Physico-mechanical properties and prosthodontic applications of Co-Cr dental alloys: a review of the literature

PubMed Central

2014-01-01

Cobalt-Chromium (Co-Cr) alloys are classified as predominantly base-metal alloys and are widely known for their biomedical applications in the orthopedic and dental fields. In dentistry, Co-Cr alloys are commonly used for the fabrication of metallic frameworks of removable partial dentures and recently have been used as metallic substructures for the fabrication of porcelain-fused-to-metal restorations and implant frameworks. The increased worldwide interest in utilizing Co-Cr alloys for dental applications is related to their low cost and adequate physico-mechanical properties. Additionally, among base-metal alloys, Co-Cr alloys are used more frequently in many countries to replace Nickel-Chromium (Ni-Cr) alloys. This is mainly due to the increased concern regarding the toxic effects of Ni on the human body when alloys containing Ni are exposed to the oral cavity. This review article describes dental applications, metallurgical characterization, and physico-mechanical properties of Co-Cr alloys and also addresses their clinical and laboratory behavior in relation to those properties. PMID:24843400

Osseointegration of surface-blasted implants made of titanium alloy and cobalt-chromium alloy in a rabbit intramedullary model.

PubMed

Jinno, T; Goldberg, V M; Davy, D; Stevenson, S

1998-10-01

The purpose of this study was to compare the osseointegration of surface-blasted Ti6A14V and CoCr implants in vivo. Ti6A14V and CoCr rods blasted with 710 microm A12O3 particles were bilaterally press-fit into the medullary space of distal femora of 24 rabbits. Evaluation was made radiographically, histologically, histomorphometrically (3, 6, and 12 weeks after implantation), and mechanically (12 weeks). Both Ti6A14V and CoCr implants demonstrated good biocompatibility radiographically and histologically. Toluidine blue-stained sections revealed an osteoconductive effect of the blasted surface, and fluorochrome labeling analysis showed active bone formation at the bone-implant interface at as late as 12 weeks for both specimens. CoCr showed significantly lower interfacial shear strength than Ti6A14V although the bone contact area with the implant surface was comparable and no intervening soft tissue at the bone-implant interface could be seen for either implant by scanning electron microscopy backscatter analysis. Unmineralized tissue (cartilage and osteoid) was observed more frequently on the CoCr surface than on the Ti6A14V surface. These data show less osseointegration of CoCr implants with this blasted surface for this short period, possibly due to a slight difference in surface roughness and some negative effects of CoCr on bone attachment.

Impact of Dynamic Specimen Shape Evolution on the Atom Probe Tomography Results of Doped Epitaxial Oxide Multilayers: Comparison of Experiment and Simulation

DOE PAGES

Madaan, Nitesh; Bao, Jie; Nandasiri, Manjula I.; ...

2015-08-31

The experimental atom probe tomography results from two different specimen orientations (top-down and side-ways) of a high oxygen ion conducting Samaria-doped-ceria/Scandia-stabilized-zirconia multilayer thin film solid oxide fuel cell electrolyte was correlated with level-set method based field evaporation simulations for the same specimen orientations. This experiment-theory correlation explains the dynamic specimen shape evolution and ion trajectory aberrations that can induce density artifacts in final reconstruction leading to inaccurate estimation of interfacial intermixing. This study highlights the need and importance of correlating experimental results with field evaporation simulations when using atom probe tomography for studying oxide heterostructure interfaces.

Seed/catalyst-free growth of zinc oxide nanostructures on multilayer graphene by thermal evaporation

PubMed Central

2014-01-01

We report the seed/catalyst-free growth of ZnO on multilayer graphene by thermal evaporation of Zn in the presence of O2 gas. The effects of substrate temperatures were studied. The changes of morphologies were very significant where the grown ZnO structures show three different structures, i.e., nanoclusters, nanorods, and thin films at 600°C, 800°C, and 1,000°C, respectively. High-density vertically aligned ZnO nanorods comparable to other methods were obtained. A growth mechanism was proposed based on the obtained results. The ZnO/graphene hybrid structure provides several potential applications in electronics and optoelectronics. PMID:24533793

Performance of multilayer coated diffraction gratings in the EUV

NASA Technical Reports Server (NTRS)

Keski-Kuha, Ritva A. M.; Thomas, Roger J.; Gum, Jeffrey S.; Condor, Charles E.

1990-01-01

The effect of multilayer coating application on the performance of a diffraction grating in the EUV spectral region was evaluated by examining the performance of a 3600-line/mm and a 1200-line/mm replica blazed gratings, designed for operation in the 300-A spectral region in first order. A ten-layer IrSi multilayer optimized for 304 A was deposited using electron-beam evaporation. The grating efficiency was measured on the SURF II calibration beamline in a chamber designed for calibrating the solar EUV rocket telescope and spectrograph multilayer coatings. A significant (by a factor of about 7) enhancement in grating efficiency in the 300-A region was demonstrated.

Hybrid Physical Vapor Deposition Instrument for Advanced Functional Multilayers and Materials

DTIC Science & Technology

2016-04-27

Hybrid Physical Vapor Deposition Instrument for Advanced Functional Multilayers and Materials PI Maria received support to construct a physical...vapor deposition (PVD) system that combines electron beam (e- beam) evaporation, magnetron sputtering, pulsed laser ablation, and ion-assisted deposition ...The instrumentation enables clean, uniform, and rapid deposition of a wide variety of metallic, semiconducting, and ceramic thin films with

Hybrid Physical Vapor Deposition Instrument for Advanced Functional Multilayers and Materials

DTIC Science & Technology

2016-04-27

Hybrid Physical Vapor Deposition Instrument for Advanced Functional Multilayers and Materials PI Maria received support to construct a physical... vapor deposition (PVD) system that combines electron beam (e- beam) evaporation, magnetron sputtering, pulsed laser ablation, and ion-assisted deposition ...peer-reviewed journals: Number of Papers published in non peer-reviewed journals: Final Report: Hybrid Physical Vapor Deposition Instrument for Advanced

Optimization of TiO2/Cu/TiO2 multilayers as a transparent composite electrode deposited by electron-beam evaporation at room temperature

NASA Astrophysics Data System (ADS)

Sun, Hong-Tao; Wang, Xiao-Ping; Kou, Zhi-Qi; Wang, Li-Jun; Wang, Jin-Ye; Sun, Yi-Qing

2015-04-01

Highly transparent indium-free composite electrodes of TiO2/Cu/TiO2 are deposited by electron-beam evaporation at room temperature. The effects of Cu thickness and annealing temperature on the electrical and optical properties of the multilayer film are investigated. The critical thickness of Cu mid-layer to form a continuous conducting layer is found to be 11 nm. The multilayer with a mid-Cu thickness of 11 nm is optimized to obtain a resistivity of 7.4×10-5 Ω·cm and an average optical transmittance of 86% in the visible spectral range. The figure of merit of the TiO2/Cu(11 nm)/TiO2 multilayer annealed at 150 °C reaches a minimum resistivity of 5.9×10-5 Ω·cm and an average optical transmittance of 88% in the visible spectral range. The experimental results indicate that TiO2/Cu/TiO2 multilayers can be used as a transparent electrode for solar cell and other display applications. Project supported by the Research Innovation Key Project of Education Committee of Shanghai, China (Grant No. 14ZZ137) and the National Cultivation Fund from University of Shanghai for Science and Technology (Grant No. 14XPM04).

Electrochemical corrosion behaviour of dental/implant alloys in saline medium.

PubMed

Sharma, Mohit; Kumar, A V Ramesh; Singh, Nirbhay

2008-07-01

Dental alloys implanted in mouth are exposed to various aggressive conditions. Keeping this in view, corrosion behaviour of various dental alloys viz. Ni-Cr, Co-Cr, Cu-Ni-Al and commercially pure Ti (c.p. Ti) were studied in 3% NaCl medium by using Tafel polarization, cyclic polarization and electrochemical impedance spectroscopy techniques. EIS studies were carried out for different duration viz. 1 h, 1 day and 7 days to evaluate the stability of passive film and change in corrosion characteristics with time. It has been found that for Ni-Cr, Co-Cr (DRDO developed) and c.p. Ti the passive film characteristic changed with time whereas for Co-Cr (commercial) and Cu-Ni-Al alloys, the passive film characteristics remained same. From DC electrochemical studies various parameters viz. i(corr), E(corr), i(pass), E(pass) were evaluated. The corrosion rates were observed to be in the order Cu-Ni-Al > Co-Cr (commercial) > Ni-Cr > c.p. Ti > Co-Cr (DRDO).

Performance assessment of femoral knee components made from cobalt-chromium alloy and oxidized zirconium.

PubMed

Brandt, J-M; Guenther, L; O'Brien, S; Vecherya, A; Turgeon, T R; Bohm, E R

2013-12-01

The surface characteristics of the femoral component affect polyethylene wear in modular total knee replacements. In the present retrieval study, the surface characteristics of cobalt-chromium (CoCr) alloy and oxidized zirconium (OxZr) femoral components were assessed and compared. Twenty-six retrieved CoCr alloy femoral components were matched with twenty-six retrieved OxZr femoral components for implantation period, body-mass index, patient gender, implant type, and polyethylene insert thickness. The surface damage on the retrieved femoral components was evaluated using a semi-quantitative assessment method, scanning electron microscopy, and contact profilometry. The retrieved CoCr alloy femoral components showed less posterior surface gouging than OxZr femoral components; however, at a higher magnification, the grooving damage features on the retrieved CoCr alloy femoral components confirmed an abrasive wear mechanism. The surface roughness values Rp, Rpm, and Rpk for the retrieved CoCr alloy femoral components were found to be significantly higher than those of the retrieved OxZr femoral components (p≤0.031). The surface roughness values were higher on the medial condyles than on the lateral condyles of the retrieved CoCr alloy femoral components; such a difference was not observed on the retrieved OxZr femoral components. The surface roughness of CoCr alloy femoral components increased while the surface roughness of the OxZr femoral components remained unchanged after in vivo service. Therefore, the OxZr femoral components' resistance to abrasive wear may enable lower polyethylene wear and ensure long-term durability in vivo. Level IV. Crown Copyright © 2013. Published by Elsevier B.V. All rights reserved.

Titanium vs cobalt chromium: what is the best rod material to enhance adolescent idiopathic scoliosis correction with sublaminar bands?

PubMed

Angelliaume, Audrey; Ferrero, E; Mazda, K; Le Hanneur, M; Accabled, F; de Gauzy, J Sales; Ilharreborde, B

2017-06-01

Cobalt chromium (CoCr) rods have recently gained popularity in adolescent idiopathic scoliosis (AIS) surgical treatment, replacing titanium (Ti) rods, with promising frontal correction rates in all-screw constructs. Posteromedial translation has been shown to emphasize thoracic sagittal correction, but the influence of rod material in this correction technique has never been investigated. The aim of this study was to compare the postoperative correction between Ti and CoCr rods for the treatment of thoracic AIS using posteromedial translation technique. 70 patients operated for thoracic (Lenke 1 or 2) AIS, in 2 institutions, between 2010 and 2013, were included. All patients underwent posterior fusion with hybrid constructs using posteromedial translation technique. The only difference between groups in the surgical procedure was the rod material (Ti or CoCr rods). Radiological measurements were compared preoperatively, postoperatively and at last follow-up (minimum 2 years). Preoperatively, groups were similar in terms of coronal and sagittal parameters. Postoperatively, no significant difference was observed between Ti and CoCr regarding frontal corrections, even when the preoperative flexibility of the curves was taken into account (p = 0.13). CoCr rods allowed greater restoration of T4T12 thoracic kyphosis, which remained stable over time (p = 0.01). Most common postoperative complication was proximal junctional kyphosis (n = 4). However, no significant difference was found between groups regarding postoperative complications rate. CoCr and Ti rods both provide significant and stable frontal correction in AIS treated with posteromedial translation technique using hybrid constructs. However, CoCr might be considered to emphasize sagittal correction in hypokyphotic patients.

Magnetocaloric effect in cubic spinel Co(Cr0.95Fe0.05)2O4

NASA Astrophysics Data System (ADS)

Kumar, Ram; Rayaprol, S.; Xiao, Y.; Ji, W.; Siruguri, V.; Pal, D.

2018-04-01

The crystal structure, magnetic properties and magnetocaloric effect (MCE) of Co(Cr0.95Fe0.05)2O4 have been studied. Co(Cr0.95Fe0.05)2O4 synthesized by solid-state reaction method, crystallizes in normal cubic spinel structure with Fd-3m space group. Neutron powder diffraction (NPD) and magnetic measurements when compared to the undoped CoCr2O4, show that the compound is ferrimagnetic (FIM) and transition temperature (TC) is enhanced due to Fe substitution. Analysis of structural and magnetic properties shows the existence of two different sites of magnetic clusters due to Fe/Cr cation disorder. The competition between the moments of the two different sub-lattices gives rise to the temperature induced magnetization reversal at compensation tempearature (Tcomp) = 44 K. The magnetocaloric effect (simply the change in magnetic entropy i.e, -ΔSM) has been observed in Co(Cr0.95Fe0.05)2O4 with different applied magnetic fields (max. H = 90 kOe). We found maximum change of magnetic entropy ˜1.2 J/kg K, for a field change of 90 kOe at FIM transition temperature (TC˜110 K) with relative cooling power (RCP) of ˜13 J/kg. Moreover, the sign change of -ΔSM across the compensation temperature (Tcomp˜ 44 K) shows another phase transition across Tcomp in Co(Cr0.95Fe0.05)2O4. The values of MCE and RCP are also appreciable so as to consider Co(Cr0.95Fe0.05)2O4 as a magnetic refrigerant above liquid nitrogen temperature.

Repair of high performance multilayer coatings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gaines, D.P.; Ceglio, N.M.; Vernon, S.P.

1991-07-01

Fabrication and environmental damage issues may require that the multilayer x-ray reflection coatings used in soft x-ray projection lithography be replaced or repaired. Two repair strategies were investigated. The first was to overcoat defective multilayers with a new multilayer. The feasibility of this approach was demonstrated by depositing high reflectivity (61% at 130 {Angstrom}) molybdenum silicon (Mo/Si) multilayers onto fused silica figured optics that had already been coated with a Mo/Si multilayer. Because some types of damage mechanisms and fabrication errors are not repairable by this method, a second method of repair was investigated. The multilayer was stripped from themore » optical substrate by etching a release layer which was deposited onto the substrate beneath the multilayer. The release layer consisted of a 1000 {Angstrom} aluminum film deposited by ion beam sputtering or by electron beam evaporation, with a 300 {Angstrom} SiO{sub 2} protective overcoat. The substrates were superpolished zerodur optical flats. The normal incidence x-ray reflectivity of multilayers deposited on these aluminized substrates was degraded, presumably due to the roughness of the aluminum films. Multilayers, and the underlying release layers, have been removed without damaging the substrates.« less

Stress analysis of ZrO2/SiO2 multilayers deposited on different substrates with different thickness periods

NASA Astrophysics Data System (ADS)

Shao, Shuying; Shao, Jianda; He, Hongbo; Fan, Zhengxiu

2005-08-01

The effects of repeating thickness periods on stress are studied in ZrO2/SiO2 multilayers deposited by electron-beam evaporation on BK7 glass and fused-silica substrates. The results show that the residual stress is compressive and decreases with an increase of the periods of repeating thickness in the ZrO2/SiO2 multilayers. At the same time, the residual stress in multilayers deposited on BK7 glass is less than that of samples deposited on fused silica. The variation of the microstructure examined by x-ray diffraction shows that microscopic deformation does not correspond to macroscopic stress, which may be due to variation of the interface stress.

Stability of Phosphonic Self Assembled Monolayers (SAMs) on Cobalt Chromium (Co-Cr) Alloy under Oxidative conditions

PubMed Central

Bhure, Rahul; Abdel-Fattah, Tarek M.; Bonner, Carl; Hall, Felicia; Mahapatro, Anil

2011-01-01

Cobalt Chromium (Co-Cr) alloys has been widely used in the biomedical arena for cardiovascular, orthopedic and dental applications. Surface modification of the alloy allows us to tailor the interfacial properties to address critical challenges of Co-Cr alloy in medical applications. Self assembled monolayers (SAMs) of Octadecylphosphonic acid (ODPA) have been used to form thin films on the oxide layer of the Co-Cr alloy surface by solution deposition technique. The SAMs formed were investigated for their stability to oxidative conditions of ambient laboratory environment over periods of 1, 3, 7 and 14 days. The samples were then characterized for their stability using X-ray Photoelectron Spectroscopy (XPS), Atomic Force Microscopy (AFM) and Contact Angle Measurements. Detailed high energy XPS elemental scans confirmed the presence of the phosphonic monolayer after oxidative exposure which suggested that the SAMs were firmly attached to the oxide layer of Co-Cr alloy. AFM images gave topographical data of the surface and showed islands of SAMs on Co-Cr alloy surface, before and after SAM formation and also over the duration of the oxidative exposure. Contact angle measurements confirmed the hydrophobicity of the surface over 14 days. Thus the SAMs were found to be stable for the duration of the study. These SAMs could be subsequently tailored by modifying the terminal functional groups and could be used for various potential biomedical applications such as drug delivery, biocompatibility and tissue integration PMID:21603056

Hard X-Ray and Wide Focusing Telescopes

NASA Technical Reports Server (NTRS)

Gorenstein, Paul

1998-01-01

Studies are being carried out to compare the performance of several different separation materials used in the replication process. This report presents the results obtained during the second year of a program which consists of replicating smooth, thin substrates, depositing multilayer coatings upon them, and evaluating their performance. Replication and multilayer coatings are both critically important to the development of focussing hard X-ray telescopes that function up to 100 keV. The activities of the current year include extending the comparison between sputtered amorphous carbon and evaporated gold to include sputtered as well as evaporated gold. The figure of merit being the smoothness of the replica which has a direct effect on the specular reflectivity. These results were obtained with epoxy replication, but they should be applicable to electroformed nickel, the process we expect to use for the ultimate replicated optics.

Studies on redox H 2-CO 2 cycle on CoCr xFe 2- xO 4

NASA Astrophysics Data System (ADS)

Ma, Ling Juan; Chen, Lin Shen; Chen, Song Ying

2009-01-01

Completely reduced CoCr xFe 2-xO 4 can be used to decompose CO 2. It was found that for pure CoFe 2O 4 there is no FeO formation in the first step while there is formation in the second step. For CoCr 0.08Fe 2-0.08O 4, there is no FeO formed in all the oxidation process, because of effect of Cr 3+. Pure CoFe 2O 4 was destroyed at the first reaction cycle of H 2 reduction and CO 2 oxidation, while doped Cr 3+ spinel CoCr 0.08Fe 1.92O 4 showed good stability. The results from H 2-TG, CO 2-TG and XRD show that the addition of Cr 3+ to CoFe 2O 4 can inhibit the increasing of crystallite size and the sintering of alloy. Most importantly, the CoCr 0.08Fe 1.92O 4 can be used to decompose CO 2 repeatedly, implying that it is a potential catalyst for dealing with the CO 2 as a 'green house effect' gas.

Induced spin-polarization of EuS at room temperature in Ni/EuS multilayers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Poulopoulos, P., E-mail: poulop@upatras.gr; Materials Science Department, University of Patras, 26504 Patras; Goschew, A.

2014-03-17

Ni/EuS multilayers with excellent multilayer sequencing are deposited via e-beam evaporation on the native oxide of Si(100) wafers at 4 × 10{sup −9} millibars. The samples have very small surface and interface roughness and show sharp interfaces. Ni layers are nanocrystalline 4–8 nm thick and EuS layers are 2–4 nm thick and are either amorphous or nanocrystalline. Unlike for Co/EuS multilayers, all Eu ions are in divalent (ferromagnetic) state. We show a direct antiferromagnetic coupling between EuS and Ni layers. At room temperature, the EuS layers are spin-polarized due to the proximity of Ni. Therefore, Ni/EuS is a candidate for room-temperature spintronics applications.

Adaptation and micro-structure of Co-Cr alloy maxillary complete denture base plates fabricated by selective laser melting technique.

PubMed

Ye, Ye; Jiao, Ting; Zhu, Jiarui; Sun, Jian

2018-01-24

The purpose of the study was to evaluate the adaptation and micro-structure of Co-Cr alloy maxillary complete denture base plates fabricated by the selective laser melting (SLM) technique. Twenty pairs of edentulous casts were randomly and evenly divided into two groups, and manufacturing of the Co-Cr alloy maxillary complete denture base was conducted either by the SLM technique or by the conventional method. The base-cast sets were transversally sectioned into three sections at the distal canines, mesial of the first molars and the posterior palatal zone. The gap between the metal base and cast was measured in these three sections with a stereoscopic microscope, and the data were analysed using t tests. A total of five specimens of 5 mm diameter were fabricated with the Co-Cr alloy by SLM and the traditional casting technology. A scanning electron microscope (SEM) was used to evaluate the differences in microstructure between these specimens. There was no statistical difference between the three sections in all four groups (P > 0.05). At the region of the canines, the clearance value for the SLM Co-Cr alloy group was larger than that of the conventional method group (P < 0.05). At the mesial of the first molar region and the posterior palatal zone, there was no statistical difference between the gaps observed in the two groups (P > 0.05). The SLM Co-Cr alloy has a denser microstructure behaviour and less casting defect than the cast Co-Cr alloy. The SLM technique showed initial feasibility for the manufacture of dental bases of complete dentures, but large sample studies are needed to prove its reliability in clinical applications. The mechanical properties and microstructure of the denture frameworks prepared by selective laser melting indicate that these dentures are appropriate for clinical use.

Effects of argon gas flow rate on laser-welding.

PubMed

Takayama, Yasuko; Nomoto, Rie; Nakajima, Hiroyuki; Ohkubo, Chikahiro

2012-01-01

The purpose of this study was to evaluate the effects of the rate of argon gas flow on joint strength in the laser-welding of cast metal plates and to measure the porosity. Two cast plates (Ti and Co-Cr alloy) of the same metal were abutted and welded together. The rates of argon gas flow were 0, 5 and 10 L/min for the Co-Cr alloy, and 5 and 10 L/min for the Ti. There was a significant difference in the ratio of porosity according to the rate of argon gas flow in the welded area. Argon shielding had no significant effect on the tensile strength of Co-Cr alloy. The 5 L/min specimens showed greater tensile strength than the 10 L/min specimens for Ti. Laser welding of the Co-Cr alloy was influenced very little by argon shielding. When the rate of argon gas flow was high, joint strength decreased for Ti.

Clinical marginal and internal fit of metal ceramic crowns fabricated with a selective laser melting technology.

PubMed

Huang, Zhuoli; Zhang, Lu; Zhu, Jingwei; Zhang, Xiuyin

2015-06-01

Selective laser melting (SLM) technology has been introduced to fabricate dental restorations. However, the fit of these restorations still needs further study. The purpose of this in vivo investigation was to compare the marginal and internal fit of SLM metal ceramic crowns with 2 lost-wax cast metal ceramic crowns and to evaluate the influence of tooth type on the marginal and internal fit of these crowns. A total of 330 metal ceramic crowns were evaluated. The metal copings were fabricated with SLM Co-Cr, cast Au-Pt, and cast Co-Cr alloy (n=110). The marginal and internal gaps of crowns were recorded by using a replica technique. The anterior and premolar replicas were sectioned 2 times, and molar replicas were sectioned 4 times. The marginal and internal gap width of each cross section was examined by stereomicroscope at ×30 magnification. Two-way analysis of variance was performed to identify the statistical difference among the groups. The marginal fit of the SLM Co-Cr group (75.6 ±32.6 μm) was not different from the cast Au-Pt group (76.8 ±32.1 μm) (P>.05) but was better than the cast Co-Cr group (91.0 ±36.3 μm) (P<.01). No significant difference was found among the SLM Co-Cr group (127.3 ±45.8 μm), cast Au-Pt group (129.9 ±61.1 μm). and cast Co-Cr group (142.5 ±63.7 μm) (P>.05). The mean occlusal gap width of the SLM Co-Cr group (309.8 ±106.6 μm) was significantly higher than that of the cast Au-Pt group (254.6 ±109.6 μm) and the cast Co-Cr group (249.6 ±110.4 μm) (P<.005). No significant difference was found in the marginal fit among the anterior group (84.4 ±35.1 μm), the premolar group (80.6 ±26.3 μm), and the molar group (82.7 ±38.0 μm) (P>.05). Also, no significant difference was found in the axial fit among the anterior group (138.3 ±52.5 μm), the premolar group (132.9 ±50.4 μm), and the molar group (134.4 ±52.5 μm) (P>.05). The anterior group (267.6 ±110.2 μm) did not differ from the premolar group (270.2 ±112.8 μm) and the molar group (268.6 ±110.5 μm) in occlusal fit (P>.05). The marginal fit of SLM Co-Cr metal ceramic crowns was similar to that of the cast Au-Pt metal ceramic crowns and was better than that of the cast Co-Cr metal ceramic crowns. The SLM Co-Cr metal ceramic crowns were not significantly different from the 2 cast metal ceramic crowns in axial fit but were less accurate in occlusal fit. Tooth type did not influence the marginal and internal fit of the metal ceramic crowns. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Hybrid framework with cobalt-chromium alloy and gold cylinder for implant superstructure: Bond strength and corrosion resistance.

PubMed

Yoshinari, Masao; Uzawa, Shinobu; Komiyama, Yataro

2016-10-01

The aim of this in vitro study was to evaluate tensile bond strengths and corrosion resistance of CoCr alloys joined with gold cylinder by a soldering system in comparison with the conventional cast-joining system. CoCr alloys joined with gold cylinder by a soldering system using a high-fusing gold solder (CoCr/Solder/Gold cylinder), gold alloy joined with gold cylinder by a cast joining system (Gold alloy/Gold cylinder) and CoCr castings were fabricated. The tensile bond strength and corrosion resistance in 0.9% NaCl solution (pH 7.4 and pH 2.3) were evaluated. Scanning electron microscopy (SEM) of the fractured surface and electron probe microanalysis (EPMA) of the joined interfaces were also performed. The tensile bond strengths of the CoCr/Solder/Gold cylinder specimens showed similar values as the Gold alloy/Gold cylinder specimens. SEM observation and EPMA analyses suggested firm bonding between the CoCr alloy and gold cylinder. The released elements from the CoCr/Solder/Gold cylinder specimens were similar to ones from CoCr castings. Results showed that superstructures made of CoCr alloys joined with the gold cylinder using a high-fusing gold solder had sufficient bond strength and high corrosion resistance. These hybrid frameworks with cobalt-chromium alloy and gold cylinder are promising prosthesis for implant superstructures with the low cost and favorable mechanical properties instead of conventional high-gold alloys. Copyright © 2016 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Articulation of Native Cartilage Against Different Femoral Component Materials. Oxidized Zirconium Damages Cartilage Less Than Cobalt-Chrome.

PubMed

Vanlommel, Jan; De Corte, Ronny; Luyckx, Jean Philippe; Anderson, Melissa; Labey, Luc; Bellemans, Johan

2017-01-01

Oxidized zirconium (OxZr) is produced by thermally driven oxidization creating an oxidized surface with the properties of a ceramic at the top of the Zr metal substrate. OxZr is much harder and has a lower coefficient of friction than cobalt-chrome (CoCr), both leading to better wear characteristics. We evaluated and compared damage to the cartilage of porcine patella plugs, articulating against OxZr vs CoCr. Our hypothesis was that, owing to its better wear properties, OxZr would damage cartilage less than CoCr. If this is true, OxZr might be a better material for the femoral component during total knee arthroplasty if the patella is not resurfaced. Twenty-one plugs from porcine patellae were prepared and tested in a reciprocating pin-on-disk machine while lubricated with bovine serum and under a constant load. Three different configurations were tested: cartilage-cartilage as the control group, cartilage-OxZr, and cartilage-CoCr. Macroscopic appearance, cartilage thickness, and the modified Mankin score were evaluated after 400,000 wear cycles. The control group showed statistically significant less damage than plugs articulating against both other materials. Cartilage plugs articulating against OxZr were statistically significantly less damaged than those articulating against CoCr. Although replacing cartilage by an implant always leads to deterioration of the cartilage counterface, OxZr results in less damage than CoCr. The use of OxZr might thus be preferable to CoCr in case of total knee arthroplasty without patella resurfacing. Copyright © 2016 Elsevier Inc. All rights reserved.

Cobalt-chromium alloys in fixed prosthodontics in Sweden

PubMed Central

Kassapidou, Maria; Franke Stenport, Victoria; Hjalmarsson, Lars; Johansson, Carina B.

2017-01-01

Abstract Aim: The aim of this study was to compile the usage of Co-Cr alloys in fixed prosthodontics (FP) among dental laboratories in Sweden. Methods: From March to October 2015, questionnaires were sent to 542 registered dental laboratories in Sweden. The questionnaires were divided in two parts, one for fixed dental-supported prosthodontics (FDP) and one for fixed implant-supported prosthodontics (FIP). Reminders were sent three times. Results: In total of 542 dental laboratories, 55% answered the questionnaires. Most dental laboratories use Co-Cr in FP, 134 (74%) in FDP and 89(66%) in FIP. The laboratories used Co-Cr alloys of various compositions in the prostheses, 35 for FDP and 30 for FIP. The most commonly used Co-Cr alloys for tooth-supported FDPs were (a) Wirobond® 280, (b) Cara SLM and (c) Wirobond® C. For implant-supported frameworks the frequently used alloys were: (a) Cara SLM, (b) Cara Milled and (c) Wirobond® 280. Except for the difference in composition of these alloys, they were also manufactured with various techniques. In tooth-supported prostheses the dominating technique was the cast technique while newer techniques as laser-sintering and milling were more commonly reported for implant-supported constructions. A fourth technique; the ‘pre-state’ milling was reported in FDP. Conclusion: More than 30 different Co-Cr alloys were reported as being used in FP. Thus, there is a need for studies exploring the mechanical and physical behavior and the biological response to the most commonly used Co-Cr alloys. PMID:29242813

CoCr wear particles generated from CoCr alloy metal-on-metal hip replacements, and cobalt ions stimulate apoptosis and expression of general toxicology-related genes in monocyte-like U937 cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Posada, Olga M., E-mail: O.M.PosadaEstefan@leeds.ac.uk; Gilmour, Denise; Tate, Rothwelle J., E-mail: r.j.tate@strath.ac.uk

Cobalt-chromium (CoCr) particles in the nanometre size range and their concomitant release of Co and Cr ions into the patients' circulation are produced by wear at the articulating surfaces of metal-on-metal (MoM) implants. This process is associated with inflammation, bone loss and implant loosening and led to the withdrawal from the market of the DePuy ASR™ MoM hip replacements in 2010. Ions released from CoCr particles derived from a resurfacing implant in vitro and their subsequent cellular up-take were measured by ICP-MS. Moreover, the ability of such metal debris and Co ions to induce both apoptosis was evaluated with bothmore » FACS and immunoblotting. qRT-PCR was used to assess the effects on the expression of lymphotoxin alpha (LTA), BCL2-associated athanogene (BAG1), nitric oxide synthase 2 inducible (NOS2), FBJ murine osteosarcoma viral oncogene homolog (FOS), growth arrest and DNA-damage-inducible alpha (GADD45A). ICP-MS showed that the wear debris released significant (p < 0.05) amounts of Co and Cr ions into the culture medium, and significant (p < 0.05) cellular uptake of both ions. There was also an increase (p < 0.05) in apoptosis after a 48 h exposure to wear debris. Analysis of qRT-PCR results found significant up-regulation (p < 0.05) particularly of NOS2 and BAG1 in Co pre-treated cells which were subsequently exposed to Co ions + debris. Metal debris was more effective as an inducer of apoptosis and gene expression when cells had been pre-treated with Co ions. This suggests that if a patient receives sequential bilateral CoCr implants, the second implant may be more likely to produce adverse effects than the first one. - Highlights: • Effects of CoCr nanoparticles and Co ions on U937 cells were investigated. • Ions released from wear debris play an important role in cellular response, • Toxicity of Co ions could be related to NO metabolic processes and apoptosis. • CoCr particles were a more effective inducer of apoptosis after cell priming. • CoCr particles were a more effective inducer of gene expression after cell priming.« less

Transfer-free synthesis of multilayer graphene using a single-step process in an evaporator and formation confirmation by laser mode-locking.

