simulation results show that the CAC simulation allows a smooth passage of cracks through the atomistic–continuum interface without the need for additional constitutive rules or special numerical treatment; both the atomic-scale structures and the energies of the four different [001] tilt GBs in bi-crystal strontium titanate obtained by CAC compare well with those obtained by existing experiments and density function theory calculations. Although 98.4% of the degrees of freedom of the simulated atomistic system have been eliminated in a coarsely meshed finite-element region, the CAC results, including the stress–strain responses, the GB–crack interaction mechanisms and the effect of the interaction on the fracture strength, are comparable with that of all-atom molecular dynamics simulation results. In addition, CAC simulation results show that the GB–crack interaction has a significant effect on the fracture behaviour of bi-crystal strontium titanate; not only the misorientation angle but also the atomic-level details of the GB structure influence the effect of the GB on impeding crack propagation. PMID:25792957

Concurrent atomistic and continuum simulation of bi-crystal strontium titanate with tilt grain boundary.

PubMed

Yang, Shengfeng; Chen, Youping

2015-03-08

In this paper, we present the development of a concurrent atomistic-continuum (CAC) methodology for simulation of the grain boundary (GB) structures and their interaction with other defects in ionic materials. Simulation results show that the CAC simulation allows a smooth passage of cracks through the atomistic-continuum interface without the need for additional constitutive rules or special numerical treatment; both the atomic-scale structures and the energies of the four different [001] tilt GBs in bi-crystal strontium titanate obtained by CAC compare well with those obtained by existing experiments and density function theory calculations. Although 98.4% of the degrees of freedom of the simulated atomistic system have been eliminated in a coarsely meshed finite-element region, the CAC results, including the stress-strain responses, the GB-crack interaction mechanisms and the effect of the interaction on the fracture strength, are comparable with that of all-atom molecular dynamics simulation results. In addition, CAC simulation results show that the GB-crack interaction has a significant effect on the fracture behaviour of bi-crystal strontium titanate; not only the misorientation angle but also the atomic-level details of the GB structure influence the effect of the GB on impeding crack propagation.

Healable thermoset polymer composite embedded with stimuli-responsive fibres

PubMed Central

Li, Guoqiang; Meng, Harper; Hu, Jinlian

2012-01-01

Severe wounds in biological systems such as human skin cannot heal themselves, unless they are first stitched together. Healing of macroscopic damage in thermoset polymer composites faces a similar challenge. Stimuli-responsive shape-changing polymeric fibres with outstanding mechanical properties embedded in polymers may be able to close macro-cracks automatically upon stimulation such as heating. Here, a stimuli-responsive fibre (SRF) with outstanding mechanical properties and supercontraction capability was fabricated for the purpose of healing macroscopic damage. The SRFs and thermoplastic particles (TPs) were incorporated into regular thermosetting epoxy for repeatedly healing macroscopic damages. The system works by mimicking self-healing of biological systems such as human skin, close (stitch) then heal, i.e. close the macroscopic crack through the thermal-induced supercontraction of the SRFs, and bond the closed crack through melting and diffusing of TPs at the crack interface. The healing efficiency determined using tapered double-cantilever beam specimens was 94 per cent. The self-healing process was reasonably repeatable. PMID:22896563

Nonlinear acoustic spectroscopy of cracked flaws and disbonds: Fundamentals, techniques, and applications

NASA Astrophysics Data System (ADS)

Maev, R. Gr.; Solodov, I. Yu.

2000-05-01

Classical nonlinear acoustics of solids operates with distributed material nonlinearity related to unharmonicity of molecular interaction forces. Weakening of molecular bonds in a defect area or intermittent lack of elastic coupling between the faces of a vibrating crack or unbond ("clapping") results in anomalously high local contact acoustic nonlinearity (CAN). CAN properties and spectral features are different from those of the classical analog and important to develop new acoustic NDE techniques. Three approaches to nonlinear NDE methodology have been experimentally verified: low-frequency (hundreds of Hz) vibration technique, intermediate-frequency (hundreds of kHz) standing wave and high-frequency (tens of MHz) propagation modes. Low-frequency nonlinear contact vibrations revealed multiple sub- and super-harmonics generation featuring non-monotonous (sinx/x type) spectra. Parametric instability observed in resonator with a nonlinear contact leads to the output spectrum splitting up into successive sub-harmonics as the wave amplitude increases. High-frequency experiments demonstrated abnormal increases in the third harmonic amplitude: 3 or 4 order enhancement of the 3-ω nonlinear parameter was measured for the nonlinear contact. The CAN spectral features in both acoustic and vibration modes were used for nonlinear NDE of simulated and realistic flaws in glass, metal welds, etc. The sensitivities of the techniques are compared and their practical applicability assessed.

A penny shaped crack in a filament-reinforced matrix. 2: The crack problem

NASA Technical Reports Server (NTRS)

Pacella, A. H.; Erdogan, F.

1973-01-01

The elastostatic interaction problem between a penny-shaped crack and a slender inclusion or filament in an elastic matrix was formulated. For a single filament as well as multiple identical filaments located symmetrically around the crack the problem is shown to reduce to a singular integral equation. The solution of the problem is obtained for various geometries and filament-to-matrix stiffness ratios, and the results relating to the angular variation of the stress intensity factor and the maximum filament stress are presented.

Visualization of Lamb Wave Interaction with a 5 mm Fatigue Crack using 1D Ultra High Frequency Laser Doppler Vibrometry

DTIC Science & Technology

2011-09-01

detection of a fatigue crack via 3D LDV measurements, both in aluminum plates. All the referenced LDV/guided wave studies made use of PZT or similar...Figure 1a). (b) (a) (c) Figure 1: (a) Test specimen in MTS fatigue test machine, (b) hole with 5 mm crack, (c) PZT placement with...mm thick aluminum plates with a small (1.59 mm) center hole added to facilitate growth of a fatigue crack. One plate was left undamaged while the

Floating Node Method and Virtual Crack Closure Technique for Modeling Matrix Cracking-Delamination Migration

NASA Technical Reports Server (NTRS)

DeCarvalho, Nelson V.; Chen, B. Y.; Pinho, Silvestre T.; Baiz, P. M.; Ratcliffe, James G.; Tay, T. E.

2013-01-01

A novel approach is proposed for high-fidelity modeling of progressive damage and failure in composite materials that combines the Floating Node Method (FNM) and the Virtual Crack Closure Technique (VCCT) to represent multiple interacting failure mechanisms in a mesh-independent fashion. In this study, the approach is applied to the modeling of delamination migration in cross-ply tape laminates. Delamination, matrix cracking, and migration are all modeled using fracture mechanics based failure and migration criteria. The methodology proposed shows very good qualitative and quantitative agreement with experiments.

Fatigue life prediction modeling for turbine hot section materials

NASA Technical Reports Server (NTRS)

Halford, G. R.; Meyer, T. G.; Nelson, R. S.; Nissley, D. M.; Swanson, G. A.

1989-01-01

A major objective of the fatigue and fracture efforts under the NASA Hot Section Technology (HOST) program was to significantly improve the analytic life prediction tools used by the aeronautical gas turbine engine industry. This was achieved in the areas of high-temperature thermal and mechanical fatigue of bare and coated high-temperature superalloys. The cyclic crack initiation and propagation resistance of nominally isotropic polycrystalline and highly anisotropic single crystal alloys were addressed. Life prediction modeling efforts were devoted to creep-fatigue interaction, oxidation, coatings interactions, multiaxiality of stress-strain states, mean stress effects, cumulative damage, and thermomechanical fatigue. The fatigue crack initiation life models developed to date include the Cyclic Damage Accumulation (CDA) and the Total Strain Version of Strainrange Partitioning (TS-SRP) for nominally isotropic materials, and the Tensile Hysteretic Energy Model for anisotropic superalloys. A fatigue model is being developed based upon the concepts of Path-Independent Integrals (PII) for describing cyclic crack growth under complex nonlinear response at the crack tip due to thermomechanical loading conditions. A micromechanistic oxidation crack extension model was derived. The models are described and discussed.

Fatigue life prediction modeling for turbine hot section materials

NASA Technical Reports Server (NTRS)

Halford, G. R.; Meyer, T. G.; Nelson, R. S.; Nissley, D. M.; Swanson, G. A.

1988-01-01

A major objective of the fatigue and fracture efforts under the Hot Section Technology (HOST) program was to significantly improve the analytic life prediction tools used by the aeronautical gas turbine engine industry. This was achieved in the areas of high-temperature thermal and mechanical fatigue of bare and coated high-temperature superalloys. The cyclic crack initiation and propagation resistance of nominally isotropic polycrystalline and highly anisotropic single crystal alloys were addressed. Life prediction modeling efforts were devoted to creep-fatigue interaction, oxidation, coatings interactions, multiaxiality of stress-strain states, mean stress effects, cumulative damage, and thermomechanical fatigue. The fatigue crack initiation life models developed to date include the Cyclic Damage Accumulation (CDA) and the Total Strain Version of Strainrange Partitioning (TS-SRP) for nominally isotropic materials, and the Tensile Hysteretic Energy Model for anisotropic superalloys. A fatigue model is being developed based upon the concepts of Path-Independent Integrals (PII) for describing cyclic crack growth under complex nonlinear response at the crack tip due to thermomechanical loading conditions. A micromechanistic oxidation crack extension model was derived. The models are described and discussed.

Modeling of heat flow and effective thermal conductivity of fractured media: Analytical and numerical methods

NASA Astrophysics Data System (ADS)

Nguyen, S. T.; Vu, M.-H.; Vu, M. N.; Tang, A. M.

2017-05-01

The present work aims to modeling the thermal conductivity of fractured materials using homogenization-based analytical and pattern-based numerical methods. These materials are considered as a network of cracks distributed inside a solid matrix. Heat flow through such media is perturbed by the crack system. The problem of heat flow across a single crack is firstly investigated. The classical Eshelby's solution, extended to the thermal conduction problem of an ellipsoidal inclusion embedding in an infinite homogeneous matrix, gives an analytical solution of temperature discontinuity across a non-conducting penny-shaped crack. This solution is then validated by the numerical simulation based on the finite elements method. The numerical simulation allows analyzing the effect of crack conductivity. The problem of a single crack is then extended to a medium containing multiple cracks. Analytical estimations for effective thermal conductivity, that take into account the interaction between cracks and their spatial distribution, are developed for the case of non-conducting cracks. Pattern-based numerical method is then employed for both cases non-conducting and conducting cracks. In the case of non-conducting cracks, numerical and analytical methods, both account for the spatial distribution of the cracks, fit perfectly. In the case of conducting cracks, the numerical analyzing of crack conductivity effect shows that highly conducting cracks weakly affect heat flow and the effective thermal conductivity of fractured media.

Durability and life prediction modeling in polyimide composites

NASA Technical Reports Server (NTRS)

Binienda, Wieslaw K.

1995-01-01

Sudden appearance of cracks on a macroscopically smooth surface of brittle materials due to cooling or drying shrinkage is a phenomenon related to many engineering problems. Although conventional strength theories can be used to predict the necessary condition for crack appearance, they are unable to predict crack spacing and depth. On the other hand, fracture mechanics theory can only study the behavior of existing cracks. The theory of crack initiation can be summarized into three conditions, which is a combination of a strength criterion and laws of energy conservation, the average crack spacing and depth can thus be determined. The problem of crack initiation from the surface of an elastic half plane is solved and compares quite well with available experimental evidence. The theory of crack initiation is also applied to concrete pavements. The influence of cracking is modeled by the additional compliance according to Okamura's method. The theoretical prediction by this structural mechanics type of model correlates very well with the field observation. The model may serve as a theoretical foundation for future pavement joint design. The initiation of interactive cracks of quasi-brittle material is studied based on a theory of cohesive crack model. These cracks may grow simultaneously, or some of them may close during certain stages. The concept of crack unloading of cohesive crack model is proposed. The critical behavior (crack bifurcation, maximum loads) of the cohesive crack model are characterized by rate equations. The post-critical behavior of crack initiation is also studied.

In-vitro characterization of stress corrosion cracking of aluminium-free magnesium alloys for temporary bio-implant applications.

PubMed

Choudhary, Lokesh; Singh Raman, R K; Hofstetter, Joelle; Uggowitzer, Peter J

2014-09-01

The complex interaction between physiological stresses and corrosive human body fluid may cause premature failure of metallic biomaterials due to the phenomenon of stress corrosion cracking. In this study, the susceptibility to stress corrosion cracking of biodegradable and aluminium-free magnesium alloys ZX50, WZ21 and WE43 was investigated by slow strain rate tensile testing in a simulated human body fluid. Slow strain rate tensile testing results indicated that each alloy was susceptible to stress corrosion cracking, and this was confirmed by fractographic features of transgranular and/or intergranular cracking. However, the variation in alloy susceptibility to stress corrosion cracking is explained on the basis of their electrochemical and microstructural characteristics. Copyright © 2014 Elsevier B.V. All rights reserved.

Discrete crack growth analysis methodology for through cracks in pressurized fuselage structures

NASA Technical Reports Server (NTRS)

Potyondy, David O.; Wawrzynek, Paul A.; Ingraffea, Anthony R.

1994-01-01

A methodology for simulating the growth of long through cracks in the skin of pressurized aircraft fuselage structures is described. Crack trajectories are allowed to be arbitrary and are computed as part of the simulation. The interaction between the mechanical loads acting on the superstructure and the local structural response near the crack tips is accounted for by employing a hierarchical modeling strategy. The structural response for each cracked configuration is obtained using a geometrically nonlinear shell finite element analysis procedure. Four stress intensity factors, two for membrane behavior and two for bending using Kirchhoff plate theory, are computed using an extension of the modified crack closure integral method. Crack trajectories are determined by applying the maximum tangential stress criterion. Crack growth results in localized mesh deletion, and the deletion regions are remeshed automatically using a newly developed all-quadrilateral meshing algorithm. The effectiveness of the methodology and its applicability to performing practical analyses of realistic structures is demonstrated by simulating curvilinear crack growth in a fuselage panel that is representative of a typical narrow-body aircraft. The predicted crack trajectory and fatigue life compare well with measurements of these same quantities from a full-scale pressurized panel test.

Crack Opening Displacement Behavior in Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Sevener, Kathy; Tracy, Jared; Chen, Zhe; Daly, Sam; Kiser, Doug

2017-01-01

Ceramic Matrix Composites (CMC) modeling and life prediction strongly depend on oxidation, and therefore require a thorough understanding of when matrix cracks occur, the extent of cracking for given conditions (time-temperature-environment-stress), and the interactions of matrix cracks with fibers and interfaces. In this work, the evolution of matrix cracks in a melt-infiltrated Silicon Carbide/Silicon Carbide (SiC/SiC) CMC under uniaxial tension was examined using scanning electron microscopy (SEM) combined with digital image correlation (DIC) and manual crack opening displacement (COD) measurements. Strain relaxation due to matrix cracking, the relationship between COD's and applied stress, and damage evolution at stresses below the proportional limit were assessed. Direct experimental observation of strain relaxation adjacent to regions of matrix cracking is presented and discussed. Additionally, crack openings were found to increase linearly with increasing applied stress, and no crack was found to pass fully through the gage cross-section. This observation is discussed in the context of the assumption of through-cracks for all loading conditions and fiber architectures in oxidation modeling. Finally, the combination of SEM with DIC is demonstrated throughout to be a powerful means for damage identification and quantification in CMC's at stresses well below the proportional limit.

Finite element techniques applied to cracks interacting with selected singularities

NASA Technical Reports Server (NTRS)

Conway, J. C.

1975-01-01

The finite-element method for computing the extensional stress-intensity factor for cracks approaching selected singularities of varied geometry is described. Stress-intensity factors are generated using both displacement and J-integral techniques, and numerical results are compared to those obtained experimentally in a photoelastic investigation. The selected singularities considered are a colinear crack, a circular penetration, and a notched circular penetration. Results indicate that singularities greatly influence the crack-tip stress-intensity factor as the crack approaches the singularity. In addition, the degree of influence can be regulated by varying the overall geometry of the singularity. Local changes in singularity geometry have little effect on the stress-intensity factor for the cases investigated.

A penny-shaped crack in a filament reinforced matrix. 1: The filament model

NASA Technical Reports Server (NTRS)

Erdogan, F.; Pacella, A. H.

1973-01-01

The electrostatic problem of a penny-shaped crack in an elastic matrix which reinforced by filaments or fibers perpendicular to the plane of the crack was studied. The elastic filament model was developed for application to evaluation studies of the stress intensity factor along the periphery of the crack, the stresses in the filaments or fibers, and the interface shear between the matrix and the filaments or fibers. The requirements expected of the model are a sufficiently accurate representation of the filament and applicability to the interaction problems involving a cracked elastic continuum with multi-filament reinforcements. The technique for developing the model and numerical examples of it are shown.

Environmental fatigue of an Al-Li-Cu alloy. Part 2: Microscopic hydrogen cracking processes

NASA Technical Reports Server (NTRS)

Piascik, Robert S.; Gangloff, Richard P.

1992-01-01

Based on a fractographic analysis of fatigue crack propagation (FCP) in Al-Li-Cu alloy 2090 stressed in a variety of inert and embrittling environments, microscopic crack paths are identified and correlated with intrinsic da/dN-delta K kinetics. FCP rates in 2090 are accelerated by hydrogen producing environments (pure water vapor, moist air, and aqueous NaCl), as defined in Part 1. For these cases, subgrain boundary fatigue cracking (SGC) dominates for delta K values where the crack tip process zone, a significant fraction of the cyclic plastic zone, is sufficiently large to envelop 5 micron subgrains in the unrecrystallized microstructure. SGC may be due to strong hydrogen trapping at T1 precipitates concentrated at sub-boundaries. At low delta K, the plastic zone diameter is smaller than the subgrain size and FCP progresses along (100) planes due to either local lattice decohesion or aluminum-lithium hydride cracking. For inert environments (vacuum, helium, and oxygen), or at high delta K where the hydrogen effect on da/dN is small, FCP is along (111) slip planes; this mode does not transition with increasing delta K and plastic zone size. The SGC and (100) crystallographic cracking modes, and the governing influence of the crack tip process zone volume (delta K), support hydrogen embrittlement rather than a surface film rupture and anodic dissolution mechanism for environmental FCP. Multi-sloped log da/dN-log delta K behavior is produced by changes in process zone hydrogen-microstructure interactions, and not by purely micromechanical-microstructure interactions, in contradiction to microstructural distance-based fatigue models.

Creep-fatigue interaction at high temperature; Proceedings of the Symposium, 112th ASME Winter Annual Meeting, Atlanta, GA, Dec. 1-6, 1991

NASA Astrophysics Data System (ADS)

Haritos, George K.; Ochoa, O. O.

Various papers on creep-fatigue interaction at high temperature are presented. Individual topics addressed include: analysis of elevated temperature fatigue crack growth mechanisms in Alloy 718, physically based microcrack propagation laws for creep-fatigue-environment interaction, in situ SEM observation of short fatigue crack growth in Waspaloy at 700 C under cyclic and dwell conditions, evolution of creep-fatigue life prediction models, TMF design considerations in turbine airfoils of advanced turbine engines. Also discussed are: high temperature fatigue life prediction computer code based on the total strain version of strainrange partitioning, atomic theory of thermodynamics of internal variables, geometrically nonlinear analysis of interlaminar stresses in unsymmetrically laminated plates subjected to uniform thermal loading, experimental investigation of creep crack tip deformation using moire interferometry. (For individual items see A93-31336 to A93-31344)

The Quantified Characterization Method of the Micro-Macro Contacts of Three-Dimensional Granular Materials on the Basis of Graph Theory.

PubMed

Guan, Yanpeng; Wang, Enzhi; Liu, Xiaoli; Wang, Sijing; Luan, Hebing

2017-08-03

We have attempted a multiscale and quantified characterization method of the contact in three-dimensional granular material made of spherical particles, particularly in cemented granular material. Particle contact is defined as a type of surface contact with voids in its surroundings, rather than a point contact. Macro contact is a particle contact set satisfying the restrictive condition of a two-dimensional manifold with a boundary. On the basis of graph theory, two dual geometrical systems are abstracted from the granular pack. The face and the face set, which satisfies the two-dimensional manifold with a boundary in the solid cell system, are extracted to characterize the particle contact and the macro contact, respectively. This characterization method is utilized to improve the post-processing in DEM (Discrete Element Method) from a micro perspective to describe the macro effect of the cemented granular material made of spherical particles. Since the crack has the same shape as its corresponding contact, this method is adopted to characterize the crack and realize its visualization. The integral failure route of the sample can be determined by a graph theory algorithm. The contact force is assigned to the weight value of the face characterizing the particle contact. Since the force vectors can be added, the macro contact force can be solved by adding the weight of its corresponding faces.

A penny-shaped crack in a filament-reinforced matrix. I - The filament model. II - The crack problem

NASA Technical Reports Server (NTRS)

Erdogan, F.; Pacella, A. H.

1974-01-01

The study deals with the elastostatic problem of a penny-shaped crack in an elastic matrix which is reinforced by filaments or fibers perpendicular to the plane of the crack. An elastic filament model is first developed, followed by consideration of the application of the model to the penny-shaped crack problem in which the filaments of finite length are asymmetrically distributed around the crack. Since the primary interest is in the application of the results to studies relating to the fracture of fiber or filament-reinforced composites and reinforced concrete, the main emphasis of the study is on the evaluation of the stress intensity factor along the periphery of the crack, the stresses in the filaments or fibers, and the interface shear between the matrix and the filaments or fibers. Using the filament model developed, the elastostatic interaction problem between a penny-shaped crack and a slender inclusion or filament in an elastic matrix is formulated.

Investigation of automated and interactive crack measurement systems : final report, May 27, 2008.

DOT National Transportation Integrated Search

2008-05-27

Currently adopted manual distress surveys involve a high degree of subjectivity, low production rates, and exposure to hazardous conditions. FDOT has acquired and validated a multi-functional survey vehicle (MPSV). However, when an automated crack di...

Thermoelastic analysis of matrix crack growth in particulate composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sridhar, N.; Rickman, J.M.; Srolovitz, D.J.

1995-04-01

The authors examine the conditions under which differences in thermal expansion between a particle and the matrix lead to crack growth within the matrix. Using linear elasticity fracture mechanics, they obtain closed-form, analytical results for the case of a penny shaped crack present in the matrix interacting with a spherical inclusion which is misfitting with respect to the matrix. A simple and direct relationship is established between the strain energy release rate, the crack size, the crack orientation with respect to the inclusion, the crack/inclusion separation, the degree of thermal expansion mismatch and the elastic properties of the medium. Themore » authors also analyze the size to which these cracks can grow and find that for a given misfit strain and material properties, crack growth is inhibited beyond a certain critical crack size. They find that beyond this critical size, the elastic strain energy released upon crack growth is no longer sufficient to compensate for the energy expended in extending the crack, since the crack is growing into the rapidly decreasing stress field. The modification of the above conditions for crack growth due to the superposition of an external stress field has also been analyzed. The preferred orientation of these cracks as a function of misfit strain is predicted. The implication of these results for thermal cycling are analyzed.« less

Robotic End Effectors for Hard-Rock Climbing

NASA Technical Reports Server (NTRS)

Kennedy, Brett; Leger, Patrick

2004-01-01

Special-purpose robot hands (end effectors) now under development are intended to enable robots to traverse cliffs much as human climbers do. Potential applications for robots having this capability include scientific exploration (both on Earth and other rocky bodies in space), military reconnaissance, and outdoor search and rescue operations. Until now, enabling robots to traverse cliffs has been considered too difficult a task because of the perceived need of prohibitively sophisticated planning algorithms as well as end effectors as dexterous as human hands. The present end effectors are being designed to enable robots to attach themselves to typical rock-face features with less planning and simpler end effectors. This advance is based on the emulation of the equipment used by human climbers rather than the emulation of the human hand. Climbing-aid equipment, specifically cams, aid hooks, and cam hooks, are used by sport climbers when a quick ascent of a cliff is desired (see Figure 1). Currently two different end-effector designs have been created. The first, denoted the simple hook emulator, consists of three "fingers" arranged around a central "palm." Each finger emulates the function of a particular type of climbing hook (aid hook, wide cam hook, and a narrow cam hook). These fingers are connected to the palm via a mechanical linkage actuated with a leadscrew/nut. This mechanism allows the fingers to be extended or retracted. The second design, denoted the advanced hook emulator (see Figure 2), shares these features, but it incorporates an aid hook and a cam hook into each finger. The spring-loading of the aid hook allows the passive selection of the type of hook used. The end effectors can be used in several different modes. In the aid-hook mode, the aid hook on one of the fingers locks onto a horizontal ledge while the other two fingers act to stabilize the end effector against the cliff face. In the cam-hook mode, the broad, flat tip of the cam hook is inserted into a non-horizontal crack in the cliff face. A subsequent transfer of weight onto the end effector causes the tip to rotate within the crack, creating a passive, self-locking action of the hook relative to the crack. In the advanced hook emulator, the aid hook is pushed into its retracted position by contact with the cliff face as the cam hook tip is inserted into the crack. When a cliff face contains relatively large pockets or cracks, another type of passive self-locking can be used. Emulating the function of the piece of climbing equipment called a "cam" (note: not the same as a "cam hook"; see Figure 1), the fingers can be fully retracted and the entire end effector inserted into the feature. The fingers are then extended as far as the feature allows. Any weight then transferred to the end effector will tend to extend the fingers further due to frictional force, passively increasing the grip on the feature. In addition to the climbing modes, these end effectors can be used to walk on (either on the palm or the fingertips) and to grasp objects by fully extending the fingers.

Crack-Free, Nondistorting Can For Hot Isostatic Pressing

NASA Technical Reports Server (NTRS)

Juhas, John J.

1991-01-01

New method of canning specimens made of composites of arc-sprayed and plasma-sprayed tape reduces outgassing and warping during hot isostatic pressing. Produces can having reliable, crack-free seal and thereby helps to ensure pressed product of high quality. Specimen placed in ring of refractory metal between two face sheets, also of refractory metal. Assembly placed in die in vacuum hot press, where simultaneously heated and pressed until plates become diffusion-welded to ring, forming sealed can around specimen. Specimen becomes partially densified, and fits snugly within can. Ready for further densification by hot isostatic pressing.

Comparison of Effective Medium Schemes For Seismic Velocities in Cracked Anisotropic Rock

NASA Astrophysics Data System (ADS)

Morshed, S.; Chesnokov, E.

2017-12-01

Understanding of elastic properties of reservoir rock is necessary for meaningful interpretation and analysis of seismic measurements. The elastic properties of a rock are controlled by the microstructural properties such as mineralogical composition, pore and crack distribution, texture and pore connectivity. However, seismic scale is much larger than microstructure scale. Understanding of macroscopic properties at relevant seismic scale (e.g. borehole sonic data) comes from effective medium theory (EMT). However, most of the effective medium theories fail at high crack density as the interactions of strain fields of the cracks can't be ignored. We compare major EMT schemes from low to high crack density. While at low crack density all method gives similar results, at high crack density they differ significantly. Then, we focus on generalized singular approximation (GSA) and effective field (EF) method as they allow cracks beyond the limit of dilute concentrations. Additionally, we use grain contact (GC) method to examine the stiffness constants of the rock matrix. We prepare simple models of a multiphase media containing low to high concentrations of isolated pores. Randomly oriented spherical pores and horizontally oriented ellipsoidal (aspect ratio =0.1) pores have been considered. For isolated spherical pores, all the three methods show exactly same or similar results. However, inclusion interactions are different in different directions in case of horizontal ellipsoidal pores and individual stiffness constants differ greatly from one method to another at different crack density. Stiffness constants remain consistent in GSA method whereas some components become unusual in EF method at a higher crack density (>0.15). Finally, we applied GSA method to interpret ultrasonic velocities of core samples. Mineralogical composition from X-ray diffraction (XRD) data and lab measured porosity data have been utilized. Both compressional and shear wave velocities from GSA method show good fit with the lab measured velocities.

Matrix cracking with irregular fracture fronts as observed in fiber reinforced ceramic composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, K.X.; Yeh, C.P.; Wyatt, K.W.

1998-01-01

As a result of matrix cracking in fiber reinforced composites, fracture planforms assume a wide variation of profiles due to the fact that fiber bridging strongly affects the behavior of local crack fronts. This observation raises the question on the legitimacy of commonly used penny-shaped crack solutions when applied to fiber reinforced composites. Accordingly, investigation of the effects of fracture front profiles on mechanical responses is the thrust of this paper. The authors start with the solution of a penny-shaped crack in a unidirectional, fiber reinforced composite, which demonstrates necessity of considering wavy fracture fronts in fiber reinforced composites. Amore » theoretical framework for fiber reinforced composites with irregular fracture fronts due to matrix cracking is then established via a micromechanics model. The difference between small crack-size matrix cracking and large crack-size matrix cracking is investigated in detail. It is shown that the bridging effect is insignificant when matrix crack size is small and solution of effective property are obtained using Mori-Tanaka`s method by treating cracks and reinforcing fibers as distinct, but interacting phases. When the crack size becomes large, the bridging effects has to be taken into consideration. With bridging tractions obtained in consistency with the micromechanics solution, and corresponding crack energy backed out, the effective properties are obtained through a modification of standard Mori-Tanaka`s treatment of multiphase composites. Analytical solutions show that the generalization of a crack density of a penny-shaped planform is insufficient in describing the effective responses of fiber-reinforced composites with matrix cracking. Approximate solutions that account for the effects of the irregularity of crack planforms are given in closed forms for several irregular crack planforms, including cracks of cross rectangle, polygon and rhombus.« less

Material Characterization for the Analysis of Skin/Stiffener Separation

NASA Technical Reports Server (NTRS)

Davila, Carlos G.; Leone, Frank A.; Song, Kyongchan; Ratcliffe, James G.; Rose, Cheryl A.

2017-01-01

Test results show that separation failure in co-cured skin/stiffener interfaces is characterized by dense networks of interacting cracks and crack path migrations that are not present in standard characterization tests for delamination. These crack networks result in measurable large-scale and sub-ply-scale R curve toughening mechanisms, such as fiber bridging, crack migration, and crack delving. Consequently, a number of unknown issues exist regarding the level of analysis detail that is required for sufficient predictive fidelity. The objective of the present paper is to examine some of the difficulties associated with modeling separation failure in stiffened composite structures. A procedure to characterize the interfacial material properties is proposed and the use of simplified models based on empirical interface properties is evaluated.

Steam Hydrocarbon Cracking and Reforming

ERIC Educational Resources Information Center

Golombok, Michael

2004-01-01

The interactive methods of steam hydrocarbon reforming and cracking of the oil and chemical industries are scrutinized, with special focus on their resemblance and variations. The two methods are illustrations of equilibrium-controlled and kinetically-controlled processes, the analysis of which involves theories, which overlap and balance each…

Investigation of automated and interactive crack measurement systems : final report, May 27, 2008 [summary].

DOT National Transportation Integrated Search

2008-05-01

The use of imaging techniques to evaluate roadway pavements for crack damage has proven to be a safe, rapid, and cost- : effective alternative to traditional highway survey techniques. The Multi-Purpose Survey Vehicle (MPSV) developed by FDOT capture...

Effects of Thermo-Mechanical Treatments on Deformation Behavior and IGSCC Susceptibility of Stainless Steels in Pwr Primary Water Chemistry

NASA Astrophysics Data System (ADS)

Nouraei, S.; Tice, D. R.; Mottershead, K. J.; Wright, D. M.

Field experience of 300 series stainless steels in the primary circuit of PWR plant has been good. Stress Corrosion Cracking of components has been infrequent and mainly associated with contamination by impurities/oxygen in occluded locations. However, some instances of failures have been observed which cannot necessarily be attributed to deviations in the water chemistry. These failures appear to be associated with the presence of cold-work produced by surface finishing and/or by welding-induced shrinkage. Recent data indicate that some heats of SS show an increased susceptibility to SCC; relatively high crack growth rates were observed even when the crack growth direction is orthogonal to the cold-work direction. SCC of cold-worked SS in PWR coolant is therefore determined by a complex interaction of material composition, microstructure, prior cold-work and heat treatment. This paper will focus on the interactions between these parameters on crack propagation in simulated PWR conditions.

Effects of Heating on Teflon(Registered Trademark) FEP Thermal Control Material from the Hubble Space Telescope

NASA Technical Reports Server (NTRS)

deGroh, Kim; Gaier, James R.; Hall, Rachelle L.; Norris, Mary Jo; Espe, Matthew P.; Cato, Daveen R.

1999-01-01

Metallized Teflon(Registered Trademark) FEP (fluorinated ethylene propylene) thermal control material on the Hubble Space Telescope (HST) is degrading in the space environment. Teflon(Registered Trademark) FEP thermal control blankets (space-facing FEP) retrieved during the first servicing mission (SM1) were found to be embrittled on solar facing surfaces and contained microscopic cracks. During the second servicing mission (SM2) astronauts noticed that the FEP outer layer of the multi-layer insulation (MLI) covering the telescope was cracked in many locations around the telescope. Large cracks were observed on the light shield, forward shell and equipment bays. A tightly curled piece of cracked FEP from the light shield was retrieved during SM2 and was severely embrittled, as witnessed by ground testing. A Failure Review Board (FRB) was organized to determine the mechanism causing the MLI degradation. Density, x-ray crystallinity and solid state nuclear magnetic resonance (NMR) analyses of FEP retrieved during SM1 were inconsistent with results of FEP retrieved during SM2. Because the retrieved SM2 material curled while in space, it experienced a higher temperature extreme during thermal cycling, estimated at 200 C, than the SM1 material, estimated at 50 C. An investigation on the effects of heating pristine and FEP exposed on HST was therefore conducted. Samples of pristine. SM1, and SM2 FEP were heated to 200 C and evaluated for changes in density and morphology. Elevated temperature exposure was found to have a major impact on the density of the retrieved materials. Characterization of polymer morphology of as-received and heated FEP samples by NMR provided results that were consistent with the density results. These findings have provided insight to the damage mechanisms of FEP in the space environment.

Kinetics of bed fracturing around mine workings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Veksler, Yu.A.

1988-03-01

A failure of the bed near the walls of the workings of a mine away from the face occurs gradually over time and in this paper the authors take a kinetic approach to evaluating its development. The influence of certain mine engineering factors on the pattern of bed fracturing is discussed. The effect of the depth of mining is shown. Cracking occurs in the portion of the seam at the face near the ground at some distance from it on the interface between soft and hard coal. The density of the fractured rocks and their response affect the bed fracturingmore » near the stope face.« less

Three-dimensional piezoelectric boundary elements

NASA Astrophysics Data System (ADS)

Hill, Lisa Renee

The strong coupling between mechanical and electrical fields in piezoelectric ceramics makes them appropriate for use as actuation devices; as a result, they are an important part of the emerging technologies of smart materials and structures. These piezoceramics are very brittle and susceptible to fracture, especially under the severe loading conditions which may occur in service. A significant portion of the applications under investigation involve dynamic loading conditions. Once a crack is initiated in the piezoelectric medium, the mechanical and electrical fields can act to drive the crack growth. Failure of the actuator can result from a catastrophic fracture event or from the cumulative effects of cyclic fatigue. The presence of these cracks, or other types of material defects, alter the mechanical and electrical fields inside the body. Specifically, concentrations of stress and electric field are present near a flaw and can lead to material yielding or localized depoling, which in turn can affect the sensor/actuator performance or cause failure. Understanding these effects is critical to the success of these smart structures. The complex coupling behavior and the anisotropy of the material makes the use of numerical methods necessary for all but the simplest problems. To this end, a three-dimensional boundary element method program is developed to evaluate the effect of flaws on these piezoelectric materials. The program is based on the linear governing equations of piezoelectricity and relies on a numerically evaluated Green's function for solution. The boundary element method was selected as the evaluation tool due to its ability to model the interior domain exactly. Thus, for piezoelectric materials the coupling between mechanical and electrical fields is not approximated inside the body. Holes in infinite and finite piezoceramics are investigated, with the localized stresses and electric fields clearly developed. The accuracy of the piezoelectric boundary element method is demonstrated with two problems: a two-dimensional circular void and a three-dimensional spherical cavity, both inside infinite solids. Application of the program to a finite body with a centered, spherical void illustrates the complex nature of the mechanical and electrical coupling. Mode I fracture is also examined, combining the linear boundary element solution with the modified crack closure integral to determine strain energy release rates. Experimental research has shown that the strain, rather than the total, energy release rate is a better predictor of crack growth in piezoelectric materials. Solutions for a two-dimensional slit-like crack and for three-dimensional penny and elliptical cracks are presented. These solutions are developed using the insulated crack face electrical boundary condition. Although this boundary condition is used by most researchers, recent discussion indicates that it may not be an accurate model for the slender crack geometry. The boundary element method is used with the penny crack problem to investigate the effect of different electrical boundary conditions on the strain energy release rate. Use of a conductive crack face boundary condition, rather than an insulated one, acts to increase the strain energy release rate for the penny crack. These conductive strain energies are closer to the values determined using a permeable electrical boundary condition than to the original conductive boundary condition ones. It is shown that conclusions about structural integrity are strongly dependent on the choice of boundary conditions.

Crack Growth Analysis for Arbitrary Spectrum Loading. Volume 1. Results and Discussion

DTIC Science & Technology

1974-10-01

amplitude growth without previous load history effects) the crack growth increments were increased. Many of the specimens were fitted with the Amsler...absolute magnitude of the maximum load.) Further, if S is defined as a function of the previous load history , then c h9 Equation (19) will predict...crack growth interaction effects. It remains then, to define S as a function of stress ratio and previous load history , and anyc other pertinent

Two dimensional modeling of elastic wave propagation in solids containing cracks with rough surfaces and friction - Part I: Theoretical background.

PubMed

Aleshin, Vladislav; Delrue, Steven; Trifonov, Andrey; Bou Matar, Olivier; Van Den Abeele, Koen

2018-01-01

Our study aims at the creation of a numerical toolbox that describes wave propagation in samples containing internal contacts (e.g. cracks, delaminations, debondings, imperfect intergranular joints) of known geometry with postulated contact interaction laws including friction. The code consists of two entities: the contact model and the solid mechanics module. Part I of the paper concerns the modeling of internal contacts (called cracks for brevity), while part II is related to the integration of the developed contact model into a solid mechanics module that allows the description of wave propagation processes. The contact model is used to produce normal and tangential load-displacement relationships, which in turn are used by the solid mechanics module as boundary conditions at the internal contacts. Due to friction, the tangential reaction curve is hysteretic and memory-dependent. In addition, it depends on the normal reaction curve. An essential feature of the proposed contact model is that it takes into account the roughness of the contact faces. On one hand, accounting for roughness makes the contact model more complicated since it gives rise to a partial slip regime when some parts on the contact area experience slip and some do not. On the other hand, as we will show, the concept of contact surfaces covered by asperities receding under load makes it possible to formulate a consistent contact model that provides nonlinear load-displacement relationships for any value of the drive displacements and their histories. This is a strong advantage, since this way, the displacement-driven model allows for a simple explicit procedure of data exchange with the solid mechanics module, while more traditional flat-surface contacts driven by loads generate a complex iterative procedure. More specifically, the proposed contact model is based on the previously developed method of memory diagrams that allows one to automatically obtain memory-dependent solutions to frictional contact problems in the particular case of partial slip. Here we extend the solution onto cases of total sliding and contact loss which is possible while using the displacement-driven formulation. The method requires the knowledge of the normal contact response obtained in our case as a result of statistical consideration of roughness of contact faces. Copyright © 2017 Elsevier B.V. All rights reserved.

Crack deflection in brittle media with heterogeneous interfaces and its application in shale fracking

NASA Astrophysics Data System (ADS)

Zeng, Xiaguang; Wei, Yujie

Driven by the rapid progress in exploiting unconventional energy resources such as shale gas, there is growing interest in hydraulic fracture of brittle yet heterogeneous shales. In particular, how hydraulic cracks interact with natural weak zones in sedimentary rocks to form permeable cracking networks is of significance in engineering practice. Such a process is typically influenced by crack deflection, material anisotropy, crack-surface friction, crustal stresses, and so on. In this work, we extend the He-Hutchinson theory (He and Hutchinson, 1989) to give the closed-form formulae of the strain energy release rate of a hydraulic crack with arbitrary angles with respect to the crustal stress. The critical conditions in which the hydraulic crack deflects into weak interfaces and exhibits a dependence on crack-surface friction and crustal stress anisotropy are given in explicit formulae. We reveal analytically that, with increasing pressure, hydraulic fracture in shales may sequentially undergo friction locking, mode II fracture, and mixed mode fracture. Mode II fracture dominates the hydraulic fracturing process and the impinging angle between the hydraulic crack and the weak interface is the determining factor that accounts for crack deflection; the lower friction coefficient between cracked planes and the greater crustal stress difference favor hydraulic fracturing. In addition to shale fracking, the analytical solution of crack deflection could be used in failure analysis of other brittle media.

Perceptions of parental bonding in freebase cocaine users versus non-illicit drug users

PubMed Central

Pettenon, Márcia; Kessler, Felix Henrique Paim; Guimarães, Luciano S. P.; Pedroso, Rosemeri Siqueira; Hauck, Simone; Pechansky, Flavio

2014-01-01

Background & objectives: Evidence has suggested that parenting styles have peculiar characteristics in families with drug-related issues. This study was undertaken to investigate the perception of crack (smoke cocaine) users and non-users about parental bonding quality regarding care and control in Brazil. Methods: A total of 198 hospitalized crack users and 104 users of any non-illicit drug were assessed using the Parental Bonding Instrument (PBI), the sixth version of the Addiction Severity Index (ASI) and Mini International Neuropsychiatric Interview (MINI). Results: Adjusted logistic regression analysis showed that crack users were more likely (ORadj = 9.68; 95% CI: 2.82, 33.20) to perceive neglectful mothers, as well as more likely (ORadj = 4.71, 95% CI: 2.17, 10.22) to perceive controlling and affectionless fathers in comparison with non-illicit drug users who were more likely to perceive optimal parenting. Interpretation & conclusions: Our findings indicate that the perception of neglectful mothers and affectionless controlling fathers may be associated with the tendency of the children to be less resilient when facing stressful events, leading them to a greater risk to use crack. PMID:25109717

Chemistry and petrography of calcite in the KTB pilot borehole, Bavarian Oberpfalz, Germany

USGS Publications Warehouse

Komor, S.C.

1995-01-01

The KTB pilot borehole in northeast Bavaria, Germany, penetrates 4000 m of gneiss, amphibolite, and subordinate calc-silicate, lamprophyre and metagabbro. There are three types of calcite in the drilled section: 1) metamorphic calcite in calc-silicate and marble; 2) crack-filling calcite in all lithologies; and 3) replacement calcite in altered minerals. Crack-filling and replacement calcite postdate metamorphic calcite. Multiple calcite generations in individual cracks suggest that different generations of water repeatedly flowed through the same cracks. Crack-filling mineral assemblages that include calcite originally formed at temperatures of 150-350??C. Presently, crack-filling calcite is in chemical and isotopic equilibrium with saline to brackish water in the borehole at temperatures of ???120??C. The saline to brackish water contains a significant proportion of meteoric water. Re-equilibration of crack-filling calcite to lower temperatures means that calcite chemistry tells us little about water-rock interactions in the crystal section of temperatures higher than ~120??C. -from Author

Anomolous Fatigue Crack Growth Phenomena in High-Strength Steel

NASA Technical Reports Server (NTRS)

Forth, Scott C.; James, Mark A.; Johnston, William M., Jr.; Newman, James C., Jr.

2004-01-01

The growth of a fatigue crack through a material is the result of a complex interaction between the applied loading, component geometry, three-dimensional constraint, load history, environment, material microstructure and several other factors. Previous studies have developed experimental and computational methods to relate the fatigue crack growth rate to many of the above conditions, with the intent of discovering some fundamental material response, i.e. crack growth rate as a function of something. Currently, the technical community uses the stress intensity factor solution as a simplistic means to relate fatigue crack growth rate to loading, geometry and all other variables. The stress intensity factor solution is a very simple linear-elastic representation of the continuum mechanics portion of crack growth. In this paper, the authors present fatigue crack growth rate data for two different high strength steel alloys generated using standard methods. The steels exhibit behaviour that appears unexplainable, compared to an aluminium alloy presented as a baseline for comparison, using the stress intensity factor solution.

Investigation of growth features in several hydraulic fractures

NASA Astrophysics Data System (ADS)

Bykov, Alexander; Galybin, Alexander; Evdokimov, Alexander; Zavialova, Natalia; Zavialov, Ivan; Negodiaev, Sergey; Perepechkin, Ilia

2017-04-01

In this paper we simulate the growth of three or more interacting hydraulic fractures in the horizontal well with a cross flow of fluid between them. Calculation of the dynamics of cracks is performed in three dimensional space. The computation of the movement of fracturing fluid with proppant is performed in the two-dimensional space (the flow was averaged along crack aperture). For determining the hydraulic pipe resistance coefficient we used a generalization of the Reynolds number for fluids with power rheology and a generalization of the von Karman equation made by Dodge and Meiner. The calculations showed that the first crack was developing faster than the rest in homogeneous medium. During the steady loading the outer cracks pinch the inner cracks and it was shown that only the first and last fracture develop in extreme case. It is also possible to simulate the parameters at which the two developing outer cracks pinch the central one in the horizontal direction. In this case, the central crack may grow in the vertical direction.

Damage Tolerant Analysis of Cracked Al 2024-T3 Panels repaired with Single Boron/Epoxy Patch

NASA Astrophysics Data System (ADS)

Mahajan, Akshay D.; Murthy, A. Ramachandra; Nanda Kumar, M. R.; Gopinath, Smitha

2018-06-01

It is known that damage tolerant analysis has two objectives, namely, remaining life prediction and residual strength evaluation. To achieve the these objectives, determination of accurate and reliable fracture parameter is very important. XFEM methodologies for fatigue and fracture analysis of cracked aluminium panels repaired with different patch shapes made of single boron/epoxy have been developed. Heaviside and asymptotic crack tip enrichment functions are employed to model the crack. XFEM formulations such as displacement field formulation and element stiffness matrix formulation are presented. Domain form of interaction integral is employed to determine Stress Intensity Factor of repaired cracked panels. Computed SIFs are incorporated in Paris crack growth model to predict the remaining fatigue life. The residual strength has been computed by using the remaining life approach, which accounts for both crack growth constants and no. of cycles to failure. From the various studies conducted, it is observed that repaired panels have significant effect on reduction of the SIF at the crack tip and hence residual strength as well as remaining life of the patched cracked panels are improved significantly. The predicted remaining life and residual strength will be useful for design of structures/components under fatigue loading.

Numerical simulation of evaluation of surface breaking cracks by array-lasers generated narrow-band SAW

NASA Astrophysics Data System (ADS)

Dong, Li-Ming; Ni, Chen-Yin; Shen, Zhong-Hua; Ni, Xiao-Wu

2011-09-01

Most of the factors limiting the extensive application of laser-based ultrasonic for nondestructive evaluation of surface breaking crack are its poor sensitivity, low efficiency relative to conventional contact ultrasonic methods and limit on the dimension of the cracks. For this reason, a new technique that multiplepulse narrow-band ultrasound generated by laser arrays has been proposed. It is found that crack detection dependent on spectrum of narrow-band ultrasound generated by laser arrays can be operated with low amplitude requirements. In this paper, the narrow-band ultrasound generated by pulse laser arrays interacting with surface breaking cracks has been simulated in detail by the finite element method (FEM) according to the thermoelastic theory. The pulsed array lasers were assumed to be transient heat source, and the surface acoustic wave (SAW) which propagating on the top of the plate was computed based on thermoelastic theory. Then the frequency spectrums of both reflected waves by crack and transmission ones through crack were compared with the direct waves. Results demonstrate that multiple-frequency components of the narrow-band ultrasound were varied with change of the depth of surface breaking cracks significantly, which provides the possibility for precise evaluation of surface breaking cracks.

