Combination of dynamic transformation and dynamic recrystallization for realizing ultrafine-grained steels with superior mechanical properties

PubMed Central

Zhao, Lijia; Park, Nokeun; Tian, Yanzhong; Shibata, Akinobu; Tsuji, Nobuhiro

2016-01-01

Dynamic recrystallization (DRX) is an important grain refinement mechanism to fabricate steels with high strength and high ductility (toughness). The conventional DRX mechanism has reached the limitation of refining grains to several microns even though employing high-strain deformation. Here we show a DRX phenomenon occurring in the dynamically transformed (DT) ferrite, by which the required strain for the operation of DRX and the formation of ultrafine grains is significantly reduced. The DRX of DT ferrite shows an unconventional temperature dependence, which suggests an optimal condition for grain refinement. We further show that new strategies for ultra grain refinement can be evoked by combining DT and DRX mechanisms, based on which fully ultrafine microstructures having a mean grain size down to 0.35 microns can be obtained without high-strain deformation and exhibit superior mechanical properties. This study will open the door to achieving optimal grain refinement to nanoscale in a variety of steels requiring no high-strain deformation in practical industrial application. PMID:27966603

Evolution of twinning in extruded AZ31 alloy with bimodal grain structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Garcés, G., E-mail: ggarces@cenim.csic.es

2017-04-15

Twinning in extruded AZ31 alloy with a bimodal grain structure is studied under compression along the extrusion direction. This study has combined in-situ measurements during the compression tests by Synchrotron Radiation Diffraction and Acoustic Emission techniques and the evaluation of the microstructure and texture in post-mortem compression samples deformed at different strains. The microstructure of the alloy is characterized by the coexistence of large areas of fine dynamic recrystallized grains and coarse non-recrystallized grains elongated along extrusion direction. Twinning occurs initially in large elongated grains before the macroscopic yield stress which is controlled by the twinning in equiaxed dynamically recrystallizedmore » grains. - Highlights: • The AZ31 extruded at low temperature exhibits a bimodal grains structure. • Twinning takes place before macroscopic yielding in coarse non-DRXed grains. • DRXed grains controls the beginning of plasticity in magnesium alloys with bimodal grain structure.« less

Strain softening during tension in cold drawn Cu–Ag alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang, L.L., E-mail: lilichang@sdu.edu.cn; Wen, S.; Li, S.L.

2015-10-15

Experiments were conducted on Cu–0.1wt.%Ag alloys to evaluate the influence of producing procedures and annealing conditions on microstructure evolution and mechanical properties of Cu–Ag alloys. Optical microscopy (OM), electron back-scattered diffraction (EBSD), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used for microstructural evaluation and mechanical properties were characterized by tensile tests. The results indicated that hot-extruded Cu–Ag alloys had a typical dynamic recrystallized microstructure with equiaxed grains. Cold drawing at room temperature leaded to partial recrystallized microstructure with a mixture of coarse and fine grains. The dominate {001}<100 > cubic texture formed during hot extrusion was changed tomore » be {112}<111 > copper texture by cold drawing. Strain softening occurred during room temperature tension of cold drawn Cu–Ag alloys with an average grain size of 13–19.7 μm. - Highlights: • Strain softening occurred during tension of Cu–Ag alloys with coarse grain size. • Work hardening was observed in hot-extruded and annealed Cu–0.1wt.%Ag alloys. • Strain softening was ascribed to dynamic recovery and dynamic recrystallization.« less

EBSD characterization of low temperature deformation mechanisms in modern alloys

NASA Astrophysics Data System (ADS)

Kozmel, Thomas S., II

For structural applications, grain refinement has been shown to enhance mechanical properties such as strength, fatigue resistance, and fracture toughness. Through control of the thermos-mechanical processing parameters, dynamic recrystallization mechanisms were used to produce microstructures consisting of sub-micron grains in 9310 steel, 4140 steel, and Ti-6Al-4V. In both 9310 and 4140 steel, the distribution of carbides throughout the microstructure affected the ability of the material to dynamically recrystallize and determined the size of the dynamically recrystallized grains. Processing the materials at lower temperatures and higher strain rates resulted in finer dynamically recrystallized grains. Microstructural process models that can be used to estimate the resulting microstructure based on the processing parameters were developed for both 9310 and 4140 steel. Heat treatment studies performed on 9310 steel showed that the sub-micron grain size obtained during deformation could not be retained due to the low equilibrium volume fraction of carbides. Commercially available aluminum alloys were investigated to explain their high strain rate deformation behavior. Alloys such as 2139, 2519, 5083, and 7039 exhibit strain softening after an ultimate strength is reached, followed by a rapid degradation of mechanical properties after a critical strain level has been reached. Microstructural analysis showed that the formation of shear bands typically preceded this rapid degradation in properties. Shear band boundary misorientations increased as a function of equivalent strain in all cases. Precipitation behavior was found to greatly influence the microstructural response of the alloys. Additionally, precipitation strengthened alloys were found to exhibit similar flow stress behavior, whereas solid solution strengthened alloys exhibited lower flow stresses but higher ductility during dynamic loading. Schmid factor maps demonstrated that shear band formation behavior was influenced by texturing in these alloys.

Grain size evolution and convection regimes of the terrestrial planets

NASA Astrophysics Data System (ADS)

Rozel, A.; Golabek, G. J.; Boutonnet, E.

2011-12-01

A new model of grain size evolution has recently been proposed in Rozel et al. 2010. This new approach stipulates that the grain size dynamics is governed by two additive and simultaneous processes: grain growth and dynamic recrystallization. We use the usual normal grain growth laws for the growth part. For dynamic recrystallization, reducing the mean grain size increases the total area of grain boundaries. Grain boundaries carry some surface tension, so some energy is required to decrease the mean grain size. We consider that this energy is available during mechanical work. It is usually considered to produce some heat via viscous dissipation. A partitioning parameter f is then required to know what amount of energy is dissipated and what part is converted in surface tension. This study gives a new calibration of the partitioning parameter on major Earth materials involved in the dynamic of the terrestrial planets. Our calibration is in adequation with the published piezometric relations available in the literature (equilibrium grain size versus shear stress). We test this new model of grain size evolution in a set of numerical computations of the dynamics of the Earth using stagYY. We show that the grain size evolution has a major effect on the convection regimes of terrestrial planets.

Understanding the Effect of Grain Boundary Character on Dynamic Recrystallization in Stainless Steel 316L

NASA Astrophysics Data System (ADS)

Beck, Megan; Morse, Michael; Corolewski, Caleb; Fritchman, Koyuki; Stifter, Chris; Poole, Callum; Hurley, Michael; Frary, Megan

2017-08-01

Dynamic recrystallization (DRX) occurs during high-temperature deformation in metals and alloys with low to medium stacking fault energies. Previous simulations and experimental research have shown the effect of temperature and grain size on DRX behavior, but not the effect of the grain boundary character distribution. To investigate the effects of the distribution of grain boundary types, experimental testing was performed on stainless steel 316L specimens with different initial special boundary fractions (SBF). This work was completed in conjunction with computer simulations that used a modified Monte Carlo method which allowed for the addition of anisotropic grain boundary energies using orientation data from electron backscatter diffraction (EBSD). The correlation of the experimental and simulation work allows for a better understanding of how the input parameters in the simulations correspond to what occurs experimentally. Results from both simulations and experiments showed that a higher fraction of so-called "special" boundaries ( e.g., Σ3 twin boundaries) delayed the onset of recrystallization to larger strains and that it is energetically favorable for nuclei to form on triple junctions without these so-called "special" boundaries.

Dynamic Recrystallization Behavior and Corrosion Resistance of a Dual-Phase Mg-Li Alloy

PubMed Central

Liu, Gang; Xie, Wen; Wei, Guobing; Yang, Yan; Liu, Junwei; Xu, Tiancai; Xie, Weidong; Peng, Xiaodong

2018-01-01

The hot deformation and dynamic recrystallization behavior of the dual-phase Mg-9Li-3Al-2Sr-2Y alloy had been investigated using a compression test. The typical dual-phase structure was observed, and average of grain size of as-homogenized alloy is about 110 µm. It mainly contains β-Li, α-Mg, Al4Sr and Al2Y phases. The dynamic recrystallization (DRX) kinetic was established based on an Avrami type equation. The onset of the DRX process occurred before the peak of the stress–strain flow curves. It shows that the DRX volume fraction increases with increasing deformation temperature or decreasing strain rate. The microstructure evolution during the hot compression at various temperatures and strain rates had been investigated. The DRX grain size became larger with the increasing testing temperature or decreasing strain rate because the higher temperature or lower strain rate can improve the migration of DRX grain boundaries. The fully recrystallized microstructure can be achieved in a small strain due to the dispersed island-shape α-Mg phases, continuous the Al4Sr phases and spheroidal Al2Y particles, which can accelerate the nucleation. The continuous Al4Sr phases along the grain boundaries are very helpful for enhancing the corrosion resistance of the duplex structured Mg-Li alloy, which can prevent the pitting corrosion and filiform corrosion. PMID:29522473

Dynamic Recrystallization Behavior and Corrosion Resistance of a Dual-Phase Mg-Li Alloy.

PubMed

Liu, Gang; Xie, Wen; Wei, Guobing; Yang, Yan; Liu, Junwei; Xu, Tiancai; Xie, Weidong; Peng, Xiaodong

2018-03-09

The hot deformation and dynamic recrystallization behavior of the dual-phase Mg-9Li-3Al-2Sr-2Y alloy had been investigated using a compression test. The typical dual-phase structure was observed, and average of grain size of as-homogenized alloy is about 110 µm. It mainly contains β-Li, α-Mg, Al₄Sr and Al₂Y phases. The dynamic recrystallization (DRX) kinetic was established based on an Avrami type equation. The onset of the DRX process occurred before the peak of the stress-strain flow curves. It shows that the DRX volume fraction increases with increasing deformation temperature or decreasing strain rate. The microstructure evolution during the hot compression at various temperatures and strain rates had been investigated. The DRX grain size became larger with the increasing testing temperature or decreasing strain rate because the higher temperature or lower strain rate can improve the migration of DRX grain boundaries. The fully recrystallized microstructure can be achieved in a small strain due to the dispersed island-shape α-Mg phases, continuous the Al₄Sr phases and spheroidal Al₂Y particles, which can accelerate the nucleation. The continuous Al₄Sr phases along the grain boundaries are very helpful for enhancing the corrosion resistance of the duplex structured Mg-Li alloy, which can prevent the pitting corrosion and filiform corrosion.

Disclination mediated dynamic recrystallization in metals at low temperature.

PubMed

Aramfard, Mohammad; Deng, Chuang

2015-09-16

Recrystallization is one of the most important physical phenomena in condensed matter that has been utilized for materials processing for thousands of years in human history. It is generally believed that recrystallization is thermally activated and a minimum temperature must be achieved for the necessary atomic mechanisms to occur. Here, using atomistic simulations, we report a new mechanism of dynamic recrystallization that can operate at temperature as low as T = 10 K in metals during deformation. In contrast to previously proposed dislocation-based models, this mechanism relies on the generation of disclination quadrupoles, which are special defects that form during deformation when the grain boundary migration is restricted by structural defects such as triple junctions, cracks or obstacles. This mechanism offers an alternative explanation for the grain refinement in metals during severe plastic deformation at cryogenic temperature and may suggest a new method to tailor the microstructure in general crystalline materials.

Disclination mediated dynamic recrystallization in metals at low temperature

PubMed Central

Aramfard, Mohammad; Deng, Chuang

2015-01-01

Recrystallization is one of the most important physical phenomena in condensed matter that has been utilized for materials processing for thousands of years in human history. It is generally believed that recrystallization is thermally activated and a minimum temperature must be achieved for the necessary atomic mechanisms to occur. Here, using atomistic simulations, we report a new mechanism of dynamic recrystallization that can operate at temperature as low as T = 10 K in metals during deformation. In contrast to previously proposed dislocation-based models, this mechanism relies on the generation of disclination quadrupoles, which are special defects that form during deformation when the grain boundary migration is restricted by structural defects such as triple junctions, cracks or obstacles. This mechanism offers an alternative explanation for the grain refinement in metals during severe plastic deformation at cryogenic temperature and may suggest a new method to tailor the microstructure in general crystalline materials. PMID:26374603

Effect of Hot Rolling on the Microstructure and Mechanical Properties of Nitrogen Alloyed Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Chenna Krishna, S.; Karthick, N. K.; Jha, Abhay K.; Pant, Bhanu; Cherian, Roy M.

2018-05-01

In the present investigation, the effect of multi-pass hot rolling in the temperature range of 700-1000 °C on the microstructure and mechanical properties of nitrogen alloyed austenitic stainless steel was studied with the aid of optical microscopy, tensile testing and x-ray diffraction measurements. The microstructural changes that occurred in the hot rolled specimens were elongation of grains in rolling direction, nucleation of new grains at the grain boundaries of elongated grains and growth of nucleated grains to form fully recrystallized grains. Elongated grains formed at lower rolling temperature (700-800 °C) due to inadequate strain/temperature for the initiation of dynamic recrystallization. At higher rolling temperature (900-1000 °C), fine grains formed due to dynamic recrystallization. Tensile properties showed strong dependency on the rolling temperature. Tensile strength increased with the decrease in the rolling temperature at the cost of ductility. Maximum strength was observed in samples hot rolled at 700 °C with yield strength of 917 MPa and ductility of 25%. This variation in the tensile properties with the rolling temperature is attributed to changes in the dislocation density and grain structure. The estimated yield strength from the dislocation density, solid solution and grain boundary strengthening closely matched with experimentally determined yield strength confirming the role of dislocation density and grain size in the strengthening.

Effect of Hot Rolling on the Microstructure and Mechanical Properties of Nitrogen Alloyed Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Chenna Krishna, S.; Karthick, N. K.; Jha, Abhay K.; Pant, Bhanu; Cherian, Roy M.

2018-04-01

In the present investigation, the effect of multi-pass hot rolling in the temperature range of 700-1000 °C on the microstructure and mechanical properties of nitrogen alloyed austenitic stainless steel was studied with the aid of optical microscopy, tensile testing and x-ray diffraction measurements. The microstructural changes that occurred in the hot rolled specimens were elongation of grains in rolling direction, nucleation of new grains at the grain boundaries of elongated grains and growth of nucleated grains to form fully recrystallized grains. Elongated grains formed at lower rolling temperature (700-800 °C) due to inadequate strain/temperature for the initiation of dynamic recrystallization. At higher rolling temperature (900-1000 °C), fine grains formed due to dynamic recrystallization. Tensile properties showed strong dependency on the rolling temperature. Tensile strength increased with the decrease in the rolling temperature at the cost of ductility. Maximum strength was observed in samples hot rolled at 700 °C with yield strength of 917 MPa and ductility of 25%. This variation in the tensile properties with the rolling temperature is attributed to changes in the dislocation density and grain structure. The estimated yield strength from the dislocation density, solid solution and grain boundary strengthening closely matched with experimentally determined yield strength confirming the role of dislocation density and grain size in the strengthening.

Deformation Behavior of a Coarse-Grained Mg-8Al-1.5Ca-0.2Sr Magnesium Alloy at Elevated Temperatures

NASA Astrophysics Data System (ADS)

Lou, Yan; Liu, Xiao

2018-02-01

The compression tests were carried out on a coarse-grained Mg-8Al-1.5Ca-0.2Sr magnesium alloy samples at temperatures from 300 to 450 °C and strain rates from 0.001 to 10 s-1. The flow stress curves were analyzed using the double-differentiation method, and double minima were detected on the flow curves. The first set of minima is shown to identify the critical strain for twinning, while the second set indicates the critical strain for the initiation of dynamic recrystallization (DRX). Twin variant selection was numerically identified by comprehensive analysis of the Schmid factors for different deformation modes and the accommodation strains imposed on neighboring grains. It was found that twinning is initiated before DRX. Dynamic recrystallization volume increases with strain rate at a given deformation temperature. At high strain rate, various twin variants are activated to accommodate deformation, leading to the formation of twin intersections and high DRX volume. Fully dynamic recrystallized structure can be obtained at both high and low strain rates due to the high mobility of the grain and twin boundaries at the temperature of 400 °C.

Dynamic recrystallization mechanisms and their transition in the Daling Thrust (DT) zone, Darjeeling-Sikkim Himalaya

NASA Astrophysics Data System (ADS)

Ghosh, Subhajit; Bose, Santanu; Mandal, Nibir; Dasgupta, Sujoy

2016-04-01

The Daling Thrust (DT) delineates a zone of intense shear localization in the Lesser Himalayan Sequence (LHS) of the Darjeeling-Sikkim Himalaya. From microstructural studies of deformed quartzite samples, we show a transition in the dynamic recrystallization mechanism with increasing distance from the DT, dominated by grain boundary bulging (BLG) recrystallization closest to the DT, and progressively replaced by sub-grain rotation (SGR) recrystallization away from the thrust. The transition is marked by a characteristic variation in the fractal dimension (D) of grain boundaries, estimated from the area-perimeter method. For the BLG regime, D ≈ 1.046, which decreases significantly to a value as low as 1.025 for the SGR regime. Using the available thermal data for BLG and SGR recrystallization, we infer increasing deformation temperatures away from the DT in the hanging wall. Based on the quartz piezometer our estimates reveal strong variations in the flow stress (59.00 MPa to 16.00 MPa) over a distance of 1.2 km from the DT. Deformation mechanism maps constructed for different temperatures indicate that the strain rates (10- 12 S- 1 to 10- 14 S- 1) comply with the geologically possible range. Finally, we present a mechanical model to provide a possible explanation for the cause of stress intensification along the DT.

Ion-specific ice recrystallization provides a facile approach for the fabrication of porous materials

NASA Astrophysics Data System (ADS)

Wu, Shuwang; Zhu, Chongqin; He, Zhiyuan; Xue, Han; Fan, Qingrui; Song, Yanlin; Francisco, Joseph S.; Zeng, Xiao Cheng; Wang, Jianjun

2017-05-01

Ice recrystallization is of great importance to both fundamental research and practical applications, however understanding and controlling ice recrystallization processes remains challenging. Here, we report the discovery of an ion-specific effect on ice recrystallization. By simply changing the initial type and concentration of ions in an aqueous solution, the size of ice grains after recrystallization can be tuned from 27.4+/-4.1 to 277.5+/-30.9 μm. Molecular dynamics simulations show that the ability of the ion to be incorporated into the ice phase plays a key role in the ultimate size of the ice grains after recrystallization. Moreover, by using recrystallized ice crystals as templates, 2D and 3D porous networks with tuneable pore sizes could be prepared from various materials, for example, NaBr, collagen, quantum dots, silver and polystyrene colloids. These porous materials are suitable for a wide range of applications, for example, in organic electronics, catalysis and bioengineering.

Microstructural evolution and rheology of quartz in a mid-crustal shear zone

NASA Astrophysics Data System (ADS)

Rahl, Jeffrey M.; Skemer, Philip

2016-06-01

We present microstructural and crystallographic preferred orientation (CPO) data on quartz deformed in the middle crust to explore the interaction and feedback between dynamic recrystallization, deformation processes, and CPO evolution. The sample investigated here is a moderately deformed quartz-rich mylonite from the Blue Ridge in Virginia. We have created high-resolution crystallographic orientation maps using electron backscatter diffraction (EBSD) of 51 isolated quartz porphyroclasts with recrystallized grain fractions ranging from 10 to 100%. Recrystallized grains are internally undeformed and display crystallographic orientations dispersed around the orientation of the associated parent porphyroclast. We document a systematic decrease in fabric intensity with recrystallization, suggesting that progressive deformation of the recrystallized domains involves processes that can weaken a pre-existing CPO. Relationships between recrystallization fraction and shear strain suggest that complete microstructural re-equilibration requires strains in excess of γ = 5. Variation in the degree of recrystallization implies that strain was accumulated heterogeneously, and that a steady-state microstructure and rheology were not achieved.

Ion-specific ice recrystallization provides a facile approach for the fabrication of porous materials

PubMed Central

Wu, Shuwang; Zhu, Chongqin; He, Zhiyuan; Xue, Han; Fan, Qingrui; Song, Yanlin; Francisco, Joseph S.; Zeng, Xiao Cheng; Wang, Jianjun

2017-01-01

Ice recrystallization is of great importance to both fundamental research and practical applications, however understanding and controlling ice recrystallization processes remains challenging. Here, we report the discovery of an ion-specific effect on ice recrystallization. By simply changing the initial type and concentration of ions in an aqueous solution, the size of ice grains after recrystallization can be tuned from 27.4±4.1 to 277.5±30.9 μm. Molecular dynamics simulations show that the ability of the ion to be incorporated into the ice phase plays a key role in the ultimate size of the ice grains after recrystallization. Moreover, by using recrystallized ice crystals as templates, 2D and 3D porous networks with tuneable pore sizes could be prepared from various materials, for example, NaBr, collagen, quantum dots, silver and polystyrene colloids. These porous materials are suitable for a wide range of applications, for example, in organic electronics, catalysis and bioengineering. PMID:28462937

Ion-specific ice recrystallization provides a facile approach for the fabrication of porous materials.

PubMed

Wu, Shuwang; Zhu, Chongqin; He, Zhiyuan; Xue, Han; Fan, Qingrui; Song, Yanlin; Francisco, Joseph S; Zeng, Xiao Cheng; Wang, Jianjun

2017-05-02

Ice recrystallization is of great importance to both fundamental research and practical applications, however understanding and controlling ice recrystallization processes remains challenging. Here, we report the discovery of an ion-specific effect on ice recrystallization. By simply changing the initial type and concentration of ions in an aqueous solution, the size of ice grains after recrystallization can be tuned from 27.4±4.1 to 277.5±30.9 μm. Molecular dynamics simulations show that the ability of the ion to be incorporated into the ice phase plays a key role in the ultimate size of the ice grains after recrystallization. Moreover, by using recrystallized ice crystals as templates, 2D and 3D porous networks with tuneable pore sizes could be prepared from various materials, for example, NaBr, collagen, quantum dots, silver and polystyrene colloids. These porous materials are suitable for a wide range of applications, for example, in organic electronics, catalysis and bioengineering.

Surface damage and structure evolution of recrystallized tungsten exposed to ELM-like transient loads

NASA Astrophysics Data System (ADS)

Yuan, Y.; Du, J.; Wirtz, M.; Luo, G.-N.; Lu, G.-H.; Liu, W.

2016-03-01

Surface damage and structure evolution of the full tungsten ITER divertor under transient heat loads is a key concern for component lifetime and plasma operations. Recrystallization caused by transients and steady-state heat loads can lead to degradation of the material properties and is therefore one of the most serious issues for tungsten armor. In order to investigate the thermal response of the recrystallized tungsten under edge localized mode-like transient thermal loads, fully recrystallized tungsten samples with different average grain sizes are exposed to cyclic thermal shocks in the electron beam facility JUDITH 1. The results indicate that not only does the microstructure change due to recrystallization, but that the surface residual stress induced by mechanical polishing strongly influences the surface cracking behavior. The stress-free surface prepared by electro-polishing is shown to be more resistant to cracking than the mechanically polished one. The resulting surface roughness depends largely on the loading conditions instead of the recrystallized-grain size. As the base temperature increases from room temperature to 400 °C, surface roughening mainly due to the shear bands in each grain becomes more pronounced, and sub-grains (up to 3 μm) are simultaneously formed in the sub-surface. The directions of the shear bands exhibit strong grain-orientation dependence, and they are generally aligned with the traces of {1 1 2} twin habit planes. The results suggest that twinning deformation and dynamic recrystallization represent the predominant mechanism for surface roughening and related microstructure evolution.

Effect of Strain Rate on Hot Ductility Behavior of a High Nitrogen Cr-Mn Austenitic Steel

NASA Astrophysics Data System (ADS)

Wang, Zhenhua; Meng, Qing; Qu, Minggui; Zhou, Zean; Wang, Bo; Fu, Wantang

2016-03-01

18Mn18Cr0.6N steel specimens were tensile tested between 1173 K and 1473 K (900 °C and 1200 °C) at 9 strain rates ranging from 0.001 to 10 s-1. The tensile strained microstructures were analyzed through electron backscatter diffraction analysis. The strain rate was found to affect hot ductility by influencing the strain distribution, the extent of dynamic recrystallization and the resulting grain size, and dynamic recovery. The crack nucleation sites were primarily located at grain boundaries and were not influenced by the strain rate. At 1473 K (1200 °C), a higher strain rate was beneficial for grain refinement and preventing hot cracking; however, dynamic recovery appreciably occurred at 0.001 s-1 and induced transgranular crack propagation. At 1373 K (1100 °C), a high extent of dynamic recrystallization and fine new grains at medium strain rates led to good hot ductility. The strain gradient from the interior of the grain to the grain boundary increased with decreasing strain rate at 1173 K and 1273 K (900 °C and 1000 °C), which promoted hot cracking. Grain boundary sliding accompanied grain rotation and did not contribute to hot cracking.

Constitutive modeling and dynamic softening mechanism during hot deformation of an ultra-pure 17%Cr ferritic stainless steel stabilized with Nb

NASA Astrophysics Data System (ADS)

Gao, Fei; Liu, Zhenyu; Misra, R. D. K.; Liu, Haitao; Yu, Fuxiao

2014-09-01

The hot deformation behavior of an ultra-pure 17%Cr ferritic stainless steel was studied in the temperature range of 750-1000 °C and strain rates of 0.5 to 10 s-1 using isothermal hot compression tests in a thermomechanical simulator. The microstructural evolution was investigated using electron backscattered diffraction and transmission electron microscopy. A modified constitutive equation considering the effect of strain on material constant was developed, which predicted the flow stress for the deformation conditions studied, except at 950 °C in 1 s-1 and 900 °C in 10 s-1. Decreasing deformation temperature and increasing strain was beneficial in refining the microstructure. Decreasing deformation temperature, the in-grain shear bands appeared in the microstructure. It is suggested that the dynamic softening mechanism is closely related to deformation temperature. At low deformation temperature, dynamic recovery was major softening mechanism and no dynamic recrystallization occurred. At high deformation temperature, dynamic softening was explained in terms of efficient dynamic recovery and limited continuous dynamic recrystallization. A drop in the flow stress was not found due to very small fraction of new grains nucleated during dynamic recrystallization.

Quarzt Fabric Insights Across a Low P-High T Shear Zone

NASA Astrophysics Data System (ADS)

Gomez Barreiro, J.; Martinez-Catalan, J. R.; Benitez Perez, J.; Wenk, H.; Vogel, S. C.; Alcock, J. E.

2013-12-01

The evolution of mylonitic fabric in quartzites across a Low-P / High-T gradient within the Lugo Dome Extensional system (NW Spain) is analyzed. Quantitative texture measurements with TOF neutron diffraction, Shape preferred orientation (SPO) and Crystal Size Distribution (CSD) analyses were correlated with tectonothermal data to constraint the prevalence of ductile deformative fabrics exposed to cycles of dynamic and static recrystallization. Results suggest two stages in the evolution of mylonites in close correlation to thermal gradient, 1) a pervasive ductile deformation affecting most of the shear zone volume, with the development of symmetric cross girdle c-axes fabric suggesting slip on {c,r,m} and dynamically recrystallized microstructures which resulted into the refinement of the grain-size. 2) An heterogeneous deformation stage where strain partition led to the formation of relatively active and passive domains. During this late stage, at deeper levels, High T detachments show [c]{m} slip system and dynamic recrystallization activation, with monoclinic texture patterns, meanwhile, passive domains followed an static recrystallization with abnormal grain growth and minor variation of early orthogonal texture patterns Neutron diffraction data (cross) and Rietveld model obtained with MAUD (solid line) of a mylonitic quartzite. Some important planes are indicated for the major phases.

The Microstructural Evolution and Special Flow Behavior of Ti-5Al-2Sn-2Zr-4Mo-4Cr During Isothermal Compression at a Low Strain Rate

NASA Astrophysics Data System (ADS)

Sun, J. Z.; Li, M. Q.; Li, H.

2017-09-01

The microstructural evolution and special flow behavior of Ti-5Al-2Sn-2Zr-4Mo-4Cr during isothermal compression at a strain rate of 0.0001 s-1 were investigated. The dislocation climbs in elongated α grains resulted in the formation of low-angle boundaries that transform into high-angle boundaries with greater deformation, and the elongated α grains subsequently separated into homogenous globular α grains with the penetration of the β phase. The simultaneous occurrence of discontinuous dynamic recrystallization and continuous dynamic recrystallization in the primary β grains resulted in a trimode grain distribution. The β grains surrounded by dislocations presented an equilateral-hexagonal morphology, which suggests that grain boundary sliding through dislocation climbs was the main deformation mechanism. The true stress-strain curves for 1073 and 1113 K abnormally intersect at a strain of 0.35, related to the α → β phase transformation and distinct growth of the β grain size.

Compositional changes of minerals associated with dynamic recrystallizatin

NASA Astrophysics Data System (ADS)

Yund, Richard A.; Tullis, Jan

1991-09-01

The rate of compositional and isotopic exchange between minerals may be enhanced significantly if the rock is deformed simultaneously. The enhanced exchange rate may result from a reduction in grain size (shorter distance for volume diffusion), dissolution and growth of grains by diffusion creep (pressure solution), or the movement of high-angle grain boundaries through strained grains during recrystallization in the dislocation creep regime. The migration of high-angle grain boundaries provides high diffusivity paths for the rapid exchange of components during recrystallization. The operation of the latter process has been demonstrated by deforming aggregates consisting of two plagioclases (An1 and An79) at 900°C, 1 GPa confining pressure, and a strain rate of ˜2x10-6s-1. The polygonal, recrystallized grains were analyzed using an analytical transmission electron microscope and have a variable but often intermediate composition. At the conditions of these experiments, the volume interdiffusion rate of NaSi/CaAl is too slow to produce any observable chemical change, and microstructural-chemical relations indicate that the contribution from diffusion creep was insignificant except for initially fine-grained (2 10 μm) aggregates. These results indicate that strain-induced recrystallization can be an effective mechanism for enhancing the kinetics of metamorphic reactions and for resetting the isotope systematics of minerals such as feldspars, pyroxenes, and amphiboles.

The effect of hydrocarbons on the microstructural evolution in rock salt: a case study on hydrocarbon bearing Ara salt from the South Oman Salt Basin

NASA Astrophysics Data System (ADS)

Schmatz, Joyce; Urai, Janos L.; Wübbeler, Franziska M. M.; Sadler, Marc

2014-05-01

It has been shown that dilatant deformation promotes the incorporation of hydrocarbons into typically low permeable rock salt (Schoenherr et al., 2007). However, there is not much knowledge on subsequent mechanisms related to recrystallization processes, which cause morphological and chemical changes of the carbonic inclusions. This work aims to contribute to an increased understanding of fluid inclusion dynamics related to grain boundary migration recrystallization and hence to facilitate the interpretation of complex microstructures in recrystallized, multiphase salt rocks. In this case study we investigate hydrocarbon-impregnated salt from the Cambrian Ara Group in the South Oman Salt Basin. The samples were cored from cm-m thick anhydrite-salt sequences overlying hydrocarbon bearing carbonate stringers in 3300 m depth. The anhydrite layers consist mainly of fine-grained anhydrite, which contains calcite, dolomite, and olivine inclusions. Solid bitumen and lighter hydrocarbon phases are observed in between the anhydrite grains and along cracks. Anhydrite layers host salt veins, which contain fragments of anhydrite. These fragments do not differ in composition or structure from the host material and the related vein microstructures indicate crack-seal mechanisms. Halite in the salt layers is almost entirely recrystallized with solid inclusions consisting of anhydrite, calcite, dolomite and olivine with hydrocarbon-coatings present inside grains and along grain boundaries. Solid inclusions cause pinning indicated by a decreased recrystallized grain size and by the presence of grains with preserved substructures representing earlier deformation phases. We observe two types of carbonic inclusions: I) solid bitumen coatings along grain boundaries and microcracks, interpreted to be incorporated into the salt in an overpressure state that allowed dilatancy of the salt, and II) less degraded, liquid hydrocarbons along grain boundaries in the vicinity of the anhydrite, interpreted to be incorporated into the salt in a subsequent deformation phase. Type II inclusions usually form arrays of isolated inclusions (liquid hydrocarbons, vapor, and aqueous phases in minor proportions) along grain boundaries of the recrystallized grains, presumably formed in a surface-energy controlled shrinking process from thin fluid films. Here, the contact with mobile grain boundaries promoted necking down and decomposition of multiphase inclusions. We present a model, which describes the dynamic behavior of liquid hydrocarbons in mobile grain boundaries after their enclosure into the salt layers. The model is based on numerous microanalytical methods, such as optical microscopy, fluorescence microscopy, cryo-SEM, and EDX. Schoenherr, J., et al. (2007), Limits to the sealing capacity of rock salt: A case study of the infra-Cambrian Ara Salt from the South Oman salt basin, AAPG Bulletin, 91(11), 1541-1557

The Prediction of Microstructure Evolution of 6005A Aluminum Alloy in a P-ECAP Extrusion Study

NASA Astrophysics Data System (ADS)

Lei, Shi; Jiu-Ba, Wen; Chang, Ren

2018-05-01

Finite element modeling (FEM) was applied for predicting the recrystallized structure in extruded 6005 aluminum alloy, and simulated results were experimentally validated. First, microstructure evolution of 6005 aluminum alloy during deformation was studied by means of isothermal compression test, where the processing parameters were chosen to reproduce the typical industrial conditions. Second, microstructure evolution was analyzed, and the obtained information was used to fit a dynamic recrystallization model implementing inside the DEFORM-3D FEM code environment. FEM of deformation of 6005 aluminum has been established and validated by microstructure comparison. Finally, the obtained dynamic recrystallization model was applied to tube extrusion by using a portholes-equal channel angular pressing die. The finite element analysis results showed that coarse DRX grains occur in the extruded tube at higher temperature and in the extruded tube at the faster speed of the stem. The test results showed material from the front end of the extruded tube has coarse grains (60 μm) and other extruded tube has finer grains (20 μm).

The Prediction of Microstructure Evolution of 6005A Aluminum Alloy in a P-ECAP Extrusion Study

NASA Astrophysics Data System (ADS)

Lei, Shi; Jiu-Ba, Wen; Chang, Ren

2018-04-01

Finite element modeling (FEM) was applied for predicting the recrystallized structure in extruded 6005 aluminum alloy, and simulated results were experimentally validated. First, microstructure evolution of 6005 aluminum alloy during deformation was studied by means of isothermal compression test, where the processing parameters were chosen to reproduce the typical industrial conditions. Second, microstructure evolution was analyzed, and the obtained information was used to fit a dynamic recrystallization model implementing inside the DEFORM-3D FEM code environment. FEM of deformation of 6005 aluminum has been established and validated by microstructure comparison. Finally, the obtained dynamic recrystallization model was applied to tube extrusion by using a portholes-equal channel angular pressing die. The finite element analysis results showed that coarse DRX grains occur in the extruded tube at higher temperature and in the extruded tube at the faster speed of the stem. The test results showed material from the front end of the extruded tube has coarse grains (60 μm) and other extruded tube has finer grains (20 μm).

Microstructure effects on the recrystallization of low-symmetry alpha-uranium

DOE Office of Scientific and Technical Information (OSTI.GOV)

McCabe, Rodney James; Richards, Andrew Walter; Coughlin, Daniel Robert

2015-10-01

We employ electron backscatter diffraction (EBSD) to investigate microstructural evolution of uranium during recrystallization. To understand the relationship between microstructure and recrystallization, we use measures of intra-granular misorientation within grains and near grain boundaries in both deformed (non-recrystallized) uranium and recrystallizing uranium. The data show that the level of intra-granular misorientation depends on crystallographic orientation. However, contrary to expectation, this relationship does not significantly affect the recrystallization texture. Rather, the analysis suggests that recrystallization nucleation occurs along high angle grain boundaries in the deformed microstructure. Specifically, we show that the nucleation of recrystallized grains correlates well with the spatially heterogeneousmore » distribution of high angle boundaries. Due to the inhomogeneous distribution of high angle boundaries, the recrystallized microstructure after long times exhibits clustered distributions of small and large grains. Twin boundaries do not appear to act as recrystallization nucleation sites.« less

A Rate-Theory-Phase-Field Model of Irradiation-Induced Recrystallization in UMo Nuclear Fuels

NASA Astrophysics Data System (ADS)

Hu, Shenyang; Joshi, Vineet; Lavender, Curt A.

2017-12-01

In this work, we developed a recrystallization model to study the effect of microstructures and radiation conditions on recrystallization kinetics in UMo fuels. The model integrates the rate theory of intragranular gas bubble and interstitial loop evolutions and a phase-field model of recrystallization zone evolution. A first passage method is employed to describe one-dimensional diffusion of interstitials with a diffusivity value several orders of magnitude larger than that of fission gas xenons. With the model, the effect of grain sizes on recrystallization kinetics is simulated. The results show that (1) recrystallization in large grains starts earlier than that in small grains, (2) the recrystallization kinetics (recrystallization volume fraction) decrease as the grain size increases, (3) the predicted recrystallization kinetics are consistent with the experimental results, and (4) the recrystallization kinetics can be described by the modified Avrami equation, but the parameters of the Avrami equation strongly depend on the grain size.

Mechanism of secondary recrystallization of Goss grains in grain-oriented electrical steel

NASA Astrophysics Data System (ADS)

Hayakawa, Yasuyuki

2017-12-01

Since its invention by Goss in 1934, grain-oriented (GO) electrical steel has been widely used as a core material in transformers. GO exhibits a grain size of over several millimeters attained by secondary recrystallization during high-temperature final batch annealing. In addition to the unusually large grain size, the crystal direction in the rolling direction is aligned with <001>, which is the easy magnetization axis of α-iron. Secondary recrystallization is the phenomenon in which a certain very small number of {110}<001> (Goss) grains grow selectively (about one in 106 primary grains) at the expense of many other primary recrystallized grains. The question of why the Goss orientation is exclusively selected during secondary recrystallization has long been a main research subject in this field. The general criterion for secondary recrystallization is a small and uniform primary grain size, which is achieved through the inhibition of normal grain growth by fine precipitates called inhibitors. This paper describes several conceivable mechanisms of secondary recrystallization of Goss grains mainly based on the selective growth model.

Mechanism of secondary recrystallization of Goss grains in grain-oriented electrical steel

PubMed Central

Hayakawa, Yasuyuki

2017-01-01

Abstract Since its invention by Goss in 1934, grain-oriented (GO) electrical steel has been widely used as a core material in transformers. GO exhibits a grain size of over several millimeters attained by secondary recrystallization during high-temperature final batch annealing. In addition to the unusually large grain size, the crystal direction in the rolling direction is aligned with <001>, which is the easy magnetization axis of α-iron. Secondary recrystallization is the phenomenon in which a certain very small number of {110}<001> (Goss) grains grow selectively (about one in 106 primary grains) at the expense of many other primary recrystallized grains. The question of why the Goss orientation is exclusively selected during secondary recrystallization has long been a main research subject in this field. The general criterion for secondary recrystallization is a small and uniform primary grain size, which is achieved through the inhibition of normal grain growth by fine precipitates called inhibitors. This paper describes several conceivable mechanisms of secondary recrystallization of Goss grains mainly based on the selective growth model. PMID:28804524

Mechanism of secondary recrystallization of Goss grains in grain-oriented electrical steel.

PubMed

Hayakawa, Yasuyuki

2017-01-01

Since its invention by Goss in 1934, grain-oriented (GO) electrical steel has been widely used as a core material in transformers. GO exhibits a grain size of over several millimeters attained by secondary recrystallization during high-temperature final batch annealing. In addition to the unusually large grain size, the crystal direction in the rolling direction is aligned with <001>, which is the easy magnetization axis of α-iron. Secondary recrystallization is the phenomenon in which a certain very small number of {110}<001> (Goss) grains grow selectively (about one in 10 6 primary grains) at the expense of many other primary recrystallized grains. The question of why the Goss orientation is exclusively selected during secondary recrystallization has long been a main research subject in this field. The general criterion for secondary recrystallization is a small and uniform primary grain size, which is achieved through the inhibition of normal grain growth by fine precipitates called inhibitors. This paper describes several conceivable mechanisms of secondary recrystallization of Goss grains mainly based on the selective growth model.

The importance of grain size to mantle dynamics and seismological observations

NASA Astrophysics Data System (ADS)

Gassmoeller, R.; Dannberg, J.; Eilon, Z.; Faul, U.; Moulik, P.; Myhill, R.

2017-12-01

Grain size plays a key role in controlling the mechanical properties of the Earth's mantle, affecting both long-timescale flow patterns and anelasticity on the timescales of seismic wave propagation. However, dynamic models of Earth's convecting mantle usually implement flow laws with constant grain size, stress-independent viscosity, and a limited treatment of changes in mineral assemblage. We study grain size evolution, its interplay with stress and strain rate in the convecting mantle, and its influence on seismic velocities and attenuation. Our geodynamic models include the simultaneous and competing effects of dynamic recrystallization resulting from dislocation creep, grain growth in multiphase assemblages, and recrystallization at phase transitions. They show that grain size evolution drastically affects the dynamics of mantle convection and the rheology of the mantle, leading to lateral viscosity variations of six orders of magnitude due to grain size alone, and controlling the shape of upwellings and downwellings. Using laboratory-derived scaling relationships, we convert model output to seismologically-observable parameters (velocity, attenuation) facilitating comparison to Earth structure. Reproducing the fundamental features of the Earth's attenuation profile requires reduced activation volume and relaxed shear moduli in the lower mantle compared to the upper mantle, in agreement with geodynamic constraints. Faster lower mantle grain growth yields best fit to seismic observations, consistent with our re-examination of high pressure grain growth parameters. We also show that ignoring grain size in interpretations of seismic anomalies may underestimate the Earth's true temperature variations.

Modeling Deformation Flow Curves and Dynamic Recrystallization of BA-160 Steel During Hot Compression

NASA Astrophysics Data System (ADS)

Shahriari, Babak; Vafaei, Reza; Mohammad Sharifi, Ehsan; Farmanesh, Khosro

2018-03-01

The hot deformation behavior of a high strength low carbon steel was investigated using hot compression test at the temperature range of 850-1100 °C and under strain rates varying from 0.001 to 1 s-1. It was found that the flow curves of the steel were typical of dynamic recrystallization at the temperature of 950 °C and above; at tested strain rates lower than 1 s-1. A very good correlation between the flow stress and Zener-Hollomon parameter was obtained using a hyperbolic sine function. The activation energy of deformation was found to be around 390 kJ mol-1. The kinetics of dynamic recrystallization of the steel was studied by comparing it with a hypothetical dynamic recovery curve, and the dynamically fraction recrystallized was modeled by the Kolmogorov-Johnson-Mehl-Avrami relation. The Avrami exponent was approximately constant around 1.8, which suggested that the type of nucleation was one of site saturation on grain boundaries and edges.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, Linyun; Mei, Zhi-Gang; Yacout, Abdellatif M.

We have developed a mesoscale phase-field model for studying the effect of recrystallization on the gas-bubble-driven swelling in irradiated U-Mo alloy fuel. The model can simulate the microstructural evolution of the intergranular gas bubbles on the grain boundaries as well as the recrystallization process. Our simulation results show that the intergranular gas-bubble-induced fuel swelling exhibits two stages: slow swelling kinetics before recrystallization and rapid swelling kinetics with recrystallization. We observe that the recrystallization can significantly expedite the formation and growth of gas bubbles at high fission densities. The reason is that the recrystallization process increases the nucleation probability of gasmore » bubbles and reduces the diffusion time of fission gases from grain interior to grain boundaries by increasing the grain boundary area and decreasing the diffusion distance. The simulated gas bubble shape, size distribution, and density on the grain boundaries are consistent with experimental measurements. We investigate the effect of the recrystallization on the gas-bubble-driven fuel swelling in UMo through varying the initial grain size and grain aspect ratio. We conclude that the initial microstructure of fuel, such as grain size and grain aspect ratio, can be used to effectively control the recrystallization and therefore reduce the swelling in U-Mo fuel.« less

Low-Temperature Friction-Stir Welding of 2024 Aluminum

NASA Technical Reports Server (NTRS)

Benavides, S.; Li, Y.; Murr, L. E.; Brown, D.; McClure, J. C.

1998-01-01

Solid state friction-stir welding (FSW) has been demonstrated to involve dynamic recrystallization producing ultra-fine, equiaxed grain structures to facilitate superplastic deformation as the welding or joining mechanism. However, the average residual, equiaxed, grain size in the weld zone has ranged from roughly 0.5 micron to slightly more than 10 micron, and the larger weld zone grain sizes have been characterized as residual or static grain growth as a consequence of the temperatures in the weld zone (where center-line temperatures in the FSW of 6061 Al have been shown to be as high as 480C or -0.8 T(sub M) where T(sub M) is the absolute melting temperature)). In addition, the average residual weld zone grain size has been observed to increase near the top of the weld, and to decrease with distance on either side of the weld-zone centerline, an d this corresponds roughly to temperature variations within the weld zone. The residual grain size also generally decreases with decreasing FSW tool rotation speed. These observations are consistent with the general rules for recrystallization where the recrystallized grain size decreases with increasing strain (or deformation) at constant strain rate, or with increasing strain-rate, or with increasing strain rate at constant strain; especially at lower ambient temperatures, (or annealing temperatures). Since the recrystallization temperature also decreases with increasing strain rate, the FSW process is somewhat complicated because the ambient temperature, the frictional heating fraction, and the adiabatic heating fraction )proportional to the product of strain and strain-rate) will all influence both the recrystallization and growth within the FSW zone. Significantly reducing the ambient temperature of the base metal or work pieces to be welded would be expected to reduce the residual weld-zone grain size. The practical consequences of this temperature reduction would be the achievement of low temperature welding. This study compares the residual grain sizes and microstructures in 2024 Al friction-stir welded at room temperature (about 30C and low temperature (-30C).

Microstructure evolution and dynamic recrystallization behavior of a powder metallurgy Ti-22Al-25Nb alloy during hot compression

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jia, Jianbo

The flow behavior of a powder metallurgy (P/M) Ti-22Al-25Nb alloy during hot compression tests has been investigated at a strain rate of 0.01 s{sup −1} and a temperature range of 980–1100 °C up to various true strains from 0.1 to 0.9. The effects of deformation temperature and strain on microstructure characterization and nucleation mechanisms of dynamic recrystallization (DRX) were assessed by means of Optical microscope (OM), electron backscatter diffraction (EBSD) and transmission electron microscope (TEM) techniques, respectively. The results indicated that the process of DRX was promoted by increasing deformation temperature and strain. By regression analysis, a power exponent relationshipmore » between peak stresses and sizes of stable DRX grains was developed. In addition, it is suggested that the discontinuous dynamic recrystallization (DDRX) and continuous dynamic recrystallization (CDRX) controlled nucleation mechanisms for DRX grains operated simultaneously during the whole hot process, and which played the leading role varied with hot process parameters of temperature and strain. It was further demonstrated that the CDRX featured by progressive subgrain rotation was weakened by elevating deformation temperatures. - Highlights: •Flow behavior of a P/M Ti-22Al-25Nb is studied by hot compression tests. •Microstructure evolution of alloy is affected by deformation temperature and strain. •The relationship between peak stress and stable DRX grain size was developed. •The process of DRX was promoted by increasing deformation temperature and strain. •Nucleation mechanisms of DRX were identified by EBSD analysis and TEM observation.« less

Negative Temperature Dependence of Recrystallized Grain Size: Formulation and Experimental Confirmation on Copper

PubMed Central

Elmasry, Mohamed; Liu, Fan; Jiang, Yao; Mao, Ze Ning; Liu, Ying; Wang, Jing Tao

2017-01-01

The catalyzing effect on nucleation of recrystallization from existing grains resulting from previous lower temperature deformation is analyzed, analogous to the size effect of foreign nucleus in heterogeneous nucleation. Analytical formulation of the effective nucleation site for recrystallization leads to a negative temperature dependence of recrystallized grain size of metals. Non-isochronal annealing—where annealing time is set just enough for the completion of recrystallization at different temperatures—is conducted on pure copper after severe plastic deformation. More homogeneous and smaller grains are obtained at higher annealing temperature. The good fit between analytical and experimental results unveils the intrinsic feature of this negative temperature dependence of recrystallized grain size. PMID:28772676

Grain Refinement Kinetics in a Low Alloyed Cu–Cr–Zr Alloy Subjected to Large Strain Deformation

PubMed Central

Morozova, Anna; Borodin, Elijah; Bratov, Vladimir; Zherebtsov, Sergey; Kaibyshev, Rustam

2017-01-01

This paper investigates the microstructural evolution and grain refinement kinetics of a solution-treated Cu–0.1Cr–0.06Zr alloy during equal channel angular pressing (ECAP) at a temperature of 673 K via route BC. The microstructural change during plastic deformation was accompanied by the formation of the microband and an increase in the misorientations of strain-induced subboundaries. We argue that continuous dynamic recrystallization refined the initially coarse grains, and discuss the dynamic recrystallization kinetics in terms of grain/subgrain boundary triple junction evolution. A modified Johnson–Mehl–Avrami–Kolmogorov relationship with a strain exponent of about 1.49 is used to express the strain dependence of the triple junctions of high-angle boundaries. Severe plastic deformation by ECAP led to substantial strengthening of the Cu–0.1Cr–0.06Zr alloy. The yield strength increased from 60 MPa in the initial state to 445 MPa after a total strain level of 12. PMID:29210990

The microstructure of polar ice. Part II: State of the art

NASA Astrophysics Data System (ADS)

Faria, Sérgio H.; Weikusat, Ilka; Azuma, Nobuhiko

2014-04-01

An important feature of natural ice, in addition to the obvious relevance of glaciers and ice sheets for climate-related issues, is its ability to creep on geological time scales and low deviatoric stresses at temperatures very close to its melting point, without losing its polycrystalline character. This fact, together with its strong mechanical anisotropy and other notable properties, makes natural ice an interesting model material for studying the high-temperature creep and recrystallization of rocks in Earth's interior. After having reviewed the major contributions of deep ice coring to the research on natural ice microstructures in Part I of this work (Faria et al., 2014), here in Part II we present an up-to-date view of the modern understanding of natural ice microstructures and the deformation processes that may produce them. In particular, we analyze a large body of evidence that reveals fundamental flaws in the widely accepted tripartite paradigm of polar ice microstructure (also known as the "three-stage model," cf. Part I). These results prove that grain growth in ice sheets is dynamic, in the sense that it occurs during deformation and is markedly affected by the stored strain energy, as well as by air inclusions and other impurities. The strong plastic anisotropy of the ice lattice gives rise to high internal stresses and concentrated strain heterogeneities in the polycrystal, which demand large amounts of strain accommodation. From the microstructural analyses of ice cores, we conclude that the formation of many and diverse subgrain boundaries and the splitting of grains by rotation recrystallization are the most fundamental mechanisms of dynamic recovery and strain accommodation in polar ice. Additionally, in fine-grained, high-impurity ice layers (e.g. cloudy bands), strain may sometimes be accommodated by diffusional flow (at low temperatures and stresses) or microscopic grain boundary sliding via microshear (in anisotropic ice sheared at high temperatures). Grain boundaries bulged by migration recrystallization and subgrain boundaries are endemic and very frequent at almost all depths in ice sheets. Evidence of nucleation of new grains is also observed at various depths, provided that the local concentration of strain energy is high enough (which is not seldom the case). As a substitute for the tripartite paradigm, we propose a novel dynamic recrystallization diagram in the three-dimensional state space of strain rate, temperature, and mean grain size, which summarizes the various competing recrystallization processes that contribute to the evolution of the polar ice microstructure.

An extension of the Saltykov method to quantify 3D grain size distributions in mylonites

NASA Astrophysics Data System (ADS)

Lopez-Sanchez, Marco A.; Llana-Fúnez, Sergio

2016-12-01

The estimation of 3D grain size distributions (GSDs) in mylonites is key to understanding the rheological properties of crystalline aggregates and to constraining dynamic recrystallization models. This paper investigates whether a common stereological method, the Saltykov method, is appropriate for the study of GSDs in mylonites. In addition, we present a new stereological method, named the two-step method, which estimates a lognormal probability density function describing the 3D GSD. Both methods are tested for reproducibility and accuracy using natural and synthetic data sets. The main conclusion is that both methods are accurate and simple enough to be systematically used in recrystallized aggregates with near-equant grains. The Saltykov method is particularly suitable for estimating the volume percentage of particular grain-size fractions with an absolute uncertainty of ±5 in the estimates. The two-step method is suitable for quantifying the shape of the actual 3D GSD in recrystallized rocks using a single value, the multiplicative standard deviation (MSD) parameter, and providing a precision in the estimate typically better than 5%. The novel method provides a MSD value in recrystallized quartz that differs from previous estimates based on apparent 2D GSDs, highlighting the inconvenience of using apparent GSDs for such tasks.

Nano-Sized Grain Refinement Using Friction Stir Processing

DTIC Science & Technology

2013-03-01

friction stir weld is a very fine grain microstructure produced as a result of dynamic recrystallization. The friction stir ... Friction Stir Processing, Magnesium, Nano-size grains Abstract A key characteristic of a friction stir weld is a very fine grain microstructure...state process developed on the basis of the friction stir welding (FSW) technique invented by The Welding Institute (TWI) in 1991 [2]. During

Cyclic Ductile-Brittle Deformation during Temperature Decrease in Quartz-Rich Mylonites: Insights from the Calamita Schists (Elba Island, Italy)

NASA Astrophysics Data System (ADS)

Papeschi, S.; Menegon, L. M.; Musumeci, G.

2017-12-01

The Calamita Schists are a metamorphic complex that experienced transient (< 1 Ma) upper Miocene HT/LP metamorphism related to the emplacement of the Porto Azzurro pluton at P<0.2 GPa. HT/LP metamorphism was coeval with regional scale contractional tectonics leading to the development of meter to decameter ductile east-verging high-strain domains marked by mylonitic fabric overprinted by non-Andersonian brittle faults. In order to investigate the switch in deformation mechanism during temperature decrease at constant pressure (P<0.2 GPa), a sample of mylonitic quartzite with S-C' fabric was examined by Electron Backscatter Diffraction (EBSD), optical microscopy and Scanning Electron Microscope (SEM). Mylonitic fabric is marked by synkinematic biotite + cordierite + andalusite + K-feldspar assemblage, which is progressively replaced by retrograde white mica + chlorite. Quartz microfabric is defined by coarse-grained (100-900 µm) quartz porphyroclasts wrapped by ribbons of dynamically recrystallized finer grains ( 50 µm) showing a strong CPO. This fabric is cross cut by conjugate and synthetic C'-shear bands localized in porphyroclasts and marked by recrystallized fine grains (5-50 µm). EBSD data indicate that prism was the dominant slip system during crystal plastic deformation and dynamic recrystallization in the polycrystalline ribbons. Subsequently, brittle deformation localized along intracrystalline bands (both in conjugate sets and parallel to C' shear bands) within quartz porphyroclasts. The bands evolved in localized cataclastic micro-shear zones and in shear fractures, which localized fluid infiltration and healing by solution precipitation. The quartz new grains filling the bands are preferentially oriented with their c-axis parallel to the shear band boundary. This work highlights that deformation in the Calamita Schists switched over time from high-temperature dynamic recrystallization, accommodated by prism slip to low grade brittle-ductile processes. At the brittle-ductile transition strain partitioning was controlled by grain size and fluid penetration and was characterized by cyclical ductile-brittle mechanisms. In particular brittle failure localized in coarse-grains acted as the precursor for ductile C' shear bands.

Strain induced grain boundary migration effects on grain growth of an austenitic stainless steel during static and metadynamic recrystallization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paggi, A., E-mail: alpaggi@tenaris.com; Angella, G.; Donnini, R.

Static and metadynamic recrystallization of an AISI 304L austenitic stainless steel was investigated at 1100 °C and 10{sup −} {sup 2} s{sup −} {sup 1} strain rate. The kinetics of recrystallization was determined through double hit compression tests. Two strain levels were selected for the first compression hit: ε{sub f} = 0.15 for static recrystallization (SRX) and 0.25 for metadynamic recrystallization (MDRX). Both the as-deformed and the recrystallized microstructures were investigated through optical microscopy and electron back-scattered diffraction (EBSD) technique. During deformation, strain induced grain boundary migration appeared to be significant, producing a square-like grain boundary structure aligned along themore » directions of the maximum shear stresses in compression. EBSD analysis revealed to be as a fundamental technique that the dislocation density was distributed heterogeneously in the deformed grains. Grain growth driven by surface energy reduction was also investigated, finding that it was too slow to explain the experimental data. Based on microstructural results, it was concluded that saturation of the nucleation sites occurred in the first stages of recrystallization, while grain growth driven by strain induced grain boundary migration (SIGBM) dominated the subsequent stages. - Highlights: • Recrystallization behavior of a stainless steel was investigated at 1100 °C. • EBSD revealed that the dislocation density distribution was heterogeneous during deformation. • Saturation of nucleation sites occurred in the first stages of recrystallization. • Strain induced grain boundary migration (SIGBM) effects were significant. • Grain growth driven by SIGBM dominated the subsequent stages.« less

Modelling and simulation of dynamic recrystallization (DRX) in OFHC copper at very high strain rates

NASA Astrophysics Data System (ADS)

Testa, G.; Bonora, N.; Ruggiero, A.; Iannitti, G.; Persechino, I.; Hörnqvist, M.; Mortazavi, N.

2017-01-01

At high strain rates, deformation processes are essentially adiabatic and if the plastic work is large enough dynamic recrystallization can occur. In this work, an examination on microstructure evolution of OFHC copper in Dynamic Tensile Extrusion (DTE) test, performed at 400 m/s, was carried out. EBSD investigations, along the center line of the fragment remaining in the extrusion die, showed a progressive elongation of the grains, and an accompanying development of a strong <001> + <111> dual fiber texture. Discontinuous dynamic recrystallization (DRX) occurred at larger strains, and it was showed that nucleation occurred during straining. A criterion for DRX to occur, based on the evolution of Zener-Hollomon parameter during the dynamic deformation process, is proposed. Finally, DTE test was simulated using the modified Rusinek-Klepaczko constitutive model incorporating a model for the prediction of DRX initiation.

The effect of deformation temperature on the microstructure evolution of Inconel 625 superalloy

NASA Astrophysics Data System (ADS)

Guo, Qingmiao; Li, Defu; Guo, Shengli; Peng, Haijian; Hu, Jie

2011-07-01

Hot compression tests of Inconel 625 superalloy were conducted using a Gleeble-1500 simulator between 900 °C and 1200 °C with different true strains and a strain rate of 0.1 s -1. Scanning electron microscope (SEM) and electron backscatter diffraction technique (EBSD) were employed to investigate the effect of deformation temperature on the microstructure evolution and nucleation mechanisms of dynamic recrystallization (DRX). It is found that the relationship between the DRX grain size and the peak stress can be expressed by a power law function. Significant influence of deformation temperatures on the nucleation mechanisms of DRX are observed at different deformation stages. At lower deformation temperatures, continuous dynamic recrystallization (CDRX) characterized by progressive subgrain rotation is considered as the main mechanism of DRX at the early deformation stage. However, discontinuous dynamic recrystallization (DDRX) with bulging of the original grain boundaries becomes the operating mechanism of DRX at the later deformation stage. At higher deformation temperatures, DDRX is the primary mechanism of DRX, while CDRX can only be considered as an assistant mechanism at the early deformation stage. Nucleation of DRX can also be activated by the twinning formation. With increasing the deformation temperature, the effect of DDRX accompanied with twinning formation grows stronger, while the effect of CDRX grows weaker. Meanwhile, the position of subgrain formation shifts gradually from the interior of original grains to the vicinity of the original boundaries.

Stress Dependence of Microstructures in Experimentally Deformed Calcite

NASA Astrophysics Data System (ADS)

Platt, J. P.; De Bresser, J. H. P.

2017-12-01

Measurements of dynamically recrystallized grain size (Dr), subgrain size (Sg), minimum bulge size (Blg), and the maximum scale length for surface-energy driven grain-boundary migration (γGBM) in experimentally deformed Cararra marble help define the dependence of these microstructural features on stress and temperature. Measurements were made optically on ultra-thin sections in order to allow these features to be defined during measurement on the basis of microstructural setting and geometry. Taken together with previously published data Dr defines a paleopiezometer with a stress exponent of -1.09. There is no discernible temperature dependence over the 500°C temperature range of the experiments. Recrystallization occured mainly by bulging and subgrain rotation, and the two processes operated together, so that it is not possible to separate grains nucleated by the two mechanisms. Sg and Dr measured in the same samples are closely similar in size, suggesting that new grains do not grow significantly after nucleation, and that subgrain size is likely to be the primary control on recrystallized grain size. Blg and γGBM measured on each sample define a relationship to stress with an exponent of approximately -1.6, which helps define the boundary in stress - grain-size space between a region of dominant strain-energy-driven grain-boundary migration at high stress, from a region of dominant surface-energy-driven grain-boundary migration at low stress.

On the use of copper-based substrates for YBCO coated conductors

NASA Astrophysics Data System (ADS)

Vannozzi, A.; Fabbri, F.; Augieri, A.; Angrisani Armenio, A.; Galluzzi, V.; Mancini, A.; Rizzo, F.; Rufoloni, A.; Padilla, J. A.; Xuriguera, E.; De Felicis, D.; Bemporad, E.; Celentano, G.

2014-05-01

It is well known that the recrystallization texture of heavily cold-rolled pure copper is almost completely cubic. However, one of the main drawbacks concerning the use of pure copper cube-textured substrates for YBCO coated conductor is the reduced secondary recrystallization temperature. The onset of secondary recrystallization (i.e., the occurrence of abnormal grains with unpredictable orientation) in pure copper substrate was observed within the typical temperature range required for buffer layer and YBCO processing (600-850 °C). To avoid the formation of abnormal grains the effect of both grain size adjustment (GSA) and recrystallization annealing was analyzed. The combined use of a small initial grain size and a recrystallization two-step annealing (TSA) drastically reduced the presence of abnormal grains in pure copper tapes. Another way to overcome the limitation imposed by the formation of abnormal grains is to deposit a buffer layer at temperatures where secondary recrystallization does not occur. For example, La2Zr2O7 (LZO) film with a high degree of epitaxy was grown by metal-organic decomposition (MOD) at 1000 °C on pure copper substrate. In several samples the substrate underwent secondary recrystallization. Our experiments indicate that the motion of grain boundaries occurring during secondary recrystallization process does not affect the quality of LZO film.

Recrystallization and grain growth phenomena in a particle-reinforced aluminum composite

NASA Astrophysics Data System (ADS)

van Aken, D. C.; Krajewski, P. E.; Vyletel, G. M.; Allison, J. E.; Jones, J. W.

1995-06-01

Recrystallization and grain growth in a 2219/TiC/15p composite were investigated as functions of the amount of deformation and deformation temperature. Both cold and hot deformed samples were annealed at the normal solution treatment temperature of 535 °C. It was shown that large recrystallized grain diameters, relative to the interparticle spacing, could be produced in a narrow range of deformation for samples cold-worked and those hot-worked below 450 °C. For cold-worked samples, between 4 to 6 pct deformation, the recrystallized grain diameters varied from 530 to 66 μm as the amount of deformation increased. Subsequent grain growth was not observed in these recrystallized materials and noncompact grain shapes were observed. For deformations greater than 15 pct, recrystallized grain diameters less than the interparticle spacing were observed and subsequent grain growth produced a pinned grain diameter of 27 μm. The pinned grain diameter agreed well with an empirical model based on three dimensional (3-D) Monte Carlo simulations of grain growth and particle pinning in a two-phase material. Tensile properties were determined as a function of grain size, and it was shown that grain size had a weak influence on yield strength. A maximum in the yield strength was observed at a grain size larger than the normal grain growth and particle-pinned diameter.

Evaluating flow laws for dynamically recrystallized quartz based on field data

NASA Astrophysics Data System (ADS)

Peters, Max; Herwegh, Marco

2013-04-01

The extrapolation of experimentally controlled deformation conditions, and the resulting relations between physical parameters acting during ductile deformation, to nature is considered controversial (see Herwegh et al., 2005 and references therein). Whereas the relationship between flow stress and recrystallized grain size can be empirically derived from lab experiments using paleopiezometers (e.g. Stipp & Tullis, 2003), the relation between recrystallized grain size, strain rate, differential stress, temperature and activation energy for dislocation creep requires further constraints. For these relations, various power law flow laws for dynamically recrystallized quartz were proposed over the past years (Paterson & Luan, 1990; Luan & Paterson, 1992; Gleason & Tullis, 1995; Hirth et al., 2001, Rutter & Brodie, 2004). The variations in the flow laws are mainly characterized by different starting materials, experimental conditions, the activation energy for dislocation creep and the stress exponent n. In this study we compare and evaluate experimentally derived flow laws regarding their reliability for the prediction of rheology of background deformation of naturally deformed crystalline samples from mylonites of the Aar massif (Swiss Central Alps). The majority of samples comprises highly deformed rocks (e.g. Central Aare granite), which exhibit severe grain size reduction. This reduction dominantly occurred by subgrain rotation (SGR), in the case of low temperature overprint by bulging recrystallization (BLG). Towards elevated temperatures, grain boundary migration (GBM) and SGR recrystallization were active. Along the metamorphic gradient (300 - 475°C) quartz microstructures and associated recrystallized grain size distributions indicate steady state mean grain sizes. The quantification of the metamorphic gradient (temperature, pressure, water fugacity) over the sampling area allowed the application of flow laws, yielding variations of 6 orders of magnitude in deformation rates between different calibrations for one corresponding grain size. The calibrations of Paterson & Luan (1990) and Hirth et al. (2001) yield most reliable results for peak metamorphic conditions, which are in line with the geological framework. Strain rates range between 10E-13 and 10E-10 s-1 (Paterson & Luan, 1990) with corresponding flow stresses between ca. 200 MPa (BLG) to ca. 20 MPa (SGR and transition SGR-GBM). Nevertheless, the applicability of single flow laws shall be discussed in greater detail. REFERENCES Herwegh, M., de Bresser, J.H.P. and ter Heege, J.H. 2005: Combining natural microstructures with composite flow laws: an improved approach for the extrapolation of lab data to nature. Journal of Structural Geology, 27. Hirth, G., Teyssier, C. and Dunlap, W.J. 2011: An evaluation of quartzite flow laws based on comparisons between experimentally and naturally deformed rocks. International Journal of Earth Sciences, 90. Luan, F.C. and Paterson, S.R. 1992: Perparation and deformation of synthetic aggregates of quartz. Journal of Geophysical Research, 97. Paterson, S.R. and Luan, F.C. 1990: Quartzite rheology under geological conditions. In: de Meer, S., Drury, M.R., de Bresser, J.H.P., Pennock, G.M Deformation mechanisms, rheology and tectonics: from minerals to the lithosphere. Geological Society of Lonodn Special Publications, 54. Rutter, E.H. and Brodie, K.H. 2004: Experimental grain size-sensitive flow of hot-pressed Brazilian quartz aggregates. Journal of Structural Geology, 26. Stipp, M. and Tullis, J. 2003: The recrystallized grain size piezometer for quartz. Geophysical Research Letters, 30.

The Recrystallization Behavior of Unalloyed Mg and a Mg-Al Alloy

NASA Astrophysics Data System (ADS)

Murphy, Aeriel D.; Allison, John E.

2018-02-01

The static recrystallization behavior of pure Mg and Mg-4Al was characterized over a range of annealing temperatures. The electron backscatter diffraction grain orientation spread technique was used to quantify the level of recrystallization at various annealing times. Recrystallization kinetics were characterized using the Johnson-Mehl-Avrami-Kolmogorov (JMAK) relationship and it was found that two sequential annealing stages exist. Stage 1 involves heterogeneous nucleation of recrystallization in regions with a high stored energy, including twins and grain boundaries, and can be represented by an Avrami exponent of n 1 ranging from 0.35 to 0.6. During Stage 2, recrystallization occurred predominately in the interior of deformed grains with incomplete recrystallization generally observed even at annealing times in excess of two weeks. The second recrystallization stage exhibited a much lower Avrami exponent, n 2, ranging from 0.02 to 0.2. Increasing the starting grain size in the pure Mg condition led to a significant delay in recrystallization. The addition of Al had a minimal effect on the recrystallization kinetics of Mg.

A Continuum Model for the Effect of Dynamic Recrystallization on the Stress⁻Strain Response.

PubMed

Kooiker, H; Perdahcıoğlu, E S; van den Boogaard, A H

2018-05-22

Austenitic Stainless Steels and High-Strength Low-Alloy (HSLA) steels show significant dynamic recovery and dynamic recrystallization (DRX) during hot forming. In order to design optimal and safe hot-formed products, a good understanding and constitutive description of the material behavior is vital. A new continuum model is presented and validated on a wide range of deformation conditions including high strain rate deformation. The model is presented in rate form to allow for the prediction of material behavior in transient process conditions. The proposed model is capable of accurately describing the stress⁻strain behavior of AISI 316LN in hot forming conditions, also the high strain rate DRX-induced softening observed during hot torsion of HSLA is accurately predicted. It is shown that the increase in recrystallization rate at high strain rates observed in experiments can be captured by including the elastic energy due to the dynamic stress in the driving pressure for recrystallization. Furthermore, the predicted resulting grain sizes follow the power-law dependence with steady state stress that is often reported in literature and the evolution during hot deformation shows the expected trend.

Comparison Between Different Processing Schedules for the Development of Ultrafine-Grained Dual-Phase Steel

NASA Astrophysics Data System (ADS)

Karmakar, Anish; Sivaprasad, S.; Nath, S. K.; Misra, R. D. K.; Chakrabarti, Debalay

2014-05-01

A comparative study was carried out on the development of ultrafine-grained dual-phase (DP) (ferrite-martensite) structures in a low-carbon microalloyed steel processed using two thermomechanical processing routes, (i) intercritical deformation and (ii) warm-deformation and intercritical annealing. The samples were deformed using Gleeble3500® simulator, maintaining a constant total strain ( ɛ = 1) and strain rate ( = 1/s). Evolution of microstructure and micro-texture was investigated by SEM, TEM, and EBSD. Ultrafine-grained DP structures could be formed by careful selection of deformation temperature, T def (for intercritical deformation) or annealing temperature, T anneal (for warm-deformation and annealing). Overall, the ferrite grain sizes ranged from 1.5 to 4.0 μm, and the sizes and fractions of the uniformly distributed fine-martensitic islands ranged from 1.5 to 3.0 μm and 15 to 45 pct, respectively. Dynamic strain-induced austenite-to-ferrite transformation followed by continuous (dynamic) recrystallization of the ferrite dictated the grain refinement during intercritical deformation, while, continuous (static) recrystallization by pronounced recovery dictated the grain refinement during the warm-deformation and the annealing. Regarding intercritical deformation, the samples cooled to T def indicated finer grain size compared with the samples heated to T def, which are explained in terms of the effects of strain partitioning on the ferrite and the heating during deformation. Alpha-fiber components dominated the texture in all the samples, and the fraction of high-angle boundaries (with >15 deg misorientation) increased with the increasing T def or T anneal, depending on the processing schedule. Fine carbide particles, microalloyed precipitates and austenitic islands played important roles in defining the mechanism of grain refinement that involved retarding conventional ferrite recrystallization and ferrite grain growth. With regard to the intercritical deformation, warm-deformation followed by annealing is a simpler process to control in the rolling mill; however, the need for high-power rolling mill and controlled annealing facility imposes industrial challenges.

Microstructural and fabric characterization of brittle-ductile transitional deformation of middle crustal rocks along the Jinzhou detachment fault zone, Northeast China

NASA Astrophysics Data System (ADS)

Zhang, Juyi; Jiang, Hao; Liu, Junlai

2017-04-01

Detachment fault zones (DFZs) of metamorphic core complexes generally root into the middle crust. Exhumed DFZs therefore generally demonstrate structural, microstructural and fabric features characteristic of middle to upper crustal deformation. The Jinzhou detachment fault zone from the Liaonan metamorphic core complex is characterized by the occurrence of a sequence of fault rocks due to progressive shearing along the fault zone during exhumation of the lower plate. From the exhumed fabric zonation, cataclastic rocks formed in the upper crust occur near the Jinzhou master detachment fault, and toward the lower plate gradually changed to mylonites, mylonitic gneisses and migmatitic gneisses. Correspondingly, these fault rocks have various structural, microstructural and fabric characteristics that were formed by different deformation and recrystallization mechanisms from middle to upper crustal levels. At the meanwhile, various structural styles for strain localization were formed in the DFZ. As strain localization occurs, rapid changes in deformation mechanisms are attributed to increases in strain rates or involvement of fluid phases during the brittle-ductile shearing. Optical microscopic studies reveal that deformed quartz aggregates in the lower part of the detachment fault zone are characterized by generation of dynamically recrystallized grains via SGR and BLG recrystallization. Quartz rocks from the upper part of the DFZ have quartz porphyroclasts in a matrix of very fine recrystallized grains. The porphyroclasts have mantles of sub-grains and margins grain boundary bulges. Electron backscattered diffraction technique (EBSD) quartz c-axis fabric analysis suggests that quartz grain aggregates from different parts of the DFZ possess distinct fabric complexities. The c-axis fabrics of deformed quartz aggregates from mylonitic rocks in the lower part of the detachment fault zone preserve Y-maxima which are ascribed to intermediate temperature deformation (500-630˚ C), whereas complicated fabric patterns (e.g. asymmetric single girdles) are formed in fault rocks from the upper part of the DFZ. The increasing fabric complexity is here interpreted as the result of progressive superposition of fault rocks by shearing either at relatively shallow levels or high rate of strain, during exhumation of the lower plate and shear zone rocks. The above observations and interpretations imply that dislocation creep processes contribute to the dynamic recrystallization of quartz in the middle crustal brittle-ductile transition. Progressive shearing as a consequence of exhumation of the lower plate of the MCC contributed to the obvious structural, microstructural and fabric superpositions. Strain localization occurs as the progressive shearing proceeded. Transition of mechanisms of deformation and dynamic recrystallization during strain localization may be resulted from changes in temperature conditions, in strain rates or addition of minor amount water.

Unraveling Recrystallization Mechanisms Governing Texture Development from Rare Earth Element Additions to Magnesium

NASA Astrophysics Data System (ADS)

Imandoust, Aidin

The origin of texture components associated with rare-earth (RE) element additions in wrought magnesium (Mg) alloys is a long-standing problem in magnesium technology. The objective of this research is to identify the mechanisms accountable for rare-earth texture during dynamic recrystallization (DRX). Towards this end, we designed binary Mg-Cerium and Mg-Gadolinium alloys along with complex alloy compositions containing zinc, yttrium and Mischmetal. Binary alloys along with pure Mg were designed to individually investigate their effects on texture evolutions, while complex compositions are designed to develop randomized texture, and be used in automotive and aerospace applications. We selected indirect extrusion to thermo-mechanically process our materials. Different extrusion ratios and speeds were designed to produce partially and fully recrystallized microstructures, allowing us to analyze DRX from its early stages to completion. X-ray diffraction, electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM) were used to conduct microstructure and texture analyses. Our analyses revealed that rare-earth elements in zinc-containing magnesium alloys promote discontinuous dynamic recrystallization at the grain boundaries. During nucleation, the effect of rare earth elements on orientation selection was explained by the concomitant actions of multiple Taylor axes in the same grain. Isotropic grain growth was observed due to rare earth elements segregating to grain boundaries, which lead to texture randomization. The nucleation in binary Mg-RE alloys took place by continuous formation of necklace structures. Stochastic relaxation of basal and non-basal dislocations into low-angle grain boundaries produced chains of embryos with nearly random orientations. Schmid factor analysis showed a lower net activation of dislocations in RE textured grains compared to ones on the other side of the stereographic triangle. Lower dislocation densities within RE grains favored their growth by setting the boundary migration direction toward grains with higher dislocation density, thereby decreasing the system energy. We investigated the influence of RE elements on extension twinning induced hardening. RE addition enhanced tensile twinning induced hardening significantly. EBSD analysis illustrated that tensile twins cross low angle grain boundaries in Mg-RE alloys, which produced large twins and facilitated transmutation of basal to prismatic dislocations. Higher activity of pyramidal II dislocations in Mg-RE alloys resulted in higher twinning induced hardening.

Effect of Aluminum on the Microstructure and Properties of Two Refractory High-Entropy Alloys (Postprint)

DTIC Science & Technology

2014-04-01

The chemical compositions of the recrystallized ic release; distribution unlimited. Fig. 5. (a) Equiaxed grain structure of the annealed...deformation bands crossing a grain boundary; (c) fine recrystallized grains formed at grain boundaries; (d) a higher magnification image shows the...presence of nano-precipitates at the boundaries of the recrystallized grains. 220 O.N. Senkov et al. / Acta Materialia 68 (2014) 214–228and non

Evolution of grain boundary character distributions in alloy 825 tubes during high temperature annealing: Is grain boundary engineering achieved through recrystallization or grain growth?

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bai, Qin; Zhao, Qing

Grain boundary engineering (GBE) of nickel-based alloy 825 tubes was carried out with different cold drawing deformations by using a draw-bench on a factory production line and subsequent annealing at various temperatures. The microstructure evolution of alloy 825 during thermal-mechanical processing (TMP) was characterized by means of the electron backscatter diffraction (EBSD) technique to study the TMP effects on the grain boundary network and the evolution of grain boundary character distributions during high temperature annealing. The results showed that the proportion of ∑ 3{sup n} coincidence site lattice (CSL) boundaries of alloy 825 tubes could be increased to > 75%more » by the TMP of 5% cold drawing and subsequent annealing at 1050 °C for 10 min. The microstructures of the partially recrystallized samples and the fully recrystallized samples suggested that the proportion of low ∑ CSL grain boundaries depended on the annealing time. The frequency of low ∑ CSL grain boundaries increases rapidly with increasing annealing time associating with the formation of large-size highly-twinned grains-cluster microstructure during recrystallization. However, upon further increasing annealing time, the frequency of low ∑ CSL grain boundaries decreased markedly during grain growth. So it is concluded that grain boundary engineering is achieved through recrystallization rather than grain growth. - Highlights: •The grain boundary engineering (GBE) is applicable to 825 tubes. •GBE is achieved through recrystallization rather than grain growth. •The low ∑ CSL grain boundaries in 825 tubes can be increased to > 75%.« less

Dynamic recrystallization and texture evolution of Mg–Y–Zn alloy during hot extrusion process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tong, L.B.; Li, X.; Guangzhou Research Institute of Non-ferrous Metals, Guangzhou 510651

2014-06-01

The microstructure and texture evolution of Mg{sub 98.5}Y{sub 1}Zn{sub 0.5} and Mg{sub 92.5}Y{sub 5}Zn{sub 2.5} (atomic percent) alloys during hot extrusion were systematically investigated. The coarse LPSO phases with higher volume fraction (∼ 57%) suppressed the twinning generation in the initial stage of extrusion, and accelerated the dynamic recrystallization through the particle deformation zones. Therefore, the volume fraction of DRXed grains in as-extruded Mg{sub 92.5}Y{sub 5}Zn{sub 2.5} alloy was much higher than that of Mg{sub 98.5}Y{sub 1}Zn{sub 0.5} alloy. The intensive recrystallization process resulted in the conventional basal texture weakening, although the texture evolution was mainly dominated by flow behavior.more » The dynamic recrystallization behavior in Mg{sub 92.5}Y{sub 5}Zn{sub 2.5} alloy restricted the formation of deformation texture, and thus the more random texture was observed during the whole extrusion process. - Highlights: • The densely coarse LPSO phases suppressed the twinning deformation. • Coarse LPSO phases induced the particle stimulated nucleation effect. • Dynamic recrystallization resulted in the basal texture weakening effect.« less

Titanium concentration in quartz as a record of multiple deformation mechanisms in an extensional shear zone

NASA Astrophysics Data System (ADS)

Nachlas, William O.; Whitney, Donna L.; Teyssier, Christian; Bagley, Brian; Mulch, Andreas

2014-04-01

Results of high precision analysis of Ti concentration ([Ti]) in quartz representing different recrystallization microstructures in a suite of progressively deformed quartzite mylonites show the effect of recrystallization on distribution of Ti in quartz. Petrographic observations and ion microprobe analysis reveals three texturally and geochemically distinct quartz microstructures in mylonites: (1) cores of recrystallized quartz ribbons preserve the highest [Ti] and are interpreted to have recrystallized via grain boundary migration recrystallization, (2) recrystallized rims and grain margins preserve a lower and more variable [Ti] and are interpreted to reflect the combined influence of subgrain rotation and bulging recrystallization, and (3) neocrystallized quartz precipitated in dilatancy sites has low (˜1 ppm) [Ti], reflecting the Ti content of the syndeformational fluid. Muscovite in nonmylonitic quartzite (at the base of the sampling traverse) is compositionally zoned, whereas muscovite in mylonitic quartzite shows a progressive decreasing in zoning in higher strain samples. Three-dimensional phase distribution mapping using X-ray computed tomography analysis of rock hand samples reveals that Ti-bearing accessory phases are less abundant and more dispersed in higher strained mylonites compared to nonmylonitic quartzite. This study demonstrates the influence of dynamic recrystallization on Ti substitution in quartz and evaluates the Ti buffering capacity of aqueous fluids (meteoric versus metamorphic/magmatic) as well as the distribution and reactivity of Ti-bearing accessory phases in a deforming quartzite. Results of this study suggest that Ti-in-quartz thermobarometry of deformed quartz is a sensitive technique for resolving the multistage history of quartz deformation and recrystallization in crustal shear zones.

Comparisons of Different Models on Dynamic Recrystallization of Plate during Asymmetrical Shear Rolling

PubMed Central

Zhang, Tao; Li, Lei; Lu, Shi-Hong; Gong, Hai; Wu, Yun-Xin

2018-01-01

Asymmetrical shear rolling with velocity asymmetry and geometry asymmetry is beneficial to enlarge deformation and refine grain size at the center of the thick plate compared to conventional symmetrical rolling. Dynamic recrystallization (DRX) plays a vital role in grain refinement during hot deformation. Finite element models (FEM) coupled with microstructure evolution models and cellular automata models (CA) are established to study the microstructure evolution of plate during asymmetrical shear rolling. The results show that a larger DRX fraction and a smaller average grain size can be obtained at the lower layer of the plate. The DRX fraction at the lower part increases with the ascending speed ratio, while that at upper part decreases. With the increase of the offset distance, the DRX fraction slightly decreases for the whole thickness of the plate. The differences in the DRX fraction and average grain size between the upper and lower surfaces increase with the ascending speed ratio; however, it varies little with the change of the speed ratio. Experiments are conducted and the CA models have a higher accuracy than FEM models as the grain morphology, DRX nuclei, and grain growth are taken into consideration in CA models, which are more similar to the actual DRX process during hot deformation. PMID:29342080

Comparisons of Different Models on Dynamic Recrystallization of Plate during Asymmetrical Shear Rolling.

PubMed

Zhang, Tao; Li, Lei; Lu, Shi-Hong; Gong, Hai; Wu, Yun-Xin

2018-01-17

Asymmetrical shear rolling with velocity asymmetry and geometry asymmetry is beneficial to enlarge deformation and refine grain size at the center of the thick plate compared to conventional symmetrical rolling. Dynamic recrystallization (DRX) plays a vital role in grain refinement during hot deformation. Finite element models (FEM) coupled with microstructure evolution models and cellular automata models (CA) are established to study the microstructure evolution of plate during asymmetrical shear rolling. The results show that a larger DRX fraction and a smaller average grain size can be obtained at the lower layer of the plate. The DRX fraction at the lower part increases with the ascending speed ratio, while that at upper part decreases. With the increase of the offset distance, the DRX fraction slightly decreases for the whole thickness of the plate. The differences in the DRX fraction and average grain size between the upper and lower surfaces increase with the ascending speed ratio; however, it varies little with the change of the speed ratio. Experiments are conducted and the CA models have a higher accuracy than FEM models as the grain morphology, DRX nuclei, and grain growth are taken into consideration in CA models, which are more similar to the actual DRX process during hot deformation.