PubMed

Kim, Won-Jun; Debnath, Pulak C; Lee, Junsu; Lee, Ju Han; Lim, Dae-Soon; Song, Yong-Won

2013-09-13

Multilayer graphene is synthesized by a simplified process employing an evaporator in which a target substrate is deposited with a Ni catalyst layer before being heated to grow graphene directly. Carbon atoms adsorbed onto the surface of the Ni source as impurities from the atmosphere are incorporated into the catalyst layer during the deposition, and diffuse toward the catalyst/substrate interface, where they crystallize as graphene with a thickness of less than 2 nm. The need for a transfer process and external carbon supply is eliminated. The graphene is characterized by conventional analysis approaches, including nano-scale visualization and Raman spectroscopy, and utilizing photonics, graphene-functionalized passive laser mode-locking is demonstrated to confirm the successful synthesis of the graphene layer, resulting in an operating center wavelength of 1569.4 nm, a pulse duration of 1.35 ps, and a repetition rate of 31.6 MHz.

Microstructures and Mechanical Properties of Co-Cr Dental Alloys Fabricated by Three CAD/CAM-Based Processing Techniques

PubMed Central

Kim, Hae Ri; Jang, Seong-Ho; Kim, Young Kyung; Son, Jun Sik; Min, Bong Ki; Kim, Kyo-Han; Kwon, Tae-Yub

2016-01-01

The microstructures and mechanical properties of cobalt-chromium (Co-Cr) alloys produced by three CAD/CAM-based processing techniques were investigated in comparison with those produced by the traditional casting technique. Four groups of disc- (microstructures) or dumbbell- (mechanical properties) specimens made of Co-Cr alloys were prepared using casting (CS), milling (ML), selective laser melting (SLM), and milling/post-sintering (ML/PS). For each technique, the corresponding commercial alloy material was used. The microstructures of the specimens were evaluated via X-ray diffractometry, optical and scanning electron microscopy with energy-dispersive X-ray spectroscopy, and electron backscattered diffraction pattern analysis. The mechanical properties were evaluated using a tensile test according to ISO 22674 (n = 6). The microstructure of the alloys was strongly influenced by the manufacturing processes. Overall, the SLM group showed superior mechanical properties, the ML/PS group being nearly comparable. The mechanical properties of the ML group were inferior to those of the CS group. The microstructures and mechanical properties of Co-Cr alloys were greatly dependent on the manufacturing technique as well as the chemical composition. The SLM and ML/PS techniques may be considered promising alternatives to the Co-Cr alloy casting process. PMID:28773718

Postoperative magnetic resonance imaging artifact with cobalt-chromium versus titanium spinal instrumentation: presented at the 2013 Joint Spine Section Meeting. Clinical article.

PubMed

Ahmad, Faiz U; Sidani, Charif; Fourzali, Roberto; Wang, Michael Y

2013-11-01

Cobalt-chromium alloy (CoCr) rods haves some preferred biomechanical properties over titanium rods for spinal fixation. The use of CoCr rods in spinal fusion is relatively new, and there is no study in the existing world literature assessing the artifact caused by these rods in patients undergoing postoperative MRI. The purpose of this study is to compare the amount of imaging artifact caused by these implants and to assess its impact on the visualization of neighboring neural structures. This study investigated MR images in patients who underwent implantation of thoracolumbar instrumentation using 5.5-mm-diameter CoCr rods between November 2009 and March 2011 and images obtained in a comparison group of patients who had 5.5-mm titanium rods implanted during the same time period. Axial measurements of the artifact created by the rods between the screw heads were compared between the groups. Two blinded board-certified radiologists performed the measurements independently. They scored the visualization of the spinal canal using a subjective scoring system of 1-3, with 1 representing very good visualization and 2 and 3 representing reduced (good or suboptimal, respectively) visualization as a result of rod-related artifact. All measurements and scores were independently provided for T1-weighted and T2-weighted fast spin echo sequences (1.5-T magnet, 5-mm slice thickness). A total of 40 levels from the CoCr group (6 patients) and 30 levels from the titanium group (9 patients) were included in the analysis. Visualization of the canal at all levels was rated a score of 1 (very good) by both evaluators for both the CoCr and titanium groups. The average artifact on T1-weighted images measured 11.8 ± 1.8 mm for the CoCr group and 8.5 ± 1.2 mm for the titanium group (p < 0.01). The corresponding measurements on T2-weighted images were 11.0 ± 2.3 mm and 8.3 ± 1.7 mm (p < 0.01), respectively. In a mixed regression model, the mean artifact measurement for the CoCr group was, on average, 3.5 mm larger than for the control group. There was no significant difference between the measurements of the 2 evaluators (p = 0.99). The artifact caused by CoCr rods is approximately 3.5 mm larger than that caused by titanium rods on axial T1- and T2-weighted MRI. However, artifact from either CoCr or titanium was not found to interfere with the evaluation of the spinal canal and surrounding neural elements.

[The measurement of thermal expansion coefficient of Co-Cr alloy fabricated by selective laser melting].

PubMed

Tian, Xiao-mei; Zeng, Li; Wei, Bin; Huang, Yi-feng

2015-12-01

To investigate the thermal expansion coefficient of different processing parameters upon the Co-Cr alloy prepared by selective laser melting (SLM) technique, in order to provide technical support for clinical application of SLM technology. The heating curve of self-made Co-Cr alloy was protracted from room temperature to 980°C centigrade with DIL402PC thermal analysis instrument, keeping temperature rise rate and cooling rate at 5 K/min, and then the thermal expansion coefficient of 9 groups of Co-Cr alloy was measured from 20°C centigrade to 500°C centigrade and 600°C centigrade. The 9 groups thermal expansion coefficient values of Co-Cr alloy heated from 20°C centigrade to 500°C centigrade were 13.9×10(-6)/K,13.6×10(-6)/K,13.9×10(-6)/K,13.7×10(-6)/K,13.5×10(-6)/K,13.8×10(-6)/K,13.7×10(-6)/K,13.7×10(-6)/K,and 13.9×10(-6)/K, respectively; when heated from 20°C centigrade to 600°C centigrade, they were 14.2×10(-6)/K,13.9×10(-6)/K,13.8×10(-6)/K,14.0×10(-6)/K,14.1×10(-6)/K,14.1×10(-6)/K,13.9×10(-6)/K,14.2×10(-6)/K, and 13.7×10(-6)/K, respectively. The results showed that the Co-Cr alloy has good matching with the VITA VMK 95 porcelain powder and can meet the requirement of clinic use.

Indium-saving effect and physical properties of transparent conductive multilayers

NASA Astrophysics Data System (ADS)

Kawamura, M.; Kiba, T.; Abe, Y.; Kim, K. H.

2018-03-01

Indium-free transparent conductive multilayer structures consisting of top and bottom MoO3 layers and an Ag interlayer (MoO3/Ag/MoO3; MAM) are deposited onto glass substrates by vacuum evaporation. The transmittance and sheet resistance of the structures are evaluated, and the optimum structure is determined to be MAM (20/14/30 nm) as it shows the best figure of merit (FOM), which is used as the index for transparent conductive films, with a value of 6.2 × 10-3 Ω-1. To further improve the performance of the films, we attempt to fabricate a multilayer consisting of MoO3 and indium zinc oxide (IZO), based on previous results. The obtained IAM (30/14/50 nm) multilayer shows an FOM higher than that of the MAM, with a value of 32 × 10-3 Ω-1. Moreover, it reduces the amount of required indium as compared with the IZO/Ag/IZO multilayer.

The effect of frictional torque and bending moment on corrosion at the taper interface : an in vitro study.

PubMed

Panagiotidou, A; Meswania, J; Osman, K; Bolland, B; Latham, J; Skinner, J; Haddad, F S; Hart, A; Blunn, G

2015-04-01

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt-chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems. In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm. In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used. Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations. ©2015 The British Editorial Society of Bone & Joint Surgery.

[The effect of C-SiO2 composite films on corrosion resistance of dental Co-Cr alloy].

PubMed

Huang, Yi; Hu, Jing-Yu; Liu, Yu-Pu; Zhao, Dong-Yuan; Yu, You-Cheng; Bi, Wei

2016-10-01

To study the effect of carbon-silica composite films on corrosion resistance of Co-Cr alloy in simulated oral environment and provide evidences for clinical application of this new material. Co-Cr alloy specimens were cut into appropriate size of 20 mm × 20 mm × 0.5 mm. Then, the carbon-silica composite films were spin-coated onto the specimens. Subsequently, ICP-AES was used to observe the Co, Cr, Mo ion concentrations. Finally, Tafel polarization curves of the specimens were used to measure the electrochemical corrosion resistance by electrochemical workstation. SAS8.0 software package was used for statistical analysis. The results of ICP-AES showed that the ion concentrations of Co, Cr, Mo of specimens coated with composite films in the testing liquid were significantly smaller than that of Co-Cr alloy specimens. Tafel polarization curves showed that in the specimens coated with composite films, the corrosion potential moved in the positive direction and increased from -0.261 V to -0.13 V. At the same time, the corrosion current density decreased from -5.0017μA/cm 2 to -5.3006 μA/cm 2 . Carbon-silica composite films (silica=61.71wt %) can reduce the release of metal ions significantly and improve the corrosion resistance of Co-Cr alloys effectively. Carbon-silica composite films may be a promising dental material.

Multilayer coating of optical substrates by ion beam sputtering

NASA Astrophysics Data System (ADS)

Daniel, M. V.; Demmler, M.

2017-10-01

Ion beam sputtering is well established in research and industry, despite its relatively low deposition rates compared to electron beam evaporation. Typical applications are coatings of precision optics, like filters, mirrors and beam splitter. Anti-reflective or high-reflective multilayer stacks benefit from the high mobility of the sputtered particles on the substrate surface and the good mechanical characteristics of the layers. This work gives the basic route from single layer optimization of reactive ion beam sputtered Ta2O5 and SiO2 thin films towards complex multilayer stacks for high-reflective mirrors and anti-reflective coatings. Therefore films were deposited using different oxygen flow into the deposition chamber Afterwards, mechanical (density, stress, surface morphology, crystalline phases) and optical properties (reflectivity, absorption and refractive index) were characterized. These knowledge was used to deposit a multilayer coating for a high reflective mirror.

Development of multi-layer plastic fuel tanks for Nissan research vehicle-II

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kurihara, Y.; Nakazawa, K.; Ohashi, K.

1987-01-01

Plastic fuel tanks are light in weight and rustproof, and have good design flexibility. For those currently in use, however, which are made of mono-layer high-density polyethylene, fuel permeability is too high to meet U.S. evaporative emission standards, which are stricter than those in Japan or the EEC. For minimize fuel permeation, the formation of a barrier layer of polyamide resin by multi-layer (three-resin five-layer) blow molding is considered more promising than sulphonation or fluorination treatment of the polyethylene resin. This paper describes the fuel permeation mechanism, then outlines the development of a multi-layer plastic fuel tank, and discusses itsmore » structural features and the development of resins.« less

Forming aspheric optics by controlled deposition

DOEpatents

Hawryluk, A.M.

1998-04-28

An aspheric optical element is disclosed formed by depositing material onto a spherical surface of an optical element by controlled deposition to form an aspheric surface of desired shape. A reflecting surface, single or multi-layer, can then be formed on the aspheric surface by evaporative or sputtering techniques. Aspheric optical elements are suitable for deep ultra-violet (UV) and x-ray wavelengths. The reflecting surface may, for example, be a thin ({approx}100 nm) layer of aluminum, or in some cases the deposited modifying layer may function as the reflecting surface. For certain applications, multi-layer reflective surfaces may be utilized, such as chromium-carbon or tungsten-carbon multi-layer, with the number of layers and thickness being determined by the intended application. 4 figs.

Forming aspheric optics by controlled deposition

DOEpatents

Hawryluk, Andrew M.

1998-01-01

An aspheric optical element formed by depositing material onto a spherical surface of an optical element by controlled deposition to form an aspheric surface of desired shape. A reflecting surface, single or multi-layer, can then be formed on the aspheric surface by evaporative or sputtering techniques. Aspheric optical elements are suitable for deep ultra-violet (UV) and x-ray wavelengths. The reflecting surface may, for example, be a thin (.about.100 nm) layer of aluminum, or in some cases the deposited modifying layer may function as the reflecting surface. For certain applications, multi-layer reflective surfaces may be utilized, such as chromium-carbon or tungsten-carbon multi-layer, with the number of layers and thickness being determined by the intended application.

[Research progress in CoCr metal-ceramic alloy fabricated by selective laser melting].

PubMed

Yan, X; Lin, H

2018-02-09

Cobalt-chromium alloys have been applied to dental porcelain fused to metal (PFM) restorations over the past decades owing to their excellent corrosion resistance, good biocompatibility and low price. The production of CoCr metal-ceramic restorations has always been based on traditional lost-wax casting techniques. However, in recent years, selective laser melting (SLM) is becoming more and more highly valued by dental laboratories and dental practitioners due to its individuation, precision and efficiency. This paper mainly reviews the recent researches on the production process of copings, microstructure, mechanical property, metal-ceramic bond strength, fit of copings, corrosion resistance and biocompatibility of SLM CoCr metal-ceramic alloy.

[Comparison of clinical effects of Co-Cr alloy cast post-core and everStick fiber post in restoration of labially or lingually inclined maxillary central incisor].

PubMed

Qian, Yu-Mei; Zhong, Qun; Chen, Shuang

2017-02-01

To compare the clinical effect of Co-Cr alloy cast post-core and everStick fiber post in restoration of maxillary central incisor with labial or lingual inclination, and provide theoretical basis for clinical application. Ninety-seven labially or lingually inclined maxillary central incisors were treated in our hospital from March 2012 to March 2014. The patients were randomly divided into group A (n=49) and group B (n=48), and received post -core and crown restoration. Patients in group A underwent Co-Cr alloy cast post and core restoration and patients in group B underwent everStick fiber post and core restoration. After two-year of follow-up, root fracture, post break, crown or post dislodgment and gingival marginal discoloration were recorded and analyzed using SPSS 19.0 software package. Chi-square test showed that the success rate of restoration was significantly different between 2 groups (P<0.05). The incidence of root fracture and gingival marginal discoloration of Co-Cr alloy cast post-core was higher than that of everStick fiber post, but there was no significant difference in the incidence of post break, crown or post dislodgment. EverStick fiber post is better than Co-Cr alloy cast post and core to prevent root fracture and gingival marginal discoloration. Its fracture pattern is repairable and favorable for preserving tooth.

Modelling non-equilibrium secondary organic aerosol formation and evaporation with the aerosol dynamics, gas- and particle-phase chemistry kinetic multilayer model ADCHAM

DOE Office of Scientific and Technical Information (OSTI.GOV)

Roldin, P.; Eriksson, A. C.; Nordin, E. Z.

2014-08-11

We have developed the novel Aerosol Dynamics, gas- and particle- phase chemistry model for laboratory CHAMber studies (ADCHAM). The model combines the detailed gas phase Master Chemical Mechanism version 3.2, an aerosol dynamics and particle phase chemistry module (which considers acid catalysed oligomerization, heterogeneous oxidation reactions in the particle phase and non-ideal interactions between organic compounds, water and inorganic ions) and a kinetic multilayer module for diffusion limited transport of compounds between the gas phase, particle surface and particle bulk phase. In this article we describe and use ADCHAM to study: 1) the mass transfer limited uptake of ammonia (NH3)more » and formation of organic salts between ammonium (NH4+) and carboxylic acids (RCOOH), 2) the slow and almost particle size independent evaporation of α-pinene secondary organic aerosol (SOA) particles, and 3) the influence of chamber wall effects on the observed SOA formation in smog chambers.« less

Cost-effectiveness of percutaneous coronary intervention with cobalt-chromium everolimus eluting stents versus bare metal stents: Results from a patient level meta-analysis of randomized trials.

PubMed

Ferko, Nicole; Ferrante, Giuseppe; Hasegawa, James T; Schikorr, Tanya; Soleas, Ireena M; Hernandez, John B; Sabaté, Manel; Kaiser, Christoph; Brugaletta, Salvatore; de la Torre Hernandez, Jose Maria; Galatius, Soeren; Cequier, Angel; Eberli, Franz; de Belder, Adam; Serruys, Patrick W; Valgimigli, Marco

2017-05-01

Second-generation drug eluting stents (DES) may reduce costs and improve clinical outcomes compared to first-generation DES with improved cost-effectiveness when compared to bare metal stents (BMS). We aimed to conduct an economic evaluation of a cobalt-chromium everolimus eluting stent (Co-Cr EES) compared with BMS in percutaneous coronary intervention (PCI). To conduct a cost-effectiveness analysis (CEA) of a cobalt-chromium everolimus eluting stent (Co-Cr EES) versus BMS in PCI. A Markov state transition model with a 2-year time horizon was applied from a US Medicare setting with patients undergoing PCI with Co-Cr EES or BMS. Baseline characteristics, treatment effects, and safety measures were taken from a patient level meta-analysis of 5 RCTs (n = 4,896). The base-case analysis evaluated stent-related outcomes; a secondary analysis considered the broader set of outcomes reported in the meta-analysis. The base-case and secondary analyses reported an additional 0.018 and 0.013 quality-adjusted life years (QALYs) and cost savings of $236 and $288, respectively with Co-Cr EES versus BMS. Results were robust to sensitivity analyses and were most sensitive to the price of clopidogrel. In the probabilistic sensitivity analysis, Co-Cr EES was associated with a greater than 99% chance of being cost saving or cost effective (at a cost per QALY threshold of $50,000) versus BMS. Using data from a recent patient level meta-analysis and contemporary cost data, this analysis found that PCI with Co-Cr EES is more effective and less costly than PCI with BMS. © 2016 The Authors. Catheterization and Cardiovascular Interventions Published by Wiley Periodicals, Inc. © 2016 The Authors. Catheterization and Cardiovascular Interventions Published by Wiley Periodicals, Inc.

A comparison of Staphylococcus aureus biofilm formation on cobalt-chrome and titanium-alloy spinal implants.

PubMed

Patel, Shalin S; Aruni, Wilson; Inceoglu, Serkan; Akpolat, Yusuf T; Botimer, Gary D; Cheng, Wayne K; Danisa, Olumide A

2016-09-01

The use of cobalt chrome (CoCr) implants in spinal surgery has become increasingly popular. However, there have been no studies specifically comparing biofilm formation on CoCr with that of titanium-alloy spinal implants. The objective of this study was to compare the difference in propensity for biofilm formation between these two materials, as it specifically relates to spinal rods. Staphylococcus aureus subsp. Aureus (ATCC 6538) were incubated with two different types of spinal rods composed of either CoCr or titanium-alloy. The spinal rods were then subject to a trypsin wash to allow for isolation of the colonized organism and associated biofilms. The associated optical density values (OD) from the bacterial isolates were obtained and the bacterial solutions were plated on brain-heart infusion agar plates and the resultant colony-forming units (CFU) were counted. The OD values for the titanium-alloy rods were 1.105±0.096nm (mean±SD) and 1.040±0.026nm at 48hours and 96hours, respectively. In contrast, the OD values for the CoCr rods were 1.332±0.161nm and 1.115±0.207nm at 48 and 96hours, respectively (p<0.05). The CFU values were 1481±417/100mm(2) and 745±159/100mm(2) at 48 and 96hours, respectively for the titanium-alloy group. These values were significantly lower than the CFU values obtained from the CoCr group which were 2721±605/100mm(2) and 928±88/100mm(2) (p<0.001) at both 48 and 96hours respectively. Our findings, evaluating both the OD and CFU values, indicate that implants composed of CoCr had a higher proclivity towards biofilm formation compared to titanium-alloy implants. Copyright © 2016 Elsevier Ltd. All rights reserved.

Multi-layer solid-phase extraction and evaporation-enrichment methods for polar organic chemicals from aqueous matrices.

PubMed

Köke, Niklas; Zahn, Daniel; Knepper, Thomas P; Frömel, Tobias

2018-03-01

Analysis of polar organic chemicals in the aquatic environment is exacerbated by the lack of suitable and widely applicable enrichment methods. In this work, we assessed the suitability of a novel combination of well-known solid-phase extraction (SPE) materials in one cartridge as well as an evaporation method and for the enrichment of 26 polar model substances (predominantly log D < 0) covering a broad range of physico-chemical properties in three different aqueous matrices. The multi-layer solid-phase extraction (mlSPE) and evaporation method were investigated for the recovery and matrix effects of the model substances and analyzed with hydrophilic interaction liquid chromatography-tandem mass spectrometry (HILIC-MS/MS). In total, 65% of the model substances were amenable (> 10% recovery) to the mlSPE method with a mean recovery of 76% while 73% of the model substances were enriched with the evaporation method achieving a mean recovery of 78%. Target and non-target screening comparison of both methods with a frequently used reversed-phase SPE method utilizing "hydrophilic and lipophilic balanced" (HLB) material was performed. Target analysis showed that the mlSPE and evaporation method have pronounced advantages over the HLB method since the HLB material retained only 30% of the model substances. Non-target screening of a ground water sample with the investigated enrichment methods showed that the median retention time of all detected features on a HILIC system decreased in the order mlSPE (3641 features, median t R 9.7 min), evaporation (1391, 9.3 min), HLB (4414, 7.2 min), indicating a higher potential of the described methods to enrich polar analytes from water compared with HLB-SPE. Graphical abstract Schematic of the method evaluation (recovery and matrix effects) and method comparison (target and non-target analysis) of the two investigated enrichment methods for very polar chemicals in aqueousmatrices.

Combinatorial preparation and characterization of thin-film multilayer electro-optical devices.

PubMed

Neuber, Christian; Bäte, Markus; Thelakkat, Mukundan; Schmidt, Hans-Werner; Hänsel, Helmut; Zettl, Heiko; Krausch, Georg

2007-07-01

In this article we present a setup for the combinatorial vapor deposition of thin-film multilayer devices as well as methods for the fast and efficient analytic screening of the libraries obtained. The preparation setup is based on a commercially available evaporation chamber equipped with various evaporation sources for both organic and metallic materials. The combinatorial approach is realized by the combination of a rotation stage for the substrate, a five-mask sampler, and an additional mask whose position can be deliberately varied along one axis during the evaporation process. The latter is used to evaporate linear as well as step gradients by continuous or stepwise movement of a shutter mask. The mask sampler allows to define the sectors of the library and to evaporate more complex structures, e.g., an electrode layout. Finally, the simultaneous evaporation of two or more materials enables us to produce layers of varying composition ratio in general and doped materials, in particular. For the control of the evaporation process we have developed an automation software, which is particularly helpful for complex library designs and which grants excellent repeatability of experiments. Efficient and fast characterization of the obtained libraries is realized by (i) a purely optical setup and (ii) an electro-optical setup. (i) The UV/vis reader FLASHScan 530 permits to map out the UV/vis absorbance or fluorescence of the whole library. The UV/vis absorbance is primarily used to determine layer thicknesses and to confirm thickness uniformity across larger regions. The fluorescence measurements are used to determine the composition of layers containing fluorescent dyes. (ii) For a detailed short- and long-term electro-optical analysis we have developed an automated measurement system, which allows the characterization of 8x8 optoelectronic devices and to study their degradation behavior. Both solar cells and organic light-emitting diodes can be tested. Finally, we have developed a data analysis software to extract characteristic values from the huge amount of data and with this facilitate the finding of systematic dependencies.

Development of high damage threshold multilayer thin film beam combiner for laser application

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nand, Mangla, E-mail: mnand@rrcat.gov.in; Babita,; Jena, S.

2016-05-23

A polarized wavelength multiplexer with high laser induced damage threshold has been developed to combine two laser beam of high peak power in the visible region. The present wavelength multiplexer is a multilayer thin film device deposited by reactive electron beam evaporation. The developed device is capable of combining two p-polarized laser beams of peak power density of 1.7 GW/cm{sup 2} at an angle of incidence of 45°. High transmission (T> 90%) in high pass region and high reflection (R> 99%) in stop band region have been achieved.

Magnetic properties of Co-based multilayers with layer-alloyed modulations

NASA Astrophysics Data System (ADS)

Poulopoulos, P.; Angelakeris, M.; Niarchos, D.; Krishnan, R.; Porte, M.; Batas, C.; Flevaris, N. K.

1995-07-01

Various types of Co-based multilayers such as Pt mCo n, Pt m[CoPt] n, Co m[CoPd] n and Co m[CoPt] n were prepared by e-gun evaporation. Strong perpendicular anisotropy with considerable coercivity of ˜ 1 kOe was found for PtCo samples with thin Co layers. Moreover, the magnetization of Pt m[CoPt] n samples was found to approach that of pure Co and in the case of n > 5 enhancement of 30% or more exhibited. Magnetic properties were found to be strongly influenced by variations of modulation parameters.

Development of high damage threshold multilayer thin film beam combiner for laser application

NASA Astrophysics Data System (ADS)

Nand, Mangla; Babita, Jena, S.; Tokas, R. B.; Rajput, P.; Mukharjee, C.; Thakur, S.; Jha, S. N.; Sahoo, N. K.

2016-05-01

A polarized wavelength multiplexer with high laser induced damage threshold has been developed to combine two laser beam of high peak power in the visible region. The present wavelength multiplexer is a multilayer thin film device deposited by reactive electron beam evaporation. The developed device is capable of combining two p-polarized laser beams of peak power density of 1.7 GW/cm2 at an angle of incidence of 45°. High transmission (T> 90%) in high pass region and high reflection (R> 99%) in stop band region have been achieved.

Cobalt Chrome Spinal Constructs Trigger Airport Security Screening in 24% of Pediatric Patients.

PubMed

Woon, Regina P; Andras, Lindsay M; Barrett, Kody K; Skaggs, David L

2015-03-01

Retrospective study. To determine whether pediatric patients undergo additional airport security screening after posterior spinal fusion. Airport security has expanded to include body scanners as well as traditional metal detectors. Families frequently ask whether spinal implants will trigger airport security, but there is limited information on modern implants and screening methods. The researchers conducted a survey of 50 pediatric patients after posterior spinal fusion from 2004 to 2013. Inclusion criteria were posterior instrumentation, pedicle screws for at least 80% of anchors, and at least 1 trip through an American airport after surgery. Charts and radiographs were reviewed for metal type, number of levels fused, number of anchors, and rod diameter. A total of 16% of patients (8 of 50) were detected by body scan or metal detector and all had cobalt chrome (CoCr) rods. No patients with stainless-steel (SS) rods were detected. The CoCr rods triggered additional screening in 24% of children (8 of 33), compared with none of 17 with SS rods (p = .03). For patients with CoCr rods, the detection rate was 18% (5 of 28) by metal detector and 17% (3 of 18) by body scanner. For patients with CoCr rods, there was no significant difference between detection rates and levels fused (p = .30), number of anchors (p = .15), or rod diameter (p = .17). In this series, CoCr constructs were more likely to incur additional airport security compared with more traditional SS constructs. Copyright © 2015 Scoliosis Research Society. Published by Elsevier Inc. All rights reserved.

Early fixation of cobalt-chromium based alloy surgical implants to bone using a tissue-engineering approach.

PubMed

Ogawa, Munehiro; Tohma, Yasuaki; Ohgushi, Hajime; Takakura, Yoshinori; Tanaka, Yasuhito

2012-01-01

To establish the methods of demonstrating early fixation of metal implants to bone, one side of a Cobalt-Chromium (CoCr) based alloy implant surface was seeded with rabbit marrow mesenchymal cells and the other side was left unseeded. The mesenchymal cells were further cultured in the presence of ascorbic acid, β-glycerophosphate and dexamethasone, resulting in the appearance of osteoblasts and bone matrix on the implant surface. Thus, we succeeded in generating tissue-engineered bone on one side of the CoCr implant. The CoCr implants were then implanted in rabbit bone defects. Three weeks after the implantation, evaluations of mechanical test, undecalcified histological section and electron microscope analysis were performed. Histological and electron microscope images of the tissue engineered surface exhibited abundant new bone formation. However, newly formed bone tissue was difficult to detect on the side without cell seeding. In the mechanical test, the mean values of pull-out forces were 77.15 N and 44.94 N for the tissue-engineered and non-cell-seeded surfaces, respectively. These findings indicate early bone fixation of the tissue-engineered CoCr surface just three weeks after implantation.

