Microstructural characterization of an SA508–309L/308L–316L domestic dissimilar metal welded safe-end joint

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ming, Hongliang; Zhang, Zhiming; Wang, Jianqiu, E-mail: wangjianqiu@imr.ac.cn

2014-11-15

The microstructure of an SA508–309L/308L–316L domestic dissimilar metal welded safe-end joint was characterized in this work by optical microscopy, scanning electron microscopy (with electron back scattering diffraction) and micro-hardness testing. Epitaxial growth and competitive growth are evident in the 308L–316L fusion boundary regions. A martensite layer, carbon-depleted zones, and type-II and type-I boundaries are found in the SA508–309L fusion boundary regions, while only martensite and austenite mixed zones are observed in the SA508–308L fusion boundary regions. The microstructure near the fusion boundary and the microstructure transition in the SA508 heat affected zone are quite complex. Both for SA508–309L/308L and 308L–316L,more » the highest residual strain is located on the outside of the weldment. The residual strain and the grain boundary character distribution change with increasing distance from the fusion boundary in the heat affected zone of 316L. Micro-hardness measurements also reveal non-uniform mechanical properties across the weldment. - Highlights: • The microstructure of SA508 HAZ, especially near the FB, is very complex. • The outside of the dissimilar metal welded joint has the highest residual. • The micro-hardness distributions along the DMWJ are non-uniform.« less

Microstructure and wear resistance of Al2O3-M7C3/Fe composite coatings produced by laser controlled reactive synthesis

NASA Astrophysics Data System (ADS)

Tan, Hui; Luo, Zhen; Li, Yang; Yan, Fuyu; Duan, Rui

2015-05-01

Based on the principle of thermite reaction of Al and Fe2O3 powders, the Al2O3 ceramic reinforced Fe-based composite coatings were fabricated on a steel substrate by laser controlled reactive synthesis and cladding. The effects of different additions of thermite reactants on the phase transition, microstructure evolution, microhardness and wear resistance of the composite coatings were investigated by means of X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Vickers microhardness and block-on-ring wear test, respectively. The results show that Al2O3 ceramic and M7C3 carbide are in situ synthesized via the laser controlled reactive synthesis. The Al2O3 ceramic and M7C3 carbides prefer to distribute along the γ-Fe phase boundary continuously, which separates the γ-Fe matrix and is beneficial to the grain refinement. With the increase of thermite reactants, the amount of Al2O3 ceramic and M7C3 carbide in the composite coatings increases gradually. Moreover the cladding layer changes from dendritic structure to columnar structure and martensite structure in the heat affected zone becomes coarse. The increased thermite reactants improve the microhardness and wear resistance of the in situ composite coatings obviously and enhance the hardness of the heat affected zone, which should be ascribed to the grain refinement, ceramic and carbide precipitation and solid solution strengthening.

Effect of Laser Power on Metallurgical, Mechanical and Tribological Characteristics of Hardfaced Surfaces of Nickel-Based Alloy

NASA Astrophysics Data System (ADS)

Gnanasekaran, S.; Padmanaban, G.; Balasubramanian, V.

2017-12-01

In this present work, nickel based alloy was deposited on 316 LN austenitic stainless steel (ASS) by a laser hardfacing technique to investigate the influence of laser power on macrostructure, microstructure, microhardness, dilution and wear characteristics. The laser power varied from 1.1 to 1.9 kW. The phase constitution, microstructure and microhardness were examined by optical microscope, scanning electron microscopy, energy dispersion spectroscopy and Vickers microhardness tester. The wear characteristics of the hardfaced surfaces and substrate were evaluated at room temperature (RT) under dry sliding wear condition (pin-on-disc). The outcome demonstrates that as the laser power increases, dilution increases and hardness of the deposit decreases. This is because excess heat melts more volume of substrate material and increases the dilution; subsequently it decreases the hardness of the deposit. The microstructure of the deposit is characterized by Ni-rich carbide, boride and silicide.

The effect of nanobioceramic reinforcement on mechanical and biological properties of Co-base alloy/hydroxyapatite nanocomposite.

PubMed

Bahrami, M; Fathi, M H; Ahmadian, M

2015-03-01

The goal of the present research was to fabricate, characterize, and evaluate mechanical and biological properties of Co-base alloy composites with different amounts of hydroxyapatite (HA) nanopowder reinforcement. The powder of Co-Cr-Mo alloy was mixed with different amounts of HA by ball milling and it was then cold pressed and sintered. X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques were used. Microhardness measurement and compressive tests were also carried out. Bioactivity behavior was evaluated in simulated body fluid (SBF). A significant decrease in modulus elasticity and an increase in microhardness of the sintered composites were observed. Apatite formation on the surface of the composites showed that it could successfully convert bioinert Co-Cr-Mo alloy to bioactive type by adding 10, 15, and 20wt.% HA which have lower modulus elasticity and higher microhardness. Copyright © 2014 Elsevier B.V. All rights reserved.

Microstructure and mechanical behavior of pulsed laser surface melted AISI D2 cold work tool steel

NASA Astrophysics Data System (ADS)

Yasavol, N.; Abdollah-zadeh, A.; Ganjali, M.; Alidokht, S. A.

2013-01-01

D2 cold work tool steel (CWTS) was subjected to pulse laser surface melting (PLSM) at constant frequency of 20 Hz Nd: YAG laser with different energies, scanning rate and pulse durations radiated to the surface. Characterizing the PLSM, with optical and field emission scanning electron microscopy, electron backscattered diffraction and surface hardness mapping technique was used to evaluate the microhardness and mechanical behavior of different regions of melting pool. Increasing laser energy and reducing the laser scanning rate results in deeper melt pool formation. Moreover, PLSM has led to entirely dissolution of the carbides and re-solidification of cellular/dendritic structure of a fine scale surrounded by a continuous interdendritic network. This caused an increase in surface microhardness, 2-4 times over that of the base metal.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alhajeri, Saleh N., E-mail: sn.alhajeri@paaet.edu.

Disks of an Al-6061 metal matrix composite, reinforced with 10 vol.% Al{sub 2}O{sub 3} particles, were processed by high-pressure torsion (HPT) at room temperature for 1/4, 1/2, 1, 5 and 10 turns under an applied pressure of 6.0 GPa. The evolution of microstructure was investigated using optical microscopy and scanning electron microscopy. During HPT processing the average grain size within the aluminum matrix decreased from ∼ 35 μm in the unprocessed condition to ∼ 170 nm after processing through 10 turns but there was no significant effect on the size and distribution of the alumina particulate clusters. The values ofmore » the Vickers microhardness were recorded across the surface of each disk and then plotted as two-dimensional and three-dimensional color-coded contour maps. The results show the hardness increases from ∼ 56 Hv in the initial condition to ∼ 165 Hv after HPT for 10 turns. The results demonstrate that, as in many unreinforced metallic alloys, the evolution of hardness with strain exhibits strain hardening without any significant recovery. - Highlights: •The average grain size of the Al matrix was ~ 170 nm after processing for 10 turns. •No significant effect of HPT on the size and distribution of the Al{sub 2}O{sub 3} particles. •The evolution of microhardness demonstrates strain hardening without recovery. •The microhardness at low strains increases linearly from the center to the edge. •The microhardness at high strains becomes homogeneous with a saturation of ~ 170 Hv.« less

Structure and Microhardness of Cu-Ta Joints Produced by Explosive Welding

PubMed Central

Maliutina, Iu. N.; Mali, V. I.; Bataev, I. A.; Bataev, A. A.; Esikov, M. A.; Smirnov, A. I.; Skorokhod, K. A.

2013-01-01

The structure and microhardness of Cu-Ta joints produced by explosive welding were studied. It was found that, during explosive welding, an intermediate layer 20⋯40 μm thick with a finely dispersed heterophase structure, formed between the welded copper and tantalum plates. The structure of the layer was studied by scanning and transmission electron microscopy. Microvolumes with tantalum particles distributed in a copper matrix and microvolumes of copper particles in a tantalum matrix were detected. The tantalum particles in copper have a size of 5⋯500 nm, with a predominance of 5⋯50 nm particles. A mechanism for the formation of the finely dispersed heterophase structure in explosive welding is proposed. The microhardness of interlayers with the heterophase structure reaches 280 HV, which far exceeds the microhardness of copper (~130 HV) and tantalum (~160 HV). Many twins of deformation origin were found in the structure of the copper plate. The effect of heating temperature in the range from 100 to 900°C on the microhardness of copper, tantalum, and the Cu-Ta welded joint was studied. Upon heating to 900°C, the microhardness of the intermediate layer decreases from 280 to 150 HV. The reduction in the strength properties of the weld material is mainly due to structural transformations in copper. PMID:24453818

Structure and properties of parts produced by electron-beam additive manufacturing

NASA Astrophysics Data System (ADS)

Klimenov, Vasilii; Klopotov, Anatolii; Fedorov, Vasilii; Abzaev, Yurii; Batranin, Andrey; Kurgan, Kirill; Kairalapov, Daniyar

2017-12-01

The paper deals with the study of structure, microstructure, composition and microhardness of a tube processed by electron-beam additive manufacturing using optical and scanning electron microscopy. The structure and macrodefects of a tube made of Grade2 titanium alloy is studied using the X-ray computed tomography. The principles of layer-by-layer assembly and boundaries after powder sintering are set out in this paper. It is found that the titanium alloy has two phases. Future work will involve methods to improve properties of created parts.

Structure and properties of fixed joints formed by ultrasonic-assisted friction-stir welding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fortuna, S. V., E-mail: s-fortuna@ispms.ru; Ivanov, K. V., E-mail: ikv@ispms.ru; Eliseev, A. A., E-mail: alan@ispms.ru

2015-10-27

This paper deals with structure and properties of aluminum alloy 7475 and its joints obtained by friction stir welding including under ultrasonic action. Microhardness measurements show that ultrasonic action increases strength properties of the joints. Optical and transmission electron microscopy reveals that this effect is related to the precipitation of tertiary coherent S-and T-phase particles.

Changes Found on Run-In and Scuffed Surfaces of Steel Chrome Plate, and Cast Iron

NASA Technical Reports Server (NTRS)

Good, J. N.; Godfrey, Douglas

1947-01-01

A study was made of run-in and scuffed steel, chrome-plate, and cast-iron surfaces. X-ray and electron diffraction techniques, micro-hardness determinations, and microscopy were used. Surface changes varied and were found to include three classes: chemical reaction, hardening, and crystallite-size alteration. The principal chemical reactions were oxidation and carburization.

Surface modification of hydroturbine steel using friction stir processing

NASA Astrophysics Data System (ADS)

Grewal, H. S.; Arora, H. S.; Singh, H.; Agrawal, A.

2013-03-01

Friction stir processing (FSP) has proved to be a viable tool for enhancing the mechanical properties of materials, however, the major focus has been upon improving the bulk properties of light metals and their alloys. Hydroturbines are susceptible to damage owing to slurry and cavitation erosion. In this study, FSP of a commonly employed hydroturbine steel, 13Cr4Ni was undertaken. Microstructural characterization of the processed steel was conducted using optical microscopy (OM), scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and electron back scatter diffraction (EBSD) techniques. Mechanical characterization of the steel was undertaken in terms of microhardness and resistance to cavitation erosion (CE). FSP resulted in the refinement of the microstructure with reduction in grain size by a factor of 10. EBSD results confirmed the existence of submicron and ultrafine grained microstructure. The microhardness of the steel was found to enhance by 2.6 times after processing. The processed steel also showed 2.4 times higher resistance against cavitation erosion in comparison to unprocessed steel. The primary erosion mechanism for both the steels was identical in nature, with plastic deformation responsible for the loss of material.

Lead-Free Sn-Ce-O Composite Coating on Cu Produced by Pulse Electrodeposition from an Aqueous Acidic Sulfate Electrolyte

NASA Astrophysics Data System (ADS)

Sharma, Ashutosh; Das, Karabi; Das, Siddhartha

2017-10-01

Pulse-electrodeposited Sn-Ce-O composite solder coatings were synthesized on a Cu substrate from an aqueous acidic solution containing stannous sulfate (SnSO4·3H2O), sulfuric acid (H2SO4), and Triton X-100 as an additive. The codeposition was achieved by adding nano-cerium oxide powder in varying concentrations from 5 g/L to 20 g/L into the electrolytic bath. Microstructural characterization was carried out using x-ray diffraction (XRD), scanning electron microscopy, and transmission electron microscopy. The XRD analysis showed that the deposits consist mainly of tetragonal β (Sn) with reduced cerium oxide species. The composite coatings thus obtained exhibit a smaller grain size, possess higher microhardness, and a lower melting point than the monolithic Sn coating. The electrical resistivity of the developed composites increases, however, but lies within the permissible limits for current lead-free solder applications. Also, an optimum balance of properties in terms of microhardness, adhesion, melting point and resistivity can be obtained with 0.9 wt.% cerium oxide in the Sn matrix, which enables potential applications in solder joints and packaging.

Lead sheathing of ship hulls in the Roman period: Archaeometallurgical characterisation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kahanov, Yaacov, E-mail: yak@research.haifa.ac.il; Ashkenazi, Dana

An archaeometallurgical analysis of samples of lead sheathing from five ships of the Roman period was carried out in order to determine their composition and microstructure, and to obtain a better understanding of their manufacturing processes. The examinations included optical microscopy of metallographic cross-sections, microhardness tests, scanning electron microscopy, including energy dispersive spectroscopy, and X-ray photoelectron spectroscopy. The results show that the samples were all composed of lead covered with an oxide layer. The sheet thicknesses, microhardness values and microhardness distribution, as well as the grain size distribution, led to the conclusion that all of the sheets were produced bymore » the same technology, using hammering, and were probably used for the same purpose. The presence of antimony was observed in the sample from the Roman ship from Caesarea, which may hint at an Italian (Sardinian) origin of the material, and perhaps of the ship. - Research Highlights: {yields} During the Roman period ship hulls were sheathed with lead. {yields} Five samples have been analysed for their characteristics and manufacturing process. {yields} The process was cold-working (strain-hardening) using hammering. {yields} The lead was open-casted on a flat stone, and later hammered at room temperature. {yields} Antimony in the Caesarea shipwreck may indicate an Italian origin of construction.« less

Synthesis and characterization of bulk metallic glasses prepared by laser direct deposition

NASA Astrophysics Data System (ADS)

Ye, Xiaoyang

Fe-based and Zr-based metallic glasses have attracted extensive interest for structural applications due to their excellent glass forming ability, superior mechanical properties, unique thermal and corrosion properties. In this study, the feasibility of synthesizing metallic glasses with good ductility by laser direct deposition is explored. Both in-situ synthesis with elemental powder mixture and ex-situ synthesis with prealloyed powder are discussed. Microstructure and properties of laser direct deposited metallic glass composites are analyzed. Synthesis of Fe-Cr-Mo-W-Mn-C-Si-B metallic glass composite with a large fraction of amorphous phase was accomplished using laser direct deposition. X-ray diffraction (XRD) and transmission electron microscopy investigations revealed the existence of amorphous structure. Microstructure analyses by optical microscopy and scanning electron microscopy (SEM) indicated the periodically repeated microstructures of amorphous and crystalline phases. Partially crystallized structure brought by laser reheating and remelting during subsequent laser scans aggregated in the overlapping area between each scan. XRD analysis showed that the crystalline particle embedded in the amorphous matrix was Cr 1.07Fe18.93 phase. No significant microstructural differences were found from the first to the last layer. Microhardness of the amorphous phase (HV0.2 1591) showed a much higher value than that of the crystalline phase (HV0.2 947). Macrohardness of the top layer had a value close to the microhardness of the amorphous region. Wear resistance property of deposited layers showed a significant improvement with the increased fraction of amorphous phase. Zr65Al10Ni10Cu15 amorphous composites with a large fraction of amorphous phase were in-situ synthesized by laser direct deposition. X-ray diffraction confirmed the existence of both amorphous and crystalline phases. Laser parameters were optimized in order to increase the fraction of amorphous phase. The microstructure analysis by scanning electron microscopy revealed the deposited structure was composed of periodically repeated amorphous and crystalline phases. Overlapping regions with nanoparticles aggregated were crystallized by laser reheating and remelting processes during subsequent laser scans. Vickers microhardness of the amorphous region showed around 35% higher than that of crystalline region. Average hardness obtained by a Rockwell macrohardness tester was very close to the microhardness of the amorphous region. The compression test showed that the fracture strain of Zr65Al10Ni10Cu15 amorphous composites was enhanced from less than 2% to as high as 5.7%, compared with fully amorphous metallic glass. Differential scanning calorimetry test results further revealed the amorphous structure and glass transition temperature Tg was observed to be around 655K. In 3 mol/L NaCl solution, laser direct deposited amorphous composites exhibited distinctly improved corrosion resistance, compared with fully-crystallized samples.

Analysis of microstructure and mechanical properties of aluminium-copper joints welded by FSW process

NASA Astrophysics Data System (ADS)

Iordache, M.; Sicoe, G.; Iacomi, D.; Niţu, E.; Ducu, C.

2017-08-01

The research conducted in this article aimed to check the quality of joining some dissimilar materials Al-Cu by determining the mechanical properties and microstructure analysis. For the experimental measurements there were used tin alloy Al - EN-AW-1050A with a thickness of 2 mm and Cu99 sheet with a thickness of 2 mm, joined by FSW weld overlay. The main welding parameters were: rotating speed of the rotating element 1400 rev/min, speed of the rotating element 50 mm/min. The experimental results were determined on samples specially prepared for metallographic analysis. In order to prepare samples for their characterization, there was designed and built a device that allowed simultaneous positioning and fixing for grinding. The characteristics analyzed in the joint welded samples were mictrostructure, microhardness and residual stresses. The techniques used to determine these characteristics were optical microscopy, electron microscopy with fluorescence radioactive elemental analysis (EDS), Vickers microhardness line - HV0.3 and X-ray diffractometry.

Boron nitride nanotubes as novel fillers for improving the properties of dental adhesives.

PubMed

Degrazia, Felipe Weidenbach; Leitune, Vicente Castelo Branco; Samuel, Susana Maria Werner; Collares, Fabrício Mezzomo

2017-07-01

This study aimed to evaluate the physical-chemical properties of experimental dental adhesives containing boron nitride nanotubes (BNNTs) as inorganic fillers. An experimental adhesive resin was prepared using HEMA-BisGMA, 66/33wt% (control). Inorganic BNNT fillers were first analyzed using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) and then incorporated into the adhesive at different concentration (0.05, 0.075, 0.1, 0.15wt%). Degree of conversion (DC), ultimate strength, contact angle, surface free energy (SFE) microhardness, softening in solvent and bioactivity were assessed. Scanning and transmission electron microscopy (SEM and TEM) showed BNNTs with diameter ranging from 5 to 10nm with close end tips. No changes in DC were observed after incorporating BNNTs up to 0.15wt%. The contact angles of water and α-bromonaphthalene increased (p<0.05) and consequently the SFE decreased after incorporating BNNTs to the polymer matrix. Microhardness and solvent degradation strength increased after incorporation of 0.075, 0.1 and 0.15wt% BNNTs. Mineral deposition was found after 7days of immersion on adhesive specimens after incorporation of BNNT. The incorporation of BNNTs up to 0.15wt% improved the chemical and mechanical properties of dental adhesives and promoted mineral deposition. Incorporation of boron nitride nanotubes into adhesive resin materials improved physical-chemical properties and increased mineral deposition on its surface allowing enhanced properties of the resin-dentin interface. Thus, the novel adhesive material is promising as a dental adhesive and may contribute to the stability of the dentin-resin bonding. Copyright © 2017 Elsevier Ltd. All rights reserved.

The relationship between vickers microhardness and compressive strength of functional surface geopolymers

NASA Astrophysics Data System (ADS)

Subaer, Ekaputri, Januari Jaya; Fansuri, Hamzah; Abdullah, Mustafa Al Bakri

2017-09-01

An experimental study to investigate the relationship between Vickers microhardness and compressive strength of geopolymers made from metakaolin has been conducted. Samples were prepared by using metakaolin activated with a sodium silicate solution at a different ratio of Si to Al and Na to Al and cured at 70oC for one hour. The resulting geopolymers were stored in an open air for 28 days before conducting any measurement. Bulk density and apparent porosity of the samples were measured by using Archimedes's method. Vickers microhardness measurements were performed on a polished surface of geopolymers with a load ranging from 0.3 - 1.0 kg. The topographic of indented samples were examined by using scanning electron microscopy (SEM). Compressive strength of the resulting geopolymers was measured on the cylindrical samples with a ratio of height to the diameter was 2:1. The results showed that the molar ratios of geopolymers compositions play important roles in the magnitude of bulk density, porosity, Vickers's microhardness as well as the compressive strength. The porosity reduced exponentially the magnitude of the strength of geopolymers. It was found that the relationship between Vickers microhardness and compressive strength was linear. At the request of all authors and with the approval of the proceedings editor, article 020188 titled, "The relationship between vickers microhardness and compressive strength of functional surface geopolymers," is being retracted from the public record due to the fact that it is a duplication of article 020170 published in the same volume.

Comparative examination of the microstructure and high temperature oxidation performance of NiCrBSi flame sprayed and pack cementation coatings

NASA Astrophysics Data System (ADS)

Chaliampalias, D.; Vourlias, G.; Pavlidou, E.; Skolianos, S.; Chrissafis, K.; Stergioudis, G.

2009-01-01

Coatings formed from NiCrBSi powder were deposited by thermal spray and pack cementation processes on low carbon steel. The microstructure and morphology of the coatings were studied by scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Flame sprayed coatings exhibited high porosity and were mechanically bonded to the substrate while pack cementation coatings were more compact and chemically bonded to the substrate. The microhardness and the high temperature oxidation resistance of the coated samples were evaluated by a Vickers microhardness tester and by thermogravimetric measurements (TG), respectively. Pack cementation coatings showed higher hardness and were more protective to high temperature environments than the flame sprayed coatings.

Effect of different Zr contents on properties and microstructure of Cu-Cr-Zr alloys

NASA Astrophysics Data System (ADS)

Jinshui, Chen; Bin, Yang; Junfeng, Wang; Xiangpeng, Xiao; Huiming, Chen; Hang, Wang

2018-02-01

The crystallography and morphology of precipitate particles of Cu-Cr-Zr alloys with varying Zr contents were studied by transmission electron microscopy (TEM) after solution treatments at 950 °C for 1 h and aging treatments at 500 °C for different times ranged from 0.5 h to 24 h. The microhardness and electrical conductivity of Cu-Cr-Zr alloys after various aging process were tested. The results show that the microhardness and electrical conductivity rapidly increased at first, then the microhardness decreased slowly after reaching the peak, while the conductivity continues to increase. Nano-scaled precipitates exhibit two kinds of morphology (coffee bean and ellipse shaped). With increasing Zr content, the Zr-containing precipitation sequence of Cu-Cr-Zr alloys at peak-ageing is Heusler CrCu2Zr → Cu5Zr → Cu4Zr. The Heusler CrCu2Zr phase decomposed into fine and homogeneous Cr and Cu4Zr, resulting in improved alloy properties.

Electrochemical and Passive Behaviors of Pure Copper Fabricated by Accumulative Roll-Bonding (ARB) Process

NASA Astrophysics Data System (ADS)

Imantalab, O.; Fattah-alhosseini, A.

2015-07-01

In the present work, electrochemical and passive behaviors of pure copper fabricated by accumulative roll-bonding (ARB) process in 0.01 M borax solution (pH = 9.1) have been studied. Before any electrochemical measurements, evaluation of microstructure was obtained by Vickers microhardness, x-ray diffraction (XRD), and transmission electron microscopy. The results of microhardness tests revealed that microhardness values increased with the increasing number of ARB cycles. Also a sharp increase was seen in microhardness after the first ARB cycle, whereas mediocre additional increases were observed afterward up to the seven cycles. Moreover, XRD patterns showed that the mean crystallite size values decrease with the increasing number of ARB cycles. To investigate the electrochemical and passive behaviors of the samples, the potentiodynamic polarization, Mott-Schottky analysis and electrochemical impedance spectroscopy (EIS) were carried out. Polarization plots revealed that as a result of ARB, the corrosion behavior of the specimens improves compared with the annealed pure copper. Also, the Mott-Schottky analysis and EIS measurements showed that the increasing number of ARB cycles offer better conditions for forming the passive films with higher protection behavior, due to the growth of less-defective films.

Shear punch and ball microhardness measurements of 14 MeV neutron irradiation hardening in five metals

NASA Astrophysics Data System (ADS)

Shinohara, K.; Lucas, G. E.; Odette, G. R.

1985-08-01

The irradiation hardening response of five metals irradiated in RTNS-II was investigated using a combination of ball microhardness and shear punch test techniques. The specimens were transmission electron microscopy disks of pure nickel, Ni-5wt%Si, pure iron, solution annealed prime candidate alloy (PCA) for Path A, and 40% cold worked MFE 316 stainless steel. Specimens were irradiated in RTNS-II to fluences in the range 6 × 10 16 to 6 × 10 17 n/cm 2. Only limited ball microhardness data could be obtained because of disk thickness. However, the ball microhardness data obtained were in good agreement with shear punch data. It was found that the pure metals exhibited little hardening after exposure to fluences of ~1 × 10 17 n/cm 2, but Ni-5 Si exhibited significant hardening after 6 × 10 17 n/cm 2. Hardening in PCA was similar to that observed in solution annealed 316 stainless steel; and hardening in 40% cold worked MFE 316 was relatively small after 6 × 10 17 n/cm 2. The Ni-5 Si response may be due to irradiation induced precipitation.

Fabrication of homogeneously dispersed graphene/Al composites by solution mixing and powder metallurgy

NASA Astrophysics Data System (ADS)

Zeng, Xiang; Teng, Jie; Yu, Jin-gang; Tan, Ao-shuang; Fu, Ding-fa; Zhang, Hui

2018-01-01

Graphene-reinforced aluminum (Al) matrix composites were successfully prepared via solution mixing and powder metallurgy in this study. The mechanical properties of the composites were studied using microhardness and tensile tests. Compared to the pure Al alloy, the graphene/Al composites showed increased strength and hardness. A tensile strength of 255 MPa was achieved for the graphene/Al composite with only 0.3wt% graphene, which has a 25% increase over the tensile strength of the pure Al matrix. Raman spectroscopy, Fourier transform infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy were used to investigate the morphologies, chemical compositions, and microstructures of the graphene and the graphene/Al composites. On the basis of fractographic evidence, a relevant fracture mechanism is proposed.

Microstructure and Antiwear Property of Laser Cladding Ni-Co Duplex Coating on Copper.

PubMed

Wang, Yiyong; Liang, Zhipeng; Zhang, Junwei; Ning, Zhe; Jin, Hui

2016-07-28

Ni-Co duplex coatings were cladded onto Cu to improve the antiwear properties of Cu products. Prior to laser cladding, n-Al₂O₃/Ni layers were introduced as interlayers between laser cladding coatings and Cu substrates to improve the laser absorptivity of these substrates and ensure defect-free laser cladding coatings. The structure and morphology of the coatings were characterized by scanning electron microscopy and optical microscopy, and the phases of the coatings were analyzed by X-ray diffraction. Their hardness was measured using a microhardness tester. Experimental results showed that defect-free composite coatings were obtained and that the coatings were metallurgically bonded to the substrates. The surface of the Ni-Co duplex coatings comprised a Co-based solid solution, Cr₇C₃, (Fe,Ni) 23 C₆, and other strengthening phases. The microhardness and wear resistance of the duplex coatings were significantly improved compared with the Cu substrates. The average microhardness of the cladded coatings was 845.6 HV, which was approximately 8.2 times greater than that of the Cu substrates (102.6 HV). The volume loss of the Cu substrates was approximately 7.5 times greater than that of the Ni-Co duplex coatings after 60 min of sliding wear testing. The high hardness of and lack of defects in the Ni-Co duplex coatings reduced the plastic deformation and adhesive wear of the Cu substrates, resulting in improved wear properties.

Surface modification of an aluminum alloy by electron beam introducing TiCN nanoparticles

NASA Astrophysics Data System (ADS)

Kolev, M.; Dimitrova, R.; Parshorov, St.; Valkov, St.; Lazarova, R.; Petrov, P.

2018-03-01

TiCN nanopowder deposited in an appropriate way on the surface of an AlSi12Cu2NiMg substrate was incorporated in the matrix using an electron beam technology. The samples were studied by means of light microscopy, SEM, and EDX; their microhardness was also determined. The formation was found of a uniform and dense coating with a thickness of 7 – 10 μgm with a good adherence to the substrate. A modified zone appeared under the coating with a thickness of 100 – 150 μgm containing dendrites of an α-solid solution and a fine eutectic between them, as well as primary silicon crystals. The microhardness of this modified zone was up to 2.4 times higher than that of the matrix. The results of SEM and EDX studies revealed unambiguously the presence of titanium in the coating and in the zones below it. Obviously, the electron beam treatment resulted in the TiCN nanoparticles penetrating into the coating and the substrate immediately below the coating.

Effect of resin infiltration on the color and microhardness of bleached white-spot lesions in bovine enamel (an in vitro study).

PubMed

Horuztepe, Sidika Aynur; Baseren, Meserret

2017-09-01

The aim of this study was to investigate both the effect of resin infiltration on the color and microhardness of white spot lesions (WSLs) that treated with bleaching and to analyze the penetration of the infiltrant. In each of 135 bovine enamel specimens, WSLs were produced. The samples were then randomly divided into three groups (n = 45): group I, bleached; group II, resin-infiltrated; group III, bleached and resin-infiltrated. The specimens were subjected to a pH-cycling regime for four weeks. The color and microhardness were measured at the baseline, after production of WSLs, after the treatments. The color alteration (ΔE*) and the percentage of surface microhardness recovery (SMHR) were calculated. The penetration of the infiltrant was evaluated by scanning electron microscopy. Results were analyzed with analysis of variance, Shapiro-Wilk, Tukey's, Kruskal-Wallis and Conover-Dunn tests (P = .05). The SMHR% in resin infiltration groups was significantly higher than that of the bleached group only (P < .05). Bleaching treatment prior to resin infiltration produced no significant change in the microhardness (P > .05). Using a bleaching treatment prior to resin infiltration produced significant color alteration (P < .05). The penetration of the resin infiltrant was deepest in-group II. The resin infiltration enhanced the microhardness of the WSLs regardless of whether or not a bleaching treatment was used. Using a bleaching treatment before resin infiltration resulted in color alteration, and it was also found to negatively influence the penetration of the infiltrant. © 2017 Wiley Periodicals, Inc.

Brazing of Carbon Carbon Composites to Cu-clad Molybdenum for Thermal Management Applications

NASA Technical Reports Server (NTRS)

Singh, M.; Asthana, R.; Shpargel, T> P.

2007-01-01

Advanced carbon carbon composites were joined to copper-clad molybdenum (Cu/Mo) using four active metal brazes containing Ti (Cu ABA, Cusin-1 ABA, Ticuni, and Ticusil) for potential use in thermal management applications. The brazed joints were characterized using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and Knoop microhardness measurements across the joint region. Metallurgically sound C-C/Cu/Mo joints, devoid of interfacial cracks formed in all cases. The joint interfaces were preferentially enriched in Ti, with Cu ABA joints exhibiting the largest interfacial Ti concentrations. The microhardness measurements revealed hardness gradients across the joint region, with a peak hardness of 300-350 KHN in Cusin-1 ABA and Ticusil joints and 200-250 KHN in Cu ABA and Ticuni joints, respectively.

Microstructures and Dry Sliding Wear Resistance of the Laser Ceramics Composite Coating on Pure Ti

NASA Astrophysics Data System (ADS)

Liu, Peng; Zhang, Yuanbin; Luo, Hui; Huo, Yushuang

2012-06-01

In this study, Al-Ti-Co was used to improve the surface performance of pure Ti. Laser cladding is an important surface modification technique, which can be used to improve the surface performance of pure Ti. Laser cladding of the Al-Ti-Co + TiB2 pre-placed powders on pure Ti can form ceramics reinforced the composite coating, which improved the wear resistance of the substrate. Characteristics of the composite coating were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), microhardness and wear tests. And the laser-cladded coating can also have major dilution from the substrate. Due to the action of the fine grain strengthening and the phase constituent, the wear resistance and microhardness of pure Ti surface were greatly improved.

The Influence of Duration of Mechanical Activation of Titanium Powder on its Morphology, Microstructure, and Microhardness

NASA Astrophysics Data System (ADS)

Ditenberg, I. A.; Korchagin, M. A.; Pinzhin, Yu. P.; Melnikov, V. V.; Tyumentsev, A. N.; Grinyaev, K. V.; Smirnov, I. V.; Radishevskii, V. L.; Tsverova, A. S.; Sukhanov, I. I.

2017-10-01

Using the methods of X-ray diffraction analysis and scanning and transmission electron microscopy, an investigation of the influence of duration of mechanical activation on morphology and structure of titanium powder is performed. In the course of processing the following stages of material transformation are revealed: fragmentation of the initial powder, conglomeration, and ovalization of the conglomerates. It is found that when the duration of mechanical activation increases, the characteristic size of coherent scattering regions is significantly decreased, which is accompanied by an increase in the value of microdistortions and intensive fragmentation of the crystal lattice inside powder particles followed by the formation of highly defective nanostructured states. The transformation of microstructure is accompanied by a considerable increase in microhardness.

Microstructure Evolution and Mechanical Properties of Al-TiB2/TiC In Situ Aluminum-Based Composites during Accumulative Roll Bonding (ARB) Process

PubMed Central

Nie, Jinfeng; Wang, Fang; Li, Yusheng; Cao, Yang; Liu, Xiangfa; Zhao, Yonghao; Zhu, Yuntian

2017-01-01

In this study, a kind of Al-TiB2/TiC in situ composite was successfully prepared using the melt reaction method and the accumulative roll-bonding (ARB) technique. The microstructure evolution of the composites with different deformation treatments was characterized using field emission scanning electron microscopy (FESEM) and a transmission electron microscope (TEM). The mechanical properties of the Al-TiB2/TiC in situ composite were also studied with tensile and microhardness tests. It was found that the distribution of reinforcement particles becomes more homogenous with an increasing ARB cycle. Meanwhile, the mechanical properties showed great improvement during the ARB process. The ultimate tensile strength (UTS) and microhardness of the composites were increased to 173.1 MPa and 63.3 Hv after two ARB cycles, respectively. Furthermore, the strengthening mechanism of the composite was analyzed based on its fracture morphologies. PMID:28772467

Experimental Study of the Microstructure and Micromechanical Properties of Laser Cladded Ni-based Amorphous Composite Coatings

NASA Astrophysics Data System (ADS)

Li, Ruifeng; Zheng, Qichi; Zhu, Yanyan; Li, Zhuguo; Feng, Kai; Liu, Chuan

2018-01-01

(Ni0.6Fe0.4)65B18Si10Nb4C3 amorphous composite coating was successfully fabricated on AISI 1045 steel substrate by using laser cladding process with coaxial powder feeding equipment. The microstructure and phase distribution of the coating were investigated by using x-ray diffraction, scanning electron microscopy and transmission electron microscope. The mechanical properties of the coating were examined by using microhardness testing and nanoindentation. The experimental results indicated that the volume fraction of amorphous phase increased with the decrease in laser cladding heat input, leading to an improvement of mean microhardness and nanohardness. NbC particles in a size ranging between 150 and 1650 nm were found embedding in the amorphous composite coatings in all situations. The presence of the NbC particles can contribute to an improvement of 96.7 HV in hardness on the basis of experimental results, while theoretical prediction suggests an improvement of 92.5 HV by using Orowan-Ashby equation.

Effect of deformation path on microstructure, microhardness and texture evolution of interstitial free steel fabricated by differential speed rolling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hamad, Kotiba; Chung, Bong Kwon; Ko, Young Gun, E-mail: younggun@ynu.ac.kr

2014-08-15

This paper reports the effect of the deformation path on the microstructure, microhardness, and texture evolution of interstitial free (IF) steel processed by differential speed rolling (DSR) method. For this purpose, total height reductions of 50% and 75% were imposed on the samples by a series of differential speed rolling operations with various height reductions per pass (deformation levels) ranging from 10 to 50% under a fixed roll speed ratio of 1:4 for the upper and lower rolls, respectively. Microstructural observations using transmission electron microscopy and electron backscattered diffraction measurements showed that the samples rolled at deformation level of 50%more » had the finest mean grain size (∼ 0.5 μm) compared to the other counterparts; also the samples rolled at deformation level of 50% showed a more uniform microstructure. Based on the microhardness measurements along the thickness direction of the deformed samples, gradual evolution of the microhardness value and its homogeneity was observed with the increase of the deformation level per pass. Texture analysis showed that, as the deformation level per pass increased, the fraction of alpha fiber and gamma fiber in the deformed samples increased. The textures obtained by the differential speed rolling process under the lubricated condition would be equivalent to those obtained by the conventional rolling. - Highlights: • Effect of DSR deformation path on microstructure of IF steel is significant. • IF steel rolled at deformation level of 50% has the ultrafine grains of ∼ 0.5 μm. • Rolling texture components are pronounced with increasing deformation level.« less

The effect of human blood on the setting and surface micro-hardness of calcium silicate cements.

PubMed

Song, Minju; Yue, Wonyoung; Kim, Soyeon; Kim, Wooksung; Kim, Yaelim; Kim, Jeong-Woong; Kim, Euiseong

2016-11-01

The purpose of the present study was to evaluate the effects of human blood on the setting and microhardness of calcium silicate cements. Three types of silicate-based cements were used: ProRoot MTA (PMTA), OrthoMTA (OMTA), and RetroMTA (RMTA). Mixed cement was placed into polyethylene molds with lengths of 2 and 4 mm. After storage for 4 days under three different storage conditions, i.e., saline, saline after 5 min of human blood, and human blood, the polyethylene molds were removed. With the specimens set, the surface microhardness was measured using a Vickers microhardness tester, crystalline structure was analyzed with X-ray diffraction (XRD), and the surface characteristics were examined with scanning electron microscopy (SEM). All specimens of 4 mm in length were set with all materials, and the blood groups exhibited lower microhardnesses than did the saline groups (p < 0.05). Among the 2-mm specimens that were stored in blood, the numbers of specimens that set were significantly different across the materials (p < 0.001). Regarding the microhardnesses of the RMTA and OMTA groups, there were no significant differences between storage conditions. For the PMTA group, only one specimen that was set in the blood group exhibited reduced microhardness. XRD showed changes of crystalline structure in the PMTA and OMTA blood group, whereas RMTA did not. SEM analysis revealed more rounded and homogeneous structures and demonstrated a clear lack of acicular or needle-like crystals in the PMTA and OMTA blood groups, while RMTA did not reveal substantial differences between the saline- and blood-stored groups. Blood contamination detrimentally affected the surface microhardnesses of all materials; furthermore, among the 2-mm specimens, blood contamination interfered with normal setting. Therefore, RMTA might be a more suitable choice when blood contamination is unavoidable due to limited depth. Clinical relevance RetroMTA might be a more suitable choice in situations in which blood contamination is unavoidable.

The microstructure and microhardness of friction stir welded dissimilar copper/Al-5% Mg alloys

NASA Astrophysics Data System (ADS)

Kalashnikova, T. A.; Shvedov, M. A.; Vasilyev, P. A.

2017-12-01

A friction stir welded joint between copper and aluminum alloy has been investigated and characterized for the microstructure and microhardness number distribution. The microstructural evolution of the joint is studied using optical microscopy and microhardness. The mechanical characteristics in structural zones of FSW joints are determined by Vickers microhardness measurements. Samples were cut across the cross section. It is shown that intermetallic Cu/Al particles are formed at interfaces. The intermetallics microhardness in the dissimilar aluminum/cooper FSW joint differs from that of the joint produced by fusion welding. The grain structures obtained in different dissimilar joint zones are examined.

Microstructure of rapidly solidified Nb-based pre-alloyed powders for additive manufacturing

NASA Astrophysics Data System (ADS)

Guo, Yueling; Jia, Lina; Kong, Bin; Zhang, Shengnan; Zhang, Fengxiang; Zhang, Hu

2017-07-01

For powder-based additive manufacturing, sphere-shaped Nb-37Ti-13Cr-2Al-1Si pre-alloyed powders were prepared by plasma rotating electrode processing (PREP). The microstructure, surface oxidation and microhardness of the pre-alloyed powders were systematically investigated. Results showed that the main phases were Nb solid solution (Nbss) and Cr2Nb. The Cr2Nb phases were further determined using transmission electron microscopy (TEM). Fine dendrite structures were observed in the as-fabricated pre-alloyed powders, which transformed to large grains after heat treatment (HT) at 1450 °C for 3 h. With the increase of powder size, the secondary dendrite arm spacing (SDAS) increased and the microhardness (HV) decreased. A clean powder surface free of oxide particles was obtained by PREP and an oxide layer with 9.39 nm in thickness was generated on the powder surface. Compared with Cr- and Nb-oxides, more Ti-oxides were formed on outmost powder surface with a higher content of Ti (up to 47.86 at.%). The differences upon the microstructure and microhardness of the pre-alloyed powders with different sizes were discussed.

Structure and Mechanical Properties of CrTiAlN/TiAlN Composite Coatings Deposited by Multi-Arc Ion Plating

NASA Astrophysics Data System (ADS)

Yan, Shaojian; Tian, Canxin; Huang, Zhihong; Yang, Bing; Fu, Dejun

2014-10-01

CrTiAlN/TiAlN composite coatings were deposited on cemented carbide by using a home-made industrial scale multi-arc ion plating system. The samples were studied by X-ray diffraction, scanning electron microscopy (SEM), microhardness and ball-on-disk testing. The properties of the CrTiAlN/TiAlN coatings were significantly influenced by the microstructure and the deposition time ratio of TiAlN over CrTiAlN layers. With the increase of deposition time ratio, the microhardness of CrTiAlN/TiAlN increased from 28.6 GPa to 37.5 GPa, much higher than that of CrTiAlN coatings. The friction coefficients of the CrTiAlN/TiAlN coatings were higher than those of CrTiAlN coatings against a cemented carbide ball. The microhardness of the CrTiAlN/TiAlN coatings was changed after annealing at 800°C, and the friction coefficients of the annealed coatings were increased against the cemented carbide ball.

Effect of Heat Input and Post-Weld Heat Treatment on the Mechanical and Metallurgical Characteristics of Laser-Welded Maraging Steel Joints

NASA Astrophysics Data System (ADS)

Karthikeyan, R.; Saravanan, M.; Singaravel, B.; Sathiya, P.

This paper investigates the impact of heat input and post-weld aging behavior at different temperatures on the laser paper welded maraging steel grade 250. Three different levels of heat inputs were chosen and CO2 laser welding was performed. Aging was done at six different temperatures: 360∘C, 400∘C, 440∘C, 480∘C, 520∘C and 560∘C. The macrostructure and microstructure of the fusion zone were obtained using optical microscope. The microhardness test was performed on the weld zone. Tensile tests and impact tests were carried out for the weld samples and different age-treated weld samples. Fracture surfaces were investigated by scanning electron microscopy (SEM). Microhardness values of the fusion zone increased with increasing aging temperature, while the base metal microhardness value decreased. Tensile properties increased with aging temperature up to 480∘C and reduced for 520∘C and 560∘C. This was mainly due to the formation of reverted austenite beyond 500∘C. XRD analysis confirmed the formation of reverted austenite.

Microstructures and Properties of Laser Cladding Al-TiC-CeO2 Composite Coatings

PubMed Central

Kong, Dejun; Song, Renguo

2018-01-01

Al-TiC-CeO2 composite coatings have been prepared by using a laser cladding technique, and the microstructure and properties of the resulting composite coatings have been investigated using scanning electron microscopy (SEM), a 3D microscope system, X-ray diffraction (XRD), micro-hardness testing, X-ray stress measurements, friction and wear testing, and an electrochemical workstation. The results showed that an Al-Fe phase appears in the coatings under different applied laser powers and shows good metallurgical bonding with the matrix. The dilution rate of the coating first decreases and then increases with increasing laser power. The coating was transformed from massive and short rod-like structures into a fine granular structure, and the effect of fine grain strengthening is significant. The microhardness of the coatings first decreases and then increases with increasing laser power, and the maximum microhardness can reach 964.3 HV0.2. In addition, the residual stress of the coating surface was tensile stress, and crack size increases with increasing stress. When the laser power was 1.6 kW, the coating showed high corrosion resistance. PMID:29373555

Microstructures and Properties of Laser Cladding Al-TiC-CeO₂ Composite Coatings.

PubMed

He, Xing; Kong, Dejun; Song, Renguo

2018-01-26

Al-TiC-CeO₂ composite coatings have been prepared by using a laser cladding technique, and the microstructure and properties of the resulting composite coatings have been investigated using scanning electron microscopy (SEM), a 3D microscope system, X-ray diffraction (XRD), micro-hardness testing, X-ray stress measurements, friction and wear testing, and an electrochemical workstation. The results showed that an Al-Fe phase appears in the coatings under different applied laser powers and shows good metallurgical bonding with the matrix. The dilution rate of the coating first decreases and then increases with increasing laser power. The coating was transformed from massive and short rod-like structures into a fine granular structure, and the effect of fine grain strengthening is significant. The microhardness of the coatings first decreases and then increases with increasing laser power, and the maximum microhardness can reach 964.3 HV 0.2 . In addition, the residual stress of the coating surface was tensile stress, and crack size increases with increasing stress. When the laser power was 1.6 kW, the coating showed high corrosion resistance.

Microhardness and morphological changes induced by Nd:Yag laser on dental enamel: an in vitro study.

PubMed

Bedini, Rossella; Manzon, Licia; Fratto, Giovanni; Pecci, Raffaella

2010-01-01

The aim of this work was a scanning electron microscopy (SEM) evaluation of the hardness and morphological changes of enamel irradiated by neodymium: yttrium aluminium garnet (Nd:YAG) laser with different energy levels. Twenty-eight human teeth samples were divided into 4 groups: control, where enamel surface was not lased, and 3 test treated with 3 different levels of energy power 0.6, 1.2 and 2.4 Watt, respectively. In each group, 5 samples underwent Vickers micro-hardness test and 2 samples were processed for SEM. No significant differences between treated and non treated samples were found by micro-hardness test. However, by SEM, test samples showed a rougher enamel surface than control. Specifically, the 0.6 Watt treated samples showed vertical scratches and glass-like areas, while in the other 2 groups enamel surface was covered by craters and cracks. These findings suggest that enamel should be lased at a low energy level to preserve its integrity and reduce demineralization, and thus for dental caries prevention purposes; while high energy level creates a retentive surface suitable for sealant or composite anchorage.

Influence of artificial saliva on abrasive wear and microhardness of dental composites filled with nanoparticles.

PubMed

Mayworm, Camila D; Camargo, Sérgio S; Bastian, Fernando L

2008-09-01

The aim of this study is to compare the wear resistance and hardness of two dental nanohybrid composites and to evaluate the influence of artificial saliva storage on those properties. Specimens were made from two commercial nanohybrid dental composites (Esthet-X-Dentsply and Filtek Supreme-3M). Abrasion tests were carried out in a ball-cratering machine (three body abrasion) and microscopic analysis of the wear surfaces was made using optical and scanning electron microscopy; hardness was quantified by Vickers hardness test. Those tests were repeated on specimens stored in artificial saliva. Results show that the wear rate of the studied materials is within 10(-7)mm(3)/Nmm range, one of the composites presenting wear rate twice as large as the other. After storage in artificial saliva, the wear resistance increases for both materials. Microhardness of the composites is around 52 and 64HV, Esthet-X presents higher hardness values than Filtek Supreme. After storage in artificial saliva, the microhardness of both materials decreases. Data were analyzed using ANOVA test, p < or = 0.05. Artificial saliva storage increases the materials' wear resistance, suggesting that in both materials bulk post-cure takes place and saliva absorption occurs only on the surface of the composites. This effect was confirmed by comparing the Vickers hardness before and after artificial saliva treatment and FTIR analyses. Surface microhardness of the composites decreases after storage in artificial saliva whereas bulk microhardness of the materials increases.

Selective Laser Treatment on Cold-Sprayed Titanium Coatings: Numerical Modeling and Experimental Analysis

NASA Astrophysics Data System (ADS)

Carlone, Pierpaolo; Astarita, Antonello; Rubino, Felice; Pasquino, Nicola; Aprea, Paolo

2016-12-01

In this paper, a selective laser post-deposition on pure grade II titanium coatings, cold-sprayed on AA2024-T3 sheets, was experimentally and numerically investigated. Morphological features, microstructure, and chemical composition of the treated zone were assessed by means of optical microscopy, scanning electron microscopy, and energy dispersive X-ray spectrometry. Microhardness measurements were also carried out to evaluate the mechanical properties of the coating. A numerical model of the laser treatment was implemented and solved to simulate the process and discuss the experimental outcomes. Obtained results highlighted the key role played by heat input and dimensional features on the effectiveness of the treatment.

Laser beam welding of Waspaloy: Characterization and corrosion behavior evaluation

NASA Astrophysics Data System (ADS)

Shoja Razavi, Reza

2016-08-01

In this work, a study on Nd:YAG laser welding of Waspaloy sheets has been made. Microstructures, phase changes and hardness of the laser joint were investigated using optical microscopy, scanning electron microscopy (SEM), field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), X-ray diffraction analysis (XRD) and vickers microhardness (HV0.3). Corrosion behavior of the weldment at low temperature in 3.5%wt NaCl solution at room temperature was also investigated using open circuit potential and cyclic potentiodynamic polarization tests. Hot corrosion studies were conducted on samples in the molten salt environment (Na2SO4-60%V2O5) at 900 °C for 50 h. Results indicated that the microstructure of weld zone was mainly dendritic grown epitaxially in the direction perpendicular to the weld boundary and heat transfer. Moreover, the Ti-Mo carbide particles were observed in the structure of the weld zone and base metal. The average size of carbides formed in the base metal (2.97±0.5 μm) was larger than that of the weld zone (0.95±0.2 μm). XRD patterns of the weld zone and base metal showed that the laser welding did not alter the phase structure of the weld zone, being in γ-Ni(Cr) single phase. Microhardness profile showed that the hardness values of the weld zone (210-261 HV) were lower than that of the base metal (323-330 HV). Electrochemical and hot corrosion tests indicated that the corrosion resistance of the weld metal was greater than the base metal in both room and high temperatures.

Microstructure evolution of heat treated NiTi alloys

NASA Astrophysics Data System (ADS)

Losertová, M.; Štencek, M.; Matýsek, D.; Štefek, O.; Drápala, J.

2017-11-01

Superelastic behavior of off-stoichiometric NiTi alloys is significantly affected by microstructure changes due to heat treatment. Applying appropriate thermal treatments important effects on microstructural changes, transformation temperatures and thermomechanical properties of final NiTi products can be achieved. The experimental samples of NiTi alloy with 55.8 wt.% Ni were submitted to heat treatment and the microstructures before and after the treatment were observed. The thermal regimes consisted of annealing treatment at 600 °C for 1 hour followed by water quenching and of ageing at eight different temperatures (250, 270, 290, 300, 350, 400, 450 and 500 °C) for 30 minutes. Microstructure features studied by means of optical and scanning electron microscopies, EDX microanalyses, X-ray diffraction analyses and microhardness measurement, have shown that higher ageing temperatures led to microstructure changes and corresponding increase in microhardness.

Tensile Deformation Temperature Impact on Microstructure and Mechanical Properties of AISI 316LN Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Xiong, Yi; He, Tiantian; Lu, Yan; Ren, Fengzhang; Volinsky, Alex A.; Cao, Wei

2018-03-01

Uniaxial tensile tests were conducted on AISI 316LN austenitic stainless steel from - 40 to 300 °C at a rate of 0.5 mm/min. Microstructure and mechanical properties of the deformed steel were investigated by optical, scanning and transmission electron microscopies, x-ray diffraction, and microhardness testing. The yield strength, ultimate tensile strength, elongation, and microhardness increase with the decrease in the test temperature. The tensile fracture morphology has the dimple rupture feature after low-temperature deformations and turns to a mixture of transgranular fracture and dimple fracture after high-temperature ones. The dominating deformation microstructure evolves from dislocation tangle/slip bands to large deformation twins/slip bands with temperature decrease. The deformation-induced martensite transformation can only be realized at low temperature, and its quantity increases with the decrease in the temperature.

Effect of various tooth whitening modalities on microhardness, surface roughness and surface morphology of the enamel.

PubMed

Kwon, So Ran; Kurti, Steven R; Oyoyo, Udochukwu; Li, Yiming

2015-09-01

The purpose of this study was to evaluate the effect of four whitening modalities on surface enamel as assessed with microhardness tester, profilometer, and scanning electron microscopy (SEM). Whitening was performed according to manufacturer's directions for over-the-counter (OTC), dentist dispensed for home use (HW) and in-office (OW) whitening. Do-it-yourself (DIY) whitening consisted of a strawberry and baking soda mix. Additionally, negative and positive controls were used. A total of 120 enamel specimens were used for microhardness testing at baseline and post-whitening. Following microhardness testing specimens were prepared for SEM observations. A total of 120 enamel specimens were used for surface roughness testing at baseline and post-whitening (n = 20 per group). Rank-based Analysis of Covariance was performed to compare microhardness and surface roughness changes. Tests of hypotheses were two-sided with α = 0.05. There was a significant difference in Knoop hardness changes (ΔKHN) among the groups (Kruskal-Wallis test, p < 0.0001). Significant hardness reduction was observed in the positive control and DIY group (p < 0.0001). Mean surface roughness changes (ΔRa) were significantly different among the groups (Kruskal-Wallis test, p < 0.0001). Surface roughness increased in the OTC group (p = 0.03) and in the positive control (p < 0.0001). The four whitening modalities-DIY, OTC, HW and OW induced minimal surface morphology changes when observed with SEM. It can be concluded that none of the four whitening modalities adversely affected enamel surface morphology. However, caution should be advised when using a DIY regimen as it may affect enamel microhardness and an OTC product as it has the potential to increase surface roughness.

Changes in surface morphology and mineralization level of human enamel following in-office bleaching with 35% hydrogen peroxide and light irradiation.

PubMed

Berger, Sandrine Bittencourt; Cavalli, Vanessa; Ambrosano, Glaucia Maria Bovi; Giannini, Marcelo

2010-01-01

The objective of this study was to evaluate the alterations on surface morphology and mineral loss of human enamel following in-office bleaching with 35% hydrogen peroxide and light irradiation. Dental enamel samples were obtained from human third molars and randomly divided into 10 groups (n = 10). The control group remained untreated. Bleached groups were treated with one of three whitening products. Bleaching was performed in a single session, during which bleaching gel was applied to the enamel surface three times for 10 minutes each time. During treatment, the bleaching agents were either irradiated by a halogen light or an LED/diode laser or were not irradiated at all. Microhardness testing was performed with a Knoop indentor and the surface morphologic observations were carried out by scanning electron microscopy (SEM). Cross-sectional microhardness (CSMH) and polarized light microscopy (PLM) were used to measure the depth of demineralization. The results revealed a significant decrease in surface microhardness values and changes to the enamel morphology after bleaching. CSMH and PLM showed that bleached enamel presented lower volume percentage of mineral up to 40 micrometers from the enamel surface and demineralization areas located in the subsuperficial region of enamel, respectively. It was concluded that 35% hydrogen peroxide can alter the surface morphology and the mineralization level of the dental enamel surface and sub-surface regardless of what type of bleaching light is used.

Microstructure and Antiwear Property of Laser Cladding Ni–Co Duplex Coating on Copper

PubMed Central

Wang, Yiyong; Liang, Zhipeng; Zhang, Junwei; Ning, Zhe; Jin, Hui

2016-01-01

Ni–Co duplex coatings were cladded onto Cu to improve the antiwear properties of Cu products. Prior to laser cladding, n-Al2O3/Ni layers were introduced as interlayers between laser cladding coatings and Cu substrates to improve the laser absorptivity of these substrates and ensure defect-free laser cladding coatings. The structure and morphology of the coatings were characterized by scanning electron microscopy and optical microscopy, and the phases of the coatings were analyzed by X-ray diffraction. Their hardness was measured using a microhardness tester. Experimental results showed that defect-free composite coatings were obtained and that the coatings were metallurgically bonded to the substrates. The surface of the Ni–Co duplex coatings comprised a Co-based solid solution, Cr7C3, (Fe,Ni)23C6, and other strengthening phases. The microhardness and wear resistance of the duplex coatings were significantly improved compared with the Cu substrates. The average microhardness of the cladded coatings was 845.6 HV, which was approximately 8.2 times greater than that of the Cu substrates (102.6 HV). The volume loss of the Cu substrates was approximately 7.5 times greater than that of the Ni–Co duplex coatings after 60 min of sliding wear testing. The high hardness of and lack of defects in the Ni–Co duplex coatings reduced the plastic deformation and adhesive wear of the Cu substrates, resulting in improved wear properties. PMID:28773755

Effect of polyvinyl siloxane impression material on the polymerization of composite resin.

PubMed

Chen, Liang; Kleverlaan, Cornelis Johannes; Liang, Kunneng; Yang, Deqin

2017-04-01

Polyvinyl siloxane impression material has been widely used as a lingual matrix for rebuilding missing tooth structure with composite resin. The composite resin is light polymerized in contact with the polyvinyl siloxane impression material. However, polyvinyl siloxane impression material has been shown to interact with other dental materials. The purpose of this study was to assess the effect of polyvinyl siloxane impression materials on the polymerization of composite resins by assessing the Vickers microhardness and degree of conversion of polyvinyl siloxane. The composite resins were light polymerized in contact with 3 polyvinyl siloxane impression materials (Flexitime Easy Putty; President Light Body; Xantopren L Blue) (n=8) and in contact with a matrix strip as the control group (n=8). Vickers microhardness and degree of conversion on contact surfaces were measured to evaluate the polymerization of composite resins. The depth of the effect was assessed by Vickers microhardness on section surfaces and observed with scanning electron microscopy. The results were analyzed by 1-way analysis of variance and the post hoc Tukey honest significant differences test (α=.05). The Vickers microhardness and degree of conversion values on the contact surfaces of the experiment groups were significantly lower than those of the control group (P<.05); the Vickers microhardness values on the section surfaces indicated that there was no significant difference at the same depth of different groups (P>.05). The scanning electron microscope observation showed that an approximately 10-μm deep unpolymerized layer was found in the experimental group. Polyvinyl siloxane impression materials have an inhibitory effect on the polymerization of the composite resins, but just limited to within approximately 10 μm from the surface in contact with the impression material. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Study of the high power laser-metal interactions in the gaseous atmospheres

NASA Astrophysics Data System (ADS)

Lugomer, Stjepan; Bitelli, G.; Stipancic, M.; Jovic, F.

1994-08-01

The tantalum and titanium plates were treated by pulsed, high power CO2 laser in the pressurized atmospheres of N2 and O2. Studies performed by the optical microscopy, microhardness measurements, and the auger electron spectroscopy revealed: (1) topographic modification of the surface caused by the temperature field; (2) metal hardening, caused by the laser shock; and (3) alloying/cladding, caused by the chemical reaction between the metal surface and the gaseous atmosphere.

Chemical Synthesis and Oxide Dispersion Properties of Strengthened Tungsten via Spark Plasma Sintering

PubMed Central

Ding, Xiao-Yu; Luo, Lai-Ma; Chen, Hong-Yu; Zhu, Xiao-Yong; Zan, Xiang; Cheng, Ji-Gui; Wu, Yu-Cheng

2016-01-01

Highly uniform oxide dispersion-strengthened materials W–1 wt % Nd2O3 and W–1 wt % CeO2 were successfully fabricated via a novel wet chemical method followed by hydrogen reduction. The powders were consolidated by spark plasma sintering at 1700 °C to suppress grain growth. The samples were characterized by performing field emission scanning electron microscopy and transmission electron microscopy analyses, Vickers microhardness measurements, thermal conductivity, and tensile testing. The oxide particles were dispersed at the tungsten grain boundaries and within the grains. The thermal conductivity of the samples at room temperature exceeded 140 W/m·K. The tensile tests indicated that W–1 wt % CeO2 exhibited a ductile–brittle transition temperature between 500 °C and 550 °C, which was a lower range than that for W–1 wt % Nd2O3. Surface topography and Vickers microhardness analyses were conducted before and after irradiations with 50 eV He ions at a fluence of 1 × 1022 m−2 for 1 h in the large-powder material irradiation experiment system. The grain boundaries of the irradiated area became more evident than that of the unirradiated area for both samples. Irradiation hardening was recognized for the W–1 wt % Nd2O3 and W–1 wt % CeO2 samples. PMID:28773999

Mechanical behavior and failure analysis of prosthetic retaining screws after long-term use in vivo. Part 2: Metallurgical and microhardness analysis.

PubMed

Al Jabbari, Youssef; Fournelle, Raymond; Ziebert, Gerald; Toth, Jeffrey; Iacopino, Anthony

2008-04-01

This study involved testing and analyzing multiple retrieved prosthetic retaining screws after long-term use in vivo to: (1) detect manufacturing defects that could affect in-service behavior; (2) characterize the microstructure and alloy composition; and (3) further characterize the wear mechanism of the screw threads. Two new (control) screws from Nobel Biocare (NB) and 18 used (in service 18-120 months) retaining screws [12 from NB and 6 from Sterngold (SG)] were: (1) metallographically examined by light microscopy and scanning electron microscopy (SEM) to determine the microstructure; (2) analyzed by energy dispersive X-ray (EDX) microanalysis to determine the qualitative and semiquantitative average alloy and individual phase compositions; and (3) tested for Vickers microhardness. Examination of polished longitudinal sections of the screws using light microscopy revealed a significant defect in only one Group 4 screw. No significant defects in any other screws were observed. The defect was considered a "seam" originating as a "hot tear" during original casting solidification of the alloy. Additionally, the examination of longitudinal sections of the screws revealed a uniform homogeneous microstructure in some groups, while in other groups the sections exhibited rows of second phase particles. The screws for some groups demonstrated severe deformation of the lower threads and the bottom part of the screw leading to the formation of crevices and grooves. Some NB screws were comprised of Au-based alloy with Pt, Cu, and Ag as alloy elements, while others (Groups 4 and 19) were Pd-based with Ga, Cu, and Au alloy elements. The microstructure was homogeneous with fine or equiaxed grains for all groups except Group 4, which appeared inhomogeneous with anomalous grains. SG screws demonstrated a typical dendritic structure and were Au-based alloy with Cu and Ag alloy elements. There were differences in the microhardness of gold alloy screws from NB and SG as well as palladium alloy screws from NB. Significant differences within NB retaining screws and between NB and SG screws were found for microstructure, major alloy constituents, and microhardness.

M551 metals melting experiment

NASA Technical Reports Server (NTRS)

Busch, G.

1977-01-01

Electron beam welding studies were conducted in the Skylab M551 metals melting experiment, on three different materials; namely 2219-T87 aluminum alloy, 304L stainless steel, and commercially pure tantalum (0.5 wt % columbium). Welds were made in both one gravity and zero gravity (Skylab) environments. Segments from each of the welds were investigated by microhardness, optical microscopy, scanning microscopy, and electron probe techniques. In the 2219-T87 aluminum alloy samples, macroscopic banding and the presence of an eutectic phase in the grain boundaries of the heat affected zone were observed. The stainless steel samples exhibited a sharp weld interface and macroscopic bands. The primary microstructural features found in the tantalum were the presence of either columnar grains (ground base) or equiaxed grains (Skylab). The factors contributing to these effects are discussed and the role of reduced gravity in welding is considered.

Chemical removal of necrotic periodontal ligament on delayed replanted teeth by sodium hypochlorite: morphological analysis and microhardness indentation test of cementum.

PubMed

Bai, J; Qin, M; Zhao, Y-M; Huang, M-W; Ji, A-P

2016-04-01

To compare the efficacy of sodium hypochlorite (NaOCl) used at different concentrations and working times for removing necrotic periodontal ligament (PDL) from delayed replanted teeth and to observe the effects of NaOCl on surface structure and microhardness of cementum. A total of 88 healthy premolars with a single root extracted for orthodontic purposes were selected and kept dry at room temperature for 1 h. The teeth were divided into 11 groups: group 1 (control): roots were untreated; group 2: necrotic PDL was removed with gauze; groups 3-11: teeth were immersed in NaOCl at different concentrations (1, 2.5 and 5.25%) and for different working times (5, 10 and 15 min). The specimens in each group were inspected separately for cementum integrity and the presence of PDL remnants by histomorphometric analysis, confocal laser scanning microscopy (CLSM) and scanning electron microscopy (SEM). Another 14 healthy premolars with roots divided into two pieces were selected for Vickers microhardness indentation tests before and after NaOCl treatment. The data were analysed statistically using Wilcoxon signed-rank test of two-related samples (P = 0.05). In teeth treated with 1% NaOCl for 15 min or 5.25% NaOCl for 5 min, the cementum remained morphologically intact without cracks, and PDL remnants were absent. In the 1% NaOCl for 15 min group, the microstructure of cementum was arranged more regularly, as observed ×8000 magnification by SEM. Teeth in each of the other groups displayed cementum damage and/or the presence of PDL remnants. Microhardness tests revealed that treatment with 1% NaOCl for 15 min or 5.25% NaOCl for 5 min significantly decreased microhardness of root cementum (P < 0.05). Use of either 1% NaOCl for 15 min or 5.25% NaOCl for 5 min was effective at removing necrotic PDL from the delayed replanted teeth whilst having a minimal influence on cementum integrity. However, 1% NaOCl for 15 min was less damaging to cementum. © 2015 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Development of nano-structured duplex and ferritic stainless steels by pulverisette planetary milling followed by pressureless sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

R, Shashanka, E-mail: shashankaic@gmail.com; Chaira, D., E-mail: chaira.debasis@gmail.com

Nano-structured duplex and ferritic stainless steel powders are prepared by planetary milling of elemental Fe, Cr and Ni powder for 40 h and then consolidated by conventional pressureless sintering. The progress of milling and the continuous refinement of stainless steel powders have been confirmed by means of X-ray diffraction and scanning electron microscopy. Activation energy for the formation of duplex and ferritic stainless steels is calculated by Kissinger method using differential scanning calorimetry and is found to be 159.24 and 90.17 KJ/mol respectively. Both duplex and ferritic stainless steel powders are consolidated at 1000, 1200 and 1400 °C in argonmore » atmosphere to study microstructure, density and hardness. Maximum sintered density of 90% and Vickers microhardness of 550 HV are achieved for duplex stainless steel sintered at 1400 °C for 1 h. Similarly, 92% sintered density and 263 HV microhardness are achieved for ferritic stainless steel sintered at 1400 °C. - Highlights: • Synthesized duplex and ferritic stainless steels by pulverisette planetary milling • Calculated activation energy for the formation of duplex and ferritic stainless steels • Studied the effect of sintering temperature on density, hardness and microstructure • Duplex stainless steel exhibits 90% sintered density and microhardness of 550 HV. • Ferritic stainless steel shows 92% sintered density and 263 HV microhardness.« less

Effect of carbonated water manufactured by a soda carbonator on etched or sealed enamel

PubMed Central

Ryu, Hyo-kyung; Kim, Yong-do; Heo, Sung-su

2018-01-01

Objective The purpose of this study was to determine the effects of carbonated water on etched or sealed enamel according to the carbonation level and the presence of calcium ions. Methods Carbonated water with different carbonation levels was manufactured by a soda carbonator. Seventy-five premolar teeth were randomly divided into a control group and 4 experimental groups in accordance with the carbonation level and the presence of calcium ions in the test solutions. After specimen preparation of the Unexposed, Etched, and Sealed enamel subgroups, all the specimens were submerged in each test solution for 15 minutes three times a day during 7 days. Microhardness tests on the Unexposed and Etched enamel subgroups were performed with 10 specimens from each group. Scanning electron microscopy (SEM) tests on the Unexposed, Etched, and Sealed enamel subgroups were performed with 5 specimens from each group. Microhardness changes in different groups were statistically compared using paired t-tests, the Wilcoxon signed rank test, and the Kruskal-Wallis test. Results The microhardness changes were significantly different between the groups (p = 0.000). The microhardness changes in all experimental groups except Group 3 (low-level carbonated water with calcium ions) were significantly greater than those in the Control group. SEM showed that etched areas of the specimen were affected by carbonated water and the magnitude of destruction varied between groups. Adhesive material was partially removed in groups exposed to carbonated water. Conclusions Carbonated water has negative effects on etched or sealed enamel, resulting in decreased microhardness and removal of the adhesive material. PMID:29291188

Evaluation of hemocompatibility and in vitro immersion on microwave-assisted hydroxyapatite-alumina nanocomposites.

PubMed

Radha, G; Balakumar, S; Venkatesan, Balaji; Vellaichamy, Elangovan

2015-05-01

This study reports the microwave-assisted synthesis and characterization of nHAp (nano-hydroxyapatite)-alumina composites. The crystalline phase and interaction of alumina with nHAp was analyzed using X-ray diffraction (XRD) and Raman microscopy analysis, respectively. High resolution transmission electron microscopy (HRTEM) micrographs exhibit morphological changes of nHAp composites with increasing alumina concentrations. Microhardness studies reveal the enhanced mechanical strength of nHAp10 and nHAp20 nanocomposites than pure nHAp. In vitro bioactivity of the nanocomposites was studied by immersing samples in simulated body fluid (Hank's solution) for 21 days. The surface of biomineralized samples were analyzed using field emission scanning electron microscopy (FESEM) and energy dispersive X-ray spectroscopy (EDX). Hemolytic assay revealed acceptable compatibility for varying concentrations of all the samples. Cell proliferation assay was systematically investigated for 1 day and 3 days on Saos-2 osteoblast-like cell lines and it was found that nHAp nanocomposites improved the proliferation. Copyright © 2015 Elsevier B.V. All rights reserved.

Effect of abrasive water jet on the structure of the surface layer of Al-Mg alloy

NASA Astrophysics Data System (ADS)

Tabatchikova, T. I.; Tereshchenko, N. A.; Yakovleva, I. L.; Gudnev, N. Z.

2017-09-01

Optical, scanning, and transmission electron microscopy methods, and X-ray diffraction analysis have been used to study the changes in the structure and the microhardness in the surface layer of the Al-Mg (5.8-6.8 wt %) alloy after water jet cutting. The dislocation density, the sizes of coherent scattering regions, and microdistortions have been determined. The transformation of the fine structure has been revealed in the displacement from the alloy volume to the abrasive-waterjet cutting surface.

Microstructure and corrosion resistance of TC2 Ti alloy by laser cladding with Ti/TiC/TiB2 powders

NASA Astrophysics Data System (ADS)

Diao, Yunhua; Zhang, Kemin

2015-10-01

In the present work, a TiC/TiB2 composite coating was produced onto a TC2 Ti alloy by laser cladding with Ti/TiC/TiB2 powders. The surface microstructure, phase components and compositions were characterized with methods of optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffractometry (XRD), and energy dispersive spectrometry (EDS). The cladding layer is consisted of Ti, TiC and TiB2. And the surface microhardness was measured. After laser cladding, a maximum hardness of 1100 HV is achieved in the laser cladding surface layer, which is more three times higher than that of the TC2 substrate (∼300 HV). Due to the formation of TiC and TiB2 intermetallic compounds in the alloyed region and grain refinement, the microhardness of coating is higher than TC2 Ti alloy. In this paper, the corrosion property of matrix material and treated samples were both measured in NaCl (3.5 wt%) aqueous solution. From the result we can see that the laser cladding specimens' corrosion property is clearly becoming better than that of the substrate.

Improvement in wear and corrosion resistance of AISI 1020 steel by high velocity oxy-fuel spray coating containing Ni-Cr-B-Si-Fe-C

NASA Astrophysics Data System (ADS)

Prince, M.; Thanu, A. Justin; Gopalakrishnan, P.

2012-04-01

In this investigation, AISI 1020 low carbon steel has been selected as the base material. The Ni based super alloy powder NiCrBSiFeC was sprayed on the base material using high velocity oxy-fuel spraying (HVOF) technique. The thickness of the coating was approximately 0.5 mm (500 μm). The coating was characterized using optical microscopy, Vickers microhardness testing, X-ray diffraction technique and scanning electron microscopy. Dry sliding wear tests were carried out at 3 m/s sliding speed under the load of 10 N for 1000 m sliding distance at various temperatures i.e., 35° C, 250° C and 350° C. The corrosion test was carried out in 1 M copper chloride in acetic acid solution. The polarization studies were also conducted for both base material and coating. The improvement in microhardness from 1.72 GPa (175 HV0.05) to 10.54 GPa (1075 HV0.05) was observed. The coatings exhibited 3-6 times improved wear resistance as compared with base material. Also, the corrosion rate was reduced by 3.5 times due to the presence of coatings.

Repulsive Interaction of Sulfide Layers on Compressor Impeller Blades Remanufactured Through Plasma Spray Welding

NASA Astrophysics Data System (ADS)

Chang, Y.; Zhou, D.; Wang, Y. L.; Huang, H. H.

2016-12-01

This study investigated the repulsive interaction of sulfide layers on compressor impeller blades remanufactured through plasma spray welding (PSW). Sulfide layers on the blades made of FV(520)B steel were prepared through multifarious corrosion experiments, and PSW was utilized to remanufacture blade specimens. The specimens were evaluated through optical microscopy, scanning electron microscopy, energy-dispersive spectroscopy, 3D surface topography, x-ray diffraction, ImageJ software analysis, Vicker's micro-hardness test and tensile tests. Results showed a large number of sulfide inclusions in the fusion zone generated by sulfide layers embodied into the molten pool during PSW. These sulfide inclusions seriously degraded the mechanical performance of the blades remanufactured through PSW.

Development of an in-situ multi-component reinforced Al-based metal matrix composite by direct metal laser sintering technique — Optimization of process parameters

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghosh, Subrata Kumar, E-mail: subratagh82@gmail.com; Bandyopadhyay, Kaushik; Saha, Partha

2014-07-01

In the present investigation, an in-situ multi-component reinforced aluminum based metal matrix composite was fabricated by the combination of self-propagating high-temperature synthesis and direct metal laser sintering process. The different mixtures of Al, TiO{sub 2} and B{sub 4}C powders were used to initiate and maintain the self-propagating high-temperature synthesis by laser during the sintering process. It was found from the X-ray diffraction analysis and scanning electron microscopy that the reinforcements like Al{sub 2}O{sub 3}, TiC, and TiB{sub 2} were formed in the composite. The scanning electron microscopy revealed the distribution of the reinforcement phases in the composite and phase identities.more » The variable parameters such as powder layer thickness, laser power, scanning speed, hatching distance and composition of the powder mixture were optimized for higher density, lower porosity and higher microhardness using Taguchi method. Experimental investigation shows that the density of the specimen mainly depends upon the hatching distance, composition and layer thickness. On the other hand, hatching distance, layer thickness and laser power are the significant parameters which influence the porosity. The composition, laser power and layer thickness are the key influencing parameters for microhardness. - Highlights: • The reinforcements such as Al{sub 2}O{sub 3}, TiC, and TiB{sub 2} were produced in Al-MMC through SHS. • The density is mainly influenced by the material composition and hatching distance. • Hatching distance is the major influencing parameter on porosity. • The material composition is the significant parameter to enhance the microhardness. • The SEM micrographs reveal the distribution of TiC, TiB{sub 2} and Al{sub 2}O{sub 3} in the composite.« less

The study of microstructure of wear-resistant coatings applied for protection from abrasive wear of horizontal and tilt drilling drill bits

NASA Astrophysics Data System (ADS)

Markova, I. Yu; Zakharova, E. S.; Maslov, A. L.; Polushin, N. I.; Laptev, A. I.; SOvchinnikova, M.

2017-05-01

Drill bits of the cutting type over the period of their existence have undergone significant changes - from the use of carbide cutters to diamond composite PDC elements, in which the diamond layer is applied to a hardmetal substrate. Using such elements, it was possible to significantly increase the service life of the drill bits, however, during work, there is a significant abrasive deterioration of the bit body, which does not fully realize the advantages of PDC elements. Therefore, to protect the body from wear use special wear-resistant coatings. This work is devoted to research of microstructural coatings, namely coatings brands WokaDur NiA, HR-6750, HR-6750 with sublayer Rock Dur 47 on various steel substrates which applied by the gas-thermal spraying in Ltd “Oerlikon Metko Rus”. They were examined with the use of scanning electron microscopy, X-ray phase analysis and a Vickers micro-hardness tester. It was established that the microhardness of the coating matrix is 590-660 HV, and the microhardness of tungsten carbide particles reinforcing the coating, is 2145-2455 HV.

Characterization of ultra-fine grained aluminum produced by accumulative back extrusion (ABE)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Alihosseini, H., E-mail: hamid.alihossieni@gmail.com; Materials Science and Engineering Department, Engineering School, Amirkabir University, Tehran; Faraji, G.

2012-06-15

In the present work, the microstructural evolutions and microhardness of AA1050 subjected to one, two and three passes of accumulative back extrusion (ABE) were investigated. The microstructural evolutions were characterized using transmission electron microscopy. The results revealed that applying three passes of accumulative back extrusion led to significant grain refinement. The initial grain size of 47 {mu}m was refined to the grains of 500 nm after three passes of ABE. Increasing the number of passes resulted in more decrease in grain size, better microstructure homogeneity and increase in the microhardness. The cross-section of ABEed specimen consisted of two different zones:more » (i) shear deformation zone, and (ii) normal deformation zone. The microhardness measurements indicated that the hardness increased from the initial value of 31 Hv to 67 Hv, verifying the significant microstructural refinement via accumulative back extrusion. - Highlights: Black-Right-Pointing-Pointer A significant grain refinement can be achieved in AA1050, Al alloy by applying ABE. Black-Right-Pointing-Pointer Microstructural homogeneity of ABEed samples increased by increasing the number of ABE cycles. Black-Right-Pointing-Pointer A substantial increase in the hardness, from 31 Hv to 67 Hv, was recorded.« less

The effect of different beverages on surface hardness of nanohybrid resin composite and giomer.

PubMed

Tanthanuch, Saijai; Kukiattrakoon, Boonlert; Siriporananon, Chantima; Ornprasert, Nawanda; Mettasitthikorn, Wathu; Likhitpreeda, Salinla; Waewsanga, Sulawan

2014-05-01

To investigate the effects of five beverages (apple cider, orange juice, Coca-Cola, coffee, and beer) on microhardness and surface characteristic changes of nanohybrid resin composite and giomer. Ninety-three specimens of each resin composite and giomer were prepared. Before immersion, baseline data of Vicker's microhardness was recorded and surface characteristics were examined using scanning electron microscopy (SEM). Five groups of discs (n = 18) were alternately immersed in 25 mL of each beverage for 5 s and in 25 mL of artificial saliva for 5 s for 10 cycles. Specimens were then stored in artificial saliva for 24 h. This process was repeated for 28 days. After immersion, specimens were evaluated and data were analyzed by two-way repeated analysis of variance (ANOVA), Tukey's honestly significant difference (HSD), and a t-test (α = 0.05). Microhardness of all groups significantly decreased after being immersed in the tested beverages (P < 0.05). SEM photomicrographs presented surface degradation of all groups. The effect of these beverages on the surface of both restorative materials also depended upon the exposure time and chemical composition of the restorative materials and beverages.

The effect of different beverages on surface hardness of nanohybrid resin composite and giomer

PubMed Central

Tanthanuch, Saijai; Kukiattrakoon, Boonlert; Siriporananon, Chantima; Ornprasert, Nawanda; Mettasitthikorn, Wathu; Likhitpreeda, Salinla; Waewsanga, Sulawan

2014-01-01

Aims: To investigate the effects of five beverages (apple cider, orange juice, Coca-Cola, coffee, and beer) on microhardness and surface characteristic changes of nanohybrid resin composite and giomer. Materials and Methods: Ninety-three specimens of each resin composite and giomer were prepared. Before immersion, baseline data of Vicker's microhardness was recorded and surface characteristics were examined using scanning electron microscopy (SEM). Five groups of discs (n = 18) were alternately immersed in 25 mL of each beverage for 5 s and in 25 mL of artificial saliva for 5 s for 10 cycles. Specimens were then stored in artificial saliva for 24 h. This process was repeated for 28 days. After immersion, specimens were evaluated and data were analyzed by two-way repeated analysis of variance (ANOVA), Tukey's honestly significant difference (HSD), and a t-test (α = 0.05). Results: Microhardness of all groups significantly decreased after being immersed in the tested beverages (P < 0.05). SEM photomicrographs presented surface degradation of all groups. Conclusions: The effect of these beverages on the surface of both restorative materials also depended upon the exposure time and chemical composition of the restorative materials and beverages. PMID:24944451

Microstructure and Phase Evolution in Mg-Gd and Mg-Gd-Nd Alloys With Additions of Zn, Y and Zr

NASA Astrophysics Data System (ADS)

Khawaled, S.; Bamberger, M.; Katsman, A.