Deformation induced dynamic recrystallization and precipitation strengthening in an Mg−Zn−Mn alloy processed by high strain rate rolling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiang, Jimiao; Song, Min

2016-11-15

The microstructure of a high strain-rate rolled Mg−Zn−Mn alloy was investigated by transmission electron microscopy to understand the relationship between the microstructure and mechanical properties. The results indicate that: (1) a bimodal microstructure consisting of the fine dynamic recrystallized grains and the largely deformed grains was formed; (2) a large number of dynamic precipitates including plate-like MgZn{sub 2} phase, spherical MgZn{sub 2} phase and spherical Mn particles distribute uniformly in the grains; (3) the major facets of many plate-like MgZn{sub 2} precipitates deviated several to tens of degrees (3°–30°) from the matrix basal plane. It has been shown that themore » high strength of the alloy is attributed to the formation of the bimodal microstructure, dynamic precipitation, and the interaction between the dislocations and the dynamic precipitates. - Highlights: •A bimodal microstructure was formed in a high strain-rate rolled Mg−Zn−Mn alloy. •Plate-like MgZn{sub 2}, spherical MgZn{sub 2} and spherical Mn phases were observed. •The major facet of the plate-like MgZn{sub 2} deviated from the matrix basal plane.« less

Friction Stir Back Extrusion of Aluminium Alloys for Automotive Applications

NASA Astrophysics Data System (ADS)

Xu, Zeren

Since the invention of Friction Stir Welding in 1991 as a solid state joining technique, extensive scientific investigations have been carried out to understand fundamental aspects of material behaviors when processed by this technique, in order to optimize processing conditions as well as mechanical properties of the welds. Based on the basic principles of Friction Stir Welding, several derivatives have also been developed such as Friction Stir Processing, Friction Extrusion and Friction Stir Back Extrusion. Friction Stir Back Extrusion is a novel technique that is proposed recently and designed for fabricating tubes from lightweight alloys. Some preliminary results have been reported regarding microstructure and mechanical properties of Friction Stir Back Extrusion processed AZ31 magnesium alloy, however, systematic study and in-depth investigations are still needed to understand the materials behaviors and underlying mechanisms when subjected to Friction Stir Back Extrusion, especially for age-hardenable Al alloys. In the present study, Friction Stir Back Extrusion processed AA6063-T5 and AA7075-T6 alloys are analyzed with respect to grain structure evolution, micro-texture change, recrystallization mechanisms, precipitation sequence as well as mechanical properties. Optical Microscopy, Electron Backscatter Diffraction, Transmission Electron Microscopy, Vickers Hardness measurements and uniaxial tensile tests are carried out to characterize the microstructural change as well as micro and macro mechanical properties of the processed tubes. Special attention is paid to the micro-texture evolution across the entire tube and dynamic recrystallization mechanisms that are responsible for grain refinement. Significant grain refinement has been observed near the processing zone while the tube wall is characterized by inhomogeneous grain structure across the thickness for both alloys. Dissolution of existing precipitates is noticed under the thermal hysterias imposed by Friction Stir Back Extrusion process, resulting in decreased strength but improved elongation of the processed tubes; a post-process aging step can effectively restore the mechanical properties of the processed tubes by allowing for the reprecipitation of solute elements in the form of fine, dispersed precipitates. Texture analysis performed for AA6063 alloy suggests the dominance of simple shear type textures with clear transition from initial texture to stable B/ ?B components via intermediate types that are stable under moderate strain levels. In order to identify the texture components properly, rigid body rotations are applied to the existing coordinate system to align it to local shear reference frame. Surprisingly, for AA7075 tubes, and fibers are observed to be the dominant texture components in the transition region as well as thermomechanically affected zone while the processing zone is characterized by random texture. The underlying mechanisms responsible for the formation of random texture are discussed in Chapter 5 based on Electron Backscatter Diffraction analysis. Comparative discussions are also carried out for the recrystallization mechanisms that are responsible for grain structure evolution of both alloys. Continuous grain subdivision and reorientation is cited as the dominant mechanism for the recrystallization of AA6063 alloys, while dynamic recrystallization occurs mainly in the form of Geometric Dynamic Recrystallization and progressive subgrain rotations near grain boundaries in AA7075 alloys.

Recrystallization and grain growth behavior of rolled tungsten under VDE-like short pulse high heat flux loads

NASA Astrophysics Data System (ADS)

Yuan, Y.; Greuner, H.; Böswirth, B.; Krieger, K.; Luo, G.-N.; Xu, H. Y.; Fu, B. Q.; Li, M.; Liu, W.

2013-02-01

Short pulse heat loads expected for vertical displacement events (VDEs) in ITER were applied in the high heat flux (HHF) test facility GLADIS at IPP-Garching onto samples of rolled W. Pulsed neutral beams with the central heat flux of 23 MW/m2 were applied for 0.5, 1.0 and 1.5 s, respectively. Rapid recrystallization of the adiabatically loaded 3 mm thick samples was observed when the pulse duration was up to 1.0 s. Grains grew markedly following recrystallization with increasing pulse length. The recrystallization temperature and temperature dependence of the recrystallized grain size were also investigated. The results showed that the recrystallization temperature of the W grade was around 2480 °C under the applied heat loading condition, which was nearly 1150 °C higher than the conventional recrystallization temperature, and the grains were much finer. A linear relationship between the logarithm of average grain size (ln d) and the inverse of maximum surface temperature (1/Tmax) was found and accordingly the activation energy for grain growth in temperature evolution up to Tmax in 1.5 s of the short pulse HHF load was deduced to be 4.1 eV. This provided an effective clue to predict the structure evolution under short pulse HHF loads.

Recrystallization characteristics of oxide dispersion strengthened nickel-base alloys

NASA Technical Reports Server (NTRS)

Hotzler, R. K.; Glasgow, T. K.

1980-01-01

Electron microscopy was employed to study the process of recrystallization in two oxide dispersion strengthened (ODS) mechanically alloyed nickel-base alloys, MA 754 and MA 6000E. MA 754 contained both fine, uniformly dispersed particles and coarser oxides aligned along the working direction. Hot rolled MA 754 had a grain size of 0.5 microns and high dislocation densities. After partial primary recrystallization, the fine grains transformed to large elongated grains via secondary (or abnormal) grain growth. Extruded and rolled MA 6000E contained equiaxed grains of 0.2 micron diameter. Primary recrystallization occurring during working eliminated virtually all dislocations. Conversion from fine to coarse grains was triggered by gamma prime dissolution; this was also a process of secondary or abnormal grain growth. Comparisons were made to conventional and oxide dispersion strengthened nickel-base alloys.

Hot Deformation Behavior and Dynamic Recrystallization of Medium Carbon LZ50 Steel

NASA Astrophysics Data System (ADS)

Du, Shiwen; Chen, Shuangmei; Song, Jianjun; Li, Yongtang

2017-03-01

Hot deformation and dynamic recrystallization behaviors of a medium carbon steel LZ50 were systematically investigated in the temperature range from 1143 K to 1443 K (870 °C to 1170 °C) at strain rates from 0.05 to 3s-1 using a Gleeble-3500 thermo-simulation machine. The flow stress constitutive equation for hot deformation of this steel was developed with the two-stage Laasraoui equation. The activation energy of the tested steel was 304.27 KJ/mol, which was in reasonable agreement with those reported previously. The flow stress of this steel in hot deformation was mainly controlled by dislocation climb during their intragranular motion. The effect of Zener-Hollomon parameter on the characteristic points of the flow curves was studied, and the dependence of critical strain on peak strain obeyed a linear equation. Dynamic recrystallization was the most important softening mechanism for the tested steel during hot deformation. Kinetic equation of this steel was also established based on the flow stress. The austenite grain size of complete dynamic recrystallization was a power law function of Zener-Hollomon parameter with an exponent of -0.2956. Moreover, the microstructures induced under different deformation conditions were analyzed.

A Continuum Model for the Effect of Dynamic Recrystallization on the Stress–Strain Response

PubMed Central

Perdahcıoğlu, E. S.; van den Boogaard, A. H.

2018-01-01

Austenitic Stainless Steels and High-Strength Low-Alloy (HSLA) steels show significant dynamic recovery and dynamic recrystallization (DRX) during hot forming. In order to design optimal and safe hot-formed products, a good understanding and constitutive description of the material behavior is vital. A new continuum model is presented and validated on a wide range of deformation conditions including high strain rate deformation. The model is presented in rate form to allow for the prediction of material behavior in transient process conditions. The proposed model is capable of accurately describing the stress–strain behavior of AISI 316LN in hot forming conditions, also the high strain rate DRX-induced softening observed during hot torsion of HSLA is accurately predicted. It is shown that the increase in recrystallization rate at high strain rates observed in experiments can be captured by including the elastic energy due to the dynamic stress in the driving pressure for recrystallization. Furthermore, the predicted resulting grain sizes follow the power-law dependence with steady state stress that is often reported in literature and the evolution during hot deformation shows the expected trend. PMID:29789492

Reconstruction of 3d grain boundaries from rock thin sections, using polarised light

NASA Astrophysics Data System (ADS)

Markus Hammes, Daniel; Peternell, Mark

2016-04-01

Grain boundaries affect the physical and chemical properties of polycrystalline materials significantly by initiating reactions and collecting impurities (Birchenall, 1959), and play an essential role in recrystallization (Doherty et al. 1997). In particular, the shape and crystallographic orientation of grain boundaries reveal the deformation and annealing history of rocks (Kruhl and Peternell 2002, Kuntcheva et al. 2006). However, there is a lack of non-destructive and easy-to-use computer supported methods to determine grain boundary geometries in 3D. The only available instrument using optical light to measure grain boundary angles is still the polarising microscope with attached universal stage; operated manually and time-consuming in use. Here we present a new approach to determine 3d grain boundary orientations from 2D rock thin sections. The data is recorded by using an automatic fabric analyser microscope (Peternell et al., 2010). Due to its unique arrangement of 9 light directions the highest birefringence colour due to each light direction and crystal orientation (retardation) can be determined at each pixel in the field of view. Retardation profiles across grain boundaries enable the calculation of grain boundary angle and direction. The data for all positions separating the grains are combined and further processed. In combination with the lateral position of the grain boundary, acquired using the FAME software (Hammes and Peternell, in review), the data is used to reconstruct a 3d grain boundary model. The processing of data is almost fully automatic by using MATLAB®. Only minor manual input is required. The applicability was demonstrated on quartzite samples, but the method is not solely restricted on quartz grains and other birefringent polycrystalline materials could be used instead. References: Birchenall, C.E., 1959: Physical Metallurgy. McGraw-Hill, New York. Doherty, R.D., Hughes, D.A., Humphreys, F.J., Jonas, J.J., Juul Jensen, D., Kassner, M.E., King, W.E., McNelley, T.R., McQueen, H.J., Rollett, A.D., 1997: Current issues in recrystallization: a review. Materials Science and Engineering A 238, 219-274. Hammes, D.M., Peternell, M., in review. FAME: Software for analysing rock microstructures. Computers & Geoscience. Kruhl, J.H., Peternell, M., 2002. The equilibration of high-angle grain boundaries in dynamically recrystallized quartz: the effect of crystallography and temperature. Journal of Structural Geology 24, 1125-1137. Kuntcheva, B., Kruhl, J.H. & Kunze, K., 2006. Crystallographic orientation of high-angle grain boundaries in dynamically recrystallized quartz: First results. Tectonophysics 421, 331-346. Peternell, M., Hasalová, P., Wilson, J.L., Piaziolo, S., Schulmann, K., 2010. Evaluating quartz crystallographic preferred orientations and the role of deformation partitioning using EBSD and fabric analyser techniques. Journal of Structural Geology 32, 803-817.

Characterizing 3D grain size distributions from 2D sections in mylonites using a modified version of the Saltykov method

NASA Astrophysics Data System (ADS)

Lopez-Sanchez, Marco; Llana-Fúnez, Sergio

2016-04-01

The understanding of creep behaviour in rocks requires knowledge of 3D grain size distributions (GSD) that result from dynamic recrystallization processes during deformation. The methods to estimate directly the 3D grain size distribution -serial sectioning, synchrotron or X-ray-based tomography- are expensive, time-consuming and, in most cases and at best, challenging. This means that in practice grain size distributions are mostly derived from 2D sections. Although there are a number of methods in the literature to derive the actual 3D grain size distributions from 2D sections, the most popular in highly deformed rocks is the so-called Saltykov method. It has though two major drawbacks: the method assumes no interaction between grains, which is not true in the case of recrystallised mylonites; and uses histograms to describe distributions, which limits the quantification of the GSD. The first aim of this contribution is to test whether the interaction between grains in mylonites, i.e. random grain packing, affects significantly the GSDs estimated by the Saltykov method. We test this using the random resampling technique in a large data set (n = 12298). The full data set is built from several parallel thin sections that cut a completely dynamically recrystallized quartz aggregate in a rock sample from a Variscan shear zone in NW Spain. The results proved that the Saltykov method is reliable as long as the number of grains is large (n > 1000). Assuming that a lognormal distribution is an optimal approximation for the GSD in a completely dynamically recrystallized rock, we introduce an additional step to the Saltykov method, which allows estimating a continuous probability distribution function of the 3D grain size population. The additional step takes the midpoints of the classes obtained by the Saltykov method and fits a lognormal distribution with a trust region using a non-linear least squares algorithm. The new protocol is named the two-step method. The conclusion of this work is that both the Saltykov and the two-step methods are accurate and simple enough to be useful in practice in rocks, alloys or ceramics with near-equant grains and expected lognormal distributions. The Saltykov method is particularly suitable to estimate the volumes of particular grain fractions, while the two-step method to quantify the full GSD (mean and standard deviation in log grain size). The two-step method is implemented in a free, open-source and easy-to-handle script (see http://marcoalopez.github.io/GrainSizeTools/).

REX3DV1.0

DOE Office of Scientific and Technical Information (OSTI.GOV)

Holm, Elizabeth A.

2002-03-28

This code is a FORTRAN code for three-dimensional Monte Carol Potts Model (MCPM) Recrystallization and grain growth. A continuum grain structure is mapped onto a three-dimensional lattice. The mapping procedure is analogous to color bitmapping the grain structure; grains are clusters of pixels (sites) of the same color (spin). The total system energy is given by the Pott Hamiltonian and the kinetics of grain growth are determined through a Monte Carlo technique with a nonconserved order parameter (Glauber dynamics). The code can be compiled and run on UNIX/Linux platforms.

Intragranular Recrystallization and Lattice Reorientation of Calcite Grains in Experimentally Deformed Crinoids and Trilobites

NASA Astrophysics Data System (ADS)

Kim, N.; Takahashi, M.; Shigematsu, N.; Ree, J. H.; Jung, H.

2017-12-01

Intragranular recrystallization, including subgrain-rotation-recrystallization (SGR) and nucleation (and growth) of new grains along boundaries of deformation twins and bands, is an important process leading to grain-size reduction and causing rheological change depending on deformation condition. Despite of its importance, the detailed processes of intragranular recrystallization are still somewhat unclear. We deformed a limestone using triaxial testing machine at AIST of Japan at temperature of 500 700 °, strain rate of 10-4 10-5 s-1, confining pressure of 200 MPa and strain of up to 30%, to explore intragranular recrystallization processes of calcite. The limestone contains two abundant fossils, crinoid and trilobite. The crinoids are mono- or poly-crystalline. We focus on the monocrystalline crinoids with a coarser grain size ( 700 μm). The trilobites are polycrystalline and much finer-grained ( 7 μm) with initially a strong c-axis preferred orientation. At a lower temperature condition, subgrains develop both in twin and host domains of crinoids and evolve into new grains by SGR. At a higher temperature, recrystallized grains have irregular grain boundaries and bimodal grain-size distribution, implying grain-boundary migration (GBM) recrystallization. At a lower temperature, new grains nucleating and growing along twin boundaries inherit lattice orientation of twin domain, and with the nucleation site and usually a smaller grain size, they can be distinguished from new grains by SGR. At a higher temperature, however, the distinction is difficult at present due to extensive GBM. For the trilobites, there is only local GBM with no significant change in grain size, and flattening of grains reflects the bulk strain at a lower temperature. At a higher temperature, individual grains of the trilobites are equi-axed with weakened LPO, although the strain of trilobites is higher than bulk strain. These microfabrics suggest that the dominant deformation mechanism of the trilobites is diffusion creep. Although the initial LPO of the trilobites is weakened, the LPO is still preserved up to strain of 30%. This implies that even if the grain size of trilobites and matrix is similar in naturally deformed limestones, the lattice orientation map may be useful in recognizing trilobite fossils.

Effect of one-step recrystallization on the grain boundary evolution of CoCrFeMnNi high entropy alloy and its subsystems.

PubMed

Chen, Bo-Ru; Yeh, An-Chou; Yeh, Jien-Wei

2016-02-29

In this study, the grain boundary evolution of equiatomic CoCrFeMnNi, CoCrFeNi, and FeCoNi alloys after one-step recrystallization were investigated. The special boundary fraction and twin density of these alloys were evaluated by electron backscatter diffraction analysis. Among the three alloys tested, FeCoNi exhibited the highest special boundary fraction and twin density after one-step recrystallization. The special boundary increment after one-step recrystallization was mainly affected by grain boundary velocity, while twin density was mainly affected by average grain boundary energy and twin boundary energy.

Microstructure and Mechanical Properties of Laser Solid Formed Ti-6Al-4V Alloy Under Dynamic Shear Loading

NASA Astrophysics Data System (ADS)

Zhou, Ping; Guo, Wei-Guo; Su, Yu; Wang, Jianjun; Lin, Xin; Huang, Weidong

2017-07-01

To investigate the mechanical properties of the Ti-6Al-4V alloy fabricated by laser solid forming technology, both static and dynamic shear tests were conducted on hat-shaped specimens by a servohydraulic testing machine and an enhanced split Hopkinson pressure bar system, over a temperature range of 173-573 K. The microstructure of both the original and deformed specimens was characterized by optical microscopy and scanning electron microscopy. The results show that: (1) the anisotropy of shear properties is not significant regardless of the visible stratification and the prior- β grains that grow epitaxially along the depositing direction; (2) the ultimate shear strength of this material is lower than that of those Ti-6Al-4V alloys fabricated by forging and extrusion; (3) the adiabatic shear bands of approximately 25.6-36.4 μm in width can develop at all selected temperatures during the dynamic shear deformation; and (4) the observed microstructure and measured microhardness indicate that the grains become refined in adiabatic shear band. Estimation of the temperature rise shows that the temperature in shear band exceeds the recrystallization temperature. The process of rotational dynamic recrystallization is considered to be the cause of the grain refinement in shear band.

BHQ revisited (1) - Looking at grain size

NASA Astrophysics Data System (ADS)

Heilbronner, Renée; Kilian, Rüdiger; Tullis, Jan

2016-04-01

Black Hills Quartzite (BHQ) has been used extensively in experimental rock deformation for numerous studies. Coaxial and general shear experiments have been carried out, for example, to define the dislocation creep regimes of quartz (Hirth & Tullis, 1992), to determine the effect of annealing (Heilbronner & Tullis, 2002) or to study the development of texture and microstructure with strain (Heilbronner & Tullis, 2006). BHQ was also used to determine the widely used quartz piezometer by Stipp & Tullis (2003). Among the microstructure analyses that were performed in those original papers, grain size was usually determined using CIP misorientation images. However, the CIP method (= computer-integrated polarization microscopy, details in Heilbronner and Barrett, 2014) is only capable of detecting the c-axis orientation of optically uniaxial materials and hence is only capable of detecting grain boundaries between grains that differ in c-axis orientation. One of the puzzling results we found (Heilbronner & Tullis, 2006) was that the recrystallized grain size seemed to depend on the crystallographic preferred orientation of the domain. In other words the grain size did not only depend on the flow stress but also on the orientation of the c-axis w/r to the shear direction. At the time, no EBSD analysis (electron back scatter diffraction) was carried out and hence the full crystallographic orientation was not known. In principle it is therefore possible that we missed some grain boundaries (between grains with parallel c-axes) and miscalculated our grain sizes. In the context of recent shear experiments on quartz gouge at the brittle-viscous transition (see Richter et al., this conference), where EBSD is used to measure the recrystallized grain size, we wanted to re-measure the CIP grain sizes of our 2006 samples (deformed in regime 1, 2 and 3 of dislocation) in exactly the same way. In two companion posters we use EBSD orientation imaging to repeat, refine and expand the microstructure and texture analysis of Heilbronner & Tullis (2006). Here, in poster (1), we focus on the recrystallized grain size with the aim of (a) comparing CIP- and EBSD derived grain size measurements, (b) of comparing the recrystallized grain size of coaxially deformed and sheared BHQ and (c) in order to confirm that the quartz piezometer indeed depends on texture, and (d) to test if it also depends on the type of deformation (irrotational versus rotational deformation). References cited: Heilbronner, R., and S.D. Barrett (2014) Image Analysis in Earth Sciences, Springer. Heilbronner, R., and J. Tullis (2002), The effect of static annealing on micro- structure and crystallographic preferred orientations of quartzites experimentally deformed in axial compression and shear, Geol. Soc. Spec. Publ., 200, 191 - 218. Heilbronner, R., and J. Tullis (2006), Evolution of c axis pole figures and grain size during dynamic recrystallization: Results from experimentally sheared quartzite. JGR, 111, B10202, doi:10.1029/2005JB004194, 2006 Hirth, G., and J. Tullis (1992), Dislocation creep regimes in quartz aggregates, JSG, 14, 145-159. Stipp, M., and J. Tullis (2003), The recrystallized grain size piezometer for quartz, Geophys. Res. Lett., 30(21), 2088, doi:10.1029/2003GL018444.

Microstructure, texture, and mechanical properties of friction stir welded commercial brass alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Heidarzadeh, A., E-mail: ak.hz62@gmail.com

Microstructural evolution during friction stir welding of single-phase brass and corresponding mechanical properties were investigated. For this purpose, 2 mm thick brass plate was friction stir welded at a rotational speed of 450 rpm and traverse speed of 100 mm/min. The microstructure of the joint was studied using optical microscopy, scanning electron microscopy equipped with electron back scattered diffraction system, and scanning transmission electron microscopy. The mechanical properties were measured using hardness and tensile tests. The formation of subgrains and their transformation into new grains in conjunction with existence of A{sub 1}{sup ⁎}, A{sub 2}{sup ⁎} and C texture componentsmore » revealed that the continuous dynamic recrystallization plays a dominant role in the microstructural evolution. However, grain boundary bulging, along with the formation of twin boundaries, and presence of the G texture component showed that the discontinues dynamic recrystallization may participate in the new grain formation. Furthermore, the different strengthening mechanisms, which caused the higher strength of the joint, were discussed. - Highlights: •Microstructural evolution during FSW of a single phase brass was investigated. •CDRX and DDRX were the main mechanisms of the grain structure formation during FSW. •GDRX and SRX were not contributed in grain structure formation. •The lamellas TBs were formed in the SZ of the joints. •Grain boundary, dislocation, and texture effects resulted in higher strength.« less

Effect of one-step recrystallization on the grain boundary evolution of CoCrFeMnNi high entropy alloy and its subsystems

PubMed Central

Chen, Bo-Ru; Yeh, An-Chou; Yeh, Jien-Wei

2016-01-01

In this study, the grain boundary evolution of equiatomic CoCrFeMnNi, CoCrFeNi, and FeCoNi alloys after one-step recrystallization were investigated. The special boundary fraction and twin density of these alloys were evaluated by electron backscatter diffraction analysis. Among the three alloys tested, FeCoNi exhibited the highest special boundary fraction and twin density after one-step recrystallization. The special boundary increment after one-step recrystallization was mainly affected by grain boundary velocity, while twin density was mainly affected by average grain boundary energy and twin boundary energy. PMID:26923713

Microstructure evolution and texture development of hot form-quench (HFQ) AZ31 twin roll cast (TRC) magnesium alloy

NASA Astrophysics Data System (ADS)

Alias, J.; Zhou, X.; Das, Sanjeev; El-Fakir, Omer; Thompson, G. E.

2017-12-01

The present study on the microstructure evolution of hot form-quench (HFQ) AZ31 twin roll cast magnesium alloy attempt to provide an understanding on the grain structure and heterogeneous intermetallic phase formation in the alloy and texture development following the HFQ process. Grain recrystallization and partial dissolution of eutectic β-Mg17Al12 phase particles were occurred during the solution heat treatment at 450°C, leaving the alloy consists of recrystallized grains and discontinuous or random β-Mg17Al12 phase particles distribution with small volume fraction. The particles act as effective nucleation sites for new grains during recrystallization and variation of recrystallization occurrence contributed to texture alteration. The partial or full β-Mg17Al12 phase dissolution following the HFQ induces void formation that act as fracture nucleation site and the corresponding texture alteration in the recrystallized grains led to poor formability in TRC alloy.

Microstructure Characterization of Weakly Textured and Fine Grained AZ61 Sheet

NASA Astrophysics Data System (ADS)

Berman, T. D.; Donlon, W.; Hung, C. K.; Milligan, P.; Decker, R.; Pollock, T. M.; Jones, J. W.

Formability in magnesium alloy sheet is strongly limited by a strong basal texture in the as-rolled material, which is difficulty to remove by thermal processing. We introduce a new process to the control of texture by combining Thixomolding and Thermomechanical Processing (TTMP). Plates of AZ61L with a divorced β-Mg17Al12 eutectic are produced by Thixomolding, resulting in a non-textured, fine grained (2.8 µm) precursor. Sheet produced from the plate by single pass warm-rolling exhibits a weaker texture, and more isotropic tensile deformation than generally observed in AZ-series alloy sheet. Recrystallization annealing produces a further reduction in texture and average grain size (2.3 µm) and results in nearly isotropic room temperature deformation, a yield strength of 220 MPa, and an elongation of 23%. Particle stimulated nucleation of new grains by the β-phase during both dynamic and static recrystallization, is critical for achieving the low levels of texture. The influence of β-phase distribution in microstructure development is discussed.

Photoacoustic Imaging.

DTIC Science & Technology

1983-12-01

recrystallization is currently an active area of research. Much effort has been made to grow large grain polysilicon with grain sizes of 100 microns from fine grain... polysilicon using laser recrystallization. The recrystallization process is inherently traumatic, producing large changes in temperature in short...temperature distribution above as the source term in the acoustic field equation, we ol fain r where B1)jwP) The general solution to this equation is given by

Texture Development and Material Flow Behavior During Refill Friction Stir Spot Welding of AlMgSc

NASA Astrophysics Data System (ADS)

Shen, Junjun; Lage, Sara B. M.; Suhuddin, Uceu F. H.; Bolfarini, Claudemiro; dos Santos, Jorge F.

2018-01-01

The microstructural evolution during refill friction stir spot welding of an AlMgSc alloy was studied. The primary texture that developed in all regions, with the exception of the weld center, was determined to be 〈110〉 fibers and interpreted as a simple shear texture with the 〈110〉 direction aligned with the shear direction. The material flow is mainly driven by two components: the simple shear acting on the horizontal plane causing an inward-directed spiral flow and the extrusion acting on the vertical plane causing an upward-directed or downward-directed flow. Under such a complex material flow, the weld center, which is subjected to minimal local strain, is the least recrystallized. In addition to the geometric effects of strain and grain subdivision, thermally activated high-angle grain boundary migration, particularly continuous dynamic recrystallization, drives the formation of refined grains in the stirred zone.

Microstructure Evolution and Mechanical Properties of High-Speed Friction Stir Welded Aluminum Alloy Thin Plate Joints

NASA Astrophysics Data System (ADS)

Liu, Fenjun; Fu, Li; Chen, Haiyan

2018-06-01

Sound friction stir welded (FSW) joints of 6061-T6 aluminum alloy sheets with an 0.8 mm thickness were obtained at conventional speed (2000 rpm, 300 mm/min) and high speed (11,000 rpm, 1500 mm/min). The recrystallization mechanism, precipitate evolution, mechanical properties and fracture behavior were investigated in detail. Microstructure analyses revealed that the grain structure evolution in the nugget zone (NZ) was dominated by continuous dynamic recrystallization. In the process of FSW, high speed facilitates the formation of finer equiaxed recrystallized grains, higher density of dislocations and substructures, and a larger number of precipitates in the NZ compared to the conventional speed, which further significantly improves the hardness and tensile strength of the joints. The maximum tensile strength was obtained with 292.6 MPa, 83.2% for the 6061-T6 aluminum alloy and 122.6% for the conventional-speed FSW joints. This work provides an effective method for preparing FSW aluminum alloy thin plate joints with excellent mechanical properties.

Effect of Mo on dynamic recrystallization and microstructure development of microalloyed steels

NASA Astrophysics Data System (ADS)

Schambron, Thomas; Dehghan-Manshadi, Ali; Chen, Liang; Gooch, Taliah; Killmore, Chris; Pereloma, Elena

2017-07-01

The dynamic recrystallization (DRX) behaviour, mechanical properties and microstructure development of four low carbon, Nb-Ti-containing micro-alloyed steels with Mo contents from 0 to 0.27 wt% were studied. Plane strain compression tests were performed in a Gleeble 3500 thermomechanical simulator. The effects of composition, deformation temperature and strain rate on the DRX parameters and resultant microstructures were examined. The volume fraction of recrystallised grains was estimated from micrographs and a DRX model. The stress-strain curves showed the typical signs of DRX over a wide range of deformation conditions. Dynamic recovery was only observed for higher strain rates (5 s-1) and/or lower deformation temperatures (below 1000 °C). It was shown that Mo increases the hot strength by around 100 MPa per weight percent. In addition, it has an effect on retarding recrystallization in microalloyed steels by increasing the activation energy for DRX by 320 kJ/molK per weight percent. This was attributed to solute drag and the interaction with other microalloying elements.

Rheology linked with phase changes as recorded by development of shear bands in the South Armorican Shear Zone

NASA Astrophysics Data System (ADS)

Jeřábek, Petr; Bukovská, Zita

2015-04-01

The South Armorican Shear Zone in France represents a major right-lateral strike slip shear zone formed in the late stages of Variscan orogeny. The active deformation in this shear zone is associated with the development of S-C fabrics in granitoids where thin shear bands (C) overprint an earlier higher grade metamorphic foliation (S). In the studied samples covering low to high intensity of shear band overprint, we identified three stages of shear band evolution associated with distinct microstructures and deformation mechanisms. The initiation of shear bands stage I is associated with the formation of microcracks crosscutting the S fabric and detected namely in the recrystallized quartz aggregates. The microcracks of suitable orientation are filled by microcline, albite, muscovite and chlorite which is a typical assemblage also for the well developed shear bands. Phase equilibrium modeling in PERPLEX indicates that this assemblage formed at pressure-temperature range of 0.1-0.4 GPa and 300-340 °C. Stage II of shear band evolution is characterized by dynamic recrystallization and grain size reduction of quartz aggregates along the microcracks and replacement of quartz by microcline along grain boundaries. This process leads to disintegration of quartz aggregate fabric and phase mixing in the shear bands. The inferred deformation mechanism for this stage is solution-precipitation creep although recrystallization of quartz is still active at the contact between quartz aggregates and shear bands. The coarse grained microstructure of quartz aggregates with ca ~250 microns average grain size reduces to ~10 microns grain size when recrystallized along extremely thin shear bands/microcracks and to ~20 microns grain size when recrystallized along the thicker shear bands. By using the flow law of Patterson and Luan (1990) for dislocation creep in quartz and the quartz piezometer of Stipp and Tullis (2003) corrected after Holyoke and Kronenberg (2010), the quartz recrystallization along thin shear bands records strain rates of ~10^-14 whereas the recrystallization along thick shear bands records strain rates of ~10^-15. The contemporaneous operation of solution-precipitation creep in shear bands and dislocation creep in quartz along the shear band boundary suggests low viscosity contrast between the mixed phase shear band matrix and pure quartz aggregate implying that the solution-precipitation creep reflect similar stress and strain rate conditions as the dislocation creep in quartz. Stage III of shear band evolution is characterized by interconnection of dispersed muscovite grains and the deformation becomes accommodated by dislocation creep in thin muscovite bands separating the inactive domains of stage II microstructure. References: Holyoke III, C. W., & Kronenberg, A. K. (2010). Accurate differential stress measurement using the molten salt cell and solid salt assemblies in the Griggs apparatus with applications to strength, piezometers and rheology. Tectonophysics, 494(1-2), 17-31. Paterson, M. S., & Luan, F. C. (1990). Quartzite rheology under geological conditions. In R. J. Knipe & E. H. Rutter (Eds.), Deformation Mechanisms, Rheology and Tectonics (pp. 299-307). London: Geological Society Special Publications. Stipp, M., & Tullis, J. (2003). The recrystallized grain size piezometer for quartz. Geophysical Research Letters, 30(21), 1-5.

Effect of Sn Micro-alloying on Recrystallization Nucleation and Growth Processes of Ferritic Stainless Steels

NASA Astrophysics Data System (ADS)

He, Tong; Bai, Yang; Liu, Xiuting; Guo, Dan; Liu, Yandong

2018-04-01

We investigated the effect of Sn micro-alloying on recrystallization nucleation and growth processes of ferritic stainless steels. The as-received hot rolled sheets were cold rolled up to 80% reduction and then annealed at 740-880 °C for 5 min. The cold rolling and recrystallization microstructures and micro-textures of Sn-containing and Sn-free ferritic stainless steels were all determined by electron backscatter diffraction. Our Results show that Sn micro-alloying has important effects on recrystallization nucleation and growth processes of ferritic stainless steels. Sn micro-alloying conduces to grain fragmentation in the deformation band, more fragmented grains are existed in Sn-containing cold rolled sheets, which provides more sites for recrystallization nucleation. Sn micro-alloying also promotes recrystallization process and inhibits the growth of recrystallized grains. The recrystallization nucleation and growth mechanism of Sn-containing and Sn-free ferritic stainless steels are both characterized by orientation nucleation and selective growth, but Sn micro-alloying promotes the formation of γ-oriented grains. Furthermore, Sn micro-alloying contributes to the formation of Σ13b CSL boundaries and homogeneous γ-fiber texture. Combining the results of microstructure and micro-texture, the formability of Sn-containing ferritic stainless steels will be improved to some extent.

Recrystallization as a controlling process in the wear of some f.c.c. metals

NASA Technical Reports Server (NTRS)

Bill, R. C.; Wisander, D.

1977-01-01

Detailed examination of copper specimens after sliding against 440 C steel in liquid methane at speeds up to 25 m/s and loads of up to 2 kg showed the metal comprising the wear surface to possess a fine cell recrystallized structure. Wear proceeded by the plastic shearing of metal in this near surface region without the occurrence of visible metal transfer. A dynamic balance between the intense shear process at the surface and the nucleation of recrystallized grains was proposed to account for the behavior of the metal at the wear surface. Sliding wear experiments were also conducted on Ag, Cu-10% Al, Cu-10% Sn, Ni and Al. It was found that low wear and the absence of heavy metal transfer were associated with those metals observed to undergo recrystallization nucleation without prior recovery.

Deformation-related recrystallization processes

NASA Astrophysics Data System (ADS)

Drury, Martyn R.; Urai, Janos L.

1990-02-01

Recrystallization is a common microstructural transformation that occurs during deformation, metamorphism and diagenesis of rocks. Studies on minerals and rock analogues have demonstrated that a wide range of recrystallization mechanisms can occur. The range of mechanisms is related to the various ways in which two basic processes, grain boundary migration and new grain boundary formation combine to transform the microstructure. Two recent papers (Drury et al., 1985; Urai et al., 1986) have proposed different schemes for the description of recrystallization mechanisms. The purpose of this paper is to provide a unified framework for the description of mechanisms. Recrystallization mechanisms are divided into three main types; rotation mechanisms which principally involve the formation of new grain boundaries; migration mechanisms which principally involve grain boundary migration; and general mechanisms which involve both basic processes. A further distinction is made on the basis of the continuity of the microstructural transformation with respect to time. Each of the three main types of mechanism can be divided into a number of sub-types depending on whether the processes of grain boundary migration, new grain boundary formation and new grain formation occur in a discontinuous or continuous manner with respect to time. As the terms continuous and discontinuous have been used in the metallurgical literature to signify the spatial continuity of the microstructural transformation, the terms discontinuai and continual are used to refer to the temporal continuity of the transformation. It is recommended that the following aspects should be specified, if possible, in a general description of recrystallization mechanisms: (1) How do the basic processes combine to transform the microstructure. (2) If new grain development occurs, what is the development mechanism, and does new grain formation occur in a continual or discontinuai manner. (3) If grain boundary migration is involved in the transformation, what is the migration mechanism (i.e. fast solute escape migration, slow solute loaded migration, fluid assisted migration, etc.), and is migration a continual or discontinuai process. The application of the unified scheme is illustrated by reviewing studies that have provided detailed information on the recrystallization mechanisms involved. The complicating effects of solid solution impurities, dispersed second phase particles and grain boundary fluid films are also considered and it is demonstrated that variations in content of these types of impurity can significantly effect the types of recrystallization that occur in a given material.

Evolution of microstructure of Haynes 230 and Inconel 617 under mechanical testing at high temperatures

NASA Astrophysics Data System (ADS)

Hrutkay, Kyle

Haynes 230 and Inconel 617 are austenitic nickel based superalloys, which are candidate structural materials for next generation high temperature nuclear reactors. High temperature deformation behavior of Haynes 230 and Inconel 617 have been investigated at the microstructural level in order to gain a better understanding of mechanical properties. Tensile tests were performed at strain rates ranging from 10-3-10-5 s -1 at room temperature, 600 °C, 800 °C and 950 °C. Subsequent microstructural analysis, including Scanning Electron Microscopy, Transmission Electron Microscopy, Energy-Dispersive X-ray Spectroscopy, and X-Ray Diffraction were used to relate the microstructural evolution at high temperatures to that of room temperature samples. Grain sizes and precipitate morphologies were used to determine high temperature behavior and fracture mechanics. Serrated flow was observed at intermediate and high temperatures as a result of discontinuous slip and dynamic recrystallization. The amplitude of serration increased with a decrease in the strain rate and increase in the temperature. Dynamic strain ageing was responsible for serrations at intermediate temperatures by means of a locking and unlocking phenomenon between dislocations and solute atoms. Dynamic recrystallization nucleated by grain and twin bulging resulting in a refinement of grain size. Existing models found in the literature were discussed to explain both of these phenomena.

Recrystallization and grain growth induced by ELMs-like transient heat loads in deformed tungsten samples

NASA Astrophysics Data System (ADS)

Suslova, A.; El-Atwani, O.; Sagapuram, D.; Harilal, S. S.; Hassanein, A.

2014-11-01

Tungsten has been chosen as the main candidate for plasma facing components (PFCs) due to its superior properties under extreme operating conditions in future nuclear fusion reactors such as ITER. One of the serious issues for PFCs is the high heat load during transient events such as ELMs and disruption in the reactor. Recrystallization and grain size growth in PFC materials caused by transients are undesirable changes in the material, since the isotropic microstructure developed after recrystallization exhibits a higher ductile-to-brittle transition temperature which increases with the grain size, a lower thermal shock fatigue resistance, a lower mechanical strength, and an increased surface roughening. The current work was focused on careful determination of the threshold parameters for surface recrystallization, grain growth rate, and thermal shock fatigue resistance under ELM-like transient heat events. Transient heat loads were simulated using long pulse laser beams for two different grades of ultrafine-grained tungsten. It was observed that cold rolled tungsten demonstrated better power handling capabilities and higher thermal stress fatigue resistance compared to severely deformed tungsten. Higher recrystallization threshold, slower grain growth, and lower degree of surface roughening were observed in the cold rolled tungsten.

Recrystallization and grain growth induced by ELMs-like transient heat loads in deformed tungsten samples

PubMed Central

Suslova, A.; El-Atwani, O.; Sagapuram, D.; Harilal, S. S.; Hassanein, A.

2014-01-01

Tungsten has been chosen as the main candidate for plasma facing components (PFCs) due to its superior properties under extreme operating conditions in future nuclear fusion reactors such as ITER. One of the serious issues for PFCs is the high heat load during transient events such as ELMs and disruption in the reactor. Recrystallization and grain size growth in PFC materials caused by transients are undesirable changes in the material, since the isotropic microstructure developed after recrystallization exhibits a higher ductile-to-brittle transition temperature which increases with the grain size, a lower thermal shock fatigue resistance, a lower mechanical strength, and an increased surface roughening. The current work was focused on careful determination of the threshold parameters for surface recrystallization, grain growth rate, and thermal shock fatigue resistance under ELM-like transient heat events. Transient heat loads were simulated using long pulse laser beams for two different grades of ultrafine-grained tungsten. It was observed that cold rolled tungsten demonstrated better power handling capabilities and higher thermal stress fatigue resistance compared to severely deformed tungsten. Higher recrystallization threshold, slower grain growth, and lower degree of surface roughening were observed in the cold rolled tungsten. PMID:25366885

Recrystallization and grain growth induced by ELMs-like transient heat loads in deformed tungsten samples.

PubMed

Suslova, A; El-Atwani, O; Sagapuram, D; Harilal, S S; Hassanein, A

2014-11-04

Tungsten has been chosen as the main candidate for plasma facing components (PFCs) due to its superior properties under extreme operating conditions in future nuclear fusion reactors such as ITER. One of the serious issues for PFCs is the high heat load during transient events such as ELMs and disruption in the reactor. Recrystallization and grain size growth in PFC materials caused by transients are undesirable changes in the material, since the isotropic microstructure developed after recrystallization exhibits a higher ductile-to-brittle transition temperature which increases with the grain size, a lower thermal shock fatigue resistance, a lower mechanical strength, and an increased surface roughening. The current work was focused on careful determination of the threshold parameters for surface recrystallization, grain growth rate, and thermal shock fatigue resistance under ELM-like transient heat events. Transient heat loads were simulated using long pulse laser beams for two different grades of ultrafine-grained tungsten. It was observed that cold rolled tungsten demonstrated better power handling capabilities and higher thermal stress fatigue resistance compared to severely deformed tungsten. Higher recrystallization threshold, slower grain growth, and lower degree of surface roughening were observed in the cold rolled tungsten.

Microstructural and rheological evolution of calcite mylonites during shear zone thinning: Constraints from the Mount Irene shear zone, Fiordland, New Zealand

NASA Astrophysics Data System (ADS)

Negrini, Marianne; Smith, Steven A. F.; Scott, James M.; Tarling, Matthew S.

2018-01-01

Layers of calc-mylonite in the Mount Irene shear zone, Fiordland, New Zealand, show substantial variations in thickness due to deflection of the shear zone boundaries around wall rock asperities. In relatively thick parts (c. 2.6 m) of the shear zone, calcite porphyroclasts are internally strained, contain abundant subgrain boundaries and have a strong shape preferred orientation (SPO) and crystallographic preferred orientation (CPO), suggesting that deformation occurred mainly by dislocation creep involving subgrain-rotation recrystallization. In relatively thin parts (c. 1.5 m) of the shear zone, aggregates of fine-grained recrystallized calcite surrounding flattened porphyroclasts have a weak SPO and CPO, and contain polygonal calcite grains with low degrees of internal misorientation. The recrystallized aggregates also contain microstructures (e.g. grain quadruple junctions, randomized misorientation axes) similar to those reported for neighbor-switching processes during grain-boundary sliding. Comparison of subgrain sizes in the porphyroclasts to published grain-size differential-stress relationships indicates that stresses and strain rates were substantially higher in relatively thin parts of the shear zone. The primary microstructural response to higher stresses and strain rates was an increase in the amount of recrystallization to produce aggregates that deformed by grain-boundary sliding. However, even after the development of interconnected networks of recrystallized grains, dislocation creep by subgrain-rotation recrystallization continued to occur within porphyroclasts. This behavior suggests that the bulk rheology of shear zones undergoing thinning and thickening can be controlled by concomitant grain-size insensitive and grain-size sensitive mechanisms. Overall, our observations show that shear zone thickness variations at constant P-T can result in highly variable stresses and strain rates, which in turn modifies microstructure, deformation mechanism and shear zone rheology.

Grain Boundary Evolution of Cold-Rolled FePd Alloy during Recrystallization at Disordering Temperature

PubMed Central

Lin, Hung-Pin; Chen, Delphic; Kuo, Jui-Chao

2015-01-01

In this study, the grain boundary character and texture of 50% and 90% cold-rolled FePd alloy was investigated during recrystallization at 700 °C. Electron backscatter diffraction (EBSD) measurements were performed on the rolling direction to normal direction section. Kernel average misorientation (KAM) calculated from EBSD measurements was employed to determine the recrystallization fraction. The Avrami exponent n of recrystallization is 1.9 and 4.9 for 50% and 90% cold rolling, respectively. The new formation of texture reveals random texture during the recrystallization process. As annealing time increased, the number of high angle boundary (HAGB) and coincidence site lattice (CSL) increased with consumption of low angle boundary (LAGB). In addition, possible transformations between different grain boundaries are observed here.

Stress in recrystallized quartz by electron backscatter diffraction mapping

NASA Astrophysics Data System (ADS)

Llana-Fúnez, S.

2017-07-01

The long-term state of stress at middle and lower crustal depths can be estimated through the study of the microstructure of exhumed rocks from active and/or ancient shear zones. Constitutive equations for deformation mechanisms in experimentally deformed rocks relate differential stress to the size of recrystallized grains. Cross et al. (2017) take advantage of electron backscatter diffraction mapping to systematically separate new recrystallized grains from host grains on the basis of the measurable lattice distorsion within the grains. They produce the first calibrated piezometer for quartz with this technique, reproducing within error a previous calibration based on optical microscopy.

Study of Improved Aluminum Materials for Vehicular Armor

DTIC Science & Technology

1977-04-07

and along cell walls. Dislocations generated during deformation cf the 17 -------------- recrystallized structure interacted with the grain...unrecrystallized (HR) 7475 plate containing dislocations within subgrains and along cell walls. Hot rolling the recrystallized structure at 750OF produced...a structure after solution heat treatment that consisted of elongated recrystallized grains containing polygonized cells . This structure developed

Influence of warm rolling temperature on ferrite recrystallization in low C and IF steels

NASA Astrophysics Data System (ADS)

Barnett, Matthew Robert

Experiments involving single pass laboratory rolling and isothermal salt bath annealing were carried out; three steels were studied: a titanium stabilized interstitial free grade and two low carbon grades, one of which contained a particularly low level of manganese (˜0.009wt.%). The two low carbon grades were produced such that any complication from AlN precipitation was avoided. X-ray, neutron diffraction, optical metallography and mechanical testing measurements were carried out on the samples before and after annealing. The main aim of this work was to further the understanding of the metallurgy of recrystallization after ferrite rolling at temperatures between room temperature and 700sp°C. Deformation textures, recrystallization kinetics, final grain sizes and recrystallization textures were quantified for all the samples and experimental conditions. A major conclusion based on these data is that the influence of rolling temperature is far greater in the low carbon samples than in the IF grade. Indeed, the IF results alter only marginally with increasing temperature. In the low carbon grades, however, the rolling texture sharpens, recrystallization slows, the final grain size coarsens, and the recrystallization texture changes when the rolling temperature is increased. This distinct difference between the two steel types is explained in terms of their contrasting deformation behaviors. Solute carbon and nitrogen in the low carbon grades interact with dislocations causing high stored energy levels after low temperature rolling (due to dynamic strain aging) and high strain rate sensitivities during high temperature rolling (due to the solute drag of dislocations in the transition region between DSA and DRC). Nucleation during subsequent recrystallization is strongly influenced by both the stored energy and the strain rate sensitivity. The latter affects the occurrence of the flow localisations that enhance nucleation.

Complete grain boundaries from incomplete EBSD maps: the influence of segmentation on grain size determinations

NASA Astrophysics Data System (ADS)

Heilbronner, Renée; Kilian, Ruediger

2017-04-01

Grain size analyses are carried out for a number of reasons, for example, the dynamically recrystallized grain size of quartz is used to assess the flow stresses during deformation. Typically a thin section or polished surface is used. If the expected grain size is large enough (10 µm or larger), the images can be obtained on a light microscope, if the grain size is smaller, the SEM is used. The grain boundaries are traced (the process is called segmentation and can be done manually or via image processing) and the size of the cross sectional areas (segments) is determined. From the resulting size distributions, 'the grain size' or 'average grain size', usually a mean diameter or similar, is derived. When carrying out such grain size analyses, a number of aspects are critical for the reproducibility of the result: the resolution of the imaging equipment (light microscope or SEM), the type of images that are used for segmentation (cross polarized, partial or full orientation images, CIP versus EBSD), the segmentation procedure (algorithm) itself, the quality of the segmentation and the mathematical definition and calculation of 'the average grain size'. The quality of the segmentation depends very strongly on the criteria that are used for identifying grain boundaries (for example, angles of misorientation versus shape considerations), on pre- and post-processing (filtering) and on the quality of the recorded images (most notably on the indexing ratio). In this contribution, we consider experimentally deformed Black Hills quartzite with dynamically re-crystallized grain sizes in the range of 2 - 15 µm. We compare two basic methods of segmentations of EBSD maps (orientation based versus shape based) and explore how the choice of methods influences the result of the grain size analysis. We also compare different measures for grain size (mean versus mode versus RMS, and 2D versus 3D) in order to determine which of the definitions of 'average grain size yields the most stable results.

A texture-component Avrami model for predicting recrystallization textures, kinetics and grain size

NASA Astrophysics Data System (ADS)

Raabe, Dierk

2007-03-01

The study presents an analytical model for predicting crystallographic textures and the final grain size during primary static recrystallization of metals using texture components. The kinetics is formulated as a matrix variant of the Johnson-Mehl-Avrami-Kolmogorov equation. The matrix form is required since the kinetic and crystallographic evolution of the microstructure is described in terms of a limited set of growing (recrystallizing) and swept (deformed) texture components. The number of components required (5-10) defines the order of the matrix since the kinetic coupling occurs between all recrystallizing and all deformed components. Each such couple is characterized by corresponding values for the nucleation energy and grain boundary mobility. The values of these parameters can be obtained by analytical or numerical coarse graining according to a renormalization scheme which replaces many individual grains which grow via recrystallization in a deformed texture component by a single equivalent recrystallization texture component or by fitting to experimental data. Each deformed component is further characterized by an average stored deformation energy. Each element of the kinetic matrix, reflecting one of the possible couplings between a deformed and a recrystallizing texture component, is then derived in each time step by a set of two differential equations. The first equation describes the thermally activated nucleation and growth processes for the expanded (free) volume for a particular couple of a deformed and a recrystallizing texture component and the second equation is used for calculating the constrained (real) volume for that couple which corrects the free volume for those portions of the deformation component which were already swept. The new method is particularly developed for the fast and physically based process simulation of recrystallization textures with respect to processing. The present paper introduces the method and applies it to the primary recrystallization of low carbon steels.

Strain Evolution in Cold-Warm Forged Steel Components Studied by Means of EBSD Technique

PubMed Central

Bonollo, Franco; Bassan, Fabio; Berto, Filippo

2017-01-01

Electron BackScatter Diffraction (EBSD) in conjunction with Field-Emission Environmental Scanning Electron Microscopy (FEG-ESEM) has been used to evaluate the microstructural and local plastic strain evolution in different alloys (AISI 1005, AISI 304L and Duplex 2205) deformed by a single-stage cold and warm forging process. The present work is aimed to describe the different behavior of the austenite and ferrite during plastic deformation as a function of different forging temperatures. Several topological EBSD maps have been measured on the deformed and undeformed states. Then, image quality factor, distributions of the grain size and misorientation have been analyzed in detail. In the austenitic stainless steel, the γ-phase has been found to harden more easily, then α-phase and γ-phase in AISI 1005 and in duplex stainless steel, sequentially. Compared to the high fraction of continuous dynamic recrystallized austenitic zones observed in stainless steels samples forged at low temperatures, the austenitic microstructure of samples forged at higher temperatures, 600–700 °C, has been found to be mainly characterized by large and elongated grains with some colonies of fine nearly-equiaxed grains attributed to discontinuous dynamic recrystallization. PMID:29258249

Microstructural evolution of a superaustenitic stainless steel during a two-step deformation process

NASA Astrophysics Data System (ADS)

Bayat, N.; Ebrahimi, G. R.; Momeni, A.; Ezatpour, H. R.

2018-02-01

Single- and two-step hot compression experiments were carried out on 16Cr25Ni6Mo superaustenitic stainless steel in the temperature range from 950 to 1150°C and at a strain rate of 0.1 s-1. In the two-step tests, the first pass was interrupted at a strain of 0.2; after an interpass time of 5, 20, 40, 60, or 80 s, the test was resumed. The progress of dynamic recrystallization at the interruption strain was less than 10%. The static softening in the interpass period increased with increasing deformation temperature and increasing interpass time. The static recrystallization was found to be responsible for fast static softening in the temperature range from 950 to 1050°C. However, the gentle static softening at 1100 and 1150°C was attributed to the combination of static and metadynamic recrystallizations. The correlation between calculated fractional softening and microstructural observations showed that approximately 30% of interpass softening could be attributed to the static recovery. The microstructural observations illustrated the formation of fine recrystallized grains at the grain boundaries at longer interpass time. The Avrami kinetics equation was used to establish a relationship between the fractional softening and the interpass period. The activation energy for static softening was determined as 276 kJ/mol.

Effects of homogenization treatment on recrystallization behavior of 7150 aluminum sheet during post-rolling annealing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Zhanying; Department of Applied Science, University of Québec at Chicoutimi, Saguenay, QC G7H 2B1; Zhao, Gang

2016-04-15

The effects of two homogenization treatments applied to the direct chill (DC) cast billet on the recrystallization behavior in 7150 aluminum alloy during post-rolling annealing have been investigated using the electron backscatter diffraction (EBSD) technique. Following hot and cold rolling to the sheet, measured orientation maps, the recrystallization fraction and grain size, the misorientation angle and the subgrain size were used to characterize the recovery and recrystallization processes at different annealing temperatures. The results were compared between the conventional one-step homogenization and the new two-step homogenization, with the first step being pretreated at 250 °C. Al{sub 3}Zr dispersoids with highermore » densities and smaller sizes were obtained after the two-step homogenization, which strongly retarded subgrain/grain boundary mobility and inhibited recrystallization. Compared with the conventional one-step homogenized samples, a significantly lower recrystallized fraction and a smaller recrystallized grain size were obtained under all annealing conditions after cold rolling in the two-step homogenized samples. - Highlights: • Effects of two homogenization treatments on recrystallization in 7150 Al sheets • Quantitative study on the recrystallization evolution during post-rolling annealing • Al{sub 3}Zr dispersoids with higher densities and smaller sizes after two-step treatment • Higher recrystallization resistance of 7150 sheets with two-step homogenization.« less

Deformation-Induced Recrystallization of Magnesium Single Crystals at Ambient Temperature

NASA Astrophysics Data System (ADS)

Molodov, K. D.; Al-Samman, T.; Molodov, D. A.

2015-04-01

Specially oriented magnesium single crystals were subjected to plane strain compression along the <112¯0> direction in c-axis extension at ambient temperature. The samples exhibited outstanding formability deforming up to a logarithmic final strain of -1. Investigations by optical and orientation imaging microscopy revealed that massive {101¯2} extension twinning at low strains consumed the whole sample and resulted in new soft orientations for slip. Observations also indicated that additional twinning took place in the completely twinned matrix by secondary and tertiary twinning events. At advanced stages of deformation newly formed, equiaxed small grains were observed within numerous bands related to former deformation twins. These “recrystallized” grains characterized by a low grain orientation spread of less than 1° generated new orientations, which led to a substantial weakening and randomization of the texture during deformation up to very large strains. The reported results in this paper are discussed with regard to the microstructure evolution arising from multiple twinning and continuous dynamic recrystallization at room temperature.

Influence of initial heating during final high temperature annealing on the offset of primary and secondary recrystallization in Cu-bearing grain oriented electrical steels

NASA Astrophysics Data System (ADS)

Rodriguez-Calvillo, P.; Leunis, E.; Van De Putte, T.; Jacobs, S.; Zacek, O.; Saikaly, W.

2018-04-01

The industrial production route of Grain Oriented Electrical Steels (GOES) is complex and fine-tuned for each grade. Its metallurgical process requires in all cases the abnormal grain growth (AGG) of the Goss orientation during the final high temperature annealing (HTA). The exact mechanism of AGG is not yet fully understood, but is controlled by the different inhibition systems, namely MnS, AlN and CuxS, their size and distribution, and the initial primary recrystallized grain size. Therefore, among other parameters, the initial heating stage during the HTA is crucial for the proper development of primary and secondary recrystallized microstructures. Cold rolled 0.3 mm Cu-bearing Grain Oriented Electrical Steel has been submitted to interrupted annealing experiments in a lab tubular furnace. Two different annealing cycles were applied:• Constant heating at 30°C/h up to 1000°C. Two step cycle with initial heating at 100°C/h up to 600°C, followed by 18 h soaking at 600°C and then heating at 30°C/h up to 1050°C. The materials are analyzed in terms of their magnetic properties, grain size, texture and precipitates. The characteristic magnetic properties are analyzed for the different extraction temperatures and Cycles. As the annealing was progressing, the coercivity values (Hc 1.7T [A/m]) decreased, showing two abrupt drops, which can be associated to the on-set of primary and secondary recrystallization. The primary recrystallized grain sizes and recrystallized fractions are fitted to a model using a non-isothermal approach. This analysis shows that, although the resulting grain sizes were similar, the kinetics for the two step annealing were faster due to the lower recovery. The on-set of secondary recrystallization was also shifted to higher temperatures in the case of the continuous heating cycle, which might end in different final grain sizes and final magnetic properties. In both samples, nearly all the observed precipitates are Al-Si-Mn nitrides, ranging from pure AlN to Si4Mn-nitride.

Fundamental Investigation of the Microstructural Parameters to Improve Dynamic Response in Al-Cu Model System

DTIC Science & Technology

2014-05-01

grain size. Recrystallization was then induced via annealing just above the solvus temperature. After quenching , the bars were immediately placed into...that the values were statistically significant. Precipitate sizes ranged from approximately 100 nanometers in diameter up to 2-5 microns in diameter

An electron microscopy examination of primary recrystallization in TD-nickel.

NASA Technical Reports Server (NTRS)

Petrovic, J. J.; Ebert, L. J.

1972-01-01

Primary recrystallization in TD-nickel 1 in. bar has previously been regarded as the process by which the initial fine grain structure is converted to a coarse grain size (increases in grain size by 500 times) under suitable deformation and annealing conditions. This process is dependent on deformation mode. While it occurs readily after rolling transverse to the bar axis and annealing (800 C), it is completely inhibited by longitudinal rolling and swaging deformations, even for very high (1320 C) annealing temperatures. A transmission electron microscopy examination of deformation and annealing substructures indicates that primary recrystallization in TD-nickel 1 in. bar actually occurs on the sub-light optical level, to produce a grain structure similar in size to the initial fine grained state.

Effects of rolling conditions on recrystallization microstructure and texture in magnetostrictive Fe-Ga-Al rolled sheets

NASA Astrophysics Data System (ADS)

Li, Jiheng; Liu, Yangyang; Li, Xiaojuan; Mu, Xing; Bao, Xiaoqian; Gao, Xuexu

2018-07-01

The effects of different rolling conditions on the microstructure and texture of primary and secondary recrystallization in magnetostrictive Fe82Ga9Al9+0.1at%NbC alloy sheets were investigated. After the primary recrystallization annealing at 850 °C for 5 min, the as-rolled sheets prepared by warm-cold rolling with an intermediate annealing, can be fully recrystallized, and obtain the homogeneous matrix in which the fine dispersed NbC precipitate particles are distributed. The primary recrystallization textures of sheets with different rolling conditions consist mostly of strong {1 0 0} textures, γ-fiber textures, {4 1 1}〈1 4 8〉 texture and weak Goss texture. In the primary recrystallized sheets prepared by warm-cold rolling with an intermediate annealing, the high energy grain boundaries and ∑9 boundaries have the highest proportion. After high temperature annealing, the secondary recrystallizations of Goss grains in these sheets are more complete, and the size of abnormal grown Goss grain is up to several centimeters, which results in the strongest Goss texture. Correspondingly, the largest magnetostriction of 183 ppm is observed. The sample prepared by warm-cold rolling with an intermediate annealing, has homogeneous primary matrix, special texture components and grain boundary distribution, all of which provide a better surrounding for the abnormal growth of Goss grains. This work indicates that the control of rolling conditions of Fe-Ga-Al alloy sheets is necessary to achieve the strong Goss texture and obtain a possible high magnetostriction if other appropriate conditions (stress, domain structure) are achieved.

On the Coupling between Recrystallization and Precipitation Following Hot Deformation in a γ-γ' Nickel-Based Superalloy

NASA Astrophysics Data System (ADS)

Seret, Anthony; Moussa, Charbel; Bernacki, Marc; Bozzolo, Nathalie

2018-06-01

Postdynamic recrystallization and γ' precipitation during cooling from γ' supersolvus temperature after hot compression were studied in the AD730 (AD730 is a trademark of Aubert et Duval Company in Paris, France) γ-γ' nickel-based superalloy. Emphasis was on not only both phenomena as distinct mechanisms but also on their mutual influence in terms of physical mechanisms. The growth of γ' precipitates is hastened in the unrecrystallized grains compared to the recrystallized ones. This could possibly be attributed to the higher dislocation content acting as high-diffusivity paths. Postdynamic recrystallization is not prevented by Smith-Zener pinning of the recrystallization front by the γ' precipitates. Instead, the recrystallization front dissolves γ' precipitates, which then reprecipitate discontinuously or continuously and coherently with the surrounding γ matrix in the recrystallized grains.

Hot deformation characteristics of INCONEL alloy MA 754 and development of a processing map

DOE Office of Scientific and Technical Information (OSTI.GOV)

Somani, M.C.; Muraleedharan, K.; Birla, N.C.

1994-08-01

The characteristics of hot deformation of INCONEL alloy MA 754 have been studies using processing maps obtained on the basis of flow stress data generated in compression in the temperature range 700 C to 1,150 C and strain rate range 0.001 to 100 s[sup [minus]1]. The map exhibited three domains. (1) A domain of dynamic recovery occurs in the temperature range 800 C to 1,075 C and strain rate range 0.02 to 2 s[sup [minus]1], with a peak efficiency of 18 pct occurring at 950 C and 0.1 s [sup [minus]1]. Transmission electron microscope (TEM) micrographs revealed stable subgrain structuremore » in this domain with the subgrain size increasing exponentially with an increase in temperature. (2) A domain exhibiting grain boundary cracking occurs at temperatures lower than 800 C and strain rates lower than 0.01 s[sup [minus]1]. (3) A domain exhibiting intense grain boundary cavitation occurs at temperatures higher than 1075 C. The material did not exhibit a dynamic recrystallization (DRX) domain, unlike other superalloys. At strain rates higher than about 1 s[sup [minus]1], the material exhibits flow instabilities manifesting as kinking of the elongated grains and adiabatic shear bands. The materials may be safely worked in the domain of dynamic recovery but can only be statically recrystallized.« less

Microstructural Evolution During Cold Rolling and Subsequent Annealing in Low-Carbon Steel with Different Initial Microstructures

NASA Astrophysics Data System (ADS)

Ogawa, Toshio; Dannoshita, Hiroyuki; Maruoka, Kuniaki; Ushioda, Kohsaku

2017-08-01

Microstructural evolution during cold rolling and subsequent annealing of low-carbon steel with different initial microstructures was investigated from the perspective of the competitive phenomenon between recrystallization of ferrite and reverse phase transformation from ferrite to austenite. Three kinds of hot-rolled sheet specimens were prepared. Specimen P consisted of ferrite and pearlite, specimen B consisted of bainite, and specimen M consisted of martensite. The progress of recovery and recrystallization of ferrite during annealing was more rapid in specimen M than that in specimens P and B. In particular, the recrystallized ferrite grains in specimen M were fine and equiaxed. The progress of ferrite-to-austenite phase transformation during intercritical annealing was more rapid in specimen M than in specimens P and B. In all specimens, the austenite nucleation sites were mainly at high-angle grain boundaries, such as those between recrystallized ferrite grains. The austenite distribution was the most uniform in specimen M. Thus, we concluded that fine equiaxed recrystallized ferrite grains were formed in specimen M, leading to a uniform distribution of austenite.

Rotation-induced grain growth and stagnation in phase-field crystal models.

PubMed

Bjerre, Mathias; Tarp, Jens M; Angheluta, Luiza; Mathiesen, Joachim

2013-08-01

We consider grain growth and stagnation in polycrystalline microstructures. From the phase-field crystal modeling of the coarsening dynamics, we identify a transition from a grain-growth stagnation upon deep quenching below the melting temperature T(m) to a continuous coarsening at shallower quenching near T(m). The grain evolution is mediated by local grain rotations. In the deep quenching regime, the grain assembly typically reaches a metastable state where the kinetic barrier for recrystallization across boundaries is too large and grain rotation with subsequent coalescence or boundary motion is infeasible. For quenching near T(m), we find that the grain growth depends on the average rate of grain rotation, and follows a power-law behavior with time, with a scaling exponent that depends on the quenching depth.

Hot deformation characteristics of as-cast high-Cr ultra-super-critical rotor steel with columnar grains

NASA Astrophysics Data System (ADS)

Ding, Zong-ye; Hu, Qiao-dan; Zeng, Long; Li, Jian-guo

2016-11-01

Isothermal hot compression tests of as-cast high-Cr ultra-super-critical (USC) rotor steel with columnar grains perpendicular to the compression direction were carried out in the temperature range from 950 to 1250°C at strain rates ranging from 0.001 to 1 s-1. The softening mechanism was dynamic recovery (DRV) at 950°C and the strain rate of 1 s-1, whereas it was dynamic recrystallization (DRX) under the other conditions. A modified constitutive equation based on the Arrhenius model with strain compensation reasonably predicted the flow stress under various deformation conditions, and the activation energy was calculated to be 643.92 kJ•mol-1. The critical stresses of dynamic recrystallization under different conditions were determined from the work-hardening rate ( θ)-flow stress ( σ) and -∂ θ/∂ σ-σ curves. The optimum processing parameters via analysis of the processing map and the softening mechanism were determined to be a deformation temperature range from 1100 to 1200°C and a strain-rate range from 0.001 to 0.08 s-1, with a power dissipation efficiency η greater than 31%.

A Comparative Study on the Static Recrystallization Behavior of Cold-Rolled Mg-3Al-1Zn Alloy Stimulated by Electropulse Treatment and Conventional Heat Treatment

NASA Astrophysics Data System (ADS)

Li, Xiaopei; Li, Xiaohui; Kure-Chu, Song-Zhu; Tang, Guoyi

2017-12-01

Cold-rolled AZ31 Mg alloy strips, with a reduction of 33 pct, were subjected to electropulse treatment (EPT) and conventional heat treatment (HT) to evaluate the respective influences of electropulses and temperature on the recrystallization behavior of AZ31. The highest measured temperature during the EPT (543 K) was used in HT. The electron backscattered diffraction results demonstrated that the EPT-stimulated recrystallization was completed within 8 seconds, whereas for HT, recrystallization was still far from completion even after 240 seconds. It was found that both the nucleation and grain growth of these two processes were totally different. In the EPT samples, nucleation tended to occur preferentially near extension twin boundaries and grain boundaries by continuous recrystallization, whereas in the HT samples, nucleation occurred mainly by grain boundaries bulging via discontinuous recrystallization. As grain growth proceeded, the texture intensities of the EPT samples decreased gradually and finally evolved into an obvious transverse-direction-split texture. This is likely attributable to the impact of electropulses on the boundary energy and the contribution of nonbasal dislocations; however, the basal-type textures of the HT samples were notably strengthened, which is associated with a 30 deg〈0001〉 orientation with respect to the deformed texture.

A Comparative Study on the Static Recrystallization Behavior of Cold-Rolled Mg-3Al-1Zn Alloy Stimulated by Electropulse Treatment and Conventional Heat Treatment

NASA Astrophysics Data System (ADS)

Li, Xiaopei; Li, Xiaohui; Kure-Chu, Song-Zhu; Tang, Guoyi

2018-02-01

Cold-rolled AZ31 Mg alloy strips, with a reduction of 33 pct, were subjected to electropulse treatment (EPT) and conventional heat treatment (HT) to evaluate the respective influences of electropulses and temperature on the recrystallization behavior of AZ31. The highest measured temperature during the EPT (543 K) was used in HT. The electron backscattered diffraction results demonstrated that the EPT-stimulated recrystallization was completed within 8 seconds, whereas for HT, recrystallization was still far from completion even after 240 seconds. It was found that both the nucleation and grain growth of these two processes were totally different. In the EPT samples, nucleation tended to occur preferentially near extension twin boundaries and grain boundaries by continuous recrystallization, whereas in the HT samples, nucleation occurred mainly by grain boundaries bulging via discontinuous recrystallization. As grain growth proceeded, the texture intensities of the EPT samples decreased gradually and finally evolved into an obvious transverse-direction-split texture. This is likely attributable to the impact of electropulses on the boundary energy and the contribution of nonbasal dislocations; however, the basal-type textures of the HT samples were notably strengthened, which is associated with a 30 deg〈0001〉 orientation with respect to the deformed texture.

Olivine tablets in peridotite xenoliths: Evidence for a static, foliation-producing recrystallization mechanism operative in the strained, fluid-bearing mantle

NASA Astrophysics Data System (ADS)

Špaček, Petr; Habler, Gerlinde; Krmíček, Lukáš; Libowitzky, Eugen

2014-05-01

The term "olivine tablet" is used for elongated, (sub-)idiomorphic, strain-free crystals of olivine with well developed parallel crystal faces, usually found in peridotite xenoliths. While only rarely occurring in basalt-hosted xenolith suites, such peculiar grains are relatively common in specific kimberlite-hosted peridotite xenoliths and often explained as a result of fluid-assisted recrystallization in xenoliths after their entrainment in host magma. Extremely well developed olivine tablets are common in some peridotite xenoliths from Pliocene Lutynia basanite (South Poland). These were studied in detail focusing on their crystallographic orientation and chemical composition in relation to their host grains, in order to learn more about their origin. The tablets are restricted to grain boundary regions of olivine(I) and enstatite or occur pervasively, in some cases constituting more than half of the rock volume. Together with strain-free mosaic grains they form a second generation of olivine growing at the expense of older and larger, strained olivine(I) grains. The tablets are typically 0.1-1 mm (up to 3 mm) long having typical aspect ratios of 2-3 (up to >10) and exhibit a strong shape preferred orientation at local scale or in the whole sample, in the latter case forming a distinct foliation in peridotite xenoliths. Tablet grains usually exhibit a lattice preferred orientation (LPOs) similar to the host olivine(I), suggesting that their orientation is inherited, likely by selective exaggerated growth of small grains at the margins of host grains (dynamically recrystallized grains were not observed directly). In some cases oriented growth of tablets along microcrackss, or planar sliding surfaces, is suggested by the microstructures. Traces of prominent tablet faces mostly correspond to (010) planes of tablet grains, while correlation to crystallographic orientations of host grains is poor. Compositional profiles across tablet/host grain boundaries (EMPA, long counting times) show Ca-enrichment (from 0.02-0.03 to 0.06-0.09 wt% CaO) in ≤50 μm wide rims both in tablets and host grains, and, in some cases a non-identified Al-rich phase at the grain boundary itself. However, the Ca-profiles are symmetric with respect to grain boundaries and therefore this enrichment is assumed to post-date the tablet growth, probably being linked to infiltration of components from the xenolith host magma (which is observed independently as pockets with alkali feldspar, a second generation of clinopyroxene and a third, high-Ca generation of olivine). Compositions in the cores of tablets and olivine(I) are virtually identical within the resolution of conventional EMPA. Trace element composition, analyzed by LA-ICP-MS in several tablet/host grain pairs, shows systematically and significantly higher P and Li contents in tablets relative to host grains: (P: 30-40 ppm in olivine(I) vs. 76-87 ppm in tablets; Li: 4.6-5.7 ppm in olivine(I) vs. 7.6-10.0 ppm in tablets). Preliminary polarized micro-FTIR spectra show generally low water contents in olivine, mostly below 10 ppm of H2O. The observed microstructural and compositional features suggest formation of tablets by fluid-assisted static recrystallization which took place in-situ in the upper mantle interacting with P- and Li-rich, Ca- and Fe-poor agents. This recrystallization resulted in the formation of a foliation in peridotite by parallelization of grain boundaries in recrystallized domains with the (010) plane of the original LPO pattern. Although such observations are relatively uncommon, they might document a poorly sampled but widespread process potentially important for shear localization and the acceleration of fluid migration in the mantle.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, Linyun; Mei, Zhi -Gang; Kim, Yeon Soo

A mesoscale model is developed by integrating the rate theory and phase-field models and is used to study the fission-induced recrystallization in U-7Mo alloy. The rate theory model is used to predict the dislocation density and the recrystallization nuclei density due to irradiation. The predicted fission rate and temperature dependences of the dislocation density are in good agreement with experimental measurements. This information is used as input for the multiphase phase-field model to investigate the fission-induced recrystallization kinetics. The simulated recrystallization volume fraction and bubble induced swelling agree well with experimental data. The effects of the fission rate, initial grainmore » size, and grain morphology on the recrystallization kinetics are discussed based on an analysis of recrystallization growth rate using the modified Avrami equation. Here, we conclude that the initial microstructure of the U-Mo fuels, especially the grain size, can be used to effectively control the rate of fission-induced recrystallization and therefore swelling.« less

Adaptive characterization of recrystallization kinetics in IF steel by electron backscatter diffraction.

PubMed

Kim, Dong-Kyu; Park, Won-Woong; Lee, Ho Won; Kang, Seong-Hoon; Im, Yong-Taek

2013-12-01

In this study, a rigorous methodology for quantifying recrystallization kinetics by electron backscatter diffraction is proposed in order to reduce errors associated with the operator's skill. An adaptive criterion to determine adjustable grain orientation spread depending on the recrystallization stage is proposed to better identify the recrystallized grains in the partially recrystallized microstructure. The proposed method was applied in characterizing the microstructure evolution during annealing of interstitial-free steel cold rolled to low and high true strain levels of 0.7 and 1.6, respectively. The recrystallization kinetics determined by the proposed method was found to be consistent with the standard method of Vickers microhardness. The application of the proposed method to the overall recrystallization stages showed that it can be used for the rigorous characterization of progressive microstructure evolution, especially for the severely deformed material. © 2013 The Authors Journal of Microscopy © 2013 Royal Microscopical Society.

Microstructure study of a severely plastically deformed Mg-Zn-Y alloy by application of low angle annular dark field diffraction contrast imaging.

PubMed

Basha, Dudekula Althaf; Rosalie, Julian M; Somekawa, Hidetoshi; Miyawaki, Takashi; Singh, Alok; Tsuchiya, Koichi

2016-01-01

Microstructural investigation of extremely strained samples, such as severely plastically deformed (SPD) materials, by using conventional transmission electron microscopy techniques is very challenging due to strong image contrast resulting from the high defect density. In this study, low angle annular dark field (LAADF) imaging mode of scanning transmission electron microscope (STEM) has been applied to study the microstructure of a Mg-3Zn-0.5Y (at%) alloy processed by high pressure torsion (HPT). LAADF imaging advantages for observation of twinning, grain fragmentation, nucleation of recrystallized grains and precipitation on second phase particles in the alloy processed by HPT are highlighted. By using STEM-LAADF imaging with a range of incident angles, various microstructural features have been imaged, such as nanoscale subgrain structure and recrystallization nucleation even from the thicker region of the highly strained matrix. It is shown that nucleation of recrystallized grains starts at a strain level of revolution [Formula: see text] (earlier than detected by conventional bright field imaging). Occurrence of recrystallization of grains by nucleating heterogeneously on quasicrystalline particles is also confirmed. Minimizing all strain effects by LAADF imaging facilitated grain size measurement of [Formula: see text] nm in fully recrystallized HPT specimen after [Formula: see text].

Evolution of quartz microstructure and c-axis crystallographic preferred orientation within ductilely deformed granitoids (Arolla unit, Western Alps)

NASA Astrophysics Data System (ADS)

Menegon, Luca; Pennacchioni, Giorgio; Heilbronner, Renee; Pittarello, Lidia

2008-11-01

We have studied quartz microstructures and the c-axis crystallographic preferred orientations (CPOs) in four granitoid samples representative of increasing ductile shear deformation, from a weakly deformed granitoid (stage 1) to a mylonitic granitoid (stage 4). The quartz c-axis CPO measured in the mylonitic granitoid has been compared with the one observed in a fully recrystallized quartz mylonite from the same area. All the samples belong to the Austroalpine Arolla unit (Western Alps) and were deformed at greenschist facies conditions. The quartz c-axis CPO was analyzed using a U-stage and the optical orientation imaging technique. The magmatic plagioclase, forming more than 50% of the volume of the granitoid, is extensively replaced by a mica-rich aggregate even in weakly deformed samples of stage 1. These aggregates flow to form an interconnected weak matrix with increasing deformation, wrapping relatively less strained quartz grains that undergo dominantly coaxial strain. Recrystallization of quartz ranges from less than 1% in the weakly deformed granitoid to up to 85% in the mylonitic granitoid, with average grain strain of 41% and 64%, respectively. With increasing strain and recrystallization, quartz grains in the granitoids show a sequence of transient microstructures and CPOs. Crystal plastic deformation is initially accomplished by dislocation glide with limited recovery, and at 50% grain strain it results in a CPO consistent with dominantly basal < a> slip. At 60% grain strain, recrystallization is preferentially localized along shear bands, which appear to develop along former intragranular cracks, and the recrystallized grains develop a strong c-axis CPO with maxima orthogonal to the shear band boundaries and independent of the host grain orientation. Within the granitoid mylonite, at an average quartz grain strain of 64%, recrystallization is extensive and the c-axis CPO of new grains displays maxima overlapping the host c-axis orientation and, therefore, unrelated to the bulk sense of shear. The host-controlled CPO is inferred to reflect pervasive recrystallization by progressive subgrain rotation. The switch from 'shear band-control' to 'host-control' on c-axis CPO occurred between 40% and 70% of recrystallization. In the quartz mylonite, the quartz c-axis CPO develops an asymmetric single girdle consistent with the bulk sense of shear and the synkinematic greenschist facies conditions. This study indicates that the CPO evolution of quartz may significantly differ in cases of polymineralic vs. monomineralic rocks under the same deformation conditions, if quartz in the polymineralic rock behaves as a 'strong' phase.

Determination of grain boundary mobility during recrystallization by statistical evaluation of electron backscatter diffraction measurements

DOE Office of Scientific and Technical Information (OSTI.GOV)

Basu, I., E-mail: basu@imm.rwth-aachen.de; Chen, M.; Loeck, M.

One of the key aspects influencing microstructural design pathways in metallic systems is grain boundary motion. The present work introduces a method by means of which direct measurement of grain boundary mobility vs. misorientation dependence is made possible. The technique utilizes datasets acquired by means of serial electron backscatter diffraction (EBSD) measurements. The experimental EBSD measurements are collectively analyzed, whereby datasets were used to obtain grain boundary mobility and grain aspect ratio with respect to grain boundary misorientation. The proposed method is further validated using cellular automata (CA) simulations. Single crystal aluminium was cold rolled and scratched in order tomore » nucleate random orientations. Subsequent annealing at 300 °C resulted in grains growing, in the direction normal to the scratch, into a single deformed orientation. Growth selection was observed, wherein the boundaries with misorientations close to Σ7 CSL orientation relationship (38° 〈111〉) migrated considerably faster. The obtained boundary mobility distribution exhibited a non-monotonic behavior with a maximum corresponding to misorientation of 38° ± 2° about 〈111〉 axes ± 4°, which was 10–100 times higher than the mobility values of random high angle boundaries. Correlation with the grain aspect ratio values indicated a strong growth anisotropy displayed by the fast growing grains. The observations have been discussed in terms of the influence of grain boundary character on grain boundary motion during recrystallization. - Highlights: • Statistical microstructure method to measure grain boundary mobility during recrystallization • Method implementation independent of material or crystal structure • Mobility of the Σ7 boundaries in 5N Al was calculated as 4.7 × 10{sup –8} m{sup 4}/J ⋅ s. • Pronounced growth selection in the recrystallizing nuclei in Al • Boundary mobility values during recrystallization 2–3 orders of magnitude larger vis-à-vis curvature driven motion.« less

Mesoscale model for fission-induced recrystallization in U-7Mo alloy

DOE PAGES

Liang, Linyun; Mei, Zhi -Gang; Kim, Yeon Soo; ...

2016-08-09

A mesoscale model is developed by integrating the rate theory and phase-field models and is used to study the fission-induced recrystallization in U-7Mo alloy. The rate theory model is used to predict the dislocation density and the recrystallization nuclei density due to irradiation. The predicted fission rate and temperature dependences of the dislocation density are in good agreement with experimental measurements. This information is used as input for the multiphase phase-field model to investigate the fission-induced recrystallization kinetics. The simulated recrystallization volume fraction and bubble induced swelling agree well with experimental data. The effects of the fission rate, initial grainmore » size, and grain morphology on the recrystallization kinetics are discussed based on an analysis of recrystallization growth rate using the modified Avrami equation. Here, we conclude that the initial microstructure of the U-Mo fuels, especially the grain size, can be used to effectively control the rate of fission-induced recrystallization and therefore swelling.« less

Microstructure evolution and texture development in a friction stir-processed AISI D2 tool steel

NASA Astrophysics Data System (ADS)

Yasavol, N.; Abdollah-zadeh, A.; Vieira, M. T.; Jafarian, H. R.

2014-02-01

Crystallographic texture developments during friction stir processing (FSP) of AISI D2 tool were studied with respect to grain sizes in different tool rotation rates. Comparison of the grain sizes in various rotation rates confirmed that grain refinement occurred progressively in higher rotation rates by severe plastic deformation. It was found that the predominant mechanism during FSP should be dynamic recovery (DRV) happened concurrently with continuous dynamic recrystallization (CDRX) caused by particle-stimulated nucleation (PSN). The developed shear texture relates to the ideal shear textures of D1 and D2 in bcc metals. The prevalence of highly dense arrangement of close-packed planes of bcc and the lowest Taylor factor showed the lowest compressive residual stress which is responsible for better mechanical properties compared with the grain-precipitate refinement.

The influence of gamma prime on the recrystallization of an oxide dispersion strengthened superalloy - MA 6000E

NASA Technical Reports Server (NTRS)

Hotzler, R. K.; Glasgow, T. K.

1982-01-01

The requirement of large, recrystallized, highly elongated grains is of primary importance to the development of suitable high temperature properties in oxide dispersion strengthened-superalloys. In the present study the recrystallization behavior of MA 6000E, a recently developed Y2O3 strengthened superalloy produced by mechanical alloying, was examined using transmission and replication microscopy. Gradient and isothermal annealing treatments were applied to extruded and hot rolled products. It was found that conversion from a very fine (0.2 micron) grain structure to a coarse (approximately 10 mm) grain structure is controlled by the dissolution of the gamma prime phase, while grain shape was controlled primarily by the thermal gradient. The fine uniform oxide dispersion appeared to have only a secondary influence in determining the grain shape as columnar grains could be grown transverse to the working direction by appropriate application of the thermal gradient.