Early Fixation of Cobalt-Chromium Based Alloy Surgical Implants to Bone Using a Tissue-engineering Approach

PubMed Central

Ogawa, Munehiro; Tohma, Yasuaki; Ohgushi, Hajime; Takakura, Yoshinori; Tanaka, Yasuhito

2012-01-01

To establish the methods of demonstrating early fixation of metal implants to bone, one side of a Cobalt-Chromium (CoCr) based alloy implant surface was seeded with rabbit marrow mesenchymal cells and the other side was left unseeded. The mesenchymal cells were further cultured in the presence of ascorbic acid, β-glycerophosphate and dexamethasone, resulting in the appearance of osteoblasts and bone matrix on the implant surface. Thus, we succeeded in generating tissue-engineered bone on one side of the CoCr implant. The CoCr implants were then implanted in rabbit bone defects. Three weeks after the implantation, evaluations of mechanical test, undecalcified histological section and electron microscope analysis were performed. Histological and electron microscope images of the tissue engineered surface exhibited abundant new bone formation. However, newly formed bone tissue was difficult to detect on the side without cell seeding. In the mechanical test, the mean values of pull-out forces were 77.15 N and 44.94 N for the tissue-engineered and non-cell-seeded surfaces, respectively. These findings indicate early bone fixation of the tissue-engineered CoCr surface just three weeks after implantation. PMID:22754313

Flexural strength of pure Ti, Ni-Cr and Co-Cr alloys submitted to Nd:YAG laser or TIG welding.

PubMed

Rocha, Rick; Pinheiro, Antônio Luiz Barbosa; Villaverde, Antonio Balbin

2006-01-01

Welding of metals and alloys is important to Dentistry for fabrication of dental prostheses. Several methods of soldering metals and alloys are currently used. The purpose of this study was to assess, using the flexural strength testing, the efficacy of two processes Nd:YAG laser and TIG (tungsten inert gas) for welding of pure Ti, Co-Cr and Ni-Cr alloys. Sixty cylindrical specimens were prepared (20 of each material), bisected and welded using different techniques. Four groups were formed (n=15). I: Nd:YAG laser welding; II- Nd:YAG laser welding using a filling material; III- TIG welding and IV (control): no welding (intact specimens). The specimens were tested in flexural strength and the results were analyzed statistically by one-way ANOVA. There was significant differences (p<0.001) among the non-welded materials, the Co-Cr alloy being the most resistant to deflection. Comparing the welding processes, significant differences (p<0.001) where found between TIG and laser welding and also between laser alone and laser plus filling material. In conclusion, TIG welding yielded higher flexural strength means than Nd:YAG laser welding for the tested Ti, Co-Cr and Ni-Cr alloys.

Remanent-magnetization decay in CoCr films

NASA Astrophysics Data System (ADS)

Skorjanec, J.; Cottles, V.; Close, J.; Iverson, P.; Edwards, J.; Dahlberg, E. Dan

1990-05-01

The decay of the remanent magnetization of several thin films of CoCr has been studied using the extraordinary Hall effect as a probe of the component of the magnetization perpendicular to the plane of the films. Consistent with previous measurements of CoCr, the remanent magnetization decays quasilogarithmically with time after the removal of a saturating magnetic field. In the present work the effect of a magnetically soft keeper layer on the decay of the magnetization has been investigated. It is found that the keeper layer does not affect the remanent magnetization nor does it decrease the decay rate of the perpendicular magnetization. This result indicates that the soft keeper layer is not effective at screening the demagnetization field on a length scale relevant to the decay-producing fields.

Ceramic Defects in Metal-Ceramic Fixed Dental Prostheses Made from Co-Cr and Au-Pt Alloys: A Retrospective Study.

PubMed

Mikeli, Aikaterini; Boening, Klaus W; Lißke, Benjamin

2015-01-01

Ceramic defects in porcelain-fused-to-metal (PFM) restorations may depend on framework alloy type. This study assessed ceramic defects on cobalt-chromium- (Co-Cr-) and gold-platinum- (Au-Pt-) based PFM restorations. In this study, 147 Co-Cr-based and 168 Au-Pt-based PFM restorations inserted between 1998 and 2010 (139 patients) were examined for ceramic defects. Detected defects were assigned to three groups according to clinical defect relevance. Ceramic defect rates (Co-Cr-based: 12.9%; Au-Pt-based: 7.2%) revealed no significant difference but a strong statistical trend (U test, P = .082). Most defects were of little clinical relevance. Co-Cr PFM restorations may be at higher risk for ceramic defects compared to Au-Pt-based restorations.

Metallurgical characterization of new palladium-containing cobalt chromium and nickel chromium alloys

NASA Astrophysics Data System (ADS)

Puri, Raghav

Recently introduced to the market has been an entirely new subclass of casting alloy composition whereby palladium (˜25 wt%) is added to traditional base metal alloys such as CoCr and NiCr. Objectives. The purpose of this study was to evaluate the microstructure and Vickers hardness of two new CoPdCr and one new NiPdCr alloy and compare them to traditional CoCr and NiCr alloys. Methods. The casting alloys investigated were: CoPdCr-A (Noble Crown NF, The Argen Corporation), CoPdCr-I (Callisto CP+, Ivoclar Vivadent), NiPdCr (Noble Crown, Argen), CoCr (Argeloy N.P. Special, Argen), and NiCr (Argeloy N.P. Star, Argen). As-cast cylindrical alloy specimens were mounted in epoxy resin and prepared with standard metallographic procedures, i.e. grinding with successive grades of SiC paper and polishing with alumina suspensions. The alloys were examined with an optical microscope, SEM/EPMA, and XRD to gain insight into their microstructure, composition, and crystal structure. Vickers hardness (VHN) was measured and statistically analyzed by one way ANOVA and Tukey's HSD test (alpha=0.05). Results. Optical microscopy showed a dendritic microstructure for all alloys. The Pd-containing alloys appear to possess a more complex microstructure. SEM/EPMA showed Cr to be rather uniformly distributed in the matrix with palladium tending to be segregated apart from Mo and Ni or Co. Areas of different composition may explain the poor electrochemical results noted in previous studies. XRD suggested the main phase in the Ni-containing solutions was a face centered cubic Ni solid solution, whereas the CoCr exhibited a hexagonal crystal structure that was altered to face centered cubic when Pd was included in the composition. For Vickers hardness, the Co-containing alloys possessed a greater hardness than the Ni-containing alloys. However, the incorporation of Pd in CoCr and NiCr had only a slight effect on microhardness. Conclusion. Overall, the inclusion of palladium increases the microstructural complexity of NiCr and CoCr alloys.

Evaluation of metal-ceramic bond characteristics of three dental Co-Cr alloys prepared with different fabrication techniques.

PubMed

Wang, Hongmei; Feng, Qing; Li, Ning; Xu, Sheng

2016-12-01

Limited information is available regarding the metal-ceramic bond strength of dental Co-Cr alloys fabricated by casting (CAST), computer numerical control (CNC) milling, and selective laser melting (SLM). The purpose of this in vitro study was to evaluate the metal-ceramic bond characteristics of 3 dental Co-Cr alloys fabricated by casting, computer numerical control milling, and selective laser melting techniques using the 3-point bend test (International Organization for Standardization [ISO] standard 9693). Forty-five specimens (25×3×0.5 mm) made of dental Co-Cr alloys were prepared by CAST, CNC milling, and SLM techniques. The morphology of the oxidation surface of metal specimens was evaluated by scanning electron microscopy (SEM). After porcelain application, the interfacial characterization was evaluated by SEM equipped with energy-dispersive spectrometry (EDS) analysis, and the metal-ceramic bond strength was assessed with the 3-point bend test. Failure type and elemental composition on the debonding interface were assessed by SEM/EDS. The bond strength was statistically analyzed by 1-way ANOVA and Tukey honest significant difference test (α=.05). The oxidation surfaces of the CAST, CNC, and SLM groups were different. They were porous in the CAST group but compact and irregular in the CNC and SLM groups. The metal-ceramic interfaces of the SLM and CNC groups showed excellent combination compared with those of the CAST group. The bond strength was 37.7 ±6.5 MPa for CAST, 43.3 ±9.2 MPa for CNC, and 46.8 ±5.1 MPa for the SLM group. Statistically significant differences were found among the 3 groups tested (P=.028). The debonding surfaces of all specimens exhibited cohesive failure mode. The oxidation surface morphologies and thicknesses of dental Co-Cr alloys are dependent on the different fabrication techniques used. The bond strength of all 3 groups exceed the minimum acceptable value of 25 MPa recommended by ISO 9693; hence, dental Co-Cr alloy fabricated with the SLM techniques could be a promising alternative for metal ceramic restorations. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Process Modeling With Inhomogeneous Thin Films

NASA Astrophysics Data System (ADS)

Machorro, R.; Macleod, H. A.; Jacobson, M. R.

1986-12-01

Designers of optical multilayer coatings commonly assume that the individual layers will be ideally homogeneous and isotropic. In practice, it is very difficult to control the conditions involved in the complex evaporation process sufficiently to produce such ideal films. Clearly, changes in process parameters, such as evaporation rate, chamber pressure, and substrate temperature, affect the microstructure of the growing film, frequently producing inhomogeneity in structure or composition. In many cases, these effects are interdependent, further complicating the situation. However, this process can be simulated on powerful, interactive, and accessible microcomputers. In this work, we present such a model and apply it to estimate the influence of an inhomogeneous layer on multilayer performance. Presently, the program simulates film growth, thermal expansion and contraction, and thickness monitoring procedures, and includes the effects of uncertainty in these parameters or noise. Although the model is being developed to cover very general cases, we restrict the present discussion to isotropic and nondispersive quarterwave layers to understand the particular effects of inhomogeneity. We studied several coating designs and related results and tolerances to variations in evaporation conditions. The model is composed of several modular subprograms, is written in Fortran, and is executed on an IBM-PC with 640 K of memory. The results can be presented in graphic form on a monochrome monitor. We are currently installing and implementing color capability to improve the clarity of the multidimensional output.

Cast iron cutting with nano TiN and multilayer TiN-CrN coated inserts

NASA Astrophysics Data System (ADS)

Perucca, M.; Durante, S.; Semmler, U.; Rüger, C.; Fuentes, G. G.; Almandoz, E.

2012-09-01

During the past decade great success has been achieved in the development of duplex and multilayer multi-functional surface systems. Among these surface systems outstanding properties have nanoscale multilayer coatings. Within the framework of the M3-2S project funded in the 7th European Framework Programme, several nanoscale multilayer coatings have been developed and investigated for experimental and industrial validation. This paper shows the performance of TiN and TiN/CrN nanoscale multilayer coatings on WC cutting inserts when machining GJL250 cast iron. The thin films have been deposited by cathodic arc evaporation in an industrial PVD system. The multilayer deposition characteristic and its properties are shown. The inserts have been investigated in systematic cutting experiments of cast iron bars on a turning machine specifically equipped for force measurements, accompanied by wear determination. Furthermore, equivalent experiments have been carried out on an industrial turning unit. Industrial validation criteria have been applied to assess the comparative performance of the coatings. The choice of the material and the machined parts is driven by an interest in automotive applications. The industrial tests show the need to further optimise the multi-scale modelling approach in order to reduce the lead time of the coating development as well as to improve simulation reliability.

Fabrication and characterization of WO3/Ag/WO3 multilayer transparent anode with solution-processed WO3 for polymer light-emitting diodes

PubMed Central

2012-01-01

The dielectric/metal/dielectric multilayer is suitable for a transparent electrode because of its high-optical and high-electrical properties; however, it is fabricated by an expensive and inefficient multistep vacuum process. We present a WO3/Ag/WO3 (WAW) multilayer transparent anode with solution-processed WO3 for polymer light-emitting diodes (PLEDs). This WAW multilayer not only has high transmittance and low resistance but also can be easily and rapidly fabricated. We devised a novel method to deposit a thin WO3 layer by a solution process in an air environment. A tungstic acid solution was prepared from an aqueous solution of Na2WO4 and then converted to WO3 nanoparticles (NPs) by a thermal treatment. Thin WO3 NP layers form WAW multilayer with a thermal-evaporated Ag layer, and they improve the transmittance of the WAW multilayer because of its high transmittance and refractive index. Moreover, the surface of the WO3 layer is homogeneous and flat with low roughness because of the WO3 NP generation from the tungstic acid solution without aggregation. We performed optical simulation and experiments, and the optimized WAW multilayer had a high transmittance of 85% with a sheet resistance of 4 Ω/sq. Finally, PLEDs based on the WAW multilayer anode achieved a maximum luminance of 35,550 cd/m2 at 8 V, and this result implies that the solution-processed WAW multilayer is appropriate for use as a transparent anode in PLEDs. PMID:22587669

Fabrication and characterization of WO3/Ag/WO3 multilayer transparent anode with solution-processed WO3 for polymer light-emitting diodes.

PubMed

Jeon, Kangmin; Youn, Hongseok; Kim, Seongbeom; Shin, Seongbeom; Yang, Minyang

2012-05-15

The dielectric/metal/dielectric multilayer is suitable for a transparent electrode because of its high-optical and high-electrical properties; however, it is fabricated by an expensive and inefficient multistep vacuum process. We present a WO3/Ag/WO3 (WAW) multilayer transparent anode with solution-processed WO3 for polymer light-emitting diodes (PLEDs). This WAW multilayer not only has high transmittance and low resistance but also can be easily and rapidly fabricated. We devised a novel method to deposit a thin WO3 layer by a solution process in an air environment. A tungstic acid solution was prepared from an aqueous solution of Na2WO4 and then converted to WO3 nanoparticles (NPs) by a thermal treatment. Thin WO3 NP layers form WAW multilayer with a thermal-evaporated Ag layer, and they improve the transmittance of the WAW multilayer because of its high transmittance and refractive index. Moreover, the surface of the WO3 layer is homogeneous and flat with low roughness because of the WO3 NP generation from the tungstic acid solution without aggregation. We performed optical simulation and experiments, and the optimized WAW multilayer had a high transmittance of 85% with a sheet resistance of 4 Ω/sq. Finally, PLEDs based on the WAW multilayer anode achieved a maximum luminance of 35,550 cd/m2 at 8 V, and this result implies that the solution-processed WAW multilayer is appropriate for use as a transparent anode in PLEDs.

Reactive multilayers fabricated by vapor deposition. A critical review

DOE PAGES

Adams, D. P.

2014-10-02

The reactive multilayer thin films are a class of energetic materials that continue to attract attention for use in joining applications and as igniters. Generally composed of two reactants, these heterogeneous solids can be stimulated by an external source to promptly release stored chemical energy in a sudden emission of light and heat. In our critical review article, results from recent investigations of these materials are discussed. Discussion begins with a brief description of the vapor deposition techniques that provide accurate control of layer thickness and film composition. More than 50 reactive film compositions have been reported to date, withmore » most multilayers fabricated by magnetron sputter deposition or electron-beam evaporation. In later sections, we review how multilayer ignition threshold, reaction rate, and total heat are tailored via thin film design. For example, planar multilayers with nanometer-scale periodicity exhibit rapid, self-sustained reactions with wavefront velocities up to 100 m/s. Numeric and analytical models have elucidated many of the fundamental processes that underlie propagating exothermic reactions while demonstrating how reaction rates vary with multilayer design. Recent, time-resolved diffraction and imaging studies have further revealed the phase transformations and the wavefront dynamics associated with propagating chemical reactions. Many reactive multilayers (e.g., Co/Al) form product phases that are consistent with published equilibrium phase diagrams, yet a few systems, such as Pt/Al, develop metastable products. The final section highlights current and emerging applications of reactive multilayers. Examples include reactive Ni(V)/Al and Pd/Al multilayers which have been developed for localized soldering of heat-sensitive components.« less

Biological Effects of Clinically Relevant CoCr Nanoparticles in the Dura Mater: An Organ Culture Study

PubMed Central

Papageorgiou, Iraklis; Abberton, Thomas; Fuller, Martin; Tipper, Joanne L.; Fisher, John; Ingham, Eileen

2014-01-01

Medical interventions for the treatment of spinal disc degeneration include total disc replacement and fusion devices. There are, however, concerns regarding the generation of wear particles by these devices, the majority of which are in the nanometre sized range with the potential to cause adverse biological effects in the surrounding tissues. The aims of this study were to develop an organ culture model of the porcine dura mater and to investigate the biological effects of CoCr nanoparticles in this model. A range of histological techniques were used to analyse the structure of the tissue in the organ culture. The biological effects of the CoCr wear particles and the subsequent structural changes were assessed using tissue viability assays, cytokine assays, histology, immunohistochemistry, and TEM imaging. The physiological structure of the dura mater remained unchanged during the seven days of in vitro culture. There was no significant loss of cell viability. After exposure of the organ culture to CoCr nanoparticles, there was significant loosening of the epithelial layer, as well as the underlying collagen matrix. TEM imaging confirmed these structural alterations. These structural alterations were attributed to the production of MMP-1, -3, -9, -13, and TIMP-1. ELISA analysis revealed that there was significant release of cytokines including IL-8, IL-6, TNF-α, ECP and also the matrix protein, tenascin-C. This study suggested that CoCr nanoparticles did not cause cytotoxicity in the dura mater but they caused significant alterations to its structural integrity that could lead to significant secondary effects due to nanoparticle penetration, such as inflammation to the local neural tissue. PMID:28344233

Magnetic and low temperature phonon studies of CoCr2O4 powders doped with Fe(III) and Ni(II) ions

NASA Astrophysics Data System (ADS)

Ptak, M.; Mączka, M.; Pikul, A.; Tomaszewski, P. E.; Hanuza, J.

2014-04-01

Extensive temperature-dependent phonon studies and low-temperature magnetic measurements of CoCr2-xFexO4 (for x=0.5, 1 and 2) and Co0.9Ni0.1Cr2O4 polycrystalline powders are presented. The main aim of these studies was to obtain information on phonon and structural properties of these compounds as well as strength of spin-phonon coupling in the magnetically ordered phases. IR and Raman spectra show that doping of CoCr2O4 with Fe(III) ions leads to broadening of bands and appearance of new bands due to the formation of inverted spinel structure. In contrast to this behavior, doping with 10 mol% of Ni(II) ions leads to weak increase of band width only. Magnetization measured as a function of temperature and external magnetic field showed that magnetic properties of Co0.9Ni0.1Cr2O4 sample are similar to those reported for pure CoCr2O4, i.e., partial substitution of Ni(II) for Co(II) leads to slight shift of the ferrimagnetic phase transition at TC and spiral spin order transition at TS towards lower values. The change of crystallization preference induced by incorporation of increasing concentration of Fe(III) ions in the spinel lattice causes significant increase of TC and decrease of TS. The latter transition disappears completely for higher concentrations of Fe(III). The performed temperature-dependent IR studies revealed interesting anomalous behavior of phonons below TC for CoCr1.5Fe0.5O4 and Co0.9Ni0.1Cr2O4, which was attributed to spin-phonon coupling.

Comparison of the microstructure and phase stability of as-cast, CAD/CAM and powder metallurgy manufactured Co-Cr dental alloys.

PubMed

Li, Kai Chun; Prior, David J; Waddell, J Neil; Swain, Michael V

2015-12-01

The objective of this study was to identify the different microstructures produced by CC, PM and as-cast techniques for Co-Cr alloys and their phase stability following porcelain firings. Three bi-layer porcelain veneered Co-Cr specimens and one monolithic Co-Cr specimen of each alloy group [cast, powder metallurgy (PM), CAD/CAM (CC)] were manufactured and analyzed using electron backscatter diffraction (EBSD), energy dispersive spectrometry (EDS) and X-ray diffraction (XRD). Specimens were treated to incremental numbers of porcelain firings (control 0, 5, 15) with crystallographic data, grain size and chemical composition subsequently obtained and analyzed. EBSD datasets of the cast alloy indicated large grains >200 μm whereas PM and CC alloy consisted of mean arithmetic grain sizes of 29.6 μm and 19.2 μm respectively. XRD and EBSD results both indicated the highest increase in hcp content (>13vol%) for cast Co-Cr alloy after treatment with porcelain firing while PM and CC indicated <2vol% hcp content. A fine grain interfacial layer developed on all surfaces of the alloy after porcelain firing. The depth of this layer increased with porcelain firings for as-cast and PM but no significant increase (p>.05) was observed in CC. EDS line scans indicated an increase in Cr content at the alloy surface after porcelain firing treatment for all three alloys. PM and CC produced alloy had superior fcc phase stability after porcelain firings compared to a traditional cast alloy. It is recommended that PM and CC alloys be used for porcelain-fused-to-metal restorations. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Clinical significance of corrosion of cemented femoral stems in metal-on-metal hips: a retrieval study.

PubMed

Hothi, Harry S; Berber, Reshid; Panagiotopoulos, Andreas C; Whittaker, Robert K; Rhead, Camilla; Skinner, John A; Hart, Alister J

2016-11-01

The clinical significance of corrosion of cemented femoral stems is unclear. The purpose of this retrieval study was to: (1) report on corrosion at the stem-cement interface and (2) correlate these findings with clinical data. We analysed cemented stems (n = 36) composed of cobalt-chromium (CoCr) and stainless steel (SS) in a series of revised metal-on-metal hips. We performed detailed inspection of each stem to assess the severity of corrosion at the stem-cement interface using a scale of 1 (low) to 5 (severe). We assessed the severity of corrosion at each stem trunnion and measured wear rates at the head taper and bearing surfaces. We used non-parametric tests to determine the significance of differences between the CoCr and SS stems in relation to: (1) pre-revision whole blood Co and Cr metal ion levels, (2) trunnion corrosion, (3) bearing surface wear and (4) taper material loss. The corrosion scores of CoCr stems were significantly greater than SS stems (p < 0.01). Virtually all stem trunnions in both alloy groups had minimal evidence of corrosion. The median pre-revision Co levels of implants with CoCr stems were significantly greater than the SS stems (p < 0.01). There was no significant difference in relation to pre-revision Cr levels (p = 0.521). There was no significant difference between the two stem types in relation to bearing wear (p = 0.926) or taper wear (p = 0.148). Severe corrosion of cemented femoral stems is a common finding at our retrieval centre; surgeons should consider corrosion of CoCr stems as a potential source of metal ions when revising a hip.

Corrosion resistance assessment of Co-Cr alloy frameworks fabricated by CAD/CAM milling, laser sintering, and casting methods.

PubMed

Tuna, Süleyman Hakan; Özçiçek Pekmez, Nuran; Kürkçüoğlu, Işin

2015-11-01

The effects of fabrication methods on the corrosion resistance of frameworks produced with Co-Cr alloys are not clear. The purpose of this in vitro study was to evaluate the electrochemical corrosion resistance of Co-Cr alloy specimens that were fabricated by conventional casting, milling, and laser sintering. The specimens fabricated with 3 different methods were investigated by potentiodynamic tests and electrochemical impedance spectroscopy in an artificial saliva. Ions released into the artificial saliva were estimated with inductively coupled plasma-mass spectrometry, and the results were statistically analyzed. The specimen surfaces were investigated with scanning electron microscopy before and after the tests. In terms of corrosion current and Rct properties, statistically significant differences were found both among the means of the methods and among the means of the material groups (P<.05). With regard to ions released, a statistically significant difference was found among the material groups (P<.05); however, no difference was found among the methods. Scanning electron microscopic imaging revealed that the specimens produced by conventional casting were affected to a greater extent by etching and electrochemical corrosion than those produced by milling and laser sintering. The corrosion resistance of a Co-Cr alloy specimens fabricated by milling or laser sintering was greater than that of the conventionally cast alloy specimens. The Co-Cr specimens produced by the same method also differed from one another in terms of corrosion resistance. These differences may be related to the variations in the alloy compositions. Copyright © 2015 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Effect of annealing procedure on the bonding of ceramic to cobalt-chromium alloys fabricated by rapid prototyping.

PubMed

Tulga, Ayca

2018-04-01

An annealing procedure is a heat treatment process to improve the mechanical properties of cobalt-chromium (Co-Cr) alloys. However, information is lacking about the effect of the annealing process on the bonding ability of ceramic to Co-Cr alloys fabricated by rapid prototyping. The purpose of this in vitro study was to evaluate the effects of the fabrication techniques and the annealing procedure on the shear bond strength of ceramic to Co-Cr alloys fabricated by different techniques. Ninety-six cylindrical specimens (10-mm diameter, 10-mm height) made of Co-Cr alloy were prepared by casting (C), milling (M), direct process powder-bed (LaserCUSING) with and without annealing (CL+, CL), and direct metal laser sintering (DMLS) with annealing (EL+) and without annealing (EL). After the application of ceramic to the metal specimens, the metal-ceramic bond strength was assessed using a shear force test at a crosshead speed of 0.5 mm/min. Shear bond strength values were statistically analyzed by 1-way ANOVA and Tukey multiple comparison tests (α=.05). Although statistically significant differences were found among the 3 groups (M, 29.87 ±2.06; EL, 38.92 ±2.04; and CL+, 40.93 ±2.21; P=.002), no significant differences were found among the others (P>.05). The debonding surfaces of all specimens exhibited mixed failure mode. These results showed that the direct process powder-bed method is promising in terms of metal-ceramic bonding ability. The manufacturing technique of Co-Cr alloys and the annealing process influence metal-ceramic bonding. Copyright © 2017 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Dynamic mask for producing uniform or graded-thickness thin films

DOEpatents

Folta, James A [Livermore, CA

2006-06-13

A method for producing single layer or multilayer films with high thickness uniformity or thickness gradients. The method utilizes a moving mask which blocks some of the flux from a sputter target or evaporation source before it deposits on a substrate. The velocity and position of the mask is computer controlled to precisely tailor the film thickness distribution. The method is applicable to any type of vapor deposition system, but is particularly useful for ion beam sputter deposition and evaporation deposition; and enables a high degree of uniformity for ion beam deposition, even for near-normal incidence of deposition species, which may be critical for producing low-defect multilayer coatings, such as required for masks for extreme ultraviolet lithography (EUVL). The mask can have a variety of shapes, from a simple solid paddle shape to a larger mask with a shaped hole through which the flux passes. The motion of the mask can be linear or rotational, and the mask can be moved to make single or multiple passes in front of the substrate per layer, and can pass completely or partially across the substrate.

Structural and morphological approach of Co-Cr dental alloys processed by alternative manufacturing technologies

NASA Astrophysics Data System (ADS)

Porojan, Sorin; Bîrdeanu, Mihaela; Savencu, Cristina; Porojan, Liliana

2017-08-01

The integration of digitalized processing technologies in traditional dental restorations manufacturing is an emerging application. The objective of this study was to identify the different structural and morphological characteristics of Co-Cr dental alloys processed by alternative manufacturing techniques in order to understand the influence of microstructure on restorations properties and their clinical behavior. Metallic specimens made of Co-Cr dental alloys were prepared using traditional casting (CST), and computerized milling (MIL), selective laser sintering (SLS) and selective laser melting (SLM). The structural information of the samples was obtained by X-ray diffraction, the morphology and the topography of the samples were investigated by Scanning Electron Microscopy and Atomic Force Microscope. Given that the microstructure was significantly different, further differences in the clinical behavior of prosthetic restorations manufactured using additive techniques are anticipated.

Dependence of Magnetic Properties of Co/Pt Multilayers on Deposition Temperature of Pt Buffer Layers

NASA Astrophysics Data System (ADS)

Shiomi, Shigeru; Nishimura, Tomotaka; Kobayashi, Tadashi; Masuda, Morio

1993-04-01

A 15-nm-thick Pt buffer layer was deposited on a glass slide at temperature Ts(Ptbuf) ranging from 30 to 300°C by e-gun evaporation. Following the cooling in vacuum to ambient temperature, Co and Pt layers have been alternately deposited on it. Very large perpendicular anisotropy and coercivity have been obtained at Ts(Ptbuf) higher than 200°C. The (111) preferred orientation of the Co/Pt multilayer as well as the Pt buffer layer became more pronounced with elevating Ts(Ptbuf), to which the enhancement of perpendicular anisotropy with elevating Ts(Ptbuf) might be ascribable.

Charge and spin transport in metal-graphene-metal vertical junctions

NASA Astrophysics Data System (ADS)

Cobas, Enrique; van't Erve, Olaf; Cheng, Shu-Fan; Culbertson, James; Jernigan, Glenn; Bussman, Konrad; Jonker, Berry

We observe negative magnetoresistance(MR) in metallic NiFe(111)|multi-layer graphene|Fe heterostructures consistent with minority spin filtering. The MR is -5 percent at room temperature and -12 percent at 10 K. The transport properties and temperature dependence are metallic. We further investigate the out-of-plane (c-axis) resistivity and magnetoresistance of multi-layer graphene between metal surfaces. We fabricate various metal-graphene-metal vertical heterostructures via chemical vapor deposition directly on lattice-matched crystalline metal films including NiFe(111) and Co(0002) and in-situ electron beam evaporation of NiFe, Co, Ni, Fe, Cu and Au.

Medial Tibial Stress Shielding: A Limitation of Cobalt Chromium Tibial Baseplates.

PubMed

Martin, J Ryan; Watts, Chad D; Levy, Daniel L; Kim, Raymond H

2017-02-01

Stress shielding is a well-recognized complication associated with total knee arthroplasty. However, this phenomenon has not been thoroughly described. Specifically, no study to our knowledge has evaluated the radiographic impact of utilizing various tibial component compositions on tibial stress shielding. We retrospectively reviewed 3 cohorts of 50 patients that had a preoperative varus deformity and were implanted with a titanium, cobalt chromium (CoCr), or an all polyethylene tibial implant. A radiographic comparative analysis was performed to evaluate the amount of medial tibial bone loss in each cohort. In addition, a clinical outcomes analysis was performed on the 3 cohorts. The CoCr was noted to have a statistically significant increase in medial tibial bone loss compared with the other 2 cohorts. The all polyethylene cohort had a statistically significantly higher final Knee Society Score and was associated with the least amount of stress shielding. The CoCr tray is the most rigid of 3 implants that were compared in this study. Interestingly, this cohort had the highest amount of medial tibial bone loss. In addition, 1 patient in the CoCr cohort had medial soft tissue irritation which was attributed to a prominent medial tibial tray which required revision surgery to mitigate the symptoms. Copyright © 2016 Elsevier Inc. All rights reserved.

