Environmental Effects on Graphite-Epoxy Fatigue Properties

NASA Technical Reports Server (NTRS)

Sumsion, H. T.

1976-01-01

Effects of torsional and flexural fatigue on the long-time Integrity of advanced graphite-epoxy structural composites have been investigated. Torsional fatigue tests were run at stress ratios of R = 0 (zero to maximum, repeated) and R = -1 (zero mean stress) on unidirectional, angleply, and woven graphite fiber materials in air and water at room temperature and at 74 C. Flexural fatigue tests (four-point bending) with R = -1 were run in air and water at room temperature, and with R = 0 in air. Results show that, in torsional cycling, both water environment and higher test temperature contribute to significant degradation of torsional stiffness. The degradation of stiffness from torsional stress cycling was observed to be much greater with R = -1 than with simple R = 0 cycling. The effect of environment also is greater in the fully reversed cycling. Flexural fatigue results on +/- 30 deg material show a large fatigue effect, with fatigue limits of less than 50% and 30% of the static failure strength for specimens tested under stress ratios of R = 0 and R = -1, respectively. Compliance measurements indicate that the final failures are preceded by damage initiation and accumulation, which begins at about 1% of the specimen life.

Properties of materials in high pressure hydrogen at cryogenic, room, and elevated temperatures

NASA Technical Reports Server (NTRS)

Harris, J. A., Jr.; Vanwanderham, M. C.

1973-01-01

Various tests were conducted to determine the mechanical properties of 12 alloys that are commonly used or proposed for use in pressurized gaseous hydrogen or hydrogen containing environments. Properties determined in the hydrogen environments were compared to properties determined in a pure helium environment at the same conditions to establish environmental degradation. The specific mechanical properties tested include: high-cycle fatigue, low-cycle fatigue, fracture mechanics, creep-rupture, and tensile.

Fatigue Damage Spectrum calculation in a Mission Synthesis procedure for Sine-on-Random excitations

NASA Astrophysics Data System (ADS)

Angeli, Andrea; Cornelis, Bram; Troncossi, Marco

2016-09-01

In many real-life environments, certain mechanical and electronic components may be subjected to Sine-on-Random vibrations, i.e. excitations composed of random vibrations superimposed on deterministic (sinusoidal) contributions, in particular sine tones due to some rotating parts of the system (e.g. helicopters, engine-mounted components,...). These components must be designed to withstand the fatigue damage induced by the “composed” vibration environment, and qualification tests are advisable for the most critical ones. In the case of an accelerated qualification test, a proper test tailoring which starts from the real environment (measured vibration signals) and which preserves not only the accumulated fatigue damage but also the “nature” of the excitation (i.e. sinusoidal components plus random process) is important to obtain reliable results. In this paper, the classic time domain approach is taken as a reference for the comparison of different methods for the Fatigue Damage Spectrum (FDS) calculation in case of Sine-on-Random vibration environments. Then, a methodology to compute a Sine-on-Random specification based on a mission FDS is proposed.

Fatigue crack growth in SA508-CL2 steel in a high temperature, high purity water environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gerber, T.L.; Heald, J.D.; Kiss, E.

1974-10-01

Fatigue crack growth tests were conducted with 1 in. plate specimens of SA508-CL 2 steel in room temperature air, 550$sup 0$F air and in a 550$sup 0$F, high purity, water environment. Zero-tension load controlled tests were run at cyclic frequencies as low as 0.037 CPM. Results show that growth rates in the simulated Boiling Water Reactor (BWR) water environment are faster than growth rates observed in 550$sup 0$F air and these rates are faster than the room temperature rate. In the BWR water environment, lowering the cyclic frequency from 0.37 to 0.037 CPM caused only a slight increase in themore » fatigue crack growth rate. All growth rates measured in these tests were below the upper bound design curve presented in Section XI of the ASME Code. (auth)« less

Predicting Fatigue and Psychophysiological Test Performance from Speech for Safety-Critical Environments.

PubMed

Baykaner, Khan Richard; Huckvale, Mark; Whiteley, Iya; Andreeva, Svetlana; Ryumin, Oleg

2015-01-01

Automatic systems for estimating operator fatigue have application in safety-critical environments. A system which could estimate level of fatigue from speech would have application in domains where operators engage in regular verbal communication as part of their duties. Previous studies on the prediction of fatigue from speech have been limited because of their reliance on subjective ratings and because they lack comparison to other methods for assessing fatigue. In this paper, we present an analysis of voice recordings and psychophysiological test scores collected from seven aerospace personnel during a training task in which they remained awake for 60 h. We show that voice features and test scores are affected by both the total time spent awake and the time position within each subject's circadian cycle. However, we show that time spent awake and time-of-day information are poor predictors of the test results, while voice features can give good predictions of the psychophysiological test scores and sleep latency. Mean absolute errors of prediction are possible within about 17.5% for sleep latency and 5-12% for test scores. We discuss the implications for the use of voice as a means to monitor the effects of fatigue on cognitive performance in practical applications.

Predicting Fatigue and Psychophysiological Test Performance from Speech for Safety-Critical Environments

PubMed Central

Baykaner, Khan Richard; Huckvale, Mark; Whiteley, Iya; Andreeva, Svetlana; Ryumin, Oleg

2015-01-01

Automatic systems for estimating operator fatigue have application in safety-critical environments. A system which could estimate level of fatigue from speech would have application in domains where operators engage in regular verbal communication as part of their duties. Previous studies on the prediction of fatigue from speech have been limited because of their reliance on subjective ratings and because they lack comparison to other methods for assessing fatigue. In this paper, we present an analysis of voice recordings and psychophysiological test scores collected from seven aerospace personnel during a training task in which they remained awake for 60 h. We show that voice features and test scores are affected by both the total time spent awake and the time position within each subject’s circadian cycle. However, we show that time spent awake and time-of-day information are poor predictors of the test results, while voice features can give good predictions of the psychophysiological test scores and sleep latency. Mean absolute errors of prediction are possible within about 17.5% for sleep latency and 5–12% for test scores. We discuss the implications for the use of voice as a means to monitor the effects of fatigue on cognitive performance in practical applications. PMID:26380259

Corrosion fatigue of high strength fastener materials in seawater

NASA Technical Reports Server (NTRS)

Tipton, D. G.

1983-01-01

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Corrosion fatigue of high strength fastener materials in seawater

NASA Astrophysics Data System (ADS)

Tipton, D. G.

1983-12-01

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Research on the Fatigue Flexural Performance of RC Beams Attacked by Salt Spray

NASA Astrophysics Data System (ADS)

Mao, Jiang-hong; Xu, Fang-yuan; Jin, Wei-liang; Zhang, Jun; Wu, Xi-xi; Chen, Cai-sheng

2018-04-01

The fatigue flexural performance of RC beams attacked by salt spray was studied. A testing method involving electro osmosis, electrical accelerated corrosion and salt spray was proposed. This corrosion process method effectively simulates real-world salt spray and fatigue loading exerted by RC components on sea bridges. Four RC beams that have different stress amplitudes were tested. It is found that deterioration by corrosion and fatigue loading reduces the fatigue life of the RC and decreases the ability of deformation. The fatigue life and deflection ability could be reduced by increasing the stress amplitude and the corrosion duration time. The test result demonstrates that this experimental method can couple corrosion deterioration and fatigue loading reasonably. This procedure may be applied to evaluate the fatigue life and concrete durability of RC components located in a natural salt spray environment.

Fatigue failure of dental implants in simulated intraoral media.

PubMed

Shemtov-Yona, K; Rittel, D

2016-09-01

Metallic dental implants are exposed to various intraoral environments and repetitive loads during service. Relatively few studies have systematically addressed the potential influence of the environment on the mechanical integrity of the implants, which is therefore the subject of this study. Four media (groups) were selected for room temperature testing, namely dry air, saliva substitute, same with 250ppm of fluoride, and saline solution (0.9%). Monolithic Ti-6Al-4V implants were loaded until fracture, using random spectrum loading. The study reveals that the only aggressive medium of all is the saline solution, as it shortens significantly the spectrum fatigue life of the implants. The quantitative scanning electron fractographic analysis indicates that all the tested implants grew fatigue cracks of similar lengths prior to catastrophic fracture. However, the average crack growth rate in the saline medium was found to largely exceed that in other media, suggesting a decreased fracture toughness. The notion of a characteristic timescale for environmental degradation was proposed to explain the results of our spectrum tests that blend randomly low and high cycle fatigue. Random spectrum fatigue testing is powerful technique to assess and compare the mechanical performance of dental implants for various designs and/or environments. Copyright © 2016 Elsevier Ltd. All rights reserved.

Uniaxial low cycle fatigue behavior for pre-corroded 16MND5 bainitic steel in simulated pressurized water reactor environment

NASA Astrophysics Data System (ADS)

Chen, Xu; Ren, Bin; Yu, Dunji; Xu, Bin; Zhang, Zhe; Chen, Gang

2018-06-01

The effects of uniaxial tension properties and low cycle fatigue behavior of 16MND5 bainitic steel cylinder pre-corroded in simulated pressurized water reactor (PWR) were investigated by fatigue at room temperature in air and immersion test system, scanning electron microscopy (SEM), energy disperse spectroscopy (EDS). The experimental results indicated that the corrosion fatigue lives of 16MND5 specimen were significantly affected by the strain amplitude and simulated PWR environments. The compositions of corrosion products were complexly formed in simulated PWR environments. The porous corrosion surface of pre-corroded materials tended to generate pits as a result of promoting contact area to the fresh metal, which promoted crack initiation. For original materials, the fatigue cracks initiated at inclusions imbedded in the micro-cracks. Moreover, the simulated PWR environments degraded the mechanical properties and low cycle fatigue behavior of 16MND5 specimens remarkably. Pre-corrosion of 16MND5 specimen mainly affected the plastic term of the Coffin-Manson equation.

Corrosion fatigue of 2219-T87 aluminum alloy

NASA Technical Reports Server (NTRS)

Mcmillan, V. C.

1986-01-01

Corrosion fatigue studies were conducted on bare, chemical conversion coated, and anodized 2219-T87 aluminum alloy. These tests were performed using a rotating beam machine running at a velocity of 2500 rpm. The corrosive environments tested were distilled water, 100 ppm NaCl, and 3.5 percent NaCl. Results were compared to the endurance limit in air. An evaluation of the effect of protective coatings on corrosion fatigue was made by comparing the fatigue properties of specimens with coatings to those without.

Fatigue crack growth and low cycle fatigue of two nickel base superalloys

NASA Technical Reports Server (NTRS)

Stoloff, N. S.; Duquette, D. J.; Choe, S. J.; Golwalkar, S.

1983-01-01

The fatigue crack growth and low cycle fatigue behavior of two P/M superalloys, Rene 95 and Astroloy, in the hot isostatically pressed (HIP) condition, was determined. Test variables included frequency, temperature, environment, and hold times at peak tensile loads (or strains). Crack initiation sites were identified in both alloys. Crack growth rates were shown to increase in argon with decreasing frequency or with the imposition of hold times. This behavior was attributed to the effect of oxygen in the argon. Auger analyses were performed on oxide films formed in argon. Low cycle fatigue lives also were degraded by tensile hold, contrary to previous reports in the literature. The role of environment in low cycle fatigue behavior is discussed.

Corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloys in different storage environments.

PubMed

Zavanelli, R A; Pessanha Henriques, G E; Ferreira, I; De Almeida Rollo, J M

2000-09-01

Removable partial dentures are affected by fatigue because of the cyclic mechanism of the masticatory system and frequent insertion and removal. Titanium and its alloys have been used in the manufacture of denture frameworks; however, preventive agents with fluorides are thought to attack titanium alloy surfaces. This study evaluated, compared, and analyzed the corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloy in different storage environments. For each metal, 33 dumbbell rods, 2.3 mm in diameter at the central segment, were cast in the Rematitan system. Corrosion-fatigue strength test was carried out through a universal testing machine with a load 30% lower than the 0.2% offset yield strength and a combined influence of different environments: in air at room temperature, with synthetic saliva, and with fluoride synthetic saliva. After failure, the number of cycles were recorded, and fracture surfaces were examined with an SEM. ANOVA and Tukey's multiple comparison test indicated that Ti-6Al-4V alloy achieved 21,269 cycles (SD = 8,355) against 19,157 cycles (SD = 3, 624) for the commercially pure Ti. There were no significant differences between either metal in the corrosion-fatigue life for dry specimens, but when the solutions were present, the fatigue life was significantly reduced, probably because of the production of corrosion pits caused by superficial reactions.

Effect of Applied Potential on Fatigue Life of Electropolished Nitinol Wires

NASA Astrophysics Data System (ADS)

Sivan, Shiril; Di Prima, Matthew; Weaver, Jason D.

2017-09-01

Nitinol is used as a metallic biomaterial in medical devices due to its shape memory and pseudoelastic properties. The clinical performance of nitinol depends on factors which include the surface finish, the local environment, and the mechanical loads to which the device is subjected. Preclinical evaluations of device durability are performed with fatigue tests while electrochemical characterization methods such as ASTM F2129 are employed to evaluate corrosion susceptibility by determining the rest potential and breakdown potential. However, it is well established that the rest potential of a metal surface can vary with the local environment. Very little is known regarding the influence of voltage on fatigue life of nitinol. In this study, we developed a fatigue testing method in which an electrochemical system was integrated with a rotary bend wire fatigue tester. Samples were fatigued at various strain levels at electropotentials anodic and cathodic to the rest potential to determine if it could influence fatigue life. Wires at potentials negative to the rest potential had a significantly higher number of cycles to fracture than wires held at potentials above the breakdown potential. For wires for which no potential was applied, they had fatigue life similar to wires at negative potentials.

Acoustic fatigue and sound transmission characteristics of a ram composite panel design

NASA Technical Reports Server (NTRS)

Cockburn, J. A.; Chang, K. Y.; Kao, G. C.

1972-01-01

An experimental study to determine the acoustic fatigue characteristics of a flat multi-layered structural panel is described. The test panel represented a proposed design for the outer skin of a research application module to be housed within the space shuttle orbiter vehicle. The test specimen was mounted in one wall of the Wyle 100,000 cu ft reverberation room and exposed to a broadband acoustic environment having an overall level of 145 db. The test panel was exposed to nine separate applications of the acoustic environment, each application consisting of 250 seconds duration. Upon completion of the ninth test run, the specimen was exposed to a simulated micrometeoroid impact near the panel center. One additional test run of 250 seconds duration was then performed to complete the overall simulation of 50 flight missions. The experimental results show that no significant fatigue damage occurred until the test specimen was exposed to a simulated micrometeoroid impact. The intermediate foam layer forming the core of the test specimen suffered considerable damage due to this impact, causing a marked variation in the dynamic characteristics of the overall test panel. During the final application of the acoustic environment, the strain and acceleration response spectra showed considerable variation from those spectra obtained prior to impact of the panel. Fatigue damage from acoustic loading however, was limited to partial de-bonding around the edges of the composite panel.

Very high-cycle fatigue failure in micron-scale polycrystalline silicon films: Effects of environment and surface oxide thickness

NASA Astrophysics Data System (ADS)

Alsem, D. H.; Timmerman, R.; Boyce, B. L.; Stach, E. A.; De Hosson, J. Th. M.; Ritchie, R. O.

2007-01-01

Fatigue failure in micron-scale polycrystalline silicon structural films, a phenomenon that is not observed in bulk silicon, can severely impact the durability and reliability of microelectromechanical system devices. Despite several studies on the very high-cycle fatigue behavior of these films (up to 1012cycles), there is still an on-going debate on the precise mechanisms involved. We show here that for devices fabricated in the multiuser microelectromechanical system process (MUMPs) foundry and Sandia Ultra-planar, Multi-level MEMS Technology (SUMMiT V™) process and tested under equi-tension/compression loading at ˜40kHz in different environments, stress-lifetime data exhibit similar trends in fatigue behavior in ambient room air, shorter lifetimes in higher relative humidity environments, and no fatigue failure at all in high vacuum. The transmission electron microscopy of the surface oxides in the test samples shows a four- to sixfold thickening of the surface oxide at stress concentrations after fatigue failure, but no thickening after overload fracture in air or after fatigue cycling in vacuo. We find that such oxide thickening and premature fatigue failure (in air) occur in devices with initial oxide thicknesses of ˜4nm (SUMMiT V™) as well as in devices with much thicker initial oxides ˜20nm (MUMPs). Such results are interpreted and explained by a reaction-layer fatigue mechanism. Specifically, moisture-assisted subcritical cracking within a cyclic stress-assisted thickened oxide layer occurs until the crack reaches a critical size to cause catastrophic failure of the entire device. The entirety of the evidence presented here strongly indicates that the reaction-layer fatigue mechanism is the governing mechanism for fatigue failure in micron-scale polycrystalline silicon thin films.

Effects of EVA gloves on grip strength and fatigue under low temperature and low pressure.

PubMed

Tian, Yinsheng; Ding, Li; Liu, Heqing; Li, Yan; Li, Deyu; Wang, Li

2016-03-01

To study the effects of wearing extravehicular activity (EVA) gloves on grip strength and fatigue in low temperature, low pressure and mixing of two factors (low temperature and low pressure). The maximum grip strength and fatigue tests were performed with 10 healthy male subjects wearing gloves in a variety of simulated environments. The data was analysed using the normalization method. The results showed that wearing gloves significantly affected the maximum grip strength and fatigue. Pressure (29.6, 39.2 kPa) had more influence on the maximum grip compared with control group while low temperatures (-50, -90, -110 °C) had no influence on grip but affected fatigue dramatically. The results also showed that the maximum grip strength and fatigue were influenced significantly in a compound environment. Space environment remarkably reduced strength and endurance of the astronauts. However, the effects brought by the compound environment cannot be understood as the superimposition of low temperature and pressure effects. Copyright © 2015 Elsevier Ltd and The Ergonomics Society. All rights reserved.

Fatigue of DIN 1.4914 martensitic stainless steel in a hydrogen environment

NASA Astrophysics Data System (ADS)

Shakib, J. I.; Ullmaier, H.; Little, E. A.; Faulkner, R. G.; Schmilz, W.; Chung, T. E.

1994-09-01

Fatigue tests at room temperature in vacuum, air and hydrogen have been carried out on specimens of DIN 1.4914 martensitic stainless steel in load-controlled, push-pull type experiments. Fatigue lifetimes in hydrogen are significantly lower than in both vacuum and air and the degradation is enhanced by lowering the test frequency or introducing hold times into the tension half-cycle. Fractographic examinations reveal hydrogen embrittlement effects in the form of internal cracking between fatigue striations together with surface modifications, particularly at low stress amplitudes. It is suggested that gaseous hydrogen can influence both fatigue crack initiation and propagation events in martensitic steels.

Effects of sour crude oil on fatigue properties of steel plates for shipbuilding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ouchi, H.; Kobayashi, J.; Ishikawa, T.

1994-12-31

The concentration of diffusible hydrogen introduced into steel was measured, and fatigue crack growth tests and fatigue life tests were carried out in sour crude oil containing a high concentration of hydrogen sulfide and under electrolytic hydrogen-charging conditions in neutral solution, using a high strength steel produced by the thermo-mechanical control process (TMCP) and a mild steel which are steels for hull plates. Comparison of the results demonstrated that a very small amount of hydrogen such as that introduced into steel from sour crude oil under atmospheric pressure accelerated the fatigue crack growth in the high {Delta}K regime and shortenedmore » the fatigue life in the high stress range region, but did not shorten the fatigue life in the low stress region. The electrolytic hydrogen-charging condition appeared to be appropriate as a fatigue-crack-growth test environment to simulate sour crude oil. The deterioration of fatigue characteristics of the TMCP high strength steel was similar with that of the mild steel.« less

Mechanical properties of several nickel alloys in hydrogen at elevated temperatures

NASA Technical Reports Server (NTRS)

Warren, J. R.; Harris, J. A., Jr.; Vanwanderham, M. C.

1977-01-01

Tests were performed to determine low cycle fatigue and crack growth rate properties of one iron-base and two forms of one cast nickel-base alloy. The alloys were tested in various forms and/or heat-treat conditions that are proposed for use in a high-pressure hydrogen or a hydrogen-water vapor environment. Some general conclusions can be made comparing the results of tests in a hydrogen environment with those in a hydrogen-water vapor environment. The hydrogen-water vapor environment caused a 50 percent average reduction in fatigue life, indicating extreme degradation when compared with tests conducted in air, for Incoloy 903 at 1033 K (1400 F). Crack growth rates increased significantly for all materials with increasing test temperature. A very significant increase (three orders of magnitude) in crack growth rate occurred for Incoloy 903 tested in the hydrogen-water vapor environment when compared with testing done in hydrogen along at 922 K (1200 F).

Orbital fatigue tester for use in Skylab experiment T032

NASA Technical Reports Server (NTRS)

Sandorff, P. E.

1973-01-01

A prototype fatigue test machine is described which is suitable for use by an astronaut in conducting constant amplitude materials fatigue tests aboard a Skylab or space shuttle vehicle. The machine is comparised of a mechanical tester, which would be passed through a small (7.6-inch square) airlock to be supported in the space environment on an extendible boom, and a control console, which would provide remote control from within the space vehicle.

Development of Fatigue and Crack Propagation Design and Analysis Methodology in a Corrosive Environment for Typical Mechanically-Fastened Joints. Volume 2. State-of-the-Art Assessment.

DTIC Science & Technology

1983-03-01

120] hypothesized a linear summation model to predict the corrosion -fatigue behavior above Kjscc for a high-strength steel . The model considers the...120] could satisfactorily predict the rates of corrosion -fatigue-crack growth for 18-Ni Maraging steels tested in several gaseous and aqueous...NADC-83126-60 Vol. II 6. The corrosion fatigue behavior of titanium alloys is very complex. Therefore, a better understanding of corrosion fatigue

Accelerated Stress-Corrosion Testing

NASA Technical Reports Server (NTRS)

1986-01-01

Test procedures for accelerated stress-corrosion testing of high-strength aluminum alloys faster and provide more quantitative information than traditional pass/fail tests. Method uses data from tests on specimen sets exposed to corrosive environment at several levels of applied static tensile stress for selected exposure times then subsequently tensile tested to failure. Method potentially applicable to other degrading phenomena (such as fatigue, corrosion fatigue, fretting, wear, and creep) that promote development and growth of cracklike flaws within material.

Fatigue, Creep-Fatigue, and Thermomechanical Fatigue Life Testing of Alloys

NASA Technical Reports Server (NTRS)

Halford, Gary R.; Lerch, Bradley A.; McGaw, Michael A.

2000-01-01

The fatigue crack initiation resistance of an alloy is determined by conducting a series of tests over a range of values of stress amplitude or strain range. The observed number of cycles to failure is plotted against the stress amplitude or strain range to obtain a fatigue curve. The fatigue properties quoted for an alloy are typically the constants used in the equation(s) that describe the fatigue curve. Fatigue lives of interest may be as low as 10(exp 2) or higher than 10(exp 9) cycles. Because of the enormous scatter associated with fatigue, dozens of tests may be needed to confidently establish a fatigue curve, and the cost may run into several thousands of dollars. To further establish the effects on fatigue life of the test temperature, environment, alloy condition, mean stress effects, creep-fatigue effects, thermomechanical cycling, etc. requires an extraordinarily large and usually very costly test matrix. The total effort required to establish the fatigue resistance of an alloy should not be taken lightly. Fatigue crack initiation tests are conducted on relatively small and presumed to be initially crack-free, samples of an alloy that are intended to be representative of the alloy's metallurgical and physical condition. Generally, samples are smooth and have uniformly polished surfaces within the test section. Some may have intentionally machined notches of well-controlled geometry, but the surface at the root of the notch is usually not polished. The purpose of polishing is to attain a reproducible surface finish. This is to eliminate surface finish as an uncontrolled variable. Representative test specimen geometries will be discussed later. Test specimens are cyclically loaded until macroscopically observable cracks initiate and eventually grow to failure. Normally, the fatigue failure life of a specimen is defined as the number of cycles to separation of the specimen into two pieces. Alternative definitions are becoming more common, particularly for low-cycle fatigue testing, wherein some prescribed indication of impending failure due to cracking is adopted. Specific criteria will be described later. As a rule, cracks that develop during testing are not measured nor are the test parameters intentionally altered owing to the presence of cracking.

Effect of Surface Impulsive Thermal Loads on Fatigue Behavior of Constant Volume Propulsion Engine Combustor Materials

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Fox, Dennis S.; Miller, Robert A.; Ghosn, Louis J.; Kalluri, Sreeramesh

2004-01-01

The development of advanced high performance constant-volume-combustion-cycle engines (CVCCE) requires robust design of the engine components that are capable of enduring harsh combustion environments under high frequency thermal and mechanical fatigue conditions. In this study, a simulated engine test rig has been established to evaluate thermal fatigue behavior of a candidate engine combustor material, Haynes 188, under superimposed CO2 laser surface impulsive thermal loads (30 to 100 Hz) in conjunction with the mechanical fatigue loads (10 Hz). The mechanical high cycle fatigue (HCF) testing of some laser pre-exposed specimens has also been conducted under a frequency of 100 Hz to determine the laser surface damage effect. The test results have indicated that material surface oxidation and creep-enhanced fatigue is an important mechanism for the surface crack initiation and propagation under the simulated CVCCE engine conditions.

The application of probabilistic design theory to high temperature low cycle fatigue

NASA Technical Reports Server (NTRS)

Wirsching, P. H.

1981-01-01

Metal fatigue under stress and thermal cycling is a principal mode of failure in gas turbine engine hot section components such as turbine blades and disks and combustor liners. Designing for fatigue is subject to considerable uncertainty, e.g., scatter in cycles to failure, available fatigue test data and operating environment data, uncertainties in the models used to predict stresses, etc. Methods of analyzing fatigue test data for probabilistic design purposes are summarized. The general strain life as well as homo- and hetero-scedastic models are considered. Modern probabilistic design theory is reviewed and examples are presented which illustrate application to reliability analysis of gas turbine engine components.

(abstract) A Brief, Selective Review of Thermal Cycling Fatigue in Eutectic Tin-Lead Solder

NASA Technical Reports Server (NTRS)

Winslow, J. W.; Silveira, C. de

1993-01-01

This paper reviews selected parts of the current literature relevant to thermo-mechanical fatigue mechanisms in eutectic tin-lead solder, and suggests a general outline to account for some observed failures. The field is found to be complex. One recent experimental study finds some failure modes to be sensitive to joint geometry. Attempts to extrapolate from test environments to service environments have had only limited success. Much work remains to be done before fatigue failures in this material can be considered as under practical control.

Hydrogen effects on Ni-Ti fatigue performance by self -heating method

NASA Astrophysics Data System (ADS)

Rokbani, M.; Saint-Sulpice, L.; Arbab Chirani, S.; Bouraoui, T.

2017-10-01

Ni-Ti superelastic alloys are extensively used in manufacturing biomedical devices because of their high mechanical performance, good fatigue durability and biocompatibility compared to traditional metallic materials. During clinical use, most of these devices are intended to work under cyclic or repetitive loadings and may be in contact with corrosive environments leading to unexpected failures. It is however recognized that the fatigue-environment interaction, especially fatigue-hydrogen absorption, can be the main cause of these failures. The aim of this work is to investigate the fatigue behavior of superelastic Ni-Ti intended for manufacturing medical devices at high number of cycles (HCF) with a particular emphasis to the effect of hydrogen on fatigue properties. Fatigue tests were analyzed using self-heating measurements based on observing thermal effects during cyclic loadings. The results obtained with self-heating approach showed a trend of a decrease in the fatigue life of Ni-Ti alloys after hydrogen absorption and the fatigue limit extrapolated will be compared with the results obtained with the classical S-N curves method.

The influence of temperature on fatigue-crack growth in a mill annealed Ti-6Al-4V alloy

NASA Technical Reports Server (NTRS)

Wei, R. P.; Ritter, D. L.

1972-01-01

To understand the influence temperature on the rate of fatigue crack growth in high strength metal alloys, constant load amplitude, fatigue crack growth experiments were carried out using a 1/4-inch-thick (6.35 mm) mill annealed Ti-6Al-4V alloy plate as a model material. The rates of fatigue crack growth were determined as a function of temperature, ranging from room temperature to about 290 C (or, about 550 F/563K) and as a function of the crack tip stress intensity factor in a dehumidified high purity argon environment. Limited correlative experiments indicate that dehumidified oxygen and hydrogen have no effect on the rate of fatigue crack growth in this alloy, while distilled water increased the rate of crack growth slightly in the range tested. Companion fractographic examinations suggest that the mechanisms for fatigue crack growth in the various environments are essentially the same.

[Cyclic fatigue of Vita mark II machinable ceramics under Hertzian's contact].

PubMed

Liu, Wei-Cai; Zhang, Zhi-Shen; Huang, Cheng-Min; Chao, Yong-Lie; Wan, Qian-Bing

2006-08-01

To investigate the cyclic fatigue modes of Vita mark II machinable ceramics under Hertzian's contact. Hertzian's contact technique (WC spheres r = 3.18 mm) was used to investigate the cyclic fatigue of Vita mark II machinable ceramic. All specimens were fatigued by cyclic loading in moist environment, furthermore, surviving strength was examined by three point test and morphology damage observation. In homogeneous Vita mark II machinable ceramics, two fatigue damage modes existed after cyclic loading with spheres under moist environment, including conventional tensile-driven cone cracking (brittle mode) and shear-driven microdamage accumulation (quasi-plastic mode). The latter generated radial cracks and deeply penetrating secondary cone crack. Initial strength degradation were caused by the cone cracks, subsequent and much more deleterious loss was caused by radial cracks. Cyclic fatigue modes of Vita mark II machinable ceramics includes brittle and quasi-plastic mode.

Combined high vacuum/high frequency fatigue tester

NASA Technical Reports Server (NTRS)

Honeycutt, C. R.; Martin, T. F.

1971-01-01

Apparatus permits application of significantly greater number of cycles or equivalent number of cycles in shorter time than conventional fatigue test machines. Environment eliminates problems associated with high temperature oxidation and with sensitivity of refractory alloy behavior to atmospheric contamination.

Factors Influencing Dwell Fatigue Cracking in Notches of Powder Metallurgy Superalloys

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Telesman, J.; Ghosn, L.; Garg, A.; Gayda, J.

2011-01-01

The influences of heat treatment and cyclic dwells on the notch fatigue resistance of powder metallurgy disk superalloys were investigated for low solvus high refractory (LSHR) and ME3 disk alloys. Disks were processed to produce material conditions with varied microstructures and associated mechanical properties. Notched specimens were first subjected to baseline dwell fatigue cycles having a dwell at maximum load, as well as tensile, stress relaxation, creep rupture, and dwell fatigue crack growth tests at 704 C. Several material heat treatments displayed a bimodal distribution of fatigue life with the lives varying by two orders-of-magnitude, while others had more consistent fatigue lives. This response was compared to other mechanical properties, in search of correlations. The wide scatter in baseline dwell fatigue life was observed only for material conditions resistant to stress relaxation. For selected materials and conditions, additional tests were then performed with the dwells shifted in part or in total to minimum tensile load. The tests performed with dwells at minimum load exhibited lower fatigue lives than max dwell tests, and also exhibited early crack initiation and a substantial increase in the number of initiation sites. These results could be explained in part by modeling evolution of peak stresses in the notch with continued dwell fatigue cycling. Fatigue-environment interactions were determined to limit life for the fatigue cycles with dwells.

Modelling and Laboratory Studies on the Adhesion Fatigue Performance for Thin-Film Asphalt and Aggregate System

PubMed Central

Wang, Dongsheng; Feng, Decheng

2014-01-01

Adhesion between asphalt and aggregate plays an important role in the performance of asphalt mixtures. A low-frequency adhesion fatigue test was proposed in this paper to study the effect of environment on the asphalt-aggregate adhesion system. The stress-based fatigue model had been utilized to describe the fatigue behavior of thin-film asphalt and aggregate system. The factors influencing the adhesion fatigue performance were also investigated. Experiment results show that asphalt has more important effect on the adhesion performance comparing with aggregate. Basalt, which is regarded as hydrophobic aggregates with low silica content, has better adhesion performance to asphalt binder when compared with granite. The effects of aging on the adhesion fatigue performance are different for PG64-22 and rubber asphalt. Long-term aging is found to reduce the adhesion fatigue lives for rubber asphalt and aggregate system, while the effect of long-term aging for aggregate and PG64-22 binder system is positive. Generally the increased stress amplitude and test temperature could induce greater damage and lead to less fatigue lives for adhesion test system. PMID:25054187

Modelling and laboratory studies on the adhesion fatigue performance for thin-film asphalt and aggregate system.

PubMed

Wang, Dongsheng; Yi, Junyan; Feng, Decheng

2014-01-01

Adhesion between asphalt and aggregate plays an important role in the performance of asphalt mixtures. A low-frequency adhesion fatigue test was proposed in this paper to study the effect of environment on the asphalt-aggregate adhesion system. The stress-based fatigue model had been utilized to describe the fatigue behavior of thin-film asphalt and aggregate system. The factors influencing the adhesion fatigue performance were also investigated. Experiment results show that asphalt has more important effect on the adhesion performance comparing with aggregate. Basalt, which is regarded as hydrophobic aggregates with low silica content, has better adhesion performance to asphalt binder when compared with granite. The effects of aging on the adhesion fatigue performance are different for PG64-22 and rubber asphalt. Long-term aging is found to reduce the adhesion fatigue lives for rubber asphalt and aggregate system, while the effect of long-term aging for aggregate and PG64-22 binder system is positive. Generally the increased stress amplitude and test temperature could induce greater damage and lead to less fatigue lives for adhesion test system.

OTEC riser cable model and prototype testing

NASA Astrophysics Data System (ADS)

Kurt, J. P.; Schultz, J. A.; Roblee, L. H. S.

1981-12-01

Two different OTEC riser cables have been developed to span the distance between a floating OTEC power plant and the ocean floor. The major design concerns for a riser cable in the dynamic OTEC environment are fatigue, corrosion, and electrical/mechanical aging of the cable components. The basic properties of the cable materials were studied through tests on model cables and on samples of cable materials. Full-scale prototype cables were manufactured and were tested to measure their electrical and mechanical properties and performance. The full-scale testing was culminated by the electrical/mechanical fatigue test, which exposes full-scale cables to simultaneous tension, bending and electrical loads, all in a natural seawater environment.

A Review of Fatigue Crack Growth in Metallics at Low Stress Intensities.

DTIC Science & Technology

1983-01-01

received R 0,35 * 257 C 2i 0*C b -sT 625C 0 0 10 0 ~1O90 co 0 C 2 2,5 3 4 5 67 8 910C12 15 20 A K MN rfiV2 Figure 31 The influence of test temperature...34 L.2. 11111 L25I MICROCOPY RESOLUTION TEST CHART NATIONAL. BUREAU OF STANDARDS 1963-A A 44-7 F 49620-82-C-0088 A REVIEW OF FATIGUE CRACK GROWTH IN...relation to the following variables, mean stress, yield stress, test temperature, test frequency, fatigue crack closure, microstructure, environment and

Fracture mechanics data for 2024-T861 and 2124-T851 aluminum

NASA Technical Reports Server (NTRS)

Pionke, L. J.; Linback, R. K.

1974-01-01

The fracture toughness and fatigue flaw growth characteristics of 2024-T861 and 2124-T851 aluminum were evaluated under plane stress conditions. Center cracked tension specimens were employed to evaluate these properties under a number of different test conditions which included variations in specimen thickness, specimen orientation, test environment, and initial flaw size. The effect of buckling was also investigated for all tests of thin gage specimens, and the effect of frequency and stress ratio was evaluated for the cyclic tests. Fracture toughness test results were analyzed and presented in terms of fracture resistance curves; fatigue flaw growth data was analyzed using empirical rate models. The results of the study indicate that both fracture toughness and resistance to fatigue crack growth improve with increasing temperature and decreasing thickness. The presence of buckling during testing of thin gage panels was found to degrade the resistance to fatigue flaw growth only at elevated temperatures.

Corrosion Fatigue of High-Strength Titanium Alloys Under Different Stress Gradients

NASA Astrophysics Data System (ADS)

Baragetti, Sergio; Villa, Francesco

2015-05-01

Ti-6Al-4V is the most widely used high strength-to-mass ratio titanium alloy for advanced engineering components. Its adoption in the aerospace, maritime, automotive, and biomedical sectors is encouraged when highly stressed components with severe fatigue loading are designed. The extents of its applications expose the alloy to several aggressive environments, which can compromise its brilliant mechanical characteristics, leading to potentially catastrophic failures. Ti-6Al-4V stress-corrosion cracking and corrosion-fatigue sensitivity has been known since the material testing for pressurized tanks for Apollo missions, although detailed investigations on the effects of harsh environment in terms of maximum stress reduction have been not carried out until recent times. In the current work, recent experimental results from the authors' research group are presented, quantifying the effects of aggressive environments on Ti-6Al-4V under fatigue loading in terms of maximum stress reduction. R = 0.1 axial fatigue results in laboratory air, 3.5 wt.% NaCl solution, and CH3OH methanol solution at different concentrations are obtained for mild notched specimens ( K t = 1.18) at 2e5 cycles. R = 0.1 tests are also conducted in laboratory air, inert environment, 3.5 wt.% NaCl solution for smooth, mild and sharp notched specimens, with K t ranging from 1 to 18.65, highlighting the environmental effects for the different load conditions induced by the specimen geometry.

Fatigue of restorative materials.

PubMed

Baran, G; Boberick, K; McCool, J

2001-01-01

Failure due to fatigue manifests itself in dental prostheses and restorations as wear, fractured margins, delaminated coatings, and bulk fracture. Mechanisms responsible for fatigue-induced failure depend on material ductility: Brittle materials are susceptible to catastrophic failure, while ductile materials utilize their plasticity to reduce stress concentrations at the crack tip. Because of the expense associated with the replacement of failed restorations, there is a strong desire on the part of basic scientists and clinicians to evaluate the resistance of materials to fatigue in laboratory tests. Test variables include fatigue-loading mode and test environment, such as soaking in water. The outcome variable is typically fracture strength, and these data typically fit the Weibull distribution. Analysis of fatigue data permits predictive inferences to be made concerning the survival of structures fabricated from restorative materials under specified loading conditions. Although many dental-restorative materials are routinely evaluated, only limited use has been made of fatigue data collected in vitro: Wear of materials and the survival of porcelain restorations has been modeled by both fracture mechanics and probabilistic approaches. A need still exists for a clinical failure database and for the development of valid test methods for the evaluation of composite materials.

Disinhibiting neurons in the dorsomedial hypothalamus delays the onset of exertional fatigue and exhaustion in rats exercising in a warm environment.

PubMed

Zaretsky, Dmitry V; Kline, Hannah; Zaretskaia, Maria V; Brown, Mary Beth; Durant, Pamela J; Alves, Nathan J; Rusyniak, Daniel E

2018-06-15

Stimulants cause hyperthermia, in part, by increasing heat generation through exercise. Stimulants also delay the onset of fatigue and exhaustion allowing animals to exercise longer. If used in a warm environment, this combination (increased exercise and decreased fatigue) can cause heat stroke. The dorsomedial hypothalamus (DMH) is involved in mediating locomotion from stimulants. Furthermore, inhibiting the DMH decreases locomotion and prevents hyperthermia in rats given stimulants in a warm environment. Whether the DMH is involved in mediating exercise-induced fatigue and exhaustion is not known. We hypothesized that disinhibiting neurons in the dorsomedial hypothalamus (DMH) would delay the onset of fatigue and exhaustion in animals exercising in a warm environment. To test this hypothesis, we used automated video tracking software to measure fatigue and exhaustion. In rats, using wearable mini-pumps, we demonstrated that disinhibiting the DMH, via bicuculline perfusion (5 µM), increased the duration of exercise in a warm environment as compared to control animals (25 ± 3 min vs 15 ± 2 min). Bicuculline-perfused animals also had higher temperatures at exhaustion (41.4 ± 0.2 °C vs 40.0 ± 0.4 °C). Disinhibiting neurons in the DMH also increased the time to fatigue. Our data show that the same region of the hypothalamus that is involved in mediating locomotion to stimulants, is also involved in controlling exhaustion and fatigue. These findings have implications for understanding the cause and treatment of stimulant-induced-hyperthermia. Copyright © 2018 Elsevier B.V. All rights reserved.

Nanosecond pulsed laser micromachining for experimental fatigue life study of Ti-3Al-2.5V tubes

NASA Astrophysics Data System (ADS)

Lin, Yaomin; Gupta, Mool C.; Taylor, Robert E.; Lei, Charles; Stone, William; Spidel, Tom; Yu, Michael; Williams, Reanne

2009-01-01

Defects on external surface of in-service hydraulic tubes can reduce total life cycles for operation. Evaluation of fatigue life of the tubes with damage is thus critical for safety reasons. A methodology of generating defects in the Ti-3Al-2.5V tube—a widely used pipeline in hydraulic systems of aircrafts—using nanosecond pulsed laser for experimental fatigue life study is described in this paper. Straight tubes of five different sizes were laser micromachined to generate notches of given length and depths on the outside surface. Approaches were developed to precisely control the notch dimensions. The laser-notched tubes were tested with cyclic internal impulse pressure and fatigue life was measured. The laser notches and fatigue cracks were characterized after the test. It is concluded that laser micromachining generated consistent notches, and the influence of notch depth on fatigue life of the tube is significant. Based on the experimental test results, the relationship between the fatigue life of the Ti-3Al-2.5V tube and the notch depth was revealed. The research demonstrated that laser micromachining is applicable for experimental fatigue life study of titanium tubes. The presented test data are useful for estimating the damage limits of the titanium tubes in service environment and for further theoretical studies.

On the Use of 3dB Qualification Margin for Structural Parts on Expendable Launch Vehicles

NASA Technical Reports Server (NTRS)

Yunis, Isam

2007-01-01

The standard random vibration qualification test used for Expendable Launch Vehicle components is Maximum Predicted Environment (MPE) + 6dB for a duration of 4 times the service life of the part. This can be a severe qualification test for these fatigue-sensitive structures. This paper uses flight data from several launch vehicles to establish that reducing the qualification approach to MPE+3dB for the duration of the peak environment (1x life) is valid for fatigue-sensitive structural components. Items that can be classified as fatigue-sensitive are probes, ducts, tubing, bellows, hoses, and any non-functional structure. Non-functional structure may be flight critical or carry fluid, but it cannot include any moving parts or electronics. This reduced qualification approach does not include primary or secondary structure which would be exclusively designed by peak loads, either transient or quasi-static, that are so large and of so few cycles as to make fatigue a moot point.

Psychosocial correlates of fatigue in multiple sclerosis.

PubMed

Schwartz, C E; Coulthard-Morris, L; Zeng, Q

1996-02-01

To explore: (1) the interrelation among the neuropsychological, psychological, and psychosocial factors and fatigue as measured by the Multidimensional Assessment of Fatigue scale, and (2) the impact of fatigue on role performance. Clinical interview with neuropsychological testing and cross-sectional study by mail. Multiple sclerosis (MS) clinic registry of a large Boston teaching hospital. 139 MS patients representing a broad range of disability. The Multidimensional Assessment of Fatigue (MAF) scale, the Extended Disability Status Scale, the Sickness Impact Profile, Rao cognitive battery, the Trailmaking Test, depression, anxiety, and social activity limitations subscales from the Arthritis Impact Measurement Scales, and the Ryff Happiness Scale. Stepwise multiple regression analyses revealed that having a low sense of environmental mastery was the best psychosocial predictor of both global fatigue and fatigue-related distress, after adjusting for sociodemographic and medical factors. Further, people who reported being more depressed tended to report more severe fatigue. Neuropsychological performance was not associated with fatigue. Fatigue was found to limit social, work, and overall role performance, but not physical role performance. People who feel that they can choose or create environments suitable to their psychic or physical conditions report less global fatigue and less fatigue-related distress, and fatigue can have an important impact on role performance. The implications of these findings for designing fatigue management interventions are discussed.

Parametric study and characterization of the isobaric thermomechanical transformation fatigue of nickel-rich NiTi SMA actuators

NASA Astrophysics Data System (ADS)

Bertacchini, Olivier W.; Schick, Justin; Lagoudas, Dimitris C.

2009-03-01

The recent development of various aerospace applications utilizing Ni-rich NiTi Shape memory Alloys (SMAs) as actuators motivated the need to characterize the cyclic response and the transformation fatigue behavior of such alloys. The fatigue life validation and certification of new designs is required in order to be implemented and used in future applications. For that purpose, a custom built fatigue test frame was designed to perform isobaric thermally induced transformation cycles on small dogbones SMA actuators (test gauge cross-section up to: 1.270 x 0.508 mm2). A parametric study on the cyclic response and transformation fatigue behavior of Ni-rich NiTi SMAs led to the optimization of several material/process and test parameters, namely: the applied stress range, the heat treatment, the heat treatment environment and the specimen thickness. However, fatigue testing was performed in a chilled waterless glycol environment maintained at a temperature of 5°C that showed evidence of corrosion-assisted transformation fatigue failure. Therefore, it was necessary to build a fatigue test frame that would employ a dry and inert cooling methodology to get away from any detrimental interactions between the specimens and the cooling medium (corrosion). The selected cooling method was gaseous nitrogen, sprayed into a thermally insulated chamber, maintaining a temperature of -20°C. The design of the gaseous nitrogen cooling was done in such a way that the actuation frequency is similar to the one obtained using the original design (~ 0.1 Hz). For both cooling methods, Joule resistive heating was used to heat the specimens. In addition and motivated by the difference in surface quality resulting from different material processing such as EDM wire cutting and heat treatments, EDM recast layer and oxide layer were removed. The removal was followed by an ultra-fine polish (0.05 μm) that was performed on a subset of the fatigue specimens. Experimental results are presented for full actuation of the SMA actuators and are given in terms of applied stress, accumulated plastic strain and number of cycles to failure. In addition, the assessment of the influence of the surface quality is supported by fatigue tests results and post-failure microstructure analysis.

Corrosion fatigue in nitrocarburized quenched and tempered steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Karim Khani, M.; Dengel, D.

1996-05-01

In order to investigate the fatigue strength and fracture mechanism of salt bath nitrocarburized steels, specimens of the steels SAE 4135 and SAE 4140, in a quenched and tempered state, and additionally in a salt bath nitrocarburized and oxidizing cooled state as well as in a polished (after the oxidizing cooling) and renewed oxidized state, were subjected to comparative rotating bending fatigue tests in inert oil and 5 pct NaCl solution. In addition, some of the quenched and tempered specimens of SAE 4135 material were provided with an approximately 50-{mu}m-thick electroless Ni-P layer, in order to compare corrosion fatigue behaviormore » between the Ni-P layer and the nitride layers. Long-life corrosion fatigue tests of SAE 4135 material were carried out under small stresses in the long-life range up to 10{sup 8} cycles with a test frequency of 100 Hz. Fatigue tests of SAE 4140 material were carried out in the range of finite life (low-cycle range) with a test frequency of 13 Hz. The results show that the 5 pct NaCl environment drastically reduced fatigue life, but nitrocarburizing plus oxidation treatment was found to improve the corrosion fatigue life over that of untreated and Ni-P coated specimens. The role of inclusions in initiating fatigue cracks was investigated. It was found that under corrosion fatigue conditions, the fatigue cracks started at cavities along the interfaces of MnS inclusions and matrix in the case of quenched and tempered specimens. The nitrocarburized specimens, however, showed a superposition of pitting corrosion and corrosion fatigue in which pores and nonmetallic inclusions in the compound layer play a predominant role concerning the formation of pits in the substrate.« less

Repeated Impact Method and Devices to Simulate the Impact Fatigue Property of Drillstring

NASA Astrophysics Data System (ADS)

Lin, Y. H.; Li, B.; Pan, J.; Li, Q.; Liu, W. Y.; Pan, Y.

2017-05-01

It is well known that drillstring failures are a pendent problem in drilling engineering, because of the fatigue accumulation caused by the low amplitude-repeated impact. In order to reveal the effect of low amplitude-repeated impact on the failure mechanism of the drillstring, a repeated impact method and instrument have been developed based on the Charpy impact method, by which a series of tests have been performed in the condition of non-corrosive medium and with H2S environment respective. Test results of non-corrosive medium environment indicates that, with the increase of single impact energy, the low amplitude-repeated impact resistance of drillstring decreases significantly; For H2S corrosion environment, the low amplitude-repeated impact resistances with H2S is much lower than that without H2S corrosion, and high strength material such as V-150 drillstring is more sensitive to H2S corrosion media. Furthermore, based on the experiment data, the accumulation fatigue model to predict the service life of the drillstring is developed, which could be used to predict the fatigue life. Research fruits are very vital to select a suitable rotational speed for drilling job and drillstring design.

Effect of environment on low-cycle fatigue of a nickel-titanium instrument.

PubMed

Cheung, Gary S P; Shen, Ya; Darvell, Brian W

2007-12-01

This study examined the low-cycle fatigue (LCF) behavior of a nickel-titanium (NiTi) engine-file under various environmental conditions. One brand of NiTi instrument was subjected to rotational-bending fatigue in air, deionized water, sodium hypochlorite, or silicone oil. The curvature of each instrument, diameter of the fracture cross-section, and the number of rotations to failure were determined. The strain-life relationship in the LCF region was examined by using one-way analysis of variance, and the number of crack origins with chi2, for differences between groups. The results showed a linear relationship, on logarithmic scales, between the LCF life and the surface strain amplitude; regression line slopes were significantly different between noncorrosive (air, silicone oil) and corrosive (water, hypochlorite) environments (P < .05), as well as number of crack origins (P < .05). Hypochlorite was more detrimental to fatigue life than water. In conclusion, environmental conditions significantly affect the LCF behavior of NiTi rotary instruments. Fatigue testing of NiTi engine-files should be in a service-like environment.

Low cycle fatigue life of two nickel-base casting alloys in a hydrogen environment. [for high-pressure oxidizer turbopump turbine nozzles

NASA Technical Reports Server (NTRS)

Cooper, R. A.

1976-01-01

Samples of two nickel-base casting alloys, Mar-M-246 (a Martin Company alloy) and 713LC (a low-carbon modification of the alloy 713C developed by International Nickel Company) were tested as candidate materials for the high-pressure fuel and high-pressure oxidizer turbopump turbine nozzles. The samples were subjected to tensile tests and to low cycle fatigue tests in high-pressure hydrogen to study the influence of the hydrogen environment. The Mar-M-246 material was found to have a three times higher cyclic life in hydrogen than the 713LC alloy, and was selected as the nozzle material.

Cyclic Deformation, Damage, and Effects of Environment in the Ni3Al Ordered Alloy at Elevated Temperature

DTIC Science & Technology

1991-03-29

restricts atomic mobility leading to slower diffusion and perhaps better creep resistance. Ordered intermetallics such as aluminides and silicides are...evaluation of the mechanical properties of these materials (specifically creep , oxidation and fatigue) must be evaluated before implementation in...rate by an order of magnitude (frcm 0.001/s to 0.01/s) doubled the fatigue life at a given plastic strain range. When tested in vacuum environments

Effect of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate. [for aerospace applications

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1984-01-01

The effects of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate at frequencies of 1 Hz and 10 Hz were investigated. Twenty-five mm thick compact specimens were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Fatigue crack growth rates were calculated from effective crack lengths determined using a compliance method. Tests were conducted in hard vacuum and at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. Fatigue crack growth rates were frequency insensitive under all environment conditions tested. For constant stress intensity factor ranges crack growth rate transitions occurred at low and high water vapor pressures. Crack growth rates at intermediate pressures were relatively constant and showed reasonable agreement with published data for two Al-Cu-Mg alloys. The existence of two crack growth rate transitions suggests either a change in rate controlling kinetics or a change in corrosion fatigue mechanism as a function of water vapor pressure. Reduced residual deformation and transverse cracking specimens tested in water vapor versus vacuum may be evidence of embrittlement within the plastic zone due to environmental interaction.

The effect of water vapor on fatigue crack Growth in 7475-t651 aluminum alloy plate. [for aerospace applications

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1982-01-01

The effects of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate at frequencies of 1 Hz and 10 Hz were investigated. Twenty-five mm thick compact specimens were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Fatigue crack growth rates were calculated from effective crack lengths determined using a compliance method. Tests were conducted in hard vacuum and at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. Fatigue crack growth rates were frequency insensitive under all environment conditions tested. For constant stress intensity factor ranges crack growth rate transitions occurred at low and high water vapor pressures. Crack growth rates at intermediate pressures were relatively constant and showed reasonable agreement with published data for two Al-Cu-Mg alloys. The existence of two crack growth rate transitions suggests either a change in rate controlling kinetics or a change in corrosion fatigue mechanism as a function of water vapor pressure. Reduced residual deformation and transverse cracking specimens tested in water vapor versus vacuum may be evidence of embrittlement within the plastic zone due to environmental interaction.

Behavior of Fatigue Crack Tip Opening in Air and Corrosive Atmosphere

NASA Astrophysics Data System (ADS)

Hayashi, Morihito; Toeda, Kazunori

In the study, a formula for predicting fatigue crack tip opening displacement is deduced firstly. And then, due to comparing actual crack growth rate with the deduced formula, the crack tip configuration factor is defined to figure out the crack tip opening configuration that is useful to clarify the behavior of fatigue crack tip formation apparently. Applying the concept, the crack growth of 7/3 brass and 6/4 brass is predicted from the formula, by replacing material properties such as plastic flow resistance, Young modulus, the Poisson ratio, and fatigue toughness, and fatigue test conditions such as the stress intensity factor range, the load ratio, and cycle frequency. Furthermore, the theoretically expected results are verified with the fatigue tests which were carried out on CT specimens under different load conditions of load ratio, cycle frequency, and cyclic peak load, in different environments of air or corrosive ammonia atmosphere, for various brasses. And by comparing and discussing the calculated crack growth rate with attained experimental results, the apparent configuration factor at the crack tip is determined. And through the attained factor which changes along with crack growth, the behaviors of fatigue crack tip formation under different test conditions have been found out.

Temperature dependence of liquid metal embrittlement susceptibility of a modified 9Cr-1Mo steel under low cycle fatigue in lead-bismuth eutectic at 160-450 °C

NASA Astrophysics Data System (ADS)

Gong, Xing; Marmy, Pierre; Qin, Ling; Verlinden, Bert; Wevers, Martine; Seefeldt, Marc

2016-01-01

Low cycle fatigue properties of a 9Cr-1Mo ferritic-martensitic steel (T91) have been tested in a low oxygen concentration (LOC) lead-bismuth eutectic (LBE) environment and in vacuum at 160-450 °C. The results show a clear fatigue endurance "trough" in LOC LBE, while no such a strong temperature dependence of the fatigue endurance is observed when the steel is tested in vacuum. The fractographic observations by means of scanning electron microscopy (SEM) show that ductile microdimples are prevalent on the fracture surfaces of the specimens tested in vacuum, whereas the fracture surfaces produced in LOC LBE at all the temperatures are characterized by quasi-cleavage. Interestingly, using electron backscatter diffraction (EBSD), martensitic laths close to the fatigue crack walls or to the fracture surfaces of the specimens tested in vacuum are found to have transformed into very fine equiaxed subgrains. Nevertheless, such microstructural modifications do not happen to the specimens tested in LOC LBE at 160-450 °C. These interesting microstructural distinctions indicate that liquid metal embrittlement (LME) is able to occur throughout the fatigue crack propagation phase in the full range of the temperatures investigated, i.e. LME is not very sensitive to temperature during the fatigue crack propagation.

Corrosion fatigue in nitrocarburized quenched and tempered steels

NASA Astrophysics Data System (ADS)

Khani, M. Karim; Dengel, D.

1996-05-01

In order to investigate the fatigue strength and fracture mechanism of salt bath nitrocarburized steels, specimens of the steels SAE 4135 and SAE 4140, in a quenched and tempered state, and additionally in a salt bath nitrocarburized and oxidizing cooled state as well as in a polished (after the oxidizing cooling) and renewed oxidized state, were subjected to comparative rotating bending fatigue tests in inert oil and 5 pct NaCl solution. In addition, some of the quenched and tempered specimens of SAE 4135 material were provided with an approximately 50-μm-thick electroless Ni-P layer, in order to compare corrosion fatigue behavior between the Ni-P layer and the nitride layers. Long-life corrosion fatigue tests of SAE 4135 material were carried out under small stresses in the long-life range up to 108 cycles with a test frequency of 100 Hz. Fatigue tests of SAE 4140 material were carried out in the range of finite life (low-cycle range) with a test frequency of 13 Hz. The results show that the 5 pct NaCl environment drastically reduced fatigue life, but nitrocarburizing plus oxidation treatment was found to improve the corrosion fatigue life over that of untreated and Ni-P coated specimens. The beneficial effect of nitrocarburizing followed by oxidation treatment on cor-rosion fatigue life results from the protection rendered by the compound layer by means of a well-sealed oxide layer, whereby the pores present in the compound layer fill up with oxides. The role of inclusions in initiating fatigue cracks was investigated. It was found that under corrosion fatigue conditions, the fatigue cracks started at cavities along the interfaces of MnS inclusions and matrix in the case of quenched and tempered specimens. The nitrocarburized specimens, however, showed a superposition of pitting corrosion and corrosion fatigue in which pores and nonmetallic inclusions in the compound layer play a predominant role concerning the formation of pits in the substrate.

Heat pipe fatigue test specimen: Metallurgical evaluation

NASA Technical Reports Server (NTRS)

Walak, Steven E.; Cronin, Michael J.; Grobstein, Toni

1992-01-01

An innovative creep/fatigue test was run to simulate the temperature, mechanical load, and sodium corrosion conditions expected in a heat pipe designed to supply thermal energy to a Stirling cycle power converter. A sodium-charged Inconel 718 heat pipe with a Nickel 200 screen wick was operated for 1090 hr at temperatures between 950 K (1250 F) and 1050 K (1430 F) while being subjected to creep and fatigue loads in a servo-hydraulic testing machine. After testing, the heat pipe was sectioned and examined using optical microscopy, scanning electron microscopy, and electron microprobe analysis with wavelength dispersive x-ray spectroscopy. The analysis concentrated on evaluating topographic, microstructural, and chemical changes in the sodium exposed surfaces of the heat pipe wall and wick. Surface changes in the evaporator, condenser, and adiabatic sections of the heat pipe were examined in an effort to correlate the changes with the expected sodium environment in the heat pipe. This report describes the setup, operating conditions, and analytical results of the sodium heat pipe fatigue test.

Corrosion Effects on the Fatigue Crack Propagation of Giga-Grade Steel and its Heat Affected Zone in pH Buffer Solutions for Automotive Application

NASA Astrophysics Data System (ADS)

Lee, H. S.

2018-03-01

Corrosion fatigue crack propagation test was conducted of giga-grade steel and its heat affected zone in pH buffer solutions, and the results were compared with model predictions. Pure corrosion effect on fatigue crack propagation, particularly, in corrosive environment was evaluated by means of the modified Forman equation. As shown in results, the average corrosion rate determined from the ratio of pure corrosion induced crack length to entire crack length under a cycle load were 0.11 and 0.37 for base metal and heat affected zone, respectively, with load ratio of 0.5, frequency of 0.5 and pH 10.0 environment. These results demonstrate new interpretation methodology for corrosion fatigue crack propagation enabling the pure corrosion effects on the behavior to be determined.

The increase in fatigue crack growth rates observed for Zircaloy-4 in a PWR environment

NASA Astrophysics Data System (ADS)

Cockeram, B. V.; Kammenzind, B. F.

2018-02-01

Cyclic stresses produced during the operation of nuclear reactors can result in the extension of cracks by processes of fatigue. Although fatigue crack growth rate (FCGR) data for Zircaloy-4 in air are available, little testing has been performed in a PWR primary water environment. Test programs have been performed by Gee et al., in 1989 and Picker and Pickles in 1984 by the UK Atomic Energy Authority, and by Wisner et al., in 1994, that have shown an enhancement in FCGR for Zircaloy-2 and Zircaloy-4 in high-temperature water. In this work, FCGR testing is performed on Zircaloy-4 in a PWR environment in the hydrided and non-hydrided condition over a range of stress-intensity. Measurements of crack extension are performed using a direct current potential drop (DCPD) method. The cyclic rate in the PWR primary water environment is varied between 1 cycle per minute to 0.1 cycle per minute. Faster FCGR rates are observed in water in comparison to FCGR testing performed in air for the hydrided material. Hydrided and non-hydrided materials had similar FCGR values in air, but the non-hydrided material exhibited much lower rates of FCGR in a PWR primary water environment than for hydrided material. Hydrides are shown to exhibit an increased tendency for cracking or decohesion in a PWR primary water environment that results in an enhancement in FCGR values. The FCGR in the PWR primary water only increased slightly with decreasing cycle frequency in the range of 1 cycle per minute to 0.1 cycle per minute. Comparisons between the FCGR in water and air show the enhancement from the PWR environment is affected by the applied stress intensity.

Environmentally assisted cracking in light water reactors.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chopra, O. K.; Chung, H. M.; Clark, R. W.

2007-11-06

This report summarizes work performed by Argonne National Laboratory on fatigue and environmentally assisted cracking (EAC) in light water reactors (LWRs) from January to December 2002. Topics that have been investigated include: (a) environmental effects on fatigue crack initiation in carbon and low-alloy steels and austenitic stainless steels (SSs), (b) irradiation-assisted stress corrosion cracking (IASCC) of austenitic SSs in BWRs, (c) evaluation of causes and mechanisms of irradiation-assisted cracking of austenitic SS in PWRs, and (d) cracking in Ni-alloys and welds. A critical review of the ASME Code fatigue design margins and an assessment of the conservation in the currentmore » choice of design margins are presented. The existing fatigue {var_epsilon}-N data have been evaluated to define the effects of key material, loading, and environmental parameters on the fatigue lives of carbon and low-alloy steels and austenitic SSs. Experimental data are presented on the effects of surface roughness on fatigue crack initiation in these materials in air and LWR environments. Crack growth tests were performed in BWR environments on SSs irradiated to 0.9 and 2.0 x 10{sup 21} n x cm{sup -2}. The crack growth rates (CGRs) of the irradiated steels are a factor of {approx}5 higher than the disposition curve proposed in NUREG-0313 for thermally sensitized materials. The CGRs decreased by an order of magnitude in low-dissolved oxygen (DO) environments. Slow-strain-rate tensile (SSRT) tests were conducted in high-purity 289 C water on steels irradiated to {approx}3 dpa. The bulk S content correlated well with the susceptibility to intergranular SCC in 289 C water. The IASCC susceptibility of SSs that contain >0.003 wt. % S increased drastically. bend tests in inert environments at 23 C were conducted on broken pieces of SSRT specimens and on unirradiated specimens of the same materials after hydrogen charging. The results of the tests and a review of other data in the literature indicate that IASCC in 289 C water is dominated by a crack-tip grain-boundary process that involves S. An initial IASCC model has been proposed. A crack growth test was completed on mill annealed Alloy 600 in high-purity water at 289 C and 320 C under various environmental and loading conditions. The results from this test are compared with data obtained earlier on several other heats of Alloy 600.« less

Fatigue performance of blade steel T552 in a corrosive environment

NASA Astrophysics Data System (ADS)

Janoušek, J.; Hřeben, S.; Špirit, Z.; Strejcius, J.; Kasl, J.

2017-02-01

This contribution is based on an experimental programme which deals with the issue of blade steel T552 corrosion fatigue damage. The specimens were taken from a reference material delivered for blade production and tested in a corrosion cell under pre-stress of 300 MPa. A chloride solution of 35 ppm was chosen as the environment at a temperature of 80 °C. Such an environment can be considered as the limit state that should not occur during the operating regime. The results are summarized and compared with experiments conducted at another workplace.

Compassion Satisfaction and Compassion Fatigue Among Critical Care Nurses.

PubMed

Sacco, Tara L; Ciurzynski, Susan M; Harvey, Megan Elizabeth; Ingersoll, Gail L

2015-08-01

Although critical care nurses gain satisfaction from providing compassionate care to patients and patients' families, the nurses are also at risk for fatigue. The balance between satisfaction and fatigue is considered professional quality of life. To establish the prevalence of compassion satisfaction and compassion fatigue in adult, pediatric, and neonatal critical care nurses and to describe potential contributing demographic, unit, and organizational characteristics. In a cross-sectional design, nurses were surveyed by using a demographic questionnaire and the Professional Quality of Life Scale to measure levels of compassion fatigue and compassion satisfaction. Nurses (n = 221) reported significant differences in compassion satisfaction and compassion fatigue on the basis of sex, age, educational level, unit, acuity, change in nursing management, and major systems change. Understanding the elements of professional quality of life can have a positive effect on work environment. The relationship between professional quality of life and the standards for a healthy work environment requires further investigation. Once this relationship is fully understood, interventions to improve this balance can be developed and tested. ©2015 American Association of Critical-Care Nurses.

Environmentally assisted cracking in light water reactors. Semiannual report, July 1998-December 1998.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chopra, O. K.; Chung, H. M.; Gruber, E. E.