Hot Ductility Characterization of Sanicro-28 Super-Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Mirzaei, A.; Zarei-Hanzaki, A.; Abedi, H. R.

2016-05-01

The hot ductility behavior of a super-austenitic stainless steel has been studied using tensile testing method in the temperature range from 1073 K to 1373 K (800 °C to 1100 °C) under the strain rates of 0.1, 0.01, and 0.001 s-1. The hot compression tests were also performed at the same deformation condition to identify the activated restoration mechanisms. At lower temperatures [ i.e., 1073 K and 1173 K (800 °C and 900 °C)], the serration of initial grain boundaries confirms the occurrence of dynamic recovery as the predominant restoration process. However, in the course of applied deformation, the initial microstructure is recrystallized at higher temperatures [ i.e., 1273 K and 1373 K (1000 °C and 1100 °C)]. In this respect, annealing the twin boundaries could well stimulate the recrystallization kinetic through initiation new annealing twins on prior annealing twin boundaries. The hot tensile results show that there is a general trend of increasing ductility by temperature. However, two regions of ductility drop are recognized at 1273 K and 1373 K (1000°C)/0.1s-1 and (1100°C)/0.01s-1. The ductility variations at different conditions of temperature and strain rate are discussed in terms of simultaneous activation of grain boundary sliding and restoration processes. The observed ductility troughs are attributed to the occurrence of grain boundary sliding and the resulting R-type and W-type cracks. The occurrence of dynamic recrystallization is also considered as the main factor increasing the ductility at higher temperatures. The enhanced ductility is primarily originated from the post-uniform elongation behavior, which is directly associated with the strain rate sensitivity of the experimental material.

Grain Cluster Microstructure and Grain Boundary Character Distribution in Alloy 690

NASA Astrophysics Data System (ADS)

Xia, Shuang; Zhou, Bangxin; Chen, Wenjue

2009-12-01

The effects of thermal-mechanical processing (TMP) on microstructure evolution during recrystallization and grain boundary character distribution (GBCD) in aged Alloy 690 were investigated by the electron backscatter diffraction (EBSD) technique and optical microscopy. The original grain boundaries of the deformed microstructure did not play an important role in the manipulation of the proportion of the Σ3 n ( n = 1, 2, 3…) type boundaries. Instead, the grain cluster formed by multiple twinning starting from a single nucleus during recrystallization was the key microstructural feature affecting the GBCD. All of the grains in this kind of cluster had Σ3 n mutual misorientations regardless of whether they were adjacent. A large grain cluster containing 91 grains was found in the sample after a small-strain (5 pct) and a high-temperature (1100 °C) recrystallization anneal, and twin relationships up to the ninth generation (Σ39) were found in this cluster. The ratio of cluster size over grain size (including all types of boundaries as defining individual grains) dictated the proportion of Σ3 n boundaries.

Influence of CdTe Deposition Temperature and Window Thickness on CdTe Grain Size and Lifetime After CdCl 2 Recrystallization

DOE PAGES

Amarasinghe, Mahisha; Colegrove, Eric; Moutinho, Helio; ...

2018-01-23

Grain structure influences both transport and recombination in CdTe solar cells. Larger grains generally are obtained with higher deposition temperatures, but commercially it is important to avoid softening soda-lime glass. Furthermore, depositing at lower temperatures can enable different substrates and reduced cost in the future. We examine how initial deposition temperatures and morphology influence grain size and lifetime after CdCl 2 recrystallization. Techniques are developed to estimate grain distribution quickly with low-cost optical microscopy, which compares well with electron backscatter diffraction data providing corroborative assessments of exposed CdTe grain structures. Average grain size increases as a function of CdCl 2more » temperature. For lower temperature close-spaced sublimation CdTe depositions, there can be more stress and grain segregation during recrystallization. However, the resulting lifetimes and grain sizes are similar to high-temperature CdTe depositions. The grain structures and lifetimes are largely independent of the presence and/or interdiffusion of Se at the interface, before and after the CdCl 2 treatment.« less

Influence of CdTe Deposition Temperature and Window Thickness on CdTe Grain Size and Lifetime After CdCl 2 Recrystallization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Amarasinghe, Mahisha; Colegrove, Eric; Moutinho, Helio

Grain structure influences both transport and recombination in CdTe solar cells. Larger grains generally are obtained with higher deposition temperatures, but commercially it is important to avoid softening soda-lime glass. Furthermore, depositing at lower temperatures can enable different substrates and reduced cost in the future. We examine how initial deposition temperatures and morphology influence grain size and lifetime after CdCl 2 recrystallization. Techniques are developed to estimate grain distribution quickly with low-cost optical microscopy, which compares well with electron backscatter diffraction data providing corroborative assessments of exposed CdTe grain structures. Average grain size increases as a function of CdCl 2more » temperature. For lower temperature close-spaced sublimation CdTe depositions, there can be more stress and grain segregation during recrystallization. However, the resulting lifetimes and grain sizes are similar to high-temperature CdTe depositions. The grain structures and lifetimes are largely independent of the presence and/or interdiffusion of Se at the interface, before and after the CdCl 2 treatment.« less

The Cora Lake Shear Zone: Strain Localization in an Ultramylonitic, Deep Crustal Shear Zone, Athabasca Granulite Terrain, Western Churchill Province, Canada

NASA Astrophysics Data System (ADS)

Regan, S.; Williams, M. L.; Mahan, K. H.; Orlandini, O. F.; Jercinovic, M. J.; Leslie, S. R.; Holland, M.

2012-12-01

Ultramylonitic shear zones typically involve intense strain localization, and when developed over large regions can introduce considerable heterogeneity into the crust. The Cora Lake shear zone (CLsz) displays several 10's to 100's of meters-wide zones of ultramylonite distributed throughout its full 3-5 km mylonitized width. Detailed mapping, petrography, thermobarometry, and in-situ monazite geochronology suggest that it formed during the waning phases of granulite grade metamorphism and deformation, within one of North America's largest exposures of polydeformed lower continental crust. Anastomosing zones of ultramylonite contain recrystallized grain-sizes approaching the micron scale and might appear to suggest lower temperature mylonitization. However, feldspar and even clinopyroxene are dynamically recrystallized, and quantitative thermobarometry of syn-deformational assemblages indicate high P and T conditions ranging from 0.9 -10.6 GPa and 775-850 °C. Even at these high T's, dynamic recovery and recrystallization were extremely limited. Rocks with low modal quartz have extremely small equilibrium volumes. This is likely the result of inefficient diffusion, which is further supported by the unannealed nature of the crystals. Local carbonate veins suggests that H2O poor, CO2 rich conditions may have aided in the preservation of fine grain sizes, and may have inhibited dynamic recovery and recrystallization. The Cora Lake shear zone is interpreted to have been relatively strong and to have hardened during progressive deformation. Garnet is commonly fractured perpendicular to host rock fabric, and statically replaced by both biotite and muscovite. Pseudotachylite, with the same sense of shear, occurs in several ultramylonitized mafic granulites. Thus, cataclasis and frictional melt are interpreted to have been produced in the lower continental crust, not during later reactivation. We suggest that strengthening of rheologically stiffer lithologies led to extreme localization, and potentially earthquakes in quartz-absent hardened lithologies. Cora Lake shearing represents the culmination of a deformation trend of increasing strength, strain partitioning, and localization within a polydeformed, strengthened lower continental crust.

Unraveling Recrystallization Mechanisms Governing Texture Development from Rare-Earth Element Additions to Magnesium

NASA Astrophysics Data System (ADS)

Imandoust, Aidin; Barrett, Christopher D.; Al-Samman, Talal; Tschopp, Mark A.; Essadiqi, Elhachmi; Hort, Norbert; El Kadiri, Haitham

2018-03-01

The origin of texture components often associated with rare-earth element (REE) additions in wrought magnesium alloys is a long-standing problem in magnesium technology. While their influence on the texture is unquestionable, it is not yet clear why certain texture components, such as < 11\\bar{2}1 > ||{extrusion}{direction}, are favored over other components typically observed in traditional magnesium alloys. The objective of this research is to identify the mechanisms accountable for these RE textures during early stages of recrystallization. Electron backscattered diffraction and transmission electron microscopy analyses reveal that REEs in zinc-containing magnesium alloys corroborate discontinuous dynamic recrystallization. REEs promote isotropic growth for all nuclei generated through the bulging mechanism. During nucleation, the effect of REEs on orientation selection was explained by the diversified activity of both < 10\\bar{1}0 > and [0001] Taylor axes in the same grain with a marked preference for [0001] rotations to occur first. During nuclei growth, no growth preference was observed when sufficient REEs are added in the zinc-containing magnesium alloys, instead isotropic nuclei growth across all grain orientations occurs. This phenomenon is attributed to REEs segregating to grain boundaries (GBs), in agreement with prior computational and theoretical results (Barrett et al., Scripta Mater 146:46-50, 2018) that show a more isotropic GB energy and mobility after segregation.

Microstructural characterization in dissimilar friction stir welding between 304 stainless steel and st37 steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jafarzadegan, M.; State Key Laboratory of Advanced Welding Production Technology, School of Materials Science and Eng., Harbin Institute of Technology, P.O. Box: 150001, Harbin; Feng, A.H.

2012-12-15

In the present study, 3 mm-thick plates of 304 stainless steel and st37 steel were welded together by friction stir welding at a welding speed of 50 mm/min and tool rotational speed of 400 and 800 rpm. X-ray diffraction test was carried out to study the phases which might be formed in the welds. Metallographic examinations, and tensile and microhardness tests were used to analyze the microstructure and mechanical properties of the joint. Four different zones were found in the weld area except the base metals. In the stir zone of the 304 stainless steel, a refined grain structure withmore » some features of dynamic recrystallization was evidenced. A thermomechanically-affected zone was characterized on the 304 steel side with features of dynamic recovery. In the other side of the stir zone, the hot deformation of the st37 steel in the austenite region produced small austenite grains and these grains transformed to fine ferrite and pearlite and some products of displacive transformations such as Widmanstatten ferrite and martensite by cooling the material after friction stir welding. The heat-affected zone in the st37 steel side showed partially and fully refined microstructures like fusion welding processes. The recrystallization in the 304 steel and the transformations in the st37 steel enhanced the hardness of the weld area and therefore, improved the tensile properties of the joint. - Highlights: Black-Right-Pointing-Pointer FSW produced sound welds between st37 low carbon steel and 304 stainless steel. Black-Right-Pointing-Pointer The SZ of the st37 steel contained some products of allotropic transformation. Black-Right-Pointing-Pointer The material in the SZ of the 304 steel showed features of dynamic recrystallization. Black-Right-Pointing-Pointer The finer microstructure in the SZ increased the hardness and tensile strength.« less

Deformation Enhanced Recrystallization of Titanite: Insight from the Western Gneiss Region Ultrahigh-Pressure Terrane

NASA Astrophysics Data System (ADS)

Gordon, S. M.; Reddy, S. M.; Blatchford, H.; Whitney, D. L.; Kirkland, C. L.; Teyssier, C.; Evans, N. J.; McDonald, B.

2017-12-01

Titanite readily recrystallizes due to metamorphism, deformation, and/or fluids making it an ideal chronometer for tracking the exhumation of high-grade rocks. The Western Gneiss Region (WGR), Norway, is a giant UHP terrane exhumed as a fairly coherent slab. Parts of the WGR underwent little deformation during exhumation; however, meters-scale shear zones, located across the WGR, deformed over a range of pressures, from (U)HP to amphibolite facies. Titanite from quartzofeldpathic gneiss within, directly adjacent to, and 300 m away from a mylonitic shear zone within the southern WGR have been analyzed to track exhumation and investigate effects of deformation on recrystallization and trace-element mobility. EBSD was used to characterize the microstructural evolution of the gneisses, and trace-element concentrations and timing of recrystallization were estimated by split-stream LA-ICPMS. Titanite grain size decreases from outside (>200) to inside (<75 µm) the shear zone. Gneiss in and directly adjacent to the shear zone contain partially to completely recrystallized grains, with 207-corrected 206Pb/238U ages of <405 Ma. Gneiss within the shear zone shows a greater percentage of recrystallized grains. EBSD data indicate that some titanite comprises multiple subgrains within an optically coherent single grain. Subgrains in titanite cores show evidence of inherited radiogenic Pb, whereas subgrains in rims and tails of deformed sigma grains were recrystallized. In a gneiss directly adjacent to the shear zone, optically coherent grains are zoned, with increasing Sr and decreasing Zr from core to rim; titanite subgrains within the shear-zone gneiss are too small to analyze. In comparison, titanite from the gneiss outside the shear zone does not show any internal microstructures or evidence for Scandian recrystallization and has low U and high 204Pb. These results show that most trace elements are unaffected by deformation of titanite; however, Pb is mobile. Deformation thus plays an important role in resetting U-Pb systematics and allows the timing of shear zone development to be linked to the early stages of eclogite exhumation at ca. 405 Ma. Atom-probe analyses of adjacent subgrains, one that has recrystallized and one with an inherited age, will provide insight into trace-element mobility on the nm-scale.

[Comporison Sduty of Microstructure by Metallographicalk on the Polarized Light and Texture by XRD of CC 5083 and CC 5182 Aluminium Alloy after Cold Rolling and Recrystallization].

PubMed

Chen, Ming-biao; Li, Yong-wei; Tan, Yuan-biao; Ma, Min; Wang, Xue-min; Liu, Wen-chang

2015-03-01

At present the study of relation between microstructure, texture and performance of CC 5083 aluminium alloy after cold tolling and recrystallization processes is still finitude. So that the use of the CC 5083 aluminium alloy be influenced. Be cased into electrical furnace, hot up with unlimited speed followed the furnace hot up to different temperature and annealed 2h respectively, and be cased into salt-beth furnace, hot up quickly to different temperature and annealed 30 min respectively for CC 5083 and CC 5182 aluminum alloy after cold roling with 91.5% reduction. The microstructure be watched use metallographic microscope, the texture be inspected by XRD. The start temperature of recrystallization and grain grow up temperature within annealing in the electric furnace of CC 5083 aluminum alloy board is 343 degrees C, and the shap of grain after grow up with long strip (the innovation point ); The start temperature of recrystallization within annealling in the salt bath furnace of CC 5083 is 343 degrees C. The start temperature and end temperature of recrystallization within annealling of CC 5083 and CC 5182 aluminum alloy is 371 degrees C. The grain grow up outstanding of cold rooled CC 5152 aluminum alloy after annealed with 454 degrees C in the electric furnace and salt bath furnace. The start temperature of grain grow up of CC 5083 alluminurn alloy annealed in the electric furnace and salt bath furnace respectively is higher than the start temperature of grain grow up of CC 5182 alluminum alloy annealed in the electric furnace and salt bath furnace respectively. The strat temperature of recrystallization grain grow up is higher than which annealled with other three manner annealing process. The recrystallization temperature of CC 5182 annealed in the salt bath furnace is higher than which annealed in the electric furnace. The recrystallization temperature of the surface layer of CC 5083 and CC 5182 aluminum alloy is higher than the inner layer (the innovation point). There is a difference each other of the structure and the texture of the four manner annealing aluminum alloy (the innovation point). There is a little difference at the recrystallization processes course reflectived by the observe results of structure transform and by the examination results of texture transmission.

Deformation Enhanced Recrystallization of Titanite: Insight from the Western Gneiss Region Ultrahigh-Pressure Terrane

NASA Astrophysics Data System (ADS)

Gordon, S. M.; Reddy, S. M.; Blatchford, H.; Whitney, D. L.; Kirkland, C. L.; Teyssier, C.; Evans, N. J.; McDonald, B.

2016-12-01

Titanite readily recrystallizes due to metamorphism, deformation, and/or fluids making it an ideal chronometer for tracking the exhumation of high-grade rocks. The Western Gneiss Region (WGR), Norway, is a giant UHP terrane exhumed as a fairly coherent slab. Parts of the WGR underwent little deformation during exhumation; however, meters-scale shear zones, located across the WGR, deformed over a range of pressures, from (U)HP to amphibolite facies. Titanite from quartzofeldpathic gneiss within, directly adjacent to, and 300 m away from a mylonitic shear zone within the southern WGR have been analyzed to track exhumation and investigate effects of deformation on recrystallization and trace-element mobility. EBSD was used to characterize the microstructural evolution of the gneisses, and trace-element concentrations and timing of recrystallization were estimated by split-stream LA-ICPMS. Titanite grain size decreases from outside (>200) to inside (<75 µm) the shear zone. Gneiss in and directly adjacent to the shear zone contain partially to completely recrystallized grains, with 207-corrected 206Pb/238U ages of <405 Ma. Gneiss within the shear zone shows a greater percentage of recrystallized grains. EBSD data indicate that some titanite comprises multiple subgrains within an optically coherent single grain. Subgrains in titanite cores show evidence of inherited radiogenic Pb, whereas subgrains in rims and tails of deformed sigma grains were recrystallized. In a gneiss directly adjacent to the shear zone, optically coherent grains are zoned, with increasing Sr and decreasing Zr from core to rim; titanite subgrains within the shear-zone gneiss are too small to analyze. In comparison, titanite from the gneiss outside the shear zone does not show any internal microstructures or evidence for Scandian recrystallization and has low U and high 204Pb. These results show that most trace elements are unaffected by deformation of titanite; however, Pb is mobile. Deformation thus plays an important role in resetting U-Pb systematics and allows the timing of shear zone development to be linked to the early stages of eclogite exhumation at ca. 405 Ma. Atom-probe analyses of adjacent subgrains, one that has recrystallized and one with an inherited age, will provide insight into trace-element mobility on the nm-scale.

Fabric and texture at Siple Dome, Antarctica

USGS Publications Warehouse

Diprinzio, C.L.; Wilen, Lawrence A.; Alley, R.B.; Fitzpatrick, J.J.; Spencer, M.K.; Gow, A.J.

2005-01-01

Preferred c-axis orientations are present in the firn at Siple Dome, West Antarctica, and recrystallization begins as shallow as 200 m depth in ice below -20??C, based on digital analysis of c-axis fabrics, grain-sizes and other characteristics of 52 vertical thin sections prepared in the field from the kilometer-long Siple Dome ice core. The shallowest section analyzed, from 22 m, shows clustering of c axes toward the vertical. By 200 m depth, girdle fabric and other features of recrystallized ice are evident in layers (or regions), separated by layers (regions) of typically finer-grained ice lacking evidence of recrystallization. Ice from about 700-780 m depth, which was deposited during the last ice age, is especially fine-grained, with strongly vertical c axes, but deeper ice shows much larger crystals and strong evidence of recrystallization. Azimuthal asymmetry of some c-axis fabrics, trends in grain-size, and other indicators reveal additional information on processes and history of ice flow at Siple Dome.

Effects of Laves phase particles on recovery and recrystallization behaviors of Nb-containing FeCrAl alloys

DOE PAGES

Sun, Zhiqian; Edmondson, Philip D.; Yamamoto, Yukinori

2017-11-15

The microstructures and mechanical properties of deformed and annealed Nb-containing FeCrAl alloys were investigated. Fine dispersion of Fe 2Nb-type Laves phase particles was observed in the bcc-Fe matrix after applying a thermomechanical treatment, especially along grain/subgrain boundaries, which effectively stabilized the recovered and recrystallized microstructures compared with the Nb-free FeCrAl alloy. The stability of recovered areas increased with Nb content up to 1 wt%. The recrystallized grain structure in Nb-containing FeCrAl alloys consisted of elongated grains along the rolling direction with a weak texture when annealed below 1100 °C. An abnormal relationship between recrystallized grain size and annealing temperature wasmore » found. Microstructural inhomogeneity in the deformed and annealed states was explained based on the Taylor factor. Annealed Nb-containing FeCrAl alloys showed a good combination of strength and ductility, which is desirable for their application as fuel cladding in light-water reactors.« less

Reinforcement of the Cube texture during recrystallization of a 1050 aluminum alloy partially recrystallized and 10% cold-rolled

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang Wei; Helbert, Anne-Laure, E-mail: anne-laure.helbert@u-psud.fr; Baudin, Thierry

In high purity Aluminum, very strong {l_brace}100{r_brace}<001> recrystallization texture is developed after 98% cold rolling and annealing at 500 Degree-Sign C. On the contrary, in Aluminum alloys of commercial purity, the Cube component hardly exceeds 30% after complete recrystallization. Parameters controlling Cube orientation development are mainly the solute dragging due to impurities in solid solution and the stored deformation energy. In the present study, besides the 85% cold rolling, two extra annealings and a slight cold rolling are introduced in the processing route to increase the Cube volume fraction. The Cube development was analyzed by X-ray diffraction and Electron BackScatteredmore » Diffraction (EBSD). The nucleation and growth mechanisms responsible for the large Cube growth were investigated using FEG/EBSD in-situ heating experiments. Continuous recrystallization was observed in Cube oriented grains and competed with SIBM (Strain Induced Boundary Migration) mechanism. This latter was favored by the stored energy gap introduced during the additional cold-rolling between the Cube grains and their neighbors. Finally, a Cube volume fraction of 65% was reached after final recrystallization. - Highlights: Black-Right-Pointing-Pointer EBSD in-situ heating experiments of aluminum alloy of commercial purity. Black-Right-Pointing-Pointer A 10% cold-rolling after a partial recrystallization improved Cube nucleation and growth. Black-Right-Pointing-Pointer Annealing before cold-rolling limited the solute drag effect and permitted a large Cube growth. Black-Right-Pointing-Pointer Cube development is enhanced by continuous recrystallization of Cube sub-grains. Black-Right-Pointing-Pointer The preferential Cube growth occurs by SIBM of small Cube grains.« less

Imaging Water in Deformed Quartzites: Examples from Caledonian and Himalayan Shear Zones

NASA Astrophysics Data System (ADS)

Kronenberg, Andreas; Ashley, Kyle; Hasnan, Hasnor; Holyoke, Caleb; Jezek, Lynna; Law, Richard; Thomas, Jay

2016-04-01

Infrared IR measurements of OH absorption bands due to water in deformed quartz grains have been collected from major shear zones of the Caledonian and Himalayan orogens. Mean intragranular water contents were determined from the magnitude of the broad OH absorption at 3400 cm-1 as a function of structural position, averaging over multiple grains, using an IR microscope coupled to a conventional FTIR spectrometer with apertures of 50-100 μm. Images of water content were generated by scanning areas of up to 4 mm2 of individual specimens with a 10 μm synchrotron-generated IR beam and contouring OH absorptions. Water contents vary with structural level relative to the central cores of shear zones and they vary at the grain scale corresponding to deformation and recrystallization microstructures. Gradients in quartz water content expressed over structural distances of 10 to 400 m from the centers of the Moine Thrust (Stack of Glencoul, NW Scotland), the Main Central Thrust (Sutlej valley of NW India), and the South Tibetan Detachment System (Rongbuk valley north of Mount Everest) indicate that these shear zones functioned as fluid conduits. However, the gradients differ substantially: in some cases, enhanced fluid fluxes appear to have increased quartz water contents, while in others, they served to decrease water contents. Water contents of Moine thrust quartzites appear to have been reduced during shear at greenschist facies by processes of regime II BLG/SGR dislocation creep. Intragranular water contents of the protolith 70 m below the central fault core are large (4078 ± 247 ppm, H/106 Si) while mylonites within 5 mm of the Moine hanging wall rocks have water contents of only 1570 (± 229) ppm. Water contents between these extremes vary systematically with structural level and correlate inversely with the extent of dynamic recrystallization (20 to 100%). Quartz intragranular water contents of Himalayan thrust and low-angle detachment zones sheared at upper amphibolite conditions by regime III GBM creep show varying trends with structural level. Water contents increase toward the Lhotse detachment of the Rongbuk valley, reaching 11,350 (± 1095) ppm, whereas they decrease toward the Main Central Thrust exposed in the western part of the Sutlej valley to values as low as 170 (± 25) ppm. Maps of intragranular water content correspond to populations of fluid inclusions, which depend on the history of deformation and dynamic recrystallization. Increases in water content require the introduction of secondary fluid inclusions, generally by brittle microcracking followed by crack healing and processes of inclusion redistribution documented in milky quartz experiments. Decreases in water content result from dynamic recrystallization, as mobile grain boundaries sweep through wet porphyroclasts, leaving behind dry recrystallized grains. Intragranular water contents throughout greenschist mylonites of the Moine thrust are comparable to those of quartz weakened by water in laboratory experiments. However, water contents of upper amphibolite mylonites of the Main Central Thrust are far below those required for water weakening at experimental strain rates and offer challenges to our understanding of quartz rheology.

Deformation Behavior and Microstructure Evolution of As-Cast 42CrMo Alloy in Isothermal and Non-isothermal Compression

NASA Astrophysics Data System (ADS)

Qin, Fangcheng; Li, Yongtang; Qi, Huiping; Lv, Zhenhua

2016-11-01

The isothermal and non-isothermal multi-pass compression tests of centrifugal casting 42CrMo steel were conducted on a Gleeble-3500 thermal simulation machine. The effects of compression passes and finishing temperatures on deformation behavior and microstructure evolution were investigated. It is found that the microstructure is homogeneous with equiaxed grains, and the flow stress does not show significant change with the increase in passes, while the peak softening coefficient increases first and then decreases during inter-pass. Moreover, the dominant mechanisms of controlled temperature and accumulated static recrystallization for grain refinement and its homogeneous distribution are found after 5 passes deformation. As the finishing temperature increases, the flow stress decreases gradually, but the dynamic recrystallization accelerates and softening effect increases, resulting in the larger grain size and homogeneous microstructure. The microhardness decreases sharply because the sufficient softening occurs in microstructure. When the finishing temperature is 890 °C, the carbide particles are precipitated in the vicinity of the grain boundaries, thus inhibiting the dislocation motion. Thus, the higher finishing temperature (≥970 °C) for centrifugal casting 42CrMo alloy should be avoided in non-isothermal multi-pass deformation, which is beneficial to grain refinement and properties improvement.

Microstructure and yield strength effects on hydrogen and tritium induced cracking in HERF (high-energy-rate-forged) stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morgan, M J; Tosten, M H

1989-01-01

Rising-load J-integral measurements and falling-load threshold stress intensity measurements were used to characterize hydrogen and tritium induced cracking in high-energy-rate-forged (HERF) 21-6-9 stainless steel. Samples having yield strengths in the range 517--930 MPa were thermally charged with either hydrogen or tritium and tested at room temperature in either air or high-pressure hydrogen gas. In general, the hydrogen isotopes reduced the fracture toughness by affecting the fracture process. Static recrystallization in the HERF microstructures affected the material's fracture toughness and its relative susceptibility to hydrogen and tritium induced fracture. In hydrogen-exposed samples, the reduction in fracture toughness was primarily dependent onmore » the susceptibility of the microstructure to intergranular fracture and only secondarily affected by strength in the range of 660 to 930 MPa. Transmission-electron microscopy observations revealed that the microstructures least susceptible to hydrogen-induced intergranular cracking contained patches of fully recrystallized grains. These grains are surrounded by highly deformed regions containing a high number density of dislocations. The microstructure can best be characterized as duplex'', with soft recrystallized grains embedded in a hard, deformed matrix. The microstructures most susceptible to hydrogen-induced intergranular fracture showed no well-developed recrystallized grains. The patches of recrystallized grains seemed to act as crack barriers to hydrogen-induced intergranular fracture. In tritium-exposed-and-aged samples, the amount of static recrystallization also affected the fracture toughness properties but to a lesser degree. 7 refs., 25 figs.« less

Investigation on temporal evolution of the grain refinement in copper under high strain rate loading via in-situ synchrotron measurement and predictive modeling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shah, Pooja Nitin; Shin, Yung C.; Sun, Tao

Synchrotron X-rays are integrated with a modified Kolsky tension bar to conduct in situ tracking of the grain refinement mechanism operating during the dynamic deformation of metals. Copper with an initial average grain size of 36 μm is refined to 6.3 μm when loaded at a constant high strain rate of 1200 s -1. The synchrotron measurements revealed the temporal evolution of the grain refinement mechanism in terms of the initiation and rate of refinement throughout the loading test. A multiscale coupled probabilistic cellular automata based recrystallization model has been developed to predict the microstructural evolution occurring during dynamic deformationmore » processes. The model accurately predicts the initiation of the grain refinement mechanism with a predicted final average grain size of 2.4 μm. As a result, the model also accurately predicts the temporal evolution in terms of the initiation and extent of refinement when compared with the experimental results.« less

Investigation on temporal evolution of the grain refinement in copper under high strain rate loading via in-situ synchrotron measurement and predictive modeling

DOE PAGES

Shah, Pooja Nitin; Shin, Yung C.; Sun, Tao

2017-10-03

Synchrotron X-rays are integrated with a modified Kolsky tension bar to conduct in situ tracking of the grain refinement mechanism operating during the dynamic deformation of metals. Copper with an initial average grain size of 36 μm is refined to 6.3 μm when loaded at a constant high strain rate of 1200 s -1. The synchrotron measurements revealed the temporal evolution of the grain refinement mechanism in terms of the initiation and rate of refinement throughout the loading test. A multiscale coupled probabilistic cellular automata based recrystallization model has been developed to predict the microstructural evolution occurring during dynamic deformationmore » processes. The model accurately predicts the initiation of the grain refinement mechanism with a predicted final average grain size of 2.4 μm. As a result, the model also accurately predicts the temporal evolution in terms of the initiation and extent of refinement when compared with the experimental results.« less

Effect of Scandium on the Interaction of Concurrent Precipitation and Recrystallization in Commercial AA3003 Aluminum Alloy

NASA Astrophysics Data System (ADS)

Tu, Yiyou; Qian, Huan; Zhou, Xuefeng; Jiang, Jianqing

2014-04-01

In the current study, the effect of Sc addition on the interaction of concurrent precipitation and recrystallization in commercial AA3003 aluminum alloy was investigated using optical microscopy, scanning electron microscopy, and transmission electron microscopy. In case of AA3003 alloy, which was cold rolled to a true strain of 2.20 and heated at a heating rate of 150 K/s, the onset of precipitation and ending of recrystallization are signified by the critical temperature, T C ~740 K (467 °C). There is a change in the shape of the recrystallized grains from pancake-like to equiaxed shape, as the annealing temperature increases greater than T C. In case of AA3003 alloy microalloyed with 0.4 wt pct of Sc, the high no. density precipitation of coherent Al3Sc precipitates always occurs before recrystallization because of the small nucleation barrier and high rate of decomposition. This leads to extremely coarse pancake-like recrystallization grains with high fraction of low-angle grain boundaries in the entire annealing temperature range, even at a high brazing temperature of 883 K (610 °C).

The Effects of Grain Size and Texture on Dynamic Abnormal Grain Growth in Mo

NASA Astrophysics Data System (ADS)

Noell, Philip J.; Taleff, Eric M.

2016-10-01

This is the first report of abnormal grain morphologies specific to a Mo sheet material produced from a commercial-purity arc-melted ingot. Abnormal grains initiated and grew during plastic deformation of this material at temperatures of 1793 K and 1813 K (1520 °C and 1540 °C). This abnormal grain growth during high-temperature plastic deformation is termed dynamic abnormal grain growth, DAGG. DAGG in this material readily consumes nearly all grains near the sheet center while leaving many grains near the sheet surface unconsumed. Crystallographic texture, grain size, and other microstructural features are characterized. After recrystallization, a significant through-thickness variation in crystallographic texture exists in this material but does not appear to directly influence DAGG propagation. Instead, dynamic normal grain growth, which may be influenced by texture, preferentially occurs near the sheet surface prior to DAGG. The large grains thus produced near the sheet surface inhibit the subsequent growth of the abnormal grains produced by DAGG, which preferentially consume the finer grains near the sheet center. This produces abnormal grains that span the sheet center but leave unconsumed polycrystalline microstructure near the sheet surface. Abnormal grains are preferentially oriented with the < 110rangle approximately along the tensile axis. These results provide additional new evidence that boundary curvature is the primary driving force for DAGG in Mo.

Crystallographic control and texture inheritance during mylonitization of coarse grained quartz veins

NASA Astrophysics Data System (ADS)

Ceccato, Alberto; Pennacchioni, Giorgio; Menegon, Luca; Bestmann, Michel

2017-10-01

Quartz veins within Rieserferner pluton underwent deformation during post-magmatic cooling at temperature around 450 °C. Different crystallographic orientations of cm-sized quartz vein crystals conditioned the evolution of microstructures and crystallographic preferred orientations (CPO) during vein-parallel simple shear up to high shear strains (γ ≈ 10). For γ < 2, crystals stretched to ribbons of variable aspect ratios. The highest aspect ratios resulted from {m} glide in ribbons with c-axis sub-parallel to the shear zone vorticity Y-axis. Ribbons with c-axis orthogonal to Y (XZ-type ribbons) were stronger and hardened more quickly: they show lower aspect ratios and fine (grain size 10-20 μm) recrystallization along sets of microshear zones (μSZs) exploiting crystallographic planes. Distortion of XZ-type ribbons and recrystallization preferentially exploited the slip systems with misorientation axis close to Y. New grains of μSZs initiated by subgrain rotation recrystallization (SGR) and thereupon achieved high angle misorientations by a concurrent process of heterogeneous rigid grain rotation around Y associated with the confined shear within the μSZ. Dauphiné twinning occurred pervasively, but did not play a dominant role on μSZ nucleation. Recrystallization became widespread at γ > 2 and pervasive at γ ≈ 10. Ultramylonitic quartz veins are fine grained ( 10 μm, similar to new grains of μSZ) and show a CPO banding resulting in a bulk c-axis CPO with a Y-maximum, as part of a single girdle about orthogonal to the foliation, and orientations at the pole figure periphery at moderate to high angle to the foliation. This bulk CPO derives from steady-state SGR associated with preferential activity, in the different CPO bands, of slip systems generating subgrain boundaries with misorientation axes close to Y. The CPO of individual recrystallized bands is largely inherited from the original crystallographic orientation of the ribbons (and therefore vein crystals) from which they derived. High strain and pervasive recrystallization were not enough to reset the initial crystallographic heterogeneity and this CPO memory is explained by the dominance of SGR. This contrast with experimental observation of a rapid erasure of a pristine CPO by cannibalism from grains with the most favourably oriented slip system under dominant grain boundary migration recrystallization.

Modeling ductile metals under large strain, pressure and high strain rate incorporating damage and microstructure evolution

NASA Astrophysics Data System (ADS)

Iannitti, Gianluca; Bonora, Nicola; Ruggiero, Andrew; Dichiaro, Simone

2012-03-01

In this work, a constitutive modeling that couples plasticity, grain size evolution (due to plastic deformation and dynamic recrystallization) and ductile damage has been developed. The effect of grain size on the material yield stress (Hall-Petch) and on the melting temperature has been considered. The model has been used to investigate computationally the behavior of high purity copper in dynamic tensile extrusion test (DTE). An extensive numerical simulation work, using implicit finite element code with direct integration, has been performed and the results have been compared with available experimental data. The major finding is that the proposed model is capable to predict most of the observed features such as the increase of material ductility with the decreasing average grain size, the overall number and size of fragments and the average grain size distribution in the fragment trapped into the dime.

Modeling ductile metals under large strain, pressure and high strain rates incorporating damage and microstructure evolution

NASA Astrophysics Data System (ADS)

Iannitti, Gianluca; Bonora, Nicola; Ruggiero, Andrew; Dichiaro, Simone

2011-06-01

In this work, a constitutive modeling that couples plasticity, grain size evolution (due to plastic deformation and dynamic recrystallization) and ductile damage has been developed. The effect of grain size on the material yield stress (Hall-Petch) and on the melting temperature has been considered. The model has been used to investigate computationally the behaviour of high purity copper in dynamic tensile extrusion test (DTE). An extensive numerical simulation work, using implicit finite element code with direct integration, has been performed and the results have been compared with available experimental data. The major finding is that the proposed model is capable to predict most of the observed features such as the increase of material ductility with the decreasing average grain size, the overall number and size of fragments and the average grain size distribution in the fragment trapped into the dime.

Effects of Static Recrystallization and Precipitation on Mechanical Properties of 00Cr12 Ferritic Stainless Steel

NASA Astrophysics Data System (ADS)

Shao, Yi; Liu, Chenxi; Yue, Tengxiao; Liu, Yongchang; Yan, Zesheng; Li, Huijun

2018-05-01

The 00Cr12 ferritic stainless steel samples were isothermally held at different temperatures in the range of 700 °C to 1000 °C to investigate the effect of static recrystallization and precipitation on mechanical properties, such as microhardness, tensile strength, and yield strength. The results show that the formation of the fine recrystallized grain, as well as precipitation, coarsening, and dissolution of the second-phase particles, influences the mechanical properties remarkably. The fine recrystallized grain can provide a positive grain boundary-strengthening effect in the sample under a relatively high holding temperature. Coarsening and dissolution of M23C6 result in partial depletion of precipitate hardening. In contrast, the size and number density of MX particles are almost constant, regardless of the holding temperature; therefore, it can provide a better precipitation-hardening effect.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Tingguang; Xia, Shuang, E-mail: xs@shu.edu.cn; Li, Hui

Grain boundary engineering was carried out on an aging-treated nickel based Alloy 690, which has precipitated carbides at grain boundaries. Electron backscatter diffraction technique was used to investigate the grain boundary networks. Results show that, compared with the solution-annealed samples, the aging-treated samples with pre-existing carbides at grain boundaries need longer duration or higher temperature during annealing after low-strain tensile deformation for forming high proportion of low-Σ coincidence site lattice grain boundaries (more than 75%). The reason is that the primary recrystallization is inhibited or retarded owing to that the pre-existing carbides are barriers to grain boundaries migration. - Highlights:more » • Study of GBE as function of pre-existing GB carbides, tensile strain and annealing • Recrystallization of GBE is inhibited or retarded by the pre-existing carbides. • Retained carbides after annealing show the original GB positions. • More than 80% of special GBs were formed after the modification of GBE processing. • Multiple twinning during recrystallization is the key process of GBE.« less

Cryogenic strength improvement by utilizing room-temperature deformation twinning in a partially recrystallized VCrMnFeCoNi high-entropy alloy

PubMed Central

Jo, Y. H.; Jung, S.; Choi, W. M.; Sohn, S. S.; Kim, H. S.; Lee, B. J.; Kim, N. J.; Lee, S.

2017-01-01

The excellent cryogenic tensile properties of the CrMnFeCoNi alloy are generally caused by deformation twinning, which is difficult to achieve at room temperature because of insufficient stress for twinning. Here, we induced twinning at room temperature to improve the cryogenic tensile properties of the CrMnFeCoNi alloy. Considering grain size effects on the critical stress for twinning, twins were readily formed in the coarse microstructure by cold rolling without grain refinement by hot rolling. These twins were retained by partial recrystallization and played an important role in improving strength, allowing yield strengths approaching 1 GPa. The persistent elongation up to 46% as well as the tensile strength of 1.3 GPa are attributed to additional twinning in both recrystallized and non-recrystallization regions. Our results demonstrate that non-recrystallized grains, which are generally avoided in conventional alloys because of their deleterious effect on ductility, can be useful in achieving high-strength high-entropy alloys. PMID:28604656

Manufacturing process to reduce large grain growth in zirconium alloys

DOEpatents

Rosecrans, Peter M.

1987-01-01

A method of treating cold-worked zirconium alloys to reduce large grain gth during thermal treatment at temperatures above the recrystallization temperature of the alloy comprising heating the cold-worked alloy between about 1300.degree.-1350.degree. F. for 1 to 3 hours prior to treatment above its recrystallization temperature.

Recrystallization and Grain Growth Kinetics in Binary Alpha Titanium-Aluminum Alloys

NASA Astrophysics Data System (ADS)

Trump, Anna Marie

Titanium alloys are used in a variety of important naval and aerospace applications and often undergo thermomechanical processing which leads to recrystallization and grain growth. Both of these processes have a significant impact on the mechanical properties of the material. Therefore, understanding the kinetics of these processes is crucial to being able to predict the final properties. Three alloys are studied with varying concentrations of aluminum which allows for the direct quantification of the effect of aluminum content on the kinetics of recrystallization and grain growth. Aluminum is the most common alpha stabilizing alloying element used in titanium alloys, however the effect of aluminum on these processes has not been previously studied. This work is also part of a larger Integrated Computational Materials Engineering (ICME) effort whose goal is to combine both computational and experimental efforts to develop computationally efficient models that predict materials microstructure and properties based on processing history. The static recrystallization kinetics are measured using an electron backscatter diffraction (EBSD) technique and a significant retardation in the kinetics is observed with increasing aluminum concentration. An analytical model is then used to capture these results and is able to successfully predict the effect of solute concentration on the time to 50% recrystallization. The model reveals that this solute effect is due to a combination of a decrease in grain boundary mobility and a decrease in driving force with increasing aluminum concentration. The effect of microstructural inhomogeneities is also experimentally quantified and the results are validated with a phase field model for recrystallization. These microstructural inhomogeneities explain the experimentally measured Avrami exponent, which is lower than the theoretical value calculated by the JMAK model. Similar to the effect seen in recrystallization, the addition of aluminum also significantly slows downs the grain growth kinetics. This is generally attributed to the solute drag effect due to segregation of solute atoms at the grain boundaries, however aluminum segregation is not observed in these alloys. The mechanism for this result is explained and is used to validate the prediction of an existing model for solute drag.

Evidence of multimicrometric coherent γ' precipitates in a hot-forged γ-γ' nickel-based superalloy.

PubMed

Charpagne, M-A; Vennéguès, P; Billot, T; Franchet, J-M; Bozzolo, N

2016-07-01

This paper demonstrates the existence of large γ' precipitates (several micrometres in diameter) that are coherent with their surrounding matrix grain in a commercial γ-γ' nickel-based superalloy. The use of combined energy dispersive X-ray spectrometry and electron backscattered diffraction (EBSD) analyses allowed for revealing that surprising feature, which was then confirmed by transmission electron microscopy (TEM). Coherency for such large second-phase particles is supported by a very low crystal lattice misfit between the two phases, which was confirmed thanks to X-ray diffractograms and TEM selected area electron diffraction patterns. Dynamic recrystallization of polycrystalline γ-γ' nickel-based superalloys has been extensively studied in terms of mechanisms and kinetics. As in many materials with low stacking fault energy, under forging conditions, the main softening mechanism is discontinuous dynamic recrystallization. This mechanism occurs with preferential nucleation on the grain boundaries of the deformed matrix. The latter is then being consumed by the growth of the newly formed grains of low energy and by nucleation that keeps generating new grains. In the case of sub-solvus forging, large γ' particles usually pin the migrating boundaries and thus limit grain growth to a size which is determined by the distribution of second-phase particles, in good agreement with the Smith-Zener model. Under particular circumstances, the driving force associated with the difference in stored energy between the growing grains and the matrix can be large enough that the pinning forces can be overcome, and some grains can then reach much larger grain sizes. In the latter exceptional case, some intragranular primary γ' particles can be observed, although they are almost exclusively located on grain boundaries and triple junctions otherwise. In both cases, primary precipitates have no special orientation relationship with the surrounding matrix grain(s). This paper demonstrates the existence of high fractions of large γ' precipitate (several micrometres in diameter) that are coherent with their surrounding matrix grain, in a commercial γ-γ' nickel-based superalloy. Such a configuration is very surprising, because there is apparently no reason for the coherency of such particles. © 2016 The Authors Journal of Microscopy © 2016 Royal Microscopical Society.

Effect of strain and deformation route on grain boundary characteristics and recrystallization behavior of aluminum

NASA Astrophysics Data System (ADS)

Sakai, Tetsuo; Utsunomiya, Hiroshi; Takahashi, Yasuo

2014-08-01

The effect of strain and deformation route on the recrystallization behavior of aluminum sheets has been investigated using well lubricated cold rolling and continuous equal channel angular extrusion. Three different deformation routes in plane strain corresponding to (1) simple shear, (2) compression, and (3) the combination of simple shear and compression were performed on 1100 aluminum sheet. Fixed amounts of the equivalent strain of 1.28 and 1.06 were accumulated in each route. In case of the combined deformation route, the ratio of shear strain to the total equivalent strain was varied. The recrystallized grain size was finer if the combined deformation route was employed instead of the monotonic route under the same amount of equivalent strain at either strain level. The density of high angle grain boundaries that act as nucleation sites for recrystallization was higher in materials deformed by the combined route. The orientation imaging micrographs revealed that the change in deformation route is effective for introducing a larger number of new high angle grain boundaries with relatively low misorientation angle.

Texture transition in experimentally deformed quartzite

NASA Astrophysics Data System (ADS)

Kilian, Rüdiger; Heilbronner, Renée

2017-04-01

Quartz crystallographic preferred orientations (textures), most commonly presented in the form of pole figures, are often used to infer deformation processes or conditions - despite the fact that we still do not understand fully how the different types of texture are generated. Here, we re-analyse experimentally deformed Black Hills Quartzite using EBSD maps. Samples were deformed in general shear in the dislocation creep regimes 1 to 3 at temperatures ranging from 875 to 915°C, constant shear strain rates of 1e-5/s (Heilbronner & Tullis, 2006), and resulting flow stresses of (600 MPa ≥ Tau ≥ 100 MPa). Already at low strain, a strong alignment of <11-20> in the shear plane and of {10-11} with the maximum principal stress direction is observed. [0001] pole figures of recrystallized grains in regime 1 exhibit a peripheral maximum, roughly perpendicular to the shear plane while in regime 3 two elongated maxima are formed very close to the kinematic y-direction. Regime 2 shows a mixture of these two texture types. In regime 1, dynamic recrystallization is dominated by bulging recrystallization (nucleation of new grains), and in regime 3 by subgrain rotation recrystallization. In regime 2, again a mixture of regime 1 and 3 can be observed. Texture strength increases with the amount of crystal plastic deformation and is generally the lowest for the texture type with peripheral [0001]. During crystal plastic deformation [0001] rotate towards the kinematic y-direction. The coexistence and transition from one to the other texture type is suggested to result from two different texture-forming processes. The first process is thought to be crystal plasticity by glide on various <11-20> slip systems and associated rotation of the crystal lattice, with the attractor of [0001] close to - but not exactly parallel to - the kinematic y-direction. The second process is suggested to be the growth of oriented grains during bulging recrystallization and associated (fracturing and) grain boundary sliding. The contribution of both processes results in the final texture type. The most distinctive difference of the three suites of experiments is the flow stress, decreasing from regime 1 to regime 3. Since the temperature and strain rate differences in these experiments are very small indeed, it is argued that the two end-member texture types do not indicate a temperature dependence of a slip system. Rather, they seem to depend on the flow stress and hence on the recrystallization mechanism. It remains to be tested whether this relation also holds in natural quartz mylonites where those texture types are frequently observed.

Recrystallization of polycrystalline silicon

NASA Technical Reports Server (NTRS)

Lall, C.; Kulkarni, S. B.; Graham, C. D., Jr.; Pope, D. P.

1981-01-01

Optical metallography is used to investigate the recrystallization properties of polycrystalline semiconductor-grade silicon. It is found that polycrystalline silicon recrystallizes at 1380 C in relatively short times, provided that the prior deformation is greater than 30%. For a prior deformation of about 40%, the recrystallization process is essentially complete in about 30 minutes. Silicon recrystallizes at a substantially slower rate than metals at equivalent homologous temperatures. The recrystallized grain size is insensitive to the amount of prestrain for strains in the range of 10-50%.

Role of Y-Al Oxides During Extended Recovery Process of a Ferritic ODS Alloy

NASA Astrophysics Data System (ADS)

Capdevila, C.; Pimentel, G.; Aranda, M. M.; Rementeria, R.; Dawson, K.; Urones-Garrote, E.; Tatlock, G. J.; Miller, M. K.

2015-08-01

The microstructural stability of Y-Al oxides during the recrystallization of Fe-Cr-Al oxide dispersion strengthened alloy is studied in this work. The goal is to determine the specific distribution pattern of oxides depending where they are located: in the matrix or at the grain boundaries. It was concluded that those located at the grain boundaries yielded a faster coarsening than the ones in the matrix, although no significant differences in composition and/or crystal structure were observed. However, the recrystallization heat treatment leads to the dissolution of the Y2O3 and its combination with Al to form the YAlO3 perovskite oxide particles process, mainly located at the grain boundaries. Finally, atom probe tomography analysis revealed a significant Ti build-up at the grain boundaries that might affect subsequent migration during recrystallization.

Subgrain Rotation Behavior in Sn3.0Ag0.5Cu-Sn37Pb Solder Joints During Thermal Shock

NASA Astrophysics Data System (ADS)

Han, Jing; Tan, Shihai; Guo, Fu

2018-01-01

Ball grid array (BGA) samples were soldered on a printed circuit board with Sn37Pb solder paste to investigate the recrystallization induced by subgrain rotation during thermal shock. The composition of the solder balls was Sn3.0Ag0.5Cu-Sn37Pb, which comprised mixed solder joints. The BGA component was cross-sectioned before thermal shock. The microstructure and grain orientations were obtained by a scanning electron microscope equipped with an electron back-scattered diffraction system. Two mixed solder joints at corners of the BGA component were selected as the subjects. The results showed that recrystallization occurred at the corner of the solder joints after 200 thermal shock cycles. The recrystallized subgrains had various new grain orientations. The newly generated grain orientations were closely related to the initial grain orientations, which indicated that different subgrain rotation behaviors could occur in one mixed solder joint with the same initial grain orientation. When the misorientation angles were very small, the rotation axes were about Sn [100], [010] and [001], as shown by analyzing the misorientation angles and subgrain rotation axes, while the subgrain rotation behavior with large misorientation angles in the solder joints was much more complicated. As Pb was contained in the solder joints and the stress was concentrated on the corner of the mixed solder joints, concaves and cracks were formed. When the adjacent recrystallized subgrains were separated, and the process of the continuous recrystallization was limited.

Effect of Prestraining of Recrystallization Temperature and Mechanical Properties of Commercial, Sintered, Wrought Molybdenum

NASA Technical Reports Server (NTRS)

Dike, Kenneth C; Long, Roger A

1953-01-01

Given three presumably identical lots of commercial, sintered, wrought molybdenum, the 1-hour recrystallization temperature of one lot remained above 2900 F by limiting the amount of effective restraining to 35 percent or less. Different recrystallization temperatures were obtained in various atmospheres, the highest in argon and the lowest in hydrogen. Metal thus fabricated and then stress-relieved possessed an ultimate tensile strength at room temperature within 10 percent of metal swaged 99 percent and also possessed equivalent ductility. At 1800 F, equivalent strength and ductility was obtained irrespective of the amount of swaging over the range of 10 to 99 percent. The amount of swaging greatly influenced the recrystallized grain size but the difference in grain size is not the major controlling factor which determines whether recrystallized molybdenum is ductile or brittle at room temperature.

Cube texture formation during the early stages of recrystallization of Al-1%wt.Mn and AA1050 aluminium alloys

NASA Astrophysics Data System (ADS)

Miszczyk, M. M.; Paul, H.

2015-08-01

The cube texture formation during primary recrystallization was analysed in plane strain deformed samples of a commercial AA1050 alloy and an Al-1%wt.Mn model alloy single crystal of the Goss{110}<001> orientation. The textures were measured with the use of X-ray diffraction and scanning electron microscopy equipped with an electron backscattered diffraction facility. After recrystallization of the Al-1%wt.Mn single crystal, the texture of the recrystallized grains was dominated by four variants of the S{123}<634> orientation. The cube grains were only sporadically detected by the SEM/EBSD system. Nevertheless, an increased density of <111> poles corresponding to the cube orientation was observed. The latter was connected with the superposition of four variants of the S{123}<634> orientation. This indicates that the cube texture after the recrystallization was a ‘compromise texture’. In the case of the recrystallized AA1050 alloy, the strong cube texture results from both the increased density of the particular <111> poles of the four variants of the S orientation and the ∼40°(∼< 111>)-type rotation. The first mechanism transforms the Sdef-oriented areas into Srex ones, whereas the second the near S-oriented, as-deformed areas into near cube-oriented grains.

Influence of Heating Rate on Ferrite Recrystallization and Austenite Formation in Cold-Rolled Microalloyed Dual-Phase Steels

NASA Astrophysics Data System (ADS)

Philippot, C.; Bellavoine, M.; Dumont, M.; Hoummada, K.; Drillet, J.; Hebert, V.; Maugis, P.

2018-01-01

Compared with other dual-phase (DP) steels, initial microstructures of cold-rolled martensite-ferrite have scarcely been investigated, even though they represent a promising industrial alternative to conventional ferrite-pearlite cold-rolled microstructures. In this study, the influence of the heating rate (over the range of 1 to 10 K/s) on the development of microstructures in a microalloyed DP steel is investigated; this includes the tempering of martensite, precipitation of microalloying elements, recrystallization, and austenite formation. This study points out the influence of the degree of ferrite recrystallization prior to the austenite formation, as well as the importance of the cementite distribution. A low heating rate giving a high degree of recrystallization, leads to the formation of coarse austenite grains that are homogenously distributed in the ferrite matrix. However, a high heating rate leading to a low recrystallization degree, results in a banded-like structure with small austenite grains surrounded by large ferrite grains. A combined approach, involving relevant multiscale microstructural characterization and modeling to rationalize the effect of the coupled processes, highlights the role of the cold-worked initial microstructure, here a martensite-ferrite mixture: recrystallization and austenite formation commence in the former martensite islands before extending in the rest of the material.

Annealing effects in plated-wire memory elements. II - Recrystallization in Permalloy films.

NASA Technical Reports Server (NTRS)

Marquardt, S. J.; Kench, J. R.

1971-01-01

Results of grain-size measurements in Permalloy platings suggest that recrystallization is possible at temperatures as low as 200 C, but that it is an extremely heterogeneous process. No worthwhile correlation was found to exist between observed grain size and magnetic dispersion in samples aged in the temperature range from 180 to 230 C. It is suggested that the magnetic aging which occurs under these conditions may be due to some other diffusion-controlled process than recrystallization; a process such as chemical homogenization is tentatively preferred.

Evolution of microstructure and grain boundary character distribution of a tin bronze annealed at different temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Huang, Weijiu; Chongqing Municipal Key Laboratory of Institutions of Higher Education for Mould Technology, Chongqing University of Technology, Chongqing 400054; Chai, Linjiang, E-mail: chailinjiang@cqut.edu.cn

2016-04-15

Specimens cut from a rolled tin bronze sheet were annealed at 400–800 °C for 1 h and evolution of their microstructures was then characterized in details by electron channeling contrast imaging and electron backscatter diffraction techniques. Particularly, statistics on special boundaries (SBs) with Σ ≤ 29 and network connectivity of random high angle boundaries (HABs) in the annealed specimens were examined to probe optimization potentials of grain boundary character distribution (GBCD) for this material. Results show that the deformed microstructure in the as-received material begins to be recrystallized when the annealing temperature increase to 500 °C and average grain sizesmore » surge with further increasing temperatures. As a result of the recrystallization, a large number of annealing twins (with Σ3 misorientation) are produced, leading to remarkably increased fractions of SBs (f{sub SBs}). Thanks to preexisting dense low angle boundaries, the majority of SBs in the 500 °C specimen with only partial recrystallization are Σ3{sub ic} (incoherent) boundaries, which effectively disrupt connectivity of random HABs network. Although the f{sub SBs} can be further increased (up to 72.5%) in specimens with full recrystallization (at higher temperatures), the Σ3{sub ic} boundaries would be replaced to some extent by Σ3{sub c} (coherent) boundaries which do not contribute directly to optimizing the GBCD. This work should be able to provide clear suggestions on applying the concept of grain boundary engineering to tin bronze alloys. - Highlights: • The rolled tin bronze begins to be recrystallized as temperature increases to 500 °C. • A lot of SBs are produced after recrystallization and the highest f{sub SBs} is 72.5%. • Partially recrystallized specimen has the optimum GBCD due to more Σ3{sub ic} boundaries. • The Σ3{sub ic} boundaries are replaced by Σ3{sub c} boundaries after full recrystallization.« less

Experimental constraints and theoretical bases for microstructural damage in plate boundary shear zones

NASA Astrophysics Data System (ADS)

Skemer, P. A.; Cross, A. J.; Bercovici, D.

2016-12-01

(Ultra)mylonites from plate boundary shear zones are characterized by severe grain-size reduction and well-mixed mineral phases. The evolution from relatively undeformed tectonite protoliths to highly deformed (ultra)mylonites via the formation of new grain and phase boundaries is described as microstructural `damage.' Microstructural damage is important for two reasons: grain-size reduction is thought to result in significant rheological weakening, while phase mixing inhibits mechanical recovery and preserves the zone of weakness to be reactivated repeatedly throughout the tectonic cycle. Grain-size reduction by dynamic recrystallization has been studied extensively in both geologic and engineered materials, yet the progressive mixing of mineral phases during high pressure/temperature shear - the other essential element of damage or mylonitization - is not well understood. In this contribution we present new experimental results and theory related to two distinct phase mixing processes. First, we describe high strain torsion experiments on calcite and anhydrite mixtures and a simple geometric mixing model related to the stretching and thinning of monophase domains. Second, we describe a grain-switching mechanism that is driven by the surface-tension driven migration of newly formed interphase triple junctions. Unlike dynamic recrystallization, which occurs at relatively small strains, both phase mixing mechanisms described here appear to require extremely large strains, a prediction that is consistent with geologic observations. These data suggest that ductile shear zones experience long, transient intervals of microstructural evolution during which rheology is not at steady state. Microstructural damage may be interpreted as the product of several interconnected physical processes, which are collectively essential to the preservation of long-lived, Earth-like plate tectonics.

Enhancing the Damping Behavior of Dilute Zn-0.3Al Alloy by Equal Channel Angular Pressing

NASA Astrophysics Data System (ADS)

Demirtas, M.; Atli, K. C.; Yanar, H.; Purcek, G.

2017-06-01

The effect of grain size on the damping capacity of a dilute Zn-0.3Al alloy was investigated. It was found that there was a critical strain value (≈1 × 10-4) below and above which damping of Zn-0.3Al showed dynamic and static/dynamic hysteresis behavior, respectively. In the dynamic hysteresis region, damping resulted from viscous sliding of phase/grain boundaries, and decreasing grain size increased the damping capacity. While the quenched sample with 100 to 250 µm grain size showed very limited damping capacity with a loss factor tanδ of less than 0.007, decreasing grain size down to 2 µm by equal channel angular pressing (ECAP) increased tanδ to 0.100 in this region. Dynamic recrystallization due to microplasticity at the sample surface was proposed as the damping mechanism for the first time in the region where the alloy showed the combined aspects of dynamic and static hysteresis damping. In this region, tanδ increased with increasing strain amplitude, and ECAPed sample showed a tanδ value of 0.256 at a strain amplitude of 2 × 10-3, the highest recorded so far in the damping capacity-related studies on ZA alloys.

Microstructural Evolution of Al-1Fe (Weight Percent) Alloy During Accumulative Continuous Extrusion Forming

NASA Astrophysics Data System (ADS)

Wang, Xiang; Guan, Ren-Guo; Tie, Di; Shang, Ying-Qiu; Jin, Hong-Mei; Li, Hong-Chao

2018-04-01

As a new microstructure refining method, accumulative continuous extrusion forming (ACEF) cannot only refine metal matrix but also refine the phases that exist in it. In order to detect the refinements of grain and second phase during the process, Al-1Fe (wt pct) alloy was processed by ACEF, and the microstructural evolution was analyzed by electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). Results revealed that the average grain size of Al-1Fe (wt pct) alloy decreased from 13 to 1.2 μm, and blocky Al3Fe phase with an average length of 300 nm was granulated to Al3Fe particle with an average diameter of 200 nm, after one pass of ACEF. Refinement of grain was attributed to continuous dynamic recrystallization (CDRX), and the granulation of Al3Fe phase included the spheroidization resulting from deformation heat and the fragmentation caused by the coupling effects of strain and thermal effect. The spheroidization worked in almost the entire deformation process, while the fragmentation required strain accumulation. However, fragmentation contributed more than spheroidization. Al3Fe particle stimulated the formation of substructure and retarded the migration of recrystallized grain boundary, but the effect of Al3Fe phase on refinement of grain could only be determined by the contrastive investigation of Al-1Fe (wt pct) alloy and pure Al.

Study of grain structure evolution during annealing of a twin-roll-cast Mg alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tripathi, A.; Department of Metallurgical Engineering and Materials Science, IIT Bombay; Department of Materials Engineering, Monash University

2016-04-15

The evolution of microstructure under static annealing was studied for mid-thickness section of a twin-roll-cast (TRC) magnesium alloy. Annealing was performed at 300 °C and 500 °C for different times. Microstructural evolution was quantitatively analyzed, from optical micrographs, using grain path envelope analysis. Additional information from electron backscatter diffraction (EBSD) was used for addressing the possible mechanism(s). It was found that the TRC structure had a bimodal grain size, which was preserved even after annealing at 300 °C. However, the annealing at 500 °C led to a unimodal grain size. This difference in the grain size distribution created a contrastingmore » behavior in the normalized standard deviations. This was primarily attributed to a competition between recovery and recrystallization, and their respective dominance at 300° and 500 °C. A deformation induced recrystallization recovery (DIRR) model was proposed. The proposed model could successfully address the experimental microstructural evolution. - Highlights: • Annealing of twin roll cast (TRC) magnesium alloy was done at temperatures of 300 °C and 500 °C. • TRC had bimodal structure. Bimodality preserved for annealing at 300 °C. Annealing at 500 °C led to unimodal structure. • Grain evolution was described based on the competition between recovery and recrystallization. • Deformation induced recrystallization recovery (DIRR) mechanistic model was developed.« less

Synthesis and deformation of a Ti doped quartz aggregate

NASA Astrophysics Data System (ADS)

Nachlas, William O.; Hirth, Greg; Teyssier, Christian; Whitney, Donna L.; Zimmerman, Mark

2013-04-01

A primary advantage of studying mylonites for thermobarometric reconstructions of tectonic events is that it enables direct comparison of P-T estimates with the mechanics of quartz deformation. Quartz is a common phase in crustal mylonites and is a particularly sensitive recorder of metamorphic and rheologic conditions in shear zones, owing to its responsiveness to dynamic recrystallization, involvement in metamorphic reaction, and propensity for dissolution and precipitation. The signature of its trace element chemistry, particularly Ti, can reflect involvement from each of these processes. The concentration of Ti in mylonites is typically heterogeneous at the thin section scale, providing a rich record of the different factors that influence the incorporation of Ti in quartz. Observations of quartz in deformed mylonite and undeformed protolith from an extensional shear zone in the North American Cordillera (Shuswap Complex, Canada) show that an originally uniform Ti distribution was modified during deformation to form zoned crystals in which the core preserves a higher Ti concentration than the rim. The zoned Ti concentration likely records a continuum of deformation conditions during extension-related exhumation, and this presents a challenge in resolving the effect of deformation on the equilibrium solubility of Ti in quartz in natural settings. By conducting deformation experiments on synthetic quartz aggregates with known Ti concentration at a constant, elevated temperature and pressure under high strain conditions, we investigate the influence of progressive dynamic recrystallization on Ti solubility in quartz. This study applies a novel doping technique that enables the synthesis of a large population of quartz crystals with a precisely controlled Ti concentration and distribution. This produces a sample that most closely replicates the protolith of extensional shear zones that typically develop under retrograde conditions. This strategy can be used to generate the equilibrium concentration predicted by previous solubility calibrations for selected P-T conditions. Experiments were performed using a shear assembly to deform quartz samples to high shear strain in dislocation creep at constant temperature, pressure, and strain rate for 24, 48, and 72 h with and without the addition of 0.1 wt% H2O. Experiments were also run under hydrostatic conditions for equivalent lengths of time for comparison with deformed samples. Experimental specimens were prepared as a two layer sample with a doped half and an undoped half to study Ti mobility during deformation. Experimental samples are analyzed with EMPA and SIMS to determine the Ti concentration of quartz in the sample, SEM-CL to observe the distribution of Ti in quartz grains, and SEM-EBSD to evaluate crystallographic fabrics and grain size. Results suggest that the duration of dynamic recrystallization influences the final Ti concentration, implying the importance of kinetics and diffusion even at the elevated temperatures of the experiments. Water content affects Ti concentration, potentially owing to the importance of point defect concentration on the solubility of Ti in quartz. Furthermore, recrystallized grain size shows a dependence on Ti concentration, as samples doped at supersaturated levels recrystallize with finer grain sizes relative to undoped samples. This suggests that exceeding the equilibrium solubility of Ti in quartz may pin grain boundary migration. The ultimate expression of Ti supersaturation in quartz is strain-induced rutilation and the progressive rotation and boudinage of exsolved rutile needles.

Infiltration of meteoric fluids in an extensional detachment shear zone (Kettle dome, WA, USA): How quartz dynamic recrystallization relates to fluid-rock interaction

NASA Astrophysics Data System (ADS)

Quilichini, Antoine; Siebenaller, Luc; Nachlas, William O.; Teyssier, Christian; Vennemann, Torsten W.; Heizler, Matthew T.; Mulch, Andreas

2015-02-01

We document the interplay between meteoric fluid flow and deformation processes in quartzite-dominated lithologies within a ductile shear zone in the footwall of a Cordilleran extensional fault (Kettle detachment system, Washington, USA). Across 150 m of shear zone section, hydrogen isotope ratios (δD) from synkinematic muscovite fish are constant (δD ˜ -130‰) and consistent with a meteoric fluid source. Quartz-muscovite oxygen isotope thermometry indicates equilibrium fractionation temperatures of ˜365 ± 30 °C in the lower part of the section, where grain-scale quartz deformation was dominated by grain boundary migration recrystallization. In the upper part of the section, muscovite shows increasing intragrain compositional zoning, and quartz microstructures reflect bulging recrystallization, solution-precipitation, and microcracking that developed during progressive cooling and exhumation. The preserved microstructural characteristics and hydrogen isotope fingerprints of meteoric fluids developed over a short time interval as indicated by consistent mica 40Ar/39Ar ages ranging between 51 and 50 Ma over the entire section. Pervasive fluid flow became increasingly channelized during detachment activity, leading to microstructural heterogeneity and large shifts in quartz δ18O values on a meter scale. Ductile deformation ended when brittle motion on the detachment fault rapidly exhumed the mylonitic footwall.

The Rheological Evolution of Brittle-Ductile Transition Rocks During the Earthquake Cycle: Evidence for a Ductile Precursor to Pseudotachylyte in an Extensional Fault System, South Mountains, Arizona

NASA Astrophysics Data System (ADS)

Stewart, Craig A.; Miranda, Elena A.

2017-12-01

We investigate how the rheological evolution of shear zone rocks from beneath the brittle-ductile transition (BDT) is affected by coeval ductile shear and pseudotachylyte development associated with seismicity during the earthquake cycle. We focus our study on footwall rocks of the South Mountains core complex, and we use electron backscatter diffraction (EBSD) analyses to examine how strain is localized in granodiorite mylonites both prior to and during pseudotachylyte development beneath the BDT. In mylonites that are host to pseudotachylytes, deformation is partitioned into quartz, where quartz exhibits crystallographic-preferred orientation patterns and microstructures indicative of dynamic recrystallization during dislocation creep. Grain size reduction during dynamic recrystallization led to the onset of grain boundary sliding (GBS) accommodated by fluid-assisted grain size-sensitive (GSS) creep, localizing strain in quartz-rich layers prior to pseudotachylyte development. The foliation-parallel zones of GBS in the host mylonites, and the presence of GBS traits in polycrystalline quartz survivor clasts indicate that GBS zones were the ductile precursors to in situ pseudotachylyte generation. During pseudotachylyte development, strain was partitioned into the melt phase, and GSS deformation in the survivor clasts continued until crystallization of melt impeded flow, inducing pseudotachylyte development in other GBS zones. We interpret the coeval pseudotachylytes with ductile precursors as evidence of seismic events near the BDT. Grain size piezometry yields high differential stresses in both host mylonites ( 160 MPa) and pseudotachylyte survivor clasts (> 200 MPa), consistent with high stresses during interseismic and coseismic phases of the earthquake cycle, respectively.

Role of Y-Al oxides during extended recovery process of a ferritic ODS alloy

DOE PAGES

Capdevila, C.; Pimentel, G.; Aranda, M. M.; ...

2015-08-04

The microstructural stability of Y-Al oxides during the recrystallization of Fe-Cr-Al oxide dispersion strengthened alloy is studied in this work. The goal is to determine the specific distribution pattern of oxides depending where they are located: in the matrix or at the grain boundaries. It was concluded that those located at the grain boundaries yielded a faster coarsening than the ones in the matrix, although no significant differences in composition and/or crystal structure were observed. However, the recrystallization heat treatment leads to the dissolution of the Y 2O 3 and its combination with Al to form the YAlO 3 perovskitemore » oxide particles process, mainly located at the grain boundaries. Lastly, atom probe tomography analysis revealed a significant Ti build-up at the grain boundaries that might affect subsequent migration during recrystallization.« less

Internal Shear Forging Processes for Missile Primary Structures.

DTIC Science & Technology

1981-07-20

received condition. The as-received micro- structure displayed elongated recrystallized grains interspersed with particles of precipitate phases. SEM...re- crystallization regime for this alloy, and rolled specimens were reheated to 3160 C between passes, some recrystallization and grain size changes...experiment revealed that the actual solution treatment temperature was probably higher than 5000C. This resulted in melting of the eutectic and solid

Feedbacks Between Deformation and Fluid Flow in Mantle Shear Zones from Zabargad, Red Sea

NASA Astrophysics Data System (ADS)

Tommasi, A.; Boudier, F. I.; Vauchez, A. R.; Zaderatzky, M.

2016-12-01

Peridotites in the Zabargad island, Red Sea, record different stages of lithospheric thinning and asthenospheric upwelling during rifting. Field mapping highlights a pervasive high-temperature NW-SE, subvertical foliation with lineations pluning 50°NW. This foliation is overprinted by a series of lower-temperature mylonitic zones with slightly oblique foliations and subhorizontal lineations, which record progressive strain localization under retrogressive conditions during the final exhumation of the peridotites (Nicolas and Boudier, JGR 1987). We performed a petrostructural study of ca. 50 samples collected by A. Nicolas and F. Boudier in the 80s from the different deformation facies. This study highlights: (1) a rather pervasive, but highly heterogeneous distribution of the LT deformation and (2) a feedback between deformation and fluid flow. The HT deformation is recorded in medium grained plagioclase- and spinel-peridotites by a homogeneous foliation and lineation marked by a shape-preferred orientation of plagioclase and olivine and a consistent CPO of all major-rock forming phases. The LT temperature deformation results in dynamic recrystallization of olivine leading to a marked grain size reduction by dynamic recrystallization of olivine, remobilization of orthopyroxene by dissolution-precipitation, and crystallization of amphibole. Increasing finite strain is recorded by the increase in the volume of the fine-grained material and of the amphibole proportion. The latter may attain in totally recrystallized cm-wide ultramylonite bands up to 30%. This together with the strong amphibole SPO and CPO corroborate fluid focusing and enhanced reaction rates into active shear zones. In the LT shear zones we also document: (1) changes in the olivine CPO, indicating changes in the dominant slip system and (2) unusual orthopyroxene CPO, which we interpret as due to oriented crystallization. Static replacement of pyroxenes by amphibole with no associated LT deformation is also observed indicating that the presence of fluids does not suffice to trigger strain localization.

Abnormal grain growth in AISI 304L stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shirdel, M., E-mail: mshirdel1989@ut.ac.ir; Mirzadeh, H., E-mail: hmirzadeh@ut.ac.ir; Advanced Metalforming and Thermomechanical Processing Laboratory, School of Metallurgy and Materials Engineering, University of Tehran, Tehran

2014-11-15

The microstructural evolution during abnormal grain growth (secondary recrystallization) in 304L stainless steel was studied in a wide range of annealing temperatures and times. At relatively low temperatures, the grain growth mode was identified as normal. However, at homologous temperatures between 0.65 (850 °C) and 0.7 (900 °C), the observed transition in grain growth mode from normal to abnormal, which was also evident from the bimodality in grain size distribution histograms, was detected to be caused by the dissolution/coarsening of carbides. The microstructural features such as dispersed carbides were characterized by optical metallography, X-ray diffraction, scanning electron microscopy, energy dispersivemore » X-ray analysis, and microhardness. Continued annealing to a long time led to the completion of secondary recrystallization and the subsequent reappearance of normal growth mode. Another instance of abnormal grain growth was observed at homologous temperatures higher than 0.8, which may be attributed to the grain boundary faceting/defaceting phenomenon. It was also found that when the size of abnormal grains reached a critical value, their size will not change too much and the grain growth behavior becomes practically stagnant. - Highlights: • Abnormal grain growth (secondary recrystallization) in AISI 304L stainless steel • Exaggerated grain growth due to dissolution/coarsening of carbides • The enrichment of carbide particles by titanium • Abnormal grain growth due to grain boundary faceting at very high temperatures • The stagnancy of abnormal grain growth by annealing beyond a critical time.« less

A re-evaluation of the mechanism of SIBM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bate, P.; Hutchinson, B.

The process for creating a new recrystallized grain by the bulging out of an existing grain boundary within the deformed structure was recognized by Beck and Sperry and described as strain induced boundary migration, often now as SIBM. For many years SIBM seemed to be accorded less significance than the subgrain growth models for nucleation of recrystallization. However, the importance of SIBM is increasingly recognized, for example in the case of cube texture development in aluminum alloys. There is increasing evidence that high angle boundaries in deformed metals are not only residues of the prior grain structure but may alsomore » be generated by the deformation itself. These also participate in the nucleation of recrystallization on annealing and must do so by some form of SIBM mechanism.« less

Microstructure and nanohardness distribution in a polycrystalline Zn deformed by high strain rate impact

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dirras, G., E-mail: dirras@univ-paris13.fr; Ouarem, A.; Couque, H.

2011-05-15

Polycrystalline Zn with an average grain size of about 300 {mu}m was deformed by direct impact Hopkinson pressure bar at a velocity of 29 m/s. An inhomogeneous grain structure was found consisting of a center region having large average grain size of 20 {mu}m surrounded by a fine-grained rim with an average grain size of 6 {mu}m. Transmission electron microscopy investigations showed a significant dislocation density in the large-grained area while in the fine-grained rim the dislocation density was negligible. Most probably, the higher strain yielded recrystallization in the outer ring while in the center only recovery occurred. The hardeningmore » effect of dislocations overwhelms the smaller grain size strengthening in the center part resulting in higher nanohardness in this region than in the outer ring. - Graphical Abstract: (a): EBSD micrograph showing the initial microstructure of polycrystalline Zn that was subsequently submitted to high strain rate impact. (b): an inhomogeneous grain size refinement was obtained which consists of a central coarse-grained area, surrounded by a fine-grained recrystallized rim. The black arrow points to the disc center. Research Highlights: {yields} A polycrystalline Zn specimen was submitted to high strain rate impact loading. {yields} Inhomogeneous grain refinement occurred due to strain gradient in impacted sample. {yields} A fine-grained recrystallized rim surrounded the coarse-grained center of specimen. {yields} The coarse-grained center exhibited higher hardness than the fine-grained rim. {yields} The higher hardness of the center was caused by the higher dislocation density.« less

Quartz grainsize evolution during dynamic recrystallization across a natural shear zone boundary

NASA Astrophysics Data System (ADS)

Xia, Haoran; Platt, John P.

2018-04-01

Although it is widely accepted that grainsize reduction by dynamic recrystallization can lead to strain localization, the details of the grainsize evolution during dynamic recrystallization remain unclear. We investigated the bulge size and grainsizes of quartz at approximately the initiation and the completion stages of bulging recrystallization across the upper boundary of a 500 m thick mylonite zone above the Vincent fault in the San Gabriel Mountains, southern California. Within uncertainty, the average bulge size of quartz, 4.7 ± 1.5 μm, is the same as the recrystallized grainsize, 4.5 ± 1.5 μm, at the incipient stage of dynamic recrystallization, and also the same within uncertainties as the recrystallized grainsize when dynamic recrystallization is largely complete, 4.7 ± 1.3 μm. These observations indicate that the recrystallized grainsize is controlled by the nucleation process and does not change afterwards. It is also consistent with the experimental finding that the quartz recrystallized grainsize paleopiezometer is independent of temperature.

Investigation of primary static recrystallization in a NiTiFe shape memory alloy subjected to cold canning compression using the coupling crystal plasticity finite element method with cellular automaton

NASA Astrophysics Data System (ADS)

Zhang, Yanqiu; Jiang, Shuyong; Hu, Li; Zhao, Yanan; Sun, Dong

2017-10-01

The behavior of primary static recrystallization (SRX) in a NiTiFe shape memory alloy (SMA) subjected to cold canning compression was investigated using the coupling crystal plasticity finite element method (CPFEM) with the cellular automaton (CA) method, where the distribution of the dislocation density and the deformed grain topology quantified by CPFEM were used as the input for the subsequent SRX simulation performed using the CA method. The simulation results were confirmed by the experimental ones in terms of microstructures, average grain size and recrystallization fraction, which indicates that the proposed coupling method is well able to describe the SRX behavior of the NiTiFe SMA. The results show that the dislocation density exhibits an inhomogeneous distribution in the deformed sample and the recrystallization nuclei mainly concentrate on zones where the dislocation density is relatively higher. An increase in the compressive deformation degree leads to an increase in nucleation rate and a decrease in grain boundary spaces in the compression direction, which reduces the growth spaces for the SRX nuclei and impedes their further growth. In addition, both the mechanisms of local grain refinement in the incomplete SRX and the influence of compressive deformation degree on the grain size of SRX were vividly illustrated by the corresponding physical models.

Analysis of soft magnetic materials by electron backscatter diffraction as a powerful tool

NASA Astrophysics Data System (ADS)

Schuller, David; Hohs, Dominic; Loeffler, Ralf; Bernthaler, Timo; Goll, Dagmar; Schneider, Gerhard

2018-04-01

The current work demonstrates that electron backscatter diffraction (EBSD) is a powerful and versatile characterization technique for investigating soft magnetic materials. The properties of soft magnets, e.g., magnetic losses strongly depend on the materials chemical composition and microstructure, including grain size and shape, texture, degree of plastic deformation and elastic strain. In electrical sheet stacks for e-motor applications, the quality of the machined edges/surfaces of each individual sheet is of special interest. Using EBSD, the influence of the punching process on the microstructure at the cutting edge is quantitatively assessed by evaluating the crystallographic misorientation distribution of the deformed grains. Using an industrial punching process, the maximum affected deformation depth is determined to be 200 - 300 μm. In the case of laser cutting, the affected deformation depth is determined to be approximately zero. Reliability and detection limits of the developed EBSD approach are evaluated on non-affected sample regions and model samples containing different indentation test bodies. A second application case is the investigation of the recrystallization process during the annealing step of soft magnetic composites (SMC) toroids produced by powder metallurgy as a function of compaction pressure, annealing parameters and powder particle size. With increasing pressure and temperature, the recrystallized area fraction (e.g., grains with crystallographic misorientations < 3°) increases from 71 % (200 MPa, 800°C) to 90% (800 MPa, 800°C). Recrystallization of the compacted powder material starts at the particle boundaries or areas with existing plastic deformation. The progress of recrystallization is visualized as a function of time and of different particle to grain size distributions. Here, large particles with coarse internal grain structures show a favorable recrystallization behavior which results in large bulk permeability of up to 600 - 700 and lower amount of residual misorientations (>3°).

Microstructures and mechanical properties of Cu-Sn alloy subjected to elevated-temperature heat deformation

NASA Astrophysics Data System (ADS)

Hui, Jun; Feng, Zaixin; Fan, Wenxin; Wang, Pengfei

2018-04-01

Cu-Sn alloy was subjected to elevated-temperature isothermal compression with 0.01 s‑1 strain rate and 500 ∼ 700 °C temperature range. The thermal compression curve reflected a competing process of work hardening versus dynamic recovery (DRV) and recrystallization, which exhibited an obvious softening trend. Meanwhile, high-temperature deformation and microstructural features in different regions of the alloy was analyzed through EBSD. The results show that grains grow as the temperature rises, competition among recrystallization, substructural, and deformation regions tends to increase with the increase of temperature, and distribution frequency of recrystallization regions gradually increases and then drops suddenly at 650 °C. At 500 ∼ 550 °C, preferentially oriented texturing phenomenon occurs, low angle boundaries(LABs) are gradually transformed into high angle boundaries (HABs) and the Σ (CSL) boundaries turn gradually into Σ3 boundaries. In tensile test of tin bronze, elongation at break increases slowly, whereas yield strength (YS) and ultimate tensile strength (TS) decrease gradually.

Solar cells with low cost substrates and process of making same

DOEpatents

Mitchell, Kim W.

1984-01-01

A solar cell having a substrate and an intermediate recrystallized film and a semiconductor material capable of absorbing light with the substrate being selected from one of a synthetic organic resin, graphite, glass and a crystalline material having a grain size less than about 1 micron.sup.2. The intermediate recrystallized film has a grain size in the range of from about 10 microns.sup.2 to about 10,000 microns.sup.2 and a lattice mismatch with the semiconductor material not greater than about 4%. The semiconductor material has a grain size not less than about 10 microns.sup.2. An anti-reflective layer and electrical contact means are provided. Also disclosed is a subcombination of substrate, intermediate recrystallized film and semiconductor material. Also, methods of formulating the solar cell and subcombination are disclosed.

Solar cells with low cost substrates, process of making same and article of manufacture

DOEpatents

Mitchell, K.W.

A solar cell is disclosed having a substrate and an intermediate recrystallized film and a semiconductor material capable of absorbing light with the substrate being selected from one of a synthetic organic resin, graphite, glass and a crystalline material having a grain size less than about 1 micron/sup 2/. The intermediate recrystallized film has a grain size in the range of from about 10 microns/sup 2/ to about 10,000 microns/sup 2/ and a lattice mismatch with the semiconductor material not greater than about 4%. The semiconductor material has a grain size not less than about 10 microns/sup 2/. An anti-reflective layer and electrical contact means are provided. Also disclosed is a subcombination of substrate, intermediate recrystallized film and semiconductor material. Also, methods of formulating the solar cell and subcombination are disclosed.

The Microstructure and Gamma Prime Distributions in Inertia Friction Welded Joint of P/M Superalloy FGH96

NASA Astrophysics Data System (ADS)

Zhang, Chi; Shen, Wenfei; Zhang, Liwen; Xia, Yingnan; Li, Ruiqin

2017-04-01

A gamma prime ( γ') precipitation ( 35% in volume)-hardened powder metallurgy (P/M) superalloy FGH96 was welded using inertia friction welding (IFW). The microstructure and γ' distributions in the joints in two conditions, hot isostatic pressed state and solution-treated and aged state, were characterized. The recrystallization of grains, the dissolution and re-precipitation of γ' in the joints were discussed in terms of the temperature evolutions which were calculated by finite element model analysis. Regardless of the initial states, fully recrystallized fine grain structure formed at welded zone. Meanwhile, very fine γ' precipitations were re-precipitated at the welded zone. These recrystallized grain structure and fine re-precipitated γ' resulted in increasing hardness of IFW joint while making the hardness dependent on the microstructure and γ' precipitation.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hu, Shenyang; Joshi, Vineet; Lavender, Curt A.