Aptamer based surface enhanced Raman scattering detection of vasopressin using multilayer nanotube arrays

PubMed Central

Huh, Yun Suk; Erickson, David

2009-01-01

Here we present an optofluidic surface enhanced Raman spectroscopy (SERS) device for on-chip detection of vasopressin using an aptamer based binding assay. To create the SERS-active substrate, densely packed, 200 nm diameter, metal nanotube arrays were fabricated using an anodized alumina nanoporous membrane as a template for shadow evaporation. We explore the use of both single layer Au structures and multilayer Au/Ag/Au structures and also demonstrate a facile technique for integrating the membranes with all polydimethylsiloxane (PDMS) microfluidic devices. Using the integrated device, we demonstrate a linear response in the main detection peak intensity to solution phase concentration and a limit of detection on the order of 5.2 μU/mL. This low limit of detection is obtained with device containing the multilayer SERS substrate which we show exhibits a stronger Raman enhancement while maintaining biocompatibility and ease or surface reactivity with the capture probe. PMID:19857952

Fabrication of artificially stacked ultrathin ZnS/MgF2 multilayer dielectric optical filters.

PubMed

Kedawat, Garima; Srivastava, Subodh; Jain, Vipin Kumar; Kumar, Pawan; Kataria, Vanjula; Agrawal, Yogyata; Gupta, Bipin Kumar; Vijay, Yogesh K

2013-06-12

We report a design and fabrication strategy for creating an artificially stacked multilayered optical filters using a thermal evaporation technique. We have selectively chosen a zinc sulphide (ZnS) lattice for the high refractive index (n = 2.35) layer and a magnesium fluoride (MgF2) lattice as the low refractive index (n = 1.38) layer. Furthermore, the microstructures of the ZnS/MgF2 multilayer films are also investigated through TEM and HRTEM imaging. The fabricated filters consist of high and low refractive 7 and 13 alternating layers, which exhibit a reflectance of 89.60% and 99%, respectively. The optical microcavity achieved an average transmittance of 85.13% within the visible range. The obtained results suggest that these filters could be an exceptional choice for next-generation antireflection coatings, high-reflection mirrors, and polarized interference filters.

Effects of Various Passivation Layers on Electrical Properties of Multilayer MoS₂ Transistors.

PubMed

Ma, Jiyeon; Yoo, Geonwook

2018-09-01

So far many of research on transition metal dichalcogenides (TMDCs) are based on a bottomgate device structure due to difficulty with depositing a dielectric film on top of TMDs channel layer. In this work, we study different effects of various passivation layers on electrical properties of multilayer MoS2 transistors: spin-coated CYTOP, SU-8, and thermal evaporated MoOX. The SU-8 passivation layer alters device performance least significantly, and MoOX induces positive threshold voltage shift of ~8.0 V due to charge depletion at the interface, and the device with CYTOP layer exhibits decreased field-effect mobility by ~50% due to electric dipole field effect of C-F bonds in the end groups. Our results imply that electrical properties of the multilayer MoS2 transistors can be modulated using a passivation layer, and therefore a proper passivation layer should be considered for MoS2 device structures.

Calcium aluminate coated and uncoated free form fabricated CoCr implants: a comparative study in rabbit.

PubMed

Palmquist, A; Jarmar, T; Hermansson, L; Emanuelsson, L; Taylor, A; Taylor, M; Engqvist, H; Thomsen, P

2009-10-01

The purpose of this study was to compare the integration in bone of uncoated free form fabricated cobalt chromium (CoCr) implants to the same implant with a calcium aluminate coating. The implants of cylindrical design with a pyramidal surface structure were press-fit into the limbs of New Zealand white rabbits. After 6 weeks, the rabbits were sacrificed, and samples were retrieved and embedded. Ground sections were subjected to histological analysis and histomorphometry. The section counter part was used for preparing an electron transparent transmission electron microscopy sample by focused ion beam milling. Calcium aluminate dip coating provided a significantly greater degree of bone contact than that of the native CoCr. The gibbsite hydrate formed in the hardening reaction of the calcium aluminate was found to be the exclusive crystalline phase material in direct contact with bone. (c) 2009 Wiley Periodicals, Inc.

In Vivo Wear Performance of Cobalt-Chromium Versus Oxidized Zirconium Femoral Total Knee Replacements.

PubMed

Gascoyne, Trevor C; Teeter, Matthew G; Guenther, Leah E; Burnell, Colin D; Bohm, Eric R; Naudie, Douglas R

2016-01-01

This study examines the damage and wear on the polyethylene (PE) inserts from 52 retrieved Genesis II total knee replacements to identify differences in tribological performance between matched pairs of cobalt-chromium (CoCr) and oxidized zirconium (OxZr) femoral components. Observer damage scoring and microcomputed tomography were used to quantify PE damage and wear, respectively. No significant differences were found between CoCr and OxZr groups in terms of PE insert damage, surface penetration, or wear. No severe damage such as cracking or delamination was noted on any of the 52 PE inserts. Observer damage scoring did not correlate with penetrative or volumetric PE wear. The more costly OxZr femoral component does not demonstrate clear tribological benefit over the standard CoCr component in the short term with this total knee replacement design. Copyright © 2016 Elsevier Inc. All rights reserved.

Hot corrosion of Co-Cr, Co-Cr-Al, and Ni-Cr alloys in the temperature range of 700-750 deg C

NASA Technical Reports Server (NTRS)

Chiang, K. T.; Meier, G. H.

1980-01-01

The effect of SO3 pressure in the gas phase on the Na2SO4 induced hot corrosion of Co-Cr, Ni-Cr, and Co-Cr-Al alloys was studied in the temperature range 700 to 750 C. The degradation of the Co-Cr and Ni-Cr alloys was found to be associated with the formation of liquid mixed sulfates (CoSO4-Na2SO4 or NiSO4-Na2SO4) which provided a selective dissolution of the Co or Ni and a subsequent sulfidation oxidation mode of attack which prevented the maintenance of a protective Cr2O3 film. A clear mechanism was not developed for the degradation of Co-Cr-Al alloys. A pitting corrosion morphology was induced by a number of different mechanisms.

Use of double-layer ITO films in reflective contacts for blue and near-UV LEDs

DOE Office of Scientific and Technical Information (OSTI.GOV)

Markov, L. K., E-mail: l.markov@mail.ioffe.ru; Smirnova, I. P.; Pavluchenko, A. S.

2014-12-15

The structural and optical properties of multilayer ITO/SiO{sub 2}/Ag composites are studied. In these composites, the ITO (indium-tin oxide) layer is produced by two different methods: electron-beam evaporation and a combined method including electron-beam evaporation and subsequent magnetron sputtering. It is shown that the reflectance of the composite based on the ITO film produced by electron-beam evaporation is substantially lower. This can be attributed to the strong absorption of light at both boundaries of the SiO{sub 2} layer, which results from the complex surface profile of ITO films deposited by electron-beam evaporation. Samples with a film deposited by the combinedmore » method have a reflectance of about 90% at normal light incidence, which, combined with their higher electrical conductivity, makes these samples advantageous for use as reflective contacts to the p-type region of AlInGaN light-emitting diodes of the flip-chip design.« less

Ceramic Heads Decrease Metal Release Caused by Head-taper Fretting and Corrosion.

PubMed

Kocagoz, Sevi B; Underwood, Richard J; MacDonald, Daniel W; Gilbert, Jeremy L; Kurtz, Steven M

2016-04-01

Metal release resulting from taper fretting and corrosion is a clinical concern, because wear and corrosion products may stimulate adverse local tissue reactions. Unimodular hip arthroplasties have a conical taper between the femoral head (head bore taper) and the femoral stem (stem cone taper). The use of ceramic heads has been suggested as a way of reducing the generation of wear and corrosion products from the head bore/stem cone taper junction. A previous semiquantitative study found that ceramic heads had less visual evidence of fretting-corrosion damage compared with CoCr heads; but, to our knowledge, no studies have quantified the volumetric material loss from the head bore and stem cone tapers of a matched cohort of ceramic and metal heads. We asked: (1) Do ceramic heads result in less volume of material loss at the head-stem junction compared with CoCr heads; (2) do stem cone tapers have less volumetric material loss compared with CoCr head bore tapers; (3) do visual fretting-corrosion scores correlate with volumetric material loss; and (4) are device, patient, or intraoperative factors associated with volumetric material loss? A quantitative method was developed to estimate volumetric material loss from the head and stem taper in previously matched cohorts of 50 ceramic and 50 CoCr head-stem pairs retrieved during revision surgery for causes not related to adverse reactions to metal particles. The cohorts were matched according to (1) implantation time, (2) stem flexural rigidity, and (3) lateral offset. Fretting corrosion was assessed visually using a previously published four-point, semiquantitative scoring system. The volumetric loss was measured using a precision roundness machine. Using 24 equally spaced axial traces, the volumetric loss was estimated using a linear least squares fit to interpolate the as-manufactured surfaces. The results of this analysis were considered in the context of device (taper angle clearance, head size, head offset, lateral offset, stem material, and stem surface finish) and patient factors that were obtained from the patients' operative records (implantation time, age at insertion, activity level, and BMI). The cumulative volumetric material losses estimated for the ceramic cohort had a median of 0.0 mm(3) per year (range, 0.0-0.4 mm(3)). The cumulative volumetric material losses estimated for the CoCr cohort had a median of 0.1 mm(3) per year (range, 0.0-8.8 mm(3)). An order of magnitude reduction in volumetric material loss was found when a ceramic head was used instead of a CoCr head (p < 0.0001). In the CoCr cohort, the femoral head bore tapers had a median material loss of 0.02 mm(3) (range, 0.0-8.7 mm(3)) and the stem cone tapers had a median material loss of 0.0 mm(3) (range, 0.0-0.32 mm(3)/year). There was greater material loss from femoral head bore tapers compared with stem cone tapers in the CoCr cohort (p < 0.001). There was a positive correlation between visual scoring and volumetric material loss (Spearman's ρ = 0.67, p < 0.01). Although visual scoring was effective for preliminary screening to separate tapers with no or mild damage from tapers with moderate to severe damage, it was not capable of discriminating in the large range of material loss observed at the taper surfaces with moderate to severe fretting-corrosion damage, indicated with a score of 3 or 4. We observed no correlations between volumetric material loss and device and patient factors. The majority of estimated material loss from the head bore-stem cone junctions resulting from taper fretting and corrosion was from the CoCr head bore tapers as opposed to the stem cone tapers. Additionally, the total material loss from the ceramic cohort showed a reduction in the amount of metal released by an order of magnitude compared with the CoCr cohort. We found that ceramic femoral heads may be an effective means by which to reduce metal release caused by taper fretting and corrosion at the head bore-stem cone modular interface in THAs.

Understanding the differences between the wear of metal-on-metal and ceramic-on-metal total hip replacements.

PubMed

Figueiredo-Pina, C G; Yan, Y; Neville, A; Fisher, J

2008-04-01

Hip simulator studies have been carried out extensively to understand and test artificial hip implants in vitro as an efficient alternative to obtaining long-term results in vivo. Recent studies have shown that a ceramic-on-metal material combination lowers the wear by up to 100 times in comparison with a typical metal-on-metal design. The reason for this reduction remains unclear and for this reason this study has undertaken simple tribometer tests to understand the fundamental material loss mechanisms in two material combinations: metal-on-metal and ceramic-on-ceramic. A simple-configuration reciprocating pin-on-plate wear study was performed under open-circuit potential (OCP) and with applied cathodic protection (CP) in a serum solution using two tribological couples: firstly, cobalt-chromium (Co-Cr) pins against Co-Cr plates; secondly, Co-Cr pins against alumina (Al2O3) plates. The pin and plate surfaces prior to and after testing were examined by profilometry and scanning electron microscopy. The results showed a marked reduction in wear when CP was applied, indicating that total material degradation under the OCP condition was attributed to corrosion processes. The substitution of the Co-Cr pin with an Al2O3 plate also resulted in a dramatic reduction in wear, probably due to the reduction in the corrosion-wear interactions between the tribological pair.

Effects of laser polishing on surface microstructure and corrosion resistance of additive manufactured CoCr alloys

NASA Astrophysics Data System (ADS)

Wang, W. J.; Yung, K. C.; Choy, H. S.; Xiao, T. Y.; Cai, Z. X.

2018-06-01

Laser polishing of 3D printed metal components has drawn great interest in view of its potential applications in the dental implant industries. In this study, corrosion resistance, surface composition and crystalline structure of CoCr alloys were investigated. The corrosion resistance, micromorphology, composition, phase transformations and crystalline structures of samples were characterized using an electrochemical analyzer, scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and transmission electron microscope (TEM), respectively. The results indicate that high laser powers and low object distances within a certain range can facilitate the formation of complex oxide films, which exhibits high corrosion resistance. Further, object distances have a significant influence on cooling rates during the solidification of the melt pool in laser polishing, and fast cooling generates vast amounts of vacancies and defects, which result in the crystalline phase transformation from γ to ε. Consequently, the formed oxides play an important role in corrosion resistance on the outer layer, and inner layer with γ phase also helps keep the CoCr alloys in a stable structure with high resistant to corrosion. The two process parameters in laser polishing, laser power and object distances, are demonstrated as being important for controlling the surface microstructures and corrosion resistance of the additive manufactured CoCr alloy components.

The entrapment of corrosion products from CoCr implant alloys in the deposits of calcium phosphate: a comparison of serum, synovial fluid, albumin, EDTA, and water.

PubMed

Lewis, A C; Kilburn, M R; Heard, P J; Scott, T B; Hallam, K R; Allen, G C; Learmonth, I D

2006-08-01

Physical wear of orthopedic implants is inevitable. CoCr alloy samples, typically used in joint reconstruction, corrode rapidly after removal of the protective oxide layer. The behavior of CoCr pellets immersed in human serum, foetal bovine serum (FBS), synovial fluid, albumin in phosphate-buffered saline (PBS), EDTA in PBS, and water were studied using X-ray Photoelectron Spectroscopy (XPS) and Time-of-Flight Secondary Ion Mass Spectroscopy (ToF-SIMS). The difference in the corrosive nature of human serum, water, albumin in PBS and synovial fluid after 5 days of immersion was highlighted by the oxide layer, which was respectively 15, 3.5, 1.5, and 1.5 nm thick. The thickness of an additional calcium phosphate deposit from human serum and synovial fluid was 40 and 2 nm, respectively. Co and Cr ions migrated from the bulk metal surface and were trapped in this deposit by the phosphate anion. This may account for the composition of wear debris from CoCr orthopedic implants, which is known to consist predominantly of hydroxy-phosphate compounds. Known components of synovial fluid including proteoglycans, pyrophosphates, phospholipids, lubricin, and superficial zone protein (SZP), have been identified as possible causes for the lack of significant calcium phosphate deposition in this environment. Circulation of these compounds around the whole implant may inhibit calcium phosphate deposition.

Stable aqueous dispersions of functionalized multi-layer graphene by pulsed underwater plasma exfoliation of graphite

NASA Astrophysics Data System (ADS)

Meyer-Plath, Asmus; Beckert, Fabian; Tölle, Folke J.; Sturm, Heinz; Mülhaupt, Rolf

2016-02-01

A process was developed for graphite particle exfoliation in water to stably dispersed multi-layer graphene. It uses electrohydraulic shockwaves and the functionalizing effect of solution plasma discharges in water. The discharges were excited by 100 ns high voltage pulsing of graphite particle chains that bridge an electrode gap. The underwater discharges allow simultaneous exfoliation and chemical functionalization of graphite particles to partially oxidized multi-layer graphene. Exfoliation is caused by shockwaves that result from rapid evaporation of carbon and water to plasma-excited gas species. Depending on discharge energy and locus of ignition, the shockwaves cause stirring, erosion, exfoliation and/or expansion of graphite flakes. The process was optimized to produce long-term stable aqueous dispersions of multi-layer graphene from graphite in a single process step without requiring addition of intercalants, surfactants, binders or special solvents. A setup was developed that allows continuous production of aqueous dispersions of flake size-selected multi-layer graphenes. Due to the well-preserved sp2-carbon structure, thin films made from the dispersed graphene exhibited high electrical conductivity. Underwater plasma discharge processing exhibits high innovation potential for morphological and chemical modifications of carbonaceous materials and surfaces, especially for the generation of stable dispersions of two-dimensional, layered materials.

Corrosion Damage and Wear Mechanisms in Long-Term Retrieved CoCr Femoral Components for Total Knee Arthroplasty.

PubMed

Arnholt, Christina M; MacDonald, Daniel W; Malkani, Arthur L; Klein, Gregg R; Rimnac, Clare M; Kurtz, Steven M; Kocagoz, Sevi B; Gilbert, Jeremy L

2016-12-01

Metal debris and ion release has raised concerns in joint arthroplasty. The purpose of this study was to characterize the sources of metallic ions and particulate debris released from long-term (in vivo >15 years) total knee arthroplasty femoral components. A total of 52 CoCr femoral condyles were identified as having been implanted for more than 15 years. The femoral components were examined for incidence of 5 types of damage (metal-on-metal wear due to historical polyethylene insert failure, mechanically assisted crevice corrosion at taper interfaces, cement interface corrosion, third-body abrasive wear, and inflammatory cell-induced corrosion [ICIC]). Third-body abrasive wear was evaluated using the Hood method for polyethylene components and a similar method quantifying surface damage of the femoral condyle was used. The total area damaged by ICIC was quantified using digital photogrammetry. Surface damage associated with corrosion and/or CoCr debris release was identified in 51 (98%) CoCr femoral components. Five types of damage were identified: 98% of femoral components exhibited third-body abrasive wear (mostly observed as scratching, n = 51/52), 29% of femoral components exhibited ICIC damage (n = 15/52), 41% exhibited cement interface damage (n = 11/27), 17% exhibited metal-on-metal wear after wear-through of the polyethylene insert (n = 9/52), and 50% of the modular femoral components exhibited mechanically assisted crevice corrosion taper damage (n = 2/4). The total ICIC-damaged area was an average of 0.11 ± 0.12 mm 2 (range: 0.01-0.46 mm 2 ). Although implant damage in total knee arthroplasty is typically reported with regard to the polyethylene insert, the results of this study demonstrate that abrasive and corrosive damage occurs on the CoCr femoral condyle in vivo. Copyright © 2016 Elsevier Inc. All rights reserved.

Annealing of Co-Cr dental alloy: effects on nanostructure and Rockwell hardness.

PubMed

Ayyıldız, Simel; Soylu, Elif Hilal; Ide, Semra; Kılıç, Selim; Sipahi, Cumhur; Pişkin, Bulent; Gökçe, Hasan Suat

2013-11-01

The aim of the study was to evaluate the effect of annealing on the nanostructure and hardness of Co-Cr metal ceramic samples that were fabricated with a direct metal laser sintering (DMLS) technique. Five groups of Co-Cr dental alloy samples were manufactured in a rectangular form measuring 4 × 2 × 2 mm. Samples fabricated by a conventional casting technique (Group I) and prefabricated milling blanks (Group II) were examined as conventional technique groups. The DMLS samples were randomly divided into three groups as not annealed (Group III), annealed in argon atmosphere (Group IV), or annealed in oxygen atmosphere (Group V). The nanostructure was examined with the small-angle X-ray scattering method. The Rockwell hardness test was used to measure the hardness changes in each group, and the means and standard deviations were statistically analyzed by one-way ANOVA for comparison of continuous variables and Tukey's HSD test was used for post hoc analysis. P values of <.05 were accepted as statistically significant. The general nanostructures of the samples were composed of small spherical entities stacked atop one another in dendritic form. All groups also displayed different hardness values depending on the manufacturing technique. The annealing procedure and environment directly affected both the nanostructure and hardness of the Co-Cr alloy. Group III exhibited a non-homogeneous structure and increased hardness (48.16 ± 3.02 HRC) because the annealing process was incomplete and the inner stress was not relieved. Annealing in argon atmosphere of Group IV not only relieved the inner stresses but also decreased the hardness (27.40 ± 3.98 HRC). The results of fitting function presented that Group IV was the most homogeneous product as the minimum bilayer thickness was measured (7.11 Å). After the manufacturing with DMLS technique, annealing in argon atmosphere is an essential process for Co-Cr metal ceramic substructures. The dentists should be familiar with the materials that are used in clinic for prosthodontics treatments.

Improving the fit of implant prosthetics: an in vitro study.

PubMed

Yannikakis, Stavros; Prombonas, Anthony

2013-01-01

Accurate and passive fit between a prosthesis and its supporting implants has been considered a prerequisite for successful long-term osseointegration. The objective of this in vitro study was to evaluate the strain development during tightening of a five-unit screw-retained superstructure constructed using five different methods. Five-unit screw-retained fixed partial prostheses (n = 25) were fabricated on three implants embedded in an epoxy resin block using five different methods: (1) cobalt-chromium (Co-Cr), plastic cylinders, one-piece cast; (2) Co-Cr, plastic cylinders, framework sectioned, preceramic laser-welding soldering; (3) gold-platinum (Au-Pt), gold cylinders, one-piece cast; (4) Au-Pt, gold cylinders, framework sectioned, preceramic laser-welding soldering; (5) Co-Cr, one-piece cast, and cementation to "passive abutments" (Southern Implants) after final finishing and polishing. Strain gauges (SG) were attached to the fixed partial prosthesis (FPP) and to the resin block to measure the stress created during screw tightening. The combination of Co-Cr alloy and plastic cylinders in a one-piece cast showed such an inadequate fit among the fabricated methods that this group was excluded from the remainder of the experiment. Specimens of Au-Pt cast on gold cylinders in one piece showed higher strain development than the other groups used in this study, with strains ranging from 223.1 to 2,198.1 Μm/m. Sectioning and soldering significantly improved the overall fit. FPPs of Co-Cr in a one-piece cast cemented to "passive abutments" produced the best level of fit, with the least strain development in the prosthesis and the resin block (59 to 204.6 Μm/m). Absolute fit of superstructures on implants is not possible using conventional laboratory procedures. Cementing FPPs onto prefabricated cylinders directly onto the implants significantly reduces strain development compared to the other fabrication methods.

Revision total hip arthroplasty due to pain from hypersensitivity to cobalt-chromium in total hip arthroplasty.

PubMed

Kosukegawa, Ima; Nagoya, Satoshi; Kaya, Mitsunori; Sasaki, Koichi; Sasaki, Mikito; Yamashita, Toshihiko

2011-09-01

We report a case with hypersensitivity to CoCr in total hip arthroplasty coupled with conventional polyethylene and CoCr femoral head. The patient complained of left hip pain and systemic fever, and computed tomography imaging revealed a periprosthetic cystic lesion, so we performed revision total hip arthroplasty using a titanium stem and ceramic head and highly crosslinked polyethylene. Hip pain and cystic lesion disappeared 3 years after revision surgery. Copyright © 2011 Elsevier Inc. All rights reserved.

Controlled assembly of nanoparticle structures: spherical and toroidal superlattices and nanoparticle-coated polymeric beads.

PubMed

Isojima, Tatsushi; Suh, Su Kyung; Vander Sande, John B; Hatton, T Alan

2009-07-21

The emulsion droplet solvent evaporation method has been used to prepare nanoclusters of monodisperse magnetite nanoparticles of varying morphologies depending on the temperature and rate of solvent evaporation and on the composition (solvent, presence of polymer, nanoparticle concentration, etc.) of the emulsion droplets. In the absence of a polymer, and with increasing solvent evaporation temperatures, the nanoparticles formed single- or multidomain crystalline superlattices, amorphous spherical aggregates, or toroidal clusters, as determined by the energetics and dynamics of the solvent evaporation process. When polymers that are incompatible with the nanoparticle coatings were included in the emulsion formulation, monolayer- and multilayer-coated polymer beads and partially coated Janus beads were prepared; the nanoparticles were expelled by the polymer as its concentration increased on evaporation of the solvent and accumulated on the surfaces of the beads in a well-ordered structure. The precise number of nanoparticle layers depended on the polymer/magnetic nanoparticle ratio in the oil droplet phase parent emulsion. The magnetic nanoparticle superstructures responded to the application of a modest magnetic field by forming regular chains with alignment of nonuniform structures (e.g., toroids and Janus beads) that are in accord with theoretical predictions and with observations in other systems.

Comparative analysis of the fit of 3-unit implant-supported frameworks cast in nickel-chromium and cobalt-chromium alloys and commercially pure titanium after casting, laser welding, and simulated porcelain firings.

PubMed

Tiossi, Rodrigo; Rodrigues, Renata Cristina Silveira; de Mattos, Maria da Glória Chiarello; Ribeiro, Ricardo Faria

2008-01-01

This study compared the vertical misfit of 3-unit implant-supported nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloy and commercially pure titanium (cpTi) frameworks after casting as 1 piece, after sectioning and laser welding, and after simulated porcelain firings. The results on the tightened side showed no statistically significant differences. On the opposite side, statistically significant differences were found for Co-Cr alloy (118.64 microm [SD: 91.48] to 39.90 microm [SD: 27.13]) and cpTi (118.56 microm [51.35] to 27.87 microm [12.71]) when comparing 1-piece to laser-welded frameworks. With both sides tightened, only Co-Cr alloy showed statistically significant differences after laser welding. Ni-Cr alloy showed the lowest misfit values, though the differences were not statistically significantly different. Simulated porcelain firings revealed no significant differences.

[Study on corrosion resistance of three non-noble porcelain alloys].

PubMed

Wu, Zhikai; Xu, Sheng; Li, Wei; Teng, Jin; Li, Ning

2011-10-01

To study the electrochemical corrosion behavior of Co-Cr, Ni-Cr and Ni-Cr-Be based porcelain alloys in NaCl solution. Five samples of each alloy were made respectively, electric polarization curve of each alloy was obtained using potentiodynamic polarization technique. Self-corrosion potential (E(corr)), self-corrosion current density (I(corr), passive region and transpassivation potential were tested. Microstructure and constituent was examined using scanning electron microscopy and energy dispersive spectroscopy. Co-Cr alloy possessed the most desirable corrosion resistance because of its integrated, homogeneous and compact passive film. The poor compactness of Ni-Cr alloy's passive film decreased its corrosion resistance. Ni-Cr-Be alloy exhibited the worst corrosion resistance due to the Cr and Mo depleted Ni-Be eutectic phases in the alloy. Taking biological security into consideration, it is necessary to avoid the application of porcelain alloys with Be element. Co-Cr alloy with better biocompatibility possesses much broader prospect in the field of dental restoration.

Biomechanical comparison of the strength of adhesion of polymethylmethacrylate cement to zirconia ceramic and cobalt-chromium alloy components in a total knee arthroplasty.

PubMed

Kumahashi, Nobuyuki; Uchio, Yuji; Kitamura, Nobuto; Satake, Shigeru; Iwamoto, Mikio; Yasuda, Kazunori

2014-11-01

The purpose of this study was to clarify the biomechanical characteristics of cement-material interfaces for the zirconia ceramic and cobalt-chromium (Co-Cr) alloy femoral components used for total knee arthroplasty. In the first sub-study, we compared the strength of adhesion of the cement to flat plates, by tensile testing under dry and moistened conditions. In the second sub-study, we compared the maximum load of the cement-component complex by tensile testing. In the third sub-study, we compared the fatigue characteristics of the cement-component complex by use of a dynamic tensile testing machine. Under dry conditions, the maximum strength of adhesion to the zirconia ceramic plate was the same as that to the Co-Cr alloy plate. Under moistened conditions, however, the strength of adhesion to the zirconia ceramic plate was significantly lower (p = 0.0017) whereas the strength of adhesion to the Co-Cr alloy plate was not reduced. Maximum load for the cement-component complexes for zirconia ceramic and Co-Cr alloy was no different under both dry and moistened conditions. Fatigue testing showed that cement-zirconia adhesion was stronger than cement-Co-Cr alloy adhesion (p = 0.0161). The strength of adhesion of cement to zirconia ceramic is substantially weaker under wet conditions than under dry conditions. The mechanical properties of cement-zirconia ceramic component complexes and cement-Co-Cr alloy component complexes are equivalent.

Removable partial denture alloys processed by laser-sintering technique.

PubMed

Alageel, Omar; Abdallah, Mohamed-Nur; Alsheghri, Ammar; Song, Jun; Caron, Eric; Tamimi, Faleh

2018-04-01

Removable partial dentures (RPDs) are traditionally made using a casting technique. New additive manufacturing processes based on laser sintering has been developed for quick fabrication of RPDs metal frameworks at low cost. The objective of this study was to characterize the mechanical, physical, and biocompatibility properties of RPD cobalt-chromium (Co-Cr) alloys produced by two laser-sintering systems and compare them to those prepared using traditional casting methods. The laser-sintered Co-Cr alloys were processed by the selective laser-sintering method (SLS) and the direct metal laser-sintering (DMLS) method using the Phenix system (L-1) and EOS system (L-2), respectively. L-1 and L-2 techniques were 8 and 3.5 times more precise than the casting (CC) technique (p < 0.05). Co-Cr alloys processed by L-1 and L-2 showed higher (p < 0.05) hardness (14-19%), yield strength (10-13%), and fatigue resistance (71-72%) compared to CC alloys. This was probably due to their smaller grain size and higher microstructural homogeneity. All Co-Cr alloys exhibited low porosity (2.1-3.3%); however, pore distribution was more homogenous in L-1 and L-2 alloys when compared to CC alloys. Both laser-sintered and cast alloys were biocompatible. In conclusion, laser-sintered alloys are more precise and present better mechanical and fatigue properties than cast alloys for RPDs. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1174-1185, 2018. © 2017 Wiley Periodicals, Inc.

Additively Manufactured Titanium and Cobalt-Chromium Implant Frameworks: Fit and Effect of Ceramic Veneering.

PubMed

Svanborg, Per; Eliasson, Alf; Stenport, Victoria

The purpose of this study was to evaluate the fit of additively manufactured cobalt-chromium and titanium and CNC-milled titanium frameworks before and after ceramic veneering. Ten stone casts simulating an edentulous maxilla provided with six abutment analogs were produced. For each stone cast, one additively manufactured cobalt-chromium framework (AM CoCr) and one titanium framework (AM Ti) were fabricated. The fit was analyzed with a coordinate measuring machine in three dimensions (x, y, and z axes) using best-fit virtual matching of center point coordinates, before and after ceramic veneering. CNC-milled titanium frameworks (CNC Ti) and earlier results from CNC-milled cobalt-chromium frameworks (CNC CoCr) were used for comparison. All frameworks presented minor misfit before and after veneering in the horizontal plane (x- and y-axes) between 2.9 and 13.5 μm and in the vertical plane (z-axis) between 1.6 and 5.4 μm. Ceramic veneering affected the fit of all groups of frameworks. Both AM Ti and AM CoCr presented significantly smaller distortion in the vertical plane compared with the CNC-milled frameworks. Implant-supported frameworks can be produced in either Ti or CoCr using either CNC milling or additive manufacturing with a fit well within the range of 20 μm in the horizontal plane and 10 μm in the vertical plane. The fit of frameworks of both materials and production techniques are affected by the ceramic veneering procedure to a small extent.