This report summarizes work performed by Argonne National Laboratory on fatigue and environmentally assisted cracking (EAC) in light water reactors from July 1998 to December 1998. Topics that have been investigated include (a) environmental effects on fatigue S-N behavior of primary pressure boundary materials, (b) irradiation-assisted stress corrosion cracking of austenitic stainless steels (SSs), and (c) EAC of Alloys 600 and 690. Fatigue tests have been conducted to determine the crack initiation and crack growth characteristics of austenitic SSs in LWR environments. Procedures are presented for incorporating the effects of reactor coolant environments on the fatigue life of pressure vesselmore » and piping steels. Slow-strain-rate tensile tests and posttest fractographic analyses were conducted on several model SS alloys irradiated to {approx}0.3 and 0.9 x 10{sup 21} n {center_dot} cm{sup -2} (E > 1 MeV) in helium at 289 C in the Halden reactor. The results have been used to determine the influence of alloying and impurity elements on the susceptibility of these steels to irradiation-assisted stress corrosion cracking. Fracture toughness J-R curve tests were also conducted on two heats of Type 304 SS that were irradiated to {approx}0.3 x 10{sup 21} n {center_dot} cm{sup -2} in the Halden reactor. Crack-growth-rate tests have been conducted on compact-tension specimens of Alloys 600 and 690 under constant load to evaluate the resistance of these alloys to stress corrosion cracking in LWR environments.« less

Low Cycle Fatigue and Creep-Fatigue Behavior of Alloy 617 at High Temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cabet, Celine; Carroll, Laura; Wright, Richard

Alloy 617 is the leading candidate material for an intermediate heat exchanger (IHX) application of the Very High Temperature Nuclear Reactor (VHTR), expected to have an outlet temperature as high as 950 degrees C. Acceptance of Alloy 617 in Section III of the ASME Code for nuclear construction requires a detailed understanding of the creep-fatigue behavior. Initial creep-fatigue work on Alloy 617 suggests a more dominant role of environment with increasing temperature and/or hold times evidenced through changes in creep-fatigue crack growth mechanism/s and failure life. Continuous cycle fatigue and creep-fatigue testing of Alloy 617 was conducted at 950 degreesmore » C and 0.3% and 0.6% total strain in air to simulate damage modes expected in a VHTR application. Continuous cycle specimens exhibited transgranular cracking. Intergranular cracking was observed in the creep-fatigue specimens, although evidence of grain boundary cavitation was not observed. Despite the absence of grain boundary cavitation to accelerate crack propagation, the addition of a hold time at peak tensile strain was detrimental to cycle life. This suggests that creepfatigue interaction may occur by a different mechanism or that the environment may be partially responsible for accelerating failure.« less

The effect of microstructure on the tensile and fatigue behavior of Ti-22Al-23Nb in air and vacuum

NASA Astrophysics Data System (ADS)

Luetjering, Stephanie

Titanium aluminide alloys containing the ordered orthorhombic (O) phase, based on Ti2AlNb, exhibit high specific strengths at elevated temperature along with good room temperature tensile ductility and fracture toughness values. They are thus considered as potential materials for aerospace applications both in their monolithic form and as matrices in metal matrix composites. Microstructure/property relationships have been studied to a great extend with regard to tensile and creep properties. However, only little is known in the key areas of fatigue crack initiation, fatigue crack propagation and fatigue life. The main objective of this work therefore is to get a comprehensive understanding of the effects of microstructural parameters (such as volume fraction of the individual phases, their size and distribution) on the cyclic properties of O-based titanium aluminides. Furthermore, the performance of these alloys in aggressive environments, a critical issue for this alloy class, is being addressed. Tensile, isothermal fatigue, and fatigue crack growth (FCG) tests were conducted at 20°C and 540°C both in lab air and vacuum (pressure ≤ 1 x 10-6 torr) on three microstructural conditions of a representative O-based titanium alloy, Ti-22Al-23Nb. Results indicate a strong effect of microstructure on tensile and FCG properties, whereas only a slight influence of microstructure on the fatigue life is evident. The O phase contributes mainly to the material's yield stress. The tensile elongation is predominantly influenced by the beta phase volume fraction. The observed effect of microstructure on the FCG behavior is attributed to crack closure, crack front geometry and crystallographic texture. Environmental effects on the fatigue life are pronounced at elevated temperature and high applied stress amplitudes only. These conditions lead to premature crack initiation at the specimen's surface for testing in air, whereas testing in vacuum results in subsurface crack nucleation and an extended fatigue life of about two orders of magnitude. The FCG behavior is influenced by the environment at both 20°C and 540°C, proposing fatigue crack growth mechanisms enhanced by hydrogen embrittlement.

The mechanical and electrochemical properties of bulk metallic glasses

NASA Astrophysics Data System (ADS)

Morrison, Mark Lee

The objectives of this study were to define and model the electrochemical and mechanical behaviors of BMGs, in addition to the interactions between these. The electrochemical behaviors of Zr-, Ti-, and Ca-based BMGs have been studied in various environments. Moreover, the electrochemical behaviors of several common, crystalline materials have also been characterized in the same environments to facilitate comparisons. Mechanical characterization of the Vitreloy 105 alloy was conducted through four-point bend fatigue testing, as well as tensile testing with in situ thermography. After the electrochemical and mechanical behaviors of the Vit 105 BMG alloy were defined separately, the corrosion-fatigue behavior of this alloy was studied. Corrosion-fatigue tests were conducted in a 0.6 M NaCl electrolyte, identical to one of the environments in which the electrochemical behavior was previously defined. The environmental effect was found to be significant at most stress levels, with decreasing effects at higher stress levels due to decreasing time in the detrimental environment, and severely depressed the corrosion-fatigue endurance limit. Cyclic-anodic-polarization tests were conducted during cyclic loading to elucidate the effect of cyclic stresses on the electrochemical behavior. It was found that a stress range of 900 MPa resulted in active pitting at the open-circuit potentials. The degradation mechanism was determined to be stress-assisted dissolution, not hydrogen embrittlement. Finally, tensile tests were conducted with the Vit 105 BMG alloy with in situ infrared (IR) thermography to observe the evolution of shear bands during deformation. More importantly, the length, location, sequence, temperature evolution, and velocity of individual shear bands have been quantified through the use of IR thermography. Based upon all of these studies on a variety of BMG alloy systems, the most important factor in the mechanical and electrochemical behavior was found to be material quality and homogeneity. Therefore, future research on the improvement of BMG alloys should be focused on this area.

Environmentally assisted cracking in light water reactors : semiannual report, July 2000 - December 2000.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chopra, O. K.; Chung, H. M.; Gruber, E. E.

This report summarizes work performed by Argonne National Laboratory on fatigue and environmentally assisted cracking (EAC) in light water reactors (LWRs) from July 2000 to December 2000. Topics that have been investigated include (a) environmental effects on fatigue S-N behavior of primary pressure boundary materials, (b) irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steels (SSs), and (c) EAC of Alloys 600 and 690. The fatigue strain-vs.-life data are summarized for the effects of various material, loading, and environmental parameters on the fatigue lives of carbon and low-alloy steels and austenitic SSs. Effects of the reactor coolant environment on themore » mechanism of fatigue crack initiation are discussed. Two methods for incorporating the effects of LWR coolant environments into the ASME Code fatigue evaluations are presented. Slow-strain-rate tensile tests and posttest fractographic analyses were conducted on several model SS alloys irradiated to {approx}0.9 x 10{sup 21} n {center_dot} cm{sup -2} (E > 1 MeV) in He at 289 C in the Halden reactor. The results were used to determine the influence of alloying and impurity elements on the susceptibility of these steels to IASCC. A fracture toughness J-R curve test was conducted on a commercial heat of Type 304 SS that was irradiated to {approx}2.0 x 10{sup 21} n {center_dot} cm{sup -2} in the Halden reactor. The results were compared with the data obtained earlier on steels irradiated to 0.3 and 0.9 x 10{sup 21} n {center_dot} cm{sup -2} (E > 1 MeV) (0.45 and 1.35 dpa). Neutron irradiation at 288 C was found to decrease the fracture toughness of austenitic SSs. Tests were conducted on compact-tension specimens of Alloy 600 under cyclic loading to evaluate the enhancement of crack growth rates in LWR environments. Then, the existing fatigue crack growth data on Alloys 600 and 690 were analyzed to establish the effects of temperature, load ratio, frequency, and stress intensity range on crack growth rates in air.« less

Evaluation of corrosion fatigue and life prediction of lower arm for automotive suspension component

NASA Astrophysics Data System (ADS)

Kim, Yong-Sang; Kim, Jung-Gu

2017-01-01

Lower arm is one of the suspension components of automobile. It is suffered from driving vibration and corrosive environment, namely corrosion fatigue. In this study, corrosion fatigue property of lower arm was investigated, and a modified model based on Palmgren-Miner rule was developed to predict the lifetimes of corrosion fatigue. The corrosion fatigue life of lower arm was about 1/6 times shorter than fatigue life. Based on the results of corrosion fatigue tests and meteorological data in Seoul and Halifax, the corrosion fatigue life of lower arm was predicted. The satisfaction of 10-year and 300,000 km warranty was dominated by the climate of automobile driving. This prediction indicates that the weather condition or driving condition influences the life of automotive parts. Therefore, to determine the warranty of automotive parts, the driving condition has to be carefully considered.

Effect of NaCl Solution Spraying on Fatigue Lives of Smooth and Slit Specimens of 0.37% Carbon Steel

NASA Astrophysics Data System (ADS)

Makabe, Chobin; Ferdous, Md. Shafiul; Shimabukuro, Akimichi; Murdani, Anggit

2017-07-01

The fatigue crack initiation life and growth rate are affected by experimental conditions. A corrosive environment can be created in a laboratory by means of dropping salt water onto the specimen surface, spraying chloride mist into the experimental chamber, etc. In the case of smooth specimens of some metals, fatigue life is shortened and the fatigue limit disappears under such corrosive experimental conditions. In this study, the effects of intermittent spraying of 3% NaCl solution-mist on corrosion fatigue behavior were investigated. The material used was 0.37% carbon steel. This is called JIS S35C in Japan. Spraying of 3% NaCl solution-mist attacked the surface layer of the specimen. It is well known that the pitting, oxidation-reduction reaction, etc. affect the fatigue strength of metals in a corrosive environment. We carried out corrosion fatigue tests with smooth specimens, holed specimens and slit specimens. Then the effects of such specimen geometry on the fatigue strength were investigated when the NaCl solution-mist was sprayed onto the specimen surface. In the case of lower stress amplitude application in slit specimens, the fatigue life in a corrosive atmosphere was longer than that in the open air. It is discussed that the behavior is related to the crack closure which happens when the oxide builds up and clogs the crack or slit.

Kinetics of Accumulation of Damage in Surface Layers of Lithium-Containing Aluminum Alloys in Fatigue Tests with Rigid Loading Cycle and Corrosive Effect of Environment

NASA Astrophysics Data System (ADS)

Morozova, L. V.; Zhegina, I. P.; Grigorenko, V. B.; Fomina, M. A.

2017-07-01

High-resolution methods of metal physics research including electron, laser and optical microscopy are used to study the kinetics of the accumulation of slip lines and bands and the corrosion damage in the plastic zone of specimens of aluminum-lithium alloys 1441 and B-1469 in rigid-cycle fatigue tests under the joint action of applied stresses and corrosive environment. The strain parameters (the density of slip bands, the sizes of plastic zones near fracture, the surface roughness in singled-out zones) and the damage parameters (the sizes of pits and the pitting area) are evaluated.

Creep fatigue life prediction for engine hot section materials (isotropic)

NASA Technical Reports Server (NTRS)

Nelson, R. S.; Levan, G. W.; Schoendorf, J. F.

1992-01-01

A series of high temperature strain controlled fatigue tests have been completed to study the effects of thermomechanical fatigue, multiaxial loading, reactive environments, and imposed mean stresses. The baseline alloy used in these tests was cast B1900+Hf (with and without coatings); a small number of tests of wrought INCO 718 are also included. A strong path dependence was demonstrated during the thermomechanical fatigue testing, using in-phase, out-phase, and non-proportional (elliptical and 'dogleg') strain-temperature cycles. The multiaxial tests also demonstrated cycle path to be a significant variable, using both proportional and non-proportional tension-torsion loading. Environmental screening tests were conducted in moderate pressure oxygen and purified argon; the oxygen reduced the specimen lives by two, while the argon testing produced ambiguous data. Both NiCoCrAlY overlay and diffusion aluminide coatings were evaluated under isothermal and TMF conditions; in general, the lives of the coated specimens were higher that those of uncoated specimens. Controlled mean stress TMF tests showed that small mean stress changes could change initiation lives by orders of magnitude; these results are not conservatively predicted using traditional linear damage summation rules. Microstructures were evaluated using optical, SEM and TEM methods.

High Pressure Oxidizer Turbopump (HPOTP) inducer dynamic design environment

NASA Technical Reports Server (NTRS)

Herda, D. A.; Gross, R. S.

1995-01-01

The dynamic environment must be known to evaluate high pressure oxidizer turbopump inducer fatigue life. This report sets the dynamic design loads for the alternate turbopump inducer as determined by water-flow rig testing. Also, guidelines are given for estimating the dynamic environment for other inducer and impeller applications.

Ceramic Matrix Composite Characterization Under a Combustion and Loading Environment

DTIC Science & Technology

2009-03-01

work showed that the material is sensitive in fatigue to center holes above 84% UTS. Barth Boyer did fatigue and creep testing double edge notched...panel obtained for this test was also used in previous AFIT thesis work by Boyer . It is a 12 in x 12 in panel consisting of an eight harness satin...weave with a [0°/90°] fiber orientation. The panel number is 4569-2. The panel properties obtained by Boyer are in Table 3. 17 Table 3

Removal Torque and Biofilm Accumulation at Two Dental Implant-Abutment Joints After Fatigue.

PubMed

Pereira, Jorge; Morsch, Carolina S; Henriques, Bruno; Nascimento, Rubens M; Benfatti, Cesar Am; Silva, Filipe S; López-López, José; Souza, Júlio Cm

2016-01-01

The aim of this study was to evaluate the removal torque and in vitro biofilm penetration at Morse taper and hexagonal implant-abutment joints after fatigue tests. Sixty dental implants were divided into two groups: (1) Morse taper and (2) external hexagon implant-abutment systems. Fatigue tests on the implant-abutment assemblies were performed at a normal force (FN) of 50 N at 1.2 Hz for 500,000 cycles in growth medium containing human saliva for 72 hours. Removal torque mean values (n = 10) were measured after fatigue tests. Abutments were then immersed in 1% protease solution in order to detach the biofilms for optical density and colony-forming unit (CFU/cm²) analyses. Groups of implant-abutment assemblies (n = 8) were cross-sectioned at 90 degrees relative to the plane of the implant-abutment joints for the microgap measurement by field-emission guns scanning electron microscopy. Mean values of removal torque on abutments were significantly lower for both Morse taper (22.1 ± 0.5 μm) and external hexagon (21.1 ± 0.7 μm) abutments after fatigue tests than those recorded without fatigue tests (respectively, 24 ± 0.5 μm and 24.8 ± 0.6 μm) in biofilm medium for 72 hours (P = .04). Mean values of microgap size for the Morse taper joints were statistically signicantly lower without fatigue tests (1.7 ± 0.4 μm) than those recorded after fatigue tests (3.2 ± 0.8 μm). Also, mean values of microgap size for external hexagon joints free of fatigue were statistically signicantly lower (1.5 ± 0.4 μm) than those recorded after fatigue tests (8.1 ± 1.7 μm) (P < .05). The optical density of biofilms and CFU mean values were lower on Morse taper abutments (Abs630nm at 0.06 and 2.9 × 10⁴ CFU/cm²) than that on external hexagon abutments (Abs630nm at 0.08 and 4.5 × 10⁴ CFU/cm²) (P = .01). The mean values of removal torque, microgap size, and biofilm density recorded at Morse taper joints were lower in comparison to those recorded at external hexagon implant-abutment joints after fatigue tests in a simulated oral environment for 72 hours.

Low cycle fatigue of PM/HIP astroloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Choe, S.J.; Stoloff, N.S.; Duquette, D.J.

Low cycle fatigue and creep-fatigue-environment interactions of PM/HIP Astrology were studied at 650 C and 725 C. Total strain range was varied from 1.5% to 2.7% at a frequency of 0.3Hz. Creep-fatigue tests were performed with 2 min. or 5 min. tensile hold times. All tests were run in high purity argon in an attempt to minimize environmental effects. Employing a tensile hold was more damaging than raising temperature by 75 C. Slopes of Coffin-Manson plots were nearly independent of temperature and hold time. Raising temperature from 650 C to 725 C did not change the transgranular (TG) crack propagationmore » mode, whereas employing hold times caused TG+IG propagation. All samples displayed multiple fracture origins associated with inclusions located at the specimen surface; pre-existing pores did not affect fatigue crack initiation. Examination of secondary cracks showed no apparent creep damage. Oxidation in high purity argon appeared to be the major factor in LCF life degradation due to hold times.« less

How oral environment simulation affects ceramic failure behavior.

PubMed

Lodi, Ediléia; Weber, Kátia R; Benetti, Paula; Corazza, Pedro H; Della Bona, Álvaro; Borba, Márcia

2018-05-01

Investigating the mechanical behavior of ceramics in a clinically simulated scenario contributes to the development of new and tougher materials, improving the clinical performance of restorations. The optimal in vitro environment for testing is unclear. The purpose of this in vitro study was to investigate the failure behavior of a leucite-reinforced glass-ceramic under compression loading and fatigue in different simulated oral environment conditions. Fifty-three plate-shaped ceramic specimens were produced from computer-aided design and computer-aided manufactured (CAD-CAM) blocks and adhesively cemented onto a dentin analog substrate. For the monotonic test (n=23), a gradual compressive load (0.5 mm/min) was applied to the center of the specimens, immersed in 37ºC water, using a universal testing machine. The initial crack was detected with an acoustic system. The fatigue test was performed in a mechanical cycling machine (37ºC water, 2 Hz) using the boundary technique (n=30). Two lifetimes were evaluated (1×10 6 and 2×10 6 cycles). Failure analysis was performed using transillumination. Weibull distribution was used to evaluate compressive load data. A cumulative damage model with an inverse power law (IPL) lifetime-stress relationship was used to fit the fatigue data. A characteristic failure load of 1615 N and a Weibull modulus of 5 were obtained with the monotonic test. The estimated probability of failure (P f ) for 1×10 6 cycles at 100 N was 31%, at 150 N it was 55%, and at 200 N it was 75%. For 2×10 6 cycles, the P f increased approximately 20% in comparison with the values predicted for 1×10 6 cycles, which was not significant. The most frequent failure mode was a radial crack from the intaglio surface. For fatigue, combined failure modes were also found (radial crack combined with cone crack or chipping). Fatigue affects the fracture load and failure mode of leucite-reinforced glass-ceramic. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Corrosion-fatigue of laser-repaired commercially pure titanium and Ti-6Al-4V alloy under different test environments.

PubMed

Zavanelli, R A; Guilherme, A S; Pessanha-Henriques, G E; de Arruda Nóbilo, M Antônio; Mesquita, M F

2004-10-01

This study evaluated the corrosion-fatigue life of laser-repaired specimens fabricated from commercially pure titanium (CP Ti) and Ti-6Al-4V alloy, tested under different storage conditions. For each metal, 30 dumbbell rods with a central 2.3 mm diameter were prepared by lost-wax casting with the Rematitan System. Simulating the failure after service, corrosion-fatigue life in different media at room temperature (air, synthetic saliva and fluoride synthetic saliva) was determined at a testing frequency of 10 Hz for intact specimens and after laser repairing, using a square waveform with equal maximum tensile and compressive stress that was 30% lower than the 0.2% offset yield strength. For laser welding, the fractured specimens were rejoined using a jig to align the sections invested in type-IV dental stone. The adjacent areas of the gap was air-abraded with 100 microm aluminum oxide, laser welded and retested under the same conditions as the initial intact specimens. The number of cycles at failure was recorded, and the fracture surface was examined with a scanning electron microscope (SEM). The number of cycles for failure of the welded and intact specimens was compared by anova and the Tukey test at a 5% probability level. Within the limitations of this study, the number of cycles required for fracture decreased in wet environments and the laser repairing process adversely affected the life of both metals under the corrosion-fatigue conditions.

The European Spacelab structural design evolution

NASA Technical Reports Server (NTRS)

Thirkettle, A. J.

1982-01-01

Spacelab is a manned, reusable laboratory which is being developed for the European Space Agency (ESA). In its working mode it will fly in low earth orbit in the cargo bay of the Shuttle Transportation System (STS) Orbiter. A description is presented of the structural development of the various features of Spacelab. System requirements are considered along with structural requirements, quasi-static loads, acoustic loads, pressure loads, crash loads, ground loads, and the fatigue profile. Aspects of thermal environment generation are discussed, and questions regarding the design evolution of the pallet structure are examined. Details of pallet structure testing are reported, taking into account static strength tests, acoustic tests, the modal survey test, crash tests, and fatigue/fracture mechanics testing.

Compressive Strength of Notched Poly(Phenylene Sulfide) Aerospace Composite: Influence of Fatigue and Environment

NASA Astrophysics Data System (ADS)

Niitsu, G. T.; Lopes, C. M. A.

2013-08-01

The purpose of this work is to evaluate the influences of fatigue and environmental conditions (-55 °C, 23 °C, and 82 °C/Wet) on the ultimate compression strength of notched carbon-fiber-reinforced poly(phenylene sulfide) composites by performing open-hole compression (OHC) tests. Analysis of the fatigue effect showed that at temperatures of -55 and 23 °C, the ultimate OHC strengths were higher for fatigued than for not-fatigued specimens; this could be attributed to fiber splitting and delamination during fatigue cycling, which reduces the stress concentration at the hole edge, thus increasing the composite strength. This effect of increasing strength for fatigued specimens was not observed under the 82 °C/Wet conditions, since the test temperature near the matrix glass transition temperature ( T g) together with moisture content resulted in matrix softening, suggesting a reduction in fiber splitting during cycling; similar OHC strengths were verified for fatigued and not-fatigued specimens tested at 82 °C/Wet. Analysis of the temperature effect showed that the ultimate OHC strengths decreased with increasing temperature. A high temperature together with moisture content (82 °C/Wet condition) reduced the composite compressive strengths, since a temperature close to the matrix T g resulted in matrix softening, which reduced the lateral support provided by the resin to the 0° fibers, leading to fiber instability failure at reduced applied loads. On the other hand, a low temperature (-55 °C) improved the compressive strength because of possible fiber-matrix interfacial strengthening, increasing the fiber contribution to compressive strength.

Closed-Loop Control for Sonic Fatigue Testing Systems

NASA Technical Reports Server (NTRS)

Rizzi, Stephen A.; Bossaert, Guido

2001-01-01

This article documents recent improvements to the acoustic control system of the Thermal Acoustic Fatigue Apparatus (TAFA), a progressive wave tube test facility at the NASA Langley Research Center, Hampton, VA. A brief summary of past acoustic performance is first given to serve as a basis of comparison with the new performance data using a multiple-input, closed-loop, narrow-band controller. Performance data in the form of test section acoustic power spectral densities and coherence are presented for a variety of input spectra including uniform, band-limited random and an expendable launch vehicle payload bay environment.

Low cycle fatigue properties of MAR-M-246 Hf in hydrogen. [a cast nickel-base alloy

NASA Technical Reports Server (NTRS)

Warren, J. R.

1979-01-01

The transverse, low cycle fatigue properties were determined for directionally solidified and single crystal samples of a cast nickel-base alloy proposed for use in space propulsion systems in pure or partial high pressure hydrogen environments at elevated temperatures. The test temperature was 760 C (1400F) and the pressure of the gaseous hydrogen was 34.5 MPa (5000 psig). Low cycle fatique life was established by strain controlled testing using smooth specimens and a servohydraulic closed-loop test machine modified with a high pressure environmental chamber. Results and conclusions are discussed.

Fatigue properties of type 316LN stainless steel in air and mercury

NASA Astrophysics Data System (ADS)

Strizak, J. P.; Tian, H.; Liaw, P. K.; Mansur, L. K.

2005-08-01

An extensive fatigue testing program on 316LN stainless steel was recently carried out to support the design of the mercury target container for the spallation neutron source (SNS) that is currently under construction at the Oak Ridge National Laboratory in the United States. The major objective was to determine the effects of mercury on fatigue behavior. The S- N fatigue behavior of 316LN stainless steel is characterized by a family of bilinear fatigue curves which are dependent on frequency, environment, mean stress and cold work. Generally, fatigue life increases with decreasing stress and levels off in the high cycle region to an endurance limit below which the material will not fail. For fully reversed loading as well as tensile mean stress loading conditions mercury had no effect on endurance limit. However, at higher stresses a synergistic relationship between mercury and cyclic loading frequency was observed at low frequencies. As expected, fatigue life decreased with decreasing frequency, but the response was more pronounced in mercury compared with air. As a result of liquid metal embrittlement (LME), fracture surfaces of specimens tested in mercury showed widespread brittle intergranular cracking as opposed to typical transgranular cracking for specimens tested in air. For fully reversed loading (zero mean stress) the effect of mercury disappeared as frequency increased to 10 Hz. For mean stress conditions with R-ratios of 0.1 and 0.3, LME was still evident at 10 Hz, but at 700 Hz the effect of mercury had disappeared ( R = 0.1). Further, for higher R-ratios (0.5 and 0.75) fatigue curves for 10 Hz showed no environmental effect. Finally, cold working (20%) increased tensile strength and hardness, and improved fatigue resistance. Fatigue behavior at 10 and 700 Hz was similar and no environmental effect was observed.

Fatigue life prediction of bonded primary joints

NASA Technical Reports Server (NTRS)

Knauss, J. F.

1979-01-01

The validation of a proposed fatigue life prediction methodology was sought through the use of aluminum butt and scarf joint and graphite/epoxy butt joint specimens in a constant amplitude fatigue environment. The structural properties of the HYSOL 9313 adhesive system were obtained by mechanical test of molded heat adhesive specimens. Aluminum contoured double cantilever beam specimens were used to generate crack velocity versus stress intensity factor data. The specific objectives were: (1) to ascertain the feasibility of predicting fatigue failure of an adhesive in a primary bonded composite structure by incorporating linear elastic crack growth behavior; and (2) to ascertain if acoustic emission and/or compliance measurement techniques can be used to detect flaws.

Fatigue damage characterization of braided and woven fiber reinforced polymer matrix composites at room and elevated temperatures

NASA Astrophysics Data System (ADS)

Montesano, John

The use of polymer matrix composites (PMC) for manufacturing primary load-bearing structural components has significantly increased in many industrial applications. Specifically in the aerospace industry, PMCs are also being considered for elevated temperature applications. Current aerospace-grade composite components subjected to fatigue loading are over-designed due to insufficient understanding of the material failure processes, and due to the lack of available generic fatigue prediction models. A comprehensive literature survey reveals that there are few fatigue studies conducted on woven and braided fabric reinforced PMC materials, and even fewer at elevated temperatures. It is therefore the objective of this study to characterize and subsequently model the elevated temperature fatigue behaviour of a triaxial braided PMC, and to investigate the elevated temperature fatigue properties of two additional woven PMCs. An extensive experimental program is conducted using a unique test protocol on the braided and woven composites, which consists of static and fatigue testing at various test temperatures. The development of mechanically-induced damage is monitored using a combination of non-destructive techniques which included infrared thermography, fiber optic sensors and edge replication. The observed microscopic damage development is quantified and correlated to the exhibited macroscopic material behaviour at all test temperatures. The fiber-dominated PMC materials considered in this study did not exhibit notable time- or temperature-dependent static properties. However, fatigue tests reveal that the local damage development is in fact notably influenced by temperature. The elevated temperature environment increases the toughness of the thermosetting polymers, which results in consistently slower fatigue crack propagation rates for the respective composite materials. This has a direct impact on the stiffness degradation rate and the fatigue lives for the braided and woven composites under investigation. The developed analytical fatigue damage prediction model, which is based on actual observed damage mechanisms, accurately predicted the development of damage and the corresponding stiffness degradation for the braided PMC, for all test temperatures. An excellent correlation was found between the experimental and the predicted results to within a 2% accuracy. The prediction model adequately captured the local temperature-induced phenomenon exhibited by the braided PMC material. The results presented in this study are novel for a braided composite material subjected to elevated temperature fatigue.

Durability of polymer/metal interfaces under cyclic loading

NASA Astrophysics Data System (ADS)

Du, Tianbao

Fatigue crack growth along metal/epoxy interface was examined in an aqueous environment and under mixed-mode conditions. A stress corrosion cracking mechanism was identified in this process. The fatigue crack growth rate in an aqueous environment was increased by several orders of magnitude and the fatigue threshold decreased by a factor of 10. The loss of adhesion in the aqueous environment was induced by the hydration of the surface oxide which resulted in a hydroxide with poor adhesion to the substrate metal. Self-assembled monolayer of long chain alkyl phosphonic acid and amino phosphonic acid were synthesized to enhance the adhesion and improve the durability of Al/epoxy interfacial bonding system. The same approach was taken to promote adhesion between copper and epoxy, where a two-component coupling system of 11-mercapto-1-undercanol and 3-aminopropyltriethoxysilane provided the most significant improvement in the copper/epoxy adhesion. The mixed-mode was applied by a piezoelectric actuator. Subcritical crack growth was observed along the epoxy/aluminum interface and the growth rate was found to depend on the magnitude of the applied electric field. Kinetics of the crack growth was correlated with the piezoelectric driving force. The resulting crack growth behavior was compared with the results from the conventional mechanical testing technique. Large differences were found between these two methods. Using this newly developed technique, effects of loading mode and frequency were studied. The fatigue resistance was found to increase with the mode II component and was expressed as a function of the KII/K I ratio. A strong frequency effect was observed for the subcritical crack growth along the Al/Epoxy interface, their fatigue resistance increased with the testing frequency.

Fatigue crack monitoring with coupled piezoelectric film acoustic emission sensors

NASA Astrophysics Data System (ADS)

Zhou, Changjiang

Fatigue-induced cracking is a commonly seen problem in civil infrastructures reaching their original design life. A number of high-profile accidents have been reported in the past that involved fatigue damage in structures. Such incidences often happen without prior warnings due to lack of proper crack monitoring technique. In order to detect and monitor the fatigue crack, acoustic emission (AE) technique, has been receiving growing interests recently. AE can provide continuous and real-time monitoring data on damage progression in structures. Piezoelectric film AE sensor measures stress-wave induced strain in ultrasonic frequency range and its feasibility for AE signal monitoring has been demonstrated recently. However, extensive work in AE monitoring system development based on piezoelectric film AE sensor and sensor characterization on full-scale structures with fatigue cracks, have not been done. A lack of theoretical formulations for understanding the AE signals also hinders the use of piezoelectric film AE sensors. Additionally, crack detection and source localization with AE signals is a very important area yet to be explored for this new type of AE sensor. This dissertation presents the results of both analytical and experimental study on the signal characteristics of surface stress-wave induced AE strain signals measured by piezoelectric film AE sensors in near-field and an AE source localization method based on sensor couple theory. Based on moment tensor theory, generalized expression for AE strain signal is formulated. A special case involving the response of piezoelectric film AE sensor to surface load is also studied, which could potentially be used for sensor calibration of this type of sensor. A new concept of sensor couple theory based AE source localization technique is proposed and validated with both simulated and experimental data from fatigue test and field monitoring. Two series of fatigue tests were conducted to perform fatigue crack monitoring on large-scale steel test specimens using piezoelectric film AE sensors. Continuous monitoring of fatigue crack growth in steel structures is demonstrated in these fatigue test specimens. The use of piezoelectric film AE sensor for field monitoring of existing fatigue crack is also demonstrated in a real steel I-girder bridge located in Maryland. The sensor couple theory based AE source localization is validated using a limited number of piezoelectric film AE sensor data from both fatigue test specimens and field monitoring bridge. Through both laboratory fatigue test and field monitoring of steel structures with active fatigue cracks, the signal characteristics of piezoelectric film AE sensor have been studied in real-world environment.

Ares I-X USS Material Testing

NASA Technical Reports Server (NTRS)

Dawicke, David S.; Smith, Stephen W.; Raju, Ivatury S.

2008-01-01

An independent assessment was conducted to determine the critical initial flaw size (CIFS) for the flange-to-skin weld in the Ares I-X Upper Stage Simulator (USS). Material characterization tests were conducted to quantify the material behavior for use in the CIFS analyses. Fatigue crack growth rate, Charpy impact, and fracture tests were conducted on the parent and welded A516 Grade 70 steel. The crack growth rate tests confirmed that the material behaved in agreement with literature data and that a salt water environment would not significantly degrade the fatigue resistance. The Charpy impact tests confirmed that the fracture resistance of the material did not have a significant reduction for the expected operational temperatures of the vehicle.

Sonic environment tests of an insulator/ablator material

NASA Technical Reports Server (NTRS)

Jackson, L. R.; Taylor, A. H.; Rucker, C. E.

1977-01-01

A 50.8 cm (20 inch) square panel of perpyrolized insulator/ablator was subjected to six 30-minute tests at 160 and 158 dB in the Langley Thermo-Acoustic Fatigue Apparatus (TAFA). This environment simulates the aerodynamic and engine noise encountered by a research airplane while in captive flight on the B-52 pylon during takeoff and climb. The pyrolized layer sustained damage in the form of three chips and numerous cracks. The chips occurred during the first test. Some cracking resulted during aerodynamic heating tests, and additional cracking resulted from the sonic environment tests.

An Experimental Investigation of the Effects of Vacuum Environment on the Fatigue Life, Fatigue-Crack-Growth Behavior, and Fracture Toughness of 7075-T6 Aluminum Alloy. Ph.D. Thesis - North Carolina State Univ.

NASA Technical Reports Server (NTRS)

Hudson, C. M.

1972-01-01

Axial load fatigue life, fatigue-crack propagation, and fracture toughness tests were conducted on 0.090-inch thick specimens made of 7075-T6 aluminum alloy. The fatigue life and fatigue-crack propagation experiments were conducted at a stress ratio of 0.02. Maximum stresses ranged from 33 to 60 ksi in the fatigue life experiments, and from 10 to 40 ksi in the fatigue-crack propagation experiments, and fatigue life experiments were conducted at gas pressures of 760, 0.5, 0.05, and 0.00000005 torr. Fatigue-crack-growth and fracture toughness experiments were conducted at gas pressures of 760 and 5 x 10 to the minus 8th power torr. Residual stress measurements were made on selected fatigue life specimens to determine the effect of such stresses on fatigue life. Analysis of the results from the fatigue life experiments indicated that fatigue life progressively increased as the gas pressure decreased. Analysis of the results from the fatigue-crack-growth experiments indicates that at low values of stress-intensity range, the fatigue crack growth rates were approximately twice as high in air as in vacuum. Fracture toughness data showed there was essentially no difference in the fracture toughness of 7075-T6 in vacuum and in air.

A Fatigue Life Prediction Model of Welded Joints under Combined Cyclic Loading

NASA Astrophysics Data System (ADS)

Goes, Keurrie C.; Camarao, Arnaldo F.; Pereira, Marcos Venicius S.; Ferreira Batalha, Gilmar

2011-01-01

A practical and robust methodology is developed to evaluate the fatigue life in seam welded joints when subjected to combined cyclic loading. The fatigue analysis was conducted in virtual environment. The FE stress results from each loading were imported to fatigue code FE-Fatigue and combined to perform the fatigue life prediction using the S x N (stress x life) method. The measurement or modelling of the residual stresses resulting from the welded process is not part of this work. However, the thermal and metallurgical effects, such as distortions and residual stresses, were considered indirectly through fatigue curves corrections in the samples investigated. A tube-plate specimen was submitted to combined cyclic loading (bending and torsion) with constant amplitude. The virtual durability analysis result was calibrated based on these laboratory tests and design codes such as BS7608 and Eurocode 3. The feasibility and application of the proposed numerical-experimental methodology and contributions for the technical development are discussed. Major challenges associated with this modelling and improvement proposals are finally presented.

Fatigue of titanium alloys in a supersonic-cruise airplane environment

NASA Technical Reports Server (NTRS)

Imig, L. A.

1976-01-01

The test programs conducted by several aerospace companies and NASA, summarized in this paper, studied several titanium materials previously identified as having high potential for application to supersonic cruise airplane structures. These studies demonstrate that the temperature (560 K) by itself produced no significant degradation of the materials. However, the fatigue resistance of titanium-alloy structures, in which thermal and loading effects are combined, has been studied insufficiently. The predominant topic for future study of fatigue problems in Mach 3 structures should be the influences of thermal stress particularly, the effects of thermal stress on failure location.

Urban Options for Psychological Restoration: Common Strategies in Everyday Situations.

PubMed

Staats, Henk; Jahncke, Helena; Herzog, Thomas R; Hartig, Terry

2016-01-01

Given the need for knowledge on the restorative potential of urban settings, we sought to estimate the effects of personal and contextual factors on preferences and restoration likelihood assessments for different urban activities-in-environments. We also sought to study the generality of these effects across different countries. We conducted a true experiment with convenience samples of university students in the Netherlands (n = 80), Sweden (n = 100), and the USA (n = 316). In each country, the experiment had a mixed design with activities-in-environments (sitting in a park, sitting in a cafe, walking in a shopping mall, walking along a busy street) manipulated within-subjects and the need for restoration (attentional fatigue, no attentional fatigue) and immediate social context (in company, alone) manipulated between-subjects. The manipulations relied on previously tested scenarios describing everyday situations that participants were instructed to remember and imagine themselves being in. For each imagined situation (activity-in-environment with antecedent fatigue condition and immediate social context), subjects provided two criterion measures: general preference and the likelihood of achieving psychological restoration. The settings received different preference and restoration likelihood ratings as expected, affirming that a busy street, often used in comparisons with natural settings, is not representative of the restorative potential of urban settings. Being with a close friend and attentional fatigue both moderated ratings for specific settings. Findings of additional moderation by country of residence caution against broad generalizations regarding preferences for and the expected restorative effects of different urban settings. Preferences and restoration likelihood ratings for urban activity-environment combinations are subject to multiple personal and contextual determinants, including level of attentional fatigue, being alone versus in company, and broader aspects of the urban context that vary across cities and countries. Claims regarding a lack of restorative quality in urban environments are problematic.

Test Method for the Fatigue Life of Layered TiB/Ti Functionally Graded Beams Subjected to Fully Reversed Bending

NASA Astrophysics Data System (ADS)

Byrd, Larry; Rickerd, Greg; Wyen, Travis; Cooley, Glenn; Quast, Jeff

2008-02-01

Sonic fatigue of aircraft is characterized by fully reversed bending of components subjected to acoustic excitation. This problem is compounded in high temperature environments because solutions for acoustics which tend to result in stiff structures make thermal problems worse. Conversely solutions to the thermal problem which allow expansion often fail in the presence of high acoustic levels. Errors in fatigue life prediction in the combined environment often range from a factor of 4 to 10. This results in either heavy, overly stiff structure or premature failure. This work will test the hypothesis that the fatigue life of a layered functionally graded material (FGM) will be dominated by the failure of the stiffest outer layer. This is based on the observation that for isotropic materials the life is approximately 90% crack initiation and only 10% crack growth before failure. Four sets of cantilever specimens will be tested using an electro-mechanical shaker for base excitation. The excitation will be narrow band random around the fundamental frequency. Two sets of specimens are of uniform composition consisting of 85%TiB/Ti and two are graded specimens consisting of layers that vary from commercially pure titanium to 85%TiB/Ti. Strain vs number of cycles to failure curves will be generated with both constant amplitude sine and narrow band random around the fundamental frequency excitation. The results will be examined to compare life of the uniform material to the functionally graded material. Also to be studied will be the use of Miner's rule to predict the fatigue life of the randomly excited specimens.

Slow crack growth in spinel in water

NASA Technical Reports Server (NTRS)

Schwantes, S.; Elber, W.

1983-01-01

Magnesium aluminate spinel was tested in a water environment at room temperature to establish its slow crack-growth behavior. Ring specimens with artificial flaws on the outside surface were loaded hydraulically on the inside surface. The time to failure was measured. Various precracking techniques were evaluated and multiple precracks were used to minimize the scatter in the static fatigue tests. Statistical analysis techniques were developed to determine the strength and crack velocities for a single flaw. Slow crack-growth rupture was observed at stress intensities as low as 70 percent of K sub c. A strengthening effect was observed in specimens that had survived long-time static fatigue tests.

Fatigue of a 3D Orthogonal Non-crimp Woven Polymer Matrix Composite at Elevated Temperature

NASA Astrophysics Data System (ADS)

Wilkinson, M. P.; Ruggles-Wrenn, M. B.

2017-12-01

Tension-tension fatigue behavior of two polymer matrix composites (PMCs) was studied at elevated temperature. The two PMCs consist of the NRPE polyimide matrix reinforced with carbon fibers, but have different fiber architectures: the 3D PMC is a singly-ply non-crimp 3D orthogonal weave composite and the 2D PMC, a laminated composite reinforced with 15 plies of an eight harness satin weave (8HSW) fabric. In order to assess the performance and suitability of the two composites for use in aerospace components designed to contain high-temperature environments, mechanical tests were performed under temperature conditions simulating the actual operating conditions. In all elevated temperature tests performed in this work, one side of the test specimen was at 329 °C while the other side was open to ambient laboratory air. The tensile stress-strain behavior of the two composites was investigated and the tensile properties measured for both on-axis (0/90) and off-axis (±45) fiber orientations. Elevated temperature had little effect on the on-axis tensile properties of the two composites. The off-axis tensile strength of both PMCs decreased slightly at elevated temperature. Tension-tension fatigue tests were conducted at elevated temperature at a frequency of 1.0 Hz with a ratio of minimum stress to maximum stress of R = 0.05. Fatigue run-out was defined as 2 × 105 cycles. Both strain accumulation and modulus evolution during cycling were analyzed for each fatigue test. The laminated 2D PMC exhibited better fatigue resistance than the 3D composite. Specimens that achieved fatigue run-out were subjected to tensile tests to failure to characterize the retained tensile properties. Post-test examination under optical microscope revealed severe delamination in the laminated 2D PMC. The non-crimp 3D orthogonal weave composite offered improved delamination resistance.

Oxidation- and Creep-Enhanced Fatigue of Haynes 188 Alloy-Oxide Scale System Under Simulated Pulse Detonation Engine Conditions

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Fox, Dennis S.; Miller, Robert A.

2002-01-01

The development of the pulse detonation engine (PDE) requires robust design of the engine components that are capable of enduring harsh detonation environments. In this study, a high cycle thermal fatigue test rig was developed for evaluating candidate PDE combustor materials using a CO2 laser. The high cycle thermal fatigue behavior of Haynes 188 alloy was investigated under an enhanced pulsed laser test condition of 30 Hz cycle frequency (33 ms pulse period, and 10 ms pulse width including 0.2 ms pulse spike). The temperature swings generated by the laser pulses near the specimen surface were characterized by using one-dimensional finite difference modeling combined with experimental measurements. The temperature swings resulted in significant thermal cyclic stresses in the oxide scale/alloy system, and induced extensive surface cracking. Striations of various sizes were observed at the cracked surfaces and oxide/alloy interfaces under the cyclic stresses. The test results indicated that oxidation and creep-enhanced fatigue at the oxide scale/alloy interface was an important mechanism for the surface crack initiation and propagation under the simulated PDE condition.

An assessment of cold work effects on strain-controlled low-cycle fatigue behavior of type 304 stainless steel

NASA Astrophysics Data System (ADS)

Rao, K. Bhanu Sankara; Valsan, M.; Sandhya, R.; Mannan, S. L.; Rodriguez, P.

1993-04-01

The influence of prior cold work (PCW) on low-cycle fatigue (LCF) behavior of type 304 stainless steel has been studied at 300, 823, 923, and 1023 K by conducting total axial strain-controlled tests in solution annealed (SA, 0 pct PCW) condition and on specimens having three levels of PCW, namely, 10, 20, and 30 pct. A triangular waveform with a constant frequency of 0.1 Hz was employed for all of the tests performed over strain amplitudes in the range of ±0.25 to ± 1.25 pct. These studies have revealed that fatigue life is strongly dependent on PCW, temperature, and strain amplitude employed in testing. The SA material generally displayed better endurance in terms of total and plastic strain amplitudes than the material in 10, 20, and 30 pct PCW conditions at all of the temperatures. However, at 300 K at very low strain amplitudes, PCW material exhibited better total strain fatigue resistance. At 823 K, LCF life decreased with increasing PCW, whereas at 923 K, 10 pct PCW displayed the lowest life. An improvement in life occurred for prior deformations exceeding 10 pct at all strain amplitudes at 923 K. Fatigue life showed a noticeable decrease with increasing temperature up to 1023 K in PCW state. On the other hand, SA material displayed a minimum in fatigue life at 923 K. The fatigue life results of SA as well as all of the PCW conditions obeyed the Basquin and Coffin-Manson relationships at 300, 823, and 923 K. The constants and exponents in these equations were found to depend on the test temperature and prior metallurgical state of the material. A study is made of cyclic stress-strain behavior in SA and PCW states and the relationship between the cyclic strain-hardening exponent and fatigue behavior at different temperatures has been explored. The influence of environment on fatigue crack initiation and propagation behavior has been examined.

Mechanical properties of turbine blade alloys in hydrogen at elevated temperatures

NASA Technical Reports Server (NTRS)

Deluca, D. P.

1981-01-01

The mechanical properties of single crystal turbine blade alloys in a gaseous hydrogen environment were determined. These alloys are proposed for use in space propulsion systems in pure or partial high pressure hydrogen environments at elevated temperatures. Mechanical property tests included: tensile, creep, low fatigue (LCF), and crack growth. Specimens were in both transverse and longitudinal directions relative to the casting solidification direction. Testing was conducted on solid specimens exposed to externally pressurized environments of gaseous hydrogen and hydrogen-enriched steam.

Intraoperative Noise Increases Perceived Task Load and Fatigue in Anesthesiology Residents: A Simulation-Based Study.

PubMed

McNeer, Richard R; Bennett, Christopher L; Dudaryk, Roman

2016-02-01

Operating rooms are identified as being one of the noisiest of clinical environments, and intraoperative noise is associated with adverse effects on staff and patient safety. Simulation-based experiments would offer controllable and safe venues for investigating this noise problem. However, realistic simulation of the clinical auditory environment is rare in current simulators. Therefore, we retrofitted our operating room simulator to be able to produce immersive auditory simulations with the use of typical sound sources encountered during surgeries. Then, we tested the hypothesis that anesthesia residents would perceive greater task load and fatigue while being given simulated lunch breaks in noisy environments rather than in quiet ones. As a secondary objective, we proposed and tested the plausibility of a novel psychometric instrument for the assessment of stress. In this simulation-based, randomized, repeated-measures, crossover study, 2 validated psychometric survey instruments, the NASA Task Load Index (NASA-TLX), composed of 6 items, and the Swedish Occupational Fatigue Inventory (SOFI), composed of 5 items, were used to assess perceived task load and fatigue, respectively, in first-year anesthesia residents. Residents completed the psychometric instruments after being given lunch breaks in quiet and noisy intraoperative environments (soundscapes). The effects of soundscape grouping on the psychometric instruments and their comprising items were analyzed with a split-plot analysis. A model for a new psychometric instrument for measuring stress that combines the NASA-TLX and SOFI instruments was proposed, and a factor analysis was performed on the collected data to determine the model's plausibility. Twenty residents participated in this study. Multivariate analysis of variance showed an effect of soundscape grouping on the combined NASA-TLX and SOFI instrument items (P = 0.003) and the comparisons of univariate item reached significance for the NASA Temporal Demand item (P = 0.0004) and the SOFI Lack of Energy item (P = 0.001). Factor analysis extracted 4 factors, which were assigned the following construct names for model development: Psychological Task Load, Psychological Fatigue, Acute Physical Load, and Performance-Chronic Physical Load. Six of the 7 fit tests used in the partial confirmatory factor analysis were positive when we fitted the data to the proposed model, suggesting that further validation is warranted. This study provides evidence that noise during surgery can increase feelings of stress, as measured by perceived task load and fatigue levels, in anesthesiologists and adds to the growing literature pointing to an overall adverse impact of clinical noise on caregivers and patient safety. The psychometric model proposed in this study for assessing perceived stress is plausible based on factor analysis and will be useful for characterizing the impact of the clinical environment on subject stress levels in future investigations.

[Study on relationship between fatigue and work ability in chemistry workers].

PubMed

Wu, Si-Ying; Wang, Mian-Zhen; Wang, Zhi-Ming; Lan, Ya-Jia

2005-01-01

Explore the relationship between fatigue and work ability in 976 chemistry workers. A test of fatigue and work ability was carried out with fatigue scale and work ability index (WAI) for 976 workers, other influence factors of the work ability (such as work environment, labor load, job factors) were investigated with questionnaire. (1) The frequency of fatigue of the unmarried workers was significantly lower than that of the married workers and other marital status workers, while the score of WAI of the unmarried was significantly higher than that of those( P < 0.05); (2) the frequency of fatigue of the mental workers was significantly lower than that of the mixed physical and mental workers, while the score of WAI of the mental workers was significantly higher than that of physical workers and mixed physical and mental workers ( P < 0.05); (3) compared with the workers free of fatigue, the other workers had lower WAI scores; (4) the fatigue score correlated negatively to the WAI score (r = -0.499, P < 0.01); (5) Cumulative odds model analysis showed that after controlling the other risk factors, fatigue was an important risk factor of work ability (OR = 4.005). Fatigue has affected work ability in chemistry workers, the frequency of fatigue is higher, the score of WAI is lower.

Fatigue strength degradation of metals in corrosive environments

NASA Astrophysics Data System (ADS)

Adasooriya, N. D.; Hemmingsen, T.; Pavlou, D.

2017-12-01

Structures exposed to aggressive environmental conditions are often subjected to time-dependent loss of coating and loss of material due to corrosion; this causes reduction in the cross-sectional properties of the members, increased surface roughness, surface irregularities and corrosion pits, and degradation of material strengths. These effects have been identified and simulated in different research studies. However, time and corrosive media dependent fatigue strength curves for materials have not been discussed in the design or assessment guidelines for structures. This paper attempts to review the corrosion degradation process and available approaches/models used to determine the fatigue strength of corroded materials and to interpolate corrosion deterioration data. High cycle fatigue and full range fatigue life formulae for fatigue strength of corroded materials are proposed. The above formulae depend on the endurance limit of corroded material, in addition to the stress-life fatigue curve parameters of the uncorroded material. The endurance limit of corroded material can either be determined by a limited number of tests in the very high-cycle fatigue region or predicted by an analytical approach. Comparison with experimentally measured corrosion fatigue behavior of several materials is provided and discussed.

High Velocity Burner Rig Oxidation and Thermal Fatigue Behavior of Si3N4- and SiC Base Ceramics to 1370 Deg C

NASA Technical Reports Server (NTRS)

Sanders, W. A.; Johnston, J. R.

1978-01-01

One SiC material and three Si3N4 materials including hot-pressed Si3N4 as a baseline were exposed in a Mach-1-gas-velocity burner rig simulating a turbine engine environment. Criteria for the materials selection were: potential for gas-turbine usage, near-net-shape fabricability and commercial/domestic availability. Cyclic exposures of test vanes up to 250 cycles (50 hr at temperature) were at leading-edge temperatures to 1370 C. Materials and batches were compared as to weight change, surface change, fluorescent penetrant inspection, and thermal fatigue behavior. Hot-pressed Si3N4 survived the test to 1370 C with slight weight losses. Two types of reaction-sintered Si3N4 displayed high weight gains and considerable weight-change variability, with one material exhibiting superior thermal fatigue behavior. A siliconized SiC showed slight weight gains, but considerable batch variability in thermal fatigue.

Effect of Light Water Reactor Water Environments on the Fatigue Life of Reactor Materials

DOE PAGES

Chopra, O. K.; Stevens, G. L.; Tregoning, R.; ...

2017-10-06

The American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code (Code) provides rules for the design of Class 1 components of nuclear power plants. Figures I-9.1 through I-9.6 of Appendix I to Section III of the Code specify fatigue design curves for applicable structural materials. However, the Code design curves do not explicitly address the effects of light water reactor (LWR) water environments. Existing fatigue strain-vs.-life (ε-N) laboratory data illustrate potentially significant effects of LWR water environments on the fatigue resistance of pressure vessel and piping steels. Extensive studies have been conducted at Argonne National Laboratory and elsewheremore » since 1990 to investigate the effects of LWR environments on the fatigue life of piping and pressure vessel steels. This article summarizes the results of these studies. Existing fatigue ε-N data were evaluated to identify the various material, environmental, and loading conditions that influence fatigue crack initiation; a methodology for estimating fatigue lives as a function of these parameters was developed. The effects were incorporated into the ASME Code Section III fatigue evaluations in terms of an environmental correction factor, F en, which is defined as the ratio of fatigue life in air at room temperature to the fatigue life in the LWR water environment at reactor operating temperatures. Available fatigue data were used to develop fatigue design curves for carbon and low-alloy steels, austenitic stainless steels, and nickel-chromium-iron (NiCr-Fe) alloys and their weld metals in air at room temperature. A review of the Code Section III fatigue adjustment factors of 2 on strain and 20 on life is also presented and the possible conservatism inherent in the choice of these adjustment factors is evaluated. A brief description of potential effects of neutron irradiation on fatigue crack initiation for these structural materials is also presented.« less

Effect of Light Water Reactor Water Environments on the Fatigue Life of Reactor Materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chopra, O. K.; Stevens, G. L.; Tregoning, R.

The American Society of Mechanical Engineers (ASME) Boiler and Pressure Vessel Code (Code) provides rules for the design of Class 1 components of nuclear power plants. Figures I-9.1 through I-9.6 of Appendix I to Section III of the Code specify fatigue design curves for applicable structural materials. However, the Code design curves do not explicitly address the effects of light water reactor (LWR) water environments. Existing fatigue strain-vs.-life (ε-N) laboratory data illustrate potentially significant effects of LWR water environments on the fatigue resistance of pressure vessel and piping steels. Extensive studies have been conducted at Argonne National Laboratory and elsewheremore » since 1990 to investigate the effects of LWR environments on the fatigue life of piping and pressure vessel steels. This article summarizes the results of these studies. Existing fatigue ε-N data were evaluated to identify the various material, environmental, and loading conditions that influence fatigue crack initiation; a methodology for estimating fatigue lives as a function of these parameters was developed. The effects were incorporated into the ASME Code Section III fatigue evaluations in terms of an environmental correction factor, F en, which is defined as the ratio of fatigue life in air at room temperature to the fatigue life in the LWR water environment at reactor operating temperatures. Available fatigue data were used to develop fatigue design curves for carbon and low-alloy steels, austenitic stainless steels, and nickel-chromium-iron (NiCr-Fe) alloys and their weld metals in air at room temperature. A review of the Code Section III fatigue adjustment factors of 2 on strain and 20 on life is also presented and the possible conservatism inherent in the choice of these adjustment factors is evaluated. A brief description of potential effects of neutron irradiation on fatigue crack initiation for these structural materials is also presented.« less

Retardation analytical model to extend service life

NASA Technical Reports Server (NTRS)

Matejczyk, D.

1984-01-01

A fatigue crack growth model that incorporates crack growth retardation effects and is applicable to the materials characteristics and service environments of high performance LH2/LO2 engine systems was developed and tested.

Human fatigue expression recognition through image-based dynamic multi-information and bimodal deep learning

NASA Astrophysics Data System (ADS)

Zhao, Lei; Wang, Zengcai; Wang, Xiaojin; Qi, Yazhou; Liu, Qing; Zhang, Guoxin

2016-09-01

Human fatigue is an important cause of traffic accidents. To improve the safety of transportation, we propose, in this paper, a framework for fatigue expression recognition using image-based facial dynamic multi-information and a bimodal deep neural network. First, the landmark of face region and the texture of eye region, which complement each other in fatigue expression recognition, are extracted from facial image sequences captured by a single camera. Then, two stacked autoencoder neural networks are trained for landmark and texture, respectively. Finally, the two trained neural networks are combined by learning a joint layer on top of them to construct a bimodal deep neural network. The model can be used to extract a unified representation that fuses landmark and texture modalities together and classify fatigue expressions accurately. The proposed system is tested on a human fatigue dataset obtained from an actual driving environment. The experimental results demonstrate that the proposed method performs stably and robustly, and that the average accuracy achieves 96.2%.

Apparatus and method for fatigue testing of a material specimen in a high-pressure fluid environment

DOEpatents

Wang, Jy-An; Feng, Zhili; Anovitz, Lawrence M; Liu, Kenneth C

2013-06-04

The invention provides fatigue testing of a material specimen while the specimen is disposed in a high pressure fluid environment. A specimen is placed between receivers in an end cap of a vessel and a piston that is moveable within the vessel. Pressurized fluid is provided to compression and tension chambers defined between the piston and the vessel. When the pressure in the compression chamber is greater than the pressure in the tension chamber, the specimen is subjected to a compression force. When the pressure in the tension chamber is greater than the pressure in the compression chamber, the specimen is subjected to a tension force. While the specimen is subjected to either force, it is also surrounded by the pressurized fluid in the tension chamber. In some examples, the specimen is surrounded by hydrogen.

Effect of Localized Corrosion on Fatigue-Crack Growth in 2524-T3 and 2198-T851 Aluminum Alloys Used as Aircraft Materials

NASA Astrophysics Data System (ADS)

Moreto, J. A.; Broday, E. E.; Rossino, L. S.; Fernandes, J. C. S.; Bose Filho, W. W.

2018-03-01

Corrosion and fatigue of aluminum alloys are major issues for the in-service life assessment of aircraft structures and for the management of aging air fleets. The aim of this work was to evaluate the effect of localized corrosion on fatigue crack growth (FCG) resistance of the AA2198-T851 Al-Li alloy (Solution Heat Treated, Cold Worked, and Artificially Aged), comparing it with the FCG resistance of AA2524-T3 (Solution Heat Treated and Cold Worked), considering the effect of seawater fog environment. Before fatigue tests, the corrosion behavior of 2198-T851 and 2524-T3 aluminum alloys was verified using open circuit potential and potentiodynamic polarization techniques. Fatigue in air and corrosion fatigue tests were performed applying a stress ratio (R) of 0.1, 15 Hz (air) and 0.1 Hz (seawater fog) frequencies, using a sinusoidal waveform in all cases. The results showed that the localized characteristics of the 2198-T851 and 2524-T3 aluminum alloys are essentially related to the existence of intermetallic compounds, which, due to their different nature, may be cathodic or anodic in relation to the aluminum matrix. The corrosive medium has affected the FCG rate of both aluminum alloys, in a quite similar way.

Thermal Exposure and Environment Effects on Tension, Fracture and Fatigue of 5XXX Alloys Tested in Different Orientations

DTIC Science & Technology

2017-12-27

were determined and the effects of changes in loading rate and solution on this susceptibility were determined. Technical Approach The technical... approach followed in this completed work has been to conduct quasi- static fracture and fatigue experiments on 5XXX commercial aluminum alloys of interest...Metallic Materials Studied by Correlative Tomography", in 38th Riso International Symposium on Materials Science - IOP Conf. Series: Materials Science

Microstructurally based variations on the dwell fatgue life of titanium alloy IMI 834

NASA Technical Reports Server (NTRS)

Thomsen, Mark L.; Hoeppner, David W.

1994-01-01

An experimental study was undertaken to determine the role of microstructure on the fatigue life reduction observed in titanium alloy IMI 834 under dwell loading conditions. The wave forms compared were a trapezoid with 15 and 30 second hold times at the maximum test load and a baseline, 10 Hertz, haversine. The stress ratio for both loading wave forms was 0.10. The fatigue loading of each specimen was conducted in a vacuum within a scanning electron microscope chamber which minimized the possibility that the laboratory environment would adversely affect the material behavior. Two microstructural conditions were investigated in the experimental program. The first involved standard 'disk' material with equiaxed alpha in a transformed beta matrix. The second material was cut from the same disk forging as the first but was heat treated to obtain a martensitic alpha prime microstructure. Tensile tests were performed prior to the onset of the fatigue loading portion of the study, and it was determined that the yield strengths of the specimens from both material conditions were within ten percent. The maximum fatigue loads were chosen to be 72 percent of the average yield strength for both materials as determined from the tensile tests. It was found that the cycles to failure from the 10 Hertz loading wave form were reduced by a factor of approximately five when the loading was changed to the trapezoidal wave form for the standard 'disk' material. The fatigue life reduction for the martensitic structure under identical test conditions was approximately 1.75. The improvement observed with the martensitic structure also was accompanied by an increase in overall fatigue life for the wave forms tested. This paper will review the results and conclusions of this effort.

Cyclic fatigue-crack propagation, stress-corrosion, and fracture-toughness behavior in pyrolytic carbon-coated graphite for prosthetic heart valve applications.

PubMed

Ritchie, R O; Dauskardt, R H; Yu, W K; Brendzel, A M

1990-02-01

Fracture-mechanics tests were performed to characterize the cyclic fatigue, stress-corrosion cracking, and fracture-toughness behavior of a pyrolytic carbon-coated graphite composite material used in the manufacture of cardiac valve prostheses. Testing was carried out using compact tension C(T) samples containing "atomically" sharp precracks, both in room-temperature air and principally in a simulated physiological environment of 37 degrees C Ringer's lactate solution. Under sustained (monotonic) loads, the composite exhibited resistance-curve behavior, with a fracture toughness (KIc) between 1.1 and 1.9 MPa square root of m, and subcritical stress-corrosion crack velocities (da/dt) which were a function of the stress intensity K raised to the 74th power (over the range approximately 10(-9) to over 10(-5) m/s). More importantly, contrary to common perception, under cyclic loading conditions the composite was found to display true (cyclic) fatigue failure in both environments; fatigue-crack growth rates (da/dN) were seen to be a function of the 19th power of the stress-intensity range delta K (over the range approximately 10(-11) to over 10(-8) m/cycle). As subcritical crack velocities under cyclic loading were found to be many orders of magnitude faster than those measured under equivalent monotonic loads and to occur at typically 45% lower stress-intensity levels, cyclic fatigue in pyrolytic carbon-coated graphite is reasoned to be a vital consideration in the design and life-prediction procedures of prosthetic devices manufactured from this material.

Surface Studies of Ultra Strength Drilling Steel after Corrosion Fatigue in Simulated Sour Environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

M. Ziomek-Moroz; J.A. Hawk; R. Thodla

2012-05-06

The Unites States predicted 60% growth in energy demand by 2030 makes oil and natural gas primary target fuels for energy generation. The fact that the peak of oil production from shallow wells (< 5000 m) is about to be reached, thereby pushing the oil and natural gas industry into deeper wells. However, drilling to depths greater than 5000 m requires increasing the strength-to weight ratio of the drill pipe materials. Grade UD-165 is one of the ultra- high yield strength carbon steels developed for ultra deep drilling (UDD) activities. Drilling UDD wells exposes the drill pipes to Cl{sup -},more » HCO{sub 3}{sup -}/CO{sub 3}{sup 2-}, and H{sub 2}S-containig corrosive environments (i.e., sour environments) at higher pressures and temperatures compared to those found in conventional wells. Because of the lack of synergism within the service environment, operational stresses can result in catastrophic brittle failures characteristic for environmentally assisted cracking (EAC). Approximately 75% of all drill string failures are caused by fatigue or corrosion fatigue. Since there is no literature data on the corrosion fatigue performance of UD-165 in sour environments, research was initiated to better clarify the fatigue crack growth (FCGR) behavior of this alloy in UDD environments. The FCGR behavior of ultra-strength carbon steel, grade UD-165, was investigated by monitoring crack growth rate in deaerated 5%NaCl solution buffered with NaHCO{sub 3}/Na{sub 2}CO{sub 3} and in contact with H{sub 2}S. The partial pressure of H{sub 2}S (p{sub H2S}) was 0.83 kPa and pH of the solution was adjusted by NaOH to 12. The fatigue experiments were performed at 20 and 85 C in an autoclave with surface investigations augmented by scanning electron microscopy (SEM) and energy dispersive x-ray (EDX) spectroscopy. In this study, research focused on surface analyses supported by the fatigue crack growth rate measurements. Fig. 1 shows an SEM micrograph of the crack that propagated from the notch in the solution at 20 C. Accumulation of the corrosion products is visible along the crack. The EDX chemical analysis near the crack tip found iron, sulfur and oxygen in the passive layer. The surface of the sample after the fatigue test in the sour environment at 85{sup o}, Fig. 2, C looks different from that fatigued surface at 20 C. The crack propagates across the passive film that covers the surface fairly uniformly. Some spallation of the passive film is observed near the notch. The EDX chemical analysis of the passive film near the crack tip identified mainly iron, carbon and oxygen. It appears that temperature plays a very important role in formation of the passive film. This may be associated with different solubility of H{sub 2}S in the solution, which will be further studied.« less

Influence of gaseous hydrogen on the mechanical properties of incoloy 903. [gas-metal interactions/iron alloys

NASA Technical Reports Server (NTRS)

1975-01-01

Solid specimens of the alloy Inconel 903 (iron based alloy) were exposed to four gaseous environments and high temperatures. Air, pure helium, pure hydrogen, and hydrogen and water vapor combined were the gaseous environments employed, and the temperature was 1400 F. Various mechanical property tests (low cycle fatigue, creep-rupture, tensile properties) were performed on the alloy. Results indicate that the hydrogen and water vapor environment cause a sharp reduction in the mechanical properties of the alloy. Photographs of the test equipment used and the microstructure of the tested alloy are included.

Effects of crack tip plastic zone on corrosion fatigue cracking of alloy 690(TT) in pressurized water reactor environments

NASA Astrophysics Data System (ADS)

Xiao, J.; Qiu, S. Y.; Chen, Y.; Fu, Z. H.; Lin, Z. X.; Xu, Q.

2015-01-01

Alloy 690(TT) is widely used for steam generator tubes in pressurized water reactor (PWR), where it is susceptible to corrosion fatigue. In this study, the corrosion fatigue behavior of Alloy 690(TT) in simulated PWR environments was investigated. The microstructure of the plastic zone near the crack tip was investigated and labyrinth structures were observed. The relationship between the crack tip plastic zone and fatigue crack growth rates and the environment factor Fen was illuminated.

Fatigue and fracture assessment of cracks in steel elements using acoustic emission

NASA Astrophysics Data System (ADS)

Nemati, Navid; Metrovich, Brian; Nanni, Antonio

2011-04-01

Single edge notches provide a very well defined load and fatigue crack size and shape environment for estimation of the stress intensity factor K, which is not found in welded elements. ASTM SE(T) specimens do not appear to provide ideal boundary conditions for proper recording of acoustic wave propagation and crack growth behavior observed in steel bridges, but do provide standard fatigue crack growth rate data. A modified versions of the SE(T) specimen has been examined to provide small scale specimens with improved acoustic emission(AE) characteristics while still maintaining accuracy of fatigue crack growth rate (da/dN) versus stress intensity factor (ΔK). The specimens intend to represent a steel beam flange subjected to pure tension, with a surface crack growing transverse to a uniform stress field. Fatigue test is conducted at low R ratio. Analytical and numerical studies of stress intensity factor are developed for single edge notch test specimens consistent with the experimental program. ABAQUS finite element software is utilized for stress analysis of crack tips. Analytical, experimental and numerical analysis were compared to assess the abilities of AE to capture a growing crack.

Ductility normalized-strainrange partitioning life relations for creep-fatigue life predictions

NASA Technical Reports Server (NTRS)

Halford, G. R.; Saltsman, J. F.; Hirschberg, M. H.

1977-01-01

Procedures based on Strainrange Partitioning (SRP) are presented for estimating the effects of environment and other influences on the high temperature, low cycle, creep fatigue resistance of alloys. It is proposed that the plastic and creep, ductilities determined from conventional tensile and creep rupture tests conducted in the environment of interest be used in a set of ductility normalized equations for making a first order approximation of the four SRP inelastic strainrange life relations. Different levels of sophistication in the application of the procedures are presented by means of illustrative examples with several high temperature alloys. Predictions of cyclic lives generally agree with observed lives within factors of three.