Effect of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate. [for aerospace applications

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1984-01-01

The effects of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate at frequencies of 1 Hz and 10 Hz were investigated. Twenty-five mm thick compact specimens were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Fatigue crack growth rates were calculated from effective crack lengths determined using a compliance method. Tests were conducted in hard vacuum and at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. Fatigue crack growth rates were frequency insensitive under all environment conditions tested. For constant stress intensity factor ranges crack growth rate transitions occurred at low and high water vapor pressures. Crack growth rates at intermediate pressures were relatively constant and showed reasonable agreement with published data for two Al-Cu-Mg alloys. The existence of two crack growth rate transitions suggests either a change in rate controlling kinetics or a change in corrosion fatigue mechanism as a function of water vapor pressure. Reduced residual deformation and transverse cracking specimens tested in water vapor versus vacuum may be evidence of embrittlement within the plastic zone due to environmental interaction.

The effect of water vapor on fatigue crack Growth in 7475-t651 aluminum alloy plate. [for aerospace applications

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1982-01-01

The effects of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate at frequencies of 1 Hz and 10 Hz were investigated. Twenty-five mm thick compact specimens were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Fatigue crack growth rates were calculated from effective crack lengths determined using a compliance method. Tests were conducted in hard vacuum and at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. Fatigue crack growth rates were frequency insensitive under all environment conditions tested. For constant stress intensity factor ranges crack growth rate transitions occurred at low and high water vapor pressures. Crack growth rates at intermediate pressures were relatively constant and showed reasonable agreement with published data for two Al-Cu-Mg alloys. The existence of two crack growth rate transitions suggests either a change in rate controlling kinetics or a change in corrosion fatigue mechanism as a function of water vapor pressure. Reduced residual deformation and transverse cracking specimens tested in water vapor versus vacuum may be evidence of embrittlement within the plastic zone due to environmental interaction.

A risk assessment method for multi-site damage

NASA Astrophysics Data System (ADS)

Millwater, Harry Russell, Jr.

This research focused on developing probabilistic methods suitable for computing small probabilities of failure, e.g., 10sp{-6}, of structures subject to multi-site damage (MSD). MSD is defined as the simultaneous development of fatigue cracks at multiple sites in the same structural element such that the fatigue cracks may coalesce to form one large crack. MSD is modeled as an array of collinear cracks with random initial crack lengths with the centers of the initial cracks spaced uniformly apart. The data used was chosen to be representative of aluminum structures. The structure is considered failed whenever any two adjacent cracks link up. A fatigue computer model is developed that can accurately and efficiently grow a collinear array of arbitrary length cracks from initial size until failure. An algorithm is developed to compute the stress intensity factors of all cracks considering all interaction effects. The probability of failure of two to 100 cracks is studied. Lower bounds on the probability of failure are developed based upon the probability of the largest crack exceeding a critical crack size. The critical crack size is based on the initial crack size that will grow across the ligament when the neighboring crack has zero length. The probability is evaluated using extreme value theory. An upper bound is based on the probability of the maximum sum of initial cracks being greater than a critical crack size. A weakest link sampling approach is developed that can accurately and efficiently compute small probabilities of failure. This methodology is based on predicting the weakest link, i.e., the two cracks to link up first, for a realization of initial crack sizes, and computing the cycles-to-failure using these two cracks. Criteria to determine the weakest link are discussed. Probability results using the weakest link sampling method are compared to Monte Carlo-based benchmark results. The results indicate that very small probabilities can be computed accurately in a few minutes using a Hewlett-Packard workstation.

Shock-induced Plasticity and Brittle Cracks in Aluminum Nitride

NASA Astrophysics Data System (ADS)

Branicio, Paulo; Kalia, Rajiv

2005-03-01

Two hundred and nine million atom molecular-dynamics simulation of hypervelocity projectile impact in aluminum nitride reveals strong interplay between shock-induced structural phase transformation, plastic deformation and brittle cracks. The shock wave splits into an elastic precursor and a wurtzite-to-rocksalt structural transformation wave. When the elastic wave reflected from the boundary of the sample interacts with the transformation wave front, nanocavities are generated along the penetration path of the projectile and dislocations in adjacent regions. The nanocavities coalesce to form mode I brittle cracks while dislocations generate kink bands that give rise to mode II cracks. These simulations provide a microscopic view of defects associated with simultaneous tensile and shear cracking at the structural phase transformation boundary due to shock impact in high-strength ceramics.

Effect of Ply Orientation and Crack Location on SIFs in Finite Multilayers with Aligned Cracks

NASA Astrophysics Data System (ADS)

Chen, Linfeng; Pindera, Marek-Jerzy

2008-02-01

An exact elasticity solution is presented for arbitrarily laminated finite multilayers in a state of generalized plane deformation under horizontally pinned end constraints that are weakened by aligned cracks. Based on half-range Fourier series and the local/global stiffness matrix approach, the mixed boundary-value problem is reduced to Cauchy-type singular integral equations in the unknown displacement discontinuities. Solution to these equations is obtained using the approach developed by Erdogan and co-workers. Numerical results quantify the thus-far undocumented geometric and material effects on Mode I, II and III stress intensity factors in composite multilayers with interacting cracks under uniform vertical displacement. These effects include finite dimensions, crack location, material anisotropy due to a unidirectional fiber-reinforced layer/s orientation, and orientational grading.

A test procedure for determining the influence of stress ratio on fatigue crack growth

NASA Technical Reports Server (NTRS)

Fitzgerald, J. H.; Wei, R. P.

1974-01-01

A test procedure is outlined by which the rate of fatigue crack growth over a range of stress ratios and stress intensities can be determined expeditiously using a small number of specimens. This procedure was developed to avoid or circumvent the effects of load interactions on fatigue crack growth, and was used to develop data on a mill annealed Ti-6Al-4V alloy plate. Experimental data suggest that the rates of fatigue crack growth among the various stress ratios may be correlated in terms of an effective stress intensity range at given values of K max. This procedure is not to be used, however, for determining the corrosion fatigue crack growth characteristics of alloys when nonsteady-state effects are significant.

Environmental fatigue of an Al-Li-Cu alloy. Part 3: Modeling of crack tip hydrogen damage

NASA Technical Reports Server (NTRS)

Piascik, Robert S.; Gangloff, Richard P.

1992-01-01

Environmental fatigue crack propagation rates and microscopic damage modes in Al-Li-Cu alloy 2090 (Parts 1 and 2) are described by a crack tip process zone model based on hydrogen embrittlement. Da/dN sub ENV equates to discontinuous crack advance over a distance, delta a, determined by dislocation transport of dissolved hydrogen at plastic strains above a critical value; and to the number of load cycles, delta N, required to hydrogenate process zone trap sites that fracture according to a local hydrogen concentration-tensile stress criterion. Transgranular (100) cracking occurs for process zones smaller than the subgrain size, and due to lattice decohesion or hydride formation. Intersubgranular cracking dominates when the process zone encompasses one or more subgrains so that dislocation transport provides hydrogen to strong boundary trapping sites. Multi-sloped log da/dN-log delta K behavior is produced by process zone plastic strain-hydrogen-microstructure interactions, and is determined by the DK dependent rates and proportions of each parallel cracking mode. Absolute values of the exponents and the preexponential coefficients are not predictable; however, fractographic measurements theta sub i coupled with fatigue crack propagation data for alloy 2090 established that the process zone model correctly describes fatigue crack propagation kinetics. Crack surface films hinder hydrogen uptake and reduce da/dN and alter the proportions of each fatigue crack propagation mode.

Finite element analysis of end notch flexure specimen

NASA Technical Reports Server (NTRS)

Mall, S.; Kochhar, N. K.

1986-01-01

A finite element analysis of the end notch flexure specimen for mode II interlaminar fracture toughness measurement was conducted. The effect of friction between the crack faces and large deflection on the evaluation of G sub IIc from this specimen were investigated. Results of this study are presented in this paper.

Finite-element analysis of end-notch flexure specimens

NASA Technical Reports Server (NTRS)

Mall, S.; Kochhar, N. K.

1986-01-01

A finite-element analysis of the end-notch flexure specimen for Mode II interlaminar fracture toughness measurement was conducted. The effects of friction between the crack faces and large deflection on the evaluation of G(IIc) from this specimen were investigated. Results of this study are presented in this paper.

77 FR 36143 - Airworthiness Directives; The Boeing Company Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2012-06-18

... this AD within the compliance times specified, unless already done. (g) Repetitive Eddy Current High... the Federal Register on January 19, 2012 (77 FR 2664). That NPRM proposed to require repetitive eddy current high frequency (ETHF) inspections for cracks on the aft face on the left and right rib hinge...

Neonatal face-to-face interactions promote later social behaviour in infant rhesus monkeys

PubMed Central

Dettmer, Amanda M.; Kaburu, Stefano S. K.; Simpson, Elizabeth A.; Paukner, Annika; Sclafani, Valentina; Byers, Kristen L.; Murphy, Ashley M.; Miller, Michelle; Marquez, Neal; Miller, Grace M.; Suomi, Stephen J.; Ferrari, Pier F.

2016-01-01

In primates, including humans, mothers engage in face-to-face interactions with their infants, with frequencies varying both within and across species. However, the impact of this variation in face-to-face interactions on infant social development is unclear. Here we report that infant monkeys (Macaca mulatta) who engaged in more neonatal face-to-face interactions with mothers have increased social interactions at 2 and 5 months. In a controlled experiment, we show that this effect is not due to physical contact alone: monkeys randomly assigned to receive additional neonatal face-to-face interactions (mutual gaze and intermittent lip-smacking) with human caregivers display increased social interest at 2 months, compared with monkeys who received only additional handling. These studies suggest that face-to-face interactions from birth promote young primate social interest and competency. PMID:27300086

Time lapse photography as an approach to understanding glide avalanche activity

USGS Publications Warehouse

Hendrikx, Jordy; Peitzsch, Erich H.; Fagre, Daniel B.

2012-01-01

Avalanches resulting from glide cracks are notoriously difficult to forecast, but are a recurring problem for numerous avalanche forecasting programs. In some cases glide cracks are observed to open and then melt away in situ. In other cases, they open and then fail catastrophically as large, full-depth avalanches. Our understanding and management of these phenomena are currently limited. It is thought that an increase in the rate of snow gliding occurs prior to full-depth avalanche activity so frequent observation of glide crack movement can provide an index of instability. During spring 2011 in Glacier National Park, Montana, USA, we began an approach to track glide crack avalanche activity using a time-lapse camera focused on a southwest facing glide crack. This crack melted in-situ without failing as a glide avalanche, while other nearby glide cracks on north through southeast aspects failed. In spring 2012, a camera was aimed at a large and productive glide crack adjacent to the Going to the Sun Road. We captured three unique glide events in the field of view. Unfortunately, all of them either failed very quickly, or during periods of obscured view, so measurements of glide rate could not be obtained. However, we compared the hourly meteorological variables during the period of glide activity to the same variables prior to glide activity. The variables air temperature, relative humidity, air pressure, incoming and reflected long wave radiation, SWE, total precipitation, and snow depth were found to be statistically different for our cases examined. We propose that these are some of the potential precursors for glide avalanche activity, but do urge caution in their use, due to the simple approach and small data set size. It is hoped that by introducing a workable method to easily record glide crack movement, combined with ongoing analysis of the associated meteorological data, we will improve our understanding of when, or if, glide avalanche activity will ensue.

Phase Transformation Induced Self-Healing Behavior of Al-Ag Alloy.

PubMed

Michalcová, Alena; Marek, Ivo; Knaislová, Anna; Sofer, Zdeněk; Vojtěch, Dalibor

2018-01-27

Self-healing alloys are promising materials that can decrease the consequences of accidents. To detect crack formation in a material is simple task that can be performed by e.g., sonic or ultrasound detection, but it is not always possible to immediately replace the damaged parts. In this situation, it is very advantageous to have the chance to heal the crack during operation, which can be done e.g., by annealing. In this paper, self-healing behavior was proven by TEM (Transmission electron microscope) observation of crack healing after annealing. The crack was observed in the rapidly solidified Al-30Ag alloy with non-equilibrium phase composition formed by a minor amount of Ag₂Al and a supersaturated solid solution of Ag in an fcc-Al matrix (fcc = face centered cubic). After annealing at 450 °C, equilibrium phase composition was obtained by forming a higher amount of Ag₂Al. This phase transformation did not allow the crack to be healed. Subsequent annealing at 550 °C caused recrystallization to a supersaturated solid solution of Ag in fcc-Al, followed by a return to the mixture of fcc-Al and Ag₂Al by cooling, and this process was accompanied by the closing of the crack. This observation proved the self-healing possibilities of the Ag₂Al phase. Practical application of this self-healing behavior could be achieved through the dispersion of fine Ag₂Al particles in a structural material, which will enrich the material with self-healing properties.

Quantitative Assessment of Fatigue Damage Accumulation in Wavy Slip Metals from Acoustic Harmonic Generation

NASA Technical Reports Server (NTRS)

Cantrell, John H.

2006-01-01

A comprehensive, analytical treatment is presented of the microelastic-plastic nonlinearities resulting from the interaction of a stress perturbation with dislocation substructures (veins and persistent slip bands) and cracks that evolve during high-cycle fatigue of wavy slip metals. The nonlinear interaction is quantified by a material (acoustic) nonlinearity parameter beta extracted from acoustic harmonic generation measurements. The contribution to beta from the substructures is obtained from the analysis of Cantrell [Cantrell, J. H., 2004, Proc. R. Soc. London A, 460, 757]. The contribution to beta from cracks is obtained by applying the Paris law for crack propagation to the Nazarov-Sutin crack nonlinearity equation [Nazarov, V. E., and Sutin, A. M., 1997, J. Acoust. Soc. Am. 102, 3349]. The nonlinearity parameter resulting from the two contributions is predicted to increase monotonically by hundreds of percent during fatigue from the virgin state to fracture. The increase in beta during the first 80-90 percent of fatigue life is dominated by the evolution of dislocation substructures, while the last 10-20 percent is dominated by crack growth. The model is applied to the fatigue of aluminium alloy 2024-T4 in stress-controlled loading at 276MPa for which experimental data are reported. The agreement between theory and experiment is excellent.

Face Sheet/Core Disbond Growth in Honeycomb Sandwich Panels Subjected to Ground-Air-Ground Pressurization and In-Plane Loading

NASA Technical Reports Server (NTRS)

Chen, Zhi M.; Krueger, Ronald; Rinker, Martin

2015-01-01

Typical damage modes in light honeycomb sandwich structures include face sheet/core disbonding and core fracture, both of which can pose a threat to the structural integrity of a component. These damage modes are of particular interest to aviation certification authorities since several in-service occurrences, such as rudder structural failure and other control surface malfunctions, have been attributed to face sheet/core disbonding. Extensive studies have shown that face sheet/core disbonding and core fracture can lead to damage propagation caused by internal pressure changes in the core. The increasing use of composite sandwich construction in aircraft applications makes it vitally important to understand the effect of ground-air-ground (GAG) cycles and conditions such as maneuver and gust loads on face sheet/core disbonding. The objective of the present study was to use a fracture mechanics based approach developed earlier to evaluate the loading at the disbond front caused by ground-air-ground pressurization and in-plane loading. A honeycomb sandwich panel containing a circular disbond at one face sheet/core interface was modeled with three-dimensional (3D) solid finite elements. The disbond was modeled as a discrete discontinuity and the strain energy release rate along the disbond front was computed using the Virtual Crack Closure Technique (VCCT). Special attention was paid to the pressure-deformation coupling which can decrease the pressure load within the disbonded sandwich section significantly when the structure is highly deformed. The commercial finite element analysis software, Abaqus/Standard, was used for the analyses. The recursive pressure-deformation coupling problem was solved by representing the entrapped air in the honeycomb cells as filled cavities in Abaqus/Standard. The results show that disbond size, face sheet thickness and core thickness are important parameters that determine crack tip loading at the disbond front. Further, the pressure-deformation coupling was found to have an important load decreasing effect [6]. In this paper, a detailed problem description is provided first. Second, the analysis methodology is presented. The fracture mechanics approach used is described and the specifics of the finite element model, including the fluid-filled cavities, are introduced. Third, the initial model verification and validation are discussed. Fourth, the findings from a closely related earlier study [6] are summarized. These findings provided the basis for the current investigation. Fifth, an aircraft ascent scenario from 0 to 12192 m (0 to 40000 ft) is considered and the resulting crack tip loading at the disbond front is determined. In-plane loading to simulate maneuvers and gust conditions are also considered. Sixth, the results are shown for a curved panel, which was used to simulate potential fuselage applications. Finally, a brief summary of observations is presented and recommendations for improvement are provided.

Second harmonic generation at fatigue cracks by low-frequency Lamb waves: Experimental and numerical studies

NASA Astrophysics Data System (ADS)

Yang, Yi; Ng, Ching-Tai; Kotousov, Andrei; Sohn, Hoon; Lim, Hyung Jin

2018-01-01

This paper presents experimental and theoretical analyses of the second harmonic generation due to non-linear interaction of Lamb waves with a fatigue crack. Three-dimensional (3D) finite element (FE) simulations and experimental studies are carried out to provide physical insight into the mechanism of second harmonic generation. The results demonstrate that the 3D FE simulations can provide a reasonable prediction on the second harmonic generated due to the contact nonlinearity at the fatigue crack. The effect of the wave modes on the second harmonic generation is also investigated in detail. It is found that the magnitude of the second harmonic induced by the interaction of the fundamental symmetric mode (S0) of Lamb wave with the fatigue crack is much higher than that by the fundamental anti-symmetric mode (A0) of Lamb wave. In addition, a series of parametric studies using 3D FE simulations are conducted to investigate the effect of the fatigue crack length to incident wave wavelength ratio, and the influence of the excitation frequency on the second harmonic generation. The outcomes show that the magnitude and directivity pattern of the generated second harmonic depend on the fatigue crack length to incident wave wavelength ratio as well as the ratio of S0 to A0 incident Lamb wave amplitude. In summary, the findings of this study can further advance the use of second harmonic generation in damage detection.

Effect of reinforcement morphology on matrix microcracking

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sridhar, N.; Srolovitz, D.J.; Rickman, J.M.

1996-03-01

The authors quantitatively examine the conditions under which a particle matrix misfit leads to matrix crack growth as a function of inclusion shape. Such misfit stresses and cracks can be generated by thermal expansion mismatch, generated by cooling a brittle matrix containing ductile inclusions. Using fracture mechanics and perturbation theory, they analyze the case of a penny-shaped crack interacting with a misfitting spheroidal inclusion. A simple and direct relationship is established between the strain energy release rate and the physical and geometrical properties of the system including: the thermal expansion mismatch, temperature change, the crack and inclusion sizes, the elasticmore » properties of the medium and the shape of the inclusion. In particular, the effects of inclusion shape on the stress intensity factors and strain energy release rate are analytically determined for nearly spherical inclusions. The authors use this information to determine the minimum crack size for crack growth to occur and the maximum size to which cracks may grown. The maximum crack size corresponds to the case where the elastic strain energy released upon crack growth is no longer sufficient to compensate for energy expended in extending the crack as the crack is growing into the rapidly decreasing stress field. The authors employ a nominally exact numerical procedure to study the effects of whiskers and platelets (i.e. spheroids very different from spheres) on matrix cracking. It is found that upon cooling a composite containing ductile inclusions, the propensity for matrix cracking is maximized for reinforcement shapes close to that of a sphere.« less

Penny-shaped crack in a fiber-reinforced matrix. [elastostatics

NASA Technical Reports Server (NTRS)

Narayanan, T. V.; Erdogan, F.

1974-01-01

Using a slender inclusion model developed earlier, the elastostatic interaction problem between a penny-shaped crack and elastic fibers in an elastic matrix is formulated. For a single set and for multiple sets of fibers oriented perpendicularly to the plane of the crack and distributed symmetrically on concentric circles, the problem was reduced to a system of singular integral equations. Techniques for the regularization and for the numerical solution of the system are outlined. For various fiber geometries numerical examples are given, and distribution of the stress intensity factor along the crack border was obtained. Sample results showing the distribution of the fiber stress and a measure of the fiber-matrix interface shear are also included.

Penny-shaped crack in a fiber-reinforced matrix

NASA Technical Reports Server (NTRS)

Narayanan, T. V.; Erdogan, F.

1975-01-01

Using the slender inclusion model developed earlier the elastostatic interaction problem between a penny-shaped crack and elastic fibers in an elastic matrix is formulated. For a single set and for multiple sets of fibers oriented perpendicularly to the plane of the crack and distributed symmetrically on concentric circles the problem is reduced to a system of singular integral equations. Techniques for the regularization and for the numerical solution of the system are outlined. For various fiber geometries numerical examples are given and distribution of the stress intensity factor along the crack border is obtained. Sample results showing the distribution of the fiber stress and a measure of the fiber-matrix interface shear are also included.

Nonlinear Response of Thin Cylindrical Shells with Longitudinal Cracks and Subjected to Internal Pressure and Axial compression Loads

NASA Technical Reports Server (NTRS)

Starnes, James H.; Rose, Cheryl A.

1998-01-01

The results of an analytical study of the nonlinear response of a thin unstiffened aluminum cylindrical shell with a longitudinal crack are presented. The shell is analyzed with a nonlinear shell analysis code that maintains the shell in a nonlinear equilibrium state while the crack is grown. The analysis accurately accounts for global and local structural response phenomena. Results are presented for internal pressure, axial compression, and combined internal pressure and axial compression loads. The effects of varying crack length on the nonlinear response of the shell subjected to internal pressure are described. The effects of varying crack length on the prebuckling, buckling and postbuckling responses of the shell subjected to axial compression, and subjected to combined internal pressure and axial compression are also described. The results indicate that the nonlinear interaction between the in-plane stress resultants and the out-of-plane displacements near a crack can significantly affect the structural response of the shell. The results also indicate that crack growth instabilities and shell buckling instabilities can both affect the response of the shell as the crack length is increased.

Nonlinear Response and Residual Strength of Damaged Stiffened Shells Subjected to Combined Loads

NASA Technical Reports Server (NTRS)

Starnes, James H., Jr.; Britt, Vicki O.; Rose, Cheryl A.; Rankin, Charles C.

1996-01-01

The results of an analytical study of the nonlinear response of stiffened fuselage shells with long cracks are presented. The shells are modeled with a hierarchical modeling strategy and analyzed with a nonlinear shell analysis code that maintains the shell in a nonlinear equilibrium state while the crack is grown. The analysis accurately accounts for global and local structural response phenomena. Fuselage skins, frames stringers and failsafe straps are included in the models. Results are presented for various combinations of internal pressure and mechanical bending, vertical shear and torsion loads, and the effects of crack orientation and location on the shell response are described. These results indicate that the nonlinear interaction between the in-plane stress resultants and the out-of-plane displacements near a crack can significantly affect the structural response of the shell, and the stress-intensity factors associated with a crack that are used to predict residual strength. The effects of representative combined loading conditions on the stress-intensity factors associated with a crack are presented. The effects of varying structural parameters on the stress-intensity factors associated with a crack, and on self-similar and non-self-similar crack-growth are also presented.

Guided wave crack detection and size estimation in stiffened structures

NASA Astrophysics Data System (ADS)

Bhuiyan, Md Yeasin; Faisal Haider, Mohammad; Poddar, Banibrata; Giurgiutiu, Victor

2018-03-01

Structural health monitoring (SHM) and nondestructive evaluation (NDE) deals with the nondestructive inspection of defects, corrosion, leaks in engineering structures by using ultrasonic guided waves. In the past, simplistic structures were often considered for analyzing the guided wave interaction with the defects. In this study, we focused on more realistic and relatively complicated structure for detecting any defect by using a non-contact sensing approach. A plate with a stiffener was considered for analyzing the guided wave interactions. Piezoelectric wafer active transducers were used to produce excitation in the structures. The excitation generated the multimodal guided waves (aka Lamb waves) that propagate in the plate with stiffener. The presence of stiffener in the plate generated scattered waves. The direct wave and the additional scattered waves from the stiffener were experimentally recorded and studied. These waves were considered as a pristine case in this research. A fine horizontal semi-circular crack was manufactured by using electric discharge machining in the same stiffener. The presence of crack in the stiffener produces additional scattered waves as well as trapped waves. These scattered waves and trapped wave modes from the cracked stiffener were experimentally measured by using a scanning laser Doppler vibrometer (SLDV). These waves were analyzed and compared with that from the pristine case. The analyses suggested that both size and shape of the horizontal crack may be predicted from the pattern of the scattered waves. Different features (reflection, transmission, and mode-conversion) of the scattered wave signals are analyzed. We found direct transmission feature for incident A0 wave mode and modeconversion feature for incident S0 mode are most suitable for detecting the crack in the stiffener. The reflection feature may give a better idea of sizing the crack.

Review on stress corrosion and corrosion fatigue failure of centrifugal compressor impeller

NASA Astrophysics Data System (ADS)

Sun, Jiao; Chen, Songying; Qu, Yanpeng; Li, Jianfeng

2015-03-01

Corrosion failure, especially stress corrosion cracking and corrosion fatigue, is the main cause of centrifugal compressor impeller failure. And it is concealed and destructive. This paper summarizes the main theories of stress corrosion cracking and corrosion fatigue and its latest developments, and it also points out that existing stress corrosion cracking theories can be reduced to the anodic dissolution (AD), the hydrogen-induced cracking (HIC), and the combined AD and HIC mechanisms. The corrosion behavior and the mechanism of corrosion fatigue in the crack propagation stage are similar to stress corrosion cracking. The effects of stress ratio, loading frequency, and corrosive medium on the corrosion fatigue crack propagation rate are analyzed and summarized. The corrosion behavior and the mechanism of stress corrosion cracking and corrosion fatigue in corrosive environments, which contain sulfide, chlorides, and carbonate, are analyzed. The working environments of the centrifugal compressor impeller show the behavior and the mechanism of stress corrosion cracking and corrosion fatigue in different corrosive environments. The current research methods for centrifugal compressor impeller corrosion failure are analyzed. Physical analysis, numerical simulation, and the fluid-structure interaction method play an increasingly important role in the research on impeller deformation and stress distribution caused by the joint action of aerodynamic load and centrifugal load.

Kinetic studies of the stress corrosion cracking of D6AC steel

NASA Technical Reports Server (NTRS)

Noronha, P. J.

1975-01-01

The effect of load interactions on the crack growth velocity of D6AC steel under stress corrosion cracking conditions was determined. The environment was a 3.5 percent salt solution. The modified-wedge opening load specimens were fatigue precracked and subjected to a deadweight loading in creep machines. The effects of load shedding on incubation times and crack growth rates were measured using high-sensitivity compliance measurement techniques. Load shedding results in an incubation time, the length of which depends on the amount of load shed and the baseline stress intensity. The sequence of unloading the specimen also controls the subsequent incubation period. The incubation period is shorter when load shedding passes through zero load than when it does not if the specimen initially had the same baseline stress intensity. The crack growth rates following the incubation period are also different from the steady-state crack growth rate at the operating stress intensity. These data show that the susceptibility of this alloy system to stress corrosion cracking depends on the plane-strain fracture toughness and on the yield strength of the material.

Effect of strain wave shape on low-cycle fatigue crack propagation of SUS 304 stainless steel at elevated temperatures

NASA Astrophysics Data System (ADS)

Okazaki, Masakazu; Hattori, Ichiro; Shiraiwa, Fujio; Koizumi, Takashi

1983-08-01

Effect of strain wave shape on strain-controlled low-cycle fatigue crack propagation of SUS 304 stainless steel was investigated at 600 and 700 °C. It was found that the rate of crack propagation in a cycle-dependent region was successfully correlated with the range of cyclic J-integral, Δ Jf, regardless of the strain wave shape, frequency, and test temperature. It was also shown that the rate of crack propagation gradually increased from cycle-dependent curve to time-dependent one with decreasing frequency and slow-fast strain wave shape, and that one of the factors governing the rate of crack propagation in such a region was the ratio of the range of creep J-integral to that of total J-integral, Δ J c/Δ JT. Based on the results thus obtained, an interaction damage rule proposed semi-empirically was interpreted, with regard to crack propagation. Furthermore, fatigue crack initiation mechanism in slow-fast strain wave shape was studied, and it was shown that grain boundary sliding took an important role in it.

Crack Growth Prediction Methodology for Multi-Site Damage: Layered Analysis and Growth During Plasticity

NASA Technical Reports Server (NTRS)

James, Mark Anthony

1999-01-01

A finite element program has been developed to perform quasi-static, elastic-plastic crack growth simulations. The model provides a general framework for mixed-mode I/II elastic-plastic fracture analysis using small strain assumptions and plane stress, plane strain, and axisymmetric finite elements. Cracks are modeled explicitly in the mesh. As the cracks propagate, automatic remeshing algorithms delete the mesh local to the crack tip, extend the crack, and build a new mesh around the new tip. State variable mapping algorithms transfer stresses and displacements from the old mesh to the new mesh. The von Mises material model is implemented in the context of a non-linear Newton solution scheme. The fracture criterion is the critical crack tip opening displacement, and crack direction is predicted by the maximum tensile stress criterion at the crack tip. The implementation can accommodate multiple curving and interacting cracks. An additional fracture algorithm based on nodal release can be used to simulate fracture along a horizontal plane of symmetry. A core of plane strain elements can be used with the nodal release algorithm to simulate the triaxial state of stress near the crack tip. Verification and validation studies compare analysis results with experimental data and published three-dimensional analysis results. Fracture predictions using nodal release for compact tension, middle-crack tension, and multi-site damage test specimens produced accurate results for residual strength and link-up loads. Curving crack predictions using remeshing/mapping were compared with experimental data for an Arcan mixed-mode specimen. Loading angles from 0 degrees to 90 degrees were analyzed. The maximum tensile stress criterion was able to predict the crack direction and path for all loading angles in which the material failed in tension. Residual strength was also accurately predicted for these cases.

Crack Turning in Integrally Stiffened Aircraft Structures

NASA Technical Reports Server (NTRS)

Pettit, Richard Glen

2000-01-01

Current emphasis in the aircraft industry toward reducing manufacturing cost has created a renewed interest in integrally stiffened structures. Crack turning has been identified as an approach to improve the damage tolerance and fail-safety of this class of structures. A desired behavior is for skin cracks to turn before reaching a stiffener, instead of growing straight through. A crack in a pressurized fuselage encounters high T-stress as it nears the stiffener--a condition favorable to crack turning. Also, the tear resistance of aluminum alloys typically varies with crack orientation, a form of anisotropy that can influence the crack path. The present work addresses these issues with a study of crack turning in two-dimensions, including the effects of both T-stress and fracture anisotropy. Both effects are shown to have relation to the process zone size, an interaction that is central to this study. Following an introduction to the problem, the T-stress effect is studied for a slightly curved semi-infinite crack with a cohesive process zone, yielding a closed form expression for the future crack path in an infinite medium. For a given initial crack tip curvature and tensile T-stress, the crack path instability is found to increase with process zone size. Fracture orthotropy is treated using a simple function to interpolate between the two principal fracture resistance values in two-dimensions. An extension to three-dimensions interpolates between the six principal values of fracture resistance. Also discussed is the transition between mode I and mode II fracture in metals. For isotropic materials, there is evidence that the crack seeks out a direction of either local symmetry (pure mode I) or local asymmetry (pure mode II) growth. For orthotropic materials the favored states are not pure modal, and have mode mixity that is a function of crack orientation.

A Comparison of Single-Cycle Versus Multiple-Cycle Proof Testing Strategies

NASA Technical Reports Server (NTRS)

McClung, R. C.; Chell, G. G.; Millwater, H. R.; Russell, D. A.; Millwater, H. R.

1999-01-01

Single-cycle and multiple-cycle proof testing (SCPT and MCPT) strategies for reusable aerospace propulsion system components are critically evaluated and compared from a rigorous elastic-plastic fracture mechanics perspective. Earlier MCPT studies are briefly reviewed. New J-integral estimation methods for semielliptical surface cracks and cracks at notches are derived and validated. Engineering methods are developed to characterize crack growth rates during elastic-plastic fatigue crack growth (FCG) and the tear-fatigue interaction near instability. Surface crack growth experiments are conducted with Inconel 718 to characterize tearing resistance, FCG under small-scale yielding and elastic-plastic conditions, and crack growth during simulated MCPT. Fractography and acoustic emission studies provide additional insight. The relative merits of SCPT and MCPT are directly compared using a probabilistic analysis linked with an elastic-plastic crack growth computer code. The conditional probability of failure in service is computed for a population of components that have survived a previous proof test, based on an assumed distribution of initial crack depths. Parameter studies investigate the influence of proof factor, tearing resistance, crack shape, initial crack depth distribution, and notches on the MCPT versus SCPT comparison. The parameter studies provide a rational basis to formulate conclusions about the relative advantages and disadvantages of SCPT and MCPT. Practical engineering guidelines are proposed to help select the optimum proof test protocol in a given application.

A Comparison of Single-Cycle Versus Multiple-Cycle Proof Testing Strategies

NASA Technical Reports Server (NTRS)

McClung, R. C.; Chell, G. G.; Millwater, H. R.; Russell, D. A.; Orient, G. E.

1996-01-01

Single-cycle and multiple-cycle proof testing (SCPT and MCPT) strategies for reusable aerospace propulsion system components are critically evaluated and compared from a rigorous elastic-plastic fracture mechanics perspective. Earlier MCPT studies are briefly reviewed. New J-integral estimation methods for semi-elliptical surface cracks and cracks at notches are derived and validated. Engineering methods are developed to characterize crack growth rates during elastic-plastic fatigue crack growth (FCG) and the tear-fatigue interaction near instability. Surface crack growth experiments are conducted with Inconel 718 to characterize tearing resistance, FCG under small-scale yielding and elastic-plastic conditions, and crack growth during simulated MCPT. Fractography and acoustic emission studies provide additional insight. The relative merits of SCPT and MCPT are directly compared using a probabilistic analysis linked with an elastic-plastic crack growth computer code. The conditional probability of failure in service is computed for a population of components that have survived a previous proof test, based on an assumed distribution of initial crack depths. Parameter studies investigate the influence of proof factor, tearing resistance, crack shape, initial crack depth distribution, and notches on the MCPT vs. SCPT comparison. The parameter studies provide a rational basis to formulate conclusions about the relative advantages and disadvantages of SCPT and MCPT. Practical engineering guidelines are proposed to help select the optimum proof test protocol in a given application.

Suppressing Crack Formation in Particulate Systems by Utilizing Capillary Forces

PubMed Central

Schneider, Monica; Maurath, Johannes; Fischer, Steffen B.; Weiß, Moritz; Willenbacher, Norbert; Koos, Erin

2017-01-01

Cracks, formed during the drying of particulate films, can reduce the effectiveness or even render products useless. We present a novel, generic approach to suppress crack formation in thin films made from hard particle suspensions, which are otherwise highly susceptible to cracking, using the capillary force between particles present when a trace amount of an immiscible liquid is added to a suspension. This secondary liquid preserves the particle cohesion, modifying the structure and increasing the drying rate. Crack-free films can be produced at thicknesses much greater than the critical cracking thickness for a suspension without capillary interactions, and even persists after sintering. This capillary suspension strategy is applicable to a broad range of materials including suspensions of metals, semiconductive and ceramic oxides or glassy polymeric particles and can be easily implemented in many industrial processes since it is based on well-established unit operations. Promising fields of application include ceramic foils and printed electronic devices. PMID:28263554

Mechanical properties and crack growth behavior of polycrystalline copper using molecular dynamics simulation

NASA Astrophysics Data System (ADS)

Qiu, Ren-Zheng; Li, Chi-Chen; Fang, Te-Hua

2017-08-01

This study investigated the mechanical properties and crack propagation behavior of polycrystalline copper using a molecular dynamics simulation. The effects of temperature, grain size, and crack length were evaluated in terms of atomic trajectories, slip vectors, common neighbor analysis, the material’s stress-strain diagram and Young’s modulus. The simulation results show that the grain boundary of the material is more easily damaged at high temperatures and that grain boundaries will combine at the crack tip. From the stress-strain diagram, it was observed that the maximum stress increased as the temperature decreased. In contrast, the maximum stress was reduced by increasing the temperature. With regard to the effect of the grain size, when the grain size was too small, the structure of the sample deformed due to the effect of atomic interactions, which caused the grain boundary structure to be disordered in general. However, when the grain size was larger, dislocations appeared and began to move from the tip of the crack, which led to a new dislocation phenomenon. With regards to the effect of the crack length, the tip of the crack did not affect the sample’s material when the crack length was less than 5 nm. However, when the crack length was above 7.5 nm, the grain boundary was damaged, and twinning structures and dislocations appeared on both sides of the crack tip. This is because the tip of the crack was blunt at first before sharpening due to the dislocation effect.

Fatigue crack growth in an aluminum alloy-fractographic study

NASA Astrophysics Data System (ADS)

Salam, I.; Muhammad, W.; Ejaz, N.

2016-08-01

A two-fold approach was adopted to understand the fatigue crack growth process in an Aluminum alloy; fatigue crack growth test of samples and analysis of fractured surfaces. Fatigue crack growth tests were conducted on middle tension M(T) samples prepared from an Aluminum alloy cylinder. The tests were conducted under constant amplitude loading at R ratio 0.1. The stress applied was from 20,30 and 40 per cent of the yield stress of the material. The fatigue crack growth data was recorded. After fatigue testing, the samples were subjected to detailed scanning electron microscopic (SEM) analysis. The resulting fracture surfaces were subjected to qualitative and quantitative fractographic examinations. Quantitative fracture analysis included an estimation of crack growth rate (CGR) in different regions. The effect of the microstructural features on fatigue crack growth was examined. It was observed that in stage II (crack growth region), the failure mode changes from intergranular to transgranular as the stress level increases. In the region of intergranular failure the localized brittle failure was observed and fatigue striations are difficult to reveal. However, in the region of transgranular failure the crack path is independent of the microstructural features. In this region, localized ductile failure mode was observed and well defined fatigue striations were present in the wake of fatigue crack. The effect of interaction of growing fatigue crack with microstructural features was not substantial. The final fracture (stage III) was ductile in all the cases.

Facebook and MySpace: complement or substitute for face-to-face interaction?

PubMed

Kujath, Carlyne L

2011-01-01

Previous studies have claimed that social-networking sites are used as a substitute for face-to-face interaction, resulting in deteriorating relationship quality and decreased intimacy among its users. The present study hypothesized that this type of communication is not a substitute for face-to-face interaction; rather, that it is an extension of communication with face-to-face partners. A survey was administered to examine the use of Facebook and MySpace in this regard among 183 college students. The study confirmed that Facebook and MySpace do act as an extension of face-to-face interaction, but that some users do tend to rely on Facebook and MySpace for interpersonal communication more than face-to-face interaction.

Nonlinear fracture mechanics-based analysis of thin wall cylinders

NASA Technical Reports Server (NTRS)

Brust, Frederick W.; Leis, Brian N.; Forte, Thomas P.

1994-01-01

This paper presents a simple analysis technique to predict the crack initiation, growth, and rupture of large-radius, R, to thickness, t, ratio (thin wall) cylinders. The method is formulated to deal both with stable tearing as well as fatigue mechanisms in applications to both surface and through-wall axial cracks, including interacting surface cracks. The method can also account for time-dependent effects. Validation of the model is provided by comparisons of predictions to more than forty full scale experiments of thin wall cylinders pressurized to failure.

Thermodynamic analysis on the role of hydrogen in anodic stress corrosion cracking

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qiao, L.; Mao, X.

1995-11-01

A synergistic effect of hydrogen and stress on a corrosion rate was analyzed with thermodynamics. The results showed that an interaction of stress and hydrogen could increase the corrosion rate remarkably. Stress corrosion cracking (SCC) of austenitic stainless steel (ASS) was investigated in boiling chloride solution to confirm the analysis. Hydrogen could be introduced into the specimen concentrated at the crack tip during SCC in boiling LiCl solution (143 C). The concentrating factor is about 3 which is consistent with calculated results according to stress induced diffusion.

Electron Beam Welding of Gear Wheels by Splitted Beam

NASA Astrophysics Data System (ADS)

Dřímal, Daniel

2014-06-01

This contribution deals with the issue of electron beam welding of high-accurate gear wheels composed of a spur gearing and fluted shaft joined with a face weld for automotive industry. Both parts made of the high-strength low-alloy steel are welded in the condition after final machining and heat treatment, performed by case hardening, whereas it is required that the run-out in the critical point of weldment after welding, i. e. after the final operation, would be 0.04 mm max.. In case of common welding procedure, cracks were formed in the weld, initiated by spiking in the weld root. Crack formation was prevented by the use of an interlocking joint with a rounded recess and suitable welding parameters, eliminating crack initiation by spiking in the weld root. Minimisation of the welding distortions was achieved by the application of tack welding with simultaneous splitting of one beam into two parts in the opposite sections of circumferential face weld attained on the principle of a new system of controlled deflection with digital scanning of the beam. This welding procedure assured that the weldment temperature after welding would not be higher than 400 °C. Thus, this procedure allowed achieving the final run-outs in the critical point of gearwheels within the maximum range up to 0.04 mm, which is acceptable for the given application. Accurate optical measurements did not reveal any changes in the teeth dimensions.

The Influence of Hydrogen on the Evolving Microstructure During Fatigue Crack Growth in Metastable and Stable Austenitic Stainless Steels

NASA Astrophysics Data System (ADS)

Nygren, Kelly Elizabeth

The effect of high levels of internal hydrogen on the microstructure evolving during stage II fatigue crack growth was investigated through a series of tensile and fatigue studies in metastable (304) and stable (316, 316L) stainless steels. The first, a tensile study in 304 stainless steel, identified the underlying microstructure which resulted in the flat and quasi-cleavage features on the fracture surface of a hydrogen-charged tensile bar. The second study utilized single-edge notched tensile specimens loaded in fatigue, and compared the evolving microstructure ahead of a fatigue crack for cases of an uncharged, 10 wppm hydrogen-charged, and 104 wppm hydrogen-charged 304 and 316L alloy. The final fatigue study, a small fatigue crack growth study in round bars of 304 and 316, provided a contextual comparison of microstructures to previous results in literature. In the metastable 304 stainless steel, hydrogen is found to change the nature of the martensitic transformation and subsequent fracture path. This transformation is attributed to enhanced plasticity and hydrogen-dislocation interactions stabilizing the austenitic matrix and confining slip to particular close-packed planes. The martensite acts as a fast diffusion pathway for hydrogen, leading to final fracture along martensitic laths or cleavage planes. In 316L, the material deforms via slip and twinning and hydrogen does not induce a change in deformation mechanisms. Instead, the enhanced plasticity and hydrogen-dislocation interactions increase the degree of plasticity, leading to smaller dislocation cell sizes with thicker walls before the onset of twinning. The crack interacts with a heavily twinned structure superimposed on dislocation cells, resulting in a curvature of one twin-variant in the direction of crack growth and the formation of a refined region at the fracture surface. These structures are localized to the crack surface and limited in rotation in the presence of hydrogen. The presence of a hydrogen content above the solution-limit led to a strengthening effect over all other samples in the round bar samples for both 304 and 316. In the SENT studies, 304 stainless steel charged to these levels showed the greatest degree of hydrogen embrittlement, while in 316L stainless steel, the samples containing these levels of hydrogen were found to be stronger in fatigue life than the 10 wppm hydrogen-charged sample. Both of the 316L hydrogen-charged samples were weaker than their uncharged counterpart. Differences in the outcomes for the two studies was attributed to the geometry and testing condition employed. When strengthening was observed, the role of hydrogen was resolved to be two-fold: hydrogen hardens the matrix in the lattice, suppressing the process zone at the crack; and hydrogen at the dislocations enhances the plasticity experienced in the region where the material is yielding ahead of crack advance in the strain lobe. Irrespective of material class, increasing stress-state on the crack within the same stage of fatigue life leads to an increase in depth of the refinement layer and level of plasticity. The refinement at the surface can be attributed to the dislocation emission created during crack advance and the deformation induced in the crack wake. The former is the primary contributor to the SENT specimen studies, while the latter is responsible for the differences observed in the round-bar studies. In 316L, when the twin structure was observed to extend to the surface, regions of light and dark contrast were observed between the twinning bundle variants which corresponded to the peaks and troughs of the striations. This observation is counter to the current understanding that striations form during the crack advance process, independently of the evolved microstructure. The resulting microstructures in all hydrogen-induced studies are discussed in terms of the impact of hydrogen-dislocation interactions and enhanced plasticity. The evolving microstructure and unique observation of striations conforming to the microstructure developed ahead of crack advance emphasize the need to revisit how fatigue models are approached. Although a challenge, models must be informed by plasticity based arguments incorporating the deformation mechanisms observed in experiments to accurately reflect fatigue crack growth.

Library Management Tips that Work

ERIC Educational Resources Information Center

Smallwood, Carol, Ed.

2011-01-01

There's no shortage of library management books out there--but how many of them actually tackle the little details of day-to-day management, the hard-to-categorize things that slip through the cracks of a larger handbook? "Library Management Tips that Work" does exactly that, addressing dozens of such issues facing library managers, including: (1)…

Adhesion strength of norbornene-based self-healing agents to an amine-cured epoxy

NASA Astrophysics Data System (ADS)

Huang, Guang Chun; Lee, Jong Keun; Kessler, Michael R.; Yoon, Sungho

2009-07-01

Self-healing is triggered by crack propagation through embedded microcapsules in an epoxy matrix, which then release the liquid healing agent into the crack plane. Subsequent exposure of the healing agent to the chemical catalyst initiates ring-opening metathesis polymerization (ROMP) and bonding of the crack faces. In order to improve self-healing functionality, it is necessary to enhance adhesion of polymerized healing agent within the crack to the matrix resin. In this study, shear bond strength between different norbornene-based healing agents and an amine-cured epoxy resin was evaluated using the single lap shear test method (ASTM D3163, modified). The healing agents tested include endodicyclopentadiene (endo-DCPD), 5-ethylidene-2-norbornene (ENB) and DCPD/ENB blends. 5-Norbornene-2-methanol (NBM) was used as an adhesion promoter, containing hydroxyl groups to form hydrogen bonds with the amine-cured epoxy. A custom synthesized norbornene-based crosslinking agent was also added to improve adhesion for ENB by increasing the crosslinking density of the adhesive after ROMP. The healing agents were polymerized with varying loadings of the 1st generation Grubbs' catalyst at different reaction times and temperatures.

Rock falls from Glacier Point above Camp Curry, Yosemite National Park, California

USGS Publications Warehouse

Wieczorek, Gerald F.; Snyder, James B.

1999-01-01

A series of rock falls from the north face of Glacier Point above Camp Curry, Yosemite National Park, California, have caused reexamination of the rock-fall hazard because beginning in June, 1999 a system of cracks propagated through a nearby rock mass outlining a future potential rock fall. If the estimated volume of the potential rock fall fails as a single piece, there could be a risk from rock-fall impact and airborne rock debris to cabins in Camp Curry. The role of joint plane orientation and groundwater pressure in the fractured rock mass are discussed in light of the pattern of developing cracks and potential modes of failure.