Macrophage responses to 316L stainless steel and cobalt chromium alloys with different surface topographies.

PubMed

Anderson, Jordan A; Lamichhane, Sujan; Mani, Gopinath

2016-11-01

The surface topography of a biomaterial plays a vital role in determining macrophage interactions and influencing immune response. In this study, we investigated the effect of smooth and microrough topographies of commonly used metallic biomaterials such as 316 L stainless steel (SS) and cobalt-chromium (CoCr) alloys on macrophage interactions. The macrophage adhesion was greater on CoCr compared to SS, irrespective of their topographies. The macrophage activation and the secretion of most pro-inflammatory cytokines (TNF-α, IL-6, and IP-10) were greater on microrough surfaces than on smooth surfaces by day-1. However, by day-2, the macrophage activation on smooth surfaces was also significantly increased up to the same level as observed on the microrough surfaces, with more amount of cytokines secreted. The secretion of anti-inflammatory cytokine (IL-10) was significantly increased from day-1 to day-2 on all the alloy surfaces with the effect most prominently observed on microrough surfaces. The production of nitric oxide by the macrophages did not show any major substrate-dependent effect. The foreign body giant cells formed by macrophages were least observed on the microrough surfaces of CoCr. Thus, this study demonstrated that the nature of material (SS or CoCr) and their surface topographies (smooth or microrough) strongly influence the macrophage responses. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 104A: 2658-2672, 2016. © 2016 Wiley Periodicals, Inc.

Pan evaporation prediction using a hybrid multilayer perceptron-firefly algorithm (MLP-FFA) model: case study in North Iran

NASA Astrophysics Data System (ADS)

Ghorbani, M. A.; Deo, Ravinesh C.; Yaseen, Zaher Mundher; H. Kashani, Mahsa; Mohammadi, Babak

2017-08-01

An accurate computational approach for the prediction of pan evaporation over daily time horizons is a useful decisive tool in sustainable agriculture and hydrological applications, particularly in designing the rural water resource systems, water use allocations, utilization and demand assessments, and the management of irrigation systems. In this study, a hybrid predictive model (Multilayer Perceptron-Firefly Algorithm (MLP-FFA)) based on the FFA optimizer that is embedded within the MLP technique is developed and evaluated for its suitability for the prediction of daily pan evaporation. To develop the hybrid MLP-FFA model, the pan evaporation data measured between 2012 and 2014 for two major meteorological stations (Talesh and Manjil) located at Northern Iran are employed to train and test the predictive model. The ability of the hybrid MLP-FFA model is compared with the traditional MLP and support vector machine (SVM) models. The results are evaluated using five performance criteria metrics: root mean square error (RMSE), mean absolute error (MAE), Nash-Sutcliffe efficiency (NS), and the Willmott's Index (WI). Taylor diagrams are also used to examine the similarity between the observed and predicted pan evaporation data in the test period. Results show that an optimal MLP-FFA model outperforms the MLP and SVM model for both tested stations. For Talesh, a value of WI = 0.926, NS = 0.791, and RMSE = 1.007 mm day-1 is obtained using MLP-FFA model, compared with 0.912, 0.713, and 1.181 mm day-1 (MLP) and 0.916, 0.726, and 1.153 mm day-1 (SVM), whereas for Manjil, a value of WI = 0.976, NS = 0.922, and 1.406 mm day-1 is attained that contrasts 0.972, 0.901, and 1.583 mm day-1 (MLP) and 0.971, 0.893, and 1.646 mm day-1 (SVM). The results demonstrate the importance of the Firefly Algorithm applied to improve the performance of the MLP-FFA model, as verified through its better predictive performance compared to the MLP and SVM model.

Flexible growing rods: a pilot study to determine if polymer rod constructs may provide stability to skeletally immature spines

PubMed Central

2015-01-01

Background Surgical treatments for early onset scoliosis (EOS), including growing rod constructs, involve many complications. Some are due to biomechanical factors. A construct that is more flexible than current instrumentation systems may reduce complications. The purpose of this preliminary study was to determine spine range of motion (ROM) after implantation of simulated growing rod constructs with a range of clinically relevant structural properties. The hypothesis was that ROM of spines instrumented with polyetheretherketone (PEEK) rods would be greater than metal rods and lower than noninstrumented controls. Further, adjacent segment motion was expected to be lower with polymer rods compared to conventional systems. Methods Biomechanical tests were conducted on 6 skeletally immature porcine thoracic spines (domestic swine, 35-40 kg). Spines were harvested after death from swine that had been utilized for other studies (IACUC approved) which had not involved the spine. Paired pedicle screws were used as anchors at proximal and distal levels. Specimens were tested under the following conditions: control, then dual rods of PEEK (6.25 mm), titanium (4 mm), and CoCr (5 mm) alloy. Lateral bending (LB) and flexion-extension (FE) moments of ±5 Nm were applied. Vertebral rotations were measured using video. Differences were determined by two-tailed t-tests and Bonferroni correction with four primary comparisons: PEEK vs control and PEEK vs CoCr, in LB and FE (α=0.05/4). Results In LB, ROM of specimens with PEEK rods was lower than control at each instrumented level. ROM was greater for PEEK rods than both Ti and CoCr at every instrumented level. Mean ROM at proximal and distal noninstrumented levels was lower for PEEK than for Ti and CoCr. In FE, mean ROM at proximal and distal noninstrumented levels was lower for PEEK than for metal. Combining treated levels, in LB, ROM for PEEK rods was 35% of control (p<0.0001) and 270% of CoCr rods (p<0.01). In FE, ROM with PEEK was 27% of control (p<0.001) and 180% of CoCr (p<0.01). Conclusions PEEK rods decreased flexibility versus noninstumented controls, and increased flexibility versus metal rods. Smaller increases in ROM at proximal and distal adjacent motion segments occurred with PEEK compared to metal rods, which may help decrease junctional kyphosis. Flexible growing rods may eventually help improve treatment options for young patients with severe deformity. PMID:25810752

Multilayer Coatings for UV Spectral Range

NASA Astrophysics Data System (ADS)

Miloushev, Ilko; Tenev, Tihomir; Peyeva, Rumiana; Panajotov, Krassimir

2010-01-01

Optical coatings for the UV spectral range play currently a significant role in the modern optical devices. For reducing of manufacturing cost the reliable design is essential. Therefore, better understanding of the optical properties of the used materials is indispensable for the proper design and manufacturing of the multilayer UV coatings. In this work we present some results on the preparation of reflective UV coatings. The implemented materials are magnesium fluoride and lanthanum fluoride. Their optical constants are determined from spectral characteristics of single layers in the 200-800 nm spectral range, obtained by thermal boat evaporation in high vacuum conditions. These results are subsequently used for the analysis of high reflection (HR) stack made of 40 layers deposited by the same deposition process.

Improved rate control for electron-beam evaporation and evaluation of optical performance improvements.

PubMed

Gevelber, Michael; Xu, Bing; Smith, Douglas

2006-03-01

A new deposition-rate-control and electron-beam-gun (e-gun) strategy was developed that significantly reduces the growth-rate variations for e-beam-deposited SiO2 coatings. The resulting improvements in optical performance are evaluated for multilayer bandpass filters. The adverse effect of uneven silica-source depletion on coating spectral performances during long deposition runs is discussed.

Time-resolved Sensing of Meso-scale Shock Compression with Multilayer Photonic Crystal Structures

NASA Astrophysics Data System (ADS)

Scripka, David; Lee, Gyuhyon; Summers, Christopher J.; Thadhani, Naresh

2017-06-01

Multilayer Photonic Crystal structures can provide spatially and temporally resolved data needed to validate theoretical and computational models relevant for understanding shock compression in heterogeneous materials. Two classes of 1-D photonic crystal multilayer structures were studied: optical microcavities (OMC) and distributed Bragg reflectors (DBR). These 0.5 to 5 micron thick structures were composed of SiO2, Al2O3, Ag, and PMMA layers fabricated primarily via e-beam evaporation. The multilayers have unique spectral signatures inherently linked to their time-resolved physical states. By observing shock-induced changes in these signatures, an optically-based pressure sensor was developed. Results to date indicate that both OMCs and DBRs exhibit nanosecond-resolved spectral shifts of several to 10s of nanometers under laser-driven shock compression loads of 0-10 GPa, with the magnitude of the shift strongly correlating to the shock load magnitude. Additionally, spatially and temporally resolved spectral shifts under heterogeneous laser-driven shock compression created by partial beam blocking have been successfully demonstrated. These results illustrate the potential for multilayer structures to serve as meso-scale sensors, capturing temporal and spatial pressure profile evolutions in shock-compressed heterogeneous materials, and revealing meso-scale pressure distributions across a shocked surface. Supported by DTRA Grant HDTRA1-12-1-005 and DoD, AFOSR, National Defense Science and Eng. Graduate Fellowship, 32 CFR 168a.

Annealing of Co-Cr dental alloy: effects on nanostructure and Rockwell hardness

PubMed Central

Soylu, Elif Hilal; İde, Semra; Kılıç, Selim; Sipahi, Cumhur; Pişkin, Bulent; Gökçe, Hasan Suat

2013-01-01

PURPOSE The aim of the study was to evaluate the effect of annealing on the nanostructure and hardness of Co-Cr metal ceramic samples that were fabricated with a direct metal laser sintering (DMLS) technique. MATERIALS AND METHODS Five groups of Co-Cr dental alloy samples were manufactured in a rectangular form measuring 4 × 2 × 2 mm. Samples fabricated by a conventional casting technique (Group I) and prefabricated milling blanks (Group II) were examined as conventional technique groups. The DMLS samples were randomly divided into three groups as not annealed (Group III), annealed in argon atmosphere (Group IV), or annealed in oxygen atmosphere (Group V). The nanostructure was examined with the small-angle X-ray scattering method. The Rockwell hardness test was used to measure the hardness changes in each group, and the means and standard deviations were statistically analyzed by one-way ANOVA for comparison of continuous variables and Tukey's HSD test was used for post hoc analysis. P values of <.05 were accepted as statistically significant. RESULTS The general nanostructures of the samples were composed of small spherical entities stacked atop one another in dendritic form. All groups also displayed different hardness values depending on the manufacturing technique. The annealing procedure and environment directly affected both the nanostructure and hardness of the Co-Cr alloy. Group III exhibited a non-homogeneous structure and increased hardness (48.16 ± 3.02 HRC) because the annealing process was incomplete and the inner stress was not relieved. Annealing in argon atmosphere of Group IV not only relieved the inner stresses but also decreased the hardness (27.40 ± 3.98 HRC). The results of fitting function presented that Group IV was the most homogeneous product as the minimum bilayer thickness was measured (7.11 Å). CONCLUSION After the manufacturing with DMLS technique, annealing in argon atmosphere is an essential process for Co-Cr metal ceramic substructures. The dentists should be familiar with the materials that are used in clinic for prosthodontics treatments. PMID:24353888

No difference in in vivo polyethylene wear particles between oxidized zirconium and cobalt-chromium femoral component in total knee arthroplasty.

PubMed

Minoda, Yukihide; Hata, Kanako; Iwaki, Hiroyoshi; Ikebuchi, Mitsuhiko; Hashimoto, Yusuke; Inori, Fumiaki; Nakamura, Hiroaki

2014-03-01

Polyethylene wear particle generation is one of the most important factors affecting mid- to long-term results of total knee arthroplasties. Oxidized zirconium was introduced as a material for femoral components to reduce polyethylene wear generation. However, an in vivo advantage of oxidized zirconium on polyethylene wear particle generation is still controversial. The purpose of this study was to compare in vivo polyethylene wear particles between oxidized zirconium total knee prosthesis and conventional cobalt-chromium (Co-Cr) total knee prosthesis. Synovial fluid was obtained from the knees of 6 patients with oxidized zirconium total knee prosthesis and from 6 patients with conventional cobalt-chromium (Co-Cr) total knee prosthesis 12 months after the operation. Polyethylene particles were isolated and examined using a scanning electron microscope and image analyser. Total number of particles in each knee was 3.3 ± 1.3 × 10(7) in the case of oxidized zirconium (mean ± SD) and 3.4 ± 1.2 × 10(7) in that of Co-Cr (n.s.). The particle size (equivalent circle diameter) was 0.8 ± 0.3 μm in the case of oxidized zirconium and 0.6 ± 0.1 μm in that of Co-Cr (n.s.). The particle shape (aspect ratio) was 1.4 ± 0.0 in the case of oxidized zirconium and 1.4 ± 0.0 in that of metal Co-Cr (n.s). Although newly introduced oxidized zirconium femoral component did not reduce the in vivo polyethylene wear particles in early clinical stage, there was no adverse effect of newly introduced material. At this moment, there is no need to abandon oxidized zirconium femoral component. However, further follow-up of polyethylene wear particle generation should be performed to confirm the advantage of the oxidized zirconium femoral component. Therapeutic study, Level III.

Photoelastic analysis of mandibular full-arch implant-supported fixed dentures made with different bar materials and manufacturing techniques.

PubMed

Zaparolli, Danilo; Peixoto, Raniel Fernandes; Pupim, Denise; Macedo, Ana Paula; Toniollo, Marcelo Bighetti; Mattos, Maria da Glória Chiarello de

2017-12-01

To compare the stress distribution of mandibular full dentures supported with implants according to the bar materials and manufacturing techniques using a qualitative photoelastic analysis. An acrylic master model simulating the mandibular arch was fabricated with four Morse taper implant analogs of 4.5×6mm. Four different bars were manufactured according to different material and techniques: fiber-reinforced resin (G1, Trinia, CAD/CAM), commercially pure titanium (G2, cpTi, CAD/CAM), cobalt‑chromium (G3, Co-Cr, CAD/CAM) and cobalt‑chromium (G4, Co-Cr, conventional cast). Standard clinical and laboratory procedures were used by an experienced dental technician to fabricate 4 mandibular implant-supported dentures. The photoelastic model was created based on the acrylic master model. A load simulation (150N) was performed in total occlusion against the antagonist. Dentures with fiber-reinforced resin bar (G1) exhibited better stress distribution. Dentures with machined Co-Cr bar (G3) exhibited the worst standard of stress distribution, with an overload on the distal part of the posteriors implants, followed by dentures with cast Co-Cr bar (G4) and machined cpTi bar (G2). The fiber-reinforced resin bar exhibited an adequate stress distribution and can serve as a viable alternative for oral rehabilitation with mandibular full dentures supported with implants. Moreover, the use of the G1 group offered advantages including reduced weight and less possible overload to the implants components, leading to the preservation of the support structure. Copyright © 2017 Elsevier B.V. All rights reserved.

Quantifying subtle but persistent peri-spine inflammation in vivo to submicron cobalt-chromium alloy particles.

PubMed

Hallab, Nadim James; Chan, Frank W; Harper, Megan L

2012-12-01

We evaluated the consequences of cobalt-chromium alloy (CoCr) wear debris challenge in the peri-spine region to determine the inflammation and toxicity associated with submicron particulates of CoCr-alloy and nickel on the peri-spine. The lumbar epidural spaces of (n = 50) New Zealand white rabbits were challenged with: 2.5 mg CoCr, 5.0 mg CoCr, 10.0 mg CoCr, a positive control (20.0 mg of nickel) and a negative control (ISOVUE-M-300). The CoCr-alloy and Ni particles had a mean diameter of 0.2 and 0.6 μm, respectively. Five rabbits per dose group were studied at 12 and 24 weeks. Local and distant tissues were analyzed histologically and quantitatively analyzed immunohistochemically (TNF-α and IL-6). Histologically, wear particles were observed in all animals. There was no evidence of toxicity or local irritation noted during macroscopic observations in any CoCr-dosed animals. However, Ni-treated control animals experienced bilateral hind leg paralysis and were euthanized at Day 2. Histopathology of the Ni particle-treated group revealed severe neuropathy. Quantitative immunohistochemistry demonstrated a CoCr-alloy dose-dependent increase in cytokines (IL-6, TNF-α, p < 0.05) at 12 and 24 weeks. Subtle peri-spine inflammation associated with CoCr-alloy implant particles was dose dependent and persistent. Neuropathy can be induced by highly reactive Ni particles. This suggests peri-spine challenge with CoCr-alloy implant debris (e.g., TDA) is consistent with past reports using titanium alloy particles, i.e., mild persistent inflammation.

Metal-ceramic bond strength between a feldspathic porcelain and a Co-Cr alloy fabricated with Direct Metal Laser Sintering technique.

PubMed

Dimitriadis, Konstantinos; Spyropoulos, Konstantinos; Papadopoulos, Triantafillos

2018-02-01

The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity ( E ) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was 222 ± 5.13 GPa and 227 ± 3 GPa, respectively. The bond strength was 51.87 ± 7.50 MPa for test group and 54.60 ± 6.20 MPa for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. Specimens produced by the DMLS technique cover the lowest acceptable metal-ceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use.

The influence of dental alloys on three-body wear of human enamel and dentin in an inlay-like situation.

PubMed

Graf, K; Johnson, G H; Mehl, A; Rammelsberg, P

2002-01-01

This in vitro study evaluated the effect of metal alloys on three-body wear resistance of enamel and dentin, and vice versa. Three-body wear of human enamel, dentin, a soft gold alloy (BiOcclus Inlay), a CoCr alloy (Remanium 2000), a resin cement (Variolink II) and a zinc oxide phosphate cement (Harvard) was investigated using the ACTA-machine. Sample chambers of eight sample wheels were prepared with pure materials or combinations of human tooth substance, alloys and cement, simulating an inlay-like situation. After 100,000 and 200,000 cycles in a millet suspension with a spring force of 20 N, the amount of abraded material was profilometrically measured and evaluated by 3D surface data analysis. After 200,000 cycles, the materials demonstrated a mean loss of 0.41 microm for CoCr, 51 microm for gold, 57 microm for enamel, 164 microm for dentin, 79 microm for Variolink and 369 microm for Harvard. Using ANOVA and the Games-Howell-test, resin cement, enamel and gold were a subset not shown to differ, as was zinc phosphate cement and dentin. CoCr demonstrated the least wear and differed significantly from all materials. Enamel wear was significantly reduced in mixed chambers with CoCr, and gold after 200,000 cycles compared to enamel in pure chambers. In summary, a soft gold alloy can be recommended for inlays when considering three-body abrasion since the wear rate of the "soft" gold alloy corresponded to that of human enamel.

Free form fabricated features on CoCr implants with and without hydroxyapatite coating in vivo: a comparative study of bone contact and bone growth induction.

PubMed

Grandfield, Kathryn; Palmquist, Anders; Gonçalves, Stéphane; Taylor, Andy; Taylor, Mark; Emanuelsson, Lena; Thomsen, Peter; Engqvist, Håkan

2011-04-01

The current study evaluates the in vivo response to free form fabricated cobalt chromium (CoCr) implants with and without hydroxyapatite (HA) plasma sprayed coatings. The free form fabrication method allowed for integration of complicated pyramidal surface structures on the cylindrical implant. Implants were press fit into the tibial metaphysis of nine New Zealand white rabbits. Animals were sacrificed and implants were removed and embedded. Histological analysis, histomorphometry and electron microscopy studies were performed. Focused ion beam was used to prepare thin sections for high-resolution transmission electron microscopy examination. The fabricated features allowed for effective bone in-growth and firm fixation after 6 weeks. Transmission electron microscopy investigations revealed intimate bone-implant integration at the nanometre scale for the HA coated samples. In addition, histomorphometry revealed a significantly higher bone contact on HA coated implants compared to native CoCr implants. It is concluded that free form fabrication in combination with HA coating improves the early fixation in bone under experimental conditions.

Laser welding of removable partial denture frameworks.

PubMed

Brudvik, James S; Lee, Seungbum; Croshaw, Steve N; Reimers, Donald L; Reimers, Dave L

2008-01-01

To identify and measure distortions inherent in the casting process of a Class III mandibular cobalt-chromium (Co-Cr) framework to illustrate the problems faced by the laboratory technician and the clinician and to measure the changes that occur during the correction of the fit discrepancy using laser welding. Five identical castings of a Co-Cr alloy partial denture casting were made and measured between 3 widely separated points using the x, y, and z adjustments of a Nikon Measurescope. The same measurements were made after each of the following clinical and laboratory procedures: sprue removal, sectioning of the casting into 3 parts through the posterior meshwork, fitting the segments to the master cast, picking up the segments using resin, and laser welding of the 3 segments. Measurements of all 5 castings showed a cross-arch decrease after sprue removal, an increase after fitting the segments to the master cast, and a slight decrease after resin pickup and laser welding. Within the limitations of this study, the findings suggest that precise tooth-frame relations can be established by resin pickup and laser welding of segments of Co-Cr removable partial denture frameworks.

Mechanical strength and microstructure of laser-welded Ti-6Al-7Nb alloy castings.

PubMed

Srimaneepong, Viritpon; Yoneyama, Takayuki; Kobayashi, Equo; Doi, Hisashi; Hanawa, Takao

2005-12-01

Mechanical properties of laser-welded castings of Ti-6Al-7Nb alloy, CP Ti, and Co-Cr alloy were investigated and compared to the unwelded castings using a tensile test. Dumbbell-shaped specimens were cut at the center, and two halves of the specimens were welded with an Nd:YAG laser welding machine at 220 or 260 V of laser voltage. The mechanical strength of 260 V groups was higher than that of 220 V groups for Ti-6Al-7Nb and Co-Cr alloys except for CP Ti. All 260 V laser-welded castings of Ti-6Al-7Nb alloy and CP Ti, which fractured outside the welded joints, exhibited ductile characteristics, while all laser-welded Co-Cr alloy castings, which fractured within the welded joints, showed brittle characteristics. This study proved that the mechanical strength of laser-welded Ti-6Al-7Nb alloy and CP Ti castings was as high as that of unwelded castings, while the mechanical properties of laser-welded alloy joints were influenced by microstructural changes.

A chemically stable PVD multilayer encapsulation for lithium microbatteries

NASA Astrophysics Data System (ADS)

Ribeiro, J. F.; Sousa, R.; Cunha, D. J.; Vieira, E. M. F.; Silva, M. M.; Dupont, L.; Goncalves, L. M.

2015-10-01

A multilayer physical vapour deposition (PVD) thin-film encapsulation method for lithium microbatteries is presented. Lithium microbatteries with a lithium cobalt oxide (LiCoO2) cathode, a lithium phosphorous oxynitride (LiPON) electrolyte and a metallic lithium anode are under development, using PVD deposition techniques. Metallic lithium film is still the most common anode on this battery technology; however, it presents a huge challenge in terms of material encapsulation (lithium reacts with almost any materials deposited on top and almost instantly begins oxidizing in contact with atmosphere). To prove the encapsulation concept and perform all the experiments, lithium films were deposited by thermal evaporation technique on top of a glass substrate, with previously patterned Al/Ti contacts. Three distinct materials, in a multilayer combination, were tested to prevent lithium from reacting with protection materials and atmosphere. These multilayer films were deposited by RF sputtering and were composed of lithium phosphorous oxide (LiPO), LiPON and silicon nitride (Si3N4). To complete the long-term encapsulation after breaking the vacuum, an epoxy was applied on top of the PVD multilayer. In order to evaluate oxidation state of lithium films, the lithium resistance was measured in a four probe setup (cancelling wires/contact resistances) and resistivity calculated, considering physical dimensions. A lithium resistivity of 0.16 Ω μm was maintained for more than a week. This PVD multilayer exonerates the use of chemical vapour deposition (CVD), glove-box chambers and sample manipulation between them, significantly reducing the fabrication cost, since battery and its encapsulation are fabricated in the same PVD chamber.

Relationship between open-circuit voltage in Cu(In,Ga)Se2 solar cell and peak position of (220/204) preferred orientation near its absorber surface

NASA Astrophysics Data System (ADS)

Chantana, J.; Watanabe, T.; Teraji, S.; Kawamura, K.; Minemoto, T.

2013-11-01

Cu(In,Ga)Se2 (CIGS) absorbers with various Ga/III, Ga/(In+Ga), profiles are prepared by the so-called "multi-layer precursor method" using multi-layer co-evaporation of material sources. It is revealed that open-circuit voltage (VOC) of CIGS solar cell is primarily dependent on averaged Ga/III near the surface of its absorber. This averaged Ga/III is well predicted by peak position of (220/204) preferred orientation of CIGS film near its surface investigated by glancing-incidence X-ray diffraction with 0.1° incident angle. Finally, the peak position of (220/204) preferred orientation is proposed as a measure of VOC before solar cell fabrication.

Evaporation-Induced Assembly of Quantum Dots into Nanorings

PubMed Central

Chen, Jixin; Liao, Wei-Ssu; Chen, Xin; Yang, Tinglu; Wark, Stacey E.; Son, Dong Hee; Batteas, James D.; Cremer, Paul S.

2011-01-01

Herein, we demonstrate the controlled formation of two-dimensional periodic arrays of ring-shaped nanostructures assembled from CdSe semiconductor quantum dots (QDs). The patterns were fabricated by using an evaporative templating method. This involves the introduction of an aqueous solution containing both quantum dots and polystyrene microspheres onto the surface of a planar hydrophilic glass substrate. The quantum dots became confined to the meniscus of the microspheres during evaporation, which drove ring assembly via capillary forces at the polystyrene sphere/glass substrate interface. The geometric parameters for nanoring formation could be controlled by tuning the size of the microspheres and the concentration of the QDs employed. This allowed hexagonal arrays of nanorings to be formed with thicknesses ranging from single dot necklaces to thick multilayer structures over surface areas of many square millimeters. Moreover, the diameter of the ring structures could be simultaneously controlled. A simple model was employed to explain the forces involved in the formation of nanoparticle nanorings. PMID:19206264

Large-area soft x-ray projection lithography using multilayer mirrors structured by RIE

NASA Astrophysics Data System (ADS)

Rahn, Steffen; Kloidt, Andreas; Kleineberg, Ulf; Schmiedeskamp, Bernt; Kadel, Klaus; Schomburg, Werner K.; Hormes, F. J.; Heinzmann, Ulrich

1993-01-01

SXPL (soft X-ray projection lithography) is one of the most promising applications of X-ray reflecting optics using multilayer mirrors. Within our collaboration, such multilayer mirrors were fabricated, characterized, laterally structured and then used as reflection masks in a projecting lithography procedure. Mo/Si-multilayer mirrors were produced by electron beam evaporation in UHV under thermal treatment with an in-situ X-ray controlled thickness in the region of 2d equals 14 nm. The reflectivities measured at normal incidence reached up to 54%. Various surface analysis techniques have been applied in order to characterize and optimize the X-ray mirrors. The multilayers were patterned by reactive ion etching (RIE) with CF(subscript 4), using a photoresist as the etch mask, thus producing X-ray reflection masks. The masks were tested in the synchrotron radiation laboratory of the electron accelerator ELSA at the Physikalisches Institut of Bonn University. A double crystal X-ray monochromator was modified so as to allow about 0.5 cm(superscript 2) of the reflection mask to be illuminated by white synchrotron radiation. The reflected patterns were projected (with an energy of 100 eV) onto the resist (Hoechst AZ PF 514), which was mounted at an average distance of about 7 mm. In the first test-experiments, structure sizes down to 8 micrometers were nicely reproduced over the whole of the exposed area. Smaller structures were distorted by Fresnel-diffraction. The theoretically calculated diffraction images agree very well with the observed images.

Will New Metal Heads Restore Mechanical Integrity of Corroded Trunnions?

PubMed

Derasari, Aditya; Gold, Jonathan E; Ismaily, Sabir; Noble, Philip C; Incavo, Stephen J

2017-04-01

Metal wear and corrosion from modular junctions in total hip arthroplasty can lead to further unwanted surgery. Trunnion tribocorrosion is recognized as an important contributor to failure. This study was performed to determine if new metal heads restore mechanical integrity of the original modular junction after impaction on corroded trunnions, and assess which variables affect stability of the new interface created at revision total hip arthroplasty. Twenty-two trunnions, cobalt-chromium (CoCr) and titanium alloy (TiAIV), (CoCr, n = 12; TiAIV, n = 10) and new metal heads were used, 10 trunnions in pristine condition and 12 with corrosion damage. Test states were performed using an MTS Machine and included the following: 1, Assembly; 2, Disassembly; 3, Assembly; 4, Toggling; and 5, Disassembly. During loading, three-dimensional motion of the head-trunnion junction was measured using a custom jig. There were no statistical differences in the tested mechanical properties between corroded and pristine trunnions implanted with a new metal femoral head. Average micromotion of the head versus trunnion interface was greatest at the start of loading, stabilizing after approximately 50 loading cycles at an average of 30.6 ± 3.2 μm. Corrosion at the trunnion does not disrupt mechanical integrity of the junction when a CoCr head is replaced with a CoCr trunnion. However, increased interface motion of a new metal head on a corroded titanium trunnion requires additional study. The evaluation of ball head size on mechanical integrity of trunnions would also be a potential subject of future investigation, as increasing the ball head size at the time of revision is not uncommon in revisions today. Copyright © 2016 Elsevier Inc. All rights reserved.

Comparison and evaluation of marginal and internal gaps in cobalt-chromium alloy copings fabricated using subtractive and additive manufacturing.

PubMed

Kim, Dong-Yeon; Kim, Ji-Hwan; Kim, Hae-Young; Kim, Woong-Chul

2018-01-01

To evaluate the marginal and internal gaps of cobalt-chromium (Co-Cr) alloy copings fabricated using subtractive and additive manufacturing. A study model of an abutment tooth 46 was prepared by a 2-step silicone impression with dental stone. Fifteen stereolithography files for Co-Cr alloy copings were compiled using a model scanner and dental CAD software. Using the lost wax (LW), wax block (WB), soft metal block (SMB), microstereolithography (μ-SLA), and selected laser melting (SLM) techniques, 15 Co-Cr alloy copings were fabricated per group. The marginal and internal gaps of these Co-Cr alloy copings were measured using a digital microscope (160×), and the data obtained were analyzed using the non-parametric Kruskal-Wallis H-test and post-hoc Mann-Whitney U-test with Bonferroni correction. The mean values of the marginal, axial wall, and occlusal gaps were 91.8, 83.4, and 163μm in the LW group; 94.2, 77.5, and 122μm in the WB group; 60.0, 79.4, and 90.8μm in the SMB group; 154, 72.4, and 258μm in the μ-SLA group; and 239, 73.6, and 384μm in the SLM group, respectively. The differences in the marginal and occlusal gaps between the 5 groups were statistically significant (P<.05). The marginal gaps of the LW, WB, and SMB groups were within the clinically acceptable limit, but further improvements in the μ-SLA and SLM approaches may be required prior to clinical implementation. Copyright © 2017 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Implant-level prostheses in the edentulous maxilla: a comparison with conventional abutment-level prostheses after 5 years of use.