Influence of dissolved hydrogen on the fatigue crack growth behaviour of AISI 4140 steel

NASA Astrophysics Data System (ADS)

Ramasagara Nagarajan, Varun

Many metallic structural components come into contact with hydrogen during manufacturing processes or forming operations such as hot stamping of auto body frames and while in service. This interaction of metallic parts with hydrogen can occur due to various reasons such as water molecule dissociation during plating operations, interaction with atmospheric hydrogen due to the moisture present in air during stamping operations or due to prevailing conditions in service (e.g.: acidic or marine environments). Hydrogen, being much smaller in size compared to other metallic elements such as Iron in steels, can enter the material and become dissolved in the matrix. It can lodge itself in interstitials locations of the metal atoms, at vacancies or dislocations in the metallic matrix or at grain boundaries or inclusions (impurities) in the alloy. This dissolved hydrogen can affect the functional life of these structural components leading to catastrophic failures in mission critical applications resulting in loss of lives and structural component. Therefore, it is very important to understand the influence of the dissolved hydrogen on the failure of these structural materials due to cyclic loading (fatigue). For the next generation of hydrogen based fuel cell vehicles and energy systems, it is very crucial to develop structural materials for hydrogen storage and containment which are highly resistant to hydrogen embrittlement. These materials should also be able to provide good long term life in cyclic loading, without undergoing degradation, even when exposed to hydrogen rich environments for extended periods of time. The primary focus of this investigation was to examine the influence of dissolved hydrogen on the fatigue crack growth behaviour of a commercially available high strength medium carbon low alloy (AISI 4140) steel. The secondary objective was to examine the influence of microstructure on the fatigue crack growth behaviour of this material and to determine the hydrogen induced failure mechanism in this material during cyclic loading. The secondary objective of this investigation was to determine the role of inclusions and their influence in affecting the fatigue crack growth rate of this material. Compact tension and tensile specimens were prepared as per ASTM E-647, E-399 and E-8 standards. The specimens were tested in three different heat treated conditions i.e. annealed (as received) as well as two austempered conditions. These specimens were precharged with hydrogen (ex situ) using cathodic charging method at a constant current density at three different time periods ranging from 150 to 250 hours before conducting fatigue crack growth tests. Mode 1 type fatigue tests were then performed in ambient atmosphere at constant amplitude using load ratio R of 0.1. The near threshold fatigue crack growth rate, fatigue threshold and the fatigue crack growth rate in the linear region were determined. Fatigue crack growth behaviour of specimens without any dissolve hydrogen were then compared with the specimens with different concentration of dissolved hydrogen. The test results show that the dissolved hydrogen concentration increases with the increase in charging time in all three heat treated conditions and the hydrogen uptake shows a strong dependence on the microstructure of the alloy. It was also observed that the microstructure has a significant influence of on the fatigue crack growth and SCC behaviour of the alloy with dissolved hydrogen. As the dissolved hydrogen concentration increases, the fatigue threshold was found to decrease and the near threshold crack growth rate increases in all three heat treated conditions showing the deleterious effect of hydrogen, but to a different extent in each condition. Current test results also indicate that the fatigue crack growth rates in the linear region increases as the dissolved hydrogen content increases in all three heat treated conditions. It is also observed that increasing the austempering temperature decreases the resistance to hydrogen embrittlement. An interesting phenomenon was also observed in annealed specimen charged with hydrogen for 250 h which had an unusually high fatigue threshold (DeltaKth).

A Brief Look at: Test Scores and the Standard Error of Measurement. E&R Report No. 10.13

ERIC Educational Resources Information Center

Holdzkom, David; Sumner, Brian; McMillen, Brad

2010-01-01

In the context of standardized testing, the standard error of measurement (SEM) is a measure of the factors other than the student's actual knowledge of the tested material that may affect the student's test score. Such factors may include distractions in the testing environment, fatigue, hunger, or even luck. This means that a student's observed…

Creep fatigue life prediction for engine hot section materials (isotropic)

NASA Technical Reports Server (NTRS)

Nelson, R. S.; Levan, G. W.; Harvey, P. R.

1992-01-01

This Final Report covers the activities completed under the optional program of the NASA HOST Contract, NAS3-23288. The initial effort of the optional program was report-in NASA CR189221, which consisted of high temperature strain controlled fatigue tests to study the effects of thermomechanical fatigue, multiaxial loading, reactive environments, and imposed stresses. The baseline alloy used in the tests included B1900+Hf (with or without coating) and wrought INCO 718. Tests conducted on B1900+Hf included environmental tests using various atmospheres (75 psig oxygen, purified argon, or block exposures) and specimen tests of wrought INCO 718 included tensile, creep, stress rupture, TMF, multiaxial, and mean stress tests. Results of these testings were used to calibrate a CDA model for INCO 718 alloy and to develop modifications or corrections to the CDA model to handle additional failure mechanisms. The Socie parameter was found to provide the best correlation for INCO multiaxial loading. Microstructural evaluations consisting of optical, Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM) techniques, and surface replication techniques to determine crack initiation lives provided data which were used to develop life prediction models.

Urban Options for Psychological Restoration: Common Strategies in Everyday Situations

PubMed Central

Staats, Henk; Jahncke, Helena; Herzog, Thomas R.; Hartig, Terry

2016-01-01

Objectives Given the need for knowledge on the restorative potential of urban settings, we sought to estimate the effects of personal and contextual factors on preferences and restoration likelihood assessments for different urban activities-in-environments. We also sought to study the generality of these effects across different countries. Methods We conducted a true experiment with convenience samples of university students in the Netherlands (n = 80), Sweden (n = 100), and the USA (n = 316). In each country, the experiment had a mixed design with activities-in-environments (sitting in a park, sitting in a cafe, walking in a shopping mall, walking along a busy street) manipulated within-subjects and the need for restoration (attentional fatigue, no attentional fatigue) and immediate social context (in company, alone) manipulated between-subjects. The manipulations relied on previously tested scenarios describing everyday situations that participants were instructed to remember and imagine themselves being in. For each imagined situation (activity-in-environment with antecedent fatigue condition and immediate social context), subjects provided two criterion measures: general preference and the likelihood of achieving psychological restoration. Results The settings received different preference and restoration likelihood ratings as expected, affirming that a busy street, often used in comparisons with natural settings, is not representative of the restorative potential of urban settings. Being with a close friend and attentional fatigue both moderated ratings for specific settings. Findings of additional moderation by country of residence caution against broad generalizations regarding preferences for and the expected restorative effects of different urban settings. Conclusions Preferences and restoration likelihood ratings for urban activity-environment combinations are subject to multiple personal and contextual determinants, including level of attentional fatigue, being alone versus in company, and broader aspects of the urban context that vary across cities and countries. Claims regarding a lack of restorative quality in urban environments are problematic. PMID:26731272

Evaluation and repair of existing bridges in extreme environments.

DOT National Transportation Integrated Search

2016-01-26

The research described in this report consisted of analysis and experimental testing of steel bridge details susceptible to fatigue and end regions of precast prestressed concrete girder ends subjected to reinforcement corrosion. Locations most affec...

Environmental Effects on Fatigue Behavior of Metals.

DTIC Science & Technology

1981-04-09

Growth Rate Behavior Above and Below KISCC in Steels ," Journal of Materials, Vol. 6, No. 4, 1971, pp. 941-964. 3. Barsom, J. M., " Corrosion -Fatigue...T., and Inoue, K., " Corrosion Fatigue Behavior of 13 Cr Stainless Steel in Sodium-Chloride Aqueous Solution and Steam Environment," Corrosion -Fatigue...34Effect of Environment on the Fatigue Behavior of a Medium Carbon Steel ," Corrosion , Vol. 30, 1974, pp. 280-284. 98. Karpenko, G. V., Romaniv, A. N., and

The fatigue life of a cobalt-chromium alloy after laser welding.

PubMed

Al-Bayaa, Nabil Jalal Ahmad; Clark, Robert K F; Juszczyk, Andrzej S; Radford, David R

2011-03-01

The aim of this study was to investigate the fatigue life of laser welded joints in a commercially available cast cobalt-chromium alloy. Twenty rod shaped specimens (40 mm x 1.5 mm) were cast and sand blasted. Ten specimens were used as controls and the remaining ten were sectioned and repaired using a pulsed Nd: YAG laser welder. All specimens were subjected to fatigue testing (30N - 2Hz) in a controlled environment. A statistically significant difference in median fatigue life was found between as-cast and laser welded specimens (p < 0.001). Consequently, the technique may not be appropriate for repairing cobalt chromium clasps on removable partial dentures. Scanning electron microscopy indicated the presence of cracks, pores and constriction of the outer surface in the welded specimens despite 70% penetration of the weld.

Determination of the Proper Rest Time for a Cyclic Mental Task Using ACT-R Architecture.

PubMed

Atashfeshan, Nooshin; Razavi, Hamideh

2017-03-01

Objective Analysis of the effect of mental fatigue on a cognitive task and determination of the right start time for rest breaks in work environments. Background Mental fatigue has been recognized as one of the most important factors influencing individual performance. Subjective and physiological measures are popular methods for analyzing fatigue, but they are restricted to physical experiments. Computational cognitive models are useful for predicting operator performance and can be used for analyzing fatigue in the design phase, particularly in industrial operations and inspections where cognitive tasks are frequent and the effects of mental fatigue are crucial. Method A cyclic mental task is modeled by the ACT-R architecture, and the effect of mental fatigue on response time and error rate is studied. The task includes visual inspections in a production line or control workstation where an operator has to check products' conformity to specifications. Initially, simulated and experimental results are compared using correlation coefficients and paired t test statistics. After validation of the model, the effects are studied by human and simulated results, which are obtained by running 50-minute tests. Results It is revealed that during the last 20 minutes of the tests, the response time increased by 20%, and during the last 12.5 minutes, the error rate increased by 7% on average. Conclusion The proper start time for the rest period can be identified by setting a limit on the error rate or response time. Application The proposed model can be applied early in production planning to decrease the negative effects of mental fatigue by predicting the operator performance. It can also be used for determining the rest breaks in the design phase without an operator in the loop.

Fatigue testing of a NiTi rotary instrument. Part 1: Strain-life relationship.

PubMed

Cheung, G S P; Darvell, B W

2007-08-01

To examine the fatigue behaviour using a strain-life approach, and to determine the effect of water on the fatigue life of a NiTi rotary instrument. Instruments of one brand of NiTi engine-file (size 25, ProFile 0.04 and 0.06) were subjected to rotational bending either in air or under water, the number of revolutions to fracture (N(f)) being recorded using an optical counter and an electronic break-detection circuit. The effective surface strain amplitude (epsilon(a)) for each specimen was determined from the curvature of the instrument (on a photograph) and the diameter of the fracture cross-section (from a scanning electron micrograph of the fracture surface). Strain was plotted against fatigue life and the low-cycle fatigue (LCF) region identified. Values were examined using two-way analysis of variance for difference between various instrument-environment combinations. A total of 212 instruments were tested. A strain-life relationship typical of metals was found. N(f) declined with an inverse power function dependence on epsilon(a). A fatigue limit was present at about 0.7% strain. The apparent fatigue-ductility exponent, a material constant for the LCF life of metals, was found to be between -0.45 and -0.55. There was a significant effect of the environmental condition on the LCF life, water being more detrimental than air. The fatigue behaviour of NiTi rotary instrument is typical of most metals, provided that the analysis is based on the surface strain amplitude, and showed a high-cycle and a LCF region. The LCF life is adversely affected by water.

Modeling Creep-Fatigue-Environment Interactions in Steam Turbine Rotor Materials for Advanced Ultra-supercritical Coal Power Plants

DOE Office of Scientific and Technical Information (OSTI.GOV)

Shen, Chen

2014-04-01

The goal of this project is to model creep-fatigue-environment interactions in steam turbine rotor materials for advanced ultra-supercritical (A-USC) coal power Alloy 282 plants, to develop and demonstrate computational algorithms for alloy property predictions, and to determine and model key mechanisms that contribute to the damages caused by creep-fatigue-environment interactions.

The combined effects of prior-corrosion and aggressive chemical environments on fatigue crack growth behavior in aluminum alloy 7075-T651

NASA Astrophysics Data System (ADS)

Mills, Thomas Brian

1997-11-01

Exfoliation corrosion is a potentially severe form of corrosion that frequently affects high-strength aluminum, particularly 2xxx- and 7xxx-series alloys. Exfoliation degrades components such as sheets, plates, and extrusions that have highly elongated grain structures. Few attempts have been made to investigate the effects of this form of corrosion on the fatigue performance of these materials, so a preliminary study was conducted to determine the effects of exfoliation corrosion on the fatigue response of quarter-inch 7075-T651 aluminum alloy plate. This was accomplished by subjecting aluminum panels to an ASTM standard corrosive solution known as EXCO then fatiguing the panels in corrosion fatigue environments of dry air, humid air, and artificial acid rain. Statistical analyses of the fatigue crack growth data suggest that prior-corrosion and corrosion fatigue are competing mechanisms that both have the potential of accelerating crack growth rates. In the dry air cases, exfoliation accelerated crack growth rates a maximum of 4.75 times over the uncorroded material at lower stress intensities such as 5 ksi surdinch. This accelerated behavior dropped off rapidly, however, and was nonexistent at higher stress intensities. Humid air increased crack velocities considerably as compared to the dry air uncorroded case, but the addition of exfoliation corrosion to the humid cases did not have a significant effect on crack growth behavior. On the other hand, specimens containing exfoliation corrosion and then exposed to artificial acid rain had significantly higher crack growth rates than their uncorroded counterparts. Finally, fractographic examinations of the specimens revealed evidence of lower energy, quasi-cleavage fracture persisting near to the exfoliated edge of specimens tested in the dry air, humid air, and artificial acid rain environments. The implications of this research are that prior-corrosion damage has the ability to significantly increase crack growth rates in this material, and this could render unconservative the inspection intervals determined by damage tolerant analyses based on pristine, uncorroded structure in aircraft where this alloy and damage mechanism are present. The problem is further compounded in the event that prior-corrosion damage and corrosion fatigue act synergisticaliy to increase cracking rates.

Cryogenic Fluid Management Experiment (CFME) trunnion verification testing

NASA Technical Reports Server (NTRS)

Bailey, W. J.; Fester, D. A.

1983-01-01

The Cryogenic Fluid Management Experiment (CFME) was designed to characterize subcritical liquid hydrogen storage and expulsion in the low-g space environment. The CFME has now become the storage and supply tank for the Cryogenic Fluid Management Facility, which includes transfer line and receiver tanks, as well. The liquid hydrogen storage and supply vessel is supported within a vacuum jacket to two fiberglass/epoxy composite trunnions which were analyzed and designed. Analysis using the limited available data indicated the trunnion was the most fatigue critical component in the storage vessel. Before committing the complete storage tank assembly to environmental testing, an experimental assessment was performed to verify the capability of the trunnion design to withstand expected vibration and loading conditions. Three tasks were conducted to evaluate trunnion integrity. The first determined the fatigue properties of the trunnion composite laminate materials. Tests at both ambient and liquid hydrogen temperatures showed composite material fatigue properties far in excess of those expected. Next, an assessment of the adequacy of the trunnion designs was performed (based on the tested material properties).

Dynamic load environment of bridge-mounted sign support structures.

DOT National Transportation Integrated Search

2005-09-01

An investigation was conducted into the failure of a welded aluminum truss sign support structure on an existing interstate highway bridge. The investigation was conducted in three main steps; 1) fatigue testing in the laboratory of surviving segment...

Fatigue crack growth behavior of pressure vessel steels and submerged arc weldments in a high-temperature pressurized water environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liaw, P.K.; Logsdon, W.A.; Begley, J.A.

1989-10-01

The fatigue crack growth rate (FCGR) properties of SA508 Cl 2a and SA533 Gr A Cl 2 pressure vessel steels and the corresponding automatic submerged arc weldments were developed in a high-temperature pressurized water (HPW) environment at 288{degrees} C (550{degrees} F) and 7.2 MPa (1044 psi) at load ratios of 0.20 and 0.50. The properties were generally conservative compared to American Society of Mechanical Engineers Section XI water environment reference curve. The growth rate of fatigue cracks in the base materials, however, was faster in the HPW environment than in a 288{degrees} C (550{degrees} F) base line air environment. Themore » growth rate of fatigue cracks in the two submerged arc weldments was also accelerated in the HPW environment but to a lesser degree than that demonstrated by the base materials. In the air environment, fatigue striations were observed, independent of material and load ratio, while in the HPW environment, some intergranular facets were present. The greater environmental effect on crack growth rates displayed by the base materials compared the weldments attributed to a different sulfide composition and morphology.« less

Fatigue crack growth behavior of railroad tank car steel TC-128B subjected to various environments. Volume 2 : appendices

DOT National Transportation Integrated Search

2006-12-01

This is Volume II-Appendices of Fatigue Crack Growth Behavior of Railroad Tank Car Steel TC-128B Subjected to Various Environments. This document contains miscellaneous supporting documentation, fatigue crack growth laboratory data, and analyses.

Low-cycle fatigue of Type 347 stainless steel and Hastelloy alloy X in hydrogen gas and in air at elevated temperatures

NASA Technical Reports Server (NTRS)

Jaske, C. E.; Rice, R. C.; Buchheit, R. D.; Roach, D. B.; Porfilio, T. L.

1976-01-01

An investigation was conducted to assess the low-cycle fatigue resistance of two alloys, Type 347 stainless steel and Hastelloy Alloy X, that were under consideration for use in nuclear-powered rocket vehicles. Constant-amplitude, strain-controlled fatigue tests were conducted under compressive strain cycling at a constant strain rate of 0.001/sec and at total axial strain ranges of 1.5, 3.0, and 5.0 %, in both laboratory-air and low-pressure hydrogen-gas environments at temperatures from 538 to 871 C. Specimens were obtained from three heats of Type 347 stainless steel bar and two heats of Hastelloy Alloy X. The tensile properties of each heat were determined at 21, 538, 649, and 760 C. The continuous cycling fatigue resistance was determined for each heat at temperatures of 538, 760, and 871 C. The Type 347 stainless steel exhibited equal or superior fatigue resistance to the Hastelloy Alloy X at all conditions of this study.

A new methodology for automating acoustic emission detection of metallic fatigue fractures in highly demanding aerospace environments: An overview

NASA Astrophysics Data System (ADS)

Holford, Karen M.; Eaton, Mark J.; Hensman, James J.; Pullin, Rhys; Evans, Sam L.; Dervilis, Nikolaos; Worden, Keith

2017-04-01

The acoustic emission (AE) phenomenon has many attributes that make it desirable as a structural health monitoring or non-destructive testing technique, including the capability to continuously and globally monitor large structures using a sparse sensor array and with no dependency on defect size. However, AE monitoring is yet to fulfil its true potential, due mainly to limitations in location accuracy and signal characterisation that often arise in complex structures with high levels of background noise. Furthermore, the technique has been criticised for a lack of quantitative results and the large amount of operator interpretation required during data analysis. This paper begins by introducing the challenges faced in developing an AE based structural health monitoring system and then gives a review of previous progress made in addresing these challenges. Subsequently an overview of a novel methodology for automatic detection of fatigue fractures in complex geometries and noisy environments is presented, which combines a number of signal processing techniques to address the current limitations of AE monitoring. The technique was developed for monitoring metallic landing gear components during pre-flight certification testing and results are presented from a full-scale steel landing gear component undergoing fatigue loading. Fracture onset was successfully identify automatically at 49,000 fatigue cycles prior to final failure (validated by the use of dye penetrant inspection) and the fracture position was located to within 10 mm of the actual location.

Plasma immersion ion implantation on 15-5PH stainless steel: influence on fatigue strength and wear resistance

NASA Astrophysics Data System (ADS)

Bonora, R.; Cioffi, M. O. H.; Voorwald, H. J. C.

2017-05-01

Surface improvement in steels is of great interest for applications in industry. The aim of this investigation is to study the effect of nitrogen ion implantation on the axial fatigue strength and wear resistance of 15-5 PH stainless steel. It is well know that electroplated coatings, which are used to improve abrasive wear and corrosion properties, affects negatively the fatigue strength. It is also important to consider requirements to reduce the use of coated materials with electroplated chromium and cadmium, that produce waste, which is harmful to health and environment. The HVOF (High velocity oxygen fuel) process provides hardness, wear strength and higher fatigue resistance in comparison to electroplated chromium. Plasma immersion ion implantation has been used to enhance the hardness, wear, fatigue and corrosion properties of metals and alloys. In the present research the fatigue life increased twice for 15-5 PH three hours PIII treated in comparison to base material. From the abrasive wear tests a lower pin mass reduction was observed, associated to the superficial treatments. The improvement of fatigue and mechanical performance is attributed to a combination of nitrides phase structure and compressive residual stresses during the PIII treatment.

The effects of state anxiety and thermal comfort on sleep quality and eye fatigue in shift work nurses.

PubMed

Dehghan, Habibollah; Azmoon, Hiva; Souri, Shiva; Akbari, Jafar

2014-01-01

Psychological problems as state anxiety (SA) in the work environment has negative effect on the employees life especially shift work nurses, i.e. negative effect on mental and physical health (sleep quality, eye fatigue and comfort thermal). The purpose of this study was determination of effects of state anxiety and thermal comfort on sleep quality and eye fatigue in shift work nurses. This cross-sectional research conducted on 82 shift-work personnel of 18 nursing workstations of Isfahan hospitals in 2012. To measure the SA, sleep quality, visual fatigue and thermal comfort, Spielberger state-trait anxiety inventory, Pittsburg sleep quality index, eye fatigue questionnaire and thermal comfort questionnaire were used respectively. The data were analyzed with descriptive statistics, student test and correlation analysis. Correlation between SA and sleep quality was -0.664(P < 0001), Pearson correlation between SA and thermal comfort was -0.276(P = 0.016) and between SA and eye fatigue was 0.57 (P < 0001). Based on these results, it can be concluded that improvement of thermal conditions and reduce state anxiety level can be reduce eye fatigue and increase the sleep quality in shift work nurses.

The effects of state anxiety and thermal comfort on sleep quality and eye fatigue in shift work nurses

PubMed Central

Dehghan, Habibollah; Azmoon, Hiva; Souri, Shiva; Akbari, Jafar

2014-01-01

Psychological problems as state anxiety (SA) in the work environment has negative effect on the employees life especially shift work nurses, i.e. negative effect on mental and physical health (sleep quality, eye fatigue and comfort thermal). The purpose of this study was determination of effects of state anxiety and thermal comfort on sleep quality and eye fatigue in shift work nurses. Methods: This cross-sectional research conducted on 82 shift-work personnel of 18 nursing workstations of Isfahan hospitals in 2012. To measure the SA, sleep quality, visual fatigue and thermal comfort, Spielberger state-trait anxiety inventory, Pittsburg sleep quality index, eye fatigue questionnaire and thermal comfort questionnaire were used respectively. The data were analyzed with descriptive statistics, student test and correlation analysis. Results: Correlation between SA and sleep quality was −0.664(P < 0001), Pearson correlation between SA and thermal comfort was −0.276(P = 0.016) and between SA and eye fatigue was 0.57 (P < 0001). Conclusion: Based on these results, it can be concluded that improvement of thermal conditions and reduce state anxiety level can be reduce eye fatigue and increase the sleep quality in shift work nurses. PMID:25077165

Fatigue Crack Propagation from Notched Specimens of 304 SS in elevated Temperature Aqueous Environment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wire, G. L.; Mills, W. J.

2002-08-01

Fatigue crack propagation (FCP) rates for 304 stainless steel (304SS) were determined in 24 degree C and 288 degree C air and 288 degree C water using double-edged notch (DEN) specimens of 304 stainless steel (304 SS). Test performed at matched loading conditions in air and water at 288 degree C with 20-6- cc h[sub]2/kg h[sub]2O provided a direct comparison of the relative crack growth rates in air and water over a wide range of crack growth rates. The DEN crack extension ranged from short cracks (0.03-0.25 mm) to long cracks up to 4.06 mm, which are consistent with conventionalmore » deep crack tests. Crack growth rates of 304 SS in water were about 12 times the air rate. This 12X environmental enhancement persisted to crack extensions up to 4.06 mm, far outside the range associated with short crack effects. The large environmental degradation for 304 SS crack growth is consistent with the strong reduction of fatigue life in high hydrogen water. Further, very similar environmental effects w ere reported in fatigue crack growth tests in hydrogen water chemistry (HWC). Most literature data in high hydrogen water show only a mild environmental effect for 304 SS, of order 2.5 times air or less, but the tests were predominantly performed at high cyclic stress intensity or equivalently, high air rates. The environmental effect in low oxygen environments at low stress intensity depends strongly on both the stress ratio, R, and the load rise time, T[sub]r, as recently reported for austenitic stainless steel in BWR water. Fractography was performed for both tests in air and water. At 288 degree C in water, the fracture surfaces were crisply faceted with a crystallographic appearance, and showed striations under high magnification. The cleavage-like facets on the fracture surfaces suggest that hydrogen embrittlement is the primary cause of accelerated cracking.« less

Temporal separation and self-rating of alertness as indicators of driver fatigue in commercial motor vehicle operators.

PubMed

Belz, Steven M; Robinson, Gary S; Casali, John G

2004-01-01

This on-road field investigation employed, for the first time, a completely automated trigger-based data collection system capable of evaluating driver performance in an extended-duration real-world commercial motor vehicle environment. The study examined the use of self-assessment of fatigue (Karolinska Sleepiness Scale) and temporal separation (minimum time to collision, minimum headway, and mean headway) as indicators of driver fatigue. Without exception, the correlation analyses for both the self-rating of alertness and temporal separation yielded models low in associative ability; neither metric was found to be a valid indicator of driver fatigue. In addition, based upon the data collected for this research, preliminary evidence suggests that driver fatigue onset within a real-world driving environment does not appear to follow the standard progression of events associated with the onset of fatigue within a simulated driving environment. Application of this research includes the development of an on-board driver performance/fatigue monitoring system that could potentially assist drivers in identifying the onset of fatigue.

Hydrogen Assisted Cracking in Pearlitic Steel Rods: The Role of Residual Stresses Generated by Fatigue Precracking

PubMed Central

Toribio, Jesús; Aguado, Leticia; Lorenzo, Miguel; Kharin, Viktor

2017-01-01

Stress corrosion cracking (SCC) of metals is an issue of major concern in engineering since this phenomenon causes many catastrophic failures of structural components in aggressive environments. SCC is even more harmful under cathodic conditions promoting the phenomenon known as hydrogen assisted cracking (HAC), hydrogen assisted fracture (HAF) or hydrogen embrittlement (HE). A common way to assess the susceptibility of a given material to HAC, HAF or HE is to subject a cracked rod to a constant extension rate tension (CERT) test until it fractures in this harsh environment. This paper analyzes the influence of a residual stress field generated by fatigue precracking on the sample’s posterior susceptibility to HAC. To achieve this goal, numerical simulations were carried out of hydrogen diffusion assisted by the stress field. Firstly, a mechanical simulation of the fatigue precracking was developed for revealing the residual stress field after diverse cyclic loading scenarios and posterior stress field evolution during CERT loading. Afterwards, a simulation of hydrogen diffusion assisted by stress was carried out considering the residual stresses after fatigue and the superposed rising stresses caused by CERT loading. Results reveal the key role of the residual stress field after fatigue precracking in the HAC phenomena in cracked steel rods as well as the beneficial effect of compressive residual stress. PMID:28772845

System-Level Heat Transfer Analysis, Thermal- Mechanical Cyclic Stress Analysis, and Environmental Fatigue Modeling of a Two-Loop Pressurized Water Reactor. A Preliminary Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mohanty, Subhasish; Soppet, William; Majumdar, Saurin

This report provides an update on an assessment of environmentally assisted fatigue for light water reactor components under extended service conditions. This report is a deliverable in April 2015 under the work package for environmentally assisted fatigue under DOE's Light Water Reactor Sustainability program. In this report, updates are discussed related to a system level preliminary finite element model of a two-loop pressurized water reactor (PWR). Based on this model, system-level heat transfer analysis and subsequent thermal-mechanical stress analysis were performed for typical design-basis thermal-mechanical fatigue cycles. The in-air fatigue lives of components, such as the hot and cold legs,more » were estimated on the basis of stress analysis results, ASME in-air fatigue life estimation criteria, and fatigue design curves. Furthermore, environmental correction factors and associated PWR environment fatigue lives for the hot and cold legs were estimated by using estimated stress and strain histories and the approach described in NUREG-6909. The discussed models and results are very preliminary. Further advancement of the discussed model is required for more accurate life prediction of reactor components. This report only presents the work related to finite element modelling activities. However, in between multiple tensile and fatigue tests were conducted. The related experimental results will be presented in the year-end report.« less

Appropriate Mechanochemical Conditions for Corrosion-Fatigue Testing of Magnesium Alloys for Temporary Bioimplant Applications

NASA Astrophysics Data System (ADS)

Harandi, Shervin Eslami; Singh Raman, R. K.

2015-05-01

Magnesium (Mg) alloys possess great potential as bioimplants. A temporary implant employed as support for the repair of a fractured bone must possess sufficient strength to maintain their mechanical integrity for the required duration of healing. However, Mg alloys are susceptible to sudden cracking or fracture under the simultaneous action of cyclic loading and the corrosive physiological environment, i.e., corrosion fatigue (CF). Investigations of such fracture should be performed under appropriate mechanochemical conditions that appropriately simulate the actual human body conditions. This article reviews the existing knowledge on CF of Mg alloys in simulated body fluid and describes a relatively more accurate testing procedure developed in the authors' laboratory.

Analysis of Railroad Car Truck and Wheel Fatigue : Part 1. Service Load Data and Procedures for the Development of Fatigue Performance Criteria.

DOT National Transportation Integrated Search

1975-05-01

The development of fatigue performance standards for freight car truck components and wheels requires a knowledge of the fluctuation service load environment, and a basis for stating the conservatism of the design with respect to the environment. On ...

Fatigue in U.S. Astronauts Onboard the International Space Station: Environmental Factors, Operational Impacts, and Implementation of Countermeasures

NASA Technical Reports Server (NTRS)

Scheuring, R. A.; Moomaw, R. C.; Johnston, S. L.

2014-01-01

Since 2000, US astronauts have been supporting missions up to a six month duration on the International Space Station (ISS). Crewmembers have experienced fatigue for reasons similar to military deployments. Astronauts experience psychological stressors such as heavy workloads, extended duty periods, circadian misalignment, inadequate/ineffective sleep, and loss of the environmental cues of a gravity environment. Complicating the psychological stressors are environmental factors; distracting background noise, unexpected and variable mission schedules, unfavorable thermal control, elevated CO2 levels, and an unusual sleep environment with schedules that impinge on pre-sleep periods. Physiological contributors to poor sleep and fatigue include a cephalad fluid shift and back pain. Restful sleep is further challenged due to a lack of gravity-related proprioceptive cues and need for restraints. The term "space fog" has been used by astronauts to describe a phenomenon of forgetfulness, slowed reaction time and transient confusion while trying to complete tasks. There is a distinct temporal correlation with arrival on the Space Station and the onset of slowed cognitive skills and a spontaneous resolution that may take up to 6 weeks. The Genesis of this phenomenon may be chronic fatigue secondary to transitioning from a planar environment to a 360deg microgravity perspective. Recently, countermeasures to improve sleep duration and quality in astronauts on the ISS have been instituted with moderate degrees of success as measured by self-reaction time (psychomotor vigilance task testing), actigraphy, and subjective reports. Judicious use of stimulants and hypnotics, light therapy, controlled sleep periods and sleep shifting and reducing ambient CO2 levels are a few of the most promising countermeasures being used in space to improve sleep and reduce fatigue.

Compassion Fatigue, Burnout, and Compassion Satisfaction Among Oncology Nurses in the United States and Canada.

PubMed

Wu, Stacey; Singh-Carlson, Savitri; Odell, Annie; Reynolds, Grace; Su, Yuhua

2016-07-01

To examine the experiences of compassion fatigue, burnout, and compassion satisfaction among oncology nurses in the United States and Canada. 
. Quantitative, descriptive, nonexperimental.
. Online survey with members from the Canadian Association of Nursing Oncology and the Oncology Nursing Society.
. 486 American and 63 Canadian practicing oncology nurses.
. The Professional Quality of Life (ProQOL) scale, version 5, and modified Abendroth Demographic Questionnaire were administered through FluidSurveys™, an online data collection instrument. Chi-square tests of independence were used to investigate associations between demographic characteristics, health, personal stressors, and work-related characteristics to experiences of compassion fatigue, burnout, and compassion satisfaction. Compassion fatigue was measured using the subscales of secondary traumatic stress and burnout. 
. Compassion fatigue, burnout, and compassion satisfaction.
. Demographic characteristics were similar in American and Canadian participants, and both cohorts reported comparable levels of compassion fatigue, burnout, and compassion satisfaction. Perception of team cohesiveness within the workplace environment was found to be significant for both groups, as indicated by significant relationships in all three subscales of secondary traumatic stress, burnout, and compassion satisfaction in the ProQOL.
. Healthy and supportive work environments are imperative to nurses' health, well-being, and satisfaction. Improvements in the workplace can help prevent negative sequelae, as well as improve health outcomes for patients and nurses, decrease nurse turnover, and reduce healthcare expenditures. 
. Findings can be used to implement institutional changes, such as creating policies and guidelines for the development of preventive interventions and psychosocial support for nurses.

Redistribution of Welding Residual Stresses of Crack Tip Opening Displacement Specimen by Local Compression.

PubMed

Kim, Young-Gon; Song, Kuk-Hyun; Lee, Dong-Hoon; Joo, Sung-Min

2018-03-01

The demand of crack tip opening displacement (CTOD) test which evaluates fracture toughness of a cracked material is very important to ensure the stability of structure under severe service environment. The validity of the CTOD test result is judged using several criterions of the specification standards. One of them is the artificially generated fatigue pre-crack length inside the specimen. For acceptable CTOD test results, fatigue pre-crack must have a reasonable sharp crack front. The propagation of fatigue crack started from the tip of the machined notch, which might have propagated irregularly due to residual stress field. To overcome this problem, test codes suggest local compression method, reversed bending method and stepwise high-R ratio method to reduce the disparity of residual stress distribution inside the specimen. In this paper, the relation between the degree of local compression and distribution of welding residual stress has been analyzed by finite element analyses in order to determine the amount of effective local compression of the test piece. Analysis results show that initial welding residual stress is dramatically varied three-dimensionally while cutting, notch machining and local compressing due to the change of internal restraint force. From the simulation result, the authors find that there is an optimum amount of local compression to modify regularly for generating fatigue pre-crack propagation. In the case of 0.5% compressions of the model width is the most effective for uniforming residual stress distribution.

Fatigue in seafarers working in the offshore oil and gas re-supply industry: effects of safety climate, psychosocial work environment and shift arrangement.

PubMed

Hystad, Sigurd W; Saus, Evelyn-Rose; Sætrevik, Bjørn; Eid, Jarle

2013-01-01

This study examined the influence of safety climate and psychosocial work environment on the reported fatigue of seafarers working in the offshore oil and gas re-supply industry (n = 402). We found that seafarers who reported high psychological demands and perceived the organisational-level safety climate negatively,reported significantly more mental fatigue, physical fatigue, and lack of energy. In addition, seafarers who reported having high levels of job control reported being significantly less mentally fatigued. We also found some combined effects of safety climate and shift arrangement. Organisational-level safety climate did not influence the levels of physical fatigue in seafarers working on the night shift. On the contrary, seafarers working during the days reported to be more physically fatigued when they perceived the organisational-level climate to be negative compared with the positive. The opposite effect was found for group-level safety climate: seafarers working during the nights reported to be more physically fatigued when they perceived the group-level climate to be negative compared with the positive. The results from this study point to the importance of taking into consideration aspects of the psychosocial work environment and safety climate,and their potential impact on fatigue and safety in the maritime organisations.

Risk factors and visual fatigue of baggage X-ray security screeners: a structural equation modelling analysis.

PubMed

Yu, Rui-Feng; Yang, Lin-Dong; Wu, Xin

2017-05-01

This study identified the risk factors influencing visual fatigue in baggage X-ray security screeners and estimated the strength of correlations between those factors and visual fatigue using structural equation modelling approach. Two hundred and five X-ray security screeners participated in a questionnaire survey. The result showed that satisfaction with the VDT's physical features and the work environment conditions were negatively correlated with the intensity of visual fatigue, whereas job stress and job burnout had direct positive influences. The path coefficient between the image quality of VDT and visual fatigue was not significant. The total effects of job burnout, job stress, the VDT's physical features and the work environment conditions on visual fatigue were 0.471, 0.469, -0.268 and -0.251 respectively. These findings indicated that both extrinsic factors relating to VDT and workplace environment and psychological factors including job burnout and job stress should be considered in the workplace design and work organisation of security screening tasks to reduce screeners' visual fatigue. Practitioner Summary: This study identified the risk factors influencing visual fatigue in baggage X-ray security screeners and estimated the strength of correlations between those factors and visual fatigue. The findings were of great importance to the workplace design and the work organisation of security screening tasks to reduce screeners' visual fatigue.

Driving time modulates accommodative response and intraocular pressure.

PubMed

Vera, Jesús; Diaz-Piedra, Carolina; Jiménez, Raimundo; Morales, José M; Catena, Andrés; Cardenas, David; Di Stasi, Leandro L

2016-10-01

Driving is a task mainly reliant on the visual system. Most of the time, while driving, our eyes are constantly focusing and refocusing between the road and the dashboard or near and far traffic. Thus, prolonged driving time should produce visual fatigue. Here, for the first time, we investigated the effects of driving time, a common inducer of driver fatigue, on two ocular parameters: the accommodative response (AR) and the intraocular pressure (IOP). A pre/post-test design has been used to assess the impact of driving time on both indices. Twelve participants (out of 17 recruited) completed the study (5 women, 24.42±2.84years old). The participants were healthy and active drivers with no visual impairment or pathology. They drove for 2h in a virtual driving environment. We assessed AR and IOP before and after the driving session, and also collected subjective measures of arousal and fatigue. We found that IOP and AR decreased (i.e., the accommodative lag increased) after the driving session (p=0.03 and p<0.001, respectively). Moreover, the nearest distances tested (20cm, 25cm, and 33cm) induced the highest decreases in AR (corrected p-values<0.05). Consistent with these findings, the subjective levels of arousal decreased and levels of fatigue increased after the driving session (all p-values<0.001). These results represent an innovative step towards an objective, valid, and reliable assessment of fatigue-impaired driving based on visual fatigue signs. Copyright © 2016 Elsevier Inc. All rights reserved.

Effects of Soundscape on the Environmental Restoration in Urban Natural Environments.

PubMed

Zhang, Yuan; Kang, Jian; Kang, Joe

2017-01-01

According to the attention restoration theory, directed attention is a limited physiological resource and is susceptible to fatigue by overuse. Natural environments are a healthy resource, which allows and promotes the restoration of individuals within it from their state of directed attention fatigue. This process is called the environmental restoration on individuals, and it is affected both positively and negatively by environmental factors. By considering the relationship among the three components of soundscape, that is, people, sound and the environment, this study aims to explore the effects of soundscape on the environmental restoration in urban natural environments. A field experiment was conducted with 70 participants (four groups) in an urban natural environment (Shenyang, China). Directed attention was first depleted with a 50-min 'consumption' phase, followed by a baseline measurement of attention level. Three groups then engaged in 40 min of restoration in the respective environments with similar visual surroundings but with different sounds present, after which attention levels were re-tested. The fourth group did not undergo restoration and was immediately re-tested. The difference between the two test scores, corrected for the practice effect, represents the attention restoration of individuals exposed to the respective environments. An analysis of variance was performed, demonstrating that the differences between the mean values for each group were statistically significant [sig. = 0.027 (<0.050)]. The results showed that the mean values (confidence interval of 95%) of each group are as follows: 'natural sounds group' (8.4), 'traffic sounds group' (2.4) and 'machine sounds group' (-1.8). It can be concluded that (1) urban natural environments, with natural sounds, have a positive effect on the restoration of an individuals' attention and (2) the presence of different types of sounds has significantly divergent effects on the environmental restoration.

Fatigue analysis of assembled marine floating platform for special purposes under complex water environments

NASA Astrophysics Data System (ADS)

Ma, Guang-ying; Yao, Yun-long

2018-03-01

In this paper, the fatigue lives of a new type of assembled marine floating platform for special purposes were studied. Firstly, by using ANSYS AQWA software, the hydrodynamic model of the platform was established. Secondly, the structural stresses under alternating change loads were calculated under complex water environments, such as wind, wave, current and ice. The minimum fatigue lives were obtained under different working conditions. The analysis results showed that the fatigue life of the platform structure can meet the requirements

Validation of a Smartphone-Based Approach to In Situ Cognitive Fatigue Assessment

PubMed Central

Linden, Mark

2017-01-01

Background Acquired Brain Injuries (ABIs) can result in multiple detrimental cognitive effects, such as reduced memory capability, concentration, and planning. These effects can lead to cognitive fatigue, which can exacerbate the symptoms of ABIs and hinder management and recovery. Assessing cognitive fatigue is difficult due to the largely subjective nature of the condition and existing assessment approaches. Traditional methods of assessment use self-assessment questionnaires delivered in a medical setting, but recent work has attempted to employ more objective cognitive tests as a way of evaluating cognitive fatigue. However, these tests are still predominantly delivered within a medical environment, limiting their utility and efficacy. Objective The aim of this research was to investigate how cognitive fatigue can be accurately assessed in situ, during the quotidian activities of life. It was hypothesized that this assessment could be achieved through the use of mobile assistive technology to assess working memory, sustained attention, information processing speed, reaction time, and cognitive throughput. Methods The study used a bespoke smartphone app to track daily cognitive performance, in order to assess potential levels of cognitive fatigue. Twenty-one participants with no prior reported brain injuries took place in a two-week study, resulting in 81 individual testing instances being collected. The smartphone app delivered three cognitive tests on a daily basis: (1) Spatial Span to measure visuospatial working memory; (2) Psychomotor Vigilance Task (PVT) to measure sustained attention, information processing speed, and reaction time; and (3) a Mental Arithmetic Test to measure cognitive throughput. A smartphone-optimized version of the Mental Fatigue Scale (MFS) self-assessment questionnaire was used as a baseline to assess the validity of the three cognitive tests, as the questionnaire has already been validated in multiple peer-reviewed studies. Results The most highly correlated results were from the PVT, which showed a positive correlation with those from the prevalidated MFS, measuring 0.342 (P<.008). Scores from the cognitive tests were entered into a regression model and showed that only reaction time in the PVT was a significant predictor of fatigue (P=.016, F=2.682, 95% CI 9.0-84.2). Higher scores on the MFS were related to increases in reaction time during our mobile variant of the PVT. Conclusions The results show that the PVT mobile cognitive test developed for this study could be used as a valid and reliable method for measuring cognitive fatigue in situ. This test would remove the subjectivity associated with established self-assessment approaches and the need for assessments to be performed in a medical setting. Based on our findings, future work could explore delivering a small set of tests with increased duration to further improve measurement reliability. Moreover, as the smartphone assessment tool can be used as part of everyday life, additional sources of data relating to physiological, psychological, and environmental context could be included within the analysis to improve the nature and precision of the assessment process. PMID:28818818

Computational simulation of acoustic fatigue for hot composite structures

NASA Technical Reports Server (NTRS)

Singhal, S. N.; Nagpal, V. K.; Murthy, P. L. N.; Chamis, C. C.

1991-01-01

This paper presents predictive methods/codes for computational simulation of acoustic fatigue resistance of hot composite structures subjected to acoustic excitation emanating from an adjacent vibrating component. Select codes developed over the past two decades at the NASA Lewis Research Center are used. The codes include computation of (1) acoustic noise generated from a vibrating component, (2) degradation in material properties of the composite laminate at use temperature, (3) dynamic response of acoustically excited hot multilayered composite structure, (4) degradation in the first-ply strength of the excited structure due to acoustic loading, and (5) acoustic fatigue resistance of the excited structure, including propulsion environment. Effects of the laminate lay-up and environment on the acoustic fatigue life are evaluated. The results show that, by keeping the angled plies on the outer surface of the laminate, a substantial increase in the acoustic fatigue life is obtained. The effect of environment (temperature and moisure) is to relieve the residual stresses leading to an increase in the acoustic fatigue life of the excited panel.

Computational simulation of acoustic fatigue for hot composite structures

NASA Technical Reports Server (NTRS)

Singhal, Surendra N.; Murthy, Pappu L. N.; Chamis, Christos C.; Nagpal, Vinod K.; Sutjahjo, Edhi

1991-01-01

Predictive methods/computer codes for the computational simulation of acoustic fatigue resistance of hot composite structures subjected to acoustic excitation emanating from an adjacent vibrating component are discussed. Select codes developed over the past two decades at the NASA Lewis Research Center are used. The codes include computation of acoustic noise generated from a vibrating component, degradation in material properties of a composite laminate at use temperature, dynamic response of acoustically excited hot multilayered composite structure, degradation in the first ply strength of the excited structure due to acoustic loading, and acoustic fatigue resistance of the excited structure, including the propulsion environment. Effects of the laminate lay-up and environment on the acoustic fatigue life are evaluated. The results show that, by keeping the angled plies on the outer surface of the laminate, a substantial increase in the acoustic fatigue life is obtained. The effect of environment (temperature and moisture) is to relieve the residual stresses leading to an increase in the acoustic fatigue life of the excited panel.

Influences of Processing and Fatigue Cycling on Residual Stresses in a NiCrY-Coated Powder Metallurgy Disk Superalloy

NASA Astrophysics Data System (ADS)

Gabb, T. P.; Rogers, R. B.; Nesbitt, J. A.; Miller, R. A.; Puleo, B. J.; Johnson, D.; Telesman, J.; Draper, S. L.; Locci, I. E.

2017-11-01

Oxidation and corrosion can attack superalloy disk surfaces exposed to increasing operating temperatures in some turbine engine environments. Any potential protective coatings must also be resistant to harmful fatigue cracking during service. The objective of this study was to investigate how residual stresses evolve in one such coating. Fatigue specimens of a powder metallurgy-processed disk superalloy were coated with a NiCrY coating, shot peened, and then subjected to fatigue in air at room and high temperatures. The effects of this processing and fatigue cycling on axial residual stresses and other aspects of the coating were assessed. While shot peening did induce beneficial compressive residual stresses in the coating and substrate, these stresses relaxed in the coating with subsequent heating. Several cast alloys having compositions near the coating were subjected to thermal expansion and tensile stress relaxation tests to help explain this response of residual stresses in the coating. For the coated fatigue specimens, this response contributed to earlier cracking of the coating than for the uncoated surface during long intervals of cycling at 760 °C. Yet, substantial compressive residual stresses still remained in the substrate adjacent to the coating, which were sufficient to suppress fatigue cracking there. The coating continued to protect the substrate from hot corrosion pitting, even after fatigue cracks initiated in the coating.

Hydraulic Fatigue-Testing Machine

NASA Technical Reports Server (NTRS)

Hodo, James D.; Moore, Dennis R.; Morris, Thomas F.; Tiller, Newton G.

1987-01-01

Fatigue-testing machine applies fluctuating tension to number of specimens at same time. When sample breaks, machine continues to test remaining specimens. Series of tensile tests needed to determine fatigue properties of materials performed more rapidly than in conventional fatigue-testing machine.

Wavelet multiresolution complex network for decoding brain fatigued behavior from P300 signals

NASA Astrophysics Data System (ADS)

Gao, Zhong-Ke; Wang, Zi-Bo; Yang, Yu-Xuan; Li, Shan; Dang, Wei-Dong; Mao, Xiao-Qian

2018-09-01

Brain-computer interface (BCI) enables users to interact with the environment without relying on neural pathways and muscles. P300 based BCI systems have been extensively used to achieve human-machine interaction. However, the appearance of fatigue symptoms during operation process leads to the decline in classification accuracy of P300. Characterizing brain cognitive process underlying normal and fatigue conditions constitutes a problem of vital importance in the field of brain science. We in this paper propose a novel wavelet decomposition based complex network method to efficiently analyze the P300 signals recorded in the image stimulus test based on classical 'Oddball' paradigm. Initially, multichannel EEG signals are decomposed into wavelet coefficient series. Then we construct complex network by treating electrodes as nodes and determining the connections according to the 2-norm distances between wavelet coefficient series. The analysis of topological structure and statistical index indicates that the properties of brain network demonstrate significant distinctions between normal status and fatigue status. More specifically, the brain network reconfiguration in response to the cognitive task in fatigue status is reflected as the enhancement of the small-worldness.

Fatigue Strength Prediction for Titanium Alloy TiAl6V4 Manufactured by Selective Laser Melting

NASA Astrophysics Data System (ADS)

Leuders, Stefan; Vollmer, Malte; Brenne, Florian; Tröster, Thomas; Niendorf, Thomas

2015-09-01

Selective laser melting (SLM), as a metalworking additive manufacturing technique, received considerable attention from industry and academia due to unprecedented design freedom and overall balanced material properties. However, the fatigue behavior of SLM-processed materials often suffers from local imperfections such as micron-sized pores. In order to enable robust designs of SLM components used in an industrial environment, further research regarding process-induced porosity and its impact on the fatigue behavior is required. Hence, this study aims at a transfer of fatigue prediction models, established for conventional process-routes, to the field of SLM materials. By using high-resolution computed tomography, load increase tests, and electron microscopy, it is shown that pore-based fatigue strength predictions for a titanium alloy TiAl6V4 have become feasible. However, the obtained accuracies are subjected to scatter, which is probably caused by the high defect density even present in SLM materials manufactured following optimized processing routes. Based on thorough examination of crack surfaces and crack initiation sites, respectively, implications for optimization of prediction accuracy of the models in focus are deduced.

The high frequency light load fatigue testing machine based on giant magnetostrictive material and stroke multiplier

NASA Astrophysics Data System (ADS)

Wang, M. D.; Li, D. S.; Huang, Y.; Zhang, C.; Zhong, K. M.; Sun, L. N.

2013-08-01

In the notebook and clamshell mobile phone, data communication wire often requires repeated bending. Generally, communication wire with the actual application conditions, the test data cannot assess bending resistance performance of data communication wire is tested conventionally using wires with weights of 90 degree to test bending number, this test method and device is not fully reflect the fatigue performance in high frequency and light load application condition, at the same time it has a large difference between the test data of the long-term reliability of high frequency and low load conditions. In this paper, high frequency light load fatigue testing machine based on the giant magnetostrictive material and stroke multiplier is put forward, in which internal reflux stroke multiplier is driven by giant magnetostrictive material to realize the rapid movement of light load. This fatigue testing device has the following advantages: (1) When the load is far less than the friction, reducing friction is very effective to improve the device performance. Because the body is symmetrical, the friction loss of radial does not exist in theory, so the stress situation of mechanism is good with high transmission efficiency and long service life. (2) The installation position of the output hydraulic cylinder, can be arranged conveniently as ordinary cylinder. (3) Reciprocating frequency, displacement and speed of high frequency movement can be programmed easily to change with higher position precision. (4)Hydraulic oil in this device is closed to transmit, which does not produce any environment pollution. The device has no hydraulic pump and tank, and less energy conversion processes, so it is with the trend of green manufacturing.

Development of biomimetic in vitro fatigue assessment for UHMWPE implant materials.

PubMed

Scholz, Ronja; Knyazeva, Marina; Porchetta, Dario; Wegner, Nils; Senatov, Fedor; Salimon, Alexey; Kaloshkin, Sergey; Walther, Frank

2018-05-26

An important research goal in the field of biomaterials lies in the progressive amendment of in vivo tests with suitable in vitro experiments. Such approaches are gaining more significance nowadays because of an increasing demand on life sciences and the ethical issues bound to the sacrifice of animals for the sake of scientific research. Another advantage of transferring the experiments to the in vitro field is the possibility of accurately control the boundary conditions and experimental parameters in order to reduce the need of validation tests involving animals. With the aim to reduce the amount of needed in vivo studies for this cause, a short-time in vitro test procedure using instrumented load increase tests with superimposed environmental loading has been developed at TUD to assess the mechanical long-term durability of ultra-high molecular weight polyethylene (UHMWPE) under fatigue loading in a biological environment. Copyright © 2018 Elsevier Ltd. All rights reserved.

Fitness for duty: A 3 minute version of the Psychomotor Vigilance Test predicts fatigue related declines in luggage screening performance

PubMed Central

Basner, Mathias; Rubinstein, Joshua

2011-01-01

Objective To evaluate the ability of a 3-min Psychomotor Vigilance Test (PVT) to predict fatigue related performance decrements on a simulated luggage screening task (SLST). Methods Thirty-six healthy non-professional subjects (mean age 30.8 years, 20 female) participated in a 4 day laboratory protocol including a 34 hour period of total sleep deprivation with PVT and SLST testing every 2 hours. Results Eleven and 20 lapses (355 ms threshold) on the PVT optimally divided SLST performance into high, medium, and low performance bouts with significantly decreasing threat detection performance A′. Assignment to the different SLST performance groups replicated homeostatic and circadian patterns during total sleep deprivation. Conclusions The 3 min PVT was able to predict performance on a simulated luggage screening task. Fitness-for-duty feasibility should now be tested in professional screeners and operational environments. PMID:21912278

The construction of life prediction models for the design of Stirling engine heater components

NASA Technical Reports Server (NTRS)

Petrovich, A.; Bright, A.; Cronin, M.; Arnold, S.

1983-01-01

The service life of Stirling-engine heater structures of Fe-based high-temperature alloys is predicted using a numerical model based on a linear-damage approach and published test data (engine test data for a Co-based alloy and tensile-test results for both the Co-based and the Fe-based alloys). The operating principle of the automotive Stirling engine is reviewed; the economic and technical factors affecting the choice of heater material are surveyed; the test results are summarized in tables and graphs; the engine environment and automotive duty cycle are characterized; and the modeling procedure is explained. It is found that the statistical scatter of the fatigue properties of the heater components needs to be reduced (by decreasing the porosity of the cast material or employing wrought material in fatigue-prone locations) before the accuracy of life predictions can be improved.

Fitness for duty: a 3-minute version of the Psychomotor Vigilance Test predicts fatigue-related declines in luggage-screening performance.

PubMed

Basner, Mathias; Rubinstein, Joshua

2011-10-01

To evaluate the ability of a 3-minute Psychomotor Vigilance Test (PVT) to predict fatigue-related performance decrements on a simulated luggage-screening task (SLST). Thirty-six healthy nonprofessional subjects (mean age = 30.8 years, 20 women) participated in a 4-day laboratory protocol including a 34-hour period of total sleep deprivation with PVT and SLST testing every 2 hours. Eleven and 20 lapses (355-ms threshold) on the PVT optimally divided SLST performance into high-, medium-, and low-performance bouts with significantly decreasing threat detection performance A'. Assignment to the different SLST performance groups replicated homeostatic and circadian patterns during total sleep deprivation. The 3-minute PVT was able to predict performance on a simulated luggage-screening task. Fitness-for-duty feasibility should now be tested in professional screeners and operational environments.

Flight service evaluation of composite helicopter components

NASA Technical Reports Server (NTRS)

Mardoian, G. H.; Ezzo, M. B.

1986-01-01

This report presents an assessment of composite helicopter tail rotor spars and horizontal stabilizers, exposed to the effects of the environment, after up to five and a half years of commercial service. This evaluation is supported by test results of helicopter components and panels which have been exposed to outdoor environmental effects since September 1979. Full scale static and fatigue tests have been conducted on graphite/epoxy and Kevlar/epoxy composite components obtained from Sikorsky Model S-76 helicopters in commercial operations in the Gulf Coast region of Louisiana. Small scale static and fatigue tests are being conducted on coupons obtained from panels under exposure to outdoor conditions in Stratford, Connecticut and West Palm, Florida. The panel layups are representative of the S-76 components. Additionally, this report discusses the results of moisture absorption evaluations and strength tests on the S-76 components and composite panels with up to five years of outdoor exposure.

Fatigue Life Estimation under Cumulative Cyclic Loading Conditions

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; McGaw, Michael A; Halford, Gary R.

1999-01-01

The cumulative fatigue behavior of a cobalt-base superalloy, Haynes 188 was investigated at 760 C in air. Initially strain-controlled tests were conducted on solid cylindrical gauge section specimens of Haynes 188 under fully-reversed, tensile and compressive mean strain-controlled fatigue tests. Fatigue data from these tests were used to establish the baseline fatigue behavior of the alloy with 1) a total strain range type fatigue life relation and 2) the Smith-Wastson-Topper (SWT) parameter. Subsequently, two load-level multi-block fatigue tests were conducted on similar specimens of Haynes 188 at the same temperature. Fatigue lives of the multi-block tests were estimated with 1) the Linear Damage Rule (LDR) and 2) the nonlinear Damage Curve Approach (DCA) both with and without the consideration of mean stresses generated during the cumulative fatigue tests. Fatigue life predictions by the nonlinear DCA were much closer to the experimentally observed lives than those obtained by the LDR. In the presence of mean stresses, the SWT parameter estimated the fatigue lives more accurately under tensile conditions than under compressive conditions.

Surface protection overview

NASA Technical Reports Server (NTRS)

Levine, S. R.

1982-01-01

A first-cut integrated environmental attack life prediction methodology for hot section components is addressed. The HOST program is concerned with oxidation and hot corrosion attack of metallic coatings as well as their degradation by interdiffusion with the substrate. The effects of the environment and coatings on creep/fatigue behavior are being addressed through a joint effort with the Fatigue sub-project. An initial effort will attempt to scope the problem of thermal barrier coating life prediction. Verification of models will be carried out through benchmark rig tests including a 4 atm. replaceable blade turbine and a 50 atm. pressurized burner rig.

Assessing Corrosion Damage and Corrosion Progression in Multistrand Anchor Systems in Use at Corps Projects

DTIC Science & Technology

2013-07-01

14  4.8  Corrosion fatigue ...particularly vulnerable. ERDC TR-13-3 15 4.8 Corrosion fatigue Fatigue that takes place in a corrosive environment can reduce the number of...cycles generally considered acceptable before fatigue and fatigue -related failure occur. ERDC TR-13-3 16 5 Historical Perspective: Post-Tensioned

Fatigue crack growth behavior of pressure vessel steels and submerged arc weldments in a high-temperature pressurized water environment

NASA Astrophysics Data System (ADS)

Liaw, P. K.; Logsdon, W. A.; Begley, J. A.

1989-10-01

The fatigue crack growth rate (FCGR) properties of SA508 C1 2a and SA533 Gr A C1 2 pressure vessel steels and the corresponding automatic submerged are weldments were developed in a high-temperature pressurized water (HPW) environment at 288 °C (550°F) and 7.2 MPa (1044 psi) at load ratios of 0.02 and 0.50. The HPW enviromment FCGR properties of these pressure vessel steels and submerged arc weldments were generally conservative, compared with the approrpriate American Society of Mechanical Engineers (ASME) Section XI water environmental reference curve. The growth rate of fatigue cracks in the base materials, however, was considerably faster in the HPW environment than in a corresponding 288°C (550°F) base line air environment. The growth rate of fatigue cracks in the two submerged are weldments was also accelerated in the HPW environment but to a significantly lesser degree than that demonstrated by the corresponding base materials. In the air environment, fatigue striations were observed, independent of material and load ratio, while in the HPW environment, some intergranular facets were present. The greater environmental effect on crack growth rates displayed by the base materials, as compared with the weldments, was attributed to a different sulfide composition and morphology.

Design and Fabrication of a Composite Morphing Radiator Panel Using High Conductivity Fibers

NASA Technical Reports Server (NTRS)

Wescott, Matthew T.; McQuien, J. Scott; Bertagne, Christopher L.; Whitcomb, John D.; Hart, Darren J.; Erickson, Lisa R.

2017-01-01

Upcoming crewed space missions will involve large internal and external heat loads and require advanced thermal control systems to maintain a desired internal environment temperature. Radiators with at least 12:1 turndown ratios (the ratio between the maximum and minimum heat rejection rates) will be needed. However, current technologies are only able to achieve turndown ratios of approximately 3:1. A morphing radiator capable of altering shape could significantly increase turndown capabilities. Shape memory alloys offer qualities that may be well suited for this endeavor; their temperature-dependent phase changes could offer radiators the ability to passively control heat rejection. In 2015, a morphing radiator prototype was constructed and tested in a thermal vacuum environment, where it successfully demonstrated the morphing behavior and variable heat rejection. Newer composite prototypes have since been designed and manufactured using two distinct types of SMA materials. These models underwent temperature cycling tests in a thermal vacuum chamber and a series of fatigue tests to characterize the lifespan of these designs. The focus of this paper is to present the design approach and testing of the morphing composite facesheet. The discussion includes: an overall description of the project background, definition of performance requirements, composite materials selection, use of analytic and numerical design tools, facesheet fabrication, and finally fatigue testing with accompanying results.

Fatigue Test Design: Scenarios for Biaxial Fatigue Testing of a 60-Meter Wind Turbine Blade

DOE Office of Scientific and Technical Information (OSTI.GOV)

Post, Nathan

Current practice in commercial certification of wind turbine blades is to perform separate flap and lead-lag fatigue tests. The National Renewable Energy Laboratory has been researching and evaluating biaxial fatigue testing techniques and demonstrating various options, typically on smaller-scale test articles at the National Wind Technology Center. This report evaluates some of these biaxial fatigue options in the context of application to a multimegawatt blade certification test program at the Wind Technology Testing Center in Charlestown, Massachusetts.

Phenomenological aspects of fatigue cracking in as-received and hardened F82H modified steel exposed to lithiated water with dissolved hydrogen at 240°C

NASA Astrophysics Data System (ADS)

Maday, Marie-Françoise

2000-12-01

The low cycle fatigue (LCF) behaviour of F82H modified steel with three different degrees of hardness produced by specific thermal treatments has been investigated at 240°C under load control, in oxygen-free lithiated solutions containing either no or 2 ppm dissolved hydrogen. In all cases, it was found that the aqueous environments reduced the fatigue life of the material and promoted fracture modes different from those observed in air tests; the fracture modes comprised intergranular and transgranular quasi-cleavage separations as well as microvoid coalescence, which depended on material conditions and water chemistry. All these features were ascribed to a hydrogen-assisted-cracking (HAC) phenomenon, as the basic mechanism for controlling the fatigue behaviour of various F82H heats in lithiated solutions. The observed differences in HAC paths are discussed from the standpoint of material microstructural and substructural parameters.

Cumulative fatigue damage behavior of MAR M-247

NASA Technical Reports Server (NTRS)

Mcgaw, Michael A.; Halford, Gary R.; Kalluri, Sreeramesh

1991-01-01

The objective was to examine the room temperature fatigue and nonlinear cumulative fatigue damage behavior of the cast nickel-based superalloy, MAR M-247. The fatigue test matrix consisted of single-level, fully reversed fatigue experiments. Two series of tests were performed: one of the two baseline fatigue LCF (Low-Cycle Fatigue) life levels was used in the first loading block, and the HCF (High-Cycle Fatigue) baseline loading level was used in the second block in each series. For each series, duplicate tests were performed at each applied LCF life fraction.

Effect of outdoor exposure at ambient and elevated temperatures on fatigue life of Ti-6Al-4V titanium alloy sheet in the annealed and the solution treated and aged condition

NASA Technical Reports Server (NTRS)

Phillips, E. P.

1974-01-01

Specimens of Ti-6Al-4V titanium alloy sheet in the annealed and the solution-treated and aged heat-treatment condition were exposed outdoors at ambient and 560 K (550 F) temperatures to determine the effect of outdoor exposure on fatigue life. Effects of exposure were determined by comparing fatigue lives of exposed specimens to those of unexpected specimens. Two procedures for fatigue testing the exposed specimens were evaluated: (1) fatigue tests conducted outdoors by applying 1200 load cycles per week until failure occurred and (2) conventional fatigue tests (continuous cycling until failure occurred) conducted indoors after outdoor exposure under static load. The exposure period ranged from 9 to 28 months for the outdoor fatigue-test group and was 24 months for the static-load group. All fatigue tests were constant-amplitude bending of specimens containing a drilled hole (stress concentration factor of 1.6). The results of the tests indicate that the fatigue lives of solution-treated and aged specimens were significantly reduced by the outdoor exposure at 560 K but not by the exposure at ambient temperature. Fatigue lives of the annealed specimens were essentially unaffected by the outdoor exposure at either temperature. The two test procedures - outdoor fatigue test and indoor fatigue test after outdoor exposure - led to the same conclusions about exposure effects.

Working hours, sleep, salivary cortisol, fatigue and neuro-behavior during Mars analog mission: five crews study.

PubMed

Rai, Balwant; Foing, Bernard H; Kaur, Jasdeep

2012-05-16

The buoyancy of humans in exploring extreme space environments has been established during missions to the moon. Long duration missions like mission to Mars however, requires humans to adapt to systemic and complex environments beyond the human body's capacity. Astronauts will encounter both physiological and psychological extremes during this trip. Very few studies are conducted on effect of long duration work and sleepiness on cognitive performance. So, this study was planned to find out effects of leadership responsibility, sleepiness and long duration working hours on cognitive performance. The 30 members (leadership: normal; 10:20) were selected from MDRS crews (Mars Desert Research Station, USA). Neurobehavioral test performance, self-ratings of fatigue and sleepiness, and salivary cortisol levels were evaluated during first day, mid and end day of mission. The leadership group did not show any signs of reduced test performance, even in elevated fatigue and sleepiness. The leadership group had faster reaction times on end of mission as compared to first and after 7 day of mission. Salivary cortisol levels were significantly higher in leadership group as compared to normal group. The results suggest that long duration work and sleepiness does not affect the cognitive performance of crew member. Further study is required while taking into account all factors and large sample size to prove this fact. Copyright © 2012 Elsevier Ireland Ltd. All rights reserved.

Development of a high-frequency and large-stroke fatigue testing system for rubber

NASA Astrophysics Data System (ADS)

Chen, Gang; Wu, Hao; Gao, Jianwen; Lin, Qiang

2017-04-01

The limited capabilities of current fatigue testing machines have resulted in studies on the fatigue behavior of rubber under large-displacement amplitude and high frequency being very sparse. In this study, a fatigue testing system that can carry out large-displacement amplitude and high-frequency fatigue tests on rubber was developed using a moving magnet voice coil motor (MMVCM) actuator, with finite element analysis applied to analyze the thrust of the MMVCM actuator. The results of a series of cyclic tension tests conducted on vulcanized natural rubber specimens using the developed fatigue testing system verify that it has high precision, low noise, large-stroke, and high-frequency characteristics. Further, the load frame with the developed MMVCM actuator is feasible for material testing, especially for large-stroke and high-frequency fatigue tests.

Fatigue tests on big structure assemblies of concorde aircraft

NASA Technical Reports Server (NTRS)

Nguyen, V. P.; Perrais, J. P.

1972-01-01

Fatigue tests on structural assemblies of the Concorde supersonic transport aircraft are reported. Two main sections of the aircraft were subjected to pressure, mechanical load, and thermal static tests. The types of fatigue tests conducted and the results obtained are discussed. It was concluded that on a supersonic aircraft whose structural weight is a significant part of the weight analysis, many fatigue and static strength development tests should be made and fatigue and thermal tests of the structures are absolutely necessary.

Validation of a Smartphone-Based Approach to In Situ Cognitive Fatigue Assessment.

