Non-flammable elastomeric fiber from a fluorinated elastomer and containing an halogenated flame retardant

NASA Technical Reports Server (NTRS)

Howarth, J. T.; Sheth, S. G.; Sidman, K. R.; Massucco, A. A. (Inventor)

1976-01-01

Flame retardant elastomeric compositions are described comprised of either spandex type polyurethane having incorporated into the polymer chain halogen containing polyols, conventional spandex type polyurethanes in physical admixture with flame retardant additives, or fluoroelastomeric resins in physical admixture with flame retardant additives. Methods are described for preparing fibers of the flame retardant elastomeric materials and articles of manufacture comprised of the flame retardant clastomeric materials and non elastic materials such as polybenzimidazoles, fiberglass, nylons, etc.

Flame retardant spandex type polyurethanes

NASA Technical Reports Server (NTRS)

Howarth, J. T.; Sheth, S.; Sidman, K. R.; Massucco, A. A. (Inventor)

1978-01-01

Flame retardant elastomeric compositions were developed, comprised of: (1) spandex type polyurethane having incorporated into the polymer chain, halogen containing polyols; (2) conventional spandex type polyurethanes in physical admixture flame retardant additives; and (3) fluoroelastomeric resins in physical admixture with flame retardant additives. Methods of preparing fibers of the flame retardant elastomeric materials are presented and articles of manufacture comprised of the elastomeric materials are mentioned.

In situ optical measurements for characterization of flame species and remote sensing

NASA Astrophysics Data System (ADS)

Cullum, Brian Michael

1998-12-01

The following dissertation describes the use of spectroscopic techniques for both characterization of combustion intermediates and remote chemical sensing. The primary techniques that have been used for these measurements include, laser-induced fluorescence (LIF), time resolved LIF, resonance enhanced multiphoton ionization (REMPI) and Raman spectroscopy. A simple and quantitative means of measuring the efficiency of halogenated flame retardants is described, using laser-induced fluorescence (LIF). Intensity based LIF measurements of OH radical have been used to quantitatively measure the efficacy of halogenated flame retardant/polymer plaques. Temporally resolved LIF has been used to determine the extent to which the chemical kinetic theory of flame retardation applies to the effect of these compounds on combustion. We have shown that LIF of OH radicals is a very sensitive means of measuring the efficiency of these flame retardants as well as the giving information about the nature of flame retardation. In addition, we have developed a technique for the introduction of insoluble polymer plaques into a flame for fluorescence analysis. A high power pulsed Nd:YAG laser is used to ablate the sample into the flame while a second pulse from a dye laser is used to measure the LIF of OH radicals. Spectroscopic techniques are also very useful for trace remote analysis of environmental pollutants via optical fibers. A simple fiber-optic probe suitable for remote analysis using resonance enhanced multiphoton ionization (REMPI) has been developed for this purpose and is used to determine the toluene/gasoline concentration in water samples via a headspace measurement. The limit of detection for toluene in water using this probe is 0.54 ppb (wt/wt) with a sample standard deviation of 0.02 ppb (wt/wt). Another technique that has great potential for optical sensing is fluorescence lifetime imaging. A new method for measuring fluorescence lifetime images of quickly decaying species has been developed. This method employs a high powered pulsed laser that excites the fluorescent species in a dual pulse manner, and a non-gated charge coupled device (CCD) for detection of the fluorescence. Unlike other fluorescence lifetime imaging methods, this technique has the potential of monitoring fluorescent species with picosecond lifetimes.

Performance of carbon material derived from starch mixed with flame retardant as electrochemical capacitor

NASA Astrophysics Data System (ADS)

Tsubota, Toshiki; Morita, Masaki; Murakami, Naoya; Ohno, Teruhisa

2014-12-01

Carbon materials derived from starch with an added flame retardant, such as melamine polyphosphate, melamine sulfate, guanylurea phosphate, or guanidine phosphate, were synthesized for investigating the performance as the electrode of an electrochemical capacitor. The yield after the heat treatment of the carbonization reaction increased by the addition of these flame retardants up to 800 °C. Although both the specific surface area and electrical resistivity are almost independent of the addition of the flame retardants, the capacitance values are improved with the addition of the flame retardants. The nitrogen atoms derived from the flame retardants are introduced to some extent into the synthesized carbon material. Moreover, the phosphorous atoms or the sulfur atoms derived from the flame retardants are doped into the synthesized carbon material. The method applied in this study, that is, the addition of flame retardants before the carbonization process can be used for the doping of the hetero atom such as N, P and S into the carbon material.

Occupational exposure to polybrominated diphenyl ethers (PBDEs) and other flame retardant foam additives at gymnastics studios: Before, during and after the replacement of pit foam with PBDE-free foams.

PubMed

Ceballos, Diana M; Broadwater, Kendra; Page, Elena; Croteau, Gerry; La Guardia, Mark J

2018-07-01

Coaches spend long hours training gymnasts of all ages aided by polyurethane foam used in loose blocks, mats, and other padded equipment. Polyurethane foam can contain flame retardant additives such as polybrominated diphenyl ethers (PBDEs), to delay the spread of fires. However, flame retardants have been associated with endocrine disruption and carcinogenicity. The National Institute for Occupational Safety and Health (NIOSH) evaluated employee exposure to flame retardants in four gymnastics studios utilized by recreational and competitive gymnasts. We evaluated flame retardant exposure at the gymnastics studios before, during, and after the replacement of foam blocks used in safety pits with foam blocks certified not to contain several flame retardants, including PBDEs. We collected hand wipes on coaches to measure levels of flame retardants on skin before and after their work shift. We measured flame retardant levels in the dust on window glass in the gymnastics areas and office areas, and in the old and new foam blocks used throughout the gymnastics studios. We found statistically higher levels of 9 out of 13 flame retardants on employees' hands after work than before, and this difference was reduced after the foam replacement. Windows in the gymnastics areas had higher levels of 3 of the 13 flame retardants than windows outside the gymnastics areas, suggesting that dust and vapor containing flame retardants became airborne. Mats and other padded equipment contained levels of bromine consistent with the amount of brominated flame retardants in foam samples analyzed in the laboratory. New blocks did not contain PBDEs, but did contain the flame retardants 2-ethylhexyl 2,3,4,5-tetrabromobenzoate and 2-ethylhexyl 2,3,4,5-tetrabromophthalate. We conclude that replacing the pit foam blocks eliminated a source of PBDEs, but not 2-ethylhexyl 2,3,4,5-tetrabromobenzoate and 2-ethylhexyl 2,3,4,5-tetrabromophthalate. We recommend ways to further minimize employee exposure to flame retardants at work and acknowledge the challenges consumers have identifying chemical contents of new products. Published by Elsevier Ltd.

Process for spinning flame retardant elastomeric compositions. [fabricating synthetic fibers for high oxygen environments

NASA Technical Reports Server (NTRS)

Howarth, J. T.; Sheth, S.; Sidman, K. R.; Massucco, A. A. (Inventor)

1978-01-01

Flame retardant elastomeric compositions comprised of either spandex type polyurethane having halogen containing polyols incorporated into the polymer chain, conventional spandex type polyurethanes in physical admixture with flame retardant additives, or fluoroelastomeric resins in physical admixture with flame retardant additives were developed. Methods are described for preparing fibers of the flame retardant elastomeric materials and manufactured articles as well as nonelastic materials such as polybenzimidazoles, fiberglass, and nylons, for high oxygen environments.

Engineering Biodegradable Flame Retardant Wood-Plastic Composites

NASA Astrophysics Data System (ADS)

Zhang, Linxi

Wood-plastic composites (WPCs), which are produced by blending wood and polymer materials, have attracted increasing attentions in market and industry due to the low cost and excellent performance. In this research, we have successfully engineered WPC by melt blending Polylactic Acid (PLA) and Poly(butylene adipate-co-terphthalate) (PBAT) with recycled wood flour. The thermal property and flammability of the composite are significantly improved by introducing flame retardant agent resorcinol bis(biphenyl phosphate) (RDP). The mechanical and morphological properties are also investigated via multiple techniques. The results show that wood material has increased toughness and impact resistance of the PLA/PBAT polymer matrix. SEM images have confirmed that PLA and PBAT are immiscible, but the incompatibility is reduced by the addition of wood. RDP is initially dispersed in the blends evenly. It migrates to the surface of the sample after flame application, and serves as a barrier between the fire and underlying polymers and wood mixture. It is well proved in the research that RDP is an efficient flame retardant agent in the WPC system.

TG-FTIR characterization of flame retardant polyurethane foams materials

NASA Astrophysics Data System (ADS)

Liu, W.; Tang, Y.; Li, F.; Ge, X. G.; Zhang, Z. J.

2016-07-01

Dimethyl methylphosphonate (DMMP) and trichloroethyl phosphtate (TCEP) have been used to enhance the flame retardancy of polyurethane foams materials (PUF). Flame retardancy and thermal degradation of PUF samples have been investigated by the LOI tests and thermal analysis. The results indicate that the excellent flame retardancy can be achieved due to the presence of the flame retardant system containing DMMP and TCEP. TG-FTIR reveals that the addition of DMMP/TCEP can not only improve the thermal stability of PUF samples but can also affect the gaseous phase at high temperature.

A robust and stretchable superhydrophobic PDMS/PVDF@KNFs membrane for oil/water separation and flame retardancy.

PubMed

Li, Deke; Gou, Xuelian; Wu, Daheng; Guo, Zhiguang

2018-04-05

The wide application of superhydrophobic membranes has been limited due to their complicated preparation technology and weak durability. Inspired by the mechanical flexibility of nanofibrous biomaterials, nanofibrils have been successfully generated from Kevlar, which is one of the strongest synthetic fibers, by appropriate hydrothermal treatment. In this study, a robust superhydrophobic PDMS/PVDF@KNFs membrane is prepared via a simple one-step process and subsequent curing without combination with inorganic fillers. The as-prepared PDMS/PVDF@KNFs membrane not only shows efficient oil/water separation ability and oil absorption capacity but also has excellent superhydrophobicity stability after deformation. The resultant membrane shows stretchability, flexibility and flame retardance because of the reinforcing effect and the excellent flame retardancy of Kevlar. We believe that this simple fabrication of PDMS/PVDF@KNFs has promising applications in filtering membranes and wearable devices.

The role of boron in flame-retardant treatments

Treesearch

S. L. LeVan; H. C. Tran

1990-01-01

Flame retardants for wood alter the combustion properties of wood to reduce surface flame spread. Flame retardant chemicals cause acid catalyzed dehydration reactions in wood to facilitate the formation of char and reduce the effective heat of combustion, resulting in lower heat release and flame spread. Boron compounds can also form glassy fiis that may inhibit mass...

Flame Retardants Used in Flexible Polyurethane Foam

EPA Pesticide Factsheets

The partnership project on flame retardants in furniture seeks to update the health and environmental profiles of flame-retardant chemicals that meet fire safety standards for upholstered consumer products with polyurethane foam

Hydrothermal synthesis of 4ZnO·B2O3·H2O/RGO hybrid material and its flame retardant behavior in flexible PVC and magnesium hydroxide composites

NASA Astrophysics Data System (ADS)

Zhang, Zhifan; Wu, Weihong; Zhang, Mengjiao; Qu, Jiamin; Shi, Lin; Qu, Hongqiang; Xu, Jianzhong

2017-12-01

As a novel and efficient halogen-free composite flame retardant, zinc borate (4ZnO·B2O3·H2O)/reduction graphene oxide (RGO) hybrid material (ZB/RGO) was designed and synthesized using a facile route involving nano-engineering. The unique structure and composition of ZB/RGO were efficaciously confirmed by XRD, FTIR, SEM, TEM, and TG. The incorporation of 7.71 wt% ZB/RGO could significantly enhance the synergistic effect with Mg(OH)2 (MH) when mixed with poly(vinyl chloride) (PVC) as a flame retardant and smoke suppressant, as evaluated by limited oxygen index (LOI), microscale combustion calorimetry (MCC), and a cone calorimetry test (CCT) and compared with PVC, PVC/ZB, PVC/MH, and PVC/ZB/MH blends. The PVC/ZB/RGO/MH formulation could achieve an LOI value of 29.5% (24% higher than neat PVC). More importantly, the heat release rate (HRR), peak heat release rate (PHRR), smoke production rate (SPR), perk smoke production rate (PSPR), total smoke production (TSP), and mass amount loss (MAL) were considerably reduced in CCT, especially the PHRR, TSP, and MAL values for PVC/ZB/RGO/MH blends were reduced to 35%, 34%, and 15%, respectively. This study showed that the design of the novel material might provide a reference for the future development of halogen-free flame retardants consisting of inorganic salt and carbon material, which exhibit excellent flame retardant and smoke suppressant behavior.

Do flame retardant chemicals increase the risk for thyroid dysregulation and cancer?

PubMed

Hoffman, Kate; Sosa, Julie A; Stapleton, Heather M

2017-01-01

Flame retardant chemicals are added to consumer products to reduce fire incidence and severity; approximately 1.5 million tons of these chemicals are used annually. However, their widespread use has led to their ubiquitous presence in the environment and chronic accumulation in human tissues. We summarize current trends in human flame retardant chemical exposure, and review recent data highlighting concerns for thyroid dysregulation and cancer risk in human populations. Polybrominated diphenyl ethers were once commonly used as flame retardant chemicals, but recently were phased out. Exposure is associated with thyroid dysregulation (mainly T4 reductions) in animals, with new work focusing on specific mechanisms of action. Polybrominated diphenyl ethers also impact human thyroid regulation and are related to clinical thyroid disease, but associations appear both dose and life-stage dependent. Emerging data suggest that common alternate flame retardant chemicals may be more potent thyroid disruptors than their predecessors, which is particularly concerning given increasing levels of exposure. Potential health impacts of flame retardant chemicals are only beginning to be understood for 'legacy flame retardant chemicals' (i.e., polybrominated diphenyl ethers), and are largely unevaluated for newer-use chemicals. Cumulatively, current data suggest impact on thyroid regulation is likely, potentially implicating flame retardant chemicals in thyroid disease and cancers for which thyroid dysregulation impacts risk or prognosis.

Simultaneous determination of brominated and phosphate flame retardants in flame-retarded polyester curtains by a novel extraction method.

PubMed

Miyake, Yuichi; Tokumura, Masahiro; Nakayama, Hayato; Wang, Qi; Amagai, Takashi; Ogo, Sayaka; Kume, Kazunari; Kobayashi, Takeshi; Takasu, Shinji; Ogawa, Kumiko; Kannan, Kurunthachalam

2017-12-01

The use of novel brominated flame retardants (BFRs) and phosphate-based flame retardants (PFRs) has increased as substitutes for hexabromocyclododecane (HBCD) in many consumer products. To facilitate collection of data on chemicals used as flame retardants in textiles and fabrics, we developed an analytical method using liquid chromatography interfaced with tandem mass spectrometry (LC-MS/MS). We compared two extraction methods, one involving ultrasonic extraction (traditional method) using dichloromethane, toluene or acetone and the other encompassing complete dissolution of textile with 25% 1,1,1,3,3,3-hexafluoro-2-propanol/chloroform. The dissolution method extracted up to 204 times more BFRs and PFRs than the traditional ultrasonic extraction. Tris(2,3-dibromopropyl) isocyanurate (TDBP-TAZTO), triphenylphosphine oxide (TPhPO), tris(1,3-dichloro-2-propyl) phosphate (TDCPP), tricresyl phosphate (TCsP), and triphenyl phosphate (TPhP) were found in 40 flame-retarded curtain samples purchased from Japanese market in 2014. TDBP-TAZTO was detected in polyester curtains for the first time. Some of the flame-retarded curtain samples did not contain any of the known target analytes, which suggested the presence of other unknown flame retardants in those fabrics. Copyright © 2017. Published by Elsevier B.V.

Recent Developments in Halogen Free Flame Retardants for Epoxy Resins for Electrical and Electronic Applications

PubMed Central

Rakotomalala, Muriel; Wagner, Sebastian; Döring, Manfred

2010-01-01

The recent implementation of new environmental legislations led to a change in the manufacturing of composites that has repercussions on printed wiring boards (PWB). This in turn led to alternate processing methods (e.g., lead-free soldering), which affected the required physical and chemical properties of the additives used to impart flame retardancy. This review will discuss the latest advancements in phosphorus containing flame retardants for electrical and electronic (EE) applications and compare them with commercially available ones. The mechanism of degradation and flame retardancy of phosphorus flame retardants in epoxy resins will also be discussed. PMID:28883331

Novel phosphonates triazine derivative as economic flame retardant for cotton

USDA-ARS?s Scientific Manuscript database

Phosphorous-containing flame retardants are widely used in standard and engineering plastics, polyurethane foams, thermosets, coatings, and textiles. Organophosphorous flame retardants have been known to be more effective when used in conjunction with nitrogen-containing systems. Their mixture produ...

Halogenated flame retardants in the Great Lakes environment.

PubMed

Venier, Marta; Salamova, Amina; Hites, Ronald A

2015-07-21

Flame retardants are widely used industrial chemicals that are added to polymers, such as polyurethane foam, to prevent them from rapidly burning if exposed to a small flame or a smoldering cigarette. Flame retardants, especially brominated flame retardants, are added to many polymeric products at percent levels and are present in most upholstered furniture and mattresses. Most of these chemicals are so-called "additive" flame retardants and are not chemically bound to the polymer; thus, they migrate from the polymeric materials into the environment and into people. As a result, some of these chemicals have become widespread pollutants, which is a concern given their possible adverse health effects. Perhaps because of their environmental ubiquity, the most heavily used group of brominated flame retardants, the polybrominated diphenyl ethers (PBDEs), was withdrawn from production and use during the 2004-2013 period. This led to an increasing demand for other flame retardants, including other brominated aromatics and organophosphate esters. Although little is known about the use or production volumes of these newer flame retardants, it is evident that some of these chemicals are also becoming pervasive in the environment and in humans. In this Account, we describe our research on the occurrence of halogenated and organophosphate flame retardants in the environment, with a specific focus on the Great Lakes region. This Account starts with a short introduction to the first generation of brominated flame retardants, the polybrominated biphenyls, and then presents our measurements of their replacement, the PBDEs. We summarize our data on PBDE levels in babies, bald eagles, and in air. Once these compounds came off the market, we began to measure several of the newer flame retardants in air collected on the shores of the Great Lakes once every 12 days. These new measurements focus on a tetrabrominated benzoate, a tetrabrominated phthalate, a hexabrominated diphenoxyethane, several brominated benzenes, and a highly chlorinated norbornene compound called Dechlorane Plus. Most recently, we have begun measuring the atmospheric concentrations of several organophosphate esters, which are an increasing part of the flame retardant market. The interesting feature of this story is how one compound or set of compounds has followed another out of and into the marketplace even though none of them have been officially regulated. This replacement of one commercial product by another with similar functions shows that the chemical industry does respond to scientific environmental measurements and to the resulting bad publicity. This is a good thing. The problem is that often the replacement chemicals also become environmentally ubiquitous.

Aluminum phosphate microcapsule flame retardants for flexible polyurethane foams

NASA Astrophysics Data System (ADS)

Zhang, Bin; Liu, Hong; Han, Jian

2018-04-01

In this study, highly efficient flame-retardant aluminum phosphate (ALP) microcapsules were synthesized from ALP and ammonium phosphomolybdate trihydrate. The chemical structure of the ALP microcapsules was characterized by scanning electron microscopy and elemental analysis, and the thermal degradation behavior was investigated by thermogravimetric analysis (TGA). Subsequently, flexible polyurethane (PU) foams were prepared with the ALP microcapsules. Limiting oxygen index (LOI) tests, vertical burning tests, smoke density rating (SDR), and cone calorimetric tests were employed to investigate the combustion of the materials. The results showed that the flexible PU foams with 15 parts per hundred polyol by weight (pphp) ALP microcapsules passed the vertical burning test and they had an increased LOI value of 28.5%. The SDR value for PU/20 pphp ALP microcapsule composites was about 16.0% and the SDR value for the pure PU was about 29.0%. The corresponding flame-retardant mechanism was investigated by Fourier transform infrared spectroscopy, TGA, Pyrolysis Gas Chromatography Mass Spectrometry (Py-GC/MS) tests, and energy-dispersive X-ray spectrometry.

Development of fiber reactive, non-halogenated flame retardant on cotton fabrics and the enhanced flame retardancy by covalent bonding

USDA-ARS?s Scientific Manuscript database

The US law requires flame resistant properties on apparel or house hold items to prevent or minimize the fire damage. The objective of this research was to develop a non-halogenated flame retardant for application onto cotton fabrics. These treated fabrics can then be used in clothes or beddings to ...

Flame retardancy of polyaniline-deposited paper composites prepared via in situ polymerization.

PubMed

Wu, Xianna; Qian, Xueren; An, Xianhui

2013-01-30

Polyaniline-deposited paper composites doped with three inorganic acids were prepared via in situ polymerization, and their flame-retardant properties were investigated. Both the conductivity and flame retardancy of the composite increased with the increase of the amount of the polyaniline deposited. The doping acid played a very key role in both the conductivity and flame retardancy of the composite. The comprehensive properties of the composite could be improved when codoped with an equimolar mixture of H(3)PO(4) and H(2)SO(4) or H(3)PO(4) and HCl. The decay of the flame retardancy of the composite in atmosphere was due to the dedoping of the polyaniline deposited on cellulose fibers. Copyright © 2012 Elsevier Ltd. All rights reserved.

Flame retardant antibacterial cotton high-loft nonwoven fabrics

USDA-ARS?s Scientific Manuscript database

Flame retardant treated gray cotton fibers were blended with antibacterial treated gray cotton fibers and polyester/polyester sheath/core bicomponent fibers to form high-loft fabrics. The high flame retardancy (FR) and antibacterial property of these high lofts were evaluated by limiting oxygen inde...

Identification of Flame Retardants in Polyurethane Foam Collected from Baby Products

PubMed Central

2011-01-01

With the phase-out of PentaBDE in 2004, alternative flame retardants are being used in polyurethane foam to meet flammability standards. However, insufficient information is available on the identity of the flame retardants currently in use. Baby products containing polyurethane foam must meet California state furniture flammability standards, which likely affects the use of flame retardants in baby products throughout the U.S. However, it is unclear which products contain flame retardants and at what concentrations. In this study we surveyed baby products containing polyurethane foam to investigate how often flame retardants were used in these products. Information on when the products were purchased and whether they contained a label indicating that the product meets requirements for a California flammability standard were recorded. When possible, we identified the flame retardants being used and their concentrations in the foam. Foam samples collected from 101 commonly used baby products were analyzed. Eighty samples contained an identifiable flame retardant additive, and all but one of these was either chlorinated or brominated. The most common flame retardant detected was tris(1,3-dichloroisopropyl) phosphate (TDCPP; detection frequency 36%), followed by components typically found in the Firemaster550 commercial mixture (detection frequency 17%). Five samples contained PBDE congeners commonly associated with PentaBDE, suggesting products with PentaBDE are still in-use. Two chlorinated organophosphate flame retardants (OPFRs) not previously documented in the environment were also identified, one of which is commercially sold as V6 (detection frequency 15%) and contains tris(2-chloroethyl) phosphate (TCEP) as an impurity. As an addition to this study, we used a portable X-ray fluorescence (XRF) analyzer to estimate the bromine and chlorine content of the foam and investigate whether XRF is a useful method for predicting the presence of halogenated flame retardant additives in these products. A significant correlation was observed for bromine; however, there was no significant relationship observed for chlorine. To the authors knowledge, this is the first study to report on flame retardants in baby products. In addition, we have identified two chlorinated OPFRs not previously documented in the environment or in consumer products. Based on exposure estimates conducted by the Consumer Product Safety Commission (CPSC), we predict that infants may receive greater exposure to TDCPP from these products compared to the average child or adult from upholstered furniture, all of which are higher than acceptable daily intake levels of TDCPP set by the CPSC. Future studies are therefore warranted to specifically measure infants exposure to these flame retardants from intimate contact with these products and to determine if there are any associated health concerns. PMID:21591615

Identification of flame retardants in polyurethane foam collected from baby products.

PubMed

Stapleton, Heather M; Klosterhaus, Susan; Keller, Alex; Ferguson, P Lee; van Bergen, Saskia; Cooper, Ellen; Webster, Thomas F; Blum, Arlene

2011-06-15

With the phase-out of PentaBDE in 2004, alternative flame retardants are being used in polyurethane foam to meet flammability standards. However, insufficient information is available on the identity of the flame retardants currently in use. Baby products containing polyurethane foam must meet California state furniture flammability standards, which likely affects the use of flame retardants in baby products throughout the U.S. However, it is unclear which products contain flame retardants and at what concentrations. In this study we surveyed baby products containing polyurethane foam to investigate how often flame retardants were used in these products. Information on when the products were purchased and whether they contained a label indicating that the product meets requirements for a California flammability standard were recorded. When possible, we identified the flame retardants being used and their concentrations in the foam. Foam samples collected from 101 commonly used baby products were analyzed. Eighty samples contained an identifiable flame retardant additive, and all but one of these was either chlorinated or brominated. The most common flame retardant detected was tris(1,3-dichloroisopropyl) phosphate (TDCPP; detection frequency 36%), followed by components typically found in the Firemaster550 commercial mixture (detection frequency 17%). Five samples contained PBDE congeners commonly associated with PentaBDE, suggesting products with PentaBDE are still in-use. Two chlorinated organophosphate flame retardants (OPFRs) not previously documented in the environment were also identified, one of which is commercially sold as V6 (detection frequency 15%) and contains tris(2-chloroethyl) phosphate (TCEP) as an impurity. As an addition to this study, we used a portable X-ray fluorescence (XRF) analyzer to estimate the bromine and chlorine content of the foam and investigate whether XRF is a useful method for predicting the presence of halogenated flame retardant additives in these products. A significant correlation was observed for bromine; however, there was no significant relationship observed for chlorine. To the authors knowledge, this is the first study to report on flame retardants in baby products. In addition, we have identified two chlorinated OPFRs not previously documented in the environment or in consumer products. Based on exposure estimates conducted by the Consumer Product Safety Commission (CPSC), we predict that infants may receive greater exposure to TDCPP from these products compared to the average child or adult from upholstered furniture, all of which are higher than acceptable daily intake levels of TDCPP set by the CPSC. Future studies are therefore warranted to specifically measure infants exposure to these flame retardants from intimate contact with these products and to determine if there are any associated health concerns.

IN VITRO DERMAL ABSORPTION OF FLAME RETARDANT CHEMICALS

EPA Science Inventory

ABSTRACT
The use of flame retardant chemicals in furniture fabric could pose a potential health risk to consumers from dermal absorption of these compounds. The objective of this study was to examine the in vitro dermal absorption of two flame retardant chemicals, [14C]-d...

Development of flame retardant cotton fabric based on ionic liquids via sol-gel technique.

NASA Astrophysics Data System (ADS)

Bentis, A.; Boukhriss, A.; Boyer, D.; Gmouh, S.

2017-10-01

In this study, flame retardant cotton fabrics were developed by the sol-gel method, in order to enhance their flame retardant proprieties. For this aim, seven sols were prepared using tetraethylorthosilicate (TEOS) and different ionic liquids (ILs) consist on pyridinium and Methylimidazolium cations with different anions such as: PF6-, CH3COO-, and Br-. Those sols were applied separately to the cotton fabrics by a pad-dry-cure process. The flame retardant properties of functionalized cotton fabrics before and after washing were determined by the vertical flame tests according to ISO6940:2004(F) standard. The effects of anions have been thoroughly investigated, aiming at the optimization of the targeted properties. Thermogravimetric and mechanical according to NF EN ISO 13934-1:2013standard, analyses have been also investigated. The results showed that flame retardancy, thermal stability and mechanical properties of treated fabrics were enhanced by using ionic liquids.

75 FR 28804 - An Exposure Assessment of Polybrominated Diphenyl Ethers (PBDEs)

Federal Register 2010, 2011, 2012, 2013, 2014

2010-05-24

... exposure of Americans to polybrominated diphenyl ethers (PBDEs), a class of brominated flame retardants. It... polybrominated diphenyl ethers (PBDEs), a class of brominated flame retardants. The use of PBDEs as flame retardants in products associated with the indoor environment has led to exposures primarily associated with...

Bioaccumulation and toxicity of the flame retardant TBPH or the polychlorinated biphenyl PCB153 during dietary exposure in mummichog (Fundulus heteroclitus)

EPA Science Inventory

The use of polybrominated diphenyl ethers as flame retardants in consumer products has been scrutinized increasingly due to their environmental persistence and potential toxicity; however, alternative replacement flame retardants may have similar drawbacks. The alternative bromin...

Use of Alternative Assays to Identify and Prioritize Organophosphorus Flame Retardants for Potential Developmental and Neurotoxicity

EPA Science Inventory

Due to their toxicity and persistence in the environment, brominated flame retardants (BFRs) are being phased out of commercial use, leading to the increased use of alternative chemicals such as the organophosphorus flame retardants (OPFRs). There is, however, limited information...

Understanding the mechanism of action of triazine-phosphonate derivatives as flame retardants for cotton fabrics

USDA-ARS?s Scientific Manuscript database

Countless hours of research and studies on triazine, phosphonate and their combination have provided insightful information into their flame retardant properties on polymeric systems. However, only limited number of studies shed light on the mechanism of flame retardant cotton fabrics. The purpose...

A Versatile and Scalable Approach toward Robust Superhydrophobic Porous Materials with Excellent Absorbency and Flame Retardancy

NASA Astrophysics Data System (ADS)

Ruan, Changping; Shen, Mengxia; Ren, Xiaoyan; Ai, Kelong; Lu, Lehui

2016-08-01

The frequent oil spillages and the industrial discharge of organic contaminants have not only created severe environmental and ecological crises, but also cause a risk of fire and explosion. These environmental and safety issues emphasize the urgent need for materials that possess superior sorption capability and less flammability and thus can effectively and safely clean up the floating oils and water-insoluble organic compounds. Here we present the successful hydrophobic modification of the flame retardant melamine sponge with a commercial fluorosilicone, by using a facile one-step solvent-free approach and demonstrate that the resultant superhydrophobic sponge not only exhibits extraordinary absorption efficiency (including high capacity, superior selectivity, good recyclability, and simple recycling routes), but also retains excellent flame retardancy and robust stability. In comparison to conventional methods, which usually utilize massive organic solvents, the present approach does not involve any complicated process or sophisticated equipment nor generates any waste liquids, and thus is a more labor-saving, environment-friendly, energy-efficient and cost-effective strategy for the hydrophobic modification. Taking into account the critical role of hydrophobic porous materials, especially in the field of environmental remediation, the approach presented herein would be highly valuable for environmental remediation and industrial applications.

A Versatile and Scalable Approach toward Robust Superhydrophobic Porous Materials with Excellent Absorbency and Flame Retardancy

PubMed Central

Ruan, Changping; Shen, Mengxia; Ren, Xiaoyan; Ai, Kelong; Lu, Lehui

2016-01-01

The frequent oil spillages and the industrial discharge of organic contaminants have not only created severe environmental and ecological crises, but also cause a risk of fire and explosion. These environmental and safety issues emphasize the urgent need for materials that possess superior sorption capability and less flammability and thus can effectively and safely clean up the floating oils and water-insoluble organic compounds. Here we present the successful hydrophobic modification of the flame retardant melamine sponge with a commercial fluorosilicone, by using a facile one-step solvent-free approach and demonstrate that the resultant superhydrophobic sponge not only exhibits extraordinary absorption efficiency (including high capacity, superior selectivity, good recyclability, and simple recycling routes), but also retains excellent flame retardancy and robust stability. In comparison to conventional methods, which usually utilize massive organic solvents, the present approach does not involve any complicated process or sophisticated equipment nor generates any waste liquids, and thus is a more labor-saving, environment-friendly, energy-efficient and cost-effective strategy for the hydrophobic modification. Taking into account the critical role of hydrophobic porous materials, especially in the field of environmental remediation, the approach presented herein would be highly valuable for environmental remediation and industrial applications. PMID:27501762

Exposure to flame retardant chemicals on commercial airplanes

PubMed Central

2013-01-01

Background Flame retardant chemicals are used in materials on airplanes to slow the propagation of fire. These chemicals migrate from their source products and can be found in the dust of airplanes, creating the potential for exposure. Methods To characterize exposure to flame retardant chemicals in airplane dust, we collected dust samples from locations inside 19 commercial airplanes parked overnight at airport gates. In addition, hand-wipe samples were also collected from 9 flight attendants and 1 passenger who had just taken a cross-country (USA) flight. The samples were analyzed for a suite of flame retardant chemicals. To identify the possible sources for the brominated flame retardants, we used a portable XRF analyzer to quantify bromine concentrations in materials inside the airplanes. Results A wide range of flame retardant compounds were detected in 100% of the dust samples collected from airplanes, including BDEs 47, 99, 153, 183 and 209, tris(1,3-dichloro-isopropyl)phosphate (TDCPP), hexabromocyclododecane (HBCD) and bis-(2-ethylhexyl)-tetrabromo-phthalate (TBPH). Airplane dust contained elevated concentrations of BDE 209 (GM: 500 ug/g; range: 2,600 ug/g) relative to other indoor environments, such as residential and commercial buildings, and the hands of participants after a cross-country flight contained elevated BDE 209 concentrations relative to the general population. TDCPP, a known carcinogen that was removed from use in children’s pajamas in the 1970’s although still used today in other consumer products, was detected on 100% of airplanes in concentrations similar to those found in residential and commercial locations. Conclusion This study adds to the limited body of knowledge regarding exposure to flame retardants on commercial aircraft, an environment long hypothesized to be at risk for maximum exposures due to strict flame retardant standards for aircraft materials. Our findings indicate that flame retardants are widely used in many airplane components and all airplane types, as expected. Most flame retardants, including TDCPP, were detected in 100% of dust samples collected from the airplanes. The concentrations of BDE 209 were elevated by orders of magnitude relative to residential and office environments. PMID:23413926

Exposure to flame retardant chemicals on commercial airplanes.

PubMed

Allen, Joseph G; Stapleton, Heather M; Vallarino, Jose; McNeely, Eileen; McClean, Michael D; Harrad, Stuart J; Rauert, Cassandra B; Spengler, John D

2013-02-16

Flame retardant chemicals are used in materials on airplanes to slow the propagation of fire. These chemicals migrate from their source products and can be found in the dust of airplanes, creating the potential for exposure. To characterize exposure to flame retardant chemicals in airplane dust, we collected dust samples from locations inside 19 commercial airplanes parked overnight at airport gates. In addition, hand-wipe samples were also collected from 9 flight attendants and 1 passenger who had just taken a cross-country (USA) flight. The samples were analyzed for a suite of flame retardant chemicals. To identify the possible sources for the brominated flame retardants, we used a portable XRF analyzer to quantify bromine concentrations in materials inside the airplanes. A wide range of flame retardant compounds were detected in 100% of the dust samples collected from airplanes, including BDEs 47, 99, 153, 183 and 209, tris(1,3-dichloro-isopropyl)phosphate (TDCPP), hexabromocyclododecane (HBCD) and bis-(2-ethylhexyl)-tetrabromo-phthalate (TBPH). Airplane dust contained elevated concentrations of BDE 209 (GM: 500 ug/g; range: 2,600 ug/g) relative to other indoor environments, such as residential and commercial buildings, and the hands of participants after a cross-country flight contained elevated BDE 209 concentrations relative to the general population. TDCPP, a known carcinogen that was removed from use in children's pajamas in the 1970's although still used today in other consumer products, was detected on 100% of airplanes in concentrations similar to those found in residential and commercial locations. This study adds to the limited body of knowledge regarding exposure to flame retardants on commercial aircraft, an environment long hypothesized to be at risk for maximum exposures due to strict flame retardant standards for aircraft materials. Our findings indicate that flame retardants are widely used in many airplane components and all airplane types, as expected. Most flame retardants, including TDCPP, were detected in 100% of dust samples collected from the airplanes. The concentrations of BDE 209 were elevated by orders of magnitude relative to residential and office environments.

Phosphorylated lignin as a halogen-free flame retardant additive for epoxy composites

Treesearch

Gamini P. Mendis; Sydney G. Weiss; Matthew Korey; Charles R. Boardman; Mark Dietenberger; Jeffrey P. Youngblood; John A. Howarter

2016-01-01

Sustainable, non-halogenated flame retardants are desired for a variety of industry applications. Lignin, as an industrially processed wood derivative, has been examined as a potential sustainable flame retardant additive to polymer systems. Here, the lignin is phosphorylated using a pyridine-catalysed esterification reaction with diphenyl phosphoryl chloride to...

Detection of halogenated flame retardants in polyurethane foam by particle induced X-ray emission

NASA Astrophysics Data System (ADS)

Maley, Adam M.; Falk, Kyle A.; Hoover, Luke; Earlywine, Elly B.; Seymour, Michael D.; DeYoung, Paul A.; Blum, Arlene; Stapleton, Heather M.; Peaslee, Graham F.

2015-09-01

A novel application of particle-induced X-ray emission (PIXE) has been developed to detect the presence of chlorinated and brominated flame retardant chemicals in polyurethane foams. Traditional Gas Chromatography-Mass Spectrometry (GC-MS) methods for the detection and identification of halogenated flame retardants in foams require extensive sample preparation and data acquisition time. The elemental analysis of the halogens in polyurethane foam performed by PIXE offers the opportunity to identify the presence of halogenated flame retardants in a fraction of the time and sample preparation cost. Through comparative GC-MS and PIXE analysis of 215 foam samples, excellent agreement between the two methods was obtained. These results suggest that PIXE could be an ideal rapid screening method for the presence of chlorinated and brominated flame retardants in polyurethane foams.

Flame Suppression Agent, System and Uses

NASA Technical Reports Server (NTRS)

Parrish, Clyde F. (Inventor)

2013-01-01

Aqueous droplets encapsulated in a flame retardant polymer are useful in suppressing combustion. Upon exposure to a flame, the encapsulated aqueous droplets rupture and vaporize, removing heat and displacing oxygen to retard the combustion process. The polymer encapsulant, through decomposition, may further add free radicals to the combustion atmosphere, thereby further retarding the combustion process. The encapsulated aqueous droplets may be used as a replacement to halon, water mist and dry powder flame suppression systems.

Advanced Morphological — Behavioral Test Platform Reveals Neurodevelopmental Defects in Embryonic Zebrafish Exposed to Comprehensive Suite of Halogenated and Organophosphate Flame Retardants

PubMed Central

Noyes, Pamela D.; Haggard, Derik E.; Gonnerman, Greg D.; Tanguay, Robert L.

2015-01-01

The increased use of flammable plastics and electronic devices along with stricter fire safety standards has led to the heavy use of flame retardant chemicals in many consumer, commercial, and industrial products. Although flame retardant use has increased, a great deal of uncertainty surrounds their safety with some evidence showing toxicity and risk to human and environmental health. Recent efforts have focused on designing high-throughput biological platforms with nonmammalian models to evaluate and prioritize chemicals with limited hazard information. To complement these efforts, this study used a new morphological and behavioral testing platform with embryonic zebrafish to characterize the developmental toxicity of 44 halogenated and organophosphate flame retardants, including several of their known metabolites. Zebrafish were exposed to flame retardants from 6 to 120 h post fertilization (hpf) across concentrations spanning 4 orders of magnitude (eg, 6.4 nM to 64 µM). Flame retardant effects on survival and development were evaluated at 24 and 120 hpf, and neurobehavioral changes were measured using 2 photomotor response (PMR) assays. Compared to controls, 93% (41/44) of flame retardants studied elicited adverse effects among one or more of the bioassays and concentrations tested with the aryl phosphate ester (APE)-based mono-isopropylated triaryl phosphate and the brominated-bisphenol-A analog tetrabromobisphenol-A producing the greatest array of malformations. Hierarchical clustering showed that APE flame retardants with isopropyl, butyl, and cresyl substituents on phenyl rings clustered tightly and were particularly potent. Both PMR assays were highly predictive of morphological defects supporting their use as nonlethal means of evaluating teratogenicity that could allow for additional evaluations of long-term or delayed effects in older animals. Taken together, evidence presented here indicates that zebrafish neurodevelopment is highly sensitive to many flame retardants currently in use and can be used to understand potential vulnerabilities to human health. PMID:25711236

Process Optimization of Eco-Friendly Flame Retardant Finish for Cotton Fabric: a Response Surface Methodology Approach

NASA Astrophysics Data System (ADS)

Yasin, Sohail; Curti, Massimo; Behary, Nemeshwaree; Perwuelz, Anne; Giraud, Stephane; Rovero, Giorgio; Guan, Jinping; Chen, Guoqiang

The n-methylol dimethyl phosphono propionamide (MDPA) flame retardant compounds are predominantly used for cotton fabric treatments with trimethylol melamine (TMM) to obtain better crosslinking and enhanced flame retardant properties. Nevertheless, such treatments are associated with a toxic issue of cancer-causing formaldehyde release. An eco-friendly finishing was used to get formaldehyde-free fixation of flame retardant to the cotton fabric. Citric acid as a crosslinking agent along with the sodium hypophosphite as a catalyst in the treatment was utilized. The process parameters of the treatment were enhanced for optimized flame retardant properties, in addition, low mechanical loss to the fabric by response surface methodology using Box-Behnken statistical design experiment methodology was achieved. The effects of concentrations on the fabric’s properties (flame retardancy and mechanical properties) were evaluated. The regression equations for the prediction of concentrations and mechanical properties of the fabric were also obtained for the eco-friendly treatment. The R-squared values of all the responses were above 0.95 for the reagents used, indicating the degree of relationship between the predicted values by the Box-Behnken design and the actual experimental results. It was also found that the concentration parameters (crosslinking reagents and catalysts) in the treatment formulation have a prime role in the overall performance of flame retardant cotton fabrics.

Flame Retardant Exposure among Collegiate U.S. Gymnasts

PubMed Central

Carignan, Courtney C.; Heiger-Bernays, Wendy; McClean, Michael D.; Roberts, Simon C.; Stapleton, Heather M.; Sjödin, Andreas; Webster, Thomas F.

2013-01-01

Gymnastics training facilities contain large volumes of polyurethane foam, a material that often contains additive flame retardants such as PentaBDE. While investigations of human exposure to flame retardants have focused on the general population, potentially higher than background exposures may occur in gymnasts and certain occupational groups. Our objectives were to compare PentaBDE body burden among gymnasts to the general U.S. population and characterize flame retardants levels in gym equipment, air and dust. We recruited 11 collegiate female gymnasts (ages 18–22) from one gym in the Eastern U.S. The geometric mean (GM) concentration of BDE-153 in gymnast sera (32.5 ng/g lipid) was 4–6.5 times higher than general U.S. population groups. Median concentrations of PentaBDE, TBB and TBPH in paired handwipe samples were 2–3 times higher after practice compared to before, indicating the gymnasts contacted these flame retardants during practice. GM concentrations of PentaBDE, TBB and TBPH were 1-3 orders of magnitude higher in gym air and dust than in residences. Our findings suggest that these collegiate gymnasts experienced higher exposures to PentaBDE flame retardants compared to the general U.S. population and that gymnasts may also have increased exposure to other additive flame retardants used in polyurethane foam such as TBB and TBPH. PMID:24195753

Silk flame retardant finish by ternary silica sol containing boron and nitrogen

NASA Astrophysics Data System (ADS)

Zhang, Qiang-hua; Chen, Guo-qiang; Xing, Tie-ling

2017-11-01

A ternary flame retardant sol system containing Si, B and N was prepared via sol gel method using tetraethoxysilane (TEOS) as a precursor, boric acid (H3BO3) and urea (CO(NH2)2) as flame retardant additives and then applied to silk fabric flame retardant finish. The FT-IR and SEM results showed that the nitrogen-boron-silica ternary sol was successfully prepared and entrapped onto the surface of silk fibers. The limiting oxygen index (LOI) test indicated that the silk fabric treated with 24% boric acid and 6% urea (relative to the TEOS) doped ternary silica sol system performed excellent flame retardancy with the LOI value of 34.6%. Furthermore, in order to endow silk fabric with durable flame retardancy, the silk fabric was pretreated with 1,2,3,4-butanetetracarboxylic acid (BTCA) before the ternary sol system treatment. The BTCA pretreat ment applied to silk could effectively promote the washing durability of the ternary sol, and the LOI value of the treated sample after 10 times washing could still maintain at 30.8% compared with that of 31.0% before washing. Thermo gravimetric (TG), micro calorimeter combustion (MCC) and smoke density test results demonstrated that the thermal stability, heat release and smoke suppression of the nitrogen-boron-silica ternary system decreased somewhat compared with the boron-silica binary flame retardant system.

Flame Retardant Fibers for Human Space Exploration - Past, Present, and Future

NASA Technical Reports Server (NTRS)

Orndoff, Evelyne

2017-01-01

The National Aeronautics and Space Administration (NASA) has led in the development of unique flame retardant fibers for human spaceflight since the beginning of the Apollo program. After the Apollo 1 fire which killed Command Pilot Virgil I 'Gus' Grissom, Senior Pilot Edward H. White II, and Pilot Roger B. Chaffee from cardiac arrest on January 27, 1967, the accident investigators found severe third degree burns and melted spacesuits on the astronauts bodies. NASA immediately initiated an extensive research program aimed at developing flame retardant and flame resistant fibers for the enriched oxygen atmosphere of the Apollo crew cabin. Fibers are flame retardant when they have been modified by chemical and thermal treatments. Fibers are flame resistant when they are made of inherently flame resistant materials (i.e. glass, ceramic, highly aromatic polymers). Immediately after this tragic accident, NASA funded extensive research in specifically developing flame retardant fibers and fabrics. The early developmental efforts for human spaceflight were for the outer layer of the Apollo spacesuit. It was imperative that non-flammable fabrics be used in a 100% oxygen environment. Owens-Corning thus developed the Beta fiber that was immediately used in the Apollo program and later in the Space Shuttle program. Aside from the urgent need for protective fabrics for the spacesuit, NASA also needed flame retardant fabrics for both clothing and equipment inside the spacecraft. From the mid-1960s to the early 1980's, NASA contracted with many companies to develop inherently flame retardant fibers and flame retardant finishes for existing fibers. Fluorocarbons and aromatic polyamides were the polymers of great interest for the development of new inherently flame retardant fibers for enriched oxygen environments. These enriched environments varied for different space programs. For example, the Apollo program requirements were for materials that would not support combustion in a 70%/30% oxygen/nitrogen environment at 6.3 pounds per square inch (psi). The Skylab program flammability requirements were set at 80%/20% oxygen/nitrogen ratios at 5 psi. While many fibers produced under several NASA contracts were never used, a few have become commercial products. The intent of this paper is to present the developmental history of some of these new or modified textile fibers. These developmental efforts are presented at various levels of details depending on the source of the historical records.

Part I. improve flame retardant textile. Part II. novel approach layer-by-layer processing for flame retardant textile.

USDA-ARS?s Scientific Manuscript database

In this presentation, new approaches for flame retardant textile by using supercritical carbon dioxide (scCO2) and layer-by-layer processing will be discussed. Due to its environmentally benign character, the scCO2 is considered in green chemistry as a substitute for organic solvents in chemical rea...

Fire self-extinguishing cotton fabric: development of piperazine derivatives containing phosphorous-sulfur-nitrogen and their flame retardant and thermal behaviors

USDA-ARS?s Scientific Manuscript database

Recent studies have shown interest in flame retardants containing phosphorus, nitrogen and sulfur a combination small molecule with a promising new approach in preparing an important class of flame retardant materials. Tetraethyl piperazine-1,4-diyldiphosphonate (TEPP) and O,O,O',O'-tetramethyl pip...

Exploratory Development of Coated Fabric for Fire Proximity Suits

DTIC Science & Technology

1978-06-01

burner flame impinged directly on the surface for 1 minute. The Solucote urethane was the only coating which incorporated a flame retardant , so all the...blistering or flashing in the above test, but only some charring. On the basis of all the above tests, it was decided to use the flame retardant treated...fch4- fabric Wa8 not flame retardant . Consequently this surface coat ignited after 10 seconds of exposure. If ignition had not occurred, this

Brominated and chlorinated flame retardants in San Francisco Bay sediments and wildlife.

PubMed

Klosterhaus, Susan L; Stapleton, Heather M; La Guardia, Mark J; Greig, Denise J

2012-10-15

Restrictions on the use of polybrominated diphenyl ethers (PBDEs) have resulted in the use of alternative flame retardants in consumer products to comply with flammability standards. In contrast to PBDEs, information on the occurrence and fate of these alternative compounds in the environment is limited, particularly in the United States. In this study, a survey of flame retardants in San Francisco Bay was conducted to evaluate whether PBDE replacement chemicals and other current use flame retardants were accumulating in the Bay food web. In addition to PBDEs, brominated and chlorinated flame retardants (hexabromocyclododecane (HBCD) and Dechlorane Plus (DP)) were detected in Bay sediments and wildlife. Median concentrations of PBDEs, HBCD, and DP, respectively, were 4.3, 0.3, and 0.2 ng g⁻¹ dry weight (dw) in sediments; 1670, <6.0, and 0.5 ng g⁻¹ lipid weight (lw) in white croaker (Genyonemus lineatus); 1860, 6.5, and 1.3 ng g⁻¹ lw in shiner surfperch (Cymatogaster aggregata); 5500, 37.4, and 0.9 ng g⁻¹ lw in eggs of double-crested cormorant (Phalacrocorax auritus); 770, 7.1, and 0.9 ng g⁻¹ lw in harbor seal (Phoca vitulina) adults; and 330, 3.5, and <0.1 ng g⁻¹ lw in harbor seal (P. vitulina) pups. Two additional flame retardants, pentabromoethylbenzene (PBEB) and 1,2-bis(2,4,6 tribromophenoxy)ethane (BTBPE) were detected in sediments but with less frequency and at lower concentrations (median concentrations of 0.01 and 0.02 ng g⁻¹ dw, respectively) compared to the other flame retardants. PBEB was also detected in each of the adult harbor seals and in 83% of the pups (median concentrations 0.2 and 0.07 ng g⁻¹ lw, respectively). The flame retardants hexabromobenzene (HBB), decabromodiphenyl ethane (DBDPE), bis(2-ethylhexyl) tetrabromophthalate (TBPH), and 2-ethylhexyl 2,3,4,5-tetrabromobenzoate (TBB), were not detected in sediments and BTBPE, HBB and TBB were not detected in wildlife samples. Elevated concentrations of some flame retardants were likely associated with urbanization and Bay hydrodynamics. Compared to other locations, concentrations of PBDEs in Bay wildlife were comparable or higher, while concentrations of the alternatives were generally lower. This study is the first to determine concentrations of PBDE replacement products and other flame retardants in San Francisco Bay, providing some of the first data on the food web occurrence of these flame retardants in a North American urbanized estuary. Copyright © 2012 Elsevier Ltd. All rights reserved.

Radiation-grafting of flame retardants on flax fabrics - A comparison between different flame retardant structures

NASA Astrophysics Data System (ADS)

Teixeira, Marie; Sonnier, Rodolphe; Otazaghine, Belkacem; Ferry, Laurent; Aubert, Mélanie; Tirri, Teija; Wilén, Carl-Eric; Rouif, Sophie

2018-04-01

Three unsaturated compounds bearing respectively phosphate, aryl bromide and sulfenamide moieties were used as flame retardants (FR) for flax fabrics. Due to the presence of carbon-carbon double bonds, radiation-grafting was considered to covalently bond these FR onto fiber structure. Grafting efficiency and location of FR molecules were investigated by weight measurements and SEM-EDX observations. Flammability and especially self-extinguishment were assessed by thermogravimetric analysis, pyrolysis-combustion flow calorimetry and a non-standardized fire test already used in previous studies. All FRs were able to diffuse into elementary fiber bulk. Nevertheless only the phosphonated monomer (noted FR-P) was significantly grafted onto flax. Self-extinguishment was obtained for fabrics containing at least around 0.5 wt% of phosphorus. On the contrary the FR content of flax fibers after radiation-grafting procedure and washing was negligible for FR-S and FR-Br, evidencing that these molecules have not been grafted upon irradiation. Moreover, the combination of these molecules prevents the radiation-grafting of other molecules which showed good grafting rate when used alone.

Brominated and organophosphate flame retardants target different neurodevelopmental stages, characterized with embryonic neural stem cells and neuronotypic PC12 cells.

PubMed

Slotkin, Theodore A; Skavicus, Samantha; Stapleton, Heather M; Seidler, Frederic J

2017-09-01

In addition to their activity as endocrine disruptors, brominated and organophosphate flame retardants are suspected to be developmental neurotoxicants, although identifying their specific mechanisms for that activity has been elusive. In the current study, we evaluated the effects of several flame retardants on neurodifferentiation using two in vitro models that assess distinct "decision nodes" in neural cell development: embryonic rat neural stem cells (NSCs), which evaluate the origination of neurons and glia from precursors, and rat neuronotypic PC12 cells, which characterize a later stage where cells committed to a neuronal phenotype undergo neurite outgrowth and neurotransmitter specification. In NSCs, both brominated and organophosphate flame retardants diverted the phenotype in favor of glia and away from formation of neurons, leading to an increased glia/neuron ratio, a common hallmark of the in vivo effects of neurotoxicants. For this early decision node, the brominated flame retardants were far more potent than the organophosphates. In PC12 cells, the brominated flame retardants were far less effective, whereas tris (1,3-dichloro-2-propyl) phosphate, an organophosphate, was more effective. Thus, the two classes of flame retardants differentially impact the two distinct vulnerable periods of neurodifferentiation. Furthermore, the effects on neurodifferentiation were separable from outright cytotoxicity, an important requirement in establishing a specific effect of these agents on neural cell development. These results reinforce the likelihood that flame retardants act as developmental neurotoxicants via direct effects on neural cell differentiation, over and above other activities that can impact nervous system development, such as endocrine disruption. Copyright © 2017 Elsevier B.V. All rights reserved.

The presence and partitioning behavior of flame retardants in waste, leachate, and air particles from Norwegian waste-handling facilities.

PubMed

Morin, Nicolas A O; Andersson, Patrik L; Hale, Sarah E; Arp, Hans Peter H

2017-12-01

Flame retardants in commercial products eventually make their way into the waste stream. Herein the presence of flame retardants in Norwegian landfills, incineration facilities and recycling sorting/defragmenting facilities is investigated. These facilities handled waste electrical and electronic equipment (WEEE), vehicles, digestate, glass, combustibles, bottom ash and fly ash. The flame retardants considered included polybrominated diphenyl ethers (∑BDE-10) as well as dechlorane plus, polybrominated biphenyls, hexabromobenzene, pentabromotoluene and pentabromoethylbenzene (collectively referred to as ∑FR-7). Plastic, WEEE and vehicles contained the largest amount of flame retardants (∑BDE-10: 45,000-210,000μg/kg; ∑FR-7: 300-13,000μg/kg). It was hypothesized leachate and air concentrations from facilities that sort/defragment WEEE and vehicles would be the highest. This was supported for total air phase concentrations (∑BDE-10: 9000-195,000pg/m 3 WEEE/vehicle facilities, 80-900pg/m 3 in incineration/sorting and landfill sites), but not for water leachate concentrations (e.g., ∑BDE-10: 15-3500ng/L in WEEE/Vehicle facilities and 1-250ng/L in landfill sites). Landfill leachate exhibited similar concentrations as WEEE/vehicle sorting and defragmenting facility leachate. To better account for concentrations in leachates at the different facilities, waste-water partitioning coefficients, K waste were measured (for the first time to our knowledge for flame retardants). WEEE and plastic waste had elevated K waste compared to other wastes, likely because flame retardants are directly added to these materials. The results of this study have implications for the development of strategies to reduce exposure and environmental emissions of flame retardants in waste and recycled products through improved waste management practices. Copyright © 2017. Published by Elsevier B.V.

Formulation of intumescent flame retardant coatings containing natural-based tea saponin.

PubMed

Qian, Wei; Li, Xiang-Zhou; Wu, Zhi-Ping; Liu, Yan-Xin; Fang, Cong-Cong; Meng, Wei

2015-03-18

Natural product tea saponin (TS), extracted from the nutshell of camellia (Camellia oleifera Abel, Theaceae), was introduced into intumescent flame retardant formulations as blowing agent and carbon source. The formulations of the flame retardant system were optimized to get the optimum proportion of TS, and intumescent flame retardant coatings containing tea saponin (TS-IFRCs) were then prepared. It was found that TS can significantly affect the combustion behavior and the thermal stability of TS-IFRCs evaluated by cone calorimetry and simultaneous thermal analyzer, respectively. It was shown that TS, degraded to water vapor and carbon at high temperatures, can combine with other components to form a well-developed char layer. The char layer was supposed to inhibit erosion upon exposure to heat and oxygen and enhance the flame retardancy of TS-IFRCs. In addition, the smoke release of TS-IFRCs was also studied, which provided a low amount of smoke production.

Thermal and mechanical behavior of flame retardant epoxy-polyesterurethane blends

NASA Astrophysics Data System (ADS)

Patel, R. H.; Hirani, A. V.; Kachhia, P. H.

2016-05-01

Polyesterurethanes are used in different applications due to their unique combination of the properties like toughness, flexibility, solvent resistance, etc. Nowadays flame retardant properties of polymers are of commercial interest because of their potential use in high performance applications. In the present study attempts have been taken to improve the flame retardant properties of conventional epoxy resin by incorporating phosphorus based polyesterurethane. Polyesterurethane has been synthesized in the laboratory and characterized by chemical and instrumental analysis techniques. Thermal stability and char value of the blends have been determined using thermogravimetric analysis technique. Limiting Oxygen Index (LOI) and UL-94 test methods have been used to determine the flame retardant properties of neat polymer and their blends in film form. Mechanical properties like tensile strength, elongation and impact resistance of the blends have been found out. Polyblend of epoxy resin with phosphorus based polyesterurethane has improved flame retardant properties compare to neat epoxy resin.

A new strategy to produce low-density polyethylene (LDPE)-based composites simultaneously with high flame retardancy and high mechanical properties

NASA Astrophysics Data System (ADS)

Shen, Liguo; Li, Jianxi; Li, Renjie; Lin, Hongjun; Chen, Jianrong; Liao, Bao-Qiang

2018-04-01

In this study, a new strategy which blends low-density polyethylene (LDPE), magnesium hydroxide (MH) and lauryl acrylate by electron-beam radiation for production of LDPE-based composites with high performance was proposed. It was found that, MH played main roles in flame retardancy but reduced processing flow and mechanical properties of the composites. Meanwhile, melt flow rate (MFR) increased while viscosity of the composites decreased with lauryl acrylate content increased, facilitating LDPE composites processing. Electron beam radiation could prompt crosslinking of lauryl acrylate, which significantly enhanced the mechanical properties of LDPE composites. Meanwhile, lauryl acrylate addition only slightly decreased the flame retardancy, suggesting that LDPE composites could remain high flame retardancy even when lauryl acrylate content was high. The study highly demonstrated the feasibility to produce LDPE-based composites simultaneously with high flame retardancy and high mechanical properties by the blending strategy provided in this study.

Nanocellular foam with solid flame retardant

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Liang; Kelly-Rowley, Anne M.; Bunker, Shana P.

Prepare nanofoam by (a) providing an aqueous solution of a flame retardant dissolved in an aqueous solvent, wherein the flame retardant is a solid at 23.degree. C. and 101 kiloPascals pressure when in neat form; (b) providing a fluid polymer composition selected from a solution of polymer dissolved in a water-miscible solvent or a latex of polymer particles in a continuous aqueous phase; (c) mixing the aqueous solution of flame retardant with the fluid polymer composition to form a mixture; (d) removing water and, if present, solvent from the mixture to produce a polymeric composition having less than 74 weight-percentmore » flame retardant based on total polymeric composition weight; (e) compound the polymeric composition with a matrix polymer to form a matrix polymer composition; and (f) foam the matrix polymer composition into nanofoam having a porosity of at least 60 percent.« less

Flame-retardant EPDM compounds containing phenanthrene to enhance radiation resistance

NASA Astrophysics Data System (ADS)

Chen, Jian; Huang, Wei; Jiang, Shu-Bin; Li, Xiao-Yan; An, You; Li, Chuang; Gao, Xiao-Ling; Chen, Hong-Bing

2017-01-01

Ethylene propylene diene monomer (EPDM) compounds with good flame-retardant and γ-ray radiation resistant properties were prepared by adding complex flame retardants and phenathrene. The resultant EPDM formulations have a long time to ignition (TTI >46 s), a low peak heat release rate (PHRR 341 kW/m2) and a high limited oxygen index (LOI >30). Effects of γ-ray radiation on the resultant flame-retardant EPDM was investigated. The formulated EPDM is a crosslinking dominated polymer under γ-ray radiation. The γ-ray radiation resistant property of EPDM was enhanced by adding phenanthrene. Elongation at break of EPDM formulated with phenanthrene could retain 91% after being irradiated to 0.3 MGy and still retains 40% elongation even after being irradiated to 0.9 MGy, which is much better the control. It is expected that the formulated flame-retardant and radiation resistant EPDM materials could meet the requirements for use in radiation environments.

Part I. Improved flame retardant textiles. Part II. Novel approach to layer-by-layer processing for flame retardant textiles.

USDA-ARS?s Scientific Manuscript database

In this presentation, new approaches for flame retardant textile by using supercritical carbon dioxide (scCO2) and layer-by-layer processing will be discussed. Due to its environmentally benign character, the scCO2 is considered in green chemistry as a substitute for organic solvents in chemical re...

Flame Retardancy of Chemically Modified Lignin as Functional Additive to Epoxy Nanocomposites

Treesearch

John A. Howarter; Gamini P. Mendis; Alex N. Bruce; Jeffrey P. Youngblood; Mark A. Dietenberger; Laura Hasburgh

2015-01-01

Epoxy printed circuit boards are used in a variety of electronics applications as rigid, thermally stable substrates. Due to the propensity of components on the boards, such as batteries and interconnects, to fail and ignite the epoxy, flame retardant additives are required to minimize fire risk. Currently, industry uses brominated flame retardants, such as TBBPA, to...

Fabrication of Cellulose Nanofiber/AlOOH Aerogel for Flame Retardant and Thermal Insulation

PubMed Central

Fan, Bitao; Chen, Shujun; Yao, Qiufang; Sun, Qingfeng; Jin, Chunde

2017-01-01

Cellulose nanofiber/AlOOH aerogel for flame retardant and thermal insulation was successfully prepared through a hydrothermal method. Their flame retardant and thermal insulation properties were investigated. The morphology image of the cellulose nanofiber/AlOOH exhibited spherical AlOOH with an average diameter of 0.5 μm that was wrapped by cellulose nanofiber or adhered to them. Cellulose nanofiber/AlOOH composite aerogels exhibited excellent flame retardant and thermal insulation properties through the flammability test, which indicated that the as-prepared composite aerogels would have a promising future in the application of some important areas such as protection of lightweight construction materials. PMID:28772670

Flame retardant finishing of cotton fabric based on synergistic compounds containing boron and nitrogen.

PubMed

Xie, Kongliang; Gao, Aiqin; Zhang, Yongsheng

2013-10-15

Boric acid and compound containing nitrogen, 2,4,6-tri[(2-hydroxy-3-trimethyl-ammonium)propyl]-1,3,5-triazine chloride (Tri-HTAC) were used to finish cotton fabric. The flame retardant properties of the finished cotton fabrics and the synergetic effects of boron and nitrogen elements were investigated and evaluated by limited oxygen index (LOI) method. The mechanism of cross-linking reaction among cotton fiber, Tri-HTAC, and boric acid was discussed by FTIR and element analysis. The thermal stability and surface morphology of the finished cotton fabrics were investigated by thermogravimetric analysis (TGA) and scanning electron microscope (SEM), respectively. The finishing system of the mixture containing boron and nitrogen showed excellent synergistic flame retardancy for cotton fabric. The cotton fabric finished with mixture system had excellent flame retardancy. The LOI value of the treated cotton fabric increased over 27.5. Tri-HTAC could form covalent bonds with cellulose fiber and boric acid. The flame retardant cotton fabric showed a slight decrease in tensile strength and whiteness. The surface morphology of flame retardant cotton fiber was smooth. Copyright © 2013 Elsevier Ltd. All rights reserved.

Efficient Flame Detection and Early Warning Sensors on Combustible Materials Using Hierarchical Graphene Oxide/Silicone Coatings.

PubMed

Wu, Qian; Gong, Li-Xiu; Li, Yang; Cao, Cheng-Fei; Tang, Long-Cheng; Wu, Lianbin; Zhao, Li; Zhang, Guo-Dong; Li, Shi-Neng; Gao, Jiefeng; Li, Yongjin; Mai, Yiu-Wing

2018-01-23

Design and development of smart sensors for rapid flame detection in postcombustion and early fire warning in precombustion situations are critically needed to improve the fire safety of combustible materials in many applications. Herein, we describe the fabrication of hierarchical coatings created by assembling a multilayered graphene oxide (GO)/silicone structure onto different combustible substrate materials. The resulting coatings exhibit distinct temperature-responsive electrical resistance change as efficient early warning sensors for detecting abnormal high environmental temperature, thus enabling fire prevention below the ignition temperature of combustible materials. After encountering a flame attack, we demonstrate extremely rapid flame detection response in 2-3 s and excellent flame self-extinguishing retardancy for the multilayered GO/silicone structure that can be synergistically transformed to a multiscale graphene/nanosilica protection layer. The hierarchical coatings developed are promising for fire prevention and protection applications in various critical fire risk and related perilous circumstances.

Analysis of surface tris (2,3-dibromopropyl) phosphate on chlorobutyl rubber SCAPE suits. [flame retardant coatings

NASA Technical Reports Server (NTRS)

Schehl, T. A.; Bennett, H. D.; Bryan, C. J.; Bright, C. W.

1978-01-01

Tris (2,30-dibromopropyl) phosphate was used to confer flame retardant properties on butyl rubber formulations used in protective clothing such as the self-contained atmospheric protective ensembles (SCAPE suits) worn at Kennedy Space Center in support of Apollo, Skylab, and Apollo-Soyuz missions since 1966. Because tris (2,3-dibromopropyl) phosphate is mutagenic, surface concentrations of the compound in SCAPE suits were investigated as were as potential methods of removing or isolating it. Analytical procedures for determining surface concentrations of the tris compound on non-porous materials are described. Soap-and-water washing is the most efficient method of removing the compound from fabricated SCAPE suits and unused material.

Synthesis of a Novel Phosphorus-Containing Flame Retardant Curing Agent and Its Application in Epoxy Resins.

PubMed

Zhang, Hongkun; Xu, Miaojun; Li, Bin

2016-03-01

A novel phosphorus-containing compound diphenyl-(2,5-dihydroxyphenyl)-phosphine oxide defined as DPDHPPO was synthesized and used as flame retardant and curing agent for epoxy resins (EP). The chemical structure was well characterized by Fourier transform infrared (FTIR) spectroscopy, 1H, 13C and 31P nuclear magnetic resonance. The flame retardant properties, combusting performances and thermal degradation behaviors of the cured epoxy resins were investigated by limiting oxygen index (LOI), vertical burning tests (UL-94), cone calorimeter and thermogravimetric analysis (TGA) tests. The morphologies and chemical compositions of char residues for cured epoxy resins were investigated by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), respectively. The water resistant properties were evaluated by putting the samples into distilled water at 70 degrees C for 168 h. The results revealed that the EP/40 wt% DPDHPPO/60 wt% PDA thermosets successfully passed UL-94 V-0 flammability rating and the LOI value was as high as 31.9%. The cone tests results revealed that the incorporation of DPDHPPO efficiently reduced the combustion parameters of epoxy resins thermosets, such as heat release rate (HRR), total heat release (THR) and so on. The TGA results indicated that the introduction of DPDHPPO promoted epoxy resins matrix decomposed ahead of time compared with that of pure EP and led to a higher char yield and thermal stability at high temperature. The morphological structures and analysis of XPS of char residues revealed that DPDHPPO benefited to the formation of a sufficient, compact and homogeneous char layer with rich flame retardant elements on the epoxy resins materials surface during combustion. After water resistance tests, EP/40 wt% DPDHPPO/60 wt% PDA thermosets still remained excellent flame retardancy, the moisture absorption of epoxy resins thermosets decreased with the increase of DPDHPPO contents in the thermosets due to the existing of P-C bonds and the rigid aromatic hydrophobic structure.