Experiments showed that recrystallization dramatically speeds up the gas bubble swelling kinetics in metallic UMo fuels. In this work a recrystallization model is developed to study the effect of microstructures and radiation conditions on recrystallization kinetics. The model integrates the rate theory of intra-granular gas bubble and interstitial loop evolution and a phase field model of recrystallization zone evolution. A fast passage method is employed to describe one dimensional diffusion of interstitials which have diffusivity several order magnitude larger than that of the fission gas Xe. With the model, the effect of grain sizes on recrystallization kinetics is simulated.

Early Stages of Microstructure and Texture Evolution during Beta Annealing of Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Pilchak, A. L.; Sargent, G. A.; Semiatin, S. L.

2018-03-01

The early stages of microstructure evolution during annealing of Ti-6Al-4V in the beta phase field were established. For this purpose, a series of short-time heat treatments was performed using sheet samples that had a noticeable degree of alpha-phase microtexture in the as-received condition. Reconstruction of the beta-grain structure from electron-backscatter-diffraction measurements of the room-temperature alpha-phase texture revealed that microstructure evolution at short times was controlled not by general grain growth, but rather by nucleation-and-growth events analogous to discontinuous recrystallization. The nuclei comprised a small subset of beta grains that were highly misoriented relative to those comprising the principal texture component of the beta matrix. From a quantitative standpoint, the transformation kinetics were characterized by an Avrami exponent of approximately unity, thus suggestive of metadynamic recrystallization. The recrystallization process led to the weakening and eventual elimination of the initial beta texture through the growth of a population of highly misoriented grains.

Recrystallization texture in nickel heavily deformed by accumulative roll bonding

NASA Astrophysics Data System (ADS)

Mishin, O. V.; Zhang, Y. B.; Godfrey, A.

2017-07-01

The recrystallization behavior of Ni processed by accumulative roll bonding to a total accumulated von Mises strain of 4.8 has been examined, and analyzed with respect to heterogeneity in the deformation microstructure. The regions near the bonding interface are found to be more refined and contain particle deformation zones around fragments of the steel wire brush used to prepare the surface for bonding. Sample-scale gradients are also observed, manifested as differences between the subsurface, intermediate and central layers, where the distributions of texture components are different. These heterogeneities affect the progress of recrystallization. While the subsurface and near-interface regions typically contain lower frequencies of cube-oriented grains than anywhere else in the sample, a strong cube texture forms in the sample during recrystallization, attributed to both a high nucleation rate and fast growth rate of cube-oriented grains. The observations highlight the sensitivity of recrystallization to heterogeneity in the deformation microstructure and demonstrate the importance of characterizing this heterogeneity over several length scales.

Improving significantly the failure strain and work hardening response of LPSO-strengthened Mg-Y-Zn-Al alloy via hot extrusion speed control

NASA Astrophysics Data System (ADS)

Tan, Xinghe; Chee, Winston; Chan, Jimmy; Kwok, Richard; Gupta, Manoj

2017-07-01

The effect of hot extrusion speed on the microstructure and mechanical properties of MgY1.06Zn0.76Al0.42 (at%) alloy strengthened by the novel long-period stacking ordered (LPSO) phase was systematically investigated. Increase in the speed of extrusion accelerated dynamic recrystallization of α-Mg via particle-stimulated nucleation and grain growth in the alloy. The intensive recrystallization and grain growth events weakened the conventional basal texture and Hall-Petch strengthening in the alloy which led to significant improvement in its failure strain from 4.9% to 19.6%. The critical strengthening contribution from LPSO phase known for attributing high strength to the alloy was observed to be greatly undermined by the parallel competition from texture weakening and the adverse Hall-Petch effect when the alloy was extruded at higher speed. Absence of work hardening interestingly observed in the alloy extruded at lower speed was discussed in terms of its ultra-fine grained microstructure which promoted the condition of steady-state defect density in the alloy; where dislocation annihilation balances out the generation of new dislocations during plastic deformation. One approach to improve work hardening response of the alloy to prevent unstable deformation and abrupt failure in service is to increase the grain diameter in the alloy by judiciously increasing the extrusion speed.

Universal scaling of grain size distributions during dislocation creep

NASA Astrophysics Data System (ADS)

Aupart, Claire; Dunkel, Kristina G.; Angheluta, Luiza; Austrheim, Håkon; Ildefonse, Benoît; Malthe-Sørenssen, Anders; Jamtveit, Bjørn

2017-04-01

Grain size distributions are major sources of information about the mechanisms involved in ductile deformation processes and are often used as paleopiezometers (stress gauges). Several factors have been claimed to influence the stress vs grain size relation, including the water content (Jung & Karato 2001), the temperature (De Bresser et al., 2001), the crystal orientation (Linckens et al., 2016), the presence of second phase particles (Doherty et al. 1997; Cross et al., 2015), and heterogeneous stress distributions (Platt & Behr 2011). However, most of the studies of paleopiezometers have been done in the laboratory under conditions different from those in natural systems. It is therefore essential to complement these studies with observations of naturally deformed rocks. We have measured olivine grain sizes in ultramafic rocks from the Leka ophiolite in Norway and from Alpine Corsica using electron backscatter diffraction (EBSD) data, and calculated the corresponding probability density functions. We compared our results with samples from other studies and localities that have formed under a wide range of stress and strain rate conditions. All distributions collapse onto one universal curve in a log-log diagram where grain sizes are normalized by the mean grain size of each sample. The curve is composed of two straight segments with distinct slopes for grains above and below the mean grain size. These observations indicate that a surprisingly simple and universal power-law scaling describes the grain size distribution in ultramafic rocks during dislocation creep irrespective of stress levels and strain rates. Cross, Andrew J., Susan Ellis, and David J. Prior. 2015. « A Phenomenological Numerical Approach for Investigating Grain Size Evolution in Ductiley Deforming Rocks ». Journal of Structural Geology 76 (juillet): 22-34. doi:10.1016/j.jsg.2015.04.001. De Bresser, J. H. P., J. H. Ter Heege, and C. J. Spiers. 2001. « Grain Size Reduction by Dynamic Recrystallization: Can It Result in Major Theological Weakening? » International Journal of Earth Sciences 90 (1): 28-45. Doherty, R. D., D. A. Hughes, F. J. Humphreys, J. J. Jonas, D. J. Jensen, M. E. Kassner, W. E. King, T. R. McNelley, H. J. McQueen, and A. D. Rollett. 1997. « Current Issues in Recrystallization: A Review ». Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 238 (2): 219-74. doi:10.1016/S0921-5093(97)00424-3. Jung, H., and S. I. Karato. 2001. « Effects of Water on Dynamically Recrystallized Grain-Size of Olivine ». Journal of Structural Geology 23 (9): 1337-44. doi:10.1016/S0191-8141(01)00005-0. Linckens, J., G. Zulauf, and J. Hammer. 2016. « Experimental Deformation of Coarse-Grained Rock Salt to High Strain ». Journal of Geophysical Research-Solid Earth 121 (8): 6150-71. doi:10.1002/2016JB012890. Platt, J.P., and W.M. Behr. 2011. « Grainsize Evolution in Ductile Shear Zones: Implications for Strain Localization and the Strength of the Lithosphere ». Journal of Structural Geology 33 (4): 537-50. doi:10.1016/j.jsg.2011.01.018.

Recrystallization characteristics and interfacial oxides on the compression bonding interface

NASA Astrophysics Data System (ADS)

Xie, Bijun; Sun, Mingyue; Xu, Bin; Li, Dianzhong

2018-05-01

Up to now, the mechanism of interface bonding is still not fully understood. This work presents interfacial characteristics of 316LN stainless steel bonding joint after cold compression bonding with subsequent annealing. EBSD analysis shows that fine recrystallization grains preferentially appear near the bonding interface and grow towards both sides of the interface. Transmission electron microscopy reveals that initial cold compression bonding disintegrates the native oxide scales and brings pristine metal from both sides of the interface come into intimate contact, while the broken oxide particles are remained at the original interface. The results indicate that partial bonding can be achieved by cold compression bonding with post-annealing treatment and recrystallization firstly occurs along the bonding interface. However, the interfacial oxides impede the recrystallization grains step over the interface and hinder the complete healing of the bonding interface.

Modifications in the AA5083 Johnson-Cook Material Model for Use in Friction Stir Welding Computational Analyses

NASA Astrophysics Data System (ADS)

Grujicic, M.; Pandurangan, B.; Yen, C.-F.; Cheeseman, B. A.

2012-11-01

Johnson-Cook strength material model is frequently used in finite-element analyses of various manufacturing processes involving plastic deformation of metallic materials. The main attraction to this model arises from its mathematical simplicity and its ability to capture the first-order metal-working effects (e.g., those associated with the influence of plastic deformation, rate of deformation, and the attendant temperature). However, this model displays serious shortcomings when used in the engineering analyses of various hot-working processes (i.e., those utilizing temperatures higher than the material recrystallization temperature). These shortcomings are related to the fact that microstructural changes involving: (i) irreversible decrease in the dislocation density due to the operation of annealing/recrystallization processes; (ii) increase in grain-size due to high-temperature exposure; and (iii) dynamic-recrystallization-induced grain refinement are not accounted for by the model. In this study, an attempt is made to combine the basic physical-metallurgy principles with the associated kinetics relations to properly modify the Johnson-Cook material model, so that the model can be used in the analyses of metal hot-working and joining processes. The model is next used to help establish relationships between process parameters, material microstructure and properties in friction stir welding welds of AA5083 (a non-age-hardenable, solid-solution strengthened, strain-hardened/stabilized Al-Mg-Mn alloy).

Recrystallization Behavior in SAC305 and SAC305 + 3.0POSS Solder Joints Under Thermal Shock

NASA Astrophysics Data System (ADS)

Han, Jing; Gu, Penghao; Ma, Limin; Guo, Fu; Liu, Jianping

2018-04-01

Sn-3.0Ag-0.5Cu (SAC305) and SAC305 + 3.0 polyhedral oligomeric silsesquioxanes (POSS) ball grid array (BGA) assemblies have been prepared, observed, and subjected to thermal shock. The microstructure and grain orientation evolution of the solder joints located at the same position of the package were characterized by scanning electron microscopy and electron backscattering diffraction, respectively. The results showed that the microstructure of the solder joints was refined by addition of POSS particles. In addition, compared with the single-grained or tricrystal joints normally observed in SAC305 BGA solder joints, the frequency of single-grained as-reflowed SAC305 + 3.0POSS BGA joints was greatly reduced, and the solder joints were typically composed of multicrystals with orientations separated by high-angle grain boundaries. These multicrystal joints appear to be obtained by dominant tricrystals or double tricrystals with deviation of the preferred [110] and [1\\bar{1}0] growth directions of Sn dendrites in Sn-Ag-based solder alloys during solidification from the melt. After 928 thermal shock cycles, the SAC305 solder joint had large-area recrystallization and cracks in contrast to the SAC305 + 3.0POSS solder joint located at the same position of the package, indicating that addition of POSS to SAC305 solder joints may contribute to postponement of recrystallization and subsequent crack initiation and propagation along recrystallized grain boundaries by pinning grain boundaries and movement of dislocations. This finding also confirms the double tricrystal solidification twinning nucleation behavior in Pb-free solder joints.

Effect of Strain Restored Energy on Abnormal Grain Growth in Mg Alloy Simulated by Phase Field Methods

NASA Astrophysics Data System (ADS)

Wu, Yan; Huang, Yuan-yuan

2018-03-01

Abnormal grain growth of single phase AZ31 Mg alloy in the spatio-temporal process has been simulated by phase field models, and the influencing factors of abnormal grain growth are studied in order to find the ways to control secondary recrystallization in the microstructure. The study aims to find out the mechanisms for abnormal grain growth in real alloys. It is shown from the simulated results that the abnormal grain growth can be controlled by the strain restored energy. Secondary recrystallization after an annealing treatment can be induced if there are grains of a certain orientation in the microstructure with local high restored energy. However, if the value of the local restored energy at a certain grain orientation is not greater than 1.1E 0, there may be no abnormal grain growth in the microstructure.

High temperature microstructural stability and recrystallization mechanisms in 14YWT alloys

DOE PAGES

Aydogan, E.; El-Atwani, O.; Takajo, S.; ...

2018-02-09

In-situ neutron diffraction experiments were performed on room temperature compressed 14YWT nanostructured ferritic alloys at 1100°C and 1150°C to understand their thermally activated static recrystallization mechanisms. The existence of high density of Y-Ti-O rich nano-oxides (<5 nm) shift the recrystallization temperature up due to Zener pinning of the grain boundaries, making these materials attractive for high temperature applications. This study serves to quantify the texture evolution in-situ and understand the effect of particles on the recrystallization mechanisms in 14YWT alloys. We have shown, both experimentally and theoretically, that there is considerable recovery in the 20% compressed sample after 6.5 hmore » annealing at 1100°C while recrystallization occurs within an hour of annealing at 1100°C and 1150°C in the 60% compressed samples. Moreover, the 60% compressed samples show {112}<110> and {112}<111> texture components during annealing, in contrast to the conventional recrystallization textures in body centered cubic alloys. Furthermore, nano-oxide size, shape, density and distribution are considerably different in unrecrystallized and abnormally grown grains. Transmission electron microscopy analysis shows that oxide particles having a size between 5 and 30 nm play a critical role for recrystallization mechanisms in 14YWT nanostructured ferritic alloys.« less

High temperature microstructural stability and recrystallization mechanisms in 14YWT alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aydogan, E.; El-Atwani, O.; Takajo, S.

In-situ neutron diffraction experiments were performed on room temperature compressed 14YWT nanostructured ferritic alloys at 1100°C and 1150°C to understand their thermally activated static recrystallization mechanisms. The existence of high density of Y-Ti-O rich nano-oxides (<5 nm) shift the recrystallization temperature up due to Zener pinning of the grain boundaries, making these materials attractive for high temperature applications. This study serves to quantify the texture evolution in-situ and understand the effect of particles on the recrystallization mechanisms in 14YWT alloys. We have shown, both experimentally and theoretically, that there is considerable recovery in the 20% compressed sample after 6.5 hmore » annealing at 1100°C while recrystallization occurs within an hour of annealing at 1100°C and 1150°C in the 60% compressed samples. Moreover, the 60% compressed samples show {112}<110> and {112}<111> texture components during annealing, in contrast to the conventional recrystallization textures in body centered cubic alloys. Furthermore, nano-oxide size, shape, density and distribution are considerably different in unrecrystallized and abnormally grown grains. Transmission electron microscopy analysis shows that oxide particles having a size between 5 and 30 nm play a critical role for recrystallization mechanisms in 14YWT nanostructured ferritic alloys.« less

Ultra-thin grain-oriented silicon steel sheet fabricated by a novel way: Twin-roll strip casting and two-stage cold rolling

NASA Astrophysics Data System (ADS)

Wang, Yin-Ping; Liu, Hai-Tao; Song, Hong-Yu; Liu, Jia-Xin; Shen, Hui-Ying; Jin, Yang; Wang, Guo-Dong

2018-04-01

0.05-0.15 mm-thick ultra-thin grain-oriented silicon steel sheets were successfully produced by a novel processing route including strip casting, hot rolling, normalizing, two-stage cold rolling with intermediate annealing, primary recrystallization annealing and secondary recrystallization annealing. The evolutions of microstructure, texture and inhibitor along the processing were briefly investigated. The results showed that the initial Goss orientation originated due to the heterogenous nucleation of δ-ferrite grains during solidification. Because of the lack of shear deformation, only a few Goss grains were observed in the hot rolled sheet. After the first cold rolling and intermediate annealing, Goss texture was enhanced and distributed in the whole thickness. A small number of Goss grains having a high fraction of high energy boundaries exhibited in the primary recrystallization annealed sheet. A large number of fine and dispersed MnS and AlN and a few co-precipitates MnS and AlN with the size range of 10-70 nm were also observed. Interestingly, a well-developed secondary recrystallization microstructure characterized by 10-60 mm grains and a sharp Goss texture were finally produced in the 0.05-0.15 mm-thick ultra-thin sheets. A magnetic induction B8 of 1.72-1.84 T was obtained. Another new finding was that a few {2 3 0}〈0 0 1〉 and {2 1 0}〈1 2 7〉 grains also can grow up abnormally because of the high fraction of high energy boundaries and the size and number advantage, respectively. These non-Goss grains finally deteriorated the magnetic properties of the ultra-thin sheets. In addition, low surface energies of {hk0} planes may also contribute to the abnormal growth of Goss, {2 3 0}〈0 0 1〉 and {2 1 0}〈1 2 7〉 grains.

Towards the determination of deformation rates - pinch-and-swell structures as a natural and simulated paleo-strain rate gage

NASA Astrophysics Data System (ADS)

Peters, Max; Poulet, Thomas; Karrech, Ali; Regenauer-Lieb, Klaus; Herwegh, Marco

2014-05-01

Layered rocks deformed under viscous deformation conditions frequently show boudinage, a phenomenon that results from differences in effective viscosity between the involved layers. In the case of continuous necking of a mechanically stiffer layer embedded in a weaker matrix, symmetric boudins are interpreted as the result of dominant visco-plastic deformation (Goscombe et al., 2004). However, information on the physical conditions, material properties and deformation processes are yet unknown. Natural samples deformed under low-grade (T<350°C) metamorphic conditions were studied in detail in the Dent de Morcles and Doldenhorn nappes of the Helvetic Alps in order to accurately simulate their deformation styles by numerical models. In these samples, monomineralic calcite (Cc) veins were repeatedly boudinaged on cm- to µm-scale. Remnants of incompletely recrystallized original vein Cc grains in the swells indicate a sequence of deformation twinning, followed by progressive dynamic recrystallization along former twin planes up to complete recrystallization in the pinches (Schmalholz and Maeder, 2012). This sequence suggests dislocation creep to be active as important deformation mechanism. In contrast to the pinch-and-swell structures, the grain size of the Cc in the surrounding matrix is much finer-grained due to pinning by secondary particles, forcing the matrix to deform under viscous granular creep, i.e. by diffusion accommodated grain boundary sliding. The deformation processes observed in the natural samples were incorporated into a numerical model in order to evaluate the rheology of both layer and matrix, using an extension to a user material subroutine (Karrech et al., 2011a) for the finite element solver ABAQUS. We implemented thermo-mechanical coupling allowing elastic, viscous and plastic deformation of Cc (Herwegh et al., in press). We simulate a pure-shear box using finite elements, each representing a grain size distribution, which undergo layer-parallel extension. The box is built up by 3 layers, consisting of a central layer of coarse-grained populations, surrounded by finer-grained populations on bottom and top. The rheology evolves from transient stages (elasticity and strain hardening) to composite viscous flow (GSI & GSS) with increasing shear strain. The small grain sizes in top and bottom layers are strain-invariant and limited in their growth (comparable to Zener pinning) forcing the matrix to deform by exclusively by GSS creep. In contrast, the initially coarse grain sizes of the central layer are allowed to adapt to the physical deformation conditions by either grain growth or grain size reduction following the Paleowattmeter of Austin and Evans (2007) combined with the thermodynamic approach of Regenauer-Lieb and Yuen (2004). Depending on the dissipated energy, grain sizes in these domains vary substantially in space and time. While low strain rates (low stresses) in the swells favor grain growth and GSI dominated deformation, high strain rates in the pinches provoke dramatic grain size reduction with an increasing contribution of GSS as a function of decreasing grain size. The development of symmetric necks observed in nature thus seems to coincide with the transition from dislocation to diffusion creep dominated flow with continuous grain size reduction and growth from swell to neck at relatively high extensional strains. REFERENCES Austin, N. and Evans, B. (2007). Paleowattmeters: A scaling relation for dynamically recrystallized grain size. Geology, 35. Goscombe, B.D., Passchier, C.W. and Hand, M. (2004). Boudinage classification: End-member boudin types and modified boudin structures, Journal of Structural Geology, 26. Herwegh, M., Poulet, T., Karrech, A. and Regenauer-Lieb, K. (in press). From transient to steady state deformation and grain size: A thermodynamic approach using elasto-visco-plastic numerical modeling. Journal of Geophysical Research. Karrech, A., Regenauer-Lieb, K. and Poulet, T. (2011a). A Damaged visco-plasticity model for pressure and temperature sensitive geomaterials. Journal of Engineering Science 49. Regenauer-Lieb, K. and Yuen, D. (2004). Positive feedback of interacting ductile faults from coupling of equation of state, rheology and thermal-mechanics. Physics of the Earth and Planetary Interiors, 142. Schmalholz, S.M. and Maeder, X. (2012). Pinch-and-swell structure and shear zones in viscoplastic layers. Journal of Structural Geology, 34.

The Effect of Grain Size on the Strain Hardening Behavior for Extruded ZK61 Magnesium Alloy

NASA Astrophysics Data System (ADS)

Zhang, Lixin; Zhang, Wencong; Chen, Wenzhen; Duan, Junpeng; Wang, Wenke; Wang, Erde

2017-12-01

The effects of grain size on the tensile and compressive strain hardening behaviors for extruded ZK61 alloys have been investigated by uniaxial tensile and compressive tests along the extrusion directions. Cylindrical tension and compression specimens of extruded ZK61 alloys with various sized grain were fabricated by annealing treatments. Tensile and compressive tests at ambient temperature were conducted at a strain rate of 0.5 × 10-3 s-1. The results indicate that both tensile strain hardening and compressive strain hardening of ZK61 alloys with different grain sizes have an athermal regime of dislocation accumulation in early deformation. The threshold stress value caused dynamic recovery is predominantly related to grain size in tensile strain hardening, but the threshold stress values for different grain sizes are almost identical in compressive strain hardening. There are obvious transition points on the tensile strain hardening curves which indicate the occurrence of dynamic recrystallization (DRX). The tensile strain hardening rate of the coarse-grained alloy obviously decreases faster than that of fine-grained alloys before DRX and the tensile strain hardening curves of different grain sizes basically tend to parallel after DRX. The compressive strain hardening rate of the fine-grained alloy obviously increases faster than that of coarse-grained alloy for twin-induced strain hardening, but compressive strain hardening curves also tend to parallel after twinning is exhausted.

Genesis of Microstructures in Friction Stir Welding of Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Tchein, Gnofam Jacques; Jacquin, Dimitri; Coupard, Dominique; Lacoste, Eric; Girot Mata, Franck

2018-06-01

This paper is focused on the genesis of microstructures in friction stir welding (FSW) of the Ti-6Al-4V alloy. Several titanium joints, initially prepared with four different preheat treatments, were processed by FSW. Detailed microstructural analyses were performed in order to investigate change in the microstructure during the process. In this work, the FSW processing allows a controlled and stable microstructure to be produced in the stirring zone, regardless of the initial heat treatment or the welding conditions. The welded material undergoes a severe thermomechanical treatment which can be divided into two steps. First, the friction in the shoulder and the plastic strain give rise to the necessary conditions to allow a continuous dynamic recrystallization of the β phase. This operation produces a fine and equiaxed β grain structure. Second, once the pin has moved away, the temperature decreases, and the material undergoes a heat treatment equivalent to air quenching. The material thus exhibits a β → β + α transformation with germination of a fine intergranular Widmanstätten phase within the ex-fully-recrystallized- β grains.

EBSD Study on Grain Boundary and Microtexture Evolutions During Friction Stir Processing of A413 Cast Aluminum Alloy

NASA Astrophysics Data System (ADS)

Shamanian, Morteza; Mostaan, Hossein; Safari, Mehdi; Szpunar, Jerzy A.

2016-07-01

The as-cast Al alloys contain heterogeneous distributions of non-deforming particles due to non-equilibrium solidification effects. Therefore, these alloys have poor tribological and mechanical behaviors. It is well known that using friction stir processing (FSP), very fine microstructure is created in the as-cast Al alloys, while their wear resistance can be improved. In this research work, FSP is used to locally refine a surface layer of the coarse as-cast microstructure of cast A413 Al alloy. The main objective of this study is to investigate the effect of FSP on microstructure and microtexture evolutions in A413 cast Al alloy. The grain boundary character distribution, grain structure, and microtexture evolutions in as-cast and friction stir processed A413 Al alloy are analyzed by electron back scatter diffraction technique. It is found that with the FSP, the fraction of low ∑boundary such as ∑3, 7, and 9 are increased. The obtained results show that there are no deformation texture components in the structure of friction stir processed samples. However, some of the main recrystallization texture components such as BR and cubeND are formed during FSP which indicate the occurrence of dynamic recrystallization phenomenon due to the severe plastic deformation induced by the rotation of tool.

FEM study of recrystallized tungsten under ELM-like heat loads

NASA Astrophysics Data System (ADS)

Du, J.; Yuan, Y.; Wirtz, M.; Linke, J.; Liu, W.; Greuner, H.

2015-08-01

FEM thermal analysis has been performed on rolled tungsten plate loaded with heat load of 23 MW/m2 for 1.5 s. Gradient temperature field is generated due to the Gaussian shape beam profile. Recrystallization and grain growth of various scales were found at different areas of the sample depending on the localized thermal field. FEM thermal-mechanical analyses have been performed on the recrystallized tungsten exposed to ELMs-like heat loads. The analyzed load conditions were 0.38 and 1.14 GW/m2 with different base temperatures. Material deterioration due to recrystallization was implemented by adopting decreased yield stress, tangent modulus, strength coefficient and ductility coefficients. Life time predicted by adopting strain life criterion indicates grain growth from 5 μm to 100 μm causes the life decrease of 80%. This result is gained by pure mathematical calculation based on the empiric assumptions of material properties.

Deformation Mechanism and Recrystallization Relationships in Galfenol Single Crystals: On the Origin of Goss and Cube Orientations

NASA Astrophysics Data System (ADS)

Na, Suok-Min; Smith, Malcolm; Flatau, Alison B.

2018-06-01

In this work, deformation mechanism related to recrystallization behavior in single-crystal disks of Galfenol (Fe-Ga alloy) was investigated to gain insights into the influence of crystal orientations on structural changes and selective grain growth that take place during secondary recrystallization. We started with the three kinds of single-crystal samples with (011)[100], (001)[100], and (001)[110] orientations, which were rolled and annealed to promote the formation of different grain structures and texture evolutions. The initial Goss-oriented (011)[100] crystal mostly rotated into {111}<112> orientations with twofold symmetry and shear band structures by twinning resulted in the exposure of rolled surface along {001}<110> orientation during rolling. In contrast, the Cube-oriented (001)[100] single crystal had no change in texture during rolling with the thickness reduction up to 50 pct. The {123}<111> slip systems were preferentially activated in these single crystals during deformation as well as {112}<111> slip systems that are known to play a role in primary slip of body-centered cubic (BCC) materials such as α-iron and Fe-Si alloys. After annealing, the deformed Cube-oriented single crystal had a small fraction (<10 pct) of recrystallized Goss-oriented grains. The weak Goss component remained in the shear bands of the 50 pct rolled Goss-oriented single crystal, and it appeared to be associated with coalescence of subgrains inside shear band structures during primary recrystallization. Rolling of the (001)[110] single crystal led to the formation of a tilted (001)[100] component close to the <120> orientation, associated with {123}<111> slip systems as well. This was expected to provide potential sites of nucleation for secondary recrystallization; however, no Goss- and Cube-oriented components actually developed in this sample during secondary recrystallization. Those results illustrated how the recrystallization behavior can be influenced by deformed structure and the slip systems.

Influence of Copper on the Hot Ductility of 20CrMnTi Steel

NASA Astrophysics Data System (ADS)

Peng, Hong-bing; Chen, Wei-qing; Chen, Lie; Guo, Dong

2015-02-01

The hot ductility of 20CrMnTi steel with x% copper (x = 0, 0.34) was investigated. Results show that copper can reduce its hot ductility, but there is no significant copper-segregation at the boundary tested by EPMA. The average copper content at grain boundaries and substrate is 0.352% and 0.318% respectively in steel containing 0.34% copper tensile-tested at 950 °C. The fracture morphology was examined with SEM and many small and shallow dimples were found on the fracture of steel with copper, and fine copper sulfide was found from carbon extraction replicas using TEM. Additionally, adding 0.34% copper caused an increase in the dynamic recrystallization temperature from 950 °C to 1000 °C, which indicates that copper can retard the dynamic recrystallization (DRX) of austenite. The detrimental influence of copper on hot ductility of 20CrMnTi steel is due mainly to the fine copper sulfide in the steel and its retarding the DRX.

Microstructural Characteristic of the Al-Fe-Cu Alloy During High-Speed Repetitive Continuous Extrusion Forming

NASA Astrophysics Data System (ADS)

Hu, Jiamin; Teng, Jie; Ji, Xiankun; Kong, Xiangxin; Jiang, Fulin; Zhang, Hui

2016-11-01

High-speed repetitive continuous extrusion forming process (R-Conform process) was performed on the Al-Fe-Cu alloy. The microstructural evolution and mechanical properties were studied by x-ray diffraction, electron backscatter diffraction, transmission electron microscopy and tensile testing. The results show that a significant improvement of tensile ductility concurs with a considerable loss of tensile strength before four passes, after that the process on mechanical properties variation tends to be steady, indicating an accelerated mechanical softening occurs when comparing to low-speed R-Conform process. Microstructure characterization indicates that the accumulated strain promotes the transformation of low angle boundaries to high angle boundaries, thus leading to the acceleration of continuous dynamic recrystallization process, and the precipitates are broken, spheroidized and homogeneously distribute in Al matrix as increasing R-Conform passes. Massive microshear bands are observed after initial passes of R-Conform process, which may promote continuous dynamic recrystallization and further grain refinement during high-speed R-Conform process.

Influence of grain size and texture prior to warm rolling on microstructure, texture and magnetic properties of Fe-6.5 wt% Si steel

NASA Astrophysics Data System (ADS)

Xu, H. J.; Xu, Y. B.; Jiao, H. T.; Cheng, S. F.; Misra, R. D. K.; Li, J. P.

2018-05-01

Fe-6.5 wt% Si steel hot bands with different initial grain size and texture were obtained through different annealing treatment. These bands were then warm rolled and annealed. An analysis on the evolution of microstructure and texture, particularly the formation of recrystallization texture was studied. The results indicated that initial grain size and texture had a significant effect on texture evolution and magnetic properties. Large initial grains led to coarse deformed grains with dense and long shear bands after warm rolling. Such long shear bands resulted in growth advantage for {1 1 3} 〈3 6 1〉 oriented grains during recrystallization. On the other hand, sharp {11 h} 〈1, 2, 1/h〉 (α∗-fiber) texture in the coarse-grained sample led to dominant {1 1 2} 〈1 1 0〉 texture after warm rolling. Such {1 1 2} 〈1 1 0〉 deformed grains provided massive nucleation sites for {1 1 3} 〈3 6 1〉 oriented grains during subsequent recrystallization. These {1 1 3} 〈3 6 1〉 grains were confirmed to exhibit an advantage on grain growth compared to γ-fiber grains. As a result, significant {1 1 3} 〈3 6 1〉 texture was developed and unfavorable γ-fiber texture was inhibited in the final annealed sheet. Both these aspects led to superior magnetic properties in the sample with largest initial grain size. The magnetic induction B8 was 1.36 T and the high frequency core loss P10/400 was 17.07 W/kg.

Evolution of microstructure, texture and inhibitor along the processing route for grain-oriented electrical steels using strip casting

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Hai-Tao, E-mail: liuht@ral.neu.edu.cn; Institute of Research of Iron and Steel, Shasteel, Zhangjiagang 215625, Jiangsu; Yao, Sheng-Jie

2015-08-15

In the present work, a regular grade GO sheet was produced successively by strip casting, hot rolling, normalizing annealing, two-stage cold rolling with intermediate annealing, primary recrystallization annealing, secondary recrystallization annealing and purification. The aim of this paper was to characterize the evolution of microstructure, texture and inhibitor along the new processing route by comprehensive utilization of optical microscopy, X-ray diffraction and transmission electron microscopy. It was found that a fine microstructure with the ferrite grain size range of 7–12 μm could be obtained in the primary recrystallization annealed sheet though a very coarse microstructure was produced in the initialmore » as-cast strip. The main finding was that the “texture memory” effect on Goss texture started on the through-thickness intermediate annealed strip after first cold rolling, which was not similar to the “texture memory” effect on Goss texture starting on the surface layers of the hot rolled strip in the conventional production route. As a result, the origin of Goss nuclei capable of secondary recrystallization lied in the grains already presented in Goss orientation in the intermediate annealed strip after first cold rolling. Another finding was that fine and dispersive inhibitors (mainly AlN) were easy to be produced in the primary recrystallization microstructure due to the initial rapid solidification during strip casting and the subsequent rapid cooling, and the very high temperature reheating usually used before hot rolling in the conventional production route could be avoided. - Highlights: • A regular grade grain-oriented electrical steel was produced. • Evolution of microstructure, texture and inhibitor was characterized. • Origin of Goss nuclei lied in the intermediate annealed strip. • A fine primary recrystallization microstructure could be produced. • Effective inhibitors were easy to be obtained in the new processing route.« less

Effect of Post-deformation Annealing Treatment on the Microstructural Evolution of a Cold-Worked Corrosion-Resistant Superalloy (CRSA) Steel

NASA Astrophysics Data System (ADS)

Mirzaei, A.; Zarei-Hanzaki, A.; Mohamadizadeh, A.; Lin, Y. C.

2018-03-01

The post-deformation annealing treatments of a commercial cold-worked corrosion-resistant superalloy steel (Sanicro 28 steel) were carried out at different temperatures in the range of 900-1100 °C for different holding durations of 5, 10, and 15 min. The effects of post-deformation annealing time and temperature on the microstructural evolution and subsequent mechanical properties of the processed Sanicro 28 steel were investigated. The observations indicated that twin-twin hardening in cold deformation condition mainly correlates with abundant nucleation of mechanical twins in multiple directions resulting in considerable strain hardening behavior. Microstructural investigations showed that the static recrystallization takes place after isothermal holding at 900 °C for 5 min. Increasing the annealing temperature from 900 to 1050 °C leads to recrystallization development and grain refinement in the as-recrystallized state. In addition, an increase in annealing duration from 5 to 15 min leads to subgrain coarsening and subsequently larger recrystallized grains size. The occurrence of large proportion of the grain refinement, which is achieved in the first annealing stage at 1050 °C after 5 min, is considered as the main factor for the maximum elongation at this stage.

The effect of water on recrystallization behavior and grain boundary morphology in calcite observations of natural marble mylonites

NASA Astrophysics Data System (ADS)

Schenk, Oliver; Urai, Janos L.; Evans, Brian

2005-10-01

Fluids are inferred to play a major role in the deformation and recrystallization of many minerals (e.g. quartz, olivine, halite, feldspar). In this study, we sought to identify the effect of fluids on grain boundary morphology and recrystallization processes in marble mylonites during shear zone evolution. We compared the chemistry, microstructure and mesostructure of calcite marble mylonites from the Schneeberg Complex, Southern Tyrole, Italy, to that from the Naxos Metamorphic Core Complex, Greece. These two areas were selected for comparison because they have similar lithology and resemble each other in chemical composition. In addition, calcite-dolomite geothermometry indicates similar temperatures for shear zone formation: 279±25 °C (Schneeberg Complex) and 271±15 °C (Naxos high-grade core). However, the two settings are different in the nature of the fluids present during the shear zone evolution. In the Schneeberg mylonites, both the alteration of minerals during retrograde metamorphism in the neighboring micaschists and the existence of veins suggest that aqueous fluids were present during mylonitization. The absence of these features in the Naxos samples indicates that aqueous fluids were not as prevalent during deformation. This conclusion is also supported by the stable isotope signature. Observations of broken and planar surfaces using optical and scanning electron microscopes did not indicate major differences between the two mylonites: grain boundaries in both settings display pores with shapes controlled by crystallography, and have pore morphologies that are similar to observations from crack and grain-boundary healing experiments. Grain size reduction was predominantly the result of subgrain rotation recrystallization. However, the coarse grains inside the wet protomylonites (Schneeberg) are characterized by intracrystalline shear zones.

Modeling the microstructural changes during hot tandem rolling of AA5 XXX aluminum alloys: Part I. Microstructural evolution

NASA Astrophysics Data System (ADS)

Wells, M. A.; Samarasekera, I. V.; Brimacombe, J. K.; Hawbolt, E. B.; Lloyd, D. J.

1998-06-01

A comprehensive mathematical model of the hot tandem rolling process for aluminum alloys has been developed. Reflecting the complex thermomechanical and microstructural changes effected in the alloys during rolling, the model incorporated heat flow, plastic deformation, kinetics of static recrystallization, final recrystallized grain size, and texture evolution. The results of this microstructural engineering study, combining computer modeling, laboratory tests, and industrial measurements, are presented in three parts. In this Part I, laboratory measurements of static recrystallization kinetics and final recrystallized grain size are described for AA5182 and AA5052 aluminum alloys and expressed quantitatively by semiempirical equations. In Part II, laboratory measurements of the texture evolution during static recrystallization are described for each of the alloys and expressed mathematically using a modified form of the Avrami equation. Finally, Part III of this article describes the development of an overall mathematical model for an industrial aluminum hot tandem rolling process which incorporates the microstructure and texture equations developed and the model validation using industrial data. The laboratory measurements for the microstructural evolution were carried out using industrially rolled material and a state-of-the-art plane strain compression tester at Alcan International. Each sample was given a single deformation and heat treated in a salt bath at 400 °C for various lengths of time to effect different levels of recrystallization in the samples. The range of hot-working conditions used for the laboratory study was chosen to represent conditions typically seen in industrial aluminum hot tandem rolling processes, i.e., deformation temperatures of 350 °C to 500 °C, strain rates of 0.5 to 100 seconds and total strains of 0.5 to 2.0. The semiempirical equations developed indicated that both the recrystallization kinetics and the final recrystallized grain size were dependent on the deformation history of the material i.e., total strain and Zener-Hollomon parameter ( Z), where Z = dot \\varepsilon exp left( {{Q_{def} }/{RT_{def }}} right) and time at the recrystallization temperature.

A continuum theory of grain size evolution and damage

NASA Astrophysics Data System (ADS)

Ricard, Y.; Bercovici, D.

2009-01-01

Lithospheric shear localization, as occurs in the formation of tectonic plate boundaries, is often associated with diminished grain size (e.g., mylonites). Grain size reduction is typically attributed to dynamic recrystallization; however, theoretical models of shear localization arising from this hypothesis are problematic because (1) they require the simultaneous action of two creep mechanisms (diffusion and dislocation creep) that occur in different deformation regimes (i.e., in grain size stress space) and (2) the grain growth ("healing") laws employed by these models are derived from normal grain growth or coarsening theory, which are valid in the absence of deformation, although the shear localization setting itself requires deformation. Here we present a new first principles grained-continuum theory, which accounts for both coarsening and damage-induced grain size reduction in a monomineralic assemblage undergoing irrecoverable deformation. Damage per se is the generic process for generation of microcracks, defects, dislocations (including recrystallization), subgrains, nuclei, and cataclastic breakdown of grains. The theory contains coupled macroscopic continuum mechanical and grain-scale statistical components. The continuum level of the theory considers standard mass, momentum, and energy conservation, as well as entropy production, on a statistically averaged grained continuum. The grain-scale element of the theory describes both the evolution of the grain size distribution and mechanisms for both continuous grain growth and discontinuous grain fracture and coalescence. The continuous and discontinuous processes of grain size variation are prescribed by nonequilibrium thermodynamics (in particular, the treatment of entropy production provides the phenomenological laws for grain growth and reduction); grain size evolution thus incorporates the free energy differences between grains, including both grain boundary surface energy (which controls coarsening) and the contribution of deformational work to these free energies (which controls damage). In the absence of deformation, only two mechanisms that increase the average grain size are allowed by the second law of thermodynamics. One mechanism, involving continuous diffusive mass transport from small to large grains, captures the essential components of normal grain growth theories of Lifshitz-Slyosov and Hillert. The second mechanism involves the aggregation of grains and is described using a Smoluchovski formalism. With the inclusion of deformational work and damage, the theory predicts two mechanisms for which the thermodynamic requirement of entropy positivity always forces large grains to shrink and small ones to grow. The first such damage-driven mechanism involving continuous mass transfer from large to small grains tends to homogenize the distribution of grain size toward its initial mean grain size. The second damage mechanism favors the creation of small grains by discontinuous division of larger grains and reduces the mean grain size with time. When considered separately, most of these mechanisms allow for self-similar grain size distributions whose scales (i.e., statistical moments such as the mean, variance, and skewness) can all be described by a single grain scale, such as the mean or maximum. However, the combination of mechanisms, e.g., one that captures the competition between continuous coarsening and mean grain size reduction by breakage, does not generally permit a self-similar solution for the grain size distribution, which contradicts the classic assumption that grain growth laws allowing for both coarsening and recrystallization can be treated with a single grain scale such as the mean size.

Metamorphic reactions, grain size reduction and deformation of mafic lower crustal rocks

NASA Astrophysics Data System (ADS)

Degli Alessandrini, Giulia; Menegon, Luca; Beltrando, Marco; Dijkstra, Arjan; Anderson, Mark

2016-04-01

This study investigates grain-scale deformation mechanisms associated with strain localization in the mafic continental lower crust, with particular focus on the role of syn-kinematic metamorphic reactions and their product - symplectites - in promoting grain size reduction and phase mixing. The investigated shear zone is hosted in the Finero mafic-ultramafic complex in the Italian Southern Alps. Shearing occurred at T ≥ 650° C and P ≥ 0.4-0.6 GPa. The shear zone reworks both mafic and ultramafic lithologies and displays anastomosing patterns of (ultra)mylonitic high strain zones wrapping less foliated, weakly deformed low strain domains. Field and microstructural observations indicate that different compositional layers of the shear zone responded differently to deformation, resulting in strain partitioning. Four distinct microstructural domains have been identified: (1) an ultramylonitic domain characterized by an amph + pl matrix (grain size < 30μm) with large amphibole porphyroclasts (grain size between 200μm and 5000μm) and rare garnets; (2) a domain rich in garnet porphyroclasts embedded in a matrix of monomineralic plagioclase displaying a core and mantle structure (average grain size 45μm) (3) a metagabbroic domain with porphyroclasts of clinopyroxene, orthopyroxene and garnets (200μm average grain size) wrapped by monomineralic ribbons of recrystallized plagioclase and (4) a garnet-free ultramylonitic domain composed of an intermixed amph + cpx + opx + pl matrix (6μm average grain size). In these domains, each porphyroclastic mineral responds differently to deformation: amphibole readily breaks down to symplectitic intergrowths of amph + pl or opx + pl. Garnet undergoes fracturing (in domain 2) or reacts to give symplectites of pl + opx (in domain 3). Plagioclase dynamically recrystallizes in mono-phase aggregates, whereas clinopyroxene undergoes fracturing and orthopyroxene undergoes plastic deformation. The behaviour of the different phases and their relative abundance in the layers are believed to influence the deformation of the layers themselves. In symplectite-rich layers (domains 1, 4) deformation is localised, grain-size is below 30μm and phases are well mixed. On the other hand, in pyroxene or plagioclase-rich layers, deformation is less localised, the phases are less mixed and the grain size is larger (domain 2, 3). These preliminary results suggest that syn-kinematic metamorphic reactions forming symplectites played an essential role in grain size reduction, phase mixing and strain localization. We speculate that the compositional domains with symplectites localized deformation more efficiently, by activation of grain size sensitive creep, most likely because those domains were originally more hydrated than the others. On the contrary, domains without symplectites accommodated deformation less efficiently, either through fracturing (clinopyroxene, garnet) or dislocation creep + recrystallization (orthopyroxene, plagioclase).

Friction stir welded AM50 and AZ31 Mg alloys: Microstructural evolution and improved corrosion resistance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Templeman, Yael

One of the major drawbacks of Mg alloys is poor weldability, caused by porosity formation during conventional fusion welding processes. Friction Stir Welding (FSW) is promising technique in this context since it is a solid state technique. Contradicting results were published in the literature regarding the FSWed Mg alloys joint's properties. Current research was performed in order to investigate the microstructure and corrosion properties of FSWed Mg alloys, studying representatives of two commercial families: wrought AZ31-H24 and die cast AM50. It was found that in both alloys recrystallization occurred during the FSW. In AM50 the mechanism of the recrystallization wasmore » continuous, manifested by dislocation rearrangement into sub grain boundaries. In AZ31 discontinuous recrystallization had occurred through grain boundaries migration - twins rotated with respect to the matrix, turning into low angle grain boundaries. Corrosion resistance has improved during the FSW in both alloys to different extents. In the AM50 alloy, the nugget exhibited significantly higher surface potential than the base metal mainly due to the higher Al concentration in the matrix of the nugget, resulting from the dissolution of Al-enrichment and β-Mg{sub 17}Al{sub 12} phase. In the AZ31 alloy, no change in Al concentration had occurred, and the surface potential measured in the nugget was only slightly higher than in the base metal. These results underline the appropriateness of the FSW for Mg alloys since during the conventional welding deterioration of the corrosion resistance occurs. - Highlights: • Following FSW, AZ31-H24 experienced discontinuous recrystallization. • In AZ31 grain boundaries migration occurred, thus twins rotated. • In die cast AM50 continuous recrystallization occurred during the FSW. • In AM50 - dislocations rearranged into sub grain boundaries. • Corrosion resistance has improved during the FSW in both alloys to different extent.« less

Thermal stability of Cu-Cr-Zr alloy processed by equal-channel angular pressing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abib, Khadidja

Thermal stability of a Cu-Cr-Zr alloy processed by equal-channel angular pressing up to16 passes was investigated using isochronal annealing ranging from 250 to 850 °C for 1 h. The microstructure, crystallographic texture and micro hardness of samples were characterized through electron back scatter diffraction and Vickers micro hardness measurements. The recrystallized grain size was stable between 250 °C and 500 °C then increased quickly. The achieved mean grain size, after 1, 4 and 16 ECAP passes, was around 5.5 μm. A discontinuous mode of recrystallization was found to occur and a Particle Simulated Nucleation mechanism was evidenced. The evolution ofmore » the high angle grain boundary fraction increased notably after annealing above 550 °C. The crystallographic texture after isochronal annealing was similar to that of ECAP simple shear, no change of the texture during annealing was observed but only slight intensity variations. Micro hardness of all Cu–Cr–Zr samples showed a hardening with two peaks at 400 and 500 °C associated with precipitation of Cu cluster and Cu{sub 5}Zr phase respectively, followed by a subsequent softening upon increasing the annealing temperature due to recrystallization. - Highlight: •The Cu-1Cr-0.1Zr alloy shows a very good thermal stability up to 550 °C after ECAP. •A discontinuous recrystallization was found to occur and PSN mechanism was evidenced. •The annealing texture was found weak and some new components appear. •Hardening is attributed to the Cr clustering followed by the Cu{sub 51}Zr{sub 14} precipitation. •Softening is a result of recrystallization and grain growth progressing.« less

Texture evolution during thermomechanical processing in rare earth free magnesium alloys

NASA Astrophysics Data System (ADS)

Miller, Victoria Mayne

The use of wrought magnesium alloys is highly desirable for a wide range of applications where low component weight is desirable due to the high specific strength and stiffness the alloys can achieve. However, the implementation of wrought magnesium has been hindered by the limited room temperature formability which typically results from deformation processing. This work identifies opportunities for texture modification during thermomechanical processing of conventional (rare earth free) magnesium alloys via a combination of experimental investigation and polycrystal plasticity simulations. During deformation, it is observed that a homogeneous distribution of coarse intermetallic particles efficiently weakens deformation texture at all strain levels, while a highly inhomogeneous particle distribution is only effective at high strains. The particle deformation effects are complemented by the addition of alkaline earth solute, which modifies the relative deformation mode activity. During recrystallization, grains with basal orientations recrystallize more readily than off-basal grains, despite similar levels of internal misorientation. Dislocation substructure investigations revealed that this is a result of enhanced nucleation in the basal grains due to the dominance of prismatic slip. This dissertation identifies avenues to enhance the potential formability of magnesium alloys during thermomechanical processing by minimizing the evolved texture strength. The following are the identified key aspects of microstructural control: -Maintaining a fine grain size, likely via Zener pinning, to favorably modify deformation mode activity and homogenize deformation. -Developing a coarse, homogeneously distributed population of coarse intermetallic particles to promote a diffuse deformation texture. -Minimizing the activity of prismatic slip to retard the recrystallization of grains with basal orientations, allowing the development of a more diffuse recrystallization texture.

The Effect of Welding Energy on the Microstructural and Mechanical Properties of Ultrasonic-Welded Copper Joints

PubMed Central

Yang, Jingwei; Cao, Biao; Lu, Qinghua

2017-01-01

The effects of welding energy on the mechanical and microstructural characteristics of ultrasonic-welded pure copper plates were investigated. Complex dynamic recrystallization and grain growth occurred inside the weld zone during ultrasonic welding. At a low welding energy, a thin band of straight weld interfaces was observed and had an ultra-fine grain structure. With an increase in welding energy, the weld interface progressively changed from flat to sinusoidal, and eventually turned into a convoluted wavy pattern, bearing similarities to shear instabilities, as observed in fluid dynamics. The lap shear load of the joints initially increased and then remained stable as the welding energy increased. The tensile characteristics of the joints significantly depended on the development of plastic deformation at the interface. The influence of the microstructure on the hardness was also discussed. PMID:28772553

The Effect of Welding Energy on the Microstructural and Mechanical Properties of Ultrasonic-Welded Copper Joints.

PubMed

Yang, Jingwei; Cao, Biao; Lu, Qinghua

2017-02-16

The effects of welding energy on the mechanical and microstructural characteristics of ultrasonic-welded pure copper plates were investigated. Complex dynamic recrystallization and grain growth occurred inside the weld zone during ultrasonic welding. At a low welding energy, a thin band of straight weld interfaces was observed and had an ultra-fine grain structure. With an increase in welding energy, the weld interface progressively changed from flat to sinusoidal, and eventually turned into a convoluted wavy pattern, bearing similarities to shear instabilities, as observed in fluid dynamics. The lap shear load of the joints initially increased and then remained stable as the welding energy increased. The tensile characteristics of the joints significantly depended on the development of plastic deformation at the interface. The influence of the microstructure on the hardness was also discussed.

Effect of Boron on the Hot Ductility of Resulfurized Low-Carbon Free-Cutting Steel

NASA Astrophysics Data System (ADS)

Liu, Hai-tao; Chen, Wei-qing

2015-09-01

The hot ductility of resulfurized low-carbon free-cutting steel with boron additives is studied in the temperature range 850 - 1200°C with the help of a Gleeble-1500 thermomechanical simulator. The introduction of boron increases hot ductility, especially at 900 - 1050°C. In the single-phase austenitic region, this effect is caused by segregation of boron over grain boundaries, acceleration of dynamic recrystallization, and solid-solution softening of deformed austenite.

Orogen-scale along-strike continuity in quartz recrystallization microstructures adjacent to the Main Central Thrust: implications for deformation temperatures, strain rates and flow stresses

NASA Astrophysics Data System (ADS)

Law, Richard

2015-04-01

Traced for ~ 1500 km along the foreland edge of the Himalaya from NW India to Bhutan published reports indicate a remarkable along-strike continuity of quartz recrystallization microstructures in the footwall and hanging wall to the Main Central Thrust (MCT). Recrystallization in Lesser Himalayan Series (LHS) rocks in the footwall to the MCT is dominated by grain boundary bulging (BLG) microstructures, while recrystallization in Greater Himalayan Series (GHS) rocks in the hanging wall is dominated by grain boundary migration microstructures that traced structurally upwards transition in to the anatectic core of the GHS. In foreland-positioned high-strain rocks adjacent to the MCT recrystallization is dominated by subgrain rotation (SGR) with transitional BLG-SGR and SGR-GBM microstructures being recorded at structural distances of up to a few hundred meters below and above the MCT, respectively. Correlation with available information on temperatures of metamorphism indicated by mineral phase equilibria and RSCM data suggests that recrystallization in the structural zones dominated by BLG, SGR and GBM occurred at temperatures of ~ 350-450, 450-550 and 550- > 650 °C, respectively. It should be kept in mind, however, that these temperatures are likely to be 'close-to-peak' temperatures of metamorphism, whereas penetrative shearing and recrystallization may have continued during cooling. The dominance of SGR along the more foreland-positioned exposures of the MCT intuitively suggests that shearing occurred under a relatively restricted range of deformation temperatures and strain rates. Plotting the 'close-to-peak' 450-500 °C temperatures of metamorphism indicated for SGR-dominated rocks located at up to a few hundred meters below/above the MCT on the quartz recrystallization map developed by Stipp et al. (2002) indicates 'ball-park' strain rates of ~ 10-13 to 10-10 sec-1. However, only strain rates slower than 10-12 sec-1 on the MCT are likely to be compatible with know convergence rates between the Indian and Asian plates. If shearing continued during retrograde cooling while remaining in the SGR field, then the recrystallization map suggests that a significant drop in deformation temperature (> ~75-100 °C) would result in a decrease in strain rate. In general, however, the presence of a single recrystallization microstructure traced over a large (regional scale) distance does not necessarily mean that deformation temperature (or strain rate) remains constant but could, for example, indicate that spatial variations in deformation temperature are compensated for by changes in strain rate, with grain-scale deformation remaining within a particular recrystallization regime. Constant stress conditions plot along a straight line in the 1/T versus log strain rate space used in the quartz recrystallization mechanism map. This suggests that the observed along-strike consistency of SGR-dominated recrystallization microstructures may indicate near to constant stress boundary conditions (albeit with varying temperatures and strain rates) prevailing along what are now the more foreland-positioned exposures of the MCT. Extrapolation of the Hirth et al. (2001) flow law suggests a flow stress of ~ 30-50 MPa based on the deformation temperatures and strain rates inferred for foreland-positioned exposures of the MCT, in agreement with flow stresses estimated from recrystallized quartz grain size data.

Effects of Strain Path on the Microstructure of Aluminum Alloys During Equal Channel Angular Pressing (ECAP)

DTIC Science & Technology

2007-12-01

processing route at this level. A recent study by Garcia-Infanta, et al., of a hypo- eutectic Al-7%Si alloy with spheroidal primary aluminum grains is a...compared with the model proposed by Garcia-Infanta, et al. [10]. Further, annealing studies will be performed to determine the recrystallization ...study conducted at 450°C as a function of time to assess recrystallization and grain growth. Two data points per sample were taken from different

A Two-Step Approach for Producing an Ultrafine-Grain Structure in Cu-30Zn Brass (Postprint)

DTIC Science & Technology

2015-08-13

crystallization anneal at 400 °C (0.55Tm, where Tm is the melting point ) for times ranging from 1 min to 10 hours, followed by water quenching; an additional...200 words) A two-step approach involving cryogenic rolling and subsequent recrystallization annealing was developed to produce an ultrafine-grain...b s t r a c t A two-step approach involving cryogenic rolling and subsequent recrystallization annealing was devel- oped to produce an ultrafine

Shock induced crystallization of amorphous Nickel powders

NASA Astrophysics Data System (ADS)

Cherukara, Mathew; Strachan, Alejandro

2015-06-01

Recent experimental work has shown the efficacy of amorphous Ni/crystalline Al composites as energetic materials, with flame velocities twice that of a comparable crystalline Ni/crystalline Al system. Of further interest is the recrystallization mechanisms in the pure amorphous Ni powders, both thermally induced and mechanically induced. We present large-scale molecular dynamics simulations of shock-induced recrystallization in loosely packed amorphous Nickel powders. We study the time dependent nucleation and growth processes by holding the shocked samples at the induced pressures and temperatures for extended periods following the passage of the shock (up to 6 ns). We find that the nanostructure of the recrystallized Ni and time scales of recrystallization are dependent on the piston velocity. At low piston velocities, nucleation events are rare, leading to long incubation times and a relatively coarse nanostructure. At higher piston velocities, local variations in temperature due to jetting phenomena and void collapse, give rise to multiple nucleation events on time scales comparable to the passage of the shock wave, leading to the formation of a fine-grained nanostructure. Interestingly, we observe that the nucleation and growth process occurs in two steps, with the first nuclei crystallizing into the BCC structure, before evolving over time into the expected FCC structure. U.S. Defense Threat Reduction Agency, HDTRA1-10-1-0119 (Program Manager Suhithi Peiris).

In-situ observation of recrystallization in an AlMgScZr alloy using confocal laser scanning microscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Taendl, J., E-mail: johannes.taendl@tugraz.atl; Nambu, S.; Orthacker, A.

2015-10-15

In this work we present a novel in-situ approach to study the recrystallization behavior of age hardening alloys. We use confocal laser scanning microscopy (CLSM) at 400 °C to investigate the static recrystallization of an AlMg4Sc0.4Zr0.12 alloy in-situ. The results are combined with electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) analyses. It was found that CLSM is a powerful tool to visualize both the local initiation and temporal sequence of recrystallization. After fast nucleation and initial growth, the grain growth rate decreases and the grain boundary migration stops after some minutes due to Zener pinning from Al{sub 3}(Sc,Zr)more » precipitates produced during the heat treatment. EBSD and TEM analyses confirm both the boundary movements and the particle-boundary interactions. - Highlights: • First time that CLSM is used to study recrystallization in-situ. • The start and end of recrystallization can be directly observed. • The procedure is easy to apply and requires only simple data interpretation. • In-situ observations on the surface correlate to modifications inside the bulk. • In-situ observations correlate to EBSD and EFTEM analyses.« less

Effects of two-step homogenization on precipitation behavior of Al{sub 3}Zr dispersoids and recrystallization resistance in 7150 aluminum alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Zhanying; Key Laboratory for Anisotropy and Texture of Materials, Northeastern University, Shenyang 110819, China,; Zhao, Gang

2015-04-15

The effect of two-step homogenization treatments on the precipitation behavior of Al{sub 3}Zr dispersoids was investigated by transmission electron microscopy (TEM) in 7150 alloys. Two-step treatments with the first step in the temperature range of 300–400 °C followed by the second step at 470 °C were applied during homogenization. Compared with the conventional one-step homogenization, both a finer particle size and a higher number density of Al{sub 3}Zr dispersoids were obtained with two-step homogenization treatments. The most effective dispersoid distribution was attained using the first step held at 300 °C. In addition, the two-step homogenization minimized the precipitate free zonesmore » and greatly increased the number density of dispersoids near dendrite grain boundaries. The effect of two-step homogenization on recrystallization resistance of 7150 alloys with different Zr contents was quantitatively analyzed using the electron backscattered diffraction (EBSD) technique. It was found that the improved dispersoid distribution through the two-step treatment can effectively inhibit the recrystallization process during the post-deformation annealing for 7150 alloys containing 0.04–0.09 wt.% Zr, resulting in a remarkable reduction of the volume fraction and grain size of recrystallization grains. - Highlights: • Effect of two-step homogenization on Al{sub 3}Zr dispersoids was investigated by TEM. • Finer and higher number of dispersoids obtained with two-step homogenization • Minimized the precipitate free zones and improved the dispersoid distribution • Recrystallization resistance with varying Zr content was quantified by EBSD. • Effectively inhibit the recrystallization through two-step treatments in 7150 alloy.« less

Effect of Carbon Nanotube on High-Temperature Formability of AZ31 Magnesium Alloy

NASA Astrophysics Data System (ADS)

Hassan, S. Fida; Paramsothy, M.; Gasem, Z. M.; Patel, F.; Gupta, M.

2014-08-01

Room-temperature tensile properties of AZ31 alloy have significantly been improved when reinforced with carbon nanotube via ingot metallurgy process. However, high-temperature (up to 250 °C) elongation-to-failure tensile test of the developed nanocomposite revealed a considerable softening in the AZ31 alloy matrix accompanied by an incredible ductility increment (up to 132%). Microstructural characterization of the fractured samples revealed that the dynamic recrystallization process has induced a complete recrystallization in the AZ31 alloy at a lower temperature (150 °C) followed by substantial grain growth at a higher temperature used in this study. Fractography on the fractured surfaces revealed that the room-temperature mixed brittle-ductile modes of fracture behavior of AZ31 alloy have transformed into a complete ductile mode of fracture at high temperature.

Plastic Flow and Microstructure Evolution during Thermomechanical Processing of a PM Nickel-Base Superalloy

NASA Astrophysics Data System (ADS)

Semiatin, S. L.; McClary, K. E.; Rollett, A. D.; Roberts, C. G.; Payton, E. J.; Zhang, F.; Gabb, T. P.

2013-06-01

Plastic flow and microstructure evolution during sub- and supersolvus forging and subsequent supersolvus heat treatment of the powder-metallurgy superalloy LSHR (low-solvus, high-refractory) were investigated to develop an understanding of methods that can be used to obtain a moderately coarse gamma grain size under well-controlled conditions. To this end, isothermal, hot compression tests were conducted over broad ranges of temperature [(1144 K to 1450 K) 871 °C to 1177 °C] and constant true strain rate (0.0005 to 10 s-1). At low temperatures, deformation was generally characterized by flow softening and dynamic recrystallization that led to a decrease in grain size. At high subsolvus temperatures and low strain rates, steady-state flow or flow hardening was observed. These latter behaviors were ascribed to superplastic deformation and microstructure evolution characterized by a constant grain size or concomitant dynamic grain growth, respectively. During supersolvus heat treatment following subsolvus deformation, increases in grain size whose magnitude was a function of the prior deformation conditions were noted. A transition in flow behavior from superplastic to nonsuperplastic and the development during forging at a high subsolvus temperature of a wide (possibly bi- or multimodal) gamma-grain-size distribution having some large grains led to a substantially coarser grain size during supersolvus annealing in comparison to that produced under all other forging conditions.

Microstructural Evolutions During Reversion Annealing of Cold-Rolled AISI 316 Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Naghizadeh, Meysam; Mirzadeh, Hamed

2018-03-01

Microstructural evolutions during reversion annealing of a plastically deformed AISI 316 stainless steel were investigated and three distinct stages were identified: the reversion of strain-induced martensite to austenite, the primary recrystallization of the retained austenite, and the grain growth process. It was found that the slow kinetics of recrystallization at lower annealing temperatures inhibit the formation of an equiaxed microstructure and might effectively impair the usefulness of this thermomechanical treatment for the objective of grain refinement. By comparing the behavior of AISI 316 and 304 alloys, it was found that the mentioned slow kinetics is related to the retardation effect of solute Mo in the former alloy. At high reversion annealing temperature, however, an equiaxed austenitic microstructure was achieved quickly in AISI 316 stainless steel due to the temperature dependency of retardation effect of molybdenum, which allowed the process of recrystallization to happen easily. Conclusively, this work can shed some light on the issues of this efficient grain refining approach for microstructural control of austenitic stainless steels.

Deformation, recrystallization, strength, and fracture of press-forged ceramic crystals.

NASA Technical Reports Server (NTRS)

Rice, R. W.

1972-01-01

Sapphire and ruby were very difficult to press-forge because they deformed without cracking only in a limited temperature range before they melted. Spinel crystals were somewhat easier and MgO, CaO, and TiC crystals much easier to forge. The degree of recrystallization that occurred during forging (which was related to the ease and type of slip intersections) varied from essentially zero in Al2O3 to complete (i.e., random polycrystalline bodies were produced) in CaO. Forging of bi- and polycrystalline bodies produced incoherent bodies as a result of grain-boundary sliding. Strengths of the forged crystals were comparable to those of dense polycrystalline bodies of similar grain size. However, forged and recrystallized CaO crystals were ductile at lower temperatures than dense hot-pressed CaO. This behavior is attributed to reduced grain-boundary impurities and porosity. Fracture origins could be located, indicating that fracture in the CaO occurs internally as a result of surface work hardening caused by machining.-

Oxide Dissolution and Oxygen Diffusion in Solid-State Recycled Ti-6Al-4V: Numerical Modeling, Verification by Nanoindentation, and Effects on Grain Growth and Recrystallization

NASA Astrophysics Data System (ADS)

Lui, E. W.; Palanisamy, S.; Dargusch, M. S.; Xia, K.

2017-12-01

The oxide dissolution and oxygen diffusion during annealing of Ti-6Al-4V solid-state recycled from machining chips by equal-channel angular pressing (ECAP) have been investigated using nanoindentation and numerical modeling. The hardness profile from nanoindentation was converted into the oxygen concentration distribution using the Fleisher and Friedel model. An iterative fitting method was then employed to revise the ideal model proposed previously, leading to correct predictions of the oxide dissolution times and oxygen concentration profiles and verifying nanoindentation as an effective method to measure local oxygen concentrations. Recrystallization started at the prior oxide boundaries where local strains were high from the severe plastic deformation incurred in the ECAP recycling process, forming a band of ultrafine grains whose growth was retarded by solute dragging thanks to high oxygen concentrations. The recrystallized fine-grained region would advance with time to eventually replace the lamellar structure formed during ECAP.

Microstructural Evolutions During Reversion Annealing of Cold-Rolled AISI 316 Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Naghizadeh, Meysam; Mirzadeh, Hamed

2018-06-01

Microstructural evolutions during reversion annealing of a plastically deformed AISI 316 stainless steel were investigated and three distinct stages were identified: the reversion of strain-induced martensite to austenite, the primary recrystallization of the retained austenite, and the grain growth process. It was found that the slow kinetics of recrystallization at lower annealing temperatures inhibit the formation of an equiaxed microstructure and might effectively impair the usefulness of this thermomechanical treatment for the objective of grain refinement. By comparing the behavior of AISI 316 and 304 alloys, it was found that the mentioned slow kinetics is related to the retardation effect of solute Mo in the former alloy. At high reversion annealing temperature, however, an equiaxed austenitic microstructure was achieved quickly in AISI 316 stainless steel due to the temperature dependency of retardation effect of molybdenum, which allowed the process of recrystallization to happen easily. Conclusively, this work can shed some light on the issues of this efficient grain refining approach for microstructural control of austenitic stainless steels.

Microstructural evolution during thermal annealing of ice-Ih

NASA Astrophysics Data System (ADS)

Hidas, Károly; Tommasi, Andréa; Mainprice, David; Chauve, Thomas; Barou, Fabrice; Montagnat, Maurine

2017-06-01

We studied the evolution of the microstructure of ice-Ih during static recrystallization by stepwise annealing experiments. We alternated thermal annealing and electron backscatter diffraction (EBSD) analyses on polycrystalline columnar ice pre-deformed in uniaxial compression at temperature of -7 °C to macroscopic strains of 3.0-5.2. Annealing experiments were carried out at -5 °C and -2 °C up to a maximum of 3.25 days, typically in 5-6 steps. EBSD crystal orientation maps obtained after each annealing step permit the description of microstructural changes. Decrease in average intragranular misorientation at the sample scale and modification of the misorientation across subgrain boundaries provide evidence for recovery from the earliest stages of annealing. This initial evolution is similar for all studied samples irrespective of their initial strain or annealing temperature. After an incubation period ≥1.5 h, recovery is accompanied by recrystallization (nucleation and grain boundary migration). Grain growth proceeds at the expense of domains with high intragranular misorientations, consuming first the most misorientated parts of primary grains. Grain growth kinetics fits the parabolic growth law with grain growth exponents in the range of 2.4-4.0. Deformation-induced tilt boundaries and kink bands may slow down grain boundary migration. They are stable features during early stages of static recrystallization, only erased by normal growth, which starts after >24 h of annealing.

Influence of intermediate annealing on abnormal Goss grain growth in the rolled columnar-grained Fe-Ga-Al alloys

NASA Astrophysics Data System (ADS)

Liu, Yangyang; Li, Jiheng; Gao, Xuexu

2017-08-01

Magnetostrictive Fe82Ga4.5Al13.5 sheets with 0.1 at% NbC were prepared from directional solidified alloys with <0 0 1> preferred orientation. The slabs were hot rolled at 650 °C and warm rolled at 500 °C. Then some warm-rolled sheets were annealed intermediately at 850 °C for 5 min but the others not. After that, all the sheets were cold rolled to a final thickness of ∼0.3 mm. The microstructures, the textures and the distributions of second phase particles in the primary recrystallized samples were investigated. With intermediate annealing, the inhomogeneous microstructure was improved remarkably and strong Goss ({1 1 0}<0 0 1>) and γ-fiber (<1 1 1>//normal direction [ND]) textures were produced in the primary recrystallized samples. But, an evident disadvantage in size and quantity was observed for Goss grains in the primary recrystallized sample without intermediate annealing. After a final annealing, the final textures and magnetostrictions of samples with and without intermediate annealing were characterized. For samples without intermediate annealing, abnormal growth of {1 1 3} grains occurred and deteriorated the magnetostriction. In contrast, abnormal Goss grain growth occurred completely in samples with intermediate annealing and led to saturation magnetostriction as high as 156 ppm.

Thermomechanical processing of aluminum micro-alloyed with Sc, Zr, Ti, B, and C

NASA Astrophysics Data System (ADS)

McNamara, Cameron T.

Critical exploration of the minimalistic high strength low alloy aluminum (HSLA-Al) paradigm is necessary for the continued development of advanced aluminum alloys. In this study, scandium (Sc) and zirconium (Zr) are examined as the main precipitation strengthening additions, while magnesium (Mg) is added to probe the synergistic effects of solution and precipitation hardening, as well as the grain refinement during solidification afforded by a moderate growth restriction factor. Further, pathways of recrystallization are explored in several potential HSLA-Al syste =ms sans Sc. Aluminum-titanium-boron (Al-Ti-B) and aluminum-titanium-carbon (Al-Ti-C) grain refining master alloys are added to a series of Al-Zr alloys to examine both the reported Zr poisoning effect on grain size reduction and the impact on recrystallization resistance through the use of electron backscattered diffraction (EBSD) imaging. Results include an analysis of active strengthening mechanisms and advisement for both constitution and thermomechanical processing of HSLA-Al alloys for wrought or near-net shape cast components. The mechanisms of recrystallization are discussed for alloys which contain a bimodal distribution of particles, some of which act as nucleation sites for grain formation during annealing and others which restrict the growth of the newly formed grains.

Shock-induced fine-grained recrystallization of olivine - Evidence against subsolidus reduction of Fe/2+/

NASA Technical Reports Server (NTRS)

Ahrens, T. J.; Tsay, F.-D.; Live, D. H.

1976-01-01

Electron spin resonance (ESR) studies have been carried out on three single grains of terrestrial olivine (Fo90) shock loaded along the 010 line to peak pressures of 280, 330, and 440 kbar. The results indicate that neither metallic Fe similar to that observed in returned lunar soils nor paramagnetic Fe(3+) caused by oxidation of Fe(2+) has been produced in these shock experiments. Trace amounts of Mn (2+) have been detected in both shocked and unshocked olivine. The ESR signals of Mn(2+) show spectral features which are found to correlate with the degree of shock-induced recrystallization observed petrographically. The increasing mass fraction of recrystallized olivine correlates with increasing shock pressures. This phenomenon is modelled assuming it results from the progressive effect of the shock-induced transformation of the olivine to a yet unknown high-pressure phase and its subsequent reversion to the low-pressure olivine phase. The mass fraction of recrystallized material is predicted to be nearly linear with shock pressure.

Stress dependence of microstructures in experimentally deformed calcite

NASA Astrophysics Data System (ADS)

Platt, John P.; De Bresser, J. H. P.

2017-12-01

Optical measurements of microstructural features in experimentally deformed Carrara marble help define their dependence on stress. These features include dynamically recrystallized grain size (Dr), subgrain size (Sg), minimum bulge size (Lρ), and the maximum scale length for surface-energy driven grain-boundary migration (Lγ). Taken together with previously published data Dr defines a paleopiezometer over the range 15-291 MPa and temperature over the range 500-1000 °C, with a stress exponent of -1.09 (CI -1.27 to -0.95), showing no detectable dependence on temperature. Sg and Dr measured in the same samples are closely similar in size, suggesting that the new grains did not grow significantly after nucleation. Lρ and Lγ measured on each sample define a relationship to stress with an exponent of approximately -1.6, which helps define the boundary between a region of dominant strain-energy-driven grain-boundary migration at high stress, from a region of dominant surface-energy-driven grain-boundary migration at low stress.

Kinetics of Sub-Micron Grain Size Refinement in 9310 Steel

NASA Astrophysics Data System (ADS)

Kozmel, Thomas; Chen, Edward Y.; Chen, Charlie C.; Tin, Sammy

2014-05-01

Recent efforts have focused on the development of novel manufacturing processes capable of producing microstructures dominated by sub-micron grains. For structural applications, grain refinement has been shown to enhance mechanical properties such as strength, fatigue resistance, and fracture toughness. Through control of the thermo-mechanical processing parameters, dynamic recrystallization mechanisms were used to produce microstructures consisting of sub-micron grains in 9310 steel. Starting with initial bainitic grain sizes of 40 to 50 μm, various levels of grain refinement were observed following hot deformation of 9310 steel samples at temperatures and strain rates ranging from 755 K to 922 K (482 °C and 649 °C) and 1 to 0.001/s, respectively. The resulting deformation microstructures were characterized using scanning electron microscopy and electron backscatter diffraction techniques to quantify the extent of carbide coarsening and grain refinement occurring during deformation. Microstructural models based on the Zener-Holloman parameter were developed and modified to include the effect of the ferrite/carbide interactions within the system. These models were shown to effectively correlate microstructural attributes to the thermal mechanical processing parameters.

Prediction of the Grain-Microstructure Evolution Within a Friction Stir Welding (FSW) Joint via the Use of the Monte Carlo Simulation Method

NASA Astrophysics Data System (ADS)

Grujicic, M.; Ramaswami, S.; Snipes, J. S.; Avuthu, V.; Galgalikar, R.; Zhang, Z.

2015-09-01

A thermo-mechanical finite element analysis of the friction stir welding (FSW) process is carried out and the evolution of the material state (e.g., temperature, the extent of plastic deformation, etc.) monitored. Subsequently, the finite-element results are used as input to a Monte-Carlo simulation algorithm in order to predict the evolution of the grain microstructure within different weld zones, during the FSW process and the subsequent cooling of the material within the weld to room temperature. To help delineate different weld zones, (a) temperature and deformation fields during the welding process, and during the subsequent cooling, are monitored; and (b) competition between the grain growth (driven by the reduction in the total grain-boundary surface area) and dynamic-recrystallization grain refinement (driven by the replacement of highly deformed material with an effectively "dislocation-free" material) is simulated. The results obtained clearly revealed that different weld zones form as a result of different outcomes of the competition between the grain growth and grain refinement processes.

Recrystallization and grain growth in NiAl

NASA Technical Reports Server (NTRS)

Haff, G. R.; Schulson, E. M.

1982-01-01

Aluminide intermetallics, because of their strength, microstructural stability, and oxidation resistance at elevated temperatures, represent potential structural materials for use in advanced energy conversion systems. This inherent potential of the intermetallics can currently not be realized in connection with the general brittleness of the materials under ambient conditions. It is pointed out, however, that brittleness is not an inherent characteristic. Single crystals are ductile and polycrystals may be, too, if their grains are fine enough. The present investigation is concerned with an approach for reducing material brittleness, taking into account thermal-mechanically induced grain refinement in NiAl, a B2 aluminide which melts at 1638 C and which retains complete order to its melting point. Attention is given to the kinetics of recrystallization and grain growth of warm-worked, nickel-rich material.

Enhancement of ductility and improvement of abnormal Goss grain growth of magnetostrictive Fe-Ga rolled alloys

NASA Astrophysics Data System (ADS)

Li, Ji-heng; Yuan, Chao; Mu, Xing; Bao, Xiao-qian; Gao, Xue-xu

2018-04-01

The influences of initial microstructures on the mechanical properties and the recrystallization texture of magnetostrictive 0.1at% NbC-doped Fe83Ga17 alloys were investigated. The directionally solidified columnar-grained structure substantially enhanced the tensile elongation at intermediate temperatures by suppressing fracture along the transverse boundaries. Compared with tensile elongations of 1.0% at 300°C and 12.0% at 500°C of the hot-forged equiaxed-grained alloys, the columnar-grained alloys exhibited substantially increased tensile elongations of 21.6% at 300°C and 46.6% at 500°C. In the slabs for rolling, the introduction of <001>-oriented columnar grains also promotes the secondary recrystallization of Goss grains in the finally annealed sheets, resulting in an improvement of the saturation magnetostriction. For the columnar-grained specimens, the inhomogeneous microstructure and disadvantage in number and size of Goss grains are improved in the primarily annealed sheets, which is beneficial to the abnormal growth of Goss grains during the final annealing process.

High-Burnup-Structure (HBS): Model Development in MARMOT for HBS Formation and Stability Under Radiation and High Temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ahmed, K.; Bai, X.; Zhang, Y.

2016-09-01

A detailed phase field model for the formation of High Burnup Structure (HBS) was developed and implemented in MARMOT. The model treats the HBS formation as an irradiation-induced recrystallization. The model takes into consideration the stored energy associated with dislocations formed under irradiation. The accumulation of radiation damage, hence, increases the system free energy and triggers recrystallization. The increase in the free energy due to the formation of new grain boundaries is offset by the reduction in the free energy by creating dislocation-free grains at the expense of the deformed grains. The model was first used to study the growthmore » of recrystallized flat and circular grains. The model reults were shown to agree well with theorrtical predictions. The case of HBS formation in UO2 was then investigated. It was found that a threshold dislocation density of (or equivalently a threshold burn-up of 33-40 GWd/t) is required for HBS formation at 1200K, which is in good agrrement with theory and experiments. In future studies, the presence of gas bubbles and their effect on the formation and evolution of HBS will be considered.« less

Unstable plastic deformation of ultrafine-grained copper at 0.5 K

NASA Astrophysics Data System (ADS)

Isaev, N. V.; Grigorova, T. V.; Shumilin, S. E.; Polishchuk, S. S.; Davydenko, O. A.

2017-12-01

We investigate the relation between the strain-hardening rate and flow instability of polycrystalline Cu-OF deformed by tension at a constant rate in a liquid 3He atmosphere. The microstructure of the ultrafine-grained crystal, obtained by the equal-channel angular hydro-extrusion method, was varied by annealing at recovery and recrystallization temperatures and was monitored by x-ray diffraction. It is shown that that the flow instability, manifesting itself as macroscopic stress serrations on the tension curve, appears at a threshold tension sufficient for activation of a dynamic recovery that leads to a decrease of the strain-hardening coefficient. We discuss the effect of grain size and the initial dislocation density on the evolution of the dislocation structure that determines the scale and the statistical properties of the flow instability in the investigated crystals at low temperature.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Myers, M.A.; LaSalvia, J.C.; Hoke, D.

Combustion synthesis followed by densification was utilized in producing monolithic TiC and TiB2 materials, and TiC-Ni, TiB2-Ni, TiB2-Al2O3, and TiB2SiC ceramic composites. Static and dynamic densification equipments were developed with the loading applied immediately after the synthesis reaction was completed and the ceramic/composite was ductile. All the ceramics exhibited an equiaxed grain structure with alternating regions at high and low dislocation densities, indicating that recovery/recrystallization mechanisms are prevalent. The grain boundaries were, as far as could be established, devoid of impurities and second phases. Quasi-static and dynamic mechanical testing were performed and revealed that the materials exhibited strength levels comparablemore » to conventionally produced materials. Instrumented densification experiments were conducted and a temperature-dependent consitutive model was applied for plastic deformation of the porous combustion synthesis product.« less

Effects of V addition on recrystallization resistance of 7150 aluminum alloy after simulative hot deformation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lai, Jing; Shi, Cangji; Chen, X.-Grant, E-mail: xgrant_chen@uqac.ca

2014-10-15

The effects of different V contents (0.01 to 0.19 wt.%) on the recrystallization resistance of 7150 aluminum alloys during post-deformation heat treatment were investigated. The microstructural evolutions at as-cast, as-homogenized conditions and after post-deformation annealing were studied using optical, scanning electron and transmission electron microscopes and using the electron backscattered diffraction technique. The precipitation of Al{sub 21}V{sub 2} dispersoids was observed in alloys containing 0.11 to 0.19 wt.% V after homogenization. The dispersoids were mainly distributed in the dendrite cells, and the precipitate-free zones occurred in the interdendritic regions and near grain boundaries. V addition could significantly enhance the recrystallizationmore » resistance during post-deformation annealing, particularly in the presence of a great number of Al{sub 21}V{sub 2} dispersoids. Recrystallized grain growth was effectively restricted because of the dispersoid pinning effect. The alloy containing 0.15 wt.% V exhibited the highest recrystallization resistance amongst all V-containing alloys studied. - Highlights: • Investigated the effect of V level on microstructure and flow stress of 7150 alloys • Characterized microstructures using optical microscopy, SEM, TEM and EBSD • Described the precipitation behavior of V-dispersoids in the dendritic structure • Studied the V effect on recrystallization resistance during post heat treatment • V addition greatly enhanced the recrystallization resistance during annealing.« less

Dynamic Grain Growth in Forsterite Aggregates Experimentally Deformed to High Strain

NASA Astrophysics Data System (ADS)

Kellermann Slotemaker, A.; de Bresser, H.; Spiers, C.; Drury, M.

2004-12-01

The dynamics of the outer Earth are largely controlled by olivine rheology. From previous work it has become clear that if olivine rocks are deformed to high strain, substantial weakening may occur before steady state mechanical behaviour is approached. This weakening appears directly related to progressive modification of the grain size distribution through competing effects of dynamic recrystallization and syn-deformational grain growth. However, most of our understanding of these processes in olivine comes from tests on coarse-grained materials that were reduced in grain size during straining by grain size insensitive (dislocation) creep mechanisms. The aim of the present study was to investigate microstructure evolution of fine-grained olivine rocks that coarsen in grain size while deforming by grain size sensitive (GSS) creep. We used fine-grained (~1 μ m) olivine aggregates (i.e., forsterite/Mg2SiO4), containing ~0.5 wt% water and 10 vol% enstatite (MgSiO3). Two types of experiments were carried out: 1) Hot isostatic pressing (HIP) followed by axial compression to varying strains up to a maximum of ~45%, at 600 MPa confining pressure and a temperature of 950°C, 2) HIP treatment without axial deformation. Microstructures were characterized by analyzing full grain size distributions and texture using SEM/EBSD. Our stress-strain curves showed continuous hardening. When samples were temporally unloaded for short time intervals, no difference in flow stress was observed before and after the interruption in straining. Strain rate sensitivity analysis showed a low value of ~1.5 for the stress exponent n. Measured grain sizes show an increase with strain up to a value twice that of the starting value. HIP-only samples showed only minor increase in grain size. A random LPO combined with the low n ~1.5 suggests dominant GSS creep controlled by grain boundary sliding. These results indicate that dynamic grain growth occurs in forsterite aggregates deforming by GSS creep, and we relate the continuous strain hardening to this process. A dynamic grain growth model involving an increase in cellular defect fraction seems best applicable to the grain growth observed in this study. We suggest that the employment of this model to fine-grained olivine rocks can further improve our understanding of the microstructural evolution of this material and related rheological behaviour.