PubMed

Price, Edward; Moore, George; Galway, Leo; Linden, Mark

2017-08-17

Acquired Brain Injuries (ABIs) can result in multiple detrimental cognitive effects, such as reduced memory capability, concentration, and planning. These effects can lead to cognitive fatigue, which can exacerbate the symptoms of ABIs and hinder management and recovery. Assessing cognitive fatigue is difficult due to the largely subjective nature of the condition and existing assessment approaches. Traditional methods of assessment use self-assessment questionnaires delivered in a medical setting, but recent work has attempted to employ more objective cognitive tests as a way of evaluating cognitive fatigue. However, these tests are still predominantly delivered within a medical environment, limiting their utility and efficacy. The aim of this research was to investigate how cognitive fatigue can be accurately assessed in situ, during the quotidian activities of life. It was hypothesized that this assessment could be achieved through the use of mobile assistive technology to assess working memory, sustained attention, information processing speed, reaction time, and cognitive throughput. The study used a bespoke smartphone app to track daily cognitive performance, in order to assess potential levels of cognitive fatigue. Twenty-one participants with no prior reported brain injuries took place in a two-week study, resulting in 81 individual testing instances being collected. The smartphone app delivered three cognitive tests on a daily basis: (1) Spatial Span to measure visuospatial working memory; (2) Psychomotor Vigilance Task (PVT) to measure sustained attention, information processing speed, and reaction time; and (3) a Mental Arithmetic Test to measure cognitive throughput. A smartphone-optimized version of the Mental Fatigue Scale (MFS) self-assessment questionnaire was used as a baseline to assess the validity of the three cognitive tests, as the questionnaire has already been validated in multiple peer-reviewed studies. The most highly correlated results were from the PVT, which showed a positive correlation with those from the prevalidated MFS, measuring 0.342 (P<.008). Scores from the cognitive tests were entered into a regression model and showed that only reaction time in the PVT was a significant predictor of fatigue (P=.016, F=2.682, 95% CI 9.0-84.2). Higher scores on the MFS were related to increases in reaction time during our mobile variant of the PVT. The results show that the PVT mobile cognitive test developed for this study could be used as a valid and reliable method for measuring cognitive fatigue in situ. This test would remove the subjectivity associated with established self-assessment approaches and the need for assessments to be performed in a medical setting. Based on our findings, future work could explore delivering a small set of tests with increased duration to further improve measurement reliability. Moreover, as the smartphone assessment tool can be used as part of everyday life, additional sources of data relating to physiological, psychological, and environmental context could be included within the analysis to improve the nature and precision of the assessment process. ©Edward Price, George Moore, Leo Galway, Mark Linden. Originally published in JMIR Mhealth and Uhealth (http://mhealth.jmir.org), 17.08.2017.

Creep, Fatigue and Fracture Behavior of Environmental Barrier Coating and SiC-SiC Ceramic Matrix Composite Systems: The Role of Environment Effects

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Ghosn, Louis J.

2015-01-01

Advanced environmental barrier coating (EBC) systems for low emission SiCSiC CMC combustors and turbine airfoils have been developed to meet next generation engine emission and performance goals. This presentation will highlight the developments of NASAs current EBC system technologies for SiC-SiC ceramic matrix composite combustors and turbine airfoils, their performance evaluation and modeling progress towards improving the engine SiCSiC component temperature capability and long-term durability. Our emphasis has also been placed on the fundamental aspects of the EBC-CMC creep and fatigue behaviors, and their interactions with turbine engine oxidizing and moisture environments. The EBC-CMC environmental degradation and failure modes, under various simulated engine testing environments, in particular involving high heat flux, high pressure, high velocity combustion conditions, will be discussed aiming at quantifying the protective coating functions, performance and durability, and in conjunction with damage mechanics and fracture mechanics approaches.

The Effects of Hot Corrosion Pits on the Fatigue Resistance of a Disk Superalloy

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Telesman, Jack; Hazel, Brian; Mourer, David P.

2009-01-01

The effects of hot corrosion pits on low cycle fatigue life and failure modes of the disk superalloy ME3 were investigated. Low cycle fatigue specimens were subjected to hot corrosion exposures producing pits, then tested at low and high temperatures. Fatigue lives and failure initiation points were compared to those of specimens without corrosion pits. Several tests were interrupted to estimate the fraction of fatigue life that fatigue cracks initiated at pits. Corrosion pits significantly reduced fatigue life by 60 to 98 percent. Fatigue cracks initiated at a very small fraction of life for high temperature tests, but initiated at higher fractions in tests at low temperature. Critical pit sizes required to promote fatigue cracking were estimated, based on measurements of pits initiating cracks on fracture surfaces.

Fatigue Characterization of Alloy 10: a 1300F Disk Alloy for Small Gas Turbine Engines

NASA Technical Reports Server (NTRS)

Gayda, John

2000-01-01

A detailed fatigue characterization of Alloy 10, a high strength nickel-based disk alloy, was conducted on test coupons machined from a 'pancake' forging. Smooth bar, strain controlled fatigue testing at various R-ratios was run at representative bore, 750 F, and rim, 1300 F, temperatures. This was followed by notch fatigue testing (Kt=2) run under load control. Analysis of the fatigue data using a Smith-Watson-Topper approach and finite element analysis of the notch root was employed to understand material behavior in these tests. Smooth bar fatigue data showed a significant R-ratio dependence at either test temperature which could be accounted for using a Smith-Watson-Topper parameter (SWT). In general, fatigue life was longer at 750 F than 1300 F for a given SWT. For notch fatigue tests, life was longer at 750 F than 1300 F but only at higher stresses. This was attributed to differences in alloy strength. At lower stresses, finite element analysis suggested that convergence of fatigue life at both temperatures resulted from relaxation of stresses at the notch root in the 1300 F tests.

The Boeing 747 fatigue integrity program

NASA Technical Reports Server (NTRS)

Spencer, M. M.

1972-01-01

The fatigue integrity program which was established to insure economic operations and to provide foundation data for inspection and maintenance is discussed. Significant features of the 747 fatigue integrity program are: (1) fatigue analyses which are continually updated to reflect design changes, fatigue test results, and static and flight load survey measurements; (2) material selection and detail design by using initial fatigue analyses, service experience, and testing; and (3) fatigue testing to check detail design quality and to verify the analyses, culminated by the test of a structurally complete airframe. Fatigue stress analyses were performed with the aid of experimental as well as analytical procedures. Extensive application was made of the stress severity factor, developed at Boeing, for evaluating peak stresses in complex joints. A frame of reference was established by families of structural fatigue performance curves (S-N curves) encompassing the range of materials and fatigue qualities anticipated for the 747 airplane design.

The Effect of O2, H2O, and N2 on the Fatigue Crack Growth Behavior of an Alpha + Beta Titanium Alloy at 24 C and 177 C

NASA Technical Reports Server (NTRS)

Smith, Stephen W.; Piascik, Robert S.

2001-01-01

To study the effects of atmospheric species on the fatigue crack growth behavior of an a+B titanium alloy (Ti 6-2-2-2-2) at room temperature and 177 C, fatigue tests were performed in laboratory air, ultrahigh vacuum, and high purity water vapor, oxygen, nitrogen and helium at various partial pressures. Accelerated fatigue crack growth rates in laboratory air compared to ultrahigh vacuum are linked to the damaging effects of both water vapor and oxygen. Observations of the fatigue crack growth behavior in ultrahigh purity environments, along with surface film analysis using X-ray photoelectron spectroscopy (XPS), suggest that multiple crack-tip processes govern the damaging effects of air. Three possible mechanisms are proposed: 1) at low pressure (less than 10(exp -1) Pa), accelerated da/dN is likely due to monolayer adsorption on crack-tip surfaces presumably resulting in decreased bond strengths at the fatigue crack tip, 2) for pressures greater than 10(exp -1) Pa, accelerated da/dN in oxygen may result from oxidation at the crack tip limiting reversible slip, and 3) in water vapor, absorption of atomic hydrogen at the reactive crack tip resulting in process zone embrittlement.

Environmental Barrier Coating Development for SiC/SiC Ceramic Matrix Composites: Recent Advances and Future Directions

NASA Technical Reports Server (NTRS)

Zhu, Dongming

2016-01-01

This presentation briefly reviews the SiC/SiC major environmental and environment-fatigue degradations encountered in simulated turbine combustion environments, and thus NASA environmental barrier coating system evolution for protecting the SiC/SiC Ceramic Matrix Composites for meeting the engine performance requirements. The presentation will review several generations of NASA EBC materials systems, EBC-CMC component system technologies for SiC/SiC ceramic matrix composite combustors and turbine airfoils, highlighting the temperature capability and durability improvements in simulated engine high heat flux, high pressure, high velocity, and with mechanical creep and fatigue loading conditions. This paper will also focus on the performance requirements and design considerations of environmental barrier coatings for next generation turbine engine applications. The current development emphasis is placed on advanced NASA candidate environmental barrier coating systems for SiC/SiC CMCs, their performance benefits and design limitations in long-term operation and combustion environments. The efforts have been also directed to developing prime-reliant, self-healing 2700F EBC bond coat; and high stability, lower thermal conductivity, and durable EBC top coats. Major technical barriers in developing environmental barrier coating systems, the coating integrations with next generation CMCs having the improved environmental stability, erosion-impact resistance, and long-term fatigue-environment system durability performance will be described. The research and development opportunities for turbine engine environmental barrier coating systems by utilizing improved compositions, state-of-the-art processing methods, and simulated environment testing and durability modeling will be briefly discussed.

Maternal fatigue and its relationship to the caregiving environment.

PubMed

White, Carmel Parker; White, Mark B; Fox, Melissa A

2009-12-01

For women with an autoimmune illness, fatigue can be a debilitating symptom that impacts many aspects of their life. There is scant research on maternal fatigue and its impact on the caregiving environment for either well women or women with chronic illnesses. The objective of this study was to examine the role maternal fatigue played in the caregiving environment, specifically in the mother's experience of the daily hassles of parenting, the discipline style she employed, and how she monitored her child's whereabouts. Two-hundred sixty-two mothers participated in this study: 103 mothers with multiple sclerosis (MS), 68 mothers with rheumatoid arthritis (RA), and a comparison group of 91 well mothers. Mothers completed questionnaires assessing their self-reported levels of fatigue, depression, quality and quantity of sleep, parenting daily hassles, discipline styles, and monitoring. After sleep, depression, and number of children were controlled for, fatigue explained additional variance in predicting monitoring for all three groups of mothers. Fatigue was also a significant predictor of parenting daily hassles for both well mothers and mothers with RA, but not for mothers with MS. For mothers with MS, it was the covariates (i.e., the number of children in the family and sleep quality and quantity) that were predictive of parenting daily hassles. Several explanations for mothers with MS not being as influenced by fatigue are discussed.

Low visual information-processing speed and attention are predictors of fatigue in elementary and junior high school students

PubMed Central

2011-01-01

Background Fatigue is a common complaint among elementary and junior high school students, and is known to be associated with reduced academic performance. Recently, we demonstrated that fatigue was correlated with decreased cognitive function in these students. However, no studies have identified cognitive predictors of fatigue. Therefore, we attempted to determine independent cognitive predictors of fatigue in these students. Methods We performed a prospective cohort study. One hundred and forty-two elementary and junior high school students without fatigue participated. They completed a variety of paper-and-pencil tests, including list learning and list recall tests, kana pick-out test, semantic fluency test, figure copying test, digit span forward test, and symbol digit modalities test. The participants also completed computerized cognitive tests (tasks A to E on the modified advanced trail making test). These cognitive tests were used to evaluate motor- and information-processing speed, immediate and delayed memory function, auditory and visual attention, divided and switching attention, retrieval of learned material, and spatial construction. One year after the tests, a questionnaire about fatigue (Japanese version of the Chalder Fatigue Scale) was administered to all the participants. Results After the follow-up period, we confirmed 40 cases of fatigue among 118 students. In multivariate logistic regression analyses adjusted for grades and gender, poorer performance on visual information-processing speed and attention tasks was associated with increased risk of fatigue. Conclusions Reduced visual information-processing speed and poor attention are independent predictors of fatigue in elementary and junior high school students. PMID:21672212

Low visual information-processing speed and attention are predictors of fatigue in elementary and junior high school students.

PubMed

Mizuno, Kei; Tanaka, Masaaki; Fukuda, Sanae; Yamano, Emi; Shigihara, Yoshihito; Imai-Matsumura, Kyoko; Watanabe, Yasuyoshi

2011-06-14

Fatigue is a common complaint among elementary and junior high school students, and is known to be associated with reduced academic performance. Recently, we demonstrated that fatigue was correlated with decreased cognitive function in these students. However, no studies have identified cognitive predictors of fatigue. Therefore, we attempted to determine independent cognitive predictors of fatigue in these students. We performed a prospective cohort study. One hundred and forty-two elementary and junior high school students without fatigue participated. They completed a variety of paper-and-pencil tests, including list learning and list recall tests, kana pick-out test, semantic fluency test, figure copying test, digit span forward test, and symbol digit modalities test. The participants also completed computerized cognitive tests (tasks A to E on the modified advanced trail making test). These cognitive tests were used to evaluate motor- and information-processing speed, immediate and delayed memory function, auditory and visual attention, divided and switching attention, retrieval of learned material, and spatial construction. One year after the tests, a questionnaire about fatigue (Japanese version of the Chalder Fatigue Scale) was administered to all the participants. After the follow-up period, we confirmed 40 cases of fatigue among 118 students. In multivariate logistic regression analyses adjusted for grades and gender, poorer performance on visual information-processing speed and attention tasks was associated with increased risk of fatigue. Reduced visual information-processing speed and poor attention are independent predictors of fatigue in elementary and junior high school students. © 2011 Mizuno et al; licensee BioMed Central Ltd.

Investigation of flaw geometry and loading effects on plane strain fracture in metallic structures

NASA Technical Reports Server (NTRS)

Hall, L. R.; Finger, R. W.

1971-01-01

The effects on fracture and flaw growth of weld-induced residual stresses, combined bending and tension stresses, and stress fields adjacent to circular holes in 2219-T87 aluminum and 5AI-2.5Sn(ELI) titanium alloys were evaluated. Static fracture tests were conducted in liquid nitrogen; fatigue tests were performed in room air, liquid nitrogen, and liquid hydrogen. Evaluation of results was based on linear elastic fracture mechanics concepts and was directed to improving existing methods of estimating minimum fracture strength and fatigue lives for pressurized structure in spacecraft and booster systems. Effects of specimen design in plane-strain fracture toughness testing were investigated. Four different specimen types were tested in room air, liquid nitrogen and liquid hydrogen environments using the aluminum and titanium alloys. Interferometry and holograph were used to measure crack-opening displacements in surface-flawed plexiglass test specimens. Comparisons were made between stress intensities calculated using displacement measurements, and approximate analytical solutions.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Skochko, G.W.; Herrmann, T.P.

Axial load cycling fatigue tests of threaded fasteners are useful in determining fastener fatigue failure or design properties. By using appropriate design factors between the failure and design fatigue strengths, such tests are used to establish fatigue failure and design parameters of fasteners for axial and bending cyclic load conditions. This paper reviews the factors which influence the fatigue strength of low Alloy steel threaded fasteners, identifies those most significant to fatigue strength, and provides design guidelines based on the direct evaluation of fatigue tests of threaded fasteners. Influences on fatigue strength of thread manufacturing process (machining and rolling ofmore » threads), effect of fastener membrane and bending stresses, thread root radii, fastener sizes, fastener tensile strength, stress relaxation, mean stress, and test temperature are discussed.« less

Effect of additional heat treatment of 2024-T3 on the growth of fatigue crack in air and in vacuum

NASA Technical Reports Server (NTRS)

Louwaard, E. P.

1986-01-01

In order to determine the influence of ductility on the fatigue crack growth rate of aluminum alloys, fatigue tests were carried out on central notched specimens of 2024-T3 and 2024-T8 sheet material. The 2024-T8 material was obtained by an additional heat treatment applied on 2024-T3 (18 hours at 192 C), which increased the static yield strength from 43.6 to 48.9 kgf/sq mm. A change in the ultimate strength was not observed. Fatigue tests were carried out on both materials in humid air and in high vacuum. According to a new crack propagation model, crack extension is supported to be caused by a slip-related process and debonding triggered by the environment. This model predicts an effect of the ductility on the crack growth rate which should be smaller in vacuum than in humid air; however, this was not confirmed. In humid air the crack-growth rate in 2024-T8 was about 2 times faster than in 2024-T3, while in vacuum the ratio was about 2.5. Crack closure measurements gave no indications that crack closure played a significant role in both materials. Some speculative explanations are briefly discussed.

Assessing fatigue in inflammatory bowel disease: comparison of three fatigue scales.

PubMed

Norton, C; Czuber-Dochan, W; Bassett, P; Berliner, S; Bredin, F; Darvell, M; Forbes, A; Gay, M; Ream, E; Terry, H

2015-07-01

Fatigue is commonly reported by patients with inflammatory bowel disease (IBD), both in quiescent and active disease. Few fatigue scales have been tested in IBD. To assess three fatigue assessment scales in IBD and to determine correlates of fatigue. Potential participants (n = 2131) were randomly selected from an IBD organisation's members' database; 605 volunteered and were posted three fatigue scales: Inflammatory Bowel Disease Fatigue scale, Multidimensional Fatigue Inventory and Multidimensional Assessment Fatigue scale and questionnaires assessing anxiety, depression, quality of life (QoL) and IBD activity. The questionnaires were tested for stability over time with another group (n = 70) of invited participants. Internal consistency was measured by Cronbach's alpha and test-retest reliability by the intraclass correlation coefficient (ICC). Four hundred and sixty-five of 605 (77%) questionnaires were returned; of 70 invited, 48/70 returned test (68.6%) and 41/70 (58.6%) returned retest. The three scales are highly correlated (P < 0.001). Test-retest suggests reasonable agreement with ICC values between 0.65 and 0.84. Lower age, female gender, IBD diagnosis, anxiety, depression and QoL were associated with fatigue (P < 0.001) on univariable analysis. However, on multivariable analysis only depression and low QoL were consistently associated with fatigue, while female gender was associated on most scales. IBD diagnosis, age and other factors were not consistently associated with severity or impact of fatigue once other variables were controlled for. All three fatigue scales are likely to measure IBD fatigue adequately. Responsiveness to change has not been tested. Depression, poorer QoL and probably female gender are the major associations of fatigue in IBD. © 2015 John Wiley & Sons Ltd.

Review on stress corrosion and corrosion fatigue failure of centrifugal compressor impeller

NASA Astrophysics Data System (ADS)

Sun, Jiao; Chen, Songying; Qu, Yanpeng; Li, Jianfeng

2015-03-01

Corrosion failure, especially stress corrosion cracking and corrosion fatigue, is the main cause of centrifugal compressor impeller failure. And it is concealed and destructive. This paper summarizes the main theories of stress corrosion cracking and corrosion fatigue and its latest developments, and it also points out that existing stress corrosion cracking theories can be reduced to the anodic dissolution (AD), the hydrogen-induced cracking (HIC), and the combined AD and HIC mechanisms. The corrosion behavior and the mechanism of corrosion fatigue in the crack propagation stage are similar to stress corrosion cracking. The effects of stress ratio, loading frequency, and corrosive medium on the corrosion fatigue crack propagation rate are analyzed and summarized. The corrosion behavior and the mechanism of stress corrosion cracking and corrosion fatigue in corrosive environments, which contain sulfide, chlorides, and carbonate, are analyzed. The working environments of the centrifugal compressor impeller show the behavior and the mechanism of stress corrosion cracking and corrosion fatigue in different corrosive environments. The current research methods for centrifugal compressor impeller corrosion failure are analyzed. Physical analysis, numerical simulation, and the fluid-structure interaction method play an increasingly important role in the research on impeller deformation and stress distribution caused by the joint action of aerodynamic load and centrifugal load.

Shift work and employee fatigue: implications for occupational health nursing.

PubMed

Yumang-Ross, Doreen J; Burns, Candace

2014-06-01

Long work hours and irregular shifts are part of the nation's 24-hour society and contribute to employee fatigue. Factors affecting employee fatigue are circadian rhythm, sleep quality and quantity, individual health, the environment, and work tasks. Employee fatigue contributes to accidents and injuries, and affects occupational performance, safety, and health. These findings should be used by occupational health nurses to address fatigue management and develop comprehensive fatigue management programs. Copyright 2014, SLACK Incorporated.

Low cycle fatigue and creep-fatigue behavior of Ni-based alloy 230 at 850 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xiang; Yang, Zhiqing; Sokolov, Mikhail A

Strain-controlled low cycle fatigue (LCF) and creep-fatigue testing of Ni-based alloy 230 were carried out at 850 C. The material creep-fatigue life decreased compared with its low cycle fatigue life at the same total strain range. Longer hold time at peak tensile strain further reduced the material creep-fatigue life. Based on the electron backscatter diffraction, a novel material deformation characterization method was applied, which revealed that in low cycle fatigue testing as the total strain range increased, the deformation was segregated to grain boundaries since the test temperature was higher than the material equicohesive temperature and grain boundaries became weakermore » regions compared with grains. Creep-fatigue tests enhanced the localized deformation, resulting in material interior intergranular cracking, and accelerated material damage. Precipitation in alloy 230 helped slip dispersion, favorable for fatigue property, but grain boundary cellular precipitates formed after material exposure to the elevated temperature had a deleterious effect on the material low cycle fatigue and creep-fatigue property.« less

Effect of Different Levels of Localized Muscle Fatigue on Knee Position Sense

PubMed Central

Gear, William S.

2011-01-01

There is little information available regarding how proprioceptive abilities decline as the amount of exertion increases during exercise. The purpose of this study was to determine the role of different levels of fatigue on knee joint position sense. A repeated measures design was used to examine changes in active joint reposition sense (AJRS) prior to and following three levels of fatigue. Eighteen participants performed knee extension and flexion isokinetic exercise until torque output was 90%, 70%, or 50% of the peak hamstring torque for three consecutive repetitions. Active joint reposition sense at 15, 30, or 45 degrees was tested following the isokinetic exercise session. Following testing of the first independent measure, participants were given a 20 minute rest period. Testing procedures were repeated for two more exercise sessions following the other levels of fatigue. Testing of each AJRS test angle was conducted on three separate days with 48 hours between test days. Significant main effect for fatigue was indicated (p = 0.001). Pairwise comparisons indicated a significant difference between the pre-test and following 90% of peak hamstring torque (p = 0.02) and between the pre-test and following 50% of peak hamstring torque (p = 0.02). Fatigue has long been theorized to be a contributing factor in decreased proprioceptive acuity, and therefore a contributing factor to joint injury. The findings of the present study indicate that fatigue may have an effect on proprioception following mild and maximum fatigue. Key points A repeated measures design was used to examine the effect of different levels of fatigue on active joint reposition sense (AJRS) of the knee at joint angles of 15°, 30° and 45° of flexion. A statistically significant main effect for fatigue was found, specifically between no fatigue and mild fatigue and no fatigue and maximum fatigue. A statistically significant interaction effect between AJRS and fatigue was not found. Secondary analysis of the results indicated a potential plateau effect of AJRS as fatigue continues to increase. Further investigation of the effect of increasing levels of fatigue on proprioception is warranted. PMID:24149565

Effect of different levels of localized muscle fatigue on knee position sense.

PubMed

Gear, William S

2011-01-01

There is little information available regarding how proprioceptive abilities decline as the amount of exertion increases during exercise. The purpose of this study was to determine the role of different levels of fatigue on knee joint position sense. A repeated measures design was used to examine changes in active joint reposition sense (AJRS) prior to and following three levels of fatigue. Eighteen participants performed knee extension and flexion isokinetic exercise until torque output was 90%, 70%, or 50% of the peak hamstring torque for three consecutive repetitions. Active joint reposition sense at 15, 30, or 45 degrees was tested following the isokinetic exercise session. Following testing of the first independent measure, participants were given a 20 minute rest period. Testing procedures were repeated for two more exercise sessions following the other levels of fatigue. Testing of each AJRS test angle was conducted on three separate days with 48 hours between test days. Significant main effect for fatigue was indicated (p = 0.001). Pairwise comparisons indicated a significant difference between the pre-test and following 90% of peak hamstring torque (p = 0.02) and between the pre-test and following 50% of peak hamstring torque (p = 0.02). Fatigue has long been theorized to be a contributing factor in decreased proprioceptive acuity, and therefore a contributing factor to joint injury. The findings of the present study indicate that fatigue may have an effect on proprioception following mild and maximum fatigue. Key pointsA repeated measures design was used to examine the effect of different levels of fatigue on active joint reposition sense (AJRS) of the knee at joint angles of 15°, 30° and 45° of flexion.A statistically significant main effect for fatigue was found, specifically between no fatigue and mild fatigue and no fatigue and maximum fatigue.A statistically significant interaction effect between AJRS and fatigue was not found.Secondary analysis of the results indicated a potential plateau effect of AJRS as fatigue continues to increase.Further investigation of the effect of increasing levels of fatigue on proprioception is warranted.

Fatigue data for polyether ether ketone (PEEK) under fully-reversed cyclic loading

PubMed Central

Shrestha, Rakish; Simsiriwong, Jutima; Shamsaei, Nima

2016-01-01

In this article, the data obtained from the uniaxial fully-reversed fatigue experiments conducted on polyether ether ketone (PEEK), a semi-crystalline thermoplastic, are presented. The tests were performed in either strain-controlled or load-controlled mode under various levels of loading. The data are categorized into four subsets according to the type of tests, including (1) strain-controlled fatigue tests with adjusted frequency to obtain the nominal temperature rise of the specimen surface, (2) strain-controlled fatigue tests with various frequencies, (3) load-controlled fatigue tests without step loadings, and (4) load-controlled fatigue tests with step loadings. Accompanied data for each test include the fatigue life, the maximum (peak) and minimum (valley) stress–strain responses for each cycle, and the hysteresis stress–strain responses for each collected cycle in a logarithmic increment. A brief description of the experimental method is also given. PMID:26937465

Fatigue data for polyether ether ketone (PEEK) under fully-reversed cyclic loading.

PubMed

Shrestha, Rakish; Simsiriwong, Jutima; Shamsaei, Nima

2016-03-01

In this article, the data obtained from the uniaxial fully-reversed fatigue experiments conducted on polyether ether ketone (PEEK), a semi-crystalline thermoplastic, are presented. The tests were performed in either strain-controlled or load-controlled mode under various levels of loading. The data are categorized into four subsets according to the type of tests, including (1) strain-controlled fatigue tests with adjusted frequency to obtain the nominal temperature rise of the specimen surface, (2) strain-controlled fatigue tests with various frequencies, (3) load-controlled fatigue tests without step loadings, and (4) load-controlled fatigue tests with step loadings. Accompanied data for each test include the fatigue life, the maximum (peak) and minimum (valley) stress-strain responses for each cycle, and the hysteresis stress-strain responses for each collected cycle in a logarithmic increment. A brief description of the experimental method is also given.

Computational Modeling to Predict Fatigue Behavior of NiTi Stents: What Do We Need?

PubMed Central

Dordoni, Elena; Petrini, Lorenza; Wu, Wei; Migliavacca, Francesco; Dubini, Gabriele; Pennati, Giancarlo

2015-01-01

NiTi (nickel-titanium) stents are nowadays commonly used for the percutaneous treatment of peripheral arterial disease. However, their effectiveness is still debated in the clinical field. In fact a peculiar cyclic biomechanical environment is created before and after stent implantation, with the risk of device fatigue failure. An accurate study of the device fatigue behavior is of primary importance to ensure a successful stenting procedure. Regulatory authorities recognize the possibility of performing computational analyses instead of experimental tests for the assessment of medical devices. However, confidence in numerical methods is only possible after verification and validation of the models used. For the case of NiTi stents, mechanical properties are strongly dependent on the device dimensions and the whole treatments undergone during manufacturing process. Hence, special attention should be paid to the accuracy of the description of the device geometry and the material properties implementation into the numerical code, as well as to the definition of the fatigue limit. In this paper, a path for setting up an effective numerical model for NiTi stent fatigue assessment is proposed and the results of its application in a specific case study are illustrated. PMID:26011245

Tension-Compression Fatigue of a Nextel™720/alumina Composite at 1200 °C in Air and in Steam

NASA Astrophysics Data System (ADS)

Lanser, R. L.; Ruggles-Wrenn, M. B.

2016-08-01

Tension-compression fatigue behavior of an oxide-oxide ceramic-matrix composite was investigated at 1200 °C in air and in steam. The composite is comprised of an alumina matrix reinforced with Nextel™720 alumina-mullite fibers woven in an eight harness satin weave (8HSW). The composite has no interface between the fiber and matrix, and relies on the porous matrix for flaw tolerance. Tension-compression fatigue behavior was studied for cyclical stresses ranging from 60 to 120 MPa at a frequency of 1.0 Hz. The R ratio (minimum stress to maximum stress) was -1.0. Fatigue run-out was defined as 105 cycles and was achieved at 80 MPa in air and at 70 MPa in steam. Steam reduced cyclic lives by an order of magnitude. Specimens that achieved fatigue run-out were subjected to tensile tests to failure to characterize the retained tensile properties. Specimens subjected to prior cyclic loading in air retained 100 % of their tensile strength. The steam environment severely degraded tensile properties. Tension-compression cyclic loading was considerably more damaging than tension-tension cyclic loading. Composite microstructure, as well as damage and failure mechanisms were investigated.

Use of Slow Strain Rate Tensile Testing to Assess the Ability of Several Superalloys to Resist Environmentally-Assisted Intergranular Cracking

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Telesman, Jack; Banik, Anthony; McDevitt, Erin

2014-01-01

Intergranular fatigue crack initiation and growth due to environmental degradation, especially at notched features, can often limit the fatigue life of disk superalloys at high temperatures. For clear comparisons, the effects of alloy composition on cracking in air needs to be understood and compared separately from variables associated with notches and cracks such as effective stress concentration, plastic flow, stress relaxation, and stress redistribution. The objective of this study was to attempt using simple tensile tests of specimens with uniform gage sections to compare the effects of varied alloy composition on environment-assisted cracking of several powder metal and cast and wrought superalloys including ME3, LSHR, Udimet 720(TradeMark) ATI 718Plus(Registered TradeMark) alloy, Haynes 282(Trademark), and Inconel 740(TradeMark) Slow and fast strain-rate tensile tests were found to be a useful tool to compare propensities for intergranular surface crack initiation and growth. The effects of composition and heat treatment on tensile fracture strain and associated failure modes were compared. Environment interactions were determined to often limit ductility, by promoting intergranular surface cracking. The response of various superalloys and heat treatments to slow strain rate tensile testing varied substantially, showing that composition and microstructure can significantly influence environmental resistance to cracking.

Predicting Fatigue Lives Of Metal-Matrix/Fiber Composites

NASA Technical Reports Server (NTRS)

Bartolotta, Paul A.

1994-01-01

Method of prediction of fatigue lives of intermetallic-matrix/fiber composite parts at high temperatures styled after method of universal slopes. It suffices to perform relatively small numbers of fatigue tests. Data from fatigue tests correlated with tensile-test data by fitting universal-slopes equation to both sets of data. Thereafter, universal-slopes equation used to predict fatigue lives from tensile properties.

Experimental and modeling results of creep fatigue life of Inconel 617 and Haynes 230 at 850 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xiang; Sokolov, Mikhail A; Sham, Sam

Creep fatigue testing of Ni-based superalloy Inconel 617 and Haynes 230 were conducted in the air at 850 C. Tests were performed with fully reversed axial strain control at a total strain range of 0.5%, 1.0% or 1.5% and hold time at maximum tensile strain for 3, 10 or 30 min. In addition, two creep fatigue life prediction methods, i.e. linear damage summation and frequency-modified tensile hysteresis energy modeling, were evaluated and compared with experimental results. Under all creep fatigue tests, Haynes 230 performed better than Inconel 617. Compared to the low cycle fatigue life, the cycles to failure formore » both materials decreased under creep fatigue test conditions. Longer hold time at maximum tensile strain would cause a further reduction in both material creep fatigue life. The linear damage summation could predict the creep fatigue life of Inconel 617 for limited test conditions, but considerably underestimated the creep fatigue life of Haynes 230. In contrast, frequency-modified tensile hysteresis energy modeling showed promising creep fatigue life prediction results for both materials.« less

Evaluation of fatigue life of CRM-reinforced SMA and its relationship to dynamic stiffness.

PubMed

Mashaan, Nuha Salim; Karim, Mohamed Rehan; Abdel Aziz, Mahrez; Ibrahim, Mohd Rasdan; Katman, Herda Yati; Koting, Suhana

2014-01-01

Fatigue cracking is an essential problem of asphalt concrete that contributes to pavement damage. Although stone matrix asphalt (SMA) has significantly provided resistance to rutting failure, its resistance to fatigue failure is yet to be fully addressed. The aim of this study is to evaluate the effect of crumb rubber modifier (CRM) on stiffness and fatigue properties of SMA mixtures at optimum binder content, using four different modification levels, namely, 6%, 8%, 10%, and 12% CRM by weight of the bitumen. The testing undertaken on the asphalt mix comprises the dynamic stiffness (indirect tensile test), dynamic creep (repeated load creep), and fatigue test (indirect tensile fatigue test) at temperature of 25°C. The indirect tensile fatigue test was conducted at three different stress levels (200, 300, and 400 kPa). Experimental results indicate that CRM-reinforced SMA mixtures exhibit significantly higher fatigue life compared to the mixtures without CRM. Further, higher correlation coefficient was obtained between the fatigue life and resilient modulus as compared to permanent strain; thus resilient modulus might be a more reliable indicator in evaluating the fatigue life of asphalt mixture.

Experimental and modeling results of creep-fatigue life of Inconel 617 and Haynes 230 at 850 °C

NASA Astrophysics Data System (ADS)

Chen, Xiang; Sokolov, Mikhail A.; Sham, Sam; Erdman, Donald L., III; Busby, Jeremy T.; Mo, Kun; Stubbins, James F.

2013-01-01

Creep-fatigue testing of Ni-based superalloy Inconel 617 and Haynes 230 were conducted in the air at 850 °C. Tests were performed with fully reversed axial strain control at a total strain range of 0.5%, 1.0% or 1.5% and hold time at maximum tensile strain for 3, 10 or 30 min. In addition, two creep-fatigue life prediction methods, i.e. linear damage summation and frequency-modified tensile hysteresis energy modeling, were evaluated and compared with experimental results. Under all creep-fatigue tests, Haynes 230 performed better than Inconel 617. Compared to the low cycle fatigue life, the cycles to failure for both materials decreased under creep-fatigue test conditions. Longer hold time at maximum tensile strain would cause a further reduction in both material creep-fatigue life. The linear damage summation could predict the creep-fatigue life of Inconel 617 for limited test conditions, but considerably underestimated the creep-fatigue life of Haynes 230. In contrast, frequency-modified tensile hysteresis energy modeling showed promising creep-fatigue life prediction results for both materials.

Corrosion-Fatigue Crack Growth in Plates: A Model Based on the Paris Law

PubMed Central

Toribio, Jesús; Matos, Juan-Carlos; González, Beatriz

2017-01-01

In this paper, a Paris law-based model is presented whereby crack propagation occurs under cyclic loading in air (fatigue) and in an aggressive environment (corrosion-fatigue) for the case of corner cracks (with a wide range of aspect ratios in the matter of the initial cracks) in finite-thickness plates of 316L austenitic stainless steel subjected to tension, bending, or combined (tension + bending) loading. Results show that the cracks tend during their growth towards a preferential propagation path, exhibiting aspect ratios slightly lower than unity only for the case of very shallow cracks, and diminishing as the crack grows (increasing the relative crack depth)—more intensely in the case of bending than in the case of tension (the mixed loading tension/bending representing an intermediate case). In addition, the crack aspect ratios during fatigue propagation evolution are lower in fatigue (in air) than in corrosion-fatigue (in aggressive environment). PMID:28772798

Experimental Study on Surrogate Nuclear Fuel Rods under Reversed Cyclic Bending

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Wang, Jy-An John

The mechanical behavior of spent nuclear fuel (SNF) rods under reversed cyclic bending or bending fatigue must be understood to evaluate their vibration integrity in a transportation environment. This is especially important for high-burnup fuels (>45 GWd/MTU), which have the potential for increased structural damage. It has been demonstrated that the bending fatigue of SNF rods can be effectively studied using surrogate rods. In this investigation, surrogate rods made of stainless steel (SS) 304 cladding and aluminum oxide pellets were tested under load or moment control at a variety of amplitude levels at 5 Hz using the Cyclic Integrated Reversible-Bendingmore » Fatigue Tester developed at Oak Ridge National Laboratory. The behavior of the rods was further characterized using flexural rigidity and hysteresis data, and fractography was performed on the failed rods. The proposed surrogate rods captured many of the characteristics of deformation and failure mode observed in SNF, including the linear-to-nonlinear deformation transition and large residual curvature in static tests, PPI and PCMI failure mechanisms, and large variation in the initial structural condition. Rod degradation was measured and characterized by measuring the flexural rigidity; the degradation of the rigidity depended on both the moment amplitude applied and the initial structural condition of the rods. It was also shown that a cracking initiation site can be located on the internal surface or the external surface of cladding. Finally, fatigue damage to the bending rods can be described in terms of flexural rigidity, and the fatigue life of rods can be predicted once damage model parameters are properly evaluated. The developed experimental approach, test protocol, and analysis method can be used to study the vibration integrity of SNF rods in the future.« less

Fatigue crack identification method based on strain amplitude changing

NASA Astrophysics Data System (ADS)

Guo, Tiancai; Gao, Jun; Wang, Yonghong; Xu, Youliang

2017-09-01

Aiming at the difficulties in identifying the location and time of crack initiation in the castings of helicopter transmission system during fatigue tests, by introducing the classification diagnostic criteria of similar failure mode to find out the similarity of fatigue crack initiation among castings, an engineering method and quantitative criterion for detecting fatigue cracks based on strain amplitude changing is proposed. This method is applied on the fatigue test of a gearbox housing, whose results indicates: during the fatigue test, the system alarms when SC strain meter reaches the quantitative criterion. The afterwards check shows that a fatigue crack less than 5mm is found at the corresponding location of SC strain meter. The test result proves that the method can provide accurate test data for strength life analysis.

Corrosion Fatigue of Metals in Marine Environments

DTIC Science & Technology

1981-07-01

Fatigue of Alloys 2014-T6 and 2024 -T4 in Air and Artificial Seawater I62 Fatigue Life of 2024 -T4 Aluminum Alloy Specimens... life was still considerably reduced. The effect of prior corrosion pitting on the fatigue life of Alloy 2024 -T4 was investigated by Harmsworth.215...Harmsworth, C. L, " Effect of Corrosion on the Fatigue Behavior of 2024 -T4 Aluminum Alloy ",

Speech perception and production in severe environments

NASA Astrophysics Data System (ADS)

Pisoni, David B.

1990-09-01

The goal was to acquire new knowledge about speech perception and production in severe environments such as high masking noise, increased cognitive load or sustained attentional demands. Changes were examined in speech production under these adverse conditions through acoustic analysis techniques. One set of studies focused on the effects of noise on speech production. The experiments in this group were designed to generate a database of speech obtained in noise and in quiet. A second set of experiments was designed to examine the effects of cognitive load on the acoustic-phonetic properties of speech. Talkers were required to carry out a demanding perceptual motor task while they read lists of test words. A final set of experiments explored the effects of vocal fatigue on the acoustic-phonetic properties of speech. Both cognitive load and vocal fatigue are present in many applications where speech recognition technology is used, yet their influence on speech production is poorly understood.

Stress corrosion cracking and corrosion fatigue characterisation of MgZn1Ca0.3 (ZX10) in a simulated physiological environment.

PubMed

Jafari, Sajjad; Raman, R K Singh; Davies, Chris H J; Hofstetter, Joelle; Uggowitzer, Peter J; Löffler, Jörg F

2017-01-01

Magnesium (Mg) alloys have attracted great attention as potential materials for biodegradable implants. It is essential that an implant material possesses adequate resistance to cracking/fracture under the simultaneous actions of corrosion and mechanical stresses, i.e., stress corrosion cracking (SCC) and/or corrosion fatigue (CF). This study investigates the deformation behaviour of a newly developed high-strength low-alloy Mg alloy, MgZn1Ca0.3 (ZX10), processed at two different extrusion temperatures of 325 and 400°C (named E325 and E400, respectively), under slow strain tensile and cyclic tension-compression loadings in air and modified simulated body fluid (m-SBF). Extrusion resulted in a bimodal grain size distribution with recrystallised grain sizes of 1.2 μm ± 0.8 μm and 7 ± 5 μm for E325 and E400, respectively. E325 possessed superior tensile and fatigue properties to E400 when tested in air. This is mainly attributed to a grain-boundary strengthening mechanism. However, both E325 and E400 were found to be susceptible to SCC at a strain rate of 3.1×10 -7 s -1 in m-SBF. Moreover, both E325 and E400 showed similar fatigue strength when tested in m-SBF. This is explained on the basis of crack initiation from localised corrosion following tests in m-SBF. Crown Copyright © 2016. Published by Elsevier Ltd. All rights reserved.

Fatigue behavior of a cross-ply ceramic matrix composite subjected to tension-tension cycling with hold time. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grant, S.A.

This study was carried out to investigate the elevated temperature behavior of the SiC-MAS5 cross- ply (O/9O)4S ceramic matrix composite manufactured by Corning Inc. to fatigue with loading waveforms that combine the characteristics of stress rupture and high cycle fatigue. The test results were compiled in the form of S-N (cycles to failure), S-T (exposure time versus cycles to failure), S-S (energy exposure versus cycles to failure), normalized modulus degradation, strain progression, and hysteresis loop progression. From the mechanical behavior demonstrated by these curves, relationships between the effect of the environment and loading waveform were developed. In addition, a post-mortemmore » SEM analysis of the fracture surface was conducted and the results compared to the mechanical behavior.« less

Test results of a resonant integrated microbeam sensor (RIMS) for acoustic emission monitoring

NASA Astrophysics Data System (ADS)

Schoess, Jeffrey N.; Zook, J. David

1998-07-01

An acoustic emission (AE) sensor has been developed by Honeywell Technology Center for avionics, industrial control, and military applications. The AE sensor design is based on an integrated silicon microstructure, a resonant microbeam with micron-level feature size, and frequency sensitivity up to 500 kHz. The AE sensor has been demonstrated successfully in the laboratory test environment to sense and characterize a simulated AE even for structural fatigue crack monitoring applications. The technical design approach and laboratory test results are presented.

Effects of Acute Fatigue of the Hip Flexor Muscles on Hamstring Muscle Extensibility.

PubMed

Muyor, José M; Arrabal-Campos, Francisco M

2016-12-01

The purpose of the present study was to evaluate the influence of acute fatigue of the hip flexor muscles on scores attained in tests frequently used in literature to measure hamstring muscle extensibility, namely the passive straight leg raise (PSLR), active straight leg raise (ASLR), passive knee extension (PKE), active knee extension (AKE), sit-and-reach (SR) and toe-touch (TT) tests. A total of seventy-five healthy and recreationally active adults voluntarily participated in this study. To reach fatigue, the participants actively lifted their legs alternately as many times as possible. In the passive tests, the results were 7.10 ± 5.21° and 5.68 ± 4.54° higher (p < 0.01) for PSLR and PKE tests, respectively, after acute fatigue. However, in the ASLR test, the results were lower post-fatigue than pre-fatigue (mean difference = -5.30° ± 9.51°; p < 0.01). The AKE, SR and TT tests did not show significant differences between pre- and post-fatigue (p > 0.05). Moderate (r = 0.40) to high (r = 0.97) correlation coefficients were found, which were statistically significant among all the measured flexibility tests both pre- and post-fatigue. In conclusion, the active implication of the hip flexor muscles until reaching fatigue had acute influences on the results of the PSLR, PKE and ASLR tests, but not on the results of the AKE, SR and TT tests. It is recommended to use the AKE test to assess hamstring muscle extensibility in situations where athletes show fatigue in their hip flexor muscles.

Strain energy release rate as a function of temperature and preloading history utilizing the edge delamination fatique test method

NASA Technical Reports Server (NTRS)

Zimmerman, Richard S.; Adams, Donald F.

1989-01-01

Static laminate and tension-tension fatigue tests of IM7/8551-7 composite materials was performed. The Edge Delamination Test (EDT) was utilized to evaluate the temperature and preloading history effect on the critical strain energy release rate. Static and fatigue testing was performed at room temperature and 180 F (82 C). Three preloading schemes were used to precondition fatigue test specimens prior to performing the normal tension-tension fatigue EDT testing. Computer software was written to perform all fatigue testing while monitoring the dynamic modulus to detect the onset of delamination and record the test information for later retrieval and reduction.

14 CFR 29.571 - Fatigue evaluation of structure.

Code of Federal Regulations, 2011 CFR

2011-01-01

... AIRCRAFT AIRWORTHINESS STANDARDS: TRANSPORT CATEGORY ROTORCRAFT Strength Requirements Fatigue Evaluation... fatigue, considering the effects of environment, intrinsic/discrete flaws, or accidental damage will be avoided. Parts to be evaluated include, but are not limited to, rotors, rotor drive systems between the...

14 CFR 29.571 - Fatigue evaluation of structure.

Code of Federal Regulations, 2010 CFR

2010-01-01

... AIRCRAFT AIRWORTHINESS STANDARDS: TRANSPORT CATEGORY ROTORCRAFT Strength Requirements Fatigue Evaluation... fatigue, considering the effects of environment, intrinsic/discrete flaws, or accidental damage will be avoided. Parts to be evaluated include, but are not limited to, rotors, rotor drive systems between the...

Is the Sørensen test valid to assess muscle fatigue of the trunk extensor muscles?

PubMed

Demoulin, Christophe; Boyer, Mathieu; Duchateau, Jacques; Grosdent, Stéphanie; Jidovtseff, Boris; Crielaard, Jean-Michel; Vanderthommen, Marc

2016-01-01

Very few studies have quantified the degree of fatigue characterized by the decline in the maximal voluntary contraction (MVC) force of the trunk extensors induced by the widely used Sørensen test. Measure the degree of fatigue of the trunk extensor muscles induced by the Sørensen test. Eighty young healthy subjects were randomly divided into a control group (CG) and an experimental group (EG), each including 50% of the two genders. The EG performed an isometric MVC of the trunk extensors (pre-fatigue test) followed by the Sørensen test, the latter being immediately followed by another MVC (post-fatigue test). The CG performed only the pre- and post-fatigue tests without any exertion in between. The comparison of the pre- and post-fatigue tests revealed a significant (P< 0.05) decrease in MVC force normalized by body mass (-13%) in the EG, whereas a small increase occurred in the CG (+2.7%, P= 0.001). This study shows that the Sørensen test performed until failure in a young healthy population results in a reduced ability of the trunk extensor muscles to generate maximal force, and indicates that this test is valid for the assessment of fatigue in trunk extensor muscles.

Fatigue in operational settings: Examples from the aviation environment

NASA Technical Reports Server (NTRS)

Rosekind, Mark R.; Gander, Philippa H.; Miller, Donna L.; Gregory, Kevin B.; Smith, Roy M.; Weldon, Keri J.; Co, Elizabeth L.; Mcnally, Karen L.; Lebacqz, J. Victor

1994-01-01

The need for 24-h operations creates nonstandard and altered work schedules that can lead to cumulative sleep loss and circadian disruption. These factors can lead to fatigue and sleepiness and affect performance and productivity on the job. The approach, research, and results of the NASA Ames Fatigue Countermeasures Program are described to illustrate one attempt to address these issues in the aviation environment. The scientific and operational relevance of these factors is discussed, and provocative issues for future research are presented.

Evaluation of Fatigue Life of CRM-Reinforced SMA and Its Relationship to Dynamic Stiffness

PubMed Central

Mashaan, Nuha Salim; Karim, Mohamed Rehan; Abdel Aziz, Mahrez; Ibrahim, Mohd Rasdan; Katman, Herda Yati

2014-01-01

Fatigue cracking is an essential problem of asphalt concrete that contributes to pavement damage. Although stone matrix asphalt (SMA) has significantly provided resistance to rutting failure, its resistance to fatigue failure is yet to be fully addressed. The aim of this study is to evaluate the effect of crumb rubber modifier (CRM) on stiffness and fatigue properties of SMA mixtures at optimum binder content, using four different modification levels, namely, 6%, 8%, 10%, and 12% CRM by weight of the bitumen. The testing undertaken on the asphalt mix comprises the dynamic stiffness (indirect tensile test), dynamic creep (repeated load creep), and fatigue test (indirect tensile fatigue test) at temperature of 25°C. The indirect tensile fatigue test was conducted at three different stress levels (200, 300, and 400 kPa). Experimental results indicate that CRM-reinforced SMA mixtures exhibit significantly higher fatigue life compared to the mixtures without CRM. Further, higher correlation coefficient was obtained between the fatigue life and resilient modulus as compared to permanent strain; thus resilient modulus might be a more reliable indicator in evaluating the fatigue life of asphalt mixture. PMID:25050406

The effect of exercise on the severity of the fatigue in colorectal cancer patients who received chemotherapy in Ahwaz.

PubMed

Shariati, Abdolali; Haghighi, Shayesteh; Fayyazi, Seddigheh; Tabesh, Hamed; Kalboland, Mehrnaz Moradi

2010-01-01

One of the common side effects of cancer is fatigue that affects patients' life quality and leads to disability. Exercise has an important role in improving these patients' life quality and can be used as a complementary treatment. Moreover, there are few studies on the impact of exercise on fatigue among patients with colon cancer. Therefore, the present study investigated the effects of exercise on the severity of fatigue in patients with colorectal cancer who underwent chemotherapy in Ahwaz. In a quasi-experimental study, the adults with colorectal cancer were enrolled. The sample included 36 people. The study environment included adult hematology and chemotherapy wards of Shefa Hospital in Ahwaz. Data were collected using a demographic form and a questionnaire in order to measure the severity of fatigue. Then, the patients had 40 minutes of exercise, 3 times a week for 4 weeks. The effect of exercise versus fatigue intensity was measured at the end of every week. Data were analyzed using SPSS software. The mean of the fatigue severity in the weeks after exercise was significantly different from the week before it. Friedman test showed significant differences between all the weeks before and after the exercise. The mean of the fatigue severity was 3.69 on the week 0 (before the exercise), and decreased to 3.57 on the first week after exercise, 3.46 on the second week, 2.58 on the third week, and 1.69 on the forth week. Considering the results of this study, exercise and work-out can be an effective factor in reducing fatigue in patients.

The effect of exercise on the severity of the fatigue in colorectal cancer patients who received chemotherapy in Ahwaz

PubMed Central

Shariati, Abdolali; Haghighi, Shayesteh; Fayyazi, Seddigheh; Tabesh, Hamed; Kalboland, Mehrnaz Moradi

2010-01-01

BACKGROUND: One of the common side effects of cancer is fatigue that affects patients’ life quality and leads to disability. Exercise has an important role in improving these patients’ life quality and can be used as a complementary treatment. Moreover, there are few studies on the impact of exercise on fatigue among patients with colon cancer. Therefore, the present study investigated the effects of exercise on the severity of fatigue in patients with colorectal cancer who underwent chemotherapy in Ahwaz. METHODS: In a quasi-experimental study, the adults with colorectal cancer were enrolled. The sample included 36 people. The study environment included adult hematology and chemotherapy wards of Shefa Hospital in Ahwaz. Data were collected using a demographic form and a questionnaire in order to measure the severity of fatigue. Then, the patients had 40 minutes of exercise, 3 times a week for 4 weeks. The effect of exercise versus fatigue intensity was measured at the end of every week. Data were analyzed using SPSS software. RESULTS: The mean of the fatigue severity in the weeks after exercise was significantly different from the week before it. Friedman test showed significant differences between all the weeks before and after the exercise. The mean of the fatigue severity was 3.69 on the week 0 (before the exercise), and decreased to 3.57 on the first week after exercise, 3.46 on the second week, 2.58 on the third week, and 1.69 on the forth week. CONCLUSIONS: Considering the results of this study, exercise and work-out can be an effective factor in reducing fatigue in patients. PMID:21589787

Physiological signal analysis for fatigue level of experienced and inexperienced drivers.

PubMed

Li, Rui; Su, Wencheng; Lu, Zhangping

2017-02-17

We studied the changes in driving fatigue levels of experienced and inexperienced drivers at 3 periods of the day: 9:00 a.m.-12:00 p.m., 12:00 p.m.-2:00 p.m., and 4:00 p.m.-6:00 p.m. Thirty drivers were involved in 120-min real-car driving, and sleepiness ratings (Stanford Sleepiness Scale, SSS; Hoddes et al. 1973 ), electroencephalogram (EEG) signals, and heart rates (HRs) were recorded. Together with principal component analysis, the relationship between EEG signals and HR was explored and used to determine a comprehensive indicator of driving fatigue. Then the comprehensive indicator was assessed via paired t test. Experienced and inexperienced drivers behaved significantly differently in terms of subjective fatigue during preliminary trials. At the beginning of trials and after termination, subjective fatigue level was aggravated with prolonged continuous driving. Moreover, we discussed the changing rules of EEG signals and HR and found that with prolonged time, the ratios of δ and β waves significantly declined, whereas that of the θ wave significantly rose. The ratio of (α + θ)/β significantly rose both before trials and after termination, but HR dropped significantly. However, one-factor analysis of variance shows that driving experience significantly affects the θ wave, (α + θ)/β ratio, and HR. We found that in a monotonous road environment, fatigue symptoms occurred in inexperienced drivers and experienced drivers after about 60 and 80 min of continuous driving, respectively. Therefore, as for drivers with different experiences, restriction on continuous driving time would avoid fatigued driving and thereby eliminate traffic accidents. We find that the comprehensive indicator changes significantly with fatigue level. The integration of different indicators improves the recognition accuracy of different driving fatigue levels.

Fatigue Strength and Related Characteristics of Aircraft Joints I : Comparison of Spot-Weld and Rivet Patterns in 24s-t Alclad and 75s-t Alclad

NASA Technical Reports Server (NTRS)

Russell, H W; Jackson, L R; Grover, H J; Beaver, W W

1944-01-01

Report contains detailed results of a number of fatigue tests on spot-welded joints in aluminum alloys. The tests described include: (1) fatigue tests on spot-welded lap joints in sheets of unequal thickness of alclad 24s-t. These tests indicate that the fatigue strength of a spot-welded joint in sheets of two different gages is slightly higher than that of a similar joint in two sheets of the thinner gage but definitely lower than that of a similar joint in two sheets of the thicker gage. (2) Fatigue tests on spot-welded alclad 75s-t spot-welded lap-joint specimens of alclad 75s-t were not any stronger in fatigue than similar specimens of alclad 24s-t. (3) Fatigue tests on lap-joint specimens spot -welded after various surface preparations--these included ac welding wire-brushed surfaces, dc welding wire-brushed surfaces, and dc welding chemically cleaned surfaces. While the ac welds were strongest statically, the dc welds on wire-brushed surfaces were strongest in fatigue. Specimens prepared in this way were very nearly as strong as the best riveted specimens tested for comparison. (4) Fatigue tests on specimens spot-welded with varying voltage so as to include a wide range of static spot-weld strengths. The fatigue strengths were in the same order as the static strengths but showed less range. (author)

Simulation of Fatigue Crack Initiation at Corrosion Pits With EDM Notches

NASA Technical Reports Server (NTRS)

Smith, Stephen W.; Newman, John A.; Piascik, Robert S.

2003-01-01

Uniaxial fatigue tests were conducted to compare the fatigue life of laboratory produced corrosion pits, similar to those observed in the shuttle main landing gear wheel bolt-hole, and an electro-discharged-machined (EDM) flaw. EDM Jaws are used to simulate corrosion pits during shuttle wheel (dynamometer) testing. The aluminum alloy, (AA 7050) laboratory fatigue tests were conducted to simulate the local stress level contained in the wheel bolt-hole. Under this high local stress condition, the EDM notch produced a fatigue life similar to test specimens containing corrosion pits of similar size. Based on the laboratory fatigue test results, the EDM Jaw (semi-circular disc shaped) produces a local stress state similar to corrosion pits and can be used to simulate a corrosion pit during the shuttle wheel dynamometer tests.

Simulation of Fatigue Behavior of High Temperature Metal Matrix Composites

NASA Technical Reports Server (NTRS)

Tong, Mike T.; Singhal, Suren N.; Chamis, Christos C.; Murthy, Pappu L. N.

1996-01-01

A generalized relatively new approach is described for the computational simulation of fatigue behavior of high temperature metal matrix composites (HT-MMCs). This theory is embedded in a specialty-purpose computer code. The effectiveness of the computer code to predict the fatigue behavior of HT-MMCs is demonstrated by applying it to a silicon-fiber/titanium-matrix HT-MMC. Comparative results are shown for mechanical fatigue, thermal fatigue, thermomechanical (in-phase and out-of-phase) fatigue, as well as the effects of oxidizing environments on fatigue life. These results show that the new approach reproduces available experimental data remarkably well.

High temperature, low-cycle fatigue of copper-base alloys for rocket nozzles. Part 2: Strainrange partitioning and low-cycle fatigue results at 538 deg C

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1976-01-01

Low-cycle fatigue tests of 1/2 Hard AMZIRC Copper and NARloy Z were performed in argon at 538 C to determine partitioned strain range versus life relationships. Strain-controlled low-cycle fatigue tests of a Zr-Cr-Mg copper-base alloy were also performed. Strain ranges, lower than those employed in previous tests, were imposed in order to extend the fatigue life curve out to approximately 400,000 cycles. An experimental copper alloy and an experimental silver alloy were also studied. Tensile tests were performed in air at room temperature and in argon at 538 C. Strain-controlled low-cycle fatigue tests were performed at 538 C in argon to define the fatigue life over the regime from 300 to 3,000 cycles. For the silver alloy, three additional heat treatments were introduced, and a limited evaluation of the short-term tensile and low-cycle fatigue behavior at 538 C was performed.

Structural Integrity of Water Reactor Pressure Boundary Components.

DTIC Science & Technology

1981-02-20

environment, and load waveform parameters . A theory of the influence of dissolved oxygen content on the fatigue crack growth results in simulated PWR ...simulated PWR coolant is - (Continues ) DD IJN7 1473 EDITION OF I NOV S ..OSL- -C 2 S/ 0102-LF-014-6601 S1ECURITY CLASSI1FICATION OF THIS PAGE (When...not seem to influence the data, which was produced for a load ratio of 0.2 and a simulated PWR coolant environment. Test results for A106 Grade C piping

Notched fatigue of single crystal PWA 1480 at turbine attachment temperatures

NASA Technical Reports Server (NTRS)

Meyer, T. G.; Nissley, D. M.; Swanson, G. A.

1989-01-01

The focus is on the lower temperature, uncoated and notched features of gas turbine blades. Constitutive and fatigue life prediction models applicable to these regions are being developed. Fatigue results are presented which were obtained thus far. Fatigue tests are being conducted on PWA 1480 single crystal material using smooth strain controlled specimens and three different notched specimens. Isothermal fatigue tests were conducted at 1200, 1400, and 1600 F. The bulk of the tests were conducted at 1200 F. The strain controlled tests were conducted at 0.4 percent per second strain rate and the notched tests were cycled at 1.0 cycle per second. A clear orientation dependence is observed in the smooth strain controlled fatigue results. The fatigue lifes of the thin, mild notched specimens agree fairly well with this smooth data when elastic stress range is used as a correlating parameter. Finite element analyses were used to calculate notch stresses. Fatigue testing will continue to further explore the trends observed thus far. Constitutive and life prediction models are being developed.

Prediction of Mean and Design Fatigue Lives of Self Compacting Concrete Beams in Flexure

NASA Astrophysics Data System (ADS)

Goel, S.; Singh, S. P.; Singh, P.; Kaushik, S. K.

2012-02-01

In this paper, result of an investigation conducted to study the flexural fatigue characteristics of self compacting concrete (SCC) beams in flexure are presented. An experimental programme was planned in which approximately 60 SCC beam specimens of size 100 × 100 × 500 mm were tested under flexural fatigue loading. Approximately 45 static flexural tests were also conducted to facilitate fatigue testing. The flexural fatigue and static flexural strength tests were conducted on a 100 kN servo-controlled actuator. The fatigue life data thus obtained have been used to establish the probability distributions of fatigue life of SCC using two-parameter Weibull distribution. The parameters of the Weibull distribution have been obtained by different methods of analysis. Using the distribution parameters, the mean and design fatigue lives of SCC have been estimated and compared with Normally vibrated concrete (NVC), the data for which have been taken from literature. It has been observed that SCC exhibits higher mean and design fatigue lives compared to NVC.

Interference-Fit-Fastener Investigation

DTIC Science & Technology

1975-09-01

Crack Initiation . .*. . . .* e . . .*. . . .*. 20 Figure 9. Actual and Predicted Fatigue Life Behavior of Notched Open Hole Plates for 2024 - T351 ... Aluminum (Reference 19) * .. . . . . . . . .. . 22 Figure 10. Gage I Strain Response With Cycles . . . . . . . . 24 Figure 11. Fatigue Damage - Life ... Fatigue Behavior", Effect of Environment and Complex Load History on Fatigue Life , ASTM STP 462, pp 74-91 (1970). (7) Grosskreutz, J. C., and Shaw, G. G

Influence of Lumbar Muscle Fatigue on Trunk Adaptations during Sudden External Perturbations

PubMed Central

Abboud, Jacques; Nougarou, François; Lardon, Arnaud; Dugas, Claude; Descarreaux, Martin

2016-01-01

Introduction: When the spine is subjected to perturbations, neuromuscular responses such as reflex muscle contractions contribute to the overall balance control and spinal stabilization mechanisms. These responses are influenced by muscle fatigue, which has been shown to trigger changes in muscle recruitment patterns. Neuromuscular adaptations, e.g., attenuation of reflex activation and/or postural oscillations following repeated unexpected external perturbations, have also been described. However, the characterization of these adaptations still remains unclear. Using high-density electromyography (EMG) may help understand how the nervous system chooses to deal with an unknown perturbation in different physiological and/or mechanical perturbation environments. Aim: To characterize trunk neuromuscular adaptations following repeated sudden external perturbations after a back muscle fatigue task using high-density EMG. Methods: Twenty-five healthy participants experienced a series of 15 sudden external perturbations before and after back muscle fatigue. Erector spinae muscle activity was recorded using high-density EMG. Trunk kinematics during perturbation trials were collected using a 3-D motion analysis system. A two-way repeated measure ANOVA was conducted to assess: (1) the adaptation effect across trials; (2) the fatigue effect; and (3) the interaction effect (fatigue × adaptation) for the baseline activity, the reflex latency, the reflex peak and trunk kinematic variables (flexion angle, velocity and time to peak velocity). Muscle activity spatial distribution before and following the fatigue task was also compared using t-tests for dependent samples. Results: An attenuation of muscle reflex peak was observed across perturbation trials before the fatigue task, but not after. The spatial distribution of muscle activity was significantly higher before the fatigue task compared to post-fatigue trials. Baseline activity showed a trend to higher values after muscle fatigue, as well as reduction through perturbation trials. Main effects of fatigue and adaptation were found for time to peak velocity. No adaptation nor fatigue effect were identified for reflex latency, flexion angle or trunk velocity. Conclusion: The results show that muscle fatigue leads to reduced spatial distribution of back muscle activity and suggest a limited ability to use across-trial redundancy to adapt EMG reflex peak and optimize spinal stabilization using retroactive control. PMID:27895569

Detecting Gear Tooth Fatigue Cracks in Advance of Complete Fracture

NASA Technical Reports Server (NTRS)

Zakrajsek, James J.; Lewicki, David G.

1996-01-01

Results of using vibration-based methods to detect gear tooth fatigue cracks are presented. An experimental test rig was used to fail a number of spur gear specimens through bending fatigue. The gear tooth fatigue crack in each test was initiated through a small notch in the fillet area of a tooth on the gear. The primary purpose of these tests was to verify analytical predictions of fatigue crack propagation direction and rate as a function of gear rim thickness. The vibration signal from a total of three tests was monitored and recorded for gear fault detection research. The damage consisted of complete rim fracture on the two thin rim gears and single tooth fracture on the standard full rim test gear. Vibration-based fault detection methods were applied to the vibration signal both on-line and after the tests were completed. The objectives of this effort were to identify methods capable of detecting the fatigue crack and to determine how far in advance of total failure positive detection was given. Results show that the fault detection methods failed to respond to the fatigue crack prior to complete rim fracture in the thin rim gear tests. In the standard full rim gear test all of the methods responded to the fatigue crack in advance of tooth fracture; however, only three of the methods responded to the fatigue crack in the early stages of crack propagation.

Crew Factors in Flight Operations X: Alertness Management in Flight Operations

NASA Technical Reports Server (NTRS)

Rosekind, Mark R.; Gander, Philippa H.; Connell, Linda J.; Co, Elizabeth L.

1999-01-01

In response to a 1980 congressional request, NASA Ames Research Center initiated a Fatigue/Jet Lag Program to examine fatigue, sleep loss, and circadian disruption in aviation. Research has examined fatigue in a variety of flight environments using a range of measures (from self-report to performance to physiological). In 1991, the program evolved into the Fatigue Countermeasures Program, emphasizing the development and evaluation of strategies to maintain alertness and performance in operational settings. Over the years, the Federal Aviation Administration (FAA) has become a collaborative partner in support of fatigue research and other Program activities. From the inception of the Program, a principal goal was to return the information learned from research and other Program activities to the operational community. The objectives of this Education and Training Module are to explain what has been learned about the physiological mechanisms that underlie fatigue, demonstrate the application of this information in flight operations, and offer some specific fatigue counter-measure recommendations. It is intended for all segments of the aeronautics industry, including pilots, flight attendants, managers, schedulers, safety and policy personnel, maintenance crews, and others involved in an operational environment that challenges human physiological capabilities because of fatigue, sleep loss, and circadian disruption.

Corrosion fatigue of biomedical metallic alloys: mechanisms and mitigation.

PubMed

Antunes, Renato Altobelli; de Oliveira, Mara Cristina Lopes

2012-03-01

Cyclic stresses are often related to the premature mechanical failure of metallic biomaterials. The complex interaction between fatigue and corrosion in the physiological environment has been subject of many investigations. In this context, microstructure, heat treatments, plastic deformation, surface finishing and coatings have decisive influence on the mechanisms of fatigue crack nucleation and growth. Furthermore, wear is frequently present and contributes to the process. However, despite all the effort at elucidating the mechanisms that govern corrosion fatigue of biomedical alloys, failures continue to occur. This work reviews the literature on corrosion-fatigue-related phenomena of Ti alloys, surgical stainless steels, Co-Cr-Mo and Mg alloys. The aim was to discuss the correlation between structural and surface aspects of these materials and the onset of fatigue in the highly saline environment of the human body. By understanding such correlation, mitigation of corrosion fatigue failure may be achieved in a reliable scientific-based manner. Different mitigation methods are also reviewed and discussed throughout the text. It is intended that the information condensed in this article should be a valuable tool in the development of increasingly successful designs against the corrosion fatigue of metallic implants. Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Crew Factors in Flight Operations X: Alertness Management in Flight Operations

NASA Technical Reports Server (NTRS)

Rosekind, Mark R.; Gander, Philippa H.; Connell, Linda J.; Co, Elizabeth L.