PubMed

Hjalmarsson, Lars; Smedberg, Jan-Ivan; Pettersson, Mattias; Jemt, Torsten

2011-01-01

Long-term comparisons of frameworks at the implant or abutment level are not available, and knowledge of the clinical function of cobalt-chromium (Co-Cr) alloy frameworks is limited. Primarily, the aim of this study was to compare the 5-year clinical performance of frameworks with or without abutment connections to implants. Secondly, the outcomes of prostheses made from Co-Cr alloy with porcelain veneers to those made of commercially pure titanium (CP Ti) with acrylic veneers were compared. The test groups comprised patients treated with screw-retained fixed prostheses made at the implant level according to the Cresco method in either dental porcelain-veneered Co-Cr alloy (n = 15) or acrylic-veneered CP Ti (n = 25). A control group of 40 randomly selected patients were provided with prostheses made at the standard abutment level in CP Ti with acrylic veneers. For all patients, clinical and radiologic 5-year data were retrospectively collected and evaluated. Five-year implant cumulative survival rates (CSRs) were 98.6% and 97.6% for test and control groups, respectively (P > .05). No major differences in bone level were demonstrated between the groups after 5 years (P > .05). Significantly more complications occurred in the test groups compared to the control group (P < .01), with the most common complications being mucositis and fracture of veneers. After 5 years, the clinical outcomes of implant-level prostheses made of porcelain-veneered Co-Cr or acrylic-veneered CP Ti seem comparable to acrylic-veneered titanium prostheses made at the standard abutment level regarding implant CSR and bone levels. However, more complications were registered in implant-level prostheses compared to the standard abutment-level prostheses.

Fixation strength of a polyetheretherketone femoral component in total knee arthroplasty.

PubMed

de Ruiter, Lennert; Janssen, Dennis; Briscoe, Adam; Verdonschot, Nico

2017-11-01

Introducing polyetheretherketone (PEEK) polymer as a material for femoral components in total knee arthroplasty (TKA) could potentially lead to a reduction of the cemented fixation strength. A PEEK implant is more likely to deform under high loads, rendering geometrical locking features less effective. Fixation strength may be enhanced by adding more undercuts or specific surface treatments. The aim of this study is to measure the initial fixation strength and investigate the associated failure patterns of three different iterations of PEEK-OPTIMA ® implants compared with a Cobalt-Chromium (CoCr) component. Femoral components were cemented onto trabecular bone analogue foam blocks and preconditioned with 86,400 cycles of compressive loading (2600 N-260 N at 1 Hz). They were then extracted while the force was measured and the initial failure mechanism was recorded. Four groups were compared: CoCr, regular PEEK, PEEK with an enhanced cement-bonding surface and the latter with additional surface primer. The mean pull-off forces for the four groups were 3814 N, 688 N, 2525 N and 2552 N, respectively. The initial failure patterns for groups 1, 3 and 4 were the same; posterior condylar foam fracture and cement-bone debonding. Implants from group 2 failed at the cement-implant interface. This study has shown that a PEEK-OPTIMA ® femoral TKA component with enhanced macro- and microtexture is able to replicate the main failure mechanism of a conventional CoCr femoral implant. The fixation strength is lower than for a CoCr implant, but substantially higher than loads occurring under in-vivo conditions. Copyright © 2017 IPEM. Published by Elsevier Ltd. All rights reserved.

[Effect of different porcelain-fused-to-metal crown inner metal materials on the level of soluble intercellular adhesion molecule-1 and interleukin-1beta in gingival crevicular fluid].

PubMed

Yuan, Tangxia; Zhang, Yanbiao; Wu, Zheng-Hua

2011-10-01

To investigate the effect of different inner metal materials of porcelain-fused-to-metal (PFM) crown on periodontal tissue by means of measuring the level of soluble intercellular adhesion molecule-1 (sICAM-1) and interleukin-1beta (IL-1beta) in gingival crevicular fluid (GCF) after PFM restorations. 30 teeth were divided into three groups (Ni-Cr alloy group, Co-Cr alloy group and Au-Pt alloy group, 10 teeth each group), and restored by Ni-Cr alloy, Co-Cr alloy and Au-Pt alloy PFM crown according grouping. At the point of pre-restoration, 6-month and 12-month after cementation, the clinical parameters including plaque index (PLI), gingival index (GI) and gingival crevice depth (GCD) were detected, and GCF was collected from labial and lingual of mesial site and distal site. The level of sICAM-1 and IL-1beta were detected. At the point of 6-month and 12-month after cementation, Ni-Cr alloy group showed significant difference for GI, GCD and all GCF indexes when compared to pre-restoration, Co-Cr alloy group and Au-Pt alloy group (P < 0.05). At the point of 12-month after cementation, Co-Cr alloy group showed significant difference for GI, GCD and all GCF indexes when compared to pre-restoration and Au-Pt alloy group (P < 0.05). All indexes have no significant difference for Au-Pt alloy group during the 12-month experiment times when compared to pre-restoration (P > 0.05). Non-noble metal has bad effect on the periodontal tissue.

Effects of chemical composition on the corrosion of dental alloys.

PubMed

Galo, Rodrigo; Ribeiro, Ricardo Faria; Rodrigues, Renata Cristina Silveira; Rocha, Luís Augusto; de Mattos, Maria da Glória Chiarello

2012-01-01

The aim of this study was to determine the effect of the oral environment on the corrosion of dental alloys with different compositions, using electrochemical methods. The corrosion rates were obtained from the current-potential curves and electrochemical impedance spectroscopy (EIS). The effect of artificial saliva on the corrosion of dental alloys was dependent on alloy composition. Dissolution of the ions occurred in all tested dental alloys and the results were strongly dependent on the general alloy composition. Regarding the alloys containing nickel, the Ni-Cr and Ni-Cr-Ti alloys released 0.62 mg/L of Ni on average, while the Co-Cr dental alloy released ions between 0.01 and 0.03 mg/L of Co and Cr, respectively.The open-circuit potential stabilized at a higher level with lower deviation (standard deviation: Ni-Cr-6Ti = 32 mV/SCE and Co-Cr = 54 mV/SCE). The potenciodynamic curves of the dental alloys showed that the Ni-based dental alloy with >70 wt% of Ni had a similar curve and the Co-Cr dental alloy showed a low current density and hence a high resistance to corrosion compared with the Ni-based dental alloys. Some changes in microstructure were observed and this fact influenced the corrosion behavior for the alloys. The lower corrosion resistance also led to greater release of nickel ions to the medium. The quantity of Co ions released from the Co-Cr-Mo alloy was relatively small in the solutions. In addition, the quantity of Cr ions released into the artificial saliva from the Co-Cr alloy was lower than Cr release from the Ni-based dental alloys.

The structure, surface topography and mechanical properties of Si-C-N films fabricated by RF and DC magnetron sputtering

NASA Astrophysics Data System (ADS)

Shi, Zhifeng; Wang, Yingjun; Du, Chang; Huang, Nan; Wang, Lin; Ning, Chengyun

2011-12-01

Silicon carbon nitride thin films were deposited on Co-Cr alloy under varying deposition conditions such as sputtering power and the partial pressure ratio of N2 to Ar by radio frequency and direct current magnetron sputtering techniques. The chemical bonding configurations, surface topography and hardness were characterized by means of X-ray photoelectron spectroscopy, atomic force microscopy and nano-indentation technique. The sputtering power exhibited important influence on the film composition, chemical bonding configurations and surface topography, the electro-negativity had primary effects on chemical bonding configurations at low sputtering power. A progressive densification of the film microstructure occurring with the carbon fraction was increased. The films prepared by RF magnetron sputtering, the relative content of the Si-N bond in the films increased with the sputtering power increased, and Si-C and Si-Si were easily detachable, and C-O, N-N and N-O on the film volatile by ion bombardment which takes place very frequently during the film formation process. With the increase of sputtering power, the films became smoother and with finer particle growth. The hardness varied between 6 GPa and 11.23 GPa depending on the partial pressure ratio of N2 to Ar. The tribological characterization of Co-Cr alloy with Si-C-N coating sliding against UHMWPE counter-surface in fetal bovine serum, shows that the wear resistance of the Si-C-N coated Co-Cr alloy/UHMWPE sliding pair show much favourable improvement over that of uncoated Co-Cr alloy/UHMWPE sliding pair. This study is important for the development of advanced coatings with tailored mechanical and tribological properties.

Comparison of fracture resistance between cast, CAD/CAM milling, and direct metal laser sintering metal post systems.

PubMed

Bilgin, Mehmet Selim; Erdem, Ali; Dilber, Erhan; Ersoy, İbrahim

2016-01-01

The purpose of this study was to compare the fracture resistance of Co-Cr post-cores fabricated with 3 different techniques: traditional casting (TC), computer-aided design and manufacturing (CAD/CAM) milling (CCM) and direct metal laser sintering (DMLS). Forty intact human mandibular premolar were endodontically treated. The roots were then randomly divided into four groups according to the post systems: the control group was only filled with gutta percha. Co-Cr metal posts were fabricated with TC, CCM and DMLS in the other three groups. The posts were luted with a resin cement and subjected to compression test at a crosshead speed of 1mm/min. The statistical analysis of the data was performed using one-way analysis of variance (ANOVA) and multiple comparison post hoc Tukey tests (α=.05). The samples were examined under a stereomicroscope with ×20 magnification for the evaluation of the fracture types. The mean fracture loads were 432.69 N for control, 608.89 N for TC, 689.40 N for DMLS and 959.26 N for CCM. One-way ANOVA revealed significant difference between the groups (p<0.01). In the post hoc Tukey test, there were significant differences between groups except DMLS and TC. While Co-Cr posts fabricated by TC and DMLS systems performed similarly in terms of fracture resistance, posts fabricated by CCM techniques showed higher fracture resistance values. Co-Cr metal posts fabricated by CCM and DMLS could be an alternative to TC processing in daily clinical application. Copyright © 2015 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Metal-ceramic bond strength between a feldspathic porcelain and a Co-Cr alloy fabricated with Direct Metal Laser Sintering technique

PubMed Central

Spyropoulos, Konstantinos

2018-01-01

PURPOSE The aim of the present study was to record the metal-ceramic bond strength of a feldspathic dental porcelain and a Co-Cr alloy, using the Direct Metal Laser Sintering technique (DMLS) for the fabrication of metal substrates. MATERIALS AND METHODS Ten metal substrates were fabricated with powder of a dental Co-Cr alloy using DMLS technique (test group) in dimensions according to ISO 9693. Another ten substrates were fabricated with a casing dental Co-Cr alloy using classic casting technique (control group) for comparison. Another three substrates were fabricated using each technique to record the Modulus of Elasticity (E) of the used alloys. All substrates were examined to record external and internal porosity. Feldspathic porcelain was applied on the substrates. Specimens were tested using the three-point bending test. The failure mode was determined using optical and scanning electron microscopy. The statistical analysis was performed using t-test. RESULTS Substrates prepared using DMLS technique did not show internal porosity as compared to those produced using the casting technique. The E of control and test group was 222 ± 5.13 GPa and 227 ± 3 GPa, respectively. The bond strength was 51.87 ± 7.50 MPa for test group and 54.60 ± 6.20 MPa for control group. No statistically significant differences between the two groups were recorded. The mode of failure was mainly cohesive for all specimens. CONCLUSION Specimens produced by the DMLS technique cover the lowest acceptable metal-ceramic bond strength of 25 MPa specified in ISO 9693 and present satisfactory bond strength for clinical use. PMID:29503711

A Comparison of the Marginal and Internal Fit of Cobalt- Chromium Copings Fabricated by Two Different CAD/CAM Systems (CAD/ Milling, CAD/ Ceramill Sintron).

PubMed

Vojdani, Mahroo; Torabi, Kianoosh; Atashkar, Berivan; Heidari, Hossein; Torabi Ardakani, Mahshid

2016-12-01

Marginal fitness is the most important criteria for evaluation of the clinical acceptability of a cast restoration. Marginal gap which is due to cement solubility and plaque retention is potentially detrimental to both tooth and periodontal tissues. This in vitro study aimed to evaluate the marginal and internal fit of cobalt- chromium (Co-Cr) copings fabricated by two different CAD/CAM systems: (CAD/ milling and CAD/ Ceramill Sintron). We prepared one machined standard stainless steel master model with following dimensions: 7 mm height, 5mm diameter, 90˚ shoulder marginal finish line with 1 mm width, 10˚ convergence angle and anti-rotational surface on the buccal aspect of the die. There were 10 copings produced from hard presintered Co-Cr blocks according to CAD/ Milling technique and ten copings from soft non- presintered Co-Cr blocks according to CAD/ Ceramill Sintron technique. Marginal and internal accuracies of copings were documented by the replica technique. Replicas were examined at ten reference points under a digital microscope (230X). The Student's t-test was used for statistical analysis. p < 0.001 was considered significant. Statistically significant differences existed between the groups ( p < 0.001). The CAD/milling group (hard copings) had a mean marginal discrepancy (MD) of 104 µm, axial discrepancy (AD) of 23 µm and occlusal discrepancy of 130 µm. For CAD/ Ceramill Sintron group, these values were 195 µm (MD), 46 µm (AD), and 232 µm (OD). Internal total discrepancy (ITD) for the CAD/milling group was 77 µm, whereas for the CAD/Ceramill Sintron group was 143 µm. Hard presintered Co-Cr copings had significantly higher marginal and internal accuracies compared to the soft non-presintered copings.

Role of SiO2 coating in multiferroic CoCr2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Kamran, M.; Ullah, Asmat; Mehmood, Y.; Nadeem, K.; Krenn, H.

2017-02-01

Effect of silica (SiO2) coating concentration on structural and magnetic properties of multiferroic cobalt chromite (CoCr2O4) nanoparticles have been studied. The nanoparticles with average crystallite size in the range 19 to 28 nm were synthesised by sol-gel method. X-ray diffraction (XRD) analysis has verified the composition of single-phase cubic normal spinel structure of CoCr2O4 nanoparticles. The average crystallite size and cell parameter decreased with increasing SiO2 concentration. TEM image revealed that the shape of nanoparticles was non-spherical. Zero field cooled/field cooled (ZFC/FC) curves revealed that nanoparticles underwent a transition from paramagnetic (PM) state to collinear short-range ferrimagnetic (FiM) state, and this PM-FiM transition temperature decreased from 101 to 95 K with increasing SiO2 concentration or decreasing crystallite size. A conical spin state at Ts = 27 K was also observed for all the samples which decreased with decreasing average crystallite size. Low temperature lock-in transition was also observed in these nanoparticles at 12 K for uncoated nanoparticles which slightly shifted towards low temperature with decreasing average crystallite size. Saturation magnetization (Ms) showed decreasing trend with increasing SiO2 concentration, which was due to decrease in average crystallite size of nanoparticles and enhanced surface disorder in smaller nanoparticles. The temperature dependent AC-susceptibility also showed the decrease in the transition temperature (Tc), broadening of the Tc peak and decrease in magnetization with increasing SiO2 concentration or decreasing average crystallite size. In summary, the concentration of SiO2 has significantly affected the structural and magnetic properties of CoCr2O4 nanoparticles.

Evaluation and comparison of the marginal adaptation of two different substructure materials.

PubMed

Karaman, Tahir; Ulku, Sabiha Zelal; Zengingul, Ali Ihsan; Guven, Sedat; Eratilla, Veysel; Sumer, Ebru

2015-06-01

In this study, we aimed to evaluate the amount of marginal gap with two different substructure materials using identical margin preparations. Twenty stainless steel models with a chamfer were prepared with a CNC device. Marginal gap measurements of the galvano copings on these stainless steel models and Co-Cr copings obtained by a laser-sintering method were made with a stereomicroscope device before and after the cementation process and surface properties were evaluated by scanning electron microscopy (SEM). A dependent t-test was used to compare the mean of the two groups for normally distributed data, and two-way variance analysis was used for more than two data sets. Pearson's correlation analysis was also performed to assess relationships between variables. According to the results obtained, the marginal gap in the galvano copings before cementation was measured as, on average, 24.47 ± 5.82 µm before and 35.11 ± 6.52 µm after cementation; in the laser-sintered Co-Cr structure, it was, on average, 60.45 ± 8.87 µm before and 69.33 ± 9.03 µm after cementation. A highly significant difference (P<.001) was found in marginal gap measurements of galvano copings and a significant difference (P<.05) was found in marginal gap measurements of the laser-sintered Co-Cr copings. According to the SEM examination, surface properties of laser sintered Co-Cr copings showed rougher structure than galvano copings. The galvano copings showed a very smooth surface. Marginal gaps values of both groups before and after cementation were within the clinically acceptable level. The smallest marginal gaps occurred with the use of galvano copings.

Evaluation and comparison of the marginal adaptation of two different substructure materials

PubMed Central

Karaman, Tahir; Ulku, Sabiha Zelal; Zengingul, Ali Ihsan; Eratilla, Veysel; Sumer, Ebru

2015-01-01

PURPOSE In this study, we aimed to evaluate the amount of marginal gap with two different substructure materials using identical margin preparations. MATERIALS AND METHODS Twenty stainless steel models with a chamfer were prepared with a CNC device. Marginal gap measurements of the galvano copings on these stainless steel models and Co-Cr copings obtained by a laser-sintering method were made with a stereomicroscope device before and after the cementation process and surface properties were evaluated by scanning electron microscopy (SEM). A dependent t-test was used to compare the mean of the two groups for normally distributed data, and two-way variance analysis was used for more than two data sets. Pearson's correlation analysis was also performed to assess relationships between variables. RESULTS According to the results obtained, the marginal gap in the galvano copings before cementation was measured as, on average, 24.47 ± 5.82 µm before and 35.11 ± 6.52 µm after cementation; in the laser-sintered Co-Cr structure, it was, on average, 60.45 ± 8.87 µm before and 69.33 ± 9.03 µm after cementation. A highly significant difference (P<.001) was found in marginal gap measurements of galvano copings and a significant difference (P<.05) was found in marginal gap measurements of the laser-sintered Co-Cr copings. According to the SEM examination, surface properties of laser sintered Co-Cr copings showed rougher structure than galvano copings. The galvano copings showed a very smooth surface. CONCLUSION Marginal gaps values of both groups before and after cementation were within the clinically acceptable level. The smallest marginal gaps occurred with the use of galvano copings. PMID:26140178

Oxidised zirconium versus cobalt alloy bearing surfaces in total knee arthroplasty: 3D laser scanning of retrieved polyethylene inserts.

PubMed

Anderson, F L; Koch, C N; Elpers, M E; Wright, T M; Haas, S B; Heyse, T J

2017-06-01

We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty. A total of 20 retrieved tibial inserts that had articulated with OxZr components were matched with 20 inserts from CoCr articulations for patient age, body mass index, length of implantation, and revision diagnosis. Changes in dimensions of the articular surfaces were compared with those of pristine inserts using laser scanning. The differences in volume between the retrieved and pristine surfaces of the two groups were calculated and compared. The loss of polyethylene volume was 122 mm 3 (standard deviation (sd) 87) in the OxZr group and 170 mm 3 (sd 96) in the CoCr group (p = 0.033). The volume loss in the OxZr group was also lower in the medial (72 mm 3 (sd 67) versus 92 mm 3 (sd 60); p = 0.096) and lateral (49 mm 3 (sd 36) versus 79 mm 3 (sd 61); p = 0.096) compartments separately, but these differences were not significant. Our results corroborate earlier findings from in vitro testing and visual retrieval analysis which suggest that polyethylene volume loss is lower with OxZr femoral components. Since both OxZr and CoCr are hard surfaces that would be expected to create comparable amounts of polyethylene creep, the differences in volume loss may reflect differences in the in vivo wear of these inserts. Cite this article: Bone Joint J 2017;99-B:793-8. ©2017 The British Editorial Society of Bone & Joint Surgery.

Large Metal Heads and Vitamin E Polyethylene Increase Frictional Torque in Total Hip Arthroplasty.

PubMed

Meneghini, R Michael; Lovro, Luke R; Wallace, Joseph M; Ziemba-Davis, Mary

2016-03-01

Trunnionosis has reemerged in modern total hip arthroplasty for reasons that remain unclear. Bearing frictional torque transmits forces to the modular head-neck interface, which may contribute to taper corrosion. The purpose of this study is to compare frictional torque of modern bearing couples in total hip arthroplasty. Mechanical testing based on in vivo loading conditions was used to measure frictional torque. All bearing couples were lubricated and tested at 1 Hz for more than 2000 cycles. The bearing couples tested included conventional, highly crosslinked (XLPE) and vitamin E polyethylene, CoCr, and ceramic femoral heads and dual-mobility bearings. Statistical analysis was performed using Student t test for single-variable and analysis of variance for multivariant analysis. P ≤ .05 was considered statistically significant. Large CoCr metal heads (≥36 mm) substantially increased frictional torque against XLPE liners (P = .01), a finding not observed in ceramic heads. Vitamin E polyethylene substantially increased frictional torque compared with XLPE in CoCr and ceramic heads (P = .001), whereas a difference between conventional and XLPE was not observed (P = .69) with the numbers available. Dual-mobility bearing with ceramic inner head demonstrated the lowest mean frictional torque of all bearing couples. In this simulated in vivo model, large-diameter CoCr femoral heads and vitamin E polyethylene liners are associated with increased frictional torque compared with smaller metal heads and XLPE, respectively. The increased frictional torque of vitamin E polyethylene and larger-diameter femoral heads should be considered and further studied, along with reported benefits of these modern bearing couples. Copyright © 2016 Elsevier Inc. All rights reserved.

Effects of Impression Material, Impression Tray Type, and Type of Partial Edentulism on the Fit of Cobalt-Chromium Partial Denture Frameworks on Initial Clinical Insertion: A Retrospective Clinical Evaluation.

PubMed

Baig, Mirza Rustum; Akbar, Jaber Hussain; Qudeimat, Muawia; Omar, Ridwaan

2018-02-15

To evaluate the effects of impression material, impression tray type, and type of partial edentulism (ie, Kennedy class) on the accuracy of fit of cobalt-chromium (Co-Cr) partial removable dental prostheses (PRDP) in terms of the number of fabricated frameworks required until the attainment of adequate fit. Electronic case documentations of 120 partially edentulous patients provided with Co-Cr PRDP treatment for one or both arches were examined. Statistical analyses of data were performed using analysis of variance and Tukey honest significant difference test to compare the relationships between the different factors and the number of frameworks that needed to be fabricated for each patient (α = .05). Statistical analysis of data derived from 143 records (69 maxillary and 74 mandibular) revealed no significant correlation between impression material, tray type, or Kennedy class and the number of construction attempts for the pooled or individual arch data (P ≥ .05). In PRDP treatment, alginate can be chosen as a first-choice material, and metal stock trays can be a preferred option for making final impressions to fabricate Co-Cr frameworks.

Biofilm Formation on Different Materials Used in Oral Rehabilitation.

PubMed

Souza, Júlio C M; Mota, Raquel R C; Sordi, Mariane B; Passoni, Bernardo B; Benfatti, Cesar A M; Magini, Ricardo S

2016-01-01

The aim of this study was to evaluate the density and the morphological aspects of biofilms adhered to different materials applied in oral rehabilitation supported by dental implants. Sixty samples were divided into four groups: feldspar-based porcelain, CoCr alloy, commercially pure titanium grade IV and yttria-stabilized zirconia. Human saliva was diluted into BHI supplemented with sucrose to grow biofilms for 24 or 48 h. After this period, biofilm was removed by 1% protease treatment and then analyzed by spectrophotometry (absorbance), colony forming unit method (CFU.cm-2) and field-emission guns scanning electron microscopy (FEG-SEM). The highest values of absorbance and CFU.cm-2 were recorded on biofilms grown on CoCr alloys when compared to the other test materials for 24 or 48 h. Also, FEG-SEM images showed a high biofilm density on CoCr. There were no significant differences in absorbance and CFU.cm-2 between biofilms grown on zirconia, porcelain and titanium (p<0.05). Microbiological assays associated with microscopic analyses detected a higher accumulation of oral biofilms on CoCr-based materials than that on titanium or zirconia that are used for prosthetic structures.

Scanning Electron Microscopy Analysis of the Adaptation of Single-Unit Screw-Retained Computer-Aided Design/Computer-Aided Manufacture Abutments After Mechanical Cycling.

PubMed

Markarian, Roberto Adrian; Galles, Deborah Pedroso; Gomes França, Fabiana Mantovani

To measure the microgap between dental implants and custom abutments fabricated using different computer-aided design/computer-aided manufacture (CAD/CAM) methods before and after mechanical cycling. CAD software (Dental System, 3Shape) was used to design a custom abutment for a single-unit, screw-retained crown compatible with a 4.1-mm external hexagon dental implant. The resulting stereolithography file was sent for manufacturing using four CAD/CAM methods (n = 40): milling and sintering of zirconium dioxide (ZO group), cobalt-chromium (Co-Cr) sintered via selective laser melting (SLM group), fully sintered machined Co-Cr alloy (MM group), and machined and sintered agglutinated Co-Cr alloy powder (AM group). Prefabricated titanium abutments (TI group) were used as controls. Each abutment was placed on a dental implant measuring 4.1× 11 mm (SA411, SIN) inserted into an aluminum block. Measurements were taken using scanning electron microscopy (SEM) (×4,000) on four regions of the implant-abutment interface (IAI) and at a relative distance of 90 degrees from each other. The specimens were mechanically aged (1 million cycles, 2 Hz, 100 N, 37°C) and the IAI width was measured again using the same approach. Data were analyzed using two-way analysis of variance, followed by the Tukey test. After mechanical cycling, the best adaptation results were obtained from the TI (2.29 ± 1.13 μm), AM (3.58 ± 1.80 μm), and MM (1.89 ± 0.98 μm) groups. A significantly worse adaptation outcome was observed for the SLM (18.40 ± 20.78 μm) and ZO (10.42 ± 0.80 μm) groups. Mechanical cycling had a marked effect only on the AM specimens, which significantly increased the microgap at the IAI. Custom abutments fabricated using fully sintered machined Co-Cr alloy and machined and sintered agglutinated Co-Cr alloy powder demonstrated the best adaptation results at the IAI, similar to those obtained with commercial prefabricated titanium abutments after mechanical cycling. The adaptation of custom abutments made by means of SLM or milling and sintering of zirconium dioxide were worse both before and after mechanical cycling.

Metal/Dielectric Multilayers for High Resolution Imaging

DTIC Science & Technology

2012-08-07

of a silicon waveguide coated by thin metal film. The proposed PWG structure consists of narrow silicon waveguide clad by gold film without top...where the waveguide thickness is 220nm and the lower oxide cladding is 2μm. The device consists of main waveguide (of waveguide width WSOI=450nm...evaporation, where 3nm thick titanium was used as adhesion layer before 40nm gold deposition took place. Finally, the samples were spun coated with

Monthly evaporation forecasting using artificial neural networks and support vector machines

NASA Astrophysics Data System (ADS)

Tezel, Gulay; Buyukyildiz, Meral

2016-04-01

Evaporation is one of the most important components of the hydrological cycle, but is relatively difficult to estimate, due to its complexity, as it can be influenced by numerous factors. Estimation of evaporation is important for the design of reservoirs, especially in arid and semi-arid areas. Artificial neural network methods and support vector machines (SVM) are frequently utilized to estimate evaporation and other hydrological variables. In this study, usability of artificial neural networks (ANNs) (multilayer perceptron (MLP) and radial basis function network (RBFN)) and ɛ-support vector regression (SVR) artificial intelligence methods was investigated to estimate monthly pan evaporation. For this aim, temperature, relative humidity, wind speed, and precipitation data for the period 1972 to 2005 from Beysehir meteorology station were used as input variables while pan evaporation values were used as output. The Romanenko and Meyer method was also considered for the comparison. The results were compared with observed class A pan evaporation data. In MLP method, four different training algorithms, gradient descent with momentum and adaptive learning rule backpropagation (GDX), Levenberg-Marquardt (LVM), scaled conjugate gradient (SCG), and resilient backpropagation (RBP), were used. Also, ɛ-SVR model was used as SVR model. The models were designed via 10-fold cross-validation (CV); algorithm performance was assessed via mean absolute error (MAE), root mean square error (RMSE), and coefficient of determination (R 2). According to the performance criteria, the ANN algorithms and ɛ-SVR had similar results. The ANNs and ɛ-SVR methods were found to perform better than the Romanenko and Meyer methods. Consequently, the best performance using the test data was obtained using SCG(4,2,2,1) with R 2 = 0.905.

Coordination-based gold nanoparticle layers.

PubMed

Wanunu, Meni; Popovitz-Biro, Ronit; Cohen, Hagai; Vaskevich, Alexander; Rubinstein, Israel

2005-06-29

Gold nanoparticle (NP) mono- and multilayers were constructed on gold surfaces using coordination chemistry. Hydrophilic Au NPs (6.4 nm average core diameter), capped with a monolayer of 6-mercaptohexanol, were modified by partial substitution of bishydroxamic acid disulfide ligand molecules into their capping layer. A monolayer of the ligand-modified Au NPs was assembled via coordination with Zr4+ ions onto a semitransparent Au substrate (15 nm Au, evaporated on silanized glass and annealed) precoated with a self-assembled monolayer of the bishydroxamate disulfide ligand. Layer-by-layer construction of NP multilayers was achieved by alternate binding of Zr4+ ions and ligand-modified NPs onto the first NP layer. Characterization by atomic force microscopy (AFM), ellipsometry, wettability, transmission UV-vis spectroscopy, and cross-sectional transmission electron microscopy showed regular growth of NP layers, with a similar NP density in successive layers and gradually increased roughness. The use of coordination chemistry enables convenient step-by-step assembly of different ligand-possessing components to obtain elaborate structures. This is demonstrated by introducing nanometer-scale vertical spacing between a NP layer and the gold surface, using a coordination-based organic multilayer. Electrical characterization of the NP films was carried out using conductive AFM, emphasizing the barrier properties of the organic spacer multilayer. The results exhibit the potential of coordination self-assembly in achieving highly controlled composite nanostructures comprising molecules, NPs, and other ligand-derivatized components.