Using silicone wristbands to evaluate preschool children’s exposure to flame retardants

PubMed Central

Kile, Molly L.; Scott, Richard P.; O’Connell, Steven G.; Lipscomb, Shannon; MacDonald, Megan; McClelland, Megan; Anderson, Kim A.

2016-01-01

Silicone wristbands can be used as passive sampling tools for measuring personal environmental exposure to organic compounds. Due to the lightweight and simple design, the wristband may be a useful technique for measuring children’s exposure. In this study, we tested the stability of flame retardant compounds in silicone wristbands and developed an analytical approach for measuring 41 flame retardants in the silicone wristband in order to evaluate exposure to these compounds in preschool-aged children. To evaluate the robustness of using wristbands to measure flame retardants, we evaluated the stability of 3 polybrominated diphenyl ethers (BDEs), and 2 organophosphate flame retardants (OPFRs) in wristbands over 84 days and did not find any evidence of significant loss over time at either 4 or −20°C (p > 0.16). We recruited a cohort of 92 preschool aged children in Oregon to wear the wristband for 7 days in order to characterize children’s acceptance of the technology, and to characterize their exposure to flame retardants. Seventy-seven parents returned the wristbands for analysis of 35 BDEs, 4 OPFRs, and 2 other brominated flame retardants although 5 were excluded from the exposure assessment due to protocol deviations (n=72). A total of 20 compounds were detected above the limit of quantitation, and 11 compounds including 4 OPFRs and 7 BDEs were detected in over 60% of the samples. Children’s gender, age, race, recruitment site, and family context were not significantly associated with returning wristbands or compliance with protocols. Comparisons between flame retardant data and socio-demographic information revealed significant differences in total exposures to both ΣBDEs and ΣOPFRs based on age of house, vacuuming frequency, and family context. These results demonstrate that preschool children in Oregon are exposed to BDEs that are no longer being produced in the United States and to OPFRs that have been used as an alternative to polybrominated compounds. Silicone wristbands were well tolerated by young children and were useful for characterizing personal exposure to flame retardants that were not bound to particulate matter. PMID:26945619

Potential human exposure to halogenated flame-retardants in elevated surface dust and floor dust in an academic environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Allgood, Jaime M.; Jimah, Tamara

Most households and workplaces all over the world possess furnishings and electronics, all of which contain potentially toxic flame retardant chemicals to prevent fire hazards. Indoor dust is a recognized repository of these types of chemicals including polybrominated diphenyl ethers (PBDEs) and non-polybrominated diphenyl ethers (non-PBDEs). However, no previous U.S. studies have differentiated concentrations from elevated surface dust (ESD) and floor dust (FD) within and across microenvironments. We address this information gap by measuring twenty-two flame-retardant chemicals in dust on elevated surfaces (ESD; n=10) and floors (FD; n=10) from rooms on a California campus that contain various concentrations of electronicmore » products. We hypothesized a difference in chemical concentrations in ESD and FD. Secondarily, we examined whether or not this difference persisted: (a) across the studied microenvironments and (b) in rooms with various concentrations of electronics. A Wilcoxon signed-rank test demonstrated that the ESD was statistically significantly higher than FD for BDE-47 (p=0.01), BDE-99 (p=0.01), BDE-100 (p=0.01), BDE-153 (p=0.02), BDE-154 (p=0.02), and 3 non-PBDEs including EH-TBB (p=0.02), BEH-TEBP (p=0.05), and TDCIPP (p=0.03). These results suggest different levels and kinds of exposures to flame-retardant chemicals for individuals spending time in the sampled locations depending on the position of accumulated dust. Therefore, further research is needed to estimate human exposure to flame retardant chemicals based on how much time and where in the room individuals spend their time. Such sub-location estimates will likely differ from assessments that assume continuous unidimensional exposure, with implications for improved understanding of potential health impacts of flame retardant chemicals. - Highlights: • Brominated flame retardants used in electronic products accumulate in room dust • Various chemical moieties of flame retardants leach differently into room dust • Flame retardant concentrations in dust differ in elevated surfaces compared to floors.« less

Biodegradation of brominated and organophosphorus flame retardants.

PubMed

Waaijers, Susanne L; Parsons, John R

2016-04-01

Brominated flame retardants account for about 21% of the total production of flame retardants and many of these have been identified as persistent, bioaccumulative and toxic. Nevertheless, debromination of these chemicals under anaerobic conditions is well established, although this can increase their toxicity. Consequently, the production and use of these chemicals has been restricted and alternative products have been developed. Many of these are brominated compounds and share some of the disadvantages of the chemicals they are meant to replace. Therefore, other, nonbrominated, flame retardants such as organophosphorus compounds are also being used in increasing quantities, despite the fact that knowledge of their biodegradation and environmental fate is often lacking. Copyright © 2015 Elsevier Ltd. All rights reserved.

EFFECT OF ORGANOPHOSPHORUS FLAME RETARDANTS ON NEURONAL DEVELOPMENT IN VITRO

EPA Science Inventory

The increased use of organophosphorus compounds as alternatives to brominated flame retardants (BFRs) has led to widespread human exposure, There is, however, limited information on their potential health effects. This study compared the effects of nii ne organophosphorus flame...

Natural Rubber/Dendrimer Modified Montmorillonite Nanocomposites: Mechanical and Flame-Retardant Properties

PubMed Central

Zhang, Chenyang; Wang, Jincheng

2017-01-01

A series of flame-retardant nanocomposites were established based on compounding of natural rubber (NR) and dendrimer modified flame-retardant organic montmorillonite (FR-DOMt). The merits of these nanocomposites were focused on their better mechanical and flame-retardant properties. X-ray diffractometer (XRD) together with scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analysis revealed that exfoliation, intercalation, or aggregation status in the NRmatrix can be achieved by addition of different amounts of FR-DOMt. The sound effects of blend ratio of FR-DOMt on mechanical, thermal stability, and flame-retardant (FR) properties of NR were studied. The NR/FR-DOMt-20 composite possessed the highest tensile strength, and this resulted from complicated interactions between layered silicates and elastomers. In addition, with loading of 20 phr of FR-DOMt, the flammability parameters of NR, such as heat release rate (HRR), smoke evolution area (SEA), and carbon monoxide (CO) concentration, were obviously reduced from cone calorimeter analysis. PMID:29283385

[Progress in environmental exposure of organophosphate flame retardants].

PubMed

Ding, J J; Yang, F X

2017-06-06

Organophosphate flame retardants (OPFRs), which have both great properties of flame retardation and plasticization, are currently widely used as additive flame retardants. Due to the restriction and phase-out of brominated flame retardants (BFRs), the market demand for OPFRs as excellent alternatives of BFRs has been rapid increasing. OPFRs can be slowly released into the environment during production and application. Some OPFRs might be persistent in the environment. As a result, OPFRs have been detected in various matrices in the environment and are expected to accumulate in human body through various pathways. OPFRs may cause adverse effects to human health as some of them have been identified as neurotoxicants, reproductive toxicants and potential carcinogens. The article summarized the occurrence and patterns of OPFRs in various environmental matrices such as air, dust, water, food and so on, and in human specimens, estimates the exposure status through different pathways and body burdens of OPFRs. The expected hotspots of OPFRs were also discussed in the future.

Flame-retardant-wrapped polyphosphazene nanotubes: A novel strategy for enhancing the flame retardancy and smoke toxicity suppression of epoxy resins.

PubMed

Qiu, Shuilai; Wang, Xin; Yu, Bin; Feng, Xiaming; Mu, Xiaowei; Yuen, Richard K K; Hu, Yuan

2017-03-05

The structure of polyphosphazene nanotubes (PZS) is similar to that of carbon nanotubes (CNTs) before modification. For applications of CNTs in polymer composites, surface wrapping is an economically attractive route to achieve functionalized nanotubes. Based on this idea, functionalized polyphosphazene nanotubes (FR@PZS) wrapped with a cross-linked DOPO-based flame retardant (FR) were synthesized via one-step strategy and well characterized. Then, the obtained FR@PZS was introduced into epoxy resin (EP) to investigate flame retardancy and smoke toxicity suppression performance. Thermogravimetric analysis indicated that FR@PZS significantly enhanced the thermal stability of EP composites. Cone calorimeter results revealed that incorporation of FR@PZS obviously improved flame retardant performance of EP, for example, 46.0% decrease in peak heat release rate and 27.1% reduction in total heat release were observed in the case of epoxy composite with 3wt% FR@PZS. The evolution of toxic CO and other volatile products from the EP decomposition was significantly suppressed after the introduction of FR@PZS, Therefore, the smoke toxicity associates with burning EP was reduced. The presence of both PZS and a DOPO-based flame retardant was probably responsible for this substantial diminishment of fire hazard. Copyright © 2016 Elsevier B.V. All rights reserved.

Electrospun core-shell microfiber separator with thermal-triggered flame-retardant properties for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Kai; Liu, Wei; Qiu, Yongcai

Although the energy densities of batteries continue to increase, safety problems (for example, fires and explosions) associated with the use of highly flammable liquid organic electrolytes remain a big issue, significantly hindering further practical applications of the next generation of high-energy batteries. We have fabricated a novel “smart” nonwoven electrospun separator with thermal-triggered flame-retardant properties for lithium-ion batteries. The encapsulation of a flame retardant inside a protective polymer shell has prevented direct dissolution of the retardant agent into the electrolyte, which would otherwise have negative effects on battery performance. Furthermore, during thermal runaway of the lithium-ion battery, the protective polymermore » shell would melt, triggered by the increased temperature, and the flame retardant would be released, thus effectively suppressing the combustion of the highly flammable electrolytes.« less

Electrospun core-shell microfiber separator with thermal-triggered flame-retardant properties for lithium-ion batteries

DOE PAGES

Liu, Kai; Liu, Wei; Qiu, Yongcai; ...

2017-01-13

Although the energy densities of batteries continue to increase, safety problems (for example, fires and explosions) associated with the use of highly flammable liquid organic electrolytes remain a big issue, significantly hindering further practical applications of the next generation of high-energy batteries. We have fabricated a novel “smart” nonwoven electrospun separator with thermal-triggered flame-retardant properties for lithium-ion batteries. The encapsulation of a flame retardant inside a protective polymer shell has prevented direct dissolution of the retardant agent into the electrolyte, which would otherwise have negative effects on battery performance. Furthermore, during thermal runaway of the lithium-ion battery, the protective polymermore » shell would melt, triggered by the increased temperature, and the flame retardant would be released, thus effectively suppressing the combustion of the highly flammable electrolytes.« less

Electrospun core-shell microfiber separator with thermal-triggered flame-retardant properties for lithium-ion batteries

PubMed Central

Liu, Kai; Liu, Wei; Qiu, Yongcai; Kong, Biao; Sun, Yongming; Chen, Zheng; Zhuo, Denys; Lin, Dingchang; Cui, Yi

2017-01-01

Although the energy densities of batteries continue to increase, safety problems (for example, fires and explosions) associated with the use of highly flammable liquid organic electrolytes remain a big issue, significantly hindering further practical applications of the next generation of high-energy batteries. We have fabricated a novel “smart” nonwoven electrospun separator with thermal-triggered flame-retardant properties for lithium-ion batteries. The encapsulation of a flame retardant inside a protective polymer shell has prevented direct dissolution of the retardant agent into the electrolyte, which would otherwise have negative effects on battery performance. During thermal runaway of the lithium-ion battery, the protective polymer shell would melt, triggered by the increased temperature, and the flame retardant would be released, thus effectively suppressing the combustion of the highly flammable electrolytes. PMID:28097221

Electrospun core-shell microfiber separator with thermal-triggered flame-retardant properties for lithium-ion batteries.

PubMed

Liu, Kai; Liu, Wei; Qiu, Yongcai; Kong, Biao; Sun, Yongming; Chen, Zheng; Zhuo, Denys; Lin, Dingchang; Cui, Yi

2017-01-01

Although the energy densities of batteries continue to increase, safety problems (for example, fires and explosions) associated with the use of highly flammable liquid organic electrolytes remain a big issue, significantly hindering further practical applications of the next generation of high-energy batteries. We have fabricated a novel "smart" nonwoven electrospun separator with thermal-triggered flame-retardant properties for lithium-ion batteries. The encapsulation of a flame retardant inside a protective polymer shell has prevented direct dissolution of the retardant agent into the electrolyte, which would otherwise have negative effects on battery performance. During thermal runaway of the lithium-ion battery, the protective polymer shell would melt, triggered by the increased temperature, and the flame retardant would be released, thus effectively suppressing the combustion of the highly flammable electrolytes.

Cross-sectional study of social behaviors in preschool children and exposure to flame retardants.

PubMed

Lipscomb, Shannon T; McClelland, Megan M; MacDonald, Megan; Cardenas, Andres; Anderson, Kim A; Kile, Molly L

2017-03-09

Children are exposed to flame retardants from the built environment. Brominated diphenyl ethers (BDE) and organophosphate-based flame retardants (OPFRs) are associated with poorer neurocognitive functioning in children. Less is known, however, about the association between these classes of compounds and children's emotional and social behaviors. The objective of this study was to determine if flame retardant exposure was associated with measurable differences in social behaviors among children ages 3-5 years. We examined teacher-rated social behaviors measured using the Social Skills Improvement Rating Scale (SSIS) and personal exposure to flame retardants in children aged 3-5 years who attended preschool (n = 72). Silicone passive samplers worn for 7 days were used to assess personal exposure to 41 compounds using gas chromatography-mass spectrophotometer. These concentrations were then summed into total BDE and total OPFR exposure prior to natural log transformation. Separate generalized additive models were used to evaluate the relationship between seven subscales of the SSIS and lnΣBDE or lnΣOPFR adjusting for other age, sex, adverse social experiences, and family context. All children were exposed to a mixture of flame retardant compounds. We observed a dose dependent relationship between lnΣOPFR and two subscales where children with higher exposures were rated by their preschool teachers as having less responsible behavior (p = 0.07) and more externalizing behavior problems (p = 0.03). Additionally, children with higher lnΣBDE exposure were rated by teachers as less assertive (p = 0.007). We observed a cross-sectional association between children's exposure to flame retardant compounds and teacher-rated social behaviors among preschool-aged children. Children with higher flame retardant exposures exhibited poorer social skills in three domains that play an important role in a child's ability to succeed academically and socially.

Unique synergism in flame retardancy in ABS based composites through blending PVDF and halloysite nanotubes

NASA Astrophysics Data System (ADS)

Remanan, Sanjay; Sharma, Maya; Jayashree, Priyadarshini; Parameswaranpillai, Jyotishkumar; Fabian, Thomas; Shih, Julie; Shankarappa, Prasad; Nuggehalli, Bharath; Bose, Suryasarathi

2017-06-01

This study demonstrates flame retardant materials designed using bi-phasic polymer blends of acrylonitrile butadiene styrene (ABS) and polyvinylidene fluoride (PVDF) containing halloysite nanotubes (HNTs) and Cloisite 30B nanoclay. The prepared blends with and without nanoparticles were extensively characterized. The nanoparticles were added in different weight concentrations to improve the flame retardancy. It was observed that prepared ABS/PVDF blends showed better flame retardancy than ABS based composites. The flame resistance was further improved by the addition of nanoparticles in the blends. The microscale combustion calorimetry (MCC) test showed better flame resistance in ABS/PVDF blends filled with 5 wt% HNTs than other composites. The total heat release of ABS/PVDF blend filled with 5 wt% HNTs decreased by 31% and also the heat of combustion decreased by 26% as compared to neat ABS. When compared with nanoparticles, the addition of PVDF reduced the peak heat release rate (PHRR) and increased the char residue more effectively. A synergistic improvement was observed from both PVDF and HNTs on the flame resistance properties.

Flammability and thermal properties studies of nonwoven flax reinforced acrylic based polyester composites

NASA Astrophysics Data System (ADS)

Rasyid, M. F. Ahmad; Salim, M. S.; Akil, H. M.; Ishak, Z. A. Mohd.

2017-12-01

In the pursuit of green and more sustainable product, natural fibre reinforced composites originating from renewable resources has gained interest in recent years. These natural fibres exhibit good mechanical properties, low production costs, and good environmental properties. However, one of the disadvantages of natural fibre reinforced composites is their high flammability that limits their application in many fields. Within this research, the effect of sodium silicate on the flammability and thermal properties of flax reinforced acrylic based polyester composites has been investigated. Sodium silicate is applied as binder and flame retardant system in impregnation process of the natural flax fiber mats. The addition of sodium silicate significantly improved the flame retardant efficiency but reduced the degree of crosslinking of the composites.

Super flame-retardant lightweight rime-like carbon-phenolic nanofoam

PubMed Central

Cheng, Haiming; Hong, Changqing; Zhang, Xinghong; Xue, Huafei; Meng, Songhe; Han, Jiecai

2016-01-01

The desire for lightweight nanoporous materials with high-performance thermal insulation and efficient anti-ablation resistance for energy conservation and thermal protection/insulation has greatly motivated research and development recently. The main challenge to synthesize such lightweight materials is how to balance the relationship of low thermal conductivity and flame retardancy. Herein, we propose a new concept of lightweight “rime-like” structured carbon-phenolic nanocomposites to solve this problem, where the 3D chopped network-structured carbon fiber (NCF) monoliths are incorporated with nanoporous phenolic aerogel to retain structural and functional integrity. The nanometer-scaled porous phenolic (NP) was synthesized through polymerization-induced phase separation and ambient pressure drying using phenolic resin (PR) solution as reaction source, ethylene glycol (EG) as solvent and hexamethylenetetramine (HMTA) as catalyst. We demonstrate that the as-prepared NCF-NP nanocomposite exhibits with a low density of 0.25–0.35 g/cm3, low thermal conductivity of 0.125 Wm−1K−1 and outstanding flame retardancy exceeding 2000 °C under arc-jet wind tunnel simulation environment. Our results show that the synthesis strategy is a promising approach for producing nanocomposites with excellent high-temperature heat blocking property. PMID:27629114

Super flame-retardant lightweight rime-like carbon-phenolic nanofoam

NASA Astrophysics Data System (ADS)

Cheng, Haiming; Hong, Changqing; Zhang, Xinghong; Xue, Huafei; Meng, Songhe; Han, Jiecai

2016-09-01

The desire for lightweight nanoporous materials with high-performance thermal insulation and efficient anti-ablation resistance for energy conservation and thermal protection/insulation has greatly motivated research and development recently. The main challenge to synthesize such lightweight materials is how to balance the relationship of low thermal conductivity and flame retardancy. Herein, we propose a new concept of lightweight “rime-like” structured carbon-phenolic nanocomposites to solve this problem, where the 3D chopped network-structured carbon fiber (NCF) monoliths are incorporated with nanoporous phenolic aerogel to retain structural and functional integrity. The nanometer-scaled porous phenolic (NP) was synthesized through polymerization-induced phase separation and ambient pressure drying using phenolic resin (PR) solution as reaction source, ethylene glycol (EG) as solvent and hexamethylenetetramine (HMTA) as catalyst. We demonstrate that the as-prepared NCF-NP nanocomposite exhibits with a low density of 0.25-0.35 g/cm3, low thermal conductivity of 0.125 Wm-1K-1 and outstanding flame retardancy exceeding 2000 °C under arc-jet wind tunnel simulation environment. Our results show that the synthesis strategy is a promising approach for producing nanocomposites with excellent high-temperature heat blocking property.

Method for producing flame retardant porous products and products produced thereby

DOEpatents

Salyer, Ival O.

1998-08-04

A method for fire retarding porous products used for thermal energy storage and products produced thereby is provided. The method includes treating the surface of the phase change material-containing porous products with a urea fire-retarding agent. Upon exposure to a flame, the urea forms an adduct with the phase change material which will not sustain combustion (is self-extinguishing) in air. No halogens or metal oxides are contained in the fire retardant, so no potentially noxious halide smoke or fumes are emitted if the product is continuously exposed to a flame.

Method for producing flame retardant porous products and products produced thereby

DOEpatents

Salyer, I.O.

1998-08-04

A method for fire retarding porous products used for thermal energy storage and products produced thereby is provided. The method includes treating the surface of the phase change material-containing porous products with a urea fire-retarding agent. Upon exposure to a flame, the urea forms an adduct with the phase change material which will not sustain combustion (is self-extinguishing) in air. No halogens or metal oxides are contained in the fire retardant, so no potentially noxious halide smoke or fumes are emitted if the product is continuously exposed to a flame. 1 fig.

Method for Producing Flame Retardant Porous Products and Products Produced Thereby

DOEpatents

Salyer, Ival O.

1998-08-04

A method for fire retarding porous products used for thermal energy storage and products produced thereby is provided. The method includes treating the surface of the phase change material-containing porous products with a urea fire-retarding agent. Upon exposure to a flame, the urea forms an adduct with the phase change material which will not sustain combustion (is self-extinguishing) in air. No halogens or metal oxides are contained in the fire retardant, so no potentially noxious halide smoke or fumes are emitted if the product is continuously exposed to a flame.

Cone calorimeter evaluation of two flame retardant cotton fabrics

USDA-ARS?s Scientific Manuscript database

Unbleached (grey) cotton needle punched nonwoven (NW) fabrics with 12.5% polypropylene scrim were treated with two phosphate-nitrogen based fire-retardant (FR) formulations, SRRC-1 and SRRC-2. The SRRC-1 formulation contains diammonium phosphate as the flame retardant chemical along with urea and d...

Organophosphate flame retardants in household dust before and after introduction of new furniture.

PubMed

Keimowitz, A R; Strunsky, N; Wovkulich, K

2016-04-01

Flame retardant compounds originating from household items collect in household dust, a reasonable proxy for human exposure. Contributions of specific items or behaviors to dust are difficult to separate. This study examined standardized college housing before and after the introduction of new, flame retardant couches in order to explore any effect that changing upholstered furniture may have on flame retardant concentrations in dust. Two contradictory hypotheses were posited: (1) that new furniture might increase flame retardant releases immediately after introduction due to initial off-gassing of new materials or (2) that older furniture would release more flame retardants due to mechanical breakdown of polyurethane foam. This study was designed to determine which of these processes dominated. Prior to the introduction of new furniture, TDCIPP was detected in 12/20 samples at a median concentration of 22 μg/g and TCEP was detected in 1/20 samples at a concentration of 16 μg/g. TDCIPP and TCEP were not detected in any samples (N = 29) after the introduction of new couches. TPHP was detected both before (in 11/20 samples) and after (in 5/29 samples) introduction of new couches; the median concentrations before and after were 63 ± 49 and 16 ± 11 μg/g (standard deviation shown). Introduced couches contained TDCIPP (and not TPHP) at ∼1.25% (w/w). These data support the second hypothesis and indicate that removal of older furniture decreases TDCIPP and TCEP concentrations in dust and may potentially reduce total flame retardant concentrations in dust, at least immediately after introduction of the new furniture. Copyright © 2016 Elsevier Ltd. All rights reserved.

Flame retardants in UK furniture increase smoke toxicity more than they reduce fire growth rate.

PubMed

McKenna, Sean T; Birtles, Robert; Dickens, Kathryn; Walker, Richard G; Spearpoint, Michael J; Stec, Anna A; Hull, T Richard

2018-04-01

This paper uses fire statistics to show the importance of fire toxicity on fire deaths and injuries, and the importance of upholstered furniture and bedding on fatalities from unwanted fires. The aim was to compare the fire hazards (fire growth and smoke toxicity) using different upholstery materials. Four compositions of sofa-bed were compared: three meeting UK Furniture Flammability Regulations (FFR), and one using materials without flame retardants intended for the mainland European market. Two of the UK sofa-beds relied on chemical flame retardants to meet the FFR, the third used natural materials and a technical weave in order to pass the test. Each composition was tested in the bench-scale cone calorimeter (ISO 5660) and burnt as a whole sofa-bed in a sofa configuration in a 3.4 × 2.25 × 2.4 m 3 test room. All of the sofas were ignited with a No. 7 wood crib; the temperatures and yields of toxic products are reported. The sofa-beds containing flame retardants burnt somewhat more slowly than the non-flame retarded EU sofa-bed, but in doing so produced significantly greater quantities of the main fire toxicants, carbon monoxide and hydrogen cyanide. Assessment of the effluents' potential to incapacitate and kill is provided showing the two UK flame retardant sofa-beds to be the most dangerous, followed by the sofa-bed made with European materials. The UK sofa-bed made only from natural materials (Cottonsafe ® ) burnt very slowly and produced very low concentrations of toxic gases. Including fire toxicity in the FFR would reduce the chemical flame retardants and improve fire safety. Crown Copyright © 2017. Published by Elsevier Ltd. All rights reserved.

Development of the phosphorus and nitrogen containing flame retardant for value added cotton product

USDA-ARS?s Scientific Manuscript database

It is our desire to develop new crosslinking agents for cotton textiles that afford useful flame protection regardless of fabric construction. Herein we present the synthesis and the application of the triazine and piperazine derivatives as flame retardant on cotton. Novel phosphorus-nitrogen contai...

Shuttle Environmental Assurance: Brominated Flame Retardants - Concerns, Drivers, Potential Impacts and Mitigation Strategies

NASA Technical Reports Server (NTRS)

Clark-Ingram, Marceia

2010-01-01

Brominated Flame Retardants (BFRs) are widely used in the manufacture of electrical and electronic components and as additives in formulations for foams, plastics and rubbers. The United States (US) and the European Union (EU)have increased regulation and monitoring of of targeted BFRs, such as Polybrominated Diphenyl Ethers (PBDEs) due to the bioaccumulative effects in humans and animals. In response, manufacturers and vendors of BFR-containing materials are changing flame-retardant additives, sometimes without notifying BFR users. In some instances, Deca-bromodiphenylether (Deca-BDE) and other families of flame retardants are being used as replacement flame retardants for penta-BDE and octa-BDE. The reformulation of the BFR-containing material typically results in the removal of the targeted PBDE and replacement with a non-PBDE chemical or non-targeted PBDE. Many users of PBDE -based materials are concerned that vendors will perform reformulation and not inform the end user. Materials performance such as flammability, adhesion , and tensile strength may be altered due to reformulation. The requalification of newly formulated materials may be required, or replacement materials may have to be identified and qualified. The Shuttle Enviornmental Assurance (SEA) team indentified a risk to the Space Shuttle Program associated with the possibility that targeted PBDEs may be replaced without notification. Resultant decreases in flame retardancy, Liquid Oxygen (LOX) compatibility, or material performance could have serious consequences.

Lithium-Ion Electrolytes Containing Flame Retardant Additives for Increased Safety Characteristics

NASA Technical Reports Server (NTRS)

Bugga, Ratnakumar V. (Inventor); Krause, Frederick Charles (Inventor); Smart, Marshall C. (Inventor); Prakash, Surya G. (Inventor); Smith, Kiah A. (Inventor)

2014-01-01

The invention discloses various embodiments of Li-ion electrolytes containing flame retardant additives that have delivered good performance over a wide temperature range, good cycle life characteristics, and improved safety characteristics, namely, reduced flammability. In one embodiment of the invention there is provided an electrolyte for use in a lithium-ion electrochemical cell, the electrolyte comprising a mixture of an ethylene carbonate (EC), an ethyl methyl carbonate (EMC), a fluorinated co-solvent, a flame retardant additive, and a lithium salt. In another embodiment of the invention there is provided an electrolyte for use in a lithium-ion electrochemical cell, the electrolyte comprising a mixture of an ethylene carbonate (EC), an ethyl methyl carbonate (EMC), a flame retardant additive, a solid electrolyte interface (SEI) film forming agent, and a lithium salt.

Halogenated flame retardants: do the fire safety benefits justify the risks?

PubMed

Shaw, Susan D; Blum, Arlene; Weber, Roland; Kannan, Kurunthachalam; Rich, David; Lucas, Donald; Koshland, Catherine P; Dobraca, Dina; Hanson, Sarah; Birnbaum, Linda S

2010-01-01

Since the 1970s, an increasing number of regulations have expanded the use of brominated and chlorinated flame retardants. Many of these chemicals are now recognized as global contaminants and are associated with adverse health effects in animals and humans, including endocrine and thyroid disruption, immunotoxicity, reproductive toxicity, cancer, and adverse effects on fetal and child development and neurologic function. Some flame retardants such as polybrominated diphenyl ethers (PBDEs) have been banned or voluntarily phased out by manufacturers because of their environmental persistence and toxicity, only to be replaced by other organohalogens of unknown toxicity. Despite restrictions on further production in some countries, consumer products previously treated with banned retardants are still in use and continue to release toxic chemicals into the environment, and the worldwide use of organohalogen retardants continues to increase. This paper examines major uses and known toxic effects of commonly-used organohalogen flame retardants, replacements for those that have been phased out, their combustion by-products, and their effectiveness at reducing fire hazard. Policy and other solutions to maintain fire safety while reducing toxicity are suggested. The major conclusions are: (1) Flammability regulations can cause greater adverse environmental and health impacts than fire safety benefits. (2) The current options for end-of-life disposal of products treated with organohalogens retardants are problematic. (3) Life-cycle analyses evaluating benefits and risks should consider the health and environmental effects of the chemicals, as well as their fire safety impacts. (4) Most fire deaths and most fire injuries result from inhaling carbon monoxide, irritant gases, and soot. The incorporation of organohalogens can increase the yield of these toxic by-products during combustion. (5) Fire-safe cigarettes, fire-safe candles, child-resistant lighters, sprinklers, and smoke detectors can prevent fires without the potential adverse effects of flame retardant chemicals. (6) Alternatives to organohalogen flame retardant chemicals include using less flammable materials, design changes, and safer chemicals. To date, before evaluating their health and environmental impacts, many flame retardant chemicals have been produced and used, resulting in high levels of human exposure. As a growing literature continues to find adverse impacts from such chemicals, a more systematic approach to their regulation is needed. Before implementing new flammability standards, decision-makers should evaluate the potential fire safety benefit versus the health and environmental impacts of the chemicals, materials, or technologies likely to be used to meet the standard. Reducing the use of toxic or untested flame retardant chemicals in consumer products can protect human and animal health and the global environment without compromising fire safety.

Piperazine-phosphonate derivatives: their flame retardant and thermal degradation properties on cotton fibers

USDA-ARS?s Scientific Manuscript database

It has been known that phosphorus-nitrogen system shows greater flame resistance in cotton textiles at a lower level than phosphorus used alone. This research aims to compare the effectiveness of Tetraethyl piperazine-1,4-diyldiphosphonate (TEPP) as a flame retardant (FR) for cotton fabric to a prev...

Synthesis, structural and flammability studies of novel phosphonates triazine derivative as economic flame retardant for cotton

USDA-ARS?s Scientific Manuscript database

Organophosphorous flame retardants have been known to be more effective when used in conjunction with nitrogen-containing systems. Their mixture produces incombustible non-toxic gases which can dilute the concentration of the oxygen near the flame, and the charred layers become protective barriers t...

Preparation of durable flame retardant PAN fabrics based on amidoximation and phosphorylation

NASA Astrophysics Data System (ADS)

Zhang, Yue; Ren, Yuanlin; Liu, Xiaohui; Huo, Tongguo; Qin, Yiwen

2018-01-01

This paper aims to develop a method to impart polyacrylonitrile (PAN) fabric durable flame retadancy. PAN fabric was modified with hydroxylamine hydrochloride (HA) to prepare amidoxime PAN fabric (A-PAN) followed by phosphorylation with phosphoric acid (PA) to obtain flame retardant PAN fabric (P-A-PAN). Thermogravimetric (TG) analysis, differential scanning calorimetry (DSC), microscale combustion calorimetry (MCC) and pyrolysis-gas chromatography-mass spectrometry (Py-GC/MS) were used to analyze the thermal degradation process and flame retardant mechanisms. The structure of the fabrics was characterized by Fourier transform infrared spectroscopy (FTIR) and X-ray Photoelectron Spectroscopy (XPS). The surface morphology of fabrics was observed by scanning electron microscope (SEM). Moreover, the flame retardancy of fabrics before and after washing was evaluated by Limiting oxygen index (LOI) and horizontal burning test. The results showed that the P-A-PAN possessed an excellent thermal stability with the highest LOI value of 34.1% and the highest char residue of 55.67% at 800 °C. Most importantly, the P-A-PAN possessed a wonderful flame retardant durability with a little decrease of LOI after 20 washing cycles. When they were ignited, the P-A-PAN fabrics before and after washing were both nonflammable due to the char residue formation of modified fabric.

Study of the Thermal Properties and the Fire Performance of Flame Retardant-Organic PCM in Bulk Form

PubMed Central

Palacios, Anabel; De Gracia, Alvaro

2018-01-01

The implementation of organic phase change materials (PCMs) in several applications such as heating and cooling or building comfort is an important target in thermal energy storage (TES). However, one of the major drawbacks of organic PCMs implementation is flammability. The addition of flame retardants to PCMs or shape-stabilized PCMs is one of the approaches to address this problem and improve their final deployment in the building material sector. In this study, the most common organic PCM, Paraffin RT-21, and fatty acids mixtures of capric acid (CA), myristic acid (MA), and palmitic acid (PA) in bulk, were tested to improve their fire reaction. Several flame retardants, such as ammonium phosphate, melamine phosphate, hydromagnesite, magnesium hydroxide, and aluminum hydroxide, were tested. The properties of the improved PCM with flame retardants were characterized by thermogravimetric analyses (TGA), the dripping test, and differential scanning calorimetry (DSC). The results for the dripping test show that fire retardancy was considerably enhanced by the addition of hydromagnesite (50 wt %) and magnesium hydroxide (50 wt %) in fatty acids mixtures. This will help the final implementation of these enhanced PCMs in building sector. The influence of the addition of flame retardants on the melting enthalpy and temperatures of PCMs has been evaluated. PMID:29329212

PCBs, PBBs and Brominated Flame Retardants

EPA Science Inventory

This chapter introduces selected organohalogen chemicals such as polychlorinated biphenyls (PCB5), polychiorinated biphenyls (PBBs), and brominated flame retardants (BFRs) with emphasis on the background, physicochemical properties, environmental levels, health effects and possib...

Comprehensive characterisation of flame retardants in textile furnishings by ambient high resolution mass spectrometry, gas chromatography-mass spectrometry and environmental forensic microscopy.

PubMed

Ionas, Alin C; Ballesteros Gómez, Ana; Uchida, Natsuyo; Suzuki, Go; Kajiwara, Natsuko; Takata, Kyoko; Takigami, Hidetaka; Leonards, Pim E G; Covaci, Adrian

2015-10-01

The presence and levels of flame retardants (FRs), such as polybrominated diphenyl ethers (PBDEs) and organophosphate flame retardants (PFRs), was determined in textile home furnishings, such as carpets and curtains from stores in Belgium. A comprehensive characterisation of FRs in textile was done by ambient high resolution mass spectrometry (qualitative screening), gas chromatography-mass spectrometry (GC-MS) (quantitation), and environmental forensic microscopy (surface distribution). Ambient ionisation coupled to a time-of-flight (TOF) high resolution mass spectrometer (direct probe-TOF-MS) was investigated for the rapid screening of FRs. Direct probe-TOF-MS proved to be useful for a first screening step of textiles to detect FRs below the levels required to impart flame retardancy and to reduce, in this way, the number of samples for further quantitative analysis. Samples were analysed by GC-MS to confirm the results obtained by ambient mass spectrometry and to obtain quantitative information. The levels of PBDEs and PFRs were typically too low to impart flame retardancy. Only high levels of BDE-209 (11-18% by weight) were discovered and investigated in localised hotspots by employing forensic microscopy techniques. Most of the samples were made of polymeric materials known to be inherently flame retarded to some extent, so it is likely that other alternative and halogen-free FR treatments/solutions are preferred for the textiles on the Belgian market. Copyright © 2015 Elsevier Inc. All rights reserved.

Effect of electron beam irradiation and microencapsulation on the flame retardancy of ethylene-vinyl acetate copolymer materials during hot water ageing test

NASA Astrophysics Data System (ADS)

Sheng, Haibo; Zhang, Yan; Wang, Bibo; Yu, Bin; Shi, Yongqian; Song, Lei; Kundu, Chanchal Kumar; Tao, Youji; Jie, Ganxin; Feng, Hao; Hu, Yuan

2017-04-01

Microencapsulated ammonium polyphosphate (MCAPP) in combination with polyester polyurethane (TPU) was used to flame retardant ethylene-vinyl acetate copolymer (EVA). The EVA composites with different irradiation doses were immersed in hot water (80 °C) to accelerate ageing process. The microencapsulation and irradiation dose ensured positive impacts on the properties of the EVA composites in terms of better dimensional stability and flame retardant performance. The microencapsulation of APP could lower its solubility in water and the higher irradiation dose led to the more MCAPP immobilized in three dimensional crosslinked structure of the EVA matrix which could jointly enhance the flame retardant and electrical insulation properties of the EVA composites. So, the EVA composites with 180 kGy irradiation dose exhibited better dimensional stability than the EVA composites with 120 kGy due to the higher crosslinking degree. Moreover, the higher irradiation dose lead to the more MCAPP immobilizated in crosslinked three-dimensional structure of EVA, enhancing the flame retardancy and electrical insulation properties of the EVA composites. After ageing test in hot water at 80 °C for 2 weeks, the EVA/TPU/MCAPP composite with 180 kGy could still maintain the UL-94 V-0 rating and the limiting oxygen index (LOI) value was as high as 30%. This investigation indicated the flame retardant EVA cable containing MCAPP could achieve stable properties and lower electrical fire hazard risk during long-term hot water ageing test.

Piloted Ignition to Flaming in Smoldering Fire-Retarded Polyurethane Foam

NASA Technical Reports Server (NTRS)

Putzeys, O.; Fernandez-Pello, A. C.; Urban, D. L.

2007-01-01

Experimental results are presented on the piloted transition from smoldering to flaming in the fire-retarded polyurethane foam Pyrell . The samples are small rectangular blocks with a square cross section, vertically placed in the wall of a vertical wind tunnel. Three of the vertical sample sides are insulated and the fourth side is exposed to an upward oxidizer flow of variable oxygen concentration and to a variable radiant heat flux. The gases emitted from the smoldering reaction pass upwards through a pilot, which consists of a coiled resistance heating wire. In order to compensate for the solid-phase and gas-phase effects of the fire retardants on the piloted transition from smoldering to flaming in Pyrell, it was necessary to assist the process by increasing the power supplied to the smolder igniter and the pilot (compared to that used for non-fire retarded foam). The experiments indicate that the piloted transition from smoldering to flaming occurs when the gaseous mixture at the pilot passes the lean flammability limit. It was found that increasing the oxygen concentration or the external heat flux increases the likelihood of a piloted transition from smoldering to flaming, and generally decreases the time delay to transition. The piloted transition to flaming is observed in oxygen concentrations of 23% and above in both low-density and high-density Pyrell. Comparisons with previous experiments show that the piloted transition from smoldering to flaming is possible under a wider range of external conditions (i.e. lower oxygen concentration) than the spontaneous transition from smoldering to flaming. The results show that the fire retardants in Pyrell are very effective in preventing the piloted transition to flaming in normal air, but Pyrell is susceptible to smoldering and the piloted transition to flaming in oxygen-enriched environments. Therefore, precautions should be taken in the design of applications of Pyrell in oxygen-enriched environments to reduce to the risk of a piloted transition to flaming.

Preparation of candidate reference materials for the determination of phosphorus containing flame retardants in styrene-based polymers.

PubMed

Roth, Thomas; Urpi Bertran, Raquel; Latza, Andreas; Andörfer-Lang, Katrin; Hügelschäffer, Claudia; Pöhlein, Manfred; Puchta, Ralph; Placht, Christian; Maid, Harald; Bauer, Walter; van Eldik, Rudi

2015-04-01

Candidate reference materials (RM) for the analysis of phosphorus-based flame retardants in styrene-based polymers were prepared using a self-made mini-extruder. Due to legal requirements of the current restriction for the use of certain hazardous substances in electrical and electronic equipment, focus now is placed on phosphorus-based flame retardants instead of the brominated kind. Newly developed analytical methods for the first-mentioned substances also require RMs similar to industrial samples for validation and verification purposes. Hence, the prepared candidate RMs contained resorcinol-bis-(diphenyl phosphate), bisphenol A bis(diphenyl phosphate), triphenyl phosphate and triphenyl phosphine oxide as phosphorus-based flame retardants. Blends of polycarbonate and acrylonitrile-co-butadiene-co-styrene as well as blends of high-impact polystyrene and polyphenylene oxide were chosen as carrier polymers. Homogeneity and thermal stability of the candidate RMs were investigated. Results showed that the candidate RMs were comparable to the available industrial materials. Measurements by ICP/OES, FTIR and NMR confirmed the expected concentrations of the flame retardants and proved that analyte loss and degradation, respectively, was below the uncertainty of measurement during the extrusion process. Thus, the candidate RMs were found to be suitable for laboratory use.

Citric acid based durable and sustainable flame retardant treatment for lyocell fabric.

PubMed

Mengal, Naveed; Syed, Uzma; Malik, Samander Ali; Ali Sahito, Iftikhar; Jeong, Sung Hoon

2016-11-20

Pyrovatex CP New, is a commonly used organophosphorus based flame retardant (FR) reagent for cellulosic materials. However, it has a drawback of high formaldehyde release when used with methylated melamine (MM) based cross-linker, a known carcinogenous compound. In the present approach, a durable and sustainable flame retarding recipe formulation for lyocell fabrics is developed using citric acid (CA) as a cross-linker. The FR finish was applied by pad-dry-cure process. The treated fabrics were characterized for surface morphology, elemental analysis, TG analysis, char study and FT-IR spectroscopy. Furthermore, flame retardancy, washing durability, formaldehyde release and breaking strength were also assessed, and compared with the conventional MM based FR recipe. The fabric samples treated with 400gL(-1) of FR with either 40 or 80gL(-1) of CA demonstrate flame retardancy even after 10 washing cycles. Furthermore, a 75% reduction in formaldehyde release is achieved. Higher char yield and lower decomposition temperature are found compared to untreated and FR+ MM treated lyocell. Such an improved sustainable recipe formulation can be used for lyocell fabric without any health risk in apparel wear. Copyright © 2016 Elsevier Ltd. All rights reserved.

Facile Fabrication of a PDMS@Stearic Acid-Kaolin Coating on Lignocellulose Composites with Superhydrophobicity and Flame Retardancy

PubMed Central

Wang, Zhe; Shen, Xiaoping; Qian, Temeng; Wang, Junjie; Sun, Qingfeng; Jin, Chunde

2018-01-01

The disadvantages such as swelling after absorbing water and flammability restrict the widespread applications of lignocellulose composites (LC). Herein, a facile and effective method to fabricate superhydrophobic surfaces with flame retardancy on LC has been investigated by coating polydimethylsiloxane (PDMS) and stearic acid (STA) modified kaolin (KL) particles. The as-prepared coatings on the LC exhibited a good repellency to water (a contact angle = 156°). Owing to the excellent flame retardancy of kaolin particles, the LC coated with PDMS@STA-KL displayed a good flame retardancy during limiting oxygen index and cone calorimeter tests. After the coating treatment, the limiting oxygen index value of the LC increased to 41.0. Cone calorimetry results indicated that the ignition time of the LC coated with PDMS@STA-KL increased by 40 s compared with that of uncoated LC. Moreover, the peak heat release rate (PHRR) and the total heat release (THR) of LC coated with PDMS@STA-KL reduced by 18.7% and 19.2% compared with those of uncoated LC, respectively. This LC coating with improved water repellency and flame retardancy can be considered as a potential alternative to protect the lignocellulose composite. PMID:29751575

Neurotoxicity of brominated flame retardants

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) have been commonly used as commercial flame retardants in a variety of products including plastics and textiles. Despite their decreasing usage worldwide, congeners continue to accumulate in the environment, including soil, dust, food, anima...

Functionalized ionic liquids and their applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hariprakasha, Humcha Krishnamurthy; Rangan, Krishnaswamy Kasthuri; Sudarshan, Tirumalai Srinivas

2018-01-16

Disclosure of functionalized ionic liquids. Use of disclosed ionic liquids as solvent for carbon dioxide. Use of disclosed ionic liquids as flame retardant. Use of disclosed ionic liquids for coating fabric to obtain flame retardant fabric.

INTRODUCTION TO BROMINATED FLAME RETARDANTS

EPA Science Inventory

Brominated flame retardants (BFRs) are a large and diverse class of major industrial products used to provide fire safety. Tetrabromobisphenol A (TBBPA), Hexabromocylocodecane (HBCD), and Polybrominated Diphenyl Ethers (PBDEs) are the major commercial compounds. TBBPA is a react...

New Trends in Reaction and Resistance to Fire of Fire-retardant Epoxies

PubMed Central

Gérard, Caroline; Fontaine, Gaëlle; Bourbigot, Serge

2010-01-01

This paper focuses on current trends in the flame retardancy of epoxy-based thermosets. This review examines the incorporation of additives in these polymers, including synergism effects. Reactive flame-retardants—which are incorporated in the polymer backbone—are reported and the use of fire-retardant epoxy coatings for materials protection is also considered. PMID:28883337

Methods of Responsibly Managing End-of-Life Foams and Plastics Containing Flame Retardants: Part II.

PubMed

Lucas, Donald; Petty, Sara M; Keen, Olya; Luedeka, Bob; Schlummer, Martin; Weber, Roland; Yazdani, Ramin; Riise, Brian; Rhodes, James; Nightingale, Dave; Diamond, Miriam L; Vijgen, John; Lindeman, Avery; Blum, Arlene; Koshland, Catherine P

2018-06-01

This is Part II of a review covering the wide range of issues associated with all aspects of the use and responsible disposal of foam and plastic wastes containing toxic or potentially toxic flame retardants. We identify basic and applied research needs in the areas of responsible collection, pretreatment, processing, and management of these wastes. In Part II, we explore alternative technologies for the management of halogenated flame retardant (HFR) containing wastes, including chemical, mechanical, and thermal processes for recycling, treatment, and disposal.

Graphene oxide based sol-gel stainless steel fiber for the headspace solid-phase microextraction of organophosphate ester flame retardants in water samples.

PubMed

Jin, Tingting; Cheng, Jing; Cai, Cuicui; Cheng, Min; Wu, Shiju; Zhou, Hongbin

2016-07-29

In this paper, graphene oxide was coated onto a stainless steel wire through sol-gel technique and it was used as a solid phase microextraction (SPME) fiber. The prepared fiber was characterized by scanning electron microscopy (SEM), which displayed that the fiber had crinkled surface and porous structure The application of the fiber was evaluated through the headspace SPME of nine organophosphate ester flame retardants (OPFRs) with different characteristics in water samples followed by gas chromatography and nitrogen-phosphorous detector (GC/NPD). The major factors influencing the extraction efficiency, including the extraction and desorption conditions, were studied and optimized. Under the optimum conditions, the proposed method was evaluated, and applied to the analysis of organophosphate ester flame retardants in real environmental water samples. The results demonstrated the HS-SPME method based on GO sol-gel fiber had good linearity (R>0.9928), and limits of detection (1.4-135.6ngL(-1)), high repeatability (RSD<9.8%) and good recovery (76.4-112.4%). The GO based sol-gel fiber displayed bigger extraction capability than the commercial PDMS fiber and the pure sol-gel fiber for both polar and apolar organophosphate esters, especially for the OPFRs containing benzene rings. Copyright © 2016 Elsevier B.V. All rights reserved.

Toxicokinetic differences between two major HBCD stereoisomers: Effect of dose, time, repeated exposure and route

EPA Science Inventory

Hexabromocyclododecane (HBCD) is a flame retardant primarily added to foam insulation used in buildings. Current demands for energy-efficient construction are increasing its use worldwide. This emerging global contaminant is a mixture of 3 stereoisomers [alpha (a), beta (B), gamm...

Synergetic Improvement in Thermal Conductivity and Flame Retardancy of Epoxy/Silver Nanowires Composites by Incorporating "Branch-Like" Flame-Retardant Functionalized Graphene.

PubMed

Feng, Yuezhan; Li, Xiongwei; Zhao, Xiaoyu; Ye, Yunsheng; Zhou, Xingping; Liu, Hu; Liu, Chuntai; Xie, Xiaolin

2018-06-27

The significant fire hazards on the polymer-based thermal interface materials (TIM) used in electronic devices are but often neglected. Also, high filler loading with the incident deterioration of mechanical, thermal, and processing properties limits the further application of the traditional polymer-based TIMs. In this work, a ternary TIMs with epoxy resin (EP) matrix, silver nanowires (AgNWs), and a small amount of flame-retardant functionalized graphene (GP-DOPO) were proposed to address the above questions. Briefly, a facile "branch-like" strategy with a polymer as the backbone and flame-retardant molecule as the branch was first used to functionalize reduced graphene oxide (RGO) toward increasing the flame-retardant grafting ratio and RGO's compatibility in matrix, and the resulted GP-DOPO was then in situ introduced into the EP/AgNW composites. As expected, the incorporation of GP-DOPO (2 wt %) can increase the thermal conductivity to 1.413 W/(m K) at a very low AgNW loading (4 vol %), which is 545 and 56% increments compared to pure EP and EP/AgNW, respectively. The prominent improvement in thermal conductivity was put down to the synergetic effect of AgNW and GP-DOPO, i.e., the improving dispersion and bridging effect for AgNWs by adding GP-DOPO. Moreover, the high flame-retardant grafting amount and the excellent compatibility of GP-DOPO resulted in a strong catalytic charring effect on EP matrix, which further formed a robust protective char layer by combining the AgNW and graphene network. Therefore, the flame retardancy of EP/AgNW was significantly improved by introducing GP-DOPO, i.e., the peak heat release rate, total heat release and total smoke production reduced by 27.0, 32.4, and 30.9% reduction compared to EP/AgNW, respectively.

Sorption of Organophosphorus Flame Retardants on Settled Dust

EPA Science Inventory

Organophosphorus flame retardants (OPFRs) are widely used as additives in industrial and consumer products such as electrical and electronic products, furniture, plastics, textiles, and building/construction materials. Due to human exposure and potential health effects, OPFRs inc...

The individual and cumulative effect of brominated flame retardant and polyvinylchloride (PVC) on thermal degradation of acrylonitrile-butadiene-styrene (ABS) copolymer.

PubMed

Brebu, Mihai; Bhaskar, Thallada; Murai, Kazuya; Muto, Akinori; Sakata, Yusaku; Uddin, Md Azhar

2004-08-01

Acrylonitrile-butadiene-styrene (ABS) copolymers without and with a polybrominated epoxy type flame retardant were thermally degraded at 450 degrees C alone (10 g) and mixed with polyvinylchloride (PVC) (8 g/2 g). Gaseous and liquid products of degradation were analysed by various gas chromatographic methods (GC with TCD, FID, AED, MSD) in order to determine the individual and cumulative effect of bromine and chlorine on the quality and quantity of degradation compounds. It was found that nitrogen, chlorine, bromine and oxygen are present as organic compounds in liquid products, their quantity depends on the pyrolysed polymer or polymer mixture. Bromophenol and dibromophenols were the main brominated compounds that come from the flame retardant. 1-Chloroethylbenzene was the main chlorine compound observed in liquid products. It was also determined that interactions appear at high temperatures during decomposition between the flame retardant, PVC and the ABS copolymer.

Construction of flame retardant nanocoating on ramie fabric via layer-by-layer assembly of carbon nanotube and ammonium polyphosphate.

PubMed

Zhang, Tao; Yan, Hongqiang; Peng, Mao; Wang, Lili; Ding, Hongliang; Fang, Zhengping

2013-04-07

A new flame retardant nanocoating has been constructed by the alternate adsorption of polyelectrolyte amino-functionalized multiwall carbon nanotube (MWNT-NH2) and ammonium polyphosphate (APP) onto flexible and porous ramie fabric. Scanning electron microscopy indicates that the adsorbed carbon nanotube coating is a randomly oriented and overlapped network structure, which is a promising candidate for flame retardancy applications. Attenuated total reflection Fourier transform infrared spectroscopy and energy-dispersive X-ray analysis confirm that the APP is successfully incorporated into the multilayers sequentially. Assessment of the thermal and flammability properties for the pristine and nanocoated ramie fabrics shows that the thermal stability, flame retardancy and residual char are enhanced as the concentration of MWNT-NH2 suspension and number of deposition cycles increases. The enhancements are mostly attributed to the barrier effect of intumescent network structure, which is composed of MWNT-NH2 and the absorbed APP.

The novel application of chitosan: Effects of cross-linked chitosan on the fire performance of thermoplastic polyurethane.

PubMed

Zhang, Sheng; Liu, Xiaodong; Jin, Xiaodong; Li, Hongfei; Sun, Jun; Gu, Xiaoyu

2018-06-01

In this paper, a novel flame retardant (ACS) was prepared by crosslinking chitosan with bis-(4-formylphenyl)-phenyl-phosphonate (ABPO). ACS in association with ammonium polyphosphate (APP) and organic modified montmorillonite (OMMT) were used to prepare flame retardant thermoplastic polyurethane (TPU) composite through melt blending. For the TPU sample containing 10% flame retardants, the limiting oxygen index was increased from 20.8 to 29.0%, the vertical burning (UL-94) rating was upgraded from no rating to V-0, and the peak heat release rate was decreased from 1090 to 284 kW/m 2 . The thermal gravity analysis (TGA) indicated that ACS had excellent char formation ability and could greatly enhance the thermal stability of TPU. The tensile strength and elongation at break for flame retardant sample could reach 16.5 MPa and 1443% respectively. Copyright © 2018 Elsevier Ltd. All rights reserved.

Platinum-doped titanate nanotubes/reduced graphene oxide: photocatalytic activity and flame retardancy

NASA Astrophysics Data System (ADS)

Liu, Guangya; Sang, Bin; Zhou, Zhiqi; Li, Zhiwei

2018-01-01

The ‘white pollution’ produced by wasted flexible polyvinyl chloride (PVC) with poor degradation ability and the potential fire hazard of PVC with high flammability not only restrict their application but also cause serious environmental problem. Thus platinum-doped titanate nanotubes/reduced graphene oxide (denoted as Pt-TNTs/rGO) nanocomposites were prepared by a facile method in order to improve the visible photodegradation and get rid of the ‘white pollution’ as well as flame retardancy of PVC. The photodegradation activity and flame retardancy effect of the as-prepared Pt-TNTs/rGO nanocomposites were investigated by ultraviolet and visible light irradiation as well as cone calorimetry. Results show that the Pt-TNTs/rGO-PVC nanocomposites exhibit enhanced visible light photodegradation performance (with mass loss being 6.5%) during 15 day exposure to solar irradiation, and good flame retardancy (providing a 44% reduction of total smoke release as compared with that of PVC matrix). Besides, Pt-TNTs/rGO-PVC nanocomposites show suppressed smoke and reduced CO production as compared with the PVC matrix. These results demonstrate that Pt-TNTs/rGO not only get rid of the ‘white pollution’ as the photocatalyst but also improve the fire safety of PVC as the flame retardant. This could be ascribed to the combination effect between Pt-TNTs and rGO. The present research, hopefully, is to pave a potential pathway to constructing polymer-matrix composites with desired photodegradation activity and flame retardancy, thereby shedding light on simultaneously dealing with the ‘white pollution’ and high flammability of polymer matrix like PVC.

Rapid methodology to screen flame retardants in upholstered furniture for compliance with new California labeling law (SB 1019).

PubMed

Petreas, Myrto; Gill, Ranjit; Takaku-Pugh, Sayaka; Lytle, Eric; Parry, Emily; Wang, Miaomiao; Quinn, John; Park, June-Soo

2016-06-01

In response to concerns regarding the widespread use of flame retardants, the California Legislature passed a law (SB1019) requiring labels on furniture products to indicate whether they do or do not contain flame retardants. To support the enforcement of the new law, our laboratory developed a step-wise, screening approach to test for brominated (BFR) and phosphorus-based flame retardants (OPFRs) in several types of furniture components (foam, fabric, batting, plumage, etc.). We used X-Ray Fluorescence (XRF) to screen for the presence of Br (and other elements) and Inductively Coupled Plasma - Optical Emission Spectrometry (ICP-OES) to identify and measure the concentration of P (and other elements). The same samples were also extracted by dichloromethane using sonication and analyzed by a single injection into a Gas Chromatograph - Tandem Mass Spectrometer to obtain concentrations of specific BFRs and OPFRs. Our approach showed excellent screening potential for Br and Sb by XRF and for P by ICP-OES, with both tests having predictive values of a negative equal to 1. To explore and screen for flame retardants in products not included in our current list of target chemicals, we used Liquid Chromatography/Time-of-Flight Mass Spectrometry operated with electrospray ionization, to identify additional flame retardants to be incorporated in quantitative methods. We are making all our methodologies public to facilitate simple and low cost methods that can help manufacturers and suppliers have their products tested and correctly labeled, ultimately benefitting the consumer. Copyright © 2016 Elsevier Ltd. All rights reserved.

Acute Neurobehavorial Toxicity of Flame Retardant Replacement Compounds in Zebrafish Larvae

EPA Science Inventory

As polybrominated diphenyl ethers (PBDEs) are phased out, numerous compounds areemerging as potential replacement flame retardants for use in consumer and electronicproducts. Little is known, however, about the neurobehavioral toxicity of thesereplacements. This study evaluated t...

HEALTH EFFECTS OF BROMINATED FLAME RETARDANTS (BFRS)

EPA Science Inventory

Abstract Brominated flame retardant use has increased dramatically in order to provide fire safety to consumers. However, there is growing concern about widespread environmental contamination and potential health risks from some of these products. The most used products...

Sorption of Organophosphorus Flame-Retardants on Settled Dust

EPA Science Inventory

Dust is an important sink for indoor air pollutants, such as organophosphorus flame-retardants (OPFRs) that are used as additives in industrial and consumer products including electrical and electronic products, furniture, plastics, textile, and building/construction materials. T...

Burning To Learn: An Introduction to Flame Retardants.

ERIC Educational Resources Information Center

Journal of Chemical Education, 2001

2001-01-01

Presents an activity that demonstrates the effectiveness of flame retardants--substances added to combustible materials to slow down or hinder burning--that can be introduced when discussing combustion reactions or during a practical or everyday chemistry unit. (ASK)

Sorption of Organophosphorus Flame Retardants (OPFRs) on Settled Dust

EPA Science Inventory

Organophosphorus flame retardants (OPFRs) are widely used as additives in industrial and consumer products such as electrical and electronic products, furniture, plastics, textiles, and building/construction materials. Due to human exposure and potential health effects, OPFRs inc...

Brominated Flame Retardants and Perfluorinated Chemicals

EPA Science Inventory

Brominated flame retardants (BFRs) and perfluorinated chemicals (PFCs) belong to a large class of chemicals known as organohalogens. It is believed that both BFRs and PFCs saved lives by reducing flammability of materials commonly used and bactericidal (biocidal) properties. Thes...

Alternatives Assessment: Partnership to Evaluate Flame Retardants in Printed Circuit Boards

EPA Pesticide Factsheets

The partnership project on flame retardants in printed circuit boards seeks to improve understanding of the environmental and human health impacts of new and current materials that can be used to meet fire safety standards

Brominated flame retardants as food contaminants

USDA-ARS?s Scientific Manuscript database

This book chapter reviews analytical methods for the three major brominated flame retardant (BFR) classes in use today, tetrabromobisphenol-A (TBBP-A), hexabromocyclododecanes (HBCDs), and polybrominated diphenyl ethers (PBDEs), a "legacy" BFR no longer in use, polybrominated biphenyls (PBBs), and a...

Characterization of organophosphorus flame retardants' sorption on building materials and consumer products

EPA Science Inventory

Better understanding the transport mechanisms of organophosphorus flame-retardants (OPFRs) in the residential environment is important to more accurately estimate their indoor exposure and develop risk management strategies that protect human health. This study describes an impro...

BROMINATED FLAME RETARDANTS: CAUSE FOR CONCERN?

EPA Science Inventory

Brominated flame retardants (BFRs) have routinely been added to consumer products for several decades in a successful effort to reduce fire-related injury and property damage. Recently, concern for this emerging class of chemicals has risen due to the occurrence of several class...

OVERVIEW AND EVALUATION OF NEUROBEHAVIORAL EFFECTS OF FLAME RETARDANTS IN LABORATORY ANIMALS.

EPA Science Inventory

Polybrominated diphenyl ether (PBDE) flame retardants are used worldwide and have been detected in numerous environmental, including human, samples. Concern has been raised regarding their potential developmental neurotoxic effects. There is an emerging literature on behavioral...

Bioaccumulation and toxicity of the flame retardant TBPH or ...

EPA Pesticide Factsheets

The use of polybrominated diphenyl ethers as flame retardants in consumer products has been scrutinized increasingly due to their environmental persistence and potential toxicity; however, alternative replacement flame retardants may have similar drawbacks. The alternative brominated flame retardant bis(2-ethylhexyl)-2,3,4,5-tetrabromophthalate (TBPH) is a component of several commercial flame retardants, including Firemaster® 550, Firemaster® BZ-54 and DP-45. Here we investigate the bioaccumulation, bioenergetics and other adverse outcomes pathways (AOPs) predicted for dietary exposure to a carrier control, two levels of TBPH, or 2,2',4,4',5,5'-hexachlorobiphenyl (PCB153, a well-studied compound acting as a positive control for some aspects of the study). The TBPH concentrations chosen were at or well above the environmental concentrations documented in the literature, but similar to those causing toxicity in a previous study. Our experimental model is a small estuarine fish, the mummichog (Fundulus heteroclitus), exposed as individually tagged fish held in small groups (2 male, 2 female) in replicate tanks and fed contaminated food from day 0-28, followed by uncontaminated food from day 29-42. Throughout the experiment, individual growth was measured weekly, and at various time points, fish from replicate tanks were sacrificed, measured and dissected. To support putative AOPs, samples were obtained for analysis of hormone levels and transcriptomic responses

Synergistic Effect of Graphene Oxide and Mesoporous Structure on Flame Retardancy of Nature Rubber/IFR Composites.

PubMed

Wang, Na; Zhang, Miao; Kang, Ping; Zhang, Jing; Fang, Qinghong; Li, Wenda

2018-06-13

Aiming to improve the flame retardancy performance of natural rubber (NR), we developed a novel flame retardant synergistic agent through grafting of MCM-41 to graphene oxide (GO), named as GO-NH-MCM-41, as an assistant to intumescent flame retardants (IFR). The flame retardancy of NR/IFR/GO-NH-MCM-41 composites was evaluated by limited oxygen index (LOI), UL-94, and cone calorimeter test. The LOI value of NR/IFR/GO-NH-MCM-41 reached 26.3%; the UL-94 ratings improved to a V-0 rating. Moreover, the addition of GO-NH-MCM-41 decreased the peak heat release rate (PHRR) and the total heat release (THR) of the natural rubber composites. Furthermore, the addition of GO-NH-MCM-41 increased the thickness of char residue. The images of SEM indicated the char residue was more compact and continuous. The degradation of GO-NH-MCM-41-based NR composites was completed with a mass loss of 35.57% at 600 °C. The tensile strength and the elongation at break of the NR/IFR/GO-NH-MCM-41 composites were 13.9 MPa and 496.7%, respectively. The results of the rubber process analyzer (RPA) reached the maximum value, probably due to a better network of fillers in the matrix.

Gas chromatography/mass spectrometry comprehensive analysis of organophosphorus, brominated flame retardants, by-products and formulation intermediates in water.

PubMed

Cristale, Joyce; Quintana, Jordi; Chaler, Roser; Ventura, Francesc; Lacorte, Silvia

2012-06-08

A multiresidue method based on gas chromatography coupled to quadrupole mass spectrometry was developed to determine organophosphorus flame retardants, polybromodiphenyl ethers (BDEs 28, 47, 99, 100, 153, 154, 183 and 209), new brominated flame retardants, bromophenols, bromoanilines, bromotoluenes and bromoanisoles in water. Two ionization techniques (electron ionization--EI, and electron capture negative ionization--ECNI) and two acquisition modes (selected ion monitoring--SIM, and selected reaction monitoring--SRM) were compared as regards to mass spectral characterization, sensitivity and quantification capabilities. The highest sensitivity, at expenses of identification capacity, was obtained by GC-ECNI-MS/SIM for most of the compounds analyzed, mainly for PBDEs and decabromodiphenyl ethane while GC-EI-MS/MS in SRM was the most selective technique and permitted the identification of target compounds at the pg level, and identification capabilities increased when real samples were analyzed. This method was further used to evaluate the presence and behavior of flame retardants within a drinking water treatment facility. Organophosphorus flame retardants were the only compounds detected in influent waters at levels of 0.32-0.03 μg L⁻¹, and their elimination throughout the different treatment stages was evaluated. Copyright © 2012 Elsevier B.V. All rights reserved.

Synthesis of a novel reactive flame retardant containing phosphaphenanthrene and triazine-trione groups and its application in unsaturated polyester resin

NASA Astrophysics Data System (ADS)

Huo, Siqi; Wang, Jun; Yang, Shuang; Cai, Haopeng; Zhang, Bin; Chen, Xi; Wu, Qilei; Yang, Lingfeng

2018-03-01

A new-type compound (DT) which contained phosphaphenanthrene and triazine-trione groups was synthesized. DT was served as a reactive flame retardant for unsaturated polyester resin (UP). The thermal degradation, flame-retarded and mechanical properties of UP/DT samples were detected by different tests. According to the results, the addition of DT improved the initial thermal decomposition temperature (T5% and T10%) and the char yields of UP thermosets. Additionally, incorporation of DT resulted in the decrease of flexural and tensile strength of UP samples, and the increase of flexural modulus. The flame-retarded performance of UP/DT samples was greatly improved compared with the neat UP thermoset. For instance, the limited oxygen index (LOI) and vertical burning (UL94) rating of UP/DT-30 sample with 30 wt% DT came up to 29.8% and V-1. In comparison to pure UP thermoset, the average of heat release rate (av-HRR), total heat release (THR) and average of effective heat of combustion (av-EHC) of UP/DT-30 thermoset were decreased by 35.9%, 31.2% and 29.1%, respectively. Phosphaphenanthrene and triazine-trione groups in DT synergistically enhanced flame-retarded capability of UP in both gas phase and condensed phase.

Flame-retardant contamination of firefighter personal protective clothing - A potential health risk for firefighters.