Microstructure and phase evolution in Mg-Gd and Mg-Gd-Nd based alloys with additions of Zn, Zr and Y were analyzed in the as-cast, solution treated and aged conditions. Alloys has been investigated after solution treatment at 540°C for 24hr followed by isothermal aging at 175°C up to 32 days by using of Vickers hardness, optical microscopy, scanning electron microscopy equipped with EDS, X-ray diffraction and transmission electron microscopy. It was found that the as-cast alloys contained primary α-Mg matrix, eutecticlike structures, cuboid-like phases and Zr-rich clusters. The homogenized and quenched alloys contained primary α-Mg solid solution, smaller amount of divorced eutectic compounds, enlarged cuboid-like particles and Zr-rich clusters. The eutectic phase was Mg5Gd prototype with the composition Mg5(GdxNd1-x, x≈0.2). The compositions of the cuboid shaped particles are characterized by enlarged amount of Gd and can be written as Mg2(Gd x Y1-x) with x≈0.85 in the Mg-5Gd based alloy, and Gd4(YxNd1-x) with x≈0.5 in the Mg-6Gd-3.7Nd based alloy. The cuboid shaped particles grew during aging and reached 3µm average size. Precipitation of ß″ and ß' phases during aging was observed. Mg-6Gd-3.7Nd based alloy reached a maximum value of microhardness after 16 days of aging; in Mg-Gd based alloy, microhardness increased more slowly and reached a maximum value after 32 days of aging.

Effect of long-term aging on microstructure and local behavior in the heat-affected zone of a Ni–Cr–Mo–V steel welded joint

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu, Ming-Liang, E-mail: mlzhu@ecust.edu.cn; Wang, De-Qiang; Xuan, Fu-Zhen

2014-01-15

Evolution of microstructure, micro-hardness and micro-tensile strength behavior was investigated in the heat-affected zone of a Ni–Cr–Mo–V steel welded joint after the artificial aging at 350 °C for 3000 h. After detailed characterization of microstructures in optical microscopy, scanning electron microscopy and transmission electron microscopy, it is revealed that the change of martensite–bainite constituent promotes more homogeneous microstructure distribution. The aging treatment facilitates redistribution of carbon and chromium elements along the welded joint, and the micro-hardness is increased slightly through the welds due to enrichment of carbon. The types of precipitates in the weldment mainly include M{sub 3}C, MC, M{submore » 2}C and M{sub 23}C{sub 6}. The carbides in base metal, weld metal and coarse-grained heat-affected zone are prone to change from ellipsoidal to platelet form whereas more uniform spherical carbides are observed in the fine-grained zone. Precipitation and coarsening of M{sub 23}C{sub 6} near the fusion line, and formation of MC and M{sub 2}C, are responsible for the tensile strength decrease and its smooth distribution in the aged heat-affected zone. This implies that the thermal aging can relieve strength mismatch in the weldments. - Highlights: • Microstructure homogeneity improved in HAZ after long-term aging. • Tensile strength decreased in HAZ due to precipitation and coarsening of M{sub 23}C{sub 6}. • Strength mismatch in NiCrMoV steel welds was relieved after aging at 350 °C × 3000 h.« less

Phase constitution characteristics of the Fe-Al alloy layer in the HAZ of calorized steel pipe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li Yajiang; Zou Zengda; Wei Xing

1997-09-01

Mechanical properties of the welding region and phase constitution characteristics in the iron-aluminum (Fe-Al) alloy layer of calorized steel pipes were researched by means of metallography, which included the use of scanning electron microscopy (SEM), transmission electron microscopy (TEM), electron probe microanalysis (EPMA) and an X-ray diffractometer. Experimental results indicated that the Fe-Al alloy layer of calorized steel pipe was mainly composed of an FeAl phase, an Fe{sub 3}Al phase and an {alpha}-Fe(Al) solid solution, and the microhardness in the Fe-Al coating was 600--310 HM from the surface layer to the inside. There were no higher aluminum content phases, suchmore » as brittle FeAl{sub 2}, Fe{sub 2}Al{sub 5} and FeAl{sub 3}. By controlling the aluminizing process parameters, the ability to bear deformation and weld-ability of the calorized steel pipe were remarkably improved.« less

γ' Precipitation Study of a Co-Ni-Based Alloy

NASA Astrophysics Data System (ADS)

Locq, D.; Martin, M.; Ramusat, C.; Fossard, F.; Perrut, M.

2018-05-01

A Co-Ni-based alloy strengthened by γ'-(L12) precipitates was utilized to investigate the precipitation evolution after various cooling rates and several aging conditions. In this study, the precipitate size and volume fraction have been studied via scanning electron microscopy and transmission electron microscopy. The influence of the precipitation evolution was measured via microhardness tests. The cooling rate study shows a more sluggish γ' precipitation reaction compared to that observed in a Ni-based superalloy. Following a rapid cooling rate, the application of appropriate double aging treatments allows for the increase of the γ' volume fraction as well as the control of the size and distribution of the precipitates. The highest hardness values reach those measured on supersolvus cast and wrought Ni-based superalloys. The observed γ' precipitation behavior should have implications for the production, the heat treatment, the welding, or the additive manufacturing of this new class of high-temperature materials.

Microstructure and antibacterial properties of microwave plasma nitrided layers on biomedical stainless steels

NASA Astrophysics Data System (ADS)

Lin, Li-Hsiang; Chen, Shih-Chung; Wu, Ching-Zong; Hung, Jing-Ming; Ou, Keng-Liang

2011-06-01

Nitriding of AISI 303 austenitic stainless steel using microwave plasma system at various temperatures was conducted in the present study. The nitrided layers were characterized via scanning electron microscopy, glancing angle X-ray diffraction, transmission electron microscopy and Vickers microhardness tester. The antibacterial properties of this nitrided layer were evaluated. During nitriding treatment between 350 °C and 550 °C, the phase transformation sequence on the nitrided layers of the alloys was found to be γ → (γ + γ N) → (γ + α + CrN). The analytical results revealed that the surface hardness of AISI 303 stainless steel could be enhanced with the formation of γ N phase in nitriding process. Antibacterial test also demonstrated the nitrided layer processed the excellent antibacterial properties. The enhanced surface hardness and antibacterial properties make the nitrided AISI 303 austenitic stainless steel to be one of the essential materials in the biomedical applications.

Effects of the Process Parameters on the Microstructure and Properties of Nitrided 17-4PH Stainless Steel

NASA Astrophysics Data System (ADS)

Wang, Jun; Lin, Yuanhua; Zeng, Dezhi; Yan, Jing; Fan, Hongyuan

2013-04-01

The effects of process parameters on the microstructure, microhardness, and dry-sliding wear behavior of plasma nitrided 17-4PH stainless steel were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and wear testing. The results show that a wear-resistant nitrided layer was formed on the surface of direct current plasma nitrided 17-4PH martensitic stainless steel. The microstructure and thickness of the nitrided layer is dependent on the treatment temperature rather than process pressure. XRD indicated that a single α N phase was formed during nitriding at 623 K (350 °C). When the temperature increased, the α N phase disappeared and CrN transformed in the nitrided layer. The hardness measurement demonstrated that the hardness of the stainless substrate steel increased from 320 HV0.1 in the untreated condition increasing to about 1275HV0.1 after nitriding 623 K (350 °C)/600 pa/4 hours. The extremely high values of the microhardness achieved by the great misfit-induced stress fields associated with the plenty of dislocation group and stacking fault. Dry-sliding wear resistance was improved by DC plasma nitriding. The best wear-resistance performance of a nitrided sample was obtained after nitriding at 673 K (350 °C), when the single α N-phase was produced and there were no CrN precipitates in the nitrided layer.

Type 1 diabetes mellitus effects on dental enamel formation revealed by microscopy and microanalysis.

PubMed

Silva, Bruna Larissa Lago; Medeiros, Danila Lima; Soares, Ana Prates; Line, Sérgio Roberto Peres; Pinto, Maria das Graças Farias; Soares, Telma de Jesus; do Espírito Santo, Alexandre Ribeiro

2018-03-01

Type 1 diabetes mellitus (T1DM) largely affects children, occurring therefore at the same period of deciduous and permanent teeth development. The aim of this work was to investigate birefringence and morphology of the secretory stage enamel organic extracellular matrix (EOECM), and structural and mechanical features of mature enamel from T1DM rats. Adult Wistar rats were maintained alive for a period of 56 days after the induction of experimental T1DM with a single dose of streptozotocin (60 mg/kg). After proper euthanasia of the animals, fixed upper incisors were accurately processed, and secretory stage EOECM and mature enamel were analyzed by transmitted polarizing and bright field light microscopies (TPLM and BFLM), energy-dispersive x-ray (EDX) analysis, scanning electron microscopy (SEM), and microhardness testing. Bright field light microscopies and transmitted polarizing light microscopies showed slight morphological changes in the secretory stage EOECM from diabetic rats, which also did not exhibit statistically significant alterations in birefringence brightness when compared to control animals (P > .05). EDX analysis showed that T1DM induced statistically significant little increases in the amount of calcium and phosphorus in outer mature enamel (P < .01) with preservation of calcium/phosphorus ratio in that structure (P > .05). T1DM also caused important ultrastructural alterations in mature enamel as revealed by SEM and induced a statistically significant reduction of about 13.67% in its microhardness at 80 μm from dentin-enamel junction (P < .01). This study shows that T1DM may disturb enamel development, leading to alterations in mature enamel ultrastructure and in its mechanical features. © 2017 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Wear Potential of Dental Ceramics and its Relationship with Microhardness and Coefficient of Friction.

PubMed

Freddo, Rafael Augusto; Kapczinski, Myriam Pereira; Kinast, Eder Julio; de Souza Junior, Oswaldo Baptista; Rivaldo, Elken Gomes; da Fontoura Frasca, Luis Carlos

2016-10-01

To evaluate, by means of pin-on-disk testing, the wear potential of different dental ceramic systems as it relates to friction parameters, surface finish, and microhardness. Three groups of different ceramic systems (Noritake EX3, Eris, Empress II) with 20 disks each (10 glazed, 10 polished) were used. Vickers microhardness (Hv) was determined with a 200-g load for 30 seconds. Friction coefficients (μ) were determined by pin-on-disk testing (5 N load, 600 seconds, and 120 rpm). Wear patterns were assessed by scanning electron microscopy (SEM). The results were analyzed using one-way ANOVA and Tukey's test, with the significance level set at α = 0.05. The coefficients of friction were as follows: Noritake EX3 0.28 ± 0.12 (polished), 0.33 ± 0.08 (glazed); Empress II 0.38 ± 0.08 (polished), 0.45 ± 0.05 (glazed); Eris 0.49 ± 0.05 (polished), 0.49 ± 0.06 (glazed). Microhardness measurements were as follows: Noritake EX3 530.7 ± 8.7 (polished), 525.9 ± 6.2 (glazed); Empress II 534.1 ± 8 (polished), 534.7 ± 4.5 (glazed); Eris, 511.7 ± 6.5 (polished), 519.5 ± 4.1 (glazed). The polished and glazed Noritake EX3 and polished and glazed Eris specimens showed statistically different friction coefficients. SEM image analysis revealed more surface changes, such as small cracks and grains peeling off, in glazed ceramics. Wear potential may be related to the coefficient of friction in Noritake ceramics, which had a lower coefficient than Eris ceramics. Within-group analysis showed no differences in polished or glazed specimens. The differences observed were not associated with microhardness. © 2015 by the American College of Prosthodontists.

Physicochemical and bioactive properties of innovative resin-based materials containing functional halloysite-nanotubes fillers.

PubMed

Degrazia, Felipe Weidenbach; Leitune, Vicente Castelo Branco; Takimi, Antonio Shigueaki; Collares, Fabrício Mezzomo; Sauro, Salvatore

2016-09-01

This study aimed to assess the degree of conversion, microhardness, solvent degradation, contact angle, surface free energy and bioactivity (e.g., mineral precipitation) of experimental resin-based materials containing, pure or triclosan-encapsulated, aluminosilicate-(halloysite) nanotubes. An experimental resin blend was prepared using bis-GMA/TEGDMA, 75/25wt% (control). Halloysite nanotubes (HNT) doped with or without triclosan (TCN) were first analyzed using transmission electron microscopy (TEM). HNT or HNT/TCN fillers were incorporated into the resin blend at different concentrations (5, 10, and 20wt%). Seven experimental resins were created and the degree of conversion, microhardness, solvent degradation and contact angle were assessed. Bioactive mineral precipitation induced by the experimental resins was evaluated through Raman spectroscopy and SEM-EDX. TEM showed a clear presence of TCN particles inside the tubular lumen and along the outer surfaces of the halloysite nanotubes. The degree of conversion, surface free energy, microhardness, and mineral deposition of polymers increased with higher amount of HNTs. Conversely, the higher the amount (20wt%) of TCN-loaded HNTs the lower the microhardness of the experimental resins. The incorporation of pure or TCN-loaded aluminosilicate-(halloysite) nanotubes into resin-based materials increase the bioactivity of such experimental restorative materials and promotes mineral deposition. Therefore, innovative resin-based materials containing functional halloysite-nanotube fillers may represent a valuable alternative for therapeutic minimally invasive treatments. Copyright © 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

The effects of different types of investments on the alpha-case layer of titanium castings.

PubMed

Guilin, Yu; Nan, Li; Yousheng, Li; Yining, Wang

2007-03-01

Different types of investments affect the formation of the alpha-case (alpha-case) layer on titanium castings. This alpha-case layer may possibly alter the mechanical properties of cast titanium, which may influence the fabrication of removable and fixed prostheses. The formation mechanism for the alpha-case layer is not clear. The aim of this study was to evaluate the effect of 3 types of investments on the microstructure, composition, and microhardness of the alpha-case layer on titanium castings. Fifteen wax columns with a diameter of 5 mm and a length of 40 mm were divided into 3 groups of 5 patterns each. Patterns were invested using 3 types of investment materials, respectively, and were cast in pure titanium. The 3 types of materials tested were SiO(2)-, Al(2)O(3)-, and MgO-based investments. All specimens were sectioned and prepared for metallographic observation. The microstructure and composition of the surface reaction layer of titanium castings were investigated by scanning electron microscopy (SEM) and electron probe microanalysis (EPMA). The surface microhardness (VHN) for all specimens was measured using a hardness testing machine, and a mean value for each group was calculated. The alpha-case layer on titanium castings invested with SiO(2)-, Al(2)O(3)-, and MgO-based investments consisted of 3 layers-namely, the oxide layer, alloy layer, and hardening layer. In this study, the oxide layer and alloy layer were called the reaction layer. The thickness of the reaction layer for titanium castings using SiO(2)-, Al(2)O(3)-, and MgO-based investments was approximately 80 microm, 50 microm, and 14 microm, respectively. The surface microhardness of titanium castings made with SiO(2)-based investments was the highest, and that with MgO-based investments was the lowest. The type of investment affects the microstructure and microhardness of the alpha-case layer of titanium castings. Based on the thickness of the surface reaction layer and the surface microhardness of titanium castings, MgO-based investment materials may be the best choice for casting these materials.

Microstructural Characteristics and Mechanical Properties of an Electron Beam-Welded Ti/Cu/Ni Joint

NASA Astrophysics Data System (ADS)

Zhang, Feng; Wang, Ting; Jiang, Siyuan; Zhang, Binggang; Feng, Jicai

2018-04-01

Electron beam welding experiments of TA15 titanium alloy to GH600 nickel superalloy with and without a copper sheet interlayer were carried out. Surface appearance, microstructure and phase constitution of the joint were examined by optical microscopy, scanning electron microscopy and x-ray diffraction analysis. Mechanical properties of Ti/Ni and Ti/Cu/Ni joint were evaluated based on tensile strength and microhardness tests. The results showed that cracking occurred in Ti/Ni electron beam weldment for the formation of brittle Ni-Ti intermetallics, while a crack-free electron beam-welded Ti/Ni joint can be obtained by using a copper sheet as filler metal. The addition of copper into the weld affected the welding metallurgical process of the electron beam-welded Ti/Ni joint significantly and was helpful for restraining the formation of Ti-Ni intermetallics in Ti/Ni joint. The microstructure of the weld was mainly characterized by a copper-based solid solution and Ti-Cu interfacial intermetallic compounds. Ti-Ni intermetallic compounds were almost entirely suppressed. The hardness of the weld zone was significantly lower than that of Ti/Ni joint, and the tensile strength of the joint can be up to 282 MPa.

Microstructural Characteristics and Mechanical Properties of an Electron Beam-Welded Ti/Cu/Ni Joint

NASA Astrophysics Data System (ADS)

Zhang, Feng; Wang, Ting; Jiang, Siyuan; Zhang, Binggang; Feng, Jicai

2018-05-01

Electron beam welding experiments of TA15 titanium alloy to GH600 nickel superalloy with and without a copper sheet interlayer were carried out. Surface appearance, microstructure and phase constitution of the joint were examined by optical microscopy, scanning electron microscopy and x-ray diffraction analysis. Mechanical properties of Ti/Ni and Ti/Cu/Ni joint were evaluated based on tensile strength and microhardness tests. The results showed that cracking occurred in Ti/Ni electron beam weldment for the formation of brittle Ni-Ti intermetallics, while a crack-free electron beam-welded Ti/Ni joint can be obtained by using a copper sheet as filler metal. The addition of copper into the weld affected the welding metallurgical process of the electron beam-welded Ti/Ni joint significantly and was helpful for restraining the formation of Ti-Ni intermetallics in Ti/Ni joint. The microstructure of the weld was mainly characterized by a copper-based solid solution and Ti-Cu interfacial intermetallic compounds. Ti-Ni intermetallic compounds were almost entirely suppressed. The hardness of the weld zone was significantly lower than that of Ti/Ni joint, and the tensile strength of the joint can be up to 282 MPa.

Microstructural evolution in ultra-low-carbon steel weldments—Part I: Controlled thermal cycling and continuous cooling transformation diagram of the weld metal

NASA Astrophysics Data System (ADS)

Fonda, R. W.; Spanos, G.

2000-09-01

The transformation behavior and microstructural evolution of the as-deposited weld metal from an ultra-low-carbon (ULC) weldment were characterized by dilatometry, optical microscopy, transmission electron microscopy, and microhardness measurements. These results were used to construct a continuous cooling transformation (CCT) diagram for this weld metal. The major microconstituents observed in this ULC weldment were (in order of decreasing cooling rate) coarse autotempered martensite, fine lath martensite, lath ferrite, and degenerate lath ferrite. No polygonal ferrite was observed. These results were also used to develop criteria to differentiate between the two predominant microstructures in these ULC steels, lath martensite, and lath ferrite, which can look quite similar but have very different properties.

Fabrication and characterization of dendrimer-functionalized nano-hydroxyapatite and its application in dentin tubule occlusion.

PubMed

Lin, Xuandong; Xie, Fangfang; Ma, Xueling; Hao, Yuhong; Qin, Hejia; Long, Jindong

2017-06-01

The occlusion of dentinal tubules is an effective method to alleviate the symptoms of dentin hypersensitivity. In this paper, we successfully modified nano-hydroxyapatite (n-HAP) with carboxyl-terminated polyamidoamine dendrimers by an aqueous-based chemical method and verified by fourier transform infrared spectroscopy (FTIR) and transmission electron microscope (TEM). Then the demineralization dentin discs were randomly divided into 4 groups, corresponding to subsequent brushing experiments: deionized water and kept in artificial saliva (AS), dendrimer-functionalized n-HAP and stored in AS, n-HAP and saved in AS, dendrimer-functionalized n-HAP and stored in deionized water. After 7 days of simulated brushing, dentin discs followed the in vitro characterization using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy and microhardness test. These data suggested that dendrimer-functionalized n-HAP could crosslink with collagen fibers and resulted in effective dentinal tubule occlusion. Moreover, the new material can induce the HAP formation with the help of superficial carboxyl and fill the spaces in dentinal tubules furtherly. The microhardness of dendrimer-functionalized n-HAP-treated specimens was significantly higher than others. In summary, dendrimer-functionalized n-HAP can be a new therapeutic material for the treatment of dentin hypersensitivity.

Investigation of the Microstructural, Mechanical and Corrosion Properties of Grade A Ship Steel-Duplex Stainless Steel Composites Produced via Explosive Welding

NASA Astrophysics Data System (ADS)

Kaya, Yakup; Kahraman, Nizamettin; Durgutlu, Ahmet; Gülenç, Behçet

2017-08-01

Grade A ship-building steel-AISI 2304 duplex stainless steel composite plates were manufactured via explosive welding. The AISI 2304 plates were used to clad the Grade A plates. Optical microscopy studies were conducted on the joining interface for characterization of the manufactured composite plates. Notch impact, tensile-shear, microhardness, bending and twisting tests were carried out to determine the mechanical properties of the composites. In addition, the surfaces of fractured samples were examined by scanning electron microscopy (SEM), and neutral salt spray (NSS) and potentiodynamic polarization tests were performed to examine corrosion behavior. Near the explosion zone, the interface was completely flat, but became wavy as the distance from the explosion zone increased. The notch impact tests indicated that the impact strength of the composites decreased with increasing distance from the explosion zone. The SEM studies detected brittle behavior below the impact transition temperature and ductile behavior above this temperature. Microhardness tests revealed that the hardness values increased with increasing distance from the explosion zone and mechanical tests showed that no visible cracking or separation had occurred on the joining interface. The NSS and potentiodynamic polarization tests determined that the AISI 2304 exhibited higher corrosion resistance than the Grade A steel.

Microstructure characteristics of Ni/WC composite cladding coatings

NASA Astrophysics Data System (ADS)

Yang, Gui-rong; Huang, Chao-peng; Song, Wen-ming; Li, Jian; Lu, Jin-jun; Ma, Ying; Hao, Yuan

2016-02-01

A multilayer tungsten carbide particle (WCp)-reinforced Ni-based alloy coating was fabricated on a steel substrate using vacuum cladding technology. The morphology, microstructure, and formation mechanism of the coating were studied and discussed in different zones. The microstructure morphology and phase composition were investigated by scanning electron microscopy, optical microscopy, X-ray diffraction, and energy-dispersive X-ray spectroscopy. In the results, the coating presents a dense and homogeneous microstructure with few pores and is free from cracks. The whole coating shows a multilayer structure, including composite, transition, fusion, and diffusion-affected layers. Metallurgical bonding was achieved between the coating and substrate because of the formation of the fusion and diffusion-affected layers. The Ni-based alloy is mainly composed of γ-Ni solid solution with finely dispersed Cr7C3/Cr23C6, CrB, and Ni+Ni3Si. WC particles in the composite layer distribute evenly in areas among initial Ni-based alloying particles, forming a special three-dimensional reticular microstructure. The macrohardness of the coating is HRC 55, which is remarkably improved compared to that of the substrate. The microhardness increases gradually from the substrate to the composite zone, whereas the microhardness remains almost unchanged in the transition and composite zones.

Effect of bond coat and preheat on the microstructure, hardness, and porosity of flame sprayed tungsten carbide coatings

NASA Astrophysics Data System (ADS)

Winarto, Winarto; Sofyan, Nofrijon; Rooscote, Didi

2017-06-01

Thermally sprayed coatings are used to improve the surface properties of tool steel materials. Bond coatings are commonly used as intermediate layers deposited on steel substrates (i.e. H13 tool steel) before the top coat is applied in order to enhance a number of critical performance criteria including adhesion of a barrier coating, limiting atomic migration of the base metal, and corrosion resistance. This paper presents the experimental results regarding the effect of nickel bond coat and preheats temperatures (i.e. 200°C, 300°C and 400°C) on microstructure, hardness, and porosity of tungsten carbide coatings sprayed by flame thermal coating. Micro-hardness, porosity and microstructure of tungsten carbide coatings are evaluated by using micro-hardness testing, optical microscopy, scanning electron microscopy, and X-ray diffraction. The results show that nickel bond coatings reduce the susceptibility of micro crack formation at the bonding area interfaces. The percentage of porosity level on the tungsten carbide coatings with nickel bond coat decreases from 5.36 % to 2.78% with the increase of preheat temperature of the steel substrate of H13 from 200°C to 400°C. The optimum hardness of tungsten carbide coatings is 1717 HVN in average resulted from the preheat temperature of 300°C.

Morphology and Performance of 5Cr5MoV Casting Die Steel in the Process of Surfacing

NASA Astrophysics Data System (ADS)

Song, Yulai; Kong, Xiangrui; Yang, Pengcong; Fu, Hongde; Wang, Xuezhu

2017-12-01

To investigate the microstructures and mechanical properties of the deposited metal on surface of die steel, two layer of weld-seam were prepared on the surface of 5Cr5MoV die steel by arc surfacing. The surface microstructures and microhardness were characterized by scanning electron microscopy, energy dispersive spectrometer and Vickers microhardness tester, respectively. The effect of load on the abrasion resistance and wear mechanism of the base metal and surfacing metal was studied by pin-on-disk tribometer. The results showed that martensite and retained austenite exist in weld-seam, both of them grow up in the form of dendrites and equiaxed grains and microhardness reach 774.2HV. The microstructures of the quenching zone mainly consist of martensite and retained austenite, while tempered martensite is the dominant phase in partial quenching zone. The abrasion resistance of the surfacing metal is superior to the base metal based on the results of wear test. The wear rates of surfacing metal and base metal raise with the increase of load. The wear rates of base metal raise extremely when the load reach 210N. Both of two kinds of materials have the similar wear mechanism, namely, abrasive wear at low load, oxidative wear and adhesive wear at high load.

Effect of Dopants and Sintering Method on the Properties of Ceria-Based Electrolytes for IT-SOFCs Applications

NASA Astrophysics Data System (ADS)

Sharma, Payal; Sharma, Chetan; Singh, Kanchan L.; Singh, Anirudh P.

2018-05-01

Doped and co-doped ceria ceramics are used as electrolyte materials in solid oxide fuel cells. In this work, ceria-based oxides, Ce0.90Gd0.06Y0.02M0.02O2-δ (M = Ca, Fe, La, and Sr) were prepared by conventional as well as microwave processing from the precursors prepared by the mixed oxide method. The consolidated calcined powders in pellet form were sintered in microwave energy at 1400°C for 20 min and in an electric furnace of IR radiation at 1400°C for 6 h. The x-ray diffraction analysis confirmed that all the compositions were crystallized into a cubic fluorite structure. Surface morphology of the sintered products was studied using scanning electron microscopy and the microhardness was investigated using the Vickers hardness test. The comparative results analysis shows that the microwave-sintered samples have uniform grain growth, higher density and higher microhardness than the corresponding conventionally sintered products. The microwave-sintered sample of composition Ce0.90Gd0.06Y0.02Sr0.02O2-δ was found to have the highest microhardness among the four compositions due to its high density and smallest grain size.

A Comparative Study on the Effect of MWCNT as Reinforcement on the Corrosion Parameters of Different Ni-W/MWCNTs Nanocomposite Coatings in Various Corrosive Media

NASA Astrophysics Data System (ADS)

Mohammadpour, Zahra; Zare, Hamid R.

2018-07-01

Nickel-tungsten multi-walled carbon nanotubes (Ni-W/MWCNTs) nanocomposite coatings were co-electrodeposited in the ammonium-free bath by means of constant direct current coulometry. The results indicate that the amount of MWCNTs incorporated into the nanocomposite coatings has a key role in the improvement of their microhardness and corrosion resistance. The corrosion behavior of the coatings was evaluated using potentiodynamic polarization and electrochemical impedance spectroscopy methods in three corrosive media of 3.5 wt% NaCl, 1.0 M NaOH, and 0.5 M H2SO4. The experimental data of the corrosion current density (jcorr), corrosion rate (CR), the polarization resistance (Rp), and microhardness indicate that the presence of MWCNTs in coatings improves the quality of those coatings. The surface morphology of the coatings and the elemental analysis data were obtained by scanning electron microscopy and energy dispersive X-ray microanalysis respectively. As the results showed, the coatings were uniform and crack-free in the presence of 5.3 wt% carbon. Also, a microhardness test revealed that the nanocomposite coating containing 5.3 wt% carbon obtained in an ammonium-free bath which provided the higher content of tungsten had the highest hardness value among others.

A Comparative Study on the Effect of MWCNT as Reinforcement on the Corrosion Parameters of Different Ni-W/MWCNTs Nanocomposite Coatings in Various Corrosive Media

NASA Astrophysics Data System (ADS)

Mohammadpour, Zahra; Zare, Hamid R.

2018-03-01

Nickel-tungsten multi-walled carbon nanotubes (Ni-W/MWCNTs) nanocomposite coatings were co-electrodeposited in the ammonium-free bath by means of constant direct current coulometry. The results indicate that the amount of MWCNTs incorporated into the nanocomposite coatings has a key role in the improvement of their microhardness and corrosion resistance. The corrosion behavior of the coatings was evaluated using potentiodynamic polarization and electrochemical impedance spectroscopy methods in three corrosive media of 3.5 wt% NaCl, 1.0 M NaOH, and 0.5 M H2SO4. The experimental data of the corrosion current density (jcorr), corrosion rate (CR), the polarization resistance (Rp), and microhardness indicate that the presence of MWCNTs in coatings improves the quality of those coatings. The surface morphology of the coatings and the elemental analysis data were obtained by scanning electron microscopy and energy dispersive X-ray microanalysis respectively. As the results showed, the coatings were uniform and crack-free in the presence of 5.3 wt% carbon. Also, a microhardness test revealed that the nanocomposite coating containing 5.3 wt% carbon obtained in an ammonium-free bath which provided the higher content of tungsten had the highest hardness value among others.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Samavatian, Majid, E-mail: m.samavatian@srbiau.ac.ir; Halvaee, Ayoub; Amadeh, Ahmad Ali

Joining mechanism of Ti/Al dissimilar alloys was studied during liquid state diffusion bonding process using Cu/Sn/Cu interlayer at 510 °C under vacuum of 7.5 × 10{sup −5} Torr for various bonding times. The microstructure and compositional changes in the joint zone were analyzed by scanning electron microscopy equipped with energy dispersive spectroscopy and X-ray diffraction. Microhardness and shear strength tests were also applied to study the mechanical properties of the joints. It was found that with an increase in bonding time, the elements of interlayer diffused into the parent metals and formed various intermetallic compounds at the interface. Diffusion processmore » led to the isothermal solidification and the bonding evolution in the joint zone. The results from mechanical tests showed that microhardness and shear strength values have a straight relation with bonding time so that the maximum shear strength of joint was obtained for a bond made with 60 min bonding time. - Highlights: • Liquid state diffusion bonding of Al2024 to Ti–6Al–4V was performed successfully. • Diffusion of the elements caused the formation of various intermetallics at the interface. • Microhardness and shear strength values have a straight relation with bonding time. • The maximum shear strength reached to 36 MPa in 60 min bonding time.« less

Effect of Co doping on structural and mechanical properties of CeO2

NASA Astrophysics Data System (ADS)

Tiwari, Saurabh; Balasubramanian, Nivedha; Biring, Sajal; Sen, Somaditya

2018-05-01

Sol-gel synthesized nanocrystalline Co doped CeO2 powders [(Ce1-xCoxO2; x=0, 0.03)] were made into cylindrical discs by uniaxial pressing and sintered at 1500°C for 24h to measure mechanical properties. The pure phase formation of undoped and Co doped samples were confirmed by X-ray diffraction and Raman analysis. The scanning electron microscopy (SEM) was used for observing the microstructure of sintered samples to investigate density, porosity, and grain size. The grains size observed for 1500°C sintered samples 5-8 µm. Vickers indentation method used for investigating the micro-hardness. For undoped CeO2 micro-hardness was found 6.2 GPa which decreased with Co doping. It was found that samples follow indentation size effect (ISE) and follow elastic than plastic deformation. Enhanced ductile nature with Co doping in CeO2 made it more promising material for optoelectronic device applications.

Mechanical properties and microstructural change of W–Y2O3 alloy under helium irradiation

PubMed Central

Tan, Xiaoyue; Luo, Laima; Chen, Hongyu; Zhu, Xiaoyong; Zan, Xiang; Luo, Guangnan; Chen, Junling; Li, Ping; Cheng, Jigui; Liu, Dongping; Wu, Yucheng

2015-01-01

A wet-chemical method combined with spark plasma sintering was used to prepare a W–Y2O3 alloy. High-temperature tensile tests and nano-indentation microhardness tests were used to characterize the mechanical properties of the alloy. After He-ion irradiation, fuzz and He bubbles were observed on the irradiated surface. The irradiation embrittlement was reflected by the crack indentations formed during the microhardness tests. A phase transformation from α-W to γ-W was investigated by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Polycrystallization and amorphization were also observed in the irradiation damage layer. The W materials tended to exhibit lattice distortion, amorphization, polycrystallization and phase transformation under He-ion irradiation. The transformation mechanism predicted by the atomic lattice model was consistent with the available experimental observations. These findings clarify the mechanism of the structural transition of W under ion irradiation and provide a clue for identifying materials with greater irradiation resistance. PMID:26227480

Quality Improvement of Chrome-Diamond Coatings on Flowing Chrome Plating

NASA Astrophysics Data System (ADS)

Belyaev, V. N.; Koslyuk, A. Yu; Lobunets, A. V.; Andreyev, A. S.

2016-04-01

The research results of the process of flowing chrome plating of internal surfaces of long-length cylindrical articles with the usage of electrolyte with ultra-dispersed diamonds when continuous article rotation, while chromium-plating, are presented. During experiments the following varying technological parameters: electrolyte temperature and article frequency rotation were chosen, and experimental samples were obtained. Estimation of porosity, micro-hardness, thickness of chrome coatings and uniformity were performed as well as the precipitation structure by the method of scanning electron microscopy. The results showed that the use of ultra-dispersed diamonds and realization of the scheme with rotation of detail-cathode when flowing chromium-plating allows one to increase servicing characteristics of the coating due to the decrease of grains size of chrome coating and porosity, and due to the increase of micro-hardness, so confirming the efficiency of using the suggested scheme of coating application and the given type of ultra-dispersed fillers when chromium-plating.

Efficacy of cold light bleaching using different bleaching times and their effects on human enamel.

PubMed

Wang, Wei; Zhu, Yuhe; Li, Jiajia; Liao, Susan; Ai, Hongjun

2013-01-01

This study investigated the efficacy of cold light bleaching using different bleaching times and the effects thereof on tooth enamel. Before and after bleaching, stained tooth specimens were subjected to visual and instrumental colorimetric assessments using Vita Shade Guide and spectrophotometric shade matching. Enamel surface alterations were examined using scanning electron microscopy (SEM) to analyze surface morphology, surface microhardness (SMH) measurement to determine changes in mechanical properties, and X-ray diffraction (XRD) to characterize post-bleaching enamel composition. Cold light bleaching successfully improved tooth color, with optimal efficacy when bleaching time was beyond 10 min. Significant differences in surface morphology were observed among the different bleaching times, but no significant differences were observed for enamel composition and surface microhardness among the different bleaching times. Results of this study revealed an association between the bleaching time of cold light bleaching and its whitening efficacy. Together with the results on enamel surface changes, this study provided positive evidence to support cold light bleaching as an in-office bleaching treatment.

In situ formation of titanium carbide using titanium and carbon-nanotube powders by laser cladding

NASA Astrophysics Data System (ADS)

Savalani, M. M.; Ng, C. C.; Li, Q. H.; Man, H. C.

2012-01-01

Titanium metal matrix composite coatings are considered to be important candidates for high wear resistance applications. In this study, TiC reinforced Ti matrix composite layers were fabricated by laser cladding with 5, 10, 15 and 20 wt% carbon-nanotube. The effects of the carbon-nanotube content on phase composition, microstructure, micro-hardness and dry sliding wear resistance of the coating were studied. Microstructural observation using scanning electron microscopy showed that the coatings consisted of a matrix of alpha-titanium phases and the reinforcement phase of titanium carbide in the form of fine dendrites, indicating that titanium carbide was synthesized by the in situ reaction during laser irradiation. Additionally, measurements on the micro-hardness and dry sliding wear resistance of the coatings indicated that the mechanical properties were affected by the amount of carbon-nanotube in the starting precursor materials and were enhanced by increasing the carbon-nanotube content. Results indicated that the composite layers exhibit high hardness and excellent wear resistance.

Dilution effect on the formation of amorphous phase in the laser cladded Ni-Fe-B-Si-Nb coatings after laser remelting process

NASA Astrophysics Data System (ADS)

Li, Ruifeng; Li, Zhuguo; Huang, Jian; Zhu, Yanyan

2012-08-01

Ni-Fe-B-Si-Nb coatings have been deposited on mild steel substrates using high power diode laser cladding. Scanning laser beam at high speeds was followed to remelt the surface of the coatings. Different laser cladding powers in the range of 700-1000 W were used to obtain various dilution ratios in the coating. The dilution effect on the chemical characterization, phase composition and microstructure is analyzed by energy dispersive spectroscopy, X-ray diffraction and scanning-electron microscopy. The microhardness distribution of the coatings after laser processing is also measured. The results reveal that Ni-based amorphous composite coatings have successfully been fabricated on mild steel substrate at low dilution ratio when the cladding power was 700 W, 800 W and 900 W. While at high laser power of 1000 W, no amorphous phase was found. The coatings with low dilution ratio exhibit the highest microhardness of 1200 HV0.5 due to their largest volume fraction of amorphous phase.

Validity of "sputtering and re-condensation" model in active screen cage plasma nitriding process

NASA Astrophysics Data System (ADS)

Saeed, A.; Khan, A. W.; Jan, F.; Abrar, M.; Khalid, M.; Zakaullah, M.

2013-05-01

The validity of "sputtering and re-condensation" model in active screen plasma nitriding for nitrogen mass transfer mechanism is investigated. The dominant species including NH, Fe-I, N2+, N-I and N2 along with Hα and Hβ lines are observed in the optical emission spectroscopy (OES) analysis. Active screen cage and dc plasma nitriding of AISI 316 stainless steel as function of treatment time is also investigated. The structure and phases composition of the nitrided layer is studied by X-ray diffraction (XRD). Surface morphology is studied by scanning electron microscopy (SEM) and hardness profile is obtained by Vicker's microhardness tester. Increasing trend in microhardness is observed in both cases but the increase in active screen plasma nitriding is about 3 times greater than that achieved by dc plasma nitriding. On the basis of metallurgical and OES observations the use of "sputtering and re-condensation" model in active screen plasma nitriding is tested.

Metallurgical characterization of M-Wire nickel-titanium shape memory alloy used for endodontic rotary instruments during low-cycle fatigue.

PubMed

Ye, Jia; Gao, Yong

2012-01-01

Rotary instruments made of a new nickel-titanium (NiTi) alloy (M-Wire) have shown improved cyclic fatigue resistance and mechanical properties compared with those made of conventional superelastic NiTi wires. The objective of this study was to characterize microstructural changes of M-Wire throughout the cyclic fatigue process under controlled strain amplitude. The average fatigue life was calculated from 30 M-Wire samples that were subjected to a strain-controlled (≈ 4%) rotating bend fatigue test at room temperature and rotational speed of 300 rpm. Microstructural evolution of M-Wire has been investigated by different metallurgical characterization techniques, including differential scanning calorimetry, Vickers microhardness, and transmission electron microscopy at 4 different stages (as-received state, 30%, 60%, and 90% of average fatigue life). During rotating bend fatigue test, no statistically significant difference (P > .05) was found on austenite finish temperatures between as-received M-Wire and fatigued samples. However, significant differences (P < .05) were observed on Vickers microhardness for samples with 60% and 90% fatigue life compared with as-received and 30% fatigue life. Coincidentally, substantial growth of martensite grains and martensite twins was observed in microstructure under transmission electron microscopy after 60% fatigue life. The results of the present study suggested that endodontic instruments manufactured with M-Wire are expected to have higher strength and wear resistance than similar instruments made of conventional superelastic NiTi wires because of its unique nano-crystalline martensitic microstructure. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Microstructure and properties of ultrafine grain nickel 200 after hydrostatic extrusion processes

NASA Astrophysics Data System (ADS)

Sitek, R.; Krajewski, C.; Kamiński, J.; Spychalski, M.; Garbacz, H.; Pachla, W.; Kurzydłowski, K. J.

2012-09-01

This paper presents the results of the studies of the structure and properties of ultrafine grained nickel 200 obtained by hydrostatic extrusion processes. Microstructure was characterized by means of optical microscopy and electron transmission microscopy. Corrosion resistance was studied by impedance and potentiodynamic methods using an AutoLab PGSTAT 100 potentiostat in 0.1 M Na2SO4 solution and in acidified (by addition of H2SO4) 0.1 M NaCl solution at pH = 4.2 at room temperature. Microhardness tests were also performed. The results showed that hydrostatic extrusion produces a heterogeneous, ultrafine-grained microstructure in nickel 200. The corrosive resistance tests showed that the grain refinement by hydrostatic extrusion is accompanied by a decreased corrosive resistance of nickel 200.

Characteristics of AZ31 Mg alloy joint using automatic TIG welding

NASA Astrophysics Data System (ADS)

Liu, Hong-tao; Zhou, Ji-xue; Zhao, Dong-qing; Liu, Yun-teng; Wu, Jian-hua; Yang, Yuan-sheng; Ma, Bai-chang; Zhuang, Hai-hua

2017-01-01

The automatic tungsten-inert gas welding (ATIGW) of AZ31 Mg alloys was performed using a six-axis robot. The evolution of the microstructure and texture of the AZ31 auto-welded joints was studied by optical microscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and electron backscatter diffraction. The ATIGW process resulted in coarse recrystallized grains in the heat affected zone (HAZ) and epitaxial growth of columnar grains in the fusion zone (FZ). Substantial changes of texture between the base material (BM) and the FZ were detected. The {0002} basal plane in the BM was largely parallel to the sheet rolling plane, whereas the c-axis of the crystal lattice in the FZ inclined approximately 25° with respect to the welding direction. The maximum pole density increased from 9.45 in the BM to 12.9 in the FZ. The microhardness distribution, tensile properties, and fracture features of the AZ31 auto-welded joints were also investigated.

Yttria catalyzed microstructural modifications in oxide dispersion strengthened V-4Cr-4Ti alloys synthesized by field assisted sintering technique

NASA Astrophysics Data System (ADS)

Krishnan, Vinoadh Kumar; Sinnaeruvadi, Kumaran; Verma, Shailendra Kumar; Dash, Biswaranjan; Agrawal, Priyanka; Subramanian, Karthikeyan

2017-08-01

The present work deals with synthesis, characterisation and elevated temperature mechanical property evaluation of V-4Cr-4Ti and oxide (yttria = 0.3, 0.6 and 0.9 at%) dispersion strengthened V-4Cr-4Ti alloy processed by mechanical alloying and field-assisted sintering, under optimal conditions. Microstructural parameters of both powder and sintered samples were deduced by X-ray diffraction (XRD) and further confirmed with high resolution transmission electron microscopy. Powder diffraction and electron microscopy study show that ball milling of starting elemental powders (V-4Cr-4Ti) with and without yttria addition has resulted in single phase α-V (V-4Cr-4Ti) alloy. Wherein, XRD and electron microscopy images of sintered samples have revealed phase separation (viz., Cr-V and Ti-V) and domain size reduction, with yttria addition. The reasons behind phase separation and domain size reduction with yttria addition during sintering are extensively discussed. Microhardness and high temperature compression tests were done on sintered samples. Yttria addition (0.3 and 0.6 at.%) increases the elevated temperature compressive strength and strain hardening exponent of α-V alloys. High temperature compression test of 0.9 at% yttria dispersed α-V alloy reveals a glassy behaviour.

Bonding and Integration of C-C Composite to Cu-Clad-Molybdenum for Thermal Management Applications

NASA Technical Reports Server (NTRS)

Asthana, R.; Singh, M.; Shpargel, T.P.

2008-01-01

Two- and three-dimensional carbon-carbon composites with either resin-derived matrix or CVI matrix were joined to Cu-clad-Mo using active Ag-Cu braze alloys for thermal management applications. The joint microstructure and composition were examined using Field-Emission Scanning Electron Microscopy and Energy-Dispersive Spectroscopy, and the joint hardness was characterized using the Knoop microhardness testing. Observations on the infiltration of the composite with molten braze, dissolution of metal substrate, and solute segregation at the C-C surface have been discussed. The thermal response of the integrated assembly is also briefly discussed.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klimenov, V. A., E-mail: klimenov@tpu.ru; National Research Tomsk Polytechnic University, 30 Lenin Av., Tomsk, 634050; Kurgan, K. A., E-mail: kirill-k2.777@mail.ru

The structure of weld joints of the titanium alloy Ti-6Al-4V in the initial ultrafine-grained state, obtained by resistance spot welding, is studied using the optical and scanning electron microscopy method and the X-ray structure analysis. The carried out studies show the relationship of the metal structure in the weld zone with main joint zones. The structure in the core zone and the heat affected zone is represented by finely dispersed grains of needle-shaped martensite, differently oriented in these zones. The change in the microhardness in the longitudinal section of the weld joint clearly correlates with structural changes during welding.

Effects of the Tempering and High-Pressure Torsion Temperatures on Microstructure of Ferritic/Martensitic Steel Grade 91

PubMed Central

Ganeev, Artur; Nikitina, Marina; Sitdikov, Vil; Islamgaliev, Rinat; Hoffman, Andrew; Wen, Haiming

2018-01-01

Grade 91 (9Cr-1Mo) steel was subjected to various heat treatments and then to high-pressure torsion (HPT) at different temperatures. Its microstructure was studied using transmission electron microscopy (TEM) and X-ray diffraction (XRD). Effects of the tempering temperature and the HPT temperature on the microstructural features and microhardness in the ultrafine-grained (UFG) Grade 91 steel were researched. The study of the UFG structure formation takes into account two different microstructures observed: before HPT in both samples containing martensite and in fully ferritic samples. PMID:29671761

The influence of severe plastic deformation by high pressure torsion on structure and mechanical properties of Hadfield steel single crystals

NASA Astrophysics Data System (ADS)

Zakharova, G. G.; Astafurova, E. G.

2010-07-01

Hadfield steel single crystals have been deformed by high pressure torsion at room temperature (P=5GPa) for 1, 2, 3 revolutions. The resulting microstructure has been studied by means of transmission electron microscopy (TEM) and X-ray analysis. The size of fragments decreases with increasing number of revolutions due to interaction of slip dislocations, microbands and thin twins. As a result of severe plastic deformation, the microhardness of the Hadfield steel has been increased, and a portion of epsilon, α' martensite has been found.

Effect of ion-beam treatment on structure and fracture resistance of 12Cr1MoV steel under static, cyclic and dynamic loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Panin, S. V., E-mail: svp@ispms.tsc.ru; Vlasov, I. V., E-mail: good0@yandex.ru; Sergeev, V. P., E-mail: retc@ispms.tsc.ru

2015-10-27

Features of the structure and properties modification of 12Cr1MoV steel subjected to irradiation by zirconium ion beam have been investigated with the use of optical and electron microscopy as well as microhardness measurement. It has been shown that upon treatment the structure modification occurred across the entire cross-section of specimens with the thickness of 1 mm. Changes in the mechanical properties of these specimens under static, cyclic and impact loading are interpreted in terms of identified structure changes.

Characteristics of combustion flame sprayed nickel aluminum using a Coanda Assisted Spray Manipulation collar for off-normal deposits

NASA Astrophysics Data System (ADS)

Archibald, Reid S.

A novel flame spray collar called the Coanda Assisted Spray Manipulation collar (CSM) has been tested for use on the Sulzer Metco 5P II combustion flame spray gun. A comparison study of the stock nozzle and the CSM has been performed by evaluating the porosity, surface roughness, microhardness, tensile strength and microscopy of normal and off-normal sprayed NiAl deposits. The use of the CSM collar resulted in the need to position the sprayed coupons closer to the gun, which in turn affected the particle impact energy and particle temperatures of the NiAl powder. For the CSM, porosities had a larger scatterband, surface roughness was comparably the same, microhardness was lower, and tensile strength was higher. The microscopy analysis revealed a greater presence of unmelted particles and steeper intersplat boundaries for the CSM. For both processes, the porosity and surface roughness increased and the microhardness decreased as the spray angle decreased.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pariona, Moises Meza, E-mail: mmpariona@uepg.br; Teleginski, Viviane; Santos, Kelly dos

Laser beam welding has recently been incorporated into the fabrication process of aircraft and automobile structures. Surface roughness is an important parameter of product quality that strongly affects the performance of mechanical parts, as well as production costs. This parameter influences the mechanical properties such as fatigue behavior, corrosion resistance, creep life, etc., and other functional characteristics such as friction, wear, light reflection, heat transmission, lubrification, electrical conductivity, etc. The effects of laser surface remelting (LSR) on the morphology of Al-Fe aerospace alloys were examined before and after surface treatments, using optical microscopy (OM), scanning electron microscopy (SEM), low-angle X-raymore » diffraction (LA-XRD), atomic force microscopy (AFM), microhardness measurements (Vickers hardness), and cyclic voltammetry. This analysis was performed on both laser-treated and untreated sanded surfaces, revealing significant differences. The LA-XRD analysis revealed the presence of alumina, simple metals and metastable intermetallic phases, which considerably improved the microhardness of laser-remelted surfaces. The morphology produced by laser surface remelting enhanced the microstructure of the Al-Fe alloys by reducing their roughness and increasing their hardness. The treated surfaces showed passivity and stability characteristics in the electrolytic medium employed in this study. - Highlights: Black-Right-Pointing-Pointer The samples laser-treated and untreated showed significant differences. Black-Right-Pointing-Pointer The La-XRD revealed the presence of alumina in Al-1.5 wt.% Fe. Black-Right-Pointing-Pointer The laser-treated reducing the roughness and increasing the hardness. Black-Right-Pointing-Pointer The laser-treated surfaces showed characteristic passive in the electrolytic medium. Black-Right-Pointing-Pointer The laser-treated is a promising technique for applications technological.« less

Effect of CO2 Laser and Fluoride Varnish Application on Microhardness of Enamel Surface Around Orthodontic Brackets

PubMed Central

Mahmoudzadeh, Majid; Rezaei-Soufi, Loghman; Farhadian, Nasrin; Jamalian, Seyed Farzad; Akbarzadeh, Mahdi; Momeni, Mohammadali; Basamtabar, Masome

2018-01-01

Introduction: Orthodontic treatment has many advantages such as esthetic improvement and self-esteem enhancement; yet it has some disadvantages such as increasing the risk of formation of white spot lesions, because it makes oral hygiene more difficult. It is rational to implement procedures to prevent these lesions. The present study was aimed to assess the effect of CO2 laser and fluoride varnish on the surface of the enamel surface microhardness around the orthodontic braces. Methods: Eighty extracted premolar teeth were selected, scaled, polished with nonfluoridated pumic and metal brackets were bonded to them. Then, they were randomly allocated to 5 groups: control (neither fluoride nor laser is used on enamel surfaces), fluoride (4 minutes fluoride varnish treatment of the enamel surfaces), CO2 laser (10.6 µm CO2 laser irradiation of the teeth), laserfluoride (fluoride application after laser irradiation) and fluoride-laser (fluoride was applied and then teeth were irradiated with laser). After surface treatment around brackets on enamel, the samples were stored in 0.1% thymol for less than 5 days and then they were exposed to a 10-day microbiological caries model. Microhardness values of enamel were evaluated with Vickers test. One sample of each group (5 teeth from 80 samples) was prepared for SEM (scanning electron microscopy) and the data from 75 remaining teeth were analyzed with analysis of variance (ANOVA) and chi-square tests (α =0.05). Results: Microhardness mean values from high to low were as follow: fluoride-laser, laser-fluoride, laser, fluoride and control. Microhardness in fluoride-laser group was significantly higher compared with that of the control group. Distribution adhesive remnant index (ARI) scores were significantly different between groups and most of bond failures occurred at the enamel-adhesive interface in groups 2 to 5 and at the adhesive-bracket interface in the control group. Conclusion: Combination of fluoride varnish and CO2 laser irradiation can reduce enamel demineralization around orthodontic brackets. PMID:29399311

Effect of CO2 Laser and Fluoride Varnish Application on Microhardness of Enamel Surface Around Orthodontic Brackets.

PubMed

Mahmoudzadeh, Majid; Rezaei-Soufi, Loghman; Farhadian, Nasrin; Jamalian, Seyed Farzad; Akbarzadeh, Mahdi; Momeni, Mohammadali; Basamtabar, Masome

2018-01-01

Introduction: Orthodontic treatment has many advantages such as esthetic improvement and self-esteem enhancement; yet it has some disadvantages such as increasing the risk of formation of white spot lesions, because it makes oral hygiene more difficult. It is rational to implement procedures to prevent these lesions. The present study was aimed to assess the effect of CO 2 laser and fluoride varnish on the surface of the enamel surface microhardness around the orthodontic braces. Methods: Eighty extracted premolar teeth were selected, scaled, polished with nonfluoridated pumic and metal brackets were bonded to them. Then, they were randomly allocated to 5 groups: control (neither fluoride nor laser is used on enamel surfaces), fluoride (4 minutes fluoride varnish treatment of the enamel surfaces), CO 2 laser (10.6 µm CO 2 laser irradiation of the teeth), laserfluoride (fluoride application after laser irradiation) and fluoride-laser (fluoride was applied and then teeth were irradiated with laser). After surface treatment around brackets on enamel, the samples were stored in 0.1% thymol for less than 5 days and then they were exposed to a 10-day microbiological caries model. Microhardness values of enamel were evaluated with Vickers test. One sample of each group (5 teeth from 80 samples) was prepared for SEM (scanning electron microscopy) and the data from 75 remaining teeth were analyzed with analysis of variance (ANOVA) and chi-square tests (α =0.05). Results: Microhardness mean values from high to low were as follow: fluoride-laser, laser-fluoride, laser, fluoride and control. Microhardness in fluoride-laser group was significantly higher compared with that of the control group. Distribution adhesive remnant index (ARI) scores were significantly different between groups and most of bond failures occurred at the enamel-adhesive interface in groups 2 to 5 and at the adhesive-bracket interface in the control group. Conclusion: Combination of fluoride varnish and CO2 laser irradiation can reduce enamel demineralization around orthodontic brackets.

Degradation Potential of Bulk Versus Incrementally Applied and Indirect Composites: Color, Microhardness, and Surface Deterioration.

PubMed

El Gezawi, M; Kaisarly, D; Al-Saleh, H; ArRejaie, A; Al-Harbi, F; Kunzelmann, K H

This study investigated the color stability and microhardness of five composites exposed to four beverages with different pH values. Composite discs were produced (n=10); Filtek Z250 (3M ESPE) and Filtek P90 (3M ESPE) were applied in two layers (2 mm, 20 seconds), and Tetric N-Ceram Bulk Fill (TetricBF, Ivoclar Vivadent) and SonicFill (Kerr) were applied in bulk (4 mm) and then light cured (40 seconds, Ortholux-LED, 1600 mW/cm 2 ). Indirect composite Sinfony (3M ESPE) was applied in two layers (2 mm) and cured (Visio system, 3M ESPE). The specimens were polished and tested for color stability; ΔE was calculated using spectrophotometer readings. Vickers microhardness (50 g, dwell time=45 seconds) was assessed on the top and bottom surfaces at baseline, 40 days of storage, subsequent repolishing, and 60 days of immersion in distilled water (pH=7.0), Coca-Cola (pH=2.3), orange juice (pH=3.75), or anise (pH=8.5) using scanning electron microscopy (SEM). The materials had similar ΔE values (40 days, p>0.05), but TetricBF had a significantly greater ΔE than P90 or SF (40 days). The ΔE was less for P90 and TetricBF than for Z250, SonicFill, and Sinfony (60 days). Repolishing and further immersion significantly affected the ΔE (p<0.05) except for P90. All composites had significantly different top vs bottom baseline microhardnesses. This was insignificant for the Z250/water, P90/orange juice (40 days), and Sinfony groups (40 and 60 days). Immersion produced variable time-dependent deterioration of microhardness in all groups. Multivariate repeated measures analysis of variance with post hoc Bonferroni tests were used to compare the results. ΔE and microhardness changes were significantly inversely correlated at 40 days, but this relationship was insignificant at 60 days (Pearson test). SEM showed degradation (40 days) that worsened (60 days). Bulk-fill composites differ regarding color-stability and top-to-bottom microhardness changes compared with those of other composites. P90 showed better surface degradation resistance. In conclusion, bulk-fill composites are not promising alternatives to incremental and indirect composites regarding biodegradation.

Effects of single pulse energy on the properties of ceramic coating prepared by micro-arc oxidation on Ti alloy

NASA Astrophysics Data System (ADS)

Wang, Jun-Hua; Wang, Jin; Lu, Yan; Du, Mao-Hua; Han, Fu-Zhu

2015-01-01

The effects of single pulse energy on the properties of ceramic coating fabricated on a Ti-6Al-4V alloy via micro-arc oxidation (MAO) in aqueous solutions containing aluminate, phosphate, and some additives are investigated. The thickness, micro-hardness, surface and cross-sectional morphology, surface roughness, and compositions of the ceramic coating are studied using eddy current thickness meter, micro-hardness tester, JB-4C Precision Surface roughness meter, scanning electron microscopy (SEM) and X-ray diffraction (XRD). Single pulse energy remarkably influences the ceramic coating properties. The accumulative time of impulse width is an important parameter in the scientific and rational measurement of the film forming law of ceramic coating. The ceramic coating thickness approximately linearly increases with the cumulative time of impulse width. Larger impulse width resulted in higher single pulse energy, film forming rates and thicker ceramic coating thickness. The sizes of oxide particles, micro-pores and micro-cracks slightly increase with impulse width and single pulse energy. The main surface conversion products generated during MAO process in aqueous solutions containing aluminate are rutile TiO2, anatase TiO2, and a large amount of Al2TiO5. The effects of single pulse energy on the micro-hardness and phase composition of ceramic coating are not as evident as those of frequency and duty cycle.

Effect of equal channel angular pressing on the microstructure and mechanical properties of Al-10Zn-2Mg alloy

NASA Astrophysics Data System (ADS)

Manjunath, G. K.; Kumar, G. V. Preetham; Bhat, K. Udaya

2018-04-01

The current investigation is focused on evaluating the mechanical properties and the microstructure of cast Al-10Zn-2Mg alloy processed through equal channel angular pressing (ECAP). The ECAP processing was attempted at minimum possible processing temperature. Microstructural characterization was carried out in optical microscopy, scanning electron microscopy, transmission electron microscopy and X-ray diffraction analysis. Hardness measurement and tensile tests were employed to estimate the mechanical properties. Experimental results showed that, ECAP processing leads to noticeable grain refinement in the alloy. Reasonable amount of dislocations were observed in the ECAP processed material. After ECAP processing, precipitates nucleation in the material was detected in the XRD analysis. ECAP leads to considerable enhancement in the mechanical properties of the material. After ECAP processing, microhardness of the material is increased from 144 Hv to 216 Hv. Also, after ECAP processing the UTS of the material is increased from 140 MPa to 302 MPa. The increase in the mechanical properties of the alloy after ECAP processing is due to the dislocation strengthening and grain refinement strengthening. Finally, fracture surface morphology of the tensile test samples also studied.

High levels of hydrogen peroxide in overnight tooth-whitening formulas: effects on enamel and pulp.

PubMed

Pugh, George; Zaidel, Lynette; Lin, Nora; Stranick, Michael; Bagley, Daniel

2005-01-01

Limited data are available to assess the safety of high levels of hydrogen peroxide in overnight tooth-whitening formulas. The purpose of this study was to assess the effects of hydrogen peroxide on enamel microhardness, pulp penetration, and enamel morphology. Colgate Platinum Professional Overnight Whitening System (Colgate Oral Pharmaceuticals, Inc., Canton, MA, USA) (10% carbamide peroxide, equivalent to 3.5% hydrogen peroxide) was compared with two prototype formulations containing either 7.0% or 12.0% hydrogen peroxide. In the pulp chamber studies, human extracted teeth were exposed to 3.5%, 7.0%, or 12.0% hydrogen peroxide for 30 minutes, 4 hours, or 7 hours. Microhardness, electron spectroscopy for chemical analysis, and atomic force microscopy evaluations were made from enamel blocks cut from human extracted molars. The enamel blocks were evaluated following 14 7-hour treatments (98 h total). At 7 hours' post-treatment, hydrogen peroxide penetrated the pulp chamber at 23.12 +/- 10.09, 24.58 +/- 6.90, and 26.39 +/- 5.43 microg for 3.5%, 7.0%, and 12.0% hydrogen peroxide, respectively. With regard to enamel morphology, pulp penetration, microhardness, and elemental composition, no statistically significant differences were observed between treatment groups following 98 hours of treatment. Hydrogen peroxide does not adversely affect enamel morphology or microhardness. The levels recovered in pulp indicate that hydrogen peroxide is not expected to inhibit pulpal enzymes. Overnight tray products containing levels of hydrogen peroxide of 3.5%, 7.0%, and 12.0% are not expected to adversely affect the enamel or pulpal enzymes. Additional safety studies are needed to assess the potential for tooth sensitivity and gingival irritation.

Effect of Shielding Gas on the Properties of AW 5083 Aluminum Alloy Laser Weld Joints

NASA Astrophysics Data System (ADS)

Vyskoč, Maroš; Sahul, Miroslav; Sahul, Martin

2018-04-01

The paper deals with the evaluation of the shielding gas influence on the properties of AW 5083 aluminum alloy weld joints produced with disk laser. Butt weld joints were produced under different shielding gas types, namely Ar, He, Ar + 5 vol.% He, Ar + 30 vol.% He and without shielding weld pool. Light and electron microscopy, computed tomography, microhardness measurements and tensile testing were used for evaluation of weld joint properties. He-shielded weld joints were the narrowest ones. On the other hand, Ar-shielded weld joints exhibited largest weld width. The choice of shielding gas had significant influence on the porosity level of welds. The lowest porosity was observed in weld joint produced in Ar with the addition of 5 vol.% He shielding atmosphere (only 0.03%), while the highest level of porosity was detected in weld joint produced in pure He (0.24%). Except unshielded aluminum alloy weld joint, the lowest tensile strength was recorded in He-shielded weld joints. On the contrary, the highest average microhardness was measured in He-shielded weld joints.

Microstructure and properties of Cu-Sn-Zn-TiO 2 nano-composite coatings on mild steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Weidong; Cao, Di; Jin, Yunxue

Cu-Sn-Zn coatings have been widely used in industry for their unique properties, such as good conductivity, high corrosion resistance and excellent solderability. To further improve the mechanical performance of Cu-Sn-Zn coatings, powder-enhanced method was applied and Cu-Sn-Zn-TiO 2 nano-composite coatings with different TiO 2 concentration were fabricated. The microstructure of Cu-Sn-Zn-TiO 2 nano-composite coatings were investigated by X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The mechanical properties of coatings including microhardness and wear resistance were studied. The results indicate that the incorporation of TiO 2 nanoparticle can significantly influence the properties of Cu-Sn-Zn coatings. The microhardness of Cu-Sn-Zn coatingmore » was increased to 383 HV from 330 HV with 1 g/L TiO 2 addition. Also, the corrosion resistance of coating was enhanced. The effects of TiO 2 nanoparticle concentration on the microstructure, mechanical properties and corrosion resistance of Cu-Sn-Zn-TiO 2 nano-composite coatings were discussed.« less

Microstructure of Vacuum-Brazed Joints of Super-Ni/NiCr Laminated Composite Using Nickel-Based Amorphous Filler Metal

NASA Astrophysics Data System (ADS)

Ma, Qunshuang; Li, Yajiang; Wu, Na; Wang, Juan

2013-06-01

Vacuum brazing of super-Ni/NiCr laminated composite and Cr18-Ni8 stainless steel was carried out using Ni-Cr-Si-B amorphous filler metal at 1060, 1080, and 1100 °C, respectively. Microstructure and phase constitution were investigated by means of optical and scanning electron microscopy, energy-dispersive spectroscopy, x-ray diffraction, and micro-hardness tester. When brazed at 1060-1080 °C, the brazed region can be divided into two distinct zones: isothermally solidified zone (ISZ) consisting of γ-Ni solid solution and athermally solidified zone (ASZ) consisting of Cr-rich borides. Micro-hardness of the Cr-rich borides formed in the ASZ was as high as 809 HV50 g. ASZ decreased with increase of the brazing temperature. Isothermal solidification occurred sufficiently at 1100 °C and an excellent joint composed of γ-Ni solid solution formed. The segregation of boron from ISZ to residual liquid phase is the reason of Cr-rich borides formed in ASZ. The formation of secondary precipitates in diffusion-affected zone is mainly controlled by diffusion of B.

Preparation and Investigation of Electrodeposited Ni-NANO-Cr2O3 Composite Coatings

NASA Astrophysics Data System (ADS)

Jiang, Jibo; Feng, Chenqi; Qian, Wei; Yu, Libin; Ye, Fengying; Zhong, Qingdong; Han, Sheng

2016-12-01

The electrodeposition of Ni-nano-Cr2O3 composite coatings was studied in electrolyte containing different contents of Cr2O3 nanoparticles (Cr2O3 NPs) on mild steel surfaces. Some techniques such as X-ray diffraction (XRD), scanning electron microscopy (SEM), microhardness, the potentiodynamic polarization curves (Tafel) and electrochemical impedance spectroscopy (EIS) were used to compare pure Ni coatings and Ni-nano-Cr2O3 composite coatings. The results show that the incorporation of Cr2O3 NPs resulted in an increase of hardness and corrosion resistance, and the maximum microhardness of Ni-nano-Cr2O3 composite coatings reaches about 495 HV. The coatings exhibit an active-passive transition and relatively large impedance values. Moreover, the effect of Cr2O3 NPs on Ni electrocrystallization is also investigated by cyclic voltammetry (CV) and EIS spectroscopy, which demonstrates that the nature of Ni-based composite coatings changes attributes to Cr2O3 NPs by offering more nucleation sites and less charge transfer resistance.

Characterization of Al/crystallized Al-based metallic glass composites produced by repeated roll bonding process

NASA Astrophysics Data System (ADS)

Alizadeh, Morteza; Khoramkhorshid, Saba; Taghvaei, Amir Hossein; Gokuldoss, Prashanth Konda

2017-07-01

Devitrified Al84Gd6Ni7Co3 glassy particles have been used to reinforce Al-matrix composites through repeated roll bonding (RRB) process. Microstructural characterization of the produced composites after various rolling cycles was performed by scanning electron microscopy. Mechanical properties of the fabricated composites were evaluated by the tensile and microhardness tests. The results indicate that the RRB process is successful to produce composites with the negligible amount of flaws and porosity, and it is followed by homogeneous distribution of Al84Gd6Ni7Co3 particles in the Al matrix after nine rolling passes. Elongation of the composites improves significantly upon RRB cycles and the tensile strength and microhardness of them increase more than two times compared to unreinforced Al. According to fractography results, the enhanced mechanical properties are correlated with formation of excellent bonding at the interface of Al84Gd6Ni7Co3 particles and Al matrix. The theoretical values of composites hardness and yield strength calculated based on iso-strain model show a good agreement with respect to the experimental results.

Structure and Properties of the Aluminide Coatings on the Inconel 625 Superalloy

NASA Astrophysics Data System (ADS)

Adamiak, Stanisław; Bochnowski, Wojciech; Dziedzic, Andrzej; Filip, Ryszard; Szeregij, Eugeniusz

2016-01-01

The research samples used in this study were based on the Inconel 625 alloy; the examined samples were coated with aluminide films deposited in a low-activity chemical vapor deposition (CVD) process. The samples' microstructure was investigated with optical and electron microscopy and energy dispersive X-ray spectroscopy analysis. Hardness measurements were performed using Vickers and Berkovich test methods. The adhesion of the aluminide coating was determined by fractography. It was shown that the fracture mechanism was different for the respective zones of the aluminide coating and the substrate material. The outer zone of the aluminide coating is characterized by an intercrystalline fracture, with a small contribution of transcrystalline fracture within individual grains (large crystallites in the bottom of the zone, composed of smaller crystallites, also show an intercrystalline fracture). The substrate material exhibited a ductile intercrystalline fracture. Based on this investigation, an increase of the microhardness of the material occurring at loads below 0.2 N was observed. When determining microhardness of aluminide coating it is necessary to take into account the optimal choice of the indentation tip.

Microstructure and properties of Cu-Sn-Zn-TiO 2 nano-composite coatings on mild steel

DOE PAGES

Gao, Weidong; Cao, Di; Jin, Yunxue; ...

2018-04-18

Cu-Sn-Zn coatings have been widely used in industry for their unique properties, such as good conductivity, high corrosion resistance and excellent solderability. To further improve the mechanical performance of Cu-Sn-Zn coatings, powder-enhanced method was applied and Cu-Sn-Zn-TiO 2 nano-composite coatings with different TiO 2 concentration were fabricated. The microstructure of Cu-Sn-Zn-TiO 2 nano-composite coatings were investigated by X-ray diffraction (XRD) and Scanning Electron Microscopy (SEM). The mechanical properties of coatings including microhardness and wear resistance were studied. The results indicate that the incorporation of TiO 2 nanoparticle can significantly influence the properties of Cu-Sn-Zn coatings. The microhardness of Cu-Sn-Zn coatingmore » was increased to 383 HV from 330 HV with 1 g/L TiO 2 addition. Also, the corrosion resistance of coating was enhanced. The effects of TiO 2 nanoparticle concentration on the microstructure, mechanical properties and corrosion resistance of Cu-Sn-Zn-TiO 2 nano-composite coatings were discussed.« less

Cold Spray Repair of Martensitic Stainless Steel Components

NASA Astrophysics Data System (ADS)

Faccoli, M.; Cornacchia, G.; Maestrini, D.; Marconi, G. P.; Roberti, R.

2014-12-01

The possibility of using cold spray as repair technique of martensitic stainless steel components was evaluated through laboratory investigations. An austenitic stainless steel feedstock powder was chosen, instead of soft metals powders like nickel, copper, or aluminum, used for repairing components made in light alloy or cast iron. The present study directly compares the microstructure, the residual stresses, and the micro-hardness of repairs obtained by cold spray and by TIG welding, that is commonly used as repair technique in large steel components. XRD and optical metallographic analysis of the repairs showed that cold spray offers some advantages, inducing compressive residual stresses in the repair and avoiding alterations of the interface between repair and base material. For these reasons, a heat treatment after the cold spray repair is not required to restore the base material properties, whereas a post-weld heat treatment is needed after the welding repair. Cold spray repair also exhibits a higher micro-hardness than the welding repair. In addition, the cavitation erosion resistance of a cold spray coating was investigated through ultrasonic cavitation tests, and the samples worn surfaces were observed by scanning electron microscopy.

Microstructure development during equal channel angular drawing of Al at room temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chakkingal, U.; Suriadi, A.B.; Thomson, P.F.

1998-08-11

In this study 3004 aluminum alloy can-stock remelt (composition 99.9% Al) was subjected to Equal Channel Angular Drawing (ECAD) at room temperature. Tests were conducted to an applied true strain of 2.95. Mechanical properties like tensile strength, ductility at fracture, and microhardness were measured. The development of the substructure was studied using optical and transmission electron microscopy. Subgrain sizes and their angular misorientations were measured as a function of the applied strain. In general, a substructure that consists of cells and subgrains was seen to evolve, as is expected for the case of high SFE fcc metals.

Formation of Superhard Chromium Carbide Crystal Microrods in Ni-Cr-C Systems

NASA Astrophysics Data System (ADS)

Val'chuk, V. P.; Zmienko, D. S.; Kolesov, V. V.; Chernozatonskii, L. A.

2018-04-01

Ni-Cr-C materials with a high hardness determined by the presence of regions consisting of Cr3C2 microrods with a record microhardness reaching 3200 kg/mm2 have been obtained. Their self-organization in a powder consisting of Ni, Cr, and carbon microparticles with a high weight percentage occurs in the process of its sintering at a temperature of 1300°C and the subsequent sharp cooling of the resulting alloy. A model has been proposed for the process of formation of such crystal microrods whose characteristics have been determined by hardness measurement, electron microscopy, and microchemical and X-ray diffraction analyses.

Precipitation kinetics during aging of an alumina-forming austenitic stainless steel

DOE PAGES

Trotter, Geneva; Hu, Bin; Sun, Annie Y.; ...

2016-04-28

The microstructural evolution of DAFA26, an alumina-forming austenitic (AFA) stainless steel, was investigated during aging. The effect of aging at 750 °C and 800 °C on the growth of spherical γ’-Ni 3(Al, Ti) particles present in the as-processed state was studied extensively using X-ray diffraction, microhardness testing, scanning electron microscopy, transmission electron microscopy, and atom probe tomography. The γ’ particles had a cube-on-cube orientation relationship with the matrix (i.e. ((010)(010) m//(010)(010) p, [100][100] m//[100][100] p)). The coarsening kinetics of γ’-Ni 3Al particles were in agreement with the Lifshitz, Slyozof-Wagner theory. Coarse Laves phase particles were also present in the as-processedmore » state, and during the aging process both smaller Laves phase precipitates and B2-NiAl precipitates formed on both the grain boundaries and in the matrix. As a result, the γ’ precipitates were determined to have the most impact on the room temperature hardness.« less

Precipitation kinetics during aging of an alumina-forming austenitic stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Trotter, Geneva; Hu, Bin; Sun, Annie Y.

The microstructural evolution of DAFA26, an alumina-forming austenitic (AFA) stainless steel, was investigated during aging. The effect of aging at 750 °C and 800 °C on the growth of spherical γ’-Ni 3(Al, Ti) particles present in the as-processed state was studied extensively using X-ray diffraction, microhardness testing, scanning electron microscopy, transmission electron microscopy, and atom probe tomography. The γ’ particles had a cube-on-cube orientation relationship with the matrix (i.e. ((010)(010) m//(010)(010) p, [100][100] m//[100][100] p)). The coarsening kinetics of γ’-Ni 3Al particles were in agreement with the Lifshitz, Slyozof-Wagner theory. Coarse Laves phase particles were also present in the as-processedmore » state, and during the aging process both smaller Laves phase precipitates and B2-NiAl precipitates formed on both the grain boundaries and in the matrix. As a result, the γ’ precipitates were determined to have the most impact on the room temperature hardness.« less

Microstructure, Mechanical Properties, and Age-Hardening Behavior of an Al-Si-Fe-Mn-Cu-Mg Alloy Produced by Spray Deposition

NASA Astrophysics Data System (ADS)

Feng, Wang; Jishan, Zhang; Baiqing, Xiong; Yongan, Zhang

2011-02-01

It has been recognized generally that the spray-deposited process is an innovative technique of rapid solidification. In this paper, Al-20Si-5Fe-3Mn-3Cu-1Mg alloy was synthesized by the spray atomization and deposition technique. The microstructure and mechanical properties of the spray-deposited alloy were studied using x-ray diffraction, scanning electron microscopy, transmission electron microscopy (TEM), and tensile tests. It is observed that the microstructure of spray-deposited Al-20Si-5Fe-3Mn-3Cu-1Mg alloy is composed of the α-Al,Si and the particle-like Al15(FeMn)3Si2 compounds. The aging process of the alloy was investigated by microhardness measurement, differential scanning calorimetry analysis, and TEM observations. The results indicate that the two types of precipitates, S-Al2CuMg and σ-Al5Cu6Mg2 precipitate from matrix and improve the tensile strength of the alloy efficiently at both the ambient and elevated temperatures (300 °C).

Historical and Metallurgical Characterization of a "Falchion" Sword Manufactured in Caino (Brescia, Italy) in the Early 17th Century A.D.

NASA Astrophysics Data System (ADS)

Tonelli, G.; Faccoli, M.; Gotti, R.; Roberti, R.; Cornacchia, G.

2016-08-01

A historical and metallurgical characterization of a "falchion" sword manufactured in Caino (Brescia, northern Italy) and dating from the early 17th century was performed to understand the manufacture methods of a Renaissance sword. At first, a set of size measurements was carried out to look for the existence of constant and/or recurring macroscopic sizes, which would indicate a standardized production, or of any type of proportionality between different parts of a sword, which would prove an intentional design activity. Light optical microscopy, scanning electron microscopy, energy-dispersive x-ray spectroscopy, quantometer analyses, and Vickers microhardness tests were then employed to analyze the microstructure and obtain the mechanical properties. All the metallurgical work is supported by an accurate study on the chemical composition of both metal-matrix and nonmetallic inclusions, which allowed for rebuilding and evaluating the efficiency of the whole production process.

Influence of Grain Refinement on Microstructure and Mechanical Properties of Tungsten Carbide/Zirconia Nanocomposites

NASA Astrophysics Data System (ADS)

Nasser, Ali; Kassem, Mohamed A.; Elsayed, Ayman; Gepreel, Mohamed A.; Moniem, Ahmed A.

2016-11-01

WC-W2C/ZrO2 nanocomposites were synthesized by pressure-less sintering (PS) and spark plasma sintering (SPS) of tungsten carbide/yttria-stabilized tetragonal zirconia, WC/TZ-3Y. Prior to sintering, WC/TZ-3Y powders were totally ball-milled for 20 and 120 h to obtain targeted nano (N) and nano-nano (N-N) structures, indicated by transmission electron microscopy and powder x-ray diffraction (PXRD). The milled powders were processed via PS at temperatures of 1773 and 1973 K for 70 min and SPS at 1773 K for 10 min. PXRD as well as SEM-EDS indicated the formation of WC-W2C/ZrO2 composites after sintering. The mechanical properties were characterized via Vicker microhardness and nanoindentation techniques indicating enhancements for sufficiently consolidated composites with high W2C content. The effects of reducing particle sizes on phase transformation, microstructure and mechanical properties are reported. In general, the composites based on the N structure showed higher microhardness than those for N-N structure, except for the samples PS-sintered at 1773 K. For instance, after SPS at 1773 K, the N structure showed a microhardness of 18.24 GPa. Nanoindentation measurements revealed that nanoscale hardness up to 22.33 and 25.34 GPa and modulus of elasticity up to 340 and 560 GPa can be obtained for WC-W2C/ZrO2 nanocomposites synthesized by the low-cost PS at 1973 K and by SPS at 1773 K, respectively.

Effect of laser power on the microstructure and mechanical properties of TiN/Ti3Al composite coatings on Ti6Al4V

NASA Astrophysics Data System (ADS)

Liu, Zhengdao; Zhang, Xiancheng; Xuan, Fuzhen; Wang, Zhengdong; Tu, Shandong

2013-07-01

Laser nitriding is one of the effective techniques to improve the surface properties of titanium alloys and has potential application in the life extension of last-stage steam turbine blades. However, cracking of surface coating is a common problem due to heat concentration in laser nitriding process. Conventionally, the cracks can be avoided through heat treatment, which may have an important influence on the mechanical properties of coating. Crack-free TiN/Ti3Al IMC coatings on Ti6Al4V are prepared by plasma spraying and laser nitriding. The microstructures, phase constitutes and compositions of the coating are observed and analyzed with scanning electron microscopy(SEM), X-ray diffraction(XRD) and X-ray energy-dispersive spectroscopy(EDS). Microhardness, elastic modulus, fracture toughness of the coating are measured. The results show that the crack- and pore-free IMC coatings can be made through the proposed method; with increasing laser power, the amount and density of TiN phase in the coating first increased and then decreased, leading to the similar trend of microhardness and elastic modulus and the reverse trend of fracture toughness of the coating. Both the average microhardness and elastic modulus of the coating increase three times higher than those of the substrate. The volume fraction of the TiN reinforced phase in composite can be controlled by varying the laser power and the cracking problem in laser nitriding process is successfully solved.

Characterization of a Messer – The late-Medieval single-edged sword of Central Europe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fajfar, Peter; Medved, Jožef; Klančnik, Grega

2013-12-15

Metallurgical characterization of a sword blade fragments dating from the second half of the 15th century found in central Slovenia was performed in order to determine its chemical composition, microstructure, microhardness, and to obtain insight into the methods of manufacture of a late-medieval Messer sword. As the artefact was broken, examinations were limited to six very small fragments that were allowed to be removed from the cutting edge, core and the back of the blade. Light optical microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, energy dispersive X-ray fluorescence spectrometry, differential scanning calorimetry, thermodynamics approach and Vickers micro-hardness tests weremore » employed to analyze the microstructure and mechanical properties. The results show that the sword was manufactured from a single wrought iron billet. The surface of the sword was carburized. No evidence of quenching was found. The ferritic microstructure is concentrated in the core, and the pearlitic in the outer layer of the blade. All metal fragments contained non-metallic inclusions that were derived mostly from slag and some from hammer scale. - Highlights: • A metallurgical characterization of a medieval sword blade has been performed. • The carbon content decreased from the surface to the core of the blade. • The dominant microstructure in the outer layer is pearlite and in the core is ferrite. • The presence of lump shaped and elongated non-metallic inclusions was observed. • The sword was manufactured from a single wrought iron billet.« less

Microstructural Analysis of Ti-6Al-4V Components Made by Electron Beam Additive Manufacturing

NASA Astrophysics Data System (ADS)

Coleman, Rashadd L.

Electron Beam Additive Manufacturing (EBAM) is a relatively new additive manufacturing (AM) technology that uses a high-energy electron beam to melt and fuse powders to build full-density parts in a layer by layer fashion. EBAM can fabricate metallic components, particularly, of complex shapes, in an efficient and cost-effective manner compared to conventional manufacturing means. EBAM is an enabling technology for rapid manufacturing (RM) of metallic components, and thus, can efficiently integrate the design and manufacturing of aerospace components. However, EBAM for aerospace-related applications remain limited because the effect of the EBAM process on part characteristics is not fully understood. In this study, various techniques including microhardness, optical microscopy (OM), X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), and electron backscatter diffraction (EBSD) were used to characterize Ti-6Al-4V components processed using EBAM. The results were compared to Ti-6Al-4V components processed using conventional techniques. In this study it is shown that EBAM built Ti-64 components have increased hardness, elastic modulus, and yield strength compared to wrought Ti-6Al-4V. Further, it is also shown in this study that the horizontal build EBAM Ti-6Al-4V has increased hardness, elastic modulus, and yield strength compared to vertical build EBAM due to a preferential growth of the beta phase.