Relations and interactions between twinning and grain boundaries in hexagonal close-packed structures

NASA Astrophysics Data System (ADS)

Barrett, Christopher Duncan

Improving the formability and crashworthiness of wrought magnesium alloys are the two biggest challenges in current magnesium technology. Magnesium is the best material candidate for enabling required improvements in fuel economy of combustion engines and increases in ranges of electric vehicles. In hexagonal closed-packed (HCP) structures, effects of grain size/morphology and crystallographic texture are particularly important. Prior research has established a general understanding of the dependences of strength and strain anisotropy on grain morphology and texture. Unfortunately, deformation, recrystallization, and grain growth strategies that control the microstructures and textures of cubic metals and alloys have not generally worked for HCPs. For example, in Magnesium, the deformation texture induced by primary forming operations (rolling, extrusion, etc.) is not randomized by recrystallization and may strengthen during grain growth. A strong texture reduces formability during secondary forming (stamping, bending, hemming etc.) Thus, the inability to randomize texture has impeded the implementation of magnesium alloys in engineering applications. When rare earth solutes are added to magnesium alloys, distinct new textures are derived. However, `rare earth texture' derivation remains insufficiently explained. Currently, it is hypothesized that unknown mechanisms of alloy processing are at work, arising from the effects of grain boundary intrinsic defect structures on microstructural evolution. This dissertation is a comprehensive attempt to identify formal methodologies of analyzing the behavior of grain boundaries in magnesium. We focus particularly on twin boundaries and asymmetric tilt grain boundaries using molecular dynamics. We begin by exploring twin nucleation in magnesium single crystals, elucidating effects of heterogeneities on twin nucleation and their relationships with concurrent slip. These efforts highlighted the necessity of imperfections to nucleate {10-12} twins. Subsequent studies encountered the importance of deformation faceting on the high mobility of {10-12} and stabilization of observed twin mode boundaries. Implementation of interfacial defect theory was necessary to decipher the complex mechanisms observed which govern the development of defects in grain boundaries, disconnection pile-up, facet nucleation, interfacial disclination nucleation, disconnection movements, disconnection transformation across interfacial disclinations, cross-faceting, and byproducts of interactions between lattice dislocations and grain boundaries.

Hot deformation behavior of uniform fine-grained GH4720Li alloy based on its processing map

NASA Astrophysics Data System (ADS)

Yu, Qiu-ying; Yao, Zhi-hao; Dong, Jian-xin

2016-01-01

The hot deformation behavior of uniform fine-grained GH4720Li alloy was studied in the temperature range from 1040 to 1130°C and the strain-rate range from 0.005 to 0.5 s-1 using hot compression testing. Processing maps were constructed on the basis of compression data and a dynamic materials model. Considerable flow softening associated with superplasticity was observed at strain rates of 0.01 s-1 or lower. According to the processing map and observations of the microstructure, the uniform fine-grained microstructure remains intact at 1100°C or lower because of easily activated dynamic recrystallization (DRX), whereas obvious grain growth is observed at 1130°C. Metallurgical instabilities in the form of non-uniform microstructures under higher and lower Zener-Hollomon parameters are induced by local plastic flow and primary γ' local faster dissolution, respectively. The optimum processing conditions at all of the investigated strains are proposed as 1090-1130°C with 0.08-0.5 s-1 and 0.005-0.008 s-1 and 1040-1085°C with 0.005-0.06 s-1.

Microstructure and Mechanical Characterization of Friction-Stir-Welded Dual-Phase Brass

NASA Astrophysics Data System (ADS)

Ramesh, R.; Dinaharan, I.; Akinlabi, E. T.; Murugan, N.

2018-03-01

Friction stir welding (FSW) is an ideal process to join brass to avoid the evaporation of zinc. In the present investigation, 6-mm-thick dual-phase brass plates were joined efficiently using FSW at various tool rotational speeds. The microstructures were studied using optical microscopy, electron backscattered diffraction and transmission electron microscopy. The optical micrographs revealed the evolution of various zones across the joint line. The microstructure of the heat-affected zone was similar to that of base metal. The weld zone exhibited finer grains due to dynamic recrystallization. The recrystallization was inhomogeneous and the inhomogeneity reduced with increased tool rotational speed. The dual phase was preserved in the weld zone due to the retention of zinc. The severe plastic deformation created a lot of dislocations in the weld zone. The weld zone was strengthened after welding. The role of tool rotational speed on the joint strength is further reported.

Grain Growth and Precipitation Behavior of Iridium Alloy DOP-26 During Long Term Aging

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pierce, Dean T.; Muralidharan, Govindarajan; Fox, Ethan E.

The influence of long term aging on grain growth and precipitate sizes and spatial distribution in iridium alloy DOP-26 was studied. Samples of DOP-26 were fabricated using the new process, recrystallized for 1 hour (h) at 1375 C, then aged at either 1300, 1400, or 1500 C for times ranging from 50 to 10,000 h. Grain size measurements (vertical and horizontal mean linear intercept and horizontal and vertical projection) and analyses of iridium-thorium precipitates (size and spacing) were made on the longitudinal, transverse, and rolling surfaces of the as-recrystallized and aged specimens from which the two-dimensional spatial distribution and meanmore » sizes of the precipitates were obtained. The results obtained from this study are intended to provide input to grain growth models.« less

Modeling of the static recrystallization for 7055 aluminum alloy by cellular automaton

NASA Astrophysics Data System (ADS)

Zhang, Tao; Lu, Shi-hong; Zhang, Jia-bin; Li, Zheng-fang; Chen, Peng; Gong, Hai; Wu, Yun-xin

2017-09-01

In order to simulate the flow behavior and microstructure evolution during the pass interval period of the multi-pass deformation process, models of static recovery (SR) and static recrystallization (SRX) by the cellular automaton (CA) method for the 7055 aluminum alloy were established. Double-pass hot compression tests were conducted to acquire flow stress and microstructure variation during the pass interval period. With the basis of the material constants obtained from the compression tests, models of the SR, incubation period, nucleation rate and grain growth were fitted by least square method. A model of the grain topology and a statistical computation of the CA results were also introduced. The effects of the pass interval time, temperature, strain, strain rate and initial grain size on the microstructure variation for the SRX of the 7055 aluminum alloy were studied. The results show that a long pass interval time, large strain, high temperature and large strain rate are beneficial for finer grains during the pass interval period. The stable size of the static recrystallized grain is not concerned with the initial grain size, but mainly depends on the strain rate and temperature. The SRX plays a vital role in grain refinement, while the SR has no effect on the variation of microstructure morphology. Using flow stress and microstructure comparisons of the simulated and experimental CA results, the established CA models can accurately predict the flow stress and microstructure evolution during the pass interval period, and provide guidance for the selection of optimized parameters for the multi-pass deformation process.

Effect of the Rate of Hot Compressive Deformation on the Kinetics of Dynamic and Static Recrystallization of Novel Medium-Carbon Medium-Alloy Steel

NASA Astrophysics Data System (ADS)

Khlusova, E. I.; Zisman, A. A.; Knyazyuk, T. V.; Novoskol'tsev, N. N.

2018-03-01

Dynamic and static recrystallization occurring under hot deformation at a rate of 1 and 100 sec - 1 in high-strength medium-carbon wear-resistant steels developed at CRISM "Prometey" for die forming of parts of driven elements of tillage machines is studied. The critical strain of dynamic recrystallization and the threshold temperatures and times of finish of static recrystallization are determined for the studied deformation rates at various temperatures.

Subgrain Rotation Recrystallization During Shearing: Insights From Full-Field Numerical Simulations of Halite Polycrystals

NASA Astrophysics Data System (ADS)

Gomez-Rivas, E.; Griera, A.; Llorens, M.-G.; Bons, P. D.; Lebensohn, R. A.; Piazolo, S.

2017-11-01

We present, for the first time, results of full-field numerical simulations of subgrain rotation recrystallization of halite polycrystals during simple shear deformation. The series of simulations show how microstructures are controlled by the competition between (i) grain size reduction by creep by dislocation glide and (ii) intracrystalline recovery encompassing subgrain coarsening by coalescence through rotation and alignment of the lattices of neighboring subgrains. A strong grain size reduction develops in models without intracrystalline recovery, as a result of the formation of high-angle grain boundaries when local misorientations exceed 15°. The activation of subgrain coarsening associated with recovery decreases the stored strain energy and results in grains with low intracrystalline heterogeneities. However, this type of recrystallization does not significantly modify crystal preferred orientations. Lattice orientation and grain boundary maps reveal that this full-field modeling approach is able to successfully reproduce the evolution of dry halite microstructures from laboratory deformation experiments, thus opening new opportunities in this field of research. We demonstrate how the mean subgrain boundary misorientations can be used to estimate the strain accommodated by dislocation glide using a universal scaling exponent of about 2/3, as predicted by theoretical models. In addition, this strain gauge can be potentially applied to estimate the intensity of intracrystalline recovery, associated with temperature, using quantitative crystallographic analyses in areas with strain gradients.

Strain Amount Dependent Grain Size and Orientation Developments during Hot Compression of a Polycrystalline Nickel Based Superalloy

PubMed Central

He, Guoai; Tan, Liming; Liu, Feng; Huang, Lan; Huang, Zaiwang; Jiang, Liang

2017-01-01

Controlling grain size in polycrystalline nickel base superalloy is vital for obtaining required mechanical properties. Typically, a uniform and fine grain size is required throughout forging process to realize the superplastic deformation. Strain amount occupied a dominant position in manipulating the dynamic recrystallization (DRX) process and regulating the grain size of the alloy during hot forging. In this article, the high-throughput double cone specimen was introduced to yield wide-range strain in a single sample. Continuous variations of effective strain ranging from 0.23 to 1.65 across the whole sample were achieved after reaching a height reduction of 70%. Grain size is measured to be decreased from the edge to the center of specimen with increase of effective strain. Small misorientation tended to generate near the grain boundaries, which was manifested as piled-up dislocation in micromechanics. After the dislocation density reached a critical value, DRX progress would be initiated at higher deformation region, leading to the refinement of grain size. During this process, the transformations from low angle grain boundaries (LAGBs) to high angle grain boundaries (HAGBs) and from subgrains to DRX grains are found to occur. After the accomplishment of DRX progress, the neonatal grains are presented as having similar orientation inside the grain boundary. PMID:28772514

Microstructure, Texture and Mechanical Properties of Titanium Grade 2 Processed by ECAP (Route C)

NASA Astrophysics Data System (ADS)

Wroński, M.; Wierzbanowski, K.; Wojtas, D.; Szyfner, E.; Valiev, R. Z.; Kawałko, J.; Berent, K.; Sztwiertnia, K.

2018-03-01

In the present work the properties of titanium grade 2 after ECAP processing with original route and regimes (route C, channel angle Φ= 120°, deformation temperature 300 °C, number of passes up to 8) were examined. Texture development and microstructure parameters after ECAP processing and after recrystallization were determined using electron back scatter diffraction and analysed. A significant increase of the mechanical strength accompanied by some increase of ductility was observed in the deformed samples. The kernel average misorientation and average grain orientation spread were strongly increased after deformation, which confirms the material refinement and fragmentation. The proportion of low angle boundaries increased after four ECAP passes, but after four consecutive passes high angle grain boundaries became predominant. No deformation twins were observed after four and eight ECAP passes. The material recrystallized after deformation retained a fine grain microstructure. The textures of deformed and recrystallized samples were determined. It was found that texture after 8 passes is more homogeneous that that after 4 passes, which partly explains higher ductility of this first sample.

Microstructural analysis of the thermal annealing of ice-Ih using EBSD

NASA Astrophysics Data System (ADS)

Hidas, Károly; Tommasi, Andréa; Mainprice, David; Chauve, Thomas; Barou, Fabrice; Montagnat, Maurine

2017-04-01

Rocks deformed in the middle crust and deeper in the Earth typically remain at high temperature for extended time spans after the cessation of deformation. This results in annealing of the deformation microstructure by a series of thermally activated, diffusion-based processes, namely: recovery and static recrystallization, which may also modify the crystal preferred orientation (CPO) or texture. Understanding the effects of annealing on the microstructure and CPO is therefore of utmost importance for the interpretation of the microstructures and for the estimation of the anisotropy of physical properties of lower crustal and mantle rocks. Ice-Ih -the typical form of water ice on the Earth's surface, with hexagonal crystal symmetry- deforms essentially by glide of dislocations on the basal plane [1], thus it has high viscoplastic anisotropy, which induces strong heterogeneity of stresses and strains at both the intra- and intergranular scales [2-3]. This behavior makes ice-Ih an excellent analog material for silicate minerals that compose the Earth. In situ observations of the evolution of the microstructures and CPO during annealing enable the study of the interplay between the various physical processes involved in annealing (recovery, nucleation, grain growth). They also allow the analysis of the impact of the preexisting deformation microstructures on the microstructural and CPO evolution during annealing. Here we studied the evolution of the microstructure of ice-Ih during static recrystallization by stepwise annealing experiments. We alternated thermal annealing and electron backscatter diffraction (EBSD) analyses on polycrystalline columnar ice-Ih pre-deformed in uniaxial compression at temperature of -7 °C to strains of 3.0-5.2. Annealing experiments were carried out at -5 °C and -2 °C up to a maximum of 3.25 days, typically in 5-6 steps. EBSD crystal orientation maps obtained after each annealing step permit the description of microstructural changes. Decrease in average intragranular misorientation at the sample scale and modification of the misorientation across subgrain boundaries provide evidence for recovery from the earliest stages of annealing. This evolution is similar for all studied samples irrespective of their initial strain or annealing temperature. After an incubation period up to 2 hours, recovery is accompanied by recrystallization (nucleation and grain boundary migration). Grain growth proceeds at the expense of domains with high intra-granular misorientations and its kinetics fits the parabolic growth law. Deformation-induced microstructures (tilt boundaries and kink bands) are stable features during early stages of static recrystallization and locally slow down grain boundary migration, pinning grain growth. REFERENCES 1. Duval, P., Ashby, M.F., Anderman, I., 1983. Rate-controlling processes in the creep of polycrystalline ice. Journal of Physical Chemistry 87, 4066-4074. 2. Grennerat, F., Montagnat, M., Castelnau, O., Vacher, P., Moulinec, H., Suquet, P., Duval, P., 2012. Experimental characterization of the intragranular strain field in columnar ice during transient creep. Acta Materialia 60, 3655-3666. 3. Chauve, T., Montagnat, M., Vacher, P., 2015. Strain field evolution during dynamic recrystallization nucleation: A case study on ice. Acta Materialia 101, 116-124. Funding: Research leading to these results was funded by the EU-FP7 Marie Curie postdoctoral grant PIEF-GA-2012-327226 to K.H.

Effect of Mn and Cr additions on kinetics of recrystallization and parameters of grain-boundary relaxation of Al-4.9Mg alloy

NASA Astrophysics Data System (ADS)

Mikhailovskaya, A. V.; Golovin, I. S.; Zaitseva, A. A.; Portnoi, V. K.; Dröttboom, P.; Cifre, J.

2013-03-01

Methods of microstructural analysis, measurements of hardness, and temperature and time dependences of internal friction (TDIF and TDIF(iso), respectively) have been used to study recrystallization in cold-rolled alloys and grain-boundary relaxation in annealed alloys. A complex analysis of the effect of additions of transition metals (Mn, Cr) on the magnitude of the activation energy of the background of the internal friction in deformed and annealed states and on the activation parameters of grain-boundary relaxation has been performed. Methods of amplitude dependences of internal friction (ADIF) have been used to determine the critical amplitude that corresponds to the beginning of microplastic deformation in the alloys at different temperatures.

Analysis of Semiconductor Structures by Nuclear and Electrical Techniques.

DTIC Science & Technology

temperatures well below the Si-Al eutectic (577C), fine grained polycrystalline Si in contact with Al films recrystallizes in the Al matrix. The... recrystallization can be deferred or suppressed by placing a buffer layer of V or Ti between the Al film and poly Si. (2) When annealing Pt films deposited on Si

Refinement of Ferrite Grain Size near the Ultrafine Range by Multipass, Thermomechanical Compression

NASA Astrophysics Data System (ADS)

Patra, S.; Neogy, S.; Kumar, Vinod; Chakrabarti, D.; Haldar, A.

2012-11-01

Plane-strain compression testing was carried out on a Nb-Ti-V microalloyed steel, in a GLEEBLE3500 simulator using a different amount of roughing, intermediate, and finishing deformation over the temperature range of 1373 K to 1073 K (1100 °C to 800 °C). A decrease in soaking temperature from 1473 K to 1273 K (1200 °C to 1000 °C) offered marginal refinement in the ferrite ( α) grain size from 7.8 to 6.6 μm. Heavy deformation using multiple passes between A e3 and A r3 with true strain of 0.8 to 1.2 effectively refined the α grain size (4.1 to 3.2 μm) close to the ultrafine size by dynamic-strain-induced austenite ( γ) → ferrite ( α) transformation (DSIT). The intensities of microstructural banding, pearlite fraction in the microstructure (13 pct), and fraction of the harmful "cube" texture component (5 pct) were reduced with the increase in finishing deformation. Simultaneously, the fractions of high-angle (>15 deg misorientation) boundaries (75 to 80 pct), beneficial gamma-fiber (ND//<111>) texture components, along with {332}<133> and {554}<225> components were increased. Grain refinement and the formation of small Fe3C particles (50- to 600-nm size) increased the hardness of the deformed samples (184 to 192 HV). For the same deformation temperature [1103 K (830 °C)], the difference in α-grain sizes obtained after single-pass (2.7 μm) and multipass compression (3.2 μm) can be explained in view of the static- and dynamic-strain-induced γ → α transformation, strain partitioning between γ and α, dynamic recovery and dynamic recrystallization of the deformed α, and α-grain growth during interpass intervals.

Quantification of Microtexture at Weld Nugget of Friction Stir-Welded Carbon Steel

NASA Astrophysics Data System (ADS)

Husain, Md M.; Sarkar, R.; Pal, T. K.; Ghosh, M.; Prabhu, N.

2017-05-01

Friction stir welding of C-Mn steel was carried out under 800-1400 rpm tool rotation. Tool traversing speed of 50 mm/min remained same for all joints. Effect of thermal state and deformation on texture and microstructure at weld nugget was investigated. Weld nugget consisted of ferrite + bainite/Widmanstatten ferrite with different matrix grain sizes depending on peak temperature. A texture around ( ϕ 2 = 0°, φ = 30°, ϕ 2 = 45°) was developed at weld nugget. Grain boundary misorientation at weld nugget indicated that continuous dynamic recrystallization influenced the development of fine equiaxed grain structure. Pole figures and orientation distribution function were used to determine crystallographic texture at weld nugget and base metal. Shear texture components D1, D2 and F were present at weld nugget. D1 shear texture was more prominent among all. Large number of high-angle grain boundaries ( 60-70%) was observed at weld nugget and was the resultant of accumulation of high amount of dislocation, followed by subgrain formation.

Metallurgy and properties of plasma spray formed materials

NASA Technical Reports Server (NTRS)

Mckechnie, T. N.; Liaw, Y. K.; Zimmerman, F. R.; Poorman, R. M.

1992-01-01

Understanding the fundamental metallurgy of vacuum plasma spray formed materials is the key to enhancing and developing full material properties. Investigations have shown that the microstructure of plasma sprayed materials must evolve from a powder splat morphology to a recrystallized grain structure to assure high strength and ductility. A fully, or near fully, dense material that exhibits a powder splat morphology will perform as a brittle material compared to a recrystallized grain structure for the same amount of porosity. Metallurgy and material properties of nickel, iron, and copper base alloys will be presented and correlated to microstructure.

Effect of controlling recrystallization from the melt on the residual stress and structural properties of the Silica-clad Ge core fiber

NASA Astrophysics Data System (ADS)

Zhao, Ziwen; Cheng, Xueli; He, Ting; Xue, Fei; Zhang, Wei; Chen, Na; Wen, Jianxiang; Zeng, Xianglong; Wang, Tingyun

2017-09-01

Effect of controlling recrystallization from the melt (1000 °C) on the residual stress and structural properties of a Ge core fiber via molten core drawing (MCD) method is investigated. Ge core fibers is investigated using Raman spectroscopy, scanning electron microscope (SEM), and X-ray diffraction (XRD). Compared with the as-drawn Ge fiber, the Raman peak of the recrystallized Ge fiber shift from 300 cm-1 to 300.6 cm-1 and full width at half maximum (FWHM) decreased from 5.36 cm-1 to 4.48 cm-1. The Ge crystal grains which sizes are of 200-600 nm were formed during the process of recrystallization; the XRD peak of (1 1 1) plane is observed after recrystallization. These results show that controlling recrystallization allows the release of the thermal stress, and improvement of the crystal quality of Ge core.

Microstructure heterogeneity after the ECAP process and its influence on recrystallization in aluminium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wronski, S., E-mail: wronski@fis.agh.edu.pl; Tarasiuk, J., E-mail: tarasiuk@ftj.agh.edu.pl; Bacroix, B., E-mail: brigitte.bacroix@univ-paris13.fr

The main purpose of the present work is to describe the qualitative and quantitative behaviours of aluminium during high strain plastic deformation and the effect of deformation on the subsequent recrystallization process. An Electron Backscatter Diffraction analysis of aluminium after the Equal channel angular pressing (ECAP) and recrystallization process is presented. In order to do this, several topological maps are measured for samples processed by 4 and 8 passes and recrystallized. The processing was conducted with route C. For all samples, distributions of grain size, misorientation, image quality factor (IQ) and texture were preceded and then analysed in some detail.more » - Highlights: ► Describe the microstructure fragmentation in aluminum. ► High strain plastic deformation and effect of deformation on recrystallization. ► The microstructure fragmentation and its influence on recrystallization. ► Image quality factor and misorientation characteristics are examined using EBSD.« less

The Deformation Behavior and Microstructure Evolution of a Mn- and Cr-Containing Al-Mg-Si-Cu Alloy During Hot Compression and Subsequent Heat Treatment

NASA Astrophysics Data System (ADS)

Xu, Yi; Nagaumi, Hiromi; Han, Yi; Zhang, Gongwang; Zhai, Tongguang

2017-03-01

Hot compression tests on a newly developed Mn- and Cr-containing Al-Mg-Si-Cu alloy were carried out at temperatures ranging from 623 K (350 °C) to 823 K (550 °C) and strain rates between 0.001 and 1 s-1 after casting and subsequent homogenization heat treatment. The true stress-true strain curves of the alloy exhibited a peak stress at a small plastic strain followed by dynamic flow softening. Using the constitutive equation containing the strain rate, peak stress, and temperature, the activation energy for hot deformation in the alloy was determined to be 249.67 kJ/mol, much higher than that (143.4 kJ/mol) for self-diffusion in pure Al. Scanning transmission electron microscopy experiments revealed that Mn- and Cr-containing α-dispersoids formed during homogenization showed a strong pinning effect on dislocations and grain boundaries, which was responsible for the increase in activation energy for hot deformation in the alloy. A threshold stress was consequently introduced and determined in the constitutive equation to count for the dispersoid hardening effect on hot deformation in the alloy. Electron back-scatter diffraction measurements revealed that the softening occurred in the alloy was mainly due to dynamic recovery taking place at relatively large Z values, and that it was dominated by continuous dynamic recrystallization at relatively low Z. In subsequent annealing after hot deformation at large Z, abnormal grain growth could occur, as a result of the critical strain-annealing effect. After upsetting at higher temperatures, the alloy showed superior tensile properties due to a high non-recrystallized area fraction.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Y. B.; Budai, J. D.; Tischler, J. Z.

How boundaries surrounding recrystallization grains migrate through the 3D network of dislocation boundaries in deformed crystalline materials is unknown and critical for the resulting recrystallized crystalline materials. Furthermore, by using X-ray Laue diffraction microscopy, we show for the first time the migration pattern of a typical recrystallization boundary through a well-characterized deformation matrix. The data provide a unique possibility to investigate effects of both boundary misorientation and plane normal on the migration, information which cannot be accessed with any other techniques. Our results show that neither of these two parameters can explain the observed migration behavior. Instead we suggest thatmore » the subdivision of the deformed microstructure ahead of the boundary plays the dominant role. Our experimental observations challenge the assumptions of existing recrystallization theories, and set the stage for determination of mobilities of recrystallization boundaries.« less

Optimized interface and recrystallized grains by CsBr treatment for enhanced photovoltaic performance of perovskite solar cells

NASA Astrophysics Data System (ADS)

Liu, Li; Su, Pengyu; Yao, Huizhen; Wang, Jun; Fu, Wuyou; Liu, Xizhe; Yang, Haibin

2018-06-01

Doping, interface optimization and recrystallization are effective approaches for fabricating high performance perovskite solar cells (PSCs). In our work, simple CsBr treatment is introduced to improve the performance of TiO2 nanorods-based PSCs. Both Cs+ and Br- are doped into CH3NH3PbI3 simultaneously, as well as optimizes the interface between perovskite and hole-transporting material (HTM). In addition, the perovskite grains are recrystallized through this method. Finally, a power conversion efficiency (PCE) of 16.02% with 0.72 in fill factor (FF) and 1.08 in open circuit voltage (VOC) is obtained through CsBr treatment, which is 19.91% higher than that of untreated devices (13.36% with 0.65 in FF and 1.02 in VOC). Furthermore, the power output maintains ∼14% after 3500 h under the humidity within 15% at room temperature.

Microstructure and Mechanical Properties of Welds of Al - Mg - Si Alloys After Different Modes of Impulse Friction Stir Welding

NASA Astrophysics Data System (ADS)

Kondrat'ev, S. Yu.; Morozova, Yu. N.; Golubev, Yu. A.; Hantelmann, C.; Naumov, A. A.; Mikhailov, V. G.

2018-03-01

Welded joints of aluminum alloy 6082-T6 formed by the method of impulse friction stir welding are studied. The effect of the power and frequency of the pulses on the microstructure and mechanical properties of the welded joints is determined. Application of an additional pulse during the welding affects the surface quality and the shape of the weld, the distribution of the oxide layer and of particles of the hardening phase, and the grain size in the zone of dynamic recrystallization.

Gas tungsten arc welding and friction stir welding of ultrafine grained AISI 304L stainless steel: Microstructural and mechanical behavior characterization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sabooni, S., E-mail: s.sabooni@ma.iut.ac.ir; Karimzadeh, F.; Enayati, M.H.

In the present study, an ultrafine grained (UFG) AISI 304L stainless steel with the average grain size of 650 nm was successfully welded by both gas tungsten arc welding (GTAW) and friction stir welding (FSW). GTAW was applied without any filler metal. FSW was also performed at a constant rotational speed of 630 rpm and different welding speeds from 20 to 80 mm/min. Microstructural characterization was carried out by High Resolution Scanning Electron Microscopy (HRSEM) with Electron Backscattered Diffraction (EBSD) and Transmission Electron Microscopy (TEM). Nanoindentation, microhardness measurements and tensile tests were also performed to study the mechanical properties ofmore » the base metal and weldments. The results showed that the solidification mode in the GTAW welded sample is FA (ferrite–austenite) type with the microstructure consisting of an austenite matrix embedded with lath type and skeletal type ferrite. The nugget zone microstructure in the FSW welded samples consisted of equiaxed dynamically recrystallized austenite grains with some amount of elongated delta ferrite. Sigma phase precipitates were formed in the region ahead the rotating tool during the heating cycle of FSW, which were finally fragmented into nanometric particles and distributed in the weld nugget. Also there is a high possibility that the existing delta ferrite in the microstructure rapidly transforms into sigma phase particles during the short thermal cycle of FSW. These suggest that high strain and deformation during FSW can promote sigma phase formation. The final austenite grain size in the nugget zone was found to decrease with increasing Zener–Hollomon parameter, which was obtained quantitatively by measuring the peak temperature, calculating the strain rate during FSW and exact examination of hot deformation activation energy by considering the actual grain size before the occurrence of dynamic recrystallization. Mechanical properties observations showed that the welding efficiency of the FSW welded sample is around 70%, which is more than 20% higher than the GTAW welded sample. - Highlights: • Microstructure and mechanical properties of UFG 304L stainless steel were studied during GTAW and FSW. • Sigma phase formation mechanism was studied during FSW of 304L stainless steel. • THERMOCALC analysis was performed to obtain possible formation temperatures for sigma phase. • Nano-mechanical twins were found in the TMAZ region.« less

Monte Carlo modeling of recrystallization processes in α-uranium

DOE PAGES

Steiner, M. A.; McCabe, R. J.; Garlea, E.; ...

2017-08-01

In this study, starting with electron backscattered diffraction (EBSD) data obtained from a warm clock-rolled α-uranium deformation microstructure, a Potts Monte Carlo model was used to simulate static site-saturated recrystallization while testing a number of different conditions for the assignment of recrystallized nuclei within the microstructure. The simulations support observations that recrystallized nuclei within α-uranium form preferentially on non-twin high-angle grain boundary sites at 450 °C, and demonstrate that the most likely nucleation sites on these boundaries can be identified by the surrounding degree of Kernel Average Misorientation (KAM), which may be considered as a proxy for the local geometricallymore » necessary dislocation (GND) density.« less

The grain size(s) of Black Hills Quartzite deformed in the dislocation creep regime

NASA Astrophysics Data System (ADS)

Heilbronner, Renée; Kilian, Rüdiger

2017-10-01

General shear experiments on Black Hills Quartzite (BHQ) deformed in the dislocation creep regimes 1 to 3 have been previously analyzed using the CIP method (Heilbronner and Tullis, 2002, 2006). They are reexamined using the higher spatial and orientational resolution of EBSD. Criteria for coherent segmentations based on c-axis orientation and on full crystallographic orientations are determined. Texture domains of preferred c-axis orientation (Y and B domains) are extracted and analyzed separately. Subdomains are recognized, and their shape and size are related to the kinematic framework and the original grains in the BHQ. Grain size analysis is carried out for all samples, high- and low-strain samples, and separately for a number of texture domains. When comparing the results to the recrystallized quartz piezometer of Stipp and Tullis (2003), it is found that grain sizes are consistently larger for a given flow stress. It is therefore suggested that the recrystallized grain size also depends on texture, grain-scale deformation intensity, and the kinematic framework (of axial vs. general shear experiments).

Constraints on strain rate and fabric partitioning in ductilely deformed black quartzites (Badajoz-Córdoba Shear Zone, Iberian Massif)

NASA Astrophysics Data System (ADS)

Puelles, Pablo; Ábalos, Benito; Fernández-Armas, Sergio

2013-04-01

The Badajoz-Córdoba Shear Zone is a is 30-40 km wide and 400 km long, NW-SE trending structure located at the boundary between the Ossa-Morena and Central-Iberian Zones of the Iberian Massif. Two elongated domains can be differentiated inside: the Obejo-Valsequillo domain to the NE and the Ductile Shear Belt (DSB) to the SW. The former exhibits Precambrian to Cambrian volcano-sedimentary rocks unconformably overlaying a Neoproterozoic basement formed by the "Serie Negra". The latter, 5-15 km wide, is composed mainly of metamorphic tectonites including the "Serie Negra" and other units located structurally under it. The petrofabric of "Serie Negra" black quartzites from the DSB is analyzed in this study with the Electron Back-Scattered Diffraction technique (EBSD). Black quartzites represent originally siliceous, chemical-biochemical shallow-water marine deposits, currently composed almost exclusively of quartz and graphite. Macroscopically they exhibit an outstanding planolinear tectonic fabric. Petrographically, coarse- and fine-grained dynamically recrystallized quartz bands alternate. The former contain quartz grains with irregular shapes, mica inclusions and "pinning" grain boundaries. Oriented mica grains and graphite particles constrain irregular quartz grain shapes. Quartz ribbons with chessboard microstructures also occur, indicating recrystallization under elevated temperatures coeval with extreme stretching. Fine-grained recrystallized quartz bands are dominated by quartz grains with straight boundaries, triple junctions, a scarcer evidence of bulging, and a higher concentration of dispersed, minute graphite grains. Quartz lattice-preferred orientation (LPO) patterns permit to identify two well-developed maxima for [c] axes: one close to the Y structural direction and the other one around Z, and -axes girdles normal to Y and Z. Although both [c] axis maxima appear in the coarse- and fine-grained bands, subsets can be isolated with grain cluster orientations around Y and Z. Quartz [c]-axis orientations close to Y predominate in coarser-grained bands, whereas [c]-axes scatter around Z in fine-grained zones. A relationship between microstructure and crystal orientation can thus be unraveled. In both fabric types the asymmetry of the LPOs with respect to the external XYZ reference unravel non-coaxial deformation components. Microstructural and LPO evidences indicate that two intracrystalline quartz deformation modes have operated in the "Serie Negra" black quartzites in parallel domains interleaved at the mm- to cm scale. Unless one of them took place under higher-temperature conditions ({m} slip in the high-T amphibolite-facies) and is a relic feature, both modes should have operated simultaneously. Thus, high-temperature boundary migration and the dispersed inclusion pattern of small mica and graphite grains constrained the pinning grain boundary microstructures, the {m} intracrystalline slip, and the larger size of some quartz crystals. Simultaneously, a larger concentration of disseminated graphite led to formation of finer-grained quartz aggregates (due to grain growth) deformed by the (0001) intracrystalline slip systems, that dominate lower-T quartz plasticity (under greenschist- to amphibolite-facies conditions). Arguably, this intracrystalline slip system partitioning was initially constrained by primary variations in inclusion concentration. Likely, these induced a domainal variation in the rate of plastic strain accommodation that led to the current banded microstructural and fabric organization.

Effect of LPSO and SFs on microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy

NASA Astrophysics Data System (ADS)

Xu, Chao; Nakata, Taiki; Qiao, Xiaoguang; Zheng, Mingyi; Wu, Kun; Kamado, Shigeharu

2017-01-01

High performance Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy with high strength and excellent ductility has been successfully developed by hot extrusion. The effect of plate-shaped long period stacking ordered (LPSO) phases and solute-segregated stacking faults (SFs) on the dynamically recrystallization (DRX) behavior was analyzed. The plate-shaped LPSO phases stimulate the DRX by particle stimulated nucleation mechanism, leading to higher DRX ratio and weaker basal texture. While for the alloy with dense fine SFs inside the original grains, discontinuous DRX initially occurs at the original grain boundaries, and the DRX is obviously restricted. Consequently, alloy containing dense SFs exhibits higher strength but lower ductility compared with alloy with plated-shaped LPSO phases.

Effect of LPSO and SFs on microstructure evolution and mechanical properties of Mg-Gd-Y-Zn-Zr alloy

PubMed Central

Xu, Chao; Nakata, Taiki; Qiao, Xiaoguang; Zheng, Mingyi; Wu, Kun; Kamado, Shigeharu

2017-01-01

High performance Mg-8.2Gd-3.8Y-1.0Zn-0.4Zr alloy with high strength and excellent ductility has been successfully developed by hot extrusion. The effect of plate-shaped long period stacking ordered (LPSO) phases and solute-segregated stacking faults (SFs) on the dynamically recrystallization (DRX) behavior was analyzed. The plate-shaped LPSO phases stimulate the DRX by particle stimulated nucleation mechanism, leading to higher DRX ratio and weaker basal texture. While for the alloy with dense fine SFs inside the original grains, discontinuous DRX initially occurs at the original grain boundaries, and the DRX is obviously restricted. Consequently, alloy containing dense SFs exhibits higher strength but lower ductility compared with alloy with plated-shaped LPSO phases. PMID:28134297

Modelling of Microstructure Changes in Hot Deformed Materials Using Cellular Automata

NASA Astrophysics Data System (ADS)

Kuc, Dariusz; Gawąd, Jerzy

2011-01-01

The paper is focused on application of multi-scale 2D method. Model approach consists of Cellular Automata (CA) model of microstructure development and the finite element code to solve thermo-mechanical problem. Dynamic recrystallization phenomenon is taken into account in 2D CA model which takes advantage of explicit representation of microstructure, including individual grains and grain boundaries. Flow stress is the main material parameter in mechanical part of FE and is calculated on the basis of average dislocation density obtained from CA model. The results attained from the model were validated with the experimental data. In the present study, austenitic steel X3CrNi18-10 was investigated. The examination of microstructure for the initial and final microstructures was carried out, using light microscopy and transmission electron microscopy.

Behavior of sheets from Ti-alloys by rolling and heat treatment

NASA Astrophysics Data System (ADS)

Isaenkova, M.; Perlovich, Yu.; Fesenko, V.; Gritskevich, M.; Stolbov, S.; Zaripova, M.

2017-10-01

Sheets from single- and two-phase Ti-alloys (VT1-0, Ti-22Nb-9%Zr and VT-16) were rolled at the room temperature up to various deformation degrees and annealed at temperatures 500-900 °C. The regularities of texture formation in both phases were established. In the technically pure Ti (VT1-0) with the single α-Ti phase the final stable texture component is (0001)±30-40°ND-TD<101 ¯0>. In the two-phase alloy the reorientation of basal axes of α-Ti occurs by the same trajectories as in the single phase alloy. However, in the case of two-phase alloy texture development in α-Ti stops at the intermediate stage, when this texture consists of components with rolling planes (0001)±15-20°ND-RD and (0001)±30-40°ND-TD. The stability of the first components can be provided both by the mutually balanced operation of pyramidal and basal slip systems, activity of which remains at the high deformation degree of two-phase alloy, and by the dynamic α↔β phase transformations, taking place in the distorted structures of α- and β-phases in the course of its cold rolling. At recrystallization of technically pure Ti the basal component disappears in its texture. At the same time, prismatic axes turn by angles 20÷30° depending on the heating rate of the rolled sheet and annealing temperature. At recrystallization of the two-phase Ti-alloy prismatic axes of its α-grains doesn't turn relative to their positions in the rolling texture, as it occurs in the single-phase alloy. This fact indicates to some alternative mode of arising new recrystallized grains in two-phase alloys.

Monolith electroplating process

DOEpatents

Agarrwal, Rajev R.

2001-01-01

An electroplating process for preparing a monolith metal layer over a polycrystalline base metal and the plated monolith product. A monolith layer has a variable thickness of one crystal. The process is typically carried in molten salts electrolytes, such as the halide salts under an inert atmosphere at an elevated temperature, and over deposition time periods and film thickness sufficient to sinter and recrystallize completely the nucleating metal particles into one single crystal or crystals having very large grains. In the process, a close-packed film of submicron particle (20) is formed on a suitable substrate at an elevated temperature. The temperature has the significance of annealing particles as they are formed, and substrates on which the particles can populate are desirable. As the packed bed thickens, the submicron particles develop necks (21) and as they merge into each other shrinkage (22) occurs. Then as micropores also close (23) by surface tension, metal density is reached and the film consists of unstable metal grain (24) that at high enough temperature recrystallize (25) and recrystallized grains grow into an annealed single crystal over the electroplating time span. While cadmium was used in the experimental work, other soft metals may be used.

In situ electron backscatter diffraction investigation of recrystallization in a copper wire.

PubMed

Brisset, François; Helbert, Anne-Laure; Baudin, Thierry

2013-08-01

The microstructural evolution of a cold drawn copper wire (reduction area of 38%) during primary recrystallization and grain growth was observed in situ by electron backscatter diffraction. Two thermal treatments were performed, and successive scans were acquired on samples undergoing heating from ambient temperature to a steady state of 200°C or 215°C. During a third in situ annealing, the temperature was continuously increased up to 600°C. Nuclei were observed to grow at the expense of the deformed microstructure. This growth was enhanced by the high stored energy difference between the nuclei and their neighbors (driving energy in recrystallization) and by the presence of high-angle grain boundaries of high mobility. In the early stages of growth, the nuclei twin and the newly created orientations continue to grow to the detriment of the strained copper. At high temperatures, the disappearance of some twins was evidenced by the migration of the incoherent twin boundaries. Thermal grooving of grain boundaries is observed at these high temperatures and affects the high mobile boundaries but tends to preserve the twin boundaries of lower energy. Thus, grooving may contribute to the twin vanishing.

A novel ultrafine-grained Fe−22Mn−0.6C TWIP steel with superior strength and ductility

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tian, Y.Z., E-mail: yztian@imr.ac.cn

A fully recrystallized ultrafine-grained (UFG) Fe−22wt.%Mn−0.6wt.%C twinning-induced plasticity (TWIP) steel with mean grain size of 576 nm was fabricated by cold rolling and annealing process. Tensile test showed that this UFG steel possessed high yield strength of 785 MPa, and unprecedented uniform elongation of 48%. The Hall-Petch relationship was verified from the coarse-grained (CG) regime to the ultrafine-grained (UFG) regime. The microstructures at specified tensile strains were characterized by electron backscattered diffraction (EBSD) and transmission electron microscopy (TEM). The microstructures and strain hardening behavior of the UFG TWIP steel were compared with the CG counterpart. The strong strain hardening capabilitymore » of the UFG steel is supposed to be responsible for the high strength and good ductility. - Highlights: • A fully recrystallized Fe−22Mn−0.6C TWIP steel with mean grain size of 576 nm was fabricated. • The ultrafine-grained (UFG) steel exhibits strong strain-hardening capability, excellent strength and ductility. • The Hall-Petch relationship is fitted well from the CG regime to the UFG regime.« less

Effects of Al3(Sc,Zr) and Shear Band Formation on the Tensile Properties and Fracture Behavior of Al-Mg-Sc-Zr Alloy

NASA Astrophysics Data System (ADS)

Huang, Hongfeng; Jiang, Feng; Zhou, Jiang; Wei, Lili; Qu, Jiping; Liu, Lele

2015-11-01

The mechanical properties and microstructures of Al-6Mg-0.25Sc-0.1Zr alloy (wt.%) during annealing were investigated by means of uniaxial tensile testing, optical microscope, scanning electron microscope, transmission electron microscope, and high-resolution transmission electron microscope. The results show that a large number of micro and grain-scale shear bands form in this alloy after cold rolling. As the tensile-loading force rises, strain softening would generate in shear bands, resulting in the occurrence of shear banding fracture in cold-rolled Al-Mg-Sc-Zr alloys. Recrystallization takes place preferentially in shear bands during annealing. Due to the formation of coarse-grain bands constructed by new subgrains, recrystallization softening tends to occur in these regions. During low-temperature annealing, recrystallization is inhibited by nano-scale Al3(Sc,Zr) precipitates which exert significant coherency strengthening and modulus hardening. However, the strengthening effect of Al3(Sc,Zr) decreases with the increasing of particle diameter at elevated annealing temperature. The mechanical properties of the recrystallized Al-Mg-Sc-Zr alloy decrease to a minimum level, and the fracture plane exhibits pure ductile fracture characteristics.

Modeling of thermomechanical and metallurgical phenomena in steel strip during hot direct rolling and runout table cooling of thin-cast slabs

NASA Astrophysics Data System (ADS)

Muojekwu, Cornelius Anaedu

The present research was directed at adequate prediction of the temperature, deformation behavior (roll force, flow stress, strain and strain rate) and microstructural evolution (recovery, recrystallization, grain growth, austenite and ferrite grain sizes) during rolling in the Compact Strip Production (CSP) process, as well as the final mechanical properties of the hot rolled strips. This was accomplished with the aid of integrated process modeling, involving mathematical simulation, laboratory experiments and industrial campaigns. The study covered two conventional plain carbon steel grades, the A36 (AISI 1018, 0.17C-0.74Mn) and DQSK (AISI 1005, 0.038C-0.3Mn), and a range of plain carbon steel grades (0.06-0.09 C, 0.16-0.9 Mn) produced at HYLSA's CSP mill at Monterrey, Mexico. In the laboratory, compression tests (both single and double-hits) were carried out on the Gleeble 1500 thermomechanical simulator in order to elucidate the effect of coarse austenite grain size on the flow stress and recrystallization behavior of the plain carbon steels. It was found that coarse grain size not only decreased the flow stress at a given strain but also substantially reduced the tendency toward dynamic recrystallization. An increase in grain size from 244 to 1110 mum which is typical of the first stands of a conventional finishing mill and CSP hot-strip mill respectively, resulted in up to a 30 MPa decrease in the flow stress of both A36 and DQSK steel grades at similar operating conditions of temperature, strain and strain rate. In order to validate the model and laboratory results with mill measurements from an operating CSP plant, an industrial trial was carried out at HYLSA's CSP mill in Monterrey, Mexico. During the industrial campaign, intermediate temperature measurements were made, CSP slab and coil samples were acquired, and all measured and recorded mill data and practices were obtained. Comprehensive mathematical modeling of the rolling process was carried out employing finite difference and finite element analysis. The CSP mill measurements were utilized to validate model predictions of temperature, roll force, grain size and mechanical properties. Good agreement was obtained between prediction and measurement in most of the cases. An estimate of the heat extraction from the various mill sub-units was conducted from the validated calculations. It was found that heat loss by radiation accounted for 48-51 percent of the total heat loss, the work rolls accounted for 41-44 percent, the descaling unit accounted for 4-6 percent and the interstand sprays accounted for the remaining 3-4 percent. It was found that the uniform strain model consistently predicts lower temperatures than the target exit temperature for thin gauges due to a low estimate of deformation heat. Model results captured the details of heat transfer, deformation, recrystallization and austenite decomposition in the CSP mill. The effect of various mill parameters were elucidated, and the similarities and differences between conventional cold-charge rolling and CSP rolling were highlighted. (Abstract shortened by UMI.)

Static Recrystallization Behavior of Z12CN13 Martensite Stainless Steel

NASA Astrophysics Data System (ADS)

Luo, Min; Zhou, Bing; Li, Rong-bin; Xu, Chun; Guo, Yan-hui

2017-09-01

In order to increase the hot workability and provide proper hot forming parameters of forging Z12CN13 martensite stainless steel for the simulation and production, the static recrystallization behavior has been studied by double-pass hot compression tests. The effects of deformation temperature, strain rate and inter-pass time on the static recrystallization fraction by the 2% offset method are extensively studied. The results indicate that increasing the inter-pass time and the deformation temperature as well as strain rate appropriately can increase the fraction of static recrystallization. At the temperature of 1050-1150 °C, inter-pass time of 30-100 s and strain rate of 0.1-5 s-1, the static recrystallization behavior is obvious. In addition, the kinetics of static recrystallization behavior of Z12CN13 steel has been established and the activation energy of static recrystallization is 173.030 kJ/mol. The substructure and precipitates have been studied by TEM. The results reveal that the nucleation mode is bulging at grain boundary. Undissolved precipitates such as MoNi3 and Fe3C have a retarding effect on the recrystallization kinetics. The effect is weaker than the accelerating effect of deformation temperature.

A Naturally-Calibrated Flow Law for Quartz

NASA Astrophysics Data System (ADS)

Lusk, A. D.; Platt, J. P.

2017-12-01

Flow laws for power-law behavior of quartz deforming by crystal-plastic processes with grain size sensitive creep included take the general form: ė = A σn f(H2O) exp(-Q/RT) dmWhere A - prefactor; σ - differential stress; n - stress exponent; f(H2O) - water fugacity; Q - activation energy; R - gas constant; T - temperature (K); d - grain size sensitivity raised to power m. Assuming the dynamically recrystallized grain size for quartz follows the peizometric relationship, substitute dm = (K σ-p)m, where K - piezometric constant; σ - differential stress; p - piezometric exponent. Rearranging the above flow law: ė = A K σ(n-pm) f(H2O) exp(-Q/RT)We use deformation temperatures, paleo-stresses, and strain rates calculated from rocks deformed in the Caledonian Orogeny, NW Scotland, along with existing experimental data, to compare naturally-calibrated values of stress exponent (n-pm) and activation energy (Q) to those determined experimentally. Microstructures preserved in the naturally-strained rocks closely resemble those produced by experimental work, indicating that quartz was deformed by the same mechanism(s). These observations validate the use of predetermined values for A as well as the addition of experimental data to calculate Q. Values for f(H2O) are based on calculated pressure and temperature conditions. Using the abovementioned constraints, we compare results, discuss challenges, and explore implications of naturally- vs. experimentally-derived flow laws for dislocation creep in quartz. Rocks used for this study include quartzite and quartz-rich psammite of the Cambrian-Ordovician shelf sequence and tectonically overlying Moine Supergroup. In both cases, quartz is likely the primary phase that controlled rheological behavior. We use the empirically derived piezometer for the dynamically recrystallized grain size of quartz to calculate the magnitude of differential stress, along with the Ti-in-quartz thermobarometer and the c-axis opening angle thermometer to determine temperatures of deformation. Tensor strain rates are calculated from plate convergence rate, based on total displacement and duration of thrusting within the Moine thrust zone, and shear zone thickness calculated from four detailed structural and microstructural transects taken parallel to the direction of displacement.

Deformation and annealing response of TD-nickel chromium sheet

NASA Technical Reports Server (NTRS)

Kane, R. D.; Ebert, L. J.

1973-01-01

The deformation and annealing response of TD-nickel chromium (TD-NiCr) 0.1 inch thick sheet was examined using various cold-rolling and annealing treatments. Upon annealing (above 816 C (1500 F), the as-received material was converted from an initially ultra-fine grain size (average grain dimension 0.51 micron) to a large grain structure. Increases in grain size by a factor of 100 to 200 were observed for this transformation. However, in those material states where the large grain transformation was absent, a fine grain recrystallized structure formed upon annealing (above 732 C (1350 F)). The deformation and annealing response of TD-NiCr sheet was evaluated with respect to the processing related variables as mode and severity of deformation and annealing temperature. Results indicate that the large grain transformation, classical primary recrystallization occurs. Using selected materials produced during the deformation and annealing study, the elevated temperature tensile properties of TD-NiCr sheet were examined in the temperature range 593 C (1100 F) to 1093 C (2000 F). It was observed that the elevated temperature tensile properties of TD-NiCr sheet could be optimized by the stabilization of a large grain size in this material using the cold working and/or annealing treatments developed during the present investigation.

Pressure Dependence of Magnesite Flow Strength

NASA Astrophysics Data System (ADS)

Millard, J. W.; Holyoke, C. W., III; McDaniel, C.; Raterron, P.; Kronenberg, A. K.; Tokle, L.

2017-12-01

Recent experiments by Holyoke et al. (2014) indicate that magnesite is weak compared with olivine, leading to strain localization into magnesite-bearing horizons of downgoing subducting slabs, potentially leading to intermediate (200-400 km) deep focus earthquakes DFEs. Flow strengths (σ) of magnesite were determined as functions of strain rate and temperature (T), but not of pressure (P). In order to determine the pressure dependence of magnesite deforming by dislocation creep and low temperature plasticity (LTP), we performed triaxial deformation experiments on natural, coarse-grained (80 μm) magnesite aggregates at T = 900oC, strain rate of 2*10-5/s and P from 3.2 to 7.9 GPa in the D-DIA at Beamline 6-BMB at the Advanced Photon Source at Argonne National Lab. Strengths of magnesite aggregates increase as a function of pressure, from σ=0.85 GPa (at P = 3.2 GPa) to 1.69 GPa (at P = 7.9 GPa). Microstructures developed at P ≤ 6.2 GPa include grain flattening and sweeping undulatory extinction, and dynamic recrystallization at grain boundaries (by bulge nucleation), consistent with dislocation creep. Microstructures generated at P ≥ 6.7 GPa include some twins and kink bands, grain flattening and patchy undulatory extinction, and bulging recrystallization at grain boundaries. These microstructures indicate contributions to strain of both LTP and dislocation creep mechanisms. The pressure dependence can be described by a thermally activated enthalpy, where s increases with P by way of an activation volume V*. Based on both D-DIA and Griggs apparatus results (of Holyoke et al., 2014), V* = 8.5 (± 0.5) × 10-6 m3 mol-1. This value is comparable to V* determined for creep of olivine (9.5 (± 7) × 10-6 m3 mol-1 Durham et al., 2009), indicating that the strength difference between magnesite and olivine will continue to be significant at high pressures, and lead to strain localization at all subduction zone depths.

Recrystallization kinetics of warm-rolled tungsten in the temperature range 1150-1350 °C

NASA Astrophysics Data System (ADS)

Alfonso, A.; Juul Jensen, D.; Luo, G.-N.; Pantleon, W.

2014-12-01

Pure tungsten is a potential candidate material for the plasma-facing first wall and the divertor of fusion reactors. Both parts have to withstand high temperatures during service. This will alter the microstructure of the material by recovery, recrystallization and grain growth and will cause degradation in material properties as a loss in mechanical strength and embrittlement. The thermal stability of a pure tungsten plate warm-rolled to 67% thickness reduction was investigated by long-term isothermal annealing in the temperature range between 1150 °C and 1350 °C up to 2200 h. Changes in the mechanical properties during annealing are quantified by Vickers hardness measurements. They are described concisely by classical kinetic models for recovery and recrystallization. The observed time spans for recrystallization and the obtained value for the activation energy of the recrystallization process indicate a sufficient thermal stability of the tungsten plate during operation below 1075 °C.

Boundary migration in a 3D deformed microstructure inside an opaque sample

DOE PAGES

Zhang, Y. B.; Budai, J. D.; Tischler, J. Z.; ...

2017-06-30

How boundaries surrounding recrystallization grains migrate through the 3D network of dislocation boundaries in deformed crystalline materials is unknown and critical for the resulting recrystallized crystalline materials. Furthermore, by using X-ray Laue diffraction microscopy, we show for the first time the migration pattern of a typical recrystallization boundary through a well-characterized deformation matrix. The data provide a unique possibility to investigate effects of both boundary misorientation and plane normal on the migration, information which cannot be accessed with any other techniques. Our results show that neither of these two parameters can explain the observed migration behavior. Instead we suggest thatmore » the subdivision of the deformed microstructure ahead of the boundary plays the dominant role. Our experimental observations challenge the assumptions of existing recrystallization theories, and set the stage for determination of mobilities of recrystallization boundaries.« less

Constraining the Texture and Composition of Pore-Filling Cements at Gale Crater, Mars

NASA Technical Reports Server (NTRS)

Siebach, K. L.; Grotzinger, J. P.; McLennan, S. M.; Hurowitz, J. A.; Ming, D. W.; Vaniman, D. T.; Rampe, E. B.; Blaney, D. L.; Kah, L. C.

2015-01-01

The Mars Science Laboratory (MSL) rover Curiosity has encountered a wide variety of sedimentary rocks deposited in fluvio-lacuestrine sequences at the base of Gale Crater. The presence of sedimentary rocks requires that initial sediments underwent diagenesis and were lithified. Lithification involves sediment compaction, cementation, and re-crystallization (or authigenic) processes. Analysis of the texture and composition of the cement can reveal the environmental conditions when the cements were deposited, enabling better understanding of early environments present within Gale Crater. The first step in lithification is sediment compaction. The Gale crater sediments do not show evidence for extensive compaction prior to cementation; the Sheepbed mudstone in Yellowknife Bay (YKB) has preserved void spaces ("hollow nodules"), indicating that sediments were cemented around the hollow prior to compaction, and conglomerates show imbrication, indicating minimal grain reorganization prior to lithification. Furthermore, assuming the maximum burial depth of these sediments is equivalent to the depth of Gale Crater, the sediments were never under more than 1 kb of pressure, and assuming a 15 C/km thermal gradient in the late Noachian, the maximum temperature of diagenesis would have been approximately 75 C. This is comparable to shallow burial diagenetic conditions on Earth. The cementation and recrystallization components of lithification are closely intertwined. Cementation describes the precipitation of minerals between grains from pore fluids, and recrystallization (or authigenesis) is when the original sedimentary mineral grains are altered into secondary minerals. The presence of authigenic smectites and magnetite in the YKB formation suggests that some recrystallization has taken place. The relatively high percentage of XRD-amorphous material (25-40%) detected by CheMin suggests that this recrystallization may be limited in scope, and therefore may not contribute significantly to the cementing material. However, relatively persistent amorphous components could exist in the Martian environment (e.g. amorphous MgSO4), so recrystallization, including loss of crystallinity, cannot yet be excluded as a method of cementation. In order to describe the rock cementation, both the rock textures and their composition must be considered. Here, we attempt to summarize the current understanding of the textural and compositional aspects of the cement across the rocks analyzed by Curiosity to this point.

Rapid Grain Size Reduction in the Upper Mantle at a Plate Boundary

NASA Astrophysics Data System (ADS)

Kidder, S. B.; Scott, J.; Prior, D. J.; Lubicich, E. J.

2017-12-01

A few spinel peridotite xenoliths found near the Alpine Fault, New Zealand, exhibit a mylonitic texture and, locally, an extremely fine 30 micron grain size. The harzburgite xenoliths were emplaced in a 200 km-long elongate dike zone interpreted as a gigantic tension fracture or Reidel shear associated with Alpine Fault initiation 25 Ma. The presence of thin ( 1 mm) ultramylonite zones with px-ol phase mixing and fine grain sizes, minimal crustal-scale strain associated with the dike swarm, and the absence of mylonites at four of the five xenolith localities associated with the dike swarm indicate that upper mantle deformation was highly localized. Strings of small, recrystallized grains (planes in 3D) are found in the interiors of olivine porphyroclasts. In some cases, bands 1-2 grains thick are traced from the edges of olivine grains and terminate in their interiors. Thicker zones of recrystallized grains are also observed crossing olivine porphyroclasts without apparent offset of the unrecrystallized remnants of the porphyroclasts. We suggest a brittle-plastic origin for these features since the traditional recrystallization mechanisms associated with dislocation creep require much more strain than occurred within these porphyroclasts. Analogous microstructures in quartz and feldspar in mid-crust deformation zones are attributed to brittle-plastic processes. We hypothesize that such fine-grained zones were the precursors of the observed, higher-strain ultramylonite zones. Given the size of the new grains preserved in the porphyroclasts ( 100 micron) and a moho temperature > 650°C, grain growth calculations indicate that the observed brittle-plastic deformation occurred <10,000 yrs. prior to eruption. It is likely then that either brittle-plastic deformation was coeval with the ductile shearing occurring in the ultramylonite bands, or possibly, if deformation can be separated into brittle-plastic (early) and ductile (later) phases, that the entire localization process was very rapid (<10,000 yrs). In either case we interpret that semi-brittle deformation was a key process responsible for rapid localization in this initiating plate-scale mantle shear zone.

Improving hydro-formability of stainless steel tubes by tube channel pressing

NASA Astrophysics Data System (ADS)

Kitano, Y.; Yuasa, M.; Miyamoto, H.; Farshidi, M. H.; Bagherpour, E.

2017-05-01

Tube channel pressing (TCP), which is one of the severe plastic deformation (SPD) technologies to refine grain size into submicron size for tubular materials, have been applied to ferritic stainless steel tubes for one pass, in order to alleviate ridging and enhance the hydro-formability. It was found that grain-scale shear bands were introduced by one-pass TCP, and texture and microstructure was successfully modified by promoting recrystallization of deformation microstructure, which is otherwise hard-to-recrystallize, in the post-TCP annealing. Elongation to failure, strain-hardening exponent (n-value) and Lankford values of both longitudinal and circumferential directions increased in comparison to with the tube fabricated by conventional process.

Dynamic Recrystallization Behavior of Zr-1Sn-0.3Nb Alloy During Hot Rolling Process

NASA Astrophysics Data System (ADS)

Zhao, Siyu; Liu, Huiqun; Lin, Gaoyong; Jiang, Yilan; Xun, Jian

2017-11-01

Zirconium alloys are advanced materials with properties that are greatly affected by their crystalline structure. To investigate this, sheets of Zr-1Sn-0.3Nb alloy were hot rolled with different reductions (10%, 30%, 50%, and 60%) at 1023 K and 1073 K to investigate the alloy's dynamic recrystallization behavior. Recrystallization kinetics was observed via electron backscattering diffraction and transmission electron microscopy, and the results were compared with estimates based on the Johnson-Mehl-Avrami-Kolmogorov (JMAK) equation. The values of the JMAK exponent n and k increased with the rolling temperature. The estimates and microstructural observations of dynamic recrystallization (DRX) kinetics were in good agreement.

Properties of Rolled AZ31 Magnesium Alloy Sheet Fabricated by Continuous Variable Cross-Section Direct Extrusion

NASA Astrophysics Data System (ADS)

Liu, Yang; Li, Feng; Li, Xue Wen; Shi, Wen Yong

2018-03-01

Rolling is currently a widely used method for manufacturing and processing high-performance magnesium alloy sheets and has received widespread attention in recent years. Here, we combined continuous variable cross-section direct extrusion (CVCDE) and rolling processes. The microstructure and mechanical properties of the resulting sheets rolled at different temperatures from CVCDE extrudate were investigated by optical microscopy, scanning electron microscope, transmission electron microscopy and electron backscatter diffraction. The results showed that a fine-grained microstructure was present with an average grain size of 3.62 μm in sheets rolled from CVCDE extrudate at 623 K. Dynamic recrystallization and a large strain were induced by the multi-pass rolling, which resulted in grain refinement. In the 573-673 K range, the yield strength, tensile strength and elongation initially increased and then declined as the CVCDE temperature increased. The above results provide an important scientific basis of processing, manufacturing and the active control on microstructure and property for high-performance magnesium alloy sheet.

Heat-Affected Zone Liquation Cracking Resistance of Friction Stir Processed Aluminum-Copper Alloy AA 2219

NASA Astrophysics Data System (ADS)

Karthik, G. M.; Janaki Ram, G. D.; Kottada, Ravi Sankar

2017-04-01

In the current work, the effect of friction stir processing on heat-affected zone (HAZ) liquation cracking resistance of aluminum-copper alloy AA 2219 was evaluated. In Gleeble hot-ductility tests and longitudinal Varestraint tests, the FSPed material, despite its very fine dynamically recrystallized equiaxed grain structure, showed considerably higher susceptibility to HAZ liquation cracking when compared to the base material. Detailed microstructural studies showed that the increased cracking susceptibility of the FSPed material is due to (i) increase in the amount of liquating θ phase (equilibrium Al2Cu) and (ii) increase in the population of grain boundary θ particles. An important learning from the current work is that, in certain materials like alloy 2219, the use of FSP as a pretreatment to fusion welding can be counterproductive.

Influence of processing parameters and alloying additions on the mechanically determined no-recrystallization temperature in niobium microalloyed steels

NASA Astrophysics Data System (ADS)

Homsher-Ritosa, Caryn Nicole

Microalloying elements are added to plate steels to improve the mechanical properties through grain refinement and precipitation strengthening. In industrial practice, such refinement is obtained by controlling the rolling near critical temperatures in austenite. Generally, a large amount of hot deformation is desired below the no-recrystallization temperature (TNR) to increase the grain boundary area to promote fine ferrite grains upon transformation during cooling. Ideally, a high TNR is desired for increased deformation below TNR at minimal rolling loads and minimal loss of productivity. To increase TNR, microalloying elements such as Nb, V, and Ti are used. The primary purpose of the current study was to determine the effect of multiple microalloying elements on the mechanically determined via torsion testing no-recrystallization temperature (TNR_Tor) in Nb-bearing plate steel. This project focused on the influence of alloying elements and deformation parameters on TNR_Tor. The main objective was to experimentally determine the TNR_Tor for various laboratory-grade steels with systematically varying amounts of Nb, V, and Ti, with C and N held constant. The synergistic effects of these microalloying elements were evaluated. Another objective was to determine the TNR_Tor with systematically varied deformation parameters for the same set of steels. Comparisons of the measured TNR through two different mechanical tests were conducted. Finally, a microstructural evaluation around the mechanically determined TNR_Tor via multistep hot torsion testing was made. To accomplish these objectives six Nb-bearing steels were laboratory produced with 0.065 wt pct C, 0.044 wt pct N, and varying amounts of Nb, V, and Ti. Multistep hot torsion tests were conducted using the GleebleRTM 3500 thermomechanical simulator between the temperatures of 1200 and 750 °C. The mean flow stress was calculated for each deformation step and plotted against the inverse absolute temperature. The TNR_Tor was determined by finding the intersection point of two linear regressions fit to the data. The TNR_Tor values were compared with measured TNR values from double-hit compression tests and with predicted values using empirical equations from the literature. Light optical micrographs and electron backscatter diffraction scans were examined for samples quenched from just above and just below the experimentally determined values of TNR_Tor for the high Nb, low Ti, and commercially produced 10V45 alloys to help verify the prior austenite grain morphology. For all processing conditions, the low Nb alloy was the least effective in increasing TNR_Tor and the high additions of Ti were the most effective at increasing TNR_Tor. The additions of V were not significantly effective in altering TNR_Tor and it is believed the Nb overpowered any influence the V additions may have had on TNR_Tor. An increase in strain or an increase strain rate decreased TNR_Tor. The T NR values measured from multistep hot torsion testing were lower than the TNR values measured from double-hit compression tests. The use of the mean flow stress versus inverse temperature curve to determine TNR_Tor does not correlate to the microstructural meaning of T NR (i.e. no recrystallization). The transition from completely recrystallized grains to less than complete recrystallization is not properly modeled by the intersection of two linear regions and is more gradual than the mechanical test implies. From the microstructural analysis of a10V45 steel, there is evidence of recrystallization at temperatures 200 °C below the measured TNR_Tor. The slope change on the mean flow stress versus inverse temperature curves is believed to be, in part, accumulated strain as well as refinement of continuously recrystallized grains causing a Hall-Petch type strength increase.

Development of re-crystallized W-1.1%TiC with enhanced room-temperature ductility and radiation performance

NASA Astrophysics Data System (ADS)

Kurishita, H.; Matsuo, S.; Arakawa, H.; Sakamoto, T.; Kobayashi, S.; Nakai, K.; Takida, T.; Kato, M.; Kawai, M.; Yoshida, N.

2010-03-01

Ultra-fine grained (UFG) W-TiC compacts fabricated by powder metallurgical methods utilizing mechanical alloying (MA) are very promising for use in irradiation environments. However, the assurance of room-temperature ductility and enhancement in surface resistances to low-energy hydrogen irradiation are unsettled issues. As an approach to solution to these, microstructural modification by hot plastic working has been applied to UFG W-TiC processed by MA in a purified Ar or H 2 atmosphere and hot isostatic pressing (HIP). Hot plastically worked compacts have been subjected to 3-point bend tests at room temperature and TEM microstructural examinations. It is found that the microstructural modification allows us to convert UFG W-1.1%TiC to compacts exhibiting a very high fracture strength and appreciable ductility at room temperature. The compacts of W-1.1%TiC/Ar (MA atmosphere: Ar) and W-1.1%TiC/H 2 (MA atmosphere: H 2) exhibit re-crystallized structures with approximately 0.5 and 1.5 μm in grain size, respectively. It is shown that the enhancement of fracture resistance by microstructural modifications is attributed to significant strengthening of weak grain boundaries in the re-crystallized state. As a result the modified compacts exhibit superior surface resistance to low-energy deuteron irradiation.

Transport properties of olivine grain boundaries from electrical conductivity experiments

NASA Astrophysics Data System (ADS)

Pommier, Anne; Kohlstedt, David L.; Hansen, Lars N.; Mackwell, Stephen; Tasaka, Miki; Heidelbach, Florian; Leinenweber, Kurt

2018-05-01

Grain boundary processes contribute significantly to electronic and ionic transports in materials within Earth's interior. We report a novel experimental study of grain boundary conductivity in highly strained olivine aggregates that demonstrates the importance of misorientation angle between adjacent grains on aggregate transport properties. We performed electrical conductivity measurements of melt-free polycrystalline olivine (Fo90) samples that had been previously deformed at 1200 °C and 0.3 GPa to shear strains up to γ = 7.3. The electrical conductivity and anisotropy were measured at 2.8 GPa over the temperature range 700-1400 °C. We observed that (1) the electrical conductivity of samples with a small grain size (3-6 µm) and strong crystallographic preferred orientation produced by dynamic recrystallization during large-strain shear deformation is a factor of 10 or more larger than that measured on coarse-grained samples, (2) the sample deformed to the highest strain is the most conductive even though it does not have the smallest grain size, and (3) conductivity is up to a factor of 4 larger in the direction of shear than normal to the shear plane. Based on these results combined with electrical conductivity data for coarse-grained, polycrystalline olivine and for single crystals, we propose that the electrical conductivity of our fine-grained samples is dominated by grain boundary paths. In addition, the electrical anisotropy results from preferential alignment of higher-conductivity grain boundaries associated with the development of a strong crystallographic preferred orientation of the grains.

Influence of grain boundary characteristics on thermal stability in nanotwinned copper

DOE PAGES

Niu, Rongmei; Han, Ke; Su, Yi-feng; ...

2016-08-12

High density grain boundaries provide high strength, but may introduce undesirable features, such as high Fermi levels and instability. We investigated the kinetics of recovery and recrystallization of Cu that was manufactured to include both nanotwins (NT) and high-angle columnar boundaries. We used the isothermal Johnson-Mehl-Avrami-Kolmogorov (JMAK) model to estimate activation energy values for recovery and recrystallization and compared those to values derived using the non-isothermal Kissinger equation. The JMAK model hinges on an exponent that expresses the growth mechanism of a material. The exponent for this Cu was close to 0.5, indicating low-dimensional microstructure evolution, which is associated withmore » anisotropic twin coarsening, heterogeneous recrystallization, and high stability. Since this Cu was of high purity, there was a negligible impurity-drag-effect on boundaries. The twin coarsening and heterogeneous recrystallization resulted from migration of high-angle columnar boundaries with their triple junctions in one direction, assisted by the presence of high concentration vacancies at boundaries. Analyses performed by electron energy loss spectroscopy of atomic columns at twin boundaries (TBs) and in the interior showed similar plasma peak shapes and L3 edge positions. As a result, this implies that values for conductivity and Fermi level are equal for atoms at TBs and in the interior.« less

Analytical modeling of the thermomechanical behavior of ASTM F-1586 high nitrogen austenitic stainless steel used as a biomaterial under multipass deformation.

PubMed

Bernardes, Fabiano R; Rodrigues, Samuel F; Silva, Eden S; Reis, Gedeon S; Silva, Mariana B R; Junior, Alberto M J; Balancin, Oscar

2015-06-01

Precipitation-recrystallization interactions in ASTM F-1586 austenitic stainless steel were studied by means of hot torsion tests with multipass deformation under continuous cooling, simulating an industrial laminating process. Samples were deformed at 0.2 and 0.3 at a strain rate of 1.0s(-1), in a temperature range of 900 to 1200°C and interpass times varying from 5 to 80s. The tests indicate that the stress level depends on deformation temperature and the slope of the equivalent mean stress (EMS) vs. 1/T presents two distinct behaviors, with a transition at around 1100°C, the non-recrystallization temperature (Tnr). Below the Tnr, strain-induced precipitation of Z-phase (NbCrN) occurs in short interpass times (tpass<30s), inhibiting recrystallization and promoting stepwise stress build-up with strong recovery, which is responsible for increasing the Tnr. At interpass times longer than 30s, the coalescence and dissolution of precipitates promote a decrease in the Tnr and favor the formation of recrystallized grains. Based on this evidence, the physical simulation of controlled processing allows for a domain refined grain with better mechanical properties. Copyright © 2015 Elsevier B.V. All rights reserved.

Recrystallization behavior and thermal shock resistance of the W-1.0 wt% TaC alloy

NASA Astrophysics Data System (ADS)

Xie, Z. M.; Miao, S.; Zhang, T.; Liu, R.; Wang, X. P.; Fang, Q. F.; Hao, T.; Zhuang, Z.; Liu, C. S.; Lian, Y. Y.; Liu, X.; Cai, L. H.

2018-04-01

The high-temperature stability and good mechanical strength of tungsten (W) alloys are highly desirable for a wide range of fusion applications, which can be achieved by dispersion strengthening. In this paper, TaC dispersion effects on the thermal stabilities, tensile properties and thermal shock resistances have been investigated. A hot-rolled W-1.0 wt% TaC plate has been fabricated which contains the high tensile strength and elongation. Nanosized particles in the W matrix improve the recrystallization temperature to about 1400 °C and the ultimate tensile strength to 571 MPa at 500 °C through hindering grain boundary migration, pinning dislocations and refining grains. The effects of edge-localized mode like transient heat events on the rolled and recrystallized W-1.0 wt% TaC alloys were investigated systematically. The cracking threshold (100 shots) at room temperature is in the range of 0.33-0.44 GW/m2 for the rolled W-1.0 wt% TaC. Recrystallization degrades mechanical strength and makes the material more prone to thermal shock damages. Coarse Ta2O5 and Ta-Cx-Oy particles are easy to fracture and introduce a preferential crack initiation in W matrix during cyclic heat loads.

Influence of grain boundary characteristics on thermal stability in nanotwinned copper

PubMed Central

Niu, Rongmei; Han, Ke; Su, Yi-feng; Besara, Tiglet; Siegrist, Theo M.; Zuo, Xiaowei

2016-01-01

High density grain boundaries provide high strength, but may introduce undesirable features, such as high Fermi levels and instability. We investigated the kinetics of recovery and recrystallization of Cu that was manufactured to include both nanotwins (NT) and high-angle columnar boundaries. We used the isothermal Johnson-Mehl-Avrami-Kolmogorov (JMAK) model to estimate activation energy values for recovery and recrystallization and compared those to values derived using the non-isothermal Kissinger equation. The JMAK model hinges on an exponent that expresses the growth mechanism of a material. The exponent for this Cu was close to 0.5, indicating low-dimensional microstructure evolution, which is associated with anisotropic twin coarsening, heterogeneous recrystallization, and high stability. Since this Cu was of high purity, there was a negligible impurity-drag-effect on boundaries. The twin coarsening and heterogeneous recrystallization resulted from migration of high-angle columnar boundaries with their triple junctions in one direction, assisted by the presence of high concentration vacancies at boundaries. Analyses performed by electron energy loss spectroscopy of atomic columns at twin boundaries (TBs) and in the interior showed similar plasma peak shapes and L3 edge positions. This implies that values for conductivity and Fermi level are equal for atoms at TBs and in the interior. PMID:27514474

Physical Simulation of a Duplex Stainless Steel Friction Stir Welding by the Numerical and Experimental Analysis of Hot Torsion Tests

NASA Astrophysics Data System (ADS)

da Fonseca, Eduardo Bertoni; Santos, Tiago Felipe Abreu; Button, Sergio Tonini; Ramirez, Antonio Jose

2016-09-01

Physical simulation of friction stir welding (FSW) by means of hot torsion tests was performed on UNS S32205 duplex stainless steel. A thermomechanical simulator Gleeble 3800® with a custom-built liquid nitrogen cooling system was employed to reproduce the thermal cycle measured during FSW and carry out the torsion tests. Microstructures were compared by means of light optical microscopy and electron backscatter diffraction. True strain and strain rate were calculated by numerical simulation of the torsion tests. Thermomechanically affected zone (TMAZ) was reproduced at peak temperature of 1303 K (1030 °C), rotational speeds of 52.4 rad s-1 (500 rpm) and 74.5 rad s-1 (750 rpm), and 0.5 to 0.75 revolutions, which represent strain rate between 10 and 16 s-1 and true strain between 0.5 and 0.8. Strong grain refinement, similar to the one observed in the stir zone (SZ), was attained at peak temperature of 1403 K (1130 °C), rotational speed of 74.5 rad s-1 (750 rpm), and 1.2 revolution, which represent strain rate of 19 s-1 and true strain of 1.3. Continuous dynamic recrystallization in ferrite and dynamic recrystallization in austenite were observed in the TMAZ simulation. At higher temperature, dynamic recovery of austenite was also observed.

Characterization of microstructure and texture across dissimilar super duplex/austenitic stainless steel weldment joint by austenitic filler metal

DOE Office of Scientific and Technical Information (OSTI.GOV)

Eghlimi, Abbas, E-mail: a.eghlimi@ma.iut.ac.ir; Shamanian, Morteza; Eskandarian, Masoomeh

The evolution of microstructure and texture across an as-welded dissimilar UNS S32750 super duplex/UNS S30403 austenitic stainless steel joint welded by UNS S30986 (AWS A5.9 ER309LMo) austenitic stainless steel filler metal using gas tungsten arc welding process was evaluated by optical micrography and EBSD techniques. Due to their fabrication through rolling process, both parent metals had texture components resulted from deformation and recrystallization. The weld metal showed the highest amount of residual strain and had large austenite grain colonies of similar orientations with little amounts of skeletal ferrite, both oriented preferentially in the < 001 > direction with cub-on-cube orientationmore » relationship. While the super duplex stainless steel's heat affected zone contained higher ferrite than its parent metal, an excessive grain growth was observed at the austenitic stainless steel's counterpart. At both heat affected zones, austenite underwent some recrystallization and formed twin boundaries which led to an increase in the fraction of high angle boundaries as compared with the respective base metals. These regions showed the least amount of residual strain and highest amount of recrystallized austenite grains. Due to the static recrystallization, the fraction of low degree of fit (Σ) coincident site lattice boundaries, especially Σ3 boundaries, was increased in the austenitic stainless steel heat affected zone, while the formation of subgrains in the ferrite phase increased the content of < 5° low angle boundaries at that of the super duplex stainless steel. - Graphical abstract: Display Omitted - Highlights: • Extensive grain growth in the HAZ of austenitic stainless steel was observed. • Intensification of < 100 > orientated grains was observed adjacent to both fusion lines. • Annealing twins with Σ3 CSL boundaries were formed in the austenite of both HAZ. • Cub-on-cube OR was observed between austenite and ferrite in the weld metal. • Weld metal had the lowest texture intensity and ratio of low angle and CSL boundaries.« less

Triangular Graphene Grain Growth on Cube-Textured Cu Substrates

DTIC Science & Technology

2011-01-01

rate of CuOx decreases with decreasing H 2 partial pressure. [ 32 ] According to the Cu-O phase diagram, [ 33 ] the eutectic temperature of Cu-CuO and...accelerating voltage of 2 KeV. The electron backscatter diffraction patterns (EBSP) were used to examine recrystallization and grain orientation of

Implications of Grain Size Evolution for the Effective Stress Exponent in Ice

NASA Astrophysics Data System (ADS)

Behn, M. D.; Goldsby, D. L.; Hirth, G.

2016-12-01

Viscous flow in ice has typically been described by the Glen law—a non-Newtonian, power-law relationship between stress and strain-rate with a stress exponent n 3. The Glen law is attributed to grain-size-insensitive dislocation creep; however, laboratory and field studies demonstrate that deformation in ice is strongly dependent on grain size. This has led to the hypothesis that at sufficiently low stresses, ice flow is controlled by grain boundary sliding [1], which explicitly incorporates the grain-size dependence of ice rheology. Yet, neither dislocation creep (n 4), nor grain boundary sliding (n 1.8), have stress exponents that match the value of n 3 for the Glen law. Thus, although the Glen law provides an approximate description of ice flow in glaciers and ice sheets, its functional form cannot be explained by a single deformation mechanism. Here we seek to understand the origin of the n 3 dependence of the Glen law through a new model for grain-size evolution in ice. In our model, grain size evolves in response to the balance between dynamic recrystallization and grain growth. To simulate these processes we adapt the "wattmeter" [2], originally developed within the solid-Earth community to quantify grain size in crustal and mantle rocks. The wattmeter posits that grain size is controlled by a balance between the mechanical work required for grain growth and dynamic grain size reduction. The evolution of grain size in turn controls the relative contributions of dislocation creep and grain boundary sliding, and thus the effective stress exponent for ice flow. Using this approach, we first benchmark our grain size evolution model on experimental data and then calculate grain size in two end-member scenarios: (1) as a function of depth within an ice-sheet, and (2) across an ice-stream margin. We show that the calculated grain sizes match ice core observations for the interior of ice sheets. Furthermore, owing to the influence of grain size on strain rate, the variation in grain size with deformation conditions results in an effective stress exponent intermediate between grain boundary sliding and dislocation creep. [1] Goldsby & Kohlstedt, JGR, 2001; [2] Austin & Evans, Geology, 1997

Great Basin Mantle Xenoliths Record Deformation Associated with Active Lithospheric Downwelling

NASA Astrophysics Data System (ADS)

Dygert, N. J.; Bernard, R. E.; Behr, W. M.

2017-12-01

Intensely deformed mylonitic mantle peridotite xenoliths are preserved in Pleistocene flows and cinder cones at Lunar Crater volcanic field in central Nevada. They are spatially and chemically associated with coarse-grained lherzolites and harzburgites with remarkably high two-pyroxene and Ca-in-olivine temperatures (all 1200-1300°C [1]), suggesting they originate from the base of the mantle lithosphere. Here we report results of a chemical and microstructural investigation of 14 previously unstudied mylonitic dunites, wehrlites, and pyroxene-poor harzburgites. Orthopyroxenes exhibit little evidence for plastic deformation and in some samples show brittle deformation. Extremely flattened porphyroclastic grains and substantial dynamic recrystallization in olivine suggests deformation occurred by dislocation creep (Fig. 1). Recrystallized olivine grain sizes are 50-86 µm yielding flow stresses of 43-63 MPa according to the grain size piezometer of [2]. Olivines in the dunites and wehrlites have Mg#s of 87-88.5, lower than in coarse grained harzburgites (Mg#s =87.5-91.3). Relatively low mylonite Mg#s suggests the rocks formed as cumulates or products of melt-rock reaction prior to deformation. Electron microprobe analyses confirm the mylonites have two-pyroxene and Ca-in-olivine temperatures >1200°C, consistent with the coarser harzburgites and lherzolites. Trace elements measured in pyroxenes in coarse-grained and mylonitic samples yield REE-in-two-pyroxene temperatures of 1278-1338°C (n=4), demonstrating that the high-temperature signature predates entrainment and eruption. Using our paleostress magnitudes and assuming a hot (1250°C) dry mantle lithosphere implies deformation occurred at strain rates of 10-10/s, too rapid for steady-state lithospheric deformation. We interpret such localized, transient deformation to be a consequence of delamination of a mantle lithospheric drip, as suggested by cylindrical shear wave splitting and body wave anomalies beneath Lunar Crater [e.g., 3]. Strain may have been localized in pyroxene-poor dunites and wherlites owing to the weaker rheology of olivine-rich rocks at these conditions. [1] Smith (2000), JGR 105, 16769-16781. [2] Van der Wal, et al. (1993), GRL 20, 1479-1482. [3] West et al. (2009), Nat. Geo. 2, 439-444.

Analysis of Particle-Stimulated Nucleation (PSN)-Dominated Recrystallization for Hot-Rolled 7050 Aluminum Alloy

NASA Astrophysics Data System (ADS)

Adam, Khaled F.; Long, Zhengdong; Field, David P.

2017-04-01

In 7xxx series aluminum alloys, the constituent large and small second-phase particles present during deformation process. The fraction and spatial distribution of these second-phase particles significantly influence the recrystallized structure, kinetics, and texture in the subsequent treatment. In the present work, the Monte Carlo Potts model was used to model particle-stimulated nucleation (PSN)-dominated recrystallization and grain growth in high-strength aluminum alloy 7050. The driving force for recrystallization is deformation-induced stored energy, which is also strongly affected by the coarse particle distribution. The actual microstructure and particle distribution of hot-rolled plate were used as an initial point for modeling of recrystallization during the subsequent solution heat treatment. Measurements from bright-field TEM images were performed to enhance qualitative interpretations of the developed microstructure. The influence of texture inhomogeneity has been demonstrated from a theoretical point of view using pole figures. Additionally, in situ annealing measurements in SEM were performed to track the orientational and microstructural changes and to provide experimental support for the recrystallization mechanism of PSN in AA7050.

