Highly visible-light-responsive Cu2O/rGO decorated with Fe3O4@SiO2 nanoparticles as a magnetically recyclable photocatalyst.

PubMed

Liu, Shou-Heng; Lu, Jun-Sheng; Yang, Sheng-Wei

2018-07-27

The rhombic dodecahedral cuprous oxide-reduced graphene oxide/core-shell Fe 3 O 4 @SiO 2 composites (denoted as rCu 2 O-rGO/Fe 3 O 4 @SiO 2 ) are successfully synthesized facilely via a wet-chemical route. The resulting rCu 2 O-rGO/Fe 3 O 4 @SiO 2 combines the unique structure of Cu 2 O, electronic characteristics of reduced graphene oxide (rGO) and magnetic property of Fe 3 O 4 @SiO 2 to be an effective and recoverable photocatalyst for the degradation of methyl orange (MO). The obtained results show that rCu 2 O-rGO/Fe 3 O 4 @SiO 2 is capable of completely degrading MO in the presence of a very low catalyst concentration (0.125 g l -1 ) within a short time (60 min) under visible light compared to the reported catalysts. The observations may be due to the distinctive interfacial structures of rhombic dodecahedral Cu 2 O nanoparticles connected to rGO sheets that can enhance the separation of photogenerated electron-hole pairs, stabilize the Cu 2 O and increase MO adsorption, as evidenced by a variety of spectroscopic analyses (transmission electron microscopy, x-ray photoelectron spectroscopy and photoluminescence). More importantly, these efficient photocatalysts can easily be recovered under a magnetic field and remain highly photoactive towards the degradation of MO after cyclic tests, and may be promising photocatalysts for practical applications in the solar-energy purification of wastewater.

Synergy of iron and copper oxides in the catalytic formation of PCDD/Fs from 2-monochlorophenol.

PubMed

Potter, Phillip M; Guan, Xia; Lomnicki, Slawomir M

2018-07-01

Transition metal oxides present in waste incineration systems have the ability to catalyze the formation of polychlorinated dibenzo-p-dioxins and dibenzofurans (PCDD/Fs) through surface reactions involving organic dioxin precursors. However, studies have concentrated on the catalytic effects of individual transition metal oxides, while the complex elemental composition of fly ash introduces the possibility of synergistic or inhibiting effects between multiple, catalytically active components. In this study, we have tested fly ash surrogates containing different ratios (by weight) of iron (III) oxide and copper (II) oxide. Such Fe 2 O 3 /CuO mixed-oxide surrogates (in the Fe:Cu ratio of 3.5, 0.9 and 0.2 ) were used to study the cooperative effects between two transition metals that are present in high concentrations in most combustion systems and are known to individually catalyze the formation of PCDD/Fs. The presence of both iron and copper oxides increased the oxidative power of the fly ash surrogates in oxygen rich conditions and led to extremely high PCDD/F yields under pyrolytic conditions (up to >5% yield) from 2-monochlorophenol precursor. PCDD/F congener profiles from the mixed oxide samples are similar to results obtained from only CuO, however the total PCDD/F yield increases with increasing Fe 2 O 3 content. Careful analysis of the reaction products and changes to the oxidation states of active metals indicate the CuO surface sites are centers for reaction while the Fe 2 O 3 is affecting the bonds in CuO and increasing the ability of copper centers to form surface-bound radicals that are precursors to PCDD/Fs. Copyright © 2018 Elsevier Ltd. All rights reserved.

Effect of Metal Oxide Nanoparticles on Microbial Community Structure and Function in Two Different Soil Types

PubMed Central

Frenk, Sammy; Ben-Moshe, Tal; Dror, Ishai; Berkowitz, Brian; Minz, Dror

2013-01-01

Increased availability of nanoparticle-based products will, inevitably, expose the environment to these materials. Engineered nanoparticles (ENPs) may thus find their way into the soil environment via wastewater, dumpsters and other anthropogenic sources; metallic oxide nanoparticles comprise one group of ENPs that could potentially be hazardous for the environment. Because the soil bacterial community is a major service provider for the ecosystem and humankind, it is critical to study the effects of ENP exposure on soil bacteria. These effects were evaluated by measuring bacterial community activity, composition and size following exposure to copper oxide (CuO) and magnetite (Fe3O4) nanosized (<50 nm) particles. Two different soil types were examined: a sandy loam (Bet-Dagan) and a sandy clay loam (Yatir), under two ENP concentrations (1%, 0.1%). Results indicate that the bacterial community in Bet-Dagan soil was more susceptible to change due to exposure to these ENPs, relative to Yatir soil. More specifically, CuO had a strong effect on bacterial hydrolytic activity, oxidative potential, community composition and size in Bet-Dagan soil. Few effects were noted in the Yatir soil, although 1% CuO exposure did cause a significant decreased oxidative potential and changes to community composition. Fe3O4 changed the hydrolytic activity and bacterial community composition in Bet-Dagan soil but did not affect the Yatir soil bacterial community. Furthermore, in Bet-Dagan soil, abundance of bacteria annotated to OTUs from the Bacilli class decreased after addition of 0.1% CuO but increased with 1% CuO, while in Yatir soil their abundance was reduced with 1% CuO. Other important soil bacterial groups, including Rhizobiales and Sphingobacteriaceae, were negatively affected by CuO addition to soil. These results indicate that both ENPs are potentially harmful to soil environments. Furthermore, it is suggested that the clay fraction and organic matter in different soils interact with the ENPs and reduce their toxicity. PMID:24349575

Facile synthesis of CuFe2O4-Fe2O3 composite for high-performance supercapacitor electrode applications

NASA Astrophysics Data System (ADS)

Khan, Rashid; Habib, Muhammad; Gondal, Mohammed A.; Khalil, Adnan; Rehman, Zia Ur; Muhammad, Zahir; Haleem, Yasir A.; Wang, Changda; Wu, Chuan Qiang; Song, Li

2017-10-01

We report the synthesis of CuFe2O4-Fe2O3 composite material for efficient and highly stable supercapacitor electrode by using eco-friendly low-temperature co-precipitation method. The CuFe2O4-Fe2O3 composite demonstrated the highest specific capacitance of 638.24 F g-1 and excellent stability up to 2000 charge/discharge cycles. The achieved capacitance value is 16 times higher than that of pure CuFe2O4. The results revealed the extraordinary performance of CuFe2O4-Fe2O3 composite as supercapacitor electrode with excellent retention in comparison to CuFe2O4. The enhanced electrochemical activity of CuFe2O4-Fe2O3 composite is attributed to the synergistic effect which is responsible for redox coupling between Cu2+ and Fe3+ that has never been achieved by single component before.

LaCrO3/CuFe2O4 Composite-Coated Crofer 22 APU Stainless Steel Interconnect of Solid Oxide Fuel Cells

NASA Astrophysics Data System (ADS)

Hosseini, Seyedeh Narjes; Enayati, Mohammad Hossein; Karimzadeh, Fathallah; Dayaghi, Amir Masoud

2017-07-01

Rapidly rising contact resistance and cathode Cr poisoning are the major problems associated with unavoidable chromia scale growth on ferritic stainless steel (FSS) interconnects of solid oxide fuel cells. This work investigates the performance of the novel screen-printed composite coatings consisting of dispersed conductive LaCrO3 particles in a CuFe2O4 spinel matrix for Crofer 22 APU FSS, with emphasis on the oxidation behavior and electrical conductivity of these coatings. The results show that the presence of protective spinel coating, accompanied by the effective role of LaCrO3 particle incorporation, prevents the Cr2O3 subscale growth as well as chromium migration into the coating surface at the end of 400 hours of oxidation at 1073 K (800 °C) in air. In addition, the composite coatings decreased the area specific resistance (ASR) from 51.7 and 13.8 mΩ cm2 for uncoated and spinel-coated samples, respectively, to a maximum of 7.7 mΩ cm2 for composite-coated samples after 400 hours of oxidation.

Equilibrium isotopic fractionation of copper during oxidation/reduction, aqueous complexation and ore-forming processes: Predictions from hybrid density functional theory

NASA Astrophysics Data System (ADS)

Sherman, David M.

2013-10-01

Copper exists as two isotopes: 65Cu (∼30.85%) and 63Cu (∼69.15%). The isotopic composition of copper in secondary minerals, surface waters and oxic groundwaters is 1-12‰ heavier than that of copper in primary sulfides. Changes in oxidation state and complexation should yield substantial isotopic fractionation between copper species but it is unclear to what extent the observed Cu isotopic variations reflect equilibrium fractionation. Here, I calculate the reduced partition function ratios for chalcopyrite (CuFeS2), cuprite (Cu2O), tenorite (CuO) and aqueous Cu+, Cu+2 complexes using periodic and molecular hybrid density functional theory to predict the equilibrium isotopic fractionation of Cu resulting from oxidation of Cu+ to Cu+2 and by complexation of dissolved Cu. Among the various copper(II) complexes in aqueous environments, there is a significant (1.3‰) range in the reduced partition function ratios. Oxidation and congruent dissolution of chalcopyrite (CuFeS2) to dissolved Cu+2 (as Cu(H2O)5+2) yields 65-63δ(Cu+2-CuFeS2) = 3.1‰ at 25 °C; however, chalcopyrite oxidation/dissolution is incongruent so that the observed isotopic fractionation will be less. Secondary precipitation of cuprite (Cu2O) would yield further enrichment of dissolved 65Cu since 65-63δ(Cu+2-Cu2O) is 1.2‰ at 25 °C. However, precipitation of tenorite (CuO) will favor the heavy isotope by +1.0‰ making dissolved Cu isotopically lighter. These are upper-limit estimates for equilibrium fractionation. Therefore, the extremely large (9‰) fractionations between dissolved Cu+2 (or Cu+2 minerals) and primary Cu+ sulfides observed in supergene environments must reflect Rayleigh (open-system) or kinetic fractionation. Finally the previously proposed (Asael et al., 2009) use of δ65Cu in chalcopyrite to estimate the oxidation state of fluids that transported Cu in stratiform sediment-hosted copper deposits is refined.

Hydrothermal synthesis of graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite for removal of Cu (II) and methylene blue

NASA Astrophysics Data System (ADS)

Long, Zhihang; Zhan, Yingqing; Li, Fei; Wan, Xinyi; He, Yi; Hou, Chunyan; Hu, Hai

2017-09-01

In this work, highly activated graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite adsorbent was prepared from a simple hydrothermal route by using ferrous sulfate as precursor. For this purpose, the graphene oxide/multiwalled carbon nanotube architectures were formed through the π-π attractions between them, followed by attaching Fe3O4 nanoparticles onto their surface. The structure and composition of as-prepared ternary nanocomposite were characterized by XRD, FTIR, XPS, SEM, TEM, Raman, TGA, and BET. It was found that the resultant porous graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite with large surface area could effectively prevent the π-π stacking interactions between graphene oxide nanosheets and greatly improve sorption sites on the surfaces. Thus, owing to the unique ternary nanocomposite architecture and synergistic effect among various components, as-prepared ternary nanocomposite exhibited high separation efficiency when they were used to remove the Cu (II) and methylene blue from aqueous solutions. Furthermore, the adsorption isotherms of ternary nanocomposite structures for Cu (II) and methylene blue removal fitted the Langmuir isotherm model. This work demonstrated that the graphene oxide/multiwalled carbon nanotube/Fe3O4 ternary nanocomposite was promising as an efficient adsorbent for heavy metal ions and organic dye removal from wastewater in low concentration.

Synthesis of low-size flower-like AlOOH structures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bakina, Olga V., E-mail: ovbakina@ispms.tsc.ru, E-mail: eagl@ispms.tsc.ru; Glazkova, Elena A., E-mail: ovbakina@ispms.tsc.ru, E-mail: eagl@ispms.tsc.ru; Lozhkomoev, Aleksandr S., E-mail: asl@ispms.tsc.ru

Al/Cu, Al/Zn, and Al/Fe bimetallic nanoparticles have been obtained using the method of simultaneous electrical explosion of metal pairs in an argon atmosphere. The nanoparticles are chemically active and interact with water at 60°C forming flower-like hierarchical porous structures with a high specific surface area. As the Al/Cu nanopowder is oxidized with water, flower-like pseudoboehmite composite structures are formed with the size of under 1.0 μm; structurally heterogeneous electron-dense spherical inclusions of unreacted metal copper and intermetallides are identified inside them. Al/Fe product transformations are presented by the flower-like pseudoboehmite surrounded by lamellar structures enriched with ferric oxides. Al/Zn nanoparticlesmore » react with water, forming the flower-like pseudoboehmite and mainly hexagonal zinc oxide laminae. The composite particles obtained can be used as antibacterial agents in manufacturing medical supplies.« less

Solubility of copper in silicate melts as function of oxygen and sulfur fugacities, temperature, and silicate composition

NASA Astrophysics Data System (ADS)

Holzheid, A.; Lodders, K.

2001-06-01

The solubility of Cu in silicate melts coexisting with liquid Cu(Fe) metal and liquid Cu(Fe) sulfide was determined experimentally at oxygen fugacities ranging from 10 -9.1 to 10 -13.6 bar and sulfur fugacities ranging from 10 -2.5 to 10 -6.3 bar at 1300°C. An iron oxide-free silicate of anorthite-diopside eutectic composition and a synthetic MgO-rich basaltic silicate (FeO-bearing) were used in the partitioning experiments. In S-containing systems, some of the metal reacted to metal sulfide. The silicates in the four systems investigated (Fe-free and S-free; Fe-containing and S-free; Fe-free and S-containing; Fe-containing and S-containing) had different colors depending on the dissolved Cu species and the presence of iron and/or sulfur. Irrespective of the presence of sulfur, the solubility of Cu in the silicate increases with increasing oxygen fugacity and metal/silicate partition coefficients for Cu decrease. Increasing the temperature from 1300°C to 1514°C increases the Cu solubility (decreases the metal/silicate partition coefficient) at an oxygen fugacity 0.5 log units below the iron-wüstite (IW) equilibrium in the Fe-free, S-free and Fe-containing, S-free systems. We infer the presence of monovalent Cu + ("CuO 0.5") in the silicate melt on the basis of the solubility of Cu as function of oxygen fugacity. Experiments containing iron yield a formal valence of ˜0.5 for Cu at very low oxygen fugacities, which is not observed in Fe-free systems. The low formal valence is explained by redox reactions between iron and copper in the silicate melts. There is no evidence for sulfidic dissolution of Cu in the silicates but sulfur has indirect effects on Cu partitioning. Iron metal/silicate partition coefficients depend on oxygen fugacity and on sulfur fugacity. Sulfidic dissolution of iron and oxide-sulfide exchange reactions with Cu cause a small increase in Cu metal/silicate partition coefficients. We derive an activity coefficient (γ CuO 0.5) of 10 ± 1 for liquid CuO 0.5 at 1300°C for the silicate melts used here. A comparison with literature data shows that log γ CuO 0.5 increases in proportion to the mass percentages [CaO +(Al 2O 3)/2] in silicate melts. We recommend the following equations for Cu metal/silicate and sulfide/silicate partitioning for geochemical and cosmochemical modeling if silicate composition and the activity of Cu in the metal or sulfide is known: log D met/sil = -0.48 - 0.25 · log fO 2 - log γ Cu metal + 0.02 · [CaO + (Al 2O 3)/2; wt%] silicate logD sul/sil=+0.76-0.25 · logfO 2+0.25logfS 2-logγ CS 0.5,sulfide +0.02 · [CaO+Al 2O 3/2;wt%] silicate. The derived Cu metal/silicate and metal/sulfide partition coefficients are applied to core formation in the Earth and Mars. The observed Cu abundances in the Earth cannot be easily explained by simple core-mantle equilibrium, but the observed Cu abundances for Mars are consistent with core-mantle equilibrium at low pressure and temperatures.

The preparation and activity of Cu-Fe-Zr-Ce based catalysts for water gas shift

NASA Astrophysics Data System (ADS)

Wu, H. D.; Liu, T. S.; Liu, H. Z.

2018-01-01

CeO2-ZrO2 composite oxide was synthesized with precipitation method as support and CuaFeb(ZrCe4)8Ox catalysts were prepared by impregnation; X-ray diffraction, H2 temperature program reduction, and scanning electron microscope techniques were jointly used to characterize the crystal phases and reduction properties of catalysts. Then the activity of catalysts in water gas shift was studied, thus investigated how catalyst composition impacted the water gas shift. Conclusions drew from the results can be briefly stated. CuaFeb(ZrCe4)8Ox was provided with stable cubic crystalline framework and Cu and Fe, as the active components, was highly dispersed on the surface of supports in the form of CuO and Fe2O3 respectively. The strong interactions between copper and iron component enhanced the reducing capacity of CuO and Fe2O3. CuaFeb(ZrCe4)8Ox catalysts exhibited high catalytic activity and selectivity while the main active components were Cu and Fe3O4. The CO conversion rate reached 96% when Cu7Fe3(ZrCe4)8Ox catalysts was used in water gas shift at 623K and the only products were H2 and CO2. The activity was still desirable even the catalysts was applied at 723K.

Responses of mixed methanotrophic consortia to variable Cu2+/Fe2+ ratios.

PubMed

Chidambarampadmavathy, Karthigeyan; Karthikeyan, Obulisamy Parthiba; Huerlimann, Roger; Maes, Gregory E; Heimann, Kirsten

2017-07-15

Methane mitigation in landfill top cover soils is mediated by methanotrophs whose optimal methane (CH 4 ) oxidation capacity is governed by environmental and complex microbial community interactions. Optimization of CH 4 remediating bio-filters need to take microbial responses into account. Divalent copper (Cu 2+ ) and iron (Fe 2+ ) are present in landfills at variable ratios and play a vital role in methane oxidation capacity and growth of methanotrophs. This study, as a first of its kind, therefore quantified effects of variable Cu 2+ and Fe 2+ (5:5, 5:25 and 5:50 μM) ratios on mixed methanotrophic communities enriched from landfill top cover (LB) and compost soils (CB). CH 4 oxidation capacity, CH 4 removal efficiencies, fatty acids content/profiles and polyhydroxybutyrate (PHB; a biopolymer) contents were also analysed to quantify performance and potential co-product development. Mixed methanotroph cultures were raised in 10 L continuous stirred tank reactors (CSTRs, Bioflo ® & Celligen ® 310 Fermentor/Bioreactor; John Morris Scientific, Chatswood, NSW, Australia). Community structure was determined by amplifying the V3-V4 region of 16s rRNA gene. Community structure and, consequently, fatty acid-profiles changed significantly with increasing Cu 2+ /Fe 2+ ratios, and responses were different for LB and CB. Effects on methane oxidation capacities and PHB content were similar in the LB- and CB-CSTR, decreasing with increasing Cu 2+ /Fe 2+ ratios, while biomass growth was unaffected. In general, high Fe 2+ concentration favored growth of the type -II methanotroph Methylosinus in the CB-CSTR, but methanotroph abundances decreased in the LB-CSTR. Increase in Cu 2+ /Fe 2+ ratio increased the growth of Sphingopyxis in both systems, while Azospirllum was co-dominant in the LB- but absent in the CB-CSTR. After 13 days, methane oxidation capacities and PHB content decreased by ∼50% and more in response to increasing Fe 2+ concentrations. Although methanotroph abundance was ∼2% in the LB- (compared to >50% in CB-CSTR), methane oxidation capacities were comparable in the two systems, suggesting that methane oxidation capacity was maintained by the dominant Azospirllum and Sphingopyxis in the LB-CSTR. Despite similar methanotroph inoculum community composition and controlled environmental variables, increasing Cu 2+ /Fe 2+ ratios resulted in significantly different microbial community structures in the LB- and CB-CSTR, indicative of complex microbial interactions. In summary, our results suggest that a detailed understanding of allelopathic interactions in mixed methanotrophic consortia is vital for constructing robust bio-filters for CH 4 emission abatement. Copyright © 2017 Elsevier Ltd. All rights reserved.

Preparation and microwave-infrared absorption of reduced graphene oxide/Cu-Ni ferrite/Al2O3 composites

NASA Astrophysics Data System (ADS)

De-yue, Ma; Xiao-xia, Li; Yu-xiang, Guo; Yu-run, Zeng

2018-01-01

Reduced graphene oxide (RGO)/Cu-Ni ferrite/Al2O3 composite was prepared by solvothermal method, and its properties were characterized by SEM, x-ray diffraction, energy-dispersive x-ray spectroscopy and FTIR. The electromagnetic parameters in 2-18 GHz and mid-infrared (IR) spectral transmittance of the composite were measured, respectively. The results show that Cu0.7Ni0.3Fe2O4 nanoparticles with an average size of tens nanometers adsorb on surface of RGO, and meanwhile, Al2O3 nanoparticles adhere to the surface of Cu0.7Ni0.3Fe2O4 nanoparticles and RGO. The composite has both dielectric and magnetic loss mechanism. Its reflection loss is lower than -19 dB in 2-18 GHz, and the maximum of -23.2 dB occurs at 15.6 GHz. With the increasing of Al2O3 amount, its reflection loss becomes lower and the maximum moves towards low frequency slightly. Compared with RGO/Cu-Ni ferrite composites, its magnetic loss and reflection loss slightly reduce with the increasing of Al2O3 amount, and the maximum of reflection loss shifts from a low frequency to a high one. However, its broadband IR absorption is significantly enhanced owing to nano-Al2O3. Therefore, RGO/Cu-Ni ferrite/Al2O3 composites can be used as excellent broadband microwave and IR absorbing materials, and maybe have broad application prospect in electromagnetic shielding, IR absorbing and coating materials.

The effect of ionic interactions on the oxidation of metals in natural waters

NASA Astrophysics Data System (ADS)

Millero, Frank J.

1985-02-01

The effect of ionic interactions of the major components of natural waters on the oxidation of Cu(I) and Fe(II) has been examined. The various ion pairs of these metals have been shown to have different rates of oxidation. For Fe(II), the chloride and sulfate ion pairs are not easily oxidized. The measured decrease in the rate constant at a fixed pH in chloride and sulfate solutions agrees very well with the values predicted. The effect of pH (6 to 8) on the oxidation of Fe(II) in water and seawater have been shown to follow the rate equation -d in [Fe(II)]/dt = k 1β 1α Fe/[H +] + k 2β 2α Fe/[H +] 2 where k1 and k2 are the pseudo first order rate constants, β1 and β2 are the hydrolysis constants for Fe(OH) + and Fe(OH) 0. The value of αFE is the fraction of free Fe 2+. The value of k1 (2.0 ±0.5 min-1) in water and seawater are similar within experimental error. The value of k2 (1.2 × 10 5 min -1) in seawater is 28% of its value in water in reasonable agreement with predictions using an ion pairing model. For the oxidation of Cu(I) a rate equation of the form -d ln [Cu(I)]/dt = k 0α Cu+ k 1β 1α Cu[Cl] was found where k0 (14.1 sec -1) and k1 (3.9 sec -1) are the pseudo first order rate constants for the oxidation of Cu + and CuCl 0, β1 is the formation constant for CuCl 0 and αCu is the fraction of free Cu +. Thus, unlike the results for Fe(II), Cu(I) chloride complexes have measurable rates of oxidation.

High strength-high conductivity Cu--Fe composites produced by powder compaction/mechanical reduction

DOEpatents

Verhoeven, John D.; Spitzig, William A.; Gibson, Edwin D.; Anderson, Iver E.

1991-08-27

A particulate mixture of Cu and Fe is compacted and mechanically reduced to form an "in-situ" Cu-Fe composite having high strength and high conductivity. Compaction and mechanical reduction of the particulate mixture are carried out at a temperature and time at temperature selected to avoid dissolution of Fe into the Cu matrix particulates to a harmful extent that substantially degrades the conductivity of the Cu-Fe composite.

Optical properties of reduced graphene oxide and CuFe2O4 composites in the IR region

NASA Astrophysics Data System (ADS)

Ma, De-yue; Li, Xiao-xia; Guo, Yu-xiang; Zeng, Yu-run

2018-01-01

The complex refractive index of reduced graphene oxide and CuFe2O4 composites prepared by hydrothermal method was calculated using infrared Micro-reflective spectra and K-K relation, and the calculation errors were analyzed according to its IR transmission and spectral reflectivity calculated by Fresnel formula. And then normal emissivity of the composite in IR atmospheric window was calculated by means of Fresnel formula and modified refraction angle formula. The calculation accuracy was verified by comparing measured normal total emissivity with the calculated one. The results show that complex refractive index and normal emissivity calculated by the formulas have a high accuracy. It has been found that the composite has a good absorption and radiation characteristics in IR atmospheric window and a strong scattering ability in middle IR region by analyzing its extinction, absorption and radiation properties in IR region. Therefore, it may be used as IR absorption, extinction and radiation materials in some special fields.

Ligand-hole localization in oxides with unusual valence Fe

PubMed Central

Chen, Wei-Tin; Saito, Takashi; Hayashi, Naoaki; Takano, Mikio; Shimakawa, Yuichi

2012-01-01

Unusual high-valence states of iron are stabilized in a few oxides. A-site-ordered perovskite-structure oxides contain such iron cations and exhibit distinct electronic behaviors at low temperatures, e.g. charge disproportionation (4Fe4+ → 2Fe3+ + 2Fe5+) in CaCu3Fe4O12 and intersite charge transfer (3Cu2+ + 4Fe3.75+ → 3Cu3+ + 4Fe3+) in LaCu3Fe4O12. Here we report the synthesis of solid solutions of CaCu3Fe4O12 and LaCu3Fe4O12 and explain how the instabilities of their unusual valence states of iron are relieved. Although these behaviors look completely different from each other in simple ionic models, they can both be explained by the localization of ligand holes, which are produced by the strong hybridization of iron d and oxygen p orbitals in oxides. The localization behavior in the charge disproportionation of CaCu3Fe4O12 is regarded as charge ordering of the ligand holes, and that in the intersite charge transfer of LaCu3Fe4O12 is regarded as a Mott transition of the ligand holes. PMID:22690318

Synthesis of Cu-Fe{sub 3}O{sub 4}@graphene composite: A magnetically separable and efficient catalyst for the reduction of 4-nitrophenol

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu, Ran; Bi, Huiping, E-mail: hpbi@njust.edu.cn; He, Guangyu

2014-09-15

Highlights: • The Cu-Fe{sub 3}O{sub 4}@GE composite was prepared by one-step solvent–thermal method. • The Cu-Fe{sub 3}O{sub 4}@GE composite exhibited the highest catalytic activity with excellent stability. • The Cu-Fe{sub 3}O{sub 4}@GE composite was magnetically separable. - Abstract: In this work, the Cu-Fe{sub 3}O{sub 4}@GE composite was prepared easily by a one-step solvent–thermal method, which achieved the formation of Cu nanoparticles (Cu NPs), Fe{sub 3}O{sub 4} nanoparticles (Fe{sub 3}O{sub 4} NPs) and reduction of GO simultaneously. The morphology and structure of the composite was fully characterized by means of X-ray diffraction (XRD), Fourier transformed infrared (FTIR) spectroscopy, transmission electron microscopymore » (TEM). The time-dependent adsorption spectra of the reaction mixture was measured by UV–vis absorption spectroscopy. The results demonstrated that the Cu NPs and Fe{sub 3}O{sub 4} NPs were densely and evenly deposited on the graphene (GE) sheets. It was found that the Cu-Fe{sub 3}O{sub 4}@GE composite exhibited high catalytic activities on the reduction of p-nitrophenol to p-aminophenol. Furthermore, the composite catalyst can be easily recovered due to its magnetic separability and high stability.« less

Highly efficient Cu-decorated iron oxide nanocatalyst for low pressure CO 2 conversion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Halder, Avik; Kilianová, Martina; Yang, Bing

We report a nanoparticulate iron oxide based catalyst for CO2 conversion with high efficiency at low pressures and on the effect of the presence of copper on the catalyst's restructuring and its catalytic performance. In situ X-ray scattering reveals the restructuring of the catalyst at the nanometer scale. In situ X-ray absorption near edge structure (XANES) shows the evolution of the composition and oxidation state of the iron and copper components under reaction conditions along with the promotional effect of copper on the chemical transformation of the iron component. X-ray diffraction (XRD), XANES and Raman spectroscopy proved that the startingmore » nano catalyst is composed of iron oxides differing in chemical nature (alpha-Fe2O3, Fe3O4, FeO(OH)) and dimensionality, while the catalyst after CO2 conversion was identified as a mixture of alpha-Fe, Fe3C, and traces of Fe5C2. The significant increase of the rate CO2 is turned over in the presence of copper nanoparticles indicates that Cu nanoparticles activate hydrogen, which after spilling over to the neighbouring iron sites, facilitate a more efficient conversion of carbon dioxide.« less

High strength-high conductivity Cu-Fe composites produced by powder compaction/mechanical reduction

DOEpatents

Verhoeven, J.D.; Spitzig, W.A.; Gibson, E.D.; Anderson, I.E.

1991-08-27

A particulate mixture of Cu and Fe is compacted and mechanically reduced to form an ''in-situ'' Cu-Fe composite having high strength and high conductivity. Compaction and mechanical reduction of the particulate mixture are carried out at a temperature and time at temperature selected to avoid dissolution of Fe into the Cu matrix particulates to a harmful extent that substantially degrades the conductivity of the Cu-Fe composite. 5 figures.

Nitrate removal by Fe0/Pd/Cu nano-composite in groundwater.

PubMed

Liu, Hongyuan; Guo, Min; Zhang, Yan

2014-01-01

Nitrate pollution in groundwater shows a great threat to the safety of drinking water. Chemical reduction by zero-valent iron is being considered as a promising technique for nitrate removal from contaminated groundwater. In this paper, Fe0/Pd/Cu nano-composites were prepared by the liquid-phase reduction method, and batch experiments of nitrate reduction by the prepared Fe0/Pd/Cu nano-composites under various operating conditions were carried out. It has been found that nano-Fe0/Pd/Cu composites processed dual functions: catalytic reduction and chemical reduction. The introduction of Pd and Cu not only improved nitrate removal rate, but also reduced the generation of ammonia. Nitrate removal rate was affected by the amount of Fe0/Pd/Cu, initial nitrate concentration, solution pH, dissolved oxygen (DO), reaction temperature, the presence of anions, and organic pollutant. Moreover, nitrate reduction by Fe0/Pd/Cu composites followed the pseudo-first-order reaction kinetics. The removal rate of nitrate and total nitrogen were about 85% and 40.8%, respectively, under the reaction condition of Fe-6.0%Pd-3.0%Cu amount of 0.25 g/L, pH value of 7.1, DO of 0.42 mg/L, and initial nitrate concentration of 100 mg/L. Compared with the previous studies with Fe0 alone or Fe-Cu, nano-Fe-6%Pd-3%Cu composites showed a better selectivity to N2.

Copper-nickel superalloys as inert alloy anodes for aluminum electrolysis

NASA Astrophysics Data System (ADS)

Shi, Zhongning; Xu, Junli; Qiu, Zhuxian; Wang, Zhaowen; Gao, Bingliang

2003-11-01

The superalloys Cu-Ni-Al, Cu-Ni-Fe, and Cu-Ni-Cr were studied as anodes for aluminum electrolysis. The alloys were tested for corrosion in acidic electrolyte molten salt and for oxidation in both air and oxygen. The results showed that the Cu-Ni-Al anodes possess excellent resistance to oxidation and corrosion, and the oxidation rates of Cu-Ni-Fe and Cu-Ni-Al anodes were slower than those of pure copper or nickel. During electrolysis, the cell voltage of the Cu-Ni-Al anode was affected most by the concentration of alumina in cryolite molten salt. The Cu-Ni-Fe anode exhibited corrosion resistance in electrolyte molten salt. Comparatively, the Cu-Ni-Cr anode showed poor resistance to oxidation and corrosion. The testing found that further study is warranted on the use of Cu-Ni-Al and Cu-Ni-Fe as inert alloy anodes.

Fe3O4@SiO2@CS-TETA functionalized graphene oxide for the adsorption of methylene blue (MB) and Cu(II)

NASA Astrophysics Data System (ADS)

Wang, Fan; Zhang, Lijuan; Wang, Yeying; Liu, Xijian; Rohani, Sohrab; Lu, Jie

2017-10-01

The graphene oxide (GO) functionalized by Fe3O4@SiO2@CS-TETA nanoparticles, Fe3O4@SiO2@CS-TETA-GO, was firstly fabricated in a mild way as a novel adsorbent for the removal of Cu(II) ions and methylene blue (MB) from aqueous solutions. The magnetic composites showed a good dispersity in water and can be conveniently collected for reuse through magnetic separation due to its excellent magnetism. When the Fe3O4@SiO2@CS- TETA-GO was used as an absorbent for the absorption of MB and Cu(II), the adsorption kinetics and isotherms data well fitted the pseudo-second-order model and the Langmuir model, respectively. Under the optimized pH and initial concentration, the maximum adsorption capacity was about 529.1 mg g-1 for MB in 20 min and 324.7 mg g-1 for Cu(II) in 16 min, respectively, exhibiting a better adsorption performance than other GO-based adsorbents reported recently. More importantly, the synthesized adsorbent could be effectively regenerated and repeatedly utilized without significant capacity loss after six times cycles. All the results demonstrated that Fe3O4@SiO2@CS-TETA-GO could be used as an excellent adsorbent for the adsorption of Cu(II) and MB in many fields.

Facile synthesis, characterization and magnetic property of CuFe12O19 nanostructures via a sol-gel auto-combustion process

NASA Astrophysics Data System (ADS)

Ansari, Fatemeh; Sobhani, Azam; Salavati-Niasari, Masoud

2016-03-01

Copper hexaferrite (CuFe12O19) nanostructures were prepared by a simple route utilizing maltose-assisted sol-gel process. The morphology, phase structure, composition and purity of nanostructures can be controlled by type of surfactant and also adjusting the Cu:surfactant, Cu:Fe and Cu:reductant ratios. The bean-shape structures are formed in the absence of the surfactant when the molar ratio of Cu:Fe and Cu:reductant are 1:12 and 1:26, respectively. The agglomerated spherical nanoparticles with diameters ranging from 7 to 20 nm are obtained in the presence of triplex, when ratio of Cu:reductant is 1:26. In the absence of surfactant and also in the presence of triplex, the samples are found to be CuFe12O19. When polymer is used, there are still the peaks of CuFe12O19 and also some boad peaks in XRD patterns, because of the small size and encapsulation of nanostructures with polymer. Magnetic measurments show superparamagnetic behavior for the all samples. The Ms for the samples obtained in the presence of polymer shows that the coating of magnetic nanostructures does not always increase Ms. FT-IR frequency bands in the range 463-626, 607 and 542 cm-1 correspond to the formation of metal oxides in ferrites.

Cu isotopes in marine black shales record the Great Oxidation Event

PubMed Central

Rodríguez, Nathalie P.; Partin, Camille A.; Andersson, Per; Weiss, Dominik J.; El Albani, Abderrazak; Rodushkin, Ilia; Konhauser, Kurt O.

2016-01-01

The oxygenation of the atmosphere ∼2.45–2.32 billion years ago (Ga) is one of the most significant geological events to have affected Earth’s redox history. Our understanding of the timing and processes surrounding this key transition is largely dependent on the development of redox-sensitive proxies, many of which remain unexplored. Here we report a shift from negative to positive copper isotopic compositions (δ65CuERM-AE633) in organic carbon-rich shales spanning the period 2.66–2.08 Ga. We suggest that, before 2.3 Ga, a muted oxidative supply of weathering-derived copper enriched in 65Cu, along with the preferential removal of 65Cu by iron oxides, left seawater and marine biomass depleted in 65Cu but enriched in 63Cu. As banded iron formation deposition waned and continentally sourced Cu became more important, biomass sampled a dissolved Cu reservoir that was progressively less fractionated relative to the continental pool. This evolution toward heavy δ65Cu values coincides with a shift to negative sedimentary δ56Fe values and increased marine sulfate after the Great Oxidation Event (GOE), and is traceable through Phanerozoic shales to modern marine settings, where marine dissolved and sedimentary δ65Cu values are universally positive. Our finding of an important shift in sedimentary Cu isotope compositions across the GOE provides new insights into the Precambrian marine cycling of this critical micronutrient, and demonstrates the proxy potential for sedimentary Cu isotope compositions in the study of biogeochemical cycles and oceanic redox balance in the past. PMID:27091980

The role of impurity ions in the formation of phase composition of Norilsk ore types

NASA Astrophysics Data System (ADS)

Mashukov, Anatoly; Mashukova, Alla

2013-04-01

Using the methods of X-ray and Mössbauer spectroscopy, scanning electron microscopy, there were studied the samples of Norilsk ore types in order to identify compounds containing Cu and Ni. Depending on elemental composition there were singled out two sample series. Maximum concentration in percentage of selected elements for this series is presented below. 1: Ni (0), Cu (0,42), S (11,2), O (20,2), H (0.02), Fe(46,8), Ca (5,85), Mg (1,75), K (0,47), Na (0). 2: Ni (4,93), Cu (0), S (14,9), O (27,1), H (0,11), Fe (28,1), Ca (14,9), Mg (0), K (0), Na (1,61). The research conducted by using the method of scanning electron microscopy and the X-ray microanalysis showed that iron and sulfur are spread uniformly over the scanned area. Sulfur is absent in the inclusions containing Fe and Ni. There are areas, sizes 8 - 120 microns, strongly enriched by Fe. The inclusions of rectangular and rhomboid shapes sizes 8 - 15 microns contain Ni as the content of Fe increases. There were identified the inclusions having a high content of Cu, with a maximum concentration of Ni. The presence of native elements testifies to the reducing mode of ore formation processes. The phases, containing Cu ? Ni, have a complex composition: pentlandite (FeNiS2), chalcopyrite (CuFeS2), bornite (CuFeS4), nickelhexahydrite (NiSO4 [6H2O]), wroewolfeite (Cu4 (OH) 6 (SO4) • 2H2O), pyrrhotine (Fe7S8), pyrite (FeS2). The position of the absorption lines in the magnetically ordered areas indicates the presence of stoichiometric FeS and CuFeS2. Some of the samples of this group have broadened lines, indicating the existence of various positions of the Fe ions in the sublattices. The ingrowths of CuFeS2 are characterized by the degree of the structure defectiveness, by various impurities, which is reflected in the studied parameters. As regards the other sample series, containing FeS and CuFeS2 in pyrrhotine matrix of Fe 1-xSx, the spectra are the superposition of the unsolved doublet, which shows the presence of paramagnetic areas. The magnetic phase has the spectrum composed of two six-linear spectrums. The peaks on the spectrum borders show the oxide presence. The isomer shifts of the samples range from 0 to 1.394 mm/s, quadrupole splitting ranges from 0 to 2.688 mm/s. This indicates that the local electronic structure depends on the genesis of compounds. Thus, most of the bulk of Cu, Ni is not dissipated in the crystal lattices of the ore, but it is part of the ore sulphides. The presence of the characteristic structures of the solid solutions decomposition shows a wide temperature range of sulphide crystallization.

For cermet inert anode containing oxide and metal phases useful for the electrolytic production of metals

DOEpatents

Ray, Siba P.; Liu, Xinghua; Weirauch, Douglas A.

2002-01-01

A cermet inert anode for the electrolytic production of metals such as aluminum is disclosed. The inert anode comprises a ceramic phase including an oxide of Ni, Fe and M, where M is at least one metal selected from Zn, Co, Al, Li, Cu, Ti, V, Cr, Zr, Nb, Ta, W, Mo, Hf and rare earths, preferably Zn and/or Co. Preferred ceramic compositions comprise Fe.sub.2 O.sub.3, NiO and ZnO or CoO. The cermet inert anode also comprises a metal phase such as Cu, Ag, Pd, Pt, Au, Rh, Ru, Ir and/or Os. A preferred metal phase comprises Cu and Ag. The cermet inert anodes may be used in electrolytic reduction cells for the production of commercial purity aluminum as well as other metals.

Factors affecting the partitioning of Cu, Zn and Pb in boulder coatings and stream sediments in the vicinity of a polymetallic sulfide deposit

USGS Publications Warehouse

Filipek, L.H.; Chao, T.T.; Carpenter, R.H.

1981-01-01

A sequential extraction scheme is utilized to determine the geochemical partitioning of Cu, Zn and Pb among hydrous Mn- and Fe-oxides, organics and residual crystalline silicates and oxides in the minus-80-mesh ( Fe-oxides > Mn-oxides; Zn, Mn-oxides {reversed tilde equals} organics > Fe-oxides; Pb, Fe-oxides > organics > Mn-oxides. In the sediments, organics are the most efficient scavengers of all three ore metals. These results emphasize the importance of organics as sinks for the ore metals, even in environments with high concentrations of Mn- and Fe-oxides. Of the ore metals, Zn appears to be the most mobile, and is partitioned most strongly into the coatings. However, anomaly contrast for hydromorphic Zn, normalized to the MnFe-oxide or organic content, is similar in sediments and coatings. Cu shows the highest anomaly on the boulder coatings, probably due to precipitation of a secondary Cu mineral. In contrast, detrital Pb in the pan concentrates shows a better anomaly than any hydromorphic Pb component. ?? 1981.

Theoretical Investigation of Calculating Temperatures in the Combining Zone of Cu/Fe Composite Plate Jointed by Explosive Welding

NASA Astrophysics Data System (ADS)

Qu, Y. D.; Zhang, W. J.; Kong, X. Q.; Zhao, X.

2016-03-01

The heat-transfer behavior of the interface of Flyer plate (or Base Plate) has great influence on the microcosmic structures, stress distributions, and interface distortion of the welded interface of composite plates by explosive welding. In this paper, the temperature distributions in the combing zone are studied for the case of Cu/Fe composite plate jointed by explosive welding near the lower limit of explosive welding. The results show that Flyer plate (Cu plate) and Base Plate (Fe plate) firstly almost have the same melting rate in the explosive welding process. Then, the melting rate of Cu plate becomes higher than that of Fe plate. Finally, the melt thicknesses of Cu plate and Fe plate trend to be different constants, respectively. Meanwhile, the melting layer of Cu plate is thicker than that of Fe plate. The research could supply some theoretical foundations for calculating the temperature distribution and optimizing the explosive welding parameters of Cu/Fe composite plate to some extent.

Moessbauer spectra of ferrite catalysts used in oxidative dehydrogenation

NASA Technical Reports Server (NTRS)

Cares, W. R.; Hightower, J. W.

1971-01-01

Room temperature Mossbauer spectroscopy was used to examine bulk changes which occur in low surface area CoFe2O4 and CuFe2O4 catalysts as a result of contact with various mixtures of trans-2-butene and O2 during oxidative dehydrogenation reactions at about 420 C. So long as there was at least some O2 in the gas phase, the CoFe2O4 spectrum was essentially unchanged. However, the spectrum changed from a random spinel in the oxidized state to an inverse spinel as it was reduced by oxide ion removal. The steady state catalyst lies very near the fully oxidized state. More dramatic solid state changes occurred as the CuFe2O4 underwent reduction. Under severe reduction, the ferrite was transformed into Cu and Fe3O4, but it could be reversibly recovered by oxidation. An intense doublet located near zero velocity persisted in all spectra of CuFe2O4 regardless of the state of reduction.

Fabrication and photocatalytic property of magnetic NiFe2O4/Cu2O composites

NASA Astrophysics Data System (ADS)

He, Zuming; Xia, Yongmei; Tang, Bin; Su, Jiangbin

2017-09-01

Magnetically separable NiFe2O4/Cu2O composites were successfully synthesized by a two-step method. The samples were characterized by XRD, XPS, SEM and VSM as well as their PL spectra and UV-vis adsorption spectra. The results showed that the NiFe2O4/Cu2O composites were composed of cubic-structured Cu2O and spinel-structured NiFe2O4, were able to absorb a large amount of visible light, exhibited excellent photocatalytic activity under simulated solar light irradiation and could be easily separated by an external magnetic field. The NiFe2O4/Cu2O composites exhibited higher photocatalytic performance than that of a single semiconductor. It was found that the prominently enhanced photocatalytic performance of NiFe2O4/Cu2O composites was ascribed to the effective separation of photo-generated electron-hole pairs and the effective generation of the hydroxyl radical •OH.

Anode-supported single-chamber solid oxide fuel cell based on cobalt-free composite cathode of Nd0.5Sr0.5Fe0.8Cu0.2O3-δ-Sm0.2Ce0.8O1.9 at intermediate temperatures

NASA Astrophysics Data System (ADS)

Yin, Jie-Wei; Zhang, Chunming; Yin, Yi-Mei; Shi, Huangang; Lin, Ye; Lu, Jun; Ma, Zi-Feng

2015-07-01

As a candidate of cathode material of single-chamber solid oxide fuel cell (SC-SOFC), cobalt-free mixed ionic electronic conductor (MIEC) Nd0.5Sr0.5Fe0.8Cu0.2O3-δ (NSFCu) is synthesized by sol-gel method with ethylene diamine tetraacetic acid and citric acid as co-complexing agents. The XRD shows NSFCu is stable after CO2 treatment and chemical compatible with SDC at high temperatures. CO2-TPD (CO2-temperature programmed desorption) demonstrates both CO2 adsorption and desorption phenomenon on NSFCu surface. However, the polarization resistances (Rp) of NSFCu and SDC (10:4 in weight) composite electrodes showed no decay in 5% CO2. Single cell using N2-O2-CH4 mixed gas (CH4 to O2 ratio = 1.5) as fuel shows maximum power density of 635 mW cm-2 at 700 °C. These results suggest that NSFCu-SDC is a promising composite cathode material for application in single-chamber solid oxide fuel cell.

Microstructure and mechanical properties of aluminium matrix composites reinforced by Al{sub 62}Cu{sub 25.5}Fe{sub 12.5} melt spun ribbon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lityńska-Dobrzyńska, Lidia, E-mail: l.litynska@imim.pl; Mitka, Mikołaj; Góral, Anna

Aluminium matrix composites containing 15, 30 and 50 vol.% of pulverized Al{sub 62}Cu{sub 25.5}Fe{sub 12.5} (in at.%) melt spun ribbons have been prepared by a vacuum hot pressing (T = 673 K, P = 600 MPa). The microstructure of the initial ribbon and the composites was investigated using X-ray, scanning and transmission electron microscopy. In the as-spun ribbon the quasicrystalline icosahedral phase (i-phase) coexisted with the cubic copper rich β-Al(Cu, Fe) intermetallic compound. The phase composition of Al-Cu-Fe particles changed after consolidation process and the i-phase transformed partially to the ω-Al{sub 70}Cu{sub 20}Fe{sub 10} phase. Additionally, the Θ-Al{sub 2}Cu phasemore » formed at the α(Al)/Al-Cu-Fe particle interfaces. With an increase in volume fraction of the reinforcement the hardness of the composites increased up to HV = 180 for the highest amount of added particles. The ultimate compression strength of the same sample reached the value of 545 MPa. - Highlights: • Al and 15, 30, 50% of pulverized Al{sub 62}Cu{sub 25.5}Fe{sub 12.5} melt spun ribbon were consolidated. • The initial ribbon consisted of the icosahedral i-phase and copper rich β-Al(Cu, Fe). • The i-phase partially transforms to ω-Al{sub 7}Cu{sub 2}Fe phase in all composites. • Increase of microhardness and compressive strength with content of reinforcement • Ultimate compression strength 545 MPa for 50% of added particles.« less

Reduction-oxidation Enabled Glass-ceramics to Stainless Steel Bonding Part II interfacial bonding analysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dai, Steve Xunhu

2015-09-01

Among glass-ceramic compositions modified with a variety of oxidants (AgO, FeO, NiO, PbO, SnO, CuO, CoO, MoO 3 and WO 3) only CuO and CoO doped glass-ceramics showed existence of bonding oxides through reduction-oxidation (redox) at the GC-SS interface. The CuO-modified glass-ceramics demonstrate the formation of a continuous layer of strong bonding Cr 2O 3 at the interface in low partial oxygen (PO 2) atmosphere. However, in a local reducing atmosphere, the CuO is preferentially reduced at the surface of glass-ceramic rather than the GC-SS interface for redox. The CoO-modified glass-ceramics demonstrate improved GC-SS bonding. But the low mobility ofmore » Co ++ ions in the GC limited the amount of CoO that can diffuse to and participate in redox at the interface.« less

Coupled Metal/Oxide Catalysts with Tunable Product Selectivity for Electrocatalytic CO2 Reduction.

PubMed

Huo, Shengjuan; Weng, Zhe; Wu, Zishan; Zhong, Yiren; Wu, Yueshen; Fang, Jianhui; Wang, Hailiang

2017-08-30

One major challenge to the electrochemical conversion of CO 2 to useful fuels and chemical products is the lack of efficient catalysts that can selectively direct the reaction to one desirable product and avoid the other possible side products. Making use of strong metal/oxide interactions has recently been demonstrated to be effective in enhancing electrocatalysis in the liquid phase. Here, we report one of the first systematic studies on composition-dependent influences of metal/oxide interactions on electrocatalytic CO 2 reduction, utilizing Cu/SnO x heterostructured nanoparticles supported on carbon nanotubes (CNTs) as a model catalyst system. By adjusting the Cu/Sn ratio in the catalyst material structure, we can tune the products of the CO 2 electrocatalytic reduction reaction from hydrocarbon-favorable to CO-selective to formic acid-dominant. In the Cu-rich regime, SnO x dramatically alters the catalytic behavior of Cu. The Cu/SnO x -CNT catalyst containing 6.2% of SnO x converts CO 2 to CO with a high faradaic efficiency (FE) of 89% and a j CO of 11.3 mA·cm -2 at -0.99 V versus reversible hydrogen electrode, in stark contrast to the Cu-CNT catalyst on which ethylene and methane are the main products for CO 2 reduction. In the Sn-rich regime, Cu modifies the catalytic properties of SnO x . The Cu/SnO x -CNT catalyst containing 30.2% of SnO x reduces CO 2 to formic acid with an FE of 77% and a j HCOOH of 4.0 mA·cm -2 at -0.99 V, outperforming the SnO x -CNT catalyst which only converts CO 2 to formic acid in an FE of 48%.

Physical properties of spin-valve films grown on naturally oxidized metal nano-oxide surfaces

NASA Astrophysics Data System (ADS)

Mao, Ming; Cerjan, Charlie; Kools, Jacques

2002-05-01

The physical properties of spin-valve films NiFe 25 Å/CoFe 10 Å/Cu(tCu)/CoFe 30 Å/IrMn 70 Å/Ta 20 Å with graded Cu layer thickness (tCu=18-45 Å) grown on the surface of metal nano-oxide layers (NOLs) were studied. The NOLs were formed from ultrathin Al, Cr, Cu, Nb, Ta, CoFe, NiFe, and NiFeCr layers by natural oxidation. The growth of the spin-valve films on NOLs has led to an enhancement in giant magnetoresistance value by up to 48%. A corresponding reduction in minimum film resistance by over 10% confirms that this enhancement originates from an increase in the mean free path of spin-polarized electrons due to the resultant specular reflection at the nano-oxide surfaces. A wide spectrum of oscillatory interlayer exchange coupling dependence on tCu for these NOL-bearing films suggests that a specular nano-oxide surface does not necessarily result in a smoother multilayer structure. The observation of an enhanced exchange biasing among these spin-valve films appears in contradiction to the observed deterioration of their crystallographic quality. As an important application, TaOx, CrOx, and NbOx could be employed as an alternative to AlOx as the barrier layer for magnetic tunnel junctions.

Biomineral microstructures in ferromanganese nodules: evidence of the biological and abiogenous origin

NASA Astrophysics Data System (ADS)

Lysyuk, G. N.

2011-10-01

Manganese oxides, which are widespread and of great practical importance, are formed and transformed by the active role of microorganisms. Manganese aggregates occur as both crystallized varieties and disordered fine-grained phases with significant ore grade and up to 50-60 vol % of X-ray amorphous components. X-ray amorphous nanosizedMn oxides in Fe-Mn nodules from the Pacific Ocean floor were examined from the standpoint of their biogenic origin. SEM examination showed abundant mineralized biofilms on the studied samples. The chemical composition of bacterial mass is as follows (wt %): 28.34 MnO, 17.14 Fe2O3, 7.11 SiO2, 2.41 CaO, 17.90 TiO2, 1.74Na2O,1.73 A12O3,1.30 MgO, 1.25P2O5,1.25 SO3,0.68 CoO, 0.54 CuO, 0.53 NiO, and 0.50 K2O. The chemical composition of fossilized cyanobacterial mats within the interlayer space of nodules is as follows (wt %): 48.35 MnO, 6.23 Fe2O3, 8.76 MgO, 5.05 A12O3, 4.45 SiO2, 3.63 NiO, 2.30 Na2O, 2.19 CuO, 1.31 CaO, and 0.68 K2O is direct evidence for participation of bacteria in Mn oxide formation. This phase consists of mineralized glycocalix consisting of nanosized flakes of todorokite. Native metals (Cu, Fe, and Zn) as inclusions 10-20 μm in size were identified in ferromanganese nodules as well. The formation of native metals can be explained by their crystallization at highly reducing conditions maintained by organic matter.

Nanostructured iron(III)-copper(II) binary oxide: a novel adsorbent for enhanced arsenic removal from aqueous solutions.

PubMed

Zhang, Gaosheng; Ren, Zongming; Zhang, Xiwang; Chen, Jing

2013-08-01

To obtain a highly efficient and low-cost adsorbent for arsenic removal from water, a novel nanostructured Fe-Cu binary oxide was synthesized via a facile co-precipitation method. Various techniques including BET surface area measurement, powder XRD, SEM, and XPS were used to characterize the synthetic Fe-Cu binary oxide. It showed that the oxide was poorly crystalline, 2-line ferrihydrite-like and was aggregated with many nanosized particles. Laboratory experiments were performed to investigate adsorption kinetics, adsorption isotherms, pH adsorption edge and regeneration of spent adsorbent. The results indicated that the Fe-Cu binary oxide with a Cu: Fe molar ratio of 1:2 had excellent performance in removing both As(V) and As(III) from water, and the maximal adsorption capacities for As(V) and As(III) were 82.7 and 122.3 mg/g at pH 7.0, respectively. The values are favorable, compared to those reported in the literature using other adsorbents. The coexisting sulfate and carbonate had no significant effect on arsenic removal. However, the presence of phosphate obviously inhibited the arsenic removal, especially at high concentrations. Moreover, the Fe-Cu binary oxide could be readily regenerated using NaOH solution and be repeatedly used. The Fe-Cu binary oxide could be a promising adsorbent for both As(V) and As(III) removal because of its excellent performance, facile and low-cost synthesis process, and easy regeneration. Copyright © 2013 Elsevier Ltd. All rights reserved.

Composite CuFe1 - xSnxO2/p-type silicon photodiodes

NASA Astrophysics Data System (ADS)

Al-Sehemi, Abdullah G.; Mensah-Darkwa, K.; Al-Ghamdi, Ahmed A.; Soylu, M.; Gupta, R. K.; Yakuphanoglu, F.

2017-06-01

CuFe1 - xSnxO2 composite thin film/p-type silicon diodes were prepared on substrate by sol-gel method (x = 0.00, 0.01, 0.03, 0.05, 0.07). The structure of CuFe1 - xSnxO2 composite thin films was studied using XRD analysis and films exhibited amorphous behavior. The elemental compositions and surface morphology of the films were characterized using SEM and EDX. EDX results confirmed the presence of the compositional elements. The optical band gap of CuFe1 - xSnxO2 composite thin films was determined using the optic spectra. The optical band gaps of the CuFe1 - xSnxO2 composite thin films were calculated using optical data and were found to be 3.75, 3.78, 3.80, 3.85 and 3.83 eV for x = 0.00, 0.01, 0.03, 0.05 and 0.07, respectively. The photoresponse and electrical properties of the Al/CuFe1 - xSnxO2/p-Si/Al diode were studied. The barrier height and ideality factor were determined to be averagely 0.67 eV and 2.6, respectively. The electrical and photoresponse characteristics of the diodes have been investigated under dark and solar light illuminations, respectively. The interface states were used to explain the results obtained in present study. CuFe1 - xSnxO2 photodiodes exhibited a high photoresponsivity to be used in optoelectronic applications.

Oxidation behaviour of zirconium alloys and their precipitates - A mechanistic study

NASA Astrophysics Data System (ADS)

Proff, C.; Abolhassani, S.; Lemaignan, C.

2013-01-01

The precipitate oxidation behaviour of binary zirconium alloys containing 1 wt.% Fe, Ni, Cr or 0.6 wt.% Nb was characterised in TEM on FIB prepared transverse sections of the oxide and reported in previous studies [1,2]. In the present study the following alloys: Zr1%Cu, Zr0.5%Cu0.5%Mo and pure Zr are analysed to add to the available information. In all cases, the observed precipitate oxidation behaviour in the oxide close to the metal-oxide interface could be described either with delayed oxidation with respect to the matrix or simultaneous oxidation as the surrounding zirconium matrix. Attempt was made to explain these observations, with different parameters such as precipitate size and structure, composition and thermodynamic properties. It was concluded that the thermodynamics with the new approach presented could explain most precisely their behaviour, considering the precipitate stoichiometry and the free energy of oxidation of the constituting elements. The surface topography of the oxidised materials, as well as the microstructure of the oxide presenting microcracks have been examined. A systematic presence of microcracks above the precipitates exhibiting delayed oxidation has been found; the height of these crack calculated using the Pilling-Bedworth ratios of different phases present, can explain their origin. The protrusions at the surface in the case of materials containing large precipitates can be unambiguously correlated to the presence of these latter, and the height can be correlated to the Pilling-Bedworth ratios of the phases present as well as the diffusion of the alloying elements to the surface and their subsequent oxidation. This latter behaviour was much more considerable in the case of Fe and Cu with Fe showing systematically diffusion to the outer surface.

Fe(II)/Cu(II) interaction on goethite stimulated by an iron-reducing bacteria Aeromonas Hydrophila HS01 under anaerobic conditions.

PubMed

Tao, Liang; Zhu, Zhen-Ke; Li, Fang-Bai; Wang, Shan-Li

2017-11-01

Copper is a trace element essential for living creatures, but copper content in soil should be controlled, as it is toxic. The physical-chemical-biological features of Cu in soil have a significant correlation with the Fe(II)/Cu(II) interaction in soil. Of significant interest to the current study is the effect of Fe(II)/Cu(II) interaction conducted on goethite under anaerobic conditions stimulated by HS01 (a dissimilatory iron reduction (DIR) microbial). The following four treatments were designed: HS01 with α-FeOOH and Cu(II) (T1), HS01 with α-FeOOH (T2), HS01 with Cu(II) (T3), and α-FeOOH with Cu(II) (T4). HS01 presents a negligible impact on copper species transformation (T3), whereas the presence of α-FeOOH significantly enhanced copper aging contributing to the DIR effect (T1). Moreover, the violent reaction between adsorbed Fe(II) and Cu(II) leads to the decreased concentration of the active Fe(II) species (T1), further inhibiting reactions between Fe(II) and iron (hydr)oxides and decelerating the phase transformation of iron (hydr)oxides (T1). From this study, the effects of the Fe(II)/Cu(II) interaction on goethite under anaerobic conditions by HS01 are presented in three aspects: (1) the accelerating effect of copper aging, (2) the reductive transformation of copper, and (3) the inhibition effect of the phase transformation of iron (hydr)oxides. Copyright © 2017 Elsevier Ltd. All rights reserved.

Characterization of copper oxides, iron oxides, and zinc copper ferrite desulfurization sorbents by X-ray photoelectron spectroscopy and scanning electron microscopy

NASA Astrophysics Data System (ADS)

Siriwardane, Ranjani V.; Poston, James A.

1993-05-01

Characterization of copper oxides, iron oxides, and zinc copper ferrite desulfurization sorbents was performed by X-ray photoelectron spectroscopy and scanning electron microscopy/energy-dispersive spectroscopy at temperatures of 298 to 823 K. Analysis of copper oxides indicated that the satellite structure of the Cu22p region was absent in the Cu(I) state but was present in the Cu(II) state. Reduction of CuO at room temperature was observed when the ion gauge was placed close to the sample. The satellite structure was absent in all the copper oxides at 823 K in vacuum. Differentiation of the oxidation state of copper utilizing both Cu(L 3M 4,5M 4,5) X-ray-induced Auger lines and Cu2p satellite structure, indicated that the copper in zinc copper ferrite was in the + 1 oxidation state at 823 K. This + 1 state of copper was not significantly changed after exposure to H 2, CO, and H 2O. There was an increase in Cu/Zn ratio and a decrease in Fe/Zn ratio on the surface of zinc copper ferrite at 823 K compared to that at room temperature. These conditions of copper offered the best sulfidation equilibrium for the zinc copper ferrite desulfurization sorbent. Analysis of iron oxides indicated that there was some reduction of both Fe 2O 3 and FeO at 823K. The iron in zinc copper ferrite was similar to that of Fe 2O 3 at room temperature but there was some reduction of this Fe(III) state to Fe(II) at 823 K. This reduction was more enhanced in the presence of H 2 and CO. Reduction to Fe(II) may not be desirable for the lifetime of the sorbent.

The oxidation state, and sulfur and Cu contents of arc magmas: implications for metallogeny

NASA Astrophysics Data System (ADS)

Richards, Jeremy P.

2015-09-01

Global data for measured Fe2O3/FeO ratios and Cu contents in unaltered volcanic and intrusive arc rocks indicate that, on average, they are slightly more oxidized than other magmas derived from depleted upper mantle (such as MORB), but contain similar Cu contents across their compositional ranges. Although Cu scatters to elevated values in some intermediate composition samples, the bulk of the data show a steady but gentle trend to lower concentrations with differentiation, reaching modal values of 50-100 ppm in andesitic rocks. These data suggest that Cu is mildly compatible during partial melting and fractionation processes, likely reflecting minor degrees of sulfide saturation throughout the magmatic cycle. However, the volume of sulfides must be small such that significant proportions of the metal content remain in the magma during fractionation to intermediate compositions. Previous studies have shown that andesitic magmas containing 50 ppm Cu can readily form large porphyry-type Cu deposits upon emplacement in the upper crust. A review of the literature suggests that the elevated oxidation state in the asthenospheric mantle wedge source of arc magmas (ΔFMQ ≈ + 1 ± 1) derives from the subduction of seawater-altered and oxidized oceanic crust, and is transmitted into the mantle wedge via prograde metamorphic dehydration fluids carrying sulfate and other oxidizing components. Progressive hydration and oxidation of the mantle wedge may take up to 10 m.y. to reach a steady state from the onset of subduction, explaining the rarity of porphyry deposits in primitive island arcs, and the late formation of porphyries in continental arc magmatic cycles. Magmas generated from this metasomatized and moderately oxidized mantle source will be hydrous basalts containing high concentrations of sulfur, mainly dissolved as sulfate or sulfite. Some condensed sulfides (melt or minerals) may be present due to the high overall fS2, despite the moderately high oxidation state. These sulfides may retain some highly siderophile elements in the source, but are unlikely to be sufficiently voluminous to significantly affect the budget of more modestly sulfide-compatible and more abundant elements such as Cu and Mo. These primary magmas can therefore be considered to be largely Cu-Mo-undepleted, although highly siderophile elements such as Au and platinum group elements (PGE) may be depleted unless no sulfides remain in the source. The latter condition seems unlikely during active subduction because of the continuous flux of fresh sulfur from the slab, but may occur during post-subduction re-melting (leading to potentially Au-rich post-subduction porphyry and alkalic-type epithermal systems). Lower crustal differentiation of main-stage arc magmas results in some loss of Cu to residual or cumulate sulfides, but again the amount appears to be minor, and does not drastically reduce the Cu content of derivative intermediate-composition melts. Fractionation and devolatilization affect the oxidation state of the magma in competing ways, but, while crystallization and segregation of Fe3 +-rich magnetite can cause reduction in reduced to moderately oxidized evolved magmas, this effect appears to be outweighed by the oxidative effects of degassing reduced or weakly oxidized gaseous species such as H2, H2S, and SIVO2, and preferential solvation and removal of Fe2 + in saline hydrothermal fluids. Consequently, most arc magmatic suites show slight increases in oxidation state during differentiation, reaching typical values of ΔFMQ = + 1 to + 2. This oxidation state is significant, because it corresponds to the transition from dissolved sulfide to sulfate dominance in magmas. It has been shown that Cu and Au solubilities in silicate magma increase up to this level (ΔFMQ ≈ + 1), but while Cu solubility continues to increase at higher oxidation states, Au shows a precipitous drop as sulfide, which solvates Au in the melt, is converted to sulfate. This may explain the somewhat restricted distribution of Au-rich porphyry Cu deposits, but the general association of porphyry Cu deposits with relatively oxidized magmas. Exsolution of a saline, high temperature aqueous fluid enables metals to partition from the magma into a highly mobile volatile phase. Sulfur also partitions strongly into this fluid phase, predominantly as SO2 at ΔFMQ = + 1 to + 2. However, as the fluid cools below 400 °C, SIVO2 disproportionates to form reduced H2S- II and oxidized H2SVIO4. The H2S bonds with metals in solution to precipitate as Cu- and Mo-sulfides, while the H2SO4 (and HCl) generates progressively acidic wallrock alteration (phyllic, argillic, advanced argillic). Gold may precipitate with early Cu/Mo-sulfides, but some may also stay in solution as bisulfide complexes, eventually reaching the epithermal environment. Thus, three components, [S], [H2O], and fO2 work together throughout subduction and arc magmatic processes to transport chalcophile and siderophile metals from the mantle into the upper crust, where they may be concentrated by hydrothermal processes to form ore deposits. These processes are far from 100% efficient, and metals (especially highly siderophile elements such as Au and PGE) may be left behind at various stages of the passage of arc magmas through the lithosphere, where they may form potentially metalliferous source rocks for partial melts and subsequent magmatic-hydrothermal ore deposits generated during later tectonomagmatic events.

Copper and cobalt mobility in soil and accumulation in a metallophyte as influenced by experimental manipulation of soil chemical factors.

PubMed

Lange, Bastien; Pourret, Olivier; Meerts, Pierre; Jitaru, Petru; Cancès, Benjamin; Grison, Claude; Faucon, Michel-Pierre

2016-03-01

The influence of Fe oxides, Mn oxides and organic matter (OM) on the Cu and Co mobility in soil and accumulation in the metallophyte Anisopappus chinensis (Ac), as compared with Helianthus annuus (Ha), was experimentally investigated. Growth and accumulation response when increasing the exchangeable Cu and Co concentrations in soil were also investigated. Plants were cultivated on soil where concentrations of Cu, Co, Fe oxides, Mn oxides and OM content were varied according to 36 treatments. The OM supply decreased the Cu mobility and increased the Co mobility, resulting in decreasing the foliar Cu of Ac and increasing the foliar Co of Ha. The Fe oxides supply could increase the Cu accumulation for Ac, but was not verified for Ha. Compared with Ha, Ac increasingly accumulated Cu and Co without negative effect on plant growth while increasing Cu and Co mobility to phytotoxic concentrations. The results revealed promising perspectives for the use of Ac in Cu-contaminated environment phytoremediation applications. Copyright © 2015 Elsevier Ltd. All rights reserved.

Reaction Mechanisms of Metals with Hydrogen Sulfide and Thiols in Model Wine. Part 2: Iron- and Copper-Catalyzed Oxidation.

PubMed

Kreitman, Gal Y; Danilewicz, John C; Jeffery, David W; Elias, Ryan J

2016-05-25

Sulfidic off-odors arising during wine production are frequently removed by Cu(II) fining. In part 1 of this study ( 10.1021/acs.jafc.6b00641 ), the reaction of H2S and thiols with Cu(II) was examined; however, the interaction of iron and copper is also known to play an important synergistic role in mediating non-enzymatic wine oxidation. The interaction of these two metals in the oxidation of H2S and thiols (cysteine, 3-sulfanylhexan-1-ol, and 6-sulfanylhexan-1-ol) was therefore examined under wine-like conditions. H2S and thiols (300 μM) were reacted with Fe(III) (100 or 200 μM) alone and in combination with Cu(II) (25 or 50 μM), and concentrations of H2S and thiols, oxygen, and acetaldehyde were monitored over time. H2S and thiols were shown to be slowly oxidized in the presence of Fe(III) alone and were not bound to Fe(III) under model wine conditions. However, Cu(II) added to model wine containing Fe(III) was quickly reduced by H2S and thiols to form Cu(I) complexes, which then rapidly reduced Fe(III) to Fe(II). Oxidation of Fe(II) in the presence of oxygen regenerated Fe(III) and completed the iron redox cycle. In addition, sulfur-derived oxidation products were observed, and the formation of organic polysulfanes was demonstrated.

Inert anode containing oxides of nickel iron and cobalt useful for the electrolytic production of metals

DOEpatents

Ray, Siba P.; Liu, Xinghua; Weirauch, Jr., Douglas A.

2002-01-01

An inert anode for the electrolytic production of metals such as aluminum is disclosed. The inert anode includes a ceramic oxide material preferably made from NiO, Fe.sub.2 O.sub.3 and CoO. The inert anode composition may comprise the following mole fractions of NiO, Fe.sub.2 O.sub.3 and CoO: 0.15 to 0.99 NiO; 0.0001 to 0.85 Fe.sub.2 O.sub.3 ; and 0.0001 to 0.45 CoO. The inert anode may optionally include other oxides and/or at least one metal phase, such as Cu, Ag, Pd, Pt, Au, Rh, Ru, Ir and/or Os. The Ni--Fe--Co--O ceramic material exhibits very low solubility in Hall cell baths used to produce aluminum.

Inert anode containing oxides of nickel, iron and zinc useful for the electrolytic production of metals

DOEpatents

Ray, Siba P.; Weirauch, Jr., Douglas A.; Liu, Xinghua

2002-01-01

An inert anode for the electrolytic production of metals such as aluminum is disclosed. The inert anode includes a ceramic oxide material preferably made from NiO, Fe.sub.2 O.sub.3 and ZnO. The inert anode composition may comprise the following mole fractions of NiO, Fe.sub.2 O.sub.3 and ZnO: 0.2 to 0.99 NiO; 0.0001 to 0.8 Fe.sub.2 O.sub.3 ; and 0.0001 to 0.3 ZnO. The inert anode may optionally include other oxides and/or at least one metal phase, such as Cu, Ag, Pd, Pt, Au, Rh, Ru, Ir and/or Os. The Ni--Fe--Co--O ceramic material exhibits very low solubility in Hall cell baths used to produce aluminum.

Origin and fate of sulfide liquids in hotspot volcanism (La Réunion): Pb isotope constraints from residual Fe-Cu oxides

NASA Astrophysics Data System (ADS)

Vlastélic, I.; Gannoun, A.; Di Muro, A.; Gurioli, L.; Bachèlery, P.; Henot, J. M.

2016-12-01

Immiscible sulfide liquids in basaltic magmas play an important role in trace metal transport and the sulfur budget of volcanic eruptions. However, sulfides are transient phases, whose origin and fate are poorly constrained. We address these issues by analyzing sulfide destabilization products preserved in lavas from La Réunion Island. Iron oxide globules and coatings, typically 20-80 μm in size, were found to occur in vesicles of differentiated lavas from Piton des Neiges, and recent pumice samples from Piton de la Fournaise. Field and mineralogical evidence indicates that the iron oxides are syn-eruptive phases not resulting from hydrothermal processes. Samples were first studied by Scanning Electron Microscopy. The globules were separated, whereas the smaller spherules and coatings were concentrated by magnetic sorting and acid leaching, and samples were processed through wet chemistry. The Fe oxide phases comprise 49-74 wt.% Fe, 26-40 wt.% O, and up to 6 wt.% Cu, 811 ppm Ni, 140 ppm Bi, and 8.5 ppm Pb. Compared to the host lava, Cu, Ni, and Bi are enriched by a factor of 101-103. Systematic Pb isotope disequilibrium (between 500 ppm and 2.9% for 206Pb/204Pb) exists between Fe oxides and host rocks, with Fe oxides generally displaying less radiogenic ratios. Unradiogenic Pb is a typical signature of sulfide, which tends to concentrate Pb, but not its parent elements U and Th. Thus, both the chemical and isotopic compositions of the vesicle-hosted Fe oxides suggest that they are more or less direct products of the destabilization of immiscible sulfide liquids. Although Pb dominantly partitions into the gas phase during sulfide breakdown, the original Pb isotope signature of sulfide is preserved in the residual oxide. The composition estimated for the parent sulfides (206Pb/204Pb = 18.20-18.77, 207Pb/204Pb = 15.575, and 208Pb/204Pb = 38.2-38.8) precludes a genetic link with the La Réunion plume, and suggests a lithospheric or crustal origin. It is estimated that magma ascent velocities at Piton de la Fournaise are high enough to counterbalance the settling velocities of millimeter-size sulfides. Despite their high density, sulfide liquids are thus transferred upward during eruptions and their destabilization contributes to SO2 emanations. Assimilation of foreign sulfides from the lithosphere can explain why SO2 emissions sometimes (e.g., during the April 2007 eruption) exceed those predicted from the S content of melt inclusions.

Band gap tuning in transition metal oxides by site-specific substitution

DOEpatents

Lee, Ho Nyung; Chisholm, Jr., Matthew F; Jellison, Jr., Gerald Earle; Singh, David J; Choi, Woo Seok

2013-12-24

A transition metal oxide insulator composition having a tuned band gap includes a transition metal oxide having a perovskite or a perovskite-like crystalline structure. The transition metal oxide includes at least one first element selected form the group of Bi, Ca, Ba, Sr, Li, Na, Mg, K, Pb, and Pr; and at least one second element selected from the group of Ti, Al, V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Nb, Mo, Ru, Rh, Hf, Ta, W, Re, Os, Ir, and Pt. At least one correlated insulator is integrated into the crystalline structure, including REMO.sub.3, wherein RE is at least one Rare Earth element, and wherein M is at least one element selected from the group of Co, V, Cr, Ni, Mn, and Fe. The composition is characterized by a band gap of less of 4.5 eV.

Preparation and study of (1 - x)CuFe2O4-xBaTiO3 (x = 0, 0.1 and 1) composite multiferroics

NASA Astrophysics Data System (ADS)

Murtaza, Tahir; Ali, Javid; Khan, M. S.

2018-07-01

The parent and mixed spinel-perovskite composite of (1 - x)CuFe2O4-xBaTiO3 (x = 0, 0.1 and 1) has been prepared by solid-state reaction method and studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), Mössbauer spectroscopy, magnetometry and P-E lope tracer. The XRD results showed the formation of single phase tetragonal spinel CuFe2O4 and tetragonal perovskite BaTiO3 at room temperature, further XRD of composite 0.1CuFe2O4-0.9BaTiO3 reflects the two crystallographic phases with 1:9 ratio. The SEM micrographs show the homogeneous and uniform formation of the samples. Through EDAX analysis, the chemical composition of the sample is found to be same as the nominal composition. The high field Mossbauer data of CuFe2O4 sample shows the ferrimagnetic ordering in the sample. The observed M-H and P-E loops of the composite 0.1CuFe2O4-0.9BaTiO3 sample show the presence of spontaneous magnetization and spontaneous electric polarization indicating the multiferroic nature of the sample.

Copper(II) sorption onto goethite, hematite and lepidocrocite: a surface complexation model based on ab initio molecular geometries and EXAFS spectroscopy

NASA Astrophysics Data System (ADS)

Peacock, Caroline L.; Sherman, David M.

2004-06-01

We measured the adsorption of Cu(II) onto goethite (α-FeOOH), hematite (α-Fe 2O 3) and lepidocrocite (γ-FeOOH) from pH 2-7. EXAFS spectra show that Cu(II) adsorbs as (CuO 4H n) n-6 and binuclear (Cu 2O 6H n) n-8 complexes. These form inner-sphere complexes with the iron (hydr)oxide surfaces by corner-sharing with two or three edge-sharing Fe(O,OH) 6 polyhedra. Our interpretation of the EXAFS data is supported by ab initio (density functional theory) geometries of analogue Fe 2(OH) 2(H 2O) 8Cu(OH) 4and Fe 3(OH) 4(H 2O) 10Cu 2(OH) 6 clusters. We find no evidence for surface complexes resulting from either monodentate corner-sharing or bidentate edge-sharing between (CuO 4H n) n-6 and Fe(O,OH) 6 polyhedra. Sorption isotherms and EXAFS spectra show that surface precipitates have not formed even though we are supersaturated with respect to CuO and Cu(OH) 2. Having identified the bidentate (FeOH) 2Cu(OH) 20 and tridentate (Fe 3O(OH) 2)Cu 2(OH) 30 surface complexes, we are able to fit the experimental copper(II) adsorption data to the reactions 3( FeOH)+2 Cu2++3 H2O=( Fe3O( OH) 2) Cu2( OH) 30+4 H+ and 2( FeOH)+ Cu2++2 H2O=( FeOH) 2Cu( OH) 20+2 H+. The two stability constants are similar for the three iron (hydr)oxide phases investigated.

The metal oxide fraction of pelagic sediment in the equatorial North Pacific Ocean: A source of metals in ferromanganese nodules

USGS Publications Warehouse

Piper, D.Z.

1988-01-01

Pelagic sediment recovered at DOMES Site A in the equatorial North Pacific (151??W, 9?? 15???N) consists of a surface homogeneous layer, approximately 10 cm thick, overlying a strongly mottled layer that is lighter in color. The radiolarian composition of both units is Quaternary. In areas where this sediment was only a few centimeters thick, the underlying sediment was early Tertiary. Clay mineralogy and major oxide composition of the two Quaternary sediments are uniform. Their similarity to continental shale suggests that the sediment has a terrigenous source. Clay mineralogy and major oxide composition of the Tertiary sediment also are uniform, although they differ markedly from the Quarternary sediment. In contrast to the major oxides, concentrations of Mn, Co, Cu, and Ni soluble in hydroxylamine hydrochlorideacetic acid are strongly different in the surface and subsurface Quaternary sediment. Mn and Ni exhibit pronounced depletions in the subsurface sediment, Ni slightly more than Mn. Cu is also depleted in the subsurface sediment, but less than Mn. It is also depleted in the subsurface Tertiary sediment, whereas the Mn concentration remains high. Concentration of Co relative to Mn increases into the subsurface Quaternary sediment to a constant Co:Mn ratio of 3 ?? 10-2. The trivalent REE (the REE exclusive of Ce) and Fe exhibit little down-core variation. Distribution of elements in these sediments is closely related to their concentration in associated surface ferromanganese nodules. The nodules are of two distinct types: those from the area where the Quaternary sediment is relatively thick have ??-MnO2 as the dominant manganese mineral. The ratios of Ni:Mn, Cu:Mn, and Fe:Mn in these nodules approximate the corresponding ratios of the soluble fraction of surface sediment. Todorokite is the dominant mineral of nodules recovered from areas where the Quaternary sediment is thin. Relatively high Cu/Mn, Ni/Mn, and low Fe/Mn ratios of these nodules mirror differences between the soluble fraction of surface and subsurface Quaternary sediment. These compositional trends of sediment and nodules at DOMES Site A reflect a diagenetic origin for the todorokite nodules and a predominantly hydrogenous origin for the ??-MnO2 nodules. ?? 1988.

Understanding Cu release into environment from Kure massive sulfide ore deposits, Kastamonu, NW Turkey

NASA Astrophysics Data System (ADS)

Demirel, Cansu; Sonmez, Seref; Balci, Nurgul

2014-05-01

Covering a wide range on the earth's crust, oxidation of metal sulfide minerals have vital environmental impacts on the aquatic environment, causing one of the major environmental problems known as acid mine drainage (AMD). Located in the Kastamonu province of the Western Black Sea region, Kure district is one of the major copper mining sites in Turkey. Mining activities in the area heads back to ancient times, such that operation is thought to be started with the Roman Empire. Currently, only the underground mining tunnels of Bakibaba and Asikoy are being operated. Thus, mining heaps and ores of those pyritic deposits have been exposed to the oxidative conditions for so long. As a result of weathering processes of past and recent heaps of the Kure volcanic massive sulfide deposits in addition to the main ore mineral (chalcopyrite), significant amount of metals, especially Cu, are being released into the environment creating undesirable environmental conditions. In order to elucidate Cu release mechanisms from Kure pyritic ore deposits and mining wastes, field and laboratory approaches were used. Surface water and sediment samples from the streams around the mining and waste sites were collected. Groundwater samples from the active underground mining site were also collected. Physical parameters (pH, Eh, T°C, and EC) of water samples were determined in situ and in the laboratory using probes (WTW pH 3110, WTW Multi 9310 and CRISON CM 35). Metal and ion concentrations of the water samples were analysed using ICP-MS and DR 2800 spectrophotometer, respectively. High Cu, Co, Zn and Fe concentrations were determined in the water samples with pH values ranging from 2.9- 4. Cu concentrions ranges from 345 ppm to 36 ppm in the water samples. Consistent with the water samples, high Cu, Fe, Zn and Co were also determined in the sediment samples. Laboratory chalcopyrite oxidation experiments under the conditions representing the field site were set up as biological and abiotic in order to elucidate Cu release from ore and wastes. Greater Cu release were measured from the biological experiments carried out with S and Fe oxidizers compared to those from the chemical experiments. Fe-oxide precipitation experiments carried out in the laboratory showed high Cu absorbtion into Fe-oxides produced by biological reactions carried out with Fe oxidizers. Overall, these preliminary experimental results showed that Cu release and migration from the source can be controlled by various microorganims which regulate S and Fe cycles in the field. Key words: Metal sulfide oxidation, Kure pyritic copper mines, AMD, Bioleaching, Secondary Fe-oxide precipitation

A perovskite oxide with high conductivities in both air and reducing atmosphere for use as electrode for solid oxide fuel cells.

PubMed

Lan, Rong; Cowin, Peter I; Sengodan, Sivaprakash; Tao, Shanwen

2016-08-22

Electrode materials which exhibit high conductivities in both oxidising and reducing atmospheres are in high demand for solid oxide fuel cells (SOFCs) and solid oxide electrolytic cells (SOECs). In this paper, we investigated Cu-doped SrFe0.9Nb0.1O3-δ finding that the primitive perovskite oxide SrFe0.8Cu0.1Nb0.1O3-δ (SFCN) exhibits a conductivity of 63 Scm(-1)and 60 Scm(-1) at 415 °C in air and 5%H2/Ar respectively. It is believed that the high conductivity in 5%H2/Ar is related to the exsolved Fe (or FeCu alloy) on exposure to a reducing atmosphere. To the best of our knowledge, the conductivity of SrFe0.8Cu0.1Nb0.1O3-δ in a reducing atmosphere is the highest of all reported oxides which also exhibit a high conductivity in air. Fuel cell performance using SrFe0.8Cu0.1Nb0.1O3-δ as the anode, (Y2O3)0.08(ZrO2)0.92 as the electrolyte and La0.8Sr0.2FeO3-δ as the cathode achieved a power density of 423 mWcm(-2) at 700 °C indicating that SFCN is a promising anode for SOFCs.

A perovskite oxide with high conductivities in both air and reducing atmosphere for use as electrode for solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Lan, Rong; Cowin, Peter I.; Sengodan, Sivaprakash; Tao, Shanwen

2016-08-01

Electrode materials which exhibit high conductivities in both oxidising and reducing atmospheres are in high demand for solid oxide fuel cells (SOFCs) and solid oxide electrolytic cells (SOECs). In this paper, we investigated Cu-doped SrFe0.9Nb0.1O3-δ finding that the primitive perovskite oxide SrFe0.8Cu0.1Nb0.1O3-δ (SFCN) exhibits a conductivity of 63 Scm-1and 60 Scm-1 at 415 °C in air and 5%H2/Ar respectively. It is believed that the high conductivity in 5%H2/Ar is related to the exsolved Fe (or FeCu alloy) on exposure to a reducing atmosphere. To the best of our knowledge, the conductivity of SrFe0.8Cu0.1Nb0.1O3-δ in a reducing atmosphere is the highest of all reported oxides which also exhibit a high conductivity in air. Fuel cell performance using SrFe0.8Cu0.1Nb0.1O3-δ as the anode, (Y2O3)0.08(ZrO2)0.92 as the electrolyte and La0.8Sr0.2FeO3-δ as the cathode achieved a power density of 423 mWcm-2 at 700 °C indicating that SFCN is a promising anode for SOFCs.

A perovskite oxide with high conductivities in both air and reducing atmosphere for use as electrode for solid oxide fuel cells

PubMed Central

Lan, Rong; Cowin, Peter I.; Sengodan, Sivaprakash; Tao, Shanwen

2016-01-01

Electrode materials which exhibit high conductivities in both oxidising and reducing atmospheres are in high demand for solid oxide fuel cells (SOFCs) and solid oxide electrolytic cells (SOECs). In this paper, we investigated Cu-doped SrFe0.9Nb0.1O3−δ finding that the primitive perovskite oxide SrFe0.8Cu0.1Nb0.1O3−δ (SFCN) exhibits a conductivity of 63 Scm−1and 60 Scm−1 at 415 °C in air and 5%H2/Ar respectively. It is believed that the high conductivity in 5%H2/Ar is related to the exsolved Fe (or FeCu alloy) on exposure to a reducing atmosphere. To the best of our knowledge, the conductivity of SrFe0.8Cu0.1Nb0.1O3−δ in a reducing atmosphere is the highest of all reported oxides which also exhibit a high conductivity in air. Fuel cell performance using SrFe0.8Cu0.1Nb0.1O3−δ as the anode, (Y2O3)0.08(ZrO2)0.92 as the electrolyte and La0.8Sr0.2FeO3−δ as the cathode achieved a power density of 423 mWcm−2 at 700 °C indicating that SFCN is a promising anode for SOFCs. PMID:27545200

Tennantite-tetrahedrite series from the Madan Pb-Zn deposits, Central Rhodopes, Bulgaria

NASA Astrophysics Data System (ADS)

Vassileva, Rossitsa D.; Atanassova, Radostina; Kouzmanov, Kalin

2014-08-01

Minerals from the tennantite-tetrahedrite series (fahlores) are found as single euhedral crystals and crustiform aggregates in hydrothermal veins of the Gradishte and Petrovitsa Pb-Zn deposits of the Madan ore field, southern Bulgaria. Unusually large compositional variations and fine oscillatory crystal zoning were investigated with electron microprobe analysis. The Gradishte samples correspond dominantly to tennantite, while Petrovitsa crystals have exclusively tetrahedrite composition. Fahlore compositions at Madan correspond to zincian varieties (1.6-1.95 apfu), with low Fe-content (<0.45 apfu). Minor silver is characteristic only for the Petrovitsa samples, reaching a maximum of 0.30 apfu. The (Cu+Ag) content of the Petrovitsa tennantites and the Cu content of the Gradishte tetrahedrites systematically exceed 10 apfu resulting in compensation of the excess Cu in the structure by Fe3+. Textural characteristics, mineral relationships and available fluid inclusion and stable isotope data suggest that fahlores precipitated in the late stages of mineralization at Madan, at temperature interval of 300-200 °C from oxidizing fluids with mixed (magmatic-meteoric) signatures.

The role of copper and oxalate in the redox cycling of iron in atmospheric waters

NASA Astrophysics Data System (ADS)

Sedlak, David L.; Hoigné, Jürg

During daytime, the redox cycling of dissolved iron compounds in atmospheric waters, and the related in-cloud transformations of photooxidants, are affected by reactions of Fe and Cu with hydroperoxy (HO 2) and superoxide (O 2-) radicals and the photoreduction of Fe(III)-oxalato complexes. We have investigated several of the important chemical reactions in this redox cycle, through laboratory simulation of the system, using γ-radiation to produce HO 2/O 2-. At concentrations comparable to those measured in atmospheric waters, the redox cycling of Fe was dramatically affected by the presence of oxalate and trace concentrations of Cu. At concentrations more than a hundred times lower than Fe, Cu consumed most of the HO 2/O 2-, and cycled between the Cu(II) and Cu(I) forms. Cu + reacted with FeOH 2+ to produce Fe(II) and Cu(II), with a second order rate constant of approximately 3 × 10 7 M -1s -1. The presence of oxalate resulted in the formation of Fe(III)-oxalato complexes that were essentially unreactive with HO 2/O 2-. Only at high oxalate concentrations was the Fe(II)C 2O 4 complex also formed, and it reacted relatively rapidly with hydrogen peroxide ( k = (3.1 ± 0.6) × 10 4 M -1s -1). Simulations incorporating measurements for other redox mechanisms, including oxidation by ozone, indicate that, during daytime, Fe should be found mostly in the ferrous oxidation state, and that reactions of FeOH 2+ with Cu(I) and HO 2/O 2-, and to a lesser degree, the photolysis of Fe(III)-oxalato complexes, are important mechanisms of Fe reduction in atmospheric waters. The catalytic effect of Cu(II)/Cu(I) and Fe(III)/Fe(II) should also significantly increase the sink function of the atmospheric liquid phase for HO 2 present in a cloud. A simple kinetic model for the reactions of Fe, Cu and HO 2/O 2-, accurately predicted the changes in Fe oxidation states that occurred when authentic fogwater samples were exposed to HO 2/O 2-.

Microstructural Characterization of Base Metal Alloys with Conductive Native Oxides for Electrical Contact Applications

NASA Astrophysics Data System (ADS)

Senturk, Bilge Seda

Metallic contacts are a ubiquitous method of connecting electrical and electronic components/systems. These contacts are usually fabricated from base metals because they are inexpensive, have high bulk electrical conductivities and exhibit excellent formability. Unfortunately, such base metals oxidize in air under ambient conditions, and the characteristics of the native oxide scales leads to contact resistances orders of magnitude higher than those for mating bare metal surface. This is a critical technological issue since the development of unacceptably high contact resistances over time is now by far the most common cause of failure in electrical/electronic devices and systems. To overcome these problems, several distinct approaches are developed for alloying base metals to promote the formation of self-healing inherently conductive native oxide scales. The objective of this dissertation study is to demonstrate the viability of these approaches through analyzing the data from Cu-9La (at%) and Fe-V binary alloy systems. The Cu-9 La alloy structure consists of eutectic colonies tens of microns in diameter wherein a rod-like Cu phase lies within a Cu6La matrix phase. The thin oxide scale formed on the Cu phase was found to be Cu2O as expected while the thicker oxide scale formed on the Cu6La phase was found to be a polycrystalline La-rich Cu2O. The enhanced electrical conductivity in the native oxide scale of the Cu-9La alloy arises from heavy n-type doping of the Cu2O lattice by La3+. The Fe-V alloy structures consist of a mixture of large elongated and equiaxed grains. A thin polycrystalline Fe3O4 oxide scale formed on all of the Fe-V alloys. The electrical conductivities of the oxide scales formed on the Fe-V alloys are higher than that formed on pure Fe. It is inferred that this enhanced conductivity arises from doping of the magnetite with V+4 which promotes electron-polaron hopping. Thus, it has been demonstrated that even in simple binary alloy systems one can obtain a dramatic reduction in the contact resistances of alloy oxidized surfaces as compared with those of the pure base metals.

Dominance of 'Gallionella capsiferriformans' and heavy metal association with Gallionella-like stalks in metal-rich pH 6 mine water discharge

USGS Publications Warehouse

Fabisch, Maria; Freyer, Gina; Johnson, Carol A.; Buchel, Georg; Akob, Denise M.; Neu, Thomas R.; Kusel, Kirsten

2016-01-01

Heavy metal-contaminated, pH 6 mine water discharge created new streams and iron-rich terraces at a creek bank in a former uranium-mining area near Ronneburg, Germany. The transition from microoxic groundwater with ~5 mm Fe(II) to oxic surface water may provide a suitable habitat for microaerobic iron-oxidizing bacteria (FeOB). In this study, we investigated the potential contribution of these FeOB to iron oxidation and metal retention in this high-metal environment. We (i) identified and quantified FeOB in water and sediment at the outflow, terraces, and creek, (ii) studied the composition of biogenic iron oxides (Gallionella-like twisted stalks) with scanning and transmission electron microscopy (SEM, TEM) as well as confocal laser scanning microscopy (CLSM), and (iii) examined the metal distribution in sediments. Using quantitative PCR, a very high abundance of FeOB was demonstrated at all sites over a 6-month study period. Gallionella spp. clearly dominated the communities, accounting for up to 88% ofBacteria, with a minor contribution of other FeOB such as Sideroxydans spp. and ‘Ferrovum myxofaciens’. Classical 16S rRNA gene cloning showed that 96% of the Gallionella-related sequences had ≥97% identity to the putatively metal-tolerant ‘Gallionella capsiferriformans ES-2’, in addition to known stalk formers such as Gallionella ferruginea and Gallionellaceae strain R-1. Twisted stalks from glass slides incubated in water and sediment were composed of the Fe(III) oxyhydroxide ferrihydrite, as well as polysaccharides. SEM and scanning TEM-energy-dispersive X-ray spectroscopy revealed that stalk material contained Cu and Sn, demonstrating the association of heavy metals with biogenic iron oxides and the potential for metal retention by these stalks. Sequential extraction of sediments suggested that Cu (52–61% of total sediment Cu) and other heavy metals were primarily bound to the iron oxide fractions. These results show the importance of ‘G. capsiferriformans’ and biogenic iron oxides in slightly acidic but highly metal-contaminated freshwater environments.