Evaporation from a partially wet forest canopy

NASA Technical Reports Server (NTRS)

Hancock, N. H.; Sellers, P. J.; Crowther, J. M.

1983-01-01

The results of experimental studies of water storage in a Sitka-spruce canopy are presented and analyzed in terms of model simulations of evaporation. Wet-branch cantilever deflection was measured along with meteorological data on three days in August, 1976, to determine the relationship of canopy evaporation to wind speed and (hence) aerodynamic resistance. Two versions of a simple unilayer model of sensible and latent heat transport from a partially wet canopy were tested in the data analysis: model F1 forbids the exchange of heat between wet and dry foliage surfaces; model F2 assumes that this exchange is highly efficient. Model F1 is found to give results consistent with the rainfall-interception model of Rutter et al. (1971, 1975, 1977), but model F2 gives results which are more plausible and correspond to the multilayer simulations of Sellers and Lockwood (1981) and the experimental findings of Hancock and Crowther (1979). It is inferred that the role of eddy diffusivity for water vapor is enhanced relative to momentum transport, and that the similarity hypothesis used in conventional models may fail in the near vicinity of a forest canopy.

Deposition pattern and tracer particle motion of evaporating multi-component sessile droplets.

PubMed

Amjad, Muhammad; Yang, Yang; Raza, Ghulam; Gao, Hui; Zhang, Jun; Zhou, Leping; Du, Xiaoze; Wen, Dongsheng

2017-11-15

The understanding of near-wall motion, evaporation behavior and dry pattern of sessile nanofluid droplets is fundamental to a wide range of applications such as painting, spray drying, thin film coating, fuel injection and inkjet printing. However, a deep insight into the heat transfer, fluid flow, near-wall particle velocity and their effects on the resulting dry patterns is still much needed to take the full advantage of these nano-sized particles in the droplet. This work investigates the effect of direct absorptive silicon/silver (Si/Ag) hybrid nanofluids via two experiments. The first experiment identifies the motion of tracer particles near the triple line of a sessile nanofluid droplet on a super-hydrophilic substrate under ambient conditions by the multilayer nanoparticle image velocimetry (MnPIV) technique. The second experiment reveals the effect of light-sensitive Si/Ag composite nanoparticles on the droplet evaporation rate and subsequent drying patterns under different radiation intensities. The results show that the presence of nanoparticle in a very small proportion significantly affects the motion of tracer particles, leading to different drying patterns and evaporation rates, which can be very important for the applications such as spray coating and inkjet printing. Copyright © 2017 Elsevier Inc. All rights reserved.

TiO2 brookite nanostructured thin layer on magneto-optical surface plasmon resonance transductor for gas sensing applications

NASA Astrophysics Data System (ADS)

Manera, M. G.; Colombelli, A.; Rella, R.; Caricato, A.; Cozzoli, P. D.; Martino, M.; Vasanelli, L.

2012-09-01

The sensing performance comparisons presented in this work were carried out by exploiting a suitable magneto-plasmonic sensor in both the traditional surface plasmon resonance configuration and the innovative magneto-optic surface plasmon resonance one. The particular multilayer transducer was functionalized with TiO2 Brookite nanorods layers deposited by matrix assisted pulsed laser evaporation, and its sensing capabilities were monitored in a controlled atmosphere towards different concentrations of volatile organic compounds mixed in dry air.

Forecasting SPEI and SPI Drought Indices Using the Integrated Artificial Neural Networks

PubMed Central

Maca, Petr; Pech, Pavel

2016-01-01

The presented paper compares forecast of drought indices based on two different models of artificial neural networks. The first model is based on feedforward multilayer perceptron, sANN, and the second one is the integrated neural network model, hANN. The analyzed drought indices are the standardized precipitation index (SPI) and the standardized precipitation evaporation index (SPEI) and were derived for the period of 1948–2002 on two US catchments. The meteorological and hydrological data were obtained from MOPEX experiment. The training of both neural network models was made by the adaptive version of differential evolution, JADE. The comparison of models was based on six model performance measures. The results of drought indices forecast, explained by the values of four model performance indices, show that the integrated neural network model was superior to the feedforward multilayer perceptron with one hidden layer of neurons. PMID:26880875

Multilayer heterostructures and their manufacture

DOEpatents

Hammond, Scott R; Reese, Matthew; Rupert, Benjamin; Miedaner, Alexander; Curtis, Clavin; Olson, Dana; Ginley, David S

2015-11-04

A method of synthesizing multilayer heterostructures including an inorganic oxide layer residing on a solid substrate is described. Exemplary embodiments include producing an inorganic oxide layer on a solid substrate by a liquid coating process under relatively mild conditions. The relatively mild conditions include temperatures below 225.degree. C. and pressures above 9.4 mb. In an exemplary embodiment, a solution of diethyl aluminum ethoxide in anhydrous diglyme is applied to a flexible solid substrate by slot-die coating at ambient atmospheric pressure, and the diglyme removed by evaporation. An AlO.sub.x layer is formed by subjecting material remaining on the solid substrate to a relatively mild oven temperature of approximately 150.degree. C. The resulting AlO.sub.x layer exhibits relatively high light transmittance and relatively low vapor transmission rates for water. An exemplary embodiment of a flexible solid substrate is polyethylene napthalate (PEN). The PEN is not substantially adversely affected by exposure to 150.degree. C

Direct growth and patterning of multilayer graphene onto a targeted substrate without an external carbon source.

PubMed

Kang, Dongseok; Kim, Won-Jun; Lim, Jung Ah; Song, Yong-Won

2012-07-25

Using only a simple tube furnace, we demonstrate the synthesis of patterned graphene directly on a designed substrate without the need for an external carbon source. Carbon atoms are absorbed onto Ni evaporator sources as impurities, and incorporated into catalyst layers during the deposition. Heat treatment conditions were optimized so that the atoms diffused out along the grain boundaries to form nanocrystals at the catalyst-substrate interfaces. Graphene patterns were obtained under patterned catalysts, which restricted graphene formation to within patterned areas. The resultant multilayer graphene was characterized by Raman spectroscopy and transmission electron microscopy to verify the high crystallinity and two-dimensional nanomorphology. Finally, a metal-semiconductor diode with a catalyst-graphene contact structure were fabricated and characterized to assess the semiconducting properties of the graphene sheets with respect to the display of asymmetric current-voltage behavior.

Forecasting SPEI and SPI Drought Indices Using the Integrated Artificial Neural Networks.

PubMed

Maca, Petr; Pech, Pavel

2016-01-01

The presented paper compares forecast of drought indices based on two different models of artificial neural networks. The first model is based on feedforward multilayer perceptron, sANN, and the second one is the integrated neural network model, hANN. The analyzed drought indices are the standardized precipitation index (SPI) and the standardized precipitation evaporation index (SPEI) and were derived for the period of 1948-2002 on two US catchments. The meteorological and hydrological data were obtained from MOPEX experiment. The training of both neural network models was made by the adaptive version of differential evolution, JADE. The comparison of models was based on six model performance measures. The results of drought indices forecast, explained by the values of four model performance indices, show that the integrated neural network model was superior to the feedforward multilayer perceptron with one hidden layer of neurons.

The effect of moisture content within multilayer protective clothing on protection from radiation and steam.

PubMed

Su, Yun; Li, Jun; Song, Guowen

2018-06-01

The moisture from skin sweat and atmospheric water affects the thermal protective performance provided by multilayer protective clothing. Four levels of moisture content were selected to evaluate the impact of moisture on thermal protection under dry (thermal radiation) and wet (thermal radiation and low-pressure steam) heat exposure. Also, the role of moisture and its relationship with exposure time were analyzed based on skin heat flux and Henriques integral value. The addition of moisture to a fabric system was found to result in differences in second-degree and third-degree skin burn times. When moisture is added to a fabric system, it both acts as a thermal conductor to present a negative effect and provides a positive effect owing to thermal storage of water and evaporative heat loss. The positive or negative effects of moisture are mainly dependent on the thermal exposure time, the moisture content and the presence of hot steam.

Deposition and characterization of titania-silica optical multilayers by asymmetric bipolar pulsed dc sputtering of oxide targets

NASA Astrophysics Data System (ADS)

Sagdeo, P. R.; Shinde, D. D.; Misal, J. S.; Kamble, N. M.; Tokas, R. B.; Biswas, A.; Poswal, A. K.; Thakur, S.; Bhattacharyya, D.; Sahoo, N. K.; Sabharwal, S. C.

2010-02-01

Titania-silica (TiO2/SiO2) optical multilayer structures have been conventionally deposited by reactive sputtering of metallic targets. In order to overcome the problems of arcing, target poisoning and low deposition rates encountered there, the application of oxide targets was investigated in this work with asymmetric bipolar pulsed dc magnetron sputtering. In order to evaluate the usefulness of this deposition methodology, an electric field optimized Fabry Perot mirror for He-Cd laser (λ = 441.6 nm) spectroscopy was deposited and characterized. For comparison, this mirror was also deposited by the reactive electron beam (EB) evaporation technique. The mirrors developed by the two complementary techniques were investigated for their microstructural and optical reflection properties invoking atomic force microscopy, ellipsometry, grazing incidence reflectometry and spectrophotometry. From these measurements the layer geometry, optical constants, mass density, topography, surface and interface roughness and disorder parameters were evaluated. The microstructural properties and spectral functional characteristics of the pulsed dc sputtered multilayer mirror were found to be distinctively superior to the EB deposited mirror. The knowledge gathered during this study has been utilized to develop a 21-layer high-pass edge filter for radio photoluminescence dosimetry.

Q-factor control of multilayer micromembrane using PZT composite material

NASA Astrophysics Data System (ADS)

Čekas, Elingas; Janušas, Giedrius; Palevicius, Arvydas; Janušas, Tomas; Ciganas, Justas

2018-02-01

Cantilever and membrane based sensors, which are capable of providing accurate detection of target analytes have been always an important research topic of medical diagnostics, food testing, and environmental monitoring fields. Here, the mechanical detection is achieved by micro- and nano-scale cantilevers for stress sensing and mass sensing, or micro- and nano-scale plates or membranes. High sensitivity is a major issue for the active element and it could be achieved via increased Q-factor. The ability to control the Q factor expands the range of application of the device and allows to achieve more accurate results. The aim of this paper is to investigate the mechanical and electrical properties, as well as, the ability to control the Q factor of the membrane with PZT nanocomposite. This multilayered membrane was formatted using the n-type <100> silicon substrate by implementing the Low Pressure Chemical Vapor Deposition (LPCVD), photolithography by using photomask with defined dimensions, deep etching, and e-beam evaporation techniques. Dynamic and electrical characteristics of the membrane were numerically investigated using COMSOL Multiphysics software. The use of the multilayered membrane can range from simple monitoring of particles concentration in a closed environment to inspecting glucose levels in human fluids (blood, tears, sweat, etc.).

High-resolution TEM Studies of Carbon Nanotubes and Catalyst Nanoparticles Produced During CVD from Metal Multilayer Films

NASA Astrophysics Data System (ADS)

Howe, Jane Y.; Puretzky, Alex A.; Geohegan, David B.; Cui, Hongtao; Eres, Varela; Maria, Alex A.; Lowndes, Douglas H.

2003-03-01

The structure of single-wall and multiwall carbon nanotubes and associated metal catalyst nanoparticles produced during chemical vapor deposition from multilayered metal films deposited on Si and Mo substrates were studied by high-resolution TEM and EDS. Electron beam-evaporated metal multilayer films (e.g. Al-Fe-Mo, typically 11-50 nm total thickness) roughen upon heat treatment to form a variety of catalyst particle sizes suitable for carbon nanotube growth by chemical vapor deposition using acetylene, hydrogen, and argon flow gases. This study investigates these nanoparticles, the type of nanotubes grown, their wall, tip, and basal structures, as well as the associated amounts of amorphous carbon deposited on their walls in different temperature and pressure ranges. Mixtures of SWNT and MWNT are found even for low growth temperatures (650-700 C), while rapid growth of vertically-aligned multiwall nanotubes (VA-MWNTs) predominate in a narrow temperature range at a given pressure. Arrested growth experiments were performed to determine the time periods for SWNT vs. MWNT growth. The nature of the catalyst nanoparticles, their support structure, and insights on the mechanisms of growth will be discussed.

Quantitative evaluation of sputtering induced surface roughness and its influence on AES depth profiles of polycrystalline Ni/Cu multilayer thin films

NASA Astrophysics Data System (ADS)

Yan, X. L.; Coetsee, E.; Wang, J. Y.; Swart, H. C.; Terblans, J. J.

2017-07-01

The polycrystalline Ni/Cu multilayer thin films consisting of 8 alternating layers of Ni and Cu were deposited on a SiO2 substrate by means of electron beam evaporation in a high vacuum. Concentration-depth profiles of the as-deposited multilayered Ni/Cu thin films were determined with Auger electron spectroscopy (AES) in combination with Ar+ ion sputtering, under various bombardment conditions with the samples been stationary as well as rotating in some cases. The Mixing-Roughness-Information depth (MRI) model used for the fittings of the concentration-depth profiles accounts for the interface broadening of the experimental depth profiling. The interface broadening incorporates the effects of atomic mixing, surface roughness and information depth of the Auger electrons. The roughness values extracted from the MRI model fitting of the depth profiling data agrees well with those measured by atomic force microscopy (AFM). The ion sputtering induced surface roughness during the depth profiling was accordingly quantitatively evaluated from the fitted MRI parameters with sample rotation and stationary conditions. The depth resolutions of the AES depth profiles were derived directly from the values determined by the fitting parameters in the MRI model.

Temperature induced CuInSe2 nanocrystal formation in the Cu2Se-In3Se2 multilayer thin films

NASA Astrophysics Data System (ADS)

Mohan, A.; Rajesh, S.

2017-04-01

The paper deals with the impact of annealing on Cu2Se-In3Se2 multilayer structure and discusses the quantum confinements. Thermal evaporation technique was used to prepare multilayer films over the glass substrates. The films were annealed at different temperatures (150 °C-350 °C) under vacuum atmosphere. The XRD pattern reveals that the films exhibit (112) peaks with CuInSe2 Chalcopyrite structure and upon annealing crystallinity improved. The grain size comes around 13-19 nm. The optical band gap value was found to be 2.21 to 2.09 eV and band gap splitting was observed for higher annealing temperatures. The increase in the band gap is related to quantum confinement effect. SEM image shows nano crystals spread over the entire surface for higher annealing temperatures. Optical absorption and PL spectra shows the blue shift during annealing. The HR-TEM shows the particle size in the nano range and which confirms the CuInSe2 nanocrystal formation. AFM image shows the rough surface with homogenous grains for the as deposited films and smooth surface for annealed films.

Cobalt chromium alloy with immobilized BMP peptide for enhanced bone growth.

PubMed

Poh, Chye Khoon; Shi, Zhilong; Tan, Xiao Wei; Liang, Zhen Chang; Foo, Xue Mei; Tan, Hark Chuan; Neoh, Koon Gee; Wang, Wilson

2011-09-01

Cobalt chromium (CoCr) alloys are widely used in orthopedic practice, however, lack of integration into the bone for long-term survival often occurs, leading to implant failure. Revision surgery to address such a failure involves increased risks, complications, and costs. Advances to enhancement of bone-implant interactions would improve implant longevity and long-term results. Therefore, we investigated the effects of BMP peptide covalently grafted to CoCr alloy on osteogenesis. The BMP peptide was derived from the knuckle epitope of bone morphogenic protein-2 (BMP-2) and was conjugated via a cysteine amino acid at the N-terminus. X-ray photoelectron spectroscopy and o-phthaldialdehyde were used to verify successful grafting at various stages of surface functionalization. Surface topography was evaluated from the surface profile determined by atomic force microscopy. Osteoblastic cells (MC3T3-E1) were seeded on the substrates, and the effects of BMP peptide on osteogenic differentiation were evaluated by measuring alkaline phosphatase (ALP) activity and calcium mineral deposition. The functionalized surfaces showed a twofold increase in ALP activity after 2 weeks incubation and a fourfold increase in calcium content after 3 weeks incubation compared to the pristine substrate. These findings are potentially useful in the development of improved CoCr implants for use in orthopedic applications. Copyright © 2011 Orthopaedic Research Society.

Effect of oxidation heat treatment on the bond strength between a ceramic and cast and milled cobalt-chromium alloys.

PubMed

Li, Jieyin; Ye, Xiuhua; Li, Bohua; Liao, Juankun; Zhuang, Peilin; Ye, Jiantao

2015-08-01

There is a dearth of dental scientific literature on the effect of different oxidation heat treatments (OHTs) (as surface pretreatments) on the bonding performance of cast and milled cobalt-chromium (CoCr) alloys. The objective of this study was to evaluate the effect of different OHTs on the bond strength between a ceramic and cast and milled CoCr alloys. Cobalt-chromium metallic specimens were prepared using either a cast or a milled method. Specimens were subjected to four different OHT methods: without OHT; OHT under normal atmospheric pressure; OHT under vacuum; and OHT under vacuum followed by sandblasting. The metal-ceramic bond strength was evaluated using a three-point bending test according to ISO9693. Scanning electron microscopy and energy-dispersive spectroscopy were used to study the specimens' microstructure and elemental composition. The bond strength was not affected by the CoCr manufacturing method. Oxidation heat treatment performed under normal atmospheric pressure resulted in the highest bond strength. The concentration of oxygen on the alloy surfaces varied with the different pretreatment methods in the following order: OHT under normal atmospheric pressure > OHT under vacuum > without OHT ≈ OHT under vacuum followed by sandblasting. © 2015 Eur J Oral Sci.

A Comparison of the Marginal and Internal Fit of Cobalt- Chromium Copings Fabricated by Two Different CAD/CAM Systems (CAD/ Milling, CAD/ Ceramill Sintron)

PubMed Central

Vojdani, Mahroo; Torabi, Kianoosh; Atashkar, Berivan; Heidari, Hossein; Torabi Ardakani, Mahshid

2016-01-01

Statement of the Problem: Marginal fitness is the most important criteria for evaluation of the clinical acceptability of a cast restoration. Marginal gap which is due to cement solubility and plaque retention is potentially detrimental to both tooth and periodontal tissues. Purpose: This in vitro study aimed to evaluate the marginal and internal fit of cobalt- chromium (Co-Cr) copings fabricated by two different CAD/CAM systems: (CAD/ milling and CAD/ Ceramill Sintron). Materials and Method: We prepared one machined standard stainless steel master model with following dimensions: 7 mm height, 5mm diameter, 90˚ shoulder marginal finish line with 1 mm width, 10˚ convergence angle and anti-rotational surface on the buccal aspect of the die. There were 10 copings produced from hard presintered Co-Cr blocks according to CAD/ Milling technique and ten copings from soft non- presintered Co-Cr blocks according to CAD/ Ceramill Sintron technique. Marginal and internal accuracies of copings were documented by the replica technique. Replicas were examined at ten reference points under a digital microscope (230X). The Student's t-test was used for statistical analysis. p< 0.001 was considered significant. Results: Statistically significant differences existed between the groups (p< 0.001). The CAD/milling group (hard copings) had a mean marginal discrepancy (MD) of 104 µm, axial discrepancy (AD) of 23 µm and occlusal discrepancy of 130 µm. For CAD/ Ceramill Sintron group, these values were 195 µm (MD), 46 µm (AD), and 232 µm (OD). Internal total discrepancy (ITD) for the CAD/milling group was 77 µm, whereas for the CAD/Ceramill Sintron group was 143 µm. Conclusion: Hard presintered Co-Cr copings had significantly higher marginal and internal accuracies compared to the soft non-presintered copings. PMID:27942545

[Influence of cobalt-chromium alloy ceramics crown on aspartate transaminase and alkaline phosphatase of gingival crevicular fluid].

PubMed

Miao, Yu; Liu, Ling-Jun; Zhang, Xiao-Min; Li, Li

2010-12-01

The purpose of this article was to evaluate the influence of cobalt-chromium (Co-Cr) alloy as the material of inner crown on periodontal tissue through detecting the weight of diseased teeth and the concentration of aspartate transaminase (AST) and alkaline phosphatase (ALP) of the gingival crevicular fluid (GCF) after Co-Cr alloy ceramics repairing. In this study, thirty cases of clinical diseased teeth were chosen from thirty patients based on patients' consent. Each tooth conformed to the inclusion criteria. All of the thirty teeth were repaired with Co-Cr alloy ceramics according to the indications. Then GCF of each diseased tooth was collected and weighed at the time of the day before prosthesis, the first and third month after repairing respectively in order to detect the concentration of AST and ALP. Furthermore, comparative analysis for different periods was performed after the data statistics. To the weight of GCF and the concentration of AST after the respective comparison of three indexes which was of different periods, numerous of each index increased in accordance with the rule of preoperation, postoperative first month, and postoperative third month (P < 0.05). To the concentration of ALP at three time points, the compared results showed that the preoperative numerous was less than that of third month after operation and there was significant difference between them (P < 0.05). To the weight of GCF and the concentration of AST and ALP, after the respective comparison of three indexes which was the diseased teeth and the contralateral teeth with the same name in the periods of pre-operation, all the differences had no statistical significance (P > 0.05), but all the differences had statistical significance in the periods of postoperative third month (P < 0.05). During the next three months after operation, GCF weight, concentration of AST and ALP of diseased teeth was gradually increased after their Co-Cr alloy ceramics crown repairing. This increase is somewhat harmful to periodontal health.

Comparative study of two commercially pure titanium casting methods

PubMed Central

RODRIGUES, Renata Cristina Silveira; FARIA, Adriana Claudia Lapria; ORSI, Iara Augusta; de MATTOS, Maria da Gloria Chiarello; MACEDO, Ana Paula; RIBEIRO, Ricardo Faria

2010-01-01

The interest in using titanium to fabricate removable partial denture (RPD) frameworks has increased, but there are few studies evaluating the effects of casting methods on clasp behavior. Objective This study compared the occurrence of porosities and the retentive force of commercially pure titanium (CP Ti) and cobalt-chromium (Co-Cr) removable partial denture circumferential clasps cast by induction/centrifugation and plasma/vacuum-pressure. Material and Methods 72 frameworks were cast from CP Ti (n=36) and Co-Cr alloy (n=36; control group). For each material, 18 frameworks were casted by electromagnetic induction and injected by centrifugation, whereas the other 18 were casted by plasma and injected by vacuum-pressure. For each casting method, three subgroups (n=6) were formed: 0.25 mm, 0.50 mm, and 0.75 mm undercuts. The specimens were radiographed and subjected to an insertion/removal test simulating 5 years of framework use. Data were analyzed by ANOVA and Tukey's to compare materials and cast methods (α=0.05). Results Three of 18 specimens of the induction/centrifugation group and 9 of 18 specimens of plasma/vacuum-pressure cast presented porosities, but only 1 and 7 specimens, respectively, were rejected for simulation test. For Co-Cr alloy, no defects were found. Comparing the casting methods, statistically significant differences (p<0.05) were observed only for the Co-Cr alloy with 0.25 mm and 0.50 mm undercuts. Significant differences were found for the 0.25 mm and 0.75 mm undercuts dependent on the material used. For the 0.50 mm undercut, significant differences were found when the materials were induction casted. Conclusion Although both casting methods produced satisfactory CP Ti RPD frameworks, the occurrence of porosities was greater in the plasma/vacuum-pressure than in the induction/centrifugation method, the latter resulting in higher clasp rigidity, generating higher retention force values. PMID:21085805

Comparative analysis of different joining techniques to improve the passive fit of cobalt-chromium superstructures.

PubMed

Barbi, Francisco C L; Camarini, Edevaldo T; Silva, Rafael S; Endo, Eliana H; Pereira, Jefferson R

2012-12-01

The influence of different joining techniques on passive fit at the interface structure/abutment of cobalt-chromium (Co-Cr) superstructures has not yet been clearly established. The purpose of this study was to compare 3 different techniques of joining Co-Cr superstructures by measuring the resulting marginal misfit in a simulated prosthetic assembly. A specially designed metal model was used for casting, sectioning, joining, and measuring marginal misfit. Forty-five cast bar-type superstructures were fabricated in a Co-Cr alloy and randomly assigned by drawing lots to 3 groups (n=15) according to the joining method used: conventional gas-torch brazing (G-TB), laser welding (LW), and tungsten inert gas welding (TIG). Joined specimens were assembled onto abutment analogs in the metal model with the 1-screw method. The resulting marginal misfit was measured with scanning electron microscopy (SEM) at 3 different points: distal (D), central (C), and mesial (M) along the buccal aspect of both abutments: A (tightened) and B (without screw). The Levene test was used to evaluate variance homogeneity and then the Welsch ANOVA for heteroscedastic data (α=.05). Significant differences were found on abutment A between groups G-TB and LW (P=.013) measured mesially and between groups G-TB and TIG (P=.037) measured centrally. On abutment B, significant differences were found between groups G-TB and LW (P<.001) and groups LW and TIG (P<.001) measured mesially; groups G-TB and TIG (P=.007) measured distally; and groups G-TB and TIG (P=.001) and LW and TIG (P=.007) measured centrally. The method used for joining Co-Cr prosthetic structures had an influence on the level of resulting passive fit. Structures joined by the tungsten inert gas method produced better mean results than did the brazing or laser method. Copyright © 2012 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Rod stiffness as a risk factor of proximal junctional kyphosis after adult spinal deformity surgery: comparative study between cobalt chrome multiple-rod constructs and titanium alloy two-rod constructs.

PubMed

Han, Sanghyun; Hyun, Seung-Jae; Kim, Ki-Jeong; Jahng, Tae-Ahn; Lee, Subum; Rhim, Seung-Chul

2017-07-01

Little is known about the effect of rod stiffness as a risk factor of proximal junctional kyphosis (PJK) after adult spinal deformity (ASD) surgery. The aim of this study was to compare radiographic outcomes after the use of cobalt chrome multiple-rod constructs (CoCr MRCs) and titanium alloy two-rod constructs (Ti TRCs) for ASD surgery with a minimum 1-year follow-up. Retrospective case-control study in two institutes. We included 54 patients who underwent ASD surgery with fusion to the sacrum in two academic institutes between 2002 and 2015. Radiographic outcomes were measured on the standing lateral radiographs before surgery, 1 month postoperatively, and at ultimate follow-up. The outcome measures were composed of pre- and postoperative sagittal vertical axis (SVA), pre- and postoperative lumbar lordosis (LL), pre- and postoperative thoracic kyphosis (TK)+LL+pelvic incidence (PI), pre- and postoperative PI minus LL, level of uppermost instrumented vertebra (UIV), evaluation of fusion after surgery, the presence of PJK, and the occurrence of rod fracture. We reviewed the medical records of 54 patients who underwent ASD surgery. Of these, 20 patients had CoCr MRC and 34 patients had Ti TRC. Baseline data and radiographic measurements were compared between the two groups. The Mann-Whitney U test, the chi-square test, and the Fisher exact test were used to compare outcomes between the groups. The patients of the groups were similar in terms of age, gender, diagnosis, number of three-column osteotomy, levels fused, bone mineral density, preoperative TK, pre- and postoperative TK+LL+PI, SVA difference, LL change, pre- and postoperative PI minus LL, and location of UIV (upper or lower thoracic level). However, there were significant differences in the occurrence of PJK and rod breakage (PJK: CoCr MRC: 12 [60%] vs. Ti TRC: 9 [26.5%], p=.015; occurrence of rod breakage: CoCr MRC: 0 [0%] vs. Ti TRC: 11 [32.4%], p=.004). The time of PJK was less than 12 months after surgery in the CoCr MRC group. However, 55.5% (5/9) of PJK developed over 12 months after surgery in the Ti TRC group. Increasing the rod stiffness by the use of cobalt chrome rod and can prevent rod breakage but adversely affects the occurrence and the time of PJK. Copyright © 2017 Elsevier Inc. All rights reserved.

Pretreatment method for immunoassay of polychlorinated biphenyls in transformer oil using multilayer capillary column and microfluidic liquid-liquid partitioning.

PubMed

Aota, Arata; Date, Yasumoto; Terakado, Shingo; Ohmura, Naoya

2013-01-01

Polychlorinated biphenyls (PCBs) are persistent organic pollutants that are present in the insulating oil inside a large number of transformers. To aid in eliminating PCB-contaminated transformers, PCBs in oil need to be measured using a rapid and cost-effective analytical method. We previously reported a pretreatment method for the immunoassay of PCBs in oil using a large-scale multilayer column and a microchip with multiple microrecesses, which permitted concentrated solvent extraction. In this paper, we report on a more rapid and facile pretreatment method, without an evaporation process, by improving the column and the microchip. In a miniaturized column, the decomposition and separation of oil were completed in 2 min. PCBs can be eluted from the capillary column at concentrations seven-times higher than those from the previous column. The total volume of the microrecesses was increased by improving the microrecess structure, the enabling extraction of four-times the amount of PCBs achieved with the previous system. By interfacing the capillary column with the improved microchip, PCBs in the eluate from the column were extracted into dimethyl sulfoxide in microrecesses with high enrichment and without the need for evaporation. Pretreatment was completed within 20 min. The pretreated oil was analyzed using a flow-based kinetic exclusion immunoassay. The limit of detection of PCBs in oil was 0.15 mg kg(-1), which satisfies the criterion set in Japan of 0.5 mg kg(-1).

The formation of α-phase SnS nanostructure from a hybrid, multi-layered S/Sn/S/Sn/S thin films: Phase stability, surface morphology and optical studies

NASA Astrophysics Data System (ADS)

Baby, Benjamin Hudson; Bharathi Mohan, D.

2017-11-01

Single phase of SnS thin film was fabricated from S/Sn/S/Sn/S multilayer prepared by using atmospheric pressure and vacuum thermal evaporation methods Glancing angle high vacuum thermal evaporation technique was employed to grow Sn nanorods which facilitated the sulphur diffusion in a faster manner to prepare SnS nanoparticles. The sulphur deposition temperature, sulphur deposition time and tin deposition time were successfully tailored in the synthesis process and stabilized α-phase SnS by probing through confocal micro-Raman spectrometer. X-ray diffraction confirms the formation of SnS crystal structure at sulphur deposition temperature 200 °C. The mechanism of formation of highly porous SnS phase with flower like morphology is explained from the morphological analysis of post deposition annealed film. The complete absence of any oxidation state as evident from Raman as well as EDAX analysis confirms that the proposed sulphurization method could be a suitable, simple and cheap technique for the successful sulphurization of metal films. Band gap calculation from Tauc plot showed a direct band gap value of 1.5 eV for films with single phase of SnS which can be used as a p-type absorber layer in thin film solar cells. Emission studies showed the energy transitions attributed to band edge transition and due to the presence of intrinsic defects.