Annealing texture of nanostructured IF steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jamaati, Roohollah, E-mail: jamaati@nit.ac.ir

In the present work, the evolution of annealing texture in nanostructured interstitial free steel fabricated via accumulative roll bonding (ARB) process was investigated. Textural evolution after post-annealing of ARB-processed samples was evaluated using X-ray diffraction. There were several texture transitions in the γ-fiber and ζ-fiber during ARB and post-annealing treatment. It was found that with increasing the number of ARB cycles, the volume fraction of the low angle grain boundary decreased and the high angle grain boundary fraction increased. Also, the shear texture was dominant after the first cycle, while for other samples, the rolling texture was dominant. The one-cyclemore » sample clearly indicated a weak α-fiber and γ-fiber and a relatively strong ζ-fiber. In addition, during the recrystallization and before the grain growth, the intensity of α-fiber and γ-fiber decreased, the intensity of ζ-fiber increased, and the intensity of (011)〈100〉 orientation in the ε-fiber and η-fiber increased. Moreover, it was concluded that the transition from the rolling texture to the shear one was a sign of occurrence of the recrystallization (before the grain growth). Finally, with increasing the number of ARB cycles, the intensity of rolling and shear textures saturated and a stable texture formed. - Highlights: • There were texture transitions in the γ-fiber and ζ-fiber. • When the number of cycles increased, the low angle grain boundaries decreased. • The shear texture was dominant after the first cycle. • Transition from rolling texture to shear one was a sign of recrystallization. • With increasing the number of ARB cycles, a stable texture formed.« less

Microstructures and mechanical behavior of magnesium processed by ECAP at ice-water temperature

NASA Astrophysics Data System (ADS)

Zuo, Dai; Li, Taotao; Liang, Wei; Wen, Xiyu; Yang, Fuqian

2018-05-01

Magnesium of high purity is processed by equal channel angular pressing (ECAP) up to eight passes at the ice-water temperature, in which a core–shell-like structure is used. The core–shell-like structure consists of pure iron (Fe) of 1.5 mm in thickness as the shell and magnesium (Mg) as the core. The microstructure, texture and mechanical behavior of the ECAP-processed Mg are studied. The ECAP processing leads to the formation of fine and equiaxed grains of ~1.1 µm. The basal planes initially parallel to the extrusion direction evolve to slanted basal planes with the tilting angle in a range of 25°–45° to the extrusion direction. Increasing the number of the extrusion passes leads to the decreasing of twins and dislocation density in grains, while individual grains after eight passes still have high dislocation density. The large decreases of twins and the dislocation density make dynamic recrystallization (DRX) difficult, resulting in the decrease of the degree of DRX. Tension test reveals that the mechanical behavior of the ECAP-processed Mg is dependent on grain refinement and textures. The yield strength of the ECAP-extruded Mg first increases with the decrease of the grain size, and then decreases with further decrease of the grain size.

Microstructural control of FeCrAl alloys using Mo and Nb additions

DOE PAGES

Sun, Zhiqian; Bei, Hongbin; Yamamoto, Yukinori

2017-08-14

The effects of Mo and Nb additions on the microstructure and mechanical properties of two FeCrAl alloys were studied in this paper. Fine and uniform recrystallized grain structures (~ 20–30 μm) were achieved in both alloys through suitable annealing after warm-rolling. The formation of Fe 2Nb-type Laves phase precipitates in the Nb-containing FeCrAl alloy effectively stabilized the deformed and recrystallized microstructures. The Mo-containing FeCrAl alloy exhibited strong γ texture fiber after annealing at 650–900 °C, whereas the annealed Nb-containing FeCrAl alloy had much weaker texture. Finally, both strength and ductility decreased as the grain size increased in both alloys.

Strain rate dependent activation of slip systems in calcite marbles from Syros (Cyclades, Greece)

NASA Astrophysics Data System (ADS)

Rogowitz, Anna; Grasemann, Bernhard; Morales, Luiz F. G.; Huet, Benjamin; White, Joseph C.

2017-04-01

The activation of certain slip systems in calcite has been experimentally proven to be highly temperature dependent, but also the strain rate plays an important role on the activation of the dominant slip system. In this study, observations from a flanking structure (i.e. shear zone) that developed under lower greenschist-facies conditions, in an almost pure calcite marble (Syros Island, Greece) are presented. The shear zone is characterized by a strain gradient from the slightly deformed tips (γ ˜ 50) to the highly strained centre (γ up to 1000) while the host rock is moderately deformed (γ ˜ 3). During the shear zone development, the strain gradient coincided with a strain rate gradient with strain rate varying from 10-13 to 10-9 s-1. The studied outcrop thus represents the final state of a natural experiment and gives us a great opportunity to get natural constraints on strain rate dependent mechanical behaviour in a calcite marble. Detailed microstructural analyses have been performed via optical microscopy, electron microscopy, electron backscatter diffraction mapping and transmission electron microscopy, on samples from the highly strained shear zone and the host rock. The analyses show that the calcite microfabric varies depending on position within the shear zone, indicating activation of different deformation, recrystallization mechanisms and slip systems at different strain rates. Up to strain rates of ˜10-10 s-1 the marble deformed exclusively within the dislocation creep field, showing a change in recrystallization mechanism and dominant active slip system. While the marble preferentially recrystallized by grain boundary migration at relatively low strain rates (˜10-13 s-1), subgrain rotation recrystallization seems to be the dominant mechanism at higher strain rates (˜10-12 to 10-10 s-1). At higher strain rates (˜10-9 s-1), the recrystallization mechanism is bulging, resulting in the development of an extremely fine grained ultramylonite (average grain size ˜3 μm) accompanied by a switch in deformation mechanism from dislocation creep to a combined deformation by grain boundary sliding and dislocation activity. Constraints on dominant active slip system depending on deformation strain rate have been made by a combination of misorientation analyses and viscoplastic self-consistent modelling.

Annealing Effects on Microstructure and Mechanical Properties of Ultrafine-Grained Al Composites Reinforced with Nano-Al2O3 by Rotary Swaging

NASA Astrophysics Data System (ADS)

Chen, Cunguang; Wang, Wenwen; Guo, Zhimeng; Sun, Chunbao; Volinsky, Alex A.; Paley, Vladislav

2018-03-01

Microstructure evolution and variations in mechanical properties of Al-Al2O3 nanocomposite produced by powder metallurgy were investigated and compared with commercially pure aluminum (Al-1050) after furnace annealing. Fine gas-atomized Al powder compacts were first sintered in flowing nitrogen, subsequently consolidated into wires by rotary swaging and eventually annealed at 300 and 500 °C for 24 h each. Scanning and transmission electron microscopy with energy-dispersive spectroscopy was utilized to document the microstructure evolution. Rotary swaging was proven to lead to a marked decrease in grain size. After heavy swaging to true deformation degree of φ = 6 and annealing at 500 °C, obvious recrystallization was observed at Al-1050's existing grain boundaries and the crystals began to grow perpendicular to the flow direction. In the Al-Al2O3 nanocomposite, fabricated from d 50 = 6 μm Al powder, recrystallization partially occurred, while grains were still extremely fine. Due to the dual role of fine-grained Al2O3 dispersion strengthening, the nanocomposite showed improved mechanical performance in terms of tensile strength, approximately twice higher than Al-1050 after annealing at 500 °C.

Contrasting accessory mineral behavior in minimum-temperature melts: Empirical constraints from the Himalayan metamorphic core

NASA Astrophysics Data System (ADS)

Cottle, John M.; Larson, Kyle P.; Yakymchuk, Chris

2018-07-01

Medium-grained leucogranite in the Tama Kosi region of the Nepalese Himalayan Metamorphic Core yields a relatively narrow range of monazite 208Pb/232Th dates with a dominant population at 21.0 Ma inferred to represent crystallization of an early plutonic phase. In contrast, the pegmatitic portion of the same intrusive complex, that cross-cuts the medium-grained leucogranite, contains zircon, monazite and xenotime that each display near-identical age spectra, recording semi-continuous (re-)crystallization from 27.5 Ma to 21.0 Ma, followed by a 2 m.y. hiatus then further (re-)crystallization between 19.4 and 18.6 Ma. The "gap" in pegmatite dates corresponds well to the crystallization age of the older leucogranite, whereas the end of accessory phase growth in the pegmatite coincides with the onset of regional-scale cooling. Detailed textural, trace element and thermochronologic data indicate that the range of zircon, monazite and xenotime dates recorded in the pegmatite reflect inherited components that underwent semi-continuous (re-)crystallization during metamorphism and/or anatexis in the source region(s), whereas dates younger than the hiatus indicate accessory phase recrystallization, related to both fluid influx and a concomitant increase in temperature. In contrast, the lack of an inherited component(s) in the medium-grained leucogranite phase is inferred to be a result of complete dissolution during partial melting. A model is proposed in which influx of heat and H2O-rich fluids associated with early leucogranite emplacement temporarily delayed zircon and monazite and xenotime crystallization, respectively. These data highlight the importance of measuring spatially resolved dates, trace elements and textural patterns from multiple accessory minerals combined with model constraints to better understand the often-complex crystallization history of anatectic melts in collisional orogens.

Phosphatized algal-bacterial assemblages in Late Cretaceous phosphorites of the Voronezh Anteclise

NASA Astrophysics Data System (ADS)

Maleonkina, Svetlana Y.

2003-01-01

Late Cretaceous phosphogenesis of the Voronezh Anteclise has occurred during Cenomanian and Early Campanian. SEM studies show the presence of phosphatized algal-bacterial assemblages both in Cenomanian and Campanian phosphorites. In some Cenomanian nodular phosphorite samples revealed empty tubes 1 - 5 microns in diameter, which are most likely trichomes of cyanobacterial filaments. Other samples contained accumulations of spheres 0,5-3 microns, similar to coccoidal bacteria. Complicated tubular forms with variable diameter 2 - 5 microns occur on surface of some quartz grains in nodules. They are probably pseudomorphs after algae. We found similar formations in the Campanian phosphate grains. Frequently, grain represents a cyanobacterial mat, which is sometimes concentrically coated by phosphatic films. The films of some grains retain the primary structure, their concentric layers are formed by pseudomorphs after different bacterial types and obviously they represent oncolite. In other cases, the primary structure is unobservable because of recrystallization process erases them. Occasionally, the central part retains the coccoidal structure and the recrystallization affects only films. Besides the core of such oncolite can be represented not only by phosphatic grain, but also by grains of other minerals, such as quartz, glauconite and heavy minerals, which serve as a substrate for cyanobacterial colonies. Bacteria also could settle on cavity surfaces and interiors frames of sponge fragments, teeth and bones.

A novel ultra-low carbon grain oriented silicon steel produced by twin-roll strip casting

NASA Astrophysics Data System (ADS)

Wang, Yang; Zhang, Yuan-Xiang; Lu, Xiang; Fang, Feng; Xu, Yun-Bo; Cao, Guang-Ming; Li, Cheng-Gang; Misra, R. D. K.; Wang, Guo-Dong

2016-12-01

A novel ultra-low carbon grain oriented silicon steel was successfully produced by strip casting and two-stage cold rolling method. The microstructure, texture and precipitate evolution under different first cold rolling reduction were investigated. It was shown that the as-cast strip was mainly composed of equiaxed grains and characterized by very weak Goss texture ({110}<001>) and λ-fiber (<001>//ND). The coarse sulfides of size 100 nm were precipitated at grain boundaries during strip casting, while nitrides remained in solution in the as-cast strip and the fine AlN particles of size 20-50 nm, which were used as grain growth inhibitors, were formed in intermediate annealed sheet after first cold rolling. In addition, the suitable Goss nuclei for secondary recrystallization were also formed during intermediate annealing, which is totally different from the conventional process that the Goss nuclei originated in the subsurface layer of the hot rolled sheet. Furthermore, the number of AlN inhibitors and the intensity of desirable Goss texture increased with increasing first cold rolling reduction. After secondary recrystallization annealing, very large grains of size 10-40 mm were formed and the final magnetic induction, B8, was as high as 1.9 T.

Structures and transitions in tungsten grain boundaries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Frolov, T.; Zhu, Q.; Marian, J.

2017-02-07

The objective of this study is to develop a computational methodology to predict structure, energies of tungsten grain boundaries as a function of misorientation and inclination. The energies and the mobilities are the necessary input for thermomechanical model of recrystallization of tungsten for magnetic fusion applications being developed by the Marian Group at UCLA.

Study of twin-roll cast Aluminium alloys subjected to severe plastic deformation by equal channel angular pressing

NASA Astrophysics Data System (ADS)

Poková, M.; Cieslar, M.

2014-08-01

Aluminium alloys prepared by twin-roll casting method become widely used in industry applications. Their high solid solution supersaturation and finer grains ensure better mechanical properties when compared with the direct-chill cast ones. One of the possibilities how to enhance their thermal stability is the addition of zirconium. After heat treatment Al3Zr precipitates form and these pin moving grain boundaries when the material is exposed to higher temperatures. In the present work twin-roll cast aluminium alloys based on AA3003 with and without Zr addition were annealed for 8 hours at 450 °C to enable precipitation of Al3Zr phase. Afterwards they were subjected to severe plastic deformation by equal channel angular pressing, which led to the reduction of average grain size under 1 μm. During subsequent isochronal annealing recovery and recrystallization took place. These processes were monitored by microhardness measurements, light optical microscopy and in-situ transmission electron microscopy. The addition of Zr stabilizes the grain size and increases the recrystallization temperature by 100 °C.

Effects of asymmetric rolling process on ridging resistance of ultra-purified 17%Cr ferritic stainless steel

NASA Astrophysics Data System (ADS)

Lu, Cheng-zhuang; Li, Jing-yuan; Fang, Zhi

2018-02-01

In ferritic stainless steels, a significant non-uniform recrystallization orientation and a substantial texture gradient usually occur, which can degrade the ridging resistance of the final sheets. To improve the homogeneity of the recrystallization orientation and reduce the texture gradient in ultra-purified 17%Cr ferritic stainless steel, in this work, we performed conventional and asymmetric rolling processes and conducted macro and micro-texture analyses to investigate texture evolution under different cold-rolling conditions. In the conventional rolling specimens, we observed that the deformation was not uniform in the thickness direction, whereas there was homogeneous shear deformation in the asymmetric rolling specimens as well as the formation of uniform recrystallized grains and random orientation grains in the final annealing sheets. As such, the ridging resistance of the final sheets was significantly improved by employing the asymmetric rolling process. This result indicates with certainty that the texture gradient and orientation inhomogeneity can be attributed to non-uniform deformation, whereas the uniform orientation gradient in the thickness direction is explained by the increased number of shear bands obtained in the asymmetric rolling process.

3D microstructural evolution of primary recrystallization and grain growth in cold rolled single-phase aluminum alloys

NASA Astrophysics Data System (ADS)

Adam, Khaled; Zöllner, Dana; Field, David P.

2018-04-01

Modeling the microstructural evolution during recrystallization is a powerful tool for the profound understanding of alloy behavior and for use in optimizing engineering properties through annealing. In particular, the mechanical properties of metallic alloys are highly dependent upon evolved microstructure and texture from the softening process. In the present work, a Monte Carlo (MC) Potts model was used to model the primary recrystallization and grain growth in cold rolled single-phase Al alloy. The microstructural representation of two kinds of dislocation densities, statistically stored dislocations and geometrically necessary dislocations were quantified based on the ViscoPlastic Fast Fourier transform method. This representation was then introduced into the MC Potts model to identify the favorable sites for nucleation where orientation gradients and entanglements of dislocations are high. Additionally, in situ observations of non-isothermal microstructure evolution for single-phase aluminum alloy 1100 were made to validate the simulation. The influence of the texture inhomogeneity is analyzed from a theoretical point of view using an orientation distribution function for deformed and evolved texture.

Mechanical Properties and Microstructural Evolution of Variable-Plane-Rolled Mg-3Al-1Zn Alloy

NASA Astrophysics Data System (ADS)

Zhu, Rong; Bian, Cunjian; Wu, Yanjun

2017-04-01

The microstructural evolution and mechanical properties of AZ31 magnesium alloy produced by variable-plane rolling (VPR) were investigated. Two types of weak textures were formed: basal texture in odd pass and double-peak basal texture in even pass. Dynamic recrystallization (DRX) was observed during the VPR treatment, and the nucleation of grains during DRX was dependent on the coalescence of subgrains. Three types of twins were observed in the VPR treatment: {10-12} extension twins, {10-13} contraction twins and {10-11}-{10-12} double twins. The {10-11}-{10-12} double twinning is the underlying mechanism in the formation of the double-peak texture. Tensile testing revealed improved strength without loss of ductility. The Hall-Petch relationship can be used to describe the strengths in any even pass with the same texture. The significant strengthening is ascribed to the refined grain, twin boundaries, texture hardening, and high dislocation density.

Contributions of phase and structural transformations in multicomponent Al-Mg alloys to the linear and nonlinear mechanisms of anelasticity

NASA Astrophysics Data System (ADS)

Golovin, I. S.; Bychkov, A. S.; Mikhailovskaya, A. V.; Dobatkin, S. V.

2014-02-01

The effects of the processes of severe plastic deformation (SPD), recrystallization, and precipitation of the β phase in multicomponent alloys of the Al-5Mg-Mn-Cr and Al-(4-5%)Mg-Mn-Zn-Sc systems on the mechanisms of grain-boundary relaxation and dislocation-induced microplasticity have been studied in some detail. To stabilize the ultrafine-grained structure and prevent grain growth, dispersed Al-transition-metal particles, such as Al3Zr, Al6Mn, Al7Cr, Al6(Mn,Cr), Al18Cr2Mg3 have been used. We have special interest in alloys with additions of scandium, which forms compounds of the Al3Sc type and favors the precipitation of finer particles compared to the aluminides of other transition metals. After SPD, Al-(4-5%)Mg-Mn-Zr-Sc alloys exhibit an enhanced recrystallization temperature. The general features of the dislocation and grain-boundary anelasticity that have been established for the binary Al-Mg alloys are retained; i.e., (1) the decrease in the dislocation density in the process of recrystallization of cold-worked alloys leads to the formation of a pseudo-peak in the curves of the temperature dependences of internal friction (TDIF) and to a decrease in the critical amplitude of deformation corresponding to the onset of dislocation motion in a stress field; (2) the precipitation of the β phase suppresses the grain-boundary relaxation; (3) the dissolution of the β phase, the passage of the magnesium atoms into the solid solution, and the precipitation of the β' phase upon heating hinder the motion of dislocations; (4) the coarsening of the highly dispersed particles containing Zr and Sc increases the dislocation mobility. The grain-boundary relaxation and dislocation-impurity interaction and their temperature dependences, as well as processes of the additional alloying of the binary alloys by Mn, Cr, Zr, and Sc, have been estimated quantitatively.

Deformation ages within the Klong Marui continental wrench fault, southern Thailand

NASA Astrophysics Data System (ADS)

Kanjanapayont, P.; Grasemann, B.; Edwards, M. A.

2009-04-01

The Klong Marui Fault is a ductile to brittle dextral strike-slip shear zone characterized by strong NNE-SSW geomorphic ridges trending up to 150 km. from Thai Gulf to Andaman Sea. At it southern part in the Phung Nga region, the ductile core forms a 40km long ridge. The geology within this wrench zone consisted of steep strongly deformed layers of migmatitic gneisses, mylonitic granites/pegmatites and phyllonitic metapelites. Brittle cataclasitc zones were localized in the eastern and western margin of this ductile core zone. The first deformation stage was dextral ductile strike-slip movement at mid to upper crustal levels and formed the main mylonitic foliation (c), secondary synthetic foliations (c'), and lineation in the migmatitic gneisses, mylonitic granites and metapelites. Locally sillimanite-clasts in high-temperature recrystallization quartz fabric fabric suggest deformation at amphibolite facies condition. More typically, quartz dynamically recrystallize by subgrain rotation and grain boundary migration under greenschist facies conditions. Microstructure of myrmekite and "V"-pull-apart clearly indicates dextral sense of shear. Pegmatites cross-cut the main mylonitic foliation but were sheared at the rims indicating syn-kinematic emplacement. Dynamically recrystallizing quartz mainly by basal gliding, bulging and low-temperature subgrain rotation record the latest stage of ductile dextral strike-slip deformation during decreasing temperature conditions. The NNE-SSW trending dextral strike-slip deformation accommodated the E-W transpression as a result of the differential movement of the northward drifting Indian craton and Asia. The brittle/ductile deformation produced cataclasites and minor faults which overprint the higher temperature fabric causing exhumation and juxtaposition of fault rocks developed under different metamorphic conditions in a positive flower structure.

Holographic fabrication of gratings in metal substrates

NASA Technical Reports Server (NTRS)

Fletcher, R. M.; Wagner, D. K.; Ballantyne, J. M.

1982-01-01

A program for investigating the grain enlargement resulting from the laser recrystallization of a thin gallium arsenide film on a patterned substrate, a technique known as graphoepitaxy was evaluated. More specifically, the effects of recrystallizing an uncapped gallium arsenide film using a continuous wave neodymium YAG laser operating at 1.06 microns were studied. In an effort to minimize arsenic loss from the film, the specimens were held in an arsine atmosphere during recrystallization. Two methods for fabricating patterned substrates were developed, one using reactive ion etching of a molybdenum film on both sapphire and silicon substates and another by preferential wet etching of a silicon substrate onto which a film of molybdenum was subsequently deposited.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Kun; Bannister, Mark E.; Meyer, Fred W.

Here, in a magnetic fusion energy (MFE) device, the plasma-facing materials (PFMs) will be subjected to tremendous fluxes of ions, heat, and neutrons. The response of PFMs to the fusion environment is still not well defined. Tungsten metal is the present candidate of choice for PFM applications such as the divertor in ITER. However, tungsten's microstructure will evolve in service, possibly to include recrystallization. How tungsten's response to plasma exposure evolves with changes in microstructure is presently unknown. In this work, we have exposed hot-worked and recrystallized tungsten to an 80 eV helium ion beam at a temperature of 900more » °C to fluences of 2 × 10 23 or 20 × 10 23 He/m 2. This resulted in a faceted surface structure at the lower fluence or short but well-developed nanofuzz structure at the higher fluence. There was little difference in the hot-rolled or recrystallized material's near-surface (≤50 nm) bubbles at either fluence. At higher fluence and deeper depth, the bubble populations of the hot-rolled and recrystallized were different, the recrystallized being larger and deeper. This may explain previous high-fluence results showing pronounced differences in recrystallized material. The deeper penetration in recrystallized material also implies that grain boundaries are traps, rather than high-diffusivity paths.« less

Texture Development in a Friction Stir Lap-Welded AZ31B Magnesium Alloy

NASA Astrophysics Data System (ADS)

Naik, B. S.; Chen, D. L.; Cao, X.; Wanjara, P.

2014-09-01

The present study was aimed at characterizing the microstructure, texture, hardness, and tensile properties of an AZ31B-H24 Mg alloy that was friction stir lap welded (FSLWed) at varying tool rotational rates and welding speeds. Friction stir lap welding (FSLW) resulted in the presence of recrystallized grains and an associated hardness drop in the stir zone (SZ). Microstructural investigation showed that both the AZ31B-H24 Mg base metal (BM) and SZ contained β-Mg17Al12 and Al8Mn5 second phase particles. The AZ31B-H24 BM contained a type of basal texture (0001)<110> with the (0001) plane nearly parallel to the rolled sheet surface and <110> directions aligned in the rolling direction. FSLW resulted in the formation of another type of basal texture (0001)<100> in the SZ, where the basal planes (0001) became slightly tilted toward the transverse direction, and the prismatic planes (100) and pyramidal planes (101) exhibited a 30 deg + ( n - 1) × 60 deg rotation ( n = 1, 2, 3, …) with respect to the rolled sheet normal direction, due to the shear plastic flow near the pin surface that occurred from the intense local stirring. With increasing tool rotational rate and decreasing welding speed, the maximum intensity of the basal poles (0001) in the SZ decreased due to a higher degree of dynamic recrystallization that led to a weaker or more random texture. The tool rotational rate and welding speed had a strong effect on the failure load of FSLWed joints. A combination of relatively high welding speed (20 mm/s) and low tool rotational rate (1000 rpm) was observed to be capable of achieving a high failure load. This was attributed to the relatively small recrystallized grains and high intensity of the basal poles in the SZ arising from the low heat input as well as the presence of a small hooking defect.

The Influence of Interfacial Roughness on Fiber Sliding in Oxide Composites with La-Monazite Interphases

NASA Technical Reports Server (NTRS)

Davis, J. B.; Hay, R. S.; Marshall, D. B.; Morgan, P. E. D.; Sayir, A.; Gray, Hugh R. (Technical Monitor); Farmer, Serene C. (Technical Monitor)

2002-01-01

Room temperature debonding and sliding of La-Monazite coated fibers is assessed using a composite with a polycrystalline alumina matrix and fibers of several different single crystal (mullite, sapphire) and directionally solidified eutectic (Al2O3/Y3Al5O12 and Al2O3/Y-ZrO2) compositions. These fibers provide a range of residual stresses and interfacial roughnesses. Sliding occurred over a debond crack at the fiber-coating interface when the sliding displacement and surface roughness were relatively small. At large sliding displacements with relatively rough interfaces, the monazite coatings were deformed extensively by fracture, dislocations and occasional twinning, whereas the fibers were undamaged. Dense, fine-grained (10 nm) microstructures suggestive of dynamic recrystallization were also observed in the coatings. Frictional heating during sliding is assessed. The possibility of low temperature recrystallization is discussed in the light of the known resistance of monazite to radiation damage. The ability of La-Monazite to undergo plastic deformation relatively easily at low temperatures may be enabling for its use as a composite interface.

Microstructure Characterization and Stress Corrosion Evaluation of Autogenous and Hybrid Friction Stir Welded Al-Cu-Li 2195 Alloy

NASA Technical Reports Server (NTRS)

Li, Zhixian; Arbegast, William J.; Meletis, Efstathios I.

1997-01-01

Friction stir welding process is being evaluated for application on the Al-Cu-Li 2195 Super-Light Weight External Tank of the Space Transportation System. In the present investigation Al-Cu-Li 2195 plates were joined by autogenous friction stir welding (FSW) and hybrid FSW (friction stir welding over existing variable polarity plasma arc weld). Optical microscopy and transmission electron microscopy (TEM) were utilized to characterize microstructures of the weldments processed by both welding methods. TEM observations of autogenous FSW coupons in the center section of the dynamically-recrystallized zone showed an equiaxed recrystallized microstructure with an average grain size of approx. 3.8 microns. No T(sub 1), precipitates were present in the above-mentioned zone. Instead, T(sub B) and alpha precipitates were found in this zone with a lower population. Alternate immersion, anodic polarization, constant load, and slow strain tests were carried out to evaluate the general corrosion and stress-corrosion properties of autogenous and hybrid FSW prepared coupons. The experimental results will be discussed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Deibler, Lisa Anne; Brown, Arthur; Puskar, Joseph D.

Drawn 304L stainless steel tubing was subjected to 42 different annealing heat treatments with the goal of initializing a microstructural model to select a heat treatment to soften the tubing from a hardness of 305 Knoop to 225–275 Knoop. The amount of recrystallization and grain size caused by 18 heat treatments were analyzed via optical microscopy and image analysis, revealing the full range of recrystallization from 0 to 100%. The formation of carbides during the longer duration and higher-temperature heat treatments was monitored via transmission electron microscope evaluation. The experimental results informed a model which includes recovery, recrystallization, and grainmore » growth to predict microstructure and hardness. After initialization of the model, it was able to predict hardness with a R 2 value of 0.95 and recrystallization with an R 2 value of 0.99. As a result, the model was then utilized in the design and testing of a heat treatment to soften the tubing.« less

On a Fast and Accurate In Situ Measuring Strategy for Recrystallization Kinetics and Its Application to an Al-Fe-Si Alloy

NASA Astrophysics Data System (ADS)

Kühbach, Markus; Brüggemann, Thiemo; Molodov, Konstantin D.; Gottstein, Günter

2015-03-01

In the current study, we detail a novel in situ X-ray diffraction-based bulk measurement technique, which allows for the continuous tracking of primary recrystallization kinetics. The approach is based on measuring the diffracted intensity that is correlated with the evolution of the volume fraction of particular texture components during annealing of a sample within a texture goniometer. The method is applied in an experimental study on a cold-rolled industrial Al-Fe-Si alloy. For comparison purposes, the macrotexture and the hardness evolution were monitored ex situ along isothermal and nonisothermal annealing. These measurements were then contrasted to the in situ obtained growth kinetics of recrystallizing grains in beta-fiber deformation and cube orientation. The results showed clearly that this method can be reliably utilized for the characterization of recrystallization kinetics in an industrial context.

Microstructure Evolution during Dissimilar Friction Stir Welding of AA7003-T4 and AA6060-T4.

PubMed

Dong, Jialiang; Zhang, Datong; Zhang, Weiwen; Zhang, Wen; Qiu, Cheng

2018-02-27

In this work, the dissimilar joint of AA7003-T4 and 6060-T4 alloy has been produced by friction stir welding (FSW). The microstructure was examined by optical microscope (OM), electron back scattered diffraction (EBSD), transmission electron microscopy (TEM), and the mechanical properties of the joint were investigated. It is demonstrated that sound dissimilar joint can be produced through FSW. In the nugget; precipitations dissolve into the matrix and η' reprecipitate subsequently; and the elongated aluminum grains are replaced by fine and equiaxed grains due to dynamic recrystallization (DRX). In the heat affected zone (HAZ), coarse β' and η precipitates are formed and the aluminum grains are coarser as compared to the base materials. In the thermo-mechanical affected zone (TMAZ), equiaxed and elongated grains coexist due to incomplete DRX. The ultimate tensile strength of the dissimilar joint is 159.2 MPa and its elongation is 10.4%. The weak area exists in the HAZ of 6060 alloy, which is placed in the retreating side during FSW. The correlations between the microstucture and mechanical properties of the dissimilar joint are discussed.

Microstructure Evolution during Dissimilar Friction Stir Welding of AA7003-T4 and AA6060-T4

PubMed Central

Dong, Jialiang; Zhang, Datong; Zhang, Weiwen; Zhang, Wen; Qiu, Cheng

2018-01-01

In this work, the dissimilar joint of AA7003-T4 and 6060-T4 alloy has been produced by friction stir welding (FSW). The microstructure was examined by optical microscope (OM), electron back scattered diffraction (EBSD), transmission electron microscopy (TEM), and the mechanical properties of the joint were investigated. It is demonstrated that sound dissimilar joint can be produced through FSW. In the nugget; precipitations dissolve into the matrix and η′ reprecipitate subsequently; and the elongated aluminum grains are replaced by fine and equiaxed grains due to dynamic recrystallization (DRX). In the heat affected zone (HAZ), coarse β′ and η precipitates are formed and the aluminum grains are coarser as compared to the base materials. In the thermo-mechanical affected zone (TMAZ), equiaxed and elongated grains coexist due to incomplete DRX. The ultimate tensile strength of the dissimilar joint is 159.2 MPa and its elongation is 10.4%. The weak area exists in the HAZ of 6060 alloy, which is placed in the retreating side during FSW. The correlations between the microstucture and mechanical properties of the dissimilar joint are discussed. PMID:29495463

Microstructure and mechanical properties of AZ91 magnesium alloy subject to deep cryogenic treatments

NASA Astrophysics Data System (ADS)

Li, Gui-rong; Wang, Hong-ming; Cai, Yun; Zhao, Yu-tao; Wang, Jun-jie; Gill, Simon P. A.

2013-09-01

AZ91 magnesium alloy was subjected to a deep cryogenic treatment. X-ray diffraction (XRD), scanning electronic microscopy (SEM), and transmission electronic microscopy (TEM) methods were utilized to characterize the composition and microstructure of the treated samples. The results show that after two cryogenic treatments, the quantity of the precipitate hardening β phase increases, and the sizes of the precipitates are refined from 8-10 μm to 2-4 μm. This is expected to be due to the decreased solubility of aluminum in the matrix at low temperature and the significant plastic deformation owing to internal differences in thermal contraction between phases and grains. The polycrystalline matrix is also noticeably refined, with the sizes of the subsequent nanocrystalline grains in the range of 50-100 nm. High density dislocations are observed to pile up at the grain boundaries, inducing the dynamic recrystallization of the microstructure, leading to the generation of a nanocrystalline grain structure. After two deep cryogenic treatments, the tensile strength and elongation are found to be substantially increased, rising from 243 MPa and 4.4% of as-cast state to 299 MPa and 5.1%.

Surface modifications on toughened, fine-grained, recrystallized tungsten with repetitive ELM-like pulsed plasma irradiation

NASA Astrophysics Data System (ADS)

Kikuchi, Y.; Sakuma, I.; Kitagawa, Y.; Asai, Y.; Onishi, K.; Fukumoto, N.; Nagata, M.; Ueda, Y.; Kurishita, H.

2015-08-01

Surface modifications of toughened, fine-grained, recrystallized tungsten (TFGR W) materials with 1.1 wt.% TiC and 3.3 wt.% TaC dispersoids due to repetitive ELM-like pulsed (∼0.15 ms) helium plasma irradiation have been investigated by using a magnetized coaxial plasma gun. No surface cracking at the center part of the TFGR W samples exposed to 20 plasma pulses of ∼0.3 MJ m-2 was observed. The suppression of surface crack formation due to the increase of the grain boundary strength by addition of TiC and TaC dispersoids was confirmed in comparison with a pure W material. On the other hand, surface cracks and small pits appeared at the edge part of the TFGR W sample after the pulsed plasma irradiation. Erosion of the TiC and TaC dispersoids due to the pulsed plasma irradiation could cause the small pits on the surface, resulting in the surface crack formation.

Post Deformation at Room and Cryogenic Temperature Cooling Media on Severely Deformed 1050-Aluminum

NASA Astrophysics Data System (ADS)

Khorrami, M. Sarkari; Kazeminezhad, M.

2018-03-01

The annealed 1050-aluminum sheets were initially subjected to the severe plastic deformation through two passes of constrained groove pressing (CGP) process. The obtained specimens were post-deformed by friction stir processing at room and cryogenic temperature cooling media. The microstructure evolutions during mentioned processes in terms of grain structure, misorientation distribution, and grain orientation spread (GOS) were characterized using electron backscattered diffraction. The annealed sample contained a large number of "recrystallized" grains and relatively large fraction (78%) of high-angle grain boundaries (HAGBs). When CGP process was applied on the annealed specimen, the elongated grains with interior substructure were developed, which was responsible for the formation of 80% low-angle grain boundaries. The GOS map of the severely deformed specimen manifested the formation of 43% "distorted" and 51% "substructured" grains. The post deformation of severely deformed aluminum at room temperature led to the increase in the fraction of HAGBs from 20 to 60%. Also, it gave rise to the formation of "recrystallized" grains with the average size of 13 μm, which were coarser than the grains predicted by Zener-Hollomon parameter. This was attributed to the occurrence of appreciable grain growth during post deformation. In the case of post deformation at cryogenic temperature cooling medium, the grain size was decreased, which was in well agreement with the predicted grain size. The cumulative distribution of misorientation was the same for both processing routes. Mechanical properties characterizations in terms of nano-indentation and tensile tests revealed that the post deformation process led to the reduction in hardness, yield stress, and ultimate tensile strength of the severely deformed aluminum.

Microstructural Evolution and Dynamic Softening Mechanisms of Al-Zn-Mg-Cu Alloy during Hot Compressive Deformation

PubMed Central

Shi, Cangji; Lai, Jing; Chen, X.-Grant

2014-01-01

The hot deformation behavior and microstructural evolution of an Al-Zn-Mg-Cu (7150) alloy was studied during hot compression at various temperatures (300 to 450 °C) and strain rates (0.001 to 10 s−1). A decline ratio map of flow stresses was proposed and divided into five deformation domains, in which the flow stress behavior was correlated with different microstructures and dynamic softening mechanisms. The results reveal that the dynamic recovery is the sole softening mechanism at temperatures of 300 to 400 °C with various strain rates and at temperatures of 400 to 450 °C with strain rates between 1 and 10 s−1. The level of dynamic recovery increases with increasing temperature and with decreasing strain rate. At the high deformation temperature of 450 °C with strain rates of 0.001 to 0.1 s−1, a partially recrystallized microstructure was observed, and the dynamic recrystallization (DRX) provided an alternative softening mechanism. Two kinds of DRX might operate at the high temperature, in which discontinuous dynamic recrystallization was involved at higher strain rates and continuous dynamic recrystallization was implied at lower strain rates. PMID:28788454

Effect of Austenite Deformation on the Microstructure Evolution and Grain Refinement Under Accelerated Cooling Conditions

NASA Astrophysics Data System (ADS)

Zhao, H.; Palmiere, E. J.

2017-07-01

Although there has been much research regarding the effect of austenite deformation on accelerated cooled microstructures in microalloyed steels, there is still a lack of accurate data on boundary densities and effective grain sizes. Previous results observed from optical micrographs are not accurate enough, because, for displacive transformation products, a substantial part of the boundaries have disorientation angles below 15 deg. Therefore, in this research, a niobium microalloyed steel was used and electron backscattering diffraction mappings were performed on all of the transformed microstructures to obtain accurate results on boundary densities and grain refinement. It was found that with strain rising from 0 to 0.5, a transition from bainitic ferrite to acicular ferrite occurs and the effective grain size reduces from 5.7 to 3.1 μm. When further increasing strain from 0.5 to 0.7, dynamic recrystallization was triggered and postdynamic softening occurred during the accelerated cooling, leading to an inhomogeneous and coarse transformed microstructure. In the entire strain range, the density changes of boundaries with different disorientation angles are distinct, due to different boundary formation mechanisms. Finally, the controversial influence of austenite deformation on effective grain size of low-temperature transformation products was argued to be related to the differences in transformation conditions and final microstructures.

Tailoring microstructure of Mg–Zn–Y alloys with quasicrystal and related phases for high mechanical strength

PubMed Central

Singh, Alok

2014-01-01

The occurrence of a stable icosahedral (i-) phase, which is quasicrystalline with an icosahedral (fivefold) symmetry, on the equilibrium phase diagram of Mg–Zn–RE (RE = Y, Gd, Tb, Dy, Ho or Er) alloys opened up an interesting possibility of developing a new series of magnesium alloys for structural applications. Alloys based on the i-phase have been studied for the past 14 years. Ultra-high strengths combined with good ductility have been shown. Here we show two strategies for tailoring microstructures for very high strengths in Mg–Zn–Y alloys. One of them involves strengthening by a fine distribution of rod-like precipitates, where the matrix grain size is not critical. The alloy is solutionized at a high temperature of 480 °C to dissolve a large part of the i-phase, followed by a high temperature extrusion (∼430 °C) and a low temperature ageing to reprecipitate phases with fine size distribution. At first, phase transformations involved in this procedure are described. The closeness of the structure of the precipitates to the i-phase is brought out. By this procedure, tensile yield strengths of over 370 MPa are obtained in grain sizes of 20 μm. In another strategy, the alloys are chill cast and then extruded at low temperatures of about 250 °C. Ultra-fine grains are produced by enhanced recrystallization due to presence of the i-phase. At the same time nano-sized precipitates are precipitated dynamically during extrusion from the supersaturated matrix. Ultra-high tensile strengths of up to 400 MPa are obtained in combination with ductility of 12 to 16%. Analysis of the microstructure shows that strengthening by the i-phase occurs by enhanced recrystallization during extrusion. It produces ultra-fine grain sizes to give very high strengths, and moderate texture for good ductility. Fine distribution of the i-phase and precipitates contribute to strengthening and provide microstructre stability. Ultra-high strength over a very wide range of grain sizes is thus demonstrated, by utilizing different strengthening effects. PMID:27877701

The Effect of Dynamic Recrystallization on Monotonic and Cyclic Behaviour of Al-Cu-Mg Alloy.

PubMed

Tomczyk, Adam; Seweryn, Andrzej; Grądzka-Dahlke, Małgorzata

2018-05-23

The paper presents an investigation that was conducted to determine the possibility of the occurrence of the process of dynamic recrystallization in 2024 alloy during monotonic tensile and creep tests at the elevated temperatures of 100 °C, 200 °C, and 300 °C. As-extruded material was subjected to creep process with constant force at elevated temperatures, until two varying degrees of deformation were reached. After cooling at ambient temperature, the pre-deformed material was subjected to monotonic and fatigue tests as well as metallographic analysis. The process of dynamic recrystallization was determined in monotonic tests to occur at low strain rate (0.0015/s) only at the temperature of 300 °C. However, in the creep tests, this process occurred with varying efficiency, both during creep at 200 °C and 300 °C. Dynamic recrystallization was indicated to have a significant influence on the monotonic and cyclic properties of the material.

Evolution mechanisms of the primary α and β phases during α/β deformation of an α/β titanium alloy TC8

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Ke, E-mail: study_ke@cqu.edu.cn

A TC8 titanium alloy was isothermally compressed at the strain rates of 10–50 s{sup −1} in the two-phase region of 820–940 °C, and the evolution mechanisms of the primary α and β phases, including grain morphology, dynamic recovery (DRV) and dynamic recrystallization (DRX), were investigated by optical microscopy (OM) and transmission electron microscopy (TEM). OM reveals that the phase content and grain morphology are more significantly influenced by the deformation temperature than the strain rate. The β grains achieve refinement only at 940 °C due to DRX in the β phase. TEM reveals the remarkable variations of the DRX grains,more » subgrains, sub-boundaries and dislocations morphology with temperature and strain rate related to DRV and DRX in the primary α phase. The DRX in the primary α phase appears most strongly at a middle temperature of 860 °C, and DRV dominates in the primary α phase at 940 °C. While the dominant mechanism varies from DRV to DRX in the β phase as the temperature increases. Finally, the influence mechanism of deformation parameters on the primary α grain morphology is revealed based on the combined effect of DRV and DRX in the primary α phase and diffusion of the β phase. - Highlights: •The β grains achieve refinement only at 940 °C due to DRX in the β phase. •The DRX in the primary α phase is most remarkable at 860 °C. •The dominant mechanism in β phase varies from DRV to DRX with increasing temperature. •The interaction between the primary α and β phases depends on the phase content.« less

A Low Resistance Infrared Bolometer for Use with a Squid Detection System.

DTIC Science & Technology

1982-09-24

sensitivity. After treatment at 350C (near the Au-Ge eutectic temperature) the sensitivity and resistance decreased, as shown in Fig. 6. The as-evaporated... recrystallize with a very fine grain size, however, the thicker film (Sample No. 7A) revealed larger topographic bumps, Figure 21(b). The light etch sample (No...LOS ANGEI.ES. CA. 900fi ....... areas were of a similar thickness on both sets of samples. The thin film (Sample 3A) recrystallized in the contact

Fundamental Studies on High Temperature Deformation, Recrystallization, and Grain Growth of Two-Phase Materials

DTIC Science & Technology

1990-09-26

50 ml. Glycerine R -etch 17 ml. Benzalkonium Chloride 35 ml. Ethanol Kroll - etch 2 ml. Hydrofluoric Acid ( 50 %) 4 ml. Nitric Acid Conc. 100 ml...The amount of work given ( 60 % reduction in area ) in this last step was found to be sufficient to recrystallize all of the alloys within 12 hours at...formed at the center of thedisc with the following solution: 10 gins. Zinc Chloride 5 gms. Aluminum Chloride 300 ml. Methanol 50 ml. N - Butanol A JEOL

Interface-Driven Phenomena in Solids: Thermodynamics, Kinetics and Chemistry

DOE PAGES

Abdeljawad, Fadi; Foiles, Stephen M.

2016-05-04

The study of materials interfaces dates back over a century. In solid systems and from an engineering perspective, free surfaces and internal (grain and/or phase) boundaries influence a wide range of properties, such as thermal, electrical and optical transport, and mechanical ones. The properties and the role of interfaces has been discussed extensively in various reviews such as by Sutton and Balluffi. As the characteristic feature size of a materials system (i.e., grain size) is decreased to the nanometer scale, interface-driven physics is expected to dominate due to the increased density of such planar defects. Moreover, interfacial attributes, thermodynamics, andmore » mobility play a key role in phase transformations, such as solidification dynamics and structural transitions in solids, and in homogenization and microstructural evolution processes, such as grain growth, coarsening, and recrystallization. In summary, the set of articles published in this special topic titled: “Interface-Driven Phenomena in Solids: Thermodynamics, Kinetics and Chemistry” covers topics related to microstructure evolution, segregation/adsorption phenomena and interface interactions with other materials defects.« less

Interface-Driven Phenomena in Solids: Thermodynamics, Kinetics and Chemistry

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abdeljawad, Fadi; Foiles, Stephen M.

The study of materials interfaces dates back over a century. In solid systems and from an engineering perspective, free surfaces and internal (grain and/or phase) boundaries influence a wide range of properties, such as thermal, electrical and optical transport, and mechanical ones. The properties and the role of interfaces has been discussed extensively in various reviews such as by Sutton and Balluffi. As the characteristic feature size of a materials system (i.e., grain size) is decreased to the nanometer scale, interface-driven physics is expected to dominate due to the increased density of such planar defects. Moreover, interfacial attributes, thermodynamics, andmore » mobility play a key role in phase transformations, such as solidification dynamics and structural transitions in solids, and in homogenization and microstructural evolution processes, such as grain growth, coarsening, and recrystallization. In summary, the set of articles published in this special topic titled: “Interface-Driven Phenomena in Solids: Thermodynamics, Kinetics and Chemistry” covers topics related to microstructure evolution, segregation/adsorption phenomena and interface interactions with other materials defects.« less

Different slip systems controlling crystallographic preferred orientation and intracrystalline deformation of amphibole in mylonites from the Neyriz mantle diapir, Iran

NASA Astrophysics Data System (ADS)

Elyaszadeh, Ramin; Prior, David J.; Sarkarinejad, Khalil; Mansouri, Hadiseh

2018-02-01

A deformed layered gabbro and a mylonitic gabbro sample from the marginal shear zone of the Neyriz mantle diapir in Iran were analyzed using electron backscatter diffraction (EBSD). Both samples have the common amphibole crystallographic preferred orientation (CPO) in which (100) lies perpendicular to foliation and <001> parallel to lineation. Amphibole grains in the layered gabbro sample have little internal deformation, whereas in the mylonitic gabbro sample the amphibole grains are strongly distorted and contain low angle grain boundaries. There is a subtle change in CPO as a function of grain size in the mylonitic gabbro. Coarse grains (porphyroclasts) have a (100) <001> CPO oriented with the main foliation reference frame whilst fine grains have a (100) <001> CPO oriented with the C‧ shear bands. Detailed analysis of porphyroclast distortions and subgrain boundary trace analysis suggests that hard slip systems, most particularly (110) <1-10> control intracrystalline deformation. Schmid factor analysis suggest that these slip systems are not involved in foliation formation but are linked kinematically to C‧ shear bands. It is unlikely that the slip systems that control intracrystalline deformation are important in CPO formation. We interpret that subgrain rotation recrystallization lead to grain size reduction and the elongate recrystallized grains were rotated towards the C‧ shear bands by grain boundary sliding. This rigid body rotation, possibly in combination with easy slip on (100) <001> are considered the main cause of CPO formation. Amphibole zonation patterns in the layered gabbro sample suggest that oriented growth of amphibole may have contributed to CPO.

The strength and ductility of polycrystalline NiAl in tension

NASA Technical Reports Server (NTRS)

Schulson, E. M.

1982-01-01

Experiments at temperatures from 20 C to 400 C at two strain rates (.0001/s and .000005/s) establish that: (1) at room temperatures, binary and microalloyed ( 1000 ppm La, Y, Mo, Ti) NiAl shows negligible ductility, independent of grain size over the range 5 to 140 micrometers; (2) at 295 C the tensile elongation of binary 51 Ni/49 Al increases from 1% to about 5% upon decreasing the grain size to below approximately 10 micrometers; (3) similarly, at 400 C the ductility increases from about 2% to 15% upon decreasing the grain size to below 15 micrometers; (4) the ductility of fine grained (7 micrometer) binary aggregates deformed at 295 C increases from approximately 5% to 12% upon decreasing the strain rate from .0001/s to .000005/s; (5) partial recrystallization (10% to 20%) of warm extruded binary and microalloyed material imparts 1% to 2% ductility at room temperature where fully recrystallized material is brittle; (6) the yield strength obeys a Hall-Petch relationship; and (7) when ductility is not observed, fracture coincides with yielding. The mechanisms underlying the flow and fracture of NiAl are discussed in terms of the nucleation and growth of microcracks. The concept of a critical grain size is considered in the light of the results.

Relationship of Technological Properties with Dynamic Recrystallization of Quartz on the Example of Objects of the Karelian-Kola Region

NASA Astrophysics Data System (ADS)

Skamnitskaya, Lubov; Rakov, Leonid; Bubnova, Tatyana; Shchiptsov, Vladimir

2017-12-01

Despite the significant reserves of quartz raw materials, there is a deficit of high purity quartz. It is due to the strict technical requirements imposed by standards for this type of raw materials and technological properties of quartz, which are determined by the features of the crystal structure. The crystalline structure is of particular importance for the technological properties of quartz, since such important characteristics as the limit of raw material enrichment, dissolution rate in acid, melting point of quartz, etc., are determined. The formation of the crystal structure of quartz under natural conditions is associated with the successive dynamic recrystallization of the mineral. The degree of dynamic recrystallization of quartz reflects the distribution of dispersed impurities. If it is weakly manifested, the dispersed impurities are not displaced from one zone to another, and all quartz microblocks contain approximately the same concentration. In this case, more or less uniform dissolution of various regions of quartz is observed, and the pattern of distribution of submicroscopic inhomogeneities is monotonic. If intensive dynamic recrystallization of quartz takes place, then it causes a significant redistribution of the scattered impurities. Then the treatment in HF leads to the appearance of a contrast pattern of the distribution of submicroscopic inhomogeneities. The details of the crystal structure of quartz in this work were investigated by the electron paramagnetic resonance (EPR) method using the ER-420 “Bruker” spectrometer. In the selected samples of quartz, the concentrations of isomorphic impurities Al and Ti were measured, and the degree of crystallinity D of the mineral was estimated from the EPR spectra of each of them. Thus, the technological properties of quartz are determined by various geological processes. The results of the studies show that when evaluating the prospects of quartz raw materials, it is necessary to take into account the staged dynamic dynamical recrystallization of quartz in natural conditions. This factor can play both a positive and a negative role at various stages of mineral formation. Its influence is reflected in the state of the crystal structure of quartz, which should be taken into account when developing effective technologies for its enrichment. The intermediate stage of dynamic recrystallization corresponding to the end of the second stage-the beginning of the third stage of quartz recrystallization-is optimal for the formation of high-purity quartz. When choosing a site for the first-stage quartz mining at large deposits in the Karelian-Kola region, one should be guided by the stage of dynamic recrystallization.

Diffusion-Controlled Recrystallization of Water Sorbed into Poly(meth)acrylates Revealed by Variable-Temperature Mid-Infrared Spectroscopy and Molecular Dynamics Simulation.

PubMed

Yasoshima, Nobuhiro; Fukuoka, Mizuki; Kitano, Hiromi; Kagaya, Shigehiro; Ishiyama, Tatsuya; Gemmei-Ide, Makoto

2017-05-18

Recrystallization behaviors of water sorbed into four poly(meth)acrylates, poly(2-methoxyethyl acrylate), poly(tetrahydrofurfuryl acrylate), poly(methyl acrylate), and poly(methyl methacrylate), are investigated by variable-temperature mid-infrared (VT-MIR) spectroscopy and molecular dynamics (MD) simulation. VT-MIR spectra demonstrate that recrystallization temperatures of water sorbed into the polymers are positively correlated with their glass-transition temperatures reported previously. The present MD simulation shows that a lower-limit temperature of the diffusion for the sorbed water and the glass-transition temperatures of the polymers also have a positive correlation, indicating that the recrystallization is controlled by diffusion mechanism rather than reorientation mechanism. Detailed molecular processes of not only recrystallization during rewarming but also crystallization during cooling and hydrogen-bonding states of water in the polymers are systematically analyzed and discussed.

Microstructure, strengthening mechanisms and hot deformation behavior of an oxide-dispersion strengthened UFG Al6063 alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Asgharzadeh, H.; Kim, H.S.; Simchi, A., E-mail: simchi@sharif.edu

2013-01-15

An ultrafine-grained Al6063/Al{sub 2}O{sub 3} (0.8 vol.%, 25 nm) nanocomposite was prepared via powder metallurgy route through reactive mechanical alloying and hot powder extrusion. Scanning electron microcopy, transmission electron microscopy, and back scattered electron diffraction analysis showed that the grain structure of the nanocomposite is trimodal and composed of nano-size grains (< 0.1 {mu}m), ultrafine grains (0.1-1 {mu}m), and micron-size grains (> 1 {mu}m) with random orientations. Evaluation of the mechanical properties of the nanocomposite based on the strengthening-mechanism models revealed that the yield strength of the ultrafine-grained nanocomposite is mainly controlled by the high-angle grain boundaries rather than nanometricmore » alumina particles. Hot deformation behavior of the material at different temperatures and strain rates was studied by compression test and compared to coarse-grained Al6063 alloy. The activation energy of the hot deformation process for the nanocomposite was determined to be 291 kJ mol{sup -1}, which is about 64% higher than that of the coarse-grained alloy. Detailed microstructural analysis revealed that dynamic recrystallization is responsible for the observed deformation softening in the ultrafine-grained nanocomposite. - Highlights: Black-Right-Pointing-Pointer The strengthening mechanisms of Al6063/Al{sub 2}O{sub 3} nanocomposite were evaluated. Black-Right-Pointing-Pointer Hot deformation behavior of the nanocomposite was studied. Black-Right-Pointing-Pointer The hot deformation activation energy was determined using consecutive models. Black-Right-Pointing-Pointer The restoration mechanisms and microstructural changes are presented.« less

Creep of quartz by dislocation and grain boundary processes

NASA Astrophysics Data System (ADS)

Fukuda, J. I.; Holyoke, C. W., III; Kronenberg, A. K.

2015-12-01

Wet polycrystalline quartz aggregates deformed at temperatures T of 600°-900°C and strain rates of 10-4-10-6 s-1 at a confining pressure Pc of 1.5 GPa exhibit plasticity at low T, governed by dislocation glide and limited recovery, and grain size-sensitive creep at high T, governed by diffusion and sliding at grain boundaries. Quartz aggregates were HIP-synthesized, subjecting natural milky quartz powder to T=900°C and Pc=1.5 GPa, and grain sizes (2 to 25 mm) were varied by annealing at these conditions for up to 10 days. Infrared absorption spectra exhibit a broad OH band at 3400 cm-1 due to molecular water inclusions with a calculated OH content (~4000 ppm, H/106Si) that is unchanged by deformation. Rate-stepping experiments reveal different stress-strain rate functions at different temperatures and grain sizes, which correspond to differing stress-temperature sensitivities. At 600-700°C and grain sizes of 5-10 mm, flow law parameters compare favorably with those for basal plasticity and dislocation creep of wet quartzites (effective stress exponents n of 3 to 6 and activation enthalpy H* ~150 kJ/mol). Deformed samples show undulatory extinction, limited recrystallization, and c-axis maxima parallel to the shortening direction. Similarly fine-grained samples deformed at 800°-900°C exhibit flow parameters n=1.3-2.0 and H*=135-200 kJ/mol corresponding to grain size-sensitive Newtonian creep. Deformed samples show some undulatory extinction and grain sizes change by recrystallization; however, grain boundary deformation processes are indicated by the low value of n. Our experimental results for grain size-sensitive creep can be compared with models of grain boundary diffusion and grain boundary sliding using measured rates of silicon grain boundary diffusion. While many quartz mylonites show microstructural and textural evidence for dislocation creep, results for grain size-sensitive creep may apply to very fine-grained (<10 mm) quartz mylonites.

Chemical signature of a migrating grain boundaries in polycrystalline olivine

NASA Astrophysics Data System (ADS)

Boneh, Y.; Marquardt, K.; Skemer, P. A.

2017-12-01

Olivine is the most abundant phase and influences strongly the physical and chemical properties of the upper mantle. The structure and chemistry of olivine grain-boundaries is important to understand, as these interfaces provide a reservoir for incompatible elements and partial melt, and serve as a fast pathway for chemical diffusion. This project investigates the chemical characteristics of grain boundaries in an olivine-rich aggregate. The sample is composed of Fo50 olivine crystals with minor amounts of enstatite. It was previously deformed (Hansen et al., 2016) and then annealed (Boneh et al., 2017) to investigate the microstructural changes during recrystallization. This transient microstructure has a bimodal grain size distribution and includes grains that experienced abnormal grain-growth, (porphyroblasts) and highly strained grains with no significant recrystallization or growth (matrix). Using high-resolution transmission electron microscopy (HR-TEM) with energy dispersive X-ray (EDX) at the Bayerisches Geoinstitut (BGI), we characterized boundaries between pairs of porphyroblasts, pairs of matrix grains, and mixed boundaries between porphyroblast and matrix grains. It was found that the boundary between porphyroblasts is enriched in Al and Ca and depleted in Mg, in comparison to grain interiors. However, matrix-matrix boundaries show less chemical segregation of these elements. The relatively high level of chemical segregation to porphyroblast grain boundaries offers different possible interpretations: 1) During grain boundary migration incompatible elements are swept up by the migrating grain boundary. 2) Large angle grain boundaries provide a large density of energetically favorable storage sites for incompatible elements. 3) Diffusion along low angle grain boundaries is too slow to allow for fast chemical equilibration between the different grain boundaries. 4) Dislocations cores serve as an important transport media for impurities (i.e., Cottrell atmosphere). We will further discuss these different interpretations, their feasibility, and implications for the geochemistry of the mantle.

Preliminary 3D In-situ measurements of the texture evolution of strained H2O ice during annealing using neutron Laue diffractometry

NASA Astrophysics Data System (ADS)

Journaux, Baptiste; Montagnat, Maurine; Chauve, Thomas; Ouladdiaf, Bachir; Allibon, John

2015-04-01

Dynamic recrystallization (DRX) strongly affects the evolution of microstructure (grain size and shape) and texture (crystal preferred orientation) in materials during deformation at high temperature. Since texturing leads to anisotropic physical properties, predicting the effect of DRX is essential for industrial applications, for interpreting geophysical data and modeling geodynamic flows, and predicting ice sheet flow and climate evolution. A large amount of literature is available related to metallurgy, geology or glaciology, but there remains overall fundamental questions about the relationship between nucleation, grain boundary migration and texture development at the microscopic scale. Previous measurements of DRX in ice were either conducted using 2D ex-situ techniques such as AITA [1,2] or Electron Backscattering Diffraction (EBSD) [3], or using 3D statistical ex-situ [4] or in-situ [5] techniques. Nevertheless, all these techniques failed to observe at the scale of nucleation processes during DRX in full 3D. Here we present a new approach using neutron Laue diffraction, which enable to perform 3D measurements of in-situ texture evolution of strained polycrystalline H2O ice (>2% at 266 K) during annealing at the microscopic scale. Thanks the CYCLOPS instrument [6] (Institut Laue Langevin Grenoble, France) and the intrinsic low background of this setup, preliminary observations enabled us to follow, in H2O ice, the evolution of serrated grain boundaries, and kink-band during annealing. Our observations show a significant evolution of the texture and internal misorientation over the course of few hours at an annealing temperature of 268.5 K. In the contrary, ice kink-band structures seem to be very stable over time at near melting temperatures. The same samples have been analyzed ex-situ using EBSD for comparison. These results represent a first step toward in-situ microscopic measurements of dynamic recrystallization processes in ice during strain. This experiment has been conducted in the frame of the ANR-funded DREAM project that focuses on the recrystallization processes in anisotropic materials. References [1] D. S. Russell-Head and C.J.L. Wilson., 2001, Journal of Glaciology, 24, 117-130. [2] Wilson, C.J.L., Peternell, M., Piazolo, S., Luzin, V., 2014, Journal of Structural Geology, Microdynamics of Ice, 61, 50-77. [3] M. Montagnat, T. Chauve, F. Barou, A. Tommasi, B. Beausir, C. Fressengeas., in prep. [4] T. H. Jacka and J. Li., 2000, In T. Hondoh, editor, Physics of Ice Core Records, pages 83-102. Hokkaido University Press, Sapporo. [5] S. Piazolo, C. J. L. Wilson, V. Luzin, C. Brouzet, and M. Peternell., 2013, Geochemistry, Geophysics, Geosystems, 14, 4185-4194. [6] B. Ouladdiaf et al., 2011, Journal of Applied Crystallography, 44, 392-397.

Effect of starting microstructure on helium plasma-materials interaction in tungsten

DOE PAGES

Wang, Kun; Bannister, Mark E.; Meyer, Fred W.; ...

2016-11-24

Here, in a magnetic fusion energy (MFE) device, the plasma-facing materials (PFMs) will be subjected to tremendous fluxes of ions, heat, and neutrons. The response of PFMs to the fusion environment is still not well defined. Tungsten metal is the present candidate of choice for PFM applications such as the divertor in ITER. However, tungsten's microstructure will evolve in service, possibly to include recrystallization. How tungsten's response to plasma exposure evolves with changes in microstructure is presently unknown. In this work, we have exposed hot-worked and recrystallized tungsten to an 80 eV helium ion beam at a temperature of 900more » °C to fluences of 2 × 10 23 or 20 × 10 23 He/m 2. This resulted in a faceted surface structure at the lower fluence or short but well-developed nanofuzz structure at the higher fluence. There was little difference in the hot-rolled or recrystallized material's near-surface (≤50 nm) bubbles at either fluence. At higher fluence and deeper depth, the bubble populations of the hot-rolled and recrystallized were different, the recrystallized being larger and deeper. This may explain previous high-fluence results showing pronounced differences in recrystallized material. The deeper penetration in recrystallized material also implies that grain boundaries are traps, rather than high-diffusivity paths.« less

Relating rheology to geometry in large-scale natural shear zones

NASA Astrophysics Data System (ADS)

Platt, John

2016-04-01

The geometry and width of the ductile roots of plate boundary scale faults are very poorly understood. Some field and geophysical data suggests widths of tens of km in the lower crust, possibly more in the upper mantle. Other observations suggest they are much narrower. Dip slip shear zones may flatten out and merge into zones of subhorizontal lower crustal or asthenospheric flow. The width of a ductile shear zone is simply related to relative velocity and strain rate. Strain rate is related to stress through the constitutive relationship. Can we constrain the stress, and do we understand the rheology of materials in ductile shear zones? A lot depends on how shear zones are initiated. If they are localized by pre-existing structures, width and/or rheology may be inherited, and we have too many variables. If shear zones are localized primarily by shear heating, initial shear stress has to be very high (> 1 GPa) to overcome conductive heat loss, and very large feedbacks (both positive and negative) make the system highly unstable. Microstructural weakening requires a minimum level of stress to cause deformation and damage in surrounding rock, thereby buffering the stress. Microstructural weakening leads to grain-size sensitive creep, for which we have constitutive laws, but these are complicated by phase mixing in polyphase materials, by viscous anisotropy, by hydration, and by changes in mineral assemblage. Here are some questions that need to be addressed. (1) If grain-size reduction by dynamic recrystallization results in a switch to grain-size sensitive creep (GSSC) in a stress-buffered shear zone, does dynamic recrystallization stop? Does grain growth set in? If grain-size is still controlled by dislocation processes, then the effective stress exponent for GSSC is 4-5, even though the dominant mechanism may be diffusion and/or grain-boundary sliding (GBS). (2) Is phase mixing in ultramylonites primarily a result of GBS + neighbour switching, creep cavitation and diffusion, or metamorphic reactions? (3) In two-phase / polyphase mixtures, does the strong phase generally form a load-bearing framework, favoring constant strain-rate (Voigt) bound behavior, or does the weak phase form through-going strain pathways, favoring constant stress (Reuss) bound behavior, or do the phases remain well mixed, favoring an intermediate behavior (e.g., Tullis et al model)? (4) How do we deal with the rheological effect of water? Is it simply an unconstrained variable in nature? Is the water fugacity model in flow laws adequate? (5) How can we better relate experimental results (often carried out at constant strain-rate, and not reaching microstructural steady state) to deformation in natural shear zones? Rheological observations on well-constrained natural shear zones are helping us answer some of these questions.

The Effect of Heat Treatment on the Sensitized Corrosion of the 5383-H116 Al-Mg Alloy

PubMed Central

Lin, Ying-Kai; Wang, Shing-Hai; Chen, Ren-Yu; Hsieh, Tso-Sheng; Tsai, Liren; Chiang, Chia-Chin

2017-01-01

In this study, the effects of heat treatment and sensitized corrosion on the 5383-H116 Al-Mg alloy were investigated for temperatures ranging from 100 to 450 °C. The results show that the heat treatment temperature is the main factor that causes changes to the microstructure and mechanical strength of the 5383-H116 Al-Mg alloy, inducing β-phase (Al3Mg2) precipitation in the form of a continuous layer along the grain boundaries. Intergranular corrosion was caused by the β-phase of the grain boundary precipitation, and the corrosion susceptibility of the recrystallized structure was significantly higher than the corrosion susceptibility of the recovered structure. According to the conductivity values detected, β-phase precipitation can enhance the 5383-H116 Al-Mg alloy conductivity, with the response due to structural dislocation density being higher than that due to the recrystallized structure. As such, the β-phase precipitation after sensitization is more significant than the β-phase precipitation prior to the sensitization, such that after sensitization, the conductivity rises to a significantly higher level than that exhibited by the recrystallization structure. PMID:28772635

High-capacity ice-recrystallization endpoint assay employing superhydrophobic coatings that is equivalent to the 'splat' assay.

PubMed

Graham, Laurie A; Agrawal, Prashant; Oleschuk, Richard D; Davies, Peter L

2018-04-01

We have developed an ice recrystallization inhibition (IRI) assay system that allows the side-by-side comparison of up to a dozen samples treated in an identical manner. This system is ideal for determining, by serial dilution, the IRI 'endpoint' where the concentration of a sample is reached that can no longer inhibit recrystallization. Samples can be an order of magnitude smaller in volume (<1 μL) than those used for the conventional 'splat' assay. The samples are pipetted into wells cut out of a superhydrophobic coating on sapphire slides that are covered with a second slide and then snap-frozen in liquid nitrogen. Sapphire is greatly superior to glass in its ability to cool quickly without cracking. As a consequence, the samples freeze evenly as a multi-crystalline mass. The ice grain size is slightly larger than that obtained by the 'splat' assay but can be followed sufficiently well to assess IRI activity by changes in mean grain boundary size. The slides can be washed in detergent and reused with no carryover of IRI activity even from the highest protein concentrations. Copyright © 2018 Elsevier Inc. All rights reserved.

Paleozoic-Mesozoic boundary in the Berry Creek Quadrangle, northwestern Sierra Nevada, California

USGS Publications Warehouse

Hietanen, Anna Martta

1977-01-01

Structural and petrologic studies in the Berry Creek quadrangle at the north end of the western metamorphic belt of the Sierra Nevada have yielded new information that helps in distinguishing between the chemically similar Paleozoic and Mesozoic rocks. The distinguishing features are structural and textural and result from different degrees of deformation. Most Paleozoic rocks are strongly deformed and thoroughly recrystallized. Phenocrysts in meta volcanic rocks are granulated and drawn out into lenses that have sutured outlines. In contrast, the phenocrysts in the Mesozoic metavolcanic rocks show well-preserved straight crystal faces, are only slightly or not at all granulated, and contain fewer mineral inclusions than do those in the Paleozoic rocks. The groundmass in the Paleozoic rocks is recrystallized to a fairly coarse grained albite-epidote-amphibole-chlorite rock, whereas in the Mesozoic rocks the groundmass is a very fine grained feltlike mesh with only spotty occurrence of well-recrystallized finegrained albite-epidote-chlorite-actinolite rock. Primary minerals, such as augite, are locally preserved in the Mesozoic rocks but are altered to a mixture of amphibole, chlorite, and epidote in the Paleozoic rocks. In the contact aureoles of the plutons, and within the Big Bend fault zone, which crosses the area parallel to the structural trends, all rocks are thoroughly recrystallized and strongly deformed. Identification of the Paleozoic and Mesozoic rocks in these parts of the area was based on the continuity of the rock units in the field and on gradual changes in microscopic textures toward the plutons.

Oxide-dispersion strengthening of porous powder metalurgy parts

DOEpatents

Judkins, Roddie R.

2002-01-01

Oxide dispersion strengthening of porous metal articles includes the incorporation of dispersoids of metallic oxides in elemental metal powder particles. Porous metal articles, such as filters, are fabricated using conventional techniques (extrusion, casting, isostatic pressing, etc.) of forming followed by sintering and heat treatments that induce recrystallization and grain growth within powder grains and across the sintered grain contact points. The result is so-called "oxide dispersion strengthening" which imparts, especially, large increases in creep (deformation under constant load) strength to the metal articles.

Effect of the Size of Al3(Sc,Zr) Precipitates on the Structure of Multi-Directionally Isothermally Forged Al-Mg-Sc-Zr Alloy

NASA Astrophysics Data System (ADS)

Sitdikov, O. Sh.; Avtokratova, E. V.; Mukhametdinova, O. E.; Garipova, R. N.; Markushev, M. V.

2017-12-01

The effect of Al3(Sc,Zr) dispersoids on the evolution of the cast Al-Mg-Sc-Zr alloy structure under multi-directional isothermal forging (MIF) has been investigated. The alloy, which has an equiaxed grain structure with a grain size of 25 μm and contains dispersoids 5-10 and 20-50 nm in size after onestage (at 360°C for 6 h) and two-stage (360°C for 6 h + 520°C for 1 h) annealing, respectively, was deformed at 325°C ( 0.65 T m) up to cumulative strains of e = 8.4. In the initial stages of MIF, new fine (sub)grains surrounded by low-angle and high-angle boundaries (HABs) were formed near the initial grain boundaries. With increasing strain, the volume fraction and misorientation of these crystallites increased, which led to the replacement of a coarse-grained structure with a fine-grained one with a grain size of 1.5-2.0 μm. Dynamic recrystallization occurred in accordance to a continuous mechanism and was controlled by the interaction of lattice dislocations and/or (sub)grain boundaries with dispersoids that effectively inhibited the migration of boundaries, as well as the rearrangement of lattice dislocations and their annihilation. The particle size and the density of their distribution significantly affected the parameters of the evolved structure; in an alloy with smaller particles, a structure with a smaller grain size and a larger HAB fraction developed.

Greenschist-Facies Pseudotachylytes and Gouge: a Microstructural Study of the Deformation Propagation at the Boundary Between Hp-Metabasite and Calcite Bearing Metasediments

NASA Astrophysics Data System (ADS)

Crispini, L.; Scambelluri, M.; Capponi, G.

2013-12-01

Recent friction experiments on calcite-bearing systems reproduce pseudotachylyte structures, that are diagnostic of dinamic calcite recrystallization related to seismic slip in the shallow crust. Here we provide the study of a pseudotachylyte (PT) bearing low angle oblique-slip fault. The fault is linked to the exhumation of Alpine HP-ophiolites and it is syn- to post-metamorphic with respect to retrograde greenschist facies metamorphism. The observed microstructures developed at the brittle-ductile transition and suggest that seismic and interseismic slip was enhanced by interaction with fluids. The fault zone is in-between high-pressure eclogite-facies metabasites (hangingwall) and calcite bearing metasediments (footwall). The mafic rocks largely consist of upper greenschist facies hornblende, albite, chlorite, epidote with relict eclogitic garnet, Na-pyroxene and rutile; metasediments correspond to calcschist and micaschist with quartz, phengite, zoisite, chlorite, calcite and relics of garnet. Key features of the oucrop are: the thickness and geometry of the PT and gouge; the multiple production of PT characterized by overprinting plastic and brittle deformation; the occurrence in footwall metasediments of mm-thick bands of finely recrystallized calcite coeval with PT development in the hangingwall. The damage zone is ca. 2 m-thick and is characterized by two black, ultra-finegrained straight and sharp Principal Slip Zones (PSZ) marked by PT. The damage zone shows a variety of fault rocks (cataclasite and ultracataclasite, gouge and PT) with multiple crosscutting relationships. Within the two main PSZ, PT occurs in 10-20 cm thick layer, in small scale injection veins and in microfractures. In the mafic hanging wall, the PT is recrystallized and does not preserve glass: it shows flow structures with subrounded, embayed and rebsorbed quartz in a fine grained matrix composed of isotropic albite + chlorite + quartz + epidote + titanite, suggesting recrystallization at ca. 270-300°C, 8-10 km of the original glass. PT show plastic deformations overprinted by shear bands and fracturing. The matrix of cataclastic layers has the same mineral assemblage as PT and clasts of recrystallised PT, to indicate polyphase PSZ formation. In the metasedimentary footwall, the original foliation is deflected parallel to the PSZ and is cut by cm-spaced shear bands parallel to PSZ. Deformation propagates in the footwall through mm-thick injections veins, shear bans, P-shears and veins. Pockets of recrystallized PT occur along the pre-existing mylonitic foliation of metasediments. Worthnote is the presence of mm-thick deformation bands (CDB) that are post-mylonitic foliation and mainly composed of fine grained calcite bounded by dissolution seams or ribbon grains of deformed calcite. CDB are characterised by subrounded embayed and rebsorbed quartz grains rimmed by new Ca-Mg amphibole, K-feldspar (90-93%K), in a dinamic recrystallized calcite 2-10 micron in size and slightly elongated. The features of the CDB suggest that these structures can be considered as diagnostic of localised deformation during coesismic slip in metasedimentary rocks.

Computational study of deformation mechanisms and grain size evolution in granulites - Implications for the rheology of the lower crust

NASA Astrophysics Data System (ADS)

Maierová, Petra; Lexa, Ondrej; Jeřábek, Petr; Schulmann, Karel; Franěk, Jan

2017-05-01

Most of granulite terrains worldwide are characterized by large mean grain sizes of 1 mm or more. An important exception are the high-pressure felsic granulites in the Bohemian Massif, the European Variscan belt. There, recrystallization of original coarse-grained ternary feldspar led to formation of a fine-grained (∼100 μm) mixed matrix dominated by plagioclase and K-feldspar. This change occurred at temperatures of ∼850 °C and was probably caused by chemically induced decomposition related to slight cooling and enhanced by deformation during continental collision. The resulting microstructure shows indications of diffusion creep assisted by melt-enhanced grain-boundary sliding. Further on, minor coarsening occurred associated with deformation by dislocation creep and aggregation of mineral phases. Using a thermodynamics-based model of grain size evolution we show that stability of the fine-grained microstructure crucially depends on Zener pinning in the two-phase mineral matrix. Pinning efficiently hinders grain growth, and the small grain size that resulted from the ternary feldspar decomposition can be stable even at high temperatures. The late switch from the grain-size-sensitive creep to dislocation creep is rather difficult to explain by temperature and strain rate (or stress) changes only. However, a simple incorporation of melt solidification can successfully simulate this behavior. Alternatively, the switch and the associated grain size growth can be related to mineral phase aggregation at lower pressure-temperature conditions resulting into a decrease of pinning efficiency. This study suggests that the fine grain size of the Bohemian granulites, in contrast to the common coarse-grained type, stems from abrupt recrystallization during the high-pressure high-temperature conditions, and pinning in the fine-grained matrix. Such a process may in some cases significantly and suddenly reduce the strength of the lower continental crust and allow for its efficient redistribution.

Microstructural Damage During High-Strain Torsion Experiments on Calcite-Anhydrite Aggregates

NASA Astrophysics Data System (ADS)

Cross, A. J.; Skemer, P. A.

2016-12-01

Ductile shear zones play a critical role in localising deformation in the Earth's crust and mantle. Severe grain size reduction - a ubiquitous feature of natural mylonites - is commonly thought to cause strain weakening via a transition to grain size sensitive deformation mechanisms. Although grain size reduction is modulated by grain growth in single-phase aggregates, grain boundary pinning in well-mixed poly-phase composites can inhibit grain growth, leading to microstructural `damage' which is likely a critical element of strain localization in the lithosphere. While dynamic recrystallization has been widely explored in rock mechanics and materials science, the mechanisms behind phase-mixing remain poorly understood. In this contribution we present results from high-strain, deformation experiments on calcite-anhydrite composites. Experiments were conducted in torsion at T = 500-700°C and P 1.5 GPa, using the new Large Volume Torsion (LVT) solid-medium apparatus, to shear strains of 0.5-30. As shear strain increases, progressive thinning and necking of initially large (≤ 1 mm) calcite domains is observed, resulting in an increase in the proportion of interphase boundaries. Grain-size is negatively correlated with the fraction of interphase boundaries, such that calcite grains in well-mixed regions are significantly smaller than those in single-phase domains. Crucially, progressive deformation leads to a reduction in grain-size beyond the lower limit established by the grain size piezometer for mono-phase calcite, implying microstructural damage. These data therefore demonstrate continued microstructural evolution in two-phase composites that is not possible in single-phase aggregates. These observations mark a new `geometric' mechanism for phase mixing, complementing previous models for phase mixing involving chemical reactions, material diffusion, and/or grain boundary sliding.

The Influence of Grain Boundary Fluids on the Recrystallization Behavior in Calcite: A Comparison of "dry" and "wet" Marble Mylonites

NASA Astrophysics Data System (ADS)

Schenk, O.; Urai, J.; Evans, B.

2003-12-01

Carbonate rocks are able to accumulate large amounts of strain and deform crystal-plastically even at low p-T conditions and thus, marble sequences are often the site of strain localization in the upper crust during late-stage deformation in mountain building processes. In this study we sought to identify the effect of fluids on grain boundary morphology and recrystallization processes in marble mylonites during shear zone evolution, as fluids play a major role in the flow behavior of many rock materials during deformation (e.g. quartz, olivine, halite, feldspar). We compared calcite marble mylonites from two geological settings: (a) Schneeberg Complex, Southern Tyrole, Italy and (b) Naxos Metamorphic Core Complex, Greece. The shear zones of the selected areas are suitable for comparison, because they consist of similar lithology and the marble mylonites resemble each other in chemical composition. In addition, calcite-dolomite solvus geothermometry and TEM observations indicate similar p-T conditions for the shear zones formation. However, the two settings are different in the availability of fluids during the shear zone evolution: In the Schneeberg mylonites, both the alteration of minerals during retrograde metamorphism of neighboring micaschists and the existence of veins suggest that fluids were present during mylonitization. The absence of these features in the Naxos samples indicates that fluids were not present during deformation of these mylonites. This difference is also supported by the signature of stable isotopes. Microstructural investigations using optical and scanning electron microscopes on broken and planar surfaces did not indicate major differences between wet and dry mylonites: Grain boundaries of both types of samples display pores with shapes controlled by crystallography, and pore morphologies that are similar to observations from crack and grain-boundary healing experiments. Grain size reduction was predominantly the result of subgrain rotation recrystallization. However, the coarse grains inside the wet protomylonites (Schneeberg) are characterized by intracrystalline shear zones. With the exception of the intracrystalline shear zones, there were no obvious microstructural signatures that were obvious indicators of the presence of fluids, at least for these two field examples.

Effect of Thermomechanical Processing on Texture and Superelasticity in Fe-Ni-Co-Al-Ti-B Alloy

NASA Astrophysics Data System (ADS)

Lee, Doyup; Omori, Toshihiro; Han, Kwangsik; Hayakawa, Yasuyuki; Kainuma, Ryosuke

2018-03-01

The texture and superelasticity were investigated in austenitic Fe-Ni-Co-Al-Ti-B alloy with various reduction ratios of cold rolling and heating ratios in annealing. The rolled sheets show the {110} <112> deformation texture at a reduction ratio higher than 80%, while the texture hardly changes in the primary recrystallization at 1000 °C. The β (B2) precipitates inhibit the grain growth at this temperature, but they dissolve during heating, and secondary recrystallization occurs due to decreased pinning force at temperatures higher than 1100 °C, resulting in texture change to {210} <001> . The recrystallization texture is more strongly developed when the reduction ratio and heating rate are high and slow, respectively. The 90% cold-rolled and slowly heated sheet shows the recrystallization texture and high fraction of low-angle boundaries. As a result, ductility and superelasticity can be drastically improved in the 90% cold-rolled sheet, although superelasticity was previously obtained only in thin sheets with 98.5% reduction.

Experiments and modeling to characterize microstructure and hardness in 304L

DOE PAGES

Deibler, Lisa Anne; Brown, Arthur; Puskar, Joseph D.

2017-01-12

Drawn 304L stainless steel tubing was subjected to 42 different annealing heat treatments with the goal of initializing a microstructural model to select a heat treatment to soften the tubing from a hardness of 305 Knoop to 225–275 Knoop. The amount of recrystallization and grain size caused by 18 heat treatments were analyzed via optical microscopy and image analysis, revealing the full range of recrystallization from 0 to 100%. The formation of carbides during the longer duration and higher-temperature heat treatments was monitored via transmission electron microscope evaluation. The experimental results informed a model which includes recovery, recrystallization, and grainmore » growth to predict microstructure and hardness. After initialization of the model, it was able to predict hardness with a R 2 value of 0.95 and recrystallization with an R 2 value of 0.99. As a result, the model was then utilized in the design and testing of a heat treatment to soften the tubing.« less

Etude de la texture des rubans EPR de silicium polycristallin photovoltaïque

NASA Astrophysics Data System (ADS)

Chibani, A.; Gauthier, R.; Pinard, P.; Andonov, P.

1991-09-01

EPR polysilicon ribbons are obtained from a 5N-6N purity grade silicon powder melting followed by a recrystallization step. Being assigned to the photocell manufacture, we study the texture by X-ray diffraction method to reveal the majority of the crystal orientations and prove the eventual existence of specific orientations adapted to the best photovoltaic conversion efficiencies such as (100), (110) or (111). Moreover, we tested the possibility to induce the (111) orientation with a monocrystalline seed having this orientation. It appears that the crystal growth is essentially anisotropic and that only the orientation of the grains with their (331) planes parallel to the ribbon surface may be considered as dominant after the recrystallization step; finally, the (111) starting seed has an effect only at the recrystallization onset.

Effect of Annealing on Microstructure and Tensile Properties of 5052/AZ31/5052 Clad Sheets

NASA Astrophysics Data System (ADS)

Nie, Huihui; Liang, Wei; Chi, Chengzhong; Li, Xianrong; Fan, Haiwei; Yang, Fuqian

2016-05-01

Three-layered 5052Al/AZ31Mg/5052Al (5052/AZ31/5052) clad sheets were fabricated by four-pass rolling and annealed under different conditions. Under the optimal annealing condition, homogeneous and equiaxial grains with an average AZ31 grain size of 5.24 µm were obtained and the maximum values of ultimate tensile strength and elongation of the clad sheet reached 230 MPa and 18%, respectively. Electron backscatter diffraction analysis showed that the AZ31 layer had a typical rolling texture with its c-axis parallel to the normal direction. The fraction of low-angle grain boundaries in the 5052 layer was nearly four times more than that in the AZ31 layer because of different deformation extent and recrystallization driving forces. The textures of Al3Mg2 and Mg17Al12 were similar to that of 5052 because of the deformation coordination during the rolling and recrystallization process. The orientation relationship between Mg17Al12 and AZ31 seemed to be (110) Mg17Al12//(10-11) AZ31.

Manufacturing process to reduce large grain growth in zirconium alloys

DOEpatents

Rosecrans, P.M.

1984-08-01

It is an object of the present invention to provide a procedure for desensitizing zirconium-based alloys to large grain growth (LGG) during thermal treatment above the recrystallization temperature of the alloy. It is a further object of the present invention to provide a method for treating zirconium-based alloys which have been cold-worked in the range of 2 to 8% strain to reduce large grain growth. It is another object of the present invention to provide a method for fabricating a zirconium alloy clad nuclear fuel element wherein the zirconium clad is resistant to large grain growth.

Dynamic moisture sorption characteristics of enzyme-resistant recrystallized cassava starch.

PubMed

Mutungi, Christopher; Schuldt, Stefan; Onyango, Calvin; Schneider, Yvonne; Jaros, Doris; Rohm, Harald

2011-03-14

The interaction of moisture with enzyme-resistant recrystallized starch, prepared by heat-moisture treatment of debranched acid-modified or debranched non-acid-modified cassava starch, was investigated in comparison with the native granules. Crystallinities of the powdered products were estimated by X-ray diffraction. Moisture sorption was determined using dynamic vapor sorption analyzer and data fitted to various models. Percent crystallinities of native starch (NS), non-acid-modified recrystallized starch (NAMRS), and acid-modified recrystallized starch (AMRS) were 39.7, 51.9, and 56.1%, respectively. In a(w) below 0.8, sorption decreased in the order NS > NAMRS > AMRS in line with increasing sample crystallinities but did not follow this crystallinity dependence at higher a(w) because of condensation and polymer dissolution effects. Adsorbed moisture became internally absorbed in NS but not in NAMRS and AMRS, which might explain the high resistance of the recrystallized starches to digestion because enzyme and starch cannot approach each other over fairly sufficient surface at the molecular level.