The Role of Anionogenic Elements (As, Sb, Mo, Se, S, P, N, Cl, F, C) In The Formation of Technogenic Geochemical Anomalies

NASA Astrophysics Data System (ADS)

Abrosimova, Natalya; Bortnikova, Svetlana

2017-12-01

The study was conducted on the example of sulphide-containing mine tailings with a varying amount of sulphide and arsenide minerals, from three distinct tailings dumps situated in Russia: Karabash Mine Site, South Ural; Komsomolsk tailings impoundment, Kemerovo region; Khovu-Aksy mine site, Tuva Republic. The aim of the study was to compare the mobility of anionogenic elements (As, Sb, Mo, Se, S, P, N, Cl, F, C) and their role in migration, precipitation, and concentration of metals during the water-tailings interaction depending on the physicochemical parameters (pH, Eh) of the medium and the mineral composition of the waste material. Using slightly acidic leaching experiments the quantitative estimation of mobile forms of elements is given. Based on the compositions of the obtained water leaching solutions, aqueous speciation of chemical elements and saturation index of key minerals in the experimental solutions were calculated. The results of calculating forms of chemical elements made it possible to construct series of mobility of metals and metalloids in solutions with different physicochemical parameters. In the alkaline conditions, Sb>As>Cd>Cu>Zn>Fe>Pb, when the medium is acidified, the series changes, As>Cd>Cu>Zn>Pb>Sb>Fe in weakly alkaline conditions, Sb>Mn>As>Zn>Fe however, when the medium is acidified, the series changes to Cd>Mn>Pb>Cu>Zn>Sb>Ni>Fe>As under acidic conditions Cd>Cu>Zn>Pb>Mn>Fe>Se>Mo>Sb>As>Ni. The mineral composition of the tailings was investigated, which will allow to determine the sources of toxic elements and to understand the processes of secondary mineral formation in technogenic objects. Arsenopyrite and pyrite predominate in the heavy fraction of the Komsomolsk tailings impoundment, arsenopyrite grains are often corroded, Sb contained in Sb oxide and Sb sulfide. The pyrite and barite are determined in the solid matter of the Karabash Mine Site and chalcopyrite, sphalerite, tennantite Cu3AsS3, and tetrahedrite (Cu,Fe)12Sb4S13 are determined in the form of inclusions in grains of pyrite.

Isotopic Evidence of Unaccounted for Fe and Cu Erythropoietic Pathways

NASA Astrophysics Data System (ADS)

Albarede, F.; Telouk, P.; Lamboux, A.; Jaouen, K.; Balter, V.

2011-12-01

Despite its potential importance for understanding perturbations in the Fe-Cu homeostatic pathways, the natural isotopic variability of these metals in the human body remains unexplored. We measured the Fe, Cu, and Zn isotope compositions of total blood, serum, and red blood cells of ~50 young blood donors by multiple-collector ICP-MS after separation and purification by anion exchange chromatography. Zn is on average 0.2 permil heavier in erythrocytes (δ 66Zn=0.44±0.33 permil) with respect to serum but shows much less overall isotopic variability than Fe and Cu, which indicates that isotope fractionation depends more on redox conditions than on ligand coordination. On average, Fe in erythrocytes (δ 56Fe=-2.59±0.47 permil) is isotopically light by 1-2 permil with respect to serum, whereas Cu in erythrocytes (δ 65Cu=0.56±0.50 permil) is 0.8 percent heavier. Fe and Cu isotope compositions clearly separate erythrocytes of men and women. Fe and Cu from B-type men erythrocytes are visibly more fractionated than all the other blood types. Isotope compositions provide an original method for evaluating metal mass balance and homeostasis. Natural isotope variability shows that the current models of Fe and Cu erythropoiesis, which assume that erythropoiesis is restricted to bone marrow, violate mass balance requirements. It unveils unsuspected major pathways for Fe, with erythropoietic production of isotopically heavy ferritin and hemosiderin, and for Cu, with isotopically light Cu being largely channeled into blood and lymphatic circulation rather than into superoxide dismutase-laden erythrocytes. Iron isotopes provide an intrinsic measuring rod of the erythropoietic yield, while Cu isotopes seem to gauge the relative activity of erythropoiesis and lymphatics.

Cyclic catalytic upgrading of chemical species using metal oxide materials

NASA Technical Reports Server (NTRS)

White, James H. (Inventor); Schutte, Erick J. (Inventor); Rolfe, Sara L. (Inventor)

2010-01-01

Processes are disclosure which comprise alternately contacting an oxygen-carrying catalyst with a reducing substance, or a lower partial pressure of an oxidizing gas, and then with the oxidizing gas or a higher partial pressure of the oxidizing gas, whereby the catalyst is alternately reduced and then regenerated to an oxygenated state. In certain embodiments, the oxygen-carrying catalyst comprises at least one metal oxide-containing material containing a composition having one of the following formulas: (a) Ce.sub.xB.sub.yB'.sub.zB''O.sub..delta., wherein B=Ba, Sr, Ca, or Zr; B'=Mn, Co, or Fe; B''=Cu; 0.01

Cyclic catalytic upgrading of chemical species using metal oxide materials

DOEpatents

White, James H.; Schutte, Erick J.; Rolfe, Sara L.

2010-11-02

Processes are disclosure which comprise alternately contacting an oxygen-carrying catalyst with a reducing substance, or a lower partial pressure of an oxidizing gas, and then with the oxidizing gas or a higher partial pressure of the oxidizing gas, whereby the catalyst is alternately reduced and then regenerated to an oxygenated state. In certain embodiments, the oxygen-carrying catalyst comprises at least one metal oxide-containing material containing a composition having one of the following formulas: (a) Ce.sub.xB.sub.yB'.sub.zB''O.sub..delta., wherein B=Ba, Sr, Ca, or Zr; B'=Mn, Co, or Fe; B''=Cu; 0.01

Rat liver mitochondrial dysfunction by addition of copper(II) or iron(III) ions.

PubMed

Saporito-Magriñá, Christian; Musacco-Sebio, Rosario; Acosta, Juan M; Bajicoff, Sofía; Paredes-Fleitas, Paola; Boveris, Alberto; Repetto, Marisa G

2017-01-01

Increased copper (Cu) and iron (Fe) levels in liver and brain are associated to oxidative stress and damage with increased phospholipid oxidation process. The aim of this work was to assess the toxic effects of Cu 2+ and Fe 3+ addition to rat liver mitochondria by determining mitochondrial respiration in states 3 (active respiration) and 4 (resting respiration), and phospholipid peroxidation. Both, Cu 2+ and Fe 3+ produced decreases in O 2 consumption in a concentration-dependent manner in active state 3: both ions by 42% with malate-glutamate as complex I substrate (concentration for half maximal response (C 50 ) 60μM Cu 2+ and 1.25mM Fe 3+ ), and with succinate as complex II substrate: 64-69% with C 50 of 50μM Cu 2+ and with C 50 of 1.25mM of Fe 3+ . Respiratory control decreased with Cu 2+ (C 50 50μM) and Fe 3+ (C 50 1.25-1-75mM) with both substrates. Cu 2+ produced a 2-fold increase and Fe 3+ a 5-fold increase of thiobarbituric acid-reactive substances (TBARS) content from 25μM Cu 2+ (C 50 40μM) and from 100μM Fe 3+ (C 50 1.75mM). Supplementations with Cu 2+ and Fe 3+ ions induce mitochondrial dysfunction with phospholipid peroxidation in rat liver mitochondria. Although is proved that a Fenton/Haber Weiss mechanism of oxidative damage occurs in metal-ion induced mitochondrial toxicity, slightly different responses to the metal ions suggest some differences in the mechanism of intracellular toxicity. The decreased rates of mitochondrial respiration and the alteration of mitochondrial function by phospholipid and protein oxidations lead to mitochondrial dysfunction, cellular dyshomeostasis and cell death. Copyright © 2016 Elsevier Inc. All rights reserved.

Role of Cu During Sintering of Fe0.96Cu0.04 Nanoparticles

NASA Astrophysics Data System (ADS)

Sivaprahasam, D.; Sriramamurthy, A. M.; Bysakh, S.; Sundararajan, G.; Chattopadhyay, K.

2018-04-01

Nanoparticle agglomerates of passivated Fe ( n-Fe) and Fe0.96Cu0.04 ( n-Fe0.96Cu0.04), synthesized through the levitational gas condensation (LGC) process, were compacted and sintered using the conventional powder metallurgy method. The n-Fe0.96Cu0.04 agglomerates produced lower green density than n-Fe, and when compacted under pressure beyond 200 MPa, they underwent lateral cracking during ejection attributed to the presence of a passive oxide layer. Sintering under dynamic hydrogen atmosphere can produce a higher density of compact in n-Fe0.96Cu0.04 in comparison to n-Fe. Both the results of dilatometry and thermogravimetric (TG) measurements of the samples under flowing hydrogen revealed enhancement of the sintering process as soon as the reduction of oxide layers could be accomplished. The shrinkage rate of n-Fe0.96Cu0.04 reached a value three times higher than n-Fe at a low temperature of 723 K (450 °C) during heating. This enhanced shrinkage rate was the manifestation of accumulation of Cu at the surface of the particles. The formation of a thin-surface melted layer enriched with copper during heating to isothermal holding facilitated as a medium of transport for diffusion of the elements. The compacts produced by sintering at 773 K (500 °C), with relative density 82 pct, were found to be unstable and oxidized instantly when exposed to ambient atmosphere. The stable compacts of density more than 92 pct with 300- to 450-nm grain size could only be produced when sintering was carried out at 973 K (700 °C) and beyond. The 0.22 wt pct residual oxygen obtained in the sintered compact is similar to what is used for conventional ferrous powder metallurgy products.

Mineralogy and geochemistry of the Tartai massif, East Siberian metallogenic province

NASA Astrophysics Data System (ADS)

Podlipsky, M. Yu.; Mekhonoshin, A. S.; Tolstykh, N. D.; Vishnevskiy, A. V.; Polyakov, G. V.

2015-05-01

The Tartai ultramafic-mafic massif is located in the central part of the East Siberian metallogenic (PGE-Cu-Ni) province (728-712 Ma), which constitutes part of the southern margin of the Siberian craton. This dunite-peridotite-pyroxenite-gabbro massif is the host to low-sulfide PGE-Cu-Ni mineralization. The massif was formed by fractional crystallization of picritic magmas and is composed of wehrlite, dunite, plagiowehrlite, and olivine melanogabbro. The composition of olivine varies from Fo89.9 in dunite to Fo83 in melanocratic olivine gabbro; clinopyroxene is esentially augite. Chrome-spinels crystallized at a low degree of oxidation and have a high iron content. Disseminated sulfide mineralization (pentlandite and heazlewoodite) with high PGE concentrations was identified in wehrlites. Pentlandite is enriched in Fe and Co and depleted in S. These features and the association pentlandite with heazlewoodite suggest that the sulfide mineralization was formed over a wide temperature range (600-400°C) at low sulfur activity (log fS2 from -16 to -9). PGM are represented by Ir-bearing sperrylite, Pd-Cu-Sb panning compounds of variable compositions, Pt-Fe-Cu and Pt-Cu alloys. The evolutionary trend of the ore system was from essentially Ni compositions at the early magmatic stage during formation of disseminated mineralization toward Cu-rich composition at the post-magmatic stage. The PGM assemblage from heavy concentrate haloes differs from bedrock-hosted mineralization in its wider variety of mineral species and the presence of refractory platinoids. Sperrylite from heavy concentrate haloes of the Tartai massif serves as a reliable prospecting guide for bedrock-hosted sulfide Cu-Ni deposits.

Cytotoxicity, permeability, and inflammation of metal oxide nanoparticles in human cardiac microvascular endothelial cells: cytotoxicity, permeability, and inflammation of metal oxide nanoparticles.

PubMed

Sun, Jing; Wang, Shaochuang; Zhao, Dong; Hun, Fei Han; Weng, Lei; Liu, Hui

2011-10-01

Wide applications and extreme potential of metal oxide nanoparticles (NPs) increase occupational and public exposure and may yield extraordinary hazards for human health. Exposure to NPs has a risk for dysfunction of the vascular endothelial cells. The objective of this study was to assess the cytotoxicity of six metal oxide NPs to human cardiac microvascular endothelial cells (HCMECs) in vitro. Metal oxide NPs used in this study included zinc oxide (ZnO), iron(III) oxide (Fe(2)O(3)), iron(II,III) oxide (Fe(3)O(4)), magnesium oxide (MgO), aluminum oxide (Al(2)O(3)), and copper(II) oxide (CuO). The cell viability, membrane leakage of lactate dehydrogenase, intracellular reactive oxygen species, permeability of plasma membrane, and expression of inflammatory markers vascular cell adhesion molecule-1, intercellular adhesion molecule-1, macrophage cationic peptide-1, and interleukin-8 in HCMECs were assessed under controlled and exposed conditions (12-24 h and 0.001-100 μg/ml of exposure). The results indicated that Fe(2)O(3), Fe(3)O(4), and Al(2)O(3) NPs did not have significant effects on cytotoxicity, permeability, and inflammation response in HCMECs at any of the concentrations tested. ZnO, CuO, and MgO NPs produced the cytotoxicity at the concentration-dependent and time-dependent manner, and elicited the permeability and inflammation response in HCMECs. These results demonstrated that cytotoxicity, permeability, and inflammation in vascular endothelial cells following exposure to metal oxide nanoparticles depended on particle composition, concentration, and exposure time. © Springer Science+Business Media B.V. 2011

The influence of structural fluorine on biotite oxidation in copper-bearing, aqueous solutions at low temperatures and pressures

NASA Astrophysics Data System (ADS)

Earley, Drummond, III; Darby Dyar, M.; Ilton, Eugene S.; Granthem, Allen A.

1995-06-01

High-F (5.4 wt%) and low-F (0.8 wt%) biotites were reacted with aqueous (Cu, Na 2)Cl 2 solutions at ambient conditions to investigate biotite oxidation mechanisms at low temperatures and pressures and at atmospheric pO 2. The exchange of Cu +2 for interlayer cations increases the rate of biotite oxidation under these conditions. Solid reactants and products were characterized by Mössbauer spectroscopy, X-ray diffraction, and comprehensive bulk chemical analyses. Even though both biotites were pretreated with a sodium tetraphenylboron (NaTPB) solution, which rapidly exchanges Na for K, only about 50% of the interlayer K was exchanged during most of these experiments. As a result, the exchange reactions produced variably expanded phases with d(001) ranging from approximately 10 to 14 Å. Octahedral Fe +2 in samples of high- and low-F biotite was oxidized rapidly during Cu exchange. The degree of Fe +2 oxidation amounted to about 50% of the total Fe in most experiments and was nearly independent of the total mass of Cu introduced into the interlayer which ranged from 2.0 to 9.2 wt% CuO. The Mössbauer spectra also show that the Fe +2 in M(1) octahedra of the high-F biotite was oxidized more slowly than Fe +2 in M(2) sites, whereas in the low-F biotite experiments M(1) Fe +2 was oxidized at a slightly faster rate than the Fe +2 in M(2) sites. Our study suggests that the total amount of Fe oxidized was limited by the amount of K exchanged, and that preferred oxidation of Fe +2 at M(2) sites relative to M(1) sites was a function of the F content of these biotites. Charge transfer from octahedral Fe +2 to the interlayer may be facilitated by deprotonation. In exchange experiments conducted on the F-rich biotite, Fe +2 oxidation at M(1) sites was limited indicating that preferential substitution of F for OH might occur at the M(1) site. We used the Fe-F avoidance law to develop an F-OH ordering model that preferentially distributes F on selected trans positions of Fe-filled M(1) octahedra in Fe- and F-rich biotites. If charge transfer is facilitated by the presence of OH then the proposed F-OH ordering model could account for the selective deactivation of the Fe +2 oxidation mechanism at the M(1) site.

Adsorption of tetracycline on Fe (hydr)oxides: effects of pH and metal cation (Cu2+, Zn2+ and Al3+) addition in various molar ratios

PubMed Central

Hsu, Liang-Ching; Liu, Yu-Ting; Syu, Chien-Hui; Huang, Mei-Hsia; Teah, Heng Yi

2018-01-01

Iron (Fe) (hydr)oxides control the mobility and bioavailability of tetracycline (TC) in waters and soils. Adsorption of TC on Fe (hydr)oxides is greatly affected by polyvalent metals; however, impacts of molar metal/TC ratios on TC adsorptive behaviours on Fe (hydr)oxides remain unclear. Results showed that maximum TC adsorption on ferrihydrite and goethite occurred at pH 5–6. Such TC adsorption was generally promoted by the addition of Cu2+, Zn2+ and Al3+. The greatest increase in TC adsorption was found in the system with molar Cu/TC ratio of 3 due to the formation of Fe hydr(oxide)–Cu–TC ternary complexes. Functional groups on TC that were responsible for the complexation with Cu2+shifted from phenolic diketone groups at Cu/TC molar ratio < 1 to amide groups at Cu/TC molar ratio ≥ 1. For the addition of Al3+, the complexation only took place with phenolic diketone groups, resulting in the enhanced TC adsorption at a molar Al/TC ratio of 1. However, TC adsorption decreased for Al/TC molar ratio > 1 as excess Al3+ led to the competitive adsorption with Al/TC complexes. For the Zn2+ addition, no significant correlation was found between TC adsorption capacity and molar Zn/TC ratios. PMID:29657795

A textural and compositional investigation on the source and timing of iron oxidation and titanium enrichment in high-pressure serpentinites

NASA Astrophysics Data System (ADS)

Crossley, R.; Evans, K. A.; Reddy, S.; Lester, G. W.

2016-12-01

The redox state, quantity and composition of subduction zone fluids influence the transport and precipitation of elements including those which are redox-sensitive, of economic importance such as Cu, Au and Ag, and those considered to be immobile, which include Fe3+. However, subduction zone fluids remain poorly understood. The redox state of Fe in high-pressure ultramafic rocks, which host a significant proportion of Fe3+, can be used to provide an insight into Fe cycling and constrain the composition and possible source of subduction zone fluids. In this work, we use a combination of oxide mineral textures, mineral parageneses, mineral composition data, and whole rock geochemistry of high-pressure retrogressed ultramafic rocks from the Zermatt-Saas Zone to constrain the distribution and oxidation state of iron, and to provide insights on the nature of fluids at depth within subduction zones. Oxide minerals host the bulk of the iron, particularly Fe3+. The increase in mode of magnetite during initial retrogression is most consistent with oxidation of existing iron via the infiltration of an oxidising fluids since it is difficult to reconcile addition of Fe3+ with the known limited solubility of this species. In addition, fluid-mediated or mechanical mixing with other lithologies in the slab could introduce elements and alter the bulk composition of serpentinites. However, the high Ti content of one sample cannot be explained by simple mixing of a depleted mantle protolith with the nearby Allalin gabbros, and provides the tantalising possibility that Ti, an element generally perceived as immobile, has been added to the rock. While we cannot completely exclude the possibility of pre-subduction Ti addition, textural analysis of Ti-rich minerals suggest mobilisation of Ti during subduction on at least a centimetre scale. If Ti addition has occurred, then the introduction of Fe3+, also generally considered to be immobile, cannot be disregarded. The Al-rich nature of the sample may be consistent with aluminosilicate complexing as the transport vector for Ti and/or Fe3+.

Understanding and Quantifying the Reactivity of Energetic NanoParticles and NanoComposites

DTIC Science & Technology

2015-01-05

Aerosol Synthesis and Reactivity of Thin Oxide Shell Aluminum Nanoparticles via Fluorocarboxylic Acid Functional Coating, Particle & Particle...Received Paper 3.00 9.00 8.00 7.00 6.00 5.00 4.00 X. Ma and M.R. Zachariah. " Oxidation Anisotropy and Size Dependent Reaction Kinetics of Zinc ...in the reaction. Experiments also conducted for neat Al, CuO, Fe2O3 and ZnO powders show that the oxygen are produced by decomposition of oxidizer

High speed 2-dimensional temperature measurements of nanothermite composites: Probing thermal vs. Gas generation effects

NASA Astrophysics Data System (ADS)

Jacob, Rohit J.; Kline, Dylan J.; Zachariah, Michael R.

2018-03-01

This work investigates the reaction dynamics of metastable intermolecular composites through high speed spectrometry, pressure measurements, and high-speed color camera pyrometry. Eight mixtures including Al/CuO and Al/Fe2O3/xWO3 (x being the oxidizer mol. %) were reacted in a constant volume pressure cell as a means of tuning gas release and adiabatic temperature. A direct correlation between gas release, peak pressure, and pressurization rate was observed, but it did not correlate with temperature. When WO3 was varied as part of the stoichiometric oxidizer content, it was found that Al/Fe2O3/70% WO3 achieved the highest pressures and shortest burn time despite a fairly constant temperature between mixtures, suggesting an interplay between the endothermic Fe2O3 decomposition and the higher adiabatic flame temperature sustained by the Al/WO3 reaction in the composite. It is proposed that the lower ignition temperature of Al/WO3 leads to the initiation of the composite and its higher flame temperature enhances the gasification of Fe2O3, thus improving advection and propagation as part of a feedback loop that drives the reaction. Direct evidence of such gas release promoting reactivity was obtained through high speed pyrometry videos of the reaction. These results set the stage for nanoenergetic materials that can be tuned for specific applications through carefully chosen oxidizer mixtures.

Effect of Ir-Mn composition on exchange bias and thermal stability of spin valves with nano-oxide layers

NASA Astrophysics Data System (ADS)

Liu, Y. F.; Cai, J. W.; Lai, W. Y.; Yu, G. H.

2008-05-01

The Ir-Mn bottom-pinned spin valves with nano-oxide layers (NOLs), Ta /Ni81Fe19/Ir-Mn/Co90Fe10/NOL/Co90Fe10/Cu/Co90Fe10/NOL/Ta, were fabricated by dc magnetron sputtering. The magnetoresistance (MR), magnetization, and exchange bias have been studied as a function of Ir-Mn composition and annealing temperature. It was observed that the spin valves with the Ir-Mn layer containing relatively low Mn content (58.9-72.4at.% Mn) show the best thermal endurance. For these samples, the Mn diffusion is effectively hampered by the NOL with a large MR value of about 12.5% even after annealing at 300°C. On the other hand, the exchange bias field of the pinned CoFe layer shows a maximum at Mn content of about 72.4at.%, which is different from the widely adopted composition, Ir-80at.% Mn, optimized from the top-pinned NiFe /Ir-Mn system. Moreover, the blocking temperature of the Ir -Mn/CoFe system with 72.4at.% Mn is higher than that with 80.6at.% Mn. The present results suggest that the Ir -Mn/CoFe pinning system with Mn content at about 72% renders the most favorable exchange bias and the best thermal stability for the bottom-pinned specular spin valves.

Cermet anode compositions with high content alloy phase

DOEpatents

Marschman, Steven C.; Davis, Norman C.

1989-01-01

Cermet electrode compositions comprising NiO-NiFe.sub.2 O.sub.4 -Cu-Ni, and methods for making, are disclosed. Addition of nickel metal prior to formation and densification of a base mixture into the cermet allows for an increase in the total amount of copper and nickel that can be contained in the NiO-NiFe.sub.2 O.sub.4 oxide system. Nickel is present in a base mixture weight concentration of from 0.1% to 10%. Copper is present in the alloy phase in a weight concentration of from 10% to 30% of the densified composition. Such cermet electrodes can be formed to have electrical conductivities well in excess of 100 ohm.sup.-1 cm.sup.-1. Other alloy and oxide system cermets having high content metal phases are also expected to be manufacturable in accordance with the invention.

Cermet anode compositions with high content alloy phase

DOEpatents

Marschman, S.C.; Davis, N.C.

1989-10-03

Cermet electrode compositions comprising NiO-NiFe[sub 2]O[sub 4]-Cu-Ni, and methods for making, are disclosed. Addition of nickel metal prior to formation and densification of a base mixture into the cermet allows for an increase in the total amount of copper and nickel that can be contained in the NiO-NiFe[sub 2]O[sub 4] oxide system. Nickel is present in a base mixture weight concentration of from 0.1% to 10%. Copper is present in the alloy phase in a weight concentration of from 10% to 30% of the densified composition. Such cermet electrodes can be formed to have electrical conductivities well in excess of 100 ohm[sup [minus]1] cm[sup [minus]1]. Other alloy and oxide system cermets having high content metal phases are also expected to be manufacturable in accordance with the invention.

Methionine sulphoxide reductases protect iron-sulphur clusters from oxidative inactivation in yeast

PubMed Central

Sideri, Theodora C.; Willetts, Sylvia A.; Avery, Simon V.

2008-01-01

Methionine residues and iron-sulphur (FeS) clusters are primary targets of reactive oxygen species in the proteins of microorganisms. Here we show that methionine redox-modifications help to preserve essential FeS cluster activities in yeast. Mutants defective for the highly conserved methionine sulphoxide reductases (MSRs; which re-reduce oxidized methionines) are sensitive to many pro-oxidants, but here exhibited an unexpected copper resistance. This phenotype was mimicked by methionine sulphoxide supplementation. Microarray analyses highlighted several Cu and Fe homeostasis genes that were upregulated in the mxrΔ double mutant, which lacks both of the yeast MSRs. Of the upregulated genes, the Cu-binding Fe-transporter Fet3p proved to be required for the Cu-resistance phenotype. FET3 is known to be regulated by the Aft1 transcription factor, which responds to low mitochondrial FeS-cluster status. Here, constitutive Aft1p expression in the wild type reproduced the Cu-resistance phenotype, and FeS cluster functions were found to be defective in the mxrΔ mutant. Genetic perturbation of FeS activity also mimicked FET3-dependent Cu resistance. 55Fe-labeling studies showed that FeS clusters are turned over more rapidly in the mxrΔ mutant than the wild type, consistent with elevated oxidative targeting of the clusters in MSR-deficient cells. The potential underlying molecular mechanisms of this targeting are discussed. Moreover, the results indicate an important new role for cellular MSR enzymes, in helping to protect the essential function of FeS clusters in aerobic settings. PMID:19202110

Graphene-Supported Spinel CuFe2O4 Composites: Novel Adsorbents for Arsenic Removal in Aqueous Media

PubMed Central

La, Duong Duc; Nguyen, Tuan Anh; Jones, Lathe A.; Bhosale, Sheshanath V.

2017-01-01

A graphene nanoplate-supported spinel CuFe2O4 composite (GNPs/CuFe2O4) was successfully synthesized by using a facile thermal decomposition route. Scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), Electron Dispersive Spectroscopy (EDS), X-ray diffraction (XRD) and X-ray Photoelectron Spectroscopy (XPS) were employed to characterize the prepared composite. The arsenic adsorption behavior of the GNPs/CuFe2O4 composite was investigated by carrying out batch experiments. Both the Langmuir and Freundlich models were employed to describe the adsorption isotherm, where the sorption kinetics of arsenic adsorption by the composite were found to be pseudo-second order. The selectivity of the adsorbent toward arsenic over common metal ions in water was also demonstrated. Furthermore, the reusability and regeneration of the adsorbent were investigated by an assembled column filter test. The GNPs/CuFe2O4 composite exhibited significant, fast adsorption of arsenic over a wide range of solution pHs with exceptional durability, selectivity, and recyclability, which could make this composite a very promising candidate for effective removal of arsenic from aqueous solution. The highly sensitive adsorption of the material toward arsenic could be potentially employed for arsenic sensing. PMID:28587257

Cermet anode with continuously dispersed alloy phase and process for making

DOEpatents

Marschman, Steven C.; Davis, Norman C.

1989-01-01

Cermet electrode compositions and methods for making are disclosed which comprise NiO--NiFe.sub.2 O.sub.4 --Cu--Ni. Addition of an effective amount of a metallic catalyst/reactant to a composition of a nickel/iron/oxide, NiO, copper, and nickel produces a stable electrode having significantly increased electrical conductivity. The metallic catalyst functions to disperse the copper and nickel as an alloy continuously throughout the oxide phase of the cermet to render the electrode compositon more highly electrically conductive than were the third metal not present in the base composition. The third metal is preferably added to the base composition as elemental metal and includes aluminum, magnesium, sodium and gallium. The elemental metal is converted to a metal oxide during the sintering process.

Rapid synthesis of Fe-doped CuO-Ce0.8Zr0.2O2 catalysts for CO preferential oxidation in H2-rich streams: Effect of iron source and the ratio of Fe/Cu

NASA Astrophysics Data System (ADS)

Wang, Jing; Han, Caiyun; Gao, Xiaoya; Lu, Jichang; Wan, Gengpin; He, Dedong; Chen, Ran; Chen, Kezhen; He, Sufang; Luo, Yongming

2017-03-01

A facile route (urea grind combustion method) is described for the rapid synthesis of Fe-doped Cu-Ce-Zr catalysts within 30 min through simple grinding and combustion. The effects of iron source and Fe/Cu mass ratio on the performances of the catalysts for CO preferential oxidation (CO-PROX) are evaluated. The influences of H2O, CO2, and their mixture on the activity as well as stability of the catalysts are also investigated. The samples are characterized by XRD, N2 adsorption-desorption, H2-TPR, TEM, Raman and XPS. Fe(NO3)3 is found to be superior to FeCl3 and Fe2(SO4)3 as the iron source for Fe-CuCZ catalyst. Among the different synthesized catalysts, 1/10Fe(N)-CuCZ is found to be the most active catalyst, indicating that the optimal Fe/Cu mass ratio is 1/10. The influences of H2O, CO2, and H2O + CO2 on the catalytic performance of 1/10Fe(N)-CuCZ are in the order of CO2 < CO2 + H2O < H2O. 1/10Fe(N)-CuCZ exhibits excellent stability during a 228 h time-on-stream test. 1/10Fe(N)-CuCZ shows the highest catalytic activity and excellent stability even in the presence of H2O and CO2. The excellent catalytic performance can be attributed to the synergy between the highly dispersed copper species and ceria, as well as the formation of more oxygen vacancies and reduced copper species.

Preparation of TbCu7-type Sm-Fe powders by low-temperature HDDR treatment

NASA Astrophysics Data System (ADS)

Takagi, Kenta; Jinno, Miho; Ozaki, Kimihiro

2018-05-01

Low-temperature hydrogen-disproportionation-desorption-recombination (HDDR) treatment of Sm-Fe alloy powder was conducted to prepare a metastable TbCu7 type Sm-Fe alloy powder with a grain size of more than a few hundreds of nanometers. While a treatment temperature above 700 °C produced the familiar Th2Zn17 type alloy, one below 600 °C resulted in successful synthesis of the TbCu7 type Sm-Fe alloy with submicron-size grains. This TbCu7 type alloy powder, however, showed no significant improvement in magnetic properties compared to the Th2Zn17 type, as its composition was estimated to be near SmFe8.5 and thus did not achieve the expected Fe-rich composition. Therefore, cross-sectional transmission electron microscope observation of the unfinished TbCu7 type alloy powder was conducted in order to explore means of forming the Fe-rich phase.

In situ Fenton reagent generated from TiO2/Cu2O composite film: a new way to utilize TiO2 under visible light irradiation.

PubMed

Zhang, Yong-Gang; Ma, Li-Li; Li, Jia-Lin; Yu, Ying

2007-09-01

TiO2/Cu2O composite is prepared by a simple electrochemical method and coated on glass matrix through a spraying method. The obtained composite is characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The effect of TiO2/Cu2O composite films with different ratio of TiO2 and Cu2O on photodegradation of the dye methylene blue under visible light is investigated in detail. It is found that the photocatalytic activity of TiO2/Cu2O composite film with the presence of FeSO4 and EDTA is much higher than that for the similar system with only TiO2 and Cu2O film respectively. Without the presence of FeSO4 and EDTA, there is no degradation for methylene blue. The exploration of the optimized parameters for the degradation of methylene blue by using TiO2/Cu2O composite film as catalyst under visible light was also carried out. The most significant factor is the amount of Ti02 in the composite, and the second significant factor is the concentration of FeSO4. During the degradation of methylene blue under visible light, TiO2/Cu2O composite film generates H202, and Fenton regent is formed with Fe2+ and EDTA, which is detected in this study. The mechanism for the great improvement of photocatalytic activity of TiO2/Cu2O composite film under visible light is proposed by the valence band theory. Electrons excitated from TiO2/Cu2O composite under visible light are transferred from the conduction band of Cu2O to that of Ti02. The formed intermediate state of Ti 3+ ion is observed by X-ray photoelectron spectroscopy (XPS) on the TiO/Cu2O composite film. Additionally, the accumulated electrons in the conduction band of TiO2 are transferred to oxygen on the TiO2 surface for the formation of O2- or O2(2-), which combines with H+ to form H2O2. The evolved H202 with FeSO4 and EDTA forms Fenton reagentto degrade methylene blue. Compared to the traditional Fenton reagent, this new kind of in situ Fenton reagent generated from TiO2/Cu2O composite film does not need to supply H202. It is expected to be easily recycled, which may reduce second pollution and the cost of wastewater treatment. Moreover, this TiO/Cu2O composite film with FeSO4 and EDTA provides a new way to take advantage of TiO2 under visible light.

Synthesis of Copper Oxide/Graphite Composite for High-Performance Rechargeable Battery Anode.

PubMed

Cho, Sanghun; Ahn, Yong-Keon; Yin, Zhenxing; You, Duck-Jae; Kim, Hyunjin; Piao, Yuanzhe; Yoo, Jeeyoung; Kim, Youn Sang

2017-08-25

A novel copper oxide/graphite composite (GCuO) anode with high capacity and long cycle stability is proposed. A simple, one-step synthesis method is used to prepare the GCuO, through heat treatment of the Cu ion complex and pristine graphite. The gases generated during thermal decomposition of the Cu ion complex (H 2 and CO 2 ) induce interlayer expansion of the graphite planes, which assists effective ion intercalation. Copper oxide is formed simultaneously as a high-capacity anode material through thermal reduction of the Cu ion complex. Material analyses reveal the formation of Cu oxide nanoparticles and the expansion of the gaps between the graphite layers from 0.34 to 0.40 nm, which is enough to alleviate layer stress for reversible ion intercalation for Li or Na batteries. The GCuO cell exhibits excellent Li-ion battery half-cell performance, with a capacity of 532 mAh g -1 at 0.2 C (C-rate) and capacity retention of 83 % after 250 cycles. Moreover, the LiFePO 4 /GCuO full cell is fabricated to verify the high performance of GCuO in practical applications. This cell has a capacity of 70 mAh g -1 and a coulombic efficiency of 99 %. The GCuO composite is therefore a promising candidate for use as an anode material in advanced Li- or Na-ion batteries. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Status of neurocognitive and oxidative stress conditions in iron-steel workers.

PubMed

Malekirad, Ali Akbar; Mirabdollahi, Mansuoreh; Pilehvarian, Ali Asghar; Nassajpour, Ali Reza; Abdollahi, Mohammad

2015-07-01

The aim of this study was to determine oxidative stress status as well as ferrous (Fe) and Copper (Cu) levels in blood, neurocognitive impairment, and clinical markers in iron-steel workers. A comparative cross-sectional analysis was performed in 50 iron-steel workers who have been in contact with Fe and Cu in comparison with a control group containing 50 healthy subjects in the same age group and sex. Blood levels of lipid peroxidation, total antioxidant capacity, Fe, and Cu along with neurocognitive impairment were measured in workers and controls. Clinical examination was accomplished to record any abnormal sign or symptoms. Comparing with controls, the workers showed higher blood levels of lipid peroxidation and Cu and also a lower total antioxidant capacity. There was a positive correlation between work history and interstitial lung disease that strengths the presumption to progress to chronic obstructive lung disease in future. The results indicate that exposure to a combination of Fe and Cu in iron-steel workers induces oxidative stress. Especially, in the present case, toxic effect of Cu has been more than positive effects of Fe, but the combined exposure resulted in no such critical toxicity. © The Author(s) 2013.

Copper-promoted circumneutral activation of H2O2 by magnetic CuFe2O4 spinel nanoparticles: Mechanism, stoichiometric efficiency, and pathway of degrading sulfanilamide.

PubMed

Feng, Yong; Liao, Changzhong; Shih, Kaimin

2016-07-01

To evaluate the heterogeneous degradation of sulfanilamide by external energy-free Fenton-like reactions, magnetic CuFe2O4 spinel nanoparticles (NPs) were synthesized and used as catalysts for activation of hydrogen peroxide (H2O2). The physicochemical properties of the CuFe2O4 NPs were characterized with several techniques, including X-ray diffraction, X-ray photoelectron spectroscopy, transmission electron microscopy, and magnetometry. In the catalytic experiments, CuFe2O4 NPs/H2O2 oxidation showed the best degradation performance in the circumneutral conditions that resulted from the presence of Cu(II) on the surface of the CuFe2O4 NPs. The surface area-normalized pseudo-first-order rate constants were calculated as 2.60 × 10(-2) L m(-1) min(-1), 2.58 × 10(-3) L m(-1) min(-1), 1.92 × 10(-3) L m(-1) min(-1), and 7.30 × 10(-4) L m(-1) min(-1) for CuO, CuFe2O4 NPs, Fe3O4, and α-Fe2O3 catalysts, respectively. Thus, solid state Cu(II) was more reactive and efficient than Fe(III) in the circumneutral activation of H2O2; this finding was further supported by the results regarding the stoichiometric efficiency of H2O2. The effects of experimental parameters such as the oxidant dosage and catalyst loading were investigated. The mechanism for H2O2 activation on the spinel surface was explored and could be explained by the solid redox cycles of Fe(II)/Fe(III) and Cu(II)/Cu(I). Based on the products detected, a degradation pathway via the CS bond cleavage is proposed for the degradation of sulfanilamide. The findings of this study suggest that copper can be used as a doping metal to improve the reactivity and expand the effective pH range of iron oxides. Copyright © 2016 Elsevier Ltd. All rights reserved.

Antibacterial activity of trimetal (CuZnFe) oxide nanoparticles.

PubMed

Alzahrani, Khalid E; Niazy, Abdurahman A; Alswieleh, Abdullah M; Wahab, Rizwan; El-Toni, Ahmed M; Alghamdi, Hamdan S

2018-01-01

The increasing resistance of pathogenic bacteria to antibiotics is a challenging worldwide health problem that has led to the search for new and more efficient antibacterial agents. Nanotechnology has proven to be an effective tool for the fight against bacteria. In this paper, we present the synthesis and traits of trimetal (CuZnFe) oxide nanoparticles (NPs) using X-ray diffraction, high-resolution transmission electron microscopy, and energy dispersive x-ray spectroscopy. We evaluated the antibacterial activity of these NPs against gram-negative Escherichia coli and gram-positive Enterococcus faecalis and then compared it to that of their pure single-metal oxide components CuO and ZnO. Our study showed that the antibacterial activity of the trimetal oxide NPs was greater against E . coli than against E . faecalis . Overall, the antimicrobial effect of trimetal NPs is between those of pure ZnO and CuO nanoparticles, which may mean that their cytotoxicity is also between that of pure ZnO and CuO NPs, making them potential antibiotics. However, the cytotoxicity of trimetal NPs to mammalian cells needs to be verified. The combination of three metal oxide NPs (ZnO, CuO, and Fe 2 O 3 ) in one multimetal (CuZnFe) oxide NPs will enhance the therapeutic strategy against a wide range of microbial infections. Bacteria are unlikely to develop resistance against this new NP because bacteria must go through a series of mutations to become resistant to the trimetal oxide NP. Therefore, this NP can combat existing and emerging bacterial infections.

Mössbauer study of oxide films of Fe-, Sn-, Cr- doped zirconium alloys during corrosion in autoclave

NASA Astrophysics Data System (ADS)

Filippov, V. P.; Bateev, A. B.; Lauer, Yu. A.

2016-12-01

Mössbauer investigations were used to compare iron atom states in oxide films of binary Zr-Fe, ternary Zr-Fe-Cu and quaternary Zr-Fe-Cr-Sn alloys. Oxide films are received in an autoclave at a temperature of 350-360 °C and at pressure of 16.8 MPa. The corrosion process decomposes the intermetallic precipitates in alloys and forms metallic iron with inclusions of chromium atoms α-Fe(Cr), α-Fe(Cu), α-Fe 2O3 and Fe 3O4 compounds. Some iron ions are formed in divalent and in trivalent paramagnetic states. The additional doping influences on corrosion kinetics and concentration of iron compounds and phases formed in oxide films. It was shown the correlation between concentration of iron in different chemical states and corrosion resistance of alloys.

Redox chemistry of a binary transition metal oxide (AB 2 O 4 ): a study of the Cu 2+ /Cu 0 and Fe 3+ /Fe 0 interconversions observed upon lithiation in a CuFe 2 O 4 battery using X-ray absorption spectroscopy

DOE PAGES

Cama, Christina A.; Pelliccione, Christopher J.; Brady, Alexander B.; ...

2016-06-06

Copper ferrite, CuFe 2 O 4, is a promising candidate for application as a high energy electrode material in lithium based batteries. Mechanistic insight on the electrochemical reduction and oxidation processes was gained through the first X-ray absorption spectroscopic study of lithiation and delithiation of CuFe 2 O 4. A phase pure tetragonal CuFe 2 O 4 material was prepared and characterized using laboratory and synchrotron X-ray diffraction, Raman spectroscopy, and transmission electron microscopy. We used ex situ X-ray absorption spectroscopy (XAS) measurements to study the battery redox processes at the Fe and Cu K-edges, using X-ray absorption near-edge structuremore » (XANES), extended X-ray absorption fine structure (EXAFS), and transmission X-ray microscopy (TXM) spectroscopies. EXAFS analysis showed upon discharge, an initial conversion of 50% of the copper(II) to copper metal positioned outside of the spinel structure, followed by a migration of tetrahedral iron(III) cations to octahedral positions previously occupied by copper(II). Then, upon charging to 3.5 V, the copper metal remained in the metallic state, while iron metal oxidation to iron(III) was achieved. Our results provide new mechanistic insight regarding the evolution of the local coordination environments at the iron and copper centers upon discharging and charging.« less

Redox chemistry of a binary transition metal oxide (AB2O4): a study of the Cu(2+)/Cu(0) and Fe(3+)/Fe(0) interconversions observed upon lithiation in a CuFe2O4 battery using X-ray absorption spectroscopy.

PubMed

Cama, Christina A; Pelliccione, Christopher J; Brady, Alexander B; Li, Jing; Stach, Eric A; Wang, Jiajun; Wang, Jun; Takeuchi, Esther S; Takeuchi, Kenneth J; Marschilok, Amy C

2016-06-22

Copper ferrite, CuFe2O4, is a promising candidate for application as a high energy electrode material in lithium based batteries. Mechanistic insight on the electrochemical reduction and oxidation processes was gained through the first X-ray absorption spectroscopic study of lithiation and delithiation of CuFe2O4. A phase pure tetragonal CuFe2O4 material was prepared and characterized using laboratory and synchrotron X-ray diffraction, Raman spectroscopy, and transmission electron microscopy. Ex situ X-ray absorption spectroscopy (XAS) measurements were used to study the battery redox processes at the Fe and Cu K-edges, using X-ray absorption near-edge structure (XANES), extended X-ray absorption fine structure (EXAFS), and transmission X-ray microscopy (TXM) spectroscopies. EXAFS analysis showed upon discharge, an initial conversion of 50% of the copper(ii) to copper metal positioned outside of the spinel structure, followed by a migration of tetrahedral iron(iii) cations to octahedral positions previously occupied by copper(ii). Upon charging to 3.5 V, the copper metal remained in the metallic state, while iron metal oxidation to iron(iii) was achieved. The results provide new mechanistic insight regarding the evolution of the local coordination environments at the iron and copper centers upon discharging and charging.

Local structure study of (In{sub 0.95−x}Fe{sub x}Cu{sub 0.05}){sub 2}O{sub 3} thin films using x-ray absorption spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ren, Yuan; Xing, Yaya; Ma, Guanxiong

2015-07-15

The (In{sub 0.95−x}Fe{sub x}Cu{sub 0.05}){sub 2}O{sub 3} (x = 0.06, 0.08, 0.15, and 0.20) films prepared by RF-magnetron sputtering were investigated by the combination of x-ray absorption spectroscopy (XAS) at Fe, Cu, and O K-edge. Although the Fe and O K-edge XAS spectra show that the Fe atoms substitute for the In sites of In{sub 2}O{sub 3} lattice for all the films, the Cu K-edge XAS spectra reveal that the codoped Cu atoms are separated to form the Cu metal clusters. After being annealed in air, the Fe atoms are still substitutionally incorporated into the In{sub 2}O{sub 3} lattice, while the Cumore » atoms form the CuO secondary phases. With the increase of Fe concentration, the bond length R{sub Fe-O} shortens and the Debye–Waller factor σ{sup 2}{sub Fe-O} increases in the first coordination shell of Fe, which are attributed to the relaxation of oxygen environment around the substitutional Fe ions. The forming of Cu relating secondary phases in the films is due to high ionization energy of Cu atoms, leading that the Cu atoms are energetically much harder to be oxidized to substitute for the In sites of In{sub 2}O{sub 3} lattice than Fe atoms. These results provide new experimental guidance in the preparation of the codoped In{sub 2}O{sub 3} based dilute magnetic oxides.« less

Cation hydrolysis and the regulation of trace metal composition in seawater

NASA Astrophysics Data System (ADS)

Kumar, M. Dileep

1987-08-01

Thermodynamic calculations have been performed for cation hydrolysis, including temperatures from 2°C to the high values of significance near Mid-Oceanic Ridge Systems (MORS). Eighteen elements with wide range of residence times ( t) in seawater (Mn, Th, Al, Bi, Ce, Co, Cr(III), Fe, Nd, Pb, Sc, Sm, Ag, Cd, Cu, Hg, Ni and Zn) have been considered. A model for the regulation of trace metal composition in seawater by cation hydrolytic processes, including those at MORS, is presented. Results show an increase in the abundance of neutral metal hydroxyl species with increase in temperature. During hydrothermal mixing, as the temperature increases, transformation from lower positive hydroxyl complexes to higher or neutral complexes would occur for Cd, Ce, Co, Cr(III), Cu, Mn, Nd, Ni, Pb, Sm and Zn. pH values for adsorption of the metal ion onto solid surfaces have direct relation with pH values of hydrolysis. Co, Mn and Pb could be oxidized to higher states (at Mn-oxide surfaces) that would occur even at MORS. Ce can also be oxidized at 25°C. Solubility calculations show that Al, Bi, Cr(III), Sc, Fe and Th are saturated while Ce, Nd and Sm are not with respect to their oxyhydroxide solids at their concentrations in seawater at 25°C. Cu, Hg, Ni and Zn reach saturation equilibrium at 250°C, whereas Co, Mn and Pb exhibit unsaturation. The results suggest an increase in scavenging capacity of a cation with rise in temperature.

Adsorption of multi-heavy metals Zn and Cu onto surficial sediments: modeling and adsorption capacity analysis.

PubMed

Li, Shanshan; Zhang, Chen; Wang, Meng; Li, Yu

2014-01-01

Improved multiple regression adsorption models (IMRAMs) was developed to estimate the adsorption capacity of the components [Fe oxides (Fe), Mn oxides (Mn), organic materials (OMs), residuals] in surficial sediments for multi-heavy metal Zn and Cu. IMRAM is an improved version over MRAM, which introduces a computer program in the model developing process. As MRAM, Zn(Cu) IMRAM, and Cu(Zn) IMRAM again confirmed that there is significant interaction effects that control the adsorption of compounded Zn and Cu, which was neglected by additional adsorption model. The verification experiment shows that the relative deviation of the IMRAMs is less than 13%. It is revealed by the IMRAMs that Mn, which has the greatest adsorption capability for compounded Zn and Cu (54.889 and 161.180 mg/l, respectively), follows by interference adsorption capacity of Fe/Mn (-1.072 and -24.591 mg/l respectively). Zn and Cu influence each other through different mechanisms. When Zn is the adsorbate, compounded Cu mainly affects the adsorption capacities of Fe/Mn and Fe/Mn/OMs; while when Cu is the adsorbate, compounded Zn mainly exerts its effect on Mn, Fe/Mn, and Mn/OMs. It also shows that the compounded Zn or Cu weakened the interference adsorption of Fe/Mn, and meanwhile, strengthened the interference adsorption of Mn/OMs.

Possibility to Use Hydrothermally Synthesized CuFeS2 Nanocomposite as an Acceptor in Hybrid Solar Cell

NASA Astrophysics Data System (ADS)

Sil, Sayantan; Dey, Arka; Halder, Soumi; Datta, Joydeep; Ray, Partha Pratim

2018-01-01

Here we have approached the plausible use of CuFeS2 nanocomposite as an acceptor in organic-inorganic hybrid solar cell. To produce CuFeS2 nanocomposite, hydrothermal strategy was employed. The room-temperature XRD pattern approves the synthesized material as CuFeS2 with no phase impurity (JCPDS Card no: 37-0471). The elemental composition of the material was analyzed from the TEM-EDX data. The obtained selected area electron diffraction (SAED) planes harmonized with the XRD pattern of the synthesized product. Optical band gap (4.14 eV) of the composite from UV-Vis analysis depicts that the synthesized material is belonging to wide band gap semiconductor family. The HOMO (- 6.97 eV) and LUMO (- 2.93 eV) positions from electrochemical study reveal that there is a possibility of electron transfer from MEH-PPV to CuFeS2. The optical absorption and photoluminescence spectra of MEH-PPV:CuFeS2 (donor:acceptor) composite were recorded sequentially by varying weight ratios. The monotonic blue shifting of the absorption peak position indicated the interaction between donor and acceptor materials. The possibility of electron transfer from donor (MEH-PPV) to acceptor (CuFeS2) was approved with photoluminescence analysis. Subsequently, we have fabricated a hybrid solar cell by incorporating CuFeS2 nanocomposite with MEH-PPV in open atmosphere and obtained 0.3% power conversion efficiency.

Molecular controls on Cu and Zn isotopic fractionation in Fe-Mn crusts

NASA Astrophysics Data System (ADS)

Little, S. H.; Sherman, D. M.; Vance, D.; Hein, J. R.

2014-06-01

The isotopic systems of the transition metals are increasingly being developed as oceanic tracers, due to their tendency to be fractionated by biological and/or redox-related processes. However, for many of these promising isotope systems the molecular level controls on their isotopic fractionations are only just beginning to be explored. Here we investigate the relative roles of abiotic and biotic fractionation processes in controlling modern seawater Cu and Zn isotopic compositions. Scavenging to Fe-Mn oxides represents the principal output for Cu and Zn to sediments deposited under normal marine (oxic) conditions. Using Fe-Mn crusts as an analogue for these dispersed phases, we investigate the phase association and crystal chemistry of Cu and Zn in such sediments. We present the results of an EXAFS study that demonstrate unequivocally that Cu and Zn are predominantly associated with the birnessite (δ-MnO2) phase in Fe-Mn crusts, as previously predicted from sequential leaching experiments (e.g., Koschinsky and Hein, 2003). The crystal chemistry of Cu and Zn in the crusts implies a reduction in coordination number in the sorbed phase relative to the free metal ion in seawater. Thus, theory would predict equilibrium fractionations that enrich the heavy isotope in the sorbed phase (e.g., Schauble, 2004). In natural samples, Fe-Mn crusts and nodules are indeed isotopically heavy in Zn isotopes (at ∼1‰) compared to deep seawater (at ∼0.5‰), consistent with the predicted direction of equilibrium isotopic fractionation based on our observations of the coordination environment of sorbed Zn. Further, ∼50% of inorganic Zn‧ is chloro-complexed (the other ∼50% is present as the free Zn2+ ion), and complexation by Cl- is also predicted to favour equilibrium partitioning of light Zn isotopes into the dissolved phase. The heavy Zn isotopic composition of Fe-Mn crusts and nodules relative to seawater can therefore be explained by an inorganic fractionation during uptake. However, Cu in Fe-Mn crusts is isotopically light (at ∼0.3 to 0.5‰) compared to the dissolved phase in seawater (at ∼0.9‰). We suggest that this is because dissolved Cu in the oceans is overwhelmingly complexed to strong organic ligands, which are better competitors for the heavy isotope.

Trace Metal Requirements for Microbial Enzymes Involved in the Production and Consumption of Methane and Nitrous Oxide

PubMed Central

Glass, Jennifer B.; Orphan, Victoria J.

2011-01-01

Fluxes of greenhouse gases to the atmosphere are heavily influenced by microbiological activity. Microbial enzymes involved in the production and consumption of greenhouse gases often contain metal cofactors. While extensive research has examined the influence of Fe bioavailability on microbial CO2 cycling, fewer studies have explored metal requirements for microbial production and consumption of the second- and third-most abundant greenhouse gases, methane (CH4), and nitrous oxide (N2O). Here we review the current state of biochemical, physiological, and environmental research on transition metal requirements for microbial CH4 and N2O cycling. Methanogenic archaea require large amounts of Fe, Ni, and Co (and some Mo/W and Zn). Low bioavailability of Fe, Ni, and Co limits methanogenesis in pure and mixed cultures and environmental studies. Anaerobic methane oxidation by anaerobic methanotrophic archaea (ANME) likely occurs via reverse methanogenesis since ANME possess most of the enzymes in the methanogenic pathway. Aerobic CH4 oxidation uses Cu or Fe for the first step depending on Cu availability, and additional Fe, Cu, and Mo for later steps. N2O production via classical anaerobic denitrification is primarily Fe-based, whereas aerobic pathways (nitrifier denitrification and archaeal ammonia oxidation) require Cu in addition to, or possibly in place of, Fe. Genes encoding the Cu-containing N2O reductase, the only known enzyme capable of microbial N2O conversion to N2, have only been found in classical denitrifiers. Accumulation of N2O due to low Cu has been observed in pure cultures and a lake ecosystem, but not in marine systems. Future research is needed on metalloenzymes involved in the production of N2O by enrichment cultures of ammonia oxidizing archaea, biological mechanisms for scavenging scarce metals, and possible links between metal bioavailability and greenhouse gas fluxes in anaerobic environments where metals may be limiting due to sulfide-metal scavenging. PMID:22363333

Giant magnetoresistance enhancement in spin valves with nano-oxide layers

NASA Astrophysics Data System (ADS)

Lai, Chih-Huang; Chen, C. J.; Chin, T. S.

2001-06-01

The magnetoresistance (MR) ratio is enhanced by 35% by inserting the nano-oxide layer (NOL) at the Ta/Co interface in the FeMn-based top spin valves (Ta/NOL/Co/Cu/Co/FeMn/Ta). The enhancement is attributed to specular reflection, resulting in a large resistance change and small sheet resistance. However, the formation of NOL at the interface of Ta/Co suppresses the (111) texture, resulting in small exchange fields. Top spin valves with NOLs show good thermal stability up to 200 °C annealing. The MR ratio is further increased after annealing at temperatures below 200 °C. Enhancement of the MR ratio by 61% can be achieved by annealing at 150 °C. For bottom spin valves (Ta/NiFe/FeMn/Co/Cu/NiFe/Ta), NOLs formed at FeMn/Co and NiFe/Ta interfaces increase MR ratios, but NOLs at Co/Cu or Cu/NiFe deteriorate the differential spin scattering and significantly reduce MR ratios.

Integrated photooxidative-extractive desulfurization system for fuel oil using Cu, Fe and Cu-Fe/TiO2 and eutectic based ionic liquids: Effect of calcination temperature and duration

NASA Astrophysics Data System (ADS)

Zaid, Hayyiratul Fatimah Mohd; Kait, Chong Fai; Mutalib, Mohamed Ibrahim Abdul

2014-10-01

Photocatalyts TiO2 doped with Cu, Fe and Cu-Fe metal at different calcination temperature and duration were successfully prepared and characterized. Photocatalytic oxidative desulfurization of model oil containing dibenzothiophene as the sulfur compound (100 ppm) using the prepared photocatalyst was investigated. The photocatalyst calcined at 500°C and duration of 1 h showed the best performance.

Iron, Manganese and Copper Release from Synthetic Hydroxyapatite

NASA Technical Reports Server (NTRS)

Sutter, B.; Hossner, L. R.; Ming, Douglas W.

1999-01-01

Kinetic stir-flow dissolution experiments were performed on iron- (Fe-SHA), manganese- (Mn-SHA), and copper- (Cu-SHA) containing synthetic hydroxyapatites. Solution treatments consisted of de-ionized water, citric acid and DTPA. Initially, Mn concentrations were higher than Cu concentrations and Fe concentrations were the lowest in all treatments. At later times Mn and Cu concentrations dropped in the DTPA treatment while Fe rose to the concentration similar to Mn and Cu. At all times, metal release concentrations in the water and citric acid treatments followed the trend of Mn>Cu>Fe. Rietveld analysis of x-ray diffraction data and ^31P NMR indicated that the metals substituted for Ca in the SHA structure. However, EPR data suggested that a metal (hydr)oxide phase existed either on the SHA surface or between the SHA crystallites. The metal concentration trend of Mn>Cu>Fe suggested that the initial solution metal concentrations are dependent on the dissolution of (hydr)oxides from SHA surfaces or between SHA crystallites. Similar metal concentrations at later times in the DTPA experiments suggests that metal concentrations were controlled by the release of Mn, Cu, or Fe from the SHA structure.

Rosette iron deficiency transcript and microRNA profiling reveals links between copper and iron homeostasis in Arabidopsis thaliana

PubMed Central

Waters, Brian M.; Stein, Ricardo J.

2012-01-01

Iron (Fe) is an essential plant micronutrient, and its deficiency limits plant growth and development on alkaline soils. Under Fe deficiency, plant responses include up-regulation of genes involved in Fe uptake from the soil. However, little is known about shoot responses to Fe deficiency. Using microarrays to probe gene expression in Kas-1 and Tsu-1 ecotypes of Arabidopsis thaliana, and comparison with existing Col-0 data, revealed conserved rosette gene expression responses to Fe deficiency. Fe-regulated genes included known metal homeostasis-related genes, and a number of genes of unknown function. Several genes responded to Fe deficiency in both roots and rosettes. Fe deficiency led to up-regulation of Cu,Zn superoxide dismutase (SOD) genes CSD1 and CSD2, and down-regulation of FeSOD genes FSD1 and FSD2. Eight microRNAs were found to respond to Fe deficiency. Three of these (miR397a, miR398a, and miR398b/c) are known to regulate transcripts of Cu-containing proteins, and were down-regulated by Fe deficiency, suggesting that they could be involved in plant adaptation to Fe limitation. Indeed, Fe deficiency led to accumulation of Cu in rosettes, prior to any detectable decrease in Fe concentration. ccs1 mutants that lack functional Cu,ZnSOD proteins were prone to greater oxidative stress under Fe deficiency, indicating that increased Cu concentration under Fe limitation has an important role in oxidative stress prevention. The present results show that Cu accumulation, microRNA regulation, and associated differential expression of Fe and CuSOD genes are coordinated responses to Fe limitation. PMID:22962679

Long term high temperature oxidation characteristics of La and Cu alloyed ferritic stainless steels for solid oxide fuel cell interconnects

NASA Astrophysics Data System (ADS)

Swaminathan, Srinivasan; Lee, Young-Su; Kim, Dong-Ik

2016-09-01

To ensure the best performance of solid oxide fuel cell metallic interconnects, the Fe-22 wt.% Cr ferritic stainless steels with various La contents (0.006-0.6 wt.%) and Cu addition (1.57 wt.%), are developed. Long-term isothermal oxidation behavior of these steels is investigated in air at 800 °C, for 2700 h. Chemistry, morphology, and microstructure of the thermally grown oxide scale are examined using XPS, SEM-EDX, and XRD techniques. Broadly, all the steels show a double layer consisting of an inner Cr2O3 and outer (Mn, Cr)3O4. Distinctly, in the La-added steels, binary oxides of Cr, Mn and Ti are found at the oxide scale surface together with (Mn, Cr)3O4. Furthermore, all La-varied steels possess the metallic Fe protrusions along with discontinuous (Mn, Cr)3O4 spinel zones at the oxide scale/metal interface and isolated precipitates of Ti-oxides in the underlying matrix. Increase of La content to 0.6 wt.% is detrimental to the oxidation resistance. For the Cu-added steel, Cu is found to segregate strongly at the oxide scale/metal interface which inhibits the ingress of oxygen thereby suppressing the subscale formation of (Mn, Cr)3O4. Thus, Cu addition to the Fe-22Cr ferritic stainless steels benefits the oxidation resistance.

Oxidation behavior and area specific resistance of La, Cu and B alloyed Fe-22Cr ferritic steels for solid oxide fuel cell interconnects

NASA Astrophysics Data System (ADS)

Swaminathan, Srinivasan; Ko, Yoon Seok; Lee, Young-Su; Kim, Dong-Ik

2017-11-01

Two Fe-22 wt% Cr ferritic stainless steels containing varying concentrations of La (0.14 or 0.52 wt%), Cu (0.17 or 1.74 wt%) and B (48 or 109 ppm) are investigated with respect to oxidation behavior and high temperature area specific resistance (ASR) of the surface oxide scales. To determine the oxidation resistance of developed steels, continuous isothermal oxidation is carried out at 800 °C in air, for 2000 h, and their thermally grown oxide scale is characterized using dynamic SIMS, SEM/EDX, XRD and GI-XRD techniques. To assess their electrical performance, the ASR measurement by four-point probe method is conducted at 800 °C in air, for 400 h. In higher La content steel, the La-oxides at the scale/alloy interface promotes the oxygen transport which resulted in sub-surface oxidation of Mn, Cr, Ti and Al. Moreover, the inward growth of oxides contributes to increase of Fe-Cr alloy protrusions within the scale, which reduced the ASR. In contrast, sub-surface oxidation is reduced in high Cu-alloyed steel by segregated Cu at the scale/alloy interface. Thus, addition of Cu is effective to oxidation resistance and also to better electrical performance. However, no obvious impact of B on the scale sequence and/or ASR is observed.

Evidence of cross-cutting and redox reaction in Khatyrka meteorite reveals metallic-Al minerals formed in outer space.

PubMed

Lin, Chaney; Hollister, Lincoln S; MacPherson, Glenn J; Bindi, Luca; Ma, Chi; Andronicos, Christopher L; Steinhardt, Paul J

2017-05-09

We report on a fragment of the quasicrystal-bearing CV3 carbonaceous chondrite Khatyrka recovered from fine-grained, clay-rich sediments in the Koryak Mountains, Chukotka (Russia). We show higher melting-point silicate glass cross-cutting lower melting-point Al-Cu-Fe alloys, as well as unambiguous evidence of a reduction-oxidation reaction history between Al-Cu-Fe alloys and silicate melt. The redox reactions involve reduction of FeO and SiO 2 to Fe and Fe-Si metal, and oxidation of metallic Al to Al 2 O 3 , occurring where silicate melt was in contact with Al-Cu-Fe alloys. In the reaction zone, there are metallic Fe and Fe-Si beads, aluminous spinel rinds on the Al-Cu-Fe alloys, and Al 2 O 3 enrichment in the silicate melt surrounding the alloys. From this and other evidence, we demonstrate that Khatyrka must have experienced at least two distinct events: first, an event as early as 4.564 Ga in which the first Al-Cu-Fe alloys formed; and, second, a more recent impact-induced shock in space that led to transformations of and reactions between the alloys and the meteorite matrix. The new evidence firmly establishes that the Al-Cu-Fe alloys (including quasicrystals) formed in outer space in a complex, multi-stage process.

Iron Sulfide Attenuates the Methanogenic Toxicity of Elemental Copper and Zinc Oxide Nanoparticles and their Soluble Metal Ion Analogs

PubMed Central

Gonzalez-Estrella, Jorge; Gallagher, Sara; Sierra-Alvarez, Reyes; Field, Jim A.

2016-01-01

Elemental copper (Cu0) and zinc oxide (ZnO) nanoparticle (NP) toxicity to methanogens has been attributed to the release of soluble metal ions. Iron sulfide (FeS) partially controls the soluble concentration of heavy metals and their toxicity in aquatic environments. Heavy metals displace the Fe from FeS forming poorly soluble metal sulfides in the FeS matrix. Therefore, FeS may be expected to attenuate the NP toxicity. This work assessed FeS as an attenuator of the methanogenic toxicity of Cu0 and ZnO NPs and their soluble salt analogs. The toxicity attenuation capacity of fine (25–75 µm) and coarse (500 to 1200 µm) preparations of FeS (FeS-f and FeS-c respectively) was tested in the presence of highly inhibitory concentrations of CuCl2, ZnCl2 Cu0 and ZnO NPs. FeS-f attenuated methanogenic toxicity better than FeS-c. The results revealed that 2.5× less FeS-f than FeS-c was required to recover the methanogenic activity to 50% (activity normalized to uninhibited controls). The results also indicated that a molar FeS-f/Cu0 NP, FeS-f/ZnO NP, FeS-f/ZnCl2, and FeS-f/CuCl2 ratio of 2.14, 2.14, 4.28, and 8.56 respectively, was necessary to recover the methanogenic activity to >75%. Displacement experiments demonstrated that CuCl2 and ZnCl2 partially displaced Fe from FeS. As a whole, the results indicate that not all the sulfide in FeS was readily available to react with the soluble Cu and Zn ions which may explain the need for a large stoichiometric excesses of FeS to highly attenuate Cu and Zn toxicity. Overall, this study provides evidence that FeS attenuates the toxicity caused by Cu0 and ZnO NPs and their soluble ion analogs to methanogens. PMID:26803736

Chemical looping combustion: A new low-dioxin energy conversion technology.

PubMed

Hua, Xiuning; Wang, Wei

2015-06-01

Dioxin production is a worldwide concern because of its persistence and carcinogenic, teratogenic, and mutagenic effects. The pyrolysis-chemical looping combustion process of disposing solid waste is an alternative to traditional solid waste incineration developed to reduce the dioxin production. Based on the equilibrium composition of the Deacon reaction, pyrolysis gas oxidized by seven common oxygen carriers, namely, CuO, NiO, CaSO4, CoO, Fe2O3, Mn3O4, and FeTiO3, is studied and compared with the pyrolysis gas directly combusted by air. The result shows that the activity of the Deacon reaction for oxygen carriers is lower than that for air. For four typical oxygen carriers (CuO, NiO, Fe2O3, and FeTiO3), the influences of temperature, pressure, gas composition, and tar on the Deacon reaction are discussed in detail. According to these simulation results, the dioxin production in China, Europe, the United States, and Japan is predicted for solid waste disposal by the pyrolysis-chemical looping combustion process. Thermodynamic analysis results in this paper show that chemical looping combustion can reduce dioxin production in the disposal of solid waste. Copyright © 2015. Published by Elsevier B.V.

Magnetic properties of (SrFe{sub 12}O{sub 19}){sub x}(CaCu{sub 3}Ti{sub 4}O{sub 12}){sub 1–x} composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eremina, R. M., E-mail: REremina@yandex.ru; Sharipov, K. R.; Yatsyk, I. V.

2016-07-15

New composite materials (SrFe{sub 12}O{sub 19}){sub x}(CaCu{sub 3}Ti{sub 4}O{sub 12}){sub 1–x} (x = 0, 0.05, 1) have been synthesized. Their magnetic properties are studied in the temperature range 5–300 K using the magnetic resonance and magnetometry methods. It is found that strontium hexaferrite microinclusions in the (SrFe{sub 12}O{sub 19}){sub 0.05}(CaCu{sub 3}Ti{sub 4}O{sub 12}){sub 0.95} composite “magnetize” CaCu{sub 3}Ti{sub 4}O{sub 12} at temperatures from 300 to 200 K, forming a ferrimagnetic particle near the SrFe{sub 12}O{sub 19} “core.” The magnetic resonance line below 200 K splits into two lines corresponding to SrFe{sub 12}O{sub 19} and CaCu{sub 3}Ti{sub 4}O{sub 12}. The coremore » effect decoration is manifested in the increase in the Curie–Weiss temperature from 25 K in CaCu{sub 3}Ti{sub 4}O{sub 12} without the doping ceramics to 80 K in the composite with 5% of SrFe{sub 12}O{sub 19}.« less

Ni exposure impacts the pool of free Fe and modifies DNA supercoiling via metal-induced oxidative stress in Escherichia coli K-12.

PubMed

Gault, Manon; Effantin, Géraldine; Rodrigue, Agnès

2016-08-01

The biology of nickel has been widely studied in mammals because of its carcinogenic properties, whereas few studies have been performed in microorganisms. In the present work, changes accompanying stress caused by nickel were evaluated at the cellular level using RNA-Seq in Escherichia coli K-12. Interestingly, a very large number of genes were found to be deregulated by Ni stress. Iron and oxidative stress homeostasis maintenance were among the most highly enriched functional categories, and genes involved in periplasmic copper efflux were among the most highly upregulated. These results suggest that the deregulation of Fe and Cu homeostatic genes is caused by a release of free Cu and Fe ions in the cell which in turn activate the Cu and Fe homeostatic systems. The content of Cu was not significantly affected upon the addition of Ni to the growth medium, nor were the Cus and CopA Cu-efflux systems important for the survival of bacteria under Ni stress In contrast the addition of Ni slightly decreased the amount of cellular Fe and activated the transcription of Fur regulated genes in a Fur-dependent manner. Cu or Fe imbalance together with oxidative stress might affect the structure of DNA. Further experiments revealed that Ni alters the state of DNA folding by causing a relaxed conformation, a phenomenon that is reversible by addition of the antioxidant Tiron or the Fe chelator Dip. The Tiron-reversible DNA relaxation was also observed for Fe and to a lesser extent with Cu but not with Co. DNA supercoiling is well recognized as an integral aspect of gene regulation. Moreover our results show that Ni modifies the expression of several nucleoid-associated proteins (NAPs), important agents of DNA topology and global gene regulation. This is the first report describing the impact of metal-induced oxidative on global regulatory networks. Copyright © 2016 Elsevier Inc. All rights reserved.

Composition gradient, structure, stress, roughness and magnetic properties of 5-500 nm thin NiFe films obtained by electrodeposition

NASA Astrophysics Data System (ADS)

Gong, Jie; Riemer, Steve; Kautzky, Michael; Tabakovic, Ibro

2016-01-01

The composition gradients of 5-500 nm thin NiFe films on Cu and NiP substrates obtained by electrodeposition in stirred plating solutions at pH 3.0 on 8 in wafers were studied. It was found that the average elemental composition of the NiFe changes during electrodeposition with steep downturns of Fe-content, from 58 to 50 wt% Fe, in composition gradient zone near the substrate interface in the thickness range 5-250 nm depending on the electrode substrate (Cu and NiP). The increase of Fe-content in the composition gradient zone is accompanied by the increase of coercivity, Hc, magnetic flux saturation, Bs, saturation magnetostriction, λs, increase of dimensionless roughness, ρrms, and change of stress, σ. The coercivity (easy and hard axis) follows the Neel's relation Hc=ct-n (t is thickness and c is a constant). The mechanisms related to the change of coercivity of the NiFe films deposited on different substrates (Cu and NiP) are discussed in terms of material properties of these films.

Complex permeability and permittivity spectra of percolated Fe50Co50/Cu granular composites

NASA Astrophysics Data System (ADS)

Massango, Herieta; Tsutaoka, Takanori; Kasagi, Teruhiro; Yamamoto, Shinichiro; Hatakeyama, Kenichi

2017-11-01

Complex permeability and permittivity spectra of Fe50Co50/Cu hybrid granular composite materials have been studied in the RF to microwave frequency range. At low Cu particle content, the Fe50Co50/Cu hybrid sample shows a metallic percolative property with the electrical conductivity value about 0.1 S/cm. However, the low frequency plasmonic (LFP) state with negative permittivity (ENG) spectrum was not observed. An abrupt increase of electrical conductivity takes place at 14 to 16 vol% Cu content where the conductivity becomes above 1.0 S/cm; the Fe50Co50/Cu composite possesses the LFP state with negative permittivity spectrum below a characteristic frequency. The complex permittivity spectra in the LFP state can be described by the Drude model. Magnetic permeability spectrum in the LFP state showed a broad frequency dispersion above 10 MHz; a small negative permeability (MNG) dispersion was observed from 2 to 10 GHz. Consequently, the double negative (DNG) electromagnetic property with MNG and ENG was realized in the microwave range for the Cu content of 26 and 30 vol%.

Drastic influence of minor Fe or Co additions on the glass forming ability, martensitic transformations and mechanical properties of shape memory Zr-Cu-Al bulk metallic glass composites.

PubMed

González, Sergio; Pérez, Pablo; Rossinyol, Emma; Suriñach, Santiago; Dolors Baró, Maria; Pellicer, Eva; Sort, Jordi

2014-06-01

The microstructure and mechanical properties of Zr 48 Cu 48 -  x Al 4 M x (M ≡ Fe or Co, x  = 0, 0.5, 1 at.%) metallic glass (MG) composites are highly dependent on the amount of Fe or Co added as microalloying elements in the parent Zr 48 Cu 48 Al 4 material. Addition of Fe and Co promotes the transformation from austenite to martensite during the course of nanoindentation or compression experiments, resulting in an enhancement of plasticity. However, the presence of Fe or Co also reduces the glass forming ability, ultimately causing a worsening of the mechanical properties. Owing to the interplay between these two effects, the compressive plasticity for alloys with x  = 0.5 (5.5% in Zr 48 Cu 47.5 Al 4 Co 0.5 and 6.2% in Zr 48 Cu 47.5 Al 4 Fe 0.5 ) is considerably larger than for Zr 48 Cu 48 Al 4 or the alloys with x  = 1. Slight variations in the Young's modulus (around 5-10%) and significant changes in the yield stress (up to 25%) are also observed depending on the composition. The different microstructural factors that have an influence on the mechanical behavior of these composites are investigated in detail: (i) co-existence of amorphous and crystalline phases in the as-cast state, (ii) nature of the crystalline phases (austenite versus martensite content), and (iii) propensity for the austenite to undergo a mechanically-driven martensitic transformation during plastic deformation. Evidence for intragranular nanotwins likely generated in the course of the austenite-martensite transformation is provided by transmission electron microscopy. Our results reveal that fine-tuning of the composition of the Zr-Cu-Al-(Fe,Co) system is crucial in order to optimize the mechanical performance of these bulk MG composites, to make them suitable materials for structural applications.

Drastic influence of minor Fe or Co additions on the glass forming ability, martensitic transformations and mechanical properties of shape memory Zr-Cu-Al bulk metallic glass composites

NASA Astrophysics Data System (ADS)

González, Sergio; Pérez, Pablo; Rossinyol, Emma; Suriñach, Santiago; Baró, Maria Dolors; Pellicer, Eva; Sort, Jordi

2014-06-01

The microstructure and mechanical properties of Zr48Cu48 - x Al4M x (M ≡ Fe or Co, x = 0, 0.5, 1 at.%) metallic glass (MG) composites are highly dependent on the amount of Fe or Co added as microalloying elements in the parent Zr48Cu48Al4 material. Addition of Fe and Co promotes the transformation from austenite to martensite during the course of nanoindentation or compression experiments, resulting in an enhancement of plasticity. However, the presence of Fe or Co also reduces the glass forming ability, ultimately causing a worsening of the mechanical properties. Owing to the interplay between these two effects, the compressive plasticity for alloys with x = 0.5 (5.5% in Zr48Cu47.5Al4Co0.5 and 6.2% in Zr48Cu47.5Al4Fe0.5) is considerably larger than for Zr48Cu48Al4 or the alloys with x = 1. Slight variations in the Young’s modulus (around 5-10%) and significant changes in the yield stress (up to 25%) are also observed depending on the composition. The different microstructural factors that have an influence on the mechanical behavior of these composites are investigated in detail: (i) co-existence of amorphous and crystalline phases in the as-cast state, (ii) nature of the crystalline phases (austenite versus martensite content), and (iii) propensity for the austenite to undergo a mechanically-driven martensitic transformation during plastic deformation. Evidence for intragranular nanotwins likely generated in the course of the austenite-martensite transformation is provided by transmission electron microscopy. Our results reveal that fine-tuning of the composition of the Zr-Cu-Al-(Fe,Co) system is crucial in order to optimize the mechanical performance of these bulk MG composites, to make them suitable materials for structural applications.

Positron Annihilation Spectroscopy and Small Angle Neutron Scattering Characterization of Nanostructural Features in Irradiated Fe-Cu-Mn Alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wirth, B D; Asoka-Kumar, P; Howell, R H

2001-01-01

Radiation embrittlement of nuclear reactor pressure vessel steels results from a high number density of nanometer sized Cu-Mn-Ni rich precipitates (CRPs) and sub-nanometer matrix features, thought to be vacancy-solute cluster complexes (VSC). However, questions exist regarding both the composition of the precipitates and the defect character and composition of the matrix features. We present results of positron annihilation spectroscopy (PAS) and small angle neutron scattering (SANS) characterization of irradiated and thermally aged Fe-Cu and Fe-Cu-Mn alloys. These complementary techniques provide insight into the composition and character of both types of nanoscale features. The SANS measurements indicate populations of CRPs andmore » VSCs in both alloys. The CRPs are coarser in the Fe-Cu alloy and the number densities of CRP and VSC increase with the addition of Mn. The PAS involved measuring both the positron lifetimes and the Doppler broadened annihilation spectra in the high momentum region to provide elemental sensitivity at the annihilation site. The spectra in Fe-Cu-Mn specimens thermally aged to peak hardness at 450 C and irradiated at 288 C are nearly identical to elemental Cu. Positron lifetime and spectrum measurements in Fe-Cu specimens irradiated at 288 C clearly show the existence of long lifetime ({approx}500 ps) open volume defects, which also contain Cu. Thus the SANS and PAS provide a self-consistent picture of nanostructures composed of CRPs and VSCs and tend to discount high Fe concentrations in the CRPs.« less

Introducing a 2-His-1-Glu Nonheme Iron Center into Myoglobin Confers Nitric Oxide Reductase Activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Y.W.; Robinson, H.; Yeung, N.

2010-07-28

A conserved 2-His-1-Glu metal center, as found in natural nonheme iron-containing enzymes, was engineered into sperm whale myoglobin by replacing Leu29 and Phe43 with Glu and His, respectively (swMb L29E, F43H, H64, called Fe{sub B}Mb(-His)). A high resolution (1.65 {angstrom}) crystal structure of Cu(II)-CN?-Fe{sub B}Mb(-His) was determined, demonstrating that the unique 2-His-1-Glu metal center was successfully created within swMb. The Fe{sub B}Mb(-His) can bind Cu, Fe, or Zn ions, with both Cu(I)-Fe{sub B}Mb(-His) and Fe(II)-Fe{sub B}Mb(-His) exhibiting nitric oxide reductase (NOR) activities. Cu dependent NOR activity was significantly higher than that of Fe in the same metal binding site. EPRmore » studies showed that the reduction of NO to N{sub 2}O catalyzed by these two enzymes resulted in different intermediates; a five-coordinate heme-NO species was observed for Cu(I)-Fe{sub B}Mb(-His) due to the cleavage of the proximal heme Fe-His bond, while Fe(II)-Fe{sub B}Mb(-His) remained six-coordinate. Therefore, both the metal ligand, Glu29, and the metal itself, Cu or Fe, play crucial roles in NOR activity. This study presents a novel protein model of NOR and provides insights into a newly discovered member of the NOR family, gNOR.« less

Dimensionally stable metallic hydride composition

DOEpatents

Heung, Leung K.

1994-01-01

A stable, metallic hydride composition and a process for making such a composition. The composition comprises a uniformly blended mixture of a metal hydride, kieselguhr, and a ballast metal, all in the form of particles. The composition is made by subjecting a metal hydride to one or more hydrogen absorption/desorption cycles to disintegrate the hydride particles to less than approximately 100 microns in size. The particles are partly oxidized, then blended with the ballast metal and the kieselguhr to form a uniform mixture. The mixture is compressed into pellets and calcined. Preferably, the mixture includes approximately 10 vol. % or more kieselguhr and approximately 50 vol. % or more ballast. Metal hydrides that can be used in the composition include Zr, Ti, V, Nb, Pd, as well as binary, tertiary, and more complex alloys of La, Al, Cu, Ti, Co, Ni, Fe, Zr, Mg, Ca, Mn, and mixtures and other combinations thereof. Ballast metals include Al, Cu and Ni.

Effect of nickel addition on mechanical properties of powder forged Fe-Cu-C

NASA Astrophysics Data System (ADS)

Archana Barla, Nikki

2018-03-01

Fe-Cu-C system is very popular in P/M industry for its good compressibility and dimensional stability with high strength. Fe-Cu-C is a structural material and is used where high strength with high hardness is required. The composition of powder metallurgy steel plays a vital role in the microstructure and physical properties of the sintered component. Fe-2Cu-0.7C-Ni alloy with varying nickel composition (0%, 0.5%, 1.0%, 1.5%, 2.0%, and 3.0%) wt. % was prepared by powder metallurgy (P/M) sinter forging process. The present work discuss the effect of varying nickel content on microstructure and mechanical properties.

The geochemical cycling of trace elements in a biogenic meromictic lake

NASA Astrophysics Data System (ADS)

Balistrieri, Laurie S.; Murray, James W.; Paul, Barbara

1994-10-01

The geochemical processes affecting the behavior and speciation of As, Co, Cr, Cu, Fe, Mn, Mo, Ni, Pb, V, and Zn in Hall Lake, Washington, USA, are assessed by examining dissolved and acid soluble particulate profiles of the elements and utilizing results from thermodynamic calculations. The water column of this meromictic lake is highly stratified and contains distinctive oxic, suboxic, and anoxic layers. Changes in the redox state of the water column with depth affect the distribution of all the elements studied. Most noticeable are increases in dissolved Co, Cr, Fe, Mn, Ni, Pb, and Zn concentrations across the oxic-suboxic boundary, increases in dissolved As, Co, Cr, Fe, Mn, and V concentrations with depth in the anoxic layer, significant decreases in dissolved Cu, Ni, Pb, and Zn concentrations in the anoxic region below the sulfide maximum, and large increases in acid soluble particulate concentrations of As, Cr, Cu, Fe, Mo, Ni, Pb, V, and Zn in the anoxic zone below the sulfide maximum. Thermodynamic calculations for the anoxic region indicate that all redox sensitive elements exist in their reduced forms, the primary dissolved forms of Cu, Ni, Pb, and Zn are metal sulfide solution complexes, and solid sulfide phases of Cu, Fe, Mo, and Pb are supersaturated. Calculations using a vertical diffusion and reaction model indicate that the oxidation rate constant for Mn(II) in Hall Lake is estimated to be 0.006 d -1 and is at the lower end of the range of microbial oxidation rates observed in other natural systems. The main geochemical processes influencing the distribution and speciation of trace elements in Hall Lake appear to be transformations of dissolved elements between their oxidation states (As, Cr, Cu, Fe, Mn, V), cocycling of trace elements with Mn and Fe (As, Co, Cr, Cu, Mo, Ni, Pb, V, Zn), formation of soluble metal sulfide complexes (Co, Cu, Ni, Pb, Zn), sorption (As, Co, Cr, Ni, V), and precipitation (Cu, Fe, Mn, Mo, Pb, Zn).

The geochemical cycling of trace elements in a biogenic meromictic lake

USGS Publications Warehouse

Balistrieri, L.S.; Murray, J.W.; Paul, B.

1994-01-01

The geochemical processes affecting the behavior and speciation of As, Co, Cr, Cu, Fe, Mn, Mo, Ni, Pb, V, and Zn in Hall Lake, Washington, USA, are assessed by examining dissolved and acid soluble particulate profiles of the elements and utilizing results from thermodynamic calculations. The water column of this meromictic lake is highly stratified and contains distinctive oxic, suboxic, and anoxic layers. Changes in the redox state of the water column with depth affect the distribution of all the elements studied. Most noticeable are increases in dissolved Co, Cr, Fe, Mn, Ni, Pb, and Zn concentrations across the oxic-suboxic boundary, increases in dissolved As, Co, Cr, Fe, Mn, and V concentrations with depth in the anoxic layer, significant decreases in dissolved Cu, Ni, Pb, and Zn concentrations in the anoxic region below the sulfide maximum, and large increases in acid soluble particulate concentrations of As, Cr, Cu, Fe, Mo, Ni, Pb, V, and Zn in the anoxic zone below the sulfide maximum. Thermodynamic calculations for the anoxic region indicate that all redox sensitive elements exist in their reduced forms, the primary dissolved forms of Cu, Ni, Pb, and Zn are metal sulfide solution complexes, and solid sulfide phases of Cu, Fe, Mo, and Pb are supersaturated. Calculations using a vertical diffusion and reaction model indicate that the oxidation rate constant for Mn(II) in Hall Lake is estimated to be 0.006 d-1 and is at the lower end of the range of microbial oxidation rates observed in other natural systems. The main geochemical processes influencing the distribution and speciation of trace elements in Hall Lake appear to be transformations of dissolved elements between their oxidation states (As, Cr, Cu, Fe, Mn, V), cocycling of trace elements with Mn and Fe (As, Co, Cr, Cu, Mo, Ni, Pb, V, Zn), formation of soluble metal sulfide complexes (Co, Cu, Ni, Pb, Zn), sorption (As, Co, Cr, Ni, V), and precipitation (Cu, Fe, Mn, Mo, Pb, Zn). ?? 1994.

Reactivity of food phenols with iron and copper ions: binding, dioxygen activation and oxidation mechanisms.

PubMed

Nkhili, Ezzohra; Loonis, Michèle; Mihai, Simona; El Hajji, Hakima; Dangles, Olivier

2014-06-01

In this work, the affinity of common dietary phenols (gallic acid, caffeic acid, catechin, and rutin) for iron and copper ions was quantitatively investigated in neutral phosphate buffer as well as the reactivity of the complexes toward dioxygen. Contrasting behaviors were observed: because of the competing phosphate ions, Fe(III) binding is much slower than Fe(II) binding, which is rapidly followed by autoxidation of Fe(II) into Fe(III). With both ions, O2 consumption and H2O2 production are modest and the phenolic ligands are only slowly oxidized. By contrast, metal-phenol binding is fast with both Cu(I) and Cu(II). With Cu(I), O2 consumption and H2O2 production are very significant and the phenolic ligands are rapidly oxidized into a complex mixture of oligomers. The corresponding mechanism with Cu(II) is hampered by the preliminary rate-determining step of Cu(II) reduction by the phenols. The consequences of these findings for the stability and antioxidant activity of plant phenols are discussed.

Corrosion behavior and oxide properties of Zr 1.1 wt%Nb 0.05 wt%Cu alloy

NASA Astrophysics Data System (ADS)

Park, Jeong-Yong; Choi, Byung-Kwon; Yoo, Seung Jo; Jeong, Yong Hwan

2006-12-01

The corrosion behavior and oxide properties of Zr-1.1 wt%Nb-0.05 wt%Cu (ZrNbCu) and Zircaloy-4 have been investigated. The corrosion rate of the ZrNbCu alloy was much lower than that of the Zirclaoy-4 in the 360 °C water and 360 °C PWR-simulating loop condition without a neutron flux and it was increased with an increase of the final annealing temperature from 470 °C to 570 °C. TEM observations revealed that the precipitates in the ZrNbCu were β-Nb and ZrNbFe-precipitate with β-Nb being more frequently observed and that the precipitates were more finely distributed in the ZrNbCu alloy. It was also observed that the oxides of the ZrNbCu and Zircaloy-4 consisted of two and seven layers, respectively, after 1000 days in the PWR-simulating loop condition and that the thickness of a fully-developed layer was higher in the ZrNbCu than in the Zircaloy-4. It was also found that the β-Nb in ZrNbCu was oxidized more slowly when compared to the Zr(Fe, Cr) 2 in Zirclaoy-4 when the precipitates in the oxide were observed by TEM. Cracks were observed in the vicinity of the oxidized Zr(Fe, Cr) 2, while no cracks were formed near β-Nb which had retained a metallic state. From the results obtained, it is suggested that the oxide formed on the ZrNbCu has a more protective nature against a corrosion when compared to that of the Zircaloy-4.

Coexistence of Cu, Fe, Pb, and Zn oxides and chlorides as a determinant of chlorinated aromatics generation in municipal solid waste incinerator fly ash.

PubMed

Fujimori, Takashi; Tanino, Yuta; Takaoka, Masaki

2014-01-01

We investigated chemical determinants of the generation of chlorinated aromatic compounds (aromatic-Cls), such as polychlorinated biphenyls (PCBs) and chlorobenzenes (CBzs), in fly ash from municipal solid waste incineration. The influences of the following on aromatic-Cls formation in model fly ash (MFA) were systematically examined quantitatively and statistically: (i) inorganic chlorides (KCl, NaCl, CaCl2), (ii) base materials (SiO2, Al2O3, CaCO3), (iii) metal oxides (CuO, Fe2O3, PbO, ZnO), (iv) metal chlorides (CuCl2, FeCl3, PbCl2, ZnCl2), and (v) "coexisting multi-models." On the basis of aromatic-Cls concentrations, the ∑CBzs/∑PCBs ratio, and the similarity between distribution patterns, MFAs were categorized into six groups. The results and analysis indicated that the formation of aromatic-Cls depended strongly on the "coexistence condition", namely multimodels composed of not only metal chlorides, but also of metal oxides. The precise replication of metal chloride to oxide ratios, such as the precise ratios of Cu-, Fe-, Pb-, and Zn-chlorides and oxides, may be an essential factor in changing the thermochemical formation patterns of aromatic-Cls. Although CuCl2 acted as a promoter of aromatic-Cls generation, statistical analyses implied that FeCl3 also largely influenced the generation of aromatic-Cls under mixture conditions. Various additional components of fly ash were also comprehensively analyzed.

Exchange biased and closed-flux pseudo spin-valve materials, device applications, and electrical reliability

NASA Astrophysics Data System (ADS)

Bae, Seongtae

Since giant magnetoresistance (GMR) and tunneling magnetoresistance (TMR) spinvalve effects were developed for the last two decades after discovered, world wide researches on applying these effects for various kinds of solid state active devices has provided a strong impact on challenging new functional micro-magnetoelectronic devices. In particular, recently developed nano-structured magnetic spin-valve thin film materials for spin-electronic devices are now considered as building blocks of state-of-the-art electronic engineering. This research has been concentrated on developing and designing magneto-electronic solid state devices with high thermal and electrical stability using an alpha-Fe 2O3 and NiO oxide anti-ferromagnetic exchange biased GMR bottom spin-valves (BSV), NiFe/Cu/Co and NiFe/Cu/CoFe based closed-flux metallic pseudo spin-valves, and PtMn exchange biased TMR spin-valves. The category covering this research is divided into four main research steps. First is to investigate exchange bias coupling characteristics of alpha-Fe2 O3 and NiO oxide Anti-ferromagnetic materials (AF)/Ferromagnetic (F) layer systems for optimizing exchange biased BSV and to study magnetic properties of various kinds of magnetic thin films including single through multi-layered structures for the fundamental research on NiFe/Cu/Co and NiFe/Cu/CoFe closed-flux metallic pseudo spin-valves. Second is to develop and improve new kinds of BSVs and closed-flux metallic spinvalves by controlling process parameters in terms of crystalline orientation texture of AF and F layers, interfacial surface roughness, grain size (its size distribution), chemical composition, and kinetics of sputtering film growth. Third is to design, to fabricate, and to investigate the magnetic and electrical properties of magneto-electronic devices as well as their applications such as GMR magnetoresistive random access memory (MRAM), GMR read head, TMR read head, and new kinds of GMR solid state devices, which can be promisingly substituted for current microelectronic devices. Finally, the last is to focus on studying electrical reliability of GMR read sensor and GMR MRAM cell in terms of electromigration-induced failures of various kinds of magnetic thin films, which are currently used in GMR spin-valve materials, and is to investigate the effects of current (or voltage) induced dielectric breakdown in aluminum oxide tunnel barrier under various testing conditions on the electrical stability of real TMR read sensors.

The aluminosilicate fraction of North Pacific manganese nodules

USGS Publications Warehouse

Bischoff, J.L.; Piper, D.Z.; Leong, K.

1981-01-01

Nine nodules collected from throughout the deep North Pacific were analyzed for their mineralogy and major-element composition before and after leaching with Chester-Hughes solution. Data indicate that the mineral phillipsite accounts for the major part (> 75%) of the aluminosilicate fraction of all nodules. It is suggested that formation of phillipsite takes place on growing nodule surfaces coupled with the oxidation of absorbed manganous ion. All the nodules could be described as ternary mixtures of amorphous iron fraction (Fe-Ti-P), manganese oxide fraction (Mn-Mg Cu-Ni), and phillipsite fraction (Al-Si-K-Na), these fractions accounting for 96% of the variability of the chemical composition. ?? 1981.

Antifriction coating of Cu-Fe-Al-Pb system for plain bearings

NASA Astrophysics Data System (ADS)

Kotenkov, Pavel; Kontsevoi, Yurii; Mejlakh, Anna; Pastukhov, Eduard; Shubin, Alexey; Goyda, Eduard; Sipatov, Ivan

2017-09-01

Aluminium, copper and their compounds are used in common as basis for antifriction coatings of plain bearings. Antifriction testing of plain bearings (based on Al and Cu) made by leading automotive manufacturers from Germany, Japan, USA, United Kingdom and Russia were carried out to make judicious selection of basis for development of new antifriction material. Testing was carried out using friction machine. It was defined that materials based on Cu provide better durability and robustness of plain bearings in comparison with Al based ones. The new antifriction composite coatings based on copper were developed taking into account the requirements specified for plain bearings of internal-combustion engine. Pilot samples of plain bearings with antifriction coatings of Cu-Fe-Al-Pb system were produced. The antifriction composite having Cu-5Fe-5Al5Fe2-10Pb (mass %) composition has demonstrated low friction factor and high wear-resistance. Metallographic analysis of pilot samples was carried out by means of optical and scanning electron microscopy.