Actual light deflections in regions of crack tips and their influence on measurements in photomechanics

NASA Astrophysics Data System (ADS)

Hecker, Friedrich W.; Pindera, Jerzy T.; Wen, Baicheng

Crack-tip photomechanics procedures are based on certain simplifying assumptions that are seldom discussed. In a recent paper the theoretical bases of the shadow optical methods of caustics have been analysed and tested using the results obtained by three analytical-experimental procedures, namely classical strain gage techniques, isodynes, and strain-gradient index method. It has been concluded that the straing-radient index method appears to be a suitable tool for analysis of stress states near crack tips and notches and, in particular, for testing the predictive power of the pertinent singular solutions of the linear elastic fracture mechanics and the ranges of their applicability. In the present paper, a more detailed analysis of all results obtained in light deflection experiments allows to quantify the contribution of both involved effects and to determine the distortion of the faces of the investigated plates along their crack planes. The ability of the strain-gradient light bending method to analyse some features of the three-dimensional stress-state is reported. Finally, the presented experimental evidence allows to draw conclusions related to limits of applicability of certain photomechanical measurements near crack tips. An extensive summary of this paper is published in the Proceedings of the Second International Conference on Photomechanics and Speckle Metrology, Vol. 1554A, part of SPIE's 1991 International Symposium on Optical Applied Science and Engineering, 22-26 July 1991, San Diego, CA, USA. 1

Curvature in solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Li, Wenxia; Hasinska, Kathy; Seabaugh, Matt; Swartz, Scott; Lannutti, John

At this point in history, curvature is inherent to the laminated components that comprise solid oxide fuel cells (SOFCs). Surprisingly, however, this fact has never been previously quantified in the literature. In addition, potential curvature changes associated with NiO reduction and re-oxidation during operation have not been investigated. In this report, an optical profilometer was employed to non-destructively quantify the surface curvature or cracking behavior observed on a large scale in industrially manufactured cells. This provides insights into the challenges that the component materials face as well as additional appreciation for why, in spite of a concerted effort to commercialize SOFC power generation, all currently manufactured SOFC stacks fail. Our results demonstrate that cracked electrolyte areas (caused by differential sintering) are flatter than uncracked regions. The height of the electrolyte surface ranged from 86 to 289 μm above the baseline following sintering. Reduction typically results in increases in curvature of up to 214 μm. Initial crack density appears to affect curvature evolution during reduction; the higher the crack density, the smaller the curvature increase following reduction at 600 °C. In general, however, we observed that the electrolyte layer is remarkably resistant to further cracking during these typographic changes. Following oxidation at 750 °C, large changes in curvature (up to 280 μm) are noted that appear to be related to the strength of the bond between the electrolyte and the underlying anode.

Characterizing open and non-uniform vertical heat sources: towards the identification of real vertical cracks in vibrothermography experiments

NASA Astrophysics Data System (ADS)

Castelo, A.; Mendioroz, A.; Celorrio, R.; Salazar, A.; López de Uralde, P.; Gorosmendi, I.; Gorostegui-Colinas, E.

2017-05-01

Lock-in vibrothermography is used to characterize vertical kissing and open cracks in metals. In this technique the crack heats up during ultrasound excitation due mainly to friction between the defect's faces. We have solved the inverse problem, consisting in determining the heat source distribution produced at cracks under amplitude modulated ultrasound excitation, which is an ill-posed inverse problem. As a consequence the minimization of the residual is unstable. We have stabilized the algorithm introducing a penalty term based on Total Variation functional. In the inversion, we combine amplitude and phase surface temperature data obtained at several modulation frequencies. Inversions of synthetic data with added noise indicate that compact heat sources are characterized accurately and that the particular upper contours can be retrieved for shallow heat sources. The overall shape of open and homogeneous semicircular strip-shaped heat sources representing open half-penny cracks can also be retrieved but the reconstruction of the deeper end of the heat source loses contrast. Angle-, radius- and depth-dependent inhomogeneous heat flux distributions within these semicircular strips can also be qualitatively characterized. Reconstructions of experimental data taken on samples containing calibrated heat sources confirm the predictions from reconstructions of synthetic data. We also present inversions of experimental data obtained from a real welded Inconel 718 specimen. The results are in good qualitative agreement with the results of liquids penetrants testing.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alam, M.E.; Pal, S.; Maloy, Stuart Andrew

The FCRD NFA-1 is a high strength, irradiation tolerant nanostructured ferritic alloy (NFA) produced by ball milling argon atomized Fe-14Cr-3W-0.35Ti-0.25Y (wt.%) and FeO powders, followed by hot extrusion at 850 °C, and subsequent annealing and cross-rolling at 1000 °C. The microstructure of the resulting ≈10 mm thick NFA-1 plate is dominated by ultrafine sub-micron pancake shaped grains, and a large population of microcracks lying on planes parallel to the plate faces. Pre-cracked fracture toughness tests in four different orientations (L-T, T-L, L-S and T-S) show stable crack growth by ductile tearing, with peak load K Jc from ≈ 88 tomore » 154 MPa√m at ambient temperature. Stable crack tearing persists down to ≈ -175 °C and is accompanied by extensive delamination due to the propagation of the microcracks. Depending on the specimen orientation, this unusual toughening mechanism is either due to a reduction of crack tip stresses in thin ligaments formed by the delaminations (L-T and T-L), or 90° deflection of cracks initially running normal to the delaminations (L-S and T-S), thereby suppressing cleavage in both cases. Lastly, understanding the fracture processes in NFA-1 is also important to its irradiation tolerance in nuclear service as well as its fabricability in making defect-free components such as thin-walled tubing.« less

Pellet Cladding Mechanical Interaction Modeling Using the Extended Finite Element Method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Spencer, Benjamin W.; Jiang, Wen; Dolbow, John E.

As a brittle material, the ceramic UO2 used as light water reactor fuel experiences significant fracturing throughout its life, beginning with the first rise to power of fresh fuel. This has multiple effects on the thermal and mechanical response of the fuel/cladding system. One such effect that is particularly important is that when there is mechanical contact between the fuel and cladding, cracks that extending from the outer surface of the fuel into the volume of the fuel cause elevated stresses in the adjacent cladding, which can potentially lead to cladding failure. Modeling the thermal and mechanical response of themore » cladding in the vicinity of these surface-breaking cracks in the fuel can provide important insights into this behavior to help avoid operating conditions that could lead to cladding failure. Such modeling has traditionally been done in the context of finite-element-based fuel performance analysis by modifying the fuel mesh to introduce discrete cracks. While this approach is effective in capturing the important behavior at the fuel/cladding interface, there are multiple drawbacks to explicitly incorporating the cracks in the finite element mesh. Because the cracks are incorporated in the original mesh, the mesh must be modified for cracks of specified location and depth, so it is difficult to account for crack propagation and the formation of new cracks at other locations. The extended finite element method (XFEM) has emerged in recent years as a powerful method to represent arbitrary, evolving, discrete discontinuities within the context of the finite element method. Development work is underway by the authors to implement XFEM in the BISON fuel performance code, and this capability has previously been demonstrated in simulations of fracture propagation in ceramic nuclear fuel. These preliminary demonstrations have included only the fuel, and excluded the cladding for simplicity. This paper presents initial results of efforts to apply XFEM to model stress concentrations induced by fuel fractures at the fuel/cladding interface during pellet cladding mechanical interaction (PCMI). This is accomplished by enhancing the thermal and mechanical contact enforcement algorithms employed by BISON to permit their use in conjunction with XFEM. The results from this methodology are demonstrated to be equivalent to those from using meshed discrete cracks. While the results of the two methods are equivalent for the case of a stationary crack, it is demonstrated that XFEM provides the additional flexibility of allowing arbitrary crack initiation and propagation during the analysis, and minimizes model setup effort for cases with stationary cracks.« less

Effect of Chamber Pressurization Rate on Combustion and Propagation of Solid Propellant Cracks

NASA Astrophysics Data System (ADS)

Yuan, Wei-Lan; Wei, Shen; Yuan, Shu-Shen

2002-01-01

area of the propellant grain satisfies the designed value. But cracks in propellant grain can be generated during manufacture, storage, handing and so on. The cracks can provide additional surface area for combustion. The additional combustion may significantly deviate the performance of the rocket motor from the designed conditions, even lead to explosive catastrophe. Therefore a thorough study on the combustion, propagation and fracture of solid propellant cracks must be conducted. This paper takes an isolated propellant crack as the object and studies the effect of chamber pressurization rate on the combustion, propagation and fracture of the crack by experiment and theoretical calculation. deformable, the burning inside a solid propellant crack is a coupling of solid mechanics and combustion dynamics. In this paper, a theoretical model describing the combustion, propagation and fracture of the crack was formulated and solved numerically. The interaction of structural deformation and combustion process was included in the theoretical model. The conservation equations for compressible fluid flow, the equation of state for perfect gas, the heat conducting equation for the solid-phase, constitutive equation for propellant, J-integral fracture criterion and so on are used in the model. The convective burning inside the crack and the propagation and fracture of the crack were numerically studied by solving the set of nonlinear, inhomogeneous gas-phase governing equations and solid-phase equations. On the other hand, the combustion experiments for propellant specimens with a precut crack were conducted by RTR system. Predicted results are in good agreement with experimental data, which validates the reasonableness of the theoretical model. Both theoretical and experimental results indicate that the chamber pressurization rate has strong effects on the convective burning in the crack, crack fracture initiation and fracture pattern.

Using Media While Interacting Face-to-Face Is Associated With Psychosocial Well-Being and Personality Traits.

PubMed

Lee, Mindy; Murphy, Karen; Andrews, Glenda

2018-01-01

Positive face-to-face human interactions are known to benefit well-being. Drawing upon previous work regarding the interference of media (via technological devices or print) in social interaction, the aim of this study was to identify whether using media during face-to-face interaction could potentially limit the positive effect of interaction on well-being. Participants were 437 university students who completed an online survey which assessed media multitasking behaviors, well-being (trait depression, trait anxiety, social anxiety, empathy, and psychological well-being), and personality traits (Big-5 and narcissism). Face-to-face interaction was positively associated with well-being. However, when media use during face-to-face interaction was considered, there was a negative relationship with well-being (more depression, more anxiety, and less psychological well-being). Those who used certain media types, such as phone or video chatting, listening to music, and gaming, while interacting with others, also had lower scores on measures of empathy. Regression analyses showed significant contributions by these media types to empathy levels, even after controlling for age, gender, and personality traits. Face-to-face media multitasking was related to higher levels of narcissism and neuroticism, and lower levels of agreeableness, conscientiousness, and openness. This study provides insight into the possible role of media multitasking during face-to-face interaction on psychosocial outcomes.

A local crack-tracking strategy to model three-dimensional crack propagation with embedded methods

DOE Office of Scientific and Technical Information (OSTI.GOV)

Annavarapu, Chandrasekhar; Settgast, Randolph R.; Vitali, Efrem

We develop a local, implicit crack tracking approach to propagate embedded failure surfaces in three-dimensions. We build on the global crack-tracking strategy of Oliver et al. (Int J. Numer. Anal. Meth. Geomech., 2004; 28:609–632) that tracks all potential failure surfaces in a problem at once by solving a Laplace equation with anisotropic conductivity. We discuss important modifications to this algorithm with a particular emphasis on the effect of the Dirichlet boundary conditions for the Laplace equation on the resultant crack path. Algorithmic and implementational details of the proposed method are provided. Finally, several three-dimensional benchmark problems are studied and resultsmore » are compared with available literature. Lastly, the results indicate that the proposed method addresses pathological cases, exhibits better behavior in the presence of closely interacting fractures, and provides a viable strategy to robustly evolve embedded failure surfaces in 3D.« less

A local crack-tracking strategy to model three-dimensional crack propagation with embedded methods

DOE PAGES

Annavarapu, Chandrasekhar; Settgast, Randolph R.; Vitali, Efrem; ...

2016-09-29

We develop a local, implicit crack tracking approach to propagate embedded failure surfaces in three-dimensions. We build on the global crack-tracking strategy of Oliver et al. (Int J. Numer. Anal. Meth. Geomech., 2004; 28:609–632) that tracks all potential failure surfaces in a problem at once by solving a Laplace equation with anisotropic conductivity. We discuss important modifications to this algorithm with a particular emphasis on the effect of the Dirichlet boundary conditions for the Laplace equation on the resultant crack path. Algorithmic and implementational details of the proposed method are provided. Finally, several three-dimensional benchmark problems are studied and resultsmore » are compared with available literature. Lastly, the results indicate that the proposed method addresses pathological cases, exhibits better behavior in the presence of closely interacting fractures, and provides a viable strategy to robustly evolve embedded failure surfaces in 3D.« less

EPRI-NASA Cooperative Project on Stress Corrosion Cracking of Zircaloys. [nuclear fuel failures

NASA Technical Reports Server (NTRS)

Cubicciotti, D.; Jones, R. L.

1978-01-01

Examinations of the inside surface of irradiated fuel cladding from two reactors show the Zircaloy cladding is exposed to a number of aggressive substances, among them iodine, cadmium, and iron-contaminated cesium. Iodine-induced stress corrosion cracking (SCC) of well characterized samples of Zircaloy sheet and tubing was studied. Results indicate that a threshold stress must be exceeded for iodine SCC to occur. The existence of a threshold stress indicates that crack formation probably is the key step in iodine SCC. Investigation of the crack formation process showed that the cracks responsible for SCC failure nucleated at locations in the metal surface that contained higher than average concentrations of alloying elements and impurities. A four-stage model of iodine SCC is proposed based on the experimental results and the relevance of the observations to pellet cladding interaction failures is discussed.

High-temperature tensile-hold crack-growth behavior of HASTELLOY® X alloy compared to HAYNES® 188 and HAYNES® 230® alloys

NASA Astrophysics Data System (ADS)

Lee, S. Y.; Lu, Y. L.; Liaw, P. K.; Choo, H.; Thompson, S. A.; Blust, J. W.; Browning, P. F.; Bhattacharya, A. K.; Aurrecoechea, J. M.; Klarstrom, D. L.

2008-03-01

The creep-fatigue crack-growth tests of HASTELLOY® X alloy were carried out at the temperatures of 649°C, 816°C, and 927°C in laboratory air. The experiments were conducted under a constant stress-intensity-factor-range (Δ K) control mode with a R-ratio of 0.05. In the constant Δ K tests, a Δ K of 27.5 MPa sqrt{m} and a triangular waveform with a frequency of 0.333 Hz were used. Various tensile hold times at the maximum load were imposed to study fatigue and creep-fatigue interactions. Crack lengths were measured by a direct current potential drop method. In this paper, effects of hold time and temperature on the crack-growth rates are discussed. Furthermore, the crack-growth rates of the HASTELLOY® X alloy are compared to those of the HAYNES® 188 and HAYNES® 230® superalloys.

Influence of Stress Corrosion Crack Morphology on Ultrasonic Examination Performances

NASA Astrophysics Data System (ADS)

Dupond, O.; Duwig, V.; Fouquet, T.

2009-03-01

Stress Corrosion Cracking represents a potential damage for several components in PWR. For this reason, NDE of stress corrosion cracks corresponds to an important stake for Electricité de France (EDF) both for availability and for safety of plants. This paper is dedicated to the ultrasonic examination of SCC crack defects. The study mixes an experimental approach conducted on artificial flaws—meant to represent the characteristic morphologic features often encountered on SCC cracks—and a 2D finite element modelling with the code ATHENA 2D developed by EDF. Results indicate that ATHENA reproduces correctly the interaction of the beam on the complex defect. Indeed specific ultrasonic responses resulting from the defect morphology have been observed experimentally and reproduced with the modelling.

Thermal Fatigue Testing of ZrO2-Y2O3 Thermal Barrier Coating Systems using a High Power CO2 Laser

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Miller, Robert A.

1997-01-01

In the present study, the mechanisms of fatigue crack initiation and propagation, and of coating failure, under thermal loads that simulate diesel engine conditions, are investigated. The surface cracks initiate early and grow continuously under thermal Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF) stresses. It is found that, in the absence of interfacial oxidation, the failure associated with LCF is closely related to coating sintering and creep at high temperatures. Significant LCF and HCF interactions have been observed in the thermal fatigue tests. The fatigue crack growth rate in the ceramic coating strongly depends on the characteristic HCF cycle number, N*(sub NCF), which is defined as the number of HCF cycles per LCF cycle. The crack growth rate is increased from 0.36 microns/LCF cycle for a pure LCF test to 2.8 microns/LCF cycle for a combined LCF and HCF test at N*(sub NCF) about 20,000. A surface wedging model has been proposed to account for the HCF crack growth in the coating systems. This mechanism predicts that HCF damage effect increases with increasing surface temperature swing, the thermal expansion coefficient and the elastic modulus of the ceramic coating, as well as with the HCF interacting depth. A good agreement has been found between the analysis and experimental evidence.

Fracture Toughness and Fatigue Crack Growth Behavior of As-Cast High-Entropy Alloys

NASA Astrophysics Data System (ADS)

Seifi, Mohsen; Li, Dongyue; Yong, Zhang; Liaw, Peter K.; Lewandowski, John J.

2015-08-01

The fracture toughness and fatigue crack growth behavior of two as-vacuum arc cast high-entropy alloys (HEAs) (Al0.2CrFeNiTi0.2 and AlCrFeNi2Cu) were determined. A microstructure examination of both HEA alloys revealed a two-phase structure consisting of body-centered cubic (bcc) and face-centered cubic (fcc) phases. The notched and fatigue precracked toughness values were in the range of those reported in the literature for two-phase alloys but significantly less than recent reports on a single phase fcc-HEA that was deformation processed. Fatigue crack growth experiments revealed high fatigue thresholds that decreased significantly with an increase in load ratio, while Paris law slopes exhibited metallic-like behavior at low R with significant increases at high R. Fracture surface examinations revealed combinations of brittle and ductile/dimpled regions at overload, with some evidence of fatigue striations in the Paris law regime.

On the contact interaction of two identical stringers with an elastic semi-infinite continuous or vertically cracked plate

NASA Astrophysics Data System (ADS)

Grigoryan, M. S.

2018-04-01

This paper considers two connected contact problems on the interaction of stringers with an elastic semi-infinite plate. In the first problem, an elastic half-infinite continuous plate is reinforced on its boundary by two identical stringers exposed to a tensile external force. In the second problem, in the presence of the same stringers, the plate contains a collinear system of cracks on its vertical axis. The solution of both problems is reduced to the solution of singular integral equations (SIE) that are solved by a known numerical-analytical method.

Early detection of tooth wear by en-face optical coherence tomography

NASA Astrophysics Data System (ADS)

Mărcăuteanu, Corina; Negrutiu, Meda; Sinescu, Cosmin; Demjan, Eniko; Hughes, Mike; Bradu, Adrian; Dobre, George; Podoleanu, Adrian G.

2009-02-01

Excessive dental wear (pathological attrition and/or abfractions) is a frequent complication in bruxing patients. The parafunction causes heavy occlusal loads. The aim of this study is the early detection and monitoring of occlusal overload in bruxing patients. En-face optical coherence tomography was used for investigating and imaging of several extracted tooth, with a normal morphology, derived from patients with active bruxism and from subjects without parafunction. We found a characteristic pattern of enamel cracks in patients with first degree bruxism and with a normal tooth morphology. We conclude that the en-face optical coherence tomography is a promising non-invasive alternative technique for the early detection of occlusal overload, before it becomes clinically evident as tooth wear.

Effect of Measured Welding Residual Stresses on Crack Growth

NASA Technical Reports Server (NTRS)

Hampton, Roy W.; Nelson, Drew; Doty, Laura W. (Technical Monitor)

1998-01-01

Welding residual stresses in thin plate A516-70 steel and 2219-T87 aluminum butt weldments were measured by the strain-gage hole drilling and X-ray diffraction methods. The residual stress data were used to construct 3D strain fields which were modeled as thermally induced strains. These 3D strain fields were then analyzed with the WARP31) FEM fracture analysis code in order to predict their effect on fatigue and on fracture. For analyses of fatigue crack advance and subsequent verification testing, fatigue crack growth increments were simulated by successive saw-cuts and incremental loading to generate, as a function of crack length, effects on crack growth of the interaction between residual stresses and load induced stresses. The specimen experimental response was characterized and compared to the WARM linear elastic and elastic-plastic fracture mechanics analysis predictions. To perform the fracture analysis, the plate material's crack tearing resistance was determined by tests of thin plate M(T) specimens. Fracture analyses of these specimen were performed using WARP31D to determine the critical Crack Tip Opening Angle [CTOA] of each material. These critical CTOA values were used to predict crack tearing and fracture in the weldments. To verify the fracture predictions, weldment M(T) specimen were tested in monotonic loading to fracture while characterizing the fracture process.

Analytical insight into "breathing" crack-induced acoustic nonlinearity with an application to quantitative evaluation of contact cracks.

PubMed

Wang, Kai; Liu, Menglong; Su, Zhongqing; Yuan, Shenfang; Fan, Zheng

2018-08-01

To characterize fatigue cracks, in the undersized stage in particular, preferably in a quantitative and precise manner, a two-dimensional (2D) analytical model is developed for interpreting the modulation mechanism of a "breathing" crack on guided ultrasonic waves (GUWs). In conjunction with a modal decomposition method and a variational principle-based algorithm, the model is capable of analytically depicting the propagating and evanescent waves induced owing to the interaction of probing GUWs with a "breathing" crack, and further extracting linear and nonlinear wave features (e.g., reflection, transmission, mode conversion and contact acoustic nonlinearity (CAN)). With the model, a quantitative correlation between CAN embodied in acquired GUWs and crack parameters (e.g., location and severity) is obtained, whereby a set of damage indices is proposed via which the severity of the crack can be evaluated quantitatively. The evaluation, in principle, does not entail a benchmarking process against baseline signals. As validation, the results obtained from the analytical model are compared with those from finite element simulation, showing good consistency. This has demonstrated accuracy of the developed analytical model in interpreting contact crack-induced CAN, and spotlighted its application to quantitative evaluation of fatigue damage. Copyright © 2018 Elsevier B.V. All rights reserved.

Use of Slow Strain Rate Tensile Testing to Assess the Ability of Several Superalloys to Resist Environmentally-Assisted Intergranular Cracking

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Telesman, Jack; Banik, Anthony; McDevitt, Erin

2014-01-01

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720(TradeMark) ATI 718Plus(Registered TradeMark) alloy, Haynes 282(Trademark), and Inconel 740(TradeMark) Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

Investigating Face-to-Face Peer Interaction Patterns in a Collaborative Web Discovery Task: The Bene?ts of a Shared Display

ERIC Educational Resources Information Center

Chung, C-W.; Lee, C-C.; Liu, C-C.

2013-01-01

Mobile computers are now increasingly applied to facilitate face-to-face collaborative learning. However, the factors affecting face-to-face peer interactions are complex as they involve rich communication media. In particular, non-verbal interactions are necessary to convey critical communication messages in face-to-face communication. Through…

Detecting the activation of a self-healing mechanism in concrete by acoustic emission and digital image correlation.

PubMed

Tsangouri, E; Aggelis, D G; Van Tittelboom, K; De Belie, N; Van Hemelrijck, D

2013-01-01

Autonomous crack healing in concrete is obtained when encapsulated healing agent is embedded into the material. Cracking damage in concrete elements ruptures the capsules and activates the healing process by healing agent release. Previously, the strength and stiffness recovery as well as the sealing efficiency after autonomous crack repair was well established. However, the mechanisms that trigger capsule breakage remain unknown. In parallel, the conditions under which the crack interacts with embedded capsules stay black-box. In this research, an experimental approach implementing an advanced optical and acoustic method sets up scopes to monitor and justify the crack formation and capsule breakage of concrete samples tested under three-point bending. Digital Image Correlation was used to visualize the crack opening. The optical information was the basis for an extensive and analytical study of the damage by Acoustic Emission analysis. The influence of embedding capsules on the concrete fracture process, the location of capsule damage, and the differentiation between emissions due to capsule rupture and crack formation are presented in this research. A profound observation of the capsules performance provides a clear view of the healing activation process.

Three-dimensional analysis of surface crack-Hertzian stress field interaction

NASA Technical Reports Server (NTRS)

Ballarini, R.; Hsu, Y.

1989-01-01

The results are presented of a stress intensity factor analysis of semicircular surface cracks in the inner raceway of an engine bearing. The loading consists of a moving spherical Hertzian contact load and an axial stress due to rotation and shrink fit. A 3-D linear elastic Boundary Element Method code was developed to perform the stress analysis. The element library includes linear and quadratic isoparametric surface elements. Singular quarter point elements were employed to capture the square root displacement variation and the inverse square root stress singularity along the crack front. The program also possesses the capability to separate the whole domain into two subregions. This procedure enables one to solve nonsymmetric fracture mechanics problems without having to separate the crack surfaces a priori. A wide range of configuration parameters was investigated. The ratio of crack depth to bearing thickness was varied from one-sixtieth to one-fifth for several different locations of the Hertzian load. The stress intensity factors for several crack inclinations were also investigated. The results demonstrate the efficiency and accuracy of the Boundary Element Method. Moreover, the results can provide the basis for crack growth calculations and fatigue life prediction.

High-Resolution Characterizations of Grain Boundary Damage and Stress Corrosion Cracks in Cold-Rolled Alloy 690

NASA Astrophysics Data System (ADS)

Bruemmer, S. M.; Olszta, M. J.; Toloczko, M. B.; Thomas, L. E.

Unidirectional cold rolling has been shown to promote intergranular stress corrosion cracking (IGSCC) in alloy 690 tested in PWR primary water. High-resolution scanning (SEM) and transmission electron microscopy (TEM) have been employed to investigate the microstructural reasons for this enhanced susceptibility in two stages, first examining grain boundary damage produced by cold rolling and second by characterization of stress corrosion crack tips. The degree of permanent grain boundary damage from cold rolling was found to depend directly on the initial IG precipitate distribution. Cold rolling to high levels of reduction was discovered to produce small IG voids and cracked carbides in alloys with a high density of grain boundary carbides. For the same degree of cold rolling, alloys with few IG carbides exhibited much less permanent damage. Although this difference in grain boundary damage appears to correlate with measured SCC growth rates, crack tip examinations reveal no interaction between the preexisting voids and cracked carbides with the propagation. In many cases, these features appeared to blunt propagation of IGSCC cracks. High-resolution characterizations are described for cold-rolled alloy 690 CRDM tubing and plate materials to gain insights into IGSCC mechanisms.

On the response of dynamic cracks to increasing overload

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gumbsch, P.

1996-12-01

One of the most interesting questions in the dynamics of brittle fracture is how a running brittle crack responds to an overload, i.e., to a mechanical energy release rate larger than that due to the increase in surface energy of the two cleavage surfaces. To address this question, dynamically running cracks in different crystal lattices are modelled atomistically under the condition of constant energy release rate. Stable crack propagation as well as the onset of crack tip instabilities are studied. It will be shown that small overloads lead to stable crack propagation with steady state velocities which quickly reach themore » terminal velocity of about 0.4 of the Rayleigh wave speed upon increasing the overload. Further increasing the overload does not change the steady state velocity but significantly changes the energy dissipation process towards shock wave emission at the breaking of every single atomic bond. Eventually the perfectly brittle crack becomes unstable, which then leads to dislocation generation and to the production of cleavage steps. The onset of the instability as well as the terminal velocity are related to the non-linearity of the interatomic interaction.« less

Detecting the Activation of a Self-Healing Mechanism in Concrete by Acoustic Emission and Digital Image Correlation

PubMed Central

Tsangouri, E.; Aggelis, D. G.; Van Tittelboom, K.; De Belie, N.; Van Hemelrijck, D.

2013-01-01

Autonomous crack healing in concrete is obtained when encapsulated healing agent is embedded into the material. Cracking damage in concrete elements ruptures the capsules and activates the healing process by healing agent release. Previously, the strength and stiffness recovery as well as the sealing efficiency after autonomous crack repair was well established. However, the mechanisms that trigger capsule breakage remain unknown. In parallel, the conditions under which the crack interacts with embedded capsules stay black-box. In this research, an experimental approach implementing an advanced optical and acoustic method sets up scopes to monitor and justify the crack formation and capsule breakage of concrete samples tested under three-point bending. Digital Image Correlation was used to visualize the crack opening. The optical information was the basis for an extensive and analytical study of the damage by Acoustic Emission analysis. The influence of embedding capsules on the concrete fracture process, the location of capsule damage, and the differentiation between emissions due to capsule rupture and crack formation are presented in this research. A profound observation of the capsules performance provides a clear view of the healing activation process. PMID:24381518

Fracture behavior of human molars.

PubMed

Keown, Amanda J; Lee, James J-W; Bush, Mark B

2012-12-01

Despite the durability of human teeth, which are able to withstand repeated loading while maintaining form and function, they are still susceptible to fracture. We focus here on longitudinal fracture in molar teeth-channel-like cracks that run along the enamel sidewall of the tooth between the gum line (cemento-enamel junction-CEJ) and the occlusal surface. Such fractures can often be painful and necessitate costly restorative work. The following study describes fracture experiments made on molar teeth of humans in which the molars are placed under axial compressive load using a hard indenting plate in order to induce longitudinal cracks in the enamel. Observed damage modes include fractures originating in the occlusal region ('radial-median cracks') and fractures emanating from the margin of the enamel in the region of the CEJ ('margin cracks'), as well as 'spalling' of enamel (the linking of longitudinal cracks). The loading conditions that govern fracture behavior in enamel are reported and observations made of the evolution of fracture as the load is increased. Relatively low loads were required to induce observable crack initiation-approximately 100 N for radial-median cracks and 200 N for margin cracks-both of which are less than the reported maximum biting force on a single molar tooth of several hundred Newtons. Unstable crack growth was observed to take place soon after and occurred at loads lower than those calculated by the current fracture models. Multiple cracks were observed on a single cusp, their interactions influencing crack growth behavior. The majority of the teeth tested in this study were noted to exhibit margin cracks prior to compression testing, which were apparently formed during the functional lifetime of the tooth. Such teeth were still able to withstand additional loading prior to catastrophic fracture, highlighting the remarkable damage containment capabilities of the natural tooth structure.

Stress-dependent permeability and wave dispersion in tight cracked rocks: Experimental validation of simple effective medium models

NASA Astrophysics Data System (ADS)

Sarout, Joel; Cazes, Emilie; Delle Piane, Claudio; Arena, Alessio; Esteban, Lionel

2017-08-01

We experimentally assess the impact of microstructure, pore fluid, and frequency on wave velocity, wave dispersion, and permeability in thermally cracked Carrara marble under effective pressure up to 50 MPa. The cracked rock is isotropic, and we observe that (1) P and S wave velocities at 500 kHz and the low-strain (<10-5) mechanical moduli at 0.01 Hz are pressure-dependent, (2) permeability decreases asymptotically toward a small value with increasing pressure, (3) wave dispersion between 0.01 Hz and 500 MHz in the water-saturated rock reaches a maximum of 26% for S waves and 9% for P waves at 1 MPa, and (4) wave dispersion virtually vanishes above 30 MPa. Assuming no interactions between the cracks, effective medium theory is used to model the rock's elastic response and its permeability. P and S wave velocity data are jointly inverted to recover the crack density and effective aspect ratio. The permeability data are inverted to recover the cracks' effective radius. These parameters lead to a good agreement between predicted and measured wave velocities, dispersion and permeability up to 50 MPa, and up to a crack density of 0.5. The evolution of the crack parameters suggests that three deformation regimes exist: (1) contact between cracks' surface asperities up to 10 MPa, (2) progressive crack closure between 10 and 30 MPa, and (3) crack closure effectively complete above 30 MPa. The derived crack parameters differ significantly from those obtained by analysis of 2-D electron microscope images of thin sections or 3-D X-ray microtomographic images of millimeter-size specimens.

Rock Your Classroom!: Use Subwoofers to Teach Electricity and Science

ERIC Educational Resources Information Center

Karns, Robert J.

2007-01-01

It may not seem like school is the best place to crank up the bass for glass-cracking extreme energy, but subwoofers just might make better teaching and learning tools than they do music makers. Faced with the fact that electricity is invisible, electrical technology students encounter significant challenges in the classroom when abstract concepts…

Modeling of fatigue crack induced nonlinear ultrasonics using a highly parallelized explicit local interaction simulation approach

NASA Astrophysics Data System (ADS)

Shen, Yanfeng; Cesnik, Carlos E. S.

2016-04-01

This paper presents a parallelized modeling technique for the efficient simulation of nonlinear ultrasonics introduced by the wave interaction with fatigue cracks. The elastodynamic wave equations with contact effects are formulated using an explicit Local Interaction Simulation Approach (LISA). The LISA formulation is extended to capture the contact-impact phenomena during the wave damage interaction based on the penalty method. A Coulomb friction model is integrated into the computation procedure to capture the stick-slip contact shear motion. The LISA procedure is coded using the Compute Unified Device Architecture (CUDA), which enables the highly parallelized supercomputing on powerful graphic cards. Both the explicit contact formulation and the parallel feature facilitates LISA's superb computational efficiency over the conventional finite element method (FEM). The theoretical formulations based on the penalty method is introduced and a guideline for the proper choice of the contact stiffness is given. The convergence behavior of the solution under various contact stiffness values is examined. A numerical benchmark problem is used to investigate the new LISA formulation and results are compared with a conventional contact finite element solution. Various nonlinear ultrasonic phenomena are successfully captured using this contact LISA formulation, including the generation of nonlinear higher harmonic responses. Nonlinear mode conversion of guided waves at fatigue cracks is also studied.

Descriptions of crack growth behaviors in glass-ZrO2 bilayers under thermal residual stresses.

PubMed

Belli, Renan; Wendler, Michael; Zorzin, José I; Petschelt, Anselm; Tanaka, Carina B; Meira, Josete; Lohbauer, Ulrich

2016-09-01

This study was intended to separate residual stresses arising from the mismatch in coefficients of thermal expansion between glass and zirconia (ZrO2) from those stresses arising solely from the cooling process. Slow crack growth experimentes were undertaken to demonstrate how cracks grow in different residual stress fields. Aluminosilicate glass discs were sintered onto ZrO2 to form glass-ZrO2 bilayers. Glass discs were allowed to bond to the ZrO2 substrate during sintering or prevented from bonding by means of coating the ZrO2 with a thin boron nitrade coating. Residual stress gradients on "bonded" and "unbonded" bilayers were assessed using birefringence measurements. Unbonded glass discs were further tested under biaxial flexure in dynamic fatigue conditions in order to evaluate the effect of residual stress on the slow crack growth behavior. When fast-ccoling was induced, residual tensile stresses on the glass increased significantly on the side toward the ZrO2 substrate. By allowing the bond between glass and ZrO2, those tensile stresses observed in unbonded specimens are overwhelmed by the contraction mismatch stresses between the ZrO2 substrate and the glassy overlayer. Specimens containing residual tensile stresses on the bending surface showed a time-dependent strength increase in relation to stress-free annealed samples in the dynamic biaxial bending test, with this effect being dependent on the magnitude of the residual tensile stress. The phenomenon observed is explained here on the basis of the water toughening effect, in which water diffuses into the glass promoting local swelling. An additional residual tensile stress at the crack tip adds an applied-stress-independent (Kres) term to the total tip stress intensity factor (Ktip), increasing the stress-enhanced diffusion and the shielding of the crack tip through swelling of the crack faces. Residual stresses in the glass influence the crack growth behavior of veneered-ZrO2 bilayered dental prostheses. The role of water in crack growth might be of higher complexity when residual stresses are present in the glass layer. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

High-temperature transverse fracture toughness of Nicalon-fiber-reinforced CAS-II glass-ceramic matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kahraman, R.; Mandell, J.F.; Deibert, M.C.

Cracking parallel to the fibers in off-axis plies is usually the initial form of damage in composite laminates. This cracking process has been associated with the (transverse) fracture toughness, defined by the critical strain energy release rate, G{sub Ic}. The measurement of G{sub Ic} provides basic information about the transverse crack resistance. In this study, the utility of the double torsion (DT) test technique to determine G{sub Ic} in a glass-ceramic matrix composite (Nicalon/CAS-II) at temperatures up to 1,000 C has been demonstrated. G{sub Ic} did decrease moderately with increasing temperature (as does the bulk matrix); however, no evidence ofmore » an interphase oxidizing effect on crack growth (parallel to the fibers) could be found. The inevitable misalignment of fibers in the material was not very efficient at bridging the crack in the DT specimens, in contrast to the significant matrix crack interactions with the fibers reported for other geometries such as double cantilever beam and flexure specimens.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stoynov, Y.; Dineva, P.

The stress, magnetic and electric field analysis of multifunctional composites, weakened by impermeable cracks, is of fundamental importance for their structural integrity and reliable service performance. The aim is to study dynamic behavior of a plane of functionally graded magnetoelectroelastic composite with more than one crack. The coupled material properties vary exponentially in an arbitrary direction. The plane is subjected to anti-plane mechanical and in-plane electric and magnetic load. The boundary value problem described by the partial differential equations with variable coefficients is reduced to a non-hypersingular traction boundary integral equation based on the appropriate functional transform and frequency-dependent fundamentalmore » solution derived in a closed form by Radon transform. Software code based on the boundary integral equation method (BIEM) is developed, validated and inserted in numerical simulations. The obtained results show the sensitivity of the dynamic stress, magnetic and electric field concentration in the cracked plane to the type and characteristics of the dynamic load, to the location and cracks disposition, to the wave-crack-crack interactions and to the magnitude and direction of the material gradient.« less

RDS-21 Face-Gear Surface Durability Tests

NASA Technical Reports Server (NTRS)

Lewicki, David G.; Heath, Gregory F.; Filler, Robert R.; Slaughter, Stephen C.; Fetty, Jason

2007-01-01

Experimental fatigue tests were performed to determine the surface durability life of a face gear in mesh with a tapered spur involute pinion. Twenty-four sets of gears were tested at three load levels: 7200, 8185, and 9075 lb-in face gear torque, and 2190 to 3280 rpm face gear speed. The gears were carburized and ground, shot-peened and vibro-honed, and made from VIM-VAR Pyrowear 53 steel per AMS 6308. The tests produced 17 gear tooth spalling failures and 7 suspensions. For all the failed sets, spalling occurred on at least one tooth of all the pinions. In some cases, the spalling initiated a crack in the pinion teeth which progressed to tooth fracture. Also, spalling occurred on some face gear teeth. The AGMA endurance allowable stress for a tapered spur involute pinion in mesh with a face gear was determined to be 275 ksi for the material tested. For the application of a tapered spur involute pinion in mesh with a face gear, proper face gear shim controlled the desired gear tooth contact pattern while proper pinion shim was an effective way of adjusting backlash without severely affecting the contact pattern.

Double trouble: violent and non-violent traumas among women at sexual risk of HIV infection.

PubMed

Brown-Peterside, Pamela; Ren, Leigh; Chiasson, Mary Ann; Koblin, Beryl A

2002-01-01

This study examines the association between trauma and HIV risk behaviors among women at sexual risk for HIV infection. From April to August 1998, high-risk HIV negative women were recruited in the South Bronx into a year-long cohort study. At the 12-month visit, 116 women were interviewed face-to-face about recent and lifetime violent and non-violent traumas. The women reported a substantial prevalence of sexual risk behaviors associated with the acquisition of HIV. At baseline, almost two-thirds (64%) reported unprotected vaginal sex in the previous six months, and in the previous year, 62% had smoked crack, 52% reported sex-for-money-or-drugs exchanges, and 47% had five or more male sex partners. The lifetime prevalence of trauma was high: 81% had experienced one or more violent traumas and 97% had experienced one or more non-violent traumas. Women who had experienced violent trauma--physical assault by a partner (OR = 2.88; 95% CI 1.12; 7.41)--and those who had experienced non-violent trauma--loss of a child to foster care (OR = 3.34; 95% CI 1.04; 10.65)--were more likely to use crack than others. Those who had experienced non-violent trauma, by witnessing a physical assault (OR = 2.31; 95% CI 0.99; 5.40), were also more likely than others to have exchanged sex. Both violent and non-violent traumas appear to play a role in the behaviors that place women at risk of HIV infection, particularly using crack and exchanging sex.

Experimental and theoretical fracture mechanics applied to volcanic conduits and domes

NASA Astrophysics Data System (ADS)

Sammonds, P.; Matthews, C.; Kilburn, C.; Smith, R.; Tuffen, H.; Meredith, P.

2008-12-01

We present an integrated modelling and experimental approach to magma deformation and fracture, which we attempt to validate against field observations of seismicity. The importance of fracture processes in magma ascent dynamics and lava dome growth and collapse are apparent from the associated seismicity. Our laboratory experiments have shown that brittle fracture of magma can occur at high temperature and stress conditions prevalent in the shallow volcanic system. Here, we use a fracture mechanics approach to model seismicity preceding volcanic eruptions. Starting with the fracture mechanics concept of a crack in an elastic body, we model crack growth around the volcanic conduit through the processes of crack interactions, leading either to the propagation and linkage of cracks, or crack avoidance and the inhibition of crack propagation. The nature of that interaction is governed by the temperature and plasticity of the magma. We find that fracture mechanics rules can account for the style of seismicity preceding eruptions. We have derived the changes in seismic b-value predicted by the model and interpret these in terms of the style of fracturing, fluid flow and heat transport. We compare our model with results from our laboratory experiments where we have deformed lava at high temperatures under triaxial stresses. These experiments were conducted in dry and water saturated conditions at effective pressures up to 10 MPa, temperatures up to 1000°C and strain rates from 10-4 s-1 to 10-6 s-1. The behaviour of these magmas was largely brittle under these conditions. We monitored the acoustic emission emitted and calculate the change in micro-seismic b-value with deformation. These we find are in accord with volcano seismicity and our fracture mechanics model.

Cracking of Clay Due to Contact with Waste Chlorinated Solvents

NASA Astrophysics Data System (ADS)

Otero, M.; Ayral, D.; Shipan, J.; Goltz, M. N.; Huang, J.; Demond, A. H.

2012-12-01

Clays are known to crack upon desiccation. Desiccation cracks of up to 3 cm wide have been reported in natural soils. This raises the question if a similar behavior is seen when a dense non-aqueous phase liquids (DNAPL) waste is in contact with clay. The contact with organic liquids causes the clay structure to shrink, leading to the formation of cracks. Moreover, DNAPL waste not only contains the organic liquid solvent but also includes surface-active solutes or surfactants. Such solutes can enhance the interaction of the organic solvents with the clay. This research will assess whether or not contact with chlorinated organic waste causes cracking. In order to evaluate the possibility of cracking in the clay, microcosms have been constructed that mimic aquifer systems, consisting of a saturated layer of sand, a saturated layer of bentonite clay and a 2.5 cm layer of either pure chlorinated solvents or DNAPL waste. The onset of cracking for the microcosm with tetrachloroethylene (PCE) waste as the DNAPL layer occurred after ten days of contact. Similarly, at eight days, cracks were observed in a microcosm containing trichloroethylene (TCE) waste . Forty-four days later, the length and number of cracks have grown considerably; with a total crack length of 50 cm on a surface of 80 cm2 in the microcosm containing PCE waste. On the other hand it took approximately 161 days for the clay layer in the microcosm containing pure PCE to crack. To quantity the degree of cracking, crack maps were developed using the image software, Image J. Characteristics like crack length, crack aperture, and the percentage of total length for a range of apertures were calculated using this software. For example, for the PCE waste microcosm, it was calculated that 3.7% of the crack length had an aperture of 100-300 microns, 15.1% of the crack length had an aperture of 300-500 microns, 29.7% of the crack length had an aperture of 500-700 microns, 40.1% of the crack length had an aperture of 700-900 microns, 6.3% had an aperture of 900-1,100 microns and 5.1% had an aperture of over 1,100 microns. These data suggest that aquitards in the field might crack when in contact with the DNAPL waste. Moreover, it is apparent that the waste contains solutes that accelerate the cracking of the clay layer. Thus, models examining the impact of storage in low permeability layers need to consider the possible impact of cracking.

On Delamination Toughening of a 14YWT Nanostructured Ferritic Alloy

DOE PAGES

Alam, M.E.; Pal, S.; Maloy, Stuart Andrew; ...

2017-06-22

The FCRD NFA-1 is a high strength, irradiation tolerant nanostructured ferritic alloy (NFA) produced by ball milling argon atomized Fe-14Cr-3W-0.35Ti-0.25Y (wt.%) and FeO powders, followed by hot extrusion at 850 °C, and subsequent annealing and cross-rolling at 1000 °C. The microstructure of the resulting ≈10 mm thick NFA-1 plate is dominated by ultrafine sub-micron pancake shaped grains, and a large population of microcracks lying on planes parallel to the plate faces. Pre-cracked fracture toughness tests in four different orientations (L-T, T-L, L-S and T-S) show stable crack growth by ductile tearing, with peak load K Jc from ≈ 88 tomore » 154 MPa√m at ambient temperature. Stable crack tearing persists down to ≈ -175 °C and is accompanied by extensive delamination due to the propagation of the microcracks. Depending on the specimen orientation, this unusual toughening mechanism is either due to a reduction of crack tip stresses in thin ligaments formed by the delaminations (L-T and T-L), or 90° deflection of cracks initially running normal to the delaminations (L-S and T-S), thereby suppressing cleavage in both cases. Lastly, understanding the fracture processes in NFA-1 is also important to its irradiation tolerance in nuclear service as well as its fabricability in making defect-free components such as thin-walled tubing.« less

Fatigue analysis of multiple site damage at a row of holes in a wide panel

NASA Technical Reports Server (NTRS)

Buhler, Kimberley; Grandt, Alten F., Jr.; Moukawsher, E. J.

1994-01-01

This paper is concerned with predicting the fatigue life of unstiffened panels which contain multiple site damage (MSD). The initial damage consists of through-the-thickness cracks emanating from a row of holes in the center of a finite width panel. A fracture mechanics analysis has been developed to predict the growth, interaction, and coalescence of the various cracks which propagate in the panel. A strain-life analysis incorporating Neuber's rule for notches, and Miner's rule for cumulative damage, is also employed to predict crack initiation for holes without initial cracking. This analysis is compared with the results of a series of fatigue tests on 2024-T3 aluminum panels, and is shown to do an excellent job of predicting the influence of MSD on the fatigue life of nine inch wide specimens. Having established confidence in the ability to analyze the influence of MSD on fatigue life, a parametric study is conducted to examine the influence of various MSD scenarios in an unstiffened panel. The numerical study considered 135 cases in all, with the parametric variables being the applied cyclic stress level, the lead crack geometry, and the number and location of MSD cracks. The numerical analysis provides details for the manner in which lead cracks and MSD cracks grow and coalesce leading to final failure. The results indicate that MSD located adjacent to lead cracks is the most damaging configuration, while for cases without lead cracks, MSD clusters which are not separated by uncracked holes are most damaging.

Predicting the 3D fatigue crack growth rate of small cracks using multimodal data via Bayesian networks: In-situ experiments and crystal plasticity simulations

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rovinelli, Andrea; Sangid, Michael D.; Proudhon, Henry

Small crack propagation accounts for most of the fatigue life of engineering structures subject to high cycle fatigue loading conditions. Determining the fatigue crack growth rate of small cracks propagating into polycrystalline engineering alloys is critical to improving fatigue life predictions, thus lowering cost and increasing safety. In this work, cycle-by-cycle data of a small crack propagating in a beta metastable titanium alloy is available via phase and diffraction contrast tomography. Crystal plasticity simulations are used to supplement experimental data regarding the micromechanical fields ahead of the crack tip. Experimental and numerical results are combined into a multimodal dataset andmore » sampled utilizing a non-local data mining procedure. Furthermore, to capture the propensity of body-centered cubic metals to deform according to the pencil-glide model, a non-local driving force is postulated. The proposed driving force serves as the basis to construct a data-driven probabilistic crack propagation framework using Bayesian networks as building blocks. The spatial correlation between the postulated driving force and experimental observations is obtained by analyzing the results of the proposed framework. Results show that the above correlation increases proportionally to the distance from the crack front until the edge of the plastic zone. Moreover, the predictions of the propagation framework show good agreement with experimental observations. Finally, we studied the interaction of a small crack with grain boundaries (GBs) utilizing various slip transmission criteria, revealing the tendency of a crack to cross a GB by propagating along the slip directions minimizing the residual Burgers vector within the GB.« less

Distributed deformation ahead of the Cocos-Nazca Rift at the Galapagos triple junction

NASA Astrophysics Data System (ADS)

Smith, Deborah K.; Schouten, Hans; Zhu, Wen-lu; Montési, Laurent G. J.; Cann, Johnson R.