Microstructural characteristics of adiabatic shear localization in a metastable beta titanium alloy deformed at high strain rate and elevated temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhan, Hongyi, E-mail: h.zhan@uq.edu.au; Zeng, Weidong; Wang, Gui

2015-04-15

The microstructural evolution and grain refinement within adiabatic shear bands in the Ti6554 alloy deformed at high strain rates and elevated temperatures have been characterized using transmission electron microscopy. No stress drops were observed in the corresponding stress–strain curve, indicating that the initiation of adiabatic shear bands does not lead to the loss of load capacity for the Ti6554 alloy. The outer region of the shear bands mainly consists of cell structures bounded by dislocation clusters. Equiaxed subgrains in the core area of the shear band can be evolved from the subdivision of cell structures or reconstruction and transverse segmentationmore » of dislocation clusters. It is proposed that dislocation activity dominates the grain refinement process. The rotational recrystallization mechanism may operate as the kinetic requirements for it are fulfilled. The coexistence of different substructures across the shear bands implies that the microstructural evolution inside the shear bands is not homogeneous and different grain refinement mechanisms may operate simultaneously to refine the structure. - Graphical abstract: Display Omitted - Highlights: • The microstructure within the adiabatic shear band was characterized by TEM. • No stress drops were observed in the corresponding stress–strain curve. • Dislocation activity dominated the grain refinement process. • The kinetic requirements for rotational recrystallization mechanism were fulfilled. • Different grain refinement mechanisms operated simultaneously to refine the structure.« less

Early Cretaceous Ductile Deformation of Marbles from the Western Hills of Beijing, North China Craton

NASA Astrophysics Data System (ADS)

Feng, H.; Liu, J.

2017-12-01

During the Early Cretaceous tectonic lithosphere extension, the pre-mesozoic rocks from the Western Hills in the central part of the North China Craton suffered from weak metamorphism but intense shear deformation. The prominent features of the deformation structures are the coexisting layer-parallel shear zones and intrafolia folds, and the along-strike thickness variations of the marble layers from the highly sheared Mesoproterozoic Jing'eryu Formation. Platy marbles are well-developed in the thinner layers, while intrafolia folds are often observed in the thicker layers. Most folds are tight recumbent folds and their axial planes are parallel to the foliations and layerings of the marbles. The folds are A-type folds with hinges being always paralleling to the stretching lineations consistently oriented at 130°-310° directions throughout the entire area. SPO and microstructural analyses of the sheared marbles suggest that the thicker layers suffered from deformations homogeneously, while strain localization can be distinguished in the thinner layers. Calcite twin morphology and CPO analysis indicate that the deformation of marbles from both thinner and thicker layers happened at temperatures of 300 to 500°C. The above analysis suggests that marbles in the thicker layers experienced a progressive sequence of thermodynamic events: 1) regional metamorphism, 2) early ductile deformation dominated by relatively higher temperature conditions, during which all the mineral particles elongated and oriented limitedly and the calcite grains are deformed mainly by mechanical twinning, and 3) late superimposition of relatively lower temperature deformation and recrystallization, which superposed the early deformation, and made the calcites finely granulated, elongated and oriented by dynamical recrystallization along with other grains. Marbles from the thinner layers, however, experienced a similar, but different sequence of thermo-dynamic events, i.e. regional metamorphism, early ductile deformation and weak superimposition by subsequent deformation, which caused the development of the strain localization. It is also shown that the intensity of progressive superimposition deformation contributed to the thinning and thickening of the marble layers.

Finite element simulation of texture evolution and Swift effect in NiAl under torsion

NASA Astrophysics Data System (ADS)

Böhlke, Thomas; Glüge, Rainer; Klöden, Burghardt; Skrotzki, Werner; Bertram, Albrecht

2007-09-01

The texture evolution and the Swift effect in NiAl under torsion at 727 °C are studied by finite element simulations for two different initial textures. The material behaviour is modelled by an elastic-viscoplastic Taylor model. In order to overcome the well-known shortcomings of Taylor's approach, the texture evolution is also investigated by a representative volume element (RVE) with periodic boundary conditions and a compatible microstructure at the opposite faces of the RVE. Such a representative volume element takes into account the grain morphology and the grain interaction. The numerical results are compared with experimental data. It is shown that the modelling of a finite element based RVE leads to a better prediction of the final textures. However, the texture evolution path is not accounted for correctly. The simulated Swift effect depends much more on the initial orientation distribution than observed in experiment. Deviations between simulation and experiment may be due to continuous dynamic recrystallization.

Effects of hot compression deformation temperature on the microstructure and properties of Al-Zr-La alloys

NASA Astrophysics Data System (ADS)

Yue, Xian-hua; Liu, Chun-fang; Liu, Hui-hua; Xiao, Su-fen; Tang, Zheng-hua; Tang, Tian

2018-02-01

The main goal of this study is to investigate the microstructure and electrical properties of Al-Zr-La alloys under different hot compression deformation temperatures. In particular, a Gleeble 3500 thermal simulator was used to carry out multi-pass hot compression tests. For five-pass hot compression deformation, the last-pass deformation temperatures were 240, 260, 300, 340, 380, and 420°C, respectively, where the first-pass deformation temperature was 460°C. The experimental results indicated that increasing the hot compression deformation temperature with each pass resulted in improved electrical conductivity of the alloy. Consequently, the flow stress was reduced after deformation of the samples subjected to the same number of passes. In addition, the dislocation density gradually decreased and the grain size increased after hot compression deformation. Furthermore, the dynamic recrystallization behavior was effectively suppressed during the hot compression process because spherical Al3Zr precipitates pinned the dislocation movement effectively and prevented grain boundary sliding.

Formability of a wrought Mg alloy evaluated by impression testing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mohamed, Walid; Gollapudi, Srikant; Charit, Indrajit

This study is focused on furthering our understanding of the different factors that influence the formability of Magnesium alloys. Towards this end, formability studies were undertaken on a wrought Mg-2Zn-1Mn (ZM21) alloy. In contrast to conventional formability studies, the impression testing method was adopted here to evaluate the formability parameter, B, at temperatures ranging from 298 to 473 K. The variation of B of ZM21 with temperature and its rather limited values were discussed in the light of different deformation mechanisms such as activation of twinning, slip, grain boundary sliding (GBS) and dynamic recrystallization (DRX). It was found that themore » material characteristics such as grain size, texture and testing conditions such as temperature and strain rate, were key determinants of the mechanism of plastic deformation. A by-product of this analysis was the observation of an interesting correlation between the Zener-Hollomon parameter, Z, and the ability of Mg alloys to undergo DRX.« less

The effect of solute additions on the steady-state creep behavior of dispersion-strengthened aluminum.

NASA Technical Reports Server (NTRS)

Reynolds, G. H.; Lenel, F. V.; Ansell, G. S.

1971-01-01

The effect of solute additions on the steady-state creep behavior of coarse-grained dispersion-strengthened aluminum alloys was studied. Recrystallized dispersion-strengthened solid solutions were found to have stress and temperature sensitivities quite unlike those observed in single-phase solid solutions having the same composition and grain size. The addition of magnesium or copper to the matrix of a recrystallized dispersion-strengthened aluminum causes a decrease in the steady-state creep rate which is much smaller than that caused by similar amounts of solute in single-phase solid solutions. All alloys exhibited essentially a 4.0 power stress exponent in agreement with the model of Ansell and Weertman. The activation energy for steady-state creep in dispersion-strengthened Al-Mg alloys, as well as the stress dependence, was in agreement with the physical model of dislocation climb over the dispersed particles.

Monazite behaviours during high-temperature metamorphism: a case study from Dinggye region, Tibetan Himalaya

NASA Astrophysics Data System (ADS)

Wang, Jia-Min; Wu, Fu-Yuan; Rubatto, Daniela; Liu, Shi-Ran; Zhang, Jin-Jiang

2017-04-01

Monazite is a key accessory mineral for metamorphic geochronology, but its growth mechanisms during melt-bearing high-temperature metamorphism is not well understood. Therefore, the petrology, pressure-temperature and timing of metamorphism have been investigated in pelitic and psammitic granulites from the Greater Himalayan Crystalline Complex (GHC) in Dinggye, southern Tibet. These rocks underwent an isothermal decompression process from pressure conditions of >10 kbar to <5 kbar with constant temperatures of 750-830°C, and recorded three metamorphic stages of kyanite-grade (M1), sillimanite-grade (M2) and cordierite-spinel grade (M3). Monazite and zircon crystals were analyzed for ages by microbeam techniques either in mounts or thin sections. Ages were linked to specific conditions of mineral growth by comprehensive studies on zoning patterns, trace element signatures, index mineral inclusions (melt inclusions, sillimanite and K-feldspar) in dated domains and textural correlations with coexisting minerals. The results show that inherited domains (500-400 Ma) are common in monazite even at granulite-facies conditions. Few monazites formed at the M1-stage ( 30-29 Ma) and recorded heterogeneous Th, Y, and HREE compositions, which formed by recrystallization related to muscovite dehydration melting reaction. These monazite grains were protected from dissolution or lateral overprinting mainly by the armour effect of matrix crystals (biotite and quartz). Most monazite grains formed at the M3-stage (21-19 Ma) through either dissolution-reprecipitation or recrystallization that was related to biotite dehydration melting reaction. These monazite grains record HREE and Y signatures in local equilibrium with different reactions involving either garnet breakdown or peritectic garnet growth. Another peak of monazite growth occurs during melt crystallization ( 15 Ma), and these monazites are unzoned and have homogeneous compositions. Our results documented the widespread recrystallization to account for monazite growth during high-temperature metamorphism and related melting reactions that trigger monazite recrystallization. In a regional sense, our P-T-t data along with published data indicate that the pre-M1 eclogite-facies metamorphism occurred at 39-30 Ma in the Dinggye Himalaya. Our results are in favour of a steady exhumation of the GHC rocks since Oligocene that was contributed by partial melting. Key words: U-Th-Pb geochronology, Monazite, Recrystallization, Pelitic granulite, Himalaya

Analysing the strength of friction stir welded dissimilar aluminium alloys using Sugeno Fuzzy model

NASA Astrophysics Data System (ADS)

Barath, V. R.; Vaira Vignesh, R.; Padmanaban, R.

2018-02-01

Friction stir welding (FSW) is a promising solid state joining technique for aluminium alloys. In this study, FSW trials were conducted on two dissimilar plates of aluminium alloy AA2024 and AA7075 by varying the tool rotation speed (TRS) and welding speed (WS). Tensile strength (TS) of the joints were measured and a Sugeno - Fuzzy model was developed to interconnect the FSW process parameters with the tensile strength. From the developed model, it was observed that the optimum heat generation at WS of 15 mm.min-1 and TRS of 1050 rpm resulted in dynamic recovery and dynamic recrystallization of the material. This refined the grains in the FSW zone and resulted in peak tensile strength among the tested specimens. Crest parabolic trend was observed in tensile strength with variation of TRS from 900 rpm to 1200 rpm and TTS from 10 mm.min-1 to 20 mm.min-1.

Structure-Property Relationships of Solid State Additive Manufactured Aluminum Alloy 2219 and Inconel 625

NASA Astrophysics Data System (ADS)

Rivera Almeyda, Oscar G.

In this investigation, the processing-structure-property relations are correlated for solid state additively manufactured (SSAM) Inconel 625 (IN 625) and a SSAM aluminum alloy 2219 (AA2219). This is the first research of these materials processed by a new SSAM method called additive friction stir (AFS). The AFS process results in a refined grain structure by extruding solid rod through a rotating tool generating heat and severe plastic deformation. In the case of the AFS IN625, the IN625 alloy is known for exhibiting oxidation resistance and temperature mechanical stability, including strength and ductility. This study is the first to investigate the beneficial grain refinement and densification produced by AFS in IN625 that results in advantageous mechanical properties (YS, UTS, epsilonf) at both quasi-static and high strain rate. Electron Backscatter Diffraction (EBSD) observed dynamic recrystallization and grain refinement during the layer deposition in the AFS specimens, where the results identified fine equiaxed grain structures formed by dynamic recrystallization (DRX) with even finer grain structures forming at the layer interfaces. The EBSD quantified grains as fine as 0.27 microns in these interface regions while the average grain size was approximately 1 micron. Additionally, this is the first study to report on the strain rate dependence of AFS IN625 through quasi-static (QS) (0.001/s) and high strain rate (HR) (1500/s) tensile experiments using a servo hydraulic frame and a direct tension-Kolsky bar, respectively, which captured both yield and ultimate tensile strengths increasing as strain rate increased. Fractography performed on specimens showed a ductile fracture surface on both QS, and HR. Alternatively, the other AFS material system investigated in this study, AA2219, is mostly used for aerospace applications, specifically for rocket fuel tanks. EBSD was performed in the cross-section of the AA2219, also exhibiting DRX with equiaxed microstructure in the three directions and an average grain size of 2.5 microns. EBSD PFs showed that the material has a strong torsional fiber A texture in the top of the build, and this texture gets weaker in the middle and bottom sections. TEM showed that there are no theta' precipitates in the as-deposited cross-section, therefore no precipitation strengthening should be expected. Strain rate and stress state dependence was study, and in both tension and compression, with an increase in strain rate, the YS increase and the UTS decreased. Ductile fracture surface was observed on specimens tested to failure in both QS and HR. The AFS AA2219 processing-structure-property relations are being studied in this investigation to address the stress-state and strain rate dependence of AFS AA2219 with an internal sate variable (ISV) plasticity-damage model to capture the different yield stress, work hardening and failure strain in the AFS AA2219 for high fidelity modeling of AFS components. The ISV plasticity model successfully captured the material behavior in tension, compression, tension-followed-by-compression and compression-followed-by-tension experiments. Furthermore, the damage parameters of the model were calibrated using the final void density measured from the fracture surfaces.

Non-destructive and three-dimensional measurement of local strain development during tensile deformation in an aluminium alloy

NASA Astrophysics Data System (ADS)

Kobayashi, M.; Miura, H.; Toda, H.

2015-08-01

Anisotropy of mechanical responses depending on crystallographic orientation causes inhomogeneous deformation on the mesoscopic scale (grain size scale). Investigation of the local plastic strain development is important for discussing recrystallization mechanisms, because the sites with higher local plastic strain may act as potential nucleation sites for recrystallization. Recently, high-resolution X-ray tomography, which is non-destructive inspection method, has been utilized for observation of the materials structure. In synchrotron radiation X-ray tomography, more than 10,000 microstructural features, like precipitates, dispersions, compounds and hydrogen pores, can be observed in aluminium alloys. We have proposed employing these microstructural features as marker gauges to measure local strains, and then have developed a method to calculate the three-dimensional strain distribution by tracking the microstructural features. In this study, we report the development of local plastic strain as a function of the grain microstructure in an aluminium alloy by means of this three-dimensional strain measurement technique. Strongly heterogeneous strain development was observed during tensile loading to 30%. In other words, some parts of the sample deform little whereas another deforms a lot. However, strain in the whole specimen was keeping harmony. Comparing the microstructure with the strain concentration that is obtained by this method has a potential to reveal potential nucleation sites of recrystallization.

Structures, microfabrics, fractal analysis and temperature-pressure estimation of the Mesozoic Xingcheng-Taili ductile shear zone in the North China craton

NASA Astrophysics Data System (ADS)

Liang, Chenyue; Neubauer, Franz; Liu, Yongjiang; Jin, Wei; Zeng, Zuoxun; Bernroider, Manfred; Li, Weimin; Wen, Quanbo; Han, Guoqing; Zhao, Yingli

2014-05-01

The ductile shear zone in Xingcheng-Taili area (western Liaoning Province in China) is tectonically located in the eastern section of the northern margin of the North China craton, and dominantly comprises deformed granitic rocks of Neoarchean and Triassic to Late Jurassic age, which were affected by shearing within middle- to low-grade metamorphic conditions. Because a high-temperature metamorphic overprint is lacking, microstructures attesting to low-temperature ductile deformation are well preserved. However, the rocks and its structures have not been previously analyzed in detail except by U-Pb zircon dating and some geochemistry. Here, we describe the deformation characteristics and tectonic evolution of the Xingcheng-Taili ductile shear zone, in order to understand the mode of lithosphericscale reactivation, extension and thinning of the North China craton. The ductile deformation history comprises four successive deformation phases: (1) In the Neoarchean granitic rocks, a steep gneissosity and banded structures trend nearly E-W (D1). (2) A NE-striking sinistral structure of Upper Triassic rocks may indicate a deformation event (D2) in Late Triassic times, which ductile deformation structures superimposed on Neoarchean granitic rocks. (3) A gneissose structure with S-C fabrics as well as an ENE-trending sinistral strike-slip characteristic (D3) developed in Upper Jurassic biotite adamellite and show the deformation characteristics of a shallow crustal level and generated mylonitic fabrics superimposed on previous structures. (4) Late granitic dykes show different deformational behavior, and shortening with D4 folds. The attitude of the foliation S and mineral stretching lineation of three main types of rocks shows remarkable differences in orientation. The shapes of recrystallized quartz grains from three main types of granitic rocks with their jagged and indented boundaries were natural records of deformation conditions (D1to D3). Crystal preferred orientation of quartz determined by electron back scatter diffraction (EBSD) suggest sinistral strike-slip displacement within a temperature at about 400 to 500° C. Quartz mainly shows low-temperature fabrics with dominant {0001}-slip system. As the deformed rocks show obvious deformation overprint, we have estimated flow stresses from dynamically recrystallized grain sizes of quartz separately. But coincident fractal analysis showed that the boundaries of recrystallized grains had statistically self similarities with the numbers of fractal dimension from 1.153 to 1.196 with the range of deformation temperatures from 500 to 600° C, which is corresponding to upper greenschist to lower amphibolite facies conditions. Together with published flow laws to estimated deformation rates between the region of 10-11 - 10-13 S-1depending on the temperature 500 ° C, and the paleo-stress was calculated with grain size of recrystallized quartz to be at 5.0 to 32.3 MPa. Even though the deformation history and kinematics are different, progressive microstructures and texture analysis indicate an overprint by the low-temperature deformation (D3). Typical regional-dynamic metamorphic conditions ere deduced by mineral pair hornblende-plagioclase and phengite barometry identified within the ductile shear zone. The hornblende-plagioclase pair of porphyritic granitic gneiss gives metamorphic conditions of T =450-500 ° C and p=0.39 GPa, which indicate a metamorphic grade of lower-amphibolite facies conditions and a depth of around 13 km estimated following a normal lithostatic pressure. All of the structural characteristics indicate that the Xingcheng-Taili ductile shear zone represents a mainly ENE-striking sinistral ductile strike-slip zone, which formed after intrusion of the Upper Jurassic biotite adamellite and transformed and superimposed previous deformation structures. This deformation event might have occurred in Early Cretaceous times and was related to the lithospheric thinning and extension, due to roll-back of the Pacific plate beneath the eastern North China craton.

Microstructural and mechanical responses to various rolling speeds determined in multi-pass break-down rolling of AZ31B alloy

NASA Astrophysics Data System (ADS)

Jia, Weitao; Tang, Yan; Ning, Fangkun; Le, Qichi; Cui, Jianzhong

2018-04-01

Different rolling operations of as-cast AZ31B alloy were performed under different rolling speed (18 ∼ 72 m min‑1) and rolling pass conditions at 400 °C. Microstructural studies, tensile testing and formability evaluation relevant to each rolling operation were investigated. For 1-pass rolling, coarse average grain size (CAGS) region gradually approached the center layer as the rolling speed increased. Moreover, twins, shear bands and coarse-grain structures were the dominant components in the microstructure of plates rolled at 18, 48 and 72 m min‑1, respectively, indicating the severe deformation inhomogeneity under the high reduction per pass condition. For 2-pass rolling and 4-pass rolling, dynamic recrystallization was observed to be well and CAGS region has substantially disappeared, indicating the significant improvement in deformation uniformity and further the grain homogenization under the conditions. Microstructure uniformity degree of 2-pass rolled plates did not vary much as the rolling speed varied. On this basis, shear band distribution dominated the deformation behavior during the uniaxial tension of the 2-pass rolled plates. However, microstructure uniformity accompanied by twin distribution played a leading role in stretching the 4-pass rolled plates.

Development of Ti microalloyed high strength steel plate by controlling thermo-mechanical control process schedule

NASA Astrophysics Data System (ADS)

Xia, Jinian; Huo, Xiangdong; Li, Liejun; Peng, Zhengwu; Chen, Songjun

2017-12-01

In this study, the TMCP parameters including non-recrystallization temperature (Tnr) and optimal isothermal temperature were determined by thermal simulation experiments, and a new Ti microalloyed high strength steel plate was developed by controlling thermo-mechanical control process (TMCP) schedule. The effects of TMCP process on microstructural features, precipitation behavior and mechanical properties of Ti microalloyed high strength steel plate were investigated. The results revealed that the double-stage rolling process consist of rolling in the γ recrystallization region and the γ non-recrystallization region was benefical to promoting the mechanical properties of Ti microalloyed steel by achieving grain refinement. It was also found that large amounts of fine TiC (<10 nm) particles were precipitated during the isothermal treatment at 600 °C, which generated a 215 MPa precipitation strengthening effect.

Tailored Net-Shape Powder Composites by Spark Plasma Sintering

NASA Astrophysics Data System (ADS)

Khaleghi, Evan Aryan

This dissertation investigates the ability to produce net-shape and tailored composites in spark plasma sintering (SPS), with an analysis of how grain growth, densification, and mechanical properties are affected. Using alumina and four progressively anisotropic dies, we studied the impact of specimen shape on densification. We found specimen shape had an impact on overall densification, but no impact on localized properties. We expected areas of the specimen to densify differently, or have higher grain growth, based on current anisotropy in the specimen during sintering, and preliminary results indicated this, but further investigation showed this did not occur. Overall average grain size and porosity decreased as shape complexity increased. In Fe-V-C steel, we mechanical alloyed two rapidly solidified powders, and used spark sintering to retain the properties imparted during the rapid solidification. We noticed VC grains being produced during densification, which improved the final properties. We conducted spark plasma extrusion (SPE) of aluminum to understand the effect on microstructure. We found, through an analysis of the grain structure, that SPE did have a grain deformation potential, and grain size was severely decreased compared to conventional sintering. Dynamic recrystallization did not occur, due to the reduced temperatures we were able to extrude with SPS. Finally, we examined whether there were particular sintering conditions for SPS that reduced the complexity of the grain growth and porosity relationship to one similar to conventional sintering, of the form G = k G0 ε -1/. We found that although a reasonable case could be made for free sintering, as found in the literature, for hot-pressing and SPS the conditions required go against the common knowledge in grain growth and densification kinetics. We were able to fit our data very well to the model, but the correlated results do not make physical sense.

Plasticity-mediated collapse and recrystallization in hollow copper nanowires: a molecular dynamics simulation.

PubMed

Dutta, Amlan; Raychaudhuri, Arup Kumar; Saha-Dasgupta, Tanusri

2016-01-01

We study the thermal stability of hollow copper nanowires using molecular dynamics simulation. We find that the plasticity-mediated structural evolution leads to transformation of the initial hollow structure to a solid wire. The process involves three distinct stages, namely, collapse, recrystallization and slow recovery. We calculate the time scales associated with different stages of the evolution process. Our findings suggest a plasticity-mediated mechanism of collapse and recrystallization. This contradicts the prevailing notion of diffusion driven transport of vacancies from the interior to outer surface being responsible for collapse, which would involve much longer time scales as compared to the plasticity-based mechanism.

Development of high-temperature Kolsky compression bar techniques for recrystallization investigation

NASA Astrophysics Data System (ADS)

Song, B.; Antoun, B. R.; Boston, M.

2012-05-01

We modified the design originally developed by Kuokkala's group to develop an automated high-temperature Kolsky compression bar for characterizing high-rate properties of 304L stainless steel at elevated temperatures. Additional features have been implemented to this high-temperature Kolsky compression bar for recrystallization investigation. The new features ensure a single loading on the specimen and precise time and temperature control for quenching to the specimen after dynamic loading. Dynamic compressive stress-strain curves of 304L stainless steel were obtained at 21, 204, 427, 649, and 871 °C (or 70, 400, 800, 1200, and 1600 °F) at the same constant strain rate of 332 s-1. The specimen subjected to specific time and temperature control for quenching after a single dynamic loading was preserved for investigating microstructure recrystallization.

On the development of a model predicting the recrystallization texture of aluminum using the Taylor model for rolling textures and the coincidence lattice site theory

NASA Astrophysics Data System (ADS)

T, Morimoto; F, Yoshida; A, Yanagida; J, Yanagimoto

2015-04-01

First, hardening model in f.c.c. metals was formulated with collinear interactions slips, Hirth slips and Lomer-Cottrell slips. Using the Taylor and the Sachs rolling texture prediction model, the residual dislocation densities of cold-rolled commercial pure aluminum were estimated. Then, coincidence site lattice grains were investigated from observed cold rolling texture. Finally, on the basis of oriented nucleation theory and coincidence site lattice theory, the recrystallization texture of commercial pure aluminum after low-temperature annealing was predicted.

Fundamental Studies on High Temperature Deformation Recrystallization, and Grain Growth of Two-Phase Materials.

DTIC Science & Technology

1988-01-01

gm (17 ml) Benzalkonium . Chloride (50%) 35 ml Ethanol The Ti-V alloys were etched with the following etchant for 6 to 10 seconds. 4 mlHN03 conc. 2 ml...60 % reduction in area was given for all the alloys. This work was found to be sufficient to recrystallize all of the alloys within 6 hours at 9730 K...condition of net reduction in surfaces 17 °.4- *. *¢ ’ N N-, . ’ . . ’,, . , . . .,...’,’." ,,_...,. ,...’.’.’, ...-.......-.. : ’If LS becomes b2 .(db]/d1

Effect of Extrusion Parameters on Texture and Microstructure Evolution of Extruded Mg-1 pctMn and Mg-1 pctMn-Sr Alloys

NASA Astrophysics Data System (ADS)

Borkar, Hemant; Pekguleryuz, Mihriban

2015-01-01

Three Mg alloys Mg-1 pctMn (M1), Mg-1 pctMn-1.3 pctSr, and Mg-1 pctMn-2.1 pctSr were subjected to two different extrusion temperatures and two different extrusion speeds in lab-scale extrusion. The extrusion temperatures of 573 K and 673 K (300 °C and 400 °C) and two ram speeds of 4 and 8 mm/s were used at constant extrusion ratio of 7. M1 exhibited strong basal texture after extrusion at 673 K (400 °C) at higher speed. At 573 K (300 °C), recrystallization in all alloys takes place completely or partially by continuous dynamic recrystallization mechanism, while particle stimulated nucleation (PSN) occurs in all M1-Sr alloys at both extrusion temperatures and speeds. At 673 K (400 °C), grain boundary bulging is the only recrystallization mechanism in alloy M1, while it occurs in combination with PSN in M1-Sr alloys. The effect of texture weakening by PSN is more significant in M1-Sr alloys extruded at 573 K (400 °C). The plant extrusion trials were carried out on Mg-1 pctMn, Mg-1 pctMn-0.3 pctSr, and Mg-1 pctMn-2.1 pctSr at 623 K (350 °C) with different speeds than in lab-scale extrusion. M1 alloy exhibited strong basal texture at both speeds, while Sr additions of 0.3 and 2.1 pct promoted similar amount of texture weakening.

Synchrotron FTIR imaging of OH in quartz mylonites

NASA Astrophysics Data System (ADS)

Kronenberg, Andreas K.; Hasnan, Hasnor F. B.; Holyoke, Caleb W., III; Law, Richard D.; Liu, Zhenxian; Thomas, Jay B.

2017-10-01

Previous measurements of water in deformed quartzites using conventional Fourier transform infrared spectroscopy (FTIR) instruments have shown that water contents of larger grains vary from one grain to another. However, the non-equilibrium variations in water content between neighboring grains and within quartz grains cannot be interrogated further without greater measurement resolution, nor can water contents be measured in finely recrystallized grains without including absorption bands due to fluid inclusions, films, and secondary minerals at grain boundaries.Synchrotron infrared (IR) radiation coupled to a FTIR spectrometer has allowed us to distinguish and measure OH bands due to fluid inclusions, hydrogen point defects, and secondary hydrous mineral inclusions through an aperture of 10 µm for specimens > 40 µm thick. Doubly polished infrared (IR) plates can be prepared with thicknesses down to 4-8 µm, but measurement of small OH bands is currently limited by strong interference fringes for samples < 25 µm thick, precluding measurements of water within individual, finely recrystallized grains. By translating specimens under the 10 µm IR beam by steps of 10 to 50 µm, using a software-controlled x - y stage, spectra have been collected over specimen areas of nearly 4.5 mm2. This technique allowed us to separate and quantify broad OH bands due to fluid inclusions in quartz and OH bands due to micas and map their distributions in quartzites from the Moine Thrust (Scotland) and Main Central Thrust (Himalayas).Mylonitic quartzites deformed under greenschist facies conditions in the footwall to the Moine Thrust (MT) exhibit a large and variable 3400 cm-1 OH absorption band due to molecular water, and maps of water content corresponding to fluid inclusions show that inclusion densities correlate with deformation and recrystallization microstructures. Quartz grains of mylonitic orthogneisses and paragneisses deformed under amphibolite conditions in the hanging wall to the Main Central Thrust (MCT) exhibit smaller broad OH bands, and spectra are dominated by sharp bands at 3595 to 3379 cm-1 due to hydrogen point defects that appear to have uniform, equilibrium concentrations in the driest samples. The broad OH band at 3400 cm-1 in these rocks is much less common. The variable water concentrations of MT quartzites and lack of detectable water in highly sheared MCT mylonites challenge our understanding of quartz rheology. However, where water absorption bands can be detected and compared with deformation microstructures, OH concentration maps provide information on the histories of deformation and recovery, evidence for the introduction and loss of fluid inclusions, and water weakening processes.

Synchrotron FTIR imaging of OH in quartz mylonites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kronenberg, Andreas K.; Hasnan, Hasnor F. B.; Holyoke III, Caleb W.

Previous measurements of water in deformed quartzites using conventional Fourier transform infrared spectroscopy (FTIR) instruments have shown that water contents of larger grains vary from one grain to another. However, the non-equilibrium variations in water content between neighboring grains and within quartz grains cannot be interrogated further without greater measurement resolution, nor can water contents be measured in finely recrystallized grains without including absorption bands due to fluid inclusions, films, and secondary minerals at grain boundaries.Synchrotron infrared (IR) radiation coupled to a FTIR spectrometer has allowed us to distinguish and measure OH bands due to fluid inclusions, hydrogen point defects,more » and secondary hydrous mineral inclusions through an aperture of 10 µm for specimens > 40 µm thick. Doubly polished infrared (IR) plates can be prepared with thicknesses down to 4–8 µm, but measurement of small OH bands is currently limited by strong interference fringes for samples < 25 µm thick, precluding measurements of water within individual, finely recrystallized grains. By translating specimens under the 10 µm IR beam by steps of 10 to 50 µm, using a software-controlled x- y stage, spectra have been collected over specimen areas of nearly 4.5 mm 2. This technique allowed us to separate and quantify broad OH bands due to fluid inclusions in quartz and OH bands due to micas and map their distributions in quartzites from the Moine Thrust (Scotland) and Main Central Thrust (Himalayas).Mylonitic quartzites deformed under greenschist facies conditions in the footwall to the Moine Thrust (MT) exhibit a large and variable 3400 cm -1 OH absorption band due to molecular water, and maps of water content corresponding to fluid inclusions show that inclusion densities correlate with deformation and recrystallization microstructures. Quartz grains of mylonitic orthogneisses and paragneisses deformed under amphibolite conditions in the hanging wall to the Main Central Thrust (MCT) exhibit smaller broad OH bands, and spectra are dominated by sharp bands at 3595 to 3379 cm -1 due to hydrogen point defects that appear to have uniform, equilibrium concentrations in the driest samples. The broad OH band at 3400 cm -1 in these rocks is much less common. The variable water concentrations of MT quartzites and lack of detectable water in highly sheared MCT mylonites challenge our understanding of quartz rheology. However, where water absorption bands can be detected and compared with deformation microstructures, OH concentration maps provide information on the histories of deformation and recovery, evidence for the introduction and loss of fluid inclusions, and water weakening processes.« less

Resistance spot welding of ultra-fine grained steel sheets produced by constrained groove pressing: Optimization and characterization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khodabakhshi, F.; Kazeminezhad, M., E-mail: mkazemi@sharif.edu; Kokabi, A.H.

2012-07-15

Constrained groove pressing as a severe plastic deformation method is utilized to produce ultra-fine grained low carbon steel sheets. The ultra-fine grained sheets are joined via resistance spot welding process and the characteristics of spot welds are investigated. Resistance spot welding process is optimized for welding of the sheets with different severe deformations and their results are compared with those of as-received samples. The effects of failure mode and expulsion on the performance of ultra-fine grained sheet spot welds have been investigated in the present paper and the welding current and time of resistance spot welding process according to thesemore » subjects are optimized. Failure mode and failure load obtained in tensile-shear test, microhardness, X-ray diffraction, transmission electron microscope and scanning electron microscope images have been used to describe the performance of spot welds. The region between interfacial to pullout mode transition and expulsion limit is defined as the optimum welding condition. The results show that optimum welding parameters (welding current and welding time) for ultra-fine grained sheets are shifted to lower values with respect to those for as-received specimens. In ultra-fine grained sheets, one new region is formed named recrystallized zone in addition to fusion zone, heat affected zone and base metal. It is shown that microstructures of different zones in ultra-fine grained sheets are finer than those of as-received sheets. - Highlights: Black-Right-Pointing-Pointer Resistance spot welding process is optimized for joining of UFG steel sheets. Black-Right-Pointing-Pointer Optimum welding current and time are decreased with increasing the CGP pass number. Black-Right-Pointing-Pointer Microhardness at BM, HAZ, FZ and recrystallized zone is enhanced due to CGP.« less

Post-igneous redistribution of components in eucrites

NASA Technical Reports Server (NTRS)

Phinney, W. C.; Lindstrom, D. J.; Mittlefehldt, D. W.; Martinez, R. R.

1993-01-01

In our analyses, we utilize a microdrilling technique that removes 40 to 100 micron diameter cores from mineral grains in thin sections analyzed by microprobe. The cores are then analyzed by INAA using the technique of Lindstrom. Three eucrites were selected for application of this analytical technique: monomict breccias Pasamonte and Stannern and unbrecciated EET90020. Pasamonte is among the most unequilibrated of the eucrites on the basis of zoning in pyroxenes and is considered to be an igneous rock not significantly affected by metamorphism. Stannern has igneous texture but its pyroxenes indicate some re-equilibration, although little, if any, recrystallization. EET90020 has a granulite texture and has been substantially recrystallized. Our sample of Pasamonte contains several clasts of different grain sizes ranging from glass to fine grained with diabasic texture containing lathy plagioclase, unexsolved pigeonite, and mesostasis. Cores were taken of the glass and from minerals and mesostases in six lithic clasts which normally allowed sampling of more than one phase per clast. Our sample of Stannern is also a breccia but with little difference in grain size between clasts and matrix. The plagioclase and pigeonite are blocky, twinned, and exsolved and coexist with a bit of mesostasis. Cores were taken of plagioclase and pigeonite with no attempt to distinguish separate clasts. EET90020 is a granular mixture of twinned plagioclase and pigeonite having rather uniform size and many triple junctions. Several cores were taken of both phases. Both clear and cloudy grains of plagioclase and pyroxene were sampled in all three eucrites.

Electron Microscopy Characterizations and Atom Probe Tomography of Intergranular Attack in Alloy 600 Exposed to PWR Primary Water

NASA Astrophysics Data System (ADS)

Olszta, Matthew J.; Schreiber, Daniel K.; Thomas, Larry E.; Bruemmer, Stephen M.

Detailed examinations of intergranular attack (IGA) in alloy 600 were performed after exposure to simulated PWR primary water at 325°C for 500 h. High-resolution analyses of IGA characteristics were conducted on specimens with either a 1 µm diamond or 1200-grit SiC surface finish using scanning electron microscopy, transmission electron microscopy and atom probe tomography techniques. The diamond-polish finish with very little preexisting subsurface damage revealed attack of high-energy grain boundaries that intersected the exposed surface to depths approaching 2 µm. In all cases, IGA from the surface is localized oxidation consisting of porous, nanocrystalline MO-structure and spinel particles along with regions of faceted wall oxidation. Surprisingly, this continuous IG oxidation transitions to discontinuous, discrete Cr-rich sulfide particles up to 50 nm in diameter. In the vicinity of the sulfides, the grain boundaries were severely Cr depleted (to <1 at%) and enriched in S. The 1200 grit SiC finish surface exhibited a preexisting highly strained recrystallized layer of elongated nanocrystalline matrix grains. Similar IG oxidation and leading sulfide particles were found, but the IGA depth was typically confined to the near-surface ( 400 nm) recrystallized region. Difference in IGA for the two surface finishes indicates that the formation of grain boundary sulfides occurs during the exposure to PWR primary water. The source of S remains unclear, however it is not present as sulfides in the bulk alloy nor is it segregated to bulk grain boundaries.

Recrystallization Behavior in Mixed Solder Joints of BGA Components during Thermal Shock

NASA Astrophysics Data System (ADS)

Tan, Shihai; Han, Jing; Guo, Fu

2018-03-01

Sn-37Pb and Sn-3.0Ag-0.5Cu solder pastes printed onto a board were attached to ball grid array (BGA) samples using Sn-3.0Ag-0.5Cu solder balls. Before thermal shock, the initial grain orientations on the cross-section were obtained by scanning electron microscopy equipped with an electron backscattered diffraction system. Three mixed solder joints (two from the corner and another from the middle of the BGA component) and three lead-free solder joints (at the same positions) were selected to investigate the recrystallization behavior under thermal shock (TS) cycling conditions. All of the mixed and lead-free solder joints were initially single crystal. The results showed that recrystallization occurred in both the mixed and lead-free solder joints after 200 TS. For the mixed solder joints, more recrystallization was observed and the location of samples had a significant influence on their recrystallization behavior, while location was not as important for the lead-free samples after 200 TS in this study. Both the mixed and lead-free solder joints at the corner of BGA components showed the poorest reliability. According to misorientation distribution maps and subgrain rotation behaviors, the reliability of mixed solder joints was much poorer than that of lead-free solder joints.

Method of producing superplastic alloys and superplastic alloys produced by the method

NASA Technical Reports Server (NTRS)

Troeger, Lillianne P. (Inventor); Starke, Jr., Edgar A. (Inventor); Crooks, Roy (Inventor)

2002-01-01

A method for producing new superplastic alloys by inducing in an alloy the formation of precipitates having a sufficient size and homogeneous distribution that a sufficiently refined grain structure to produce superplasticity is obtained after subsequent PSN processing. An age-hardenable alloy having at least one dispersoid phase is selected for processing. The alloy is solution heat-treated and cooled to form a supersaturated solid solution. The alloy is plastically deformed sufficiently to form a high-energy defect structure useful for the subsequent heterogeneous nucleation of precipitates. The alloy is then aged, preferably by a multi-stage low and high temperature process, and precipitates are formed at the defect sites. The alloy then is subjected to a PSN process comprising plastically deforming the alloy to provide sufficient strain energy in the alloy to ensure recrystallization, and statically recrystallizing the alloy. A grain structure exhibiting new, fine, equiaxed and uniform grains is produced in the alloy. An exemplary 6xxx alloy of the type capable of being produced by the present invention, and which is useful for aerospace, automotive and other applications, is disclosed and claimed. The process is also suitable for processing any age-hardenable aluminum or other alloy.

Modeling of intragranular misorientation and grain fragmentation in polycrystalline materials using the viscoplastic self-consistent formulation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zecevic, Miroslav; Lebensohn, Ricardo A.; McCabe, Rodney J.

In this paper, the recently established methodology to use known algorithmic expressions of the second moments of the stress field in the grains of a polycrystalline aggregate for calculating average fluctuations of lattice rotation rates and the associated average intragranular misorientation distributions using the mean-field viscoplastic self-consistent (VPSC) formulation is extended to solve the coupled problem of considering the effect of intragranular misorientations on stress and rotation rate fluctuations. In turn, these coupled expressions are used to formulate and implement a grain fragmentation (GF) model in VPSC. Case studies, including tension and plane-strain compression of face-centered cubic polycrystals are usedmore » to illustrate the capabilities of the new model. GF-VPSC predictions of intragranular misorientation distributions and texture evolution are compared with experiments and full-field numerical simulations, showing good agreement. In particular, the inclusion of misorientation spreads reduced the intensity of the deformed texture and thus improved the texture predictions. Finally and moreover, considering that intragranular misorientations act as driving forces for recrystallization, the new GF-VPSC formulation is shown to enable modeling of microstructure evolution during deformation and recrystallization, in a computationally efficient manner.« less

Modeling of intragranular misorientation and grain fragmentation in polycrystalline materials using the viscoplastic self-consistent formulation

DOE PAGES

Zecevic, Miroslav; Lebensohn, Ricardo A.; McCabe, Rodney J.; ...

2018-06-15

In this paper, the recently established methodology to use known algorithmic expressions of the second moments of the stress field in the grains of a polycrystalline aggregate for calculating average fluctuations of lattice rotation rates and the associated average intragranular misorientation distributions using the mean-field viscoplastic self-consistent (VPSC) formulation is extended to solve the coupled problem of considering the effect of intragranular misorientations on stress and rotation rate fluctuations. In turn, these coupled expressions are used to formulate and implement a grain fragmentation (GF) model in VPSC. Case studies, including tension and plane-strain compression of face-centered cubic polycrystals are usedmore » to illustrate the capabilities of the new model. GF-VPSC predictions of intragranular misorientation distributions and texture evolution are compared with experiments and full-field numerical simulations, showing good agreement. In particular, the inclusion of misorientation spreads reduced the intensity of the deformed texture and thus improved the texture predictions. Finally and moreover, considering that intragranular misorientations act as driving forces for recrystallization, the new GF-VPSC formulation is shown to enable modeling of microstructure evolution during deformation and recrystallization, in a computationally efficient manner.« less

Analysis of crystallographic preferred orientations of experimentally deformed Black Hills Quartzite

NASA Astrophysics Data System (ADS)

Kilian, Rüdiger; Heilbronner, Renée

2017-10-01

The crystallographic preferred orientations (textures) of three samples of Black Hills Quartzite (BHQ) deformed experimentally in the dislocation creep regimes 1, 2 and 3 (according to Hirth and Tullis, 1992) have been analyzed using electron backscatter diffraction (EBSD). All samples were deformed to relatively high strain at temperatures of 850 to 915 °C and are almost completely dynamically recrystallized. A texture transition from peripheral [c] axes in regime 1 to a central [c] maximum in regime 3 is observed. Separate pole figures are calculated for different grain sizes, aspect ratios and long-axis trends of grains, and high and low levels of intragranular deformation intensity as measured by the mean grain kernel average misorientation (gKAM). Misorientation relations are analyzed for grains of different texture components (named Y, B, R and σ grains, with reference to previously published prism, basal, rhomb and σ1 grains). Results show that regimes 1 and 3 correspond to clear end-member textures, with regime 2 being transitional. Texture strength and the development of a central [c]-axis maximum from a girdle distribution depend on deformation intensity at the grain scale and on the contribution of dislocation creep, which increases towards regime 3. Adding to this calculations of resolved shear stresses and misorientation analysis, it becomes clear that the peripheral [c]-axis maximum in regime 1 is not due to deformation by basal a slip. Instead, we interpret the texture transition as a result of different texture forming processes, one being more efficient at high stresses (nucleation or growth of grains with peripheral [c] axes), the other depending on strain (dislocation glide involving prism and rhomb a slip systems), and not as a result of temperature-dependent activity of different slip systems.

SUMMARY REPORT ON THE STUDY OF BETA TREATMENT OF URANIUM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Russell, R.B.; Wolff, A.K.

A study was made on the effects of beta treatment variables on the texture, grain size, and distortion in unalloyed dingot and ingot uranium. The effects of delta heat treatment, various cooling regimes, recrystallization, etc., were studied. (D.L.C.)

Plasticity-mediated collapse and recrystallization in hollow copper nanowires: a molecular dynamics simulation

PubMed Central

Raychaudhuri, Arup Kumar; Saha-Dasgupta, Tanusri

2016-01-01

Summary We study the thermal stability of hollow copper nanowires using molecular dynamics simulation. We find that the plasticity-mediated structural evolution leads to transformation of the initial hollow structure to a solid wire. The process involves three distinct stages, namely, collapse, recrystallization and slow recovery. We calculate the time scales associated with different stages of the evolution process. Our findings suggest a plasticity-mediated mechanism of collapse and recrystallization. This contradicts the prevailing notion of diffusion driven transport of vacancies from the interior to outer surface being responsible for collapse, which would involve much longer time scales as compared to the plasticity-based mechanism. PMID:26977380

Molecular Dynamics at the Interface between Ice and Poly(vinyl alcohol) and Ice Recrystallization Inhibition.

PubMed

Weng, Lindong; Stott, Shannon L; Toner, Mehmet

2018-05-01

Ice formation is a ubiquitous process that poses serious challenges for many areas. Nature has evolved a variety of different mechanisms to regulate ice formation. For example, many cold-adapted species produce antifreeze proteins (AFPs) and/or antifreeze glycoproteins (AFGPs) to inhibit ice recrystallization. Although several synthetic substitutes for AF(G)Ps have been developed, the fundamental principles of designing AF(G)P mimics are still missing. In this study, we explored the molecular dynamics of ice recrystallization inhibition (IRI) by poly(vinyl alcohol) (PVA), a well-recognized ice recrystallization inhibitor, to shed light on the otherwise hidden ice-binding mechanisms of chain polymers. Our molecular dynamics simulations revealed a stereoscopic, geometrical match between the hydroxyl groups of PVA and the water molecules of ice, and provided microscopic evidence of the adsorption of PVA to both the basal and prism faces of ice and the incorporation of short-chain PVA into the ice lattice. The length of PVA, i.e., the number of hydroxyl groups, seems to be a key factor dictating the performance of IRI, as the PVA molecule must be large enough to prevent the joining together of adjacent curvatures in the ice front. The findings in this study will help pave the path for addressing a pressing challenge in designing synthetic ice recrystallization inhibitors rationally, by enriching our mechanistic understanding of IRI process by macromolecules.

The Neutron Tomography Studies of the Rocks from the Kola Superdeep Borehole

NASA Astrophysics Data System (ADS)

Kichanov, S. E.; Kozlenko, D. P.; Ivankina, T. I.; Rutkauskas, A. V.; Lukin, E. V.; Savenko, B. N.

The volume morphology of a gneiss sample K-8802 recovered from the deep of 8802 m of the Kola Superdeep Borehole and its surface homologue sample PL-36 have been studied by means of neutron radiography and tomography methods. The volumes and size distributions of a biotite-muscovite grains as well as grains orientation distribution have been obtained from experimental data. It was found that the average volumes of the biotite-muscovite grains in surface homologue sample is noticeably larger than the average volume of grains in the deep-seated gneiss sample K-8802. This drastically differences in grains volumes can be explained by the recrystallization processes in deep of the Kola Superdeep Borehole at high temperatures and high pressures.

Artificial meteor ablation studies: Olivine

NASA Technical Reports Server (NTRS)

Blanchard, M. B.; Cunningham, G. G.

1973-01-01

Artificial meteor ablation was performed on a Mg-rich olivine sample using an arc-heated plasma of ionized air. Experimental conditions simulated a meteor traveling about 12 km/sec at an altitude of 70 km. The mineral content of the original olivine sample was 98% olivine (including traces of olivine alteration products) and 2% chromite. Forsterite content of the original olivine was Fo-89. After ablation, the forsterite content had increased to Fo-94 in the recrystallized olivine. In addition, lamella-like intergrowths of magnetite were prevalent constituents. Wherever magnetite occurred, there was an increase in Mg and a corresponding decrease in Fe for the recrystallized olivine. The Allende fusion crust consisted of a recrystallized olivine, which was more Mg-rich and Fe-deficient than the original meteorite's olivine, and abundant magnetite grains. Although troilite and pentlandite were the common opaque mineral constituents in this meteorite, magnetite was the principal opaque mineral found in the fusion crust.

Investigation on the optimized heat treatment procedure for laser fabricated IN718 alloy

NASA Astrophysics Data System (ADS)

Zhang, Yaocheng; Yang, Li; Chen, Tingyi; Zhang, Weihui; Huang, Xiwang; Dai, Jun

2017-12-01

The laser fabricated IN718 alloys were prepared by laser cladding system. The microstructure and microhardness of laser fabricated IN718 alloys were investigated after heat treatment. The microstructure and the elevated temperature mechanical properties of laser fabricated IN718 alloys were analyzed. The results showed that the microstructure of laser fabricated IN718 alloy consisted of austenitic matrix and dendritic Laves/γ eutectic. Most all Laves/γ eutectic was dissolved into austenitic matrix, and the complete recrystallization and the large grains occurred in the laser fabricated IN718 alloy after homogenization at 1080-1140 °C for 1 h, the dendritic Laves/γ eutectic was refined and the partial recrystallization occurred during the solid solution at 940-1000 °C for 1.5 h, the microhardness of the double aging (DA) alloys was about more than twice that of as-fabricated IN718 alloy. The recrystallized microstructure was obtained in the heat-treated laser fabricated IN718 alloy after 1100 °C/1 h air cooling (AC), 980 °C/1.5 h (AC), 700 °C/8 h furnace cooling (FC, 100 °C/h) to 600 °C/8 h (AC). The microhardness and the elevated temperature tensile strength were more than twice that of as-fabricated IN718 alloy due to a large concentration of γ″ phase precipitation to improve the transgranular strength and large grain to guarantee the grain boundary strength. The fracture morphologies of as-fabricated and heat-treated laser fabricated IN718 alloys were presented as the fiber dimples, the fracture mechanism of as-fabricated and heat-treated laser fabricated IN718 alloys was ductile fracture.

Deformation, static recrystallization, and reactive melt transport in shallow subcontinental mantle xenoliths (Tok Cenozoic volcanic field, SE Siberia)

NASA Astrophysics Data System (ADS)

Tommasi, Andréa; Vauchez, Alain; Ionov, Dmitri A.

2008-07-01

Partial melting and reactive melt transport may change the composition, microstructures, and physical properties of mantle rocks. Here we explore the relations between deformation and reactive melt transport through detailed microstructural analysis and crystallographic orientation measurements in spinel peridotite xenoliths that sample the shallow lithospheric mantle beneath the southeastern rim of the Siberian craton. These xenoliths have coarse-grained, annealed microstructures and show petrographic and chemical evidence for variable degrees of reaction with silicate melts and fluids, notably Fe-enrichment and crystallization of metasomatic clinopyroxene (cpx). Olivine crystal preferred orientations (CPO) range from strong to weak. [010]-fiber patterns, characterized by a point concentration of [010] normal to the foliation and by dispersion of [100] in the foliation plane with a weak maximum parallel to the lineation, predominate relative to the [100]-fiber patterns usually observed in lithospheric mantle xenoliths and peridotite massifs. Variations in olivine CPO patterns or intensity are not correlated with modal and chemical compositions. This, together with the analysis of microstructures, suggests that reactive melt percolation postdated both deformation and static recrystallization. Preferential crystallization of metasomatic cpx along (010) olivine grain boundaries points to an influence of the preexisting deformation fabrics on melt transport, with higher permeability along the foliation. Similarity between orthopyroxene (opx) and cpx CPO suggests that cpx orientations may be inherited from those of opx during melt-rock reaction. As observed in previous studies, reactive melt transport does not weaken olivine CPO and seismic anisotropy in the upper mantle, except in melt accumulation domains. In contrast, recovery and selective grain growth during static recrystallization may lead to development of [010]-fiber olivine CPO and, if foliations are horizontal, result in apparent isotropy for vertically propagating SKS waves, but strong anisotropy for horizontally propagating surface waves.

Evolution of Deformation and Recrystallization Textures in High-Purity Ni and the Ni-5 at. pct W Alloy

NASA Astrophysics Data System (ADS)

Bhattacharjee, Pinaki P.; Ray, Ranjit K.; Tsuji, Nobuhiro

2010-11-01

An attempt has been made to study the evolution of texture in high-purity Ni and Ni-5 at. pct W alloy prepared by the powder metallurgy route followed by heavy cold rolling ( 95 pct deformation) and recrystallization. The deformation textures of the two materials are of typical pure metal or Cu-type texture. Cube-oriented ( left\\{ {00 1} right\\}left< { 100} rightrangle ) regions are present in the deformed state as long thin bands, elongated in the rolling direction (RD). These bands are characterized by a high orientation gradient inside, which is a result of the rotation of the cube-oriented cells around the RD toward the RD-rotated cube ( left\\{ {0 1 3} right\\}left< { 100} rightrangle ). Low-temperature annealing produces a weak cube texture along with the left\\{ {0 1 3} right\\}left< { 100} rightrangle component, with the latter being much stronger in high-purity Ni than in the Ni-W alloy. At higher temperatures, the cube texture is strengthened considerably in the Ni-W alloy; however, the cube volume fraction in high-purity Ni is significantly lower because of the retention of the left\\{ {0 1 3} right\\}left< { 100} rightrangle component. The difference in the relative strengths of the cube, and the left\\{ {0 1 3} right\\}left< { 100} rightrangle components in the two materials is evident from the beginning of recrystallization in which more left\\{ {0 1 3} right\\}left< { 100} rightrangle -oriented grains than near cube grains form in high-purity Ni. The preferential nucleation of the near cube and the left\\{ {0 1 3} right\\}left< { 100} rightrangle grains in these materials seems to be a result of the high orientation gradients associated with the cube bands that offer a favorable environment for early nucleation.

Hot Ductility Behavior of an 8 Pct Cr Roller Steel

NASA Astrophysics Data System (ADS)

Wang, Zhenhua; Sun, Shuhua; Shi, Zhongping; Wang, Bo; Fu, Wantang

2015-04-01

The hot ductility of an 8 pct Cr roller steel was determined between 1173 K and 1473 K (900 °C and 1200 °C) at strain rates of 0.01 to 10 s-1 through tensile testing. The fracture morphology was observed using scanning electron microscopy, and the microstructure was examined through optical microscopy and transmission electron microscopy. The dependence of the hot ductility behavior on the deformation conditions, grain size, and precipitation was analyzed. The relationship between the reduction in area and the natural logarithm of the Zener-Hollomon parameter (ln Z) was found to be a second-order polynomial. When ln Z was greater than 40 s-1, the hot ductility was poor and fracture was mainly caused by incompatible deformation between the grains. When ln Z was between 32 and 40 s-1, the hot ductility was excellent and the main fracture mechanism was void linking. When ln Z was below 32 s-1, the hot ductility was poor and fracture was mainly caused by grain boundary sliding. A fine grain structure is beneficial for homogenous deformation and dynamic recrystallization, which induces better hot ductility. The effect of M7C3 carbide particles dispersed in the matrix on the hot ductility was small. The grain growth kinetics in the 8 pct Cr steel were obtained between 1373 K and 1473 K (1100 °C and 1200 °C). Finally, optimized preheating and forging procedures for 8 pct Cr steel rollers are provided.

Numerical Study on Stress Heterogeneity Development in Two-Phase Rocks with Large Rheological Contrast and Implications in the Lower Crust

NASA Astrophysics Data System (ADS)

Xu, Junshan; Zhang, Baohua

2018-03-01

Development of stress heterogeneity in two-phase rocks was investigated via a finite element method at 1000-1200 K and 100 MPa. Two groups of rock models were considered: anorthite-diopside and anorthite-clinopyroxene, with a phase volume ratio of 1:1 in each group and different dislocation creep rates between phases ( 4-8 orders of magnitude). Our numerical results indicate that the stress inside the model can be several times higher than the differential stress applied to the model and stress will tend to concentrate in hard phase, especially near the sharp boundaries with soft phase. Moreover, large stress gradient in hard phase and nearly homogeneous stress in soft phase will lead to the initialization of localized dynamic recrystallization or fracture. These numerical observations suggest that the rheological contrast between two phases plays a crucial role in stress heterogeneity rather than other factors (such as grain size, the boundary conditions or mesh density), which may eventually accelerate development of stress heterogeneity in the lower crust. Our study provides new insights into the dynamic processes of grain size reduction in the lower crust, which may cause the transformation from dislocation creep to diffusion creep and enable the weakened shear zones.

Fundamental Studies on High Temperature Deformation, Recrystallization, and Grain Growth of Two-Phase Materials.

DTIC Science & Technology

1987-02-18

17 ml) Benzalkonium Chloride (50%) 4 35 ml Ethanol The Ti-V alloys were etched with the following ethant for about 10 sec. 4% HNO 3 2% HF Bal. H 0 2...that in the last *step all the alloys were processed in the ax+ 6 field from 973 0K L 0 (700 C). The amount of work given in this step (60% reduction in...interfaces (29). The interfaces move by random jumping of atoms from grain to grain, the driving force for the process being the reduction of free

Processing and Characterization of NiTi Shape Memory Alloy Particle Reinforced Sn-In Solders

DTIC Science & Technology

2006-12-01

solders generally operate at a high homologous temperature. Thermally induced grain growth, mechanical stress-induced grain growth and recrystallization ...the number of I/O connects available for flip chip as compared to the wirebond chip For interconnection and packaging, Pb-Sn and eutectic 63Sn...lower melting point is desired. The maximum use temperature for this alloy is around 120°C due to the fact that the eutectic reaction happened at

Deformation and annealing response of TD-nickel chromium

NASA Technical Reports Server (NTRS)

Kane, R. D.; Ebert, L. J.

1975-01-01

The recrystallization and grain growth processes occurring in TD-NiCr were examined with respect to deformation severity, annealing time, and temperature. Results indicated that two different annealing responses of TD-NiCr are possible, depending on the initial state and processing history prior to annealing. As-received sheet showed a dramatic increase in grain size with decreasing annealing temperature, whereas sheet prior-annealed at 1316 C for 1 hr exhibited very little variation with subsequent annealing temperature.

Influence of hydration and annealing on structure, PSL yield and spatial resolution of pressed powder imaging plates of the X-ray storage phosphor CsBr:Eu2+

NASA Astrophysics Data System (ADS)

Kersting, E.; von Seggern, H.

2017-08-01

A new production route for europium doped cesium bromide (CsBr:Eu2+) imaging plates has been developed, synthesizing CsBr:Eu2+ powder from a precipitation reaction of aqueous CsBr solution with ethanol. This new route allows the control of features like homogeneous grain size and grain shape of the obtained powder. After drying and subsequent compacting the powder, disk-like samples were fabricated, and their resulting photostimulated luminescence (PSL) properties like yield and spatial resolution were determined. It will be shown that hydration of such disks causes the CsBr:Eu2+ powder to recrystallize starting from the humidity exposed surfaces to the sample interior up to a completely polycrystalline sample resulting in a decreasing PSL yield and an increasing resolution. Subsequent annealing leads to grain refinement combined with a large PSL yield increment and a minor effect on the spatial resolution. By first annealing the "as made" disk, one observes a strong increment of the PSL yield and almost no effect on the spatial resolution. During subsequent hydration, the recrystallization is hindered by minor structural changes of the grains. The related PSL yield drops slightly with increasing hydration time, and the spatial resolution drops considerably. The obtained PSL properties with respect to structure will be discussed with a simple model.

Structure and phase composition of ultrafine-grained TiNb alloy after high-temperature annealings

NASA Astrophysics Data System (ADS)

Eroshenko, Anna Yu.; Glukhov, Ivan A.; Mairambekova, Aikol; Tolmachev, Alexey I.; Sharkeev, Yurii P.

2017-12-01

The paper presents the experimental data observed in the microstructure and phase composition of ultrafine-grained Ti-40 mass % Nb (Ti40Nb) alloy after high-temperature annealings. The ultrafine-grained Ti40Nb alloy is produced by severe plastic deformation (SPD). This method includes multiple abc-pressing and multi-pass rolling followed by further pre-recrystallizing annealing which, in its turn, enhances the formation of ultrafine-grained structures with mean size of 0.28 µm involving stable β- and α-phase and metastable nanosized ω-phase in the alloy. It is shown that annealing at 500°C preserves the ultrafine-grained structure and phase composition. In cases of annealing at 800°C the ultrafine-grained state transforms into the coarse-grained state. The stable β-phase and the nanosized metastable ω-phase have been identified in the coarse-grained structure.

Microstructure Evolution During Creep of Cold Worked Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Krishan Yadav, Hari; Ballal, A. R.; Thawre, M. M.; Vijayanand, V. D.

2018-04-01

The 14Cr–15Ni austenitic stainless steel (SS) with additions of Ti, Si, and P has been developed for their superior creep strength and better resistance to void swelling during service as nuclear fuel clad and wrapper material. Cold working induces defects such as dislocations that interact with point defects generated by neutron irradiation and facilitates recombination to make the material more resistant to void swelling. In present investigation, creep properties of the SS in mill annealed condition (CW0) and 40 % cold worked (CW4) condition were studied. D9I stainless steel was solution treated at 1333 K for 30 minutes followed by cold rolling. Uniaxial creep tests were performed at 973 K for various stress levels ranging from 175-225 MPa. CW4 samples exhibited better creep resistance as compared to CW0 samples. During creep exposure, cold worked material exhibited phenomena of recovery and recrystallization wherein new strain free grains were observed with lesser dislocation network. In contrast CW0 samples showed no signs of recovery and recrystallization after creep exposure. Partial recrystallization on creep exposure led to higher drop in hardness in cold worked sample as compared to that in mill annealed sample. Accelerated precipitation of carbides at the grain boundaries was observed during creep exposure and this phenomenon was more pronounced in cold worked sample.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Zhangwei; Baker, Ian; Guo, Wei

We investigated the effects of cold rolling followed by annealing on the mechanical properties and dislocation substructure evolution of undoped and 1.1 at. % carbon-doped Fe 40.4Ni 11.3Mn 34.8Al 7.5Cr 6 high entropy alloys (HEAs). X-ray diffraction, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atom probe tomography (APT) were employed to characterize the microstructures. The as-cast HEAs were coarse-grained and single phase f.c.c., whereas the thermo-mechanical treatment caused recrystallization (to fine grain sizes) and precipitation (a B2 phase for the undoped HEA; and a B2 phase, and M 23C 6 and M 7C 3 carbides for the C-dopedmore » HEA). Carbon, which was found to have segregated to the grain boundaries using APT, retarded recrystallization. The reduction in grain size resulted in a sharp increase in strength, while the precipitation, which produced only a small increase in strength, probably accounted for the small decrease in ductility for both undoped and C-doped HEAs. For both undoped and C-doped HEAs, the smaller grain-sized material initially exhibited higher strain hardening than the coarse-grained material but showed a much lower strain hardening at large tensile strains. Wavy slip in the undoped HEAs and planar slip in C-doped HEAs were found at the early stages of deformation irrespective of grain size. At higher strains, dislocation cell structures formed in the 19 μm grain-sized undoped HEA, while microbands formed in the 23 μm grain-sized C-doped HEA. Conversely, localized dislocation clusters were found in both HEAs at the finest grain sizes (5 μm). The inhibition of grain subdivision by the grain boundaries and precipitates lead to the transformation from regular dislocation configurations consisting of dislocation-cells and microbands to irregular dislocation configurations consisting of localized dislocation clusters, which further account for the decrease in ductility. Our investigation of the formation mechanism and strain hardening of dislocation cells and microbands could benefit future structural material design.« less

Evidence of sealing and brine distribution at grain boundaries in natural fine-grained Halite (Qum Kuh salt fountain, Central Iran): implications for rheology of salt extrusions

NASA Astrophysics Data System (ADS)

Desbois, Guillaume; Urai, Janos L.; de Bresser, J. H. P.

2010-05-01

When grain boundary movement is stopped, surface energy related forces reassert themselves driving the system to its equilibrium conditions ([2], [6], [7], [8]). This could result in growth of islands and shrinking of channels and hence in healing the boundary by internal redistribution of fluid and solid in the contact region. Such islands are proposed to grow preferentially close to the contact rim and promote the healing of the grain-grain contact, which in turn prevents transport in or out the boundary region and thus traps the fluids in isolated inclusions. This contribution is focused on observation of grain boundary microstructures in natural mylonitic rocksalt collected from the distal part of Kum-Quh salt fountain (central Iran) in order to give unprecedented insight of grain boundary microstructures using argon-beam cross-sectioning to prepare high quality polished surfaces suitable for high-resolution SEM imaging. The possibility to use our SEM under cryogenic conditions allows also imaging the in-situ distribution of fluids. Results show that brine at grain boundaries occurs as thick layers (> µm in scale) corresponding to cross-sectioned wetted triple junction tubes, as filling at triple junction and as array of isolated fluids inclusions at grain-grain contacts. Close observations at islands contacts suggest the presence of a very thin fluid film (<100 nm). The most remarkable is evidence for sealing of pore space appearing as subhedral crystals filling the void space and decoupled from surrounding crystals by a thin brine layer. In parallel to this microstructural study, we deformed the same samples in order to simulate the simple shear flow at very low mean stress as in the salt fountain. First results suggest a complicated rheology. Samples loaded at σ < 0.7 MPa show no measurable deformation in a month, indicating strain rates less than 10-12 s-1 though, in fully activated pressure-solution (PS) creep, strain rates of several orders of magnitude are expected for similar grain size ([5]). Other samples, which were loaded to 1 MPa before reducing the stress to 0.5 MPa deformed at much higher but variable rates, up to 10-8 s-1, in good agreement with activated PS creep. If, at first look, our pilot deformation experiments seem to reflect a kind of "yield stress" for activation PS creep ([7]); the experimental stress does not reach the theoritical condition to enable activation of PS. Thus, we interpret that the apparent "yielding stress" may not reflect strictu senso the "yielding stress" as described in [7] but rather to a "yielding stress" corresponding to the elastic reassessment of the grain system before the initiation of PS at privileged seal-brine-grain contacts. In salt fountain conditions, mylonitic samples are expected to be in the healing domain, but "jumps" in active stress required to activate PS creep is hardly probable. Thus, we suggest that rainwater influx plays a fundamental role in activation of PS. Rainwater should enable the marginal dissolution of healed contacts and then decreases in the area fraction of grain boundary occupied by solid island contact causing an increase in island stress. Therefore, this points to cyclic deformation of salt fountain: (1) during rainy periods the fountain will deformed at relative high strain rate by dominant PS; while (2) during dry seasons, it will not significantly flow because the grain boundary healing will prevent PS and lead to dominant dislocation creep. This interpretation is in good agreement with recent structural studies ([1], [4]), which gives evidence for both dynamic dislocation and pressure-solution creeps, and measurement of rapid flow after rainy periods with flow rates compatible with fully activated PS ([3]). [1] Desbois G., Zavada P., Schleder Z. and Urai J.L. (In review). Deformation and recrystallization mechanisms in naturally deformed salt fountain: microstructural evidence for a switch in deformation mechanisms with increased availability of meteoric water and decreased grain size (Qum Kuh, central Iran). Submitted to Journal of Structural Geology. [2] Ghoussoub J., and Leroy Y.M. (2001), Solid-fluid phase transformation within grain boundaries during compaction by pressure solution, J. Mech. Phys. Solids, 49, 737 2385-2430. 738 [3] Jackson, M.P.A., (1985). Natural strain in diapiric and glacial rock salt, with emphasis on Oakwood dome, East Texas, Bureau of Economic Geology, The University of Texas at Austin, Texas. [4] Schléder Z. and Urai J.L. (2007). Deformation and recrystallization mechanisms in mylonitic shear zones in naturally deformed extrusive Eocene-Oligocene rock salt from Eyvanekey plateau and Garmsar hills (central Iran). Journal of structural geology, 29, 241-255. [5] Spiers C.J. and Carter N.L. (1988). Microphysics of rock salt flow in nature. In: M. Aubertin and H.R. Hardy, Editors, The Mechanical Behaviour of Salt: Proceedings of the Fourth Conference Series on Rock and Soil Mechanics, TTP Trans Tech Publications, Clausthal-Zellerfeld, 22: 115-128. [6] Urai J. L. (1983). Water assisted dynamic recrystallization and weakening in polycrystalline bischofite. Tectonophysics 96 (1-2): 125-157. [7] Van Noort R., Visser H.J.M., Spiers C.J. (2008) Influence of grain boundary structure on dissolution controlled pressure solution and retarding effects of grain boundary healing. Journal of Geophysical Research, 113, B03201. [8] Visser, H. J. M. (1999). Mass transfer processes in crystalline aggregates containing a fluid phase, Ph. D. thesis, Utrecht University, Utrecht.

Tensile behavior of the L(1)2 compound Al67Ti25Cr8

NASA Technical Reports Server (NTRS)

Kumar, K. S.; Brown, S. A.

1992-01-01

Temperature-related variations in tensile yield strength and ductility were studied on cast, homogenized and isothermally forged Al67Ti25Cr8. Yield strength dropped discontinuously between 623 K and 773 K and then decreased gradually with increasing temperature. Below 623 K, fracture occurred prior to macroscopic yielding. Ductility decreased from 0.2 percent at 623 K to zero at 773 K, but increased again at higher temperatures. At 1073 K, an elongation of 19 percent was obtainable, and ultimate tensile strength and localized necking were observed. Fracture surfaces and deformed microstructures were examined. The 1073 K tensile specimen that exhibited 19 percent elongation showed grain boundary serrations and some evidence of recrystallization (likely dynamic) although fracture occurred predominantly via an intergranular mode.

A model to describe the surface gradient-nanograin formation and property of friction stir processed laser Co-Cr-Ni-Mo alloy

NASA Astrophysics Data System (ADS)

Li, Ruidi; Yuan, Tiechui; Qiu, Zili

2014-07-01

A gradient-nanograin surface layer of Co-base alloy was prepared by friction stir processing (FSP) of laser-clad coating in this work. However, it is lack of a quantitatively function relationship between grain refinement and FSP conditions. Based on this, an analytic model is derived for the correlations between carbide size, hardness and rotary speed, layer depth during in-situ FSP of laser-clad Co-Cr-Ni-Mo alloy. The model is based on the principle of typical plastic flow in friction welding and dynamic recrystallization. The FSP experiment for modification of laser-clad Co-based alloy was conducted and its gradient nanograin and hardness were characterized. It shows that the model is consistent with experimental results.

Effects of the Strain Rate and Temperature on the Microstructural Evolution of Twin-Rolled Cast Wrought AZ31B Alloys Sheets

NASA Astrophysics Data System (ADS)

Rodriguez, A. K.; Kridli, G.; Ayoub, G.; Zbib, H.

2013-10-01

This article investigates the effects of the strain rate and temperature on the microstructural evolution of twin-rolled cast wrought AZ31B sheets. This was achieved through static heating and through tensile test performed at strain rates from 10-4 to 10-1 s-1 and temperatures between room temperature (RT) and 300 °C. While brittle fracture with high stresses and limited elongation was observed at the RT, ductile behavior was obtained at higher temperatures with low strain rates. The strain rate sensitivity and activation energy calculations indicate that grain boundary diffusion and lattice diffusion are the two rate-controlling mechanisms at warm and high temperatures, respectively. An analysis of the evolution of the microstructure provided some indications of the most probable deformation mechanisms in the material: twinning operates at lower temperatures, and dynamic recrystallization dominates at higher temperatures. The static evolution of the microstructure was also studied, proving a gradual static grain growth of the AZ31B with annealing temperature and time.

Mechanism of Martensitic to Equiaxed Microstructure Evolution during Hot Deformation of a Near-Alpha Ti Alloy

NASA Astrophysics Data System (ADS)

Shams, Seyed Amir Arsalan; Mirdamadi, Shamsoddin; Abbasi, Seyed Mahdi; Kim, Daehwan; Lee, Chong Soo

2017-06-01

In this study, mechanisms of microstructural evolution during hot deformation of Ti-1100 were investigated by EBSD analysis. Misorientation angle distribution of initial microstructure showed that diffusionless martensitic phase transformation in Ti-1100 obeys Burgers orientation relationship, and most of the high-angle-grain boundaries consist of angles of 60 and 63 deg. Calculated activation energy of hot deformation ( 338 kJ/mol) and EBSD grain boundary maps revealed that continuous dynamic recrystallization (CDRX) is the dominant mechanism during hot compression at 1073 K (800 °C) and strain rate of 0.005 s-1. At a temperature range of 1073 K to 1173 K (800 °C to 900 °C), not only the array of variants lying perpendicular to compression axis but also CDRX contributes to flow softening. Increasing the rolling temperature from 1123 K to 1273 K (850 °C to 1000 °C) brought about changes in spheroidization mechanism from CDRX to conventional boundary splitting and termination migration correlated with the higher volume fraction of beta phase at higher temperatures.

Physical nature of surface structure degradation in long term operated rails

NASA Astrophysics Data System (ADS)

Gromov, V. E.; Yuriev, A. A.; Peregudov, O. A.; Konovalov, S. V.; Ivanov, Yu. F.; Glezer, A. M.; Semin, A. P.

2017-12-01

Here we present research data on the structural-phase state and surface properties of rails after long-term operation with a transported tonnage of gross weight 500 and 1000 mln tons. Using optical, scanning, and transmission electron diffraction microscopy, and measurements of microhardness and tribological parameters, it is shown that the wear rate of the material after transport of 500 and 1000 mln tons increases 3 and 3.4 times, respectively, and the friction coefficient decreases 1.4 and 1.1 times. After transport of 500 mln tons, complete failure of cementite plates occurs resulting in round cementite particles of size 10-50 nm. After transport of 1000 mln tons, dynamic recrystallization develops in the material. Two competitive mechanisms are suggested for such evolution: (1) decomposition of cementite particles with their transfer to the volume of ferrite grains or plates in pearlite and (2) decomposition and dissolution of cementite particles, transition of carbon atoms to dislocations (to Cottrell atmospheres), transfer of carbon atoms by dislocations to the volume of ferrite grains or plates, and formation of nano-sized cementite particles.

Serial Sectioning Methods for Generating 3D Characterization Data of Grain- and Precipitate-Scale Microstructures (Preprint)

DTIC Science & Technology

2010-04-01

Nielsen SF, Gundlach C, Margulies L, Huang X, Juul Jensen D (2004) Watch- ing the Growth of Bulk Grains During Recrystallization of Deformed Metals. Science...solid-solution dendrites, while the voids in the reconstruction correspond to the Pb-Sn eutectic phase (B) 3D reconstruction of an Al-Cu alloy after...a 3 week coarsening experiment. The solid corresponds to Al dendrites, while the voids in the reconstruction correspond to the Al-Cu eutectic phase

The influence of surface friction on the AA2024 microstructure

NASA Astrophysics Data System (ADS)

Eliseev, A. A.; Kolubaev, E. A.; Fortuna, S. V.

2017-12-01

This work is devoted to the study of the effect of sliding at velocities close to those achieved during friction stir welding or friction drilling on the microstructural evolution of 2024 aluminum alloy. The distribution of both solid solution grains and intermetallic precipitates is analyzed. No layers of recrystallized grains depleted by precipitates, which is a common finding in FSW or friction drilling, are found below the worn surface independently of the sliding velocity. A small precipitate content and size changes alone are observed.

Influence of aerothermoacoustic treatment on the structure and the properties of a TS6 titanium alloy

NASA Astrophysics Data System (ADS)

Remshev, E. Yu.; Danilin, G. A.; Vorob'eva, G. A.; Kuznetsov, V. V.

2017-01-01

The influence of standard heat or aerothermoacoustic treatment on the structure and the properties of a TS6 titanium alloy is considered. The interrelation between variations in the structure, the grain size, and the properties of the alloy has been detected. The possibilities of aerothermoacoustic treatment to provide a simultaneous increase in the strength and the plasticity of a TS6 alloy upon refining of its grain structure in the course of microplastic deformation and recrystallization are demonstrated.

On the role of grain boundary character distribution in grain growth of Al-Mg alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Matsumoto, K.; Shibayanagi, T.; Umakoshi, Y.

1997-02-01

Grain growth behavior of recrystallized Al-Mg alloys containing 0.3 and 2.7 mass% Mg was investigated, focusing on the interconnection between development of the texture and grain boundary character distribution. An Al-0.3 mass% Mg alloy showed two stages in the change of microstructure during grain growth: the frequency of cube oriented grains and the {Sigma}1 boundary significantly increased at an early stage and then decreased. In the second stage a small amount of isolated large grains with the non-cube component grew and consumed the surrounding cube grains. In contrast, the frequency of cube oriented grains and the grain boundary character distributionmore » showed no significant change during grain growth of Al-2.7 mass% Mg. Small clusters composed of several cube grains containing {Sigma}1 boundaries were formed and their spatial distribution played an important role in the change of microstructure during grain growth. The effect of the spatial distribution on the grain growth behavior was discussed considering the energy balance at triple junctions of grain boundaries.« less

Characterization of Hot Deformation Behavior of a Fe-Cr-Ni-Mo-N Superaustenitic Stainless Steel Using Dynamic Materials Modeling

NASA Astrophysics Data System (ADS)

Pu, Enxiang; Zheng, Wenjie; Song, Zhigang; Feng, Han; Zhu, Yuliang

2017-03-01

Hot deformation behavior of a Fe-24Cr-22Ni-7Mo-0.5N superaustenitic stainless steel was investigated by hot compression tests in a wide temperature range of 950-1250 °C and strain rate range of 0.001-10 s-1. The flow curves show that the flow stress decreases as the deformation temperature increases or the strain rate decreases. The processing maps developed on the basis of the dynamic materials model and flow stress data were adopted to optimize the parameters of hot working. It was found that the strain higher than 0.2 has no significant effect on the processing maps. The optimum processing conditions were in the temperature range of 1125-1220 °C and strain rate range of 0.1-3 s-1. Comparing to other stable domains, microstructural observations in this domain revealed the complete dynamic recrystallization (DRX) with finer and more uniform grain size. Flow instability occurred in the domain of temperature lower than 1100 °C and strain rate higher than 0.1 s-1.

Microstructure and Tensile Properties of Friction Stir Processed Mg–Sn–Zn Alloy

PubMed Central

Chen, Xiaoyang; Dai, Qiao; Li, Xingcheng; Lu, Yalin; Zhang, Yang

2018-01-01

In this study, as-cast Mg–6Sn–2Zn (wt.%) alloy was subjected to friction stir processing (FSP) and the microstructure and tensile properties of FSP Mg–6Sn–2Zn samples were investigated. It was found that, in the stir zone (SZ) of FSP Mg–6Sn–2Zn samples, α-Mg grains were significantly refined via dynamic recrystallization (DRX) and the Mg2Sn phase was broken and partially dissolved. The microstructure in SZ was nonuniform and DRXed grains in the SZ-up regions were coarser than those in the SZ-down regions. Coarse broken Mg2Sn particles were observed in the SZ-up regions, while only fine Mg2Sn particles were observed in the SZ-down regions. Strong {0001} basal texture developed in the SZ regions of Mg–6Sn–2Zn samples after FSP. The increase of travel speed had little effect on the texture of different SZ regions. The ductility of FSP Mg–6Sn–2Zn samples was obviously improved, while the improvement in strength was negligible when compared to the as-cast sample. The tensile properties of FSP Mg–6Sn–2Zn samples were influenced by grain refinement, texture modification, and the breaking up and dissolution of the Mg2Sn phase. PMID:29690590

Microstructure and Tensile Properties of Friction Stir Processed Mg⁻Sn⁻Zn Alloy.

PubMed

Chen, Xiaoyang; Dai, Qiao; Li, Xingcheng; Lu, Yalin; Zhang, Yang

2018-04-23

In this study, as-cast Mg⁻6Sn⁻2Zn (wt.%) alloy was subjected to friction stir processing (FSP) and the microstructure and tensile properties of FSP Mg⁻6Sn⁻2Zn samples were investigated. It was found that, in the stir zone (SZ) of FSP Mg⁻6Sn⁻2Zn samples, α-Mg grains were significantly refined via dynamic recrystallization (DRX) and the Mg₂Sn phase was broken and partially dissolved. The microstructure in SZ was nonuniform and DRXed grains in the SZ-up regions were coarser than those in the SZ-down regions. Coarse broken Mg₂Sn particles were observed in the SZ-up regions, while only fine Mg₂Sn particles were observed in the SZ-down regions. Strong {0001} basal texture developed in the SZ regions of Mg⁻6Sn⁻2Zn samples after FSP. The increase of travel speed had little effect on the texture of different SZ regions. The ductility of FSP Mg⁻6Sn⁻2Zn samples was obviously improved, while the improvement in strength was negligible when compared to the as-cast sample. The tensile properties of FSP Mg⁻6Sn⁻2Zn samples were influenced by grain refinement, texture modification, and the breaking up and dissolution of the Mg₂Sn phase.

Effect of Extrusion Temperature on the Plastic Deformation of an Mg-Y-Zn Alloy Containing LPSO Phase Using In Situ Neutron Diffraction

NASA Astrophysics Data System (ADS)

Garces, G.; Perez, P.; Cabeza, S.; Kabra, S.; Gan, W.; Adeva, P.

2017-11-01

The evolution of the internal strains during in situ tension and compression tests has been measured in an MgY2Zn1 alloy containing long-period stacking ordered (LPSO) phase using neutron diffraction. The alloy was extruded at two different temperatures to study the influence of the microstructure and texture of the magnesium and the LPSO phases on the deformation mechanisms. The alloy extruded at 623 K (350 °C) exhibits a strong fiber texture with the basal plane parallel to the extrusion direction due to the presence of areas of coarse non-recrystallised grains. However, at 723 K (450 °C), the magnesium phase is fully recrystallised with grains randomly oriented. On the other hand, at the two extrusion temperatures, the LPSO phase orients their basal plane parallel to the extrusion direction. Yield stress is always slightly higher in compression than in tension. Independently on the stress sign and the extrusion temperature, the beginning of plasticity is controlled by the activation of the basal slip system in the dynamic recrystallized grains. Therefore, the elongated fiber-shaped LPSO phase which behaves as the reinforcement in a metal matrix composite is responsible for this tension-compression asymmetry.

Strength of Rocks Affected by Deformation Enhanced Grain Growth

NASA Astrophysics Data System (ADS)

Kellermann Slotemaker, A.; de Bresser, H.; Spiers, C.