Iron Oxide-Supported Copper Oxide Nanoparticles (Nanocat-Fe-CuO): Magnetically Recyclable Catalysts for the Synthesis of Pyrazole Derivatives, 4-Methoxyaniline, and Ullmann-type Condensation Reactions

EPA Science Inventory

An efficient and benign protocol is reported for the synthesis of 4-methoxyaniline, medicinally important pyrazole derivatives, and Ullmann-type condensation reaction using magnetically separable and reusable magnetite-supported copper (nanocat-Fe-CuO) nanoparticles under mild co...

Dopaminergic Neurons Respond to Iron-Induced Oxidative Stress by Modulating Lipid Acylation and Deacylation Cycles

PubMed Central

Sánchez Campos, Sofía; Rodríguez Diez, Guadalupe; Oresti, Gerardo Martín; Salvador, Gabriela Alejandra

2015-01-01

Metal-imbalance has been reported as a contributor factor for the degeneration of dopaminergic neurons in Parkinson Disease (PD). Specifically, iron (Fe)-overload and copper (Cu) mis-compartmentalization have been reported to be involved in the injury of dopaminergic neurons in this pathology. The aim of this work was to characterize the mechanisms of membrane repair by studying lipid acylation and deacylation reactions and their role in oxidative injury in N27 dopaminergic neurons exposed to Fe-overload and Cu-supplementation. N27 dopaminergic neurons incubated with Fe (1mM) for 24 hs displayed increased levels of reactive oxygen species (ROS), lipid peroxidation and elevated plasma membrane permeability. Cu-supplemented neurons (10, 50 μM) showed no evidence of oxidative stress markers. A different lipid acylation profile was observed in N27 neurons pre-labeled with [3H] arachidonic acid (AA) or [3H] oleic acid (OA). In Fe-exposed neurons, AA uptake was increased in triacylglycerols (TAG) whereas its incorporation into the phospholipid (PL) fraction was diminished. TAG content was 40% higher in Fe-exposed neurons than in controls. This increase was accompanied by the appearance of Nile red positive lipid bodies. Contrariwise, OA incorporation increased in the PL fractions and showed no changes in TAG. Lipid acylation profile in Cu-supplemented neurons showed AA accumulation into phosphatidylserine and no changes in TAG. The inhibition of deacylation/acylation reactions prompted an increase in oxidative stress markers and mitochondrial dysfunction in Fe-overloaded neurons. These findings provide evidence about the participation of lipid acylation mechanisms against Fe-induced oxidative injury and postulate that dopaminergic neurons cleverly preserve AA in TAG in response to oxidative stress. PMID:26076361

Influence of Composition on the Environmental Impact of a Cast Aluminum Alloy

PubMed Central

Gómez, Patricia; Elduque, Daniel; Sarasa, Judith; Pina, Carmelo; Javierre, Carlos

2016-01-01

The influence of alloy composition on the environmental impact of the production of six aluminum casting alloys (Al Si12Cu1(Fe), Al Si5Mg, Al Si9Cu3Zn3Fe, Al Si10Mg(Fe), Al Si9Cu3(Fe)(Zn) and Al Si9) has been analyzed. In order to perform a more precise environmental impact calculation, Life Cycle Assessment (LCA) with ReCiPe Endpoint methodology has been used, with the EcoInvent v3 AlMg3 aluminum alloy dataset as a reference. This dataset has been updated with the material composition ranges of the mentioned alloys. The balanced, maximum and minimum environmental impact values have been obtained. In general, the overall impact of the studied aluminum alloys varies from 5.98 × 10−1 pts to 1.09 pts per kg, depending on the alloy composition. In the analysis of maximum and minimum environmental impact, the alloy that has the highest uncertainty is AlSi9Cu3(Fe)(Zn), with a range of ±9%. The elements that contribute the most to increase its impact are Copper and Tin. The environmental impact of a specific case, an LED luminaire housing made out of an Al Si12Cu1(Fe) cast alloy, has been studied, showing the importance of considering the composition. Significant differences with the standard datasets that are currently available in EcoInvent v3 have been found. PMID:28773536

Influence of Composition on the Environmental Impact of a Cast Aluminum Alloy.

PubMed

Gómez, Patricia; Elduque, Daniel; Sarasa, Judith; Pina, Carmelo; Javierre, Carlos

2016-05-25

The influence of alloy composition on the environmental impact of the production of six aluminum casting alloys (Al Si12Cu1(Fe), Al Si5Mg, Al Si9Cu3Zn3Fe, Al Si10Mg(Fe), Al Si9Cu3(Fe)(Zn) and Al Si9) has been analyzed. In order to perform a more precise environmental impact calculation, Life Cycle Assessment (LCA) with ReCiPe Endpoint methodology has been used, with the EcoInvent v3 AlMg3 aluminum alloy dataset as a reference. This dataset has been updated with the material composition ranges of the mentioned alloys. The balanced, maximum and minimum environmental impact values have been obtained. In general, the overall impact of the studied aluminum alloys varies from 5.98 × 10 -1 pts to 1.09 pts per kg, depending on the alloy composition. In the analysis of maximum and minimum environmental impact, the alloy that has the highest uncertainty is AlSi9Cu3(Fe)(Zn), with a range of ±9%. The elements that contribute the most to increase its impact are Copper and Tin. The environmental impact of a specific case, an LED luminaire housing made out of an Al Si12Cu1(Fe) cast alloy, has been studied, showing the importance of considering the composition. Significant differences with the standard datasets that are currently available in EcoInvent v3 have been found.

Introducing a 2-His-1-Glu Nonheme Iron Center into Myoglobin Confers Nitric Oxide Reductase Activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Y Lin; N Yeung; Y Gao

2011-12-31

A conserved 2-His-1-Glu metal center, as found in natural nonheme iron-containing enzymes, was engineered into sperm whale myoglobin by replacing Leu29 and Phe43 with Glu and His, respectively (swMb L29E, F43H, H64, called Fe{sub B}Mb(-His)). A high resolution (1.65 {angstrom}) crystal structure of Cu(II)-CN{sup -}-Fe{sub B}Mb(-His) was determined, demonstrating that the unique 2-His-1-Glu metal center was successfully created within swMb. The Fe{sub B}Mb(-His) can bind Cu, Fe, or Zn ions, with both Cu(I)-Fe{sub B}Mb(-His) and Fe(II)-Fe{sub B}Mb(-His) exhibiting nitric oxide reductase (NOR) activities. Cu dependent NOR activity was significantly higher than that of Fe in the same metal binding site.more » EPR studies showed that the reduction of NO to N{sub 2}O catalyzed by these two enzymes resulted in different intermediates; a five-coordinate heme-NO species was observed for Cu(I)-Fe{sub B}Mb(-His) due to the cleavage of the proximal heme Fe-His bond, while Fe(II)-Fe{sub B}Mb(-His) remained six-coordinate. Therefore, both the metal ligand, Glu29, and the metal itself, Cu or Fe, play crucial roles in NOR activity. This study presents a novel protein model of NOR and provides insights into a newly discovered member of the NOR family, gNOR.« less

On the nature of the Fe-bearing particles influencing hard anodizing behavior of AA 7075 extrusion products

NASA Astrophysics Data System (ADS)

Mukhopadhyay, A. K.

1998-03-01

The deleterious effects of Fe-bearing constituent particles on the fracture toughness of wrought A1 alloys have been known. Recent studies have shown that the presence of Fe-bearing, constituent particles is also determental to the nature and growth of the hard anodic oxide coating formed on such materials. The present study, using a combination of scanning electron microscopy (SEM), transmission electron microscopy (TEM), and electron probe microanalysis (EPMA), was made to examine the influence of the nature of the Fe-bearing particles on the hard anodizing behavior of AA 7075 extrusion products containing varying amounts of Si, Mn, and Fe impurities. It was found that, in the alloy containing 0.25 wt pct Si, 0.27 wt pct Mn, and 0.25 wt pct Fe, the Fe-bearing constituent particles are based on the Al12(FeMn)3Si phase (bcc with α=1.260 nm). These particles survive the hard anodizing treatment, add resistance to the electrical path, causing a rapid rise in the bath voltage with time, and cause a nonuniform growth of the anodic oxide film. In the materials containing 0.05 wt pct Si, 0.04 wt pct Mn, and 0.18 wt pct Fe, on the other hand, the formation of the Al12(FeMn)3Si-based phase is suppressed, and two different Fe-bearing phases, based on Al-Fe-Cu-Mn-based (simple cubic with a=1.265 nm) and Al7Cu2Fe, respectively form. Neither the Al-Fe-Cu-Mn-based phase nor the Al7Cu2Fe-based phase survive the hard anodizing treatment, and this results in a steady rise in the bath voltage with time and a relatively uniform growth of the anodic oxide film. Consideration of the size of the Fe-bearing, particles reveals that the smaller the particle, the more uniform the growth of the anodic oxide film.

Fabrication and Electromagnetic Properties of Conjugated NH2-CuPc@Fe3O4

NASA Astrophysics Data System (ADS)

Yan, Liang; Pu, Zejun; Xu, Mingzhen; Wei, Renbo; Liu, Xiaobo

2017-10-01

Conjugated amino-phthalocyanine copper containing carboxyl groups/magnetite (NH2-CuPc@Fe3O4) has been fabricated from FeCl3·6H2O and NH2-CuPc via a simple solvothermal method and its electromagnetic properties investigated. Scanning electron microscopy and transmission electron microscopy revealed that the NH2-CuPc@Fe3O4 was a waxberry-like nanomaterial with NH2-CuPc molecules effectively embedded in the interior of Fe3O4 particles in the form of beads. Introduction of NH2-CuPc effectively improved the complementarity between the dielectric and magnetic losses of the system, resulting in excellent electromagnetic performance. The minimum reflection loss of the as-prepared composite reached -33.4 dB at 7.0 GHz for coating layer thickness of 4.0 mm and bandwidth below -10.0 dB (90% absorption) of up to 3.8 GHz. These results indicate that introduction of NH2-CuPc results in a composite with potential for use as an electromagnetic microwave absorption material.

Humic substances and trace metals associated with Fe and Al oxides deposited in an acidic mountain stream

USGS Publications Warehouse

McKnight, Diane M.; Wershaw, R. L.; Bencala, K.E.; Zellweger, G.W.; Feder, G.L.

1992-01-01

Hydrous iron and aluminum oxides are deposited on the streambed in the confluence of the Snake River and Deer Creek, two streams in the Colorado Rocky Mountains. The Snake River is acidic and has high concentrations of dissolved Fe and Al. These metals precipitate at the confluence with the pristine, neutral pH, Deer Creek because of the greater pH (4.5-6.0) in the confluence. The composition of the deposited oxides changes consistently with distance downstream, with the most upstream oxide samples having the greatest Fe and organic carbon content. Fulvic acid accounts for most of the organic content of the oxides. Results indicate that streambed oxides in the confluence are not saturated with respect to their capacity to sorb dissolved humic substances from streamwater. The contents of several trace metals (Mn, Zn, Cu, Pb, Ni and Co) also decrease with distance downstream and are correlated with both the Fe and organic carbon contents. Strong metal-binding sites associated with the sorbed fulvic acid are more than sufficient to account for the trace metal content of the oxides. Complexation of trace metals by sorbed fulvic acid may explain the observed downstream decrease in trace metal content.

Redistribution of iron and titanium in subduction zones: insights from high-pressure serpentinites

NASA Astrophysics Data System (ADS)

Crossley, Rosalind; Evans, Katy; Reddy, Steven; Lester, Gregory

2017-04-01

The redox state, quantity and composition of subduction zone fluids influence the transport and precipitation of elements including those which are redox-sensitive, of economic importance such as Cu, Au and Ag, and those considered to be immobile, which include Fe3+. However, subduction zone fluids remain poorly understood. The redox state of Fe in high-pressure ultramafic rocks, which host a significant proportion of Fe3+, can be used to provide an insight into Fe cycling and constrain the composition of subduction zone fluids. In this work, a combination of the study of oxide and silicate mineral textures, interpretation of mineral parageneses, mineral composition data, and the whole rock geochemistry of high-pressure retrogressed ultramafic rocks from the Zermatt-Saas Zone constrains the distribution of iron and titanium, and oxidation state of iron, to provide constraints on fluids at depth in subduction zones. Oxide minerals host the bulk of the iron, particularly Fe3+. The increase in mode of magnetite during initial retrogression is most consistent with oxidation of existing iron within the samples during the infiltration of an oxidising fluid since it is difficult to reconcile addition of Fe3+ with the known limited solubility of this species. These fluids may be sourced from hybrid samples and/or serpentinites at greater depths. However, high Ti contents are not typical of serpentinites and additionally cannot be accounted for by simple mixing of a depleted mantle protolith with the nearby Allalin gabbro. Titanium-rich samples are suggested to result from fluid-facilitated hybridisation of gabbro and serpentinite protoliths prior to peak metamorphism, and provides the tantalising possibility that Ti, an element generally perceived as immobile, has been added to the rock during this process. If Ti addition has occurred, then the introduction of Fe3+, also generally considered to be immobile, cannot be disregarded. Aluminosilicate complexing could provide a transport vector for Ti where this mechanism of Ti transport is consistent with the Al-rich nature of the sample.

Colloidal metal oxide nanoparticle systems: the new promising way to prevent antibiotic resistance during treatment of local infectious processes

NASA Astrophysics Data System (ADS)

Karasenkov, Y.; Frolov, G.; Pogorelsky, I.; Latuta, N.; Gusev, A.; Kuznetsov, D.; Leont'ev, V.

2015-11-01

New bactericidal containing nanoparticles colloids for application in dentistry, maxillofacial surgery, urology, obstetrics, gynaecology, ENT, proctology have been developed. The various water colloidal nanodispersive systems of metals and oxides have been obtained by means of electric impulse - condensation (electroerosion) method. These systems are based pure elements and alloys of argentum (Ag), titanium dioxide (TiO2), iron oxide (Fe2O3), tantalum oxide (TaO), vanadium oxide (VO2), cobalt oxide (CoO), tantalum dioxide TaO2, zinc oxide (ZnO), copper oxide (CuO) and mixed suspensions of titanium, aluminium and molybdenum oxides. The research has been made on culture of dentobacterial plaque and mixed culture issued from gingival spaces. The composition of culture was identified with S.aureus, S.epidermidis and nonfermentable kinds of E.coli. The observation period lasted more than nineteen days. All solutions showed highly prolonged bactericidal activity in dilutions from the whole solution 1-20 mg/L. The bactericidal activity of powder specimen of silica containing Ag and Fe2O3 nanoparticles used as dental filling material and disintegrates of composite materials (produced by “StomaDent” CJSC) have been studied. Tested materials have long (up to 19 days and more) bactericidal activity.

Hydroxyl Radical Formation in Solutions of Fe(III) and Hydrogen Peroxide - Impact of Freezing and Thawing Process

NASA Astrophysics Data System (ADS)

Arakaki, T.; Kinjo, M.; Shiroma, K.; Shibata, M.; Miyake, T.; Hirakawa, T.; Sakugawa, H.

2003-12-01

Hydroxyl radical formation was studied by detecting concentration of formate in solutions of hydrated formaldehyde, HOOH, and Fe(III) or Cu(II). Oxidation of hydrated formaldehyde by OH radical is known to form formate. Formate formation increased by about 4 times when the solution underwent freezing and thawing. Although the reaction mechanisms are not clearly understood, we believe that the concentration effect of freezing enhanced the catalytic reactions between HOOH and Fe(III) or Cu(II) and the reduction of transition metals, i.e., Fe(III) to Fe(II) and Cu(II) to Cu(I). The concentration effect also enhanced reactions between Fe(II) and HOOH or Cu(I) and HOOH, which generated OH radical (freeze-Fenton reaction). Study of the effects of pH showed that formate formation was the highest at pH = 4.0, indicating that the speciation of Fe(III) affected the formation of formate. Concentration-dependent experiments demonstrated that Fe is probably the limiting agent under typical atmospheric conditions. Our results suggested that the freezing process could be an important source of hydroxyl radical in high cloud, winter fog, rime ice and freezing acidic rain, and more importantly, a potentially additional oxidation mechanism in the atmosphere.

Enhanced thermal stability of Cu alloy films by strong interaction between Ni and Zr (or Fe)

NASA Astrophysics Data System (ADS)

Zheng, Yuehong; Li, Xiaona; Cheng, Xiaotian; Li, Zhuming; Liu, Yubo; Dong, Chuang

2018-04-01

Low resistivity, phase stability and nonreactivity with surrounding dielectrics are the key to the application of Cu to ultra-large-scale integrated circuits. Here, a stable solid solution cluster model was introduced to design the composition of barrierless Cu-Ni-Zr (or Fe) seed layers. The third elements Fe and Zr were dissolved into Cu via a second element Ni, which is soluble in both Cu and Zr (or Fe). The films were prepared by magnetron sputtering on the single-crystal p-Si (1 0 0) wafers. Since the diffusion characteristics of the alloying elements are different, the effects of the strong interaction between Ni and Zr (or Fe) on the film’s stability and resistivity were studied. The results showed that a proper addition of Zr-Ni (Zr/Ni  ⩽  0.6/12) into Cu could form a large negative lattice distortion, which inhibits Cu-Si interdiffusion and enhances the stability of Cu film. When Fe-Ni was co-added into Cu, the lattice distortion of Cu reached a lower value, 0.0029 Å  ⩽  |Δa|  ⩽  0.0046 Å, and the films showed poor stability. Therefore, when the model is applied to the composition design of the films, the strong interaction between the elements and the addition ratio should be taken into consideration.

Structural, optical, dielectric and magnetic studies of gadolinium-added Mn-Cu nanoferrites

NASA Astrophysics Data System (ADS)

Kanna, R. Rajesh; Lenin, N.; Sakthipandi, K.; Kumar, A. Senthil

2018-05-01

Spinel ferrite with the general formula Mn1-xCuxFe1.85Gd0.15O4 (x = 0.2, 0.4, 0.6 and 0.8) was synthesized using the standard sonochemical method. The structure, optical, morphology, dielectric and magnetic properties of the prepared Mn1-xCuxFe1.85Gd0.15O4 nanoferrites were exhaustively investigated using various characterization techniques. The phase purity, secondary phase and crystallite parameters were studied from X-ray diffraction patterns. Fourier transform infrared spectra showed two absorption bands of transition metal oxides in the frequency range from 400 to 650 cm-1, which are related to asymmetric stretching modes of the spinel ferrites (AB2O4). Raman spectra have five active modes illustrating the vibration of O2- ions at both tetrahedral (A) site and octahedral (B) site ions. The wide and narrow scan spectrum from X-ray photoelectron spectroscopy results confirmed the presence of Mn, Cu, Gd, Fe, C and O elements in the composition. The oxidation state and core level of the photo electron peaks of Mn 2p, Cu 2p, Gd 3d, Fe 2p and O 1s were analyzed. The influence of the Cu2+ concentration in Mn1-xCuxFe1.85Gd0.15O4 on the morphology, varying from nanorods, nanoflakes to spherical, was explored on the basis of scanning electron microscopy images. Ultraviolet diffuse reflectance spectroscopy studies indicated that the optical bandgap (5.12-5.32 eV) of the nanoferrites showed an insulating behavior. The dielectric constant, loss tangent and complex dielectric constant values decreased with an increase in frequency with the addition of Gd3+ content. A vibrating sample magnetometer showed that the prepared nanoferrites had a soft ferromagnetic nature. The magnetic parameter changed markedly with an increase in the Cu content in Mn1-xCuxFe1.85Gd0.15O4 nanoferrites. The optical, dielectric and magnetic properties were considerably enhanced with the addition of Gd3+ ions in the spinel nanoferrites.

Fabrication of Cu-Ag core-shell bimetallic superfine powders by eco-friendly reagents and structures characterization

NASA Astrophysics Data System (ADS)

Zhao, Jun; Zhang, Dongming; Zhao, Jie

2011-09-01

Superfine bimetallic Cu-Ag core-shell powders were synthesized by reduction of copper sulfate pentahydrate and silver nitrate with eco-friendly ascorbic acid as a reducing agent and cyclodextrins as a protective agent in an aqueous system. The influence of Ag/Cu ratio on coatings was investigated. Ag was homogeneously distributed on the surface of Cu particles at a mole ratio of Ag/Cu=1. FE-SEM showed an uniformity of Ag coatings on Cu particles. Antioxidation of Cu particles was improved by increasing Ag/Cu ratio. TEM-EDX and UV-vis spectra also revealed that Cu cores were covered by Ag nanoshells on the whole. The surface composition analysis by XPS indicated that only small parts of Cu atoms in the surface were oxidized. It was noted that the hindrance of cyclodextrins chemisorbed on particles plays an important role in forming high quality and good dispersity Cu-Ag (Cu@Ag) core-shell powders.

Modeling Ductile-Phase Toughened Tungsten for Plasma-Facing Materials: Progress in Damage Finite Element Analysis of the Tungsten-Copper Bend Bar Tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nguyen, Ba Nghiep; Henager, Charles H.; Kurtz, Richard J.

The objective of this study is to investigate the deformation behavior of ductile phase toughened W-composites such as W-Cu and W-Ni-Fe by means of a multiscale finite element model that involves a microstructural dual-phase model where the constituent phases (i.e., W, Cu, Ni-Fe) are finely discretized and are described by a continuum damage model. Such a model is suitable for modeling deformation, cracking, and crack bridging for W-Cu, W-Ni-Fe, and other ductile phase toughened W-composites, or more generally, any multi-phase composite structure where two or more phases undergo cooperative deformation in a composite system. Our current work focuses on simulatingmore » the response and damage development of the W-Cu specimen subjected to three-point bending.« less

Pd-Catalyzed Aerobic Oxidative Biaryl Coupling: Non-Redox Cocatalysis by Cu(OTf)2 and Discovery of Fe(OTf)3 as a Highly Effective Cocatalyst.

PubMed

Wang, Dian; Stahl, Shannon S

2017-04-26

Copper salts find widespread use in Pd-catalyzed oxidation reactions, and they are typically used as oxidants or redox-active cocatalysts. Here, we probe the origin of a dramatic acceleration effect of Cu(OTf) 2 in the C-H/C-H aerobic oxidative coupling of o-xylene. NMR spectroscopic analysis of the Pd II catalyst in the presence of Cu(OTf) 2 , together with other experimental and DFT computational studies of the catalytic reaction, show that Cu(OTf) 2 activates the Pd II catalyst for C-H activation via a non-redox pathway and has negligible impact on catalyst reoxidation. These observations led to the testing of other metal triflate salts as cocatalysts, the results of which show that Fe(OTf) 3 is even more effective than Cu(OTf) 2 .

Co-precipitated and collocated carbides and Cu-rich precipitates in a Fe-Cu steel characterized by atom-probe tomography.

PubMed

Kolli, R Prakash; Seidman, David N

2014-12-01

The composition of co-precipitated and collocated NbC carbide precipitates, Fe3C iron carbide (cementite), and Cu-rich precipitates are studied experimentally by atom-probe tomography (APT). The Cu-rich precipitates located at a grain boundary (GB) are also studied. The APT results for the carbides are supplemented with computational thermodynamics predictions of composition at thermodynamic equilibrium. Two types of NbC carbide precipitates are distinguished based on their stoichiometric ratio and size. The Cu-rich precipitates at the periphery of the iron carbide and at the GB are larger than those distributed in the α-Fe (body-centered cubic) matrix, which is attributed to short-circuit diffusion of Cu along the GB. Manganese segregation is not observed at the heterophase interfaces of the Cu-rich precipitates that are located at the periphery of the iron carbide or at the GB, which is unlike those located at the edge of the NbC carbide precipitates or distributed in the α-Fe matrix. This suggests the presence of two populations of NiAl-type (B2 structure) phases at the heterophase interfaces in multicomponent Fe-Cu steels.

Coercivity Recovery Effect of Sm-Fe-Cu-Al Alloy on Sm2Fe17N3 Magnet

NASA Astrophysics Data System (ADS)

Otogawa, Kohei; Asahi, Toru; Jinno, Miho; Yamaguchi, Wataru; Takagi, Kenta; Kwon, Hansang

2018-03-01

The potential of a Sm-Fe-Cu-Al binder for improvement of the magnetic properties of Sm2Fe17N3 was examined. Transmission electron microscope (TEM) observation of a Sm-Fe-Cu-Al alloy-bonded Sm2Fe17N3 magnet which showed high coercivity revealed that the Sm-Fe-Cu-Al alloy had an effect of removing the surface oxide layer of the Sm2 Fe17N3 grains. However, the Sm-Fe-Cu-Al binder was contaminated by carbon and nitrogen, which originated from the organic solvent used as the milling medium during pulverization. To prevent carbon and nitrogen contamination, the Sm-Fe- Cu-Al alloy was added directly on the surface of the Sm2Fe17N3 grains by sputtering. Comparing the recovered coercivity per unit amount of the added binder the uncontaminated binder-coated sample had a higher coercivity recovery effect than the milled binder-added sample. These results suggested that sufficient addition of the contamination-free Sm-Fe-Cu-Al binder has the possibility to reduce the amount of binder necessary to produce a high coercive Sm2Fe17N3 magnet.

Sulfate radical degradation of acetaminophen by novel iron-copper bimetallic oxidation catalyzed by persulfate: Mechanism and degradation pathways

NASA Astrophysics Data System (ADS)

Zhang, Yuanchun; Zhang, Qian; Hong, Junming

2017-11-01

A novel iron coupled copper oxidate (Fe2O3@Cu2O) catalyst was synthesized to activate persulfate (PS) for acetaminophen (APAP) degradation. The catalysts were characterized via field-emission scanning electron microscopy and energy-dispersive X-ray spectrometry. The effects of the catalyst, PS concentration, catalyst dosage, initial pH, dissolved oxygen were analyzed for treatment optimization. Results indicated that Fe2O3@Cu2O achieved higher efficiency in APAP degradation than Fe2O3/PS and Cu2O/PS systems. The optimal removal efficiency of APAP (90%) was achieved within 40 min with 0.6 g/L PS and 0.3 g/L catalyst. To clarify the mechanism for APAP degradation, intermediates were analyzed with gas chromatography-mass spectrometry. Three possible degradation pathways were identified. During reaction, Cu(I) was found to react with Fe(III) to generate Fe(II), which is the most active phase for PS activation. Through the use of methanol and tert-butyl alcohol (TBA) as radical trappers, SO4rad - was identified as the main radical species that is generated during oxidation.

Nitrogen Oxide Atom-Transfer Redox Chemistry; Mechanism of NO(g) to Nitrite Conversion Utilizing µ-oxo Heme-FeIII−O−CuII(L) Constructs

PubMed Central

Hematian, Shabnam; Kenkel, Isabell; Shubina, Tatyana E.; Dürr, Maximilian; Liu, Jeffrey J.; Siegler, Maxime A.; Ivanovic-Burmazovic, Ivana; Karlin, Kenneth D.

2015-01-01

While nitric oxide (NO, nitrogen monoxide) is a critically important signaling agent, its cellular concentrations must be tightly controlled, generally through its oxidative conversion to nitrite (NO2−) where it is held in reserve to be reconverted as needed. In part, this reaction is mediated by the binuclear heme a3/CuB active site of cytochrome c oxidase. In this report, the oxidation of NO(g) to nitrite is shown to occur efficiently in new synthetic µ-oxo heme-FeIII−O−CuII(L) constructs (L being a tridentate or tetradentate pyridyl/alkylamino ligand), and spectroscopic and kinetic investigations provide detailed mechanistic insights. Two new X-ray structures of µ-oxo complexes have been determined and compared to literature analogs. All µ-oxo complexes react with 2 mol equiv NO(g) to give 1:1 mixtures of discrete [(L)CuII(NO2−)]+ plus ferrous heme-nitrosyl compounds; when the first NO(g) equiv reduces the heme center and itself is oxidized to nitrite, the second equiv of NO(g) traps the ferrous heme thus formed. For one µ-oxo heme-FeIII−O−CuII(L) compound, the reaction with NO(g) reveals an intermediate species (“intermediate”), formally a bis-NO adduct, [(NO)(porphyrinate)FeII-(NO2−)−CuII(L)]+ (λmax = 433 nm), confirmed by cryo-spray ionization mass spectrometry and EPR spectroscopy, along with the observation that cooling a 1:1 mixture of [(L)CuII(NO2−)]+ and heme-FeII(NO) to −125 °C leads to association and generation of the key 433 nm UV–vis feature. Kinetic-thermodynamic parameters obtained from low-temperature stopped-flow measurements are in excellent agreement with DFT calculations carried out which describe the sequential addition of NO(g) to the µ-oxo complex. PMID:25974136

Metal-Organic Coordination Polymer to Prepare Density Controllable and High Nitrogen-Doped Content Carbon/Graphene for High Performance Supercapacitors.

PubMed

Luo, Jinwei; Zhong, Wenbin; Zou, Yubo; Xiong, Changlun; Yang, Wantai

2017-01-11

Design and preparation of carbon-based electrode material with high nitrogen-doping ratio and appropriate density attract much interest for supercapacitors in practical application. Herein, three porous carbon/graphene (NCG Cu , NCG Fe , and NCG Zn ) with high doping ratio of nitrogen have been prepared via directly pyrolysis of graphene oxide (GO)/metal-organic coordination polymer (MOCP) composites, which were formed by reacting 4,4'-bipyridine (BPD) with CuCl 2 , FeCl 3 , and ZnCl 2 , respectively. As-prepared NCG Cu , NCG Fe and NCG Zn showed high nitrogen doping ratio of 10.68, 12.99, and 11.21 at. %; and high density of 1.52, 0.84, and 1.15 g cm -3 , respectively. When as-prepared samples were used as supercapacitor electrodes, NCG Cu , NCG Fe and NCG Zn exhibited high gravimetric specific capacitances of 369, 298.5, 309.5 F g -1 , corresponding to high volumetric specific capacitances of 560.9, 250.7, 355.9 F cm -3 at a current density of 0.5 A g -1 , as well as good cycling stability, nearly 100% of the capacitance retained after 1000 cycles even at a large current density of 10 A g -1 . It is expected that the provided novel strategy can be used to develop electrode materials in high performance energy conversion/storage devices.

Speciation and distribution of copper in a mining soil using multiple synchrotron-based bulk and microscopic techniques.

PubMed

Yang, Jianjun; Liu, Jin; Dynes, James J; Peak, Derek; Regier, Tom; Wang, Jian; Zhu, Shenhai; Shi, Jiyan; Tse, John S

2014-02-01

Molecular-level understanding of soil Cu speciation and distribution assists in management of Cu contamination in mining sites. In this study, one soil sample, collected from a mining site contaminated since 1950s, was characterized complementarily by multiple synchrotron-based bulk and spatially resolved techniques for the speciation and distribution of Cu as well as other related elements (Fe, Ca, Mn, K, Al, and Si). Bulk X-ray absorption near-edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) spectroscopy revealed that soil Cu was predominantly associated with Fe oxides instead of soil organic matter. This agreed with the closest association of Cu to Fe by microscopic X-ray fluorescence (U-XRF) and scanning transmission X-ray microscopy (STXM) nanoanalysis, along with the non-occurrence of photoreduction of soil Cu(II) by quick Cu L3,2-edge XANES spectroscopy (Q-XANES) which often occurs when Cu organic complexes are present. Furthermore, bulk-EXAFS and STXM-coupled Fe L3,2-edge nano-XANES analysis revealed soil Cu adsorbed primarily to Fe(III) oxides by inner-sphere complexation. Additionally, Cu K-edge μ-XANES, L3,2-edge bulk-XANES, and successive Q-XANES results identified the presence of Cu2S rather than radiation-damage artifacts dominant in certain microsites of the mining soil. This study demonstrates the great benefits in use of multiple combined synchrotron-based techniques for comprehensive understanding of Cu speciation in heterogeneous soil matrix, which facilitates our prediction of Cu reactivity and environmental fate in the mining site.

Brazing characteristics of a Zr-Ti-Cu-Fe eutectic alloy filler metal for Zircaloy-4

NASA Astrophysics Data System (ADS)

Lee, Jung G.; Lim, C. H.; Kim, K. H.; Park, S. S.; Lee, M. K.; Rhee, C. K.

2013-10-01

A Zr-Ti-Cu-Fe quaternary eutectic alloy was employed as a new Be-free brazing filler metal for Zircaloy-4 to supersede physically vapor-deposited Be coatings used conventionally with several disadvantages. The quaternary eutectic composition of Zr58Ti16Cu10Fe16 (at.%) showing a low melting temperature range from 832 °C to 853 °C was designed by a partial substitution of Zr with Ti based on a Zr-Cu-Fe ternary eutectic system. By applying an alloy ribbon with the determined composition, a highly reliable joint was obtained with a homogeneous formation of predominantly grown α-Zr phases owing to a complete isothermal solidification, exhibiting strength higher than that of Zircaloy-4. The homogenization of the joint was rate-controlled by the diffusion of the filler elements (Ti, Cu, and Fe) into the Zircaloy-4 base metal, and the detrimental segregation of the Zr2Fe phase in the central zone was completely eliminated by an isothermal holding at a brazing temperature of 920 °C for 10 min.

Spin-filter spin valves with nano-oxide layers for high density recording heads

NASA Astrophysics Data System (ADS)

Al-Jibouri, Abdul; Hoban, M.; Lu, Z.; Pan, G.

2002-05-01

A new spin-filter spin valve with nano-oxide specular layers with structure of Ta/NiFe/IrMn/CoFe/NOL1/CoFe/Cu/CoFetfl/CutCu/NOL2/Ta was deposited using a Nordiko 9606 physical vapor deposition system. The data clearly show that the magnetoresistive (MR) ratio has been significantly improved for spin valves with thinner free layers. The MR ratio remains larger than 12% even when the CoFe free layer is as thin as 1 nm. An optimized MR ratio of ˜15% was obtained when tfl was about 1.2 nm and tCu about 1.5 nm, and was a result of the balance between the increase in the electron mean free path difference and current shunting through the conducting layer. It is also found that the Cu enhancing layer can improve soft magnetic properties of the CoFe free layer due to the low atomic intermixing observed between Co and Cu. The CoFe free layer of 1-4 nm exhibited coercivity of ˜3 Oe after annealing in a static magnetic field. This kind of spin valve with a very thin soft CoFe free layer is particularly attractive for ultra high density read head applications.

Reduction of aqueous transition metal species on the surfaces of Fe(II)-containing oxides

USGS Publications Warehouse

White, A.F.; Peterson, M.L.

1996-01-01

Experimental studies demonstrate that structural Fe(II) in magnetite and ilmenite heterogeneously reduce aqueous ferric, cupric, vanadate, and chromate ions at the oxide surfaces over a pH range of 1-7 at 25??C. For an aqueous transition metal m, such reactions are 3[Fe2+Fe3+2]O4(magnetite) + 2/nmz ??? 4[Fe3+2]O3(maghemite) + Fe2+ + 2/nmz-n and 3[Fe2+Ti]O3(ilmenite) + 2/nmz ??? Fe3+2Ti3O9(pseudorutile) + Fe2+ + 2/nmz-n, where z is the valance state and n is the charge transfer number. The half cell potential range for solid state oxidation [Fe(II)] ??? [Fe(III)] is -0.34 to -0.65 V, making structural Fe(II) a stronger reducing agent than aqueous Fe2+ (-0.77 V). Reduction rates for aqueous metal species are linear with time (up to 36 h), decrease with pH, and have rate constants between 0.1 and 3.3 ?? 10-10 mol m-2 s-1. Iron is released to solution both from the above reactions and from dissolution of the oxide surface. In the presence of chromate, Fe2+ is oxidized homogeneously in solution to Fe3+. X-ray photoelectron spectroscopy (XPS) denotes a Fe(III) oxide surface containing reduced Cr(III) and V(IV) species. Magnetite and ilmenite electrode potentials are insensitive to increases in divalent transition metals including Zn(II), Co(II), Mn(II), and Ni(II) and reduced V(IV) and Cr(III) but exhibit a log-linear concentration-potential response to Fe(III) and Cu(II). Complex positive electrode responses occur with increasing Cr(VI) and V(V) concentrations. Potential dynamic scans indicate that the high oxidation potential of dichromate is capable of suppressing the cathodic reductive dissolution of magnetite. Oxide electrode potentials are determined by the Fe(II)/Fe(III) composition of the oxide surface and respond to aqueous ion potentials which accelerate this oxidation process. Natural magnetite sands weathered under anoxic conditions are electrochemically reactive as demonstrated by rapid chromate reduction and the release of aqueous Fe(III) to experimental solution. In contrast, magnetite weathered under oxidizing vadose conditions show minimum reactivity toward chromate ions. The ability of Fe(II) oxides to reduce transition metals in soils and groundwaters will be strongly dependent on the redox environment.

Reduction of aqueous transition metal species on the surfaces of Fe(II) -containing oxides

NASA Astrophysics Data System (ADS)

White, Art F.; Peterson, Maria L.

1996-10-01

Experimental studies demonstrate that structural Fe(II) in magnetite and ilmenite heterogeneously reduce aqueous ferric, cupric, vanadate, and chromate ions at the oxide surfaces over a pH range of 1-7 at 25°C. For an aqueous transition metal m, such reactions are 3[FeFe23+]O+2/nm→4[Fe23+]O+Fe+2/nm and 3[FeTi]O+→Fe23+TiO+Fe+2/nm, where z is the valance state and n is the charge transfer number. The half cell potential range for solid state oxidation [Fe(II)] → [Fe(III)] is -0.34 to -0.65 V, making structural Fe(II) a stronger reducing agent than aqueous Fe 2+ (-0.77 V). Reduction rates for aqueous metal species are linear with time (up to 36 h), decrease with pH, and have rate constants between 0.1 and 3.3 × 10 -10 mol m -2 s -1. Iron is released to solution both from the above reactions and from dissolution of the oxide surface. In the presence of chromate, Fe 2+ is oxidized homogeneously in solution to Fe 3+. X-ray photoelectron spectroscopy (XPS) denotes a Fe(III) oxide surface containing reduced Cr(III) and V(IV) species. Magnetite and ilmenite electrode potentials are insensitive to increases in divalent transition metals including Zn(II), Co(II), Mn(II), and Ni(II) and reduced V(IV) and Cr(III) but exhibit a log-linear concentration-potential response to Fe(III) and Cu(II). Complex positive electrode responses occur with increasing Cr(VI) and V(V) concentrations. Potential dynamic scans indicate that the high oxidation potential of dichromate is capable of suppressing the cathodic reductive dissolution of magnetite. Oxide electrode potentials are determined by the Fe(II)/Fe(III) composition of the oxide surface and respond to aqueous ion potentials which accelerate this oxidation process. Natural magnetite sands weathered under anoxic conditions are electrochemically reactive as demonstrated by rapid chromate reduction and the release of aqueous Fe(III) to experimental solution. In contrast, magnetite weathered under oxidizing vadose conditions show minimum reactivity toward chromate ions. The ability of Fe(II) oxides to reduce transition metals in soils and groundwaters will be strongly dependent on the redox environment.

Surface Oxidation of the High-Strength Steels Electrodeposited with Cu or Fe and the Resultant Defect Formation in Their Coating during the Following Galvanizing and Galvannealing Processes

NASA Astrophysics Data System (ADS)

Choi, Yun-Il; Beom, Won-Jin; Park, Chan-Jin; Paik, Doojin; Hong, Moon-Hi

2010-12-01

This study examined the surface oxidation of high-strength steels electrodeposited with Cu or Fe and the resultant defect formation in their coating during the following galvanizing and galvannealing processes. The high-strength steels were coated with an Cu or Fe layer by the electroplating method. Then, the coated steels were annealed in a reducing atmosphere, dipped in a molten zinc, and finally transformed into galvannealed steels through the galvannealing process. The formation of Si and Mn oxides on the surface of the high-strength steel was effectively suppressed, and the density of surface defects on the galvanized steel was significantly reduced by the pre-electrodeposition of Cu and Fe. This effect was more prominent for the steels electrodeposited at higher cathodic current densities. The finer electrodeposit layer formed at higher cathodic current density on the steels enabled the suppression of partial surface oxidation by Mn or Si and better wetting of Zn on the surface of the steels in the following galvanizing process. Furthermore, the pre-electrodeposited steels exhibited a smoother surface without surface cracks after the galvannealing process compared with the untreated steel. The diffusion of Fe and Zn in the Zn coating layer in the pre-electrodeposited steels appears to occur more uniformly during the galvannealing process due to the low density of surface defects induced by oxides.

Correlation between the oxide impedance and corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys

NASA Astrophysics Data System (ADS)

Park, Sang-Yoon; Lee, Myung-Ho; Jeong, Yong-Hwan; Jung, Youn-Ho

2004-12-01

The correlation between the oxide impedance and corrosion behavior of two series of Zr-Nb-Sn-Fe-Cu alloys was evaluated. Corrosion tests were performed in a 70 ppm LiOH aqueous solution at 360°C for 300 days. The results of the corrosion tests revealed that the corrosion behavior of the alloys depended on the Nb and Sn content. The impedance characteristics for the pre- and post-transition oxide layers formed on the surface of the alloys were investigated in sulfuric acid at room temperature. From the results, a pertinent equivalent circuit model was preferably established, explaining the properties of double oxide layers. The impedance of the oxide layers correlated with the corrosion behavior; better corrosion resistance always showed higher electric resistance for the inner layers. It is thus concluded that a pertinent equivalent circuit model would be useful for evaluating the long-term corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys.

Enhanced reactivity of microscale Fe/Cu bimetallic particles (mFe/Cu) with persulfate (PS) for p-nitrophenol (PNP) removal in aqueous solution.

PubMed

Ji, Qingqing; Li, Jun; Xiong, Zhaokun; Lai, Bo

2017-04-01

In this study, batch experiments were conducted to examine the enhanced reactivity of microscale Fe/Cu bimetallic particles (mFe/Cu) with persulfate (PS) for p-nitrophenol (PNP) removal in aqueous solution. The key operating parameters (i.e., theoretical Cu mass loadings (TML Cu ), mFe/Cu dosage, PS dose, initial pH and temperature) were optimized by the batch experiments, respectively. The experimental data were followed well the pseudo-first-order kinetic model. Result reveals that refractory PNP (500 mg L -1 ) was effectively degraded by mFe/Cu-PS system with removal of 98.4% and k obs of 1.91 min -1 after only 3 min treatment under the optimal operating conditions. Moreover, compared with control experiments (i.e., mFe/Cu, microscale Fe 0 with PS (mFe 0 -PS), and PS alone), mFe/Cu-PS system exerted better performance for PNP removal due to the strong synergistic effect between PS and mFe/Cu. According to the analysis results of degradation kinetics of PNP, COD (chemical oxygen demand) removal, UV-vis absorption spectra and the intermediates formed, the results reveal that the PNP removal by mFe/Cu-PS system was mainly attributed to reduction accompanied slight oxidation. And based on the analysis of surface characteristics of mFe/Cu particles, it is further demonstrated that PS could enhance the reactivity of mFe/Cu through rapid corrosion of iron surface and decrease of surface passivation of mFe/Cu surface when the low molar ratio of PS to mFe/Cu (i.e., 1:43) was used in this study. These results also illustrates mFe/Cu-PS can be as a high efficient pretreatment technology for the removal of toxic refractory PNP from wastewater. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effect of nano-oxide layers on giant magnetoresistance in pseudo-spin-valves using Co 2FeAl electrodes

NASA Astrophysics Data System (ADS)

Zhang, D. L.; Xu, X. G.; Wu, Y.; Miao, J.; Jiang, Y.

2011-03-01

We studied the pseudo-spin-valves (PSVs) with a structure of Ta/Co 2FeAl/NOL 1/Co 2FeAl/Cu/Co 2FeAl/NOL 2/Ta, where NOL represents the nano-oxide layer. Compared with the normal Co 2FeAl (CFA) PSV with a structure of Ta/Co 2FeAl/Cu/Co 2FeAl/Ta, which shows only a current-in-plane (CIP) giant magnetoresistance (GMR) of 0.03%, the CFA PSV with NOLs shows a large CIP-GMR of 5.84%. The enhanced GMR by the NOLs inserted in the CFA PSV is due to the large specular reflection caused by [(CoO)(Fe 2O 3)(Al 2O 3)] in NOL 1 and [(Fe 2O 3)(Al 2O 3)(Ta 2O 5)] in NOL 2. Another reason is that the roughness of the interface between Ta and CFA is improved by the oxidation procedure.

Influence of Oxygen Partial Pressure during Processing on the Thermoelectric Properties of Aerosol-Deposited CuFeO₂.

PubMed

Stöcker, Thomas; Exner, Jörg; Schubert, Michael; Streibl, Maximilian; Moos, Ralf

2016-03-24

In the field of thermoelectric energy conversion, oxide materials show promising potential due to their good stability in oxidizing environments. Hence, the influence of oxygen partial pressure during synthesis on the thermoelectric properties of Cu-Delafossites at high temperatures was investigated in this study. For these purposes, CuFeO₂ powders were synthetized using a conventional mixed-oxide technique. X-ray diffraction (XRD) studies were conducted to determine the crystal structures of the delafossites associated with the oxygen content during the synthesis. Out of these powders, films with a thickness of about 25 µm were prepared by the relatively new aerosol-deposition (AD) coating technique. It is based on a room temperature impact consolidation process (RTIC) to deposit dense solid films of ceramic materials on various substrates without using a high-temperature step during the coating process. On these dense CuFeO₂ films deposited on alumina substrates with electrode structures, the Seebeck coefficient and the electrical conductivity were measured as a function of temperature and oxygen partial pressure. We compared the thermoelectric properties of both standard processed and aerosol deposited CuFeO₂ up to 900 °C and investigated the influence of oxygen partial pressure on the electrical conductivity, on the Seebeck coefficient and on the high temperature stability of CuFeO₂. These studies may not only help to improve the thermoelectric material in the high-temperature case, but may also serve as an initial basis to establish a defect chemical model.

Variability of Fe isotope compositions of hydrothermal sulfides and oxidation products at mid-ocean ridges

NASA Astrophysics Data System (ADS)

Li, Xiaohu; Wang, Jianqiang; Chu, Fengyou; Wang, Hao; Li, Zhenggang; Yu, Xing; Bi, Dongwei; He, Yongsheng

2018-04-01

Significant Fe isotopic fractionation occurs during the precipitation and oxidative weathering of modern seafloor hydrothermal sulfides, which has an important impact on the cycling of Fe isotopes in the ocean. This study reports the Fe-isotope compositions of whole-rock sulfides and single-mineral pyrite collected from hydrothermal fields at the South Mid-Atlantic Ridge (SMAR) and the East Pacific Rise (EPR) and discusses the impacts of precipitation and late-stage oxidative weathering of sulfide minerals on Fe isotopic fractionation. The results show large variation in the Fe-isotope compositions of the sulfides from the different hydrothermal fields on the mid-oceanic ridges, indicating that relatively significant isotope fractionation occurs during the sulfide precipitation and oxidative weathering processes. The Fe-isotope compositions of the sulfides from the study area at the SMAR vary across a relatively small range, with an average value of 0.01‰. This Fe-isotope composition is similar to the Fe-isotope composition of mid-oceanic ridge basalt, which suggests that Fe was mainly leached from basalt. In contrast, the Fe-isotope composition of the sulfides from the study area at the EPR are significantly enriched in light Fe isotopes (average value - 1.63‰), mainly due to the kinetic fractionation during the rapid precipitation process of hydrothermal sulfide. In addition, the pyrite from different hydrothermal fields is enriched in light Fe isotopes, which is consistent with the phenomenon in which light Fe isotopes are preferentially enriched during the precipitation of pyrite. The red oxides have the heaviest Fe-isotope compositions (up to 0.80‰), indicating that heavy Fe isotopes are preferentially enriched in the oxidation product during the late-stage oxidation process. The data obtained from this study and previous studies show a significant difference between the Fe-isotope compositions of the sulfides from the SMAR and EPR. The relatively heavy Fe isotopes compositions of the sulfides from the SMAR may suggest the equilibrium fractionation process under high temperature conditions. The red Fe oxides are enriched in heavy Fe isotopes, indicating that the oxidative weathering processes result in the occurrence of significant Fe-isotope fractionation and the preferential enrichment of heavy Fe isotopes in the oxidation product.

Diffuse-flow hydrothermal field in an oceanic fracture zone setting, Northeast Pacific: Deposit composition

USGS Publications Warehouse

Hein, J.R.; Koski, R.A.; Embley, R.W.; Reid, J.; Chang, S.-W.

1999-01-01

This is the first reported occurrence of an active hydrothermal field in an oceanic fracture zone setting. The hydrothermal field occurs in a pull-apart basin within the Blanco Fracture Zone (BFZ), which has four distinct mineral deposit types: (1) barite mounds and chimneys, (2) barite stockwork breccia, (3) silica-barite beds, and (4) silica, barite, and Fe-Mn oxyhydroxide in sediments. All deposit types contain minor amounts of sulfides. In barite stockwork, silica-barite beds, and mineralized sediment, Ba, Ph, Ag, S, Au, Zn, Cu, Hg, TI, As, Mo, Sb, U, Cd, and Cu are enriched relative to unmineralized rocks and sediments of the BFZ. Fe and Mn are not enriched in the barite stockwork or silica-barite beds, but along with P, Co, and Mg are enriched in the mineralized sediments. Silver contents in deposits of the hydrothermal field range up to 86 ppm, gold to 0.7 ppm, zinc to 3.2%, copper to 0.8%, and barium to 22%. Mineralization occurred by diffuse, low to intermediate temperature (mostly <250??C) discharge of hydrothermal fluids through pillow lavas and ponds of mixed volcaniclastic and biosiliceous sediments. Bacterial mats were mineralized by silica, barite, and minor Fe hydroxides, or less commonly, by Mn oxyhydroxides. Pervasive mineralization of bacterial mats resulted in formation of silica-barite beds. Silica precipitated from hydrothermal fluids by conductive cooling and mixing with seawater. Sulfate, U, and rare earth elements (REEs) in barite were derived from seawater, whereas the REE content of hydrothermal silica deposits and mineralized sediments is associated with the aluminosilicate detrital fraction. Fe-, Zn-, Cu-, Pb-, and Hg-sulfide minerals, Ba in barite, and Eu in all mineralized deposits were derived from hydrothermal fluids. Manganese oxides and associated elements (Co, Sb, Mo, W, Cl, and Cu) and Fe oxides and associated elements (Be, B, P, and Mo) precipitated as the result of mixing of hydrothermal fluids with seawater. ?? 2001 Canadian Institute of Mining, Metallurgy and Petroleum. All rights reserved.

Rapid Assessment of the Ce-Co-Fe-Cu System for Permanent Magnetic Applications

NASA Astrophysics Data System (ADS)

Meng, F.; Chaudhary, R. P.; Gandha, K.; Nlebedim, I. C.; Palasyuk, A.; Simsek, E.; Kramer, M. J.; Ott, R. T.

2018-06-01

This work focuses on the rapid synthesis and characterization of quaternary Ce(CoFeCu)5 alloy libraries to assess their potential viability as permanent magnets. Arrays of bulk specimens with controlled compositions were synthesized via laser engineered net shaping (LENS) by feeding different ratios of alloy powders into a melt pool created by a laser. Based on the assessment of the magnetic properties of the LENS printed samples, arc-melted and cast ingots were prepared with varying Fe (5-20 at.%) and Co (60-45 at.%) compositions while maintaining constant Ce (16 at.%) and Cu (19 at.%) content. The evolution of the microstructure and phases with varying chemical compositions and their dependence on magnetic properties are analyzed in as-cast and heat-treated samples. In both the LENS printed and cast samples, we find the best magnetic properties correspond to a predominantly single-phase Ce(CoFeCu)5 microstructure in which high coercivity ( H c > 10 kOe) can be achieved without any microstructural refinement.

Rapid Assessment of the Ce-Co-Fe-Cu System for Permanent Magnetic Applications

NASA Astrophysics Data System (ADS)

Meng, F.; Chaudhary, R. P.; Gandha, K.; Nlebedim, I. C.; Palasyuk, A.; Simsek, E.; Kramer, M. J.; Ott, R. T.

2018-04-01

This work focuses on the rapid synthesis and characterization of quaternary Ce(CoFeCu)5 alloy libraries to assess their potential viability as permanent magnets. Arrays of bulk specimens with controlled compositions were synthesized via laser engineered net shaping (LENS) by feeding different ratios of alloy powders into a melt pool created by a laser. Based on the assessment of the magnetic properties of the LENS printed samples, arc-melted and cast ingots were prepared with varying Fe (5-20 at.%) and Co (60-45 at.%) compositions while maintaining constant Ce (16 at.%) and Cu (19 at.%) content. The evolution of the microstructure and phases with varying chemical compositions and their dependence on magnetic properties are analyzed in as-cast and heat-treated samples. In both the LENS printed and cast samples, we find the best magnetic properties correspond to a predominantly single-phase Ce(CoFeCu)5 microstructure in which high coercivity (H c > 10 kOe) can be achieved without any microstructural refinement.

Different recycle behavior of Cu2+ and Fe3+ ions for phenol photodegradation over TiO2 and WO3.

PubMed

Wan, Lianghui; Sheng, Jiayi; Chen, Haihang; Xu, Yiming

2013-11-15

Photocatalytic degradation of organic pollutants on TiO2 and WO3 have been widely studied, but the effects of Cu(2+) and Fe(3+) ions still remain unclear. In this work, we have found that the recycle behavior of Cu(2+) and Fe(3+) are greatly dependent on the photocatalytic activity of metal oxide used. With TiO2 (P25, anatase, and rutile), all the time profiles of phenol degradation in water under UV light well fitted to the apparent first-order rate equation. On the addition of Cu(2+), phenol degradation on anatase, rutile and WO3 also followed the first-order kinetics. On the addition of Fe(3+), the initial rate of phenol degradation on each oxide was increased, but only the reactions on three TiO2 became to follow the first order kinetics after half an hour. The relevant rate constants for phenol degradation in the presence of Cu(2+) or Fe(3+) were larger than those in the absence of metal ions. Under visible light, phenol degradation on WO3 was also accelerated on the addition of Fe(3+) or Cu(2+). Moreover, several influencing factors were examined, including the metal ion photolysis in solution. It becomes clear that as electron scavengers of TiO2 and WO3, Fe(3+) is better than Cu(2+), while they are better than O2. We propose that Fe(3+) recycle occurs through H2O2, photogenerated from TiO2, not from WO3, while Cu(2+) regeneration on a moderate photocatalyst is through the dissolved O2 in water. Copyright © 2013. Published by Elsevier B.V.

Synthesis, spectroscopy, and binding constants of ketocatechol-containing iminodiacetic acid and its Fe(III), Cu(II), and Zn(II) complexes and reaction of Cu(II) complex with H₂O₂ in aqueous solution.

PubMed

Gao, Jiaojiao; Xing, Feifei; Bai, Yueling; Zhu, Shourong

2014-06-07

A new neuromelanin-like ketocatechol-containing iminodiacetic acid ligand, (N-(3,4-dihydroxyl)phenacylimino)diacetic acid (H4L), which is also quite similar to compounds found in insect cuticle, has been synthesized and characterized. The X-ray crystal structure of H4L has been successfully determined. Proton binding and coordination with Fe(III), Cu(II), and Zn(II) have been studied by potentiometric titrations and UV-vis spectrophotometry in aqueous solution. UV spectra of H4L in the absence and presence of different metal ions indicate complexes formed with the catechol moiety of H4L in aqueous solution. Visible spectra and NMR reveal that H4L with Fe(III), Cu(II), and Zn(II) can all give stable mono-(ML) and dinuclear complexes [M(ML)]. Fe(III) can also form {Fe(FeL)2} and {Fe(FeL)3} species with sufficient base. The process is accompanied by a drastic color change from light blue to deep-blue to wine-red. The Fe(III)-Cu(II) heteronuclear complex also exists in aqueous solution whose spectra are similar to the homonuclear Fe(III) complex. However, the spectra of {Fe(CuL)} shifted to a longer wavelength and {Fe(CuL)2} and {Fe(CuL)3} shifted to a shorter wavelength. Keto-enol tautomerism was observed in weak basic aqueous solution as indicated by (1)H NMR spectra. The reaction products of Cu(II) complex with H2O2 depend on the H2O2 concentration and pH value. Low concentrations of H2O2 oxidize H4L to a series of semiquinone and quinone compounds with absorption maxima at 314-400 nm, while a high concentration of H2O2 oxidizes H4L to colorless muconic acid derivatives. NaIO4 gives different oxidase products, but no 2,4,5-trihydroxyphenylalanine quinone (TPQ)-like hydroxyquinone can be found.

Determination of band gap in epitaxial delafossite Cu oxide using optical techniques

NASA Astrophysics Data System (ADS)

Cabrera, Alejandro; Wheatley, R.; Seifert, B.; Wallentowitz, S.; Joshi, T.; Lederman, D.

Highly epitaxial delafossite CuFeO2 and CuFe1-xGaxO2 films were grown using Pulsed Laser Deposition techniques. The sample thicknesses were estimated to be 21 nm, 75 nm.The estimated gallium fraction of substituted ferric atoms was x =0.25 for the composite sample. We present the study of the fundamental band gap(s) for each sample via observation of their respective optical absorption properties in the NIR-VIS region using transmittance and diffuse reflection spectroscopy. Predominant absorption edges measured were between 1.1eV and 3.1eV from transmittance spectra. The sample of CuFe1-xGaxO2 showed measurable absorption features located at 2.4eV and 2.8eV. This study also found evidence of changes between apparent absorption edges between transmittance and diffuse reflectance spectroscopies of each sample and it may be resultant from absorption channels via surface states. Future photoluminescence experiments are planned to determine the photo-induced semiconductor behavior of these materials. ACNOWLEDGEMENTS: This work was supported by FONDECyT 1130372 and Proyecto Anillo ACT1409 at PUC and supported in part by the WV Higher Education Policy Commission (Grant HEPC.dsr.12.29) and by FAME sponsored by MARCO and DARPA (contract # 2013-MA-2382).

Metal-organic framework derived hollow polyhedron metal oxide posited graphene oxide for energy storage applications.

PubMed

Ramaraju, Bendi; Li, Cheng-Hung; Prakash, Sengodu; Chen, Chia-Chun

2016-01-18

A composite made from hollow polyhedron copper oxide and graphene oxide was synthesized by sintering a Cu-based metal-organic framework (Cu-MOF) embedded with exfoliated graphene oxide. As a proof-of-concept application, the obtained Cu(ox)-rGO materials were used in a lithium-ion battery and a sodium-ion battery as anode materials. Overall, the Cu(ox)-rGO composite delivers excellent electrochemical properties with stable cycling when compared to pure CuO-rGO and Cu-MOF.

Functionalized graphene oxide quantum dot-PVA hydrogel: a colorimetric sensor for Fe2+, Co2+ and Cu2+ ions

NASA Astrophysics Data System (ADS)

Baruah, Upama; Chowdhury, Devasish

2016-04-01

Functionalized graphene oxide quantum dots (GOQDs)-poly(vinyl alcohol) (PVA) hybrid hydrogels were prepared using a simple, facile and cost-effective strategy. GOQDs bearing different surface functional groups were introduced as the cross-linking agent into the PVA matrix thereby resulting in gelation. The four different types of hybrid hydrogels were prepared using graphene oxide, reduced graphene oxide, ester functionalized graphene oxide and amine functionalized GOQDs as cross-linking agents. It was observed that the hybrid hydrogel prepared with amine functionalized GOQDs was the most stable. The potential applicability of using this solid sensing platform has been subsequently explored in an easy, simple, effective and sensitive method for optical detection of M2+ (Fe2+, Co2+ and Cu2+) in aqueous media involving colorimetric detection. Amine functionalized GOQDs-PVA hybrid hydrogel when put into the corresponding solution of Fe2+, Co2+ and Cu2+ renders brown, orange and blue coloration respectively of the solution detecting the presence of Fe2+, Co2+ and Cu2+ ions in the solution. The minimum detection limit observed was 1 × 10-7 M using UV-visible spectroscopy. Further, the applicability of the sensing material was also tested for a mixture of co-existing ions in solution to demonstrate the practical applicability of the system. Insight into the probable mechanistic pathway involved in the detection process is also being discussed.

Mechanisms controlling Cu, Fe, Mn, and Co profiles in peat of the Filson Creek Fen, northeastern Minnesota

USGS Publications Warehouse

Walton-Day, K.; Filipek, L.H.; Papp, C.S.E.

1990-01-01

Filson Creek Fen, located in northeastern Minnesota, overlies a Cu-Ni sulfide deposit. A site in the fen was studied to evaluate the hydrogeochemical mechanisms governing the development of Fe, Mn, Co, and Cu profiles in the peat. At the study site, surface peat approximately 1 m thick is separated from the underlying mineralized bedrock by a 6-12 m thickness of lake and glaciofluvial sediments and till. Concentrations of Fe, Mn, Co, and Cu in peat and major elements in pore water delineate a shallow, relatively oxidized, Cu-rich zone overlying a deeper, reduced, Fe-, Mn-, and Co-rich zone within the peat. Sequential metal extractions from peat samples reveal that 40-55% of the Cu in the shallow zone is associated with organic material, whereas the remaining Cu is distributed between iron-oxide, sulfide, and residual fractions. Sixty to seventy percent of the Fe, Mn, and Co concentrated in the deeper zone occur in the residual phase. The metal profiles and associations probably result from non-steady-state input of metals and detritus into the fen during formation of the peat column. The enrichment of organic-associated Cu in the upper, oxidized zone represents a combination of Cu transported into the fen with detrital plant fragments and soluble Cu, derived from weathering of outcrop and subcrop of the mineral deposit, transported into the fen, and fixed onto organic matter in the peat. The variable stratigraphy of the peat indicates that weathering processes and surface vegetation have changed through time in the fen. The Fe, Mn, and Co maxima at the base of the peat are associated with a maximum in detrital matter content of the peat resulting from a transition between the underlying inorganic sedimentary environment to an organic sedimentary environment. The chemistry of sediments and ground water collected beneath the peat indicate that mobilization of metals from sulfide minerals in the buried mineral deposit or glacial deposits is minimal. Therefore, the primary source of Cu to the peat at the study site is outcrops and shallow subcrops of the mineral deposit adjacent to the fen. ?? 1990.

Oxidative degradation of the antibiotic oxytetracycline by Cu@Fe3O4 core-shell nanoparticles.

PubMed

Pham, Van Luan; Kim, Do-Gun; Ko, Seok-Oh

2018-08-01

A core-shell nanostructure composed of zero-valent Cu (core) and Fe 3 O 4 (shell) (Cu@Fe 3 O 4 ) was prepared by a simple reduction method and was evaluated for the degradation of oxytetracycline (OTC), an antibiotic. The Cu core and the Fe 3 O 4 shell were verified by X-ray diffractometry (XRD) and transmission electron microscopy. The optimal molar ratio of [Cu]/[Fe] (1/1) in Cu@Fe 3 O 4 created an outstanding synergic effect, leading to >99% OTC degradation as well as H 2 O 2 decomposition within 10min at the reaction conditions of 1g/L Cu@Fe 3 O 4 , 20mg/L OTC, 20mM H 2 O 2 , and pH3.0 (and even at pH9.0). The OTC degradation rate by Cu@Fe 3 O 4 was higher than obtained using single nanoparticle of Cu or Fe 3 O 4 . The results of the study using radical scavengers showed that OH is the major reactive oxygen species contributing to the OTC degradation. Finally, good stability, reusability, and magnetic separation were obtained with approximately 97% OTC degradation and no notable change in XRD patterns after the Cu@Fe 3 O 4 catalyst was reused five times. These results demonstrate that Cu@Fe 3 O 4 is a novel prospective candidate for the pharmaceutical and personal care products degradation in the aqueous phase. Copyright © 2018 Elsevier B.V. All rights reserved.

Skeletal Ru/Cu catalysts prepared from crystalline and quasicrystalline ternary alloy precursors: characterization by X-ray absorption spectroscopy and CO oxidation.

PubMed

Highfield, James; Liu, Tao; Loo, Yook Si; Grushko, Benjamin; Borgna, Armando

2009-02-28

The Ru/Cu system is of historical significance in catalysis. The early development and application of X-ray absorption spectroscopy (XAS) led to the original 'bimetallic cluster" concept for highly-immiscible systems. This work explores alkali leaching of Al-based ternary crystalline and quasicrystalline precursors as a potential route to bulk Ru/Cu alloys. Single-phase ternary alloys at 3 trial compositions; Al(71)Ru(22)Cu(7), Al(70.5)Ru(17)Cu(12.5), and Al(70)Ru(10)Cu(20), were prepared by arc melting of the pure metal components. After leaching, the bimetallic residues were characterized principally by transmission XAS, "as-leached" and after annealing in H(2) (and passivation) in a thermobalance. XRD and BET revealed a nanocrystalline product with a native structure of hexagonal Ru. XPS surface analysis of Ru(22)Cu(7) and Ru(17)Cu(12.5) found only slight enrichment by Cu in the as-leached forms, with little change upon annealing. Ru(10)Cu(20) was highly segregated as-leached. XANES data showed preferential oxidation of Cu in Ru(22)Cu(7), implying that it exists as an encapsulating layer. TG data supports this view since it does not show the distinct two-stage O(2) uptake characteristic of skeletal Ru. Cu K-edge EXAFS data for Ru(22)Cu(7) were unique in showing a high proportion of Ru neighbours. The spacing, d(CuRu) = 2.65 A, was that expected from a hypothetical (ideal) solid solution at this composition, but this is unlikely in such a bulk-immiscible system and Ru K-edge EXAFS failed to confirm bulk alloying. Furthermore its invariance under annealing was more indicative of an interfacial bond between bulk components, although partial alloying with retention of local order cannot entirely be ruled out. The XAS and XPS data were reconciled in a model involving surface and bulk segregation, Cu being present at both the grain exterior and in ultra-fine internal pores. This structure can be considered as the 3-dimensional analogue of the classical type. Preliminary studies in CO and H(2) oxidation were made in a DRIFTS flow reactor with on-line MS, and their activities and selectivities were compared against skeletal Ru and Cu controls, Ru/Al(2)O(3), and Au/Fe(2)O(3). All samples were active in CO oxidation above approximately 50 degrees C, showing light-off temperatures in the range 60-70 degrees C. Ru(22)Cu(7) and Ru(17)Cu(12.5) also showed good selectivities (vs. H(2) oxidation), attributed tentatively to Ru-modified Cu surfaces of varying thickness. These compositions are promising candidates to test in a (PROX) fuel processor to supply purified (CO-free) H(2) to a PEM fuel cell.

Metal dynamics in Lake Vanda (Wright Valley, Antarctica)

NASA Technical Reports Server (NTRS)

Green, W. J.; Ferdelman, T. G.; Canfield, D. E.; DeVincenzi, D. L. (Principal Investigator)

1989-01-01

Data are reported for Mn, Fe, Co, Ni, Cu and Cd in the Onyx River, and for Mn, Co, Ni, Cu and Cd in Lake Vanda, a closed-basin Antarctic lake. Oxic water concentrations for Co, Ni, Cu and Cd were quite low and approximate pelagic ocean values. Scavenging of these metals by sinking particles is strongly indicated. Deep-lake profiles reveal a sharp peak in the concentrations of Mn, Fe and Co at the oxic-anoxic boundary at 60 m. Maxima for Ni, Cu and Cd occur higher in the water column, in the vicinity of a Mn submaximum, suggesting early release of these metals from sinking manganese oxide-coated particles. A rough steady-state model leads to the conclusion that there is a large downward flux of Mn into the deep lake and that this flux is sufficient to explain the annual loss of Co, Ni, Cu and Cd. A pronounced geochemical separation between Fe and Mn apparently occurs in this system--Fe being best lost in near-shore environments and Mn being lost in deeper waters. Comparison of metal residence times in Lake Vanda with those in the oceans shows that in both systems Mn, Fe and Co are much more reactive than Ni, Cu and Cd. Energetically favorable inclusion of the more highly charged metals, Mn(IV), Fe(III) and Co(III), into oxide-based lattices is a plausible explanation.

Note: Resonance magnetoelectric interactions in laminate of FeCuNbSiB and multilayer piezoelectric stack for magnetic sensor

NASA Astrophysics Data System (ADS)

Li, Jianqiang; Lu, Caijiang; Xu, Changbao; Zhong, Ming

2015-09-01

This paper develops a simple miniature magnetoelectric (ME) laminate FeCuNbSiB/PZT-stack made up of magnetostrictive Fe73.5Cu1Nb3Si13.5B9 (FeCuNbSiB) foils and piezoelectric Pb(Zr, Ti)O3 (PZT) multilayer stack vibrator. Resonant ME interactions of FeCuNbSiB/PZT-stack with different layers of FeCuNbSiB foil (L) are investigated in detail. The experimental results show that the ME voltage coefficient reaches maximum value of 141.5 (V/cm Oe) for FeCuNbSiB/PZT-stack with L = 6. The AC-magnetic sensitivities can reach 524.29 mV/Oe and 1.8 mV/Oe under resonance 91.6 kHz and off-resonance 1 kHz, respectively. The FeCuNbSiB/PZT-stack can distinguish small dc-magnetic field of ˜9 nT. The results indicate that the proposed ME composites are very promising for the cheap room-temperature magnetic field sensing technology.

A simple route to improve rate performance of LiFePO4/reduced graphene oxide composite cathode by adding Mg2+ via mechanical mixing

NASA Astrophysics Data System (ADS)

Huang, Yuan; Liu, Hao; Gong, Li; Hou, Yanglong; Li, Quan

2017-04-01

Introducing Mg2+ to LiFePO4 and reduced graphene oxide composite via mechanical mixing and annealing leads to largely improved rate performance of the cathode (e.g. ∼78 mA h g-1 at 20 C for LiFePO4 and reduced graphene oxide composite with Mg2+ introduction vs. ∼37 mA h g-1 at 20 C for LiFePO4 and reduced graphene oxide composite). X-ray photoelectron spectroscopy unravels that the enhanced reduction of Fe2+ to Fe0 occurs in the simultaneous presence of Mg2+ and reduced graphene oxide, which is beneficial for the rate capability of cathode. The simple fabrication process provides a simple and effective means to improve the rate performance of the LiFePO4 and reduced graphene oxide composite cathode.

Plankton copper requirements and uptake in the subarctic Northeast Pacific Ocean

NASA Astrophysics Data System (ADS)

Semeniuk, David M.; Cullen, Jay T.; Johnson, W. Keith; Gagnon, Katie; Ruth, Thomas J.; Maldonado, Maria T.

2009-07-01

We undertook the first measurements of metabolic Cu requirements (net Cu:C assimilation ratios) and steady-state Cu uptake rates (ρCu ss) of natural plankton assemblages in the northeast subarctic Pacific using the short-lived radioisotope 67Cu. Size-fractionated net Cu:C assimilation ratios varied ˜3 fold (1.35-4.21 μmol Cu mol C -1) among the stations along Line P, from high Fe coastal waters to the Fe-limited open ocean. The variability in Cu:C was comparable to biogenic Fe:C ratios in this region. As previously observed for Fe uptake, the bacterial size class accounted for half of the total particulate ρCu ss. Interestingly, carbon biomass-normalized rates of Fe uptake from the siderophore desferrioxamine B (DFB) (ρFe DFB; a physiological proxy for Fe-limitation) by the >20 μm size class were positively correlated with the intracellular net Cu:C assimilation ratios in this size class, suggesting that intracellular Cu requirements for large phytoplankton respond to increased Fe-limitation. At Fe-limited Ocean Station Papa (OSP), we performed short-term Cu uptake (ρCu L) assays to determine the relative bioavailability of Cu bound to natural and synthetic ligands. Like the volumetric ρCu ss measured along Line P, the bacterial size class was responsible for at least 50% of the total ρCu L. Uptake rates of Cu from the various organic complexes suggest that Cu uptake was controlled by the oxidation state of the metal and by the metal:ligand concentration ratio, rather than the concentration of inorganic species of Cu in solution. Collectively, these data suggest that Cu likely plays an important role in the physiology of natural plankton communities beyond the toxicological effects studied previously.

Copper(II) cyanido-bridged bimetallic nitroprusside-based complexes: Syntheses, X-ray structures, magnetic properties, {sup 57}Fe Moessbauer spectroscopy and thermal studies

DOE Office of Scientific and Technical Information (OSTI.GOV)

Travnicek, Zdenek, E-mail: zdenek.travnicek@upol.c; Herchel, Radovan; Mikulik, Jiri

2010-05-15

Three heterobimetallic cyanido-bridged copper(II) nitroprusside-based complexes of the compositions [Cu(tet)Fe(CN){sub 5}NO].H{sub 2}O (1), where tet=N,N'-bis(3-aminopropyl)ethylenediamine, [Cu(hto)Fe(CN){sub 5}NO].2H{sub 2}O (2), where hto=1,3,6,9,11,14-hexaazatricyclo[12.2.1.1{sup 6,9}]octadecane and [Cu(nme){sub 2}Fe(CN){sub 5}NO].H{sub 2}O (3), where nme=N-methylethylenediamine, were synthesized and characterized by elemental analyses, {sup 57}Fe Moessbauer and FTIR spectroscopies, thermal analysis, magnetic measurements and single-crystal X-ray analysis. The products of thermal degradation processes of 2 and 3 were studied by XRD, {sup 57}Fe Moessbauer spectroscopy, SEM and EDS, and they were identified as mixtures of CuFe{sub 2}O{sub 4} and CuO. - Three heterobimetallic cyano-bridged copper(II) nitroprusside-based complexes of the general compositions of [Cu(L)Fe(CN){sub 5}NO].xH{sub 2}O, wheremore » L=N,N'-bis(3-aminopropyl)ethylenediamine (complex 1), 1,3,6,9,11,14-hexaazatricyclo[12.2.1.1{sup 6,9}]-octadecane (complex 2) and N-methylethylenediamine (complex 3), were synthesized, and fully structurally and magnetically characterized. SEM, EDS, XRD and {sup 57}Fe Moessbauer experiments were used for characterization of thermal decomposition products of complexes 2 and 3.« less

The Role of Metal Oxides in Nanothermite Reactions: Evidence of Condensed Phase Initiation

DTIC Science & Technology

2010-01-01

ignition on the gaseous oxidizer release from the metal oxides CuO, Fe2O3, and ZnO .[14] However, there is uncertainty as to whether oxidizer release to the...and how it differs from some other systems. In our previous work, we studied the nanothermite reaction of Al/CuO, Al/Fe2O3, and Al/ ZnO .[9] For...Jomard, Oxygen Diffusion in Bi2O3-doped ZnO , Materials Research-Ibero-American Journal of Materials, 11 (2008) 221-225. [20] T. Ivetic, M.V. Nikolic

Spin dynamics near a putative antiferromagnetic quantum critical point in Cu-substituted BaFe 2 As 2 and its relation to high-temperature superconductivity

DOE PAGES

Kim, M. G.; Wang, M.; Tucker, G. S.; ...

2015-12-02

We present the results of elastic and inelastic neutron scattering measurements on nonsuperconducting Ba(Fe 0.957Cu 0.043) 2As 2, a composition close to a quantum critical point between antiferromagnetic (AFM) ordered and paramagnetic phases. By comparing these results with the spin fluctuations in the low-Cu composition as well as the parent compound BaFe 2As 2 and superconducting Ba(Fe 1–xNi x) 2As 2 compounds, we demonstrate that paramagnon-like spin fluctuations are evident in the antiferromagnetically ordered state of Ba(Fe 0.957Cu 0.043) 2As 2, which is distinct from the AFM-like spin fluctuations in the superconducting compounds. Our observations suggest that Cu substitution decouplesmore » the interaction between quasiparticles and the spin fluctuations. In addition, we show that the spin-spin correlation length ξ(T) increases rapidly as the temperature is lowered and find ω/T scaling behavior, the hallmark of quantum criticality, at an antiferromagnetic quantum critical point.« less

Optical absorption and disorder in delafossites

DOE PAGES

Senty, Tess R.; Haycock, Barry; Lekse, Jonathan; ...

2017-07-06

Here, we present compelling experimental results of the optical characteristics of transparent oxide CuGaO 2 and related CuGa 1-xFe xO 2 (with 0.00 ≤ x ≤ 0.05) alloys, whereby the forbidden electronic transitions for CuGaO 2 become permissible in the presence of B-site (Ga sites) alloying with Fe. Our computational structural results imply a correlation between the global strain on the system and a decreased optical absorption edge. However, herein, we show that the relatively ordered CuGa 1-xFe xO 2 (for 0.00 ≤ x ≤ 0.04) structures exhibit much weaker vis-absorption compared to the relatively disordered CuGa 0.95Fe 0.05O 2.

Mössbauer study of Cu1-xZnxFe2O4 catalytic materials

NASA Astrophysics Data System (ADS)

Koleva, K.; Velinov, N.; Tsoncheva, T.; Mitov, I.

2014-04-01

Copper zinc ferrites (Cu1-xZnxFe2O4) with different composition (x = 1; 0.2; 0.5; 0.8) were prepared by conventional thermal method. Formation of well crystallized ferrite phase with cubic structure and crystallites size of about 19.08-24.39 nm was observed by Powder X-ray diffraction and Mössbauer spectroscopy. The ferrite materials were tested as catalysts in methanol decomposition to CO and H2. A strong dependence of the catalytic behaviour of Cu1-xZnxFe2O4 ferrites of their composition and the phase transformations which occurred under the reaction medium was established.

The effect of solution pH on the electrochemical performance of nanocrystalline metal ferrites MFe2O4 (M=Cu, Zn, and Ni) thin films

NASA Astrophysics Data System (ADS)

Elsayed, E. M.; Rashad, M. M.; Khalil, H. F. Y.; Ibrahim, I. A.; Hussein, M. R.; El-Sabbah, M. M. B.

2016-04-01

Nanocrystalline metal ferrite MFe2O4 (M=Cu, Zn, and Ni) thin films have been synthesized via electrodeposition-anodization process. Electrodeposited (M)Fe2 alloys were obtained from aqueous sulfate bath. The formed alloys were electrochemically oxidized (anodized) in aqueous (1 M KOH) solution, at room temperature, to the corresponding hydroxides. The parameters controlling the current efficiency of the electrodeposition of (M)Fe2 alloys such as the bath composition and the current density were studied and optimized. The anodized (M)Fe2 alloy films were annealed in air at 400 °C for 2 h. The results revealed the formation of three ferrite thin films were formed. The crystallite sizes of the produced films were in the range between 45 and 60 nm. The microstructure of the formed film was ferrite type dependent. The corrosion behavior of ferrite thin films in different pH solutions was investigated using open circuit potential (OCP) and potentiodynamic polarization measurements. The open circuit potential indicates that the initial potential E im of ZnFe2O4 thin films remained constant for a short time, then sharply increased in the less negative direction in acidic and alkaline medium compared with Ni and Cu ferrite films. The values of the corrosion current density I corr were higher for the ZnFe2O4 films at pH values of 1 and 12 compared with that of NiFe2O4 and CuFe2O4 which were higher only at pH value 1. The corrosion rate was very low for the three ferrite films when immersion in the neutral medium. The surface morphology recommended that Ni and Cu ferrite films were safely used in neutral and alkaline medium, whereas Zn ferrite film was only used in neutral atmospheres.

Comparison of catalytic activities for photocatalytic and sonocatalytic degradation of organic dye in the presence of ternary Fe{sub 3}O{sub 4}/ZnO/CuO magnetic heteregenous nanocatalyst

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taufik, Ardiansyah; Saleh, Rosari, E-mail: rosari.saleh@gmail.com, E-mail: rosari.saleh@ui.ac.id; Integrated Laboratory of Energy and Environment, Fakultas MIPA-Universitas Indonesia, 16424 Depok

2016-04-19

The Fe{sub 3}O{sub 4}/ZnO/CuO nanocatalyst with various CuO loading were synthesized by sol-gel method and were characterized by powder X-ray diffraction, field emission scanning electron microscopy, energy-dispersive X-ray spectroscopy, UV-Vis spectroscopy, and vibrating sample magnetometry. The findings demonstrate that all samples exhibit ferromagnetic behavior at room temperatureand containa well-crystalline ternary oxide nanocatalyst. Methylene blue was taken as the model of organic dye to evaluate its photocatalytic and sonocatalytic degradation in the presence of Fe{sub 3}O{sub 4}/ZnO/CuO nanocatalyst. The observed degradation activity indicate that the order of degradation of methylene blue issonocatalysis> photocatalysis. Fe{sub 3}O{sub 4}/ZnO/CuO nanocatalyst with the lowest CuOmore » loading exhibit the highest rate of degradation of methylene blue during the sono- and photocatalytic processes. The experimental data shows that holes are the predominant oxidative species involved in the sono- and photodegradation of methylene blue.« less

Influence of Oxygen Partial Pressure during Processing on the Thermoelectric Properties of Aerosol-Deposited CuFeO2

PubMed Central

Stöcker, Thomas; Exner, Jörg; Schubert, Michael; Streibl, Maximilian; Moos, Ralf

2016-01-01

In the field of thermoelectric energy conversion, oxide materials show promising potential due to their good stability in oxidizing environments. Hence, the influence of oxygen partial pressure during synthesis on the thermoelectric properties of Cu-Delafossites at high temperatures was investigated in this study. For these purposes, CuFeO2 powders were synthetized using a conventional mixed-oxide technique. X-ray diffraction (XRD) studies were conducted to determine the crystal structures of the delafossites associated with the oxygen content during the synthesis. Out of these powders, films with a thickness of about 25 µm were prepared by the relatively new aerosol-deposition (AD) coating technique. It is based on a room temperature impact consolidation process (RTIC) to deposit dense solid films of ceramic materials on various substrates without using a high-temperature step during the coating process. On these dense CuFeO2 films deposited on alumina substrates with electrode structures, the Seebeck coefficient and the electrical conductivity were measured as a function of temperature and oxygen partial pressure. We compared the thermoelectric properties of both standard processed and aerosol deposited CuFeO2 up to 900 °C and investigated the influence of oxygen partial pressure on the electrical conductivity, on the Seebeck coefficient and on the high temperature stability of CuFeO2. These studies may not only help to improve the thermoelectric material in the high-temperature case, but may also serve as an initial basis to establish a defect chemical model. PMID:28773351

Interfacial magnetism and exchange coupling in BiFeO3-CuO nanocomposite.

PubMed

Chakrabarti, Kaushik; Sarkar, Babusona; Ashok, Vishal Dev; Das, Kajari; Chaudhuri, Sheli Sinha; De, S K

2013-12-20

Ferromagnetic BiFeO3 nanocrystals of average size 9 nm were used to form a composite with antiferromagnetic CuO nanosheets, with the composition (x)BiFeO3/(100-x)CuO, x = 0, 20, 40, 50, 60, 80 and 100. The dispersion of BiFeO3 nanocrystals into the CuO matrix was confirmed by x-ray diffraction and transmission electron microscopy. The ferromagnetic ordering as observed in pure BiFeO3 occurs mainly due to the reduction in the particle size as compared to the wavelength (62 nm) of the spiral modulated spin structure of the bulk BiFeO3. Surface spin disorder of BiFeO3 nanocrystals gives rise to an exponential behavior of magnetization with temperature. Strong magnetic exchange coupling between the BiFeO3 nanocrystal and the CuO matrix induces an interfacial superparamagnetic phase with a blocking temperature of about 80 K. Zero field and field cooled magnetizations are analyzed by a ferromagnetic core and disordered spin shell model. The temperature dependence of the calculated saturation magnetization exhibits three magnetic contributions in three temperature regimes. The BiFeO3/CuO nanocomposites reveal an exchange bias effect below 170 K. The maximum exchange bias field HEB is 1841 Oe for x = 50 at 5 K under field cooling of 50 kOe. The exchange bias coupling results in an increase of coercivity of 1934 Oe at 5 K. Blocked spins within an interfacial region give rise to a remarkable exchange bias effect in the nanocomposite due to strong magnetic exchange coupling between the BiFeO3 nanocrystals and the CuO nanosheets.

Fe{sub 3}O{sub 4}/CuO/ZnO/Nano graphene platelets (Fe{sub 3}O{sub 4}/CuO/ZnO/NGP) composites prepared by sol-gel method with enhanced sonocatalytic activity for the removal of dye

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hendry, Tju; Taufik, Ardiansyah; Saleh, Rosari, E-mail: rosari.saleh@gmail.com, E-mail: rosari.saleh@ui.ac.id

2016-04-19

In this study, an attempt has been made to synthesize nanographene platelets coupled with Fe3O4/CuO/ZnO (Fe3O4/CuO/ZnO/NGP) with various ZnO loadings using a two step methods, sol-gel followed by hydrothermal method. Characterization was carried out by X-ray diffraction, energy-dispersive X-ray spectroscopy and vibrating sample magnetometer. The sonocatalytic performance was evaluated by degradation of methylene blue under ultrasonic irradiation.The Fe3O4/CuO/ZnO/NGP showed superior sonocatalytic activity than the Fe3O4/CuO/ZnO materials. They also showed high stability and can be easily separated from the reaction system for recycling process.

Mercury removal from coal combustion flue gas by modified fly ash.

PubMed

Xu, Wenqing; Wang, Hairui; Zhu, Tingyu; Kuang, Junyan; Jing, Pengfei

2013-02-01

Fly ash is a potential alternative to activated carbon for mercury adsorption. The effects of physicochemical properties on the mercury adsorption performance of three fly ash samples were investigated. X-ray fluorescence spectroscopy, X-ray photoelectron spectroscopy, and other methods were used to characterize the samples. Results indicate that mercury adsorption on fly ash is primarily physisorption and chemisorption. High specific surface areas and small pore diameters are beneficial to efficient mercury removal. Incompletely burned carbon is also an important factor for the improvement of mercury removal efficiency, in particular. The C-M bond, which is formed by the reaction of C and Ti, Si and other elements, may improve mercury oxidation. The samples modified with CuBr2, CuCl2 and FeCl3 showed excellent performance for Hg removal, because the chlorine in metal chlorides acts as an oxidant that promotes the conversion of elemental mercury (Hg0) into its oxidized form (Hg2+). Cu2+ and Fe3+ can also promote Hg0 oxidation as catalysts. HCl and O2 promote the adsorption of Hg by modified fly ash, whereas SO2 inhibits the Hg adsorption because of competitive adsorption for active sites. Fly ash samples modified with CuBr2, CuCl2 and FeCl3 are therefore promising materials for controlling mercury emissions.

Influence of Oxygen on Cu Distribution Behavior Between Molten Iron and FeS-Based Flux

NASA Astrophysics Data System (ADS)

Kang, Youngjo; Shin, Kil-Sun; Morita, Kazuki

2018-06-01

Cu distribution behavior between molten iron and a sulfide flux was investigated under different oxygen contents in the sulfide flux to clarify the effect of oxygen content in FeS-based flux on Cu removal. The activity coefficient of CuS0.5 could be experimentally estimated according to the oxygen content. Based on the present result, the possibility of Cu removal by sulfide flux containing a certain amount of oxide was discussed.

Polypyrrole Coated Cellulosic Substrate Modified by Copper Oxide as Electrode for Nitrate Electroreduction

NASA Astrophysics Data System (ADS)

Hamam, A.; Oukil, D.; Dib, A.; Hammache, H.; Makhloufi, L.; Saidani, B.

2015-08-01

The aim of this work is to synthesize polypyrrole (PPy) films on nonconducting cellulosic substrate and modified by copper oxide particles for use in the nitrate electroreduction process. Firstly, the chemical polymerization of polypyrrole onto cellulosic substrate is conducted by using FeCl3 as an oxidant and pyrrole as monomer. The thickness and topography of the different PPy films obtained were estimated using a profilometer apparatus. The electrochemical reactivity of the obtained electrodes was tested by voltamperometry technique and electrochemical impedance spectroscopy. Secondly, the modification of the PPy film surface by incorporation of copper oxide particles is conducted by applying a galvanostatic procedure from a CuCl2 solution. The SEM, EDX and XRD analysis showed the presence of CuO particles in the polymer films with dimensions less than 50 nm. From cyclic voltamperometry experiments, the composite activity for the nitrate electroreduction reaction was evaluated and the peak of nitrate reduction is found to vary linearly with initial nitrate concentration.

Non-toxic invert analog glass compositions of high modulus

NASA Technical Reports Server (NTRS)

Bacon, J. F. (Inventor)

1974-01-01

Glass compositions having a Young's modulus of at least 15 million psi are described. They and a specific modulus of at least 110 million inches consist essentially of, in mols, 15 to 40% SiO2, 6 to 15% Li2O, 24 to 45% of at least two bivalent oxides selected from the group consisting of Ca, NzO, MgO and CuO; 13 to 39% of at least two trivalent oxides selected from the group consisting of Al2O3, Fe2O3, B2O3, La2O3, and Y2O3 and up to 15% of one or more tetravelent oxides selected from the group consisting of ZrO2, TiO2 and CeO2. The high modulus, low density glass compositions contain no toxic elements. The composition, glass density, Young's modulus, and specific modulus for 28 representative glasses are presented. The fiber modulus of five glasses are given.

Experimental investigation of inhomogeneities, nanoscopic phase separation, and magnetism in arc melted Fe-Cu metals with equal atomic ratio of the constituents

NASA Astrophysics Data System (ADS)

Hassnain Jaffari, G.; Aftab, M.; Anjum, D. H.; Cha, Dongkyu; Poirier, Gerald; Ismat Shah, S.

2015-12-01

Composition gradient and phase separation at the nanoscale have been investigated for arc-melted and solidified with equiatomic Fe-Cu. Diffraction studies revealed that Fe and Cu exhibited phase separation with no trace of any mixing. Microscopy studies revealed that immiscible Fe-Cu form dense bulk nanocomposite. The spatial distribution of Fe and Cu showed existence of two distinct regions, i.e., Fe-rich and Cu-rich regions. Fe-rich regions have Cu precipitates of various sizes and different shapes, with Fe forming meshes or channels greater than 100 nm in size. On the other hand, the matrix of Cu-rich regions formed strips with fine strands of nanosized Fe. Macromagnetic response of the system showed ferromagnetic behavior with a magnetic moment being equal to about 2.13 μB/ Fe atom and a bulk like negligible value of coercivity over the temperature range of 5-300 K. Anisotropy constant has been calculated from various laws of approach to saturation, and its value is extracted to be equal to 1350 J/m3. Inhomogeneous strain within the Cu and Fe crystallites has been calculated for the (unannealed) sample solidified after arc-melting. Annealed sample also exhibited local inhomogeneity with removal of inhomogeneous strain and no appreciable change in magnetic character. However, for the annealed sample phase separated Fe exhibited homogenous strain.

Efficiency of several leaching reagents on removal of Cu, Pb, Cd, and Zn from highly contaminated paddy soil.

PubMed

Gao, Ruili; Zhu, Pengfei; Guo, Guangguang; Hu, Hongqing; Zhu, Jun; Fu, Qingling

2016-11-01

The efficiency of five different single leaching reagents (tartaric acid (TA), citric acid (CA), CaCl 2 , FeCl 3 , EDTA) and two different composite leaching reagents (CA + FeCl 3 , CA + EDTA) on removing Cu, Pb, Zn, and Cd from contaminated paddy soil in Hunan Province (in China) was studied. The results indicated that the efficiencies of CA, FeCl 3 , and EDTA on extracting Cu, Pb, Cd, and Zn from soil were greater than that of TA and CaCl 2 , and their extraction efficiencies were EDTA ≥ FeCl 3 > CA. The efficiencies of CA + FeCl 3 on extracting Cu, Pb, Cd, and Zn were higher than that of single CA or FeCl 3 . The 25 mmol L -1 CA + 20 mmol L -1 FeCl 3 was a promising composite leaching reagent for paddy soil, and it could remove Cu (57.6 %), Pb (59.3 %), Cd (84.8 %), and Zn (28.0 %), respectively. With the same amount of leaching reagent, the efficiency of continuous leaching by several times was higher than that by once. In addition, the easily reducible and oxidizable fractions of heavy metals showed significant decrease during the process of leaching.

Mechanism insight of pollutant degradation and bromate inhibition by Fe-Cu-MCM-41 catalyzed ozonation.

PubMed

Chen, Weirui; Li, Xukai; Tang, Yiming; Zhou, Jialu; Wu, Dan; Wu, Yin; Li, Laisheng

2018-03-15

A flexible catalyst, Fe-Cu-MCM-41, was employed to enhance diclofenac (DCF) mineralization and inhibit bromate formation in catalytic ozonation process. Greater TOC removal was achieved in Fe-Cu-MCM-41/O 3 process (78%) than those in Fe-MCM-41/O 3 (65%), Cu-MCM-41/O 3 (73%) and sole ozonation (42%). But it was interesting that both Cu-MCM-41/O 3 and Fe-MCM-41/O 3 achieved 93% bromate inhibition efficiency, only 71% inhibition efficiency was observed in Fe-Cu-MCM-41/O 3 . Influence of pH, TBA/NaHSO 3 and detection of by-products were conducted to explore the mechanism. By Pyridine adsorption-IR and XPS, a relationship was found among activity of catalysts, Lewis acid sites and electron transfer effect between Fe (II/III) and Cu (I/II). Fe-Cu-MCM-41 promoted ozone decomposition to generate OH, which accounted for enhanced DCF mineralization. The consumption of aqueous O 3 also suppressed the oxidative of Br - and HBrO/Br - . More HBrO/BrO - accumulated in catalytic ozonation process and less bromate generated. Bromate formation in Fe-Cu-MCM-41/O 3 process was sensitive with pH value, the acidic condition was not favor for bromate formation. Both DCF mineralization and bromate inhibition were influenced by surface reaction. Moreover, Fe-Cu-MCM-41 showed excellent catalytic performance in suppressing the accumulation of carboxylic acid, especially for oxalic acid. Nearly no oxalic acid was detected during Fe-Cu-MCM-41/O 3 process. Copyright © 2017 Elsevier B.V. All rights reserved.