Evaluation of the effects of the solution used for electrochemical dissolution of nickel-titanium endodontic files on dentine structure, microhardness and cell viability.

PubMed

Amaral, C C F; Ormiga, F; Boldrini, L C; Miranda, P G; Mendonça, T A; Granjeiro, J M; Gomes, J A C P

2018-05-15

To evaluate the effects of the [NaF 12 g/L + NaCl 1 g/L] solution used in the electrochemical dissolution process of fractured endodontic files, as well as its NiTi-containing product, on dentine hardness, topography and human fibroblast viability. Sixty single-rooted human teeth were evaluated for dentine microhardness using the Vickers hardness test and the area and number of dentinal tubules by scanning electron microscopy. The samples were divided according to the dentine surface treatment: distilled water; 17% EDTA; [NaF 12 g/L + NaCl 1 g/L]; and 17% EDTA + [NaF 12 g/L + NaCl 1 g/L]. Thirty-six single-rooted human teeth were divided according to the irrigation protocol: Dulbecco's Modified Eagle's Medium + 10% fetal bovine serum; 5.25% NaOCl; [NaF 12 g/L + NaCl 1 g/L]; and [NaF 12 g/L + NaCl 1 g/L+NiTi]. The extracts in contact with the apical foramen were used in the MTT assay to evaluate human fibroblast viability, with dilutions of 100, 50, 25 and 12.5%. Statistical tests used were paired t-tests, one-way ANOVA, Tukey's test, Kruskal-Wallis test and Dunn's post-test. The [NaF 12 g/L + NaCl 1 g/L] solution did not modify the dentine microhardness or the average dentinal tubule area. However, the EDTA induced changes in the dentine structure and microhardness (p<0.05). The [NaF 12 g/L + NaCl 1 g/L] solution and its NiTi-containing product had lower cytotoxicity than NaOCl at dilutions of 25% and 50% (p<0.01). The [NaF 12 g/L + NaCl 1 g/L] solution did not alter dentine microhardness or damage the dentine structure. It also demonstrated lower cytotoxicity than NaOCl. This article is protected by copyright. All rights reserved. This article is protected by copyright. All rights reserved.

Special Features of the Structure of Laser-Welded Joints of Dissimilar Alloys Based on Titanium and Aluminum

NASA Astrophysics Data System (ADS)

Nikulina, A. A.; Smirnov, A. I.; Turichin, G. A.; Klimova-Korsmik, O. G.; Babkin, K. D.

2017-11-01

The structure of laser-welded joints of parts having different thicknesses fabricated from alloys based on aluminum and titanium has been studied. Results of transmission and scanning electron microscopy measurements and x-ray diffraction analysis show that the diffusion interaction of microvolumes of two alloys in the weld leads to the formation of two interlayers: (i) a continuous intermetallic TiAl layer with thickness below 1 μm adjacent to the titanium alloy and (ii) a layer consisting of TiAl3 intermetallic dendrites with thickness of 2 - 6 μm adjacent to the TiAl layer. The average microhardness of the intermetallic layer is about 490 HV.

Finding an Optimal Thermo-Mechanical Processing Scheme for a Gum-Type Ti-Nb-Zr-Fe-O Alloy

NASA Astrophysics Data System (ADS)

Nocivin, Anna; Cojocaru, Vasile Danut; Raducanu, Doina; Cinca, Ion; Angelescu, Maria Lucia; Dan, Ioan; Serban, Nicolae; Cojocaru, Mirela

2017-09-01

A gum-type alloy was subjected to a thermo-mechanical processing scheme to establish a suitable process for obtaining superior structural and behavioural characteristics. Three processes were proposed: a homogenization treatment, a cold-rolling process and a solution treatment with three heating temperatures: 1073 K (800 °C), 1173 K (900 °C) and 1273 K (1000 °C). Results of all three proposed processes were analyzed using x-ray diffraction and scanning electron microscopy imaging, to establish and compare the structural modifications. The behavioural status was completed with micro-hardness and tensile strength tests. The optimal results were obtained for solution treatment at 1073 K.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arul, K. Thanigai; Kolanthai, Elayaraja; Manikandan, E.

Highlights: • Rapid technique to synthesize nanorods of magnesium ion incorporated hydroxyapatite. • Enhanced electrical and mechanical properties. • Improved photoluminescence and wettability on magnesium incorporation. • Increased in vitro bioactivity. - Abstract: Nanocrystalline hydroxyapatite (HAp-Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2,} 35 nm) and magnesium (Mg{sup 2+}) ion incorporated HAp were synthesized by microwave technique. XRD (X-ray diffraction), FTIR (Fourier transform infrared spectroscopy), FE-HRTEM (Field emission high resolution transmission electron microscopy), DLS (dynamic light scattering), EDXRF (energy dispersive X-ray fluorescence spectrometry), microhardness, permittivity and alternating current (ac) conductivity, besides the PL (photoluminescence), wettability and in vitro bioactivity of the samples weremore » analysed. EDXRF revealed the Mg{sup 2+} ion incorporation in HAp. The Mg{sup 2+} ion incorporation did not alter the phase but drastically reduced the crystallite size and particle size respectively by 48% and 32%. There was enhanced microhardness (24%) at low level (<13%) and decreased zeta potential of Mg{sup 2+} ion incorporation. The permittivity, ac conductivity, PL, wettability and in vitro bioactivity were enhanced on Mg{sup 2+} ion incorporation. These properties enable them to be a promising candidate for wound healing, bone replacement applications and also as a biosensor.« less

Fabrication of naturel pumice/hydroxyapatite composite for biomedical engineering.

PubMed

Komur, Baran; Lohse, Tim; Can, Hatice Merve; Khalilova, Gulnar; Geçimli, Zeynep Nur; Aydoğdu, Mehmet Onur; Kalkandelen, Cevriye; Stan, George E; Sahin, Yesim Muge; Sengil, Ahmed Zeki; Suleymanoglu, Mediha; Kuruca, Serap Erdem; Oktar, Faik Nuzhet; Salman, Serdar; Ekren, Nazmi; Ficai, Anton; Gunduz, Oguzhan

2016-07-07

We evaluated the Bovine hydroxyapatite (BHA) structure. BHA powder was admixed with 5 and 10 wt% natural pumice (NP). Compression strength, Vickers micro hardness, Fourier transform infrared spectroscopy, scanning electron microscopy (SEM) and X-ray diffraction studies were performed on the final NP-BHA composite products. The cells proliferation was investigated by MTT assay and SEM. Furthermore, the antimicrobial activity of NP-BHA samples was interrogated. Variances in the sintering temperature (for 5 wt% NP composites) between 1000 and 1300 °C, reveal about 700 % increase in the microhardness (~100 and 775 HV, respectively). Composites prepared at 1300 °C demonstrate the greatest compression strength with comparable result for 5 wt% NP content (87 MPa), which are significantly better than those for 10 wt% and those that do not include any NP (below 60 MPa, respectively). The results suggested the optimal parameters for the preparation of NP-BHA composites with increased mechanical properties and biocompatibility. Changes in micro-hardness and compression strength can be tailored by the tuning the NP concentration and sintering temperature. NP-BHA composites have demonstrated a remarkable potential for biomedical engineering applications such as bone graft and implant.

Laser-deposited thin films of biocompatible ceramic

NASA Astrophysics Data System (ADS)

Jelinek, Miroslav; Olsan, V.; Jastrabik, Lubomir; Dostalova, Tatjana; Himmlova, Lucia; Kadlec, Jaromir; Pospichal, M.; Simeckova, M.; Fotakis, Costas

1995-03-01

Thin films of biocompatible materials such as hydroxylapatite (HA) - Ca10 (PO4)6(OH)2 were deposited by laser ablation technique. The films of HA were created on Ti substrates by KrF laser. The layers were deposited in vacuum, in pure H2O vapors (pressure 2 X 10-3 mbar - 2 X 10-1 mbar), and in Ar/H2O vapor mixture. Influence of laser energy density ET (3 Jcm-2, 13 Jcm-2) and substrate temperature Tg (500 degree(s)C - 760 degree(s)C) on the film parameters was studied. Two different technological processes were used for HA target preparation. Films and targets were characterized by Rutherford backscattering analysis (RBS), particle induced x-ray emission (PIXE), x-ray diffraction (XRD), scanning electron microscopy (SEM) and by Knoop microhardness and scratch test. The best crystalline HA films were reached in the mixture of Ar/H2O. Higher Tg had to be used for such deposition. Higher Tg was also preferable from the point of film microhardness. Adhesion of films to the substrates in the range of tens of Newtons was measured. The preliminary results of in vitro experiments of films biotolerance and resorbability are also presented.

Development and characterization of laser surface cladding (Ti,W)C reinforced Ni-30Cu alloy composite coating on copper

NASA Astrophysics Data System (ADS)

Yan, Hua; Zhang, Peilei; Yu, Zhishui; Li, Chonggui; Li, Ruidi

2012-07-01

To improve the wear resistance of copper components, laser surface cladding (LSC) was applied to deposit (Ti,W)C reinforced Ni-30Cu alloy composite coating on copper using a cladding interlayer of Ni-30Cu alloy by Nd:YAG laser. The microstructure and phases of the composite coating were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD) and X-ray energy dispersive microanalysis (EDX). Microhardness tester and pin-on-disc wear tester were employed to evaluate the hardness and dry-sliding wear resistance. The results show that crack-free composite coating with metallurgical bonding to the copper substrate is obtained. Phases identified in the (Ti,W)C-reinforced Ni-30Cu alloy composite layer are composed of TiWC2 reinforcements and (Ni,Cu) solid solution. TiWC2 reinforcements are distributed uniformly in the (Ni,Cu) solid solution matrix with dendritic morphology in the upper region and with particles in the mid-lower region. The microhardness and wear properties of the composite coating are improved significantly in comparison to the as-received copper substrate due to the addition of 50 wt% (Ti,W)C multicarbides.

Corrosion Behavior and Microhardness of Ni-P-SiO2-Al2O3 Nano-composite Coatings on Magnesium Alloy

NASA Astrophysics Data System (ADS)

Sadreddini, S.; Rahemi Ardakani, S.; Rassaee, H.

2017-05-01

In the present work, nano-composites of Ni-P-SiO2-Al2O3 were coated on AZ91HP magnesium alloy. The surface morphology of the nano-composite coating was studied by field emission scanning electron microscopy (FESEM). The amount of SiO2 in the coating was determined by energy-dispersive analysis of x-ray (EDX), and the crystalline structure of the coating was examined by x-ray diffractometer (XRD). All the experiments concerning the corrosion behavior of the coating carried out in 3.5 wt.% NaCl solution and evaluated by electrochemical impedance spectroscopy (EIS) and polarization technique. The results showed that an incorporation of SiO2 and Al2O3 in Ni-P coating at the SiO2 concentration of 10 g/Land 14 g/LAl2O3 led to the lowest corrosion rate ( i corr = 1.3 µA/cm2), the most positive E corr and maximum microhardness (496 VH). Furthermore, Ni-P-SiO2-Al2O3 nano-composite coating possesses less porosity than that in Ni-P coating, resulting in improving corrosion resistance.

Application of Laser Treatment for Hardening Parts of Gas Turbine Engines from Titanium Alloys

NASA Astrophysics Data System (ADS)

Girzhon, V. V.; Ovchinnikov, A. V.

2017-03-01

X-ray diffraction analysis and light microscopy are used to study the structure of surface layers of helically extruded specimens of titanium alloy VT25U after laser fusion of the surface. It is shown that the rates of cooling of the melt promote formation of a martensitic α″-phase in the zone of laser fusion and of a submicrocrystalline microstructure. The microhardness in the zone of fusion of the initial specimens exceeds the microhardness of the specimens after the extrusion.

The Mechanical and Microstructural Changes of Sn-Ag-Bi Solders with Cooling Rate and Bi Content Variations

NASA Astrophysics Data System (ADS)

Abd El-Rehim, A. F.; Zahran, H. Y.; AlFaify, S.

2018-02-01

The purpose of this study is to investigate the influence of cooling rate and Bi addition on the microstructure evolution and mechanical properties of Sn-3.5Ag alloy. A series of Sn-3.5Ag-xBi solders has been fabricated with Bi content in the range of 0.5-3.5 wt.%. After solution heat treatment at 170 °C for 24 h and subsequent aging heat treatment at 100 °C for 2 h, samples were divided into two groups. One group was rapidly quenched into iced water (water quenching) for the fast cooling rate (20 °C/s), while the second group was slowly cooled (furnace cooling) in the furnace for the slow cooling rate (0.2 °C/s) after the furnace reflow. The microstructural evolutions of the present solders have been investigated using x-ray diffraction and scanning electron microscopy. The microhardness was measured to correlate the mechanical properties to alloy compositions and cooling rate. It was found that the microhardness of Sn-3.5Ag-xBi solders increased with increasing cooling rate. The indentation creep curves have been evaluated from the obtained microhardness values. Results revealed the steady-state creep rate decreased with increasing Bi content exhibiting an anomalous behavior at 2.5Bi. The reason for improved creep resistance of Sn-3.5Ag-xBi solders is the result of the combination of the solid solution strengthening and precipitation strengthening of Bi. The mean values of stress exponent indicated that the operative creep mechanism is dislocation climb.

Composite Ni-Co-fly ash coatings on 5083 aluminium alloy

NASA Astrophysics Data System (ADS)

Panagopoulos, C. N.; Georgiou, E. P.; Tsopani, A.; Piperi, L.

2011-03-01

Ni-Co-fly ash coatings were deposited on zincate treated 5083 wrought aluminium alloy substrates with the aid of the electrodeposition technique. Structural and chemical characterization of the produced composite coatings was performed with the aid of X-ray diffraction (XRD), scanning electron microscopy (SEM) and electron dispersive X-ray analysis (EDS) techniques. The Ni-Co-fly ash coatings were found to consist of a crystalline Ni-Co solid solution with dispersed fly ash particles. In addition, chemical analysis of the Ni-Co matrix showed that it consisted of 80 wt.% Ni and 20 wt.% Co. The co-deposition of fly ash particles leads to a significant increase of the microhardness of the coating. The corrosion behaviour of the Ni-Co-fly ash/zincate coated aluminium alloy, in a 0.3 M NaCl solution (pH = 3.5), was studied by means of potentiodynamic corrosion experiments.

Quantitative description of the T1 morphology and strengthening mechanisms in an age-hardenable Al-Li-Cu alloy

NASA Astrophysics Data System (ADS)

Dorin, Thomas; Deschamps, Alexis; De Geuser, Frédéric; Weyland, Matthew

In the Al-Cu-Li system, the main strengthening precipitate is the T1 phase (Al2CuLi). In order to understand the strengthening related to the formation of this phase, we first present an investigation of the morphology of the T1 phase in an AA2198 alloy using Transmission Electron Microscopy (TEM) and Differential Scanning Calorimetry (DSC) in relation with the evolution of micro-hardness. In parallel, we present an investigation of the interaction between T1 precipitates and dislocations using High Angle Annular Dark Field (HAADF) imaging in an atomic resolution Scanning Transmission Electron Microscope (STEM). The atomic scale imaging of precipitates makes it possible to quantify the density of shearing events, which turns out to be insufficient to account for the imposed plastic strain. We discuss the implications of this result in terms of precipitate-dislocation interactions.

Adaptive characterization of recrystallization kinetics in IF steel by electron backscatter diffraction.

PubMed

Kim, Dong-Kyu; Park, Won-Woong; Lee, Ho Won; Kang, Seong-Hoon; Im, Yong-Taek

2013-12-01

In this study, a rigorous methodology for quantifying recrystallization kinetics by electron backscatter diffraction is proposed in order to reduce errors associated with the operator's skill. An adaptive criterion to determine adjustable grain orientation spread depending on the recrystallization stage is proposed to better identify the recrystallized grains in the partially recrystallized microstructure. The proposed method was applied in characterizing the microstructure evolution during annealing of interstitial-free steel cold rolled to low and high true strain levels of 0.7 and 1.6, respectively. The recrystallization kinetics determined by the proposed method was found to be consistent with the standard method of Vickers microhardness. The application of the proposed method to the overall recrystallization stages showed that it can be used for the rigorous characterization of progressive microstructure evolution, especially for the severely deformed material. © 2013 The Authors Journal of Microscopy © 2013 Royal Microscopical Society.

Effects of the Treating Time on Microstructure and Erosion Corrosion Behavior of Salt-Bath-Nitrided 17-4PH Stainless Steel

NASA Astrophysics Data System (ADS)

Wang, Jun; Lin, Yuanhua; Li, Mingxing; Fan, Hongyuan; Zeng, Dezhi; Xiong, Ji

2013-08-01

The effects of salt-bath nitriding time on the microstructure, microhardness, and erosion-corrosion behavior of nitrided 17-4PH stainless steel at 703 K (430 °C) were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and erosion-corrosion testing. The experimental results revealed that the microstructure and phase constituents of the nitrided surface alloy are highly process condition dependent. When 17-4PH stainless steel was subjected to complex salt-bathing nitriding, the main phase of the nitrided layer was expanded martensite ( α`), expanded austenite (S), CrN, Fe4N, and Fe2N. The thickness of nitrided layers increased with the treating time. The salt-bath nitriding improves effectively the surface hardness. The maximum values measured from the treated surface are observed to be 1100 HV0.1 for 40 hours approximately, which is about 3.5 times as hard as the untreated material (309 HV0.1). Low-temperature nitriding can improve the erosion-corrosion resistance against two-phase flow. The sample nitrided for 4 hours has the best corrosion resistance.

Effect of ion irradiation on the surface, structural and mechanical properties of brass

NASA Astrophysics Data System (ADS)

Ahmad, Shahbaz; Bashir, Shazia; Ali, Nisar; Umm-i-Kalsoom; Yousaf, Daniel; Faizan-ul-Haq; Naeem, Athar; Ahmad, Riaz; Khlaeeq-ur-Rahman, M.

2014-04-01

Modifications to the surface, structural and mechanical properties of brass after ion irradiation have been investigated. Brass targets were bombarded by carbon ions of 2 MeV energy from a Pelletron linear accelerator for various fluences ranging from 56 × 1012 to 26 × 1013 ions/cm2. A scanning electron microscope and X-ray diffractometer were utilized to analyze the surface morphology and crystallographic structure respectively. To explore the mechanical properties e.g., yield stress, ultimate tensile strength and microhardness of irradiated brass, an universal tensile testing machine and Vickers microhardness tester were used. Scanning electron microscopy results revealed an irregular and randomly distributed sputter morphology for a lower ion fluence. With increasing ion fluence, the incoherently shaped structures were transformed into dendritic structures. Nano/micro sized craters and voids, along with the appearance of pits, were observed at the maximum ion fluence. From X-ray diffraction results, no new phases were observed to be formed in the brass upon irradiation. However, a change in the peak intensity and higher and lower angle shifting were observed, which represents the generation of ion-induced defects and stresses. Analyses confirmed modifications in the mechanical properties of irradiated brass. The yield stress, ultimate tensile strength and hardness initially decreased and then increased with increasing ion fluence. The changes in the mechanical properties of irradiated brass are well correlated with surface and crystallographic modifications and are attributed to the generation, augmentation, recombination and annihilation of the ion-induced defects.

Characterization of ZnAl cast alloys with Na addition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gancarz, Tomasz, E-mail: t.gancarz@imim.pl; Cempura, Grzegorz; Skuza, Wojciech

2016-01-15

This study was aimed at evaluating the microstructural change and thermal, electrical and mechanical properties with the addition of Na to eutectic ZnAl alloys. Solders based on eutectic ZnAl containing 0.2 to 3.0 (wt.%) of Na were developed for high temperature solder. Differential scanning calorimetry (DSC) measurements were performed to determine the melting temperatures of the alloys. Thermal linear expansion and electrical resistivity measurements were performed over − 50 °C to 300 °C and 30 °C to 300 °C temperature ranges, respectively. The microstructure of the specimens was analyzed using scanning (SEM) and transmission electron microscopy (TEM) techniques. Chemical microanalysismore » was performed by energy-dispersive X-ray spectroscopy (EDS) on SEM and TEM. The precipitates of NaZn{sub 13} were confirmed by X-ray diffraction (XRD) measurements and selected area electron diffraction (SAED) techniques. The addition of Na to eutectic ZnAl alloy increased the electrical resistivity and reduced the coefficient of thermal expansion; however, the melting point did not change. The mechanical properties, strain and microhardness increased with Na content in alloys. - Highlights: • High temperature soldering materials of ZnAl with Na were designed and characterized. • Precipitates of NaZn{sub 13}were observed and confirmed using TEM and XRD. • Addition of Na to eutectic ZnAl cussed increased mechanical properties. • NaZn{sub 13} caused increased electrical resistivity and microhardness, and reduced the CTE.« less

Measurements of microhardness during transient horizontal directional solidification of Al-Rich Al-Cu alloys: Effect of thermal parameters, primary dendrite arm spacing and Al2Cu intermetallic phase

NASA Astrophysics Data System (ADS)

Barros, André Santos; Magno, Igor Alexsander; Souza, Fabrício Andrade; Mota, Carlos Alberto; Moreira, Antonio Luciano; Silva, Maria Adrina; Rocha, Otávio Lima

2015-05-01

In this work, the effect of the growth rate (VL) and cooling rate (TR), primary dendritic arm spacing (λ1) and Al2Cu intermetallic phase on the microhardness was investigated during transient horizontal directional solidification of Al-3wt%Cu and Al-8wt%Cu alloys. Microstructural characterization of the investigated alloys was performed using traditional techniques of metallography, optical and SEM microscopy and X-Ray diffraction. The microhardness evolution as a function of the thermal and microstructural parameters (VL, TR, and λ1) was evaluated using power and Hall-Petch type experimental laws, which were compared with other laws in the literature. In order to examine the effect of the Al2Cu intermetallic phase, microhardness measurements were performed in interdendritic regions. Finally, a comparative analysis was performed between the experimental data of this work and theoretical models from the literature that have been proposed to predict primary dendrite arm spacing, which have been tested in numerous works considering upward directional solidification.

Effects of high temperature treatment on microstructure and mechanical properties of laser-clad NiCrBSi/WC coatings on titanium alloy substrate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li, Guang Jie; Li, Jun, E-mail: jacob_lijun@sina.com; Luo, Xing

2014-12-15

Laser-clad composite coatings on the Ti6Al4V substrate were heat-treated at 700, 800, and 900 °C for 1 h. The effects of post-heat treatment on the microstructure, microhardness, and fracture toughness of the coatings were investigated by scanning electron microscopy, X-ray diffractometry, energy dispersive spectroscopy, and optical microscopy. The wear resistance of the coatings was evaluated under dry reciprocating sliding friction at room temperature. The coatings mainly comprised some coarse gray blocky (W,Ti)C particles accompanied by the fine white WC particles, a large number of black TiC cellular/dendrites, and the matrix composed of NiTi and Ni{sub 3}Ti; some unknown rich Ni-more » and Ti-rich particles with sizes ranging from 10 nm to 50 nm were precipitated and uniformly distributed in the Ni{sub 3}Ti phase to form a thin granular layer after heat treatment at 700 °C. The granular layer spread from the edge toward the center of the Ni{sub 3}Ti phase with increasing temperature. A large number of fine equiaxed Cr{sub 23}C{sub 6} particles with 0.2–0.5 μm sizes were observed around the edges of the NiTi supersaturated solid solution when the temperature was further increased to 900 °C. The microhardness and fracture toughness of the coatings were improved with increased temperature due to the dispersion-strengthening effect of the precipitates. Dominant wear mechanisms for all the coatings included abrasive and delamination wear. The post-heat treatment not only reduced wear volume and friction coefficient, but also decreased cracking susceptibility during sliding friction. Comparatively speaking, the heat-treated coating at 900 °C presented the most excellent wear resistance. - Highlights: • TiC + WC reinforced intermetallic compound matrix composite coatings were produced. • The formation mechanism of the reinforcements was analyzed. • Two precipitates were generated at elevated temperature. • Cracking susceptibility and microhardness of the coatings were improved. • Post-heat treatment enhances wear resistance of the coatings.« less

Remineralization potential of nano-hydroxyapatite on enamel and cementum surrounding margin of computer-aided design and computer-aided manufacturing ceramic restoration

PubMed Central

Juntavee, Niwut; Juntavee, Apa; Plongniras, Preeyarat

2018-01-01

Objective This study investigates the effects of nano-hydroxyapatite (NHA) gel and Clinpro (CP) on remineralization potential of enamel and cementum at the cavosurface area of computer-aided design and computer-aided manufacturing ceramic restoration. Materials and methods Thirty extracted human mandibular third molars were sectioned at 1 mm above and below the cemento–enamel junction to remove the cemento–enamel junction portions and replaced them with zirconia ceramic disks by bonding them to the crown and root portions with resin cement. The enamel and cementum with an area of 4×4 mm2 surrounding the ceramic disk was demineralized with carbopol. The demineralized surfaces were treated with either NHA or CP, while 1 group was left with no treatment. Vickers microhardness of enamel and cementum were determined before demineralization, after demineralization, and after remineralization. Analysis of variance and Tukey multiple comparisons were used to determine statistically significant differences at 95% level of confidence. Scanning electron microscopy and X-ray diffraction were used to evaluate for surface alterations. Results The mean ± SD of Vickers microhardness for before demineralization, after demineralization, and after remineralization for enamel and cementum were 377.37±22.99, 161.95±10.54, 161.70±5.92 and 60.37±3.81, 17.65±0.91, 17.04±1.00 for the no treatment group; 378.20±18.76, 160.72±8.38, 200.08±8.29 and 62.58±3.37, 18.38±1.33, 27.99±2.68 for the NHA groups; and 380.53±25.14, 161.94±5.66, 193.16±7.54 and 62.78±4.75, 19.07±1.30, 24.46±2.02 for the CP groups. Analysis of variance indicated significant increase in microhardness of demineralized enamel and cementum upon the application of either NHA or CP (p<0.05). Post hoc multiple comparisons indicated significantly higher remineralization capability of NHA for both enamel and cementum than CP (p<0.05), as evidenced by scanning electron microscopy, indicating NHA particle deposition in the area of remineralization, and crystallinity accumulation, as indicated by X-ray diffraction. Conclusion NHA gel and CP were capable of remineralization of the enamel and cementum. NHA was more capable in the remineralization process than CP. NHA was extremely capable in the remineralization process for enamel and cementum surrounding the margin of the computer-aided design and computer-aided manufacturing ceramic. PMID:29780246

Effects of ion- and electron-beam treatment on surface physicochemical properties of polylactic acid

NASA Astrophysics Data System (ADS)

Pukhova, I. V.; Savkin, K. P.; Laput, O. A.; Lytkina, D. N.; Botvin, V. V.; Medovnik, A. V.; Kurzina, I. A.

2017-11-01

We describe our investigations of the surface physicochemical and mechanical properties of polylactic acid modified by silver, argon and carbon ion implantation to doses of 1 × 1014, 1 × 1015 and 1 × 1016 ions/cm2 at energies of 20 keV (for C and Ar) and 40 keV (for Ag), and by electron beam treatment with pulse-width of 100-300 μs in 50 μs increments at a beam energy 8 keV. Carbonyl bonds (sbnd Cdbnd O) related IR peak was reduced after ion and electron beam irradiation. Molecular weight of PLA decreases twice and does not depend on the nature of the bombarding particles. The microhardness of treated samples decreases by a factor of 1.3, and the surface conductivity increases by 6 orders of magnitude after ion implantation, and increases only modestly after electron beam treatment. Atomic force microscopy shows that surface roughness increases with irradiation dose. Samples irradiated with Ag to a dose of 1 × 1016 ions/cm2 show the greatest roughness of 190 nm.

Titanium Alloys Thin Sheet Welding with the Use of Concentrated Solar Energy

NASA Astrophysics Data System (ADS)

Pantelis, D. I.; Kazasidis, M.; Karakizis, P. N.

2017-12-01

The present study deals with the welding of titanium alloys thin sheets 1.3 mm thick, with the use of concentrated solar energy. The experimental part of the work took place at a medium size solar furnace at the installation of the Centre National de la Recherche Scientifique, at Odeillo, in Southern France, where similar and dissimilar defect-free welds of titanium Grades 4 and 6 were achieved, in the butt joint configuration. After the determination of the appropriate welding conditions, the optimum welded structures were examined and characterized microstructurally, by means of light optical microscopy, scanning electron microscopy, and microhardness testing. In addition, test pieces extracted from the weldments were tested under uniaxial tensile loading aiming to the estimation of the strength and the ductility of the joint. The analysis of the experimental results and the recorded data led to the basic concluding remarks which demonstrate increased hardness distribution inside the fusion area and severe loss of ductility, but adequate yield and tensile strength of the welds.

Enhancement of the wear resistance and microhardness of aluminum alloy by Nd:YaG laser treatment.

PubMed

Hussein, Haitham T; Kadhim, Abdulhadi; Al-Amiery, Ahmed A; Kadhum, Abdul Amir H; Mohamad, Abu Bakar

2014-01-01

Influence of laser treatment on mechanical properties, wear resistance, and Vickers hardness of aluminum alloy was studied. The specimens were treated by using Nd:YaG laser of energy 780 mj, wavelength 512 nm, and duration time 8 ns. The wear behavior of the specimens was studied for all specimens before and after treatment by Nd:YaG laser and the dry wear experiments were carried out by sing pinon-disc technique. The specimens were machined as a disk with diameter of 25 mm and circular groove in depth of 3 mm. All specimens were conducted by scanning electron microscopy (SEM), energy-dispersive X-ray fluorescence analysis (EDS), optical microscopy, and Vickers hardness. The results showed that the dry wear rate was decreased after laser hardening and increased Vickers hardness values by ratio of 2.4:1. The results showed that the values of wear rate for samples having circular grooves are less than samples without grooves after laser treatment.

The effect of surface nanocrystallization on plasma nitriding behaviour of AISI 4140 steel

NASA Astrophysics Data System (ADS)

Li, Yang; Wang, Liang; Zhang, Dandan; Shen, Lie

2010-11-01

A plastic deformation surface layer with nanocrystalline grains was produced on AISI 4140 steel by means of surface mechanical attrition treatment (SMAT). Plasma nitriding of SMAT and un-SMAT AISI 4140 steel was carried out by a low-frequency pulse excited plasma unit. A series of nitriding experiments has been conducted at temperatures ranging from 380 to 500 °C for 8 h in an NH 3 gas. The samples were characterized using X-ray diffraction, scanning electron microscopy, optical microscopy and Vickers microhardness tester. The results showed that a much thicker compound layer with higher hardness was obtained for the SMAT samples when compared with un-SMAT samples after nitriding at the low temperature. In particular, plasma nitriding SMAT AISI 4140 steel at 380 °C for 8 h can produced a compound layer of 2.5 μm thickness with very high hardness on the surface, which is similar to un-SMAT samples were plasma nitrided at approximately 430 °C within the same time.

Microstructure and properties of ceramic coatings prepared by micro-arc oxidation on 7075 aluminum alloy

NASA Astrophysics Data System (ADS)

Cao, G. P.; Song, R. G.

2018-02-01

Micro-arc oxidation (MAO) ceramic coatings were prepared in silicate-based electrolyte on 7075 aluminum alloy. The effects of current density on microstructure and properties of the MAO coatings were studied by scanning electron microscopy (SEM), stereoscopic microscopy, x-ray diffraction (XRD), electrochemical tests as well as tribological and wear tests. The results showed that the current density plays an important role in affecting the quality of the MAO coatings. XRD results showed that the α-Al2O3 phase first increased then decreased with increasing the current density, which matched well with the micro-hardness test and the wearing test results. On the other hand, the coalescent strength measurements revealed that the coating prepared at the current density of 12 A dm-2 is of the highest adhesion force. The potentiodynamic polarization test proved that the coating obtained under 10 A dm-2 exhibits the best corrosion resistance, which is directly related to the morphology of coating.

Synthesis and characterization of aluminium–alumina micro- and nano-composites by spark plasma sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dash, K., E-mail: khushbudash@gmail.com; Chaira, D.; Ray, B.C.

Graphical abstract: The evolution of microstructure by varying the particle size of reinforcement in the matrix employing spark plasma sintering has been demonstrated here in Al–Al{sub 2}O{sub 3} system. An emphasis has been laid on varying the reinforcement particle size and evaluating the microstructural morphologies and their implications on mechanical performance of the composites. Nanocomposites of 0.5, 1, 3, 5, 7 volume % alumina (average size < 50 nm) reinforced in aluminium matrix were fabricated by powder metallurgy route using spark plasma sintering technique technique at a temperature of 773 K and pressure of 50 MPa. Another set of specimensmore » having composition 1, 5, 20 vol.% of alumina (average size ∼ 10 μm) had been fabricated to compare the physical as well as mechanical attributes of the microcomposite as well as the nanocomposites. These micro- and nano-composites have been characterized using X-ray diffraction, scanning electron microscopy and transmission electron microscopy followed by density, microhardness and nanoindentation measurements. The alumina nanoparticles revealed an interface showing appreciable physical intimacy with the aluminium matrix compared to that of the alumina microparticles. The interfacial integrity in case of nanocomposites is better than in the microcomposite which has been studied using microscopic techniques. Spark plasma sintering imparts enhanced densification as well as matrix-reinforcement proximity which has been corroborated with the experimental results. - Highlights: • The Al–Al{sub 2}O{sub 3} micro- and nano-composites fabricated by spark plasma sintering. • Better matrix-reinforcement integrity in nanocomposites than microcomposites. • Spark plasma sintering method results in higher density and hardness values. • High density and hardness values of nanocomposites than microcomposites. • High dislocation density in spark plasma sintered Al–Al{sub 2}O{sub 3} composites. - Abstract: In the present study, an emphasis has been laid on evaluation of the microstructural morphologies and their implications on mechanical performance of the composites by varying the reinforcement particle size. Nanocomposites of 0.5, 1, 3, 5, 7 volume % alumina (average size < 50 nm) and microcomposites of 1, 5, 20 volume % of alumina (average size ∼ 10 μm) reinforced in aluminium matrix were fabricated by spark plasma sintering technique at a temperature of 773 K and pressure of 50 MPa. These micro- and nano-composites have been characterized using X-ray diffraction, scanning electron microscopy and transmission electron microscopy followed by density, microhardness and nanoindentation hardness measurements. The alumina nanoparticles revealed appreciable physical intimacy with the aluminium matrix than that of alumina microparticles. The highest nanohardness recorded 0.85 GPa and 99% densification for 7 and 1 vol.% Al–Al{sub 2}O{sub 3} nancomposites respectively. Spark plasma sintering imparts enhanced densification and matrix-reinforcement proximity which have been corroborated with the experimental results.« less

Analysis of microstructure in electro-spark deposited IN718 superalloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Anisimov, E.; Khan, A.K.; Ojo, O.A., E-mail: olanr

2016-09-15

The microstructure of electro-spark deposited (ESD) superalloy IN718 was studied by the use of scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS) techniques. In converse to general assumption, the extremely high cooling rate involved in the ESD process did not produce partitionless solidification that is devoid of second phase microconstituents in the material, nano-sized Laves phase and MC carbide particles were observed within the deposited layer. Notwithstanding the several thermal cycles involved in the process, the extremely low heat input of the process produced a deposited region that is free ofmore » the main strengthening phase of the alloy, γ″ phase precipitates, which is in contrast to what have been reported on laser deposition. Nevertheless, application of the standard full heat treatment of the alloy resulted in extensive formation of the γ″ phase precipitates and δ phase precipitates, the most stable secondary phase of the alloy, with nearly, if not complete, dissolution of the Laves phase particles. Furthermore, the XPS analysis done in the study revealed the formation of nano-oxides within the deposited layer, which increased the microhardness of the superalloy in the as-deposited condition and inhibited its grain growth during post-process heat treatment. The microstructure analysis done in this work is crucial to the understanding of properties of the superalloy processed by the ESD technique. - Highlights: •Electron microscopy analyses of electro-spark deposited IN 718 superalloy were performed. •Nano-sized secondary phase particles were observed within the deposited layer. •The study shows that the ESD did not produce partitionless solidification of the alloy.« less

Comparison of the Effects of Two Different Drinks on Microhardness of a Silorane-based Composite Resin.

PubMed

Sadat HashemiKamangar, Sedighe; Ghavam, Maryam; Mirkhezri, Zhina; Karazifard, Mohammad Javad

2015-09-01

Acidic foods and drinks can erode composite resins. Silorane-based composite is a new low shrinkage composite with higher hydrophobicity which might resist the erosive effect of beverages. The aim of this study was to determine the effects of 100% orange juice and non-alcoholic carbonated beer on microhardness of a silorane-based composite in comparison with two methacrylate-based composite resins. Ninety disc-shaped composite specimens were fabricated of Filtek P90, Filtek Z350 XT Enamel and Filtek Z250 (3M-ESPE) (n=30) and randomly divided into 3 subgroups of 10.Group 1 was immersed in distilled water, group 2 in 100% orange juice, and group 3 in non-alcoholic beer for 3 h/day. Primary, secondary and final Vickers microhardness tests were performed at the beginning of the study and 7 and 28 days later. Surface of 2 specimens in each group was evaluated under scanning electron microscope on day 28. Data were analyzed using repeated measures of ANOVA model (α=0.05). The primary and secondary microhardness of P90 was significantly lower than that of Z350, and Z250 (p< 0.001). Microhardness of Z350 was also lower than that of Z250 (p= 0.002). On day 28, microhardness of P90 was lower than Z250 and Z350 (p< 0.001); however, microhardness values of Z250 and Z350 were not significantly different (p= 0.054). Microhardness of specimens subjected to non-alcoholic beer was significantly lower than that of controls (p= 0.003). Meanwhile, the microhardness value of resins in orange juice was somewhere between the two mentioned values with no significant difference with any of them (p> 0.05). Although 28 days of immersion in 100% orange juice and non-alcoholic beer decreased the microhardness of all specimens, P90 experienced the greatest reduction of microhardness and non-alcoholic beer had the highest effect on reducing microhardness.

Gradient microstructure and microhardness in a nitrided 18CrNiMo7-6 gear steel

NASA Astrophysics Data System (ADS)

Yang, R.; Wu, G. L.; Zhang, X.; Fu, W. T.; Huang, X.

2017-07-01

A commercial gear steel (18CrNiMo7-6) containing a tempered martensite structure was nitrided using a pressurized gas nitriding process under a pressure of 5 atm at 530 °C for 5 hours. The mechanical properties and microstructure of the nitrided sample were characterized by Vickers hardness measurements, X-ray diffraction, and backscatter electron imaging in a scanning electron microscope. A micro-hardness gradient was identified over a distance of 500 μm with hardness values of 900 HV at the top surface and 300 HV in the core. This micro-hardness gradient corresponds to a gradient in the microstructure that changes from a nitride compound layer at the top surface (∼ 20 μm thick) to a diffusion zone with a decreasing nitrogen concentration and precipitate density with distance from the surface, finally reaching the core matrix layer with a recovered martensite structure.

Mechanical properties, microstructural and thermal evolution of Mg65Ni20Y15-xSix (X = 1, 2, 3) alloys by mechanical alloying

NASA Astrophysics Data System (ADS)

Kursun, Celal; Gogebakan, Musa; Eskalen, Hasan

2018-03-01

We report on a work of the influence of the mechanical alloying on the microstructure, thermal and mechanical features of Mg65Ni20Y15-xSix (X = 1, 2, 3) alloys. The Mg-based alloys were produced by mechanical alloying technique from mixtures of pure crystalline Mg, Ni, Y and Si powders. These alloys were investigated using a variety of analytical techniques including x-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrometry (EDX) and differential scanning calorimetry (DSC). The mechanical properties of the alloys were investigated by Vickers microhardness (HV) tester. After 75 h of milling time, three different intermetallic phases were obtained. These phases were defined as Mg24Y5, Mg2Ni3Si and Mg2Ni by XRD data. The particle and crystallite sizes of the Mg-based alloys were decreased by increasing milling time and they were calculated 2 μm and ˜9 nm, respectively. From the EDX analysis, it was determined that compositional homogeneity of the Mg-based alloys was fairly high. The microhardness values of the Mg65Ni20Y15-xSix (X = 1, 2, 3) alloys increased by increasing Si into the alloys and were determined 101, 131 and 158 HV, respectively.

Preparation and evaluation of cerium oxide-bovine hydroxyapatite composites for biomedical engineering applications.

PubMed

Gunduz, O; Gode, C; Ahmad, Z; Gökçe, H; Yetmez, M; Kalkandelen, C; Sahin, Y M; Oktar, F N

2014-07-01

The fabrication and characterization of bovine hydroxyapatite (BHA) and cerium oxide (CeO2) composites are presented. CeO2 (at varying concentrations 1, 5 and 10wt%) were added to calcinated BHA powder. The resulting mixtures were shaped into green cylindrical samples by powder pressing (350MPa) followed by sintering in air (1000-1300°C for 4h). Density, Vickers microhardness (HV), compression strength, scanning electron microscopy (SEM) and X-ray diffraction (XRD) studies were performed on the products. The sintering behavior, microstructural characteristics and mechanical properties were evaluated. Differences in the sintering temperature (for 1wt% CeO2 composites) between 1200 and 1300°C, show a 3.3% increase in the microhardness (564 and 582.75HV, respectively). Composites prepared at 1300°C demonstrate the greatest compression strength with comparable results for 5 and 10wt% CeO2 content (106 and 107MPa) which are significantly better than those for 1wt% and those that do not include any CeO2 (90 and below 60MPa, respectively). The results obtained suggest optimal parameters to be used in preparation of BHA and CeO2 composites, while also highlighting the potential of such materials in several biomedical engineering applications. Copyright © 2014 Elsevier Ltd. All rights reserved.

The influences of N-acetyl cysteine (NAC) on the cytotoxicity and mechanical properties of Poly-methylmethacrylate (PMMA)-based dental resin

PubMed Central

Jiao, Yang; Ma, Sai; Li, Jing; Shan, Lequn; Yang, Yanwei; Li, Meng

2015-01-01

Objectives. This study aimed to investigate the influences of N-acetyl cysteine (NAC) on cytotoxicity and mechanical properties of Poly-methylmethacrylate (PMMA) dental resins. Methods. Experimental PMMA resin was prepared by incorporating various concentrations of NAC (0, 0.15, 0.3, 0.6 and 0.9 wt.%). MTT assay was performed to investigate viability of human dental pulp cells after exposure to extract of PMMA resin with or without NAC. Cell adhesion on resin specimens was examined with scanning electron microscopy. Degree of conversion was studied with Fourier Transform Infrared Spectroscopy (FTIR). Flexural strength, microhardness and surface roughness was evaluated using a universal testing machine, microhardness tester and optical profilometer, respectively. Results. Incorporation of NAC into PMMA resin significantly reduced its cytotoxicity and enhanced cell adhesion on its surface. NAC induced negative influences on the mechanical and physical properties of PMMA resin in a dose-dependent manner. The degree of conversion for all experimental PMMA resins reached as high as 72% after 24 h of polymerization. All the tested properties were maintained when the concentration of incorporated NAC was 0.15 wt.%. Conclusion. The addition of 0.15 wt.% NAC remarkably improved biocompatibility of PMMA resin without exerting significant negative influence on its mechanical and physical properties. PMID:25922788

Microstructure Characterization and Corrosion Properties of Nitrocarburized AISI 4140 Low Alloy Steel

NASA Astrophysics Data System (ADS)

Fattah, M.; Mahboubi, F.

2012-04-01

Plasma nitrocarburizing treatments of AISI 4140 low alloy steel have been carried out in a gas mixture of 85% N2-12% H2-3% CO2. All treatments were performed for 5 h at a chamber pressure of 4 mbar. Different treatment temperatures varying from 520 to 620 °C have been used to investigate the effect of treatment temperature on the corrosion and hardness properties and also microstructure of the plasma nitrocarburized steel. Scanning electron and optical microscopy, x-ray diffraction, microhardness measurement, and potentiodynamic polarization technique in 3.5% NaCl solution were used to study the treated surfaces. The results revealed that plasma nitrocarburizing at temperatures below 570 °C can readily produce a monophase ɛ compound layer. The compound layer formed at 620 °C is composed of two sub-layers and is supported by an austenite zone followed by the diffusion layer. The thickest diffusion layer was related to the sample treated at 620 °C. Microhardness results showed a reduction of surface hardness with increasing the treatment temperature from 520 to 620 °C. It has also been found that with increasing treatment temperature from 520 to 545 °C the corrosion resistance increases up to a maximum and then decreases with further increasing treatment temperature from 545 to 620 °C.

In vitro study of the effects of fluoride-releasing dental materials on remineralization in an enamel erosion model.

PubMed

Zhou, San Ling; Zhou, Jun; Watanabe, Shigeru; Watanabe, Koji; Wen, Ling Ying; Xuan, Kun

2012-03-01

This study was conducted to compare the remineralization effects of five regimens on the loss of fluorescence intensity, surface microhardness, roughness and microstructure of bovine enamel after remineralization. We hope that these results can provide some basis for the clinical application of these materials. One hundred bovine incisors were prepared and divided into the following five groups, which were treated with distinct dental materials: (1) Clinpro™ XT varnish (CV), (2) F-varnish (FV), (3) Tooth Mousse (TM), (4) Fuji III LC(®) light-cured glass ionomer pit and fissure sealant (FJ) and (5) Base Cement(®) glass polyalkenoate cement (BC). Subsequently, they were detected using four different methods: quantitative light-induced fluorescence, microhardness, surface 3D topography and scanning electron microscopy (SEM). The loss of fluorescence intensity of CV, BC and FJ groups showed significant decreases after remineralization (p<0.05). The microhardness values of the BC group were significantly higher than those of the other groups (p<0.05) after 6 weeks of remineralization. The CV group's surface roughness was significantly lower than those of the other groups after 6 weeks of remineralization (p<0.05). Regarding microstructure values, the FV group showed many round particles deposited in the bovine enamel after remineralization. However, the other four groups mainly showed needle-like crystals. Glass ionomer cement (GIC)-based dental materials can promote more remineralization of the artificial enamel lesions than can NaF-based dental materials. Resin-modified GIC materials (e.g., CV and FJ) have the potential for more controlled and sustained release of remineralized agents. The effect of TM requires further study. Crown Copyright © 2011. Published by Elsevier Ltd. All rights reserved.

Effect of bismuth oxide on white mineral trioxide aggregate: chemical characterization and physical properties.

PubMed

Grazziotin-Soares, R; Nekoofar, M H; Davies, T E; Bafail, A; Alhaddar, E; Hübler, R; Busato, A L S; Dummer, P M H

2014-06-01

To assess the effect of bismuth oxide (Bi2 O3 ) on the chemical characterization and physical properties of White mineral trioxide aggregate (MTA) Angelus. Commercially available White MTA Angelus and White MTA Angelus without Bi2 O3 provided by the manufacturer especially for this study were subjected to the following tests: Rietveld X-ray diffraction analysis (XRD), energy-dispersive X-ray analysis (EDX), scanning electron microscopy (SEM), compressive strength, Vickers microhardness test and setting time. Chemical analysis data were reported descriptively, and physical properties were expressed as means and standard deviations. Data were analysed using Student's t-test and Mann-Whitney U test (P = 0.05). Calcium silicate peaks were reduced in the diffractograms of both hydrated materials. Bismuth particles were found on the surface of White MTA Angelus, and a greater amount of particles characterized as calcium hydroxide was observed by visual examination on White MTA without Bi2 O3 . The material without Bi2 O3 had the shortest final setting time (38.33 min, P = 0.002), the highest Vickers microhardness mean value (72.35 MPa, P = 0.000) and similar compressive strength results (P = 0.329) when compared with the commercially available White MTA Angelus containing Bi2 O3 . The lack of Bi2 O3 was associated with an increase in Vickers microhardness, a reduction in final setting time, absence of Bi2 O3 peaks in diffractograms, as well as a large amount of calcium and a morphology characteristic of calcium hydroxide in EDX/SEM analysis. © 2013 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Mechanical properties of cobalt-chromium 3-unit fixed dental prostheses fabricated by casting, milling, and additive manufacturing.

PubMed

Øilo, Marit; Nesse, Harald; Lundberg, Odd Johan; Gjerdet, Nils Roar

2018-04-25

New additive manufacturing techniques for nonprecious alloys have made the fabrication of metal-ceramic fixed partial dentures (FPDs) less expensive and less time-consuming. However, whether the mechanical properties produced by these techniques are comparable is unclear. The purpose of this in vitro study was to evaluate the mechanical properties of cobalt-chromium frameworks for FPDs fabricated by 3 different techniques. Thirty frameworks for 3-unit FPDs were fabricated by traditional casting, computer-aided design and computer-aided manufacturing (CAD-CAM) milling, and selective laser melting (SLM), with n=10 in each group. The frameworks were weighed, and distal and mesial connector areas measured. The frameworks were cemented and loaded centrally (0.5 mm/s) until deformation above 1 mm occurred. Stiffness was measured as the slope of the axis between 500 and 2000 N. Microhardness was measured on sectioned specimens by Vickers indentation. The microstructure was also analyzed by scanning electron microscopy. One-way ANOVA with Tukey post hoc analysis was used to compare the groups (α=.05). The framework design differed among the groups, making a comparison of strength impossible. The milled frameworks appeared bulky, while the cast and SLM frameworks were more slender. Statistically significant differences were found in microhardness, stiffness, wall thickness, weight, and connector size (P<.05), and a significant correlation was found between hardness and stiffness (-0.4, P<.005). Fabrication method affects the design, stiffness, microhardness, and microstructure of cobalt-chromium FPD frameworks. The SLM frameworks were stiffer and harder than the cast and milled specimens. Copyright © 2018 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Nano and micro mechanical properties of uncross-linked and cross-linked chitosan films

PubMed Central

Aryaei, Ashkan; Jayatissa, Ahalapitiya H.; Jayasuriya, A. Champa

2016-01-01

The aim of this study is to determine the nano and micro mechanical properties for uncross-linked and cross-linked chitosan films. Specifically, we looked at nanoindentation hardness, microhardness, and elastic modulus. It is important to study the nano and microscale mechanical properties of chitosan since chitosan has been widely used for biomedical applications. Using the solvent-cast method, the chitosan films were prepared at room temperature on the cleaned glass plates. The chitosan solution was prepared by dissolving chitosan in acetic acid 1% (v/v). Tripolyphosphate (TPP) was used to create the cross-links between amine groups in chitosan and phosphate groups in TPP. In this study, atomic force microscopy was used to measure the nanoindentation hardness and surface topography of the uncross-linked and cross-linked chitosan films. Elastic modulus was then calculated from the nanoindentation results. The effective elastic modulus was determined by microhardness with some modifications to previous theories. The microhardness of the chitosan films were measured using Vicker’s hardness meter under three different loads. Our results show that the microhardness and elastic modulus for cross-linked chitosan films are higher than the uncross-linked films. However, the cross-linked chitosan films show increased brittleness when compared to uncross-linked films. By increasing the load magnitude, the microhardness increases for both uncross-linked and cross-linked chitosan films. PMID:22100082

Microstructural evolution and thermal stability of Fe-Zr metastable alloys developed by mechanical alloying followed by annealing

NASA Astrophysics Data System (ADS)

Sooraj, S.; Muthaiah, V. M. Suntharavel; Kang, P. C.; Koch, Carl C.; Mula, Suhrit

2016-09-01

The effect of Zr (up to 1 at.%) addition on the formation of Fe-Zr metastable alloys and their thermal stability were investigated for their possible nuclear applications. Fe-xZr (x = 0.25, 0.5, 1%) alloys were synthesised by mechanical alloying under a high-purity argon atmosphere using stainless steel grinding media in a SPEX 8000M high energy mill. The milling was conducted for 20 h with a ball-to-powder weight ratio of 10:1. The formation of metastable solid solutions after milling was confirmed from the change in the Gibbs free energy analysis as per Miedema's model. The microstructural characterisation was carried out by analysis of X-ray diffraction, atomic force microscopy and transmission electron microscopy. The effect of Zr on the thermal stability of Fe-Zr alloys was investigated by extensive annealing experiments followed by microstructural analysis and microhardness measurements. The stabilisation was found to occur at 800 °C and thereafter, no significant change in the crystallite size was observed for the samples annealed between 800 and 1200 °C. The supersaturated solid solution, especially 1% Zr alloy, found to be highly stable up to 800 °C and the microhardness value of the same measured to be as high as 8.8 GPa corresponding to a crystallite size of 57 nm. The stabilisation effect has been discussed in the light of both the thermodynamic and kinetic mechanisms and the grain size stabilisation is attributed to the grain boundary segregation of Zr atoms and/or Zener pinning by nanoscale precipitation of the Fe2Zr phase.

Effects of fluoride and epigallocatechin gallate on soft-drink-induced dental erosion of enamel and root dentin.

PubMed

Wang, Yin-Lin; Chang, Hao-Hueng; Chiang, Yu-Chih; Lu, Yu-Chen; Lin, Chun-Pin

2018-04-01

Fluoride and epigallocatechin gallate (EGCG) have been proven to prevent dental caries. The purpose of this study was to evaluate the effects of fluoride and EGCG on soft-drink-induced dental erosion in vitro. Forty enamel and dentin specimens were prepared from extracted human teeth. The specimens were divided into 4 groups and treated separately with distilled water (as control), 0.5 M sodium fluoride (NF), 400 μM EGCG (EG), and a solution containing 0.5 M NaF and 400 μM EGCG (FG). Cyclic erosive treatment was performed according to the experimental procedures. The specimens were analyzed using laser scanning confocal microscopy, scanning electron microscopy, and a microhardness tester. The data were analyzed using ANOVA and Bonferroni's post hoc test. The significance level was set at 5%. The amount of substance loss was lower in the NF and EG groups than in the control group (p < 0.05). The erosion-caused substance loss was more pronounced in the dentin than in the enamel specimens. Surface microhardness loss was lower in the NF and EG groups than in the control group (p < 0.05). The diameter of the dentinal tubule was wider in the control group than in the NF and EG groups (p < 0.05). No combined effects were observed in the FG group. Both fluoride and EGCG are effective in preventing soft-drink-induced erosion compared with the control group. Fluoride and EGCG may interfere with each other. The mechanisms of the anti-erosive effect need to be explored in the future. Copyright © 2018. Published by Elsevier B.V.

Effect of intra-oral aging on t→m phase transformation, microstructure, and mechanical properties of Y-TZP dental ceramics.

PubMed

Miragaya, Luciana Meireles; Guimarães, Renato Bastos; Souza, Rodrigo Othávio de Assunção E; Santos Botelho, Glauco Dos; Antunes Guimarães, José Guilherme; da Silva, Eduardo Moreira

2017-08-01

The aim of the present study was to evaluate the influence of intra-oral aging on the tetragonal-to-monoclinic (t→m) phase transformation of two Y-TZP dental ceramics - Lava Frame (Frame) and Lava Plus (Plus) - and determine the impact of this response on their microstructures and mechanical properties: flexural strength, Young's modulus, microhardness and fracture toughness. Standardized ceramic specimens were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). After the baseline analysis, the specimens were attached to personalized intra-oral resin appliances and exposed to the oral cavity of 20 subjects for 60 days and then analyzed again. Specimens produced for mechanical properties evaluation were also analyzed before and after the 60-day intra-oral aging. The data were analyzed using two-way ANOVA and Tukey HSD's post hoc test (α=0.05). Weibull analysis was used to evaluate the strength reliability. Both Y-TZP ceramics suffered t→m phase transformation after 60-day intra-oral aging (Plus=4.7%/Frame=7.7%). SEM and AFM analyses showed dislodgement of ZrO 2 grains and a significant increase in roughness after intra-oral aging for both ceramics. Both Y-TZP ceramics suffered a decrease on flexural strength, Young's modulus and fracture toughness after intra-oral aging (p<0.05). Only Plus presented a decrease of microhardness after intra-oral aging (p<0.05). Intra-oral aging for 60 days produced t→m phase transformation, changed the microstructure and decreased the mechanical properties of two Y-TZP dental ceramics. Copyright © 2017 Elsevier Ltd. All rights reserved.

Microstructure evolution in dissimilar AA6060/copper friction stir welded joints

NASA Astrophysics Data System (ADS)

Kalashnikova, T. A.; Shvedov, M. A.; Vasilyev, P. A.

2017-12-01

Friction stir welding process has been applied for making a dissimilar copper/aluminum alloy joint. The grain microstructure and mechanical properties of the obtained joint were studied. The structure of the cross-section of the FSW compound was analyzed. The microstructural evolution of the joint was examined using optical microscopy. The mechanical properties of the intermetallic particles were evaluated by measuring the microhardness according to the Vickers method. The microhardness of the intermetallic particles was by a factor of 4 lower than that of the particles obtained by fusion welding. The results of the investigations enable using friction stir welding for making dissimilar joints.

Synthesis and properties of nanocrystalline Bi-Te based thermoelectric materials for energy application

NASA Astrophysics Data System (ADS)

Almohaimeed, Sulaiman

Thermoelectric phenomenon is the science associated with converting thermal energy into electricity based on the Seebeck effect. Bismuth telluride Bi 2Te3 is currently considered to be the state-of-the art thermoelectric material with high efficiency for low temperature applications and is therefore attractive for energy harvesting processes. Nanostructures thermoelectric materials provide a novel way to enhance thermoelectric properties and are considered to be the efficient building blocks for thermoelectric devices. In this work, n- and p-type bulk nanocrystalline Bismuth telluride thermoelectric materials were prepared by mechanical alloying / ball milling technique. The produced nano-crystalline powder were then consolidated using hot compaction under inert atmosphere. The novel processing of these materials maintained the nanostructure in both n- and p-type. Structural properties of the n- and p-types were characterized using X ray diffraction, scanning electron microscopy and transmission electron microscope. These techniques proved that the average grian size of the milled thermoelectric materials was about 20 nm. Accordingly, a Significant improvement in the figure of merit (ZT) is achieved through significant lattice thermal conductivity reduction and Seebeck coefficient improvement. The maximum ZT value for the n-type nanocrystalline thermoelectric was 1.67 at 373 K while the maximum ZT value for the p-type was 1.78 at the same temperature. These values are considered to be the highest values reported for similar materials. Evaluation of the mechanical properties was also performed through microhardness measurement using Vickers micro-hardness test, which shows an enhancement in mechanical properties for the produced materials.

Laser shock processing effects on isothermal oxidation resistance of GH586 superalloy

NASA Astrophysics Data System (ADS)

Hua, Yinqun; Rong, Zhen; Ye, Yunxia; Chen, Kangmin; Chen, Ruifang; Xue, Qing; Liu, Haixia

2015-03-01

The oxidation is one of the main failure mode of Ni-based alloy at high temperature, laser shock processing not only can improve the mechanical properties but also the oxidation resistance. So the study on laser shock processing effects on oxidation resistance of this alloy is necessary. The aim of this paper is to investigate the effects of laser shock processing on microstructure, micro-hardness and isothermal oxidation resistance of GH586 superalloy. Scanning electron microscopy, energy-dispersive spectrum, transmission electron microscope, and X-ray diffraction technique were used to analyze the microstructure changes and the surface morphologies of the oxide scales. In addition, micro-hardness of LSP-treated samples was measured. The results show that the average grains size on the surfaces of LSP specimen was found to be significantly finer compared to the untreated one (33.3 μm vs. 18.5 μm). Highly tangled and dense dislocation arrangements and a high amount of twins have been observed. After the oxidation, the defects density (dislocations and twins) in the specimen decreased. The oxidation kinetics approximately followed a parabolic oxidation law at 800 °C and 900 °C. The oxidation layer was composed of Cr2O3, NiCr2O4, TiO2, and Al2O3, which generated more quickly on the surface treated by LSP during initial oxidation. The average oxidation rate was lower after LSP due to the dense, tiny and homogeneous oxidation layer. The results show that the specimens treated by LSP have a better high temperature oxidation resistance.

High-compactness coating grown by plasma electrolytic oxidation on AZ31 magnesium alloy in the solution of silicate-borax

NASA Astrophysics Data System (ADS)

Shen, M. J.; Wang, X. J.; Zhang, M. F.

2012-10-01

A ceramic coating was formed on the surface of AZ31 magnesium alloy by plasma electrolytic oxidation (PEO) in the silicate solution with and without borax doped. The composition, morphology, elements and roughness as well as mechanical property of the coating were investigated by X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive X-ray spectrometry (EDS), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and reciprocal-sliding tribometer. The results show that the PEO coating is mainly composed of magnesia. When using borax dope, boron element is permeating into the coating and the boron containing phase exist in the form of amorphous. In addition, the microhardness and compactness of the PEO coating are improved significantly due to doped borax.

The effect of aluminum nanoparticles on the structure, mechanical properties and failure of aluminum processed by accumulative roll bonding

NASA Astrophysics Data System (ADS)

Ivanov, K. V.; Fortuna, S. V.; Kalashnikova, T. A.; Rodkevich, N. G.

2017-12-01

The microstructure, mechanical properties, and fracture type of aluminum with and without aluminum nanoparticles processed by accumulative roll bonding (ARB) have been studied using transmission and scanning electron microscopy, microhardness measurements, and tensile tests. It is shown that the injection of aluminum nanoparticles increases the structure refinement rate during ARB due to the increasing tendency for dynamic recrystallization. It has a different effect on different mechanical characteristics. The different effect of nanoparticles on different structural features is the reason for the different effect on different mechanical properties related with these features. The fracture mechanism is shown to change from ductile in aluminum to mixed ductile-brittle in the composite with a 1.5-fold decrease in ductility as a result of nanoparticle injection.

Microstructure characterization of the stir zone of submerged friction stir processed aluminum alloy 2219

DOE Office of Scientific and Technical Information (OSTI.GOV)

Feng, Xiuli, E-mail: feng.97@osu.edu; State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001; Liu, Huijie, E-mail: liuhj@hit.edu.cn

Aluminum alloy 2219-T6 was friction stir processed using a novel submerged processing technique to facilitate cooling. Processing was conducted at a constant tool traverse speed of 200 mm/min and spindle rotation speeds in the range from 600 to 800 rpm. The microstructural characteristics of the base metal and processed zone, including grain structure and precipitation behavior, were studied using optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Microhardness maps were constructed on polished cross sections of as-processed samples. The effect of tool rotation speed on the microstructure and hardness of the stir zone was investigated. Themore » average grain size of the stir zone was much smaller than that of the base metal, but the hardness was also lower due to the formation of equilibrium θ precipitates from the base metal θ′ precipitates. Stir zone hardness was found to decrease with increasing rotation speed (heat input). The effect of processing conditions on strength (hardness) was rationalized based on the competition between grain refinement strengthening and softening due to precipitate overaging. - Highlights: • SZ grain size (∼ 1 μm) is reduced by over one order of magnitude relative to the BM. • Hardness in the SZ is lower than that of the precipitation strengthened BM. • Metastable θ′ in the base metal transforms to equilibrium θ in the stir zone. • Softening in the SZ results from a decrease of precipitation strengthening.« less

Carbon Nanotube-Reinforced Aluminum Matrix Composites Produced by High-Energy Ball Milling

NASA Astrophysics Data System (ADS)

Travessa, Dilermando N.; da Rocha, Geovana V. B.; Cardoso, Kátia R.; Lieblich, Marcela

2017-05-01

Although multiwall carbon nanotubes (MWCNT) are promising materials to strengthen lightweight aluminum matrix composites, their dispersion into the metallic matrix is challenge. In the present work, MWCNT were dispersed into age-hardenable AA6061 aluminum alloy by high-energy ball milling and the blend was subsequently hot-extruded. The composite bars obtained were heat-treated by solution heat treatment at 520 °C and artificially aged at 177 °C for 8 h, in order to reach the T6 temper. Special attention was given to the integrity of the MWCNT along the entire composite production. The microstructure of the obtained bars was evaluated by optical and scanning electron microscopy, and the mechanical properties were evaluated by Vickers microhardness tests. Raman spectroscopy, x-ray diffraction and transmission electron microscopy were employed to evaluate the structural integrity of MWCNT. It was found that milling time is critical to reach a proper dispersion of the reinforcing phase. The composite hardness increased up to 67% with the dispersion of 2% in weight of MWCNT, when comparing with un-reinforced bars produced by similar route. However, age hardening was not observed in composite bars after heat treatment. It was also found that MWCNT continuously degraded along the process, being partially converted into Al4C3 in the final composite.

Dental glass ionomer cement reinforced by cellulose microfibers and cellulose nanocrystals.

PubMed

Silva, Rafael M; Pereira, Fabiano V; Mota, Felipe A P; Watanabe, Evandro; Soares, Suelleng M C S; Santos, Maria Helena

2016-01-01

The aim of this work was to evaluate if the addition of cellulose microfibers (CmF) or cellulose nanocrystals (CNC) would improve the mechanical properties of a commercial dental glass ionomer cement (GIC). Different amounts of CmF and CNC were previously prepared and then added to reinforce the GIC matrix while it was being manipulated. Test specimens with various concentrations of CmF or CNC in their total masses were fabricated and submitted to mechanical tests (to evaluate their compressive and diametral tensile strength,modulus, surface microhardness and wear resistance) and characterized by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FTIR). The incorporation of CmF in the GIC matrix did not greatly improve the mechanical properties of GIC. However, the addition of a small amount of CNC in the GIC led to significant improvements in all of the mechanical properties evaluated: compressive strength (increased up to 110% compared with the control group), elastic modulus increased by 161%, diametral tensile strength increased by 53%, and the mass loss decreased from 10.95 to 3.87%. Because the composites presented a considerable increase in mechanical properties, the modification of the conventional GIC with CNC can represent a new and promising dental restorative material.

The effect of incorporated self-lubricated BN(h) particles on the tribological properties of Ni-P/BN(h) composite coatings

NASA Astrophysics Data System (ADS)

Hsu, Chih-I.; Hou, Kung-Hsu; Ger, Ming-Der; Wang, Gao-Liang

2015-12-01

Ni-P/BN(h) composite coatings are prepared by means of the conventional electroless plating from the bath containing up to 10.0 g/l of hexagonal boron nitride particles with size 0.5 μm. The Ni-P coating is also prepared as a comparison. Cationic surfactant cetyltrimethylammonium bromide (CTAB) is used to stabilize the electrolyte, and the optimum CTAB concentration resulting in a nonagglomerated dispersion of particles is obtained using a dispersion stability analyzer. Morphology of the coatings and the effect of incorporated particles on coating structure and composition are investigated via scanning electron microscopy, field emission electron probe micro-analyzer and X-ray diffraction analysis. Hardness, roughness, friction coefficient and wear resistance of the coatings are also evaluated using Vickers microhardness tester, atomic force microscopy and ball-on disk machine. The presence of CTAB in the depositing bath has a positive effect on the surface roughness and performance of Ni-P/BN(h) composite coatings. The friction and wear tests results show that incorporation of 14.5 vol% BN(h) particles into the Ni-P coating lowers the coating friction coefficient by about 75% and the wear resistance of the Ni-P composites is approximately 10 times higher than Ni-P coating.

Microstructural evolution and sliding wear studies of copper-alumina micro- and nano-composites fabricated by spark plasma sintering

NASA Astrophysics Data System (ADS)

Dash, Khushbu; Chaira, Debasis; Ray, Bankim Chandra

2015-05-01

Copper-alumina nanocomposites of 0.5, 1, 3, 5, 7 vol.% alumina (average size <50 nm) reinforced in copper matrix were fabricated using spark plasma sintering (SPS) technique. Another set of microcomposites containing 1, 5, 20 vol.% of alumina (average size ˜10 μm) had been fabricated to compare the physical as well as mechanical attributes of composites with variation of reinforcement particle size. These micro- and nano-composites have been characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS), transmission electron microscopy (TEM) followed by microhardness, nanoindentation hardness, and wear measurements. It has been found that hardness values are higher for nanocomposites as compared to microcomposites. It is also found that wear resistance increases with increasing alumina content. The microcomposites show better wear resistance than nanocomposites for the same composition. The interaction of copper and alumina results in the formation of CuAlO2 which manifests differential interfacial phenomenon. We have obtained 95.82% densification and 93.17 HV hardness for spark plasma sintered Cu-20 vol.% Al2O3 microcomposite. The wear rate is appreciably low, that is, 0.86×10-4 mm3N-1m-1 for 20 vol.% alumina reinforced copper microcomposite.

Microstructure and Texture Evolutions of Biomedical Ti-13Nb-13Zr Alloy Processed by Hydrostatic Extrusion

NASA Astrophysics Data System (ADS)

Ozaltin, K.; Panigrahi, A.; Chrominski, W.; Bulutsuz, A. G.; Kulczyk, M.; Zehetbauer, M. J.; Lewandowska, M.

2017-11-01

A biomedical β-type Ti-13Nb-13Zr (TNZ) (wt pct) ternary alloy was subjected to severe plastic deformation by means of hydrostatic extrusion (HE) at room temperature without intermediate annealing. Its effect on microstructure, mechanical properties, phase transformations, and texture was investigated by light and electron microscopy, mechanical tests (Vickers microhardness and tensile tests), and XRD analysis. Microstructural investigations by light microscope and transmission electron microscope showed that, after HE, significant grain refinement took place, also reaching high dislocation densities. Increases in strength up to 50 pct occurred, although the elongation to fracture left after HE was almost 9 pct. Furthermore, Young's modulus of HE-processed samples showed slightly lower values than the initial state due to texture. Such mechanical properties combined with lower Young's modulus are favorable for medical applications. Phase transformation analyses demonstrated that both initial and extruded samples consist of α' and β phases but that the phase fraction of α' was slightly higher after two stages of HE.

Development of Cu Reinforced SiC Particulate Composites

NASA Astrophysics Data System (ADS)

Singh, Harshpreet; Kumar, Lailesh; Nasimul Alam, Syed

2015-02-01

This paper presents the results of Cu-SiCp composites developed by powder metallurgy route and an attempt has been made to make a comparison between the composites developed by using unmilled Cu powder and milled Cu powder. SiC particles as reinforcement was blended with unmilled and as-milled Cu powderwith reinforcement contents of 10, 20, 30, 40 vol. % by powder metallurgy route. The mechanical properties of pure Cu and the composites developed were studied after sintering at 900°C for 1 h. Density of the sintered composites were found out based on the Archimedes' principle. X-ray diffraction of all the composites was done in order to determine the various phases in the composites. Scanning electron microscopy (SEM) and EDS (electron diffraction x-ray spectroscopy) was carried out for the microstructural analysis of the composites. Vickers microhardness tester was used to find out the hardness of the samples. Wear properties of the developed composites were also studied.

Comparative abrasive wear resistance and surface analysis of dental resin-based materials

PubMed Central

Nayyer, Maleeha; Zahid, Shahreen; Hassan, Syed Hammad; Mian, Salman Aziz; Mehmood, Sana; Khan, Haroon Ahmed; Kaleem, Muhammad; Zafar, Muhammad Sohail; Khan, Abdul Samad

2018-01-01

Objective: The objective of this study was to assess the surface properties (microhardness and wear resistance) of various composites and compomer materials. In addition, the methodologies used for assessing wear resistance were compared. Materials and Methods: This study was conducted using restorative material (Filtek Z250, Filtek Z350, QuiXfil, SureFil SDR, and Dyract XP) to assess wear resistance. A custom-made toothbrush simulator was employed for wear testing. Before and after wear resistance, structural, surface, and physical properties were assessed using various techniques. Results: Structural changes and mass loss were observed after treatment, whereas no significant difference in terms of microhardness was observed. The correlation between atomic force microscopy (AFM) and profilometer and between wear resistance and filler volume was highly significant. The correlation between wear resistance and microhardness were insignificant. Conclusions: The AFM presented higher precision compared to optical profilometers at a nanoscale level, but both methods can be used in tandem for a more detailed and precise roughness analysis. PMID:29657526

Modification of the sample's surface of hypereutectic silumin by pulsed electron beam

NASA Astrophysics Data System (ADS)

Rygina, M. E.; Ivanov, Yu F.; Lasconev, A. P.; Teresov, A. D.; Cherenda, N. N.; Uglov, V. V.; Petricova, E. A.; Astashinskay, M. V.

2016-04-01

The article presents the results of the analysis of the elemental and phase composition, defect substructures. It demonstrates strength and tribological characteristics of the aluminium-silicon alloy of the hypereutectic composition in the cast state and after irradiation with a high-intensity pulsed electron beam of a submillisecond exposure duration (a Solo installation, Institute of High Current Electrons of the Siberian Branch of the Russian Academy of Sciences). The research has been conducted using optical and scanning electron microscopy, and the X-ray phase analysis. Mechanical properties have been characterized by microhardness, tribological properties - by wear resistance and the friction coefficient value. Irradiation of silumin with the high-intensity pulsed electron beam has led to the modification of the surface layer up to 1000 microns thick. The surface layer with the thickness of up to 100 microns is characterized by melting of all phases present in the alloy; subsequent highspeed crystallization leads to the formation of a submicro- and nanocrystalline structure in this layer. The hardness of the modified layer decreases with the increasing distance from the surface exposure. The hardness of the surface layer is more than twice the hardness of cast silumin. Durability of silumin treated with a high intensity electron beam is ≈ 1, 2 times as much as the wear resistance of the cast material.

[Effect of resin infiltration on microhardness of artificial caries lesions].

PubMed

Liu, Yonghong; Deng, Hui; Tang, Longmei; Zhang, Zhiyong

2015-12-01

To compare the changes of enamel surface and cross-sectional microhardness of artificial caries immediately and after the twice demineralization through coating resin infiltration, fluoride varnish and fissure sealant. A total of forty bovine lower incisors enamel samples with artificial caries lesions by the demineralization liquid were used in the experiment. The specimens were then randomly divided into four groups as group A(resin infiltration), B(fluoride varnish), C (fissure sealant), D(control), 10 specimens in each group. The samples were sectioned vertically into two halves through the centre. One half of each sample the surface and cross-sectional microhardness was measured. The other half was put into demineralization liquid for 14 days, then the surface and cross-sectional microhardness was measured again. The cross section morphology of the samples was observed by scanning electron microscope. The surface of enamel had the highest microhardness value, and with the increase of cross- sectional depth, the microhardness value declined gradually. Variance analysis showed that the difference was statistically significant in the cross-section of different depth among the four groups(P<0.05). The microhardness values of the surface and the cross- section at 40 µm of each group in immediate measure showed the values were significantly higher in group A, B and C than in group D. There was no significant difference in the microhardness value of cross-section at 80 µm between group A[(324 ± 17) kg/mm(2)] and group C[(316 ± 20) kg/mm(2)], but they were significantly higher than group D. There was no significant difference between group B[(303 ± 13) kg/mm(2)] and group D[(294 ± 23) kg/mm(2)]. At 120 µm level, the microhardness value of group A was significantly higher than those of the other three groups. After the twice demineralization, the enamel surface microhardness value of the specimens was the same as the first measurement. In the cross-section at 40 µm level, the microhardness value was equal to the value of cross-section at 80 µm level of the first measurement. In the cross- section at 80 µm and 120 µm level, the microhardness value of group A was significantly higher than those of the other three groups. Resin infiltration can effectively strengthen microhardness of enamel surface and cross-section of different depth of artificial caries.

Enhancement of the Wear Resistance and Microhardness of Aluminum Alloy by Nd:YaG Laser Treatment

PubMed Central

Hussein, Haitham T.; Kadhim, Abdulhadi; Al-Amiery, Ahmed A.; Kadhum, Abdul Amir H.; Mohamad, Abu Bakar

2014-01-01

Influence of laser treatment on mechanical properties, wear resistance, and Vickers hardness of aluminum alloy was studied. The specimens were treated by using Nd:YaG laser of energy 780 mj, wavelength 512 nm, and duration time 8 ns. The wear behavior of the specimens was studied for all specimens before and after treatment by Nd:YaG laser and the dry wear experiments were carried out by sing pinon-disc technique. The specimens were machined as a disk with diameter of 25 mm and circular groove in depth of 3 mm. All specimens were conducted by scanning electron microscopy (SEM), energy-dispersive X-ray florescence analysis (EDS), optical microscopy, and Vickers hardness. The results showed that the dry wear rate was decreased after laser hardening and increased Vickers hardness values by ratio of 2.4 : 1. The results showed that the values of wear rate for samples having circular grooves are less than samples without grooves after laser treatment. PMID:25136694

Microstructure and Properties of Fe3Al-Fe3AlC x Composite Prepared by Reactive Liquid Processing

NASA Astrophysics Data System (ADS)

Verona, Maria Nalu; Setti, Dalmarino; Paredes, Ramón Sigifredo Cortés

2018-04-01

A Fe3Al-Fe3AlC x composite was prepared using reactive liquid processing (RLP) through controlled mixture of carbon steel and aluminum in the liquid state. The microstructure and phases of the composite were assessed using X-ray diffraction, scanning electron microscopy, energy-dispersive X-ray spectroscopy, optical microscopy, and differential scanning calorimetry. In addition, the density, hardness, microhardness, and elastic modulus were evaluated. The Fe3Al-Fe3AlC x composite consisted of 65 vol pct Fe3Al and 35 vol pct Fe3AlC x ( κ). The κ phase contained 10.62 at. pct C, resulting in the stoichiometry Fe3AlC0.475. The elastic modulus of the Fe3Al-Fe3AlC0.475 composite followed the rule of mixtures. The RLP technique was shown to be capable of producing Fe3Al-Fe3AlC0.475 with a microstructure and properties similar to those achieved using other processing techniques reported in the literature.

Microstructure and Mechanical Properties of Laves Phase-strengthened Fe-Cr-Zr Alloys

DOE PAGES

Tan, Lizhen; Yang, Ying

2014-12-05

Laves phase-reinforced alloys have shown some preliminary promising performance at room temperatures. This paper aims at evaluating mechanical properties of Laves phase-strengthened alloys at elevated temperatures. Three Fe-Cr-Zr alloys were designed to favor the formation of eutectic microstructures containing Laves and body-centered cubic phases with the aid of thermodynamic calculations. Microstructural characterization was carried out on the alloys in as-processed and aged states using optical microscopy, scanning electron microscopy, energy-dispersive X-ray spectroscopy, and X-ray diffraction. The effect of thermal aging and alloy composition on microstructure has been discussed based on microstructural characterization results. Mechanical properties have been evaluated by meansmore » of Vickers microhardness measurements, tensile testing at temperatures up to 973.15 K (700.15 °C), and creep testing at 873.15 K (600.15 °C) and 260 MPa. Alloys close to the eutectic composition show significantly superior strength and creep resistance compared to P92. Finally, however, their low tensile ductility may limit their applications at relatively low temperatures.« less

Study of twin-roll cast Aluminium alloys subjected to severe plastic deformation by equal channel angular pressing

NASA Astrophysics Data System (ADS)

Poková, M.; Cieslar, M.

2014-08-01

Aluminium alloys prepared by twin-roll casting method become widely used in industry applications. Their high solid solution supersaturation and finer grains ensure better mechanical properties when compared with the direct-chill cast ones. One of the possibilities how to enhance their thermal stability is the addition of zirconium. After heat treatment Al3Zr precipitates form and these pin moving grain boundaries when the material is exposed to higher temperatures. In the present work twin-roll cast aluminium alloys based on AA3003 with and without Zr addition were annealed for 8 hours at 450 °C to enable precipitation of Al3Zr phase. Afterwards they were subjected to severe plastic deformation by equal channel angular pressing, which led to the reduction of average grain size under 1 μm. During subsequent isochronal annealing recovery and recrystallization took place. These processes were monitored by microhardness measurements, light optical microscopy and in-situ transmission electron microscopy. The addition of Zr stabilizes the grain size and increases the recrystallization temperature by 100 °C.

Effect of the content of B4C on microstructural evolution and wear behaviors of the laser-clad coatings fabricated on Ti6Al4V

NASA Astrophysics Data System (ADS)

Bai, L. L.; Li, J.; Chen, J. L.; Song, R.; Shao, J. Z.; Qu, C. C.

2016-01-01

TiNi/Ti2Ni-based composite coatings reinforced by TiC and TiB2 were produced on Ti6Al4V by laser cladding the mixture of a Ni-based alloy and different contents of B4C (0 wt%, 5 wt%, 15 wt%, and 25 wt%). The macromorphologies and microstructures of the coatings were examined through optical microscopy, X-ray diffractometry, scanning electron microscopy, and energy dispersive spectrometry. The microhardness, fracture toughness, and wear behaviors of the coatings were also investigated by using a microhardness tester and an ultra-functional wear testing machine. Results showed that the coatings were mainly composed of TiNi/Ti2Ni and TiC/TiB2 as the matrix and reinforcement particles, respectively. The phase constituents of the coatings were not influenced by addition of different contents of B4C. The microstructure of the reinforcements in the coatings presented the following evolution: hypereutectic consisting of blocky (TiC+TiB2)e eutectic and primary TiCp cellular dendrites (0 wt% B4C), mixture of hypereutectic and willow-shaped (TiB2+TiC)p pseudoeutectic (5 wt% B4C), and pseudoeutectic (15 and 25 wt% B4C). With increasing B4C content, the volume fraction and size of the pseudoeutectic structures as well as the average microhardness of the coatings (850, 889, 969, and 1002 HV0.2) were increased. By contrast, the average fracture toughness of the coatings was gradually decreased (4.47, 4.21, 4.06, and 3.85 Mpa m1/2) along with their wear volumes (0 wt%, 5 wt%, and 15 wt% B4C). The increase in B4C content to 25 wt% did not further reduce wear loss. The wear mechanism transformed from micro-cutting (0 wt% B4C) into a combination of micro-cutting and brittle debonding (5 wt% B4C) and finally led to brittle debonding (15 wt% and 25 wt% B4C). Coatings with suitable contents of B4C (less than 15 wt%) showed excellent comprehensive mechanical properties.