PubMed

Alexander, Barbara M; Baxter, C Stuart

2016-09-01

There is a high incidence of cardiovascular disease and certain cancers in firefighters that may be related to their occupational exposure to hazardous substances. Exposure may result from contaminated personal protective gear, as well as from direct exposure at fire scenes. This study characterized flame-retardant contamination on firefighter personal protective clothing to assess exposure of firefighters to these chemicals. Samples from used and unused firefighter protective clothing, including gloves, hoods and a coat wristlet, were extracted with methylene chloride and analyzed by EPA method 8270D Specific Ion Method (SIM) for polybrominated diphenyl ethers (PBDEs). Until recently PBDEs were some of the most common flame-retardant chemicals used in the US. Fifteen of the seventeen PBDEs for which analysis was performed were found on at least one clothing swatch. Every clothing sample, including an unused hood and all three layers of an unused glove, held a detectable concentration of at least one PBDE. These findings, along with previous research, suggest that firefighters are exposed to PBDE flame retardants at levels much higher than the general public. PBDEs are found widely dispersed in the environment and still persist in existing domestic materials such as clothing and furnishings. Firefighter exposure to flame retardants therefore merits further study.

BROMINATED FLAME RETARDANTS: WHAT WE KNOW, AND WHAT WE DON’T

EPA Science Inventory

Brominated flame retardants (BFRs) represent a large and diverse class of high volume industrial chemicals which have been developed to provide fire safety. There are many other BFRs which have been used and are under development. Historically, polybrominated biphenyls (PBBs) ...

CONGENER-DEPENDENT DISTRIBUTION AND EXCRETION: A COMPARISON OF BDES 47, 99, 100, AND 153 TOXICOKINETICS.

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) represent a novel class of chemicals used as flame retardants predominantly in textiles, furniture, and electronics. Evidence demonstrating the bioaccumulation of these brominated flame retardants in humans has spurred research into potenti...

PBDE FLAME RETARDANTS: TOXICOLOGY, HEALTH EFFECTS, AND RISK ASSESSMENT

EPA Science Inventory

Polybrominated diphenyl ether (PBDE) flame retardants have been routinely added to consumer products for several decades in a successful effort to reduce fire-related injury and property damage. Global production of PBDEs has reached 67,000 metric tons per year. Recently concer...

Brominated flame retardants and perfluorinated chemicals

EPA Science Inventory

Brominated flame retardants (BFRs) and perfluorinated chemicals (PFCs) belong to a class of chemicals known as organohalogens. It is believed that use of both BFRs and PFCs has resulted in lives saved by reducing flammability of materials commonly used and also due to their bacte...

Migration of Organophorus Flame Retardants From Closed cell form to Settled Dust

EPA Science Inventory

Many industrial and consumer products, such as electrical and electronic products, furniture, plastics, textile, and building materials are manufactured with organophosphorus flame retardants (OPFRs). OPFRs can leach or diffuse out of the products and are released to the surround...

Migration of Organophosphate Flame Retardants from Closed Cell Foam to Settled Dust

EPA Science Inventory

Many industrial and consumer products, such as electrical and electronic products, furniture, plastics, textile, and building materials are manufactured with organophosphorus flame retardants (OPFRs). OPFRs can leach or diffuse out of the products and are released to the surround...

Innovative green technique for preparing of flame retardant cotton

USDA-ARS?s Scientific Manuscript database

Due to its environmentally benign character, microwave-assisted or supercritical carbon dioxide high pressure reactors are considered in green chemistry as a substitute for organic solvents in chemical reactions. In this paper, an innovative approach for preparation of flame retardant cotton fabric ...

Measuring and modeling surface sorption dynamics of organophosphate flame retardants in chambers

EPA Science Inventory

Understanding the sorption mechanisms for organophosphate flame retardants (OPFRs) on impervious surfaces is important to improve our understanding of the fate and transport of OPFRs in indoor environments. Langmuir and Freundlich models are widely adopted to describe sorption be...

Flame Retardant Effect of Nano Fillers on Polydimethylsiloxane Composites.

PubMed

Jagdale, Pravin; Salimpour, Samera; Islam, Md Hujjatul; Cuttica, Fabio; Hernandez, Francisco C Robles; Tagliaferro, Alberto; Frache, Alberto

2018-02-01

Polydimethylsiloxane has exceptional fire retardancy characteristics, which make it a popular polymer in flame retardancy applications. Flame retardancy of polydimethylsiloxane with different nano fillers was studied. Polydimethylsiloxane composite fire property varies because of the shape, size, density, and chemical nature of nano fillers. In house made carbon and bismuth oxide nano fillers were used in polydimethylsiloxane composite. Carbon from biochar (carbonised bamboo) and a carbon by-product (carbon soot) were selected. For comparative study of nano fillers, standard commercial multiwall carbon nano tubes (functionalised, graphitised and pristine) as nano fillers were selected. Nano fillers in polydimethylsiloxane positively affects their fire retardant properties such as total smoke release, peak heat release rate, and time to ignition. Charring and surface ceramization are the main reasons for such improvement. Nano fillers in polydimethylsiloxane may affect the thermal mobility of polymer chains, which can directly affect the time to ignition. The study concludes that the addition of pristine multiwall carbon nano tubes and bismuth oxide nano particles as filler in polydimethylsiloxane composite improves the fire retardant property.

Flame retardant exposure assessment: findings from a behavioral intervention study.

PubMed

Gibson, Elizabeth A; Stapleton, Heather M; Calero, Lehyla; Holmes, Darrell; Burke, Kimberly; Martinez, Rodney; Cortes, Boris; Nematollahi, Amy; Evans, David; Herbstman, Julie B

2018-06-28

Polybrominated diphenyl ethers (PBDEs) have been largely replaced by organophosphate flame retardants (OPFRs) and alternative brominated flame retardants (Alt-BFRs) to meet flammability requirements. Humans are ubiquitously exposed to some variety of flame retardants through contact with consumer products directly or through household dust. To evaluate the effectiveness of house cleaning and hand washing practices to reduce exposure to flame retardants, we measured concentrations in dermal hand wipes and urinary metabolites before and after assignment to two consecutive interventions. We selected 32 mother and child dyads from an existing cohort. This analysis focuses on mothers. Participants provided baseline measurements (urine, hand wipes, and questionnaires) and were then assigned for 1 week to either a house cleaning (including instruction on proper technique and cleaning supplies) or hand washing (including instruction on proper technique and soaps) intervention arm. For the second week, participants were assigned to the second intervention in addition to their initial assignment, thus all subjects both washed their hands and cleaned according to the intervention guidelines during week 2. We collected measurements at the end of weeks 1 and 2. We found reductions in urinary analytes after week 1 of house cleaning (BCIPHIPP and ip-DPHP), week 1 of hand washing (BCIPP, BCIPHIPP, and tbutyl-DPHP), and week 2 of combined interventions (BCIPHIPP and tbutyl-DPHP), compare to baseline. We found no significant decline in hand wipes in the entire sample but did find reductions after week 1 of house cleaning (BDE 209), week 1 of hand washing (TCEP), and week 2 of combined interventions (TDCIPP and BDE 209) in women with exposure above the median at baseline (verified through simulations). Exposure to individual flame retardants was reduced by about half, in some cases, by 1 week of increased hand washing, house cleaning to reduce dust, or combined activities.

A comparison of the in vitro cyto- and neurotoxicity of brominated and halogen-free flame retardants: prioritization in search for safe(r) alternatives.

PubMed

Hendriks, Hester S; Meijer, Marieke; Muilwijk, Mirthe; van den Berg, Martin; Westerink, Remco H S

2014-04-01

Brominated flame retardants (BFRs) are abundant persistent organic pollutants with well-studied toxicity. The toxicological and ecological concerns associated with BFRs argue for replacement by safe(r) alternatives. Though previous research identified the nervous system as a sensitive target organ for BFRs, the (neuro) toxic potential of alternative halogen-free flame retardants (HFFRs) is largely unknown. We therefore investigated the in vitro (neuro) toxicity of 13 HFFRs and three BFRs in dopaminergic pheochromocytoma (PC12) and neuroblastoma (B35) cells by assessing several cytotoxic and neurotoxic endpoints. Effects on cell viability and production of reactive oxygen species (ROS) were measured using a combined Alamar Blue and Neutral Red assay and a H2-DCFDA assay, respectively, whereas effects on calcium homeostasis were measured using single-cell fluorescent Ca(2+)-imaging. The majority of the tested flame retardants induced negligible cytotoxicity, except zinc hydroxystannate (ZHS) and zinc stannate (ZS). A considerable fraction of flame retardants affected ROS production (decabromodiphenyl ether (BDE-209), triphenylphosphate (TPP), aluminium trihydroxide (ATH), ammonium polyphosphate (APP), magnesium hydroxide (MHO), ZHS, ZS and melamine polyphosphate (MPP)). Interestingly, ATH, ZHS, ZS and montmorillonite (MMT) increased the basal intracellular calcium concentration ([Ca(2+)]i), whereas tetrabromobisphenol A (TBBPA), resorcinol bis (diphenylphosphate) (RDP), TPP, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO), ATH, ZHS, ZS and MMT reduced depolarization-evoked increases in [Ca(2+)]i as a result of inhibition of voltage-gated calcium channels. These combined data on the in vitro (neuro) toxicity of HFFRs in comparison with BFRs are essential for prioritization of safe(r) flame retardants. Though additional data are required for a complete (toxic) risk assessment, our data demonstrate that several HFFRs could be suitable substitutes for BFRs.

Neurotoxicity and risk assessment of brominated and alternative flame retardants.

PubMed

Hendriks, Hester S; Westerink, Remco H S

2015-01-01

Brominated flame retardants (BFRs) are widely used chemicals that prevent or slow the onset and spreading of fire. Unfortunately, many of these compounds pose serious threats for human health and the environment, indicating an urgent need for safe(r) and less persistent alternative flame retardants (AFRs). As previous research identified the nervous system as a sensitive target organ, the neurotoxicity of past and present flame retardants is reviewed. First, an overview of the neurotoxicity of BFRs in humans and experimental animals is provided, and some common in vitro neurotoxic mechanisms of action are discussed. The combined epidemiological and toxicological studies clearly underline the need for replacing BFRs. Many potentially suitable AFRs are already in use, despite the absence of a full profile of their environmental behavior and toxicological properties. To prioritize the suitability of some selected halogenated and non-halogenated organophosphorous flame retardants and inorganic halogen-free flame retardants, the available neurotoxic data of these AFRs are discussed. The suitability of the AFRs is rank-ordered and combined with human exposure data (serum concentrations, breast milk concentrations and house dust concentrations) and physicochemical properties (useful to predict e.g. bioavailability and persistence in the environment) for a first semi-quantitative risk assessment of the AFRs. As can be concluded from the reviewed data, several BFRs and AFRs share some neurotoxic effects and modes of action. Moreover, the available neurotoxicity data indicate that some AFRs may be suitable substitutes for BFRs. However, proper risk assessment is hampered by an overall scarcity of data, particularly regarding environmental persistence, human exposure levels, and the formation of breakdown products and possible metabolites as well as their toxicity. Until these data gaps in environmental behavioral and toxicological profiles are filled, large scale use of these chemicals should be cautioned.

[Toxicity of selected brominated aromatic compounds].

PubMed

Szymańska, J A

1996-01-01

Flame retardants are added to plastic materials, textiles, wood, hydraulic liquids etc. for reducing their inflammability. These substances reduce the heat and carbon monoxide formation in case of fire. They are added in high amounts, even up to 30% of product mass (e.g. plastic material). The production of brominated flame retardants has been steadily rising in the last 20 years, e.g. in the 1990s the world production of polybromodiphenyl ethers (PBDE) reached 40,000 tons annually. Mainly polybrominated flame retardants are produced, e.g. polybromobiphenyls (PBB), PBDE, hexabromobenzene (HBB). Their toxicity is low or nil, the DL 50 values are over 1 g/kg. However, when administered in low doses over longer time periods they can cause changes leading to porphyria. The information on the toxicity of polybrominated flame retardants for humans is derived mainly from the accident in Michigan, where PBB contamination of fodder for farm animals occurred with consequent contamination of food. In consumers of contaminated food cutaneous changes and neurological and muscular symptoms were noted. Polybrominated flame retardants can be metabolized and undergo biodegradation mainly trough debromination. The data on the toxicity of debromination products point to di- and tribromobenzenes, some of which are highly hepatotoxic. In acute poisoning hepatocellular damage manifest itself as necrotic changes in experimental animals receiving 0.1-0.8 of DL 50 of di- or tribromobenzene. After repeated administration of lower doses the hepatocellular damage assumes the features of porphyrogenic injury. In the environment polybrominated flame retardants can be transformed by various factors (high temperature during fire accidents, incomplete incineration of waste) to polybrominated dibenzodioxins of dibenzofurans whose lethal doses can in extreme cases be 0.001 mg for 1 kg body weight.

Potential human exposure to halogenated flame-retardants in elevated surface dust and floor dust in an academic environment.

PubMed

Allgood, Jaime M; Jimah, Tamara; McClaskey, Carolyn M; La Guardia, Mark J; Hammel, Stephanie C; Zeineddine, Maryam M; Tang, Ian W; Runnerstrom, Miryha G; Ogunseitan, Oladele A

2017-02-01

Most households and workplaces all over the world possess furnishings and electronics, all of which contain potentially toxic flame retardant chemicals to prevent fire hazards. Indoor dust is a recognized repository of these types of chemicals including polybrominated diphenyl ethers (PBDEs) and non-polybrominated diphenyl ethers (non-PBDEs). However, no previous U.S. studies have differentiated concentrations from elevated surface dust (ESD) and floor dust (FD) within and across microenvironments. We address this information gap by measuring twenty-two flame-retardant chemicals in dust on elevated surfaces (ESD; n=10) and floors (FD; n=10) from rooms on a California campus that contain various concentrations of electronic products. We hypothesized a difference in chemical concentrations in ESD and FD. Secondarily, we examined whether or not this difference persisted: (a) across the studied microenvironments and (b) in rooms with various concentrations of electronics. A Wilcoxon signed-rank test demonstrated that the ESD was statistically significantly higher than FD for BDE-47 (p=0.01), BDE-99 (p=0.01), BDE-100 (p=0.01), BDE-153 (p=0.02), BDE-154 (p=0.02), and 3 non-PBDEs including EH-TBB (p=0.02), BEH-TEBP (p=0.05), and TDCIPP (p=0.03). These results suggest different levels and kinds of exposures to flame-retardant chemicals for individuals spending time in the sampled locations depending on the position of accumulated dust. Therefore, further research is needed to estimate human exposure to flame retardant chemicals based on how much time and where in the room individuals spend their time. Such sub-location estimates will likely differ from assessments that assume continuous unidimensional exposure, with implications for improved understanding of potential health impacts of flame retardant chemicals. Copyright © 2016 Elsevier Inc. All rights reserved.

Flame resistant fibrous materials. [developed from chlorofluoropolymers

NASA Technical Reports Server (NTRS)

1973-01-01

Four chlorofluoropolymer systems were developed that satisfactorily met the criteria for classification as self-extinguishing. Three of these systems consisted of Halar (a copolymer of chlorotrifluoroethylene and ethylene) and tin-based flame retardants. The fourth system was a copolymer of chlorotrifluoroethylene and tetrafluoroethylene with no flame retardants added. Production of fibers from all four candidates, by melt extrusion, was demonstrated. Fibers produced from the chlorotrifluoroethylene tetrafluoroethylene copolymer showed the most promise.

BROMINATED FLAME RETARDANTS: WHAT WE KNOW, AND WHAT WE DON�T

EPA Science Inventory

Brominated flame retardants (BFRs) represent a large and diverse class of high volume industrial chemicals which have been developed to provide fire safety. There are many other BFRs which have been used and are under development. Historically, polybrominated biphenyls (PBBs) w...

BROMINATED FLAME RETARDANTS: WHY DO WE CARE?

EPA Science Inventory

Brominated flame retardants (BFRs) save lives and property by preventing the spread of fires or delaying the time of flashover, enhancing the time people have to escape. The worldwide production of BFRs exceeded 200,000 metric tons in 2003 placing them in the high production vol...

Acute and Developmental Behavioral Effects of Flame Retardants and Related Chemicals in Zebrafish

EPA Science Inventory

As polybrominated diphenyl ethers are phased out, numerous compounds are emerging as potential replacement flame retardants for use in consumer and electronic products. Little is known, however, about the neurobehavioral toxicity of these replacements. This study evaluated the ne...

Developmental Exposure to Organophosphate Flame Retardants Elicits Overt Toxicity and Alters Behavior in Zebrafish (Danio rerio)

EPA Science Inventory

Organophosphate flame retardants (OPFRs) are common replacements for the phased-out polybrominated diphenyl ethers (PBDEs) and have been detected at high concentrations in environmental samples. OPFRs are structurally similar to organophosphate pesticides and may adversely affect...

Genetic control of flame retardancy in white lint cotton (gossypium hirsutum)

USDA-ARS?s Scientific Manuscript database

Varieties of cotton (Gossypium hirsutum L.) exhibit differences in fiber combustion properties and flame retardancy (FR) as measured by microscale combustion calorimetry (MCC) and standardized flammability testing. Some naturally colored brown lint cotton lines produce fibers that can create self-ex...

Green Flame Retardant Cotton Highlofts for Mattresses and Upholstered Furniture

USDA-ARS?s Scientific Manuscript database

Green flame retardant (FR) barrier fabric is environmentally-friendly because it is from a natural renewable resource, biodegradable, economical, employing greige cotton that is soft to touch. Greige unbleached cotton is cheaper and softer than bleached cotton, thus, increasing its marketability par...

Measuring and Modeling Surface Sorption Dynamics of Organophosphate Flame Retardants in Chambers

EPA Science Inventory

Understanding the sorption mechanisms for organophosphate flame retardants (OPFRs) on impervious surfaces is important if we are to improve our understanding of the fate and transport of OPFRs in indoor environments. Traditional Langmuir and Freundlich models are widely adopted t...

Brominated flame retardants and perfluorinated chemicals- Vet Tox

EPA Science Inventory

Brominated flame retardants (BFRs) and perfluorinated chemicals (PFCs) belong to a class of chemicals known as organohalogens. It is believed that use of both BFRs and PFCs has resulted in lives saved by reducing flammability of materials commonly used and also due to their bacte...

Design and UV-curable behaviour of boron based reactive diluent for epoxy acrylate oligomer used for flame retardant wood coating

PubMed Central

Chambhare, Sachin U.; Lokhande, Gunawant P.; Jagtap, Ramanand N.

2017-01-01

Abstract Difunctional boron-containing reactive flame retardant for UV-curable epoxy acrylate oligomer was synthesized from phenyl boronic acid and glycidyl methacrylate. The synthesized reactive diluent was utilized to formulate ultraviolet (UV)-curable wood coatings. The weight fractions of reactive diluent in coatings formulation was varied from 5 to 25 wt % with constant photoinitiator concentration. The molecular structure of reactive flame retardant was confirmed by Fourier-transform infrared, Nuclear magnetic resonance (NMR) and 11B NMR spectral analysis. Further, the efficacy of flame retardant behaviour of coatings was evaluated using limiting oxygen index and UL-94 vertical burning test. Thermal stability of cured coatings films were estimated from thermogravimetric and differential scanning calorimetry analysis. The effects of varying concentration of reactive diluent on the viscosity of coatings formulation along with optical, mechanical and chemical resistance properties of coatings were also evaluated. The coatings gel content, water absorption behaviour, contact angle analysis and stain resistance were also studied. PMID:29491786

Durable flame retardant and antibacterial finishing on cotton fabrics with cyclotriphosphazene/polydopamine/silver nanoparticles hybrid coatings

NASA Astrophysics Data System (ADS)

Li, Yingzhan; Wang, Bijia; Sui, Xiaofeng; Xie, Ruyi; Xu, Hong; Zhang, Linping; Zhong, Yi; Mao, Zhiping

2018-03-01

Durable flame retardant and antibacterial hybrid coatings were developed for cotton fabrics via simultaneous polymerization of dopamine and hydrolytic condensation of N3P3[NH(CH2)3Si(OC2H5)3]6. Silver nanoparticles were also introduced to the coatings by in situ reaction of AgNO3 with catechol moieties on polydopamine (PDA) in the absence of any external reducing agents. Energy dispersive spectrometer (EDS), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) were employed to study the morphology and constitution of the coatings. Thermal stability and combustion behaviors were characterized with thermogravimetric analysis (TGA) and vertical flammability tests. Considerable flame retardancy was obtained for the modified cotton fabrics, which also exhibited decent antibacterial activities (99.99%) against Gram-positive bacteria S. aureus and Gram-negative bacteria E. coli. The modification was durable with largely intact flame retardancy and antimicrobial properties after 30 washing cycles.

Occurrence and risk assessment of organophosphorus and brominated flame retardants in the River Aire (UK).

PubMed

Cristale, Joyce; Katsoyiannis, Athanasios; Sweetman, Andrew J; Jones, Kevin C; Lacorte, Silvia

2013-08-01

This study presents the occurrence and risk of PBDEs, new brominated and organophosphorus flame retardants along a river affected by urban and industrial pressures (River Aire, UK). Tris(2-choroethyl) phosphate (TCEP), tris(2-chloro-1-methylethyl) phosphate (TCPP), tris[2-chloro-1-(chloromethyl)ethyl] phosphate (TDCP) and triphenyl phosphate (TPhP) were detected in all samples, with TCPP present at the highest concentrations, ranging from 113 to 26,050 ng L⁻¹. BDE-209 was detected in most of the sampled sites, ranging from 17 to 295 ng L⁻¹, while hexabromobenzene (HBB) and pentabromoethyl benzene (PBEB) were seldom detected. A risk quotients based on predicted no effect concentrations (PNEC) and flame retardants water concentration proved significant risk for adverse effects for algae, Daphnia and fish in sites close to industrial and urban sewage discharges. This study provides a protocol for the risk estimation of priority and new generation flame retardants based on river concentrations and toxicological values. Copyright © 2013 Elsevier Ltd. All rights reserved.

Brominated flame retardant: environmental and exposed individuals' health impact.

PubMed

Dufour, Patrice; Charlier, Corinne

2017-04-01

Since Antiquity, men have used chemicals to protect their goods against fire. Effective and easy to use, brominated flame retardants are used since decades massively in plastic industry. Such like other organohalogenated compounds, brominated flame retardants are very persistent in the environment and able to accumulate along the food chain. Many authors highlight their presence in the environment, in many animal species and in the human serum. Worryingly, man is exposed as soon as the pregnancy and then by the breastfeeding. This exposition may have consequence on our health. Many studies (in vitro, in vivo or epidemiologic) highlight brominated flame retardant negative effects on the endocrine system, mainly on the thyroid function but also on the reproduction, the neurodevelopment in the children and on the metabolism with increasing diabetes risk. If authorities and some big enterprises are aware about the problematic, new studies are needed to confirm previous results, elucidate endocrine disrupting mechanisms and highlight hypothetical synergies with other pollutants such like PCBs.

Sustainable, heat-resistant and flame-retardant cellulose-based composite separator for high-performance lithium ion battery

PubMed Central

Zhang, Jianjun; Yue, Liping; Kong, Qingshan; Liu, Zhihong; Zhou, Xinhong; Zhang, Chuanjian; Xu, Quan; Zhang, Bo; Ding, Guoliang; Qin, Bingsheng; Duan, Yulong; Wang, Qingfu; Yao, Jianhua; Cui, Guanglei; Chen, Liquan

2014-01-01

A sustainable, heat-resistant and flame-retardant cellulose-based composite nonwoven has been successfully fabricated and explored its potential application for promising separator of high-performance lithium ion battery. It was demonstrated that this flame-retardant cellulose-based composite separator possessed good flame retardancy, superior heat tolerance and proper mechanical strength. As compared to the commercialized polypropylene (PP) separator, such composite separator presented improved electrolyte uptake, better interface stability and enhanced ionic conductivity. In addition, the lithium cobalt oxide (LiCoO2)/graphite cell using this composite separator exhibited better rate capability and cycling retention than that for PP separator owing to its facile ion transport and excellent interfacial compatibility. Furthermore, the lithium iron phosphate (LiFePO4)/lithium cell with such composite separator delivered stable cycling performance and thermal dimensional stability even at an elevated temperature of 120°C. All these fascinating characteristics would boost the application of this composite separator for high-performance lithium ion battery. PMID:24488228

Plasma-enhanced synthesis of green flame retardant cellulosic materials

NASA Astrophysics Data System (ADS)

Totolin, Vladimir

The natural fiber-containing fabrics and composites are more environmentally friendly, and are used in transportation (automobiles, aerospace), military applications, construction industries (ceiling paneling, partition boards), consumer products, etc. Therefore, the flammability characteristics of the composites based on polymers and natural fibers play an important role. This dissertation presents the development of plasma assisted - green flame retardant coatings for cellulosic substrates. The overall objective of this work was to generate durable flame retardant treatment on cellulosic materials. In the first approach sodium silicate layers were pre-deposited onto clean cotton substrates and cross linked using low pressure, non-equilibrium oxygen plasma. A statistical design of experiments was used to optimize the plasma parameters. The modified cotton samples were tested for flammability using an automatic 45° angle flammability test chamber. Aging tests were conducted to evaluate the coating resistance during the accelerated laundry technique. The samples revealed a high flame retardant behavior and good thermal stability proved by thermo-gravimetric analysis. In the second approach flame retardant cellulosic materials have been produced using a silicon dioxide (SiO2) network coating. SiO 2 network armor was prepared through hydrolysis and condensation of the precursor tetraethyl orthosilicate (TEOS), prior coating the substrates, and was cross linked on the surface of the substrates using atmospheric pressure plasma (APP) technique. Due to protection effects of the SiO2 network armor, the cellulosic based fibers exhibit enhanced thermal properties and improved flame retardancy. In the third approach, the TEOS/APP treatments were extended to linen fabrics. The thermal analysis showed a higher char content and a strong endothermic process of the treated samples compared with control ones, indicating a good thermal stability. Also, the surface analysis proved the existence of the silica-based coatings on all treated cellulosic substrates after intense ultrasound washes. The results obtained in this work allow us to conclude that silica-based coatings used in conjunction with plasma processes have high potential to obtain green flame retardant cellulosic materials with potential applications in the development of upholstered furniture, clothing and military applications.

Organophosphate flame retardants and plasticizers in indoor dust, air and window wipes in newly built low-energy preschools.

PubMed

Persson, Josefin; Wang, Thanh; Hagberg, Jessika

2018-07-01

The construction of extremely airtight and energy efficient low-energy buildings is achieved by using functional building materials, such as age-resistant plastics, insulation, adhesives, and sealants. Additives such as organophosphate flame retardants (OPFRs) can be added to some of these building materials as flame retardants and plasticizers. Some OPFRs are considered persistent, bioaccumulative and toxic. Therefore, in this pilot study, the occurrence and distribution of nine OPFRs were determined for dust, air, and window wipe samples collected in newly built low-energy preschools with and without environmental certifications. Tris(1,3-dichloroisopropyl) phosphate (TDCIPP) and triphenyl phosphate (TPHP) were detected in all indoor dust samples at concentrations ranging from 0.014 to 10μg/g and 0.0069 to 79μg/g, respectively. Only six OPFRs (predominantly chlorinated OPFRs) were detected in the indoor air. All nine OPFRs were found on the window surfaces and the highest concentrations, which occurred in the reference preschool, were measured for 2-ethylhexyl diphenyl phosphate (EHDPP) (maximum concentration: 1500ng/m 2 ). Interestingly, the OPFR levels in the environmental certified low-energy preschools were lower than those in the reference preschool and the non-certified low-energy preschool, probably attributed to the usage of environmental friendly and low-emitting building materials, interior decorations, and consumer products. Copyright © 2018 Elsevier B.V. All rights reserved.

Hapten syntheses and antibody generation for the development of a polybrominated flame retardant ELISA.

PubMed

Shelver, Weilin L; Keum, Young-Soo; Kim, Hee-Joo; Rutherford, Drew; Hakk, Heldur H; Bergman, Ake; Li, Qing X

2005-05-18

Polybrominated diphenyl ethers (PBDEs) are a class of brominated flame retardants that are increasingly an environmental concern. Several antibodies were developed for the polybrominated diphenyl ether flame retardant BDE-47 (1), often found in the highest concentration in human milk, plasma, and adipose tissue. Four haptens with different bromine and linker substitution patterns were synthesized and utilized to generate five polyclonal antibodies from goats and two polyclonal antibodies from rabbits. Competition was assessed using four different coating antigens for all seven antibodies. The coating antigen showed marked effects on competition. When the same hapten was used for antibody and the coating antigen less competition was observed. The effect of BDE structure on competition was evaluated by using BDE-47 (1), BDE-99 (2), BDE-100 (3), BDE-153 (4), and BDE-183 (5). None of the compounds showed high competition with antibody I-KLH, presumably because steric hindrance prevented formation of an efficient binding site. As predicted from structural considerations, BDE-47 (1) competed well with the remaining antibodies, whereas BDE-100 (3) competed well with only II-KLH. The remaining congeners (BDE-99 (2), BDE-153 (4), and BDE-183 (5)) contain bromines that cannot be positioned in binding sites and thus cross-react poorly. The competition study demonstrated that a bromine substitution on the congener could occupy a position analogous to the linker's position.

Ethoxy (pentafluoro) cyclotriphosphazene (PFPN) as a multi-functional flame retardant electrolyte additive for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Li, Xi; Li, Weikang; Chen, Lai; Lu, Yun; Su, Yuefeng; Bao, Liying; Wang, Jing; Chen, Renjie; Chen, Shi; Wu, Feng

2018-02-01

With the wide application of lithium-ion batteries (LiBs), safety performance is an important constraint on the commercialization of large-scale, high-capacity LIBs. The main reason for the safety problem is that the electrolyte of LiBs is highly flammable, especially under high temperature and high voltage. It is an effective method to improve the safety of cells by mixing flame retardant with conventional electrolyte comprising of LiPF6 and carbonates. Herein, ethoxy (pentafluoro) cyclotriphosphazene (PFPN) is studied as a high efficiency flame retardant. Adding 5 vol% of PFPN results in a non-flammable electrolyte with self-extinguishing time (SET) of 12.38 s g-1 and critical oxygen index (COI) of 22.9, without compromising the capacity of cathode material. The initial discharge capacity of the LiCoO2 electrode with 5% PFPN is 150.7 mAh g-1, with a capacity retention of 99.14% after 30 cycles at 0.1 C. The results show that 5 vol% is the best adding amount of PFPN for electrolyte, which can modify the solid electrolyte interface (SEI). Moreover, PFPN reduces charge transfer resistance of the cells, resulting decreased electrode polarization and enhanced electrochemistry performances at low temperature. These results have confirmed that PFPN has the potential to be a multi-function additive for commercial LIBs production.

Brominated Flame Retardants: Spatial and Temporal Trends in the Environment and Biota from the Pacific Basin Countries

EPA Science Inventory

Brominated flame retardants (BFRs) are used as additive or reactive components in a variety of polymers including high-impact polystyrene and epoxy resins, commercial products such as computers, electronics and electrical equipment, thermal insulation, textiles and furniture foam...

The influences of piperazine-phosphonates derivatives on flame retardancy and thermal behaviors of cotton cellulose

USDA-ARS?s Scientific Manuscript database

In an effort to create the environmentally-friendly flame retardants (FRs) for cotton cellulose, two phosphoramidates derivatives, tetraethyl piperazine-1,4-diyldiphosphonate (PDP) and diethyl 4-methylpiperazin-1-ylphosphoramidate (PAP), have been developed. Both were synthesized in high yield and ...

Toxicokinetics of the Flame Retardant Hexabromocylodecane alpha: Effect of dose, timing, route, repeated exposure and metabolism

EPA Science Inventory

Alpha-hexabromocyclododecane (a-HBCD) is an emerging persistent organic pollutant present in the hexabromocyclododecane (HBCD) commercial mixture. HBCD is used as an additive flame retardant in a wide variety of household consumer products. Three main stereoisomers, alpha (a), be...

Development and validation of a multi-residue method for the analysis of brominated and organophosphate flame retardants in indoor dust.

PubMed

He, Chang; Wang, Xianyu; Thai, Phong; Mueller, Jochen F; Gallen, Christie; Li, Yan; Baduel, Christine

2017-03-01

Flame retardants are associated to numerous adverse health effects, can accumulate in humans and have been used intensively worldwide. Recently, dust has been identified as a major human exposure route for flame retardants. The aim of this study was to develop a multi-residue method using a two-step SPE purification. It enabled us to effectively limit co-extracted matrix/interferets and therefore a simultaneous analysis of brominated and organophosphate flame retardants for indoor dust was achieved. The optimized method was validated according to standard protocol and achieved good accuracy and reproducibility (percent error ranged from -29% to 28%). Standard Reference Material (SRM) for dust was also analysed, and good agreement was found with reported brominated and organophosphate flame retardants (OPFRs) concentrations. The applicability of the validated method was demonstrated by the analysis of ten indoor dust samples from ten Australian homes. Overall 89% of the analytes were detected in these samples. The average concentrations of ∑OPFRs and ∑PBDEs in those samples were 41 and 3.6μg/g, respectively. Tris(2-butoxyethyl) phosphate and tris(2-chloroisopropyl) phosphate were the most abundant OPFRs, accounting for 57-92% ∑OPFRs, while decabromodiphenyl ether dominated the Polybrominated diphenyl ethers (PBDE) congeners contributing between 71-94% to the ∑PBDEs. Copyright © 2016 Elsevier B.V. All rights reserved.

Approach for achieving flame retardancy while retaining physical properties in a compatible polymer matrix

NASA Technical Reports Server (NTRS)

Williams, Martha K. (Inventor); Smith, Trent M. (Inventor)

2007-01-01

The invention provides polymer blends containing polyhydroxyamide and one or more flammable polymers. The polymer blends are flame retardant and have improved durability and heat stability compared to the flammable polymer portion of the blends. Articles containing the polymer blends are also provided.

NOVEL 'GREENER' ROUTES TO HALOGEN-FREE FLAME RETARDANT MATERIALS

EPA Science Inventory

The increased use of polymeric materials in numerous applications over the past decade has prompted a surge in the need for additives in the polymer industry. Flame retardant (FR) materials are additives that are used to control or reduce/eliminate the risk of fire in flammabl...

Approach for achieving flame retardancy while retaining physical properties in a compatible polymer matrix

NASA Technical Reports Server (NTRS)

Smith, Trent M. (Inventor); Williams, Martha K. (Inventor)

2011-01-01

The invention provides polymer blends containing polyhydroxyamide and one or more flammable polymers. The polymer blends are flame retardant and have improved durability and heat stability compared to the flammable polymer portion of the blends. Articles containing the polymer blends are also provided.

Studies of flammability and thermal degradation for flame retardant cotton fabric with P-N containing derivatives

USDA-ARS?s Scientific Manuscript database

The effectiveness of a phosphoramidate Tetraethyl piperazine-1,4- diyldiphosphoramidate (TEPP) as a flame retardant (FR) on cotton twill fabrics was compared with that of a previously studied Diethyl 4- methylpiperazin-1-ylphosphoramidate (DEPP). TEPP was formed in a reaction between two phosphonat...

Innovative layer-by-layer processing for flame retardant behavior of cotton fabric

USDA-ARS?s Scientific Manuscript database

Flame retardant behavior has been prepared by the layer-by layer assemblies of kaolin/casein with inorganic chemicals on cotton fabrics. Three different kinds of cotton fabrics (print cloth, mercerized print cloth, and mercerized twill fabric) were prepared with solutions of mixture of BPEI, urea, ...

Green application of flame retardant cotton fabric using supercritical carbon dioxide

USDA-ARS?s Scientific Manuscript database

Due to its environmentally benign character, supercritical carbon dioxide (scCO2) is considered in green chemistry as a substitute for organic solvents in chemical reactions. In this poster, an innovative approach for preparation of flame retardant woven and nonwoven fabrics were obtained by utiliz...

Comparison of Air Sampling Methods for Organophosphate Flame Retardants in Small Environmental Chambers

EPA Science Inventory

Organophosphorus flame retardants (OPFRs), such as tris(2-chloroethyl) phosphate (TCEP), tris(1-chlor-2-propyl) phosphate (TCPP), and tris(1,3-dichloro-2-propyl) phosphate (TDCPP), used as additives in industrial and consumer products are being detected in indoor air, house dust,...

Toxicokinetics of the Sterioisomer Specific Flame Retardant Hexabromocyclododecane (HBCD) Gamma: Effect of Dose, Time, and Repeated Exposure

EPA Science Inventory

Hexabromocyclododecanes (HBCDs) are high production volume brominated aliphatic cyclic hydrocarbons used as flame-retardants in foams, plastics and textiles. Commercial HBCD is a mixture of three main stereoisomers, alpha (α), beta (β) and gamma (γ). A shift from the high percent...

Using the parallelogram approach to estimate human percutaneous bioavailability for novel & legacy brominated flame retardants

EPA Science Inventory

(This is an extended abstract. The following text was taken from the Discussion and Conclusion section.) Humans are frequently exposed to brominated flame retardants (BFRs), especially via dermal contact with contaminated dust. Human and rat skin data were integrated using a pa...

Bioaccumulation and Effects of the Alternative Flame Retardant, Bis(2-ethylhexyl) tetrabromophthalate (TBPH), in Atlantic killifish, Fundulus heteroclitus

EPA Science Inventory

Bis(2-ethylhexyl) tetrabromophthalate (TBPH), is a high production volume chemical classified as an alternative flame retardant (FR), which replaces legacy FRs withdrawn from US markets dues to health and environmental concerns. This study provides experimental data on the bioacc...

Effects of Organophosphorus Flame Retardants on Spontaneous Activity in Neuronal Networks Grown on Microelectrode Arrays

EPA Science Inventory

EFFECTS OF ORGANOPHOSPHORUS FLAME RETARDANTS ON SPONTANEOUS ACTIVITY IN NEURONAL NETWORKS GROWN ON MICROELECTRODE ARRAYS TJ Shafer1, K Wallace1, WR Mundy1, M Behl2,. 1Integrated Systems Toxicology Division, NHEERL, USEPA, RTP, NC, USA, 2National Toxicology Program, NIEHS, RTP, NC...

Effects of brominated flame retardants on calcium buffering mechanisms in rat brain in vitro.

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs; used as additive flame-retardants) have been detected in human blood, adipose tissue, and breast milk. Developmental and long-term exposures to these chemicals may pose a human health risk, especially to children. It has been demonstrated th...

TSCA Work Plan Chemical Problem Formulation and Initial Assessment Tetrabromobisphenol A and Related Chemicals Cluster Flame Retardants

EPA Pesticide Factsheets

EPA released a problem formulation for TBBPA and related chemicals used as a flame retardants in plastics/printed circuit boards for electronics. The goal of this problem formulation was to identify scenarios where further risk analysis may be necessary.

Comparative study of through-air bonded and thermal calendered nonwovens

USDA-ARS?s Scientific Manuscript database

Over the years there has been increasing interest in developing flame retardant (FR) cotton-based nonwovens. Whereas majority of the work has been done with high loft nonwovens, since this has been of interest to bedding and home furnishing industry, the effect of web density on flame retardancy is ...

Utilizing alternative developmental and neurotoxicity screening methods to prioritize compounds for further mammalian testing

EPA Science Inventory

Due to their toxicity and persistence in the environment, brominated flame retardants (BFRs) are being phased out of commercial use, leading to the increased use of alternative chemicals such as the organophosphorus flame retardants (OPFRs). Due to the structural similarity of th...

Heat sealable, flame and abrasion resistant coated fabric. [clothing and containers for space exploration

NASA Technical Reports Server (NTRS)

Tschirch, R. P.; Sidman, K. R. (Inventor)

1981-01-01

Flame retardant, abrasion resistant elastomeric compositions are comprised of thermoplastic polyurethane polymer and flame retarding amounts of a filler selected from decabromodiphenyloxide and antimony oxide in a 3:1 weight ratio, and decabromodiphenyloxide, antimony oxide, and ammonium polyphosphate in a 3:1:3 weight ratio respectively. Coated fabrics employing such elastomeric compositions as coating film are flexible, lightweight, and air impermeable and can be made using heat or dielectric sealing procedures.

Environmental Impact of Flame Retardants (Persistence and Biodegradability)

PubMed Central

Segev, Osnat; Kushmaro, Ariel; Brenner, Asher

2009-01-01

Flame-retardants (FR) are a group of anthropogenic environmental contaminants used at relatively high concentrations in many applications. Currently, the largest market group of FRs is the brominated flame retardants (BFRs). Many of the BFRs are considered toxic, persistent and bioaccumulative. Bioremediation of contaminated water, soil and sediments is a possible solution for the problem. However, the main problem with this approach is the lack of knowledge concerning appropriate microorganisms, biochemical pathways and operational conditions facilitating degradation of these chemicals at an acceptable rate. This paper reviews and discusses current knowledge and recent developments related to the environmental fate and impact of FRs in natural systems and in engineered treatment processes. PMID:19440395

Flame Retardant Epoxy Resins

NASA Technical Reports Server (NTRS)

Thompson, C. M.; Smith, J. G., Jr.; Connell, J. W.; Hergenrother, P. M.; Lyon, R. E.

2004-01-01

As part of a program to develop fire resistant exterior composite structures for future subsonic commercial aircraft, flame retardant epoxy resins are under investigation. Epoxies and their curing agents (aromatic diamines) containing phosphorus were synthesized and used to prepare epoxy formulations. Phosphorus was incorporated within the backbone of the epoxy resin and not used as an additive. The resulting cured epoxies were characterized by thermogravimetric analysis, propane torch test, elemental analysis and microscale combustion calorimetry. Several formulations showed excellent flame retardation with phosphorous contents as low as 1.5% by weight. The fracture toughness of plaques of several cured formulations was determined on single-edge notched bend specimens. The chemistry and properties of these new epoxy formulations are discussed.

Polybrominated diphenyl ether (PBDE) concentrations and resulting exposure in homes in California: relationships among passive air, surface wipe and dust concentrations, and temporal variability

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) are used as flame retardants in furniture foam, electronics, and other home furnishings. A field study was conducted that enrolled 139 households from California, which has had more stringent flame retardant requirements than other countries...

Brominated flame retardant levels in human milk and serum from MAMA study participants: Correlations over time, matrix, and with questionnaire results

EPA Science Inventory

Brominated flame retardants (BFRs) are synthetic, lipophilic, and bioaccumulative compounds used to prevent the combustion of a variety of items including electronics and furniture. There are 75 classes of BFRs, two of which are the polybrominated biphenyls (PBB) and the polybrom...

Layer-by-Layer Assembly of Halogen-Free Polymeric Materials on Nylon/Cotton Blend for Flame Retardant Applications

DTIC Science & Technology

2015-07-01

phosphate) and renewable materials such as chitosan , phytic acid and graphene oxide [18–26]. However, polysiloxane containing FR materials have...98:627–634. 24. Laufer G, Kirkland C, Cain AA, Grunlan JC. Clay– chitosan nanobrick walls: completely renewable gas barrier and flame-retardant

Intumescent flame-retardant cotton produced by tannic acid and sodium hydroxide

USDA-ARS?s Scientific Manuscript database

This study showed that tannic acid can form intumescent flame-retardant coating on cotton nonwoven fabric with an aid of NaOH. Tannic acid alone altered the thermal patterns of the pyrolysis and combustion of cotton and increased the char yield, but its improvement in limiting oxygen index (LOI) wa...

Thermal decomposition reactions of cotton fabric treated with piperazine-phosphonates derivatives as a flame retardant

USDA-ARS?s Scientific Manuscript database

There has been a great scientific interest in exploring the great potential of the piperazine-phosphonates in flame retardant (FR) application on cotton fabric by investigating the thermal decomposition of cotton fabric treated with them. This research tries to understand the mode of action of the t...

Multi-class, multi-residue analysis of pesticides, polychlorinated biphenyls, polycyclic aromatic hydrocarbons, polybrominated diphenyl ethers and novel flame retardants....mass spectrometry

USDA-ARS?s Scientific Manuscript database

A multi-class, multi-residue method for the analysis of 13 novel flame retardants, 18 representative pesticides, 14 polychlorinated biphenyl (PCB) congeners, 16 polycyclic aromatic hydrocarbons (PAHs), and 7 polybrominated diphenyl ether (PBDE) congeners in catfish muscle was developed and evaluated...

Toxicokinetics of the flame retardant hexabromocyclododecane alpha: effect of dose, timing, route, repeated exposure and metabolism

USDA-ARS?s Scientific Manuscript database

Hexabromocyclododecane (HBCD) is an additive flame retardant in many household products. Three stereoisomers, alpha (a), beta (b), and gamma (g), comprise roughly 10%, 10%, and 80% of the mixture, respectively. a-HBCD is the major stereoisomer found in biota, including breast milk and blood in Nor...

A CASE STUDY ON THE RISKS AND BENEFITS OF DECABDE, A MAJOR BROMINATED FLAME RETARDANT

EPA Science Inventory

This is a proposal for a roundtable presentation at the 2008 Society of Toxicology Annual Meeting. ABSTRACT BODY: Decabromodiphenyl ether (DecaBDE) is a high production volume chemical used as a flame retardant in a variety of consumer applications; examples of uses in h...

[Total dietary exposure assessment of emerging brominated flame retardants in Beijing].

PubMed

Lü, Surong; Niu, Yumin; Zhang, Jing; Shao, Bing; Du, Zhenxia

2016-05-01

To estimate the exposure characteristic of six emerging brominated flame retardant for Beijing residents by dietary intake. 2,3,5,6-tetrabromo-p-xylene (pTBX), pentabromotoluene (PBT), 1, 2, 3, 4, 5-pentabromo-6- ethylbenzene (PBEB), hexahromobenzene (HBB), hexachlorocyclopentadienyl- dibromocyclooctane (DBHCTD) and 1,2-bis(2 ,4 ,6-tribromo phenoxy) ethane (BTBPE) were detected by atmospheric pressure gas chromatography tandem mass spectrometry (APGC-MS/MS) in total dietary samples from Beijing. Dietary intake assessments of human exposure were carried out according to results of determination. PBT, PBEB, HBB and BTBPE were occurred with concentration between 1.2-29.4 pg/g wet weight. The detection rates of HBB and BTBPE in animal--origin samples were higher than those in plant-origin samples, and there were significant differences (P < 0.05). The exposure level of Beijing residents to six emerging brominated flame retardants were 296.8 pg/(kg-d). The exposure level of emerging brominated flame retardants by dietary intake in Beijing is relatively low, and meat is the main source of BTBPE dietary intake.

Preparation of zinc hydroxystannate-decorated graphene oxide nanohybrids and their synergistic reinforcement on reducing fire hazards of flexible poly (vinyl chloride)

NASA Astrophysics Data System (ADS)

Gao, Tingting; Chen, Laicheng; Li, Zhiwei; Yu, Laigui; Wu, Zhishen; Zhang, Zhijun

2016-04-01

A novel flame retardant, zinc hydroxystannate-decorated graphene oxide (ZHS/GO) nanohybrid, was successfully prepared and well characterized. Herein, the ZHS nanoparticles could not only enhance the flame retardancy of GO with the synergistic flame-retardant effect of ZHS but also prevent the restack of GO to improve the mechanical properties of poly (vinyl chloride) (PVC) matrix. The structure characterization showed ZHS nanoparticles were bonded onto the surface of GO nanosheets and the ZHS nanoparticles were well distributed on the surface of GO. Subsequently, resulting ZHS/GO was introduced into flexible PVC and fire hazards and mechanical properties of PVC nanocomposites were investigated. Compared to neat PVC, thermogravimetric analysis exhibited that the addition of ZHS/GO into PVC matrix led to an improvement of the charring amount and thermal stability of char residue. Moreover, the incorporation of 5 wt.% ZHS/GO imparted excellent flame retardancy to flexible PVC, as shown by increased limiting oxygen index, reduced peak heat release rate, and total heat release tested by an oxygen index meter and a cone calorimeter, respectively. In addition, the addition of ZHS/GO nanohybrids decreased the smoke products and increased the tensile strength of PVC. Above-excellent flame-retardant properties are generally attributed to the synergistic effect of GO and ZHS, containing good dispersion of ZHS/GO in PVC matrix, the physical barrier of GO, and the catalytic char function of ZHS.

Levels of Urinary Metabolites of Organophosphate Flame Retardants, TDCIPP, and TPHP, in Pregnant Women in Shanghai

PubMed Central

Ouyang, Fengxiu; Liu, Liangpo; Wang, Xu; Wang, Xia; Li, Yi-Ju; Murtha, Amy; Shen, Heqing; Zhang, Junfeng; Zhang, Jun Jim

2016-01-01

Flame retardants are widely used in consumer products to reduce their flammability. Previously used flame retardants have been sequentially banned due to their environmental and human toxicity. Currently, tris(1,3-dichloropropyl) phosphate (TDCIPP) and triphenyl phosphate (TPHP) are among the most commonly used flame retardants. TDCIPP and TPHP are reproductive toxins and have carcinogenic, neurotoxic, and endocrine-disrupting properties. Although high levels of TDCIPP and TPHP have been found in drinking water, seawater, and office air in China, data regarding human exposure are lacking. In this study, we assessed the level of urinary TPHP and TDCIPP metabolites (DPHP and BDCIPP, resp.) in a cohort of pregnant women (N = 23) from Shanghai, China, using liquid chromatography-tandem mass spectrometry. DPHP were detected in 100% urine samples, while only four urine samples had detectable level of BDCIPP in this cohort (17% detected). Geometric means of DPHP and BDCIPP concentrations were 1.1 ng/mL (interquartile range [IQR]: 0.6, 1.5 ng/mL) and 1.2 ng/mL (IQR: 0.6, 2.2 ng/mL), respectively. In this small cohort, urinary DPHP and BDCIPP levels were not significantly correlated with miscarriages, neonatal birthweight, gestational diabetes, or maternal age. These data suggest that exposure to TPHP is widespread, and they demonstrate the feasibility of using urinary biomarkers to measure exposures to modern flame-retardant chemicals. PMID:28115951

Species-specific accumulation of polybrominated diphenyl ethers (PBDEs) and other emerging flame retardants in several species of birds from Korea.

PubMed

Jin, Xiangzi; Lee, Sunggyu; Jeong, Yunsun; Yu, Jae-Pyoung; Baek, Woon Kee; Shin, Kyung-Hoon; Kannan, Kurunthachalam; Moon, Hyo-Bang

2016-12-01

Few studies have been conducted on the alternatives to legacy flame retardants in avian species worldwide. In this study, polybrominated diphenyl ethers (PBDEs) and alternative flame retardants such as novel brominated flame retardants (NBFRs) and dechlorane plus (DP) were determined in livers of 10 species of birds from Korea to elucidate species-specific accumulation, biological factors that affect accumulation, and bioaccumulation potentials of these contaminants. Among the emerging alternative flame retardants, the highest occurrence was found for bis(2-ethylhexyl)-3,4,5,6-tetrabromo-phthalate (BEHTBP), syn-DP, anti-DP, and decabromodiphenyl ethane (DBDPE). PBDE concentrations (median: 17.1 ng/g lipid wt) measured in our study were within the ranges reported in previous studies, while the concentrations of BEHTBP, BTBPE and DP were greater than those reported earlier. Residential predatory birds showed significantly greater concentrations of PBDEs and NBFRs than migratory predators and passerine birds. The concentrations of PBDEs, BEHTBP, and DP in residential predatory birds were significantly correlated with increasing stable nitrogen isotope ratio (δ 15 N), which indicated biomagnification potentials of these contaminants. Our results suggest that the concentrations and accumulation patterns of PBDEs, NBFRs, and DP depend on the feeding habits and migration patterns of avian species. This is the first report on the accumulation of emerging alternatives to PBDEs in birds from Korea. Copyright © 2016 Elsevier Ltd. All rights reserved.

Study of thermal, flammability and mechanical properties of intumescent flame retardant PP/kenaf nanocomposites

NASA Astrophysics Data System (ADS)

Subasinghe; Das; Bhattacharyya

2016-07-01

Detrimental physical and mechanical properties are common problems for composites when their flame retardancy is improved through filler additions. An increased interest of the synergistic nanoparticle addition to improve the flame retardancy of natural fiber composites is the aim of this work. The paper investigates the synergistic effect of two different nanoparticles (halloysite nanotubes (HNTs) and montmorillonite (MMT) nanoclay) on the flame and mechanical properties in an intumescent ammonium polyphosphate (APP)-based polypropylene (PP)/kenaf composite system. First, the nature of nanoparticle dispersion in PP through X-ray diffraction (XRD) and transmission electron microscopy (TEM) reveals that under twin screw compounding process, the partial exfoliation and intercalation have taken place within the nanocomposites. An increase in the decomposition temperature was observed under thermogravimetric analysis (TGA), with the presence of HNT. However, MMT tends to lower the maximum decomposition temperature under inert atmosphere. The flammability analysis in an intumescent flame retardant (IFR) system shows that the suitable amount of high aspect ratio nanoparticles with their exfoliation characteristics effectively helps to reduce the sustained combustion. Even though, improved stiffness properties can be observed with the presence of increased filler content, particle agglomeration tends to reduce the mechanical strengths of these composites due to low compatibilization and crack propagation.

Intumescent formulations based on lignin and phosphinates for the bio-based textiles

NASA Astrophysics Data System (ADS)

Mandlekar, N.; Cayla, A.; Rault, F.; Giraud, S.; Salaün, F.; Malucelli, G.; Guan, J.

2017-10-01

This study investigates new intumescent formulations based on lignin and phosphinates to improve the flame retardant properties of Polyamide 11, while preserving the bio-based characteristics of this latter. Lignin has the advantage of being a bio-based compound and can be effectively used as carbon source for the design of intumescent systems in combination with other flame retardant additives. Metal phosphinates belong to a novel class of phosphorus flame retardants. Despite their increasing use, there is lack of scientific understanding as far as their fire retardancy mechanism is considered, especially in char forming polymeric materials. In this context, Polyamide 11 was melt blended with lignin and metal phosphinates. The possibility of melt spinning the prepared blends were assessed through melt flow index (MFI) tests; thermogravimetric (TG) analyses and cone calorimetry tests were exploited for investigating the thermal stability and the combustion behaviour of the obtained products, respectively. MFI results indicate that some formulations are suitable for melt spinning processes to generate flame retardant multifilament. Furthermore, the combination of lignin and phosphinates provides charring properties to polyamide 11. Finally, cone calorimetry data confirmed that the designed intumescent formulations could remarkably reduce PHRR through formation of protective char layer, hence slowing down the combustion process.

Study on the Synergetic Fire-Retardant Effect of Nano-Sb₂O₃ in PBT Matrix.

PubMed

Niu, Lei; Xu, Jianlin; Yang, Wenlong; Ma, Jiqiang; Zhao, Jinqiang; Kang, Chenghu; Su, Jiaqiang

2018-06-22

Nano-Sb₂O₃ has excellent synergistic flame-retardant effects. It can effectively improve the comprehensive physical and mechanical properties of composites, reduce the use of flame retardants, save resources, and protect the environment. In this work, nanocomposites specimens were prepared by the melt-blending method. The thermal stability, mechanical properties, and flame retardancy of a nano-Sb₂O₃⁻brominated epoxy resin (BEO)⁻poly(butylene terephthalate) (PBT) composite were analyzed, using TGA and differential scanning calorimetry (DSC), coupled with EDX analysis, tensile testing, cone calorimeter tests, as well as scanning electron microscopy (SEM) and flammability tests (limiting oxygen index (LOI), UL94). SEM observations showed that the nano-Sb₂O₃ particles were homogeneously distributed within the PBT matrix, and the thermal stability of PBT was improved. Moreover, the degree of crystallinity and the tensile strength were improved, as a result of the superior dispersion and interfacial interactions between nano-Sb₂O₃ and PBT. At the same time, the limiting oxygen index and flame-retardant grade were increased as the nano-Sb₂O₃ content increased. The results from the cone calorimeter test showed that the peak heat release rate (PHRR), total heat release rate (THR), peak carbon dioxide production (PCO₂P), and peak carbon monoxide production (PCOP) of the nanocomposites were obviously reduced, compared to those of the neat PBT matrix. Meanwhile, the SEM⁻energy dispersive spectrometry (EDX) analysis of the residues indicated that a higher amount of C element was left, thus the charring layer of the nanocomposites was compact. This showed that nano-Sb₂O₃ could promote the degradation and charring of the PBT matrix, improving thermal stability and flame retardation.

Degradation of brominated flame retardant in computer housing plastic by supercritical fluids.

PubMed

Wang, Yanmin; Zhang, Fu-Shen

2012-02-29

The degradation process of brominated flame retardant (BFR) and BFR-containing waste computer housing plastic in various supercritical fluids (water, methanol, isopropanol and acetone) was investigated. The results showed that the debromination and degradation efficiencies, final products were greatly affected by the solvent type. Among the four tested solvents, isopropanol was the most suitable solvent for the recovery of oil from BFR-containing plastic for its (1) excellent debromination effectiveness (debromination efficiency 95.7%), (2) high oil production (60.0%) and (3) mild temperature and pressure requirements. However, in this case, the removed bromine mostly existed in the oil. Introduction of KOH into the sc-isopropanol could capture almost all the inorganic bromine from the oil thus bromine-free oil could be obtained. Furthermore, KOH could enhance the depolymerization of the plastic. The obtained oil mainly consisted of single- and duplicate-ringed aromatic compounds in a carbon range of C9-C17, which had alkyl substituents or aliphatic bridges, such as butyl-benzene, (3-methylbutyl)-benzene, 1,1'-(1,3-propanediyl)bis benzene. Phenol, alkyl phenols and esters were the major oxygen-containing compounds in the oil. This study provides an efficient approach for debromination and simultaneous recovering valuable chemicals from BFR-containing plastic in e-waste. Copyright © 2011 Elsevier B.V. All rights reserved.

Determination of organophosphate flame retardants in soil and fish using ultrasound-assisted extraction, solid-phase clean-up, and liquid chromatography with tandem mass spectrometry.

PubMed

Lorenzo, María; Campo, Julián; Picó, Yolanda

2018-03-22

A solid-liquid extraction method in combination with high-performance liquid chromatography and tandem mass spectrometry was developed and optimized for extraction and analysis of organophosphorus flame retardants in soil and fish. Methanol was chosen as the optimum extraction solvent, not only in terms of extraction efficiency, but also for its broader analyte coverage. The subsequent clean-up by solid-phase extraction is required to eliminate matrix coextractives and reduce matrix effects. Recoveries of the optimized method were 50-121% for soil and 47-123% for biota, both with high precision (RSDs <12% in soil and <23% in biota). The method limits of detection ranged from 0.06 to 0.20 ng/g dry weight and between 0.02 and 0.30 ng/g wet weight for soil and biota samples, respectively. However, samples with a high lipid content produce several problems as solid-phase extraction cartridge clogging that increase variability and analysis time. The method was successfully applied for the determination of organophosphorus flame retardants in soil and fish from L'Albufera Natural Park (Valencia, Spain). Target compounds were detected in all soil and fish samples with values varying from 13.8 to 89.7 ng/g dry weight and from 3.3 to 53.0 ng/g wet weight, respectively. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Functionalized Carbon Nanotubes with Phosphorus- and Nitrogen-Containing Agents: Effective Reinforcer for Thermal, Mechanical, and Flame-Retardant Properties of Polystyrene Nanocomposites.

PubMed

Xing, Weiyi; Yang, Wei; Yang, Wenjie; Hu, Qihang; Si, Jingyu; Lu, Hongdian; Yang, Benhong; Song, Lei; Hu, Yuan; Yuen, Richard K K

2016-10-05

Aminated multiwalled carbon nanotubes (A-MWCNT) were reacted with diphenylphosphinic chloride (DPP-Cl) to prepare the functionalized MWCNT (DPPA-MWCNT). A-MWCNT and DPPA-MWCNT were respectively mixed with polystyrene (PS) to obtain composites through the melt compounding method. SEM observations demonstrated that the DPPA-MWCNT nanofillers were more uniformly distributed within the PS matrix than A-MWCNT. PS/DPPA-MWCNT showed improved thermal stability, glass transition temperature, and tensile strength in comparison with PS/A-MWCNT, resulting from good dispersion and interfacial interactions between DPPA-MWCNT and PS matrix. The incorporation of DPPA-MWCNT to PS significantly reduced peak heat release rate, smoke production rate, and carbon monoxide and carbon dioxide release in cone calorimeter tests. The enhanced fire-retardant properties should be ascribed to the barrier effect of carbon nanotubes, which could provide enough time for DPPA-MWCNT and its functionalized groups to trap the degrading polymer radicals to catalyze char formation. The char layer served as an efficient insulating barrier to reduce the exposure of polymer matrix to an external heat source as well as retarding the flammable gases from feeding the flame.

Synthesis and characterization of a novel phosphorus-nitrogen containing flame retardant and its application for textile

USDA-ARS?s Scientific Manuscript database

The economic and environmentally friendly flame retardant compound, tetramethyl (6-chloro-1,3,5-triazine-2,4-diyl)bis(oxy)bis (methylene)diphosphonate (FR-1) was synthesized by a simple 2 step procedure from dimethyl phosphate, and its chemical structure was characterized by 1H, 13C, and 31P nuclea...

Cone calorimeter evaluation of two flame retardant cotton fabrics

Treesearch

Robert H. White; Sunghyun Nam; Dharnidhar V. Parikh

2012-01-01

Unbleached (gray) cotton needle-punched nonwoven (NW) fabrics with 12.5% polypropylene scrim were treated with two phosphate–nitrogen-based flame retardant (FR) formulations, Southern Regional Research Center (SRRC)-1 and SRRC-2. The SRRC-1 formulation contains diammonium phosphate as the FR chemical along with urea and dimethyloldihydroxyethyleneurea. Because a trace...

BASS Hardware Setup

NASA Image and Video Library

2016-01-27

ISS046e025945 (01/27/2016) --- NASA astronaut Tim Kopra sets up hardware for the Burning and Suppression of Solids – Milliken, or BASS-M, experiment. The BASS-M investigation tests flame-retardant cotton fabrics to determine how well they resist burning in microgravity. Results benefit research on flame-retardant textiles that can be used on Earth and in space

Estimation of human percutaneous uptake for two novel brominated flame retardants, 2-ethylhexyl tetrabromobenzoate (TBB) and bis(2-ethylhexyl) tetrabromophthalate (TBPH) using the parallelogram method

EPA Science Inventory

2-ethylhexyl- tetrabromobenzoate (TBB) and bis(2-ethylhexyl)-tetrabromobenzoate (TBPH) are novel brominated flame retardants (FRs). TBPH is used as a plasticizer or with TBB in polyurethane foam FRs. TBB & TBPH have been detected in both indoor and outdoor environmental sampl...

TOXICOKINETICS OF THE FLAME RETARDANT HEXABROMOCYCLODODECANE GAMMA: EFFECT OF DOSE, TIMING, ROUTE, REPEATED EXPOSURE AND METABOLISM

EPA Science Inventory

1,2,5,6,9,10-Hexabromocyc1ododecane-gamma (y-HBCD) is the predominate diastereoisomer in the commercial HBCD mixture used as a flame retardant in a wide variety of consumer products. Three main diastereoisomers, alpha (a), beta (B) and gamma (y) comprise the commercial mixture. D...

Comprehensive Environmental Assessment Applied to Multiwalled Carbon Nanotube Flame-Retardant Coatings in Upholstery Textiles: A Case Study Presenting Priority Research Gaps for Future Risk Assessments (Final Report)

EPA Science Inventory

In September 2013, EPA announced the availability of the final report, Comprehensive Environmental Assessment Applied to Multiwalled Carbon Nanotube Flame-Retardant Coatings in Upholstery Textiles: A Case Study Presenting Priority Research Gaps for Future Risk Assessments...

Nanomaterial Case Study: A Comparison of Multiwalled Carbon Nanotube and Decabromodiphenyl Ether Flame-Retardant Coatings Applied to Upholstery Textiles (Independent Peer Review Draft)

EPA Science Inventory

This Independent Peer Review Draft document presents a case study of multiwalled carbon nanotubes (MWCNTs); it focuses on the specific example of MWCNTs as used in flame-retardant coatings applied to upholstery textiles. This case study is organized around the comprehensive envir...

Effect of urea additive on the thermal decomposition kinetics of flame retardant greige cotton nonwoven fabric

Treesearch

Sunghyun Nam; Brian D. Condon; Robert H. White; Qi Zhao; Fei Yao; Michael Santiago Cintrón

2012-01-01

Urea is well known to have a synergistic action with phosphorus-based flame retardants (FRs) in enhancing the FR performance of cellulosic materials, but the effect of urea on the thermal decomposition kinetics has not been thoroughly studied. In this study, the activation energy (Ea) for the thermal decomposition of greige...

Flame resistant elastic elastomeric fiber

NASA Technical Reports Server (NTRS)

Howarth, J. T.; Sheth, S.; Massucco, A. A.; Sidman, K. R.

1974-01-01

Compositions exhibit elastomeric properties and possess various degrees of flame resistance. First material polyurethane, incorporates halogen containing polyol and is flame resistant in air; second contains spandex elastomer with flame retardant additives; and third material is prepared from fluorelastomer composition of copolymer of vinylidene fluoride and hexafluoropropylene.

Optimization of microwave-assisted extraction with saponification (MAES) for the determination of polybrominated flame retardants in aquaculture samples.

PubMed

Fajar, N M; Carro, A M; Lorenzo, R A; Fernandez, F; Cela, R

2008-08-01

The efficiency of microwave-assisted extraction with saponification (MAES) for the determination of seven polybrominated flame retardants (polybrominated biphenyls, PBBs; and polybrominated diphenyl ethers, PBDEs) in aquaculture samples is described and compared with microwave-assisted extraction (MAE). Chemometric techniques based on experimental designs and desirability functions were used for simultaneous optimization of the operational parameters used in both MAES and MAE processes. Application of MAES to this group of contaminants in aquaculture samples, which had not been previously applied to this type of analytes, was shown to be superior to MAE in terms of extraction efficiency, extraction time and lipid content extracted from complex matrices (0.7% as against 18.0% for MAE extracts). PBBs and PBDEs were determined by gas chromatography with micro-electron capture detection (GC-muECD). The quantification limits for the analytes were 40-750 pg g(-1) (except for BB-15, which was 1.43 ng g(-1)). Precision for MAES-GC-muECD (%RSD < 11%) was significantly better than for MAE-GC-muECD (%RSD < 20%). The accuracy of both optimized methods was satisfactorily demonstrated by analysis of appropriate certified reference material (CRM), WMF-01.

Chicago's Sanitary and Ship Canal sediment: Polycyclic aromatic hydrocarbons, polychlorinated biphenyls, brominated flame retardants, and organophosphate esters.

PubMed

Peverly, Angela A; O'Sullivan, Colin; Liu, Liang-Ying; Venier, Marta; Martinez, Andres; Hornbuckle, Keri C; Hites, Ronald A

2015-09-01

The Chicago Sanitary and Ship Canal (CSSC) links the Great Lakes to the Mississippi River starting in downtown Chicago. In addition to storm water, the CSSC receives water from Chicago's wastewater treatment plants (WWTP). Such effluents are known to be sources of organic pollutants to water and sediment. Therefore in 2013, we collected 10 sediment samples from the CSSC and measured the concentrations of polycyclic aromatic hydrocarbons (PAHs), polychlorinated biphenyls (PCBs), brominated flame retardants, and organophosphate esters (OPEs). Geometric mean concentrations of the summed concentrations of 16 PAHs ranged from 11,000 to 420,000 ng/g dw, with the highest concentrations located at each end of the canal. Total PCB concentrations had a geometric mean of 1,400 ± 500 ng/g dw. Brominated flame retardants were separated into two groups: polybrominated diphenyl ethers (PBDEs) and non-PBDEs. Concentrations of PBDEs and those of the non-PBDE flame retardants had a geometric average of 83 ± 19 and 7.0 ± 5.8 ng/g dw, respectively. The summed concentrations of 8 OPEs ranged from 470 to 2,800 ng/g dw, with the highest concentration detected at a site located downstream of the Stickney water reclamation plant. Using ANOVA results, some hypotheses on sources to the CSSC could be formulated: downtown Chicago is probably a source of PAHs, the Cal-Sag Channel may be a source of PCBs, and neither the WWTP nor the Cal-Sag Channel seem to be significant sources of brominated flame retardants or OPEs. Copyright © 2015 Elsevier Ltd. All rights reserved.