2011-11-01

The Galapagos triple junction is not a simple ridge-ridge-ridge (RRR) triple junction. The Cocos-Nazca Rift (C-N Rift) tip does not meet the East Pacific Rise (EPR). Instead, two secondary rifts form the link: Incipient Rift at 2°40‧N and Dietz Deep volcanic ridge, the southern boundary of the Galapagos microplate (GMP), at 1°10‧N. Recently collected bathymetry data are used to investigate the regional tectonics prior to the establishment of the GMP (∼1.5 Ma). South of C-N Rift a band of northeast-trending cracks cuts EPR-generated abyssal hills. It is a mirror image of a band of cracks previously identified north of C-N Rift on the same age crust. In both areas, the western ends of the cracks terminate against intact abyssal hills suggesting that each crack initiated at the EPR spreading center and cut eastward into pre-existing topography. Each crack formed a short-lived triple junction until it was abandoned and a new crack and triple junction initiated nearby. Between 2.5 and 1.5 Ma, the pattern of cracking is remarkably symmetric about C-N Rift providing support for a crack interaction model in which crack initiation at the EPR axis is controlled by stresses associated with the tip of the westward-propagating C-N Rift. The model also shows that offsets of the EPR axis may explain times when cracking is not symmetric. South of C-N Rift, cracks are observed on seafloor as old as 10.5 Ma suggesting that this triple junction has not been a simple RRR triple junction during that time.

Predicting the 3D fatigue crack growth rate of small cracks using multimodal data via Bayesian networks: In-situ experiments and crystal plasticity simulations

NASA Astrophysics Data System (ADS)

Rovinelli, Andrea; Sangid, Michael D.; Proudhon, Henry; Guilhem, Yoann; Lebensohn, Ricardo A.; Ludwig, Wolfgang

2018-06-01

Small crack propagation accounts for most of the fatigue life of engineering structures subject to high cycle fatigue loading conditions. Determining the fatigue crack growth rate of small cracks propagating into polycrystalline engineering alloys is critical to improving fatigue life predictions, thus lowering cost and increasing safety. In this work, cycle-by-cycle data of a small crack propagating in a beta metastable titanium alloy is available via phase and diffraction contrast tomography. Crystal plasticity simulations are used to supplement experimental data regarding the micromechanical fields ahead of the crack tip. Experimental and numerical results are combined into a multimodal dataset and sampled utilizing a non-local data mining procedure. Furthermore, to capture the propensity of body-centered cubic metals to deform according to the pencil-glide model, a non-local driving force is postulated. The proposed driving force serves as the basis to construct a data-driven probabilistic crack propagation framework using Bayesian networks as building blocks. The spatial correlation between the postulated driving force and experimental observations is obtained by analyzing the results of the proposed framework. Results show that the above correlation increases proportionally to the distance from the crack front until the edge of the plastic zone. Moreover, the predictions of the propagation framework show good agreement with experimental observations. Finally, we studied the interaction of a small crack with grain boundaries (GBs) utilizing various slip transmission criteria, revealing the tendency of a crack to cross a GB by propagating along the slip directions minimizing the residual Burgers vector within the GB.

Predicting the 3D fatigue crack growth rate of small cracks using multimodal data via Bayesian networks: In-situ experiments and crystal plasticity simulations

DOE PAGES

Rovinelli, Andrea; Sangid, Michael D.; Proudhon, Henry; ...

2018-03-11

Small crack propagation accounts for most of the fatigue life of engineering structures subject to high cycle fatigue loading conditions. Determining the fatigue crack growth rate of small cracks propagating into polycrystalline engineering alloys is critical to improving fatigue life predictions, thus lowering cost and increasing safety. In this work, cycle-by-cycle data of a small crack propagating in a beta metastable titanium alloy is available via phase and diffraction contrast tomography. Crystal plasticity simulations are used to supplement experimental data regarding the micromechanical fields ahead of the crack tip. Experimental and numerical results are combined into a multimodal dataset andmore » sampled utilizing a non-local data mining procedure. Furthermore, to capture the propensity of body-centered cubic metals to deform according to the pencil-glide model, a non-local driving force is postulated. The proposed driving force serves as the basis to construct a data-driven probabilistic crack propagation framework using Bayesian networks as building blocks. The spatial correlation between the postulated driving force and experimental observations is obtained by analyzing the results of the proposed framework. Results show that the above correlation increases proportionally to the distance from the crack front until the edge of the plastic zone. Moreover, the predictions of the propagation framework show good agreement with experimental observations. Finally, we studied the interaction of a small crack with grain boundaries (GBs) utilizing various slip transmission criteria, revealing the tendency of a crack to cross a GB by propagating along the slip directions minimizing the residual Burgers vector within the GB.« less

The interaction of fatigue cracks with a residual stress field using thermoelastic stress analysis and synchrotron X-ray diffraction experiments

PubMed Central

Amjad, Khurram; Asquith, David; Sebastian, Christopher M.; Wang, Wei-Chung

2017-01-01

This article presents an experimental study on the fatigue behaviour of cracks emanating from cold-expanded holes utilizing thermoelastic stress analysis (TSA) and synchrotron X-ray diffraction (SXRD) techniques with the aim of resolving the long-standing ambiguity in the literature regarding potential relaxation, or modification, of beneficial compressive residual stresses as a result of fatigue crack propagation. The crack growth rates are found to be substantially lower as the crack tip moved through the residual stress zone induced by cold expansion. The TSA results demonstrated that the crack tip plastic zones were reduced in size by the presence of the residual compressive stresses induced by cold expansion. The crack tip plastic zones were found to be insignificant in size in comparison to the residual stress zone resulting from cold expansion, which implied that they were unlikely to have had a notable impact on the surrounding residual stresses induced by cold expansion. The residual stress distributions measured along the direction of crack growth, using SXRD, showed no signs of any significant stress relaxation or redistribution, which validates the conclusions drawn from the TSA data. Fractographic analysis qualitatively confirmed the influence on crack initiation of the residual stresses induced by the cold expansion. It was found that the application of single compressive overload caused a relaxation, or reduction in the residual stresses, which has wider implications for improving the fatigue life. PMID:29291095

Hardness properties and microscopic investigation of crack- crystal interaction in SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F glass ceramic system.

PubMed

Roy, Shibayan; Basu, Bikramjit

2010-01-01

In view of the potential engineering applications requiring machinability and wear resistance, the present work focuses to evaluate hardness property and to understand the damage behavior of some selected glass-ceramics having different crystal morphologies with SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F composition, using static micro-indentation tests as well as dynamic scratch tests, respectively. Vickers hardness of up to 5.5 GPa has been measured in glass-ceramics containing plate like mica crystals. Scratch tests at a high load of 50 Nin artificial saliva were carried out in order to simulate the crack-microstructure interaction during real-time abrasion wear and machining operation. The experimental observations indicate that the novel "spherulitic-dendritic shaped "crystals, similar to the plate like crystals, have the potential to hinder the scratching induced crack propagation. In particular, such potential of the 'spherulitic-dendritic' crystals become more effective due to the larger interfacial area with the glass matrix as well as the dendritic structure of each mica plate, which helps in crack deflection and crack blunting, to a larger extent.While modest damage tolerant behavior is observed in case of 'spherulitic-dendritic' crystal containing material, severe brittle fracture of plate like crystals were noted, when both were scratched at 50 N load.

Measurement and visualization of face-to-face interaction among community-dwelling older adults using wearable sensors.

PubMed

Masumoto, Kouhei; Yaguchi, Takaharu; Matsuda, Hiroshi; Tani, Hideaki; Tozuka, Keisuke; Kondo, Narihiko; Okada, Shuichi

2017-10-01

A number of interventions have been undertaken to develop and promote social networks among community-dwelling older adults. However, it has been difficult to examine the effects of these interventions, because of problems in assessing interactions. The present study was designed to quantitatively measure and visualize face-to-face interactions among elderly participants in an exercise program. We also examined relationships among interactional variables, personality and interest in community involvement, including interactions with the local community. Older adults living in the same community were recruited to participate in an exercise program that consisted of four sessions. We collected data on face-to-face interactions of the participants by using a wearable sensor technology device. Network analysis identified the communication networks of participants in the exercise program, as well as changes in these networks. Additionally, there were significant correlations between the number of people involved in face-to-face interactions and changes in both interest in community involvement and interactions with local community residents, as well as personality traits, including agreeableness. Social networks in the community are essential for solving problems caused by the aging society. We showed the possible applications of face-to-face interactional data for identifying core participants having many interactions, and isolated participants having only a few interactions within the community. Such data would be useful for carrying out efficient interventions for increasing participants' involvement with their community. Geriatr Gerontol Int 2017; 17: 1752-1758. © 2017 Japan Geriatrics Society.

Fatigue crack growth behavior in equine cortical bone

NASA Astrophysics Data System (ADS)

Shelton, Debbie Renee

2001-07-01

Objectives for this research were to experimentally determine crack growth rates, da/dN, as a function of alternating stress intensity factor, DeltaK, for specimens from lateral and dorsal regions of equine third metacarpal cortical bone tissue, and to determine if the results were described by the Paris law. In one set of experiments, specimens were oriented for crack propagation in the circumferential direction with the crack plane transverse to the long axis of the bone. In the second set of experiments, specimens were oriented for radial crack growth with the crack plane parallel to the long axis of the bone. Results of fatigue tests from the latter specimens were used to evaluate the hypothesis that crack growth rates differ regionally. The final experiments were designed to determine if crack resistance was dependent on region, proportion of hooped osteons (those with circumferentially oriented collagen fibers in the outer lamellae) or number of osteons penetrated by the crack, and to address the hypothesis that hooped osteons resist invasion by cracks better than other osteonal types. The transverse crack growth data for dorsal specimens were described by the Paris law with an exponent of 10.4 and suggested a threshold stress intensity factor, DeltaKth, of 2.0 MPa·m1/2 and fracture toughness of 4.38 MPa·m 1/2. Similar results were not obtained for lateral specimens because the crack always deviated from the intended path and ran parallel to the loading direction. Crack growth for the dorsal and lateral specimens in the radial orientation was described by the Paris law with exponents of 8.7 and 10.2, respectively, and there were no regional differences in the apparent DeltaK th (0.5 MPa·m1/2) or fracture toughness (1.2 MPa·m 1/2). Crack resistance was not associated with cortical region, proportion of hooped osteons or the number of osteons penetrated by the crack. The extent to which cracks penetrate osteons was influenced by whether the collagen fiber orientation in the outer osteon layers was circumferential or longitudinal. The majority of hooped osteons were skirted by the crack. The angle of interaction between the osteon and the crack was also significant in determining whether an osteon was penetrated.

Geometry and Material Constraint Effects on Creep Crack Growth Behavior in Welded Joints

NASA Astrophysics Data System (ADS)

Li, Y.; Wang, G. Z.; Xuan, F. Z.; Tu, S. T.

2017-02-01

In this work, the geometry and material constraint effects on creep crack growth (CCG) and behavior in welded joints were investigated. The CCG paths and rates of two kinds of specimen geometry (C(T) and M(T)) with initial cracks located at soft HAZ (heat-affected zone with lower creep strength) and different material mismatches were simulated. The effect of constraint on creep crack initiation (CCI) time was discussed. The results show that there exists interaction between geometry and material constraints in terms of their effects on CCG rate and CCI time of welded joints. Under the condition of low geometry constraint, the effect of material constraint on CCG rate and CCI time becomes more obvious. Higher material constraint can promote CCG due to the formation of higher stress triaxiality around crack tip. Higher geometry constraint can increase CCG rate and reduce CCI time of welded joints. Both geometry and material constraints should be considered in creep life assessment and design for high-temperature welded components.

Buckling of Cracked Laminated Composite Cylindrical Shells Subjected to Combined Loading

NASA Astrophysics Data System (ADS)

Allahbakhsh, Hamidreza; Shariati, Mahmoud

2013-10-01

A series of finite element analysis on the cracked composite cylindrical shells under combined loading is carried out to study the effect of loading condition, crack size and orientation on the buckling behavior of laminated composite cylindrical shells. The interaction buckling curves of cracked laminated composite cylinders subject to different combinations of axial compression, bending, internal pressure and external pressure are obtained, using the finite element method. Results show that the internal pressure increases the critical buckling load of the CFRP cylindrical shells and bending and external pressure decrease it. Numerical analysis show that axial crack has the most detrimental effect on the buckling load of a cylindrical shell and results show that for lower values of the axial compressive load and higher values of the external pressure, the buckling is usually in the global mode and for higher values of axial compressive load and lower levels of external pressure the buckling mode is mostly in the local mode.

Expressing and negotiating face in community pharmacist-patient interactions.

PubMed

Murad, Muna S; Spiers, Judith A; Guirguis, Lisa M

2017-11-01

A collaborative patient-pharmacist interaction is fundamental to greater patient satisfaction with pharmacy care and improved medication adherence. Effective pharmacist-patient communication occurs when both pharmacist and patient are able to successfully attend to not only the typical tasks and goals of the interaction but also basic face needs that underlie all social interaction; autonomy, competence or esteem, and fellowship. Addressing face needs occurs through conventional and strategic communication strategies that respond to the emerging needs throughout an interaction. Pharmacist-patient interactions are not just about transfer of information and medications. Both parties assess the situation, the others' intentions within the context of their own goals and this influences how they choose to act throughout the interaction. Face-work Theory provides a framework to understand these interaction processes in pharmacist-patient communication. The aim of this study was to determine face needs, threats and the strategic communication strategies used to address these within community pharmacist-patient interactions. This exploratory descriptive study drew upon principles of ethology to first describe naturally occurring behaviour and then to interpret this behaviour within the context of Face-work theory. Twenty-five audio-recorded community pharmacist-patient interactions were collected and analyzed. The average length of these interactions was 3:67 min with a range of 0.39 s-9:35 min. Multiple face needs for both pharmacist and patient were evident in most interactions. Autonomy, competence and fellowship face needs were negotiated in the following contexts: participative relationships, concordant role expectations, sensitive topics, and negotiating expertise and knowledge. Competence face needs for both parties were the most dominant need found in negotiating role expectations. The most common communication strategies used to support face were solidarity based strategies while indirect and depersonalized questions were commonly employed to mitigate face threat. Face-work Theory is a novel approach to understand processes and outcomes of patient-pharmacist interactions in community pharmacies. Linking speech acts with face needs and threats may help to elucidate how pharmacist-patient interactions achieve both task oriented and interpersonal goals. Copyright © 2016 Elsevier Inc. All rights reserved.

Failure study of helium-cooled tungsten divertor plasma-facing units tested at DEMO relevant steady-state heat loads

NASA Astrophysics Data System (ADS)

Ritz, G.; Hirai, T.; Norajitra, P.; Reiser, J.; Giniyatulin, R.; Makhankov, A.; Mazul, I.; Pintsuk, G.; Linke, J.

2009-12-01

Tungsten was selected as armor material for the helium-cooled divertor in future DEMO-type fusion reactors and fusion power plants. After realizing the design and testing of them under cyclic thermal loads of up to ~14 MW m-2, the tungsten divertor plasma-facing units were examined by metallography; they revealed failures such as cracks at the thermal loaded and as-machined surfaces, as well as degradation of the brazing layers. Furthermore, in order to optimize the machining processes, the quality of tungsten surfaces prepared by turning, milling and using a diamond cutting wheel were examined. This paper presents a metallographic examination of the tungsten plasma-facing units as well as technical studies and the characterization on machining of tungsten and alternative brazing joints.

Optical enhancement of Au doped ZrO2 thin films by sol-gel dip coating method

NASA Astrophysics Data System (ADS)

John Berlin, I.; Joy, K.

2015-01-01

Homogeneous and transparent Au doped ZrO2 thin films were prepared by sol-gel dip coating method. The films have mixed phase of tetragonal, monoclinic and face centered cubic with crack free surface. Due to the increase in Au doping concentration many-body interaction occurs between free carriers and ionized impurities causing decrease in optical band gap from 5.72 to 5.40 eV. Localized surface plasmon resonance peak of the Au doped films appeared at 610 nm. Conversion of photons to surface plasmons allows the sub-wavelength manipulation of electromagnetic radiation. Hence the prepared Au doped ZrO2 thin films can be applied in nanoscale photonic devices such as lenses, switches, waveguides etc. Moreover the photoluminescence (PL) intensity of Au doped ZrO2 thin films decrease due to decrease in the radiative recombination, life time of the excitons and suppression of grain growth of ZrO2 with increasing Au dopant.

Improved Fabrication of Ceramic Matrix Composite/Foam Core Integrated Structures

NASA Technical Reports Server (NTRS)

Hurwitz, Frances I.

2009-01-01

The use of hybridized carbon/silicon carbide (C/SiC) fabric to reinforce ceramic matrix composite face sheets and the integration of such face sheets with a foam core creates a sandwich structure capable of withstanding high-heatflux environments (150 W/cm2) in which the core provides a temperature drop of 1,000 C between the surface and the back face without cracking or delamination of the structure. The composite face sheet exhibits a bilinear response, which results from the SiC matrix not being cracked on fabrication. In addition, the structure exhibits damage tolerance under impact with projectiles, showing no penetration to the back face sheet. These attributes make the composite ideal for leading edge structures and control surfaces in aerospace vehicles, as well as for acreage thermal protection systems and in high-temperature, lightweight stiffened structures. By tailoring the coefficient of thermal expansion (CTE) of a carbon fiber containing ceramic matrix composite (CMC) face sheet to match that of a ceramic foam core, the face sheet and the core can be integrally fabricated without any delamination. Carbon and SiC are woven together in the reinforcing fabric. Integral densification of the CMC and the foam core is accomplished with chemical vapor deposition, eliminating the need for bond-line adhesive. This means there is no need to separately fabricate the core and the face sheet, or to bond the two elements together, risking edge delamination during use. Fibers of two or more types are woven together on a loom. The carbon and ceramic fibers are pulled into the same pick location during the weaving process. Tow spacing may be varied to accommodate the increased volume of the combined fiber tows while maintaining a target fiber volume fraction in the composite. Foam pore size, strut thickness, and ratio of face sheet to core thickness can be used to tailor thermal and mechanical properties. The anticipated CTE for the hybridized composite is managed by the choice of constituents, varying fiber tow sizes and constituent part ratios. This structural concept provides high strength and stiffness at low density 1.06 g/cm3 in panels tested. Varieties of face sheet constructions are possible, including variations in fiber type and weave geometry. The integrated structures possible with this composite could eliminate the need for non-load-bearing thermal protection systems on top of a structural component. The back sheet can readily be integrated to substructures through the incorporation of ribs. This would eliminate weight and cost for aerospace missions.

Inert Welding/Brazing Gas Filters and Dryers

NASA Technical Reports Server (NTRS)

Goudy, Jerry

2009-01-01

The use of hybridized carbon/silicon carbide (C/SiC) fabric to reinforce ceramic matrix composite face sheets and the integration of such face sheets with a foam core creates a sandwich structure capable of withstanding high-heat-flux environments (150 W/sq cm) in which the core provides a temperature drop of 1,000 C between the surface and the back face without cracking or delamination of the structure. The composite face sheet exhibits a bilinear response, which results from the SiC matrix not being cracked on fabrication. In addition, the structure exhibits damage tolerance under impact with projectiles, showing no penetration to the back face sheet. These attributes make the composite ideal for leading-edge structures and control surfaces in aerospace vehicles, as well as for acreage thermal protection systems and in high-temperature, lightweight stiffened structures. By tailoring the coefficient of thermal expansion (CTE) of a carbon fiber containing ceramic matrix composite (CMC) face sheet to match that of a ceramic foam core, the face sheet and the core can be integrally fabricated without any delamination. Carbon and SiC are woven together in the reinforcing fabric. Integral densification of the CMC and the foam core is accomplished with chemical vapor deposition, eliminating the need for bond-line adhesive. This means there is no need to separately fabricate the core and the face sheet, or to bond the two elements together, risking edge delamination during use. Fibers of two or more types are woven together on a loom. The carbon and ceramic fibers are pulled into the same "pick" location during the weaving process. Tow spacing may be varied to accommodate the increased volume of the combined fiber tows while maintaining a target fiber volume fraction in the composite. Foam pore size, strut thickness, and ratio of face sheet to core thickness can be used to tailor thermal and mechanical properties. The anticipated CTE for the hybridized composite is managed by the choice of constituents, varying fiber tow sizes and constituent part ratios. This structural concept provides high strength and stiffness at low density 1.06 g/cu cm in panels tested. Varieties of face sheet constructions are possible, including variations in fiber type and weave geometry. The integrated structures possible with this composite could eliminate the need for non-load-bearing thermal protection systems on top of a structural component. The back sheet can readily be integrated to substructures through the incorporation of ribs. This would eliminate weight and cost for aerospace missions.

Fatigue crack growth in 7475-T651 aluminum alloy plate in hard vacuum and water vapor. M.S. Thesis - George Washington Univ.

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1981-01-01

Compact specimens of 25 mm thick aluminum alloy plate were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Crack growth rates were determined at frequencies of 1 Hz and 10 Hz in hard vacuum and laboratory air, and in mixtures of water vapor and nitrogen at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. A significant effect of water vapor on fatigue crack growth rates was observed at the lowest water vapor pressure tested. Crack rates changed little for pressures up to 1.03 kPa, but abruptly accelerated at higher pressures. At low stress intensity factor ranges, cracking rates at the lowest and highest water vapor pressure tested were, respectively, two and five times higher than rates in vacuum. Although a frequency was observed in laboratory air, cracking rates in water vapor and vacuum are insensitive to a ten-fold change in frequency. Surfaces of specimens tested in water vapor and vacuum exhibited different amounts of residual deformation. Reduced deformation on the fracture surfaces of the specimens tested in water vapor suggests embrittlement of the plastic zone ahead of the crack tip as a result of environmental interaction.

Fracture under combined modes in 4340 steel

NASA Technical Reports Server (NTRS)

Shah, R. C.

1974-01-01

An experimental investigation was conducted to study the interaction of combined modes of loading on crack instability in the presence of the opening and sliding modes of stress intensity factors, the opening and tearing modes of stress intensity factors, and all three modes of stress intensity factors. Through-cracked and surface-cracked flat and round specimens, and round notched bar specimens fabricated from high strength 4340 steel were used for the investigation. The results are evaluated to determine fracture criteria under the combined modes of stress intensity factors for the 4340 steel. These results are compared with the results of other investigators obtained for different materials.

An analytical approach for the calculation of stress-intensity factors in transformation-toughened ceramics

NASA Astrophysics Data System (ADS)

Müller, W. H.

1990-12-01

Stress-induced transformation toughening in Zirconia-containing ceramics is described analytically by means of a quantitative model: A Griffith crack which interacts with a transformed, circular Zirconia inclusion. Due to its volume expansion, a ZrO2-particle compresses its flanks, whereas a particle in front of the crack opens the flanks such that the crack will be attracted and finally absorbed. Erdogan's integral equation technique is applied to calculate the dislocation functions and the stress-intensity-factors which correspond to these situations. In order to derive analytical expressions, the elastic constants of the inclusion and the matrix are assumed to be equal.

Gaze Aversion during Social Style Interactions in Autism Spectrum Disorder and Williams Syndrome

ERIC Educational Resources Information Center

Doherty-Sneddon, Gwyneth; Whittle, Lisa; Riby, Deborah M.

2013-01-01

During face-to-face interactions typically developing individuals use gaze aversion (GA), away from their questioner, when thinking. GA is also used when individuals with autism (ASD) and Williams syndrome (WS) are thinking during question-answer interactions. We investigated GA strategies during face-to-face social style interactions with…

Near-Field Acoustical Imaging using Lateral Bending Mode of Atomic Force Microscope Cantilevers

NASA Astrophysics Data System (ADS)

Caron, A.; Rabe, U.; Rödel, J.; Arnold, W.

Scanning probe microscopy techniques enable one to investigate surface properties such as contact stiffness and friction between the probe tip and a sample with nm resolution. So far the bending and the torsional eigenmodes of an atomic force microscope cantilever have been used to image variations of elasticity and shear elasticity, respectively. Such images are near-field images with the resolution given by the contact radius typically between 10 nm and 50 nm. We show that the flexural modes of a cantilever oscillating in the width direction and parallel to the sample surface can also be used for imaging. Additional to the dominant in-plane component of the oscillation, the lateral modes exhibit a vertical component as well, provided there is an asymmetry in the cross-section of the cantilever or in its suspension. The out-of-plane deflection renders the lateral modes detectable by the optical position sensors used in atomic force microscopes. We studied cracks which were generated by Vickers indents, in submicro- and nanocrystalline ZrO2. Images of the lateral contact stiffness were obtained by vibrating the cantilever close to a contact-resonance frequency. A change in contact stiffness causes a shift of the resonant frequency and hence a change of the cantilever vibration amplitude. The lateral contact-stiffness images close to the crack faces display a contrast that we attribute to altered elastic properties indicating a process zone. This could be caused by a stress-induced phase transformation during crack propagation. Using the contact mode of an atomic force microscope, we measured the crack-opening displacement as a function of distance from the crack tip, and we determined the crack-tip toughness Ktip. Furthermore, K1c was inferred from the length of radial cracks of Vickers indents that were measured using classical scanning acoustic microscopy

Mechanistic Analysis of Mechano-Electrochemical Interaction in Silicon Electrodes with Surface Film

DOE Office of Scientific and Technical Information (OSTI.GOV)

Verma, Ankit; Mukherjee, Partha P.

2017-11-17

High-capacity anode materials for lithium-ion batteries, such as silicon, are prone to large volume change during lithiation/delithiation which may cause particle cracking and disintegration, thereby resulting in severe capacity fade and reduction in cycle life. In this work, a stochastic analysis is presented in order to understand the mechano-electrochemical interaction in silicon active particles along with a surface film during cycling. Amorphous silicon particles exhibiting single-phase lithiation incur lower amount of cracking as compared to crystalline silicon particles exhibiting two-phase lithiation for the same degree of volumetric expansion. Rupture of the brittle surface film is observed for both amorphous andmore » crystalline silicon particles and is attributed to the large volumetric expansion of the silicon active particle with lithiation. The mechanical property of the surface film plays an important role in determining the amount of degradation in the particle/film assembly. A strategy to ameliorate particle cracking in silicon active particles is proposed.« less

Experimental Characterization and Simulation of Slip Transfer at Grain Boundaries and Microstructurally-Sensitive Crack Propagation

NASA Technical Reports Server (NTRS)

Gupta, Vipul; Hochhalter, Jacob; Yamakov, Vesselin; Scott, Willard; Spear, Ashley; Smith, Stephen; Glaessgen, Edward

2013-01-01

A systematic study of crack tip interaction with grain boundaries is critical for improvement of multiscale modeling of microstructurally-sensitive fatigue crack propagation and for the computationally-assisted design of more durable materials. In this study, single, bi- and large-grain multi-crystal specimens of an aluminum-copper alloy are fabricated, characterized using electron backscattered diffraction (EBSD), and deformed under tensile loading and nano-indentation. 2D image correlation (IC) in an environmental scanning electron microscope (ESEM) is used to measure displacements near crack tips, grain boundaries and within grain interiors. The role of grain boundaries on slip transfer is examined using nano-indentation in combination with high-resolution EBSD. The use of detailed IC and EBSD-based experiments are discussed as they relate to crystal-plasticity finite element (CPFE) model calibration and validation.

Heavy section fracture toughness screening specimen

NASA Technical Reports Server (NTRS)

Shannon, J. L., Jr.; Donald, J. K.; Brown, W. F., Jr.

1976-01-01

Size requirements for a pin loaded double edge notch + crack tension specimen proposed for fracture toughness screening heavy section alloys were studied. Ranking of eight selected alloys based on the specimen's net strength was compared with that based on the valid plane strain fracture toughness separately determined. Performance of the specimen was judged on the basis of that comparison. The specimen's net strength was influenced by three critical specimen dimensions: distance between the crack plane and the loading hole, specimen width, and specimen thickness. Interaction between the stress fields of the crack and the loading holes reduced the net strength, but this effect disappeared as the separation reached a dimension equal to the specimen width. The effects of specimen width and thickness are interrelated and affect the net strength through their influence on the development of the crack tip plastic zone.

Advanced quantitative magnetic nondestructive evaluation methods - Theory and experiment

NASA Technical Reports Server (NTRS)

Barton, J. R.; Kusenberger, F. N.; Beissner, R. E.; Matzkanin, G. A.

1979-01-01

The paper reviews the scale of fatigue crack phenomena in relation to the size detection capabilities of nondestructive evaluation methods. An assessment of several features of fatigue in relation to the inspection of ball and roller bearings suggested the use of magnetic methods; magnetic domain phenomena including the interaction of domains and inclusions, and the influence of stress and magnetic field on domains are discussed. Experimental results indicate that simplified calculations can be used to predict many features of these results; the data predicted by analytic models which use finite element computer analysis predictions do not agree with respect to certain features. Experimental analyses obtained on rod-type fatigue specimens which show experimental magnetic measurements in relation to the crack opening displacement and volume and crack depth should provide methods for improved crack characterization in relation to fracture mechanics and life prediction.

Effects of insolation on habitability and the isotopic history of Martian water

NASA Astrophysics Data System (ADS)

Moores, John

Three aspects of the Habitability of the Northern Plains of Mars to organics and terrestrial-like microbial life were assessed. (1) Protection offered by small surface features and; (2) the breakdown of rocks to form soils were examined using a radiative transfer computer model. Two separate sublimation experiments provided a basis to improve; (3) estimates of the amount of available water today and in the past by determining the fractionation of HDO between present-day reservoirs. (1) UV radiation sterilizes the hardiest of terrestrial organisms within minutes on the Martian surface. Small surface features including pits, trenches, flat faces and overhangs may create "safe havens" for organisms by blocking much of the UV flux. In the most favorable cases, this flux is sufficiently reduced such that organic in-fall could accumulate beneath overhanging surfaces and in pits and cracks while terrestrial microorganisms could persist for several tens of martian years. (2) The production of soils on the surface is considered by analogy with the arid US Southwest. Here differential insolation of incipient cracks of random orientations predicts crack orientation distributions consistent with field observations by assuming that only crack orientations which shield their interiors, minimizing their water loss, can grow, eventually disrupting the clast. (3) Disaggregated water ice to simulate the polar caps was produced by flash freezing in liquid nitrogen and crushing. When dust was added to the mixtures, the D/H ratio of the sublimate gas was seen to decrease with time from the bulk ratio. The more dust was added to the mixture, the more pronounced was this effect. The largest fractionation factor observed during these experiments was 2.5. Clean ice was also prepared and overlain by dust to simulate ground ice. Here, the movement of water vapor was modeled using an effective diffusivity that incorporated both adsorption on grains and diffusion. For low temperatures (<-55°C) a significant difference between the diffusivities of H 2 O and HDO was observed. This suggests adsorptive-control within the regolith as energies of interaction are 60-70kJmol -1 . This ability of the martian regolith to preferentially adsorb HDO decouples the ice table and polar caps from the atmosphere and allows for geographic variations in the D/H ratio on Mars.

A Fracture-Mechanical Model of Crack Growth and Interaction: Application to Pre-eruptive Seismicity

NASA Astrophysics Data System (ADS)

Matthews, C.; Sammonds, P.; Kilburn, C.

2007-12-01

A greater understanding of the physical processes occurring within a volcano is a key aspect in the success of eruption forecasting. By considering the role of fracture growth, interaction and coalescence in the formation of dykes and conduits as well as the source mechanism for observed seismicity we can create a more general, more applicable model for precursory seismicity. The frequency of volcano-tectonic earthquakes, created by fracturing of volcanic rock, often shows a short-term increase prior to eruption. Using fracture mechanics, the model presented here aims to determine the conditions necessary for the acceleration in fracture events which produces the observed pre-eruptive seismicity. By focusing on the cause of seismic events rather than simply the acceleration patterns observed, the model also highlights the distinction between an accelerating seismic sequence ending with an eruption and a short-term increase which returns to background levels with no activity occurring, an event also observed in the field and an important capability if false alarms are to be avoided. This 1-D model explores the effects of a surrounding stress field and the distribution of multi-scale cracks on the interaction and coalescence of these cracks to form an open pathway for magma ascent. Similarly to seismic observations in the field, and acoustic emissions data from the laboratory, exponential and hyperbolic accelerations in fracturing events are recorded. Crack distribution and inter-crack distance appears to be a significant controlling factor on the evolution of the fracture network, dominating over the effects of a remote stress field. The generality of the model and its basis on fundamental fracture mechanics results makes it applicable to studies of fracture networks in numerous situations. For example looking at the differences between high temperature fracture processes and purely brittle failure the model can be similarly applied to fracture dynamics in the edifice of a long repose volcano and a lava dome.

Preliminary results on the fracture analysis of multi-site cracking of lap joints in aircraft skins

NASA Astrophysics Data System (ADS)

Beuth, J. L., Jr.; Hutchinson, John W.

1992-07-01

Results of a fracture mechanics analysis relevant to fatigue crack growth at rivets in lap joints of aircraft skins are presented. Multi-site damage (MSD) is receiving increased attention within the context of problems of aging aircraft. Fracture analyses previously carried out include small-scale modeling of rivet/skin interactions, larger-scale two-dimensional models of lap joints similar to that developed here, and full scale three-dimensional models of large portions of the aircraft fuselage. Fatigue testing efforts have included flat coupon specimens, two-dimensional lap joint tests, and full scale tests on specimens designed to closely duplicate aircraft sections. Most of this work is documented in the proceedings of previous symposia on the aging aircraft problem. The effect MSD has on the ability of skin stiffeners to arrest the growth of long skin cracks is a particularly important topic that remains to be addressed. One of the most striking features of MSD observed in joints of some test sections and in the joints of some of the older aircraft fuselages is the relative uniformity of the fatigue cracks from rivet to rivet along an extended row of rivets. This regularity suggests that nucleation of the cracks must not be overly difficult. Moreover, it indicates that there is some mechanism which keeps longer cracks from running away from shorter ones, or, equivalently, a mechanism for shorter cracks to catch-up with longer cracks. This basic mechanism has not been identified, and one of the objectives of the work is to see to what extent the mechanism is revealed by a fracture analysis of the MSD cracks. Another related aim is to present accurate stress intensity factor variations with crack length which can be used to estimate fatigue crack growth lifetimes once cracks have been initiated. Results are presented which illustrate the influence of load shedding from rivets with long cracks to neighboring rivets with shorter cracks. Results are also included for the effect of residual stress due to the riveting process itself.

Preliminary results on the fracture analysis of multi-site cracking of lap joints in aircraft skins

NASA Technical Reports Server (NTRS)

Beuth, J. L., Jr.; Hutchinson, John W.

1992-01-01

Results of a fracture mechanics analysis relevant to fatigue crack growth at rivets in lap joints of aircraft skins are presented. Multi-site damage (MSD) is receiving increased attention within the context of problems of aging aircraft. Fracture analyses previously carried out include small-scale modeling of rivet/skin interactions, larger-scale two-dimensional models of lap joints similar to that developed here, and full scale three-dimensional models of large portions of the aircraft fuselage. Fatigue testing efforts have included flat coupon specimens, two-dimensional lap joint tests, and full scale tests on specimens designed to closely duplicate aircraft sections. Most of this work is documented in the proceedings of previous symposia on the aging aircraft problem. The effect MSD has on the ability of skin stiffeners to arrest the growth of long skin cracks is a particularly important topic that remains to be addressed. One of the most striking features of MSD observed in joints of some test sections and in the joints of some of the older aircraft fuselages is the relative uniformity of the fatigue cracks from rivet to rivet along an extended row of rivets. This regularity suggests that nucleation of the cracks must not be overly difficult. Moreover, it indicates that there is some mechanism which keeps longer cracks from running away from shorter ones, or, equivalently, a mechanism for shorter cracks to catch-up with longer cracks. This basic mechanism has not been identified, and one of the objectives of the work is to see to what extent the mechanism is revealed by a fracture analysis of the MSD cracks. Another related aim is to present accurate stress intensity factor variations with crack length which can be used to estimate fatigue crack growth lifetimes once cracks have been initiated. Results are presented which illustrate the influence of load shedding from rivets with long cracks to neighboring rivets with shorter cracks. Results are also included for the effect of residual stress due to the riveting process itself.

Transient cracks and triple junctions induced by Cocos-Nazca propagating rift

NASA Astrophysics Data System (ADS)

Schouten, H.; Smith, D. K.; Zhu, W.; Montesi, L. G.; Mitchell, G. A.; Cann, J. R.

2009-12-01

The Galapagos triple junction is a ridge-ridge-ridge triple junction where the Cocos, Nazca, and Pacific plates meet around the Galapagos microplate (GMP). On the Cocos plate, north of the large gore that marks the propagating Cocos-Nazca (C-N) Rift, a 250-km-long and 50-km-wide band of NW-SE-trending cracks crosscuts the N-S-trending abyssal hills of the East Pacific Rise (EPR). These appear as a succession of minor rifts, accommodating some NE-SW extension of EPR-generated seafloor. The rifts successively intersected the EPR in triple junctions at distances of 50-100 km north of the tip of the C-N Rift. We proposed a simple crack interaction model to explain the location of the transient rifts and their junction with the EPR. The model predicts that crack locations are controlled by the stress perturbation along the EPR, induced by the dominant C-N Rift, and scaled by the distance of its tip to the EPR (Schouten et al., 2008). The model also predicts that tensile stresses are symmetric about the C-N Rift and thus, similar cracks should have occurred south of the C-N Rift prior to formation of the GMP about 1 Ma. There were no data at the time to test this prediction. In early 2009 (AT 15-41), we mapped an area on the Nazca plate south of the C-N rift out to 4 Ma. The new bathymetric data confirm the existence of a distinctive pattern of cracks south of the southern C-N gore that mirrors the pattern on the Cocos plate until about 1 Ma, and lends support to the crack interaction model. The envelope of the symmetric cracking pattern indicates that the distance between the C-N Rift tip and the EPR varied between 40 and 65 km during this time (1-4 Ma). The breakdown of the symmetry at 1 Ma accurately dates the onset of a southern plate boundary of the GMP, now Dietz Deep Rift. At present, the southern rift boundary of the GMP joins the EPR with a steep-sided, 80 km long ridge. This ridge releases the stress perturbation otherwise induced along the EPR by elastic interaction with the C-N Rift and prevents the formation of minor rifts of the type in the North of the C-N Rift. However, the seafloor displays traces of rifts formed as the Dietz Deep Rift was approaching the EPR. In fact, the present day ridge appears to have originated as one of these minor rifts, probably stabilized by enhanced magma supply from a nearby volcano at the southwestern end of Dietz Deep.

Development and characterization of powder metallurgically produced discontinuous tungsten fiber reinforced tungsten composites

NASA Astrophysics Data System (ADS)

Mao, Y.; Coenen, J. W.; Riesch, J.; Sistla, S.; Almanstötter, J.; Jasper, B.; Terra, A.; Höschen, T.; Gietl, H.; Bram, M.; Gonzalez-Julian, J.; Linsmeier, Ch; Broeckmann, C.

2017-12-01

In future fusion reactors, tungsten is the prime candidate material for the plasma facing components. Nevertheless, tungsten is prone to develop cracks due to its intrinsic brittleness—a major concern under the extreme conditions of fusion environment. To overcome this drawback, tungsten fiber reinforced tungsten (Wf/W) composites are being developed. These composite materials rely on an extrinsic toughing principle, similar to those in ceramic matrix composite, using internal energy dissipation mechanisms, such as crack bridging and fiber pull-out, during crack propagation. This can help Wf/W to facilitate a pseudo-ductile behavior and allows an elevated damage resilience compared to pure W. For pseudo-ductility mechanisms to occur, the interface between the fiber and matrix is crucial. Recent developments in the area of powder-metallurgical Wf/W are presented. Two consolidation methods are compared. Field assisted sintering technology and hot isostatic pressing are chosen to manufacture the Wf/W composites. Initial mechanical tests and microstructural analyses are performed on the Wf/W composites with a 30% fiber volume fraction. The samples produced by both processes can give pseudo-ductile behavior at room temperature.

Interference among the Processing of Facial Emotion, Face Race, and Face Gender.

PubMed

Li, Yongna; Tse, Chi-Shing

2016-01-01

People can process multiple dimensions of facial properties simultaneously. Facial processing models are based on the processing of facial properties. The current study examined the processing of facial emotion, face race, and face gender using categorization tasks. The same set of Chinese, White and Black faces, each posing a neutral, happy or angry expression, was used in three experiments. Facial emotion interacted with face race in all the tasks. The interaction of face race and face gender was found in the race and gender categorization tasks, whereas the interaction of facial emotion and face gender was significant in the emotion and gender categorization tasks. These results provided evidence for a symmetric interaction between variant facial properties (emotion) and invariant facial properties (race and gender).

Interference among the Processing of Facial Emotion, Face Race, and Face Gender

PubMed Central

Li, Yongna; Tse, Chi-Shing

2016-01-01

People can process multiple dimensions of facial properties simultaneously. Facial processing models are based on the processing of facial properties. The current study examined the processing of facial emotion, face race, and face gender using categorization tasks. The same set of Chinese, White and Black faces, each posing a neutral, happy or angry expression, was used in three experiments. Facial emotion interacted with face race in all the tasks. The interaction of face race and face gender was found in the race and gender categorization tasks, whereas the interaction of facial emotion and face gender was significant in the emotion and gender categorization tasks. These results provided evidence for a symmetric interaction between variant facial properties (emotion) and invariant facial properties (race and gender). PMID:27840621

An equivalent domain integral for analysis of two-dimensional mixed mode problems

NASA Technical Reports Server (NTRS)

Raju, I. S.; Shivakumar, K. N.

1989-01-01

An equivalent domain integral (EDI) method for calculating J-integrals for two-dimensional cracked elastic bodies subjected to mixed mode loading is presented. The total and product integrals consist of the sum of an area or domain integral and line integrals on the crack faces. The EDI method gave accurate values of the J-integrals for two mode I and two mixed mode problems. Numerical studies showed that domains consisting of one layer of elements are sufficient to obtain accurate J-integral values. Two procedures for separating the individual modes from the domain integrals are presented. The procedure that uses the symmetric and antisymmetric components of the stress and displacement fields to calculate the individual modes gave accurate values of the integrals for all the problems analyzed.

Analysis of Surface and Subsurface Damage Morphology in Rotary Ultrasonic Machining of BK7 Glass

NASA Astrophysics Data System (ADS)

Hong-xiang, Wang; Chu, Wang; Jun-liang, Liu; Shi, Gao; Wen-Jie, Zhai

2017-11-01

This paper investigates the formation process of surface/subsurface damage in the rotary ultrasonic machining of BK7 glass. The results show that during the milling using the end face of the tool, the cutting depth and the residual height between the abrasive grains constantly change with the high-frequency vibration, generating lots of cracks on both sides of the scratches. The high-frequency vibration accelerates the chips falling from the surface, so that the chips and thermal damage are reduced, causing the grinding surface quality better. A plastic deformation area is formed during the grinding, due to the non-uniform cutting force on the material surface, and the residual stress is produced in the deformation area, inducing the median/lateral cracks.

Damage Characterization Using the Extended Finite Element Method for Structural Health Management

NASA Technical Reports Server (NTRS)

Krishnamurthy, Thiagarajan; Gallegos, Adam M.

2011-01-01

The development of validated multidisciplinary Integrated Vehicle Health Management (IVHM) tools, technologies, and techniques to enable detection, diagnosis, prognosis, and mitigation in the presence of adverse conditions during flight will provide effective solutions to deal with safety related challenges facing next generation aircraft. The adverse conditions include loss of control caused by environmental factors, actuator and sensor faults or failures, and damage conditions. A major concern in these structures is the growth of undetected damage/cracks due to fatigue and low velocity foreign impact that can reach a critical size during flight, resulting in loss of control of the aircraft. Hence, development of efficient methodologies to determine the presence, location, and severity of damage/cracks in critical structural components is highly important in developing efficient structural health management systems.

Cracking the Lavender Ceiling: Lesbian, Gay, and Bisexual Student Affairs Professionals and Their Personal Perspectives on Career Trajectory

ERIC Educational Resources Information Center

Smith, James Capshaw

2013-01-01

In higher education, the people working in student affairs are as diverse as the students who are served by these professionals. Those who identify as lesbian, gay, or bisexual are often faced with challenges to moving up the career ladder. Many who seek senior-level administrative positions, such as director, dean of students, vice president or…

Analysis and Design of Connections, Openings and Attachments for Protective Construction

DTIC Science & Technology

1989-10-01

precast connection details were subjected to cyclic simulated earthquake loads . The detail... column and beam flexural steel. At the onset of flexural yield under cyclical loading , crack sizes at the face of the joint increase and reinforcement... beam / column connections may be a necessity and can be placed without a great deal of difficulty. However, their placement in slab/wall connections

Crack turning in integrally stiffened aircraft structures

NASA Astrophysics Data System (ADS)

Pettit, Richard Glen

Current emphasis in the aircraft industry toward reducing manufacturing cost has created a renewed interest in integrally stiffened structures. Crack turning has been identified as an approach to improve the damage tolerance and fail-safety of this class of structures. A desired behavior is for skin cracks to turn before reaching a stiffener, instead of growing straight through. A crack in a pressurized fuselage encounters high T-stress as it nears the stiffener---a condition favorable to crack turning. Also, the tear resistance of aluminum alloys typically varies with crack orientation, a form of anisotropy that can influence the crack path. The present work addresses these issues with a study of crack turning in two-dimensions, including the effects of both T-stress and fracture anisotropy. Both effects are shown to have relation to the process zone size, an interaction that is central to this study. Following an introduction to the problem, the T-stress effect is studied for a slightly curved semi-infinite crack with a cohesive process zone, yielding a closed form expression for the future crack path in an infinite medium. For a given initial crack tip curvature and tensile T-stress, the crack path instability is found to increase with process zone size. Fracture orthotropy is treated using a simple function to interpolate between the two principal fracture resistance values in two-dimensions. An extension to three-dimensions interpolates between the six principal values of fracture resistance. Also discussed is the transition between mode I and mode II fracture in metals. For isotropic materials, there is evidence that the crack seeks out a direction of either local symmetry (pure mode I) or local asymmetry (pure mode II) growth. For orthotropic materials the favored states are not pure modal, and have mode mixity that is a function of crack orientation. Drawing upon these principles, two crack turning prediction approaches are extended to include fracture resistance orthotropy---a second-order linear elastic method with a characteristic length parameter to incorporate T-stress/process-zone effects, and an elastic-plastic method that uses the Crack Tip Opening Displacement (CTOD) to determine the failure response. Together with a novel method for obtaining enhanced accuracy T-stress calculations, these methods are incorporated into an adaptive-mesh, finite-element fracture simulation code. A total of 43 fracture tests using symmetrically and asymmetrically loaded double cantilever beam specimens were run to develop crack turning parameters and compare predicted and observed crack paths.

Multiaxial and thermomechanical fatigue considerations in damage tolerant design

NASA Technical Reports Server (NTRS)

Leese, G. E.; Bill, R. C.

1985-01-01

In considering damage tolerant design concepts for gas turbine hot section components, several challenging concerns arise: Complex multiaxial loading situations are encountered; Thermomechanical fatigue loading involving very wide temperature ranges is imposed on components; Some hot section materials are extremely anisotropic; and coatings and environmental interactions play an important role in crack propagation. The effects of multiaxiality and thermomechanical fatigue are considered from the standpoint of their impact on damage tolerant design concepts. Recently obtained research results as well as results from the open literature are examined and their implications for damage tolerant design are discussed. Three important needs required to advance analytical capabilities in support of damage tolerant design become readily apparent: (1) a theoretical basis to account for the effect of nonproportional loading (mechanical and mechanical/thermal); (2) the development of practical crack growth parameters that are applicable to thermomechanical fatigue situations; and (3) the development of crack growth models that address multiple crack failures.

The role of surface roughness on dislocation bending and stress evolution in low mobility AlGaN films during growth

NASA Astrophysics Data System (ADS)

Bardhan, Abheek; Mohan, Nagaboopathy; Chandrasekar, Hareesh; Ghosh, Priyadarshini; Sridhara Rao, D. V.; Raghavan, Srinivasan

2018-04-01

The bending and interaction of threading dislocations are essential to reduce their density for applications involving III-nitrides. Bending of dislocation lines also relaxes the compressive growth stress that is essential to prevent cracking on cooling down due to tensile thermal expansion mismatch stress while growing on Si substrates. It is shown in this work that surface roughness plays a key role in dislocation bending. Dislocations only bend and relax compressive stresses when the lines intersect a smooth surface. These films then crack. In rough films, dislocation lines which terminate at the bottom of the valleys remain straight. Compressive stresses are not relaxed and the films are relatively crack-free. The reasons for this difference are discussed in this work along with the implications on simultaneously meeting the requirements of films being smooth, crack free and having low defect density for device applications.