The role of grape seed extract in the remineralization of demineralized dentine: micromorphological and physical analyses.

PubMed

Tang, Cheng-fang; Fang, Ming; Liu, Rui-rui; Dou, Qi; Chai, Zhi-guo; Xiao, Yu-hong; Chen, Ji-hua

2013-12-01

Grape seed extract (GSE) is known to have a positive effect on the demineralization and/or remineralization of artificial root caries lesions. The present study aimed to investigate whether biomodification of caries-like acid-etched demineralized dentine, using proanthocyanidins-rich GSE, would promote its remineralization potential. Dentine specimens were acid-etched for 30s, then biomodified using proanthocyanidin-based preconditioners (at different concentrations and pH values) for 2min, followed by a 15-day artificial remineralization regimen. They were subsequently subjected to microhardness measurements, micromorphological evaluation and X-ray diffraction analyses. Stability of the preconditioners was also analyzed, spectrophotometrically. A concentration-dependent increase was observed in the microhardness of the specimens that were biomodified using GSE preconditioners, without pH adjustment. Field emission scanning electron microscopy revealed greater mineral deposition on their surfaces, which was further identified mainly as hydroxylapatite. The absorbances of preconditioner dilutions at pH 7.4 and pH 10.0 decreased at the two typical polyphenol bands. Transient GSE biomodification promoted remineralization on the surface of demineralized dentine, and this process was influenced by the concentration and pH value of the preconditioner. GSE preconditioner at a concentration of 15%, without pH adjustment, presented with the best results, and this may be attributed to its high polyphenolic content. Copyright © 2013 Elsevier Ltd. All rights reserved.

Microstructure and mechanical properties of stainless steel/calcium silicate composites manufactured by selective laser melting.

PubMed

Zheng, Zeng; Wang, Lianfeng; Jia, Min; Cheng, Lingyu; Yan, Biao

2017-02-01

Selective laser melting (SLM) is raised as one kind of additive manufacturing (AM) which is based on the discrete-stacking concept. This technique can fabricate advanced composites with desirable properties directly from 3D CAD data. In this research, 316L stainless steel (316L SS) and different fractions of calcium silicate (CaSiO 3 ) composites (weight fractions of calcium silicate are 0%, 5%,10% and 15%, respectively) were prepared by SLM technique with a purpose to develop biomedical metallic materials. The relative density, tensile, microhardness and elastic modulus of the composites were tested, their microstructures and fracture morphologies were observed using optical microscope (OM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). It was found that the addition of CaSiO 3 particles influenced the microstructure and mechanical properties of specimens significantly. The CaSiO 3 precipitates from the overlap of adjacent tracks and became the origin of the defects. The tensile strength of specimens range 320-722MPa. The microhardness and elastic modulus are around 250HV and 215GPa respectively. These composites were ductile materials and the fracture mode of the composites was mixed mode of ductile and brittle fracture. The 316L SS/CaSiO 3 composites can be a potential biomedical metallic materials in the medical field. Copyright © 2016. Published by Elsevier B.V.

Effect of different pH solvents on micro-hardness and surface topography of dental nano-composite: An in vitro analysis

PubMed Central

Khan, Aftab Ahmed; Siddiqui, Adel Zia; Al-Kheraif, Abdulaziz A; Zahid, Ambreen; Divakar, Darshan Devang

2015-01-01

Objective: Erosion of tooth surface is attributed to recent shift in diet pattern and frequent use of beverages. The aim of this research was to evaluate the effects of different beverages on surface topography and hardness of nano-filled composite material. Methods: Sixty flat disc shaped resin composite samples were fabricated and placed in distilled water for 24 hours. After 24 hours test samples were dried and divided into 4 groups. Group A (n=15) specimens were placed in tight amber bottle comprising 25 ml of artificial saliva. Similarly Group B, C and D were stored in equal amounts of orange juice, milk and coca cola drink respectively. Samples were checked for hardness and surface changes were evaluated with scanning electron microscopy. Results: There were strong significant difference observed in samples immersed in orange juice and artificial saliva. A strong significant difference was seen between Group D and Group A. Group A and Group C showed no significant difference. The micro-hardness test showed reduced values among all samples. Conclusion: Beverages consumed daily have a negative influence on hardness and surface degradation of nano-filled dental composite. Comparatively, nano-filled composites possess higher surface area to volume ratio of their fillers particle size may lead to higher surface roughness than other resin based dental biomaterials. PMID:26430417

Laser Cladding of γ-TiAl Intermetallic Alloy on Titanium Alloy Substrates

NASA Astrophysics Data System (ADS)

Maliutina, Iuliia Nikolaevna; Si-Mohand, Hocine; Piolet, Romain; Missemer, Florent; Popelyukh, Albert Igorevich; Belousova, Natalya Sergeevna; Bertrand, Philippe

2016-01-01

The enhancement of titanium and titanium alloy's tribological properties is of major interest in many applications such as the aerospace and automotive industry. Therefore, the current research paper investigates the laser cladding of Ti48Al2Cr2Nb powder onto Ti6242 titanium alloy substrates. The work was carried out in two steps. First, the optimal deposition parameters were defined using the so-called "combined parameters," i.e., the specific energy E specific and powder density G. Thus, the results show that those combined parameters have a significant influence on the geometry, microstructure, and microhardness of titanium aluminide-formed tracks. Then, the formation of dense, homogeneous, and defect-free coatings based on optimal parameters has been investigated. Optical and scanning electron microscopy techniques as well as energy-dispersive spectroscopy and X-ray diffraction analyses have shown that a duplex structure consisting of γ-TiAl and α 2-Ti3Al phases was obtained in the coatings during laser cladding. Moreover, it was shown that produced coatings exhibit higher values of microhardness (477 ± 9 Hv0.3) and wear resistance (average friction coefficient is 0.31 and volume of worn material is 5 mm3 after 400 m) compared to those obtained with bare titanium alloy substrates (353 Hv0.3, average friction coefficient is 0.57 and a volume of worn material after 400 m is 35 mm3).

Microstructure, Wear Resistance and Oxidation Behavior of Ni-Ti-Si Coatings Fabricated on Ti6Al4V by Laser Cladding.

PubMed

Zhuang, Qiaoqiao; Zhang, Peilei; Li, Mingchuan; Yan, Hua; Yu, Zhishui; Lu, Qinghua

2017-10-30

The Ni-Ti-Si composite coatings were successfully fabricated on Ti6Al4V by laser cladding. The microstructure were studied by SEM (scanning electron microscopy) and EDS (energy dispersive spectrometer). It has been found that Ti₂Ni and Ti₅Si₃ phases exist in all coatings, and some samples have TiSi₂ phases. Moreover, due to the existence of these phases, coatings presented relatively higher microhardness than that of the substrate (826 HV (Vickers hardness)) and the microhardness value of coating 3 is about twice larger than that of the substrate. During the dry sliding friction and wear test, due to the distribution of the relatively ductile phase of Ti₂Ni and reinforcement phases of Ti₅Si₃ and TiSi₂, the coatings performed good wear resistance. The oxidation process contains two stages: the rapid oxidation and slow oxidation by high temperature oxidation test at 800 °C for 50 h. Meanwhile, the value of the oxidation weight gain of the substrate is approximately three times larger than that of the coating 4. During the oxidation process, the oxidation film formed on the coating is mainly consisted of TiO₂, Al₂O₃ and SiO₂. Phases Ti₂Ni, Ti₅Si₃, TiSi₂ and TiSi were still found and it could be responsible for the improvement in oxidation resistance of the coatings by laser cladding.

Characterisation of an Al-BN nanocomposite prepared by ball milling and hot extrusion

NASA Astrophysics Data System (ADS)

Arlic, U.; Drozd, Z.; Trojanová, Z.; Molnárová, O.; Kasakewitsch, A.

2017-07-01

Aluminium-matrix-nanocomposites were manufactured by ball milling of microscale aluminium powder with BN nanoparticles in air, followed by subsequent consolidation by hot extrusion. The microstructure of the samples was studied using scanning electron microscopy. Vickers microhardness measurements were used to probe the mechanical properties of the samples. The amplitude dependent damping of the nanocomposites was measured at room temperature after thermal treatment of samples, and the linear thermal expansion was measured over a wide temperature range from room temperature up to 670K in the as-extruded state. The experimental results give a comprehensive picture of the behaviour of this nanocomposite system over the range of thermomechanical treatment conditions examined in this study. Based on these experimental data some possible influences of BN nanoparticles on the anelastic, plastic and thermal properties of microcrystalline aluminium are discussed.

Evolution of secondary-phase precipitates during annealing of the 12Kh18N9T steel irradiated with neutrons to a dose of 5 DPA

NASA Astrophysics Data System (ADS)

Tsai, K. V.; Maksimkin, O. P.; Turubarova, L. G.

2007-03-01

The formation and evolution of thermally-induced secondary precipitates in an austenitic stainless steel 12Kh18N9T irradiated in the core of a laboratory reactor VVR-K to a dose of 5 dpa and subjected to post-radiation isochronous annealings for 1 h in a temperature range from 450 to 1050°C have been studied using transmission electron microscopy (TEM) and microhardness measurements. It has been shown that the formation of stitch (secondary) titanium carbides and M 23C6 carbides at grain and twin boundaries after annealing at 1050°C is preceded by a complex evolution of fineparticles of secondary phases (titanium carbides and nitrides) precipitated at dislocation loops and dislocations during annealing at temperatures above 750°C.

Dual function of EDTA with silver nanoparticles for root canal treatment-A novel modification.

PubMed

Martinez-Andrade, Juan M; Avalos-Borja, Miguel; Vilchis-Nestor, Alfredo R; Sanchez-Vargas, Luis O; Castro-Longoria, Ernestina

2018-01-01

The chelating and antimicrobial capacity of a novel modification of 17% EDTA with silver nanoparticles (AgNPs) (EDTA-AgNPs) was evaluated in-vitro for root canal treatment (RCT). The EDTA-AgNPs solution was characterized by UV-Vis spectroscopy, ζ-potential and high-resolution transmission electron microscopy (HRTEM). Antimicrobial capacity was evaluated against Candida albicans and Staphylococcus aureus in planktonic and biofilm cells by broth macrodilution (24 h) and XTT assays, (1, 10 and 30 min) respectively. The chelating capacity of EDTA-AgNPs was assessed indirectly (smear layer removal) and directly (demineralizing effect) in bovine dentin at two silver concentrations, 16 and 512 μg/ml at 1 and 10 minutes of exposure time. Smear layer removal was evaluated by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The demineralizing effect was determined by atomic absorption spectroscopy (AAS), microhardness test (MH) and X-ray diffractometer (XRD). Synthesized AgNPs were quasi-spherical in shape with an average size of 13.09 ± 8.05 nm. 17% EDTA-AgNPs was effective to inhibit C. albicans and S. aureus in planktonic and biofilm cultures. The smear layer removal and demineralizing effect were similar between 17% EDTA-AgNPs and 17% EDTA treatments. The 17% EDTA-AgNPs solution proved to be an effective antimicrobial agent, and has a similar chelating capacity to 17% EDTA alone. These in-vitro studies strongly suggest that EDTA-AgNPs could be used for effective smear layer removal, having an antimicrobial effect at the same time during RCT.

Dual function of EDTA with silver nanoparticles for root canal treatment–A novel modification

PubMed Central

Martinez-Andrade, Juan M.; Avalos-Borja, Miguel; Vilchis-Nestor, Alfredo R.; Sanchez-Vargas, Luis O.

2018-01-01

The chelating and antimicrobial capacity of a novel modification of 17% EDTA with silver nanoparticles (AgNPs) (EDTA-AgNPs) was evaluated in-vitro for root canal treatment (RCT). The EDTA-AgNPs solution was characterized by UV-Vis spectroscopy, ζ-potential and high-resolution transmission electron microscopy (HRTEM). Antimicrobial capacity was evaluated against Candida albicans and Staphylococcus aureus in planktonic and biofilm cells by broth macrodilution (24 h) and XTT assays, (1, 10 and 30 min) respectively. The chelating capacity of EDTA-AgNPs was assessed indirectly (smear layer removal) and directly (demineralizing effect) in bovine dentin at two silver concentrations, 16 and 512 μg/ml at 1 and 10 minutes of exposure time. Smear layer removal was evaluated by atomic force microscopy (AFM) and scanning electron microscopy (SEM). The demineralizing effect was determined by atomic absorption spectroscopy (AAS), microhardness test (MH) and X-ray diffractometer (XRD). Synthesized AgNPs were quasi-spherical in shape with an average size of 13.09 ± 8.05 nm. 17% EDTA-AgNPs was effective to inhibit C. albicans and S. aureus in planktonic and biofilm cultures. The smear layer removal and demineralizing effect were similar between 17% EDTA-AgNPs and 17% EDTA treatments. The 17% EDTA-AgNPs solution proved to be an effective antimicrobial agent, and has a similar chelating capacity to 17% EDTA alone. These in-vitro studies strongly suggest that EDTA-AgNPs could be used for effective smear layer removal, having an antimicrobial effect at the same time during RCT. PMID:29346398

Phase structures and morphologies of tempered CA6NM stainless steel welded by hybrid laser-arc process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mirakhorli, F., E-mail: Fatemeh.mirakhorli.1@ens.e

The post-weld tempered microstructure of hybrid laser-arc welded CA6NM, a cast low carbon martensitic stainless steel, was investigated. The microstructural evolutions from the fusion zone to the base metal were characterized in detail using optical microscopy, scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), X-ray diffraction (XRD) and microhardness techniques. The fusion zone, in its post-weld tempered condition, consisted of tempered lath martensite, residual delta-ferrite with various morphologies, reversed austenite and chromium carbides. The reversed austenite, which can be detected through both EBSD and XRD techniques, was found to be finely dispersed along the martensite lath boundaries, particularly at triplemore » junctions. Based on the EBSD analysis, the orientation relationship between the reversed austenite and the adjacent martensite laths seemed to follow the Kurdjumov-Sachs (K-S) model. The results also revealed the presence of the reversed austenite in the different regions of the heat affected zone after post-weld tempering. The microindentation hardness distribution was measured, and correlated to the evolution of the corresponding microstructure across the welds. - Highlights: •The EBSD analysis was performed on hybrid laser-arc welded CA6NM. •The FZ consisted of tempered lath martensite, reversed austenite, carbides and δ ferrite after tempering. •The reversed γ was formed along the α′ lath boundaries, particularly at triple junctions.« less

Additive Manufacturing of AlSi10Mg Alloy Using Direct Energy Deposition: Microstructure and Hardness Characterization

NASA Astrophysics Data System (ADS)

Javidani, M.; Arreguin-Zavala, J.; Danovitch, J.; Tian, Y.; Brochu, M.

2017-04-01

This paper aims to study the manufacturing of the AlSi10Mg alloy with direct energy deposition (DED) process. Following fabrication, the macro- and microstructural evolution of the as-processed specimens was initially investigated using optical microscopy and scanning electron microscopy. Columnar dendritic structure was the dominant solidification feature of the deposit; nevertheless, detailed microstructural analysis revealed cellular morphology near the substrate and equiaxed dendrites at the top end of the deposit. Moreover, the microstructural morphology in the melt pool boundary of the deposit differed from the one in the core of the layers. The remaining porosity of the deposit was evaluated by Archimedes' principle and by image analysis of the polished surface. Crystallographic texture in the deposit was also assessed using electron backscatter diffraction and x-ray diffraction analysis. The dendrites were unidirectionally oriented at an angle of 80° to the substrate. EPMA line scans were performed to evaluate the compositional variation and elemental segregation in different locations. Eventually, microhardness (HV) tests were conducted in order to study the hardness gradient in the as-DED-processed specimen along the deposition direction. The presented results, which exhibited a deposit with an almost defect free structure, indicate that the DED process can suitable for the deposition of Al-Si-based alloys with a highly consolidated structure.

Effects of graphene plates' adoption on the microstructure, mechanical properties, and in vivo biocompatibility of calcium silicate coating.

PubMed

Xie, Youtao; Li, Hongqin; Ding, Chuanxian; Zheng, Xuebin; Li, Kai

2015-01-01

Calcium silicate (CS) ceramic is a good coating candidate for biomedical implants to improve biocompatibility and accelerate early osseointegration. However, the poor fracture toughness and wear resistance of this ceramic material restricts the long-term performance of implants. In this study, graphene plates (GPs) were used as reinforcement to improve the mechanical properties of CS coating. Composite coating containing 1.5 weight % GPs was prepared by vacuum plasma spraying technology. The good survival of the GPs in the composite coating was demonstrated by Raman analysis, although the defects of the GPs were increased after plasma spraying. Effects of the GPs' adoption on the microstructure of the coating were studied by scanning electron microscopy and transmission electron microscopy. Results showed that the GPs were homogenously distributed in the CS grains interface or enwrapped on the particles, and exhibited good wetting behavior with the CS matrix. The wear properties of the composite coating were obviously enhanced by the reinforcement of GPs. The reinforcement mechanism was attributed to the enhanced micro-hardness and interfacial bonding of the particles in the coating. In vivo experiments demonstrated that the composite coating possessed similarly good biocompatibility compared to pure CS coating. The bone-implant contact ratio reached 84.3%±7.4% for GPs/CS coating and 79.6%±9.4% for CS coating after 3 months' implantation.

Effects of graphene plates’ adoption on the microstructure, mechanical properties, and in vivo biocompatibility of calcium silicate coating

PubMed Central

Xie, Youtao; Li, Hongqin; Ding, Chuanxian; Zheng, Xuebin; Li, Kai

2015-01-01

Calcium silicate (CS) ceramic is a good coating candidate for biomedical implants to improve biocompatibility and accelerate early osseointegration. However, the poor fracture toughness and wear resistance of this ceramic material restricts the long-term performance of implants. In this study, graphene plates (GPs) were used as reinforcement to improve the mechanical properties of CS coating. Composite coating containing 1.5 weight % GPs was prepared by vacuum plasma spraying technology. The good survival of the GPs in the composite coating was demonstrated by Raman analysis, although the defects of the GPs were increased after plasma spraying. Effects of the GPs’ adoption on the microstructure of the coating were studied by scanning electron microscopy and transmission electron microscopy. Results showed that the GPs were homogenously distributed in the CS grains interface or enwrapped on the particles, and exhibited good wetting behavior with the CS matrix. The wear properties of the composite coating were obviously enhanced by the reinforcement of GPs. The reinforcement mechanism was attributed to the enhanced micro-hardness and interfacial bonding of the particles in the coating. In vivo experiments demonstrated that the composite coating possessed similarly good biocompatibility compared to pure CS coating. The bone-implant contact ratio reached 84.3%±7.4% for GPs/CS coating and 79.6%±9.4% for CS coating after 3 months’ implantation. PMID:26089662

Influence of laser irradiation on pits and fissures: an in situ study.

PubMed

Correa-Afonso, Alessandra M; Pécora, Jesus D; Palma-Dibb, Regina G

2013-02-01

The aim of this in situ study was to analyze the influence of the Er:YAG, Nd:YAG, and CO(2) lasers on the enamel acid resistance of pits and fissures. The laser tissue interaction has been studied as a method of preventing occlusal caries. Thirteen volunteers wore palatal acrylic appliances containing human occlusal enamel blocks that were divided into four groups (G1, control; G2, Er:YAG; G3, Nd:YAG; G4, CO(2)). Each palatal acrylic appliance was used in the four studied groups and was used for 14 consecutive days. A sucrose solution was applied to the specimens six times per day. The specimens were then sectioned in half, and a microhardness test was applied. The other halves were analyzed using polarized light microscopy to measure the caries-like lesion areas, and a morphological analysis was conducted using a scanning electron microscope (SEM). For the statistical analysis of the data obtained from the microhardness test (Knoop hardness number. [KHN]) (α=5%), Fisher's exact test was performed, and the group means were as follows: G1, 247±71; G2, 258±70; G3, 272±73; and G4, 298±56. The results demonstrated that the control group was significantly different from G3 and G4, which presented higher microhardness values. The Wilcoxon signed-rank test was used to analyze the data obtained from the caries-lesion area measurements (mm(2)) (α=5%) (G1, 0.01±1.08; G2, 0.13±0.18; G3, 0.05±0.17; and G4, 0.09±0.22). The results no showed significant differences among the groups in this analysis. Based on the results from the present study, it may be concluded that the CO(2) and Nd:YAG lasers increased the enamel acid resistance in pits and fissures.

Antibacterial and physical properties of EGCG-containing glass ionomer cements.

PubMed

Hu, Jieqiong; Du, Xijin; Huang, Cui; Fu, Dongjie; Ouyang, Xiaobai; Wang, Yake

2013-10-01

To evaluate the effect of the addition of epigallocatechin-3-gallate (EGCG) on the antibacterial and physical properties of glass ionomer cement (GIC). A conventional GIC, Fuji IX, was used as a control. EGCG was incorporated into GIC at 0.1% (w/w) and used as the experimental group. Chlorhexidine (CHX) was added into GIC at 1% (w/w) as a positive control. The anti-biofilm effect of the materials was assessed by a colorimetric technique (MTT assay) and scanning electron microscopy (SEM). The leaching antibacterial activity of the materials on Streptococcus mutans was evaluated by an agar-diffusion test. The flexural strength of the materials was evaluated using a universal testing machine and the surface microhardness was measured using a microhardness tester. The fluoride-releasing property of the materials was tested by ion chromatography. The optical density (OD) values of the GIC-EGCG group were significantly decreased at 4h compared with the GIC group, but only a slightly decreased tendency was observed at 24h (P>0.05). No inhibition zones were detected in the GIC group during the study period. Significant differences were found between each group (P<0.05). Compared with the control group, there was a significant increase in the flexural strength and surface microhardness for the GIC-EGCG group (P<0.05). The fluoride ion release was not influenced by EGCG-incorporation (P>0.05). These findings suggested that GIC-containing 0.1% (w/w) EGCG is a promising restorative material with improved mechanical properties and a tendency towards preferable antibacterial properties. Modification of the glass ionomer cements with EGCG to improve the antibacterial and physical properties showed some encouraging results. This suggested that the modification of GIC with EGCG might be an effective strategy to be used in the dental clinic. However, this was only an in vitro study and clinical trials would need to verify true outcomes. Copyright © 2013 Elsevier Ltd. All rights reserved.

Electron Beam Welding of IN792 DS: Effects of Pass Speed and PWHT on Microstructure and Hardness.

PubMed

Angella, Giuliano; Barbieri, Giuseppe; Donnini, Riccardo; Montanari, Roberto; Richetta, Maria; Varone, Alessandra

2017-09-05

Electron Beam (EB) welding has been used to realize seams on 2 mm-thick plates of directionally solidified (DS) IN792 superalloy. The first part of this work evidenced the importance of pre-heating the workpiece to avoid the formation of long cracks in the seam. The comparison of different pre-heating temperatures (PHT) and pass speeds ( v ) allowed the identification of optimal process parameters, namely PHT = 300 °C and v = 2.5 m/min. The microstructural features of the melted zone (MZ); the heat affected zone (HAZ), and base material (BM) were investigated by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS), electron back-scattered diffraction (EBSD), X-ray diffraction (XRD), and micro-hardness tests. In the as-welded condition; the structure of directionally oriented grains was completely lost in MZ. The γ' phase in MZ consisted of small (20-40 nm) round shaped particles and its total amount depended on both PHT and welding pass speed, whereas in HAZ, it was the same BM. Even if the amount of γ' phase in MZ was lower than that of the as-received material, the nanometric size of the particles induced an increase in hardness. EDS examinations did not show relevant composition changes in the γ' and γ phases. Post-welding heat treatments (PWHT) at 700 and 750 °C for two hours were performed on the best samples. After PWHTs, the amount of the ordered phase increased, and the effect was more pronounced at 750 °C, while the size of γ' particles in MZ remained almost the same. The hardness profiles measured across the joints showed an upward shift, but peak-valley height was a little lower, indicating more homogeneous features in the different zones.

Interface morphology and mechanical properties of Al-Cu-Al laminated composites fabricated by explosive welding and subsequent rolling process

NASA Astrophysics Data System (ADS)

Hoseini-Athar, M. M.; Tolaminejad, B.

2016-07-01

Explosive welding is a well-known solid state method for joining similar and dissimilar materials. In the present study, tri-layered Al-Cu-Al laminated composites with different interface morphologies were fabricated by explosive welding and subsequent rolling. Effects of explosive ratio and rolling thickness reduction on the morphology of interface and mechanical properties were evaluated through optical/scanning electron microscopy, micro-hardness, tensile and tensile-shear tests. Results showed that by increasing the thickness reduction, bonding strength of specimens including straight and wavy interfaces increases. However, bonding strength of the specimens with melted layer interface decreases up to a threshold thickness reduction, then rapidly increases by raising the reduction. Hardness Values of welded specimens were higher than those of original material especially near the interface and a more uniform hardness profile was obtained after rolling process.

Sliding seal materials for adiabatic engines

NASA Technical Reports Server (NTRS)

Lankford, J.

1985-01-01

The sliding friction coefficients and wear rates of promising carbide, oxide, and nitride materials were measured under temperature, environmental, velocity, loading conditions that are representative of the adiabatic engine environment. In order to provide guidance needed to improve materials for this application, the program stressed fundamental understanding of the mechanisms involved in friction and wear. Microhardness tests were performed on the candidate materials at elevated temperatures, and in atmospheres relevant to the piston seal application, and optical and electron microscopy were used to elucidate the micromechanisms of wear following wear testing. X-ray spectroscopy was used to evaluate interface/environment interactions which seemed to be important in the friction and wear process. Electrical effects in the friction and wear processes were explored in order to evaluate the potential usefulness of such effects in modifying the friction and wear rates in service. However, this factor was found to be of negligible significance in controlling friction and wear.

Microstructures and mechanical properties of nanocrystalline NiTi intermetallics formed by mechanosynthesis

NASA Astrophysics Data System (ADS)

Arunkumar, S.; Kumaravel, P.; Velmurugan, C.; Senthilkumar, V.

2018-01-01

The formulation of nanocrystalline NiTi shape memory alloys has potential effects in mechanical stimulation and medical implantology. The present work elucidates the effect of milling time on the product's structural characteristics, chemical composition, and microhardness for NiTi synthesized by mechanical alloying for different milling durations. Increasing the milling duration led to the formation of a nanocrystalline NiTi intermetallic at a higher level. The formation of nanocrystalline materials was directed through cold fusion, fracturing, and the development of a steady state, which were influenced by the accumulation of strain energy. In the morphological study, uninterrupted cold diffusion and fracturing were visualized using transmission electron microscopy. Particle size analysis revealed that the mean particle size was reduced to 93 μm after 20 h of milling. The mechanical strength was enhanced by the formation of a nanocrystalline intermetallic phase at longer milling time, which was confirmed by the results of Vickers hardness analyses.

Investigation on the modification behavior of A356.2 alloy with Yb-La composite modifier

NASA Astrophysics Data System (ADS)

Zhang, Shaochen; Leng, Jinfeng; Wang, Zhibin; Wang, Qi; Shao, Yuewen; Teng, Xinying

2018-01-01

In this work, an investigation was conducted to evaluate the influence of the Yb + La addition on the microstructures and mechanical properties of A356.2 alloy. The results show that the the grain size was refined and morphological structure of Si changed from needle-like to fine spheroidal particle by adding Yb + La. The eutectic temperature decreased from 589 °C to 581 °C and the freezing range of primary α-Al become wider after adding Yb + La. The mechanical properties showed great improvement after T6 heat treatment. The ultimate tensile strength and microhardness of the composites were increased to 279.0 MPa and 99.2 HB after T6 heat treatment which increased by 28.2% and 47.3%, respectively. The fracture mechanism was analyzed using the scanning electron microscopy and proved to be a transgranular/intergranular fracture modes.

Development of Al-Al3Ni Nanocomposite by Duplex Processing of Flame Spray and Friction Stir Processing, and Evaluation of Its Properties

NASA Astrophysics Data System (ADS)

Adel Mehraban, F.; Karimzadeh, F.; Abbasi, M. H.

2017-10-01

In this study, Al-Al3Ni nanocomposite was fabricated by friction stir processing (FSP) of a nickel-deposited Al6061-T6 plate. X-ray diffraction results showed that Al3Ni phase was formed because of an in situ reaction between the preplaced nickel and aluminum substrate. To predict the first phase formed during FSP, effective heat of formation (EHF) thermodynamic model was applied, and the results were in agreement with experimental data. The presence of facet nanoparticles in transmission electron microscopy micrographs of the stir zone (SZ) confirmed the formation of Al3Ni nano-reinforcements. Although microhardness and ultimate tensile strength in the SZ of nanocomposite degraded because of precipitates dissolution in Al6061-T6 during FSP, it showed improved tribological behavior at elevated temperatures.

Three-dimensional flow characteristics of aluminum alloy in multi-pass equal channel angular pressing

NASA Astrophysics Data System (ADS)

Jin, Young-Gwan; Son, Il-Heon; Im, Yong-Taek

2010-06-01

Experiments with a square specimen made of commercially pure aluminum alloy (AA1050) were conducted to investigate deformation behaviour during a multi-pass Equal Channel Angular Pressing (ECAP) for routes A, Bc, and C up to four passes. Three-dimensional finite element numerical simulations of the multi-pass ECAP were carried out in order to evaluate the influence of processing routes and number of passes on local flow behaviour by applying a simplified saturation model of flow stress under an isothermal condition. Simulation results were investigated by comparing them with the experimentally measured data in terms of load variations and microhardness distributions. Also, transmission electron microscopy analysis was employed to investigate the microstructural changes. The present work clearly shows that the three-dimensional flow characteristics of the deformed specimen were dependent on the strain path changes due to the processing routes and number of passes that occurred during the multi-pass ECAP.

MoNbTaV Medium-Entropy Alloy

DOE PAGES

Yao, Hongwei; Qiao, Jun -Wei; Gao, Michael; ...

2016-05-19

Guided by CALPHAD (Calculation of Phase Diagrams) modeling, the refractory medium-entropy alloy MoNbTaV was synthesized by vacuum arc melting under a high-purity argon atmosphere. A body-centered cubic solid solution phase was experimentally confirmed in the as-cast ingot using X-ray diffraction and scanning electron microscopy. The measured lattice parameter of the alloy (3.208 Å) obeys the rule of mixtures (ROM), but the Vickers microhardness (4.95 GPa) and the yield strength (1.5 GPa) are about 4.5 and 4.6 times those estimated from the ROM, respectively. Using a simple model on solid solution strengthening predicts a yield strength of approximately 1.5 GPa. Inmore » conclusion, thermodynamic analysis shows that the total entropy of the alloy is more than three times the configurational entropy at room temperature, and the entropy of mixing exhibits a small negative departure from ideal mixing.« less

Comparison of mechanical and friction properties of composite materials based on AlMg2 containing nano-dimensional particles of crystalline graphite and nanofibers of gamma oxide of aluminum

NASA Astrophysics Data System (ADS)

Aborkin, A. V.; Babin, D. M.; Soboĺkov, A. V.

2018-04-01

The method of mechanical synthesis in a planetary ball mill was used for production of composite powders based on the AlMg2 alloy containing 1 wt. % of nanosized particles of crystalline graphite or γ-Al2O3. The resulting powders are consolidated by the sintering under pressure. Using the methods of X-ray diffraction analysis, scanning and transmission electron microscopy, the structural-phase composition of bulk composite materials was studied. Comparative analysis of the microhardness, the conditional yield stress at compression, and the friction coefficient of bulk composite materials is carried out. It has been found out that the mechanical properties of composites reinforced with γ-Al2O3 nanofibers are higher than when reinforcing with nanoscale particles of crystalline graphite.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xiao, Y.; Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai 200240; Li, W., E-mail: weilee@sjtu.edu.cn

Low temperature tempering is important in improving the mechanical properties of steels. In this study, the thermoelectric power method was employed to investigate carbon segregation during low temperature tempering ranging from 110 °C to 170 °C of a medium carbon alloyed steel, combined with micro-hardness, transmission electron microscopy and atom probe tomography. Evolution of carbon dissolution from martensite and segregation to grain boundaries/interfaces and dislocations were investigated for different tempering conditions. Carbon concentration variation was quantified from 0.33 wt.% in quenching sample to 0.15 wt.% after long time tempering. The kinetic of carbon diffusion during tempering process was discussed throughmore » Johnson-Mehl-Avrami equation. - Highlights: • The thermoelectric power (TEP) was employed to investigate the low temperature tempering of a medium carbon alloyed steel. • Evolution of carbon dissolution was investigated for different tempering conditions. • Carbon concentration variation was quantified from 0.33 wt.% in quenching sample to 0.15 wt.% after long time tempering.« less

Hardening Potential of an Al-Cu-Li Friction Stir Weld

NASA Astrophysics Data System (ADS)

Ivanov, Rosen; Boselli, Julien; Denzer, Diana; Larouche, Daniel; Gauvin, Raynald; Brochu, Mathieu

The evolution of the microstructure during friction stir welding of a third generation AA2199 Al-Li alloy has been described and related to the mechanical properties of welds. The coupling of electron microscopy and micro-hardness have helped generate an understanding of the relationship between grain structure, precipitate density and morphology behind the observed changes in mechanical properties during post weld artificial ageing. The ability of welds to recover hardness and strength during post weld heat treatment was linked to the limited formation of large scale precipitates which act as sinks for alloying elements. Welds obtained with high tool rotation speed (within parameters studied) showed ultimate tensile strength levels of about 93% of the base metal, an elongation of 6% at fracture, and hardness values ranging between 120-140 HV in the stir zone, thermo-mechanically affected zone, and heat affected zone upon post weld heat treatment.

Mechanical Characteristics of Welded Joints of Aluminum Alloy 6061 T6 Formed by Arc and Friction Stir Welding

NASA Astrophysics Data System (ADS)

Astarita, A.; Squillace, A.; Nele, L.

2016-01-01

Butt welds formed by arc welding in inert gas with nonconsumable electrode (tungsten inert gas (TIG) welding) and by friction stir welding (FSW) from aluminum alloy AA6061 T6 are studied. Comparative analysis of the structures and mechanical properties of the welded joints is performed using the results of optical and electron microscopy, tensile tests, tests for residual bending ductility, and measurements of microhardness. The changes in the microstructure in different zones and the degrees of degradation of the mechanical properties after the welding are determined. It is shown that the size of the tool for the friction stir welding affects the properties of the welds. Quantitative results showing the relation between the microscopic behavior of the alloy and the welding-induced changes in the microstructure are obtained. Friction stir welding is shown to provide higher properties of the welds.

Effect of Resin Infiltration on Artificial Caries: An in vitro Evaluation of Resin Penetration and Microhardness.

PubMed

Prajapati, Deepesh; Nayak, Rashmi; Pai, Deepika; Upadhya, Nagraj; K Bhaskar, Vipin; Kamath, Pujan

2017-01-01

To evaluate the effectiveness of resin infiltration on artificial caries lesion by assessing the depth of resin penetration and the change in microhardness of lesion postinfiltration. Totally 45 human extracted premolars were used to create an artificial demineralized lesion in enamel using demineralizing solution. A total of 15 samples (group I) were infiltrated with resin. The depth of resin penetration was studied using scanning electron microscope (SEM). Other half (n = 30) of samples was equally divided into three subgroups and Vickers hardness number (VHN) values were obtained to measure the surface microhardness as group 11 a-before demineralization, 11 b-after demineralization, IIc-postresin infiltration. Mean depth of penetration in group I was 516.8 urn. There was statistically significant increase in VHN values of demineralized lesion postresin infiltration (independent Student's t-test, p < 0.001). Penetration depth of the resin infiltrant was deep enough to render beneficial effects, while significant increase in microhardness was observed postresin infiltration. Infiltrant used can be considered as a valid treatment option for noncavitated lesions. Prajapati D, Nayak R, Pai D, Upadhya N, Bhaskar VK, Kamath P. Effect of Resin Infiltration on Artificial Caries: An in vitro Evaluation of Resin Penetration and Microhardness. Int J Clin Pediatr Dent 2017;10(3):250-256.

The use of a directional solidification technique to investigate the interrelationship of thermal parameters, microstructure and microhardness of Bi–Ag solder alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Spinelli, José Eduardo, E-mail: spinelli@ufscar.br; Silva, Bismarck Luiz; Cheung, Noé

2014-10-15

Bi–Ag alloys have been stressed as possible alternatives to replace Pb-based solder alloys. Although acceptable melting temperatures and suitable mechanical properties may characterize such alloys, as referenced in literature, there is a lack of comprehension regarding their microstructures (morphologies and sizes of the phases) considering a composition range from 1.5 to 4.0 wt.%Ag. In order to better comprehend such aspects and their correlations with solidification thermal parameters (growth rate, v and cooling rate, T-dot), directional solidification experiments were carried out under transient heat flow conditions. The effects of Ag content on both cooling rate and growth rate during solidification aremore » examined. Microstructure parameters such as eutectic/dendritic spacing, interphase spacing and diameter of the Ag-rich phase were determined by optical microscopy and scanning electron microscopy. The competition between eutectic cells and dendrites in the range from 1.5 to 4.0 wt.%Ag is explained by the coupled zone concept. Microhardness was determined for different microstructures and alloy Ag contents with a view to permitting correlations with microstructure parameters to be established. Hardness is shown to be directly affected by both solute macrosegregation and morphologies of the phases forming the Bi–Ag alloys, with higher hardness being associated with the cellular morphology of the Bi-2.5 and 4.0 wt.%Ag alloys. - Highlights: • Asymmetric zone of coupled growth for Bi–Ag is demonstrated. • Faceted Bi-rich dendrites have been characterized for Bi–1.5 wt.%Ag alloy. • Eutectic cells were shown for the Bi-2.5 and 4.0 wt.%Ag solder alloys. • Interphase spacing relations with G × v are able to represent the experimental scatters. • Hall-Petch type equations are proposed relating microstructural spacings to hardness.« less

Surface pre-conditioning with bioactive glass air-abrasion can enhance enamel white spot lesion remineralization.

PubMed

Milly, Hussam; Festy, Frederic; Andiappan, Manoharan; Watson, Timothy F; Thompson, Ian; Banerjee, Avijit

2015-05-01

To evaluate the effect of pre-conditioning enamel white spot lesion (WSL) surfaces using bioactive glass (BAG) air-abrasion prior to remineralization therapy. Ninety human enamel samples with artificial WSLs were assigned to three WSL surface pre-conditioning groups (n=30): (a) air-abrasion with BAG-polyacrylic acid (PAA-BAG) powder, (b) acid-etching using 37% phosphoric acid gel (positive control) and (c) unconditioned (negative control). Each group was further divided into three subgroups according to the following remineralization therapy (n=10): (I) BAG paste (36 wt.% BAG), (II) BAG slurry (100 wt.% BAG) and (III) de-ionized water (negative control). The average surface roughness and the lesion step height compared to intra-specimen sound enamel reference points were analyzed using non-contact profilometry. Optical changes within the lesion subsurface compared to baseline scans were assessed using optical coherence tomography (OCT). Knoop microhardness evaluated the WSLs' mechanical properties. Raman micro-spectroscopy measured the v-(CO3)(2-)/v1-(PO4)(3-) ratio. Structural changes in the lesion were observed using confocal laser scanning microscopy (CLSM) and scanning electron microscopy-energy dispersive X-ray spectrometry (SEM-EDX). All comparisons were considered statistically significant if p<0.05. PAA-BAG air-abrasion removed 5.1 ± 0.6 μm from the lesion surface, increasing the WSL surface roughness. Pre-conditioning WSL surfaces with PAA-BAG air-abrasion reduced subsurface light scattering, increased the Knoop microhardness and the mineral content of the remineralized lesions (p<0.05). SEM-EDX revealed mineral depositions covering the lesion surface. BAG slurry resulted in a superior remineralization outcome, when compared to BAG paste. Pre-conditioning WSL surfaces with PAA-BAG air-abrasion modified the lesion surface physically and enhanced remineralization using BAG 45S5 therapy. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effects of post-heat treatment on microstructure and properties of laser cladded composite coatings on titanium alloy substrate

NASA Astrophysics Data System (ADS)

Li, G. J.; Li, J.; Luo, X.

2015-01-01

The composite coatings were produced on the Ti6Al4V alloy substrate by laser cladding. Subsequently, the coatings were heated at 500 °C for 1 h and 2 h and then cooled in air. Effects of post-heat treatment on microstructure, microhardness and fracture toughness of the coatings were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), optical microscopy (OM). Wear resistance of the coatings was evaluated under the dry sliding reciprocating friction condition at room temperature. The results indicated that the coatings mainly consist of a certain amount of coarse white equiaxed WC particles surrounded by the white-bright W2C, a great deal of fine dark spherical TiC particles and the matrix composed of the α(Ti), Ti2Ni and TiNi phases. Effects of the post-heat treatment on phase constituents and microstructure of the coatings were almost negligible due to the low temperature. However, the post-heat treatment could decrease the residual stress and increase fracture toughness of the coatings, and fracture toughness of the coatings was improved from 2.77 MPa m1/2 to 3.80 MPa m1/2 and 4.43 MPa m1/2 with the heat treatment for 1 h and 2 h, respectively. The mutual role would contribute to the reduction in cracking susceptibility. Accompanied with the increase in fracture toughness, microhardness of the coatings was reduced slightly. The dominant wear mechanism for all the coatings was abrasive wear, characterized by micro-cutting or micro-plowing. The heat treatment could significantly decrease the average friction coefficient and reduce the fluctuation of the friction coefficient with the change in sliding time. The appropriate heat treatment time (approximately 1 h) had a minimal effect on wear mass loss and volume loss. Moreover, the improvement in fracture toughness will also be beneficial to wear resistance of the coatings under the long service.

Fine grained 304 ASS processed by a severe plastic deformation and subsequent annealing; microstructure and mechanical properties evaluation

NASA Astrophysics Data System (ADS)

Salout, Shima Ahmadzadeh; Shirazi, Hasan; Nili-Ahmadabadi, Mahmoud

2018-01-01

The current research is an attempt to study the effect of a novel severe plastic deformation technique so called "repetitive corrugation and straightening by rolling" (RCSR) and subsequent annealing on the microstructure and mechanical properties of AISI type 304 austenitic stainless steel. In this study, RCSR process was carried out at 200 °C on the 304 austenitic stainless steel (above Md30 temperature that is about 50 °C for this stainless steel) in order to avoid the formation of martensite phase when a high density of dislocations was introduced into the austenite phase and also high density of mechanical twins was induced in the deformed 304 austenitic stainless steel. Because of relationship between deformation temperature, stacking fault energy (SFE) and mechanisms of deformation. Thereafter subsequently, annealing treatment was applied into deformed structure in order to refine the microstructure of 304 stainless s teel. The specimens were examined by means of optical microscopy (OM), scanning electron microscopy (SEM), tensile and micro-hardness tests. The results indicate that by increasing the cycles of RCSR process (increasing applied strain), further mechanical twins are induced, the hardness and in particular, the yield stress of specimens have been increased.

Determination of 200 °C Isothermal Section of Al-Ag-Ga Phase Diagram by Microanalysis, X-ray Diffraction, Hardness and Electrical Conductivity Measurements

NASA Astrophysics Data System (ADS)

Premović, Milena; Tomović, Milica; Minić, Duško; Manasijević, Dragan; Živković, Dragana; Ćosović, Vladan; Grković, Vladan; Đorđević, Aleksandar

2017-04-01

Ternary Al-Ag-Ga system at 200 °C was experimentally and thermodynamically assessed. Isothermal section was extrapolated using optimized thermodynamic parameters for constitutive binary systems. Microstructure and phase composition of the selected alloy samples were analyzed using light microscopy, scanning electron microscopy combined with energy-dispersive spectrometry and x-ray powder diffraction technique. The obtained experimental results were found to be in a close agreement with the predicted phase equilibria. Hardness and electrical conductivity of the alloy samples from four vertical sections Al-Ag80Ga20, Al-Ag60Ga40, Ag-Al80Ga20 and Ag-Al60Ga40 of the ternary Al-Ag-Ga system at 200 °C were experimentally determined using Brinell method and eddy current measurements. Additionally, hardness of the individual phases present in the microstructure of the studied alloy samples was determined using Vickers microhardness test. Based on experimentally obtained results, isolines of Brinell hardness and electrical conductivity were calculated for the alloys from isothermal section of the ternary Al-Ag-Ga system at 200 °C.

Synthesis, Characterization and Cold Workability of Cast Copper-Magnesium-Tin Alloys

NASA Astrophysics Data System (ADS)

Bravo Bénard, Agustín Eduardo; Martínez Hernández, David; González Reyes, José Gonzalo; Ortiz Prado, Armando; Schouwenaars Franssens, Rafael

2014-02-01

The use of Mg as an alloying element in copper alloys has largely been overlooked in scientific literature and technological applications. Its supposed tribological compatibility with iron makes it an interesting option to replace Pb in tribological alloys. This work describes the casting process of high-quality thin slabs of Cu-Mg-Sn alloys with different compositions by means of conventional methods. The resulting phases were analyzed using X-ray diffraction, scanning electron microscopy, optical microscopy, and energy dispersive X-ray spectroscopy techniques. Typical dendritic α-Cu, eutectic Cu2Mg(Sn) and eutectoid non-equilibrium microstructures were found. Tensile tests and Vickers microhardness show the excellent hardening capability of Mg as compared to other copper alloys in the as-cast condition. For some of the slabs and compositions, cold rolling reductions of over 95 pct have been easily achieved. Other compositions and slabs have failed during the deformation process. Failure analysis after cold rolling reveals that one cause for brittleness is the presence of casting defects such as microshrinkage and inclusions, which can be eliminated. However, for high Mg contents, a high volume fraction of the intermetallic phase provides a contiguous path for crack propagation through the connected interdendritic regions.

Characterization of a wollastonite glass-ceramic material prepared using sugar cane bagasse ash (SCBA) as one of the raw materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Teixeira, Silvio R., E-mail: rainho@fct.unesp.br; Souza, Agda E.; Carvalho, Claudio L.

Glass-ceramic material prepared with sugar cane bagasse ash as one of the raw materials was characterized to determine some important properties for its application as a coating material. X-ray diffraction patterns showed that wollastonite-2M (CaSiO{sub 3}) was the major glass-ceramic phase. The Rietveld method was used to quantify the crystalline (60 wt.%) and vitreous (40 wt.%) phases in the glass-ceramic. The microstructure (determined by scanning electron microscopy) of this material had a marble appearance, showing a microporous network of elongated crystals with some areas with dendritic, feather-like ordering. Microhardness data gave a mean hardness value of 564.4 HV (Vickers-hardness), andmore » light microscopy disclosed a greenish brown colored material with a vitreous luster. - Highlights: • We studied the properties of a glass-ceramic material obtained from sugarcane ash. • This material has the appearance and hardness of natural stones. • A refining method gave information about its amorphous and crystalline phases. • This material has potential to be used as coating plates for buildings.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shrestha, Triratna; Alsagabi, Sultan; Charit, Indrajit

The modified 9Cr-1Mo steel (Grade 91) is a material of choice in fossil-fuel-fired power plants with increased efficiency, service life, and reduction in emission of greenhouse gases. It is also considered a prospective material for the Next Generation Nuclear Power Plant for application in reactor pressure vessels at temperatures up to 650°C. In this paper, heat treatment of the modified 9Cr-1Mo steel was studied by normalizing and tempering the steel at various temperatures and times, with the ultimate goal of improving its creep resistance and optimizing material hardness. The microstructural evolution of the heat treated steels was correlated with themore » differential scanning calorimetric results. Optical microscopy, scanning and transmission electron microscopy in conjunction with microhardness profiles and calorimetric plots were used to understand the evolution of microstructure including precipitate structures in modified 9Cr-1Mo steel and relate it to the mechanical behavior of the steel. Thermo-CalcTM calculations were used to support experimental work and provide guidance in terms of the precipitate stability and microstructural evolution. Furthermore, the carbon isopleth and temperature dependencies of the volume fraction of different precipitates were constructed. The predicted and experimentally observed results were found to be in good agreement.« less

Deposition of magnesium nitride thin films on stainless steel-304 substrates by using a plasma focus device

NASA Astrophysics Data System (ADS)

Ramezani, Amir Hoshang; Habibi, Maryam; Ghoranneviss, Mahmood

2014-08-01

In this research, for the first time, we synthesize magnesium nitride thin films on 304-type stainless steel substrates using a Mather-type (2 kJ) plasma focus (PF) device. The films of magnesium nitride are coated with different number of focus shots (like 15, 25 and 35) at a distance of 8 cm from the anode tip and at 0° angular position with respect to the anode axis. For investigation of the structural properties and surface morphology of magnesium nitride films, we utilized the X-ray diffractometer (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM) analysis, respectively. Also, the elemental composition is characterized by energy-dispersive X-ray (EDX) analysis. Furthermore, Vicker's microhardness is used to study the mechanical properties of the deposited films. The results show that the degree of crystallinity of deposited thin films (from XRD), the average size of particles and surface roughness (from AFM), crystalline growth of structures (from SEM) and the hardness values of the films depend on the number of focus shots. The EDX analysis demonstrates the existence of the elemental composition of magnesium in the deposited samples.

Corrosion behavior of as-cast Mg-8Li-3Al+ xCe alloy in 3.5wt% NaCl solution

NASA Astrophysics Data System (ADS)

Manivannan, S.; Dinesh, P.; Mahemaa, R.; MariyaPillai, Nandhakumaran; Kumaresh Babu, S. P.; Sundarrajan, Srinivasan

2016-10-01

Mg-8Li-3Al+ xCe alloys ( x = 0.5wt%, 1.0wt%, and 1.5wt%) were prepared through a casting route in an electric resistance furnace under a controlled atmosphere. The cast alloys were characterized by X-ray diffraction, optical microscopy, scanning electron microscopy, and energy-dispersive X-ray spectroscopy. The corrosion behavior of the as-cast Mg-8Li-3Al+ xCe alloys were studied under salt spray tests in 3.5wt% NaCl solution at 35°C, in accordance with standard ASTM B-117, in conjunction with potentiodynamic polarization (PDP) tests. The results show that the addition of Ce to Mg-8Li-3Al (LA83) alloy results in the formation of Al2Ce intermetallic phase, refines both the α-Mg phase and the Mg17Al12 intermetallic phase, and then increases the microhardness of the alloys. The results of PDP and salt spray tests reveal that an increase in Ce content to 1.5wt% decreases the corrosion rate. The best corrosion resistance is observed for the LA83 alloy sample with 1.0wt% Ce.

Development of TiN particulates reinforced SS316 based metal matrix composite by direct metal laser sintering technique and its characterization

NASA Astrophysics Data System (ADS)

Hussain, Manowar; Mandal, Vijay; Kumar, Vikas; Das, A. K.; Ghosh, S. K.

2017-12-01

The present study describes the fabrication of TiN particulates reinforced SS316 based Metal Matrix Composites (MMCs) in nitrogen and argon atmosphere. The influence of sintering process parameters on microstructure, density, porosity, wear rate and microhardness of the fabricated samples has been analyzed. The input variable process parameters, such as, laser power density (range: 4.13-5.57 W/cm2 (× 104)), scanning speed (range: 3500-4500 mm/min) and the constant parameters, such as, laser beam diameter (0.4 mm), hatching distance (0.2 mm) and layer thickness (0.4 mm) have been considered in the process. It has been observed from Field Emission Scanning Electron Microscopy (FESEM) analysis that TiN and SS316 powder mixture can be sintered in which chromium acts as a binder. Fine gaps are not found at the interface between TiN and SS316 when the mixture is sintered in nitrogen atmosphere. With an increase in the percentage of TiN, the density and wear rate decreases. However, when the reinforcement is taken beyond 18% by weight, the wear rate starts increasing. The microhardness also increases with an increase in the percentage of TiN. The microstructure, elemental compositions and phase characterization of the developed sintered MMCs have been examined by FESEM, EDX (Energy-dispersive X-ray spectroscopy) and XRD (X-ray diffractometer) analysis, respectively. The results have demonstrated the suitability of the TiN reinforced SS316 MMCs for industrial applications.

Metallurgical characterization of orthodontic brackets produced by Metal Injection Molding (MIM).

PubMed

Zinelis, Spiros; Annousaki, Olga; Makou, Margarita; Eliades, Theodore

2005-11-01

The aim of this study was to investigate the bonding base surface morphology, alloy type, microstructure, and hardness of four types of orthodontic brackets produced by Metal Injection Molding technology (Discovery, Extremo, Freedom, and Topic). The bonding base morphology of the brackets was evaluated by scanning electron microscopy (SEM). Brackets from each manufacturer were embedded in epoxy resin, and after metallographic grinding, polishing and coating were analyzed by x-ray energy-dispersive spectroscopic (EDS) microanalysis to assess their elemental composition. Then, the brackets were subjected to metallographic etching to reveal their metallurgical structure. The same specimen surfaces were repolished and used for Vickers microhardness measurements. The results were statistically analyzed with one-way analysis of variance and Student-Newman-Keuls multiple comparison test at the 0.05 level of significance. The findings of SEM observations showed a great variability in the base morphology design among the brackets tested. The x-ray EDS analysis demonstrated that each bracket was manufactured from different ferrous or Co-based alloys. Metallographic analysis showed the presence of a large grain size for the Discovery, Freedom, and Topic brackets and a much finer grain size for the Extremo bracket. Vickers hardness showed great variations among the brackets (Topic: 287 +/- 16, Freedom: 248 +/- 13, Discovery: 214 +/- 12, and Extremo: 154 +/- 9). The results of this study showed that there are significant differences in the base morphology, composition, microstructure, and microhardness among the brackets tested, which may anticipate significant clinical implications.

Effect of mo Content on Microstructure and Properties of Laser Cladding Fe-BASED Alloy Coatings

NASA Astrophysics Data System (ADS)

Xiaoli, Ma; Kaiming, Wang; Hanguang, Fu; Jiang, Ju; Yongping, Lei; Dawei, Yi

Mo alloying Fe-based coating was fabricated on the surface of Q235 steel by using 6 kW fiber laser. The effects of Mo additions on the microstructure, microhardness and wear resistance of the cladding layer were studied by means of optical microscopy (OM), scanning electron microscope (SEM), X-ray diffraction (XRD), energy dispersive spectrometer (EDS), Vickers hardness tester and M-200 ring block wear tester. Research results showed that the microstructure of Mo-free cladding layer mainly consisted of matrix and eutectic structure. The matrix was martensite and retained austenite. The eutectic structure mainly consisted of M2(B,C) and M7(C,B)3 type of eutectic borocarbides. With the increase of Mo content, there was no significant change in the matrix. However, the eutectic structure was transformed from M2(B,C)- and M7(C,B)3-type borocarbides into M2(B,C)-, M7(C,B)3- and M23(C,B)6-type borocarbides. When the content of Mo is 4.0wt.%, the Mo2C-type carbide appear on the matrix, and parts of the borocarbide networks are broken. The change of microhardness of the cladding layer was not obvious with the increase of Mo content. But the increase of Mo content increases the wear resistance of the cladding layer. The wear resistance of cladding layer with 4.0wt.% Mo is 2.4 times as much as the cladding layer which is Mo-free.

A novel anti-frictional multiphase layer produced by plasma nitriding of PVD titanium coated ZL205A aluminum alloy

NASA Astrophysics Data System (ADS)

Lu, C.; Yao, J. W.; Wang, Y. X.; Zhu, Y. D.; Guo, J. H.; Wang, Y.; Fu, H. Y.; Chen, Z. B.; Yan, M. F.

2018-02-01

The heat treatment (consisting of solid solution and aging), is integrated with the nitriding process of titanium coated ZL205A aluminum alloy to improve the surface and matrix mechanical properties simultaneously. Two-step duplex treatment is adopted to prepare the gradient multiphase layer on a magnesium-free ZL205A aluminum-copper based alloy. Firstly, pure titanium film is deposited on the aluminum alloy substrate using magnetron sputtering. Secondly, the Ti-coated specimen is nitrided at the solid solution temperature of the substrate alloying elements in a gas mixture of N2 and H2 and aged at 175 °C. The microstructure evolution, microhardness as well as the wear resistance of obtained multiphase layers are investigated by means of scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectrometer (EDS), microhardness tester and pin-on-disc tribometer. The multiphase layer, dominated by TiN0.3 or Al3Ti, is prepared with significantly increased layer depth after duplex treatment. The surface hardness of multiphase layer is remarkably improved from 23.7HV to 457HV. The core matrix hardness is also increased to 65HV after aging. The wear rate of the multiphase layer decreases about 55.22% and 49.28% in comparison with the aged and Ti coated specimens, respectively. The predominant wear mechanism for the multiphase layer is abrasive and oxidation, but severe adhesive wear for the aged and Ti coated specimens.

Influence of Titanium Dioxide Nanoparticles on the Sulfate Attack upon Ordinary Portland Cement and Slag-Blended Mortars

PubMed Central

Atta-ur-Rehman; Qudoos, Abdul; Kim, Hong Gi

2018-01-01

In this study, the effects of titanium dioxide (TiO2) nanoparticles on the sulfate attack resistance of ordinary Portland cement (OPC) and slag-blended mortars were investigated. OPC and slag-blended mortars (OPC:Slag = 50:50) were made with water to binder ratio of 0.4 and a binder to sand ratio of 1:3. TiO2 was added as an admixture as 0%, 3%, 6%, 9% and 12% of the binder weight. Mortar specimens were exposed to an accelerated sulfate attack environment. Expansion, changes in mass and surface microhardness were measured. Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), X-ray Diffraction (XRD), Thermogravimetry Analysis (TGA) and Differential Scanning Calorimetry (DSC) tests were conducted. The formation of ettringite and gypsum crystals after the sulfate attack were detected. Both these products had caused crystallization pressure in the microstructure of mortars and deteriorated the mortars. Our results show that the addition of nano-TiO2 accelerated expansion, variation in mass, loss of surface microhardness and widened cracks in OPC and slag-blended mortars. Nano-TiO2 containing slag-blended mortars were more resistant to sulfate attack than nano-TiO2 containing OPC mortars. Because nano-TiO2 reduced the size of coarse pores, so it increased crystallization pressure due to the formation of ettringite and gypsum thus led to more damage under sulfate attack. PMID:29495616

Influence of tooth bleaching on dental enamel microhardness: a systematic review and meta-analysis.

PubMed

Zanolla, J; Marques, Abc; da Costa, D C; de Souza, A S; Coutinho, M

2017-09-01

Several studies have investigated the effect of bleaching on dental tissues. The evaluation of the effect of home bleaching with 10% carbamide peroxide is important for assessing alterations in enamel microhardness that may affect dental health in terms of resistance to masticatory forces. This meta-analysis was performed in order to determine scientific evidence regarding the effects of home vital bleaching with 10% carbamide peroxide gel on the microhardness of human dental enamel. A systematic electronic literature search was conducted in the PubMed and Web of Science databases using search terms. Two independent researchers evaluated the information and methodological quality of the studies. Inclusion and exclusion criteria were established for article selection; further, only studies published in English were selected. Thirteen studies that met all of the inclusion and exclusion criteria were selected and underwent statistical analysis. The results of this meta-analysis showed no significant changes in enamel microhardness when using the 10% carbamide peroxide bleaching gel over periods of 7, 14 and 21 days. © 2016 Australian Dental Association.

Effect of process parameters on microstructure and mechanical properties of friction stir welded joints: A review

NASA Astrophysics Data System (ADS)

Wanare, S. P.; Kalyankar, V. D.

2018-04-01

Friction stir welding is emerging as a promising technique for joining of lighter metal alloys due to its several advantages over conventional fusion welding processes such as low thermal distortion, good mechanical properties, fine weld joint microstructure, etc. This review article mainly focuses on analysis of microstructure and mechanical properties of friction stir welded joints. Various microstructure characterization techniques used by previous researchers such as optical microscopes, x-ray diffraction, electron probe microscope, transmission electron microscope, scanning electron microscopes with electron back scattered diffraction, electron dispersive microscopy, etc. are thoroughly overviewed and their results are discussed. The effects of friction stir welding process parameters such as tool rotational speed, welding speed, tool plunge depth, axial force, tool shoulder diameter to tool pin diameter ratio, tool geometry etc. on microstructure and mechanical properties of welded joints are studied and critical observations are noted down. The microstructure examination carried out by previous researchers on various zones of welded joints such as weld zone, heat affected zone and base metal are studied and critical remarks have been presented. Mechanical performances of friction stir welded joints based on tensile test, micro-hardness test, etc. are discussed. This article includes exhaustive literature review of standard research articles which may become ready information for subsequent researchers to establish their line of action.

Designing of silk and ZnO based antibacterial and noncytotoxic bionanocomposite films and study of their mechanical and UV absorption behavior.

PubMed

Kiro, Anamika; Bajpai, Jaya; Bajpai, A K

2017-01-01

Bionanocomposites of sericin and polyvinyl alcohol (PVA) were prepared by solution casting method and zinc oxide nanoparticles were impregnated within the polymer blend matrix through homogenous phase reaction between zinc chloride and sodium hydroxide at high temperature following an ex-situ co-precipitation method. The prepared bionanocomposites were characterized using Fourier Transform Infrared Spectroscopy, X-ray diffraction, Field Emission Scanning Electron Microscopy, Transmission Electron Microscopy and Atomic Force Microscopy techniques. The presence of characteristic groups of sericin and ZnO nanoparticles was ascertained by the FTIR spectra. XRD analysis confirmed the impregnation of ZnO nanoparticles and sericin within the PVA matrix. XRD and FESEM of the bionanocomposites provided information about their semicrystalline nature, crystallite size of the particles, and irregular rough surfaces. The TEM confirmed the size of ZnO particles to be in the nanometer range. AFM confirmed the platykurtic nature of the surface while the negative surface skewness shows the predominance of valleys over peaks suggesting for the planar nature of the surface of the bionanocomposites. UV absorption properties of bionanocomposite films were determined by UV absorption spectroscopy. UV absorption increased with increasing amount of ZnO nanoparticles in the nanocomposites. Sericin was found to absorb UV-C radiations between 200-290nm which is mainly due to aromatic amino acids like tryptophan, tyrosine and phenylalanine. The ZnO nanoparticles and sericin protein showed antimicrobial properties as evident from the inhibition zones obtained against Staphylococcus aureus and Escherichia coli. The bionanocomposite was found to be noncytotoxic which was proved by in vitro cytotoxicity test. Microhardness of bionanocomposite films increased with increase in the amount of ZnO nanoparticles in the sericin and PVA matrix. Copyright © 2016 Elsevier Ltd. All rights reserved.

Enamel Surface with Pit and Fissure Sealant Containing 45S5 Bioactive Glass.

PubMed

Yang, S-Y; Kwon, J-S; Kim, K-N; Kim, K-M

2016-05-01

Enamel demineralization adjacent to pit and fissure sealants leads to the formation of marginal caries, which can necessitate the replacement of existing sealants. Dental materials with bioactive glass, which releases ions that inhibit dental caries, have been studied. The purpose of this study was to evaluate the enamel surface adjacent to sealants containing 45S5 bioactive glass (BAG) under simulated microleakage between the material and the tooth in a cariogenic environment. Sealants containing 45S5BAG filler were prepared as follows: 0% 45S5BAG + 50.0% glass (BAG0 group), 12.5% 45S5BAG + 37.5% glass (BAG12.5 group), 25.0% 45S5BAG + 25.0% glass (BAG25.0 group), 37.5% 45S5BAG + 12.5% glass (BAG37.5 group), and 50.0% 45S5BAG + 0% glass (BAG50.0 group). A cured sealant disk was placed over a flat bovine enamel disk, separated by a 60-µm gap, and immersed in lactic acid solution (pH 4.0) at 37 °C for 15, 30, and 45 d. After the storage period, each enamel disk was separated from the cured sealant disk, and the enamel surface was examined with optical 3-dimensional surface profilometer, microhardness tester, and scanning electron microscopy. The results showed a significant increase in roughness and a decrease in microhardness of the enamel surface as the proportion of 45S5BAG decreased (P< 0.05). In the scanning electron microscopy images, enamel surfaces with BAG50.0 showed a smooth surface, similar to those in the control group with distilled water, even after prolonged acid storage. Additionally, an etched pattern was observed on the surface of the demineralized enamel with a decreasing proportion of 45S5BAG. Increasing the 45S5BAG filler contents of the sealants had a significant impact in preventing the demineralization of the enamel surface within microgaps between the material and the tooth when exposed to a cariogenic environment. Therefore, despite some marginal leakage, these novel sealants may be effective preventive dental materials for inhibiting secondary caries at the margins. © International & American Associations for Dental Research 2016.

Microstructure and wear characterization of aluminum matrix composites reinforced with industrial waste fly ash particulates synthesized by friction stir processing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dinaharan, I., E-mail: dinaweld2009@gmail.com

Fly ash (FA) is a waste product of coal combustion in thermal power plants which is available in massive quantities all over the world causing land pollution. This paper reports the characterization of AA6061 aluminum matrix composites (AMCs) reinforced with FA particles synthesized using friction stir processing (FSP). The volume fraction of FA particles was varied from 0 to 18 in steps of 6. The prepared AMCs were characterized using optical microscopy (OM), scanning electron microscopy (SEM) and electron backscattered diagram (EBSD). The wear rate was estimated using a pin-on-disc wear apparatus. FA particles were observed to be distributed homogeneouslymore » in the AMC irrespective of the location within the stir zone. The EBSD micrographs revealed remarkable grain refinement in the AMC. The incorporation of FA particles enhanced the microhardness and wear resistance of the AMC. The strengthening mechanisms of the AMC were discussed and correlated to the observed microstructures. The wear mechanisms were identified by characterizing the wear debris and worn surfaces. - Highlights: •Industrial waste fly ash was used to produce aluminum matrix composites. •Friction stir processing was used to produce AA6061/Fly Ash composite. •Fly ash particles refined the grains of aluminum matrix. •Fly ash particles enhanced the hardness and wear resistance. •Successful utilization of fly ash to make aluminum composites reduces land pollution.« less

Thermal oxidation behavior of an Al-Li-Cu-Mg-Zr alloy

NASA Astrophysics Data System (ADS)

Ahmad, Maqsood

1987-04-01

The chemical composition of oxide films formed during thermal treatments of an Al-Li-Cu-Mg-Zr alloy has been studied by means of Auger electron spectroscopy and X-ray photoelectron spectroscopy. The oxide layers formed after oxidation of 2.5 minutes to 30 minutes at 530 °C in lab air have been characterized. In the early stages of oxidation the surface is composed of both the lithium rich oxides and magnesium rich oxides. However, after longer oxidation times the oxidation of lithium becomes predominant and the air/oxide interface is completely covered by lithium compounds. Oxidation products formed on the alloy surface have been studied by X-ray diffraction analysis. The following three phases, namely, Li2CO3, α-Li5AlO4, and γ-LiAlO2, were identified. During heat treatment in lab air at 530 °C and at atmospheric pressure the dominating reaction product is Li2CO3. Due to the selective oxidation of lithium a soft surface layer is developed. The width of the soft layer formed during solution heat treatments carried out in lab air and in salt bath environments has been determined by microhardness measurements. The lithium concentration profiles were calculated from a diffusion equation. The depletion of alloying elements from the near surface region during heat treatments has been investigated using energy dispersive X-ray analysis. The oxide morphology was examined using scanning electron microscopy and optical microscopy.

Thermal oxidation behavior of an Al-Li-Cu-Mg-Zr alloy

NASA Astrophysics Data System (ADS)

Ahmad, Maqsood

1987-05-01

The chemical composition of oxide films formed during thermal treatments of an Al-Li-Cu-Mg-Zr alloy has been studied by means of Auger electron spectroscopy and X-ray photoelectron spectroscopy. The oxide layers formed after oxidation of 2.5 minutes to 30 minutes at 530 °C in lab air have been characterized. In the early stages of oxidation the surface is composed of both the lithium rich oxides and magnesium rich oxides. However, after longer oxidation times the oxidation of lithium becomes predominant and the air/oxide interface is completely covered by lithium compounds. Oxidation products formed on the alloy surface have been studied by X-ray diffraction analysis. The following three phases, namely, Li2CO3, α-Li5AlO4, and γ-LiAlO2, were identified. During heat treatment in lab air at 530 °C and at atmospheric pressure the dominating reaction product is Li2CO3. Due to the selective oxidation of lithium a soft surface layer is developed. The width of the soft layer formed during solution heat treatments carried out in lab air and in salt bath environments has been determined by microhardness measurements. The lithium concentration profiles were calculated from a diffusion equation. The depletion of alloying elements from the near surface region during heat treatments has been investigated using energy dispersive X-ray analysis. The oxide morphology was examined using scanning electron microscopy and optical microscopy.

Effects of dextrose and lipopolysaccharide on the corrosion behavior of a Ti-6Al-4V alloy with a smooth surface or treated with double-acid-etching.

PubMed

Faverani, Leonardo P; Assunção, Wirley G; de Carvalho, Paulo Sérgio P; Yuan, Judy Chia-Chun; Sukotjo, Cortino; Mathew, Mathew T; Barao, Valentim A

2014-01-01

Diabetes and infections are associated with a high risk of implant failure. However, the effects of such conditions on the electrochemical stability of titanium materials remain unclear. This study evaluated the corrosion behavior of a Ti-6Al-4V alloy, with a smooth surface or conditioned by double-acid-etching, in simulated body fluid with different concentrations of dextrose and lipopolysaccharide. For the electrochemical assay, the open-circuit-potential, electrochemical impedance spectroscopy, and potentiodynamic test were used. The disc surfaces were characterized by scanning electron microscopy and atomic force microscopy. Their surface roughness and Vickers microhardness were also tested. The quantitative data were analyzed by Pearson's correlation and independent t-tests (α = 0.05). In the corrosion parameters, there was a strong lipopolysaccharide correlation with the Ipass (passivation current density), Cdl (double-layer capacitance), and Rp (polarization resistance) values (p<0.05) for the Ti-6Al-4V alloy with surface treatment by double-acid-etching. The combination of dextrose and lipopolysaccharide was correlated with the Icorr (corrosion current density) and Ipass (p<0.05). The acid-treated groups showed a significant increase in Cdl values and reduced Rp values (p<0.05, t-test). According to the topography, there was an increase in surface roughness (R2 = 0.726, p<0.0001 for the smooth surface; R2 = 0.405, p = 0.036 for the double-acid-etching-treated surface). The microhardness of the smooth Ti-6Al-4V alloy decreased (p<0.05) and that of the treated Ti-6Al-4V alloy increased (p<0.0001). Atomic force microscopy showed changes in the microstructure of the Ti-6Al-4V alloy by increasing the surface thickness mainly in the group associated with dextrose and lipopolysaccharide. The combination of dextrose and lipopolysaccharide affected the corrosion behavior of the Ti-6Al-4V alloy surface treated with double-acid-etching. However, no dose-response corrosion behavior could be observed. These results suggest a greater susceptibility to corrosion of titanium implants in diabetic patients with associated infections.

Effects of Dextrose and Lipopolysaccharide on the Corrosion Behavior of a Ti-6Al-4V Alloy with a Smooth Surface or Treated with Double-Acid-Etching

PubMed Central

Faverani, Leonardo P.; Assunção, Wirley G.; de Carvalho, Paulo Sérgio P.; Yuan, Judy Chia-Chun; Sukotjo, Cortino; Mathew, Mathew T.; Barao, Valentim A.

2014-01-01

Diabetes and infections are associated with a high risk of implant failure. However, the effects of such conditions on the electrochemical stability of titanium materials remain unclear. This study evaluated the corrosion behavior of a Ti-6Al-4V alloy, with a smooth surface or conditioned by double-acid-etching, in simulated body fluid with different concentrations of dextrose and lipopolysaccharide. For the electrochemical assay, the open-circuit-potential, electrochemical impedance spectroscopy, and potentiodynamic test were used. The disc surfaces were characterized by scanning electron microscopy and atomic force microscopy. Their surface roughness and Vickers microhardness were also tested. The quantitative data were analyzed by Pearson's correlation and independent t-tests (α = 0.05). In the corrosion parameters, there was a strong lipopolysaccharide correlation with the Ipass (passivation current density), Cdl (double-layer capacitance), and Rp (polarization resistance) values (p<0.05) for the Ti-6Al-4V alloy with surface treatment by double-acid-etching. The combination of dextrose and lipopolysaccharide was correlated with the Icorr (corrosion current density) and Ipass (p<0.05). The acid-treated groups showed a significant increase in Cdl values and reduced Rp values (p<0.05, t-test). According to the topography, there was an increase in surface roughness (R2 = 0.726, p<0.0001 for the smooth surface; R2 = 0.405, p = 0.036 for the double-acid-etching-treated surface). The microhardness of the smooth Ti-6Al-4V alloy decreased (p<0.05) and that of the treated Ti-6Al-4V alloy increased (p<0.0001). Atomic force microscopy showed changes in the microstructure of the Ti-6Al-4V alloy by increasing the surface thickness mainly in the group associated with dextrose and lipopolysaccharide. The combination of dextrose and lipopolysaccharide affected the corrosion behavior of the Ti-6Al-4V alloy surface treated with double-acid-etching. However, no dose-response corrosion behavior could be observed. These results suggest a greater susceptibility to corrosion of titanium implants in diabetic patients with associated infections. PMID:24671257

Effect of various tooth-whitening products on enamel microhardness.

PubMed

Grobler, S R; Majeed, A; Moola, M H

2009-11-01

The purpose of this in vitro study was to evaluate the effect of various tooth-whitening products containing carbamide peroxide (CP) or hydrogen peroxide (HP), on enamel microhardness. Enamel blocks were exposed to: Nite White ACP 10% CP (Group 2, n=10); Yotuel Patient 10% CP (Group 3, n=10); Opalescence PF 10% CP (Group 4, n=10); Opalescence PF 20% CP (Group 5, n=10); Opalescence Treswhite Supreme 10% HP (Group 6, n=10); Yotuel 10 Minutes 30% CP (Group 7, n=10); Opalescence Quick 45% CP (Group 8, n=10), Yotuel Special 35% HP (Group 9, n=10), Opalescence Boost 38% HP (Group 10, n=10) according to the instructions of the manufacturers. The control (Group 1, n=10) was enamel blocks kept in artificial saliva at 37 degrees C without any treatment. The microhardness values were obtained before exposure and after a 14-day treatment period. Specimens were kept in artificial saliva at 37 degrees C between treatments. Data were analysed using Kruskal-Wallis one-way ANOVA and Tukey-Kramer Multiple Comparison Test. Indent marks on the enamel blocks were also examined under the Scanning Electron Microscope. All whitening products decreased enamel microhardness except group 10 but only Groups 2, 3, 4, 5 and 7 showed significant decrease in enamel microhardness as compared to the control group (p < 0.05). Groups 2, 3 and 7 differed significantly from all the other groups (p < 0.05). The highest damage was recorded for Group 2 (Nite White ACP 10% CP), which differed significantly from Groups 3 and 7. SEM images also showed damage to enamel. All products tested in this study decreased enamel microhardness except Opalescence Boost 38% HP. The products containing carbamide peroxide were more damaging to enamel because of the longer application times. Nite White ACP 10% CP showed the highest reduction in enamel microhardness as compared to other products tested.

Improving the Mechanical Properties of the Fusion Zone in Electron-Beam Welded Ti-5Al-5Mo-5V-3Cr Alloys

NASA Astrophysics Data System (ADS)

Marvel, Christopher J.; Sabol, Joseph C.; Pasang, Timotius; Watanabe, Masashi; Misiolek, Wojciech Z.

2017-04-01

It is well-known that ω-phase precipitates embrittle Ti-5553 alloys and that ω-phase embrittlement can be overcome with appropriate heat treatments. However, the microstructural evolution of electron-beam welded Ti-5553 is not as understood as compared to the cast or wrought material. This study compared the microstructures of as-welded and post-weld heat-treated specimens by scanning and transmission electron microscopy, and similarly compared the localized mechanical behavior of the fusion zones with microhardness testing and digital image correlation coupled tensile testing. The primary observations were that the embrittling ω-phase precipitates formed upon cooling, and could not be fully solutionized in a single-step treatment of 1077 K (804 °C) for 1 hour. It was also discovered that nanoscale α-phase precipitates nucleated after the single-step treatment, although they were small in number and sparsely distributed. However, a two-step heat treatment of 1077 K (804 °C) for 1 hour and 873 K (600 °C) for 4 hours completely solutionized the ω-phase and produced a dense network of 2- μm-wide α-phase plates, which significantly improved the mechanical properties. Overall, this study has shown that post-weld heat treatments improve the strength and ductility of electron-beam welded Ti-5553 alloys by controlling ω- and α-phase evolution.

Experimental research on microhardness and wear resistances of pure Cu subjected to surface dynamic plastic deformation by ultrasonic impact

NASA Astrophysics Data System (ADS)

Chen, Zhaoxia; He, Yangming

2018-04-01

Dynamic plastic deformation (DPD) has been induced in the surface of pure Cu by ultrasonic impact treating (UIT) with the varied impact current and coverage percentage. The microstructures of the treated surface were analyzed by a scanning electron microscope (SEM). And the wear resistance of pure Cu was experimentally researched both with the treated and untreated specimens. The effect of DPD on the hardness was also investigated using microhardness tester. The results show that the grains on the top surfaces of pure Cu are highly refined. The maximum depth of the plastic deformation layer is approximately 1400 µm. The larger the current and coverage percentage, the greater of the microhardness and wear resistance the treated surface layer of pure Cu will be. When the impact current is 2 A and coverage percentage is 300%, the microhardness and wear resistance of the treated sample is about 276.1% and 68.8% higher than that of the untreated specimen, respectively. But the properties of the treated sample deteriorate when the UIT current is 3 A and the coverage percentage is 300% because of the formation of a new phase forms in the treated surface.

Effect of Bonding Temperature on Interfacial Reaction and Mechanical Properties of Diffusion-Bonded Joint Between Ti-6Al-4V and 304 Stainless Steel Using Nickel as an Intermediate Material

NASA Astrophysics Data System (ADS)

Thirunavukarasu, Gopinath; Kundu, Sukumar; Mishra, Brajendra; Chatterjee, Subrata

2014-04-01

An investigation was carried out on the solid-state diffusion bonding between Ti-6Al-4V (TiA) and 304 stainless steel (SS) using pure nickel (Ni) of 200- μm thickness as an intermediate material prepared in vacuum in the temperature range from 973 K to 1073 K (700 °C to 800 °C) in steps of 298 K (25 °C) using uniaxial compressive pressure of 3 MPa and 60 minutes as bonding time. Scanning electron microscopy images, in backscattered electron mode, had revealed existence of layerwise Ti-Ni-based intermetallics such as either Ni3Ti or both Ni3Ti and NiTi at titanium alloy-nickel (TiA/Ni) interface, whereas nickel-stainless steel (Ni/SS) diffusion zone was free from intermetallic phases for all joints processed. Chemical composition of the reaction layers was determined in atomic percentage by energy dispersive spectroscopy and confirmed by X-ray diffraction study. Room-temperature properties of the bonded joints were characterized using microhardness evaluation and tensile testing. The maximum hardness value of ~800 HV was observed at TiA/Ni interface for the bond processed at 1073 K (800 °C). The hardness value at Ni/SS interface for all the bonds was found to be ~330 HV. Maximum tensile strength of ~206 MPa along with ~2.9 pct ductility was obtained for the joint processed at 1023 K (750 °C). It was observed from the activation study that the diffusion rate at TiA/Ni interface is lesser than that at the Ni/SS interface. From microhardness profile, fractured surfaces and fracture path, it was demonstrated that failure of the joints was initiated and propagated apparently at the TiA/Ni interface near Ni3Ti intermetallic phase.

Discontinuous Precipitation Reactions in Co-10Al-4C (At. Pct)

NASA Astrophysics Data System (ADS)

Kamali, H.; Hossein Nedjad, S.; Kaufman, M. J.; Field, R. D.; Clarke, A. J.

2018-05-01

The evolution of microstructure and microhardness of a Co-10Al-4C (at. pct) alloy during isothermal aging at 800 and 900 °C is reported. Fine κ-Co3AlC0.5 intermetallic precipitates form in an FCC α-Co matrix after aging at both temperatures. Lamellar discontinuous precipitation also occurred at grain boundaries and the lamellar transformation product consumed the fine κ-Co3AlC0.5 precipitates in the matrix during aging. The microhardness of the alloy decreased dramatically upon formation of the lamellar product. Transmission electron microscopy revealed that the lamellar product consists of α-Co, κ-Co3AlC0.5, and B2-CoAl phases at 800 °C. The orientation relationship between α-Co and κ-Co3AlC0.5 phases, and between α-Co and B2-CoAl phases were identified as cube-on-cube and Kurdjumov-Sachs, respectively. The discontinuous product at 900 °C was composed of alternating α-Co and κ-Co3AlC0.5 lamellae, without the B2-CoAl phase that formed at 800 °C. Additional continuous coarsening of κ-Co3AlC0.5 phase was observed in the lamellar aggregate during prolonged aging at 900 °C. The main driving force for the discontinuous reaction appears to be the reduction in both interfacial energy and elastic strain energy where the latter is attributed to the relatively high lattice mismatch between the κ-Co3AlC0.5 precipitates and the α-Co matrix.