Rapid Assessment of the Ce-Co-Fe-Cu System for Permanent Magnetic Applications

DOE PAGES

Meng, F.; Chaudhary, R. P.; Gandha, K.; ...

2018-04-23

Here, this work focuses on the rapid synthesis and characterization of quaternary Ce(CoFeCu) 5 alloy libraries to assess their potential viability as permanent magnets. Arrays of bulk specimens with controlled compositions were synthesized via laser engineered net shaping (LENS) by feeding different ratios of alloy powders into a melt pool created by a laser. Based on the assessment of the magnetic properties of the LENS printed samples, arc-melted and cast ingots were prepared with varying Fe (5–20 at.%) and Co (60–45 at.%) compositions while maintaining constant Ce (16 at.%) and Cu (19 at.%) content. The evolution of the microstructure andmore » phases with varying chemical compositions and their dependence on magnetic properties are analyzed in as-cast and heat-treated samples. In both the LENS printed and cast samples, we find the best magnetic properties correspond to a predominantly single-phase Ce(CoFeCu) 5 microstructure in which high coercivity ( H c > 10 kOe) can be achieved without any microstructural refinement.« less

Rapid Assessment of the Ce-Co-Fe-Cu System for Permanent Magnetic Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meng, F.; Chaudhary, R. P.; Gandha, K.

Here, this work focuses on the rapid synthesis and characterization of quaternary Ce(CoFeCu) 5 alloy libraries to assess their potential viability as permanent magnets. Arrays of bulk specimens with controlled compositions were synthesized via laser engineered net shaping (LENS) by feeding different ratios of alloy powders into a melt pool created by a laser. Based on the assessment of the magnetic properties of the LENS printed samples, arc-melted and cast ingots were prepared with varying Fe (5–20 at.%) and Co (60–45 at.%) compositions while maintaining constant Ce (16 at.%) and Cu (19 at.%) content. The evolution of the microstructure andmore » phases with varying chemical compositions and their dependence on magnetic properties are analyzed in as-cast and heat-treated samples. In both the LENS printed and cast samples, we find the best magnetic properties correspond to a predominantly single-phase Ce(CoFeCu) 5 microstructure in which high coercivity ( H c > 10 kOe) can be achieved without any microstructural refinement.« less

Fenton-like Degradation of Phenol Catalyzed by a Series of Fe-Containing Mixed Oxides Systems

NASA Astrophysics Data System (ADS)

Alhmoud, T. T.; Mahmoud, S. S.; Hammoudeh, A. Y.

2018-02-01

In our attempts to develop a solid catalyst to degrade organic pollutants in wastewater via the Fenton-like reaction, six Fe-containing mixed oxide systems were prepared by means of the sol-gel auto-combustion method to have the following stoichiometries: CuFe1.2O2.8, BaFe7.2O11.8, BaFe7.2Cu2O13.8, BaFe5.4V3O16.6, BaFe4.8Cu2V3O17.7 and Ag2Fe5.4V3O16.6. The prepared systems were thermally treated at 550°C, 650°C, 800°C and 1100°C, and then characterized by XRD to identify the present phases. The systems were tested with respect to their catalytic efficiency in the degradation of phenol (200 ppm) in water where CuFe1.2O2.8 was found to be the most reactive one (80% removal in 60 min). It showed thereby first-order kinetics and an enhanced behavior under irradiation with a 30-W LED light source. The positive role of irradiation was most obvious in the case of Ag2Fe5.4V3O16.6 in which almost complete conversion was achieved in 120 min compared to only 45% in the same period but without irradiation. However, increasing the temperature at which thermal treatment is performed was found to suppress the catalytic activity of the system. Due to their high efficiency and rather low leaching rates of constituents, CuFe1.2O2.8 or Ag2Fe5.4V3O16.6 seem to be very promising in the Fenton-like degradation of organic pollutants.

Engineering nonspherical hollow structures with complex interiors by template-engaged redox etching.

PubMed

Wang, Zhiyu; Luan, Deyan; Li, Chang Ming; Su, Fabing; Madhavi, Srinivasan; Boey, Freddy Yin Chiang; Lou, Xiong Wen

2010-11-17

Despite the significant advancement in making hollow structures, one unsolved challenge in the field is how to engineer hollow structures with specific shapes, tunable compositions, and desirable interior structures. In particular, top-down engineering the interiors inside preformed hollow structures is still a daunting task. In this work, we demonstrate a facile approach for the preparation of a variety of uniform hollow structures, including Cu(2)O@Fe(OH)(x) nanorattles and Fe(OH)(x) cages with various shapes and dimensions by template-engaged redox etching of shape-controlled Cu(2)O crystals. The composition can be readily modulated at different structural levels to generate other interesting structures such as Cu(2)O@Fe(2)O(3) and Cu@Fe(3)O(4) rattles, as well as Fe(2)O(3) and Fe(3)O(4) cages. More remarkably, this strategy enables top-down engineering the interiors of hollow structures as demonstrated by the fabrication of double-walled nanorattles and nanoboxes, and even box-in-box structures. In addition, this approach is also applied to form Au and MnO(x) based hollow structures.

Copper(II) cyanido-bridged bimetallic nitroprusside-based complexes: Syntheses, X-ray structures, magnetic properties, 57Fe Mössbauer spectroscopy and thermal studies

NASA Astrophysics Data System (ADS)

Trávníček, Zdeněk; Herchel, Radovan; Mikulík, Jiří; Zbořil, Radek

2010-05-01

Three heterobimetallic cyanido-bridged copper(II) nitroprusside-based complexes of the compositions [Cu(tet)Fe(CN) 5NO]·H 2O ( 1), where tet= N,N' -bis(3-aminopropyl)ethylenediamine, [Cu(hto)Fe(CN) 5NO]·2H 2O ( 2), where hto=1,3,6,9,11,14-hexaazatricyclo[12.2.1.1 6,9]octadecane and [Cu(nme) 2Fe(CN) 5NO]·H 2O ( 3), where nme= N-methylethylenediamine, were synthesized and characterized by elemental analyses, 57Fe Mössbauer and FTIR spectroscopies, thermal analysis, magnetic measurements and single-crystal X-ray analysis. The products of thermal degradation processes of 2 and 3 were studied by XRD, 57Fe Mössbauer spectroscopy, SEM and EDS, and they were identified as mixtures of CuFe 2O 4 and CuO.

Concretionary manganese-iron oxides in streams and their usefulness as a sample medium for geochemical prospecting

USGS Publications Warehouse

Nowlan, G.A.

1976-01-01

Correlation studies of 400 samples of sieved stream sediments and 325 samples of fluvial, concretionary Mn-Fe oxides from Maine resulted in the separation of elements into the following categories: (1) elements not scavenged by Mn-Fe oxides - B, Cr, K, Mg, Rb, Sc, Ti, V, and Zr; (2) elements probably not scavenged by Mn-Fe oxides - Ag, Be, Ca, Ga, La, Sb, and Y; (3) elements scavenged weakly by Mn-Fe oxides - Cu, Mo, Pb, and Sr; (4) elements scavenged strongly by Mn oxides - Ba, Cd, Co, Ni, Tl, and Zn; and (5) elements scavenged strongly by Fe oxides - As and In. Studies of the scavenged elements showed that the deviation from the mean is characteristically greater in oxide samples as compared to sieved sediments from the same locality. However, a significant increase in contrast between anomalous and background localities, when oxides are the sample medium, more than offsets the disadvantage of data scatter. The use of oxides as a sampling medium clearly and significantly accentuates anomalous localities. In general, non-ratioed data on oxides give very nearly the same results as data consisting of scavenged elements ratioed to Mn and Fe. However, ratioed data expand the geographic area of specific anomalies. Cd and Zn consistently show strong correlations with concretionary Mn-Fe oxides, but their concentrations in the oxides do not generally show as much contrast between anomalous and background localities as do Cu, Mo, and Pb. These latter elements are strongly scavenged where rocks are mineralized. ?? 1976.

Effect of synthesis method on structure, band gap and surface morphology of delafossite oxides, CuAlO2 and CuFeO2

NASA Astrophysics Data System (ADS)

Shah, Aadil Abass; Azam, Ameer

2018-04-01

In this research work we have reported the synthesis of two different delafossites, CuAlO2 and CuFeO2 by two different synthesis methods viz hydrothermal method and the combustion method. The effect of synthesis on structure, band gap and morphology of the synthesized delafossites was carried out using various techniques. The phase and structure of the synthesized delafossites were studied and confirmed using X-ray diffraction and the crystallite size was calculated. FTIR measurements showed the presence of different stretching modes and functional groups in the synthesized oxides. The surface morphology was studied using the scanning electron microscopy. The band gap of the synthesized delafossite oxides was found to be in the range of 2.8 and 3.3 eV.

Interfacial Redox Reactions Associated Ionic Transport in Oxide-Based Memories.

PubMed

Younis, Adnan; Chu, Dewei; Shah, Abdul Hadi; Du, Haiwei; Li, Sean

2017-01-18

As an alternative to transistor-based flash memories, redox reactions mediated resistive switches are considered as the most promising next-generation nonvolatile memories that combine the advantages of a simple metal/solid electrolyte (insulator)/metal structure, high scalability, low power consumption, and fast processing. For cation-based memories, the unavailability of in-built mobile cations in many solid electrolytes/insulators (e.g., Ta 2 O 5 , SiO 2 , etc.) instigates the essential role of absorbed water in films to keep electroneutrality for redox reactions at counter electrodes. Herein, we demonstrate electrochemical characteristics (oxidation/reduction reactions) of active electrodes (Ag and Cu) at the electrode/electrolyte interface and their subsequent ions transportation in Fe 3 O 4 film by means of cyclic voltammetry measurements. By posing positive potentials on Ag/Cu active electrodes, Ag preferentially oxidized to Ag + , while Cu prefers to oxidize into Cu 2+ first, followed by Cu/Cu + oxidation. By sweeping the reverse potential, the oxidized ions can be subsequently reduced at the counter electrode. The results presented here provide a detailed understanding of the resistive switching phenomenon in Fe 3 O 4 -based memory cells. The results were further discussed on the basis of electrochemically assisted cations diffusions in the presence of absorbed surface water molecules in the film.

Solvothermal fabrication and enhanced visible light photocatalytic activity of Cu2O-reduced graphene oxide composite microspheres for photodegradation of Rhodamine B

NASA Astrophysics Data System (ADS)

Sun, Lingling; Wang, Guohong; Hao, Ruirui; Han, Deyan; Cao, Sheng

2015-12-01

The addition of graphene oxide (GO) in the semiconductors has been regarded as one of the effective methods to enhance their photocatalytic activity. In this study, Cu2O-reduced graphene oxide (Cu2O-rGO) composites with low loading (0-0.5 wt.%) of graphene oxide (GO) were produced by a one-step green solvothermal method in ethanol system by using Cu(NO3)2·3H2O and glutamic acid as copper precursor and reducing agent, respectively. During the solvothermal treatment, GO was reduced to rGO. The as-prepared Cu2O-reduced graphene oxide composite microspheres exhibited enhanced photocatalytic activity toward the degradation of RhB aqueous solution under visible light irradiation. At the optimal loading of graphene oxide (0.05 wt.%), Cu2O-rGO composites showed the highest photocatalytic activity, exceeding that of pure Cu2O and commercial Degussa P25 by a factor of 2.9 and 7.9, respectively. The enhanced photocatalytic activity may be ascribed to the strong coupling interaction between Cu2O particles and rGO nanosheets, which reduces the recombination of charge carriers.

Structure and Mechanical Properties of Al-Cu-Fe-X Alloys with Excellent Thermal Stability.

PubMed

Školáková, Andrea; Novák, Pavel; Mejzlíková, Lucie; Průša, Filip; Salvetr, Pavel; Vojtěch, Dalibor

2017-11-05

In this work, the structure and mechanical properties of innovative Al-Cu-Fe based alloys were studied. We focused on preparation and characterization of rapidly solidified and hot extruded Al-Cu-Fe, Al-Cu-Fe-Ni and Al-Cu-Fe-Cr alloys. The content of transition metals affects mechanical properties and structure. For this reason, microstructure, phase composition, hardness and thermal stability have been investigated in this study. The results showed exceptional thermal stability of these alloys and very good values of mechanical properties. Alloying by chromium ensured the highest thermal stability, while nickel addition refined the structure of the consolidated alloy. High thermal stability of all tested alloys was described in context with the transformation of the quasicrystalline phases to other types of intermetallics.

Structure and Mechanical Properties of Al-Cu-Fe-X Alloys with Excellent Thermal Stability

PubMed Central

Školáková, Andrea; Novák, Pavel; Mejzlíková, Lucie; Průša, Filip; Salvetr, Pavel; Vojtěch, Dalibor

2017-01-01

In this work, the structure and mechanical properties of innovative Al-Cu-Fe based alloys were studied. We focused on preparation and characterization of rapidly solidified and hot extruded Al-Cu-Fe, Al-Cu-Fe-Ni and Al-Cu-Fe-Cr alloys. The content of transition metals affects mechanical properties and structure. For this reason, microstructure, phase composition, hardness and thermal stability have been investigated in this study. The results showed exceptional thermal stability of these alloys and very good values of mechanical properties. Alloying by chromium ensured the highest thermal stability, while nickel addition refined the structure of the consolidated alloy. High thermal stability of all tested alloys was described in context with the transformation of the quasicrystalline phases to other types of intermetallics. PMID:29113096

Photoinduced formation of reactive oxygen species and electrons from metal oxide-silica nanocomposite: An EPR spin-trapping study

NASA Astrophysics Data System (ADS)

Zhao, Hongxia; Chen, Xiuying; Li, Xintong; Shen, Chen; Qu, Baocheng; Gao, Jingsuo; Chen, Jingwen; Quan, Xie

2017-09-01

Metal oxide nanocomposites with photocatalytic activity have the potential for many applications in environmental remediation and biomedicine. In this study, we investigated the formation and stabilization of electrons/holes from three metal oxide-silica nanocomposites (CuO-SiO2, Fe2O3-SiO2 and ZnO-SiO2) under irradiation by electron paramagnetic resonance (EPR) technology. The characteristic EPR signals with g = 2.00070-2.00105, ΔHp-p = 2.17-2.37 G were determined, which corresponded to lattice-trapped electrons. Moreover, the generation of active species from CuO-SiO2, Fe2O3-SiO2 and ZnO-SiO2 in aqueous solution under irradiation was also systematically studied. The results showed that all the three nanocomposites could generate hydroxyl radical, singlet oxygen and electron. CuO-SiO2 was more effective than Fe2O3-SiO2 and ZnO-SiO2 in producing hydroxyl radical and electrons, while ZnO-SiO2 was the most efficient in generating singlet oxygen. In addition, CuO-SiO2 exhibited most obviously photocatalytic activity toward degradation of bisphenol A, followed by Fe2O3-SiO2 and ZnO-SiO2. These findings will provide vital insights into photocatalytic mechanisms and potentially photoinduced toxicity of metal oxide-silica nanocomposites.

Stabilizing CuPd Nanoparticles via CuPd Coupling to WO 2.72 Nanorods in Electrochemical Oxidation of Formic Acid

DOE PAGES

Xi, Zheng; Li, Junrui; Su, Dong; ...

2017-10-05

Stabilizing a 3d-transition metal component M from an MPd alloy structure in an acidic environment is key to the enhancement of MPd catalysis for various reactions. Here we show a strategy to stabilize Cu in 5 nm CuPd nanoparticles (NPs) by coupling the CuPd NPs with perovskite-type WO 2.72 nanorods (NRs). The CuPd NPs are prepared by controlled diffusion of Cu into Pd NPs and the coupled CuPd/WO 2.72 are synthesized by growing WO 2.72 NRs in the presence of CuPd NPs. The CuPd/WO 2.72 can stabilize Cu in 0.1 M HClO4 solution and, as a result, they show Cu,more » Pd composition dependent activity for the electrochemical oxidation of formic acid in 0.1 M HClO 4 + 0.1 M HCOOH. Among three different CuPd/WO 2.72 studied, the Cu 48Pd 52/WO 2.72 is the most efficient catalyst with its mass activity reaching 2086 mA/mgPd in a broad potential range of 0.40 to 0.80 V (vs. RHE) and staying at this value after the 12 h chronoamperometry test at 0.40 V. The synthesis can be extended to obtain other MPd/WO 2.72 (M = Fe, Co, Ni), making it possible to study MPd-WO 2.72 interactions and MPd stabilization on enhancing MPd catalysis for various chemical reactions.« less

Amorphous Mixed-Metal Oxide Thin Films from Aqueous Solution Precursors with Near-Atomic Smoothness.

PubMed

Kast, Matthew G; Cochran, Elizabeth A; Enman, Lisa J; Mitchson, Gavin; Ditto, Jeffrey; Siefe, Chris; Plassmeyer, Paul N; Greenaway, Ann L; Johnson, David C; Page, Catherine J; Boettcher, Shannon W

2016-12-28

Thin films with tunable and homogeneous composition are required for many applications. We report the synthesis and characterization of a new class of compositionally homogeneous thin films that are amorphous solid solutions of Al 2 O 3 and transition metal oxides (TMO x ) including VO x , CrO x , MnO x , Fe 2 O 3 , CoO x , NiO, CuO x , and ZnO. The synthesis is enabled by the rapid decomposition of molecular transition-metal nitrates TM(NO 3 ) x at low temperature along with precondensed oligomeric Al(OH) x (NO 3 ) 3-x cluster species, both of which can be processed from aq solution. The films are dense, ultrasmooth (R rms < 1 nm, near 0.1 nm in many cases), and atomically mixed amorphous metal-oxide alloys over a large composition range. We assess the chemical principles that favor the formation of amorphous homogeneous films over rougher phase-segregated nanocrystalline films. The synthesis is easily extended to other compositions of transition and main-group metal oxides. To demonstrate versatility, we synthesized amorphous V 0.1 Cr 0.1 Mn 0.1 Fe 0.1 Zn 0.1 Al 0.5 O x and V 0.2 Cr 0.2 Fe 0.2 Al 0.4 O x with R rms ≈ 0.1 nm and uniform composition. The combination of ideal physical properties (dense, smooth, uniform) and broad composition tunability provides a platform for film synthesis that can be used to study fundamental phenomena when the effects of transition metal cation identity, solid-state concentration of d-electrons or d-states, and/or crystallinity need to be controlled. The new platform has broad potential use in controlling interfacial phenomena such as electron transfer in solar-cell contacts or surface reactivity in heterogeneous catalysis.

Ecosystems supporting clusters of sporadic TSEs demonstrate excesses of the radical-generating divalent cation manganese and deficiencies of antioxidant co factors Cu, Se, Fe, Zn. Does a foreign cation substitution at prion protein's Cu domain initiate TSE?

PubMed

Purdey, M

2000-02-01

Analyses of food chains supporting isolated clusters of sporadic TSEs (CWD in N Colorado, scrapie in Iceland, CJD in Slovakia) demonstrate a consistent 2 1/2+ fold greater concentration of the pro-oxidant divalent cation, manganese (Mn), in relation to normal levels recorded in adjoining TSE-free localities. Deficiencies of the antioxidant co factors Cu/Se/Zn/Fe and Mg, P and Na were also consistently recorded in TSE foodchains. Similarities between the clinical/pathological profile of TSEs and Mn delayed psycho-neurotoxicity in miners are cited, and a novel theory generated which suggests that sporadic TSE results from early life dependence of TSE susceptible genotypes on ecosystems characterised by this specific pattern of mineral imbalance. Low Cu/Fe induces an excessive absorption of Mn in ruminants and an increased oxidation of Mn2+ into its pro oxidant species, Mn3+, which accumulates in mitochondria of CNS astrocytes in Mn SOD deficient genotypes. Deficiencies of scavenger co factors Cu/Zn/Se/Fe in the CNS permits Mn3+ initiated chain reactions of auto-oxidant mediated neuronal degeneration to proliferate, which, in turn, up-regulates the expression of the Cu-metalloprotein, prion protein (PrP). Once the rate of PrP turnover and its demand for Cu exceeds the already depleted supply of Cu within the CNS, PrP can no longer bind sufficient Cu to maintain its conformation. Mn3+ substitutes at the vacated Cu domain on PrP, thus priming up a latent capacity for lethal auto-oxidative activity to be carried along with PrP like a 'trojan horse'; where Mn 3+ serves as the integral 'infectious' transmissible component of the misfolded PrP-cation complex. The Mn overactivation of concanavalin A binding to glycoprotein and Mn-initiated autoxidation results in a diverse pathological profile involving receptor capping, aggregation/modification of CNS membrane/cytoskeletal proteins. TSE ensues. The BSE/nv CJD strain entails a 'synthetic' induction of the same CNS mineral disturbance, where 'in utero' exposure to Cu-chelating insecticides/Mn supplements accelerates the onset of a more virulent 'strain' of adolescent TSE. Copyright 2000 Harcourt Publishers Ltd.

A comprehensive study of magnetic exchanges in the layered oxychalcogenides Sr 3 Fe 2 O 5 Cu 2 Q 2 ( Q = S, Se)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lü, Minfeng; Mentré, Olivier; Gordon, Elijah E.

2017-12-01

The layered oxysulfide Sr3Fe2O5Cu2S2 was prepared, and its crystal structure and magnetic properties were characterized by synchrotron X-ray diffraction (XRD), powder neutron diffraction (PND), Mössbauer spectroscopy measurements and by density functional theory (DFT) calculations. In addition, the spin exchange interactions leading to the ordered magnetic structure of Sr3Fe2O5Cu2S2 were compared with those of its selenium analogue Sr3Fe2O5Cu2Se2. The oxysulfide Sr3Fe2O5Cu2S2 adopts a G-type antiferromagnetic (AFM) structure at a temperature in the range 485–512 K, which is comparable with the three-dimensional (3D) AFM ordering temperature, TN ≈ 490 K, found for Sr3Fe2O5Cu2Se2. Consistent with this observation, the spin exchange interactions ofmore » the magnetic (Sr3Fe2O5)2+ layers are slightly greater (but comparable) for oxysulfide than for the oxyselenide. Attempts to reduce or oxidize Sr3Fe2O5Cu2S2 using topochemical routes yield metallic Fe.« less

Conditions and mechanisms for the formation of nano-sized Delafossite (CuFeO2) at temperatures ≤90 °C in aqueous solution

NASA Astrophysics Data System (ADS)

John, Melanie; Heuss-Aßbichler, Soraya; Ullrich, Aladin

2016-02-01

In this study, we present the mechanism of CuFeO2 formation in aqueous solution at low temperatures ≤90 °C, using sulfate salts as reactants. Furthermore, we demonstrate the influence of experimental conditions (alkalization, reaction and ageing temperature and time) on the synthesized nanoparticles. In all cases, GR-SO4, a Fe(II-III) layered double hydroxysulphate (Fe2+4Fe3+2(OH)12·SO4) and Cu2O precipitate first. During further OH- supply GR-SO4 oxidizes and forms Fe10O14(OH)2, Cu2O and CuFeO2 crystals. Due to the high pH further CuFeO2 crystals grow at the cost of the unstable intermediate products. The reaction rate increases with increasing ageing temperature, reaction pH and, in particular, NaOH concentrations in the solution. As a result, highly crystalline CuFeO2 (3R and 2H polytypes) nanoparticles showing hexagonal morphology can be synthesized at 70 °C within 10 h or at 50 °C within 1 week. The formation of 2H polytype is favored by additional OH- supply during the pH-stat time and rather low temperatures.

A double Fe-Ti oxide and Fe-sulphide liquid immiscibility in the Itsindro Gabbro Complex, Madagascar

NASA Astrophysics Data System (ADS)

Augé, Thierry; Bailly, Laurent; Roig, Jean-Yves

2017-11-01

The petrology and mineralogy of the Itsindro complex in south-central Madagascar has been investigated through samples obtained from the 320.7 m-deep Lanjanina borehole. The section consists of a 254 m-thick pyroxenite unit with interbedded gabbro layers that overlies a gabbro unit and is itself overlain by a 19 m-thick granite unit. Most of the structures are sub-horizontal. A weak magmatic layering is locally observed but at the scale of the core, the intrusion does not appear to be a layered complex. Pyroxenite and gabbro show a systematic disseminated mineralization consisting of Fe-Ti-P oxides and Fe-(Cu-Ni) sulphides that takes the form of ilmenite-titanomagnetite ± apatite and pyrrhotite ± chalcopyrite ± pentlandite. In the upper zone, from 90 to 72 m, sub-massive centimetre-to decimetre-sized layers of oxides and sulphides comprise a total of 16 m of sub-massive sulphide (the main mineralized zone). In this mineralized zone the oxide/sulphide ratio is close to 1/1. The sulphide is strongly dominated by pyrrhotite, which may locally contain inclusions of molybdenite crystals with the Re sulphide rheniite (ReS2). Oxides are generally euhedral, included in or attached to the Fe-sulphide, and also locally form sub-massive centimetre-sized bands. Apatite as a cumulus phase is ubiquitous. Locally it may account for 30% of the ore-rich samples and some samples consist of apatite-Fe-Ti oxides-Fe-Cu-Ni sulphides with virtually no silicate. Apatite is the main REE carrier but the total REE content remains low (<90 ppm). Mineral compositions and whole rock geochemistry indicate that the rocks are highly differentiated, and in spite of a relatively limited thickness, the differentiation process is observed. Two zones can be distinguished: from the bottom to 162.8 m we see a decrease in the Mg number of olivine and pyroxene, and a drop in TiO2 and Al2O3 for the latter. A reverse trend is then observed within the pyroxenite unit from the 162.8 m level upwards. The main mineralized zone is located in the upper part of this unit, about 70 m above this discontinuity. The highly differentiated Fe-Ti-P facies of the Lanjanina series in the Itsindro Gabbro Complex have been interpreted as corresponding to the Fe-Ti-P rich, Si-poor member remaining after an immiscible segregation of an evolved mafic magma. The granite dykes and the overlying granite unit represent the second, Si-rich member of the immiscibility process. The presence of large amounts of sulphide is attributed to sulphur contamination of the Fe-Ti-rich liquid. Fe-Ti oxides will tend to crystallize on the sulphide droplets and the accumulation of dense Fe-sulphides (liquid) and associated Fe-Ti oxides (solid) will result in this complex and unusual association taking the form of a net texture.

Effect of adsorbed films on friction of Al2O3-metal systems

NASA Technical Reports Server (NTRS)

Pepper, S. V.

1976-01-01

The kinetic friction of polycrystalline Al2O3 sliding on Cu, Ni, and Fe in ultrahigh vacuum was studied as a function of the surface chemistry of the metal. Clean metal surfaces were exposed to O2, Cl2, C2H4, and C2H3Cl, and the change in friction due to the adsorbed species was observed. Auger electron spectroscopy assessed the elemental composition of the metal surface. It was found that the systems exposed to Cl2 exhibited low friction, interpreted as the van der Waals force between the Al2O3 and metal chloride. The generation of metal oxide by oxygen exposures resulted in an increase in friction, interpreted as due to strong interfacial bonds established by reaction of metal oxide with Al2O3 to form the complex oxide (spinel). The only effect of C2H4 was to increase the friction of the Fe system, but C2H3Cl exposures decreases friction in both Ni and Fe systems, indicating the dominance of the chlorine over the ethylene complex on the surface

Integrated photooxidative extractive deep desulfurization using metal doped TiO2 and eutectic based ionic liquid

NASA Astrophysics Data System (ADS)

Zaid, Hayyiratul Fatimah Mohd; Kait, Chong Fai; Mutalib, Mohamed Ibrahim Abdul

2016-11-01

A series of metal doped TiO2 namely Fe/TiO2, Cu/TiO2 and Cu-Fe/TiO2 were synthesized and characterized, to be used as a photocatalyst in the integrated photooxidative extractive deep desulfurization for model oil (dodecane) and diesel fuel. The order of the photocatalytic activity was Cu-Fe/TiO2 followed by Cu/TiO2 and then Fe/TiO2. Cu-Fe/TiO2 was an effective photocatalyst for sulfur conversion at ambient atmospheric pressure. Hydrogen peroxide was used as the source of oxidant and eutectic-based ionic liquid as the extractant. Sulfur conversion in model oil reached 100%. Removal of sulfur from model oil was done by two times extraction with a removal of 97.06% in the first run and 2.94% in the second run.

Determining the composition of small features in atom probe: bcc Cu-rich precipitates in an Fe-rich matrix.

PubMed

Morley, A; Sha, G; Hirosawa, S; Cerezo, A; Smith, G D W

2009-04-01

Aberrations in the ion trajectories near the specimen surface are an important factor in the spatial resolution of the atom probe technique. Near the boundary between two phases with dissimilar evaporation fields, ion trajectory overlaps may occur, leading to a biased measurement of composition in the vicinity of this interface. In the case of very small second-phase precipitates, the region affected by trajectory overlaps may extend to the centre of the precipitate prohibiting a direct measurement of composition. A method of quantifying the aberrant matrix contribution and thus estimating the underlying composition is presented. This method is applied to the Fe-Cu-alloy system, where the precipitation of low-nanometre size Cu-rich precipitates is of considerable technical importance in a number of materials applications. It is shown definitively that there is a non-zero underlying level of Fe within precipitates formed upon thermal ageing, which is augmented and masked by trajectory overlaps. The concentration of Fe in the precipitate phase is shown to be a function of ageing temperature. An estimate of the underlying Fe level is made, which is at lower levels than commonly reported by atom probe investigations.

Oxidation of nitroxyl anion to nitric oxide by copper ions

PubMed Central

Nelli, Silvia; Hillen, Mark; Buyukafsar, Kansu; Martin, William

2000-01-01

This study made use of a nitric oxide-sensitive electrode to examine possible means of generating nitric oxide from nitroxyl anion (NO−) released upon the decomposition of Angeli's salt. Our results show that copper ions (from CuSO4) catalyze the rapid and efficient oxidation of nitroxyl to nitric oxide. Indeed, the concentrations of copper required to do so (0.1–100 μM) are roughly 100-times lower than those required to generate equivalent amounts of nitric oxide from S-nitroso-N-acetyl-D,L-penicillamine (SNAP). Experiments with ascorbate (1 mM), which reduces Cu2+ ions to Cu+, and with the Cu2+ chelators, EDTA and cuprizone, and the Cu+ chelator, neocuproine, each at 1 mM, suggest that the oxidation is catalyzed by copper ions in both valency states. Some compounds containing other transition metals, i.e. methaemoglobin, ferricytochrome c and Mn(III)TMPyP, were much less efficient than CuSO4 in catalyzing the formation of nitric oxide from nitroxyl, while FeSO4, FeCl3, MnCl2, and ZnSO4 were inactive. Of the copper containing enzymes examined, Cu-Zn superoxide dismutase and ceruloplasmin were weak generators of nitric oxide from nitroxyl, even at concentrations (2500 and 30 u ml−1, respectively) vastly greater than are present endogenously. Two others, ascorbate oxidase (10 u ml−1) and tyrosinase (250 u ml−1) were inactive. Our findings suggest that a copper-containing enzyme may be responsible for the rapid oxidation of nitroxyl to nitric oxide by cells, but the identity of such an enzyme remains elusive. PMID:10991931

Characteristics of oxide scale formed on Cu-bearing austenitic stainless steel during early stages of high temperature oxidation

NASA Astrophysics Data System (ADS)

Swaminathan, Srinivasan; Krishna, Nanda Gopala; Kim, Dong-Ik

2015-10-01

Oxide scale evolution on Cu-bearing austenitic stainless steel 304H at 650 °C, in ambient air, for exposure times 100, 300, 500 and 1000 h, has been investigated. Surface morphology and chemistry of the oxide scale grown were examined using SEM/EDX and XPS. The oxidation kinetics was determined by measuring the weight change using an electronic balance. At the initial stage, up to 500 h of exposure time, the oxidation rate was rapid due to surface reactions governed primarily by oxygen ingress, and then, dropped to a low rate after prolonged oxidation for 1000 h. The diffusion of reactants through the initially formed oxide scale limits the oxidation rate at longer times, thus, the progress of reaction followed the parabolic kinetics. The formed oxide scale was enriched significantly with segregation and subsequent oxidation of Nb, and finely dispersed metallic Cu particles. Within the time frame of oxidation, the oxide scale was mainly composed of mixed oxides such as FeCr2O4 and MnCr2O4 along with the binary oxides of Fe, Cr and Mn. Moreover, the precipitation fraction of Cu-rich particles on the oxide scale increased markedly with increase of exposure times. The chemical heterogeneity of oxide scale suggests that the oxidation occurred in a non-selective manner.

Microstructure and Shear Strength in Brazing Joint of Mo-Cu Composite with 304 Stainless Steel by Ni-Cr-P Filler Metal

NASA Astrophysics Data System (ADS)

Wang, Juan; Wang, Jiteng; Li, Yajiang; Zheng, Deshuang

2015-07-01

The brazing of Mo-Cu composite and 304 stainless steel was carried out in vacuum with Ni-Cr-P filler metal at 980 °C for 20 min. Microstructure in Mo-Cu/304 stainless steel joint was investigated by field-emission scanning electron microscope (FE-SEM) with energy dispersive spectrometer (EDS) and shear strength was measured by shearing test. The results indicate that shear strength of the Mo-Cu/304 stainless steel joint is about 155 MPa. There forms eutectic structure of γ-Ni solid solution with Ni3P in the braze seam. Ni-Cu(Mo) and Ni-Fe solid solution are at the interface beside Mo-Cu composite and 304 stainless steel, respectively. Shear fracture exhibits mixed ductile-brittle fracture feature with trans-granular fracture, ductile dimples and tearing edges. Fracture originates from the interface between brazing seam and Mo-Cu composite and it propagates to the braze seam due to the formation of brittle Ni5P2 and Cr3P precipitation.

A High-Performance Sodium-Ion Full Cell with a Layered Oxide Cathode and a Phosphorous-Based Composite Anode

DOE PAGES

Oh, Seung-Min; Oh, Pilgun; Kim, Sang-Ok; ...

2016-12-29

A low-cost sodium-ion full cell with a O3-type layered Na[Cu 0.2(Fe 1/3Mn2/3) 0.8]O 2 cathode and an alloy-type P-TiP2-C anode is presented. The cathode is synthesized by an oxalate coprecipitation method and optimized cathodes shows a high specific capacity of 135 mAh g -1 at 0.1C rate with a high rate capability of 90 mAh g-1 at 1C rate and 70 mAh g -1 at 2C rate with good cyclability. The full cell exhibits better capacity retention than the half cell with the cathode due to the elimination of the degradation caused by sodium-metal anode. The dramatically enhanced electrochemical performancemore » of the Na[Cu 0.2(Fe 1/3Mn 2/3) 0.8]O 2 / P-TiP 2-C full cell compared to that of the sample with no Cu is attributed to the structural stabilization imparted by Cu by suppressing the phase change from the O3 structure to the P3 structure during cycling.« less

Effects of temperature and holding time on bonding W and W-Cu composites with an amorphous W-Fe coated copper foil as the interlayer by hot-pressing

NASA Astrophysics Data System (ADS)

Zhao, Pei; Wang, Song; Guo, Shibin; Chen, Yixiang; Ling, Yunhan; Li, Jiangtao

2013-07-01

W and W-Cu composites were bonded with an amorphous W-Fe coated copper foil as the interlayer at different temperature and holding time by hot pressing method. Effects of the bonding temperature and holding time on the microstructure and thermal conductivity of the bonded specimens were investigated. The thermal conductivity of the bonded sample increased with the bonding temperature and reached the maximum at 1000 °C, but essentially unchanged with the holding time. Because at 1000 °C more W-Fe compounds would be formed at the interlayer, which were helpful for tight bonding of W and W-Cu composites, and the grain size was larger which could reduce thermal resistance. The W-Cu FGM bonded by this method showed good resistance to thermal load, and performed well when facing to short pulse plasma in experimental advanced superconducting tokamak (the first full superconductive fusion device in the world).

Assessing the cytotoxicity of ambient particulate matter (PM) using Chinese hamster ovary (CHO) cells and its relationship with the PM chemical composition and oxidative potential

NASA Astrophysics Data System (ADS)

Wang, Yixiang; Plewa, Michael J.; Mukherjee, Ujjal Kumar; Verma, Vishal

2018-04-01

We assessed mammalian cell cytotoxicity of ambient PM2.5 and investigated its association with the oxidative potential (OP) and chemical composition of the particles. Sixteen PM samples spanning in various seasons (fall, winter, spring and summer) were collected from an urban site in central Illinois. Cytotoxicity (LC50) in terms of the volume of air that kills 50% of the cells were calculated, which varied from 4.3 to 7.2 m3 of air. The OP was measured by two assays - the dithiothreitol (DTT) and the surrogate lung fluid (SLF) assay. In DTT assay, we measured two endpoints - hydroxyl radicals (•OH) generation and DTT consumption (the conventionally measured endpoint), while only •OH generation was measured in the SLF assay. Although, all three endpoints in the OP assays correlated significantly (P ≤ 0.05) with LC50, the correlation of reactive oxygen species (ROS) generation in DTT and SLF assays was much higher (r > 0.80 for •OH generation versus LC50) than the DTT consumption (r = 0.58). To further understand the components in PM that drive cytotoxicity and OP, concentration of water-soluble metals (Fe, Cu, Co, Cr, Mn, Ni, Pb, V, Hg, and Zn), organic carbon (OC), water soluble organic carbon (WSOC), and elemental carbon (EC) were measured. Among all the chemical components, Fe, Cu and WSOC correlated most (r > 0.70; P ≤ 0.01) with the cytotoxicity. DTT consumption correlated only with OC and WSOC (r > 0.80; P ≤ 0.01), while •OH generation in DTT and SLF assay correlated with both WSOC (r > 0.70; P ≤ 0.01) and metals (i.e. Fe and Cu; r > 0.75; P ≤ 0.01). Our results suggest a strong link between the PM2.5 OP and its cytotoxicity. Furthermore, the synergistic interactions among the organic compounds (i.e. WSOC) and metals (Fe and Cu) to enhance the ROS generation, which are more effectively captured in •OH generation endpoints in DTT and SLF assay than the DTT consumption, appear to be largely responsible for the observed mammalian cell cytotoxicity of PM2.5.

Physicochemical and thermal characteristics of the sludge produced after thermochemical treatment of petrochemical wastewater.

PubMed

Verma, Shilpi; Prasad, Basheshwar; Mishra, I M

2012-01-01

The present work describes the physicochemical and thermal characteristics of the sludge generated after thermochemical treatment of wastewater from a petrochemical plant manufacturing purified terephthalic acid (PTA). Although FeCl3 was found to be more effective than CuSO4 in removing COD from wastewater, the settling and filtration characteristics of FeCl3 sludge were poorer. Addition of cationic polyacrylamide (CPAA; 0.050kg/m3) to the FeCl3 wastewater system greatly improved the values of the filter characteristics of specific cake resistance (1.2 x 10(8) m/kg) and resistance of filter medium (9.9 x 10(8) m(-1)) from the earlier values of 1.9 x 10(9) m/kg and 1.7 x 10(8) m(-1), respectively. SEM-EDAX and FTIR studies were undertaken, to understand the sludge structure and composition, respectively. The moisture distribution in the CuSO4 sludge, FeCl3 sludge and FeCl3 + CPAA sludge showed that the amount of bound water content in the CuSO4 and FeCl3 + CPAA sludges is less than that of the FeCl3 sludge and there was a significant reduction in the solid-water bond strength of FeCl3 + CPAA sludge, which was responsible for better settling and filtration characteristics. Due to the hazardous nature of the sludge, land application is not a possible route of disposal. The thermal degradation behaviour of the sludge was studied for its possible use as a co-fuel. The studies showed that degradation behaviour of the sludge was exothermic in nature. Because of the exothermic nature of the sludge, it can be used in making fuel briquettes or it can be disposed of via wet air oxidation.

Sorption Mechanisms of Cesium on Cu II2Fe II(CN) 6and Cu II3[Fe III(CN) 6] 2Hexacyanoferrates and Their Relation to the Crystalline Structure

NASA Astrophysics Data System (ADS)

Ayrault, S.; Jimenez, B.; Garnier, E.; Fedoroff, M.; Jones, D. J.; Loos-Neskovic, C.

1998-12-01

CuII2FeII(CN)6·xH2O and CuII3[FeIII(CN)6]2·xH2O can be prepared with reproducible chemical compositions and structures after careful washing. They have cubicFmoverline3mstructures with iron vacancies. In CuII2FeII(CN)6, copper occupies two different sites: Cu1 in position 4blinked to Fe through the CN groups, and Cu2 not linked to the CN groups and partially occupying the interstitial 24epositions. The second type of site is not present in CuII3[FeIII(CN)6]2. Sorption kinetics and isotherms were determined for cesium on both hexacyanoferrates by batch experiments. On CuII3[FeIII(CN)6]2, the maximum uptake is only 0.073 Cs/Fe (at./at.). On CuII2FeII(CN)6, the uptake reaches 1.5 Cs/Fe. The sorption kinetics include at least two steps: at1/2variation until approximately 72 h and then a slow evolution studied up to 6 months. The sorption mechanism is complex. The main process seems to be diffusion of ion pairs, followed by a reorganization of the solid, resulting in one or more new solid phases. The presence of the Cu2 site seems to play a favorable role in the sorption. Owing to its good midterm stability and the first rapid step of exchange, CuII2FeII(CN)6·xH2O seems to be one of the most promising compounds for the recovery of cesium from nuclear liquid wastes.

As(V) removal capacity of FeCu bimetallic nanoparticles in aqueous solutions: The influence of Cu content and morphologic changes in bimetallic nanoparticles.

PubMed

Sepúlveda, Pamela; Rubio, María A; Baltazar, Samuel E; Rojas-Nunez, J; Sánchez Llamazares, J L; Garcia, Alejandra García; Arancibia-Miranda, Nicolás

2018-08-15

In this study, bimetallic nanoparticles (BMNPs) with different mass ratios of Cu and Fe were evaluated. The influence of the morphology on the removal of pollutants was explored through theoretical and experimental studies, which revealed the best structure for removing arsenate (As(V)) in aqueous systems. To evidence the surface characteristics and differences among BMNPs with different mass proportions of Fe and Cu, several characterization techniques were used. Microscopy techniques and molecular dynamics simulations were applied to determine the differences in morphology and structure. In addition, X-ray diffraction (XRD) was used to determine the presence of various oxides. Finally, the magnetization response was evaluated, revealing differences among the materials. Our cumulative data show that BMNPs with low amounts of Cu (Fe 0.9 Cu 0.1 ) had a non-uniform core-shell structure with agglomerate-type chains of magnetite, whereas a Janus-like structure was observed in BMNPs with high amounts of Cu (Fe 0.5 Cu 0.5 ). However, a non-uniform core-shell structure (Fe 0.9 Cu 0.1 ) facilitated electron transfer among Fe, Cu and As, which increased the adsorption rate (k), capacity (q e ) and intensity (n). The mechanism of As removal was also explored in a comparative study of the phase and morphology of BMNPs pre- and post-sorption. Copyright © 2018 Elsevier Inc. All rights reserved.

Collisions in outer space produced an icosahedral phase in the Khatyrka meteorite never observed previously in the laboratory.

PubMed

Bindi, Luca; Lin, Chaney; Ma, Chi; Steinhardt, Paul J

2016-12-08

We report the first occurrence of an icosahedral quasicrystal with composition Al 62.0(8) Cu 31.2(8) Fe 6.8(4) , outside the measured equilibrium stability field at standard pressure of the previously reported Al-Cu-Fe quasicrystal (Al x Cu y Fe z , with x between 61 and 64, y between 24 and 26, z between 12 and 13%). The new icosahedral mineral formed naturally and was discovered in the Khatyrka meteorite, a recently described CV3 carbonaceous chondrite that experienced shock metamorphism, local melting (with conditions exceeding 5 GPa and 1,200 °C in some locations), and rapid cooling, all of which likely resulted from impact-induced shock in space. This is the first example of a quasicrystal composition discovered in nature prior to being synthesized in the laboratory. The new composition was found in a grain that has a separate metal assemblage containing icosahedrite (Al 63 Cu 24 Fe 13 ), currently the only other known naturally occurring mineral with icosahedral symmetry (though the latter composition had already been observed in the laboratory prior to its discovery in nature). The chemistry of both the icosahedral phases was characterized by electron microprobe, and the rotational symmetry was confirmed by means of electron backscatter diffraction.

Synthesis of KMnO4-treated magnetic graphene oxide nanocomposite (Fe3O4@GO/MnO x ) and its application for removing of Cu2+ ions from aqueous solution

NASA Astrophysics Data System (ADS)

Zhang, Huining; Chang, Qing; Jiang, Yu; Li, Huili; Yang, Yahong

2018-04-01

A magnetic KMnO4-treated graphene-oxide-based nanocomposite, Fe3O4@GO/MnO x , was synthesized through a facile hydrothermal technique. The properties of the Fe3O4@GO/MnO x nanocomposite were characterized by SEM, XRD and FTIR. Batch experiments showed that the maximum adsorption capacity calculated by the Langmuir model for Cu2+ was 62.65 mg g-1 at T = 303.15 K. Kinetics and XPS analysis also revealed that the mechanism of Cu2+ removal was mainly a chemical adsorption process involving both the MnO x particles and oxygen functional groups. The prepared Fe3O4@GO/MnO x was found to be an ideal adsorbent for the removal of Cu2+ ions due to the MnO x particle coating, and was easily separated using a magnetic field after utilization. Reusability studies imply that Fe3O4@GO/MnO x is a suitable material for heavy metal ion removal from aqueous solutions in real applications.

Facile synthesis of iron oxides/reduced graphene oxide composites: application for electromagnetic wave absorption at high temperature.

PubMed

Zhang, Lili; Yu, Xinxin; Hu, Hongrui; Li, Yang; Wu, Mingzai; Wang, Zhongzhu; Li, Guang; Sun, Zhaoqi; Chen, Changle

2015-03-19

Iron oxides/reduced graphene oxide composites were synthesized by facile thermochemical reactions of graphite oxide and FeSO4 · 7H2O. By adjusting reaction temperature, α-Fe2O3/reduced graphene oxide and Fe3O4/reduced graphene oxide composites can be obtained conveniently. Graphene oxide and reduced graphene oxide sheets were demonstrated to regulate the phase transition from α-Fe2O3 to Fe3O4 via γ-Fe2O3, which was reported for the first time. The hydroxyl groups attached on the graphene oxide sheets and H2 gas generated during the annealing of graphene oxide are believed to play an important role during these phase transformations. These samples showed good electromagnetic wave absorption performance due to their electromagnetic complementary effect. These samples possess much better electromagnetic wave absorption properties than the mixture of separately prepared Fe3O4 with rGO, suggesting the crucial role of synthetic method in determining the product properties. Also, these samples perform much better than commercial absorbers. Most importantly, the great stability of these composites is highly advantageous for applications as electromagnetic wave absorption materials at high temperatures.

Facile synthesis of iron oxides/reduced graphene oxide composites: application for electromagnetic wave absorption at high temperature

PubMed Central

Zhang, Lili; Yu, Xinxin; Hu, Hongrui; Li, Yang; Wu, Mingzai; Wang, Zhongzhu; Li, Guang; Sun, Zhaoqi; Chen, Changle

2015-01-01

Iron oxides/reduced graphene oxide composites were synthesized by facile thermochemical reactions of graphite oxide and FeSO4·7H2O. By adjusting reaction temperature, α-Fe2O3/reduced graphene oxide and Fe3O4/reduced graphene oxide composites can be obtained conveniently. Graphene oxide and reduced graphene oxide sheets were demonstrated to regulate the phase transition from α-Fe2O3 to Fe3O4 via γ-Fe2O3, which was reported for the first time. The hydroxyl groups attached on the graphene oxide sheets and H2 gas generated during the annealing of graphene oxide are believed to play an important role during these phase transformations. These samples showed good electromagnetic wave absorption performance due to their electromagnetic complementary effect. These samples possess much better electromagnetic wave absorption properties than the mixture of separately prepared Fe3O4 with rGO, suggesting the crucial role of synthetic method in determining the product properties. Also, these samples perform much better than commercial absorbers. Most importantly, the great stability of these composites is highly advantageous for applications as electromagnetic wave absorption materials at high temperatures. PMID:25788158

Non-injection synthesis of monodisperse Cu-Fe-S nanocrystals and their size dependent properties.

PubMed

Gabka, Grzegorz; Bujak, Piotr; Żukrowski, Jan; Zabost, Damian; Kotwica, Kamil; Malinowska, Karolina; Ostrowski, Andrzej; Wielgus, Ireneusz; Lisowski, Wojciech; Sobczak, Janusz W; Przybylski, Marek; Pron, Adam

2016-06-01

It is demonstrated that ternary Cu-Fe-S nanocrystals differing in composition (from Cu-rich to Fe-rich), structure (chalcopyrite or high bornite) and size can be obtained from a mixture of CuCl, FeCl3, thiourea and oleic acid (OA) in oleylamine (OLA) using the heating up procedure. This new preparation method yields the smallest Cu-Fe-S nanocrystals ever reported to date (1.5 nm for the high bornite structure and 2.7 nm for the chalcopyrite structure). A comparative study of nanocrystals of the same composition (Cu1.6Fe1.0S2.0) but different in size (2.7 nm and 9.3 nm) revealed a pronounced quantum confinement effect, confirmed by three different techniques: UV-vis spectroscopy, cyclic voltammetry and Mössbauer spectroscopy. The optical band gap increased from 0.60 eV in the bulk material to 0.69 eV in the nanocrystals of 9.3 nm size and to 1.39 eV in nanocrystals of 2.7 nm size. The same trend was observed in the electrochemical band gaps, derived from cyclic voltammetry studies (band gaps of 0.74 eV and 1.54 eV). The quantum effect was also manifested in Mössbauer spectroscopy by an abrupt change in the spectrum from a quadrupole doublet to a Zeeman sextet below 10 K, which could be interpreted in terms of the well defined energy states in these nanoparticles, resulting from quantum confinement. The Mössbauer spectroscopic data confirmed, in addition to the results of XPS spectroscopy, the co-existence of Fe(iii) and Fe(ii) in the synthesized nanocrystals. The organic shell composition was investigated by NMR (after dissolution of the inorganic core) and IR spectroscopy. Both methods identified oleylamine (OLA) and 1-octadecene (ODE) as surfacial ligands, the latter being formed in situ via an elimination-hydrogenation reaction occurring between OLA and the nanocrystal surface.

Surfactant-free electrodeposition of reduced graphene oxide/copper composite coatings with enhanced wear resistance

NASA Astrophysics Data System (ADS)

Mai, Y. J.; Zhou, M. P.; Ling, H. J.; Chen, F. X.; Lian, W. Q.; Jie, X. H.

2018-03-01

How to uniformly disperse graphene sheets into the electrolyte is one of the main challenges to synthesize graphene enhanced nanocomposites by electrodeposition. A surfactant-free colloidal solution comprised of copper (II)-ethylene diamine tetra acetic acid ([CuIIEDTA]2-) complexes and graphene oxide (GO) sheets is proposed to electrodeposit reduced graphene oxide/copper (RGO/Cu) composite coatings. Anionic [CuIIEDTA]2- complexes stably coexist with negatively charged GO sheets due to the electrostatic repulsion between them, facilitating the electrochemical reduction and uniform dispersion of GO sheets into the copper matrix. The RGO/Cu composite coatings are well characterized by XRD, Raman, SEM and XPS. Their tribological behavior as a function of RGO content in composite coatings and normal loads are investigated. Also the chemical composition and topography of the wear tracks for the composite coatings are analyzed to deduce the lubricating and anti-wear mechanism of RGO/Cu composite coatings.

Optoelectronic properties of Fe impurities in delafossite oxide materials. A high-throughput investigation

NASA Astrophysics Data System (ADS)

Haycock, Barry; Lewis, James P.

2014-03-01

A group of materials that shows promise in optoelectronic applications is the family of oxide materials (delafossites), of the form ABO2, where the A site is a monovalent cation (e . g . , Cu, Ag, or Au) and the B site is a trivalent cation (e . g ., Ga, Y, Al, or In). The bandgap of some delafossites can be tailored for specific purposes, such as in photocatalysis applications, with B-site doping. We report on our recent investigations of the properties of CuGaO2, CuInO2, CuAlO2 and NaInO2 and predict the relative disorder of Fe impurities by comparing crystallographic metrics resulting from Fe doping. We performed approximately 10K calculations, in parallel on the Titan platform (Oak Ridge Leadership Computing Facility), of possible Fe-impurity permutations to determine the most-likely configurations of Fe impurities relative to each another. Our computational approach allows us to study large supercells, consisting of 432 atoms, which enable us to examine the properties of these materials in increments of 1% for the B-site doping of Fe. We will present results from our energetically-preferred supercells and discuss further applications of our techniques applied for characterization of new reconstructions via derived metrics.

Heterogeneous photo-Fenton processes using graphite carbon coating hollow CuFe2O4 spheres for the degradation of methylene blue

NASA Astrophysics Data System (ADS)

Guo, Xiaojun; Wang, Kebai; Li, Dai; Qin, Jiabin

2017-10-01

The novel graphite carbon coating hollow CuFe2O4 spheres were fabricated through solvothermal method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Raman spectra, etc. The catalytic performance of the graphite carbon coating hollow CuFe2O4 spheres was evaluated in photo-Fenton-like degradation of methylene blue (MB) using H2O2 as a green oxidant under light irradiation (λ > 400 nm). The results demonstrated that the hollow CuFe2O4 spheres with graphite carbon coating exhibited superior catalytic activity. In the preparation process of catalyst, the addition of glucose was very important to its catalytic performance. Photoresponse analysis of the typical samples proved that CuFe2O4@graphite carbon core-shell hollow spheres possessed excellent photocurrent response and lower electrochemical impedance. In addition, a possible mechanism for photocatalytic degradation of MB had been presumed. Moreover, after five regeneration cycles, the graphite carbon coating hollow CuFe2O4 spheres still exhibited better properties.

Creep and Oxidation Behavior of Modified CF8C-Plus with W, Cu, Ni, and Cr

NASA Astrophysics Data System (ADS)

Unocic, Kinga A.; Dryepondt, Sebastien; Yamamoto, Yukinori; Maziasz, Philip J.

2016-04-01

The microstructures of modified CF8C-Plus (Fe-19Cr-12Ni-0.4W-3.8Mn-0.2Mo-0.6Nb-0.5Si-0.9C) with W and Cu (CF8CPWCu) and CF8CPWCu enhanced with 21Cr + 15Ni or 22Cr + 17.5Ni were characterized in the as-cast condition and after creep testing. When imaged at lower magnifications, the as-cast microstructure was similar among all three alloys as they all contained a Nb-rich interdendritic phase and Mn-based inclusions. Transmission electron microscopy (TEM) analysis showed the presence of nanoscale Cu-rich nanoprecipitates distributed uniformly throughout the matrix of CF8CPWCu, whereas in CF8CPWCu22/17, Cu precipitates were found primarily at the grain boundaries. The presence of these nanoscale Cu-rich particles, in addition to W-rich Cr23C6, nanoscale Nb carbides, and Z-phase (Nb2Cr2N2), improved the creep strength of the CF8CPWCu steel. Modification of CF8CPWCu with Cr and Ni contents slightly decreased the creep strength but significantly improved the oxidation behavior at 1073 K (800 °C). In particular, the addition of 22Cr and 17.5Ni strongly enhanced the oxidation resistance of the stainless steel resulting in a 100 degrees or greater temperature improvement, and this composition provided the best balance between improving both mechanical properties and oxidation resistance.

Creep and oxidation behavior of modified CF8C-plus with W, Cu, Ni, and Cr

DOE Office of Scientific and Technical Information (OSTI.GOV)

Unocic, Kinga A.; Dryepondt, Sebastien N.; Yamamoto, Yukinori

Here, the microstructures of modified CF8C-Plus (Fe-19Cr-12Ni-0.4W-3.8Mn-0.2Mo-0.6Nb-0.5Si-0.9C) with W and Cu (CF8CPWCu) and CF8CPWCu enhanced with 21Cr + 15Ni or 22Cr + 17.5Ni were characterized in the as-cast condition and after creep testing. When imaged at lower magnifications, the as-cast microstructure was similar among all three alloys as they all contained a Nb-rich interdendritic phase and Mn-based inclusions. Transmission electron microscopy (TEM) analysis showed the presence of nanoscale Cu-rich nanoprecipitates distributed uniformly throughout the matrix of CF8CPWCu, whereas in CF8CPWCu22/17, Cu precipitates were found primarily at the grain boundaries. The presence of these nanoscale Cu-rich particles, in addition to W-richmore » Cr 23C 6, nanoscale Nb carbides, and Z-phase (Nb 2Cr 2N 2), improved the creep strength of the CF8CPWCu steel. Modification of CF8CPWCu with Cr and Ni contents slightly decreased the creep strength but significantly improved the oxidation behavior at 1073 K (800 °C). In particular, the addition of 22Cr and 17.5Ni strongly enhanced the oxidation resistance of the stainless steel resulting in a 100 degrees or greater temperature improvement, and this composition provided the best balance between improving both mechanical properties and oxidation resistance.« less

Creep and oxidation behavior of modified CF8C-plus with W, Cu, Ni, and Cr

DOE PAGES

Unocic, Kinga A.; Dryepondt, Sebastien N.; Yamamoto, Yukinori; ...

2016-02-01

Here, the microstructures of modified CF8C-Plus (Fe-19Cr-12Ni-0.4W-3.8Mn-0.2Mo-0.6Nb-0.5Si-0.9C) with W and Cu (CF8CPWCu) and CF8CPWCu enhanced with 21Cr + 15Ni or 22Cr + 17.5Ni were characterized in the as-cast condition and after creep testing. When imaged at lower magnifications, the as-cast microstructure was similar among all three alloys as they all contained a Nb-rich interdendritic phase and Mn-based inclusions. Transmission electron microscopy (TEM) analysis showed the presence of nanoscale Cu-rich nanoprecipitates distributed uniformly throughout the matrix of CF8CPWCu, whereas in CF8CPWCu22/17, Cu precipitates were found primarily at the grain boundaries. The presence of these nanoscale Cu-rich particles, in addition to W-richmore » Cr 23C 6, nanoscale Nb carbides, and Z-phase (Nb 2Cr 2N 2), improved the creep strength of the CF8CPWCu steel. Modification of CF8CPWCu with Cr and Ni contents slightly decreased the creep strength but significantly improved the oxidation behavior at 1073 K (800 °C). In particular, the addition of 22Cr and 17.5Ni strongly enhanced the oxidation resistance of the stainless steel resulting in a 100 degrees or greater temperature improvement, and this composition provided the best balance between improving both mechanical properties and oxidation resistance.« less

The microstructure-processing-property relationships in an aluminum matrix composite system reinforced by aluminum-copper-iron alloy particles

NASA Astrophysics Data System (ADS)

Tang, Fei

Solid state vacuum sintering was studied in tap densified Al powder and in hot quasi-isostatically forged samples composed of commercial inert gas atomized or high purity Al powder, generated by a gas atomization reaction synthesis (GARS) technique. The GARS process results in spherical Al powder with a far thinner surface oxide. The overall results indicated the enhanced ability of GARS-processed Al and Al alloy powders for solid state sintering, which may lead to simplification of current Al powder consolidation processing methods. Elemental Al-based composites reinforced with spherical Al-Cu-Fe alloy powders were produced by quasi-isostatic forging and vacuum hot pressing (VHP) consolidation methods. It was proved that spherical Al-Cu-Fe alloy powders can serve as an effective reinforcement particulate for elemental Al-based composites, because of their high hardness and a preferred type of matrix/reinforcement interfacial bonding, with reduced strain concentration around the particles. Ultimate tensile strength and yield strength of the composites were increased over the corresponding Al matrix values, far beyond typical observations. This remarkable strengthening was achieved without precipitation hardening and without severe strain hardening during consolidation because of the matrix choice (elemental Al) and the "low shear" consolidation methods utilized. This reinforcement effectiveness is further evidenced by elastic modulus measurements of the composites that are very close to the upper bound predictions of the rule of mixtures. The load partitioning measurements by neutron diffraction showed that composite samples made from GARS powders present significantly higher load transfer efficiency than the composites made from commercially atomized powders. Further analysis of the load sharing measurements and the calculated values of the mismatch of coefficient of thermal expansion (CTE) and the geometrically necessary dislocation (GND) effects suggest that these strengthening mechanisms can be combined to predict accurately the strength of the composites. By neutron diffraction measurements, it also was found that the composites consolidated from Al and Al63Cu25Fe12 quasicrystal alloy reinforcement powders have compressive residual stress in the Al matrix, contrary to the tensile residual stress in typical Al/SiC composites. The composites made by the quasi-isostatic forging process exhibited higher tensile strengths and much higher compressive residual stresses than the composites made by the VHP process.

Chalcophile element geochemistry of the Boggy Plain zoned pluton, southeastern Australia: a S-saturated barren compositionally diverse magmatic system

NASA Astrophysics Data System (ADS)

Park, Jung-Woo; Campbell, Ian H.; Ickert, Ryan B.; Allen, Charlotte M.

2013-02-01

The behavior of the platinum group elements (PGE) and Re in felsic magmas is poorly understood due to scarcity of data. We report the concentrations of Ni, Cu, Re, and PGE in the compositionally diverse Boggy Plain zoned pluton (BPZP), which shows a variation of rock type from gabbro through granodiorite and granite to aplite with a SiO2 range from 52 to 74 wt %. In addition, major silicate and oxide minerals were analyzed for Ni, Cu, and Re, and a systematic sulfide study was carried out to investigate the role of silicate, oxide, and sulfide minerals on chalcophile element geochemistry of the BPZP. Mass balance calculation shows that the whole rock Cu budget hosted by silicate and oxide minerals is <13 wt % and that Cu is dominantly located in sulfide phases, whereas most of the whole rock Ni budget (>70 wt %) is held in major silicate and oxide minerals. Rhenium is dominantly hosted by magnetite and ilmenite. Ovoid-shaped sulfide blebs occur at the boundary between pyroxene phenocrysts and neighboring interstitial phases or within interstitial minerals in the gabbro and the granodiorite. The blebs are composed of pyrrhotite, pyrite, chalcopyrite, and S-bearing Fe-oxide, which contain total trace metals (Co, Ni, Cu, Ag, Pb) up to ~16 wt %. The mineral assemblage, occurrence, shape, and composition of the sulfide blebs are a typical of magmatic sulfide. PGE concentrations in the BPZP vary by more than two orders of magnitude from gabbro (2.7-7.8 ppb Pd, 0.025-0.116 ppb Ir) to aplite (0.05 ppb Pd, 0.001 ppb Ir). Nickel, Cu, Re, and PGE concentrations are positively correlated with MgO in all the rock types although there is a clear discontinuity between the granodiorite and the granite in the trends for Ni, Rh, and Ir when plotted against MgO. Cu/Pd values gradually increase from 6,100 to 52,600 as the MgO content decreases. The sulfide petrology and chalcophile element geochemistry of the BPZP show that sulfide saturation occurred in the late gabbroic stage of magma differentiation. Segregation and distribution of these sulfide blebs controlled Cu and PGE variations within the BPZP rocks although the magma of each rock type may have experienced a different magma evolution history in terms of crustal assimilation and crystal fractionation. The sulfide melt locked in the cumulate rocks must have sequestered a significant portion of the chalcophile elements, which restricted the availability of these metals to magmatic-hydrothermal ore fluids. Therefore, we suggest that the roof rocks that overlay the BPZP were not prospective for magmatic-hydrothermal Cu, Au, or Cu-Au deposits.

Metal contamination as a possible etiology of fibropapillomatosis in juvenile female green sea turtles Chelonia mydas from the southern Atlantic Ocean.

PubMed

da Silva, Cinthia Carneiro; Klein, Roberta Daniele; Barcarolli, Indianara Fernanda; Bianchini, Adalto

2016-01-01

Environmental contaminants have been suggested as a possible cause of fibropapillomatosis (FP) in green sea turtles. In turn, a reduced concentration of serum cholesterol has been indicated as a reliable biomarker of malignancy in vertebrates, including marine turtles. In the present study, metal (Ag, Cd, Cu, Fe, Ni, Pb and Zn) concentrations, oxidative stress parameters [antioxidant capacity against peroxyl radicals (ACAP), protein carbonyls (PC), lipid peroxidation (LPO), frequency of micronucleated cells (FMC)], water content, cholesterol concentration and 3-hydroxy-3-methylglutaryl-CoA reductase (HMGR) activity were analyzed in the blood/serum of juvenile (29.3-59.5cm) female green sea turtles (Chelonia mydas) with FP (n=14) and without FP (n=13) sampled at Ubatuba coast (São Paulo State, southeastern Brazil). Green sea turtles were grouped and analyzed according to the severity of tumors. Individuals heavily afflicted with FP showed significantly higher blood Cu, Pb and Fe concentrations, blood LPO levels, as well as significantly lower serum cholesterol concentrations and HMGR activity than turtles without FP. Significant and positive correlations were observed between HMGR activity and cholesterol concentrations, as well as LPO levels and Fe and Pb concentrations. In turn, Cu and Pb concentrations were significantly and negatively correlated with HMGR activity and cholesterol concentration. Furthermore, Cu, Fe and Pb were positively correlated with each other. Therefore, the reduced concentration of serum cholesterol observed in green sea turtles heavily afflicted with FP is related to a Cu- and Pb-induced inhibition of HMGR activity paralleled by a higher LPO rate induced by increased Fe and Pb concentrations. As oxidative stress is implicated in the pathogenesis of viral infections, our findings support the idea that metal contamination, especially by Cu, Fe and Pb, may be implicated in the etiology of FP in green sea turtles through oxidative stress generation. Copyright © 2015 Elsevier B.V. All rights reserved.

Superconducting transition temperature in the Y(1-x)M(x)Ba2Cu3O(y) system

NASA Astrophysics Data System (ADS)

Suzuki, Takeyuki; Yamazaki, Tsutomu; Sekine, Ryuuta; Koukitsu, Akinori; Seki, Hisashi

1989-04-01

Experimental results are presented for the inclusion of compositional additives, M, to the sintered high-temperature superconductor Y(1-x)M(x)Ba2Cu3O(y); M can be the oxides of Mg, Ce, Gd, Yb, Ti, Zr, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Co, Ni, Zn, B, Al, Ga, In, Si, Ge, Sn, Pb, Sb, Bi, and Te, as well as Li, Na, K, Ca, Sr, and La carbonates. Temperature dependence of the electrical resistance was measured down to about 80 K. Attention is given to the influence of ionic radius and the valence of the M species.

Progressive Oxidation of Pyrite in Five Bituminous Coal Samples: An As XANES and 57Fe Mossbauer Spectroscopic Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kolker,A.; Huggins, F.

2007-01-01

Naturally occurring pyrite commonly contains minor substituted metals and metalloids (As, Se, Hg, Cu, Ni, etc.) that can be released to the environment as a result of its weathering. Arsenic, often the most abundant minor constituent in pyrite, is a sensitive monitor of progressive pyrite oxidation in coal. To test the effect of pyrite composition and environmental parameters on the rate and extent of pyrite oxidation in coal, splits of five bituminous coal samples having differing amounts of pyrite and extents of As substitution in the pyrite, were exposed to a range of simulated weathering conditions over a period ofmore » 17 months. Samples investigated include a Springfield coal from Indiana (whole coal pyritic S = 2.13 wt.%; As in pyrite = detection limit (d.l.) to 0.06 wt.%), two Pittsburgh coal samples from West Virginia (pyritic S = 1.32-1.58 wt.%; As in pyrite = d.l. to 0.34 wt.%), and two samples from the Warrior Basin, Alabama (pyritic S = 0.26-0.27 wt.%; As in pyrite = d.l. to 2.72 wt.%). Samples were collected from active mine faces, and expected differences in the concentration of As in pyrite were confirmed by electron microprobe analysis. Experimental weathering conditions in test chambers were maintained as follows: (1) dry Ar atmosphere; (2) dry O{sub 2} atmosphere; (3) room atmosphere (relative humidity {approx}20-60%); and (4) room atmosphere with samples wetted periodically with double-distilled water. Sample splits were removed after one month, nine months, and 17 months to monitor the extent of As and Fe oxidation using As X-ray absorption near-edge structure (XANES) spectroscopy and {sup 57}Fe Mossbauer spectroscopy, respectively. Arsenic XANES spectroscopy shows progressive oxidation of pyritic As to arsenate, with wetted samples showing the most rapid oxidation. {sup 57}Fe Mossbauer spectroscopy also shows a much greater proportion of Fe{sup 3+} forms (jarosite, Fe{sup 3+} sulfate, FeOOH) for samples stored under wet conditions, but much less difference among samples stored under dry conditions in different atmospheres. The air-wet experiments show evidence of pyrite re-precipitation from soluble ferric sulfates, with As retention in the jarosite phase. Extents of As and Fe oxidation were similar for samples having differing As substitution in pyrite, suggesting that environmental conditions outweigh the composition and amount of pyrite as factors influencing the oxidation rate of Fe sulfides in coal.« less

Metal ferrite oxygen carriers for chemical looping combustion of solid fuels

DOEpatents

Siriwardane, Ranjani V.; Fan, Yueying

2017-01-31

The disclosure provides a metal ferrite oxygen carrier for the chemical looping combustion of solid carbonaceous fuels, such as coal, coke, coal and biomass char, and the like. The metal ferrite oxygen carrier comprises MFe.sub.xO.sub.y on an inert support, where MFe.sub.xO.sub.y is a chemical composition and M is one of Mg, Ca, Sr, Ba, Co, Mn, and combinations thereof. For example, MFe.sub.xO.sub.y may be one of MgFe.sub.2O.sub.4, CaFe.sub.2O.sub.4, SrFe.sub.2O.sub.4, BaFe.sub.2O.sub.4, CoFe.sub.2O.sub.4, MnFeO.sub.3, and combinations thereof. The MFe.sub.xO.sub.y is supported on an inert support. The inert support disperses the MFe.sub.xO.sub.y oxides to avoid agglomeration and improve performance stability. In an embodiment, the inert support comprises from about 5 wt. % to about 60 wt. % of the metal ferrite oxygen carrier and the MFe.sub.xO.sub.y comprises at least 30 wt. % of the metal ferrite oxygen carrier. The metal ferrite oxygen carriers disclosed display improved reduction rates over Fe.sub.2O.sub.3, and improved oxidation rates over CuO.

Electronic, Magnetic, and Redox Properties of [MFe(3)S(4)] Clusters (M = Cd, Cu, Cr) in Pyrococcus furiosus Ferredoxin.

PubMed

Staples, Christopher R.; Dhawan, Ish K.; Finnegan, Michael G.; Dwinell, Derek A.; Zhou, Zhi Hao; Huang, Heshu; Verhagen, Marc F. J. M.; Adams, Michael W. W.; Johnson, Michael K.

1997-12-03

The ground- and excited-state properties of heterometallic [CuFe(3)S(4)](2+,+), [CdFe(3)S(4)](2+,+), and [CrFe(3)S(4)](2+,+) cubane clusters assembled in Pyrococcus furiosus ferredoxin have been investigated by the combination of EPR and variable-temperature/variable-field magnetic circular dichroism (MCD) studies. The results indicate Cd(2+) incorporation into [Fe(3)S(4)](0,-) cluster fragments to yield S = 2 [CdFe(3)S(4)](2+) and S = (5)/(2) [CdFe(3)S(4)](+) clusters and Cu(+) incorporation into [Fe(3)S(4)](+,0) cluster fragments to yield S = (1)/(2) [CuFe(3)S(4)](2+) and S = 2 [CuFe(3)S(4)](+) clusters. This is the first report of the preparation of cubane type [CrFe(3)S(4)](2+,+) clusters, and the combination of EPR and MCD results indicates S = 0 and S = (3)/(2) ground states for the oxidized and reduced forms, respectively. Midpoint potentials for the [CdFe(3)S(4)](2+,+), [CrFe(3)S(4)](2+,+), and [CuFe(3)S(4)](2+,+) couples, E(m) = -470 +/- 15, -440 +/- 10, and +190 +/- 10 mV (vs NHE), respectively, were determined by EPR-monitored redox titrations or direct electrochemistry at a glassy carbon electrode. The trends in redox potential, ground-state spin, and electron delocalization of [MFe(3)S(4)](2+,+) clusters in P. furiosus ferredoxin are discussed as a function of heterometal (M = Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, and Tl).

One-step assembly of Fe(III)-CMC chelate hydrogel onto nanoneedle-like CuO@Cu membrane with superhydrophilicity for oil-water separation

NASA Astrophysics Data System (ADS)

Dai, Jiangdong; Chang, Zhongshuai; Xie, Atian; Zhang, Ruilong; Tian, Sujun; Ge, Wenna; Yan, Yongsheng; Li, Chunxiang; Xu, Wei; Shao, Rong

2018-05-01

The research of superhydrophilic interface is developing rapidly, but the preparations of superhydrophilic surfaces through simple methods are still challenging. Herein, we reported a facile, rapid and environmentally-friendly approach for preparing a novel superhydrophilic and underwater superoleophobic membrane via the thermal oxidation of Cu mesh and one-step coordinated assembly of Fe(III)-CMC chelate hydrogel. Superhydrophilicity was attributed to the hydrophilicity of Fe(III)-CMC chelate hydrogel and nanoneedle-like rough structure of CuO@Cu membrane. The membrane was used to separate a variety of oil/water mixtures and exhibited excellent separation performance. Moreover, the membrane exhibited the excellent durability and superior stability against corrosion conditions. We envision that the Fe(III)-CMC@CuO@Cu membrane with good underwater superoleophobicity could provide a candidate not only for oil/water separation but also many other potential applications such as underwater oil manipulation, self-clean, and bio-adhesion control.

[Advanced treatment of coking wastewater with a novel heterogeneous electro-Fenton technology].

PubMed

Li, Hai-Tao; Li, Yu-Ping; Zhang, An-Yang; Cao, Hong-Bin; Li, Xin-Gang; Zhang, Yi

2011-01-01

A novel electro-catalytic reactor, with oxygen-reduction cathode (PAQ/GF), dimensionally stable anode (IrO2-RuO2 -TiO2/ Ti) and heterogeneous catalysts, is developed for advanced treatment of coking wastewater after biological process, integrating cathodic and anodic simultaneous oxidation processes. A PAQ/GF electrode was synthesized by the electro-polymerization of 2-ethyl anthraquinone on graphite felt, which was characterized with cyclic voltametry measurements; the results indicated that the PAQ/GF electrode showed high reversibility for oxidation-reduction reaction of anthraquinone and catalytic activity for O2 reduction to H2O2; 13.5 mmol/L H2O2 was obtained after electrolysis for 6 h at -0.7 V (vs. SCE) and pH 6 with a current efficiency of 50% in a membrane reactor. Fe-Cu/Y350 catalysts, prepared by impregnation method, could catalyze the production of hydroxyl radicals (*OH) from H2O2, which was confirmed both by fading reaction of crystal violet and oxidation of *OH-probe compound (p-chlorobenzoic acid); Fe-Cu/Y350 also showed high catalytic-activity for the oxidation of organics by hypochlorous sodium, because COD removal of coking wastewater reached 26% in the catalytic process while only 11% of COD removal was obtained in the absence of Fe-Cu/Y350. COD removal of coking wastewater reached 49.4% (26.0% and 23.4% in cathodic system and anodic system, respectively) in the developed electrolytic-reactor, which was higher than that of conventional cathodic-anodic-oxidation process (29.8%). At optimal reaction condition of initial COD = 192 mg/L, I = 10A x m(-2) and pH 4-5, more than 50% COD were removed after electrolysis for 1 h. The mechanism might be as follows: in cathodic system, H2O2 is generated from reduction of O2 on PAQ/GF cathode, and catalyzed by Fe-Cu/Y350 for production of *OH, which causes mineralization and degradation of organic pollutants; in anodic system, Cl2 and HClO are generated from Cl- oxidation on IrO2-RuO2-TiO2/Ti anode and the organic pollutants are oxidized by Cl2, and HClO with Fe-Cu/Y350 catalysts or by direct anodic oxidation.

On-surface Fenton and Fenton-like reactions appraised by paper spray ionization mass spectrometry.

PubMed

Resende, S F; Oliveira, B S; Augusti, R

2018-06-21

On-surface degradation of sildenafil (an adequate substrate as it contains assorted functional groups in its structure) promoted by the Fenton (Fe 2+ / H 2 O 2 ) and Fenton-like (M n+ / H 2 O 2 ; M n+ = Fe 3+ , Co 2+ , Cu 2+ , Mn 2+ ) systems was investigated by using paper spray ionization mass spectrometry (PS-MS). The performance of each system was compared by measuring the ratio between the relative intensities of the ions of m/z 475 (protonated sildenafil) and m/z 235 (protonated lidocaine, used as a convenient internal standard and added to the paper just before the PS-MS analyzes). The results indicated the following order in the rates of such reactions: Fe 2+ /H 2 O 2 > H 2 O 2 > Cu 2+ /H 2 O 2 > M n+ / H 2 O 2 (M n+ = Fe 3+ , Co 2+ , Mn 2+ ) ~ M n+ (M n+ = Fe 2+ , Fe 3+ , Co 2+ , Cu 2+ , Mn 2 . The superior capability of Fe 2+ /H 2 O 2 in causing the degradation of sildenafil indicates that Fe 2+ efficiently decomposes H 2 O 2 to yield hydroxyl radicals, quite reactive species that cause the substrate oxidation. The results also indicate that H 2 O 2 can spontaneously decompose likely to yield hydroxyl radicals, although in a much smaller extension than the Fenton system. This effect, however, is strongly inhibited by the presence of the other cations, i. e. Fe 3+ , Co 2+ , Cu 2+ and Mn 2+ . A unique oxidation by-product was detected in the reaction between Fe 2+ /H 2 O 2 with sildenafil and a possible structure for it was proposed based on the MS/MS data. The on-surface reaction of other substrates (trimethoprim and tamoxifen) with the Fenton system was also investigated. In conclusion, PS-MS shown to be a convenient platform to promptly monitor on-surface oxidation reactions. This article is protected by copyright. All rights reserved.

TEM study on a new Zr-(Fe, Cu) phase in furnace-cooled Zr-1.0Sn-0.3Nb-0.3Fe-0.1Cu alloy

NASA Astrophysics Data System (ADS)

Liu, Yushun; Qiu, Risheng; Luan, Baifeng; Hao, Longlong; Tan, Xinu; Tao, Boran; Zhao, Yifan; Li, Feitao; Liu, Qing

2018-06-01

A new Zr-(Fe, Cu) phase was found in furnace-cooled Zr-1.0Sn-0.3Nb-0.3Fe- 0.1Cu alloy and alloys aged at 580 °C for 10min, 2 h and 10 h. Electron diffraction experiment shows the crystal structure of this phase to be body-centered tetragonal with unit cell dimensions determined to be a = b = 6.49 Å, c = 5.37 Å. Its possible space groups have been discussed and the reason accounting for its formation is believed to be the addition of Cu according to the atom-level images. In addition, no crystal structural or chemical composition changes were observed throughout the aging process.

Structure, bonding, and catalytic activity of monodisperse, transition-metal-substituted CeO2 nanoparticles.

PubMed

Elias, Joseph S; Risch, Marcel; Giordano, Livia; Mansour, Azzam N; Shao-Horn, Yang

2014-12-10

We present a simple and generalizable synthetic route toward phase-pure, monodisperse transition-metal-substituted ceria nanoparticles (M0.1Ce0.9O2-x, M = Mn, Fe, Co, Ni, Cu). The solution-based pyrolysis of a series of heterobimetallic Schiff base complexes ensures a rigorous control of the size, morphology and composition of 3 nm M0.1Ce0.9O2-x crystallites for CO oxidation catalysis and other applications. X-ray absorption spectroscopy confirms the dispersion of aliovalent (M(3+) and M(2+)) transition metal ions into the ceria matrix without the formation of any bulk transition metal oxide phases, while steady-state CO oxidation catalysis reveals an order of magnitude increase in catalytic activity with copper substitution. Density functional calculations of model slabs of these compounds confirm the stabilization of M(3+) and M(2+) in the lattice of CeO2. These results highlight the role of the host CeO2 lattice in stabilizing high oxidation states of aliovalent transition metal dopants that ordinarily would be intractable, such as Cu(3+), as well as demonstrating a rational approach to catalyst design. The current work demonstrates, for the first time, a generalizable approach for the preparation of transition-metal-substituted CeO2 for a broad range of transition metals with unparalleled synthetic control and illustrates that Cu(3+) is implicated in the mechanism for CO oxidation on CuO-CeO2 catalysts.

Performance of magnetic activated carbon composite as peroxymonosulfate activator and regenerable adsorbent via sulfate radical-mediated oxidation processes.

PubMed

Oh, Wen-Da; Lua, Shun-Kuang; Dong, Zhili; Lim, Teik-Thye

2015-03-02

Magnetic activated carbon composite (CuFe2O4/AC, MACC) was prepared by a co-precipitation-calcination method. The MACC consisted of porous micro-particle morphology with homogeneously distributed CuFe2O4 and possessed high magnetic saturation moment (8.1 emu g(-1)). The performance of MACC was evaluated as catalyst and regenerable adsorbent via peroxymonosulfate (PMS, Oxone(®)) activation for methylene blue (MB) removal. Optimum CuFe2O4/AC w/w ratio was 1:1.5 giving excellent performance and can be reused for at least 3 cycles. The presence of common inorganic ions, namely Cl(-) and NO3(-) did not exert significant influence on MB degradation but humic acid decreased the MB degradation rate. As a regenerable adsorbent, negligible difference in regeneration efficiency was observed when a higher Oxone(®) dosage was employed but a better efficiency was obtained at a lower MACC loading. The factors hindering complete MACC regeneration are MB adsorption irreversibility and AC surface modification by PMS making it less favorable for subsequent MB adsorption. With an additional mild heat treatment (150 °C) after regeneration, 82% of the active sites were successfully regenerated. A kinetic model incorporating simultaneous first-order desorption, second-order adsorption and pseudo-first order degradation processes was numerically-solved to describe the rate of regeneration. The regeneration rate increased linearly with increasing Oxone(®):MACC ratio. The MACC could potentially serve as a catalyst for PMS activation and regenerable adsorbent. Copyright © 2014 Elsevier B.V. All rights reserved.

Development of land use regression models for particle composition in twenty study areas in Europe.

PubMed

de Hoogh, Kees; Wang, Meng; Adam, Martin; Badaloni, Chiara; Beelen, Rob; Birk, Matthias; Cesaroni, Giulia; Cirach, Marta; Declercq, Christophe; Dėdelė, Audrius; Dons, Evi; de Nazelle, Audrey; Eeftens, Marloes; Eriksen, Kirsten; Eriksson, Charlotta; Fischer, Paul; Gražulevičienė, Regina; Gryparis, Alexandros; Hoffmann, Barbara; Jerrett, Michael; Katsouyanni, Klea; Iakovides, Minas; Lanki, Timo; Lindley, Sarah; Madsen, Christian; Mölter, Anna; Mosler, Gioia; Nádor, Gizella; Nieuwenhuijsen, Mark; Pershagen, Göran; Peters, Annette; Phuleria, Harisch; Probst-Hensch, Nicole; Raaschou-Nielsen, Ole; Quass, Ulrich; Ranzi, Andrea; Stephanou, Euripides; Sugiri, Dorothea; Schwarze, Per; Tsai, Ming-Yi; Yli-Tuomi, Tarja; Varró, Mihály J; Vienneau, Danielle; Weinmayr, Gudrun; Brunekreef, Bert; Hoek, Gerard

2013-06-04

Land Use Regression (LUR) models have been used to describe and model spatial variability of annual mean concentrations of traffic related pollutants such as nitrogen dioxide (NO2), nitrogen oxides (NOx) and particulate matter (PM). No models have yet been published of elemental composition. As part of the ESCAPE project, we measured the elemental composition in both the PM10 and PM2.5 fraction sizes at 20 sites in each of 20 study areas across Europe. LUR models for eight a priori selected elements (copper (Cu), iron (Fe), potassium (K), nickel (Ni), sulfur (S), silicon (Si), vanadium (V), and zinc (Zn)) were developed. Good models were developed for Cu, Fe, and Zn in both fractions (PM10 and PM2.5) explaining on average between 67 and 79% of the concentration variance (R(2)) with a large variability between areas. Traffic variables were the dominant predictors, reflecting nontailpipe emissions. Models for V and S in the PM10 and PM2.5 fractions and Si, Ni, and K in the PM10 fraction performed moderately with R(2) ranging from 50 to 61%. Si, NI, and K models for PM2.5 performed poorest with R(2) under 50%. The LUR models are used to estimate exposures to elemental composition in the health studies involved in ESCAPE.

Influences of annealing temperature on sprayed CuFeO2 thin films

NASA Astrophysics Data System (ADS)

Abdelwahab, H. M.; Ratep, A.; Abo Elsoud, A. M.; Boshta, M.; Osman, M. B. S.

2018-06-01

Delafossite CuFeO2 thin films were successfully prepared onto quartz substrates using simple spray pyrolysis technique. Post annealing under nitrogen atmosphere for 2 h was necessary to form delafossite CuFeO2 phase. The effect of alteration in annealing temperature (TA) 800, 850 and 900 °C was study on structural, morphology and optical properties. The XRD results for thin film annealed at TA = 850 °C show single phase CuFeO2 with rhombohedral crystal system and R 3 bar m space group with preferred orientation along (0 1 2). The prepared copper iron oxide thin films have an optical transmission ranged ∼40% in the visible region. The optical direct optical band gap of the prepared thin films was ranged ∼2.9 eV.

Novel Preparation of Nano-Composite CuO-Cr2O3 Using Ctab-Template Method and Efficient for Hydrogenation of Biomass-Derived Furfural

NASA Astrophysics Data System (ADS)

Yan, Kai; Wu, Xu; An, Xia; Xie, Xianmei

2013-02-01

A simple route to fabricate nano-composite oxides CuO-Cr2O3 using hexadecyltrimethylammonium bromide (CTAB)-templated Cu-Cr hydrotalcite as the precursor is presented. This novel method is based on CTAB-templating effect for mesostructure directing and using the cheap metal nitrate, followed by removal of CTAB. It was indicated that the nano-composite CuO-Cr2O3 was formed during the removal of CTAB. X-ray diffraction (XRD) and transitional electronic microscopy (TEM) revealed nice nano-composite oxides CuO-Cr2O3 were formed with high crystallinity. N2 adsorption and desorption indicated that a high surface area of 170.5 m2/g with a pore size of 2.7 nm of the nano-composite CuO-Cr2O3 was facilely resulted. The as-synthesized nano-composite oxides CuO-Cr2O3 display good catalytic activities for hydrogenation of furfural to furfuryl alcohol, whereas 86% selectivity was achieved at 75% conversion of furfural.

Self-assembled 3D heterometallic Cu(II)/Fe(II) coordination polymers with octahedral net skeletons: structural features, molecular magnetism, thermal and oxidation catalytic properties.

PubMed

Karabach, Yauhen Y; Guedes da Silva, M Fátima C; Kopylovich, Maximilian N; Gil-Hernández, Beatriz; Sanchiz, Joaquin; Kirillov, Alexander M; Pombeiro, Armando J L

2010-12-06

The new three-dimensional (3D) heterometallic Cu(II)/Fe(II) coordination polymers [Cu(6)(H(2)tea)(6)Fe(CN)(6)](n)(NO(3))(2n)·6nH(2)O (1) and [Cu(6)(Hmdea)(6)Fe(CN)(6)](n)(NO(3))(2n)·7nH(2)O (2) have been easily generated by aqueous-medium self-assembly reactions of copper(II) nitrate with triethanolamine or N-methyldiethanolamine (H(3)tea or H(2)mdea, respectively), in the presence of potassium ferricyanide and sodium hydroxide. They have been isolated as air-stable crystalline solids and fully characterized including by single-crystal X-ray diffraction analyses. The latter reveal the formation of 3D metal-organic frameworks that are constructed from the [Cu(2)(μ-H(2)tea)(2)](2+) or [Cu(2)(μ-Hmdea)(2)](2+) nodes and the octahedral [Fe(CN)(6)](4-) linkers, featuring regular (1) or distorted (2) octahedral net skeletons. Upon dehydration, both compounds show reversible escape and binding processes toward water or methanol molecules. Magnetic susceptibility measurements of 1 and 2 reveal strong antiferromagnetic [J = -199(1) cm(-1)] or strong ferromagnetic [J = +153(1) cm(-1)] couplings between the copper(II) ions through the μ-O-alkoxo atoms in 1 or 2, respectively. The differences in magnetic behavior are explained in terms of the dependence of the magnetic coupling constant on the Cu-O-Cu bridging angle. Compounds 1 and 2 also act as efficient catalyst precursors for the mild oxidation of cyclohexane by aqueous hydrogen peroxide to cyclohexanol and cyclohexanone (homogeneous catalytic system), leading to maximum total yields (based on cyclohexane) and turnover numbers (TONs) up to about 22% and 470, respectively.

A Hybrid Mineral Battery: Energy Storage and Dissolution Behavior of CuFeS2 in a Fixed Bed Flow Cell.

PubMed

Deen, Kashif Mairaj; Asselin, Edouard

2018-05-09

The development of a hybrid system capable of storing energy and the additional benefit of Cu extraction is discussed in this work. A fixed bed flow cell (FBFC) was used in which a composite negative electrode containing CuFeS 2 (80 wt %) and carbon black (20 wt %) in graphite felt was separated from a positive (graphite felt) electrode by a proton-exchange membrane. The anolyte (0.2 m H 2 SO 4 ) and catholyte (0.5 m Fe 2+ in 0.2 m H 2 SO 4 with or without 0.1 m Cu 2+ ) were circulated in the cell. The electrochemical activity of the Fe 2+ /Fe 3+ redox couple over graphite felt significantly improved after the addition of Cu 2+ in the catholyte. Ultimately, in the CuFeS 2 ∥Fe 2+ /Cu 2+ (CFeCu) FBFC system, the specific capacity increased continuously to 26.4 mAh g -1 in 500 galvanostatic charge-discharge (GCD) cycles, compared to the CuFeS 2 ∥Fe 2+ (CFe) system (13.9 mAh g -1 ). Interestingly, the specific discharge energy gradually increased to 3.6 Wh kg -1 in 500 GCD cycles for the CFeCu system compared to 3.29 Wh kg -1 for the CFe system in 150 cycles. In addition to energy storage, 10.75 % Cu was also extracted from the mineral, which is an important feature of the CFeCu system as it would allow Cu extraction and recovery through hydrometallurgical methods. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Charge dynamics of 57Fe probe atoms in La2Li0.5Cu0.5O4

NASA Astrophysics Data System (ADS)

Presniakov, I. A.; Sobolev, A. V.; Rusakov, V. S.; Moskvin, A. S.; Baranov, A. V.

2018-06-01

The objective of this study is to characterize the electronic state and local surrounding of 57Fe Mössbauer probe atoms within iron-doped layered perovskite La2Li0.5Cu0.5O4 containing transition metal in unusual formal oxidation states "+3". An approach based on the qualitative energy diagrams analysis and the calculations within the cluster configuration interaction method have been developed. It was shown that a large amount of charge is transferred via Cu-O bonds from the O: 2p bands to the Cu: 3d orbitals and the ground state is dominated by the d9L configuration ("Cu2+-O-" state). The dominant d9L ground state for the (CuO6) sublattice induces in the environment of the 57Fe probe cations a charge transfer Fe3+ + O-(L) → Fe4+ + O2-, which transforms "Fe3+" into "Fe4+" state. The experimental spectra in the entire temperature range 77-300 K were described with the use of the stochastic two-level model based on the assumption of dynamic equilibrium between two Fe3+↔Fe4+ valence states related to the iron atom in the [Fe(1)O4]4- center. The relaxation frequencies and activation energies of the corresponding charge fluctuations were estimated based on Mössbauer data. The results are discussed assuming a temperature-induced change in the electronic state of the [CuO4]5- clusters in the layered perovskite.