Editor’s Highlight: Comparative Toxicity of Organophosphate Flame Retardants and Polybrominated Diphenyl Ethers to Caenorhabditis elegans

PubMed Central

Behl, Mamta; Rice, Julie R.; Smith, Marjo V.; Co, Caroll A.; Bridge, Matthew F.; Hsieh, Jui-Hua; Freedman, Jonathan H.; Boyd, Windy A.

2016-01-01

With the phasing-out of the polybrominated diphenyl ether (PBDE) flame retardants due to concerns regarding their potential developmental toxicity, the use of replacement compounds such as organophosphate flame retardants (OPFRs) has increased. Limited toxicity data are currently available to estimate the potential adverse health effects of the OPFRs. The toxicological effects of 4 brominated flame retardants, including 3 PBDEs and 3,3',5,5'-tetrabromobisphenol A, were compared with 6 aromatic OPFRs and 2 aliphatic OPFRs. The effects of these chemicals were determined using 3 biological endpoints in the nematode Caenorhabditis elegans (feeding, larval development, and reproduction). Because C. elegans development was previously reported to be sensitive to mitochondrial function, results were compared with those from an in vitro mitochondrial membrane permeabilization (MMP) assay. Overall 11 of the 12 flame retardants were active in 1 or more C. elegans biological endpoints, with only tris(2-chloroethyl) phosphate inactive across all endpoints including the in vitro MMP assay. For 2 of the C. elegans endpoints, at least 1 OPFR had similar toxicity to the PBDEs: triphenyl phosphate (TPHP) inhibited larval development at levels comparable to the 3 PBDEs; whereas TPHP and isopropylated phenol phosphate (IPP) affected C. elegans reproduction at levels similar to the PBDE commercial mixture, DE-71. The PBDEs reduced C. elegans feeding at lower concentrations than any OPFR. In addition, 9 of the 11 chemicals that inhibited C. elegans larval development also caused significant mitochondrial toxicity. These results suggest that some of the replacement aromatic OPFRs may have levels of toxicity comparable to PBDEs. PMID:27566445

Flame Retardant Fibers for Human Space Exploration - Past, Present, and Future

NASA Technical Reports Server (NTRS)

Orndoff, Evelyne

2017-01-01

The National Aeronautics and Space Administration (NASA) has led the development of unique flame retardant fibers for the specific requirements of different space programs. Three of these fibers have greatly contributed to the safety of all the space missions since the Apollo program. Beta alumina-silica microfiber developed for the outer layer of the space suit after the Apollo 1 fire is no longer used and has been replaced by other glass fibers. Expanded polytetrafluoroethylene (e-PTFE) fiber used in the current spacesuit is mostly known today through its trade mark Gore-Tex®. Polybenzimidazole (PBI) filament fiber used in many applications from the Apollo to the Space Shuttle program is no longer available. More recently, TOR"TM" copolymer of polyimide fiber developed during the space shuttle program to resist the atomic oxygen present in Low Earth Orbit has been barely used. The high cost and narrow range of aeronautical and aerospace applications have, however, led to a limited production of these fibers. Only fibers that found niche markets survived. Yet, deep space exploration will require more of these inherently flame retardant fibers than what is available today. There is a need for new flame retardant fabrics inside the space vehicles as well as a need for logistics reduction for long term space missions. Materials like modacrylic and polyimide are good candidates for future flame retardant aerospace fabrics. New fabrics must be developed for astronauts' clothing, as well as crew quarters and habitat. Therefore, both staple and filament fibers of various linear densities are needed for a three years mission to Mars.

A study of the dynamic flammability of radiation cross-linked flame-retardant HDPE/EPDM/silicon-elastomer compound

NASA Astrophysics Data System (ADS)

Jia, Shaojin; Zhang, Zhicheng; Du, Zhiwen; Teng, Renrui; Wang, Zhengzhou

2003-04-01

A dynamic flammability study of flame-retardant compound consisting of HDPE, EPDM and silicon elastomer blended with additives, as wire and cable insulation was made before and after irradiation. The data of RHR, EHC, SEC and the concentration of CO and CO 2 from cone colorimeter shown in the burning process were accessed. By blending silicon elastomer, CO release rate was reduced and the thermal endurance was improved. Oxygen index, mechanical property, morphology of the char formed in dynamical flame and thermal stability were also investigated.

Guide to PBDE: Toxic Flame Retardant--What Women, Children and School Personnel Need to Know. Revised

ERIC Educational Resources Information Center

Healthy Schools Network, Inc., 2012

2012-01-01

Chemical flame-retardants are used in a variety of products to prevent the spread and occurrence of fire. While fire safety is critical, this family of chemicals, known as Polybrominated diphenyl ethers (PBDEs) are highly toxic. They are found in carpeting, foam cushions, polyester clothing and bedding, wallpaper, toys, household dust, a variety…

Estimation of human percutaneous bioavailability for two novel brominated flame retardants, 2-ethylhexyl tetrabromobenzoate (EH-TBB) and bis(2-ethylhexyl) tetrabromophthalate (BEH-TEBP), using the parallelogram approach

EPA Science Inventory

2-ethylhexyltetrabromobenzoate (EH-TBB) and bis(2-ethylhexyl)tetrabromophthalate (BEH-TEBP) are novel brominated flame retardants (FRs). BEH-TEBP is used alone as a plasticizer or with EH-TBB in polyurethane foams; both are contaminants in the indoor and outdoor environments. In ...

Gene Transcription, Metabolite and Lipid Profiling in Eco-Indicator Daphnia magna Indicate Diverse Mechanisms of Toxicity by Legacy and Emerging Flame-Retardants

EPA Science Inventory

The use of chemical flame-retardants (FR) in consumer products has steadily increased over the last 30 years. Toxicity data exist for legacy FRs such as pentabromodiphenyl ether (pentaBDE), but less is known about effects of new formulations. To address this issue, the toxicity o...

Chemical regulation on fire: rapid policy advances on flame retardants.

PubMed

Cordner, Alissa; Mulcahy, Margaret; Brown, Phil

2013-07-02

Chemicals that are widely used in consumer products offer challenges to product manufacturers, risk managers, environmental regulators, environmental scientists, and the interested public. However, the factors that cause specific chemicals to rise to the level of regulatory, scientific, and social movement concern and scrutiny are not well documented, and scientists are frequently unclear about exactly how their research impacts policy. Through a case study of advocacy around flame retardant chemicals, this paper traces the pathways through which scientific evidence and concern is marshaled by both advocacy groups and media sources to affect policy change. We focus our analysis around a broad coalition of environmental and public health advocacy organizations and an investigative journalism series published in 2012 in the Chicago Tribune. We demonstrate that the Tribune series both brought the issue to a wider public audience and precipitated government action, including state policy revisions and federal Senate hearings. We also show how a broad and successful flame retardant coalition developed, leveraged a media event, and influenced policy at multiple institutional levels. The analysis draws on over 110 in-depth interviews, literature and Web site reviews, and observations at a flame retardant manufacturing company, government offices, and scientific and advocacy conferences.

Flame retardants: Dust - And not food - Might be the risk.

PubMed

de Boer, J; Ballesteros-Gómez, A; Leslie, H A; Brandsma, S H; Leonards, P E G

2016-05-01

Flame retardants (FRs) are used to delay ignition of materials such as furniture and electric and electronic instruments. Many FRs are persistent and end up in the environment. Environmental studies on flame retardants (FRs) took off in the late 1990s. Polybrominated diphenylethers (PBDEs) appeared to be bioaccumulative and were found in many organisms all over the world. When PBDEs were banned or their production voluntarily terminated, alternatives appeared on the market that often had similar properties or were of more concern due to their toxicity such as halogenated phosphorus-based FRs. Here we show that in spite of the ban on PBDEs more brominated FRs are being produced, an increasing number of other FRs is being applied and FR levels in our homes are much higher than in the outdoor environment. While nowadays we live in better isolated houses and sit in front of the computer or television, on flame retarded upholstery, we are at risk due to the toxic effects of a suite of FRs. The high exposure to these substances indoors calls for better risk assessments that include mixture effects. Copyright © 2015 Elsevier Ltd. All rights reserved.

The properties of neutron shielding and flame retardant of EVA polymer after modified by EB accelerator

NASA Astrophysics Data System (ADS)

Wang, Guo-hui; He, Man-li; Jiang, Dan-feng; He, Fan; Chang, Shu-quan; Dai, Yao-dong

2017-11-01

According to the requirements for neutron shielding and flame retardant properties of some nuclear devices, a new kind of polymer composite materials based on ethylene and vinyl acetate (EVA) polymer have been studied. EVA is the copolymer of ethylene and vinyl acetate, It can be used as materials for applications due to its flexibility, good processability, and low cost. Insulating EVA can be used for cable sheath, automotive sound damping and many other appication. Boron nitride (BN), zinc borate (ZB), magnesium hydroxide (MH) and EVA consisted the compounds with the properties of neutron shielding and flame retardant. With increasing of the contents of BN and ZB, the neutron shielding performance of materials increased up to 33.08%. With the increasing contents of MH and ZB as flame retardant, oxygen index of material have been improved. The elongation at break and tensile strength of material decreased with the increasing of filler powders. Sheet E was chosen and modified by electron beam accelerator in different doses. After modification by electron beam irradiation the sheets showed varying degrees of transformation in the OI, neutron shielding rate and mechanical properties.

Development of a flameproof elastic elastomeric fiber

NASA Technical Reports Server (NTRS)

Howarth, J. T.; Nilgrom, J.; Massucco, A.; Sheth, S. G.; Dawn, F. S.

1971-01-01

Various flexible polyurethane structures containing halogen were synthesized from polyesters derived from aliphatic or aromatic polyols and dibasic acids. Aliphatic halide structures could not be used because they are unstable at the required reaction temperatures, giving of hydrogen halide which hydrolyzes the ester linkages. In contract, halogen-containing aromatic polyols were stable and satisfactory products were made. The most promising composition, a brominated neopentyl glycol capped with toluene disocyanate, was used as a conventional diisocyanate, in conjunction with hydroxy-terminated polyethers or polyesters to form elastomeric urethanes containing about 10% bromine with weight. Products made in this manner will not burn in air, have an oxygen index value of about 25, and have tensile strength values of about 5,000 psi at 450% elongation. The most efficient additives for imparting flame retardancy to Spandex urethanes are aromatic halides and the most effective of these are the bromide compounds. Various levels of flame retardancy have been achieved depending on the levels of additives used.

Hierarchical Polyphosphazene@Molybdenum Disulfide Hybrid Structure for Enhancing the Flame Retardancy and Mechanical Property of Epoxy Resins.

PubMed

Zhou, Xia; Qiu, Shuilai; Xing, Weiyi; Gangireddy, Chandra Sekhar Reddy; Gui, Zhou; Hu, Yuan

2017-08-30

A novel polyphosphazene (PZS) microsphere@molybdenum disulfide nanoflower (MoS 2 ) hierarchical hybrid architecture was first synthesized and applied for enhancing the mechanical performance and flame retardancy of epoxy (EP) resin via a cooperative effect. Herein, using PZS microsphere as the template, a layer of MoS 2 nanoflowers were anchored to PZS spheres via a hydrothermal strategy. The well-designed PZS@MoS 2 exhibits excellent fire retardancy and a reinforcing effect. The obtained PZS@MoS 2 significantly enhanced the flame-retardant performance of EP composites, which can be proved by thermogravimetric and cone calorimeter results. For instance, the incorporation of 3 wt % PZS@MoS 2 brought about a 41.3% maximum reduction in the peak heat-release rate and decreased by 30.3% maximum in the total heat release, accompanying the higher graphitized char layer. With regard to mechanical property, the storage modulus of EP/PZS@MoS 2 3.0 in the glassy state was dramatically increased to 22.4 GPa in comparison with that of pure EP (11.15 GPa). It is sensible to know that the improved flame-retardant performance for EP composites is primarily assigned to a physical barrier effect of the MoS 2 nanoflowers and the polyphosphazene structure has an positive impact on promoting char formation in the condensed phase.

Life cycle assessment of the application of nanoclays in wire coating

NASA Astrophysics Data System (ADS)

Tellaetxe, A.; Blázquez, M.; Arteche, A.; Egizabal, A.; Ermini, V.; Rose, J.; Chaurand, P.; Unzueta, I.

2012-09-01

A life cycle assessment (LCA) is carried out to compare nanoclay-reinforced polymer wire coatings with conventional ones. While the conventional wire coatings contain standard halogen free retardants, in reinforced coatings, montmorillonite (nanoclay) is incorporated into electric cable linings as a rheological agent for an increased resistance to fire. In addition, a reduced load of standard halogen free retardants is obtained. The synergistic effect of the montmorillonite on traditional flame retardant additives (by the formation of a three-dimensional char network) can lead to a revolution in wire production. The application of nanoclays contributes also to anti-dripping effect and flexibility increase [1]. Some producers have already started commercializing wire with nanotechnology-based coating; in the short term the use of nanoclay in wire coating production will probably reach a significant market share replacing traditional formulations. The main aim of this study is to compare the environmental impacts along the life cycle of a traditional wire coating (mineral flame retardants like ATH or MDH in a polymer matrix) with the nanoclay-reinforced wire coating, where the montmorillonite replaces a low percentage of the mineral flame retardant. The system boundaries of the study include the following unit processes: nanoclay production, thermoplastic material and mineral flame retardants production, cable coating manufacturing by extrusion and different end of life scenarios (recycling, incineration and landfill disposal). Whereas nanoreinforced composites have shown and increased fire retardance, the addition of nanomaterials seems to have no significant relevance in the environmental assessment. However, the lack of nano-specific characterization factors for nanomaterials and emission rates associated to the different life cycle stages -mainly in the extrusion and use phase, where accidental combustions can take place- still remains a challenge for realistic life cycle assessment modelling.

Flame-retardant polyvinyl alcohol membrane with high transparency based on a reactive phosphorus-containing compound

NASA Astrophysics Data System (ADS)

Peng, Sha; Zhou, Ming; Liu, Feiyan; Zhang, Chang; Liu, Xueqing; Liu, Jiyan; Zou, Liyong; Chen, Jia

2017-08-01

Flame-retardant polyvinyl alcohol (PVA) membranes with high transparency and flexibility were prepared by mixing an aqueous solution of a phosphorus-containing acrylic acid (AOPA) with PVA. The reaction between AOPA and PVA, the transparency, the crystallinity and the flexibility of the membrane were investigated with Fourier transform infrared spectrometry (FTIR), UV-vis light transmittance, X-ray diffraction and tensile tests, respectively. The limited oxygen index (LOI) and vertical flame (UL 94 VTM), microscale combustion calorimetry, thermogravimetric analysis (TGA) and TGA-FTIR were employed to evaluate the flame retardancy as well as to reveal the corresponding mechanisms. Results showed that PVA containing 30 wt% of AOPA can reach the UL 94 VTM V0 rating with an LOI of 27.3% and retain 95% of the original transparency of pure PVA. Adding AOPA reduces crystallinity of PVA, while the flexibility is increased. AOPA depresses the thermal degradation of PVA and promotes char formation during combustion. The proposed decomposition mechanism indicates that AOPA acts mainly in the condensed phase.

Detection of Organophosphate Flame Retardants in Furniture Foam and US House Dust

PubMed Central

Stapleton, Heather M.; Klosterhaus, Susan; Eagle, Sarah; Fuh, Jennifer; Meeker, John D.; Blum, Arlene; Webster, Thomas F.

2009-01-01

Restrictions on the use of polybrominated diphenyl ethers (PBDEs) have resulted in the increased use of alternate flame retardant chemicals to meet flammability standards. However, it has been difficult to determine which chemical formulations are currently being used in high volumes to meet flammability standards since the use of flame retardant formulations in consumer products is not transparent (i.e. not provided to customers). To investigate chemicals being used as replacements for PentaBDE in polyurethane foam, we analyzed foam samples from 26 different pieces of furniture purchased in the United States primarily between 2003 and 2009 using gas chromatography mass spectrometry. Samples included foam from couches, chairs, mattress pads, pillows, and, in one case, foam from a sound proofing system of a laboratory grade dust sieve. Fifteen of the foam samples contained the flame retardant tris(1,3-dichloro-2-propyl) phosphate (TDCPP; 1–5% by weight), four samples contained tris(1-chloro-2-propyl) phosphate (TCPP; 0.5 –2.2 % by weight), one sample contained brominated chemicals found in a new flame retardant mixture called Firemaster 550 (4.2% by weight), and one foam sample collected from a futon likely purchased prior to 2004 contained PentaBDE (0.5% by weight). Due to the high frequency of detection of the chlorinated phosphate compounds in furniture foam, we analyzed extracts from 50 house dust samples collected between 2002 and 2007 in the Boston, MA area for TDCPP, TCPP, and another high volume use organophosphate-based flame retardant used in foam, triphenylphosphate (TPP). Detection frequencies for TDCPP and TPP in the dust samples were >96% and were log normally distributed, similar to observations for PBDEs. TCPP was positively detected in dust in only 24% of the samples, but detection was significantly limited by a co-elution problem. The geometric mean concentrations for TCPP, TDCPP and TPP in house dust were 570, 1890, and 7360 ng/g, respectively, and maximum values detected in dust were 5490, 56,080 and 1,798,000 ng/g, respectively. These data suggest that levels of these organophosphate flame retardants are comparable, or in some cases, greater than, levels of PBDEs in house dust. The high prevalence of these chemicals in foam and the high concentrations measured in dust (as high as 1.8 mg/g), warrant further studies to evaluate potential health effects from dust exposure, particularly for children. PMID:19848166

Cyanuric Chloride and Hexachlorocyclotriphosphazene Derivatives as Flame Retardants in Cotton Textile Applications

USDA-ARS?s Scientific Manuscript database

In a series of experiments cyanuric chloride and hexachlorocyclotriphosphazene derivatives were synthesized and characterized using spectroscopic, thermogravimetric, limiting oxygen index, and vertical flame analyses. Standardized test results have determined these compounds are promising flame reta...

The GhTT2_A07 gene is linked to the brown color and natural flame retardancy phenotypes of Lc1 cotton (Gossypium hirsutum L.) fibers

USDA-ARS?s Scientific Manuscript database

Some naturally-colored brown cotton fibers from accessions of Gossypium hirsutum L. can be used to make textiles with enhanced flame retardancy (FR). Several independent brown fiber loci have been identified and mapped to chromosomes, but the underlying genes have not yet been identified, and the me...

Application of a phosphazene derivative as a flame retardant for cotton fabric using conventional method and supercritical CO2

USDA-ARS?s Scientific Manuscript database

Conventional pad-dry-cure (non-scCO2) and supercritical carbon dioxide (scCO2) application methods were investigated to study the effectiveness of a phosphazene derivative as a flame retardant on cotton fabric. 1,1',4,5-tetrahydrotrispiro[1,3,2-diazaphosphole-2,2'-[1,3,5,2,4,6]triazatriphosphinine-4...

The GhTT2_A07 gene is linked to the brown colour and natural flame retardancy phenotypes of Lc1 cotton (Gossypium hirsutum L.) fibres

USDA-ARS?s Scientific Manuscript database

Some naturally-coloured brown cotton fibres from accessions of Gossypium hirsutum can be used to make textiles with enhanced flame retardancy (FR). Several independent brown fibre loci have been identified and mapped to chromosomes, but the underlying genes have yet to be identified, and the mechan...

Novel and high volume use flame retardants in US couches reflective of the 2005 PentaBDE phase out.

PubMed

Stapleton, Heather M; Sharma, Smriti; Getzinger, Gordon; Ferguson, P Lee; Gabriel, Michelle; Webster, Thomas F; Blum, Arlene

2012-12-18

California's furniture flammability standard Technical Bulletin 117 (TB 117) is believed to be a major driver of chemical flame retardant (FR) use in residential furniture in the United States. With the phase-out of the polybrominated diphenyl ether (PBDE) FR mixture PentaBDE in 2005, alternative FRs are increasingly being used to meet TB 117; however, it was unclear which chemicals were being used and how frequently. To address this data gap, we collected and analyzed 102 samples of polyurethane foam from residential couches purchased in the United States from 1985 to 2010. Overall, we detected chemical flame retardants in 85% of the couches. In samples purchased prior to 2005 (n = 41) PBDEs associated with the PentaBDE mixture including BDEs 47, 99, and 100 (PentaBDE) were the most common FR detected (39%), followed by tris(1,3-dichloroisopropyl) phosphate (TDCPP; 24%), which is a suspected human carcinogen. In samples purchased in 2005 or later (n = 61) the most common FRs detected were TDCPP (52%) and components associated with the Firemaster550 (FM 550) mixture (18%). Since the 2005 phase-out of PentaBDE, the use of TDCPP increased significantly. In addition, a mixture of nonhalogenated organophosphate FRs that included triphenyl phosphate (TPP), tris(4-butylphenyl) phosphate (TBPP), and a mix of butylphenyl phosphate isomers were observed in 13% of the couch samples purchased in 2005 or later. Overall the prevalence of flame retardants (and PentaBDE) was higher in couches bought in California compared to elsewhere, although the difference was not quite significant (p = 0.054 for PentaBDE). The difference was greater before 2005 than after, suggesting that TB 117 is becoming a de facto standard across the U.S. We determined that the presence of a TB 117 label did predict the presence of a FR; however, lack of a label did not predict the absence of a flame retardant. Following the PentaBDE phase out, we also found an increased number of flame retardants on the market. Given these results, and the potential for human exposure to FRs, health studies should be conducted on the types of FRs identified here.

Recent activities in flame retardancy of wood-plastic composites at the Forest Products Laboratory

Treesearch

Robert H. White; Nicole M. Stark; Nadir Ayrilmis

2011-01-01

For a variety of reasons, wood-plastic composite (WPC) products are widely available for some building applications. In applications such as outdoor decking, WPCs have gained a significant share of the market. As an option to improve the efficient use of wood fiber, the USDA Forest Service, Forest Products Laboratory (FPL), has an extensive research program on WPCs....

Analysis of polybrominated diphenyl ethers and emerging halogenated and organophosphate flame retardants in human hair and nails.

PubMed

Liu, Liang-Ying; Salamova, Amina; He, Ka; Hites, Ronald A

2015-08-07

A method for the digestion, extraction, fractionation, and analysis of three classes of flame retardants, including 36 polybrominated diphenyl ethers (PBDEs), 9 halogenated alternative flame retardants (AFRs), and 12 organophosphate esters (OPEs) in human hair and nail samples was developed. The method employed HNO3/H2O2 digestion, liquid-liquid extraction with (4:1 vol) hexane:dichloromethane, fractionation on a 6g column of 2.5% water deactivated Florisil, and analysis by gas chromatographic mass spectrometry. The accuracy and precision of the method was validated using spiked samples of 6 replicates for both hair and nail samples. The method validation results showed good accuracy and precision for all PBDEs except BDE-209, all AFRs except hexabromobenzene (HBB), and all of the 12 OPEs, with average recovery efficiencies>90% and relative standard deviations (RSDs)<10%. The average recovery efficiencies for HBB were between 60% and 86%, with RSDs<10%. BDE-209 had recovery efficiencies of 64% (RSD, 13%) for hair and 71% (RSD, 10%) for nail. This method was applied to analyze 5 human hair and 5 fingernail samples from the general student population at Indiana University Bloomington campus. BDE-47 and BDE-99 were the predominant PBDEs detected in both hair and nail samples, with a concentration range of 11-620 and 4.6-780ng/g (dry weight) in hair and 7.3-43 and 2.1-11ng/g in nails, respectively. Di-(2-ethylhexyl)-tetrabromophthalate (TBPH) and 2-ethylhexyl-2,3,4,5-tetrabromobenzoate (TBB) were detected in all the samples, with concentrations of 20-240 and 11-350ng/g in hair and <17-80 and <9.2-71ng/g in nails, respectively. Among the 12 OPEs analyzed, tris(2-chloroethyl)phosphate (TCEP), tris(1-chloro-2-propyl)phosphate (TCIPP), tris(1,3-dichloro-2-propyl) phosphate (TDCIPP), and triphenyl phosphate (TPHP) were most often detected. The concentrations of these OPEs (summed together) were 1100-3900 and 380-18,000ng/g in hair and nails, respectively. These levels exceed those of both the PBDEs and the AFRs. Copyright © 2015 Elsevier B.V. All rights reserved.

Indoor pollutants emitted by office equipment: A review ofreported data and information needs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Destaillats, Hugo; Maddalena, Randy L.; Singer, Brett C.

2007-02-01

There is concern that potentially harmful pollutants may be emitted from office equipment. Although office equipment has been a focal point for governmental efforts to promote energy efficiency through programs such as the US EPA's Energy Star, little is known about the relationship between office equipment use and indoor air quality, and information on pollutant emissions is sparse. In this review, we summarize available information on emission rates and/or ambient concentrations of various pollutants that are related to office equipment use. Experimental methods used in the characterization of emissions are briefly described. The office equipment evaluated in this review includesmore » computers (desktops and notebooks), printers (laser, ink-jet and all-in-one machines) and photocopy machines. Reported emission rates of the following pollutant groups are summarized: volatile organic chemicals (VOCs), ozone, particulate matter and several semivolatile organic chemicals (SVOCs). The latter include phthalate esters, brominated flame retardants, organophosphate flame retardants and polycyclic aromatic hydrocarbons (PAHs). We also review studies reporting airborne concentrations in indoor environments where office equipment was present and thought to be a significant contributor to the total pollutant burden (offices, residences, schools, electronics recycling plants). For certain pollutants, such as organophosphate flame retardants, the link between emission by office equipment and indoor air concentrations is relatively well established. However, indoor VOCs, ozone, PAHs and phthalate esters can originate from a variety of sources, and their source apportionment is less straightforward. This literature review identifies substances of toxicological significance, with the purpose of serving as a guide to evaluate their potential importance with respect to human exposures.« less

Priority and emerging flame retardants in rivers: occurrence in water and sediment, Daphnia magna toxicity and risk assessment.

PubMed

Cristale, Joyce; García Vázquez, Alejandro; Barata, Carlos; Lacorte, Silvia

2013-09-01

The occurrence, partitioning and risk of eight polybrominated diphenyl ethers (PBDEs), nine new brominated (NBFRs) and ten organophosphorus flame retardants (OPFRs) were evaluated in three Spanish rivers suffering different anthropogenic pressures (Nalón, Arga and Besòs). OPFRs were ubiquitous contaminants in water (ΣOPFRs ranging from 0.0076 to 7.2μgL(-1)) and sediments (ΣOPFRs ranging 3.8 to 824μgkg(-1)). Brominated flame retardants were not detected in waters, whereas ΣPBDEs ranged from 88 to 812μgkg(-1) and decabromodiphenyl ethane (DBDPE) reached 435μgkg(-1) in sediments from the River Besòs, the most impacted river. The occurrence of flame retardants in river water and sediment was clearly associated with human activities, since the highest levels occurred near urban and industrial zones and after wastewater treatment plants discharge. Daphnia magna toxicity was carried out for OPFRs, the most ubiquitous flame retardants, considering individual compounds and mixtures. Toxicity of nine tested OPFRs differed largely among compounds, with EC50 values ranging over three magnitude orders (0.31-381mgL(-1)). Results evidenced that these compounds act by non-polar narcosis, since their toxicity was proportional to their lipophilicity (Kow). Furthermore, their joint toxicity was additive, which means that single and joint toxicity can be predicted knowing their concentration levels in water using quantitative structure activity relationships (QSARs) and predictive mixture models. Based on these results, a risk assessment considering joint effect was performed calculating and summing risk quotients (RQs) for the water and sediment samples. No significant risk to D. magna (ΣRQs <1) was observed for any of the monitored rivers. © 2013.

One-step fabrication of novel superhydrophobic and superoleophilic sponge with outstanding absorbency and flame-retardancy for the selective removal of oily organic solvent from water

NASA Astrophysics Data System (ADS)

Xiang, Yuqian; Pang, Youyou; Jiang, Xiaomei; Huang, Jie; Xi, Fengna; Liu, Jiyang

2018-01-01

Absorbent materials integrated with superhydrophobicity, superoleophilicity and flame-retardancy are highly desired in the adsorption/removal of flammable oils/organic compounds as well as reducing the risk of fire and explosion. Here, one-step fabrication of novel superhydrophobic and superoleophilic sponge with outstanding absorbency and flame-retardancy was presented. Using raw melamine (ME) sponge as the supporting matrix, the formation of polydopamine (PDA) nanoaggregates via in-situ self-polymerization of high-concentrated dopamine and the covalent grafting of hydrophobic n-dodecylthiol (DT) onto PDA were combined in a feasible alkaline water/ethanol medium. As investigated by scanning electron microscopy (SEM) and X-ray energy-dispersive spectroscopy (EDS), the as-prepared ME/PDA/DT sponge possessed hierarchical structure with submicron PDA nanoaggregates containing DT motif (low surface energy) on 3D interconnected porous network. It exhibited superhydrophobic (water contact angle 157.7°) and superoleophilic (oily/organic solvent contact angle 0° properties. Owing to the highly porous structure, superhydrophobic property, chemical and mechanical stability, the ME/PDA/DT sponge exhibited outstanding absorbency properties of oily organic solvents including fast absorption kinetics, high absorption capacity, and easy reusability. Also, the ME/PDA/DT sponge could be used for one-line continuous organic solvent/water separation. More interestingly, the ME/PDA/DT sponge demonstrated improved flame-retardant property as compared to the intrinsic flame-retardant nature of the raw melamine sponge. Consequently, the risk of fire and explosion was expected to reduce when the fabricated sponge was used as an absorbent for flammable oils and organic compounds. The ease of the one-step superhydrophobic/superoleophilic modification and the promising feature of the obtained materials exhibit great potential for application in oils/organic solvents clean-up.

Emissions of organophosphate and brominated flame retardants from selected consumer products and building materials

NASA Astrophysics Data System (ADS)

Kemmlein, Sabine; Hahn, Oliver; Jann, Oliver

The emissions of selected flame retardants were measured in 1- and 0.02-m 3 emission test chambers and 0.001-m 3 emission test cells. Four product groups were of interest: insulating materials, assembly foam, upholstery/mattresses, and electronics equipment. The experiments were performed under constant environmental conditions (23°C, 50% RH) using a fixed sample surface area and controlled air flow rates. Tris (2-chloro-isopropyl)phosphate (TCPP) was observed to be one of the most commonly emitted organophosphate flame retardants in polyurethane foam applications. Depending on the sample type, area-specific emission rates (SER a) of TCPP varied between 20 ng m -2 h -1 and 140 μg m -2 h -1. The emissions from electronic devices were measured at 60°C to simulate operating conditions. Under these conditions, unit specific emission rates (SER u) of organophosphates were determined to be 10-85 ng unit -1 h -1. Increasing the temperature increased the emission of several flame retardants by up to a factor of 500. The results presented in this paper indicate that emissions of several brominated and organophosphate flame retardants are measurable. Polybrominated diphenylethers exhibited an SER a of between 0.2 and 6.6 ng m -2 h -1 and an SER u of between 0.6 and 14.2 ng unit -1 h -1. Because of sink effects, i.e., sorption to chamber components, the emission test chambers and cells used in this study have limited utility for substances low vapour pressures, especially the highly brominated compounds; hexabromocyclododecane had an SER a of between 0.1 and 29 ng m -2 h -1 and decabromodiphenylether was not detectable at all.

Heat sealable, flame and abrasion resistant coated fabric

NASA Technical Reports Server (NTRS)

Tschirch, R. P.; Sidman, K. R. (Inventor)

1983-01-01

Flame retardant, abrasion resistant elastomeric compositions are disclosed which are comprised of thermoplastic polyurethane polymer and flame retarding amounts of a filler selected from decabromodiphenyloxide and antimony oxide in a 3:1 weight ratio, and decabromodiphenyloxide, antimony oxide, and ammonium polyphosphate in a 3:1:3 weight ratio respectively. Heat sealable coated fabrics employing such elastomeric compositions as coating film are produced by dissolving the elastomeric composition to form a solution, casting the solution onto a release paper and drying it to form an elastomeric film. The film is then bonded to a woven, knitted, or felted fabric.

Isolation and Identification of Persistent Chlorinated Organophosphorus Flame Retardant-Degrading Bacteria ▿

PubMed Central

Takahashi, Shouji; Satake, Ikuko; Konuma, Isao; Kawashima, Koji; Kawasaki, Manami; Mori, Shingo; Morino, Jun; Mori, Junichi; Xu, Hongde; Abe, Katsumasa; Yamada, Ryo-hei; Kera, Yoshio

2010-01-01

Tris(2-chloroethyl) and tris(1,3-dichloro-2-propyl) phosphates are chlorinated persistent flame retardants that have recently emerged as environmental pollutants. Two bacterial strains that can degrade the compounds when they are the sole phosphorus sources have been isolated and identified as members of the sphingomonads. The strains can be useful for the bioremediation of environments contaminated with these compounds. PMID:20525857

Effect of flame retardants on the properties of monolithic and foamed polyurethanes at low temperatures

NASA Astrophysics Data System (ADS)

Yakushin, V. A.; Stirna, U. K.; Zhmud', N. P.

1999-09-01

The dependence of physical and mechanical properties of monolithic and foamed rigid polyurethanes on the content of flame retardants was investigated at 293 and 98 K. The character of the influence of the content of trichloroethyl phosphate on the ultimate tensile elongation and the coefficient of linear thermal expansion for monolithic and foamed polyurethanes at a temperature of 98 K was established.

Effect of DMMP on the pyrolysis products of polyurethane foam materials in the gaseous phase

NASA Astrophysics Data System (ADS)

Liu, W.; Li, F.; Ge, X. G.; Zhang, Z. J.; He, J.; Gao, N.

2016-07-01

Dimethyl methylphosphonate (DMMP) has been used as a flame retardant containing phosphorus to decrease the flammability of the polyurethane foam material (PUF). Flame retardancy and thermal degradation of PUF samples have been investigated by the LOI tests and thermal analysis. The results show that LOI values of all PUF/DMMP samples are higher than that of the neat PUF sample and the LOI value of the samples increases with both DMMP concentration and the %P value. Thermal analysis indicates that flame retardant PUF shows a dominant condensed flame retardant activity during combustion. Thermogravimetric analysis-infrared spectrometry (TG-FTIR) has been used to study the influence of DMMP on the pyrolysis products in the gaseous phase during the thermal degradation of the PUF sample. Fourier transform infrared spectrometry (FTIR) spectra of the PUF sample at the maximum evolution rates and the generated trends of water and the products containing -NCO have been examined to obtain more information about the pyrolysis product evolutions of the samples at high temperature. These results reveal that although DMMP could improve the thermal stability of PUF samples through the formation of the residual char layer between fire and the decomposed materials, the influence of DMMP on the gaseous phase can be also observed during the thermal degradation process of materials.

Degradation of Polymeric Brominated Flame Retardants: Development of an Analytical Approach Using PolyFR and UV Irradiation.

PubMed

Koch, Christoph; Dundua, Alexander; Aragon-Gomez, Jackelyn; Nachev, Milen; Stephan, Susanne; Willach, Sarah; Ulbricht, Mathias; Schmitz, Oliver J; Schmidt, Torsten C; Sures, Bernd

2016-12-06

Many well-established methods for studying the degradation of brominated flame retardants are not useful when working with polymeric and water insoluble species. An example for this specific class of flame retardants is PolyFR (polymeric flame retardant; CAS No 1195978-93-8), which is used as a substituent for hexabromocyclododecane. Although it has been on the market for two years now, almost no information is available about its long time behavior in the environment. Within this study, we focus on how to determine a possible degradation of both pure PolyFR as well as PolyFR in the final insulation product, expanded polystyrene foam. Therefore, we chose UV radiation followed by analyses of the total bromine content at different time points via ICP-MS and identified possible degradation products such as 2,4,6-tribromophenol through LC-MS. These results were then linked with measurements of the adsorbable organically bound bromine and total organic carbon in order to estimate their concentrations. With respect to the obtained 1 H NMR, GPC, and contact angle results, the possibility for further degradation was discussed, as UV irradiation can influence the decomposition of molecules in combination with other environmental factors like biodegradation.

Brominated flame retardants in food and environmental samples from a production area in China: concentrations and human exposure assessment.

PubMed

Li, Peng; Wu, Hui; Li, Qiuxu; Jin, Jun; Wang, Ying

2015-11-01

Human exposure to brominated flame retardants (BFRs: decabromodiphenyl ether (BDE209), decabromodiphenyl ethane (DBDPE), hexabromobenzene (HBB), pentabromoethylbenzene (PBEB), pentabromotoluene (PBT), 1,2,3,4,5-pentabromobenzene (PBBz), and 2,3,5,6-tetrabromo-p-xylene (TBX)) in a brominated flame retardant production area (Weifang, Shandong Province, China) was estimated. Thirty food samples, 14 air samples, and 13 indoor dust samples were analyzed. BDE209 and DBDPE were the dominant BFRs in all samples. Higher alternative brominated flame retardant (including DBDPE, HBB, PBEB, PBT, PBBz, and TBX) concentrations were found in vegetables than in fish and meat; thus, plant-original foods might be important alternative BFR sources in the study area. The BDE209 and alternative BFR concentrations in air were 1.5×10(4) to 2.2×10(5) and 620 to 3.6×10(4) pg/m3, respectively. Mean total BFR exposures through the diet, inhalation, and indoor dust ingestion were 570, 3000, and 69 ng/d, respectively (16, 82, and 2% of total intake, respectively). Inhalation was the dominant BFR source except for DBDPE, for which diet dominated. BDE209 contributed 85% of the total BFR intake in the study area.

Current-use flame retardants in the water of Lake Michigan tributaries

USGS Publications Warehouse

Guo, Jiehong; Romanak, Kevin; Westenbroek, Stephen M.; Hites, Ronald A.; Venier, Marta

2017-01-01

In this study, we measured the concentrations of 65 flame retardants in water samples from five Lake Michigan tributaries. These flame retardants included organophosphate esters (OPEs), brominated flame retardants (BFRs), and Dechlorane-related compounds. A total of 59 samples, including both the particulate and the dissolved phases, were collected from the Grand, Kalamazoo, Saint Joseph, and Lower Fox rivers and from the Indiana Harbor and Ship Canal (IHSC) in 2015. OPEs were the most abundant among the targeted compounds with geometric mean concentrations ranging from 20 to 54 ng/L; OPE concentrations were comparable among the five tributaries. BFR concentrations were about 1 ng/L, and the most-abundant compounds were bis(2-ethylhexyl) tetrabromophthalate, 2-ethylhexyl 2,3,4,5-tetrabromobenzoate, and decabromodiphenyl ether. The highest BFR concentrations were measured in either the IHSC or the Saint Joseph River. The dechlorane-related compounds were detected at low concentrations (<1 pg/L). The fraction of target compounds in the particulate phase relative to the dissolved phase varied by chemical and tended to increase with their octanol–water partition coefficient. The chemical loading from all the five tributaries into Lake Michigan were <10 kg/year for the BFRs and about 500 kg/year for the OPEs.

Flame-retardant polyvinyl alcohol membrane with high transparency based on a reactive phosphorus-containing compound.

PubMed

Peng, Sha; Zhou, Ming; Liu, Feiyan; Zhang, Chang; Liu, Xueqing; Liu, Jiyan; Zou, Liyong; Chen, Jia

2017-08-01

Flame-retardant polyvinyl alcohol (PVA) membranes with high transparency and flexibility were prepared by mixing an aqueous solution of a phosphorus-containing acrylic acid (AOPA) with PVA. The reaction between AOPA and PVA, the transparency, the crystallinity and the flexibility of the membrane were investigated with Fourier transform infrared spectrometry (FTIR), UV-vis light transmittance, X-ray diffraction and tensile tests, respectively. The limited oxygen index (LOI) and vertical flame (UL 94 VTM), microscale combustion calorimetry, thermogravimetric analysis (TGA) and TGA-FTIR were employed to evaluate the flame retardancy as well as to reveal the corresponding mechanisms. Results showed that PVA containing 30 wt% of AOPA can reach the UL 94 VTM V0 rating with an LOI of 27.3% and retain 95% of the original transparency of pure PVA. Adding AOPA reduces crystallinity of PVA, while the flexibility is increased. AOPA depresses the thermal degradation of PVA and promotes char formation during combustion. The proposed decomposition mechanism indicates that AOPA acts mainly in the condensed phase.

Influences of metal ions crosslinked alginate based coatings on thermal stability and fire resistance of cotton fabrics.

PubMed

Pan, Ying; Wang, Wei; Liu, Longxiang; Ge, Hua; Song, Lei; Hu, Yuan

2017-08-15

Bio-based and phosphorus-free coating was fabricated by layer-by-layer assembly method to obtain the flame retardant cotton fabric. For the first time, the modified cotton fabrics were prepared by utilizing positively charged polyethylenimine and negatively charged alginate together with subsequent crosslinking of barium, nickel and cobalt ions. Scanning electron microscopy and energy-dispersive X-ray demonstrated that the metal ions crosslinked coating was successfully constructed on the substrate. The thermal stability and flame retardancy were investigated by thermogravimetric analysis (TGA) and horizontal flame tests. TGA results showed that the degradation of the coated cotton fabrics were retarded at high temperature and the char residue of the cotton fabrics were improved after covered with the barium, nickel and cobalt ions crosslinked coatings. Furthermore, the fire resistance of cotton-Ba sample was enhanced significantly compared with the untreated sample, as evidenced by the obvious reduction (28%) of flame spread rate and complete char residue. Finally, the washing durability of coating on the fabric was enhanced after metal ions crosslinked with alginate based coating. Copyright © 2017. Published by Elsevier Ltd.

Development of thermoregulating microcapsules with cyclotriphosphazene as a flame retardant agent

NASA Astrophysics Data System (ADS)

Szczotok, A. M.; Carmona, M.; Serrano, A.; Kjøniksen, A. L.; Rodriguez, J. F.

2017-10-01

Thermoregulating microcapsules containing phase change material (Rubitherm®RT27) was produced by using the suspension-like polymerization technique with styrene (St), divinylbenzene (DVB) and hexa(methacryloylethylenedioxy) cyclotriphosphazene (PNC-HEMA) as co-monomers. The effect of PNC-HEMA for improving the flame retardant properties of the microcapsules were analyzed by scanning electron microscopy (SEM), differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). It was found that the thermal energy storage (TES) capacity of the microcapsules increased in the presence of PNC-HEMA. However, the morphology of the microcapsules became irregular when the content of monomer with flame retardant properties was increased. Thermogravimetric analysis performed under atmospheric air confirmed that the PNC-HEMA raised the amount of residue after the burning process, proving the formation of thermally stable char. Thus, these materials could be considered as an important alternative to commonly used microcapsules containing phase change materials (PCMs), where a lower flammability is required for their application.

The stability of new transparent polymeric materials: The epoxy trimethoxyboroxine system. Part 1: The preparation, characterization and curing of epoxy resins and their copolymers

NASA Technical Reports Server (NTRS)

Pearce, E.; Lin, S. C.

1981-01-01

The effects of resin composition, curing conditions fillers, and flame retardant additives on the flammability of diglycidyl ether of bisphenol-A (DGEBA) as measured by the oxygen index is examined. The oxygen index of DGEBA cured with various curing agents was between 0.198 to 0.238. Fillers and flame retardant additives can increase the oxygen index dependent on the material and the amount used. Changes in the basic cured resin properties can be anticipated with the addition of noncompatible additives. High flame resistant epoxy resins with good stability and mechanical properties are investigated.

The chemistry of dimethacrylate-styrene networks, and, Development of flame retardant, halogen-free fiber reinforced vinyl ester composites

NASA Astrophysics Data System (ADS)

Rosario, Astrid Christa

One of the major classes of polymer matrix resins under consideration for structural composite applications in the infrastructure and construction industries is vinyl ester resin. Vinyl ester resin is comprised of low molecular weight poly(hydroxyether) oligomers with methacrylate endgroups diluted with styrene monomer. The methacrylate endgroups cure with styrene via free radical copolymerization to yield thermoset networks. The copolymerization behavior of these networks was monitored by Fourier Transform Infrared Spectroscopy (FTIR) at various cure conditions. Reactions of the carbon-carbon double bonds of the methacrylate (943 cm-1) and styrene (910 cm-1 ) were followed independently. Oligomers possessing number average molecular weights of 700 g/mole were studied with systematically increasing levels of styrene. The Mortimer-Tidwell reactivity ratios indicated that at low conversion more styrene was incorporated into the network at lower cure temperatures. The experimental vinyl ester-styrene network compositions deviated significantly from those predicted by the Meyer-Lowry integrated copolymer equation at higher conversion, implying that the reactivity ratios for these networks may change with conversion. The kinetic data were used to provide additional insight into the physical and mechanical properties of these materials. In addition to establishing the copolymerization kinetics of these materials, the development of halogen free fiber reinforced vinyl ester composites exhibiting good flame properties was of interest. Flame retardant vinyl ester resins are used by many industries for applications requiring good thermal resistance. The current flame-retardant technology is dependent on brominated vinyl esters, which generate high levels of smoke and carbon monoxide. A series of halogen free binder systems has been developed and dispersed in the vinyl ester to improve flame retardance. The binder approach enables the vinyl ester resin to maintain its low temperature viscosity so that fabrication of composites via Vacuum Assisted Resin Transfer Molding (VARTM) is possible. The first binder system investigated was a polycaprolactone layered silicate nanocomposite, which was prepared via intercalative polymerization. Transmission Electron Microscopy (TEM) and X-ray Diffraction (XRD) data indicated a mixed morphology of exfoliated and intercalated structures. The mechanical properties and the normalized peak heat release rates were comparable to the neat vinyl ester resin. Alternative binder systems possessing inherent flame retardance were also investigated. A series of binders comprised of novolac, bisphenol A diphosphate, and montmorillonite clay were developed and dispersed into the vinyl ester matrix. Cone calorimetry showed reductions in the peak heat release rate comparable to the brominated resin. Keywords: dimethacrylate; vinyl ester; network; reactivity ratios; nanocomposites; layered silicates; exfoliated; thermoset matrix resin; flame retardant

Curing and toughening of epoxy resins with phosphorus containing monomers and polymers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, Y.R.; Park, I.Y.; Yoon, T.H.

1996-12-31

Epoxy resins have been utilized in many areas, from house holds to airplanes, for the past several decades due to some exceptional properties such as low cost, good mechanical properties and excellent adhesive properties. However, low fracture toughness and flame resistance of epoxy resins have limited their applicability. Therefore, enhancing those properties have been of great interest to many researchers and scientists. As introduced by McGrath and co-workers in 1980s, the reactive thermoplastic polymers have proven to be an excellent toughener for improving not only fracture toughness but also adhesive properties without sacrificing thermo-mechanical properties and chemical resistance. Flame retardencymore » could be improved by adding flame retardent additives which are divided into two groups; additives and reactives. However, among the additives, halogen compounds are known to be toxic gas generator and ozone depleter. Moreover, additives could be potentially leached out of the material, while reactives are inferior to additives. Recently, a reactive type phosphine oxide containing flame retardants have been introduced by McGrath and co-workers and proven to be an excellent flame retardant. In this paper, phospine oxide containing monomers were prepared and utilized as curing agents for expoxy resins, and starting materials for the polymers.« less

Novel and High Volume Use Flame Retardants in US Couches Reflective of the 2005 PentaBDE Phase Out

PubMed Central

2012-01-01

California’s furniture flammability standard Technical Bulletin 117 (TB 117) is believed to be a major driver of chemical flame retardant (FR) use in residential furniture in the United States. With the phase-out of the polybrominated diphenyl ether (PBDE) FR mixture PentaBDE in 2005, alternative FRs are increasingly being used to meet TB 117; however, it was unclear which chemicals were being used and how frequently. To address this data gap, we collected and analyzed 102 samples of polyurethane foam from residential couches purchased in the United States from 1985 to 2010. Overall, we detected chemical flame retardants in 85% of the couches. In samples purchased prior to 2005 (n = 41) PBDEs associated with the PentaBDE mixture including BDEs 47, 99, and 100 (PentaBDE) were the most common FR detected (39%), followed by tris(1,3-dichloroisopropyl) phosphate (TDCPP; 24%), which is a suspected human carcinogen. In samples purchased in 2005 or later (n = 61) the most common FRs detected were TDCPP (52%) and components associated with the Firemaster550 (FM 550) mixture (18%). Since the 2005 phase-out of PentaBDE, the use of TDCPP increased significantly. In addition, a mixture of nonhalogenated organophosphate FRs that included triphenyl phosphate (TPP), tris(4-butylphenyl) phosphate (TBPP), and a mix of butylphenyl phosphate isomers were observed in 13% of the couch samples purchased in 2005 or later. Overall the prevalence of flame retardants (and PentaBDE) was higher in couches bought in California compared to elsewhere, although the difference was not quite significant (p = 0.054 for PentaBDE). The difference was greater before 2005 than after, suggesting that TB 117 is becoming a de facto standard across the U.S. We determined that the presence of a TB 117 label did predict the presence of a FR; however, lack of a label did not predict the absence of a flame retardant. Following the PentaBDE phase out, we also found an increased number of flame retardants on the market. Given these results, and the potential for human exposure to FRs, health studies should be conducted on the types of FRs identified here. PMID:23186002

A new brominated polymeric additive for flame retardant glass-filled polybutylene terephthalate

NASA Technical Reports Server (NTRS)

Nir, Z.; Kourtides, D. A.; Parker, J. A.; Bar-Yaacov, Y.; Minke, R.; Touval, I.

1982-01-01

Attention is called to the undesirable effects (poor ultraviolet light stability and blooming) sometimes introduced by brominated flame retarders. A brominated polymeric additive (BPA) with little or none of these undesirable side effects is compared with decabromobiphenyl oxide (DBBPO). The additive bears the product name F-2300. It is found to be more easily dispersed than DBBPO. The F-2300 is as effective as the DBBPO in the oxygen index test. The improved efficiency of the F-2300 may be explained by its better dispersion in polybutylene terephthalate (PBT). Glass-filled PBT containing F-2300 is found to be more resistant to UV degradation than DBBPO-containing formulas. Formulations with F-2300 therefore have a longer useful outdoor life. F-2300 is a diglycidyl-type polymer containing 50 percent aromatically bound bromine. Its melting point is 112 C, and it is stable up to 372 C. It is pointed out that since its melts at a relatively low temperature, it can be introduced into the formulation as a large agglomerate and still be dispersed evenly throughout the polymer.

Treasure of the Past VIII: Molecular Basis of Flame Inhibition*

PubMed Central

Hastie, J. W.

2001-01-01

The role played by inorganic chemical additives in fire retardancy and flame inhibition is considered. Particular attention is given to the molecular level aspects of commercially important systems containing compounds of antimony, halogens, and phosphorus. The flame inhibiting function of metal containing additives is also discussed. PMID:27500045

Hydroxyapatite Nanowire-Based All-Weather Flexible Electrically Conductive Paper with Superhydrophobic and Flame-Retardant Properties.

PubMed

Chen, Fei-Fei; Zhu, Ying-Jie; Xiong, Zhi-Chao; Dong, Li-Ying; Chen, Feng; Lu, Bing-Qiang; Yang, Ri-Long

2017-11-15

How to survive under various harsh working conditions is a key challenge for flexible electronic devices because their performances are always susceptible to environments. Herein, we demonstrate the novel design and fabrication of a new kind of the all-weather flexible electrically conductive paper based on ultralong hydroxyapatite nanowires (HNs) with unique combination of the superhydrophobic surface, electrothermal effect, and flame retardancy. The superhydrophobic surface with water repellency stabilizes the electrically conductive performance of the paper in water. For example, the electrical current through the superhydrophobic paper onto which water droplets are deposited shows a little change (0.38%), and the electrical performance is steady as well even when the paper is immersed in water for 120 s (just 3.65% change). In addition, the intrinsic electrothermal effect of the electrically conductive paper can efficiently heat the paper to reach a high temperature, for example, 224.25 °C, within 10 s. The synergistic effect between the electrothermal effect and superhydrophobic surface accelerates the melting and removal of ice on the heated electrically conductive paper. Deicing efficiency of the heated superhydrophobic electrically conductive paper is ∼4.5 times that of the unheated superhydrophobic electrically conductive paper and ∼10.4 times that of the heated superhydrophilic paper. More importantly, benefiting from fire-resistant ultralong HNs, thermally stable Ketjen black, and Si-O backbone of poly(dimethylsiloxane), we demonstrate the stable and continuous service of the as-prepared electrically conductive paper in the flame for as long as 7 min. The electrical performance of the electrically conductive paper after flame treatment can maintain as high as 90.60% of the original value. The rational design of the electrically conductive paper with suitable building materials and structure demonstrated here will give an inspiration for the development of new kinds of all-weather flexible electronic devices that can work under harsh conditions.

A rapid throughput approach identifies cognitive deficits in adult zebrafish from developmental exposure to polybrominated flame retardants.

PubMed

Truong, Lisa; Mandrell, David; Mandrell, Rick; Simonich, Michael; Tanguay, Robert L

2014-07-01

A substantial body of evidence has correlated the human body burdens of some polybrominated diphenyl ether (PBDE) flame retardants with cognitive and other behavioral deficits. Adult zebrafish exhibit testable learning and memory, making them an increasingly attractive model for neurotoxicology. Our goal was to develop a rapid throughput means of identifying the cognitive impact of developmental exposure to flame retardants in the zebrafish model. We exposed embryos from 6h post fertilization to 5 days post fertilization to either PBDE 47 (0.1μM), PBDE 99 (0.1μM) or PBDE 153 (0.1μM), vehicle (0.1% DMSO), or embryo medium (EM). The larvae were grown to adulthood and evaluated for the rate at which they learned an active-avoidance response in an automated shuttle box array. Zebrafish developmentally exposed to PBDE 47 learned the active avoidance paradigm significantly faster than the 0.1% DMSO control fish (P<0.0001), but exhibited significantly poorer performance when retested suggestive of impaired memory retention or altered neuromotor activity. Learning in the PBDE 153 group was not significantly different from the DMSO group. Developmental exposure to 0.1% DMSO impaired adult active avoidance learning relative to the sham group (n=39; P<0.0001). PBDE 99 prevented the DMSO effect, yielding a learning rate not significantly different from the sham group (n=36; P>0.9). Our results underscore the importance of vehicle choice in accurately assessing chemical effects on behavior. Active avoidance response in zebrafish is an effective model of learning that, combined with automated shuttle box testing, will provide a highly efficient platform for evaluating persistent neurotoxic hazard from many chemicals. Copyright © 2014 Elsevier Inc. All rights reserved.

Effects of Hoods and Flame-Retardant Fabrics on WBGT Clothing Adjustment Factors.

PubMed

Ashley, Candi D; Bernard, Thomas E

2008-01-01

Personal protective clothing (PPC) may include hoods and flame-retardant (FR) fabrics that may affect heat transfer and, thus, the critical wet bulb globe temperature (WBGT crit) to maintain thermal equilibrium. The purpose of this study was to compare the differences in WBGT crit for hooded vs. nonhooded versions of particle barrier and vapor barrier coveralls as well as for coveralls made of two flame-retardant fabrics (INDURA cotton and Nomex). Acclimated men (n = 11) and women (n = 4) walked on a treadmill in a climatic chamber at 180 W/m2 wearing four different ensembles: limited-use, particle barrier coveralls with and without a hood (Tyvek 1427), and limited-use vapor barrier coveralls with and without a hood (Tychem QC, polyethylene-coated Tyvek). Twelve of the participants wore one of two flame-retardant coveralls. All participants wore standard cotton clothing. Progressive exposure testing at 50% relative humidity (rh) was designed so that each subject established a physiological steady-state followed by a clear loss of thermal equilibrium. WBGT crit was the WBGT 5 min prior to a loss of thermal equilibrium. Hooded ensembles had a lower WBGT crit than the nonhooded ensembles. The difference suggested a clothing adjustment of 1 degrees C for hoods. There were no significant differences among the FR ensembles and cotton work cloths, and the proposed clothing adjustment for FR coveralls clothing is 0 degrees C.

Determination of organophosphorus flame retardants in fish by pressurized liquid extraction using aqueous solutions and solid-phase microextraction coupled with gas chromatography-flame photometric detector.

PubMed

Gao, Zhanqi; Deng, Yuehua; Yuan, Wenting; He, Huan; Yang, Shaogui; Sun, Cheng

2014-10-31

A novel method was developed for the determination of organophosphorus flame retardants (PFRs) in fish. The method consists of a combination of pressurized liquid extraction (PLE) using aqueous solutions and solid-phase microextraction (SPME), followed by gas chromatography-flame photometric detector (GC-FPD). The experimental parameters that influenced extraction efficiency were systematically evaluated. The optimal responses were observed by extracting 1g of fish meat with the solution of water:acetonitrile (90:10, v/v) at 150°C for 5min and acid-washed silica gel used as lipid sorbent. The obtained extract was then analyzed by SPME coupled with GC-FPD without any additional clean-up steps. Under the optimal conditions, the proposed procedure showed a wide linear range (0.90-5000ngg(-1)) obtained by analyzing the spiked fish samples with increasing concentrations of PFRs and correlation coefficient (R) ranged from 0.9900 to 0.9992. The detection limits (S/N=3) were in the range of 0.010-0.208ngg(-1) with standard deviations (RSDs) ranging from 2.0% to 9.0%. The intra-day and inter-day variations were less than 9.0% and 7.8%, respectively. The proposed method was successfully applied to the determination of PFRs in real fish samples with recoveries varying from 79.8% to 107.3%. The results demonstrate that the proposed method is highly effective for analyzing PFRs in fish samples. Copyright © 2014 Elsevier B.V. All rights reserved.

Occurrence, removal and release characteristics of dissolved brominated flame retardants and their potential metabolites in various kinds of wastewater.

PubMed

Kim, Un-Jung; Lee, In-Seok; Oh, Jeong-Eun

2016-11-01

The dissolved phase compound and congener specific distribution characteristics of three widely used brominated flame retardants (BFRs) comprising 27 polybrominated diphenyl ethers (PBDEs), 12 hydroxylated and methoxylated metabolites (OH- and MeO-BDEs), 3 hexabromocyclododecanes (HBCDs) and tetrabromobisphenol A (TBBPA) were investigated in influents and effluents of various kinds of wastewater treatment plants (WWTPs), with varying source of wastewater and type of treatment, and nearby rivers in Korea. The concentration of total BFRs were the highest in industrial WWTPs nearby large industrial complexes specialized in heavy chemicals. The distribution of BFRs was differed according to composition of wastewater, with predominance of TBBPA in WWTPs with higher portion of inflowing industrial wastewater. Among HBCD diastereomers, γ-HBCD was dominant in industrial wastewater as consistent to the previous reports, however, similar contribution of α- and γ-HBCD was found in sewage and human wastewater. Through treatment process, PBDEs were the most effectively removed with a mean removal efficiency of 68.3%. HBCDs and TBBPA had removal efficiencies of 41.3% and 48.7%, respectively. The lowest removal efficiency (10.3%) was observed for PBDE metabolites and their concentration in effluent of human wastewater was even increased at maximum 1.9 fold compared with influent, implying the possibility of transformation during treatment. The estimated dissolved phase daily load of PBDEs was highest in sewage while that of TBBPA was highest in industrial wastewater. Copyright © 2016. Published by Elsevier Ltd.

Flame retardants and organochlorines in indoor dust from several e-waste recycling sites in South China: composition variations and implications for human exposure.

PubMed

Zheng, Xiaobo; Xu, Fuchao; Chen, Kehui; Zeng, Yanhong; Luo, Xiaojun; Chen, Shejun; Mai, Bixian; Covaci, Adrian

2015-05-01

Several classes of flame retardants, such as polybrominated diphenyl ethers (PBDEs), novel brominated flame retardants (NBFRs), dechlorane plus (DPs), and organophosphate flame retardants (PFRs), together with polychlorinated biphenyls (PCBs) were measured in indoor dust from five villages located in three e-waste recycling regions in Guangdong Province, South China. The medians of PBDEs, NBFRs, and PFRs in dust in five sites ranged from 685-67,500, 1460-50,010, and 2180-29,000ng/g, respectively. These concentrations were much higher than the medians of PCBs (52-2900ng/g). BDE 209 and decabromodiphenyl ethane (DBDPE) were the two major halogen flame retardants in dust, while tris-(1-chloro-2-propyl) phosphate (TCIPP) and triphenyl phosphate (TPHP) were the major PFRs. Principle component analysis revealed the different pollutant patterns among different sites. The estimated median human exposures of PBDEs, NBFRs, PFRs, and PCBs via dust ingestion were 1.1-24.1, 0.73-20.3, 1.36-23.5, and 0.04-0.93ng/kgbw/day for adults, and 16.2-352, 10.7-296, 19.9-343, 0.05-0.61, 0.65-13.6ng/kgbw/day for toddlers, respectively. Residents from Site 5 had the highest exposure (95 percentile levels and high dust ingestion for toddlers) of PBDEs (3920ng/kgbw/day), NBFRs (3200ng/kgbw/day), and PFRs (5280ng/kgbw/day). More attention should be paid to the contamination with NBFRs and PFRs, instead of PCBs, in these e-waste recycling regions, and local public health threat from PBDE alternatives should remain of concern. To the best of our knowledge, this is the first study on human exposure assessment of PFRs at e-waste sites. Copyright © 2015 Elsevier Ltd. All rights reserved.

The effect of electron-beam irradiation and halogen-free flame retardants on properties of poly butylene terephthalate

NASA Astrophysics Data System (ADS)

Hooshangi, Zhila; Feghhi, Seyed Amir Hossein; Sheikh, Nasrin

2015-03-01

Engineering plastics like Poly (butylene terephthalate) due to their desirable properties have various industrial applications. Neat PBT is highly combustible, so it is necessary to improve significantly its fire retardancy to meet the fire safety requirements. The combustion performance of PBT can be improved by addition of appropriate flame retardant additives. In this study we have investigated the effect of halogen free flame retardants, i.e. melamine and aluminum phosphate, and instantaneously electron beam radiation-induced crosslinking in the presence of Triallyl cyanurate on various properties of PBT. The results of gel content showed that a dose range of 200-400 kGy leads to high cross linked structure in this polymer. Also mechanical experiments showed that its structure became rigid and fragile due to irradiation. Radiation crosslinking of this polymer made its dielectric loss coefficient ten times lower than non-irradiated polymer, but had no effect on its dielectric constant. Moreover the addition of the fire retardant additives as impurity decreased the dielectric loss coefficient. TGA analysis in nitrogen exhibited that irradiation increases char formation and use of the fire retardant additives leads to reduction of onset temperature and formation of higher char quantity than pure PBT. According to the results of UL-94, irradiated samples burned with lower speed and less dripping in vertical and horizontal positions than pure polymer. Finally irradiation of the polymers containing fire retardant additives with a dose of 400 kGy led to self-extinguishing and non-dripping and reach to V-0 level in the UL-94 V.

Study of coatings for improved fire and decay resistance of mine timbers

NASA Technical Reports Server (NTRS)

Baum, B.

1977-01-01

The purpose of this program was to find a fire- and rot-retardant polymer/fungicide reaction product for coating mine timbers. Fire-retardant polymers were screened as films and coatings on fir wood. Curable polyimide appeared to be flame retardant and evolved a minimum of fumes when exposed to a flame. Several organic and metal, low toxicity, fungicides were reacted with the polyimide in-situ on the wood. These coated samples were screened for fungus resistance. All formulations rated well - even the polyimide film without additives was fungicidal. The fir wood control itself resisted internal damage during the ten weeks of fungus exposure. A more severe test for fungus resistance will be required.

Construction of flame retardant coating on polyamide 6.6 via UV grafting of phosphorylated chitosan and sol-gel process of organo-silane.

PubMed

Kundu, Chanchal Kumar; Wang, Xin; Hou, Yanbei; Hu, Yuan

2018-02-01

Phosphorylated chitosan (PCS) was synthesized and grafted onto the surface of polyamide 6.6 (PA 6.6) fabrics via UV-induced grafting polymerization in order to improve the flame retardant properties. Subsequently, PCS grafted PA 6.6 fabrics were modified by (3-aminopropyl) triethoxysilane (APTES) through sol-gel process in order to form a cross-linking coating. The results obtained from the vertical burning test indicated that only the PCS grafted and simultaneously sol-gel treated fabrics could stop the melt dripping. A maximum reduction (30%) in the peak heat release rate was achieved for the PA6.6-PCS-4W-SG fabric sample. The optimal flame retardant effect was achieved for the PA6.6 fabrics treated by PCS and APTES simultaneously, which was attributed to the joint effect of thermal shielding exerted by the silica and char-forming effect derived from PCS. Copyright © 2017 Elsevier Ltd. All rights reserved.

Brominated flame retardants and dechlorane plus on a remote high mountain of the eastern Tibetan Plateau: implications for regional sources and environmental behaviors.

PubMed

Liu, Xin; Bing, Haijian; Chen, Yanzhi; Li, Jun; Wu, Yanhong; Zhang, Gan

2017-04-10

We investigated the occurrence of halogenated flame retardants (HFRs) including polybrominated diphenyl ethers (PBDEs), six novel brominated flame retardants (NBFRs) and dechlorane plus in air and soils on the eastern slope of Mt. Gongga on the eastern Tibetan Plateau. We detected all of the NBFR except bis(2-ethylhexyl)-tetrabromophthalate and pentabromoethyl benzene. NBFRs constituted the most prevalent group. BDE-28 and BDE-47 dominated among the PBDE congeners. Decabromodiphenyl ethane was detected at relatively high levels up to 171 pg/m 3 and 1450 pg/g dry weight in air and soils, respectively; however, it appeared to be easily degraded in the environment. A general decreasing trend was observed among the HFR concentrations with increasing altitude, and this was due to the prominent contribution of source emissions over possible influence of environmental conditions. This study also suggests that HFRs are supplied to forest soils mainly in the form of precipitation and retained in the O horizon layers.

Deriving freshwater safety thresholds for hexabromocyclododecane and comparison of toxicity of brominated flame retardants.

PubMed

Dong, Liang; Zheng, Lei; Yang, Suwen; Yan, Zhenguang; Jin, Weidong; Yan, Yuhong

2017-05-01

Hexabromocyclododecane (HBCD) is a brominated flame retardant used throughout the world. It has been detected in various environmental media and has been shown toxic to aquatic life. The toxic effects of HBCD to aquatic organisms in Chinese freshwater ecosystems are discussed here. Experiments were conducted with nine types of acute toxicity testing and three types of chronic toxicity testing. After comparing a range of species sensitivity distribution models, the optimal model of Bull III was used to derive the safety thresholds for HBCD. The acute safety threshold and the chronic safety threshold of HBCD for Chinese freshwater organisms were found to be 2.32mg/L and 0.128mg/L, respectively. Both values were verified by the methods of the Netherlands and the United States. HBCD was found to be less toxic compared to other widely used brominated flame retardants. The present results provide valuable information for revision of the water quality standard of HBCD in China. Copyright © 2017 Elsevier Inc. All rights reserved.