Effect of cooling rate and Mg addition on the structural evaluation of rapidly solidified Al-20wt%Cu-12wt%Fe alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Karaköse, Ercan, E-mail: ekarakose@karatekin.edu.t

2016-11-15

The present work examines the effect of Mg contents and cooling rate on the morphology and mechanical properties of Al{sub 20}Cu{sub 12}Fe quasicrystalline alloy. The microstructure of the alloys was analyzed by scanning electron microscopy and the phase composition was identified by X-ray diffractometry. The melting characteristics were studied by differential thermal analysis under an Ar atmosphere. The mechanical features of the melt-spun and conventionally solidified alloys were tested by tensile-strength test and Vickers micro-hardness test. It was found that the final microstructure of the Al{sub 20}Cu{sub 12}Fe samples mainly depends on the cooling rate and Mg contents, which suggestsmore » that different cooling rates and Mg contents produce different microstructures and properties. The average grain sizes of the melt spun samples were about 100–300 nm at 35 m/s. The nanosize, dispersed, different shaped quasicrystal particles possessed a remarkable effect to the mechanical characteristics of the rapidly solidified ribbons. The microhardness values of the melt spun samples were approximately 18% higher than those of the conventionally counterparts. - Highlights: •Quasicrystal-creating materials have high potential for applications. •Different shaped nanosize quasicrystal particles were observed. •The addition of Mg has an important impact on the mechanical properties. •H{sub V} values of the MS0, MS3 and MS5 samples at 35 m/s were 8.56, 8.66 and 8.80 GPa. •The volume fraction of IQC increases with increasing cooling rates.« less

Microstructure, Wear Resistance and Oxidation Behavior of Ni-Ti-Si Coatings Fabricated on Ti6Al4V by Laser Cladding

PubMed Central

Zhuang, Qiaoqiao; Zhang, Peilei; Li, Mingchuan; Yan, Hua; Yu, Zhishui; Lu, Qinghua

2017-01-01

The Ni-Ti-Si composite coatings were successfully fabricated on Ti6Al4V by laser cladding. The microstructure were studied by SEM (scanning electron microscopy) and EDS (energy dispersive spectrometer). It has been found that Ti2Ni and Ti5Si3 phases exist in all coatings, and some samples have TiSi2 phases. Moreover, due to the existence of these phases, coatings presented relatively higher microhardness than that of the substrate (826 HV (Vickers hardness)) and the microhardness value of coating 3 is about twice larger than that of the substrate. During the dry sliding friction and wear test, due to the distribution of the relatively ductile phase of Ti2Ni and reinforcement phases of Ti5Si3 and TiSi2, the coatings performed good wear resistance. The oxidation process contains two stages: the rapid oxidation and slow oxidation by high temperature oxidation test at 800 °C for 50 h. Meanwhile, the value of the oxidation weight gain of the substrate is approximately three times larger than that of the coating 4. During the oxidation process, the oxidation film formed on the coating is mainly consisted of TiO2, Al2O3 and SiO2. Phases Ti2Ni, Ti5Si3, TiSi2 and TiSi were still found and it could be responsible for the improvement in oxidation resistance of the coatings by laser cladding. PMID:29084174

Meretrix lusoria--a natural biocomposite material: in situ analysis of hierarchical fabrication and micro-hardness.

PubMed

Zhu, Zhihong; Tong, Hua; Ren, Yaoyao; Hu, Jiming

2006-01-01

The ultrastructure of clam (Meretrix lusoria) was investigated by means of scanning electron microscope (SEM), transmission electron microscope (TEM) and X-ray diffraction analyzer (XRD) combining with in situ texture decalcified technique and the micro-hardness of clam was determined, in order to understand the spatial relationship between the mineral phase and organic matrix and further explain the correlation between the property and structure. The results showed that hierarchical fabrication is the major structure character of this mollusc shell. There is specific braided structure forming from domains composed of needle-like structure made up of the single crystal of aragonite. High magnification TEM image of clam indicates the intracrystal region of the aragonite single crystal is made up of subgrain phase and some amorphous substance. There are various crystal grain growth preferential orientations in the different growth direction of the shell. An amount of organic microtubule distribute evenly in the base of calcium carbonate as reinforcement phase. The mechanical property of this natural biological composite is better than other aragonite layer of mollusc shells and pearls according to the data of micro-hardness testing. The braided structure and organic microtubule reinforcement phase are responsible for its high mechanical performance. The stereo hierarchical fabrication of clam was elucidated for the first time.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paillard, Pascal

Two try-out campaigns of friction stir welding (FSW) were performed with different friction parameters to join S690QL high yield strength steel. The welds were investigated at macroscopic and microscopic scales using optical and electronic microscopy and microhardness mapping. Welds of the second campaign exhibit microstructures and mechanical properties in accordance with requirements for service use. Microtexture measurements were carried out in different zones of welds by electron backscattered diffraction (EBSD). It is shown that that texture of the bottom of the weld is similar to that of the base metal, suggesting a diffusion bonding mechanism. Finally, the mechanical properties (tensilemore » strength, resilience, bending) were established on the most promising welds. It is shown that it is possible to weld this high yield strength steel using FSW process with satisfactory geometric, microstructural and mechanical properties. - Highlights: •1000 mm ∗ 400 mm ∗ 8 mm S690QL steel plates are joined by friction stir welding (FSW). •Maximum hardness is reduced by optimization of process parameters. •Various microstructures are formed but no martensite after process optimization. •Texture is modified in mechanically affected zones of the weld. •Texture in the bottom of the weld is preserved, suggesting diffusion bonding.« less

Characterization of Multilayered Multipass Friction Stir Weld on ASTM A572 G50 Steel

DOE PAGES

Lim, Yong Chae; Sanderson, Samuel; Mahoney, Murray; ...

2014-01-01

A multilayered multipass friction stir weld (MM-FSW) on ASTM A572 Grade 50 steel was characterized to understand its potential application for thick-section structures. The 15-mm-thick section was fabricated by stacking up three steel plates and then friction stir welding the plates together in a total of 5 passes. The unique butt/lap joint configuration encountered in the multilayer weld was examined to understand the effect of tool rotation direction on the joint quality especially the formation of hooking defect. Charpy V-notch impact toughness tests showed generally higher impact toughness energy for the stir zone than the base metal with a ductilemore » fracture mode. The microhardness value was measured from 195 to 220 HV in the stir zone, while the base metal showed an average value of 170 HV. The microstructure in the stir zone and the adjacent heat affected zone was quantified using Optical and Scanning Electron Microscopy (SEM) including Electron Backscatter Diffraction (EBSD). The increased toughness and hardness were correlated with the refined microstructure in stir zone, resulting from severe plastic deformation and subsequent dynamic recrystallization during friction stir welding.« less

A study of the micro- and nanoscale deformation behavior of individual austenitic dendrites in a FeCrMoVC cast alloy using micro- and nanoindentation experiments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zeisig, J., E-mail: j.zeisig@ifw-dresden.de; Hufenbach, J.; Wendrock, H.

2016-04-04

Micro- and nanoindentation experiments were conducted to investigate the deformation mechanisms in a Fe79.4Cr13Mo5V1C1.6 (wt. %) cast alloy. This alloy consists of an as cast microstructure mainly composed of austenite, martensite, and a complex carbide network. During microhardness testing, metastable austenite transforms partially into martensite confirmed by electron backscatter diffraction. For nanoindentation tests, two different indenter geometries were applied (Berkovich and cube corner type). Load-displacement curves of nanoindentation in austenitic dendrites depicted pop-ins after transition into plastic deformation for both nanoindenters. Characterizations of the region beneath a nanoindent by transmission electron microscopy revealed a martensitic transformation as an activated deformationmore » mechanism and suggest a correlation with the pop-in phenomena of the load-displacement curves. Furthermore, due to an inhomogeneous chemical composition within the austenitic dendrites, more stabilized regions deform by mechanical twinning. This additional deformation mechanism was only observed for the cube corner indenter with the sharper geometry since higher shear stresses are induced beneath the contact area.« less

Recovery and recrystalization kinetics of cold-worked Zircaloy-4 plate and tubing (LWBR Development Program)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Katz, O.M.

1968-02-01

Empirical kinetic equations were derived to describe the recovery region between 550 and 1020/sup 0/F for times to 4000 hours for 15 to 78% cold-worked Zircaloy-4 plate and tubing. The properties studied were electrical resistivity and X-ray line sharpening. Recrystallization kinetics were described with sigmoidal curves derived from X-ray intensity and microhardness data. Light, replica, and transmission electron microscopy and selected-area electron diffraction were used to postulate recovery and recrystallization mechanisms. From a structural aspect, the annealing process in cold-worked Zircaloy-4 is visualized as a dislocation climb and annihilation process to the limit allowed by the size of the deformationmore » subcells, a reorientation of the subgrain material into a recrystallization texture, a growth of reoriented cells located in the most highly worked bands, and a consumption of less favorably strained and/or oriented cells by the high-angle boundaries of the reoriented cells. Comparison of 15 and 73% cold-worked tubing showed the activation energy to be less (21 versus 60 kcal/mol) and the subcell size greater (8000A versus 1000A) for the 15% cold-worked material. (NSA 22: 21698)« less

Studies on A-TIG welding of Low Activation Ferritic/Martensitic (LAFM) steel

NASA Astrophysics Data System (ADS)

Vasantharaja, P.; Vasudevan, M.

2012-02-01

Low Activation Ferritic-Martensitic steels (LAFM) are chosen as the candidate material for structural components in fusion reactors. The structural components are generally fabricated by welding processes. Activated Tungsten Inert Gas (A-TIG) welding is an emerging process for welding of thicker components. In the present work, attempt was made to develop A-TIG welding technology for LAFM steel plates of 10 mm thick. Activated flux was developed for LAFM steel by carrying out various bead-on-plate TIG welds without flux and with flux. The optimum flux was identified as one which gave maximum depth of penetration at minimum heat input values. With the optimized flux composition, LAFM steel plate of 10 mm thickness was welded in square butt weld joint configuration using double side welding technique. Optical and Scanning Electron Microscopy was used for characterizing the microstructures. Microhardness measurements were made across the weld cross section for as welded and post weld heat treated samples. Tensile and impact toughness properties were determined. The mechanical properties values obtained in A-TIG weld joint were comparable to that obtained in weld joints of LAFM steel made by Electron beam welding process.

Remineralisation of enamel white spot lesions pre-treated with chitosan in the presence of salivary pellicle.

PubMed

Zhang, Jing; Lynch, Richard J M; Watson, Timothy F; Banerjee, Avijit

2018-05-01

To investigate the remineralisation of chitosan pre-treated enamel white spot lesions (WSLs) by bioglass in the presence of the pellicle layer. 50 artificial enamel white spot lesions were created by acidic gel. Two lesions were used to investigate the formation of the pellicle layer by treating with human whole saliva for 3 min. 48 lesions were assigned to 6 experimental groups (n = 8): (1) bioactive glass slurry, (2) bioactive glass containing polyacrylic acid (BG + PAA) slurry, (3) chitosan pre-treated WSLs with BG slurry (CS-BG), (4) chitosan pre-treated WSLs with BG + PAA slurry (CS-BG + PAA), (5) "standard" remineralisation solution (RS) and (6) de-ionised water (negative control, NC). Remineralisation was carried out using a pH-cycling model for 7 days. Before each treatment using remineralising agents, 3-min pellicle was formed on lesions' surfaces. Mineral content changes, surface and subsurface microhardness and ultrastructure were evaluated by Raman intensity mapping, Knoop microhardness and scanning electron microscopy, respectively. Data were statistically analysed using one-way ANOVA with Tukey's test (p < 0.05 is considered as significant). Despite the heterogeneously formed pellicle layer, all groups showed an increase in surface mineral content after pH-cycling. Chitosan pre-treatment enhanced the subsurface remineralisation of WSLs using bioglass as both pre-treated groups showed greater surface and subsurface microhardness compared to NC. CS-BG exhibited denser subsurface structure than BG, while in CS-BG + PAA the crystals were bigger in size but resemble more enamel-like compared to BG + PAA as shown in SEM observations. Remineralisation of RS was limited to the surface as no significant subsurface changes of mechanical properties and structure were found. Chitosan pre-treatment can enhance WSL remineralisation with bioglass biomaterials when a short-term salivary pellicle is present. A further investigation using a long-term pH-cycling model with mature pellicle is suggested with regards to clinical application. Chitosan pre-treatment has the potential in clinical application to remineralise subsurface lesions to achieve lesion consolidation. Copyright © 2018 Elsevier Ltd. All rights reserved.

Joining and Integration of Silicon Nitride Ceramics for Aerospace and Energy Systems

NASA Technical Reports Server (NTRS)

Singh, M.; Asthana, R.

2009-01-01

Light-weight, creep-resistant silicon nitride ceramics possess excellent high-temperature strength and are projected to significantly raise engine efficiency and performance when used as turbine components in the next-generation turbo-shaft engines without the extensive cooling that is needed for metallic parts. One key aspect of Si3N4 utilization in such applications is its joining response to diverse materials. In an ongoing research program, the joining and integration of Si3N4 ceramics with metallic, ceramic, and composite materials using braze interlayers with the liquidus temperature in the range 750-1240C is being explored. In this paper, the self-joining behavior of Kyocera Si3N4 and St. Gobain Si3N4 using a ductile Cu-based active braze (Cu-ABA) containing Ti will be presented. Joint microstructure, composition, hardness, and strength as revealed by optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), Knoop microhardness test, and offset compression shear test will be presented. Additionally, microstructure, composition, and joint strength of Si3N4/Inconel 625 joints made using Cu-ABA, will be presented. The results will be discussed with reference to the role of chemical reactions, wetting behavior, and residual stresses in joints.

Micro friction stir lap welding of AISI 430 ferritic stainless steel: a study on the mechanical properties, microstructure, texture and magnetic properties

NASA Astrophysics Data System (ADS)

Mostaan, Hossein; Safari, Mehdi; Bakhtiari, Arash

2018-04-01

In this study, the effect of friction stir welding of AISI 430 (X6Cr17, material number 1.4016) ferritic stainless steel is examined. Two thin sheets with dimensions of 0.4 × 50 × 200 mm3 are joined in lap configuration. Optical microscopy and field emission electron microscopy were used in order to microstructural evaluations and fracture analysis, respectively. Tensile test and microhardness measurements are employed in order to study the mechanical behaviors of welds. Also, vibrational sample magnetometry (VSM) is employed for characterizing magnetic properties of welded samples. Texture analysis is carried out in order to clarify the change mechanism of magnetic properties in the welded area. The results show that AISI 430 sheets are successfully joined considering both, the appearance of the welding bead and the strength of the welded joint. It is found that by friction stir welding of AISI 430 sheets, texture components with easy axes magnetization have been replaced by texture components with harder magnetization axes. VSM analysis showed that friction stir welding leads to increase in residual induction (Br) and coercivity (Hc). This increase is attributed to the grain refining due the friction stir welding and formation of texture components with harder axes of magnetizations.

Tribological behavior of Al-WC nano-composites fabricated by ultrasonic cavitation assisted stir-cast method

NASA Astrophysics Data System (ADS)

Pal, Arpan; Poria, Suswagata; Sutradhar, Goutam; Sahoo, Prasanta

2018-03-01

In the present study, the effects of WC nano-particles content on the microstructure, hardness, wear, and friction behavior of aluminum matrix composites are investigated. Al-WC nano composites with varying wt% of WC (0, 1, 1.5, and 2) are fabricated using ultrasonic cavitation assisted stir-cast method. The microstructure of the nano-composite samples is analyzed using optical microscopy and scanning electron microscopy. Elemental composition is determined by energy dispersive x-ray analysis. Vicker’s microhardness test is performed in different locations on the composite sample surface with a load of 50 gf and 10s dwell time. Wear and friction of the composites under dry sliding is studied using a pin-on-disk tribotester for varying normal load (10–40 N) and sliding speed (0.1–0.4 m/s). Uniform distribution of nano-WC is observed over composite surface without noticeable clustering. Reinforcement of nano-WC particles improves wear resistance and frictional behavior of the composite. Hardness is seen to increase with increase in wt% of nano-particles. Wear behavior of composites depends on formation of layers over the surface mixed with oxidized debris and counter-face particles. Wear mechanism changes from adhesion to abrasion with increase in wt% of hard nano particles.

Microstructure and Mechanical Properties of Laser Solid Formed Ti-6Al-4V Alloy Under Dynamic Shear Loading

NASA Astrophysics Data System (ADS)

Zhou, Ping; Guo, Wei-Guo; Su, Yu; Wang, Jianjun; Lin, Xin; Huang, Weidong

2017-07-01

To investigate the mechanical properties of the Ti-6Al-4V alloy fabricated by laser solid forming technology, both static and dynamic shear tests were conducted on hat-shaped specimens by a servohydraulic testing machine and an enhanced split Hopkinson pressure bar system, over a temperature range of 173-573 K. The microstructure of both the original and deformed specimens was characterized by optical microscopy and scanning electron microscopy. The results show that: (1) the anisotropy of shear properties is not significant regardless of the visible stratification and the prior- β grains that grow epitaxially along the depositing direction; (2) the ultimate shear strength of this material is lower than that of those Ti-6Al-4V alloys fabricated by forging and extrusion; (3) the adiabatic shear bands of approximately 25.6-36.4 μm in width can develop at all selected temperatures during the dynamic shear deformation; and (4) the observed microstructure and measured microhardness indicate that the grains become refined in adiabatic shear band. Estimation of the temperature rise shows that the temperature in shear band exceeds the recrystallization temperature. The process of rotational dynamic recrystallization is considered to be the cause of the grain refinement in shear band.

Effect of heat treatment on microstructure and hardness of Grade 91 steel

DOE PAGES

Shrestha, Triratna; Alsagabi, Sultan; Charit, Indrajit; ...

2015-01-21

The modified 9Cr-1Mo steel (Grade 91) is a material of choice in fossil-fuel-fired power plants with increased efficiency, service life, and reduction in emission of greenhouse gases. It is also considered a prospective material for the Next Generation Nuclear Power Plant for application in reactor pressure vessels at temperatures up to 650°C. In this paper, heat treatment of the modified 9Cr-1Mo steel was studied by normalizing and tempering the steel at various temperatures and times, with the ultimate goal of improving its creep resistance and optimizing material hardness. The microstructural evolution of the heat treated steels was correlated with themore » differential scanning calorimetric results. Optical microscopy, scanning and transmission electron microscopy in conjunction with microhardness profiles and calorimetric plots were used to understand the evolution of microstructure including precipitate structures in modified 9Cr-1Mo steel and relate it to the mechanical behavior of the steel. Thermo-CalcTM calculations were used to support experimental work and provide guidance in terms of the precipitate stability and microstructural evolution. Furthermore, the carbon isopleth and temperature dependencies of the volume fraction of different precipitates were constructed. The predicted and experimentally observed results were found to be in good agreement.« less

Fracture Analysis of 40Cr Steel Pin Roll

NASA Astrophysics Data System (ADS)

Li, Yong; Jia, Youlu; Xie, Xianjiao

2018-01-01

Fracture of 40Cr steel pin roll happened along the cross-section at the spot of filling aperture. By the use of analysis of optical microscopy and microhardness, it can be known that filling aperture and its nitration case (ε phase) and large amounts of non-metal inclusions (bulk obscure inclusions) in steel were the main reasons which led to the facture of 40Cr steel pin roll.

The Influence of Hot-Rolled Temperature on Plasma Nitriding Behavior of Iron-Based Alloys

NASA Astrophysics Data System (ADS)

El-Hossary, F. M.; Khalil, S. M.; Lotfy, Kh.; Kassem, M. A.

2009-07-01

Experiments were performed with an aim of studying the effect of hot-rolled temperature (600 and 900°C) on radio frequency (rf) plasma nitriding of Fe93Ni4Zr3 alloy. Nitriding was carried out for 10 min in a nitrogen atmosphere at a base pressure of 10-2 mbarr. Different continuous plasma processing powers of 300-550 W in steps 50 W or less were applied. Nitrided hot-rolled specimens were characterized by optical microscopy (OM), X-ray diffraction (XRD) and microhardness measurements. The results reveal that the surface of hot-rolled rf plasma nitrided specimens at 600°C is characterized with a fine microstructure as a result of the high nitrogen solubility and diffusivity. Moreover, the hot-rolled treated samples at 600°C exhibit higher microhardness value than the associated values of hot-rolled treated samples at 900°C. The enhancement of microhardness is due to precipitation and predominance of new phases ( γ and ɛ phases). Mainly, this conclusion has been attributed to the high defect densities and small grain sizes of the samples hot-rolled at 600°C. Generally, the refinement of grain size plays a dramatic role in improvement of mechanical properties of tested samples.

The Effect of Constant and Pulsed Current Gas Tungsten Arc Welding on Joint Properties of 2205 Duplex Stainless Steel to 316L Austenitic Stainless Steel

NASA Astrophysics Data System (ADS)

Neissi, R.; Shamanian, M.; Hajihashemi, M.

2016-05-01

In this study, dissimilar 316L austenitic stainless steel/2205 duplex stainless steel (DSS) joints were fabricated by constant and pulsed current gas tungsten arc welding process using ER2209 DSS as a filler metal. Microstructures and joint properties were characterized using optical and electron scanning microscopy, tensile, Charpy V-notch impact and micro-hardness tests, and cyclic polarization measurements. Microstructural observations confirmed the presence of chromium nitride and delta ferrite in the heat-affected zone of DSS and 316L, respectively. In addition, there was some deviation in the austenite/ferrite ratio of the surface welding pass in comparison to the root welding pass. Besides having lower pitting potential, welded joints produced by constant current gas tungsten arc welding process, consisted of some brittle sigma phase precipitates, which resulted in some impact energy reduction. The tensile tests showed high tensile strength for the weld joints in which all the specimens were broken in 316L base metal.

Matrix coatings based on anodic alumina with carbon nanostructures in the pores

NASA Astrophysics Data System (ADS)

Gorokh, G. G.; Pashechko, M. I.; Borc, J. T.; Lozovenko, A. A.; Kashko, I. A.; Latos, A. I.

2018-03-01

The nanoporous anodic alumina matrixes thickness of 1.5 mm and pore sizes of 45, 90 and 145 nm were formed on Si substrates. The tubular carbon nanostructures were synthesized into the matrixes pores by pyrolysis of fluid hydrocarbon xylene with 1% ferrocene. The structure and composition of the matrix coatings were examined by scanning electron microscopy, Auger analysis and Raman spectroscopy. The carbon nanostructures completely filled the pores of templates and uniformly covered the tops. The structure of carbon nanostructures corresponded to the structure of multiwall carbon nanotubes. Investigations of mechanical and tribological properties of nanostructured oxide-carbon composite performed by scratching and nanoindentation showed nonlinear dependencies of the frictional force, penetration depth of the cantilever, hardness and plane strain modulus on the load. It was found that the microhardness of the samples increases with reduced of alumina pore diameter, and the penetration depth of the cantilever into the film grows with carbon nanostructures size. The results showed the high mechanical strength of nanostructured oxide-carbon composite.

Comparative characteristic and erosion behavior of NiCr coatings deposited by various high-velocity oxyfuel spray processes

NASA Astrophysics Data System (ADS)

Sidhu, Hazoor Singh; Sidhu, Buta Singh; Prakash, S.

2006-12-01

The purpose of this study is to analyze and compare the mechanical properties and microstructure details at the interface of high-velocity oxyfuel (HVOF)-sprayed NiCr-coated boiler tube steels, namely ASTM-SA-210 grade A1, ASTM-SA213-T-11, and ASTM-SA213-T-22. Coatings were developed by two different techniques, and in these techniques liquefied petroleum gas was used as the fuel gas. First, the coatings were characterized by metallographic, scanning electron microscopy/energy-dispersive x-ray analysis, x-ray diffraction, surface roughness, and microhardness, and then were subjected to erosion testing. An attempt has been made to describe the transformations taking place during thermal spraying. It is concluded that the HVOF wire spraying process offers a technically viable and cost-effective alternative to HVOF powder spraying process for applications in an energy generation power plant with a point view of life enhancement and to minimize the tube failures because it gives a coating having better resistance to erosion.

Al-TiC in situ composite coating fabricated by low power pulsed laser cladding on AZ91D magnesium alloy

NASA Astrophysics Data System (ADS)

Yang, Liuqing; Li, Zhiyong; Zhang, Yingqiao; Wei, Shouzheng; Liu, Fuqiang

2018-03-01

Al + (Ti + B4C) composite coating was cladded on AZ91D magnesium alloy by a low power pulsed Nd-YAG laser. The Ti+B4C mixed powder is with the ratio of Ti: B4C = 5:1, which was then mixed with Al powder by weight fraction of 10%, 15% and 20%, respectively. Scanning electron microscopy, energy dispersive spectrometer and X-ray diffraction were used to study the microstructure, chemical composition and phase composition of the coating. Results showed that the coating had satisfied metallurgical bonding with the magnesium substrate. Al3Mg2, Al12Mg17, Al3Ti and TiC were formed by in-situ reaction. The coatings have micro-hardness of 348HV, which is about 5-6 times higher than that of AZ91D. The wear resistance and corrosion resistance of the coatings are enhanced with the addition of the mixed powder.

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy

PubMed Central

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-01-01

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition. PMID:28774103

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy.

PubMed

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-12-05

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition.

Effects of pulsed CO2 laser in caries selective ablation

NASA Astrophysics Data System (ADS)

Colojoara, Carmen; David, Ion; Marinovici, Mariana

1995-03-01

We have evaluated the effect of pulsed carbon dioxide laser in the treatment for deep carious decay. The so called `caries profonda' is still a problem for conservative dentistry. A `Valvfivre' Master 20S carbon dioxide laser was pulsed to determine the effects on dentine and for testing the properties of softened dentine in selective ablation. Laser treatment parameters were from 1 to 2 W, 50 to 150 ms, 200 to 320 Hz. Fifteen human teeth samples were exposed to irradiation: extracted third molar were exposed to CO2 pulsed laser to determine in vitro the effects on pulp morphology. The tissue samples were analyzed histologically and by means of scanning electron microscopy for evidence of thermal damage. Next, we have evaluated the morphologic changes in vivo on 10 cases in patients with deep carious decay. Pulsed infrared lasers are capable of inducing physical and chemical changes in dentine structure. The results showed an artificially sclerosing and micro-hardness on the remaining dentine. CO2 laser can vaporized carious dentine.

Proving the viability of manufacturing of multi-layer steel/vanadium alloy/steel composite tubes by numerical simulations and experiment

NASA Astrophysics Data System (ADS)

Nechaykina, T.; Nikulin, S.; Rozhnov, A.; Molotnikov, A.; Zavodchikov, S.; Estrin, Y.

2018-05-01

Vanadium alloys are promising structural materials for fuel cladding tubes for fast-neutron reactors. However, high solubility of oxygen and nitrogen in vanadium alloys at operating temperatures of 700 °C limits their application. In this work, we present a novel composite structure consisting of vanadium alloy V-4Ti-4Cr (provides high long-term strength of the material) and stainless steel Fe-0.2C-13Cr (as a corrosion resistant protective layer). It is produced by co-extrusion of these materials forming a three-layered tube. Finite element simulations were utilised to explore the influence of the various co-extrusion parameters on manufacturability of multi-layered tubes. Experimental verification of the numerical modelling was performed using co-extrusion with the process parameters suggested by the numerical simulations. Scanning electron microscopy and microhardness measurements revealed a defect-free diffusion layer at the interfaces between both materials indicating a good quality bonding for these co-extrusion conditions.

Effect of 2D WS2 Addition on Cold-Sprayed Aluminum Coating

NASA Astrophysics Data System (ADS)

Loganathan, Archana; Rengifo, Sara; Hernandez, Alexander Franco; Emirov, Yusuf; Zhang, Cheng; Boesl, Benjamin; Karthikeyan, Jeganathan; Agarwal, Arvind

2017-10-01

Tungsten disulfide (WS2) has excellent solid lubrication properties due to its 2D layered structure. This study focuses on depositing Al-2 wt.% WS2 composite coating by cold spray technique. The effect of WS2 addition on the microstructure, mechanical and tribological properties of the composite coatings is examined in the as-deposited and heat-treated conditions. After heat treatment, the coating density increased to 99% with improved intersplat bonding. The microhardness of the heat-treated Al-2 wt.% WS2 coating increased by 56% as compared to the as-sprayed coating. The wear resistance of heat-treated Al-2 wt.% WS2 coating improved by 75% with a synergistic reduction in the coefficient of friction (COF) by 51%. Transmission electron microscopy investigation reveals the presence of layered WS2 within aluminum splats with a strong interface. This study shows that cold spraying can be effectively used to integrate 2D layered WS2 as a solid lubricant in the metallic coatings.

Cracking in dissimilar laser welding of tantalum to molybdenum

NASA Astrophysics Data System (ADS)

Zhou, Xingwen; Huang, Yongde; Hao, Kun; Chen, Yuhua

2018-06-01

Dissimilar joining of tantalum (Ta) to molybdenum (Mo) is of great interest in high temperature structural component applications. However, few reports were found about joining of these two hard-to-weld metals. The objective of this experimental study was to assess the weldability of laser butt joining of 0.2 mm-thick Ta and Mo. In order to study cracking mechanism in Ta/Mo joint, similar Ta/Ta and Mo/Mo joints were compared under the same welding conditions. An optical microscope observation revealed presence of intergranular cracks in the Mo/Mo joint, while both transgranular and intergranular cracks were observed in Ta/Mo joint. The cracking mechanism of the Ta/Mo joint was investigated further by micro-hardness testing, micro X-ray diffraction and scanning electron microscopy. The results showed that solidification cracking tendency of Mo is a main reason for crack initiation in the Ta/Mo joint. Low ductility feature in fusion zone most certainly played a role in the transgranular propagation of cracking.

Microstructure and Mechanical Behavior of Microwave Sintered Cu50Ti50 Amorphous Alloy Reinforced Al Metal Matrix Composites

NASA Astrophysics Data System (ADS)

Reddy, M. Penchal; Ubaid, F.; Shakoor, R. A.; Mohamed, A. M. A.

2018-06-01

In the present work, Al metal matrix composites reinforced with Cu-based (Cu50Ti50) amorphous alloy particles synthesized by ball milling followed by a microwave sintering process were studied. The amorphous powders of Cu50Ti50 produced by ball milling were used to reinforce the aluminum matrix. They were examined by x-ray diffraction (XRD), scanning electron microscopy (SEM), microhardness and compression testing. The analysis of XRD patterns of the samples containing 5 vol.%, 10 vol.% and 15 vol.% Cu50Ti50 indicates the presence of Al and Cu50Ti50 peaks. SEM images of the sintered composites show the uniform distribution of reinforced particles within the matrix. Mechanical properties of the composites were found to increase with an increasing volume fraction of Cu50Ti50 reinforcement particles. The hardness and compressive strength were enhanced to 89 Hv and 449 MPa, respectively, for the Al-15 vol.% Cu50Ti50 composites.

Effect of powders refinement on the tribological behavior of Ni-based composite coatings by laser cladding

NASA Astrophysics Data System (ADS)

Wang, Lingqian; Zhou, Jiansong; Yu, Youjun; Guo, Chun; Chen, Jianmin

2012-06-01

NiCr + Cr3C2 + Ag + BaF2/CaF2 composite coatings were produced on stainless steel (1Cr18Ni9Ti) substrates by laser cladding. Corresponding powders were prepared by high-energy ball milling technique. The friction and wear behavior at room temperature was investigated through sliding against the Si3N4 ball. The morphologies of the wear debris, worn surfaces of both samples and the Si3N4 ball were analyzed by scanning electron microscopy and three dimensional non-contact surface mapping. Results showed that milling time had a great effect on the size, morphology, uniformity of the powders as well as the microstructure and properties of laser cladding coatings. The wear mechanism of the coatings is dominated by abrasive wear, plastic deformation and slight adhesive wear. The consecutive evolution trend of friction coefficient, wear rate as well as microhardness of the serials of coatings produced with powders of different sizes was presented.

Effect of electric discharge machining on the fatigue life of Inconel 718

NASA Technical Reports Server (NTRS)

Jeelani, S.; Collins, M. R.

1988-01-01

The effect of electric discharge machining on the fatigue life of Inconel 718 alloy at room temperature was investigated. Data were generated in the uniaxial tension fatigue mode at ambient temperature using flat 3.175 mm thick specimens. The specimens were machined on a wire-cut electric discharge machine at cutting speeds ranging from 0.5 to 2 mm per minute. The specimens were fatigued at a selected stress, and the resulting fatigue lives compared with that of the virgin material. The surfaces of the fatigued specimens were examined under optical and scanning electron microscopes, and the roughness of the surfaces was measured using a standard profilometer. From the results of the investigation, it was concluded that the fatigue life of the specimens machined using EDM decreased slightly as compared with that of the virgin material, but remained unchanged as the cutting speed was changed. The results are explained using data produced employing microhardness measurements, profilometry, and optical and scanning microscopy.

Gigacycle fatigue behavior by ultrasonic nanocrystalline surface modification.

PubMed

Ahn, D G; Amanov, A; Cho, I S; Shin, K S; Pyoun, Y S; Lee, C S; Park, I G

2012-07-01

Nanocrystalline surface layer up to 84 microm in thick is produced on a specimen made of Al6061-T6 alloy by means of surface treatment called ultrasonic nanocrystalline surface modification (UNSM) technique. The refined grain size is produced in the top-layer and it is increased with increasing depth from the top surface. Vickers microhardness measurement for each nanocrystalline surface layer is performed and measurement results showed that the microhardness is increased from 116 HV up to 150 HV, respectively. In this study, fatigue behavior of Al6061-T6 alloy was studied up to 10(7)-10(9) cycles by using a newly developed ultrasonic fatigue testing (UFT) rig. The fatigue results of the UNSM-treated Al6061-T6 alloy specimens were compared with those of the untreated specimens. The microstructure of the untreated and UNSM-treated specimens was characterized by means of scanning electron microscopey (SEM) and transmission electron microscopey (TEM).

Electron Beam Welding of IN792 DS: Effects of Pass Speed and PWHT on Microstructure and Hardness

PubMed Central

Angella, Giuliano; Montanari, Roberto; Richetta, Maria; Varone, Alessandra

2017-01-01

Electron Beam (EB) welding has been used to realize seams on 2 mm-thick plates of directionally solidified (DS) IN792 superalloy. The first part of this work evidenced the importance of pre-heating the workpiece to avoid the formation of long cracks in the seam. The comparison of different pre-heating temperatures (PHT) and pass speeds (v) allowed the identification of optimal process parameters, namely PHT = 300 °C and v = 2.5 m/min. The microstructural features of the melted zone (MZ); the heat affected zone (HAZ), and base material (BM) were investigated by optical microscopy (OM), scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS), electron back-scattered diffraction (EBSD), X-ray diffraction (XRD), and micro-hardness tests. In the as-welded condition; the structure of directionally oriented grains was completely lost in MZ. The γ’ phase in MZ consisted of small (20–40 nm) round shaped particles and its total amount depended on both PHT and welding pass speed, whereas in HAZ, it was the same BM. Even if the amount of γ’ phase in MZ was lower than that of the as-received material, the nanometric size of the particles induced an increase in hardness. EDS examinations did not show relevant composition changes in the γ’ and γ phases. Post-welding heat treatments (PWHT) at 700 and 750 °C for two hours were performed on the best samples. After PWHTs, the amount of the ordered phase increased, and the effect was more pronounced at 750 °C, while the size of γ’ particles in MZ remained almost the same. The hardness profiles measured across the joints showed an upward shift, but peak-valley height was a little lower, indicating more homogeneous features in the different zones. PMID:28872620

Laser welding of NiTi shape memory alloy: Comparison of the similar and dissimilar joints to AISI 304 stainless steel

NASA Astrophysics Data System (ADS)

Mirshekari, G. R.; Saatchi, A.; Kermanpur, A.; Sadrnezhaad, S. K.

2013-12-01

The unique properties of NiTi alloy, such as its shape memory effect, super-elasticity and biocompatibility, make it ideal material for various applications such as aerospace, micro-electronics and medical device. In order to meet the requirement of increasing applications, great attention has been given to joining of this material to itself and to other materials during past few years. Laser welding has been known as a suitable joining technique for NiTi shape memory alloy. Hence, in this work, a comparative study on laser welding of NiTi wire to itself and to AISI 304 austenitic stainless steel wire has been made. Microstructures, mechanical properties and fracture morphologies of the laser joints were investigated using optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction analysis (XRD), Vickers microhardness (HV0.2) and tensile testing techniques. The results showed that the NiTi-NiTi laser joint reached about 63% of the ultimate tensile strength of the as-received NiTi wire (i.e. 835 MPa) with rupture strain of about 16%. This joint also enabled the possibility to benefit from the pseudo-elastic properties of the NiTi component. However, tensile strength and ductility decreased significantly after dissimilar laser welding of NiTi to stainless steel due to the formation of brittle intermetallic compounds in the weld zone during laser welding. Therefore, a suitable modification process is required for improvement of the joint properties of the dissimilar welded wires.

Nanocrystalline-grained tungsten prepared by surface mechanical attrition treatment: Microstructure and mechanical properties

NASA Astrophysics Data System (ADS)

Guo, Hong-Yan; Xia, Min; Wu, Zheng-Tao; Chan, Lap-Chung; Dai, Yong; Wang, Kun; Yan, Qing-Zhi; He, Man-Chao; Ge, Chang-Chun; Lu, Jian

2016-11-01

A nanostructured surface layer was fabricated on commercial pure tungsten using the method of surface mechanical attrition treatment (SMAT). The microstructure evolution of the surface layer was characterized by using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) and its formation mechanism was discussed as well. Both refinement and elongation of the brittle W grains were confirmed. The elongated SMATed W was heavily strained, the maximum value of the strain at the grain boundaries reaches as high as 3-5%. Dislocation density in the SMATed W nanograins was found to be 5 × 1012 cm-2. The formation of the nanograins in the top surface layer of the W was ascribed to the extremely high strain and strain rate, as well as the multidirectional repetitive loading. Bending strength of commercial W could be improved from 825 MPa to 1850 MPa by SMAT process. Microhardness results indicated the strain range in SMATed W can reach up to 220 μm beneath the top surface. The notched Charpy testing results demonstrated that SMATed W possess higher ductility than that of commercial W. The top surface of the W plates with and without SMATe processing possesses residual compressive stress of about -881 MPa and -234 MPa in y direction, and -872 MPa and -879 MPa in x direction respectively. The improvement of toughness (DBTT shift) of SMATed W may be the synergistic effect of residual compressive stress, dislocation density improvement and microstructure refinement induced by SMAT processing. SMAT processing could be a complementary method to further decrease the DBTT value of tungsten based materials.

Effect of pulse frequency on microstructural, nanomechanical, and wear properties of electrodeposited Ni-TiN composite coatings

NASA Astrophysics Data System (ADS)

Xia, Fafeng; Tian, Jiyu; Ma, Chunyang; Potts, Matt; Guo, Xue

2014-12-01

The current paper reports successful syntheses of Ni-TiN composite coatings by pulse electrodeposition. The effect of pulse frequency on the microstructures, nanomechanical, and wear properties of the coatings was investigated using transmission electron microscopy, X-ray diffraction, nanoindenter, scanning electron microscopy, and wear test instrument. The results showed that the Ni-TiN composite coating prepared at the pulse frequency of 100 Hz showed the presence of a less number of TiN particles and some degrees of aggregation in micro-regions. By contrast, in the Ni-TiN coating deposited at the pulse frequency of 500 Hz, the TiN particles were large in number and dispersed homogeneously, thereby, offering the coating a uniform and fine structure. The average grain diameters of Ni and TiN in the coating prepared at 100 Hz were 154.7 and 44.8 nm, respectively, whereas those for the coating prepared at 500 Hz were 67.3 and 25.9 nm, respectively. The maximum TiN content in the Ni-TiN coating deposited at 800 Hz was approximately 10.5 wt. %. The maximum microhardness and the Young's modulus values for the Ni-TiN composite coatings deposited at 800 Hz were 35.7 GPa and 167.4 GPa, respectively. Furthermore, the Ni-TiN composite coating prepared at 100 Hz had more severe damages, whereas the morphologies of worn surface of the coatings deposited at 500 Hz and 800 Hz were smooth and only a few small pits appeared on the surface.

Preparation and properties of calcium-silicate filled resins for dental restoration. Part II: Micro-mechanical behaviour to primed mineral-depleted dentine.

PubMed

Profeta, Andrea Corrado

2014-11-01

Evaluating microtensile bond strength (μTBS) and Knoop micro-hardness (KHN) of resin bonded-dentine interfaces created with two methacrylate-based systems either incorporating Bioglass 45S5 (3-E&RA/BG) or MTA (3-E&RA/WMTA). Solvated resins (50% ethanol/50% co-monomers) were used as primers while their neat counterparts were filled with the two calcium-silicate compounds. Application of neat resin adhesive with no filler served as control (3-E&RA). μTBS, KHN analysis and confocal tandem scanning microscopy (TSM) micropermeability were carried out after 24 h and 10 months of storage in phosphate buffer solution (DPBS). Scanning electron microscopy (SEM) was also performed after debonding. High μTBS values were achieved in all groups after 24 h of DPBS storage. On the contrary, solely the specimens created using 3-E&RA/BG and 3-E&RA/WMTA agents showed no significant reduction in terms of μTBS even after 10 months in DPBS; similarly, they did not restore the average superficial micro-hardness to the level of sound dentine, but maintained unchanged KHN values, and no statistical decrease was found following 10 months of DPBS storage. The only statistically significant changes occurred in the resin-dentine interfaces bonded with 3-E&RA that were subjected to a reduction of both μTBS and KHN values with ageing. In terms of micropermeability, adverse results were obtained with 3-E&RA while 3-E&RA/BG and 3-E&RA/WMTA demonstrated a beneficial effect after prolonged DPBS storage. Calcium-silicate filled composite resins performed better than a current etch-and-rinse adhesive and had a therapeutic/protective effect on the micro-mechanical properties of mineral-depleted resin-dentine interfaces. The incorporation of calcium-silicates into dental restorative and bonding agents can create more biomimetic (life-like) restorations. This will not only enable these materials to mimic the physical characteristics of the tooth structure, but will also stabilize and protect the remaining dental hard tissues.

Effect of the scanning speed on microstructural evolution and wear behaviors of laser cladding NiCrBSi composite coatings

NASA Astrophysics Data System (ADS)

Chen, J. L.; Li, J.; Song, R.; Bai, L. L.; Shao, J. Z.; Qu, C. C.

2015-09-01

Laser cladding composite coatings were fabricated on the surface of the Ti6Al4V substrate by fiber laser cladding the NiCrBSi alloy powder. The influences of scanning speed on the dilution rate and microstructure of the coatings were investigated in detail by X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). Combined with the analyses of microhardness and fracture toughness, the wear behaviors of the coatings obtained at different scanning speeds were revealed. Results indicated that the dilution rates of the coatings were similar (about 64.23%) with variations in scanning speed ranging from 5 mm/s to 15 mm/s. An abrupt decrease in dilution rate (37.06%) was observed at the scanning speed of 20 mm/s. Microstructural observation showed that the blocky TiB2 and the cellular dendrite TiC particles were uniformly dispersed in the TiNi-Ti2Ni dual-phase intermetallic compound matrix at scanning speeds of 5-15 mm/s. When the scanning speed was further increased to 20 mm/s, the stripe-shaped CrB, gray irregular-shaped Cr3C2 and black blocky TiC particles uniformly dispersed in the γ(Ni) matrix were synthesized in situ. The particles became finer with the increase in scanning speed. The average microhardness of the coating (1026.5 HV0.2) at the scanning speed of 20 mm/s was enhanced significantly compared with that of the other three coatings (about 886.4 HV0.2). The lowest average friction coefficient (about 0.371) was obtained at the scanning speed of 20 mm/s and was relatively stable with the change in sliding time. The lowest wear loss of the coating was also obtained at the scanning speed of 20 mm/s. Analyses of the worn surfaces showed that the coating prepared at the scanning speed of 20 mm/s was in good condition because of its excellent combination of resistance to micro-cutting and brittle debonding. Comparatively speaking, the coating produced at the scanning speed of 20 mm/s possessed excellent comprehensive mechanical properties.

Safety of nonthermal atmospheric pressure plasma for tooth bleaching evaluated in terms of microhardness and mineral content

NASA Astrophysics Data System (ADS)

Nam, S. H.; Hong, J. W.; Lee, H. J.; Jeon, Y. C.; Kim, G. C.

2017-08-01

The purpose of this study was to evaluate the influence of bleaching with nonthermal atmospheric pressure plasma and 15% hydrogen peroxide (HP) or 15% carbamide peroxide (CP). Sixty human enamel and dentin slabs were randomly assigned to six groups as follows: Group 1 was a control group and did not receive any treatment; Group 2 was exposed only to plasma, as a negative control; Group 3 was treated with 15% HP; Group 4 was treated with 15% HP plus plasma; Group 5 was treated with 15% CP alone; and Group 6 was treated with 15% CP plus plasma during 30 min bleaching treatments. A microhardness measurement was conducted according to a microhardness tester. The amount of calcium (Ca), phosphorus (P), chloride (Cl), sodium (Na), magnesium (Mg), and zinc (Zn) in the enamel and dentin was quantified with an electron probe microanalyzer (EPMA). The data were analyzed by using the Student’s t test and one-way analysis of variance (ANOVA), complemented by Tukey’s test. The statistical analysis did not show any significant differences in microhardness values and six mineral contents in all groups (p  >  0.05). Therefore, we believe that the application of nonthermal atmospheric pressure plasma is a safe energy source for tooth bleaching.

Effect of Naturally Acidic Agents on Microhardness and Surface Micromorphology of Restorative Materials

PubMed Central

Hengtrakool, Chanothai; Kukiattrakoon, Boonlert; Kedjarune-Leggat, Ureporn

2011-01-01

Objectives: This study investigated the titratable acidity and erosive potential of acidic agents on the microhardness and surface micromorphology of four restorative materials. Methods: Forty-seven discs of each restorative material; metal-reinforced glass ionomer cement (Ketac-S), resin-modified glass ionomer cement (Fuji II LC), resin composite (Filtek Z250) and amalgam (Valiant-Ph.D.), 12 mm in diameter and 2.5 mm in thickness, were divided into four groups (5 discs/group). Specimens were then immersed for 7 days into four storage media; deionized water (control), citrate buffer solution, green mango juice and pineapple juice. Microhardness testing before and after immersions was performed. Micromorphological changes were evaluated under a scanning electron microscope (SEM). Statistical significance among each group was analyzed using two-way repeated ANOVA and Tukey’s tests. Results: The Fuji II LC and the Ketac-S showed the highest reduction in microhardness (P<.05). The Valiant-Ph.D. and the Filtek Z250 showed some minor changes over the period of 7 days. The mango juice produced the greatest degradation effect (P<.05). Conclusions: This study suggested that for restorations in patients who have tooth surface loss, materials selected should be considered. In terms of materials evaluated, amalgam and resin composite are the most suitable for restorations. PMID:21311608

Microstructure and Microhardness of 17-4PH Deposited with Co-based Alloy Hardfacing Coating

NASA Astrophysics Data System (ADS)

Deng, D. W.; Zhang, C. P.; Chen, R.; Xia, H. F.

Hardfacing is widely used to improve the performance of components exposed to severe service conditions. In this paper, the surface modification was evaluated for precipitation hardening martensitic stainless steel 17-4PH deposited with Co-based alloy stellite12 by the plasma-transferred arc welding (PTAW). The microstructure and microhardness of coating and heat affected zone(HAZ) of base metal were characterized by optical microscope (OM), scanning electron scanning microscope (SEM), X-ray diffractometer and hardness tester. The results show that the interface between weld metal and base metal is favorable without pore and crack, at the same time elements diffusion is observed in the fusion area. However, as the distance from the interface increases, HAZ comprises three different microstructural zones, namely, zones of coarse overheated structures, quenching martensite and martensite, ferrite. The microhardness decreases gradually from the HAZ near interface to the base metal, except the zone of coarse overheated structures. The microhardness of the coating improves a lot and fluctuates in a definitive range, and microstructural gradient is observed including the fusion area (the planar region and the bulky dendrite in a direction perpendicular to the weld interface), the transition zone (the dendrite in a multi-direction way) and the fine grain zone near the surface in the coating (fine equiaxial structure).

Surface laser alloying of 17-4PH stainless steel steam turbine blades

NASA Astrophysics Data System (ADS)

Yao, Jianhua; Wang, Liang; Zhang, Qunli; Kong, Fanzhi; Lou, Chenghua; Chen, Zhijun

2008-09-01

As a known high-quality precipitation hardening stainless steel with high strength, high antifatigue, excellent corrosion resistance and good weldability, 17-4PH has been widely used to produce steam turbine blades. However, under the impact of high-speed steam and water droplets, the blades are prone to cavitation, which could lead to lower efficiency, shorter life time, and even accidents. In this article, the 17-4PH blade's surface was alloyed using a high power CO 2 laser. The microstructure and microhardness of hardened 17-4PH were tested by scanning electronic microscope (SEM), X-ray diffraction (XRD), energy disperse spectroscopy (EDS) and a microhardness tester. After laser alloying, the surface layer was denser and the grain refined, while the microhardness of the surface (average 610HV 0.2) was about one times higher than that of the substrate material (330HV 0.2). The friction coefficient of the laser-alloyed 17-4PH layer was much lower than that of the substrate.

Laboratory comparison of the mechanical properties of TRUShape with several nickel-titanium rotary instruments.

PubMed

Elnaghy, A M; Elsaka, S E

2017-08-01

To assess and compare the mechanical properties of TRUShape (TRS) with several nickel-titanium rotary instruments. Cyclic fatigue, torsional resistance, flexibility and surface microhardness of TRS (size 25, 0.06v taper), ProTaper Next X2 (PTN X2, size 25, 0.06 taper), ProTaper Gold (PTG F2; size 25, 0.08 taper) and ProTaper Universal (PTU F2; size 25, 0.08 taper) instruments were evaluated. The topographical structures of the fracture surfaces of instruments were assessed using a scanning electron microscope. The cyclic fatigue resistance, torsional resistance and microhardness data were analysed using one-way analysis of variance (anova) and Tukey's post hoc tests. The fragment length and bending resistance data were analysed statistically with the Kruskal-Wallis H-test and Mann-Whitney U-tests. The statistical significance level was set at P < 0.05. PTN and PTG instruments revealed significantly higher resistance to cyclic fatigue than TRS and PTU instruments (P < 0.001). PTN instruments revealed significantly higher torsional resistance compared with the other instruments (P < 0.001). PTG instrument had significantly higher flexibility than the other tested brands (P < 0.05). However, for microhardness, the PTU had significantly higher surface microhardness values compared with other tested brands (P < 0.05). TRS instruments had lower resistance to cyclic fatigue and lower flexibility compared with PTG and PTN instruments. TRS, PTG and PTU instruments had lower resistance to torsional stress than PTN instruments. TRS and PTG instruments had comparable surface microhardness. © 2016 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Effects of tooth whitening and orange juice on surface properties of dental enamel.

PubMed

Ren, Yan-Fang; Amin, Azadeh; Malmstrom, Hans

2009-06-01

To study the effects of 6% H2O2 activated with LED light on surface enamel as compared to orange juice challenges in vitro. A total of 40 human enamel discs were incubated in saliva overnight to allow pellicle formation and then divided into three groups: 15 for whitening treatments, 15 for orange juice immersions and 10 for normal saline controls. Baseline microhardness was measured with a microhardness Knoop indenter (50g, 10s) and surface topography was evaluated with a focus-variation 3D scanning microscopy. Enamel discs were treated with H2O2 or orange juice for 20 min each cycle for five cycles to simulate daily treatment with the products for 5 days. The discs were stored in saliva between treatment cycles. Microhardness and surface topography were evaluated again after treatments. Changes in microhardness and in surface area roughness (Sa), mean maximum peak-to-valley distance (Sz) and the developed surface area ratio (Sdr) were compared before and after treatments (t-test) and among groups (ANOVA). Enamel surface hardness decreased by 84% after orange juice immersion but no statistically significant changes were observed in the whitening and control groups. Surface topography changed significantly only in the orange juice group as shown by increased Sa (1.2 microm vs. 2.0 microm), Sz (7.7 microm vs. 10.2 microm) and Sdr (2.8% vs. 6.0%). No such changes were observed in the whitening and control groups. In comparison to orange juice challenges, the effects of 6% H2O2 on surface enamel are insignificant. Orange juice erosion markedly decreased hardness and increased roughness of enamel.

TiF4 varnish protects the retention of brackets to enamel after in vitro mild erosive challenge.

PubMed

Medeiros, Maria Isabel Dantas de; Carlo, Hugo Lemes; Santos, Rogério Lacerda Dos; Sousa, Frederico Barbosa; Castro, Ricardo Dias de; França, Renata Cristina Sobreira; Carvalho, Fabíola Galbiatti de

2018-05-14

The effect of fluoride agents on the retention of orthodontic brackets to enamel under erosive challenge is little investigated. The aim of this study was to evaluate the effect of titanium tetrafluoride (TiF4) and sodium fluoride (NaF) agents on the shear bond strength of brackets to enamel and on the enamel microhardness around brackets under erosive challenge. Brackets were bonded to bovine incisors. Five groups were formed according to fluoride application (n=10): TiF4 varnish, TiF4 solution, NaF varnish, NaF solution and control (without application). The specimens were submitted to erosive challenge (90 s cola drink/2h artificial saliva, 4x per day for 7 days). Solutions were applied before each erosive cycle and varnishes were applied once. Vickers Microhardness (VHN) was obtained before and after all cycles of erosion and the percentage of microhardness loss was calculated. Shear bond strength, adhesive remnant index and polarized light microscopy were conducted after erosion. The data were analyzed by ANOVA, Tukey, Kruskal-Wallis and Mann-Whitney U tests (α=0.05). The %VHN had no statistically significant differences among the experimental groups. However, considering the comparisons of all groups with the control group, TiF4 varnish showed the highest protection from enamel demineralization (effect size of 2.94, while the effect size for the other groups was >2.4). The TiF4 varnish group had significantly higher shear bond strength compared to other groups. There was no difference among groups for adhesive remnant index. Polarized light microscopy showed higher demineralization depth for the control group. Application of NaF and TiF4 agents during mild erosive challenge minimized the enamel mineral loss around brackets, however only the experimental TiF4 varnish was able to prevent the reduction of shear bond strength of brackets to enamel.

Microstructural Development and Technical Challenges in Laser Additive Manufacturing: Case Study with a 316L Industrial Part

NASA Astrophysics Data System (ADS)

Marya, Manuel; Singh, Virendra; Marya, Surendar; Hascoet, Jean Yves

2015-08-01

Additive manufacturing (AM) brings disruptive changes to the ways parts, and products are designed, fabricated, tested, qualified, inspected, marketed, and sold. These changes introduce novel technical challenges and concerns arising from the maturity and diversity of today's AM processes, feedstock materials, and process parameter interactions. AM bears a resemblance with laser and electron beam welding in the so-called conduction mode, which involves a multitude of dynamic physical events between the projected feedstock and a moving heat source that eventually influence AM part properties. For this paper, an air vent was selected for its thin-walled, hollow, and variable cross section, and limited size. The studied air vents, randomly selected from a qualification batch, were fabricated out of 316L stainless steel using a 4 kW fiber laser powder-fed AM system, referred to as construction laser additive direct (CLAD). These were systematically characterized by microhardness indentation, visual examination, optical and scanning electron microscopy, and electron-back-scattering diffraction in order to determine AM part suitability for service and also broadly discuss metallurgical phenomena. The paper then briefly expands the discussion to include additional engineering alloys and further analyze relationships between AM process parameters and AM part properties, consistently utilizing past experience with the same powder-fed CLAD 3D printer, the well-established science and technology of welding and joining, and recent publications on additive manufacturing.

Characteristics microstructure and microhardness of cast Ti-6Al-4V ELI for biomedical application submitted to solution treatment

NASA Astrophysics Data System (ADS)

Damisih, Jujur, I. Nyoman; Sah, Joni; Agustanhakri, Prajitno, Djoko Hadi

2018-05-01

Ti 6Al-4V ELI (Extra Low Interstitial)alloy containing 6wt% of aluminum, 4wt% of vanadium with controlled level of iron and oxygen is one of most popular alloy employed in biomedical applications as implant material. Heat treatment process for titanium alloys becomes important and could be performed by some of different ways in order to develop microstructure as well as its properties. The objective of this paper is to study the effects of solution treatment temperature on microstructure and mechanical properties of as-cast Ti-6Al-4V ELI especially microhardness value. The alloy was melted by single arc melting furnace with a water-cooled copper crucible hearth under argon atmosphere and then casted. It was heat treated through solution treatment at 3 (three) different temperaturesi.e. 850°C, 950°C and 1050°C in an argon gas atmosphere for around 30 minutes. After solution treatment, samples were water quenched and then aged at temperature of 500°C for 4 hours. To investigate its microstructure, the alloy was investigated under optical microscope and scanning electron microscope (SEM). It was observed Widmanstätten microstructure consisting of mixture α and β phase with basket-weave pattern. The Vickers microhardness test was performed and the results exhibited the optimum value was obtained at temperature of 950°C of solution treatment. From the observation, it revealed that the heat treatment has substantial effect on microstructural properties where microhardness increased due to formation of α' martensite structure. It was showed also that solution treatment followed by aging could improve mechanical properties especially microhardness value of Ti-6Al-4V ELI alloy. These results were suggesting the optimized conditions of heat treatment to obtain the best microstructure properties and microhardness value.

Effect of Nano-Y2O3 on Microstructure and Crack Formation in Laser Direct-Deposited In Situ Particle-Reinforced Fe-Based Coatings

NASA Astrophysics Data System (ADS)

Yin, Guili; Chen, Suiyuan; Liu, Yuanyuan; Liang, Jing; Liu, Changsheng; Kuang, Zheng

2018-03-01

In situ hard-particle-reinforced Fe-based composite coatings were prepared on Q235 steel substrates by direct laser deposition using Fe-based alloy powders containing 2 wt.% B, 3 wt.% Si and 1-3 wt.% nano-Y2O3. The microstructures, phase compositions, hardnesses and wear resistances of the deposited coatings with different nano-Y2O3 contents were studied using metallographic microscopy, scanning electron microscopy, x-ray diffraction, transmission electron microscopy, microhardness tests and pin-on-disk abrasion tests (MMW-1A), respectively. The results showed that the appropriate addition of Y2O3 played a role in grain refinement and in decreasing the number of brittle phases and impurity elements in the grain boundaries. Consequently, the number of cracks in the laser-deposited coating also decreased. The Fe-based composite coatings were mainly composed of α-Fe, γ-Fe and in situ-produced reinforced particle phases, such as Cr23C6, Cr7C3, (Cr, Fe)7C3, Fe2B, and CrFeB. When the content of nano-Y2O3 was 2 wt.%, a Fe-based composite coating with a thickness of 4 mm that was free of cracks was obtained, and its surface hardness reached 650HV. Moreover, the wear resistance of the coating with 2 wt.% nano-Y2O3 was the best among the samples studied. The presence of nano-Y2O3 increased the solubility of Cr and Si in the solid solution, which eliminated the residual austenite region, and as a result, the phase transformation from γ-Fe to α-Fe was restrained and the transformation stress was also limited, thereby decreasing the probability of cracks in the coatings.

Creep Deformation, Rupture Analysis, Heat Treatment and Residual Stress Measurement of Monolithic and Welded Grade 91 Steel for Power Plant Components

NASA Astrophysics Data System (ADS)

Shrestha, Triratna

Modified 9Cr-1 Mo (Grade 91) steel is currently considered as a candidate material for reactor pressure vessels (RPVs) and reactor internals for the Very High Temperature Reactor (VHTR), and in fossil-fuel fired power plants at higher temperatures and stresses. The tensile creep behavior of Grade 91 steel was studied in the temperature range of 600°C to 750°C and stresses between 35 MPa and 350 MPa. Heat treatment of Grade 91 steel was studied by normalizing and tempering the steel at various temperatures and times. Moreover, Thermo-Ca1c(TM) calculation was used to predict the precipitate stability and their evolution, and construct carbon isopleths of Grade 91 steel. Residual stress distribution across gas tungsten arc welds (GTAW) in Grade 91 steel was measured by the time-of-flight neutron diffraction using the Spectrometer for Materials Research at Temperature and Stress (SMARTS) diffractometer at Lujan Neutron Scattering Center, Los Alamos National Laboratory, Los Alamos, NM, USA. Analysis of creep results yielded stress exponents of ˜9-11 in the higher stress regime and ˜1 in the lower stress regime. The creep behavior of Grade 91 steel was described by the modified Bird-Mukherjee-Dorn relation. The rate-controlling creep deformation mechanism in the high stress regime was identified as the edge dislocation climb with a stress exponent of n = 5. On the other hand, the deformation mechanism in the Newtonian viscous creep regime (n = 1) was identified as the Nabarro-Herring creep. Creep rupture data were analyzed in terms of Monkman-Grant relation and Larson-Miller parameter. Creep damage tolerance factor and stress exponent were used to identify the cause of creep damage. The fracture surface morphology of the ruptured specimens was studied by scanning electron microscopy to elucidate the failure mechanisms. Fracture mechanism map for Grade 91 steel was developed based on the available material parameters and experimental observations. The microstructural evolution of heat treated steel was correlated with the differential scanning calorimetric study. The combination of microstructural studies with optical microscopy, scanning and transmission electron microscopy, microhardness profiles, and calorimetric plots helped in the understanding of the evolution of microstructure and precipitates in Grade 91 steel. The residual stresses were determined at the mid-thickness of the plate, 4.35 mm and 2.35 mm below the surface of the as-welded and post-weld heat treated plate. The residual stresses of the as-welded plate were compared with the post-weld heat treated plate. The post-weld heat treatment significantly reduced the residual stress in the base metal, heat affected zone, and the weld zone. Vickers microhardness profiles of the as-welded, and post-weld heat treated specimens were also determined and correlated with the observed residual stress profile and microstructure.

Effect of bioactive glass-containing resin composite on dentin remineralization.

PubMed

Lee, Myoung Geun; Jang, Ji-Hyun; Ferracane, Jack L; Davis, Harry; Bae, Han Eul; Choi, Dongseok; Kim, Duck-Su

2018-05-25

The purpose of this study was to evaluate the effect of bioactive glass (BAG)-containing composite on dentin remineralization. Sixty-six dentin disks with 3 mm thickness were prepared from thirty-three bovine incisors. The following six experimental groups were prepared according to type of composite (control and experimental) and storage solutions (simulated body fluid [SBF] and phosphate-buffered saline [PBS]): 1 (undemineralized); 2 (demineralized); 3 (demineralized with control in SBF); 4 (demineralized with control in PBS); 5 (demineralized with experimental composite in SBF); and 6 (demineralized with experimental composite in PBS). BAG65S (65% Si, 31% Ca, and 4% P) was prepared via the sol-gel method. The control composite was made with a 50:50 Bis-GMA:TEGDMA resin matrix, 57 wt% strontium glass, and 15 wt% aerosol silica. The experimental composite had the same resin and filler, but with 15 wt% BAG65S replacing the aerosol silica. For groups 3-6, composite disks (20 × 10 × 2 mm) were prepared and approximated to the dentin disks and stored in PBS or SBF for 2 weeks. Micro-hardness measurements, attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR) and field-emission scanning electron microscopy (FE-SEM) was investigated. The experimental BAG-containing composite significantly increased the micro-hardness of the adjacent demineralized dentin. ATR-FTIR revealed calcium phosphate peaks on the surface of the groups which used experimental composite. FE-SEM revealed surface deposits partially occluding the dentin surface. No significant difference was found between SBF and PBS storage. BAG-containing composites placed in close proximity can partially remineralize adjacent demineralized dentin. Copyright © 2018. Published by Elsevier Ltd.

Glass ceramic obtained by tailings and tin mine waste reprocessing from Llallagua, Bolivia

NASA Astrophysics Data System (ADS)

Arancibia, Jony Roger Hans; Villarino, Cecilia; Alfonso, Pura; Garcia-Valles, Maite; Martinez, Salvador; Parcerisa, David

2014-05-01

In Bolivia Sn mining activity produces large tailings of SiO2-rich residues. These tailings contain potentially toxic elements that can be removed into the surface water and produce a high environmental pollution. This study determines the thermal behaviour and the viability of the manufacture of glass-ceramics from glass. The glass has been obtained from raw materials representative of the Sn mining activities from Llallagua (Bolivia). Temperatures of maximum nucleation rate (Tn) and crystallization (Tcr) were calculated from the differential thermal analyses. The final mineral phases were determined by X-ray diffraction and textures were observed by scanning electron microscopy. Crystalline phases are nefeline occurring with wollastonite or plagioclase. Tn for nepheline is between 680 ºC and 700 ºC, for wollastonite, 730 ºC and for plagioclase, 740 ºC. Tcr for nefeline is between 837 and 965 ºC; for wollastonite, 807 ºC and for plagioclase, 977 ºC. In order to establish the mechanical characteristics and efficiency of the vitrification process in the fixation of potentially toxic elements the resistance to leaching and micro-hardness were determined. The obtained contents of the elements leached from the glass ceramic are well below the limits established by the European legislation. So, these analyses confirm that potentially toxic elements remain fixed in the structure of mineral phases formed in the glass-ceramic process. Regarding the values of micro-hardness results show that they are above those of a commercial glass. The manufacture of glass-ceramics from mining waste reduces the volume of tailings produced for the mining industry and, in turn enhances the waste, transforming it into a product with industrial application. Acknowledgements: This work was partly financed by the project AECID: A3/042750/11, and the SGR 2009SGR-00444.

Deletion of epithelial cell-specific Cdc42 leads to enamel hypermaturation in a conditional knockout mouse model.

PubMed

Tian, Zhihui; Lv, Xiaolin; Zhang, Min; Wang, Xueer; Chen, Yinghua; Tang, Pei; Xu, Pengcheng; Zhang, Lu; Wu, Buling; Zhang, Lin

2018-04-21

Recent evidence suggests that GTPases Rho family plays an important role in tooth development; however, the role of Cdc42 in tooth development remains unclear. We aimed to investigate the function of Cdc42 in tooth development and amelogenesis. We generated an epithelial cell-specific K5-Cdc42 knockout (KO) mouse to evaluate post-eruption dental phenotypes using a K5-Cre driver line. This model overcomes the previously reported perinatal lethality. Tooth phenotypes were analyzed by micro X-ray, micro-computed tomography (CT), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), wear rate, shear strength, and a microhardness test. Enamel matrix protein expression was determined by immunohistochemistry. KO mice displayed a hypomaturation phenotype, including incisors that lacked yellow pigmentation and were abnormally white, rapid attrition of molars following eruption, and decreased micro-hardness and shearing strength. Micro-CT data revealed that of incisor and molar enamel volumes were smaller in the KO than in wild-type (WT) mice. SEM analysis showed that the enamel prism structure was disordered. In addition, HE staining indicated a remarkable difference in the ameloblast morphology and function between KO and WT mice, and immunohistochemistry showed increased expression of amelogenin, ameloblastin, matrix metallopeptidase 20, kallikrein-related peptidase 4 and amelotin in the KO mice teeth. Our results suggest epithelium cell-specific Cdc42 deletion leads to tooth hypomaturation and transformation of the enamel prism structure that is likely due to altered ameloblast morphology and the secretion of enamel matrix proteins and proteases. This is the first in vivo evidence suggesting that Cdc42 is essential for proper tooth development and amelogenesis. Copyright © 2018. Published by Elsevier B.V.

In vitro evaluation of enamel demineralization after several overlapping CO2 laser applications.

PubMed

Vieira, K A; Steiner-Oliveira, C; Soares, L E S; Rodrigues, L K A; Nobre-dos-Santos, M

2015-02-01

This study aimed to evaluate the effects of repeated CO2 laser applications on the inhibition of enamel demineralization. Sixty-five human dental enamel slabs were randomly assigned to the following groups (n = 13): control (C), one application of the CO2 laser (L1), two applications of the CO2 laser (L2), three applications of the CO2 laser (L3), and four applications of the CO2 laser (L4). Enamel slabs were irradiated by a 10.6-μm CO2 laser operating at 5 J/cm(2). The slabs were subjected to a pH-cycling regimen and then analyzed by FT-Raman spectroscopy, energy-dispersive X-ray fluorescence spectrometry (EDXRF), cross-sectional micro-hardness, and scanning electron microscopy (SEM). Statistical analysis was performed using ANOVA and Tukey tests (p < 0.05). FT-Raman spectroscopy showed a reduced carbonate content for L1, L3, and L4 groups when compared to C (p < 0.05). The EDXRF data showed no statistical differences between the control and irradiated groups for calcium and phosphorus components (p > 0.05). Cross-sectional micro-hardness data showed a statistically significant difference between the control and all irradiated groups (p < 0.05), but no difference was found among the irradiated groups (p > 0.05) up to 30-μm depth. A tendency of lower demineralization occurred in deeper depths for L3 and L4 groups. The SEM results showed that with repeated applications of the CO2 laser, a progressive melting and recrystallization of the enamel surface occurred. Repeated irradiations of dental enamel may enhance the inhibition of enamel demineralization.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fayomi, O. S. I., E-mail: ojosundayfayomi3@gmail.com; Department of Mechanical Engineering, Covenant University, P.M.B. 1023, Canaanland, Ota; Popoola, A. P. I.

This paper studies effects of the composite particle infringement of ZnO/Cr{sub 2}O{sub 3} on zinc rich ternary based coating. The corrosion-degradation property in 3.5% NaCl was investigatedusing polarization technique. The structural characteristics of the multilayer produce coatings were evaluated by scanning electron microscope (SEM) equipped with an energy dispersive spectrometer (EDS). The mechanical response of the coated samples was studied using a diamond base Dura –Scan) micro-hardness tester and a MTR-300 dry abrasive wear tester. The combined effect of the coatings gave highly-improved performance on microhardness, corrosion and wear damage. This also implies that protection of wind-energy structures in marinemore » environments can be achieved by composite strengthening capacity.« less

The Femtosecond Laser Ablation on Ultrafine-Grained Copper

NASA Astrophysics Data System (ADS)

Lu, Jianxun; Wu, Xiaoyu; Ruan, Shuangchen; Guo, Dengji; Du, Chenlin; Liang, Xiong; Wu, Zhaozhi

2018-07-01

To investigate the effects of femtosecond laser ablation on the surface morphology and microstructure of ultrafine-grained copper, point, single-line scanning, and area scanning ablation of ultrafine-grained and coarse-grained copper were performed at room temperature. The ablation threshold gradually increased and materials processing became more difficult with decreasing grain size. In addition, the ablation depth and width of the channels formed by single-line scanning ablation gradually increased with increasing grain size for the same laser pulse energy. The microhardness of the ablated specimens was also evaluated as a function of laser pulse energy using area scanning ablation. The microhardness difference before and after ablation increased with decreasing grain size for the same laser pulse energy. In addition, the microhardness after ablation gradually decreased with increasing laser pulse energy for the ultrafine-grained specimens. However, for the coarse-grained copper specimens, no clear changes of the microhardness were observed after ablation with varying laser pulse energies. The grain sizes of the ultrafine-grained specimens were also surveyed as a function of laser pulse energy using electron backscattered diffraction (EBSD). The heat generated by laser ablation caused recrystallization and grain growth of the ultrafine-grained copper; moreover, the grain size gradually increased with increasing pulse energy. In contrast, no obvious changes in grain size were observed for the coarse-grained copper specimens with increasing pulse energy.

The Femtosecond Laser Ablation on Ultrafine-Grained Copper

NASA Astrophysics Data System (ADS)

Lu, Jianxun; Wu, Xiaoyu; Ruan, Shuangchen; Guo, Dengji; Du, Chenlin; Liang, Xiong; Wu, Zhaozhi

2018-05-01

To investigate the effects of femtosecond laser ablation on the surface morphology and microstructure of ultrafine-grained copper, point, single-line scanning, and area scanning ablation of ultrafine-grained and coarse-grained copper were performed at room temperature. The ablation threshold gradually increased and materials processing became more difficult with decreasing grain size. In addition, the ablation depth and width of the channels formed by single-line scanning ablation gradually increased with increasing grain size for the same laser pulse energy. The microhardness of the ablated specimens was also evaluated as a function of laser pulse energy using area scanning ablation. The microhardness difference before and after ablation increased with decreasing grain size for the same laser pulse energy. In addition, the microhardness after ablation gradually decreased with increasing laser pulse energy for the ultrafine-grained specimens. However, for the coarse-grained copper specimens, no clear changes of the microhardness were observed after ablation with varying laser pulse energies. The grain sizes of the ultrafine-grained specimens were also surveyed as a function of laser pulse energy using electron backscattered diffraction (EBSD). The heat generated by laser ablation caused recrystallization and grain growth of the ultrafine-grained copper; moreover, the grain size gradually increased with increasing pulse energy. In contrast, no obvious changes in grain size were observed for the coarse-grained copper specimens with increasing pulse energy.

Mechanical properties and electrical conductivity of Al 6101 and 6201 alloys processed by hydro-extrusion

NASA Astrophysics Data System (ADS)

Pakiela, Z.; Ludwichowska, K.; Ferenc, J.; Kulczyk, M.

2014-08-01

The aim of this work was to produce a material with high strength and electrical conductivity. Two aluminium alloys: Al 6101 and 6201 were used for investigation. Improvement of mechanical properties was obtained by severe plastic deformation, using Hydrostatic Extrusion (HE). To examine mechanical properties of the materials microhardness and tensile tests were carried out. Furthermore, the microstructure analysis was carried out using TEM and light microscopy. Electrical conductivity of materials was measured by 4-wire method. It was found that in the material processed by HE tensile strength and microhardness increased about twice. The biggest strength of 356 MPa was obtained for alloy 6201 after HE. In this case the reduction of a diameters from 20 to 5 mm was used. Examination of the microstructure revealed that as a result of HE grain size refinement to 0.5 micrometer occurred. It was also found that the material has the electric conductivity of about 52% IACS.

Preparation and characterization of laser cladding wollastonite derived bioceramic coating on titanium alloy.

PubMed

Li, Huan-cai; Wang, Dian-gang; Chen, Chuan-zhong; Weng, Fei; Shi, Hua

2015-09-25

The bioceramic coating is fabricated on titanium alloy (Ti6Al4V) by laser cladding the preplaced wollastonite (CaSiO3) powders. The coating on Ti6Al4V is characterized by x-ray diffraction, scanning electron microscopy coupled with energy dispersive spectroscopy, and attenuated total reflection Fourier-transform infrared. The interface bonding strength is measured using the stretching method using an RGD-5-type electronic tensile machine. The microhardness distribution of the cross-section is determined using an indentation test. The in vitro bioactivity of the coating on Ti6Al4V is evaluated using the in vitro simulated body fluid (SBF) immersion test. The microstructure of the laser cladding sample is affected by the process parameters. The coating surface is coarse, accidented, and microporous. The cross-section microstructure of the ceramic layer from the bottom to the top gradually changes from cellular crystal, fine cellular-dendrite structure to underdeveloped dendrite crystal. The coating on Ti6Al4V is composed of CaTiO3, CaO, α-Ca2SiO4, SiO2, and TiO2. After soaking in the SBF solution, the calcium phosphate layer is formed on the coating surface.

A study of Bi-Pb-Sn-Cd-Sb penta-alloys rapidly quenched from melt

NASA Astrophysics Data System (ADS)

Kamal, M.; El-Bediwi, A. B.

2004-11-01

Optical microscopy, X-ray diffractometry, the double bridge method, the Vickers microhardness testing and dynamic resonance techniques have been used to investigate structure, electrical resistivity, hardness, internal friction and elastic modulus of quenched Bi-Pb-Sn-Cd-Sb penta-alloys. The properties of these penta-alloys are greatly affected by rapid quenching. The intermetallic compound chi(Pb-Bi) or Bi3Pb7 is obtained after rapid quenching using the melt-spinning technique, and this is in agreement with reports by other authors [Marshall, T.J., Mott, G. T. and Grieverson, M. H. (1975). Br. J. Radiol., 48, 924, Kamal, M., El-Bediwi, A. B. and Karman, M. B. (1998). Structure, mechanical properties and electrical resistivity of rapidly solidified Pb-Sn-Cd and Pb-Bi-Sn-Cd alloys. J. Mater. Sci.: Mater. Electron., 9, 425, Borromee-Gautier, C., Giessen, B. C. and Grrant, N. J. (1968). J. Chem. Phys., 48,1905, Moon, K.-W., Boettinger, W. J., Kanner, U. R., Handwerker, C. A. and Lee, D.-J. (2001). The effect of Pb contamination on the solidification behavior of Sn-Bi solders. J. Electron. Mater, 30, 45.]. The quenched Bi43.5Pb44.5Cd5Sn2Sb5 alloy has important properties for safety devices in fire detection and extinguishing systems.

Effects of Sn Addition on the Microstructures and Mechanical Properties of Mg-6Zn-3Cu- xSn Magnesium Alloys

NASA Astrophysics Data System (ADS)

Zhang, Tao; Shen, Jun; Sang, Jia-Xin; Li, Yang; He, Pei-Pei

2015-08-01

In this paper, Mg-6Zn-3Cu- xSn (ZC63- xSn) magnesium alloys with different Sn contents (0, 1, 2, 4 wt pct) were fabricated and subjected to different heat treatments. The microstructures and mechanical properties of the obtained ZC63- xSn samples were investigated by optical microscopy, X-ray diffraction, scanning electron microscopy, Vickers hardness testing, and tensile testing. It was found that the As-cast Mg-6Zn-3Cu (ZC63) magnesium alloy mainly contained α-Mg grains and Mg(Zn,Cu) particles. Sn dissolved in α-Mg grains when Sn content was below 2 wt pct while Mg2Sn phase forms in the case of Sn content was above 4 wt pct. Addition of Sn refined both α-Mg grains and Mg(Zn,Cu) particles, and increased the volume fraction of Mg(Zn,Cu) particles. Compared with the Sn-free alloy, the microhardness of Sn-containing alloys increased greatly and that of As-extrude ZC63-4Sn sample achieved the highest value. The strength of ZC63 magnesium alloy was significantly enhanced because of Sn addition, which was attributed to grain refinement strengthening, solid solution strengthening, and precipitation strengthening. Furthermore, the ultimate yield stress, yield strength, and elongation of ZC63- xSn magnesium alloys were increased owing to the deceasing grain size induced by extrusion process.

Continuous cooling transformations and microstructures in a low-carbon, high-strength low-alloy plate steel

NASA Astrophysics Data System (ADS)

Thompson, S. W.; Vin, D. J., Col; Krauss, G.

1990-06-01

A continuous-cooling-transformation (CCT) diagram was determined for a high-strength low-alloy plate steel containing (in weight percent) 0.06 C, 1.45 Mn, 1.25 Cu, 0.97 Ni, 0.72 Cr, and 0.42 Mo. Dilatometric measurements were supplemented by microhardness testing, light microscopy, and transmission electron microscopy. The CCT diagram showed significant suppression of polygonal ferrite formation and a prominent transformation region, normally attributed to bainite formation, at temperatures intermediate to those of polygonal ferrite and martensite formation. In the intermediate region, ferrite formation in groups of similarly oriented crystals about 1 μm in size and containing a high density of dislocations dominated the transformation of austenite during continuous cooling. The ferrite grains assumed two morphologies, elongated or acicular and equiaxed or granular, leading to the terms “acicular ferrite” and “granular ferrite,” respectively, to describe these structures. Austenite regions, some transformed to martensite, were enriched in carbon and retained at interfaces between ferrite grains. Coarse interfacial ledges and the nonacicular morphology of the granular ferrite grains provided evidence for a phase transformation mechanism involving reconstructive diffusion of substitutional atoms. At slow cooling rates, polygonal ferrite and Widmanstätten ferrite formed. These latter structures contained low dislocation densities and e-copper precipitates formed by an interphase transformation mechanism.

Effect of graphite addition into mill scale waste as a potential bipolar plates material of proton exchange membrane fuel cells

NASA Astrophysics Data System (ADS)

Khaerudini, D. S.; Prakoso, G. B.; Insiyanda, D. R.; Widodo, H.; Destyorini, F.; Indayaningsih, N.