UV-Vis-Induced Degradation of Phenol over Magnetic Photocatalysts Modified with Pt, Pd, Cu and Au Nanoparticles

PubMed Central

Wysocka, Izabela; Trzciński, Konrad; Łapiński, Marcin; Nowaczyk, Grzegorz; Zielińska-Jurek, Anna

2018-01-01

The combination of TiO2 photocatalyst and magnetic oxide nanoparticles enhances the separation and recoverable properties of nanosized TiO2 photocatalyst. Metal-modified (Me = Pd, Au, Pt, Cu) TiO2/SiO2@Fe3O4 nanocomposites were prepared by an ultrasonic-assisted sol-gel method. All prepared samples were characterized by X-ray powder diffraction (XRD) analysis, Brunauer-Emmett-Teller (BET) method, X-ray photoelectron spectroscopy (XPS), scanning transmission electron microscopy (STEM), Mott-Schottky analysis and photoluminescence spectroscopy (PL). Phenol oxidation pathways of magnetic photocatalysts modified with Pt, Pd, Cu and Au nanoparticles proceeded by generation of reactive oxygen species, which oxidized phenol to benzoquinone, hydroquinone and catechol. Benzoquinone and maleic acid were products, which were determined in the hydroquinone oxidation pathway. The highest mineralization rate was observed for Pd-TiO2/SiO2@Fe3O4 and Cu-TiO2/SiO2@Fe3O4 photocatalysts, which produced the highest concentration of catechol during photocatalytic reaction. For Pt-TiO2/SiO2@Fe3O4 nanocomposite, a lack of catechol after 60 min of irradiation resulted in low mineralization rate (CO2 formation). It is proposed that the enhanced photocatalytic activity of palladium and copper-modified photocatalysts is related to an increase in the amount of adsorption sites and efficient charge carrier separation, whereas the keto-enol tautomeric equilibrium retards the rate of phenol photomineralization on Au-TiO2/SiO2@Fe3O4. The magnetization hysteresis loop indicated that the obtained hybrid photocatalyst showed magnetic properties and therefore could be easily separated after treatment process. PMID:29316667

Coating magnetic CuFe2O4 nanoparticles with OMS-2 for enhanced degradation of organic pollutants via peroxymonosulfate activation

NASA Astrophysics Data System (ADS)

Ye, Peng; Wu, Deming; Wang, Manye; Wei, Yi; Xu, Aihua; Li, Xiaoxia

2018-01-01

A heterogeneous magnetic CuFe2O4@OMS-2 catalyst was fabricated through a facile solvent-free process using Mn(CH3COO)2 and KMnO4 in the presence of CuFe2O4. It was found that the BET surface area of OMS-2 as well as the ratio of low-valent manganese species significantly increased in the hybrid catalyst, due to interactions between CuFe2O4 and the precursor of amorphous manganese oxide. Acid Orange 7 (AO7) and other organic pollutants could be completely degraded by the CuFe2O4@OMS-2 catalyst within 30 min in the presence of peroxymonosulfate (PMS), while CuFe2O4 and OMS-2 showed no significant activity for the reaction. The hybrid catalyst also exhibited excellent long-term stability and could be easily recovered with the assistance of an external magnetic field. A possible degradation mechanism for the synergistic effects of different valent metal species and reactive radicals was proposed, which involved the electron transfer from Mn(III) or Mn(II) species to PMS with the generation of sulfate and hydroxyl radicals, and from AO7 and Cu(I) in CuFe2O4 to Mn(IV) and Mn(III) to reduce these Mn species.

Dissolution behavior of Cu, Fe and Zn from gold sulfide concentrate during pre-oxidation using ozone in neutral media

NASA Astrophysics Data System (ADS)

Kurniawan, Mubarok, M. Zaki

2018-04-01

The aim of this work was to observe the dissolution behaviour of Cu, Fe and Zn from gold sulfide concentrate during preoxidation with ozone as the oxidant and distillation water as the media. The preoxidation experiments were carried out in five-necked reactor with variations of retention time, percent solid, particle size and oxygen dosage injected to ozone generator. The retention time was varied at 6 hours, 8 hours, 12 hours and 24 hours. The percent solid was varied at 10%, 20% and 30% while the particle size was varied at P80 -75 mesh dan P80 -20 mesh. The dosage of oxygen injection to ozone generator was varried at 1 liter per minute and 2 liter per minute. The ozone gas was produced by using ozone generator type OZ-03 and injected to the slurry by using Mazzei injector. The soluble Cu, Fe and Zn were measured by using Atomic Absorption Spectrophotometry (AAS). The concentrates were characterized by X-Ray Diffraction (XRD), mineragraphy, fire assay and Inductively Coupled Plasma (ICP). Fire assay, ICP and XRD were used to analyse the residues and froth. The solubilition of metals (Cu, Fe and Zn) was obtained through the formation of sulphate ion and H+ which decreased the pH, released a number of heat and then was continued by the formation of elemental sulphur (S°). The interaction of particles and gas yielded the formation of froth. The highest dissolution percentage of Cu, Fe and Zn was achieved through 24 hours oxidation at 20% (w/w), P80 -20 mesh and one liter per minute of oxygen injection dosage by 83.016%, 24.7303% and 91.6808%, respectively.

Facile method for the synthesis of a magnetic CNTs-C@Fe-chitosan composite and its application in tetracycline removal from aqueous solutions.

PubMed

Ma, Jie; Zhuang, Yuan; Yu, Fei

2015-06-28

A magnetic CNTs-C@Fe-chitosan composite (CNTs-C@Fe-CS) was prepared based on as-prepared carbon nanotubes (APCNTs). The metal nanoparticles in APCNTs could be utilized directly without any purification treatment, and the carbon shells provide an effective barrier against oxidation, acid dissolution, and movement of the MNPs, thus ensuring the long-term stability of CNTs-C@Fe-CS. The results showed that CNTs-C@Fe-CS contained more abundant oxygen and nitrogen containing functional groups after chitosan modification and the composite had good magnetization characteristics, even in acidic solutions. Then CNTs-C@Fe-CS was used as an adsorbent for the removal of tetracycline from aqueous solutions. Adsorption experiments indicated that CNTs-C@Fe-CS have a good adsorption capacity (qe) of tetracycline (104 mg g(-1)). The Freundlich isotherm model fitted the experimental data better than the Langmuir isotherm model. Kinetic regression results showed that the adsorption kinetics was more accurately represented by a pseudo second-order model. Intra-particle diffusion was involved in the adsorption, but it was not the only rate-controlling step. Cu(2+) and humic acid could promote the adsorption of tetracycline on CNTs-C@Fe-CS. The CNTs-C@Fe-CS adsorbents could be effectively and quickly separated by applying an external magnetic field and the adsorption capacity was still maintained at 99.3 mg g(-1) after being used 10 times. Therefore, CNTs-C@Fe-CS is a promising magnetic nanomaterial for preconcentration and separation of organic pollutants for environmental remediation.

Conditions and mechanisms for the formation of nano-sized Delafossite (CuFeO{sub 2}) at temperatures ≤90 °C in aqueous solution

DOE Office of Scientific and Technical Information (OSTI.GOV)

John, Melanie, E-mail: melanie.john@min.uni-muenchen.de; Heuss-Aßbichler, Soraya; Ullrich, Aladin

In this study, we present the mechanism of CuFeO{sub 2} formation in aqueous solution at low temperatures ≤90 °C, using sulfate salts as reactants. Furthermore, we demonstrate the influence of experimental conditions (alkalization, reaction and ageing temperature and time) on the synthesized nanoparticles. In all cases, GR–SO{sub 4}, a Fe(II–III) layered double hydroxysulphate (Fe{sup 2+}{sub 4}Fe{sup 3+}{sub 2}(OH){sub 12}·SO{sub 4}) and Cu{sub 2}O precipitate first. During further OH{sup −} supply GR–SO{sub 4} oxidizes and forms Fe{sub 10}O{sub 14}(OH){sub 2}, Cu{sub 2}O and CuFeO{sub 2} crystals. Due to the high pH further CuFeO{sub 2} crystals grow at the cost of themore » unstable intermediate products. The reaction rate increases with increasing ageing temperature, reaction pH and, in particular, NaOH concentrations in the solution. As a result, highly crystalline CuFeO{sub 2} (3R and 2H polytypes) nanoparticles showing hexagonal morphology can be synthesized at 70 °C within 10 h or at 50 °C within 1 week. The formation of 2H polytype is favored by additional OH{sup −} supply during the pH-stat time and rather low temperatures. - Highlights: • We solve the formation mechanism of pure CuFeO{sub 2} using sulfates as reactants. • CuFeO{sub 2} nanoparticles crystallize on cost of green rust, Fe{sub 10}O{sub 14}(OH){sub 2} and Cu{sub 2}O. • The reaction rate increases with increasing temperature and OH- concentration. • CuFeO{sub 2} nanoparticles form at 50 °C within one week and at 70 °C within 10 h. • 2H-polytype of CuFeO{sub 2} is favored by additional NaOH supply during pH-stat-time.« less

Fabrication of Fe3O4@CuO core-shell from MOF based materials and its antibacterial activity

NASA Astrophysics Data System (ADS)

Rajabi, S. K.; Sohrabnezhad, Sh.; Ghafourian, S.

2016-12-01

Magnetic Fe3O4@CuO nanocomposite with a core/shell structure was successfully synthesized via direct calcinations of magnetic Fe3O4@HKUST-1 in air atmosphere. The morphology, structure, magnetic and porous properties of the as-synthesized nano composites were characterized by using scanning electron microscope (SEM), transmission electron microscopy (TEM), powder X-ray diffraction (PXRD), and vibration sample magnetometer (VSM). The results showed that the nanocomposite material included a Fe3O4 core and a CuO shell. The Fe3O4@CuO core-shell can be separated easily from the medium by a small magnet. The antibacterial activity of Fe3O4-CuO core-shell was investigated against gram-positive and gram-negative bacteria. A new mechanism was proposed for inactivation of bacteria over the prepared sample. It was demonstrated that the core-shell exhibit recyclable antibacterial activity, acting as an ideal long-acting antibacterial agent.

Effects of surface crystallization and oxidation in nanocrystalline FeNbCuSiB(P) ribbons

NASA Astrophysics Data System (ADS)

Butvinová, B.; Butvin, P.; Brzózka, K.; Kuzminski, M.; Maťko, I.; Švec, P., Sr.; Chromčíková, M.

2017-02-01

Si-poor Fe74Nb3Cu1Si8B14-xPx, (x=0, 3) nanocrystalline ribbon-form alloys often form surfaces, which exert in-plane force on underlying ribbon interior when nanocrystallized in even modest presence of oxygen. Mostly unwanted hard-ribbon-axis magnetic anisotropy is standard result. Essential sources of the surface-caused stress have been sought and influence of P instead of B substitution on this effect was studied too. Preferred surface crystallization (PSC) was found to be the major reason. However P substitution suppresses PSC and promotes Fe-oxide formation, which eases the stress, softens the surfaces and provides different annealing evolution of surface properties.

Evolution of Primary Fe-Rich Compounds in Secondary Al-Si-Cu Alloys

NASA Astrophysics Data System (ADS)

Fabrizi, Alberto; Capuzzi, Stefano; Timelli, Giulio

Although iron is usually added in die cast Al-Si foundry alloys to prevent die soldering, primary Fe-rich particles are generally considered as "hardspot" inclusions which compromise the mechanical properties of the alloy, namely ductility and toughness. As there is no economical methods to remove the Fe excess in secondary Al-Si alloys at this time, the control of solidification process and chemical composition of the alloy is a common industrial practice to overcome the negative effects connected with the presence of Fe-rich particles. In this work, the size and morphology as well as the nucleation density of primary Fe-rich particles have been studied as function of cooling rate and alloy chemical composition for secondary Al-Si-Cu alloys. The solidification experiments were carried out using differential scanning calorimetry whereas morphology investigations were conducted using optical and scanning electron microscopy. Mcrosegregations and chemical composition of primary Fe-rich particles were examined by energy dispersive spectroscopy.

Structural, dielectric and ferroelectric studies of BZT doped Mg0.2Cu0.3Zn0.5Fe2O4 magnetoelectric composites

NASA Astrophysics Data System (ADS)

Khader, S. Abdul; Parveez, Asiya; Giridharan, N. V.; Sankarappa, T.

2018-05-01

The composites of ferrite-ferroelectric system (x) Mg0.2Cu0.3Zn0.5Fe2O4+ (1-x) Ba0.8Zr0.2TiO3 (x=15%, 30%, 45%) were synthesized by sintering mixtures of ferroelectric Ba0.8Zr0.2TiO3 (BZT) and ferrite component Mg0.2Cu0.3Zn0.5Fe2O4 (MCZF). The presences of two phases in magneto-electric composites were probed by X-ray diffraction (XRD) studies. The peaks observed in the XRD spectrum indicated spinel cubic structure for MCZF ferrite and tetragonal perovskite structure for BZT and, both spinel and pervoskite structures for synthesized composites. Surface morphology of the samples has been investigated using Field Emission Scanning Electron Microscope (FESEM). Frequency dependent dielectric properties of synthesized composites were measured from 100 Hz to 1 MHz at RT using HIOKI LCR HI-TESTER. The dielectric dispersion is observed at lower frequencies for the synthesized ME composites. The ferroelectric properties of synthesized composites were analyzed using a Precision ferroelectric tester. It is observed that the composites exhibited ferroelectric hysteresis with wide loops indicating lossy nature of composites.

Solubility of copper in a sulfur-free mafic melt

NASA Astrophysics Data System (ADS)

Ripley, Edward M.; Brophy, James G.

1995-12-01

The solubility of Cu in S-free mafic melts has been measured at a series of ƒ O2 values and temperatures of 1245 and 1300°C. At constant temperature Cu solubility increases from 0.04 wt% at log ƒ O2 = -11.9 to 1.10 wt% at log ƒ O 2 = -7.4 . Copper solubilities were in excess of 8 wt% in two runs controlled at very high ƒ O2 conditions of 10 -1.4 and 10 -22 Partitioning of Cu between metal and glass shows a strong ƒ O2 dependence, with D Cumet/gl ranging from 90 at log ƒ O2 = -7.4 to 2190 at log ƒ O2 = -11.9 . Slopes of Cu solubility and DCumet/gl vs. log ƒ O2 suggest that Cu dissolves predominantly in the +1 valence state. Copper solubility decreases with increasing temperature at constant ƒ O2, similar to experimental results for Ni, Co, and Mo (Dingwell et al., 1994; Holzheid et al., 1994). The data are consistent with Cu dissolution as an oxide (represented by CuO 0.5) and suggest that changes in ƒ O2 ( Fe2+/Fe3+ variations and Cu 1+ complexation with Fe 3+) may have large effects on the distribution of Cu between silicate and sulfide magmas. Results also suggest that the extraction of oxide-bonded Cu in mafic magmas by externally derived S may be an important mechanism in the generation of Cu-rich sulfide ores.

Synthesis of mesoporous triple-metal nanosorbent from layered double hydroxide as an efficient new sorbent for removal of dye from water and wastewater.

PubMed

Kostić, Miloš; Radović, Miljana; Velinov, Nena; Najdanović, Slobodan; Bojić, Danijela; Hurt, Andrew; Bojić, Aleksandar

2018-09-15

In this study, co-precipitation synthesis of the mesoporous triple-metal nanosorbent from Fe, Cu, Ni layered double hydroxide (FeCuNi-LDH), on the basis of the data obtained from the TG analysis was carried out. The FTIR spectroscopy and XRD results confirm the formation of CuO, NiO and Fe 2 O 3 nanoparticles, while the EDX analysis does not show significant variations on the surface in elemental composition. BET analysis shows that FeCuNi-280 (FeCuNi-LDH calcinated at 280 °C) with mesoporous structure, has larger surface area compared to FeCuNi-LDH and FeCuNi-550 (FeCuNi-LDH calcinated at 550 °C). The value of pH PZC of FeCuNi-280 is found to be 8.66. Obtained FeCuNi-280 material showed the ability for efficient removal of dye Reactive Blue 19 (RB19) from water, with a very high sorption capacity of 480.79 mg/g at optimal conditions: the sorbent dose of 0.6 g/dm 3 , stirring speed of 280 rpm and pH 2. The kinetics results of the sorption process were well fitted by pseudo-second order and Chrastil model, and the sorption isotherm was well described by Sips, Langmuir and Brouers-Sotolongo model. FeCuNi-280 was easily regenerated with aqueous solution of NaOH, and reutilization was successfully done in five sorption cycles. The present study show that easy-to-prepare, relatively inexpensive nanosorbent FeCuNi-280 is among the best sorbents for the removal of RB19 dye from water solution and wastewater from textile industry in wide range of pH. Copyright © 2018 Elsevier Inc. All rights reserved.

Silicon induced Fe deficiency affects Fe, Mn, Cu and Zn distribution in rice (Oryza sativa L.) growth in calcareous conditions.

PubMed

Carrasco-Gil, Sandra; Rodríguez-Menéndez, Sara; Fernández, Beatriz; Pereiro, Rosario; de la Fuente, Vicenta; Hernandez-Apaolaza, Lourdes

2018-04-01

A protective effect by silicon in the amelioration of iron chlorosis has recently been proved for Strategy 1 species, at acidic pH. However in calcareous conditions, the Si effect on Fe acquisition and distribution is still unknown. In this work, the effect of Si on Fe, Mn, Cu and Zn distribution was studied in rice (Strategy 2 species) under Fe sufficiency and deficiency. Plants (+Si or-Si) were grown initially with Fe, and then Fe was removed from the nutrient solution. The plants were then analysed using a combined approach including LA-ICP-MS images for each element of interest, the analysis of the Fe and Si concentration at different cell layers of root and leaf cross sections by SEM-EDX, and determining the apoplastic Fe, total micronutrient concentration and oxidative stress indexes. A different Si effect was observed depending on plant Fe status. Under Fe sufficiency, Si supply increased Fe root plaque formation, decreasing Fe concentration inside the root and increasing the oxidative stress in the plants. Therefore, Fe acquisition strategies were activated, and Fe translocation rate to the aerial parts was increased, even under an optimal Fe supply. Under Fe deficiency, +Si plants absorbed Fe from the plaque more rapidly than -Si plants, due to the previous activation of Fe deficiency strategies during the growing period (+Fe + Si). Higher Fe plaque formation due to Si supply during the growing period reduced Fe uptake and could activate Fe deficiency strategies in rice, making it more efficient against Fe chlorosis alterations. Silicon influenced Mn and Cu distribution in root. Copyright © 2018 Elsevier Masson SAS. All rights reserved.

Electrochemiluminescence quenching of luminol by CuS in situ grown on reduced graphene oxide for detection of N-terminal pro-brain natriuretic peptide.

PubMed

Li, Xiaojian; Lu, Peng; Wu, Bin; Wang, Yaoguang; Wang, Huan; Du, Bin; Pang, Xuehui; Wei, Qin

2018-07-30

A novel electrochemiluminescence (ECL) signal-off strategy based on CuS in situ grown on reduced graphene oxide (CuS-rGO) quenching luminol/H 2 O 2 system was firstly proposed. Luminol was grafted on the surface of Au@Fe 3 O 4 -Cu 3 (PO 4 ) 2 nanoflowers (Luminol-Au@Fe 3 O 4 -Cu 3 (PO 4 ) 2 ) which exhibited excellent catalytic effect towards the reduction of H 2 O 2 to enhance the ECL intensity of luminol. Cu 3 (PO 4 ) 2 nanoflowers showed large surface area which can immobilize more Fe 3 O 4 and Au nanoparticles. The quenching mechanism of CuS-rGO was due to ECL resonance energy transfer (RET). The spectral overlap between fluorescence spectrum of Luminol-Au@Fe 3 O 4 -Cu 3 (PO 4 ) 2 and UV-vis absorption spectrum of CuS-rGO revealed that resonance energy transfer was possible. Au nanoparticles were immobilized on the surface of CuS-rGO to capture secondary antibodies. After a sandwich-type immunoreaction, a remarkable decrease of ECL signal was observed. Under the optimal conditions, the immunosensor showed excellent performance for N-terminal pro-brain natriuretic peptide (NT-proBNP) detection with a wide detection range from 0.5 pg mL -1 to 20 ng mL -1 and a low detection limit of 0.12 pg mL -1 (S/N = 3). The prepared NT-proBNP immunosensor displayed high sensitivity, excellent stability and good specificity. Copyright © 2018 Elsevier B.V. All rights reserved.

Single-crystalline MFe(2)O(4) nanotubes/nanorings synthesized by thermal transformation process for biological applications.

PubMed

Fan, Hai-Ming; Yi, Jia-Bao; Yang, Yi; Kho, Kiang-Wei; Tan, Hui-Ru; Shen, Ze-Xiang; Ding, Jun; Sun, Xiao-Wei; Olivo, Malini Carolene; Feng, Yuan-Ping

2009-09-22

We report a general thermal transformation approach to synthesize single-crystalline magnetic transition metal oxides nanotubes/nanorings including magnetite Fe(3)O(4), maghematite gamma-Fe(2)O(3), and ferrites MFe(2)O(4) (M = Co, Mn, Ni, Cu) using hematite alpha-Fe(2)O(3) nanotubes/nanorings template. While the straightforward reduction or reduction-oxides process was employed to produce Fe(3)O(4) and gamma-Fe(2)O(3), the alpha-Fe(2)O(3)/M(OH)(2) core/shell nanostructure was used as precursor to prepare MFe(2)O(4) nanotubes via MFe(2)O(4-x) (0 < x < 1) intermediate. The transformed ferrites nanocrystals retain the hollow structure and single-crystalline nature of the original templates. However, the crystallographic orientation-relationships of cubic spinel ferrites and trigonal hematite show strong correlation with their morpologies. The hollow-structured MFe(2)O(4) nanocrystals with tunable size, shape, and composition have exhibited unique magnetic properties. Moreover, they have been demonstrated as a highly effective peroxidase mimic catalysts for laboratory immunoassays or as a universal nanocapsules hybridized with luminescent QDs for magnetic separation and optical probe of lung cancer cells, suggesting that these biocompatible magnetic nanotubes/nanorings have great potential in biomedicine and biomagnetic applications.

Copper-promoted methylene C-H oxidation to a ketone derivative by O2.

PubMed

Deville, Claire; McKee, Vickie; McKenzie, Christine J

2017-01-17

The methylene group of the ligand 1,2-di(pyridin-2-yl)-ethanone oxime (dpeo) is slowly oxygenated by the O 2 in air under ambient conditions when [Cu(dpeo) 2 ](ClO 4 ) 2 is dissolved in ethanol or acetonitrile. An initial transient ketone product, 2-(hydroxyimino)-1,2-di(pyridine-2-yl)ethanone, (hidpe) was characterized in the heteroleptic copper(ii) complex [Cu(bpca)(hidpe)](ClO 4 ). The co-ligand in this complex, N-(2'-pyridylcarbonyl)pyridine-2-carboximidate (bpca - ), is derived from a copper-promoted Beckmann rearrangement of hidpe. In the presence of bromide only [Cu(bpca)Br] is isolated. When significant water is present in reaction mixtures copper complexes of dpeo, hidpe and bpca - are not recovered and [Cu(pic) 2 H 2 O] is isolated. This occurs since two equivalents of picolinate are ultimately generated from one equivalent of oxidized and hydrolysed dpeo. The copper-dependent O 2 activation and consequent stoichiometric dpeo C-H oxidation is reminiscent of the previously observed catalysis of dpeo oxidation by Mn(ii) [C. Deville, S. K. Padamati, J. Sundberg, V. McKee, W. R. Browne, C. J. McKenzie, Angew. Chem., Int. Ed., 2016, 55, 545-549]. By contrast dpeo oxidation is not observed during complexation reactions with other late transition metal(ii) ions (M = Fe, Co, Ni, Zn) under aerobic conditions. In these cases bis and tris complexes of bidentate dpeo are isolated in good yields. It is interesting to note that dpeo is not oxidised by H 2 O 2 in the absence of Cu or Mn, suggesting that metal-based oxidants capable of C-H activation are produced from the dpeo-Cu/Mn systems and specifically O 2 . The metastable copper complexes [Cu(dpeo) 2 ](ClO 4 ) 2 and [Cu(bpca)(hidpe)](ClO 4 ), along with [NiX 2 (dpeo) 2 ] (X = Cl, Br), [Ni(dpeo) 3 ](ClO 4 ) 2 , [Co(dpeo) 3 ](ClO 4 ) 3 and the mixed valence complex [Fe III Fe(dpeo-H) 3 (dpeo) 3 ](PF 6 ) 4 , have been structurally characterized.

Production and Isomeric Distribution of Xanthylium Cation Pigments and Their Precursors in Wine-like Conditions: Impact of Cu(II), Fe(II), Fe(III), Mn(II), Zn(II), and Al(III).

PubMed

Guo, Anque; Kontoudakis, Nikolaos; Scollary, Geoffrey R; Clark, Andrew C

2017-03-22

This study establishes the influence of Cu(II), Fe(II), Fe(III), Zn(II), Al(III), and Mn(II) on the oxidative production of xanthylium cations from (+)-catechin and either tartaric acid or glyoxylic acid in model wine systems. The reaction was studied at 25 °C using UHPLC and LC-HRMS for the analysis of phenolic products and their isomeric distribution. In addition to the expected products, a colorless product, tentatively assigned as a lactone, was detected for the first time. The results show the importance of Fe ions and a synergistic influence of Mn(II) in degrading tartaric acid to glyoxylic acid, whereas the other metal ions had minimal activity in this mechanistic step. Fe(II) and Fe(III) were shown to mediate the (+)-catechin-glyoxylic acid addition reaction, a role previously attributed to only Cu(II). Importantly, the study demonstrates that C-8 addition products of (+)-catechin are promoted by Cu(II), whereas C-6 addition products are promoted by Fe ions.

Environmental application of millimeter-scale sponge iron (s-Fe(0)) particles (II): the effect of surface copper.

PubMed

Ju, Yongming; Liu, Xiaowen; Liu, Runlong; Li, Guohua; Wang, Xiaoyan; Yang, Yanyan; Wei, Dongyang; Fang, Jiande; Dionysiou, Dionysios D

2015-04-28

To enhance the catalytic reactivity of millimeter-scale particles of sponge iron (s-Fe(0)), Cu(2+) ions were deposited on the surface of s-Fe(0) using a simple direct reduction reaction, and the catalytic properties of the bimetallic system was tested for removal of rhodamine B (RhB) from an aqueous solution. The influence of Cu(0) loading, catalyst dosage, particle size, initial RhB concentration, and initial pH were investigated, and the recyclability of the catalyst was also assessed. The results demonstrate that the 3∼5 millimeter s-Fe(0) particles (s-Fe(0)(3∼5mm)) with 5wt% Cu loading gave the best results. The removal of RhB followed two-step, pseudo-first-order reaction kinetics. Cu(0)-s-Fe(0) showed excellent stability after five reuse cycles. Cu(0)-s-Fe(0) possesses great advantages compared to nanoscale zero-valent iron, iron power, and iron flakes as well as its bimetals. The surface Cu(0) apparently catalyzes the production of reactive hydrogen atoms for indirect reaction and generates Fe-Cu galvanic cells that enhance electron transfer for direct reaction. This bimetallic catalyst shows great potential for the pre-treatment of recalcitrant wastewaters. Additionally, some oxides containing iron element are selected to simulate the adsorption process. The results prove that the adsorption process of FeOOH, Fe2O3 and Fe3O4 played minor role for the removal of RhB. Copyright © 2015 Elsevier B.V. All rights reserved.

[Oxidation behavior and kinetics of representative VOCs emitted from petrochemical industry over CuCeOx composite oxides].

PubMed

Chen, Chang-Wei; Yu, Yan-Ke; Chen, Jin-Sheng; He, Chi

2013-12-01

CuCeOx composite catalysts were synthesized via coprecipitation (COP-CuCeO,) and incipient impregnation (IMP-CuCeOx) methods, respectively. The physicochemical properties of the samples were characterized by XRD, low-temperature N2 sorption, H2-TPR and O2-TPD. The influences of reactant composition and concentration, reaction space velocity, O2 content, H2O concentration, and catalyst type on the oxidation behaviors of benzene, toluene, and n-hexane emitted from petrochemical industry were systematically investigated. In addition, the related kinetic parameters were model fitted. Compared with IMP-CuCeOx, COP-CuCeOx had well-dispersed active phase, better low-temperature reducibility, and more active surface oxygen species. The increase of reactant concentration was unfavorable for toluene oxidation, while the opposite phenomenon could be observed in n-hexane oxidation. The inlet concentration of benzene was irrelevant to its conversion under high oxidation rate. The introduction of benzene obviously inhibited the oxidation of toluene and n-hexane, while the presence of toluene had a positive effect on beuzene conversion. The presence of n-hexane could promote the oxidation of toluene, while toluene had a negative influence on e-hexane oxidation. Both low space velocity and high oxygen concentration were beneficial for the oxidation process, and the variation of oxygen content had negligible effect on n-hexane and henzene oxidation. The presence of H2O noticeably inhibited the oxidation of toluene, while significantly accelerated the oxidation procedure of henzene and n-hexane. COP-CuCeOx had superior catalytic performance for toluene and benzene oxidation, while IMP-CuCeOx showed higher n-hexane oxidation activity under dry condition. The oxidation behaviors under different conditions could be well fitted and predicted by the pseudo first-order kinetic model.

Removal of Cd2+ and Cu2+ ions from aqueous solution by using Fe-Fe3O4/graphene oxide as a novel and efficient adsorbent

NASA Astrophysics Data System (ADS)

Le, Giang H.; Ha, Anh Q.; Nguyen, Quang K.; Nguyen, Kien T.; Dang, Phuong T.; Tran, Hoa T. K.; Vu, Loi D.; Nguyen, Tuyen V.; Lee, Gun D.; Vu, Tuan A.

2016-10-01

The nano Fe-Fe3O4/graphene oxide (GO) was successfully synthesized by the precipitation method and followed by chemical reduction using FeCl3 as iron sources and NaBH4 as reducing agent. The products were characterized by x-ray diffraction (XRD), Fourier transform infrared spectroscopy, transmission electron microscopy (TEM), BET, x-ray photoelectron spectroscopy (XPS) and VMS. From the obtained XRD and XPS results, it revealed the formation of both Fe and Fe3O4 nano particles on GO surface. TEM images showed that both Fe3O4/GO and Fe-Fe3O4/GO had small particle size of 10-20 nm and uniform size distribution. Fe3O4/GO and Fe-Fe3O4/GO were used as adsorbents for removal of Cd2+ and Cu2+ ions from aqueous solution. Maximum adsorption capacity (Q max) of Fe-Fe3O4/GO for Cu2+ and Cd2+ are 90.0 mg g-1 and 108.6 mg g-1, respectively. These values are much higher as compared to those of Fe3O4/GO as well as those reported in the literature. Additionally, this novel adsorbent can be reused by washing with diluted Hcl solution and easily recovered by applying the magnetic field. The Cd2+ adsorption isotherm fits better for the Langmuir model that of the Freundlich model and it obeys the pseudo-second order kinetic equation.

Magnetic, Electric and Optical Properties of Mg-Substituted Ni-Cu-Zn Ferrites

NASA Astrophysics Data System (ADS)

Kabbur, S. M.; Ghodake, U. R.; Kambale, Rahul C.; Sartale, S. D.; Chikhale, L. P.; Suryavanshi, S. S.

2017-10-01

The Ni0.25- x Mg x Cu0.30Zn0.45Fe2O4 ( x = 0.00 mol, 0.05 mol, 0.10 mol, 0.15 mol, 0.20 mol and 0.25 mol) magnetic oxide system was prepared by a sol-gel auto-combustion method using glycine as a fuel. X-ray diffraction study reveals the formation of pure spinel lattice symmetry along with the presence of a small fraction of unreacted Fe2O3 phase as a secondary phase due to incomplete combustion reaction between fuel and oxidizer. The lattice constant ( a) was found to decrease with the increase of Mg2+ content; the average crystallite size ( D) is observed in the range of 26.78-33.14 nm. At room temperature, all the samples show typical magnetic hysteresis loops with the decrease of magnetic moment ( n B) of Ni-Cu-Zn ferrites with the increase of Mg2+ content. The intrinsic vibrational absorption bands for the tetrahedral and octahedral sites of the spinel structure were confirmed by infrared (IR) spectroscopy. The optical parameters such as refractive index ( η), velocity of IR waves ( v) and jump rates ( J 1, J 2, J) were studied and found to be dependent on the variation of the lattice constant. The Curie temperature ( T c) of Ni-Cu-Zn mixed ferrite was found to decrease with Mg2+ addition. The composition x = 0.15 mol.% with a low dielectric loss tangent of 2% seems to have potential for multilayer chip inductor applications at a wide range of frequencies.

Evaluating the potential of three Fe- and Mn-(nano)oxides for the stabilization of Cd, Cu and Pb in contaminated soils.

PubMed

Michálková, Zuzana; Komárek, Michael; Šillerová, Hana; Della Puppa, Loïc; Joussein, Emmanuel; Bordas, François; Vaněk, Aleš; Vaněk, Ondřej; Ettler, Vojtěch

2014-12-15

The potential of three Fe- and Mn-(nano)oxides for stabilizing Cd, Cu and Pb in contaminated soils was investigated using batch and column experiments, adsorption tests and tests of soil microbial activity. A novel synthetic amorphous Mn oxide (AMO), which was recently proposed as a stabilizing amendment, proved to be the most efficient in decreasing the mobility of the studied metals compared to nano-maghemite and nano-magnetite. Its application resulted in significant decreases of exchangeable metal fractions (92%, 92% and 93% decreases of Cd, Cu and Pb concentrations, respectively). The adsorption capacity of the AMO was an order of magnitude higher than those recorded for the other amendments. It was also the most efficient treatment for reducing Cu concentrations in the soil solution. No negative effects on soil microorganisms were recorded. On the other hand, the AMO was able to dissolve soil organic matter to some extent. Copyright © 2014 Elsevier Ltd. All rights reserved.

Electrochemical properties and electrocatalytic activity of conducting polymer/copper nanoparticles supported on reduced graphene oxide composite

NASA Astrophysics Data System (ADS)

Ehsani, Ali; Jaleh, Babak; Nasrollahzadeh, Mahmoud

2014-07-01

Reduced graphene oxide (rGO) was used to support Cu nanoparticles. As electro-active electrodes for supercapacitors composites of reduced graphene oxide/Cu nanoparticles (rGO/CuNPs) and polytyramine (PT) with good uniformity are prepared by electropolymerization. Composite of rGO/CuNPs-PT was synthesized by cyclic voltammetry (CV) methods and electrochemical properties of film were investigated by using electrochemical techniques. The results show that, the rGO/CuNPs-PT/G has better capacitance performance. This is mainly because of the really large surface area and the better electronic and ionic conductivity of rGO/CuNPs-PT/G, which lead to greater double-layer capacitance and faradic pseudo capacitance. Modified graphite electrodes (rGO/CuNPs-PT/G) were examined for their redox process and electrocatalytic activities towards the oxidation of methanol in alkaline solutions. The methods of cyclic voltammetry (CV), chronoamperometry (CA) and electrochemical impedance spectroscopy (EIS) were employed. In comparison with a Cu-PT/G (Graphite), rGO/CuNPs-PT/G modified electrode shows a significantly higher response for methanol oxidation. A mechanism based on the electro-chemical generation of Cu(III) active sites and their subsequent consumptions by methanol have been discussed.

Auto-combustion synthesis, Mössbauer study and catalytic properties of copper-manganese ferrites

NASA Astrophysics Data System (ADS)

Velinov, N.; Petrova, T.; Tsoncheva, T.; Genova, I.; Koleva, K.; Kovacheva, D.; Mitov, I.

2016-12-01

Spinel ferrites with nominal composition Cu 0.5Mn 0.5Fe 2 O 4 and different distribution of the ions are obtained by auto-combustion method. Mössbauer spectroscopy, X-ray Diffraction, Thermogravimetry-Differential Scanning Calorimetry, Scanning Electron Microscopy and catalytic test in the reaction of methanol decomposition is used for characterization of synthesized materials. The spectral results evidence that the phase composition, microstructure of the synthesized materials and the cation distribution depend on the preparation conditions. Varying the pH of the initial solution microstructure, ferrite crystallite size, cation oxidation state and distribution of ions in the in the spinel structure could be controlled. The catalytic behaviour of ferrites in the reaction of methanol decomposition also depends on the pH of the initial solution. Reduction transformations of mixed ferrites accompanied with the formation of Hägg carbide χ-Fe 5 C 2 were observed by the influence of the reaction medium.

Structural, dielectric and magnetic studies of (x) Ni0.7Co0.1Cu0.2Fe2O4 + (1-x) BaTiO3 magnetoelectric composites

NASA Astrophysics Data System (ADS)

Khader, S. Abdul; Parveez, Asiya; Giridharan, N. V.; Sankarappa, T.

2016-05-01

The Magneto-electric composites (x) Ni0.7Co0.1Cu0.2Fe2O4 + (1-x) BaTiO3 (x=10%, 20% and 30%) were synthesized by sintering mixtures of highly ferroelectric BaTiO3 (BT) and highly magneto-strictive component Ni0.7Co0.1Cu0.2Fe2O4 (NCCF). The presences of constituent phases in magneto-electric composites were probed by X-ray diffraction (XRD) studies. The peaks observed in the XRD spectrum indicated spinel cubic structure for NCCF ferrite phase and tetragonal perovskite structure for BT and, both spinel and pervoskite structures for synthesized ME composites. Surface morphology of the samples has been investigated using Field Emission Scanning Electron Microscope (FESEM). Frequency and composition dependent dielectric properties of synthesized composites were measured from 100 Hz to 1 MHz at room temperature using Hioki LCR Hi-TESTER. The dielectric dispersion is observed at lower frequencies for the synthesized ME composites. The hysteresis behavior was studied to understand the magnetic ordering in the synthesized composites using a Vibrating Sample Magnetometer (VSM). It is observed that the values of saturation magnetization increases along with the ferrite content.

A novel detection approach based on chromophore-decolorizing with free radical and application to photometric determination of copper with acid chrome dark blue.

PubMed

Gao, Hong-Wen; Chen, Fang-Fang; Chen, Ling; Zeng, Teng; Pan, Lu-Ting; Li, Jian-Hua; Luo, Hua-Fei

2007-03-21

A novel detection approach named chromophore-decolorizing with free radicals is developed for determination of trace heavy metal. The hydroxyl radicals (HO) generated from Fe(III) and hydrogen peroxide will oxidize the free chromophore into almost colorless products. The copper-acid chrome dark blue (ACDB) complexation was investigated at pH 5.07. In the presence of Fe(III) and hydrogen peroxide, the excess ACDB was decolorized in the Cu-ACDB reaction solution, and the final solution contained only one color compound, the Cu-ACDB complex. After oxidation of free hydroxyl radicals, the complexation becomes sensitive and selective and it has been used for the quantitation of trace amounts of Cu(II) dissolved in natural water. Beer's law is obeyed in the range from 0 to 0.500 microg mL(-1) Cu(II) and the limit of detection is only 6 microg L(-1) Cu(II). Besides, the Cu-ACDB complex formed was characterized.

Reduction-oxidation Enabled Glass-ceramics to Stainless Steel Bonding Part I: screening of doping oxidants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dai, Steve Xunhu

Lithium silicate-based glass-ceramics with high coefficients of thermal expansion, designed to form matched hermetic seals in 304L stainless steel housing, show little evidence of interfacial chemical bonding, despite extensive inter-diffusion at the glass-ceramic-stainless steel (GC-SS) interface. A series of glass-ceramic compositions modified with a variety of oxidants, AgO, FeO, NiO, PbO, SnO, CuO, CoO, MoO 3 and WO 3, are examined for the feasibility of forming bonding oxides through reduction-oxidation (redox) at the GC-SS interface. The oxidants were selected according to their Gibbs free energy to allow for oxidation of Cr/Mn/Si from stainless steel, and yet to prevent a reductionmore » of P2O5 in the glass-ceramic where the P 2O 5 is to form Li 3PO 4 nuclei for growth of high expansion crystalline SiO 2 phases. Other than the CuO and CoO modified glass-ceramics, bonding from interfacial redox reactions were not achieved in the modified glass-ceramics, either because of poor wetting on the stainless steel or a reduction of the oxidants at the surface of glass-ceramic specimens rather than the GC-SS interface.« less

Comparison of the Isothermal Oxidation Behavior of As-Cast Cu-17 Percent Cr and Cu-17 Percent Cr-5 Percent Al. Part 2; Scale Microstructures

NASA Technical Reports Server (NTRS)

Raj, S. V.

2008-01-01

The isothermal oxidation kinetics of as-cast Cu-17%Cr and Cu-17%Cr-5%Al in air were studied between 773 and 1173 K under atmospheric pressure. Details of the oxidation kinetics of these alloys were discussed in Part I. This paper analyzes the microstructures of the scale and its composition in an attempt to elucidate the oxidation mechanisms in these alloys. The scales formed on Cu-17%Cr specimens oxidized between 773 and 973 K consisted of external CuO and subsurface Cu2O layers. The total thickness of these scales varied from about 10 m at 773 K to about 450 m at 973 K. In contrast, thin scales formed on Cu-17%Cr-5%Al alloys oxidized between 773 and 1173 K. The exact nature of these scales could not be determined by x-ray diffraction but energy dispersive spectroscopy analyses were used to construct a scale composition map. Phenomenological oxidation mechanisms are proposed for the two alloys.

Comparison of the Isothermal Oxidation Behavior of As-Cast Cu-17 Percent Cr and Cu-17 Percent Cr-5 Percent Al Part II: Scale Microstructures

NASA Technical Reports Server (NTRS)

Raj, Sai V.

2008-01-01

The isothermal oxidation kinetics of as-cast Cu-17%Cr and Cu-17%Cr-5%Al in air were studied between 773 and 1173 K under atmospheric pressure. Details of the oxidation kinetics of these alloys were discussed in Part I. This paper analyzes the microstructures of the scale and its composition in an attempt to elucidate the oxidation mechanisms in these alloys. The scales formed on Cu-17%Cr specimens oxidized between 773 and 973 K consisted of external CuO and subsurface Cu2O layers. The total thickness of these scales varied from about 10 m at 773 K to about 450 m at 973 K. In contrast, thin scales formed on Cu-17%Cr-5%Al alloys oxidized between 773 and 1173 K. The exact nature of these scales could not be determined by x-ray diffraction but energy dispersive spectroscopy analyses were used to construct a scale composition map. Phenomenological oxidation mechanisms are proposed for the two alloys.

COMPARATIVE ASSESSMENT OF THE COMPOSITION AND CHARGE STATE OF NITROGENASE FeMo-COFACTOR

PubMed Central

Harris, Travis V.; Szilagyi, Robert K.

2011-01-01

A significant limitation in our understanding of the molecular mechanism of biological nitrogen fixation is the uncertain composition of the FeMo-cofactor (FeMo-co) of nitrogenase. In this study we present a systematic, density functional theory-based evaluation of spin coupling schemes, iron oxidation states, ligand protonation states, and interstitial ligand composition using a wide range of experimental criteria. The employed functionals and basis sets were validated with molecular orbital information from X-ray absorption spectroscopic data of relevant iron-sulfur clusters. Independently from the employed level of theory, the electronic structure with the greatest number of antiferromagnetic interactions corresponds to the lowest energy state for a given charge and oxidation state distribution of the iron ions. The relative spin state energies of resting and oxidized FeMo-co already allowed the exclusion of certain iron oxidation state distributions and interstitial ligand compositions. Geometry optimized FeMo-co structures of several models further eliminated additional states and compositions, while reduction potentials indicated a strong preference for the most likely charge state of FeMo-co. Mössbauer and ENDOR parameter calculations were found to be remarkably dependent on the employed training set, density functional and basis set. Overall, we found that a more oxidized [MoIV-2FeII-5FeIII-9S2−-C4−] composition with a hydroxyl-protonated homocitrate ligand satisfies all of the available experimental criteria, and is thus favored over the currently preferred composition of [MoIV-4FeII-3FeIII-9S2−-N3−] from the literature. PMID:21545160

High-Performance Epoxy-Resin-Bonded Magnets Produced from the Sm2Fe17Nx Powders Coated by Copper and Zinc Metals

NASA Astrophysics Data System (ADS)

Noguchi, Kenji; Machida, Ken-ichi; Adachi, Gin-ya

2001-04-01

Fine powders of Sm2Fe17Nx coated with copper metal reduced from CuCl2 and/or zinc metal subsequently derived by photo-decomposition of diethylzinc [Zn(C2H5)2] were prepared, and their magnetic properties were characterized in addition to those of epoxy-resin-bonded magnets produced from the coated powders (Cu/Sm2Fe17Nx, Zn/Sm2Fe17Nx and Zn/Cu/Sm2Fe17Nx). The remanence (Br) and maximum energy product [(\\mathit{BH})max] of double metal-coated Zn/Cu/Sm2Fe17Nx powders were maintained at higher levels than those of single Zn metal-coated Sm2Fe17Nx ones (Zn/Sm2Fe17Nx) even after heat treatment at 673 K since the oxidation resistance and thermal stability were effectively improved by formation of the thick and uniform protection layer on the surface of Sm2Fe17Nx particles. Moreover, the epoxy-resin-bonded magnets produced from the Zn/Cu/Sm2Fe17Nx powders possessed good corrosion resistance in air at 393 K which it resulted in the smaller thermal irreversible flux loss than that of uncoated and single Zn metal-coated Sm2Fe17Nx powders in the temperature range of above 393 K.

Ferrous ion as a reducing agent in the generation of antibiofilm nitric oxide from a copper-based catalytic system.

PubMed

Wonoputri, Vita; Gunawan, Cindy; Liu, Sanly; Barraud, Nicolas; Yee, Lachlan H; Lim, May; Amal, Rose

2018-05-01

The work found that the electron-donating properties of ferrous ions (Fe 2+ ) can be used for the conversion of nitrite (NO 2 - ) into the biofilm-dispersing signal nitric oxide (NO) by a copper(II) complex (CuDTTCT) catalyst, a potentially applicable biofilm control technology for the water industries. The availability of Fe 2+ varied depending on the characteristics of the aqueous systems (phosphate- and carbonate-containing nitrifying bacteria growth medium, NBGM and phosphate buffered saline, PBS at pH 6 to 8, to simulate conditions typically present in the water industries) and was found to affect the production of NO from nitrite by CuDTTCT (casted into PVC). Greater amounts of NO were generated from the CuDTTCT-nitrite-Fe 2+ systems in PBS compared to those in NBGM, which was associated with the reduced extent of Fe 2+ -to-Fe 3+ autoxidation by the iron-precipitating moieties phosphates and carbonate in the former system. Further, acidic conditions at pH 6.0 were found to favor NO production from the catalytic system in both PBS and NBGM compared to neutral or basic pH (pH 7.0 or 8.0). Lower pH was shown to stabilize Fe 2+ and reduce its autoxidation to Fe 3+ . These findings will be beneficial for the potential implementation of the NO-generating catalytic technology and indeed, a 'non-killing' biofilm dispersal activity of CuDTTCT-nitrite-Fe 2+ was observed on nitrifying bacteria biofilms in PBS at pH 6. Copyright © 2018 Elsevier Inc. All rights reserved.

Controlled Synthesis and Utilization of Metal and Oxide Hybrid Nanoparticles

NASA Astrophysics Data System (ADS)

Crane, Cameron

This dissertation reports the development of synthetic methods concerning rationally-designed, hybrid, and multifunctional nanomaterials. These methods are based on a wet chemical, solution phase approach that utilizes the knowledge of synthetic organic and inorganic chemistry to generate building blocks in solution for the growth of nanocrystals and hybrid nanostructures. This work builds on the prior knowledge of shape-controlled synthesis of noble metal nanocrystals and expands into the challenging realm of the more reactive first row transition metals. Specifically, a microemulsion sol-gel method was developed to synthesize Au-SiO2 dimers as precursors for the synthesis of segmented heterostructures of noble metals that can be used for catalysis. This microemulsion sol-gel method was modified to synthesize an aqueous suspension of oxidation-resistant Cu-SiO2 core-shell nanoparticles that can be used for sensing and catalysis. A thermal decomposition approach was developed, wherein zero-valence metal precursor complexes in the presence of seed nanoparticles produced metal-metal oxide core-shell structures with well-controlled shell thickness. This method was demonstrated on AuCu 3-Fe3O4, AuCu3-NiO, and AuCu3 -MnO core-shell systems. Switching the core from AuCu3 alloy to pure Cu, this method could extend to Cu-Fe3O4 and Cu-MnO systems. Further etching the Cu core in these core-shell structures led to the formation of the hollow metal oxides which provides a versatile route to hollow nanostructures of metal oxides. This work develops the synthetic library of tools for the production of hybrid nanostructures with multiple functionalities.

The formation of unsaturated zones within cemented paste backfill mixtures-effects on the release of copper, nickel, and zinc.

PubMed

Hamberg, Roger; Maurice, Christian; Alakangas, Lena

2018-05-13

Flooding of cemented paste backfill (CPB) filled mine workings is, commonly, a slow process and could lead to the formation of unsaturated zones within the CPB fillings. This facilitates the oxidation of sulfide minerals and thereby increases the risk of trace metal leaching. Pyrrhotitic tailings from a gold mine (cyanidation tailing (CT)), containing elevated concentrations of nickel (Ni), copper (Cu), and zinc (Zn), were mixed with cement and/or fly ash (1-3 wt%) to form CT-CPB mixtures. Pyrrhotite oxidation progressed more extensively during unsaturated conditions, where acidity resulted in dissolution of the Ni, Cu, and Zn associated with amorphous Fe precipitates and/or cementitious phases. The establishment of acidic, unsaturated conditions in CT-CBP:s with low fractions (1 wt%) of binders increased the Cu release (to be higher than that from CT), owing to the dissolution of Cu-associated amorphous Fe precipitates. In CT-CPB:s with relatively high proportions of binder, acidity from pyrrhotite oxidation was buffered to a greater extent. At this stage, Zn leaching increased due the occurrence of fly ash-specific Zn species soluble in alkaline conditions. Irrespective of binder proportion and water saturation level, the Ni and Zn release were lower, compared to that in CT. Fractions of Ni, Zn, and Cu associated with acid-soluble phases or amorphous Fe precipitates, susceptible to remobilization under acidic conditions, increased in tandem with binder fractions. Pyrrhotite oxidation occurred irrespective of the water saturation level in the CPB mixtures. That, in turn, poses an environmental risk, whereas a substantial proportion of Ni, Cu, and Zn was associated with acid-soluble phases.

Positron Annihilation Spectroscopy Characterization of Nanostructural Features in Reactor Steels

NASA Astrophysics Data System (ADS)

Glade, Stephen; Wirth, Brian; Asoka-Kumar, Palakkal; Sterne, Philip; Alinger, Matthew; Odette, George

2004-03-01

Irradiation embrittlement in nuclear reactor pressure vessel steels results from the formation of a high number density of nanometer sized copper rich precipitates and sub-nanometer defect-solute clusters. We present results of study to characterize the size and compositions of simple binary and ternary Fe-Cu-Mn model alloys and more representative Fe-Cu-Mn-Ni-Si-Mo-C reactor pressure vessel steels using positron annihilation spectroscopy (PAS). Using a recently developed spin-polarized PAS technique, we have also measured the magnetic properties of the nanometer-sized copper rich precipitates. Mn retards the precipitation kinetics and inhibits large vacancy cluster formation, suggesting a strong Mn-vacancy interaction which reduces radiation enhanced diffusion. The spin-polarized PAS measurements reveal the non-magnetic nature of the copper precipitates, discounting the notion that the precipitates contain significant quantities of Fe and providing an upper limit of at most a few percent Fe in the precipitates. PAS results on oxide dispersion-strengthened steel for use in fusion reactors will also be presented. Part of this work was performed under the auspices of the US Department of Energy by the University of California, Lawrence Livermore National Laboratory, under contract No. W-7405-ENG-48 with partial support provided from Basic Energy Sciences, Division of Materials Science.

Corrosion behavior in high-temperature pressurized water of Zircaloy-4 joints brazed with Zr-Cu-based amorphous filler alloys

NASA Astrophysics Data System (ADS)

Lee, Jung Gu; Lee, Gyoung-Ja; Park, Jin-Ju; Lee, Min-Ku

2017-05-01

The compositional effects of ternary Zr-Cu-X (X: Al, Fe) amorphous filler alloys on galvanic corrosion susceptibility in high-temperature pressurized water were investigated for Zircaloy-4 brazed joints. Through an Al-induced microgalvanic reaction that deteriorated the overall nobility of the joint, application of the Zr-Cu-Al filler alloy caused galvanic coupling to develop readily between the Al-bearing joint and the Al-free base metal, finally leading to massive localized corrosion of the joint. Contrastingly, joints prepared with a Zr-Cu-Fe filler alloy showed excellent corrosion resistance comparable to that of the Zircaloy-4 base metal, since the Cu and Fe elements forming fine intermetallic particles with Zr did not influence the electrochemical stability of the resultant joints. The present results demonstrate that Fe is a more suitable alloying element than Al for brazing filler alloys subjected to high-temperature corrosive environments.

Structural, dielectric and magnetic studies of (x) Mg0.2Cu0.3Zn0.5Fe2O4 + (1-x) Ba0.8Zr0.2TiO3 magnetoelectric composites

NASA Astrophysics Data System (ADS)

Khader, S. Abdul; Giridharan, N. V.; Chaudhuri, Arka; Sankarappa, T.

2016-05-01

The Magneto-electric composites (x) Mg0.2Cu0.3Zn0.5Fe2O4 + (1-x) Ba0.8Zr0.2TiO3 (x=15%,30%,45%) were synthesized by sintering mixtures of highly ferroelectric Ba0.8Zr0.2TiO3 (BZT) and highly magneto-strictive component Mg0.2Cu0.3Zn0.5Fe2O4 (MCZF). The presences of two phases in magneto-electric composites were probed by X-ray diffraction (XRD) studies. The peaks observed in the XRD spectrum indicated spinel cubic structure for MCZF ferrite and tetragonal perovskite structure for BZT and, both spinel and pervoskite structures for synthesized composites. Surface morphology of the samples has been investigated using Field Emission Scanning Electron Microscope (FESEM). Frequency dependent dielectric properties of synthesized composites were measured from 100 Hz to 1 MHz at RT using HIOKI LCR HI-TESTER. The dielectric dispersion is observed at lower frequencies for the synthesized ME composites. The magnetic properties of synthesized composites were analyzed using a Vibrating Sample Magnetometer (VSM). It is observed that the values of saturation magnetization increases along with the ferrite content.

THE WEATHERING OF A SULFIDE OREBODY: SPECIATION AND FATE OF SOME POTENTIAL CONTAMINANTS

DOE Office of Scientific and Technical Information (OSTI.GOV)

Courtin-Nomade, Alexandra; Grosbois, Cecile; Marcus, Matthew A.

2010-07-16

Various potentially toxic trace elements such as As, Cu, Pb and Zn have been remobilized by the weathering of a sulfide orebody that was only partially mined at Leona Heights, California. As a result, this body has both natural and anthropogenically modified weathering profiles only 500 m apart. The orebody is located in a heavily urbanized area in suburban Oakland, and directly affects water quality in at least one stream by producing acidic conditions and relatively high concentrations of dissolved elements (e.g., {approx}500 mg/L Cu, {approx}3700 mg/L Zn). Micrometric-scale mineralogical investigations were performed on the authigenic metal-bearing phases (less thanmore » 10 {mu}m in size) using electron-probe micro-analysis (EPMA), micro-Raman, micro X-ray absorption spectroscopy (mXAS), scanning X-ray diffraction (mSXRD) and scanning X-ray fluorescence (mSXRF) mapping techniques. Those measurements were coupled with classical mineralogical laboratory techniques, X-ray diffraction (XRD) and scanning electron microscopy (SEM). Authigenic metal-bearing phases identified are mainly sulfates (jarosite, epsomite, schwertmannite), Fe (oxy-)hydroxides (goethite, hematite and poorly crystalline Fe products) and poorly crystalline Mn (hydr-)oxides. Sulfates and Fe (oxy-)hydroxides are the two main secondary products at both sites, whereas Mn (hydr-) oxides were only observed in the samples from the non-mining site. In these samples, the various trace elements show different affinities for Fe or Mn compounds. Lead is preferentially associated with Mn (hydr-)oxides and As with Fe (oxy-)hydroxides or sulfates. Copper association with Mn and Fe phases is questionable, and the results obtained rather indicate that Cu is present as individual Cu-rich grains (Cu hydroxides). Some ochreous precipitates were found at both sites and correspond to a mixture of schwertmannite, goethite and jarosite containing some potentially toxic trace elements such as Cu, Pb and Zn. According to the trace element distribution and relative abundance of the unweathered sulfides, this orebody still represents a significant reservoir of potential contaminants for the watershed, especially in the non-mining site, as a much greater proportion of sulfides is left to react and because of the lower porosity in this site.« less

The weathering of a sulfide orebody: Speciation and fate of some potential contaminants

USGS Publications Warehouse

Courtin-Nomade, A.; Grosbois, C.; Marcus, M.A.; Fakra, S.C.; Beny, J.-M.; Foster, A.L.

2009-01-01

Various potentially toxic trace elements such as As, Cu, Pb and Zn have been remobilized by the weathering of a sulfide orebody that was only partially mined at Leona Heights, California. As a result, this body has both natural and anthropogeni- cally modified weathering profiles only 500 m apart. The orebody is located in a heavily urbanized area in suburban Oakland, and directly affects water quality in at least one stream by producing acidic conditions and relatively high concentrations of dissolved elements (e.g., ??500 ??g/L Cu, ??3700 ??g/L Zn). Micrometric-scale mineralogical investigations were performed on the authigenic metal-bearing phases (less than 10 ??m in size) using electron-probe micro-analysis (EPMA), micro-Raman, micro X-ray absorption spectroscopy (??XAS), scanning X-ray diffraction ((??SXRD) and scanning X-ray fluorescence (??-SXRF) mapping techniques. Those measurements were coupled with classical mineralogical laboratory techniques, X-ray diffraction (XRD) and scanning electron microscopy (SEM). Authigenic metal-bearing phases identified are mainly sulfates (jarosite, epsomite, schwertmannite), Fe (oxy-)hydroxides (goethite, hematite and poorly crystalline Fe products) and poorly crystalline Mn (hydr-)oxides. Sulfates and Fe (oxy-)hydroxides are the two main secondary products at both sites, whereas Mn (hydr-) oxides were only observed in the samples from the non-mining site. In these samples, the various trace elements show different affinities for Fe or Mn compounds. Lead is preferentially associated with Mn (hydr-)oxides and As with Fe (oxy-)hydroxides or sulfates. Copper association with Mn and Fe phases is questionable, and the results obtained rather indicate that Cu is present as individual Cu-rich grains (Cu hydroxides). Some ochreous precipitates were found at both sites and correspond to a mixture of schwertmannite, goethite and jarosite containing some potentially toxic trace elements such as Cu, Pb and Zn. According to the trace element distribution and relative abundance of the unweathered sulfides, this orebody still represents a significant reservoir of potential contaminants for the watershed, especially at the non-mining site, as a much greater proportion of sulfides is left to react and because of the lower porosity at this site.

Magnetoresistance enhancement in specular, bottom-pinned, Mn83Ir17 spin valves with nano-oxide layers

NASA Astrophysics Data System (ADS)

Veloso, A.; Freitas, P. P.; Wei, P.; Barradas, N. P.; Soares, J. C.; Almeida, B.; Sousa, J. B.

2000-08-01

Bottom-pinned Mn83Ir17 spin valves with enhanced specular scattering were fabricated, showing magnetoresistance (MR) values up to 13.6%, lower sheet resistance R□ and higher ΔR□. Two nano-oxide layers (NOL) are grown on both sides of the CoFe/Cu/CoFe spin valve structure by natural oxidation or remote plasma oxidation of the starting CoFe layer. Maximum MR enhancement is obtained after just 1 min plasma oxidation. Rutherford backscattering analysis shows that a 15±2 Å oxide layer grows at the expense of the initial (prior to oxidation) CoFe layer, with ˜12% reduction of the initial 40 Å CoFe thickness. X-ray reflectometry indicates that Kiessig fringes become better defined after NOL growth, indicating smoother inner interfaces, in agreement with the observed decrease of the spin valve ferromagnetic Néel coupling.

Partitioning of copper between olivine, orthopyroxene, clinopyroxene, spinel, garnet and silicate melts at upper mantle conditions

NASA Astrophysics Data System (ADS)

Liu, Xingcheng; Xiong, Xiaolin; Audétat, Andreas; Li, Yuan; Song, Maoshuang; Li, Li; Sun, Weidong; Ding, Xing

2014-01-01

Previously published Cu partition coefficients (DCu) between silicate minerals and melts cover a wide range and have resulted in large uncertainties in model calculations of Cu behavior during mantle melting. In order to obtain true DCumineral/melt values, this study used Pt95Cu05 alloy capsules as the source of Cu to experimentally determine the DCu between olivine (ol), orthopyroxene (opx), clinopyroxene (cpx), spinel (spl), garnet (grt) and hydrous silicate melts at upper mantle conditions. Three synthetic silicate compositions, a Komatiite, a MORB and a Di70An30, were used to produce these minerals and melts. The experiments were conducted in piston cylinder presses at 1.0-3.5 GPa, 1150-1300 °C and oxygen fugacities (fO2) of from ∼2 log units below to ∼5 log units above fayalite-magnetite-quartz (FMQ). The compositions of minerals and quenched melts in the run products were measured with EMP and LA-ICP-MS. Attainment of equilibrium is verified by reproducible DCu values obtained at similar experimental conditions but different durations. The results show that DCu for ol/, opx/, spl/ and possibly cpx/melt increase with increasing fO2 when fO2 > FMQ + 1.2, while DCu for cpx/ and spl/melt also increase with increasing Na2O in cpx and Fe2O3 in spinel, respectively. In the investigated P-T-fO2 conditions, the DCumineral/melt values are 0.04-0.14 for ol, 0.04-0.09 for opx, 0.02-0.23 for cpx, 0.19-0.77 for spl and 0.03-0.05 for grt. These results confirm that Cu is highly incompatible (DCu < ∼0.2) in all the silicate minerals and oxides of the upper mantle with the exception of the high-Fe spinel, in which Cu is moderately incompatible (DCu = 0.4-0.8) and thus Cu will be enriched in the derived melts during mantle partial melting and magmatic differentiation if sulfide is absent. These experimental DCu values are used to assess the controls on Cu behavior during mantle melting. The model results suggest that MORBs and most arc basalts must form by sulfide-present melting at relatively reduced conditions, while high Cu (>70 ppm) arc basalts may form at oxidized, sulfide-absent conditions, which is consistent with the possibility of some high fO2 regions present in the arc mantle.

La0.8Sr0.2Fe0.8Cu0.2O3-δ as “cobalt-free” cathode for La0.8Sr0.2Ga0.8Mg0.2O3-δ electrolyte

NASA Astrophysics Data System (ADS)

Zurlo, Francesca; Di Bartolomeo, Elisabetta; D'Epifanio, Alessandra; Felice, Valeria; Natali Sora, Isabella; Tortora, Luca; Licoccia, Silvia

2014-12-01

A "cobalt-free" cathode material with stoichiometric composition La0.8Sr0.2Fe0.8Cu0.2O3-δ (LSFCu) was specifically developed for use with La0.8Sr0.2Ga0.8Mg0.2O3-δ (LSGM) electrolyte in intermediate temperature solid oxide fuel cell (IT-SOFC) systems. The chemical stability of LSFCu in contact with LSGM electrolyte was investigated by structural and morphological analysis. The electrochemical properties of LSFCu dense pellets were investigated in the temperature range 600-750 °C by electrochemical impedance spectroscopy (EIS). LSFCu|LSGM|LSFCu symmetrical cells were prepared and area specific resistance (ASR) values, directly depending on the rate limiting step of the oxygen reduction reaction, were evaluated. Fuel cells were prepared using LSFCu as cathode material on a LSGM pellet and electrochemical tests were performed in the 700-800 °C temperature range and compared to similar fuel cells prepared by using commercial La0.6Sr0.4Fe0.8Co0.2O3-δ (LSFCo) as a cathode. The maximum current density and power density recorded for LSFCu and LSFCo were similar. This fact demonstrates that Cu can be used as Co substitute in perovskite cathode materials.

Phase equilibria in the nominally Al65Cu23Fe12 system at 3, 5 and 21 GPa: Implications for the quasicrystal-bearing Khatyrka meteorite

NASA Astrophysics Data System (ADS)

Stagno, Vincenzo; Bindi, Luca; Steinhardt, Paul J.; Fei, Yingwei

2017-10-01

Two of the three natural quasiperiodic crystals found in the Khatyrka meteorite show a composition within the Al-Cu-Fe system. Icosahedrite, with formula Al63Cu24Fe13, coexists with the new Al62Cu31Fe7 quasicrystal plus additional Al-metallic minerals such as stolperite (AlCu), kryachkoite [(Al,Cu)6(Fe,Cu)], hollisterite (AlFe3), khatyrkite (Al2Cu) and cupalite (AlCu), associated to high-pressure phases like ringwoodite/ahrensite, coesite, and stishovite. These high-pressure minerals represent the evidence that most of the Khatyrka meteoritic fragments formed at least at 5 GPa and 1200 °C, if not at more extreme conditions. On the other hand, experimental studies on phase equilibria within the representative Al-Cu-Fe system appear mostly limited to ambient pressure conditions, yet. This makes the interpretation of the coexisting mineral phases in the meteoritic sample quite difficult. We performed experiments at 3, 5 and 21 GPa and temperatures of 800-1500 °C using the multi-anvil apparatus to investigate the phase equilibria in the Al65Cu23Fe12 system representative of the first natural quasicrystal, icosahedrite. Our results, supported by single-crystal X-ray diffraction and analyses by scanning electron microscopy, confirm the stability of icosahedrite at high pressure and temperature along with additional coexisting Al-bearing phases representative of khatyrkite and stolperite as those found in the natural meteorite. One reversal experiment performed at 5 GPa and 1200 °C shows the formation of the icosahedral quasicrystal from a pure Al, Cu and Fe mixture, a first experimental synthesis of icosahedrite under those conditions. Pressure appears to not play a major role in the distribution of Al, Cu and Fe between the coexisting phases, icosahedrite in particular. Results from this study extend our knowledge on the stability of icosahedral AlCuFe at higher temperature and pressure than previously examined, and provide a new constraint on the stability of icosahedrite.

Copper isotope fractionation during its interaction with soil and aquatic microorganisms and metal oxy(hydr)oxides: Possible structural control

NASA Astrophysics Data System (ADS)

Pokrovsky, O. S.; Viers, J.; Emnova, E. E.; Kompantseva, E. I.; Freydier, R.

2008-04-01

This work is aimed at quantifying the main environmental factors controlling isotope fractionation of Cu during its adsorption from aqueous solutions onto common organic (bacteria, algae) and inorganic (oxy(hydr)oxide) surfaces. Adsorption of Cu on aerobic rhizospheric ( Pseudomonas aureofaciens CNMN PsB-03) and phototrophic aquatic ( Rhodobacter sp. f-7bl, Gloeocapsa sp. f-6gl) bacteria, uptake of Cu by marine ( Skeletonema costatum) and freshwater ( Navicula minima, Achnanthidium minutissimum and Melosira varians) diatoms, and Cu adsorption onto goethite (FeOOH) and gibbsite (AlOOH) were studied using a batch reaction as a function of pH, copper concentration in solution and time of exposure. Stable isotopes of copper in selected filtrates were measured using Neptune multicollector ICP-MS. Irreversible incorporation of Cu in cultured diatom cells at pH 7.5-8.0 did not produce any isotopic shift between the cell and solution (Δ 65/63Cu(solid-solution)) within ±0.2‰. Accordingly, no systematic variation was observed during Cu adsorption on anoxygenic phototrophic bacteria ( Rhodobacter sp.), cyanobacteria ( Gloeocapsa sp.) or soil aerobic exopolysaccharide (EPS)-producing bacteria ( P. aureofaciens) in circumneutral pH (4-6.5) and various exposure times (3 min to 48 h): Δ 65Cu(solid-solution) = 0.0 ± 0.4‰. In contrast, when Cu was adsorbed at pH 1.8-3.5 on the cell surface of soil the bacterium P. aureofacienshaving abundant or poor EPS depending on medium composition, yielded a significant enrichment of the cell surface in the light isotope (Δ 65Cu (solid-solution) = -1.2 ± 0.5‰). Inorganic reactions of Cu adsorption at pH 4-6 produced the opposite isotopic offset: enrichment of the oxy(hydr)oxide surface in the heavy isotope with Δ 65Cu(solid-solution) equals 1.0 ± 0.25‰ and 0.78 ± 0.2‰ for gibbsite and goethite, respectively. The last result corroborates the recent works of Mathur et al. [Mathur R., Ruiz J., Titley S., Liermann L., Buss H. and Brantley S. (2005) Cu isotopic fractionation in the supergene environment with and without bacteria. Geochim. Cosmochim. Acta69, 5233-5246] and Balistrieri et al. [Balistrieri L. S., Borrok D. M., Wanty R. B. and Ridley W. I. (2008) Fractionation of Cu and Zn isotopes during adsorption onto amorhous Fe(III) oxyhydroxide: experimental mixing of acid rock drainage and ambient river water. Geochim. Cosmochim. Acta72, 311-328] who reported heavy Cu isotope enrichment onto amorphous ferric oxyhydroxide and on metal hydroxide precipitates on the external membranes of Fe-oxidizing bacteria, respectively. Although measured isotopic fractionation does not correlate with the relative thermodynamic stability of surface complexes, it can be related to their structures as found with available EXAFS data. Indeed, strong, bidentate, inner-sphere complexes presented by tetrahedrally coordinated Cu on metal oxide surfaces are likely to result in enrichment of the heavy isotope on the surface compared to aqueous solution. The outer-sphere, monodentate complex, which is likely to form between Cu 2+ and surface phosphoryl groups of bacteria in acidic solutions, has a higher number of neighbors and longer bond distances compared to inner-sphere bidentate complexes with carboxyl groups formed on bacterial and diatom surfaces in circumneutral solutions. As a result, in acidic solution, light isotopes become more enriched on bacterial surfaces (as opposed to the surrounding aqueous medium) than they do in neutral solution. Overall, the results of the present study demonstrate important isotopic fractionation of copper in both organic and inorganic systems and provide a firm basis for using Cu isotopes for tracing metal transport in earth-surface aquatic systems. It follows that both adsorption on oxides in a wide range of pH values and adsorption on bacteria in acidic solutions are capable of producing a significant (up to 2.5-3‰ (±0.1-0.15‰)) isotopic offset. At the same time, Cu interaction with common soil and aquatic bacteria, as well as marine and freshwater diatoms, at 4 < pH < 8 yields an isotopic shift of only ±0.2-0.3‰, which is not related to Cu concentration in solution, surface loading, the duration of the experiment, or the type of aquatic microorganisms.

Au-HKUST-1 Composite Nanocapsules: Synthesis with a Coordination Replication Strategy and Catalysis on CO Oxidation.

PubMed

Liu, Yongxin; Zhang, Jiali; Song, Lingxiao; Xu, Wenyuan; Guo, Zanru; Yang, Xiaomin; Wu, Xiaoxin; Chen, Xi

2016-09-07

A novel coordination replication of Cu2O redox-template strategy is reported to efficiently fabricate Au-HKUST-1 composite nanocapsule, with a HKUST-1 sandwich shell and an embedded Au nanoparticles layer. The novel synthesis procedure involves forming Au nanoparticles on the surface of Cu2O, transforming partial Cu2O into HKUST-1 shell via coordination replication, and removing the residual Cu2O by acid. The as-prepared Au-HKUST-1 composite nanocapsules displayed high catalytic activity on CO oxidation.

Synthesis and redox activity of "clicked" triazolylbiferrocenyl polymers, network encapsulation of gold and silver nanoparticles and anion sensing.

PubMed

Rapakousiou, Amalia; Deraedt, Christophe; Irigoyen, Joseba; Wang, Yanlan; Pinaud, Noël; Salmon, Lionel; Ruiz, Jaime; Moya, Sergio; Astruc, Didier

2015-03-02

The design of redox-robust polymers is called for in view of interactions with nanoparticles and surfaces toward applications in nanonetwork design, sensing, and catalysis. Redox-robust triazolylbiferrocenyl (trzBiFc) polymers have been synthesized with the organometallic group in the side chain by ring-opening metathesis polymerization using Grubbs-III catalyst or radical polymerization and with the organometallic group in the main chain by Cu(I) azide alkyne cycloaddition (CuAAC) catalyzed by [Cu(I)(hexabenzyltren)]Br. Oxidation of the trzBiFc polymers with ferricenium hexafluorophosphate yields the stable 35-electron class-II mixed-valent biferrocenium polymer. Oxidation of these polymers with Au(III) or Ag(I) gives nanosnake-shaped networks (observed by transmission electron microscopy and atomic force microscopy) of this mixed-valent Fe(II)Fe(III) polymer with encapsulated metal nanoparticles (NPs) when the organoiron group is located on the side chain. The factors that are suggested to be synergistically responsible for the NP stabilization and network formation are the polymer bulk, the trz coordination, the nearby cationic charge of trzBiFc, and the inter-BiFc distance. For instance, reduction of such an oxidized trzBiFc-AuNP polymer to the neutral trzBiFc-AuNP polymer with NaBH4 destroys the network, and the product flocculates. The polymers easily provide modified electrodes that sense, via the oxidized Fe(II)Fe(III) and Fe(III)Fe(III) polymer states, respectively, ATP(2-) via the outer ferrocenyl units of the polymer and Pd(II) via the inner Fc units; this recognition works well in dichloromethane, but also to a lesser extent in water with NaCl as the electrolyte.

Self-adjusted flux for the traveling solvent floating zone growth of YBaCuFeO5 crystal

NASA Astrophysics Data System (ADS)

Lai, Yen-Chung; Shu, Guo-Jiun; Chen, Wei-Tin; Du, Chao-Hung; Chou, Fang-Cheng

2015-03-01

A modified traveling solvent floating zone (TSFZ) technique was used to successfully grow a large size and high quality single crystal of multiferroic material YBaCuFeO5. This modified TSFZ growth uses a stoichiometric feed rod and pure copper oxide as the initial flux without prior knowledge of the complex phase diagram involving four elements, and the optimal flux for the growth of incongruently melt crystal is self-adjusted after a prolonged stable pulling. The wetting of the feed rod edge that often perturbs the molten zone stability was avoided by adding 2 wt% B2O3. The optimal flux concentration for the YBaCuFeO5 growth can be extracted to be near YBaCuFeO5:CuO=13:87 in molar ratio. The crystal quality was confirmed by the satisfactory refinement of crystal structure of space group P4mm and the two consecutive anisotropic antiferromagnetic phase transitions near 455 K and 170 K.

Electrolytic production of high purity aluminum using ceramic inert anodes

DOEpatents

Ray, Siba P.; Liu, Xinghua; Weirauch, Douglas A.; DiMilia, Robert A.; Dynys, Joseph M.; Phelps, Frankie E.; LaCamera, Alfred F.

2002-01-01

A method of producing commercial purity aluminum in an electrolytic reduction cell comprising ceramic inert anodes is disclosed. The method produces aluminum having acceptable levels of Fe, Cu and Ni impurities. The ceramic inert anodes used in the process may comprise oxides containing Fe and Ni, as well as other oxides, metals and/or dopants.

Influence of substrate rocks on Fe Mn crust composition

NASA Astrophysics Data System (ADS)

Hein, James R.; Morgan, Charles L.

1999-05-01

Principal Component and other statistical analyses of chemical and mineralogical data of Fe-Mn oxyhydroxide crusts and their underlying rock substrates in the central Pacific indicate that substrate rocks do not influence crust composition. Two ridges near Johnston Atoll were dredged repetitively and up to seven substrate rock types were recovered from small areas of similar water depths. Crusts were analyzed mineralogically and chemically for 24 elements, and substrates were analyzed mineralogically and chemically for the 10 major oxides. Compositions of crusts on phosphatized substrates are distinctly different from crusts on substrates containing no phosphorite. However, that relationship only indicates that the episodes of phosphatization that mineralized the substrate rocks also mineralized the crusts that grew on them. A two-fold increase in copper contents in crusts that grew on phosphatized clastic substrate rocks, relative to crusts on other substrate rock types, is also associated with phosphatization and must have resulted from chemical reorganization during diagenesis. Phosphatized crusts show increases in Sr, Zn, Ca, Ba, Cu, Ce, V, and Mo contents and decreases in Fe, Si, and As contents relative to non-phosphatized crusts. Our statistical results support previous studies which show that crust compositions reflect predominantly direct precipitation from seawater (hydrogenetic), and to lesser extents reflect detrital input and diagenetic replacement of parts of the older crust generation by carbonate fluorapatite.

Influence of substrate rocks on Fe-Mn crust composition

USGS Publications Warehouse

Hein, J.R.; Morgan, C.L.

1999-01-01

Principal Component and other statistical analyses of chemical and mineralogical data of Fe-Mn oxyhydroxide crusts and their underlying rock substrates in the central Pacific indicate that substrate rocks do not influence crust composition. Two ridges near Johnston Atoll were dredged repetitively and up to seven substrate rock types were recovered from small areas of similar water depths. Crusts were analyzed mineralogically and chemically for 24 elements, and substrates were analyzed mineralogically and chemically for the 10 major oxides. Compositions of crusts on phosphatized substrates are distinctly different from crusts on substrates containing no phosphorite. However, that relationship only indicates that the episodes of phosphatization that mineralized the substrate rocks also mineralized the crusts that grew on them. A two-fold increase in copper contents in crusts that grew on phosphatized clastic substrate rocks, relative to crusts on other substrate rock types, is also associated with phosphatization and must have resulted from chemical reorganization during diagenesis. Phosphatized crusts show increases in Sr, Zn, Ca, Ba, Cu, Ce, V, and Mo contents and decreases in Fe, Si, and As contents relative to non-phosphatized crusts. Our statistical results support previous studies which show that crust compositions reflect predominantly direct precipitation from seawater (hydrogenetic), and to lesser extents reflect detrital input and diagenetic replacement of parts of the older crust generation by carbonate fluorapatite.

NiFeCo/Cu superlattices with high magnetoresistive sensitivity and weak hysteresis

NASA Astrophysics Data System (ADS)

Bannikova, N. S.; Milyaev, M. A.; Naumova, L. I.; Krinitsina, T. P.; Patrakov, E. I.; Proglyado, V. V.; Chernyshova, T. A.; Ustinov, V. V.

2016-10-01

The microstructure and the magetoresistive characteristics of [NiFeCo/Cu]8 superlattices prepared by magnetron sputtering with various thickness of the buffer NiFeCr layer and exhibiting a giant magnetoresistive effect have been studied. It has been found that these nanostructures are formed with a strong or weak hysteresis depending on the structure (bcc or fcc) formed in the NiFeCr buffer layer. The method of the substantial decrease in the hysteresis loop width of the magnetoresistance by using the composite Ta/NiFeCr buffer layer has been suggested.

Re-evaluation of the impact of ternary additions of Ni and Cu on the A1 to L1{sub 0} transformation in FePt films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, B.; Barmak, K.

2011-06-15

The impact of ternary additions of Ni (1.6-21.5 at. %) and Cu (1.3-17.3 at. %) on the A1 (face centered cubic, fcc) to L1{sub 0} phase transformation in FePt films has been re-evaluated based on compositions obtained using energy dispersive x-ray spectrometry (EDS). The data presented here serve as corrections to results reported in six previous studies [D. C. Berry and K. Barmak, J. Appl. Phys. 102, 024912 (2007); 101, 014905 (2007); 99, 08G901 (2006); D. C. Berry, J. Kim, K. Barmak, K. Wierman, E. B. Svedberg, and J. K. Howard, Scr. Mater. 53, 423 (2005); K. Barmak, J. Kim,more » D. C. Berry, W. N. Hanani, K. Wierman, E. B. Svedberg, and J. K. Howard, J. Appl. Phys. 97, 024902 (2005); K. Barmak, J. Kim, D. C. Berry, K. W. Wierman, E. B. Svedberg, and J. K. Howard, ibid. 95, 7486 (2004)]. The new EDS compositions do not change the following conclusions of these previous studies: (i) when ternary FeNiPt and FeCuPt alloys are compared with binary FePt alloys with the same Pt content, it is seen that additions of Ni slow the transformation kinetics, whereas additions of Cu have no measurable impact on the kinetics, (ii) the Curie temperature of the L1{sub 0} phase is lowered by additions of Ni or Cu, (iii) the Curie temperature of the A1 phase is increased by additions of Ni, but lowered by additions of Cu, and (iv) the transformation enthalpy is lowered by large additions of Ni, but is unaffected by additions of Cu. The ordering behavior of FeCuPt alloys as evidenced by the kinetic ordering temperature is compared with other reports in the literature based on magnetic measurements.« less

The dependence of nano-contact magnetoresistance on the bulk scattering spin asymmetry in CoFe alloys with oxidation impurities

NASA Astrophysics Data System (ADS)

Shiokawa, Yohei; Jung, JinWon; Otsuka, Takahiko; Sahashi, Masashi

2015-08-01

Nano-contact magnetoresistance (NCMR) spin-valves (SVs) using an AlOx nano-oxide-layer (NOL) have numerous nanocontacts in the thin AlOx oxide layer. The NCMR theoretically depends on the bulk scattering spin asymmetry ( β) of the ferromagnetic material in the nanocontacts. To determine the relationship between NCMR and β, we investigated the dependence of NCMR on the composition of the ferromagnetic material Co1-xFex. The samples were annealed at 270 °C and 380 °C to enhance the MR ratio. For both annealing temperatures, the magnetorsistance ratio in the low-resistance area product region at less than 1 Ω μm2 was maximized for Co0.5Fe0.5. To evaluate β exactly, we fabricated current-perpendicular-to-plane giant magnetoresistance SVs with Co1-xFex/Cu/Co1-xFex layers and used Valet and Fert's theory to solve the diffusion equation of the spin accumulation for a ferromagnetic layer/non-ferromagnetic layer of five layers with a finite diffusion length. The evaluated β for Co1-xFex was also maximized for Co0.5Fe0.5. Additionally, to determine the difference between the experimental MR ratio of NCMR SVs and the theoretical MR ratio, we fabricated Co0.5Fe0.5 with oxygen impurities and estimated the decrease in β with increasing oxygen impurity concentration. Our Co0.5Fe0.5 nano-contacts fabricated using ion-assisted oxidation may contain oxygen impurities, and the oxygen impurities might cause a decrease in β and the MR ratio.

Trace metals in the Ob and Yenisei Rivers' Estuaries (the Kara Sea).

NASA Astrophysics Data System (ADS)

Demina, L. L.

2014-12-01

Behavior of some trace metals (Al, As, Cd, Co, Cr, Cu, Fe, Mn, Ni and Pb) in water column (soluble <0.45 µm and particulate fractions) and bottom sediments (surface and cores) along the two transects from the Ob River and Yenisei River Estuaries to the Kara Sea was studied. The length of both transects was about 700 km. Water depth was 12-63 m, O2 dissolved :5.36-9.55 ml l-1. Along the transects salinity increased from 0.07 to 34.2 psu, while the SPM' concentration decreased from 10.31 to 0.31 mg/l. Total suspended particulate matter load is more than one order of magnitude higher in the Ob River Estuary comparing to that of the Yenisei River. It has led to a significant difference between the suspended trace metals' concentrations (µg/l) in water of the two estuaries. With salinity increase along transects Fe susp., Mn susp. and Zn susp. decreased by a factor of 100-500, that has led to a growth of a relative portion of dissolved trace metals followed by their bioaccumulation (Demina et al., 2010). A strong direct correlation between suspended Cu, Fe and SPM mass concentration was found. For the first time along the Yenisei River' Estuary -the Kara Sea transect a direct positive correlation between Cu suspended and volume concentration of SPM (mg/ml3) was found, that was attributed to contribution of phytoplankton aggregates in the SPM composition. A trend of relationship between content of suspended As and pelitic fraction (2-10 µm) of SPM was firstly found in theses basins also. Study of trace metal speciation in the bottom sediments (adsorbed, associated with Fe-Mn (oxyhydr)oxides, organic matter and fixed in the mineral lattice or refractory) has revealed the refractory fraction to be prevailing (70-95% total content) for Fe, Zn, Cu, Co, Ni, Cr, Cd and Pb. That means that toxic heavy metals were not available for bottom fauna. Mn was predominantly found in the adsorbed and (oxyhydr)oxides geochemically labile forms, reflecting the redox condition change along both transects and within the sedimentary cores. References. Demina L.L., Gordeev V.V., Galkin S.V., Kravchishina M.D. Biogeochemistry of some heavy metals and metalloids along the transect the Ob River Estuary - the Kara Sea. Oceanology, 2010, vo. 50, No 5, pp. 729- 742.

Aeolian removal of dust from radiator surfaces on Mars

NASA Technical Reports Server (NTRS)

Gaier, James R.; Perez-Davis, Marla E.; Rutledge, Sharon K.; Hotes, Deborah

1990-01-01

Simulated radiator surfaces made of arc-textured Cu and Nb-1 percent-Zr and ion beam textured graphite and C-C composite were fabricated and their integrated spectral emittance characterized from 300 to 3000 K. A thin layer of aluminum oxide, basalt, or iron (III) oxide dust was then deposited on them, and they were subjected to low pressure winds in the Martian Surface Wind Tunnel. It was found that dust deposited on simulated radiator surfaces may or may not seriously lower their integrated spectral emittance, depending upon the characteristics of the dust. With Al2O3 there is no appreciable degradation of emittance on a dusted sample, with basaltic dust there is a 10 to 20 percent degradation, and with Fe2O3 a 20 to 40 percent degradation. It was also found that very high winds on dusted highly textured surfaces can result in their abrasion. Degradation in emittance due to abrasion was found to vary with radiator material. Arc-textured Cu and Nb-1 percent Zr was found to be more susceptible to emittance degradation than graphite or C-C composite. The most abrasion occurred at low angles, peaking at the 22.5 deg test samples.

Fabrication of Fe{sub 3}O{sub 4}@CuO core-shell from MOF based materials and its antibacterial activity

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rajabi, S.K.; Sohrabnezhad, Sh., E-mail: sohrabnezhad@guilan.ac.ir; Ghafourian, S.

Magnetic Fe{sub 3}O{sub 4}@CuO nanocomposite with a core/shell structure was successfully synthesized via direct calcinations of magnetic Fe{sub 3}O{sub 4}@HKUST-1 in air atmosphere. The morphology, structure, magnetic and porous properties of the as-synthesized nano composites were characterized by using scanning electron microscope (SEM), transmission electron microscopy (TEM), powder X-ray diffraction (PXRD), and vibration sample magnetometer (VSM). The results showed that the nanocomposite material included a Fe{sub 3}O{sub 4} core and a CuO shell. The Fe{sub 3}O{sub 4}@CuO core-shell can be separated easily from the medium by a small magnet. The antibacterial activity of Fe{sub 3}O{sub 4}-CuO core-shell was investigated againstmore » gram-positive and gram-negative bacteria. A new mechanism was proposed for inactivation of bacteria over the prepared sample. It was demonstrated that the core-shell exhibit recyclable antibacterial activity, acting as an ideal long-acting antibacterial agent. - Graphical abstract: Fe{sub 3}O{sub 4}@CuO core-shell release of copper ions. These Cu{sup 2+} ions were responsible for the exhibited antibacterial activity. - Highlights: • The Fe{sub 3}O{sub 4}@CuO core-shell was prepared by MOF method. • This is the first study of antibacterial activity of core-shell consist of CuO and Fe{sub 3}O{sub 4}. • The core-shell can be reused effectively. • Core-shell was separated from the reaction solution by external magnetic field.« less

Simulation of acid mine drainage generation around Küre VMS Deposits, Northern Turkey

NASA Astrophysics Data System (ADS)

Demirel, Cansu; Kurt, Mehmet Ali; Çelik Balci, Nurgül

2015-04-01

This study investigated comparative leaching characteristics of acidophilic bacterial strains under shifting environmental conditions at proposed two stages as formation stage or post acidic mine drainage (AMD) generation. At the first stage, initial reactions associated with AMD generation was simulated in shaking flasks containing massive pyritic chalcopyrite ore by using a pure strain Acidithiobacillus ferrooxidans and a mixed culture of Acidithiobacillus sp. mostly dominated by A. ferrooxidans and A. thiooxidans at 26oC. At the second stage, long term bioleaching experiments were carried out with the same strains at 26oC and 40oC to investigate the leaching characteristics of pyritic chalcopyrite ore under elevated heavy metal and temperature conditions. During the experiments, physicochemical characteristics (e.i. Eh, pH, EC) metal (Fe, Co, Cu, Zn) and sulfate concentration of the experimental solution were monitored during 180 days. Significant acid generation and sulfate release were determined during bioleaching of the ore by mixed acidophilic cultures containing both iron and sulfur oxidizers. In the early stage of the experiments, heavy metal release from the ore was caused by generation of acid due to accelerated bacterial oxidation of the ore. Generally high concentrations of Co and Cu were released into the solution from the experiments conducted by pure cultures of Acidithiobacillus ferrooxidans whereas high Zn and Fe was released into the solution from the mixed culture experiments. In the later stage of AMD generation and post AMD, chemical oxidation is accelerated causing excessive amounts of contamination, even exceeding the amounts resulted from bacterial oxidation by mixed cultures. Acidithibacillus ferrooxidans was found to be more effective in leaching Cu, Fe and Co at higher temperatures in contrary to mixed acidophiles that are more prone to operate at optimal moderate conditions. Moreover, decreasing Fe values are noted in bioleaching experiments with mixed acidophiles at higher temperatures. Further depleted Fe(III) values coinciding with decreasing pH may point to precipitation of secondary phases (i.e. jarosite). This study revealed that the metals (Fe, Cu, Co and Zn) released during short term leaching of the ore (34 days) are generally caused by acid produced by dissolution reactions rather than oxidation. In the long term experiments a more complex biogeochemical reactions (oxidation and dissolution) take place in conjunction. Key words: Bioleaching, AMD, heavy metal release, environment, acidophilic bacteria, Küre copper ore deposits, volcanogenic massive sulfide deposits

The Gibbs free energy of nukundamite (Cu3.38Fe0.62S4): A correction and implications for phase equilibria

USGS Publications Warehouse

Seal, R.R.; Inan, E.E.; Hemingway, B.S.

2001-01-01

The Gibbs free energy of formation of nukundamite (Cu3.38Fe0.62S4) was calculated from published experimental studies of the reaction 3.25 Cu3.38Fe0.62S4 + S2 = 11 CuS + 2 FeS2 in order to correct an erroneous expression in the published record. The correct expression describing the Gibbs free energy of formation (kJ???mol-1) of nukundamite relative to the elements and ideal S2 gas is ??fG?? nukundamite T(K) = -549.75 + 0.23242 T + 3.1284 T0.5, with an uncertainty of 0.6%. An evaluation of the phase equilibria of nukundamite with associated phases in the system Cu-Fe-S as a function of temperature and sulfur fugacity indicates that nukundamite is stable from 224 to 501??C at high sulfidation states. At its greatest extent, at 434??C, the stability field of nukundamite is only 0.4 log f(S2) units wide, which explains its rarity. Equilibria between nukundamite and bornite, which limit the stability of both phases, involve bornite compositions that deviate significantly from stoichiometric Cu5FeS4. Under equilibrium conditions in the system Cu-Fe-S, nukundamite + chalcopyrite is not a stable assemblage at any temperature.

Dietary uptake of Cu sorbed to hydrous iron oxide is linked to cellular toxicity and feeding inhibition in a benthic grazer

USGS Publications Warehouse

Cain, Daniel J.; Croteau, Marie-Noele; Fuller, Christopher C.; Ringwood, Amy H.

2016-01-01

Whereas feeding inhibition caused by exposure to contaminants has been extensively documented, the underlying mechanism(s) are less well understood. For this study, the behavior of several key feeding processes, including ingestion rate and assimilation efficiency, that affect the dietary uptake of Cu were evaluated in the benthic grazer Lymnaea stagnalis following 4–5 h exposures to Cu adsorbed to synthetic hydrous ferric oxide (Cu–HFO). The particles were mixed with a cultured alga to create algal mats with Cu exposures spanning nearly 3 orders of magnitude at variable or constant Fe concentrations, thereby allowing first order and interactive effects of Cu and Fe to be evaluated. Results showed that Cu influx rates and ingestion rates decreased as Cu exposures of the algal mat mixture exceeded 104 nmol/g. Ingestion rate appeared to exert primary control on the Cu influx rate. Lysosomal destabilization rates increased directly with Cu influx rates. At the highest Cu exposure where the incidence of lysosomal membrane damage was greatest (51%), the ingestion rate was suppressed 80%. The findings suggested that feeding inhibition was a stress response emanating from excessive uptake of dietary Cu and cellular toxicity.

STRESS-INDUCED ASYMMETRIC MAGNETOIMPEDANCE EFFECT IN Ni80Fe20/Cu COMPOSITE WIRES

NASA Astrophysics Data System (ADS)

Lv, Wenxing; Li, Xin; Xie, Wenhui; Zhao, Qiang; Zhao, Zhenjie

The magnetoimpedance effect of Ni80Fe20/Cu composited wires was experimentally investigated by varying the Ni80Fe20 coating thickness. An asymmetric MI behavior with a tunable linear region around zero magnetic field by altering the thickness of Ni80Fe20 layer was demonstrated. And the MI behavior was governed by the different anisotropy induced by the residual local stress in the multi-layer region. In addition, our investigation also suggested that the interactions between interface phase and outer phase of coating layer decreased with thickness, resulting in the domination of the asymmetric MI characteristic. For thickness of 485nm, the sensitivity was up to 225%/Oe from -2 Oe to 2 Oe, providing a promising candidate for linear sensor application.

Chlorination of bromide-containing waters: enhanced bromate formation in the presence of synthetic metal oxides and deposits formed in drinking water distribution systems.