The surface crack problem in an orthotropic plate under bending and tension

NASA Technical Reports Server (NTRS)

Wu, Bing-Hua; Erdogan, F.

1987-01-01

The elasticity problem for an infinite orthotropic flat plate containing a series of through and part through cracks and subjected to bending and tension loads is considered. The problem is formulated by using Reissner's plate bending theory and considering three-dimensional material orthotropy. The Line-spring model developed by Rice and Levy is used to formulate the surface crack problem in which a total of nine material constants were used. The effects of material orthotropy on the stress intensity factors was determined, the interaction between two asymmetrically arranged collinear cracks was investigated, and extensive numerical results regarding the stress intensity factors are provided. The problem is reduced to a system of singular integral equations which is solved by using the Gauss-Chebyshev quadrature formulas. The calculated results show that the material orthotropy does have a significant effect on the stress intensity factor.

The surface crack problem in an orthotropic plate under bending and tension

NASA Technical Reports Server (NTRS)

Wu, B. H.; Erdogan, F.

1986-01-01

The elasticity problem for an infinite orthotropic flat plate containing a series of through and part-through cracks and subjected to bending and tension loads is considered. The problem is formulated by using Reissner's plate bending theory and considering three dimensional materials orthotropy. The Line-spring model developed by Rice and Levy is used to formulate the surface crack problem in which a total of nine material constants has been used. The main purpose of this study is to determine the effect of material orthotropy on the stress intensity factors, to investigate the interaction between two asymmetrically arranged collinear cracks, and to provide extensive numerical results regarding the stress intensity factors. The problem is reduced to a system of singular integral equations which is solved by using the Gauss-Chebyshev quadrature formulas. The calculated results show that the material orthotropy does have a significant effect on the stress intensity factor.

Multi-phase-field modeling of anisotropic crack propagation for polycrystalline materials

NASA Astrophysics Data System (ADS)

Nguyen, Thanh-Tung; Réthoré, Julien; Yvonnet, Julien; Baietto, Marie-Christine

2017-08-01

A new multi-phase-field method is developed for modeling the fracture of polycrystals at the microstructural level. Inter and transgranular cracking, as well as anisotropic effects of both elasticity and preferential cleavage directions within each randomly oriented crystal are taken into account. For this purpose, the proposed phase field formulation includes: (a) a smeared description of grain boundaries as cohesive zones avoiding defining an additional phase for grains; (b) an anisotropic phase field model; (c) a multi-phase field formulation where each preferential cleavage direction is associated with a damage (phase field) variable. The obtained framework allows modeling interactions and competition between grains and grain boundary cracks, as well as their effects on the effective response of the material. The proposed model is illustrated through several numerical examples involving a full description of complex crack initiation and propagation within 2D and 3D models of polycrystals.

Electrochemical Interpretation of a Stress Corrosion Cracking of Thermally Treated Ni base Alloys in a Lead Contaminated Water

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hwang, Seong Sik; Lim, Yun Soo; Kim, Hong Pyo

2007-08-20

Since the PbSCC(Lead stress corrosion cracking) of alloy 600 tubing materials was reported by Copson and Dean in 1965, the effect of lead on a corrosion film and cracking morphology have been continually debated. An electrochemical interaction of lead with the alloying elements of SG tubings was studied and the corrosion products were analyzed. It was found that lead enhanced the anodic dissolution of alloy 600 and alloy 690 in the electrochemical test. The lead preferentially dissolved the Cr from the corrosion film of alloy 600 and alloy 690 in alkaline water. The lead ion seemed to penetrate into themore » TG crack tip and react with the corrosion film. A selective Cr depletion was observed to weaken the stability of the passive film on the alloys. Whereas passivity of Ni became stable in lead containing solution, Cr and Fe passivity became unstable.« less

Review of the Effects of Microstructure on Fatigue in Aluminum Alloys. Ph.D. Thesis - Cincinnati Univ.

NASA Technical Reports Server (NTRS)

Telesman, J.

1984-01-01

Literature survey was conducted to determine the effects of different microstructural features and different load histories on fatigue crack initiation and propagation of aluminum alloys. Comparison of microstructure and monotonic and cyclic properties between powder metallurgy (P/M) and ingot metallurgy (I/M) alloys is presented. The two alloys that are representative of each process on which the comparison is focused are X7091 and 7050. Included is a detailed description of the microstructure produced through the P/M and I/M proesses. The effect of each pertinent microstructural feature on monotonic and cyclic properties, such as yield strength, toughness, crack initiation and propagation is discussed. Also discussed are the proposed mechanisms for crack initiation and propagation, as well as the effects of aggressive environments on these cyclic properties. The effects of variable amplitude loadin on fatigue crack propagation and the various models proposed to predict load interaction effects are discussed.

Fracture on Curved Surfaces

NASA Astrophysics Data System (ADS)

Mitchell, Noah; Koning, Vinzenz; Vitelli, Vincenzo; Irvine, William T. M.

2014-03-01

When an elastic film conforms to a surface with Gaussian curvature, stresses arise in the film. As a result, cracks--typically studied in flat materials--interact with curvature when propagating through the system. Using silicone elastomer sheets that conform to the surface of a Gaussian bump, we find experimental evidence for the deflection of a crack propagating through the material. We interpret our experiments with reference to analytical modeling and simulations of a simplified model system.

Correlation of microstructure, tensile properties and hole expansion ratio in cold rolled advanced high strength steels

NASA Astrophysics Data System (ADS)

Terrazas, Oscar R.

The demand for advanced high strength steels (AHSS) with higher strengths is increasing in the automotive industry. While there have been major improvements recently in the trade-off between ductility and strength, sheared-edge formability of AHSS remains a critical issue. AHSS sheets exhibit cracking during stamping and forming operations below the predictions of forming limits. It has become important to understand the correlation between microstructure and sheared edge formability. The present work investigates the effects of shearing conditions, microstructure, and tensile properties on sheared edge formability. Seven commercially produced steels with tensile strengths of 1000 +/- 100 MPa were evaluated: five dual-phase (DP) steels with different compositions and varying microstructural features, one trip aided bainitic ferrite (TBF) steel, and one press-hardened steel tempered to a tensile strength within the desired range. It was found that sheared edge formability is influenced by the martensite in DP steels. Quantitative stereology measurements provided results that showed martensite size and distribution affect hole expansion ratio (HER). The overall trend is that HER increases with more evenly dispersed martensite throughout the microstructure. This microstructure involves a combination of martensite size, contiguity, mean free distance, and number of colonies per unit area. Additionally, shear face characterization showed that the fracture and burr region affect HER. The HER decreases with increasing size of fracture and burr region. With a larger fracture and burr region more defects and/or micro-cracks will be present on the shear surface. This larger fracture region on the shear face facilitates cracking in sheared edge formability. Finally, the sheared edge formability is directly correlated to true fracture strain (TFS). The true fracture strain from tensile samples correlates to the HER values. HER increases with increasing true fracture strain.

Investigation of Thermal High Cycle and Low Cycle Fatigue Mechanisms of Thick Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Miller, Robert A.

1998-01-01

Thick thermal barrier coating systems in a diesel engine experience severe thermal low cycle fatigue (LCF) and high cycle fatigue (HCF) during engine operation. In this paper, the mechanisms of fatigue crack initiation and propagation in a ZrO2-8wt.% Y2O3 thermal barrier coating, under simulated engine thermal LCF and HCF conditions, are investigated using a high power CO2 laser. Experiments showed that the combined LCF/HCF tests induced more severe coating surface cracking, microspallation and accelerated crack growth, as compared to the pure LCF test. Lateral crack branching and the ceramic/bond coat interface delaminations were also facilitated by HCF thermal loads, even in the absence of severe interfacial oxidation. Fatigue damages at crack wake surfaces, due to such phenomena as asperity/debris contact induced cracking and splat pull-out bending during cycling, were observed especially for the combined LCF/HCF tests. It is found that the failure associated with LCF is closely related to coating sintering and creep at high temperatures, which induce tensile stresses in the coating after cooling. The failure associated with HCF process, however, is mainly associated with a surface wedging mechanism. The interaction between the LCF, HCF and ceramic coating creep, and the relative importance of LCF and HCF in crack propagation are also discussed based on the experimental evidence.

Assessment of Cracks in Stress Concentration Regions with Localized Plastic Zones

DOE Office of Scientific and Technical Information (OSTI.GOV)

Friedman, E.

1998-11-25

Marty brittle fracture evaluation procedures include plasticity corrections to elastically computed stress intensity factors. These corrections, which are based on the existence of a plastic zone in the vicinity of the crack tip, can overestimate the plasticity effect for a crack embedded in a stress concentration region in which the elastically computed stress exceeds the yield strength of the material in a localized zone. The interactions between the crack, which acts to relieve the high stresses driving the crack, plasticity effects in the stress concentration region, and the nature and source of the loading are examined by formulating explicit flawmore » finite element models for a crack emanating from the root of a notch located in a panel subject to an applied tensile stress. The results of these calculations provide conditions under which a crack-tip plasticity correction based on the Irwin plastic zone size overestimates the plasticity effect. A failure assessment diagram (FAD) curve is used to characterize the effect of plasticity on the crack driving force and to define a less restrictive plasticity correction for cracks at notch roots when load-controlled boundary conditions are imposed. The explicit flaw finite element results also demonstrate that stress intensity factors associated with load-controlled boundary conditions, such as those inherent in the ASME Boiler and Pressure Vessel Code as well as in most handbooks of stress intensity factors, can be much higher than those associated with displacement-controlled conditions, such as those that produce residual or thermal stresses. Under certain conditions, the inclusion of plasticity effects for cracks loaded by displacement-controlled boundary conditions reduces the crack driving force thus justifying the elimination of a plasticity correction for such loadings. The results of this study form the basis for removing unnecessary conservatism from flaw evaluation procedures that utilize plasticity corrections.« less

Learning, Interactional, and Motivational Outcomes in One-to-One Synchronous Computer-Mediated versus Face-to-Face Tutoring

ERIC Educational Resources Information Center

Siler, Stephanie Ann; VanLehn, Kurt

2009-01-01

Face-to-face (FTF) human-human tutoring has ranked among the most effective forms of instruction. However, because computer-mediated (CM) tutoring is becoming increasingly common, it is instructive to evaluate its effectiveness relative to face-to-face tutoring. Does the lack of spoken, face-to-face interaction affect learning gains and…

Factors controlling the size of graphene oxide sheets produced via the graphite oxide route.

PubMed

Pan, Shuyang; Aksay, Ilhan A

2011-05-24

We have studied the effect of the oxidation path and the mechanical energy input on the size of graphene oxide sheets derived from graphite oxide. The cross-planar oxidation of graphite from the (0002) plane results in periodic cracking of the uppermost graphene oxide layer, limiting its lateral dimension to less than 30 μm. We use an energy balance between the elastic strain energy associated with the undulation of graphene oxide sheets at the hydroxyl and epoxy sites, the crack formation energy, and the interaction energy between graphene layers to determine the cell size of the cracks. As the effective crack propagation rate in the cross-planar direction is an order of magnitude smaller than the edge-to-center oxidation rate, graphene oxide single sheets larger than those defined by the periodic cracking cell size are produced depending on the aspect ratio of the graphite particles. We also demonstrate that external energy input from hydrodynamic drag created by fluid motion or sonication, further reduces the size of the graphene oxide sheets through tensile stress buildup in the sheets.

Data-Science Analysis of the Macro-scale Features Governing the Corrosion to Crack Transition in AA7050-T7451

NASA Astrophysics Data System (ADS)

Co, Noelle Easter C.; Brown, Donald E.; Burns, James T.

2018-05-01

This study applies data science approaches (random forest and logistic regression) to determine the extent to which macro-scale corrosion damage features govern the crack formation behavior in AA7050-T7451. Each corrosion morphology has a set of corresponding predictor variables (pit depth, volume, area, diameter, pit density, total fissure length, surface roughness metrics, etc.) describing the shape of the corrosion damage. The values of the predictor variables are obtained from white light interferometry, x-ray tomography, and scanning electron microscope imaging of the corrosion damage. A permutation test is employed to assess the significance of the logistic and random forest model predictions. Results indicate minimal relationship between the macro-scale corrosion feature predictor variables and fatigue crack initiation. These findings suggest that the macro-scale corrosion features and their interactions do not solely govern the crack formation behavior. While these results do not imply that the macro-features have no impact, they do suggest that additional parameters must be considered to rigorously inform the crack formation location.

Gum formation tendencies of olefinic structures in gasoline and synergistic effect of sulphur compounds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nagpal, J.M.; Joshi, G.C.; Aswal, D.S.

1995-04-01

The high octane gasoline pool contains varying amounts of cracked naphthas as an important ingredient in formulating high octane lead free gasoline. The cracked naphthas are largely from Fluidized Catalytic Cracking (FCC) units and to lesser extend from thermal cracking units. While the role of olefinic unsaturation in gum formation during storage of gasoline has been extensively studied, there is little published work on contribution of individual olefin types in storage stability and gum formation tendency of gasoline containing these compound types. In the present work we report our results on storage stability and gum formation tendency of different olefinmore » types present in cracked naphthas through model compound matrix. It is found that cyclic olefins and cyclic diolefins are the most prolific gum formers. We have also studied the role of sulfur compounds present in the gasolines on gum formation tendency of olefins. While thiols enhance gum formation from all olefinic types, sulfides and disulfides interact depending on the structure of olefins. These can have either an accelerating, or inhibiting effect on gum formation.« less

A flexural crack model for damage detection in reinforced concrete structures

NASA Astrophysics Data System (ADS)

Hamad, W. I.; Owen, J. S.; Hussein, M. F. M.

2011-07-01

The use of changes in vibration data for damage detection of reinforced concrete structures faces many challenges that obstruct its transition from a research topic to field applications. Among these is the lack of appropriate damage models that can be deployed in the damage detection methods. In this paper, a model of a simply supported reinforced concrete beam with multiple cracks is developed to examine its use for damage detection and structural health monitoring. The cracks are simulated by a model that accounts for crack formation, propagation and closure. The beam model is studied under different dynamic excitations, including sine sweep and single excitation frequency, for various damage levels. The changes in resonant frequency with increasing loads are examined along with the nonlinear vibration characteristics. The model demonstrates that the resonant frequency reduces by about 10% at the application of 30% of the ultimate load and then drops gradually by about 25% at 70% of the ultimate load. The model also illustrates some nonlinearity in the dynamic response of damaged beams. The appearance of super-harmonics shows that the nonlinearity is higher when the damage level is about 35% and then decreases with increasing damage. The restoring force-displacement relationship predicted the reduction in the overall stiffness of the damaged beam. The model quantitatively predicts the experimental vibration behaviour of damaged RC beams and also shows the damage dependency of nonlinear vibration behaviour.

Self-healing atmospheric plasma sprayed Mn1.0Co1.9Fe0.1O4 protective interconnector coatings for solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Grünwald, Nikolas; Sebold, Doris; Sohn, Yoo Jung; Menzler, Norbert Heribert; Vaßen, Robert

2017-09-01

Dense coatings on metallic interconnectors are necessary to suppress chromium poisoning of SOFC cathodes. Atmospherically plasma sprayed (APS) Mn1.0Co1.9Fe0.1O4 (MCF) protective layers demonstrated reduced chromium related degradation in laboratory and stack tests. Previous analyses revealed strong microstructural changes comparing the coating's as-sprayed and operated condition. This work concentrates on the layer-densification and crack-healing observed by annealing APS-MCF in air, which simulates the cathode operation conditions. The effect is described by a volume expansion induced by a phase transformation. Reducing conditions during the spray process lead to a deposition of the MCF in a metastable rock salt configuration. Annealing in air activates diffusion processes for a phase transformation to the low temperature stable spinel phase (T < 1050 °C). This transformation is connected to an oxygen incorporation which occurs at regions facing high oxygen partial pressures, as there are the sample surface, cracks and pore surfaces. Calculations reveal a volume expansion induced by the oxygen uptake which seals the cracks and densifies the coating. The process decelerates when the cracks are closed, as the gas route is blocked and further oxidation continues over solid state diffusion. The self-healing abilities of metastable APS coatings could be interesting for other applications.

Probing the rhizosphere to define mineral organic relationships

NASA Astrophysics Data System (ADS)

Schulz, M. S.; Dohnalkova, A.; Stonestrom, D. A.

2016-12-01

Soil organic matter (SOM) accumulation and stabilization over time is an important process as soils are a large carbon reservoir in which feedbacks under changing climates are unclear. The association of SOM with poorly crystalline or short-range-ordered secondary minerals has been shown to be important for carbon stabilization. Commonly used soil extraction techniques display correlations of SOM with secondary phases but do not show causation. The fate of root exudates in soils and processes controlling exudate associations with mineral phases are as yet structurally undefined. Sub-micron exploration of in-situ relations provides valuable information on SOM-mineral interactions. Soils of the Santa Cruz (California) marine terrace chronosequence are used to illustrate changes in deep (> 1 m) rhizosphere through time. Cracks and soil ped faces are sites of high root density and organic matter (biofilm or mucilage) deposition. We employ a variety of scanning electron microscopy (SEM) and scanning transmission electron microscopy (STEM) techniques for high resolution imaging and elemental analyses of deep rhizosphere and associated carbon mineral interactions. In these coastal prairie soils microscopy reveals secondary clay minerals associated with and possibly forming from organic-rich mucilage that occurs along the aforementioned rooting networks on fracture surfaces. We hypothesize that the production of secondary clays in the rhizosphere is an important mode of C incorporation into secondary minerals.

Further Development of Crack Growth Detection Techniques for US Test and Research Reactors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kohse, Gordon; Carpenter, David M.; Ostrovsky, Yakov

One of the key issues facing Light Water Reactors (LWRs) in extending lifetimes beyond 60 years is characterizing the combined effect of irradiation and water chemistry on material degradation and failure. Irradiation Assisted Stress Corrosion Cracking (IASCC), in which a crack propagates in a susceptible material under stress in an aggressive environment, is a mechanism of particular concern. Full understanding of IASCC depends on real time crack growth data acquired under relevant irradiation conditions. Techniques to measure crack growth in actively loaded samples under irradiation have been developed outside the US - at the Halden Boiling Water Reactor, for example.more » Several types of IASCC tests have also been deployed at the MITR, including passively loaded crack growth measurements and actively loaded slow strain rate tests. However, there is not currently a facility available in the US to measure crack growth on actively loaded, pre-cracked specimens in LWR irradiation environments. A joint program between the Idaho National Laboratory (INL) and the Massachusetts Institute of Technology (MIT) Nuclear Reactor Laboratory (NRL) is currently underway to develop and demonstrate such a capability for US test and research reactors. Based on the Halden design, the samples will be loaded using miniature high pressure bellows and a compact loading mechanism, with crack length measured in real time using the switched Direct Current Potential Drop (DCPD) method. The basic design and initial mechanical testing of the load system and implementation of the DCPD method have been previously reported. This paper presents the results of initial autoclave testing at INL and the adaptation of the design for use in the high pressure, high temperature water loop at the MITR 6 MW research reactor, where an initial demonstration is planned in mid-2015. Materials considerations for the high pressure bellows are addressed. Design modifications to the loading mechanism required by the size constraints of the MITR water loop are described. The safety case for operation of the high pressure gas-driven bellows mechanism is also presented. Key issues are the design and response of systems to limit gas flow in the event of a high pressure gas leak in the in-core autoclave. Integrity of the autoclave must be maintained and reactivity effects due to voiding of the loop coolant must be shown to be within the reactor technical specifications. The technical development of the crack growth monitor for application in the INL Advanced Test Reactor or the MITR can act as a template for adaptation of this technology in other reactors. (authors)« less

Extending Face-to-Face Interactions: Understanding and Developing an Online Teacher and Family Community

ERIC Educational Resources Information Center

Zhang, Chun; Du, Jianxia; Sun, Li; Ding, Yi

2018-01-01

Technology has been quickly changing human interactions, traditional practices, and almost every aspect of our lives. It is important to maintain effective face-to-face communication and interactions between teachers and families. Nonetheless, technology and its tools can also extend and enhance family-teacher relationships and partnerships. This…

Damage Tolerance of Sandwich Plates With Debonded Face Sheets

NASA Technical Reports Server (NTRS)

Sankar, Bhavani V.

2001-01-01

A nonlinear finite element analysis was performed to simulate axial compression of sandwich beams with debonded face sheets. The load - end-shortening diagrams were generated for a variety of specimens used in a previous experimental study. The energy release rate at the crack tip was computed using the J-integral, and plotted as a function of the load. A detailed stress analysis was performed and the critical stresses in the face sheet and the core were computed. The core was also modeled as an isotropic elastic-perfectly plastic material and a nonlinear post buckling analysis was performed. A Graeco-Latin factorial plan was used to study the effects of debond length, face sheet and core thicknesses, and core density on the load carrying capacity of the sandwich composite. It has been found that a linear buckling analysis is inadequate in determining the maximum load a debonded sandwich beam can carry. A nonlinear post-buckling analysis combined with an elastoplastic model of the core is required to predict the compression behavior of debonded sandwich beams.

Crack cocaine inhalation induces schizophrenia-like symptoms and molecular alterations in mice prefrontal cortex.

PubMed

Areal, Lorena Bianchine; Herlinger, Alice Laschuk; Pelição, Fabrício Souza; Martins-Silva, Cristina; Pires, Rita Gomes Wanderley

2017-08-01

Crack cocaine (crack) addiction represents a major social and health burden, especially seeing as users are more prone to engage in criminal and violent acts. Crack users show a higher prevalence of psychiatric comorbidities - particularly antisocial personality disorders - when compared to powder cocaine users. They also develop cognitive deficits related mainly to executive functions, including working memory. It is noteworthy that stimulant drugs can induce psychotic states, which appear to mimic some symptoms of schizophrenia among users. Social withdraw and executive function deficits are, respectively, negative and cognitive symptoms of schizophrenia mediated by reduced dopamine (DA) tone in the prefrontal cortex (PFC) of patients. That could be explained by an increased expression of D2R short isoform (D2S) in the PFC of such patients and/or by hypofunctioning NMDA receptors in this region. Reduced DA tone has already been described in the PFC of mice exposed to crack smoke. Therefore, it is possible that behavioral alterations presented by crack users result from molecular and biochemical neuronal alterations akin to schizophrenia. Accordingly, we found that upon crack inhalation mice have shown decreased social interaction and working memory deficits analogous to schizophrenia's symptoms, along with increased D2S/D2L expression ratio and decreased expression of NR1, NR2A and NR2B NMDA receptor subunits in the PFC. Herein we propose two possible mechanisms to explain the reduced DA tone in the PFC elicited by crack consumption in mice, bringing also the first direct evidence that crack use may result in schizophrenia-like neurochemical, molecular and behavioral alterations. Copyright © 2017 Elsevier Ltd. All rights reserved.

The behaviour of fatigue-induced microdamage in compact bone samples from control and ovariectomised sheep.

PubMed

Kennedy, Oran D; Brennan, Orlaith; Mauer, Peter; O'Brien, Fergal J; Rackard, Susan M; Taylor, David; Lee, T Clive

2008-01-01

This study investigates the effect of microdamage on bone quality in osteoporosis using an ovariectomised (OVX) sheep model of osteoporosis. Thirty-four sheep were divided into an OVX group (n=16) and a control group (n=18). Fluorochromes were administered intravenously at 3 monthly intervals after surgery to label bone turnover. After sacrifice, beams were removed from the metatarsal and tested in three-point bending. Following failure, microcracks were identified and quantified in terms of region, location and interaction with osteons. Number of cycles to failure (Nf) was lower in the OVX group relative to controls by approximately 7%. Crack density (CrDn) was higher in the OVX group compared to controls. CrDn was 2.5 and 3.5 times greater in the compressive region compared to tensile in control and OVX bone respectively. Combined results from both groups showed that 91% of cracks remained in interstitial bone, approximately 8% of cracks penetrated unlabelled osteons and less than 1% penetrated into labelled osteons. All cases of labelled osteon penetration occurred in controls. Crack surface density (CrSDn), was 25% higher in the control group compared to OVX. It is known that crack behaviour on meeting microstructural features such as osteons will depend on crack length. We have shown that osteon age also affects crack propagation. Long cracks penetrated unlabelled osteons but not labelled ones. Some cracks in the control group did penetrate labelled osteons. This may be due the fact that control bone is more highly mineralized. CrSDn was increased by 25% in the control group compared to OVX. Further study of these fracture mechanisms will help determine the effect of microdamage on bone quality and how this contributes to bone fragility.

Informal Face-to-Face Interaction Improves Mood State Reflected in Prefrontal Cortex Activity

PubMed Central

Watanabe, Jun-ichiro; Atsumori, Hirokazu; Kiguchi, Masashi

2016-01-01

Recent progress with wearable sensors has enabled researchers to capture face-to-face interactions quantitatively and given great insight into human dynamics. One attractive field for applying such sensors is the workplace, where the relationship between the face-to-face behaviors of employees and the productivity of the organization has been investigated. One interesting result of previous studies showed that informal face-to-face interaction among employees, captured by wearable sensors that the employees wore, significantly affects their performance. However, the mechanism behind this relationship has not yet been adequately explained, though experiences at the job scene might qualitatively support the finding. We hypothesized that informal face-to-face interaction improves mood state, which in turn affects the task performance. To test this hypothesis, we evaluated the change of mood state before and after break time for two groups of participants, one that spent their breaks alone and one that spent them with other participants, by administering questionnaires and taking brain activity measurements. Recent neuroimaging studies have suggested a significant relationship between mood state and brain activity. Here, we show that face-to-face interaction during breaks significantly improved mood state, which was measured by Profiles of Mood States (POMS). We also observed that the verbal working memory (WM) task performance of participants who did not have face-to-face interaction during breaks decreased significantly. In this paper, we discuss how the change of mood state was evidenced in the prefrontal cortex (PFC) activity accompanied by WM tasks measured by near-infrared spectroscopy (NIRS). PMID:27199715

Crack Growth Behavior in the Threshold Region for High Cycle Fatigue Loading

NASA Technical Reports Server (NTRS)

Forman, Royce G.; Figert, J.; Beek, J.; Ventura, J.; Martinez, J.; Samonski, F.

2011-01-01

This presentation describes results obtained from a research project conducted at the NASA Johnson Space Center (JSC) that was jointly supported by the FAA Technical Center and JSC. The JSC effort was part of a multi-task FAA program involving several U.S. laboratories and initiated for the purpose of developing enhanced analysis tools to assess damage tolerance of rotorcraft and aircraft propeller systems. The research results to be covered in this presentation include a new understanding of the behavior of fatigue crack growth in the threshold region. This behavior is important for structural life analysis of aircraft propeller systems and certain rotorcraft structural components (e.g., the mast). These components are often designed to not allow fatigue crack propagation to exceed an experimentally determined fatigue crack growth threshold value. During the FAA review meetings for the program, disagreements occurred between the researchers regarding the observed fanning (spread between the da/dN curves of constant R) in the threshold region at low stress ratios, R. Some participants believed that the fanning was a result of the ASTM load shedding test method for threshold testing, and thus did not represent the true characteristics of the material. If the fanning portion of the threshold value is deleted or not included in a life analysis, a significant penalty in the calculated life and design of the component would occur. The crack growth threshold behavior was previously studied and reported by several research investigators in the time period: 1970-1980. Those investigators used electron microscopes to view the crack morphology of the fatigue fracture surfaces. Their results showed that just before reaching threshold, the crack morphology often changed from a striated to a faceted or cleavage-like morphology. This change was reported to have been caused by particular dislocation properties of the material. Based on the results of these early investigations, a program was initiated at JSC to repeat these examinations on a number of aircraft structural alloys that were currently being tested for obtaining fatigue crack growth properties. These new scanning electron microscope (SEM) examinations of the fatigue fracture faces confirmed the change in crack morphology in the threshold crack tip region. In addition, SEM examinations were further performed in the threshold crack-tip region before breaking the specimens open (not done in the earlier published studies). In these examinations, extensive crack forking and even 90-degree crack bifurcations were found to have occurred in the final threshold crack-tip region. The forking and bifurcations caused numerous closure points to occur that prevented full crack closure in the threshold region, and thus were the cause of the fanning at low-R values. Therefore, we have shown that the fanning behavior was caused by intrinsic dislocation properties of the different alloy materials and were not the result of a plastic wake that remains from the load-shedding test phase. Also, to accommodate the use of da/dN data which includes fanning at low R-values, an updated fanning factor term has been developed and will be implemented into the NASGRO fatigue crack growth software. The term can be set to zero if it is desired that the fanning behavior is not be modeled for particular cases, such as when fanning is not a result of the intrinsic properties of a material.

Exploring relationship between face-to-face interaction and team performance using wearable sensor badges.

PubMed

Watanabe, Jun-ichiro; Ishibashi, Nozomu; Yano, Kazuo

2014-01-01

Quantitative analyses of human-generated data collected in various fields have uncovered many patterns of complex human behaviors. However, thus far the quantitative evaluation of the relationship between the physical behaviors of employees and their performance has been inadequate. Here, we present findings demonstrating the significant relationship between the physical behaviors of employees and their performance via experiments we conducted in inbound call centers while the employees wore sensor badges. There were two main findings. First, we found that face-to-face interaction among telecommunicators and the frequency of their bodily movements caused by the face-to-face interaction had a significant correlation with the entire call center performance, which we measured as "Calls per Hour." Second, our trial to activate face-to-face interaction on the basis of data collected by the wearable sensor badges the employees wore significantly increased their performance. These results demonstrate quantitatively that human-human interaction in the physical world plays an important role in team performance.

Exploring Relationship between Face-to-Face Interaction and Team Performance Using Wearable Sensor Badges

PubMed Central

Watanabe, Jun-ichiro; Ishibashi, Nozomu; Yano, Kazuo

2014-01-01

Quantitative analyses of human-generated data collected in various fields have uncovered many patterns of complex human behaviors. However, thus far the quantitative evaluation of the relationship between the physical behaviors of employees and their performance has been inadequate. Here, we present findings demonstrating the significant relationship between the physical behaviors of employees and their performance via experiments we conducted in inbound call centers while the employees wore sensor badges. There were two main findings. First, we found that face-to-face interaction among telecommunicators and the frequency of their bodily movements caused by the face-to-face interaction had a significant correlation with the entire call center performance, which we measured as “Calls per Hour.” Second, our trial to activate face-to-face interaction on the basis of data collected by the wearable sensor badges the employees wore significantly increased their performance. These results demonstrate quantitatively that human-human interaction in the physical world plays an important role in team performance. PMID:25501748

Relation of cyclic loading pattern to microstructural fracture in creep fatigue

NASA Technical Reports Server (NTRS)

Manson, S. S.; Halford, G. R.; Oldrieve, R. E.

1983-01-01

Creep-fatigue-environment interaction is discussed using the 'strainrange partitioning' (SRP) framework as a basis. The four generic SRP strainrange types are studied with a view of revealing differences in micromechanisms of deformation and fatigue degradation. Each combines in a different manner the degradation associated with slip-plane sliding, grain-boundary sliding, migration, cavitation, void development and environmental interaction; hence the approch is useful in delineating the relative importance of these mechanisms in the different loadings. Micromechanistic results are shown for a number of materials, including 316 SS, wrought heat resistant alloys, several nickel-base superalloys, and a tantalum base alloy, T-111. Although there is a commonality of basic behavior, the differences are useful in delineation several important principles of interpretation. Some quantitative results are presented for 316 SS, involving crack initiation and early crack growth, as well as the interaction of low-cycle fatigue with high-cycle fatigue.

A comparison of single-cycle versus multiple-cycle proof testing strategies

NASA Technical Reports Server (NTRS)

Hudak, S. J., Jr.; Mcclung, R. C.; Bartlett, M. L.; Fitzgerald, J. H.; Russell, D. A.

1990-01-01

An evaluation of single-cycle and multiple-cycle proof testing (MCPT) strategies for SSME components is described. Data for initial sizes and shapes of actual SSME hardware defects are analyzed statistically. Closed-form estimates of the J-integral for surface flaws are derived with a modified reference stress method. The results of load- and displacement-controlled stable crack growth tests on thin IN-718 plates with deep surface flaws are summarized. A J-resistance curve for the surface-cracked configuration is developed and compared with data from thick compact tension specimens. The potential for further crack growth during large unload/reload cycles is discussed, highlighting conflicting data in the literature. A simple model for ductile crack growth during MCPT based on the J-resistance curve is used to study the potential effects of key variables. The projected changes in the crack size distribution during MCPT depend on the interactions between several key parameters, including the number of proof cycles, the nature of the resistance curve, the initial crack size distribution, the component boundary conditions (load vs. displacement control), and the magnitude of the applied load or displacement. The relative advantages of single-cycle and multiple-cycle proof testing appear to be specific, therefore, to individual component geometry, material, and loading.

Shell cracking strength in almond (Prunus dulcis [Mill.] D.A. Webb.) and its implication in uses as a value-added product.

PubMed

Ledbetter, C A

2008-09-01

Researchers are currently developing new value-added uses for almond shells, an abundant agricultural by-product. Almond varieties are distinguished by processors as being either hard or soft shelled, but these two broad classes of almond also exhibit varietal diversity in shell morphology and physical characters. By defining more precisely the physical and chemical characteristics of almond shells from different varieties, researchers will better understand which specific shell types are best suited for specific industrial processes. Eight diverse almond accessions were evaluated in two consecutive harvest seasons for nut and kernel weight, kernel percentage and shell cracking strength. Shell bulk density was evaluated in a separate year. Harvest year by almond accession interactions were highly significant (p0.01) for each of the analyzed variables. Significant (p0.01) correlations were noted for average nut weight with kernel weight, kernel percentage and shell cracking strength. A significant (p0.01) negative correlation for shell cracking strength with kernel percentage was noted. In some cases shell cracking strength was independent of the kernel percentage which suggests that either variety compositional differences or shell morphology affect the shell cracking strength. The varietal characterization of almond shell materials will assist in determining the best value-added uses for this abundant agricultural by-product.

Nonverbal behavior during face-to-face social interaction in schizophrenia: a review.

PubMed

Lavelle, Mary; Healey, Patrick G T; McCabe, Rosemarie

2014-01-01

Patients with a diagnosis of schizophrenia display social cognitive deficits. However, little is known about patients' nonverbal communication during their social encounters with others. This review identified 17 studies investigating nonverbal communication in patients' unscripted face-to-face interactions, addressing a) nonverbal differences between patients and others, b) nonverbal behavior of the patients' partners, c) the association between nonverbal behavior and symptoms, and d) the association between nonverbal behavior and social outcomes. Patients displayed fewer nonverbal behaviors inviting interaction, with negative symptoms exacerbating this pattern. Positive symptoms were associated with heightened nonverbal behavior. Patients' partners changed their own nonverbal behavior in response to the patient. Reduced prosocial behaviors, inviting interaction, were associated with poorer social outcomes. The evidence suggests that patients' nonverbal behavior, during face-to-face interaction, is influenced by patients symptoms and impacts the success of their social interactions.

Dislocation dynamics modelling of the ductile-brittle-transition

NASA Astrophysics Data System (ADS)

Hennecke, Thomas; Hähner, Peter

2009-07-01

Many materials like silicon, tungsten or ferritic steels show a transition between high temperature ductile fracture with stable crack grow and high deformation energy absorption and low temperature brittle fracture in an unstable and low deformation mode, the ductile-brittle-transition. Especially in steels, the temperature transition is accompanied by a strong increase of the measured fracture toughness over a certain temperature range and strong scatter in the toughness data in this transition regime. The change in fracture modes is affected by dynamic interactions between dislocations and the inhomogeneous stress fields of notches and small cracks. In the present work a dislocation dynamics model for the ductile-brittle-transition is proposed, which takes those interactions into account. The model can explain an increase with temperature of apparent toughness in the quasi-brittle regime and different levels of scatter in the different temperature regimes. Furthermore it can predict changing failure sites in materials with heterogeneous microstructure. Based on the model, the effects of crack tip blunting, stress state, external strain rate and irradiation-induced changes in the plastic flow properties can be discussed.

Stimulation by Hyphopichia burtonii and Bacillus amyloliquefaciens of aflatoxin production by Aspergillus flavus in irradiated maize and rice grains

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cuero, R.G.; Smith, J.E.; Lacey, J.

Aspergillus flavus was grown on maize and rice extract agars and on irradiated viable cracked maize and rice grains, either in pure culture or in dual culture with wild strains of either Hyphopichia burtonii or Bacillus amyloliquefaciens. Aflatoxin production by A. flavus and its growth and interactions with the other microorganisms were studied at three water activities (a/sub w/) (0.98, 0.95, and 0.90) and two temperatures (25 and 16/sup 0/C). Both H. burtonii and B. amyloliquefaciens markedly stimulated growth and aflotoxin production by A. flavus on cracked maize, especially at 25/sup 0/C and 0.95 and 0.98 a/sub w/. No aflatoxinmore » was detected in pure cultures of A. flavus on cracked rice after 12 days of incubation at 25/sup 0/C, but some was produced by mixed cultures at 16/sup 0/C and 0.98 a/sub w/. The morphological interactions among A. flavus, H. burtonii, and B. amyloliquefaciens were also examined on maize and rice extract agars under similar controlled conditions.« less

Simulation of Crack Propagation in Engine Rotating Components under Variable Amplitude Loading

NASA Technical Reports Server (NTRS)

Bonacuse, P. J.; Ghosn, L. J.; Telesman, J.; Calomino, A. M.; Kantzos, P.

1998-01-01

The crack propagation life of tested specimens has been repeatedly shown to strongly depend on the loading history. Overloads and extended stress holds at temperature can either retard or accelerate the crack growth rate. Therefore, to accurately predict the crack propagation life of an actual component, it is essential to approximate the true loading history. In military rotorcraft engine applications, the loading profile (stress amplitudes, temperature, and number of excursions) can vary significantly depending on the type of mission flown. To accurately assess the durability of a fleet of engines, the crack propagation life distribution of a specific component should account for the variability in the missions performed (proportion of missions flown and sequence). In this report, analytical and experimental studies are described that calibrate/validate the crack propagation prediction capability ]or a disk alloy under variable amplitude loading. A crack closure based model was adopted to analytically predict the load interaction effects. Furthermore, a methodology has been developed to realistically simulate the actual mission mix loading on a fleet of engines over their lifetime. A sequence of missions is randomly selected and the number of repeats of each mission in the sequence is determined assuming a Poisson distributed random variable with a given mean occurrence rate. Multiple realizations of random mission histories are generated in this manner and are used to produce stress, temperature, and time points for fracture mechanics calculations. The result is a cumulative distribution of crack propagation lives for a given, life limiting, component location. This information can be used to determine a safe retirement life or inspection interval for the given location.

Life and Damage Monitoring-Using NDI Data Interpretation for Corrosion Damage and Remaining Life Assessments

DTIC Science & Technology

2003-02-01

Holistic Life Prediction Methodology Engineering is a profession based in science, but in the face of limited data or resources, the application of...the process. (see Table 1). "* HLPM uses continuum mechanics but defines limits of applicability - is material and process specific. "* HLPM defines...LEFM - EPFM ?) Nucleated Structure dominated Data base** Tensile/compressive discontinuity (not crack growth buckling inherent) type, size, Appropriate

Simulating Fragmentation and Fluid-Induced Fracture in Disordered Media Using Random Finite-Element Meshes

DOE PAGES

Bishop, Joseph E.; Martinez, Mario J.; Newell, Pania

2016-11-08

Fracture and fragmentation are extremely nonlinear multiscale processes in which microscale damage mechanisms emerge at the macroscale as new fracture surfaces. Numerous numerical methods have been developed for simulating fracture initiation, propagation, and coalescence. In this paper, we present a computational approach for modeling pervasive fracture in quasi-brittle materials based on random close-packed Voronoi tessellations. Each Voronoi cell is formulated as a polyhedral finite element containing an arbitrary number of vertices and faces. Fracture surfaces are allowed to nucleate only at the intercell faces. Cohesive softening tractions are applied to new fracture surfaces in order to model the energy dissipatedmore » during fracture growth. The randomly seeded Voronoi cells provide a regularized discrete random network for representing fracture surfaces. The potential crack paths within the random network are viewed as instances of realizable crack paths within the continuum material. Mesh convergence of fracture simulations is viewed in a weak, or distributional, sense. The explicit facet representation of fractures within this approach is advantageous for modeling contact on new fracture surfaces and fluid flow within the evolving fracture network. Finally, applications of interest include fracture and fragmentation in quasi-brittle materials and geomechanical applications such as hydraulic fracturing, engineered geothermal systems, compressed-air energy storage, and carbon sequestration.« less

Simulating Fragmentation and Fluid-Induced Fracture in Disordered Media Using Random Finite-Element Meshes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bishop, Joseph E.; Martinez, Mario J.; Newell, Pania

Fracture and fragmentation are extremely nonlinear multiscale processes in which microscale damage mechanisms emerge at the macroscale as new fracture surfaces. Numerous numerical methods have been developed for simulating fracture initiation, propagation, and coalescence. In this paper, we present a computational approach for modeling pervasive fracture in quasi-brittle materials based on random close-packed Voronoi tessellations. Each Voronoi cell is formulated as a polyhedral finite element containing an arbitrary number of vertices and faces. Fracture surfaces are allowed to nucleate only at the intercell faces. Cohesive softening tractions are applied to new fracture surfaces in order to model the energy dissipatedmore » during fracture growth. The randomly seeded Voronoi cells provide a regularized discrete random network for representing fracture surfaces. The potential crack paths within the random network are viewed as instances of realizable crack paths within the continuum material. Mesh convergence of fracture simulations is viewed in a weak, or distributional, sense. The explicit facet representation of fractures within this approach is advantageous for modeling contact on new fracture surfaces and fluid flow within the evolving fracture network. Finally, applications of interest include fracture and fragmentation in quasi-brittle materials and geomechanical applications such as hydraulic fracturing, engineered geothermal systems, compressed-air energy storage, and carbon sequestration.« less

Indentation damage and mechanical properties of human enamel and dentin.

PubMed

Xu, H H; Smith, D T; Jahanmir, S; Romberg, E; Kelly, J R; Thompson, V P; Rekow, E D

1998-03-01

Understanding the mechanical properties of human teeth is important to clinical tooth preparation and to the development of "tooth-like" restorative materials. Previous studies have focused on the macroscopic fracture behavior of enamel and dentin. In the present study, we performed indentation studies to understand the microfracture and deformation and the microcrack-microstructure interactions of teeth. It was hypothesized that crack propagation would be influenced by enamel rods and the dentino-enamel junction (DEJ), and the mechanical properties would be influenced by enamel rod orientation and tooth-to-tooth variation. Twenty-eight human third molars were used for the measurement of hardness, fracture toughness, elastic modulus, and energy absorbed during indentation. We examined the effect of enamel rod orientation by propagating cracks in the occlusal surface, and in the axial section in directions parallel and perpendicular to the occlusal surface. The results showed that the cracks in the enamel axial section were significantly longer in the direction perpendicular to the occlusal surface than parallel. The cracks propagating toward the DEJ were always arrested and unable to penetrate dentin. The fracture toughness of enamel was not single-valued but varied by a factor of three as a function of enamel rod orientation. The elastic modulus of enamel showed a significant difference between the occlusal surface and the axial section. It is concluded that the cracks strongly interact with the DEJ and the enamel rods, and that the mechanical properties of teeth are functions of microstructural orientations; hence, single values of properties (e.g., a single toughness value or a single modulus value) should not be used without information on microstructural orientation.

Diffraction of Harmonic Flexural Waves in a Cracked Elastic Plate Carrying Electrical Current

NASA Technical Reports Server (NTRS)

Ambur, Damodar R.; Hasanyan, Davresh; Librescu, iviu; Qin, Zhanming

2005-01-01

The scattering effect of harmonic flexural waves at a through crack in an elastic plate carrying electrical current is investigated. In this context, the Kirchhoffean bending plate theory is extended as to include magnetoelastic interactions. An incident wave giving rise to bending moments symmetric about the longitudinal z-axis of the crack is applied. Fourier transform technique reduces the problem to dual integral equations, which are then cast to a system of two singular integral equations. Efficient numerical computation is implemented to get the bending moment intensity factor for arbitrary frequency of the incident wave and of arbitrary electrical current intensity. The asymptotic behaviour of the bending moment intensity factor is analysed and parametric studies are conducted.

Self-Replicating Cracks: A Collaborative Fracture Mode in Thin Films

NASA Astrophysics Data System (ADS)

Marthelot, Joël; Roman, Benoît; Bico, José; Teisseire, Jérémie; Dalmas, Davy; Melo, Francisco

2014-08-01

Straight cracks are observed in thin coatings under residual tensile stress, resulting into the classical network pattern observed in china crockery, old paintings, or dry mud. Here, we present a novel fracture mechanism where delamination and propagation occur simultaneously, leading to the spontaneous self-replication of an initial template. Surprisingly, this mechanism is active below the standard critical tensile load for channel cracks and selects a robust interaction length scale on the order of 30 times the film thickness. Depending on triggering mechanisms, crescent alleys, spirals, or long bands are generated over a wide range of experimental parameters. We describe with a simple physical model, the selection of the fracture path and provide a configuration diagram displaying the different failure modes.

Penetration of carbon-fabric-reinforced composites by edge cracks during thermal aging

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.; Kamvouris, John E.

1994-01-01

Thermo-oxidative stability (TOS) test results are significantly influenced by the formation and growth or presence of interlaminar and interlaminar cracks in the cut edges of all carbon-fiber-crosslinked high-temperature polymer matrix composites(exp 1-5) (i.e., unidirectional, crossplied, angle-plied, and fabric composites). The thermo-oxidative degradation of these composites is heavily dependent on the surface area that is exposed to the harmful environment and on the surface-to-volume ratio of the structure under study. Since the growth of cracks and voids on the composite surfaces significantly increases the exposed surface areas, it is imperative that the interaction between the aging process and the formation of new surface area as the aging time progresses be understood.

Multimillion to billion atom simulations of nanosystems under extreme conditions

NASA Astrophysics Data System (ADS)

Vashishta, P.

2008-12-01

Advanced materials and devices with nanometer grain/feature sizes are being developed to achieve higher strength and toughness in ceramic materials and greater speeds in electronic devices. Below 100 nm, however, continuum description of materials and devices must be supplemented by atomistic descriptions. Current state of the art atomistic simulations involve 10 million - 1 billion atoms. We investigate initiation, growth and healing of wing cracks in confined silica glass by multimillion atom molecular dynamics (MD) simulations. Under dynamic compression, frictional sliding of pre-crack surfaces nucleates nanovoids, which evolve into nanocrack columns at the pre-crack tip. Nanocrack columns merge to form a wing crack, which grows via coalescence with nanovoids in the direction of maximum compression. Lateral confinement arrests the growth and partially heals the wing crack. Growth and arrest of the wing crack occur repeatedly, as observed in dynamic compression experiments on brittle solids under lateral confinement. MD simulation of hypervelocity projectile impact in aluminum nitride and alumina has also been studied. The simulations reveal strong interplay between shock- induced structural phase transformation, plastic deformation and brittle cracks. The shock wave splits into an elastic precursor and a wurtzite-to-rocksalt structural transformation wave. When the elastic wave reflected from the boundary of the sample interacts with the transformation wave front, nanocavities are generated along the penetration path of the projectile and dislocations in adjacent regions. The nanocavities coalesce to form mode I brittle cracks while dislocations generate kink bands that give rise to mode II cracks. These simulations provide a microscopic view of defects associated with simultaneous tensile and shear cracking at the structural phase transformation boundary due to shock impact in high-strength ceramics. Initiation of chemical reactions at shock fronts prior to detonation and dynamic transition in the shock structure of an energetic material (RDX) and reaction of aluminium nanoparticles in oxygen atmosphere followed by explosive burning is also discussed.