2001-01-01

In response to a 1980 congressional request, NASA Ames Research Center initiated a Fatigue/Jet Lag Program to examine fatigue, sleep loss, and circadian disruption in aviation. Research has examined fatigue in a variety of flight environments using a range of measures (from self-report to performance to physiological). In 1991, the program evolved into the Fatigue Countermeasures Program, emphasizing the development and evaluation of strategies to maintain alertness and performance in operational settings. Over the years, the Federal Aviation Administration (FAA) has become a collaborative partner in support of fatigue research and other Program activities. From the inception of the Program, a principal goal was to return the information learned from research and other Program activities to the operational community. The objectives of this Education and Training Module are to explain what has been learned about the physiological mechanisms that underlie fatigue, demonstrate the application of this information in flight operations, and offer some specific fatigue countermeasure recommendations. It is intended for all segments of the aeronautics industry, including pilots, flight attendants, managers, schedulers, safety and policy personnel, maintenance crews, and others involved in an operational environment that challenges human physiological capabilities because of fatigue, sleep loss, and circadian disruption.

Environment enhanced fatigue crack propagation in metals: Inputs to fracture mechanics life prediction models

NASA Technical Reports Server (NTRS)

Gangloff, Richard P.; Kim, Sang-Shik

1993-01-01

This report is a critical review of both environment-enhanced fatigue crack propagation data and the predictive capabilities of crack growth rate models. This information provides the necessary foundation for incorporating environmental effects in NASA FLAGRO and will better enable predictions of aerospace component fatigue lives. The review presents extensive literature data on 'stress corrosion cracking and corrosion fatigue.' The linear elastic fracture mechanics approach, based on stress intensity range (Delta(K)) similitude with microscopic crack propagation threshold and growth rates, provides a basis for these data. Results are presented showing enhanced growth rates for gases (viz., H2 and H2O) and electrolytes (e.g. NaCl and H2O) in aerospace alloys including: C-Mn and heat treated alloy steels, aluminum alloys, nickel-based superalloys, and titanium alloys. Environment causes purely time-dependent accelerated fatigue crack growth above the monotonic load cracking threshold (KIEAC) and promotes cycle-time dependent cracking below (KIEAC). These phenomenon are discussed in terms of hydrogen embrittlement, dissolution, and film rupture crack tip damage mechanisms.

Investigating the effects of maximal anaerobic fatigue on dynamic postural control using the Y-Balance Test.

PubMed

Johnston, William; Dolan, Kara; Reid, Niamh; Coughlan, Garrett F; Caulfield, Brian

2018-01-01

The Y Balance Test is one of the most commonly used dynamic balance assessments, providing an insight into the integration of the sensorimotor subsystems. In recent times, there has been an increase in interest surrounding it's use in various clinical populations demonstrating alterations in motor function. Therefore, it is important to examine the effect physiological influences such as fatigue play in dynamic postural control, and establish a timeframe for its recovery. Descriptive laboratory study. Twenty male and female (age 23.75±4.79years, height 174.12±8.45cm, mass 69.32±8.76kg) partaking in competitive sport, completed the Y Balance Test protocol at 0, 10 and 20min, prior to a modified 60s Wingate fatiguing protocol. Post-fatigue assessments were then completed at 0, 10 and 20 min post-fatiguing intervention. Intraclass correlation coefficients demonstrated excellent intra-session reliability (0.976-0.982) across the three pre-fatigue YBT tests. Post-hoc paired sample t-tests demonstrated that all three reach directions demonstrated statistically significant differences between pre-fatigue and the first post-fatigue measurement (anterior; p=0.019, posteromedial; p=0.019 & posterolateral; p=0.003). The anterior reach direction returned to pre-fatigue levels within 10min (p=0.632). The posteromedial reach direction returned to pre-fatigue levels within 20min (p=0.236), while the posterolateral direction maintained a statistically significant difference at 20min (p=0.023). Maximal anaerobic fatigue has a negative effect on normalised Y balance test scores in all three directions. Following the fatiguing protocol, dynamic postural control returns to pre-fatigue levels for the anterior (<10min), posteromedial (<20min) and posterolateral (>20min). Copyright © 2017 Sports Medicine Australia. Published by Elsevier Ltd. All rights reserved.

Fatigue behavior of ULTIMETRTM alloy: Experiment and theoretical modeling

NASA Astrophysics Data System (ADS)

Jiang, Liang

ULTIMETRTM alloy is a commercial Co-26Cr-9Ni (weight percent) superalloy, which possesses excellent resistance to both wear and corrosion. In order to extend the structural applications of this alloy and improve the fundamental understanding of the fatigue damage mechanisms, stress- and strain-controlled fatigue tests were performed at various temperatures and in different environments. The stress- and strain-life data were developed for the structural design and engineering applications of this material. Fractographic studies characterized the crack-initiation and propagation behavior of the alloy. Microstructure evolution during fatigue was revealed by x-ray diffraction, scanning electron microscopy, and transmission electron microscopy. Specifically, it was found that the metastable face-centered-cubic structure of this alloy in the as-received condition could be transformed into a hexagonal-close-packed structure either under the action of plastic deformation at room temperature, or due to the aging and cyclic deformation at intermediate temperatures. This interesting observation constructed a sound basis for the alloy development. The dominant mechanisms, which control the fatigue behavior of ULTIMET alloy, were characterized. High-speed, high-resolution infrared (IR) thermography, as a non-contact, full-field, and nondestructive technique, was used to characterize the damage during fatigue. The temperature variations during each fatigue cycle, which were due to the thermal-elastic-plastic effect, were observed and related to stress-strain analyses. The temperature evolution during fatigue manifested the cumulative fatigue damage process. A constitutive model was developed to predict thermal and mechanical responses of ULTIMET alloy subjected to cyclic deformation. The predicted cyclic stress-strain responses and temperature variations were found to be in good agreement with the experimental results. In addition, a fatigue life prediction model was developed based on the strain-energy consideration, and the measured temperature could be utilized as an index for fatigue-life prediction.

Study of Near-Threshold Fatigue Crack Propagation in Pipeline Steels in High Pressure Environments

NASA Technical Reports Server (NTRS)

Mitchell, M.

1981-01-01

Near threshold fatigue crack propagation in pipeline steels in high pressure environments was studied. The objective was to determine the level of threshold stress intensity for fatigue crack growth rate behavior in a high strength low alloy X60 pipeline-type steel. Complete results have been generated for gaseous hydrogen at ambient pressure, laboratory air at ambient pressure and approximately 60% relative humidity as well as vacuum of 0.000067 Pa ( 0.0000005 torr) at R-ratios = K(min)/K(max) of 0.1, 0.5, and 0.8. Fatigue crack growth rate behavior in gaseous hydrogen, methane, and methane plus 10 percent hydrogen at 6.89 MPa (100 psi) was determined.

Comments on the origin of acoustic emission in fatigue testing of aluminum alloys

NASA Astrophysics Data System (ADS)

Heiple, C. R.; Carpenter, S. H.; Armentrout, D. L.

The size of acoustic emission (AE) signals expected from inclusion fracture during fatigue testing of 7075 aluminum has been estimated on the basis of previous measurements of AE produced by the fracture of boron particles incorporated into 2219 aluminum. The AF signal size expected from deformation in the plastic zone ahead of the fatigue crack was estimated from the results of tensile tests on 7075 aluminum. The signals predicted from both processes are near or below the noise level in the fatigue experiments and are therefore far too small to account for the signals actually observed. Nearly simultaneous fracture of multiple inclusions could produce signals as large as those observed in fatigue tests of 7075 aluminum, however, fatigue tests of 7050 aluminum produced signals as large or larger than in 7075. Since 7050 has substantially fewer inclusions than 7075, the simultaneous failure of multiple inclusions is unlikely to be a major AE source in fatigue testing of either aluminum alloy. Thus, the most probable source of acoustic emission during fatigue testing of 7075 and 7050 aluminum is the crack advance itself. The measured crack advance per cycle is large enough to release sufficient elastic energy to account for the AE signals observed.

Crack initiation modeling of a directionally-solidified nickel-base superalloy

NASA Astrophysics Data System (ADS)

Gordon, Ali Page

Combustion gas turbine components designed for application in electric power generation equipment are subject to periodic replacement as a result of cracking, damage, and mechanical property degeneration that render them unsafe for continued operation. In view of the significant costs associated with inspecting, servicing, and replacing damaged components, there has been much interest in developing models that not only predict service life, but also estimate the evolved microstructural state of the material. This thesis explains manifestations of microstructural damage mechanisms that facilitate fatigue crack nucleation in a newly-developed directionally-solidified (DS) Ni-base superalloy components exposed to elevated temperatures and high stresses. In this study, models were developed and validated for damage and life prediction using DS GTD-111 as the subject material. This material, proprietary to General Electric Energy, has a chemical composition and grain structure designed to withstand creep damage occurring in the first and second stage blades of gas-powered turbines. The service conditions in these components, which generally exceed 600°C, facilitate the onset of one or more damage mechanisms related to fatigue, creep, or environment. The study was divided into an empirical phase, which consisted of experimentally simulating service conditions in fatigue specimens, and a modeling phase, which entailed numerically simulating the stress-strain response of the material. Experiments have been carried out to simulate a variety of thermal, mechanical, and environmental operating conditions endured by longitudinally (L) and transversely (T) oriented DS GTD-111. Both in-phase and out-of-phase thermo-mechanical fatigue tests were conducted. In some cases, tests in extreme environments/temperatures were needed to isolate one or at most two of the mechanisms causing damage. Microstructural examinations were carried out via SEM and optical microscopy. A continuum crystal plasticity model was used to simulate the material behavior in the L and T orientations. The constitutive model was implemented in ABAQUS and a parameter estimation scheme was developed to obtain the material constants. A physically-based model was developed for correlating crack initiation life based on the experimental life data and predictions are made using the crack initiation model. Assuming a unique relationship between the damage fraction and cycle fraction with respect to cycles to crack initiation for each damage mode, the total crack initiation life has been represented in terms of the individual damage components (fatigue, creep-fatigue, creep, and oxidation-fatigue) observed at the end state of crack initiation.

Development of a remote-controlled fatigue test machine using a laser extensometer for investigation of irradiation effect on fatigue properties

NASA Astrophysics Data System (ADS)

Yonekawa, M.; Ishii, T.; Ohmi, M.; Takada, F.; Hoshiya, T.; Niimi, M.; Ioka, I.; Miwa, Y.; Tsuji, H.

2002-12-01

In order to investigate effects of neutron irradiation on fatigue properties of nuclear materials, a remote-controlled high temperature fatigue test machine was developed at the hot laboratory of the Japan Materials Testing Reactor (JMTR) in the Japan Atomic Energy Research Institute (JAERI). A small-sized fatigue specimen having double blades to measure strain with a laser extensometer was designed for this machine. A strain amplitude in fatigue tests of a completely reversed push-pull type using a triangular wave was controlled with an accuracy of ±3% of the total strain range during test. Low cycle fatigue tests of type 304 stainless steel irradiated in JMTR at 823 K up to a fast neutron fluence of 1×10 25 n/m 2 ( E>1 MeV) were performed in total strain ranges of 0.7-1.4% at 823 K using the designed small-sized specimens.

A fracture mechanics approach for estimating fatigue crack initiation in carbon and low-alloy steels in LWR coolant environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, H. B.; Chopra, O. K.

2000-04-10

A fracture mechanics approach for elastic-plastic materials has been used to evaluate the effects of light water reactor (LWR) coolant environments on the fatigue lives of carbon and low-alloy steels. The fatigue life of such steel, defined as the number of cycles required to form an engineering-size crack, i.e., 3-mm deep, is considered to be composed of the growth of (a) microstructurally small cracks and (b) mechanically small cracks. The growth of the latter was characterized in terms of {Delta}J and crack growth rate (da/dN) data in air and LWR environments; in water, the growth rates from long crack testsmore » had to be decreased to match the rates from fatigue S-N data. The growth of microstructurally small cracks was expressed by a modified Hobson relationship in air and by a slip dissolution/oxidation model in water. The crack length for transition from a microstructurally small crack to a mechanically small crack was based on studies on small crack growth. The estimated fatigue S-N curves show good agreement with the experimental data for these steels in air and water environments. At low strain amplitudes, the predicted lives in water can be significantly lower than the experimental values.« less

14 CFR 25.571 - Damage-tolerance and fatigue evaluation of structure.

Code of Federal Regulations, 2014 CFR

2014-01-01

... contribute to a catastrophic failure (such as wing, empennage, control surfaces and their systems, the... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: TRANSPORT CATEGORY AIRPLANES Structure Fatigue Evaluation § 25... of similar structural design and sonic excitation environment, that— (1) Sonic fatigue cracks are not...

14 CFR 25.571 - Damage-tolerance and fatigue evaluation of structure.

Code of Federal Regulations, 2012 CFR

2012-01-01

... contribute to a catastrophic failure (such as wing, empennage, control surfaces and their systems, the... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: TRANSPORT CATEGORY AIRPLANES Structure Fatigue Evaluation § 25... of similar structural design and sonic excitation environment, that— (1) Sonic fatigue cracks are not...

14 CFR 25.571 - Damage-tolerance and fatigue evaluation of structure.

Code of Federal Regulations, 2013 CFR

2013-01-01

... contribute to a catastrophic failure (such as wing, empennage, control surfaces and their systems, the... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: TRANSPORT CATEGORY AIRPLANES Structure Fatigue Evaluation § 25... of similar structural design and sonic excitation environment, that— (1) Sonic fatigue cracks are not...

75 FR 75882 - Airworthiness Directives; British Aerospace Regional Aircraft Models Jetstream Series 3101 and...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-12-07

... describes the unsafe condition as: As a result of the fatigue-testing programme on the Jetstream fatigue... result of the fatigue-testing programme on the Jetstream fatigue test specimen, it has been identified....S. registry. We also estimate that it will take about 15 work-hours per product to comply with the...

Fatigue Behavior of Steel Fiber Reinforced High-Strength Concrete under Different Stress Levels

NASA Astrophysics Data System (ADS)

Zhang, Chong; Gao, Danying; Gu, Zhiqiang

2017-12-01

The investigation was conducted to study the fatigue behavior of steel fiber reinforced high-strength concrete (SFRHSC) beams. A series of 5 SFRHSC beams was conducted flexural fatigue tests at different stress level S of 0.5, 0.55, 0.6, 0.7 and 0.8 respectively. Static test was conducted to determine the ultimate static capacity prior to fatigue tests. Fatigue modes and S-N curves were analyzed. Besides, two fatige life prediction model were analyzed and compared. It was found that stress level S significantly influenced the fatigue life of SFRHSC beams and the fatigue behavior of SFRHSC beams was mainly determined by the tensile reinforcement.

Tension and fatigue behavior of 316LVM 1x7 multi-strand cables used as implantable electrodes.

PubMed

Lewandowski, John J; Varadarajan, Ravikumar; Smith, Brian; Tuma, Chris; Shazly, Mostafa; Vatamanu, Luciano O

2008-07-15

The mechanical behavior of 316LVM 1x7 cables were evaluated in uniaxial tension, and in cyclic strain-controlled fatigue with the use of a Flex tester operated to provide fully reversed bending fatigue. The magnitude of cyclic strains imparted to each cable tested was controlled via the use of different diameter mandrels. Smaller diameter mandrels produced higher values of cyclic strain and lower fatigue life. Multiple samples were tested and analyzed via scanning electron microscopy. The fatigue results were analyzed via a Coffin-Manson-Basquin approach and compared to fatigue data obtained from the literature where testing was conducted on similar materials, but under rotating bending fatigue conditions.

Fatigue Life Methodology for Bonded Composite Skin/Stringer Configurations

NASA Technical Reports Server (NTRS)

Krueger, Ronald; Paris, Isabelle L.; OBrien, T. Kevin; Minguet, Pierre J.

2001-01-01

A methodology is presented for determining the fatigue life of composite structures based on fatigue characterization data and geometric nonlinear finite element (FE) analyses. To demonstrate the approach, predicted results were compared to fatigue tests performed on specimens which represented a tapered composite flange bonded onto a composite skin. In a first step, tension tests were performed to evaluate the debonding mechanisms between the flange and the skin. In a second step, a 2D FE model was developed to analyze the tests. To predict matrix cracking onset, the relationship between the tension load and the maximum principal stresses transverse to the fiber direction was determined through FE analysis. Transverse tension fatigue life data were used to -enerate an onset fatigue life P-N curve for matrix cracking. The resulting prediction was in good agreement with data from the fatigue tests. In a third step, a fracture mechanics approach based on FE analysis was used to determine the relationship between the tension load and the critical energy release rate. Mixed mode energy release rate fatigue life data were used to create a fatigue life onset G-N curve for delamination. The resulting prediction was in good agreement with data from the fatigue tests. Further, the prediction curve for cumulative life to failure was generated from the previous onset fatigue life curves. The results showed that the methodology offers a significant potential to Predict cumulative fatigue life of composite structures.

Energy-based fatigue model for shape memory alloys including thermomechanical coupling

NASA Astrophysics Data System (ADS)

Zhang, Yahui; Zhu, Jihong; Moumni, Ziad; Van Herpen, Alain; Zhang, Weihong

2016-03-01

This paper is aimed at developing a low cycle fatigue criterion for pseudoelastic shape memory alloys to take into account thermomechanical coupling. To this end, fatigue tests are carried out at different loading rates under strain control at room temperature using NiTi wires. Temperature distribution on the specimen is measured using a high speed thermal camera. Specimens are tested to failure and fatigue lifetimes of specimens are measured. Test results show that the fatigue lifetime is greatly influenced by the loading rate: as the strain rate increases, the fatigue lifetime decreases. Furthermore, it is shown that the fatigue cracks initiate when the stored energy inside the material reaches a critical value. An energy-based fatigue criterion is thus proposed as a function of the irreversible hysteresis energy of the stabilized cycle and the loading rate. Fatigue life is calculated using the proposed model. The experimental and computational results compare well.

14 CFR 25.571 - Damage-tolerance and fatigue evaluation of structure.

Code of Federal Regulations, 2010 CFR

2010-01-01

... contribute to a catastrophic failure (such as wing, empennage, control surfaces and their systems, the... TRANSPORTATION AIRCRAFT AIRWORTHINESS STANDARDS: TRANSPORT CATEGORY AIRPLANES Structure Fatigue Evaluation § 25... and sonic excitation environment, that— (1) Sonic fatigue cracks are not probable in any part of the...

Investigation of Gear and Bearing Fatigue Damage Using Debris Particle Distributions

NASA Technical Reports Server (NTRS)

Dempsey, Paula J.; Lewicki, David G.; Decker, Harry J.

2004-01-01

A diagnostic tool was developed for detecting fatigue damage to spur gears, spiral bevel gears, and rolling element bearings. This diagnostic tool was developed and evaluated experimentally by collecting oil debris data from fatigue tests performed in the NASA Glenn Spur Gear Fatigue Rig, Spiral Bevel Gear Test Facility, and the 500hp Helicopter Transmission Test Stand. During each test, data from an online, in-line, inductance type oil debris sensor was monitored and recorded for the occurrence of pitting damage. Results indicate oil debris alone cannot discriminate between bearing and gear fatigue damage.

Influence of sustained submaximal clenching fatigue test on electromyographic activity and maximum voluntary bite forces in healthy subjects and patients with temporomandibular disorders.

PubMed

Xu, L; Fan, S; Cai, B; Fang, Z; Jiang, X

2017-05-01

This study aimed to investigate whether the fatigue induced by sustained motor task in the jaw elevator muscles differed between healthy subjects and patients with temporomandibular disorder (TMD). Fifteen patients with TMD and thirteen age- and sex-matched healthy controls performed a fatigue test consisting of sustained clenching contractions at 30% maximal voluntary clenching intensity until test failure (the criterion for terminating the fatigue test was when the biting force decreased by 10% or more from the target force consecutively for >3 s). The pre- and post-maximal bite forces (MBFs) were measured. Surface electromyographic signals were recorded from the superficial masseter muscles and anterior temporal muscles bilaterally, and the median frequency at the beginning, middle and end of the fatigue test was calculated. The duration of the fatigue test was also quantified. Both pre- and post-MBFs were lower in patients with TMD than in controls (P < 0·01). No significant difference was found in the percentage change in MBF between groups. The duration of the fatigue test in TMD patients was significantly shorter than that of the controls (P < 0·05). Our results suggest that, compared to healthy subjects, patients with TMD become more easily fatigued, but the electromyographic activation process during the fatigue test is similar between healthy subjects and patients with TMD. However, the mechanisms involved in this process remain unclear, and further research is warranted. © 2017 John Wiley & Sons Ltd.

Corrosion Susceptibility of AA5083-H116 in Biologically Active Atmospheric Marine Environments

DTIC Science & Technology

2014-03-01

by the standardized nitric acid test ASTM G67." Fatigue and stress corrosion cracking behaviors of sensitized AA5083 have also been evaluated.1213... acid (NAMLT Test)," ASTM Hanbook 3.02 Corrosion of Metals; Wear and Erosion. ASTM Hanbook 3.02 Corrosion of Metals; Wear and Erosion (ASTM...DATE (DD-MM-YYYY) 12-05-2014 REPORT TYPE Conference Proceeding (refereed) 3. DATES COVERED (From - To) 4. TITLE AND SUBTITLE Corrosion

Compilation of Abstracts of Theses Submitted by Candidates for Degrees.

DTIC Science & Technology

1982-05-01

which either ti- tanium or aluminum tubes are used in the heat exchanges . Master of Science in Advisor: R. H. Nunn Mechanical Engineering Department... Testing in an Inert Environment Holihan, R. G., Jr. Investigation of Heat Transfer in 208 LCDR, USN Straight and Curved Rectangular Ducts for Laminar...for c-ft materials fatigue testing . The system uses an HP-9835 Desktop . .tnr, an HP-2240A Measurement and Control Processor and a Materials P System

Detection of mycotoxins in patients with chronic fatigue syndrome.

PubMed

Brewer, Joseph H; Thrasher, Jack D; Straus, David C; Madison, Roberta A; Hooper, Dennis

2013-04-11

Over the past 20 years, exposure to mycotoxin producing mold has been recognized as a significant health risk. Scientific literature has demonstrated mycotoxins as possible causes of human disease in water-damaged buildings (WDB). This study was conducted to determine if selected mycotoxins could be identified in human urine from patients suffering from chronic fatigue syndrome (CFS). Patients (n = 112) with a prior diagnosis of CFS were evaluated for mold exposure and the presence of mycotoxins in their urine. Urine was tested for aflatoxins (AT), ochratoxin A (OTA) and macrocyclic trichothecenes (MT) using Enzyme Linked Immunosorbent Assays (ELISA). Urine specimens from 104 of 112 patients (93%) were positive for at least one mycotoxin (one in the equivocal range). Almost 30% of the cases had more than one mycotoxin present. OTA was the most prevalent mycotoxin detected (83%) with MT as the next most common (44%). Exposure histories indicated current and/or past exposure to WDB in over 90% of cases. Environmental testing was performed in the WDB from a subset of these patients. This testing revealed the presence of potentially mycotoxin producing mold species and mycotoxins in the environment of the WDB. Prior testing in a healthy control population with no history of exposure to a WDB or moldy environment (n = 55) by the same laboratory, utilizing the same methods, revealed no positive cases at the limits of detection.

Detection of Mycotoxins in Patients with Chronic Fatigue Syndrome

PubMed Central

Brewer, Joseph H.; Thrasher, Jack D.; Straus, David C.; Madison, Roberta A.; Hooper, Dennis

2013-01-01

Over the past 20 years, exposure to mycotoxin producing mold has been recognized as a significant health risk. Scientific literature has demonstrated mycotoxins as possible causes of human disease in water-damaged buildings (WDB). This study was conducted to determine if selected mycotoxins could be identified in human urine from patients suffering from chronic fatigue syndrome (CFS). Patients (n = 112) with a prior diagnosis of CFS were evaluated for mold exposure and the presence of mycotoxins in their urine. Urine was tested for aflatoxins (AT), ochratoxin A (OTA) and macrocyclic trichothecenes (MT) using Enzyme Linked Immunosorbent Assays (ELISA). Urine specimens from 104 of 112 patients (93%) were positive for at least one mycotoxin (one in the equivocal range). Almost 30% of the cases had more than one mycotoxin present. OTA was the most prevalent mycotoxin detected (83%) with MT as the next most common (44%). Exposure histories indicated current and/or past exposure to WDB in over 90% of cases. Environmental testing was performed in the WDB from a subset of these patients. This testing revealed the presence of potentially mycotoxin producing mold species and mycotoxins in the environment of the WDB. Prior testing in a healthy control population with no history of exposure to a WDB or moldy environment (n = 55) by the same laboratory, utilizing the same methods, revealed no positive cases at the limits of detection. PMID:23580077

Thermal-Mechanical Fatigue Testing of a Titanium-Aluminide Alloy.

DTIC Science & Technology

1987-12-01

DIMSTRIBUTION STA Approved for pubi robing e% dQ *- AFIT/GAB/AA/87D-18 THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS John J...THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS Presented to the Faculty of the School of Engineering of the Air Force Institute...develop a Thermal-Mechanical Fatigue (TMF) testing system for titanium - aluminide compact tension specimens. I could not have accomplished this without the

Single-leg hop testing following fatiguing exercise: reliability and biomechanical analysis.

PubMed

Augustsson, J; Thomeé, R; Lindén, C; Folkesson, M; Tranberg, R; Karlsson, J

2006-04-01

A fatiguing exercise protocol was combined with single-leg hop testing to improve the possibilities of evaluating the effects of training or rehabilitation interventions. In the first test-retest experiment, 11 healthy male subjects performed two trials of single-leg hops under three different test conditions: non-fatigued and following fatiguing exercise, which consisted of unilateral weight machine knee extensions at 80% and 50%, respectively, of 1 repetition maximum (1 RM) strength. Intraclass correlation coefficients ranged from 0.75 to 0.98 for different hop test conditions, indicating that all tests were reliable. For the second experiment, eight healthy male subjects performed the fatiguing exercise protocol to investigate how fatigue influences lower-extremity joint kinematics and kinetics during single-leg hops. Hip, knee and ankle joint angles, moments and powers, as well as ground-reaction forces were recorded with a six-camera, motion-capture system and a force platform. Recovery of hop performance following the fatiguing exercise was also measured. During the take-off for the single-leg hops, hip and knee flexion angles, generated powers for the knee and ankle joints, and ground-reaction forces decreased for the fatigued hop conditions compared with the non-fatigued condition (P<0.05). Compared with landing during the non-fatigued condition, hip moments and ground-reaction forces were lower for the fatigued hop conditions (P<0.05). The negative joint power was two to three times greater for the knee than for the hip and five to 10 times greater for the knee than for the ankle during landing for all test conditions (P<0.05). Most measured variables had recovered three minutes post-exercise. It is concluded that the fatiguing exercise protocol combined with single-leg hop testing was a reliable method for investigating functional performance under fatigued test conditions. Further, subjects utilized an adapted hop strategy, which employed less hip and knee flexion and generated powers for the knee and ankle joints during take-off, and less hip joint moments during landing under fatigued conditions. The large negative power values observed at the knee joint during the landing phase of the single-leg hop, during which the quadriceps muscle activates eccentrically, indicate that not only hop distance but also the ability to perform successful landings should be investigated when assessing dynamic knee function.

Experimental Investigation and Finite Element Analysis on Fatigue Behavior of Aluminum Alloy 7050 Single-Lap Joints

NASA Astrophysics Data System (ADS)

Zhou, Bing; Cui, Hao; Liu, Haibo; Li, Yang; Liu, Gaofeng; Li, Shujun; Zhang, Shangzhou

2018-03-01

The fatigue behavior of single-lap four-riveted aluminum alloy 7050 joints was investigated by using high-frequency fatigue test and scanning electron microscope (SEM). Stress distributions obtained by finite element (FE) analysis help explain the fatigue performance. The fatigue test results showed that the fatigue lives of the joints depend on cold expansion and applied cyclic loads. FE analysis and fractography indicated that the improved fatigue lives can be attributed to the reduction in maximum stress and evolution of fatigue damage at the critical location. The beneficial effects of strengthening techniques result in tearing ridges or lamellar structure on fracture surface, decrease in fatigue striations spacing, delay of fatigue crack initiation, crack deflection in fatigue crack propagation and plasticity-induced crack closure.

Fatigue of Chinese railway employees and its influential factors: Structural equation modelling.

PubMed

Tsao, Liuxing; Chang, Jing; Ma, Liang

2017-07-01

Fatigue is an identifiable and preventable cause of accidents in transport operations. Regarding the railway sector, incident logs and simulation studies show that employee fatigue leads to lack of alertness, impaired performance, and occurrence of incidents. China has one of the largest rail systems in the world, and Chinese railway employees work under high fatigue risks; therefore, it is important to assess their fatigue level and find the major factors leading to fatigue. We designed a questionnaire that uses Multidimensional Fatigue Instrument (MFI-20), NASA-TLX and subjective rating of work overtime feelings to assess employee fatigue. The contribution of each influential factor of fatigue was analysed using structural equation modelling. In total, 297 employees from the rail maintenance department and 227 employees from the locomotive department returned valid responses. The average scores and standard deviations for the five subscales of MFI-20, namely General Fatigue, Physical Fatigue, Reduced Activity, Reduced Motivation, and Mental Fatigue, were 2.9 (0.8), 2.8 (0.8), 2.5 (0.8), 2.5 (0.7), and 2.4 (0.8) among the rail maintenance employees and 3.5 (0.8), 3.5 (0.7), 3.3 (0.7), 3.0 (0.6), and 3.1 (0.7), respectively, among the locomotive employees. The fatigue of the locomotive employees was influenced by feelings related to working overtime (standardized r = 0.22) and workload (standardized r = 0.27). The work overtime control and physical working environment significantly influenced subjective feelings (standardized r = -0.25 and 0.47, respectively), while improper work/rest rhythms and an adverse physical working environment significantly increased the workload (standardized r = 0.48 and 0.33, respectively). Copyright © 2017 Elsevier Ltd. All rights reserved.

Fatigue Lives Of Laser-Cut Metals

NASA Technical Reports Server (NTRS)

Martin, Michael R.

1988-01-01

Fatigue lives made to approach those attainable by traditional grinding methods. Fatigue-test specimens prepared from four metallic alloys, and material removed from specimens by manual grinding, by Nd:glass laser, and by Nd:YAG laser. Results of fatigue tests of all specimens indicated reduction of fatigue strengths of laser-fired specimens. Laser machining holds promise for improved balancing of components of gas turbines.

Cyclic crack growth behavior of reactor pressure vessel steels in light water reactor environments

DOE Office of Scientific and Technical Information (OSTI.GOV)

Van Der Sluys, W.A.; Emanuelson, R.H.

1986-01-01

During normal operation light water reactor (LWR) pressure vessels are subjected to a variety of transients resulting in time varying stresses. Consequently, fatigue and environmentally assisted fatigue are growth mechanisms relevant to flaws in these pressure vessels. In order to provide a better understanding of the resistance of nuclear pressure vessel steels to flaw growth process, a series of fracture mechanics experiments were conducted to generate data on the rate of cyclic crack growth in SA508-2 and SA533b-1 steels in simulated 550/sup 0/F boiling water reactor (BWR) and 550/sup 0/F pressurized water reactor (PWR) environments. Areas investigated over the coursemore » of the test program included the effects of loading frequency and r ratio (Kmin-Kmax) on crack growth rate as a function of the stress intensity factor (deltaK) range. In addition, the effect of sulfur content of the test material on the cyclic crack growth rate was studied. Cyclic crack growth rates were found to be controlled by deltaK, R ratio, and loading frequency. The sulfur impurity content of the reactor pressure vessel steels studied had a significant effect on the cyclic crack growth rates. The higher growth rates were always associated with materials of higher sulfur content. For a given level of sulfur, growth rates were in a 550/sup 0/F simulated BWR environment than in a 550/sup 0/F simulated PWR environment. In both environments cyclic crack growth rates were a strong function of the loading frequency.« less

The Effect of Ultrasonic Peening on Service Life of the Butt-Welded High-Temperature Steel Pipes

NASA Astrophysics Data System (ADS)

Daavari, Morteza; Vanini, Seyed Ali Sadough

2015-09-01

Residual stresses introduced by manufacturing processes such as casting, forming, machining, and welding have harmful effects on the mechanical behavior of the structures. In addition to the residual stresses, weld toe stress concentration can play a determining effect. There are several methods to improve the mechanical properties such as fatigue behavior of the welded structures. In this paper, the effects of ultrasonic peening on the fatigue life of the high-temperature seamless steel pipes, used in the petrochemical environment, have been investigated. These welded pipes are fatigued due to thermal and mechanical loads caused by the cycle of cooling, heating, and internal pressure fluctuations. Residual stress measurements, weld geometry estimation, electrochemical evaluations, and metallography investigations were done as supplementary examinations. Results showed that application of ultrasonic impact treatment has led to increased fatigue life, fatigue strength, and corrosion resistance of A106-B welded steel pipes in petrochemical corrosive environment.

Initiation and growth of multiple-site damage in the riveted lap joint of a curved stiffened fuselage panel: An experimental and analytical study

NASA Astrophysics Data System (ADS)

Ahmed, Abubaker Ali

As part of the structural integrity research of the National Aging Aircraft Research Program, a comprehensive study on multiple-site damage (MSD) initiation and growth in a pristine lap-joint fuselage panel has been conducted. The curved stiffened fuselage panel was tested at the Full-Scale Aircraft Structural Test Evaluation and Research (FASTER) facility located at the Federal Aviation Administration William J. Hughes Technical Center. A strain survey test was conducted to verify proper load application. The panel was then subjected to a fatigue test with constant-amplitude cyclic loading. The applied loading spectrum included underload marker cycles so that crack growth history could be reconstructed from post-test fractographic examinations. Crack formation and growth were monitored via nondestructive and high-magnification visual inspections. Strain gage measurements recorded during the strain survey tests indicated that the inner surface of the skin along the upper rivet row of the lap joint experienced high tensile stresses due to local bending. During the fatigue loading, cracks were detected by eddy-current inspections at multiple rivet holes along the upper rivet row. Through-thickness cracks were detected visually after about 80% of the fatigue life. Once MSD cracks from two adjacent rivet holes linked up, there was a quick deterioration in the structural integrity of the lap joint. The linkup resulted in a 2.87" (72.9-mm) lead fatigue crack that rapidly propagated across 12 rivet holes and crossed over into the next skin bay, at which stage the fatigue test was terminated. A post-fatigue residual strength test was then conducted by loading the panel quasi-statically up to final failure. The panel failed catastrophically when the crack extended instantaneously across three additional bays. Post-test fractographic examinations of the fracture surfaces in the lap joint of the fuselage panel were conducted to characterize subsurface crack initiation and growth. Results showed evidence of fretting damage and crack initiation at multiple locations near the rivet holes along the faying surface of the skin. The subsurface cracks grew significantly along the faying surface before reaching the outer surface of the skin, forming elliptical crack fronts. A finite element model (FE) of the panel was constructed and geometrically-nonlinear analyses conducted to determine strain distribution under the applied loads. The FE model was validated by comparing the analysis results with the strain gage measurements recorded during the strain survey test. The validated FE model was then used to determine stress-intensity factors at the crack tips. Stress-intensity factor results indicated that crack growth in the lap joint was under mixed-mode; however, the opening-mode stress intensity factor was dominant. The stress-intensity factors computed from the FE analysis were used to conduct cycle-by-cycle integration of fatigue crack growth. In the cycle-by-cycle integration, the NASGRO crack growth model was used with its parameters selected to account for the effects of plasticity-induced crack closure and the test environment on crack growth rate. Fatigue crack growth predictions from cycle-by-cycle computation were in good agreement with the experimental measured crack growth data. The results of the study provide key insights into the natural development and growth of MSD cracks in the pristine lap joint. The data provided by the study represent a valuable source for the evaluation and validation of analytical methodologies used for predicting MSD crack initiation and growth.

Cumulative Axial and Torsional Fatigue: An Investigation of Load-Type Sequencing Effects

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Bonacuse, Peter J.

2000-01-01

Cumulative fatigue behavior of a wrought cobalt-base superalloy, Haynes 188 was investigated at 538 C under various single-step sequences of axial and torsional loading conditions. Initially, fully-reversed, axial and torsional fatigue tests were conducted under strain control at 538 C on thin-walled tubular specimens to establish baseline fatigue life relationships. Subsequently, four sequences (axial/axial, torsional/torsional, axial/torsional, and torsional/axial) of two load-level fatigue tests were conducted to characterize both the load-order (high/low) and load-type sequencing effects. For the two load-level tests, summations of life fractions and the remaining fatigue lives at the second load-level were computed by the Miner's Linear Damage Rule (LDR) and a nonlinear Damage Curve Approach (DCA). In general, for all four cases predictions by LDR were unconservative. Predictions by the DCA were within a factor of two of the experimentally observed fatigue lives for a majority of the cumulative axial and torsional fatigue tests.

Rolling-element fatigue life of AMS 5749 corrosion resistant, high temperature bearing steel

NASA Technical Reports Server (NTRS)

Parker, R. J.; Hodder, R. S.

1977-01-01

The rolling element fatigue lives of AMS 5749 and AISI M-50 were compared in tests run in the five ball fatigue tester and the rolling contact fatigue tester. The effects of double vacuum melting and retained austenite on the life of AMS 5749 were determined in five ball fatigue tests. The double vacuum melting process consisted of induction vacuum melting followed by vacuum arc remelting (VIM-VAR). In the five ball tests, VIM-VAR AMS 5749 gave lives at least six times that of VIM-VAR AISI M-50. Similar tests in the rolling contact fatigue tester showed no significant difference in the lives of the two materials. The rolling element fatigue life of VIM-VAR AMS 5749 was at least 14 times that of vacuum induction melted AMS 5749. A trend toward increased rolling element fatigue life with decreased retained austenite is apparent, but the confidence that all experimental differences are significant is not great.

Automation software for a materials testing laboratory

NASA Technical Reports Server (NTRS)

Mcgaw, Michael A.; Bonacuse, Peter J.

1990-01-01

The software environment in use at the NASA-Lewis Research Center's High Temperature Fatigue and Structures Laboratory is reviewed. This software environment is aimed at supporting the tasks involved in performing materials behavior research. The features and capabilities of the approach to specifying a materials test include static and dynamic control mode switching, enabling multimode test control; dynamic alteration of the control waveform based upon events occurring in the response variables; precise control over the nature of both command waveform generation and data acquisition; and the nesting of waveform/data acquisition strategies so that material history dependencies may be explored. To eliminate repetitive tasks in the coventional research process, a communications network software system is established which provides file interchange and remote console capabilities.

Fatigue and physical fitness of mildly disabled persons with multiple sclerosis: a cross-sectional study.

PubMed

Valet, Maxime; Lejeune, Thierry; Glibert, Yumiko; Hakizimana, Jean C; Van Pesch, Vincent; El Sankari, Souraya; Detrembleur, Christine; Stoquart, Gaëtan

2017-09-01

Fatigue is frequent and disabling in persons with multiple sclerosis (pwMS) with mild neurological disability. These patients also have impaired physical fitness. Whether mildly disabled pwMS are deconditioned, and this deconditioning is linked to fatigue, remains unknown. Our aim is to determine the physical fitness of mildly disabled patients with multiple sclerosis and study its relationship with perceived fatigue and to link perceived fatigue with other parameters. Twenty patients (14 women; mean age: 45.5 years) with mild disability (Expanded Disability Status Scale 0-4) underwent a 2-min walking test, Timed Up-and-Go test, aerobic capacity testing, and isometric knee extension testing to assess strength and neuromuscular fatigability. They completed questionnaires assessing perceived fatigue, psychological status, and physical activity. Correlation coefficients and multivariate regression were used to analyze the relationships among variables. Seventeen (85%) patients reported a high level of fatigue. Thirteen (65%) patients had subnormal aerobic capacity. Fatigue was weakly to moderately associated with aerobic capacity, mobility, walking capacity, depression, and neuromuscular fatigability. An association of disease duration, aerobic capacity, and the neuromuscular fatigability index explained 65.1% of fatigue. A high proportion of pwMS with mild neurological disability are fatigued and deconditioned. Perceived fatigue is linked to aerobic capacity, neuromuscular fatigability, depression, mobility, and walking capacity. Focusing on these parameters could help in the management of fatigue.

Probabilistic Flexural Fatigue in Plain and Fiber-Reinforced Concrete

PubMed Central

Ríos, José D.

2017-01-01

The objective of this work is two-fold. First, we attempt to fit the experimental data on the flexural fatigue of plain and fiber-reinforced concrete with a probabilistic model (Saucedo, Yu, Medeiros, Zhang and Ruiz, Int. J. Fatigue, 2013, 48, 308–318). This model was validated for compressive fatigue at various loading frequencies, but not for flexural fatigue. Since the model is probabilistic, it is not necessarily related to the specific mechanism of fatigue damage, but rather generically explains the fatigue distribution in concrete (plain or reinforced with fibers) for damage under compression, tension or flexion. In this work, more than 100 series of flexural fatigue tests in the literature are fit with excellent results. Since the distribution of monotonic tests was not available in the majority of cases, a two-step procedure is established to estimate the model parameters based solely on fatigue tests. The coefficient of regression was more than 0.90 except for particular cases where not all tests were strictly performed under the same loading conditions, which confirms the applicability of the model to flexural fatigue data analysis. Moreover, the model parameters are closely related to fatigue performance, which demonstrates the predictive capacity of the model. For instance, the scale parameter is related to flexural strength, which improves with the addition of fibers. Similarly, fiber increases the scattering of fatigue life, which is reflected by the decreasing shape parameter. PMID:28773123

Probabilistic Flexural Fatigue in Plain and Fiber-Reinforced Concrete.

PubMed

Ríos, José D; Cifuentes, Héctor; Yu, Rena C; Ruiz, Gonzalo

2017-07-07

The objective of this work is two-fold. First, we attempt to fit the experimental data on the flexural fatigue of plain and fiber-reinforced concrete with a probabilistic model (Saucedo, Yu, Medeiros, Zhang and Ruiz, Int. J. Fatigue, 2013, 48, 308-318). This model was validated for compressive fatigue at various loading frequencies, but not for flexural fatigue. Since the model is probabilistic, it is not necessarily related to the specific mechanism of fatigue damage, but rather generically explains the fatigue distribution in concrete (plain or reinforced with fibers) for damage under compression, tension or flexion. In this work, more than 100 series of flexural fatigue tests in the literature are fit with excellent results. Since the distribution of monotonic tests was not available in the majority of cases, a two-step procedure is established to estimate the model parameters based solely on fatigue tests. The coefficient of regression was more than 0.90 except for particular cases where not all tests were strictly performed under the same loading conditions, which confirms the applicability of the model to flexural fatigue data analysis. Moreover, the model parameters are closely related to fatigue performance, which demonstrates the predictive capacity of the model. For instance, the scale parameter is related to flexural strength, which improves with the addition of fibers. Similarly, fiber increases the scattering of fatigue life, which is reflected by the decreasing shape parameter.

Assessment of corrosion fatigue damage by acoustic emission and periodic proof tests

NASA Astrophysics Data System (ADS)

Mehdizadeh, P.

1976-03-01

The development of a better nondestructive inspection method for detecting corrosion fatigue damage based on acoustic emission (AE) and periodic proof testing (PPT) is studied for corrosion fatigue tests in salt water solution under tension-tension loading. It is shown that PPT combined with AE monitoring can be a sensitive method for assessing the progress of corrosion fatigue damage as the continuous AE monitoring method. The AE-PPT technique is shown to be dependent on the geometry and size of the crack relative to the test specimen. A qualitative method based on plateauing of acoustic emission counts during proof tests due to changes in the fracture mode is used to predict the remaining fatigue life up to 70% of the actual values. PPT is shown to have no adverse effect on fatigue performance in salt water.

Conducting High Cycle Fatigue Strength Step Tests on Gamma TiAl

NASA Technical Reports Server (NTRS)

Lerch, Brad; Draper, Sue; Pereira, J. Mike

2002-01-01

High cycle fatigue strength testing of gamma TiAl by the step test method is investigated. A design of experiments was implemented to determine if the coaxing effect occurred during testing. Since coaxing was not observed, step testing was deemed a suitable method to define the fatigue strength at 106 cycles.

Oxygen uptake during peak graded exercise and single-stage fatigue tests of wheelchair propulsion in manual wheelchair users and the able-bodied.

PubMed

Keyser, R E; Rodgers, M M; Gardner, E R; Russell, P J

1999-10-01

To determine if a single-stage, submaximal fatigue test on a wheelchair ergometer would result in higher than expected energy expenditure. An experimental survey design contrasting physiologic responses during peak graded exercise tests and fatigue tests. A rehabilitation science laboratory that included a prototypical wheelchair ergometer, open-circuit spirometry system, and heart rate monitor. Nine able-bodied non-wheelchair users (the NWC group: 6 men and 3 women, mean +/- SD age 30 +/- 7yrs) and 15 manual wheelchair users (the WC group: 12 men and 3 women, age 40 +/- 9yrs, time in wheelchair 16 +/- 9yrs). No subject had any disease, medication regimen, or upper body neurologic, orthopedic, or other condition that would limit wheelchair exercise. Peak oxygen uptake (VO2) for graded exercise testing and during fatigue testing, using a power output corresponding to 75% peak aerobic capacity on graded exercise test. In the WC group, VO2 at 6 minutes of fatigue testing was not significantly different from peak VO2. In the NWC group, VO2 was similar to the expected level throughout fatigue testing. Energy expenditure was higher than expected in the WC group but not in the NWC group. Fatigue testing may provide a useful evaluation of cardiorespiratory status in manual wheelchair users.

Fatigue impact on Mod-1 wind turbine design

NASA Technical Reports Server (NTRS)

Stahle, C. V., Jr.

1978-01-01

Fatigue is a key consideration in the design of a long-life Wind Turbine Generator (WTG) system. This paper discusses the fatigue aspects of the large Mod-1 horizontal-axis WTG design starting with the characterization of the environment and proceeding through the design. Major sources of fatigue loading are discussed and methods of limiting fatigue loading are described. NASTRAN finite element models are used to determine dynamic loading and internal cyclic stresses. Recent developments in determining the allowable fatigue stress consistent with present construction codes are discussed relative to their application to WTG structural design.

Repeatability of testing procedures for resilient modulus and fatigue : appendices.

DOT National Transportation Integrated Search

1989-04-01

The article is the appendices of "Repeatability of testing procedures for resilient modulus and fatigue". : Extensive use of diametral resilient modulus and fatigue testing is made by the Oregon State Highway Division to evaluate asphaltic concrete m...

Three-dimensional measurements of fatigue crack closure

NASA Technical Reports Server (NTRS)

Ray, S. K.; Grandt, A. F., Jr.

1984-01-01

Fatigue crack growth and retardation experiments conducted in polycarbonate test specimen are described. The transparent test material allows optical interferometry measurements of the fatigue crack opening (and closing) profiles. Crack surface displacements are obtained through the specimen thickness and three dimensional aspects of fatigue crack closure are discussed.

The assessment and analysis of astronaut mental fatigue in long-duration spaceflight

NASA Astrophysics Data System (ADS)

Li, Yun; Zhou, Qianxiang; Zu, Xiaoqi

2012-07-01

In the field of aerospace, mental work has become the main form of most operations, and the other operations are mixed works which are mental work dominated. Confined spaces, silent space environment, specified mode of communication, limited contract with the ground and discomfort of weightlessness also can lead to the aggravation and acceleration of mental fatigue. In aerospace activities, due to the instantaneous distraction of operator, slow response or lack of coordination could lead to serious accident, the study of mental fatigue is particularly important. In order to study the impact of continuous mental task and rest, we conducted an experiment which combined subjective evaluation with physiology index evaluation. Five subjects were selected in the experiment, and they were asked to perform continuous operation task in a simulator to imitate astronaut schedule. In the course of the experiment, subjective fatigue score (used Samn-Perelli and SWAT) and EEG power spectra were measured at the following hours: 8:00(starting time), 11:30, 15:00, 19:00, 23:00(before sleep), 6:00(after sleep), and 8:00(end time). The experiment showed that a short rest is not enough to make the subjects restored to the original state. The reduction of high frequency components and increase of low frequency in EEG also became more obvious with the increased mental fatigue. Gravity frequency of EEG had a shift to low frequency and is strongly correlated with mental fatigue level. These phenomena were similar with the results of subjective test. The SWAT also could tell us the main causes of metal fatigue during this process.

Creep Behavior of Hafnia and Ytterbium Silicate Environmental Barrier Coating Systems on SiC/SiC Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Fox, Dennis S.; Ghosn, Louis J.; Harder, Bryan

2011-01-01

Environmental barrier coatings will play a crucial role in future advanced gas turbine engines because of their ability to significantly extend the temperature capability and stability of SiC/SiC ceramic matrix composite (CMC) engine components, thus improving the engine performance. In order to develop high performance, robust coating systems for engine components, appropriate test approaches simulating operating temperature gradient and stress environments for evaluating the critical coating properties must be established. In this paper, thermal gradient mechanical testing approaches for evaluating creep and fatigue behavior of environmental barrier coated SiC/SiC CMC systems will be described. The creep and fatigue behavior of Hafnia and ytterbium silicate environmental barrier coatings on SiC/SiC CMC systems will be reported in simulated environmental exposure conditions. The coating failure mechanisms will also be discussed under the heat flux and stress conditions.

Development Status and Performance Comparisons of Environmental Barrier Coating Systems for SiCSiC Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Harder, Bryan

2016-01-01

Environmental barrier coatings (EBC) and SiCSiC ceramic matrix composites (CMCs) will play a crucial role in future aircraft turbine engine systems, because of their ability to significantly increase engine operating temperatures, reduce engine weight and cooling requirements. This paper presents current NASA EBC-CMC development emphases including: the coating composition and processing improvements, laser high heat flux-thermal gradient thermo-mechanical fatigue - environmental testing methodology development, and property evaluations for next generation EBC-CMC systems. EBCs processed with various deposition techniques including Plasma Spray, Electron Beam - Physical Vapor Deposition, and Plasma Spray Physical Vapor Deposition (PS-PVD) will be particularly discussed. The testing results and demonstrations of advanced EBCs-CMCs in complex simulated engine thermal gradient cyclic fatigue, oxidizing-steam and CMAS environments will help provide insights into the coating development strategies to meet long-term engine component durability goals.

Impact of Fatigue in Rheumatic Diseases in the Work Environment: A Qualitative Study.

PubMed

Connolly, Deirdre; Fitzpatrick, Clodagh; O'Toole, Lynn; Doran, Michele; O'Shea, Finbar

2015-10-28

Fatigue is a symptom of arthritis that causes difficulty at work. An improved understanding of this symptom could assist its management in the work environment. The aim of this study was to explore people with rheumatic diseases' experiences of fatigue in work. A qualitative descriptive design was used with semi-structured interviews and a constant comparative method of data analysis. There were 18 participants, the majority of them female with Rheumatoid Arthritis (RA) and working full-time. Three themes were identified: "Impact of fatigue on work performance" with cognition, mood and physical abilities being the main difficulties reported. In the second theme "Disclosure at Work" participants discussed disclosing their disease to employers but reported a lack of understanding of fatigue from colleagues. The final theme "work-based fatigue management strategies" included cognitive strategies and energy management techniques, which were mainly self-taught. In this study, fatigue was reported to impact on many areas of work performance with limited understanding from colleagues and employers. Interventions from health professionals to assist with development of work-related self-management skills are required to assist with symptom management in the work place. Such interventions should include education to employers and colleagues on the nature of fatigue in Rheumatic diseases.

Impact of Fatigue in Rheumatic Diseases in the Work Environment: A Qualitative Study

PubMed Central

Connolly, Deirdre; Fitzpatrick, Clodagh; O’Toole, Lynn; Doran, Michele; O’Shea, Finbar

2015-01-01

Fatigue is a symptom of arthritis that causes difficulty at work. An improved understanding of this symptom could assist its management in the work environment. The aim of this study was to explore people with rheumatic diseases’ experiences of fatigue in work. A qualitative descriptive design was used with semi-structured interviews and a constant comparative method of data analysis. There were 18 participants, the majority of them female with Rheumatoid Arthritis (RA) and working full-time. Three themes were identified: “Impact of fatigue on work performance” with cognition, mood and physical abilities being the main difficulties reported. In the second theme “Disclosure at Work” participants discussed disclosing their disease to employers but reported a lack of understanding of fatigue from colleagues. The final theme “work-based fatigue management strategies” included cognitive strategies and energy management techniques, which were mainly self-taught. In this study, fatigue was reported to impact on many areas of work performance with limited understanding from colleagues and employers. Interventions from health professionals to assist with development of work-related self-management skills are required to assist with symptom management in the work place. Such interventions should include education to employers and colleagues on the nature of fatigue in Rheumatic diseases. PMID:26516896

Fatigue risk management by volunteer fire-fighters: Use of informal strategies to augment formal policy.

PubMed

Dawson, Drew; Mayger, Katherine; Thomas, Matthew J W; Thompson, Kirrilly

2015-11-01

An increasing number and intensity of catastrophic fire events in Australia has led to increasing demands on a mainly volunteer fire-fighting workforce. Despite the increasing likelihood of fatigue in the emergency services environment, there is not yet a systematic, unified approach to fatigue management in fire agencies across Australia. Accordingly, the aim of this study was to identify informal strategies used in volunteer fire-fighting and examine how these strategies are transmitted across the workforce. Thirty experienced Australian volunteer fire-fighters were interviewed in August 2010. The study identified informal fatigue-management behaviours at the individual, team and brigade level that have evolved in fire-fighting environments and are regularly implemented. However, their purpose was not explicitly recognized as such. This apparent paradox - that fatigue proofing behaviours exist but that they are not openly understood as such - may well resolve a potential conflict between a culture of indefatigability in the emergency services sector and the frequent need to operate safely while fatigued. However, formal controls require fire-fighters and their organisations to acknowledge and accept their vulnerability. This suggests two important areas in which to improve formal fatigue risk management in the emergency services sector: (1) identifying and formalising tacit or informal fatigue coping strategies as legitimate elements of the fatigue risk management system; and (2) developing culturally appropriate techniques for systematically communicating fatigue levels to self and others. Copyright © 2015 Elsevier Ltd. All rights reserved.

High Frequency Vibration Based Fatigue Testing of Developmental Alloys

NASA Astrophysics Data System (ADS)

Holycross, Casey M.; Srinivasan, Raghavan; George, Tommy J.; Tamirisakandala, Seshacharyulu; Russ, Stephan M.

Many fatigue test methods have been previously developed to rapidly evaluate fatigue behavior. This increased test speed can come at some expense, since these methods may require non-standard specimen geometry or increased facility and equipment capability. One such method, developed by George et al, involves a base-excited plate specimen driven into a high frequency bending resonant mode. This resonant mode is of sufficient frequency (typically 1200 to 1700 Hertz) to accumulate 107 cycles in a few hours. One of the main limitations of this test method is that fatigue cracking is almost certainly guaranteed to be surface initiated at regions of high stress. This brings into question the validity of the fatigue test results, as compared to more traditional uniaxial, smooth-bar testing, since high stresses are subjecting only a small volume to fatigue damage. This limitation also brings into question the suitability of this method to screen developmental alloys, should their initiation life be governed by subsurface flaws. However, if applicable, the rapid generation of fatigue data using this method would facilitate faster design iterations, identifying more quickly, material and manufacturing process deficiencies. The developmental alloy used in this study was a powder metallurgy boron-modified Ti-6Al-4V, a new alloy currently being considered for gas turbine engine fan blades. Plate specimens were subjected to fully reversed bending fatigue. Results are compared with existing data from commercially available Ti-6Al-4V using both vibration based and more traditional fatigue test methods.

Effect of fatigue loading on critical current in stainless steel-laminated DI-BSCCO superconducting composite tape

NASA Astrophysics Data System (ADS)

Hojo, M.; Osawa, K.; Adachi, T.; Inoue, Y.; Osamura, K.; Ochiai, S.; Ayai, N.; Hayashi, K.

2010-11-01

Tensile strain tolerance of the critical current in (Bi,Pb)2Sr2Ca2Cu3Ox (Bi2223) composite superconductor is dramatically improved when the tape is laminated with stainless steel. For practical applications, it is important to understand whether this reinforcement by lamination is effective under fatigue loading. In the present study, we carried out fatigue tests in LN2 and measured the critical current at the specific fatigue cycles to clarify the strain tolerance of the critical current in stainless steel-laminated drastically innovative Bi2223 (DI-BSCCO®) tapes. The fatigue tests were carried out using a computer-controlled 10 kN servo-hydraulic fatigue testing machine with a load cell capacity of 2.5 kN. Tests under static loading showed that the irreversible stress at which the critical current is reduced by 1% from the original value (tensile stress at Ic/Ic0 = 0.99) was 315 MPa when measured at unloading state. The present fatigue tests results indicated that the critical current was maintained at over 98% of the original value at unloading state after stress cycles of 106 when the static irreversible stress was selected as the maximum stress under fatigue loading. Thus, laminated DI-BSCCO tapes showed excellent mechanical properties even under fatigue loading.

Axial-Load Fatigue Tests on 17-7 PH Stainless Steel Under Constant-Amplitude Loading

NASA Technical Reports Server (NTRS)

Leybold, Herbert A.

1960-01-01

Axial-load fatigue tests were conducted at room temperature on notched and unnotched sheet specimens of 17-7 PH stainless steel in Condition TH 1050. The notched specimens had theoretical stress-concentration factors of 2.32, 4.00, and 5.00. All specimens were tested under completely reversed loading. S-N curves are presented for each specimen configuration and ratios of fatigue strengths of unnotched specimens to those of notched specimens are given. Predictions of the fatigue behavior of notched specimens near the fatigue limit were made.

Strain-controlled fatigue of acrylic bone cement.

PubMed

Carter, D R; Gates, E I; Harris, W H

1982-09-01

Monotonic tensile tests and tension-compression fatigue tests were conducted of wet acrylic bone cement specimens at 37 degrees C. All testing was conducted in strain control at a strain rate of 0.02/s. Weibull analysis of the tensile tests indicated that monotonic fracture was governed more strongly by strain than stress. The number of cycles to fatigue failure was also more strongly controlled by strain amplitude than stress amplitude. Specimen porosity distribution played a major role in determining the tensile and fatigue strengths. The degree of data scatter suggests that Weibull analysis of fatigue data may be useful in developing design criteria for the surgical use of bone cement.

Characterization of fatigue behavior of 2-D woven fabric reinforced ceramic matrix composite at elevated temperature. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Groner, D.J.

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced SiC/SiC ceramic matrix composite specimens at 1100 deg C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle/low stress fatigue tests, far less fiber/matrix interface debond was evident than in low cycle/high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.

Comparison of Mode II and III Monotonic and Fatigue Delamination Onset Behavior for Carbon/Toughened Epoxy Composites

NASA Technical Reports Server (NTRS)

Li, Jian; OBrien, T. Kevin; Lee, Shaw Ming

1997-01-01

Monotonic and fatigue tests were performed to compare the Mode II and III interlaminar fracture toughness and fatigue delamination onset for Tenax-HTA/R6376 carbon/toughened epoxy composites. The Mode II interlaminar fracture toughness and fatigue delamination onset were characterized using the end-notched flexure (ENF) test while the Mode III interlaminar fracture toughness and fatigue delamination onset were characterized by using the edge crack torsion (ECT) test. Monotonic tests show that the Mode III fracture toughness is higher than the Mode II fracture toughness. Both Mode II and III cyclic loading greatly increases the tendency for a delamination to grow relative to a single monotonically increasing load. Under fatigue loading, the Mode III specimen also has a longer life than the Mode II specimen.

Analysis of methods for determining high cycle fatigue strength of a material with investigation of titanium-aluminum-vanadium gigacycle fatigue behavior

NASA Astrophysics Data System (ADS)

Pollak, Randall D.

Today, aerospace engineers still grapple with the qualitative and quantitative understanding of fatigue behavior in the design and testing of turbine-driven jet engines. The Department of Defense has taken a very active role in addressing this problem with the formation of the National High Cycle Fatigue Science & Technology Program in 1994. The primary goal of this program is to further the understanding of high cycle fatigue (HCF) behavior and develop methods in order to mitigate the negative impact of HCF on aerospace operations. This research supports this program by addressing the fatigue strength testing guidance currently provided by the DoD to engine manufacturers, with the primary goal to investigate current methods and recommend a test strategy to characterize the fatigue strength of a material at a specified number of cycles, such as the 109 design goal specified by MIL-HDBK-1783B, or range of cycles. The research utilized the benefits of numerical simulation to initially investigate the staircase method for use in fatigue strength testing. The staircase method is a commonly used fatigue strength test, but its ability to characterize fatigue strength variability is extremely suspect. A modified staircase approach was developed and shown to significantly reduce bias and scatter in estimates for fatigue strength variance. Experimental validation of this proposed test strategy was accomplished using a dual-phase Ti-6Al-4V alloy. The HCF behavior of a second material with a very different microstructure (beta annealed Ti-6Al-4V) was also investigated. The random fatigue limit (RFL) model, a recently developed analysis tool, was investigated to characterize stress-life behavior but found to have difficulty representing fatigue life curves with sharp transitions. Two alternative models (bilinear and hyperbolic) were developed based on maximum likelihood methods to better characterize the Ti-6Al-4V fatigue life behavior. These models provided a good fit to the experimental data for the dual-phase Ti-6Al-4V and were applied to the beta annealed variant in order to estimate stress-life behavior using a small-sample approach. Based on this research, designers should be better able to make reliable estimates of fatigue strength parameters using small-sample testing.

Synthesis of Sine-on-Random vibration profiles for accelerated life tests based on fatigue damage spectrum equivalence

NASA Astrophysics Data System (ADS)

Angeli, Andrea; Cornelis, Bram; Troncossi, Marco

2018-03-01

In many real life environments, mechanical and electronic systems are subjected to vibrations that may induce dynamic loads and potentially lead to an early failure due to fatigue damage. Thus, qualification tests by means of shakers are advisable for the most critical components in order to verify their durability throughout the entire life cycle. Nowadays the trend is to tailor the qualification tests according to the specific application of the tested component, considering the measured field data as reference to set up the experimental campaign, for example through the so called "Mission Synthesis" methodology. One of the main issues is to define the excitation profiles for the tests, that must have, besides the (potentially scaled) frequency content, also the same damage potential of the field data despite being applied for a limited duration. With this target, the current procedures generally provide the test profile as a stationary random vibration specified by a Power Spectral Density (PSD). In certain applications this output may prove inadequate to represent the nature of the reference signal, and the procedure could result in an unrealistic qualification test. For instance when a rotating part is present in the system the component under analysis may be subjected to Sine-on-Random (SoR) vibrations, namely excitations composed of sinusoidal contributions superimposed to random vibrations. In this case, the synthesized test profile should preserve not only the induced fatigue damage but also the deterministic components of the environmental vibration. In this work, the potential advantages of a novel procedure to synthesize SoR profiles instead of PSDs for qualification tests are presented and supported by the results of an experimental campaign.

Fracture mechanics and corrosion fatigue.

NASA Technical Reports Server (NTRS)

Mcevily, A. J.; Wei, R. P.

1972-01-01

Review of the current state-of-the-art in fracture mechanics, particularly in relation to the study of problems in environment-enhanced fatigue crack growth. The usefulness of this approach in developing understanding of the mechanisms for environmental embrittlement and its engineering utility are discussed. After a brief review of the evolution of the fracture mechanics approach and the study of environmental effects on the fatigue behavior of materials, a study is made of the response of materials to fatigue and corrosion fatigue, the modeling of the mechanisms of the fatigue process is considered, and the application of knowledge of fatigue crack growth to the prediction of the high cycle life of unnotched specimens is illustrated.

Sonic fatigue testing of an advanced composite aileron

NASA Technical Reports Server (NTRS)

Soovere, J.

1982-01-01

The sonic fatigue test program to verify the design of the composite inboard aileron for the L-1011 airplane is described. The composite aileron is fabricated from graphite/epoxy minisandwich covers which are attached to graphite/epoxy front spar and ribs, and to an aluminum rear spar with fasteners. The program covers the development of random fatigue data by means of coupon testing and modal studies on a representative section of the composite aileron, culminating in the accelerated sonic fatigue proof test. The composite aileron sustained nonlinear panel vibration during the proof test without failure. Viscous damping coefficients as low as 0.4% were measured on the panels. The effects of moisture conditioning and elevated temperature on the random fatigue life of both undamaged and impact damaged coupons were investigated. The combination of impact damage, moisture, and a 180 F temperature could reduce the random fatigue life by 50%.

Isothermal and thermal-mechanical fatigue of VVER-440 reactor pressure vessel steels

NASA Astrophysics Data System (ADS)

Fekete, Balazs; Trampus, Peter

2015-09-01

The fatigue life of the structural materials 15Ch2MFA (CrMoV-alloyed ferritic steel) and 08Ch18N10T (CrNi-alloyed austenitic steel) of VVER-440 reactor pressure vessel under completely reserved total strain controlled low cycle fatigue tests were investigated. An advanced test facility was developed for GLEEBLE-3800 physical simulator which was able to perform thermomechanical fatigue experiments under in-service conditions of VVER nuclear reactors. The low cycle fatigue results were evaluated with the plastic strain based Coffin-Manson law, and plastic strain energy based model as well. It was shown that both methods are able to predict the fatigue life of reactor pressure vessel steels accurately. Interrupted fatigue tests were also carried out to investigate the kinetic of the fatigue evolution of the materials. On these samples microstructural evaluation by TEM was performed. The investigated low cycle fatigue behavior can provide reference for remaining life assessment and lifetime extension analysis.

Fatigue limit and Hysteresis Behavior of Type 304L Stainless Steel in Air and PWR Water, at 150°C and 300°C

NASA Astrophysics Data System (ADS)

Solomon, H. D.; Amzallag, C.; Vallee, A. J.; DeLair, R. E.

This is a study of the 107 cycle fatigue limit of Type 304L Stainless Steel, as measured in fully reversed (R=-1) load-controlled tests, at 150°C and 300°C, in air and PWR water. The staircase method was used to determine the fatigue limit. The tests run here utilized a cycle frequency of 1.818Hz and are compared to other tests from the literature that were run at 30Hz. The fatigue limit measured in the tests run at the high frequency was higher than that measured here. This is explained by measurements of the strain developed during cycling, using the different cycle frequencies. The tests run at the higher frequencies yielded lower strains for a given stress and, as expected, this resulted in higher fatigue limits. Using 107 cycles to define a run-out also led to a lower fatigue limit. These results are important as most previous fatigue limit measurements utilized 106 cycles or less to define a run-out, and when lives as long as 107 cycles are used the tests are generally run at high cycle frequencies, thus leading to higher fatigue limits than those measured here.

Fatigue Crack Growth Behavior Evaluation of Grainex Mar-M 247 for NASA's High Temperature, High Speed Turbine Seal Test Rig

NASA Technical Reports Server (NTRS)

Delgado, Irebert R.; Steinetz, Bruce M.; Rimnac, Clare M.; Lewandowski, John J.