PubMed

Liu, Chao; von Gunten, Urs; Croué, Jean-Philippe

2013-09-15

Bromate formation from the reaction between chlorine and bromide in homogeneous solution is a slow process. The present study investigated metal oxides enhanced bromate formation during chlorination of bromide-containing waters. Selected metal oxides enhanced the decay of hypobromous acid (HOBr), a requisite intermediate during the oxidation of bromide to bromate, via (i) disproportionation to bromate in the presence of nickel oxide (NiO) and cupric oxide (CuO), (ii) oxidation of a metal to a higher valence state in the presence of cuprous oxide (Cu2O) and (iii) oxygen formation by NiO and CuO. Goethite (α-FeOOH) did not enhance either of these pathways. Non-charged species of metal oxides seem to be responsible for the catalytic disproportionation which shows its highest rate in the pH range near the pKa of HOBr. Due to the ability to catalyze HOBr disproportionation, bromate was formed during chlorination of bromide-containing waters in the presence of CuO and NiO, whereas no bromate was detected in the presence of Cu2O and α-FeOOH for analogous conditions. The inhibition ability of coexisting anions on bromate formation at pH 8.6 follows the sequence of phosphate > sulfate > bicarbonate/carbonate. A black deposit in a water pipe harvested from a drinking water distribution system exerted significant residual oxidant decay and bromate formation during chlorination of bromide-containing waters. Energy dispersive spectroscopy (EDS) analyses showed that the black deposit contained copper (14%, atomic percentage) and nickel (1.8%, atomic percentage). Cupric oxide was further confirmed by X-ray diffraction (XRD). These results indicate that bromate formation may be of concern during chlorination of bromide-containing waters in distribution systems containing CuO and/or NiO. Copyright © 2013 Elsevier Ltd. All rights reserved.

A computational study of the catalytic aerobic epoxidation of propylene over the coordinatively unsaturated metal-organic framework Fe3(btc)2: formation of propylene oxide and competing reactions.

PubMed

Maihom, Thana; Sawangphruk, Montree; Probst, Michael; Limtrakul, Jumras

2018-02-28

The aerobic epoxidation of propylene over the metal-organic framework Fe 3 (btc) 2 (btc = 1,3,5-benzentricarboxylate) as catalyst has been investigated by means of density functional calculations. The mechanisms of the reaction towards propylene oxide, carbonylic products (acetone and propanal) and a pi-allyl radical were investigated to assess the efficiency of Fe 3 (btc) 2 for the selective formation of propylene oxide. Propylene oxide and carbonylic products are formed on Fe 3 (btc) 2 by proceeding via propyleneoxy intermediates in the first step. Subsequently, the intermediates can then either be transformed to propylene oxide by way of ring closure of the intermediate or to the carbonylic compounds of propanal and acetone via 1,2-hydride shift. The results show that the formation of propylene oxide is favored over the formation of carbonylic products mainly due to the activation barriers being 2-3 times smaller. The activation barriers for the formation of the propyleneoxy intermediates on the Fe 3 (btc) 2 catalyst for the first and second reaction cycle are also lower than the barriers obtained for the formation of the pi-allyl radical that acts as the precursor to combustion products. On the basis of these computational results, we therefore expect a high catalytic selectivity of the Fe 3 (btc) 2 catalyst with respect to the formation of propylene oxide. We also compared the catalytic activities of Fe 3 (btc) 2 and Cu 3 (btc) 2 . The activation energy of the rate-determining step is almost 2 times lower for Fe 3 (btc) 2 than that for Cu 3 (btc) 2 , due to a larger charge transfer from the catalytic site to the O 2 molecule in the case of Fe 3 (btc) 2 .

Copper solubility in a basaltic melt and sulfide liquid/silicate melt partition coefficients of Cu and Fe

NASA Astrophysics Data System (ADS)

Ripley, Edward M.; Brophy, James G.; Li, Chusi

2002-09-01

The solubility of copper in a sulfur-saturated basaltic melt has been determined at 1245°C as a function of fO 2 and fS 2. Copper solubilities at log fO 2 values between -8 and -11 fall into two distinct populations as a function of fS 2. At log fS 2 values < -1.65, sulfide liquid that coexists with the basaltic glass quenches to sulfur-poor bornite solid solution. At log fS 2 values in excess of -1.65, the sulfide liquid quenches to a complex intergrowth of sulfur-rich bornite and intermediate solid solution. Copper solubilities in the low-fS 2 population range from 594 to 1550 ppm, whereas those in the high-fS 2 population range from 80 to 768 ppm. Sulfide liquid/silicate liquid partition coefficients (D) for Cu and Fe range from 480 to 1303 and 0.7 to 13.6, respectively. Metal-sulfur complexing in the silicate liquid is shown to be insignificant relative to metal-oxide complexing for Fe but permissible for Cu at high fS 2 values. On log D Fe (sulfide-silicate) and log D Cu (sulfide-silicate) vs. 1/2 (log fS 2 - log fO 2) diagrams, both fS 2 populations show distinct but parallel trends. The observation of two D values for any fS 2/fO 2 ratio indicates nonideal mixing of species involved in the exchange reaction. The two distinct trends observed for both Cu and Fe are thought to be due to variations in activity coefficient ratios (e.g., γ FeO/γ FeS and γ CuO 0.5/γ CuS 0.5). Results of the experiments suggest that accurate assessments of fS 2/fO 2 ratios are required for the successful numerical modeling of processes such as the partial melting of sulfide-bearing mantle and the crystallization of sulfide-bearing magmas, as well as the interpretation of sulfide mineralogical zoning. In addition, the experiments provide evidence for oxide or oxy-sulfide complexing for Cu in silicate magmas and suggest that the introduction of externally derived sulfur to mafic magma may be an important process for the formation of Cu-rich disseminated magmatic sulfide ore deposits.

Saline-water bioleaching of chalcopyrite with thermophilic, iron(II)- and sulfur-oxidizing microorganisms.

PubMed

Watling, Helen R; Collinson, David M; Corbett, Melissa K; Shiers, Denis W; Kaksonen, Anna H; Watkin, Elizabeth L J

2016-09-01

The application of thermoacidophiles for chalcopyrite (CuFeS2) bioleaching in hot, acidic, saline solution was investigated as a possible process route for rapid Cu extraction. The study comprised a discussion of protective mechanisms employed for the survival and/or adaptation of thermoacidophiles to osmotic stress, a compilation of chloride tolerances for three genera of thermoacidophiles applied in bioleaching and an experimental study of the activities of three species in a saline bioleaching system. The data showed that the oxidation rates of iron(II) and reduced inorganic sulfur compounds (tetrathionate) were reduced in the presence of chloride levels well below chloride concentrations in seawater, limiting the applicability of these microorganisms in the bioleaching of CuFeS2 in saline water. Copyright © 2016. Published by Elsevier Masson SAS.

Synthesis of Bilayer Graphene on 90/10 Copper (Cu)/Nickel (Ni) Alloy and Transfer by Electrochemical Delamination

DTIC Science & Technology

2017-09-01

C) and slow decomposition rate in methane (CH4).11 Cu alone has sometimes been shown to form incomplete bilayers with a significant fraction of...argon BLG bilayer graphene C carbon CH4 methane Cu2O cuprous oxide Cu copper CVD chemical vapor deposition DI deionized FeCl3 iron

Geochemical processes controlling the distribution and concentration of metals in soils from a Patagonian (Argentina) salt marsh affected by mining residues.

PubMed

Idaszkin, Yanina L; Alvarez, María Del Pilar; Carol, Eleonora

2017-10-15

Heavy metal pollution that affects salt marshes is a major environmental concern due to its toxic nature, persistence, and potential risk to organisms and to human health. Mining waste deposits originated four decades ago, by the metallurgical extraction of heavy metals, are found near to the San Antonio salt marsh in Patagonia. The aim of the work was to determine the geochemical processes that control the distribution and concentration of Cu, Fe, Pb and Zn in the soils of this Patagonian salt marsh. A survey of the mining waste deposits was carried out where three dumps were identified. Samples were collected to determine soil texture, Eh pH, organic matter and metal contents and the soil mineralogical composition. The results shows that the soils developed over the mining waste deposits are predominantly reddish constituted mainly by iron oxide, hydroxide and highly soluble minerals such as Zn and Cu sulphates. The drainage from these deposits tends to move towards the salt marsh. Within the salt marsh, the highest concentrations of Cu, Pb and Zn occur in the sectors closest to the mining wastes deposits. The sulphide oxidation and the dissolution of the Cu, Pb and Zn sulphates could be the mainly source of these metals in the drainage water. The metals in solution that reach the salt marsh, are adsorbed by the organic matter and the fine fraction of the soils. These adsorbed metals are then remobilized by tides in the lower sectors of the marsh by desorption from the cations present in the tidal flow. On the other hand, Fe tends to form non soluble oxides, hydroxides and sulphates which remain as altering material within the mining waste deposit. Finally, the heavy metal pollutants recorded in the San Antonio salt marsh shows that the mining waste deposits that were abandoned four decades ago are still a source metal contamination. Copyright © 2017 Elsevier B.V. All rights reserved.

X-ray absorption fine structure and x-ray diffraction studies of crystallographic grains in nanocrystalline FePd:Cu thin films

NASA Astrophysics Data System (ADS)

Krupinski, M.; Perzanowski, M.; Polit, A.; Zabila, Y.; Zarzycki, A.; Dobrowolska, A.; Marszalek, M.

2011-03-01

FePd alloys have recently attracted considerable attention as candidates for ultrahigh density magnetic storage media. In this paper we investigate FePd thin alloy film with a copper admixture composed of nanometer-sized grains. [Fe(0.9 nm)/Pd(1.1 nm)/Cu(d nm)]×5 multilayers were prepared by thermal deposition at room temperature in UHV conditions on Si(100) substrates covered by 100 nm SiO2. The thickness of the copper layer has been changed from 0 to 0.4 nm. After deposition, the multilayers were rapidly annealed at 600 °C in a nitrogen atmosphere, which resulted in the creation of the FePd:Cu alloy. The structure of alloy films obtained this way was determined by x-ray diffraction (XRD), glancing angle x-ray diffraction, and x-ray absorption fine structure (EXAFS). The measurements clearly showed that the L10 FePd:Cu nanocrystalline phase has been formed during the annealing process for all investigated copper compositions. This paper concentrates on the crystallographic grain features of FePd:Cu alloys and illustrates that the EXAFS technique, supported by XRD measurements, can help to extend the information about grain size and grain shape of poorly crystallized materials. We show that, using an appropriate model of the FePd:Cu grains, the comparison of EXAFS and XRD results gives a reasonable agreement.

Stabilized super-thermite colloids: A new generation of advanced highly energetic materials

NASA Astrophysics Data System (ADS)

Elbasuney, Sherif; Gaber Zaky, M.; Radwan, Mostafa; Mostafa, Sherif F.

2017-10-01

One of the great impetus of nanotechnology on energetic materials is the achievement of nanothermites (metal-oxide/metal) which are characterized by massive heat output. Yet, full exploitation of super-thermites in highly energetic systems has not been achieved. This manuscript reports on the sustainable fabrication of colloidal Fe2O3 and CuO nanoparticles for thermite applications. TEM micrographs demonstrated mono-dispersed Fe2O3 and CuO with an average particle size of 3 and 15 nm respectively. XRD diffractograms demonstrated highly crystalline materials. SEM micrographs demonstrated a great tendency of the developed oxides to aggregate over drying process. The effective integration and dispersion of mono-dispersed colloidal thermite particles into energetic systems are vital for enhanced performance. Aluminum is of interest as highly energetic metal fuel. In this paper, synthesized Fe2O3 and CuO nanoparticles were re-dispersed in isopropyl alcohol (IPA) with aluminum nanoparticles using ultrasonic prope homogenizer. The colloidal thermite peraticles can be intgegrated into highly energetic system for subsequent nanocomposite development. Thanks to stabilization of colloidal CuO nanoparticles in IPA which could offer intimate mixing between oxidizer and metal fuel. The stabilization mechanism of CuO in IPA was correlated to steric stabilization with solvent molecules. This approach eliminated nanoparticle drying and the re-dispersion of dry aggregates into energetic materials. This manuscript shaded the light on the real development of colloidal thermite mixtures and their integration into highly energetic systems.

A study of the semiconductor compound СuAlO2 by the method of nuclear quadrupole resonance of Cu

NASA Astrophysics Data System (ADS)

Matukhin, V. L.; Khabibulin, I. Kh.; Shul'gin, D. A.; Smidt, S. V.

2012-07-01

The method of nuclear quadrupole resonance of Cu (NQR Cu) is used to study the samples of a semiconductor compound CuAlO2. The crystal structure of CuAlO2 belongs to the family of delafossite - the mineral of a basic CuFeO2 structure. Transparent semiconductor oxides, such as CuAlO2, have attracted recent attention as promising thermoelectric materials.

Synthesis and characterization of Chitosan-CuO-MgO polymer nanocomposites

NASA Astrophysics Data System (ADS)

Praffulla, S. R.; Bubbly, S. G.

2018-05-01

In the present work, we have synthesized Chitosan-CuO-MgO nanocomposites by incorporating CuO and MgO nanoparticles in chitosan matrix. Copper oxide and magnesium oxide nanoparticles synthesized by precipitation method were characterized by X-ray diffraction and the diffraction patterns confirmed the monoclinic and cubic crystalline structures of CuO and MgO nanoparticles respectively. Chitosan-CuO-MgO composite films were prepared using solution- cast method with different concentrations of CuO and MgO nanoparticles (15 - 50 wt % with respect to chitosan) and characterized by XRD, FTIR and UV-Vis spectroscopy. The X-ray diffraction pattern shows that the crystallinity of the chitosan composite increases with increase in nanoparticle concentration. FTIR spectra confirm the chemical interaction between chitosan and metal oxide nanoparticles (CuO and MgO). UV absorbance of chitosan nanocomposites were up to 17% better than pure chitosan, thus confirming its UV shielding properties. The mechanical and electrical properties of the prepared composites are in progress.

Facile synthesis of highly active reduced graphene oxide-CuI catalyst through a simple combustion method for photocatalytic reduction of CO2 to methanol

NASA Astrophysics Data System (ADS)

Zhang, Wenjun; Li, Yingjie; Zhang, Xiaoxiong; Li, Cuiluo

2017-09-01

We report a facile combustion method synthesis of reduced graphene oxide/CuI composites as a photocatalyst, in which CuI nanoparticles were homogeneously distributed on the surface of reduced graphene oxide (rGO), showing a good visible light response. The rGO-supported and unsupported CuI hybrids were tested over the photocatalytic reduction of CO2 for methanol evolution in visible light. In the current study rGO-CuI composites have shown excellent yields (19.91 μmol g-cat-1). rGO provides a light-weight, charge complementary and two-dimensional material that interacts effectively with the CuI nanoparticles.

Synthesis of hierarchical Mg-doped Fe3O4 micro/nano materials for the decomposition of hexachlorobenzene.

PubMed

Su, Guijin; Liu, Yexuan; Huang, Linyan; Lu, Huijie; Liu, Sha; Li, Liewu; Zheng, Minghui

2014-03-01

An ethylene-glycol (EG) mediated self-assembly process was firstly developed to synthesize micrometer-sized nanostructured Mg-doped Fe3O4 composite oxides to decompose hexachlorobenzene (HCB) at 300°C. The synthesized samples were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, energy dispersive X-ray spectroscopy and inductively coupled plasma optical emission spectrometer. The morphology and composition of the composite oxide precursor were regulated by the molar ratio of the magnesium acetate and ferric nitrate as the reactants. Calcination of the precursor particles, prepared with different molar ratio of the metal salts, under a reducing nitrogen atmosphere, generated three kinds of Mg doped Fe3O4 composite oxide micro/nano materials. Their reactivity toward HCB decomposition was likely influenced by the material morphology and content of Mg dopants. Ball-like MgFe2O4-Fe3O4 composite oxide micro/nano material showed superior HCB dechlorination efficiencies when compared with pure Fe3O4 micro/nano material, prepared under similar experimental conditions, thus highlighting the benefits of doping Mg into Fe3O4 matrices. Copyright © 2013 Elsevier Ltd. All rights reserved.

A review of the structure, and fundamental mechanisms and kinetics of the leaching of chalcopyrite.

PubMed

Li, Y; Kawashima, N; Li, J; Chandra, A P; Gerson, A R

2013-09-01

Most investigators regard CuFeS2 as having the formal oxidation states of Cu(+)Fe(3+)(S(2-))2. However, the spectroscopic characterisation of chalcopyrite is clearly influenced by the considerable degree of covalency between S and both Fe and Cu. The poor cleavage of CuFeS2 results in conchoidal surfaces. Reconstruction of the fractured surfaces to form, from what was previously bulk S(2-), a mixture of surface S(2-), S2(2) and S(n)(2-) (or metal deficient sulfide) takes place. Oxidation of chalcopyrite in air (i.e. 0.2 atm of O2 equilibrated with atmospheric water vapour) results in a Fe(III)-O-OH surface layer on top of a Cu rich sulfide layer overlying the bulk chalcopyrite with the formation of Cu(II) and Fe(III) sulfate, and Cu(I)-O on prolonged oxidation. Cu2O and Cu2S-like species have also been proposed to form on exposure of chalcopyrite to air. S2(2-), S(n)(2-) and S(0) form on the chalcopyrite surface upon aqueous leaching. The latter two of these species along with a jarosite-like species are frequently proposed to result in surface leaching passivation. However, some investigators have reported the formation of S(0) sufficiently porous to allow ion transportation to and from the chalcopyrite surface. Moreover, under some conditions both S(n)(2-) and S(0) were observed to increase in surface concentration for the duration of the leach with no resulting passivation. The effect of a number of oxidants, e.g. O2, H2O2, Cu(2+), Cr(6+) and Fe(3+), has been examined. However, this is often accompanied by poor control of leach parameters, principally pH and E(h). Nevertheless, there is general agreement in the literature that chalcopyrite leaching is significantly affected by solution redox potential with an optimum E(h) range suggesting the participation of leach steps that involve both oxidation and reduction. Three kinetic models have generally been suggested by researchers to be applicable: diffusion, chemical reaction and a mixed model containing diffusion and chemical components which occur at different stages of leaching. Passivation effects, due to surface diffusion rate control, may be affected by leach conditions such as pH or E(h). However, only initial conditions are generally described and these parameters are not controlled in most studies. However, at fixed pH, E(h) and temperature, it appears most likely that leaching in sulfuric acid media in the presence of added Fe(3+) is surface reaction rate controlled with some initial period, depending on leach conditions, where the leach rate is surface layer diffusion controlled. Although bioleaching of some copper ores has been adopted by industry, bioleaching has yet to be applied to predominantly chalcopyrite ores due to the slow resulting leach rates. Mixed microbial strains usually yield higher leach rates, as compared to single strains, as different bacterial strains are able to adapt to the changing leach conditions throughout the leach process. As for chemical leaching, passivation is also observed on bioleaching with jarosite being likely to be the main contributor. In summary, whilst much has been observed at the macro-scale regarding the chalcopyrite leach process it is clear that interpretation of these phenomena is hampered by lack of understanding at the molecular or atomic scale. Three primary questions that require elucidation, before the overall mechanism can be understood are: 1. How does the surface of chalcopyrite interact with solution or air borne oxidants? 2. How does the nature of these oxidants affect the surface products formed? 3. What determines whether the surface formed will be passivating or not? These can only realistically be tackled by the application of near atomic-scale analytical approaches, which may include quantum chemical modelling, PEEM/SPEM, TEM, AFM etc. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Lattice distortion of square iron nitride monolayers induced by changing symmetry of substrate

NASA Astrophysics Data System (ADS)

Hattori, Takuma; Iimori, Takushi; Miyamachi, Toshio; Komori, Fumio

2018-04-01

Rectangular iron nitride monatomic layers are fabricated on the threefold symmetric Cu(111) substrate by taking advantage of the stability of the square nitride film. Two different ordered structures are observed on the Cu(111) substrate by scanning tunneling microscopy after annealing at 510 K and 580 K. Their chemical composition and lattice symmetry are investigated by x-ray photoelectron spectroscopy and low energy electron diffraction. The monolayer film prepared at 580 K is a distorted Fe2N monolayer analogous to a ferromagnetic square Fe2N monolayer with a clock reconstruction on the Cu(001) substrate. The lattice deformation of the square Fe2N monolayer is induced by using Cu(111) with threefold symmetry.

Commentary on the sphalerite geobarometer

USGS Publications Warehouse

Toulmin, P.; Barton, P.B.; Wiggins, L.B.

1991-01-01

The FeS content of sphalerite in assemblages with pyrite and pyrrhotite has been widely used and widely criticized as a geobarometer. The commonly accepted form of the geobarometer is based on the composition of sphalerite being independent of temperature below about 550??C at all pressures up to at least 10 kbar, but strong thermodynamic arguments require a significant temperature dependence in this region. Most minor components have a negligible effect on the relevant equilibria, but the effect of CuS is somewhat more significant. Molar and partial molar volumes for binary (ZnS-FeS) and ternary (ZnS-FeS-CuS) sphalerite solutions are presented; the ternary data are consistent with charge transfer between Cu and Fe. -from Authors

Redox-induced mobilization of copper, selenium, and zinc in deltaic soils originating from Mississippi (U.S.A.) and Nile (Egypt) River Deltas: A better understanding of biogeochemical processes for safe environmental management.

PubMed

Shaheen, Sabry M; Frohne, Tina; White, John R; DeLaune, Ron D; Rinklebe, Jörg

2017-01-15

Studies about the mobilization of potentially toxic elements (PTEs) in deltaic soils can be challenging, provide critical information on assessing the potential risk and fate of these elements and for sustainable management of these soils. The impact of redox potential (E H ), pH, iron (Fe), manganese (Mn), sulfate (SO 4 2- ), chloride (Cl - ), aliphatic dissolved organic carbon (DOC), and aromatic dissolved organic carbon (DAC) on the mobilization of copper (Cu), selenium (Se), and zinc (Zn) was studied in two soils collected from the Nile and Mississippi Rivers deltaic plains focused on increasing our understanding of the fate of these toxic elements. Soils were exposed to a range of redox conditions stepwise from reducing to oxidizing soil conditions using an automated biogeochemical microcosm apparatus. Concentrations of DOC and Fe were high under reducing conditions as compared to oxidizing conditions in both soils. The proportion of DAC in relation to DOC in solution (aromaticity) was high in the Nile Delta soil (NDS) and low in the Mississippi Delta soil (MDS) under oxidizing conditions. Mobilization of Cu was low under reducing conditions in both soils which was likely caused by sulfide precipitation and as a result of reduction of Cu 2+ to Cu 1+ . Mobilization of Se was high under low E H in both soils. Release of Se was positively correlated with DOC, Fe, Mn, and SO 4 2- in the NDS, and with Fe in the MDS. Mobilization of Zn showed negative correlations with E H and pH in the NDS while these correlations were non-significant in the MDS. The release dynamics of dissolved Zn could be governed mainly by the chemistry of Fe and Mn in the NDS and by the chemistry of Mn in the MDS. Our findings suggest that a release of Se and Zn occurs under anaerobic conditions, while aerobic conditions favor the release of Cu in both soils. In conclusion, the release of Cu, Se, and Zn under different reducing and oxidizing conditions in deltaic wetland soils should be taken into account due to increased mobilization and the potential environmental risks associated with food security in utilizing these soils for flooded agricultural and fisheries systems. Copyright © 2016 Elsevier Ltd. All rights reserved.

Moving Fe2+ from ferritin ion channels to catalytic OH centers depends on conserved protein cage carboxylates.

PubMed

Behera, Rabindra K; Theil, Elizabeth C

2014-06-03

Ferritin biominerals are protein-caged metabolic iron concentrates used for iron-protein cofactors and oxidant protection (Fe(2+) and O2 sequestration). Fe(2+) passage through ion channels in the protein cages, like membrane ion channels, required for ferritin biomineral synthesis, is followed by Fe(2+) substrate movement to ferritin enzyme (Fox) sites. Fe(2+) and O2 substrates are coupled via a diferric peroxo (DFP) intermediate, λmax 650 nm, which decays to [Fe(3+)-O-Fe(3+)] precursors of caged ferritin biominerals. Structural studies show multiple conformations for conserved, carboxylate residues E136 and E57, which are between ferritin ion channel exits and enzymatic sites, suggesting functional connections. Here we show that E136 and E57 are required for ferritin enzyme activity and thus are functional links between ferritin ion channels and enzymatic sites. DFP formation (Kcat and kcat/Km), DFP decay, and protein-caged hydrated ferric oxide accumulation decreased in ferritin E57A and E136A; saturation required higher Fe(2+) concentrations. Divalent cations (both ion channel and intracage binding) selectively inhibit ferritin enzyme activity (block Fe(2+) access), Mn(2+) < Co(2+) < Cu(2+) < Zn(2+), reflecting metal ion-protein binding stabilities. Fe(2+)-Cys126 binding in ferritin ion channels, observed as Cu(2+)-S-Cys126 charge-transfer bands in ferritin E130D UV-vis spectra and resistance to Cu(2+) inhibition in ferritin C126S, was unpredicted. Identifying E57 and E136 links in Fe(2+) movement from ferritin ion channels to ferritin enzyme sites completes a bucket brigade that moves external Fe(2+) into ferritin enzymatic sites. The results clarify Fe(2+) transport within ferritin and model molecular links between membrane ion channels and cytoplasmic destinations.

Modelling removal mechanisms of Pb, Cu, Zn and Cd in acidic groundwater during the neutralization by ambient surface and ground waters

USGS Publications Warehouse

Paulson, Anthony J.; Balistrieri, Laurie S.

1999-01-01

Removal of Pb, Cu, Zn, and Cd during neutralization of acid rock drainage is examined using model simulations of field conditions and laboratory experiments involving mixing of natural drainage and surface waters or groundwaters. The simulations consider sorption onto hydrous Fe and Al oxides and particulate organic carbon, mineral precipitation, and organic and inorganic solution complexation of metals for two physical systems where newly formed oxides and particulate organic matter are either transported or retained along the chemical pathway. The calculations indicate that metal removal is a strong function of the physical system. Relative to direct discharge of ARD into streams, lower metal removals are observed where ARD enters streamwaters during the latter stages of neutralization by ambient groundwater after most of the Fe has precipitated and been retained in the soils. The mixing experiments, which represent the field simulations, also demonstrated the importance of dissolved metal to particle Fe ratios in controlling dissolved metal removal along the chemical pathway. Finally, model calculations indicate that hydrous Fe oxides and particulate organic carbon are more important than hydrous Al oxides in removing metals and that both inorganic and organic complexation must be considered when modeling metal removal from aquatic systems that are impacted by sulfide oxidation.

Cu isotope fractionation response to oxidative stress in a hepatic cell line studied using multi-collector ICP-mass spectrometry.

PubMed

Flórez, María R; Costas-Rodríguez, Marta; Grootaert, Charlotte; Van Camp, John; Vanhaecke, Frank

2018-03-01

Reactive oxygen species (ROS) are generated in biological processes involving electron transfer reactions and can act in a beneficial or deleterious way. When intracellular ROS levels exceed the cell's anti-oxidant capacity, oxidative stress occurs. In this work, Cu isotope fractionation was evaluated in HepG2 cells under oxidative stress conditions attained in various ways. HepG2 is a well-characterised human hepatoblastoma cell line adapted to grow under high oxidative stress conditions. During a pre-incubation stage, cells were exposed to a non-toxic concentration of Cu for 24 h. Subsequently, the medium was replaced and cells were exposed to one of three different external stressors: H 2 O 2 , tumour necrosis factor α (TNFα) or UV radiation. The isotopic composition of the intracellular Cu was determined by multi-collector ICP-mass spectrometry to evaluate the isotope fractionation accompanying Cu fluxes between cells and culture medium. For half of these setups, the pre-incubation solution also contained N-acetyl-cysteine (NAC) as an anti-oxidant to evaluate its protective effect against oxidative stress via its influence on the extent of Cu isotope fractionation. Oxidative stress caused the intracellular Cu isotopic composition to be heavier compared to that in untreated control cells. The H 2 O 2 and TNFα exposures rendered similar results, comparable to those obtained after mild UV exposure. The heaviest Cu isotopic composition was observed under the strongest oxidative conditions tested, i.e., when the cell surfaces were directly exposed to UV radiation without apical medium and in absence of NAC. NAC mitigated the extent of isotope fractionation in all cases.

Fe-MoS4: An Effective and Stable LDH-Based Adsorbent for Selective Removal of Heavy Metals.

PubMed

Jawad, Ali; Liao, Zhuwei; Zhou, Zhihua; Khan, Aimal; Wang, Ting; Ifthikar, Jerosha; Shahzad, Ajmal; Chen, Zhulei; Chen, Zhuqi

2017-08-30

It has always been a serious challenge to design efficient, selective, and stable absorbents for heavy-metal removal. Herein, we design layered double hydroxide (LDH)-based Fe-MoS 4 , a highly efficient adsorbent, for selective removal of heavy metals. We initially synthesized FeMgAl-LDH and then enriched its protective layers with MoS 4 2- anions as efficient binding sites for heavy metals. Various characterization tools, such as X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy, Raman spectroscopy, scanning electron microscopy, energy-dispersive X-ray, X-ray photoelectron spectroscopy (XPS), CHN analysis, and inductively coupled plasma analysis, were applied to confirm structural and compositional changes during the synthesis of Fe-MoS 4 as final product. The prepared Fe-MoS 4 offered excellent attraction for heavy metals, such as Hg 2+ , Ag + , Pb 2+ , and Cu 2+ , and displayed selectivity in the order Hg 2+ ∼ Ag + > Pb 2+ > Cu 2+ > Cr 6+ > As 3+ > Ni 2+ ∼ Zn 2+ ∼ Co 2+ . The immense capacities of Hg 2+ , Ag + , and Pb 2+ (583, 565, and 346 mg/g, respectively), high distribution coefficient (K d ∼ 10 7 -10 8 ), and fast kinetics place Fe-MoS 4 on the top of materials list known for removal of such metals. The sorption kinetics and isothermal studies conducted on Hg 2+ , Ag + , Pb 2+ , and Cu 2+ suit well pseudo-second-order kinetics and Langmuir model, suggesting monolayer chemisorption mechanism through M-S linkages. XRD and FTIR studies suggested that adsorbed metals could result as coordinated complexes in LDH interlayer region. More interestingly, LDH structure offers protective space for MoS 4 2- anions to avoid oxidation under ambient environments, as confirmed by XPS studies. These features provide Fe-MoS 4 with enormous capacity, good reusability, and excellent selectivity even in the presence of huge concentration of common cations.

Facile One-pot Transformation of Iron Oxides from Fe2O3 Nanoparticles to Nanostructured Fe3O4@C Core-Shell Composites via Combustion Waves

PubMed Central

Shin, Jungho; Lee, Kang Yeol; Yeo, Taehan; Choi, Wonjoon

2016-01-01

The development of a low-cost, fast, and large-scale process for the synthesis and manipulation of nanostructured metal oxides is essential for incorporating materials with diverse practical applications. Herein, we present a facile one-pot synthesis method using combustion waves that simultaneously achieves fast reduction and direct formation of carbon coating layers on metal oxide nanostructures. Hybrid composites of Fe2O3 nanoparticles and nitrocellulose on the cm scale were fabricated by a wet impregnation process. We demonstrated that self-propagating combustion waves along interfacial boundaries between the surface of the metal oxide and the chemical fuels enabled the release of oxygen from Fe2O3. This accelerated reaction directly transformed Fe2O3 into Fe3O4 nanostructures. The distinctive color change from reddish-brown Fe2O3 to dark-gray Fe3O4 confirmed the transition of oxidation states and the change in the fundamental properties of the material. Furthermore, it simultaneously formed carbon layers of 5–20 nm thickness coating the surfaces of the resulting Fe3O4 nanoparticles, which may aid in maintaining the nanostructures and improving the conductivity of the composites. This newly developed use of combustion waves in hybridized nanostructures may permit the precise manipulation of the chemical compositions of other metal oxide nanostructures, as well as the formation of organic/inorganic hybrid nanostructures. PMID:26902260

Synthesizing Nanomaterials for Energy Applications: Probing Activity as a Function of Composition, Morphology and Purity to Address Key Issues Associated with Fuel Cells and Li-Ion Batteries

NASA Astrophysics Data System (ADS)

Scofield, Megan Elaine

With the growing need to find alternative clean energy sources to fossil fuels, research into developing efficient fuel cells and batteries stands at the forefront of this grand effort. However, before mass commercialization, fundamental key issues need to be addressed. For example, fuel cells are subject to high catalyst costs and poor durability of the underlying carbon support. As a way to alleviate these issues, we have synthesized ultrathin one-dimensional (1D) alloy nanowires to probe the effect of composition, purity, and one-dimensionality upon the observed overall activity, performance, and durability. In terms of chemical composition, crystalline ultrathin PtM alloy nanowires (NWs) ('M' = Fe, Co, Ru, Cu, and Au) were generated and subsequently evaluated for the hydrogen oxidation reaction (HOR). Additionally, ternary-based catalysts were synthesized (PtRuFe) in order to analyze how chemical composition influences CO tolerance as well as methanol oxidation reaction (MOR) and formic acid oxidation reaction (FAOR) activities. In both cases, we utilized a sustainably mild, ambient wet-synthesis method for the fabrication of chemically pure and crystalline systems in order to fabricate ultrathin, homogeneous alloy NWs. Moreover, in these studies, our NW systems exhibit favorable synergistic electronic effects with respect to controls. To address another fundamental issue associated with the durability of fuel cells, we have synthesized various metal oxide and perovskite materials of different sizes and chemical compositions as supports for Pt nanoparticles (NPs). Specifically, we have demonstrated favorable metal support interactions between the Pt NPs and the SrRuO3 NP supports, which lead to increased MOR activity as compared with not only the other metal oxide supports tested but also the commercial Pt NP/C standard. In terms of Li-ion batteries, LiFePO4 materials have become increasingly popular as a cathode material due to the many benefits they possess including thermal stability, durability, low cost, and long life span. However, to broaden the general appeal of this material for practical electrochemical applications, it was useful to develop a relatively mild, reasonably simple synthesis method of this cathode material. We describe a generalizable, 2-step methodology of sustainably synthesizing LiFePO4 by incorporating a template-based, ambient, surfactantless, seedless, U-tube protocol in order to generate size and morphologically tailored, crystalline, phase-pure nanowires. Specifically, we demonstrate for the first time experimentally that the Fe-O3 chemical bond plays an important role in determining the overall conductivity of the material, an assertion which is further supported by recent "first-principles" calculations.

Shock synthesis of quasicrystals with implications for their origin in asteroid collisions.

PubMed

Asimow, Paul D; Lin, Chaney; Bindi, Luca; Ma, Chi; Tschauner, Oliver; Hollister, Lincoln S; Steinhardt, Paul J

2016-06-28

We designed a plate impact shock recovery experiment to simulate the starting materials and shock conditions associated with the only known natural quasicrystals, in the Khatyrka meteorite. At the boundaries among CuAl5, (Mg0.75Fe(2+) 0.25)2SiO4 olivine, and the stainless steel chamber walls, the recovered specimen contains numerous micron-scale grains of a quasicrystalline phase displaying face-centered icosahedral symmetry and low phason strain. The compositional range of the icosahedral phase is Al68-73Fe11-16Cu10-12Cr1-4Ni1-2 and extends toward higher Al/(Cu+Fe) and Fe/Cu ratios than those reported for natural icosahedrite or for any previously known synthetic quasicrystal in the Al-Cu-Fe system. The shock-induced synthesis demonstrated in this experiment reinforces the evidence that natural quasicrystals formed during a shock event but leaves open the question of whether this synthesis pathway is attributable to the expanded thermodynamic stability range of the quasicrystalline phase at high pressure, to a favorable kinetic pathway that exists under shock conditions, or to both thermodynamic and kinetic factors.

Shock synthesis of quasicrystals with implications for their origin in asteroid collisions

NASA Astrophysics Data System (ADS)

Asimow, Paul D.; Lin, Chaney; Bindi, Luca; Ma, Chi; Tschauner, Oliver; Hollister, Lincoln S.; Steinhardt, Paul J.

2016-06-01

We designed a plate impact shock recovery experiment to simulate the starting materials and shock conditions associated with the only known natural quasicrystals, in the Khatyrka meteorite. At the boundaries among CuAl5, (Mg0.75Fe2+0.25)2SiO4 olivine, and the stainless steel chamber walls, the recovered specimen contains numerous micron-scale grains of a quasicrystalline phase displaying face-centered icosahedral symmetry and low phason strain. The compositional range of the icosahedral phase is Al68-73Fe11-16Cu10-12Cr1-4Ni1-2 and extends toward higher Al/(Cu+Fe) and Fe/Cu ratios than those reported for natural icosahedrite or for any previously known synthetic quasicrystal in the Al-Cu-Fe system. The shock-induced synthesis demonstrated in this experiment reinforces the evidence that natural quasicrystals formed during a shock event but leaves open the question of whether this synthesis pathway is attributable to the expanded thermodynamic stability range of the quasicrystalline phase at high pressure, to a favorable kinetic pathway that exists under shock conditions, or to both thermodynamic and kinetic factors.

Extremely High Phosphate Sorption Capacity in Cu-Pb-Zn Mine Tailings.

PubMed

Huang, Longbin; Li, Xiaofang; Nguyen, Tuan A H

2015-01-01

Elevated inorganic phosphate (Pi) concentrations in pore water of amended tailings under direct revegetation may cause toxicity in some native woody species but not native forbs or herb species, all of which are key constituents in target native plant communities for phytostabilizing base metal mine tailings. As a result, Pi sorption capacity has been quantified by a conventional batch procedure in three types of base metal mine tailings sampled from two copper (Cu)-lead (Pb)-zinc (Zn) mines, as the basis for Pi-fertiliser addition. It was found that the Pi-sorption capacity in the tailings and local soil was extremely high, far higher than highly weathered agricultural soils in literature, but similar to those of volcanic ash soils. The Langmuir P-sorption maximum was up to 7.72, 4.12, 4.02 and 3.62 mg P g-1 tailings, in the fresh tailings of mixed Cu-Pb-Zn streams (MIMTD7), the weathered tailings of mixed Cu-Pb-Zn streams (MIMTD5), EHM-TD (fresh Cu-stream, high magnetite content) and local soil (weathered shale and schist), respectively. Physicochemical factors highly correlated with the high Pi-sorption in the tailings were fine particle distribution, oxalate and dithionite-citrate-bicarbonate extractable Fe (FeO and Fed), oxalate-extractable Al and Mn, and the levels of soluble Cd and Zn, and total S and Fe. Large amounts of amorphous Fe oxides and oxyhydroxides may have been formed from the oxidation of pyritic materials and redox cycles of Fe-minerals (such as pyrite (FeS2), ankerite (Ca(Fe Mg)(CO3)2 and siderite (FeCO3), as indicated by the extractable FeO values. The likely formation of sparingly soluble Zn-phosphate in the Pb-Zn tailings containing high levels of Zn (from sphalerite ((Zn,Fe)S, ZnS, (Zn,Cd)S)) may substantially lower soluble Zn levels in the tailings through high rates of Pi-fertiliser addition. As a result, the possibility of P-toxicity in native plant species caused by the addition of soluble phosphate fertilizers would be minimal.

Extremely High Phosphate Sorption Capacity in Cu-Pb-Zn Mine Tailings

PubMed Central

Huang, Longbin; Li, Xiaofang; Nguyen, Tuan A. H.

2015-01-01

Elevated inorganic phosphate (Pi) concentrations in pore water of amended tailings under direct revegetation may cause toxicity in some native woody species but not native forbs or herb species, all of which are key constituents in target native plant communities for phytostabilizing base metal mine tailings. As a result, Pi sorption capacity has been quantified by a conventional batch procedure in three types of base metal mine tailings sampled from two copper (Cu)-lead (Pb)-zinc (Zn) mines, as the basis for Pi-fertiliser addition. It was found that the Pi-sorption capacity in the tailings and local soil was extremely high, far higher than highly weathered agricultural soils in literature, but similar to those of volcanic ash soils. The Langmuir P-sorption maximum was up to 7.72, 4.12, 4.02 and 3.62 mg P g-1 tailings, in the fresh tailings of mixed Cu-Pb-Zn streams (MIMTD7), the weathered tailings of mixed Cu-Pb-Zn streams (MIMTD5), EHM-TD (fresh Cu-stream, high magnetite content) and local soil (weathered shale and schist), respectively. Physicochemical factors highly correlated with the high Pi-sorption in the tailings were fine particle distribution, oxalate and dithionite-citrate-bicarbonate extractable Fe (FeO and Fed), oxalate-extractable Al and Mn, and the levels of soluble Cd and Zn, and total S and Fe. Large amounts of amorphous Fe oxides and oxyhydroxides may have been formed from the oxidation of pyritic materials and redox cycles of Fe-minerals (such as pyrite (FeS2), ankerite (Ca(Fe Mg)(CO3)2 and siderite (FeCO3), as indicated by the extractable FeO values. The likely formation of sparingly soluble Zn-phosphate in the Pb-Zn tailings containing high levels of Zn (from sphalerite ((Zn,Fe)S, ZnS, (Zn,Cd)S)) may substantially lower soluble Zn levels in the tailings through high rates of Pi-fertiliser addition. As a result, the possibility of P-toxicity in native plant species caused by the addition of soluble phosphate fertilizers would be minimal. PMID:26295582

Performance of ethanol electro-oxidation on Ni-Cu alloy nanowires through composition modulation.

PubMed

Tian, Xi-Ke; Zhao, Xiao-Yu; Zhang, Li-de; Yang, Chao; Pi, Zhen-Bang; Zhang, Su-Xin

2008-05-28

To reduce the cost of the catalyst for direct ethanol fuel cells and improve its catalytic activity, highly ordered Ni-Cu alloy nanowire arrays have been fabricated successfully by differential pulse current electro-deposition into the pores of a porous anodic alumina membrane (AAMs). The energy dispersion spectrum, scanning and transmission electron microscopy were utilized to characterize the composition and morphology of the Ni-Cu alloy nanowire arrays. The results reveal that the nanowires in the array are uniform, well isolated and parallel to each other. The catalytic activity of the nanowire electrode arrays for ethanol oxidation was tested and the binary alloy nanowire array possesses good catalytic activity for the electro-oxidation of ethanol. The performance of ethanol electro-oxidation was controlled by varying the Cu content in the Ni-Cu alloy and the Ni-Cu alloy nanowire electrode shows much better stability than the pure Ni one.

Pyrite nanoparticles as a Fenton-like reagent for in situ remediation of organic pollutants

PubMed Central

Losa-Adams, Elisabeth; F.-Dávila, Alfonso; Gago-Duport, Luis

2014-01-01

Summary The Fenton reaction is the most widely used advanced oxidation process (AOP) for wastewater treatment. This study reports on the use of pyrite nanoparticles and microparticles as Fenton reagents for the oxidative degradation of copper phthalocyanine (CuPc) as a representative contaminant. Upon oxidative dissolution in water, pyrite (FeS2) particles can generate H2O2 at their surface while simultaneously promoting recycling of Fe3+ into Fe2+ and vice versa. Pyrite nanoparticles were synthesized by the hot injection method. The use of a high concentration of precursors gave individual nanoparticles (diameter: 20 nm) with broader crystallinity at the outer interfaces, providing a greater number of surface defects, which is advantageous for generating H2O2. Batch reactions were run to monitor the kinetics of CuPc degradation in real time and the amount of H2O2. A markedly greater degradation of CuPc was achieved with nanoparticles as compared to microparticles: at low loadings (0.08 mg/L) and 20 h reaction time, the former enabled 60% CuPc removal, whereas the latter enabled only 7% removal. These results confirm that the use of low concentrations of synthetic nanoparticles can be a cost effective alternative to conventional Fenton procedures for use in wastewater treatment, avoiding the potential risks caused by the release of heavy metals upon dissolution of natural pyrites. PMID:24991522

Pyrite nanoparticles as a Fenton-like reagent for in situ remediation of organic pollutants.

PubMed

Gil-Lozano, Carolina; Losa-Adams, Elisabeth; F-Dávila, Alfonso; Gago-Duport, Luis

2014-01-01

The Fenton reaction is the most widely used advanced oxidation process (AOP) for wastewater treatment. This study reports on the use of pyrite nanoparticles and microparticles as Fenton reagents for the oxidative degradation of copper phthalocyanine (CuPc) as a representative contaminant. Upon oxidative dissolution in water, pyrite (FeS2) particles can generate H2O2 at their surface while simultaneously promoting recycling of Fe(3+) into Fe(2+) and vice versa. Pyrite nanoparticles were synthesized by the hot injection method. The use of a high concentration of precursors gave individual nanoparticles (diameter: 20 nm) with broader crystallinity at the outer interfaces, providing a greater number of surface defects, which is advantageous for generating H2O2. Batch reactions were run to monitor the kinetics of CuPc degradation in real time and the amount of H2O2. A markedly greater degradation of CuPc was achieved with nanoparticles as compared to microparticles: at low loadings (0.08 mg/L) and 20 h reaction time, the former enabled 60% CuPc removal, whereas the latter enabled only 7% removal. These results confirm that the use of low concentrations of synthetic nanoparticles can be a cost effective alternative to conventional Fenton procedures for use in wastewater treatment, avoiding the potential risks caused by the release of heavy metals upon dissolution of natural pyrites.

Hemoglobin and Myoglobin as Reducing Agents in Biological Systems. Redox Reactions of Globins with Copper and Iron Salts and Complexes.

PubMed

Postnikova, G B; Shekhovtsova, E A

2016-12-01

In addition to reversible O2 binding, respiratory proteins of the globin family, hemoglobin (Hb) and myoglobin (Mb), participate in redox reactions with various metal complexes, including biologically significant ones, such as those of copper and iron. HbO 2 and MbO 2 are present in cells in large amounts and, as redox agents, can contribute to maintaining cell redox state and resisting oxidative stress. Divalent copper complexes with high redox potentials (E 0 , 200-600 mV) and high stability constants, such as [Cu(phen) 2 ] 2+ , [Cu(dmphen) 2 ] 2+ , and CuDTA oxidize ferrous heme proteins by the simple outer-sphere electron transfer mechanism through overlapping π-orbitals of the heme and the copper complex. Weaker oxidants, such as Cu2+, CuEDTA, CuNTA, CuCit, CuATP, and CuHis (E 0 ≤ 100-150 mV) react with HbO 2 and MbO 2 through preliminary binding to the protein with substitution of the metal ligands with protein groups and subsequent intramolecular electron transfer in the complex (the site-specific outer-sphere electron transfer mechanism). Oxidation of HbO 2 and MbO 2 by potassium ferricyanide and Fe(3) complexes with NTA, EDTA, CDTA, ATP, 2,3-DPG, citrate, and pyrophosphate PP i proceeds mainly through the simple outer-sphere electron transfer mechanism via the exposed heme edge. According to Marcus theory, the rate of this reaction correlates with the difference in redox potentials of the reagents and their self-exchange rates. For charged reagents, the reaction may be preceded by their nonspecific binding to the protein due to electrostatic interactions. The reactions of LbO 2 with carboxylate Fe complexes, unlike its reactions with ferricyanide, occur via the site-specific outer-sphere electron transfer mechanism, even though the same reagents oxidize structurally similar MbO 2 and cytochrome b 5 via the simple outer-sphere electron transfer mechanism. Of particular biological interest is HbO 2 and MbO 2 transformation into met-forms in the presence of small amounts of metal ions or complexes (catalysis), which, until recently, had been demonstrated only for copper compounds with intermediate redox potentials. The main contribution to the reaction rate comes from copper binding to the "inner" histidines, His97 (0.66 nm from the heme) that forms a hydrogen bond with the heme propionate COO - group, and the distal His64. The affinity of both histidines for copper is much lower than that of the surface histidines residues, and they are inaccessible for modification with chemical reagents. However, it was found recently that the high-potential Fe(3) complex, potassium ferricyanide (400 mV), at a 5 to 20% of molar protein concentration can be an efficient catalyst of MbO 2 oxidation into metMb. The catalytic process includes binding of ferrocyanide anion in the region of the His119 residue due to the presence there of a large positive local electrostatic potential and existence of a "pocket" formed by Lys16, Ala19, Asp20, and Arg118 that is sufficient to accommodate [Fe(CN) 6 ] 4- . Fast, proton-assisted reoxidation of the bound ferrocyanide by oxygen (which is required for completion of the catalytic cycle), unlike slow [Fe(CN) 6 ] 4- oxidation in solution, is provided by the optimal location of neighboring protonated His113 and His116, as it occurs in the enzyme active site.

Structural, magnetic and transport properties of 2D structured perovskite oxychalcogenides

NASA Astrophysics Data System (ADS)

Berthebaud, David; Lebedev, Oleg I.; Pelloquin, Denis; Maignan, Antoine

2014-10-01

We have been looking for new potential thermoelectric materials in the family of 2D structured perovskite oxychalcogenides containing [Cu2Ch2]2- blocks (Ch = S or Se). Using high temperature syntheses, a new oxyselenide Sr2CuFeO3Se has been isolated and its structure has been compared to the isotypes sulfides, Ca2CuFeO3S and Sr2CuFeO3S, prepared by the same technique. By combining powder XRD and TEM analyses their composition and structure were analyzed. They all three crystallize in the Sr2CuGaO3S-type structure, with only the oxyselenide showing a Fe deficiency which is related to the stacking faults evidenced by high resolution TEM. Transport and magnetic properties of the samples have been studied; especially their electrical resistivity is characterized by high values in the range from 1 to 10 kΩ cm at 300 K. Thermoelectric potential of these materials is also discussed.

Relationship between the catalytic properties of the products of the oxidative thermolysis of certain complexes and the porous structures of samples in the oxidation reactions of volatile organic compounds

NASA Astrophysics Data System (ADS)

Semushina, Yu. P.; Pechenyuk, S. I.; Kuzmich, L. F.; Knyazeva, A. I.

2017-01-01

The rate of the gas-phase oxidation of ethanol, 2-propanol, acetone, ethyl acetate, dioxane, and benzene with atmospheric oxygen is studied on surfaces of bimetallic oxide catalysts Co-Fe, Cu-Fe, Cr-Co, and Ni-Fe, prepared via thermal decomposition of double complex compounds in air. It is found that the rate of oxidation of volatile compounds depends on the volume of the transient pores in the catalyst sample. The rate of oxidation on the same catalyst at 350°C depends on the nature of the substance in the order: acetone > ethyl acetate > ethanol > propanol > dioxane, benzene.

Fabrication and Analysis of the Wear Properties of Hot-Pressed Al-Si/SiCp + Al-Si-Cu-Mg Metal Matrix Composite

NASA Astrophysics Data System (ADS)

Bang, Jeongil; Oak, Jeong-Jung; Park, Yong Ho

2016-01-01

The aim of this study was to characterize microstructures and mechanical properties of aluminum metal matrix composites (MMC's) prepared by powder metallurgy method. Consolidation of mixed powder with gas atomized Al-Si/SiCp powder and Al-14Si-2.5Cu-0.5Mg powder by hot pressing was classified according to sintering temperature and sintering time. Sintering condition was optimized using tensile properties of sintered specimens. Ultimate tensile strength of the optimized sintered specimen was 228 MPa with an elongation of 5.3% in longitudinal direction. In addition, wear properties and behaviors of the sintered aluminum-based MMC's were analyzed in accordance with vertical load and linear speed. As the linear speed and vertical load of the wear increased, change of the wear behavior occurred in order of oxidation of Al-Si matrix, formation of C-rich layer, Fe-alloying to matrix, and melting of the specimen

Organized one dimensional nanomaterials: From preparations to applications

NASA Astrophysics Data System (ADS)

Wen, Xiaogang

This thesis is mainly concerned with the development of organized one dimensional (1D) nanomaterials and their applications. We have synthesized Ag2S, Cu2S nanowires, Fe2O3 nanobelt and nanowire arrays and ZnO nanobelt arrays from corresponding metal substrate respectively via gas solid reaction methods under different growth conditions. The effect of various parameters including temperature, reaction time, composition of gas, surface pre-oxidation, size of source materials etc. on the growth of metal oxide/sulfide 1D nanostructure have been studied systemically. The size and morphology of these 1D nanomaterials could be rationally controlled by adjusting the growth conditions. A tip growth mechanism has been confirmed based our results. The properties including PL, Raman, field effect transistors, and field emission of these materials have been measured. Cu(OH)2 nanoribbons have been synthesized by a solution solid reaction method using Cu and Cu2S nanowires as precursors. Cu(OH) 2 nanoribbons can form well-aligned arrays on Cu substrate. Low temperature facilitate the formation of Cu(OH)2 nanoribbon arrays. Reaction conditions affect the morphology, crystal structure, even composition of the products much. CuO nanorod arrays of several nm in diameter could be synthesis in changed condition. Cu(OH)2 nanoribbon arrays are good sacrifice template for synthesizing other Cu-based 1D nanomaterials. It has been converted to CuO, Cu2O, Cu8S9, Cu etc. 1D nanostructure through different physical and chemical reaction process. Au/Cu2S core/sheath nanowires have been synthesized in solution phase via a simple template-induced redox deposition process, after removing the Cu2S template, Au nanotubes have been formed. The photoelectrochemistry (PEC) properties of it have been studied. Ag dendritic nanostructures have been prepared via solution reaction. We have revealed that the stem, branch, and sub-branch grow along <100>, <111> and <100> directions, respectively. Such a preferential growth pattern along <100> and <111> alternately lead to the formation of the Ag nanodendrites. In another development, we have synthesized unltrathin Zn nanowires (<5nm) by a vapor transport method. Small molecules are induced into the gas phase as capping reagents. In this process, the small molecules serve as capping reagents or templates to confine the lateral growth and facilitate the formation of ultrathin 1D nanostructures. (Abstract shortened by UMI.)

Anomalous fast diffusion in Cu-NiFe nanolaminates.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jankowski, Alan F.

2017-09-01

For this work, the decomposition of the one-dimensional composition wave in Cu-NiFe nanolaminate structures is examined using x-ray diffraction to assess the kinetics of phase decomposition. The anomalously high diffusivity value found for long-term aging at room temperature is attributed to the inherent nanostructure that features paths for short-circuit diffusion in nanolaminates as attributed to interlayer grain boundaries.

The Chemical Composition of the Galactic Bulge and Implications for its Evolution

NASA Astrophysics Data System (ADS)

McWilliam, Andrew

2016-08-01

At a bulge latitude of b = -4°, the average [Fe/H] and [Mg/H] values are +0.06 and +0.17 dex, roughly 0.2 and 0.7 dex higher than the local thin and thick disk values, respectively, suggesting a large bulge effective yield, perhaps due to efficient retention of supernova ejecta. The bulge vertical [Fe/H] gradient, at ∼0.5 dex/kpc, appears to be due to a changing mixture of sub-populations (near +0.3 dex and -0.3 dex and one possibly near -0.7 dex) with latitude. At solar [Fe/H], the bulge [Al/Fe] and [α/Fe] ratios are ∼ +0.15 dex. Below [Fe/H] ∼ -0.5 dex, the bulge and local thick disk compositions are very similar; but the measured [Mg/Fe], [/Fe], [La/Eu] and dramatic [Cu/Fe] ratios suggest higher SFR in the bulge. However, these composition differences with the thick disk could be due to measurement errors and non-LTE effects. Unusual zig-zag trends of [Cu/Fe] and [Na/Fe] suggest metallicity-dependent nucleosynthesis by core-collapse supernovae in the Type Ia supernova time-delay scenario. The bulge sub-population compositions resemble the local thin and thick disks, but at higher [Fe/H], suggesting a radial [Fe/H] gradient of -0.04 to -0.05 dex/kpc for both the thin and thick disks. If the bulge formed through accretion of inner thin and thick disk stars, it appears that these stars retained vertical scale heights characteristic of their kinematic origin, resulting in the vertical [Fe/H] gradient and [α/Fe] trends seen today.

Oxidized nanocrystalline Fe-Cu pseudoalloy subjected to high pressure and electrodischarge pulses: Mössbauer and x-ray investigations

NASA Astrophysics Data System (ADS)

Gavriliuk, A. G.; Voitkovsky, V. S.; Sidorov, V. A.; Filonenko, V. P.; Tsiok, O. B.; Khvostantsev, L. G.

1998-05-01

Nanocrystalline Fe15Cu85 pseudoalloy has been subjected to pulsed heating up to 1500 K at high pressure (8 GPa). Two regimes were studied: the direct heating using electrodischarge through the sample and indirect heating with the use of cylindrical heater around the sample. The temperature and time conditions in both types of experiments were adjusted to be equivalent. The discharge parameters (stored energy, discharge time, and magnitude of current pulse) were sufficient to move defects by conduction electrons, but insufficient to melt the sample. The properties of treated samples were studied using Mössbauer absorption spectra and x-ray diffraction for three types of samples: (a) primary powder treated by high pressure up to 8 GPa, (b) powder subjected to indirect pulsed heating at 8 GPa, (c) powder treated by electrical pulses at 8 GPa. The x-ray diffraction pattern of primary powder exhibits peaks of copper, iron, and copper oxide (CuO). The Mössbauer spectrum of primary powder exhibits six peaks of alpha iron and some peaks near zero velocity due to the small iron clusters in the copper matrix and ultrafine clusters of paramagnetic phase x-Fe2O3. The transformation of CuO to Cu2O takes place in the course of indirect heating, the Mössbauer spectrum being almost unchanged. The direct electrodischarge heating causes the appearance of new magnetic phase with the magnetic field on iron nucleus 505 kOe, which corresponds to α-Fe2O3. The formation of α-Fe2O3 was confirmed by x-ray diffraction. At the same time the transformation of CuO to Cu2O is incomplete. These experiments demonstrate that high density current pulses, causing the electron wind, can be a useful tool to influence the structure of nanocrystalline powder.

Determination of adsorptive and catalytic properties of copper, silver and iron contain titanium-pillared bentonite for the removal bisphenol A from aqueous solution

NASA Astrophysics Data System (ADS)

Tomul, Fatma; Turgut Basoglu, Funda; Canbay, Hale

2016-01-01

Ti-pillared bentonite, Cu, Ag and Fe modified Ti-pillared bentonite and Cu/Ti- and Fe/Ti-mixed pillared bentonite were synthesized using different titanium sources by direct synthesis or by modification after synthesis. The effects of synthesis conditions on the surface characteristics, pore structure and acidity of the pillared bentonites were investigated by SEM⿿EDS, XPS, XRD, N2-adsorption/desorption and FTIR analyses before and after ammonia adsorption. The results of EDS, XPS and XRD analysis confirmed that titanium, copper, silver and iron were incorporated into the bentonite structure. In the XRD patterns, the formation of delaminated structure reflecting the non-parallel distribution of the bentonite layers by pillaring with Ti, Cu/Ti and Fe/Ti-pillars was observed. XPS spectra indicated the presence of TiO2, CuO, Ag and Ag2O and Fe2O3 species depending on the source of active metals in the synthesized samples. In the FTIR spectra, an increase in the Bronsted/Lewis peak intensity was observed with the loading of copper and iron, whereas a decrease in Lewis and Bronsted acidities was observed with incorporation of silver. Adsorption studies indicated that the adsorption capacity of the sample synthesized using titanium (IV) propoxide and incorporating iron to the structure by ion exchange (Fe-PTi-PILC) were higher than those in other samples. The adsorption of BPA (bisphenol A) by all tested samples was found to fit the Langmuir isotherm. In the catalytic wet peroxide oxidation (CWPO) over PTi-PILC (prepared by titanium (IV) propoxide), Fe-PTi-PILC and Cu-PTi-PILC (prepared by copper impregnated Ti-pillared bentonite) samples, BPA values close to complete conversion were achieved within 30 min at 25 °C, pH 4 and 5 g/L mcat. CWPO results showed that increasement of pH causes a decrease the rate of oxidation. On the other hand, by the time catalyst and BPA concentration is increased, the rate of oxidation is increased as well.

Comparison of iron and copper doped manganese cobalt spinel oxides as protective coatings for solid oxide fuel cell interconnects

NASA Astrophysics Data System (ADS)

Talic, Belma; Molin, Sebastian; Wiik, Kjell; Hendriksen, Peter Vang; Lein, Hilde Lea

2017-12-01

MnCo2O4, MnCo1.7Cu0.3O4 and MnCo1.7Fe0.3O4 are investigated as coatings for corrosion protection of metallic interconnects in solid oxide fuel cell stacks. Electrophoretic deposition is used to deposit the coatings on Crofer 22 APU alloy. All three coating materials reduce the parabolic oxidation rate in air at 900 °C and 800 °C. At 700 °C there is no significant difference in oxidation rate between coated samples and uncoated pre-oxidized Crofer 22 APU. The cross-scale area specific resistance (ASR) is measured in air at 800 °C using La0.85Sr0.1Mn1.1O3 (LSM) contact plates to simulate the interaction with the cathode in a SOFC stack. All coated samples have three times lower ASR than uncoated Crofer 22 APU after 4370 h aging. The ASR increase with time is lowest with the MnCo2O4 coating, followed by the MnCo1.7Fe0.3O4 and MnCo1.7Cu0.3O4 coatings. LSM plates contacted to uncoated Crofer 22 APU contain significant amounts of Cr after aging, while all three coatings effectively prevent Cr diffusion into the LSM. A complex Cr-rich reaction layer develops at the coating-alloy interface during oxidation. Cu and Fe doping reduce the extent of this reaction layer at 900 °C, while at 800 °C the effect of doping is insignificant.

LIBS spectra of multi-component Al, Fe, Cu alloys and composite materials used for selected elements of armament and munition

NASA Astrophysics Data System (ADS)

Ostrowski, R.; Skrzeczanowski, W.; Rycyk, A.; CzyŻ, K.; Sarzyński, A.; Strzelec, M.; Jach, K.; Świerczyński, R.

2017-10-01

Spectral investigations in the UV-VIS range of selected Al, Cu, and Fe alloys and composite materials were performed using LIBS technique. The investigated objects were typical rifle cartridges, mortars, rocket launchers and samples of different type steel, Cu and Al alloys, as well as composite materials of special chemical composition. Two Nd:YAG lasers were applied: a short 4 ns, 60 mJ Brio Quantel/BigSky laser (1064 nm) and a long pulse 200/400 (up to 1000) µs ({ 2/4 up to 10 J) laser (1064 nm) constructed at the Institute of Optoelectronics MUT. This spectrochemical analysis was possible for Al, Cu, and Fe alloys objects for both lasers, and in case of composites only if the samples were irradiated by short laser pulse since in the experiment with the long pulse, all composite materials spectra, in general, were very similar to each other - they imitated a grey/black body spectra. For metal alloys in experiments with a short laser pulse only atomic spectra were observed while for long microsecond laser pulses molecular transitions have been registered for Al alloys. Electron temperatures of plasma created on different materials for short and long laser pulses were found on the base of Boltzmann plots. Temperatures are clearly higher for plasmas generated with a short laser pulse which results from much higher laser power density on the sample surface for short pulse and not from fluence which is 20-40 times larger for long pulse.

Selective synthesis and redox sequence of a heterobimetallic nickel/copper complex of the noninnocent Siamese-twin porphyrin.

PubMed

Blusch, Lina K; Mitevski, Oliver; Martin-Diaconescu, Vlad; Pröpper, Kevin; DeBeer, Serena; Dechert, Sebastian; Meyer, Franc

2014-08-04

The Siamese-twin porphyrin (1H4) is a redox noninnocent pyrazole-expanded porphyrin with two equivalent dibasic {N4} binding sites. It is now shown that its selective monometalation can be achieved to give the nickel(II) complex 1H2Ni with the second {N4} site devoid of a metal ion. This intermediate is then cleanly converted to 1Ni2 and to the first heterobimetallic Siamese-twin porphyrin 1CuNi. Structural characterization of 1H2Ni shows that it has the same helical structure previously seen for 1Cu2, 1Ni2, and free base 1H6(2+). Titration experiments suggest that the metal-devoid pocket of 1H2Ni can accommodate two additional protons, giving [1H4Ni](2+). Both bimetallic complexes 1Ni2 and 1CuNi feature rich redox chemistry, similar to the recently reported 1Cu2, including two chemically reversible oxidations at moderate potentials between -0.3 and +0.5 V (vs Cp2Fe/Cp2Fe(+)). The locus of these oxidations, in singly oxidized [1Ni2](+) and [1CuNi](+) as well as twice oxidized [1CuNi](2+), has been experimentally derived from comparison of the electrochemical properties of the complete series of complexes 1Cu2, 1Ni2, and 1CuNi, and from electron paramagnetic resonance (EPR) spectroscopy and X-ray absorption spectroscopy (XAS) (Ni and Cu K edges). All redox events are largely ligand-based, and in heterobimetallic 1CuNi, the first oxidation takes place within its Cu-subunit, while the second oxidation then occurs in its Ni-subunit. Adding pyridine to solutions of [1Ni2](+) and [1CuNi](2+) cleanly converts them to metal-oxidized redox isomers with axial EPR spectra typical for Ni(III) having significant dz(2)(1) character, reflecting close similarity with nickel complexes of common porphyrins. The possibility of selectively synthesizing heterobimetallic complexes 1MNi from a symmetric binucleating ligand scaffold, with the unusual situation of three distinct contiguous redox sites (M, Ni, and the porphyrin-like ligand), further expands the Siamese-twin porphyrin's potential to serve as an adjustable platform for multielectron redox processes in chemical catalysis and in electronic applications.

Magnetic analysis of a melt-spun Fe-dilute Cu60Ag35Fe5 alloy

NASA Astrophysics Data System (ADS)

Kondo, Shin-ichiro; Kaneko, Kazuhiro; Morimura, Takao; Nakashima, Hiromichi; Kobayashi, Shin-Taro; Michioka, Chishiro; Yoshimura, Kazuyoshi

2015-04-01

The magnetic properties of a melt-spun Fe-dilute Cu60Ag35Fe5 alloy are examined by X-ray diffraction, magnetic measurements, and transmission electron microscopy (TEM). The X-ray diffraction patterns show that the as-spun and annealed (773 K×36 ks) samples contain Cu and Ag phases and no Fe phases; thus, most Fe atoms are dispersed as clusters. Magnetic measurements indicate that the as-spun and annealed samples exhibit superparamagnetic behavior at 300 K, whereas ferromagnetic and superparamagnetic behaviors coexist at 4.2 K. The magnetic moments of small clusters at 300 K are determined by the nonlinear least squares method as 5148 and 4671 μB for as-spun and annealed samples, respectively, whereas those at 300 K are experimentally determined as 3500 and 3200 μB. This decrease in magnetic moments may imply the formation of anti-ferromagnetic coupling by annealing. TEM observation of the melt-spun sample suggests that there are three regions with different compositions: Cu-rich, Ag-rich, and Fe-rich with no precipitation in the matrix. In addition, these regions have obscure interfaces. The magnetic clusters are attributed to the Fe-rich regions.

Colloidal Synthesis and Thermoelectric Properties of CuFeSe2 Nanocrystals

PubMed Central

Zhang, Bing-Qian; Zuo, Yong; Chen, Jing-Shuai; Niu, He-Lin; Mao, Chang-Jie

2017-01-01

Copper-based chalcogenides that contain abundant, low-cost and environmentally-friendly elements, are excellent materials for numerous energy conversion applications, such as photocatalysis, photovoltaics, photoelectricity and thermoelectrics (TE). Here, we present a high-yield and upscalable colloidal synthesis route for the production of monodisperse ternary I-III-VI2 chalcogenides nanocrystals (NCs), particularly stannite CuFeSe2, with uniform shape and narrow size distributions by using selenium powder as the anion precursor and CuCl2·2H2O and FeCl3 as the cationic precursors. The composition, the state of valence, size and morphology of the CuFeSe2 materials were examined by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), transmission electron microscope (TEM) and high resolution transmission electron microscope (HRTEM), respectively. Furthermore, the TE properties characterization of these dense nanomaterials compacted from monodisperse CuFeSe2 NCs by hot press at 623 K were preliminarily studied after ligand removal by means of hydrazine and hexane solution. The TE performances of the sintered CuFeSe2 pellets were characterized in the temperature range from room temperature to 653 K. Finally, the dimensionless TE figure of merit (ZT) of this Earth-abundant and intrinsic p-type CuFeSe2 NCs is significantly increased to 0.22 at 653 K in this work, which is demonstrated to show a promising TE materialand makes it a possible p-type candidate for medium-temperature TE applications. PMID:29278381

Magmatic sulphides in Quaternary Ecuadorian arc magmas

NASA Astrophysics Data System (ADS)

Georgatou, Ariadni; Chiaradia, Massimo; Rezeau, Hervé; Wälle, Markus

2018-01-01

New petrographic and geochemical data on magmatic sulphide inclusions (MSIs) are presented and discussed for 15 Quaternary volcanic centers of the Ecuadorian frontal, main and back volcanic arc. MSIs occur mostly in Fe-Ti oxides (magnetite and/or magnetite-ilmenite pair) and to a lesser extent in silicate minerals (amphibole, plagioclase, and pyroxene). MSIs are present in all volcanic centers ranging in composition from basalt to dacite (SiO2 = 50-67 wt.%), indicating that sulphide saturation occurs at various stages of magmatic evolution and independently from the volcano location along the volcanic arc. MSIs also occur in dioritic, gabbroic and hornblenditic magmatic enclaves of the volcanic rocks. MSIs display variable sizes (1-30 μm) and shapes (globular, ellipsoidal, angular, irregular) and occur mostly as polymineralic inclusions composed of Fe-rich and Cu-poor (pyrrhotite) and Cu-rich (mostly chalcopyrite) phases. Aerial sulphide relative abundances range from 0.3 to 7 ppm in volcanic host rocks and from 13 to 24 ppm in magmatic enclaves. Electron microprobe analyses of MSIs indicate maximum metal contents of Cu = 65.7 wt.%, Fe = 65.2 wt.%, Ni = 10.1 wt.% for those hosted in the volcanic rocks and of Cu = 57.7 wt.%, Fe = 60.9 wt.%, Ni = 5.1 wt.%, for those hosted in magmatic enclaves. Relationships of the sulphide chemistry to the host whole rock chemistry show that with magmatic differentiation (e.g., increasing SiO2) the Cu and Ni content of sulphides decrease whereas the Fe and S contents increase. The opposite behavior is observed with the increase of Cu in the whole rock, because the latter is anti-correlated with the SiO2 whole rock content. Laser ablation ICP-MS analyses of MSIs returned maximum values of PGEs and noble metals of Pd = 30 ppm, Rh = 8.1 ppm, Ag = 92.8 ppm and Au = 0.6 ppm and Pd = 43 ppm, Rh = 22.6 ppm, Ag = 89 ppm and Au = 1 ppm for those hosted in volcanic rocks and magmatic enclaves, respectively. These PGE contents display a different range of values with respect to those in previously investigated magmatic sulphides. MSIs that are Cu- and PGE/Cu-rich are found in less evolved rocks (i.e., lower SiO2 contents) that also display a lower amount of sulphide inclusions. Cu-rich sulphide phases (chalcopyrite ± bornite) are mostly hosted by magnetite, whereas PGE-rich ones consist of a Cu-poor phase (pyrrhotite) hosted by plagioclase. However, no systematic changes in the chemistry of the host silicate mineral are observed in coincidence with the occurrence of MSIs. We use the results of our study to draw some implications on Cu (and other chalcophile elements) behavior during arc magmatic processes potentially associated with the formation of porphyry-type deposits.

Ni, Cu, Au, and platinum-group element contents of sulphides associated with intraplate magmatism: A synthesis

USGS Publications Warehouse

Barnes, S.-J.; Zientek, M.L.; Severson, M.J.

1997-01-01

The tectonic setting of intraplate magmas, typically a plume intersecting a rift, is ideal for the development of Ni - Cu - platinum-group element-bearing sulphides. The plume transports metal-rich magmas close to the mantle - crust boundary. The interaction of the rift and plume permits rapid transport of the magma into the crust, thus ensuring that no sulphides are lost from the magma en route to the crust. The rift may contain sediments which could provide the sulphur necessary to bring about sulphide saturation in the magmas. The plume provides large volumes of mafic magma; thus any sulphides that form can collect metals from a large volume of magma and consequently the sulphides will be metal rich. The large volume of magma provides sufficient heat to release large quantities of S from the crust, thus providing sufficient S to form a large sulphide deposit. The composition of the sulphides varies on a number of scales: (i) there is a variation between geographic areas, in which sulphides from the Noril'sk - Talnakh area are the richest in metals and those from the Muskox intrusion are poorest in metals; (ii) there is a variation between textural types of sulphides, in which disseminated sulphides are generally richer in metals than the associated massive and matrix sulphides; and (iii) the massive and matrix sulphides show a much wider range of compositions than the disseminated sulphides, and on the basis of their Ni/Cu ratio the massive and matrix sulphides can be divided into Cu rich and Fe rich. The Cu-rich sulphides are also enriched in Pt, Pd, and Au; in contrast, the Fe-rich sulphides are enriched in Fe, Os, Ir, Ru, and Rh. Nickel concentrations are similar in both. Differences in the composition between the sulphides from different areas may be attributed to a combination of differences in composition of the silicate magma from which the sulphides segregated and differences in the ratio of silicate to sulphide liquid (R factors). The higher metal content of the disseminated sulphides relative to the massive and matrix sulphides may be due to the fact that the disseminated sulphides equilibrated with a larger volume of magma than massive and matrix sulphides. The difference in composition between the Cu- and Fe-rich sulphides may be the result of the fractional crystallization of monosulphide solid solution from a sulphide liquid, with the Cu-rich sulphides representing the liquid and the Fe-rich sulphides representing the cumulate.

Cu@Fe3O4 core-shell nanoparticle-catalyzed oxidative degradation of the antibiotic oxytetracycline in pre-treated landfill leachate.

PubMed

Pham, Van Luan; Kim, Do-Gun; Ko, Seok-Oh

2018-01-01

Novel Cu@Fe 3 O 4 core-shell nanoparticles prepared via a simple reduction method were evaluated for degradation of oxytetracycline (OTC) in pre-treated leachate (L p-TREA ) (leachate treated by conventional methods). Changes in the characteristics of dissolved organic matter (DOM) in the leachate were also investigated to gain a better understanding of the effects of DOM on the performance of Cu@Fe 3 O 4 . An excellent OTC degradation of >99% was achieved within 30 min under conditions of 1 g/L Cu@Fe 3 O 4 , 20 mg/L OTC, 20 mM H 2 O 2 , and initial pH 3.0, which was similar to the efficiency obtained in deionized water (90% even at pH 9.05). Humic acid (HA) and fulvic acid (FA) were completely degraded at initial pH 3, while aromatic protein (AP) with 32.7% of 1-3 kDa constituents were totally transformed to 0.5-1 kDa compounds, and 17% < 0.5 kDa material was degraded. The OTC removal rate decreased gradually as Cu@Fe 3 O 4 was repeatedly used, but it was significantly enhanced when Cu@Fe 3 O 4 was washed after five uses to remove the organic matter on its surface. The results suggest that Cu@Fe 3 O 4 is a promising and effective catalyst for pharmaceutical and personal care product degradation in landfill leachates. Copyright © 2017 Elsevier Ltd. All rights reserved.

TEMPO-oxidized cellulose hydrogel as a high-capacity and reusable heavy metal ion adsorbent.

PubMed

Isobe, Noriyuki; Chen, Xiaoxia; Kim, Ung-Jin; Kimura, Satoshi; Wada, Masahisa; Saito, Tsuguyuki; Isogai, Akira

2013-09-15

Nitroxy radical catalyzed oxidation with hypochlorite/bromide (TEMPO-mediated oxidation) was performed on a cellulose hydrogel prepared using LiOH/urea solvent. TEMPO oxidation successfully introduced carboxyl groups onto the surface of the cellulose hydrogel with retention of the gel structure and its nanoporous property. The equilibrium measurement of Cu(2+) adsorption showed favorable interaction with Cu(2+) and high maximum adsorption capacity. In addition, over 98% of the adsorbed Cu(2+) was recovered using acid treatment, and the subsequent washing allowed the TEMPO-oxidized gels to be used repeatedly. Furthermore, the TEMPO-oxidized cellulose hydrogel showed high adsorption capacity for other toxic metal ions such as Zn(2+), Fe(3+), Cd(2+), and Cs(+). Copyright © 2013 Elsevier B.V. All rights reserved.

High heating rate decomposition dynamics of copper oxide by nanocalorimetry-coupled time-of-flight mass spectrometry

NASA Astrophysics Data System (ADS)

Yi, Feng; DeLisio, Jeffery B.; Nguyen, Nam; Zachariah, Michael R.; LaVan, David A.

2017-12-01

The thermodynamics and evolved gases were measured during the rapid decomposition of copper oxide (CuO) thin film at rates exceeding 100,000 K/s. CuO decomposes to release oxygen when heated and serves as an oxidizer in reactive composites and chemical looping combustion. Other instruments have shown either one or two decomposition steps during heating. We have confirmed that CuO decomposes by two steps at both slower and higher heating rates. The decomposition path influences the reaction course in reactive Al/CuO/Al composites, and full understanding is important in designing reactive mixtures and other new reactive materials.

Graphene-copper composite with micro-layered grains and ultrahigh strength

PubMed Central

Wang, Lidong; Yang, Ziyue; Cui, Ye; Wei, Bing; Xu, Shichong; Sheng, Jie; Wang, Miao; Zhu, Yunpeng; Fei, Weidong

2017-01-01

Graphene with ultrahigh intrinsic strength and excellent thermal physical properties has the potential to be used as the reinforcement of many kinds of composites. Here, we show that very high tensile strength can be obtained in the copper matrix composite reinforced by reduced graphene oxide (RGO) when micro-layered structure is achieved. RGO-Cu powder with micro-layered structure is fabricated from the reduction of the micro-layered graphene oxide (GO) and Cu(OH)2 composite sheets, and RGO-Cu composites are sintered by spark plasma sintering process. The tensile strength of the 5 vol.% RGO-Cu composite is as high as 608 MPa, which is more than three times higher than that of the Cu matrix. The apparent strengthening efficiency of RGO in the 2.5 vol.% RGO-Cu composite is as high as 110, even higher than that of carbon nanotube, multilayer graphene, carbon nano fiber and RGO in the copper matrix composites produced by conventional MLM method. The excellent tensile and compressive strengths, high hardness and good electrical conductivity are obtained simultaneously in the RGO-Cu composites. The results shown in the present study provide an effective method to design graphene based composites with layered structure and high performance. PMID:28169306

FeCoNi coated glass fibers in composite sheets for electromagnetic absorption and shielding behaviors

NASA Astrophysics Data System (ADS)

Lee, Joonsik; Jung, Byung Mun; Lee, Sang Bok; Lee, Sang Kwan; Kim, Ki Hyeon

2017-09-01

To evaluate the electromagnetic (EM) absorption and shield of magnetic composite sheet, we prepared the FeCoNi coated glass fibers filled in composite sheet. The FeCoNi was coated by electroless plating on glass fiber as a filler. The coated FeCoNi found that consist of mixtures of bcc and fcc phase. The magnetization and coercivity of coated FeCoNi are about 110 emu/g and 57 Oe, respectively. The permittivity and permeability of the FeCoNi composite sheet were about 21 and 1, respectively. Power absorption increased 95% with the increment of frequency up to 10 GHz. Inter-decoupling of this composite sheet showed maximum 30 dB at around 5.3 GHz, which is comparable to that of a conductive Cu foil. Shielding effectiveness (SE) was measured by using rectangular waveguide method. SE of composite obtained about 37 dB at X-band frequency region.

Diamond and Unusual Minerals Discovered from the Chromitite in Polar Ural: A First Report

NASA Astrophysics Data System (ADS)

Yang, J.; Bai, W.; Fang, Q.; Meng, F.; Chen, S.; Zhang, Z.

2007-12-01

Ultrahigh pressure (UHP) minerals, such as diamond, coesite, and pseudomorphs of octahedral olivine, and as well as about 80 other mineral species have been recovered from podiform chromitites of the Luobusa ophiolite, southern Tibet, and a new mineral, Luobusaite (Fe0.82Si2), has been approved recently by CNMMN. The UHP minerals from Luobusa are controversial because they have not found in situ and because ophiolites are currently believed to form at shallow levels above oceanic spreading centers. More detailed study and experimental work are needed to understand the origin and significance of these unusual minerals and investigations of other ophiolites are needed to determine if such minerals occur elsewhere. For this purpose, we collected about 1500 kg of chromitite from two orebodies in an ultramafic body in the Polar Urals. Thus far, more than 60 different mineral species have been separated from these ores. The most exciting discovery is the common occurrence of diamond, a typical UHP mineral in the Luobusa chromitites. Diamonds from Ural chromitite are clear, colorless, well-developed crystals with octahedral morphology, generally 0.2-0.3 mm in size. Attached with the diamonds and perhaps also occurring as inclusions within them are many minerals as chromite, MnNiCrFe alloy, native Si and Ta, corundum, zircon, feldspar, garnet, moissanite, confirming their natural origin and suggesting a long residence time in the mantle. Other mineral group include: (1) native elements: Cr, W, Ni, Co, Si, Al and Ta; (2) carbides: SiC and WC; (3) alloys: Cr-Fe, Si-Al-Fe, Ni-Cu, Ag-Au, Ag-Sn, Fe-Si, Fe-P, and Ag-Zn-Sn; (4) oxides: NiCrFe, PbSn, REE, rutile and Si- bearing rutile, ilmenite, corundum, chromite, MgO, and SnO2; (5) silicates: kyanite, pseudomorphs of octahedral olivine, zircon, garnet, feldspar, and quartz,; (6) sulfides of Fe, Ni, Cu, Mo, Pb, Ab, AsFe, FeNi, CuZn, and CoFeNi; and (7) iron groups: native Fe, FeO, and Fe2O3. These minerals are very similar in composition and structure to those reported from the Luobusa chromitites. For examples, some spherules of native iron contain spherical inclusions of FeO, exactly like comparable grains in the Luobusa sample.

Structural Changes and Material Transport in Al2O3-Supported Cu/Fe Spinel Particles in a Simulated Chemical Looping Combustion Environment

NASA Astrophysics Data System (ADS)

Nealley, W. H. Harrison; Nakano, Anna; Nakano, Jinichiro; Bennett, James P.

2018-05-01

Alumina-supported Cu/Fe spinel particles were exposed to oxidation/reduction atmospheres at 800°C. Structural changes of the particles subjected to gas cycles between air and 10 vol.% CO-90 vol.% Ar were studied from physical data and real-time images collected using a confocal scanning laser microscope equipped with a heating chamber. Overall particle volume slowly expanded with cycles while surface roughness decreased. Cross-sections of the exposed particles showed segregation of Cu and Fe to the edges of inner grains, which may have acted as oxygen carriers during the exposures. The particles remained whole during the cyclic exposures without any noticeable structural breakdown.

Oxidation and evaporation of sulfur species at atmospheric entry of iron sulfide fine particles

NASA Astrophysics Data System (ADS)

Isobe, H.; Murozono, K.

2017-12-01

Micrometeorites have the most abundant flux in current accumulation of planetary materials to the Earth. Micrometeorites are heated and reacted with upper atmosphere at atmospheric entry. Evaporation of meteoritic materials, especially sulfur species, may have environmental effect at upper atmosphere (e.g. Court and Sephton, 2011; Tomkins et al., 2016). Troilite is typical FeS phase in chondritic meteorites. In this study, quick heating and cooling experiments of FeS reagent particles were carried out with a fine particles free falling apparatus with controlled gas flow (Isobe and Gondo, 2013). Starting material reagent is inhomogeneous mixture of troilite, iron oxide and iron metal. Oxygen fugacity was controlled to FMQ +1.5 log unit. Maximum temperature of the particles was higher than 1400°C for approximately 0.5 seconds. Run products with rounded shape and smooth surface show the particles were completely melted. Chemical compositions of particles analyzed on cross sections are generally well homogenized from inhomogeneous starting materials by complete melting. Molar ratios of Fe in melted regions are close to 0.5, while compositions of S and O are various. Varieties of S and O compositions show various degree of oxidation and evaporation of sulfur. Distribution of compositions of melted regions in Fe-S-O system is plotted in liquidus compositions of FeO and FeS saturated melt. Troilite in micrometeorite is melted and oxidized by atmospheric entry. Compositions of FeS melt in fine spherules are following Fe-S-O phase relations even in a few seconds. Molar ratios of Fe in melt are close to 0.5, while compositions of S and O are various. Varieties of S and O compositions show various degree of oxidation and evaporation of sulfur. Evaporation of sulfur from meteoritic materials in atmospheric entry heating may depend on oxygen fugacity of the upper atmosphere. Sulfur supply from meteoritic materials to atmosphere may be limited on planets with oxygen-free atmosphere.

The Effect of Mo Particles Addition in Ag-Cu-Ti Filler Alloy on Ti(C,N)-Based Cermet/45 Steel-Brazed Joints

NASA Astrophysics Data System (ADS)

He, Hu; Du, Xueming; Huang, Xiaokai; Xu, Weijian; Yao, Zhenhua

2018-05-01

Reliable brazing of Ti(C,N)-based cermet and 45 steel was successfully achieved by using the Mo-particle-reinforced Ag-Cu-Ti composite filler. The effects of Mo content on the interfacial microstructure and mechanical properties of Ti(C,N)-based cermet/45 steel joints were analyzed. The results showed that the joint microstructure was primarily composed of Ni3Ti+Cu3Ti2, Ag(s,s)+Cu(s.s), CuTi+Mo, Ti-based solid solution, and FeTi+Fe2Ti. With the increase in Mo content in filler, the thickness of the Ni3Ti+Cu3Ti2 layer adjacent to the Ti(C,N)-based cermet decreases, while more blocky Ti-Cu intermetallic were observed in the brazing seam. The shear strength of the joint could be significantly improved by adding suitable amounts of Mo into the Ag-Cu-Ti filler, and the peak value of 263 MPa was achieved when the alloys were brazed with Ag-Cu-Ti+8wt.%Mo composite filler at 920 °C for 20 min.

Diffuse flow hydrothermal manganese mineralization along the active Mariana and southern Izu-Bonin arc system, western Pacific

USGS Publications Warehouse

Hein, J.R.; Schulz, M.S.; Dunham, R.E.; Stern, R.J.; Bloomer, S.H.

2008-01-01

Abundant ferromanganese oxides were collected along 1200 km of the active Izu-Bonin-Mariana arc system. Chemical compositions and mineralogy show that samples were collected from two deposit types: Fe-Mn crusts of mixed hydrogenetic/hydrothermal origin and hydrothermal Mn oxide deposits; this paper addresses only the second type. Mn oxides cement volcaniclastic and biogenic sandstone and breccia layers (Mn sandstone) and form discrete dense stratabound layers along bedding planes and within beds (stratabound Mn). The Mn oxide was deposited within coarse-grained sediments from diffuse flow systems where precipitation occurred below the seafloor. Deposits were exposed at the seabed by faulting, mass wasting, and erosion. Scanning electron microscopy and microprobe analyses indicate the presence of both amorphous and crystalline 10 ?? and 7 ?? manganate minerals, the fundamental chemical difference being high water contents in the amorphous Mn oxides. Alternation of amorphous and crystalline laminae occurs in many samples, which likely resulted from initial rapid precipitation of amorphous Mn oxides from waxing pulses of hydrothermal fluids followed by precipitation of slow forming crystallites during waning stages. The chemical composition is characteristic of a hydrothermal origin including strong fractionation between Fe (mean 0.9 wt %) and Mn (mean 48 wt %) for the stratabound Mn, generally low trace metal contents, and very low rare earth element and platinum group element contents. However, Mo, Cd, Zn, Cu, Ni, and Co occur in high concentrations in some samples and may be good indicator elements for proximity to the heat source or to massive sulfide deposits. For the Mn sandstones, Fe (mean-8.4%) and Mn (12.4%) are not significantly fractionated because of high Fe contents in the volcaniclastic material. However, the proportion of hydrothermal Fe (nondetrital Fe) to total Fe is remarkably constant (49-58%) for all the sample groups, regardless of the degree of Mn mineralization. Factor analyses indicate various mixtures of two dominant components: hydrothermal Mn oxide for the stratabound Mn and detrital aluminosilicate for the Mn-cemented sandstone; and two minor components, hydrothermal Fe oxyhydroxide and biocarbonate/biosilica. Our conceptual model shows that Mn mineralization was produced by hydrothermal convection cells within arc volcanoes and sedimentary prisms that occur along, the flanks and within calderas. The main source of hydrothermal fluid was seawater that penetrated through fractures, faults, and permeable volcanic edifices. The fluids were heated by magma, enriched in metals by leaching of basement rocks and sediments, and mixed with magmatic fluids and gases. Dikes and sills may have been another source of heat that drove small-scale circulation within sedimentary prisms. Copyright 2008 by the American Geophysical Union.

Diffuse flow hydrothermal manganese mineralization along the active Mariana and southern Izu-Bonin arc system, western Pacific

NASA Astrophysics Data System (ADS)

Hein, James R.; Schulz, Marjorie S.; Dunham, Rachel E.; Stern, Robert J.; Bloomer, Sherman H.

2008-08-01

Abundant ferromanganese oxides were collected along 1200 km of the active Izu-Bonin-Mariana arc system. Chemical compositions and mineralogy show that samples were collected from two deposit types: Fe-Mn crusts of mixed hydrogenetic/hydrothermal origin and hydrothermal Mn oxide deposits; this paper addresses only the second type. Mn oxides cement volcaniclastic and biogenic sandstone and breccia layers (Mn sandstone) and form discrete dense stratabound layers along bedding planes and within beds (stratabound Mn). The Mn oxide was deposited within coarse-grained sediments from diffuse flow systems where precipitation occurred below the seafloor. Deposits were exposed at the seabed by faulting, mass wasting, and erosion. Scanning electron microscopy and microprobe analyses indicate the presence of both amorphous and crystalline 10 Å and 7 Å manganate minerals, the fundamental chemical difference being high water contents in the amorphous Mn oxides. Alternation of amorphous and crystalline laminae occurs in many samples, which likely resulted from initial rapid precipitation of amorphous Mn oxides from waxing pulses of hydrothermal fluids followed by precipitation of slow forming crystallites during waning stages. The chemical composition is characteristic of a hydrothermal origin including strong fractionation between Fe (mean 0.9 wt %) and Mn (mean 48 wt %) for the stratabound Mn, generally low trace metal contents, and very low rare earth element and platinum group element contents. However, Mo, Cd, Zn, Cu, Ni, and Co occur in high concentrations in some samples and may be good indicator elements for proximity to the heat source or to massive sulfide deposits. For the Mn sandstones, Fe (mean 8.4%) and Mn (12.4%) are not significantly fractionated because of high Fe contents in the volcaniclastic material. However, the proportion of hydrothermal Fe (nondetrital Fe) to total Fe is remarkably constant (49-58%) for all the sample groups, regardless of the degree of Mn mineralization. Factor analyses indicate various mixtures of two dominant components: hydrothermal Mn oxide for the stratabound Mn and detrital aluminosilicate for the Mn-cemented sandstone; and two minor components, hydrothermal Fe oxyhydroxide and biocarbonate/biosilica. Our conceptual model shows that Mn mineralization was produced by hydrothermal convection cells within arc volcanoes and sedimentary prisms that occur along the flanks and within calderas. The main source of hydrothermal fluid was seawater that penetrated through fractures, faults, and permeable volcanic edifices. The fluids were heated by magma, enriched in metals by leaching of basement rocks and sediments, and mixed with magmatic fluids and gases. Dikes and sills may have been another source of heat that drove small-scale circulation within sedimentary prisms.

Magnetoresistance of antiferromagnetic Ir22Mn78-pinned spin filter specular spin valves

NASA Astrophysics Data System (ADS)

Hwang, J. Y.; Kim, M. Y.; Rhee, J. R.; Lee, S. S.; Hwang, D. G.; Yu, S. C.; Lee, H. B.

2004-06-01

Specular spin valves (SSVs) having the spin filter layer (SFL) in contact with the ultrathin free layer of composition Ta3/NiFe2/IrMn7/CoFe1/(NOL1)/CoFe2/Cu1.8/CoFe(tF)/Cu(tSF)/(NOL2)/Ta3.5 (in nm) deposited by magnetron sputtering were studied. For these antiferromagnetic Ir22Mn78-pinned spin filter specular spin valve (SFSSV) films, an optimal magnetoresistance (MR) ratio of 11.9% was obtained when both the free layer thickness (tF) and the SFL thickness (tSF) were 1.5 nm, and a MR ratio higher than 11% was maintained even when tF was reduced to 1.0 nm. This was due to an increase of specular electrons by the nano-oxide layer (NOL) and of current shunting through the SFL. Moreover, the interlayer coupling field (Hint) between the free layer and pinned layer could be explained by considering the RKKY and magnetostatic coupling. The coercivity of the free layer (Hcf) was significantly reduced as compared to traditional spin valves (TSV), and remained as low as 4 Oe when tF varied from 1 to 4 nm. It was found that the SFL made it possible to reduce the free layer thickness and enhance the MR ratio without degrading the soft magnetic property of the free layer.