Experimental and Computational Studies on the Scattering of an Edge-Guided Wave by a Hidden Crack on a Racecourse Shaped Hole.

PubMed

Vien, Benjamin Steven; Rose, Louis Raymond Francis; Chiu, Wing Kong

2017-07-01

Reliable and quantitative non-destructive evaluation for small fatigue cracks, in particular those in hard-to-inspect locations, is a challenging problem. Guided waves are advantageous for structural health monitoring due to their slow geometrical decay of amplitude with propagating distance, which is ideal for rapid wide-area inspection. This paper presents a 3D laser vibrometry experimental and finite element analysis of the interaction between an edge-guided wave and a small through-thickness hidden edge crack on a racecourse shaped hole that occurs, in practice, as a fuel vent hole. A piezoelectric transducer is bonded on the straight edge of the hole to generate the incident wave. The excitation signal consists of a 5.5 cycle Hann-windowed tone burst of centre frequency 220 kHz, which is below the cut-off frequency for the first order Lamb wave modes (SH1). Two-dimensional fast Fourier transformation (2D FFT) is applied to the incident and scattered wave field along radial lines emanating from the crack mouth, so as to identify the wave modes and determine their angular variation and amplitude. It is shown experimentally and computationally that mid-plane symmetric edge waves can travel around the hole's edge to detect a hidden crack. Furthermore, the scattered wave field due to a small crack length, a , (compared to the wavelength λ of the incident wave) is shown to be equivalent to a point source consisting of a particular combination of body-force doublets. It is found that the amplitude of the scattered field increases quadratically as a function of a/λ , whereas the scattered wave pattern is independent of crack length for small cracks a < λ . This study of the forward scattering problem from a known crack size provides a useful guide for the inverse problem of hidden crack detection and sizing.

Ductile-Phase-Toughened Tungsten for Plasma-Facing Materials

NASA Astrophysics Data System (ADS)

Cunningham, Kevin Hawkins

A variety of processing approaches were employed to fabricate ductile-phase-toughened (DPT) tungsten (W) composites. Mechanical testing and analytical modeling were used to guide composite development. This work provides a basis for further development of W composites to be used in structural divertor components of future fusion reactors. W wire was tested in tension, showing significant ductility and strength. Coatings of copper (Cu) or tungsten carbide (WC) were applied to the W wire via electrodeposition and carburization, respectively. Composites were fabricated using spark plasma sintering (SPS) to consolidate W powders together with each type of coated W wire. DPT behavior, e.g. crack arrest and crack bridging, was not observed in three-point bend testing of the sintered composites. A laminate was fabricated by hot pressing W and Cu foils together with W wires, and subsequently tested in tension. This laminate was bonded via hot pressing to thick W plate as a reinforcing layer, and the composite was tested in three-point bending. Crack arrest was observed along with some fiber pullout, but significant transverse cracking in the W plate confounded further fracture toughness analysis. The fracture toughness of thin W plate was measured in three-point bending. W plates were brazed with Cu foils to form a laminate. Crack arrest and crack bridging were observed in three-point bend tests of the laminate, and fracture resistance curves were successfully calculated for this DPT composite. An analytical model of crack bridging was developed using the basis described by Chao in previous work by the group. The model uses the specimen geometry, matrix properties, and the stress-displacement function of a ductile reinforcement ("bridging law") to calculate the fracture resistance curve (R-curve) and load-displacement curve (P-D curve) for any test specimen geometry. The code was also implemented to estimate the bridging law of an arbitrary composite using R-curve data. Finally, a parametric study was performed to quantitatively determine the necessary mechanical properties of useful toughening reinforcements for a DPT W composite. The analytical model has a broad applicability for any DPT material.

An examination of impact damage in glass-phenolic and aluminum honeycomb core composite panels

NASA Technical Reports Server (NTRS)

Nettles, A. T.; Lance, D. G.; Hodge, A. J.

1990-01-01

An examination of low velocity impact damage to glass-phenolic and aluminum core honeycomb sandwich panels with carbon-epoxy facesheets is presented. An instrumented drop weight impact test apparatus was utilized to inflict damage at energy ranges between 0.7 and 4.2 joules. Specimens were checked for extent of damage by cross sectional examination. The effect of core damage was assessed by subjecting impact-damaged beams to four-point bend tests. Skin-only specimens (facings not bonded to honeycomb) were also tested for comparison purposes. Results show that core buckling is the first damage mode, followed by delaminations in the facings, matrix cracking, and finally fiber breakage. The aluminum honeycomb panels exhibited a larger core damage zone and more facing delaminations than the glass-phenolic core, but could withstand more shear stress when damaged than the glass-phenolic core specimens.

Preliminary investigation and application of alternate dry gas seal face materials{copyright}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Evenson, R.; Peterson, R.; Hanson, R.

1994-01-01

Traditional seal mating ring materials such as tungsten carbide (WC) are commonly used in high pressure centrifugal gas compressor dry gas (gas lubricating film) seal applications. Although these materials possess desirable properties for minimizing thermal distortion and deformation when subjected to pressure and centrifugal force, they have low toughness, i.e., they are brittle and have poor resistance to thermal shock. It has been found that these materials are easily heat checked during seal face touchdown. Heat checking as well as other crack indications inherent in these materials can quickly propagate, resulting in a catastrophic seal ring failure. In this paper,more » an investigation of alternate seal face materials is described. Two ductile, nitrided, low ferrous materials proved to be readily manufacturable into dry gas seal rings and performed comparably to tungsten carbide in natural gas service. 10 refs., 13 figs., 5 tabs.« less

Analysis of an Aircraft Honeycomb Sandwich Panel with Circular Face Sheet/Core Disbond Subjected to Ground-Air Pressurization

NASA Technical Reports Server (NTRS)

Rinker, Martin; Krueger, Ronald; Ratcliffe, James

2013-01-01

The ground-air pressurization of lightweight honeycomb sandwich structures caused by alternating pressure differences between the enclosed air within the honeycomb core and the ambient environment is a well-known and controllable loading condition of aerospace structures. However, initial face sheet/core disbonds intensify the face sheet peeling effect of the internal pressure load significantly and can decrease the reliability of the sandwich structure drastically. Within this paper, a numerical parameter study was carried out to investigate the criticality of initial disbonds in honeycomb sandwich structures under ground-air pressurization. A fracture mechanics approach was used to evaluate the loading at the disbond front. In this case, the strain energy release rate was computed via the Virtual Crack Closure Technique. Special attention was paid to the pressure-deformation coupling which can decrease the pressure load within the disbonded sandwich section significantly when the structure is highly deformed.

The effect of postnatal depression on mother-infant interaction, infant response to the Still-face perturbation, and performance on an Instrumental Learning task.

PubMed

Stanley, Charles; Murray, Lynne; Stein, Alan

2004-01-01

A representative community sample of primiparous depressed women and a nondepressed control group were assessed while in interaction with their infants at 2 months postpartum. At 3 months, infants were assessed on the Still-face perturbation of face to face interaction, and a subsample completed an Instrumental Learning paradigm. Compared to nondepressed women, depressed mothers' interactions were both less contingent and less affectively attuned to infant behavior. Postnatal depression did not adversely affect the infant's performance in either the Still-face perturbation or the Instrumental Learning assessment. Maternal responsiveness in interactions at 2 months predicted the infant's performance in the Instrumental Learning assessment but not in the Still-face perturbation. The implications of these findings for theories of infant cognitive and emotional development are discussed.

Synchronized practice helps bearded capuchin monkeys learn to extend attention while learning a tradition

PubMed Central

Eshchar, Yonat; Visalberghi, Elisabetta; Resende, Briseida; Laity, Kellie; Izar, Patrícia

2017-01-01

Culture extends biology in that the setting of development shapes the traditions that individuals learn, and over time, traditions evolve as occasional variations are learned by others. In humans, interactions with others impact the development of cognitive processes, such as sustained attention, that shape how individuals learn as well as what they learn. Thus, learning itself is impacted by culture. Here, we explore how social partners might shape the development of psychological processes impacting learning a tradition. We studied bearded capuchin monkeys learning a traditional tool-using skill, cracking nuts using stone hammers. Young monkeys practice components of cracking nuts with stones for years before achieving proficiency. We examined the time course of young monkeys’ activity with nuts before, during, and following others’ cracking nuts. Results demonstrate that the onset of others’ cracking nuts immediately prompts young monkeys to start handling and percussing nuts, and they continue these activities while others are cracking. When others stop cracking nuts, young monkeys sustain the uncommon actions of percussing and striking nuts for shorter periods than the more common actions of handling nuts. We conclude that nut-cracking by adults can promote the development of sustained attention for the critical but less common actions that young monkeys must practice to learn this traditional skill. This work suggests that in nonhuman species, as in humans, socially specified settings of development impact learning processes as well as learning outcomes. Nonhumans, like humans, may be culturally variable learners. PMID:28739944

[The cause of polyurethane catheter cracking during constant infusion of etoposide (VP-16) injection].

PubMed

Yokoyama, H; Aoyama, T; Matsuyama, T; Yamamura, Y; Nakajima, K; Nakamura, K; Sato, H; Kotaki, H; Chiba, S; Hirai, H; Yazaki, Y; Iga, T

1998-12-01

We studied the cause of cracking of a clinically used polyurethane (PU) catheter during the constant infusion of etoposide (VP-16) injection (Lastet), administered without dilution to patients as a part of combination high-dose chemotherapy. After VP-16 injection was infused into the PU catheter at a constant infusion rate (30 ml/h) for 24 h, a decrease in the elasticity (36% of untreated) and on increase in the length of the catheter (3.7%) were observed. These changes were significantly higher than those treated with the control saline. The similar changes of the PU catheter were observed after treatment with a basal solution containing polyethylene glycol 400 (PEG 400), polysorbate 80 and ethanol, which is the vehicle of the VP-16 injection, and with ethanol alone. Moreover, obvious degeneration of the internal wall (occurrence of spots like melting) and cutting face (micro-cracking) of the catheter was observed with an electron microscope after treatment with the vehicle. On the other hand, the elasticity or extension of the PU catheter were not changed after treatment with saline or PEG 400. From these findings, it was suggested that the degeneration and subsequent cracking of the PU catheter during the infusion of VP-16 injection was caused by ethanol contained in its injection solution. No cracking or morphological changes of polyvinyl chloride (PVC) and silicone catheters were found after treatment with the vehicle solution. However, since it has been reported in previous reports that di(2-ethylhexyl)phthalate was leached from PVC bags, the high dose chemotherapy with the dilution-free VP-16 injection should be achieved safely and effectively using a silicon catheter, rather than the PU catheter.

The Microstructural Evolution of Fatigue Cracks in FCC Metals

NASA Astrophysics Data System (ADS)

Gross, David William

The microstructural evolution during fatigue crack propagation was investigated in a variety of planar and wavy slip FCC metals. The planar materials included Haynes 230, Nitronic 40, and 316 stainless steel, and the wavy materials included pure nickel and pure copper. Three different sets of experiments were performed to fully characterize the microstructural evolution. The first, performed on Haynes 230, mapped the strain field ahead a crack tip using digital image correlation and electron backscatter diffraction techniques. Focused ion beam (FIB) lift-out techniques were then utilized to extract transmission electron microscopy (TEM) samples at specific distances from the crack tip. TEM investigations compared the measured strain to the microstructure. Overall, the strain measured via DIC and EBSD was only weakly correlated to the density of planar slip bands in the microstructure. The second set of experiments concerned the dislocation structure around crack tips. This set of experiments was performed on all the materials. The microstructure at arrested fatigue cracks on the free surface was compared to the microstructure found beneath striations on the fracture surfaces by utilizing FIB micromachining to create site-specific TEM samples. The evolved microstructure depended on the slip type. Strong agreement was found between the crack tip microstructure at the free surface and the fracture surface. In the planar materials, the microstructure in the plastic zone consisted of bands of dislocations or deformation twins, before transitioning to a refined sub-grain microstructure near the crack flank. The sub-grain structure extended 300-500 nm away from the crack flank in all the planar slip materials studied. In contrast, the bulk structure in the wavy slip material consisted of dislocation cells and did not transition to a different microstructure as the crack tip was approached. The strain in wavy slip was highest near the crack tip, as the misorientations between the dislocation cells increased and the cell size decreased as the crack flank was approached. The final set of experiments involved reloading the arrested crack tips in monotonic tension. This was performed on both the Haynes 230 and 316 stainless steel. This technique exposed the fracture surface and location of the arrested crack tip away from the free surface, allowing for a sample to be extracted via FIB micromachining and TEM evaluation of the microstructure. This permitted the crack tip microstructure to be investigated without exposing the microstructure to crack closure or free surface effects. These experiments confirmed what was inferred from the earlier experiments, namely that the banded structure was a product of the crack tip plastic zone and the refined structure was a product of the strain associated with crack advance. Overall the microstructural complexity presented in this work was much higher than would be predicted by current models of fatigue crack propagation. It is recommended that future models attempt to simulate interactions between the dislocations emitted during fatigue crack growth and the pre-existing microstructure to more accurately simulate the processes occurring at the crack tip during crack growth.

Rupture Dynamics along Thrust Dipping Fault: Inertia Effects due to Free Surface Wave Interactions

NASA Astrophysics Data System (ADS)

Vilotte, J. P.; Scala, A.; Festa, G.

2017-12-01

We numerically investigate the dynamic interaction between free surface and up-dip, in-plane rupture propagation along thrust faults, under linear slip-weakening friction. With reference to shallow along-dip rupture propagation during large subduction earthquakes, we consider here low dip-angle fault configurations with fixed strength excess and depth-increasing initial stress. In this configuration, the rupture undergoes a break of symmetry with slip-induced normal stress perturbations triggered by the interaction with reflected waves from the free surface. We found that both body-waves - behind the crack front - and surface waves - at the crack front - can trigger inertial effects. When waves interact with the rupture before this latter reaches its asymptotic speed, the rupture can accelerate toward the asymptotic speed faster than in the unbounded symmetric case, as a result of these inertial effects. Moreover, wave interaction at the crack front also affects the slip rate generating large ground motion on the hanging wall. Imposing the same initial normal stress, frictional strength and stress drop while varying the static friction coefficient we found that the break of symmetry makes the rupture dynamics dependent on the absolute value of friction. The higher the friction the stronger the inertial effect both in terms of rupture acceleration and slip amount. When the contact condition allows the fault interface to open close to the free surface, the length of the opening zone is shown to depend on the propagation length, the initial normal stress and the static friction coefficient. These new results are shown to agree with analytical results of rupture propagation in bounded media, and open new perspectives for understanding the shallow rupture of large subduction earthquakes and tsunami sources.

Comparative study for surface topography of bone drilling using conventional drilling and loose abrasive machining.

PubMed

Singh, Gurmeet; Jain, Vivek; Gupta, Dheeraj

2015-03-01

Drilling through the bone is a complicated process in orthopaedic surgery. It involves human as a part of the work so it needs better perfection and quality which leads to the sustainability. Different studies were carried out on this curious topic and some interesting results were obtained, which help the orthopaedic surgeon on the operation table. Major problems faced during bone drilling were crack initiation, thermal necrosis and burr formation. The surface topography of the bone is an indirect indication for the sustainability of bone joint. In this study, a comparison is made between conventional and a loose abrasive unconventional drilling technique for the surface characterization of the bone. The attempt has been made to show the feasibility of bone drilling with non-conventional technique and its aftereffect on the bone structure. The burr formation during conventional bone drilling was found to be more which leads to problems such as crack initiation and thermal necrosis. Scanning electrode microscope and surface roughness tester were used to characterize the surface of the fine drilled bone specimen and the results testified quite better surface finish and least crack formation while drilling with loose abrasive unconventional technique. © IMechE 2015.

Women recovering from social rejection: The effect of the person and the situation on a hormonal mechanism of affiliation.

PubMed

Duffy, Korrina A; Harris, Lasana T; Chartrand, Tanya L; Stanton, Steven J

2017-02-01

Rejection can motivate either affiliation or withdrawal. In order to study how personality and situational variables influence whether women will be motivated to affiliate versus withdraw, we manipulate social feedback (rejection vs. acceptance) and opportunity for face-to-face interaction (blocked vs. face-to-face) and measure the individual difference variables rejection sensitivity and social anxiety. We test how these variables affect endogenous progesterone and cortisol concentrations, which are presumed to signal motivational responses to rejection. We find that three-way interactions involving social feedback, opportunity for face-to-face interactions, and either social anxiety or rejection sensitivity significantly predict progesterone change, but not cortisol change. Both interactions are driven by sharp progesterone decreases for women high in social anxiety/rejection sensitivity who have been rejected and who have no opportunity to reaffiliate in a face-to-face interaction. This progesterone change may be a physiological marker of motivation for social avoidance following rejection for women who cannot reaffiliate and who are particularly socially anxious or sensitive to rejection. Published by Elsevier Ltd.

Structures associated with strike-slip faults that bound landslide elements

USGS Publications Warehouse

Fleming, R.W.; Johnson, A.M.

1989-01-01

Large landslides are bounded on their flanks and on elements within the landslides by structures analogous to strike-slip faults. We observed the formation of thwse strike-slip faults and associated structures at two large landslides in central Utah during 1983-1985. The strike-slip faults in landslides are nearly vertical but locally may dip a few degrees toward or away from the moving ground. Fault surfaces are slickensided, and striations are subparallel to the ground surface. Displacement along strike-slip faults commonly produces scarps; scarps occur where local relief of the failure surface or ground surface is displaced and becomes adjacent to higher or lower ground, or where the landslide is thickening or thinning as a result of internal deformation. Several types of structures are formed at the ground surface as a strike-slip fault, which is fully developed at some depth below the ground surface, propagates upward in response to displacement. The simplest structure is a tension crack oriented at 45?? clockwise or counterclockwise from the trend of an underlying right- or left-lateral strike-slip fault, respectively. The tension cracks are typically arranged en echelon with the row of cracks parallel to the trace of the underlying strike-slip fault. Another common structure that forms above a developing strike-slip fault is a fault segment. Fault segments are discontinuous strike-slip faults that contain the same sense of slip but are turned clockwise or counterclockwise from a few to perhaps 20?? from the underlying strike-slip fault. The fault segments are slickensided and striated a few centimeters below the ground surface; continued displacement of the landslide causes the fault segments to open and a short tension crack propagates out of one or both ends of the fault segments. These structures, open fault segments containing a short tension crack, are termed compound cracks; and the short tension crack that propagates from the tip of the fault segment is typically oriented 45?? to the trend of the underlying fault. Fault segments are also typically arranged en echelon above the upward-propagating strike-slip fault. Continued displacement of the landslide causes the ground to buckle between the tension crack portions of the compound cracks. Still more displacement produces a thrust fault on one or both limbs of the buckle fold. These compressional structures form at right angles to the short tension cracks at the tips of the fault segments. Thus, the compressional structures are bounded on their ends by one face of a tension crack and detached from underlying material by thrusting or buckling. The tension cracks, fault segments, compound cracks, folds, and thrusts are ephemeral; they are created and destroyed with continuing displacement of the landslide. Ultimately, the structures are replaced by a throughgoing strike-slip fault. At one landslide, we observed the creation and destruction of the ephemeral structures as the landslide enlarged. Displacement of a few centimeters to about a decimeter was sufficient to produce scattered tension cracks and fault segments. Sets of compound cracks with associated folds and thrusts were produced by displacements of up to 1 m, and 1 to 2 m of displacement was required to produce a throughgoing strike-slip fault. The type of first-formed structure above an upward-propagating strike-slip fault is apparently controlled by the rheology of the material. Brittle material such as dry topsoil or the compact surface of a gravel road produces echelon tension cracks and sets of tension cracks and compressional structures, wherein the cracks and compressional structures are normal to each other and 45?? to the strike-slip fault at depth. First-formed structures in more ductile material such as moist cohesive soil are fault segments. In very ductile material such as soft clay and very wet soil in swampy areas, the first-formed structure is a throughgoing strike-slip fault. There are othe

Fracture spacing in tensile brittle layers adhering to a rigid substrate

NASA Astrophysics Data System (ADS)

Lazarus, Véronique

2017-01-01

A natural question arising when observing crack networks in brittle layers such as, e.g., paints, muds, skins, pottery glazes, coatings, ceramics, is what determines the distance between cracks. This apparently simple question received a wealth of more or less complex and appropriate answers, but no consensus has emerged. Here, we show that the cracks interact mutually as soon as the spacing between them is smaller than ten times the thickness of the layer. Then, a simple Griffith-type balance between the elastic deformation energy and the fracture bulk and debonding costs captures a broad number of observations, going from the square-root or linear increase of the spacing with the thickness, to its decrease with loading until saturation. The adhesion strength is identified as playing a key role in these behaviour changes. As illustration, we show how the model can be applied to study the influence of the layer thickness on crack patterns. We believe that the versatility of the approach should permit wide applicability, from geosciences to engineering.

Fracture toughness and fracture behavior of CLAM steel in the temperature range of 450 °C-550 °C

NASA Astrophysics Data System (ADS)

Zhao, Yanyun; Liang, Mengtian; Zhang, Zhenyu; Jiang, Man; Liu, Shaojun

2018-04-01

In order to analyze the fracture toughness and fracture behavior (J-R curves) of China Low Activation Martensitic (CLAM) steel under the design service temperature of Test Blanket Module of the International Thermonuclear Experimental Reactor, the quasi-static fracture experiment of CLAM steel was carried out under the temperature range of 450 °C-550 °C. The results indicated that the fracture behavior of CLAM steel was greatly influenced by test temperature. The fracture toughness increased slightly as the temperature increased from 450 °C to 500 °C. In the meanwhile, the fracture toughness at 550 °C could not be obtained due to the plastic deformation near the crack tip zone. The microstructure analysis based on the fracture topography and the interaction between dislocations and lath boundaries showed two different sub-crack propagation modes: growth along 45° of the main crack direction at 450 °C and growth perpendicular to the main crack at 500 °C.

Literature survey on oxidations and fatigue lives at elevated temperatures

NASA Technical Reports Server (NTRS)

Liu, H. W.; Oshida, Y.

1984-01-01

Nickel-base superalloys are the most complex and the most widely used for high temperature applications such as aircraft engine components. The desirable properties of nickel-base superalloys at high temperatures are tensile strength, thermomechanical fatigue resistance, low thermal expansion, as well as oxidation resistance. At elevated temperature, fatigue cracks are often initiated by grain boundary oxidation, and fatigue cracks often propagate along grain boundaries, where the oxidation rate is higher. Oxidation takes place at the interface between metal and gas. Properties of the metal substrate, the gaseous environment, as well as the oxides formed all interact to make the oxidation behavior of nickel-base superalloys extremely complicated. The important topics include general oxidation, selective oxidation, internal oxidation, grain boundary oxidation, multilayer oxide structure, accelerated oxidation under stress, stress-generation during oxidation, composition and substrate microstructural changes due to prolonged oxidation, fatigue crack initiation at oxidized grain boundaries and the oxidation accelerated fatigue crack propagation along grain boundaries.

The Nature of Elementary Science Teachers' Experiences with Synchronous Online, Asynchronous Online and Face-to-Face Coaching

NASA Astrophysics Data System (ADS)

Gilbert, Amanda M.

This study investigated the nature of instructional coaching interactions in three formats: online synchronous, online asynchronous, and face-to-face. Knight's (2007) Seven Partnership Principles of Instructional Coaching were used as a framework to analyze and compare the coaching interactions between coach and teacher to determine whether online coaching may be a viable option to provide support for the teachers unprepared to teach the new science standards. Some previous research has suggested that online communication can result in deeper personal interactions (Walther, 1996), while other studies suggest that interactions are more natural and easier in formats that are more similar to face-to-face interactions (Kock, 2005). The findings of this study support the media naturalness theory (Kock, 2005) and suggest that collaboration may be especially difficult in asynchronous online communication. Although differences were noted in the actual interactions, teacher perception remained fairly consistently positive across the three formats. Research beyond this exploratory study is needed to make findings generalizable.

FASTRAN II - FATIGUE CRACK GROWTH STRUCTURAL ANALYSIS (UNIX VERSION)

NASA Technical Reports Server (NTRS)

Newman, J. C.

1994-01-01

Predictions of fatigue crack growth behavior can be made with the Fatigue Crack Growth Structural Analysis (FASTRAN II) computer program. As cyclic loads are applied to a selected crack configuration with an initial crack size, FASTRAN II predicts crack growth as a function of cyclic load history until either a desired crack size is reached or failure occurs. FASTRAN II is based on plasticity-induced crack-closure behavior of cracks in metallic materials and accounts for load-interaction effects, such as retardation and acceleration, under variable-amplitude loading. The closure model is based on the Dugdale model with modifications to allow plastically deformed material to be left along the crack surfaces as the crack grows. Plane stress and plane strain conditions, as well as conditions between these two, can be simulated in FASTRAN II by using a constraint factor on tensile yielding at the crack front to approximately account for three-dimensional stress states. FASTRAN II contains seventeen predefined crack configurations (standard laboratory fatigue crack growth rate specimens and many common crack configurations found in structures); and the user can define one additional crack configuration. The baseline crack growth rate properties (effective stress-intensity factor against crack growth rate) may be given in either equation or tabular form. For three-dimensional crack configurations, such as surface cracks or corner cracks at holes or notches, the fatigue crack growth rate properties may be different in the crack depth and crack length directions. Final failure of the cracked structure can be modelled with fracture toughness properties using either linear-elastic fracture mechanics (brittle materials), a two-parameter fracture criterion (brittle to ductile materials), or plastic collapse (extremely ductile materials). The crack configurations in FASTRAN II can be subjected to either constant-amplitude, variable-amplitude or spectrum loading. The applied loads may be either tensile or compressive. Several standardized aircraft flight-load histories, such as TWIST, Mini-TWIST, FALSTAFF, Inverted FALSTAFF, Felix and Gaussian, are included as options. FASTRAN II also includes two other methods that will help the user input spectrum load histories. The two methods are: (1) a list of stress points, and (2) a flight-by-flight history of stress points. Examples are provided in the user manual. Developed as a research program, FASTRAN II has successfully predicted crack growth in many metallic materials under various aircraft spectrum loading. A computer program DKEFF which is a part of the FASTRAN II package was also developed to analyze crack growth rate data from laboratory specimens to obtain the effective stress-intensity factor against crack growth rate relations used in FASTRAN II. FASTRAN II is written in standard FORTRAN 77. It has been successfully compiled and implemented on Sun4 series computers running SunOS and on IBM PC compatibles running MS-DOS using the Lahey F77L FORTRAN compiler. Sample input and output data are included with the FASTRAN II package. The UNIX version requires 660K of RAM for execution. The standard distribution medium for the UNIX version (LAR-14865) is a .25 inch streaming magnetic tape cartridge in UNIX tar format. It is also available on a 3.5 inch diskette in UNIX tar format. The standard distribution medium for the MS-DOS version (LAR-14944) is a 5.25 inch 360K MS-DOS format diskette. The contents of the diskette are compressed using the PKWARE archiving tools. The utility to unarchive the files, PKUNZIP.EXE, is included. The program was developed in 1984 and revised in 1992. Sun4 and SunOS are trademarks of Sun Microsystems, Inc. IBM PC is a trademark of International Business Machines Corp. MS-DOS is a trademark of Microsoft, Inc. F77L is a trademark of the Lahey Computer Systems, Inc. UNIX is a registered trademark of AT&T Bell Laboratories. PKWARE and PKUNZIP are trademarks of PKWare, Inc.

FASTRAN II - FATIGUE CRACK GROWTH STRUCTURAL ANALYSIS (IBM PC VERSION)

NASA Technical Reports Server (NTRS)

Newman, J. C.

1994-01-01

Predictions of fatigue crack growth behavior can be made with the Fatigue Crack Growth Structural Analysis (FASTRAN II) computer program. As cyclic loads are applied to a selected crack configuration with an initial crack size, FASTRAN II predicts crack growth as a function of cyclic load history until either a desired crack size is reached or failure occurs. FASTRAN II is based on plasticity-induced crack-closure behavior of cracks in metallic materials and accounts for load-interaction effects, such as retardation and acceleration, under variable-amplitude loading. The closure model is based on the Dugdale model with modifications to allow plastically deformed material to be left along the crack surfaces as the crack grows. Plane stress and plane strain conditions, as well as conditions between these two, can be simulated in FASTRAN II by using a constraint factor on tensile yielding at the crack front to approximately account for three-dimensional stress states. FASTRAN II contains seventeen predefined crack configurations (standard laboratory fatigue crack growth rate specimens and many common crack configurations found in structures); and the user can define one additional crack configuration. The baseline crack growth rate properties (effective stress-intensity factor against crack growth rate) may be given in either equation or tabular form. For three-dimensional crack configurations, such as surface cracks or corner cracks at holes or notches, the fatigue crack growth rate properties may be different in the crack depth and crack length directions. Final failure of the cracked structure can be modelled with fracture toughness properties using either linear-elastic fracture mechanics (brittle materials), a two-parameter fracture criterion (brittle to ductile materials), or plastic collapse (extremely ductile materials). The crack configurations in FASTRAN II can be subjected to either constant-amplitude, variable-amplitude or spectrum loading. The applied loads may be either tensile or compressive. Several standardized aircraft flight-load histories, such as TWIST, Mini-TWIST, FALSTAFF, Inverted FALSTAFF, Felix and Gaussian, are included as options. FASTRAN II also includes two other methods that will help the user input spectrum load histories. The two methods are: (1) a list of stress points, and (2) a flight-by-flight history of stress points. Examples are provided in the user manual. Developed as a research program, FASTRAN II has successfully predicted crack growth in many metallic materials under various aircraft spectrum loading. A computer program DKEFF which is a part of the FASTRAN II package was also developed to analyze crack growth rate data from laboratory specimens to obtain the effective stress-intensity factor against crack growth rate relations used in FASTRAN II. FASTRAN II is written in standard FORTRAN 77. It has been successfully compiled and implemented on Sun4 series computers running SunOS and on IBM PC compatibles running MS-DOS using the Lahey F77L FORTRAN compiler. Sample input and output data are included with the FASTRAN II package. The UNIX version requires 660K of RAM for execution. The standard distribution medium for the UNIX version (LAR-14865) is a .25 inch streaming magnetic tape cartridge in UNIX tar format. It is also available on a 3.5 inch diskette in UNIX tar format. The standard distribution medium for the MS-DOS version (LAR-14944) is a 5.25 inch 360K MS-DOS format diskette. The contents of the diskette are compressed using the PKWARE archiving tools. The utility to unarchive the files, PKUNZIP.EXE, is included. The program was developed in 1984 and revised in 1992. Sun4 and SunOS are trademarks of Sun Microsystems, Inc. IBM PC is a trademark of International Business Machines Corp. MS-DOS is a trademark of Microsoft, Inc. F77L is a trademark of the Lahey Computer Systems, Inc. UNIX is a registered trademark of AT&T Bell Laboratories. PKWARE and PKUNZIP are trademarks of PKWare, Inc.

In-person contact begets calling and texting: interpersonal motives for cell phone use, face-to-face interaction, and loneliness.

PubMed

Jin, Borae; Park, Namkee

2010-12-01

This study examined how cell-phone use is related to interpersonal motives for using cell phones, face-to-face communication, and loneliness. A survey of 232 college students who owned a cell phone revealed that affection and inclusion were relatively strong motivations for using voice calls and text messaging, and that interpersonal motives were positively related to the amount of cell-phone use, including calling and texting. The amount of face-to-face interaction was positively associated with the participants' cell-phone use and their interpersonal motives for using cell phones: the more the participants engaged in face-to-face interaction with other people, the higher their motives were and the more frequent cell-phone use was. Loneliness did not have a direct relation to cell-phone use. Instead, the participants with higher levels of loneliness were less likely to engage in face-to-face social interaction, which led them to use cell phones less and to be less motivated to use cell phones for interpersonal purposes.

Asynchronous cracking with dissimilar paths in multilayer graphene.

PubMed

Jang, Bongkyun; Kim, Byungwoon; Kim, Jae-Hyun; Lee, Hak-Joo; Sumigawa, Takashi; Kitamura, Takayuki

2017-11-16

Multilayer graphene consists of a stack of single-atomic-thick monolayer graphene sheets bound with π-π interactions and is a fascinating model material opening up a new field of fracture mechanics. In this study, fracture behavior of single-crystalline multilayer graphene was investigated using an in situ mode I fracture test under a scanning electron microscope, and abnormal crack propagation in multilayer graphene was identified for the first time. The fracture toughness of graphene was determined from the measured load-displacement curves and the realistic finite element modelling of specimen geometries. Nonlinear fracture behavior of the multilayer graphene is discussed based on nonlinear elastic fracture mechanics. In situ scanning electron microscope images obtained during the fracture test showed asynchronous crack propagation along independent paths, causing interlayer shear stress and slippages. We also found that energy dissipation by interlayer slippages between the graphene layers is the reason for the enhanced fracture toughness of multilayer graphene. The asynchronous cracking with independent paths is a unique cracking and toughening mechanism for single-crystalline multilayer graphene, which is not observed for the monolayer graphene. This could provide a useful insight for the design and development of graphene-based composite materials for structural applications.

Modeling Human Dynamics of Face-to-Face Interaction Networks

NASA Astrophysics Data System (ADS)

Starnini, Michele; Baronchelli, Andrea; Pastor-Satorras, Romualdo

2013-04-01

Face-to-face interaction networks describe social interactions in human gatherings, and are the substrate for processes such as epidemic spreading and gossip propagation. The bursty nature of human behavior characterizes many aspects of empirical data, such as the distribution of conversation lengths, of conversations per person, or of interconversation times. Despite several recent attempts, a general theoretical understanding of the global picture emerging from data is still lacking. Here we present a simple model that reproduces quantitatively most of the relevant features of empirical face-to-face interaction networks. The model describes agents that perform a random walk in a two-dimensional space and are characterized by an attractiveness whose effect is to slow down the motion of people around them. The proposed framework sheds light on the dynamics of human interactions and can improve the modeling of dynamical processes taking place on the ensuing dynamical social networks.

Determination of the Fracture Parameters in a Stiffened Composite Panel

NASA Technical Reports Server (NTRS)

Lin, Chung-Yi

2000-01-01

A modified J-integral, namely the equivalent domain integral, is derived for a three-dimensional anisotropic cracked solid to evaluate the stress intensity factor along the crack front using the finite element method. Based on the equivalent domain integral method with auxiliary fields, an interaction integral is also derived to extract the second fracture parameter, the T-stress, from the finite element results. The auxiliary fields are the two-dimensional plane strain solutions of monoclinic materials with the plane of symmetry at x(sub 3) = 0 under point loads applied at the crack tip. These solutions are expressed in a compact form based on the Stroh formalism. Both integrals can be implemented into a single numerical procedure to determine the distributions of stress intensity factor and T-stress components, T11, T13, and thus T33, along a three-dimensional crack front. The effects of plate thickness and crack length on the variation of the stress intensity factor and T-stresses through the thickness are investigated in detail for through-thickness center-cracked plates (isotropic and orthotropic) and orthotropic stiffened panels under pure mode-I loading conditions. For all the cases studied, T11 remains negative. For plates with the same dimensions, a larger size of crack yields larger magnitude of the normalized stress intensity factor and normalized T-stresses. The results in orthotropic stiffened panels exhibit an opposite trend in general. As expected, for the thicker panels, the fracture parameters evaluated through the thickness, except the region near the free surfaces, approach two-dimensional plane strain solutions. In summary, the numerical methods presented in this research demonstrate their high computational effectiveness and good numerical accuracy in extracting these fracture parameters from the finite element results in three-dimensional cracked solids.

31. VIEW OF DRILL HALL FROM NORTH END OF DRILL ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

31. VIEW OF DRILL HALL FROM NORTH END OF DRILL FLOOR FACING SOUTH. SHOWS EAST AND WEST BALCONIES, VEHICLE ENTRANCE AT THE SOUTHWEST CORNER OF THE DRILL FLOOR, THE CONCESSION STAND IN THE SOUTHEAST CORNER OF THE DRILL FLOOR AND THE FOUR WINDOWS IN THE SOUTH TRUSS SPACE. NOTE CRACKS IN THE UPPER RIGHT CORNER (WEST) OF THE SOUTH WALL. - Yakima National Guard Armory, 202 South Third Street, Yakima, Yakima County, WA

Yemen: Background and U.S. Relations

DTIC Science & Technology

2009-07-07

In a speech to the Atlantic Council of the United States, CIA Director Michael Hayden stated that “Yemen is another country of concern, a place where...Saleh has pledged to crack down on the southern separatist movement. In a pivotal speech in May 2009, Saleh remarked: “Now, the popular committees...will face the apostate elements. I call them apostate, vandalizing, and hireling elements. They are not new since they were products of the sedition

A study of the solvent effect on the morphology of RDX crystal by molecular modeling method.

PubMed

Chen, Gang; Xia, Mingzhu; Lei, Wu; Wang, Fengyun; Gong, Xuedong

2013-12-01

Molecular dynamics simulations have been performed to investigate the effect of acetone solvent on the crystal morphology of RDX. The results show that the growth morphology of RDX crystal in vacuum is dominated by the (111), (020), (200), (002), and (210) faces using the BFDH laws, and (111) face is morphologically the most important. The analysis of surface structures of RDX crystal indicates that (020) face is non-polar, while (210), (111), (002), and (200) faces are polar among which (210) face has the strongest polarity. The interaction between acetone solvent and each RDX crystal face is different, and the order of binding energy on these surfaces is (210) > (111) > (002) > (200) > (020). The analysis of interactions among RDX and acetone molecules reveal that the system nonbond interactions are primary strong van der Waals and electrostatic interactions containing π-hole interactions, the weak hydrogen bond interactions are also existent. The effect of acetone on the growth of RDX crystal can be evaluated by comparing the binding energies of RDX crystalline faces. It can be predicted that compared to that in vacuum, in the process of RDX crystallization from acetone, the morphological importance of (210) face is increased more and (111) face is not the most important among RDX polar surfaces, while the non-polar (020) face probably disappears. The experimentally obtained RDX morphology grown from acetone is in agreement with the theoretical prediction.

Elastic plastic fracture mechanics methodology for surface cracks

NASA Technical Reports Server (NTRS)

Ernst, Hugo A.; Lambert, D. M.

1994-01-01

The Elastic Plastic Fracture Mechanics Methodology has evolved significantly in the last several years. Nevertheless, some of these concepts need to be extended further before the whole methodology can be safely applied to structural parts. Specifically, there is a need to include the effect of constraint in the characterization of material resistance to crack growth and also to extend these methods to the case of 3D defects. As a consequence, this project was started as a 36 month research program with the general objective of developing an elastic plastic fracture mechanics methodology to assess the structural reliability of pressure vessels and other parts of interest to NASA which may contain flaws. The project is divided into three tasks that deal with (1) constraint and thickness effects, (2) three-dimensional cracks, and (3) the Leak-Before-Burst (LBB) criterion. This report period (March 1994 to August 1994) is a continuation of attempts to characterize three dimensional aspects of fracture present in 'two dimensional' or planar configuration specimens (Chapter Two), especially, the determination of, and use of, crack face separation data. Also, included, are a variety of fracture resistance testing results (J(m)R-curve format) and a discussion regarding two materials of NASA interest (6061-T651 Aluminum alloy and 1N718-STA1 nickel-base super alloy) involving a bases for like constraint in terms of ligament dimensions, and their comparison to the resulting J(m)R-curves (Chapter Two).

Crack Development in Cross-Ply Laminates Under Uniaxial Tension

NASA Technical Reports Server (NTRS)

Gyekenyesi, Andrew L.

1996-01-01

This study addresses matrix-dominated failures in carbon fiber/polymer matrix composite laminates in a cross-ply lay-up. The events of interest are interlaminar fracture in the form of transverse cracks in the 90' plies and longitudinal splitting in the 0 deg plies and interlaminar fracture in the form of 0/90 delamination. These events were observed using various nondestructive evaluation (NDE) techniques during static tensile tests. Acoustic emission (AE) x radiography, and edge view microscopy were the principal ones utilized in a real-time environment. A comparison of the NDE results with an analytical model based on the classical linear fracture mechanics concept of strain energy release rate as a criterion for crack growth was performed. The virtual crack closure theory was incorporated with a finite element model to generate strain energy release rate curves for the analytical case. Celion carbon fiber/polyimide matrix (G30-500/PMR-15) was the material tested with cross-ply lay-ups of (0(2)/90(6))s and (0(4)/90(4))s. The test specimens contained thermally induced cracks caused by the high-temperature processing. The analytical model was updated to compensate for the initial damage and to study further accumulation by taking into account the crack interactions. By correlating the experimental and analytical data, the critical energy release rates were found for the observable events of interest.

Laser cutting sandwich structure glass-silicon-glass wafer with laser induced thermal-crack propagation

NASA Astrophysics Data System (ADS)

Cai, Yecheng; Wang, Maolu; Zhang, Hongzhi; Yang, Lijun; Fu, Xihong; Wang, Yang

2017-08-01

Silicon-glass devices are widely used in IC industry, MEMS and solar energy system because of their reliability and simplicity of the manufacturing process. With the trend toward the wafer level chip scale package (WLCSP) technology, the suitable dicing method of silicon-glass bonded structure wafer has become necessary. In this paper, a combined experimental and computational approach is undertaken to investigate the feasibility of cutting the sandwich structure glass-silicon-glass (SGS) wafer with laser induced thermal-crack propagation (LITP) method. A 1064 nm semiconductor laser cutting system with double laser beams which could simultaneously irradiate on the top and bottom of the sandwich structure wafer has been designed. A mathematical model for describing the physical process of the interaction between laser and SGS wafer, which consists of two surface heating sources and two volumetric heating sources, has been established. The temperature stress distribution are simulated by using finite element method (FEM) analysis software ABAQUS. The crack propagation process is analyzed by using the J-integral method. In the FEM model, a stationary planar crack is embedded in the wafer and the J-integral values around the crack front edge are determined using the FEM. A verification experiment under typical parameters is conducted and the crack propagation profile on the fracture surface is examined by the optical microscope and explained from the stress distribution and J-integral value.

E-Mentoring the Online Doctoral Student from the Dissertation Prospectus through Dissertation Completion

ERIC Educational Resources Information Center

Black, Ronald

2017-01-01

Faculty who mentor online doctoral candidates face many of the same challenges and opportunities as those mentoring doctoral candidates in traditional, face-to-face modalities. The main difference is that E-Mentoring is based on interacting in the online space rather than interacting face-to-face, which may present challenges for both the…

Face-to-face: Perceived personal relevance amplifies face processing

PubMed Central

Pittig, Andre; Schupp, Harald T.; Alpers, Georg W.

2017-01-01

Abstract The human face conveys emotional and social information, but it is not well understood how these two aspects influence face perception. In order to model a group situation, two faces displaying happy, neutral or angry expressions were presented. Importantly, faces were either facing the observer, or they were presented in profile view directed towards, or looking away from each other. In Experiment 1 (n = 64), face pairs were rated regarding perceived relevance, wish-to-interact, and displayed interactivity, as well as valence and arousal. All variables revealed main effects of facial expression (emotional > neutral), face orientation (facing observer > towards > away) and interactions showed that evaluation of emotional faces strongly varies with their orientation. Experiment 2 (n = 33) examined the temporal dynamics of perceptual-attentional processing of these face constellations with event-related potentials. Processing of emotional and neutral faces differed significantly in N170 amplitudes, early posterior negativity (EPN), and sustained positive potentials. Importantly, selective emotional face processing varied as a function of face orientation, indicating early emotion-specific (N170, EPN) and late threat-specific effects (LPP, sustained positivity). Taken together, perceived personal relevance to the observer—conveyed by facial expression and face direction—amplifies emotional face processing within triadic group situations. PMID:28158672

Coupling fluid-structure interaction with phase-field fracture

NASA Astrophysics Data System (ADS)

Wick, Thomas

2016-12-01

In this work, a concept for coupling fluid-structure interaction with brittle fracture in elasticity is proposed. The fluid-structure interaction problem is modeled in terms of the arbitrary Lagrangian-Eulerian technique and couples the isothermal, incompressible Navier-Stokes equations with nonlinear elastodynamics using the Saint-Venant Kirchhoff solid model. The brittle fracture model is based on a phase-field approach for cracks in elasticity and pressurized elastic solids. In order to derive a common framework, the phase-field approach is re-formulated in Lagrangian coordinates to combine it with fluid-structure interaction. A crack irreversibility condition, that is mathematically characterized as an inequality constraint in time, is enforced with the help of an augmented Lagrangian iteration. The resulting problem is highly nonlinear and solved with a modified Newton method (e.g., error-oriented) that specifically allows for a temporary increase of the residuals. The proposed framework is substantiated with several numerical tests. In these examples, computational stability in space and time is shown for several goal functionals, which demonstrates reliability of numerical modeling and algorithmic techniques. But also current limitations such as the necessity of using solid damping are addressed.

Review of the damage mechanism in wind turbine gearbox bearings under rolling contact fatigue

NASA Astrophysics Data System (ADS)

Su, Yun-Shuai; Yu, Shu-Rong; Li, Shu-Xin; He, Yan-Ni

2017-12-01

Wind turbine gearbox bearings fail with the service life is much shorter than the designed life. Gearbox bearings are subjected to rolling contact fatigue (RCF) and they are observed to fail due to axial cracking, surface flaking, and the formation of white etching areas (WEAs). The current study reviewed these three typical failure modes. The underlying dominant mechanisms were discussed with emphasis on the formation mechanism of WEAs. Although numerous studies have been carried out, the formation of WEAs remains unclear. The prevailing mechanism of the rubbing of crack faces that generates WEAs was questioned by the authors. WEAs were compared with adiabatic shear bands (ASBs) generated in the high strain rate deformation in terms of microstructural compositions, grain refinement, and formation mechanism. Results indicate that a number of similarities exist between them. However, substantial evidence is required to verify whether or not WEAs and ASBs are the same matters.

Modeling Ductile-Phase Toughened Tungsten for Plasma-Facing Materials: Progress in Damage Finite Element Analysis of the Tungsten-Copper Bend Bar Tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nguyen, Ba Nghiep; Henager, Charles H.; Kurtz, Richard J.

The objective of this study is to investigate the deformation behavior of ductile phase toughened W-composites such as W-Cu and W-Ni-Fe by means of a multiscale finite element model that involves a microstructural dual-phase model where the constituent phases (i.e., W, Cu, Ni-Fe) are finely discretized and are described by a continuum damage model. Such a model is suitable for modeling deformation, cracking, and crack bridging for W-Cu, W-Ni-Fe, and other ductile phase toughened W-composites, or more generally, any multi-phase composite structure where two or more phases undergo cooperative deformation in a composite system. Our current work focuses on simulatingmore » the response and damage development of the W-Cu specimen subjected to three-point bending.« less

Application of nonlinear ultrasonics to inspection of stainless steel for dry storage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ulrich, Timothy James II; Anderson, Brain E.; Remillieux, Marcel C.

This report summarized technical work conducted by LANL staff an international collaborators in support of the UFD Storage Experimentation effort. The focus of the current technical work is on the detection and imaging of a failure mechanism known as stress corrosion cracking (SCC) in stainless steel using the nonlinear ultrasonic technique known as TREND. One of the difficulties faced in previous work is in finding samples that contain realistically sized SCC. This year such samples were obtained from EPRI. Reported here are measurements made on these samples. One of the key findings is the ability to detect subsurface changes tomore » the direction in which a crack is penetrating into the sample. This result follows from last year's report that demonstrated the ability of TREND techniques to image features below the sample surface. A new collaboration was established with AGH University of Science and Technology, Krakow, Poland.« less

Prosodic Modification and Vocal Adjustments in Mothers' Speech during Face-to-Face Interaction with Their Two- to Four-Month-Old Infants: A Double Video Study

ERIC Educational Resources Information Center

Braarud, Hanne Cecilie; Stormark, Kjell Morten

2008-01-01

The purpose of this study was to examine 32 mothers' sensitivity to social contingency during face-to-face interaction with their two- to four-month-old infants in a closed circuit TV set-up. Prosodic qualities and vocal sounds in mother's infant-directed (ID) speech during sequences of live interaction were compared to sequences where expressive…

When and where to practice: social influences on the development of nut-cracking in bearded capuchins (Sapajus libidinosus).