2008-01-01

The fatigue crack growth behavior of Grainex Mar-M 247 is evaluated for NASA s Turbine Seal Test Facility. The facility is used to test air-to-air seals primarily for use in advanced jet engine applications. Because of extreme seal test conditions of temperature, pressure, and surface speeds, surface cracks may develop over time in the disk bolt holes. An inspection interval is developed to preclude catastrophic disk failure by using experimental fatigue crack growth data. By combining current fatigue crack growth results with previous fatigue strain-life experimental work, an inspection interval is determined for the test disk. The fatigue crack growth life of the NASA disk bolt holes is found to be 367 cycles at a crack depth of 0.501 mm using a factor of 2 on life at maximum operating conditions. Combining this result with previous fatigue strain-life experimental work gives a total fatigue life of 1032 cycles at a crack depth of 0.501 mm. Eddy-current inspections are suggested starting at 665 cycles since eddy current detection thresholds are currently at 0.381 mm. Inspection intervals are recommended every 50 cycles when operated at maximum operating conditions.

Proof test and fatigue crack growth modeling on 2024-T3 aluminum alloy

NASA Technical Reports Server (NTRS)

Newman, J. C., Jr.; Poe, C. C., Jr.; Dawicke, D. S.

1990-01-01

Pressure proof testing of aircraft fuselage structures has been suggested as a means of screening critical crack sizes and of extending their useful life. The objective of this paper is to study the proof-test concept and to model the crack-growth process on a ductile material. Simulated proof and operational fatigue life tests have been conducted on cracked panels made of 2024-T3 aluminum alloy sheet material. A fatigue crack-closure model was modified to simulate the proof test and operational fatigue cycling. Using crack-growth rate and resistance-curve data, the model was able to predict crack growth during and after the proof load. These tests and analyses indicate that the proof test increases fatigue life; but the beneficial life, after a 1.33 or 1.5 proof, was less than a few hundred cycles.

Improved High-Cycle Fatigue (HCF) Life Prediction

DTIC Science & Technology

2001-01-01

fatigue in 2024 - T351 aluminum alloy ’, Wear 221, 24-36. Appendix 6C CHARACTERIZATION OF FRETTING FATIGUE INITIATED CRACKS P.J. Golden A.F...0.8. To evaluate the effects of surface residual stresses on notch fatigue life , shot peened specimens were tested at R = -1.0 and 0.1. Data in...Behavior - Response • The undamaged fatigue test program demonstrates the sensitivity of surface effects (for different

The influence of cyclic shear fatigue on the bracket-adhesive-enamel complex: an in vitro study.

PubMed

Daratsianos, Nikolaos; Musabegovic, Ena; Reimann, Susanne; Grüner, Manfred; Jäger, Andreas; Bourauel, Christoph

2013-05-01

To describe the effect of fatigue on the strength of the bracket-adhesive-enamel complex and characterize the fatigue behavior of the materials tested. Upper central incisor brackets (Discovery(®), Dentaurum) were bonded with a light-curing (Transbond XT™, 3M Unitek) and a chemically-curing adhesive (Concise™, 3M Unitek) on bovine teeth embedded in cylindrical resign bases and stored in water at 37(±2)°C for 24 (±2)h. The first 15 specimens were tested with a universal testing machine ZMART.PRO(®) (Zwick GmbH & Co. KG, Ulm, Germany) for ultimate shear bond strength according to the DIN-13990-2-standard. The remaining three groups of 20 specimens underwent fatigue staircase testing of 100, 1000 and 3000 cycles at 1Hz with a self-made testing machine. The survived specimens were subjected to shear strength testing. The fatigued specimens showed decreased shear strength with both adhesives at all cycle levels. The shear strength after fatigue for 100, 1000 and 3000 cycles was in the Concise™-groups 34.8%, 59.0%, 47.3% and in the Transbond™ XT-groups 33.6%, 23.1%, 27.3% relative to the ultimate shear strength. The fatigue life of the Concise™-groups decreased with increasing stress and Transbond™ XT showed lower fatigue ratio with no obvious trend. The specimens bonded with Transbond™ XT showed typically favorable fracture modes in contrary to Concise™. Fatigue of the bracket-adhesive-enamel complex decreased its shear strength. The staircase method can provide a standardized experimental protocol for fatigue studies, however testing at various cycle numbers is recommended. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Experimental Study on Fatigue Performance of Foamed Lightweight Soil

NASA Astrophysics Data System (ADS)

Qiu, Youqiang; Yang, Ping; Li, Yongliang; Zhang, Liujun

2017-12-01

In order to study fatigue performance of foamed lightweight soil and forecast its fatigue life in the supporting project, on the base of preliminary tests, beam fatigue tests on foamed lightweight soil is conducted by using UTM-100 test system. Based on Weibull distribution and lognormal distribution, using the mathematical statistics method, fatigue equations of foamed lightweight soil are obtained. At the same time, according to the traffic load on real road surface of the supporting project, fatigue life of formed lightweight soil is analyzed and compared with the cumulative equivalent axle loads during the design period of the pavement. The results show that even the fatigue life of foamed lightweight soil has discrete property, the linear relationship between logarithmic fatigue life and stress ratio still performs well. Especially, the fatigue life of Weibull distribution is more close to that derived from the lognormal distribution, in the instance of 50% guarantee ratio. In addition, the results demonstrated that foamed lightweight soil as subgrade filler has good anti-fatigue performance, which can be further adopted by other projects in the similar research domain.

Bithermal fatigue: A simplified alternative to thermomechanical fatigue

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.

1988-01-01

A bithermal fatigue test technique was proposed as a simplified alternative to the thermomechanical fatigue test. Both the thermomechanical cycle and the bithermal technique can be used to study nonisothermal fatigue behavior. The difference between the two cycles is that in a conventional thermomechanical fatigue cycle the temperature is continuously varied concurrently with the applied mechanical strains, but in the bithermal fatigue cycle the specimen is held at zero load during the temperature excursions and all the loads are applied at the two extreme temperatures of the cycle. Experimentally, the bithermal fatigue test technique offers advantages such as ease in synchronizing the temperature and mechanical strain waveforms, in minimizing temperature gradients in the specimen gauge length, and in reducing and interpreting thermal fatigue such as the influence of alternate high and low temperatures on the cyclic stress-strain response characteristics, the effects of thermal state, and the possibility of introducing high- and low-temperature deformation mechanisms within the same cycle. The bithermal technique was used to study nonisothermal fatigue behavior of alloys such as single-crystal PWA 1480, single-crystal Rene N4, cast B1900+Hf, and wrought Haynes 188.

Creep-fatigue of low cobalt superalloys

NASA Technical Reports Server (NTRS)

Halford, G. R.

1982-01-01

Testing for the low cycle fatigue and creep fatigue resistance of superalloys containing reduced amounts of cobalt is described. The test matrix employed involves a single high temperature appropriate for each alloy. A single total strain range, again appropriate to each alloy, is used in conducting strain controlled, low cycle, creep fatigue tests. The total strain range is based upon the level of straining that results in about 10,000 cycles to failure in a high frequency (0.5 Hz) continuous strain-cycling fatigue test. No creep is expected to occur in such a test. To bracket the influence of creep on the cyclic strain resistance, strain hold time tests with ore minute hold periods are introduced. One test per composition is conducted with the hold period in tension only, one in compression only, and one in both tension and compression. The test temperatures, alloys, and their cobalt compositions that are under study are given.

Investigation of fatigue failure in bituminous base mixes.

DOT National Transportation Integrated Search

1980-01-01

A correlation between the results obtained with the fatigue test and those from the indirect tensile test on two base mixes was attempted in anticipation of the possible use of the latter test to design base mixes for maximum fatigue life. Two base m...

Cyclic fatigue damage characteristics observed for simple loadings extended to multiaxial life prediction

NASA Technical Reports Server (NTRS)

Jones, David J.; Kurath, Peter

1988-01-01

Fully reversed uniaxial strain controlled fatigue tests were performed on smooth cylindrical specimens made of 304 stainless steel. Fatigue life data and cracking observations for uniaxial tests were compared with life data and cracking behavior observed in fully reversed torsional tests. It was determined that the product of maximum principle strain amplitude and maximum principle stress provided the best correlation of fatigue lives for these two loading conditions. Implementation of this parameter is in agreement with observed physical damage and it accounts for the variation of stress-strain response, which is unique to specific loading conditions. Biaxial fatigue tests were conducted on tubular specimens employing both in-phase and out-of-phase tension torsion cyclic strain paths. Cracking observations indicated that the physical damage which occurred in the biaxial tests was similar to the damage observed in uniaxial and torsional tests. The Smith, Watson, and Topper parameter was then extended to predict the fatigue lives resulting from the more complex loading conditions.

Test Population Selection from Weibull-Based, Monte Carlo Simulations of Fatigue Life

NASA Technical Reports Server (NTRS)

Vlcek, Brian L.; Zaretsky, Erwin V.; Hendricks, Robert C.

2008-01-01

Fatigue life is probabilistic and not deterministic. Experimentally establishing the fatigue life of materials, components, and systems is both time consuming and costly. As a result, conclusions regarding fatigue life are often inferred from a statistically insufficient number of physical tests. A proposed methodology for comparing life results as a function of variability due to Weibull parameters, variability between successive trials, and variability due to size of the experimental population is presented. Using Monte Carlo simulation of randomly selected lives from a large Weibull distribution, the variation in the L10 fatigue life of aluminum alloy AL6061 rotating rod fatigue tests was determined as a function of population size. These results were compared to the L10 fatigue lives of small (10 each) populations from AL2024, AL7075 and AL6061. For aluminum alloy AL6061, a simple algebraic relationship was established for the upper and lower L10 fatigue life limits as a function of the number of specimens failed. For most engineering applications where less than 30 percent variability can be tolerated in the maximum and minimum values, at least 30 to 35 test samples are necessary. The variability of test results based on small sample sizes can be greater than actual differences, if any, that exists between materials and can result in erroneous conclusions. The fatigue life of AL2024 is statistically longer than AL6061 and AL7075. However, there is no statistical difference between the fatigue lives of AL6061 and AL7075 even though AL7075 had a fatigue life 30 percent greater than AL6061.

Test Population Selection from Weibull-Based, Monte Carlo Simulations of Fatigue Life

NASA Technical Reports Server (NTRS)

Vlcek, Brian L.; Zaretsky, Erwin V.; Hendricks, Robert C.

2012-01-01

Fatigue life is probabilistic and not deterministic. Experimentally establishing the fatigue life of materials, components, and systems is both time consuming and costly. As a result, conclusions regarding fatigue life are often inferred from a statistically insufficient number of physical tests. A proposed methodology for comparing life results as a function of variability due to Weibull parameters, variability between successive trials, and variability due to size of the experimental population is presented. Using Monte Carlo simulation of randomly selected lives from a large Weibull distribution, the variation in the L10 fatigue life of aluminum alloy AL6061 rotating rod fatigue tests was determined as a function of population size. These results were compared to the L10 fatigue lives of small (10 each) populations from AL2024, AL7075 and AL6061. For aluminum alloy AL6061, a simple algebraic relationship was established for the upper and lower L10 fatigue life limits as a function of the number of specimens failed. For most engineering applications where less than 30 percent variability can be tolerated in the maximum and minimum values, at least 30 to 35 test samples are necessary. The variability of test results based on small sample sizes can be greater than actual differences, if any, that exists between materials and can result in erroneous conclusions. The fatigue life of AL2024 is statistically longer than AL6061 and AL7075. However, there is no statistical difference between the fatigue lives of AL6061 and AL7075 even though AL7075 had a fatigue life 30 percent greater than AL6061.

Human performance capabilities in a simulated space station-like environment. 1: Fixed beam luminance and location

NASA Technical Reports Server (NTRS)

Haines, R. F.; Bartz, A. E.; Zahn, J. R.

1972-01-01

The effects of a fixed, intense, one-foot diameter beam of simulated sunlight imaged within the field of view, upon responses to a battery of visual, body balance and stability, eye-hand coordination, and mental tests were studied. Each subject's electrocardiogram and electro-oculograms (vertical and horizontal) were recorded throughout each two-hour testing period within the space-station-like environment. It is possible to say that both subjects adapted to the brightly illuminated white panels in approximately 30 seconds after their first exposure each day and thereafter did not experience ocular fatigue, eye strain, or other kinds of disturbances as a result of these viewing conditions.

Advanced single crystal for SSME turbopumps

NASA Technical Reports Server (NTRS)

Fritzemeier, L. G.

1989-01-01

The objective of this program was to evaluate the influence of high thermal gradient casting, hot isostatic pressing (HIP) and alternate heat treatments on the microstructure and mechanical properties of a single crystal nickel base superalloy. The alloy chosen for the study was PWA 1480, a well characterized, commercial alloy which had previously been chosen as a candidate for the Space Shuttle Main Engine high pressure turbopump turbine blades. Microstructural characterization evaluated the influence of casting thermal gradient on dendrite arm spacing, casting porosity distribution and alloy homogeneity. Hot isostatic pressing was evaluated as a means of eliminating porosity as a preferred fatigue crack initiation site. The alternate heat treatment was chosen to improve hydrogen environment embrittlement resistance and for potential fatigue life improvement. Mechanical property evaluation was aimed primarily at determining improvements in low cycle and high cycle fatigue life due to the advanced processing methods. Statistically significant numbers of tests were conducted to quantitatively demonstrate life differences. High thermal gradient casting improves as-cast homogeneity, which facilitates solution heat treatment of PWA 1480 and provides a decrease in internal pore size, leading to increases in low cycle and high cycle fatigue lives.

Relationship Between Unusual High-Temperature Fatigue Crack Growth Threshold Behavior in Superalloys and Sudden Failure Mode Transitions

NASA Technical Reports Server (NTRS)

Telesman, J.; Smith, T. M.; Gabb, T. P.; Ring, A. J.

2017-01-01

An investigation of high temperature cyclic fatigue crack growth (FCG) threshold behavior of two advanced nickel disk alloys was conducted. The focus of the study was the unusual crossover effect in the near-threshold region of these type of alloys where conditions which produce higher crack growth rates in the Paris regime, produce higher resistance to crack growth in the near threshold regime. It was shown that this crossover effect is associated with a sudden change in the fatigue failure mode from a predominant transgranular mode in the Paris regime to fully intergranular mode in the threshold fatigue crack growth region. This type of a sudden change in the fracture mechanisms has not been previously reported and is surprising considering that intergranular failure is typically associated with faster crack growth rates and not the slow FCG rates of the near-threshold regime. By characterizing this behavior as a function of test temperature, environment and cyclic frequency, it was determined that both the crossover effect and the onset of intergranular failure are caused by environmentally driven mechanisms which have not as yet been fully identified. A plausible explanation for the observed behavior is proposed.

Sleep and Sleepiness among First-Time Postpartum Parents: A Field- and Laboratory-Based Multimethod Assessment

PubMed Central

Insana, Salvatore P.; Montgomery-Downs, Hawley E.

2012-01-01

The study aim was to compare sleep, sleepiness, fatigue, and neurobehavioral performance among first-time mothers and fathers during their early postpartum period. Participants were 21 first-time postpartum mother-father dyads (N=42) and seven childless control dyads (N=14). Within their natural environment, participants completed one week of wrist actigraphy monitoring, along with multi-day self-administered sleepiness, fatigue, and neurobehavioral performance measures. The assessment week was followed by an objective laboratory based test of sleepiness. Mothers obtained more sleep compared to fathers, but mothers’ sleep was more disturbed by awakenings. Fathers had greater objectively measured sleepiness than mothers. Mothers and fathers did not differ on subjectively measured sleep quality, sleepiness, or fatigue; however, mothers had worse neurobehavioral performance than fathers. Compared to control dyads, postpartum parents experienced greater sleep disturbance, sleepiness, and sleepiness associated impairments. Study results inform social policy, postpartum sleep interventions, and research on postpartum family systems and mechanisms that propagate sleepiness. PMID:22553114

Health Monitoring for Airframe Structural Characterization

NASA Technical Reports Server (NTRS)

Munns, Thomas E.; Kent, Renee M.; Bartolini, Antony; Gause, Charles B.; Borinski, Jason W.; Dietz, Jason; Elster, Jennifer L.; Boyd, Clark; Vicari, Larry; Ray, Asok;

Cognitive and Physical Fatigue Tasks Enhance Pain, Cognitive Fatigue and Physical Fatigue in People with Fibromyalgia

PubMed Central

Dailey, Dana L; Keffala, Valerie J; Sluka, Kathleen A

2014-01-01

Objective Fibromyalgia is a condition characterized by chronic widespread muscle pain and fatigue. The primary objective of this study was to determine if pain, perceived cognitive fatigue, and perceived physical fatigue were enhanced in participants with fibromyalgia compared to healthy controls during a cognitive fatigue task, a physical fatigue task and a dual fatigue task. Methods Twenty four people with fibromyalgia and 33 healthy controls completed pain, fatigue and function measures. A cognitive fatigue task (Controlled Oral Word Association Test) and physical fatigue task (Valpar peg test) were done individually and combined for a dual fatigue task. Resting pain, perceived cognitive fatigue and perceived physical fatigue were assessed during each task using visual analogue scales. Function was assessed with shoulder range of motion and grip. Results People with fibromyalgia had significantly higher increases in pain, cognitive fatigue and physical fatigue when compared to healthy controls after completion of a cognitive fatigue task, a physical fatigue task, or a dual fatigue task (p<0.01). People with fibromyalgia performed equivalently on measures of physical performance and cognitive performance on the physical and cognitive fatigue tasks, respectively. Conclusions These data show that people with fibromyalgia show larger increases in pain, perceived cognitive fatigue and perceived physical fatigue to both cognitive and physical fatigue tasks compared to healthy controls. The increases in pain and fatigue during cognitive and physical fatigue tasks could influence subject participation in daily activities and rehabilitation. PMID:25074583

Laboratory Study on the Fatigue Resistance of Asphaltic Concrete Containing Titanium Dioxide

NASA Astrophysics Data System (ADS)

Buhari, Rosnawati; Ezree Abdullah, Mohd; Khairul Ahmad, Mohd; Azhar Tajudin, Saiful; Khatijah Abu Bakar, Siti

2018-03-01

This study aims to evaluate the fatigue performance of modified asphalt mixture using Indirect Tensile Fatigue Test. Titanium Dioxide (TiO2) powder in a form of rutile was used for producing asphalt concrete with lower mixing and compaction temperature compared to conventional hot mix asphalt without reducing its physical and mechanical also resistance to fatigue. The characteristic of the asphalt and modified asphalt was evaluated using penetration test, softening test and rotational viscosity test. Titanium dioxide of 2%, 4%, 6%, 8% and 10% by weight of asphalt has been incorporated into unaged 80/100 asphalt mix in order to improvise its performance and to fulfill the objectives of this experimental study. As a result, TiO2 as an additive is potential to decrease the penetration and increasing the softening point of the asphalt. In terms of fatigue performance testing, addition TiO2 additive does help in improving the fatigue properties as it shows greater result than the control asphalt. In conclusion, TiO2 is great in improving fatigue properties.

High temperature, low cycle fatigue of copper-base alloys in argon. Part 3: Zirconium-copper; thermal-mechanical strain cycling, hold-time and notch fatigue results

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1973-01-01

The low-cycle fatigue characteristics of smooth bar and notched bar specimens (hourglass shape) of zirconium-copper, 1/2 Hard, material (R-2 Series) were evaluated at room temperature in axial strain control. Over the fatigue life range from about 300 to 3000 cycles the ratio of fatigue life for smooth bar to fatigue life for notched bar remained constant at a value of about 6.0. Some additional hold-time data for the R-2 alloy tested in argon at 538 C are reported. An analysis of the relaxation data obtained in these hold-time tests is also reported and it is shown that these data yield a fairly consistent correlation in terms of instantaneous stress rate divided by instantaneous stress. Two thermal-mechanical strain cycling tests were also performed using a cyclic frequency of 4.5 cycles per hour and a temperature cycling interval from 260 to 538 C. The fatigue life values in these tests were noticeably lower than that observed in isothermal tests at 538 C.

Review of specimen heating in mechanical tests at cryogenic temperatures

NASA Astrophysics Data System (ADS)

Ogata, T.; Yuri, T.; Ono, Y.

2014-01-01

At cryogenic temperatures near 4 K, a discontinuous deformation produces a large amount of specimen temperature rise that might bring significant changes in mechanical properties. The authors measured the specimen heating in tensile tests, fatigue test, and other tests in liquid helium for stainless steels and other materials. In this paper, we have measured the specimen temperature in high-cycle and low-cycle fatigue tests for stainless steels at various frequencies and stress levels and evaluated the testing conditions to keep the specimen at a specified temperature. We proposed maximum frequency in load-controlled fatigue tests for specified loading variables and a maximum strain rate in strain-controlled fatigue tests.

Rolling-element fatigue life with two synthetic cycloaliphatic traction fluids

NASA Technical Reports Server (NTRS)

Loewenthal, S. H.; Parker, R. J.

1976-01-01

The life potential of two synthetic cycloaliphatic hydrocarbon traction fluids in rolling element fatigue was evaluated in a five ball fatigue tester. Life comparisons with a MIL-L-23699 qualified tetraester oil showed that the traction test oils had good fatigue life performance, comparable to that of the tetraester oil. No statistically significant life differences between the traction fluids and the tetraester oil were exhibited under the accelerated fatigue test conditions. Erratic operating behavior was occasionally encountered during tests with the antiwear additive containing traction fluid for reasons thought to be related to excessive chemical activity under high contact pressure. This behavior occasionally resulted in premature test termination due to excessive surface distress and overheating.

Effects of Total SAT® Test Time on Performance and Fatigue. Research Notes. RN-37

ERIC Educational Resources Information Center

Ackerman, Phillip L.; Kanfer, Ruth; Wolman, Stacey D.

2005-01-01

The current study was designed to examine performance effects and fatigue effects associated with different total SAT testing times. In addition, the researchers examined personality, motivation, and other determinants of individual differences in examinee fatigue before, during, and after testing.

An evaluation of the fatigue crack growth and fracture toughness properties of beryllium-copper alloy CDA172

NASA Technical Reports Server (NTRS)

Forman, Royce G.; Henkener, Julie A.

1990-01-01

A series of fracture mechanics tests, using the Be-Cu alloy CDA172 in the round rod product form, was conducted in a lab air environment at room temperature. Tensile data is presented in both the L and C directions and K sub Ic data in both the C-R and C-L orientations. Fracture toughness values were derived from M(T) (center cracked), PS(T) (surface cracked) and CC01 (corner cracked) specimens of varying thickness. Fatigue crack growth data were obtained for the C-R orientation at stress ratio of 0.1, 0.4, and 0.7 and for the C-L orientation at stress ratios of 0.1, 0.3, 0.4, and 0.7.

Accelerated life assessment of coating on the radar structure components in coastal environment.

PubMed

Liu, Zhe; Ming, ZhiMao

2016-07-04

This paper aimed to build an accelerated life test scheme and carry out quantitative analysis between accelerated life test in the laboratory and actual service for the coating composed of epoxy primer and polyurethane paint on structure components of some kind of radar served in the coastal environment of South China Sea. The accelerated life test scheme was built based on the service environment and failure analysis of the coating. The quantitative analysis between accelerated life test and actual service was conducted by comparing the gloss loss, discoloration, chalking, blistering, cracking and electrochemical impedance spectroscopy of the coating. The main factors leading to the coating failure were ultraviolet radiation, temperature, moisture, salt fog and loads, the accelerated life test included ultraviolet radiation, damp heat, thermal shock, fatigue and salt spray. The quantitative relationship was that one cycle of the accelerated life test was equal to actual service for one year. It was established that one cycle of the accelerated life test was equal to actual service for one year. It provided a precise way to predict actual service life of newly developed coatings for the manufacturer.

Fatigue and Creep Crack Propagation behaviour of Alloy 617 in the Annealed and Aged Conditions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Julian K. Benz; Richard N. Wright

2013-10-01

The crack propagation behaviour of Alloy 617 was studied under various conditions. Elevated temperature fatigue and creep-fatigue crack growth experiments were conducted at 650 and 800 degrees C under constant stress intensity (triangle K) conditions and triangular or trapezoidal waveforms at various frequencies on as-received, aged, and carburized material. Environmental conditions included both laboratory air and characteristic VHTR impure helium. As-received Alloy 617 displayed an increase in the crack growth rate (da/dN) as the frequency was decreased in air which indicated a time-dependent contribution component in fatigue crack propagation. Material aged at 650°C did not display any influence on themore » fatigue crack growth rates nor the increasing trend of crack growth rate with decreasing frequency even though significant microstructural evolution, including y’ (Ni3Al) after short times, occurred during aging. In contrast, carburized Alloy 617 showed an increase in crack growth rates at all frequencies tested compared to the material in the standard annealed condition. Crack growth studies under quasi-constant K (i.e. creep) conditions were also completed at 650 degrees C and a stress intensity of K = 40 MPa9 (square root)m. The results indicate that crack growth is primarily intergranular and increased creep crack growth rates exist in the impure helium environment when compared to the results in laboratory air. Furthermore, the propagation rates (da/dt) continually increased for the duration of the creep crack growth either due to material aging or evolution of a crack tip creep zone. Finally, fatigue crack propagation tests at 800 degrees C on annealed Alloy 617 indicated that crack propagation rates were higher in air than impure helium at the largest frequencies and lowest stress intensities. The rates in helium, however, eventually surpass the rates in air as the frequency is reduced and the stress intensity is decreased which was not observed at 650 degrees C.« less

Fracture characteristics, microstructure, and tissue reaction of Ti-5Al-2.5Fe for orthopedic surgery

NASA Astrophysics Data System (ADS)

Niinomi, Mitsuo; Kobayashi, Toshiro; Toriyama, Osamu; Kawakami, Noriaki; Ishida, Yoshihito; Matsuyama, Yukihiro

1996-12-01

The microstructure of Ti-5Al-2.5Fe, which is expected to be used widely as an implant material not only for artificial hip joints but also for instrumentations of scoliosis surgery, was variously changed by heat treatments. The effect of the microstructure on mechanical properties, fracture toughness, and rotating-bending fatigue strength in the air and simulated body environment, that is, Ringer’s solution, was then investigated. Furthermore, the effect of the living body environment on mechanical properties and fracture toughness in Ti-5Al-2.5Fe were investigated on the specimens implanted into rabbit for about 11 months. The data of Ti-5Al-2.5Fe were compared with those of Ti-6Al-4V ELI, which has been used as an implant material mainly for artificial hip joints, and SUS 316L, which has been used as an implant material for many parts, including the instrumentation of scoliosis surgery. The equiaxed α structure, which is formed by annealing at a temperature below β transus, gives the best balance of strength and ductility in Ti-5Al-2.5Fe. The coarse Widmanstätten α structure, which is formed by solutionizing over β transus followed by air cooling and aging, gives the greatest fracture toughness in Ti-5Al-2.5Fe. This trend is similar to that reported in Ti-6Al-4V ELI. The rotating-bending fatigue strength is the greatest in the equiaxed α structure, which is formed by solutionizing below β transus followed by air cooling and aging in Ti-5Al-2.5Fe. Ti-5Al-2.5Fe exhibits much greater rotating-bending fatigue strength compared with SUS 316L, and equivalent rotating-bending fatigue strength to that of Ti-6Al-4V ELI in both the air and simulated body environments. The rotating-bending fatigue strength of SUS 316L is degraded in the simulated body environment. The corrosion fatigue, therefore, occurs in SUS 316L in the simulated body environment. Fatigue strength of Ti-5Al-2.5Fe in the simulated body environment is degraded by lowering oxygen content in the simulated body environment because the formability of oxide on the specimen surface is considered to be lowered comparing with that in air. The mechanical property and fracture toughness of Ti-5Al-2.5Fe and Ti-6Al-4V ELI are not changed in the living body environment. The hard-surface corrosion layer is, however, formed on the surface of SUS 316L in the living body environment. The C1 peak is detected from the hard-surface corrosion layer by energy-dispersive X-ray (EDX) analysis. These facts suggests a possibility for corrosion fatigue to occur in the living body environment when SUS 316L is used. The fibrous connective tissue and new bone formation are formed beside all metals. There is, however, no big difference between tissue morphology around each implant material.

High burn-up spent nuclear fuel transport reliability investigation

DOE PAGES

Wang, Jy-An; Wang, Hong; Jiang, Hao; ...

2018-04-15

Transportation packages for spent nuclear fuel (SNF) must meet safety requirements under normal and accident conditions as specified by federal regulations. During road or rail transportation, SNF will experience unique conditions that could affect the structural integrity of the cladding due to vibrational and impact loading. Lack of SNF inertia-induced dynamic fatigue data, especially for the high burn-up (HBU) SNF systems, has brought significant challenges to quantify the reliability of SNF during transportation with a high degree of confidence. To address this shortcoming, Oak Ridge National Laboratory (ORNL) developed a SNF vibration testing protocol without fuel pellets removal, which hasmore » provided significant insight regarding the dynamics of mechanical interactions between pellet and cladding. This research has provided a detailed understanding about the effect of loading rate and loading mode on the fatigue damage evolution of HBU SNF under normal conditions of transport (NCT). Static and dynamic loading experimental data were generated for SNF under simulated transportation environments using a cyclic integrated reversible-bending fatigue tester (CIRFT), an enabling hot-cell testing technology developed at ORNL. SNF flexural tensile strength and fatigue S-N data from pressurized water reactors (PWRs) and boiling water reactor (BWR) HBU SNF are presented in this paper, including the potential effects of pellet-cladding interface bonding, hydride reorientation, and thermal annealing to SNF vibration reliability. The data presented here can be used to meet the nuclear industry and U.S. Nuclear Regulatory Commission needs in safety of SNF transportation operations.« less

High burn-up spent nuclear fuel transport reliability investigation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An; Wang, Hong; Jiang, Hao

Transportation packages for spent nuclear fuel (SNF) must meet safety requirements under normal and accident conditions as specified by federal regulations. During road or rail transportation, SNF will experience unique conditions that could affect the structural integrity of the cladding due to vibrational and impact loading. Lack of SNF inertia-induced dynamic fatigue data, especially for the high burn-up (HBU) SNF systems, has brought significant challenges to quantify the reliability of SNF during transportation with a high degree of confidence. To address this shortcoming, Oak Ridge National Laboratory (ORNL) developed a SNF vibration testing protocol without fuel pellets removal, which hasmore » provided significant insight regarding the dynamics of mechanical interactions between pellet and cladding. This research has provided a detailed understanding about the effect of loading rate and loading mode on the fatigue damage evolution of HBU SNF under normal conditions of transport (NCT). Static and dynamic loading experimental data were generated for SNF under simulated transportation environments using a cyclic integrated reversible-bending fatigue tester (CIRFT), an enabling hot-cell testing technology developed at ORNL. SNF flexural tensile strength and fatigue S-N data from pressurized water reactors (PWRs) and boiling water reactor (BWR) HBU SNF are presented in this paper, including the potential effects of pellet-cladding interface bonding, hydride reorientation, and thermal annealing to SNF vibration reliability. The data presented here can be used to meet the nuclear industry and U.S. Nuclear Regulatory Commission needs in safety of SNF transportation operations.« less

Ultrasonic Fatigue Endurance of Thin Carbon Fiber Sheets

NASA Astrophysics Data System (ADS)

Domínguez Almaraz, Gonzalo M.; Ruiz Vilchez, Julio A.; Dominguez, Aymeric; Meyer, Yann

2016-04-01

Ultrasonic fatigue tests were carried out on thin carbon fiber sheets (0.3 mm of thickness) to determine the fatigue endurance under very high-frequency loading (20 kHz). This material, called the gas diffusion layer (GDL), plays a major role in the overall performances of proton exchange membrane fuel cells (PEMFCs). The study of its physical-chemical properties is an on-going subject in the literature; nevertheless, no knowledge is available concerning the high-frequency fatigue endurance. A principal difficulty in carrying out ultrasonic fatigue tests on this material was to determine the dimensions of testing specimen to fit the resonance condition. This aspect was solved by modal numerical simulation: The testing specimen has been a combination of a low-strength steel frame (to facilitate the attachment to the ultrasonic machine and to increase the mass of the specimen), and the carbon fiber hourglass-shape profile. Under resonance condition, a stationary elastic wave is generated along the specimen that induces high stress at the neck section and high displacements at the ends. Results show that fatigue life was close to 3 × 108 cycles when the high Von Misses stress at the neck section was 170 MPa, whereas fatigue life attains the 4.5 × 109 cycles when stress decreases to 117 MPa. Crack initiation and propagation were analyzed, and conclusions were drawn concerning the fatigue endurance of these fiber carbon sheets under ultrasonic fatigue testing.

Fatigue analysis and testing of wind turbine blades

NASA Astrophysics Data System (ADS)

Greaves, Peter Robert

This thesis focuses on fatigue analysis and testing of large, multi MW wind turbine blades. The blades are one of the most expensive components of a wind turbine, and their mass has cost implications for the hub, nacelle, tower and foundations of the turbine so it is important that they are not unnecessarily strong. Fatigue is often an important design driver, but fatigue of composites is poorly understood and so large safety factors are often applied to the loads. This has implications for the weight of the blade. Full scale fatigue testing of blades is required by the design standards, and provides manufacturers with confidence that the blade will be able to survive its service life. This testing is usually performed by resonating the blade in the flapwise and edgewise directions separately, but in service these two loads occur at the same time.. A fatigue testing method developed at Narec (the National Renewable Energy Centre) in the UK in which the flapwise and edgewise directions are excited simultaneously has been evaluated by comparing the Palmgren-Miner damage sum around the blade cross section after testing with the damage distribution caused by the service life. A method to obtain the resonant test configuration that will result in the optimum mode shapes for the flapwise and edgewise directions was then developed, and simulation software was designed to allow the blade test to be simulated so that realistic comparisons between the damage distributions after different test types could be obtained. During the course of this work the shortcomings with conventional fatigue analysis methods became apparent, and a novel method of fatigue analysis based on multi-continuum theory and the kinetic theory of fracture was developed. This method was benchmarked using physical test data from the OPTIDAT database and was applied to the analysis of a complete blade. A full scale fatigue test method based on this new analysis approach is also discussed..

Resistance Spot Welding Characteristics and High Cycle Fatigue Behavior of DP 780 Steel Sheet

NASA Astrophysics Data System (ADS)

Pal, Tapan Kumar; Bhowmick, Kaushik

2012-02-01

Resistance spot welding characteristics of DP 780 steel was investigated using peel test, microhardness test, tensile shear test, and fatigue test. Tensile shear test provides better spot weld quality than conventional peel test and hardness is not a good indicator of the susceptibility to interfacial fracture. The results of high-cycle fatigue behavior of spot welded DP 780 steel under two different parameters show that at high load low cycle range a significant difference in the S- N curve and almost similar fatigue behavior of spot welds at low load high cycle range are obtained. However, when applied load was converted to stress intensity factor, the difference in the fatigue behavior between welds diminished. Furthermore, a transition in fracture mode, i.e., interfacial and plug and hole-type at about 50% of yield load is observed.

Fatigue and nanomechanical properties of K3XF nickel-titanium instruments.

PubMed

Shen, Y; Zhou, H; Campbell, L; Wang, Z; Wang, R; Du, T; Haapasalo, M

2014-12-01

To examine the fatigue behaviour of heat-treated NiTi instruments when immersed in aqueous media and to determine the effect of cyclic fatigue on the hardness and elastic modulus of NiTi instruments using a nanoindentation technique. K3XF and K3 NiTi instruments, both in sizes 25, 0.04 taper and 40, 0.04 taper, were subjected to rotational bending at a curvature of 42° either in air or under deionized water, and the number of revolutions to fracture (Nf ) was recorded. The fracture surface of all fragments was examined with a scanning electron microscope. The hardness and elastic modulus of the fracture surface of instruments sized 25, 0.04 taper were then measured using a nanoindentation test. The K3XF instruments had a fatigue resistance superior to K3 instruments under dry and aqueous environments (P < 0.05). The fatigue life of K3 instruments was similar under both conditions, whereas the Nf of K3XF was greater under water than in air, especially at the size 40, 0.04 taper (P < 0.05). The values for the fraction of the area occupied by the dimple region were significantly smaller in K3XF instruments than in K3 instruments, especially under water (P < 0.05). There was no difference in hardness on K3XF instruments between new files and instruments subjected to the fatigue process. The hardness of instruments subjected to the fatigue process was significantly lower in K3XF than in K3 instruments (P < 0.05). The fatigue life of K3XF instruments under water is longer than it is for K3XF instruments in air. There was no work-hardening effect on K3XF instruments subjected to the fatigue process. © 2014 International Endodontic Journal. Published by John Wiley & Sons Ltd.

Synergistic Effects of Temperature, Oxidation and Stress Level on Fatigue Damage Evolution and Lifetime Prediction of Cross-Ply SiC/CAS Ceramic-Matrix Composites Through Hysteresis-Based Parameters

NASA Astrophysics Data System (ADS)

Li, Longbiao

2017-12-01

The damage development and cyclic fatigue lifetime of cross-ply SiC/CAS ceramic-matrix composites have been investigated at different testing temperatures in air atmosphere. The relationships between the fatigue hysteresis-based damage parameters, i.e., fatigue hysteresis dissipated energy, fatigue hysteresis modulus and fatigue peak strain and the damage mechanisms of matrix multicracking, fiber/matrix interface debonding, interface sliding and fibers failure, have been established. With the increase in the cycle number, the evolution of the fatigue hysteresis modulus, fatigue peak strain and fatigue hysteresis dissipated energy depends upon the fatigue peak stress levels, interface and fibers oxidation and testing temperature. The fatigue life S-N curves of cross-ply SiC/CAS composite at room and elevated temperatures have been predicted, and the fatigue limit stresses at room temperature, 750 and 850 °C, are 50, 36 and 30% of the tensile strength, respectively.

Analysis of SNL/MSU/DOE Fatigue Database Trends for Wind Turbine Blade Materials 2010-2015.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mandell, John F.; Samborsky, Daniel D.; Miller, David A.

Wind turbine blades are designed to several major structural conditions, including tip deflection, strength and b uckling during severe loading, as well as very high numbers of fatigue cycles and various service environments. The MSU Database Program has, since 1989, addressed the broad range of properties needed for current and potential blade materials through stati c and fatigue testing and test development in cooperation with Sandia National Laboratories and wind industry and supplier partners. This report is the latest in a series, giving test results and analysis for the period 2010 - 2015. Program data are compiled in a publicmore » database [1] and other reports and publications given in the cited references. The report begins with an executive summary and introductory material including background discussion of previous related studies. Section 3 describes experimental methods including processing, test methods, instrumentation and test development. Section 4 provides static tension, compression and shear stress - strain properties in three directions using coupons sectioned from a thick infused unidirectional glass/epoxy laminate. The nonlinear, shear dominated static properties were characterized with loading - u nloading - reloading (LUR) tests in tension and compression to increasing load levels, for +-45O laminates. Section 5 explores the origins of tensile fatigue sensitivity in glass fiber dominated laminates with variations in fabric architecture including speci ally prepared fabrics and aligned strand laminates. Several types of resins are considered, with variations in resin toughness and bonding to fibers, as well as cure cycle variations for an epoxy. Conclusions are drawn as to the limits of tensile fatigue r esistance and the effects of resin type and fabric architecture, including the behavior of a commercial aligned glass strand product. Interactions between cyclic fatigue response and creep are addressed for off - axis (+-45O) glass/epoxy laminates in Sectio n 6. The nonlinear fatigue and creep stress - strain and cumulative strain response are characterized in tension and compression as a function of stress level, cycles and cumulative time, using square and sinewave loading over a broad range of frequency. The results are analyzed in terms of the cycles and cumulative time under load. A cumulative strain failure criterion is established, and used to construct shear and tension constant life diagrams (CLD's) with data for nine R - values. The effects of a more duc tile urethne resin are also explored. A previous study of thick adhesives testing is extended to mixed mode fracture mechanics testing in Section 7. Mechanisms of static and fatigue crack extension near the laminate adherend interface are reported in deta il. Data are presented for mixed mode adhesive fracture, compared to mixed mode fracture in ply delamination. Fatigue crack growth exponents are also developed for a mixed mode cracked lap shear coupon. The data for fatigue trends and relative failure stra ins and exponents are compared for various blade component materials in Section 8. The effects of temperature and seawater saturation are considered for selected materials of interest for wind and hydrokinetic turbine blades in Section 9. Section 10 gives detailed conclusions for each section. A cknowledgements The research presented in this report was carried out under Sandia National Laboratories purchase orders 1325028 an d 1543945 between 2010 and 2015, with support from the DOE Wind and Water Technologies Office . In addition to the authors listed, significant contributions were made by Patrick Flaherty, Pancastya Agastra, Michael Schuster, and Michael Voth. Industry m aterials suppliers include Vectorply, Saertex, OCV, AGY, Bayer, Ashland, 3M and Nextel. Industry suppliers with significant contributions to the study were Hexion, PPG, Reichhold, Gurit and NEPTCO. Intentionally Left Blank« less

A study of life prediction differences for a nickel-base Alloy 690 using a threshold and a non-threshold model

NASA Astrophysics Data System (ADS)

Young, B. A.; Gao, Xiaosheng; Srivatsan, T. S.

2009-10-01

In this paper we compare and contrast the crack growth rate of a nickel-base superalloy (Alloy 690) in the Pressurized Water Reactor (PWR) environment. Over the last few years, a preponderance of test data has been gathered on both Alloy 690 thick plate and Alloy 690 tubing. The original model, essentially based on a small data set for thick plate, compensated for temperature, load ratio and stress-intensity range but did not compensate for the fatigue threshold of the material. As additional test data on both plate and tube product became available the model was gradually revised to account for threshold properties. Both the original and revised models generated acceptable results for data that were above 1 × 10 -11 m/s. However, the test data at the lower growth rates were over-predicted by the non-threshold model. Since the original model did not take the fatigue threshold into account, this model predicted no operating stress below which the material would effectively undergo fatigue crack growth. Because of an over-prediction of the growth rate below 1 × 10 -11 m/s, due to a combination of low stress, small crack size and long rise-time, the model in general leads to an under-prediction of the total available life of the components.

Electrostatic apparatus for measurement of microfracture strength

DOEpatents

de Boer, Maarten; Bitsie, Fernando; Jensen, Brian D.

2002-01-01

A new class of materials testing apparatus has been invented. Particularly suited to the measurement of fracture and fatigue properties in the extremely strong materials encountered in microelectromechanical systems, material strains well in excess of 1% can be applied pseudostatically, dynamically, or repetitively by these testers. There are no other practical methods to determine these material properties routinely in a process environment, and few alternatives in any circumstances.

Delivery of cardiopulmonary resuscitation in the microgravity environment

NASA Technical Reports Server (NTRS)

Barratt, M. R.; Billica, R. D.

1992-01-01

The microgravity environment presents several challenges for delivering effective cardiopulmonary resuscitation (CPR). Chest compressions must be driven by muscular force rather than by the weight of the rescuer's upper torso. Airway stabilization is influenced by the neutral body posture. Rescuers will consist of crew members of varying sizes and degrees of physical deconditioning from space flight. Several methods of CPR designed to accommodate these factors were tested in the one G environment, in parabolic flight, and on a recent shuttle flight. Methods: Utilizing study participants of varying sizes, different techniques of CPR delivery were evaluated using a recording CPR manikin to assess adequacy of compressive force and frequency. Under conditions of parabolic flight, methods tested included conventional positioning of rescuer and victim, free floating 'Heimlich type' compressions, straddling the patient with active and passive restraints, and utilizing a mechanical cardiac compression assist device (CCAD). Multiple restrain systems and ventilation methods were also assessed. Results: Delivery of effective CPR was possible in all configurations tested. Reliance on muscular force alone was quickly fatiguing to the rescuer. Effectiveness of CPR was dependent on technique, adequate restraint of the rescuer and patient, and rescuer size and preference. Free floating CPR was adequate but rapidly fatiguing. The CCAD was able to provide adequate compressive force but positioning was problematic. Conclusions: Delivery of effective CPR in microgravity will be dependent on adequate resuer and patient restraint, technique, and rescuer size and preference. Free floating CPR may be employed as a stop gap method until patient restraint is available. Development of an adequate CCAD would be desirable to compensate for the effects of deconditioning.

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2014 CFR

2014-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2012 CFR

2012-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2013 CFR

2013-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2011 CFR

2011-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

Analytical and experimental investigation of fatigue in a sheet specimen with an interference-fit bolt

NASA Technical Reports Server (NTRS)

Crews, J. H., Jr.

1975-01-01

A fatigue analysis, based on finite-element calculations and fatigue tests, was conducted for an aluminum-alloy sheet specimen with a steel interference-fit bolt. The stress analysis of the region near the bolt hole showed that the beneficial effect of an interference-fit bolt can be interpreted as the combined result of two effects: (1) load transfer through the bolt and (2) the compressive interference stresses in the sheet. Results of the fatigue tests show that progressively higher interference levels produced longer fatigue lives. The tests also show that a high level of interference prevents fretting at the bolt-sheet interface and that interferences larger than this level produced little additional improvement in fatigue life.

Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 High Strength Aluminum Alloy

DTIC Science & Technology

2013-06-01

Corrosion Fatigue Corrosion fatigue is defined as the failure of metal due to a cyclical load in combination with exposure to a caustic environment...lifetime is spent creating the crack while the actual crack growth makes up a smaller portion of the total lifetime. With corrosion fatigue however

Fatigue crack growth in an aluminum alloy-fractographic study

NASA Astrophysics Data System (ADS)

Salam, I.; Muhammad, W.; Ejaz, N.

2016-08-01

A two-fold approach was adopted to understand the fatigue crack growth process in an Aluminum alloy; fatigue crack growth test of samples and analysis of fractured surfaces. Fatigue crack growth tests were conducted on middle tension M(T) samples prepared from an Aluminum alloy cylinder. The tests were conducted under constant amplitude loading at R ratio 0.1. The stress applied was from 20,30 and 40 per cent of the yield stress of the material. The fatigue crack growth data was recorded. After fatigue testing, the samples were subjected to detailed scanning electron microscopic (SEM) analysis. The resulting fracture surfaces were subjected to qualitative and quantitative fractographic examinations. Quantitative fracture analysis included an estimation of crack growth rate (CGR) in different regions. The effect of the microstructural features on fatigue crack growth was examined. It was observed that in stage II (crack growth region), the failure mode changes from intergranular to transgranular as the stress level increases. In the region of intergranular failure the localized brittle failure was observed and fatigue striations are difficult to reveal. However, in the region of transgranular failure the crack path is independent of the microstructural features. In this region, localized ductile failure mode was observed and well defined fatigue striations were present in the wake of fatigue crack. The effect of interaction of growing fatigue crack with microstructural features was not substantial. The final fracture (stage III) was ductile in all the cases.

Statistical characterization of the fatigue behavior of composite lamina

NASA Technical Reports Server (NTRS)

Yang, J. N.; Jones, D. L.

1979-01-01

A theoretical model was developed to predict statistically the effects of constant and variable amplitude fatigue loadings on the residual strength and fatigue life of composite lamina. The parameters in the model were established from the results of a series of static tensile tests and a fatigue scan and a number of verification tests were performed. Abstracts for two other papers on the effect of load sequence on the statistical fatigue of composites are also presented.

The neural effects of positively and negatively re-experiencing mental fatigue sensation: a magnetoencephalography study.

PubMed

Ishii, Akira; Ishizuka, Takuya; Muta, Yuki; Tanaka, Masaaki; Yamano, Emi; Watanabe, Yasuyoshi

2018-06-01

Fatigue sensation is an essential biological alarm that urges us to take rest to avoid disrupting homeostasis and thus plays an important role in maintaining well-being. However, there are situations in which the anticipation of unpleasant fatigue sensation undesirably reduces motivation for activity. The aim of this study was to examine whether thinking positively about the fatigue sensation would increase motivation to accomplish the workload. Fourteen healthy male volunteers participated in this study and performed a two-back test for 30 min to induce mental fatigue sensation. After their subjective level of fatigue had recovered to the baseline level, they re-experienced the fatigue sensation experienced in the two-back test positively, negatively, and without any modification (i.e., re-experienced the fatigue sensation as it was). The level of motivation to perform another two-back test they felt during the re-experiencing was assessed. The neural activity related to the re-experiencing was recorded using magnetoencephalography. The level of the motivation to perform another two-back test was increased by positively re-experiencing the fatigue sensation. The increase in delta band power in Brodmann area 7 was positively associated with the increase in motivation. These results show that positive thinking about fatigue sensation can enhance motivation and suggest that this enhanced motivation may have some effects on visual attention system.

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy

PubMed Central

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-01-01

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition. PMID:28774103

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy.

PubMed

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-12-05

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition.

Assessment of Proper Bonding Methods and Mechanical Characterization FPGA CQFPs

NASA Technical Reports Server (NTRS)

Davis, Milton C.

2008-01-01

This presentation discusses fractured leads on field-programmable gate array (FPGA) during flight vibration. Actions taken to determine root cause and resolution of the failure include finite element analysis (FEA) and vibration testing and scanning electron microscopy (with X-ray microanalysis) and energy dispersive spectrometry (SEM/EDS) failure assessment. Bonding methods for surface mount parts is assessed, including critical analysis and assessment of random fatigue damage. Regarding ceramic quad flat pack (CQFP) lead fracture, after disassembling the attitude control electronics (ACE) configuration, photographs showed six leads cracked on FPGA RTSX72SU-1 CQ208B package located on the RWIC card. An identical package (FPGA RTSX32SU-1 CQ208B) mounted on the RWIC did not results in cracked pins due to vibration. FPGA lead failure theories include workmanship issues in the lead-forming, material defect in the leads of the FPGA packages, and the insecure mounting of the board in the card guides, among other theories. Studies were conducted using simple calculations to determine the response and fatigue life of the package. Shorter packages exhibited more response when loaded by out-of-plane displacement of PCB while taller packages exhibit more response when loaded by in-plane acceleration of PCB. Additionally, under-fill did not contribute to reducing stress in leads due to out-of-plane PCB loading or from component twisting, as much as corner bonding. The combination of corner bond and under-fill is best to address mechanical and thermal S/C environment. Test results of bonded parts showed reduced (dampened) amplitude and slightly shifted peaks at the un-bonded natural frequency and an additional response at the bonded frequency. Stress due to PCBB out-of-plane loading was decreased on in the corners when only a corner bond was used. Future work may address CQFP fatigue assessment, including the investigation of discrepancy in predicted fatigue damage, as well as comparing fatigue life and fatigue damage cycle ration computed using FEA and Miner's rule to results from a fatigue assessment software program.

Thermomechanical and bithermal fatigue behavior of cast B1900 + Hf and wrought Haynes 188

NASA Technical Reports Server (NTRS)

Halford, G. R.; Verrilli, M. J.; Kalluri, S.; Ritzert, F. J.; Duckert, R. E.; Holland, F. A.

1992-01-01

A thermomechanical fatigue (TMF) high-temperature life prediction method has been evaluated using the experimental data. Bithermal fatigue (BTF), bithermal creep-fatigue (BTC-F), and TMF experiments were performed using two aerospace structural alloys, cast B1900 + Hf and wrought Haynes 188. The method which is based on the total strain version of strain range partitioning and unified cyclic constitutive modeling requires, as an input, information on the flow and failure behavior of the material of interest. Bithermal temperatures of 483 and 871 C were used for the cast B1900 + Hf nickel-base alloy and 316 and 760 C for the wrought Haynes 188 cobalt-base alloy. Maximum and minimum temperatures were also used in both TMF and BTF tests. Comparisons were made between the results of these tests and isothermal tensile and fatigue test data obtained previously. Qualitative correlations were observed between tensile and isothermal fatigue tests.

The direct-stress fatigue strength of 17S-T aluminum alloy throughout the range from 1/2 to 500,000,000 cycles of stress

NASA Technical Reports Server (NTRS)

Hartmann, E C; Stickley, G W

1942-01-01

Fatigue-test were conducted on six specimens made from 3/4-inch-diameter 17S-T rolled-and-drawn rod for the purpose of obtaining additional data on the fatigue life of the material at stresses up to the static strength. The specimens were tested in direct tension using a stress range from zero to a maximum in tension. A static testing machine was used to apply repeated loads in the case of the first three specimens; the other three specimens were tested in a direct tension-compression fatigue machine. The direct-stress fatigue curve obtained for the material indicates that, in the range of stresses above about two-thirds the tensile strength, the fatigue strength is higher than might be expected by simply extrapolating the ordinary curve of stress plotted against the number of cycles determined at lower stresses.

A proposed USAF fatigue evaluation program based upon recent systems experience

NASA Technical Reports Server (NTRS)

Haviland, G. P.; Purkey, G. F.

1972-01-01

The United States Air Force has published a document entitled Aircraft Structural Integrity Program. One phase of the program is concerned with the fatigue life certification of all types of military aircraft. The document describes the criteria, analyses, and tests that are necessary in order to satisfy the USAF fatigue life requirement. Some recent and valid criticism has been directed toward the document, particularly the fatigue-life requirements contained in it. Some changes are proposed based on surveys conducted in the United States and abroad as well as some recent systems' experience. The surveys covered both military and civilian organizations. The fatigue certification case histories of selected military and commercial aircraft are presented. The design development element tests, preproduction design verification tests, and full-scale fatigue tests of each are described. A brief status report on the revisions to the MIL-A-008860 series specifications is included.

Computational predictive methods for fracture and fatigue

NASA Technical Reports Server (NTRS)

Cordes, J.; Chang, A. T.; Nelson, N.; Kim, Y.

1994-01-01

The damage-tolerant design philosophy as used by aircraft industries enables aircraft components and aircraft structures to operate safely with minor damage, small cracks, and flaws. Maintenance and inspection procedures insure that damages developed during service remain below design values. When damage is found, repairs or design modifications are implemented and flight is resumed. Design and redesign guidelines, such as military specifications MIL-A-83444, have successfully reduced the incidence of damage and cracks. However, fatigue cracks continue to appear in aircraft well before the design life has expired. The F16 airplane, for instance, developed small cracks in the engine mount, wing support, bulk heads, the fuselage upper skin, the fuel shelf joints, and along the upper wings. Some cracks were found after 600 hours of the 8000 hour design service life and design modifications were required. Tests on the F16 plane showed that the design loading conditions were close to the predicted loading conditions. Improvements to analytic methods for predicting fatigue crack growth adjacent to holes, when multiple damage sites are present, and in corrosive environments would result in more cost-effective designs, fewer repairs, and fewer redesigns. The overall objective of the research described in this paper is to develop, verify, and extend the computational efficiency of analysis procedures necessary for damage tolerant design. This paper describes an elastic/plastic fracture method and an associated fatigue analysis method for damage tolerant design. Both methods are unique in that material parameters such as fracture toughness, R-curve data, and fatigue constants are not required. The methods are implemented with a general-purpose finite element package. Several proof-of-concept examples are given. With further development, the methods could be extended for analysis of multi-site damage, creep-fatigue, and corrosion fatigue problems.

Computational predictive methods for fracture and fatigue

NASA Astrophysics Data System (ADS)

Cordes, J.; Chang, A. T.; Nelson, N.; Kim, Y.

1994-09-01

The damage-tolerant design philosophy as used by aircraft industries enables aircraft components and aircraft structures to operate safely with minor damage, small cracks, and flaws. Maintenance and inspection procedures insure that damages developed during service remain below design values. When damage is found, repairs or design modifications are implemented and flight is resumed. Design and redesign guidelines, such as military specifications MIL-A-83444, have successfully reduced the incidence of damage and cracks. However, fatigue cracks continue to appear in aircraft well before the design life has expired. The F16 airplane, for instance, developed small cracks in the engine mount, wing support, bulk heads, the fuselage upper skin, the fuel shelf joints, and along the upper wings. Some cracks were found after 600 hours of the 8000 hour design service life and design modifications were required. Tests on the F16 plane showed that the design loading conditions were close to the predicted loading conditions. Improvements to analytic methods for predicting fatigue crack growth adjacent to holes, when multiple damage sites are present, and in corrosive environments would result in more cost-effective designs, fewer repairs, and fewer redesigns. The overall objective of the research described in this paper is to develop, verify, and extend the computational efficiency of analysis procedures necessary for damage tolerant design. This paper describes an elastic/plastic fracture method and an associated fatigue analysis method for damage tolerant design. Both methods are unique in that material parameters such as fracture toughness, R-curve data, and fatigue constants are not required. The methods are implemented with a general-purpose finite element package. Several proof-of-concept examples are given. With further development, the methods could be extended for analysis of multi-site damage, creep-fatigue, and corrosion fatigue problems.

Is fatigue after work a barrier for leisure-time physical activity? Cross-sectional study among 10,000 adults from the general working population.

PubMed

Bláfoss, Rúni; Micheletti, Jéssica K; Sundstrup, Emil; Jakobsen, Markus D; Bay, Hans; Andersen, Lars L

2018-04-01

In spite of the many health-related benefits of regular physical activity, fatiguing work may be a barrier to performing leisure-time physical activity. This study investigates the association between work-related fatigue and the duration of low- and high-intensity leisure-time physical activity in workers with sedentary and physically demanding jobs. From the 2010 round of the Danish Work Environment Cohort Study, currently employed wage earners from the general working population ( N=10,427) replied to questions about work-related fatigue (predictor) and duration of low- and high-intensity leisure-time physical activity (outcome). Associations were modelled using general linear models controlling for various confounders. Among workers with physically demanding jobs, higher levels of work-related fatigue were associated with gradually lower levels of leisure-time physical activity - for low, moderate and high levels of work-related fatigue the duration of high-intensity leisure-time physical activity was 133 (95% confidence interval (CI) 127-178), 134 (95% CI 109-160) and 113 (95% CI 86-140) min per week, respectively (trend test p<0.001). The duration of high-intensity leisure-time physical activity was lower among older workers (≥50 years) compared to younger workers (<50 years) (132 ± 126 vs 168 ± 150 min per week) ( p<0.0001). The duration of high-intensity leisure-time physical activity gradually decreases with increased work-related fatigue in workers with physically demanding jobs. Older workers perform less high-intensity physical activity than younger workers. Workplaces should consider initiatives to allow workers with physically demanding jobs and older workers to perform physical exercise during working hours and thereby increase physical capacity to meet the job demands.

Novel Electrochemical Test Bench for Evaluating the Functional Fatigue Life of Biomedical Alloys

NASA Astrophysics Data System (ADS)

Ijaz, M. F.; Dubinskiy, S.; Zhukova, Y.; Korobkova, A.; Pustov, Y.; Brailovski, V.; Prokoshkin, S.

2017-08-01

The aim of the present work was first to develop and validate a test bench that simulates the in vitro conditions to which the biomedical implants will be actually subjected in vivo. For the preliminary application assessments, the strain-controlled fatigue tests of biomedically pure Ti and Ti-Nb-Zr alloy in simulated body fluid were undertaken. The in situ open-circuit potential measurements from the test bench demonstrated a strong dependence on the dynamic cycling and kind of material under testing. The results showed that during fatigue cycling, the passive oxide film formed on the surface of Ti-Nb-Zr alloy was more resistant to fatigue degradation when compared with pure Ti. The Ti-Nb-Zr alloy exhibited prolonged fatigue life when compared with pure Ti. The fractographic features of both materials were also characterized using scanning electron microscopy. The electrochemical results and the fractographic evidence confirmed that the prolonged functional fatigue life of the Ti-Nb-Zr alloy is apparently ascribable to the reversible martensitic phase transformation.

Advanced Environmental Barrier Coating Development for SiC/SiC Ceramic Matrix Composites: NASA's Perspectives

NASA Technical Reports Server (NTRS)

Zhu, Dongming

2016-01-01

This presentation reviews NASA environmental barrier coating (EBC) system development programs and the coating materials evolutions for protecting the SiC/SiC Ceramic Matrix Composites in order to meet the next generation engine performance requirements. The presentation focuses on several generations of NASA EBC systems, EBC-CMC component system technologies for SiC/SiC ceramic matrix composite combustors and turbine airfoils, highlighting the temperature capability and durability improvements in simulated engine high heat flux, high pressure, high velocity, and with mechanical creep and fatigue loading conditions. The current EBC development emphasis is placed on advanced NASA 2700F candidate environmental barrier coating systems for SiC/SiC CMCs, their performance benefits and design limitations in long-term operation and combustion environments. Major technical barriers in developing environmental barrier coating systems, the coating integrations with next generation CMCs having the improved environmental stability, erosion-impact resistance, and long-term fatigue-environment system durability performance are described. The research and development opportunities for advanced turbine airfoil environmental barrier coating systems by utilizing improved compositions, state-of-the-art processing methods, and simulated environment testing and durability modeling are discussed.

Empowering a healthy practice environment.

PubMed

Kushner, Jodi; Ruffin, Tasha

2015-03-01

This article provides frontline nurses a tool kit so they can advocate a healthy practice environment. The healthy nurse, healthy work hours, job satisfaction, adequate sleep, power naps at work, and balancing family/work are discussed. The overweight nurse, nurse fatigue, compassion fatigue, shift work sleep disorder, and role strain are discussed as barriers to a healthy practice environment. Case reports with analysis and recommendations are discussed to overcome these barriers. Resources are presented for frontline nurses to develop a tool kit for transforming their environment to a healthy practice environment and to empower them to become healthy nurses. Copyright © 2015 Elsevier Inc. All rights reserved.

Taltirelin alleviates fatigue-like behavior in mouse models of cancer-related fatigue.

PubMed

Dougherty, John P; Wolff, Brian S; Cullen, Mary J; Saligan, Leorey N; Gershengorn, Marvin C

2017-10-01

Fatigue affects most cancer patients and has numerous potential causes, including cancer itself and cancer treatment. Cancer-related fatigue (CRF) is not relieved by rest, can decrease quality of life, and has no FDA-approved therapy. Thyrotropin-releasing hormone (TRH) has been proposed as a potential novel treatment for CRF, but its efficacy against CRF remains largely untested. Thus, we tested the TRH analog, taltirelin (TAL), in mouse models of CRF. To model fatigue, we used a mouse model of chemotherapy, a mouse model of radiation therapy, and mice bearing colon 26 carcinoma tumors. We used the treadmill fatigue test to assess fatigue-like behavior after treatment with TAL. Additionally, we used wild-type and TRH receptor knockout mice to determine which TRH receptor was necessary for the actions of TAL. Tumor-bearing mice displayed muscle wasting and all models caused fatigue-like behavior, with mice running a shorter distance in the treadmill fatigue test than controls. TAL reversed fatigue-like behavior in all three models and the mouse TRH 1 receptor was necessary for the effects of TAL. These data suggest that TAL may be useful in alleviating fatigue in all cancer patients and provide further support for evaluating TAL as a potential therapy for CRF in humans. Published by Elsevier Ltd.

The effect of matrix mechanical properties on (0)8 unidirectional SiC/Ti composite fatigue resistance

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Gayda, J.; Lerch, B. A.; Halford, G. R.

1991-01-01

The relationship between constituent and MMC properties in fatigue loading is investigated with low-cycle fatigue-resistance testing of an alloy Ti-15-3 matrix reinforced with SiC SCS-6 fibers. The fabrication of the composite is described, and specimens are generated that are weak and ductile (WD), strong and moderately ductile (SM), or strong and brittle (SB). Strain is measured during MMC fatigue tests at a constant load amplitude with a load-controlled waveform and during matrix-alloy fatigue tests at a constant strain amplitude using a strain-controlled waveform. The fatigue resistance of the (0)8 SiC/Ti-15-3 composite is found to be slightly influenced by matrix mechanical properties, and the composite- and matrix-alloy fatigue lives are not correlated. This finding is suggested to relate to the different crack-initiation and -growth processes in MMCs and matrix alloys.

The effect of porosity and gamma-gamma' eutectic content on the low cycle fatigue behavior of hydrogen-charged PWA-1480

NASA Technical Reports Server (NTRS)

Gayda, John; Dreshfield, Robert L.; Gabb, Timothy P.

1991-01-01

Single crystal superalloys such as PWA 1480 are considered for turbopump blades in the main engines of the space shuttle. As fatigue resistance in a hydrogen environment is a key issue in this application, a study of the effect of porosity and gamma-gamma' eutectic content on the fatigue life of a hydrogen-charged PWA 1480 was performed. Porosity and eutectic were linked to fatigue initiation, and therefore reduction of either of both may be one means to improve fatigue life of PWA 1480 when hydrogen is present.

Room Temperature and Elevated Temperature Composite Sandwich Joint Testing

NASA Technical Reports Server (NTRS)

Walker, Sandra P.

1998-01-01

Testing of composite sandwich joint elements has been completed to verify the strength capacity of joints designed to carry specified running loads representative of a high speed civil transport wing. Static tension testing at both room and an elevated temperature of 350 F and fatigue testing at room temperature were conducted to determine strength capacity, fatigue life, and failure modes. Static tension test results yielded failure loads above the design loads for the room temperature tests, confirming the ability of the joint concepts tested to carry their design loads. However, strength reductions as large as 30% were observed at the elevated test temperature, where all failure loads were below the room temperature design loads for the specific joint designs tested. Fatigue testing resulted in lower than predicted fatigue lives.

Influence of gaseous hydrogen on the mechanical properties of high temperature alloys

NASA Technical Reports Server (NTRS)

1976-01-01

Tensile tests of six nickel-base and one cobalt-base alloy were conducted in 34.5 MN/sq m helium and hydrogen environments at temperatures from 297 K to 1,088 K. Mechanical properties tests of the nickel-base alloy MAR M-246 (Hf modified), in two cast conditions, were conducted in gaseous environments at temperatures from 297 K to 1,144 K and pressures from one atmosphere to 34.5 MN/sq m. The objective of this program was to obtain the mechanical properties of the various alloys proposed for use in space propulsion systems in a pure hydrogen environment at different temperatures and to compare with the mechanical properties in helium at the same conditions. All testing was conducted on solid specimens exposed to external gaseous pressure. Smooth and notched tensile properties were determined using ASTM tensile testing techniques, and creep-rupture life was determined using ASTM creep-rupture techniques. Low-cycle fatigue life was established by constant total strain and constant stress testing using smooth specimens and a closed-loop test machine.

Reviews on factors affecting fatigue behavior of high-Mn steels

NASA Astrophysics Data System (ADS)

Kim, Sangshik; Jeong, Daeho; Sung, Hyokyung

2018-01-01

A variety of factors affect the fatigue behavior of high-Mn steels, which include both extrinsic (i.e., loading type, R ratio, specimen type, surface condition, temperature, and environment) and intrinsic (i.e., chemical composition, grain size, microstructure, stacking fault energy) factors. Very often, the influence of extrinsic factors on the fatigue behavior is even greater than that of intrinsic factors, misleading the interpretation of fatigue data. The metallurgical factors influence the initiation and propagation behaviors of fatigue by altering the characteristics of slip that is prerequisite for fatigue damage accumulation. It is however not easy to separate the effect of each factor since they affect the fatigue behavior of high-Mn steels in complex and synergistic way. In this review, the fatigue data of high-Mn steels are summarized and the factors complicating the interpretation are discussed.