Anode materials for lithium ion batteries

DOEpatents

Abouimrane, Ali; Amine, Khalil

2017-04-11

An electrochemical device includes a composite material of general Formula (1-x)J-(x)Q wherein: J is a metal carbon alloy of formula Sn.sub.zSi.sub.z'Met.sub.wMet'.sub.w'C.sub.t; Q is a metal oxide of formula A.sub..gamma.M.sub..alpha.M'.sub..alpha.'O.sub..beta.; and wherein: A is Li, Na, or K; M and M' are individually Ge, Mo, Al, Ga, As, Sb, Te, Ti, Ta, Zr, Ca, Mg, Sr, Ba, Li, Na, K, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Nb, Rt, Ru or Cd; Met and Met' are individually Ge, Mo, Al, Ga, As, Sb, Te, Ti, Ta, Zr, Ca, Mg, Sr, Ba, Li, Na, K, V, Cr, Mn, Fe, Co, Ni, Cu, Zn, Nb, Rt, Ru or Cd; 0

Fate of corrosion products released from stainless steel in marine sediments and seawater. Part 2. Sequim Bay clayey silt

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schmidt, R.L.

1982-04-01

This report describes laboratory experiments in which neutron-activated 347 stainless steel specimens were exposed to clayey silt from Sequim Bay, Washington. The properties and trace metal geochemistry of the sediment and the amounts of corrosion products that were released under oxic and reduced conditions and their distribution among different chemical fractions of the sediment are discussed. The distributions of Cr, Mn, Fe, Ni and Cu among different chemical forms in the Sequim Bay sediment show that DTPA removed <10% of extractable Cr, Fe and Mn, approx. 20% of extractable Ni and approx. 30% of extractable Cu. The inorganic fraction (materialmore » soluble in 2.5% acetic acid) accounted for approx. 30% of total extractable Mn and approx. 10% or less of Cr, Fe, Ni and Cu. Major portions of Cr and Cu, and a large amount of Fe were in the organic fraction. Extractable Mn, Fe and Ni were associated with hydrous oxides likely as coatings on the mineral substrate of the sediment. No Co was detectable in any of the extracts. (PSB)« less

Cyclic Oxidation of FeCrAlY/Al2O3 Composites

NASA Technical Reports Server (NTRS)

Nesbitt, James A.; Draper, Susan L.; Barrett, Charles A.

1999-01-01

Three-ply FeCrAlY/Al2O3 composites and FeCrAlY matrix-only samples were cyclically oxidized at 1000 C and 1100 C for up to 1000 1-hr cycles. Fiber ends were exposed at the ends of the composite samples. Following cyclic oxidation, cracks running parallel to and perpendicular to the fibers were observed on the large surface of the composite. In addition, there was evidence of increased scale damage and spallation around the exposed fiber ends, particularly around the middle ply fibers. This damage was more pronounced at the higher temperature. The exposed fiber ends showed cracking between fibers in the outer plies, occasionally with Fe and Cr-rich oxides growing out of the cracks. Large gaps developed at the fiber/matrix interface around many of the fibers, especially those in the outer plies. Oxygen penetrated many of these gaps resulting in significant oxide formation at the fiber/matrix interface far within the composite sample. Around several fibers, the matrix was also internally oxidized showing Al2O3 precipitates in a radial band around the fibers. The results show that these composites have poor cyclic oxidation resistance due to the CTE mismatch and inadequate fiber/matrix bond strength at temperatures of 1000 C and above.

Microwave absorbing performance enhancement of Fe75Si15Al10 composites by selective surface oxidation

NASA Astrophysics Data System (ADS)

Zhang, Nan; Wang, Xin; Liu, Tao; Xie, Jianliang; Deng, Longjiang

2017-09-01

An excessively large dielectric constant is a challenge to improve the performances of the Fe-based absorbing material. Here, we propose a selective surface oxidation method to reduce the permittivity without sacrificing the permeability, by annealing under 5%H2—95%N2 (H2/N2). It is found that a thin layer of aluminum and silicon oxides formed on the surface of Fe75Si15Al10 particles during annealing in the range of 500-780 °C under H2/N2, thereby leading to an obvious decrease of permittivity of the Fe75Si15Al10 composite. According to Gibbs free energy, aluminum and silicon oxides are formed and iron oxides are reduced during annealing under H2/N2 at above 500 °C. Interestingly, the XPS result shows that the atomic ratio of Fe decreases significantly on the particle surface, which infers that the reduced Fe atoms diffuse to the interior of the particles. The surface oxide layer can protect the inner part of the alloy from further oxidation, which contributes to a high permeability. Meanwhile, the XRD result shows the formation of DO3-type ordering, which leads to the promotion of permeability. The two reasons lead to the improvement of permeability of the Fe75Si15Al10 composite after annealing. The composite is confirmed to have high permeability and low permittivity, exhibiting better electromagnetic wave absorption properties.

Catalytic evaluation on liquid phase oxidation of vanillyl alcohol using air and H2O2 over mesoporous Cu-Ti composite oxide

NASA Astrophysics Data System (ADS)

Saha, Subrata; Hamid, Sharifah Bee Abd; Ali, Tammar Hussein

2017-02-01

A mesoporous, highly crystalline Cu-Ti composite oxide catalyst was prepared via facile, simple and modified solution method varying Cu and Ti ratio for selective liquid phase oxidation of vanillyl alcohol. Various spectroscopic procedures were employed to systematically characterize the catalyst structural and physicochemical properties. The defect chemistry of the catalyst was confirmed from the presence of surface defects revealed through HRTEM imagery between the TiO2 (101) and Cu3TiO4 (012) planes, complemented by the XRD profiling. Further, presence of oxygen vacancy evidenced by O 1s XPS spectra were observed on the catalyst surface. Moreover, the stoichiometry of Cu and Ti in the catalyst synthesis protocol was notably found to be the vital determinant to alter the redox properties of Cu-Ti composite oxide catalyst supported by H2-TPR. O2-TPD analysis. Moreover, a rational investigation was done using different oxidants such as air and H2O2 with variables reaction conditions. The catalyst was active for liquid phase oxidation of vanillyl alcohol to vanillin with performance of 66% conversion and 71% selectivity using H2O2 in base free condition. And also, catalytic activity was significantly improved by 94% conversion with 86% selectivity to vanillin in liquid phase aerobic oxidation at the optimum reaction conditions. To expand the superiority of the catalyst, three times reusability study was also examined with appreciable catalytic activity.

High Dielectric Constants of Composites of Fiber-Like Copper Phthalocyanine-Coated Graphene Oxide Embedded in Poly(arylene Ether Nitriles)

NASA Astrophysics Data System (ADS)

Li, Jingwei; Pu, Zejun; Wang, Zicheng; Long, Ya; Jia, Kun; Liu, Xiaobo

2015-07-01

The surfaces of graphene oxide (GO) sheets were coated with fiber-like copper phthalocyanine (CuPc) by use of a solvothermal process. The product, GO@ CuPc, was used as a filler in high-performance poly(arylene ether nitrile) (PEN) composites. Films of the composites had high thermal stability, and glass-transition temperatures in the range 170-182°C. Thermogravimetric analysis revealed their initial decomposition temperatures were in the range 470-483°C. Scanning electron microscopy showed that dispersion of GO@ CuPc in PEN was much better than that of unmodified GO; this can be attributed to relatively strong interaction between GO@CuPc and the PEN matrix. All the composite films were highly flexible and had enhanced mechanical properties. Tensile strengths of the composites were as high as 89 MPa in the presence of 1 wt.% GO@CuPc, an increase of 20% compared with pure PEN film. Dielectric constants of the composite films were as high as 52 at 100 Hz when the GO@CuPc content was 5%. Because of these excellent mechanical and dielectric properties, PEN/GO@CuPc composites have much potential for use as film capacitors.

Influence of the domain structure of nano-oxide layers on the transport properties of specular spin valves

NASA Astrophysics Data System (ADS)

Ventura, J.; Sousa, J. B.; Veloso, A.; Freitas, P. P.

2007-05-01

Specular spin valves show enhanced giant magnetoresistive ratio when compared to other simpler, spin valve structures as a result of specular reflection in nano-oxide layers (NOLs) formed by the partial oxidation of the CoFe pinned and free layers. The oxides forming the NOL were recently shown to order antiferromagnetically below T ˜175K. Here we study the training effect in MnIr /CoFe/NOL/CoFe/Cu/CoFe/NOL specular spin valves at low temperatures (15K). We observed that the training effect is related to the nano-oxide layer antiferromagnet ordering and to the evolution of the corresponding domain structure with the number of cycles performed. This allowed us to study the influence of the NOL domain structure on the magnetotransport of specular spin valves.

Gas-phase fragmentation of coordination compounds: loss of CO(2) from inorganic carbonato complexes to give metal oxide ions

PubMed

Dalgaard; McKenzie

1999-10-01

Using electrospray ionization mass spectrometry, novel transition metal oxide coordination complex ions are proposed as the products of the collision-induced dissociation (CID) of some carbonato complex ions through the loss of a mass equivalent to CO(2). CID spectra of [(tpa)CoCO(3)](+) (tpa = tris(2-pyridylmethyl)methylamine), [(bispicMe(2)en)Fe(&mgr;-O)(&mgr;-CO(3))Fe(bispicMe(2)en)]2+ (bispicMe(2)en = N,N'-dimethyl-N,N'-bis(2-pyridylmethy)eth- ane-1, 2-diamine) and [(bpbp)Cu(2)CO(3)](+) (bpbp(-) = bis[(bis-(2-pyridylmethyl)amino)methyl]-4-tertbutylpheno-lato(1-)), show peaks assigned to the mono- and dinuclear oxide cations, [(tpa)CoO](+), [(bispicMe(2)en)(2)Fe(2)(O)(2)]2+ and [(bpbp)Cu(2)O](+), as the dominant species. These results can be likened to the reverse of typical synthetic reactions in which metal hydroxide compounds react with CO(2) to give metal carbonato compounds. Because of the lack of available protons in the gas phase, novel oxide species rather than the more common hydroxide ions are generated. These oxide ions are relevant to the highly oxidizing species proposed in oxygenation reactions catalysed by metal oxides and metalloenzymes. Copyright 1999 John Wiley & Sons, Ltd.

Characteristics and environmental aspects of slag: a review

USGS Publications Warehouse

Piatak, Nadine M.; Parsons, Michael B.; Seal, Robert R.

2015-01-01

The composition of ferrous slag is dominated by Ca and Si. Steel slag may contain significant Fe, whereas Mg and Al may be significant in Fe slag. Calcium-rich olivine-group silicates, melilite-group silicates that contain Al or Mg, Ca-rich glass, and oxides are the most commonly reported major phases in ferrous slag. Calcite and trace amounts of a variety of sulfides, intermetallic compounds, and pure metals are typically also present. The composition of non-ferrous slag, most commonly from base-metal production, is dominated by Fe and Si with significant but lesser amounts of Al and Ca. Silicates in the olivine, pyroxene, and melilite groups, as well as glass, spinels, and SiO2 (i.e., quartz and other polymorphs) are commonly found in non-ferrous slag. Sulfides and intermetallic compounds are less abundant than the silicates and oxides. The concentrations of some elements exceed generic USEPA soil screening levels for human contact based on multiple exposure pathways; these elements include Al, Cr, Cu, Fe, Mn, Pb, and Zn based on bulk chemical composition. Each slag type usually contains a specific suite of elements that may be of environmental concern. In general, non-ferrous slag may have a higher potential to negatively impact the environment compared to ferrous slag, and is thus a less attractive material for reuse, based on trace element chemistry, principally for base metals. However, the amount of elements released into the environment is not always consistent with bulk chemical composition. Many types of leaching tests have been used to help predict slag’s long-term environmental behavior. Overall, ferrous slags produce an alkaline leachate due to the dissolution of Ca oxides and silicates derived from compounds originally added as fluxing agents, such as lime. Ferrous slag leachate is commonly less metal-rich than leachate from non-ferrous slag generated during base metal extraction; the latter leachate may even be acidic due to the oxidation of sulfides. Because of its characteristics, ferrous slag is commonly used for construction and environmental applications, whereas both non-ferrous and ferrous slag may be reprocessed for secondary metal recovery. Both types of slag have been a source of some environmental contamination. Research into the environmental aspects of slag will continue to be an important topic whether the goal is its reuse, recycling, or remediation.

Catalyzed and Electrocatalyzed Oxidation of l-Tyrosine and l-Phenylalanine to Dopachrome by Nanozymes.

PubMed

Hou, Jianwen; Vázquez-González, Margarita; Fadeev, Michael; Liu, Xia; Lavi, Ronit; Willner, Itamar

2018-06-13

Catalyzed oxygen insertion into C-H bonds represents a continuous challenge in chemistry. Particularly, driving this process at ambient temperature and aqueous media represents a "holy grail" in catalysis. We report on the catalyzed cascade transformations of l-tyrosine or l-phenylalanine to dopachrome in the presence of l-ascorbic acid/H 2 O 2 as oxidizing mixture and CuFe-Prussian Blue-like nanoparticles, Fe 3 O 4 nanoparticles or Au nanoparticles as catalysts. The process involves the primary transformation of l-tyrosine to l-DOPA that is further oxidized to dopachrome. The transformation of l-phenylalanine to dopachrome in the presence of CuFe-Prussian Blue-like nanoparticles and l-ascorbic acid/H 2 O 2 involves in the first step the formation of l-tyrosine and, subsequently, the operation of the catalytic oxidation cascade of l-tyrosine to l-DOPA and dopachrome. Electron spin resonance experiments demonstrate that ascorbate radicals and hydroxyl radicals play cooperative functions in driving the different oxygen-insertion processes. In addition, the aerobic elecrocatalyzed oxidation of l-tyrosine to dopachrome in the presence of naphthoquinone-modified Fe 3 O 4 nanoparticles and l-ascorbic acid is demonstrated. In this system, magnetic-field attraction of the naphthoquinone-modified Fe 3 O 4 nanoparticles onto the electrode allows the quinone-mediated electrocatalyzed reduction of O 2 to H 2 O 2 (bias potential -0.5 V vs SCE). The electrogenerated H 2 O 2 is then utilized to promote the transformation of l-tyrosine to dopachrome in the presence of l-ascorbic acid and Fe 3 O 4 catalyst.

Coordinatively Unsaturated Metal-Organic Frameworks M3(btc)2 (M = Cr, Fe, Co, Ni, Cu, and Zn) Catalyzing the Oxidation of CO by N2O: Insight from DFT Calculations.

PubMed

Ketrat, Sombat; Maihom, Thana; Wannakao, Sippakorn; Probst, Michael; Nokbin, Somkiat; Limtrakul, Jumras

2017-11-20

The oxidation of CO by N 2 O over metal-organic framework (MOF) M 3 (btc) 2 (M = Fe, Cr, Co, Ni, Cu, and Zn) catalysts that contain coordinatively unsaturated sites has been investigated by means of density functional theory calculations. The reaction proceeds in two steps. First, the N-O bond of N 2 O is broken to form a metal oxo intermediate. Second, a CO molecule reacts with the oxygen atom of the metal oxo site, forming one C-O bond of CO 2 . The first step is a rate-determining step for both Cu 3 (btc) 2 and Fe 3 (btc) 2 , where it requires the highest activation energy (67.3 and 19.6 kcal/mol, respectively). The lower value for the iron compound compared to the copper one can be explained by the larger amount of electron density transferred from the catalytic site to the antibonding of N 2 O molecules. This, in turn, is due to the smaller gap between the highest occupied molecular orbital (HOMO) of the MOF and the lowest unoccupied molecular orbital (LUMO)  of N 2 O for Fe 3 (btc) 2 compared to Cu 3 (btc) 2 . The results indicate the important role of charge transfer for the N-O bond breaking in N 2 O. We computationally screened other MOF M 3 (btc) 2 (M = Cr, Fe, Co, Ni, Cu, and Zn) compounds in this respect and show some relationships between the activation energy and orbital properties like HOMO energies and the spin densities of the metals at the active sites of the MOFs.

An assessment of the accuracy of stable Fe isotope ratio measurements on samples with organic and inorganic matrices by high-resolution multicollector ICP-MS

NASA Astrophysics Data System (ADS)

Schoenberg, Ronny; von Blanckenburg, Friedhelm

2005-04-01

Multicollector ICP-MS-based stable isotope procedures provide the capability to determine small variations in metal isotope composition of materials, but they are prone to substantial bias introduced by inadequate sample preparation. Such a "cryptic" bias is not necessarily identifiable from the measured isotope ratios. The analytical protocol for Fe isotope analyses of organic and inorganic materials described here identifies and avoids such pitfalls. In medium-mass resolution mode of the ThermoFinnigan Neptune MC-ICP-MS, a 1-ppm Fe solution with an uptake rate of 50-70 [mu]L min-1 yielded 3 × 10-11 A on 56Fe for the ThermoFinnigan stable introduction system and 1.2-1.8 × 10-10 A for the ESI Apex-Q uptake system. Sensitivity was increased again 3-5-fold when using Finnigan X-cones instead of the standard H-cones. The combination of the ESI Apex-Q apparatus and X-cones allowed the determination of the isotope composition on as little as 50 ng of Fe. Fe isotope compositions were corrected for mass bias with both the standard-sample bracketing (SSB) method, and by using the 65Cu/63Cu ratio of added synthetic copper (Cu-doping) as internal monitor of mass discrimination. Both methods provide identical results on high-purity Fe solutions of either synthetic or natural samples. We prefer the SSB method because of its shorter analysis time and more straightforward correction of instrumental mass bias compared to Cu-doping. Strong error correlations of the data are observed in three isotope diagrams. Thus, we suggest that the quality assessment in such diagrams should be performed with error ellipses rather than error bars. Reproducibility of [delta]56Fe, [delta]57Fe and [delta]58Fe values of natural samples alone is not a sufficient criterion for accuracy. A set of tests is lined out that identify cryptic matrix effects and ensure a reproducible level of quality control. Using these criteria and the SSB correction method, we determined the external reproducibilities for [delta]56Fe, [delta]57Fe and [delta]58Fe at the 95% confidence interval from 318 measurements of 95 natural samples to be 0.049, 0.071 and 0.28[per mille sign], respectively.

Synthesis of hierarchically porous perovskite-carbon aerogel composite catalysts for the rapid degradation of fuchsin basic under microwave irradiation and an insight into probable catalytic mechanism

NASA Astrophysics Data System (ADS)

Wang, Yin; Wang, Jiayuan; Du, Baobao; Wang, Yun; Xiong, Yang; Yang, Yiqiong; Zhang, Xiaodong

2018-05-01

3D hierarchically porous perovskites LaFe0.5M0.5O3-CA (M = Mn, Cu) were synthesized by a two-step method using PMMA as template and supporting with carbon aerogel, which were characterized with SEM, TEM, XRD, XPS and FT-IR spectroscopy. The as-prepared composites were used in microwave (MW) catalytic degradation of fuchsin basic (FB) dye wastewater. Batch experiment results showed that the catalytic degradation of FB could be remarkably improved by coating with CA. And LaFe0.5Cu0.5O3-CA exhibited higher catalytic performance than LaFe0.5Mn0.5O3-CA, which had a close connection with the activity of substitution metal ion in B site of the catalysts. The FB removal fit pseudo-first-order model and the degradation rate constant increased with initial pH value and MW powder while decreases with initial FB concentration. All catalysts presented favorable recycling and stability in the repeated experiment. Radical scavenger measurements indicated that hydroxyl radicals rather than surface peroxide and hole played an important role in the catalytic process, and its quantity determined the degradation of FB. Furthermore, both Cu and Fe species were involved in the formation of active species, which were responsible to the excellent performance of the LaFe0.5Cu0.5O3-CA/MW system. Therefore, LaFe0.5Cu0.5O3-CA/MW showed to be a promising technology for the removal of organic pollutants in wastewater treatment applications.

Microwave absorbing properties and enhanced infrared reflectance of Fe/Cu composites prepared by chemical plating

NASA Astrophysics Data System (ADS)

Li, Xiaoguang; Ji, Guangbin; Lv, Hualiang; Wang, Min; Du, Youwei

2014-04-01

Fe/Cu composite samples with Cu particles depositing on carbonyl iron sheets were prepared by chemical plating. Cu additions were uniformly distributed on the grain boundaries of the flaky carbonyl iron while keeping the internal structure of iron. Meanwhile, we found that the chemical plating time made a key point on both the microwave absorbing properties and infrared emissivity. With the growth of chemical plating time, the value of reflection loss gives a linear decrease and the infrared emissivity is reduced with a tendency of index reduction. When the plating time is less than 30 min, the reflection loss of the samples maintains above -20 GHz, moreover, prolonging the plating time more than 30 min, the infrared emissivity of the samples is reduced to 0.50 or less. It can be concluded that both the microwave absorbing and infrared properties are excellent at the optimal plating time of 30 min.

A simple way to prepare reduced graphene oxide nanosheets/Fe2O3-Pd/N-doped carbon nanosheets and their application in catalysis.

PubMed

Yao, Tongjie; Zhang, Junshuai; Zuo, Quan; Wang, Hao; Wu, Jie; Zhang, Xiao; Cui, Tieyu

2016-04-15

The catalysts with Pd and γ-Fe2O3 nanoparticles embedded between reduced graphene oxide nanosheets (rGS) and N-doped carbon nanosheets (NCS) were prepared through a two-step method. Firstly, graphene oxide nanosheets (GS)/prussian blue (PB)-Pd/polypyrrole (PPy) composites were synthesized by using pyrrole monomer as reductant, K3Fe(CN)6 and PdCl2 as oxidants in the presence of GS via a redox reaction. Subsequently, the as-obtained GS/PB-Pd/PPy composites were calcinated in N2 atmosphere. During the heat-treatment, carbonization of PPy to NCS, conversion of nonmagnetic PB to magnetic γ-Fe2O3 nanoparticles, and reduction of GS to rGS were finished, simultaneously. rGS/Fe2O3-Pd/NCS composites exhibited good catalytic activity toward reduction of 4-nitrophenol. The rate constant k and turnover frequency were calculated and compared with recent reports. Owing to γ-Fe2O3 nanoparticles, the rGS/Fe2O3-Pd/NCS composites could be quickly separated by magnet and reused without obvious decrease in activity. Copyright © 2016 Elsevier Inc. All rights reserved.

The Role of Magmatic Volatile Input, Near-surface Seawater Entrainment and Sulfide Deposition in Regulating Metal Concentrations Within Manus Basin Hydrothermal Systems

NASA Astrophysics Data System (ADS)

Craddock, P. R.; Tivey, M. K.; Seewald, J. S.; Rouxel, O.; Bach, W.

2007-12-01

Analyses of Fe, Mn, Cu, Zn, Pb, Ag, Cd, Co and Sb in vent fluid samples from four hydrothermal systems in the Manus back-arc basin, Papua New Guinea, were carried out by ICP-MS. Vienna Woods is located on the well- defined, basalt-dominated Manus Spreading Center, while the other systems are hosted in felsic volcanics on the Pual Ridge (PACMANUS), within a caldera (DESMOS), and on volcanic cones (SuSu Knolls). Metal concentrations were coupled with other fluid data (pH, SO4, Ca, H2S) to discriminate effects of deep- seated water-rock reaction and magmatic volatile input from near surface seawater entrainment, mixing, and consequent mineral precipitation and metal remobilization. Both magmatic volatile input (e.g. SO2, HCl, HF) and sulfide precipitation can increase fluid acidity and thus affect the aqueous mobility of metals. At Vienna Woods, 280°C end-member (Mg = 0) fluids have high pH (>4.2) and low metal contents (Fe <160 uM, Cu <10 uM, Zn <40 uM) relative to most mid-ocean ridge (MOR) vent fluids. The high pH and lack of evidence for magmatic volatile input are consistent with fluid compositions regulated by subsurface seawater- basalt/andesite reactions. Despite low aqueous Zn concentrations, Zn-rich (wurtzite-lined) chimneys are common at Vienna Woods active vents, reflecting deposition from fluids characterized by low Fe and Cu and high pH. At PACMANUS, black smoker fluids (T >300°C, pH ~ 2.7) are enriched in sulfide-forming metals by an order of magnitude relative to Vienna Woods fluids. Enrichments at PACMANUS reflect efficient leaching of metals at low pH, with the lower pH likely a result of input of magmatic volatiles. In addition, some vents fluids show clear evidence for seawater entrainment, subsurface precipitation of Cu-Fe-sulfides and preferential remobilization of Zn-sulfides (lower T, non-zero Mg, lower Fe, Cu, H2S and pH (2.3-2.4), but higher Zn, Pb, Cd and Ag, compared to black smokers). The higher metal concentrations and lower pH of fluids from PACMANUS versus Vienna Woods are reflected in chimney deposit compositions with Zn-poor sulfide linings composed of Cu-Fe-sulfides and As-Sb-sulfosalts in high T and lower T vents, respectively. At DESMOS caldera, fluid data suggest extensive magmatic volatile input (e.g. pH <1.5, elevated F and SO4) but lesser reaction with the basement felsic rocks (low Li, Rb, Mn). Sampled "acid-sulfate" fluids are low temperature (T ~180°C) with Mg >46 mM, and very high concentrations of some metals for these Mg concentrations (Fe >5 mM, Zn >50 - 400 uM). At SuSu Knolls, vent fluid compositions similar to those at both PACMANUS and DESMOS are observed. Smoker fluids have high but variable metal concentrations of similar magnitude to PACMANUS. Acid-sulfate fluids from North Su have low pH (<2), non-zero Mg (>40 mM), and high Fe and Zn concentrations, similar to DESMOS fluids. At SuSu Knolls, fluid compositions reflect either high temperature water-rock reaction (smoker fluids) or magmatic volatile input (acid-sulfate fluids). As at PACMANUS, chimney deposits that correspond to venting fluids are Cu-Fe-As-Sb-rich and Zn-poor, likely reflecting deposition from low pH, high Cu and Fe fluids.

Iron and chlorine as guides to stratiform Cu-Co-Au deposits, Idaho Cobalt Belt, USA

USGS Publications Warehouse

Nash, J.T.; Connor, J.J.

1993-01-01

The Cu-Co-Au deposits of the Idaho Cobalt Belt are in lithostratigraphic zones of the Middle Proterozoic Yellowjacket Formation characterized by distinctive chemical and mineralogical compositions including high concentrations of Fe (15- > 30 wt. percent Fe2O3), Cl (0.1-1.10 wt. percent), and magnetite or biotite (> 50 vol. percent). The Cu-Co-Au deposits of the Blackbird mine are stratabound in Fe-silicate facies rocks that are rich in biotite, Fe, and Cl, but stratigraphically equivalent rocks farther than 10 km from ore deposits have similar compositions. A lower lithostratigraphic zone containing magnetite and small Cu-Co-Au deposits extends for more than 40 km. The Fe-rich strata are probably exhalative units related to mafic volcanism and submarine hot springs, but the origin of the high Cl concentrations is less clear. Former chlorine-rich pore fluids are suggested by the presence of supersaline fluid inclusions, by Cl-rich biotite and scapolite (as much as 1.87 percent Cl in Fe-rich biotite), and by high Cl concentrations in rock samples. Chlorine is enriched in specific strata and in zones characterized by soft-sediment deformation, thus probably was introduced during sedimentation or diagenesis. Unlike some metasedimentary rocks containing scapolite and high Cl, the Yellowjacket Formation lacks evidence for evaporitic strata that could have been a source of Cl. More likely, the Cl reflects a submarine brine that carried Fe, K, and base metals. Strata containing anomalous Fe-K-Cl are considered to be a guide to sub-basins favorable for the occurrence of stratiform base-metal deposits. ?? 1993 Springer-Verlag.

A New CuO-Fe2 O3 -Mesocarbon Microbeads Conversion Anode in a High-Performance Lithium-Ion Battery with a Li1.35 Ni0.48 Fe0.1 Mn1.72 O4 Spinel Cathode.

PubMed

Di Lecce, Daniele; Verrelli, Roberta; Campanella, Daniele; Marangon, Vittorio; Hassoun, Jusef

2017-04-10

A ternary CuO-Fe 2 O 3 -mesocarbon microbeads (MCMB) conversion anode was characterized and combined with a high-voltage Li 1.35 Ni 0.48 Fe 0.1 Mn 1.72 O 4 spinel cathode in a lithium-ion battery of relevant performance in terms of cycling stability and rate capability. The CuO-Fe 2 O 3 -MCMB composite was prepared by using high-energy milling, a low-cost pathway that leads to a crystalline structure and homogeneous submicrometrical morphology as revealed by XRD and electron microscopy. The anode reversibly exchanges lithium ions through the conversion reactions of CuO and Fe 2 O 3 and by insertion into the MCMB carbon. Electrochemical tests, including impedance spectroscopy, revealed a conductive electrode/electrolyte interface that enabled the anode to achieve a reversible capacity value higher than 500 mAh g -1 when cycled at a current of 120 mA g -1 . The remarkable stability of the CuO-Fe 2 O 3 -MCMB electrode and the suitable characteristics in terms of delivered capacity and voltage-profile retention allowed its use in an efficient full lithium-ion cell with a high-voltage Li 1.35 Ni 0.48 Fe 0.1 Mn 1.72 O 4 cathode. The cell had a working voltage of 3.6 V and delivered a capacity of 110 mAh g cathode -1 with a Coulombic efficiency above 99 % after 100 cycles at 148 mA g cathode -1 . This relevant performances, rarely achieved by lithium-ion systems that use the conversion reaction, are the result of an excellent cell balance in terms of negative-to-positive ratio, favored by the anode composition and electrochemical features. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Microfluidic reactor synthesis and photocatalytic behavior of Cu@Cu2O nanocomposite

NASA Astrophysics Data System (ADS)

Xu, Lei; Srinivasakannan, C.; Peng, Jinhui; Yan, Mi; Zhang, Di; Zhang, Libo

2015-03-01

The Cu@Cu2O nanocomposites were synthesized by solution-phase synthesis of Cu nanoparticles in microfluidic reactor at room temperature, followed by controlling the oxidation process. The size, morphology, elemental compositions, and the chemical composition on the surface of Cu@Cu2O nanocomposite were characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS). Experimental results demonstrated that the surface of the Cu nanoparticles was oxidized to Cu2O which serves as the shell of nanoparticle. The amount of Cu2O can be controlled by varying the drying temperature. Additionally the binary Cu@Cu2O nanocomposite along with H2O2 exhibited its potential as an excellent photocatalyst for degradation of methylene blue (MB) under UV irradiation.

Modes of Ignition of Powder Layers of Nanocomposite Thermites by Electrostatic Discharge

NASA Astrophysics Data System (ADS)

Monk, I.; Schoenitz, M.; Dreizin, E. L.

2017-01-01

Nanocomposite powders with aluminum as a fuel and oxides of molybdenum, copper, bismuth, and iron as oxidizers were prepared by arrested reactive milling. The powders were placed in 0.5-mm-thick layers and ignited by electrostatic discharge (ESD) in air. In different tests, time-resolved light emission was recorded at 568 nm or in the range of 373-641 nm. The amount of material consumed was recorded as well. Time-resolved temperatures were determined. Two distinct ignition regimes were observed. Prompt ignition occurred within 10 µs of the electric discharge, comparable to what had previously been observed for corresponding powder monolayers. This ignition mode was observed for composites with Bi2O3 and Fe2O3 ignited with a 12-kV discharge, whereas it only occurred at higher spark voltage (20 kV) and energy for CuO and MoO3 composites. Delayed ignition, occurring after 0.1-1 ms following the discharge, was observed for all composites with consistently stronger light emission. Analysis of quenched, partially burned particles showed that the original nanostructure was preserved after prompt ignition but not after delayed ignition. It is proposed that prompt ignition represents direct ESD initiation of composite particles rapidly and adiabatically preheated to high temperatures while keeping the nanostructure intact, resulting in a heterogeneous reaction consuming most of the aluminum. Delayed ignition occurs when particles preheated to lower temperatures start oxidizing at much lower rates, leading to cloud combustion, in which thermal interaction between individual aerosolized burning particles is substantial. During this process, the nanostructure may be lost. Temperature measurements show that nanocomposites with CuO and MoO3 burned superadiabatically with flame temperatures exceeding thermodynamic predictions.

Synthesis of AlFeCuCrMg{sub x} (x = 0, 0.5, 1, 1.7) alloy powders by mechanical alloying

DOE Office of Scientific and Technical Information (OSTI.GOV)

Maulik, Ornov; Kumar, Vinod, E-mail: vkt.meta@mnit.ac.in; Adjunct Faculty, Materials Research Centre, Malaviya National Institute of Technology, Jaipur 302017

2015-12-15

Novel AlFeCuCrMg{sub x} (x = 0, 0.5, 1, 1.7 mol) high-entropy alloys (HEAs) were synthesized by mechanical alloying. The effect of Mg content on the phase evolution of HEAs was investigated using X-Ray diffractometry (XRD), transmission electron microscopy (TEM) and selected area electron diffraction (SAED) pattern analysis. The particle morphology and composition of HEAs were investigated by scanning electron microscopy (SEM). Thermodynamic parameters were calculated and analyzed to explain the formation of a solid solution. XRD analysis revealed BCC as major phase and FCC as a minor phase in as-milled AlFeCuCr and AlFeCuCrMg{sub 0.5} HEAs. Also, XRD analysis of as-milledmore » AlFeCuCrMg, AlFeCuCrMg{sub 1.7} confirmed the formation of two BCC phases (BCC 1 and BCC 2). TEM–SAED analysis of AlFeCuCrMg{sub x} HEAs concurred with XRD results. Microstructural features and mechanism for solid solution formation have been conferred in detail. Phase formation of the present HEAs has been correlated with calculated thermodynamic parameters. Differential thermal analysis (TGA-DTA) of these alloys confirmed that there is no substantial phase change up to 500 °C. - Highlights: • Novel AlFeCuCrMg{sub x} (x = 0, 0.5, 1, 1.7) HEAs were prepared by mechanical alloying. • Phase evolution and lattice parameter were studied by X-Ray Diffraction. • Crystallite size and lattice microstrain calculated failed to obey the Williamson–Hall method. • Criterions for formation of simple solid solution were compared to the thermodynamic parameters of the present HEAs. • Increase in the Mg concentration in AlMg{sub x}FeCuCr (x = 0, 0.5, 1, 1.7) HEAs supports the formation of BCC phase.« less

In-situ XRD and EDS method study on the oxidation behaviour of Ni-Cu sulphide ore.

PubMed

Li, Guangshi; Cheng, Hongwei; Xiong, Xiaolu; Lu, Xionggang; Xu, Cong; Lu, Changyuan; Zou, Xingli; Xu, Qian

2017-06-12

The oxidation mechanism of sulfides is the key issue during the sulphide-metallurgy process. In this study, the phase transformation and element migration were clearly demonstrated by in-situ laboratory-based X-ray diffraction (XRD) and energy-dispersive X-ray spectroscopy (EDS), respectively. The reaction sequence and a four-step oxidation mechanism were proposed and identified. The elemental distribution demonstrated that at a low temperature, the Fe atoms diffused outward and the Ni/Cu atoms migrated toward the inner core, whereas the opposite diffusion processes were observed at a higher temperature. Importantly, the unique visual presentation of the oxidation behaviour provided by the combination of in-situ XRD and EDS might be useful for optimising the process parameters to improve the Ni/Cu extraction efficiency during Ni-Cu sulphide metallurgy.

PM2.5 water-soluble elements in the southeastern United States: automated analytical method development, spatiotemporal distributions, source apportionment, and implications for heath studies

NASA Astrophysics Data System (ADS)

Fang, T.; Guo, H.; Verma, V.; Peltier, R. E.; Weber, R. J.

2015-06-01

Water-soluble redox-active metals are potentially toxic due to the ability to catalytically generate reactive oxygen species (ROS) in vivo, leading to oxidative stress. As part of the Southeastern Center for Air Pollution and Epidemiology (SCAPE), we developed a method to quantify water-soluble elements, including redox-active metals, from a large number of filter samples (N = 530) in support of the Center's health studies. PM2.5 samples were collected during 2012-2013 at various sites (three urban, two rural, a near-road, and a road-side site) in the southeastern US, using high-volume samplers. Water-soluble elements (S, K, Ca, Ti, Mn, Fe, Cu, Zn, As, Se, Br, Sr, Ba, and Pb) were determined by extracting filters in deionized water and re-aerosolized for analyses by X-ray fluorescence (XRF) using an online aerosol element analyzer (Xact, Cooper Environmental). Concentrations ranged from detection limits (nominally 0.1 to 30 ng m-3) to 1.2 μg m-3, with S as the most abundant element, followed by Ca, K, Fe, Cu, Zn, and Ba. Positive Matrix Factorization (PMF) identified four factors that were associated with specific sources based on relative loadings of various tracers. These include: brake/tire wear (with tracers Ba and Cu); biomass burning (K); secondary formation (S, Se, and WSOC); and mineral dust (Ca). Of the four potentially toxic and relatively abundant metals (redox active Cu, Mn, Fe, and redox-inactive Zn), 51 % of Cu, 32 % of Fe, 17 % of Mn, and 45 % of Zn, were associated with the brake/tire factor. Mn was mostly associated with the mineral dust factor (45 %). These two factors were higher in warm (dryer) periods that favored particle re-suspension. Zn was found in a mixture of factors, with 26 % associated with mineral dust, 14 % biomass burning, and 13 % secondary formation. Roughly 50 % of Fe and 40 % of Cu was apportioned to the secondary formation factor, likely through increased solubility by sulfur-driven aerosol acidity. Linkages between sulfate and water-soluble Fe and Cu may account for some of the past observed associations between sulfate/sulfur oxide and health outcomes. For Cu, Mn, Fe, and Zn, only Fe was correlated with PM2.5 mass (r = 0.73-0.80). Overall, mobile source emissions generated through mechanical processes (re-entrained road dust, tire and break wear) and processing by secondary sulfate were major contributors to water-soluble metals known to be capable of generating ROS.

Application of silica-supported Fe-Cu nanoparticles in the selective hydrogenation of p-dinitrobenzene to p-phenylenediamine

NASA Astrophysics Data System (ADS)

Shesterkina, A. A.; Shuvalova, E. V.; Kirichenko, O. A.; Strelkova, A. A.; Nissenbaum, V. D.; Kapustin, G. I.; Kustov, L. M.

2017-02-01

Supported bimetallic Fe-Cu/SiO2 materials are synthesized, and their catalytic activity in hydrogenation of dinitrobenzene to phenylenediamine at 145-180°C and 1.3 MPa hydrogen pressure is studied for the first time. The best results (89% selectivity toward p-phenylenediamine at complete conversion of p-dinitrobenzene) are obtained for the sample synthesized via co-deposition with subsequent calcination at 300°C. The sample contains 7% iron and 3% copper. The formation of separate phases of metal oxides (for the catalysts prepared by impregnation) and mixed bimetallic oxide phases (in case of co-deposition procedure) in calcined samples is revealed via thermoprogrammed reduction with hydrogen.

Cu@C nanoporous composites containing little copper oxides derived from dimethyl imidazole modified MOF199 as electrocatalysts for hydrogen evolution reaction

NASA Astrophysics Data System (ADS)

Wei, Xuedong; Li, Na; Zhang, Xianming

2017-12-01

It remains a huge challenge to develop non precious electrocatalysts with high activity to substitute commercial Pt catalysts for hydrogen evolution reactions (HER). Here, the C-Cu-DI and C-Cu materials with the copper based nanoporous carbon structures were synthesized by carbonizing MOF199 and DI-MOF199. The composite structure and HER electrocatalytic properties of the C-Cu-DI and C-Cu materials are studied. The results show that C-Cu-DI and C-Cu samples exhibit good catalytic activity. And C-Cu-DI sample through the addition of Dimethyl imidazole(DI) in the DI-MOF199 precursor has higher electrocatalytic activity than the C-Cu sample. The superior catalytic activity is attributed to the special composite structure of nanoscale deposition particles on the framework with plenty of nano pores and nano copper and few copper oxidation particles distributed or wrapped into the amorphous porous carbon phase. The nano copper and few copper oxidation particles in the C-Cu and C-Cu-DI catalysts maybe provide the more effective catalytic activity sites. The C-Cu-DI composite with large size spherical hollow deposition particles has higher conductivity, better BET surface area and reasonable micro-meso-macro porous distribution, so the overpotentials at the current density of 1 mA cm-2 and 10 mA cm-2 are respectively 270 mV and 390 mV vs. RHE. Although the HER activity has a big gap with commercial platinum catalyst, this study can provide an important experimental exploration for the design of copper based non noble metal/nano porous carbon composite HER electrocatalyst.

Iron and manganese oxide mineralization in the Pacific

USGS Publications Warehouse

Hein, J.R.; Koschinsky, A.; Halbach, P.; Manheim, F.T.; Bau, M.; Kang, J.-K.; Lubick, N.

1997-01-01

Iron, manganese, and iron-manganese deposits occur in nearly all geomorphologic and tectonic environments in the ocean basins and form by one or more of four processes: (1) hydrogenetic precipitation from cold ambient seawater, (2) precipitation from hydrothermal fluids, (3) precipitation from sediment pore waters that have been modified from bottom water compositions by diagenetic reactions in the sediment column and (4) replacement of rocks and sediment. Iron and manganese deposits occur in five forms: nodules, crusts, cements, mounds and sediment-hosted stratabound layers. Seafloor oxides show a wide range of compositions from nearly pure iron to nearly pure manganese end members. Fe/Mn ratios vary from about 24 000 (up to 58% elemental Fe) for hydrothermal seamount ironstones to about 0.001 (up to 52% Mn) for hydrothermal stratabound manganese oxides from active volcanic arcs. Hydrogenetic Fe-Mn crusts that occur on most seamounts in the ocean basins have a mean Fe/Mn ratio of 0.7 for open-ocean seamount crusts and 1.2 for continental margin seamount crusts. Fe-Mn nodules of potential economic interest from the Clarion-Clipperton Zone have a mean Fe/Mn ratio of 0.3, whereas the mean ratio for nodules from elsewhere in the Pacific is about 0.7. Crusts are enriched in Co, Ni and Pt and nodules in Cu and Ni, and both have significant concentrations of Pb, Zn, Ba, Mo, V and other elements. In contrast, hydrothermal deposits commonly contain only minor trace metal contents, although there are many exceptions, for example, with Ni contents up to 0.66%, Cr to 1.2%, and Zn to 1.4%. Chondrite-normalized REE patterns generally show a positive Ce anomaly and abundant ΣREEs for hydrogenetic and mixed hydrogenetic-diagenetic deposits, whereas the Ce anomaly is negative for hydrothermal deposits and ΣREE contents are low. However, the Ce anomaly in crusts may vary from strongly positive in East Pacific crusts to slightly negative in West Pacific crusts, which may reflect the redox conditions of seawater. The concentration of elements in hydrogenetic Fe-Mn crusts depends on a wide variety of water column and crust surface characteristics, whereas concentration of elements in hydrothermal oxide deposits depends of the intensity of leaching, rock types leached, and precipitation of sulphides at depth in the hydrothermal system.

Enhanced Reactant-Contaminant Contact through the Use of Persulfate In Situ Chemical Oxidation (ISCO)

DTIC Science & Technology

2011-02-01

cuprite [Cu2O], hematite [Fe2O3], ilmenite [FeTiO3], magnesite [MgCO3], malachite [Cu2(CO3)(OH)2], pyrite [FeS2], pyrolusite [MnO2], siderite [FeCO3...0.3 m2/g], malachite [3.65 ± 0.03 m2/g], pyrite [2.12 ± 0.01 m2/g], pyrolusite [1.39 ± 0.04 m2/g], siderite [6.8 ± 0.4 m2/g], willemite [1.8 ± 0.02 m2...0.4 0.6 0.8 1 0 10 20 30 40 50 60 Anatase Bauxite Calcite Cobaltite Control Cuprite Hematite Ilmenite Magnesite Malachite Pyrite Pyrolusite Siderite

Ordered PdCu-Based Nanoparticles as Bifunctional Oxygen-Reduction and Ethanol-Oxidation Electrocatalysts

DOE PAGES

Jiang, Kezhu; Wang, Pengtang; Guo, Shaojun; ...

2016-06-02

Here, the development of superior non-platinum electrocatalysts for enhancing the electrocatalytic activity and stability for the oxygen-reduction reaction (ORR) and liquid fuel oxidation reaction is very important for the commercialization of fuel cells,but still agreat challenge.Herein, we demonstrate a new colloidal chemistry technique for making structurally ordered PdCu-based nanoparticles (NPs) with composition control from PdCu to PdCuNi and PtCuCo.Under the dual tuning on the composition and intermetallic phase,the ordered PdCuCo NPs exhibit better activity and much enhanced stability for ORR and ethanol-oxidation reaction (EOR)than those of disordered PdCuM NPs,the commercial Pt/Cand Pd/C catalysts.The density functional theory (DFT)calculations reveal that themore » improved ORR activity on the PdCuM NPs stems from the catalytically active hollow sites arising from the ligand effect and the compressive strain on thePd surface owing to the smaller atomic size of Cu, Co,and Ni.« less

Cu-Mn-Fe alloys and Mn-rich amphiboles in ancient copper slags from the Jabal Samran area, Saudi Arabia: With synopsis on chemistry of Fe-Mn(III) oxyhydroxides in alteration zones

NASA Astrophysics Data System (ADS)

Surour, Adel A.

2015-01-01

In the Jabal Samran area (western Saudi Arabia), secondary copper mineralization in a NE-trending shear zone in which the arc metavolcanic host rocks (dacite-rhyodacite) show conjugate fractures and extensive hydrothermal alteration and bleaching. The zones contain frequent Fe-Mn(III) oxyhydroxides (FeOH-MnOH) that resulted from oxidation of pyrite and Mn-bearing silicates. In the bleached part, the groundmass is represented by Fe-bearing interstratified illite-smectite with up to 4.02 wt% FeOt. FeOH-MnOH are pre-weathering phases formed by hydrothermal alteration in a submarine environment prior to uplifting. Five varieties of FeOH are distinguished, four of them are exclusively hydrothermal with ∼20 wt% H2O whereas the fifth contains ∼31-33 wt% H2O and might represent reworking of earlier hydrothermal FeOH phases by weathering. FeOH fills thin fractures in the form of veinlets and crenulated laminae or as a pseudomorph for pyrite, goethite and finally ferrihydrite, and this oxyhydroxide is characterized by positive correlation of Fe2O3 with SiO2 and Al2O3. On the other hand, MOH shows positive correlation between MnO2 and Al2O3 whereas it is negative between Fe2O3 and SiO2. Paratacamite is the most common secondary copper mineral that fills fractures and post-dates FeOH and MnOH. It is believed that Cl- in the structure of paratacamite represents inherited marine storage rather than from surfacial evaporates or meteoric water. The mineralogy of slags suggests a complicated mineral assemblage that includes native Cu prills, synthetic spinifixed Mn-rich amphiboles with 16.73 wt% MnO, brown glass and Ca-Mn-Fe phase close to the olivine structure. EMPA indicate that the some Cu prills have either grey discontinuous boarder zone of S-rich Mn-Cu alloy (with up to 21.95 wt% S and 19.45 wt% Mn) or grey Cu-Mn-Fe alloy (with up to 15.9 wt% Cu, 39. 12 wt% Mn and 61.64 wt% Fe). Mn in the Cu prills is expelled inward as Cu-Mn-Fe alloy inclusions whereas S is expelled outward as S-rich Mn-Cu alloy crust. Remains in the Samran smelter sites suggest the use of charcoal as a source of energy, quartzite as a flux and an air-cooling technique was used.

New insights on the biomineralisation process developing in human lungs around inhaled asbestos fibres

NASA Astrophysics Data System (ADS)

Bardelli, Fabrizio; Veronesi, Giulia; Capella, Silvana; Bellis, Donata; Charlet, Laurent; Cedola, Alessia; Belluso, Elena

2017-03-01

Once penetrated into the lungs of exposed people, asbestos induces an in vivo biomineralisation process that leads to the formation of a ferruginous coating embedding the fibres. The ensemble of the fibre and the coating is referred to as asbestos body and is believed to be responsible for the high toxicological outcome of asbestos. Lung tissue of two individuals subjected to prolonged occupational exposure to crocidolite asbestos was investigated using synchrotron radiation micro-probe tools. The distribution of K and of elements heavier than Fe (Zn, Cu, As, and Ba) in the asbestos bodies was observed for the first time. Elemental quantification, also reported for the first time, confirmed that the coating is highly enriched in Fe (~20% w/w), and x-ray absorption spectroscopy indicated that Fe is in the 3+ oxidation state and that it is present in the form of ferritin or hemosiderin. Comparison of the results obtained studying the asbestos bodies upon removing the biological tissue by chemical digestion and those embedded in histological sections, allowed unambiguously distinguishing the composition of the asbestos bodies, and understanding to what extent the digestion procedure altered their chemical composition. A speculative model is proposed to explain the observed distribution of Fe.

A-site ordered quadruple perovskite oxides

NASA Astrophysics Data System (ADS)

Youwen, Long

2016-07-01

The A-site ordered perovskite oxides with chemical formula display many intriguing physical properties due to the introduction of transition metals at both A‧ and B sites. Here, research on the recently discovered intermetallic charge transfer occurring between A‧-site Cu and B-site Fe ions in LaCu3Fe4O12 and its analogues is reviewed, along with work on the magnetoelectric multiferroicity observed in LaMn3Cr4O12 with cubic perovskite structure. The Cu-Fe intermetallic charge transfer leads to a first-order isostructural phase transition accompanied by drastic variations in magnetism and electrical transport properties. The LaMn3Cr4O12 is a novel spin-driven multiferroic system with strong magnetoelectric coupling effects. The compound is the first example of cubic perovskite multiferroics to be found. It opens up a new arena for studying unexpected multiferroic mechanisms. Project supported by the National Basic Research Program of China (Grant No. 2014CB921500), the Strategic Priority Research Program of the Chinese Academy of Sciences (Grant No. XDB07030300), and the National Natural Science Foundation of China (Grant No. 11574378).

An Atom-Probe Tomographic Study of Arc Welds in a Multi-Component High-Strength Low-Alloy Steel

NASA Astrophysics Data System (ADS)

Hunter, Allen H.; Farren, Jeffrey D.; DuPont, John N.; Seidman, David N.

2013-04-01

An experimental plate steel with the composition Fe-1.39Cu-2.7Ni-0.58Al-0.48Mn-0.48Si-0.065Nb-0.05C (wt pct) or alternatively Fe-1.43Cu-2.61Ni-1.21Al-0.48Mn-0.98Si-0.039Nb-0.23C at. pct has been recently produced at Northwestern University for use in Naval hull and deck applications—it is designated NUCu-140. To understand the microstructural changes occurring in NUCu-140 steel after gas-metal arc welding (GMAW), a detailed study of the heat-affected and fusion zones was performed throughout the weld cross section using microhardness, metallographic, chemical, and atom-probe tomographic analyses. Local-electrode atom-probe (LEAP) tomography was employed to measure the morphology and compositions of Cu-rich precipitates from each region. The mean radius, number density, volume fraction, and compositions of the precipitates, as well as the interfacial concentration profiles, are measured. The Cu precipitates dissolve partially from the heat-affected zone (HAZ) thermal cycle, and freshly formed sub-nanometer radius Cu-rich precipitates nucleate in both the HAZ and fusion zone (FZ) during cooling; however, the precipitation of Cu during cooling in the HAZ and FZ is not sufficient to restore the lost strength. The precipitation in the FZ is reduced compared to the HAZ due to a mismatched Cu composition of the weld. Multi-pass welding is suggested to restore strength in the GMAW sample by promoting Cu precipitate nucleation and growth in the HAZ and FZ.

Renierite, Cu10ZnGe2Fe4S16-Cu11GeAsFe4S16: a coupled solid solution series.

USGS Publications Warehouse

Bernstein, L.R.

1986-01-01

The composition of renierite is found to be Cu10(Zn1-xCux)Ge2-xAsxFe4S16 (0 = or < x = or < 1), with continuous solid solution between the zincian and arsenian end-members, Cu10ZnGe2Fe4S16 and Cu11GeAsFe4S16, through the coupled substitution Zn(II) + Ge(IV) = Cu(I) + As(V). This is the first reported example of extensive coupled solid solution in a sulphide mineral. Arsenian renierite, not previously characterized, is similar to zincian renierite in polished section, with a slightly redder colour and lower anisotropy. It is reddish orange with relief very similar to that of bornite, though it is harder (VHN25 = 286) and does not tarnish in air. It is slightly bireflective, with colours varying from orange-yellow to reddish orange in nearly crossed polarizers. The strongest powder XRD lines are: 3.042(100), 1.861(29), 1.869(16), 1.594(11) and 1.017(10) A; D(calc.) 4.50 g/cm3. Specimens have been found at the Ruby Creek copper deposit, Alaska, where zincian renierite also occurs, and at the Inexco no. 1 mine, Jamestown, Colorado.-J.A.Z.

Collisions in outer space produced an icosahedral phase in the Khatyrka meteorite never observed previously in the laboratory

PubMed Central

Bindi, Luca; Lin, Chaney; Ma, Chi; Steinhardt, Paul J.

2016-01-01

We report the first occurrence of an icosahedral quasicrystal with composition Al62.0(8)Cu31.2(8)Fe6.8(4), outside the measured equilibrium stability field at standard pressure of the previously reported Al-Cu-Fe quasicrystal (AlxCuyFez, with x between 61 and 64, y between 24 and 26, z between 12 and 13%). The new icosahedral mineral formed naturally and was discovered in the Khatyrka meteorite, a recently described CV3 carbonaceous chondrite that experienced shock metamorphism, local melting (with conditions exceeding 5 GPa and 1,200 °C in some locations), and rapid cooling, all of which likely resulted from impact-induced shock in space. This is the first example of a quasicrystal composition discovered in nature prior to being synthesized in the laboratory. The new composition was found in a grain that has a separate metal assemblage containing icosahedrite (Al63Cu24Fe13), currently the only other known naturally occurring mineral with icosahedral symmetry (though the latter composition had already been observed in the laboratory prior to its discovery in nature). The chemistry of both the icosahedral phases was characterized by electron microprobe, and the rotational symmetry was confirmed by means of electron backscatter diffraction. PMID:27929519

Comparative leaching of six toxic metals from raw and chemically stabilized MSWI fly ash using citric acid.

PubMed

Wang, Huawei; Fan, Xinxiu; Wang, Ya-Nan; Li, Weihua; Sun, Yingjie; Zhan, Meili; Wu, Guizhi

2018-02-15

The leaching behavior of six typical toxic metals (Pb, Zn, Cr, Cd, Cu and Ni) from raw and chemically stabilized (phosphate and chelating agent) municipal solid waste incineration (MSWI) fly ash were investigated using citric acid. Leaching tests indicated that phosphate stabilization can effectively decrease the leaching of Zn, Cd and Cr; whereas chelating agent stabilization shows a strong ability to lower the release of Pb, Cd and Cu, but instead increases the solubility of Zn and Cr at low pH conditions. Sequential extraction results suggested that the leaching of Pb, Zn and Cd in both the stabilized MSWI fly ash samples led to the decrease in Fe/Mn oxide fraction and the increase in exchangeable and carbonate fractions. The leaching of Cr was due to the decrease in exchangeable, carbonate and Fe/Mn oxide fractions in phosphate-stabilized and chelating agent-stabilized MSWI fly ash. The leaching of Cu in both stabilized MSWI fly ash was greatly ascribed to the decrease in Fe/Mn oxide and oxidisable fractions. Moreover, predicted curves by geochemical model indicated that both stabilized MSWI fly ash have the risk of releasing toxic metals under strong acid environment. Copyright © 2017 Elsevier Ltd. All rights reserved.

Shock synthesis of quasicrystals with implications for their origin in asteroid collisions

DOE PAGES

Asimow, Paul D.; Lin, Chaney; Bindi, Luca; ...

2016-06-28

Here, we designed a plate impact shock recovery experiment to simulate the starting materials and shock conditions associated with the only known natural quasicrystals, in the Khatyrka meteorite. At the boundaries among CuAl5, (Mg 0.75Fe 0.25 2+) 2SiO 4 olivine, and the stainless steel chamber walls, the recovered specimen contains numerous micron-scale grains of a quasicrystalline phase displaying face-centered icosahedral symmetry and low phason strain. The compositional range of the icosahedral phase is Al 68-73Fe 11-16Cu 10-12Cr 1-4Ni 1-2 and extends toward higher Al/(Cu+Fe) and Fe/Cu ratios than those reported for natural icosahedrite or for any previously known synthetic quasicrystalmore » in the Al-Cu-Fe system. The shock-induced synthesis demonstrated in this experiment reinforces the evidence that natural quasicrystals formed during a shock event but leaves open the question of whether this synthesis pathway is attributable to the expanded thermodynamic stability range of the quasicrystalline phase at high pressure, to a favorable kinetic pathway that exists under shock conditions, or to both thermodynamic and kinetic factors.« less

Shock synthesis of quasicrystals with implications for their origin in asteroid collisions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Asimow, Paul D.; Lin, Chaney; Bindi, Luca

Here, we designed a plate impact shock recovery experiment to simulate the starting materials and shock conditions associated with the only known natural quasicrystals, in the Khatyrka meteorite. At the boundaries among CuAl5, (Mg 0.75Fe 0.25 2+) 2SiO 4 olivine, and the stainless steel chamber walls, the recovered specimen contains numerous micron-scale grains of a quasicrystalline phase displaying face-centered icosahedral symmetry and low phason strain. The compositional range of the icosahedral phase is Al 68-73Fe 11-16Cu 10-12Cr 1-4Ni 1-2 and extends toward higher Al/(Cu+Fe) and Fe/Cu ratios than those reported for natural icosahedrite or for any previously known synthetic quasicrystalmore » in the Al-Cu-Fe system. The shock-induced synthesis demonstrated in this experiment reinforces the evidence that natural quasicrystals formed during a shock event but leaves open the question of whether this synthesis pathway is attributable to the expanded thermodynamic stability range of the quasicrystalline phase at high pressure, to a favorable kinetic pathway that exists under shock conditions, or to both thermodynamic and kinetic factors.« less

Laser induced surface structuring of Cu for enhancement of field emission properties

NASA Astrophysics Data System (ADS)

Akram, Mahreen; Bashir, Shazia; Jalil, Sohail Abdul; Shahid Rafique, Muhammad; Hayat, Asma; Mahmood, Khaliq

2018-02-01

The effect of Nd:YAG (1064 nm, 10 ns, 10 Hz) laser induced surface structuring of copper (Cu) for enhancement of field emission (FE) properties has been investigated. X-ray diffraction analysis was employed to investigate the surface structural and compositional modifications. The surface structuring was explored by scanning electron microscope investigation. FE properties were studied under UHV conditions in a parallel plate configuration of planar un-irradiated Cu anode and laser irradiated Cu cathode. The Fowler-Nordheim plots were drawn to confirm the dominance of FE behavior of the measured I-V characteristics. The obtained values of turn-on field ‘E o’, field enhancement factor ‘β’ and maximum current density ‘J max’ come out to be to be in the range of 5.5-8.5 V μm-1, 1380-2730 and 147-375 μA cm-2 respectively for the Cu samples irradiated at laser irradiance ranging from 13 to 50 GW cm-2. The observed enhancement in the FE properties has been correlated with the growth of various surface structures such as ridged protrusions, cones and pores/tiny holes. The porous morphology is found to be responsible for a significant enhancement in the FE parameters.

Aluminum Hydride as a Fuel Supplement to NanoThermites

DTIC Science & Technology

2014-01-01

nanocomposite thermite based on CuO, Bi2O3, and Fe2O3. Pressure cell and burn tube experiments demonstrated enhancements in absolute pressure...pressurization rate, and burning velocity when micron-scale aluminum hydride was used as a minor fuel component in a nanoaluminum–copper-oxide thermite ...alane, AlH3) replaced nanoaluminum incrementally as a fuel in a nanocomposite thermite based on CuO, Bi2O3, and Fe2O3. Pressure cell and burn tube

Transition metal ion-assisted photochemical generation of alkyl halides and hydrocarbons from carboxylic acids.

PubMed

Carraher, Jack M; Pestovsky, Oleg; Bakac, Andreja

2012-05-21

Near-UV photolysis of aqueous solutions of propionic acid and aqueous Fe(3+) in the absence of oxygen generates a mixture of hydrocarbons (ethane, ethylene and butane), carbon dioxide, and Fe(2+). The reaction becomes mildly catalytic (about five turnovers) in the presence of oxygen which converts a portion of alkyl radicals to oxidizing intermediates that reoxidize Fe(2+). The photochemistry in the presence of halide ions (X(-) = Cl(-), Br(-)) generates ethyl halides via halogen atom abstraction from FeX(n)(3-n) by ethyl radicals. Near-quantitative yields of C(2)H(5)X are obtained at ≥0.05 M X(-). Competition experiments with Co(NH(3))(5)Br(2+) provided kinetic data for the reaction of ethyl radicals with FeCl(2+) (k = (4.0 ± 0.5) × 10(6) M(-1) s(-1)) and with FeBr(2+) (k = (3.0 ± 0.5) × 10(7) M(-1) s(-1)). Photochemical decarboxylation of propionic acid in the presence of Cu(2+) generates ethylene and Cu(+). Longer-chain acids also yield alpha olefins as exclusive products. These reactions become catalytic under constant purge with oxygen which plays a dual role. It reoxidizes Cu(+) to Cu(2+), and removes gaseous olefins to prevent accumulation of Cu(+)(olefin) complexes and depletion of Cu(2+). The results underscore the profound effect that the choice of metal ions, the medium, and reaction conditions exert on the photochemistry of carboxylic acids.

Cooperative oscillations of electron-copper-oxygen interaction: Possible relevance for superconduction theory

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tributsch, H.

1989-01-01

Interfaces of copper containing crystallized materials (Cu/sub 5/FeS/sub 4/, CuFeS/sub 2/, Cu/sub 2/S, CuS, CuInS/sub 2/, and CuInSe/sub 2/), exposed to oxidation by H/sub 2/O/sub 2/, undergo sustained electrochemical oscillations. They involve electronic (Cu/sup +/), (Cu/sup 2 +/), and (Cu/sup 3 +/) interactions with chemically bound oxygen similar as in superconducting YBa/sub 2/Cu/sub 3/O/sub 7/ or (La,Sr)/sub 2/CuO/sub 4/ and may be a phenomenon of irreversible thermodynamics which is related to the kind of cooperative electron-copper-oxygen interactions which also give rise to high-temperature superconduction. The relevance of the model system is supported by the formation of the H/sub 2/O/sub 2/more » species on the surface of high-temperature superconducting materials in contact with ambiental humidity. It is shown how, by a simple modification of the interaction mechanism, an oscillatory phenomenon such as that observed with oxidized copper sulfide interfaces, which follows a limiting cycle, can be converted into a triple-state phenomenon. Such a cooperative mechanism that involves a lowest steady state which is unable to turn over energy may be the background for the pairing of electrons or a related cooperative interaction process in superconduction. As a possible support, no interfacial oscillations could yet be induced with Ba/sub 2/Cu/sub 3/Y/sub 7/.« less

Enargite oxidation: A review

NASA Astrophysics Data System (ADS)

Lattanzi, Pierfranco; Da Pelo, Stefania; Musu, Elodia; Atzei, Davide; Elsener, Bernhard; Fantauzzi, Marzia; Rossi, Antonella

2008-01-01

Enargite, Cu 3AsS 4, is common in some deposit types, e.g. porphyry systems and high sulphidation epithermal deposits. It is of environmental concern as a potential source of arsenic. In this communication, we review the current knowledge of enargite oxidation, based on the existing literature and our own original data. Explicit descriptions of enargite oxidation in natural environments are scarce. The most common oxidized alteration mineral of enargite is probably scorodite, FeAsO 4.2H 2O, with iron provided most likely by pyrite, a phase almost ubiquitously associated with enargite. Other secondary minerals after enargite include arsenates such as chenevixite, Cu 2Fe 2(AsO 4) 2(OH) 4.H 2O, and ceruleite, Cu 2Al 7(AsO 4) 4.11.5H 2O, and sulphates such as brochantite, Cu 4(SO 4)(OH) 6, and posnjakite, Cu 4(SO 4)(OH) 6·H 2O. Detailed studies of enargite field alteration at Furtei, Sardinia, suggest that most alteration occurs through dissolution, as testified by the appearance of etch pits at the surface of enargite crystals. However, apparent replacement by scorodite and cuprian melanterite was observed. Bulk oxidation of enargite in air is a very slow process. However, X-ray photoelectron spectroscopy (XPS) reveals subtle surface changes. From synchrotron-based XPS it was suggested that surface As atoms react very fast, presumably by forming bonds with oxygen. Conventional XPS shows the formation, on aged samples, of a nanometer-size alteration layer with an appreciably distinct composition with respect to the bulk. Mechanical activation considerably increases enargite reactivity. In laboratory experiments at acidic to neutral pH, enargite oxidation/dissolution is slow, although it is accelerated by the presence of ferric iron and/or bacteria such as Acidithiobacillus ferrooxidans and Sulfolobus BC. In the presence of sulphuric acid and ferric iron, the reaction involves dissolution of Cu and formation of native sulphur, subsequently partly oxidized to sulphate. At alkaline pH, the reactivity of enargite is apparently slightly greater. XPS spectra of surfaces conditioned at pH 11 have been interpreted as evidence of formation of a number of surface species, including cupric oxide and arsenic oxide. Treatment with hypochlorite solutions at pH 12.5 quickly produces a coating of cupric oxide. Electrochemical oxidation of enargite typically involves low current densities, confirming that the oxidation process is slow. Important surface changes occur only at high applied potentials, e.g. + 0.74 V vs. SHE. It is confirmed that, at acidic pH, the dominant process is Cu dissolution, accompanied (at + 0.56 V vs. SHE, pH = 1) by formation of native sulphur. At alkaline pH, a number of surface products have been suggested, including copper and arsenic oxides, and copper arsenates. XPS studies of the reacted surfaces demonstrate the evolution of Cu from the monovalent to the divalent state, the formation of As-O bonds, and the oxidation of sulphur to polysulphide, sulphite and eventually sulphate. In most natural and quasi-natural (mining) situations, it is expected that enargite reactivity will be slow. Moreover, it is likely that the release of arsenic will be further slowed down by at least temporary trapping in secondary phases. Therefore, an adequate management of exposed surfaces and wastes should minimize the environmental impact of enargite-bearing deposits. In spite of an increasing body of data, there are several gaps in our knowledge of enargite oxidation. The exact nature of most mechanisms and products remains poorly constrained, and there is a lack of quantitative data on the dependence on parameters such as pH and dissolved oxygen.

Copper and Iron Homeostasis in Plants: The Challenges of Oxidative Stress

PubMed Central

Pilon, Marinus

2013-01-01

Abstract Significance: Photosynthesis, the process that drives life on earth, relies on transition metal (e.g., Fe and Cu) containing proteins that participate in electron transfer in the chloroplast. However, the light reactions also generate high levels of reactive oxygen species (ROS), which makes metal use in plants a challenge. Recent Advances: Sophisticated regulatory networks govern Fe and Cu homeostasis in response to metal ion availability according to cellular needs and priorities. Molecular remodeling in response to Fe or Cu limitation leads to its economy to benefit photosynthesis. Fe toxicity is prevented by ferritin, a chloroplastic Fe-storage protein in plants. Recent studies on ferritin function and regulation revealed the interplay between iron homeostasis and the redox balance in the chloroplast. Critical Issues: Although the connections between metal excess and ROS in the chloroplast are established at the molecular level, the mechanistic details and physiological significance remain to be defined. The causality/effect relationship between transition metals, redox signals, and responses is difficult to establish. Future Directions: Integrated approaches have led to a comprehensive understanding of Cu homeostasis in plants. However, the biological functions of several major families of Cu proteins remain unclear. The cellular priorities for Fe use under deficiency remain largely to be determined. A number of transcription factors that function to regulate Cu and Fe homeostasis under deficiency have been characterized, but we have not identified regulators that mediate responses to excess. Importantly, details of metal sensing mechanisms and cross talk to ROS-sensing mechanisms are so far poorly documented in plants. Antioxid. Redox Signal. 19, 919–932. PMID:23199018

Novel Solar Energy Conversion Materials by Design of Mn(II) Oxides

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lany, S.; Peng, H.; Ndione, P.

2013-01-01

Solar energy conversion materials need to fulfill simultaneously a number of requirements in regard of their band-structure, optical properties, carrier transport, and doping. Despite their desirable chemical properties, e.g., for photo-electrocatalysis, transition-metal oxides usually do not have desirable semiconducting properties. Instead, oxides with open cation d-shells are typically Mott or charge-transfer insulators with notoriously poor transport properties, resulting from large effective electron/hole masses or from carrier self-trapping. Based on the notion that the electronic structure features (p-d interaction) supporting the p-type conductivity in d10 oxides like Cu2O and CuAlO2 occurs in a similar fashion also in the d5 (high-spin) oxides,more » we recently studied theoretically the band-structure and transport properties of the prototypical binary d5 oxides MnO and Fe2O3 [PRB 85, 201202(R)]. We found that MnO tends to self-trap holes by forming Mn+III, whereas Fe2O3 self-traps electrons by forming Fe+II. However, the self-trapping of holes is suppressed by when Mn is tetrahedrally coordinated, which suggests specific routes to design novel solar conversion materials by considering ternary Mn(II) oxides or oxide alloys. We are presenting theory, synthesis, and initial characterization for these novel energy materials.« less

Phase Equilibria in the ZnO-"FeO"-SiO2 System in Reducing Atmosphere and in the ZnO-"FeO"-SiO2-"Cu2O" System in Equilibrium with Liquid Copper Metal at 1250 °C (1523 K)

NASA Astrophysics Data System (ADS)

Hidayat, Taufiq; Hayes, Peter C.; Jak, Evgueni

2018-05-01

Recent experimental studies in the ZnO-"FeO"-SiO2 system in reducing atmosphere demonstrated significant discrepancies with the current FactSage thermodynamic model developed using previous experimental data in this system in equilibrium with metallic iron and air. The present experimental study on phase equilibria in the ZnO-"FeO"-SiO2-"Cu2O" system in equilibrium with liquid copper at 1250 °C (1523 K) at low copper oxide concentrations in slag was initiated and undertaken to resolve these discrepancies. A high-temperature equilibration-rapid quenching-electron-probe X-ray microanalysis (EPMA) technique using a primary phase substrate support and closed system approach with Cu metal introduced to determine effective equilibrium oxygen partial pressure from the Cumetal/Cu2Oslag equilibria was applied to provide accurate information on the liquidus and corresponding solid compositions in the spinel, willemite, and tridymite primary phase fields. The present results confirmed the accuracy of the FactSage model, resolved discrepancies, and demonstrated significant uncertainties in the recent studies by other authors on the system in the open reducing atmosphere. The present study shows how this closed system approach can be used to obtain key thermodynamic data on phase equilibria in systems containing volatile metal species, overcoming the limitations and uncertainties encountered in conventional open gas/condensed phase equilibration with these systems. The study highlights the importance of the focus on obtaining accurate experimental data and the risks of misleading information from inadequate experimental control and analysis. The study also demonstrates that continuing in-depth critical review and analysis of the elemental reactions taking place in complex systems is an essential step in phase equilibrium research.

Structural, dielectric and ferroelectric studies of (x) Mg0.25Cu0.25Zn0.5Fe2O4 + (1-x) BaTiO3 magnetoelectric nano-composites

NASA Astrophysics Data System (ADS)

Khader, S. Abdul; Muneeswaran, M.; Giridharan, N. V.; Sankarappa, T.

2016-05-01

The Particulate nano-composites of ferrite and ferroelectric phases having the general formula (x) Mg0.25Cu0.25Zn0.5Fe2O4 + (1-x) BaTiO3 (x=15%, 30% and 45%) were synthesized by sintering mixtures of highly ferroelectric BaTiO3 (BT) and highly magneto-strictive magnetic component Mg0.25Cu0.25Zn0.5Fe2O4(MCZF). The presence of constituent phases of ferrite, ferroelectric and their composites were probed and confirmed by X-ray diffraction (XRD) studies. Surface morphology of the samples has been investigated using Field Emission Scanning Electron Microscope (FESEM). The variation of dielectric constant and dissipation factor as a function of frequency from 100 Hz to 1 MHz at room temperature were carried out using a Hioki LCR Hi-Tester. The dielectric constant and dielectric loss were found to decrease rapidly in the low frequency region and became almost constant in the high frequency region. The electrical conductivity deduced from the measured dielectric data has been thoroughly analyzed and found that the conduction mechanism in these composites is in conformity with small polaron hopping model. The ferroelectric properties of synthesized magneto-electric nano-composites were measured using P-E loop tracer.

Microstructure and High Temperature Oxidation Property of Fe-Cr-B Based Metal/Ceramic Composite Manufactured by Powder Injection Molding Process

NASA Astrophysics Data System (ADS)

Joo, Yeun-Ah; Kim, Young-Kyun; Yoon, Tae-Sik; Lee, Kee-Ahn

2018-03-01

This study investigated the microstructure and high temperature oxidation property of Fe-Cr-B metal/ceramic composite manufactured using powder injection molding process. Observations of initial microstructure showed a unique structure where α-Fe and (Cr, Fe)2B form a continuous three-dimensional network. High temperature oxidation tests were performed at 900, 1000 and 1100 °C, for 24 h, and the oxidation weight gain according to each temperature condition was 0.13, 0.84 and 6.4 mg/cm2, respectively. The oxidation results according to time at 900 and 1000 °C conditions represented parabolic curves, and at 1100 °C condition formed a rectilinear curve. Observation and phase analysis results of the oxides identified Cr2O3 and SiO2 at 900 and 1000 °C. In addition to Cr2O3 and SiO2, CrBO3 and FeCr2O4 formed due to phase decomposition of boride were identified at 1100 °C. Based on the findings above, this study suggested the high temperature oxidation mechanism of Fe-Cr-B metal/ceramic composite manufactured using powder injection molding, and the possibility of its application as a high temperature component material was also discussed.

Evolution of the Oxidation State of the Earth's Mantle

NASA Technical Reports Server (NTRS)

Danielson, L. R.; Righter, K.; Keller, L.; Christoffersen, E.; Rahman, Z.

2015-01-01

The oxidation state of the Earth's mantle during formation remains an unresolved question, whether it was constant throughout planetary accretion, transitioned from reduced to oxidized, or from oxidized to reduced. We investigate the stability of Fe3(+) at depth, in order to constrain processes (water, late accretion, dissociation of FeO) which may reduce or oxidize the Earth's mantle. In our previous experiments on shergottite compositions, variable fO2, T, and P less than 4 GPa, Fe3(+)/sigma Fe decreased slightly with increasing P, similar to terrestrial basalt. For oxidizing experiments less than 7GPa, Fe3(+)/sigma Fe decreased as well, but it's unclear from previous modelling whether the deeper mantle could retain significant Fe3(+). Our current experiments expand our pressure range deeper into the Earth's mantle and focus on compositions and conditions relevant to the early Earth. Preliminary multi-anvil experiments with Knippa basalt as the starting composition were conducted at 5-7 GPa and 1800 C, using a molybdenum capsule to set the fO2 near IW, by buffering with Mo-MoO3. TEM and EELS analyses revealed the run products quenched to polycrystalline phases, with the major phase pyroxene containing approximately equal to Fe3(+)/2(+). Experiments are underway to produce glassy samples that can be measured by EELS and XANES, and are conducted at higher pressures.

Chemical Composition and Oxidation State of Iron-Containing Aerosol Particles Over West Antarctic Peninsula

NASA Astrophysics Data System (ADS)

Fan, S.; Yu, S.; Lai, B.; Gao, Y.

2017-12-01

Iron is a limiting micronutrient element critical for the marine ecosystem. In the extensive high-nutrient low-chlorophyll (HNLC) regions of the Southern Ocean, the activities of phytoplankton are partly controlled by iron (Fe) from different sources, including atmospheric deposition. Among important properties of atmospheric Fe are the elemental composition and Fe oxidation state of Fe-containing aerosol particles, as these properties affect aerosol Fe solubility. To explore these issues, aerosol samples were collected at Palmer Station in West Antarctic Peninsula. Samples were analyzed by submicron synchrotron-based X-ray fluorescence (XRF) and X-ray absorption near edge structure (XANES) spectroscopy for the Fe oxidation state and elemental composition of aerosol particles. The morphological information of aerosol particles was also observed by the high-resolution fluorescence microscopy, revealing possible sources and formation processes of iron-containing particles. More detailed results will be discussed in this presentation.

Effects of inorganic electrolyte anions on enrichment of Cu(II) ions with aminated Fe3O4/graphene oxide: Cu(II) speciation prediction and surface charge measurement.

PubMed

Hu, Xin-jiang; Liu, Yun-guo; Zeng, Guang-ming; Wang, Hui; You, Shao-hong; Hu, Xi; Tan, Xiao-fei; Chen, An-wei; Guo, Fang-ying

2015-05-01

The present work evaluated the effects of six inorganic electrolyte anions on Cu(II) removal using aminated Fe3O4/graphene oxide (AMGO) in single- and multi-ion systems. A 2(6-2) fractional factorial design (FFD) was employed for assessing the effects of multiple anions on the adsorption process. The results indicated that the Cu(II) adsorption was strongly dependent on pH and could be significantly affected by inorganic electrolyte anions due to the changes in Cu(II) speciation and surface charge of AMGO. In the single-ion systems, the presence of monovalent anions (Cl(-), ClO4(-), and NO3(-)) slightly increased the Cu(II) adsorption onto AMGO at low pH, while the Cu(II) adsorption was largely enhanced by the presence of SO4(2-), CO3(2-), and HPO4(2-). Based on the estimates of major effects and interactions from FFD, the factorial effects of the six selected species on Cu(II) adsorption in multi-ion system were in the following sequence: HPO4(2-)>CO3(2-)>Cl(-)>SO4(2-)>NO3(-)=ClO4(-), and the combined factors of AD (Cl(-)×SO4(2-)) and EF (Cl(-)×SO4(2-)) had significant effects on Cu(II) removal. Copyright © 2015 Elsevier Ltd. All rights reserved.

[Adsorption of Cu on Core-shell Structured Magnetic Particles: Relationship Between Adsorption Performance and Surface Properties].

PubMed

Li, Qiu-mei; Chen, Jing; Li, Hai-ning; Zhang, Xiao-lei; Zhang, Gao-sheng

2015-12-01

In order to reveal the relationship between the adsorption performance of adsorbents and their compositions, structure, and surface properties, the core-shell structured Fe₃O₄/MnO2 and Fe-Mn/Mn₂2 magnetic particles were systematically characterized using multiple techniques and their Cu adsorption behaviors as well as mechanism were also investigated in details. It was found that both Fe₃O4 and Fe-Mn had spinel structure and no obvious crystalline phase change was observed after coating with MnO₂. The introduction of Mn might improve the affinity between the core and the shell, and therefore enhanced the amount and distribution uniformity of the MnO₂ coated. Consequently, Fe-Mn/MnO₂ exhibited a higher BET specific surface area and a lower isoelectric point. The results of sorption experiments showed that Fe-Mn had a higher maximal Cu adsorption capacity of 33.7 mg · g⁻¹ at pH 5.5, compared with 17.5 mg · g⁻¹ of Fe₃O4. After coating, the maximal adsorption capacity of Fe-Mn/MnO₂ was increased to 58.2 mg · g⁻¹, which was 2.6 times as high as that of Fe₃O₄/MnO₂ and outperformed the majority of magnetic adsorbents reported in literature. In addition, a specific adsorption of Cu occurred at the surface of Fe₃O₄/MnO₂ or Fe-Mn/MnO₂ through the formation of inner-sphere complexes. In conclusion, the adsorption performance of the magnetic particles was positively related to their compositions, structure, and surface properties.

Composite Magnetic Nanoparticles (CuFe₂O₄) as a New Microsorbent for Extraction of Rhodamine B from Water Samples.

PubMed

Roostaie, Ali; Allahnoori, Farzad; Ehteshami, Shokooh

2017-09-01

In this work, novel composite magnetic nanoparticles (CuFe2O4) were synthesized based on sol-gel combustion in the laboratory. Next, a simple production method was optimized for the preparation of the copper nanoferrites (CuFe2O4), which are stable in water, magnetically active, and have a high specific area used as sorbent material for organic dye extraction in water solution. CuFe2O4 nanopowders were characterized by field-emission scanning electron microscopy (SEM), FTIR spectroscopy, and energy dispersive X-ray spectroscopy. The size range of the nanoparticles obtained in such conditions was estimated by SEM images to be 35-45 nm. The parameters influencing the extraction of CuFe2O4 nanoparticles, such as desorption solvent, amount of sorbent, desorption time, sample pH, ionic strength, and extraction time, were investigated and optimized. Under the optimum conditions, a linear calibration curve in the range of 0.75-5.00 μg/L with R2 = 0.9996 was obtained. The LOQ (10Sb) and LOD (3Sb) of the method were 0.75 and 0.25 μg/L (n = 3), respectively. The RSD for a water sample spiked with 1 μg/L rhodamine B was 3% (n = 5). The method was applied for the determination of rhodamine B in tap water, dishwashing foam, dishwashing liquid, and shampoo samples. The relative recovery percentages for these samples were in the range of 95-99%.

Thermodynamic analysis of in situ gasification-chemical looping combustion (iG-CLC) of Indian coal.

PubMed

Suresh, P V; Menon, Kavitha G; Prakash, K S; Prudhvi, S; Anudeep, A

2016-10-01

Chemical looping combustion (CLC) is an inherent CO 2 capture technology. It is gaining much interest in recent years mainly because of its potential in addressing climate change problems associated with CO 2 emissions from power plants. A typical chemical looping combustion unit consists of two reactors-fuel reactor, where oxidation of fuel occurs with the help of oxygen available in the form of metal oxides and, air reactor, where the reduced metal oxides are regenerated by the inflow of air. These oxides are then sent back to the fuel reactor and the cycle continues. The product gas from the fuel reactor contains a concentrated stream of CO 2 which can be readily stored in various forms or used for any other applications. This unique feature of inherent CO 2 capture makes the technology more promising to combat the global climate changes. Various types of CLC units have been discussed in literature depending on the type of fuel burnt. For solid fuel combustion three main varieties of CLC units exist namely: syngas CLC, in situ gasification-CLC (iG-CLC) and chemical looping with oxygen uncoupling (CLOU). In this paper, theoretical studies on the iG-CLC unit burning Indian coal are presented. Gibbs free energy minimization technique is employed to determine the composition of flue gas and oxygen carrier of an iG-CLC unit using Fe 2 O 3 , CuO, and mixed carrier-Fe 2 O 3 and CuO as oxygen carriers. The effect of temperature, suitability of oxygen carriers, and oxygen carrier circulation rate on the performance of a CLC unit for Indian coal are studied and presented. These results are analyzed in order to foresee the operating conditions at which economic and smooth operation of the unit is expected.

Sliding friction and wear behavior of high entropy alloys at room and elevated temperatures

NASA Astrophysics Data System (ADS)

Kadhim, Dheyaa

Structure-tribological property relations have been studied for five high entropy alloys (HEAs). Microhardness, room and elevated (100°C and 300°C) temperature sliding friction coefficients and wear rates were determined for five HEAs: Co0.5 Cr Cu0.5 Fe Ni1.5 Al Ti0.4; Co Cr Fe Ni Al0.25 Ti0.75; Ti V Nb Cr Al; Al0.3CoCrFeNi; and Al0.3CuCrFeNi2. Wear surfaces were characterized with scanning electron microscopy and micro-Raman spectroscopy to determine the wear mechanisms and tribochemical phases, respectively. It was determined that the two HEAs Co0.5 Cr Cu0.5 Fe Ni1.5 Al Ti0.4 and Ti V Nb Cr Al exhibit an excellent balance of high hardness, low friction coefficients and wear rates compared to 440C stainless steel, a currently used bearing steel. This was attributed to their more ductile body centered cubic (BCC) solid solution phase along with the formation of tribochemical Cr oxide and Nb oxide phases, respectively, in the wear surfaces. This study provides guidelines for fabricating novel, low-friction, and wear-resistant HEAs for potential use at room and elevated temperatures, which will help reduce energy and material losses in friction and wear applications.

The sources and evolution of mineralising fluids in iron oxide-copper-gold systems, Norrbotten, Sweden: Constraints from Br/Cl ratios and stable Cl isotopes of fluid inclusion leachates

NASA Astrophysics Data System (ADS)

Gleeson, S. A.; Smith, M. P.

2009-10-01

We have analysed the halogen concentrations and chlorine stable isotope composition of fluid inclusion leachates from three spatially associated Fe-oxide ± Cu ± Au mineralising systems in Norrbotten, Sweden. Fluid inclusions in late-stage veins in Fe-oxide-apatite deposits contain saline brines and have a wide range of Br/Cl molar ratios, from 0.2 to 1.1 × 10 -3 and δ 37Cl values from -3.1‰ to -1.0‰. Leachates from saline fluid inclusions from the Greenstone and Porphyry hosted Cu-Au prospects have Br/Cl ratios that range from 0.2 to 0.5 × 10 -3 and δ 37Cl values from -5.6‰ to -1.3‰. Finally, the Cu-Au deposits hosted by the Nautanen Deformation Zone (NDZ) have Br/Cl molar ratios from 0.4 to 1.1 × 10 -3 and δ 37Cl values that range from -2.4‰ to +0.5‰, although the bulk of the data fall within 0‰ ± 0.5‰. The Br/Cl ratios of leachates are consistent with the derivation of salinity from magmatic sources or from the dissolution of halite. Most of the isotopic data from the Fe-oxide-apatite and Greenstone deposits are consistent with a mantle derived source of the chlorine, with the exception of the four samples with the most negative values. The origin of the low δ 37Cl values in these samples is unknown but we suggest that there may have been some modification of the Cl-isotope signature due to fractionation between the mineralising fluids and Cl-rich silicate assemblages found in the alteration haloes around the deposits. If such a process has occurred then a modified crustal source of the chlorine for all the samples cannot be ruled out although the amount of fractionation necessary to generate the low δ 37Cl values would be significantly larger. The source of Cl in the NDZ deposits has a crustal signature, which suggests the Cl in this system may be derived from (meta-) evaporites or from input from crustal melts such as granitic pegmatites of the Lina Suite.

Synthesis of Multimetal-Graphene Composite by Mechanical Milling

NASA Astrophysics Data System (ADS)

Saiphaneendra, Bachu; Srivastava, Avi Krishna; Srivastava, Chandan

2016-10-01

Multimetal-graphene composites were synthesized using the ball milling technique. To prepare the composite, graphite powder was mixed with Fe, Cr, Co, Cu and Mg powders. This mixture was then mechanically milled for 35 h in toluene medium. After milling, the multimetal-graphite mixture was mixed with sodium lauryl sulfate and sonicated for 2 h. Sonication led to the exfoliation of graphene sheets. Formation of graphene was confirmed from x-ray diffraction and Raman spectroscopy. Transmission electron microscopy-based analysis revealed the formation of multimetal deposits over the graphene surface. Compositional analysis of the multimetal deposits revealed fairly uniform distribution of all the five component metal atoms over the graphene sheet. The average composition of the multimetal deposit was determined to be 11.4 ± 4 at.% Mg, 33.8 ± 19 at.% Cr, 21.8 ± 16 at.% Fe, 9.4 ± 5.7 at.% Co and 23.6 ± 12 at.% Cu.

Development of ultrafine Ti-Fe-Sn in-situ composite with enhanced plasticity

NASA Astrophysics Data System (ADS)

Mondal, B.; Samal, S.; Biswas, K.; Govind

2012-01-01

The present investigation is aimed at developing ultrafine eutectic/dendrite Ti-Fe-Sn in-situ composite with balanced combination of strength and plasticity. It also studies the microstructure evolution in the series of hypereutectic Ti-Fe-Sn ternary alloys. Sn concentration of these alloys has been varied from 0 - 10 atom% in the binary alloy (Ti71Fe29) keeping the Ti concentration fixed. These alloys have been prepared by arc melting under an Ar atmosphere on a water-cooled Cu hearth, which are subsequently suction cast in a split Cu-mold under an Ar atmosphere. Detailed X-ray diffraction (XRD) study shows the presence of TiFe, β-Ti, and Ti3Sn phases. The SEM micrographs reveal that the microstructures consist of fine scale eutectic matrix (β-Ti and TiFe) with primary dendrite phases (TiFe and/or Ti3Sn) depending on concentration of Sn. α -Ti forms as a eutectoid reaction product of β-Ti. The room temperature uniaxial compressive test reveals simultaneous improvement in the strength (1942 MPa) and plasticity (13.1 %) for Ti71Fe26Sn3 ternary alloy. The fracture surface indicates a ductile mode of fracture for the alloy.

Attrition Resistant Fischer-Tropsch Catalysts Based on FCC Supports

DOE Office of Scientific and Technical Information (OSTI.GOV)

Adeyiga, Adeyinka

2010-02-05

Commercial spent fluid catalytic cracking (FCC) catalysts provided by Engelhard and Albemarle were used as supports for Fe-based catalysts with the goal of improving the attrition resistance of typical F-T catalysts. Catalysts with the Ruhrchemie composition (100 Fe/5 Cu/4.2 K/25 spent FCC on mass basis) were prepared by wet impregnation. XRD and XANES analysis showed the presence of Fe{sub 2}O{sub 3} in calcined catalysts. FeC{sub x} and Fe{sub 3}O{sub 4} were present in the activated catalysts. The metal composition of the catalysts was analyzed by ICP-MS. F-T activity of the catalysts activated in situ in CO at the same conditionsmore » as used prior to the attrition tests was measured using a fixed bed reactor at T = 573 K, P = 1.38 MPa and H{sub 2}:CO ratio of 0.67. Cu and K promoted Fe supported over Engelhard provided spent FCC catalyst shows relatively good attrition resistance (8.2 wt% fines lost), high CO conversion (81%) and C{sub 5}+ hydrocarbons selectivity (18.3%).« less

Complex impedance analyses and magnetoelectric effect in ferrite ferroelectric composite ceramics

NASA Astrophysics Data System (ADS)

Patankar, K. K.; Kanade, S. A.; Padalkar, D. S.; Chougule, B. K.

2007-02-01

Magnetoelectric (ME) composites yBa0.8Pb0.2TiO3 (1-y)CuFe2O4 are prepared by ceramic method. The component phases are prepared from two different routes, viz. CuFe2O4 (ferrite phase) is prepared by oxalate precursor route and Ba0.8Pb0.2TiO3 (ferroelectric phase) by solid-state reaction route. No intermediate phases are observed in the composites containing these ferrite and ferroelectric phases. ME conversion factor (measure of ME effect) is found to be enhanced compared to those reported in the composites, in which the component phases were prepared by only one route, i.e. solid-state reaction route. The results on ME conversion are well accounted by measuring the complex impedance and analyzing their Nyquist plots.

Formation of nickel and copper ferrites in ceramics: a potential reaction in the reuse of iron-rich sludge incineration ash.

PubMed

Shih, Kaimin

2012-12-01

This study investigates potential solid-state reactions for the stabilization of hazardous metals when reusing the incineration ash from chemically enhanced primary treatment (CEPT) sludge to fabricate ceramic products. Nickel and copper were used as examples of hazardous metals, and the iron content in the reaction system was found to play a major role in incorporating these hazardous metals into their ferrite phases (NiFe2O4 and CuFe2O4). The results from three-hour sintering experiments on NiO + Fe2O3 and CuO + Fe2O3 systems clearly demonstrate the potential for initiating metal incorporation mechanisms using an iron-containing precursor at attainable ceramic sintering temperatures (above 750 degrees C). Both ferrite phases were examined using a prolonged leaching experiment modified from the widely used toxicity characteristic leaching procedure (TCLP) to evaluate their long-term metal leachability. The leaching results indicate that both the NiFe2O4 and the CuFe2O4 products were significantly superior to their oxide forms in immobilizing hazardous metals.

Moving Fe2+ from ferritin ion channels to catalytic OH centers depends on conserved protein cage carboxylates

PubMed Central

Behera, Rabindra K.; Theil, Elizabeth C.

2014-01-01

Ferritin biominerals are protein-caged metabolic iron concentrates used for iron–protein cofactors and oxidant protection (Fe2+ and O2 sequestration). Fe2+ passage through ion channels in the protein cages, like membrane ion channels, required for ferritin biomineral synthesis, is followed by Fe2+ substrate movement to ferritin enzyme (Fox) sites. Fe2+ and O2 substrates are coupled via a diferric peroxo (DFP) intermediate, λmax 650 nm, which decays to [Fe3+–O–Fe3+] precursors of caged ferritin biominerals. Structural studies show multiple conformations for conserved, carboxylate residues E136 and E57, which are between ferritin ion channel exits and enzymatic sites, suggesting functional connections. Here we show that E136 and E57 are required for ferritin enzyme activity and thus are functional links between ferritin ion channels and enzymatic sites. DFP formation (Kcat and kcat/Km), DFP decay, and protein-caged hydrated ferric oxide accumulation decreased in ferritin E57A and E136A; saturation required higher Fe2+ concentrations. Divalent cations (both ion channel and intracage binding) selectively inhibit ferritin enzyme activity (block Fe2+ access), Mn2+ << Co2+ < Cu2+ < Zn2+, reflecting metal ion–protein binding stabilities. Fe2+–Cys126 binding in ferritin ion channels, observed as Cu2+–S–Cys126 charge-transfer bands in ferritin E130D UV-vis spectra and resistance to Cu2+ inhibition in ferritin C126S, was unpredicted. Identifying E57 and E136 links in Fe2+ movement from ferritin ion channels to ferritin enzyme sites completes a bucket brigade that moves external Fe2+ into ferritin enzymatic sites. The results clarify Fe2+ transport within ferritin and model molecular links between membrane ion channels and cytoplasmic destinations. PMID:24843174

Graphene-based copper oxide thin film nanostructures as high-efficiency photocathode for p-type dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Kilic, Bayram; Turkdogan, Sunay; Astam, Aykut; Baran, Sümeyra Seniha; Asgin, Mansur; Cebeci, Hulya; Urk, Deniz

2017-10-01

Graphene-based p-type dye-sensitized solar cells (p-DSSCs) have been proposed and fabricated using copper oxide urchin-like nanostructures (COUN) as photocathode with an FeS2 counter electrode (CE). COUN composed of Cu2O core sphere and CuO shell nanorods with overall diameters of 2 to 4 μm were grown by a simple hydrothermal method with self-assemble nucleation. It was figured out that the formation of copper oxide core/shell structures could be adjusted by an ammonia additive leading to pH change of the precursor solution. In addition to a photocathode, we also demonstrated FeS2 thin films as an efficient CE material alternative to the conventional Pt CEs in DSSCs. FeS2 nanostructures, with diameters of 50 to 80 nm, were synthesized by a similar hydrothermal approach. FeS2 nanostructures are demonstrated to be an outstanding CE material in p-DSSCs. We report graphene/COUN as photocathode and Pt/FeS2 as CE in p-DSSCs, and results show that the synergetic combination of electrodes in each side (increased interconnectivity between COUN and graphene layer, high surface area, and high catalytic activity of FeS2) increased the power conversion efficiency from 1.56% to 3.14%. The excellent performances of COUN and FeS2 thin film in working and CEs, respectively, make them unique choices among the various photocathode and CE materials studied.