2018-03-01

Bipolar plates (BPP) is a vital component of proton exchange membrane fuel cells (PEMFC), which supplies fuel and oxidant to reactive sites, remove reaction products, collects produced current and provide mechanical support for the cells in the stack. This work concerns the utilization of mill scale, a by-product of iron and steel formed during the hot rolling of steel, as a potential material for use as BPP in PEMFC. On the other hand, mill scale is considered a very rich in iron source having characteristic required such as for current collector in BPP and would significantly contribute to lower the overall cost of PEMFC based fuel cell systems. In this study, the iron reach source of mill scale powder, after sieving of 150 mesh, was mechanically alloyed with the carbon source containing 5, 10, and 15 wt.% graphite using a shaker mill for 3 h. The mixed powders were then pressed at 300 MPa and sintered at 900 °C for 1 h under inert gas atmosphere. The structural changes of powder particles during mechanical alloying and after sintering were studied by X-ray diffractometry, optical microscopy, scanning electron microscopy, and microhardness measurement. The details of the presence of iron, carbon, and iron carbide (Fe-C) as the products of reactions as well as sufficient mechanical strength of the sintered materials were presented in this report.

Microstructure and mechanical properties of bulk and plasma-sprayed y2O3-partially stabilized zirconia

NASA Technical Reports Server (NTRS)

Valentine, P. G.; Maier, R. D.

1980-01-01

Bulk 8.0 weight percent yttria partially stabilied zirconia (PSZ) was studied by light microscopy, transmission electron microscopy, X-ray analysis, microhardness testing, and fracture toughness testing. The as received PSZ contained spheroidal and grain boundary precipitates up to 4 micrometers in size. Spheroids up to 1.26 micrometers were metastable tetragonal; large spheroids were monoclinic. Grinding the PSZ into powder did not cause a significant amount of tetragonal to transform to monoclinic. This indicates that transformation toughness is not a significant mechanism in PSZ. Aging the PSZ at 1500 C caused the fine tetragonal precipitates to grow from 0.06 to 0.12 micrometers, in 250 minutes. A peak hardness of 1400 kg/sq mm was attained after 50 minutes. Solution annealing and quenching the as received PSZ eliminated the large precipitates, but fine tetragonal precipitates reformed on quenching. Aging at 1500 C caused the fine 0.02 micrometers tetragonal precipitates to grow into plates about 0.10 by 0.50 micrometers. A peak hardness of 1517 kg/sq mm was obtained after 250 minutes. On further aging, monoclinic percipitates formed along grain boundaries. The fracture toughness of the aged and unaged solution annealed and quenched PSZ was found to be between 2 and 3 MN /square root of m cubed. This range of fracture toughness is consistent with PSZ's that do not undergo transformation toughening.

Microstructural and superficial modification in a Cu-Al-Be shape memory alloy due to superficial severe plastic deformation under sliding wear conditions

NASA Astrophysics Data System (ADS)

Figueroa, C. G.; Garcia-Castillo, F. N.; Jacobo, V. H.; Cortés-Pérez, J.; Schouwenaars, R.

2017-05-01

Stress induced martensitic transformation in copper-based shape memory alloys has been studied mainly in monocrystals. This limits the use of such results for practical applications as most engineering applications use polycristals. In the present work, a coaxial tribometer developed by the authors was used to characterise the tribological behaviour of polycrystalline Cu-11.5%Al-0.5%Be shape memory alloy in contact with AISI 9840 steel under sliding wear conditions. The surface and microstructure characterization of the worn material was conducted by conventional scanning electron microscopy and atomic force microscopy, while the mechanical properties along the transversal section were measured by means of micro-hardness testing. The tribological behaviour of Cu-Al-Be showed to be optimal under sliding wear conditions since the surface only presented a slight damage consisting in some elongated flakes produced by strong plastic deformation. The combination of the plastically modified surface and the effects of mechanically induced martensitic transformation is well-suited for sliding wear conditions since the modified surface provides the necessary strength to avoid superficial damage while superelasticity associated to martensitic transformation is an additional mechanism which allows absorbing mechanical energy associated to wear phenomena as opposed to conventional ductile alloys where severe plastic deformation affects several tens of micrometres below the surface.

Radiation-Thermal Sintering of Zirconia Powder Compacts Under Conditions of Bilateral Heating Using Beams of Low-Energy Electrons

NASA Astrophysics Data System (ADS)

Ghyngazov, S. A.; Frangulyan, T. S.; Chernyavskii, A. V.; Goreev, A. K.; Naiden, E. P.

2015-06-01

Comparative experiments on sintering zirconia ceramics are performed using colliding beams of low-energy electrons and under conditions of thermal heating. The density and microhardness of ceramic materials manufactured via different processes are determined. The use of a regime of bilateral heating by high-intensity,low-energy electron beams is shown to intensify the sintering process and yield material specimens with improved characteristics compared to those formed by thermal sintering.

Reminova and EAER: Keeping Enamel Whole through Caries Remineralization.

PubMed

Pitts, N B; Wright, J P

2018-02-01

This article aims to outline the early development of a King's College London dental spinout company, Reminova, formed to commercialize a novel clinical method of caries remineralization: electrically accelerated and enhanced remineralization (EAER). This method is being developed to address the unmet clinical need identified by modern caries management strategies to keep enamel "whole" through remineralization of clinical caries as a form of nonoperative caries treatment for initial-stage and moderate lesions. A progressive movement within dentistry is shifting away from the restorative-only model, which, it is suggested, has failed. The high prevalence of initial-stage caries across populations provides a significant opportunity to prevent restorations and reduce repeat restorations over a patient's lifetime. Reminova has set out to provide a method to repair lesions without drilling, filling, pain, or injections. The article outlines the rationale for and the chronological stages of the technology and company development. It then outlines corroborative evidence to show that EAER treatment can, in this preliminary in vitro investigation, remineralize clinically significant caries throughout the depth of the lesion as measured by Knoop microhardness and corroborated by scanning electron microscopy. Furthermore, the presented data show that EAER-treated enamel is harder than the healthy enamel measured nearby in each sample and is very similar in appearance to healthy enamel from the subjective interpretation made possible by scanning electron microscopy imagery. The data presented also show that this more "complete" remineralization to a high hardness level has been achieved with 2 remineralizing agents via in vitro human tooth samples. The broad clinical potential of this new treatment methodology seems to be very encouraging from these results. Reminova will strive to continue its mission, to ensure that, in the future, dental teams will not need to drill holes for the treatment of initial-stage and moderate caries lesions.

Leucine-rich amelogenin peptide (LRAP) as a surface primer for biomimetic remineralization of superficial enamel defects: An in vitro study.

PubMed

Shafiei, Farhad; Hossein, Bagheri G; Farajollahi, Mohammad M; Fathollah, Moztarzadeh; Marjan, Behroozibakhsh; Tahereh, Jafarzadeh Kashi

2015-01-01

This study was carried out to obtain more information about the assembly of hydroxyapatite bundles formed in the presence of Leucine-Rich Amelogenin Peptide (LRAP) and to evaluate its effect on the remineralization of enamel defects through a biomimetic approach. One or 2 mg/mL LRAP solutions containing 2.5 mM of Ca(+2) and 1.5 mM phosphate were prepared (pH = 7.2) and stored at 37 °C for 24 h. The products of the reaction were studied using atomic force microscopy (AFM), transmission electron microscopy (TEM), and selected area electron diffraction (SAED). Vickers surface microhardness recovery (SMR%) of acid-etched bovine enamel, with or without LRAP surface treatment, were calculated to evaluate the influence of peptide on the lesion remineralization. Distilled water and 1 or 2 mg/mL LRAP solution (pH = 7.2) were applied on the lesions and the specimens were incubated in mineralization solution (2.5mM Ca(+2) , 1.5mM PO4 (-3) , pH = 7.2) for 24 h. One-way ANOVA and Tukey's multi-comparison tests were used for statistical analysis. The pattern of enamel surface repair was studied using FE-SEM. AFM showed the formation of highly organized hierarchical structures, composed of hydroxyapatite (HA) crystals, similar to the dental enamel microstructure. ANOVA procedure showed significant effect of peptide treatment on the calculated SMR% (p < 0.001). Tukey's test revealed that peptide treated groups had significantly higher values of SMR%. In conclusion, LRAP is able to regulate the formation of HA and enhances the remineralization of acid-etched enamel as a surface treatment agent. © Wiley Periodicals, Inc.

Synthesis of wrinkled mesoporous silica and its reinforcing effect for dental resin composites.

PubMed

Wang, Ruili; Habib, Eric; Zhu, X X

2017-10-01

The aim of this work is to explore the reinforcing effect of wrinkled mesoporous silica (WMS), which should allow micromechanical resin matrix/filler interlocking in dental resin composites, and to investigate the effect of silica morphology, loading, and compositions on their mechanical properties. WMS (average diameter of 496nm) was prepared through the self-assembly method and characterized by the use of the electron microscopy, dynamic light scattering, and the N 2 adsorption-desorption measurements. The mechanical properties of resin composites containing silanized WMS and nonporous smaller silica were evaluated with a universal mechanical testing machine. Field-emission scanning electron microscopy was used to study the fracture morphology of dental composites. Resin composites including silanized silica particles (average diameter of 507nm) served as the control group. Higher filler loading of silanized WMS substantially improved the mechanical properties of the neat resin matrix, over the composites loaded with regular silanized silica particles similar in size. The impregnation of smaller secondary silica particles with diameters of 90 and 190nm, denoted respectively as Si90 and Si190, increased the filler loading of the bimodal WMS filler (WMS-Si90 or WMS-Si190) to 60wt%, and the corresponding composites exhibited better mechanical properties than the control fillers made with regular silica particles. Among all composites, the optimal WMS-Si190- filled composite (mass ratio WMS:Si190=10:90, total filler loading 60wt%) exhibited the best mechanical performance including flexural strength, flexural modulus, compressive strength and Vickers microhardness. The incorporation of WMS and its mixed bimodal fillers with smaller silica particles led to the design and formulation of dental resin composites with superior mechanical properties. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

SEM Evaluation of Enamel Surface Changes and Enamel Microhardness around Orthodontic Brackets after Application of CO2 Laser, Er,Cr:YSGG Laser and Fluoride Varnish: An In vivo Study.

PubMed

Kaur, Tarundeep; Tripathi, Tulika; Rai, Priyank; Kanase, Anup

2017-09-01

One of the most undesirable consequences of orthodontic treatment is occurrence of enamel demineralization around orthodontic brackets. Numerous in vitro studies have reported the prevention of enamel demineralization by surface treatment with lasers and fluoride varnish. To evaluate the changes on the enamel surface and microhardness around orthodontic brackets after surface treatment by CO 2 laser, Er, Cr:YSGG laser and fluoride varnish in vivo. A double blind interventional study was carried out on 100 premolars which were equally divided into five groups, out of which one was the control group (Group 0). The intervention groups (Group I to IV) comprised of patients requiring fixed orthodontic treatment with all 4 first premolars extraction. Brackets were bonded on all 80 premolars which were to be extracted. Enamel surface treatment of Groups I, II and III was done by CO 2 laser, Er, Cr:YSGG laser and 5% sodium fluoride varnish respectively and Group IV did not receive any surface treatment. A modified T-loop was ligated to the bracket and after two months, the premolars were extracted. Surface changes were evaluated by Scanning Electron Microscopic (SEM) and microhardness testing. Comparison of mean microhardness between all the groups was assessed using post-hoc test with Bonferroni correction. Group I showed a melted enamel appearance with fine cracks and fissures while Group II showed a glossy, homogenous enamel surface with well coalesced enamel rods. Group III showed slight areas of erosions and Group IV presented areas of stripped enamel. Significant difference was observed between the mean microhardness (VHN) of Group I, Group II, Group III, Group IV and Group 0 with p<0.001. A significant difference of p<0.001 was observed while comparing Group I vs II,III,IV,0 and Group II vs III,IV,0. However, difference while comparing Group III vs IV was p=0.005 and difference between the mean microhardness of Group 0 vs Group III was non significant. Surface treatment with Er,Cr:YSGG laser causes a positive alteration of the enamel surface increasing its ability to resist demineralization with optimum microhardness as compared to CO 2 laser and sodium fluoride varnish.

Effect of Nickel Contents on the Microstructure and Mechanical Properties for Low-Carbon Bainitic Weld Metals

NASA Astrophysics Data System (ADS)

Mao, Gaojun; Cao, Rui; Yang, Jun; Jiang, Yong; Wang, Shuai; Guo, Xili; Yuan, Junjun; Zhang, Xiaobo; Chen, Jianhong

2017-05-01

Multi-pass weld metals were deposited on Q345 base steel using metal powder-flux-cored wire with various Ni contents to investigate the effects of the Ni content on the weld microstructure and property. The types of the microstructures were identified by optical microscope, scanning electron microscope, transmission electron microscope, and micro-hardness tests. As a focusing point, the lath bainite and lath martensite were distinguished by their compositions, morphologies, and hardness. In particular, a number of black plane facets appearing between lath bainite or lath martensite packets were characterized by laser scanning confocal microscope. The results indicated that with the increase in Ni contents in the range of 0, 2, 4, and 6%, the microstructures in the weld-deposited metal were changed from the domination of the granular bainite to the majority of the lath bainite and/or the lath martensite and the micro-hardness of the weld-deposited metal increased. Meanwhile, the average width of columnar grain displays a decreasing trend and prior austenite grain size decreases while increases with higher Ni content above 4%. Yield strength and ultimate tensile strength decrease, while the reduction in fracture area increases with the decreasing Ni mass fraction and the increasing test temperature, respectively. And poor yield strength in Ni6 specimen can be attributed to elements segregation caused by weld defect. Finally, micro-hardness distribution in correspondence with specimens presents as a style of cloud-map.

The effect of photo-activated glazes on the microhardness of acrylic baseplate resins.

PubMed

Emmanouil, J K; Kavouras, P; Kehagias, Th

2002-01-01

A comparative investigation of acrylic denture base surface microhardness, induced through glazing with different photo-activated liquids. Thermopolymerized acrylic resin Paladon 65 (Kulzer) was used for this study. The samples were mechanically thinned by silicon carbide grinding papers and finally, mechanically polished by alumina pastes. The samples were then glazed with Palaseal, Plaquit and Lightplast-Lack photo-activated liquids. Microhardness tests were carried out via a Zeiss optical microscope equipped with an Anton Paar microhardness tester fitted with a Knoop indenter. Microhardness testing performed on surfaces glazed by Plaquit, Lightplast-Lack, and Palaseal photo-activated liquids showed enhanced microhardness values compared to the mechanically polished acrylic resin denture base material. Comparative microhardness tests performed on acrylic base resin treated with photo-activated acrylic glazes showed that all increases the surface microhardness. The enhancement of surface microhardness of acrylic denture bases suggests that they are likely to resist wear during service.

Structure and mechanical properties of coatings fabricated by nonvacuum electron beam cladding of Ti-Ta-Zr powder mixtures

NASA Astrophysics Data System (ADS)

Samoylenko, Vitaliy V.; Lenivtseva, Olga G.; Polyakov, Igor A.; Laptev, Ilya S.

2015-10-01

In this paper structural investigations and mechanical tests of Ti-Ta-Zr coatings obtained on surfaces of cp-titanium workpieces were carried out. It was found that the coatings had a dendrite structure; investigations at high-power magnifications revealed a platelet structure. An increase of tantalum concentration led to refinement of structural components. The microhardness level of all coatings, excepting a specimen with the maximum tantalum content, was 370 HV. The microhardness of this coating reached 400 HV. The ultimate tensile strength of cladded layers varied from 697 to 947 MPa. Adhesion tests showed that bimetallic composites were characterized by high bond strength of cladded layers to the substrate, which exceeded cp-titanium strength characteristics.

Spark plasma sintering of ceramic matrix composite based on alumina, reinforced by carbon nanotubes

NASA Astrophysics Data System (ADS)

Leonov, A. A.; Khasanov, A. O.; Danchenko, V. A.; Khasanov, O. L.

2017-12-01

Alumina composites reinforced with 3 vol.% multi-walled carbon nanotubes (MWCNTs) were prepared by spark plasma sintering (SPS). The influence of sintering temperature (1400-1600 °C) on the composites microstructure and mechanical properties was investigated. Microstructure observations of the composite shows that some CNTs site along alumina grains boundary, while others embed into the alumina grains and shows that CNTs bonded strongly with the alumina matrix contributing to fracture toughness and microhardness increase. MWCNTs reinforcing mechanisms including CNT pull-out and crack deflection were directly observed by scanning electron microscope (SEM). For Al2O3/CNT composite sintered at 1600 °C, fracture toughness and microhardness are 4.93 MPa·m1/2 and 23.26 GPa respectively.

Influence of Bond Coat on HVOF-Sprayed Gradient Cermet Coating on Copper Alloy

NASA Astrophysics Data System (ADS)

Ke, Peng; Cai, Fei; Chen, Wanglin; Wang, Shuoyu; Ni, Zhenhang; Hu, Xiaohong; Li, Mingxi; Zhu, Guanghong; Zhang, Shihong

2017-06-01

Coatings are required on mold copper plates to prolong their service life through enhanced hardness, wear resistance, and oxidation resistance. In the present study, NiCr-30 wt.%Cr3C2 ceramic-metallic (cermet) layers were deposited by high velocity oxy-fuel (HVOF) spraying on different designed bond layers, including electroplated Ni, HVOF-sprayed NiCr, and double-decker Ni-NiCr. Annealing was also conducted on the gradient coating (GC) with NiCr bond layer to improve the wear resistance and adhesion strength. Coating microstructure was investigated by scanning electron microscopy and x-ray diffraction analysis. Mechanical properties including microhardness, wear resistance, and adhesion strength of the different coatings were evaluated systematically. The results show that the types of metallic bond layer and annealing process had a significant impact on the mechanical properties of the GCs. The GCs with electroplated Ni bond layer exhibited the highest adhesion strength (about 70 MPa). However, the GC with HVOF-sprayed NiCr bond layer exhibited better wear resistance. The wear resistance and adhesion strength of the coating with NiCr metallic bond layer were enhanced after annealing.

A miniaturized test method for the mechanical characterization of structural materials for fusion reactors

NASA Astrophysics Data System (ADS)

Gondi, P.; Donato, A.; Montanari, R.; Sili, A.

1996-10-01

This work deals with a non-destructive method for mechanical tests which is based on the indentation of materials at a constant rate by means of a cylinder with a small radius and penetrating flat surface. The load versus penetration depth curves obtained using this method have shown correspondences with those of tensile tests and have given indications about the mechanical properties on a reduced scale. In this work penetration tests have been carried out on various kinds of Cr martensitic steels (MANET-2, BATMAN and modified F82H) which are of interest for first wall and structural applications in future fusion reactors. The load versus penetration depth curves have been examined with reference to data obtained in tensile tests and to microhardness measurements. Penetration tests have been performed at various temperature (from -180 to 100°C). Conclusions, which can be drawn for the ductile to brittle transition, are discussed for MANET-2 steel. Preliminary results obtained on BATMAN and modified F82H steels are reported. The characteristics of the indenter imprints have been studied by scanning electron microscopy.

Tribological and corrosion behaviour of electroless Ni-B coating possessing a blackberry like structure

NASA Astrophysics Data System (ADS)

Bülbül, Ferhat; Altun, Hikmet; Küçük, Özkan; Ezirmik, Vefa

2012-08-01

This study aims to evaluate the tribological and corrosion properties of the electroless Ni-B coating deposited on AISI 304 stainless steels. The microstructure of the coating was characterized using x-ray diffraction (XRD) and scanning electron microscopy-energy dispersive spectrometry (SEM-EDS). XRD analysis revealed that the prepared coating possessed an amorphous character. SEM-EDS investigation also indicated that a non-stoichiometric Ni-B coating was deposited with a columnar growth mechanism on the stainless steel substrate and the morphology of the growth surface was blackberry-like. The hardness and tribological properties were characterized by microhardness and a pin-on-disc wear test. The electroless Ni-B coated sample had a higher degree of hardness, a lower friction coefficient and a lower wear rate than the uncoated substrate. The electrochemical potentiodynamic polarization method was used to evaluate the corrosion resistance of the coating. The electroless Ni-B coating offered cathodic protection on the substrate by acting as a sacrificial anode although it was electrochemically more reactive than the stainless steel substrate.

Microstructural and mechanical investigation of aluminium alloy (Al 1050) melted by microwave hybrid heating

NASA Astrophysics Data System (ADS)

Shashank Lingappa, M.; Srinath, M. S.; Amarendra, H. J.

2017-07-01

Microwave processing of metals is an emerging area. Melting of bulk metallic materials through microwave irradiation is still immature. In view of this, the present paper discusses the melting of bulk Al 1050 metallic material through microwave irradiation. The melting process is carried out successfully in a domestic microwave oven with 900 W power at 2450 MHz frequency. Metallurgical and mechanical characterization of the processed and as-received material is carried out. Aluminium phase is found to be dominant in processed material when tested through x-ray diffraction (XRD). Microstructure study of as-cast metal through scanning electron microscopy (SEM) reveals the formation of uniform hexagonal grain structure free from pores and cavities. The average tensile strength of the cast material is found to be around 21% higher, when compared to as-received material. Vickers’ microhardness of the as-cast metal is measured and is 10% higher than that of the as-received metal. Radiography on as-cast metal shows no significant defects. Al 1050 material melted through microwave irradiation has exhibited superior properties than the as-received Al 1050.

Effect of solidification parameters on mechanical properties of directionally solidified Al-Rich Al-Cu alloys

NASA Astrophysics Data System (ADS)

Çadırlı, Emin

2013-05-01

Al(100-x)-Cux alloys (x=3 wt%, 6 wt%, 15 wt%, 24 wt% and 33 wt%) were prepared using metals of 99.99% high purity in vacuum atmosphere. These alloys were directionally solidified under steady-state conditions by using a Bridgman-type directional solidification furnace. Solidification parameters (G, V and ), microstructure parameters (λ1, λ2 and λE) and mechanical properties (HV, σ) of the Al-Cu alloys were measured. Microstructure parameters were expressed as functions of solidification parameters by using a linear regression analysis. The dependency of HV, σ on the cooling rate, microstructure parameters and composition were determined. According to experimental results, the microhardness and ultimate tensile strength of the solidified samples was increased by increasing the cooling rate and Cu content, but decreased with increasing microstructure parameters. The microscopic fracture surfaces of the different samples were observed using scanning electron microscopy. Fractographic analysis of the tensile fracture surfaces showed that the type of fracture significantly changed from ductile to brittle depending on the composition.

Mechanical properties of a Gum-type Ti-Nb-Zr-Fe-O alloy

NASA Astrophysics Data System (ADS)

Nocivin, Anna; Cinca, Ion; Raducanu, Doina; Cojocaru, Vasile Danut; Popovici, Ion Alexandru

2017-08-01

A new Gum-type alloy (Ti-Nb-Zr-Fe-O) in which Fe is used instead of Ta was subjected to a particular thermomechanical processing scheme to assess whether its mechanical characteristics (fine β-grains with high strength and low modulus) render it suitable as a biomedical implant material. After a homogenization treatment followed by cold-rolling with 50% reduction, the specimens were subjected to one of three different recrystallization treatments at 1073, 1173, and 1273 K. The structural and mechanical properties of all of the treated specimens were analyzed. The mechanical characterization included tensile tests, microhardness determinations, and fractography by scanning electron microscopy. The possible deformation mechanisms were discussed using the \\overline {Bo} - \\overline {Md} diagram. By correlating all of the experimental results, we concluded that the most promising processing variant corresponds to recrystallization at 1073 K, which can provide suitable mechanical characteristics for this type of alloys: high yield and ultimate tensile strengths (1038 and 1083 MPa, respectively), a low modulus of elasticity (62 GPa), and fine crystalline grain size (approximately 50 μm).

Physical nature of surface structure degradation in long term operated rails

NASA Astrophysics Data System (ADS)

Gromov, V. E.; Yuriev, A. A.; Peregudov, O. A.; Konovalov, S. V.; Ivanov, Yu. F.; Glezer, A. M.; Semin, A. P.

2017-12-01

Here we present research data on the structural-phase state and surface properties of rails after long-term operation with a transported tonnage of gross weight 500 and 1000 mln tons. Using optical, scanning, and transmission electron diffraction microscopy, and measurements of microhardness and tribological parameters, it is shown that the wear rate of the material after transport of 500 and 1000 mln tons increases 3 and 3.4 times, respectively, and the friction coefficient decreases 1.4 and 1.1 times. After transport of 500 mln tons, complete failure of cementite plates occurs resulting in round cementite particles of size 10-50 nm. After transport of 1000 mln tons, dynamic recrystallization develops in the material. Two competitive mechanisms are suggested for such evolution: (1) decomposition of cementite particles with their transfer to the volume of ferrite grains or plates in pearlite and (2) decomposition and dissolution of cementite particles, transition of carbon atoms to dislocations (to Cottrell atmospheres), transfer of carbon atoms by dislocations to the volume of ferrite grains or plates, and formation of nano-sized cementite particles.

Laser polishing of additive manufactured Ti alloys

NASA Astrophysics Data System (ADS)

Ma, C. P.; Guan, Y. C.; Zhou, W.

2017-06-01

Laser-based additive manufacturing has attracted much attention as a promising 3D printing method for metallic components in recent years. However, surface roughness of additive manufactured components has been considered as a challenge to achieve high performance. In this work, we demonstrate the capability of fiber laser in polishing rough surface of additive manufactured Ti-based alloys as Ti-6Al-4V and TC11. Both as-received surface and laser-polished surfaces as well as cross-section subsurfaces were analyzed carefully by White-Light Interference, Confocal Microscope, Focus Ion Beam, Scanning Electron Microscopy, Energy Dispersive Spectrometer, and X-ray Diffraction. Results revealed that as-received Ti-based alloys with surface roughness more than 5 μm could be reduce to less than 1 μm through laser polishing process. Moreover, microstructure, microhardness and wear resistance of laser-polished zone was investigated in order to examine the thermal effect of laser polishing processing on the substrate of additive manufactured Ti alloys. This proof-of-concept process has the potential to effectively improve the surface roughness of additive manufactured metallic alloy by local polishing method without damage to the substrate.

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding

PubMed Central

Liu, Yanhui; Qu, Weicheng; Su, Yu

2016-01-01

In this study, a TiC-reinforced composite coating was produced to improve the wear resistance of a pearlite matrix grey iron using a pre-placed Ti powder by laser cladding. Results of scanning electron microscopy (SEM), X-ray diffractometer (XRD), and energy dispersive X-ray spectroscopy (EDS) confirmed that the coating was composed of TiC particles and two kinds of α-Fe phase. The fine TiC particles were only a few microns in size and uniformly distributed on the matrix phase in the composite coating. The microstructure characteristic of the composite coating resulted in the microhardness rising to about 1000 HV0.3 (China GB/T 4342-1991) and the wear resistance significantly increased relative to the substrate. In addition, the fine and homogeneous solidification microstructure without graphite phase in the transition zone led to a good metallurgical bonding and transition between the coating and the substrate. It was of great significance for the cast iron to modify the surface and repair surface defects or surface damage. PMID:28773934

Effect of surfactant concentration in the electrolyte on the tribological properties of nickel-tungsten carbide composite coatings produced by pulse electro co-deposition

NASA Astrophysics Data System (ADS)

Kartal, Muhammet; Uysal, Mehmet; Gul, Harun; Alp, Ahmet; Akbulut, Hatem

2015-11-01

A nickel plating bath containing WC particles was used to obtain hard and wear-resistant particle reinforced Ni/WC MMCs on steel surfaces for anti-wear applications. Copper substrates were used for electro co-deposition of Ni matrix/WC with the particle size of <1 μm tungsten carbide reinforcements. The influence of surfactant (sodium dodecyl sulfate, SDS) concentration on particle distribution, microhardness and wear resistance of composite coatings has been studied. The nickel films were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The effects of the surfactant on the zeta potential, co-deposition and distribution of WC particles in the nickel matrix, as well as the tribological properties of composite coatings were also investigated. The tribological behaviors of the electrodeposited WC composite coatings sliding against M50 steel ball (Ø 10 mm) were examined on a CSM Instrument. All friction and wear tests were performed without lubrication at room temperature and in the ambient air (relative humidity 55-65%).

TEM Analysis of Diffusion-Bonded Silicon Carbide Ceramics Joined Using Metallic Interlayers

NASA Technical Reports Server (NTRS)

Ozaki, T.; Tsuda, H.; Halbig, M. C.; Singh, M.; Hasegawa, Y; Mori, S.; Asthana, R.

2017-01-01

Silicon Carbide (SiC) is a promising material for thermostructural applications due to its excellent high-temperature mechanical properties, oxidation resistance, and thermal stability. However, joining and integration technologies are indispensable for this material in order to fabricate large size and complex shape components with desired functionalities. Although diffusion bonding techniques using metallic interlayers have been commonly utilized to bond various SiC ceramics, detailed microstructural observation by Transmission Electron Microscopy (TEM) of the bonded area has not been carried out due to difficulty in preparing TEM samples. In this study, we tried to prepare TEM samples from joints of diffusion bonded SiC ceramics by Focused Ion Beam (FIB) system and carefully investigated the interfacial microstructure by TEM analysis. The samples used in this study were SiC fiber bonded ceramics (SA-Tyrannohex: SA-THX) diffusion bonded with metallic interlayers such as Ti, TiMo, Mo-B and TiCu. In this presentation, we report the microstructure of diffusion bonded SA-THX mainly with TiCu interlayers obtained by TEM observations, and the influence of metallic interlayers on the joint microstructure and microhardness will be discussed.

Characterization and electrochemical properties of Ni(Si)/Ni5Si2 multiphase coatings prepared by HVOF spraying

NASA Astrophysics Data System (ADS)

Verdian, M. M.; Raeissi, K.; Salehi, M.

2012-11-01

Ni(Si)/Ni5Si2 powders were produced by mechanical alloying (MA) of Ni-25 at.% Si powder mixture. Then, the as-milled powders were sprayed onto copper substrate using high velocity oxy-fuel (HVOF) process. The phase composition and microstructure of the coatings were examined by X-ray diffractometry and scanning electron microscopy. Polarization tests and electrochemical impedance spectroscopy (EIS) measurements were also employed to study corrosion performance of the coatings in 3.5% NaCl solution. The results showed that although single phase Ni3Si was formed during annealing of Ni(Si)/Ni5Si2 powders, but, only Ni(Si) and Ni5Si2 are present in HVOF coatings and no new phase has been formed during spraying. The coatings had microhardness up to 746 HV0.05. Further investigations showed the corrosion performance of multiphase coatings in 3.5% NaCl solution was better than that of copper substrate. The phase transitions during MA, HVOF and annealing processes were discussed in association with Ni-Si phase diagram and nature of each process.

Powder metallurgy of Ge, Si, and Ge-Si

NASA Astrophysics Data System (ADS)

Schilz, Jürgen; Langenbach, Marion

1993-03-01

id="ab1"Planetary ball-milling and pressing behaviour of Ge, Si and Ge-Si powder mixtures are investigated. Scanning and transmission electron microscopy observations revealed the different microstructure of the two elements after milling: Ge remains in a microcrystalline state, whereas Si can be comminuted into grains consisting of nanocrystalline regions. Planetary milling of the two elements together, using agate balls and vial, did not reveal any compound formation. By hot-isostatic pressing, pure Ge and Ge-Si mixtures were densified to a higher value than pure Si. This denotes a plastic flow of the Ge component at a process temperature of 800°C. The microhardness of hot-pressed Ge reaches the bulk value; hot-pressed Si is very soft. Energy dispersive X-ray analysis and X-ray diffraction did not detect any impurity contamination from vial and milling media wear. Moreover, by electrical transport measurements it turned out that the net carrier concentration density resulting from electrical active impurities introduced by the milling and pressing process is below 2 x 1016 cm 3 at room temperature.

TiC Reinforcement Composite Coating Produced Using Graphite of the Cast Iron by Laser Cladding.

PubMed

Liu, Yanhui; Qu, Weicheng; Su, Yu

2016-09-30

In this study, a TiC-reinforced composite coating was produced to improve the wear resistance of a pearlite matrix grey iron using a pre-placed Ti powder by laser cladding. Results of scanning electron microscopy (SEM), X-ray diffractometer (XRD), and energy dispersive X-ray spectroscopy (EDS) confirmed that the coating was composed of TiC particles and two kinds of α -Fe phase. The fine TiC particles were only a few microns in size and uniformly distributed on the matrix phase in the composite coating. The microstructure characteristic of the composite coating resulted in the microhardness rising to about 1000 HV0.3 (China GB/T 4342-1991) and the wear resistance significantly increased relative to the substrate. In addition, the fine and homogeneous solidification microstructure without graphite phase in the transition zone led to a good metallurgical bonding and transition between the coating and the substrate. It was of great significance for the cast iron to modify the surface and repair surface defects or surface damage.

He implantation induced microstructure- and hardness-modification of the intermetallic γ-TiAl

NASA Astrophysics Data System (ADS)

Pouchon, Manuel A.; Chen, Jiachao; Hoffelner, Wolfgang

2009-05-01

TiAl is a well known high temperature material with good creep properties. It is investigated as a potential structural material for Generation IV high temperature gas cooled nuclear reactors. The tests are performed with the ABB-2 (Ti-rich TiAl with 2 at.% W) developed by ASEA Brown Boveri Ltd. (ABB). Thin samples are irradiated throughout with 24 MeV 4He2+ ions; the irradiated material is then investigated towards its microstructure and its hardness. The microstructure is studied by transmission electron microscopy and the hardness is investigated using a micro-hardness tester and a nano-indenter. Different effects can be identified. From room to moderate irradiation temperatures, the radiation induced hardening of the material slowly vanishes until the material completely recovers at about 943 K. Beyond this temperature, He-bubble formation seems to harden the material again, until beyond 1200 K a steep increase in hardening is detected. This effect can be correlated with bubbles being identified in the micrographs. The results are consistent and give strong indications to a microstructural development as a function of temperature.

Synthesis and characterization of Ti-Si-C-N films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shtansky, D.V.; Levashov, E.A.; Sheveiko, A.N.

1999-09-01

This study represents one of the first attempts to deposit multicomponent (more than three components) thin films by magnetron sputtering of multiphase composite targets (three phases or even more). Films of Ti-Si-C-N were synthesized through dc magnetron sputtering of xTiC + yTi{sub 3}SiC{sub 2} + zA composite targets (A was TiSi{sub 2}, SiC, or a mixture of these phases) in an argon atmosphere or in a gaseous mixture of argon and nitrogen. The as-deposited films were characterized using Auger electron spectroscopy, X-ray diffraction, transmission electron microscopy using selected area electron diffraction and high-resolution techniques, and microhardness. It was shown thatmore » the substrate temperature and the nitrogen concentration in the reactive gas had a strong influence on the structure and the composition of the as-deposited films. Polycrystalline grains contained a high density of dislocations and exhibited a curved appearance of the lattice fringes that is probably due to the presence of the long-range stress fields. The measurements of the lattice parameters using the selected area electron diffraction pattern (SA EDP) method indicated, with a high probability, that the polycrystalline grains consist of clusters of atoms with varying compositions. The grain boundaries in the nanocrystalline Ti-Si-C-N films had both ordered and disordered regions, although some regions close to the interface exhibited neither a fully crystalline nor a homogeneously amorphous structure. The contribution of compressive stress as determined by an increase in the fcc lattice parameter is also discussed.« less

Surface microhardness of a resin composite exposed to a "first-generation" LED curing lamp, in vitro.

PubMed

Keogh, Pauraic; Ray, Noel J; Lynch, Christopher D; Burke, Francis M; Hannigan, Ailish

2004-12-01

This investigation determined the minimum exposure times consistent with optimised surface microhardness parameters for a commercial resin composite cured using a "first-generation" light-emitting diode activation lamp. Disk specimens were exposed and surface microhardness numbers measured at the top and bottom surfaces for elapsed times of 1 hour and 24 hours. Bottom/top microhardness number ratios were also calculated. Most microhardness data increased significantly over the elapsed time interval but microhardness ratios (bottom/top) were dependent on exposure time only. A minimum exposure of 40 secs is appropriate to optimise microhardness parameters for the combination of resin composite and lamp investigated.

Fabrication of anti-adhesion surfaces on aluminium substrates of rubber plastic moulds using electrolysis plasma treatment

NASA Astrophysics Data System (ADS)

Meng, Jianbing; Dong, Xiaojuan; Wei, Xiuting; Yin, Zhanmin

2015-04-01

An anti-adhesion surface with a water contact angle of 167° was fabricated on aluminium samples of rubber plastic moulds by electrolysis plasma treatment using mixed electrolytes of C6H5O7(NH4)3 and Na2SO4, followed by fluorination. To optimise the fabrication conditions, several important processing parameters such as the discharge voltage, discharge time, concentrations of supporting electrolyte and stearic acid ethanol solution were examined systematically. Using scanning electron microscopy (SEM) to analyse surfaces morphology, micrometer scale pits, and protrusions were found on the surface, with numerous nanometer mastoids contained in the protrusions. These binary micro/nano-scale structures, which are similar to the micro-structures of soil-burrowing animals, play a critical role in achieving low adhesion properties. Otherwise, the anti-adhesion behaviours of the resulting samples were analysed by the atomic force microscope (AFM), Fourier-transform infrared spectrophotometer (FTIR), electrons probe micro-analyzer (EPMA), optical contact angle meter, digital Vickers microhardness (Hv) tester, and electronic universal testing. The results show that the electrolysis plasma treatment does not require complex processing parameters, using a simple device, and is an environment-friendly and effective method. Under the optimised conditions, the contact angle (CA) for the modified anti-adhesion surface is up to 167°, the sliding angle (SA) is less than 2°, roughness of the sample surface is only 0.409μm. Moreover, the adhesion force and Hv are 0. 9KN and 385, respectively.

In vitro remineralization effects of grape seed extract on artificial root caries.

PubMed

Xie, Qian; Bedran-Russo, Ana Karina; Wu, Christine D

2008-11-01

Grape seed extract (GSE) contains proanthocyanidins (PA), which has been reported to strengthen collagen-based tissues by increasing collagen cross-links. We used an in vitro pH-cycling model to evaluate the effect of GSE on the remineralization of artificial root caries. Sound human teeth fragments obtained from the cervical portion of the root were stored in a demineralization solution for 96 h at 37 degrees C to induce artificial root caries lesions. The fragments were then divided into three treatment groups including: 6.5% GSE, 1,000 ppm fluoride (NaF), and a control (no treatment). The demineralized samples were pH-cycled through treatment solutions, acidic buffer and neutral buffer for 8 days at 6 cycles per day. The samples were subsequently evaluated using a microhardness tester, polarized light microscopy (PLM) and confocal laser scanning microscopy (CLSM). Data were analyzed using ANOVA and Fisher's tests (p<0.05). GSE and fluoride significantly increased the microhardness of the lesions (p<0.05) when compared to a control group. PLM data revealed a significantly thicker mineral precipitation band on the surface layer of the GSE-treated lesions when compared to the other groups (p>0.05), which was confirmed by CLSM. We concluded that grape seed extract positively affects the demineralization and/or remineralization processes of artificial root caries lesions, most likely through a different mechanism than that of fluoride. Grape seed extract may be a promising natural agent for non-invasive root caries therapy.

Determination of the Mechanical Properties of Plasma-Sprayed Hydroxyapatite Coatings Using the Knoop Indentation Technique

NASA Astrophysics Data System (ADS)

Hasan, Md. Fahad; Wang, James; Berndt, Christopher

2015-06-01

The microhardness and elastic modulus of plasma-sprayed hydroxyapatite coatings were evaluated using Knoop indentation on the cross section and on the top surface. The effects of indentation angle, testing direction, measurement location and applied load on the microhardness and elastic modulus were investigated. The variability and distribution of the microhardness and elastic modulus data were statistically analysed using the Weibull modulus distribution. The results indicate that the dependence of microhardness and elastic modulus on the indentation angle exhibits a parabolic shape. Dependence of the microhardness values on the indentation angle follows Pythagoras's theorem. The microhardness, Weibull modulus of microhardness and Weibull modulus of elastic modulus reach their maximum at the central position (175 µm) on the cross section of the coatings. The Weibull modulus of microhardness revealed similar values throughout the thickness, and the Weibull modulus of elastic modulus shows higher values on the top surface compared to the cross section.

[Effects of tooth whitening agents and acidic drinks on the surface properties of dental enamel].

PubMed

Chen, Xiaoling; Chen, Zhiqun; Lin, Yao; Shao, Jinquan; Yin, Lu

2013-10-01

Using tooth whitening agents (bleaching clip) in vitro and acidic drinks, we conducted a comparative study of the changes in enamel surface morphology, Ca/P content, and hardness. Tooth whitening glue pieces, cola, and orange juice were used to soak teeth in artificial saliva in vitro. Physiological saline was used as a control treatment. The morphology of the four groups was observed under a scanning electron microscope (SEM) immediately after the teeth were soaked for 7 and 14 d. The changes in Ca/P content and microhardness were analyzed. The enamel surfaces of the teeth in the three test groups were demineralized. The Ca/P ratio and the average microhardness were significantly lower than those of the control group immediately after the teeth were soaked (P < 0.05). The Ca/P ratio and microhardness gradually increased after 7 d. No significant difference was observed between the control group and the test groups after 14 d (P > 0.05). Bleaching agents caused transient demineralization of human enamel, but these agents could induce re-mineralization and repair of enamel over time. Demineralization caused by bleaching covered a relatively normal range compared with acidic drinks and daily drinking.

Annealing effect on thermal conductivity and microhardness of carbon nanotube containing Se80Te16Cu4 glassy composites

NASA Astrophysics Data System (ADS)

Upadhyay, A. N.; Tiwari, R. S.; Singh, Kedar

2018-02-01

This study deals with the effect of thermal annealing on structural/microstructural, thermal and mechanical behavior of pristine Se80Te16Cu4 and carbon nanotubes (CNTs) containing Se80Te16Cu4 glassy composites. Pristine Se80Te16Cu4, 3 and 5 wt%CNTs-Se80Te16Cu4 glassy composites are annealed in the vicinity of glass transition temperature to onset crystallization temperature (340-380 K). X-ray diffraction (XRD) pattern revealed formation of polycrystalline phases of hexagonal CuSe and trigonal selenium. The indexed d-values in XRD patterns are in well conformity with the d-values obtained after the indexing of the ring pattern of selected area electron diffraction pattern of TEM images. The SEM investigation exhibited that the grain size of the CNTs containing Se80Te16Cu4 glassy composites increased with increasing annealing temperature and decreased at further higher annealing temperature. Thermal conductivity, microhardness exhibited a substantial increase with increasing annealing temperature of 340-360 K and slightly decreases for 380 K. The variation of thermal conductivity and microhardness can be explained by cross-linking formation and voids reduction.

Structural properties of H13 tool steel parts produced with use of selective laser melting technology

NASA Astrophysics Data System (ADS)

Šafka, J.; Ackermann, M.; Voleský, L.

2016-04-01

This paper deals with establishing of building parameters for 1.2344 (H13) tool steel processed using Selective Laser Melting (SLM) technology with layer thickness of 50 µm. In the first part of the work, testing matrix of models in the form of a cube with chamfered edge were built under various building parameters such as laser scanning speed and laser power. Resulting models were subjected to set of tests including measurement of surface roughness, inspection of inner structure with aid of Light Optical Microscopy and Scanning Electron Microscopy and evaluation of micro-hardness. These tests helped us to evaluate an influence of changes in building strategy to the properties of the resulting model. In the second part of the work, mechanical properties of the H13 steel were examined. For this purpose, the set of samples in the form of “dog bone” were printed under three different alignments towards the building plate and tested on universal testing machine. Mechanical testing of the samples should then reveal if the different orientation and thus different layering of the material somehow influence its mechanical properties. For this type of material, the producer provides the parameters for layer thickness of 30 µm only. Thus, our 50 µm building strategy brings shortening of the building time which is valuable especially for large models. Results of mechanical tests show slight variation in mechanical properties for various alignment of the sample.

Characterisation of titanium-titanium boride composites processed by powder metallurgy techniques

DOE Office of Scientific and Technical Information (OSTI.GOV)

Selva Kumar, M., E-mail: sel_mcet@yahoo.co.in; Chandrasekar, P.; Chandramohan, P.

2012-11-15

In this work, a detailed characterisation of titanium-titanium boride composites processed by three powder metallurgy techniques, namely, hot isostatic pressing, spark plasma sintering and vacuum sintering, was conducted. Two composites with different volume percents of titanium boride reinforcement were used for the investigation. One was titanium with 20% titanium boride, and the other was titanium with 40% titanium boride (by volume). Characterisation was performed using X-ray diffraction, electron probe micro analysis - energy dispersive spectroscopy and wavelength dispersive spectroscopy, image analysis and scanning electron microscopy. The characterisation results confirm the completion of the titanium boride reaction. The results reveal themore » presence of titanium boride reinforcement in different morphologies such as needle-shaped whiskers, short agglomerated whiskers and fine plates. The paper also discusses how mechanical properties such as microhardness, elastic modulus and Poisson's ratio are influenced by the processing techniques as well as the volume fraction of the titanium boride reinforcement. - Highlights: Black-Right-Pointing-Pointer Ti-TiB composites were processed by HIP, SPS and vacuum sintering. Black-Right-Pointing-Pointer The completion of Ti-TiB{sub 2} reaction was confirmed by XRD, SEM and EPMA studies. Black-Right-Pointing-Pointer Hardness and elastic properties of Ti-TiB composites were discussed. Black-Right-Pointing-Pointer Processing techniques were compared with respect to their microstructure.« less

EFFECT OF HEAT TREATMENT ON (Cr, Fe)7C3/γ-Fe COATINGS IN SITU SYNTHESIZED BY VACUUM ELECTRON BEAM IRRADIATION

NASA Astrophysics Data System (ADS)

Lu, Binfeng; Chen, Yunxia; Xu, Mengjia

(Cr, Fe)7C3/γ-Fe composite layer has been in situ synthesized on a low carbon steel surface by vacuum electron beam VEB irradiation. The synthesized samples were then subdued to different heat treatments to improve their impaired impact toughness. The microstructure, impact toughness and wear resistance of the heat-treated samples were studied by means of optical microscope (OM), X-ray diffraction (XRD), scanning electron microscope (SEM), microhardness tester, impact test machine and tribological tester. After heat treatment, the primary and eutectic carbides remained in their original shape and size, and a large number of secondary carbides precipitated in the iron matrix. Since the Widmanstatten ferrite in the heat affected zone (HAZ) transformed to fine ferrite completely, the impact toughness of the heat-treated samples increased significantly. The microhardness of the heat-treated samples decreased slightly due to the decreased chromium content in the iron matrix. The wear resistance of 1000∘C and 900∘C heat-treated samples was almost same with the as-synthesized sample. While the wear resistance of the 800∘C heat-treated one decreased slightly because part of the austenite matrix had transformed to ferrite matrix, which reduced the bonding of carbides particulates.

Microhardness of carbon-doped (111) p-type Czochralski silicon

NASA Technical Reports Server (NTRS)

Danyluk, S.; Lim, D. S.; Kalejs, J.

1985-01-01

The effect of carbon on (111) p-type Czochralski silicon is examined. The preparation of the silicon and microhardness test procedures are described, and the equation used to determine microhardness from indentations in the silicon wafers is presented. The results indicate that as the carbon concentration in the silicon increases the microhardness increases. The linear increase in microhardness is the result of carbon hindering dislocation motion, and the effect of temperature on silicon deformation and dislocation mobility is explained. The measured microhardness was compared with an analysis which is based on dislocation pinning by carbon; a good correlation was observed. The Labusch model for the effect of pinning sites on dislocation motion is given.

Fabrication of ultra-fine grained aluminium tubes by RTES technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jafarzadeh, H., E-mail: h.jafarzadeh@ut.ac.ir; Abrinia, K.

Recently, repetitive tube expansion and shrinking have been exploited as a means for producing ultra-fine grained and nano-crystalline microstructures for magnesium alloy tubes. This method includes two different half-cycles and was based on pressing a tubular part through an angular channel die with two shear zones. Since the aluminium alloys are the most widely used materials in industries, in this study, repetitive tube expansion and shrinking as a new severe plastic deformation technique was applied to commercially pure aluminium for fabricating ultra-fine grained aluminium tubes for the first time and the ability of this process in significant grain refinement ismore » determined even after single cycle. Transmission electron microscopy and X-ray diffraction were used to evaluate the microstructure of the repetitive tube expansion and shrinking processed materials and the examinations showed ultra-fine grains with the average grain size of 320 nm after one cycle of repetitive tube expansion and shrinking. The yield strength, ultimate tensile strength increased notably by the factor of 2.17 and 1.27 respectively, after one cycle of repetitive tube expansion and shrinking, whereas the elongation to failure as well as the uniform elongation decreased. Furthermore, micro-hardness distribution through the part's section proposed the hardness increasing to ~ 55 HV from the initial value of ~ 28 HV after one cycle of repetitive tube expansion and shrinking. - Highlights: • RTES was introduced for fabricating the UFGed AA1050 tubes for the first time. • Nano-grained AA1050 tube was obtained by RTES process. • Grain size of ~ 320 nm was obtained after two half-cycles of RTES process. • Yield and ultimate strength increased by the factor of 2.17 and 1.27 respectively. • The microhardness increased to ~ 55 HV from the initial value of ~ 28 HV.« less

Fluoride releasing and enamel demineralization around orthodontic brackets by fluoride-releasing composite containing nanoparticles.

PubMed

Melo, Mary A S; Morais, Weslanny A; Passos, Vanara F; Lima, Juliana P M; Rodrigues, Lidiany K A

2014-05-01

Fluoride-containing materials have been suggested to control enamel demineralization around orthodontic brackets during the treatment with fixed appliances. The improvement of their properties has been made through innovations, such as the application of nanotechnology by incorporation of nanofillers. This in vitro study evaluated the capacity of fluoride releasing and enamel demineralization inhibition of fluoride-releasing nanofilled cement around orthodontic brackets using an artificial caries biofilm model. Forty bovine enamel discs were selected by evaluating surface microhardness and randomized into four groups (n = 10): non-fluoride-releasing microfilled composite, fluoride-releasing microfilled composite, resin-modified glass ionomer cement (RMGI), and fluoride-releasing nanofilled composite (FN). After brackets bonding in each disc, the specimens were subjected to a cariogenic challenge through a Streptococcus mutans biofilm model. After the experimental period, the biofilm formed around the brackets was collected for fluoride analysis and the mineral loss around the brackets was determined by integrated demineralization via cross-sectional microhardness measurement at 20 and 70 μm from the bracket margin. Additionally, samples of each group were subjected to energy-dispersive X-ray spectroscopy (EDX) analysis examined under a scanning electron microscopy (SEM). ANOVA followed by Tukey test were applied for fluoride concentration and mineral loss data, respectively. At both distances, only RMGI statistically differed from the other groups presenting the lowest demineralization, although there was a trend to a lower demineralization of enamel around brackets in FN group. Similar condition was found to fluoride concentration and EDX/SEM analysis. Under the cariogenic exposure condition of this study, the fluoride-releasing nanofilled material had similar performance to fluoride-releasing microfilled materials. The presence of nanofillers in the fluoride-releasing materials studied did not promote further benefits against caries lesion development around brackets and presented inferior demineralization inhibition than the resin-modified glass ionomer material.

Microstructural Evolution of AlCoCrFeNiSi High-Entropy Alloy Powder during Mechanical Alloying and Its Coating Performance

PubMed Central

Fu, Ming; Xiong, Wei

2018-01-01

High-entropy alloys (HEAs) are promising structural materials due to their excellent comprehensive performances. The use of mechanically alloyed powders to deposit HEA coatings through atmospheric plasma spraying (APS) is an effective approach that can broaden the application areas of the HEAs. In this paper, a ductility–brittleness AlCoCrFeNiSi system was chosen as an object of study, and the detailed evolution of the surface morphology, particle size distribution, and microstructure of the powder during mechanical alloying was investigated. An AlCoCrFeNiSi HEA coating was deposited using powder milled for 10 h, which can be used as an ideal feedstock for APS. The surface morphology, microstructure, microhardness, and wear behavior of the coating at room temperature were investigated. The results showed that as the milling time increased, the particle size first increased, and then decreased. At the milling time of 10 h, simple body-centered cubic (BCC) and face-centered cubic (FCC) solid solution phases were formed. After spraying, the lamellar structure inside a single particle disappeared. An ordered BCC phase was detected, and the diffraction peaks of the Si element also disappeared, which indicates that phase transformation occurred during plasma spraying. A transmission electron microscopy analysis showed that nanometer crystalline grains with a grain size of about 30 nm existed in the APS coating. For the coating, an average microhardness of 612 ± 41 HV was obtained. Adhesive wear, tribo-oxidation wear, and slight abrasion wear took place during the wear test. The coating showed good wear resistance, with a volume wear rate of 0.38 ± 0.08 × 10−4 mm3·N−1·m−1, which makes it a promising coating for use in abrasive environments. PMID:29473872

Precipitation strengthened high strength, high conductivity Cu-Cr-Nb alloys produced by chill block melt spinning. Final Report Ph.D. Thesis

NASA Technical Reports Server (NTRS)

Ellis, David L.; Michal, Gary M.

1989-01-01

A series of Cu-based alloys containing 2 to 10 a/o Cr and 1 to 5 a/o Nb were produced by chill block melt spinning (CBMS). The melt spun ribbons were consolidated and hot rolled to sheet to produce a supersaturated Cu-Cr-Nb solid solution from which the high melting point intermetallic compound Cr2Nb could be precipitated to strengthen the Cu matrix. The results show that the materials possess electrical conductivities in excess of 90 percent that of pure Cu at 200 C and above. The strengths of the Cu-Cr-Nb alloys were much greater than Cu, Cu-0.6 Cr, NARloy-A, and NARloy-Z in the as-melt spun condition. The strengths of the consolidated materials were less than Cu-Cr and Cu-Cr-Zr below 500 C and 600 C respectively, but were significantly better above these temperatures. The strengths of the consolidated materials were greater than NARloy-Z, at all temperatures. The GLIDCOP possessed similar strength levels up to 750 C when the strength of the Cu-Cr-Nb alloys begins to degrade. The long term stability of the Cu-Cr-Nb alloys was measured by the microhardness of aged samples and the growth of precipitates. The microhardness measurements indicate that the alloys overage rapidly, but do not suffer much loss in strength between 10 and 100 hours which confirms the results of the electrical resistivity measurements taken during the aging of the alloys at 500 C. The loss in strength from peak strength levels is significant, but the strength remains exceptionally good. Transmission electron microscopy (TEM) of the as-melt spun samples revealed that Cr2Nb precipitates formed in the liquid Cu during the chill block melt spinning, indicating a very strong driving force for the formation of the precipitates. The TEM of the aged and consolidated materials indicates that the precipitates coarsen considerably, but remain in the submicron range.

Processing and characterization of laser sintered hybrid B4C/cBN reinforced Ti-based metal matrix composite

NASA Astrophysics Data System (ADS)

Gupta, Ankit; Hussain, Manowar; Misra, Saurav; Das, Alok Kumar; Mandal, Amitava

2018-06-01

The purpose of this study is to make a boron carbide (B4C) and cubic boron nitride (cBN) reinforced Ti6Al4V metal matrix composites (MMC's) by direct metal laser sintering (DMLS) technique using the continuous wave (CW) SPI fiber laser and to check the feasibility of the formation of three dimensional objects by this process. For this study, the process parameters like laser power density (3.528-5.172 W/cm2 (×104), scanning speed (3500-4500 mm/min), composition of the reinforced materials B4C (5-25% by volume) and cBN (3% by volume) were taken as input variables and hatching gap (0.2 mm), spot diameter (0.4 mm), layer thickness (0.4 mm) were taken as constant. It was analyzed that surface characteristic, density and the mechanical properties of sintered samples were greatly influenced by varying the input process parameters. Field emission scanning electron microscopy (FESEM), Energy dispersive X-ray spectroscopy (EDX) and X-Ray diffraction (XRD) were performed for microstructural analysis, elemental analysis, and recognition of intermetallic compounds respectively. Mechanical properties like micro-hardness & wear rate were examined by Vickers micro-hardness tester & pin on disc arrangement respectively. From hardness tests, it was observed that hardness property of the sintered specimens was increased as compared to the parent material. The XRD results show that there is a good affinity between Ti6Al4V-B4C-cBN to produce various intermetallic compounds which themselves enhance the mechanical properties of the samples. From FESEM analysis, we can conclude that there is a uniform distribution of reinforcements in the titanium alloy matrix. Furthermore, the coefficient of friction (COF) was characterized by the irregular pattern and it tends to decrease with an increase in the volume % of reinforcement. The results obtained in this work may be useful in preparing the MMC's with improved mechanical properties and overall characteristics.

Fabrication of anti-adhesion surfaces on aluminium substrates of rubber plastic moulds using electrolysis plasma treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meng, Jianbing, E-mail: jianbingmeng@126.com; Dong, Xiaojuan; Wei, Xiuting

An anti-adhesion surface with a water contact angle of 167° was fabricated on aluminium samples of rubber plastic moulds by electrolysis plasma treatment using mixed electrolytes of C{sub 6}H{sub 5}O{sub 7}(NH{sub 4}){sub 3} and Na{sub 2}SO{sub 4}, followed by fluorination. To optimise the fabrication conditions, several important processing parameters such as the discharge voltage, discharge time, concentrations of supporting electrolyte and stearic acid ethanol solution were examined systematically. Using scanning electron microscopy (SEM) to analyse surfaces morphology, micrometer scale pits, and protrusions were found on the surface, with numerous nanometer mastoids contained in the protrusions. These binary micro/nano-scale structures, whichmore » are similar to the micro-structures of soil-burrowing animals, play a critical role in achieving low adhesion properties. Otherwise, the anti-adhesion behaviours of the resulting samples were analysed by the atomic force microscope (AFM), Fourier-transform infrared spectrophotometer (FTIR), electrons probe micro-analyzer (EPMA), optical contact angle meter, digital Vickers microhardness (Hv) tester, and electronic universal testing. The results show that the electrolysis plasma treatment does not require complex processing parameters, using a simple device, and is an environment-friendly and effective method. Under the optimised conditions, the contact angle (CA) for the modified anti-adhesion surface is up to 167°, the sliding angle (SA) is less than 2°, roughness of the sample surface is only 0.409μm. Moreover, the adhesion force and H{sub v} are 0. 9KN and 385, respectively.« less

Microstructure and properties of thermally sprayed Al-Sn-based alloys for plain bearing applications

NASA Astrophysics Data System (ADS)

Marrocco, T.; Driver, L. C.; Harris, S. J.; McCartney, D. G.

2006-12-01

Al-Sn plain bearings for automotive applications traditionally comprise a multilayer structure. Conventionally, bearing manufacturing involves casting the Al-Sn alloy and roll-bonding to a steel backing strip. Recently, high-velocity oxyfuel (HVOF) thermal spraying has been used as a novel alternative manufacturing route. The present project extends previous work on ternary Al-Sn-Cu alloys to quaternary systems, which contain specific additions for potentially enhanced properties. Two alloys were studied in detail, namely, Al-20wt.%Sn-1wt.%Cu-2wt.%Ni and Al-20wt.%Sn-1wt.%Cu-7wt.%Si. This article will describe the microstructural evolution of these alloys following HVOF spraying onto steel substrates and subsequent heat treatment. The microstructures of powders and coatings were investigated by scanning electron microscopy, and the phases were identified by x-ray diffraction. Coating microhardnesses were determined under both as-sprayed and heat-treated conditions, and by the differences related to the microstructures that developed. Finally, the wear behavior of the sprayed and heat-treated coatings in hot engine oil was measured using an industry standard test and was compared with that of previous work on a ternary alloy.

Influence of dust and mud on the optical, chemical, and mechanical properties of a pv protective glass

NASA Astrophysics Data System (ADS)

Yilbas, Bekir Sami.; Ali, Haider; Khaled, Mazen M.; Al-Aqeeli, Nasser; Abu-Dheir, Numan; Varanasi, Kripa K.

2015-10-01

Recent developments in climate change have increased the frequency of dust storms in the Middle East. Dust storms significantly influence the performances of solar energy harvesting systems, particularly (photovoltaic) PV systems. The characteristics of the dust and the mud formed from this dust are examined using various analytical tools, including optical, scanning electron, and atomic force microscopies, X-ray diffraction, energy spectroscopy, and Fourier transform infrared spectroscopy. The adhesion, cohesion and frictional forces present during the removal of dry mud from the glass surface are determined using a microtribometer. Alkali and alkaline earth metal compounds in the dust dissolve in water to form a chemically active solution at the glass surface. This solution modifies the texture of the glass surface, thereby increasing the microhardness and decreasing the transmittance of the incident optical radiation. The force required to remove the dry mud from the glass surface is high due to the cohesive forces that result from the dried mud solution at the interface between the mud and the glass. The ability altering the characteristics of the glass surface could address the dust/mud-related limitations of protective surfaces and has implications for efficiency enhancements in solar energy systems.

Characterization of irradiated AISI 316L stainless steel disks removed from the Spallation Neutron Source

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vevera, Bradley J; Hyres, James W; McClintock, David A

2014-01-01

Irradiated AISI 316L stainless steel disks were removed from the Spallation Neutron Source (SNS) for post-irradiation examination (PIE) to assess mechanical property changes due to radiation damage and erosion of the target vessel. Topics reviewed include high-resolution photography of the disk specimens, cleaning to remove mercury (Hg) residue and surface oxides, profile mapping of cavitation pits using high frequency ultrasonic testing (UT), high-resolution surface replication, and machining of test specimens using wire electrical discharge machining (EDM), tensile testing, Rockwell Superficial hardness testing, Vickers microhardness testing, scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS). The effectiveness of the cleaning proceduremore » was evident in the pre- and post-cleaning photography and permitted accurate placement of the test specimens on the disks. Due to the limited amount of material available and the unique geometry of the disks, machine fixturing and test specimen design were critical aspects of this work. Multiple designs were considered and refined during mock-up test runs on unirradiated disks. The techniques used to successfully machine and test the various specimens will be presented along with a summary of important findings from the laboratory examinations.« less

High-Performance Molybdenum Coating by Wire–HVOF Thermal Spray Process

NASA Astrophysics Data System (ADS)

Tailor, Satish; Modi, Ankur; Modi, S. C.

2018-04-01

Coating deposition on many industrial components with good microstructural, mechanical properties, and better wear resistance is always a challenge for the thermal spray community. A number of thermal spray methods are used to develop such promising coatings for many industrial applications, viz. arc spray, flame spray, plasma, and HVOF. All these processes have their own limitations to achieve porous free, very dense, high-performance wear-resistant coatings. In this work, an attempt has been made to overcome this limitation. Molybdenum coatings were deposited on low-carbon steel substrates using wire-high-velocity oxy-fuel (W-HVOF; WH) thermal spray system (trade name HIJET 9610®). For a comparison, Mo coatings were also fabricated by arc spray, flame spray, plasma spray, and powder-HVOF processes. As-sprayed coatings were analyzed using x-ray diffraction, scanning electron microscopy for phase, and microstructural analysis, respectively. Coating microhardness, surface roughness, and porosity were also measured. Adhesion strength and wear tests were conducted to determine the mechanical and wear properties of the as-sprayed coatings. Results show that the coatings deposited by W-HVOF have better performance in terms of microstructural, mechanical, and wear resistance properties, in comparison with available thermal spray process (flame spray and plasma spray).

Influence of dust and mud on the optical, chemical, and mechanical properties of a pv protective glass.

PubMed

Yilbas, Bekir Sami; Ali, Haider; Khaled, Mazen M; Al-Aqeeli, Nasser; Abu-Dheir, Numan; Varanasi, Kripa K

2015-10-30

Recent developments in climate change have increased the frequency of dust storms in the Middle East. Dust storms significantly influence the performances of solar energy harvesting systems, particularly (photovoltaic) PV systems. The characteristics of the dust and the mud formed from this dust are examined using various analytical tools, including optical, scanning electron, and atomic force microscopies, X-ray diffraction, energy spectroscopy, and Fourier transform infrared spectroscopy. The adhesion, cohesion and frictional forces present during the removal of dry mud from the glass surface are determined using a microtribometer. Alkali and alkaline earth metal compounds in the dust dissolve in water to form a chemically active solution at the glass surface. This solution modifies the texture of the glass surface, thereby increasing the microhardness and decreasing the transmittance of the incident optical radiation. The force required to remove the dry mud from the glass surface is high due to the cohesive forces that result from the dried mud solution at the interface between the mud and the glass. The ability altering the characteristics of the glass surface could address the dust/mud-related limitations of protective surfaces and has implications for efficiency enhancements in solar energy systems.

Pulse electrodeposition of self-lubricating Ni-W/PTFE nanocomposite coatings on mild steel surface

NASA Astrophysics Data System (ADS)

Sangeetha, S.; Kalaignan, G. Paruthimal; Anthuvan, J. Tennis

2015-12-01

Ni-W/PTFE nanocomposite coatings with various contents of PTFE (polytetafluoroethylene) particles were prepared by pulse current (PC) electrodeposition from the Ni-W plating bath containing self lubricant PTFE particles to be co-deposited. Co-deposited PTFE particulates were uniformly distributed in the Ni-W alloy matrix. The coatings were characterized by Scanning Electron Microscopy (SEM), Energy Dispersive X-Ray Analysis (EDAX), X-ray Diffractometry (XRD) and Vicker's micro hardness tester. Tafel Polarization and electrochemical Impedance methods were used to evaluate the corrosion resistance behaviour of the nanocomposite coatings in 3.5% NaCl solution. It was found that, the Ni-W/PTFE nanocomposite coating has better corrosion resistance than the Ni-W alloy coating. Surface roughness and friction coefficient of the coated samples were assessed by Mitutoyo Surftest SJ-310 (ISO1997) and Scratch tester TR-101-M4 respectively. The contact angle (CA) of a water droplet on the surface of nanocomposite coating was measured by Optical Contact Goniometry (OCA 35). These results indicated that, the addition of PTFE in the Ni-W alloy matrix has resulted moderate microhardness, smooth surface, less friction coefficient, excellent water repellency and enhanced corrosion resistance of the nanocomposite coatings.

Microstructural defect evolution in neutron - Irradiated 12Cr18Ni9Ti stainless steel during subsequent isochronous annealing

NASA Astrophysics Data System (ADS)

Tsay, K. V.; Maksimkin, O. P.; Turubarova, L. G.; Rofman, O. V.; Garner, F. A.

2013-08-01

Transmission electron microscopy and microhardness measurements were used to examine changes in microstructure and associated strengthening induced in austenitic stainless steel 12Cr18Ni9Ti irradiated to ˜0.001 and ˜5 dpa in the WWR-K reactor before and after being subjected to post-irradiation isochronal annealing. The relatively low values of irradiation temperature and dpa rate (˜80 °C and ˜1.2 × 10-8 dpa/s) experienced by this steel allowed characterization of defect microstructures over a wide range of defect ensembles, all at constant composition, produced first by irradiation and then by annealing at temperatures between 450 and 1050 °C. It was shown that the dispersed barrier hardening model with commonly accepted physical properties successfully predicted the observed hardening. It was also observed that when TiC precipitates form at higher annealing temperatures, the alloy does not change in hardness, reflecting a balance between precipitate-hardening and matrix-softening due to removal of solute-strengthening elements titanium and carbon. Such matrix-softening is not often considered in other studies, especially where the contribution of precipitates to hardening is a second-order effect.

Degradation of FEP thermal control materials returned from the Hubble Space Telescope

NASA Technical Reports Server (NTRS)

Zuby, Thomas M.; Degroh, Kim K.; Smith, Daniela C.

1995-01-01

After an initial 3.6 years of space flight, the Hubble Space Telescope was serviced through a joint effort with the NASA and the European Space Agency. Multi-layer insulation (MLI) was retrieved from the electronics boxes of the two magnetic sensing systems (MSS), also called the magnetometers, and from the returned solar array (SA-I) drive arm assembly. The top layer of each MLI assembly is fluorinated ethylene propylene (FEP, a type of Teflon). Dramatic changes in material properties were observed when comparing areas of high solar fluence to areas of low solar fluence. Cross sectional analysis shows atomic oxygen (AO) erosion values up to 25.4 mu m (1 mil). Greater occurrences of through-thickness cracking and surface microcracking were observed in areas of high solar exposure. Atomic force microscopy (AFM) showed increases in surface microhardness measurements with increasing solar exposure. Decreases in FEP tensile strength and elongation were measured when compared to non-flight material. Erosion yield and tensile results are compared with FEP data from the Long Duration Exposure Facility. AO erosion yield data, solar fluence values, contamination, micrometeoroid or debris impact sites, and optical properties are presented.

Synthesis and characterization of magnesium aluminate (MgAl2O4) spinel (MAS) thin films

NASA Astrophysics Data System (ADS)

Ahmad, Syed Muhammad; Hussain, Tousif; Ahmad, Riaz; Siddiqui, Jamil; Ali, Dilawar

2018-01-01

In a quest to identify more economic routes for synthesis of magnesium aluminate (MgAl2O4) spinel (MAS) thin films, dense plasma focus device was used with multiple plasma focus shots. Structural, bonding between composite films, surface morphological, compositional and hardness properties of MAS thin films were investigated by using x-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive x-rays (EDX) analysis and Vickers micro hardness test respectively. In XRD graph, the presence of MgAl2O4 diffraction peaks in crystallographic orientations (222), (400) and (622) pointed out the successful formation of polycrystalline thin films of MgAl2O4 with face centered cubic structure. The FTIR spectrums showed a major common transmittance band at 697.95 cm-1 which belongs to MgAl2O4. SEM micrographs illustrated a mesh type, granular and multi layers microstructures with significant melting effects. EDX spectrum confirmed the existence of magnesium, oxygen and aluminum in MAS films. A common increasing behavior in micro-hardness of composite MgAl2O4 films by increasing number of plasma focus shots was found.

Mechanical and thermal properties of SrO/BaO modified Y2O3-Al2O3-B2O3-SiO2 glasses and their compatibility with solid oxide fuel cell components

NASA Astrophysics Data System (ADS)

Kaur, Navdeep; Kaur, Gurbinder; Kumar, Devender; Singh, K.

2018-07-01

In this study, various compositions of (30-x) SrO-xBaO-10Al2O3-45SiO2-5B2O3-10Y2O3 (mol%) (5 ≤ x ≤ 25) were synthesized using the melt-quench technique. The as-prepared glasses were characterized by X-ray diffraction, micro-hardness testing, dilatometry, and scanning electron microscopy to determine their thermal and mechanical properties. Powders of the glasses were used to make diffusion couples with Crofer 22 APU (interconnect) and yttria stabilized zirconia (YSZ) for the interfacial study. Diffusion couples of the pre-oxidized Crofer 22 APU/glasses and YSZ/glasses were tested for 500 h at 850 °C. The coefficients of thermal expansion obtained for all the glasses were in the required range for applications in solid oxide fuel cells. The highest hardness and fracture toughness were obtained for the glass with x = 10 mol% due to the mixed modifier effect. However, the glass with x = 15 mol% exhibited better adhesion with YSZ and Crofer 22 APU.

Effect of Casein Phosphopeptide-Amorphous Calcium Phosphate and Three Calcium Phosphate on Enamel Microhardness.

PubMed

Haghgou, En Hr; Haghgoo, Roza; Roholahi, Mohamad R; Ghorbani, Zahra

2017-07-01

This study aims to investigate the effect of casein phos-phopeptide-amorphous calcium phosphate and three calcium phosphate (CPP-ACP and TCP) on increasing the microhardness of human enamel after induction of erosion. A total of 26 healthy human-impacted third molar teeth were chosen, and their hardness measured using a microhardness testing machine. The samples were immersed in Coca Cola (pH = 4.7) for 8 minutes. Then, micro-hardness was measured again, and these samples were randomly divided into four groups (two control groups and two experimental groups). (1) Negative control group: Artificial saliva was used for 10 minutes, (2) positive control group: Fluoride gel was used for 10 minutes, (3) β-TCP group: TCP was used for 10 minutes, (4) CCP-ACP group: CCP-ACP was used for 10 minutes. The final microhardness of those samples was measured, and the changes in microhardness of teeth within group and between groups were analyzed using the paired and analysis of variance tests respectively. Results were considered statistically significant at a level of p < 0.05. No significant difference was observed in microhard-ness between CPP-ACP group and TCP group (p = 0.368) during the time microhardness significantly dropped after soaking in soda. Casein phosphopeptide-amorphous calcium phosphate and TCP increased the microhardness of teeth. The increase in hardness in the TCP group was higher than in the CPP-ACP group, but this difference was not significant (p = 0.36). Casein phosphopeptide-amorphous calcium phosphate and TCP can affect the remineralization of erosive lesions.

Mechanical properties of ProTaper Gold nickel-titanium rotary instruments.

PubMed

Elnaghy, A M; Elsaka, S E

2016-11-01

To evaluate and compare the resistance to cyclic fatigue and torsional stress, flexibility and surface microhardness of ProTaper Gold (PTG; Dentsply, Tulsa Dental Specialties, Tulsa, OK, USA) system with ProTaper Universal (PTU; Dentsply Maillefer, Ballaigues, Switzerland). PTG and PTU instruments were rotated in simulated canals and the number of cycles to failure was recorded to assess their cyclic fatigue resistance. Torsional strength was measured using a torsiometer after fixing firmly the apical 3 mm of the instrument. A scanning electron microscope was used to characterize the topographic features of the fracture surfaces of the broken instruments. The instruments were tested for bending resistance using cantilever-bending test. Vickers microhardness was measured on the cross section of instruments with 300 g load and 15 s dwell time. Data were analysed statistically using independent t-tests. Statistical significance was set at P < 0.05. PTG instruments had a significantly higher resistance to cyclic fatigue and flexibility than PTU (P < 0.001). The fractured cross-sectional surfaces revealed typical features of cyclic fractures, including crack origins, fatigue zones and overload fast fracture zones. On the other hand, PTU instruments were associated with higher resistance to torsional stress and microhardness than PTG instruments (P < 0.001). After torsional tests, the fractured cross-sectional surfaces revealed skewed dimples near the centre of the fracture surfaces and circular abrasion streaks. The PTG instrument had improved resistance to cyclic fatigue and flexibility compared with PTU. PTU instruments had improved resistance to torsional stress and microhardness compared with PTG. © 2015 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Comparative assessment of the microhardness and plastic degradation mechanism of deposited modulated coatings on mild steel

NASA Astrophysics Data System (ADS)

Fayomi, O. S. I.; Anawe, P. A. L.; Inegbenebor, A. O.; Udoye, N. E.

2018-05-01

Zinc based coatings modified with aluminium and tin inclusions were electrodeposited in chloride zinc sulfate electrolytes containing a metallic powder of titanium. It was found that presence of these particulates is suitable to obtain ZnAlSn-Ti composites coating that could help increase the microhardnesss characteristics and wear properties. The hardness and wear properties of the deposited coatings were examined with diamond base micro-hardness tester and CETR reciprocating sliding tester respectively. The structural properties were examined with the help of scanning electron microscope. It was observed that structural coating surface impact on the hardness propagation with increases from 33.4 to 299 kgf mm-2 (HVN40), and shows a considerably higher wear resistance from 2.351g/min to 0.002g/min. It is obvious that plastic deformation of the working steel structure is dependent on protective coating and the concentration of the individual particulate.

Comparative evaluation of Nano-Hydroxyapatite preparation and Calcium Sucrose Phosphate on microhardness of deciduous teeth after iron drop exposure - An in-vitro study.

PubMed

Rathi, Nilesh; Baid, Rutika; Baliga, Sudhindra; Thosar, Nilima

2017-04-01

To evaluate and compare the microhardness of deciduous teeth treated with nano-hydroxyapatite and calcium sucrose phosphate after iron drop exposure. Twenty healthy anterior deciduous teeth were collected and stored in 0.9% saline solution at room temperature. All the teeth were immersed in artificial saliva in an incubator shaker at 37° for an hour and then subjected to Vickers microhardness test at 100g load for 5 seconds. The teeth were then immersed in iron drop for 5 minutes, twice daily, rinsed with distilled water and kept in artificial saliva. This procedure was repeated for 7 days and teeth were subjected to microhardness testing. Further, the teeth were divided in two groups, each group containing 10 teeth. In group I, nanohydroxyapatite preparation and in group II, calcium sucrose phosphate were applied for 10 minutes, twice daily for 7 days and subjected again to microhardness testing again. Vickers microhardness analysis revealed that iron drop exposure to teeth caused significant decrease in microhardness ( p <0.05). Application of nanohydroxyapatite preparation in Group I showed significantly increased enamel microhardness (206.90) than that after iron drop exposure. Similarly, application of calcium sucrose phosphate in Group II showed significantly increased enamel microhardness (200.89) than that after iron drop exposure. Statistical difference was seen between the two groups, with nanohydroxyapatite preparation showing increased microhardness than calcium sucrose phosphate. Nanohydroxyapatite preparation and calcium sucrose phosphate have remineralizing effect over teeth affected by acid challenge of iron drops, nanohydroxyapatite preparation showing better results than calcium sucrose phosphate. Key words: Iron drops, Nanohydroxyapaptite, calcium sucrose phosphate, anticay.

Determination of fracture toughness of calcium phosphate coatings deposited onto Ti6Al4V substrate by using indentation technique

NASA Astrophysics Data System (ADS)

Aydin, Ibrahim; Cetinel, Hakan; Pasinli, Ahmet

2012-09-01

In this study, fracture toughness values of calcium phosphate (CaP) coatings deposited onto Ti6Al4V substrate were determined by using Vickers indentation method. In this new patent holding method, the activation processes were performed with NaOH and NaOH+H2O2 on the Ti6Al4V material surface. Thicknesses of CaP coatings were measured from cross-sections of the samples by using optical microscopy. Vickers indentation tests were performed by using microhardness tester. Young's modulus values of the coatings were determined by using ultra microhardness tester. As a result, fracture toughness (K1C) values of the CaP coatings produced by using two different activation processes, were calculated by using experimental study results. These were found to be 0.43 MPa m1/2 and 0.39 MPa m1/2, respectively. It was determined that the CaP coating on Ti6Al4V activated by NaOH+H2O2 had higher fracture toughness than the CaP coating on Ti6Al4V activated by NaOH.

Effect of at-home bleaching with different thickeners and aging on physical properties of a nanocomposite.

PubMed

Gouveia, Thayla Hellen Nunes; Públio, Juliana do Carmo; Ambrosano, Glaucia Maria Bovi; Paulillo, Luís Alexandre Maffei Sartini; Aguiar, Flávio Henrique Baggio; Lima, Débora Alves Nunes Leite

2016-01-01

To evaluate the influence of 16% carbamide peroxide (CP) containing different thickeners on the physical characteristics of a nanocomposite resin submitted or not to accelerated artificial aging (AAA). One hundred samples were randomly distributed into two groups (n = 50) according to AAA. Each group was divided into 5 subgroups (n = 10) depending on the bleaching/thickener treatment: CP + carbopol, CP + natrosol, carbopol, natrosol, and no treatment (control). The physical properties tested were color (ΔE), gloss (GU), mean roughness (Ra), and Knoop microhardness (KHN). The resin surface was performed with atomic force microscopy (AFM). The color (variable Δ E) was assessed with two-way analysis of variance (ANOVA) and additionally with Tukey's and Dunnett's tests, the roughness values were submitted to Kruskal-Wallis, Dunn's, and Mann-Whitney's tests. Data on gloss and KHN were submitted to two-way ANOVA and Tukey's test (α = 0.05). Among the physical properties evaluated, CP + carbopol promoted a reduction in composite microhardness only, thus differing statistically from the controls. As for CP + natrosol, such a change was not observed. The aging process reduced all the physical properties, thus differing statistically from the nonaging group. CP + carbopol increased the roughness and decreased the gloss of aged resins, whereas natrosol reduced gloss only, which differed statistically from the controls. AFM showed evidence of the loss of organic matrix and exposure to load particles in the aged samples. Therefore, the replacement of carbopol with natrosol provided maintenance of the composite microhardness following bleaching. The aging process reduced the physical properties evaluated, and some changes were enhanced by the application of bleaching.

Structural, mechanical, electrical and wetting properties of ZrNx films deposited by Ar/N2 vacuum arc discharge: Effect of nitrogen partial pressure

NASA Astrophysics Data System (ADS)

Abdallah, B.; Naddaf, M.; A-Kharroub, M.

2013-03-01

Non-stiochiometric zirconium nitride (ZrNx) thin films have been deposited on silicon substrates by vacuum arc discharge of (N2 + Ar) gas mixtures at different N2 partial pressure ratio. The microstructure, mechanical, electrical and wetting properties of these films are studied by means of X-ray diffraction (XRD), micro-Raman spectroscopy, Rutherford back scattering (RBS) technique, conventional micro-hardness testing, electrical resistivity, atomic force microscopy (AFM) and contact angle (CA) measurements. RBS results and analysis show that the (N/Zr) ratio in the film increases with increasing the N2 partial pressure. A ZrNx film with (Zr/N) ratio in the vicinity of stoichiometric ZrN is obtained at N2 partial pressure of 10%. XRD and Raman results indicate that all deposited films have strained cubic crystal phase of ZrN, regardless of the N2 partial pressure. On increasing the N2 partial pressure, the relative intensity of (1 1 1) orientation with respect to (2 0 0) orientation is seen to decrease. The effect of N2 partial pressure on micro-hardness and the resistivity of the deposited film is revealed and correlated to the alteration of grain size, crystallographic texture, stoichiometry and residual stress developed in the film. In particular, it is found that residual stress and nitrogen incorporation in the film play crucial role in the alteration of micro-hardness and resistivity respectively. In addition, CA and AFM results demonstrate that as N2 partial pressure increases, both the surface hydrophobicity and roughness of the deposited film increase, leading to a significant decrease in the film surface free energy (SFE).