Electrochemical performance of tris(2-chloroethyl) phosphate as a flame-retarding additive for lithium-ion batteries

NASA Astrophysics Data System (ADS)

Shim, Eun-Gi; Park, In-Jun; Nam, Tae-Heum; Kim, Jung-Gu; Kim, Hyun-Soo; Moon, Seong-In

2010-08-01

We studied tris(2-chloroethyl) phosphate (TCEP) as a potential flame-retarding additive and its effect on the electrochemical cell performance of lithium-ion battery electrolytes. The electrochemical cell performance of additive-containing electrolytes in combination with a cell comprised of a LiCoO2 cathode and a mesocarbon microbeads anode was tested in coin cells. The cyclic voltammetry results show that the oxidation potential of TCEP-containing electrolyte is about 5.1 V (vs. Li/Li+). A cell with TCEP has a better electrochemical cell performance than a cell without TCEP in an initial charge and discharge test. In a cycling test, a cell containing a TCEP-containing electrolyte has a greater discharge capacity and better capacity retention than a TCEP-free electrolyte after cycling. The results confirm the promising potential of TCEP as a flame-retarding additive and as a means of improving the electrochemical cell performance of lithium-ion batteries.

ACCUMULATION AND DNA DAMAGE IN FATHEAD MINNOWS (PIMEPHALES PROMELAS) EXPOSED TO 2 BROMINATED FLAME-RETARDANT MIXTURES, FIREMASTER® 550 AND FIREMASTER® BZ-54

PubMed Central

BEARR, JONATHAN S.; STAPLETON, HEATHER M.; MITCHELMORE, CARYS L.

2015-01-01

Firemaster® 550 and Firemaster® BZ-54 are two brominated formulations that are in use as replacements for polybrominated diphenyl ether (PBDE) flame retardants. Two major components of these mixtures are 2,3,4,5-tetrabromo-ethylhexylbenzoate (TBB) and 2,3,4,5-tetrabromo-bis(2-ethylhexyl) phthalate (TBPH). Both have been measured in environmental matrices; however, scant toxicological information exists. The present study aimed to determine if these brominated flame-retardant formulations are bioavailable and adversely affect DNA integrity in fish. Fathead minnows (Pimephales promelas) were orally exposed to either FM 550, FM BZ54, or the nonbrominated form of TBPH, di-(2-ethylhexyl) phthalate (DEHP) for 56 d and depurated (e.g., fed clean food) for 22 d. At several time points, liver and blood cells were collected and assessed for DNA damage. Homogenized fish tissues were extracted and analyzed on day 0 and day 56 to determine the residue of TBB and TBPH and the appearance of any metabolites using gas chromatography-electron-capture negative ion mass spectrometry (GC/ECNI-MS). Significant increases ( p<0.05) in DNA strand breaks from liver cells (but not blood cells) were observed during the exposure period compared with controls, although during depuration these levels returned to control. Both parent compounds, TBB and TBPH, were detected in tissues at approximately 1% of daily dosage along with brominated metabolites. The present study provides evidence for accumulation, metabolism, and genotoxicity of these new formulation flame retardants in fish and highlights the potential adverse effects of TBB- and TBPH-formulated fire retardants to aquatic species. PMID:20821500

Thermal runaway inhibitors

DOEpatents

Mandal, Braja K.; Filler, Robert

2004-06-08

The present invention provides for a battery having an anode, a cathode, and a flame-retarding electrolyte with a conductivity greater than about 10.sup.-3 S/cm at ambient temperature and which includes a compound that chemically interferes with flame propagation.

Nontarget approach for environmental monitoring by GC × GC-HRTOFMS in the Tokyo Bay basin.

PubMed

Zushi, Yasuyuki; Hashimoto, Shunji; Tanabe, Kiyoshi

2016-08-01

In this study, we developed an approach for sequential nontarget and target screening for the rapid and efficient analysis of multiple samples as an environmental monitoring using a comprehensive two-dimensional gas chromatograph coupled to a high resolution time-of-flight mass spectrometer (GC × GC-HRTOFMS). A key feature of the approach was the construction of an accurate mass spectral database learned from the sample via nontarget screening. To enhance the detection power in the nontarget screening, a global spectral deconvolution procedure based on non-negative matrix factorization was applied. The approach was applied to the monitoring of rivers in the Tokyo Bay basin. The majority of the compounds detected by the nontarget screening were alkyl chain-based compounds (55%). In the quantitative target screening based on the output from the nontarget screening, particularly high levels of organophosphorus flame retardants (median concentrations of 31, 116 and 141 ng l(-1) for TDCPP, TCIPP and TBEP, respectively) were observed among the target compounds. Flame retardants used for household furniture and building materials were detected in river basins where buildings and arterial traffic were dominated. The developed GC × GC-HRTOFMS approach was efficient and effective for environmental monitoring and provided valuable new information on various aspects of monitoring in the context of environmental management. Copyright © 2016 Elsevier Ltd. All rights reserved.

Flame resistant elastomeric polymer development. [for use in space shuttle instrument packaging

NASA Technical Reports Server (NTRS)

Howarth, J. T.; Sheth, S. G.; Sidman, K. R.

1975-01-01

Elastomeric products were developed for use in the space shuttle program, and investigations were conducted to improve the properties of elastomers developed in previous programs, and to evaluate the possibility of using lower-cost general purpose polymers. Products were fabricated and processed on conventional processing equipment; these products include: foams based on fluorinated rubber flame-retarded compounds with a density of 20-30 pounds/cubic foot for use as padding and in helmets; foams based on urethane for use in instrument packaging in the space shuttle; flexible and semi-rigid films of fluorinated rubber and neoprene compounds that would not burn in a 70% nitrogen, 30% oxygen atmosphere, and in a 30% nitrogen, 70% oxygen atmosphere, respectively for use in packaging or in laminates; coated fabrics which used both nylon and Kelvar fabric substrates, coated with either fluorinated or neoprene polymer compositions to meet specific levels of flame retardancy; and other flame-resistant materials.

Spatial distribution and implications to sources of halogenated flame retardants in riverine sediments of Taizhou, an intense e-waste recycling area in eastern China.

PubMed

Zhou, Shanshan; Fu, Jie; He, Huan; Fu, Jianjie; Tang, Qiaozhi; Dong, Minfeng; Pan, Yongqiang; Li, An; Liu, Weiping; Zhang, Limin

2017-10-01

Concentrations and spatial distribution pattern of organohalogen flame retardants were investigated in the riverine surface sediments from Taizhou, an intensive e-waste recycling region in China. The analytes were syn- and anti- Dechlorane Plus (DP), Dechloranes 602, 603, and 604, a DP monoadduct, two dechlorinated DPs and 8 congeners of polybrominated diphenyl ethers (PBDEs). The concentrations of Σ 8 PBDEs, ΣDP, ΣDec600s, and ΣDP-degradates ranged from <100 to 172,000, 100 to 55,000, not detectable (nd) to 1600, and nd to 2800 pg/g dry weight, respectively. BDE-209 and DP, both have been manufactured in China, had similar spatial distribution patterns in the study area, featured by distinctly recognizable hotspots some of which are in proximity to known e-waste dumping or metal recycling facilities. Such patterns were largely shared by Dec602 and dechlorinated DP, although their concentration levels were much lower. These major flame retardants significantly correlate with each other, and cluster together in the loading plot of principle component analysis. In contrast, most non-deca PBDE congeners do not correlate with DPs. Dec604 stood out having distinctly different spatial distribution pattern, which could be linked to historical use of mirex. Organic matter content of the sediment was not the dominant factor in determining the spatial pattern of pollution by halogenated flame retardants in the rivers of this study. Copyright © 2017 Elsevier Ltd. All rights reserved.

A novel and facile strategy for highly flame retardant polymer foam composite materials: Transforming silicone resin coating into silica self-extinguishing layer.

PubMed

Wu, Qian; Zhang, Qian; Zhao, Li; Li, Shi-Neng; Wu, Lian-Bin; Jiang, Jian-Xiong; Tang, Long-Cheng

2017-08-15

In this study, a novel strategy was developed to fabricate highly flame retardant polymer foam composite materials coated by synthesized silicone resin (SiR) polymer via a facile dip-coating processing. Applying the SiR polymer coating, the mechanical property and thermal stability of SiR-coated polymer foam (PSiR) composites are greatly enhanced without significantly altering their structure and morphology. The minimum oxygen concentration to support the combustion of foam materials is greatly increased, i.e. from LOI 14.6% for pure foam to LOI 26-29% for the PSiR composites studied. Especially, adjusting pendant group to SiOSi group ratio (R/Si ratio) of SiRs produces highly flame retardant PSiR composites with low smoke toxicity. Cone calorimetry results demonstrate that 44-68% reduction in the peak heat release rate for the PSiR composites containing different R/Si ratios over pure foam is achieved by the presence of appropriate SiR coating. Digital and SEM images of post-burn chars indicate that the SiR polymer coating can be transformed into silica self-extinguishing porous layer as effective inorganic barrier effect, thus preserving the polymer foam structure from fire. Our results show that the SiR dip-coating technique is a promising strategy for producing flame retardant polymer foam composite materials with improved mechanical properties. Copyright © 2017 Elsevier B.V. All rights reserved.

New brominated flame retardants and their metabolites as activators of the pregnane X receptor.

PubMed

Gramec Skledar, Darja; Tomašič, Tihomir; Carino, Adriana; Distrutti, Eleonora; Fiorucci, Stefano; Peterlin Mašič, Lucija

2016-09-30

The present study investigated the activities on different nuclear receptors of the new brominated flame retardants 2-ethylhexyl 2,3,4,5-tetrabromobenzoate (TBB) and bis(2-ethylhexyl) 2,3,4,5-tetrabromophthalate (TBPH), and their main carboxylic acid metabolites 2,3,4,5-tetrabromobenzoic acid (TBBA) and mono(2-ethylhexyl) tetrabromophthalate (TBMEPH). None of selected chemicals exhibited marked activity towards PPARα and PPARγ by the use of transactivation assays in HepG2 cells transfected with peroxisome proliferator-activated receptors. In contrast, selected flame retardants all exhibited potent agonist activity on pregnane X receptor (PXR), with EC50 values of 5.5μM for TBPH and 2.0μM for its metabolite TBMEPH. Molecular docking of TBPH and TBMEPH to the PXR ligand binding site revealed similar interactions, with differences only for conformation and orientation of the alkyl chains. Additionally, TBPH showed antagonist activity on PXR (IC50, 13.9μM). Moreover, there was significant up-regulation of CYP3A4 expression via PXR activation for TBB and TBPH and their metabolites. Induction of CYP3A4 might cause undesired drug-drug interactions, lower bioavailability of pharmaceutical drugs, higher formation of reactive toxic metabolites, or enhanced elimination of endogenous hormones, such as T3/T4, to lead to endocrine disruption. These data provide new and important insights into the toxicity of these new polybrominated flame retardants, TBB and TBPH, and their metabolites. Copyright © 2016 Elsevier Ireland Ltd. All rights reserved.

Occurrence and sources of brominated and organophosphorus flame retardants in dust from different indoor environments in Barcelona, Spain.

PubMed

Cristale, Joyce; Hurtado, Alba; Gómez-Canela, Cristian; Lacorte, Silvia

2016-08-01

In this study, the simultaneous presence of eight polybrominated diphenyl ethers (PBDEs), nine new brominated flame retardants (NBFRs) and ten organophosphorus flame retardants (OPFRs) was investigated in dust samples collected from different indoor environments (homes, schools, theatres, a university and a Research Institute) in Barcelona, Spain. OPFRs were detected at the highest concentrations followed by PBDEs. ∑OPFRs ranged from 2053 to 72,090ngg(-1) and tris(2-chloroisopropyl) phosphate (TCIPP) was the most abundant compound. BDE-209 was the main PBDE congener detected (up to 14,990ngg(-1)), while other PBDEs ranged from 2.6 to 118ngg(-1). Among the studied NBFRs, decabromodiphenyl ethane (DBDPE - up to 4432ngg(-1)) followed by bis(2-ethylhexyl) tetrabromophthalate (BEH-TEBP - up to 508ngg(-1)) were detected at the highest concentration, whereas a lower detection frequency was observed for 2-ethylhexyl 2,3,4,5-tetrabromobenzoate (EH-TBB), 1,2-bis(2,4,6-tribromophenoxy)ethane (BTBPE), pentabromotoluene (PBT) and hexabromobenzene (HBB). The levels and profile of flame retardants (FRs) were characteristic of each environment, where theatres followed by homes presented the highest concentrations and schools had the lowest levels. Principal Component Analysis permitted to identify the main sources and distribution of all FRs, according to specific uses in each environment. The simultaneous presence of all FR families in indoor dust points to the need to monitor these compounds to minimize human exposure. Copyright © 2016 Elsevier Inc. All rights reserved.

Toxicity of new generation flame retardants to Daphnia magna.

PubMed

Waaijers, Susanne L; Hartmann, Julia; Soeter, A Marieke; Helmus, Rick; Kools, Stefan A E; de Voogt, Pim; Admiraal, Wim; Parsons, John R; Kraak, Michiel H S

2013-10-01

There is a tendency to substitute frequently used, but relatively hazardous brominated flame retardants (BFRs) with halogen-free flame retardants (HFFRs). Consequently, information on the persistence, bioaccumulation and toxicity (PBT) of these HFFRs is urgently needed, but large data gaps and inconsistencies exist. Therefore, in the present study the toxicity of a wide range of HFFRs to the water flea Daphnia magna was investigated. Our results revealed that four HFFRs were showing no effect at their Sw (saturated water concentration) and three had a low toxicity (EC50>10 mg L(-1)), suggesting that these compounds are not hazardous. Antimony trioxide had a moderate toxicity (EC50=3.01 mg L(-1), 95% CL: 2.76-3.25) and triphenyl phosphate and the brominated reference compound tetra bromobisphenol A were highly toxic to D. magna (EC50=0.55 mg L(-1), 95% CL: 0.53-0.55 and EC50=0.60 mg L(-1), 95% CL: 0.24-0.97 respectively). Aluminum trihydroxide and bisphenol A bis(diphenyl phosphate) caused limited mortality at Sw (26 and 25% respectively) and have a low solubility (<10 mg L(-1)). Hence, increased toxicity of these compounds may be observed when for instance decreasing pH could increase solubility. By testing all compounds under identical conditions we provided missing insights in the environmental hazards of new generation flame retardants and propose as best candidates for BFR replacements: APP, ALPI, DOPO, MHO, MPP, ZHS and ZS. © 2013 Elsevier B.V. All rights reserved.

Tribromophenoxy flame retardants in the Great Lakes atmosphere.

PubMed

Ma, Yuning; Venier, Marta; Hites, Ronald A

2012-12-18

The 2,4,6-tribromophenoxy moiety is a common structural feature of several brominated flame retardants, and we have previously reported on the environmental concentrations of one such compound, 1,2-bis(2,4,6-tribromophenoxy) ethane (TBE). Here we report the atmospheric concentrations of TBE and three other tribromophenoxy compounds: allyl 2,4,6-tribromophenyl ether (ATE), 2-bromoallyl 2,4,6-tribromophenyl ether (BATE), and 2,3-dibromopropyl 2,4,6-tribromophenyl ether (DPTE). The samples were collected at five sites near the shores of the Great Lakes during the period 2008-2009, inclusive. Of these four compounds, TBE and ATE are currently used as flame retardants, and DPTE was formerly used as a flame retardant until its production ceased in the mid-1980s. The total concentrations of ATE, BATE, and DPTE were ∼2 pg/m³ in the cities of Chicago and Cleveland and 0.1-0.4 pg/m³ at the rural and remote sites. The concentrations of TBE were ∼1 pg/m³ in these cities and 0.2-0.8 pg/m³ at the rural and remote sites. In both cases, this was a very significant urban effect. The concentrations of ATE, BATE, and DPTE did not change significantly over the two-year study, but the concentrations of TBE decreased by about a factor of 2 during this time. This temporal change was statistically significant but not strong compared to the urban effect.

Preparation and characterization of flame retardant n-hexadecane/silicon dioxide composites as thermal energy storage materials.

PubMed

Fang, Guiyin; Li, Hui; Chen, Zhi; Liu, Xu

2010-09-15

Flame retardant n-hexadecane/silicon dioxide (SiO(2)) composites as thermal energy storage materials were prepared using sol-gel methods. In the composites, n-hexadecane was used as the phase change material for thermal energy storage, and SiO(2) acted as the supporting material that is fire resistant. In order to further improve flame retardant property of the composites, the expanded graphite (EG) was added in the composites. Fourier transformation infrared spectroscope (FT-IR), X-ray diffractometer (XRD) and scanning electronic microscope (SEM) were used to determine chemical structure, crystalloid phase and microstructure of flame retardant n-hexadecane/SiO(2) composites, respectively. The thermal properties and thermal stability were investigated by a differential scanning calorimeter (DSC) and a thermogravimetric analysis apparatus (TGA), respectively. The SEM results showed that the n-hexadecane was well dispersed in the porous network of the SiO(2). The DSC results indicated that the melting and solidifying latent heats of the composites are 147.58 and 145.10 kJ/kg when the mass percentage of the n-hexadecane in the composites is 73.3%. The TGA results showed that the loading of the EG increased the charred residue amount of the composites at 700 degrees C, contributing to the improved thermal stability of the composites. It was observed from SEM photographs that the homogeneous and compact charred residue structure after combustion improved the flammability of the composites. Copyright 2010 Elsevier B.V. All rights reserved.

Plasma impregnation of wood with fire retardants

NASA Astrophysics Data System (ADS)

Pabeliña, Karel G.; Lumban, Carmencita O.; Ramos, Henry J.

2012-02-01

The efficacy of chemical and plasma treatments with phosphate and boric compounds, and nitrogen as flame retardants on wood are compared in this study. The chemical treatment involved the conventional method of spraying the solution over the wood surface at atmospheric condition and chemical vapor deposition in a vacuum chamber. The plasma treatment utilized a dielectric barrier discharge ionizing and decomposing the flame retardants into innocuous simple compounds. Wood samples are immersed in either phosphoric acid, boric acid, hydrogen or nitrogen plasmas or a plasma admixture of two or three compounds at various concentrations and impregnated by the ionized chemical reactants. Chemical changes on the wood samples were analyzed by Fourier transform infrared spectroscopy (FTIR) while the thermal changes through thermo gravimetric analysis (TGA). Plasma-treated samples exhibit superior thermal stability and fire retardant properties in terms of highest onset temperature, temperature of maximum pyrolysis, highest residual char percentage and comparably low total percentage weight loss.

Fireproofing and heat insulating performance improvement of EG/ATH modified intumescent flame retardant coating treated under Co-60 radiation

NASA Astrophysics Data System (ADS)

Zhang, Yuehong; Luan, Weiling; Jiang, Tao

2017-12-01

New intumescent flame retardant (IFR) coatings with different fire retardants were prepared in this paper. Expandable graphite (EG) and Aluminium hydroxide (ATH) were respectively added into the conventional IFR coating system, which included ammonium polyphosphate (APP) / pentaerythritol (PER) / melamine (MEL). The fireproofing time and heat insulating properties of the additives acted as fire retardants were investigated via thermogravimetry analysis (TGA) and fire resistance test of homemade big panel test. The morphology of the char layer structure was achieved by scanning electron microscopy (SEM). The highlight of the paper was that the coating samples were pretreated under Co-60 radiation. The influence of radiation on the fire resistance time and char layer height was investigated. The results showed that the prepared IFR coatings can be used in Co-60 radiation for more than 90 min when encountering fire. It would be a reference for radiation shielding in nuclear environment.

Hybrid films of chitosan, cellulose nanofibrils and boric acid: Flame retardancy, optical and thermo-mechanical properties.

PubMed

Uddin, Khan M A; Ago, Mariko; Rojas, Orlando J

2017-12-01

Chitosan (CS), cellulose nanofibrils (CNF) and boric acid, the latter of which was used as flame retardant, were combined in transparent, hybrid films that were produced by solvent casting. The flammability and the thermal stability of the films were studied with respect to the loading of the inorganic component. Chitosan films displayed fire retardancy properties, which were enhanced in the presence of boric acid. CNF films, in contrast to those from chitosan, were readily flammable; however, when combined with boric acid (30w%), they became self-extinguishing. Most remarkably, bicomponent films comprising CNF and chitosan, displayed better fire retardancy than that of neat CS films. Moreover, boric acid improved the thermal stability of the bicomponent films. The tensile strength and Young's modulus of CS, CNF and CS-CNF films improved at intermediate boric acid addition, although a negative effect on elongation was observed. Copyright © 2017 Elsevier Ltd. All rights reserved.

Eco-friendly functionalized superhydrophobic recycled paper with enhanced flame-retardancy.

PubMed

Si, Yifan; Guo, Zhiguang

2016-09-01

Recycled paper with superhydrophobicity and flame-retardancy has been demonstrated here due to the synergistic action of dopamine-silica trimethylsilyl modified gel powder and stearic acid modified Mg(OH)2. This multifunctional recycled paper displays great self-cleaning and anti-fouling ability and can be used for oil-water separation. Surprisingly, the absorbed organic can be reused as fuel via simple combustion method for multiple cycles. This work will not only expand the usable range of paper but also ease the energy and environment crisis. Copyright © 2016 Elsevier Inc. All rights reserved.

Intumescent flame retardant properties of graft copolymerized vinyl monomers onto cotton fabric

NASA Astrophysics Data System (ADS)

Rosace, G.; Colleoni, C.; Trovato, V.; Iacono, G.; Malucelli, G.

2017-10-01

In this paper, an intumescent flame retardant treatment, obtained by a combination of vinylphosphonic acid (VPA) and methacrylamide (MAA), was applied to cotton fabrics. In order to improve the cross-linking degree onto cellulose polymers, potassium persulfate was used as initiator of a radical polymerization technique. The application on cotton was carried out by padding, followed by drying and a curing treatment. The treated samples were characterized by SEM, TGA and FTIR-ATR analyses and tested in terms of flammability and washing fastness. The thermal and fire behavior of the treated fabrics was thoroughly investigated. The results clearly showed that the VPA/MAA coating was able to exert a protective action, giving rise to the formation of a stable char on the surface of textile fibers upon heating, hence improving the flame retardant performance of cotton. Horizontal flame spread tests confirmed that the coated fabrics achieved self-extinction, and the residues well preserved the original weave structure and fiber morphology; at variance, the uncoated fabric left only ashes. A remarkable weight loss was observed only after the first washing cycle, then the samples did not show any significant weight loss, hence confirming the durability of the self-extinguishing treatment, even after five laundering cycles.

Flame retardant behavior of polyelectrolyte-clay thin film assemblies on cotton fabric.

PubMed

Li, Yu-Chin; Schulz, Jessica; Mannen, Sarah; Delhom, Chris; Condon, Brian; Chang, Sechin; Zammarano, Mauro; Grunlan, Jaime C

2010-06-22

Cotton fabric was treated with flame-retardant coatings composed of branched polyethylenimine (BPEI) and sodium montmorillonite (MMT) clay, prepared via layer-by-layer (LbL) assembly. Four coating recipes were created by exposing fabric to aqueous solutions of BPEI (pH 7 or 10) and MMT (0.2 or 1 wt %). BPEI pH 10 produces the thickest films, while 1 wt % MMT gives the highest clay loading. Each coating recipe was evaluated at 5 and 20 bilayers. Thermogravimetric analysis showed that coated fabrics left as much as 13% char after heating to 500 degrees C, nearly 2 orders of magnitude more than uncoated fabric, with less than 4 wt % coming from the coating itself. These coatings also reduced afterglow time in vertical flame tests. Postburn residues of coated fabrics were examined with SEM and revealed that the weave structure and fiber shape in all coated fabrics were preserved. The BPEI pH 7/1 wt % MMT recipe was most effective. Microcombustion calorimeter testing showed that all coated fabrics reduced the total heat release and heat release capacity of the fabric. Fiber count and strength of uncoated and coated fabric are similar. These results demonstrate that LbL assembly is a relatively simple method for imparting flame-retardant behavior to cotton fabric. This work lays the foundation for using these types of thin film assemblies to make a variety of complex substrates (foam, fabrics, etc.) flame resistant.

Exposure to brominated and organophosphate ester flame retardants in U.S. childcare environments: Effect of removal of flame-retarded nap mats on indoor levels.

PubMed

Stubbings, W A; Schreder, E D; Thomas, M B; Romanak, K; Venier, M; Salamova, A

2018-07-01

We assessed exposure to 39 brominated and 16 organophosphate ester flame retardants (FRs) from both dust and indoor air at seven childcare centres in Seattle, USA, and investigated the importance of nap mats as a source of these chemicals. Many childcare centres serving young children use polyurethane foam mats for the children's naptime. Until recently, the vast majority of these mats sold in the United States contained flame-retarded polyurethane foam to meet California Technical Bulletin 117 (TB117) requirements. With the 2013 update of TB117, allowing manufacturers to meet flammability standards without adding FRs to filling materials, FR-free nap mats have become widely available. We conducted an intervention study by actively switching out FR-treated nap mats with FR-free nap mats and measuring FR levels in indoor air and dust before and after the switch-out. The predominant FRs found in dust and indoor air were 2-ethylhexyl tetrabromobenzoate (EHTBB) and tris(1-chloro-2-propyl) phosphate (TCIPP), respectively. Nap mat samples analysed from four of the six centres contained a Firemaster ® mixture, while one mat was predominantly treated with tris(1,3-dichloroisopropyl) phosphate (TDCIPP) and the other contained no detectable target FRs. After replacement, there was a significant decrease (p = 0.03-0.09) in median dust concentrations for bis(2-ethylhexyl) tetrabromophthalate (BEHTBP), EHTBB, tris(4-butylphenyl) phosphate (TBPP), and TDCIPP with reductions of 90%, 79%, 65%, and 42%, respectively. These findings suggest that the nap mats were an important source of these FRs to dust in the investigated childcare environments and that a campaign of swapping out flame-retarded mats for FR-free ones would reduce exposure to these chemicals. While calculated exposure estimates to the investigated FRs via inhalation, dust ingestion, and dermal absorption were below established reference dose values, they are likely underestimated when considering the toddlers' direct contact to the mats and personal cloud effects. Copyright © 2018 Elsevier Ltd. All rights reserved.

Temporal trends of hexabromocyclododecanes (HBCDs) and polybrominated diphenyl ethers (PBDEs) and detection of two novel flame retardants in marine mammals from Hong Kong, South China.

PubMed

Lam, James C W; Lau, Ridge K F; Murphy, Margaret B; Lam, Paul K S

2009-09-15

Concentrations of hexabromocyclododecanes (HBCDs), polybrominated diphenyl ethers (PBDEs), and three novel flame retardants, namely2-ethylhexyl 2,3,4,5-tetrabromobenzoate (TBB), bis-(2-ethylhexyl)-tetrabromophthalate (TBPH), and hexachlorocyclopentadienyldibromocyclooctane (HCDBCO), were determined in blubber samples of Indo-Pacific humpback dolphins (Sousa chinensis) and finless porpoises (Neophocaena phocaenoides). The levels of HBCDs and PBDEs in cetacean samples ranged from 4.1 to 519 and 103 to 51,100 ng/g lw, respectively. A significant increasing trend of SigmaHBCDs was observed in dolphin samples from 1997 to 2007 with an estimated annual rate of 5%, whereas no significant temporal trends of SigmaPBDEs appeared over the sampling period. This pattern may be attributed to the increasing usage of HBCDs following the restriction/voluntary withdrawal of the production and use of PBDE commercial mixtures in several countries. HCDBCO was not found in the blubber samples. This is the first report of the presence of TBB and TBPH, two new flame retardants that have previously been identified in house dust from the U.S., in marine mammals; concentrations of these compounds in dolphins and porpoises ranged from the instrumental detection limit (IDL) (<0.04) to 70 and IDL (<0.04) to 3859 ng/g lw, respectively. Levels of TBPH were comparable to SigmaHBCDs in porpoise samples. The presence of these novel flame retardants in top-trophic-level marine organisms raises concern about their release into the environment and indicates the need for further monitoring of these compounds in other environmental matrices.

Physical-chemical properties and evaluative fate modelling of 'emerging' and 'novel' brominated and organophosphorus flame retardants in the indoor and outdoor environment.

PubMed

Liagkouridis, Ioannis; Cousins, Anna Palm; Cousins, Ian T

2015-08-15

Several groups of flame retardants (FRs) have entered the market in recent years as replacements for polybrominated diphenyl ethers (PBDEs), but little is known about their physical-chemical properties or their environmental transport and fate. Here we make best estimates of the physical-chemical properties and undertake evaluative modelling assessments (indoors and outdoors) for 35 so-called 'novel' and 'emerging' brominated flame retardants (BFRs) and 22 organophosphorus flame retardants (OPFRs). A QSPR (Quantitative Structure-Property Relationship) based technique is used to reduce uncertainty in physical-chemical properties and to aid property selection for modelling, but it is evident that more, high quality property data are required for improving future assessments. Evaluative modelling results show that many of the alternative FRs, mainly alternative BFRs and some of the halogenated OPFRs, behave similarly to the PBDEs both indoors and outdoors. These alternative FRs exhibit high overall persistence (Pov), long-range transport potential (LRTP) and POP-like behaviour and on that basis cannot be regarded as suitable replacements to PBDEs. A group of low molecular weight alternative BFRs and non-halogenated OPFRs show a potentially better environmental performance based on Pov and LRTP metrics. Results must be interpreted with caution though since there are significant uncertainties and limited data to allow for thorough model evaluation. Additional environmental parameters such as toxicity and bioaccumulative potential as well as functionality issues should be considered in an industrial substitution strategy. Copyright © 2015 Elsevier B.V. All rights reserved.

Quantitative structure-activity relationship modeling on in vitro endocrine effects and metabolic stability involving 26 selected brominated flame retardants.

PubMed

Harju, Mikael; Hamers, Timo; Kamstra, Jorke H; Sonneveld, Edwin; Boon, Jan P; Tysklind, Mats; Andersson, Patrik L

2007-04-01

In this work, quantitative structure-activity relationships (QSARs) were developed to aid human and environmental risk assessment processes for brominated flame retardants (BFRs). Brominated flame retardants, such as the high-production-volume chemicals polybrominated diphenyl ethers (PBDEs), tetrabromobisphenol A, and hexabromocyclododecane, have been identified as potential endocrine disruptors. Quantitative structure-activity relationship models were built based on the in vitro potencies of 26 selected BFRs. The in vitro assays included interactions with, for example, androgen, progesterone, estrogen, and dioxin (aryl hydrocarbon) receptor, plus competition with thyroxine for its plasma carrier protein (transthyretin), inhibition of estradiol sulfation via sulfotransferase, and finally, rate of metabolization. The QSAR modeling, a number of physicochemical parameters were calculated describing the electronic, lipophilic, and structural characteristics of the molecules. These include frontier molecular orbitals, molecular charges, polarities, log octanol/water partitioning coefficient, and two- and three-dimensional molecularproperties. Experimental properties were included and measured for PBDEs, such as their individual ultraviolet spectra (200-320 nm) and retention times on three different high-performance liquid chromatography columns and one nonpolar gas chromatography column. Quantitative structure-activity relationship models based on androgen antagonism and metabolic degradation rates generally gave similar results, suggesting that lower-brominated PBDEs with bromine substitutions in ortho positions and bromine-free meta- and para positions had the highest potencies and metabolic degradation rates. Predictions made for the constituents of the technical flame retardant Bromkal 70-5DE found BDE 17 to be a potent androgen antagonist and BDE 66, which is a relevant PBDE in environmental samples, to be only a weak antagonist.

Associations between brominated flame retardants in house dust and hormone levels in men

PubMed Central

Johnson, Paula I.; Stapleton, Heather M.; Mukherjee, Bhramar; Hauser, Russ; Meeker, John D.

2013-01-01

Brominated flame retardants (BFRs) are used in the manufacture of a variety of materials and consumer products in order to meet fire safety standards. BFRs may persist in the environment and have been detected in wildlife, humans and indoor dust and air. Some BFRs have demonstrated endocrine and reproductive effects in animals, but human studies are limited. In this exploratory study, we measured serum hormone levels and flame retardant concentrations [31 polybrominated diphenyl ether (PBDE) congeners and 6 alternate flame retardants] in house dust from men recruited through a US infertility clinic. PBDE congeners in dust were grouped by commercial mixtures (i.e. penta-, octaand deca-BDE). In multivariable linear regression models adjusted by age and body mass index (BMI), significant positive associations were found between house dust concentrations of pentaBDEs and serum levels of free T4, total T3, estradiol, and sex hormone binding globulin (SHBG), along with an inverse association with follicle stimulating hormone (FSH). There were also positive associations of octaBDE concentrations with serum free T4, thyroid stimulating hormone (TSH), luteinizing hormone (LH) and testosterone and an inverse association of decaBDE concentrations with testosterone. Hexabromocyclododecane (HBCD) was associated with decreased SHBG and increased free androgen index. Dust concentrations of bis-tribromophenoxyethane (BTBPE) and tetrabromo-diethylhexylphthalate (TBPH) were positively associated with total T3. These findings are consistent with our previous report of associations between PBDEs (BDE 47, 99 and 100) in house dust and hormone levels in men, and further suggest that exposure to contaminants in indoor dust may be leading to endocrine disruption in men. PMID:23333513

A review of chamber experiments for determining specific emission rates and investigating migration pathways of flame retardants

NASA Astrophysics Data System (ADS)

Rauert, Cassandra; Lazarov, Borislav; Harrad, Stuart; Covaci, Adrian; Stranger, Marianne

2014-01-01

The widespread use of flame retardants (FRs) in indoor products has led to their ubiquitous distribution within indoor microenvironments with many studies reporting concentrations in indoor air and dust. Little information is available however on emission of these compounds to air, particularly the measurement of specific emission rates (SERs), or the migration pathways leading to dust contamination. Such knowledge gaps hamper efforts to develop understanding of human exposure. This review summarizes published data on SERs of the following FRs released from treated products: polybrominated diphenyl ethers (PBDEs), hexabromocyclododecanes (HBCDs), tetrabromobisphenol-A (TBBPA), novel brominated flame retardants (NBFRs) and organophosphate flame retardants (PFRs), including a brief discussion of the methods used to derive these SERs. Also reviewed are published studies that utilize emission chambers for investigations/measurements of mass transfer of FRs to dust, discussing the chamber configurations and methods used for these experiments. A brief review of studies investigating correlations between concentrations detected in indoor air/dust and possible sources in the microenvironment is included along with efforts to model contamination of indoor environments. Critical analysis of the literature reveals that the major limitations with utilizing chambers to derive SERs for FRs arise due to the physicochemical properties of FRs. In particular, increased partitioning to chamber surfaces, airborne particles and dust, causes loss through “sink” effects and results in long times to reach steady state conditions inside the chamber. The limitations of chamber experiments are discussed as well as their potential for filling gaps in knowledge in this area.

Durable flame retardant finish for silk fabric using boron hybrid silica sol

NASA Astrophysics Data System (ADS)

Zhang, Qiang-hua; Gu, Jiali; Chen, Guo-qiang; Xing, Tie-ling

2016-11-01

A hybrid silica sol was prepared via sol gel method using tetraethoxysilane (TEOS) as a precursor and boric acid (H3BO3) as flame retardant additive and then applied to silk fabric. In order to endow silk fabric with durable flame retardancy, 1,2,3,4-butanetetracarboxylic acid (BTCA) was used as cross-linking agent for the sake of strong linkage formation between the hybrid silica sol and silk fabric. The FT-IR and XPS analysis demonstrated the Si-O-B formation in the sol system, as well as the linkage between the sol and silk after the treatment. The limiting oxygen index (LOI) and smoke density test indicated good flame retardancy and smoke suppression of the treated silk fabrics. The micro calorimeter combustion (MCC) test and thermo gravimetric (TG) analysis showed that the treated samples had less weight loss in the high temperature and lower heat release rate when burning. The washing durability evaluation results indicated that there was a distinct improvement for the silk samples treated with BTCA even after 30 times washing. In addition, the influence of the processing order of BTCA and silica sol treatment on the limiting oxygen index (LOI) of the finished silk fabric was also investigated. And the results demonstrated that the sample treated with BTCA first and then with the silica sol exhibited better LOI value (32.3%) than that of the sample by the conversed treatment order. Moreover the tensile property of treated samples was nearly unchanged, but the handle of sol treated samples obviously decreased.

Multi-functional carbon microspheres with double shell layers for flame retardant poly (ethylene terephthalate)

NASA Astrophysics Data System (ADS)

Xue, Baoxia; Niu, Mei; Yang, Yongzhen; Bai, Jie; Song, Yinghao; Peng, Yun; Liu, Xuguang

2018-03-01

Carbon microspheres (CMSs) as a core material had been coated by two capsule walls: an inorganic material of magnesium hydroxide (MH) as inner shell layer and an organic material of poly (ethylene terephthalate) (PET) as outer shell layer. MH coating CMSs (MCMSs) were fabricated by liquid phase deposition method, then grafted 3-Aminopropyltriethoxysilane (APTS) to obtain the Si-MCMSs. Microencapsulated Si-MCMSs (PMCMSs) was prepared by in situ polymerization method. Morphology structure, dispersion, flame retardant and other properties of PMCMSs have been investigated. A series of PET blends were prepared by melt compounding. The results showed that MH and PET as two layers were coated on CMSs surface with the optimal thickness of about 70 nm. The PMCMSs owned better dispersion in PET matrix. Compared with MCMSs/PET composites, the mechanical property of PMCMSs/PET composites had significantly increased because of the strong interface binding force between PMCMSs and PET matrix. Moreover, PMCMSs was proved to be an effective flame retardant. For PMCMSs/PET with 2 wt% PMCMSs, the limiting oxygen index (LOI) value increased from 21.0% (pristine PET) to 27.2%, and the peak heat release rate (pk-HRR) decreased from 513.22 kW/m2 to 352.14 kW/m2. The decreased smoke production rate (SPR) and total smoke production (TSP) values demonstrated PMCMSs suppressed the smoke production. The increased Fire performance index (FPI) value illustrated PMCMSs significantly reduced the fire risk of PET. Overall, the two capsular walls endowed the PMCMSs/PET composites with good mechanical and flame-retardant properties.

Inhalation a significant exposure route for chlorinated organophosphate flame retardants.

PubMed

Schreder, Erika D; Uding, Nancy; La Guardia, Mark J

2016-05-01

Chlorinated organophosphate flame retardants (ClOPFRs) are widely used as additive flame retardants in consumer products including furniture, children's products, building materials, and textiles. Tests of indoor media in homes, offices, and other environments have shown these compounds are released from products and have become ubiquitous indoor pollutants. In house dust samples from Washington State, U.S.A., ClOPFRs were the flame retardants detected in the highest concentrations. Two ClOPFRs, tris(1,3-dichloro-2-propyl)phosphate (TDCPP or TDCIPP) and tris(2-chloroethyl)phosphate (TCEP), have been designated as carcinogens, and there is growing concern about the toxicity of the homologue tris(1-chloro-2-propyl)phosphate (TCPP or TCIPP). In response to concerns about exposure to these compounds, the European Union and a number of U.S. states have taken regulatory action to restrict their use in certain product categories. To better characterize exposure to ClOPFRs, inhalation exposure was assessed using active personal air samplers in Washington State with both respirable and inhalable particulate fractions collected to assess the likelihood particles penetrate deep into the lungs. Concentrations of ∑ClOPFRs (respirable and inhalable) ranged from 97.1 to 1190 ng m(-3) (mean 426 ng m(-3)), with TCPP detected at the highest concentrations. In general, higher levels were detected in the inhalable particulate fraction. Total intake of ClOPFRs via the inhalation exposure route was estimated to exceed intake via dust ingestion, indicating that inhalation is an important route that should be taken into consideration in assessments of these compounds. Copyright © 2015 Elsevier Ltd. All rights reserved.

Preparation of novel flame-retardant organoclay and its application to natural rubber composites

NASA Astrophysics Data System (ADS)

Zhang, Guangjian; Wang, Jincheng

2018-04-01

In this study, a novel type of flame-retardant montmorillonite (MMT) was prepared using a new approach to obtain highly branched polymer chains. First, MMT was modified using a small liquid crystal molecule comprising N,N,N tris(2-hydroxyethyl)sbnd N-dodecylammonium bromide and organic MMT (OMMT) was obtained. Next, three generations of dendrimer-modified organoclay comprising DOMMT-1, DOMMT-2, and DOMMT-3 were successfully prepared using OMMT and branching units of ethylenediamine and methyl acrylate. Their chemical structures were characterized and confirmed by different methods. The DOMMT organoclay was used in the preparation of natural rubber (NR) composites. The tensile strength and elongation at breakage for NR/DOMMT-10 were 17.3 MPa and 697%, respectively, which were about 13.8% and 10.8% higher, respectively, compared with that for the pure NR. After the addition of DOMMT, the horizontal burning time increased by about 69% and the thermal stability was also improved. We also propose a possible flame-retardant and reinforcing mechanism for this novel organoclay in an NR matrix.

Fire behavior of halogen-free flame retardant electrical cables with the cone calorimeter.

PubMed

Meinier, Romain; Sonnier, Rodolphe; Zavaleta, Pascal; Suard, Sylvain; Ferry, Laurent

2018-01-15

Fires involving electrical cables are one of the main hazards in Nuclear Power Plants (NPPs). Cables are complex assemblies including several polymeric parts (insulation, bedding, sheath) constituting fuel sources. This study provides an in-depth characterization of the fire behavior of two halogen-free flame retardant cables used in NPPs using the cone calorimeter. The influence of two key parameters, namely the external heat flux and the spacing between cables, on the cable fire characteristics is especially investigated. The prominent role of the outer sheath material on the ignition and the burning at early times was highlighted. A parameter of utmost importance called transition heat flux, was identified and depends on the composition and the structure of the cable. Below this heat flux, the decomposition is limited and concerns only the sheath. Above it, fire hazard is greatly enhanced because most often non-flame retarded insulation part contributes to heat release. The influence of spacing appears complex, and depends on the considered fire property. Copyright © 2017 Elsevier B.V. All rights reserved.

Levels, distribution and human exposure of new non-BDE brominated flame retardants in the indoor dust of China.

PubMed

Qi, Hong; Li, Wen-Long; Liu, Li-Yan; Zhang, Zi-Feng; Zhu, Ning-Zheng; Song, Wei-Wei; Ma, Wan-Li; Li, Yi-Fan

2014-12-01

Indoor environment is an important source of human exposure to several toxicants, such as brominated flame retardants. This study presents the concentrations of 22 Non-BDE brominated flame retardants (NBFRs) in 81 indoor dust samples from 23 provinces across China in the winter of 2010. The concentrations of ΣNBFRs ranged from 6.3 to 20,000 ng/g, with a median concentration of 720 ng/g. DBDPE was the dominated compound, followed by HBCD and BEHTBP. Significant differences of concentrations were found between samples from rural and urban areas, and between family and public houses, indicating different applications of NBFRs. The geographical distribution of NBFRs highlighted several hotspots in North China, suggesting the influence of room temperature (heating). The exposure via dust ingestion of NBFRs was 3.8-14 times higher than that of dermal absorption. The toddlers demonstrated the highest exposure dose (9.6 ng/kg-bw/day) of NBFRs through indoor dust among all life stages. Copyright © 2014 Elsevier Ltd. All rights reserved.

Brominated flame retardants in Chinese air before and after the phase out of polybrominated diphenyl ethers

NASA Astrophysics Data System (ADS)

Li, Wen-Long; Qi, Hong; Ma, Wan-Li; Liu, Li-Yan; Zhang, Zhi; Mohammed, Mohammed O. A.; Song, Wei-Wei; Zhang, Zifeng; Li, Yi-Fan

2015-09-01

Brominated flame retardants (BFRs), including polybrominated diphenyl ethers (PBDEs) and novel non-BDE flame retardants (NBFRs), were analyzed in Chinese air during China's POPs Soil and Air Monitoring Program Phase I (SAMP-I) and Phase II (SAMP-II). The levels of Σ12PBDEs and Σ6NBFRs in urban sites were significantly higher than those in rural sites and background sites. The higher detection rate and concentrations of high molecular weight PBDEs and NBFRs in Phase II indicated the changing of the commercial pattern of BFRs after the phase out of PBDEs in China. Temperature was the major factor affecting the seasonal variations of molecular weight BFRs in atmosphere. A significant correlation between BFRs concentration and gross domestic product (GDP) was observed, with the GDP parameter explained 59.4% and 72.7% of the total variability for Octa-BDEs and low molecular weight NBFRs, respectively. Our findings indicated an evolving commercial usage of BFRs from SAMP-I to SAMP-II, i.e. shifting from lower molecular weight to higher molecular weight congeners in China.

Analytical and environmental aspects of the flame retardant tetrabromobisphenol-A and its derivatives.

PubMed

Covaci, Adrian; Voorspoels, Stefan; Abdallah, Mohamed Abou-Elwafa; Geens, Tinne; Harrad, Stuart; Law, Robin J

2009-01-16

The present article reviews the available literature on the analytical and environmental aspects of tetrabromobisphenol-A (TBBP-A), a currently intensively used brominated flame retardant (BFR). Analytical methods, including sample preparation, chromatographic separation, detection techniques, and quality control are discussed. An important recent development in the analysis of TBBP-A is the growing tendency for liquid chromatographic techniques. At the detection stage, mass-spectrometry is a well-established and reliable technology in the identification and quantification of TBBP-A. Although interlaboratory exercises for BFRs have grown in popularity in the last 10 years, only a few participating laboratories report concentrations for TBBP-A. Environmental levels of TBBP-A in abiotic and biotic matrices are low, probably due to the major use of TBBP-A as reactive FR. As a consequence, the expected human exposure is low. This is in agreement with the EU risk assessment that concluded that there is no risk for humans concerning TBBP-A exposure. Much less analytical and environmental information exists for the various groups of TBBP-A derivatives which are largely used as additive flame retardants.

Initial Fire Suppression Reactions of Halons Phase 1. Development of Experimental Approach

DTIC Science & Technology

1990-09-01

Engineering News, pp. 22-46, August 31, 1987. Mitani, T., " Flame Retardant Effects of CF 3Br and NaHCO 3 Combustion and Flame , Vol. 50, pp. 177-188, 1983...occurring when halons enter flame fronts are unclear. It is these initial reactions, however, that determine differences in halon performance, the effect of...LABORATORY FLAMES Over the past four decades, numerous tests have been performed in an effort to characterize the relative effectiveness of candidate

Develop of innovative technologies for flame resistant cotton fabrics at USDA

USDA-ARS?s Scientific Manuscript database

Supercritical carbon dioxide (scCO2) high pressure and microwave reactor are considered in green chemistry as a substitute for organic solvents in chemical reactions. In this presentation, innovative approaches for preparation of flame retardant fabrics were obtained by utilizing supercritical carb...

Development of innovative technologies for flame resistant cotton fabrics at USDA

USDA-ARS?s Scientific Manuscript database

Supercritical carbon dioxide (scCO2) high pressure and microwave reactor are considered in green chemistry as a substitute for organic solvents in chemical reactions. In this presentation, innovative approaches for preparation of flame retardant fabrics were obtained by utilizing supercritical carbo...

High temperature ablative foam

NASA Technical Reports Server (NTRS)

Liu, Matthew T. (Inventor)

1992-01-01

An ablative foam composition is formed of approximately 150 to 250 parts by weight polymeric isocyanate having an isocyanate functionality of 2.6 to 3.2; approximately 15 to 30 parts by weight reactive flame retardant having a hydroxyl number range from 200-260; approximately 10 to 40 parts by weight non-reactive flame retardant; approximately 10 to 40 parts by weight nonhydrolyzable silicone copolymer having a hydroxyl number range from 75-205; and approximately 3 to 16 parts by weight amine initiated polyether resin having an isocyanate functionality greater than or equal to 3.0 and a hydroxyl number range from 400-800.

Effects of selected polybrominated diphenyl ether flame retardants on lake trout (Salvelinus namaycush) thymocyte viability, apoptosis, and necrosis

USGS Publications Warehouse

Birchmeier, Kelly L.; Smith, Kimberly A.; Passino-Reader, Dora R.; Sweet, Leonard I.; Chernyak, Sergei M.; Adams, Jean V.; Omann, Geneva M.

2005-01-01

Polybrominated diphenyl ether (PBDE) flame-retardants have been identified as an emergent contaminants issue in many parts of the world. In vitro analyses were conducted to test the hypothesis that selected PBDEs congeners affect viability, apoptosis, and necrosis of thymocytes from laboratory-reared lake trout (Salvelinus namaycush). At current environmental levels (<1 mg/L), effects of the tested PBDEs on thymocytes were negligible. However, at 100 mg/L, major effects were seen for congener brominated diphenyl ether 47 (BDE-47) and minor effects were seen for congener BDE-99.

Health risk characterization for resident inhalation exposure to particle-bound halogenated flame retardants in a typical e-waste recycling zone.

PubMed

Luo, Pei; Bao, Lian-Jun; Wu, Feng-Chang; Li, Shao-Meng; Zeng, Eddy Y

2014-01-01

Inhalation of pollutants is an important exposure route for causing human health hazards, and inhalation exposure assessment must take into account particle size distribution because particle-bound pollutants are size-dependent. Such information is scarce, particularly for residents dwelling within e-waste recycling zones where abundant atmospheric halogenated flame retardants (HFRs) commonly used in electronic/electrical devices have been widely reported. Atmospheric size-fractioned particle samples were collected using a 10-stage Micro-Orifice Uniform Deposit Impactor from an e-waste recycling zone in South China. The deposition efficiencies and fluxes of size-fractioned HFRs including polybrominated diphenyl ethers (PBDEs), alternative brominated flame retardants, and Dechlorane Plus in the human respiratory tract were estimated using the International Commission on Radiological Protection deposition model. The majority of HFRs was found to deposit in the head airways, with coarse particles (aerodynamic diameter (Dp) > 1.8 μm) contributing the most (69-91%). Conversely, fine particles (Dp < 1.8 μm) were dominant in the alveolar region (62-80%). The inhalation intake of PBDEs within the e-waste recycling zone was 44 ng/d (95% confidence interval (CI): 30-65 ng/d), close to those through food consumption in non-e-waste recycling regions. The estimated total hazard quotient of particle-bound HFRs was 5.6 × 10(-4) (95% CI: 3.8 × 10(-4)-8.8 × 10(-4)). In addition, incremental lifetime cancer risk induced by BDE-209 was 1.36 × 10(-10) (95% CI: 7.3 × 10(-11)-2.3 × 10(-10)), much lower than the Safe Acceptable Range (1.0 × 10(-6)-1.0 × 10(-4)) established by the United States Environmental Protection Agency. These results indicate that the potential health risk from inhalation exposure to particle-bound HFRs for residents dwelling in the e-waste recycling zone was low.

Pilot-scale incineration of wastes with high content of chlorinated and non-halogenated organophosphorus flame retardants used as alternatives for PBDEs.

PubMed

Matsukami, Hidenori; Kose, Tomohiro; Watanabe, Mafumi; Takigami, Hidetaka

2014-09-15

Chlorinated and non-halogenated organophosphorus flame retardants (OPFRs) including tris(2-chloroisopropyl) phosphate (TCIPP), diethylene glycol bis(di(2-chloroisopropyl) phosphate) (DEG-BDCIPP), triphenyl phosphate (TPHP), and bisphenol A bis(diphenyl phosphate) (BPA-BDPP) have been used increasingly as alternatives to polybrominated diphenyl ethers and other brominated flame retardants. For this study, five batches of incineration experiments of wastes containing approximately 1% of TCIPP, DEG-BDCIPP, TPHP, and BPA-BDPP were conducted using a pilot-scale incinerator. Destruction and emission behaviors of OPFRs were investigated along with the effects on behaviors of unintentional persistent organic pollutants (POPs) such as polychlorinated dibenzo-p-dioxins (PCDDs), polychlorinated dibenzofurans (PCDFs), dioxin-like polychlorinated biphenyls (dl-PCBs), hexachlorobenzene (HCB), pentachlorobenzene (PeCB), and pentachlorophenol (PCP). Incineration conditions were chosen according to current regulations for waste incinerators in Japan and UNEP. The OPFRs in the input materials were mainly destroyed in the primary combustion with destruction efficiencies greater than 99.999%. Concentrations of the OPFRs in the exhaust gases and ash were, respectively, <0.01-0.048 μg m(-3) and <0.5-68 μg kg(-1). Almost all of the total phosphorus in the input materials was partitioned into the ash, but less into final exit gases, indicating negligible emissions of volatile phosphorus compounds during incineration. Inputs of chlorinated OPFRs did not affect the formation markedly. Destruction and emission behaviors of unintentional POPs were investigated. Emissions of such POPs in exhaust gases and the ash were lower than the Japanese and international standards. Results show that even in wastes with high contents of chlorinated and non-halogenated OPFRs, waste incineration by the current regulations for the waste incinerators can control environmental emissions of OPFRs and unintentional POPs. Incineration is regarded as a best available technology (BAT) for waste management systems. Copyright © 2014 Elsevier B.V. All rights reserved.

Determination of novel brominated flame retardants and polybrominated diphenyl ethers in serum using gas chromatography-mass spectrometry with two simplified sample preparation procedures.

PubMed

Gao, Le; Li, Jian; Wu, Yandan; Yu, Miaohao; Chen, Tian; Shi, Zhixiong; Zhou, Xianqing; Sun, Zhiwei

2016-11-01

Two simple and efficient pretreatment procedures have been developed for the simultaneous extraction and cleanup of six novel brominated flame retardants (NBFRs) and eight common polybrominated diphenyl ethers (PBDEs) in human serum. The first sample pretreatment procedure was a quick, easy, cheap, effective, rugged, and safe (QuEChERS)-based approach. An acetone/hexane mixture was employed to isolate the lipid and analytes from the serum with a combination of MgSO 4 and NaCl, followed by a dispersive solid-phase extraction (d-SPE) step using C18 particles as a sorbent. The second sample pretreatment procedure was based on solid-phase extraction. The sample extraction and cleanup were conducted directly on an Oasis HLB SPE column using 5 % aqueous isopropanol, concentrated sulfuric acid, and 10 % aqueous methanol, followed by elution with dichloromethane. The NBFRs and PBDEs were then detected using gas chromatography-negative chemical ionization mass spectrometry (GC-NCI MS). The methods were assessed for repeatability, accuracy, selectivity, limits of detection (LODs), and linearity. The results of spike recovery experiments in fetal bovine serum showed that average recoveries ranged from 77.9 % to 128.8 % with relative standard deviations (RSDs) from 0.73 % to 12.37 % for most of the analytes. The LODs for the analytes in fetal bovine serum ranged from 0.3 to 50.8 pg/mL except for decabromodiphenyl ethane. The proposed method was successfully applied to the determination of the 14 brominated flame retardants in human serum. The two pretreatment procedures described here are simple, accurate, and precise, and are suitable for the routine analysis of human serum. Graphical Abstract Workflow of a QuEChERS-based approach (top) and an SPE-based approach (bottom) for the detection of PBDEs and NBFRs in serum.

Effect of clays on the fire-retardant properties of a polyethylenic copolymer containing intumescent formulation

PubMed Central

Ribeiro, Simone P S; Estevão, Luciana R M; Nascimento, Regina S V

2008-01-01

Organophilic clay particles were added to a standard intumescent formulation and, since the role of clay expansion or intercalation is still a matter of much controversy, several clays with varying degrees of interlayer distances were evaluated. The composites were obtained by blending the nanostructured clay and the intumescent system with a polyethylenic copolymer. The flame-retardant properties of the materials were evaluated by the limiting oxygen index (LOI), the UL-94 rating and thermogravimetric analysis (TGA). The results showed that the addition of highly expanded clays to the ammonium polyphosphate and pentaerythritol formulation does not significantly increase the flame retardancy of the mixture, when measured by the LOI and UL-94. However, when clays with smaller basal distances were added to the intumescent formulation, a synergistic effect was observed. In contrast, the simple addition of clays to the copolymer, without the intumescent formulation, did not increase the fire retardance of the materials. PMID:27877975

Flyweight 3D Graphene Scaffolds with Microinterface Barrier-Derived Tunable Thermal Insulation and Flame Retardancy.

PubMed

Zhang, Qiangqiang; Hao, Menglong; Xu, Xiang; Xiong, Guoping; Li, Hui; Fisher, Timothy S

2017-04-26

In this article, flyweight three-dimensional (3D) graphene scaffolds (GSs) have been demonstrated with a microinterface barrier-derived thermal insulation and flame retardancy characteristics. Such 3D GSs were fabricated by a modified hydrothermal method and a unidirectional freeze-casting process with hierarchical porous microstructures. Because of high porosity (99.9%), significant phonon scattering, and strong π-π interaction at the interface barriers of multilayer graphene cellular walls, the GSs demonstrate a sequence of multifunctional properties simultaneously, such as lightweight density, thermal insulating characteristics, and outstanding mechanical robustness. At 100 °C, oxidized GSs exhibit a thermal conductivity of 0.0126 ± 0.0010 W/(m K) in vacuum. The thermal conductivity of oxidized GSs remains relatively unaffected despite large-scale deformation-induced densification of the microstructures, as compared to the behavior of reduced GSs (rGSs) whose thermal conductivity increases dramatically under compression. The contrasting behavior of oxidized GSs and rGSs appears to derive from large differences in the intersheet contact resistance and varying intrinsic thermal conductivity between reduced and oxidized graphene sheets. The oxidized GSs also exhibit excellent flame retardant behavior and mechanical robustness, with only 2% strength decay after flame treatment. In a broader context, this work demonstrates a useful strategy to design porous nanomaterials with a tunable heat conduction behavior through interface engineering at the nanoscale.

Organo-modified bentonites as new flame retardant fillers in epoxy resin nanocomposites

NASA Astrophysics Data System (ADS)

Benelli, Tiziana; D'Angelo, Emanuele; Mazzocchetti, Laura; Saraga, Federico; Sambri, Letizia; Franchini, Mauro Comes; Giorgini, Loris

2016-05-01

The present work deals with two organophilic bentonites, based on nitrogen-containing compounds: these organoclays were synthesized via an ion exchange process starting from pristine bentonite with 6-(4-butylphenyl)-1,3,5-triazine-2,4-diamine (BFTDA) and 11-amino-N-(pyridine-2yl)undecanamide (APUA) and then used for the production of epoxy-based flame retardant nanocomposites. The amount of organic modifier in the organoclays Bento-BFTDA and Bento-APUA was determined with a TGA analysis and is around 0.4mmol/g for both samples. The effect of the organoclays on a commercial epoxy resin nanocomposite's thermo-mechanical and flammability properties was investigated. Composites containing 3wt% and 5wt% of the nanofillers were prepared by solventless addition of each organoclay to the epoxy resin, followed by further addition of the hardener component. For the sake of comparison a similar nanocomposite with the plain unmodified bentonite was produced in similar condition. The nanocomposites's thermo-mechanical properties of all the produced samples were measured and they resulted slightly improved or practically unaffected. On the contrary, when the flame behaviour was assessed in the cone-calorimeter, an encouraging decrease of 17% in the peak heat released rate (pHRR) was obtained at 3wt% loading level with Bento-APUA. This is a promising result, assessing that the APUA modified organoclay might act as flame retardant.

Phosphate flame retardants and novel brominated flame retardants in home-produced eggs from an e-waste recycling region in China.

PubMed

Zheng, Xiaobo; Xu, Fuchao; Luo, Xiaojun; Mai, Bixian; Covaci, Adrian

2016-05-01

Phosphate flame retardants (PFRs) and novel brominated flame retardants (NBFRs) (2-ethylhexyl-2,3,4,5-tetrabromo-benzoate (EH-TBB) and bis-(2-ethylhexyl)-3,4,5,6-tetrabromo-phthalate (BEH-TEBP)) were measured in free-range chicken eggs from three e-waste recycling sites and a negative control site located in Guangdong province, Southern China. BEH-TEBP, tris-(chloroethyl)-phosphate (TCEP), tris-(chloropropyl)-phosphate (∑TCPP, two isomers) and tris-(1,3-dichloroisopropyl)-phosphate (TDCIPP) were detected in more than 50% of eggs samples with low concentrations. The median values of BEH-TEBP and total PFRs were 0.17-0.46 ng/g ww (wet weight) and 1.62-2.59 ng/g ww in eggs from the e-waste sites, respectively. The results indicate that EH-TBB, BEH-TEBP and PFRs are less persistent and bioaccumulative than polybrominated diphenyl ethers (PBDEs) in chicken eggs, and possibly also in other bio-matrices. Triphenyl phosphate (TPHP) were identified in albumen with higher frequencies, but at similar concentrations compared to yolk, while BEH-TEBP was mainly detected in yolk. The estimated daily intake (EDI) of BEH-TEBP and total PFRs from consumption of chicken eggs ranged from 0.03 to 0.09 and 0.32-0.52 ng/kg bw/day for adults, and 0.20-0.54 and 1.89-3.02 ng/kg bw/day for children in e-waste sites, respectively. Indoor dust ingestion seems to be a more important pathway for the intake of these FRs, while egg consumption is probably a more important exposure pathway for PBDEs. Copyright © 2015 Elsevier Ltd. All rights reserved.

Alternative Flame Retardant, 2,4,6-Tris(2,4,6-tribromophenoxy)-1,3,5-triazine, in an E-waste Recycling Facility and House Dust in North America.

PubMed

Guo, Jiehong; Stubbings, William A; Romanak, Kevin; Nguyen, Linh V; Jantunen, Liisa; Melymuk, Lisa; Arrandale, Victoria; Diamond, Miriam L; Venier, Marta

2018-03-20

A high molecular weight compound, 2,4,6-tris(2,4,6-tribromophenoxy)-1,3,5-triazine (TTBP-TAZ), was detected during the analysis of brominated flame retardants in dust samples collected from an electrical and electronic waste (e-waste) recycling facility in Ontario, Canada. Gas chromatography coupled with both high-resolution and low-resolution mass spectrometry (MS) was used to determine TTBP-TAZ's chemical structure and concentrations. To date, TTBP-TAZ has only been detected in plastic casings of electrical and electronic equipment and house dust from The Netherlands. Here we report on the concentrations of TTBP-TAZ in selected samples from North America: e-waste dust ( n = 7) and air ( n = 4), residential dust ( n = 30), and selected outdoor air ( n = 146), precipitation ( n = 19), sediment ( n = 11) and water ( n = 2) samples from the Great Lakes environment. TTBP-TAZ was detected in all the e-waste dust and air samples, and in 70% of residential dust samples. The median concentrations of TTBP-TAZ in these three types of samples were 5540 ng/g, 5.75 ng/m 3 and 6.76 ng/g, respectively. The flame retardants 2,4,6-tribromophenol, tris(2,3-dibromopropyl) isocyanurate, and 3,3',5,5'-tetrabromobisphenol A bis(2,3-dibromopropyl) ether, BDE-47 and BDE-209 were also measured for comparison. None of these other flame retardants concentrations was significantly correlated with those of TTBP-TAZ in any of the sample types suggesting different sources. TTBP-TAZ was not detected in any of the outdoor environmental samples, which may relate to its application history and physicochemical properties. This is the first report of TTBP-TAZ in North America.

Anti-flammable vinyl ester resin nano-composite with nano-titania

NASA Astrophysics Data System (ADS)

Das, Rajib

Anti-flammable material is a common expectation for any industry and household applications to protect the material from fire accident. Polymer composites also play a significant role in preparing anti flammable materials. Vinyl ester resins (VERs) are thermosetting resins that have excellent mechanical and thermal properties of epoxy resins and Nanotitania is an inexpensive, nontoxic and biocompatible inorganic material. In this paper to investigate the flame retardency of polymer nanocomposites VER is used as polymer matrix and TiO2 is used as inorganic nanofiller.3-[2-(2-aminoethylamino) ethylamino]propyl-trimethoxysilane (TATMS), a kind of silane is used as a coupling agent to functionalize the surface of nanoTiO2 to improve its flame retardency by adding Si and N2 group. TGA test and FTIR test have been performed and different peaks for Si and N2 in the modified nanofiller and weight loss of fabricated nanofiller confirmed that fabrication method was successful. After that, nanocomposite sample of VERs reinforced with nano TiO2 prepared and the effects of different loadings on mechanical and flame retardant properties are investigated after and before the modification of nanofillers. From tensile test result it is found that up to 5% loading of modified nanofiller the tensile strength is 62 MPa that is almost as same as pure VER and the tensile strength of unmodified nanofiller based PNC is 68 MPa which is not significant improvement in its mechanical property. From MCC test of flame retardancy it is found that the normalized heat release capacity of modified nanofiller based nanocomposite is decreased by 27.7% than unmodified nanofiller based PNC that is 9.8%. Also the normalized total heat release of modified nanofiller based PNC is 21.4% than unmodified PNC that is 12.4%.

Nanotechnology finding its way into flame retardancy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schartel, Bernhard, E-mail: bernhard.schartel@bam.de

2014-05-15

Nanotechnology is one of the key technologies of the 21{sup st} century. The exploitation of 'new' effects that arise from materials structured on the nano-scale has also been proposed successfully for flame retardancy of polymers since the end of the 90s. Of all of the approaches these include, at this time the use of nanocomposites offers the best potential for industrial application, also some other ideas are sketched, such as using electrospun nanofibers mats or layer-by-layer deposits as protection coatings, as well as sub-micrometer multilayer coatings as effective IR-mirrors. The general phenomena, inducing a flow limit in the pyrolysing meltmore » and changing the fire residue, are identified in nanocomposites. Key experiments are performed such as quasi online investigation of the protection layer formation to understand what is going on in detail. The flame retardancy mechanisms are discussed and their impact on fire behaviour quantified. With the latter, the presentation pushes forward the state of the art. For instance, the heat shielding is experimentally quantified for a layered silicate epoxy resin nanocomposite proving that it is the only import mechanism controlling the reduction in peak heat release rate in the investigated system for different irradiations. The flame retardancy performance is assessed comprehensively illuminating not only the strengths but also the weak points of the concepts. Guidelines for materials development are deduced and discussed. Apart from inorganic fillers (layered silicate, boehmite, etc.) not only carbon nanoobjects such as multiwall carbon nanotubes, multilayer graphene and graphene are investigated, but also nanoparticles that are more reactive and harbor the potential for more beneficial interactions with the polymer matrix.« less

Exposure to an environmentally relevant mixture of brominated flame retardants affects fetal development in Sprague-Dawley rats.

PubMed

Berger, Robert G; Lefèvre, Pavine L C; Ernest, Sheila R; Wade, Michael G; Ma, Yi-Qian; Rawn, Dorothea F K; Gaertner, Dean W; Robaire, Bernard; Hales, Barbara F

2014-06-05

Brominated flame retardants are incorporated into a wide variety of consumer products and are known to enter into the surrounding environment, leading to human exposure. There is accumulating evidence that these compounds have adverse effects on reproduction and development in humans and animal models. Animal studies have generally characterized the outcome of exposure to a single technical mixture or congener. Here, we determined the impact of exposure of rats prior to mating and during gestation to a mixture representative of congener levels found in North American household dust. Adult female Sprague-Dawley rats were fed a diet containing 0, 0.75, 250 or 750mg/kg of a mixture of flame retardants (polybrominated diphenyl ethers, hexabromocyclododecane) from two weeks prior to mating to gestation day 20. This formulation delivered nominal doses of 0, 0.06, 20 and 60mg/kg body weight/day. The lowest dose approximates high human exposures based on house dust levels and the dust ingestion rates of toddlers. Litter size and resorption sites were counted and fetal development evaluated. No effects on maternal health, litter size, fetal viability, weights, crown rump lengths or sex ratios were detected. The proportion of litters with fetuses with anomalies of the digits (soft tissue syndactyly or malposition of the distal phalanges) was increased significantly in the low (0.06mg/kg/day) dose group. Skeletal analysis revealed a decreased ossification of the sixth sternebra at all exposure levels. Thus, exposure to an environmentally relevant mixture of brominated flame retardants results in developmental abnormalities in the absence of apparent maternal toxicity. The relevance of these findings for predicting human risk is yet to be determined. Copyright © 2014. Published by Elsevier Ireland Ltd.