PubMed

Eshchar, Y; Izar, P; Visalberghi, E; Resende, B; Fragaszy, D

2016-05-01

The habitual use of tools by wild capuchin monkeys presents a unique opportunity to study the maintenance and transmission of traditions. Young capuchins spend several years interacting with nuts before cracking them efficiently with stone tools. Using a two-observer method, we quantified the magnitude of the social influences that sustain this long period of practice. During five collection periods (over 26 months), one observer recorded the behavior of 16 immature monkeys, and another observer concurrently recorded behavior of group members in the focal monkey's vicinity. The two-observer method provides a means to quantify distinct social influences. Data show that immatures match the behavior of the adults in time and especially in space. The rate of manipulation of nuts by the immatures quadrupled when others in the group cracked and ate nuts, and immatures were ten times more likely to handle nuts and 40 times more likely to strike a nut with a stone when they themselves were near the anvils. Moreover, immature monkeys were three times more likely to be near an anvil when others were cracking. We suggest a model for social influence on nut-cracking development, based on two related processes: (1) social facilitation from observing group members engaged in nut-cracking, and (2) opportunity for practice provided by the anvils, hammer stones and nut shells available on and around the anvils. Nut-cracking activities by others support learning by drawing immatures to the anvils, where extended practice can take place, and by providing materials for practice at these places.

Molecular-dynamics Simulation-based Cohesive Zone Representation of Intergranular Fracture Processes in Aluminum

NASA Technical Reports Server (NTRS)

Yamakov, Vesselin I.; Saether, Erik; Phillips, Dawn R.; Glaessgen, Edward H.

2006-01-01

A traction-displacement relationship that may be embedded into a cohesive zone model for microscale problems of intergranular fracture is extracted from atomistic molecular-dynamics simulations. A molecular-dynamics model for crack propagation under steady-state conditions is developed to analyze intergranular fracture along a flat 99 [1 1 0] symmetric tilt grain boundary in aluminum. Under hydrostatic tensile load, the simulation reveals asymmetric crack propagation in the two opposite directions along the grain boundary. In one direction, the crack propagates in a brittle manner by cleavage with very little or no dislocation emission, and in the other direction, the propagation is ductile through the mechanism of deformation twinning. This behavior is consistent with the Rice criterion for cleavage vs. dislocation blunting transition at the crack tip. The preference for twinning to dislocation slip is in agreement with the predictions of the Tadmor and Hai criterion. A comparison with finite element calculations shows that while the stress field around the brittle crack tip follows the expected elastic solution for the given boundary conditions of the model, the stress field around the twinning crack tip has a strong plastic contribution. Through the definition of a Cohesive-Zone-Volume-Element an atomistic analog to a continuum cohesive zone model element - the results from the molecular-dynamics simulation are recast to obtain an average continuum traction-displacement relationship to represent cohesive zone interaction along a characteristic length of the grain boundary interface for the cases of ductile and brittle decohesion. Keywords: Crack-tip plasticity; Cohesive zone model; Grain boundary decohesion; Intergranular fracture; Molecular-dynamics simulation

Stress-intensity factors of r-cracks in fiber-reinforced composites under thermal and mechanical loading

NASA Astrophysics Data System (ADS)

Mueller, W. H.; Schmauder, S.

1993-02-01

This paper is concerned with the problem of the calculation of stress-intensity factors at the tips of radial matrix cracks (r-cracks) in fiber-reinforced composites under thermal and/or transverse uniaxial or biaxial mechanical loading. The crack is either located in the immediate vicinity of a single fiber or it terminates at the interface between the fiber and the matrix. The problem is stated and solved numerically within the framework of linear elasticity using Erdogan's integral equation technique. It is shown that the solutions for purely thermal and purely mechanical loading can simply be superimposed in order to obtain the results of the combined loading case. Stress-intensity factors (SIFs) are calculated for various lengths and distances of the crack from the interface for each of these loading conditions. The behavior of the SIFs for cracks growing towards or away from the interface is examined. The role of the elastic mismatch between the fibers and the matrix is emphasized and studied extensively using the so-called Dundurs' parameters. It is shown that an r-crack, which is remotely located from the fiber, can either be stabilized or destabilized depending on both the elastic as well as the thermal mismatch of the fibrous composite. Furthermore, Dundurs' parameters are used to predict the exponent of the singularity of the crack tip elastic field and the behavior of the corresponding SIFs for cracks which terminate at the interface. An analytical solution for the SIFs is derived for all three loading conditions under the assumption that the elastic constants of the matrix and the fiber are equal. It is shown that the analytical solution is in good agreement with the corresponding numerical results. Moreover, another analytical solution from the literature, which is based upon Paris' equation for the calculation of stress-intensity factors, is compared with the numerical results and it is shown to be valid only for extremely short r-cracks touching the interface. The numerical results presented are valid for practical fiber composites with r-cracks close to or terminating at the interface provided the matrix material is brittle and the crack does not interact with other neighboring fibers. They may be applied to predict the transverse mechanical behavior of high strength fiber composites.

Modified silicon carbide whiskers

DOEpatents

Tiegs, Terry N.; Lindemer, Terrence B.

1991-01-01

Silicon carbide whisker-reinforced ceramic composites are fabricated in a highly reproducible manner by beneficating the surfaces of the silicon carbide whiskers prior to their usage in the ceramic composites. The silicon carbide whiskers which contain considerable concentrations of surface oxides and other impurities which interact with the ceramic composite material to form a chemical bond are significantly reduced so that only a relatively weak chemical bond is formed between the whisker and the ceramic material. Thus, when the whiskers interact with a crack propagating into the composite the crack is diverted or deflected along the whisker-matrix interface due to the weak chemical bonding so as to deter the crack propagation through the composite. The depletion of the oxygen-containing compounds and other impurities on the whisker surfaces and near surface region is effected by heat treating the whiskers in a suitable oxygen sparaging atmosphere at elevated temperatures. Additionally, a sedimentation technique may be utilized to remove whiskers which suffer structural and physical anomalies which render them undesirable for use in the composite. Also, a layer of carbon may be provided on the surface of the whiskers to further inhibit chemical bonding of the whiskers to the ceramic composite material.

Modified silicon carbide whiskers

DOEpatents

Tiegs, T.N.; Lindemer, T.B.

1991-05-21

Silicon carbide whisker-reinforced ceramic composites are fabricated in a highly reproducible manner by beneficating the surfaces of the silicon carbide whiskers prior to their usage in the ceramic composites. The silicon carbide whiskers which contain considerable concentrations of surface oxides and other impurities which interact with the ceramic composite material to form a chemical bond are significantly reduced so that only a relatively weak chemical bond is formed between the whisker and the ceramic material. Thus, when the whiskers interact with a crack propagating into the composite the crack is diverted or deflected along the whisker-matrix interface due to the weak chemical bonding so as to deter the crack propagation through the composite. The depletion of the oxygen-containing compounds and other impurities on the whisker surfaces and near surface region is effected by heat treating the whiskers in a suitable oxygen sparging atmosphere at elevated temperatures. Additionally, a sedimentation technique may be utilized to remove whiskers which suffer structural and physical anomalies which render them undesirable for use in the composite. Also, a layer of carbon may be provided on the surface of the whiskers to further inhibit chemical bonding of the whiskers to the ceramic composite material.

Ceramic composites reinforced with modified silicon carbide whiskers and method for modifying the whiskers

DOEpatents

Tiegs, Terry N.; Lindemer, Terrence B.

1991-01-01

Silicon carbide whisker-reinforced ceramic composites are fabricated in a highly reproducible manner by beneficating the surfaces of the silicon carbide whiskers prior to their usage in the ceramic composites. The silicon carbide whiskers which contain considerable concentrations of surface oxides and other impurities which interact with the ceramic composite material to form a chemical bond are significantly reduced so that only a relatively weak chemical bond is formed between the whisker and the ceramic material. Thus, when the whiskers interact with a crack propagating into the composite the crack is diverted or deflected along the whisker-matrix interface due to the weak chemical bonding so as to deter the crack propagation through the composite. The depletion of the oxygen-containing compounds and other impurities on the whisker surfaces and near surface region is effected by heat treating the whiskers in a suitable oxygen sparaging atmosphere at elevated temperatures. Additionally, a sedimentation technique may be utilized to remove whiskers which suffer structural and physical anomalies which render them undesirable for use in the composite. Also, a layer of carbon may be provided on the surface of the whiskers to further inhibit chemical bonding of the whiskers to the ceramic composite material.

Ceramic composites reinforced with modified silicon carbide whiskers and method for modifying the whiskers

DOEpatents

Tiegs, T.N.; Lindemer, T.B.

1991-02-19

Silicon carbide whisker-reinforced ceramic composites are fabricated in a highly reproducible manner by beneficating the surfaces of the silicon carbide whiskers prior to their usage in the ceramic composites. The silicon carbide whiskers which contain considerable concentrations of surface oxides and other impurities which interact with the ceramic composite material to form a chemical bond are significantly reduced so that only a relatively weak chemical bond is formed between the whisker and the ceramic material. Thus, when the whiskers interact with a crack propagating into the composite the crack is diverted or deflected along the whisker-matrix interface due to the weak chemical bonding so as to deter the crack propagation through the composite. The depletion of the oxygen-containing compounds and other impurities on the whisker surfaces and near surface region is effected by heat treating the whiskers in a suitable oxygen sparging atmosphere at elevated temperatures. Additionally, a sedimentation technique may be utilized to remove whiskers which suffer structural and physical anomalies which render them undesirable for use in the composite. Also, a layer of carbon may be provided on the surface of the whiskers to further inhibit chemical bonding of the whiskers to the ceramic composite material.

Ceramic composites reinforced with modified silicon carbide whiskers

DOEpatents

Tiegs, Terry N.; Lindemer, Terrence B.

1990-01-01

Silicon carbide whisker-reinforced ceramic composites are fabricated in a highly reproducible manner by beneficating the surfaces of the silicon carbide whiskers prior to their usage in the ceramic composites. The silicon carbide whiskers which contain considerable concentrations of surface oxides and other impurities which interact with the ceramic composite material to form a chemical bond are significantly reduced so that only a relatively weak chemical bond is formed between the whisker and the ceramic material. Thus, when the whiskers interact with a crack propagating into the composite the crack is diverted or deflected along the whisker-matrix interface due to the weak chemical bonding so as to deter the crack propagation through the composite. The depletion of the oxygen-containing compounds and other impurities on the whisker surfaces and near surface region is effected by heat treating the whiskers in a suitable oxygen sparaging atmosphere at elevated temperatures. Additionally, a sedimentation technique may be utilized to remove whiskers which suffer structural and physical anomalies which render them undesirable for use in the composite. Also, a layer of carbon may be provided on the surface of the whiskers to further inhibit chemical bonding of the whiskers to the ceramic composite material.

Deformation-induced structural transition in body-centred cubic molybdenum

PubMed Central

Wang, S. J.; Wang, H.; Du, K.; Zhang, W.; Sui, M. L.; Mao, S. X.

2014-01-01

Molybdenum is a refractory metal that is stable in a body-centred cubic structure at all temperatures before melting. Plastic deformation via structural transitions has never been reported for pure molybdenum, while transformation coupled with plasticity is well known for many alloys and ceramics. Here we demonstrate a structural transformation accompanied by shear deformation from an original <001>-oriented body-centred cubic structure to a <110>-oriented face-centred cubic lattice, captured at crack tips during the straining of molybdenum inside a transmission electron microscope at room temperature. The face-centred cubic domains then revert into <111>-oriented body-centred cubic domains, equivalent to a lattice rotation of 54.7°, and ~15.4% tensile strain is reached. The face-centred cubic structure appears to be a well-defined metastable state, as evidenced by scanning transmission electron microscopy and nanodiffraction, the Nishiyama–Wassermann and Kurdjumov–Sachs relationships between the face-centred cubic and body-centred cubic structures and molecular dynamics simulations. Our findings reveal a deformation mechanism for elemental metals under high-stress deformation conditions. PMID:24603655

What's So Hard about Staff Development? A Study in Face-to-Face Interaction. Occasional Paper No. 14.

ERIC Educational Resources Information Center

Anang, Arlene; Florio-Ruane, Susan

Staff development carried out within a conference format is multidimensional, ambiguous, potentially face-threatening, and complex. It is dependent upon the interactional work that takes place during face-to-face negotiations. The skills and knowledge of the staff developer cannot be shared with a teacher in a vacuum, but are dependent upon the…

Investigating the association between social interactions and personality states dynamics

PubMed Central

Finnerty, Ailbhe N.; Staiano, Jacopo; Teso, Stefano; Passerini, Andrea; Pianesi, Fabio; Lepri, Bruno

2017-01-01

The recent personality psychology literature has coined the name of personality states to refer to states having the same behavioural, affective and cognitive content (described by adjectives) as the corresponding trait, but for a shorter duration. The variability in personality states may be the reaction to specific characteristics of situations. The aim of our study is to investigate whether specific situational factors, that is, different configurations of face-to-face interactions, are predictors of variability of personality states in a work environment. The obtained results provide evidence that within-person variability in personality is associated with variation in face-to-face interactions. Interestingly, the effects differ by type and level of the personality states: adaptation effects for Agreeableness and Emotional Stability, whereby the personality states of an individual trigger similar states in other people interacting with them and complementarity effects for Openness to Experience, whereby the personality states of an individual trigger opposite states in other people interacting with them. Overall, these findings encourage further research to characterize face-to-face and social interactions in terms of their relevance to personality states. PMID:28989732

A Comparison of Mental Health Diagnoses Treated via Interactive Video and Face to Face in the Veterans Healthcare Administration.

PubMed

Grubbs, Kathleen M; Fortney, John C; Dean, Tisha; Williams, James S; Godleski, Linda

2015-07-01

This study compares the mental health diagnoses of encounters delivered face to face and via interactive video in the Veterans Healthcare Administration (VHA). We compiled 1 year of national-level VHA administrative data for Fiscal Year 2012 (FY12). Mental health encounters were those with both a VHA Mental Health Stop Code and a Mental Health Diagnosis (n=11,906,114). Interactive video encounters were identified as those with a Mental Health Stop Code, paired with a VHA Telehealth Secondary Stop Code. Primary diagnoses were grouped into posttraumatic stress disorder (PTSD), depression, anxiety, bipolar disorder, psychosis, drug use, alcohol use, and other. In FY12, 1.5% of all mental health encounters were delivered via interactive video. Compared with face-to-face encounters, a larger percentage of interactive video encounters was for PTSD, depression, and anxiety, whereas a smaller percentage was for alcohol use, drug use, or psychosis. Providers and patients may feel more comfortable treating depression and anxiety disorders than substance use or psychosis via interactive video.

Investigating the association between social interactions and personality states dynamics.

PubMed

Gundogdu, Didem; Finnerty, Ailbhe N; Staiano, Jacopo; Teso, Stefano; Passerini, Andrea; Pianesi, Fabio; Lepri, Bruno

2017-09-01

The recent personality psychology literature has coined the name of personality states to refer to states having the same behavioural, affective and cognitive content (described by adjectives) as the corresponding trait, but for a shorter duration. The variability in personality states may be the reaction to specific characteristics of situations. The aim of our study is to investigate whether specific situational factors, that is, different configurations of face-to-face interactions, are predictors of variability of personality states in a work environment. The obtained results provide evidence that within-person variability in personality is associated with variation in face-to-face interactions. Interestingly, the effects differ by type and level of the personality states: adaptation effects for Agreeableness and Emotional Stability, whereby the personality states of an individual trigger similar states in other people interacting with them and complementarity effects for Openness to Experience, whereby the personality states of an individual trigger opposite states in other people interacting with them. Overall, these findings encourage further research to characterize face-to-face and social interactions in terms of their relevance to personality states.

Enhanced Visual Short-Term Memory for Angry Faces

ERIC Educational Resources Information Center

Jackson, Margaret C.; Wu, Chia-Yun; Linden, David E. J.; Raymond, Jane E.

2009-01-01

Although some views of face perception posit independent processing of face identity and expression, recent studies suggest interactive processing of these 2 domains. The authors examined expression-identity interactions in visual short-term memory (VSTM) by assessing recognition performance in a VSTM task in which face identity was relevant and…

On Being Liked on the Web and in the “Real World”: Consistency in First Impressions across Personal Webpages and Spontaneous Behavior

PubMed Central

Weisbuch, Max; Ivcevic, Zorana; Ambady, Nalini

2009-01-01

With recent growth in the use of personal webpages and online social networking, people are changing the way that they meet and form impressions of each other. The current research examines the correspondence in impressions formed from face-to-face interaction and personal webpages. As expected, people liked by interaction partners were also liked on the basis of their Facebook® pages. Across the two social mediums, social perceivers utilized analogous criteria in forming impressions: interaction partners and webpage viewers liked people who were socially expressive in face-to-face interaction and personal webpages, respectively. Finally, webpage expressivity and webpage self-disclosure were independent constructs, predictive of face-to-face counterparts: nonverbal expressivity and verbal self-disclosure. Implications for the changing landscape of social perception are discussed. PMID:20161314

Structures and properties of molecular torsion balances to decipher the nature of substituent effects on the aromatic edge-to-face interaction.

PubMed

Gardarsson, Haraldur; Schweizer, W Bernd; Trapp, Nils; Diederich, François

2014-04-14

Various recent computational studies initiated this systematic re-investigation of substituent effects on aromatic edge-to-face interactions. Five series of Tröger base derived molecular torsion balances (MTBs), initially introduced by Wilcox and co-workers, showing an aromatic edge-to-face interaction in the folded, but not in the unfolded form, were synthesized. A fluorine atom or a trifluoromethyl group was introduced onto the edge ring in ortho-, meta-, and para-positions to the C-H group interacting with the face component. The substituents on the face component were varied from electron-donating to electron-withdrawing. Extensive X-ray crystallographic data allowed for a discussion on the conformational behavior of the torsional balances in the solid state. While most systems adopt the folded conformation, some were found to form supramolecular intercalative dimers, lacking the intramolecular edge-to-face interaction, which is compensated by the gain of aromatic π-stacking interactions between four aryl rings of the two molecular components. This dimerization does not take place in solution. The folding free enthalpy ΔG(fold) of all torsion balances was determined by (1)H NMR measurements by using 10 mM solutions of samples in CDCl3 and C6D6. Only the ΔG(fold) values of balances bearing an edge-ring substituent in ortho-position to the interacting C-H show a steep linear correlation with the Hammett parameter (σ(meta)) of the face-component substituent. Thermodynamic analysis using van't Hoff plots revealed that the interaction is enthalpy-driven. The ΔG(fold) values of the balances, in addition to partial charge calculations, suggest that increasing the polarization of the interacting C-H group makes a favorable contribution to the edge-to-face interaction. The largest contribution, however, seems to originate from local direct interactions between the substituent in ortho-position to the edge-ring C-H and the substituted face ring. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Modeling Quasi-Static and Fatigue-Driven Delamination Migration

NASA Technical Reports Server (NTRS)

De Carvalho, N. V.; Ratcliffe, J. G.; Chen, B. Y.; Pinho, S. T.; Baiz, P. M.; Tay, T. E.

2014-01-01

An approach was proposed and assessed for the high-fidelity modeling of progressive damage and failure in composite materials. It combines the Floating Node Method (FNM) and the Virtual Crack Closure Technique (VCCT) to represent multiple interacting failure mechanisms in a mesh-independent fashion. Delamination, matrix cracking, and migration were captured failure and migration criteria based on fracture mechanics. Quasi-static and fatigue loading were modeled within the same overall framework. The methodology proposed was illustrated by simulating the delamination migration test, showing good agreement with the available experimental data.

Quantitative understanding of the role of grain boundaries in polycrystalline deformation via multiscale digital image correlation

NASA Astrophysics Data System (ADS)

Abuzaid, Wael Z. M.

In this study, high resolution ex situ digital image correlation (DIC) was used to measure plastic strain accumulation in polycrystalline Hastelloy X, a nickel-based superalloy, subjected to monotonic and cyclic loading conditions. In addition, the underlying microstructure was characterized with similar spatial resolution using electron backscatter diffraction (EBSD). The experimental results were utilized to investigate the localization of plastic strains in the vicinity of grain boundaries (GBs). Particularly we address the interaction of slip with GBs which can result in slip blockage or slip transmission and investigate how these two possible outcomes of slip-GB interaction influence the plastic strain magnitudes and fatigue crack formation in GB regions. In the first part of this work, we focus on slip transmission across GBs. Strain measurements with sub-grain level spatial resolution were acquired for Hastelloy X deformed plastically in uniaxial tension. The full field DIC measurements show a high level of heterogeneity in the plastic response with large variations in strain magnitudes within grains and across GBs. We used the experimental results to study these variations in strains, focusing specifically on the role of slip transmission across GBs in the development of strain heterogeneities. For every GB in the polycrystalline aggregate, we have established the most likely dislocation reaction and used that information to calculate the residual Burgers vector and plastic strain magnitudes due to slip transmission across each interface. From our analysis, we show an inverse relation between the magnitudes of the residual Burgers vector and the plastic strains across GBs. We therefore emphasize the importance of considering the magnitude of the residual Burgers vector to obtain a better description of the GB resistance to slip transmission, which in turn influences the local plastic strains in the vicinity of grain boundaries. In the second part of this work, we consider fatigue micro-crack formation. It is widely accepted that the localization in plastic strains is a necessary condition and a precursor for the nucleation of fatigue cracks. However a clear and quantitative assessment of the correlation between strain localization and fatigue micro-crack lengths requires further investigation. To address this point, high resolution deformation measurements using DIC were conducted on polycrystalline Hastelloy X subjected to fatigue loading. The sub-grain level strain measurements were made prior to the formation of micro-cracks. The correlation between the localization of plastic strains, very early on during the loading (e.g., less than 1,000 cycles), and the micro-cracks which were detected later in the life of the sample ( e.g., around 10,000 cycles) is discussed in this thesis. Particular focus is given to the difference in grain boundary response, either blocking or transmitting slip, and the associated fatigue micro-crack lengths generated in the vicinity of these boundaries. The results show a clear correlation between both the locations and lengths of fatigue micro-cracks and the localization of plastic strains very early in the loading process. In addition, we observed that for the same number of cycles, the transmission of slip across grain boundaries resulted in longer transgranular cracks compared to cracks near grains surrounded by blocking grain boundaries which were shorter cracks and confined within single grains. In the last part of this study, experiments were conducted on Hastelloy X subjected to fatigue loading. The purpose of the experiments was to investigate the scatter in fatigue lives under similar loading conditions. We also used a recent novel fatigue model based on persistent slip band (PSB) -- GB interaction to investigate the scatter in fatigue lives and shed light into the critical types of GBs which nucleate cracks. The implementation of this model provides simulation results of the scatter in fatigue life, which are consistent with the scatter observed from experiments. Finally, with the use of high resolution strain measurements, we provide a critical evaluation of some aspects of the modeling approach, for example the formation of grain clusters and their influence on fatigue life. Also the role of special GBs, mainly annealing twin boundaries (Sigma3 GBs), was evaluated.

Social and clinical predictors of drug-resistant tuberculosis in a public hospital, Monterrey, Mexico.

PubMed

Young, Bonnie N; Burgos, Marcos; Handal, Alexis J; Baker, Jack; Rendón, Adrian; Rosas-Taraco, Adrian; Long, Jeffrey; Hunley, Keith

2014-10-01

Drug-resistant tuberculosis (DRTB) is steadily increasing in Mexico, but little is known of patient risk factors in the Mexico-United States border region. This preliminary case-control study included 95 patients with active pulmonary TB with drug susceptibility results attending the José E. González University Hospital in the urban hub of Nuevo León-the Monterrey Metropolitan Area. We report potential social and clinical risk factors of DRTB among this hospital-based sample. We collected data through face-to-face interviews and medical record reviews from 25 cases with DRTB and 70 drug-sensitive controls. DNA was collected to assess an effect of genetic ancestry on DRTB by using a panel of 291,917 genomic markers. We calculated crude and multivariate logistic regression. After adjusting for potential confounding factors, we found that prior TB treatment (odds ratio, 4.5; 95% confidence interval, 0.9-21.1) and use of crack cocaine (odds ratio, 4.6; 95% confidence interval, 1.1-18.7) were associated with DRTB. No other variables, including genetic ancestry and comorbidities, were predictive. Health care providers may benefit from recognizing predictors of DRTB in regions where routine drug susceptibility testing is limited. Prior TB treatment and illicit drug use, specifically crack cocaine, may be important risk factors for DRTB in this region. Copyright © 2014 Elsevier Inc. All rights reserved.

Face-to-face: Perceived personal relevance amplifies face processing.

PubMed

Bublatzky, Florian; Pittig, Andre; Schupp, Harald T; Alpers, Georg W

2017-05-01

The human face conveys emotional and social information, but it is not well understood how these two aspects influence face perception. In order to model a group situation, two faces displaying happy, neutral or angry expressions were presented. Importantly, faces were either facing the observer, or they were presented in profile view directed towards, or looking away from each other. In Experiment 1 (n = 64), face pairs were rated regarding perceived relevance, wish-to-interact, and displayed interactivity, as well as valence and arousal. All variables revealed main effects of facial expression (emotional > neutral), face orientation (facing observer > towards > away) and interactions showed that evaluation of emotional faces strongly varies with their orientation. Experiment 2 (n = 33) examined the temporal dynamics of perceptual-attentional processing of these face constellations with event-related potentials. Processing of emotional and neutral faces differed significantly in N170 amplitudes, early posterior negativity (EPN), and sustained positive potentials. Importantly, selective emotional face processing varied as a function of face orientation, indicating early emotion-specific (N170, EPN) and late threat-specific effects (LPP, sustained positivity). Taken together, perceived personal relevance to the observer-conveyed by facial expression and face direction-amplifies emotional face processing within triadic group situations. © The Author (2017). Published by Oxford University Press.

Synchrotron Vacuum Ultraviolet Light and Soft X-Ray Radiation Effects on Aluminized Teflon FEP Investigated

NASA Technical Reports Server (NTRS)

Dever, Joyce A.; Townsend, Jacqueline A.; Gaier, James R.; Jalics, Alice I.

1999-01-01

Since the Hubble Space Telescope (HST) was deployed in low Earth orbit in April 1990, two servicing missions have been conducted to upgrade its scientific capabilities. Minor cracking of second-surface metalized Teflon FEP (DuPont; fluorinated ethylene propylene) surfaces from multilayer insulation (MLI) was first observed upon close examination of samples with high solar exposure retrieved during the first servicing mission, which was conducted 3.6 years after deployment. During the second HST servicing mission, 6.8 years after deployment, astronaut observations and photographic documentation revealed significant cracks in the Teflon FEP layer of the MLI on both the solar- and anti-solar-facing surfaces of the telescope. NASA Goddard Space Flight Center directed the efforts of the Hubble Space Telescope MLI Failure Review Board, whose goals included identifying the low-Earth-orbit environmental constituent(s) responsible for the cracking and embrittling of Teflon FEP which was observed during the second servicing mission. The NASA Lewis Research Center provided significant support to this effort. Because soft x-ray radiation from solar flares had been considered as a possible cause for the degradation of the mechanical properties of Teflon FEP (ref. 1), the effects of soft xray radiation and vacuum ultraviolet light on Teflon FEP were investigated. In this Lewisled effort, samples of Teflon FEP with a 100-nm layer of vapor-deposited aluminum (VDA) on the backside were exposed to synchrotron radiation of various vacuum ultraviolet and soft x-ray wavelengths between 18 nm (69 eV) and 0.65 nm (1900 eV). Synchrotron radiation exposures were conducted using the National Synchrotron Light Source at Brookhaven National Laboratory. Samples of FEP/VDA were exposed with the FEP surface facing the synchrotron beam. Doses and fluences were compared with those estimated for the 20-yr Hubble Space Telescope mission.

Advanced Vacuum Plasma Spray (VPS) for a Robust, Longlife and Safe Space Shuttle Main Engine (SSME)

NASA Technical Reports Server (NTRS)

Holmes, Richard R.; Elam, Sandra K.; McKechnie, Timothy N.; Power, Christopher A.

2010-01-01

In 1984, the Vacuum Plasma Spray Lab was built at NASA/Marshall Space Flight Center for applying durable, protective coatings to turbine blades for the space shuttle main engine (SSME) high pressure fuel turbopump. Existing turbine blades were cracking and breaking off after five hot fire tests while VPS coated turbine blades showed no wear or cracking after 40 hot fire tests. Following that, a major manufacturing problem of copper coatings peeling off the SSME Titanium Main Fuel Valve Housing was corrected with a tenacious VPS copper coating. A patented VPS process utilizing Functional Gradient Material (FGM) application was developed to build ceramic lined metallic cartridges for space furnace experiments, safely containing gallium arsenide at 1260 degrees centigrade. The VPS/FGM process was then translated to build robust, long life, liquid rocket combustion chambers for the space shuttle main engine. A 5K (5,000 Lb. thrust) thruster with the VPS/FGM protective coating experienced 220 hot firing tests in pristine condition with no wear compared to the SSME which showed blanching (surface pulverization) and cooling channel cracks in less than 30 of the same hot firing tests. After 35 of the hot firing tests, the injector face plates disintegrated. The VPS/FGM process was then applied to spraying protective thermal barrier coatings on the face plates which showed 50% cooler operating temperature, with no wear after 50 hot fire tests. Cooling channels were closed out in two weeks, compared to one year for the SSME. Working up the TRL (Technology Readiness Level) to establish the VPS/FGM process as viable technology, a 40K thruster was built and is currently being tested. Proposed is to build a J-2X size liquid rocket engine as the final step in establishing the VPS/FGM process TRL for space flight.

Interactive Distance Learning Effectively Provides Winning Sports Nutrition Workshops.

ERIC Educational Resources Information Center

Ricketts, Jennifer; Hoelscher-Day, Sharon; Begeman, Gale; Houtkooper, Linda

2001-01-01

Interactive distance-education (n=226) and face-to-face (n=129) continuing education workshops for health care and education professionals on sports nutrition were evaluated immediately and after 6 months. The well-designed distance-education format was as effective and acceptable as face to face and increased sports nutrition knowledge. (SK)

Explaining Student Interaction and Satisfaction: An Empirical Investigation of Delivery Mode Influence

ERIC Educational Resources Information Center

Johnson, Zachary S.; Cascio, Robert; Massiah, Carolyn A.

2014-01-01

How interpersonal interactions within a course affect student satisfaction differently between face-to-face and online modes is an important research question to answer with confidence. Using students from a marketing course delivered face-to-face and online concurrently, our first study demonstrates that student-to-professor and…

Children Can Learn New Facts Equally Well From Interactive Media Versus Face to Face Instruction

PubMed Central

Kwok, Kristine; Ghrear, Siba; Li, Vivian; Haddock, Taeh; Coleman, Patrick; Birch, Susan A. J.

2016-01-01

Today’s children have more opportunities than ever before to learn from interactive technology, yet experimental research assessing the efficacy of children’s learning from interactive media in comparison to traditional learning approaches is still quite scarce. Moreover, little work has examined the efficacy of using touch-screen devices for research purposes. The current study compared children’s rate of learning factual information about animals during a face-to-face instruction from an adult female researcher versus an analogous instruction from an interactive device. Eighty-six children ages 4 through 8 years (64% male) completed the learning task in either the Face-to-Face condition (n = 43) or the Interactive Media condition (n = 43). In the Learning Phase of the experiment, which was presented as a game, children were taught novel facts about animals without being told that their memory of the facts would be tested. The facts were taught to the children either by an adult female researcher (Face-to-Face condition) or from a pre-recorded female voice represented by a cartoon Llama (Interactive Media condition). In the Testing Phase of the experiment that immediately followed, children’s memory for the taught facts was tested using a 4-option forced-choice paradigm. Children’s rate of learning was significantly above chance in both conditions and a comparison of the rates of learning across the two conditions revealed no significant differences. Learning significantly improved from age 4 to age 8, however, even the preschool-aged children performed significantly above chance, and their performance did not differ between conditions. These results suggest that, interactive media can be equally as effective as one-on-one instruction, at least under certain conditions. Moreover, these results offer support for the validity of using interactive technology to collect data for research purposes. We discuss the implications of these results for children’s learning from interactive media, parental attitudes about interactive technology, and research methods. PMID:27826263

A study of spectrum fatigue crack propagation in two aluminum alloys. 2: Influence of microstructures

NASA Technical Reports Server (NTRS)

Telesman, J.; Antolovich, S. D.

1985-01-01

The important metallurgical factors that influence both constant amplitude and spectrum crack growth behavior in aluminum alloys were investigated. The effect of microstructural features such as grain size, inclusions, and dispersoids was evaluated. It was shown that a lower stress intensities, the I/M 7050 alloy showed better fatigue crack propagation (FCP) resistance than P/M 7091 alloy for both constant amplitude and spectrum testing. It was suggested that the most important microstructural variable accounting for superior FCP resistance of 7050 alloy is its large grain size. It was further postulated that the inhomogenous planar slip and large grain size of 7050 limit dislocation interactions and thus increase slip reversibility which improves FCP performance. The hypothesis was supported by establishing that the cyclic strain hardening exponent for the 7091 alloy is higher than that of 7050.

Attention Deficit Hyperactivity Disorder, Aggression, and Illicit Stimulant Use: Is This Self-Medication?

PubMed

Odell, Annie P; Reynolds, Grace L; Fisher, Dennis G; Huckabay, Loucine M; Pedersen, William C; Xandre, Pamela; Miočević, Milica

2017-05-01

This study compares adults with and without attention deficit hyperactivity disorder (ADHD) on measures of direct and displaced aggression and illicit drug use. Three hundred ninety-six adults were administered the Wender Utah Rating Scale, the Risk Behavior Assessment, the Aggression Questionnaire (AQ), and the Displaced Aggression Questionnaire (DAQ). Those with ADHD were higher on all scales of the AQ and DAQ, were younger at first use of amphetamines, and were more likely to have ever used crack and amphetamines. A Structural Equation Model found a significant interaction in that for those with medium and high levels of verbal aggression, ADHD predicts crack and amphetamine. Follow-up logistic regression models suggest that blacks self-medicate with crack and whites and Hispanics self-medicate with amphetamine when they have ADHD and verbal aggression.

Fractographic evaluation of creep effects on strain-controlled fatigue-cracking of AISI 304LC and 316 stainless steel

NASA Technical Reports Server (NTRS)

Oldrieve, R. E.

1978-01-01

Analysis of high temperature low cycle fatigue of AISI 304LC and 316 stainless steels by the method of strainrange partitioning results in four separate strainrange versus life relationships, depending upon the way in which creep-strain and plastic strain are combined within a cycle. Fractography is used in this investigation of the creep-fatigue interaction associated with these cycles. The PP and PC-cycle fractures were transgranular. The PC-cycle resulted in fewer cycles of initiation and shorter total cyclic life for the same applied inelastic strainrange. The CC-cycle had mixed transgranular and intergranular fracture, fewer cycles of initiation and shorter cycle life than PP or PC. The CP-cycle had fully integranular cracking, and failed in fewer cycles than were required for cracks to initate for PP,PC, and CC.

Investigation of smooth specimen scc test procedures; variations in environment, specimen size, stressing frame, and stress state. [for high strength aluminum alloys

NASA Technical Reports Server (NTRS)

Lifka, B. W.; Sprowls, D. O.; Kelsey, R. A.

1975-01-01

The variables studied in the stress-corrosion cracking performance of high strength aluminum alloys were: (1) corrosiveness of the environment, (2) specimen size and stiffness of the stressing system, (3) interpretation of transgranular cracking, and (4) interaction of the state of stress and specimen orientation in a product with an anisotropic grain structure. It was shown that the probability of failure and time to fracture for a specimen loaded in direct tension are influenced by corrosion pattern, the stressing assembly stiffness, and the notch tensile strength of the alloy. Results demonstrate that the combination of a normal tension stress and a shear stress acting on the plane of maximum susceptibility in a product with a highly directional grain cause the greatest tendency for stress-corrosion cracking.

Inter-hemispheric interaction facilitates face processing.

PubMed

Compton, Rebecca J

2002-01-01

Many recent studies have revealed that interaction between the left and right cerebral hemispheres can aid in task performance, but these studies have tended to examine perception of simple stimuli such as letters, digits or simple shapes, which may have limited naturalistic validity. The present study extends these prior findings to a more naturalistic face perception task. Matching tasks required subjects to indicate when a target face matched one of two probe faces. Matches could be either across-field, requiring inter-hemispheric interaction, or within-field, not requiring inter-hemispheric interaction. Subjects indicated when faces matched in emotional expression (Experiment 1; n=32) or in character identity (Experiment 2; n=32). In both experiments, across-field performance was significantly better than within-field performance, supporting the primary hypothesis. Further, this advantage was greater for the more difficult character identity task. Results offer qualified support for the hypothesis that inter-hemispheric interaction is especially advantageous as task demands increase.

Effects of the earthquake of March 27, 1964 in the Copper River Basin area, Alaska: Chapter E in The Alaska earthquake, March 27, 1964: regional effects

USGS Publications Warehouse

Ferrians, Oscar J.

1966-01-01

The Copper River Basin area is in south-central Alaska and covers 17,800 square miles. It includes most of the Copper River Basin and parts of the surrounding Alaska Range and the Talkeetna, Chugach, and Wrangell Mountains. On March 27, 1964, shortly after 5:36 p.m. Alaska standard time, a great earthquake having a Richter magnitude of about 8.5 struck south-central Alaska. Computations by the U.S. Coast and Geodetic Survey place the epicenter of the main shock at lat 61.1° N. and long 147.7° W., and the hypocenter, or actual point of origin, from 20 to 50 kilometers below the surface. The epicenter is near the western shore of Unakwik Inlet in northern Prince William Sound; it is 30 miles from the closest point within the area of study and 180 miles from the farthest point. Releveling data obtained in 1964 after the earthquake indicates that broad areas of south-central Alaska were warped by uplift and subsidence. The configuration of these areas generally parallels the trend of the major tectonic elements of the region. Presumably a large part of this change took place during and immediately after the 1964 earthquake. The water level in several wells in the area lowered appreciably, and the water in many became turbid; generally, however, within a few days after the earthquake the water level returned to normal and the suspended sediment settled out. Newspaper reports that the Copper River was completely dammed and Tazlina Lake drained proved erroneous. The ice on most lakes was cracked, especially around the margins of the lakes where floating ice broke free from the ice frozen to the shore. Ice on Tazlina, Klutina, and Tonsina Lakes was intensely fractured by waves generated by sublacustrine landslides off the fronts of deltas. These waves stranded large blocks of ice above water level along the shores. River ice was generally cracked in the southern half of the area and was locally cracked in the northern half. In the area of study, the majority of the ground cracks occurred within a radius of 100 miles from the epicenter of the earthquake. Ground cracks formed in flood plains of rivers, in deltas, and along the toes of alluvial fans. They also occurred locally in low terraces adjacent to flood plains, in highway and other fill material, along the margins of lakes, along the faces of steep slopes of river bluffs and hillsides, and in areas cleared of vegetation for several years. The ground cracks were restricted to areas underlain by unconsolidated deposits where one or more of the following conditions existed: (1) permafrost was absent or deep lying, (2) the ground-water table was near the surface, (3) bedrock was relatively deep lying, and (4) slopes were steep. Because the earthquake occurred in March, seasonal frost was present throughout the area. Despite the diversity of local conditions, the origin of most of the ground cracks can be explained by the following mechanisms: (1) lateral extension, caused by materials moving toward an unconfined face such as a lakeshore, river bluff, hillside, or terrace escarpment; (2) horizontal compaction, caused by repeated alternate compression and dilation (in the horizontal direction) of materials in flat-lying areas where there are no unconfined faces; (3) differential vertical compaction, caused by the shaking of materials that vary laterally in thickness or character; and (4) combinations of the above. Snowslides, avalanches, and rockslides were restricted to the mountainous areas surrounding the Copper River Basin. They were especially numerous in the Chugach Mountains which are closest to the epicenter of the earthquake. The large amount of snow and rock debris that has cascaded onto the icefield and glaciers of these mountains, and, probably even more important, the overall disturbance to the ice field will affect the regimen of the glaciers. Most of the damage to manmade structures occurred in the southern half of the area, and, primarily because of the sparsity of population and manmade structures, property damage was not great and no lives were lost.

Nonlinear Lamb waves for fatigue damage identification in FRP-reinforced steel plates.

PubMed

Wang, Yikuan; Guan, Ruiqi; Lu, Ye

2017-09-01

A nonlinear Lamb-wave-based method for fatigue crack detection in steel plates with and without carbon fibre reinforcement polymer (CFRP) reinforcement is presented in this study. Both numerical simulation and experimental evaluation were performed for Lamb wave propagation and its interaction with a fatigue crack on these two steel plate types. With the generation of the second harmonic, the damage-induced wave nonlinearities were identified by surface-bonded piezoelectric sensors. Numerical simulation revealed that the damage-induced wave component at the second harmonic was slightly affected by the existence of CFRP laminate, although the total wave energy was decreased because of wave leakage into the CFRP laminate. Due to unavoidable nonlinearity from the experimental environments, it was impractical to directly extract the time-of-flight of the second harmonic for locating the crack. To this end, the correlation coefficient of benchmark and signal with damage at double frequency in the time domain was calculated, based on which an imaging method was introduced to locate the fatigue crack in steel plates with and without CFRP laminates. Copyright © 2017 Elsevier B.V. All rights reserved.

Numerical analysis of a main crack interactions with micro-defects/inhomogeneities using two-scale generalized/extended finite element method

NASA Astrophysics Data System (ADS)

Malekan, Mohammad; Barros, Felício B.

2017-12-01

Generalized or extended finite element method (G/XFEM) models the crack by enriching functions of partition of unity type with discontinuous functions that represent well the physical behavior of the problem. However, this enrichment functions are not available for all problem types. Thus, one can use numerically-built (global-local) enrichment functions to have a better approximate procedure. This paper investigates the effects of micro-defects/inhomogeneities on a main crack behavior by modeling the micro-defects/inhomogeneities in the local problem using a two-scale G/XFEM. The global-local enrichment functions are influenced by the micro-defects/inhomogeneities from the local problem and thus change the approximate solution of the global problem with the main crack. This approach is presented in detail by solving three different linear elastic fracture mechanics problems for different cases: two plane stress and a Reissner-Mindlin plate problems. The numerical results obtained with the two-scale G/XFEM are compared with the reference solutions from the analytical, numerical solution using standard G/XFEM method and ABAQUS as well, and from the literature.

Interactions Between Chlorinated Waste Solvents and Clay Minerals in Low Permeability Subsurface Layers

NASA Astrophysics Data System (ADS)

Ayral, D.; Otero-Diaz, M.; Demond, A. H.

2014-12-01

Waste organic contaminants stored in low permeability subsurface layers serve as long-term sources for dissolved phase contaminant plumes. These layers may have a different mineralogical make up than the surrounding geologic media; specifically, they may be characterized by a high clay content. Although these layers are often considered inert, interactions may occur between the clay minerals and the waste liquids that may influence transport. Measurements of the basal spacing of Na-montmorillonite in contact with pure chlorinated organic liquids such as trichloroethylene (TCE) showed that it is similar to that with water; however, its basal spacing in contact with waste chlorinated liquids was reduced, leading to cracking. In fact, the basal spacing in contact with the waste chlorinated liquids was closer to that in contact with air than in contact with water. The observation that contact with pure organic liquids did not cause cracking, but contact with chlorinated wastes obtained from the field did, suggests that other components of the waste are critical to the basal spacing reduction process. Screening experiments indicated that the presence of a binary mixture of surfactants, a nonionic and an anionic surfactant, in the chlorinated solvent were necessary to cause the cracking at the same rate and magnitude as the chlorinated wastes obtained from the field. Fourier transform infrared (FT-IR) spectroscopy measurements suggest that the mixture alters the adsorbed water OH-bending band, implying a displacement of adsorbed water. Coupling these results with sorption and x-ray diffraction (XRD) measurements, a hypothesis of component conformation in the clay interlayer space that leads to cracking can be constructed.

Learning Opportunities in Synchronous Computer-Mediated Communication and Face-to-Face Interaction

ERIC Educational Resources Information Center

Kim, Hye Yeong

2014-01-01

This study investigated how synchronous computer-mediated communication (SCMC) and face-to-face (F2F) oral interaction influence the way in which learners collaborate in language learning and how they solve their communicative problems. The findings suggest that output modality may affect how learners produce language, attend to linguistic forms,…

Internet Communication versus Face-to-Face Interaction in Quality of Life

ERIC Educational Resources Information Center

Lee, Paul S. N.; Leung, Louis; Lo, Venhwei; Xiong, Chengyu; Wu, Tingjun

2011-01-01

This study seeks to understand the role of the Internet in quality of life (QoL). Specifically, it examines the question of whether Internet communication serves, like face-to-face interactions, to enhance quality of life. It is hypothesized that the use of the Internet for interpersonal communication can improve quality of life among Internet…

A Working Typology of Intentions Driving Face-to-Face and Online Interaction in a Graduate Teacher Education Course.

ERIC Educational Resources Information Center

Vrasidas, Charalambos

2002-01-01

Describes a study that examined the intentions, social organization, and meaning of online interaction in a graduate distance education course in teacher education delivered by a combination of online and face-to-face instruction. Explains the theoretical framework which was based on symbolic interactionism and the methodological approach which…

Impression Management in Kindergarten Classrooms: An Analysis of Children's Face-Work in Peer Interactions.

ERIC Educational Resources Information Center

Hatch, J. Amos

A systematic analysis was made of the communications of 5- and 6-year-old children in two kindergarten classrooms to discover whether children's face-to-face interactions with peers included "face work" components (rituals through which individuals manage impressions when it becomes difficult to maintain a social situation) and, if so,…

The failure of brittle materials under overall compression: Effects of loading rate and defect distribution

NASA Astrophysics Data System (ADS)

Paliwal, Bhasker

The constitutive behaviors and failure processes of brittle materials under far-field compressive loading are studied in this work. Several approaches are used: experiments to study the compressive failure behavior of ceramics, design of experimental techniques by means of finite element simulations, and the development of micro-mechanical damage models to analyze and predict mechanical response of brittle materials under far-field compression. Experiments have been conducted on various ceramics, (primarily on a transparent polycrystalline ceramic, aluminum oxynitride or AlON) under loading rates ranging from quasi-static (˜ 5X10-6) to dynamic (˜ 200 MPa/mus), using a servo-controlled hydraulic test machine and a modified compression Kolsky bar (MKB) technique respectively. High-speed photography has also been used with exposure times as low as 20 ns to observe the dynamic activation, growth and coalescence of cracks and resulting damage zones in the specimen. The photographs were correlated in time with measurements of the stresses in the specimen. Further, by means of 3D finite element simulations, an experimental technique has been developed to impose a controlled, homogeneous, planar confinement in the specimen. The technique can be used in conjunction with a high-speed camera to study the in situ dynamic failure behavior of materials under confinement. AlON specimens are used for the study. The statically pre-compressed specimen is subjected to axial dynamic compressive loading using the MKB. Results suggest that confinement not only increases the load carrying capacity, it also results in a non-linear stress evolution in the material. High-speed photographs also suggest an inelastic deformation mechanism in AlON under confinement which evolves more slowly than the typical brittle-cracking type of damage in the unconfined case. Next, an interacting micro-crack damage model is developed that explicitly accounts for the interaction among the micro-cracks in brittle materials. The model incorporates pre-existing defect distributions and a crack growth law. The damage is defined as a scalar parameter which is a function of the micro-crack density, the evolution of which is a function of the existing defect distribution and the crack growth dynamics. A specific case of a uniaxial compressive loading under constant strain-rate has been studied to predict the effects of the strain-rate, defect distribution and the crack growth dynamics on the constitutive response and failure behavior of brittle materials. Finally, the effects of crack growth dynamics on the strain-rate sensitivity of brittle materials are studied with the help of the micro-mechanical damage model. The results are compared with the experimentally observed damage evolution and the rate-sensitive behavior of the compressive strength of several engineering ceramics. The dynamic failure of armor-grade hot-pressed boron carbide (B 4C) under loading rates of ˜ 5X10-6 to 200 MPa/mus is also discussed.