Efficacy of calcium- and fluoride-containing materials for the remineralization of primary teeth with early enamel lesion.

PubMed

Memarpour, Mahtab; Soltanimehr, Elham; Sattarahmady, Naghmeh

2015-09-01

The aim of the study was to determine the efficacy of different products containing fluoride, calcium and phosphate for enamel remineralization in eroded primary teeth. A total of 90 sound primary canine teeth were randomly divided into 5 groups of 18 teeth each: 1) control (polished enamel), 2) 5% DuraShield sodium fluoride varnish, 3) 500 ppm fluoridated toothpaste, 4) casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) cream, and 5) Clinpro White varnish containing functionalized tri-calcium phosphate (fTCP). Enamel microhardness (EMH) was measured in all samples before and after demineralization and after 28 days of remineralization. Also 8 samples in groups 2 to 5 and four samples of sound and demineralized enamel were examined with atomic force microscopy (AFM). All data were analyzed with one-way ANOVA (p<0.05). Mean microhardness of demineralized enamel was significantly lower than in enamel at baseline (p<0.001). Remineralization significantly increased microharness in groups 2 to 5 compared to the control group (p<0.001). Percent EMH after remineralization with CPP-ACP was significantly higher than after fTCP (p=0.029), toothpaste (p< 0.001) or fluoride varnish (p<0.001); however, there was no significant difference between toothpaste and fluoride varnish (p=0.062). Microhardness increased more after fTCP treatment than after treatment with sodium fluoride varnish (p<0.001) or fluoridated toothpaste (p=0.045). AFM images showed that enamel roughness decreased most after treatment with fTCP, followed by CPP-ACP, toothpaste and fluoride varnish. The efficacy of CPP-ACP cream for remineralizing eroded enamel was greater than fluoride toothpaste, fluoride varnish or fTCP varnish. © 2015 Wiley Periodicals, Inc.

Characterization and mechanical properties investigation of TiN-Ag films onto Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Du, Dongxing; Liu, Daoxin; Zhang, Xiaohua; Tang, Jingang; Xiang, Dinggen

2016-03-01

To investigate their effect on fretting fatigue (FF) resistance of a Ti-6Al-4V alloy, hard solid lubricating composite films of TiN with varying silver contents (TiN-Ag) were deposited on a Ti-6Al-4V alloy using ion-assisted magnetron sputtering. The surface morphology and structure were analyzed by atomic force microscopy, X-ray diffractometry, X-ray photoelectron spectroscopy, and transmission electron microscopy. The hardness, bonding strength, and toughness of films were tested using a micro-hardness tester, scratch tester, and a repeated press-press test system that was manufactured in-house, respectively. The FF resistance of TiN-Ag composite films was studied using self-developed devices. The results show that the FF resistance of a titanium alloy can be improved by TiN-Ag composite films, which were fabricated using hard TiN coating doped with soft Ag. The FF life of Ag0.5, Ag2, Ag5, Ag10 and Ag20 composite films is 2.41, 3.18, 3.20, 2.94 and 2.87 times as great as that of the titanium alloy, respectively. This is because the composite films have the better toughness, friction lubrication, and high bonding strength. When the atomic fraction of Ag changes from 2% to 5%, the FF resistance of the composite films shows the best performance. This is attributed to the surface integrity of the composite film is sufficiently fine to prevent the initiation and early propagation of FF cracks.

Characterization of retrieved orthodontic miniscrew implants.

PubMed

Eliades, Theodore; Zinelis, Spiros; Papadopoulos, Moschos A; Eliades, George

2009-01-01

The purposes of this study were to characterize the morphologic, structural, and compositional alterations and to assess any hardness changes in used orthodontic miniscrew implants. Eleven miniscrew implants (Aarhus Anchorage System, Medicon eG, Tuttlingen, Germany) placed in 5 patients were retrieved after successful service of 3.5 to 17.5 months; none showed signs of mobility or failure. These implants, and brand-, type-, and size-matched specimens as controls, were subjected to multi-technique characterization. Optical microscopy indicated loss of gloss with variable discoloration. Scanning electron microscopy and x-ray microanalysis showed morphologic alteration of the miniscrew implant surfaces with integuments formed on the surface. The materials precipitated on the surfaces were sodium, potassium, chlorine, iron, calcium, and phosphorus from the contact of the implant with biologic fluids such as blood and exudates, forming sodium chloride, potassium chloride, and calcium-phosphorus precipitates. The composition of the implant was similar to that of a titanium alloy. X-ray microtomography analysis showed no bulk structure alterations. Vickers microhardness testing showed no increased bulk or surface hardness of the retrieved specimens compared with the controls, excluding the possibility of strain-hardening phenomena as a result of self-tapping and self-drilling placement and related loading conditions. Used titanium-alloy miniscrew implants have morphologic and surface structural alterations including adsorption of an integument that is calcified as a result of contact of the implants with biologic fluids. Randomly organized osseointegration islets on these smooth titanium-alloy miniscrew surfaces might be enhanced by the extended period of retention in alveolar bone in spite of the smooth surface and immediate loading pattern of these implants.

Development of binary and ternary titanium alloys for dental implants.

PubMed

Cordeiro, Jairo M; Beline, Thamara; Ribeiro, Ana Lúcia R; Rangel, Elidiane C; da Cruz, Nilson C; Landers, Richard; Faverani, Leonardo P; Vaz, Luís Geraldo; Fais, Laiza M G; Vicente, Fabio B; Grandini, Carlos R; Mathew, Mathew T; Sukotjo, Cortino; Barão, Valentim A R

2017-11-01

The aim of this study was to develop binary and ternary titanium (Ti) alloys containing zirconium (Zr) and niobium (Nb) and to characterize them in terms of microstructural, mechanical, chemical, electrochemical, and biological properties. The experimental alloys - (in wt%) Ti-5Zr, Ti-10Zr, Ti-35Nb-5Zr, and Ti-35Nb-10Zr - were fabricated from pure metals. Commercially pure titanium (cpTi) and Ti-6Al-4V were used as controls. Microstructural analysis was performed by means of X-ray diffraction and scanning electron microscopy. Vickers microhardness, elastic modulus, dispersive energy spectroscopy, X-ray excited photoelectron spectroscopy, atomic force microscopy, surface roughness, and surface free energy were evaluated. The electrochemical behavior analysis was conducted in a body fluid solution (pH 7.4). The albumin adsorption was measured by the bicinchoninic acid method. Data were evaluated through one-way ANOVA and the Tukey test (α=0.05). The alloying elements proved to modify the alloy microstructure and to enhance the mechanical properties, improving the hardness and decreasing the elastic modulus of the binary and ternary alloys, respectively. Ti-Zr alloys displayed greater electrochemical stability relative to that of controls, presenting higher polarization resistance and lower capacitance. The experimental alloys were not detrimental to albumin adsorption. The experimental alloys are suitable options for dental implant manufacturing, particularly the binary system, which showed a better combination of mechanical and electrochemical properties without the presence of toxic elements. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

High temperature wear performance of HVOF-sprayed Cr3C2-WC-NiCoCrMo and Cr3C2-NiCr hardmetal coatings

NASA Astrophysics Data System (ADS)

Zhou, Wuxi; Zhou, Kesong; Li, Yuxi; Deng, Chunming; Zeng, Keli

2017-09-01

A novel Cr3C2-WC-NiCoCrMo and commercial Cr3C2-NiCr thermal spray-grade powders with particle size of -45 + 15 μm were prepared by an agglomeration and sintering process. Cr3C2-WC-NiCoCrMo and Cr3C2-NiCr coatings were deposited by high velocity oxygen fuel (HVOF) spraying. The fundamental properties of both coatings were evaluated and friction wear test against Al2O3 counterbodies of both coatings at high temperatures (450 °C, 550 °C, 650 °C) were carried out ball-on-disk high temperature tribometer. All specimens were characterized by optical microscopy, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy with energy dispersive spectroscopy (SEM/EDS) and 3D non-contact surface mapping profiler. The results have shown that the Cr3C2-WC-NiCoCrMo coating exhibited lower porosity, higher micro-hardness compared to the Cr3C2-NiCr coating. The Cr3C2-WC-NiCoCrMo coating also exhibited better wear resistance and higher friction coefficient compared to the Cr3C2-NiCr coating when sliding against the Al2O3 counterpart. Wear rates of both coatings increased with raising temperature. Both coatings experienced abrasive wear; hard phase particles (WC and Cr3C2) with different sizes, distributed in the matrix phase, will effectively improve the resistance against wear at high temperatures.

Physical properties and biocompatibility of UHMWPE-derived materials modified by synchrotron radiation.

PubMed

Bykova, Iu; Weinhardt, V; Kashkarova, A; Lebedev, S; Baumbach, T; Pichugin, V; Zaitsev, K; Khlusov, I

2014-08-01

The applications of synchrotron radiation (SR) in medical imaging have become of great use, particularly in angiography, bronchography, mammography, computed tomography, and X-ray microscopy. Thanks to recently developed phase contrast imaging techniques non-destructive preclinical testing of low absorbing materials such as polymers has become possible. The focus of the present work is characterization and examination of UHMWPE-derived materials widely used in medicine, before and after their exposure to SR during such testing. Physical properties, such as wettability, surface energy, IR-spectroscopy, roughness, optical microscopy, microhardness measurements of UHMWPE samples were studied before and after SR. The relationship between a growth of UHMWPE surface hydrophilicity after SR and surface colonization by stromal cells was studied in vitro. Obtained results demonstrate that SR may be used as prospective direction to examine bulk (porous) structure of polymer materials and/or to modify polymer surface and volume for tissue engineering.

Study on Composition, Microstructure and Wear Behavior of Fe-B-C Wear-Resistant Surfacing Alloys

NASA Astrophysics Data System (ADS)

Zhuang, Minghui; Li, Muqin; Wang, Jun; Ma, Zhen; Yuan, Shidan

2017-12-01

Fe-B-C alloy layers with various microstructures were welded on Q235 steel plates using welding powders/H08Mn2Si and welding wires composite surfacing technology. The relationship existing between the chemical composition, microstructure and wear resistance of the surfacing alloy layers was investigated by scanning electron microscopy, x-ray diffraction, electron backscatter diffraction and wear tests. The results demonstrated that the volume fractions and morphologies of the microstructures in the surfacing alloy layers could be controlled by adjusting the boron and carbon contents in the welding powders, which could further regulate the wear resistance of the surfacing alloy layers. The typical microstructures of the Fe-B-C surfacing alloy layers included dendritic Fe, rod-like Fe2B, fishbone-like Fe2B and daisy-like Fe3(C, B). The wear resistance of the alloy layers with various morphologies differed. The wear resistance order of the different microstructures was: rod-like Fe2B > fishbone-like Fe2B > daisy-like Fe3(C, B) > dendritic Fe. A large number of rod-like Fe2B with high microhardness could be obtained at the boron content of 5.70 5.90 wt.% and the carbon content of 0.50 0.60wt.%. The highest wear resistance of the Fe-B-C alloy layers reached the value of 24.1 g-1, which demonstrates the main microscopic cutting wear mechanism of the Fe-B-C alloy layers.

Interfacial characterization of SLM parts in multi-material processing: Metallurgical diffusion between 316L stainless steel and C18400 copper alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, Z.H., E-mail: AZHLIU@ntu.edu.sg; Zhang, D.Q., E-mail: ZHANGDQ@ntu.edu.sg; Sing, S.L., E-mail: SING0011@e.ntu.edu.sg

2014-08-15

Multi-material processing in selective laser melting using a novel approach, by the separation of two different materials within a single dispensing coating system was investigated. 316L stainless steel and UNS C18400 Cu alloy multi-material samples were produced using selective laser melting and their interfacial characteristics were analyzed using focused ion beam, scanning electron microscopy, energy dispersive spectroscopy and electron back scattered diffraction techniques. A substantial amount of Fe and Cu element diffusion was observed at the bond interface suggesting good metallurgical bonding. Quantitative evidence of good bonding at the interface was also obtained from the tensile tests where the fracturemore » was initiated at the copper region. Nevertheless, the tensile strength of steel/Cu SLM parts was evaluated to be 310 ± 18 MPa and the variation in microhardness values was found to be gradual along the bonding interface from the steel region (256 ± 7 HV{sub 0.1}) to the copper region (72 ± 3 HV{sub 0.1}). - Highlights: • Multi-material processing was successfully implemented and demonstrated in SLM. • Bi-metallic laminates of steel/Cu were successfully produced with the SLM process. • A substantial amount of Fe and Cu diffusion was observed at the bond interface. • Good metallurgical bonding was obtained at the interface of the steel/Cu laminates. • Highly refined microstructure was obtained due to rapid solidification in SLM.« less

Strengthening of Cu–Ni–Si alloy using high-pressure torsion and aging

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lee, Seungwon, E-mail: chominamlsw@gmail.com; WPI, International Institute for Carbon-Neutral Energy Research; Matsunaga, Hirotaka

2014-04-01

An age-hardenable Cu–2.9%Ni–0.6%Si alloy was subjected to high-pressure torsion. Aging behavior was investigated in terms of hardness, electrical conductivity and microstructural features. Transmission electron microscopy showed that the grain size is refined to ∼ 150 nm and the Vickers microhardness was significantly increased through the HPT processing. Aging treatment of the HPT-processed alloy led to a further increase in the hardness. Electrical conductivity is also improved with the aging treatment. It was confirmed that the simultaneous strengthening by grain refinement and fine precipitation is achieved while maintaining high electrical conductivity. Three dimensional atom probe analysis including high-resolution transmission electron microscopymore » revealed that nanosized precipitates having compositions of a metastable Cu{sub 3}Ni{sub 5}Si{sub 2} phase and a stable NiSi phase were formed in the Cu matrix by aging of the HPT-processed samples and these particles are responsible for the additional increase in strength after the HPT processing. - Highlights: • Grain refinement is achieved in Corson alloy the size of ∼150nm by HPT. • Aging at 300°C after HPT leads to further increase in the mechanical property. • Electrical conductivity reaches 40% IACS after aging for 100 h. • 3D-APT revealed the formation of nanosized-precipitates during aging treatment. • Simultaneous hardening in both grain refinement and precipitation is achieved.« less

Effect of Heat Treatment on Microstructure and Mechanical Properties of Laser Additively Manufactured AISI H13 Tool Steel

NASA Astrophysics Data System (ADS)

Chen, ChangJun; Yan, Kai; Qin, Lanlan; Zhang, Min; Wang, Xiaonan; Zou, Tao; Hu, Zengrong

2017-11-01

The effect of heat treatment on microstructure and mechanical properties (microhardness, wear resistance and impact toughness) of laser additively manufactured AISI H13 tool steel was systemically investigated. To understand the variation of microstructure and mechanical properties under different heat treatments, the as-deposited samples were treated at 350, 450, 550, 600 and 650 °C/2 h, respectively. Microstructure and phase transformation were investigated through optical microscopy, scanning electron microscope and transmission electron microscope. The mechanical properties were characterized by nanoindentation tests, Charpy tests and high-temperature wear tests. The microstructure of as-deposited samples consisted of martensite, ultrafine carbides and retained austenite. After the tempering treatment, the martensite was converted into tempered martensite and some fine alloy carbides which precipitated in the matrix. When treated at 550 °C, the greatest hardness and nanohardness were 600 HV0.3 and 6119.4 MPa due to many needle-like carbides precipitation. The value of hardness increased firstly and then decreased when increasing the temperature. When tempered temperatures exceeded 550 °C, the carbides became coarse, and martensitic matrix recrystallized at the temperature of 650 °C. The least impact energy was 6.0 J at a temperature of 550 °C. Samples tempered at 550 °C had larger wear volume loss than that of others. Wear resistances of all samples under atmospheric condition at 400 °C showed an oxidation mechanism.

Effect of storage solutions on microhardness of crown enamel and dentin.

PubMed

Aydın, Berdan; Pamir, Tijen; Baltaci, Aysun; Orman, Mehmet N; Turk, Tugba

2015-01-01

The aim of this study was to determine alterations in microhardness of crown dentin and enamel, after 2 and 12-month storage in de-ionized water, 0.2% glutaraldehyde, Hanks' Balanced Salt Solution (HBSS), 0.1% sodium hypochlorite (NaOCl) or 0.1% thymol. Freshly extracted, nonsterile 60 intact human premolars were distributed to five groups. Six teeth from each group were evaluated after two, and other six teeth were evaluated after 12 months storage. After grinding and polishing of teeth, Vickers hardness was evaluated with making indentations on enamel and dentin, using a pyramid diamond indenter tip exerting 100 g load for 15 s. After 2 months storage in solutions, range of the hardness values (HV) of enamel and dentin were in between 315-357 and 64-67, respectively. However, 12 months storage of the teeth resulted in a statistically significant decrease in microhardness when compared to microhardness of teeth stored for 2 months (P = 0.001). Although the differences were not significant regarding solutions, all solutions decreased the microhardness both in enamel and dentin (P > 0.05). However, decrease in microhardness was relatively less in de-ionized water and thymol solutions while glutaraldehyde decreased microhardness the most: 63% for enamel and 53% for dentin. Microhardness of enamel and dentin was in an acceptable range when teeth were stored for 2 months in de-ionized water, glutaraldehyde, HBSS, NaOCl or in thymol; thus, teeth kept up to 2 months in these solutions can be used for mechanical in vitro tests. However, 12 months storage significantly decreased the microhardness of enamel and dentin.

Effect of tray-based and trayless tooth whitening systems on microhardness of enamel surface and subsurface.

PubMed

Teixeira, Erica C N; Ritter, André V; Thompson, Jeffrey Y; Leonard, Ralph H; Swift, Edward J

2004-12-01

To evaluate the effect of tray-based and trayless tooth whitening systems on surface and subsurface microhardness of human enamel. Enamel slabs were obtained from recently extracted human third molars. Specimens were randomly assigned to six groups according to tooth whitening treatment (n = 10): 6.0% hydrogen peroxide (HP) (Crest Whitestrips), 6.5% HP (Crest Professional Whitestrips), 7.5% HP (Day White Excel 3), 9.5% HP (Day White Excel 3), 10% carbamide peroxide (Opalescence), and a control group (untreated). Specimens were treated for 14 days following manufacturers' recommended protocols, and were immersed in artificial saliva between treatments. Enamel surface Knoop microhardness (KHN) was measured immediately before treatment, and at days 1, 7, and 14 of treatment. After treatment, subsurface microhardness was measured at depths of 50-500 microm. Data were analyzed for statistical significance using analysis of variance. Differences in microhardness for treated vs. untreated enamel surface were not statistically significant at any time interval. For 6.5% and 9.5% HP, there was a decrease in surface microhardness values during treatment, but at the end of treatment the microhardness values were not statistically different from the baseline values. For the enamel subsurface values, no differences were observed between treated vs. untreated specimens at each depth. Trayless and tray-based tooth whitening treatments do not significantly affect surface or subsurface enamel microhardness.

Evaluation of remineralization capacity of casein phosphopeptide-amorphous calcium phosphate on the carbamide peroxide treated enamel

PubMed Central

Penumatsa, Narendra Varma; Kaminedi, Raja Rajeswari; Baroudi, Kusai; Barakath, Ola

2015-01-01

Objective: The aim of this study was to evaluate the potential of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) in remineralizing the bleached enamel surface using micro-hardness. Materials and Methods: Thirty human enamel slabs were randomly divided into three groups (n = 10). Groups A and B were exposed to 20% carbamide peroxide and 35% carbamide peroxide gel, respectively. After the exposure to the bleaching agent, the slabs were kept in artificial saliva for 1-week. Group C (control group) were kept in artificial saliva for 1-week. Vickers micro-hardness test was performed by Leica VMHT-Mot micro-hardness tester. CPP-ACP (Gc Tooth Mousse, Melbourne, Australia) was then applied to specimens of Groups A and B for 3 min for 2 weeks. Micro-hardness values of postbleach Group A (Ar) and Group B (Br) were recorded and statistically analyzed by paired t-test and one-way analysis of variance at the significance level of α =0.05. Results: There was a significant decrease in micro-hardness of enamel in carbamide peroxide bleached groups. However, there was a significant increase in micro-hardness after the remineralization by CPP-ACP and the extent of remineralization is more for the Group B. Conclusions: That bleaching agents reduced enamel micro-hardness and the use of CPP-ACP after bleaching can significantly enhance the micro-hardness of bleached enamel. PMID:26538923

Microhardness of light- and dual-polymerizable luting resins polymerized through 7.5-mm-thick endocrowns.

PubMed

Gregor, Ladislav; Bouillaguet, Serge; Onisor, Ioana; Ardu, Stefano; Krejci, Ivo; Rocca, Giovanni Tommaso

2014-10-01

The complete polymerization of luting resins through thick indirect restorations is still questioned. The purpose of this study was to evaluate the degree of polymerization of light- and dual-polymerizable luting resins under thick indirect composite resin and ceramic endocrowns by means of Vickers microhardness measurements. The Vickers microhardness measurements of a light-polymerizable microhybrid composite resin and a dual-polymerizable luting cement directly polymerized in a natural tooth mold for 40 seconds with a high-power light-emitting diode lamp (control) were compared with measurements after indirect irradiation through 7.5-mm-thick composite resin and ceramic endocrowns for 3 × 90 seconds. A test-to-control microhardness values ratio of 0.80 at a depth of 0.5 mm below the surface was assumed as the criterion for adequate conversion. For the Vickers microhardness measurements of a dual-polymerizable luting cement, no differences (P>.05) were found between Vickers microhardness control values and values reported after polymerization through composite resin and ceramic endocrowns. For The Vickers microhardness measurements (±SD) of a light-polymerizable microhybrid composite resin, control values were significantly (P<.05) higher (111 ±3.3) than those reported after polymerization through composite resin (100.5 ±3.8) and ceramic (99.7 ±2.3) endocrowns. However, the hardness values of The Vickers microhardness measurements of a light-polymerizable microhybrid composite resin polymerized through the endocrowns were approximately 10% to 12% lower than those of the control values. Two-way ANOVA showed the influence of the luting material on the Vickers microhardness values (P<.05). The effect of endocrown material was not significant (P>.05). Under the conditions of this in vitro study, Vickers microhardness values of the dual-polymerizable resin cement and the light-polymerizable restorative composite resin irradiated for 3 × 90 seconds with a high irradiance light-emitting diode lamp through 7.5-mm-thick endocrowns reached at least 80% of the control Vickers microhardness values, which means that both materials can be adequately polymerized when they are used for luting thick indirect restorations. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Microstructure stability of ultra-fine grained magnesium alloy AZ31 processed by extrusion and equal-channel angular pressing (EX–ECAP)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stráská, Jitka, E-mail: straska.jitka@gmail.com; Janeček, Miloš, E-mail: janecek@met.mff.cuni.cz; Čížek, Jakub, E-mail: jcizek@mbox.troja.mff.cuni.cz

Thermal stability of the ultra-fine grained (UFG) microstructure of magnesium AZ31 alloy was investigated. UFG microstructure was achieved by a combined two-step severe plastic deformation process: the extrusion (EX) and subsequent equal-channel angular pressing (ECAP). This combined process leads to refined microstructure and enhanced microhardness. Specimens with UFG microstructure were annealed isochronally at temperatures 150–500 °C for 1 h. The evolution of microstructure, mechanical properties and dislocation density was studied by electron backscatter diffraction (EBSD), microhardness measurements and positron annihilation spectroscopy (PAS). The coarsening of the fine-grained structure at higher temperatures was accompanied by a gradual decrease of the microhardnessmore » and decrease of dislocation density. Mechanism of grain growth was studied by general equation for grain growth and Arrhenius equation. Activation energies for grain growth were calculated to be 115, 33 and 164 kJ/mol in temperature ranges of 170–210 °C, 210–400 °C and 400–500 °C (443–483 K, 483–673 K and 673–773 K), respectively. - Highlights: • Microhardness of UFG AZ31 alloy decreases with increasing annealing temperature. • This fact has two reasons: dislocation annihilations and/or grain growth. • The activation energies for grain growth were calculated for all temperature ranges.« less

Catalase and sodium fluoride mediated rehabilitation of enamel bleached with 37% hydrogen peroxide.

PubMed

Thakur, Ruchi; Shigli, Anand L; Sharma, Divya; Thakur, Gagan

2015-01-01

Bleaching agents bring about a range of unwanted changes in the physical structure of enamel which needs to be restored qualitatively and timely. Catalase being an antioxidant ensures the effective removal of free radicals and improvement in fluoride mediated remineralization from the enamel microstructure which if retained may harm the integrity and affect the hardness of enamel. Thirty freshly extracted incisors were sectioned to 6 slabs which were divided into 5 groups: Group A, control; Group B, treatment with 37% hydrogen peroxide (HP); Group C, treatment with 37% HP and catalase, Group D, treatment with 37% HP and 5% sodium fluoride application, Group E, treatment with 37% HP followed by catalase and 5% sodium fluoride. Scanning electron microscope and microhardness analysis were done for all slabs. One-way ANOVA test was applied among different groups. Vicker's microhardness number (VHN) of Group B and C was significantly lower. No significant difference between VHN of Group B and C. VHN of Group D was significantly higher than Group A, B, and C; but significantly lower than Group E. VHN of Group E was significantly higher than any other experimental group. One-way ANOVA revealed a highly significant P value (P = 0.0001) and so Tukey's post-hoc Test for the group comparisons was employed. Subsequent treatment of bleached enamel with catalase and fluoride varnish separately results in repairing and significantly increasing the microhardness.

Effects of nano-LaF3 on the friction and wear behaviors of PTFE-based bonded solid lubricating coatings under different lubrication conditions

NASA Astrophysics Data System (ADS)

Jia, Yulong; Wan, Hongqi; Chen, Lei; Zhou, Huidi; Chen, Jianmin

2016-09-01

Influence of nanometer lanthanum fluoride (nano-LaF3) on the tribological behaviors of polytetrafluoroethylene (PTFE) bonded solid lubricating coatings were investigated using a ring-on-block friction-wear tester under dry friction and RP-3 jet fuel lubrication conditions. The worn surfaces and transfer films formed on the counterpart steel rings were observed by scanning electron microscope (SEM) and optical microscope (OM), respectively. The microstructures of the nano-LaF3 modified coatings and the distribution states of nano-LaF3 were studied by field-emission scanning electron microscope (FESEM) and transmission electron microscopy (TEM), respectively. The results show that incorporation of nano-LaF3 improves the microhardness and the friction-reduced and anti-wear abilities of PTFE bonded solid lubricating coatings. The wear life of the modified coating is about 6 times longer than that of the coating without nano-LaF3 filler at a relatively low applied load (200 N) and rotary speed (1000 rev/min) under dry friction condition. The friction coefficient and wear life of the modified coating decrease with increase of applied load under dry friction, but the friction coefficient has hardly any variation and wear life decreases under RP-3 jet fuel lubrication condition. In addition, the friction coefficient of the modified coating reduces with the rotary speed increasing under dry sliding but has little change under RP-3 lubrication, the wear life increases firstly and then decreases. The results indicated that the wear failure mechanism is dominated by applied load, which plays an important role in guidance of application of nano-LaF3 modified PTFE bonded coating under different working environment.

Mechanisms of ultrafine-grained austenite formation under different isochronal conditions in a cold-rolled metastable stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Celada-Casero, C., E-mail: c.celada@cenim.csic.es

The primary objective of this work is to obtain fundamental insights on phase transformations, with focus on the reaustenitization process (α′→γ transformation), of a cold-rolled (CR) semi-austenitic metastable stainless steel upon different isochronal conditions (0.1, 1, 10 and 100 °C/s). For this purpose, an exhaustive microstructural characterization has been performed by using complementary experimental such as scanning and transmission electron microscopy (SEM and TEM), electron backscattered diffraction (EBSD), electron probe microanalysis (EPMA), micro-hardness Vickers and magnetization measurements. It has been detected that all microstructural changes shift to higher temperatures as the heating rate increases. The reaustenitization occurs in two-steps formore » all heating rates, which is attributed to the chemical banding present in the CR state. The α′→γ transformation is controlled by the migration of substitutional alloying elements across the austenite/martensite (γ/α′) interface, which finally leads to ultrafine-grained reaustenitized microstructures (440–280 nm). The morphology of the martensite phase in the CR state has been found to be the responsible for such a grain refinement, along with the presence of χ-phase and nanometric Ni{sub 3}(Ti,Al) precipitates that pin the austenite grain growth, especially upon slowly heating at 0.1 °C/s. - Highlights: •Ultrafine-grained austenite structures are obtained isochronally at 0.1–100 °C/s •The α′→γ transformation occurs in two steps due to the initial chemical banding •A diffusional mechanism governs the α′→γ transformation for all heating rates •The dislocation-cell-type of martensite promotes a diffusional mechanism •Precipitates located at α′/γ interfaces hinder the austenite growth.« less

Effects of the bleaching procedures on enamel micro-hardness: Plasma Arc and diode laser comparison.

PubMed

Nematianaraki, Saeid; Fekrazad, Reza; Naghibi, Nasim; Kalhori, Katayoun Am; Junior, Aldo Brugnera

2015-10-02

One of the major side effects of vital bleaching is the reduction of enamel micro-hardness. The purpose of this study was to evaluate the influence of two different bleaching systems, Plasma Arc and GaAlAs laser, on the enamel micro-hardness. 15 freshly extracted human third molars were sectioned to prepare 30 enamel blocks (5×5 mm). These samples were then randomly divided into 2 groups of 15 each (n=15): a plasma arc bleaching group (: 350-700 nm) + 35% Hydrogen Peroxide whitening gel and a laser bleaching group (GaAlAs laser, λ: 810 nm, P: 10 W, CW, Special Tip) + 35% Hydrogen Peroxide whitening gel. Samples were subjected to the Vickers micro-hardness test (VHN) at a load of 50 g for 15s before and after treatment. Data were statistically analyzed by a Mann-Whitney test (p≤0.05). In the GaAlAs laser group, the enamel micro-hardness was 618.2 before and was reduced to 544.6 after bleaching procedures. In the plasma arc group, the enamel micro-hardness was 644.8 before and 498.9 after bleaching. Although both techniques significantly reduced VHN, plasma arc bleaching resulted in a 22.62% reduction in VHN for enamel micro-hardness, whereas an 11.89% reduction in VHN was observed for laser bleaching; this difference is statistically significant (p<0.001). Both bleaching techniques reduced enamel micro-hardness, although the reduction is much less significant with the GaAlAs laser than with the plasma arc. Therefore GaAlAs laser bleaching has fewer harmful effects than plasma arc in respect to enamel micro-hardness reduction.

The study of the modes of Ta-Zr powder mixture non-vacuum electron-beam cladding on the surface of the cp-titanium plates

NASA Astrophysics Data System (ADS)

Samoylenko, V. V.; Lozhkina, E. A.; Polyakov, I. A.; Lenivtseva, O. G.; Ivanchik, I. S.; Matts, O. E.

2016-11-01

The effect of the modes of non-vacuum electron-beam cladding of Ta-Zr powder mixtures on the structure and properties of the layers formed on the surface of cp-titanium were studied. The mode of the electron-beam alloying of titanium with zirconium and tantalum, which ensured the formation of a defect-free layer with a high content of alloying elements was selected. Metallographic examination indicated the presence of a dendritic- and plate-type structure of cladded layers. The microhardness of the layers, formed at the optimum mode, was not changed in the cross section and was equal to 450 HV.

[Correlation between degree of conversion, microhardness and inorganic content in composites].

PubMed

Neves, Alisson Discacciati; Discacciati, José Augusto César; Orêfice, Rodrigo Lambert; Jansen, Wellington Corrêa

2002-01-01

The purpose of this study was to evaluate the correlation between degree of conversion and microhardness in dental composites, as well as the effect of the inorganic content and type of photo-curing unit on these parameters. Three indirect composites (Artglass, Solidex and Zeta LC) were polymerized by means of three different laboratorial units (UniXS, Solidilite and an experimental device). For each material, fifteen samples were prepared using a metal matrix. The degree of conversion was analyzed by means of infrared spectroscopy, and microhardness was also assessed. The inorganic content was measured by means of thermogravimetric analysis (TGA). The Pearson s test was carried out in order to determine correlations. The degree of conversion of Artglass ranged from 37.5% to 79.2%, and its microhardness, from 32.4 to 50.3 (r = 0.904). The degree of conversion of Solidex ranged from 41.2% to 60.4%, and its microhardness, from 33.3 to 44.1 (r = 0.707). The degree of conversion and the microhardness of Zeta LC ranged from 62.0% to 78.0% and from 22.6 to 33.6, respectively (r = 0.710). It was concluded that the utilization of different photo-curing units caused variations on the degree of conversion, as a result of specific characteristics of each unit. For each material, there was strong correlation between the degree of conversion and microhardness. In addition, when different materials were compared, microhardness was more affected by filler content than by the degree of conversion.

In-vitro study investigating influence of toothpaste containing green tea extract on the microhardness of demineralized human enamel

NASA Astrophysics Data System (ADS)

Febrian, K.; Triaminingsih, S.; Indrani, DJ

2017-08-01

The aim of this study was to analyze the influence of toothpaste containing green tea extract on the microhardness of demineralized enamel. Human tooth, which was demineralised in citric acid solution, had a toothpaste containing green tea extract of concentration of 5, 10 or 15% application. Microhardness measurement was carried out on each enamel surface of the teeth for initial, after the demineralization and after application of the tooth pastes. It showed that there was significant decrease between enamel microhardness of the teeth at the initial condition and after demineralization. After application of the toothpaste containing green tea extract of each concentration the microhardnss increased significantly. However, there the microhardness was insignificant between the applications of each green tea concentration.

Evaluation of a 6% hydrogen peroxide tooth whitening gel on enamel and dentine microhardness in vitro.

PubMed

Joiner, Andrew; Thakker, Gopal; Cooper, Yvonne

2004-01-01

The aims of this study were to evaluate the effects of a novel 6% hydrogen peroxide containing tooth whitener, Xtra White (XW), on enamel and dentine microhardness in vitro. Polished human enamel and dentine specimens were prepared and baseline microhardness determined. In study 1, enamel specimens were exposed to 20 min cycles of either water, XW or Sprite Light for up to 28 cycles. In studies 2 and 3, enamel specimens were treated with 20 min cycles of either XW or water and exposed to whole saliva at all other times. In study 3, an additional exposure to a fluoride containing toothpaste was conducted. In total, 28 treatments were conducted in order to simulate a 2 weeks product use. In study 4, dentine specimens were treated as per study 3. Final microhardness measurements were taken and for studies 3 and 4 colour measurements were additionally taken. XW and water gave no statistically significant (p>0.05) changes in enamel and dentine microhardness after 28 treatments. Sprite Light gave a significant (p<0.00002) reduction in enamel microhardness after one 20 min treatment. XW showed significant bleaching of enamel and dentine specimens as compared to the water control. XW does not have any significant effect on enamel and dentine microhardness.

The effect of 10% carbamide peroxide bleaching material on microhardness of sound and demineralized enamel and dentin in situ.

PubMed

Basting, R T; Rodrigues Júnior, A L; Serra, M C

2001-01-01

This in situ study evaluated the microhardness of sound and demineralized enamel and dentin submitted to treatment with 10% carbamide peroxide for three weeks. A 10% carbamide peroxide bleaching agent--Opalescence/Ultradent (OPA)--was evaluated against a placebo agent (PLA). Two hundred and forty dental fragments--60 sound enamel fragments (SE), 60 demineralized enamel fragments (DE), 60 sound dentin fragments (SD) and 60 demineralized dentin fragments (DD)--were randomly fixed on the vestibular surface of the first superior molars and second superior premolars of 30 volunteers. The volunteers were divided into two groups that received bleaching or the placebo agent at different sequences and periods at a double blind 2 x 2 crossover study with a wash-out period of two weeks. Microhardness tests were performed on the enamel and dentin surface. The SE and DE submitted to treatment with OPA showed lower microhardness values than the SE and DE submitted to treatment with PLA. There were no statistical differences in microhardness values for SD and DD submitted to the treatment with OPA and PLA. The results suggest that treatment with 10% carbamide peroxide bleaching material for three weeks alters the enamel microhardness, although it does not seem to alter the dentin microhardness.

The effect of EDTA, EGTA, EDTAC, and tetracycline-HCl with and without subsequent NaOCl treatment on the microhardness of root canal dentin.

PubMed

Sayin, Taner Cem; Serper, Ahmet; Cehreli, Zafer C; Otlu, Harika G

2007-09-01

The purpose of this study was to evaluate the effect of single and combined use of ethylenediamine tetra acetic acid (EDTA), ethylene glycol bis [b-aminoethylether] N,N,N',N'-tetraacetic acid (EGTA), EDTA plus Cetavlon (EDTAC), tetracycline-HCl, and NaOCl on the microhardness of root canal dentin. The crowns of 30 single-rooted human teeth were discarded at the cementoenamel junction and the roots were bisected longitudinally to obtain root halves (N = 60). The specimens were embedded in autopolymerizing acrylic resin, leaving the root canal dentin exposed. Dentin surfaces were prepared for microhardness test by grinding and polishing. The reference microhardness values of untreated specimens were recorded using a Vicker's microhardness tester at the apical, midroot, and cervical levels of the root canal. Thereafter, the specimens treated with single (test solution only) or combined (test solution, followed by 2.5% NaOCl) versions of the irrigants for 5 minutes. Posttreatment microhardness values were obtained as with initial ones. Statistical comparisons between the test groups and among single and combined treatments were carried out using 2-way ANOVA with repeated measures (P =.05). Comparisons within each group with respect to application regions were made with Friedman's nonparametric 2-way analysis of variance at the same level of significance. All treatment regimens except distilled water significantly decreased the microhardness of the root canal dentin (P < . 05). The single and combined use of EDTA decreased the microhardness of the root canal dentin significantly more than all other treatment regimens (P < .05). Compared with their single-treatment versions, all combined treatment regimens decreased the mean microhardness values significantly (P < .05). A comparison of single and combined treatment regimens revealed significant decreases only for EDTA and EDTA + NaOCl in the coronal region and for EDTAC and EDTAC + NaOCl in the apical and middle regions of the root canal (P < .05). The use of EDTA alone or prior to NaOCl resulted in the maximum decrease in dentin microhardness. The softening effect of subsequent NaOCl treatment was both material and region dependent. However, for combined treatment regimens, subsequent use of NaOCl levels the statistical differences between the regional microhardness values obtained after treatment with EGTA, EDTAC, and tetracycline-HCl.

The effect of McInnes solution on enamel and the effect of Tooth mousse on bleached enamel: An in vitro study

PubMed Central

Darshan, H E; Shashikiran, N D

2008-01-01

Aims: To evaluate the effect of McInnes bleaching agent on the micro hardness of enamel before and after bleaching and to evaluate the effect of G C Tooth Mousse on the bleached enamel surface for its microhardness. Materials and Methods: McInnes bleaching solution, Casein phosphopeptide-amorphous calcium phosphate CCP-ACP (G C Tooth mousse) artificial saliva (Dept of Oral Pathology, College of Dental Sciences, Davengere), deionized water, Vickers Micro Hardness tester (Zwick/ZHV, Germany), freshly extracted teeth, cold cure acrylic, Diamond disc (Horico - PFINGST New jersey USA, KAVO- Germany), straight handpiece (kavo peca reta) and plastic moulds (6.5 × 2 mm). The purpose of this study was to evaluate and compare microhardness of the sound enamel surface by Vickers Hardness Number before and after bleaching with McInnes solution, and to evaluate the effect of casein phosphopeptide amorphous calcium phosphate (G C Tooth Mousse) on the bleached enamel surface for its microhardness. Statistical analysis: The data obtained from the test were subjected for statistical analysis and are presented as range, mean and standard deviation. P value of 0.05 or less was considered for statistical significance. The changes in microhardness at different times of assessment were analyzed using the paired ‘t’ test Results: All the samples showed decrease in the microhardness after two cycles of bleaching, though immediately after bleaching the decrease in the microhardness was not significant (P = 0.34). However, after the second cycles, it showed a significant decrease (P<0.01) in the microhardness. After application of remineralization solution (GC Tooth mousse), the samples showed a marginal increase in the microhardness (P<0.05) after seven days and a marked increase after fourteen days (P<0.001). Conclusion: McInnes bleaching agent does decrease the microhardness of enamel by causing enamel demineralization and GC Tooth mousse used in the study causes an increase in the microhardness of bleached enamel by maintaining a high gradient of calcium and phosphate ions at the enamel subsurface. PMID:20142891

Investigation of structure and mechanical properties of plasma vapor deposited nanocomposite TiBN films

NASA Astrophysics Data System (ADS)

Han, Bin; Neena, D.; Wang, Zesong; Kondamareddy, K. k.; Li, Na; Zuo, Wenbin; Yan, Shaojian; Liu, Chuansheng; Fu, Dejun

2017-04-01

TiBN coatings have huge potential applications as they have excellent properties with increasing modern industrial requirements. Nanocomposite TiBN coatings were synthesized on cemented carbide, high speed steel and Si substrates by using cathodic arc plasma ion plating from pure TiB2 ceramic targets. The structure and mechanical properties of the TiBN coatings were significantly influenced by the nitrogen partial pressure. Rutherford backscattering spectrometry demonstrates that the nitrogen content of the coating varied from 2.8% to 34.5% and high-resolution electron microscopy images reveal that all coatings have the characteristic of nanocrystals embedded in an amorphous matrix. The root-mean-square roughness of the coatings increases from 3.73 to 14.64 nm and the coefficients of friction of the coatings at room temperature vary from 0.54 to 0.73 with increasing nitrogen partial pressure. The microhardness of the coating increases up to 35.7 GPa at 10 sccm N2 flow rate. The smallest wear rate is 2.65 × 10-15 m3 N-1 m-1 which indicates that TiBN coatings have excellent wear resistance. The adhesion test revealed that the TiBN coatings have good adhesion at low nitrogen partial pressure.

The effect of heat treatment on microstructure evolution in artificially aged carbon nanotube/Al2024 composites synthesized by mechanical alloying

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pérez-Bustamante, R.

Although carbon nanotubes/aluminum (CNT/Al) composites are promising materials in the production of structural components, their mechanical behavior under overaging conditions has not been considered. In this paper the effect of CNTs on the microstructural and mechanical behavior of a 2024 aluminum alloy (Al2024) synthesized by mechanical alloying (MA) and powder metallurgy routes is discussed, as well as the effect of aging heat treatments at different temperatures and aging times. The mechanical behavior of composites was screened by hardness measurements as function of aging time. After 96 h of aging time, composites showed mechanical stability in their hardness performance. Images frommore » transmission electron microscopy showed that the mechanical stability of composites was due to a homogeneous dispersion of CNTs in the aluminum matrix and a subsequent alteration in the kinetics of precipitation is due to their presence in the aluminum matrix. Even though strengthening precipitation took place during aging, this was not the main strengthening mechanism observed in composites. - Highlights: • Dispersion of carbon nanotubes during mechanical alloying • Microstructural evolution observed by HRTEM. • Mechanical performance evaluated through micro-hardness test. • Increased mechanical performance at high working temperatures • Acceleration of kinetics of precipitation due to CNTs, and milling conditions.« less

Evaluating the Properties of Dissimilar Metal Welding Between Inconel 625 and 316L Stainless Steel by Applying Different Welding Methods and Consumables

NASA Astrophysics Data System (ADS)

Kourdani, Ahmad; Derakhshandeh-Haghighi, Reza

2018-04-01

The current work was carried out to characterize welding of Inconel 625 superalloy and 316L stainless steel. In the present study, shielded metal arc welding (SMAW) and gas tungsten arc welding (GTAW) with two types of filler metals (ERNiCrMo-3 and ERSS316L) and an electrode (ENiCrMo-3) were utilized. This paper describes the selection of the proper welding method and welding consumables in dissimilar metal joining. During solidification of ERNiCrMo-3 filler metal, Nb and Mo leave dendritic cores and are rejected to inter-dendritic regions. However, ERSS316L filler metal has small amounts of elements with a high tendency for segregation. So, occurrence of constitutional super-cooling for changing the solidification mode from cellular to dendritic or equiaxed is less probable. Using GTAW with lower heat input results in higher cooling rate and finer microstructure and less Nb segregation. The interface between weld metal and base metal and also unmixed zones was evaluated by scanning electron microscopy and energy dispersive X-ray (EDX) analysis. Microhardness measurements, tensile test, and Charpy impact test were performed to see the effect of these parameters on mechanical properties of the joints.

Effect of ethanol-wet bonding with hydrophobic adhesive on caries-affected dentine.

PubMed

Huang, Xueqing; Li, Li; Huang, Cui; Du, Xijin

2011-08-01

Frequently encountered in clinical practice, caries-affected dentine (CAD) is the most challenging bonding substrate. This study evaluated the effect of ethanol-wet bonding with hydrophobic adhesive to sound dentine and to CAD. In the control groups, prepared sound dentine and CAD were bonded with Adper Single Bond 2 using a traditional water-wet bonding technique. In the experimental groups, the specimens were treated as follows: Group 1, rinsed with stepwise ethanol dehydration; Group 2, immersion in 100% ethanol, three times, for 20 s each time; and Group 3, immersion in 100% ethanol for 20 s. Microtensile bond strength (μTBS) testing was used to evaluate the effects of the different protocols on bonding. The microhardness of debonded dentine surfaces was measured to ensure the presence of CAD. Interfacial nanoleakage was evaluated by field-emission scanning electron microscopy. Treatment significantly improved the μTBS in CAD in Groups 1 and 2, but had no effect on Group 3. Conversely, treatment significantly reduced the μTBS in sound dentine in Groups 2 and 3, but had no effect in Group 1. The presence of nanoleakage varied with the ethanol-wet protocol used. In conclusion, ethanol-wet bonding can potentially improve bond efficacy to CAD when an appropriate protocol is used. © 2011 Eur J Oral Sci.

Synthesis of Ti-6Al-4V alloy with nano-TiN microstructure via spark plasma sintering technique

NASA Astrophysics Data System (ADS)

E Falodun, O.; Obadele, B. A.; Oke, S. R.; E Maja, M.; Olubambi, P. A.

2017-12-01

The effect of nano-TiN dispersion strengthened Ti-6Al-4V via spark plasma sintering method has been investigated. Ti-6Al-4V with 4 vol. percent of nano-TiN were mixed in a Turbula shaker mixer for 8 h at a speed of 49 rpm and the admixed powders were sintered at sintering temperature range of 1000 - 1100 °C, holding time of 10-30 mins, heating rate of 100 °C/min under an applied pressure of 50 MPa. The morphology of the as-received and sintered compacts was examined by scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS) and phase analysis was done by X-ray diffractometry (XRD). The sintered compacts without nano-TiN reveal lamellar structure while reinforced Ti-6Al-4V with nano-TiN shows a bimodal structure and titanium nitride has a great influence on a grain growth at high temperature. Furthermore, the microstructural formation mechanism was investigated. With the addition of the content of Ti-6Al-4V with 4 vol.% of nano-TiN, the micro-hardness also improved and this was due to homogenous distribution of TiN in Ti-6Al-4V matrix.

Contribution of Lattice Distortion to Solid Solution Strengthening in a Series of Refractory High Entropy Alloys

NASA Astrophysics Data System (ADS)

Chen, H.; Kauffmann, A.; Laube, S.; Choi, I.-C.; Schwaiger, R.; Huang, Y.; Lichtenberg, K.; Müller, F.; Gorr, B.; Christ, H.-J.; Heilmaier, M.

2018-03-01

We present an experimental approach for revealing the impact of lattice distortion on solid solution strengthening in a series of body-centered-cubic (bcc) Al-containing, refractory high entropy alloys (HEAs) from the Nb-Mo-Cr-Ti-Al system. By systematically varying the Nb and Cr content, a wide range of atomic size difference as a common measure for the lattice distortion was obtained. Single-phase, bcc solid solutions were achieved by arc melting and homogenization as well as verified by means of scanning electron microscopy and X-ray diffraction. The atomic radii of the alloying elements for determination of atomic size difference were recalculated on the basis of the mean atomic radii in and the chemical compositions of the solid solutions. Microhardness (μH) at room temperature correlates well with the deduced atomic size difference. Nevertheless, the mechanisms of microscopic slip lead to pronounced temperature dependence of mechanical strength. In order to account for this particular feature, we present a combined approach, using μH, nanoindentation, and compression tests. The athermal proportion to the yield stress of the investigated equimolar alloys is revealed. These parameters support the universality of this aforementioned correlation. Hence, the pertinence of lattice distortion for solid solution strengthening in bcc HEAs is proven.

Roman mystery iron blades from Serbia

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balos, Sebastian; Benscoter, Arlan; Pense, Alan

A First to Forth Century Roman spear blade from Serbia was found to have an unusual microstructure inconsistent with typical Roman Period iron. An analysis of the blade undertaken at Lehigh University in the US and at the Faculty of Technical Sciences in Novi Sad, Serbia established that it was metallic in appearance, magnetic and had an external layer of red rust. But as metallographically polished, it appeared to contain multiple internal phases and internal cracking. Even after aggressive etching, no typical low carbon microstructure was developed. Scanning electron microscopy, classical and energy dispersive X-ray analysis indicated that the specimenmore » was essentially iron, although its microhardness was too high for typical Roman iron. It was then dubbed 'Mystery Iron.' Analysis of all the data led to the proposal that it was essentially a Roman iron 'fossil' in which the iron had been converted to high temperature iron oxide while retaining the form of the blade, conversion probably occurring in a fire. Subsequent X-ray diffraction analysis confirmed that the blade consisted of FeO and Fe{sub 3}O{sub 4} and the mystery of the iron fossil was at least partially solved. A hypothesis is proposed regarding a potential cause for the fire.« less

Effect of nano-SiO{sub 2} particles and curing time on development of fiber-matrix bond properties and microstructure of ultra-high strength concrete

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Zemei; Department of Civil, Architectural and Environmental Engineering, Missouri University of Science and Technology, Rolla 65409, MO; Khayat, Kamal Henri, E-mail: khayatk@mst.edu

Bond properties between fibers and cementitious matrix have significant effect on the mechanical behavior of composite materials. In this study, the development of steel fiber-matrix interfacial bond properties in ultra-high strength concrete (UHSC) proportioned with nano-SiO{sub 2} varying between 0 and 2%, by mass of cementitious materials, was investigated. A statistical model relating either bond strength or pullout energy to curing time and nano-SiO{sub 2} content was proposed by using the response surface methodology. Mercury intrusion porosimetry (MIP) and backscatter scanning electron microscopy (BSEM) were used to characterize the microstructure of the matrix and the fiber-matrix interface, respectively. Micro-hardness aroundmore » the embedded fiber and hydration products of the matrix were evaluated as well. Test results indicated that the optimal nano-SiO{sub 2} dosage was 1% in terms of the bond properties and the microstructure. The proposed quadratic model efficiently predicted the bond strength and pullout energy with consideration of curing time and nano-SiO{sub 2} content. The improvement in bond properties associated with nano-silica was correlated with denser matrix and/or interface and stronger bond and greater strength of hydration products based on microstructural analysis.« less

The Wear Behavior of HVOF Sprayed Near-Nanostructured WC-17%Ni(80/20)Cr Coatings in Dry and Slurry Wear Conditions

NASA Astrophysics Data System (ADS)

Ben Mahmud, Tarek A.; Atieh, Anas M.; Khan, Tahir I.

2017-07-01

The ability to deposit nanostructured feedstock by using high-velocity oxygen-fuel (HVOF) spray offers potential improvements in coating hardness, wear resistance and toughness for applications in the oil sands industry. In this study, the wear behavior of a near-nanostructured coating was compared under dry and slurry abrasive wear test using an uncoated AISI-1018 low-carbon steel substrate as a reference. The coating microstructures were analyzed in the as-sprayed, dry and slurry test conditions using scanning electron microscopy, x-ray diffraction and microhardness measurements. Wear behavior of the steel and coating surfaces were assessed using a pin-on-plate wear test under various loads. The results showed that a coating could be successfully deposited using the HVOF spraying technique and with retention of the near-nanosized WC dispersion within the coating structure. The wear rate under dry test conditions was greater for the steel and coating compared to tests performed under slurry conditions. Examination of the wear tracks revealed that the wear mechanism was different for the two test conditions. Wear in the dry test condition resulted from 2-body abrasion, while 3-body abrasion dominated wear in slurry conditions. The latter showed lower wear rates due to a lubricating effect of the oil.

Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly

PubMed Central

Lu, Xiaoli; Xia, Yang; Liu, Mei; Qian, Yunzhu; Zhou, Xuefeng; Gu, Ning; Zhang, Feimin

2012-01-01

To fabricate high-strength diatomite-based ceramics for dental applications, the layer-by-layer technique was used to coat diatomite particles with cationic [poly(allylamine hydrochloride)] and anionic [poly(sodium 4-styrenesulfonate)] polymers to improve the dispersion and adsorption of positively charged nano-ZrO2 (zirconia) as a reinforcing agent. The modified diatomite particles had reduced particle size, narrower size distribution, and were well dispersed, with good adsorption of nano-ZrO2. To determine the optimum addition levels for nano-ZrO2, ceramics containing 0, 20, 25, 30, and 35 wt% nano-ZrO2 were sintered and characterized by the three-point bending test and microhardness test. In addition to scanning electron microscopy, propagation phase-contrast synchrotron X-ray microtomography was used to examine the internal structure of the ceramics. The addition of 30 wt% nano-ZrO2 resulted in the highest flexural strength and fracture toughness with reduced porosity. Shear bond strength between the core and veneer of our diatomite ceramics and the most widely used dental ceramics were compared; the shear bond strength value for the diatomite-based ceramics was found to be significantly higher than for other groups (P < 0.05). Our results show that diatomite-based nanocomposite ceramics are good potential candidates for ceramic-based dental materials. PMID:22619551

Influence of Sintering Temperature on Mechanical and Physical properties of Mill Scale based Bipolar Plates for PEMFC

NASA Astrophysics Data System (ADS)

Khaerudini, Deni S.; Berliana, Rina; Prakoso, Gatra B.; Insiyanda, Dita R.; Alva, Sagir

2018-03-01

This work concerns the utilization of mill scale, a by-product of iron and steel formed during the hot rolling of steel, as a potential material for use as bipolar plates in proton exchange membrane fuel cells (PEMFCs). On the other hand, mill scale is considered a very rich in iron source having characteristic required such as for current collector in bipolar plate and would significantly contribute to lower the overall cost of PEMFC based fuel cell systems. In this study, the iron reach source of mill scale powder, after sieving of 150 mesh, was mechanically alloyed with the aluminium source containing 30 wt.% using a shaker mill for 3 h. The mixed powders were then pressed at 300 MPa and sintered at various temperatures of 400, 450 and 500 °C for 1 h under inert gas atmosphere. The structural changes of powder particles during mechanical alloying and after sintering were studied by x-ray diffractometry, scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy (EDX), microhardness measurement, and density - porosity analysis. The details of the performance variation of three different sintering conditions can be preliminary explained by the metallographic and crystallographic structure and phase analysis as well as sufficient mechanical strength of the sintered materials was presented in this report.

Microstructure and Dry Sliding Wear Resistance of Laser Cladding Ti-Al-Si Composite Coating

NASA Astrophysics Data System (ADS)

Zhang, H. X.; Yu, H. J.; Chen, C. Z.; Dai, J. J.

In order to improve the wear resistance of Ti alloys, different mass ratios of Ti-Si-Al powders were designed to fabricate hard phases reinforced intermetallic matrix composite coatings on the Ti-6Al-4V substrate by laser cladding. The corresponding coatings were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectrometer (EDS) and high resolution transmission microscopy (HRTEM). The HV-1000 hardness tester and MM200 wear test machine were employed to test the hardness and the wear resistance of the composite coatings, respectively. The composite coatings mainly consisted of the reinforcements of Ti5Si3, Ti3AlC2 and Ti7Al5Si12 and the matrix of Ti3Al, TiAl, TiAl3 and α-Ti. The micro-hardness of the Ti-35Al-15Si coating was from 956 HV0.2 to 1130 HV0.2, which was approximately 3-4 times of the substrate and the highest in the three samples. The wear rate of the Ti-35Al-15Si coating was 0.023cm3ṡmin-1, which was about 1/4 of the Ti-6Al-4V substrate. It was the lowest in the three samples.

Microstructural evolution and wear behaviors of laser cladding Ti2Ni/α(Ti) dual-phase coating reinforced by TiB and TiC

NASA Astrophysics Data System (ADS)

Song, R.; Li, J.; Shao, J. Z.; Bai, L. L.; Chen, J. L.; Qu, C. C.

2015-11-01

The Ti2Ni/α(Ti) dual-phase coating reinforced by TiB and TiC was fabricated on the Ti6Al4V substrate by laser cladding. Phase constituents were confirmed by a theoretical prediction combined with X-ray diffraction (XRD) analyses. From the surface to the bottom of the coating, a regular evolution of the reinforcements' microstructure, namely TiCp+(TiB+TiC)e, (TiB+TiC)e and TiBp+(TiB+TiC)e (p and e were the abbreviations of primary and eutectic, respectively), was investigated by scanning electron microscopy (SEM). The coating possessed the higher microhardness than that of the substrate. An in situ dynamic method (in situ continuing tests at different time intervals) was designed to reveal wear behaviors at different wear stages. A quantitative calculation formula was established by a mathematic model to predict wear losses under different sliding time and applied loads in a definite precision. The wear mechanism was transformed from brittle debonding (at 10 N) to the joint action of brittle debonding and micro-cutting (at 20 N and 30 N) due to the microstructural evolution across the depth from the surface of the coating.

Electrophoretic Deposition of Cu-SiO2 Coatings by DC and Pulsed DC for Enhanced Surface-Mechanical Properties

NASA Astrophysics Data System (ADS)

Maharana, H. S.; Lakra, Suprabha; Pal, S.; Basu, A.

2016-01-01

The present study explored the possibilities of improvement in the surface-mechanical properties of electrodeposited Cu-SiO2 composite coating and its underlying mechanism. Composite coatings were developed using SiO2-dispersed acidic copper sulfate electrolyte by direct current and pulse-current electro-codeposition techniques with variation of pulse frequencies at a fixed duty cycle. X-ray diffraction analysis of the coatings revealed information regarding the presence of various phases and crystallographic orientations of the deposited Cu matrix. Scanning electron microscopy and energy dispersive x-ray spectroscopy techniques were used to investigate the surface morphology and chemical composition of the coatings, respectively, and it was observed that SiO2 particles were uniformly distributed in the composite coatings. Surface roughness was found to be reduced with the increasing pulse frequency. The Vickers microhardness and ball-on-plate wear study showed improvement in surface-mechanical properties due to the formation of fine Cu matrix, dispersion strengthening due to homogeneously distributed SiO2 particles, and the preferred orientation of the Cu matrix. Marginal decrease in electrical conductivity with the increasing SiO2 content and pulse frequency was observed from the four-probe electrical conductivity measurement technique.

Improved performance of diatomite-based dental nanocomposite ceramics using layer-by-layer assembly.

PubMed

Lu, Xiaoli; Xia, Yang; Liu, Mei; Qian, Yunzhu; Zhou, Xuefeng; Gu, Ning; Zhang, Feimin

2012-01-01

To fabricate high-strength diatomite-based ceramics for dental applications, the layer-by-layer technique was used to coat diatomite particles with cationic [poly(allylamine hydrochloride)] and anionic [poly(sodium 4-styrenesulfonate)] polymers to improve the dispersion and adsorption of positively charged nano-ZrO(2) (zirconia) as a reinforcing agent. The modified diatomite particles had reduced particle size, narrower size distribution, and were well dispersed, with good adsorption of nano-ZrO(2). To determine the optimum addition levels for nano-ZrO(2), ceramics containing 0, 20, 25, 30, and 35 wt% nano-ZrO(2) were sintered and characterized by the three-point bending test and microhardness test. In addition to scanning electron microscopy, propagation phase-contrast synchrotron X-ray microtomography was used to examine the internal structure of the ceramics. The addition of 30 wt% nano-ZrO(2) resulted in the highest flexural strength and fracture toughness with reduced porosity. Shear bond strength between the core and veneer of our diatomite ceramics and the most widely used dental ceramics were compared; the shear bond strength value for the diatomite-based ceramics was found to be significantly higher than for other groups (P < 0.05). Our results show that diatomite-based nanocomposite ceramics are good potential candidates for ceramic-based dental materials.

Influence of dust and mud on the optical, chemical, and mechanical properties of a pv protective glass

PubMed Central

Yilbas, Bekir Sami.; Ali, Haider; Khaled, Mazen M.; Al-Aqeeli, Nasser; Abu-Dheir, Numan; Varanasi, Kripa K.

2015-01-01

Recent developments in climate change have increased the frequency of dust storms in the Middle East. Dust storms significantly influence the performances of solar energy harvesting systems, particularly (photovoltaic) PV systems. The characteristics of the dust and the mud formed from this dust are examined using various analytical tools, including optical, scanning electron, and atomic force microscopies, X-ray diffraction, energy spectroscopy, and Fourier transform infrared spectroscopy. The adhesion, cohesion and frictional forces present during the removal of dry mud from the glass surface are determined using a microtribometer. Alkali and alkaline earth metal compounds in the dust dissolve in water to form a chemically active solution at the glass surface. This solution modifies the texture of the glass surface, thereby increasing the microhardness and decreasing the transmittance of the incident optical radiation. The force required to remove the dry mud from the glass surface is high due to the cohesive forces that result from the dried mud solution at the interface between the mud and the glass. The ability altering the characteristics of the glass surface could address the dust/mud-related limitations of protective surfaces and has implications for efficiency enhancements in solar energy systems. PMID:26514102

Analysis of the properties of dental cements after exposure to incubation media containing Streptococcus mutans.

PubMed

de Menezes, Fernando Carlos Hueb; Junior, Geraldo Thedei; de Oliveira, Wildomar Jose; Paulino, Tony de Paiva; de Moura, Marcelo Boaventura; da Silva, Igor Lima; de Moura, Marcos Boaventura

2011-09-01

Indirect restorations are increasingly used in dentistry, and the cementation interface is possibly the most critical region of the work. The objective of the present work was to evaluate the influence of exposure to a culture medium containing S. mutans on the hardness and solubility of four different cementing agents (zinc phosphate, glass ionomer, glass ionomer modified with resin and resin cement). Test specimens composed of these cements were exposed for 30 days in a culture medium containing S. mutans. After leaching, the test materials were assessed in terms of their solubility (loss of mass) and Knoop (KHN) microhardness. Changes in surface morphology were identified using scanning electron microscopy (SEM). The resin cement showed no significant solubility and its hardness increased following exposure and leaching, while the zinc phosphate cement was the most soluble and its hardness decreased after exposure to the culture medium. SEM analyses identified morphological alterations on the surfaces of the test materials that were compatible with the solubility results. It is concluded that resinous cements perform better than water-based cements when exposed to acidic conditions. The effects of acids from Streptococcus mutans can interfere with the efficiency and properties of some cements used for fixation of indirect restorations, exposed to the buccal environment.

Cryomilled and spark plasma sintered titanium: the evolution of microstructure

NASA Astrophysics Data System (ADS)

Kozlík, Jiří; Becker, Hanka; Harcuba, Petr; Stráský, Josef; Janeček, Milos

2017-05-01

Bulk ultra-fine grained (UFG) commercially pure Ti was prepared by cryogenic milling in liquid argon and subsequent spark plasma sintering (SPS). During cryogenic milling, individual powder particles are repetitively severely deformed by attrition forces. Powder particles were not significantly refined, but due to severe repetitive plastic deformation, ultra-fine grained microstructure emerges within each powder particle. Cryogenic milling can be therefore considered as a specific severe plastic deformation (SPD) method. Compactization of cryomilled powder by SPS technique (also referred to as field assisted sintering technique - FAST) requires significantly lower sintering temperatures and shorter sintering times for successful compaction when compared to any other sintering technique. This is crucial for maintaining the UFG microstructure due to its limited thermal stability. Several specimens were prepared by varying processing parameters, in particular the sintering temperature. The microstructure of powders and compacted samples was observed by scanning electron microscopy (SEM). Increased sintering temperature results in recrystallization and grain growth. A trade-off relationship between the density of compacted material and grain size was identified. Microhardness of the material was found to depend on residual porosity rather than grain size. This contribution presents cryogenic milling and spark plasma sintering as a viable alternative for achieving UFG microstructure in commercially pure Ti.

Effect of tetracalcium phosphate/monetite toothpaste on dentin remineralization and tubule occlusion in vitro.

PubMed

Medvecky, L; Stulajterova, R; Giretova, M; Mincik, J; Vojtko, M; Balko, J; Briancin, J

2018-03-01

To investigate the tubule occlusion and remineralization potential of a novel toothpaste with active tetracalcium phosphate/monetite mixtures under de/remineralization cycling. Dentin de/remineralization cycling protocol consisted of demineralization in 1% citric acid at pH 4.6 with following remineralization with toothpastes and soaking in artificial saliva. Effectiveness of toothpastes to promote remineralization was evaluated by measurement of microhardness recovery, analysis of surface roughness, thickness of coating and scanning electron microscopy. The novel tetracalcium phosphate/monetite dentifrice had comparable remineralization potential as commercial calcium silicate/phosphate (SENSODYNE ® ) and magnesium aluminum silicate (Colgate ® ) toothpastes and significantly higher than control saliva (p<0.02). Surface roughness was significantly lower after treatment with prepared and SENSODYNE ® dentifirice (p<0.05). The coatings on dentin surfaces was significantly thicker after applying toothpastes as compared to negative control (p<0.001). The new fluoride toothpaste formulation with bioactive tetracalcium phosphate/monetite calcium phosphate mixture effectively occluded dentin tubules and showed good dentin remineralization potential under de/remineralization cycling. It could replace professional powder preparation based on this mixture. It was demonstrated that prepared dentifrice had comparable properties with commercial fluoride calcium silicate/phosphate or magnesium aluminum silicate dentifrices. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel

NASA Astrophysics Data System (ADS)

Durmaz, M.; Kilinc, B.; Abakay, E.; Sen, U.; Sen, S.

2015-03-01

In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layer formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr2N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV0.025. For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results.

Wear and Corrosion Properties of 316L-SiC Composite Coating Deposited by Cold Spray on Magnesium Alloy

NASA Astrophysics Data System (ADS)

Chen, Jie; Ma, Bing; Liu, Guang; Song, Hui; Wu, Jinming; Cui, Lang; Zheng, Ziyun

2017-08-01

In order to improve the wear and corrosion resistance of commonly used magnesium alloys, 316L stainless steel coating and 316L-SiC composite coating have been deposited directly on commercial AZ80 magnesium alloy using cold spraying technology (CS). The microstructure, hardness and bonding strength of as-sprayed coatings were studied. Their tribological properties sliding against Si3N4 and GCr15 steel under unlubricated conditions were evaluated by a ball-on-disk tribometer. Corrosion behaviors of coated samples were also evaluated and compared to that of uncoated magnesium alloy substrate in 3.5 wt.% NaCl solution by electrochemical measurements. Scanning electron microscopy was used to characterize the corresponding wear tracks and corroded surfaces to determine wear and corrosion mechanisms. The results showed that the as-sprayed coatings possessed higher microhardness and more excellent wear resistance than magnesium alloy substrate. Meanwhile, 316L and 316L-SiC coating also reduced the corrosion current density of magnesium alloy and the galvanic corrosion of the substrates was not observed after 200-h neutral salt spray exposure, which demonstrated that corrosion resistance of a magnesium alloy substrate could be greatly improved by cold-sprayed stainless steel-based coatings.

Mechanical and corrosive behavior of Ti/TiN multilayer films with different modulation periods

NASA Astrophysics Data System (ADS)

Zhang, Q.; Leng, Y. X.; Qi, F.; Tao, T.; Huang, N.

2007-04-01

Ti/TiN multilayer films with different periods Λ (Λ = λTiN + λTi) were synthesized on 17-4PH stainless steel and silicon wafer using unbalanced magnetron sputtering. The microstructure of the films was characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The mechanical properties such as hardness, sliding wear behavior and adhesion were analyzed by means of micro-hardness, ball-on-disc and scratch tests. The anodic polarization characteristics were measured in a 3% NaCl solution at room temperature to examine the corrosion resistance. Moreover, the corrosion resistance in a 350 °C water vapor ambience also was analyzed. XRD revealed a gradual TiNx transition layer between Ti and TiN. The SEM results confirmed the periodicity of the Ti/TiN multilayer films. The hardness and wear resistance of the Ti/TiN multilayer films increased with decrease of the modulation period. The adhesion strength between Ti/TiN multilayer films and 17-4PH substrate was improved with proper modulation period. The Ti/TiN multilayer films can for a corrosion protective coating on 17-4PH stainless steel in 3% NaCl solution, however the corrosion resistance at 350 °C vapor ambience decreased for the period Λ below 200 nm.

Nanocomposite SAC Solders: The Effect of Adding Ni and Ni-Sn Nanoparticles on Morphology and Mechanical Properties of Sn-3.0Ag-0.5Cu Solders

NASA Astrophysics Data System (ADS)

Yakymovych, A.; Švec, P.; Orovcik, L.; Bajana, O.; Ipser, H.

2018-01-01

This study investigates the effect of minor additions of Ni, Ni3Sn or Ni3Sn2 nanoparticles on the microstructure and mechanical properties of Cu/solder/Cu joints. The nanocomposite Sn-3.0Ag-0.5Cu (SAC305) solders with 0.5, 1.0 and 2.0 wt.% metallic nanoparticles were prepared through a paste mixing method. The employed Ni and Ni-Sn nanoparticles were produced via a chemical reduction method. The microstructure of as-solidified Cu/solder/Cu joints was studied by x-ray diffraction and scanning electron microscopy. The results showed that additions of Ni and Ni-Sn nanoparticles to the SAC305 solder paste lead initially to a decrease in the average thickness of the intermetallic compound layer in the interface between solder and substrate, while further additions up to 2.0 wt.% did not induce any significant changes. In addition, shear strength and microhardness tests were performed to investigate the relationship between microstructure and mechanical properties of the investigated solder joints. The results indicated an increase in both of these properties which was most significant for the solder joints using SAC305 with 0.5 wt.% Ni or Ni-Sn nanoparticles.

Tribological properties of CrN coatings deposited by nitro-chromizing treatment on AISI D2 steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Durmaz, M., E-mail: mdurmaz@sakarya.edu.tr; Abakay, E.; Sen, U.

2015-03-30

In this work, the wear test of uncoated and chromium nitride coated AISI D2 cold work tool steel against alumina ball realized at 0.1 m/s sliding speeds and under the loads of 2.5N, 5N and 10N. Steel samples were nitrided at 575°C for 8 h in the first step of the coating process, and then chromium nitride coating was performed thermo-reactive deposition technique (TRD) in a powder mixture consisting of ferro-chromium, ammonium chloride and alumina at 1000°C for 2 h. Nitro-chromized samples were characterized by X-Ray diffraction analysis (XRD), scanning electron microscopy (SEM), micro-hardness and ball on disk wear tests. The coating layermore » formed on the AISI D2 steel was compact and homogeneous. X-ray studies showed that the phase formed in the coated layer is Cr{sub 2}N. The depth of the layer was 8.15 µm. The average hardness of the layer was 2160±15 HV{sub 0.025}. For uncoated and chromium nitride materials, wear rate increased with increasing load. The results of friction coefficient and wear rate of the tested materials showed that the CrN coating presents the lowest results.« less

In Vitro Effect of Bleaching With 810 nm and 980 nm Diode Laser on Microhardness of Self-cure and Light-Cure Glass Ionomer Cements.

PubMed

Ranjbar Omrani, Ladan; Khoshamad, Sara; Tabatabaei Ghomshe, Elham; Chiniforush, Nasim; Hashemi Kamangar, Sedighe Sadat

2017-01-01

Introduction: This study sought to assess the effect of bleaching combined with irradiation of 810 nm and 980 nm diode laser on microhardness of 2 commonly used self-cure and light-cure glass ionomer cements (GICs) in comparison with conventional bleaching (without laser). Methods: In this in vitro, experimental study, 60 samples were fabricated of A2 shade of Fuji IX and Fuji II LC GICs (n=30) and each group was divided into 3 subgroups (n=10). The first subgroups were subjected to bleaching with Opalescence Xtra Boost plus 980 nm diode laser irradiation. The second subgroups were subjected to bleaching with Opalescence Boost plus 810 nm diode laser irradiation and the third subgroups were subjected to bleaching with Opalescence Xtra Boost without laser. Microhardness was measured at baseline and after the intervention using Vickers hardness tester. The data were analyzed using two-way analysis of variance (ANOVA) ( P <0.05). Results: Microhardness decreased in all subgroups after the intervention (P<0.001) irrespective of the type of GIC ( P =0.201) or surface treatment ( P =0.570). The baseline microhardness of the three subgroups within each group of GIC was not significantly different ( P =0.456), but the baseline microhardness of conventional GIC was significantly higher than that of resin modified GIC ( P =0.004). Conclusion: Bleaching with/without laser irradiation decreases the microhardness of GICs. The baseline microhardness of conventional GIC is higher than that of resin modified GIC.

Effect of high- or low-concentration bleaching agents containing calcium and/or fluoride on enamel microhardness.

PubMed

Furlan, Isabella Spinardi; Bridi, Enrico Coser; Amaral, Flávia Lucisano Botelho do; França, Fabiana Mantovani Gomes; Turssi, Cecilia Pedroso; Basting, Roberta Tarkany

2017-01-01

The aim of this in vitro study was to evaluate enamel microhardness following bleaching treatments using either high- or low-concentration hydrogen peroxide (HP) agents containing calcium and/or fluoride. Sixty enamel blocks were bleached with 1 of 6 different bleaching agents (n = 10). The high-concentration HP agents were Whiteness HP Maxx (35% HP), Whiteness HP Blue (35% HP, 2% calcium gluconate), Pola Office+ (37.5% HP, 5% potassium nitrate), and Opalescence Boost (38% HP, 1.1% fluoride ion, 3% potassium nitrate). The low-concentration HP agents evaluated were Pola Day (9.5% HP) and White Class (10% HP, potassium nitrate, calcium, fluoride). High-concentration agents were applied in 3 sessions, whereas low-concentration agents were applied for 14 days. Knoop microhardness measurements were taken on the surface of the enamel before bleaching, at various timepoints during bleaching, and 14 days after the final bleaching treatment. The 2-way analysis of variance test showed that microhardness values were significantly influenced by the bleaching agent (P < 0.001) and application time (P < 0.001). The Tukey test showed that enamel bleached with Whiteness HP Maxx or White Class presented lower microhardness values than did the enamel treated with the remaining products. There was a reduction in micro-hardness values up to the end of the treatment. The results showed that the composition, concentration, and application protocol for each bleaching agent influenced the enamel microhardness values in that the microhardness decreased over time, regardless of the agent used or the addition of calcium and/or fluoride.

Non-destructive Magnetic Evaluation of Laser Weld Quality in Hot Rolled Coils

NASA Astrophysics Data System (ADS)

Mohapatra, J. N.; Chakradhar, I.; Rao, K. R. C.; Rao, V. V. L.; Kaza, Marutiram

2015-06-01

Weld quality evaluation was conducted on laser welded thin sectsions (2 mm) of hot-rolled (HR) low-carbon steel coils during cold rolling process. The analysis revealed that the poor welds consisting of the weld defects like incomplete fusion, cluster of porosity, and large difference in hardness between the weld zone and base metal were responsible for the weld failures. Experiments were conducted by varying the welding parameters; laser power and welding speed to optimize the parameters for minimizing the weld defects. The optimized weld process parameters have helped elimination of weld defects and the results are verified with microscopy and microhardness measurements. As destructive evaluation techniques are time consuming and not always permitted in industrial applications, attempts have been made in the present investigation for the utilization of suitable non-destructive techniques for the evaluation of weld quality. Non-destructive magnetic techniques of magnetic hysteresis loop and magnetic Barkhausen emissions were used in the present investigation to establish possible correlations of magnetic properties across the weld seam with the mechanical property (microhardness) for evaluation of weld quality. It is inferred that the magnetic properties of coercivity and inverse of root mean square voltage can be effectively utilized to determine weld quality in HR steel coils.

Mineral loss and morphological changes in dental enamel induced by a 16% carbamide peroxide bleaching gel.

PubMed

Soares, Diana Gabriela; Ribeiro, Ana Paula Dias; Sacono, Nancy Tomoko; Loguércio, Alessandro Dourado; Hebling, Josimeri; Costa, Carlos Alberto de Souza

2013-01-01

The aim of this study was to compare the effect of a 16% carbamide peroxide (CP) gel and a 10% CP gel on mineralized enamel content and morphology. Enamel blocks from bovine incisors were subjected to a 14-day treatment (8 h/day) with 10% or 16% CP gels. Knoop microhardness was evaluated before bleaching and at 1, 7 or 14 days after this treatment (50 g/15 s). Mineral content (energy-dispersive x-ray spectroscopy), surface roughness and topography (atomic force microscopy) were evaluated at the 14-day period. Data were analyzed statistically by two-way ANOVA and Tukey's test (α=0.05). Significant microhardness reduction was observed at the 7 th and 14 th days for 10% CP gel, and for all bleaching times for 16% CP gel (p<0.05). At the 14-day period, a significant decrease in Ca and P content, increase on surface roughness (p<0.05) as well as on picks and valleys distance were observed when both bleaching gels were used. These enamel alterations were more intense for 16% CP gel. It was concluded that both CP-based gels promoted loss of mineral structure from enamel, resulting in a rough and porous surface. However, 16% CP gel caused the most intense adverse effects on enamel.

Direct Metal Deposition of H13 Tool Steel on Copper Alloy Substrate: Parametric Investigation

NASA Astrophysics Data System (ADS)

Imran, M. Khalid; Masood, S. H.; Brandt, Milan

2015-12-01

Over the past decade, researchers have demonstrated interest in tribology and prototyping by the laser aided material deposition process. Laser aided direct metal deposition (DMD) enables the formation of a uniform clad by melting the powder to form desired component from metal powder materials. In this research H13 tool steel has been used to clad on a copper alloy substrate using DMD. The effects of laser parameters on the quality of DMD deposited clad have been investigated and acceptable processing parameters have been determined largely through trial-and-error approaches. The relationships between DMD process parameters and the product characteristics such as porosity, micro-cracks and microhardness have been analysed using scanning electron microscope (SEM), image analysis software (ImageJ) and microhardness tester. It has been found that DMD parameters such as laser power, powder mass flow rate, feed rate and focus size have an important role in clad quality and crack formation.

Microstructure Evolution and Mechanical Properties of Mg-14%Li-1%Al Alloy During the High-Pressure Torsion

NASA Astrophysics Data System (ADS)

Tian, Chenguang; Lu, Huimin; Zhao, Liyuan

The super-light LA141 (Mg-14%Li-1%Al) alloy was produced and processed by high-pressure torsion (HPT) under the imposed pressure of 3 GPa and different shear strains γ through 3, 6, 9 and 12 turns at room temperature (RT). The microstructure evolution of the alloy during the HPT treatment was investigated by transmission electron microscope (TEM) and optical microscope (OM). It turned out that the grains were substantially refined, and the optical microscope revealed that the grains of HPT processed samples at the edge of the disc were finer by comparison with the ones near the center of the disc. Later, Vickers indentation analysis was used to evaluate the micro-hardness of deformed samples, and tension test was employed to obtain the strength and elongation at room temperature. The results indicated that the micro-hardness and tensile strength had increased to a certain extent, and the elongation had been significantly improved.

Microstructural variation through weld thickness and mechanical properties of peened friction stir welded 6061 aluminum alloy joints

DOE Office of Scientific and Technical Information (OSTI.GOV)

Abdulstaar, Mustafa A., E-mail: mustafa.abdulstaar

The current study examined the effect of microstructure variation on the development of mechanical properties in friction stir welded joints of 6061-T6 aluminum alloy, which were subsequently processed by shot peening (SP). Following to FSW, fatigue specimens were extracted perpendicularly to the welding direction. Surface Skimming to 0.5 mm from crown and root sides of the joint was made and SP was later applied on the two sides using ceramic shots of two different Almen intensities of 0.18 mmA and 0.24 mmA. Microstructural examination by electron back scattered diffraction (EBSD) indicated variation in the grain refinement of the weld zone,more » with coarsest grains (5 μm) at the crown side and finest grains (2 μm) at the root side. Reduction of microhardness to 60 HV occurred in the weld zone for samples in FSW condition. Application of SP promoted significant strain hardening at the crown side, with Almen intensities of 0.24 mmA providing maximum increase in microhardness to 120 HV. On the contrary, only a maximum microhardness of 75 HV was obtained at the root side. The difference in strain hardening capability at the two sides was strongly dependent on grain size. The two Almen intensities produced similar distribution of compressive residual stresses in the subsurface regions that led to enhance the fatigue strength to the level of base metal for N ≥ 10{sup 5} cycles. Yet, the increase in fatigue strength was more pronounced with increasing Almen intensity to 0.24 mmA, demonstrating further enhancement by strain hardening. - Highlights: • Grain refinement was observed after friction stir welding of AA 6061-T6. • Reduction in microhardness and fatigue strength were obtained after welding. • Variation in grain refinement led to different hardening behavior after peening. • Shot peening induced beneficial compressive residual stresses. • Shot peening and surface skimming markedly improved the fatigue performance.« less

Comparing the Effects of Whey Extract and Casein Phosphopeptide-Amorphous Calcium Phosphate (CPP-ACP) on Enamel Microhardness

PubMed Central

Rezvani, Mohammad Bagher; Karimi, Mehrdad; Akhavan Rasoolzade, Raheleh; Haghgoo, Roza

2015-01-01

Statement of the Problem With the recent focus of researches on the development of non-invasive treatment modalities, the non-invasive treatment of early carious lesions by remineralization would bring a major advance in the clinical management of these dental defects. Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) is considered to be effective in tooth remineralization. Purpose The aim of this in-vitro study was to compare the effects of whey and CPP-ACP in increasing the enamel microhardness. Materials and Method Microhardness of 30 sound human permanent premolars was measured before and after 8-minute immersion of samples in Coca-Cola. The teeth were then randomly divided into 3 groups and were immersed in artificial saliva, whey, and tooth mousse for 10 minutes. The changes of microhardness within each group and among the groups were recorded and analyzed using paired t-test. Results The microhardness increased in each group and between the groups; this increase was statistically significant (p= 0.009). Conclusion The effect of whey on increasing the enamel microhardness was more than that of tooth mousse. PMID:25759858

Effect of four over-the-counter tooth-whitening products on enamel microhardness.