Recycling of plastic waste: Screening for brominated flame retardants (BFRs).

PubMed

Pivnenko, K; Granby, K; Eriksson, E; Astrup, T F

2017-11-01

Flame retardants are chemicals vital for reducing risks of fire and preventing human casualties and property losses. Due to the abundance, low cost and high performance of bromine, brominated flame retardants (BFRs) have had a significant share of the market for years. Physical stability on the other hand, has resulted in dispersion and accumulation of selected BFRs in the environment and receiving biota. A wide range of plastic products may contain BFRs. This affects the quality of waste plastics as secondary resource: material recycling may potentially reintroduce the BFRs into new plastic product cycles and lead to increased exposure levels, e.g. through use of plastic packaging materials. To provide quantitative and qualitative data on presence of BFRs in plastics, we analysed bromophenols (tetrabromobisphenol A (TBBPA), dibromophenols (2,4- and 2,6-DBP) and 2,4,6-tribromophenol (2,4,6-TBP)), hexabromocyclododecane stereoisomers (α-, β-, and γ-HBCD), as well as selected polybrominated diphenyl ethers (PBDEs) in samples of household waste plastics, virgin and recycled plastics. A considerable number of samples contained BFRs, with highest concentrations associated with acrylonitrile butadiene styrene (ABS, up to 26,000,000ngTBBPA/g) and polystyrene (PS, up to 330,000ng∑HBCD/g). Abundancy in low concentrations of some BFRs in plastic samples suggested either unintended addition in plastic products or degradation of higher molecular weight BFRs. The presence of currently restricted flame retardants (PBDEs and HBCD) identified in the plastic samples illustrates that circular material flows may be contaminated for extended periods. The screening clearly showed a need for improved documentation and monitoring of the presence of BFRs in plastic waste routed to recycling. Copyright © 2017 Elsevier Ltd. All rights reserved.

Metabolsim of a-and y~Hexabromocylododecane and Enantioselective Fractions of a-, B-, y-Isomers in Mice.

EPA Science Inventory

Hexabromocyclododecane (HBCD) is the third-highest production volume brominated flame retardant (BFR). It is incorporated into expanded polystyrene foam used in thermal insulation of buildings, and currently is the only suitable BFR for this application. HBCD is an additive flame...

IN VITRO EFFECTS OF BROMINATED FLAME RETARDANS ON CALCIUM BUFFERING MECHANISMS IN RAT BRAINS.

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) are widely used as additive flame-retardants and have been detected in human blood, adipose tissue, and breast milk. Developmental and long-term exposures to these chemicals may pose a human health risk, especially to children. It has been d...

Fish energy budget under ocean warming and flame retardant exposure.

PubMed

Anacleto, Patrícia; Figueiredo, Cátia; Baptista, Miguel; Maulvault, Ana Luísa; Camacho, Carolina; Pousão-Ferreira, Pedro; Valente, Luísa M P; Marques, António; Rosa, Rui

2018-07-01

Climate change and chemical contamination are global environmental threats of growing concern for the scientific community and regulatory authorities. Yet, the impacts and interactions of both stressors (particularly ocean warming and emerging chemical contaminants) on physiological responses of marine organisms remain unclear and still require further understanding. Within this context, the main goal of this study was to assess, for the first time, the effects of warming (+ 5 °C) and accumulation of a polybrominated diphenyl ether congener (BDE-209, brominated flame retardant) through dietary exposure on energy budget of the juvenile white seabream (Diplodus sargus). Specifically, growth (G), routine metabolism (R), excretion (faecal, F and nitrogenous losses, U) and food consumption (C) were calculated to obtain the energy budget. The results demonstrated that the energy proportion spent for G dominated the mode of the energy allocation of juvenile white seabream (56.0-67.8%), especially under the combined effect of warming plus BDE-209 exposure. Under all treatments, the energy channelled for R varied around 26% and a much smaller percentage was channelled for excretion (F: 4.3-16.0% and U: 2.3-3.3%). An opposite trend to G was observed to F, where the highest percentage (16.0 ± 0.9%) was found under control temperature and BDE-209 exposure via diet. In general, the parameters were significantly affected by increased temperature and flame retardant exposure, where higher levels occurred for: i) wet weight, relative growth rate, protein and ash contents under warming conditions, ii) only for O:N ratio under BDE-209 exposure via diet, and iii) for feed efficiency, ammonia excretion rate, routine metabolic rate and assimilation efficiency under the combination of both stressors. On the other hand, decreased viscerosomatic index was observed under warming and lower fat content was observed under the combined effect of both stressors. Overall, under future warming and chemical contamination conditions, fish energy budget was greatly affected, which may dictate negative cascading impacts at population and community levels. Further research combining other climate change stressors (e.g. acidification and hypoxia) and emerging chemical contaminants are needed to better understand and forecast such biological effects in a changing ocean. Copyright © 2018 Elsevier Inc. All rights reserved.

Solvent effects on quantitative analysis of brominated flame retardants with Soxhlet extraction.

PubMed

Zhong, Yin; Li, Dan; Zhu, Xifen; Huang, Weilin; Peng, Ping'an

2017-05-18

Reliable quantifications of brominated flame retardants (BFRs) not only ensure compliance with laws and regulations on the use of BFRs in commercial products, but also is key for accurate risk assessments of BFRs. Acetone is a common solvent widely used in the analytical procedure of BFRs, but our recent study found that acetone can react with some BFRs. It is highly likely that such reactions can negatively affect the quantifications of BFRs in environmental samples. In this study, the effects of acetone on the extraction yields of three representative BFRs [i.e., decabrominated diphenyl ether (decaBDE), hexabromocyclododecane (HBCD) and tetrabromobisphenol A (TBBPA)] were evaluated in the Soxhlet extraction (SE) system. The results showed that acetone-based SE procedure had no measureable effect for the recovery efficiencies of decaBDE but could substantially lower the extraction yields for both TBBPA and HBCD. After 24 h of extraction, the recovery efficiencies of TBBPA and HBCD by SE were 93 and 78% with acetone, 47 and 70% with 3:1 acetone:n-hexane, and 82 and 94% with 1:1 acetone:n-hexane, respectively. After 72 h of extraction, the extraction efficiencies of TBBPA and HBCD decreased to 68 and 55% with acetone, 0 and 5% with 3:1 acetone/n-hexane mixtures, and 0 and 13% with 1:1 acetone/n-hexane mixtures, respectively. The study suggested that the use of acetone alone or acetone-based mixtures should be restricted in the quantitative analysis of HBCD and TBBPA. We further evaluated nine alternative solvents for the extraction of the three BFRs. The result showed that diethyl ether might be reactive with HBCD and may not be considered as the alternative to acetone used solvents for the extraction of HBCD.

76 FR 21339 - Certain New Chemicals; Receipt and Status Information

Federal Register 2010, 2011, 2012, 2013, 2014

2011-04-15

...- tetramethyldisil tetramethyl-* oxane--see gls138; reducing agent for organic substrates, e.g. pharmaceutical... Specialties, Inc. (G) Flame (G) Organic-N,P- retardant for compound incorporation into polymer resins (open...) Organic-N,P- retardant for compound incorporation into polymer resins (open non- dispersive use). P-11...

From Clothing to Laundry Water: Investigating the Fate of Phthalates, Brominated Flame Retardants, and Organophosphate Esters.

PubMed

Saini, Amandeep; Thaysen, Clara; Jantunen, Liisa; McQueen, Rachel H; Diamond, Miriam L

2016-09-06

The accumulation of phthalate esters, brominated flame retardants (BFRs) and organophosphate esters (OPEs) by clothing from indoor air and transfer via laundering to outdoors were investigated. Over 30 days cotton and polyester fabrics accumulated 3475 and 1950 ng/dm(2) ∑5phthalates, 65 and 78 ng/dm(2) ∑10BFRs, and 1200 and 310 ng/dm(2) ∑8OPEs, respectively. Planar surface area concentrations of OPEs and low molecular weight phthalates were significantly greater in cotton than polyester and similar for BFRs and high molecular weight phthalates. This difference was significantly and inversely correlated with KOW, suggesting greater sorption of polar compounds to polar cotton. Chemical release from cotton and polyester to laundry water was >80% of aliphatic OPEs (log KOW < 4), < 50% of OPEs with an aromatic structure, 50-100% of low molecular weight phthalates (log KOW 4-6), and < detection-35% of higher molecular weight phthalates (log KOW > 8) and BFRs (log KOW > 6). These results support the hypothesis that clothing acts an efficient conveyer of soluble semivolatile organic compounds (SVOCs) from indoors to outdoors through accumulation from air and then release during laundering. Clothes drying could as well contribute to the release of chemicals emitted by electric dryers. The results also have implications for dermal exposure.

Low-smoke, halogenfree ship-offshore/onshore cables with improved flame retardance and fire resistance

NASA Astrophysics Data System (ADS)

Pedersen, J. R.; Holte, T. A.; Johansen, E.

Cables with improved fire resistance and flame retardance have been developed. They will continue to function at least 3 hours even at temperatures up to 1000 C and do not propagate fire when tested according to IEC 332 part 3 1982, category A. Made with halogenfree materials they give off no corrosive gases and very little visible smoke in cases of fire. Cables are made for power, signal and instrument installations in hospitals, high rise buildings, railroad cars, subways, on board ship, oil rigs and oil production platforms. The offshore cables are specially constructed to withstand the rugged climatic conditions in the North Sea area.

Preparation, testing, and delivery of low density polyimide foam panels

NASA Technical Reports Server (NTRS)

Ball, G. L., III; Post, L. K.; Salyer, I. O.

1975-01-01

Plastic foams based on polyimide resins were shown to be stable at relatively high temperatures, and to possess very low flame spread and smoke generation characteristics. A system and process were developed to prepare low-density polyimide foam from a liquid formulation. The system is based on the reaction of micropulverized grade pyromellitic dianhydride with a polymeric diisocyanate. The panels produced were postcured at elevated temperatures to achieve maximum thermal and fire resistance, and incorporation of a fire retardant into the formulation was considered. The effects of a flame retardant (Flameout 5600B1) were investigated, but eliminated in preference to the postcuring approach.

Organophosphorus Flame Retardants Inhibit Specific Liver Carboxylesterases and Cause Serum Hypertriglyceridemia

PubMed Central

2015-01-01

Humans are prevalently exposed to organophosphorus flame retardants (OPFRs) contained in consumer products and electronics, though their toxicological effects and mechanisms remain poorly understood. We show here that OPFRs inhibit specific liver carboxylesterases (Ces) and cause altered hepatic lipid metabolism. Ablation of the OPFR target Ces1g has been previously linked to dyslipidemia in mice. Consistent with OPFR inhibition of Ces1g, we also observe OPFR-induced serum hypertriglyceridemia in mice. Our findings suggest novel toxicities that may arise from OPFR exposure and highlight the utility of chemoproteomic and metabolomic platforms in the toxicological characterization of environmental chemicals. PMID:24597639

Li-Ion Electrolytes with Improved Safety and Tolerance to High-Voltage Systems

NASA Technical Reports Server (NTRS)

Smart, Marshall C.; Bugga, Ratnakumar V.; Prakash, Surya; Krause, Frederick C.

2013-01-01

Given that lithium-ion (Li-ion) technology is the most viable rechargeable energy storage device for near-term applications, effort has been devoted to improving the safety characteristics of this system. Therefore, extensive effort has been devoted to developing nonflammable electrolytes to reduce the flammability of the cells/battery. A number of promising electrolytes have been developed incorporating flame-retardant additives, and have been shown to have good performance in a number of systems. However, these electrolyte formulations did not perform well when utilizing carbonaceous anodes with the high-voltage materials. Thus, further development was required to improve the compatibility. A number of Li-ion battery electrolyte formulations containing a flame-retardant additive [i.e., triphenyl phosphate (TPP)] were developed and demonstrated in high-voltage systems. These electrolytes include: (1) formulations that incorporate varying concentrations of the flame-retardant additive (from 5 to 15%), (2) the use of mono-fluoroethylene carbonate (FEC) as a co-solvent, and (3) the use of LiBOB as an electrolyte additive intended to improve the compatibility with high-voltage systems. Thus, improved safety has been provided without loss of performance in the high-voltage, high-energy system.

Pregnant Women's perceptions of exposure to brominated flame retardants.

PubMed

Lane, A; Goodyer, C G; Rab, F; Ashley, J M; Sharma, S; Hodgson, A; Nisker, J

2016-12-01

Recent media reports on human studies associating brominated flame retardants (BFRs) in household products in pregnancy with urogenital anomalies in boys and endocrine disruption in both sexes. We sought to explore the perceptions of pregnant women of brominated flame retardant (BFR) exposure, in light of recent media reports on the adverse health effects of BFR exposure prenatally. Pregnant women were recruited for interviews through posters and pamphlets in prenatal clinics, prenatal fairs and community centres. Interviews were audiotaped and transcribed verbatim for Charmaz-based qualitative analysis supported by NVIVO 10™. Theoretical sufficiency was reached after analyzing the interviews of 23 pregnant women. Themes co-constructed were: I-Lack of Awareness of BFRs; II-Factors Influencing BFR Exposure; III-Responsibility; IV-Informed Choice. Almost all participants felt it was difficult to make informed choices to avoid BFRs, and wanted communication from clinicians and regulation from governments regarding decreasing BFR exposure. Pregnant women in Canada may be unaware of the potential risks of exposure to BFRs. Professional organizations and governments should further study risk associated with BFR exposure in pregnancy and provide educational materials for pregnant women and clinicians regarding BFR exposure.

Brominated flame retardants in the surrounding soil of two manufacturing plants in China: Occurrence, composition profiles and spatial distribution.

PubMed

Li, Wen-Long; Liu, Li-Yan; Zhang, Zi-Feng; Song, Wei-Wei; Huo, Chun-Yan; Qiao, Li-Na; Ma, Wan-Li; Li, Yi-Fan

2016-06-01

Surface soil samples were collected surrounding two brominated flame retardants (BFRs) manufacturing plants in China in August 2014 and analyzed for 23 polybrominated diphenyl ethers (PBDEs) and 8 novel brominated flame retardants (NBFRs). BDE209 and decabromodiphenylethane (DBDPE) were the predominant compounds in soil with the median levels of 1600 and 560 ng/g dw, respectively. The PBDEs profiles in soil samples were consistent with that of commercial product (comDecaBDE). The percentage contributions to total PBDEs decreased from higher to lower brominated homologues. Lower concentrations of NBFRs (excluding DBDPE) were detected in soil surrounding the two plants, suggesting they are byproducts or degradation products of the manufacturing activities. The concentrations of most BFRs dropped exponentially within 3-5 km of the manufacturing plants, suggesting recent deposition of these compounds to the soil. Directional distribution indicated that PBDEs and DBDPE concentrations were highest in the north direction of Plants 1. Three-day air parcel forward trajectories confirmed that the air parcel was responsible for the higher concentration of BFRs in the soil of north direction of the plant. Copyright © 2016 Elsevier Ltd. All rights reserved.

Dermal uptake and percutaneous penetration of ten flame retardants in a human skin ex vivo model.

PubMed

Frederiksen, Marie; Vorkamp, Katrin; Jensen, Niels Martin; Sørensen, Jens Ahm; Knudsen, Lisbeth E; Sørensen, Lars S; Webster, Thomas F; Nielsen, Jesper B

2016-11-01

The dermal uptake and percutaneous penetration of ten organic flame retardants was measured using an ex vivo human skin model. The studied compounds were DBDPE, BTBPE, TBP-DBPE, EH-TBB, BEH-TEBP, α, β and γ-HBCDD as well as syn- and anti-DDC-CO. Little or none of the applied flame retardants was recovered in either type of the receptor fluids used (physiological and worst-case). However, significant fractions were recovered in the skin depot, particularly in the upper skin layers. The primary effect of the worst-case receptor fluid was deeper penetration into the skin. The recovered mass was used to calculate lower- and upper-bound permeability coefficients kp. Despite large structural variation between the studied compounds, a clear, significant decreasing trend of kp was observed with increasing log Kow. The results indicate that the dermis may provide a significant barrier for these highly lipophilic compounds. However, based on our results, dermal uptake should be considered in exposure assessments, though it may proceed in a time-lagged manner compared to less hydrophobic compounds. Copyright © 2016 Elsevier Ltd. All rights reserved.

Novel brominated flame retardants and dechloranes in three fish species from the St. Lawrence River, Canada.

PubMed

Houde, Magali; Berryman, David; de Lafontaine, Yves; Verreault, Jonathan

2014-05-01

Restrictions in the utilization of polybrominated diphenyl ether (PBDE) mixtures have led to the increased usage of alternative flame retardant additives in a wide range of commercial applications. The present study examined the occurrence of established and emerging flame retardants (FRs) in fish from a densely-populated urbanized sector of the St. Lawrence River (Montreal, Quebec, Canada). Thirty-eight PBDE congeners and sixteen emerging FRs were determined in fish belonging to three predatory species (yellow perch, northern pike, and muskellunge). The ∑PBDE in fish were up to 24,115 ng/g lipid weight (l.w.) in the apex predator muskellunge. Twelve emerging FRs including bis(2-ethylhexyl)-tetrabromophthalate (BEHTBP), pentabromoethylbenzene (PBEB), Dechlorane Plus (anti and syn), dechloranes (Dec) 602, Dec 604, Dec 604 Compound B (Dec 604 CB), and Chlordene Plus (CP) were detected (>0.01 ng/gl.w.) in the liver of muskellunge and northern pike but not in yellow perch homogenates. This is the first report of Dec 604 CB in any fish species. The bioavailability of these FRs in human-impacted aquatic ecosystems warrants further environmental assessment and toxicity testing. Crown Copyright © 2014. Published by Elsevier B.V. All rights reserved.

Occurrence of halogenated flame retardants in commercial seafood species available in European markets.

PubMed

Aznar-Alemany, Òscar; Trabalón, Laura; Jacobs, Silke; Barbosa, Vera Liane; Tejedor, Margarita Fernández; Granby, Kit; Kwadijk, Christiaan; Cunha, Sara C; Ferrari, Federico; Vandermeersch, Griet; Sioen, Isabelle; Verbeke, Wim; Vilavert, Lolita; Domingo, José L; Eljarrat, Ethel; Barceló, Damià

2017-06-01

PBDEs (congeners 28, 47, 99, 100, 153, 154, 183, 209), HBCD (α, β, γ), emerging brominated flame retardants (PBEB, HBB and DBDPE), dechloranes (Dec 602, 603, 604, syn- and anti-DP), TBBPA, 2,4,6-TBP and MeO-PBDEs (8 congeners) were analysed in commercial seafood samples from European countries. Levels were similar to literature and above the environmental quality standards (EQS) limit of the Directive 2013/39/EU for PBDEs. Contaminants were found in 90.5% of the seafood samples at n. d.-356 ng/g lw (n. d.-41.1 ng/g ww). DBDPE was not detected and 2,4,6-TBP was detected only in mussels, but at levels comparable to those of PBDEs. Mussel and seabream were the most contaminated species and the Mediterranean Sea (FAO Fishing Area 37) was the most contaminated location. The risk assessment revealed that there was no health risk related to the exposure to brominated flame retardants via seafood consumption. However, a refined risk assessment for BDE-99 is of interest in the future. Moreover, the cooking process concentrated PBDEs and HBB. Copyright © 2016 Elsevier Ltd. All rights reserved.

Evaluation of the Epoxy/Antimony Trioxide Nanocomposites as Flame Retardant

NASA Astrophysics Data System (ADS)

Dheyaa, Balqees M.; Jassim, Widad H.; Hameed, Noor A.

2018-05-01

Antimony trioxide nanopowder was added for epoxy resin in various amount weight percentages (0, 2, 4, 6, 8, and 10) wt% to increase the combustion resistance and decrease the flammability for it. The study included three standard tests used to measure: limiting oxygen index (LOI), rate of burning (R.B), burning extent (E.B), burning time (T.B), maximum flame height (H) and residue percentage after burning in order to determine the effectiveness of the used additives to decrease the flammability of epoxy resin and increase the combustion resistance. Thermal test was done by using Lee’s disk to measure the thermal conductivity coefficient. The thermal stability and degradation kinetics of epoxy resin without reinforcement and with reinforcement by (10 wt%) were studied by using thermogravimetric analysis (TGA). The recorded results indicated that epoxy reinforced by (10 wt%) has a good effect as flame retardants for epoxy resin and active to inhibit burning and reduce the flammability.

Improving Fire Resistance of Cotton Fabric through Layer-by-Layer Assembled Graphene Multilayer Nanocoating

NASA Astrophysics Data System (ADS)

Jang, Wonjun; Chung, Il Jun; Kim, Junwoo; Seo, Seongmin; Park, Yong Tae; Choi, Kyungwho

2018-05-01

In this study, thin films containing poly(vinyl alcohol) (PVA) and graphene nanoplatelets (GNPs), stabilized with poly(4-styrene-sulfonic acid) (PSS), were assembled by a simple and cost-effective layer-by-layer (LbL) technique in order to introduce the anti-flammability to cotton. These antiflammable layers were characterized by using UV-vis spectrometry and quartz crystal microbalance as a function of the number of bilayers deposited. Scanning electron microscopy was used to visualize the morphology of the thin film coatings on the cotton fabric. The graphene-polymer thin films introduced anti-flammable properties through thermally stable carbonaceous layers at a high temperature. The thermal stability and flame retardant property of graphene-coated cotton was demonstrated by thermogravimetric analysis, cone calorimetry, and vertical flame test. The results indicate that LbL-assembled graphene-polymer thin films can be applied largely in the field of flame retardant.

Intumescent all-polymer multilayer nanocoating capable of extinguishing flame on fabric

USDA-ARS?s Scientific Manuscript database

Cotton fabric was treated with flame-retardant coatings composed of poly (sodium phosphate), PSP, which acts as the acid source, and poly (allylamine), PAAm, which is used as the blowing agent, prepared via layer-by-layer (LbL) assembly. By applying these thin coating on fabric, after-glow is elimi...

Novel chemical synthesis and characterization of copper pyrovanadate nanoparticles and its influence on the flame retardancy of polymeric nanocomposites

NASA Astrophysics Data System (ADS)

Ghiyasiyan-Arani, Maryam; Masjedi-Arani, Maryam; Ghanbari, Davood; Bagheri, Samira; Salavati-Niasari, Masoud

2016-05-01

In this work, copper pyrovanadate (Cu3V2O7(OH)2(H2O)2) nanoparticles have been synthesized by a simple and rapid chemical precipitation method. Different copper-organic complexes were used to control the size and morphology of products. The morphology and structure of the as-synthesized products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR) spectrum, electron dispersive X-ray spectroscopy (EDX), thermal gravimetric analysis (TGA), differential thermal analysis (DTA) and photoluminescence (PL) spectroscopy. The influence of copper pyrovanadate nanostructures on the flame retardancy of the polystyrene, poly vinyl alcohol and cellulose acetate was studied. Dispersed nanoparticles play the role of a magnetic barrier layer, which slows down product volatilization and prevents the flame and oxygen from the sample during decomposition of the polymer. Cu3V2O7(OH)2(H2O)2 is converted to Cu3V2O8 with an endothermic reaction which simultaneously releases water and decrease the temperature of the flame region.

Flame Suppression of Cotton with Polymer-Clay Thin Film Assemblies

NASA Astrophysics Data System (ADS)

Sukhonosova, Galina; Li, Yu-Chin; Grunlan, Jaime

2010-03-01

Cotton fabric was treated with flame-retardant coatings composed of branched polyethylenimine (PEI) and montmorillonite (MMT), prepared via layer-by-layer (LbL) assembly. Four coatings were created with solutions of BPEI (pH 7 or 10) and MMT (0.2 or 1 wt. %). The thickness and composition of the coatings were studied by ellipsometry and quartz crystal microbalance. PEI at pH 10 produces the thickest films. Each coating recipe was evaluated at 5 and 20 bilayers. Thermogravimetric analysis showed that coated fabrics left 13 % char after heating at 500 C, over an order of magnitude more char than from uncoated fabric, with less than 4% coming from the coating itself. Coating reduced afterglow time by 9 seconds in vertical flame tests. Post-burn chars of coated fabrics were examined by scanning electron microscopy, revealing that weave structure and fiber shape in all coated fabrics were preserved through burning. This is the first study of its kind to use layer-by-layer assembly to generate a flame retardant coating on a complex substrate like cotton fabric.

Measurements in flame retardant textiles and protective clothing using an instrumented

NASA Astrophysics Data System (ADS)

Kort-Kamp, V. M.; Santos, A. M.; Azevedo, A. F.; Lima, R. M. V.; Bittencourt, E.

2018-03-01

The flame test manikin system can be used to evaluate the performance of thermal protective clothing under fire simulation conditions. Different weights of thermal protective garments were tested and the total clothed burn injury area decreased as the fabric weight increased. In addition, a comparison of different compositions for the same weight was analyzed too.

Brominated and organophosphate flame retardants in indoor dust of Jeddah, Kingdom of Saudi Arabia: Implications for human exposure.

PubMed

Ali, Nadeem; Eqani, Syed Ali Musstjab Akber Shah; Ismail, Iqbal Mohammad Ibrahim; Malarvannan, Govindan; Kadi, Mohammad W; Albar, Hussain Mohammed Salem; Rehan, Mohammad; Covaci, Adrian

2016-11-01

Different flame retardants (FRs) namely polybrominated diphenyl ethers (PBDEs), emerging brominated/chlorinated flame retardants (Br/Cl FRs), and organophosphate FRs (OPFRs) were analyzed in cars, air conditioner (AC) filters and floor dust of different households from Jeddah, Kingdom of Saudi Arabia (KSA). To the best of our knowledge, this is first study in literature reporting emerging Br/Cl FRs and OPFRs in AC filter dust and also first to report on their occurrence in dust from KSA. Chlorinated alkyl phosphate, penta-BDEs, BDE-209, and decabromodiphenylethane (DBDPE) were the major chemicals in dust samples from all microenvironments. ΣOPFRs occurred at median concentrations (ng/g dust) of 15,400, 10,500, and 3750 in AC filter, car and house floor dust, respectively. For all analyzed chemicals, relatively lower levels were observed in floor dust than car and AC filter dust. The profiles of FRs in car dust were different from AC filter and floor dust, which reflected their wider application as FR and plasticizer in variety of household and commercial products. For toddlers, assuming high dust intake and 95th percentile concentrations, the computed exposure estimation for BDE-99 was higher than RfD values. Copyright © 2016 Elsevier B.V. All rights reserved.

New halogenated flame retardants in the atmosphere of nine urban areas in China: Pollution characteristics, source analysis and variation trends.

PubMed

Li, Qilu; Yang, Kong; Li, Kechang; Liu, Xin; Chen, Duohong; Li, Jun; Zhang, Gan

2017-05-01

Since the ban of polybrominated diphenyl ethers (PBDEs) excluding deca-BDE in China, new halogenated flame retardants (NHFRs), such as new brominated flame retardants and Dechlorane Plus, have become widely used. In this study, we assessed the atmospheric gaseous and particulate levels of eight NHFRs in nine urban areas in China. We detected high mean atmospheric (vapour plus particle phases) concentrations of tetrabromophthalate (TBPH) (74.8 pg m -3 ) and decabromodiphenyl ethane (DBDPE) (68.8 pg m -3 ), two major NHFRs. Most of the gaseous and particulate NHFR concentrations presented seasonal variations (from summer to autumn), possibly driven by temperature. Spatially, concentrations and patterns of the NHFRs differed among the nine cities. Significantly higher concentrations were detected in cities with higher gross domestic products. The composition, especially the DBDPE/TBPH ratio (S), were clearly different among the cities, which pattern in each city are likely driven by variations in the type of industries operating in each city. Based on the temporal analysis of other researches and our data, PBDE levels have decreased markedly, while NHFRs levels have increased. Since high NHFR levels had detrimental effects on public health, NHFRs research warrants more attention. Copyright © 2017 Elsevier Ltd. All rights reserved.

The effect of brominated flame retardants on neurotransmitter uptake into rat brain synaptosomes and vesicles.

PubMed

Mariussen, Espen; Fonnum, Frode

2003-01-01

The environmental levels of brominated flame retardants (BFRs) are increasing, but little is known about their toxic effects. In this paper, we show that some of the most important BFRs in commercial use today, have a neurotoxicological potential. Hexabromocyclododecane (HBCD) and tetrabromobisphenol-A (TBBPA) inhibit plasma membrane uptake of the neurotransmitters dopamine, glutamate and gamma-amino-n-butyric acid (GABA) at a concentration level similar to what previously found for polychlorinated biphenyls (PCBs) and even for ecstasy. The IC(50) value for HBCD on dopamine uptake was 4 microM, and the IC(50) values for TBBPA were 9, 6 and 16 microM for dopamine, glutamate and GABA, respectively. HBCD also inhibited glutamate uptake at low concentrations, but never achieved more than 50% inhibition. The inhibition was primarily due to their effect on the membrane potential, measured by the membrane potential marker tetraphenylphosphonium bromide (TPP(+)). Other brominated flame retardants such as octaBDE and decaBDE did not have any effects on uptake. TBBPA, HBCD and even the pentabrominated diphenylether mixture (pentaBDE, DE-71, Great Lakes) also inhibited the vesicular uptake of dopamine with an IC(50) value of 3, 3 and 8 microM, respectively. The neurotoxicological consequences of these findings for environmental contaminants such as BFRs and PCBs are discussed.

Levels and distribution of brominated flame retardants in the soil of Harbin in China.

PubMed

Wang, Xu; Ren, Nanqi; Qi, Hong; Ma, Wanli; Li, Yifan

2009-01-01

This study reports the presence of brominated flame retardants in the topsoil in and around Harbin, a city in northeastern China. Samples of soil were collected from 17 locations in 2006, and the levels of 9 polybrominated diphenylethers (PBDEs 17, 28, 47, 66, 99, 100, 153, 154, and 183) ranged from 2.45 to 55.9 pg/g dry weight (dw) with a mean of 26.3 pg/g dw. These levels are very low comparing with those for some cities in Europe and USA. BDE 209 and hexabromocyclododecane were the two dominant congeners, with mean concentrations of 520 pg/g dw and 1750 pg/g dw, respectively. The concentrations of the total nine PBDE congeners clearly decreased from urban areas to background, but the compositions of individual congeners differed. Proportions of heavier congeners decreased while those of lighter congeners increased, along urban-rural-background transect, providing evidence for an urban fractionation effect. Correlation analysis indicated similar sources for PBDEs, hexabromocyclododecane, and 1,2-bis(2,4,6-tribromophenoxy)-ethane from urban areas but pentabromoethylbenzene was probably present due to long-range atmospheric transport. Principal component analysis was used to determine the characteristics of the relationships among these brominated flame retardants in the field.

Assessing oestrogenic effects of brominated flame retardants hexabromocyclododecane and tetrabromobisphenol A on MCF-7 cells.

PubMed

Dorosh, A; Děd, L; Elzeinová, F; Pěknicová, J

2011-01-01

Tetrabromobisphenol A (TBBPA) is the main flame retardant used in printed circuit boards and laminates. The human population is highly exposed to TBBPA as it is used in consumer electronics as well as office and communication equipment. The main use of hexabromocyclododecane (HBCD) is in insulation foam boards, which are widely used in the construction sector. Brominated flame retardants may possess endocrine disrupting activity and thus represent a threat to the environment, including humans and their reproduction. The aim of this work was to evaluate the oestrogenic effects of TBBPA and HBCD in vitro on MCF-7 cells. We used the proliferation test (E-screen assay) in MCF-7 breast cancer cells and reverse transcription quantitative polymerase chain reaction analysis of TFF1 gene expression to analyse oestrogenicity of the studied compounds. RT-qPCR has proved to be a fast and valuable molecular technique in gene expression quantification. HBCD but not TBBPA increased cell proliferation in MCF-7 cells and up-regulated TFF1 gene expression in a concentration-dependent manner. Anti-oestrogen ICI 182,780 inhibited up-regulation of TFF1 by HBCD. We have shown that HBCD displays oestrogen- like effects on MCF-7 cells. TBBPA, on the other hand, has not shown any oestrogenic effect mediated by the oestrogen receptor α.

Flame retardant and hydrophobic properties of novel sol-gel derived phytic acid/silica hybrid organic-inorganic coatings for silk fabric

NASA Astrophysics Data System (ADS)

Cheng, Xian-Wei; Liang, Cheng-Xi; Guan, Jin-Ping; Yang, Xu-Hong; Tang, Ren-Cheng

2018-01-01

In this work, a novel phosphorus-rich hybrid organic-inorganic silica coating for improving the flame retardancy of silk fabric was prepared using naturally occurring phytic acid as phosphorus precursor and catalyst for the hydrolysis of tetraethoxysilane. In addition, three silane coupling agents, namely 3-aminopropyldimethoxymethylsilane, 3-chloropropyltrimethoxysilane and 3-methacryloxypropyltrimethoxysilane, were added in the hybrid sol as cross-linkers with the aim of developing hydrophobic coatings and improving the washing durability of the treated silk fabric. The condensation degree of the hybrid sol was characterized by solid-state 29Si nuclear magnetic resonance spectroscopy. The flammability and thermal degradation properties of the treated silk fabrics were determined in terms of limiting oxygen index, vertical burning, pyrolysis combustion flow calorimetry and thermogravimetric analyses. The surface morphology and hydrophobicity of the treated silk fabrics were evaluated by scanning electron microscopy, atomic force microscopy and water contact angle tests. The flammability tests revealed that the silicon sol could endow silk fabric with excellent flame retardancy when doped with phytic acid, and the treated silk fabrics self-extinguished immediately when the ignition source was removed. The silk fabrics treated with the modified hybrid sols exhibited hydrophobic surface and also better durability to washing.

Solidifying process and flame retardancy of epoxy resin cured with boron-containing phenolic resin

NASA Astrophysics Data System (ADS)

Deng, Peng; Shi, Yan; Liu, Yuansen; Liu, Yuan; Wang, Qi

2018-01-01

For the sake of improving the charring performance and flame retardancy of epoxy resin (EP), boron-containing phenolic resin (BPR) instead of a conventional curing agent, linear phenolic resin (LPR) was employed to cure EP. Of several possible chemical structures for BPR, the existence of benzyl hydroxy groups in BPR chains has been confirmed using 1H nuclear magnetic resonance spectroscopy. The resonance of these groups may reasonably explain the higher curing reactivity of BPR-cured EP than that of LPR-cured EP. Thermogravimetric analysis, observation of the morphologies of the char residues and X-ray photoelectron spectroscopic were performed to characterize the charring process. Due to the presence of B2O3 produced on the char surface from decomposition of phenyl borates and the facile high self-crosslinking reaction of BPR, a more continuous and stronger char barrier was formed for BPR-cured EP compared to that for the LPR-cured EP system. Therefore the former exhibited much better flame retardancy. In addition, BPR-cured EP also displayed better dynamic mechanical properties, than those observed for LPR-cured EP. It is not subject to the significant lowering the glass transition temperature of the polymer which accompanies curing with LPR. This suggests that BPR cured resin may meet the requirement for utilization at high temperature.

Evaluation of in vitro vs. in vivo methods for assessment of dermal absorption of organic flame retardants: a review.

PubMed

Abdallah, Mohamed Abou-Elwafa; Pawar, Gopal; Harrad, Stuart

2015-01-01

There is a growing interest to study human dermal exposure to a large number of chemicals, whether in the indoor or outdoor environment. Such studies are essential to predict the systemic exposure to xenobiotic chemicals for risk assessment purposes and to comply with various regulatory guidelines. However, very little is currently known about human dermal exposure to persistent organic pollutants. While recent pharmacokinetic studies have highlighted the importance of dermal contact as a pathway of human exposure to brominated flame retardants, risk assessment studies had to apply assumed values for percutaneous penetration of various flame retardants (FRs) due to complete absence of specific experimental data on their human dermal bioavailability. Therefore, this article discusses the current state-of-knowledge on the significance of dermal contact as a pathway of human exposure to FRs. The available literature on in vivo and in vitro methods for assessment of dermal absorption of FRs in human and laboratory animals is critically reviewed. Finally, a novel approach for studying human dermal absorption of FRs using in vitro three-dimensional (3D) human skin equivalent models is presented and the challenges facing future dermal absorption studies on FRs are highlighted. Copyright © 2014 Elsevier Ltd. All rights reserved.

Hair and Nails as Noninvasive Biomarkers of Human Exposure to Brominated and Organophosphate Flame Retardants.

PubMed

Liu, Liang-Ying; He, Ka; Hites, Ronald A; Salamova, Amina

2016-03-15

After the phase-out of polybrominated diphenyl ethers (PBDEs), the use of alternative flame retardants (AFRs), such as FireMaster 550, and of organophosphate esters (OPEs) has increased. However, little is known about human exposure to these chemicals. This lack of biomonitoring studies is partially due to the absence of reliable noninvasive biomarkers of exposure. Human hair and nails can provide integrated exposure measurements, and as such, these matrices can potentially be used as noninvasive biomarkers of exposure to these flame retardants. Paired human hair, fingernail, toenail, and serum samples obtained from 50 adult participants recruited at Indiana University Bloomington campus were analyzed by gas chromatographic mass spectrometry for 36 PBDEs, 9 AFRs, and 12 OPEs. BDE-47, BDE-99, 2-ethylhexyl-2,3,4,5-tetrabromobenzoate (TBB), di(2-ethylhexyl) tetrabromophthalate (TBPH), tris(1,3-dichloro-2-propyl)phosphate (TDCIPP), and triphenyl phosphate (TPHP) were the most abundant compounds detected in almost all hair, fingernail, and toenail samples. The concentrations followed the order OPEs > TBB+TBPH > Σpenta-BDE. PBDE levels in the hair and nail samples were significantly correlated with their levels in serum (P < 0.05), suggesting that human hair and nails can be used as biomarkers to assess human exposure to PBDEs.

Fire retardancy assessment of polypropylene composite filed with nano clay prepared from Iraqi bentonite

NASA Astrophysics Data System (ADS)

Kareem Salih, Watheq

2018-05-01

Fire retardants have an extraordinary importance because of their role in saving the people, property and reducing the damages and minimizing the dangers resulting from fires and burning of polymeric composites which are used in different civil and industrial fields. The work in this paper can be divided into two main stages. In first one nano-clay was manufactured from Iraqi bentonite and it was characterized using AFM, XRD, XRF, SEM, and BET. The AFM test showed the particle size of prepared nano clay was about 99.25 nm. In the second stage, polypropylene/nano clay composites at three low loading percents (0%,2%,4%,6%) were formulated via twin screw extruder. The fire retardancy tests included burning rate according to ASTM:D-635 and maximum flame height of flame according to ASTM:D-3014. Besides, the mechanical tests and thermal behavior of prepared samples were investigated. The results showed that (4%) of nano-clay had the maximum fire retardancy and while at (2%) loading, the maximum value of tensile strength and Yong modulus were obtained. The maximum heat of fusion was recorded for 6% nano clay sample. The final results assessment confirmed on the possibility of using low loadings of prepared nano clay to improve the fire retardancy, mechanical and thermal properties successfully.

Oxygen index evaluation of fire-retardant-treated wood

Treesearch

Robert H. White

1979-01-01

The applicability of using the oxygen index test (ASTM D 2863-76) to obtain an indication of the relative flammability of fire-retardant- treated wood products was investigated. The oxygen index is the minimum percentage oxygen that is required to maintain flaming combustion of a specimen under specified laboratory conditions. Within the plastics industry, the test is...

Cone calorimeter evaluation of wood products

Treesearch

Robert H. White; Mark A. Dietenberger

2004-01-01

The Forest Products Laboratory uses the cone calorimeter for the initial evaluation of the flammability of untreated and fire retardant treated wood products. The results of various studies are reviewed using a model presented at the 12th Annual BBC Conference on Flame Retardancy. The model uses data from the cone calorimeter to provide measures of fire growth...

Environmental concentration and atmospheric deposition of halogenated flame retardants in soil from Nepal: Source apportionment and soil-air partitioning.

PubMed

Yadav, Ishwar Chandra; Devi, Ningombam Linthoingambi; Li, Jun; Zhang, Gan

2018-02-01

While various investigations have been driven on polybrominated diphenyl ethers (PBDEs) and other flame retardants (FRs) in different framework around the world, information about contamination and fate of PBDEs and other FRs in developing countries especially in the Indian subcontinent is uncommon. Nepal being located in the Indian subcontinent, very little is known about contamination level of semi-volatile organic pollutants discharged into the environment. This motivated us to investigate the environmental fate of halogenated flame retardant (HFRs) in Nepalese condition. In this study, we investigated the concentration, fate, and sources of 9 PBDEs, 2 dechlorane plus isomers (DPs), and 6 novel brominated flame retardants (NBFRs). Moreover, air-soil exchange and soil-air partitioning were also evaluated to characterize the pattern of air-soil exchange and environmental fate. In general, the concentrations of NBFRs in soil were more prevalent than PBDEs and DPs, and accounted 95% of ∑HFRs. By and large, the concentrations of NBFRs and DPs were measured high in Kathmandu, while PBDEs level exceeded in Pokhara. Principal component analysis (PCA) study suggested contributions from commercial penta-, octa-, and deca-BDEs products and de-bromination of highly brominated PBDEs as the significant source of PBDEs. Likewise, low f anti ratio suggested DPs in soil might have originated from long-range atmospheric transport from remote areas, while high levels of decabromodiphenyl ethane (DBDPE) in soil were linked with the use of wide varieties of consumer products. The estimated fugacity fraction (ff) for individual HFR was quite lower (<0.05) than equilibrium value, suggesting that deposition and net transport from air to the soil is overwhelming. Soil-air partitioning study revealed neither octanol-air partition coefficient (K OA ) nor black carbon partition coefficient (K BC-A ) is an appropriate surrogate for soil organic matter (SOM), subsequently, absorption by SOM has no or little role in the partitioning of HFRs. Copyright © 2017 Elsevier Ltd. All rights reserved.

Polybrominated diphenyl ethers (PBDEs), hexabromocyclododecane (HBCD) and "novel" brominated flame retardants in house dust in Germany.

PubMed

Fromme, H; Hilger, B; Kopp, E; Miserok, M; Völkel, W

2014-03-01

Brominated flame retardants (BFRs) are used in a wide variety of products such as electronic devices, upholstery and carpets and in insulation boards. The study presented here aimed to quantify the amounts of BFRs in house dust in Germany. For this purpose 20 residences' dust samples were collected from vacuum cleaner bags and analysed with LC-MS/MS and simultaneously with GC/MS. Using GC/MS, the median (95th percentile) concentrations of PBDEs (sum of tetra- to hepta-congeners), BDE 209, Σ-HBCD (sum of three congeners), and decabromodiphenylethane (DBDPE) were 42ng/g (230ng/g), 950ng/g (3426ng/g), 335ng/g (1545ng/g), and 146ng/g (1059ng/g), respectively. Using LC-MS/MS some "novel" flame retardants were found in median concentrations of 343ng/g (bis(2-ethyl-1-hexyl)tetrabromophthalate, TBPH), and 28ng/g (tetrabromobisphenol A, TBBPA). Whilst 1,2-bis-(2,4,6-tribromophenoxy)ethane (BTBPE) and 2-ethyl-1-hexyl-2,3,4,5-tetrabromobenzoate (EH-TBB) could not be detected. Based on these measurements an exposure assessment for the sum of tetra- to heptabrominated congeners, BDE 209, and Σ-HBCD resulted in a "high" daily intake for toddlers (based on 95th percentiles) of 1.2ng/kg b.w., 0.69ng/kg b.w., and 8.9ng/kg b.w., respectively. For TBPH the "high" intake was calculated at 4.1ng/kg b.w. and for DBDPE at 5.3ng/kg b.w. A clear tendency was observed to apply "novel" BFRs in Germany. Moreover, the results suggest that the recent exposure to PBDEs and HBCD via house dust in Germany is well below the levels that are associated with health effects. For the "novel" brominated flame retardants such an assessment is not possible due to limited toxicological information. Copyright © 2013 Elsevier Ltd. All rights reserved.

Occurrence of PBDEs and other alternative brominated flame retardants in sludge from wastewater treatment plants in Korea.

PubMed

Lee, Sunggyu; Song, Geum-Ju; Kannan, Kurunthachalam; Moon, Hyo-Bang

2014-02-01

Studies on the occurrence of polybrominated diphenyl ethers (PBDEs) and other alternative brominated flame retardants in the environment are scarce. In this study, PBDEs and non-PBDE brominated flame retardants (NBFRs), including decabromodiphenyl ethane (DBDPE) and 1,2-bis(2,4,6-tribromophenoxy)ethane (BTBPE), were measured in sludge collected from three types of wastewater treatment plants (WWTPs) in Korea. Total concentrations of PBDEs (∑PBDE) in sludge ranged from 298 to 48,000 (mean: 3240) ng/g dry weight. Among 10 NBFRs analyzed, DBDPE and BTBPE were the only ones detected in sludge samples. Concentrations of DBDPE and BTBPE ranged from 1) of DBDPE/BDE 209 were found in sludge from I-WWTPs, reflecting a shift in the usage pattern of BFRs by the Korean industry. The nationwide annual emission fluxes of ∑PBDE, DBDPE and BTBPE via WWTPs to the environment were estimated to be 7400, 480, and 3.7 kg/year, respectively. This is the first study on the occurrence of alternative brominated flame retardants in sludge from Korea. © 2013 Elsevier B.V. All rights reserved.

Occurrence and human exposure to brominated and organophosphorus flame retardants via indoor dust in a Brazilian city.

PubMed

Cristale, Joyce; Aragão Belé, Tiago Gomes; Lacorte, Silvia; Rodrigues de Marchi, Mary Rosa

2018-06-01

Indoor dust is considered an important human exposure route to flame retardants (FRs), which has arised concern due the toxic properties of some of these substances. In this study, ten organophosphorus flame retardants (OPFRs), eight polybrominated diphenyl ethers (PBDEs) and four new brominated flame retardants (NBFRs) were determined in indoor dust from different places in Araraquara-SP (Brazil). The sampled places included houses, apartments, offices, primary schools and cars. The analysis of the sample extracts was performed by gas chromatography coupled to mass spectrometry and two ionization techniques were used (electron ionization - EI; electron capture negative ionization - ECNI). OPFRs were the most abundant compounds and tris(2-butoxyethyl) phosphate (TBOEP), tris(phenyl) phosphate (TPHP), tris(1,3-dichloroisopropyl) phosphate (TDCIPP) and tris(2-chloroisopropyl) phosphate (TCIPP) were present at the highest concentrations. Among the brominated FRs, the most ubiquitous compounds were BDE-209, bis(2-ethylhexyl) tetrabromophthalate (BEH-TEBP) and decabromodiphenyl ethane (DBDPE). Statistical analysis revealed that there were differences among dust typologies for TBOEP, TDCIPP, ethylhexyl diphenyl phosphate (EHDPHP), BDE-209, 2-ethylhexyl 2,3,4,5-tetrabromobenzoate (EH-TBB), BEH-TEBP and DBDPE, which were attributed to different construction materials in each particular environment and to the age of the buildings. The highest levels of brominated FRs were observed in offices, TBOEP was at high concentration in primary schools, and TDCIPP was at high concentration in cars. A preliminary risk assessment revealed that toddlers were exposed to TBOEP levels higher than the reference dose when considering the worst case scenario. The results obtained in this study showed for the first time that although Brazil does not regulate the use of FRs, these substances are present in indoor dust at levels similar to the observed in countries that have strict fire safety standards, and that humans are exposed to complex mixtures of these contaminants via indoor dust. Copyright © 2017 Elsevier Ltd. All rights reserved.

Brominated and phosphate flame retardants (FRs) in indoor dust from different microenvironments: Implications for human exposure via dust ingestion and dermal contact.

PubMed

Zheng, Xiaobo; Qiao, Lin; Covaci, Adrian; Sun, Runxia; Guo, Huiying; Zheng, Jing; Luo, Xiaojun; Xie, Qilai; Mai, Bixian

2017-10-01

Indoor dust has been widely used to monitor flame retardants (FRs) in indoor environment, but most studies only focused on floor dust. In the present study, FRs were examined in indoor dust from different locations. Dust from air conditioner (AC) filters, beddings, floor, and windows in bedrooms, and dust from AC filters, printer table surface, computer table surface, floor, and windows in offices were collected, respectively. Polybrominated diphenyl ether congener 209 (BDE 209) and decabromodiphenyl ethane (DBDPE) were the most abundant brominated flame retardants (BFRs), and tris(chloroisopropyl) phosphate (TCIPP), tris(1,3-dichloroisopropyl) phosphate (TDCIPP), and triphenyl phosphate (TPHP) were the most abundant phosphate flame retardants (PFRs). In bedrooms, the AC filter dust had the highest median levels of BDE 209 (536 ng/g) and DBDPE (2720 ng/g), while bed dust had the highest median levels of ΣPFRs (2750 ng/g) among dust samples. In offices, printer table dust had higher median levels of BDE 209 (1330 ng/g), DBDPE (8470 ng/g), and ΣPFRs (11,000 ng/g) than those in other dust samples. The high dust ingestion values of BDE 209, DBDPE, and individual PFR were 0.28, 1.20, and <0.01-0.32 ng/kg bw/day and 7.37, 31.2, and <0.01-4.54 ng/kg bw/day for BDE 209, DBDPE, and individual PFR for adults and toddlers, respectively. The high dermal exposure values of individual PFR during sleeping were <0.01-0.23 and <0.01-0.36 ng/kg bw/day for adults and toddlers, respectively. More human exposure pathways other than dust ingestion should be considered, such as the dermal contact with beddings and furniture. Copyright © 2017 Elsevier Ltd. All rights reserved.

Prenatal Exposure to Organohalogens, Including Brominated Flame Retardants, Influences Motor, Cognitive, and Behavioral Performance at School Age

PubMed Central

Roze, Elise; Meijer, Lisethe; Bakker, Attie; Van Braeckel, Koenraad N.J.A.; Sauer, Pieter J.J.; Bos, Arend F.

2009-01-01

Background Organohalogen compounds (OHCs) are known to have neurotoxic effects on the developing brain. Objective We investigated the influence of prenatal exposure to OHCs, including brominated flame retardants, on motor, cognitive, and behavioral outcome in healthy children of school age. Methods This study was part of the prospective Groningen infant COMPARE (Comparison of Exposure-Effect Pathways to Improve the Assessment of Human Health Risks of Complex Environmental Mixtures of Organohalogens) study. It included 62 children in whose mothers the following compounds had been determined in the 35th week of pregnancy: 2,2′-bis-(4 chlorophenyl)-1,1′-dichloroethene, pentachlorophenol (PCP), polychlorinated biphenyl congener 153 (PCB-153), 4-hydroxy-2,3,3′,4′,5-pentachlorobiphenyl (4OH-CB-107), 4OH-CB-146, 4OH-CB-187, 2,2′,4,4′-tetrabromodiphenyl ether (BDE-47), BDE-99, BDE-100, BDE-153, BDE-154, and hexabromocyclododecane. Thyroid hormones were determined in umbilical cord blood. When the children were 5–6 years of age, we assessed their neuropsychological functioning: motor performance (coordination, fine motor skills), cognition (intelligence, visual perception, visuomotor integration, inhibitory control, verbal memory, and attention), and behavior. Results Brominated flame retardants correlated with worse fine manipulative abilities, worse attention, better coordination, better visual perception, and better behavior. Chlorinated OHCs correlated with less choreiform dyskinesia. Hydroxylated polychlorinated biphenyls correlated with worse fine manipulative abilities, better attention, and better visual perception. The wood protective agent (PCP) correlated with worse coordination, less sensory integrity, worse attention, and worse visuomotor integration. Conclusions Our results demonstrate for the first time that transplacental transfer of polybrominated flame retardants is associated with the development of children at school age. Because of the widespread use of these compounds, especially in the United States, where concentrations in the environment are four times higher than in Europe, these results cause serious concern. PMID:20049217

Prenatal exposure to organohalogens, including brominated flame retardants, influences motor, cognitive, and behavioral performance at school age.

PubMed

Roze, Elise; Meijer, Lisethe; Bakker, Attie; Van Braeckel, Koenraad N J A; Sauer, Pieter J J; Bos, Arend F

2009-12-01

Organohalogen compounds (OHCs) are known to have neurotoxic effects on the developing brain. We investigated the influence of prenatal exposure to OHCs, including brominated flame retardants, on motor, cognitive, and behavioral outcome in healthy children of school age. This study was part of the prospective Groningen infant COMPARE (Comparison of Exposure-Effect Pathways to Improve the Assessment of Human Health Risks of Complex Environmental Mixtures of Organohalogens) study. It included 62 children in whose mothers the following compounds had been determined in the 35th week of pregnancy: 2,2'-bis-(4 chlorophenyl)-1,1'-dichloroethene, pentachlorophenol (PCP), polychlorinated biphenyl congener 153 (PCB-153), 4-hydroxy-2,3,3',4',5-pentachlorobiphenyl (4OH-CB-107), 4OH-CB-146, 4OH-CB-187, 2,2',4,4'-tetrabromodiphenyl ether (BDE-47), BDE-99, BDE-100, BDE-153, BDE-154, and hexabromocyclododecane. Thyroid hormones were determined in umbilical cord blood. When the children were 5-6 years of age, we assessed their neuropsychological functioning: motor performance (coordination, fine motor skills), cognition (intelligence, visual perception, visuomotor integration, inhibitory control, verbal memory, and attention), and behavior. Brominated flame retardants correlated with worse fine manipulative abilities, worse attention, better coordination, better visual perception, and better behavior. Chlorinated OHCs correlated with less choreiform dyskinesia. Hydroxylated polychlorinated biphenyls correlated with worse fine manipulative abilities, better attention, and better visual perception. The wood protective agent (PCP) correlated with worse coordination, less sensory integrity, worse attention, and worse visuomotor integration. Our results demonstrate for the first time that transplacental transfer of polybrominated flame retardants is associated with the development of children at school age. Because of the widespread use of these compounds, especially in the United States, where concentrations in the environment are four times higher than in Europe, these results cause serious concern.

Impact of particle size on distribution and human exposure of flame retardants in indoor dust.

PubMed

He, Rui-Wen; Li, Yun-Zi; Xiang, Ping; Li, Chao; Cui, Xin-Yi; Ma, Lena Q

2018-04-01

The effect of dust particle size on the distribution and bioaccessibility of flame retardants (FRs) in indoor dust remains unclear. In this study, we analyzed 20 FRs (including 6 organophosphate flame retardants (OPFRs), 8 polybrominated diphenyl ethers (PBDEs), 4 novel brominated flame retardants (NBFRs), and 2 dechlorane plus (DPs)) in composite dust samples from offices, public microenvironments (PME), and cars in Nanjing, China. Each composite sample (one per microenvironment) was separated into 6 size fractions (F1-F6: 200-2000µm, 150-200µm, 100-150µm, 63-100µm, 43-63µm, and <43µm). FRs concentrations were the highest in car dust, being 16 and 6 times higher than those in offices and PME. The distribution of FRs in different size fractions was Kow-dependent and affected by surface area (Log Kow=1-4), total organic carbon (Log Kow=4-9), and FR migration pathways into dust (Log Kow>9). Bioaccessibility of FRs was measured by the physiologically-based extraction test, with OPFR bioaccessibility being 1.8-82% while bioaccessible PBDEs, NBFRs, and DPs were under detection limits due to their high hydrophobicity. The OPFR bioaccessibility in 200-2000µm fraction was significantly higher than that of <43µm fraction, but with no difference among the other four fractions. Risk assessment was performed for the most abundant OPFR-tris(2-chloroethyl) phosphate. The average daily dose (ADD) values were the highest for the <43µm fraction for all three types of dust using total concentrations, but no consistent trend was found among the three types of dust if based on bioaccessible concentrations. Our results indicated that dust size impacted human exposure estimation of FRs due to their variability in distribution and bioaccessibility among different fractions. For future risk assessment, size selection for dust sampling should be standardized and bioaccessibility of FRs should not be overlooked. Copyright © 2018 Elsevier Inc. All rights reserved.

Neurobehavioral function and low-level exposure to brominated flame retardants in adolescents: a cross-sectional study.

PubMed

Kiciński, Michał; Viaene, Mineke K; Den Hond, Elly; Schoeters, Greet; Covaci, Adrian; Dirtu, Alin C; Nelen, Vera; Bruckers, Liesbeth; Croes, Kim; Sioen, Isabelle; Baeyens, Willy; Van Larebeke, Nicolas; Nawrot, Tim S

2012-11-14

Animal and in vitro studies demonstrated a neurotoxic potential of brominated flame retardants, a group of chemicals used in many household and commercial products to prevent fire. Although the first reports of detrimental neurobehavioral effects in rodents appeared more than ten years ago, human data are sparse. As a part of a biomonitoring program for environmental health surveillance in Flanders, Belgium, we assessed the neurobehavioral function with the Neurobehavioral Evaluation System (NES-3), and collected blood samples in a group of high school students. Cross-sectional data on 515 adolescents (13.6-17 years of age) was available for the analysis. Multiple regression models accounting for potential confounders were used to investigate the associations between biomarkers of internal exposure to brominated flame retardants [serum levels of polybrominated diphenyl ether (PBDE) congeners 47, 99, 100, 153, 209, hexabromocyclododecane (HBCD), and tetrabromobisphenol A (TBBPA)] and cognitive performance. In addition, we investigated the association between brominated flame retardants and serum levels of FT3, FT4, and TSH. A two-fold increase of the sum of serum PBDE's was associated with a decrease of the number of taps with the preferred-hand in the Finger Tapping test by 5.31 (95% CI: 0.56 to 10.05, p = 0.029). The effects of the individual PBDE congeners on the motor speed were consistent. Serum levels above the level of quantification were associated with an average decrease of FT3 level by 0.18 pg/mL (95% CI: 0.03 to 0.34, p = 0.020) for PBDE-99 and by 0.15 pg/mL (95% CI: 0.004 to 0.29, p = 0.045) for PBDE-100, compared with concentrations below the level of quantification. PBDE-47 level above the level of quantification was associated with an average increase of TSH levels by 10.1% (95% CI: 0.8% to 20.2%, p = 0.033), compared with concentrations below the level of quantification. We did not observe effects of PBDE's on neurobehavioral domains other than the motor function. HBCD and TBBPA did not show consistent associations with performance in the neurobehavioral tests. This study is one of few studies and so far the largest one investigating the neurobehavioral effects of brominated flame retardants in humans. Consistently with experimental animal data, PBDE exposure was associated with changes in the motor function and the serum levels of the thyroid hormones.

Lithium-Ion Electrolytes Containing Phosphorous-Based, Flame-Retardant Additives

NASA Technical Reports Server (NTRS)

Smart, Marshall C.; Smith, Kiah A.; Bugga, Ratnakumar V.; Prakash, G. K. Surya

2010-01-01

Future NASA missions aimed at exploring Mars, the Moon, and the outer planets require rechargeable batteries that can operate over a wide temperature range (-60 to +60 C) to satisfy the requirements of various applications. In addition, many of these applications will require improved safety, due to their use by humans. Currently, the state-of-the-art lithium-ion (Li-ion) system has been demonstrated to operate over a wide range of temperatures (-40 to +40 C); however, abuse conditions can often lead to cell rupture and fire. The nature of the electrolyte can greatly affect the propensity of the cell/battery to catch fire, given the flammability of the organic solvents used within. Li-ion electrolytes have been developed that contain a flame-retardant additive in conjunction with fluorinated co-solvents to provide a safe system with a wide operating temperature range. Previous work incorporated fluorinated esters into multi-component electrolyte formulations, which were demonstrated to cover a temperature range from 60 to +60 C. This work was described in Fluoroester Co-Solvents for Low-Temperature Li+ Cells (NPO-44626), NASA Tech Briefs, Vol. 33, No. 9 (September 2009), p. 37; and Optimized Li-Ion Electrolytes Con tain ing Fluorinated Ester Co-Solvents (NPO-45824), NASA Tech Briefs, Vol. 34, No. 3 (March 2010), p. 48. Other previous work improved the safety characteristics of the electrolytes by adding flame-retardant additives such as triphenyl phosphate (TPhPh), tri-butyl phosphate (TBuPh), triethyl phosphate (TEtPh), and bis(2,2,2-trifluoroethyl) methyl phosphonate (TFMPo). The current work involves further investigation of other types of flame-retardant additives, including tris(2,2,2-trifluoroethyl) phosphate, tris(2,2,2-trifluoroethyl) phosphite, triphenylphosphite, diethyl ethylphosphonate, and diethyl phenylphosphonate added to an electrolyte composition intended for wide operating temperatures. In general, many of the formulations investigated in this study displayed good performance over a wide temperature range, good cycle life characteristics, and are expected to have improved safety characteristics, such as low flammability. Of the electrolytes studied, 1.0 M LiPF6 in EC+EMC+DEP (20:75:5 v/v %) and 1.0 M LiPF6 in EC+EMC+DPP (20:75:5 v/v %) displayed the best operation at low temperatures, whereas the electrolyte containing triphenylphosphite displayed the best cycle life performance compared to the baseline solution. It is anticipated that further improvements can be made to the life characteristics with the incorporation of a SET promoters (such as VC, vinylene carbonate), which will likely inhibit the decomposition of the flame-retardant additives.

Neurobehavioral function and low-level exposure to brominated flame retardants in adolescents: a cross-sectional study

PubMed Central

2012-01-01

Background Animal and in vitro studies demonstrated a neurotoxic potential of brominated flame retardants, a group of chemicals used in many household and commercial products to prevent fire. Although the first reports of detrimental neurobehavioral effects in rodents appeared more than ten years ago, human data are sparse. Methods As a part of a biomonitoring program for environmental health surveillance in Flanders, Belgium, we assessed the neurobehavioral function with the Neurobehavioral Evaluation System (NES-3), and collected blood samples in a group of high school students. Cross-sectional data on 515 adolescents (13.6-17 years of age) was available for the analysis. Multiple regression models accounting for potential confounders were used to investigate the associations between biomarkers of internal exposure to brominated flame retardants [serum levels of polybrominated diphenyl ether (PBDE) congeners 47, 99, 100, 153, 209, hexabromocyclododecane (HBCD), and tetrabromobisphenol A (TBBPA)] and cognitive performance. In addition, we investigated the association between brominated flame retardants and serum levels of FT3, FT4, and TSH. Results A two-fold increase of the sum of serum PBDE’s was associated with a decrease of the number of taps with the preferred-hand in the Finger Tapping test by 5.31 (95% CI: 0.56 to 10.05, p = 0.029). The effects of the individual PBDE congeners on the motor speed were consistent. Serum levels above the level of quantification were associated with an average decrease of FT3 level by 0.18 pg/mL (95% CI: 0.03 to 0.34, p = 0.020) for PBDE-99 and by 0.15 pg/mL (95% CI: 0.004 to 0.29, p = 0.045) for PBDE-100, compared with concentrations below the level of quantification. PBDE-47 level above the level of quantification was associated with an average increase of TSH levels by 10.1% (95% CI: 0.8% to 20.2%, p = 0.033), compared with concentrations below the level of quantification. We did not observe effects of PBDE’s on neurobehavioral domains other than the motor function. HBCD and TBBPA did not show consistent associations with performance in the neurobehavioral tests. Conclusions This study is one of few studies and so far the largest one investigating the neurobehavioral effects of brominated flame retardants in humans. Consistently with experimental animal data, PBDE exposure was associated with changes in the motor function and the serum levels of the thyroid hormones. PMID:23151181

Flame Retardant: Cyberbullies Torment Their Victims 24/7: Here's How to Stop the Abuse

ERIC Educational Resources Information Center

Willard, Nancy

2006-01-01

Cyberbullying is the use of electronic information such as e-mail and other digital age tools to bully or harass individuals. Cyberbullies post angry and vulgar messages in online "flaming" wars or hack into a peer's e-mail account to wreak havoc, assaulting the reputations and already fragile egos of their young victims. The devastating effects…

Catalysts for polyimide foams from aromatic isocyanates and aromatic dianhydrides. [flame retardant foams

NASA Technical Reports Server (NTRS)

Riccitiello, S. R.; Sawko, P. M.; Estrella, C. A. (Inventor)

1979-01-01

Polyimide foam products having greatly improved burn-through and flame-spread resistance are prepared by the reaction of aromatic polyisocyanates with aromatic dianhydrides in the presence of metallic salts of octoic acid. The salts, for example stannous octoate, ferric octoate and aluminum octoate, favor the formation of imide linkages at the expense of other possible reactions.

Occupational exposure of air crews to tricresyl phosphate isomers and organophosphate flame retardants after fume events.

PubMed

Schindler, Birgit Karin; Weiss, Tobias; Schütze, Andre; Koslitz, Stephan; Broding, Horst Christoph; Bünger, Jürgen; Brüning, Thomas

2013-04-01

Aircraft cabin air can possibly be contaminated by tricresyl phosphates (TCP) from jet engine oils during fume events. o-TCP, a known neurotoxin, has been addressed to be an agent that might cause the symptoms reported by cabin crews after fume events. A total of 332 urine samples of pilots and cabin crew members in common passenger airplanes, who reported fume/odour during their last flight, were analysed for three isomers of tricresyl phosphate metabolites as well as dialkyl and diaryl phosphate metabolites of four flame retardants. None of the samples contained o-TCP metabolites above the limit of detection (LOD 0.5 μg/l). Only one sample contained metabolites of m- and p-tricresyl phosphates with levels near the LOD. Median metabolite levels of tributyl phosphate (TBP), tris-(2-chloroethyl) phosphate (TCEP) and triphenyl phosphate (TPP) (DBP 0.28 μg/l; BCEP 0.33 μg/l; DPP 1.1 μg/l) were found to be significantly higher than in unexposed persons from the general population. Median tris-(2-chloropropyl) phosphate (TCPP) metabolite levels were significantly not higher in air crews than in controls. Health complaints reported by air crews can hardly be addressed to o-TCP exposure in cabin air. Elevated metabolite levels for TBP, TCEP and TPP in air crews might occur due to traces of hydraulic fluid in cabin air (TBP, TPP) or due to release of commonly used flame retardants from the highly flame protected environment in the airplane. A slight occupational exposure of air crews to organophosphates was shown.

Fish DNA-modified clays: Towards highly flame retardant polymer nanocomposite with improved interfacial and mechanical performance.

PubMed

Zabihi, Omid; Ahmadi, Mojtaba; Khayyam, Hamid; Naebe, Minoo

2016-12-05

Deoxyribonucleic Acid (DNA) has been recently found to be an efficient renewable and environmentally-friendly flame retardant. In this work, for the first time, we have used waste DNA from fishing industry to modify clay structure in order to increase the clay interactions with epoxy resin and take benefit of its additional thermal property effect on thermo-physical properties of epoxy-clay nanocomposites. Intercalation of DNA within the clay layers was accomplished in a one-step approach confirmed by FT-IR, XPS, TGA, and XRD analyses, indicating that d-space of clay layers was expanded from ~1.2 nm for pristine clay to ~1.9 nm for clay modified with DNA (d-clay). Compared to epoxy nanocomposite containing 2.5%wt of Nanomer I.28E organoclay (m-clay), it was found that at 2.5%wt d-clay loading, significant enhancements of ~14%, ~6% and ~26% in tensile strength, tensile modulus, and fracture toughness of epoxy nanocomposite can be achieved, respectively. Effect of DNA as clay modifier on thermal performance of epoxy nanocomposite containing 2.5%wt d-clay was evaluated using TGA and cone calorimetry analysis, revealing significant decreases of ~4000 kJ/m 2 and ~78 kW/m 2 in total heat release and peak of heat release rate, respectively, in comparison to that containing 2.5%wt of m-clay.