Fatigue acceptance test limit criterion for larger diameter rolled thread fasteners

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kephart, A.R.

1997-05-01

This document describes a fatigue lifetime acceptance test criterion by which studs having rolled threads, larger than 1.0 inches in diameter, can be assured to meet minimum quality attributes associated with a controlled rolling process. This criterion is derived from a stress dependent, room temperature air fatigue database for test studs having a 0.625 inch diameter threads of Alloys X-750 HTH and direct aged 625. Anticipated fatigue lives of larger threads are based on thread root elastic stress concentration factors which increase with increasing thread diameters. Over the thread size range of interest, a 30% increase in notch stress ismore » equivalent to a factor of five (5X) reduction in fatigue life. The resulting diameter dependent fatigue acceptance criterion is normalized to the aerospace rolled thread acceptance standards for a 1.0 inch diameter, 0.125 inch pitch, Unified National thread with a controlled Root radius (UNR). Testing was conducted at a stress of 50% of the minimum specified material ultimate strength, 80 Ksi, and at a stress ratio (R) of 0.10. Limited test data for fastener diameters of 1.00 to 2.25 inches are compared to the acceptance criterion. Sensitivity of fatigue life of threads to test nut geometry variables was also shown to be dependent on notch stress conditions. Bearing surface concavity of the compression nuts and thread flank contact mismatch conditions can significantly affect the fastener fatigue life. Without improved controls these conditions could potentially provide misleading acceptance data. Alternate test nut geometry features are described and implemented in the rolled thread stud specification, MIL-DTL-24789(SH), to mitigate the potential effects on fatigue acceptance data.« less

Fatigue test results of the rotating steel blades of steam turbine K-25-0.6 GEO with ion-plasma coating

NASA Astrophysics Data System (ADS)

Kachalin, G. V.; Mednikov, A. F.; Tkhabisimov, A. B.; Arkad'ev, D. A.; Temkin, S. G.; Senina, N. A.

2016-12-01

Fatigue test results of the rotating steel blades of the fourth stage of the K-25-0.6 low pressure cylinder Geo steam turbine manufactured in the Kaluga Turbine Plant (hereinafter, KTP) with the ion-plasma coating were presented. Coating formation was carried out at the National Research University (MPEI) on the Gefest vacuum pilot plant by the magnetron sputtering method. Characteristics of the obtained coating were analyzed with the use of the scientific-research equipment of the National Research University (MPEI). Fatigue tests of the rotating blades and determination of the fatigue strength of the material with the ion-plasma coating were carried out on the electrodynamic vibration machines VEDS-400A in the KTP structural laboratory. The following characteristics were obtained after tests: Ti-TiN composition, 10-11 μm thickness, 1200 HV 0.05 microhardness. Fatigue tests showed that destruction, regardless of availability or nonavailability of the coating, took place by cross-section in the root zone both on the leading and trailing edges of the blade, i.e., in the most stressed zones. It was found out that the maximum stresses during tests were revealed in the root section along the trailing edge on the blade pressure side, and the less stresses were on the leading edge. Fatigue strength of the working blades after coating formation increased by 12% minimum. Results of the fatigue tests prove the previously obtained data concerning 10-12% increase of the fatigue strength of the blade steel with the ion-plasma coating and allow claiming that the process of their formation exerts the positive influence on the fatigue characteristics of the blade materials.

Study on Determination Method of Fatigue Testing Load for Wind Turbine Blade

NASA Astrophysics Data System (ADS)

Liao, Gaohua; Wu, Jianzhong

2017-07-01

In this paper, the load calculation method of the fatigue test was studied for the wind turbine blade under uniaxial loading. The characteristics of wind load and blade equivalent load were analyzed. The fatigue property and damage theory of blade material were studied. The fatigue load for 2MW blade was calculated by Bladed, and the stress calculated by ANSYS. Goodman modified exponential function S-N curve and linear cumulative damage rule were used to calculate the fatigue load of wind turbine blades. It lays the foundation for the design and experiment of wind turbine blade fatigue loading system.

Creep-Fatigue Damage Investigation and Modeling of Alloy 617 at High Temperatures

NASA Astrophysics Data System (ADS)

Tahir, Fraaz

The Very High Temperature Reactor (VHTR) is one of six conceptual designs proposed for Generation IV nuclear reactors. Alloy 617, a solid solution strengthened Ni-base superalloy, is currently the primary candidate material for the tubing of the Intermediate Heat Exchanger (IHX) in the VHTR design. Steady-state operation of the nuclear power plant at elevated temperatures leads to creep deformation, whereas loading transients including startup and shutdown generate fatigue. A detailed understanding of the creep-fatigue interaction in Alloy 617 is necessary before it can be considered as a material for nuclear construction in ASME Boiler and Pressure Vessel Code. Current design codes for components undergoing creep-fatigue interaction at elevated temperatures require creep-fatigue testing data covering the entire range from fatigue-dominant to creep-dominant loading. Classical strain-controlled tests, which produce stress relaxation during the hold period, show a saturation in cycle life with increasing hold periods due to the rapid stress-relaxation of Alloy 617 at high temperatures. Therefore, applying longer hold time in these tests cannot generate creep-dominated failure. In this study, uniaxial isothermal creep-fatigue tests with non-traditional loading waveforms were designed and performed at 850 and 950°C, with an objective of generating test data in the creep-dominant regime. The new loading waveforms are hybrid strain-controlled and force-controlled testing which avoid stress relaxation during the creep hold. The experimental data showed varying proportions of creep and fatigue damage, and provided evidence for the inadequacy of the widely-used time fraction rule for estimating creep damage under creep-fatigue conditions. Micro-scale damage features in failed test specimens, such as fatigue cracks and creep voids, were quantified using a Scanning Electron Microscope (SEM) to find a correlation between creep and fatigue damage. Quantitative statistical imaging analysis showed that the microstructural damage features (cracks and voids) are correlated with a new mechanical driving force parameter. The results from this image-based damage analysis were used to develop a phenomenological life-prediction methodology called the effective time fraction approach. Finally, the constitutive creep-fatigue response of the material at 950°C was modeled using a unified viscoplastic model coupled with a damage accumulation model. The simulation results were used to validate an energy-based constitutive life-prediction model, as a mechanistic model for potential component and structure level creep-fatigue analysis.

Multiaxial Fatigue Life Prediction Based on Nonlinear Continuum Damage Mechanics and Critical Plane Method

NASA Astrophysics Data System (ADS)

Wu, Z. R.; Li, X.; Fang, L.; Song, Y. D.

2018-04-01

A new multiaxial fatigue life prediction model has been proposed in this paper. The concepts of nonlinear continuum damage mechanics and critical plane criteria were incorporated in the proposed model. The shear strain-based damage control parameter was chosen to account for multiaxial fatigue damage under constant amplitude loading. Fatigue tests were conducted on nickel-based superalloy GH4169 tubular specimens at the temperature of 400 °C under proportional and nonproportional loading. The proposed method was checked against the multiaxial fatigue test data of GH4169. Most of prediction results are within a factor of two scatter band of the test results.

Study of fatigue behavior of longitudinal welded pipes

NASA Astrophysics Data System (ADS)

Simion, P.; Dia, V.; Istrate, B.; Hrituleac, G.; Hrituleac, I.; Munteanu, C.

2016-08-01

During transport and storage of the various fluids, welded pipes are subjected to cyclic loading due to pressure fluctuations that often exceed the prescribed values for normal operation. These cyclic loading can significantly reduce the life of the pipes; as a result the design should be based on the fatigue strength not only on static resistance. In general the fatigue strength of pipes is dependent by strength, pipe geometry and surface quality. In case of the electric longitudinal welded pipes, the fatigue strength is significantly limited by concentration of residual stress and the size of existing defects in the weld seam. This paper presents the fatigue behaviour of the electric welded pipes by high frequency, under conditions that simulate real operating conditions pipes. Fatigue testing was performed on welded pipes made of micro alloyed carbon steels. Some of these pipes were previously subjected to a heat treatment of normalization, in order to also determine the influence of heat treatment on the fatigue strength of welded pipes. To determine and correlate the different factors affecting the fatigue strength, welded pipes were also subjected to various tests: tensile tests, impact tests, measurement of micro hardness, microstructural analysis by optical microscopy and scanning electron microscopy.

Indentation hardness: A simple test that correlates with the dissipated-energy predictor for fatigue-life in bovine pericardium membranes for bioprosthetic heart valves.

PubMed

Tobaruela, Almudena; Rojo, Francisco Javier; García Paez, José María; Bourges, Jean Yves; Herrero, Eduardo Jorge; Millán, Isabel; Alvarez, Lourdes; Cordon, Ángeles; Guinea, Gustavo V

2016-08-01

The aim of this study was to evaluate the variation of hardness with fatigue in calf pericardium, a biomaterial commonly used in bioprosthetic heart valves, and its relationship with the energy dissipated during the first fatigue cycle that has been shown to be a predictor of fatigue-life (García Páez et al., 2006, 2007; Rojo et al., 2010). Fatigue tests were performed in vitro on 24 pericardium specimens cut in a root-to-apex direction. The specimens were subjected to a maximum stress of 1MPa in blocks of 10, 25, 50, 100, 250, 500, 1000 and 1500 cycles. By means of a modified Shore A hardness test procedure, the hardness of the specimen was measured before and after fatigue tests. Results showed a significant correlation of such hardness with fatigue performance and with the energy dissipated in the first cycle of fatigue, a predictor of pericardium durability. The study showed indentation hardness as a simple and reliable indicator of mechanical performance, one which could be easily implemented in improving tissue selection. Copyright © 2016 Elsevier Ltd. All rights reserved.

Analysis of the Mechanical Behavior, Creep Resistance and Uniaxial Fatigue Strength of Martensitic Steel X46Cr13

PubMed Central

Brnic, Josip; Krscanski, Sanjin; Lanc, Domagoj; Brcic, Marino; Turkalj, Goran; Canadija, Marko; Niu, Jitai

2017-01-01

The article deals with the analysis of the mechanical behavior at different temperatures, uniaxial creep and uniaxial fatigue of martensitic steel X46Cr13 (1.4034, AISI 420). For the purpose of considering the aforementioned mechanical behavior, as well as determining the appropriate resistance to creep and fatigue strength levels, numerous uniaxial tests were carried out. Tests related to mechanical properties performed at different temperatures are presented in the form of engineering stress-strain diagrams. Short-time creep tests performed at different temperatures and different stress levels are presented in the form of creep curves. Fatigue tests carried out at stress ratios R=0.25 and R=−1 are shown in the form of S–N (fatigue) diagrams. The finite fatigue regime for each of the mentioned stress ratios is modeled by an inclined log line, while the infinite fatigue regime is modeled by a horizontal line, which represents the fatigue limit of the material and previously was calculated by the modified staircase method. Finally, the fracture toughness has been calculated based on the Charpy V-notch impact energy. PMID:28772749

Developing measures of fatigue using an alcohol comparison to validate the effects of fatigue on performance.

PubMed

Williamson, A M; Feyer, A M; Mattick, R P; Friswell, R; Finlay-Brown, S

2001-05-01

The effects of 28 h of sleep deprivation were compared with varying doses of alcohol up to 0.1% blood alcohol concentration (BAC) in the same subjects. The study was conducted in the laboratory. Twenty long-haul truck drivers and 19 people not employed as professional drivers acted as subjects. Tests were selected that were likely to be affected by fatigue, including simple reaction time, unstable tracking, dual task, Mackworth clock vigilance test, symbol digit coding, visual search, sequential spatial memory and logical reasoning. While performance effects were seen due to alcohol for all tests, sleep deprivation affected performance on most tests, but had no effect on performance on the visual search and logical reasoning tests. Some tests showed evidence of a circadian rhythm effect on performance, in particular, simple reaction time, dual task, Mackworth clock vigilance, and symbol digit coding, but only for response speed and not response accuracy. Drivers were slower but more accurate than controls on the symbol digit test, suggesting that they took a more conservative approach to performance of this test. This study demonstrated which tests are most sensitive to sleep deprivation and fatigue. The study therefore has established a set of tests that can be used in evaluations of fatigue and fatigue countermeasures.

Evaluating cyclic fatigue of sealants during outdoor testing

Treesearch

R. Sam Williams; Steven Lacher; Corey Halpin; Christopher White

2009-01-01

A computer-controlled test apparatus (CCTA) and other instrumentation for subjecting sealant specimens to cyclic fatigue during outdoor exposure was developed. The CCTA enables us to use weather-induced conditions to cyclic fatigue specimens and to conduct controlled tests in-situ during the outdoor exposure. Thermally induced dimensional changes of an aluminum bar...

A Full-Scale Fatigue Test of 9-m CX-100 Wind Turbine Blades

DTIC Science & Technology

2011-09-01

A Full-Scale Fatigue Test of 9-m CX-100 Wind Turbine Blades G. PARK, K. M. FARINHOLT, S. G. TAYLOR and C. R. FARRAR ABSTRACT This paper...presents the SHM result of a 9m CX-100 wind turbine blade under full- scale fatigue loads. The test was performed at the National Renewable Energy...surface of the blade. The blade underwent fatigue excitation at 1.8 Hz for defined intervals, and data from the sensors were collected between and

Method of Fatigue-Life Prediction for an Asphalt Mixture Based on the Plateau Value of Permanent Deformation Ratio.

PubMed

Sun, Yazhen; Fang, Chenze; Wang, Jinchang; Yuan, Xuezhong; Fan, Dong

2018-05-03

Laboratory predictions for the fatigue life of an asphalt mixture under cyclic loading based on the plateau value (PV) of the permanent deformation ratio (PDR) were carried out by three-point bending fatigue tests. The influence of test conditions on the recovery ratio of elastic deformation (RRED), the permanent deformation (PD) and PDR, and the trends of RRED, PD, and PDR were studied. The damage variable was defined by using PDR, and the relation of the fatigue life to PDR was determined by analyzing the damage evolution process. The fatigue equation was established based on the PV of PDR and the fatigue life was predicted by analyzing the relation of the fatigue life to the PV. The results show that the RRED decreases with the increase of the number of loading cycles, and the elastic recovery ability of the asphalt mixture gradually decreases. The two mathematical models proposed are based on the change laws of the RRED, and the PD can well describe the change laws. The RRED or the PD cannot well predict the fatigue life because they do not change monotonously with the fatigue life, and one part of the deformation causes the damage and the other part causes the viscoelastic deformation. The fatigue life decreases with the increase of the PDR. The average PDR in the second stage is taken as the PV, and the fatigue life decreases in a power law with the increase of the PV. The average relative error of the fatigue life predicted by the fatigue equation to the test fatigue life is 5.77%. The fatigue equation based on PV can well predict the fatigue life.

The Growth of Small Corrosion Fatigue Cracks in Alloy 7075

NASA Technical Reports Server (NTRS)

Piascik, Robert S.

2015-01-01

The corrosion fatigue crack growth characteristics of small (greater than 35 micrometers) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500×) crack length measurements in laboratory air and 1% sodium chloride (NaCl) environments. To quantify the "small crack effect" in the corrosive environment, the corrosion fatigue crack propagation behavior of small cracks is compared to long through-the-thickness cracks grown under identical experimental conditions. In salt water, long crack constant K(sub max) growth rates are similar to small crack da/dN.

The Growth of Small Corrosion Fatigue Cracks in Alloy 7075

NASA Technical Reports Server (NTRS)

Piascik, R. S.

2001-01-01

The corrosion fatigue crack growth characteristics of small (less than 35 microns) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500X) crack length measurements in laboratory air and 1% NaCl environments. To quantify the "small crack effect" in the corrosive environment, the corrosion fatigue crack propagation behavior of small cracks is compared to long through-the-thickness cracks grown under identical experimental conditions. In salt water, long crack constant K(sub max) growth rates are similar to small crack da/dN.

Linking asphalt binder fatigue to asphalt mixture fatigue performance using viscoelastic continuum damage modeling

NASA Astrophysics Data System (ADS)

Safaei, Farinaz; Castorena, Cassie; Kim, Y. Richard

2016-08-01

Fatigue cracking is a major form of distress in asphalt pavements. Asphalt binder is the weakest asphalt concrete constituent and, thus, plays a critical role in determining the fatigue resistance of pavements. Therefore, the ability to characterize and model the inherent fatigue performance of an asphalt binder is a necessary first step to design mixtures and pavements that are not susceptible to premature fatigue failure. The simplified viscoelastic continuum damage (S-VECD) model has been used successfully by researchers to predict the damage evolution in asphalt mixtures for various traffic and climatic conditions using limited uniaxial test data. In this study, the S-VECD model, developed for asphalt mixtures, is adapted for asphalt binders tested under cyclic torsion in a dynamic shear rheometer. Derivation of the model framework is presented. The model is verified by producing damage characteristic curves that are both temperature- and loading history-independent based on time sweep tests, given that the effects of plasticity and adhesion loss on the material behavior are minimal. The applicability of the S-VECD model to the accelerated loading that is inherent of the linear amplitude sweep test is demonstrated, which reveals reasonable performance predictions, but with some loss in accuracy compared to time sweep tests due to the confounding effects of nonlinearity imposed by the high strain amplitudes included in the test. The asphalt binder S-VECD model is validated through comparisons to asphalt mixture S-VECD model results derived from cyclic direct tension tests and Accelerated Loading Facility performance tests. The results demonstrate good agreement between the asphalt binder and mixture test results and pavement performance, indicating that the developed model framework is able to capture the asphalt binder's contribution to mixture fatigue and pavement fatigue cracking performance.

Advanced Gear Alloys for Ultra High Strength Applications

NASA Technical Reports Server (NTRS)

Shen, Tony; Krantz, Timothy; Sebastian, Jason

2011-01-01

Single tooth bending fatigue (STBF) test data of UHS Ferrium C61 and C64 alloys are presented in comparison with historical test data of conventional gear steels (9310 and Pyrowear 53) with comparable statistical analysis methods. Pitting and scoring tests of C61 and C64 are works in progress. Boeing statistical analysis of STBF test data for the four gear steels (C61, C64, 9310 and Pyrowear 53) indicates that the UHS grades exhibit increases in fatigue strength in the low cycle fatigue (LCF) regime. In the high cycle fatigue (HCF) regime, the UHS steels exhibit better mean fatigue strength endurance limit behavior (particularly as compared to Pyrowear 53). However, due to considerable scatter in the UHS test data, the anticipated overall benefits of the UHS grades in bending fatigue have not been fully demonstrated. Based on all the test data and on Boeing s analysis, C61 has been selected by Boeing as the gear steel for the final ERDS demonstrator test gearboxes. In terms of potential follow-up work, detailed physics-based, micromechanical analysis and modeling of the fatigue data would allow for a better understanding of the causes of the experimental scatter, and of the transition from high-stress LCF (surface-dominated) to low-stress HCF (subsurface-dominated) fatigue failure. Additional STBF test data and failure analysis work, particularly in the HCF regime and around the endurance limit stress, could allow for better statistical confidence and could reduce the observed effects of experimental test scatter. Finally, the need for further optimization of the residual compressive stress profiles of the UHS steels (resulting from carburization and peening) is noted, particularly for the case of the higher hardness C64 material.

Fatigue testing of energy storing prosthetic feet.

PubMed

Toh, S L; Goh, J C; Tan, P H; Tay, T E

1993-12-01

This paper describes a simple approach to the fatigue testing of prosthetic feet. A fatigue testing machine for prosthetic feet was designed as part of the programme to develop an energy storing prosthetic foot (ESPF). The fatigue tester does not simulate the loading pattern on the foot during normal walking. However, cyclic vertical loads are applied to the heel and forefoot during heel-strike and toe-off respectively, for 500,000 cycles. The maximum load applied was chosen to be 1.5 times that applied by the bodyweight of the amputee and the test frequency was chosen to be 2 Hz to shorten the test duration. Four prosthetic feet were tested: two Lambda feet (a newly developed ESPF), a Kingsley SACH foot and a Proteor SACH foot. It was found that the Lambda feet have very good fatigue properties. The Kingsley SACH foot performed better than the Proteor model, with no signs of wear at the heel. The results obtained using the simple approach was found to be comparable to the results from more complex fatigue machines which simulate the load pattern during normal walking. This suggests that simple load simulating machines, which are less costly and require less maintenance, are useful substitutes in studying the fatigue properties of prosthetic feet.

A comparison of fatigue life prediction methodologies for rotorcraft

NASA Technical Reports Server (NTRS)

Everett, R. A., Jr.

1990-01-01

Because of the current U.S. Army requirement that all new rotorcraft be designed to a 'six nines' reliability on fatigue life, this study was undertaken to assess the accuracy of the current safe life philosophy using the nominal stress Palmgrem-Miner linear cumulative damage rule to predict the fatigue life of rotorcraft dynamic components. It has been shown that this methodology can predict fatigue lives that differ from test lives by more than two orders of magnitude. A further objective of this work was to compare the accuracy of this methodology to another safe life method called the local strain approach as well as to a method which predicts fatigue life based solely on crack growth data. Spectrum fatigue tests were run on notched (k(sub t) = 3.2) specimens made of 4340 steel using the Felix/28 tests fairly well, being slightly on the unconservative side of the test data. The crack growth method, which is based on 'small crack' crack growth data and a crack-closure model, also predicted the fatigue lives very well with the predicted lives being slightly longer that the mean test lives but within the experimental scatter band. The crack growth model was also able to predict the change in test lives produced by the rainflow reconstructed spectra.

Investigation of the effect of vacuum environment on the fatigue and fracture behavior of 7075-T6.

NASA Technical Reports Server (NTRS)

Hudson, C. M.

1972-01-01

Axial-load fatigue-life, fatigue-crack propagation, and fracture-toughness experiments were conducted on sheet specimens made of 7075-T6 aluminum alloy. These experiments were conducted at air pressures ranging from 101 kN/sq m to 7 micronewtons/sq m to determine the effect of air pressure on fatigue behavior. Analysis of the results from the fatigue-life experiments indicated that for a given stress level, the lower the air pressure was the longer the fatigue life. At a pressure of 7 micronewtons/sq m, fatigue lives were 15 to 30 times longer than at 101 kN/sq m. Analysis of the results from the fatigue-crack-growth experiments indicates that at low values of stress-intensity range, the fatigue-crack-growth rates were approximately twice as high at atmospheric pressure as in vacuum. However, at higher values of stress-intensity range, the fatigue-crack-growth rates were nominally the same in vacuum and at atmospheric pressure.

An Experimental Evaluation of the Effect of Hole Fabrication/Treatment Techniques on Residual Strength and Fatigue Life of Polycarbonate Specimens with Holes

DTIC Science & Technology

1993-08-01

34The Effect of Dimpling on the Fatigue Strength of Loaded Holes in a Corrosive Environment," Experimental Techniques, Vol. 9, September 1985, 33-36. 34...Expansion on the Fatigue Behavior of 7079-T652 Alluminium [sic] Alloy," NLR TR 74016 U, National Aerospace Laboratory (NLR), Amsterdam, The

Ultrasonic fatigue of SiC particle reinforced aluminum in the VHCF-regime

NASA Astrophysics Data System (ADS)

Wolf, M.; Wagner, G.; Eifler, D.

At the WKK ultrasonic testing facilities (UTF) are used to perform fatigue experiments in the VHCF regime with a frequency of 20 kHz. These systems allow an on-line characterization of the actual fatigue state by changes of different process parameters such as generator power, displacement, temperature or frequency-response characteristic. Moreover the experiments can be interrupted at user defined events in order to investigate variations of the surface microstructure or changes in the electrical resistance of the specimens. The fatigue tests were realized as load increase tests as well as constant amplitude tests.

Compassion fatigue among nurses working with older adults.

PubMed

Kolthoff, Kay L; Hickman, Susan E

Nurses who care for older patients are exposed to significant suffering and loss that can lead to the development of compassion fatigue and burnout. An exploratory descriptive study was conducted to assess compassion fatigue, burnout, and compassion satisfaction in a group of 42 nurses who worked on a geriatric medicine unit using the Professional Quality of Life (ProQOL) compassion satisfaction and compassion fatigue 5 scale. Nurses reported average levels of compassion fatigue, burnout, and compassion satisfaction. However, new nurses reported higher levels of compassion fatigue (p < .01) and burnout (p = .02) than experienced nurses. Findings suggest the need to purposely build a supportive environment that focuses on new nurses to reduce compassion fatigue and burnout while enhancing compassion satisfaction. Copyright © 2016 Elsevier Inc. All rights reserved.

Monotony of road environment and driver fatigue: a simulator study.

PubMed

Thiffault, Pierre; Bergeron, Jacques

2003-05-01

Studies have shown that drowsiness and hypovigilance frequently occur during highway driving and that they may have serious implications in terms of accident causation. This paper focuses on the task induced factors that are involved in the development of these phenomena. A driving simulator study was conducted in order to evaluate the impact of the monotony of roadside visual stimulation using a steering wheel movement (SWM) analysis procedure. Fifty-six male subjects each drove during two different 40-min periods. In one case, roadside visual stimuli were essentially repetitive and monotonous, while in the other one, the environment contained disparate visual elements aiming to disrupt monotony without changing road geometry. Subject's driving performance was compared across these conditions in order to determine whether disruptions of monotony can have a positive effect and help alleviate driver fatigue. Results reveal an early time-on-task effect on driving performance for both driving periods and more frequent large SWM when driving in the more monotonous road environment, which implies greater fatigue and vigilance decrements. Implications in terms of environmental countermeasures for driver fatigue are discussed.

Overview of the Space Launch System Transonic Buffet Environment Test Program

NASA Technical Reports Server (NTRS)

Piatak, David J.; Sekula, Martin K.; Rausch, Russ D.; Florance, James R.; Ivanco, Thomas G.

2015-01-01

Fluctuating aerodynamic loads are a significant concern for the structural design of a launch vehicle, particularly while traversing the transonic flight environment. At these trajectory conditions, unsteady aerodynamic pressures can excite the vehicle dynamic modes of vibration and result in high structural bending moments and vibratory environments. To ensure that vehicle structural components and subsystems possess adequate strength, stress, and fatigue margins in the presence of buffet and other environments, buffet forcing functions are required to conduct the coupled load analysis of the launch vehicle. The accepted method to obtain these buffet forcing functions is to perform wind-tunnel testing of a rigid model that is heavily instrumented with unsteady pressure transducers designed to measure the buffet environment within the desired frequency range. Two wind-tunnel tests of a 3 percent scale rigid buffet model have been conducted at the Langley Research Center Transonic Dynamics Tunnel (TDT) as part of the Space Launch System (SLS) buffet test program. The SLS buffet models have been instrumented with as many as 472 unsteady pressure transducers to resolve the buffet forcing functions of this multi-body configuration through integration of the individual pressure time histories. This paper will discuss test program development, instrumentation, data acquisition, test implementation, data analysis techniques, and several methods explored to mitigate high buffet environment encountered during the test program. Preliminary buffet environments will be presented and compared using normalized sectional buffet forcing function root-meansquared levels along the vehicle centerline.

Crack propagation analysis and fatigue life prediction for structural alloy steel based on metal magnetic memory testing

NASA Astrophysics Data System (ADS)

Ni, Chen; Hua, Lin; Wang, Xiaokai

2018-09-01

To monitor the crack propagation and predict the fatigue life of ferromagnetic material, the metal magnetic memory (MMM) testing was carried out to the single edge notched specimen made from structural alloy steel under three-point bending fatigue experiment in this paper. The variation of magnetic memory signal Hp (y) in process of fatigue crack propagation was investigated. The gradient K of Hp (y) was investigated and compared with the stress of specimen obtained by finite element analysis. It indicated that the gradient K can qualitatively reflect the distribution and variation of stress. The maximum gradient Kmax and crack size showed a good linear relationship, which indicated that the crack propagation can be estimated by MMM testing. Furthermore, the damage model represented by magnetic memory characteristic was created and a fatigue life prediction method was developed. The fatigue life can be evaluated by the relationship between damage parameter and normalized life. The method was also verified by another specimen. Because of MMM testing, it provided a new approach for predicting fatigue life.

Preliminary Study on Fatigue Strengths of Fretted Ti-48Al-2Cr-2Nb

NASA Technical Reports Server (NTRS)

Miyoshi, Kazuhisa; Lerch, Bradley A.; Draper, Susan L.

2002-01-01

The fatigue behavior (stress-life curve) of gamma titanium aluminide (Ti-48Al-2Cr-2Nb, atomic percent) was examined by conducting two tests: first, a fretting wear test with a fatigue specimen in contact with a typical nickel-based superalloy contact pad in air at temperatures of 296 and 823 K and second, a high-cycle fatigue test of the prefretted Ti-48Al-2Cr-2Nb fatigue specimen at 923 K. Reference high-cycle fatigue tests were also conducted with unfretted Ti-48Al-2Cr-2Nb specimens at 923 K. All Ti-48Al-2Cr-2Nb fatigue specimens were machined from cast slabs. The results indicate that the stress-life results for the fretted Ti-48Al-2Cr-2Nb specimens exhibited a behavior similar to those of the unfretted Ti-48Al-2Cr-2Nb specimens. The values of maximum stress and life for the fretted specimens were almost the same as those for the unfretted specimens. The resultant stress-life curve for the unfretted fatigue specimens was very flat. The flat appearance in the stress-life curve of the unfretted specimens is attributed to the presence of a high density of casting pores. The fatigue strengths of both the fretted and unfretted specimens can be significantly affected by the presence of this porosity, which can decrease the fatigue life of Ti-48Al-2Cr-2Nb. The presence of the porosity made discerning the effect of fretting damage on fatigue strength and life of the specimens difficult.

Analysis of the binder yield energy test as an indicator of fatigue behaviour of asphalt mixes

NASA Astrophysics Data System (ADS)

O'Connell, Johan; Mturi, Georges A. J.; Komba, Julius; Du Plessis, Louw

2017-09-01

Empirical binder testing has increasingly failed to predict pavement performance in South Africa, with fatigue cracking being one of the major forms of premature pavement distress. In response, it has become a national aspiration to incorporate a performance related fatigue test into the binder specifications for South Africa. The Binder Yield Energy Test (BYET) was the first in a series of tests analysed for its potential to predict the fatigue performance of the binder. The test is performed with the dynamic shear rheometer, giving two key parameters, namely, yield energy and shear strain at maximum shear stress (γτmax). The objective of the investigation was to perform a rudimentary evaluation of the BYET; followed by a more in-depth investigation should the initial BYET results prove promising. The paper discusses the results generated from the BYET under eight different conditions, using six different binders. The results are then correlated with four point bending beam fatigue test results obtained from asphalt mix samples that were manufactured from the same binders. Final results indicate that the BYET is not ideal as an indicator of fatigue performance.

Low-cycle thermal fatigue

NASA Technical Reports Server (NTRS)

Halford, G. R.

1986-01-01

A state-of-the-art review is presented of the field of thermal fatigue. Following a brief historical review, the concept is developed that thermal fatigue can be viewed as processes of unbalanced deformation and cracking. The unbalances refer to dissimilar mechanisms occurring in opposing halves of thermal fatigue loading and unloading cycles. Extensive data summaries are presented and results are interpreted in terms of the unbalanced processes involved. Both crack initiation and crack propagation results are summarized. Testing techniques are reviewed, and considerable discussion is given to a technique for thermal fatigue simulation, known as the bithermal fatigue test. Attention is given to the use of isothermal life prediction methods for the prediction of thermal fatigue lives. Shortcomings of isothermally-based life prediction methods are pointed out. Several examples of analyses and thermal fatigue life predictions of high technology structural components are presented. Finally, numerous dos and don'ts relative to design against thermal fatigue are presented.

Low cycle fatigue behavior of polycrystalline NiAl at 300 and 1000 K

NASA Technical Reports Server (NTRS)

Lerch, Bradley A.; Noebe, Ronald D.

1993-01-01

The low cycle fatigue behavior of polycrystalline NiAl was determined at 300 and 1000 K - temperatures below and above the brittle- to-ductile transition temperature (BDTT). Fully reversed, plastic strain-controlled fatigue tests were conducted on two differently fabricated alloy samples: hot isostatically pressed (HIP'ed) prealloyed powder and hot extruded castings. HIP'ed powder (HP) samples were tested only at 1000 K, whereas the more ductile cast-and-extruded (C+E) NiAl samples were tested at both 1000 and 300 K. Plastic strain ranges of 0.06 to 0.2 percent were used. The C+E NiAl cyclically hardened until fracture, reaching stress levels approximately 60 percent greater than the ultimate tensile strength of the alloy. Compared on a strain basis, NiAl had a much longer fatigue life than other B2 ordered compounds in which fracture initiated at processing-related defects. These defects controlled fatigue life at 300 K, with fracture occurring rapidly once a critical stress level was reached. At 1000 K, above the BDTT, both the C+E and HP samples cyclically softened during most of the fatigue tests in air and were insensitive to processing defects. The processing method did not have a major effect on fatigue life; the lives of the HP samples were about a factor of three shorter than the C+E NiAl, but this was attributed to the lower stress response of the C+E material. The C+E NiAl underwent dynamic grain growth, whereas the HP material maintained a constant grain size during testing. In both materials, fatigue life was controlled by intergranular cavitation and creep processes, which led to fatigue crack growth that was primarily intergranular in nature. Final fracture by overload was transgranular in nature. Also, HP samples tested in vacuum had a life three times longer than their counterparts tested in air and, in contrast to those tested in air, hardened continuously over half of the sample life, thereby indicating an environmentally assisted fatigue damage mechanism. The C+E samples were tested only in air. At 1000 K, NiAl exhibited a superior fatigue life when compared to most superalloys on a plastic strain basis, but was inferior to most superalloys on a stress basis.

Fatigue proofing: The role of protective behaviours in mediating fatigue-related risk in a defence aviation environment.

PubMed

Dawson, Drew; Cleggett, Courtney; Thompson, Kirrilly; Thomas, Matthew J W

2017-02-01

In the military or emergency services, operational requirements and/or community expectations often preclude formal prescriptive working time arrangements as a practical means of reducing fatigue-related risk. In these environments, workers sometimes employ adaptive or protective behaviours informally to reduce the risk (i.e. likelihood or consequence) associated with a fatigue-related error. These informal behaviours enable employees to reduce risk while continuing to work while fatigued. In this study, we documented the use of informal protective behaviours in a group of defence aviation personnel including flight crews. Semi-structured interviews were conducted to determine whether and which protective behaviours were used to mitigate fatigue-related error. The 18 participants were from aviation-specific trades and included aircrew (pilots and air-crewman) and aviation maintenance personnel (aeronautical engineers and maintenance personnel). Participants identified 147 ways in which they and/or others act to reduce the likelihood or consequence of a fatigue-related error. These formed seven categories of fatigue-reduction strategies. The two most novel categories are discussed in this paper: task-related and behaviour-based strategies. Broadly speaking, these results indicate that fatigued military flight and maintenance crews use protective 'fatigue-proofing' behaviours to reduce the likelihood and/or consequence of fatigue-related error and were aware of the potential benefits. It is also important to note that these behaviours are not typically part of the formal safety management system. Rather, they have evolved spontaneously as part of the culture around protecting team performance under adverse operating conditions. When compared with previous similar studies, aviation personnel were more readily able to understand the idea of fatigue proofing than those from a fire-fighting background. These differences were thought to reflect different cultural attitudes toward error and formal training using principles of Crew Resource Management and Threat and Error Management. Copyright © 2015 Elsevier Ltd. All rights reserved.

Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP)

Treesearch

Jinghao Li; John F. Hunt; Shaoqin Gong; Zhiyong Cai

2015-01-01

The static and fatigue bending behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP) has been investigated by four-point bending tests. Fatigue panels and weakened panels (wESCP) with an initial interface defect were manufactured for the fatigue tests. Stress σ vs. number of cycles curves (S-N) were recorded under the different stress...

Fatigue in people with localized colorectal cancer who do and do not receive chemotherapy: a longitudinal prospective study

PubMed Central

Vardy, J. L.; Dhillon, H. M.; Pond, G. R.; Renton, C.; Dodd, A.; Zhang, H.; Clarke, S. J.; Tannock, I. F.

2016-01-01

Background Fatigue is associated with cancer and chemotherapy and may be sustained. Here, we describe a prospective longitudinal study evaluating fatigue and putative mechanisms in people with colorectal cancer (CRC). Patients and methods People with localized CRC completed the Functional Assessment of Cancer Treatment-Fatigue (FACT-F) questionnaire at baseline (before chemotherapy, if given), 6, 12, and 24 months. Healthy controls (HCs) were assessed at the first three time points. Fatigue was defined by standardized FACT-F scores ≤68/100. Quality-of-life (QoL, assessed by the FACT-G questionnaire), affective, and cognitive symptoms were evaluated. Associations were sought between fatigue, baseline factors, and blood tests (including hemoglobin, cytokines, and sex hormones). Regression analyses, Fisher's exact tests, and Wilcoxon rank-sum tests assessed levels of fatigue at each time point and change in fatigue from baseline. A repeated-measures analysis investigated prognostic factors of fatigue across all time points. Results A total of 289 subjects with localized CRC (173 received chemotherapy) and 72 HCs were assessed. More CRC patients had fatigue than HCs at baseline (52% versus 26%, P < 0.001). Fatigue was increased in the chemotherapy (CTh) group at 6 months [CTh+ 70% versus CTh− 31% (P < 0.001), HCs 22%] and remained more common at 12 [CTh+ 44% versus CTh− 31% (P = 0.079)] and 24 months [CTh+ 39% versus CTh− 24% (P = 0.047)]. There was no significant difference between those not receiving chemotherapy and HCs at follow-up assessments. Fatigue was associated with poor QoL, affective and cognitive symptoms, but not consistently with cytokine levels. Predictors for sustained fatigue were baseline fatigue, treatment group, cognitive and affective symptoms, poorer QoL, and comorbidities. Conclusions CRC patients have more fatigue than HCs at baseline. Fatigue peaks immediately after adjuvant chemotherapy, but remains common for 2 years in those who receive chemotherapy. Cognitive and affective symptoms, QoL, comorbidities, chemotherapy, and baseline fatigue predict for longer term fatigue. PMID:27443634

Cyclic fatigue behavior of nickel-titanium dental rotary files in clinical simulated root canals.

PubMed

Chi, Chih-Wen; Li, Chun-Chieh; Lin, Chun-Pin; Shin, Chow-Shing

2017-04-01

Dental rotary instruments can be applied in multiple conditions of canals, but unpredictable fatigue fracture may happen. This study evaluated the fatigue lives of two batches of nickel-titanium (NiTi) dental rotary files operating in clinically simulated root canals. Single-step cyclic fatigue tests were carried out to assess the performance of two batches of NiTi files (ProTaper and ProFile) in nine combinations of simulated canals (cylinder radii 5 mm, 7.5 mm, and 10 mm, and insertion angles 20°, 40°, and 60°). Two-step cyclic fatigue tests were carried out in simulated root canals with the same radius by using the following two sets of insertion angles: (20°, 40°), (20°, 60°), (40°, 20°), and (60°, 20°). Fracture surfaces were observed by scanning electron microscopy. The single-step cyclic fatigue results showed that cyclic fatigue lives of the files decreased with increasing insertion angles or decreasing cylinder radius. The ProFile #25 .04 file was more fatigue resistant than the ProTaper F2 file. In two-step cyclic fatigue tests, the total fatigue lives were usually more than 100% when the files operated at a lower strain and then at a higher strain. By scanning electron microscopy, a larger area of fatigue striation corresponded to a longer fatigue life. Cyclic fatigue life can be influenced by the strains and geometries of files. The fatigue life was prolonged when the files operated at a lower strain and then at a higher strain. However, the fatigue life was shortened if the loading sequence was reversed. Copyright © 2016. Published by Elsevier B.V.

Validation of the role of bulk charging of hydrogen in the corrosion fatigue cracking of a low alloy steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Griffiths, A.J.; Hutchings, R.B.; Turnbull, A.

1993-09-01

The enhanced corrosion fatigue crack growth rates of low alloy steels cathodically protected in marine environments results from absorbed hydrogen atoms. Hydrogen atoms are generated at the crack tip, crack walls and the external surface of the specimen (bulk charging). In previous work, Turnbull and Saenz de Santa Maria developed a model to predict the rate of generation of hydrogen atoms at the tips of fatigue cracks for steels cathodically polarized in marine environments. The main prediction from this work was that the external surface of the specimen can be the dominant source of hydrogen atoms at potentials more negativemore » than about [minus]900 mV (SCE), at a cyclic frequency of 0.1 Hz and a stress ratio of 0.5. The relative importance of bulk charging depends on the specific test conditions and is influenced by the applied potential, bulk chemistry, cyclic frequency, specimen thickness, temperature and use of coatings. Since laboratory test times are usually short in relation to the time required for hydrogen transport measured crack growth rates may be lower than those occurring in practice, for which there is sufficient time for full hydrogen charging. The purpose of this study is to verify experimentally the importance of bulk charging. Since the sensitivity of cracking to variations in hydrogen concentration will be material dependent a high strength steel was selected in this initial study because of its sensitivity to hydrogen. This will enable validation of the basic premise that bulk charging can be important, prior to more extensive studies using lower strength alloys.« less

Evaluation of materials during outdoor testing using a computer-controlled test apparatus

Treesearch

R. Sam Williams; Steven Lacher; Corey Halpin; Christopher White

2006-01-01

Ultraviolet radiation, moisture, heat, and cyclic fatigue are some of the stressors that cause materials to degrade outdoors. Considerable research has addressed the effects of ultraviolet radiation and moisture on the rate of this degradation. An often overlooked stressor on materials, during outdoor testing, is the cyclic fatigue. Cyclic fatigue is caused by self-...

75 FR 8479 - Airworthiness Directives; Airbus Model A340-541 and -642 Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2010-02-25

... A340-600 full scale fatigue test, cracks were found on left and right sides of the rear spar vertical... scale fatigue test, cracks were found on left and right sides of the rear spar vertical cruciform at... this full scale fatigue test completion, it has been determined that the current inspections values...

Crack Initiation and Growth Behavior at Corrosion Pit in 2024-T3 Aluminum Alloy

DTIC Science & Technology

2014-09-01

63 Figure B.1: The crack length vs. number of cycles during fatigue testing for the 2AI-01 specimen...number of cycles during fatigue testing for the the 2AI- 02 specimen...64 Figure B.3: The crack length vs. number of cycles during fatigue testing for the 2Sl-01 specimen

[The effects of foot reflexology on fatigue and insomnia in patients suffering from coal workers' pneumoconiosis].

PubMed

Lee, Young-Mee; Sohng, Kyeong-Yae

2005-12-01

The purpose of this study was to determine the effects of foot reflexology on fatigue and insomnia in patients suffering from coal workers' pneumoconiosis. This study was a quasi-experimental study of pre-test and post-test design in a non-equivalent control group. The subjects of this study consisted of both the experimental group of twenty-nine and the control group of thirty coal workers' pneumoconiosis patients. Data was collected from December 10, 2002 to February 15, 2003. Foot reflexology was performed for 60 minutes twice a week through five weeks in the experimental group, but none in the control group. To evaluate the effects of foot reflexology, the scores of fatigue and insomnia were measured before and after the experiment in both groups. Fatigue was evaluated by Fatigue Symptoms Inventory. Insomnia was measured with the visual analogue scale (VAS). Data of this experiment was analyzed by Chi-square test, t-test, unpaired t-test and Repeated Measures ANOVA with the SAS Program. The scores of fatigue and insomnia decreased in the experimental group but not in the control group. There was a significant difference of fatigue and insomnia between the two groups. It is suggested that foot reflexology might have beneficial effects on reducing fatigue and insomnia in patients suffering from coal workers' pneumoconiosis, and can be recommended as a nursing intervention program for patients with coal workers' pneumoconiosis.

Crack-growth behavior in thick welded plates of Inconel 718 at room and cryogenic temperatures

NASA Technical Reports Server (NTRS)

Forman, R. G.

1974-01-01

Results of mechanical-properties and axial-load fatigue and fracture tests performed on thick welded plates of Inconel 718 superalloy are presented. The test objectives were to determine the tensile strength properties and the crack-growth behavior in electron-beam, plasma-arc, and gas tungsten are welds for plates 1.90 cm (0.75 in) thick. Base-metal specimens were also tested to determine the flaw-growth behavior. The tests were performed in room-temperature-air and liquid nitrogen environments. The experimental crack-growth-rate data are correlated with theoretical crack-growth-rate predictions for semielliptical surface flaws.

Effect of Creep and Oxidation on Reduced Creep-Fatigue life of Ni-based Alloy 617 at 850 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xiang; Yang, Zhiqing; Sokolov, Mikhail A

Low cycle fatigue (LCF) and creep fatigue testing of Ni-based alloy 617 was carried out at 850 C. Compared with its LCF life, the material s creep fatigue life decreases to different extents depending on test conditions. To elucidate the microstructure-fatigue property relationship for alloy 617 and the effect of creep and oxidation on its fatigue life, systematic microstructural investigations were carried out using scanning electron microscopy, energy-dispersive X-ray spectroscopy, and electron backscatter diffraction (EBSD). In LCF tests, as the total strain range increased, deformations concentrated near high angle grain boundaries (HAGBs). The strain hold period in the creep fatiguemore » tests introduced additional creep damage to the material, which revealed the detrimental effect of the strain hold time on the material fatigue life in two ways. First, the strain hold time enhanced the localized deformation near HAGBs, resulting in the promotion of intergranular cracking of alloy 617. Second, the strain hold time encouraged grain boundary sliding, which resulted in interior intergranular cracking of the material. Oxidation accelerated the initiation of intergranular cracking in alloy 617. In the crack propagation stage, if oxidation was promoted and the cyclic oxidation damage was greater than the fatigue damage, oxidation-assisted intergranular crack growth resulted in a significant reduction in the material s fatigue life.« less

Effect of welding structure and δ-ferrite on fatigue properties for TIG welded austenitic stainless steels at cryogenic temperatures

NASA Astrophysics Data System (ADS)

Yuri, Tetsumi; Ogata, Toshio; Saito, Masahiro; Hirayama, Yoshiaki

2000-04-01

High-cycle and low-cycle fatigue properties of base and weld metals for SUS304L and SUS316L and the effects of welding structure and δ-ferrite on fatigue properties were investigated at cryogenic temperatures in order to evaluate the long-life reliability of the structural materials to be used in liquid hydrogen supertankers and storage tanks and to develop a welding process for these applications. The S-N curves of the base and weld metals shifted towards higher levels, i.e., the longer life side, with decreasing test temperatures. High-cycle fatigue tests demonstrated the ratios of fatigue strength at 10 6 cycles to tensile strength of the weld metals to be 0.35-0.7, falling below those of base metals with decreasing test temperatures. Fatigue crack initiation sites in SUS304L weld metals were mostly at blowholes with diameters of 200-700 μm, and those of SUS316L weld metals were at weld pass interface boundaries. Low-cycle fatigue tests revealed the fatigue lives of the weld metals to be somewhat lower than those of the base metals. Although δ-ferrite reduces the toughness of austenitic stainless steels at cryogenic temperatures, the effects of δ-ferrite on high-cycle and low-cycle fatigue properties are not clear or significant.

Determinants of seafarers' fatigue: a systematic review and quality assessment.

PubMed

Dohrmann, Solveig Boeggild; Leppin, Anja

2017-01-01

Fatigue jeopardizes seafarer's health and safety. Thus, knowledge on determinants of fatigue is of great importance to facilitate its prevention. However, a systematic analysis and quality assessment of all empirical evidence specifically for fatigue are still lacking. The aim of the present article was therefore to systematically detect, analyze and assess the quality of this evidence. Systematic searches in ten databases were performed. Searches considered articles published in scholarly journals from 1980 to April 15, 2016. Nineteen out of 98 eligible studies were included in the review. The main reason for exclusion was fatigue not being the outcome variable. Most evidence was available for work time-related factors suggesting that working nights was most fatiguing, that fatigue levels were higher toward the end of watch or shift, and that the 6-h on-6-h off watch system was the most fatiguing. Specific work demands and particularly the psychosocial work environment have received little attention, but preliminary evidence suggests that stress may be an important factor. A majority of 12 studies were evaluated as potentially having a high risk of bias. Realistic countermeasures ought to be established, e.g., in terms of shared or split night shifts. As internal as well as external validity of many study findings was limited, the range of factors investigated was insufficient and few studies investigated more complex interactions between different factors, knowledge derived from studies of high methodological quality investigating different factors, including psychosocial work environments, are needed to support future preventive programs.

Investigation of fatigue by Australian general practice registrars: a cross-sectional study.

PubMed

Morgan, Simon; Henderson, Kim M; Tapley, Amanda; Thomson, Allison; Wilson, Jessica; Scott, John; Spike, Neil A; McArthur, Lawrie; van Driel, Mieke L; Magin, Parker J

2015-06-01

Fatigue is the most common undifferentiated problem presenting in general practice. Previous studies have shown that this presentation leads to multiple investigations. There is no published literature describing the management of patients with fatigue by general practice (GP) registrars. To document the investigation-ordering behaviour of GP registrars in managing patients with a new diagnosis of unexplained fatigue. This was a cross-sectional analysis of data from Registrar Clinical Encounters in Training (ReCEnT), an ongoing cohort study of GP registrars' consultations. We established the prevalence of new diagnoses of unexplained fatigue and associations with that diagnosis, the rate of test ordering and the number and types of investigations ordered. 644 registrars contributed data from 68 986 encounters. In 0.78% of patient encounters, a new diagnosis of unexplained fatigue was made. Pathology was ordered in 78.4% of these problems (versus 18.1% in non-fatigue problems), at a rate of 488 tests per 100 new fatigue problems. Our study suggests that unexplained fatigue elicits a non-rational approach to test ordering by registrars. These findings contribute to the understanding of GP registrar management of fatigue, and undifferentiated presentations more broadly, and suggest educational approaches to improve practice, including dealing with uncertainty.

Accelerated fatigue durability of a high performance composite

NASA Technical Reports Server (NTRS)

Rotem, A.

1982-01-01

The fatigue behavior of multidirectional graphite-epoxy laminates was analyzed theoretically and experimentally in an effort to establish an accelerated testing methodology. Analysis of the failure mechanism in fatigue of the laminates led to the determination of the failure mode governing fracture. The nonlinear, cyclic-dependent shear modulus was used to calculate the changing stress field in the laminate during the fatigue loading. Fatigue tests were performed at three different temperatures: 25 C, 74 C, and 114 C. The prediction of the S-N curves was made based on the artificial static strength artificial static strength at a reference temperature and the fatigue functions associated with them. The prediction of an S-N curve at other temperatures was performed using shifting factors determined for the specific failure mode. For multidirectional laminates, different S-N curves at different temperatures could be predicted using these shifting factors. Different S-N curves at different temperatures occur only when the fatigue failure mode is matrix dominated. It was found that whenever the fatigue failure mode is fiber dominated, temperature, over the range investigated, had no influence on the fatigue life. These results permit the prediction of long-time, low temperature fatigue behavior from data obtained in short time, high temperature testing, for laminates governed by a matrix failure mode.

Four-point-bending-fatigue behavior of the Zr-based Vitreloy 105 bulk metallic glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morrison, M. L.; Buchanan, R. A.; Liaw, Peter K

The purpose of this study was to make a direct comparison between four-point-bending and uniaxial fatigue tests with the Zr{sub 52.5}Cu{sub 17.9}Ni{sub 14.6}Al{sub 10.0}Ti{sub 5.0} (at.%) BMG alloy (Vitreloy 105). The fatigue lifetimes in four-point bending were found to be greater than those reported in uniaxial testing. However, the fatigue-endurance limit found in four-point bending was slightly less than that reported for uniaxial fatigue. Thus, the significant differences between fatigue studies in the literature are not likely due to this difference in testing geometry. On the contrary, the fatigue lifetimes were found to be highly dependent upon surface defects andmore » material quality. The four-point-bending-fatigue performance of the Vit 105 alloy was found to be greater than most BMGs and similar to the 300 M high-strength steel and other crystalline alloys in spite of not being 'perfectly amorphous.' Due to the detrimental effects of these inhomogeneities and wear at the supporting pins, this fatigue behavior can be assumed to be a conservative estimate of the potential fatigue performance of a perfectly amorphous and homogeneous BMG.« less

The effects of mental fatigue on cricket-relevant performance among elite players.

PubMed

Veness, Darren; Patterson, Stephen David; Jeffries, Owen; Waldron, Mark

2017-12-01

This study investigated the effects of a mentally fatiguing test on physical tasks among elite cricketers. In a cross-over design, 10 elite male cricket players from a professional club performed a cricket run-two test, a Batak Lite reaction time test and a Yo-Yo-Intermittent Recovery Level 1 (Yo-Yo-IR1) test, providing a rating of perceived exertion (RPE) after completing a 30-min Stroop test (mental fatigue condition) or 30-min control condition. Perceived fatigue was assessed before and after the two conditions and motivation was measured before testing. There were post-treatment differences in the perception of mental fatigue (P < 0.001; d = -7.82, 95% CIs = -9.05-6.66; most likely). Cricket run-two (P = 0.002; d = -0.51, 95% CIs = -0.72-0.30; very likely), Yo-Yo-IR1 distance (P = 0.023; d = 0.39, 95% CIs = 0.14-0.64; likely) and RPE (P = 0.001; d = -1.82, 95% CIs = -2.49-1.14; most likely) were negatively affected by mental fatigue. The Batak Lite test was not affected (P = 0.137), yet a moderate (d = 0.41, 95% CIs = -0.05-0.87) change was likely. Mental fatigue, induced by an app-based Stroop test, negatively affected cricket-relevant performance.

A novel evaluation strategy for fatigue reliability of flexible nanoscale films

NASA Astrophysics Data System (ADS)

Zheng, Si-Xue; Luo, Xue-Mei; Wang, Dong; Zhang, Guang-Ping

2018-03-01

In order to evaluate fatigue reliability of nanoscale metal films on flexible substrates, here we proposed an effective evaluation way to obtain critical fatigue cracking strain based on the direct observation of fatigue damage sites through conventional dynamic bending testing technique. By this method, fatigue properties and damage behaviors of 930 nm-thick Au films and 600 nm-thick Mo-W multilayers with individual layer thickness 100 nm on flexible polyimide substrates were investigated. Coffin-Manson relationship between the fatigue life and the applied strain range was obtained for the Au films and Mo-W multilayers. The characterization of fatigue damage behaviors verifies the feasibility of this method, which seems easier and more effective comparing with the other testing methods.

Evaluation of Giga-cycle Fatigue Properties of Austenitic Stainless Steels Using Ultrasonic Fatigue Test

NASA Astrophysics Data System (ADS)

Takahashi, Kyouhei; Ogawa, Takeshi

Ultrasonic fatigue tests have been performed in austenitic stainless steel, SUS316NG, in order to investigate giga-cycle fatigue strength of pre-strained materials, i.e. 5, 10 and 20% tensile pre-strains and -20% compressive pre-strain. The pre-strains were applied before specimen machining. The austenitic stainless steels are known to exhibit remarkable self-heating during the fatigue experiment. Therefore, heat radiation method was established by setting fatigue specimens in a low temperature chamber at about -100°C. The self-heating was controlled by intermittent loading condition, which enabled us to maintain the test section of the specimens at about room temperature. The results revealed that the fatigue strength increased with increasing pre-strain levels. Fish-eye fracture was observed for -20% pre-strained specimen fractured at 4.11×107 cycles, while the other specimens exhibited ordinary fatigue fracture surface originated from stage I facet on the specimen surface. The increase in fatigue limit was predicted by Vickers hardness, HV, which depended on the size of indented region. The prediction was successful using HV values obtained by the size of the indented region similar to those of the stage I facets.

a Study on the Fretting Fatigue Life of Zircaloy Alloys

NASA Astrophysics Data System (ADS)

Kwon, Jae-Do; Park, Dae-Kyu; Woo, Seung-Wan; Chai, Young-Suck

Studies on the strength and fatigue life of machines and structures have been conducted in accordance with the development of modern industries. In particular, fine and repetitive cyclic damage occurring in contact regions has been known to have an impact on fretting fatigue fractures. The main component of zircaloy alloy is Zr, and it possesses good mechanical characteristics at high temperatures. This alloy is used in the fuel rod material of nuclear power plants because of its excellent resistance. In this paper, the effect of the fretting damage on the fatigue behavior of the zircaloy alloy is studied. Further, various types of mechanical tests such as tension and plain fatigue tests are performed. Fretting fatigue tests are performed with a flat-flat contact configuration using a bridge-type contact pad and plate-type specimen. Through these experiments, it is found that the fretting fatigue strength decreases by about 80% as compared to the plain fatigue strength. Oblique cracks are observed in the initial stage of the fretting fatigue, in which damaged areas are found. These results can be used as the basic data for the structural integrity evaluation of corrosion-resisting alloys considering the fretting damages.

Effect of mental fatigue on the central nervous system: an electroencephalography study

PubMed Central

2012-01-01

Background Fatigue can be classified as mental and physical depending on its cause, and each type of fatigue has a multi-factorial nature. We examined the effect of mental fatigue on the central nervous system using electroencephalography (EEG) in eighteen healthy male volunteers. Methods After enrollment, subjects were randomly assigned to two groups in a single-blinded, crossover fashion to perform two types of mental fatigue-inducing experiments. Each experiment consisted of four 30-min fatigue-inducing 0- or 2-back test sessions and two evaluation sessions performed just before and after the fatigue-inducing sessions. During the evaluation session, the participants were assessed using EEG. Eleven electrodes were attached to the head skin, from positions F3, Fz, F4, C3, Cz, C4, P3, Pz, P4, O1, and O2. Results In the 2-back test, the beta power density on the Pz electrode and the alpha power densities on the P3 and O2 electrodes were decreased, and the theta power density on the Cz electrode was increased after the fatigue-inducing mental task sessions. In the 0-back test, no electrodes were altered after the fatigue-inducing sessions. Conclusions Different types of mental fatigue produced different kinds of alterations of the spontaneous EEG variables. Our findings provide new perspectives on the neural mechanisms underlying mental fatigue. PMID:22954020

Fatigue methodology III; Proceedings of the AHS National Technical Specialists' Meeting on Advanced Rotorcraft Structures, Scottsdale, AZ, Oct. 3-5, 1989

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1989-01-01

Papers on rotorcraft and fatigue methodology are presented, covering topics such as reliability design for rotorcraft, a comparison between theory and fatigue test data on stress concentration factors, the retirement lives of rolling element bearings, hydrogen embrittlement risk analysis for high hardness steel parts, and rotating system load monitoring with minimum fixed system instrumentation. Additional topics include usage data collection to improve structural integrity of operational helicopters, usage monitory of military helicopters, improvements to the fatigue substantiation of the H-60 composite tail rotor blade, helicopter surviellance programs, and potential application of automotive fatigue technology in rotorcraft design. Also, consideration ismore » given to fatigue evaluation of C/MH-53 E main rotor damper threaded joints, SH-2F airframe fatigue test program, a ply termination concept for improving fracture and fatigue strength of composite laminates, the analysis and testing of composite panels subject to muzzle blast effects, the certification plan for an all-composite main rotor flexbeam, and the effects of stacking sequence on the flexural strength of composite beams.« less

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

NASA Astrophysics Data System (ADS)

Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

2014-12-01

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 108 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Lee, Sung Min; Wang, James L.

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10^8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and themore » fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Assessment of physical fatigability and fatigue perception in myasthenia gravis.

PubMed

Jordan, Berit; Mehl, Theresa; Schweden, Tabea L K; Menge, Uwe; Zierz, Stephan

2017-05-01

Fatigue includes both performance fatigability and fatigue perception. In 32 stable patients with generalized myasthenia gravis (MG) and 17 controls, time-dependent physical performance was assessed by the arm movement test (AMT) and 6-minute walk test (6MWT). MG patients presented with low quantitative MG scores (mean 0.5, SD 0.5) and without pathologic decrement. Fatigability was based on calculation of linear trend (LT) reflecting dynamic performance within subsequent constant time intervals. Perception of physical fatigue was analyzed using fatigue questionnaires. MG patients showed a negative LT in both AMT and 6MWT, significantly differing from stable performance in controls. LT inversely correlated with elevation of acetylcholine receptor antibodies (r = -0.59, P < 0.005) but not with quantitative MG score and fatigue perception. LT allows quantification of fatigability as an objective measurement of decline in individual performance, even in patients without obvious neuromuscular deficits in routine testing. The missing correlation of experienced fatigue supports the multidimensional fatigue model. Muscle Nerve 55: 657-663, 2017. © 2016 Wiley Periodicals, Inc.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE PAGES

Wang, Hong; Lee, Sung Min; Wang, James L.; ...

2014-12-19

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10^8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and themore » fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Fatigue of notched fiber composite laminates. Part 2: Analytical and experimental evaluation

NASA Technical Reports Server (NTRS)

Kulkarni, S. V.; Mclaughlin, P. V., Jr.; Pipes, R. B.

1976-01-01

The analytical/experimental correlation study was performed to develop an understanding of the behavior of notched Boron/epoxy laminates subjected to tension/tension fatigue loading. It is postulated that the fatigue induced property changes (stiffness as well as strength) of the laminate can be obtained from the lamina fatigue properties. To that end, the Boron/epoxy lamina static and fatigue data (lifetime, residual stiffness and strength) were obtained initially. The longitudinal and transverse tension data were determined from the (0) and (90) laminate tests while the in-plane shear data were obtained from the (+ or - 45) sub s laminates. The static tests obtained the notched strength and mode of failure while the fatigue tests determined lifetime, damage propagation and residual strength. The failure in static tension occurred in a transverse crack propagation mode.

Fatigue Behavior of AM60B Subjected to Variable Amplitude Loading

NASA Astrophysics Data System (ADS)

Kang, H.; Kari, K.; Khosrovaneh, A. K.; Nayaki, R.; Su, X.; Zhang, L.; Lee, Y.-L.

Magnesium alloys are considered as an alternative material to reduce vehicle weight due to their weight which are 33% lighter than aluminum alloys. There has been a significant expansion in the applications of magnesium alloys in automotives components in an effort to improve fuel efficiency through vehicle mass reduction. In this project, a simple front shock tower of passenger vehicle is constructed with various magnesium alloys. To predict the fatigue behavior of the structure, fatigue properties of the magnesium alloy (AM60B) were determined from strain controlled fatigue tests. Notched specimens were also tested with three different variable amplitude loading profiles obtained from the shock tower of the similar size of vehicle. The test results were compared with various fatigue prediction results. The effect of mean stress and fatigue prediction method were discussed.

ORNL Interim Progress Report on Hydride Reorientation CIRFT Tests

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An John; Yan, Yong; Wang, Hong

A systematic study of H. B. Robinson (HBR) high burnup spent nuclear fuel (SNF) vibration integrity was performed in Phase I project under simulated transportation environments, using the Cyclic Integrated Reversible-Bending Fatigue Tester (CIRFT) hot cell testing technology developed at Oak Ridge National Laboratory in 2013–14. The data analysis on the as-irradiated HBR SNF rods demonstrated that the load amplitude is the dominant factor that controls the fatigue life of bending rods. However, previous studies have shown that the hydrogen content and hydride morphology has an important effect on zirconium alloy mechanical properties. To address the effect of radial hydridesmore » in SNF rods, in Phase II a test procedure was developed to simulate the effects of elevated temperatures, pressures, and stresses during transfer-drying operations. Pressurized and sealed fuel segments were heated to the target temperature for a preset hold time and slow-cooled at a controlled rate. The procedure was applied to both non-irradiated/prehydrided and high-burnup Zircaloy-4 fueled cladding segments using the Nuclear Regulatory Commission-recommended 400°C maximum temperature limit at various cooling rates. Before testing high-burnup cladding, four out-of-cell tests were conducted to optimize the hydride reorientation (R) test condition with pre-hydride Zircaloy-4 cladding, which has the same geometry as the high burnup fuel samples. Test HR-HBR#1 was conducted at the maximum hoop stress of 145 MPa, at a 400°C maximum temperature and a 5°C/h cooling rate. On the other hand, thermal cycling was performed for tests HR-HBR#2, HR-HBR#3, and HR-HBR#4 to generate more radial hydrides. It is clear that thermal cycling increases the ratio of the radial hydride to circumferential hydrides. The internal pressure also has a significant effect on the radial hydride morphology. This report describes a procedure and experimental results of the four out-of-cell hydride reorientation tests of hydrided Zircaloy-4 cladding, which served as a guideline to prepare in-cell hydride reorientation samples with high burnup HBR fuel segments. This report also provides the Phase II CIRFT test data for the hydride reorientation irradiated samples. The variations in fatigue life are provided in terms of moment, equivalent stress, curvature, and equivalent strain for the tested SNFs. The CIRFT results appear to indicate that hydride reoriented treatment (HRT) have a negative effect on fatigue life, in addition to hydride reorientation effect. For HR4 specimen that had no pressurization procedure applied, the thermal annealing treatment alone showed a negative impact on the fatigue life compared to the HBR rod.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scholbrock, A. K.; Fleming, P. A.; Fingersh, L. J.

Wind turbines are complex, nonlinear, dynamic systems driven by aerodynamic, gravitational, centrifugal, and gyroscopic forces. The aerodynamics of wind turbines are nonlinear, unsteady, and complex. Turbine rotors are subjected to a chaotic three-dimensional (3-D) turbulent wind inflow field with imbedded coherent vortices that drive fatigue loads and reduce lifetime. In order to reduce cost of energy, future large multimegawatt turbines must be designed with lighter weight structures, using active controls to mitigate fatigue loads, maximize energy capture, and add active damping to maintain stability for these dynamically active structures operating in a complex environment. Researchers at the National Renewable Energymore » Laboratory (NREL) and University of Stuttgart are designing, implementing, and testing advanced feed-back and feed-forward controls in order to reduce the cost of energy for wind turbines.« less

Hydrogen accelerated fatigue crack growth of friction stir welded X52 steel pipe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ronevich, Joseph Allen; Somerday, Brian P.; Feng, Zhili

Friction stir welded steel pipelines were tested in high pressure hydrogen gas to examine the effects of hydrogen accelerated fatigue crack growth. Fatigue crack growth rate (da/dN) vs. stress-intensity factor range (ΔK) relationships were measured for an X52 friction stir welded pipe tested in 21 MPa hydrogen gas at a frequency of 1 Hz and R = 0.5. Tests were performed on three regions: base metal (BM), center of friction stir weld (FSW), and 15 mm off-center of the weld. For all three material regions, tests in hydrogen exhibited accelerated fatigue crack growth rates that exceeded an order of magnitudemore » compared to companion tests in air. Among tests in hydrogen, fatigue crack growth rates were modestly higher in the FSW than the BM and 15 mm off-center tests. Select regions of the fracture surfaces associated with specified ΔK levels were examined which revealed intergranular fracture in the BM and 15 mm off-center specimens but an absence of intergranular features in the FSW specimens. In conclusion, the X52 friction stir weld and base metal tested in hydrogen exhibited fatigue crack growth rate relationships that are comparable to those for conventional arc welded steel pipeline of similar strength found in the literature.« less

Hydrogen accelerated fatigue crack growth of friction stir welded X52 steel pipe

DOE PAGES

Ronevich, Joseph Allen; Somerday, Brian P.; Feng, Zhili

2016-11-17

Friction stir welded steel pipelines were tested in high pressure hydrogen gas to examine the effects of hydrogen accelerated fatigue crack growth. Fatigue crack growth rate (da/dN) vs. stress-intensity factor range (ΔK) relationships were measured for an X52 friction stir welded pipe tested in 21 MPa hydrogen gas at a frequency of 1 Hz and R = 0.5. Tests were performed on three regions: base metal (BM), center of friction stir weld (FSW), and 15 mm off-center of the weld. For all three material regions, tests in hydrogen exhibited accelerated fatigue crack growth rates that exceeded an order of magnitudemore » compared to companion tests in air. Among tests in hydrogen, fatigue crack growth rates were modestly higher in the FSW than the BM and 15 mm off-center tests. Select regions of the fracture surfaces associated with specified ΔK levels were examined which revealed intergranular fracture in the BM and 15 mm off-center specimens but an absence of intergranular features in the FSW specimens. In conclusion, the X52 friction stir weld and base metal tested in hydrogen exhibited fatigue crack growth rate relationships that are comparable to those for conventional arc welded steel pipeline of similar strength found in the literature.« less

Hydrogen gas embrittlement and the disc pressure test

NASA Technical Reports Server (NTRS)

Bachelet, E. J.; Troiano, A. R.