PubMed

Majeed, A; Grobler, S R; Moola, M H; Oberholzer, T G

2011-10-01

This in vitro study evaluated the effect of four over-the-counter tooth-whitening products on enamel microhardness. Fifty enamel blocks were prepared from extracted human molar teeth. The enamel surfaces were polished up to 1200 grit fineness and the specimens randomly divided into five groups. Enamel blocks were exposed to: Rapid White (n=10); Absolute White (n=10); Speed White (n=10) and White Glo (n=10) whitening products, according to the manufacturers' instructions. As control, ten enamel blocks were kept in artificial saliva at 37 degrees C without any treatment. Microhardness values were obtained before exposure (baseline) and after 1, 7 and 14-day treatment periods using a digital hardness tester with a Vickers diamond indenter. Data were analysed using Wilcoxon Signed Rank Sum Test, one-way ANOVA and Tukey-Kramer Multiple Comparison Test (p<0.05). Both Rapid White and Absolute White reduced enamel microhardness. Speed White increased the microhardness of enamel, while White Glo and artificial saliva had no effect on hardness. Over-the-counter tooth-whitening products might decrease enamel microhardness depending on the type of product.

New developments in electron microscopy for serial image acquisition of neuronal profiles.

PubMed

Kubota, Yoshiyuki

2015-02-01

Recent developments in electron microscopy largely automate the continuous acquisition of serial electron micrographs (EMGs), previously achieved by laborious manual serial ultrathin sectioning using an ultramicrotome and ultrastructural image capture process with transmission electron microscopy. The new systems cut thin sections and capture serial EMGs automatically, allowing for acquisition of large data sets in a reasonably short time. The new methods are focused ion beam/scanning electron microscopy, ultramicrotome/serial block-face scanning electron microscopy, automated tape-collection ultramicrotome/scanning electron microscopy and transmission electron microscope camera array. In this review, their positive and negative aspects are discussed. © The Author 2015. Published by Oxford University Press on behalf of The Japanese Society of Microscopy. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

Experimental and numerical study on plasma nitriding of AISI P20 mold steel

NASA Astrophysics Data System (ADS)

Nayebpashaee, N.; Vafaeenezhad, H.; Kheirandish, Sh.; Soltanieh, M.

2016-09-01

In this study, plasma nitriding was used to fabricate a hard protective layer on AISI P20 steel, at three process temperatures (450°C, 500°C, and 550°C) and over a range of time periods (2.5, 5, 7.5, and 10 h), and at a fixed gas N2:H2 ratio of 75vol%:25vol%. The morphology of samples was studied using optical microscopy and scanning electron microscopy, and the formed phase of each sample was determined by X-ray diffraction. The elemental depth profile was measured by energy dispersive X-ray spectroscopy, wavelength dispersive spectroscopy, and glow dispersive spectroscopy. The hardness profile of the samples was identified, and the microhardness profile from the surface to the sample center was recorded. The results show that ɛ-nitride is the dominant species after carrying out plasma nitriding in all strategies and that the plasma nitriding process improves the hardness up to more than three times. It is found that as the time and temperature of the process increase, the hardness and hardness depth of the diffusion zone considerably increase. Furthermore, artificial neural networks were used to predict the effects of operational parameters on the mechanical properties of plastic mold steel. The plasma temperature, running time of imposition, and target distance to the sample surface were all used as network inputs; Vickers hardness measurements were given as the output of the model. The model accurately reproduced the experimental outcomes under different operational conditions; therefore, it can be used in the effective simulation of the plasma nitriding process in AISI P20 steel.

CO2 laser irradiation enhances CaF2 formation and inhibits lesion progression on demineralized dental enamel-in vitro study.

PubMed

Zancopé, Bruna R; Rodrigues, Lívia P; Parisotto, Thais M; Steiner-Oliveira, Carolina; Rodrigues, Lidiany K A; Nobre-dos-Santos, Marinês

2016-04-01

This study evaluated if Carbon dioxide (CO2) (λ 10.6 μm) laser irradiation combined with acidulated phosphate fluoride gel application (APF gel) enhances "CaF2" uptake by demineralized enamel specimens (DES) and inhibits enamel lesion progression. Thus, two studies were conducted and DES were subjected to APF gel combined or not with CO2 laser irradiation (11.3 or 20.0 J/cm(2), 0.4 or 0.7 W) performed before, during, or after APF gel application. In study 1, 165 DES were allocated to 11 groups. Fluoride as "CaF2 like material" formed on enamel was determined in 100 DES (n = 10/group), and the surface morphologies of 50 specimens were evaluated by scanning electron microscopy (SEM) before and after "CaF2" extraction. In study 2, 165 DES (11 groups, n = 15), subjected to the same treatments as in study 1, were further subjected to a pH-cycling model to simulate a high cariogenic challenge. The progression of demineralization in DES was evaluated by cross-sectional microhardness and polarized light microscopy analyses. Laser at 11.3 J/cm(2) applied during APF gel application increased "CaF2" uptake on enamel surface. Laser irradiation and APF gel alone arrested the lesion progression compared with the control (p < 0.05). Areas of melting, fusion, and cracks were observed. CO2 laser irradiation, combined with a single APF application enhanced "CaF2" uptake on enamel surface and a synergistic effect was found. However, regarding the inhibition of caries lesion progression, no synergistic effect could be demonstrated. In conclusion, the results have shown that irradiation with specific laser parameters significantly enhanced CaF2 uptake by demineralized enamel and inhibited lesion progression.

Effect of titanium dioxide nanoparticle addition into orthodontic adhesive resin on enamel microhardness

NASA Astrophysics Data System (ADS)

Andriani, A.; Krisnawati; Purwanegara, M. K.

2017-08-01

White spots are an early sign of enamel demineralization, which may lead to development of dental caries. Enamel demineralization can be determined by examining the microhardness number of the enamel. Addition of antibacterial agents such as TiO2 nanoparticles into the orthodontic adhesive (TiO2 nanocomposite) is expected to prevent enamel demineralization. The objective of this study is to evaluate the effect of TiO2 nanocomposites in maintaining enamel microhardness around orthodontic brackets. The bracket was bonded to the premolar using Transbond XT (group 1), 1% TiO2 nanocomposites (group 2), and 2% TiO2 nanocomposites (group 3). Group 4 was the control group, and it was not given any treatment prior to the microhardness test. The samples of groups 1, 2, and 3 were soaked in BHI solution containing Streptococcus mutans, and then stored in an incubator at 37°C for 30 days. Demineralizations were determined on cross-sectioned tooth 100μm and 200μm cervical to the bracket by the Vickers microhardness test. The microhardness values were significantly different between every group, with the highest value obtained for control group, followed by the 2% TiO2 nanocomposite group, 1% TiO2 nanocomposite group, and then the Transbond XT group. The results of this study reveal that 2% TiO2 nanocomposites have the ability to maintain enamel microhardness around the orthodontic bracket.

Influence of remineralizing gels on bleached enamel microhardness in different time intervals.

PubMed

Borges, Alessandra Bühler; Yui, Karen Cristina Kazue; D'Avila, Thaís Corrêa; Takahashi, Camila Lurie; Torres, Carlos Rocha Gomes; Borges, Alexandre Luis Souto

2010-01-01

This study evaluated the influence of bleaching gel pH, the effect of applying remineralizing gels after bleaching and the effect of artificial saliva on enamel microhardness. Seventy bovine incisors were divided into three groups: Group 1 (n=10) received no bleaching procedure (control); Group 2 was bleached with a 35% hydrogen peroxide neutral gel (n=30) and Group 3 was bleached with a 35% hydrogen peroxide acid gel (n=30). Each experimental group was subdivided into three groups (n=10) according to the post-bleaching treatment: storage in artificial saliva, application of a fluoride gel and application of a combination of calcium and fluoride gel. The specimens were stored in artificial saliva for 7, 15 and 30 days and enamel microhardness was evaluated. The Vickers microhardness data were analyzed by three-way RM ANOVA, which revealed a significant difference only for treatment factor. The Tukey's test showed that the groups bleached followed by no additional treatment exhibited microhardness means significantly lower than the bleached groups treated with remineralizing gels. The Dunnet's test showed a significant difference only for the group bleached with acid gel without remineralizing treatment compared to the control group measured immediately after bleaching. It was concluded that acid bleaching gel significantly reduced enamel microhardness and that use of remineralizing gels after bleaching can significantly enhance the microhardness of bleached enamel.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, Xiangyu

The ordering transformation occurring in a model Ni-Cr-W superalloy during prolonged exposure to proper temperature has been investigated systematically. It is demonstrated that nanometer-sized precipitates with a DO{sub 22} structure can precipitate in the Ni-Cr-W alloy by means of simple aging treatment at 650–700 °C. The mechanism of transformation to DO{sub 22} superlattice has been determined to be continuous ordering based on the results of high resolution transmission electron microscopy investigation and variation trend in Vickers microhardness. Different variants of DO{sub 22} phase can coexist in the matrix with no signs of overaging as aging time increases, indicating it hasmore » a high thermal stability. The precipitates of DO{sub 22} superlattice has been found to be of ellipsoidal shape which results in the greatest reduction of strain energy. The interfaces between DO{sub 22} precipitates and matrix have been revealed to be coherent at the atomic scale, resulting in considerable coherency strain attributing to the lattice misfit between DO{sub 22} particle and matrix. Because of the high-density nanometer-sized DO{sub 22} phase, the microhardness of the alloy has been improved remarkably after aging treatment. - Graphical abstract: Different variants of the DO{sub 22} superlattice can coexist in the matrix, and the interface between precipitate and the matrix remain coherence at the atomic scale. The three dimensional form of the DO{sub 22} precipitates constructed from three mutually perpendicular projections is an ellipsoidal stick, and the directions of elongations are along the longest axis of the unit cell for DO{sub 22} phase. - Highlights: •The DO{sub 22} phase precipitated in the Ni-Cr-W alloy has a high thermal stability. •The morphology of DO{sub 22} superlattice has been determined to be ellipsoid. •The interface between DO{sub 22} phase and matrix are fully coherent at the atomic scale. •Different variants of DO{sub 22} phase occur equiprobably. •The alloy strength can be improved dramatically by the nanoscale DO{sub 22} particles.« less

Investigation of physical and mechanical properties of (BaSnO3)x(Bi,Pb)-2223 composite

NASA Astrophysics Data System (ADS)

Habanjar, K.; Barakat, M. M. E.; Awad, R.

2017-07-01

The effect of BaSnO3 nanoparticles addition on the structural and mechanical properties of (Bi,Pb)-2223 superconducting phase by means of X-rays diffraction analysis (XRD), scanning electron microscope (SEM), electrical resistance and Vickers microhardness measurement was studied. BaSnO3 nanomaterial and (BaSnO3)x(Bi,Pb)-2223 superconducting samples were prepared using co-precipitation method and standard solid-state reaction techniques, respectively. From XRD data, the addition of BaSnO3 into (Bi,Pb)-2223 phase does not affect the tetragonal structure and the lattice parameters. SEM images indicate that the microstructure of (Bi,Pb)-2223 was enhanced by adding BaSnO3 nanoparticles by filling its pores and voids. The superconducting transition temperature Tc as well as the critical transport current density Jc, estimated from electrical resistivity measurements, are increased up to x = 0.5 wt%, then decreased with further increase in x. Vickers microhardness measurements Hv were carried out at room temperature as a function of applied. The experimental Hv results were analysed in view of Meyer’s law, Hays and Kendall (HK) approach, elastic/plastic deformation (EPD) and proportional specimen resistance (PSR). All samples exhibit normal indentation size effect (ISE), in addition to that, the analysis shows that the Hays and Kendall model is the most suitable one to describe the load independent microhardness for (BaSnO3)x(Bi,Pb)-2223 superconducting samples.

Effect of Bonding Time on Interfacial Reaction and Mechanical Properties of Diffusion-Bonded Joint Between Ti-6Al-4V and 304 Stainless Steel Using Nickel as an Intermediate Material

NASA Astrophysics Data System (ADS)

Thirunavukarasu, Gopinath; Kundu, Sukumar; Mishra, Brajendra; Chatterjee, Subrata

2014-04-01

In the current study, solid-state diffusion bonding between Ti-6Al-4V (TiA) and 304 stainless steel (SS) using pure nickel (Ni) of 200- μm thickness as an intermediate material was carried out in vacuum. Uniaxial compressive pressure and temperature were kept at 4 MPa and 1023 K (750 °C), respectively, and the bonding time was varied from 30 to 120 minutes in steps of 15 minutes. Scanning electron microscopy images, in backscattered electron mode, revealed the layerwise Ti-Ni-based intermetallics like either Ni3Ti or both Ni3Ti and NiTi at titanium alloy-nickel (TiA/Ni) interface, whereas nickel-stainless steel (Ni/SS) interface was free from intermetallic phases for all the joints. Chemical composition of the reaction layers was determined by energy dispersive spectroscopy (SEM-EDS) and confirmed by X-ray diffraction study. Maximum tensile strength of ~382 MPa along with ~3.7 pct ductility was observed for the joints processed for 60 minutes. It was found that the extent of diffusion zone at Ni/SS interface was greater than that of TiA/Ni interface. From the microhardness profile, fractured surfaces, and fracture path, it was demonstrated that the failure of the joints was initiated and propagated apparently at TiA/Ni interface near Ni3Ti intermetallic for bonding time less than 90 minutes, and through Ni for bonding time 90 minutes and greater.

Gas tungsten arc welding and friction stir welding of ultrafine grained AISI 304L stainless steel: Microstructural and mechanical behavior characterization

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sabooni, S., E-mail: s.sabooni@ma.iut.ac.ir; Karimzadeh, F.; Enayati, M.H.

In the present study, an ultrafine grained (UFG) AISI 304L stainless steel with the average grain size of 650 nm was successfully welded by both gas tungsten arc welding (GTAW) and friction stir welding (FSW). GTAW was applied without any filler metal. FSW was also performed at a constant rotational speed of 630 rpm and different welding speeds from 20 to 80 mm/min. Microstructural characterization was carried out by High Resolution Scanning Electron Microscopy (HRSEM) with Electron Backscattered Diffraction (EBSD) and Transmission Electron Microscopy (TEM). Nanoindentation, microhardness measurements and tensile tests were also performed to study the mechanical properties ofmore » the base metal and weldments. The results showed that the solidification mode in the GTAW welded sample is FA (ferrite–austenite) type with the microstructure consisting of an austenite matrix embedded with lath type and skeletal type ferrite. The nugget zone microstructure in the FSW welded samples consisted of equiaxed dynamically recrystallized austenite grains with some amount of elongated delta ferrite. Sigma phase precipitates were formed in the region ahead the rotating tool during the heating cycle of FSW, which were finally fragmented into nanometric particles and distributed in the weld nugget. Also there is a high possibility that the existing delta ferrite in the microstructure rapidly transforms into sigma phase particles during the short thermal cycle of FSW. These suggest that high strain and deformation during FSW can promote sigma phase formation. The final austenite grain size in the nugget zone was found to decrease with increasing Zener–Hollomon parameter, which was obtained quantitatively by measuring the peak temperature, calculating the strain rate during FSW and exact examination of hot deformation activation energy by considering the actual grain size before the occurrence of dynamic recrystallization. Mechanical properties observations showed that the welding efficiency of the FSW welded sample is around 70%, which is more than 20% higher than the GTAW welded sample. - Highlights: • Microstructure and mechanical properties of UFG 304L stainless steel were studied during GTAW and FSW. • Sigma phase formation mechanism was studied during FSW of 304L stainless steel. • THERMOCALC analysis was performed to obtain possible formation temperatures for sigma phase. • Nano-mechanical twins were found in the TMAZ region.« less

Microhardness study of the nonlinear optical crystal L-arginine hydrochloride monohydrate

NASA Astrophysics Data System (ADS)

Mukerji, Sudeshna; Kar, Tanusree

2000-12-01

The results of measurement of the Vickers microhardness ( H v ) of the (100), (010), and (001) faces of the nonlinear optical (NLO) crystal L-arginine hydrochloride monohydrate (LAHCl) have been reported. It was observed that the microhardnesses of the three crystal planes decrease with the increase of applied load, and the hardness profile is different for different planes. The proportional specimen-resistance (PSR) model of Li and Bradt is used to explain the microhardness behavior of LAHCl. The indentation work-hardening coefficients ( n) for three planes were found to be greater than 1.8, and this indicates that LAHCl is a soft crystal.

Effect of three nanobiomaterials on microhardness of bleached enamel

PubMed Central

Kaveh, Sara

2016-01-01

Objectives The aim of this in vitro study was to evaluate the effect of incorporating three different nanobiomaterials into bleaching material on microhardness of bleached enamel. Materials and Methods The crowns of 24 extracted sound human molars were sectioned. Sixty enamel specimens (2 × 3 × 4 mm) were selected and divided into five groups (n = 12): Group 1 received no bleaching procedure (control); Group 2 underwent bleaching with a 40% hydrogen peroxide (HP) gel; Groups 3, 4, and 5 were bleached with a 40% HP gel modified by incorporation of bioactive glass (BAG), amorphous calcium phosphate (ACP) and hydroxyapatite (HA), respectively. The enamel microhardness was evaluated. The differences in Knoop microhardness data of each group were analyzed by one-way ANOVA, followed by post hoc Tukey tests. Results Significant differences were observed between the study groups. The enamel microhardness changes in Groups 1, 3, 4, and 5 were significantly lower than that of Group 2 (p < 0.001). Conclusions Within the limitations of this study, it can be concluded that incorporation of each one of the three tested biomaterials as remineralizing agents might be effective in decreasing enamel microhardness changes subsequent to in-office bleaching. PMID:27508161

Friction Stir Spot Welding of Advanced High Strength Steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hovanski, Yuri; Grant, Glenn J.; Santella, M. L.

Friction stir spot welding techniques were developed to successfully join several advanced high strength steels. Two distinct tool materials were evaluated to determine the effect of tool materials on the process parameters and joint properties. Welds were characterized primarily via lap shear, microhardness, and optical microscopy. Friction stir spot welds were compared to the resistance spot welds in similar strength alloys by using the AWS standard for resistance spot welding high strength steels. As further comparison, a primitive cost comparison between the two joining processes was developed, which included an evaluation of the future cost prospects of friction stir spotmore » welding in advanced high strength steels.« less

Influence of investment, disinfection, and storage on the microhardness of ocular resins.

PubMed

Goiato, Marcelo Coelho; dos Santos, Daniela Micheline; Gennari-Filho, Humberto; Zavanelli, Adriana Cristina; Dekon, Stefan Fiuza de Carvalho; Mancuso, Daniela Nardi

2009-01-01

The longevity of an ocular prosthesis is directly related to the resistance to erosion of its material. The purpose of this study was to evaluate the effects of chemical disinfection and the method of investment on the microhardness of ocular prosthesis acrylic resin. Thirty-two test specimen investments were obtained in two silicones. A segment was cut in each test specimen, and each specimen was fixed in an acrylic disk. The specimens were then polished and submitted to the first microhardness test before immersion in distilled water and incubation for 2 months. During this 2-month period, the specimens were immersed in a water bath at 37 degrees C and were disinfected daily; half were disinfected with neutral soap and the other half were disinfected with 4% chlorhexidine gluconate. After the storage phase and disinfection, a second microhardness test was performed. The surface microhardness values for the acrylic resins were submitted to ANOVA, followed by the Tukey test. The disinfection and the period of storage did not statistically influence the surface microhardness of the acrylic resin, independent of the method of investment of the specimens (Zetalabor or Vipi Sil). The investment of specimens with Zetalabor silicone presented a greater surface hardness, independent of the type of disinfection and the period of storage. Based on these results, we suggest that the microhardness of the resin evaluated was not influenced by the method of disinfection or the time of storage used and was affected only by the investment material.

Mechanically induced self-propagating reaction and consequent consolidation for the production of fully dense nanocrystalline Ti{sub 55}C{sub 45} bulk material

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sherif El-Eskandarany, M., E-mail: msherif@kisr.edu.kw; Al-Hazza, Abdulsalam

2014-11-15

We employed a high-energy ball mill for the synthesis of nanograined Ti{sub 55}C{sub 45} powders starting from elemental Ti and C powders. The mechanically induced self-propagating reaction that occurred between the reactant materials was monitored via a gas atmosphere gas-temperature-monitoring system. A single phase of NaCl-type TiC was obtained after 5 h of ball milling. To decrease the powder and grain sizes, the material was subjected to further ball milling time. The powders obtained after 200 h of milling possessed spherical-like morphology with average particle and grain sizes of 45 μm and 4.2 nm, respectively. The end-products obtained after 200more » h of ball milling time, were then consolidated into full dense compacts, using hot pressing and spark plasma sintering at 1500 and 34.5 MPa, with heating rates of 20 °C/min and 500 °C/min, respectively. Whereas hot pressing of the powders led to severe grain growth (∼ 436 nm in diameter), the as-spark plasma sintered powders maintained their nanograined characteristics (∼ 28 nm in diameter). The as-synthesized and as-consolidated powders were characterized, using X-ray diffraction, high-resolution electron microscopy, and scanning electron microscopy. The mechanical properties of the consolidated samples obtained via the hot pressing and spark plasma sintering techniques were characterized, using Vickers microhardness and non-destructive testing techniques. The Vickers hardness, Young's modulus, shear modulus and fracture toughness of as-spark plasma sintered samples were 32 GPa, 358 GPa, 151 GPa and 6.4 MPa·m{sup 1/2}, respectively. The effects of the consolidation approach on the grain size and mechanical properties were investigated and are discussed. - Highlights: • Room-temperature synthesizing of NaCl-type TiC • Dependence on the grain size on the ball milling time • Fabrication of equiaxed nanocrystalline grains with a diameter of 4.2 nm • Fabrication of nanocrystalline bulk TiC material by SPS with minimal grain growth • Dependence of improved mechanical properties on the consolidation techniques.« less

Platinum replica electron microscopy: Imaging the cytoskeleton globally and locally.

PubMed

Svitkina, Tatyana M

2017-05-01

Structural studies reveal how smaller components of a system work together as a whole. However, combining high resolution of details with full coverage of the whole is challenging. In cell biology, light microscopy can image many cells in their entirety, but at a lower resolution, whereas electron microscopy affords very high resolution, but usually at the expense of the sample size and coverage. Structural analyses of the cytoskeleton are especially demanding, because cytoskeletal networks are unresolvable by light microscopy due to their density and intricacy, whereas their proper preservation is a challenge for electron microscopy. Platinum replica electron microscopy can uniquely bridge the gap between the "comfort zones" of light and electron microscopy by allowing high resolution imaging of the cytoskeleton throughout the entire cell and in many cells in the population. This review describes the principles and applications of platinum replica electron microscopy for studies of the cytoskeleton. Copyright © 2017 Elsevier Ltd. All rights reserved.

Platinum Replica Electron Microscopy: Imaging the Cytoskeleton Globally and Locally

PubMed Central

SVITKINA, Tatyana M.

2017-01-01

Structural studies reveal how smaller components of a system work together as a whole. However, combining high resolution of details with full coverage of the whole is challenging. In cell biology, light microscopy can image many cells in their entirety, but at a lower resolution, whereas electron microscopy affords very high resolution, but usually at the expense of the sample size and coverage. Structural analyses of the cytoskeleton are especially demanding, because cytoskeletal networks are unresolvable by light microscopy due to their density and intricacy, whereas their proper preservation is a challenge for electron microscopy. Platinum replica electron microscopy can uniquely bridge the gap between the “comfort zones” of light and electron microscopy by allowing high resolution imaging of the cytoskeleton throughout the entire cell and in many cells in the population. This review describes the principles and applications of platinum replica electron microscopy for studies of the cytoskeleton. PMID:28323208

Microhardness of anodic aluminum oxide formed in an alkaline electrolyte

NASA Astrophysics Data System (ADS)

Kanygina, O. N.; Filyak, M. M.

2017-04-01

The microhardness of anodic aluminum oxide formed by anodizing of aluminum sheet in electrolyte on the basis of sodium hydroxide has been determined experimentally. The microhardness of the hard film/soft substrate system has been estimated by three approaches: indentation geometry (length of diagonals) in film surfaces, the sum of the hardnesses of the film and the surface with allowance for the indentation surface area and geometry, and with allowance for the indentation depth. It is demonstrated that the approach accounting for the indentation depth makes it possible to eliminate the influence of the substrate. It is established that the microhardness of the films formed in alkaline electrolytes is comparable with that formed in acid electrolytes.

Effect of FSW welding speed on microstructure and microhardness of Al-0.84Mg-0.69Si-0.76Fe alloy at moderate rotational tool velocity

NASA Astrophysics Data System (ADS)

Chand, Suresh; Vineetha, S.; Madhusudhan, D.; Sai Krishna, CH; Kusuma Devi, G.; Bhawani; Hemarao, K.; Ganesh Naidu, G.

2018-03-01

The plate of 7.0 mm thickness was double side welded using friction stir welding is investigated. The rotational velocity of friction stir welding tool is used 1400 rpm. The influence of welding speed on the microstructure and microhardness values of Al-0.84Mg-0.69Si-0.76Fe aluminum alloy is presented. Two welding speeds 25 mm/min and 31.5 mm/min are used. The microhardness values of friction stir weld are measured at various locations from the weld interface. The microhardness values in stir zone of weld are found larger than lower welding speed at constant rotational velocity of 1400 rpm of friction stir welding tool. The similar effects on microhardness values are found in the thermo-mechanically affected zone and heat affected zone. The fine microstructure is observed at 31.5 mm/min welding speed compared to the 25 mm/min welding speed at 1400 rpm.

Microhardness evaluations of CAD/CAM ceramics irradiated with CO2 or Nd:YAP laser

PubMed Central

Rocca, Jean Paul; Fornaini, Carlo; Medioni, Etienne; Brulat-Bouchard, Nathalie

2017-01-01

Background and aims The aim of this study was to measure the microhardness values of irradiated computer-aided design/computer-aided manufacturing (CAD/CAM) ceramics surfaces before and after thermal treatment. Materials and Methods Sixty CAD/CAM ceramic discs were prepared and grouped by material, i.e. lithium disilicate ceramic (Emax CAD) and zirconia ceramic (Emax ZirCAD). Laser irradiation at the material surface was performed with a carbon dioxide laser at 5 Watt (W) or 10 W power in continuous mode (CW mode), or with a neodymium:yttrium aluminum perovskite (Nd:YAP) laser at 10 W on graphite and non-graphite surfaces. Vickers hardness was tested at 0.3 kgf for lithium disilicate and 1 kgf for zirconia. Results Emax CAD irradiated with CO2 at 5 W increased microhardness by 6.32 GPa whereas Emax ZirCAD irradiated with Nd:YAP decreased microhardness by 17.46 GPa. Conclusion CO2 laser effectively increases the microhardness of lithium disilicate ceramics (Emax CAD). PMID:28740324

Silver stain for electron microscopy

NASA Technical Reports Server (NTRS)

Corbett, R. L.

1972-01-01

Ammoniacal silver stain used for light microscopy was adapted advantageously for use with very thin biological sections required for electron microscopy. Silver stain can be performed in short time, has more contrast, and is especially useful for low power electron microscopy.

Correlated Light and Electron Microscopy/Electron Tomography of Mitochondria In Situ

PubMed Central

Perkins, Guy A.; Sun, Mei G.; Frey, Terrence G.

2009-01-01

Three-dimensional light microscopy and three-dimensional electron microscopy (electron tomography) separately provide very powerful tools to study cellular structure and physiology, including the structure and physiology of mitochondria. Fluorescence microscopy allows one to study processes in live cells with specific labels and stains that follow the movement of labeled proteins and changes within cellular compartments but does not have sufficient resolution to define the ultrastructure of intracellular organelles such as mitochondria. Electron microscopy and electron tomography provide the highest resolution currently available to study mitochondrial ultrastructure but cannot follow processes in living cells. We describe the combination of these two techniques in which fluorescence confocal microscopy is used to study structural and physiologic changes in mitochondria within apoptotic HeLa cells to define the apoptotic timeframe. Cells can then be selected at various stages of the apoptotic timeframe for examination at higher resolution by electron microscopy and electron tomography. This is a form of “virtual” 4-dimensional electron microscopy that has revealed interesting structural changes in the mitochondria of HeLa cells during apoptosis. The same techniques can be applied, with modification, to study other dynamic processes within cells in other experimental contexts. PMID:19348881

Effect of Diode Laser Irradiation Combined with Topical Fluoride on Enamel Microhardness of Primary Teeth.

PubMed

Bahrololoomi, Zahra; Lotfian, Malihe

2015-02-01

Laser irradiation has been suggested as an adjunct to traditional caries prevention methods. But little is known about the cariostatic effect of diode laser and most studies available are on permanent teeth.The purpose of the present study was to investigate the effect of diode laser irradiation combined with topical fluoride on enamel surface microhardness. Forty-five primary teeth were used in this in vitro study. The teeth were sectioned to produce 90 slabs. The baseline Vickers microhardness number of each enamel surface was determined. The samples were randomly divided into 3 groups. Group 1: 5% NaF varnish, group 2: NaF varnish+ diode laser at 5 W power and group 3: NaF varnish+ diode laser at 7 W power. Then, the final microhardness number of each surface was again determined. The data were statistically analyzed by repeated measures ANOVA at 0.05 level of significance. In all 3 groups, microhardness number increased significantly after surface treatment (P<0.05). However, Microhardness change after treatment was not significantly different among groups (P >0.05). The combined application of diode laser and topical fluoride varnish on enamel surface did not show any significant additional effect on enamel resistance to caries.

Microhardness of demineralized enamel following home bleaching and laser-assisted in office bleaching

PubMed Central

Ghanbarzadeh, Majid; Akbari, Majid; Hamzei, Haniye

2015-01-01

Background There is little data regarding the effect of tooth whitening on microhardness of white spot lesions. This study was conducted to investigate the effect of home-bleaching and laser-assisted in-office bleaching on microhardness of demineralized enamel. Material and Methods Forty bovine incisors were selected and immersed in a demineralizing solution for 12 weeks to induce white spot lesions. Enamel blocks were prepared and randomly assigned to two groups of 20 each. The first group underwent home bleaching with 15% carbamide peroxide which was applied for 8 hours a day over a period of 15 days. In the second group, in-office bleaching was performed by 40% hydrogen peroxide and powered by irradiation from an 810 nm gallium-aluminum-arsenide (GaAlAs) diode laser (CW, 2W). This process was performed for 3 sessions every seven days, in 15 days. The specimens were stored in Fusayama Meyer artificial saliva during the experiment. Surface microhardness was assessed before and after the bleaching therapies in both groups. Results Microhardness decreased significantly following both home bleaching and laser-assisted in-office bleaching (p<0.05). There were no significant differences in hardness values among the two groups either before (p=0.131) or after (p=0.182) the bleaching procedures. Conclusions Tooth whitening through home bleaching or laser-assisted in-office bleaching can result in a significant reduction in microhardness of white spot lesions. Therefore, it is suggested to take protective measures on bleached demineralized enamel. Key words:White spot lesion, bleaching, laser, microhardness, demineralized enamel, home bleaching, in-office bleaching. PMID:26330939

The In vitro Evaluation of the effect of xyliwhite, probiotic, and the conventional toothpastes on the enamel roughness and microhardness.

PubMed

Maden, E Arat; Altun, C; Polat, G Guven; Basak, F

2018-03-01

The aim of this study was to evaluate the effect of fluoride, Xylitol, Probiotic, and Whitening toothpastes on the permanent teeth enamel roughness and microhardness. One hundred and twenty teeth were randomly divided into 2 groups, each group having 60 samples. G1: The group in which enamel roughness was examined (n = 60). G2: The group in which enamel microhardness was examined (n = 60). Then, these groups were randomly divided into 4 groups among themselves (n = 15). Each group was brushed using four different toothpastes for 1 week with a battery-powered toothbrush in the morning and evening for 2 min. Vicker's hardness tester was used to measure the changes in microhardness, and the profilometer was used to measure the changes in surface roughness. No statistically significant differences were found on surface roughness and microhardness values measured after tooth brushing process in group brushed with Colgate MaxFresh toothpaste (P > 0.01). Statistically significant decrease was observed on Vicker's hardness values measured after tooth brushing process in groups brushed with Ipana White Power Carbonate toothpaste, Xyliwhite Toothpaste Gel, and Periobiotic Probiotic Toothpaste (P < 0.01). Statistically significant increase was observed on surface roughness values in groups brushed with Ipana White Power Carbonate toothpaste, Xyliwhite Toothpaste Gel, Periobiotic Probiotic Toothpaste (P < 0.01). As a result, Colgate MaxFresh abrasive-free toothpaste with fluoride has no effect on permanent tooth enamel surface roughness and microhardness. Xyliwhite, Periobiotic, and Ipana White Power Carbonate-containing abrasive toothpastes led to changes negatively on permanent tooth enamel surface roughness and microhardness.

Effect of different bleaching strategies on microhardness of a silorane-based composite resin.

PubMed

Bahari, Mahmoud; Savadi Oskoee, Siavash; Mohammadi, Narmin; Ebrahimi Chaharom, Mohammad Esmaeel; Godrati, Mostafa; Savadi Oskoee, Ayda

2016-01-01

Background. Dentists' awareness of the effects of bleaching agents on the surface and mechanical properties of restorative materials is of utmost importance. Therefore, this in vitro study was undertaken to investigate the effects of different bleaching strategies on the microhardness of a silorane-based composite resin. Methods. Eighty samples of a silorane-based composite resin (measuring 4 mm in diameter and 2 mm in thickness) were prepared within acrylic molds. The samples were polished and randomly assigned to 4 groups (n=20). Group 1 (controls) were stored in distilled water for 2 weeks. The samples in group 2 underwent a bleaching procedure with 15% carbamide peroxide for two weeks two hours daily. The samples in group 3 were bleached with 35% hydrogen peroxide twice 5 days apart for 30 minutes each time. The samples in group 4 underwent a bleaching procedure with light-activated 35% hydrogen peroxide under LED light once for 40 minutes. Then the microhardness of the samples was determined using Vickers method. Data were analyzed with one-way ANOVA and post hoc Tukey tests (P < 0.05). Results. All the bleaching agents significantly decreased microhardness compared to the control group (P < 0.05). In addition, there were significant differences in microhardness between groups 2 and 4 (P = 0.001) and between groups 3 and 4 (P<0.001). However, no significant differences were detected in microhardness between groups 2 and 3 (P > 0.05). Conclusion. Bleaching agents decreased microhardness of silorane-based composite resin restorations, the magnitude of which depending on the bleaching strategy used.

Light transmittance of zirconia as a function of thickness and microhardness of resin cements under different thicknesses of zirconia

PubMed Central

Egilmez, Ferhan; Ergun, Gulfem; Kaya, Bekir M.

2013-01-01

Objective: The objective of this study was to compare microhardness of resin cements under different thicknesses of zirconia and the light transmittance of zirconia as a function of thickness. Study design: A total of 126 disc-shaped specimens (2 mm in height and 5 mm in diameter) were prepared from dual-cured resin cements (RelyX Unicem, Panavia F and Clearfil SA cement). Photoactivation was performed by using quartz tungsten halogen and light emitting diode light curing units under different thicknesses of zirconia. Then the specimens (n=7/per group) were stored in dry conditions in total dark at 37°C for 24 h. The Vicker’s hardness test was performed on the resin cement layer with a microhardness tester. Statistical significance was determined using multifactorial analysis of variance (ANOVA) (alpha=.05). Light transmittance of different thicknesses of zirconia (0.3, 0.5 and 0.8 mm) was measured using a hand-held radiometer (Demetron, Kerr). Data were analyzed using one-way ANOVA test (alpha=.05). Results: ANOVA revealed that resin cement and light curing unit had significant effects on microhardness (p < 0.001). Additionally, greater zirconia thickness resulted in lower transmittance. There was no correlation between the amount of light transmitted and microhardness of dual-cured resin cements (r = 0.073, p = 0.295). Conclusion: Although different zirconia thicknesses might result in insufficient light transmission, dual-cured resin cements under zirconia restorations could have adequate microhardness. Key words:Zirconia, microhardness, light transmittance, resin cement. PMID:23385497

Evaluation and Comparison of Changes in Microhardness of Primary and Permanent Enamel on Exposure to Acidic Center-filled Chewing Gum: An in vitro Study

PubMed Central

Muppa, Radhika; Srinivas, NCH; Kumar, Duddu Mahesh

2014-01-01

ABSTRACT Objectives: The study is to evaluate changes in microhardness of enamel after exposure to acidic center filled chewing gum on primary and permanent teeth. Methods: Thirty primary and 30 permanent molar extracted teeth were painted with acid resistant varnish except a small window over buccal surface. Teeth were divided into four groups according to type of teeth and type of chewing gum (Center fresh and Bubbaloo) (D1, P1, D2 and P2); each tooth was exposed to whole chewing gum mashed with 5 ml of artificial saliva for five minutes at room temperature twice a day for 5 days. After the exposure, teeth were stored in deionized water and submitted for microhardness tests. Results: Paired t-test and independent sample t-test were used for statistical analysis. A significant reduction in microhardness was found between exposed and unexposed areas in all groups. There was no statistically significant difference in reduction of microhardness to chewing gums, and between primary and permanent enamel. Conclusion: There is a definite reduction in microhardness in all groups exposed to chewing gums. Both the chewing gums are equally erosive; both permanent and primary teeth were affected. How to cite this article: Mudumba VL, Muppa R, Srinivas NCH, Kumar DM. Evaluation and Comparison of Changes in Microhardness of Primary and Permanent Enamel on Exposure to Acidic Center-filled Chewing Gum: An in vitro Study. Int J Clin Pediatr Dent 2014;7(1):24-29. PMID:25206233

[Influence of Coca-Cola on early erosion and surface microhardness of human enamel: an in situ study].

PubMed

Yuan, M; Zhang, Q; Gao, X J

2016-06-01

Assessed the effect of single dose attack of Coca-Cola on early erosion and surface microhardness of permanent human enamel, in order to provide diet instructions on minimum amount and frequency of carbonated beverage consumption. Eighty enamel slabs were prepared out of 10 extracted human mandibular third molars, and distributed into 8 groups with randomized block design(n=10). Ten generally healthy volunteers with normal saliva secretion wore acrylic palatal appliances containing 2 enamel slabs, with formation of a salivary pellicle 2 h ahead. The volunteers were instructed to drink 100 ml fresh Coca-Cola within 20 s. And then the alterations of the enamel slabs were measured using a Vicker's microhardness tester at 1, 2, 4, 6, 8, 10, 20 and 30 min after the consumption of Coca-Cola. For each volunteer, the experiment was carried out in four days, 2 samples were examined each time. Data were analyzed using Kruskal-Wallis and Wilcoxon tests(α =0.05). Significant decreases in surface microhardness(SMH)were observed in each time point(P<0.01). The percentages of surface microhardness changes on each exposure time were(12.2±3.9)%,(16.8±5.5)%,(16.7±5.6)%,(16.2±6.2)%,(16.6±9.0)%,(15.6±3.7)%,(13.8±4.8)% and(11.4±3.2)%, respectively. Significant differences were observed between G1 min and G2-8 min(P=0.029), G2-8 min and G30 min(P=0.008). Single intake of 100 ml Coca-Cola could lead to significant decrease of enamel microhardness and initiate erosion of enamel surface. Enamel surface microhardness decreased to the lowest points at 2-8 min, and began to recover after 10 min. The enamel surface microhardness could not fully recovered to the baseline level in 30 min if no intervention was performed.

Graphene-enabled electron microscopy and correlated super-resolution microscopy of wet cells.

PubMed

Wojcik, Michal; Hauser, Margaret; Li, Wan; Moon, Seonah; Xu, Ke

2015-06-11

The application of electron microscopy to hydrated biological samples has been limited by high-vacuum operating conditions. Traditional methods utilize harsh and laborious sample dehydration procedures, often leading to structural artefacts and creating difficulties for correlating results with high-resolution fluorescence microscopy. Here, we utilize graphene, a single-atom-thick carbon meshwork, as the thinnest possible impermeable and conductive membrane to protect animal cells from vacuum, thus enabling high-resolution electron microscopy of wet and untreated whole cells with exceptional ease. Our approach further allows for facile correlative super-resolution and electron microscopy of wet cells directly on the culturing substrate. In particular, individual cytoskeletal actin filaments are resolved in hydrated samples through electron microscopy and well correlated with super-resolution results.

Laser surface alloying of FeCoCrAlNi high-entropy alloy on 304 stainless steel to enhance corrosion and cavitation erosion resistance

NASA Astrophysics Data System (ADS)

Zhang, S.; Wu, C. L.; Zhang, C. H.; Guan, M.; Tan, J. Z.

2016-10-01

FeCoCrAlNi high-entropy alloy coating was synthesized with premixed high-purity Co, Cr, Al and Ni powders on 304 stainless steel by laser surface alloying, aiming at improving corrosion and cavitation erosion resistance. Phase constituents, microstructure and microhardness were investigated using XRD, SEM, and microhardness tester, respectively. The cavitation erosion and electrochemical corrosion behavior of FeCoCrAlNi coating in 3.5% NaCl solution were also evaluated using an ultrasonic vibrator and potentiodynamic polarization measurement. Experimental results showed that with appropriate laser processing parameters, FeCoCrAlNi coating with good metallurgical bonding to the substrate could be achieved. FeCoCrAlNi coating was composed of a single BCC solid solution. The formation of simple solid solutions in HEAs was the combined effect of mixing entropy (ΔSmix), mixing enthalpy (ΔHmix), atom-size difference (δ) and valence electron concentration (VEC), and the effect of ΔSmix was much larger than that of the other factors. The microhardness of the FeCoCrAlNi coating was ~3 times that of the 304 stainless steel. Both the corrosion and cavitation erosion resistance of the coating were improved. The cavitation erosion resistance for FeCoCrAlNi HEA coating was ~7.6 times that of 304 stainless steel. The corrosion resistance was also improved as reflected by a reduction in the current density of one order of magnitude as compared with 304 stainless steel.

Effect of generation 4.0 polyamidoamine dendrimer on the mineralization of demineralized dentinal tubules in vitro.

PubMed

Jia, Ru; Lu, Yi; Yang, Chang-Wei; Luo, Xiao; Han, Ying

2014-10-01

Dentine hypersensitivity is a type of clinical oral disease, which is highly prevalent worldwide. Although there are many materials to treat dentine hypersensitivity, their long-term therapeutic effects are not satisfactory. Therefore, the aim of this research was to observe and identify the biological mineralization of the generation 4.0 polyamidoamine dendrimer on the demineralized dentinal tubules at different time points. 2mm-thick slices were obtained from the cemento-enamel junction of 36 third molar teeth that simulated the condition of sensitivity with acid etching. Slices were treated with generation 4.0 polyamidoamine dendrimer and peptide bond condensing agent, while no treatment was applied on the slices of the control group. Following immersion in artificial saliva for 2, 4, 6, and 8 weeks respectively, the mineralization condition of dentine slices was observed using the scanning electron microscope (SEM). In addition, the differences in the samples of dental slices between the 2 groups were also detected using the microhardness test. SEM results showed that the average diameter and density of the dentinal tubules in the experimental group were significantly lower than those in the control group (P<0.001). The microhardness test exhibited a similar result, which suggested that the microhardness of the experimental group was significantly higher than the control group (P<0.001). Generation 4.0 polyamidoamine dendrimer promotes the biomineralization of demineralized dentinal tubules. Moreover, this result also suggests that the 4.0th generation polyamidoamine dendrimer has the potential value for dentine hypersensitivity treatment. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of gamma irradiation on the wear behavior of human tooth dentin.

PubMed

Qing, Ping; Huang, Shengbin; Gao, ShanShan; Qian, LinMao; Yu, HaiYang

2016-12-01

The objective of this study was to evaluate the effect of gamma irradiation on the wear behavior of human tooth dentin in terms of possible alterations in crystallinity, grain size, and composition. Human premolars (n = 19) were collected to obtain the perpendicular or parallel to the direction of the dentin tubule specimens. Each specimen was subjected to 60 Gy of gamma irradiation, in daily increments of 2 Gy. The nanoscratch tests were conducted. The scratch traces were observed via scanning electron microscope (SEM) and surface profilometer. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) were used to investigate the alteration of crystallography and chemical composition of dentin after irradiation. The change of surface microhardness (SMH) was also evaluated. The nanoscratch results showed that the friction coefficient of dentin after irradiation became higher, and the depths and widths of scratch were greater than that of dentin before irradiation. Additionally, irradiation decreased the crystallinity of dentin and induced the formation of bigger crystals. The carbonate/mineral ratio was increased. Furthermore, a significant reduction in microhardness after irradiation was observed. The main damage mechanisms consisted of the formation of delamination and crack in both the specimens cut perpendicular and parallel to tubule dentin after irradiation. Irradiation affected directly the wear behavior of tooth dentin, accompanied by the alterations in crystallography, chemical composition, and surface microhardness of dentin. This would help extend understanding the influence of irradiation on dentin and provide suggestions for selecting more suitable materials for irradiated tooth.

Evaluation of crystalline changes and resistance to demineralization of the surface of human dental enamel treated with Er:YAG laser and fluoride using x-ray diffraction analysis and Vickers microhardness

NASA Astrophysics Data System (ADS)

Behroozibakhsh, Marjan; Shahabi, Sima; Ghavami-Lahiji, Mehrsima; Sadeghian, Safura; Sadat Faal Nazari, Neda

2018-06-01

This study aimed to investigate the changes in crystalline structure and resistance to demineralization of human dental surface enamel treated with erbium-doped yttrium aluminium garnet laser (Er:YAG) laser and fluoride. The enamel surfaces were divided into four groups according to the treatment process including, (L): irradiated with Er:YAG; (F): treated with acidulated phosphate fluoride gel (LF): Pre-irradiated surfaces with Er:YAG subjected to acidulated phosphate fluoride gel and (FL): laser irradiation was performed on the fluoridated enamel surface. Before and after the treatment procedure, the samples were evaluated using X-ray diffraction, scanning electron microscope (SEM) and the Vickers microhardness test. The surface microhardness values also were measured after a pH-cycling regime and acid challenge. The a-axis of all lased groups was contracted after treatment procedure. Measurement of the area under the peaks showed the highest crysallinity in the FL group. The hardness values of all laser treated samples significantly reduced after treatment procedure compared to the F group (p  ⩽  0.001). The morphological observations showed remarkable changes on the lased enamel surfaces including cracks, craters and exposed prisms. These findings suggest, irradiation of the Er:YAG laser accompanying with fluoride application can induce some beneficial crystalline changes regarding the acid-resistance properties of enamel, however, the craters and cracks produced by laser irradiation can promote enamel demineralization and consequently the positive effects of the Er:YAG laser will be eliminated.

Effect of flavonoids on remineralization of artificial root caries.

PubMed

Epasinghe, D J; Yiu, Cky; Burrow, M F

2016-06-01

This study compared the effects of three flavonoids, including proanthocyanidin, naringin and quercetin on remineralization of artificial root caries. Demineralized root fragments (n = 75) were randomly divided into five groups for treatment with the remineralizing agents for 10 minutes: (1) 6.5% proanthocyanidin; (2) 6.5% naringin; (3) 6.5% quercetin; (4) 1000 ppm fluoride; and (5) deionized water (control). The demineralized samples were pH-cycled through treatment solutions, acidic buffer and neutral buffer for eight days at six cycles per day. The remineralization effects were evaluated using Knoop microhardness, transverse microradiography (lesion depth and mineral loss) and confocal laser scanning microscopy. Microhardness at different lesion depths was analysed with two-way ANOVA and Tukey's test, while lesion depths and mineral loss were analysed with one-way ANOVA and Tukey's test. Artificial caries lesions treated with fluoride and flavonoids showed significantly greater hardness than the control group (p < 0.05). Both lesion depths and mineral loss of the flavonoid treated groups were significantly lower than the control group (p < 0.05), but significantly higher than the fluoride treated group. No significant difference in lesion depth and mineral loss was found among the three flavonoids (p > 0.05). All three flavonoids showed positive effects on artificial root caries remineralization, which are significantly lower than that of 1000 ppm fluoride. © 2016 Australian Dental Association.

Scanning ultrafast electron microscopy.

PubMed

Yang, Ding-Shyue; Mohammed, Omar F; Zewail, Ahmed H

2010-08-24

Progress has been made in the development of four-dimensional ultrafast electron microscopy, which enables space-time imaging of structural dynamics in the condensed phase. In ultrafast electron microscopy, the electrons are accelerated, typically to 200 keV, and the microscope operates in the transmission mode. Here, we report the development of scanning ultrafast electron microscopy using a field-emission-source configuration. Scanning of pulses is made in the single-electron mode, for which the pulse contains at most one or a few electrons, thus achieving imaging without the space-charge effect between electrons, and still in ten(s) of seconds. For imaging, the secondary electrons from surface structures are detected, as demonstrated here for material surfaces and biological specimens. By recording backscattered electrons, diffraction patterns from single crystals were also obtained. Scanning pulsed-electron microscopy with the acquired spatiotemporal resolutions, and its efficient heat-dissipation feature, is now poised to provide in situ 4D imaging and with environmental capability.

Water Droplet Erosion Behavior of High-Power Diode Laser Treated 17Cr4Ni PH Stainless Steel

NASA Astrophysics Data System (ADS)

Mann, B. S.

2014-05-01

This article deals with water droplet erosion (WDE) behavior of high-power diode laser (HPDL) treated 17Cr4Ni PH stainless steel. After HPDL treatment, the water droplet erosion resistance (WDER) of 17Cr4Ni PH stainless steel has not improved. The main reason is the surface hardness, which has not improved after HPDL treatment though the microstructure has become much finer. On the other hand, precipitation hardening of the alloy at 490°C for 3 h has resulted in improved WDER more than twice. This is because of its increased microhardness and improved modified ultimate resilience (MUR), and formation of fine grained microstructure. The WDER has been correlated with MUR, a single mechanical property, based upon microhardness, ultimate tensile strength, and Young's modulus. WDERs of HPDL treated, untreated, and precipitation hardened 17Cr4Ni PH stainless steel samples were determined using a WDE test facility as per ASTM G73-1978. The WDE damage mechanism, compared on the basis of MUR and scanning electron micrographs, is discussed and reported in this article.

Laser texturing of Hastelloy C276 alloy surface for improved hydrophobicity and friction coefficient

NASA Astrophysics Data System (ADS)

Yilbas, B. S.; Ali, H.

2016-03-01

Laser treatment of Hastelloy C276 alloy is carried out under the high pressure nitrogen assisting gas environment. Morphological and metallurgical changes in the laser treated layer are examined using the analytical tools including, scanning electron and atomic force microscopes, X-ray diffraction, energy dispersive spectroscopy, and Fourier transform infrared spectroscopy. Microhardness is measured and the residual stress formed in the laser treated surface is determined from the X-ray data. The hydrophibicity of the laser treated surface is assessed using the sessile drop method. Friction coefficient of the laser treated layer is obtained incorporating the micro-tribometer. It is found that closely spaced laser canning tracks create a self-annealing effect in the laser treated layer and lowers the thermal stress levels through modifying the cooling rates at the surface. A dense structure, consisting of fine size grains, enhances the microhardness of the surface. The residual stress formed at the surface is compressive and it is in the order of -800 MPa. Laser treatment improves the surface hydrophobicity significantly because of the formation of surface texture composing of micro/nano-pillars.

Metallography studies and hardness measurements on ferritic/martensitic steels irradiated in STIP

NASA Astrophysics Data System (ADS)

Zhang, H.; Long, B.; Dai, Y.

2008-06-01

In this work metallography investigations and microhardness measurements have been performed on 15 ferritic/martensitic (FM) steels and 6 weld metals irradiated in the SINQ Target Irradiation Program (STIP). The results demonstrate that all the steels have quite similar martensite lath structures. However, the sizes of the prior austenite grain (PAG) of these steels are quite different and vary from 10 to 86 μm. The microstructure in the fusion zones (FZ) of electron-beam welds (EBWs) of 5 steels (T91, EM10, MANET-II, F82H and Optifer-IX) is similar in respect to the martensite lath structure and PAG size. The FZ of the inert-gas-tungsten weld (TIGW) of the T91 steel shows a duplex structure of large ferrite gains and martensite laths. The microhardness measurements indicate that the normalized and tempered FM steels have rather close hardness values. The unusual high hardness values of the EBW and TIGW of the T91 steel were detected, which suggests that these materials are without proper tempering or post-welding heat treatment.

Effect of medium on friction and wear properties of compacted graphite cast iron processed by biomimetic coupling laser remelting process

NASA Astrophysics Data System (ADS)

Guo, Qing-chun; Zhou, Hong; Wang, Cheng-tao; Zhang, Wei; Lin, Peng-yu; Sun, Na; Ren, Luquan

2009-04-01

Stimulated by the cuticles of soil animals, an attempt to improve the wear resistance of compact graphite cast iron (CGI) with biomimetic units on the surface was made by using a biomimetic coupled laser remelting process in air and various thicknesses water film, respectively. The microstructures of biomimetic units were examined by scanning electron microscope and X-ray diffraction was used to describe the microstructure and identify the phases in the melted zone. Microhardness was measured and the wear behaviors of biomimetic specimens as functions of different mediums as well as various water film thicknesses were investigated under dry sliding condition, respectively. The results indicated that the microstructure zones in the biomimetic specimens processed with water film are refined compared with that processed in air and had better wear resistance increased by 60%, the microhardness of biomimetic units has been improved significantly. The application of water film provided finer microstructures and much more regular grain shape in biomimetic units, which played a key role in improving the friction properties and wear resistance of CGI.

Layer growth kinetics and wear resistance of martensitic precipitation hardening stainless steel plasma nitrocarburized at 460°C with rare earth addition

NASA Astrophysics Data System (ADS)

Liu, R. L.; Qiao, Y. J.; Yan, M. F.; Fu, Y. D.

2013-09-01

To study the effect of rare earth (RE) addition on low temperature plasma nitrocarburizing of martensitic precipitation hardening stainless steel, 17-4PH stainless steel was plasma nitrocarburized at 460 °C for different times with RE addition. The modified layers were tested by optical microscope, scanning electron microscope, X-ray diffraction, microhardness tester and pin-on-disc tribometer. The experimental results show that the layer depth of plasma RE nitrocarburized layer can be increased up to 56% compared with plasma nitrocarburizing without RE addition. Incorporation of RE element is beneficial to the formation of nitrogen and carbon expanded martensite (α'N). The surface microhardness of plasma RE nitrocarburized layer can be increased to 1286 HV and higher up to 80 HV than that obtained from the conventional treated one. The friction coefficient of martensitic stainless steel can be dramatically decreased by low temperature plasma nitrocarburizing with RE addition, and the friction coefficient of the modified specimens decrease gradually with increasing process time in the present test condition.

High-Resolution of Electron Microscopy of Montmorillonite and Montmorillonite/Epoxy Nanocomposites

DTIC Science & Technology

2005-01-01

AFRL-ML-WP-TP-2006-464 HIGH-RESOLUTION OF ELECTRON MICROSCOPY OF MONTMORILLONITE AND MONTMORILLONITE /EPOXY NANOCOMPOSITES Lawrence F...HIGH-RESOLUTION OF ELECTRON MICROSCOPY OF MONTMORILLONITE AND MONTMORILLONITE /EPOXY NANOCOMPOSITES 5c. PROGRAM ELEMENT NUMBER 62102F 5d...transmission electron microscopy the structure and morphology of montmorillonite (MMT), a material of current interest for use in polymer nanocomposites, was

Correlative fluorescence microscopy and scanning transmission electron microscopy of quantum-dot-labeled proteins in whole cells in liquid.

PubMed

Dukes, Madeline J; Peckys, Diana B; de Jonge, Niels

2010-07-27

Correlative fluorescence microscopy and transmission electron microscopy (TEM) is a state-of-the-art microscopy methodology to study cellular function, combining the functionality of light microscopy with the high resolution of electron microscopy. However, this technique involves complex sample preparation procedures due to its need for either thin sections or frozen samples for TEM imaging. Here, we introduce a novel correlative approach capable of imaging whole eukaryotic cells in liquid with fluorescence microscopy and with scanning transmission electron microscopy (STEM); there is no additional sample preparation necessary for the electron microscopy. Quantum dots (QDs) were bound to epidermal growth factor (EGF) receptors of COS7 fibroblast cells. Fixed whole cells in saline water were imaged with fluorescence microscopy and subsequently with STEM. The STEM images were correlated with fluorescence images of the same cellular regions. QDs of dimensions 7x12 nm were visible in a 5 microm thick layer of saline water, consistent with calculations. A spatial resolution of 3 nm was achieved on the QDs.

Correlative Fluorescence Microscopy and Scanning Transmission Electron Microscopy of Quantum Dot Labeled Proteins in Whole Cells in Liquid

PubMed Central

Dukes, Madeline J.; Peckys, Diana B.; de Jonge, Niels

2010-01-01

Correlative fluorescence microscopy and transmission electron microscopy (TEM) is a state-of-the-art microscopy methodology to study cellular function, combining the functionality of light microscopy with the high resolution of electron microscopy. However, this technique involves complex sample preparation procedures due to its need for either thin sections or frozen samples for TEM imaging. Here, we introduce a novel correlative approach capable of imaging whole eukaryotic cells in liquid with fluorescence microscopy and with scanning transmission electron microscopy (STEM); there is no additional sample preparation necessary for the electron microscopy. Quantum dots (QDs) were bound to epidermal growth factor (EGF) receptors of COS7 fibroblast cells. Fixed whole cells in saline water were imaged with fluorescence microscopy and subsequently with STEM. The STEM images were correlated with fluorescence images of the same cellular regions. QDs of dimensions 7 × 12 nm were visible in a 5 μm thick layer of saline water, consistent with calculations. A spatial resolution of 3 nm was achieved on the QDs. PMID:20550177

In Vitro Comparative Study of Two Different Bleaching Agents on Micro-hardness Dental Enamel.

PubMed

Fatima, Nazish; Ali Abidi, Syed Yawar; Meo, Ashraf Ali

2016-02-01

To evaluate the effect of home-use bleaching agent containing 16% Carbamide Peroxide (CP) and in-office bleaching agent containing 38% Hydrogen Peroxide (HP) on enamel micro-hardness. An in vitroexperimental study. Department of Operative Dentistry and Science of Dental Materials at Dr. Ishrat-ul-Ebad Khan Institute of Oral Health Sciences, Dow University of Health Sciences and Material Engineering Department of NED University of Engineering and Technology, Karachi, from July to December 2014. Atotal of 90 enamel slabs from 45 sound human 3rd molar were randomly divided into 3 groups. Each group contained 30 specimens (n=30). Group 1 was kept in artificial saliva at 37°C in incubator during the whole experiment. However, Groups 2 and 3 were treated with power whitening gel and tooth whitening pen respectively. After bleaching session, specimens were thoroughly rinsed with deionized water again for 10 seconds and then stored in artificial saliva at 37°C in incubator. Artificial saliva was changed after every 2 days. The Vickers hardness tester (Wolpert 402 MVD, Germany) was adjusted to a load of 0.1 kg (100 gm) and dwell time of 5 seconds. Three Vickers were performed on each specimen using a hardness tester according to the ISO 6507-3:1998 specification. Micro-hardness measurements were performed before and after bleaching at day 1, 7 and 14. In the control group, the baseline micro-hardness was 181.1 ±9.3 which was reduced after the storage on day 1, 7 and 14 (p = 0.104). In Group 2, baseline micro-hardness was 180.4 ±10.1 which was reduced to 179.79 ±10.0 units after day 1. Whereas, on day 7 and 14, the values of micro-hardness were 179.8 ±10 and 179.7 ±10.29, respectively (p=0.091). Furthermore, the baseline micro-hardness in Group 3 was 174.0 ±22.9 units which was reduced to 173 ±23 on day 1, 170 ±30 on day 7 and 173 ±23 on day 14 (p = 0.256). The statistically insignificant difference was found among micro-hardness values of different bleaching agents (p = 0.118). Bleaching with 38% Hydrogen Peroxide (HP) and 16% Carbamide Peroxide (CP) resulted in insignificant effect on surface micro-hardness of enamel.

Evaluation of the effect of a home bleaching agent on surface characteristics of indirect esthetic restorative materials--part II microhardness.

PubMed

Torabi, Kianoosh; Rasaeipour, Sasan; Ghodsi, Safoura; Khaledi, Amir Ali Reza; Vojdani, Mahroo

2014-07-01

The exponential usage of esthetic restorative materials is beholden to society needs and desires. Interaction between the bleaching agents and the esthetic restorative materials is of critical importance. This in vitro study has been conducted to evaluate the effect of a home bleaching agent, carbamide peroxide (CP) 38%, on the microhardness of the fiber reinforced composite (FRC), overglazed, autoglazed, or polished porcelain specimens. For overglazed, autoglazed, polished ceramics and also FRC cylindrical specimens (n = 20 per group) were prepared. The specimens were stored in distilled water at 37°C for 48 hours prior to testing. Six samples from each group were selected randomly as negative controls which were stored in distilled water at 37°C that was changed daily. CP 38% was applied on the test specimens for 15 minutes, twice a day for 14 days. By using Knoop-microhardness tester microhardness testing for baseline, control and test specimens was conducted. Data were statistically analyzed using paired t-test, Mann-Whitney test, and Kruskal-Wallis test. Home bleaching significantly decreased the surface microhardness of all the test samples (p < 0.05), whereas the control groups did not show statistically significant changes after 2 weeks. The polished porcelain and polished composite specimens showed the most significant change in microhard-ness after bleaching process (p < 0.05). Although the type of surface preparation affects the susceptibility of the porcelain surface to the bleaching agent, no special preparation can preclude such adverse effects. The contact of home bleaching agents with esthetic restorative materials is unavoidable. Therefore protecting these restorations from bleaching agents and reglazing or at least polishing the restorations after bleaching is recommended.

Comparative evaluation of two different remineralizing agents on the microhardness of bleached enamel surface: Results of an in vitro study.

PubMed

Kaur, Gunpriya; Sanap, Anita U; Aggarwal, Shalini D; Kumar, Tanaya

2015-01-01

Various agents are studied for their remineralization potential. To evaluate the effect of GC Tooth Mousse and Toothmin Tooth Cream on microhardness of bleached enamel. In vitro- study. Twenty freshly extracted anterior teeth were cut sagittally and impregnated in cold cure acrylic resin. Specimens were kept in artificial saliva to prevent from dehydration. After measuring baseline hardness, teeth were randomly divided into two groups. Everbrite In - Office Tooth whitening kit (Dentamerica) was used to demineralize the teeth following which hardness was measured again. Teeth in group one (n=10) and group two (n=10) were treated with GC tooth mousse (Recaldent) and Toothmin tooth cream (Abbott Healthcare Pvt.Ltd) daily for seven days and microhardness of enamel surface was measured. Mean, SD, and percentage change in the microhardness were calculated. Student's paired t-test was used to evaluate the signifi cance of change from initial, after bleaching for 5 min and after 1-week remineralization Unpaired't' test was used to compare difference between groups. Microhardness significantly decreased in both groups after bleaching (% change group one: 3.24% group two: 3.26% in group; P<0.01 in both groups). Both products significantly increased mineralization after seven days of treatment (P<0.01). Remineralization was numerically better in Toothmin group (Abbott Healthcare Pvt.Ltd ) compared to GC Mousse(Recaldent) (% change 3.27% vs 6.34%). However, difference was not significant (P >0.05). Both GC Tooth Mousse (Recaldent) and Toothmin Tooth cream (Abbott Healthcare Pvt.Ltd) increase the microhardness of bleached enamel. Toothmin tooth cream is a better agent for increasing microhardness, although difference is not significant.

Effect of light irradiation on tooth whitening: enamel microhardness and color change.

PubMed

Gomes, Mauricio Neves; Francci, Carlos; Medeiros, Igor Studart; De Godoy Froes Salgado, Nívea Regina; Riehl, Heraldo; Marasca, José Milton; Muench, Antônio

2009-01-01

The aim of this study was to evaluate the influence of light exposure associated with 35% hydrogen peroxide (Pola Office, SDI, Melbourne, Vic., Australia) or 15% hydrogen peroxide (BriteSmile, Discus, Culver City, CA, USA) on the microhardness and color changes of bovine enamel. Experimental groups were Britesmile + Light (BL) (15% hydrogen peroxide + plasm arc; 4 x 20 minutes), Britesmile + No Light (BN) (BL, no light), Pola office + Light (PL) (35% hydrogen peroxide + LED; 4 x 8 minutes), and Pola office + No light (PN) (PL, no light). Color changes (DeltaE) and the CIELAB (Commission Internationale de l' Eclairage, L* a* b* color system) parameters (L*, a*, and b*) were assessed with a spectrophotometer before (B), immediately (A), 1 day and 7 days after bleaching. The microhardness was measured before (B) and after (A), the obtained data were submitted to a two-way analysis of variance, and DeltaE were submitted to t-test for each period. Only Pola Office, in which the peroxide is associated with the light, improved DeltaE when evaluated immediately after bleaching (p < 0.001). Light exposure did not influence DeltaE after 1 day or 7 days for either bleaching system. The enamel microhardness was not altered after bleaching for BriteSmile. However, enamel microhardness was reduced after bleaching for Pola Office, 283 MPa (+/-21) and 265 MPa (+/-27), respectively. It was concluded that these two bleaching systems were efficient regardless of the light systems used. However, the 35% hydrogen peroxide altered the enamel microhardness. CLINICAL SIGNIFICANCE Enamel microhardness was affected by a 35% hydrogen peroxide in-office bleaching therapy. Moreover, the in-office bleaching outcome was not improved by using the light associated with systems tested in this study. (J Esthet Restor Dent 21:387-396, 2009).

Effect of super-oxidized water, sodium hypochlorite and EDTA on dentin microhardness.

PubMed

Ghisi, Alexandre Corrêa; Kopper, Patrícia Maria Poli; Baldasso, Flávia E R; Stürmer, Caroline P; Rossi-Fedele, Giampiero; Steier, Liviu; Figueiredo, José Antonio Poli de; Morgental, Renata Dornelles; Vier-Pelisser, Fabiana Vieira

2014-01-01

The present study aimed to evaluate the influence of the following irrigating solutions on the microhardness of root canal dentin: 2% sodium hypochlorite (2NaOCl), 5% sodium hypochlorite (5NaOCl), super-oxidized water (400 ppm Sterilox - Sx) and 17% EDTA (E). Eighty roots from bovine incisors were randomly divided into 8 groups (n=10): 2NaOCl, 5NaOCl, Sx, and 2NaOCl + E, 5NaOCl + E, Sx + E (associated with E as final irrigant for 5 min), E solely and distilled water (dH2O) as the negative control. Root canal preparation was performed by hand instruments, using one of the irrigation protocols for 30 min. Then, 5 mm of the cervical root third were cut out from each sample and subjected to the Vickers microhardness test, at two points, one at approximately 500-1000 µm from the root canal lumen (distance 1), and the other at approximately 500-1000 µm from the external root surface (distance 2). Data were analyzed by Wilcoxon and Kruskal-Wallis tests at 5% significance level. Microhardness values at distance 1 were significantly lower than those at distance 2 for all groups, except 5NaOCl and 5NaOCl + E groups (p>0.05). EDTA showed the lowest microhardness values. However, no statistically significant difference was detected among groups at distance 1 and EDTA was significantly different only from Sx at distance 2. In conclusion, all tested solutions showed lower microhardness at the most superficial root canal dentin layer compared to the one found near the external root surface, except 5NaOCl and 5NaOCl + E; EDTA promoted lower microhardness values in comparison to Sterilox at this site.

Evaluation of Polymerization Efficacy in Composite Resins via FT-IR Spectroscopy and Vickers Microhardness Test.

PubMed

Jafarzadeh, Tahereh-Sadat; Erfan, Mohammad; Behroozibakhsh, Marjan; Fatemi, Mostafa; Masaeli, Reza; Rezaei, Yashar; Bagheri, Hossein; Erfan, Yasaman

2015-01-01

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vickers microhardness testing at two different depths (top surface, 2 mm). Materials and methods. For FT-IR spectrometry, five cylindrical specimens (5mm in diameter × 2 mm in length) were prepared from each composite resin using Teflon molds and polymerized for 20 seconds. Then, 70-μm wafers were sectioned at the top surface and at2mm from the top surface. The degree of conversion for each sample was calculated using FT-IR spectroscopy. For Vickers micro-hardness testing, three cylindrical specimens were prepared from each composite resin and polymerized for 20 seconds. The Vickers microhardness test (Shimadzu, Type M, Japan) was performed at the top and bottom (depth=2 mm) surfaces of each specimen. Three-way ANOVA with independent variables and Tukey tests were performed at 95% significance level. Results. No significant differences were detected in degree of conversion and microhardness between LED and QTH light-curing units except for the ormocer-based specimen, CeramX, which exhibited significantly higher DC by LED. All the composite resins showed a significantly higher degree of conversion at the surface. Microhardness was not significantly affected by depth, except for Herculite XRV Ultra and CeramX, which showed higher values at the surface. Conclusion. Composite resins containing nano-particles generally exhibited more variations in degree of conversion and microhardness.

The role of fluoride and chlorhexidine in preserving hardness and mineralization of enamel and cementum after gamma irradiation.

PubMed

Abdalla, Rowida; Niazy, Maha A; Jamil, Wael E; Hazzaa, Hala A; Elbatouti, Amal A

2017-05-01

The purpose of this study was to evaluate the effect of 0.05% sodium fluoride and 0.12% chlorhexidine mouthwashes on the micro-hardness of tooth enamel and cementum that was exposed to therapeutic doses of gamma radiation. Sixty extracted human teeth were divided into two groups, one was irradiated, the other was not irradiated. The two groups were further subdivided into three subgroups, which were each treated either with 0.05% sodium fluoride or with 0.12% chlorhexidine; the third subgroup served as a control. After demineralization-remineralization cycling, teeth from the irradiated groups showed a significantly lower micro-hardness when compared to those from the non-irradiated groups. Both in the irradiated and non-irradiated groups, teeth from the control subgroups showed a significantly lower micro-hardness, as compared to teeth treated with sodium fluoride and chlorhexidine. For non-irradiated enamel samples, those treated with chlorhexidine showed a significantly less micro-hardness compared to those treated with sodium fluoride. In contrast, irradiated enamel showed no significant difference in micro-hardness, whatever treatment (chlorhexidine or sodium fluoride) was applied. For cementum, treatment with chlorhexidine resulted in a significantly lower micro-hardness compared to sodium fluoride, both for the irradiated and non-irradiated groups. It is concluded that gamma irradiation with therapeutic doses typically used for head and neck carcinoma treatment has a direct effect in reducing micro-hardness of tooth enamel and cementum. Mouthwash protocols including, for example, application of 0.05% sodium fluoride or 0.12% chlorhexidine three times per day for 6 weeks, can protect enamel and cementum against the reduction in hardness and demineralization caused by gamma irradiation. Sodium fluoride offers more protection compared to chlorhexidine.

Effects of curing protocol and storage time on the micro-hardness of resin cements used to lute fiber-reinforced resin posts

PubMed Central

RAMOS, Marcelo Barbosa; PEGORARO, Thiago Amadei; PEGORARO, Luiz Fernando; CARVALHO, Ricardo Marins

2012-01-01

Objectives To determine the micro-hardness profile of two dual cure resin cements (RelyX - U100®, 3M-ESPE and Panavia F 2.0®, Kuraray) used for cementing fiber-reinforced resin posts (Fibrekor® - Jeneric Pentron) under three different curing protocols and two water storage times. Material and methods Sixty 16mm long bovine incisor roots were endodontically treated and prepared for cementation of the Fibrekor posts. The cements were mixed as instructed, dispensed in the canal, the posts were seated and the curing performed as follows: a) no light activation; b) light-activation immediately after seating the post, and; c) light-activation delayed 5 minutes after seating the post. The teeth were stored in water and retrieved for analysis after 7 days and 3 months. The roots were longitudinally sectioned and the microhardness was determined at the cervical, middle and apical regions along the cement line. The data was analyzed by the three-way ANOVA test (curing mode, storage time and thirds) for each cement. The Tukey test was used for the post-hoc analysis. Results Light-activation resulted in a significant increase in the microhardness. This was more evident for the cervical region and for the Panavia cement. Storage in water for 3 months caused a reduction of the micro-hardness for both cements. The U100 cement showed less variation in the micro-hardness regardless of the curing protocol and storage time. Conclusions The micro-hardness of the cements was affected by the curing and storage variables and were material-dependent. PMID:23138743

Evaluation of Polymerization Efficacy in Composite Resins via FT-IR Spectroscopy and Vickers Microhardness Test

PubMed Central

Jafarzadeh, Tahereh-Sadat; Erfan, Mohammad; Behroozibakhsh, Marjan; Fatemi, Mostafa; Masaeli, Reza; Rezaei, Yashar; Bagheri, Hossein; Erfan, Yasaman

2015-01-01

Background and aims. Polymerization efficacy affects the properties and performance of composite resin restorations.The purpose of this study was to evaluate the effectiveness of polymerization of two micro-hybrid, two nano-hybrid and one nano-filled ormocer-based composite resins, cured by two different light-curing systems, using Fourier transformation infrared (FT-IR) spectroscopy and Vickers microhardness testing at two different depths (top surface, 2 mm). Materials and methods. For FT-IR spectrometry, five cylindrical specimens (5mm in diameter × 2 mm in length) were prepared from each composite resin using Teflon molds and polymerized for 20 seconds. Then, 70-μm wafers were sectioned at the top surface and at2mm from the top surface. The degree of conversion for each sample was calculated using FT-IR spectroscopy. For Vickers micro-hardness testing, three cylindrical specimens were prepared from each composite resin and polymerized for 20 seconds. The Vickers microhardness test (Shimadzu, Type M, Japan) was performed at the top and bottom (depth=2 mm) surfaces of each specimen. Three-way ANOVA with independent variables and Tukey tests were performed at 95% significance level. Results. No significant differences were detected in degree of conversion and microhardness between LED and QTH light-curing units except for the ormocer-based specimen, CeramX, which exhibited significantly higher DC by LED. All the composite resins showed a significantly higher degree of conversion at the surface. Microhardness was not significantly affected by depth, except for Herculite XRV Ultra and CeramX, which showed higher values at the surface. Conclusion. Composite resins containing nano-particles generally exhibited more variations in degree of conversion and microhardness. PMID:26889359

Electrochemical and Dry Sand Impact Erosion Studies on Carbon Steel

PubMed Central

Naz, M. Y.; Ismail, N. I.; Sulaiman, S. A.; Shukrullah, S.

2015-01-01

This study investigated the dry and aqueous erosion of mild steel using electrochemical and dry sand impact techniques. In dry sand impact experiments, mild steel was eroded with 45 μm and 150 μm sand particles. Scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX) and micro-hardness techniques were used to elaborate the surface morphology of the eroded samples. The results revealed significant change in morphology of the eroded samples. In-depth analysis showed that although the metal erosion due to larger particles was significantly higher, the fines also notably damaged the metal surface. The surface damages were appreciably reduced with decrease in impact angle of the accelerated particles. The maximum damages were observed at an impact angle of 90°. The hardness of the samples treated with 45 μm and 150 μm sand remained in the range of 88.34 to 102.31 VHN and 87.7 to 97.55 VHN, respectively. In electrochemical experiments, a triple electrode probe was added into the metal treatment process. The linear polarization resistance (LPR) measurements were performed in slurries having 5% (by weight) of sand particles. LPR of the samples treated with 45 μm and 150 μm sand slurries was calculated about 949 Ω.cm2 and 809 Ω.cm2, respectively. PMID:26561231

Effect of welding process on the microstructure and properties of dissimilar weld joints between low alloy steel and duplex stainless steel

NASA Astrophysics Data System (ADS)

Wang, Jing; Lu, Min-xu; Zhang, Lei; Chang, Wei; Xu, Li-ning; Hu, Li-hua

2012-06-01

To obtain high-quality dissimilar weld joints, the processes of metal inert gas (MIG) welding and tungsten inert gas (TIG) welding for duplex stainless steel (DSS) and low alloy steel were compared in this paper. The microstructure and corrosion morphology of dissimilar weld joints were observed by scanning electron microscopy (SEM); the chemical compositions in different zones were detected by energy-dispersive spectroscopy (EDS); the mechanical properties were measured by microhardness test, tensile test, and impact test; the corrosion behavior was evaluated by polarization curves. Obvious concentration gradients of Ni and Cr exist between the fusion boundary and the type II boundary, where the hardness is much higher. The impact toughness of weld metal by MIG welding is higher than that by TIG welding. The corrosion current density of TIG weld metal is higher than that of MIG weld metal in a 3.5wt% NaCl solution. Galvanic corrosion happens between low alloy steel and weld metal, revealing the weakness of low alloy steel in industrial service. The quality of joints produced by MIG welding is better than that by TIG welding in mechanical performance and corrosion resistance. MIG welding with the filler metal ER2009 is the suitable welding process for dissimilar metals jointing between UNS S31803 duplex stainless steel and low alloy steel in practical application.

Comparison of Maraging Steel Micro- and Nanostructure Produced Conventionally and by Laser Additive Manufacturing.

PubMed

Jägle, Eric A; Sheng, Zhendong; Kürnsteiner, Philipp; Ocylok, Sörn; Weisheit, Andreas; Raabe, Dierk

2016-12-24

Maraging steels are used to produce tools by Additive Manufacturing (AM) methods such as Laser Metal Deposition (LMD) and Selective Laser Melting (SLM). Although it is well established that dense parts can be produced by AM, the influence of the AM process on the microstructure-in particular the content of retained and reversed austenite as well as the nanostructure, especially the precipitate density and chemistry, are not yet explored. Here, we study these features using microhardness measurements, Optical Microscopy, Electron Backscatter Diffraction (EBSD), Energy Dispersive Spectroscopy (EDS), and Atom Probe Tomography (APT) in the as-produced state and during ageing heat treatment. We find that due to microsegregation, retained austenite exists in the as-LMD- and as-SLM-produced states but not in the conventionally-produced material. The hardness in the as-LMD-produced state is higher than in the conventionally and SLM-produced materials, however, not in the uppermost layers. By APT, it is confirmed that this is due to early stages of precipitation induced by the cyclic re-heating upon further deposition-i.e., the intrinsic heat treatment associated with LMD. In the peak-aged state, which is reached after a similar time in all materials, the hardness of SLM- and LMD-produced material is slightly lower than in conventionally-produced material due to the presence of retained austenite and reversed austenite formed during ageing.

Comparison of Maraging Steel Micro- and Nanostructure Produced Conventionally and by Laser Additive Manufacturing

PubMed Central

Jägle, Eric A.; Sheng, Zhendong; Kürnsteiner, Philipp; Ocylok, Sörn; Weisheit, Andreas; Raabe, Dierk

2016-01-01

Maraging steels are used to produce tools by Additive Manufacturing (AM) methods such as Laser Metal Deposition (LMD) and Selective Laser Melting (SLM). Although it is well established that dense parts can be produced by AM, the influence of the AM process on the microstructure—in particular the content of retained and reversed austenite as well as the nanostructure, especially the precipitate density and chemistry, are not yet explored. Here, we study these features using microhardness measurements, Optical Microscopy, Electron Backscatter Diffraction (EBSD), Energy Dispersive Spectroscopy (EDS), and Atom Probe Tomography (APT) in the as-produced state and during ageing heat treatment. We find that due to microsegregation, retained austenite exists in the as-LMD- and as-SLM-produced states but not in the conventionally-produced material. The hardness in the as-LMD-produced state is higher than in the conventionally and SLM-produced materials, however, not in the uppermost layers. By APT, it is confirmed that this is due to early stages of precipitation induced by the cyclic re-heating upon further deposition—i.e., the intrinsic heat treatment associated with LMD. In the peak-aged state, which is reached after a similar time in all materials, the hardness of SLM- and LMD-produced material is slightly lower than in conventionally-produced material due to the presence of retained austenite and reversed austenite formed during ageing. PMID:28772369