Fish DNA-modified clays: Towards highly flame retardant polymer nanocomposite with improved interfacial and mechanical performance

NASA Astrophysics Data System (ADS)

Zabihi, Omid; Ahmadi, Mojtaba; Khayyam, Hamid; Naebe, Minoo

2016-12-01

Deoxyribonucleic Acid (DNA) has been recently found to be an efficient renewable and environmentally-friendly flame retardant. In this work, for the first time, we have used waste DNA from fishing industry to modify clay structure in order to increase the clay interactions with epoxy resin and take benefit of its additional thermal property effect on thermo-physical properties of epoxy-clay nanocomposites. Intercalation of DNA within the clay layers was accomplished in a one-step approach confirmed by FT-IR, XPS, TGA, and XRD analyses, indicating that d-space of clay layers was expanded from ~1.2 nm for pristine clay to ~1.9 nm for clay modified with DNA (d-clay). Compared to epoxy nanocomposite containing 2.5%wt of Nanomer I.28E organoclay (m-clay), it was found that at 2.5%wt d-clay loading, significant enhancements of ~14%, ~6% and ~26% in tensile strength, tensile modulus, and fracture toughness of epoxy nanocomposite can be achieved, respectively. Effect of DNA as clay modifier on thermal performance of epoxy nanocomposite containing 2.5%wt d-clay was evaluated using TGA and cone calorimetry analysis, revealing significant decreases of ~4000 kJ/m2 and ~78 kW/m2 in total heat release and peak of heat release rate, respectively, in comparison to that containing 2.5%wt of m-clay.

Fish DNA-modified clays: Towards highly flame retardant polymer nanocomposite with improved interfacial and mechanical performance

PubMed Central

Zabihi, Omid; Ahmadi, Mojtaba; Khayyam, Hamid; Naebe, Minoo

2016-01-01

Deoxyribonucleic Acid (DNA) has been recently found to be an efficient renewable and environmentally-friendly flame retardant. In this work, for the first time, we have used waste DNA from fishing industry to modify clay structure in order to increase the clay interactions with epoxy resin and take benefit of its additional thermal property effect on thermo-physical properties of epoxy-clay nanocomposites. Intercalation of DNA within the clay layers was accomplished in a one-step approach confirmed by FT-IR, XPS, TGA, and XRD analyses, indicating that d-space of clay layers was expanded from ~1.2 nm for pristine clay to ~1.9 nm for clay modified with DNA (d-clay). Compared to epoxy nanocomposite containing 2.5%wt of Nanomer I.28E organoclay (m-clay), it was found that at 2.5%wt d-clay loading, significant enhancements of ~14%, ~6% and ~26% in tensile strength, tensile modulus, and fracture toughness of epoxy nanocomposite can be achieved, respectively. Effect of DNA as clay modifier on thermal performance of epoxy nanocomposite containing 2.5%wt d-clay was evaluated using TGA and cone calorimetry analysis, revealing significant decreases of ~4000 kJ/m2 and ~78 kW/m2 in total heat release and peak of heat release rate, respectively, in comparison to that containing 2.5%wt of m-clay. PMID:27917901

Brominated Flame Retardants in Sediments of Four Coastal Lagoons of Yucatan, Mexico.

PubMed

Valenzuela-Sánchez, I S; Gold-Bouchot, G; Hernández-Núñez, E; Barrientos-Medina, R C; Garza-Gisholt, E; Zapata-Pérez, O

2018-05-02

We examined the sediments of four coastal lagoons (Ria Lagartos, Bocas de Dzilam, Laguna de Chelem and Ria Celestun) from the state of Yucatan, Mexico, for three widely used commercial polybrominated diphenyl ethers formulations (penta-, octa- and deca-BDE). The most commonly found congeners in all four lagoons were BDEs 47, 99 and 100 (all in the penta-BDE formulation) and BDE209 (deca-BDE formulation). The greatest variety and highest concentrations of brominated flame retardants were found in Ria Lagartos, which also showed the highest BDE 100 concentration (24.129 ng/g). Hexabromocyclododecane was found in all lagoons, but at lower concentrations than those of the various polybrominated diphenyl ethers. Dispersal routes of these compounds are discussed, such as a ring of sinkholes (cenotes) adjacent to the lagoons. Moreover, electronic waste is a serious problem because municipal landfills have been the primary disposal method for these wastes and therefore represent a reservoir of brominated fire retardants.

Advances in Instrumental Analysis of Brominated Flame Retardants: Current Status and Future Perspectives

PubMed Central

2014-01-01

This review aims to highlight the recent advances and methodological improvements in instrumental techniques applied for the analysis of different brominated flame retardants (BFRs). The literature search strategy was based on the recent analytical reviews published on BFRs. The main selection criteria involved the successful development and application of analytical methods for determination of the target compounds in various environmental matrices. Different factors affecting chromatographic separation and mass spectrometric detection of brominated analytes were evaluated and discussed. Techniques using advanced instrumentation to achieve outstanding results in quantification of different BFRs and their metabolites/degradation products were highlighted. Finally, research gaps in the field of BFR analysis were identified and recommendations for future research were proposed. PMID:27433482

Flammability of Epoxy Resins Containing Phosphorus

NASA Technical Reports Server (NTRS)

Hergenrother, P. M.; Thompson, C. M.; Smith, J. G.; Connell, J. W.; Hinkley, J. A.

2005-01-01

As part of a program to develop fire-resistant exterior composite structures for future subsonic commercial and general aviation aircraft, flame-retardant epoxy resins are under investigation. Epoxies and their curing agents (aromatic diamines) containing phosphorus were synthesized and used to prepare epoxy formulations. Phosphorus was incorporated within the backbone of the epoxy resin and not used as an additive. The resulting cured neat epoxy formulations were characterized by thermogravimetric analysis, propane torch test, elemental analysis, microscale combustion calorimetry, and fire calorimetry. Several formulations showed excellent flame retardation with phosphorous contents as low as 1.5% by weight. The fracture toughness and compressive strength of several cured formulations showed no detrimental effect due to phosphorus content. The chemistry and properties of these new epoxy formulations are discussed.

Use of Mass Spectrometry for Identification of Biomarkers of Exposure to the Flame Retardant DI(2-Ethylhexyl)-2,3,4,5-Tetrabromophthlate

EPA Science Inventory

Di-(2-ethylhexyl)-2,3,4,5-tetrabromophthalate (TBPH) is one component in the technical formulation of Firemaster 550, a fire retardant used after phasing out certain polybrominated diphenyl ethers. Firemaster 550 is used widely and its use may result in human exposure to TBPH. To...

40 CFR Table 3 to Subpart Mmmmm of... - Performance Test Requirements for New or Reconstructed Flame Lamination Affected Sources

Code of Federal Regulations, 2013 CFR

2013-07-01

... Hazardous Air Pollutants: Flexible Polyurethane Foam Fabrication Operations Pt. 63, Subpt. MMMMM, Table 3... use chlorinated fire retardants in the laminated foam a. Method 26A in appendix A to part 60 of this... chlorinated fire retardants in the laminated foam a. A method approved by the Administrator i. Conduct the...

40 CFR Table 3 to Subpart Mmmmm of... - Performance Test Requirements for New or Reconstructed Flame Lamination Affected Sources

Code of Federal Regulations, 2012 CFR

2012-07-01

... Hazardous Air Pollutants: Flexible Polyurethane Foam Fabrication Operations Pt. 63, Subpt. MMMMM, Table 3... use chlorinated fire retardants in the laminated foam a. Method 26A in appendix A to part 60 of this... chlorinated fire retardants in the laminated foam a. A method approved by the Administrator i. Conduct the...

40 CFR Table 3 to Subpart Mmmmm of... - Performance Test Requirements for New or Reconstructed Flame Lamination Affected Sources

Code of Federal Regulations, 2010 CFR

2010-07-01

... Hazardous Air Pollutants: Flexible Polyurethane Foam Fabrication Operations Pt. 63, Subpt. MMMMM, Table 3... use chlorinated fire retardants in the laminated foam a. Method 26A in appendix A to part 60 of this... chlorinated fire retardants in the laminated foam a. A method approved by the Administrator i. Conduct the...

40 CFR Table 3 to Subpart Mmmmm of... - Performance Test Requirements for New or Reconstructed Flame Lamination Affected Sources

Code of Federal Regulations, 2011 CFR

2011-07-01

... Hazardous Air Pollutants: Flexible Polyurethane Foam Fabrication Operations Pt. 63, Subpt. MMMMM, Table 3... use chlorinated fire retardants in the laminated foam a. Method 26A in appendix A to part 60 of this... chlorinated fire retardants in the laminated foam a. A method approved by the Administrator i. Conduct the...

40 CFR Table 3 to Subpart Mmmmm of... - Performance Test Requirements for New or Reconstructed Flame Lamination Affected Sources

Code of Federal Regulations, 2014 CFR

2014-07-01

... Hazardous Air Pollutants: Flexible Polyurethane Foam Fabrication Operations Pt. 63, Subpt. MMMMM, Table 3... use chlorinated fire retardants in the laminated foam a. Method 26A in appendix A to part 60 of this... chlorinated fire retardants in the laminated foam a. A method approved by the Administrator i. Conduct the...

Fire performance, microstructure and thermal degradation of an epoxy based nano intumescent fire retardant coating for structural applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aziz, Hammad, E-mail: engr.hammad.aziz03@gmail.com; Ahmad, Faiz, E-mail: faizahmad@petronas.com.my; Yusoff, P. S. M. Megat

Intumescent fire retardant coating (IFRC) is a passive fire protection system which swells upon heating to form expanded multi-cellular char layer that protects the substrate from fire. In this research work, IFRC’s were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder and cured together using curing agent. IFRC was then reinforced with nano magnesium oxide and nano alumina as inorganic fillers to study their effect towards fire performance, microstructure and thermal degradation. Small scale fire test was conducted to investigate themore » thermal insulation of coating whereas fire performance was calculated using thermal margin value. Field emission scanning electron microscopy was used to examine the microstructure of char obtained after fire test. Thermogravimetric analysis was conducted to investigate the residual weight of coating. Results showed that the performance of the coating was enhanced by reinforcement with nano size fillers as compared to non-filler based coating. Comparing both nano size magnesium oxide and nano size alumina; nano size alumina gave better fire performance with improved microstructure of char and high residual weight.« less

Fire performance, microstructure and thermal degradation of an epoxy based nano intumescent fire retardant coating for structural applications

NASA Astrophysics Data System (ADS)

Aziz, Hammad; Ahmad, Faiz; Yusoff, P. S. M. Megat; Zia-ul-Mustafa, M.

2015-07-01

Intumescent fire retardant coating (IFRC) is a passive fire protection system which swells upon heating to form expanded multi-cellular char layer that protects the substrate from fire. In this research work, IFRC's were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder and cured together using curing agent. IFRC was then reinforced with nano magnesium oxide and nano alumina as inorganic fillers to study their effect towards fire performance, microstructure and thermal degradation. Small scale fire test was conducted to investigate the thermal insulation of coating whereas fire performance was calculated using thermal margin value. Field emission scanning electron microscopy was used to examine the microstructure of char obtained after fire test. Thermogravimetric analysis was conducted to investigate the residual weight of coating. Results showed that the performance of the coating was enhanced by reinforcement with nano size fillers as compared to non-filler based coating. Comparing both nano size magnesium oxide and nano size alumina; nano size alumina gave better fire performance with improved microstructure of char and high residual weight.

Environmental monitoring of selected pesticides and organic chemicals in urban stormwater recycling systems using passive sampling techniques

NASA Astrophysics Data System (ADS)

Page, Declan; Miotliński, Konrad; Gonzalez, Dennis; Barry, Karen; Dillon, Peter; Gallen, Christie

2014-03-01

Water recycling via aquifers has become a valuable tool to augment urban water supplies in many countries. This study reports the first use of passive samplers for monitoring of organic micropollutants in Managed Aquifer Recharge (MAR). Five different configurations of passive samplers were deployed in a stormwater treatment wetland, groundwater monitoring wells and a recovery tank to capture a range of polar and non-polar micropollutants present in the system. The passive samplers were analysed for a suite of pesticides, polycyclic aromatic hydrocarbons (PAHs) and other chemicals. As a result, 17 pesticides and pesticide degradation products, 5 PAHs and 8 other organic chemicals including flame retardants and fragrances were detected in urban stormwater recharging Aquifer Storage and Recovery (ASR) and an Aquifer Storage Transfer and Recovery (ASTR) system. Of the pesticides detected, diuron, metolachlor and chlorpyrifos were generally detected at the highest concentrations in one or more passive samplers, whereas chlorpyrifos, diuron, metolachlor, simazine, galaxolide and triallate were detected in multiple samplers. Fluorene was the PAH detected at the highest concentration and the flame retardant Tris(1-chloro-2-propyl)phosphate was the chemical detected in the greatest abundance at all sites. The passive samplers showed different efficiencies for capture of micropollutants with the Empore disc samplers giving the most reliable results. The results indicate generally low levels of organic micropollutants in the stormwater, as the contaminants detected were present at very low ng/L levels, generally two to four orders of magnitude below the drinking water guidelines (NHMRC, 2011). The efficiency of attenuation of these organic micropollutants during MAR was difficult to determine due to variations in the source water concentrations. Comparisons were made between different samplers, to give a field-based calibration where existing lab-based calibrations were unavailable.

Fact Sheet: Assessing Risks from Flame Retardants

EPA Pesticide Factsheets

EPA's assessing and managing risk programs address pollution prevention, risk assessment, hazard and exposure assessment and/or characterization, and risk management for chemicals substances in commercial use.

Endocrine Disruptors

MedlinePlus

... cans, detergents, flame retardants, food, toys, cosmetics, and pesticides. NIEHS supports studies to determine whether exposure to endocrine disruptors may result in human health effects including lowered fertility and an increased incidence ...

Impact of a novel phosphorus-nitrogen flame retardant curing agent on the properties of epoxy resin

NASA Astrophysics Data System (ADS)

Liu, Xiaoli; Liang, Bing

2017-12-01

A phosphorus-nitrogen flame retardant curing agent diethyl phosphonic p-Phenylenediamine diamide (DEPPPD) was synthesized. The chemical structure of the obtained compound was identified by Fourier transform infrared (FTIR), 1H nuclear magnetic resonance (1HNMR), and mass spectroscopies. A series of t hermosetting systems were prepared by conventional epoxy resins (E-44) and DEPPPD. The effects of DEPPPD on flame retardancy, thermal degradation behavior, mechanical properties and the morphologies of char residues of EP/DEPPPD thermosets were investigated. The results demonstrated that when the phosphorus content of 2.88 wt%, EP-3 successfully passed UL-94 V-0 flammability rating, the LOI value was as high as 31.1%, the impact strength and tensile strength of it was 6.50 KJ m-2 and 48.21 MPa, the adhesive strength could reach 14.61 MPa, respectively. The TGA results indicated that the introduction of DEPPPD promoted EP matrix decomposed at a lower temperature, the rate of the thermal decomposition also decreased compared with EP-0. The residual char ratio of 800 °C was increased whether in nitrogen or in the air. The morphological structures of char residue were more compact and homogeneous which could prevent the heat transmission and diffusion, limit the production of combustible gases and reduced the heat release rate.

A novel brominated triazine-based flame retardant (TTBP-TAZ) in plastic consumer products and indoor dust.

PubMed

Ballesteros-Gómez, Ana; de Boer, Jacob; Leonards, Pim E G

2014-04-15

The presence of a novel brominated flame retardant named 2,4,6-tris(2,4,6-tribromophenoxy)-1,3,5-triazine (TTBP-TAZ) is reported for the first time in plastic parts of consumer products and indoor dust samples. TTBP-TAZ was identified by untargeted screening and can be a replacement of the banned polybrominated diphenyl ethers. Analysis techniques based on ambient mass spectrometry and on liquid chromatography with atmospheric pressure chemical ionization combined with high resolution time-of-flight mass spectrometry were developed for the screening, detection and quantification of this low volatility and high molecular weight compound. TTBP-TAZ was present in 8 of 13 plastic parts of consumer products (from mainly electric and electronic equipment acquired in 2012) at estimated concentrations of 0.01-1.9% by weight of the product (%, w/w). It was not present in any of the older 13 plastic samples that were collected in a recycling park (manufacture date before 2006), this suggests a recent use of TTBP-TAZ. It was also found in 9 of 17 house dust samples in the range of 160-22150 ng g(-1), with the highest levels being found in samples collected on electronic and electrical equipment. These preliminary results highlight the need for further research on TTBP-TAZ and the potential of using alternative analysis methods for the identification of new flame retardants.

Distribution of brominated flame retardants and dechloranes between sediments and benthic fish--A comparison of a freshwater and marine habitat.

PubMed

Sühring, Roxana; Busch, Friederike; Fricke, Nicolai; Kötke, Danijela; Wolschke, Hendrik; Ebinghaus, Ralf

2016-01-15

A total of 53 halogenated flame retardants (HFRs) were analysed in sediments, European eels and dabs from both freshwater and marine sampling stations in the German Bight and the river Elbe. Classic HFRs, such as polybrominated diphenylethers (PBDEs), were the highest concentrated HFRs in eels as well as in most dabs (apart from 1,2,5,6-tetrabromocyclooctane (TBCO)). In sediments, on the other hand, alternate BFRs and especially dechloranes dominated the contamination pattern. Dabs were still found to be statistically representative for the contamination patterns and relative magnitude in sediments from their respective habitats. Contamination patterns in eels seemed to be more driven by the contamination situation in the food chain or historical contamination of their habitat. Unsuspectedly the alternate flame retardant TBCO was found in comparably high concentrations (up to 12 ng g(-1) ww) in dabs from two sampling stations as well as in sediments from these stations (up to 1.2 ng g(-1) dw). It could not be detected in any other analysed fish or sediment samples, indicating a localised contamination source in the area. This study provides information on HFR contamination patterns and behaviour in both marine and freshwater sediments and their potential role as contamination source for benthic fish. Copyright © 2015 Elsevier B.V. All rights reserved.

Nano-Al{sub 2}O{sub 3} multilayer film deposition on cotton fabrics by layer-by-layer deposition method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ugur, Sule S., E-mail: sule@mmf.sdu.edu.tr; Sariisik, Merih; Aktas, A. Hakan

Highlights: {yields} Cationic charges were created on the cotton fibre surfaces with 2,3-epoxypropyltrimethylammonium chloride. {yields} Al{sub 2}O{sub 3} nanoparticles were deposited on the cotton fabrics by layer-by-layer deposition. {yields} The fabrics deposited with the Al{sub 2}O{sub 3} nanoparticles exhibit better UV-protection and significant flame retardancy properties. {yields} The mechanical properties were improved after surface film deposition. -- Abstract: Al{sub 2}O{sub 3} nanoparticles were used for fabrication of multilayer nanocomposite film deposition on cationic cotton fabrics by electrostatic self-assembly to improve the mechanical, UV-protection and flame retardancy properties of cotton fabrics. Cotton fabric surface was modified with a chemical reaction tomore » build-up cationic charge known as cationization. Attenuated Total Reflectance Fourier Transform Infrared Spectroscopy, X-ray Photoelectron Spectroscopy and Scanning Electron Microscopy were used to verify the presence of deposited nanolayers. Air permeability, whiteness value, tensile strength, UV-transmittance and Limited Oxygen Index properties of cotton fabrics were analyzed before and after the treatment of Al{sub 2}O{sub 3} nanoparticles by electrostatic self-assemblies. It was proved that the flame retardancy, tensile strength and UV-transmittance of cotton fabrics can be improved by Al{sub 2}O{sub 3} nanoparticle additive through electrostatic self-assembly process.« less

Thyroid axis disruption in juvenile brown trout (Salmo trutta) exposed to the flame retardant β-tetrabromoethylcyclohexane (β-TBECH) via the diet.

PubMed

Park, Bradley J; Palace, Vince; Wautier, Kerry; Gemmill, Bonnie; Tomy, Gregg

2011-09-15

Tetrabromoethylcyclohexane (TBECH) is an additive brominated flame retardant used in domestic and industrial applications. It has been detected in wildlife, and there is early evidence that it is an endocrine disruptor. Whereas other brominated flame retardants with similar physicochemical properties have been shown to disrupt the thyroid axis, no such evaluation has been conducted for TBECH. To elucidate this, juvenile brown trout (Salmo trutta) were fed either a control diet or diets containing low, medium, or high doses of β-TBECH, the isomer most frequently detected in wildlife, for 56 days (uptake phase) followed by a control diet for an additional 77 days (depuration phase). Eight fish per treatment were lethally sampled on uptake days 7, 14, 21, 35, 49, and 56 and on depuration days 7, 21, 35, 49, and 77 to assess fish condition, circulating free and total triiodothyronine and thyroxine, and thyroid epithelial cell height. Although there was no effect on condition factor, there was a significant reduction in total plasma thyroxine in the high dose group and a significant increase in mean thyroid epithelial cell height in the low, medium, and high dose groups during the uptake phase, whereas there were no differences in the depuration phase. These results indicate that β-TBECH may modulate the thyroid axis in fish at environmentally relevant concentrations.

Legacy and alternative halogenated flame retardants in human milk in Europe: Implications for children's health.

PubMed

Čechová, Eliška; Vojta, Šimon; Kukučka, Petr; Kočan, Anton; Trnovec, Tomáš; Murínová, Ľubica Palkovičová; de Cock, Marijke; van de Bor, Margot; Askevold, Joakim; Eggesbø, Merete; Scheringer, Martin

2017-11-01

In this study, 10 polybrominated diphenyl ethers (PBDEs) and 19 alternative halogenated flame retardants (AFRs) were determined in >450 human milk samples across three European countries, representing northern, western and eastern Europe. This study provides first insights into the occurrence of selected AFRs in mother milk samples and compares them among three European countries. Sums of median concentrations of the most frequently detected PBDEs were 2.16, 0.88 and 0.45ngg -1 lipid weight (lw) in Norway, the Netherlands and Slovakia, respectively. The sum of the concentrations of AFRs ranged from 0.14 to 0.25ngg -1 lw in all countries, which was 2 to 15 times less compared to Σ 7 PBDEs. The Penta-BDE replacement, bis(2-ethylhexyl) tetrabromophthalate, BEH-TEBP, was present at the greatest concentrations of any of the AFRs and in some samples exceeded concentrations of BDE 47 and BDE 153. Four AFRs including bromobenzenes (hexabromobenzene, pentabromobenzene, pentabromotoluene) and another Penta-BDE replacement (2-ethylhexyl-2,3,4,5-tetrabromobenzoate, EH-TBB) were detected in >42% of all human milk samples. Because of the potential developmental neurotoxicity of the halogenated flame retardants, infant dietary intakes via breastfeeding were estimated; in four cases the intakes of BDE 47 exceeded the reference dose indicating that the present concentrations may pose a risk for children. Copyright © 2017 Elsevier Ltd. All rights reserved.

E-Waste Driven Pollution in Pakistan: The First Evidence of Environmental and Human Exposure to Flame Retardants (FRs) in Karachi City.

PubMed

Iqbal, Mehreen; Syed, Jabir Hussain; Breivik, Knut; Chaudhry, Muhammad Jamshed Iqbal; Li, Jun; Zhang, Gan; Malik, Riffat Naseem

2017-12-05

Informal e-waste recycling activities have been shown to be a major emitter of organic flame retardants (FRs), contributing to both environmental and human exposure to laborers at e-waste recycling sites in some West African countries, as well as in China and India. The main objective of this study was to determine the levels of selected organic FRs in both air and soil samples collected from areas with intensive informal e-waste recycling activities in Karachi, Pakistan. Dechlorane Plus (DP) and "novel" brominated flame retardants (NBFRs) were often detected in high concentrations in soils, while phosphorus-based FRs (OPFRs) dominated atmospheric samples. Among individual substances and substance groups, decabromodiphenyl ether (BDE-209) (726 ng/g), decabromodiphenyl ethane (DBDPE) (551 ng/g), 1,2-bis(2,4,6-tribromophenoxy) ethane (BTBPE) (362 ng/g), and triphenyl-phosphate (∑TPP) (296 ng/g) were found to be prevalent in soils, while OPFR congeners (5903-24986 ng/m 3 ) were prevalent in air. The two major e-waste recycling areas (Shershah and Lyari) were highly contaminated with FRs, suggesting informal e-waste recycling activities as a major emission source of FRs in the environment in Karachi City. However, the hazards associated with exposure to PM 2.5 appear to exceed those attributed to exposure to selected FRs via inhalation and soil ingestion.

The GhTT2_A07 gene is linked to the brown colour and natural flame retardancy phenotypes of Lc1 cotton (Gossypium hirsutum L.) fibres

PubMed Central

Hinchliffe, Doug J.; Condon, Brian D.; Thyssen, Gregory; Naoumkina, Marina; Madison, Crista A.; Reynolds, Michael; Delhom, Christopher D.; Fang, David D.; Li, Ping; McCarty, Jack

2016-01-01

Some naturally coloured brown cotton fibres from accessions of Gossypium hirsutum L. can be used to make textiles with enhanced flame retardancy (FR). Several independent brown fibre loci have been identified and mapped to chromosomes, but the underlying genes have not yet been identified, and the mechanism of lint fibre FR is not yet fully understood. In this study, we show that both the brown colour and enhanced FR of the Lc1 lint colour locus are linked to a 1.4Mb inversion on chromosome A07 that is immediately upstream of a gene with similarity to Arabidopsis TRANSPARENT TESTA 2 (TT2). As a result of the alternative upstream sequence, the transcription factor GhTT2_A07 is highly up-regulated in developing fibres. In turn, genes in the phenylpropanoid metabolic pathway are activated, leading to biosynthesis of proanthocyanidins and accumulation of inorganic elements. We show that enhanced FR and anthocyanin precursors appear in developing brown fibres well before the brown colour is detectible, demonstrating for the first time that the polymerized proanthocyanidins that constitute the brown colour are not the source of enhanced FR. Identifying the particular colourless metabolite that provides Lc1 cotton with enhanced FR could help minimize the use of synthetic chemical flame retardant additives in textiles. PMID:27567364

Catalytic degradation of brominated flame retardants by copper oxide nanoparticles

NASA Astrophysics Data System (ADS)

Dror, I.; Yecheskel, Y.; Berkowitz, B.

2013-12-01

Brominated flame retardants (BFRs) have been added to various products like plastic, textile, electronics and synthetic polymers at growing rates. In spite of the clear advantages of reducing fire damages, many of these BFRs may be released to the environment after their beneficial use which may lead to contamination of water resources. In this work we present the catalytic degradation of two brominated flame retardants (BFRs), tribromoneopentyl alcohol (TBNPA) and 2,4 dibromophenol (2,4-DBP) by copper oxide nanoparticles (nCuO) in aqueous solution. The degradation kinetics, the debromination, and the formation of intermediates by nCuO catalysis are compared to Fenton oxidation and to reduction by nano zero-valent iron (nZVI). The two studied BFRs are shown to degrade fully by the nCuO system within hours to days. Shorter reaction times showed differences in reaction pathways and kinetics for the two compounds. The 2,4-DBP showed faster degradation than TBNPA, by nCuO catalysis. Relatively high resistance to degradation was recorded for 2,4-DBP with nZVI, yielding 20% degradation after 24 h, while the TBNPA was degraded by 85% within 12 hours. A catalytic mechanism for radical generation and BFR degradation by nCuO is proposed. It is further suggested that H2O2 plays an essential role in the activation of the catalyst.

Distributions and compositions of old and emerging flame retardants in the rhizosphere and non-rhizosphere soil in an e-waste contaminated area of South China.

PubMed

Wang, Shaorui; Wang, Yan; Song, Mengke; Luo, Chunling; Li, Jun; Zhang, Gan

2016-01-01

We investigated rhizosphere effects on the distributions and compositions of polybrominated diphenyl ethers (PBDEs), novel brominated flame retardants (NBFRs), and dechlorane plus (DPs) in rhizosphere soils (RS) and non-rhizosphere soils (NRS) in an e-waste recycling area in South China. The concentrations of PBDEs, NBFRs, and DPs ranged from 13.9 to 351, 11.6 to 70.8, and 0.64 to 8.74 ng g(-1) in RS and 7.56 to 127, 8.98 to 144, and 0.38 to 8.45 ng g(-1) in NRS, respectively. BDE-209 and DBDPE were the dominant congeners of PBDEs and NBFRs, respectively. PBDEs, NBFRs, and DPs were more enriched in RS than NRS in most vegetables species. Further analysis suggested that the differentiation of the rhizosphere effect on halogenated flame retardants (HFRs) was not solely controlled by the octanol-water coefficients. This difference was also reflected by the correlations between total organic carbon (TOC) and PBDEs, NBFRs, or DPs, which indicated that organic carbon was a more pivotal controlling factor for PBDEs and DPs than for NBFRs in soil. We also found significant positive correlations between PBDEs and their replacement products, which indicated a similar emission pattern and environmental behaviour. Copyright © 2015 Elsevier Ltd. All rights reserved.

Spatial Distribution and Air-Water Exchange of Organic Flame Retardants in the Lower Great Lakes.

PubMed

McDonough, Carrie A; Puggioni, Gavino; Helm, Paul A; Muir, Derek; Lohmann, Rainer

2016-09-06

Organic flame retardants (OFRs) such as polybrominated diphenyl ethers (PBDEs) and novel halogenated flame retardants (NHFRs) are ubiquitous, persistent, and bioaccumulative contaminants that have been used in consumer goods to slow combustion. In this study, polyethylene passive samplers (PEs) were deployed throughout the lower Great Lakes (Lake Erie and Lake Ontario) to measure OFRs in air and water, calculate air-water exchange fluxes, and investigate spatial trends. Dissolved Σ12BDE was greatest in Lake Ontario near Toronto (18 pg/L), whereas gaseous Σ12BDE was greatest on the southern shoreline of Lake Erie (11 pg/m(3)). NHFRs were generally below detection limits. Air-water exchange was dominated by absorption of BDEs 47 and 99, ranging from -964 pg/m(2)/day to -30 pg/m(2)/day. Σ12BDE in air and water was significantly correlated with surrounding population density, suggesting that phased-out PBDEs continued to be emitted from population centers along the Great Lakes shoreline in 2012. Correlation with dissolved Σ12BDE was strongest when considering population within 25 km while correlation with gaseous Σ12BDE was strongest when using population within 3 km to the south of each site. Bayesian kriging was used to predict dissolved Σ12BDE over the lakes, illustrating the utility of relatively highly spatially resolved measurements in identifying potential hot spots for future study.

Organophosphorus flame retardants and heavy metals in municipal landfill leachate treatment system in Guangzhou, China.

PubMed

Deng, Mingjun; Kuo, Dave T F; Wu, Qihang; Zhang, Ying; Liu, Xinyu; Liu, Shengyu; Hu, Xiaodong; Mai, Bixian; Liu, Zhineng; Zhang, Haozhi

2018-05-01

The occurrence, distribution and removal efficiencies of organophosphorus flame retardants (OPFRs) and metals were examined in a municipal landfill leachate treatment system in Guangzhou, China. Five OPFRs and thirty-five metals were detected in wastewater samples collected at different treatment stages. ∑OPFRs was reduced from 4807.02 ng L -1 to 103.91 ng L -1 through the treatment system, with close to 98% removed from the dissolved phase. Tris(clorisopropyl) phosphates (TCPPs) dominated through the treatment process and accounted for over 80% and 50% of ∑OPFRs at the influent and the effluent, respectively. TCPPs were most efficiently removed (98.6%) followed by tris(2-chloroethyl) phosphate (TCEP) (96.6%) and triphenyl phosphate (TPP) (88.5%). For metals, Fe, Cr, and Rb were dominant in the raw leachate, detected at 7.55, 2.82, and 4.50 mg L -1 , respectively. Thirteen regulated heavy metals - including eight major pollutants (i.e., As. Cd, Cr, Cu, Hg, Ni, Pb, and Zn) - have been detected in all wastewater samples at sub-mg L -1 levels. Over 99.5% removal was achieved for Cr, Ni, and Fe, and close to 95% removal efficiency was observed for Rb. For the eight major heavy metals, over 99% removal was observed; the only exception was Cu, which was removed at 89%. It was found that microfiltration/reverse osmosis was critical for the removal of OPFRs and heavy metals while the core biological treatment played a minor role towards their removal. Remobilization of Co, Cu, Fe, Hg, Mn, Ni, Sb, and Sr from the returned sludge occurred during the second denitrification, indicating the need for additional post-biological process for effective removal of both contaminants. This study highlights the critical need to develop cheap, effective treatment technologies for contaminants-laden leachate generated from open dumps and under-designed landfills. Copyright © 2018 Elsevier Ltd. All rights reserved.

Propelling plastics into the circular economy - weeding out the toxics first.

PubMed

Leslie, H A; Leonards, P E G; Brandsma, S H; de Boer, J; Jonkers, N

2016-09-01

The Stockholm Convention bans toxic chemicals on its persistent organic pollutants (POPs) list in order to promote cleaner production and prevent POPs accumulation in the global environment. The original 'dirty dozen' set of POPs has been expanded to include some of the brominated diphenyl ether flame retardants (POP-BDEs). In addition to cleaner production, there is an urgent need for increased resource efficiency to address the finite amount of raw materials on Earth. Recycling plastic enhances resource efficiency and is part of the circular economy approach, but how clean are the materials we are recycling? With the help of a new screening method and detailed analyses, we set out to investigate where these largely obsolete BDEs were showing up in Dutch automotive and electronics waste streams, calculate mass flows and determine to what extent they are entering the new product chains. Our study revealed that banned BDEs and other toxic flame retardants are found at high concentrations in certain plastic materials destined for recycling markets. They were also found in a variety of new consumer products, including children's toys. A mass flow analysis showed that 22% of all the POP-BDE in waste electrical and electronic equipment (WEEE) is expected to end up in recycled plastics because these toxic, bioaccumulative and persistent substances are currently not effectively separated out of plastic waste streams. In the automotive sector, this is 14%, while an additional 19% is expected to end up in second-hand parts (reuse). These results raise the issue of delicate trade-offs between consumer safety/cleaner production and resource efficiency. As petroleum intensive materials, plastic products ought to be repaired, reused, remanufactured and recycled, making good use of the 'inner circles' of the circular economy. Keeping hazardous substances - whether they are well known POPs or emerging contaminants - out of products and plastic waste streams could make these cycles work better for businesses, people and nature. Copyright © 2016 Elsevier Ltd. All rights reserved.

46 CFR 111.60-17 - Connections and terminations.

Code of Federal Regulations, 2011 CFR

2011-10-01

... general, connections and terminations to all conductors must retain the original electrical, mechanical, flame-retarding, and, where necessary, fire-resisting properties of the cable. All connecting devices...

46 CFR 111.60-17 - Connections and terminations.

Code of Federal Regulations, 2010 CFR

2010-10-01

... general, connections and terminations to all conductors must retain the original electrical, mechanical, flame-retarding, and, where necessary, fire-resisting properties of the cable. All connecting devices...

Flammability and Photo-Stability of Selected Polymer Systems

NASA Technical Reports Server (NTRS)

Lo, Jeelin

1981-01-01

A systematic approach to the improvement of the flammability of epoxy resins, bisphenol-A polycarbonate poly(butylene terephthalate), and Nylon 6.6 by introducing halogens and loop functionality into the flame retardants is described. The phthalides (the loop functionality containing molecules) include 3,3-bis(4-bromophenyl)-phthalide, 3,3-bis(4-chlorophenyl)phthalide, and phenolphthalein. The phthalide containing epoxy resins are synthesized and characterized in comparison with the bisphenol-A epoxy resins in terms of flammability in the copolymer systems. The resins include diglycidyl ethers of phenolphthalein, bisphenol-A. tetrabromobisphenol-A, and tetraoromophenolphthalein. The vaporization of the phthalide additive in the polymers is observed in Thermal Gravimetric Analysis. The flame retardancy is primarily due to the presence of halogens. In the poly(butylene terephthalate) system, the cleavage of the C(sub aromatic) -B bond of the flame retardant additive enhances the crosslinking react ions between the aromatic rings resulting in an increase of char formation. In the epoxy resin systems, loop functionality contributes to char formation to a larger extent. The interaction between the epoxy resin and poly-(butylene terephthalate) follows the mechanism of insertion of the oxirane ring into the ester bond. This mechanism is studied by FT-IR. The investigation of the thermal properties of the char-forming phenol-formaldehyde resins is conducted to provide information for the systematic design of high temperature flame-resistant phenolics. NMR and FT-IR are used to characterize the oligomeric resins and the cured resins. The curing agents used in the study include formaldehyde, s-trioxane and terephthaloyl chloride. The brominated phenolic resins are found to have higher oxygen indices with lower char yields.

Polybrominated Diphenyl Ethers (PBDEs) Action Plan

EPA Pesticide Factsheets

Polybrominated diphenyl ethers (PBDEs) have been widely used as flame retardants in a number of applications. EPA is concerned that some of the component congeners are persistent, bioaccumulative and toxic.

Polyfunctional epoxies - Different molecular weights of brominated polymeric additives as flame retardants in graphite composites

NASA Technical Reports Server (NTRS)

Nir, Z.; Gilwee, W. J.; Kourtides, D. A.; Parker, J. A.

1983-01-01

The imparting of flame retardancy to graphite-reinforced composites without incurring mechanical property deterioration is investigated for the case of an experimental, trifunctional epoxy resin incorporating brominated polymeric additives (BPAs) of the diglycidyl type. Such mechanical properties as flexural strength and modulus, and short beam shear strength, were measured in dry and in hot/wet conditions, and the glass transition temperature, flammability, and water absorption were measured and compared with nonbromilated systems. Another comparison was made with a tetrafunctional epoxy system. The results obtained are explained in terms of differences in the polymeric backbone length of the bromine carrier polymer. BPAs are found to be a reliable bromine source for fire inhibition in carbon-reinforced composites without compromise of mechanical properties.

Separation of Flame and Nonflame-retardant Plastics Utilizing Magneto-Archimedes Method

NASA Astrophysics Data System (ADS)

Misawa, Kohei; Kobayashi, Takayuki; Mori, Tatsuya; Mishima, Fumihito; Akiyama, Yoko; Nishijima, Shigehiro

2017-07-01

In physical recycling process, the quality of recycled plastics becomes usually poor in case various kinds of plastic materials are mixed. In order to solve the problem, we tried to separate flame and nonflame-retardant plastics used for toner cartridges as one example of mixed plastics by using magneto-Archimedes method. By using this method, we can control levitation and settlement of the particles in the medium by controlling the density and magnetic susceptibility of the medium and the magnetic field. In this study, we introduced the separation system of plastics by the combination of wet type specific gravity separation and magneto-Archimedes separation. In addition, we examined continuous and massive separation by introducing the system which can separate the plastics continuously in the flowing fluid.

Chemistry of green encapsulating molding compounds at interfaces with other materials in electronic devices

NASA Astrophysics Data System (ADS)

Scandurra, A.; Zafarana, R.; Tenya, Y.; Pignataro, S.

2004-07-01

The interface chemistry between encapsulating epoxy phenolic molding compound (EMC) containing phosphorous based organic flame retardant (the so called "green materials") and copper oxide-hydroxide and aluminum oxide-hydroxide surfaces have been studied in comparison with "conventional" EMC containing bromine and antimony as flame retardant. These green materials are designed to reduce the presence of toxic elements in the electronic packages and, consequently, in the environment. For the study were used a Scanning Acoustic Microscopy for delamination measurements, a dynamometer for the pull strength measurements and an ESCA spectrometer for chemical analysis of the interface. The general behavior of the green compound in terms of delamination, adhesion, and corrosion is found better or at least comparable than that of the conventional EMC.

Durability of foam insulation for LH2 fuel tanks of future subsonic transports

NASA Technical Reports Server (NTRS)

Sharpe, E. L.; Helenbrook, R. G.

1979-01-01

Organic foams were tested to determine their suitability for insulating liquid hydrogen tanks of subsonic aircraft. The specimens, including nonreinforced foams and foams with chopped glass reinforcements, flame retardants, and vapor barriers, were scaled to simulate stress conditions in large tanks. The tests were conducted within aluminum tank compartments filled with liquid hydrogen and the boil-off rate was used as the criterion of thermal performance. It was found that while all insulations deteriorated with increased cycles, two nonreinforced polyurethane foams showed no structural deterioration after 4200 thermal cycles (equivalent to 15 years of airline service). It was also found that fiberglass reinforcement and flame retardants impaired thermal performance and reduced useful life of the foams. Vapor barriers enhanced structural integrity without any deterioration in thermal properties.

Wet air co-oxidation of decabromodiphenyl ether (BDE209) and tetrahydrofuran.

PubMed

Zhao, Hongxia; Zhang, Feifang; Qu, Baocheng; Xue, Xingya; Liang, Xinmiao

2009-09-30

The wet air co-oxidation (WACO) of a major commercial polybrominated diphenyl ether flame retardant congener, decabromodiphenyl ether (BDE209), was investigated using tetrahydrofuran (THF) as an initiator in a stainless autoclave at temperature range of 120-170 degrees C and 0.5MPa oxygen pressure. Compared to the single oxidation of BDE209 under the same conditions, the addition of THF in the reaction system greatly improved the removal efficiency of BDE209. The effect of temperature on the reaction was studied. The removals of BDE209 and Br increased with increasing temperature. In addition, the effect of NaNO(2) as the catalyst on the WACO was also investigated and the results showed that the addition of NaNO(2) could improve the Br removal efficiency.

Catalytic and electrocatalytic hydrogenolysis of brominated diphenyl ethers.

PubMed

Bonin, Pascale M L; Edwards, Patrick; Bejan, Dorin; Lo, Chun Chi; Bunce, Nigel J; Konstantinov, Alexandre D

2005-02-01

Polybrominated diphenyl ethers (PBDEs) are ubiquitous environmental contaminants due to their use as additive flame-retardants. Conventional catalytic hydrogenolysis in methanol solution and electrocatalytic hydrogenolysis in aqueous methanol were examined as methods for debrominating mono- and di-bromodiphenyl ethers, as well as a commercial penta-PBDE mixture, in each case using palladium on alumina as the catalyst. Electrocatalytic hydrogenolysis employed a divided flow-through batch cell, with reticulated vitreous carbon cathodes and IrO2/Ti dimensionally stable anodes. Both methods gave efficient sequential debromination, with essentially complete removal of bromine from the PBDEs, but the electrocatalytic method was limited by the poor solubility of PBDEs in aqueous methanol.

Highly flexible cross-linked cellulose nanofibril sponge-like aerogels with improved mechanical property and enhanced flame retardancy.

PubMed

Guo, Limin; Chen, Zhilin; Lyu, Shaoyi; Fu, Feng; Wang, Siqun

2018-01-01

Cellulose nanofibril (CNF) aerogel is highly flammable and its mechanical strength is very soft, which is unfavourable due to safety concerns and impractical when used as the thermal insulation material. In this work, we used N-methylol dimethylphosphonopropionamide (MDPA) and 1,2,3,4-butanetetracarboxylic acid (BTCA) as co-additives and then prepared lightweight flame resistant CNF sponge-like aerogels via an eco-friendly freeze-drying and post cross-linking method. The CNF/BTCA/MDPA aerogel exhibited a better flame retardant performance, outstanding self-extinguishing behaviour and significantly increased char residue (by as much as 268%) compared with the neat CNF aerogel. Meanwhile, the resilience of the aerogel samples improved significantly as the flexibility decreased slightly. Furthermore, the aerogel samples still exhibited excellent thermal insulating properties with thermal conductivity as low as 0.03258W/(m k). The combination of these characteristics makes the CNF-based aerogel a promising insulation candidate for thermal protective equipment (e.g., fire-protection clothing or advanced spacesuit elements) in the future. Copyright © 2017 Elsevier Ltd. All rights reserved.

Polybrominated diphenyl ethers (PBDEs) and alternative brominated flame retardants (aBFRs) in sediments from four bays of the Yellow Sea, North China.

PubMed

Zhen, Xiaomei; Tang, Jianhui; Xie, Zhiyong; Wang, Runmei; Huang, Guopei; Zheng, Qian; Zhang, Kai; Sun, Yongge; Tian, Chongguo; Pan, Xiaohui; Li, Jun; Zhang, Gan

2016-06-01

The distribution characteristics and potential sources of polybrominated diphenyl ethers (PBDEs) and alternative brominated flame retardants (aBFRs) were investigated in 54 surface sediment samples from four bays (Taozi Bay, Sishili Bay, Dalian Bay, and Jiaozhou Bay) of North China's Yellow Sea. Of the 54 samples studied, 51 were collected from within the four bays and 3 were from rivers emptying into Jiaozhou Bay. Decabromodiphenylethane (DBDPE) was the predominant flame retardant found, and concentration ranged from 0.16 to 39.7 ng g(-1) dw and 1.13-49.9 ng g(-1) dw in coastal and riverine sediments, respectively; these levels were followed by those of BDE 209, and its concentrations ranged from n.d. to 10.2 ng g(-1) dw and 0.05-7.82 ng g(-1) dw in coastal and riverine sediments, respectively. The levels of DBDPE exceeded those of decabromodiphenyl ether (BDE 209) in most of the samples in the study region, whereas the ratio of DBDPE/BDE 209 varied among the four bays. This is indicative of different usage patterns of brominated flame retardants (BFRs) and also different hydrodynamic conditions among these bay areas. The spatial distribution and composition profile analysis indicated that BFRs in Jiaozhou Bay and Dalian Bay were mainly from local sources, whereas transport from Laizhou Bay by coastal currents was the major source of BFRs in Taozi Bay and Sishili Bay. Both the ∑PBDEs and ∑aBFRs (sum of pentabromotoluene (PBT), 2,3-diphenylpropyl-2,4,6-tribromophenyl ether (DPTE), pentabromoethylbenzene (PBEB), and hexabromobenzene (HBB)) were at low concentrations in all the sediments. This is probably attributable to a combination of factors such as low regional usage of these products, atmospheric deposition patterns, coastal currents transportation patterns, and degradation processes for higher BDE congeners. This paper is the first study that has investigated the levels of DBDPE in the coastal sediments of China's Yellow Sea. Copyright © 2016 Elsevier Ltd. All rights reserved.

Flame-retardant carbon nanotube films

NASA Astrophysics Data System (ADS)

Janas, Dawid; Rdest, Monika; Koziol, Krzysztof K. K.

2017-07-01

We have demonstrated fire-retardancy properties of a polymer matrix-free CNT film for the first time. As compared with classical fire-retardant materials such as Kevlar, Twaron or Nomex, the CNT film showed a spectrum of advantages. The material is lightweight, flexible and well-adherent to even the most complicated shapes. The results have showed that by using CNTs for fire-retardancy we can extend the operational time almost two-fold, what makes CNTs a much better protection than the solutions employed nowadays. We believe that among other great properties of CNT, their macroscopic assemblies such as CNT films show significant potential for becoming a fire protective coating, which exhibits high performance in not sustaining fire.

Novel combined stir bar sorptive extraction coupled with ultrasonic assisted extraction for the determination of brominated flame retardants in environmental samples using high performance liquid chromatography.

PubMed

Yu, Chunhe; Hu, Bin

2007-08-10

A combined stir bar coated with poly (dimethysiloxane)-beta-cyclodextrin (PDMS-beta-CD) on single side has been prepared for the first time by sol-gel method and was coupled with ultrasonic assisted extraction (UAE) for the determination of some brominated flame-retardant compounds (BFRs) in soil and dust samples by high performance liquid chromatography (HPLC). Four different kinds of coatings including PDMS-beta-CD, PDMS, carbowax (CW)-PDMS-poly (vinyl alcohol) (PVA) and PDMS-PVA were evaluated for stir bar sorptive extraction of BFRs by orthogonal experiment design. The experimental results reveal that the PDMS-beta-CD combined stir bar exhibited the best extraction efficiency for the target analytes. The reproducibility for the preparation of PDMS-beta-CD combined stir bar ranged from 1.3% to 15.7% in one batch, and 7.2% to 15.1% among batches. Extraction time, desorption solvent, concentration of methanol and NaCl in the matrix, pH, temperature and stirring speed were optimized. The combined stir bar can avoid direct friction of the coating with the bottom of the vessel, and could be used for more than 100 times. Linearity (>0.993), repeatability (<10.5%), reproducibility (<16.5%), recovery (56-118%) and detection limits (2.9-4.2 microg L(-1)) were proper to determine the seven BFRs. The developed method was applied to the determination of BFRs in soil and dust with satisfactory results.

Fire propagation performance of intumescent fire protective coatings using eggshells as a novel biofiller.

PubMed

Yew, M C; Ramli Sulong, N H; Yew, M K; Amalina, M A; Johan, M R

2014-01-01

This paper aims to synthesize and characterize an effective intumescent fire protective coating that incorporates eggshell powder as a novel biofiller. The performances of thermal stability, char formation, fire propagation, water resistance, and adhesion strength of coatings have been evaluated. A few intumescent flame-retardant coatings based on these three ecofriendly fire retardant additives ammonium polyphosphate phase II, pentaerythritol and melamine mixed together with flame-retardant fillers, and acrylic binder have been prepared and designed for steel. The fire performance of the coatings has conducted employing BS 476: Part 6-Fire propagation test. The foam structures of the intumescent coatings have been observed using field emission scanning electron microscopy. On exposure, the coated specimens' B, C, and D had been certified to be Class 0 due to the fact that their fire propagation indexes were less than 12. Incorporation of ecofriendly eggshell, biofiller into formulation D led to excellent performance in fire stopping (index value, (I) = 4.3) and antioxidation of intumescent coating. The coating is also found to be quite effective in water repellency, uniform foam structure, and adhesion strength.

Fire Propagation Performance of Intumescent Fire Protective Coatings Using Eggshells as a Novel Biofiller

PubMed Central

Yew, M. C.; Ramli Sulong, N. H.; Yew, M. K.; Amalina, M. A.; Johan, M. R.

2014-01-01

This paper aims to synthesize and characterize an effective intumescent fire protective coating that incorporates eggshell powder as a novel biofiller. The performances of thermal stability, char formation, fire propagation, water resistance, and adhesion strength of coatings have been evaluated. A few intumescent flame-retardant coatings based on these three ecofriendly fire retardant additives ammonium polyphosphate phase II, pentaerythritol and melamine mixed together with flame-retardant fillers, and acrylic binder have been prepared and designed for steel. The fire performance of the coatings has conducted employing BS 476: Part 6-Fire propagation test. The foam structures of the intumescent coatings have been observed using field emission scanning electron microscopy. On exposure, the coated specimens' B, C, and D had been certified to be Class 0 due to the fact that their fire propagation indexes were less than 12. Incorporation of ecofriendly eggshell, biofiller into formulation D led to excellent performance in fire stopping (index value, (I) = 4.3) and antioxidation of intumescent coating. The coating is also found to be quite effective in water repellency, uniform foam structure, and adhesion strength. PMID:25136687

Mechanochemical pre-treatment for viable recycling of plastic waste containing haloorganics.

PubMed

Cagnetta, Giovanni; Zhang, Kunlun; Zhang, Qiwu; Huang, Jun; Yu, Gang

2018-05-01

Chemical recycling technologies are the most promising for a waste-to-energy/material recovery of plastic waste. However, 30% of such waste cannot be treated in this way due to the presence of halogenated organic compounds, which are often utilized as flame retardants. In fact, high quantities of hydrogen halides and dioxin would form. In order to enabling such huge amount of plastic waste as viable feedstock for recycling, an investigation on mechanochemical pre-treatment by high energy ball milling is carried out on polypropylene containing decabromodiphenyl ether. Results demonstrate that co-milling with zero valent iron and quartz sand ensures complete debromination and mineralization of the flame retardant. Furthermore, a comparative experiment demonstrates that the mechanochemical debromination kinetics is roughly proportional to the polymer-to-haloorganics mass ratio. Copyright © 2018 Elsevier Ltd. All rights reserved.

2-Ethylhexyl tetrabromobenzoate and bis(2-ethylhexyl) tetrabromophthalate flame retardants in the Great Lakes atmosphere.

PubMed

Ma, Yuning; Venier, Marta; Hites, Ronald A

2012-01-03

Two relatively new flame retardants, 2-ethylhexyl-2,3,4,5-tetrabromobenzoate (TBB) and bis(2-ethylhexyl)-tetrabromophthalate (TBPH), were identified and quantitated in gas and particle-phase air samples collected from six sites near the shores of the Great Lakes. TBB and TBPH were detected in more than half of the samples collected from 2008 to 2010. Urban areas, such as Chicago and Cleveland, showed the highest concentrations (0.36-290 pg/m(3)), while remote areas, such as Eagle Harbor and Sleeping Bear Dunes, exhibited the lowest levels (0.050-32 pg/m(3)). The atmospheric concentrations of TBB and TBPH increased rapidly and significantly over this time period, perhaps indicating that these compounds are replacing the polybrominated diphenyl ethers (PBDEs), which have been removed or soon will be removed from the marketplace.

Biomimetic nanocoatings with exceptional mechanical, barrier, and flame-retardant properties from large-scale one-step coassembly

PubMed Central

Ding, Fuchuan; Liu, Jingjing; Zeng, Songshan; Xia, Yan; Wells, Kacie M.; Nieh, Mu-Ping; Sun, Luyi

2017-01-01

Large-scale biomimetic organic/inorganic hybrid nanocoatings with a nacre-like microstructure were prepared via a facile coassembly process. Different from conventional polymer nanocomposites, these nanocoatings contain a high concentration of nanosheets, which can be well aligned along the substrate surface. Moreover, the nanosheets and polymer matrix can be chemically co–cross-linked. As a result, the nanocoatings exhibit exceptional mechanical properties (high stiffness and strength), barrier properties (to both oxygen and water vapor), and flame retardancy, but they are also highly transparent (maintaining more than 85% of their original transmittance to visible light). The nanocoatings can be applied to various substrates and regular or irregular surfaces (for example, films and foams). Because of their excellent performance and high versatility, these nanocoatings are expected to find widespread application. PMID:28776038

Food risk assessment for perfluoroalkyl acids and brominated flame retardants in the French population: results from the second French total diet study.

PubMed

Rivière, G; Sirot, V; Tard, A; Jean, J; Marchand, P; Veyrand, B; Le Bizec, B; Leblanc, J C

2014-09-01

To determine the exposure of the French population to toxic compounds contaminating the food chain, a total diet study was performed in France between 2007 and 2009. This study was designed to reflect the consumption habits of the French population and covered the most important foods in terms of consumption, selected nutrients and contribution to contamination. Based on French consumption data, the present study reports the dietary exposure to perfluoroalkyl acids (16 congeners) and brominated flame retardants (polybrominated diphenyl ethers, hexabromocyclododecane and polybrominated biphenyls). Comparison of the calculated dietary exposures with the generally accepted health-based guidance values revealed that most compounds do not pose any risk. There are however knowledge gaps for some congeners in these large chemical classes. Copyright © 2014 Elsevier B.V. All rights reserved.

Development of nonflammable cellulosic foams

NASA Technical Reports Server (NTRS)

Luttinger, M.

1972-01-01

The development of a moldable cellulosic foam for use in Skylab instrument storage cushions is considered. Requirements include density of 10 lb cu ft or less, minimal friability with normal handling, and nonflammability in an atmosphere of 70 percent oxygen and 30 percent nitrogen at 6.2 psia. A study of halogenated foam components was made, including more highly chlorinated binders, halogen-containing additives, and halogenation of the cellulose. The immediate objective was to reduce the density of the foam through reduction in inorganic phosphate without sacrificing flame-retarding properties of the foams. The use of frothing techniques was investigated, with particular emphasis on a urea-formaldehyde foam. Halogen-containing flame retardants were deemphasized in favor of inorganic salts and the preparation of phosphate and sulphate esters of cellulose. Utilization of foam products for civilian applications was also considered.

Accumulation of flame retardants in paired eggs and plasma of bald eagles.

PubMed

Guo, Jiehong; Simon, Kendall; Romanak, Kevin; Bowerman, William; Venier, Marta

2018-06-01

In this study, we measured the concentrations of 58 flame retardants (and related compounds) in bald eagle (Haliaeetus leucocephalus) egg and plasma samples from the Michigan. These analytes include polybrominated diphenyl ethers (PBDEs), novel flame retardants (nFRs), Dechlorane-related compounds (Decs), and organophosphate esters (OPEs). A total of 24 paired eaglet plasma and egg samples were collected from inland (IN, N = 13) and the Great Lakes (GL, N = 11) breeding areas from 2000 to 2012. PBDEs were the most abundant chemical group with a geometric mean of 181 ng/g wet weight (ww) in egg and 5.31 ng/g ww in plasma. Decs were barely found in plasma samples, but they were frequently found in eggs (geometric mean 23.5 ng/g ww). OPE levels were comparable to those of PBDEs in the plasma but lower than those of PBDEs in eggs. Dec and PBDE concentrations were significantly higher in GL than in IN (p < 0.05). The ratio of egg to plasma concentrations (lipid normalized) varied with chemicals and correlated with the chemical's octanol-water partition coefficient. The lipid normalized bald eagle egg and plasma concentrations from Lake Superior and Huron were one to three orders of magnitude higher than concentrations measured in composite lake trout (Salvelinus namaycush) from the same lake, implying that they biomagnify in the environment. Copyright © 2018 Elsevier Ltd. All rights reserved.

Human exposure to brominated flame retardants through dust in different indoor environments: Identifying the sources of concentration differences in hair from men and women.

PubMed

Li, Junqi; Dong, Zheng; Wang, Ying; Bao, Junsong; Yan, Yijun; Liu, Anming; Jin, Jun

2018-08-01

Brominated flame retardants (BFRs) can accumulate in humans and are associated with adverse health effects. The study was conducted to determine the differences in Polybrominated diphenyl ethers (PBDEs) and alternative brominated flame retardant (Alt-BFR) concentrations between men and women. We analyzed hair samples from 14 male and 20 female university students, paired dust samples from their dormitories (10 for males and 8 for females), and six dust samples from university teaching buildings. The total PBDE concentrations in hair from females were significantly (three times) higher (p = 0.012) than that from males (means 372 and 109 ng/g, respectively). The mean total PBDE concentrations in classroom and dormitory dust were 36100 and 2012 ng/g, respectively. The PBDE patterns were different in the male and female hair samples, as were the patterns in the classroom and dormitory dust. There are no reports concerning human exposure to BFRs through dust that was assessed considering academic and residential environments simultaneously. The differences between BFR exposure for males and females and the differences between BFR concentrations in hair samples from males and females were consistent for 71.4% of the compounds. However, using only dormitory dust in the calculations gave consistent differences only for 28.6% of the compounds, suggesting that the BFR concentration differences in hair were mainly because females spent much more time than males in classrooms. Copyright © 2018 Elsevier Ltd. All rights reserved.

Plant selective uptake of halogenated flame retardants at an e-waste recycling site in southern China.

PubMed

Wang, Shaorui; Wang, Yan; Luo, Chunling; Li, Jun; Yin, Hua; Zhang, Gan

2016-07-01

The concentrations and homolog patterns of halogenated flame retardants (HFRs) in vegetables grown at an e-waste contaminated site were investigated. Polybrominated diphenyl ethers (PBDEs) were the dominant HFRs in vegetable tissues, with concentrations ranging from 10.3 to 164 ng g(-1) and 1.16-107 ng g(-1) in shoots and roots, respectively, followed by novel brominated flame retardants (NBFRs) and dechlorane plus (DPs). This is an indication that PBDE contamination in vegetables grown around e-waste recycling sites may pose a risk to the local terrestrial ecosystem and residents. In addition, this is the first report on the concentrations and compositions of NBFRs in vegetables around e-waste recycling sites. The HFRs concentrations in vegetables varied greatly with the vegetable species, with the highest concentrations observed in Brassica oleracea var. capitata. Root concentration factors (RCF) decreased with increasing log Kow of HFRs, which indicated that the uptake of HFRs was controlled mainly by log Kow. Dissimilar HFRs profiles in shoots and roots suggested that the uptake and translocation of HFRs by plants were selective, with lower halogenated congeners prone to accumulation in vegetable tissues. Positive relationships between PBDEs and their substitutes were observed in vegetable tissues, suggesting that the replacement of PBDEs by NBFRs has not resulted in an obvious transition in plants within the study area. Copyright © 2016 Elsevier Ltd. All rights reserved.

Occurrence and exposure assessment of organophosphate flame retardants (OPFRs) through the consumption of drinking water in Korea.

PubMed

Lee, Sunggyu; Jeong, Woochang; Kannan, Kurunthachalam; Moon, Hyo-Bang

2016-10-15

Organophosphate flame retardants (OPFRs) have been widely used as flame retardants and plasticizers in commercial products. Limited data are available on the occurrence and exposure of OPFRs via drinking water consumption. In this study, 127 drinking water samples were collected from tap water, purified water (tap water that is passed through in-house filters) and bottled water from major cities in Korea in 2014. The total concentrations of OPFRs (ΣOPFR) in all of the samples ranged from below the method detection limit (MDL) to 1660 (median: 48.7) ng/L. The predominant OPFR compounds in drinking water were tris(2-chloroethyl) phosphate (TCEP), tris(2-chloroethyl) phosphate (TCPP), and tris(2-butoxyethyl) phosphate (TBEP). Significant differences were observed in the levels of TCPP, TBEP and ΣOPFR among various types of drinking water. TCPP is introduced in the drinking water during the water purification process. Regional differences existed in the levels and patterns of OPFRs in water samples, which indicated the existence of diverse sources of these contaminants. Purified water was a significant contributor to the total OPFR intake by humans. The estimated daily intake of OPFRs was lower than the tentative oral reference dose (RfD) values. In comparison with exposure of OPFRs via dust ingestion, water consumption was a significant source of chlorinated PFRs (99% for TCEP and 34% for TCPP to the total intakes) for Koreans. Copyright © 2016 Elsevier Ltd. All rights reserved.

[Flame retardants--use and hazards for human].

PubMed

Góralczyk, Katarzyna; Struciński, Paweł; Czaja, Katarzyna; Hernik, Agnieszka; Ludwicki, Jan K

2002-01-01

Flame retardants (FRs) are chemicals which added to materials during or after manufacture, inhibit or even suppress the combustion process due to their thermal stability. Large quantities of FRs are added to the plastic material (resins) in variety of electrical and electronic appliances including television and computer casing. The other uses of these compounds include production of building materials, upholstered furniture, textiles, wall covering, carpets, hydraulic fluids as well as vehicles and aircraft. Taking into account the chemical structure, there are five main groups of FRs: brominated, chlorinated, phosphorous-containing, nitrogen-containing (i.e. melamines) and inorganic compounds. Halogenated compounds, especially polybrominated diphenyl ethers (PBDEs), a class of brominated flame retardants, due to their lipophilic characteristics and persistence have become ubiquitous environmental contaminants. There are indications that PBDEs may affect hormone function acting as endocrine disruption and may be toxic for developing brain. These compounds have been associated with non-Hodgkin's lymphoma in humans, a variety of cancers in rodents and disruption of thyroid hormones balance. Similarly to other persistent halogenated compounds they are also able to affect the xenobiotic metabolizing enzymes activity. PBDEs are now found as residues in sediments, wildlife and human (milk, serum adipose tissue) samples. The predominant congeners in environmental samples, including human specimens are two congeners: 47 and 99. Currently, the estimated daily intake of PBDEs by adult humans is equal 51 ng x day-1 while by breast-fed infants equals 110 ng x day-1.

[Comparative study of the level and distribution of polybrominated diphenyl ethers and new brominated flame retardants in the atmosphere of typical urban].

PubMed

Wu, Hui; Jin, Jun; Wang, Ying; Li, Ming-Yuan; He, Song-Jie; Xu, Meng; Sun, Yi-Ming

2014-04-01

Brominated flame retardants (BFRs) are widely used in industrial and commercial products and are frequently detected in various environmental media. It might be potential harm to the environment and the human body. This study reported the levels of 8 kinds of polybrominated diphenyl ethers (PBDEs: BDE-28, -47, -100, -99, -154, -153, -183, -209) and 3 kinds of new brominated flame retardants (NBFRs: PBT, PBEB, HBB) in the atmosphere of Binhai Development Zone, Weifang City, Shandong Province, which was taken as a BFR production source area and of Nanning City, Guangxi Province, which was taken as a contrast area. The results showed that the average concentrations of sigma8 PBDEs in the atmosphere of Weifang and Nanning were 1.4 x 10(5) pg x m(-3) and 323.0 pg x m(-3), respectively, and the average concentrations of sigma3 NBFRs were 4.2 x 10(3) pg x m(-3) and 11.9 pg x m(-3), respectively. Compared with other cities, the concentrations of BFRs in the atmosphere of the production area were at a high level in the globe, and the concentrations of BFRs in Nanning were similar with other cities in China. The distribution characteristics of PBDEs and NBFRs in the atmosphere of the production area were different from those of Nanning, and the correlations between PBEB, PBT, HBB and BDE-209 were different between Weifang and Nanning.

Mg2B2O5 Nanowire Enabled Multifunctional Solid-State Electrolytes with High Ionic Conductivity, Excellent Mechanical Properties, and Flame-Retardant Performance.

PubMed

Sheng, Ouwei; Jin, Chengbin; Luo, Jianmin; Yuan, Huadong; Huang, Hui; Gan, Yongping; Zhang, Jun; Xia, Yang; Liang, Chu; Zhang, Wenkui; Tao, Xinyong

2018-05-09

High ionic conductivity, satisfactory mechanical properties, and wide electrochemical windows are crucial factors for composite electrolytes employed in solid-state lithium-ion batteries (SSLIBs). Based on these considerations, we fabricate Mg 2 B 2 O 5 nanowire enabled poly(ethylene oxide) (PEO)-based solid-state electrolytes (SSEs). Notably, these SSEs have enhanced ionic conductivity and a large electrochemical window. The elevated ionic conductivity is attributed to the improved motion of PEO chains and the increased Li migrating pathway on the interface between Mg 2 B 2 O 5 and PEO-LiTFSI. Moreover, the interaction between Mg 2 B 2 O 5 and -SO 2 - in TFSI - anions could also benefit the improvement of conductivity. In addition, the SSEs containing Mg 2 B 2 O 5 nanowires exhibit improved the mechanical properties and flame-retardant performance, which are all superior to the pristine PEO-LiTFSI electrolyte. When these multifunctional SSEs are paired with LiFePO 4 cathodes and lithium metal anodes, the SSLIBs show better rate performance and higher cyclic capacity of 150, 106, and 50 mAh g -1 under 0.2 C at 50, 40, and 30 °C. This strategy of employing Mg 2 B 2 O 5 nanowires provides the design guidelines of assembling multifunctional SSLIBs with high ionic conductivity, excellent mechanical properties, and flame-retardant performance at the same time.

Human exposure to brominated flame retardants through the consumption of fish and shellfish in Tarragona County (Catalonia, Spain).