Interactive optical panel

DOEpatents

Veligdan, J.T.

1995-10-03

An interactive optical panel assembly includes an optical panel having a plurality of ribbon optical waveguides stacked together with opposite ends thereof defining panel first and second faces. A light source provides an image beam to the panel first face for being channeled through the waveguides and emitted from the panel second face in the form of a viewable light image. A remote device produces a response beam over a discrete selection area of the panel second face for being channeled through at least one of the waveguides toward the panel first face. A light sensor is disposed across a plurality of the waveguides for detecting the response beam therein for providing interactive capability. 10 figs.

Brief Report: Patterns of Eye Movements in Face to Face Conversation are Associated with Autistic Traits: Evidence from a Student Sample.

PubMed

Vabalas, Andrius; Freeth, Megan

2016-01-01

The current study investigated whether the amount of autistic traits shown by an individual is associated with viewing behaviour during a face-to-face interaction. The eye movements of 36 neurotypical university students were recorded using a mobile eye-tracking device. High amounts of autistic traits were neither associated with reduced looking to the social partner overall, nor with reduced looking to the face. However, individuals who were high in autistic traits exhibited reduced visual exploration during the face-to-face interaction overall, as demonstrated by shorter and less frequent saccades. Visual exploration was not related to social anxiety. This study suggests that there are systematic individual differences in visual exploration during social interactions and these are related to amount of autistic traits.

From Narcissism to Face Work: Two Views on the Self in Social Interaction.

PubMed

Peräkylä, Anssi

2015-09-01

Through the analysis of conversational interaction and clinical notes, this article develops conceptual linkages between the Goffmanian concept of face and the psychoanalytic and psychiatric understandings of narcissism. Self-cathexis--the investment of libidinal emotion to the image of self--is a key issue both for Goffman and in psychoanalytic studies of narcissism. For Goffman, the self and its cathexis are inherently fragile interactional achievements, whereas for psychoanalysts such as Kernberg and Kohut, they are relatively stable intrapsychic structures. An application of Goffman's theory to narcissistic personality disorders suggests that pathological narcissism involves the isolation of the person's self-image from interactional. practices and a consequent inability to benefit from face work in ordinary social encounters. Clinical experience suggests revisions to the theory of face work: there is a biographical continuity in a person's experience of face, and successful participation in face work is made possible by the psychic capacity of playful orientation to one's own and others' narcissistic illusions. Such playful orientation is manifested through the interactional practices of role distancing.

Underwater Facilities and Inspections and Assessments at Naval Air Station, Pensacola, Florida.

DTIC Science & Technology

1983-01-01

hairline crack at 4-43 pile cap (vertical face) bent 34 27 Pier, 303 - Spalled concrete and exposed rebar 4-44 in pile cap bent 38 28 Pier 303 - Typical...of steel sheet pile 4-53 3’ below concrete encasement at station 83+25 37 Pier 303 - Exposed rebar and spall in concrete 4-54 encasement at station 83... corrosion and concrete deterioration due to exposure to the elements. 3.3 Inspection Equipment The following equipment was employed by diving engineers

Cockrell washs hair and face

NASA Image and Video Library

1996-12-16

STS080-312-004 (19 Nov.-7 Dec. 1996) --- Astronaut Kenneth D. Cockrell, STS-80 mission commander, washes his hair on the middeck of the Earth-orbiting space shuttle Columbia. Displaying a sense of humor, the commander asked astronaut Story Musgrave, who is bald, to address this visual during a briefing with Johnson Space Center (JSC) employees on Jan. 14, 1997. Equal to the task, Musgrave cracked a number of bald jokes and remarked that it was much easier to polish a head in zero gravity than to wash one.

Ground Runup Noise Suppression Program. Part 3. Dry Suppressor Technology Base.

DTIC Science & Technology

1982-06-20

ref 7) used mineral wool to fill the bays. A facing of corrugated metal liner supports the mineral wool . During operation two types of problems...1978 52 tube. The hot jet velocity exhaust flow shifted/decinerated the mineral wool and caused the metal liner to crack/break off. Programs were...PREDICTED) 0 MINERAL WOOL FIBROUS LINER 315 630 1250 2500 5000 10000 20000 1/15 SCALE FREQUENCY Figure 2-30. Noise attenuation of liners in augmenter. K

Application of Extra Virgin Olive Oil to Prevent Nipple Cracking in Lactating Women.

PubMed

Cordero, María José Aguilar; Villar, Norma Mur; Barrilao, Rafael Guisado; Cortés, Manuel Eduardo Cortés; López, Antonio Manuel Sánchez

2015-12-01

It is well established that extra virgin olive oil (EVOO), applied to the skin, has healing and anti-inflammatory properties. To evaluate the effectiveness of EVOO in the prevention of nipple cracking in lactating women. Experimental, prospective, randomized study of 300 lactating women, admitted to the postpartum unit of the city's general hospital (Cienfuegos, Cuba). The study was carried out in 2012. Eligible patients were randomized into two groups of 150 women. In Group 1, EVOO was applied on the nipple after feeding, and in Group 2, drops of breast milk were applied to the nipple after feeding. Clinical evaluations were made during the first week of treatment and after the first month. All women who initiated breastfeeding were considered eligible to be included in this study; breastfeeding was characterized as the moment of mother-child interaction with suction on the nipple. Efficacy was evaluated quantitatively, as the absence of cracks in the nipple during the first 2 weeks of lactation using as the proportion of women with or without nipple cracks, and if present, whether they were moderate or slight. The quantitative efficacy was 97.3% and no adverse effects occurred in mothers and newborns during the administration of EVOO. EVOO helps prevent nipple cracking in lactating women. It has been shown to have protective effects when breastfeeding presents technical difficulties. This conclusion is borne out by the frequency distribution results obtained, which reflect a significantly higher proportion of nipple cracking in the population that was not treated with EVOO. Use EVOO to prevent nipple cracking during breastfeeding by administering 3 drops on each nipple after each feeding. Decreased nipple cracking will reduce pain and enhance breastfeedinging by administering 3 drops on each nipple after each feeding, improving the health of mothers and infants. © 2015 Sigma Theta Tau International.

Enhanced Diffusion of Chlorinated Organic Compounds into Aquitards due to Cracking

NASA Astrophysics Data System (ADS)

Ayral, D.; Otero, M.; Chung, S.; Goltz, M. N.; Huang, J.; Demond, A. H.

2012-12-01

Despite great efforts, remediation of sites contaminated with dense non-aqueous phase liquids (DNAPLs) is very challenging because, even at residual saturations, DNAPLs can act as a long-term source for a dissolved phase contaminant plume. Current models consider the possibility of diffusion and storage of these compounds in unfractured low permeability layers. However, there is a need to consider the impact of cracks, whether naturally occurring or induced by the interaction between low permeable layers and DNAPLs. To evaluate the impact on diffusive fluxes, diffusion coefficients were measured in low permeability materials representative of aquitards at steady-state using the time-lag method. The experimental setup comprised silty soil, packed into a retaining ring, sandwiched in between two reservoirs. The analytical solution for the time-lag method requires constant conditions in the upper and lower reservoirs. The lower reservoir contained pure trichloroethylene (TCE), while the upper reservoir was maintained at a concentration of zero by bubbling air through it, sweeping TCE into toluene trap. In order to predict the flux, the experimental effective diffusion coefficients were used to calculate the flux through uncracked matrix whereas bulk diffusion coefficient was used to calculate flux through the cracks. By using the experimentally-obtained diffusion coefficients and experimentally-measured crack intensity factors (the ratio of the area of cracks to the uncracked area), the total flux was estimated over extended time periods. These calculations, based on experimental data, were used to evaluate if diffusive-based fluxes in the presence of cracks were significantly greater than in the case of diffusion into an uncracked matrix. The enhanced diffusive fluxes were evaluated to determine whether there is the potential for significantly greater storage in the low permeable layers in the case of cracks, or whether the possibility of advective fluxes into the cracks needs to be considered as well.

Pair Interactions and Mode of Communication: Comparing Face-to-Face and Computer Mediated Communication

ERIC Educational Resources Information Center

Tan, Lan Liana; Wigglesworth, Gillian; Storch, Neomy

2010-01-01

In today's second language classrooms, students are often asked to work in pairs or small groups. Such collaboration can take place face-to-face, but now more often via computer mediated communication. This paper reports on a study which investigated the effect of the medium of communication on the nature of pair interaction. The study involved…

The Nature of Negotiations in Face-to-Face versus Computer-Mediated Communication in Pair Interactions

ERIC Educational Resources Information Center

Rouhshad, Amir; Wigglesworth, Gillian; Storch, Neomy

2016-01-01

The Interaction Approach argues that negotiation for meaning and form is conducive to second language development. To date, most of the research on negotiations has been either in face-to-face (FTF) or text-based synchronous computer-mediated communication (SCMC) modes. Very few studies have compared the nature of negotiations across the modes.…

A Systems View of Mother-Infant Face-to-Face Communication

ERIC Educational Resources Information Center

Beebe, Beatrice; Messinger, Daniel; Bahrick, Lorraine E.; Margolis, Amy; Buck, Karen A.; Chen, Henian

2016-01-01

Principles of a dynamic, dyadic systems view of mother-infant face-to-face communication, which considers self- and interactive processes in relation to one another, were tested. The process of interaction across time in a large low-risk community sample at infant age 4 months was examined. Split-screen videotape was coded on a 1-s time base for…

Analyzing Interactions by an IIS-Map-Based Method in Face-to-Face Collaborative Learning: An Empirical Study

ERIC Educational Resources Information Center

Zheng, Lanqin; Yang, Kaicheng; Huang, Ronghuai

2012-01-01

This study proposes a new method named the IIS-map-based method for analyzing interactions in face-to-face collaborative learning settings. This analysis method is conducted in three steps: firstly, drawing an initial IIS-map according to collaborative tasks; secondly, coding and segmenting information flows into information items of IIS; thirdly,…

Double Cantilever Beam and End Notched Flexure Fracture Toughness Testing of Two Composite Materials

NASA Technical Reports Server (NTRS)

Kessler, Jeff A.; Adams, Donald F.

1993-01-01

Two different unidirectional composite materials were provided by NASA Langley Research Center and tested by the Composite Materials Research Group within the Department of Mechanical Engineering at the University of Wyoming. Double cantilever beam and end notched flexure tests were performed to measure the mode I (crack opening) and mode II (sliding or shear) interlaminar fracture toughness of the two materials. The two composites consisted of IM7 carbon fiber combined with either RP46 resin toughened with special formulation of LaRC IA resin, known as JJS1356; or PES chain extended thermoplastic resin known as JJS1361. Double Cantilever Beam Specimen Configuration and Test Methods As received from NASA, the test specimens were nominally 0.5 inch wide, 6 inches long, and 0.2 inch thick. A 1 inch long Kapton insert at the midplane of one end of the specimen (placed during laminate fabrication) facilitated crack initiation and extension. It was noted that the specimens provided were smaller than the nominal 1.5 inch wide, 9.0 inch long configuration specified. Similarly, the Kapton inserts were of greater length than those in the present specimens. Hence, the data below should not be compared directly to those generated with the referenced methods. No preconditioning was performed on the specimens prior to testing. In general, the methodology was used for the present work. Crack opening loads were introduced to the specimens via piano hinges attached to the main specimen faces at a single end of each specimen. Hinges were bolted to the specimens using the technique presented. The cracks were extended a small distance from the end of the Kapton insert prior to testing. Just before precracking, the sides of the specimens were coated with water-soluble typewriter correction fluid to aid in crack visualization. Scribe marks were then made in the coating at half-inch intervals.

Social and emotional relevance in face processing: happy faces of future interaction partners enhance the late positive potential

PubMed Central

Bublatzky, Florian; Gerdes, Antje B. M.; White, Andrew J.; Riemer, Martin; Alpers, Georg W.

2014-01-01

Human face perception is modulated by both emotional valence and social relevance, but their interaction has rarely been examined. Event-related brain potentials (ERP) to happy, neutral, and angry facial expressions with different degrees of social relevance were recorded. To implement a social anticipation task, relevance was manipulated by presenting faces of two specific actors as future interaction partners (socially relevant), whereas two other face actors remained non-relevant. In a further control task all stimuli were presented without specific relevance instructions (passive viewing). Face stimuli of four actors (2 women, from the KDEF) were randomly presented for 1s to 26 participants (16 female). Results showed an augmented N170, early posterior negativity (EPN), and late positive potential (LPP) for emotional in contrast to neutral facial expressions. Of particular interest, face processing varied as a function of experimental tasks. Whereas task effects were observed for P1 and EPN regardless of instructed relevance, LPP amplitudes were modulated by emotional facial expression and relevance manipulation. The LPP was specifically enhanced for happy facial expressions of the anticipated future interaction partners. This underscores that social relevance can impact face processing already at an early stage of visual processing. These findings are discussed within the framework of motivated attention and face processing theories. PMID:25076881

Microcracking in composite laminates under thermal and mechanical loading. Thesis

NASA Technical Reports Server (NTRS)

Maddocks, Jason R.

1995-01-01

Composites used in space structures are exposed to both extremes in temperature and applied mechanical loads. Cracks in the matrix form, changing the laminate thermoelastic properties. The goal of the present investigation is to develop a predictive methodology to quantify microcracking in general composite laminates under both thermal and mechanical loading. This objective is successfully met through a combination of analytical modeling and experimental investigation. In the analysis, the stress and displacement distributions in the vicinity of a crack are determined using a shear lag model. These are incorporated into an energy based cracking criterion to determine the favorability of crack formation. A progressive damage algorithm allows the inclusion of material softening effects and temperature-dependent material properties. The analysis is implemented by a computer code which gives predicted crack density and degraded laminate properties as functions of any thermomechanical load history. Extensive experimentation provides verification of the analysis. AS4/3501-6 graphite/epoxy laminates are manufactured with three different layups to investigate ply thickness and orientation effects. Thermal specimens are cooled to progressively lower temperatures down to -184 C. After conditioning the specimens to each temperature, cracks are counted on their edges using optical microscopy and in their interiors by sanding to incremental depths. Tensile coupons are loaded monotonically to progressively higher loads until failure. Cracks are counted on the coupon edges after each loading. A data fit to all available results provides input parameters for the analysis and shows them to be material properties, independent of geometry and loading. Correlation between experiment and analysis is generally very good under both thermal and mechanical loading, showing the methodology to be a powerful, unified tool. Delayed crack initiation observed in a few cases is attributed to a lack of preexisting flaws assumed by the analysis. Some interactions between adjacent ply groups are attributed to local stress concentrations. These two effects are not captured by the analysis due to its global nature. The analysis is conservative in these cases and agrees well with data after the observed onset of cracking.

A study of spectrum fatigue crack propagation in two aluminum alloys. 1: Spectrum simplification

NASA Technical Reports Server (NTRS)

Telesman, J.; Antolovich, S. D.

1985-01-01

The fatigue crack propagation behavior of two commercial Al alloys was studied using spectrum loading conditions characteristics of those encountered at critical locations in high performance fighter aircraft. A tension dominated (TD) and tension compression (TC) spectrum were employed for each alloy. Using a mechanics-based analysis, it was suggested that negative loads could be eliminated for the TC spectrum for low to intermediate maximum stress intensities. The suggestion was verified by subsequent testing. Using fractographic evidence, it was suggested that a further similification in the spectra could be accomplished by eliminating low and intermediate peak load points resulting in near or below threshold maximum peak stress intensity values. It is concluded that load interactions become more important at higher stress intensities and more plasticity at the crack tip. These results suggest that a combined mechanics/fractographic mechanisms approach can be used to simplify other complex spectra.

Low-Cycle Fatigue Properties of P92 Ferritic-Martensitic Steel at Elevated Temperature

NASA Astrophysics Data System (ADS)

Zhang, Zhen; Hu, ZhengFei; Schmauder, Siegfried; Mlikota, Marijo; Fan, KangLe

2016-04-01

The low-cycle fatigue behavior of P92 ferritic-martensitic steel and the corresponding microstructure evolution at 873 K has been extensively studied. The test results of fatigue lifetime are consistent with the Coffin-Manson relationship over a range of controlled total strain amplitudes from 0.15 to 0.6%. The influence of strain amplitude on the fatigue crack initiation and growth has been observed using optical microscopy and scanning electron microscopy. The formation mechanism of secondary cracks is established according to the observation of fracture after fatigue process and there is an intrinsic relationship between striation spacing, current crack length, and strain amplitude. Transmission electron microscopy has been employed to investigate the microstructure evolution after fatigue process. It indicates the interaction between carbides and dislocations together with the formation of cell structure inhibits the cyclic softening. The low-angle sub-boundary elimination in the martensite is mainly caused by the cyclic stress.

Interpersonal brain synchronization in the right temporo-parietal junction during face-to-face economic exchange.

PubMed

Tang, Honghong; Mai, Xiaoqin; Wang, Shun; Zhu, Chaozhe; Krueger, Frank; Liu, Chao

2016-01-01

In daily life, interpersonal interactions are influenced by uncertainty about other people's intentions. Face-to-face (FF) interaction reduces such uncertainty by providing external visible cues such as facial expression or body gestures and facilitates shared intentionality to promote belief of cooperative decisions and actual cooperative behaviors in interaction. However, so far little is known about interpersonal brain synchronization between two people engaged in naturally occurring FF interactions. In this study, we combined an adapted ultimatum game with functional near-infrared spectroscopy (fNIRS) hyperscanning to investigate how FF interaction impacts interpersonal brain synchronization during economic exchange. Pairs of strangers interacted repeatedly either FF or face-blocked (FB), while their activation was simultaneously measured in the right temporo-parietal junction (rTPJ) and the control region, right dorsolateral prefrontal cortex (rDLPFC). Behaviorally, FF interactions increased shared intentionality between strangers, leading more positive belief of cooperative decisions and more actual gains in the game. FNIRS results indicated increased interpersonal brain synchronizations during FF interactions in rTPJ (but not in rDLPFC) with greater shared intentionality between partners. These results highlighted the importance of rTPJ in collaborative social interactions during FF economic exchange and warrant future research that combines FF interactions with fNIRS hyperscanning to study social brain disorders such as autism. © The Author (2015). Published by Oxford University Press. For Permissions, please email: journals.permissions@oup.com.

Interactions between facial emotion and identity in face processing: evidence based on redundancy gains.

PubMed

Yankouskaya, Alla; Booth, David A; Humphreys, Glyn

2012-11-01

Interactions between the processing of emotion expression and form-based information from faces (facial identity) were investigated using the redundant-target paradigm, in which we specifically tested whether identity and emotional expression are integrated in a superadditive manner (Miller, Cognitive Psychology 14:247-279, 1982). In Experiments 1 and 2, participants performed emotion and face identity judgments on faces with sad or angry emotional expressions. Responses to redundant targets were faster than responses to either single target when a universal emotion was conveyed, and performance violated the predictions from a model assuming independent processing of emotion and face identity. Experiment 4 showed that these effects were not modulated by varying interstimulus and nontarget contingencies, and Experiment 5 demonstrated that the redundancy gains were eliminated when faces were inverted. Taken together, these results suggest that the identification of emotion and facial identity interact in face processing.

Interactive multimedia consent for biobanking: a randomized trial.

PubMed

Simon, Christian M; Klein, David W; Schartz, Helen A

2016-01-01

The potential of interactive multimedia to improve biobank informed consent has yet to be investigated. The aim of this study was to test the separate effectiveness of interactivity and multimedia at improving participant understanding and confidence in understanding of informed consent compared with a standard, face-to-face (F2F) biobank consent process. A 2 (face-to-face versus multimedia) × 2 (standard versus enhanced interactivity) experimental design was used with 200 patients randomly assigned to receive informed consent. All patients received the same information provided in the biobank's nine-page consent document. Interactivity (F(1,196) = 7.56, P = 0.007, partial η(2) = 0.037) and media (F(1,196) = 4.27, P = 0.04, partial η(2) = 0.021) independently improved participants' understanding of the biobank consent. Interactivity (F(1,196) = 6.793, P = 0.01, partial η(2) = 0.033), but not media (F(1,196) = 0.455, not significant), resulted in increased participant confidence in their understanding of the biobank's consent materials. Patients took more time to complete the multimedia condition (mean = 18.2 min) than the face-to-face condition (mean = 12.6 min). This study demonstrated that interactivity and multimedia each can be effective at promoting an individual's understanding and confidence in their understanding of a biobank consent, albeit with additional time investment. Researchers should not assume that multimedia is inherently interactive, but rather should separate the two constructs when studying electronic consent.

Impact of Face-to-Face Interaction in Meeting Needs of Adult Students Enrolled in Web-Based Nursing Courses

ERIC Educational Resources Information Center

Murabito, Sandra Womeldorf

2013-01-01

The purpose of this dissertation is to study the impact of student to faculty face-to-face interaction in meeting the needs of adult students enrolled in web-based nursing courses. The study compared adult and traditional nursing students enrolled in online courses. A non-equivalent control group research design was utilized to compare students…

Reciprocal Altruism: The Effect of Self-Esteem and Anticipation of Face-to-Face Interaction on Reciprocation.

ERIC Educational Resources Information Center

Gregor, Gary L.; Conner, Hubert

The study attempts to measure the effects of self-esteem and face-to-face interaction on a person's giving behavior (altruism). Seventy-two introductory psychology students were paired on a task which required that one of each pair become "indebted" to the other. Their roles were then reversed, and data was collected to see if the…

Marketing Learning Communities to Generation Z: The Importance of Face-to-Face Interaction in a Digitally Driven World

ERIC Educational Resources Information Center

Spears, Julia; Zobac, Stephanie R.; Spillane, Allison; Thomas, Shannon

2015-01-01

This article aims to identify the marketing strategies utilized by Learning Community (LC) administrators at two large, public, four-year research universities in the Midwest. The use of digital media coupled with face-to-face interaction is identified as an effective method of marketing LCs to the newest population of incoming college students,…

A Pilot Randomized Clinical Trial of Two Medication Adherence and Drug Use Interventions For HIV+ Crack Cocaine Users*

PubMed Central

Ingersoll, Karen S.; Farrell-Carnahan, Leah; Cohen-Filipic, Jessye; Heckman, Carolyn J.; Ceperich, Sherry D.; Hettema, Jennifer; Marzani-Nissen, Gabrielle

2011-01-01

Background Crack cocaine use undermines adherence to highly active antiretroviral therapy (HAART). This pilot randomized clinical trial tested the feasibility and efficacy of 2 interventions based on the Information-Motivation-Behavioral Skills model to improve HAART adherence and reduce crack cocaine problems. Methods Participants were 54 adults with crack cocaine use and HIV with <90% HAART adherence. Most participants were African-American (82%) heterosexual (59%), and crack cocaine dependent (92%). Average adherence was 58% in the past 2 weeks. Average viral loads (VL) were detectable (log VL 2.97). The interventions included 6 sessions of Motivational Interviewing plus feedback and skills building (MI+), or Video information plus debriefing (Video+) over 8 weeks. Primary outcomes were adherence by 14-day timeline follow-back and Addiction Severity Index (ASI) Drug Composite Scores at 3 and 6 months. Repeated measures ANOVA assessed main effects of the interventions and interactions by condition. Results Significant increases in adherence and reductions in ASI Drug Composite Scores occurred in both conditions by 3 months and were maintained at 6 months, representing medium effect sizes. No between group differences were observed. No VL changes were observed in either group. Treatment credibility, retention, and satisfaction were high and not different by condition. Conclusions A counseling and a video intervention both improved adherence and drug problems durably among people with crack cocaine use and poor adherence in this pilot study. The interventions should be tested further among drug users with poor adherence. Video interventions may be feasible and scalable for people with HIV and drug use. PMID:21306837

Effects of spatial heterogeneity and material anisotropy on the fracture pattern and macroscopic effective toughness of Mancos Shale in Brazilian tests

NASA Astrophysics Data System (ADS)

Na, SeonHong; Sun, WaiChing; Ingraham, Mathew D.; Yoon, Hongkyu

2017-08-01

For assessing energy-related activities in the subsurface, it is important to investigate the impact of the spatial variability and anisotropy on the geomechanical behavior of shale. The Brazilian test, an indirect tensile-splitting method, is performed in this work, and the evolution of strain field is obtained using digital image correlation. Experimental results show the significant impact of local heterogeneity and lamination on the crack pattern characteristics. For numerical simulations, a phase field method is used to simulate the brittle fracture behavior under various Brazilian test conditions. In this study, shale is assumed to consist of two constituents including the stiff and soft layers to which the same toughness but different elastic moduli are assigned. Microstructural heterogeneity is simplified to represent mesoscale (e.g., millimeter scale) features such as layer orientation, thickness, volume fraction, and defects. The effect of these structural attributes on the onset, propagation, and coalescence of cracks is explored. The simulation results show that spatial heterogeneity and material anisotropy highly affect crack patterns and effective fracture toughness, and the elastic contrast of two constituents significantly alters the effective toughness. However, the complex crack patterns observed in the experiments cannot completely be accounted for by either an isotropic or transversely isotropic effective medium approach. This implies that cracks developed in the layered system may coalesce in complicated ways depending on the local heterogeneity, and the interaction mechanisms between the cracks using two-constituent systems may explain the wide range of effective toughness of shale reported in the literature.

Effects of spatial heterogeneity and material anisotropy on the fracture pattern and macroscopic effective toughness of Mancos Shale in Brazilian tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

Na, SeonHong; Sun, WaiChing; Ingraham, Mathew D.

For assessing energy-related activities in the subsurface, it is important to investigate the impact of the spatial variability and anisotropy on the geomechanical behavior of shale. The Brazilian test, an indirect tensile-splitting method, is performed in this work, and the evolution of strain field is obtained using digital image correlation. Experimental results show the significant impact of local heterogeneity and lamination on the crack pattern characteristics. For numerical simulations, a phase field method is used to simulate the brittle fracture behavior under various Brazilian test conditions. In this study, shale is assumed to consist of two constituents including the stiffmore » and soft layers to which the same toughness but different elastic moduli are assigned. Microstructural heterogeneity is simplified to represent mesoscale (e.g., millimeter scale) features such as layer orientation, thickness, volume fraction, and defects. The effect of these structural attributes on the onset, propagation, and coalescence of cracks is explored. The simulation results show that spatial heterogeneity and material anisotropy highly affect crack patterns and effective fracture toughness, and the elastic contrast of two constituents significantly alters the effective toughness. However, the complex crack patterns observed in the experiments cannot completely be accounted for by either an isotropic or transversely isotropic effective medium approach. In conclusion, this implies that cracks developed in the layered system may coalesce in complicated ways depending on the local heterogeneity, and the interaction mechanisms between the cracks using two-constituent systems may explain the wide range of effective toughness of shale reported in the literature.« less

Effects of spatial heterogeneity and material anisotropy on the fracture pattern and macroscopic effective toughness of Mancos Shale in Brazilian tests

DOE PAGES

Na, SeonHong; Sun, WaiChing; Ingraham, Mathew D.; ...

2017-07-31

For assessing energy-related activities in the subsurface, it is important to investigate the impact of the spatial variability and anisotropy on the geomechanical behavior of shale. The Brazilian test, an indirect tensile-splitting method, is performed in this work, and the evolution of strain field is obtained using digital image correlation. Experimental results show the significant impact of local heterogeneity and lamination on the crack pattern characteristics. For numerical simulations, a phase field method is used to simulate the brittle fracture behavior under various Brazilian test conditions. In this study, shale is assumed to consist of two constituents including the stiffmore » and soft layers to which the same toughness but different elastic moduli are assigned. Microstructural heterogeneity is simplified to represent mesoscale (e.g., millimeter scale) features such as layer orientation, thickness, volume fraction, and defects. The effect of these structural attributes on the onset, propagation, and coalescence of cracks is explored. The simulation results show that spatial heterogeneity and material anisotropy highly affect crack patterns and effective fracture toughness, and the elastic contrast of two constituents significantly alters the effective toughness. However, the complex crack patterns observed in the experiments cannot completely be accounted for by either an isotropic or transversely isotropic effective medium approach. In conclusion, this implies that cracks developed in the layered system may coalesce in complicated ways depending on the local heterogeneity, and the interaction mechanisms between the cracks using two-constituent systems may explain the wide range of effective toughness of shale reported in the literature.« less

Double torsion fracture mechanics testing of shales under chemically reactive conditions

NASA Astrophysics Data System (ADS)

Chen, X.; Callahan, O. A.; Holder, J. T.; Olson, J. E.; Eichhubl, P.

2015-12-01

Fracture properties of shales is vital for applications such as shale and tight gas development, and seal performance of carbon storage reservoirs. We analyze the fracture behavior from samples of Marcellus, Woodford, and Mancos shales using double-torsion (DT) load relaxation fracture tests. The DT test allows the determination of mode-I fracture toughness (KIC), subcritical crack growth index (SCI), and the stress-intensity factor vs crack velocity (K-V) curves. Samples are tested at ambient air and aqueous conditions with variable ionic concentrations of NaCl and CaCl2, and temperatures up to 70 to determine the effects of chemical/environmental conditions on fracture. Under ambient air condition, KIC determined from DT tests is 1.51±0.32, 0.85±0.25, 1.08±0.17 MPam1/2 for Marcellus, Woodford, and Mancos shales, respectively. Tests under water showed considerable change of KIC compared to ambient condition, with 10.6% increase for Marcellus, 36.5% decrease for Woodford, and 6.7% decrease for Mancos shales. SCI under ambient air condition is between 56 and 80 for the shales tested. The presence of water results in a significant reduction of the SCI from 70% to 85% compared to air condition. Tests under chemically reactive solutions are currently being performed with temperature control. K-V curves under ambient air conditions are linear with stable SCI throughout the load-relaxation period. However, tests conducted under water result in an initial cracking period with SCI values comparable to ambient air tests, which then gradually transition into stable but significantly lower SCI values of 10-20. The non-linear K-V curves reveal that crack propagation in shales is initially limited by the transport of chemical agents due to their low permeability. Only after the initial cracking do interactions at the crack tip lead to cracking controlled by faster stress corrosion reactions. The decrease of SCI in water indicates higher crack propagation velocity due to faster stress corrosion rate in water than in ambient air. The experimental results are applicable for the prediction of fracture initiation based on KIC, modeling fracture pattern based on SCI, and the estimation of dynamic fracture propagation such as crack growth velocity and crack re-initiation.

Analytical and experimental investigation of rubbing interaction in labyrinth seals for a liquid hydrogen fuel pump. [space shuttle main engine

NASA Technical Reports Server (NTRS)

Dolan, F. X.; Kennedy, F. E.; Schulson, E. M.

1984-01-01

Cracking of the titanium knife edges on the labyrinth seals of the liquid hydrogen fuel pump in the Space Shuttle main engine is considered. Finite element analysis of the thermal response of the knife edge in sliding contact with the wear ring surface shows that interfacial temperatures can be quite high and they are significantly influenced by the thermal conductivity of the surfaces in rubbing contact. Thermal shock experiments on a test specimen similar to the knife edge geometry demonstrate that cracking of the titanium alloy is possible in a situation involving repeated thermal cycles over a wide temperature range, as might be realized during a rub in the liquid hydrogen fuel pump. High-speed rub interaction tests were conducted using a representative knife edge and seal geometry over a broad range of interaction rates and alternate materials were experimentally evaluated. Plasma-sprayed aluminum-graphite was found to be significantly better than presently used aluminum alloy seals from the standpoint of rub performance. Ion nitriding the titanium alloy knife-edges also improved rub performance compared to the untreated baseline.

An experimental investigation of rubbing interaction in labyrinth seals at cryogenic temperature

NASA Technical Reports Server (NTRS)

Dolan, F. X.; Kennedy, F. E.; Schulson, E. M.

1985-01-01

An experimental program was carried out to address issues related to the observed cracking of the titanium knife edges on the labyrinth seals of the high pressure fuel pump (HPFP) in the Space Shuttle main engine (SSME). Thermal shock experiments were carried out using a jet specimen with geometry similar to the knife edge geometry. These tests demonstrate that cracking of the titanium alloy is possible in a situation involving repeated thermal cycles over a wide temperature range, as might be realized during a rub in the liquid hydrogen fuel pump. High speed rub interaction tests were conducted using a representative knife edge and seal geometry over a broad range of interaction rates. Alternative materials were also experimentally evaluated. These tests provide information which can be used to design improved labyrinth seals for the HPFP of the SSME. In particular, plasma-sprayed aluminum-graphite was found to be significantly better than aluminum alloy seals used at present from the standpoint of rub performance. Ion nitriding of the titanium alloy knife edges was also found to improve rub performance compared with the untreated baseline knife edge material.

Self-healing of low-velocity impact damage in glass fabric/epoxy composites using an epoxy-mercaptan healing agent

NASA Astrophysics Data System (ADS)

Chao Yuan, Yan; Ye, Yueping; Zhi Rong, Min; Chen, Haibin; Wu, Jingshen; Qiu Zhang, Ming; Qin, Shi Xiang; Yang, Gui Cheng

2011-01-01

Self-healing woven glass fabric-reinforced epoxy composite laminates were made by embedding epoxy- and mercaptan-loaded microcapsules. After being subjected to low-velocity impact, the laminates were able to heal the damage in an autonomic way at room temperature. The healing-induced reduction in the damaged areas was visualized using a scanning acoustic microscope. The rate of damage area reduction, which is closely related to the effect of crack rehabilitation and mechanical recovery, is a function of impact energy, content and size of the healing microcapsules. Minor damage, such as microcracks in the matrix, can be completely repaired by the healing system without manual intervention, including external pressure. Microcapsules with larger size and/or higher concentration are propitious for delivering more healing agent to cracked portions, while imposition of lateral pressure on damaged specimens forces the separated faces to approach each other. Both can improve the rate of damage area reduction in the case of severe damage.

Asymmetric crack propagation near waterfall cliff and its influence on the waterfall lip shape

NASA Astrophysics Data System (ADS)

Vastola, G.

2011-11-01

By means of Finite Element Method (FEM) calculations and fatigue fracture mechanics analysis, we show that crack propagation in bedrocks close to the waterfall cliff is preferential towards the cliff face rather than upstream the river. Based on this effect, we derive the corresponding expression for the velocity of recession vr of the waterfall lip, and find that vr has a quadratic dependence on the hydrostatic pressure. Quantitatively, this erosion mechanism generates recession rates of the order of ~cm-dm/y, consistent with the recession rates of well-known waterfalls. We enclose our expression for vr into a growth model to investigate the time evolution of a waterfall lip subject to this erosional mechanism. Because of the dependence on hydrostatic pressure, the shape of the waterfall is influenced by the transverse profile of the river that generates the waterfall. If the river has a transverse concavity, the waterfall evolves a curved shape. Evolution for the case of meanders with asymmetric transverse profile is also given.

Online Social Interactions Predict Academic and Emotional Adjustment in the Transition to University.

PubMed

Mikami, Amori Yee; Szwedo, David E; Khalis, Adri; Jia, Mary; Na, Jennifer Jiwon

2018-02-05

We investigated the developmental implications of online social interactions among 590 youth transitioning to university. We observed friends' posts on participants' Facebook pages, and considered attributes of friends' posts used to indicate positive and negative relationship quality in face-to-face interactions. After statistical control of beginning-of-year functioning and participants' Facebook content, Facebook friends' deviant content posts (swearing; illegal/sexualized activities) predicted participants' lower grade point average, Facebook friends' posts indicating connection to participants predicted participants' lower psychopathology, and Facebook friends' verbal aggression posts predicted participants' lower institutional attachment, by the end of the year. Negative effects of friends' posts were strongest for participants who were disliked by peers face to face. The online context may uniquely influence youth adjustment in conjunction with face-to-face relationships. © 2018 Society for Research on Adolescence.

Evaluation of asphalt pavement interface conditions for enhanced bond performance : [summary].

DOT National Transportation Integrated Search

2017-05-01

In this project, University of Florida researchers conducted a comprehensive program of modeling to understand interface debonding and near-surface longitudinal cracking in the wheel path of asphalt pavements. : To understand the interaction of debon...

Dynamic assessment of bridge deck performance considering realistic bridge-traffic interaction

DOT National Transportation Integrated Search

2017-09-01

Concrete bridge decks are directly exposed to daily traffic loads and may experience some surface cracking caused by excessive stress or fatigue accumulation, which requires repair or replacement. Among typical bridges in North America, bridge decks ...

A literature review on fatigue and creep interaction

NASA Technical Reports Server (NTRS)

Chen, W. C.

1978-01-01

Life-time prediction methods, which are based on a number of empirical and phenomenological relationships, are presented. Three aspects are reviewed: effects of testing parameters on high temperature fatigue, life-time prediction, and high temperature fatigue crack growth.

THE EFFECTS OF CRACKING ON THE SURFACE POTENTIAL OF ICY GRAINS IN SATURN’S E-RING: LABORATORY STUDIES

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bu, Caixia; Bahr, David A.; Dukes, Catherine A.

2016-07-10

Within Saturn's E-ring, dust grains are coated by water vapor co-released with ice grains from the geyser-like eruptions of Enceladus. These ice-coated grains have intrinsic surface potential and interact synergistically with the ions and electrons of Saturn's magnetospheric plasmas. We perform laboratory experiments to investigate the effects of water-ice growth on the surface potential, using amorphous solid water (ASW) films. We estimate the growth of the surface potential to be ∼ 2.5 mV (Earth) yr{sup 1} and 112 mV yr{sup 1} for E-ring grains at ∼4.5 R {sub s} and 3.95 R {sub s} outside Enceladus’s plume, respectively. In addition,more » our measurements show that the linear relationship between the surface potential and the film thickness, as described in previous studies, has an upper limit, where the film spontaneously cracks above a porosity-dependent critical thickness. Heating of the cracked films with (and without) deposited charge shows that significant positive (and negative) surface potentials are retained at temperatures above 110 K, contrary to the minimal values (roughly zero) for thin, transparent ASW films. The significant surface potentials observed on micron-scale cracked ice films after thermal cycling, (5–20) V, are consistent with Cassini measurements, which indicate a negative charge of up to 5 V for E-ring dust particles at ∼5 R {sub s}. Therefore, the native grain surface potential resulting from water-vapor coating must be included in modeling studies of interactions between E-ring icy surfaces and Saturn's magnetospheric plasma.« less

Finite Element Simulation of Solid Rocket Booster Separation Motors During Motor Firing

NASA Technical Reports Server (NTRS)

Yu. Weiping; Crane, Debora J.

2007-01-01

One of the toughest challenges facing Solid Rocket Booster (SRB) engineers is to ensure that any design changes made to the Shuttle-Derived Booster Separation Motors (BSM) for future space exploration vehicles is able to withstand the increasingly hostile motor firing environment without cracking its critical component - the graphite throat. This paper presents a critical analysis methodology and techniques for assessing effects of BSM design changes with great accuracy and precision. For current Space Shuttle operation, the motor firing occurs at SRB separation - approximately 125 seconds after Shuttle launch at an altitude of about 28 miles. The motor operation event lasts about two seconds, however, the surface temperature of the graphite throat increases approximately 3400 F in less than one second with a corresponding increase in surface pressure of approximately 2200 pounds per square inch (psi) in less than one-tenth of a second. To capture this process fully and accurately, a two-phase sequentially coupled thermal-mechanical finite element approach was developed. This method allows the time- and location-dependent pressure fields to interact with the spatial-temporal thermal fields throughout the operation. The material properties of graphite throat are orthotropic and temperature-dependent. The analysis involves preload and multiple body contacts.

Measurement and modeling of temperature-dependent hydrogen embrittlement of chromium-molybdenum steel to enable fitness-for-service life prediction

NASA Astrophysics Data System (ADS)

Al-Rumaih, Abdullah M.

Thick-wall vessels in petrochemical applications, fabricated from 2.25Cr-1Mo steel, operate in pressurized H2 at elevated temperature for more than 20 years. There is a concern regarding the interactive effects of temper-embrittlement and hydrogen-embrittlement on fitness-for-service during startup/shutdown near ambient temperatures. The database of degraded material properties is inadequate to enable accurate assessment. Specifically, H loss from small fracture mechanics specimens was substantial during either long-term or elevated temperature experiments. In addition, the influence of temperature on H-embrittlement of Cr-Mo steel is not fundamentally understood. The objectives of this research are to (1) design a novel laboratory method to retain H in small fracture mechanics specimens, (2) characterize the temperature dependent internal hydrogen embrittlement (IHE) of Cr-Mo weld metal using the developed method, and (3) model H distribution near a stressed crack tip in a H-trap laden bainitic microstructure to fundamentally understand the temperature dependent IHE. The new slotted CT specimen approach, with 3.0 wppm total H produced on the slot surface from acidified thiosulfate charging, quantitatively characterized the temperature dependent threshold stress intensity (KIH and K TH) and kinetics (da/dtRISE and da/dtHOLD) of IHE in Cr-Mo weld metal during both rising and slowly falling K loading. IHE was produced successfully and damage was more severe during rising K loading due to the role of crack tip plasticity in H cracking of low to moderate strength steel. The critical temperature at which embrittlement ceased is in the range 45°C < Tc ≤ 60°C for the weld metal and H content studied. This method provides a useful new tool to generate fracture mechanics based fitness-for-service data. A three-dimensional finite element diffusion model, that accounts for the effect of crack tip plasticity and trapping on H transport, established K, dK/dt and temperature dependencies of H distributed about the stressed crack tip in the slotted and standard CT specimens. The slot approach provides higher H levels for long times and/or elevated temperatures, and solves the problem of H loss during testing. The diffusion model was used to understand temperature dependent ME Stress field interaction energy (EH) vs. temperature at the blunted crack tip for Cr-Mo steel is lower than the estimated binding energies (EB) for the various surrounding reversible trap sites; indicating with probability calculations that H is unlikely to repartition from these traps to the stress field. Hydrogen transport to the fracture process zone (FPZ) from the surrounding bulk is by diffusion, enhanced by a plasticity-related mechanism. Interfaces and boundaries within the FPZ in the dilated region at the crack tip are the sites that form the interconnected H-fracture path. Trapped H concentration in these fracture sites critically governs the temperature dependent IHE, with negligible effect of temperature (≤100°C) on the crack tip stress field. The measured KIH for subcritical H cracking under rising K decreases systematically with increasing H trapped in the FPZ, as established by diffusion modeling for a variety of H cracking and temperature conditions. Diffusion model predictions of the critical trapped H concentration indicate that the Tc at which IHE is eliminated from Cr-Mo weld metal should be ≥110°C for a thick-wall hydroprocessing vessel with total-peak H of ≈4.0 wppm.

Solar Effects on Tensile and Optical Properties of Hubble Space Telescope Silver-Teflon(Registered Trademark) Insulation

NASA Technical Reports Server (NTRS)

deGroh, Kim, K.; Dever, Joyce A.; Snyder, Aaron; Kaminski, Sharon; McCarthy, Catherine E.; Rapoport, Alison L.; Rucker, Rochelle N.

2006-01-01

A section of the retrieved Hubble Space Telescope (HST) solar array drive arm (SADA) multilayer insulation (MLI), which experienced 8.25 years of space exposure, was analyzed for environmental durability of the top layer of silver-Teflon (DuPont) fluorinated ethylene propylene (Ag-FEP). Because the SADA MLI had solar and anti-solar facing surfaces and was exposed to the space environment for a long duration, it provided a unique opportunity to study solar effects on the environmental degradation of Ag-FEP, a commonly used spacecraft thermal control material. Data obtained included tensile properties, solar absorptance, surface morphology and chemistry. The solar facing surface was found to be extremely embrittled and contained numerous through-thickness cracks. Tensile testing indicated that the solar facing surface lost 60% of its mechanical strength and 90% of its elasticity while the anti-solar facing surface had ductility similar to pristine FEP. The solar absorptance of both the solar facing surface (0.155 plus or minus 0.032) and the anti-solar facing surface (0.208 plus or minus 0.012) were found to be greater than pristine Ag-FEP (0.074). Solar facing and anti-solar facing surfaces were microscopically textured, and locations of isolated contamination were present on the anti-solar surface resulting in increased localized texturing. Yet, the overall texture was significantly more pronounced on the solar facing surface indicating a synergistic effect of combined solar exposure and increased heating with atomic oxygen erosion. The results indicate a very strong dependence of degradation, particularly embrittlement, upon solar exposure with orbital thermal cycling having a significant effect.

Comparing Interactions in Literature Circles in Both Online and in Class Discussions

ERIC Educational Resources Information Center

Skeen, Christel Ghrist

2014-01-01

Discourse analysis of literature circles can lead educators to understand the different types of interactions taking place as students talk about text. Social and academic interactions exist in both face-to-face and online discussions of reading material. This study examines two different settings of literature circles and compares interactions of…

Anticipated Ongoing Interaction versus Channel Effects of Relational Communication in Computer-Mediated Interaction.

ERIC Educational Resources Information Center

Walther, Joseph B.

1994-01-01

Assesses the related effects of anticipated future interaction and different communication media (computer-mediated versus face-to-face communication) on the communication of relational intimacy and composure. Shows that the assignment of long-term versus short-term partnerships has a larger impact on anticipated future interaction reported by…

Microbial network of the carbonate precipitation process induced by microbial consortia and the potential application to crack healing in concrete.

PubMed

Zhang, Jiaguang; Zhou, Aijuan; Liu, Yuanzhen; Zhao, Bowei; Luan, Yunbo; Wang, Sufang; Yue, Xiuping; Li, Zhu

2017-11-06

Current studies have employed various pure-cultures for improving concrete durability based on microbially induced carbonate precipitation (MICP). However, there have been very few reports concerned with microbial consortia, which could perform more complex tasks and be more robust in their resistance to environmental fluctuations. In this study, we constructed three microbial consortia that are capable of MICP under aerobic (AE), anaerobic (AN) and facultative anaerobic (FA) conditions. The results showed that AE consortia showed more positive effects on inorganic carbon conversion than AN and FA consortia. Pyrosequencing analysis showed that clear distinctions appeared in the community structure between different microbial consortia systems. Further investigation on microbial community networks revealed that the species in the three microbial consortia built thorough energetic and metabolic interaction networks regarding MICP, nitrate-reduction, bacterial endospores and fermentation communities. Crack-healing experiments showed that the selected cracks of the three consortia-based concrete specimens were almost completely healed in 28 days, which was consistent with the studies using pure cultures. Although the economic advantage might not be clear yet, this study highlights the potential implementation of microbial consortia on crack healing in concrete.

Cracks in Complex Bodies: Covariance of Tip Balances

NASA Astrophysics Data System (ADS)

Mariano, Paolo Maria

2008-04-01

In complex bodies, actions due to substructural changes alter (in some cases drastically) the force driving the tip of macroscopic cracks in quasi-static and dynamic growth, and must be represented directly. Here it is proven that tip balances of standard and substructural interactions are covariant. In fact, the former balance follows from the Lagrangian density’s requirement of invariance with respect to the action of the group of diffeomorphisms of the ambient space to itself, the latter balance accrues from an analogous invariance with respect to the action of a Lie group over the manifold of substructural shapes. The evolution equation of the crack tip can be obtained by exploiting invariance with respect to relabeling the material elements in the reference place. The analysis is developed by first focusing on general complex bodies that admit metastable states with substructural dissipation of viscous-like type inside each material element. Then we account for gradient dissipative effects that induce nonconservative stresses; the covariance of tip balances in simple bodies follows as a corollary. When body actions and boundary data of Dirichlet type are absent, the standard variational description of quasi-static crack growth is simply extended to the case of complex materials.