1973-01-01

A disc pressure test has been used to study the influenced of a hydrogen gas environment on the mechanical properties of three high strength superalloys, Inconel 718, L-605 and A-286, in static and dynamic conditions. The influence of the hydrogen pressure, loading rate, temperature, mechanical and thermal fatigue has investigated. The permeation characteristics of Inconel 718 have been determined in collaboration with the French AEC. The results complemented by a fractographic study are consistent either with a stress-sorption or with an internal embrittlement type of mechanism.

Fatigue Crack Growth Behavior and Microstructural Mechanisms in Ti-6Al-4V Manufactured by Laser Engineered Net Shaping

DTIC Science & Technology

2015-12-01

hardening heat treatment were the controlling factors of the fatigue resistance, while testing directions have the least impact. Leuders et al. [16...radius. The microstructurally-small fatigue crack growth test was run under load control at constant stress ratio R=0.1 and a cyclic frequency of 20 Hz...not been thoroughly investigated. In this study, long fatigue crack growth tests were conducted at two stress ratios (R=0.1 and 0.8), using Ti-6Al

In situ SEM thermal fatigue of Al/graphite metal matrix composites

NASA Technical Reports Server (NTRS)

Zong, G. S.; Rabenberg, L.; Marcus, H. L.

1990-01-01

Several thermal fatigue-induced failure mechanisms are deduced for unidirectional graphite-reinforced 6061 Al-alloy MMCs subjected to in situ thermal cycling. These thermal cycling conditions are representative of MMC service cycles in aerospace environments, where thermal fatigue is primarily associated with changes in the stress states near the interfaces due to coefficient of thermal expansion mismatch between fiber and matrix. This in situ SEM thermal-cycling study clarified such factors affecting MMCs' thermal fatigue as local fiber content and distribution, void volume, fiber stiffness, thermal excursion magnitude, and number of thermal cycles. MMC microfailure modes in thermal fatigue have been deduced.

Several submaximal exercise tests are reliable, valid and acceptable in people with chronic pain, fibromyalgia or chronic fatigue: a systematic review.

PubMed

Ratter, Julia; Radlinger, Lorenz; Lucas, Cees

2014-09-01

Are submaximal and maximal exercise tests reliable, valid and acceptable in people with chronic pain, fibromyalgia and fatigue disorders? Systematic review of studies of the psychometric properties of exercise tests. People older than 18 years with chronic pain, fibromyalgia and chronic fatigue disorders. Studies of the measurement properties of tests of physical capacity in people with chronic pain, fibromyalgia or chronic fatigue disorders were included. Studies were required to report: reliability coefficients (intraclass correlation coefficient, alpha reliability coefficient, limits of agreements and Bland-Altman plots); validity coefficients (intraclass correlation coefficient, Spearman's correlation, Kendal T coefficient, Pearson's correlation); or dropout rates. Fourteen studies were eligible: none had low risk of bias, 10 had unclear risk of bias and four had high risk of bias. The included studies evaluated: Åstrand test; modified Åstrand test; Lean body mass-based Åstrand test; submaximal bicycle ergometer test following another protocol other than Åstrand test; 2-km walk test; 5-minute, 6-minute and 10-minute walk tests; shuttle walk test; and modified symptom-limited Bruce treadmill test. None of the studies assessed maximal exercise tests. Where they had been tested, reliability and validity were generally high. Dropout rates were generally acceptable. The 2-km walk test was not recommended in fibromyalgia. Moderate evidence was found for reliability, validity and acceptability of submaximal exercise tests in patients with chronic pain, fibromyalgia or chronic fatigue. There is no evidence about maximal exercise tests in patients with chronic pain, fibromyalgia and chronic fatigue. Copyright © 2014. Published by Elsevier B.V.

An Axial-Torsional, Thermomechanical Fatigue Testing Technique

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Bonacuse, Peter J.

1995-01-01

A technique for conducting strain-controlled, thermomechanical, axial-torsional fatigue tests on thin-walled tubular specimens was developed. Three waveforms of loading, namely, the axial strain waveform, the engineering shear strain waveform, and the temperature waveform were required in these tests. The phasing relationships between the mechanical strain waveforms and the temperature and axial strain waveforms were used to define a set of four axial-torsional, thermomechanical fatigue (AT-TMF) tests. Real-time test control (3 channels) and data acquisition (a minimum of 7 channels) were performed with a software program written in C language and executed on a personal computer. The AT-TMF testing technique was used to investigate the axial-torsional thermomechanical fatigue behavior of a cobalt-base superalloy, Haynes 188. The maximum and minimum temperatures selected for the AT-TMF tests were 760 and 316 C, respectively. Details of the testing system, calibration of the dynamic temperature profile of the thin-walled tubular specimen, thermal strain compensation technique, and test control and data acquisition schemes, are reported. The isothermal, axial, torsional, and in- and out-of-phase axial-torsional fatigue behaviors of Haynes 188 at 316 and 760 C were characterized in previous investigations. The cyclic deformation and fatigue behaviors of Haynes 188 in AT-TMF tests are compared to the previously reported isothermal axial-torsional behavior of this superalloy at the maximum and minimum temperatures.

Relationship of fatigue to the tensile stiffness of asphaltic concrete : final report on phase 1, laboratory investigation.

DOT National Transportation Integrated Search

1972-01-01

The correlation between asphaltic concrete tensile stiffness and fatigue life was determined in the laboratory. Constant strain fatigue tests were utilized and indirect tensile tests were selected because of their simplicity and applicability. Four a...

PZT Active Frequency Based Wind Blade Fatigue to Failure Testing Results for Various Blade Designs

DTIC Science & Technology

2011-09-01

PZT Active Frequency Based Wind Blade Fatigue to Failure Testing Results for Various Blade Designs R. J. WERLINK...number. 1. REPORT DATE SEP 2011 2. REPORT TYPE N/A 3. DATES COVERED - 4. TITLE AND SUBTITLE PZT Active Frequency Based Wind Blade Fatigue ...18 Abstract: This paper summarizes NASA PZT Health Monitoring System results previously reported for 9 meter blade Fatigue loading to failure

Effect of environment on fatigue failure of controlled memory wire nickel-titanium rotary instruments.

PubMed

Shen, Ya; Qian, Wei; Abtin, Houman; Gao, Yuan; Haapasalo, Markus

2012-03-01

This study examined the fatigue behavior of 2 types of nickel-titanium (NiTi) instruments made from a novel controlled memory NiTi wire (CM wire) under various environment conditions. Three conventional superelastic NiTi instruments of ProFile (Dentsply Maillefer, Ballaigues, Switzerland), Typhoon (Clinician's Choice Dental Products, New Milford, CT), and DS-SS0250425NEYY (Clinician's Choice Dental Products) and 2 new CM wire instruments of Typhoon CM and DS-SS0250425NEYY CM were subjected to rotational bending at the curvature of 35° in air, deionized water, 17% EDTA, or deionized water after immersion in 6% sodium hypochlorite for 25 minutes, and the number of revolutions of fracture (N(f)) was recorded. The fracture surface of all fragments was examined by a scanning electron microscope. The crack-initiation sites and the percentage of dimple area to the whole fracture cross-section were noted. Two new CM Wire instruments yielded an improvement of >4 to 9 times in N(f) than conventional NiTi files with the same design under various environments (P < .05). The fatigue life of 3 conventional superelastic NiTi instruments was similar under various environments, whereas the N(f) of 2 new CM Wire instruments was significantly longer in liquid media than in air (P < .05). The vast majority of CM instruments showed multiple crack origins, whereas most instruments made from conventional NiTi wire had one crack origin. The values of the area fraction occupied by the dimple region were significantly smaller on CM NiTi instruments than in conventional NiTi instruments under various environments (P < .05). Within the limitations of this study, the type of NiTi metal alloy (CM files vs conventional superelastic NiTi files) influences the cyclic fatigue resistance under various environments. The fatigue life of CM instruments is longer in liquid media than in air. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Estimating the Contact Endurance of the AISI 321 Stainless Steel Under Contact Gigacycle Fatigue Tests

NASA Astrophysics Data System (ADS)

Savrai, R. A.; Makarov, A. V.; Osintseva, A. L.; Malygina, I. Yu.

2018-02-01

Mechanical testing of the AISI 321 corrosion resistant austenitic steel for contact gigacycle fatigue has been conducted with the application of a new method of contact fatigue testing with ultrasonic frequency of loading according to a pulsing impact "plane-to-plane" contact scheme. It has been found that the contact endurance (the ability to resist the fatigue spalling) of the AISI 321 steel under contact gigacycle fatigue loading is determined by its plasticity margin and the possibility of additional hardening under contact loading. It is demonstrated that the appearance of localized deep and long areas of spalling on a material surface can serve as a qualitative characteristic for the loss of the fatigue strength of the AISI 321 steel under impact contact fatigue loading. The value of surface microhardness measured within contact spots and the maximum depth of contact damages in the peripheral zone of contact spots can serve as quantitative criteria for that purpose.

The isothermal fatigue behavior of a unidirectional SiC/Ti composite and the Ti alloy matrix

NASA Technical Reports Server (NTRS)

Gayda, John, Jr.; Gabb, Timothy P.; Freed, Alan D.

1989-01-01

The high temperature fatigue behavior of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) matrix reinforced by 33 vol percent of continuous unidirectional SiC fibers was experimentally and analytically evaluated. Isothermal MMC fatigue tests with constant amplitude loading parallel to the fiber direction were performed at 300 and 550 C. Comparative fatigue tests of the Ti-15-3 matrix alloy were also conducted. Composite fatigue behavior and the in-situ stress state of the fiber and matrix were analyzed with a micromechanical model, the Concentric Cylinder Model (CCM). The cyclic stress-strain response of the composite was stable at 300 C. However, an increase in cyclic mean strain foreshortened MMC fatigue life at high strain ranges at 550 C. Fatigue tests of the matrix alloy and CCM analyses indicated this response was associated with stress relaxation of the matrix in the composite.

High temperature strain gage technology for gas turbine engines

NASA Technical Reports Server (NTRS)

Fichtel, Edward J.; Mcdaniel, Amos D.

1994-01-01

This report summarizes the results of a six month study that addressed specific issues to transfer the Pd-13Cr static strain sensor to a gas turbine engine environment. The application issues that were addressed include: (1) evaluation of a miniature, variable potentiometer for use as the ballast resistor, in conjunction with a conventional strain gage signal conditioning unit; (2) evaluation of a metal sheathed, platinum conductor leadwire assembly for use with the three-wire sensor; and (3) subjecting the sensor to dynamic strain cyclic testing to determine fatigue characteristics. Results indicate a useful static strain gage system at all temperature levels up to 1350 F. The fatigue characteristics also appear to be very promising, indicating a potential use in dynamic strain measurement applications. The procedure, set-up, and data for all tests are presented in this report. This report also discusses the specific strain gage installation technique for the Pd-13Cr gage because of its potential impact on the quality of the output data.

Bending fatigue tests on SiC-Al tapes under alternating stress at room temperature

NASA Technical Reports Server (NTRS)

Herzog, J. A.

1981-01-01

The development of a testing method for fatigue tests on SiC-Al tapes containing a small amount of SiC filaments under alternating stress is reported. The fatigue strength curves resulting for this composite are discussed. They permit an estimate of its behavior under continuous stress and in combination with various other matrices, especially metal matrices.

Experiments of thermomechanical fatigue of SMAs

NASA Astrophysics Data System (ADS)

Lagoudas, Dimitris C.; Miller, David A.

1999-07-01

As SMA wires are gaining in popularity for use as actuators, one constitutive parameter that remain unknown is the thermomechanical fatigue life. Even though the effect of thermal cycles on the transformation characteristics of SMAs has been studied, these teste have not been extended to high number of cycles. In this study, a novel test frame developed to study the thermomechanical fatigue life of SMAs is described. Additionally, a testing protocol is discussed necessary to fully establish the fatigue characteristics of SMAs under various conditions. Initial results of the initial test show a substantial increase in the number of cycles to failure as the applied stress level reduces to approximately 100 MPa.

The effect of weld porosity on the cryogenic fatigue strength of ELI grade Ti-5Al-2.5Sn

NASA Technical Reports Server (NTRS)

Rogers, P. R.; Lambdin, R. C.; Fox, D. E.

1992-01-01

The effect of weld porosity on the fatigue strength of ELI grade Ti-5Al-2.5Sn at cryogenic temperature was determined. A series of high cycle fatigue (HCF) and tensile tests were performed at -320 F on specimens made from welded sheets of the material. All specimens were tested with weld beads intact and some amount of weld offset. Specimens containing porosity and control specimens containing no porosity were tested. Results indicate that for the weld configuration tested, the fatigue life of the material is not affected by the presence of spherical embedded pores.

Effect of stress ratio on the fatigue behaviour of glass/epoxy composite

NASA Astrophysics Data System (ADS)

Syayuthi, A. R. A.; Majid, M. S. Abdul; Ridzuan, M. J. M.; Basaruddin, K. S.; Peng, T. L.

2017-10-01

The effect of stress ratio on the fatigue behaviour of the GFRE composite has been investigated. The glass fibre reinforced epoxy (GFRE) composite plates were fabricated using vacuum infusion method. Static tensile was performed in accordance with the ASTM D5766 standard, and the cyclic test was conducted according to ASTM D3479 with three different stress ratio, R = 0, 0.5, -1. Static tensile tests were carried out to determine the ultimate strength of this composite. Subsequently, fatigue tests loads ranging from 30% to 90% of the ultimate load were applied to each specimen. The S-N curve of different stress ratio loading of fibreglass/epoxy composites was then established. The results show that the number of cycles to failure increases as the loading is decreased. The specimens for fatigue tests loads 30% at R = 0 and -1 recorded the highest number of cycles at 2 million cycles. The results obtained from this test indicated a significant life reduction for R = -1 compared with the tension-tension loading, with the life reduction for R = -1 being greatest. The fatigue behaviour of the GFRE composite materials is not only influenced by the percentage of fatigue tests load but with different of stress ratio.

Computational micromechanics of fatigue of microstructures in the HCF–VHCF regimes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Castelluccio, Gustavo M.; Musinski, William D.; McDowell, David L.

Advances in higher resolution experimental techniques have shown that metallic materials can develop fatigue cracks under cyclic loading levels significantly below the yield stress. Indeed, the traditional notion of a fatigue limit can be recast in terms of limits associated with nucleation and arrest of fatigue cracks at the microstructural scale. Though fatigue damage characteristically emerges from irreversible dislocation processes at sub-grain scales, the specific microstructure attributes, environment, and loading conditions can strongly affect the apparent failure mode and surface to subsurface transitions. This paper discusses multiple mechanisms that occur during fatigue loading in the high cycle fatigue (HCF) tomore » very high cycle fatigue (VHCF) regimes. We compare these regimes, focusing on strategies to bridge experimental and modeling approaches exercised at multiple length scales and discussing particular challenges to modeling and simulation regarding microstructure-sensitive fatigue driving forces and thresholds. Finally, we discuss some of the challenges in predicting the transition of failure mechanisms at different stress and strain amplitudes.« less

Computational micromechanics of fatigue of microstructures in the HCF–VHCF regimes

DOE PAGES

Castelluccio, Gustavo M.; Musinski, William D.; McDowell, David L.

2016-05-19

Advances in higher resolution experimental techniques have shown that metallic materials can develop fatigue cracks under cyclic loading levels significantly below the yield stress. Indeed, the traditional notion of a fatigue limit can be recast in terms of limits associated with nucleation and arrest of fatigue cracks at the microstructural scale. Though fatigue damage characteristically emerges from irreversible dislocation processes at sub-grain scales, the specific microstructure attributes, environment, and loading conditions can strongly affect the apparent failure mode and surface to subsurface transitions. This paper discusses multiple mechanisms that occur during fatigue loading in the high cycle fatigue (HCF) tomore » very high cycle fatigue (VHCF) regimes. We compare these regimes, focusing on strategies to bridge experimental and modeling approaches exercised at multiple length scales and discussing particular challenges to modeling and simulation regarding microstructure-sensitive fatigue driving forces and thresholds. Finally, we discuss some of the challenges in predicting the transition of failure mechanisms at different stress and strain amplitudes.« less

Surface fatigue life and failure characteristics of EX-53, CBS 1000M, and AISI 9310 gear materials

NASA Technical Reports Server (NTRS)

Townsend, D. P.

1985-01-01

Spur gear endurance tests and rolling-element surface fatigue tests are conducted to investigate EX-53 and CBS 1000M steels for use as advanced application gear materials, to determine their endurance characteristics, and to compare the results with the standard AISI 9310 gear material. The gear pitch diameter is 8.89 cm (3.50 in). Gear test conditions are an oil inlet temperature of 320 K (116 F), an oil outlet temperature of 350 K (170 F), a maximum Hertz stress of 1.71 GPa (248 ksi), and a speed of 10,000 rpm. Bench-type rolling-element fatigue tests are conducted at ambient temperature with a bar specimen speed of 12,500 rpm and a maximum Hertz stress of 4.83 GPa (700 ksi). The EX-53 test gears have a surface fatigue life of twice that of the AISI 9310 spur gears. The CBS 1000M test gears have a surface fatigue life of more than twice that of the AISI 9310 spur gears. However, the CBS 1000M gears experience a 30-percent tooth fracture failure which limits its use as a gear material. The rolling-contact fatigue lines of RC bar specimens of EX-53 and ASISI 9310 are approximately equal. However, the CBS 1000M RC specimens have a surface fatigue life of about 50 percent that of the AISI 9310.

Fiber reinforced superalloys for rocket engines

NASA Technical Reports Server (NTRS)

Petrasek, Donald W.; Stephens, Joseph R.

1989-01-01

High pressure turbopumps for advanced reusable liquid propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several fold increase in life and over a 200 C increase in temperature capability over the current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.

Fiber reinforced superalloys for rocket engines

NASA Technical Reports Server (NTRS)

Petrasek, Donald W.; Stephens, Joseph R.

1988-01-01

High-pressure turbopumps for advanced reusable liquid-propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several-fold increase in life and over a 200C increase in temperature capability over current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.

Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a “sandwich structure” as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50–55% of ultimate tensile strength). The dynamic modulus (E⁎) was found to stay almost constant at 47 GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials.

Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a "sandwich structure" as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50-55% of ultimate tensile strength). The dynamic modulus (E(⁎)) was found to stay almost constant at 47GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials. Copyright © 2014 Elsevier Ltd. All rights reserved.

Pitting and Bending Fatigue Evaluations of a New Case-Carburized Gear Steel

NASA Technical Reports Server (NTRS)

Krantz, Timothy; Tufts, Brian

2007-01-01

The power density of a gearbox is an important consideration for many applications and is especially important for gearboxes used on aircraft. One approach to improving power density of gearing is to improve the steel properties by design of the alloy. The alloy tested in this work was designed to be case-carburized with surface hardness of Rockwell C66 after hardening. Test gear performance was evaluated using surface fatigue tests and single-tooth bending fatigue tests. The performance of gears made from the new alloy was compared to the performance of gears made from two alloys currently used for aviation gearing. The new alloy exhibited significantly better performance in surface fatigue testing, demonstrating the value of the improved properties in the case layer. However, the alloy exhibited lesser performance in single-tooth bending fatigue testing. The fracture toughness of the tested gears was insufficient for use in aircraft applications as judged by the behavior exhibited during the single tooth bending tests. This study quantified the performance of the new alloy and has provided guidance for the design and development of next generation gear steels.

Cognitive fatigue in patients with myasthenia gravis.

PubMed

Jordan, Berit; Schweden, Tabea L K; Mehl, Theresa; Menge, Uwe; Zierz, Stephan

2017-09-01

Cognitive fatigue has frequently been reported in myasthenia gravis (MG). However, objective assessment of cognitive fatigability has never been evaluated. Thirty-three MG patients with stable generalized disease and 17 healthy controls underwent a test battery including repeated testing of attention and concentration (d2-R) and Paced Auditory Serial Addition Test. Fatigability was based on calculation of linear trend (LT) reflecting dynamic performance within subsequent constant time intervals. Additionally, fatigue questionnaires were used. MG patients showed a negative LT in second d2-R testing, indicating cognitive fatigability. This finding significantly differed from stable cognitive performance in controls (P < 0.05). Results of Paced Auditory Serial Addition Test testing did not differ between groups. Self-assessed fatigue was significantly higher in MG patients compared with controls (P < 0.001), but did not correlate with LT. LT quantifies cognitive fatigability as an objective measurement of performance decline in MG patients. Self-assessed cognitive fatigue is not correlated with objective findings. Muscle Nerve 56: 449-457, 2017. © 2016 Wiley Periodicals, Inc.

The effect of hold-times on the fatigue behavior of type AISI 316L stainless steel under deuteron irradiation

NASA Astrophysics Data System (ADS)

Scholz, R.; Mueller, R.

1998-10-01

Strain controlled fatigue tests have been performed in torsion at 400°C on type 316L stainless steel samples in both 20% cold worked and annealed conditions during an irradiation with 19 MeV deuterons. A hold-time was imposed in the loading cycle. For the cold worked (cw) material, at shear strain ranges of 1.13% and 1.3%, irradiation creep induced stress relaxation led to the built up of a mean stress. The fatigue life was significantly reduced in comparison to thermal control tests. For the annealed (ann) material, tested under similar experimental conditions, irradiation creep effects were negligibly small compared to cyclic and irradiation hardening. The fatigue life was only slightly reduced. Continuous cycling tests conducted under irradiation conditions lay in the scatter band of the thermal control tests. The difference in fatigue life between continuous cycling and hold-time tests is attributed mainly to the observed difference in irradiation hardening.

Microstructural and Material Quality Effects on Rolling Contact Fatigue of Highly Elastic Intermetallic Ball Bearings

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher; Howard, S. Adam; Thomas, Fransua; Stanford, Malcolm K.

2016-01-01

Rolling element bearings made from highly-elastic intermetallic materials (HIM)s, such as 60NiTi, are under development for applications that require superior corrosion and shock resistance. Compared to steel, intermetallics have been shown to have much lower rolling contact fatigue (RCF) stress capability in simplified 3-ball on rod (ASTM STP 771) fatigue tests. In the 3-ball tests, poor material quality and microstructural flaws negatively affect fatigue life but such relationships have not been established for full-scale 60NiTi bearings. In this paper, 3-ball-on-rod fatigue behavior of two quality grades of 60NiTi are compared to the fatigue life of full-scale 50mm bore ball bearings made from the same materials. 60NiTi RCF rods with material or microstructural flaws suffered from infant mortality failures at all tested stress levels while high quality 60NiTi rods exhibited no failures at lower stress levels. Similarly, tests of full-scale bearings made from flawed materials exhibited early surface fatigue and through crack type failures while bearings made from high quality material did not fail even in long-term tests. Though the full-scale bearing test data is yet preliminary, the results suggest that the simplified RCF test is a good qualitative predictor of bearing performance. These results provide guidance for materials development and to establish minimum quality levels required for successful bearing operation and life.

Microstructural and Material Quality Effects on Rolling Contact Fatigue of Highly Elastic Intermetallic NiTi Ball Bearings

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Howard, S. Adam; Thomas, Fransua; Stanford, Malcolm K.

2017-01-01

Rolling element bearings made from highly-elastic intermetallic materials (HIM)s, such as 60NiTi, are under development for applications that require superior corrosion and shock resistance. Compared to steel, intermetallics have been shown to have much lower rolling contact fatigue (RCF) stress capability in simplified 3-ball on rod (ASTM STP 771) fatigue tests. In the 3-ball tests, poor material quality and microstructural flaws negatively affect fatigue life but such relationships have not been established for full-scale 60NiTi bearings. In this paper, 3-ball-on-rod fatigue behavior of two quality grades of 60NiTi are compared to the fatigue life of full-scale 50mm bore ball bearings made from the same materials. 60NiTi RCF rods with material or microstructural flaws suffered from infant mortality failures at all tested stress levels while high quality 60NiTi rods exhibited no failures at lower stress levels. Similarly, tests of full-scale bearings made from flawed materials exhibited early surface fatigue and through crack type failures while bearings made from high quality material did not fail even in long-term tests. Though the full-scale bearing test data is yet preliminary, the results suggest that the simplified RCF test is a good qualitative predictor of bearing performance. These results provide guidance for materials development and to establish minimum quality levels required for successful bearing operation and life.

Evaluation of tilting disc valves after fatigue life testing: preliminary results within a comparison program.

PubMed

Barbaro, V; Boccanera, G; Daniele, C; Grigioni, M; Palombo, A

1995-09-01

A fatigue life test, by accelerating the beat rate, simulates several years of virtual life of a prosthetic heart valve in a short period of time. The correlation between the in vivo life of a valve and in vitro testing expectations is as yet not well established, but reproducible test conditions yield precious information about wear and failure. The paper reports a qualitative analysis of mechanical valve wear as part of a comparison program designed to investigate the significance of fatigue testing with the ultimate aim of defining standard guidelines for these type of tests. Two tilting disc valves (29 mm) were subjected to 16 years of fatigue life simulated by means of a Rowan Ash fatigue tester (accelerated rate of 1,200 bpm). Fatigue-induced effects on valve disc and ring surfaces were observed under a monitor microscope to identify wear sites and patterns. A high speed cinematographic system was used to investigate the mechanisms responsible for the wear (wear modes). Valve closure was inspected at a 6,000 frame/s rate. Because of disc rotation during the tilting movement, the points of contact between disc and ring are distributed all around the disc edge but focally on the ring. On both sides of the disc, the surfaces present ring-like concentric grooves. After 16 years of fatigue life the valves showed neither severe wear nor alteration of their fluidodynamic behavior in the pulsatile flow test.

An analysis of isothermal, bithermal, and thermomechanical fatigue data of Haynes 188 and B1900+Hf by energy considerations

NASA Technical Reports Server (NTRS)

Radhakrishnan, V. M.; Kalluri, Sreeramesh; Halford, Gary R.

1993-01-01

The low-cycle fatigue behavior of Haynes 188 and B1900+Hf under isothermal, bithermal, and thermomechanical loading conditions has been analyzed on the basis of the total hysteresis energy expended per cycle. It has been observed that in the case of isothermal fatigue the total hysteresis energy correlates well with the fatigue life. In the case of bithermal 'high rate' fatigue, for a given total hysteresis energy per cycle, the fatigue life is equal to or greater than the isothermal fatigue life at the maximum bithermal temperature. This observation could be used to establish a lower bound on life for design purposes. In one case of bithermal creep-fatigue and in thermomechanical fatigue, the life is shorter than that corresponding to the isothermal life at the maximum temperature. The energy supplied, per se, may not always give a systematic correlation with the fatigue life in the cases where time-dependent creep and environmental effects are encountered. Thus, in bithermal creep-fatigue and thermomechanical fatigue, the role of creep and environment and their dependence on the energy supplied have to be properly accounted for before the energy term can be used for life prediction.

The effects of Nitinol phases on corrosion and fatigue behavior

NASA Astrophysics Data System (ADS)

Denton, Melissa

The purpose of these studies was to provide a detailed understanding of Nitinol phases and their effects on corrosion and fatigue life. The two primary phases, austenite and martensite, were carefully evaluated with respect to material geometry, corrosion behavior, wear, and fatigue life. Material characterization was performed using several techniques that include metallography, scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), x-ray photoelectron spectrum (XPS), and Auger electron spectroscopy (AES). Uniaxial tensile tests were conducted to determine the mechanical properties such as elongation, ultimate tensile strength, modulus, transformation strain, and plateau stress. In addition, accelerated wear testing and four point bend fatigue testing were completed to study the fatigue life and durability of the material. The corrosion of Nitinol was found to be dependent on various surface conditions. Electrochemical corrosion behavior of each phase was investigated using cyclic potentiodyamic polarization testing. The corrosion response of electropolished Nitinol was found to be acceptable, even after durability testing. Stress-induced martensite had a lower breakdown potential due to a rougher surface morphology, while thermally induced martensite and austenite performed similarly well. The surface conditioning also had a significant effect on Nitinol mechanical properties. Electropolishing provided a smooth mirror finish that reduced localized texture and enhanced the ductility of the material. Quasi-static mechanical properties can be good indicators of fatigue life, but further fatigue testing revealed that phase transformations had an important role as well. The governing mechanisms for the fatigue life of Nitinol were determined to be both martesitic phase transformations and surface defects. A new ultimate dislocation strain model was proposed based on specific accelerated step-strain testing.

Comparison of Fatigue Life Between C/SiC and SiC/SiC Ceramic-Matrix Composites at Room and Elevated Temperatures

NASA Astrophysics Data System (ADS)

Longbiao, Li

2016-10-01

In this paper, the comparison of fatigue life between C/SiC and SiC/SiC ceramic-matrix composites (CMCs) at room and elevated temperatures has been investigated. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. Under cyclic fatigue loading, the fibers broken fraction was determined by combining the interface wear model and fibers statistical failure model at room temperature, and interface/fibers oxidation model, interface wear model and fibers statistical failure model at elevated temperatures in the oxidative environments. When the broken fibers fraction approaches to the critical value, the composites fatigue fracture. The fatigue life S-N curves and fatigue limits of cross-ply, 2D and 3D C/SiC and SiC/SiC composites at room temperature, 550 °C in air, 750 °C in dry and humid condition, 800 °C in air, 1000 °C in argon and air, 1100 °C, 1300 °C and 1500 °C in vacuum, have been predicted. At room temperature, the fatigue limit of 2D C/SiC composite with ECFL of 20 % lies between 0.78 and 0.8 tensile strength; and the fatigue limit of 2D SiC/SiC composite with ECFL of 20 % lies between 0.75 and 0.85 tensile strength. The fatigue limit of 2D C/SiC composite increases to 0.83 tensile strength with ECFL increasing from 20 to 22.5 %, and the fatigue limit of 3D C/SiC composite is 0.85 tensile strength with ECFL of 37 %. The fatigue performance of 2D SiC/SiC composite is better than that of 2D C/SiC composite at elevated temperatures in oxidative environment.

Studies on Automobile Clutch Release Bearing Characteristics with Acoustic Emission

NASA Astrophysics Data System (ADS)

Chen, Guoliang; Chen, Xiaoyang

Automobile clutch release bearings are important automotive driveline components. For the clutch release bearing, early fatigue failure diagnosis is significant, but the early fatigue failure response signal is not obvious, because failure signals are susceptible to noise on the transmission path and to working environment factors such as interference. With an improvement in vehicle design, clutch release bearing fatigue life indicators have increasingly become an important requirement. Contact fatigue is the main failure mode of release rolling bearing components. Acoustic emission techniques in contact fatigue failure detection have unique advantages, which include highly sensitive nondestructive testing methods. In the acoustic emission technique to detect a bearing, signals are collected from multiple sensors. Each signal contains partial fault information, and there is overlap between the signals' fault information. Therefore, the sensor signals receive simultaneous source information integration is complete fragment rolling bearing fault acoustic emission signal, which is the key issue of accurate fault diagnosis. Release bearing comprises the following components: the outer ring, inner ring, rolling ball, cage. When a failure occurs (such as cracking, pitting), the other components will impact damaged point to produce acoustic emission signal. Release bearings mainly emit an acoustic emission waveform with a Rayleigh wave propagation. Elastic waves emitted from the sound source, and it is through the part surface bearing scattering. Dynamic simulation of rolling bearing failure will contribute to a more in-depth understanding of the characteristics of rolling bearing failure, because monitoring and fault diagnosis of rolling bearings provide a theoretical basis and foundation.

All Fatigue is Not Created Equal: The Association of Fatigue and Its Subtypes on Pain Interference in Orofacial Pain.

PubMed

Boggero, Ian A; Rojas-Ramirez, Marcia V; Carlson, Charles R

2017-03-01

Fatigue is known to be a pathway through which depression, psychological distress, pain intensity, and sleep disturbance influence pain interference, but the independent effects of fatigue on pain interference after controlling for these variables remains unknown. In addition, no study to date has tested whether fatigue subtypes of general fatigue, mental fatigue, emotional fatigue, physical fatigue, or vigor differentially predict pain interference. The current study tested these associations using archival medical data of 2133 chronic orofacial pain patients, who completed a battery of psychological questionnaires at the time of their first appointment at an orofacial pain clinic. Hierarchical linear regression analysis revealed that after controlling for depression, psychological distress, sleep disturbance, pain intensity, and demographic variables, fatigue predicted higher pain interference (B=0.70, SE=0.17, P<0.001, η=0.01). Physical fatigue (B=1.70, SE=0.48, P<0.001, η=0.01) and vigor (B=-3.24, SE=0.47, P<0.001, η=0.03) were independently associated with pain interference after controlling for the aforementioned variables. The findings suggest that fatigue is an important independent predictor of pain interference and not merely a mediator. These findings also suggest that not all fatigue is created equal. Interventions aimed at reducing pain interference should target specific fatigue symptoms of physical fatigue and vigor. Future research investigating the independent associations of fatigue subtypes on pain outcomes may help clarify the nature of the interrelationships between pain and fatigue.

The reliability and validity of fatigue measures during short-duration maximal-intensity intermittent cycling.

PubMed

Glaister, Mark; Stone, Michael H; Stewart, Andrew M; Hughes, Michael; Moir, Gavin L

2004-08-01

The purpose of the present study was to assess the reliability and validity of fatigue measures, as derived from 4 separate formulae, during tests of repeat sprint ability. On separate days over a 3-week period, 2 groups of 7 recreationally active men completed 6 trials of 1 of 2 maximal (20 x 5 seconds) intermittent cycling tests with contrasting recovery periods (10 or 30 seconds). All trials were conducted on a friction-braked cycle ergometer, and fatigue scores were derived from measures of mean power output for each sprint. Apart from formula 1, which calculated fatigue from the percentage difference in mean power output between the first and last sprint, all remaining formulae produced fatigue scores that showed a reasonably good level of test-retest reliability in both intermittent test protocols (intraclass correlation range: 0.78-0.86; 95% likely range of true values: 0.54-0.97). Although between-protocol differences in the magnitude of the fatigue scores suggested good construct validity, within-protocol differences highlighted limitations with each formula. Overall, the results support the use of the percentage decrement score as the most valid and reliable measure of fatigue during brief maximal intermittent work.

Sensitivity, reliability and the effects of diurnal variation on a test battery of field usable upper limb fatigue measures.

PubMed

Yung, Marcus; Wells, Richard P

2017-07-01

Fatigue has been linked to deficits in production quality and productivity and, if of long duration, work-related musculoskeletal disorders. It may thus be a useful risk indicator and design and evaluation tool. However, there is limited information on the test-retest reliability, the sensitivity and the effects of diurnal fluctuation on field usable fatigue measures. This study reports on an evaluation of 11 measurement tools and their 14 parameters. Eight measures were found to have test-retest ICC values greater than 0.8. Four measures were particularly responsive during an intermittent fatiguing condition. However, two responsive measures demonstrated rhythmic behaviour, with significant time effects from 08:00 to mid-afternoon and early evening. Action tremor, muscle mechanomyography and perceived fatigue were found to be most reliable and most responsive; but additional analytical considerations might be required when interpreting daylong responses of MMG and action tremor. Practitioner Summary: This paper presents findings from test-retest and daylong reliability and responsiveness evaluations of 11 fatigue measures. This paper suggests that action tremor, muscle mechanomyography and perceived fatigue were most reliable and most responsive. However, mechanomyography and action tremor may be susceptible to diurnal changes.

Microstructural examination of fatigue crack tip in high strength steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuoka, C.; Yoshizawa, H.; Nakagawa, Y.G.

1993-10-01

Fatigue tests were performed to examine how microstructural conditioning influences crack initiation and propagation in SA508 class 3 low-carbon steel. A 3-mm-long crack was introduced in compact tension (CT) fatigue test specimens under four different loads in order to obtain crack tip plastic zones at different stress intensity factor ranges, [Delta]K = 18, 36, 54, and 72 MPa[radical]m. The microstructure of the plastic zones around the crack tip were examined by transmission electron microscopy (TEM) and selected area electron diffraction (SAD). Micro-orientation of the dislocation cells in the plastic zones of all of the CT samples increased to 4 degmore » from the level of an as-received sample. Four-point bending fatigue tests were performed for plate shape samples with a large cyclic strain range. The SAD value of the bending samples was also 4 deg in the damaged area where cracks already initiated at an early stage of the fatigue process. These test results indicate that the microstructural conditioning is a prerequisite for the fatigue crack initiation and propagation in SA508. These observations may lead to better understanding of how fatigue initiation processes transit to cracks.« less

Elevated temperature biaxial fatigue

NASA Technical Reports Server (NTRS)

Jordan, E. H.

1984-01-01

A three year experimental program for studying elevated temperature biaxial fatigue of a nickel based alloy Hastelloy-X has been completed. A new high temperature fatigue test facility with unique capabilities has been developed. Effort was directed toward understanding multiaxial fatigue and correlating the experimental data to the existing theories of fatigue failure. The difficult task of predicting fatigue lives for non-proportional loading was used as an ultimate test for various life prediction methods being considered. The primary means of reaching improved undertanding were through several critical non-proportional loading experiments. It was discovered that the cracking mode switched from primarily cracking on the maximum shear planes at room temperature to cracking on the maximum normal strain planes at 649 C.

Characterization of wear debris generated in accelerated rolling-element fatigue tests

NASA Technical Reports Server (NTRS)

Jones, W. R., Jr.; Parker, R. J.

1978-01-01

A ferrographic analysis was used to determine the types and quantities of wear debris generated during accelerated rolling contact fatigue tests. The five-ball rolling contact fatigue tester was used. Ball specimens were made of a corrosion resistant, high-temperature bearing steel. The lubricant was a superrefined naphthenic mineral oil. Conditions included a maximum Hertz stress of 5.52 10 to the 9th power Pa and a shaft speed of 10,000 rpm. Four types of wear debris were observed: (1) normal rubbing wear particles, (2) fatigue microspall particles, (3) spheres, and (4) friction polymer deposits. The characterization of wear debris as a function of time was of limited use in predicting fatigue failures in these accelerated tests.

Fatigue of immature baboon cortical bone.

PubMed

Keller, T S; Lovin, J D; Spengler, D M; Carter, D R

1985-01-01

Strain-controlled uniaxial fatigue and monotonic tensile tests were conducted on turned femoral cortical bone specimens obtained from baboons at various ages of maturity. Fatigue loading produced a progressive loss in stiffness and an increase in hysteresis prior to failure, indicating that immature primate cortical bone responds to repeated loading in a fashion similar to that previously observed for adult human cortical bone. Bone fatigue resistance under this strain controlled testing decreased during maturation. Maturation was also associated with an increase in bone dry density, ash fraction and elastic modulus. The higher elastic modulus of more mature bone meant that these specimens were subjected to higher stress levels during testing than more immature bone specimens. Anatomical regions along the femoral shaft exhibited differences in strength and fatigue resistance.

Influence of neutron irradiation at 430$deg;C on the fatigue properties of SA 316L steel

NASA Astrophysics Data System (ADS)

Vandermeulen, W.; Hendrix, W.; Massaut, V.; Van de Velde, J.

1988-07-01

Fatigue tests have been carried out at 430°C on hour-glass shaped specimens of the CEC reference heat of SA 316L stainless steel. The tests were performed under constant total axial strain control with a triangular fully reversed wave shape at frequencies of 0.5, 0.05 and 0.005 Hz. Specimens irradiated at 430°C to doses of 9-12 dpa and helium contents of 80 to 145 appm showed a fatigue life reduction by about a factor of two, compared to unirradiated specimens. The cyclic stress is found to be strongly increased by the irradiation. The test frequency influences the fatigue hardening slightly but it does not affect the fatigue life.

Machining of Aircraft Titanium with Abrasive-Waterjets for Fatigue Critical Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, H. T.; Hovanski, Yuri; Dahl, Michael E.

2010-10-04

Laboratory tests were conducted to determine the fatigue performance of AWJ-machined aircraft titanium. Dog-bone specimens machined with AWJs were prepared and tested with and without sanding and dry-grit blasting with Al2O3 as secondary processes. The secondary processes were applied to remove the visual appearance of AWJ-generated striations and to clean up the garnet embedment. The fatigue performance of AWJ-machined specimens was compared with baseline specimens machined with CNC milling. Fatigue test results not only confirmed the findings of the aluminum dog-bone specimens but also further enhance the fatigue performance. In addition, titanium is known to be notoriously difficult to cutmore » with contact tools while AWJs cut it 34% faster than stainless steel. AWJ cutting and dry-grit blasting are shown to be a preferred combination for processing aircraft titanium that is fatigue critical.« less

High temperature fatigue behavior of Haynes 188

NASA Technical Reports Server (NTRS)

Halford, Gary R.; Saltsman, James F.; Kalluri, Sreeramesh

1988-01-01

The high temperature, creep-fatigue behavior of Haynes 188 was investigated as an element in a broader thermomechanical fatigue life prediction model development program at the NASA-Lewis. The models are still in the development stage, but the data that were generated possess intrinsic value on their own. Results generated to date is reported. Data were generated to characterize isothermal low cycle fatigue resistance at temperatures of 316, 704, and 927 C with cyclic failure lives ranging from 10 to more than 20,000. These results follow trends that would be predicted from a knowledge of tensile properties, i.e., as the tensile ductility varies with temperature, so varies the cyclic inelastic straining capacity. Likewise, as the tensile strength decreases, so does the high cyclic fatigue resistance. A few two-minute hold-time cycles at peak compressive strain were included in tests at 760 C. These results were obtained in support of a redesign effort for the Orbital Maneuverable System engine. No detrimental effects on cyclic life were noted despite the added exposure time for creep and oxidation. Finally, a series of simulated thermal fatigue tests, referred to as bithermal fatigue tests, were conducted using 316 C as the minimum and 760 C as the maximum temperature. Only out-of-phase bithermal tests were conducted to date. These test results are intended for use as input to a more general thermomechanical fatigue life prediction model based on the concepts of the total strain version of Strainrange Partitioning.

Rolling-Element Fatigue Testing and Data Analysis - A Tutorial

NASA Technical Reports Server (NTRS)

Vlcek, Brian L.; Zaretsky, Erwin V.

2011-01-01

In order to rank bearing materials, lubricants and other design variables using rolling-element bench type fatigue testing of bearing components and full-scale rolling-element bearing tests, the investigator needs to be cognizant of the variables that affect rolling-element fatigue life and be able to maintain and control them within an acceptable experimental tolerance. Once these variables are controlled, the number of tests and the test conditions must be specified to assure reasonable statistical certainty of the final results. There is a reasonable correlation between the results from elemental test rigs with those results obtained with full-scale bearings. Using the statistical methods of W. Weibull and L. Johnson, the minimum number of tests required can be determined. This paper brings together and discusses the technical aspects of rolling-element fatigue testing and data analysis as well as making recommendations to assure quality and reliable testing of rolling-element specimens and full-scale rolling-element bearings.

Advanced composite stabilizer for Boeing 737 aircraft

NASA Technical Reports Server (NTRS)

1978-01-01

Activities related to development of an advanced composites stabilizer for the Boeing 737 commercial transport are reported. Activities include discussion of criteria and objectives, design loads, the fatigue spectrum definition to be used for all spectrum fatigue testing, fatigue analysis, manufacturing producibility studies, the ancillary test program, quality assurance, and manufacturing development.

Endurance and fatigue characteristics in the neck muscles during sub-maximal isometric test in patients with cervical radiculopathy.

PubMed

Halvorsen, Marie; Abbott, Allan; Peolsson, Anneli; Dedering, Åsa

2014-03-01

The aim of the study was to compare myoelectric manifestation in neck muscle endurance and fatigue characteristics during sub-maximal isometric endurance test in patients with cervical radiculopathy and asymptomatic subjects. An additional aim was to explore associations between primary neck muscle endurance, myoelectric fatigability, and self-rated levels of fatigue, pain and subjective health measurements in patients with cervical radiculopathy. Muscle fatigue in the ventral and dorsal neck muscles was assessed in patients with cervical radiculopathy and in an asymptomatic group during an isometric neck muscle endurance test in prone and supine. 46 patients and 34 asymptomatic subjects participated. Surface electromyography signals were recorded from the sternocleidomastoid, cervical paraspinal muscles and upper and middle trapezius bilaterally during the endurance test. Subjective health measurements were assessed with questionnaires. The results showed altered neck muscle endurance in several of the muscles investigated with greater negative median frequency slope, greater variability, side imbalance, lower endurance time and higher experience of fatigue among the cervical radiculopathy patients compared with healthy subjects. Endurance times were significantly lower in both prone and in supine positions between the patients compared to asymptomatic subjects. During the neck muscle endurance test, fatigues in the upper trapezius muscles during the prone test and in the sternocleidomastoid muscles during the supine test were of more importance than self-perceived pain, fatigue, disability and kinesiophobia in predicting neck muscle endurance (NME). NME testing in the primary neck muscles seems to be an important factor to take into consideration in rehabilitation.

Effects of stress ratio on the temperature-dependent high-cycle fatigue properties of alloy steels

NASA Astrophysics Data System (ADS)

Lü, Zhi-yang; Wan, Ao-shuang; Xiong, Jun-jiang; Li, Kuang; Liu, Jian-zhong

2016-12-01

This paper addresses the effects of stress ratio on the temperature-dependent high-cycle fatigue (HCF) properties of alloy steels 2CrMo and 9CrCo, which suffer from substantial vibrational loading at small stress amplitude, high stress ratio, and high frequency in the high-temperature environments in which they function as blade and rotor spindle materials in advanced gas or steam turbine engines. Fatigue tests were performed on alloy steels 2CrMo and 9CrCo subjected to constant-amplitude loading at four stress ratios and at four and three temperatures, respectively, to determine their temperature-dependent HCF properties. The interaction mechanisms between high temperature and stress ratio were deduced and compared with each other on the basis of the results of fractographic analysis. A phenomenological model was developed to evaluate the effects of stress ratio on the temperature-dependent HCF properties of alloy steels 2CrMo and 9CrCo. Good correlation was achieved between the predictions and actual experiments, demonstrating the practical and effective use of the proposed method.

Scanning and Transmission Electron Microscopy of High Temperature Materials

NASA Technical Reports Server (NTRS)

1994-01-01

Software and hardware updates to further extend the capability of the electron microscope were carried out. A range of materials such as intermetallics, metal-matrix composites, ceramic-matrix composites, ceramics and intermetallic compounds, based on refractory elements were examined under this research. Crystal structure, size, shape and volume fraction distribution of various phases which constitute the microstructures were examined. Deformed materials were studied to understand the effect of interfacial microstructure on the deformation and fracture behavior of these materials. Specimens tested for a range of mechanical property requirements, such as stress rupture, creep, low cycle fatigue, high cycle fatigue, thermomechanical fatigue, etc. were examined. Microstructural and microchemical stability of these materials exposed to simulated operating environments were investigated. The EOIM Shuttle post-flight samples were also examined to understand the influence of low gravity processing on microstructure. In addition, fractographic analyses of Nb-Zr-W, titanium aluminide, molybdenum silicide and silicon carbide samples were carried out. Extensive characterization of sapphire fibers in the fiber-reinforced composites made by powder cloth processing was made. Finally, pressure infiltration casting of metal-matrix composites was carried out.

Transverse Tension Fatigue Life Characterization Through Flexure Testing of Composite Materials

NASA Technical Reports Server (NTRS)

OBrien, T. Kevin; Chawan, Arun D.; Krueger, Ronald; Paris, Isabelle

2001-01-01

The transverse tension fatigue life of S2/8552 glass-epoxy and IM7/8552 carbon-epoxy was characterized using flexure tests of 90-degree laminates loaded in 3-point and 4-point bending. The influence of specimen polishing and specimen configuration on transverse tension fatigue life was examined using the glass-epoxy laminates. Results showed that 90-degree bend specimens with polished machined edges and polished tension-side surfaces, where bending failures where observed, had lower fatigue lives than unpolished specimens when cyclically loaded at equal stress levels. The influence of specimen thickness and the utility of a Weibull scaling law was examined using the carbon-epoxy laminates. The influence of test frequency on fatigue results was also documented for the 4-point bending configuration. A Weibull scaling law was used to predict the 4-point bending fatigue lives from the 3-point bending curve fit and vice-versa. Scaling was performed based on maximum cyclic stress level as well as fatigue life. The scaling laws based on stress level shifted the curve fit S-N characterizations in the desired direction, however, the magnitude of the shift was not adequate to accurately predict the fatigue lives. Furthermore, the scaling law based on fatigue life shifted the curve fit S-N characterizations in the opposite direction from measured values. Therefore, these scaling laws were not adequate for obtaining accurate predictions of the transverse tension fatigue lives.

Muscle contractile characteristics: relationship to high-intensity exercise.

PubMed

Morris, Martyn G; Dawes, Helen; Howells, Ken; Scott, Oona M; Cramp, Mary; Izadi, Hooshang

2010-09-01

We investigated the relationship between muscle contractile characteristics, collected using percutaneous electrical stimulation, and high-intensity exercise performance. Seventeen participants performed a muscle performance test for the calculation of rate of torque development (RTD), rate of relaxation (RR(1/2)), rate of fatigue and fatigue resistance. On a second visit the participants completed a Wingate cycle ergometer test with peak power, mean power, fatigue index and fatigue rate calculated. The muscle fatigue index related significantly to the WAnT fatigue index and fatigue rate (p < 0.01). The change in rate of torque development (%DeltaRTD) was also related significantly to the fatigue rate (W/s) during the WAnT. Subjects displaying the greatest reduction in RTD had the greatest fatigue rate during the WAnT and greater fatigue during the electrical stimulation protocol. There were no significant relationships between peak (r 0.36; p > 0.01) or mean power (r -0.11, p > 0.01) with any of the muscle performance measures. These findings demonstrate that muscle contractile characteristics, elicited during standardised in vivo electrical stimulation, relate to performance during a Wingate anaerobic test. They suggest that muscle contraction characteristics play an important role in high-intensity exercise performance and indicate that electrical stimulation protocols can be a useful additional tool to explore muscle contraction characteristics in relation to exercise performance and trainability.

Fatigue and durability of Nitinol stents.

PubMed

Pelton, A R; Schroeder, V; Mitchell, M R; Gong, Xiao-Yan; Barney, M; Robertson, S W

2008-04-01

Nitinol self-expanding stents are effective in treating peripheral artery disease, including the superficial femoral, carotid, and renal arteries. However, fracture occurrences of up to 50% have been reported in some stents after one year. These stent fractures are likely due to in vivo cyclic displacements. As such, the cyclic fatigue and durability properties of Nitinol-based endovascular stents are discussed in terms of an engineering-based experimental testing program. In this paper, the combined effects of cardiac pulsatile fatigue and stent-vessel oversizing are evaluated for application to both stents and stent subcomponents. In particular, displacement-controlled fatigue tests were performed on stent-like specimens processed from Nitinol microtubing. Fatigue data were collected with combinations of simulated oversizing conditions and pulsatile cycles that were identified by computer modeling of the stent that mimic in vivo deformation conditions. These data are analyzed with non-linear finite element computations and are illustrated with strain-life and strain-based constant-life diagrams. The utility of this approach is demonstrated in conjunction with 10 million cycle pulsatile fatigue tests of Cordis SMART Control((R)) Nitinol self-expanding stents to calculate fatigue safety factors and thereby predict in vivo fatigue resistance. These results demonstrate the non-linear constant fatigue-life response of Nitinol stents, whereby, contrary to conventional engineering materials, the fatigue life of Nitinol is observed to increase with increasing mean strain.

Use of atomic force microscopy for characterizing damage evolution during fatigue

NASA Astrophysics Data System (ADS)

Cretegny, Laurent

2000-10-01

A study of the development of surface fatigue damage in PH 13-8 Mo stainless steel and copper by atomic force microscopy (AFM) was performed. AFM observations allow highly automated, quantitative characterization of surface deformation with a resolution of 5 nm or better, which is ideal for understanding fatigue damage evolution. A secondary objective was to establish a correlation between fatigue life exhausted and impedance spectroscopy. Strain controlled fatigue tests were conducted both in high and low cycle fatigue regimes, and interruptions of the fatigue tests allowed characterizing the evolution of the surface upset at various life-fractions. In the low strain amplitude tests on stainless steel (Deltaepsilonpl/2 = 0.0026%), surface damage occurred in the shape of narrow streaks at the interface between martensite laths where reverted austenite was present. The streaks eventually coalesced to form crack nuclei. In high strain amplitude tests (Deltaepsilon pl/2 = 0.049%), fatigue surface damage was essentially dominated by the formation of extrusions. In copper, both low (Deltaepsilonpl/2 = 0.061%) and high (Deltaepsilonpl/2 = 0.134%) strain amplitude tests showed the formation of slip bands (mainly extrusions) across entire grains. Protrusions were present only in copper specimens tested at the high strain amplitude. Crack nucleation in the low strain amplitude tests occurred in both materials at the interface between a region that sustained a high level of deformation and one with little evidence of surface upset. This commonality between these two materials that are otherwise very dissimilar in nature suggests a universal scheme for location of fatigue crack nucleation sites during HCF. A procedure was developed in this study to quantitatively characterize the amount of irreversible surface strain. The proposed formalism is applicable to any material, independently of the type of surface damage, and leads to a criterion for crack nucleation based on physical evidence of surface damage. A correlation between fatigue damage and impedance spectroscopy measurements was shown in copper, in particular during the primary cyclic hardening stage. The measurements were however less sensitive to the development of surface upset that occurred beyond that stage.

Reference values for fatigued versus non-fatigued limb symmetry index measured by a newly designed single-leg hop test battery in healthy subjects: a pilot study.

PubMed

Leister, Iris; Mattiassich, Georg; Kindermann, Harald; Ortmaier, Reinhold; Barthofer, Jürgen; Vasvary, Imre; Katzensteiner, Klaus; Stelzhammer, Christine; Kulnik, Stefan Tino

2018-01-01

There is sparse evidence for return to sport criteria after knee injury. Functional performance deficits, particularly in fatigued muscular condition, should be verified prior to the attempt to return to high-risk pivoting sports. The purpose of this study was to generate reference values for the limb symmetry index (LSI) of healthy subjects in fatigued and non-fatigued muscular condition in a newly designed test battery. Forty-two healthy subjects [22 females, 20 males; mean (SD) age 30.4 (6.6) years] were evaluated using a test battery consisting of an isometric strength test, a series of five single-leg hop tests and an integrated fatigue protocol. Subjective physical activity was assessed with the Tegner Activity Scale (TAS). The cut-off values for healthy subjects were calculated considering the fifth percentile as the minimum reference value for the LSI and single-leg hop distance. The mean (SD) overall LSI was 98.8% (4.6). No significant gender or age specific differences in limb symmetry were observed. The comparison of the non-fatigued LSI with the overall LSI revealed no clinically relevant change due to muscular fatigue. Repeated measures ANOVA revealed a significant within effect on fatigue/non-fatigue condition ( F (1,38)  = 18.000; p  < 0.001, η 2  = 0.321) on absolute single-leg hop distance. Moreover, a significant between effect on the TAS-parameter ( F (1,38)  = 5.928; p  = 0.020, η 2  = 0.135 between: TAS ≤ 5/TAS > 5) and on gender ( F (1,38)  = 23.956; p  < 0.001, η 2  = 0.387) could be detected. The absolute jumping distance in the single-leg hop for distance was significantly reduced due to fatigue. No clinically relevant effect of muscular fatigue was observed on limb symmetry in our study sample. Gender and physical activity are important factors to be considered when interpreting reference values.

The Relationships Between Microstructure, Tensile Properties and Fatigue Life in Ti-5Al-5V-5Mo-3Cr-0.4Fe (Ti-5553)

NASA Astrophysics Data System (ADS)

Foltz, John W., IV

beta-titanium alloys are being increasingly used in airframes as a way to decrease the weight of the aircraft. As a result of this movement, Ti-5Al-5V-5Mo-3Cr-0.4Fe (Timetal 555), a high-strength beta titanium alloy, is being used on the current generation of landing gear. This alloy features good combinations of strength, ductility, toughness and fatigue life in alpha+beta processed conditions, but little is known about beta-processed conditions. Recent work by the Center for the Accelerated Maturation of Materials (CAMM) research group at The Ohio State University has improved the tensile property knowledge base for beta-processed conditions in this alloy, and this thesis augments the aforementioned development with description of how microstructure affects fatigue life. In this work, beta-processed microstructures have been produced in a Gleeble(TM) thermomechanical simulator and subsequently characterized with a combination of electron and optical microscopy techniques. Four-point bending fatigue tests have been carried out on the material to characterize fatigue life. All the microstructural conditions have been fatigue tested with the maximum test stress equal to 90% of the measured yield strength. The subsequent results from tensile tests, fatigue tests, and microstructural quantification have been analyzed using Bayesian neural networks in an attempt to predict fatigue life using microstructural and tensile inputs. Good correlation has been developed between lifetime predictions and experimental results using microstructure and tensile inputs. Trained Bayesian neural networks have also been used in a predictive fashion to explore functional dependencies between these inputs and fatigue life. In this work, one section discusses the thermal treatments that led to the observed microstructures, and the possible sequence of precipitation that led to these microstructures. The thesis then describes the implications of microstructure on fatigue life and implications of tensile properties on fatigue life. Several additional experiments are then described that highlight possible causes for the observed dependence of microstructure on fatigue life, including fractographic evidence to provide support of microstructural dependencies.

Effect of lubricant extreme-pressure additives on surface fatigue life of AISI 9310 spur gears

NASA Technical Reports Server (NTRS)

Scibbe, H. W.; Townsend, D. P.; Aron, P. R.

1984-01-01

Surface fatigue tests were conducted with AISI 9310 spur gears using a formulated synthetic tetraester oil (conforming to MIL-L-23699 specifications) as the lubricant containing either sulfur or phosphorus as the EP additive. Four groups of gears were tested. One group of gears tested without an additive in the lubricant acted as the reference oil. In the other three groups either a 0.1 wt % sulfur or phosphorus additive was added to the tetraester oil to enhance gear surface fatigue life. Test conditions included a gear temperature of 334 K (160 F), a maximum Hertz stress of 1.71 GPa (248 000 psi), and a speed of 10,000 rpm. The gears tested with a 0.1 wt % phosphorus additive showed pitting fatigue life 2.6 times the life of gears tested with the reference tetraester based oil. Although fatigue lives of two groups of gears tested with the sulfur additive in the oil showed improvement over the control group gear life, the results, unlike those obtained with the phosphorus oil, were not considered to be statistically significant.

Effect of interlaminar normal stresses on the uniaxial zero-to-tension fatigue behavior of graphite/epoxy tubes

NASA Technical Reports Server (NTRS)

Krempl, Erhard; An, Deukman

1991-01-01

Fatigue tests conducted with and without internal pressure have been found to possess approximately the same fatigue life as (+/-45)s graphite/epoxy tubes for zero-to-tension axial load-controlled conditions on an axial torsion servohydraulic apparatus. These tests therefore cannot be considered as confirmations of the suspected detrimental effect of interlaminar tensile stresses on the fatigue performance of thin-walled tubes. The addition of 90-deg plies on both the inside and the outside is found to significantly improve the tubes' static and fatigue strengths.

Reliability improvement of wire bonds subjected to fatigue stresses.

NASA Technical Reports Server (NTRS)

Ravi, K. V.; Philofsky, E. M.

1972-01-01

The failure of wire bonds due to repeated flexure when semiconductor devices are operated in an on-off mode has been investigated. An accelerated fatigue testing apparatus was constructed and the major fatigue variables, aluminum alloy composition, and bonding mechanism, were tested. The data showed Al-1% Mg wires to exhibit superior fatigue characteristics compared to Al-1% Cu or Al-1% Si and ultrasonic bonding to be better than thermocompression bonding for fatigue resistance. Based on these results highly reliable devices were fabricated using Al-1% Mg wire with ultrasonic bonding which withstood 120,000 power cycles with no failures.

Laser High-Cycle Thermal Fatigue of Pulse Detonation Engine Combustor Materials Tested

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Fox, Dennis S.; Miller, Robert A.

2001-01-01

Pulse detonation engines (PDE's) have received increasing attention for future aerospace propulsion applications. Because the PDE is designed for a high-frequency, intermittent detonation combustion process, extremely high gas temperatures and pressures can be realized under the nearly constant-volume combustion environment. The PDE's can potentially achieve higher thermodynamic cycle efficiency and thrust density in comparison to traditional constant-pressure combustion gas turbine engines (ref. 1). However, the development of these engines requires robust design of the engine components that must endure harsh detonation environments. In particular, the detonation combustor chamber, which is designed to sustain and confine the detonation combustion process, will experience high pressure and temperature pulses with very short durations (refs. 2 and 3). Therefore, it is of great importance to evaluate PDE combustor materials and components under simulated engine temperatures and stress conditions in the laboratory. In this study, a high-cycle thermal fatigue test rig was established at the NASA Glenn Research Center using a 1.5-kW CO2 laser. The high-power laser, operating in the pulsed mode, can be controlled at various pulse energy levels and waveform distributions. The enhanced laser pulses can be used to mimic the time-dependent temperature and pressure waves encountered in a pulsed detonation engine. Under the enhanced laser pulse condition, a maximum 7.5-kW peak power with a duration of approximately 0.1 to 0.2 msec (a spike) can be achieved, followed by a plateau region that has about one-fifth of the maximum power level with several milliseconds duration. The laser thermal fatigue rig has also been developed to adopt flat and rotating tubular specimen configurations for the simulated engine tests. More sophisticated laser optic systems can be used to simulate the spatial distributions of the temperature and shock waves in the engine. Pulse laser high-cycle thermal fatigue behavior has been investigated on a flat Haynes 188 alloy specimen, under the test condition of 30-Hz cycle frequency (33-msec pulse period and 10-msec pulse width including a 0.2-msec pulse spike; ref. 4). Temperature distributions were calculated with one-dimensional finite difference models. The calculations show that that the 0.2-msec pulse spike can cause an additional 40 C temperature fluctuation with an interaction depth of 0.08 mm near the specimen surface region. This temperature swing will be superimposed onto the temperature swing of 80 C that is induced by the 10-msec laser pulse near the 0.53-mm-deep surface interaction region.

Developing software to "track and catch" missed follow-up of abnormal test results in a complex sociotechnical environment.

PubMed

Smith, M; Murphy, D; Laxmisan, A; Sittig, D; Reis, B; Esquivel, A; Singh, H

2013-01-01

Abnormal test results do not always receive timely follow-up, even when providers are notified through electronic health record (EHR)-based alerts. High workload, alert fatigue, and other demands on attention disrupt a provider's prospective memory for tasks required to initiate follow-up. Thus, EHR-based tracking and reminding functionalities are needed to improve follow-up. The purpose of this study was to develop a decision-support software prototype enabling individual and system-wide tracking of abnormal test result alerts lacking follow-up, and to conduct formative evaluations, including usability testing. We developed a working prototype software system, the Alert Watch And Response Engine (AWARE), to detect abnormal test result alerts lacking documented follow-up, and to present context-specific reminders to providers. Development and testing took place within the VA's EHR and focused on four cancer-related abnormal test results. Design concepts emphasized mitigating the effects of high workload and alert fatigue while being minimally intrusive. We conducted a multifaceted formative evaluation of the software, addressing fit within the larger socio-technical system. Evaluations included usability testing with the prototype and interview questions about organizational and workflow factors. Participants included 23 physicians, 9 clinical information technology specialists, and 8 quality/safety managers. Evaluation results indicated that our software prototype fit within the technical environment and clinical workflow, and physicians were able to use it successfully. Quality/safety managers reported that the tool would be useful in future quality assurance activities to detect patients who lack documented follow-up. Additionally, we successfully installed the software on the local facility's "test" EHR system, thus demonstrating technical compatibility. To address the factors involved in missed test results, we developed a software prototype to account for technical, usability, organizational, and workflow needs. Our evaluation has shown the feasibility of the prototype as a means of facilitating better follow-up for cancer-related abnormal test results.

Damage mechanisms in bithermal and thermomechanical fatigue of Haynes 188

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Halford, Gary R.

1992-01-01

Post failure fractographic and metallographic studies were conducted on Haynes 188 specimens fatigued under bithermal and thermomechanical loading conditions between 316 and 760 C. Bithermal fatigue specimens examined included those tested under high strain rate in-phase and out-phase, tensile creep in-phase, and compressive creep out-of-phase loading conditions. Specimens tested under in-phase and out-of-phase thermomechanical fatigue were also examined. The nature of failure mode (transgrandular versus intergranular), the topography of the fracture surface, and the roles of oxidation and metallurgical changes were studied for each type of bithermal and thermomechanical test.

Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 Under Biaxial and Uniaxial Fatigue

DTIC Science & Technology

2014-06-19

al. examined the effect of biaxial loading on the fatigue crack growth [52]. They conducted their fatigue tests on SUS 304 stainless steel using a...specimens. Their experiments were carried out on cruciform test coupons using a digitally controlled four actuator biaxial testing system. Steel ...as shown in Figure 3.7. The test specimen was placed between two stainless steel chambers. These chambers were connected together using screws, and

Overload and Underload Effects on the Fatigue Crack Growth Behavior of the 2024-T3 Aluminum Alloy

NASA Technical Reports Server (NTRS)

Dawicke, David S.

1997-01-01

Fatigue crack growth tests were conducted on 0.09 inch thick, 3.0 inch wide middle-crack tension specimens cut from sheets of 2024-T3 aluminum alloy. The tests were conducted using a load sequence that consisted of a single block of 2,500 cycles of constant amplitude loading followed by an overload/underload combination. The largest fatigue crack growth life occurred for the tests with the overload stress equal to 2 times the constant amplitude stress and the underload stress equal to the constant amplitude minimum stress. For the tests with compressive underloads, the fatigue crack growth life decreased with increasing compressive underload stress.