PubMed

Trabalón, Laura; Vilavert, Lolita; Domingo, José L; Pocurull, Eva; Borrull, Francesc; Nadal, Martí

2017-06-01

The concentrations of 19 brominated flame retardants (BFRs) (8 polybrominated diphenyl ethers (PBDEs), 8 methoxylated PBDEs (MeO-PBDEs) and 3 emerging flame retardants) were determined in 10 species of fish and shellfish widely consumed in Tarragona County (Catalonia, Spain), by pressurized liquid extraction followed by gas chromatography coupled to tandem mass spectrometry. A higher occurrence of PBDEs was found in all the analyzed samples, while MeO-PBDEs were only detected in a few ones and the levels of emerging pollutants were relatively low. In contrast, hexabromobenzene was found in almost all samples at concentrations ranging between non detected and 0.2 ng g -1 wet weight (w.w.). Salmon, sole, hake, cod and tuna showed the highest concentrations of ΣPBDEs (>0.8 ng g -1  w.w.), while mussel was the species with the highest level of MeO-PBDEs (1.5 ng g -1  w.w.). The dietary exposure of BFRs through consumption of these 10 species of fish and shellfish by the population of Tarragona County was estimated for different subpopulations, classified according to age and gender. Furthermore, calculations were performed in upper-, middle- and lower-bound risk scenarios. According to our data, the current concentrations of BFRs in fish and shellfish suggest no significant health risks for the consumers. Copyright © 2016 Elsevier Ltd. All rights reserved.

The GhTT2_A07 gene is linked to the brown colour and natural flame retardancy phenotypes of Lc1 cotton (Gossypium hirsutum L.) fibres.

PubMed

Hinchliffe, Doug J; Condon, Brian D; Thyssen, Gregory; Naoumkina, Marina; Madison, Crista A; Reynolds, Michael; Delhom, Christopher D; Fang, David D; Li, Ping; McCarty, Jack

2016-10-01

Some naturally coloured brown cotton fibres from accessions of Gossypium hirsutum L. can be used to make textiles with enhanced flame retardancy (FR). Several independent brown fibre loci have been identified and mapped to chromosomes, but the underlying genes have not yet been identified, and the mechanism of lint fibre FR is not yet fully understood. In this study, we show that both the brown colour and enhanced FR of the Lc1 lint colour locus are linked to a 1.4Mb inversion on chromosome A07 that is immediately upstream of a gene with similarity to Arabidopsis TRANSPARENT TESTA 2 (TT2). As a result of the alternative upstream sequence, the transcription factor GhTT2_A07 is highly up-regulated in developing fibres. In turn, genes in the phenylpropanoid metabolic pathway are activated, leading to biosynthesis of proanthocyanidins and accumulation of inorganic elements. We show that enhanced FR and anthocyanin precursors appear in developing brown fibres well before the brown colour is detectible, demonstrating for the first time that the polymerized proanthocyanidins that constitute the brown colour are not the source of enhanced FR. Identifying the particular colourless metabolite that provides Lc1 cotton with enhanced FR could help minimize the use of synthetic chemical flame retardant additives in textiles. © The Author 2016. Published by Oxford University Press on behalf of the Society for Experimental Biology.

Occurence of legacy and novel brominated flame retardants in food and feed in France for the period 2014 to 2016.

PubMed

Vénisseau, A; Bichon, E; Brosseaud, A; Vaccher, V; Lesquin, E; Larvor, F; Durand, S; Dervilly-Pinel, G; Marchand, P; Le Bizec, B

2018-09-01

Determination of the occurrence levels of legacy and novel BFRs is today required to better understand the trends of BFRs contamination in food consecutive to the EU PBDEs restrictions and to proceed to a recent human food exposure in parallel. Therefore, concentrations of a large set of brominated flame retardants (BFRs) (n = 27) including PBDEs, HBCDDs, TBBPA and novel flame retardants (nBFRs) have been determined in more than 600 food and feed samples collected between 2014 and 2016 in the context of French monitoring plans. Although legacy BFRs had already been studied in France, such a survey constituted the very first determination of nBFRs occurrence in foodstuffs at the national level. The concentration levels measured in fish and fish products were in general higher than in the other food categories. PBDEs were detected in 70% of the samples and were observed as the most abundant congeners (representing 80% of the sum of the monitored BFRs), while α-HBCDD could also be considered as a predominant congener (up to 26% of the sum of the monitored BFRs in fishes). nBFRs concentration levels were most of the time below the LOQ, except PBT, PBBz and HBBz which were more frequently detected at low levels. Also investigated in the study, BRPs exhibited high concentration levels in crustaceous (maximum value > 2700 pg/g ww). Copyright © 2018 Elsevier Ltd. All rights reserved.

Aryl- and alkyl-phosphorus-containing flame retardants induced mitochondrial impairment and cell death in Chinese hamster ovary (CHO-k1) cells.

PubMed

Huang, Chao; Li, Na; Yuan, Shengwu; Ji, Xiaoya; Ma, Mei; Rao, Kaifeng; Wang, Zijian

2017-11-01

Phosphorus-containing flame retardants (PFRs) are increasingly in demand worldwide as replacements for brominated flame retardants (BFRs), but insufficient available toxicological information on PFRs makes assessing their health risks challenging. Mitochondria are important targets of various environmental pollutants, and mitochondrial dysfunction may lead to many common diseases. In the present study, mitochondria impairment-related endpoints were measured by a high content screening (HCS) assay for 11 selected non-halogen PFRs in Chinese hamster ovary (CHO-k1) cells. A cluster analysis was used to categorize these PFRs into three groups according to their structural characteristics and results from the HCS assay. Two groups, containing long-chain alkyl-PFRs and all aryl-PFRs, were found to cause mitochondrial impairment but showed different mechanisms of toxicity. Due to the high correlation between cell death and mitochondrial impairment, two PFRs with different structures, trihexyl phosphate (THP) and cresyl diphenyl phosphate (CDP), were selected and compared with chlorpyrifos (CPF) to elucidate their mechanism of inducing cell death. THP (an alkyl-PFR) was found to utilize a similar pathway as CPF to induce apoptosis. However, cell death induced by CDP (an aryl-PFR) was different from classical necrosis based on experiments to discriminate among the different modes of cell death. These results confirm that mitochondria might be important targets for some PFRs and that differently structured PFRs could function via distinct mechanisms of toxicity. Copyright © 2017 Elsevier Ltd. All rights reserved.

Inhibition of O-linked N-acetylglucosamine transferase activity in PC12 cells - A molecular mechanism of organophosphate flame retardants developmental neurotoxicity.

PubMed

Gu, Yuxin; Yang, Yu; Wan, Bin; Li, Minjie; Guo, Liang-Hong

2018-06-01

Organophosphate flame retardants (OPFRs), as alternatives of brominated flame retardants, can cause neurodevelopmental effects similar to organophosphate pesticides. However, the molecular mechanisms underlying the toxicity remain elusive. O-linked N-acetylglucosamine (O-GlcNAc) transferase (OGT) regulates numerous neural processes through the O-GlcNAcylation modification of nuclear and cytoplasmic proteins. In this study, we aimed to investigate the molecular mechanisms accounting for the developmental neurotoxicity of OPFRs by identifying potential targets of OPFRs and the attendant effects. Twelve OPFRs were evaluated for inhibition of OGT activity using an electrochemical biosensor. Their potency differed with substituent groups. The alkyl group substituted OPFRs had no inhibitory effect. Instead, the six OPFRs substituted with aromatic or chlorinated alkyl groups inhibited OGT activity significantly, with tri-m-cresyl phosphate (TCrP) being the strongest. The six OPFRs (0-100 μM exposure) also inhibited OGT activity in PC12 cells and decreased protein O-GlcNAcylation level. Inhibition of OGT by OPFRs might be involved in the subsequent toxic effects, including intracellular reactive oxygen species (ROS), calcium level, as well as cell proliferation and autophagy. Molecular docking of the OGT/OPFR complexes provided rationales for the difference in their structure-dependent inhibition potency. Our findings may provide a new biological target of OPFRs in their neurotoxicological actions, which might be a major molecular mechanism of OPFRs developmental neurotoxicity. Copyright © 2018 Elsevier Inc. All rights reserved.

Flexible Superhydrophobic and Superoleophilic MoS2 Sponge for Highly Efficient Oil-Water Separation.

PubMed

Gao, Xiaojia; Wang, Xiufeng; Ouyang, Xiaoping; Wen, Cuie

2016-06-02

Removal of oils and organic solvents from water is an important global challenge for energy conservation and environmental protection. Advanced sorbent materials with excellent sorption capacity need to be developed. Here we report on a superhydrophobic and superoleophilic MoS2 nanosheet sponge (SMS) for highly efficient separation and absorption of oils or organic solvents from water. This novel sponge exhibits excellent absorption performance through a combination of superhydrophobicity, high porosity, robust stability in harsh conditions (including flame retardance and inertness to corrosive and different temperature environments) and excellent mechanical properties. The dip-coating strategy proposed for the fabrication of the SMS, which does not require a complicated process or sophisticated equipment, is very straightforward and easy to scale up. This finding shows promise for water remediation and oil recovery.

TSCA Work Plan Chemical Technical Supplement – Physicochemical Properties and Environmental Fate of the Brominated Phthalates Cluster (BPC) Chemicals

EPA Pesticide Factsheets

TSCA Work Plan Chemical Technical Supplement – Physicochemical Properties and Environmental Fate of the Brominated Phthalates Cluster (BPC) Chemicals -- Brominated Phthalates Cluster Flame Retardants.

40 CFR 721.775 - Brominated aromatic com-pound (generic name).

Code of Federal Regulations, 2011 CFR

2011-07-01

...) TOXIC SUBSTANCES CONTROL ACT SIGNIFICANT NEW USES OF CHEMICAL SUBSTANCES Significant New Uses for.... Requirements as specified in § 721.80 (j) (use as an additive flame retardant for plastics) and (q). (iv...

Effect of basalt fibres reinforcement and aluminum trihydrate on the thermal properties of intumescent fire retardant coatings

NASA Astrophysics Data System (ADS)

Yasir, Muhammad; Amir, Norlaili Binti; Ahmad, Faiz; Syahirah Rodzhan, N.

2017-08-01

This research is carried out in order to study the synergistic effect of aluminium trihydrate and basalt fibres on the properties of fire resistant intumescent coatings. Intumescent fire retardant coatings were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder along with curing agent. Furthermore, individual and combinations of aluminium trihydrate and basalt fibres was incorporated in the formulations to analyse mechanical and chemical properties of the coatings. Char expansion was observed using furnace test, thermogravimetric analysis was used to determine residual weight, X-Ray Diffraction was performed to investigate compounds present in the char, shear test was conducted to determine char strength and scanning electron microscopy analysis was performed to observe morphology of the burnt char. From the microscopic investigation it was concluded that the dense structure of the char increased the char integrity by adding basalt and aluminium trihydrate as fillers. X-Ray Diffraction results shows the presence boron phosphate, and boric acid which enhanced the thermal performance of the coating up to 800°C. From the Thermogravimetric analysis it was concluded that the residual weight of the char was increased up to 34.9 % for IC-B2A4 which enhanced thermal performance of intumescent coating.

Brominated Flame Retardants.

EPA Science Inventory

BFRs belong to a growing group of organohalogen chemicals. They can be highly persistent, bioaccumulative and cause adverse effects in humans and wildlife. Although some BFRs are banned or voluntarily withdrawn from usage by the manufacturer, emerging and existing BFRs continue t...

BRFS: TOXICOLOGY AND RISK

EPA Science Inventory

Brominated flame retardants are a large class of diverse chemicals which are being used in increasing amounts world wide to protect against fires. The major classes include the polybrominated diphenyl ethers (PBDEs), the brominated bisphenols (e.g., tetrabromobisphenol A, TBBPA)...

Acute and Developmental Behavioral Effects of Flame ...

EPA Pesticide Factsheets

As polybrominated diphenyl ethers are phased out, numerous compounds are emerging as potential replacement flame retardants for use in consumer and electronic products. Little is known, however, about the neurobehavioral toxicity of these replacements. This study evaluated the neurobehavioral effects of acute or developmental exposure to t-butylphenyl diphenyl phosphate (BPDP), 2-ethylhexyl diphenyl phosphate (EHDP), isodecyl diphenyl phosphate (IDDP), isopropylated phenyl phosphate (IPP), tricresyl phosphate (TMPP; also abbreviated TCP), triphenyl phosphate (TPHP; also abbreviated TPP), tetrabromobisphenol A (TBBPA), tris (2-chloroethyl) phosphate (TCEP), tris (1,3-dichloroisopropyl) phosphate (TDCIPP; also abbreviated TDCPP), tri-o-cresyl phosphate (TOCP), and 2,2-,4,4’-tetrabromodiphenyl ether (BDE-47) in zebrafish (Danio rerio) larvae. Larvae (n≈24 per dose per compound) were exposed to test compounds (0.4 - 120 µM) at sub-teratogenic concentrations either developmentally or acutely, and locomotor activity was assessed at 6 days post fertilization. When given developmentally, all chemicals except BPDP, IDDP and TBBPA produced behavioral effects. When given acutely, all chemicals produced behavioral effects, with TPHP, TBBPA, EHDP, IPP, and BPDP eliciting the most effects at the most concentrations. The results indicate that these replacement flame retardants may have developmental or pharmacological effects on the vertebrate nervous system. This study

Responses of the rotifer Brachionus plicatilis to flame retardant (BDE-47) stress.

PubMed

Jian, Xiaoyang; Tang, Xuexi; Xu, Ningning; Sha, Jingjing; Wang, You

2017-03-15

A series of short-term toxicological tests were conducted on the rotifer Brachionus plicatilis to assess the toxicity of the flame retardant 2,2',4,4'-tetrabrominated biphenyl ether (BDE-47). BDE-47 increased mortality, morphological damage, and altered population dynamics and fecundity of rotifer. Antioxidant enzymes were differentially changed to maintain the balance between antioxidant and pro-oxidant activity. However, with increases in the concentration of BDE-47, the metabolic and antioxidant activity decreased. Moreover, the reactive oxygen species (ROS) and malondialdehyde contents increased and the ratio between glutathione and glutathione-SH decreased, indicating oxidative stress. The addition of the ROS-inhibitor N-acetylcysteine alleviated the degree of damage and stimulated the activity of xenobiotic-metabolizing and antioxidant system, which suggested that ROS were the most important loop in the stress response. Copyright © 2017 Elsevier Ltd. All rights reserved.

Legacy and emerging brominated flame retardants in China: A review on food and human milk contamination, human dietary exposure and risk assessment.

PubMed

Shi, Zhixiong; Zhang, Lei; Li, Jingguang; Wu, Yongning

2018-05-01

Brominated flame retardants (BFRs) are a large group of widely used chemicals, which have been produced and used since 1970s. As a consequence of substantial and long-term usage, BFRs have been found to be ubiquitous in humans, wildlife, and abiotic matrices around the world. Although several reports have reviewed BFRs contamination in general, none have focused specifically on foods and human milk, and the corresponding dietary exposure. Foods (including human milk) have long been recognized as a major pathway of BFRs intake for non-occupationally exposed persons. This review summarizes most available BFRs data in foods and human milk from China in recent years, and emphasizes several specific aspects, i.e., contamination levels of legacy and emerging BFRs, dietary exposure assessment and related health concerns, comparison between various BFRs, and temporal changes in BFRs contamination. Copyright © 2018 Elsevier Ltd. All rights reserved.

Exposures, Mechanisms, and Impacts of Endocrine-Active Flame Retardants

PubMed Central

Dishaw, Laura; Macaulay, Laura; Roberts, Simon C.; Stapleton, Heather M.

2014-01-01

This review summarizes the endocrine and neurodevelopmental effects of two current-use additive flame retardants (FRs), tris (1,3-dichloro-isopropyl) phosphate (TDCPP) and Firemaster® 550 (FM 550), and the recently phased-out polybrominated diphenyl ethers (PBDEs), all of which were historically or are currently used in polyurethane foam applications. Use of these chemicals in consumer products has led to widespread exposure in indoor environments. PBDEs and their hydroxylated metabolites appear to primarily target the thyroid system, likely due to their structural similarity to endogenous thyroid hormones. In contrast, much less is known about the toxicity of TDCPP and FM550. However, recent in vitro and in vivo studies suggest that both should be considered endocrine disruptors as studies have linked TDCPP exposure with changes in circulating hormone levels, and FM 550 exposure with changes in adipogenic and osteogenic pathways. PMID:25306433

Effect of single flame retardant aluminum tri-hydroxide and boric acid against inflammability and biodegradability of recycled PP/KF composites

NASA Astrophysics Data System (ADS)

Suharty, Neng Sri; Dihardjo, Kuncoro; Handayani, Desi Suci; Firdaus, Maulidan

2016-03-01

Composites rPP/DVB/AA/KF had been reactively synthesized in melt using starting material: recycled polypropylene (rPP), kenaf fiber (KF), multifunctional compound acrylic acid (AA), compatibilizer divinyl benzene (DVB). To improve the inflammability of composites, single flame retardant aluminum tri-hydroxide (ATH) and boric acid (BA) as an additive was added. The inflammability of the composites was tested according to ASTM D635. By using 20% ATH and 5% BA additive in the composites it is effectively inhibiting its time to ignition (TTI). Its burning rate (BR) can be reduced and its heat realease (%HR) decreases. The biodegradability of composites was quantified by its losing weight (LW) of composites after buried for 4 months in the media with rich cellulolytic bacteria. The result shows that the LW of composites in the presence 20% ATH and 5% BA is 6.3%.

Vapor Pressure of Three Brominated Flame Retardants Determined via Knudsen Effusion Method

PubMed Central

Fu, Jinxia; Suuberg, Eric M.

2012-01-01

Brominated flame retardants (BFRs) have been used in a variety of consumer products in the past four decades. The vapor pressures for three widely used BFRs, that is, tetrabromobisphenol A (TBBPA), hexabromocyclododecane (HBCD), and octabromodiphenyl ethers (octaBDEs) mixtures, were determined using the Knudsen effusion method and compared to those of decabromodiphenyl ether (BDE209). The values measured extrapolated to 298.15 K are 8.47 × 10−9, 7.47 × 10−10, and 2.33 × 10−9 Pa, respectively. The enthalpies of sublimation for these BFRs were estimated using the Clausius-Clapeyron equation and are 143.6 ± 0.4, 153.7 ± 3.1, and 150.8 ± 3.2 kJ/mole, respectively. In addition, the enthalpies of fusion and melting temperatures for these BFRs were also measured in the present study. PMID:22213441

Reproductive Outcomes Among Women Exposed to a Brominated Flame Retardant In Utero

PubMed Central

Small, Chanley M.; Murray, Deanna; Terrell, Metrecia L.; Marcus, Michele

2014-01-01

The authors studied 194 women exposed to polybrominated biphenyls (PBB) in utero when their mothers consumed products accidentally contaminated in Michigan in 1973. Generalized estimating equations were used to examine the effect of in utero PBB exposure on adult pregnancy-related outcomes. Compared to those with the lowest exposure (≤1 ppb), those with mid-range (>1–3.16 ppb) and high (≥3.17 ppb) PBB exposure had increased odds of spontaneous abortion with wide confidence intervals (odds ratio [OR] = 2.75, 95% confidence interval [CI] = 0.64–11.79, OR = 4.08, 95% CI = 0.94–17.70; respectively; p for trend = .05). Exposure during infancy to PBB-contaminated breast milk further increased this risk. Time to pregnancy and infertility were not associated with in utero exposure to PBB. Future studies should examine the suggested relationship between spontaneous abortion and other brominated flame retardants. PMID:22014192

Phenols, flame retardants and phthalates in water and wastewater - a global problem.

PubMed

Ayanda, Olushola Sunday; Olutona, Godwin Oladele; Olumayede, Emmanuel G; Akintayo, Cecilia O; Ximba, Bhekumusa J

Organic pollutants in water and wastewater have been causing serious environmental problems. The arbitrary discharge of wastewater by industries, and handling, use, and disposal constitute a means by which phenols, flame retardants (FRs), phthalates (PAEs) and other toxic organic pollutants enter the ecosystem. Moreover, these organic pollutants are not completely removed during treatment processes and might be degraded into highly toxic derivatives, which has led to their occurrence in the environment. Phenols, FRs and PAEs are thus highly toxic, carcinogenic and mutagenic, and are capable of disrupting the endocrine system. Therefore, investigation to understand the sources, pathways, behavior, toxicity and exposure to phenols, FRs and PAEs in the environment is necessary. Formation of different by-products makes it difficult to compare the efficacy of the treatment processes, most especially when other organic matters are present. Hence, high levels of phenols, FRs and PAEs removal could be attained with in-line combined treatment processes.

Chemical alternatives assessment: the case of flame retardants.

PubMed

Howard, Gregory J

2014-12-01

Decisions on chemical substitution are made rapidly and by many stakeholders; these decisions may have a direct impact on consumer exposures, and, when a hazard exists, to consumer risks. Flame retardants (FRs) represent particular challenges, including very high production volumes, designed-in persistence, and often direct consumer exposure. Newer FR products, as with other industrial chemicals, typically lack data on hazard and exposure, and in many cases even basic information on structure and use in products is unknown. Chemical alternatives assessment (CAA) provides a hazard-focused approach to distinguishing between possible substitutions; variations on this process are used by several government and numerous corporate entities. By grouping chemicals according to functional use, some information on exposure potential can be inferred, allowing for decisions based on those hazard properties that are most distinguishing. This approach can help prevent the "regrettable substitution" of one chemical with another of equal, or even higher, risk. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of cuprous oxide with different sizes on thermal and combustion behaviors of unsaturated polyester resin.

PubMed

Hou, Yanbei; Hu, Weizhao; Gui, Zhou; Hu, Yuan

2017-07-15

Cuprous oxide (Cu 2 O) as an effective catalyst has been applied to enhance the fire safety of unsaturated polyester resin (UPR), but the particle size influence on combustion behaviors has not been previously reported. Herein, the UPR/Cu 2 O composites (metal oxide particles with average particle-size of 10, 100, and 200nm) were successfully synthesized by thermosetting process. The effects of Cu 2 O with different sizes on thermostability and combustion behaviors of UPR were characterized by TGA, MCC, TG-IR, FTIR, and SSTF. The results revel that the addition of Cu 2 O contributes to sufficient decomposition of oxygen-containing compounds, which is beneficial to the release of nontoxic compounds. The smallest-sized Cu 2 O performs the excellent catalytic decomposition effect and promotes the complete combustion of UPR, which benefits the enhancement of fire safety. While the other additives retard pyrolysis process and yield more char residue, and thus the flame retardancy of UPR composites was improved. Therefore, catalysis plays a major role for smaller-sized particles during thermal decomposition of matrix, while flame retarded effect became gradual distinctly for the larger-sized additives. Copyright © 2017 Elsevier B.V. All rights reserved.

Assessment of dermal hazard from acid burns with fire retardant garments in a full-size simulation of an engulfment flash fire.

PubMed

Mackay, Christopher E; Vivanco, Stephanie N; Yeboah, George; Vercellone, Jeff

2016-09-01

There have been concerns that fire-derived acid gases could aggravate thermal burns for individuals wearing synthetic flame retardant garments. A comparative risk assessment was performed on three commercial flame retardant materials with regard to relative hazards associated with acidic combustion gases to skin during a full engulfment flash fire event. The tests were performed in accordance with ASTM F1930 and ISO 13506: Standard Test Method for Evaluation of Flame Resistant Clothing for Protection against Fire Simulations Using an Instrumented Manikin. Three fire retardant textiles were tested: an FR treated cotton/nylon blend, a low Protex(®) modacrylic blend, and a medium Protex(®) modacrylic blend. The materials, in the form of whole body coveralls, were subjected to propane-fired flash conditions of 84kW/m(2) in a full sized simulator for a duration of either 3 or 4s. Ion traps consisting of wetted sodium carbonate-impregnated cellulose in Teflon holders were placed on the chest and back both above and under the standard undergarments. The ion traps remained in position from the time of ignition until 5min post ignition. Results indicated that acid deposition did increase with modacrylic content from 0.9μmol/cm(2) for the cotton/nylon, to 12μmol/cm(2) for the medium modacrylic blend. The source of the acidity was dominated by hydrogen chloride. Discoloration was inversely proportional to the amount of acid collected on the traps. A risk assessment was performed on the potential adverse impact of acid gases on both the skin and open wounds. The results indicated that the deposition and dissolution of the acid gases in surficial fluid media (perspiration and blood plasma) resulted in an increase in acidity, but not sufficient to induce irritation/skin corrosion or to cause necrosis in open third degree burns. Copyright © 2016 The Authors. Published by Elsevier Ltd.. All rights reserved.

Potential Role of Pet Cats As a Sentinel Species for Human Exposure to Flame Retardants

PubMed Central

Henríquez-Hernández, Luis A.; Carretón, Elena; Camacho, María; Montoya-Alonso, José Alberto; Boada, Luis D.; Bernal Martín, Verónica; Falcón Cordón, Yaiza; Falcón Cordón, Soraya; Zumbado, Manuel; Luzardo, Octavio P.

2017-01-01

Flame retardants are a wide group of chemicals used by the industry to avoid combustion of materials. These substances are commonly found in plastics, electronic equipment, fabrics, and in many other everyday articles. Subsequently, ubiquitous environmental contamination by these common chemical is frequently reported. In the present study, we have evaluated the level of exposure to polychlorinated biphenyls (PCBs), brominated diphenyl ethers (BDEs), and organophosphorous flame retardants (OPFRs) in pet cats through the analysis of their serum. We also analyzed the level exposure to such chemicals in a series of 20 cat owners, trying to disclose the role of pet cats as sentinel species of human exposure to FRs. Our results showed that PCBs, banned 40 years ago, showed the lowest levels of exposure, followed by BDEs—banned recently. Congeners PCB-138 and PCB-180 were detected in ≥50% of the series, while BDE-47 was detected in near 90% of the pet cats. On the other hand, the highest levels were that of OPFRs, whose pattern of detection was similar to that observed in humans, thus suggesting a potential role of cats as a sentinel species for human exposure to these currently used FRs. Six out of 11 OPFRs determined [2-ethylhexyldiphenyl phosphate, tributylphosphate, triisobutylphosphate, triphenylphosphate, tris (2-chloroethyl) phosphate, and tris (2-chloroisopropyl) phosphate] were detected in 100% of the samples. It will be interesting to perform future studied aimed to elucidating the potential toxicological effects of these highly detected chemicals both, in cats and humans. PMID:28620612

Brominated flame retardants in the indoor environment - Comparative study of indoor contamination from three countries.

PubMed

Venier, Marta; Audy, Ondřej; Vojta, Šimon; Bečanová, Jitka; Romanak, Kevin; Melymuk, Lisa; Krátká, Martina; Kukučka, Petr; Okeme, Joseph; Saini, Amandeep; Diamond, Miriam L; Klánová, Jana

2016-09-01

Concentrations of more than 20 brominated flame retardants (FRs), including polybrominated diphenyl ethers (PBDEs) and emerging FRs, were measured in air, dust and window wipes from 63 homes in Canada, the Czech Republic and the United States in the spring and summer of 2013. Among the PBDEs, the highest concentrations were generally BDE-209 in all three matrices, followed by Penta-BDEs. Among alternative FRs, EHTBB and BEHTBP were detected at the highest concentrations. DBDPE was also a major alternative FR detected in dust and air. Bromobenzenes were detected at lower levels than PBDEs and other alternative FRs; among the bromobenzenes, HBB and PBEB were the most abundant compounds. In general, FR levels were highest in the US and lowest in the Czech Republic - a geographic trend that reflects the flame retardants' market. No statistically significant differences were detected between bedroom and living room FR concentrations in the same house (n=10), suggesting that sources of FRs are widespread indoors and mixing between rooms. The concentrations of FRs in air, dust, and window film were significantly correlated, especially for PBDEs. We found a significant relationship between the concentrations in dust and window film and in the gas phase for FRs with log KOA values <14, suggesting that equilibrium was reached for these but not compounds with log KOA values >14. This hypothesis was confirmed by a large discrepancy between values predicted using a partitioning model and the measured values for FRs with log KOA values >14. Copyright © 2016 Elsevier Ltd. All rights reserved.

Emerging brominated flame retardants and dechlorane-related compounds in European eels (Anguilla anguilla) from Latvian lakes.

PubMed

Zacs, D; Ikkere, L E; Bartkevics, V

2018-04-01

Fifteen halogenated flame retardants (HFRs) including seven emerging brominated flame retardants (EBFRs) and eight dechlorane-related compounds (DRCs) were analyzed in eels (Anguilla anguilla) sampled from five Latvian lakes. Out of the seven EBFRs, hexabromocyclododecane (HBCD) and decabromodiphenyl ethane (DBDPE) were found in eels in quantifiable concentrations, up to 6.58 and 33.0 ng g -1 lipid weight (l.w.), respectively. The mean total concentration of DRCs (∑ DRC ) in the samples was 0.62 ng g -1 l.w. and the geographical distribution of DRC contamination was nearly uniform among the selected lakes. Dechlorane 602 (Dec 602) was the predominant component, whereas the composition of mixture containing syn- and anti-Dechlorane Plus (DP) stereoisomers showed a pronounced enrichment of the anti-DP isomer and was close to the composition of OxyChem ® DP commercial product. The determined concentrations of HFRs were lower than in other studies of aquatic biota from Europe and Asia, and the obtained results reflect the acceptable environmental status of Latvian lakes with regard to the total content of HBCD (∑ HBCD ), considering the environmental quality standards (EQS) stated in the Directive 2013/39/EU. The highest ∑ HBCD levels were observed in eels from lakes corresponding to the industrialization of those areas, while the results of principal component analysis (PCA) showed that the concentration of HBCD depended on the particular sampling lake, reflecting non-uniform contamination of the Latvian environment with this EBFR. Copyright © 2018 Elsevier Ltd. All rights reserved.

Concentrations in air of organobromine, organochlorine and organophosphate flame retardants in Toronto, Canada

NASA Astrophysics Data System (ADS)

Shoeib, Mahiba; Ahrens, Lutz; Jantunen, Liisa; Harner, Tom

2014-12-01

Concentrations of organobromine (BFRs), organochlorine (CFRs) and organophosphate esters flame retardants and plasticizers (PFRs) in air were monitored for over one year at an urban site in Toronto, Canada during 2010-2011. The mean value for polybrominated diphenyl ethers (BDEs) (gas + particle phase) was 38 pg/m3 with BDE-47 and BDE-99 as the dominant congeners. The mean concentrations in air for ∑non-BDE (BFRs and CFRs), was 9.6 pg/m3 - about four times lower than the BDEs. The brominated FRs: TBP-AE, BTBPE, EH-TBB, BEH-TEBP and the chlorinated syn- and anti-DP were detected frequently, ranging from 87% to 96%. Highest concentrations in air among all flame retardant classes were observed for the Σ-PFRs. The yearly mean concentration in air for ΣPFRs was 2643 pg/m3 with detection frequency higher than 80%. Except for TBP-AE and b- DBE-DBCH, non-BDEs (BFRs, CFRs and PFRs) were mainly associated with the particle phase. BDE concentrations in air were positively correlated with temperature indicating that volatilization from local sources was an important factor controlling levels in air. This correlation did not hold for most BFRs, CFRs and PFRs which were mainly on particles. For these compounds, air concentrations in Toronto are likely related to emissions from point sources and advective inputs. This study highlights the importance of urban air monitoring for FRs. Urban air can be considered a sentinel for detecting changes in the use and application of FRs in commercial products.

Transcriptomic and metabolomic approaches to investigate the molecular responses of human cell lines exposed to the flame retardant hexabromocyclododecane (HBCD).

PubMed

Zhang, Jinkang; Williams, Timothy D; Abdallah, Mohamed Abou-Elwafa; Harrad, Stuart; Chipman, James K; Viant, Mark R

2015-12-01

The potential for human exposure to the brominated flame retardant, hexabromocyclododecane (HBCD) has given rise to health concerns, yet there is relatively limited knowledge about its possible toxic effects and the underlying molecular mechanisms that may mediate any impacts on health. In this study, unbiased transcriptomic and metabolomic approaches were employed to investigate the potential molecular changes that could lead to the toxicity of HBCD under concentrations relevant to human exposure conditions using in vitro models. A concentration-dependent cytotoxic effect of HBCD to A549 and HepG2/C3A cells was observed based on MTT assays or CCK-8 assays with EC50 values of 27.4 μM and 63.0 μM, respectively. Microarray-based transcriptomics and mass spectrometry-based metabolomics revealed few molecular changes in A549 cells or HepG2/C3A cells following a 24-hour exposure to several sub-lethal concentrations (2 to 4000 nM) of HBCD. Quantification of the level of HBCD in the HepG2/C3A exposed cells suggested that the flame retardant was present at concentrations several orders of magnitude higher than those reported to occur in human tissues. We conclude that at the concentrations known to be achievable following exposure in humans, HBCD exhibits no detectable acute toxicity in A549 cells, representative of the lung, or in HepG2/C3A cells, that are hepatocytes with some xenobiotic metabolic capacity. Copyright © 2015 Elsevier B.V. All rights reserved.

In vitro endocrine disruption and TCDD-like effects of three novel brominated flame retardants: TBPH, TBB, & TBCO.

PubMed

Saunders, David M V; Higley, Eric B; Hecker, Markus; Mankidy, Rishikesh; Giesy, John P

2013-11-25

The novel brominated flame retardants (NBFRs), 2-ethylhexyl-2,3,4,5-tetrabromobenzoate (TBB), Bis(2-ethylhexyl)-2,3,4,5-tetrabromophtalate (TBPH), and 1,2,5,6-tetrabromocyclooctane (TBCO) are components of flame retardant mixtures including Firemaster 550 and Saytex BC-48. Despite the detection of these NBFRs in environmental and biotic matrices, studies regarding their toxicological effects are poorly represented in the literature. The present study examined endocrine disruption by these three NBFRs using the yeast YES/YAS reporter assay and the mammalian H295R steroidogenesis assay. Activation of the aryl hydrocarbon receptor (AhR) was also assessed using the H4IIE reporter assay. The NBFRs produced no TCDD-like effects in the H4IIE assay or agonistic effects in the YES/YAS assays. TBB produced a maximal antiestrogenic effect of 62% at 0.5mgL(-1) in the YES assay while TBPH and TBCO produced maximal antiandrogenic effects of 74% and 59% at 300mgL(-1) and 1500mgL(-1), respectively, in the YAS assay. Significant effects were also observed in the H295R assay. At 0.05mgL(-1), 15mgL(-1), and 15mgL(-1) TBB, TBPH, and TBCO exposures, respectively resulted in a 2.8-fold, 5.4-fold, and 3.3-fold increase in concentrations of E2. This is one of the first studies to demonstrate the in vitro endocrine disrupting potentials of TBB, TBPH, and TBCO. Copyright © 2013 Elsevier Ireland Ltd. All rights reserved.

Assessing the persistence, bioaccumulation potential and toxicity of brominated flame retardants: data availability and quality for 36 alternative brominated flame retardants.

PubMed

Stieger, Greta; Scheringer, Martin; Ng, Carla A; Hungerbühler, Konrad

2014-12-01

Polybrominated diphenylethers (PBDEs) and hexabromocyclododecane (HBCDD) are major brominated flame retardants (BFRs) that are now banned or under restrictions in many countries because of their persistence, bioaccumulation potential and toxicity (PBT properties). However, there is a wide range of alternative BFRs, such as decabromodiphenyl ethane and tribromophenol, that are increasingly used as replacements, but which may possess similar hazardous properties. This necessitates hazard and risk assessments of these compounds. For a set of 36 alternative BFRs, we searched 25 databases for chemical property data that are needed as input for a PBT assessment. These properties are degradation half-life, bioconcentration factor (BCF), octanol-water partition coefficient (Kow), and toxic effect concentrations in aquatic organisms. For 17 of the 36 substances, no data at all were found for these properties. Too few persistence data were available to even assess the quality of these data in a systematic way. The available data for Kow and toxicity show surprisingly high variability, which makes it difficult to identify the most reliable values. We propose methods for systematic evaluations of PBT-related chemical property data that should be performed before data are included in publicly available databases. Using these methods, we evaluated the data for Kow and toxicity in more detail and identified several inaccurate values. For most of the 36 alternative BFRs, the amount and the quality of the PBT-related property data need to be improved before reliable hazard and risk assessments of these substances can be performed. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effects of the brominated flame retardants hexabromocyclododecane (HBCDD), and tetrabromobisphenol A (TBBPA), on hepatic enzymes and other biomarkers in juvenile rainbow trout and feral eelpout.

PubMed

Ronisz, D; Finne, E Farmen; Karlsson, H; Förlin, L

2004-08-25

Brominated flame retardants (BFRs) leak out in the environment, including the aquatic one. Despite this, sublethal effects of these chemicals are poorly investigated in fish. In this study, a screening of selected biomarkers in juvenile rainbow trout (Oncorhynchus mykiss) and feral eelpout (Zoarces viviparus) was performed after exposure to hexabromocyclododecane (HBCDD) and tetrabromobisphenol A (TBBPA). Rainbow trout was injected intraperitoneally (i.p.) with HBCDD or TBBPA. Two out of four short-term experiments with HBCDD showed an increase in the activity of catalase. A 40% increase in liver somatic index (LSI) could be observed after 28 days. HBCDD did also seem to have an inhibitory effect on CYP1A's activity (ethoxyresorufin-O-deethylase (EROD)). A putative peroxisome proliferating activity of the compound was investigated without giving a definite answer. HBCDD did not seem to be estrogenic or genotoxic. TBBPA increased the activity of glutathione reductase (GR) after 4, 14 and 28 days in rainbow trout suggesting a possible role of this compound in inducing oxidative stress. The compound did not seem to be estrogenic. TBBPA seemed to compete with the artificial substrate ethoxyresorufin in vitro, during the EROD assay. In eelpout, only one 5 days in vivo experiment was performed. Neither of the compounds gave rise to any effect in this fish. This was the first screening of sublethal effects of the two chemicals in fish, using high doses. Our results indicate that there is a need for further studies of long-term, low-dose effects of these two widely used flame retardants.

Evaluating the Bioaccessibility of Flame Retardants in House Dust Using an In Vitro Tenax Bead-Assisted Sorptive Physiologically Based Method

PubMed Central

2015-01-01

Exposure to house dust is a significant source of exposure to flame retardant chemicals (FRs), particularly in the US. Given the high exposure there is a need to understand the bioaccessibility of FRs from dust. In this study, Tenax beads (TA) encapsulated within a stainless steel insert were used as an adsorption sink to estimate the dynamic absorption of a suite of FRs commonly detected in indoor dust samples (n = 17), and from a few polyurethane foam samples for comparison. Organophosphate flame retardants (OPFRs) had the highest estimated bioaccessibility (∼80%) compared to brominated compounds (e.g., PBDEs), and values generally decreased with increasing Log Kow, with <30% bioaccessibility measured for BDE209. These measurements were in very close agreement with reported PBDE bioavailability measures from an in vivo rat exposure study using indoor dust. The bioaccessibility of very hydrophobic FRs (Log Kow > 6) in foam was much less than that in house dust, and increasing bioaccessibility was observed with decreasing particle size. In addition, we examined the stability of more labile FRs containing ester groups (e.g., OPFRs and 2-ethylhexyl-tetrabromo-benzoate (EH-TBB)) in a mock-digestive fluid matrix. No significant changes in the OPFR concentrations were observed in this fluid; however, EH-TBB was found to readily hydrolyze to tetrabromobenzoic acid (TBBA) in the intestinal fluid in the presence of lipases. In conclusion, our study demonstrates that the bioaccessibility and stability of FRs following ingestion varies by chemical and sample matrix and thus should be considered in exposure assessments. PMID:25330458

Extent and mechanisms of brominated flame retardant emissions from waste soft furnishings and fabrics: A critical review.

PubMed

Stubbings, William A; Harrad, Stuart

2014-10-01

Use of brominated flame retardants (BFRs) in soft furnishings has occurred for over thirty years with the phase out of polybrominated diphenyl ethers (PBDEs) and hexabromocyclododecane (HBCD) only relatively recently begun. As products treated with BFRs reach the end of their lifecycle they enter the waste stream, thereby constituting an important and increasing reservoir of these chemicals. This review highlights the dearth of data on the extent and potential mechanisms of BFR emissions from waste soft furnishings. However, insights into what may occur are provided by scrutiny of the larger (though still incomplete) database related to BFR emissions from electronic waste (e-waste). In many countries, municipal landfills have historically been the primary disposal method of waste consumer products and therefore represent a substantial reservoir of BFRs. Published data for BFR emissions to both air and water from landfill and other waste disposal routes are collated, presented and reviewed. Reported concentrations of PBDEs in landfill leachate range considerably from <1ngL(-1) to 133,000ngΣPBDEL(-1). In addition to direct migration of BFRs from waste materials; there is evidence that some higher brominated flame retardants are able to undergo degradation and debromination during waste treatment, that in some instances may lead to the formation of more toxic and bioavailable compounds. We propose that waste soft furnishings be treated with the same concern as e-waste, given its potential as a reservoir and source of environmental contamination with BFRs. Copyright © 2014 Elsevier Ltd. All rights reserved.

Legacy and emerging halogenated flame retardants in the middle and lower stream of the Yellow River.

PubMed

Su, Xianfa; Li, Qilu; Feng, Jinglan; Guo, Liya; Sun, Jianhui

2017-12-01

Halogenated flame retardants (HFRs), mainly encompassing polybrominated diphenylethers (PBDEs), dechlorane plus (DP) and emerging bromine flame retardants (EBFRs), are widely employed nowadays in daily lives. However, limited knowledge has been gained to date on the concentrations and distributions of HFRs in particular within certain regions. In the present study, legacy and emerging HFRs were systematically measured in suspended particle matter (SPM) and sediments collected in 2014 from the middle and lower reach of the Yellow River in Henan province. The total concentrations of HFRs in SPM among the three seasons were 42.2±91.2ngg -1 , which was far higher than the corresponding values of HFRs in sediments (1.82±2.94ngg -1 ). In this study, PBDEs, DP and EBFRs in sediment almost exhibited relatively lower levels as compared to those found in other studies, where the limited usage of HFRs in the middle and lower stream of the Yellow River was probably the major impact factor. EBFR was the predominate pollutant from SPM and sediments in most of the sampling sites, suggesting that EBFRs were widely used nowadays as substitute materials of 'old' FRs. The mean concentration values of DBDPE/BDE-209 in SPM and sediments were apparently higher than those of previous studies. Furthermore, it is interesting to reveal that herein almost all of the HFR concentrations were unrelated to the population and GDP, which might be attributed to the characteristics of 'elevated stream' of the Yellow River as well as the complex river systems in Henan province. Copyright © 2017 Elsevier B.V. All rights reserved.

An Aqueous Inorganic Polymer Binder for High Performance Lithium–Sulfur Batteries with Flame-Retardant Properties

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhou, Guangmin; Liu, Kai; Fan, Yanchen

Lithium–sulfur (Li–S) batteries are regarded as promising next-generation high energy density storage devices for both portable electronics and electric vehicles due to their high energy density, low cost, and environmental friendliness. However, there remain some issues yet to be fully addressed with the main challenges stemming from the ionically insulating nature of sulfur and the dissolution of polysulfides in electrolyte with subsequent parasitic reactions leading to low sulfur utilization and poor cycle life. The high flammability of sulfur is another serious safety concern which has hindered its further application. Herein, an aqueous inorganic polymer, ammonium polyphosphate (APP), has been developedmore » as a novel multifunctional binder to address the above issues. The strong binding affinity of the main chain of APP with lithium polysulfides blocks diffusion of polysulfide anions and inhibits their shuttling effect. The coupling of APP with Li ion facilitates ion transfer and promotes the kinetics of the cathode reaction. Moreover, APP can serve as a flame retardant, thus significantly reducing the flammability of the sulfur cathode. In addition, the aqueous characteristic of the binder avoids the use of toxic organic solvents, thus significantly improving safety. As a result, a high rate capacity of 520 mAh g –1 at 4 C and excellent cycling stability of ~0.038% capacity decay per cycle at 0.5 C for 400 cycles are achieved based on this binder. In conclusion, this work offers a feasible and effective strategy for employing APP as an efficient multifunctional binder toward building next-generation high energy density Li–S batteries.« less

An Aqueous Inorganic Polymer Binder for High Performance Lithium–Sulfur Batteries with Flame-Retardant Properties

PubMed Central

2018-01-01

Lithium–sulfur (Li–S) batteries are regarded as promising next-generation high energy density storage devices for both portable electronics and electric vehicles due to their high energy density, low cost, and environmental friendliness. However, there remain some issues yet to be fully addressed with the main challenges stemming from the ionically insulating nature of sulfur and the dissolution of polysulfides in electrolyte with subsequent parasitic reactions leading to low sulfur utilization and poor cycle life. The high flammability of sulfur is another serious safety concern which has hindered its further application. Herein, an aqueous inorganic polymer, ammonium polyphosphate (APP), has been developed as a novel multifunctional binder to address the above issues. The strong binding affinity of the main chain of APP with lithium polysulfides blocks diffusion of polysulfide anions and inhibits their shuttling effect. The coupling of APP with Li ion facilitates ion transfer and promotes the kinetics of the cathode reaction. Moreover, APP can serve as a flame retardant, thus significantly reducing the flammability of the sulfur cathode. In addition, the aqueous characteristic of the binder avoids the use of toxic organic solvents, thus significantly improving safety. As a result, a high rate capacity of 520 mAh g–1 at 4 C and excellent cycling stability of ∼0.038% capacity decay per cycle at 0.5 C for 400 cycles are achieved based on this binder. This work offers a feasible and effective strategy for employing APP as an efficient multifunctional binder toward building next-generation high energy density Li–S batteries. PMID:29532026

An Aqueous Inorganic Polymer Binder for High Performance Lithium–Sulfur Batteries with Flame-Retardant Properties

DOE PAGES

Zhou, Guangmin; Liu, Kai; Fan, Yanchen; ...

2018-02-14

Lithium–sulfur (Li–S) batteries are regarded as promising next-generation high energy density storage devices for both portable electronics and electric vehicles due to their high energy density, low cost, and environmental friendliness. However, there remain some issues yet to be fully addressed with the main challenges stemming from the ionically insulating nature of sulfur and the dissolution of polysulfides in electrolyte with subsequent parasitic reactions leading to low sulfur utilization and poor cycle life. The high flammability of sulfur is another serious safety concern which has hindered its further application. Herein, an aqueous inorganic polymer, ammonium polyphosphate (APP), has been developedmore » as a novel multifunctional binder to address the above issues. The strong binding affinity of the main chain of APP with lithium polysulfides blocks diffusion of polysulfide anions and inhibits their shuttling effect. The coupling of APP with Li ion facilitates ion transfer and promotes the kinetics of the cathode reaction. Moreover, APP can serve as a flame retardant, thus significantly reducing the flammability of the sulfur cathode. In addition, the aqueous characteristic of the binder avoids the use of toxic organic solvents, thus significantly improving safety. As a result, a high rate capacity of 520 mAh g –1 at 4 C and excellent cycling stability of ~0.038% capacity decay per cycle at 0.5 C for 400 cycles are achieved based on this binder. In conclusion, this work offers a feasible and effective strategy for employing APP as an efficient multifunctional binder toward building next-generation high energy density Li–S batteries.« less

ANAEROBIC MICROBIAL REDUCTIVE DEBROMINATION OF POLYBROMINATED DIPHENYL ETHERS

EPA Science Inventory

Polybrominated diphenyl ether (PBDE) flame retardants have been detected in sediments, sewage sludge, fish, mammals (including humans), and air throughout the northern hemisphere. While concentrations of PCBs, DDT, and PCDDs in biota are generally decreasing, PBDE concentratio...

DIFFERENTIAL URINARY PROTEIN BINDING OF PBDES IN MICE

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs), commercial chemicals used as flame retardants in consumer goods, have become the focus of increasing scientific research due to their persistent detection in humans and the environment in conjunction with their potential for toxicity. PBDE...

Separator material for electrochemical cells

DOEpatents

Cieslak, Wendy R.; Storz, Leonard J.

1991-01-01

An electrochemical cell characterized as utilizing an aramid fiber as a separator material. The aramid fibers are especially suited for lithium/thionyl chloride battery systems. The battery separator made of aramid fibers possesses superior mechanical strength, chemical resistance, and is flame retardant.

POLYBROMINATED DIPHENYL ETHERS (PBDES) CONTAMINATION OF UNITED STATES FOOD

EPA Science Inventory

Elevated levels of polybrominated diphenyl ethers (PBDEs), a type of brominated flame retardant, were recently detected in United States (U.S.) nursing mothers' milk. These halogenated compounds chemically and toxicologically resemble others such as polychlorinated biphenyls (PC...

2008 Meeting in Germany: Emerging Environmental Contaminants and Current Issues

EPA Science Inventory

This presentation will discuss emerging environmental contaminants that are currently of concern to the U.S. EPA and to other agencies. Emerging contaminants include drinking water disinfection by-products (DBPs), perfluorinated chemicals, pharmaceuticals, flame retardants, benzo...

PBDES: TOXICOLOGY UPDATE

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) have been major commercial products used as flame retardants. While two of the commercial mixtures, Penta and Octa, have either been withdrawn or banned in Europe and the US respectively, the largest volume mixture, Deca, continues to be wi...

Environmental monitoring of selected pesticides and organic chemicals in urban stormwater recycling systems using passive sampling techniques.

PubMed

Page, Declan; Miotliński, Konrad; Gonzalez, Dennis; Barry, Karen; Dillon, Peter; Gallen, Christie

2014-03-01

Water recycling via aquifers has become a valuable tool to augment urban water supplies in many countries. This study reports the first use of passive samplers for monitoring of organic micropollutants in Managed Aquifer Recharge (MAR). Five different configurations of passive samplers were deployed in a stormwater treatment wetland, groundwater monitoring wells and a recovery tank to capture a range of polar and non-polar micropollutants present in the system. The passive samplers were analysed for a suite of pesticides, polycyclic aromatic hydrocarbons (PAHs) and other chemicals. As a result, 17 pesticides and pesticide degradation products, 5 PAHs and 8 other organic chemicals including flame retardants and fragrances were detected in urban stormwater recharging Aquifer Storage and Recovery (ASR) and an Aquifer Storage Transfer and Recovery (ASTR) system. Of the pesticides detected, diuron, metolachlor and chlorpyrifos were generally detected at the highest concentrations in one or more passive samplers, whereas chlorpyrifos, diuron, metolachlor, simazine, galaxolide and triallate were detected in multiple samplers. Fluorene was the PAH detected at the highest concentration and the flame retardant Tris(1-chloro-2-propyl)phosphate was the chemical detected in the greatest abundance at all sites. The passive samplers showed different efficiencies for capture of micropollutants with the Empore disc samplers giving the most reliable results. The results indicate generally low levels of organic micropollutants in the stormwater, as the contaminants detected were present at very low ng/L levels, generally two to four orders of magnitude below the drinking water guidelines (NHMRC, 2011). The efficiency of attenuation of these organic micropollutants during MAR was difficult to determine due to variations in the source water concentrations. Comparisons were made between different samplers, to give a field-based calibration where existing lab-based calibrations were unavailable. Crown Copyright © 2014. Published by Elsevier B.V. All rights reserved.

Investigating A Novel Flame Retardant Known as V6: Measurements in Baby Products, House Dust and Car Dust

PubMed Central

Fang, Mingliang; Webster, Thomas F.; Gooden, David; Cooper, Ellen M.; McClean, Michael D.; Carignan, Courtney; Makey, Colleen; Stapleton, Heather M.

2013-01-01

With the phase-out of polybrominated diphenyl ether (PBDE) flame retardants, the use of new and alternate flame retardants has been increasing. 2,2-bis(chloromethyl)propane-1,3-diyltetrakis(2-chloroethyl) bisphosphate, known as V6, is a flame retardant applied to polyurethane foam commonly found in furniture and automobile foam. However, to the authors’ knowledge, no research has been conducted on V6 levels in the environment. The intention of this study was to measure the concentration of V6 in foam collected from baby products where it was recently detected, and measure levels in dust samples collected from homes and automobiles in the Boston, MA area. To accomplish this a pure V6 commercial standard was purchased from a Chinese manufacturer and purified (> 98%). An analytical method to measure V6 in dust samples using liquid chromatography tandem mass spectrometry (LC/MS-MS) was developed. Extraction was conducted using Accelerated Solvent Extraction (ASE) and extracts were purified using an ENVI-Florisil SPE column (500 mg, 3mL). V6 was measured in foam samples collected from baby products with a concentration ranging from 24,500,000 to 59,500,000 ng/g of foam (n = 12, average ± sd: 46,500,000 ± 12,000,000 ng/g; i.e., on average, 4.6 % of the foam mass was V6). V6 was also detected in 19 of 20 car dust samples and 14 of 20 house dust samples analyzed. The concentration of V6 in the house dust ranged from < 5 ng/g to 1,110 ng/g with a median of 12.5 ng/g, and < 5 ng/g to 6,160 ng/g in the car dust with a median of 103.0 ng/g. Concentrations in car dust were significantly higher than the house dust, potentially indicating higher use of V6 in automobiles compared to products found in the home. Furthermore, tris (2-chloroethyl) phosphate (TCEP), a known carcinogen, was found in the V6 commercial mixture (14% by weight) as an impurity and was consistently detected with V6 in the foam samples analyzed. A significant correlation was also observed between V6 and TCEP in the dust samples, suggesting that the use of V6 is a significant source of TCEP in the indoor environment. PMID:23565680

A mixture of the novel brominated flame retardants TBPH and TBB affects fecundity and transcript profiles of the HPGL-axis in Japanese medaka.

PubMed

Saunders, David M V; Podaima, Michelle; Codling, Garry; Giesy, John P; Wiseman, Steve

2015-01-01

The novel brominated flame retardants (NBFRs), bis(2-ethylhexyl)-2,3,4,5-tetrabromophthalate (TBPH) and 2-ethylhexyl-2,3,4,5 tetrabromobenzoate (TBB) are components of the flame retardant mixture Firemaster 550 and both TBPH and TBB have recently been listed as high production volume chemicals by the US EPA. These NBFRs have been detected in several environmental matrices but very little is known about their toxic effects or potencies. Results of in vitro assays demonstrated potentials of these NBFRs to modulate endocrine function through interactions with estrogen (ER) and androgen receptors (AR) and via alterations to synthesis of 17-β-estradiol (E2) and testosterone (T), but in vivo effects of these chemicals on organisms are not known. Therefore a 21-day short term fish fecundity assay with Japanese medaka (Oryzias latipes) was conducted to investigate if these NBFRs affect endocrine function in vivo. Medaka were fed a diet containing either 1422 TBPH:1474 TBB or 138:144 μg/g food, wet weight (w/w). Cumulative production of eggs was used as a measure of fecundity and abundances of transcripts of 34 genes along the hypothalamus-pituitary-gonadal-liver (HPGL) axis were quantified to determine mechanisms of observed effects. Cumulative fecundity was impaired by 32% in medaka exposed to the greatest dose of the mixture of TBPH/TBB. A pattern of global down-regulation of gene transcription at all levels of the HPGL axis was observed, but effects were sex-specific. In female medaka the abundance of transcripts of ERβ was lesser in livers, while abundances of transcripts of VTG II and CHG H were greater. In male medaka, abundances of transcripts of ERα, ERβ, and ARα were lesser in gonads and abundances of transcripts of ERβ and ARα were lesser in brain. Abundances of transcripts of genes encoding proteins for synthesis of cholesterol (HMGR), transport of cholesterol (HDLR), and sex hormone steroidogenesis (CYP 17 and 3β-HSD) were significantly lesser in male medaka, which might have implications for concentrations of sex hormones. The results of this study demonstrate that exposure to components of the flame retardant mixture Firemaster(®) 550 has the potential to impair the reproductive axis of fishes. Copyright © 2014 Elsevier B.V. All rights reserved.

In Vitro Metabolism of the Brominated Flame Retardants 2-Ethylhexyl-2,3,4,5-Tetrabromobenzoate (TBB) and Bis(2-Ethylhexyl) 2,3,4,5-Tetrabromophthalate (TBPH) in Human and Rat Tissues

PubMed Central

Roberts, Simon C.; Macaulay, Laura J.; Stapleton, Heather M.

2012-01-01

Due to the phaseout of polybrominated diphenyl ether (PBDE) flame retardants, new chemicals, such as 2-ethylhexyl-2,3,4,5-tetrabromobenzoate (TBB) and bis(2-ethylhexyl) 2,3,4,5-tetrabromophthalate (TBPH), have been used as replacements in some commercial flame retardant mixtures. Both chemicals have been detected in indoor dust at concentrations approaching the concentrations of PBDEs; however, little is known about their fate, metabolism, or toxicity. The goal of this study was to investigate the potential metabolism of these two brominated flame retardants in human and rat tissues by conducting in vitro experiments with liver and intestinal subcellular fractions. In all the experiments, TBB was consistently metabolized to 2,3,4,5-tetrabromobenzoic acid (TBBA) via cleavage of the 2-ethylhexyl chain without requiring any added cofactors. TBBA was also formed in purified porcine carboxylesterase, but at a much faster rate of 6.29 ± 0.58 nmol min-1 mg protein-1. The estimated Km and Vmax values for TBB metabolism in human microsomes were 11.1 ± 3.9 μM and 0.644 ± 0.144 nmol min-1 mg protein-1, respectively. A similar Km of 9.3 ± 2.2 μM was calculated for porcine carboxylesterase, indicating similar enzyme specificity. While the rapid formation of TBBA may reduce the bioaccumulation potential of TBB in mammals and may be useful as a biomarker of TBB exposure, the toxicity of this brominated benzoic acid is unknown and may be a concern based on its structural similarity to other toxic pollutants. In contrast to TBB, no metabolites of TBPH were detected in human or rat subcellular fractions. However, a metabolic product of TBPH, mono(2-ethylhexyl) tetrabromophthalate (TBMEHP), was formed in purified porcine carboxylesterase at an approximate rate of 1.08 pmol min-1 mg protein-1. No Phase II metabolites of TBBA or TBMEHP were observed. More research is needed to understand the in vivo toxicokinetics and health effects of these compounds given their current ubiquitous presence in most US households and the resulting probability of chronic exposure, particularly to young children. PMID:22575079

Biofiltration vs conventional activated sludge plants: what about priority and emerging pollutants removal?

PubMed

Mailler, R; Gasperi, J; Rocher, V; Gilbert-Pawlik, S; Geara-Matta, D; Moilleron, R; Chebbo, G

2014-04-01

This paper compares the removal performances of two complete wastewater treatment plants (WWTPs) for all priority substances listed in the Water Framework Directive and additional compounds of interest including flame retardants, surfactants, pesticides, and personal care products (PCPs) (n = 104). First, primary treatments such as physicochemical lamellar settling (PCLS) and primary settling (PS) are compared. Similarly, biofiltration (BF) and conventional activated sludge (CAS) are then examined. Finally, the removal efficiency per unit of nitrogen removed of both WWTPs for micropollutants is discussed, as nitrogenous pollution treatment results in a special design of processes and operational conditions. For primary treatments, hydrophobic pollutants (log K ow > 4) are well removed (>70 %) for both systems despite high variations of removal. PCLS allows an obvious gain of about 20 % regarding pollutant removals, as a result of better suspended solids elimination and possible coagulant impact on soluble compounds. For biological treatments, variations of removal are much weaker, and the majority of pollutants are comparably removed within both systems. Hydrophobic and volatile compounds are well (>60 %) or very well removed (>80 %) by sorption and volatilization. Some readily biodegradable molecules are better removed by CAS, indicating a better biodegradation. A better sorption of pollutants on activated sludge could be also expected considering the differences of characteristics between a biofilm and flocs. Finally, comparison of global processes efficiency using removals of micropollutants load normalized to nitrogen shows that PCLS + BF is as efficient as PS + CAS despite a higher compactness and a shorter hydraulic retention time (HRT). Only some groups of pollutants seem better removed by PS + CAS like alkylphenols, flame retardants, or di-2-ethylhexyl phthalate (DEHP), thanks to better biodegradation and sorption resulting from HRT and biomass characteristics. For both processes, and out of the 68 molecules found in raw water, only half of them are still detected in the water discharged, most of the time close to their detection limit. However, some of them are detected at higher concentrations (>1 μg/L and/or lower than environmental quality standards), which is problematic as they represent a threat for aquatic environment.

Determination of hexabromocyclododecane by flowing atmospheric pressure afterglow mass spectrometry.

PubMed

Smoluch, Marek; Silberring, Jerzy; Reszke, Edward; Kuc, Joanna; Grochowalski, Adam

2014-10-01

The first application of a flowing atmospheric-pressure afterglow ion source for mass spectrometry (FAPA-MS) for the chemical characterization and determination of hexabromocyclododecane (HBCD) is presented. The samples of technical HBCD and expanded polystyrene foam (EPS) containing HBCD as a flame retardant were prepared by dissolving the appropriate solids in dichloromethane. The ionization of HBCD was achieved with a prototype FAPA source. The ions were detected in the negative-ion mode. The ions corresponding to a deprotonated HBCD species (m/z 640.7) as well as chlorine (m/z 676.8), nitrite (m/z 687.8) and nitric (m/z 703.8) adducts were observed in the spectra. The observed isotope pattern is characteristic for a compound containing six bromine atoms. This technique is an effective approach to detect HBCD, which is efficiently ionized in a liquid phase, resulting in high detection efficiency and sensitivity. Copyright © 2014 Elsevier B.V. All rights reserved.

Measuring and Modeling Surface Sorption Dynamics of OPFRs in Stainless Steel Empty Chambers

EPA Science Inventory

Organophosphorus flame retardants (OPFRs) are produced and used widely as alternative additives in building materials and consumer products such as spray polyurethane foam (SPF), polyvinyl chloride flooring, electrical and electronic products, furniture, textile coatings, and pla...

Separator material for electrochemical cells

DOEpatents

Cieslak, W.R.; Storz, L.J.

1991-03-26

An electrochemical cell is characterized as utilizing an aramid fiber as a separator material. The aramid fibers are especially suited for lithium/thionyl chloride battery systems. The battery separator made of aramid fibers possesses superior mechanical strength, chemical resistance, and is flame retardant.

Predictions of developmental neurotoxicity potential of TDCPP

EPA Science Inventory

Tris(1 ,3-dichloro-2-propyl)phosphate (TDCPP) is an organophosphate flame retardant with widespread usage and documented human exposures through food, inhalation, dust ingestion, and breast milk. Concern for neurodevelopmental effects in infants and children has been raised by fi...

Innovative technologies for anti-flammable cotton fabrics

USDA-ARS?s Scientific Manuscript database

Due to its environmentally friendly properties, supercritical carbon dioxide (scCO2) is considered in green chemistry as a substitute for organic solvents in chemical reactions. In this presentation, innovative approaches for preparation of flame retardant fabrics were obtained by utilizing supercr...

Fire and smoke retardants

NASA Astrophysics Data System (ADS)

Drews, M. J.

Despite a reduction in Federal regulatory activity, research concerned with flame retardancy and smoke suppression in the private sector appears to be increasing. This trend seem related to the increased utilization of plastics for end uses which traditionally have employed metal or wood products. As a result, new markets have appeared for thermally stable and fire resistance thermoplastic materials, and this in turn has spurred research and development activity. In addition, public awareness of the dangers associated with fire has increased as a result of several highly publicized hotel and restaurant fires within the past two years. The consumers recognition of flammability characteristics as important materials property considerations has increased. The current status of fire and smoke retardant chemistry and research are summarized.

16 CFR 1632.5 - Mattress pad test procedure.

Code of Federal Regulations, 2010 CFR

2010-01-01

... 1632.5 Commercial Practices CONSUMER PRODUCT SAFETY COMMISSION FLAMMABLE FABRICS ACT REGULATIONS... substrate. (b) Flame resistant mattress pads. The following additional requirements shall be applicable to mattress pads which contain a chemical fire retardant. (1) These mattress pads shall be tested in...

Time Trends of Polybrominated Diphenyl Ethers (PBDEs) in Antarctic Biota

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) are “emerged” contaminants that were produced and used as flame retardants in numerous consumer and industrial applications for decades until banned. They remain ubiquitously present in the environment today. Here, a unique set of >200 bioti...

A systems-based approach to predict biological responses of aquatic organisms to complex environmental mixtures

EPA Science Inventory

Contaminants of emerging concern (CECs) such as new-generation pesticides, pharmaceuticals, household and personal care products, steroid hormones, and flame retardants enter the aquatic environment through multiple sources such as wastewater treatment plants and agricultural ope...

STIMULATION OF [3H] ARACHIDONIC ACID RELEASE IN RAT CEREBELLAR GRANULE NEURONS BY POLYBROMINATED DIPHENYL.

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) are widely used as flame retardants in electronic equipment, plastics, textiles, and building materials. While the presence of other persistent organic pollutants, such as polychlorinated biphenyls (PCBs) and polychlorinated dibenzo-p-dioxin...

HEALTH EFFECTS OF BROMINATED FLAME RETARDANTS (BFRS)

EPA Science Inventory

BFRs are a broad class of compounds providing fire safety. Because of high production and usage and recent findings that they are ubiquitous in environmental samples and biota, concerns exist about potential health effects. Some of the major commercial products, such as tetrabr...

POLYBROMINATED DIPHENYL ETHERS IN SOUTHERN MISSISSIPPI CATFISH

EPA Science Inventory

Polybrominated diphenyl ethers (PBDEs) are used as flame retardants in a wide variety of consumer products. Concerns surrounding these compounds are primarily due do their ubiquitous presence in the environment as well as in human tissue, such as milk, coupled with evidence indi...

Activation of human peroxisome-activated receptor-gamma (PPARy) by house dust extracts

EPA Science Inventory

Obesity in children has become an epidemic and recent research suggests a possible contribution from exposure to environmental chemicals. Several chemicals, such as phthalates, brominated flame retardants, and perfluorinated chemicals, are common in house dust on floors where chi...

POLYBROMINATED DIPHENYL ETHERS IN HOUSE DUST AND CLOTHES DRYER LINT

EPA Science Inventory

Polybrominated diphenyl ether (PBDE) flame retardants are now considered ubiquitous and persistent pollutants. Few studies have examined the concentrations of these chemicals in the home and here we report measurements of PBDEs in house dust samples collected from the Washington...

PBDES IN US HUMANS, FOOD, AND ENVIRONMENTAL SAMPLES

EPA Science Inventory

Polybrominated diphenyl ether (PBDE) flame retardants were measured in US human milk and blood, food and environmental samples. All 59 milk samples were positive for multiple congeners measured. Milk was collected beginning in 2001 from various locations in the US. PBDEs varied f...

Developing testing methods for characterizing emissions and sources of exposures from polyurehane products

EPA Science Inventory

The relationship between onsite manufacture of spray polyurethane foam insulation (SPFI) and potential exposures to diisocyanate compounds, amine catalysts, flame retardants, and blowing agents, as well as aldehydes and other volatile or semivolatile organic compounds that may be...

Safety research of insulating materials of cable for nuclear power generating station

NASA Technical Reports Server (NTRS)

Lee, C. K.; Choi, J. H.; Kong, Y. K.; Chang, H. S.

1988-01-01

The polymers PE, EPR, PVC, Neoprene, CSP, CLPE, EP and other similar substances are frequently used as insulation and protective covering for cables used in nuclear power generating stations. In order to test these materials for flame retardation, environmental resistance, and cable specifications, they were given the cable normal test, flame test, chemical tests, and subjected to design analysis and loss of coolant accident tests. Material was collected on spark tests and actual experience standards were established through these contributions and technology was accumulated.