Fractionation of Fe isotopes during Fe(II) oxidation by a marine photoferrotroph is controlled by the formation of organic Fe-complexes and colloidal Fe fractions

NASA Astrophysics Data System (ADS)

Swanner, Elizabeth D.; Wu, Wenfang; Schoenberg, Ronny; Byrne, James; Michel, F. Marc; Pan, Yongxin; Kappler, Andreas

2015-09-01

Much interest exists in finding mineralogical, organic, morphological, or isotopic biosignatures for Fe(II)-oxidizing bacteria (FeOB) that are retained in Fe-rich sediments, which could indicate the activity of these organisms in Fe-rich seawater, more common in the Precambrian Era. To date, the effort to establish a clear Fe isotopic signature in Fe minerals produced by Fe(II)-oxidizing metabolisms has been thwarted by the large kinetic fractionation incurred as freshly oxidized aqueous Fe(III) rapidly precipitates as Fe(III) (oxyhydr)oxide minerals at near neutral pH. The Fe(III) (oxyhydr)oxide minerals resulting from abiotic Fe(II) oxidation are isotopically heavy compared to the Fe(II) precursor and are not clearly distinguishable from minerals formed by FeOB isotopically. However, in marine hydrothermal systems and Fe(II)-rich springs the minerals formed are often isotopically lighter than expected considering the fraction of Fe(II) that has been oxidized and experimentally-determined fractionation factors. We measured the Fe isotopic composition of aqueous Fe (Feaq) and the final Fe mineral (Feppt) produced in batch experiment using the marine Fe(II)-oxidizing phototroph Rhodovulum iodosum. The δ56Feaq data are best described by a kinetic fractionation model, while the evolution of δ56Feppt appears to be controlled by a separate fractionation process. We propose that soluble Fe(III), and Fe(II) and Fe(III) extracted from the Feppt may act as intermediates between Fe(II) oxidation and Fe(III) precipitation. Based on 57Fe Mössbauer spectroscopy, extended X-ray absorption fine structure (EXAFS) spectroscopy, and X-ray total scattering, we suggests these Fe phases, collectively Fe(II/III)interm, may consist of organic-ligand bound, sorbed, and/or colloidal Fe(II) and Fe(III) mineral phases that are isotopically lighter than the final Fe(III) mineral product. Similar intermediate phases, formed in response to organic carbon produced by FeOB and inorganic ligands (e.g., SiO44- or PO43-), may form in many natural Fe(II)-oxidizing environments. We propose that the formation of these intermediates is likely to occur in organic-rich systems, and thus may have controlled the ultimate isotopic composition of Fe minerals in systems where Fe(II) was being oxidized by or in the presence of microbes in Earth's past.

Chemical dynamics of acidity and heavy metals in a mine water-polluted soil during decontamination using clean water.

PubMed

Chen, A; Lin, C; Lu, W; Ma, Y; Bai, Y; Chen, H; Li, J

2010-03-15

A column leaching experiment was conducted to investigate the chemical dynamics of the percolating water and washed soil during decontamination of an acidic mine water-polluted soil. The results show that leaching of the contaminated soil with clean water rapidly reduced soluble acidity and ion concentrations in the soils. However, only <20% of the total actual acidity in the soil column was eliminated after 30 leaching cycles. It is likely that the stored acidity continues to be released to the percolating water over a long period of time. During the column leaching, dissolved Cu and Pb were rapidly leached out, followed by mobilization of colloidal Cu and Pb from the exchangeable and the oxide-bound fractions as a result of reduced ionic strength in the soil solution. The soluble Fe contained in the soil was rare, probably because the soil pH was not sufficiently low; marked mobility of colloidal Fe took place after the ionic strength of the percolating water was weakened and the mobilized Fe was mainly derived from iron oxides. In contrast with Cu, Pb and Fe, the concentration of leachate Zn and Mn showed a continuously decreasing trend during the entire period of the experiment. (c) 2009 Elsevier B.V. All rights reserved.

Chemical composition and varieties of fahlore-group minerals from Oligocene mineralization in the Rhodope area, Southern Bulgaria and Northern Greece

NASA Astrophysics Data System (ADS)

Repstock, Alexander; Voudouris, Panagiotis; Zeug, Manuela; Melfos, Vasilios; Zhai, Mingguo; Li, Hongzhong; Kartal, Tamara; Matuszczak, Julia

2016-02-01

Fahlore-group minerals in Oligocene magmatic-hydrothermal deposits from the central and eastern Rhodope area, Bulgaria and Greece (e.g. porphyry-epithermal systems at Pagoni Rachi, Maronia and Kassiteres-Sapes, polymetallic epithermal high- and intermediate-sulfidation veins at Kirki, Perama Hill, Mavrokoryfi, Pefka, Zvezdel-Pcheloyad and Madzharovo, skarn-carbonate replacement deposits at Laki, Davidkovo, Madan, Enyovche and intrusion-related deposits at Kimmeria), cover the whole range of the tetrahedrite-tennantite solid solution series and are dominated by zincian and ferroan varieties reflecting deposition from Zn-(and Fe)-rich fluids. The majority of the studied fahlores are "normal" fully-substituted with Cu (+Ag) close to 10 apfu. However, high-sulfidation epithermal deposits in Greece contain "Cu-excess" tetrahedrite-tennantite; those with extreme high Cu-excess > Fe + Zn occur in transitional high- to intermediate-sulfidation systems, whereas low "Cu-excess" tetrahedrite-tennantite with Zn > Cu-excess + Fe and Fe > Cu-excess + Zn are part of tellurides-bearing intermediate-sulfidation assemblages. The epithermal St. Demetrios and Pefka deposits display the most Cu-rich tetrahedrites (11.039 apfu Cu) and tennantite (11.784 apfu Cu) worldwide. Although Ag substitutes for Cu in the structure of Ag-rich tetrahedrite in several deposits, freibergite with 6.800 apfu Ag occurs only at Mavrokoryfi; in particular, the cadmian freibergite at Mavrokoryfi is the second finding of this variety worldwide. Tellurium-bearing fahlore varieties occur in association with enargite/luzonite and native gold in high-sulfidation ore assemblages. Tetravalent tellurium substitutes for trivalent As and Sb in goldfieldite and Te-rich tennantite and tetrahedrite at Mavrokoryfi, Perama Hill, St. Demetrios and Pefka deposits. Goldfieldite at Mavrokoryfi and Perama Hill is remarkably Te-rich (up to 3.766 apfu and 3.711 apfu Te, respectively), with total metal content of 10.591 apfu and are the closest natural occurrence to the theoretical synthetic endmember Cu10Te4S13. The telluride-bearing fahlores in several epithermal deposits in Greece do not represent decomposition products of early goldfieldite. They are possibly the result of a new influx of Te-rich magmatic volatiles in the system. Decreasing Te (and Cu)-content in tetrahedrite-tennantite solid solution series reflects an evolution from initial high-T, high-sulfidation, oxidizing conditions, towards lower-T and lower-sulfidation, more reduced conditions with time. Fahlores, although they are minor constituents in the studied mineralization types, are carriers of Ag (and Au in goldfieldite) and may be used as an exploration tool, since they are closely associated with either native gold, gold-silver tellurides or Ag-sulfosalts.

Oxidation Potentials in Matte Smelting of Copper and Nickel

NASA Astrophysics Data System (ADS)

Matousek, Jan W.

2014-09-01

The oxidation potential, given as the base-ten logarithm of the oxygen partial pressure in bars and the temperature [log pO2/ T, °C], defines the state of oxidation of pyrometallurgical extraction and refining processes. This property varies from copper making, [-6/1150]; to lead/zinc smelting, [-10/1200]; to iron smelting, [-13/1600]. The current article extends the analysis to the smelting of copper and nickel/copper sulfide concentrates to produce mattes of the type Cu(Ni)FeS(O) and iron silicate slags, FeOxSiO2—with oxidation potentials of [-7.5/1250].

Unique phase identification of trimetallic copper iron manganese oxygen carrier using simultaneous differential scanning calorimetry/thermogravimetric analysis during chemical looping combustion reactions with methane

DOE PAGES

Benincosa, William; Siriwardane, Ranjani; Tian, Hanjing; ...

2017-07-05

Chemical looping combustion (CLC) is a promising combustion technology that generates heat and sequestration-ready carbon dioxide that is undiluted by nitrogen from the combustion of carbonaceous fuels with an oxygen carrier, or metal oxide. This process is highly dependent on the reactivity and stability of the oxygen carrier. The development of oxygen carriers remains one of the major barriers for commercialization of CLC. Synthetic oxygen carriers, consisting of multiple metal components, have demonstrated enhanced performance and improved CLC operation compared to single metal oxides. However, identification of the complex mixed metal oxide phases that form after calcination or during CLCmore » reactions has been challenging. Without an understanding of the dominant metal oxide phase, it is difficult to determine reaction parameters and the oxygen carrier reduction pathway, which are necessary for CLC reactor design. This is particularly challenging for complex multi-component oxygen carriers such as copper iron manganese oxide (CuFeMnO 4). This study aims to differentiate the unique phase formation of a highly reactive, complex trimetallic oxygen carrier, CuFeMnO 4, from its single and bimetallic counterparts using thermochemical and reaction data obtained from simultaneous differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) during temperature programmed reductions (TPR) with methane. DSC/TGA experiments during TPR with methane provides heat flow data and corresponding reaction rate data that can be used to determine reaction routes and mechanisms during methane reduction. Furthermore, non-isothermal TPR data provides the advantage of distinguishing reactions that may not be observable in isothermal analysis. The detailed thermochemical and reaction data, obtained during TPR with methane, distinguished a unique reduction pathway for CuFeMnO 4 that differed from its single and bimetallic counterparts. This is remarkable since X-ray diffraction (XRD) data alone could not be used to distinguish the reactive trimetallic oxide phase due to overlapping peaks from various single and mixed metal oxides. The unique reduction pathway of CuFeMnO 4 was further characterized in this study using in-situ XRD TPR with methane to determine changes in the dominant trimetallic phase that influenced the thermochemical and reaction rate data.« less

Unique phase identification of trimetallic copper iron manganese oxygen carrier using simultaneous differential scanning calorimetry/thermogravimetric analysis during chemical looping combustion reactions with methane

DOE Office of Scientific and Technical Information (OSTI.GOV)

Benincosa, William; Siriwardane, Ranjani; Tian, Hanjing

Chemical looping combustion (CLC) is a promising combustion technology that generates heat and sequestration-ready carbon dioxide that is undiluted by nitrogen from the combustion of carbonaceous fuels with an oxygen carrier, or metal oxide. This process is highly dependent on the reactivity and stability of the oxygen carrier. The development of oxygen carriers remains one of the major barriers for commercialization of CLC. Synthetic oxygen carriers, consisting of multiple metal components, have demonstrated enhanced performance and improved CLC operation compared to single metal oxides. However, identification of the complex mixed metal oxide phases that form after calcination or during CLCmore » reactions has been challenging. Without an understanding of the dominant metal oxide phase, it is difficult to determine reaction parameters and the oxygen carrier reduction pathway, which are necessary for CLC reactor design. This is particularly challenging for complex multi-component oxygen carriers such as copper iron manganese oxide (CuFeMnO 4). This study aims to differentiate the unique phase formation of a highly reactive, complex trimetallic oxygen carrier, CuFeMnO 4, from its single and bimetallic counterparts using thermochemical and reaction data obtained from simultaneous differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) during temperature programmed reductions (TPR) with methane. DSC/TGA experiments during TPR with methane provides heat flow data and corresponding reaction rate data that can be used to determine reaction routes and mechanisms during methane reduction. Furthermore, non-isothermal TPR data provides the advantage of distinguishing reactions that may not be observable in isothermal analysis. The detailed thermochemical and reaction data, obtained during TPR with methane, distinguished a unique reduction pathway for CuFeMnO 4 that differed from its single and bimetallic counterparts. This is remarkable since X-ray diffraction (XRD) data alone could not be used to distinguish the reactive trimetallic oxide phase due to overlapping peaks from various single and mixed metal oxides. The unique reduction pathway of CuFeMnO 4 was further characterized in this study using in-situ XRD TPR with methane to determine changes in the dominant trimetallic phase that influenced the thermochemical and reaction rate data.« less

A method for preparing ferric activated carbon composites adsorbents to remove arsenic from drinking water.

PubMed

Zhang, Qiao Li; Lin, Y C; Chen, X; Gao, Nai Yun

2007-09-30

Iron oxide/activated carbon (FeO/AC) composite adsorbent material, which was used to modify the coal-based activated carbon (AC) 12 x 40, was prepared by the special ferric oxide microcrystal in this study. This composite can be used as the adsorbent to remove arsenic from drinking water, and Langmuir isotherm adsorption equation well describes the experimental adsorption isotherms. Then, the arsenic desorption can subsequently be separated from the medium by using a 1% aqueous NaOH solution. The apparent characters and physical chemistry performances of FeO/AC composite were investigated by X-ray diffraction (XRD), nitrogen adsorption, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Batch and column adsorption experiments were carried out to investigate and compare the arsenic removal capability of the prepared FeO/AC composite material and virgin activated carbon. It can be concluded that: (1) the main phase present in this composite are magnetite (Fe(3)O(4)), maghemite (gamma-Fe(2)O(3)), hematite (alpha-Fe(2)O(3)) and goethite (alpha-FeO(OH)); (2) the presence of iron oxides did not significantly affect the surface area or the pore structure of the activated carbon; (3) the comparisons between the adsorption isotherms of arsenic from aqueous solution onto the composite and virgin activated carbon showed that the FeO/AC composite behave an excellent capacity of adsorption arsenic than the virgin activated carbon; (4) column adsorption experiments with FeO/AC composite adsorbent showed that the arsenic could be removed to below 0.01 mg/L within 1250 mL empty bed volume when influent concentration was 0.5mg/L.

Synergistic effect of biogenic Fe3+ coupled to S° oxidation on simultaneous bioleaching of Cu, Co, Zn and As from hazardous Pyrite Ash Waste.

PubMed

Panda, Sandeep; Akcil, Ata; Mishra, Srabani; Erust, Ceren

2017-03-05

Pyrite ash, a waste by-product formed during roasting of pyrite ores, is a good source of valuable metals. The waste is associated with several environmental issues due to its dumping in sea and/or land filling. Although several other management practices are available for its utilization, the waste still awaits and calls for an eco-friendly biotechnological application for metal recovery. In the present study, chemolithotrophic meso-acidophilic iron and sulphur oxidisers were evaluated for the first time towards simultaneous mutli-metal recovery from pyrite ash. XRD and XRF analysis indicated higher amount of Hematite (Fe 2 O 3 ) in the sample. ICP-OES analysis indicated concentrations of Cu>Zn>Co>As that were considered for bioleaching. Optimization studies indicated Cu - 95%, Co - 97%, Zn - 78% and As - 60% recovery within 8days at 10% pulp density, pH - 1.75, 10% (v/v) inoculum and 9g/L Fe 2+ . The productivity of the bioleaching system was found to be Cu - 1696ppm/d (12% dissolution/d), Co - 338ppm/d (12.2% dissolution/d), Zn k 576ppm/d (9.8% dissolution/d) and As - 75ppm/d (7.5% dissolution/d). Synergistic actions for Fe 2+ - S° oxidation by iron and sulphur oxidisers were identified as the key drivers for enhanced metal dissolution from pyrite ash sample. Copyright © 2016 Elsevier B.V. All rights reserved.

Geochemical and iron isotopic insights into hydrothermal iron oxyhydroxide deposit formation at Loihi Seamount

NASA Astrophysics Data System (ADS)

Rouxel, Olivier; Toner, Brandy; Germain, Yoan; Glazer, Brian

2018-01-01

Low-temperature hydrothermal vents, such as those encountered at Loihi Seamount, harbor abundant microbial communities and provide ideal systems to test hypotheses on biotic versus abiotic formation of hydrous ferric oxide (FeOx) deposits at the seafloor. Hydrothermal activity at Loihi Seamount produces abundant microbial mats associated with rust-colored FeOx deposits and variably encrusted with Mn-oxyhydroxides. Here, we applied Fe isotope systematics together with major and trace element geochemistry to study the formation mechanisms and preservation of such mineralized microbial mats. Iron isotope composition of warm (<60 °C), Fe-rich and H2S-depleted hydrothermal fluids yielded δ56Fe values near +0.1‰, indistinguishable from basalt values. Suspended particles in the vent fluids and FeOx deposits recovered nearby active vents yielded systematically positive δ56Fe values. The enrichment in heavy Fe isotopes between +1.05‰ and +1.43‰ relative to Fe(II) in vent fluids suggest partial oxidation of Fe(II) during mixing of the hydrothermal fluid with seawater. By comparing the results with experimentally determined Fe isotope fractionation factors, we determined that less than 20% of Fe(II) is oxidized within active microbial mats, although this number may reach 80% in aged or less active deposits. These results are consistent with Fe(II) oxidation mediated by microbial processes considering the expected slow kinetics of abiotic Fe oxidation in low oxygen bottom water at Loihi Seamount. In contrast, FeOx deposits recovered at extinct sites have distinctly negative Fe-isotope values down to -1.77‰ together with significant enrichment in Mn and occurrence of negative Ce anomalies. These results are best explained by the near-complete oxidation of an isotopically light Fe(II) source produced during the waning stage of hydrothermal activity under more oxidizing conditions. Light Fe isotope values of FeOx are therefore generated by subsurface precipitation of isotopically heavy Fe-oxides rather than by the activity of dissimilatory Fe reduction in the subsurface. Overall, Fe-isotope compositions of microbial mats at Loihi Seamount display a remarkable range between -1.2‰ and +1.6‰ which indicate that Fe isotope compositions of hydrothermal Fe-oxide precipitates are particularly sensitive to local environmental conditions where they form, and are less sensitive to abiotic versus biotic origins. It follows that FeOx deposits at Loihi Seamount provides important modern analogues for ancient seafloor Fe-rich deposits allowing for testing hypotheses about the biogeochemical cycling of Fe isotopes on early Earth.

Comparative microstructural and corrosion development of VCrNiCoFeCu equiatomic multicomponent alloy produced by induction melting and spark plasma sintering

NASA Astrophysics Data System (ADS)

Fazakas, É.; Heczel, A.; Molnár, D.; Varga, B.; Zadorozhnyy, V.; Vida, Á.

2018-03-01

The present study focuses on the corrosion behavior of a single-phase FCC high entropy alloy (VCrNiCoFeCu) casted by two different methods: induction melting and spark plasma sintering. The corrosion resistance has been evaluated using immersion tests in 3.5% NaCl solution, the potentiodynamic polarization measurements and the results are compared how is dependent the corrosion rate as a function of the production methods. Our results show that induction melted sample is stable in salty environment. On the other hand, based on the changes of polarization curves, there must be an evolution of oxide films on the SPSed sample until reaching the stable oxide layer.

Nucleation and growth of oxide islands during the initial-stage oxidation of (100)Cu-Pt alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luo, Langli; Zhou, Guangwen, E-mail: gzhou@binghamton.edu; Kang, Yihong

2015-02-14

The initial-stage oxidation of (100) Cu-Pt alloys has been examined by in situ environmental transmission electron microscopy and ex situ atomic force microscopy (AFM). It is shown that the oxidation proceeds via the nucleation and growth of Cu{sub 2}O islands that show dependence on the alloy composition and oxidation temperature. The kinetic measurements on the oxide nucleation reveal that both the nucleation density and surface coverage of Cu{sub 2}O islands can be promoted by alloying more Pt in the Cu-Pt alloys. Increasing the oxidation temperature above 700 °C results in the growth of large Cu{sub 2}O islands that transits to amore » dendritic growth morphology. The ex situ AFM studies reveal that the nucleation of oxide islands can occur on surface terraces and the subsequent oxide growth depletes local terrace Cu atoms that results in the formation of surface pits.« less

Fabrication and electrochemical properties of activated CNF/Cu x Mn1- x Fe2O4 composite nanostructures

NASA Astrophysics Data System (ADS)

Nilmoung, Sukanya; Sonsupap, Somchai; Sawangphruk, Montree; Maensiri, Santi

2018-06-01

This work reports the fabrication and electrochemical properties of activated carbon nanofibers composited with copper manganese ferrite (ACNF/Cu x Mn1- x Fe2O4: x = 0.0, 0.2, 0.4, 0.6, 0.8) nanostructures. The obtained samples were characterized by means of X-ray diffraction, field emission scanning electron microscopy, Brunauer-Emmett-Teller analyzer, thermal gravimetric analysis, X-ray photoemission spectroscopy, and X-ray absorption spectroscopy. The supercapacitive behavior of the electrodes is tested using cyclic voltammetery, galvanostatic charge-discharge and electrochemical impedance spectroscopy. By varying ` x', the highest specific capacitance of 384 F/g at 2 mV/s using CV and 314 F/g at 2 A/g using GCD are obtained for the x = 0.2 electrode. The second one of 235 F/g at 2 mV/s using CV and 172 F/g at 2 A/g using GCD are observed for x = 0.8 electrode. The corresponding energy densities are 74 and 41 Wh/kg, respectively. It is observed that the cyclic stability of the prepared samples strongly depend on the amount of carbon, while the specific capacitance was enhanced by the sample with nearly proportional amount between carbon and CuMnFe2O4. Such results may arise from the synergetic effect between CuMnFe2O4 and ACNF.

Cladding glass ceramic for use in high powered lasers

DOEpatents

Marker, A.J.; Campbell, J.H.

1998-02-17

A Cu-doped/Fe-doped low expansion glass ceramic composition comprising in Wt. %: SiO{sub 2} 50--65; Al{sub 2}O{sub 3} 18--27; P{sub 2}O{sub 5} 0--10; Li{sub 2}O 2--6; Na{sub 2}O 0--2; K{sub 2}O 0--2; B{sub 2}O{sub 3} 0--1; MgO 0--4; ZnO 0--5; CaO 0--4; BaO 0--5; TiO{sub 2} 1--3; ZrO{sub 3} 1--3; As{sub 2}O{sub 3} 0--1.5; Sb{sub 2}O{sub 3} 0--1.5; CuO 0--3; and Fe{sub 2}O{sub 3} 0--1 wherein the total amount of SiO{sub 2}, Al{sub 2}O{sub 3} and P{sub 2}O{sub 5} is 80--89 wt. %, and said glass ceramic contains as a dopant 0.1--3 wt. % CuO, 0.1--1 wt. % Fe{sub 2}O{sub 3} or a combined CuO+Fe{sub 2}O{sub 3} amount of 0.1--4 wt. %. The glass ceramic composition is suitable for use as a cladding material for solid laser energy storage mediums as well as for use in beam attenuators for measuring laser energy level and beam blocks or beam dumps used for absorbing excess or unused laser energy.

Cladding glass ceramic for use in high powered lasers

DOEpatents

Marker, Alexander J.; Campbell, John H.

1998-01-01

A Cu-doped/Fe-doped low expansion glass ceramic composition comprising in Wt. %: SiO{sub 2} 50--65; Al{sub 2}O{sub 3} 18--27; P{sub 2}O{sub 5} 0--10; Li{sub 2}O 2--6; Na{sub 2}O 0--2; K{sub 2}O 0--2; B{sub 2}O{sub 3} 0--1; MgO 0--4; ZnO 0--5; CaO 0--4; BaO 0--5; TiO{sub 2} 1--3; ZrO{sub 3} 1--3; As{sub 2}O{sub 3} 0--1.5; Sb{sub 2}O{sub 3} 0--1.5; CuO 0--3; and Fe{sub 2}O{sub 3} 0--1 wherein the total amount of SiO{sub 2}, Al{sub 2}O{sub 3} and P{sub 2}O{sub 5} is 80--89 wt. %, and said glass ceramic contains as a dopant 0.1--3 wt. % CuO, 0.1--1 wt. % Fe{sub 2}O{sub 3} or a combined CuO+Fe{sub 2}O{sub 3} amount of 0.1--4 wt. %. The glass ceramic composition is suitable for use as a cladding material for solid laser energy storage mediums as well as for use in beam attenuators for measuring laser energy level and beam blocks or beam dumps used for absorbing excess or unused laser energy.

Transport current density at temperatures up to 25 K of Cu/Ag composite sheathed 122-type tapes and wires

NASA Astrophysics Data System (ADS)

Liu, Shifa; Lin, Kaili; Yao, Chao; Zhang, Xianping; Dong, Chiheng; Wang, Dongliang; Awaji, Satoshi; Kumakura, Hiroaki; Ma, Yanwei

2017-11-01

The fabrication of iron-based superconductors with high transport critical current density (J c) and low cost is a crucial determinant of whether they can be used for practical applications. In this paper, Cu/Ag composite sheathed Sr0.6K0.4Fe2As2 (Sr122) tapes and Ba0.6K0.4Fe2As2 (Ba122) round wires were fabricated via an ex situ powder-in-tube method and heat-treated by the hot pressing and hot isostatic pressing process respectively. In order to thoroughly reveal the application potential of Cu/Ag composite sheathed ‘122’ iron pnictide superconductors, transport J c of tapes and wires in high fields at temperatures up to 25 K was measured. High transport J c of 4.4 × 104 A cm-2 at 4.2 K and 3.6 × 103 A cm-2 at 20 K in 10 T was achieved in Cu/Ag composite sheathed Sr122 tapes. Transport J c of Ba122 wires is 9.4 × 103 A cm-2 at 4.2 K and 1.9 × 103 A cm-2 at 20 K in 10 T. These results demonstrate the great potential of Cu/Ag composite sheathed ‘122’ iron pnictide superconducting tapes and wires for high-field applications at intermediate temperatures around 20 K, which can be easily obtained by using cryocoolers.

Pb, Cu, and Zn distributions at humic acid-coated metal-oxide surfaces

DOE PAGES

Wang, Yingge; Michel, F. Marc; Choi, Yongseong; ...

2016-05-09

Here, mineral surfaces are often coated by natural organic matter (NOM), which has a major influence on metal-ion sorption and sequestration because of the abundance of binding sites in such coatings and the changes they cause in local nanoscale environments. The effects of NOM coatings on mineral surfaces are, however, still poorly understood at the molecular level due to the complexity of these systems. In this study, we have applied long-period X-ray standing wave-fluorescence yield (LP-XSW-FY) spectroscopy to measure the partitioning of naturally present Cu(II) (0.0226%), Zn(II) (0.009%), and Pb(II) ( 0.0004%) between Elliott Soil Humic Acid (ESHA) coatings andmore » three model single-crystal metal-oxide substrates: α-Al 2O 3 (0 0 0 1), α-Al 2O 3 (1 1 0 2), and α-Fe 2O 3 (0 0 0 1). The competitive sorption effects among these metal ions for binding sites in the ESHA coatings and on the metal-oxide surfaces were investigated as a function of reaction time, calcium content, and solution pH. Pb(II) ions present in the ESHA coatings were found to redistribute to reactive α-Al 2O 3 (1 1 0 2) and α-Fe 2O 3 (0 0 0 1) surfaces after 3 h of reaction (pH = 6.0, [Ca(II)] = 2 mM). Pb(II) partitioning onto these reactive metal-oxide surfaces increased with increasing reaction time (up to 7 d). In addition, the partitioning of Cu(II) and Zn(II) from the ESHA coating to the α-Fe 2O 3 (0 0 0 1) substrate increased slightly with reaction time (2.4% and 3.7% for Cu(II) and Zn(II), respectively, after 3 h and 6.4% and 7.7% for Cu(II) and Zn(II), respectively, after 72 h of reaction time).« less

Structural and functional responses of periphyton and macroinvertebrate communities to ferric Fe, Cu, and Zn in stream mesocosms.

PubMed

Cadmus, Pete; Guasch, Helena; Herdrich, Adam T; Bonet, Berta; Urrea, Gemma; Clements, William H

2018-05-01

Two mesocosm experiments were conducted to examine effects of ferric iron (Fe) and mixtures of ferric Fe with aqueous metals (Cu, Zn) on stream benthic communities. Naturally colonized benthic communities were exposed to a gradient of ferric Fe (0, 0.4, 1.0, 2.5, 6.2, and 15.6 mg/L) that bracketed the current US Environmental Protection Agency water quality criterion value (1.0 mg/L). After 10 d of exposure to ferric Fe, total macroinvertebrate abundance, number of taxa, and abundance of all major macroinvertebrate groups (Ephemeroptera, Plecoptera, Trichoptera, and Diptera) were significantly reduced. Heptageniid mayflies and chironomids were especially sensitive to Fe oxide deposition and were significantly reduced at 0.4 and 1.0 mg/L total Fe, respectively. In a second mesocosm experiment, periphyton and macroinvertebrate communities were exposed to ferric Fe (0.60 mg/L) with or without aqueous Cu and Zn at 2 treatment levels: low (0.01 mg/L Cu + 0.1 mg/L Zn) and high (0.05 mg/L Cu + 0.5 mg/L Zn). In contrast to previous research, we observed no evidence of a protective effect of Fe on toxicity of metals. Growth rates and protein content of periphyton were significantly reduced by both ferric Fe and aqueous metals, whereas abundance of heptageniid mayflies (Cinygmula) and whole community metabolism were significantly reduced by ferric Fe alone. We hypothesize that Fe oxides inhibited algal growth and enhanced metal accumulation, leading to a reduction in the quantity and quality of food resources for grazers. Mesocosm experiments conducted using natural benthic communities provide a unique opportunity to quantify the relative importance of indirect physical effects and to develop a better understanding of the relationship between basal food resources and consumers in natural stream ecosystems. Environ Toxicol Chem 2018;37:1320-1329. © 2017 SETAC. © 2017 SETAC.

Ferrate(VI)-prompted removal of metals in aqueous media: mechanistic delineation of enhanced efficiency via metal entrenchment in magnetic oxides.

PubMed

Prucek, Robert; Tuček, Jiří; Kolařík, Jan; Hušková, Ivana; Filip, Jan; Varma, Rajender S; Sharma, Virender K; Zbořil, Radek

2015-02-17

The removal efficiency of heavy metal ions (cadmium(II), Cd(II); cobalt(II), Co(II); nickel(II), Ni(II); copper(II), Cu(II)) by potassium ferrate(VI) (K2FeO4, Fe(VI)) was studied as a function of added amount of Fe(VI) (or Fe) and varying pH. At pH = 6.6, the effective removal of Co(II), Ni(II), and Cu(II) from water was observed at a low Fe-to-heavy metal ion ratio (Fe/M(II) = 2:1) while a removal efficiency of 70% was seen for Cd(II) ions at a high Fe/Cd(II) weight ratio of 15:1. The role of ionic radius and metal valence state was explored by conducting similar removal experiments using Al(III) ions. The unique combination of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), in-field Mössbauer spectroscopy, and magnetization measurements enabled the delineation of several distinct mechanisms for the Fe(VI)-prompted removal of metal ions. Under a Fe/M weight ratio of 5:1, Co(II), Ni(II), and Cu(II) were removed by the formation of MFe2O4 spinel phase and partially through their structural incorporation into octahedral positions of γ-Fe2O3 (maghemite) nanoparticles. In comparison, smaller sized Al(III) ions got incorporated easily into the tetrahedral positions of γ-Fe2O3 nanoparticles. In contrast, Cd(II) ions either did not form the spinel ferrite structure or were not incorporated into the lattic of iron(III) oxide phase due to the distinct electronic structure and ionic radius. Environmentally friendly removal of heavy metal ions at a much smaller dosage of Fe than those of commonly applied iron-containing coagulants and the formation of ferrimagnetic species preventing metal ions leaching back into the environment and allowing their magnetic separation are highlighted.

Reconstruction of the Nd isotope composition of seawater on epicontinental seas: Testing the potential of Fe-Mn oxyhydroxide coatings on foraminifera tests for deep-time investigations

NASA Astrophysics Data System (ADS)

Charbonnier, Guillaume; Pucéat, Emmanuelle; Bayon, Germain; Desmares, Delphine; Dera, Guillaume; Durlet, Christophe; Deconinck, Jean-François; Amédro, Francis; Gourlan, Alexandra T.; Pellenard, Pierre; Bomou, Brahimsamba

2012-12-01

The Fe-Mn oxide fraction leached from deep-sea sediments has been increasingly used to reconstruct the Nd isotope composition of deep water masses, that can be used to track changes in oceanic circulation with a high temporal resolution. Application of this archive to reconstruct the Nd isotope composition of bottom seawater in shallow shelf environments remained however to be tested. Yet as the Nd isotope composition of seawater on continental margins is particularly sensitive to changes in erosional inputs, establishment of neritic seawater Nd isotope evolution around areas of deep water formation would be useful to discriminate the influence of changes in oceanic circulation and in isotopic composition of erosional inputs on the Nd isotope record of deep waters. The purpose of this study is to test the potential of Fe-Mn coatings leached from foraminifera tests to reconstruct the Nd isotope composition of seawater in shelf environments for deep-time intervals. Albian to Turonian samples from two different outcrops have been recovered, from the Paris Basin (Wissant section, northern France) and from the Western Interior Seaway (Hot Spring, South Dakota, USA), that were deposited in epicontinental seas. Rare Earth Element (REE) spectra enriched in middle REEs in the foraminifera leach at Wissant highlight the presence of Fe-Mn oxides. The similarity of the Nd isotopic signal of the Fe-Mn oxide fraction leached from foraminifera tests with that of fish teeth suggests that Fe-Mn oxides coating foraminifera can be good archives of shelf bottom seawater Nd isotopic composition. Inferred bottom shelf water Nd isotope compositions at Wissant range from -8.5 to -9.7 ɛ-units, about 1.5-2 ɛ-units higher than that of the contemporaneous local detrital fraction. At Hot Spring, linear REE spectra characterizing foraminifera leach may point to an absence of authigenic marine Fe-Mn oxide formation in this area during the Late Cenomanian-Early Turonian, consistent with dysoxic to anoxic conditions at Hot Spring, contemporaneous to an Oceanic Anoxic Event. The similarity of the Nd isotopic signal of the carbonate matrix of foraminifera with that of fish teeth suggests that it records the Nd isotope composition of bottom shelf seawater as well. Inferred bottom shelf water Nd isotope compositions at Hot Spring are quite radiogenic, between -7 and -6 ɛ-units, about 2.5-4 ɛ-units higher than that of the contemporaneous local detrital fraction. In contrast, in both sections Fe-Mn oxides leached directly from the decarbonated sediment tend to yield a less radiogenic Nd isotopic composition, typically between 0.2 and 0.8 ɛ-units lower, that is intermediate between that of fish teeth and of the detrital fraction. This suggests the contribution of pre-formed continental Fe-Mn oxides to the Nd isotopic signal, along with authigenic marine oxides, or a detrital contamination during leaching.

A DFT study on the enthalpies of thermite reactions and enthalpies of formation of metal composite oxide

NASA Astrophysics Data System (ADS)

Zhang, Yu-ying; Wang, Meng-jie; Chang, Chun-ran; Xu, Kang-zhen; Ma, Hai-xia; Zhao, Feng-qi

2018-05-01

The standard thermite reaction enthalpies (ΔrHmθ) for seven metal oxides were theoretically analyzed using density functional theory (DFT) under five different functional levels, and the results were compared with experimental values. Through the comparison of the linear fitting constants, mean error and root mean square error, the Perdew-Wang functional within the framework of local density approximation (LDA-PWC) and Perdew-Burke-Ernzerhof exchange-correlation functional within the framework of generalized gradient approximation (GGA-PBE) were selected to further calculate the thermite reaction enthalpies for metal composite oxides (MCOs). According to the Kirchhoff formula, the standard molar reaction enthalpies for these MCOs were obtained and their standard molar enthalpies of formation (ΔfHmθ) were finally calculated. The results indicated that GGA-PBE is the most suitable one out of the total five methods to calculate these oxides. Tungstate crystals present the maximum deviation of the enthalpies of thermite reactions for MCOs and these of their physical metal oxide mixtures, but ferrite crystals are the minimum. The correlation coefficients are all above 0.95, meaning linear fitting results are very precise. And the molar enthalpies of formation for NiMoO4, CuMoO4, PbZrO3 (Pm/3m), PbZrO3 (PBA2), PbZrO3 (PBam), MgZrO3, CdZrO3, MnZrO3, CuWO4 and Fe2WO6 were first obtained as -1078.75, -1058.45, -1343.87, -1266.54, -1342.29, -1333.03, -1210.43, -1388.05, -1131.07 and - 1860.11 kJ·mol-1, respectively.

Fabrication of nanocrystalline surface composite layer on Cu plate under ball collisions.

PubMed

Romankov, S; Park, Y C; Yoon, J M

2014-10-01

It was demonstrated that the severe plastic deformation of a surface induced by repeated ball collisions can be effectively used for fabrication of the nanocrystalline surface composite layers. The Cu disk was fixed at the top of a vibration chamber and ball treated. Al, Zr, Ni, Co and Fe were introduced into a Cu plate as contaminants from the grinding media one after the other by 15-min ball treatment. The composite structure was formed as a result of mechanical intermixing of the components. The particle size in as-fabricated layer ranged from 2 nm to 20 nm, with average values of about 7 nm. As-fabricated layer contained non-equilibrium multicomponent solid solution based on FCC Cu crystal structure, Zr-based phase, nanosized steel debris and amorphous phase. The hardness of the as-fabricated composite was almost ten times that of the initial Cu plate.

Oxidative potential of subway PM2.5

NASA Astrophysics Data System (ADS)

Moreno, Teresa; Kelly, Frank J.; Dunster, Chrissi; Oliete, Ana; Martins, Vânia; Reche, Cristina; Minguillón, Maria Cruz; Amato, Fulvio; Capdevila, Marta; de Miguel, Eladio; Querol, Xavier

2017-01-01

Air quality in subway systems is of interest not only because particulate matter (PM) concentrations can be high, but also because of the peculiarly metalliferous chemical character of the particles, most of which differ radically from those of outdoor ambient air. We report on the oxidative potential (OP) of PM2.5 samples collected in the Barcelona subway system in different types of stations. The PM chemical composition of these samples showed typically high concentrations of Fe, Total Carbon, Ba, Cu, Mn, Zn and Cr sourced from rail tracks, wheels, catenaries, brake pads and pantographs. Two toxicological indicators of oxidative activity, ascorbic acid (AA) oxidation (expressed as OPAA μg-1 or OPAA m-3) and glutathione (GSH) oxidation (expressed as OPGSH μg-1 or OPGSH m-3), showed low OP for all samples (compared with outdoor air) but considerable variation between stations (0.9-2.4 OPAA μg-1; 0.4-1.9 OPGSH μg-1). Results indicate that subway PM toxicity is not related to variations in PM2.5 concentrations produced by ventilation changes, tunnel works, or station design, but may be affected more by the presence of metallic trace elements such as Cu and Sb sourced from brakes and pantographs. The OP assays employed do not reveal toxic effects from the highly ferruginous component present in subway dust.

Cu2O/CuO Bilayered Composite as a High-Efficiency Photocathode for Photoelectrochemical Hydrogen Evolution Reaction

NASA Astrophysics Data System (ADS)

Yang, Yang; Xu, Di; Wu, Qingyong; Diao, Peng

2016-10-01

Solar powered hydrogen evolution reaction (HER) is one of the key reactions in solar-to-chemical energy conversion. It is desirable to develop photocathodic materials that exhibit high activity toward photoelectrochemical (PEC) HER at more positive potentials because a higher potential means a lower overpotential for HER. In this work, the Cu2O/CuO bilayered composites were prepared by a facile method that involved an electrodeposition and a subsequent thermal oxidation. The resulting Cu2O/CuO bilayered composites exhibited a surprisingly high activity and good stability toward PEC HER, expecially at high potentials in alkaline solution. The photocurrent density for HER was 3.15 mA·cm-2 at the potential of 0.40 V vs. RHE, which was one of the two highest reported at the same potential on copper-oxide-based photocathode. The high photoactivity of the bilayered composite was ascribed to the following three advantages of the Cu2O/CuO heterojunction: (1) the broadened light absorption band that made more efficient use of solar energy, (2) the large space-charge-region potential that enabled a high efficiency for electron-hole separation, and (3) the high majority carrier density that ensured a faster charge transportation rate. This work reveals the potential of the Cu2O/CuO bilayered composite as a promising photocathodic material for solar water splitting.

Structure and composition of Fe-OM co-precipitates that form in soil-derived solutions

NASA Astrophysics Data System (ADS)

Fritzsche, Andreas; Schröder, Christian; Wieczorek, Arkadiusz K.; Händel, Matthias; Ritschel, Thomas; Totsche, Kai U.

2015-11-01

Iron oxides represent a substantial fraction of secondary minerals and particularly affect the reactive properties of natural systems in which they formed, e.g. in soils and sediments. Yet, it is still obscure how transient conditions in the solution will affect the properties of in situ precipitated Fe oxides. Transient compositions, i.e. compositions that change with time, arise due to predominant non-equilibrium states in natural systems, e.g. between liquid and solid phases in soils. In this study, we characterize Fe-OM co-precipitates that formed in pH-neutral exfiltrates from anoxic topsoils under transient conditions. We applied soil column outflow experiments, in which Fe2+ was discharged with the effluent from anoxic soil and subsequently oxidized in the effluent due to contact with air. Our study features three novel aspects being unconsidered so far: (i) the transient composition of soil-derived solutions, (ii) that pedogenic Fe oxides instead of Fe salts serve as major source for Fe2+ in soil solution and (iii) the presence of exclusively soil-derived organic and inorganic compounds during precipitation. The experiments were carried out with two topsoil materials that differed in composition, texture and land use. Derived from Mössbauer spectroscopy, broad distributions in quadrupole splittings (0-2 mm s-1) and magnetic hyperfine fields (35-53 T) indicated the presence of low-crystalline ferrihydrite and even lower crystalline Fe phases in all Fe-OM co-precipitates. There was no unequivocal evidence for other Fe oxides, i.e. lepidocrocite and (nano)goethite. The Fe-OM co-precipitates contained inorganic (P, sulfate, silicate, Al, As) and organic compounds (proteins, polysaccharides), which were concurrently discharged from the soils. Their content in the Fe-OM co-precipitates was controlled by their respective concentration in the soil-derived solution. On a molar basis, OC and Fe were the main components in the Fe-OM co-precipitates (OC/Fe ratio = 0.5-2). The elemental composition of the Fe-OM co-precipitates was in accordance with the sequential precipitation of Fe(III)phosphates/arsenates prior to the formation of ferrihydrite. This explains decreasing Si contents in the Fe-OM co-precipitates with increasing availability of P. With respect to constant mean quadrupole splittings and slightly decreasing mean magnetic hyperfine fields, increasing contents of OC, P and Al in the Fe-OM co-precipitates did not further increase the structural disorder of the Fe polyhedra, while the crystallite interactions slightly decreased. Scanning electron microscopy and dynamic light scattering revealed the coincidental presence of variably sized aggregates and a considerable amount of Fe-OM co-precipitates, which remained dispersed in solution for months. Thus, variably composed Fe-OM co-precipitates with highly diverse aggregate sizes and comparably constant poor crystallinity can be expected after the oxidation of Fe2+ in transient, soil-derived solutions.

Investigation of Cu-, Zn- and Fe-containing human brain proteins using isotopic-enriched tracers by LA-ICP-MS and MALDI-FT-ICR-MS

NASA Astrophysics Data System (ADS)

Becker, J. Susanne; Zoriy, Miroslav; Pickhardt, Carola; Przybylski, Michael; Becker, J. Sabine

2005-04-01

Identification of metal-containing proteins and determination of Cu, Fe, Zn concentration in very small protein volumes is of increasing importance in protein research. Proteins containing metal ions were analyzed directly and simultaneously in separated protein spots in two-dimensional gels (2D gels) by laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS) as an element mass spectrometric technique. In order to study the formation of proteins containing Cu, Zn and Fe in a human brain sample, isotopic-enriched tracers (54Fe, 65Cu and 67Zn) were doped to two-dimensional gels of separated Alzheimer-diseased brain proteins after two-dimensional (2D) gel electrophoresis. The protein spots were screened systematically by LA-ICP-MS with respect to these metal ion intensities. 54Fe/56Fe, 65Cu/63Cu and 67Zn/64Zn isotope ratios in metal-containing proteins were measured directly by LA-ICP-MS. The isotope ratio measurements obtained by LA-ICP-MS indicate certain protein spots with a natural isotope composition of Cu, Zn and/or Fe. These proteins already contained the metal investigated in the original proteins and are stable enough to survive the reducing conditions during gel electrophoresis. On the other hand, proteins with a changed isotope ratio of metals in comparison to the isotope ratio in nature demonstrate the accumulation of tracers within the protein complexes during the tracer experiments in 2D gels. The identification of singular protein spots from Alzheimer-diseased brain separated by 2D gel electrophoresis was attempted by biopolymer mass spectrometry using MALDI-FTICR-MS after excision from the 2D gel and tryptic digestion.

Improved magnetic and electrical properties of Cu doped Fe-Ni invar alloys synthesized by chemical reduction technique

NASA Astrophysics Data System (ADS)

Ahmad, Sajjad; Ziya, Amer Bashir; Ashiq, Muhammad Naeem; Ibrahim, Ather; Atiq, Shabbar; Ahmad, Naseeb; Shakeel, Muhammad; Khan, Muhammad Azhar

2016-12-01

Fe-Ni-Cu invar alloys of various compositions (Fe65Ni35-xCux, x=0, 0.2, 0.6, 1, 1.4 and 1.8) were synthesized via chemical reduction route. These alloys were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometry (VSM) techniques. The XRD analysis revealed the formation of face centered cubic (fcc) structure. The lattice parameter and the crystallite size of the investigated alloys were calculated and the line broadening indicated the nano-crystallites size of alloy powder. The particle size was estimated from SEM and it decreases by the incorporation of Cu and found to be in the range of 24-40 nm. The addition of Cu in these alloys appreciably enhances the saturation magnetization and it increases from 99 to 123 emu/g. Electrical conductivity has been improved with Cu addition. The thermal conductivity was calculated using the Wiedemann-Franz law.

Experimental Investigation of Gas/Slag/Matte/Spinel Equilibria in the Cu-Fe-O-S-Si System at 1473 K (1200 °C) and P(SO2) = 0.25 atm

NASA Astrophysics Data System (ADS)

Hidayat, Taufiq; Fallah-Mehrjardi, Ata; Hayes, Peter C.; Jak, Evgueni

2018-04-01

New experimental data were obtained on the gas/slag/matte/spinel equilibria in the Cu-Fe-O-S-Si system at 1473 K (1200 °C) and P(SO2) = 0.25 atm covering Cu concentrations in matte between 42 and 78 wt pct Cu. Accurate measurements were obtained using high-temperature equilibration and the rapid quenching technique, followed by electron-probe X-ray microanalysis of equilibrium phase compositions. The use of spinel substrates made to support the samples ensures equilibrium with this primary phase solid, eliminates crucible contamination, and facilitates direct gas-condensed phase equilibrium and high quenching rates. Particular attention was given to the confirmation of the achievement of equilibrium. The results quantify the relationship between Cu in matte and oxygen partial pressure, sulfur in matte, oxygen in matte, Fe/SiO2 at slag liquidus, sulfur in slag, and dissolved copper in slag.

Causes of Different Vivid Colors in Chalcedonies: Kutahya-Turkey

NASA Astrophysics Data System (ADS)

Ozcan Kilic, Cumhur; Kagan Kadıoglu, Yusuf

2016-04-01

Chalcedony is a silicate mineral which is a mixture of fibrous quartz (trigonal) and granular moganite (monoclinic) minerals. They are both SiO2 in composition but differs in crystal system. Chalcedony is widely used as semi-precious gemstone in many countries. It has many different kinds due to their various colors and structures. The colour changes in mineral depends on different causes. Most important causes are transition metal impurities in minerals chemical composition and charge transfer between ions. Different chalcedony types have different colors due to their elemental composition. Chalcedony can be show almost every colour strating from white, black, gray, red, blue, green to brown or a combinations of more than one color in case of agates and jasper formations. Although they have same major oxide compositions,chrysopras (green chalcedony) have Ni which gives the green color and carnelian (orange chalcedony) have Fe+3 which gives the orange color. Kutahya, Eskisehir, Ankara, Manisa, Balıkesir, Canakkale and Yozgat represent the most cities which chalcedony can be mostly observed in Turkey. In Kutahya, chalcedony occurs in cavity or vein fillings in pyroclastic rocks such as tuff and formed by precipitation of silica bearing fluids in low temperatures. They can be also formed within the hydrothermal alteration zone of ultramafic rocks. Although chalcedonies in Kutahya form under almost same condition, they have various colors within the same unit. To specify the cause of the different colors, chemical analysis and Confocal Raman studies performed on Kutahya chalcedonies. Firstly, samples are crushed to 2 mm. size. After that, different colors of chalcedonies are separated by hand picking under binocular microscope and grouped into different color sets such as white, blue, dark yellow, light orange, dark orange and claret red. Each color set is measured by PED-XRF method to obtain chemical compositions. Also Raman studies performed to identify the effect of Fe element and OH bonds in each color set groups. Due to chemical results, 'Fe2O3-TiO2'assemblage gives claret red-dark orange, only "Fe2O3"gives claret red, 'Fe2O3-Ni' assemblage gives orange to claret red, 'Cr-Ni-Co' assemblage gives light orange, 'As' gives yellow, 'Fe2O3-Cu' assemblage gives claret red to orange, 'As-Zr' and 'Cr2O3-MgO' assemblage gives blue color to chalcedonies in Kutahya. Also 'Fe' Raman shift is figured in Raman studies in Fe containing orange-claret red colored samples. The vivid colors in all the sets derived from the OH Raman shift bonds of the chalcedony. Chemical results show that the colour differences in chalcedony is not related with only one element.The mobility and charge of Fe element with some other (Co, Mn, Cu, Cr, Ni etc.) elements also effects the variability of the colour.

Synthesis of Ordered Mesoporous CuO/CeO2 Composite Frameworks as Anode Catalysts for Water Oxidation

PubMed Central

Markoulaki, Vassiliki Ι.; Papadas, Ioannis T.; Kornarakis, Ioannis; Armatas, Gerasimos S.

2015-01-01

Cerium-rich metal oxide materials have recently emerged as promising candidates for the photocatalytic oxygen evolution reaction (OER). In this article, we report the synthesis of ordered mesoporous CuO/CeO2 composite frameworks with different contents of copper(II) oxide and demonstrate their activity for photocatalytic O2 production via UV-Vis light-driven oxidation of water. Mesoporous CuO/CeO2 materials have been successfully prepared by a nanocasting route, using mesoporous silica as a rigid template. X-ray diffraction, electron transmission microscopy and N2 porosimetry characterization of the as-prepared products reveal a mesoporous structure composed of parallel arranged nanorods, with a large surface area and a narrow pore size distribution. The molecular structure and optical properties of the composite materials were investigated with Raman and UV-Vis/NIR diffuse reflectance spectroscopy. Catalytic results indicated that incorporation of CuO clusters in the CeO2 lattice improved the photochemical properties. As a result, the CuO/CeO2 composite catalyst containing ~38 wt % CuO reaches a high O2 evolution rate of ~19.6 µmol·h−1 (or 392 µmol·h−1·g−1) with an apparent quantum efficiency of 17.6% at λ = 365 ± 10 nm. This OER activity compares favorably with that obtained from the non-porous CuO/CeO2 counterpart (~1.3 µmol·h−1) and pure mesoporous CeO2 (~1 µmol·h−1). PMID:28347106

Cu2O Photocathode for Low Bias Photoelectrochemical Water Splitting Enabled by NiFe-Layered Double Hydroxide Co-Catalyst

PubMed Central

Qi, Huan; Wolfe, Jonathan; Fichou, Denis; Chen, Zhong

2016-01-01

Layered double hydroxides (LDHs) are bimetallic hydroxides that currently attract considerable attention as co-catalysts in photoelectrochemical (PEC) systems in view of water splitting under solar light. A wide spectrum of LDHs can be easily prepared on demand by tuning their chemical composition and structural morphology. We describe here the electrochemical growth of NiFe-LDH overlayers on Cu2O electrodes and study their PEC behavior. By using the modified Cu2O/NiFe-LDH electrodes we observe a remarkable seven-fold increase of the photocurrent intensity under an applied voltage as low as −0.2 V vs Ag/AgCl. The origin of such a pronounced effect is the improved electron transfer towards the electrolyte brought by the NiFe-LDH overlayer due to an appropriate energy level alignment. Long-term photostability tests reveal that Cu2O/NiFe-LDH photocathodes show no photocurrent loss after 40 hours of operation under light at −0.2 V vs Ag/AgCl low bias condition. These improved performances make Cu2O/NiFe-LDH a suitable photocathode material for low voltage H2 production. Indeed, after 8 hours of H2 production under −0.2 V vs Ag/AgCl the PEC cell delivers a 78% faradaic efficiency. This unprecedented use of Cu2O/NiFe-LDH as an efficient photocathode opens new perspectives in view of low biasd or self-biased PEC water splitting under sunlight illumination. PMID:27487918

Use of La 0.75Sr 0.25Cr 0.5Mn 0.5O 3 materials in composite anodes for direct ethanol solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Ye, Xiao-Feng; Wang, S. R.; Wang, Z. R.; Hu, Q.; Sun, X. F.; Wen, T. L.; Wen, Z. Y.

The perovskite system La 1- xSr xCr 1- yM yO 3- δ (M, Mn, Fe and V) has recently attracted much attention as a candidate material for the fabrication of solid oxide fuel cells (SOFCs) due to its stability in both H 2 and CH 4 atmospheres at temperatures up to 1000 °C. In this paper, we report the synthesis of La 0.75Sr 0.25Cr 0.5Mn 0.5O 3 (LSCM) by solid-state reaction and its employment as an alternative anode material for anode-supported SOFCs. Because LSCM shows a greatly decreased electronic conductivity in a reducing atmosphere compared to that in air, we have fabricated Cu-LSCM-ScSZ (scandia-stabilized zirconia) composite anodes by tape-casting and a wet-impregnation method. Additionally, a composite structure (support anode, functional anode and electrolyte) structure with a layer of Cu-LSCM-YSZ (yttria-stabilized zirconia) on the supported anode surface has been manufactured by tape-casting and screen-printing. Single cells with these two kinds of anodes have been fabricated, and their performance characteristics using hydrogen and ethanol have been measured. In the operation period, no obvious carbon deposition was observed when these cells were operated on ethanol. These results demonstrate the stability of LSCM in an ethanol atmosphere and its potential utilization in anode-supported SOFCs.

Effect of Cooling Rates on γ → α Transformation and Metastable States in Fe-Cu Alloys with Addition of Ni

NASA Astrophysics Data System (ADS)

Crozet, C.; Verdier, M.; Lay, S.; Antoni-Zdziobek, A.

2018-07-01

α/γ phase transformations occurring in Fe-10Cu-xNi alloys (0 ≤ x ≤ 15 in mass%) were studied using X-ray diffraction, scanning electron microscopy, electron back scattered diffraction, transmission electron microscopy and chemical analysis, combining X-ray microanalysis with energy dispersive spectrometry in the scanning electron microscope and electron microprobe analysis with wavelength dispersive spectrometry. The influence of cooling rate on the microstructure was investigated using ice-brine quenching and 2 °C/min slow cooling rate performed with dilatometry. Ni addition induces metastable transformations on cooling: massive and bainitic ferrite are formed depending on the alloy composition and cooling rate. Moreover, most of the Cu phase precipitates on cooling giving rise to a fine distribution of Cu particles in the ferrite grains. For both cooling conditions, the hardness increases with increasing Ni content and a higher hardness is obtained in the quenched alloy for each composition. The change in hardness is correlated to the effect of Ni solid solution, transformation structure and size of Cu particles.

Effect of Cu2+ substitution on the structural, magnetic and electrical properties of gadolinium orthoferrite

NASA Astrophysics Data System (ADS)

Sai Vandana, C.; Hemalatha Rudramadevi, B.

2018-04-01

The pure and copper (Cu) substituted Gadolinium orthoferrites, GdFeO3, GdCu0.1Fe0.9O3, GdCu0.2Fe0.8O3 and GdCu0.3Fe0.7O3 were synthesized by conventional solid state method. The structural, morphological, dielectric, magnetic and impedance properties of Cu substituted Gadolinium orthoferrites have been investigated. The crystallographic phase as well as the substitution of Cu2+ ions in the lattice of GdFeO3 is confirmed from the x-ray diffraction patterns. The Fourier transform infrared spectra exhibit two prominent fundamental absorption peaks at ∼417 cm‑1 and 545 cm‑1. These bands are related to inherent stretching vibrations of metals at octahedral and tetrahedral sites respectively. The coercivity (Hc) and saturation magnetization (Ms) of the synthesized samples at different temperatures were determined from the hysteresis plots. Higher coercive values, 598 Oe and 600 Oe were achieved in GdCu0.1Fe0.9O3 ferrites compared to 527 Oe and 360 Oe in pure GdFeO3 at room temperature (300 K) and low temperature (20 k) respectively. Dielectric dispersion has been observed for gadolinium ferrite samples with Maxwell–Wagner type interfacial polarization. The decrease of dielectric constant and dielectric loss tangent with an increase in frequency was observed. The conduction due to charge hopping between localized states was confirmed from AC conductivity measurements. The composition dependent cationic distributions estimated from XRD, magnetic and electrical studies are in good agreement with each other. The achieved results indicate that the substitution of Cu in gadolinium orthoferrite strongly influences the crystal structure, magnetic and electrical properties thereby making them suitable as multiple state memory devices, transducers, electronic field controlled ferromagnetic resonance devices and spintronic devices.

Role of hydrous iron oxide formation in attenuation and diel cycling of dissolved trace metals in a stream affected by acid rock drainage

USGS Publications Warehouse

Parker, S.R.; Gammons, C.H.; Jones, Clain A.; Nimick, D.A.

2007-01-01

Mining-impacted streams have been shown to undergo diel (24-h) fluctuations in concentrations of major and trace elements. Fisher Creek in south-central Montana, USA receives acid rock drainage (ARD) from natural and mining-related sources. A previous diel field study found substantial changes in dissolved metal concentrations at three sites with differing pH regimes during a 24-h period in August 2002. The current work discusses follow-up field sampling of Fisher Creek as well as field and laboratory experiments that examine in greater detail the underlying processes involved in the observed diel concentration changes. The field experiments employed in-stream chambers that were either transparent or opaque to light, filled with stream water and sediment (cobbles coated with hydrous Fe and Al oxides), and placed in the stream to maintain the same temperature. Three sets of laboratory experiments were performed: (1) equilibration of a Cu(II) and Zn(II) containing solution with Fisher Creek stream sediment at pH 6.9 and different temperatures; (2) titration of Fisher Creek water from pH 3.1 to 7 under four different isothermal conditions; and (3) analysis of the effects of temperature on the interaction of an Fe(II) containing solution with Fisher Creek stream sediment under non-oxidizing conditions. Results of these studies are consistent with a model in which Cu, Fe(II), and to a lesser extent Zn, are adsorbed or co-precipitated with hydrous Fe and Al oxides as the pH of Fisher Creek increases from 5.3 to 7.0. The extent of metal attenuation is strongly temperature-dependent, being more pronounced in warm vs. cold water. Furthermore, the sorption/co-precipitation process is shown to be irreversible; once the Cu, Zn, and Fe(II) are removed from solution in warm water, a decrease in temperature does not release the metals back to the water column. ?? 2006 Springer Science+Business Media B.V.

Highly antifouling and antibacterial performance of poly (vinylidene fluoride) ultrafiltration membranes blending with copper oxide and graphene oxide nanofillers for effective wastewater treatment.

PubMed

Zhao, Chuanqi; Lv, Jinling; Xu, Xiaochen; Zhang, Guoquan; Yang, Yuesuo; Yang, Fenglin

2017-11-01

Innovation and effective wastewater treatment technology is still in great demand given the emerging contaminants frequently spotted from the aqueous environment. By blending with poly (vinylidene fluoride) (PVDF), the strong hydrophilic graphene oxide (GO) and antibacterial copper oxide (Cu x O) were used as nanofillers to develop the novel, highly antifouling composite membranes via phase inversion process in our latest work. The existence and dispersion of GO and Cu x O posed a significant role on morphologies, structures, surface composition and hydrophilicity of the developed composite membranes, confirmed by SEM, TEM, FTIR and XPS in depth characterization. The SEM images showed that the modified membranes presented a lower resistant structure with developed finger-like macrovoids and thin-walled even interconnected sponge-like pores after adding nanofillers, much encouraging membrane permeation. The XPS results revealed that Cu x O contained Cu 2 O and CuO in the developed membrane and the Cu 2 O nanoparticles were dominant accounting for about 79.3%; thus the modified membrane specifically exhibited an efficient antibacterial capacity. Due to the hydrophilic and bactericidal membrane surface, the composite membranes demonstrated an excellent antifouling performance, including higher flux recovery rate, more resistant against accumulated contaminants and lower filtration resistance, especially lower irreversible resistance. The antifouling property, especially anti-irreversible fouling, was significantly improved, showing a significant engineering potential. Copyright © 2017 Elsevier Inc. All rights reserved.

Zn1-xAlxO:Cu2O transparent metal oxide composite thin films by sol gel method

NASA Astrophysics Data System (ADS)

AlHammad, M. S.

2017-05-01

We have synthesized undoped zinc oxide (ZnO) and Cu2O doped Zn1-XAlXO (AZO; Al/Zn = 1.5 at.%) metal oxide films by sol-gel spin coating method. Atomic force microscopy results indicate that the Zn1-xAlxO:Cu2O is are formed form the fibers. The surface morphology of the films is found to depend on the concentration of Cu2O. The optical constants such as band gap, Urbach energy, refractive index, extinction coefficient and dielectric constants of the films were determined. The transmittance spectra shows that all the films are highly transparent. The study revealed that undoped ZnO film has direct bang gap of 3.29 eV and the optical band gap of films is increased with doping content. The hot probe measurements indicate that Zn1-xAlxO:Cu2O transparent metal oxide composite thin films exhibited p-type electrical conductivity.

The effects of CuO particle size on microstructure evolution of AgCuO compo-sites in plastic deformation process: finite element simulation and experimental study

NASA Astrophysics Data System (ADS)

Li, Zhiguo; Cao, Hanxing; Zhou, Xiaolong; Zhou, Zhaobo; Cao, Jianchun

2018-04-01

The effects of CuO with different particle sizes on the microstructure evolution of AgCuO composite material during plastic deformation process were investigated by finite element (FE) analysis and experiment. The results are as follows: with the decrease of CuO particle size, the degree of radial compression and axial elongation of CuO particle cluster increase gradually, as well as the dispersion of CuO also increase. Meanwhile, the shape of CuO particles is constantly transformed from polygonal to fibrous, which makes the number of linear fibrous CuO increase continuously while bent fibrous CuO reduce gradually. By comparing the simulation and experiment results we find that there are four different typical microstructure regions, which caused by the interaction between monoclinic and cubic CuO during the extrusion process.

Comparison between semiconducting and oxide layers as a reflection layer in spin-valve films

NASA Astrophysics Data System (ADS)

Dinia, A.; Schmerber, G.; Ulhaq, C.

2003-07-01

It is well established that appropriate oxide capping is effective in forming nano-oxide layers (NOL) in spin-valve films for specular enhancement of giant magnetoresistance (GMR) effect. However, the beneficial effect of a NOL is strongly dependent on its process of formation. Therefore, we are interested to use a nano-semiconducting layer (NSL) for specular reflection instead of oxide layers because its achievement is easier since no specific growth conditions are needed. Moreover, we intend to compare the efficiency of the electronic confinement inside the spin valve induced either by NSL or NOLs for structures with the same stack. We have prepared hard-soft spin valve structures by sputtering on glass substrates with the following stacking sequence: Fe6 nm/Cu3 nm/CoFe1.8 nmRu0.8 nmCoFe3 nmCu2 nmRu2 nm. The reflecting layers have been inserted in the middle of the Fe soft layer and on the top of the spin valve. The GMR effect is enhanced by 60% and 75% respectively for the NSL and the NOL. This shows that the NOL is more efficient in term of electronic confinement. To understand the origin of the difference between the NOL and NSL magnetization measurements as well as transmission electron microscopy are presented.

The use of nuclear muprobe techniques to study the chemistry of lacustrine sediments and particles

NASA Astrophysics Data System (ADS)

Grime, G. W.; Davison, W.

1993-05-01

The Oxford SPM has been used in two novel studies of lake chemistry: (a) The distribution of dissolved iron in sediment pore waters close to the sediment/water interface has been measured using the novel technique of diffusive equilibration in a thin film (DET). In this technique, which has a spatial resolution of < 1 mm, much less than that of competing techniques (1 cm), a thin layer of polyacrylamide gel is inserted into the sediment and after the rapid equilibration with the pore water, the gel is dried and fixed. The distribution of trace elements can then be measured using mubeam PIXE. Preliminary results have shown for the first time a subsurface maximum of Fe consistent with current theories of Fe dynamics. This paper presents some results obtained using the technique and discusses the limits on resolution and sensitivity, (b) Individual suspended lake particles (predominantly iron oxides and sulphides) have been analysed using point mubeam RBS and PIXE. Of particular interest in this study is the oxidation state of iron rich particles, so RBS with a 1 μm beam was used to determine the Fe: O stoichiometry of single particles. The particles were filtered from a depth of 14 m in Esthwaite Water in the English Lake District and handled in anoxic conditions until evacuation in the SPM sample chamber. Two distinct compositions of iron oxide were determined in clusters of about 5 μm diameter. Analysis by PIXE revealed that FeS was uniformly distributed in the particulate material and that it also contained elevated levels of Cu and Zn. This study was the first to demonstrate directly that discrete clusters of iron oxides are present in black particulate material which is commonly considered to comprise iron sulphides.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luňáček, J., E-mail: jiri.lunacek@vsb.cz

The present paper is devoted to detailed study of the magnetically separable sorbents based on a cerium dioxide/iron oxide composite annealed at temperatures T{sub a} = 773 K, 873 K, and 973 K. The X-ray diffraction and high resolution transmission electron microscopy are used to determine the phase composition and microstructure morphology. Mössbauer spectroscopy at room (300 K) and low (5 K) temperatures has contributed to more exact identification of iron oxides and their transformations Fe{sub 3}O{sub 4} → γ-Fe{sub 2}O{sub 3} (ε-Fe{sub 2}O{sub 3}) → α-Fe{sub 2}O{sub 3} in dependence on calcination temperature. Different iron oxide phase compositions andmore » grain size distributions influence the magnetic characteristics determined from the room- and low-temperature hysteresis loop measurements. The results are supported by zero-field-cooled and field-cooled magnetization measurements allowing a quantitative estimation of the grain size distribution and its effect on the iron oxide transformations. - Highlights: •Magnetically separable sorbents based on a CeO{sub 2}/Fe{sub 2}O{sub 3} composite were investigated. •Microstructure of sorbents was determined by XRD, TEM and Mössbauer spectroscopy. •Magnetic properties were studied by hysteresis loops at room- and low-temperatures. •Phase transitions of iron oxides with increasing annealing temperature are observed.« less

iron phase control during pressure leaching at elevated temperature

NASA Astrophysics Data System (ADS)

Fleuriault, Camille

Iron is a common contaminant encountered in most metal recovery operations, and particularly hydrometallurgical processes. For example, the Hematite Process uses autoclaves to precipitate iron oxide out of the leaching solution, while other metals are solubilized for further hydrometallurgical processing. In some cases, Basic Iron Sulfate (BIS) forms in place of hematite. The presence of BIS is unwanted in the autoclave discharge because it diminishes recovery and causes environmental matters. The focus of this master thesis is on the various iron phases forming during the pressure oxidation of sulfates. Artificial leaching solutions were produced from CuSO4, FeSO4 and H2SO4 in an attempt to recreate the matrix composition and conditions used for copper sulfides autoclaving. The following factors were investigated in order to determine which conditions hinder the formation of BIS: initial free acidity (5 -- 98 g/L), initial copper concentration (12.7 -- 63.5 g/L), initial iron concentration (16.7 -- 30.7 g/L) and initial iron oxidation state. There were three solid species formed in the autoclave: hematite, BIS and hydronium jarosite. The results show that free acid is the main factor influencing the composition of the residue. At an initial concentration of 22.3 g/L iron and no copper added, the upper limit for iron oxide formation is 41 g/L H2SO4. The increase of BIS content in the residue is not gradual and occurs over a change of a few grams per liter around the aforementioned limit. Increasing copper sulfate concentration in the solution hinders the formation of BIS. At 63.5g/L copper, the upper free acidity limit is increased to 61g/L. This effect seems to be related to the buffering action of copper sulfate, decreasing the overall acid concentration and thus extending the stability range of hematite. The effect of varying iron concentration on the precipitate chemistry is unclear. At high iron levels, the only noticeable effect was the inhibition of jarosite. The results were reported within a Cu-Fe-S ternary system and modeled. The modeling confirmed the experimental observations with the exception that increasing iron concentrations seem to promote BIS stability.

Influence of iron and copper oxides on polychlorinated diphenyl ether formation in heterogeneous reactions.

PubMed

Liu, Wenxia; Shen, Lianfeng; Zhang, Fawen; Liu, Wenbin; Zheng, Minghui; Yang, Xitian

2013-08-01

Polychlorinated diphenyl ether (PCDE) has attracted great attention recently as an important type of environmental pollutant. The influence of iron and copper oxides on formation of PCDEs was investigated using laboratory-scale flow reactors under air and under nitrogen at 350 °C, a temperature corresponding to the post-combustion zone of a municipal solid waste incinerator. The results show that the 2,2',3,4,4',5,5',6-otachlorodiphenyl ether (OCDE) formed from the condensation of pentachlorophenol (PCP) and 1,2,4,5-tetrachlorobenzene (Cl4Bz) is the predominant congener formed on the SiO2/Fe2O3 surface with and without oxygen. This indicated that HCl elimination between PCP and 1,2,4,5-Cl4Bz molecules formed 2,2',3,4,4',5,5',6-OCDE in the presence of Fe2O3. On the other hand, decachlorodiphenyl ether, nonachlorodiphenyl ether, and OCDE were the dominant products on the SiO2/CuO surface without oxygen, although the 2,2',3,4,4',5,5',6-OCDE was the dominant product on the SiO2/CuO surface with oxygen. Therefore, the presence of Fe2O3 and CuO influences the formation and homologue distribution of PCDEs, which shifted towards the lower chlorinated species. Fe2O3 can promote both the condensation and dechlorination reaction without oxygen. On the contrary, with oxygen, Fe2O3 suppresses the condensation of chlorobenzene and chlorophenol to form PCDEs and polychlorinated dibenzo-p-dioxins and polychlorinated dibenzofurans (PCDD/Fs). CuO can increase the formation of lower chlorinated PCDEs and PCDDs without oxygen. In conclusion, the different fly ash components have a major influence on PCDE emissions.

Influence of the insertion of a nano-oxide layer on the interfacial magnetism of FeMn /NiFe/Cu/NiFe spin valves

NASA Astrophysics Data System (ADS)

Tafur, Miguel; Alayo, W.; Munayco, P.; Baggio-Saitovitch, E.; Nascimento, V. P.; Alvarenga, A. D.; Brewer, W. D.

2007-05-01

We have studied the influence of an inserted nano-oxide layer (NOL) on the interfacial magnetism in spin-valve systems showing the giant magnetoresistance effect. Specifically, we performed a magnetic depth profile of these structures with and without a NOL, using the x-ray magnetic circular dichroism technique. We found that insertion of a NOL into the spin-valve structure is correlated with a stronger reduction of the magnetic moments at the ferromagnetic (FM)/NOL/FM interface in comparison with a spin valve without NOL.

Synthesis of graphene oxide-copper molybdate (GO-CuM) nanocomposites for photocatalytic application

NASA Astrophysics Data System (ADS)

Singh, Gajendar; Bhargava, V. Sai; Sharma, Manu

2018-05-01

Transition metal molybdates (TMBs) MMoO4 (M=Ni, Cu, Fe, Zn, Co, etc.) based nanocomposites have been considered as remarkable materials in the field of electronics, optics, catalysis, supercapicitors and energy storage devices. Nanocomposites of TMBs with graphene oxide have also been chosen as an effective material in photocatalytic application. GO-CuM nanocomposites were synthesized by ultra-sonication method at RT, followed by reflux route for preparation of CuM and GO by modified Hemmer's method. As prepared nanocomposites were characterized using analytical techniques such as PXRD, SEM, FT-IR and UV-Visible spectroscopy. The enhanced photocatalytic activity of Methylene blue (MB) dye was observed by GO-CuM nanocomposites as compared to pure copper molybdate. GO-CuM nanocomposites show high photodegradation rate (0.094 min-1) whereas CuM was degraded only 30 % with the rate of 0.0029 min-1. The high photocatalytic efficiency is due to the presence of graphene oxide that helps to delay the charge recombination in photocatalytic reaction The effect of the different amount of graphene oxide on the photocatalytic activity of as prepared photocatalyst has also been investigated.

Experimental Phase Equilibria Studies of the Pb-Fe-O System in Air, in Equilibrium with Metallic Lead and at Intermediate Oxygen Potentials

NASA Astrophysics Data System (ADS)

Shevchenko, M.; Jak, E.

2017-12-01

The phase equilibria information on the Pb-Fe-O system is of practical importance for the improvement of the existing thermodynamic database of lead-containing slag systems (Pb-Zn-Fe-Cu-Si-Ca-Al-Mg-O). Phase equilibria of the Pb-Fe-O system have been investigated: (a) in air at temperatures between 1053 K and 1373 K (780 °C and 1100 °C); (b) in equilibrium with metallic lead at temperatures between 1053 K and 1373 K (780 °C and 1100 °C); and (c) at intermediate oxidation conditions for the liquid slag in equilibrium with two solids (spinel + magnetoplumbite), at temperatures between 1093 K and 1373 K (820 °C and 1100 °C). The high-temperature equilibration/quenching/electron probe X-ray microanalysis technique has been used to accurately determine the compositions of the phases in equilibrium in the system. The Pb and Fe concentrations in the phases were determined directly; preliminary thermodynamic modeling with FactSage was used to estimate the ferrous-to-ferric ratios and to present the results in the ternary diagram.

Studies Of Oxidation And Thermal Reduction Of The Cu(100) Surface Using Positron Annihilation Induced Auger Electron Spectroscopy

NASA Astrophysics Data System (ADS)

Fazleev, N. G.; Nadesalingam, M. P.; Maddox, W.; Weiss, A. H.

2011-06-01

Positron annihilation induced Auger electron spectroscopy (PAES) measurements from the surface of an oxidized Cu(100) single crystal show a large increase in the intensity of the annihilation induced Cu M2,3VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 300 °C. The PAES intensity then decreases monotonically as the annealing temperature is increased to ˜550 °C. Experimental positron annihilation probabilities with Cu 3p and O 1s core electrons are estimated from the measured intensities of the positron annihilation induced Cu M2,3VV and O KLL Auger transitions. PAES results are analyzed by performing calculations of positron surface states and annihilation probabilities of the surface-trapped positrons with relevant core electrons taking into account the charge redistribution at the surface and various surface structures associated with low and high oxygen coverages. The variations in atomic structure and chemical composition of the topmost layers of the oxidized Cu(100) surface are found to affect localization and spatial extent of the positron surface state wave function. The computed positron binding energy and annihilation characteristics reveal their sensitivity to charge transfer effects, atomic structure and chemical composition of the topmost layers of the oxidized Cu(100) surface. Theoretical positron annihilation probabilities with Cu 3p and O 1s core electrons computed for the oxidized Cu(100) surface are compared with experimental ones. The obtained results provide a demonstration of thermal reduction of the copper oxide surface after annealing at 300 °C followed by re-oxidation of the Cu(100) surface at higher annealing temperatures presumably due to diffusion of subsurface oxygen to the surface.

Studies Of Oxidation And Thermal Reduction Of The Cu(100) Surface Using Positron Annihilation Induced Auger Electron Spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fazleev, N. G.; Department of Physics, Kazan State University, Kazan 420008; Nadesalingam, M. P.

2011-06-01

Positron annihilation induced Auger electron spectroscopy (PAES) measurements from the surface of an oxidized Cu(100) single crystal show a large increase in the intensity of the annihilation induced Cu M2,3VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 300 deg. C. The PAES intensity then decreases monotonically as the annealing temperature is increased to {approx}550 deg. C. Experimental positron annihilation probabilities with Cu 3p and O 1s core electrons are estimated from the measured intensities of the positron annihilation induced Cu M{sub 2,3}VV and O KLL Auger transitions. PAESmore » results are analyzed by performing calculations of positron surface states and annihilation probabilities of the surface-trapped positrons with relevant core electrons taking into account the charge redistribution at the surface and various surface structures associated with low and high oxygen coverages. The variations in atomic structure and chemical composition of the topmost layers of the oxidized Cu(100) surface are found to affect localization and spatial extent of the positron surface state wave function. The computed positron binding energy and annihilation characteristics reveal their sensitivity to charge transfer effects, atomic structure and chemical composition of the topmost layers of the oxidized Cu(100) surface. Theoretical positron annihilation probabilities with Cu 3p and O 1s core electrons computed for the oxidized Cu(100) surface are compared with experimental ones. The obtained results provide a demonstration of thermal reduction of the copper oxide surface after annealing at 300 deg. C followed by re-oxidation of the Cu(100) surface at higher annealing temperatures presumably due to diffusion of subsurface oxygen to the surface.« less

Constraints on the source of Cu in a submarine magmatic-hydrothermal system, Brothers volcano, Kermadec island arc

NASA Astrophysics Data System (ADS)

Keith, Manuel; Haase, Karsten M.; Klemd, Reiner; Smith, Daniel J.; Schwarz-Schampera, Ulrich; Bach, Wolfgang

2018-05-01

Most magmatic-hydrothermal Cu deposits are genetically linked to arc magmas. However, most continental or oceanic arc magmas are barren, and hence new methods have to be developed to distinguish between barren and mineralised arc systems. Source composition, melting conditions, the timing of S saturation and an initial chalcophile element-enrichment represent important parameters that control the potential of a subduction setting to host an economically valuable deposit. Brothers volcano in the Kermadec island arc is one of the best-studied examples of arc-related submarine magmatic-hydrothermal activity. This study, for the first time, compares the chemical and mineralogical composition of the Brothers seafloor massive sulphides and the associated dacitic to rhyolitic lavas that host the hydrothermal system. Incompatible trace element ratios, such as La/Sm and Ce/Pb, indicate that the basaltic melts from L'Esperance volcano may represent a parental analogue to the more evolved Brothers lavas. Copper-rich magmatic sulphides (Cu > 2 wt%) identified in fresh volcanic glass and phenocryst phases, such as clinopyroxene, plagioclase and Fe-Ti oxide suggest that the surrounding lavas that host the Brothers hydrothermal system represent a potential Cu source for the sulphide ores at the seafloor. Thermodynamic calculations reveal that the Brothers melts reached volatile saturation during their evolution. Melt inclusion data and the occurrence of sulphides along vesicle margins indicate that an exsolving volatile phase extracted Cu from the silicate melt and probably contributed it to the overlying hydrothermal system. Hence, the formation of the Cu-rich seafloor massive sulphides (up to 35.6 wt%) is probably due to the contribution of Cu from a bimodal source including wall rock leaching and magmatic degassing, in a mineralisation style that is hybrid between Cyprus-type volcanic-hosted massive sulphide and subaerial epithermal-porphyry deposits.

Radical loss in the atmosphere from Cu-Fe redox coupling in aerosols

NASA Astrophysics Data System (ADS)

Mao, J.; Fan, S.; Jacob, D. J.; Travis, K.; Naik, V.; Horowitz, L. W.

2012-12-01

The hydroperoxyl radical (HO2) is a major precursor of OH and tropospheric ozone. OH is the main atmospheric oxidant, while tropospheric ozone is an important surface pollutant and greenhouse gas. Standard gas-phase models for atmospheric chemistry tend to overestimate observed HO2 concentrations, and this has been tentatively attributed to heterogeneous uptake by aerosol particles. It is generally assumed that HO2 uptake by aerosol involves conversion to H2O2, but this is of limited efficacy as an HO2 sink because H2O2 can photolyze to regenerate OH and from there HO2. Joint atmospheric observations of HO2 and H2O2 suggest that HO2 uptake by aerosols may in fact not produce H2O2. Here we propose a catalytic mechanism involving coupling of the transition metal ions (TMI) Cu(I)/Cu(II) and Fe(II)/Fe(III) to rapidly convert HO2 to H2O in aerosols. The implied HO2 uptake significantly affects global model predictions of tropospheric OH, ozone, and other species, improving comparisons to observations, and may have a major and previously unrecognized impact on atmospheric oxidant chemistry.

NanoE-Tox: New and in-depth database concerning ecotoxicity of nanomaterials.

PubMed

Juganson, Katre; Ivask, Angela; Blinova, Irina; Mortimer, Monika; Kahru, Anne

2015-01-01

The increasing production and use of engineered nanomaterials (ENMs) inevitably results in their higher concentrations in the environment. This may lead to undesirable environmental effects and thus warrants risk assessment. The ecotoxicity testing of a wide variety of ENMs rapidly evolving in the market is costly but also ethically questionable when bioassays with vertebrates are conducted. Therefore, alternative methods, e.g., models for predicting toxicity mechanisms of ENMs based on their physico-chemical properties (e.g., quantitative (nano)structure-activity relationships, QSARs/QNARs), should be developed. While the development of such models relies on good-quality experimental toxicity data, most of the available data in the literature even for the same test species are highly variable. In order to map and analyse the state of the art of the existing nanoecotoxicological information suitable for QNARs, we created a database NanoE-Tox that is available as Supporting Information File 1. The database is based on existing literature on ecotoxicology of eight ENMs with different chemical composition: carbon nanotubes (CNTs), fullerenes, silver (Ag), titanium dioxide (TiO2), zinc oxide (ZnO), cerium dioxide (CeO2), copper oxide (CuO), and iron oxide (FeO x ; Fe2O3, Fe3O4). Altogether, NanoE-Tox database consolidates data from 224 articles and lists altogether 1,518 toxicity values (EC50/LC50/NOEC) with corresponding test conditions and physico-chemical parameters of the ENMs as well as reported toxicity mechanisms and uptake of ENMs in the organisms. 35% of the data in NanoE-Tox concerns ecotoxicity of Ag NPs, followed by TiO2 (22%), CeO2 (13%), and ZnO (10%). Most of the data originates from studies with crustaceans (26%), bacteria (17%), fish (13%), and algae (11%). Based on the median toxicity values of the most sensitive organism (data derived from three or more articles) the toxicity order was as follows: Ag > ZnO > CuO > CeO2 > CNTs > TiO2 > FeO x . We believe NanoE-Tox database contains valuable information for ENM environmental hazard estimation and development of models for predicting toxic potential of ENMs.

Petrology of iron-rich magmatic segregations associated with strongly peraluminous trondhjemite in the Cornucopia stock, northeastern Oregon

NASA Astrophysics Data System (ADS)

Johnson, K.; Barnes, C. G.; Browning, J. M.; Karlsson, H. R.

The Middle Cretaceous Cornucopia stock in the Blue Mountains of northeastern Oregon is a small composite intrusion consisting of hornblende biotite tonalite, biotite trondhjemite, and three cordierite two mica trondhjemite units. Unusual magnetite + biotite-rich tonalitic rocks are associated with the Crater Lake cordierite trondhjemite, the youngest of the intrusions. Oxide-rich tonalites are characterized by high Fe ( 47-68 wt% total Fe as FeO), low SiO2 (<36 wt%), and enrichments in HFSE and REE (La(N)=361-903). Oxide-rich tonalites appear in a variety of forms, including composite dikes and sheets, in which they are associated with leucocratic tonalite. Leucotonalite is lower in SiO2 (60-72 wt%) than Crater Lake trondhjemite, and generally has ΣREE contents and Eu anomalies intermediate between the oxide-rich tonalite and Crater Lake compositions. Oxide-rich tonalites crosscut, and are crosscut by, shear zones in the host trondhjemite, indicating their emplacement late in the pluton's crystallization history. Granitic dikes crosscut the composite dikes in all localities. Geochemical considerations and sedimentary-like structures, such as load casts and bedding of magnetite-rich assemblages in the composite dikes and sheets, are suggestive of crystal settling from an Fe-rich parental magma. The Fe-rich liquid parental to the oxide-rich tonalite-leucotonalite pairs formed by extensive, in-situ, plagioclase + quartz-dominated crystallization of strongly peraluminous trondhjemite. Early magnetite saturation in the trondhjemite was suppressed, either because the parental trondhjemitic magma had a lower initial total Fe content or because it had a lower ferric-ferrous ratio, possibly reflecting a lower oxygen fugacity. Accumulation of magnetite from Fe-rich residual magma is a viable mechanism for the concentration of iron, and the subsequent formation of Fe-rich rocks, in calcic siliceous intrusions. Apparently, Fe-enrichment can occur locally in calcic magmas, and is not restricted to rocks of mafic tholeiitic or anorthositic affinity.

Petrology of iron-rich magmatic segregations associated with strongly peraluminous trondhjemite in the Cornucopia stock, northeastern Oregon

NASA Astrophysics Data System (ADS)

Johnson, K.; Barnes, C. G.; Browning, J. M.; Karlsson, H. R.

2001-11-01

The Middle Cretaceous Cornucopia stock in the Blue Mountains of northeastern Oregon is a small composite intrusion consisting of hornblende biotite tonalite, biotite trondhjemite, and three cordierite two mica trondhjemite units. Unusual magnetite + biotite-rich tonalitic rocks are associated with the Crater Lake cordierite trondhjemite, the youngest of the intrusions. Oxide-rich tonalites are characterized by high Fe ( 47-68 wt% total Fe as FeO), low SiO2 (<36 wt%), and enrichments in HFSE and REE (La(N)=361-903). Oxide-rich tonalites appear in a variety of forms, including composite dikes and sheets, in which they are associated with leucocratic tonalite. Leucotonalite is lower in SiO2 (60-72 wt%) than Crater Lake trondhjemite, and generally has ΣREE contents and Eu anomalies intermediate between the oxide-rich tonalite and Crater Lake compositions. Oxide-rich tonalites crosscut, and are crosscut by, shear zones in the host trondhjemite, indicating their emplacement late in the pluton's crystallization history. Granitic dikes crosscut the composite dikes in all localities. Geochemical considerations and sedimentary-like structures, such as load casts and bedding of magnetite-rich assemblages in the composite dikes and sheets, are suggestive of crystal settling from an Fe-rich parental magma. The Fe-rich liquid parental to the oxide-rich tonalite-leucotonalite pairs formed by extensive, in-situ, plagioclase + quartz-dominated crystallization of strongly peraluminous trondhjemite. Early magnetite saturation in the trondhjemite was suppressed, either because the parental trondhjemitic magma had a lower initial total Fe content or because it had a lower ferric-ferrous ratio, possibly reflecting a lower oxygen fugacity. Accumulation of magnetite from Fe-rich residual magma is a viable mechanism for the concentration of iron, and the subsequent formation of Fe-rich rocks, in calcic siliceous intrusions. Apparently, Fe-enrichment can occur locally in calcic magmas, and is not restricted to rocks of mafic tholeiitic or anorthositic affinity.

Multi-functional ultrathin Pd xCu 1-x and Pt~Pd xCu 1-x one-dimensional nanowire motifs for various small molecule oxidation reactions

DOE PAGES

Liu, Haiqing; Wong, Stanislaus S.; Adzic, Radoslav R.

2015-11-18

Developing novel electrocatalysts for small molecule oxidation processes, including formic acid oxidation (FAOR), methanol oxidation reaction (MOR), and ethanol oxidation reaction (EOR), denoting the key anodic reactions for their respective fuel cell configurations, is a significant and relevant theme of recent efforts in the field. Herein, in this report, we demonstrated a concerted effort to couple and combine the benefits of small size, anisotropic morphology, and tunable chemical composition in order to devise a novel “family” of functional architectures. In particular, we have fabricated not only ultrathin 1-D Pd 1–xCu x alloys but also Pt-coated Pd 1–xCu x (i.e., Pt~Pdmore » 1–xCu x; herein the ~ indicates an intimate association, but not necessarily actual bond formation, between the inner bimetallic core and the Pt outer shell) core–shell hierarchical nanostructures with readily tunable chemical compositions by utilizing a facile, surfactant-based, wet chemical synthesis coupled with a Cu underpotential deposition technique. Our main finding is that our series of as-prepared nanowires are functionally flexible. More precisely, we demonstrate that various examples within this “family” of structural motifs can be tailored for exceptional activity with all 3 of these important electrocatalytic reactions. In particular, we note that our series of Pd 1–xCu x nanowires all exhibit enhanced FAOR activities as compared with not only analogous Pd ultrathin nanowires but also commercial Pt and Pd standards, with Pd 9Cu representing the “optimal” composition. Moreover, our group of Pt~Pd 1–xCu x nanowires consistently outperformed not only commercial Pt NPs but also ultrathin Pt nanowires by several fold orders of magnitude for both the MOR and EOR reactions in alkaline media. As a result, the variation of the MOR and EOR performance with the chemical composition of our ultrathin Pt~Pd 1–xCu x nanowires was also discussed.« less

Ferrate(VI)-Prompted Removal of Metals in Aqueous Media: Mechanistic Delineation of Enhanced Efficiency via Metal Entrenchment in Magnetic Oxides

EPA Science Inventory

The removal efficiency of heavy metal ions (cadmium(II) – Cd(II), cobalt(II) – Co(II), nickel(II) – Ni(II), and copper(II) – Cu(II)) by potassium ferrate(VI) (K2FeO4, Fe(VI)), was studied as a function of added amount of Fe(VI) (or Fe) and varying pH. At pH = 6.6, the effective r...

Ionic configuration of copper ferrimanganites Cu 0.5Mn xFe 2.5- xO 4

NASA Astrophysics Data System (ADS)

Lenglet, M.; Kasperek, J.; Hannoyer, B.; Lopitaux, J.; d'Huysser, A.; Tellier, J. C.

1992-06-01

Mössbauer spectrometry, neutron diffraction, XANES, and XPS have led to the determination of the cation distributions of the system Cu 0.5Mn xFe 2.5- xO 4 (0≤ x≤1.5). The three cations are present in both tetrahedral and octahedral sites, and the relative number of Fe ions on A- and B-sites remains nearly constant in the whole range of x. It appears that for x≤0.5 manganese is divalent and copper is in its two oxidation states. For x>0.5 copper and iron are respectively divalent and trivalent; the manganese is in +2 and +3 oxydation states.

Air plasma spray processing and electrochemical characterization of Cu-SDC coatings for use in solid oxide fuel cell anodes

NASA Astrophysics Data System (ADS)

Benoved, Nir; Kesler, O.

Air plasma spraying has been used to produce porous composite anodes based on Ce 0.8Sm 0.2O 1.9 (SDC) and Cu for use in solid oxide fuel cells (SOFCs). Preliminarily, a range of plasma conditions has been examined for the production of composite coatings from pre-mixed SDC and CuO powders. Plasma gas compositions were varied to obtain a range of plasma temperatures. After reduction in H 2, coatings were characterized for composition and microstructure using EDX and SEM. As a result of these tests, symmetrical sintered electrolyte-supported anode-anode cells were fabricated by air plasma spraying of the anodes, followed by in situ reduction of the CuO to Cu. Full cells deposited on SS430 porous substrates were then produced in one integrated process. Fine CuO and SDC powders have been used to produce homogeneously mixed anode coatings with higher surface area microstructures, resulting in area-specific polarization resistances of 4.8 Ω cm 2 in impedance tests in hydrogen at 712 °C.

STUDY OF THE FUNDAMENTALS OF MERCURY SPECIATION IN COAL-FIRED BOILERS UNDER SIMULATED POST-COMBUSTION CONDITIONS

EPA Science Inventory

The report discusses a continuation of the study on mercury speciation initiated in the fiscal year 1997 (FY97). The previous study found that cupric oxide (CuO) and ferric oxide (Fe2O3) in the presence of hydrogen chloride (HCl) promote elemental mercury oxidation in simulated f...