2005-12-01

One way of looking into the possibility of long-term strength changes in the lithosphere is to study transient effects resulting from modifications of the microstructure of rocks. It is generally accepted that mechanical weakening may occur due to progressive grain size refinement resulting from dynamic recrystallization. A decrease in grain size may induce a switch from creep controlled by grain size insensitive dislocation mechanisms to creep governed by grain size sensitive (GSS) mechanisms involving diffusion and grain boundary sliding processes. This switch forms a well-known scenario to explain localization in the lithosphere. However, fine-grained rocks in localized deformation zones are prone to grain coarsening due to surface energy driven grain boundary migration (SED-GBM). This might harden the rock, affecting its role in localizing strain in the long term. The question has arisen if grain growth by SED-GBM in a rock deforming in the GSS creep field can be significantly affected by strain. The broad aim of this study is to shed more light onto this. We have experimentally investigated the microstructural and strength evolution of fine-grained (~0.6 μm) synthetic forsterite and Fe-bearing olivine aggregates that coarsen in grain size while deforming by GSS creep at elevated pressure (600 MPa) and temperature (850-1000 °C). The materials were prepared by `sol-gel' method and contained 0.3-0.5 wt% water and 5-10 vol% enstatite. We performed i) static heat treatment tests of various time durations involving hot isostatic pressing (HIP), and ii) heat treatment tests starting with HIP and continuing with deformation up to 45% axial strain at strain rates in the range 4x10-7 - 1x10-4 s-1. Microstructures were characterized by analyzing full grain size distributions and textures using SEM/EBSD. In addition to the experiments, we studied microstructural evolution in simple two-dimensional numerical models, combining deformation and SED-GBM by means of the modeling package ELLE. Synthetic olivine samples that were heat treated without straining showed only minor grain growth. Presumably, the second phase (enstatite) and/or porosity remaining in the starting material after densification slowed down or inhibited SED-GBM in the static situation. In contrast, samples heat treated and deformed for time durations similar to those of the static tests demonstrated, at identical temperature, an increase in grain size with increasing strain up to a value twice that of the static counterpart. This grain coarsening was associated with continuous hardening of the material, witnessed by the stress-strain curves. A random lattice preferred orientation combined with a low stress sensitivity (n~2) suggested dominant GSS creep controlled by grain boundary sliding. A dynamic grain growth model involving an increase in the fraction of non-hexagonal grains, related to grain neighbor switching, appears applicable to the observed grain growth that is held responsible for the hardening. The ELLE numerical modeling demonstrated that a combination of SED-GBM and geometrical deformation of a 2D grain aggregate can indeed result in enhanced grain growth compared to static grain growth tests. The fraction of non-hexagonal grains was found to remain more or less constant during static grain growth but increased during deformation. We suggest that the application of the dynamic grain growth model to the long-term microstructural evolution of fine-grained lithospheric shear zones can further improve our understanding of the transient or permanent character of strain localizations and related rheological behavior.

Effect of Initial Microstructure on the Microstructural Evolution and Joint Efficiency of a WE43 Alloy During Friction Stir Welding

DTIC Science & Technology

2013-04-01

to maximize joint efficiency. 15. SUBJECT TERMS friction stir welding, strain rate, dynamic recrystallization , joint efficiency, stir zone (SZ...stir welding, Strain rate, Dynamic recrystallization , Joint efficiency, Stir Zone (SZ) Abstract The initial microstructure plays an important role in... eutectic Mg17Al12 phase. Park et al. [7] demonstrated the importance of texture and related it to the mechanical properties of an AZ61 alloy

Development of the Microstructure Based Stochastic Life Prediction Models

DTIC Science & Technology

1991-06-27

sizes and shapes of the recrystallized and unrecrystallized grains and also measure sizes of subgrains. We will also determine the degree of...J. Lankford et al., STP 811, ASTM STP 811. ASTM, 1983. 5. M. R. James and W. L. Morris, "The Role of Microplastic Deformation in Fatigue Crack

Solid State Recrystallization of Single Crystal Ce:LSO Scintillator Crystals for High Resolution Detectors

DTIC Science & Technology

2012-06-01

this report. The property measurements that have been focused on were the assessment of density ( Archimedes ). grain structure {optical and SEM...Scintillator", Materials Letters 60 1960-1963 (2006) [15] J.S. Reed, Forming Processes, Chapter 20 in Introduction to the Principles of Ceramic

Glass-Transition Temperature of the β-Relaxation as the Major Predictive Parameter for Recrystallization of Neat Amorphous Drugs.

PubMed

Kissi, Eric Ofosu; Grohganz, Holger; Löbmann, Korbinian; Ruggiero, Michael T; Zeitler, J Axel; Rades, Thomas

2018-03-15

Recrystallization of amorphous drugs is currently limiting the simple approach to improve solubility and bioavailability of poorly water-soluble drugs by amorphization of a crystalline form of the drug. In view of this, molecular mobility, α-relaxation and β-relaxation processes with the associated transition temperatures T gα and T gβ , was investigated using dynamic mechanical analysis (DMA). The correlation between the transition temperatures and the onset of recrystallization for nine amorphous drugs, stored under dry conditions at a temperature of 296 K, was determined. From the results obtained, T gα does not correlate with the onset of recrystallization under the experimental storage conditions. However, a clear correlation between T gβ and the onset of recrystallization was observed. It is shown that at storage temperature below T gβ , amorphous nifedipine retains its amorphous form. On the basis of the correlation, an empirical correlation is proposed for predicting the onset of recrystallization for drugs stored at 0% RH and 296 K.

Matrix and fine-grained rims in the unequilibrated CO3 chondrite, ALHA77307 - Origins and evidence for diverse, primitive nebular dust components

NASA Technical Reports Server (NTRS)

Brearley, Adrian J.

1993-01-01

SEM, TEM, and electron microprobe analysis were used to investigate in detail the mineralogical and chemical characteristics of dark matrix and fine-grained rims in the unequilibrated CO3 chondrite ALHA77307. Data obtained revealed that there was a remarkable diversity of distinct mineralogical components, which can be identified using their chemical and textural characteristics. The matrix and rim components in ALHA77307 formed by disequilibrium condensation process as fine-grained amorphous dust that is represented by the abundant amorphous component in the matrix. Subsequent thermal processing of this condensate material, in a variety of environments in the nebula, caused partial or complete recrystallization of the fine-grained dust.

Influence of Pulsed Current on Superplasticity of Fine Grained 1420 Al-Li Alloy

NASA Astrophysics Data System (ADS)

Zhang, Yanling; Hou, Hongliang; Bi, Jing; Wang, Yaoqi

2018-01-01

The effects of an externally applied electropulse on the superplastic deformation behavior and microstructure of 1420 Al-Li alloy were studied. The flow stress of superplastic deformation was reduced by the high-density electropulse while the elongation was increased. The optimal electrical parameters for superplastic deformation were 192A/mm2 of current density, 150Hz of frequency and 30s of duration at 480°C and 0.001s-1. The elongation raised by 68% compared to that without electropulse. Furthermore, the grain was refined and the average grain size was reduced after superplastic deformation with the optimal electropulse. It is noted that the electropulse promoted the recrystallization and restrained the grain growth.

Net Shaped Component Fabrication of Refractory Metal Alloys using Vacuum Plasma Spraying

NASA Technical Reports Server (NTRS)

Sen, S.; ODell, S.; Gorti, S.; Litchford, R.

2006-01-01

The vacuum plasma spraying (VPS) technique was employed to produce dense and net shaped components of a new tungsten-rhenium (W-Re) refractory metal alloy. The fine grain size obtained using this technique enhanced the mechanical properties of the alloy at elevated temperatures. The alloy development also included incorporation of thermodynamically stable dispersion phases to pin down grain boundaries at elevated temperatures and thereby circumventing the inherent problem of recrystallization of refractory alloys at elevated temperatures. Requirements for such alloys as related to high temperature space propulsion components will be discussed. Grain size distribution as a function of cooling rate and dispersion phase loading will be presented. Mechanical testing and grain growth results as a function of temperature will also be discussed.

The Influence of Impurities and Metallic Capping Layers on the Microstructure of Copper Interconnects

NASA Astrophysics Data System (ADS)

Rizzolo, Michael

As copper interconnects have scaled to ever smaller dimensions on semiconductor devices, the microstructure has become increasingly detrimental for performance and reliability. Small grains persist in interconnects despite annealing at high temperatures, leading to higher line resistance and more frequent electromigration-induced failures. Conventionally, it was believed that impurities from the electrodeposition pinned grain growth, but limitations in analytical techniques meant the effect was inferred rather than observed. Recent advances in analytical techniques, however, have enabled this work to quantify impurity content, location, and diffusion in relation to microstructural changes in electroplated copper. Surface segregation of impurities during the initial burst of grain growth was investigated. After no surface segregation was observed, a microfluidic plating cell was constructed to plate multilayer films with regions of intentionally high and low impurity concentrations to determine if grain growth could be pinned by the presence of impurities; it was not. An alternate mechanism for grain boundary pinning based on the texture of the seed layer is proposed, supported by time-resolved transmission electron microscopy and transmission electron backscatter diffraction data. The suggested model posits that the seed in narrow features has no preferred orientation, which results in rapid nucleation of subsurface grains in trench regions prior to recrystallization from the overburden down. These rapidly growing grains are able to block off several trenches from the larger overburden grains, inhibiting grain growth in narrow features. With this knowledge in hand, metallic capping layers were employed to address the problematic microstructure in 70nm lines. The capping layers (chromium, nickel, zinc, and tin) were plated on the copper overburden prior to annealing to manipulate the stress gradient and microstructural development during annealing. It appeared that regardless of as-plated stress, nickel capping altered the recrystallized texture of the copper over patterned features. The nickel capping also caused a 2x increase in the number of advantageous 'bamboo' grains that span the entire trench, which effectively block electromigration pathways. These data provides a more fundamental understanding of manipulating the microstructure in copper interconnects using pre-anneal capping layers, and demonstrates a strategy to improve the microstructure beyond the capabilities of simple annealing.

Mineral Replacement Reactions as a Precursor to Strain Localisation: an (HR-)EBSD approach

NASA Astrophysics Data System (ADS)

Gardner, J.; Wheeler, J.; Wallis, D.; Hansen, L. N.; Mariani, E.

2017-12-01

Much remains to be learned about the links between metamorphism and deformation. Our work investigates the behaviour of fluid-mediated mineral replacement reaction products when exposed to subsequent shear stresses. We focus on albite from a metagabbro that has experienced metamorphism and subsequent deformation at greenschist facies, resulting in a reduction in grain size and associated strain localisation. EBSD maps show that prior to grain size reduction, product grains are highly distorted, yet they formed, and subsequently deformed, at temperatures at which extensive dislocation creep is unlikely. The Weighted Burgers Vector can be used to quantitatively describe the types of Burgers vectors present in geometrically necessary dislocation (GND) populations derived from 2-D EBSD map data. Application of this technique to the distorted product grains reveals the prominence of, among others, dislocations with apparent [010] Burgers vectors. This supports (with some caveats) the idea that dislocation creep is not responsible for the observed lattice distortion, as there are no known slip systems in plagioclase with a [010] Burgers vector. Distortion in a replacement microstructure has also been attributed to the presence of nanoscale product grains, which share very similar, but not identical, orientations due to topotactic nucleation from adjacent sites on the same substrate. As a precipitate, the product grains should be expected to be largely free of elastic strain. However, high angular resolution EBSD results demonstrate that product grains contain both elastic strains (> 10-3) and residual stresses (several hundred MPa), as well as GND densities on the order of 1014-1015 m-2. Thus we suggest the observed distortion (elastic strain plus rotations) in the lattice is produced during the mineral replacement reaction by a lattice mismatch and volume change between parent and product. Stored strain energy then provides a driving force for recovery and recrystallization. Recrystallization produces smaller grains with high angle boundaries, reducing the strength of, and allowing deformation to localise in, the albite phase. Grain size reduction in turn facilitates shear deformation to high strains by a grain size sensitive mechanism (fluid-assisted diffusion creep).

Large scale, highly dense nanoholes on metal surfaces by underwater laser assisted hydrogen etching near nanocrystalline boundary

NASA Astrophysics Data System (ADS)

Lin, Dong; Zhang, Martin Yi; Ye, Chang; Liu, Zhikun; Liu, C. Richard; Cheng, Gary J.

2012-03-01

A new method to generate large scale and highly dense nanoholes is presented in this paper. By the pulsed laser irradiation under water, the hydrogen etching is introduced to form high density nanoholes on the surfaces of AISI 4140 steel and Ti. In order to achieve higher nanohole density, laser shock peening (LSP) followed by recrystallization is used for grain refinement. It is found that the nanohole density does not increase until recrystallization of the substructures after laser shock peening. The mechanism of nanohole generation is studied in detail. This method can be also applied to generate nanoholes on other materials with hydrogen etching effect.

Fatigue crack initiation and microcrack propagation in X7091 type aluminum P/M alloys

NASA Astrophysics Data System (ADS)

Hirose, S.; Fine, M. E.

1983-06-01

Fatigu crack initiation in extruded X7091 RSP-P/M aluminum type alloys o°Curs at grain boundaries at both low and high stresses. By a process of elimination this grain boundary embrittlement was attributed to Al2O3 particles formed mainly during atomization and segregated to some grain boundaries. It is not due to the small grain size, to Co2Al9, to η precipitates at grain boundaries, nor to a precipitate free zone. Thermomechanical processing after extrusion of X7091 with 0.8 pct Co was done by Alcoa to produce large recrystallized grains. This resulted in initiation of fatigue cracks at slip bands, and the resistance to initiation of fatigue cracks at low stresses was much greater. Microcrack growth is, however, much faster in the thermomechanically treated samples, as well as in ingot alloys, than in extruded and aged X7091.

Effects of Temperature and Pressure of Hot Isostatic Pressing on the Grain Structure of Powder Metallurgy Superalloy

PubMed Central

Tan, Liming; He, Guoai; Liu, Feng; Li, Yunping; Jiang, Liang

2018-01-01

The microstructure with homogeneously distributed grains and less prior particle boundary (PPB) precipitates is always desired for powder metallurgy superalloys after hot isostatic pressing (HIPping). In this work, we studied the effects of HIPping parameters, temperature and pressure on the grain structure in PM superalloy FGH96, by means of scanning electron microscope (SEM), electron backscatter diffraction (EBSD), transmission electron microscope (TEM) and Time-of-flight secondary ion spectrometry (ToF-SIMS). It was found that temperature and pressure played different roles in controlling PPB precipitation and grain structure during HIPping, the tendency of grain coarsening under high temperature could be inhibited by increasing HIPping pressure which facilitates the recrystallization. In general, relatively high temperature and pressure of HIPping were preferred to obtain an as-HIPped superalloy FGH96 with diminished PPB precipitation and homogeneously refined grains. PMID:29495312

Effects of Temperature and Pressure of Hot Isostatic Pressing on the Grain Structure of Powder Metallurgy Superalloy.

PubMed

Tan, Liming; He, Guoai; Liu, Feng; Li, Yunping; Jiang, Liang

2018-02-24

The microstructure with homogeneously distributed grains and less prior particle boundary (PPB) precipitates is always desired for powder metallurgy superalloys after hot isostatic pressing (HIPping). In this work, we studied the effects of HIPping parameters, temperature and pressure on the grain structure in PM superalloy FGH96, by means of scanning electron microscope (SEM), electron backscatter diffraction (EBSD), transmission electron microscope (TEM) and Time-of-flight secondary ion spectrometry (ToF-SIMS). It was found that temperature and pressure played different roles in controlling PPB precipitation and grain structure during HIPping, the tendency of grain coarsening under high temperature could be inhibited by increasing HIPping pressure which facilitates the recrystallization. In general, relatively high temperature and pressure of HIPping were preferred to obtain an as-HIPped superalloy FGH96 with diminished PPB precipitation and homogeneously refined grains.

Electron backscatter and X-ray diffraction studies on the deformation and annealing textures of austenitic stainless steel 310S

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nezakat, Majid, E-mail: majid.nezakat@usask.ca

We studied the texture evolution of thermo-mechanically processed austenitic stainless steel 310S. This alloy was cold rolled up to 90% reduction in thickness and subsequently annealed at 1050 °C. At the early stages of deformation, strain-induced martensite was formed from deformed austenite. By increasing the deformation level, slip mechanism was found to be insufficient to accommodate higher deformation strains. Our results demonstrated that twinning is the dominant deformation mechanism at higher deformation levels. Results also showed that cold rolling in unidirectional and cross rolling modes results in Goss/Brass and Brass dominant textures in deformed samples, respectively. Similar texture components aremore » observed after annealing. Thus, the annealing texture was greatly affected by texture of the deformed parent phase and martensite did not contribute as it showed an athermal reversion during annealing. Results also showed that when the fraction of martensite exceeds a critical point, its grain boundaries impeded the movement of austenite grain boundaries during annealing. As a result, recrystallization incubation time would increase. This caused an incomplete recrystallization of highly deformed samples, which led to a rational drop in the intensity of the texture components. - Highlights: •Thermo-mechanical processing through different cold rolling modes can induce different textures. •Martensite reversion is athermal during annealing. •Higher fraction of deformation-induced martensite can increase the annealing time required for complete recrystallization. •Annealing texture is mainly influenced by the deformation texture of austenite.« less

The threshold effects of Nd and Ho: YAG laser-induced surface modification on demineralization of dentin surfaces.

PubMed

Kinney, J H; Haupt, D L; Balooch, M; White, J M; Bell, W L; Marshall, S J; Marshall, G W

1996-06-01

Laser irradiation alters the structure of dentin and produces surface layers that give the appearance of being more enamel-like. The laser-modified surface may be more resistant to demineralization; hence, many investigators are proposing continued development of the laser as a possible preventive treatment for caries. The purpose of this study was to explore the morphological changes that occur in dentin when treated at threshold illuminance with two clinically interesting laser wavelengths, and to evaluate the effectiveness of the laser-treated surface at resisting demineralization in an acid-gel solution. The Nd: YAG laser (wavelength 1060 nm) produced significant recrystallization and grain growth of the apatite, without the formation of second phases such as beta-tricalcium phosphate. This recrystallized surface layer showed resistance to demineralization; however, the layer did not provide protection of the underlying dentin from demineralization because of cracks and macroscopic voids that allowed for penetration of the demineralizing gel. The Ho: YAG laser-treated surface (wavelength 2100 nm) did not show significant evidence of recrystallization and grain growth, and only a trace amount of an acid-resistant layer was observed with demineralization. It is speculated that the Ho:YAG laser is coupling with absorbed water, and that the heat transfer from the water to the mineral phase is inefficient. For the purposes of creating a demineralization-resistant layer, threshold illuminance with both Nd: YAG and Ho: YAG was ineffective.

Effect of Heat Treatment Parameters on the Microstructure and Properties of Inconel-625 Superalloy

NASA Astrophysics Data System (ADS)

Sukumaran, Arjun; Gupta, R. K.; Anil Kumar, V.

2017-07-01

Inconel-625 is a solid solution-strengthened alloy used for long-duration applications at high temperatures and moderate stresses. Different heat treatment cycles (temperatures of 625-1025 °C and time of 2-6 h) have been studied to obtain optimum mechanical properties suitable for a specific application. It has been observed that room temperature strength and, hardness decreased and ductility increased with increase in heat treatment temperature. The rate of change of these properties is found to be moderate for the samples heat-treated up to 850 °C, and thereafter, it increases rapidly. It is attributed to the microstructural changes like dissolution of carbides, recrystallization and grain growth. Microstructures are found to be predominantly single-phase austenitic with the presence of fine alloy carbides. The presence of twins is observed in samples heat-treated at lower temperature, which act as nucleation sites for recrystallization at 775 °C. Beyond 850 °C, the role of carbides present in the matrix is subsided by the coarsening of recrystallized grains and finally at 1025 °C, significant dissolution of carbide results in substantial reduction in strength and increase in ductility. Elongation to an extent of >71% has been obtained in sample heat-treated at 1025 °C indicating excellent tendency for cold workability. Failure of heat-treated specimens is found to be mainly due to carbide particle-matrix decohesion which acts as locations for crack initiation.

Deformation Behavior of Ultra-Strong and Ductile Mg-Gd-Y-Zn-Zr Alloy with Bimodal Microstructure

NASA Astrophysics Data System (ADS)

Xu, C.; Fan, G. H.; Nakata, T.; Liang, X.; Chi, Y. Q.; Qiao, X. G.; Cao, G. J.; Zhang, T. T.; Huang, M.; Miao, K. S.; Zheng, M. Y.; Kamado, S.; Xie, H. L.

2018-02-01

An ultra-strong and ductile Mg-8.2Gd-3.8Y-1Zn-0.4Zr (wt pct) alloy was developed by using hot extrusion to modify the microstructure via forced-air cooling and an artificial aging treatment. A superior strength-ductility balance was obtained that had a tensile yield strength of 466 MPa and an elongation to failure of 14.5 pct. The local strain evolution during the in situ testing of the ultra-strong and ductile alloy was quantitatively analyzed with high-resolution electron backscattered diffraction and digital image correlation. The fracture behavior during the tensile test was characterized by synchrotron X-ray tomography along with SEM and STEM observations. The alloy showed a bimodal microstructure, consisting of dynamically recrystallized (DRXed) grains with random orientations and elongated hot-worked grains with < { 10{\\bar{1}}0} > parallel to the extrusion direction. The DRXed grains were deformed by the basal <;a> slip and the hot-worked grains were deformed by the prismatic slip dominantly. The strain evolution analysis indicated that the multilayered structure relaxed the strain localization via strain transfer from the DRXed to the hot-worked regions, which led to the high ductility of the alloy. Precipitation of the γ' on basal planes and the β' phases on the prismatic planes of the α-Mg generated closed volumes, which enhanced the strength by pinning dislocations effectively, and contributed to the high ductility by impeding the propagation of micro-cracks inside the grains. The deformation incompatibility between the hot-worked grains and the arched block-shaped long-period stacking ordered (LPSO) phases induced the crack initiation and propagation, which fractured the alloy.

Texture studies of hot compressed near alpha titanium alloy (IMI 834) at 1000°C with different strain rates

NASA Astrophysics Data System (ADS)

Kodli, B. K.; Saxena, K. K.; Dey, S. R.; Pancholi, V.; Bhattacharjee, A.

2015-04-01

IMI 834 Titanium alloy is a near alpha (hcp) titanium alloy used for high temperature applications with the service temperature up to 600°C. Generally, this alloy is widely used in gas turbine engine applications such as low pressure compressor discs. For these applications, good fatigue and creep properties are required, which have been noticed better in a bimodal microstructure, containing 15-20% volume fraction of primary alpha grains (αp) and remaining bcc beta (β) grains transformed secondary alpha laths (αs). The bimodal microstructure is achieved during processing of IMI 834 in the high temperature α+β region. The major issue of bimodal IMI 834 during utilization is its poor dwell fatigue life time caused by textured macrozones. Textured macrozone is the spatial accumulation of similar oriented grains in the microstructure generated during hot processing in the high temperature α+β region. Textured macrozone can be mitigated by controlling the hot deformation with certain strain rate under stable plastic conditions having β grains undergoing dynamic recrystallization. Hence, a comprehensive study is required to understand the deformation behavior of α and β grains at different strain rates in that region. Hot compression tests up to 5°% strain of the samples are performed with five different strain rates i.e. 10-3 s-1, 10-2 s-1, 10-1 s-1, 1 s-1 and 10 s-1 at 1000°C using Gleeble 3800. The resultant bimodal microstructure and the texture studies of primary alpha grains (αp) and secondary alpha laths (αs) are carried out using scanning electron microscopy (SEM)-electron back scattered diffraction (EBSD) method.

Positron annihilation lifetime study of oxide dispersion strengthened steels

NASA Astrophysics Data System (ADS)

Krsjak, V.; Szaraz, Z.; Hähner, P.

2012-09-01

A comparative positron annihilation lifetime study has been performed on various commercial ferritic and ferritic/martensitic oxide dispersion strengthened (ODS) steels. Both as-extruded and recrystallized materials were investigated. In the materials with recrystallized coarse-grained microstructures, only the positron trapping at small vacancy clusters and yttria nanofeatures was observed. Materials which had not undergone recrystallization treatment clearly showed additional positron trapping which is associated with dislocations. Dislocation densities were calculated from a two-component decomposition of the positron lifetime spectra by assuming the first component to be a superposition of the bulk controlled annihilation rate and the dislocation controlled trapping rate. The second component (which translates into lifetimes of 240-260 ps) was found to be well separated in all those ODS materials. This paper presents the potentialities and limitations of the positron annihilation lifetime spectroscopy, and discusses the results of the experimental determination of the defect concentrations and sensitivity of this technique to the material degradation due to thermally induced precipitation of chromium-rich α' phases.

A Cosserat crystal plasticity and phase field theory for grain boundary migration

NASA Astrophysics Data System (ADS)

Ask, Anna; Forest, Samuel; Appolaire, Benoit; Ammar, Kais; Salman, Oguz Umut

2018-06-01

The microstructure evolution due to thermomechanical treatment of metals can largely be described by viscoplastic deformation, nucleation and grain growth. These processes take place over different length and time scales which present significant challenges when formulating simulation models. In particular, no overall unified field framework exists to model concurrent viscoplastic deformation and recrystallization and grain growth in metal polycrystals. In this work a thermodynamically consistent diffuse interface framework incorporating crystal viscoplasticity and grain boundary migration is elaborated. The Kobayashi-Warren-Carter (KWC) phase field model is extended to incorporate the full mechanical coupling with material and lattice rotations and evolution of dislocation densities. The Cosserat crystal plasticity theory is shown to be the appropriate framework to formulate the coupling between phase field and mechanics with proper distinction between bulk and grain boundary behaviour.

Investigation of olivine and orthopyroxene grain boundaries by atom probe tomography

NASA Astrophysics Data System (ADS)

Krawczynski, M.; Skemer, P. A.; Bachhav, M.; Dong, Y.; Marquis, E. A.

2016-12-01

Accurate chemical analysis at grain boundaries is challenging by traditional microscopic techniques, especially for poor conducting geological samples. Atom probe tomography (APT) is a unique technique that can elucidate chemistry and 3-D distribution of elements within a sample volume at the sub-nanometer length scale. With advances in laser and sample preparation techniques in the last decade, APT is now successfully applied to a wide range of poor conducting materials like metal oxides, ceramics, and biological minerals. In this study, we apply the APT technique to investigate the grain boundary chemistry of orthopyroxene (opx) and olivine. These minerals are the most abundant in the upper mantle and their grain boundaries may be important geochemical reservoirs in Earth. Moreover, physical properties such as grain boundary diffusivity, conductivity, and mobility, are likely influenced by the presence or absence of impurities. Single crystals of opx and olivine grains, separated from a San Carlos xenolith, were deformed at 1 GPa and 1500 K. Plastic deformation promoted dynamic recrystallization, creating new grain boundaries within a chemically homogeneous medium. Needle shaped specimens of opx-opx and olivine-olivine grain boundaries were prepared using standard lift out techniques and a dual beam focused ion beam (FIB). APT analyses were performed in laser mode with laser energy of 50 pJ/pulse, repetition rate of 200 kHz, and detection rate of 1%. A 3-D distribution of elements was reconstructed and 1-D profiles across the grain boundary have been calculated. Fe, Al, and Ca show enrichments at the grain boundaries for both phases, consistent with previous studies that used STEM/EDX or EPMA techniques. Although qualitatively similar, the spatial resolution of the APT method is significantly better than other methods, and our data show that the grain-boundary enrichment of minor elements in both olivine and pyroxene compositions is limited to a region no greater than 2-4 nm thick. These new data place constraints on the thickness of the grain boundary zone with unparalleled precision, allowing more accurate calculation of partition coefficients as well as diffusion coefficients from experimental studies of grain boundary diffusion.

Progressive deformation of ultramafic rocks accompanied with deflection of layered structure and mylonitization culminating into a pseudotachylyte-bearing seismogenic fault - a field evidence of plastic instability

NASA Astrophysics Data System (ADS)

Ueda, T.; Obata, M.

2011-12-01

Plastic instability leading to rupture nucleation and propagetion (e.g. Hobbs et al.1986, Kelemen and Hirth, 2007) is an attractive hypothesis for deep earthquakes but lacked clear field evidences. 1D across-fault shear localization observed in some places (e.g. Jin et al.1998) is not clear if the deformation is directly related with seismicity. We present a clear field evidence of plastic instability as guided by pyroxenite/peridotite layering deflection structure (hereafter called LD structure, see figure) accompanied with mylonitization in spinel(Sp)-peridotite facies (P>~1GPa) in Balmuccia peridotite, Ivrea-Verbano Zone, Italy. The studied area contains abundant PST-bearing faults and N-S trending primary pyroxenite layers. Many faults in the area cut pyroxenite layers, but LD structure is found only in one place presented here. Many PSTs in the area have been (re)crystallized in Sp-peridotite facies, and have typically ultramylonitic texture (Ueda et al., 2008) with some injection veins. The fault with LD structure is situated in a fault system, which has two dominant attitudes with regional N-S extension. The shear strain of LD structure measured on outcrop surface is ~2.0. Near the fault, elongated Opx porphyroclasts (ellipses in figure) oblique to local layering are visible in peridotite. The dominant deformation textures are dynamic recrystallization in peridotite and kinking or undulatory extinction in pyroxenite. The mineral assemblages of the mylonite neoblast in the peridotite and the pyroxenite are Ol+Opx+Cpx+Sp+hornblende(Hbl), Cpx+Opx+Sp, respectively. Hbl typically occur only in neoblast. In the vicinity (several hundreds of micron) of the fault, dolomite(Dol) also occur in equilibrium with the assemblage above. The recrystallized grain sizes are 20-50 microns in peridotite and 10-30 microns in pyroxenite. The rarity of LD structure is consistent with general conception that deformation processes which lead to dynamic rupture initiation ought to be recorded in limited area on a resultant fault surface. The N-S extensional arrangement of the fault system including the fault of LD structure, the depth of PST (re)crystallization and mylonitization, all indicate that the rupture nucleation occurred in extensional tectonics (Souquiere and Fabbri , 2010). The occurrence of Dol in the vicinity of the PST fault suggests that this is the very place where plastic instability accompanied with fluid chemistry evolution (from H2O-rich to CO2-rich, caused by mylonitization and hydration) of Ueda et al. (2008.) had taken place.

Mechanical properties of a Gum-type Ti-Nb-Zr-Fe-O alloy

NASA Astrophysics Data System (ADS)

Nocivin, Anna; Cinca, Ion; Raducanu, Doina; Cojocaru, Vasile Danut; Popovici, Ion Alexandru

2017-08-01

A new Gum-type alloy (Ti-Nb-Zr-Fe-O) in which Fe is used instead of Ta was subjected to a particular thermomechanical processing scheme to assess whether its mechanical characteristics (fine β-grains with high strength and low modulus) render it suitable as a biomedical implant material. After a homogenization treatment followed by cold-rolling with 50% reduction, the specimens were subjected to one of three different recrystallization treatments at 1073, 1173, and 1273 K. The structural and mechanical properties of all of the treated specimens were analyzed. The mechanical characterization included tensile tests, microhardness determinations, and fractography by scanning electron microscopy. The possible deformation mechanisms were discussed using the \\overline {Bo} - \\overline {Md} diagram. By correlating all of the experimental results, we concluded that the most promising processing variant corresponds to recrystallization at 1073 K, which can provide suitable mechanical characteristics for this type of alloys: high yield and ultimate tensile strengths (1038 and 1083 MPa, respectively), a low modulus of elasticity (62 GPa), and fine crystalline grain size (approximately 50 μm).

High-pressure crystallization vs. recrystallization origin of garnet pyroxenite-eclogite within subduction related lithologies

NASA Astrophysics Data System (ADS)

Faryad, S. W.; Jedlicka, R.; Hauzenberger, C.; Racek, M.

2018-03-01

Mafic layers displaying transition between clinopyroxenite and eclogite within peridotite from felsic granulite in the Bohemian Massif (Lower Austria) have been investigated. The mafic-ultramafic bodies shared a common granulite facies metamorphism with its hosting felsic rocks, but they still preserve evidence of eclogite facies metamorphism. The selected mafic layer for this study is represented by garnet with omphacite in the core of coarse-grained clinopyroxene, while fine-grained clinopyroxene in the matrix is diopside. In addition, garnet contains inclusions of omphacite, alkali feldspars, hydrous and other phases with halogens and/or CO2. Textural relations along with compositional zoning in garnet from the clinopyroxenite-eclogite layers favour solid-state recrystallization of the precursor minerals in the inclusions and formation of garnet and omphacite during subduction. Textures and major and trace element distribution in garnet indicate two stages of garnet growth that record eclogite facies and subsequent granulite facies overprint. The possible model explaining the textural and compositional changes of minerals is that the granulite facies overprint occurred after formation and exhumation of the eclogite facies rocks.

Rapid trench initiated recrystallization and stagnation in narrow Cu interconnect lines

DOE Office of Scientific and Technical Information (OSTI.GOV)

O'Brien, Brendan B.; Rizzolo, Michael; Prestowitz, Luke C.

2015-10-26

Understanding and ultimately controlling the self-annealing of Cu in narrow interconnect lines has remained a top priority in order to continue down-scaling of back-end of the line interconnects. Recently, it was hypothesized that a bottom-up microstructural transformation process in narrow interconnect features competes with the surface-initiated overburden transformation. Here, a set of transmission electron microscopy images which captures the grain coarsening process in 48 nm lines in a time resolved manner is presented, supporting such a process. Grain size measurements taken from these images have demonstrated that the Cu microstructural transformation in 48 nm interconnect lines stagnates after only 1.5 h atmore » room temperature. This stubborn metastable structure remains stagnant, even after aggressive elevated temperature anneals, suggesting that a limited internal energy source such as dislocation content is driving the transformation. As indicated by the extremely low defect density found in 48 nm trenches, a rapid recrystallization process driven by annihilation of defects in the trenches appears to give way to a metastable microstructure in the trenches.« less

The effect of carbon on the microstructures, mechanical properties, and deformation mechanisms of thermo-mechanically treated Fe 40.4Ni 11.3Mn 34.8Al 7.5Cr 6 high entropy alloys

DOE PAGES

Wang, Zhangwei; Baker, Ian; Guo, Wei; ...

2017-03-01

We investigated the effects of cold rolling followed by annealing on the mechanical properties and dislocation substructure evolution of undoped and 1.1 at. % carbon-doped Fe 40.4Ni 11.3Mn 34.8Al 7.5Cr 6 high entropy alloys (HEAs). X-ray diffraction, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atom probe tomography (APT) were employed to characterize the microstructures. The as-cast HEAs were coarse-grained and single phase f.c.c., whereas the thermo-mechanical treatment caused recrystallization (to fine grain sizes) and precipitation (a B2 phase for the undoped HEA; and a B2 phase, and M 23C 6 and M 7C 3 carbides for the C-dopedmore » HEA). Carbon, which was found to have segregated to the grain boundaries using APT, retarded recrystallization. The reduction in grain size resulted in a sharp increase in strength, while the precipitation, which produced only a small increase in strength, probably accounted for the small decrease in ductility for both undoped and C-doped HEAs. For both undoped and C-doped HEAs, the smaller grain-sized material initially exhibited higher strain hardening than the coarse-grained material but showed a much lower strain hardening at large tensile strains. Wavy slip in the undoped HEAs and planar slip in C-doped HEAs were found at the early stages of deformation irrespective of grain size. At higher strains, dislocation cell structures formed in the 19 μm grain-sized undoped HEA, while microbands formed in the 23 μm grain-sized C-doped HEA. Conversely, localized dislocation clusters were found in both HEAs at the finest grain sizes (5 μm). The inhibition of grain subdivision by the grain boundaries and precipitates lead to the transformation from regular dislocation configurations consisting of dislocation-cells and microbands to irregular dislocation configurations consisting of localized dislocation clusters, which further account for the decrease in ductility. Our investigation of the formation mechanism and strain hardening of dislocation cells and microbands could benefit future structural material design.« less

Effects of hot extrusion and heat treatment on microstructure and properties of industrial large-scale spray-deposited 7055 aluminum alloy

NASA Astrophysics Data System (ADS)

Yang, Yonggang; Zhao, Yutao; Kai, Xizhou; Zhang, Zhen; Zhang, Hao; Tao, Ran; Chen, Gang; Yin, Houshang; Wang, Min

2018-01-01

The industrial large-scale 7055 aluminum alloy fabricated by spray forming technology was subjected to hot extrusion and heat treatment to achieve high strength and ductility. Microstructure of the as-deposited alloy indicates that higher density billets with equiaxed grains (20-40 μm) were fabricated rather than a typical dendritic microstructure of the as-cast alloy. The grains of the as-extruded alloy exhibit fibrous morphology, the original boundaries disappear and fined second phases with size about 0.5-5 μm distribute along with extrusion direction. Meanwhile, the defects could be eliminated by hot extrusion, which resulted in good strength as well as ductility. The ultimate tensile strength, yield strength and elongation of the as-extruded alloy are 345 MPa, 236 MPa and 18.5%, respectively. After heat treatment, the partial recrystallization is observed around the un-recrystallized grains and sub-grains. And the platelet/rod-shaped precipitates (MgZn2) show a uniform distribution in the matrix alloy. The alloy reaches the maximum tensile strength of 730 MPa after T6 temper treatment, associated with a fine precipitation (MgZn2). However, with further deepen aging degree (from T6 to T73 temper), the size of dominant precipitated phases (MgZn2) grows obviously, the grain boundary precipitates transform from continuous to individual ones and the width of precipitate free zone increases. The result shows that the alloy after T7X temper treatment exhibits higher electrical conductivity (>35 %IACS) and facture toughness (>25.6 MPa m1/2) although a 8%-17% reduction in strength compared with that at T6 temper.

A Geothermochronologic Investigation of the Coyote Mountains Metamorphic Core Complex (AZ)

NASA Astrophysics Data System (ADS)

Borel, M.; Gottardi, R.; Casale, G.

2017-12-01

The Coyote Mountains metamorphic core complex (CM-MCC) makes up the northern end of the Baboquivari Mountain complex, which is composed of Mesozoic rocks, Tertiary granites, pegmatites, and metasediments. The CM-MCC expose the Pan Tak granite, a 58 Ma intrusive muscovite-biotite-garnet peraluminous granite. The Pan Tak and other intrusions within the Baboquivari Mountains have been interpreted as anatectic melts representing the culmination of a Laramide crustal shortening orogenic event started in the Late Cretaceous ( 70 Ma). Evidence of this magmatic episode includes polysynthetic twinning in plagioclase, myrmekitic texture in alkali feldspars, and garnet, mica and feldspar assemblages. The magmatic fabric is overprinted by a Tertiary tectonic fabric, associated with the exhumation of the CM-MCC along the Ajo road décollement and associated shear zone. In the shear zone, the Pan Tak mylonite display N-dipping foliation defined by gneissic layering and aligned muscovite, and N-trending mineral stretching lineation. Various shear sense indicators are all consistent with a top-to the-N shear sense. Preliminary argon geochronology results suggest that the shear zone was exhumed 29 Ma ago, an age similar to the onset of detachment faulting in other nearby MCCs (Catalina, Rincon, Pinaleño). In the Pan Tak mylonite, quartz grains display regime 2 to 3 microstructures and shows extensive recrystallization by subgrain rotation and grain boundary migration. The recrystallized grain size ranges between 20 and 50 µm in all samples. Quartz crystallographic preferred orientation measured using electron backscatter diffraction (EBSD) shows that recrystallization was accommodated by dominant prism and minor rhomb slip, suggesting deformation temperature ranging from 450°C to 550°C. These preliminary results constrain the timing of uplift and exhumation, and thermomechanical evolution of the CM-MCC, and improve our understanding of recycling of the continental crust in southern Arizona.

Equal Channel Angular Pressing (ECAP) and Its Application to Grain Refinement of Al-Zn-Mg-Cu Alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tekeli, Sueleyman; Gueral, Ahmet

Microstructure of a metal can be considerably changed by severe plastic deformation techniques such as high pressure torsion, extrusion and equal-channel angular pressing (ECAP). Among these methods, ECAP is particularly attractive because it has a potential for introducing significant grain refinement and homogeneous microstructure into bulk materials. Typically, it reduces the grain size to the submicrometer level or even nanometer range and thus produces materials that are capable of exhibiting unusual mechanical properties. In the present study, a test unites for equal channel angular pressing was constructed and this system was used for Al-Zn-Mg-Cu alloy. After the optimization tests, itmore » was seen that the most effective lubricant for the dies was MoS{sub 2}, the pressing pressure was around 25-35 ton and the pressing speed was 2 mm/s. By using these parameters, the Al-Zn-Mg-Cu alloy was successfully ECAPed up to 14 passes at 200 deg. C using route C. After ECAP tests, the specimens were characterized by transmission electron microscope (TEM), hardness and macrostructural investigations. It was seen that the plastic deformation in the ECAPed specimens occurred from edge to the centre like whirlpool. In addition, the deformation intensity increased with increasing pass number. The grain size of the specimens effectively also decreased with increasing pass number. That is, while the grain size of unECAPed specimen was 10 {mu}m, this value decreased to 300 nm after 14 passes. At the beginning, while there was a banding tendency in the grains toward deformation direction, homogeneous and equiaxed grains were formed with increasing pass number. This grain refinement was as a result of an interaction between shear strain and thermal recovery during ECAP processing. Hardness measurements showed that the hardness values increased up to 4 passes, decreased effectively at 6th pass, again increased at 8th pass and after this pass, the hardness again decreased due to dynamic recrystallization.« less

Semantic modeling of the structural and process entities during plastic deformation of crystals and rocks

NASA Astrophysics Data System (ADS)

Babaie, Hassan; Davarpanah, Armita

2016-04-01

We are semantically modeling the structural and dynamic process components of the plastic deformation of minerals and rocks in the Plastic Deformation Ontology (PDO). Applying the Ontology of Physics in Biology, the PDO classifies the spatial entities that participate in the diverse processes of plastic deformation into the Physical_Plastic_Deformation_Entity and Nonphysical_Plastic_Deformation_Entity classes. The Material_Physical_Plastic_Deformation_Entity class includes things such as microstructures, lattice defects, atoms, liquid, and grain boundaries, and the Immaterial_Physical_Plastic_Deformation_Entity class includes vacancies in crystals and voids along mineral grain boundaries. The objects under the many subclasses of these classes (e.g., crystal, lattice defect, layering) have spatial parts that are related to each other through taxonomic (e.g., Line_Defect isA Lattice_Defect), structural (mereological, e.g., Twin_Plane partOf Twin), spatial-topological (e.g., Vacancy adjacentTo Atom, Fluid locatedAlong Grain_Boundary), and domain specific (e.g., displaces, Fluid crystallizes Dissolved_Ion, Void existsAlong Grain_Boundary) relationships. The dynamic aspect of the plastic deformation is modeled under the dynamical Process_Entity class that subsumes classes such as Recrystallization and Pressure_Solution that define the flow of energy amongst the physical entities. The values of the dynamical state properties of the physical entities (e.g., Chemical_Potential, Temperature, Particle_Velocity) change while they take part in the deformational processes such as Diffusion and Dislocation_Glide. The process entities have temporal parts (phases) that are related to each other through temporal relations such as precedes, isSubprocessOf, and overlaps. The properties of the physical entities, defined under the Physical_Property class, change as they participate in the plastic deformational processes. The properties are categorized into dynamical, constitutive, spatial, temporal, statistical, and thermodynamical. The dynamical properties, categorized under the Dynamical_Rate_Property and Dynamical_State_Property classes, subsume different classes of properties (e.g., Fluid_Flow_Rate, Temperature, Chemical_Potential, Displacement, Electrical_Charge) based on the physical domain (e.g., fluid, heat, chemical, solid, electrical). The properties are related to the objects under the Physical_Entity class through diverse object type (e.g., physicalPropertyOf) and data type (e.g., Fluid_Pressure unit 'MPa') properties. The changes of the dynamical properties of the physical entities, described by the empirical laws (equations) modeled by experimental structural geologists, are modeled through the Physical_Property_Dependency class that subsumes the more specialized constitutive, kinetic, and thermodynamic expressions of the relationships among the dynamic properties. Annotation based on the PDO will make it possible to integrate and reuse experimental plastic deformation data, knowledge, and simulation models, and conduct semantic-based search of the source data originating from different rock testing laboratories.

Effect of upsetting deformation temperature on the formation of the fine-grained cast alloy structure of the Ni-Mn-Ga system

NASA Astrophysics Data System (ADS)

Musabirov, I. I.; Safarov, I. M.; Sharipov, I. Z.; Nagimov, M. I.; Koledov, V. V.; Khovailo, V. V.; Mulyukov, R. R.

2017-08-01

The plastic behavior during deformation by upsetting and its effect on the microstructure in the polycrystalline Ni2.19Fe0.04Mn0.77Ga alloy are studied. The temperatures of martensitic and magnetic phase transformations were determined by the method for analyzing the temperature dependence of the specific magnetization as M F = 320 K, A S = 360 K, and T C = 380 K. Using differential scanning calorimetry, it is shown that the phase transition from the ordered phase L21 to the disordered phase B2 is observed in the alloy during sample heating in the temperature range of 930-1070 K. The melting temperature is 1426 K. An analysis of the load curves constructed for sample deposition at temperatures of 773, 873, and 973 K shows that the behavior of the stress-strain curve at a temperature of 773 K is inherent to cold deformation. The behavior of the dependences for 873 and 973 K is typical of hot deformation. After deforming the alloy, its microstructure is studied using backscattered scanning electron microscopy. Plastic deformation of the alloy at study temperatures results in grain structure fragmentation in the localized deformation region. At all temperatures, a recrystallized grain structure is observed. It is found that the structure is heterogeneously recrystallized after upsetting at 973 K due to the process intensity at such a high temperature. The alloy microstructure after plastic deformation at a temperature of 873 K is most homogeneous in terms of the average grain size.

Rheological stratification of the Hormuz Salt Formation in Iran - microstructural study of the dirty and pure rock salts from the Kuh-e-Namak (Dashti) salt diapir

NASA Astrophysics Data System (ADS)

Závada, Prokop; Desbois, Guillaume; Urai, Janos; Schulmann, Karel; Rahmati, Mahmoud; Lexa, Ondrej; Wollenberg, Uwe

2014-05-01

Significant viscosity contrasts displayed in flow structures of a mountain namakier (Kuh-e-Namak - Dashti), between 'weak' terrestrial debris bearing rock salt types and 'strong' pure rock salt types are questioned for deformation mechanisms using detailed quantitative microstructural study including crystallographic preferred orientation (CPO) mapping of halite grains. While the solid impurity rich ("dirty") rock salts contain disaggregated siltstone and dolomite interlayers, "clean" salts (debris free) reveal microscopic hematite and remnants of abundant fluid inclusions in non-recrystallized cores of porphyroclasts. Although flow in both, the recrystallized dirty and clean salt types is accommodated by combined mechanisms of pressure-solution creep (PS), grain boundary sliding (GBS) and dislocation creep accommodated grain boundary migration (GBM), their viscosity contrasts are explained by significantly slower rates of intergranular diffusion and piling up of dislocations at hematite inclusions in clean salt types. Porphyroclasts of clean salts deform by semi-brittle and plastic mechanisms with intra-crystalline damage being induced also by fluid inclusions that explode in the crystals at high fluid pressures. Boudins of clean salt types with coarse grained and original sedimentary microstructure suggest that clean rock salts are associated with dislocation creep dominated power law flow in the source layer and the diapiric stem. Rheological contrasts between both rock salt classes apply in general for the variegated and terrestrial debris rich ("dirty") Lower Hormuz and the "clean" rock salt forming the Upper Hormuz, respectively, and suggest that large strain rate gradients likely exist along horizons of mobilized salt types of different composition and microstructure.

Effect of Thermal History on Microstructures and Mechanical Properties of AZ31 Magnesium Alloy Prepared by Friction Stir Processing

PubMed Central

Chai, Fang; Zhang, Datong; Li, Yuanyuan

2014-01-01

Hot-rolled AZ31 (Mg-2.57Al-0.84Zn-0.32Mn, in mass percentage) magnesium alloy is subjected to friction stir processing in air (normal friction stir processing, NFSP) and under water (submerged friction stir processing, SFSP). Thermal history of the two FSP procedures is measured, and its effect on microstructures and mechanical properties of the experimental materials is investigated. Compared with NFSP, the peak temperature during SFSP is lower and the duration time at a high temperature is shorter due to the enhanced cooling effect of water. Consequently, SFSP results in further grain refinement, and the average grain size of the NFSP and SFSP specimens in the stir zone (SZ) are 2.9 μm and 1.3 μm, respectively. Transmission electron microscopy (TEM) examinations confirm that grain refinement is attributed to continuous dynamic recrystallization both for NFSP and SFSP. The average Vickers hardness in the SZ of the NFSP and SFSP AZ31 magnesium alloy are 76 HV and 87 HV. Furthermore, the ultimate tensile strength and the elongation of the SFSP specimen increase from 191 MPa and 31.3% in the NFSP specimen to 210 MPa and 50.5%, respectively. Both the NFSP and SFSP alloys fail through ductile fracture, but the dimples are much more obvious in the SFSP alloy. PMID:28788532

Microstructure and Crystallographic Texture Evolution During the Friction-Stir Processing of a Precipitation-Hardenable Aluminum Alloy

NASA Astrophysics Data System (ADS)

Nadammal, Naresh; Kailas, Satish V.; Szpunar, Jerzy; Suwas, Satyam

2015-05-01

Friction-stir processing (FSP) has been proven as a successful method for the grain refinement of high-strength aluminum alloys. The most important attributes of this process are the fine-grain microstructure and characteristic texture, which impart suitable properties in the as-processed material. In the current work, FSP of the precipitation-hardenable aluminum alloy 2219 has been carried out and the consequent evolution of microstructure and texture has been studied. The as-processed materials were characterized using electron back-scattered diffraction, x-ray diffraction, and electron probe microanalysis. Onion-ring formation was observed in the nugget zone, which has been found to be related to the precipitation response and crystallographic texture of the alloy. Texture development in the alloy has been attributed to the combined effect of shear deformation and dynamic recrystallization. The texture was found heterogeneous even within the nugget zone. A microtexture analysis revealed the dominance of shear texture components, with C component at the top of nugget zone and the B and A2* components in the middle and bottom. The bulk texture measurement in the nugget zone revealed a dominant C component. The development of a weaker texture along with the presence of some large particles in the nugget zone indicates particle-stimulated nucleation as the dominant nucleation mechanism during FSP. Grain growth follows the Burke and Turnbull mechanism and geometrical coalescence.

Validation of the Dynamic Recrystallization (DRX) Mechanism for Whisker and Hillock Growth on Sn Thin Films

NASA Astrophysics Data System (ADS)

Vianco, P. T.; Neilsen, M. K.; Rejent, J. A.; Grant, R. P.

2015-10-01

A study was performed to validate a first-principles model for whisker and hillock formation based on the cyclic dynamic recrystallization (DRX) mechanism in conjunction with long-range diffusion. The test specimens were evaporated Sn films on Si having thicknesses of 0.25 μm, 0.50 μm, 1.0 μm, 2.0 μm, and 4.9 μm. Air annealing was performed at 35°C, 60°C, 100°C, 120°C, or 150°C over a time duration of 9 days. The stresses, anelastic strains, and strain rates in the Sn films were predicted by a computational model based upon the constitutive properties of 95.5Sn-3.9Ag-0.6Cu (wt.%) as a surrogate for pure Sn. The cyclic DRX mechanism and, in particular, whether long whiskers or hillocks were formed, was validated by comparing the empirical data against the three hierarchal requirements: (1) DRX to occur at all: ɛc = A D o m Z n , (2) DRX to be cyclic: D o < 2 D r, and (3) Grain boundary pinning (thin films): h versus d. Continuous DRX took place in the 2.0- μm and 4.9- μm films that resulted in short stubby whiskers. Depleted zones, which resulted solely from a tensile stress-driven diffusion mechanism, confirmed the pervasiveness of long-range diffusion so that it did not control whisker or hillock formation other than a small loss of activity by reduced thermal activation at lower temperatures. A first-principles DRX model paves the way to develop like mitigation strategies against long whisker growth.

Detailed Microstructural Characterization and Restoration Mechanisms of Duplex and Superduplex Stainless Steel Friction-Stir-Welded Joints

NASA Astrophysics Data System (ADS)

Santos, T. F. A.; Torres, E. A.; Lippold, J. C.; Ramirez, A. J.

2016-12-01

Duplex stainless steels are successfully used in a wide variety of applications in areas such as the food industry, petrochemical installations, and sea water desalination plants, where high corrosion resistance and high mechanical strength are required. However, during fusion welding operations, there can be changes to the favorable microstructure of these materials that compromise their performance. Friction stir welding with a non-consumable pin enables welded joints to be obtained in the solid state, which avoids typical problems associated with solidification of the molten pool, such as segregation of alloying elements and the formation of solidification and liquefaction cracks. In the case of superduplex stainless steels, use of the technique can avoid unbalanced proportions of ferrite and austenite, formation of deleterious second phases, or growth of ferritic grains in the heat-affected zone. Consolidated joints with full penetration were obtained for 6-mm-thick plates of UNS S32101 and S32205 duplex stainless steels, and S32750 and S32760 superduplex steels. The welding heat cycles employed avoided the conditions required for formation of deleterious phases, except in the case of the welded joint of the S32760 steel, where SEM images indicated the formation of secondary phases, as corroborated by decreased mechanical performance. Analysis using EBSD and transmission electron microscopy revealed continuous dynamic recrystallization by the formation of cellular arrays of dislocations in the ferrite and discontinuous dynamic recrystallization in the austenite. Microtexture evaluation indicated the presence of fibers typical of shear in the thermomechanically affected zone. These fibers were not obviously present in the stir zone, probably due to the intensity of microstructural reformulation to which this region was subjected.

Validation of the dynamic recrystallization (DRX) mechanism for whisker and hillock growth on thin films

DOE PAGES

Vianco, Paul T.; Neilsen, Michael K.; Rejent, Jerome A.; ...

2015-05-01

Our study was performed to validate a first-principles model for whisker and hillock formation based on the cyclic dynamic recrystallization (DRX) mechanism in conjunction with long-range diffusion. The test specimens were evaporated Sn films on Si having thicknesses of 0.25 μm, 0.50 μm, 1.0 μm, 2.0 μm, and 4.9 μm. Air annealing was performed at 35°C, 60°C, 100°C, 120°C, or 150°C over a time duration of 9 days. The stresses, anelastic strains, and strain rates in the Sn films were predicted by a computational model based upon the constitutive properties of 95.5Sn-3.9Ag-0.6Cu (wt.%) as a surrogate for pure Sn. Themore » cyclic DRX mechanism and, in particular, whether long whiskers or hillocks were formed, was validated by comparing the empirical data against the three hierarchal requirements: (1) DRX to occur at all: εc = A D o m Z n , (2) DRX to be cyclic: D o < 2D r, and (3) Grain boundary pinning (thin films): h versus d. Continuous DRX took place in the 2.0-μm and 4.9-μm films that resulted in short stubby whiskers. Depleted zones, which resulted solely from a tensile stress-driven diffusion mechanism, confirmed the pervasiveness of long-range diffusion so that it did not control whisker or hillock formation other than a small loss of activity by reduced thermal activation at lower temperatures. Furthermore, a first-principles DRX model paves the way to develop like mitigation strategies against long whisker growth.« less

Enhanced diffusion welding

NASA Technical Reports Server (NTRS)

Holko, K. H.; Moore, T. J. (Inventor)

1973-01-01

Surfaces of unrecrystallized alloys are sanded and polished. This is followed by a two-step welding process by which the strength of the parent metal is retained at the weld joint. The first step forces the surfaces into intimate contact at a temperature where the metal still has good ductility. The second step causes diffusion, recrystallization, and grain growth across the original weld interface.

Evaluation of Microstructure, Mechanical Properties and Corrosion Resistance of Friction Stir-Welded Aluminum and Magnesium Dissimilar Alloys

NASA Astrophysics Data System (ADS)

Verma, Jagesvar; Taiwade, Ravindra V.; Sapate, Sanjay G.; Patil, Awanikumar P.; Dhoble, Ashwinkumar S.

2017-10-01

Microstructure, mechanical properties and corrosion resistance of dissimilar friction stir-welded aluminum and magnesium alloys were investigated by applying three different rotational speeds at two different travel speeds. Sound joints were obtained in all the conditions. The microstructure was examined by an optical and scanning electron microscope, whereas localized chemical information was studied by energy-dispersive spectroscopy. Stir zone microstructure showed mixed bands of Al and Mg with coarse and fine equiaxed grains. Grain size of stir zone reduced compared to base metals, indicated by dynamic recrystallization. More Al patches were observed in the stir zone as rotational speed increased. X-ray diffraction showed the presence of intermetallics in the stir zone. Higher tensile strength and hardness were obtained at a high rotational speed corresponding to low travel speed. Tensile fractured surface indicated brittle nature of joints. Dissimilar friction stir weld joints showed different behaviors in different corrosive environments, and better corrosion resistance was observed at a high rotational speed corresponding to low travel speed (FW3) in a sulfuric and chloride environments. Increasing travel speed did not significantly affect on microstructure, mechanical properties and corrosion resistance as much as the rotational speed.

Effect of 0.1 wt.% Co on the Hot Deformation and Toughness of Fine-Grained Low-Carbon Steel at Sub-zero Temperatures

NASA Astrophysics Data System (ADS)

Liu, Xiqin; Zhou, Shuangshuang; Liu, Zili; Hou, Zhiguo; Tian, Qingchao

2017-12-01

The effect of 0.1 wt.% Co on the hot deformation behavior of fine-grained low-carbon microalloyed steel was investigated at temperatures of 850-1200 °C and a strain rate of 5 s-1. Furthermore, the toughness of the steel with and without Co at sub-zero temperatures was evaluated. The results suggest that the addition of 0.1 wt.% Co increases the flow stress and delays the occurrence of dynamic recrystallization (DRX) at the same deformation temperature and strain. The DRX fraction of steel specimens without and with 0.1 wt.% Co was about 67.4 and 43.9% at 850 °C, respectively. Then, it increased to 100% at 1100 °C. Compared with steel without Co, cementite particles in the tempered sorbite of steel with 0.1 wt.% Co decreased in size but increased in quantity, yield strength increased from 756 to 787 MPa, and Charpy V-notch energy at - 20 and - 50 °C improved from 69 and 41 to 102 and 65 J, respectively. The fracture morphology and crack propagation characteristics were consistent with the variation in impact energy.

Effect of 0.1 wt.% Co on the Hot Deformation and Toughness of Fine-Grained Low-Carbon Steel at Sub-zero Temperatures

NASA Astrophysics Data System (ADS)

Liu, Xiqin; Zhou, Shuangshuang; Liu, Zili; Hou, Zhiguo; Tian, Qingchao

2018-01-01

The effect of 0.1 wt.% Co on the hot deformation behavior of fine-grained low-carbon microalloyed steel was investigated at temperatures of 850-1200 °C and a strain rate of 5 s-1. Furthermore, the toughness of the steel with and without Co at sub-zero temperatures was evaluated. The results suggest that the addition of 0.1 wt.% Co increases the flow stress and delays the occurrence of dynamic recrystallization (DRX) at the same deformation temperature and strain. The DRX fraction of steel specimens without and with 0.1 wt.% Co was about 67.4 and 43.9% at 850 °C, respectively. Then, it increased to 100% at 1100 °C. Compared with steel without Co, cementite particles in the tempered sorbite of steel with 0.1 wt.% Co decreased in size but increased in quantity, yield strength increased from 756 to 787 MPa, and Charpy V-notch energy at - 20 and - 50 °C improved from 69 and 41 to 102 and 65 J, respectively. The fracture morphology and crack propagation characteristics were consistent with the variation in impact energy.

Role of orthopyroxene in rheological weakening of the lithosphere via dynamic recrystallization

PubMed Central

Farla, Robert J. M.; Karato, Shun-ichiro; Cai, Zhengyu

2013-01-01

For plate tectonics to operate on a terrestrial planet, the surface layer (the lithosphere) must have a modest strength (Earth, ≤200 MPa), but a standard strength profile based on olivine far exceeds this threshold value. Consequently, it is essential to identify mechanisms that reduce the strength of the lithosphere on Earth. Here we report results of high-strain laboratory deformation experiments on a representative olivine–orthopyroxene composition that show the addition of orthopyroxene substantially reduces the strength in the ductile regime within a certain temperature window. The reduction in strength is associated with the formation of small orthopyroxene and olivine grains. Our samples show heterogeneous microstructures similar to those observed in natural peridotites in shear zones: fine-grained regions containing both orthopyroxene and olivine that form interconnected bands where a large fraction of strain is accommodated. A model is developed to apply these results to geological conditions. Such a model, combined with our experimental observations, suggests that orthopyroxene may play a key role in the plastic deformation of the lithosphere in a critical temperature range, leading to long-term weakening associated with strain localization in the lithosphere. PMID:24067645

Microstructural change in electroformed copper liners of shaped charges upon plastic deformation at ultra-high strain rate

NASA Astrophysics Data System (ADS)

Tian, W. H.; Hu, S. L.; Fan, A. L.; Wang, Z.

2002-01-01

Transmission electron microscopy (TEM) observations were carried out for examining the as-formed and post-deformed microstructures in a variety of electroformed copper liners of shaped charges. The deformation was carried out at an ultra-high strain rate. Specifically, the electron backscattering Kikuchi pattern (EBSP) technique was utilized to examine the micro-texture of these materials. TEM observations revealed that these electroformed copper liners of shaped charges have a grain size of about 1-3 mum, EBSP analysis demonstrated that the as-grown copper liners of shaped charges exhibit a l 10) fiber micro-texture which is parallel to the normal direction of the surface of the liners of shaped charges. Having undergone plastic deformation at ultra-high strain rate (10(7) s(-1)), the specimens which were recovered from the copper slugs were found to have grain size of the same order as that before deformation. EBSP analysis revealed that the (110) fiber texture existed in the as-formed copper liners disappears in the course of deformation. TEM examination results indicate that dynamic recovery and recrystallization play a significant role in this deformation process.

Experimental determination of the effects of annealing on the micro-structures and mechanical properties of cold-worked alpha-brass

NASA Astrophysics Data System (ADS)

Edward, Aghogho Bright; Izelu, Christopher

2013-12-01

Experimental determination of the effect of annealing on the microstructure and mechanical properties of a cold work 70 - 30 brass, was carried out by subjecting specimens of the material to various degrees of cold-work (20%, 40% and 60%), by straining using a tensile machine. The specimens for each degree of cold work were then annealed at 250°C, 350°C, 450°C and 600°C, for 30 minutes. The approach involves the use of metallographic techniques: grinding, polishing and etching to reveal the microstructure while tensile test was carried out on the specimen using a Monsanto tensometer so as to obtain the load/extension graph from which the tensile strength and hardness values were obtained. From the results obtained, it was conclusive that annealing produced finer grains and eliminates prior cold work whereby the material becomes ductile. However, there should be an appreciable deformation for this effect to be noticed. One important aspect of re-crystallization in structural materials is that there is a loss of strength which accompanies disappearance of the cold-worked grains when subjected to high temperature applications. Yet, it is often difficult to establish the exact range of permissible temperature. This work establishes a range for the re-crystallization of alpha brass as 350°C < TC < 450°C, where TC is the re-crystallization temperature. Thus, it will be safe to apply this material at temperatures below 350°C, without fear of structural changes with accompanying lost in strength.

Grain refinement and texture development of cast bismuth-antimony alloy via severe plastic deformation

NASA Astrophysics Data System (ADS)

Im, Jae-Taek

The purpose of this work was to study learn about grain refinement mechanisms and texture development in cast n-type Bi90Sb10 alloy caused by severe plastic deformation. The practical objective is to produce a fine grained and textured microstructure in Bi90Sb10 alloy with enhanced thermoelectric performance and mechanical strength. In the study, twelve millimeter diameter cast bars of Bi90Sb 10 alloy were encapsulated in square cross section aluminum 6061 alloy containers. The composite bars were equal channel angular (ECAE) extruded through a 90 degree angle die at high homologous temperature. Various extrusion conditions were studied including punch speed (0.1, 0.3 and 0.6 in/min), extrusion temperature (220, 235 and 250°C), number of extrusion passes (1, 2 and 4), route (A, BC and C), and exit channel area reduction ratio (half and quarter area of inlet channel). The affect of an intermediate long term heat treatment (for 100 hours at 250°C under 10-3 torr vacuum) was explored. Processed materials were characterized by optical microscopy, x-ray diffraction, energy dispersive spectroscopy, wavelength dispersive spectroscopy and scanning electron microscopy. Texture was analyzed using the {006} reflection plane to identify the orientation of the basal poles in processed materials. The cast grains were irregularly shaped, had a grain size of hundreds-of-microns to millimeters, and showed inhomogeneous chemical composition. Severe plastic deformation refines the cast grains through dynamic recrystallization and causes the development of a bimodal microstructure consisting of fine grains (5-30 micron) and coarse grains (50-300 micron). ECAE processing of homogenizied Bi-Sb alloy causes grain refinement and produces a more uniform microstructure. Texture results show that ECAE route C processing gives a similar or slightly stronger texture than ECAE route A processing. In both cases, the basal-plane poles become aligned with the shear direction. Reduction area exit channel extrusion is more effective for both grain refinement and texture enhancement than simple ECAE processing.

Construction of edge cracks pre-criterion model based on hot rolling experiment and simulation of AZ31 magnesium alloy

NASA Astrophysics Data System (ADS)

Ning, Fangkun; Jia, Weitao; Hou, Jian; Chen, Xingrui; Le, Qichi

2018-05-01

Various fracture criteria, especially Johnson and Cook (J-C) model and (normalized) Cockcroft and Latham (C-L) criterion were contrasted and discussed. Based on normalized C-L criterion, adopted in this paper, FE simulation was carried out and hot rolling experiments under temperature range of 200 °C–350 °C, rolling reduction rate of 25%–40% and rolling speed from 7–21 r/min was implemented. The microstructure was observed by optical microscope and damage values of simulation results were contrasted with the length of cracks on diverse parameters. The results show that the plate generated less edge cracks and the microstructure emerged slight shear bands and fine dynamic recrystallization grains rolled at 350 °C, 40% reduction and 14 r/min. The edge cracks pre-criterion model was obtained combined with Zener-Hollomon equation and deformation activation energy.

Modeling the Flow Behavior, Recrystallization, and Crystallographic Texture in Hot-Deformed Fe-30 Wt Pct Ni Austenite

NASA Astrophysics Data System (ADS)

Abbod, M. F.; Sellars, C. M.; Cizek, P.; Linkens, D. A.; Mahfouf, M.

2007-10-01

The present work describes a hybrid modeling approach developed for predicting the flow behavior, recrystallization characteristics, and crystallographic texture evolution in a Fe-30 wt pct Ni austenitic model alloy subjected to hot plane strain compression. A series of compression tests were performed at temperatures between 850 °C and 1050 °C and strain rates between 0.1 and 10 s-1. The evolution of grain structure, crystallographic texture, and dislocation substructure was characterized in detail for a deformation temperature of 950 °C and strain rates of 0.1 and 10 s-1, using electron backscatter diffraction and transmission electron microscopy. The hybrid modeling method utilizes a combination of empirical, physically-based, and neuro-fuzzy models. The flow stress is described as a function of the applied variables of strain rate and temperature using an empirical model. The recrystallization behavior is predicted from the measured microstructural state variables of internal dislocation density, subgrain size, and misorientation between subgrains using a physically-based model. The texture evolution is modeled using artificial neural networks.

Lunar "dunite", "pyroxenite" and "anorthosite"

USGS Publications Warehouse

Wilshire, H.G.; Jackson, E.D.

1972-01-01

Monomineralic aggregates of olivine, clinopyroxene, orthopyroxene and plagioclase with granoblastic textures are widespread minor constituents of Apollo 14 breccias. Recrystallization is commonly incomplete within these aggregates, leaving relict material that clearly indicates single-mineral-grain sources for the aggregates. The aggregates are not, therefore, properly characterized by igneous rock names, nor can any conclusions regarding differentiation be drawn from them. Average sizes of the aggregates indicate source rocks with grain sizes mostly larger than 1 to 5 mm, a few clasts of which occur in the breccias; the proportions of the different types of aggregates suggest dominantly feldspathic source rocks. ?? 1972.

Microstructural Evolution at Micro/Meso-Scale in an Ultrafine-Grained Pure Aluminum Processed by Equal-Channel Angular Pressing with Subsequent Annealing Treatment.

PubMed

Xu, Jie; Li, Jianwei; Zhu, Xiaocheng; Fan, Guohua; Shan, Debin; Guo, Bin

2015-11-04

Micro-forming with ultrafine-grained (UFG) materials is a promising direction for the fabrication of micro-electro-mechanical systems (MEMS) components due to the improved formability, good surface quality, and excellent mechanical properties it provides. In this paper, micro-compression tests were performed using UFG pure aluminum processed by equal-channel angular pressing (ECAP) with subsequent annealing treatment. Microstructural evolution was investigated by electron back-scattered diffraction (EBSD) and transmission electron microscopy (TEM). The results show that microstructural evolutions during compression tests at the micro/meso-scale in UFG pure Al are absolutely different from the coarse-grained (CG) materials. A lot of low-angle grain boundaries (LAGBs) and recrystallized fine grains are formed inside of the original large grains in CG pure aluminum after micro-compression. By contrast, ultrafine grains are kept with few sub-grain boundaries inside the grains in UFG pure aluminum, which are similar to the original microstructure before micro-compression. The surface roughness and coordinated deformation ability can be signmicrostructure; micro/meso-forming; ultrafine grains; ECAP; aluminumificantly improved with UFG pure aluminum, which demonstrates that the UFG materials have a strong potential application in micro/meso-forming.

Microstructure in Worn Surface of Hadfield Steel Crossing

NASA Astrophysics Data System (ADS)

Zhang, F. C.; Lv, B.; Wang, T. S.; Zheng, C. L.; Li, M.; Zhang, M.

In this paper a failed Hadfield (high manganese austenite) steel crossing used in railway system was studied. The microstructure in the worn surfaces of the crossing was investigated using optical microscopy, scanning electron microscopy, transmission electron microscopy and Mössbauer spectroscopy. The results indicated that a nanocrystallization layer formed on the surface of the crossing served. The formation mechanism of the nanocrystalline is the discontinuous dynamic recrystallization. The energy for the recrystallization nucleus formation originates from the interactions between the twins, the dislocations, as well as twin and dislocation. High-density vacancies promoted the recrystallization process including the dislocation climb and the atom diffusion.

Influence of brazing conditions on the strength of brazed joints of alumina dispersion-strengthened copper to 316 stainless steel

NASA Astrophysics Data System (ADS)

Nishi, H.; Kikuchi, K.

1998-10-01

Brazing of alumina dispersion-strengthened copper (DS Cu) to 316 stainless steel were conducted in order to investigate the influence of filler metals and brazing conditions on the joint strength. The brazing were performed with a silver-base (BAg-8) and three kinds of gold-base (BAu-2,4,11) filler metals with varying brazing joint clearance and brazing time. The filler metal had a greater effect on the joint strength than the brazing joint clearance and brazing time. The joint with BAu-2 was superior to the joint with other filler metals. The tensile strength of the joint with BAu-2 was as large as that of DS Cu, however, the Charpy and low cycle fatigue strength were lower than those of DS Cu. The DS Cu melted near the brazed zone, consequently recrystallization and agglomeration of alumina occurred in the diffusion layer for all filler metals. The grain size after the recrystallization was small in order of BAu-2, BAu-4 and BAu-11, that was in accordance with the order of the brazing temperature. The excellent fracture strength for the joint with BAu-2 was attributed to the smallest grain size.

Structural characterization and gas reactions of small metal particles by high-resolution TEM and TED

NASA Technical Reports Server (NTRS)

Heinemann, K.

1985-01-01

The interaction of 100 and 200 keV electron beams with amorphous alumina, titania, and aluminum nitride substrates and nanometer-size palladium particulate deposits was investigated for the two extreme cases of (1) large-area electron-beam flash-heating and (2) small-area high-intensity electron-beam irradiation. The former simulates a short-term heating effect with minimum electron irradiation exposure, the latter simulates high-dosage irradiation with minimum heating effect. All alumina and titania samples responded to the flash-heating treatment with significant recrystallization. However, the size, crystal structure, shape, and orientation of the grains depended on the type and thickness of the films and the thickness of the Pd deposit. High-dosage electron irradiation also readily crystallized the alumina substrate films but did not affect the titania films. The alumina recrystallization products were usually either all in the alpha phase, or they were a mixture of small grains in a number of low-temperature phases including gamma, delta, kappa, beta, theta-alumina. Palladium deposits reacted heavily with the alumina substrates during either treatment, but they were very little effected when supported on titania. Both treatments had the same, less prominent localized crystallization effect on aluminum nitride films.

Microdeformation in Vredefort rocks; evidence for shock metamorphism

NASA Technical Reports Server (NTRS)

Reimold, W. U.; Andreoli, M. A. G.; Hart, R. J.

1988-01-01

Planar microdeformations in quartz from basement or collar rocks of the Vredefort Dome have been cited for years as the main microtextural evidence for shock metamorphism in this structure. In addition, Schreyer describes feldspar recrystallization in rocks from the center of the Dome as the result of transformation of diaplectic glass, and Lilly reported the sighting of mosaicism in quartz. These textural observations are widely believed to indicate either an impact or an internally produced shock origin for the Vredefort Dome. Two types of (mostly sub) planar microdeformations are displayed in quartz grains from Vredefort rocks: (1) fluid inclusion trails, and (2) straight optical discontinuities that sometimes resemble lamellae. Both types occur as single features or as single or multiple sets in quartz grains. Besides qualitative descriptions of cleavage and recrystallization in feldspar and kinkbands in mica, no further microtextural evidence for shock metamorphism at Vredefort has been reported to date. Some 150 thin sections of Vredefort basement rocks were re-examined for potential shock and other deformation effects in all rock-forming minerals. This included petrographic study of two drill cores from the immediate vicinity of the center of the Dome. Observations recorded throughout the granitic core are given along with conclusions.

Mechanical Behavior of Additively Manufactured Uranium-6 wt. pct. Niobium

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, A. S.; Wraith, M. W.; Burke, S. C.

This report describes an effort to process uranium-6 weight% niobium using laser powder bed fusion. The chemistry, crystallography, microstructure and mechanical response resulting from this process are discussed with particular emphasis on the effect of the laser powder bed fusion process on impurities. In an effort to achieve homogenization and uniform mechanical behavior from different builds, as well as to induce a more conventional loading response, we explore post-processing heat treatments on this complex alloy. Elevated temperature heat treatment for recrystallization is evaluated and the effect of recrystallization on mechanical behavior in laser powder bed fusion processed U-6Nb is discussed.more » Wrought-like mechanical behavior and grain sizes are achieved through post-processing and are reported herein.« less

Recrystallization and superplasticity at 300 C in an aluminum-magnesium alloy

NASA Technical Reports Server (NTRS)

Hales, S. J.; Mcnelley, T. R.; Mcqueen, H. J.

1991-01-01

Variations in thermomechanical processing (TMP) which regulate the microstructural characteristics and superplastic response of an Al-10Mg-0.1Zr alloy at 300 C were evaluated. Mechanical property data revealed that the superplastic ductility can be enhanced by simultaneously increasing the total rolling strain, the reduction per pass, and the duration of reheating intervals between passes during isothermal rolling. Texture and microscopy data were consistent with the development of a refined microstructure by recovery-dominated processes, i.e., continuous recrystallization, during the processing. The mechanisms by which a refined substructure can be progressively converted into a fine-grained structure during repeated cycles of deformation and annealing are addressed. A qualitative description of the complex sequence of developments leading to a microstructure better suited to support superplastic response is presented.

Oxygen isotope geospeedometry by SIMS

NASA Astrophysics Data System (ADS)

Bonamici, C. E.; Valley, J. W.

2013-12-01

Geospeedometry, a discipline closely related and complimentary to thermochronology, exploits the phenomenon of diffusion in order to extract rate and duration information for segments of a rock's thermal history. Geospeedometry data, when anchored in absolute time by geochronologic data, allow for the construction of detailed temperature-time paths for specific terranes and geologic processes. We highlight the developing field of SIMS-based oxygen isotope geospeedometry with an application from granulites of the Adirondack Mountains (New York) and discuss potential future applications based on a recently updated and expanded modeling tool, the Fast Grain Boundary diffusion program (FGB; Eiler et al. 1994). Equilibrium oxygen isotope ratios in minerals are a function of temperature and bulk rock composition. In dynamic systems, intragrain oxygen isotope zoning can develop in response to geologic events that affect the thermal state of a rock and/or induce recrystallization, especially tectonic deformation and fluid infiltration. As an example, titanite grains from late-Grenville shear zones in the northwestern Adirondack Mountains exhibit a range of δ18O zoning patterns that record post-peak metamorphic cooling, episodic fluid infiltration, and deformation-facilitated recrystallization. Many titanite grains preserve smooth, core-to-rim decreasing, diffusional δ18O profiles, which are amenable to diffusion modeling. FGB models that best fit the measured δ18O profiles indicate cooling from ~700-500°C in just 2-5 m.y., a rapid thermal change signaling the final gravitational collapse of the late-Grenville orogen. Titanite can also be utilized as a U-Pb chronometer, and comparison of δ18O and U-Pb age zoning patterns within the Adirondack titanites pins the episode of rapid cooling inferred from the δ18O record to some time between 1054 and 1047 Ma. The expanded capabilities of FGB also allow for evaluation of a range of heating-cooling histories for the Adirondack granulites. Diffusional δ18O zoning profiles in titanite are best fit by complete re-equilibration at temperatures above 675 °C followed by rapid, monotonic cooling; FGB models that include only partial re-equilibration and/or episodes of reheating along the retrograde path do not fit the observed δ18O profiles. Beyond the Adirondack titanite example, FGB can be used as a predictive tool to target either specific minerals within a rock or specific rock types within a terrane for oxygen isotope geospeedometry and zoning studies. FGB generates predictions of δ18O zoning for all minerals in a rock of a given mineralogy and heating-cooling history. Different minerals within the same rock will record different segments of the thermal and fluid history based on their individual diffusivities, phase stabilities, and propensities for deformation-induced/facilitated recrystallization. It should therefore be possible to extract long thermal histories from a single sample by measuring oxygen isotope zoning profiles across several minerals with different partial retention zones for oxygen.

Deformation and damage mechanisms of zinc coatings on hot-dip galvanized steel sheets: Part II. Damage modes

NASA Astrophysics Data System (ADS)

Parisot, Rodolphe; Forest, Samuel; Pineau, André; Grillon, François; Demonet, Xavier; Mataigne, Jean-Michel

2004-03-01

Zinc-based coatings are widely used for protection against corrosion of steel-sheet products in the automotive industry. The objective of the present article is to investigate the damage modes at work in three different microstructures of a zinc coating on an interstitial-free steel substrate under tension, planestrain tension, and expansion loading. Plastic-deformation mechanisms are addressed in the companion article. Two main fracture mechanisms, namely, intergranular cracking and transgranular cleavage fracture, were identified in an untempered cold-rolled coating, a tempered cold-rolled coating, and a recrystallized coating. No fracture at the interface between the steel and zinc coating was observed that could lead to spalling, in the studied zinc alloy. A complex network of cleavage cracks and their interaction with deformation twinning is shown to develop in the material. An extensive quantitative analysis based on systematic image analysis provides the number and cumulative length of cleavage cracks at different strain levels for the three investigated microstructures and three loading conditions. Grain refinement by recrystallization is shown to lead to an improved cracking resistance of the coating. A model for crystallographic cleavage combining the stress component normal to the basal plane and the amount of plastic slip on the basal slip systems is proposed and identified from equibiaxial tension tests and electron backscattered diffraction (EBSD) analysis of the cracked grains. This analysis requires the computation of the nonlinear stress-strain response of each grain using a crystal-plasticity constitutive model. The model is then applied successfully to other loading conditions and is shown to account for the preferred orientations of damaged grains observed in the case of plane-strain tension.

Microfabric and Structures in Glacial Ice

NASA Astrophysics Data System (ADS)

Monz, M.; Hudleston, P. J.

2017-12-01

Similar to rocks in active orogens, glacial ice develops both structures and fabrics that reflect deformation. Crystallographic preferred orientation (CPO), associated with mechanical anisotropy, develops as ice deforms, and as in rock, directly reflects the conditions and mechanisms of deformation and influences the overall strength. This project aims to better constrain the rheologic properties of natural ice through microstructural analysis and to establish the relationship of microfabric to macroscale structures. The focus is on enigmatic fabric patterns found in coarse grained, "warm" (T > -10oC) ice deep in ice sheets and in valley glaciers. Deformation mechanisms that produce such patterns are poorly understood. Detailed mapping of surface structures, including bedding, foliation, and blue bands (bubble-free veins of ice), was done in the ablation zone of Storglaciären, a polythermal valley glacier in northern Sweden. Microstructural studies on samples from a transect across the ablation zone were carried out in a cold room. Crystal size was too large for use of electron backscattered diffraction to determine CPO, therefore a Rigsby universal stage, designed specifically for ice, was used. In thick and thin sections, recrystallized grains are locally variable in both size (1mm-7cm in one thin section) and shape and clearly reflect recrystallization involving highly mobile grain boundaries. Larger crystals are often branching, and appear multiple times throughout one thin section. There is a clear shape preferred orientation that is generally parallel with foliation defined by bubble alignment and concentration. Locally, there appears to be an inverse correlation between bubble concentration and smoothness of grain boundaries. Fabric in samples that have undergone prolonged shear display roughly symmetrical multimaxima patterns centered around the pole to foliation. The angular distances between maxima suggest a possible twin relationship that may have developed from a preexisting single-maximum fabric.

Microstructure and texture evolution in cold-rolled and annealed alloy MA-956

NASA Astrophysics Data System (ADS)

Hosoda, Takashi

The microstructural and texture development with thermomechanical processing, performed through a combination of cold-rolling and annealing, in MA-956 plate consisting of a layered and inhomogeneous microstructure was systematically assessed. The alloy contained in mass percent, 20 Cr, 4.8 Al, 0.4 Ti, 0.4 Y2O3, and the balance iron. The starting material was as-hot-rolled plate, 9.7 mm thick. The as-hot-rolled plate was subjected to 40%, 60%, and 80% cold-rolling reduction and subsequently annealed at 1000, 1200, or 1380. Assessment of microstructural and texture developments before and after cold-rolling and annealing was performed using light optical microscopy (LOM), Vickers hardness testing, and electron backscatter diffraction (EBSD). Locally introduced misorientations by cold-rolling in each region were evaluated by Kernel Average Misorientation (KAM) maps. The as-hot-rolled condition contained a layered and inhomogeneous microstructure consisting of thin and coarse elongated grains, and aggregated regions which consisted of fine grains and sub-grains with {100} texture parallel to the longitudinal direction. The microstructure of the 40% cold-rolled condition contained deformation bands, and the 60% and 80% cold-rolled conditions also contained highly deformed regions where the deformation bands were intricately tangled. A predominant orientation of (001) parallel to the rolling direction was developed during cold-rolling, becoming more prominent with increasing reduction. The magnitudes of KAM angles varied through the thickness depending on the initial microstructures. Recrystallization occurred in regions where high KAM angles were dense after annealing and nucleation sites were the aggregation regions, deformation bands, and highly deformed regions. The shape and size of the recrystallized grains varied depending on the nucleation sites.

Recrystallization of freezable bound water in aqueous solutions of medium concentration

NASA Astrophysics Data System (ADS)

Lishan, Zhao; Liqing, Pan; Ailing, Ji; Zexian, Cao; Qiang, Wang

2016-07-01

For aqueous solutions with freezable bound water, vitrification and recrystallization are mingled, which brings difficulty to application and misleads the interpretation of relevant experiments. Here, we report a quantification scheme for the freezable bound water based on the water-content dependence of glass transition temperature, by which also the concentration range for the solutions that may undergo recrystallization finds a clear definition. Furthermore, we find that depending on the amount of the freezable bound water, different temperature protocols should be devised to achieve a complete recrystallization. Our results may be helpful for understanding the dynamics of supercooled aqueous solutions and for improving their manipulation in various industries. Project supported by the Knowledge Innovation Project of Chinese Academy of Sciences on Water Science Research (Grant No. KJZD-EW-M03) and the National Natural Science Foundation of China (Grant Nos. 11474325 and 11290161).