Theoretical and experimental validation study on automotive air-conditioning based on heat pipe and LNG cold energy for LNG-fueled heavy vehicles

NASA Astrophysics Data System (ADS)

Deng, Dong; Cheng, Jiang-ping; Zhang, Sheng-chang; Ge, Fang-gen

2017-08-01

As a clean fuel, LNG has been used in heavy vehicles widely in China. Before reaching the engine for combustion, LNG store in a high vacuum multi-layer thermal insulation tank and need to be evaporated from its cryogenic state to natural gas. During the evaporation, the available cold energy of LNG has been calculated. The concept has been proposed that the separated type heat pipe technology is employed to utilize the available cold energy for automotive air-conditioning. The experiment has been conducted to validate the proposal. It is found that it is feasible to use the separated type heat pipe to convey the cold energy from LNG to automotive air-conditioning. And the cooling capacity of the automotive air-conditioning increase with the LNG consumption and air flow rate increasing.

Seasonal groundwater contribution to crop-water use assessed with lysimeter observations and model simulations

USGS Publications Warehouse

Luo, Y.; Sophocleous, M.

2010-01-01

Groundwater evaporation can play an important role in crop-water use where the water table is shallow. Lysimeters are often used to quantify the groundwater evaporation contribution influenced by a broad range of environmental factors. However, it is difficult for such field facilities, which are operated under limited conditions within limited time, to capture the whole spectrum of capillary upflow with regard to the inter-seasonal variability of climate, especially rainfall. Therefore, in this work, the method of combining lysimeter and numerical experiments was implemented to investigate seasonal groundwater contribution to crop-water use. Groundwater evaporation experiments were conducted through a weighing lysimeter at an agricultural experiment station located within an irrigation district in the lower Yellow River Basin for two winter wheat growth seasons. A HYDRUS-1D model was first calibrated and validated with weighing lysimeter data, and then was employed to perform scenario simulations of groundwater evaporation under different depths to water table (DTW) and water input (rainfall plus irrigation) driven by long term meteorological data. The scenario simulations revealed that the seasonally averaged groundwater evaporation amount was linearly correlated to water input for different values of DTW. The linear regression could explain more than 70% of the variability. The seasonally averaged ratio of the groundwater contribution to crop-water use varied with the seasonal water input and DTW. The ratio reached as high as 75% in the case of DTW=1.0. m and no irrigation, and as low as 3% in the case of DTW=3.0. m and three irrigation applications. The results also revealed that the ratio of seasonal groundwater evaporation to potential evapotranspiration could be fitted to an exponential function of the DTW that may be applied to estimate seasonal groundwater evaporation. In this case study of multilayered soil profile, the depth at which groundwater may evaporate at potential rate was 0.60-0.65. m, and the extinction depth of groundwater evaporation was approximately 3.8. m. ?? 2010 Elsevier B.V.

Simulation of tibial counterface wear in mobile bearing knees with uncoated and ADLC coated surfaces.

PubMed

Jones, V C; Barton, D C; Auger, D D; Hardaker, C; Stone, M H; Fisher, J

2001-01-01

A multidirectional pin-on-plate reciprocating machine was used to compare the wear performance of UHMWPE sliding against cast cobalt chrome (CoCr) plates that were either untreated or coated with Amorphous Diamond Like Carbon (ADLC). The test conditions were based on a 1/5 scale model representative of in vivo motion at the tibial counterfaces of unconstrained mobile bearing knees. The average +/- STERR wear rates were 13.78+/-1.06 mm3/Mcycles for the ADLC counterfaces and 0.504+/-0.12 mm3/Mcycles for the control CoCr counterfaces. All of the pins run on the ADLC counterfaces exhibited the same patterns of blistering along the central axis, and severe abrasion elsewhere to the extent that all of the original machining marks were removed after just one week of testing. The average value of friction coefficient was 0.24 for the ADLC counterfaces and 0.073 for the control CoCr counterfaces. The factor of 3.5 increase was statistically significant at p < 0.05. In the tribological evaluation of ADLC coatings for tibial trays in mobile bearing knees, this study shows that this specific Physical Vapour Deposition (PVD) ADLC showed significantly poorer frictional and wear performance than uncoated surfaces which was sufficient to negate any potential benefits of improved resistance to third body damage.

Marginal Accuracy and Internal Fit of 3-D Printing Laser-Sintered Co-Cr Alloy Copings.

PubMed

Kim, Myung-Joo; Choi, Yun-Jung; Kim, Seong-Kyun; Heo, Seong-Joo; Koak, Jai-Young

2017-01-23

Laser sintered technology has been introduced for clinical use and can be utilized more widely, accompanied by the digitalization of dentistry and the development of direct oral scanning devices. This study was performed with the aim of comparing the marginal accuracy and internal fit of Co-Cr alloy copings fabricated by casting, CAD/CAM (Computer-aided design/Computer-assisted manufacture) milled, and 3-D laser sintered techniques. A total of 36 Co-Cr alloy crown-copings were fabricated from an implant abutment. The marginal and internal fit were evaluated by measuring the weight of the silicone material, the vertical marginal discrepancy using a microscope, and the internal gap in the sectioned specimens. The data were statistically analyzed by One-way ANOVA (analysis of variance), a Scheffe's test, and Pearson's correlation at the significance level of p = 0.05, using statistics software. The silicone weight was significantly low in the casting group. The 3-D laser sintered group showed the highest vertical discrepancy, and marginal-, occlusal-, and average- internal gaps ( p < 0.05). The CAD/CAM milled group revealed a significantly high axial internal gap. There are moderate correlations between the vertical marginal discrepancy and the internal gap variables ( r = 0.654), except for the silicone weight. In this study, the 3-D laser sintered group achieved clinically acceptable marginal accuracy and internal fit.

Marginal Accuracy and Internal Fit of 3-D Printing Laser-Sintered Co-Cr Alloy Copings

PubMed Central

Kim, Myung-Joo; Choi, Yun-Jung; Kim, Seong-Kyun; Heo, Seong-Joo; Koak, Jai-Young

2017-01-01

Laser sintered technology has been introduced for clinical use and can be utilized more widely, accompanied by the digitalization of dentistry and the development of direct oral scanning devices. This study was performed with the aim of comparing the marginal accuracy and internal fit of Co-Cr alloy copings fabricated by casting, CAD/CAM (Computer-aided design/Computer-assisted manufacture) milled, and 3-D laser sintered techniques. A total of 36 Co-Cr alloy crown-copings were fabricated from an implant abutment. The marginal and internal fit were evaluated by measuring the weight of the silicone material, the vertical marginal discrepancy using a microscope, and the internal gap in the sectioned specimens. The data were statistically analyzed by One-way ANOVA (analysis of variance), a Scheffe’s test, and Pearson’s correlation at the significance level of p = 0.05, using statistics software. The silicone weight was significantly low in the casting group. The 3-D laser sintered group showed the highest vertical discrepancy, and marginal-, occlusal-, and average- internal gaps (p < 0.05). The CAD/CAM milled group revealed a significantly high axial internal gap. There are moderate correlations between the vertical marginal discrepancy and the internal gap variables (r = 0.654), except for the silicone weight. In this study, the 3-D laser sintered group achieved clinically acceptable marginal accuracy and internal fit. PMID:28772451

Induction heating pure vapor source of high temperature melting point materials on electron cyclotron resonance ion source.

PubMed

Kutsumi, Osamu; Kato, Yushi; Matsui, Yuuki; Kitagawa, Atsushi; Muramatsu, Masayuki; Uchida, Takashi; Yoshida, Yoshikazu; Sato, Fuminobu; Iida, Toshiyuki

2010-02-01

Multicharged ions that are needed are produced from solid pure material with high melting point in an electron cyclotron resonance ion source. We develop an evaporator by using induction heating (IH) with multilayer induction coil, which is made from bare molybdenum or tungsten wire without water cooling and surrounding the pure vaporized material. We optimize the shapes of induction coil and vaporized materials and operation of rf power supply. We conduct experiment to investigate the reproducibility and stability in the operation and heating efficiency. IH evaporator produces pure material vapor because materials directly heated by eddy currents have no contact with insulated materials, which are usually impurity gas sources. The power and the frequency of the induction currents range from 100 to 900 W and from 48 to 23 kHz, respectively. The working pressure is about 10(-4)-10(-3) Pa. We measure the temperature of the vaporized materials with different shapes, and compare them with the result of modeling. We estimate the efficiency of the IH vapor source. We are aiming at the evaporator's higher melting point material than that of iron.

Induction heating pure vapor source of high temperature melting point materials on electron cyclotron resonance ion sourcea)

NASA Astrophysics Data System (ADS)

Kutsumi, Osamu; Kato, Yushi; Matsui, Yuuki; Kitagawa, Atsushi; Muramatsu, Masayuki; Uchida, Takashi; Yoshida, Yoshikazu; Sato, Fuminobu; Iida, Toshiyuki

2010-02-01

Multicharged ions that are needed are produced from solid pure material with high melting point in an electron cyclotron resonance ion source. We develop an evaporator by using induction heating (IH) with multilayer induction coil, which is made from bare molybdenum or tungsten wire without water cooling and surrounding the pure vaporized material. We optimize the shapes of induction coil and vaporized materials and operation of rf power supply. We conduct experiment to investigate the reproducibility and stability in the operation and heating efficiency. IH evaporator produces pure material vapor because materials directly heated by eddy currents have no contact with insulated materials, which are usually impurity gas sources. The power and the frequency of the induction currents range from 100to900W and from 48to23kHz, respectively. The working pressure is about 10-4-10-3Pa. We measure the temperature of the vaporized materials with different shapes, and compare them with the result of modeling. We estimate the efficiency of the IH vapor source. We are aiming at the evaporator's higher melting point material than that of iron.

Spreading of a liquid film on a substrate by the evaporation-adsorption process

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wayner, P.C. Jr.; Schonberg, J.

1992-09-01

The importance of evaporation followed by multilayer adsorption in comparison to liquid flow at the leading edge of a volatile spreading film is analyzed. Presuming that both flows are functions of the same chemical potential gradient, a dimensionless group (N) which delineates the relative importance of vapor diffusion flow to viscous flow on the surface is obtained: N = [rho][sub i]D[nu]x/([minus][bar A][pi]). The relative importance of vapor flow increases with the vapor-pressure dependent partial density, [rho][sub i], and diffusivity, D, of the diffusing vapor, the kinematic viscosity of the liquid, [nu], and the distance downstream from the bulk liquid region,more » x, and decreases with the Hamaker constant, 6[pi][bar A]. Using physical properties the modifiers volatile'' and nonvolatile'' can thereby be put in perspective. Changes in the interfacial force field are a function of [bar A]. The spreading velocity due to the vapor diffusion process is obtained and is found to decrease with a decrease in the interfacial force field and the bulk vapor pressure. The infinite stress at the contact line can be easily relieved by evaporation-adsorption in many systems.« less

Evaluation of fit of cement-retained implant-supported 3-unit structures fabricated with direct metal laser sintering and vacuum casting techniques.

PubMed

Oyagüe, Raquel Castillo; Sánchez-Turrión, Andrés; López-Lozano, José Francisco; Montero, Javier; Albaladejo, Alberto; Suárez-García, María Jesús

2012-07-01

This study evaluated the vertical discrepancy of implant-fixed 3-unit structures. Frameworks were constructed with laser-sintered Co-Cr, and vacuum-cast Co-Cr, Ni-Cr-Ti, and Pd-Au. Samples of each alloy group were randomly luted in standard fashion using resin-modified glass-ionomer, self-adhesive, and acrylic/urethane-based cements (n = 12 each). Discrepancies were SEM analyzed. Three-way ANOVA and Student-Newman-Keuls tests were run (P < 0.05). Laser-sintered structures achieved the best fit per cement tested. Within each alloy group, resin-modified glass-ionomer and acrylic/urethane-based cements produced comparably lower discrepancies than the self-adhesive agent. The abutment position did not yield significant differences. All misfit values could be considered clinically acceptable.

Metal oxide multilayer hard mask system for 3D nanofabrication

NASA Astrophysics Data System (ADS)

Han, Zhongmei; Salmi, Emma; Vehkamäki, Marko; Leskelä, Markku; Ritala, Mikko

2018-02-01

We demonstrate the preparation and exploitation of multilayer metal oxide hard masks for lithography and 3D nanofabrication. Atomic layer deposition (ALD) and focused ion beam (FIB) technologies are applied for mask deposition and mask patterning, respectively. A combination of ALD and FIB was used and a patterning procedure was developed to avoid the ion beam defects commonly met when using FIB alone for microfabrication. ALD grown Al2O3/Ta2O5/Al2O3 thin film stacks were FIB milled with 30 keV gallium ions and chemically etched in 5% tetramethylammonium hydroxide at 50 °C. With metal evaporation, multilayers consisting of amorphous oxides Al2O3 and Ta2O5 can be tailored for use in 2D lift-off processing, in preparation of embedded sub-100 nm metal lines and for multilevel electrical contacts. Good pattern transfer was achieved by lift-off process from the 2D hard mask for micro- and nano-scaled fabrication. As a demonstration of the applicability of this method to 3D structures, self-supporting 3D Ta2O5 masks were made from a film stack on gold particles. Finally, thin film resistors were fabricated by utilizing controlled stiction of suspended Ta2O5 structures.

Coherency strain engineered decomposition of unstable multilayer alloys for improved thermal stability

NASA Astrophysics Data System (ADS)

Forsén, R.; Ghafoor, N.; Odén, M.

2013-12-01

A concept to improve hardness and thermal stability of unstable multilayer alloys is presented based on control of the coherency strain such that the driving force for decomposition is favorably altered. Cathodic arc evaporated cubic TiCrAlN/Ti1-xCrxN multilayer coatings are used as demonstrators. Upon annealing, the coatings undergo spinodal decomposition into nanometer-sized coherent Ti- and Al-rich cubic domains which is affected by the coherency strain. In addition, the growth of the domains is restricted by the surrounding TiCrN layer compared to a non-layered TiCrAlN coating which together results in an improved thermal stability of the cubic structure. A significant hardness increase is seen during decomposition for the case with high coherency strain while a low coherency strain results in a hardness decrease for high annealing temperatures. The metal diffusion paths during the domain coarsening are affected by strain which in turn is controlled by the Cr-content (x) in the Ti1-xCrxN layers. For x = 0 the diffusion occurs both parallel and perpendicular to the growth direction but for x > =0.9 the diffusion occurs predominantly parallel to the growth direction. Altogether this study shows a structural tool to alter and fine-tune high temperature properties of multicomponent materials.

Ageing under mechanical stress: first experiments for a silver based multilayer mirror

NASA Astrophysics Data System (ADS)

Lalo, Arnaud; Ravel, Guillaume; Ignat, Michel; Cousin, Bernard; Swain, Michael V.

2017-11-01

Improving materials and devices reliability is a major concern to the spatial industry. Results are reported for satellite mirrors-like specimens consisting in oxide-protected metal systems. Optical coatings were deposited by electron beam evaporation. Mechanical stress fields in multi-layered materials play an important role. The stress state can have far-reaching implications both in kinetics and thermodynamics. Therefore an integrated apparatus with four-point bending equipment was designed. The technique allowed us to exert stress into a film or a system of films on a substrate concurrently with thermal treatment. In order to achieve the first tests performed with the help of the apparatus, various preliminary characterizations were required. The article reports the preliminary micro-mechanical testing of the materials (ultra micro-indentation to evaluate the elastic modulus of the samples materials and wafer curvature technique to determine the specimen residual stress) and the first ageing experiment. Experimental evidence of accelerated ageing under stress is successfully reported.

An investigation of Au/Ti multilayer thin-films: surface morphology, structure and interfacial/surface migration of constituents under applied thermal stress

NASA Astrophysics Data System (ADS)

Senevirathne, Indrajith; Kemble, Eric; Lavoie, John

2014-03-01

Multilayer thin films are ubiquitous in industry. Au/Ti/substrate is unique due to possible biological applications in proof of concept devices. Material used for substrates include borosilicate glass, and quartz. Typical Ti depositions on substrates give rise to Stanski-Krastonov (SK) like growth while Frank-van der Merwe (FM) like growth is preferred. Ti films with thickness of ~ 100nm were deposited onto varying substrates using a thermal evaporator. The additional Au layer is then deposited via magnetron sputter deposition at 100mtorr at low deposition rates (~ 1ML/min) onto the Ti thin film. These systems were annealed at varying temperatures and at different durations. Systems were investigated via AFM (Atomic Force Microscopy) probes to examine the surface morphology, and structure. Further, the ambient contamination and elemental distribution/diffusion at annealing was investigated via Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray spectroscopy (EDX). PASSHE FPDC Annual Grant (LOU # 2010-LHU-03)

Climate warming due to increasing atmospheric CO2 - Simulations with a multilayer coupled atmosphere-ocean seasonal energy balance model

NASA Technical Reports Server (NTRS)

Li, Peng; Chou, Ming-Dah; Arking, Albert

1987-01-01

The transient response of the climate to increasing CO2 is studied using a modified version of the multilayer energy balance model of Peng et al. (1982). The main characteristics of the model are described. Latitudinal and seasonal distributions of planetary albedo, latitude-time distributions of zonal mean temperatures, and latitudinal distributions of evaporation, water vapor transport, and snow cover generated from the model and derived from actual observations are analyzed and compared. It is observed that in response to an atmospheric doubling of CO2, the model reaches within 1/e of the equilibrium response of global mean surface temperature in 9-35 years for the probable range of vertical heat diffusivity in the ocean. For CO2 increases projected by the National Research Council (1983), the model's transient response in annually and globally averaged surface temperatures is 60-75 percent of the corresponding equilibrium response, and the disequilibrium increases with increasing heat diffusivity of the ocean.

Organic heterostructures deposited by MAPLE on AZO substrate

NASA Astrophysics Data System (ADS)

Socol, M.; Preda, N.; Stanculescu, A.; Breazu, C.; Florica, C.; Stanculescu, F.; Iftimie, S.; Girtan, M.; Popescu-Pelin, G.; Socol, G.

2017-09-01

Organic heterostructures based on poly(3-hexylthiophene) (P3HT) and fullerene (C60) as blends or multilayer were deposited on Al:ZnO (AZO) by Matrix-Assisted Pulsed Laser Evaporation (MAPLE) technique. The AZO layers were obtained by Pulsed Laser Deposition (PLD) on glass substrate, the high quality of the films being reflected by the calculated figure of merit. The organic heterostructures were investigated from morphological, optical and electrical point of view by atomic force microscopy (AFM), UV-vis spectroscopy, photoluminescence (PL) and current-voltage (I-V) measurements, respectively. The increase of the C60 content in the blend heterostructure has as result a high roughness. Compared with the multilayer heterostructure, those based on blends present an improvement in the electrical properties. Under illumination, the highest current value was recorded for the heterostructure based on the blend with the higher C60 amount. The obtained results showed that MAPLE is a useful technique for the deposition of the organic heterostructures on AZO as transparent conductor electrode.

Fluoride coatings for vacuum ultraviolet reflection filters.

PubMed

Guo, Chun; Kong, Mingdong; Lin, Dawei; Li, Bincheng

2015-12-10

LaF3/MgF2 reflection filters with a high spectral-discrimination capacity of the atomic-oxygen lines at 130.4 and 135.6 nm, which were employed in vacuum ultraviolet imagers, were prepared by molybdenum-boat thermal evaporation. The optical properties of reflection filters were characterized by a high-precision vacuum ultraviolet spectrophotometer. The vulnerability of the filter's microstructures to environmental contamination and the recovery of the optical properties of the stored filter samples with ultraviolet ozone cleaning were experimentally demonstrated. For reflection filters with the optimized nonquarter-wave multilayer structures, the reflectance ratios R135.6 nm/R130.4 nm of 92.7 and 20.6 were achieved for 7° and 45° angles of incidence, respectively. On the contrary, R135.6 nm/R130.4 nm ratio of 12.4 was obtained for a reflection filter with a standard π-stack multilayer structure with H/L=1/4 at 7° AOI.

Vertical discrepancy and microleakage of laser-sintered and vacuum-cast implant-supported structures luted with different cement types.

PubMed

Oyagüe, Raquel Castillo; Sánchez-Turrión, Andrés; López-Lozano, José Francisco; Suárez-García, M Jesús

2012-02-01

This study aimed to evaluate the vertical misfit and microleakage of laser-sintered and vacuum-cast cement-retained implant-supported frameworks. Three-unit implant-fixed structures were constructed with: (1) laser-sintered Co-Cr (LS); (2) vacuum-cast Co-Cr (CC); and (3) vacuum-cast Pd-Au (CP). Every framework was luted onto 2 prefabricated abutments under constant seating pressure. Each alloy group was randomly divided into three subgroups (n=10) according to the cement used: (1) Ketac Cem Plus (KC); (2) Panavia F 2.0 (PF); and (3) RelyX Unicem 2 Automix (RXU). After 30 days of water ageing, vertical discrepancy was measured by SEM, and marginal microleakage was scored using a digital microscope. Three-way ANOVA and Student-Newman-Keuls tests were run to investigate the effect of alloy/fabrication technique, FDP retainer, and cement type on vertical misfit. Data for marginal microleakage were analysed with Kruskal-Wallis and Dunn's tests (α=0.05). Vertical discrepancy was affected by alloy/manufacturing technique and cement type (p<0.001). Despite the luting agent, LS structures showed the best marginal adaptation, followed by CP, and CC. Within each alloy group, KC provided the best fit, whilst the use of PF or RXU resulted in no significant differences. Regardless of the framework alloy, KC exhibited the highest microleakage scores, whilst PF and RXU showed values that were comparable to each other. Laser-sintered Co-Cr structures achieved the best fit in the study. Notwithstanding the framework alloy, resin-modified glass-ionomer demonstrated better marginal fit but greater microleakage than did MDP-based and self-adhesive dual-cure resin cements. All groups were within the clinically acceptable misfit range. Laser-sintered Co-Cr may be an alternative to cast base metal and noble alloys to obtain passive-fitting structures. Despite showing higher discrepancies, resin cements displayed lower microleakage than resin-modified glass-ionomer. Further research is necessary to determine whether low microleakage scores may guarantee a suitable seal that could compensate for misfit. Copyright © 2011 Elsevier Ltd. All rights reserved.

Mass accommodation of water: bridging the gap between molecular dynamics simulations and kinetic condensation models.

PubMed

Julin, Jan; Shiraiwa, Manabu; Miles, Rachael E H; Reid, Jonathan P; Pöschl, Ulrich; Riipinen, Ilona

2013-01-17

The condensational growth of submicrometer aerosol particles to climate relevant sizes is sensitive to their ability to accommodate vapor molecules, which is described by the mass accommodation coefficient. However, the underlying processes are not yet fully understood. We have simulated the mass accommodation and evaporation processes of water using molecular dynamics, and the results are compared to the condensation equations derived from the kinetic gas theory to shed light on the compatibility of the two. Molecular dynamics simulations were performed for a planar TIP4P-Ew water surface at four temperatures in the range 268-300 K as well as two droplets, with radii of 1.92 and 4.14 nm at T = 273.15 K. The evaporation flux from molecular dynamics was found to be in good qualitative agreement with that predicted by the simple kinetic condensation equations. Water droplet growth was also modeled with the kinetic multilayer model KM-GAP of Shiraiwa et al. [Atmos. Chem. Phys. 2012, 12, 2777]. It was found that, due to the fast transport across the interface, the growth of a pure water droplet is controlled by gas phase diffusion. These facts indicate that the simple kinetic treatment is sufficient in describing pure water condensation and evaporation. The droplet size was found to have minimal effect on the value of the mass accommodation coefficient. The mass accommodation coefficient was found to be unity (within 0.004) for all studied surfaces, which is in agreement with previous simulation work. Additionally, the simulated evaporation fluxes imply that the evaporation coefficient is also unity. Comparing the evaporation rates of the mass accommodation and evaporation simulations indicated that the high collision flux, corresponding to high supersaturation, present in typical molecular dynamics mass accommodation simulations can under certain conditions lead to an increase in the evaporation rate. Consequently, in such situations the mass accommodation coefficient can be overestimated, but in the present cases the corrected values were still close to unity with the lowest value at ≈0.99.

Mass Accommodation of Water: Bridging the Gap Between Molecular Dynamics Simulations and Kinetic Condensation Models

PubMed Central

2012-01-01

The condensational growth of submicrometer aerosol particles to climate relevant sizes is sensitive to their ability to accommodate vapor molecules, which is described by the mass accommodation coefficient. However, the underlying processes are not yet fully understood. We have simulated the mass accommodation and evaporation processes of water using molecular dynamics, and the results are compared to the condensation equations derived from the kinetic gas theory to shed light on the compatibility of the two. Molecular dynamics simulations were performed for a planar TIP4P-Ew water surface at four temperatures in the range 268–300 K as well as two droplets, with radii of 1.92 and 4.14 nm at T = 273.15 K. The evaporation flux from molecular dynamics was found to be in good qualitative agreement with that predicted by the simple kinetic condensation equations. Water droplet growth was also modeled with the kinetic multilayer model KM-GAP of Shiraiwa et al. [Atmos. Chem. Phys.2012, 117, 2777]. It was found that, due to the fast transport across the interface, the growth of a pure water droplet is controlled by gas phase diffusion. These facts indicate that the simple kinetic treatment is sufficient in describing pure water condensation and evaporation. The droplet size was found to have minimal effect on the value of the mass accommodation coefficient. The mass accommodation coefficient was found to be unity (within 0.004) for all studied surfaces, which is in agreement with previous simulation work. Additionally, the simulated evaporation fluxes imply that the evaporation coefficient is also unity. Comparing the evaporation rates of the mass accommodation and evaporation simulations indicated that the high collision flux, corresponding to high supersaturation, present in typical molecular dynamics mass accommodation simulations can under certain conditions lead to an increase in the evaporation rate. Consequently, in such situations the mass accommodation coefficient can be overestimated, but in the present cases the corrected values were still close to unity with the lowest value at ≈0.99. PMID:23253100

A cloud-evaporation parameterization for general ciculation models

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schlesinger, M.E.; Oh, J.H.

1993-04-01

An evaporation-zone (EZ) model for cloud evaporation is developed. In this model a cloud consists of I [open quotes]cloudlets,[close quotes] each comprising cloud droplets with radii from zero to r[sub max], the latter value depending on the drop size distribution (DSD). Evaporation occurs only within the EZ comprised of J[le]I cloudlets. When the cloudlet at cloud edge evaporates, the EZ progresses one cloudlet into the cloud's interior. This eventually results in evaporation of the cloud in time t[sub E] = K(H/h)r[sup 2][sub max](1[minus]S[sub e])[sup [minus]1] where H is the cloud thickness, h the EZ thickness, S[sub e] the environmental saturationmore » ratio, and K a constant. Values of t[sub E](1[minus]S[sub e]) versus h are presented for eight observed DSDs. For use in atmospheric general circulation models (GCMs), the cloud evaporation process is represented by dm/dt=[minus](1[minus]S[sub e])m/[tau], where m is the cloud-water mixing ratio and [tau]=K(H/h)r[sup 2][sub max]n[sup [minus]1]. With parameter n chosen sufficiently large, a GCM cloud will evaporate virtually entirely in time t[sub E], for example, 99.3% for n = 5. Values of [tau] for use in the multilayer atmospheric CRCM have been determined by performing ten perpetual-January simulations and ten perpetual-July simulations, each set of ten for prescribed pairs of [tau] values for stratiform ([tau][sub s]) and cumuloform ([tau][sub c]) clouds. An optimum choice of [tau][sub s] and [tau][sub c], based on minimizing the errors of the model's simulated cloudiness, planetary albedo, outgoing longwave radiation, and precipitation, is [tau][sub s]=[tau][sub c] = 3 min. This corresponds to t[sub E](1-S[sub e]) = 15 min for both stratiform and cumuloform clouds; hence, to an EZ thickness of about 0.6-0.8 m for stratus, stratocumulus, and altostratus clouds, 2-3 m for nimbostratus and cumulus clouds, and 17 m for cumulonimbus clouds. 18 refs., 6 figs.« less

Preparation of hydroxyapatite-titania hybrid coatings on titanium alloy.

PubMed

Un, Serhat; Durucan, Caner

2009-08-01

Hydroxypapatite-titania hybrid films on Ti6Al4V alloys were prepared by sol-gel technique by incorporating presynthesized hydroxypapatite (Ca(10)(PO(4))(6)(OH)(2) or HAp) powders into a titanium-alkoxide dip coating solution. Titania network was formed by the hydrolysis and condensation of Ti-isopropoxide Ti[OCH(CH(3))(2)](4)-based sols. The effect of titania sol formulation, specifically the effect of organic solvents on the microstructure of the dip coated films calcined at 500 degrees C has been investigated. The coatings exhibit higher tendency for cracking when a high vapor pressure solvent, such as ethanol (C(2)H(5)OH) is used causing development of higher macroscopic stresses during evaporation of the sol. Titania sol formulations replacing the solvent with n-proponal (CH(3)(CH(2))(2)OH) and acetly-acetone (C(5)H(8)O) combinations enhanced the microstructural integrity of the coating during evaporation and calcination treatments. Sol-gel processing parameters, such as multilayer coating application and withdrawal rate, can be employed to change the titania thickness in the range of 0.120-1.1 microm and to control the microstructure of HAp-titania hybrid coatings. A high-calcination temperature in the range of 400-600 degrees C does not cause a distinct change in crystals nature of the titania matrix or HAp, but results in more cracking due to the combined effect of densification originated stresses and thermal stresses upon cooling. Slower withdraw rates and multilayer dip coating lead to coatings more vulnerable to microcracking.

Mechanical, Electrical and Magnetic Properties of Ferrogels with Embedded Iron Oxide Nanoparticles Obtained by Laser Target Evaporation: Focus on Multifunctional Biosensor Applications.

PubMed

Blyakhman, Felix A; Buznikov, Nikita A; Sklyar, Tatyana F; Safronov, Alexander P; Golubeva, Elizaveta V; Svalov, Andrey V; Sokolov, Sergey Yu; Melnikov, Grigory Yu; Orue, Iñaki; Kurlyandskaya, Galina V

2018-03-15

Hydrogels are biomimetic materials widely used in the area of biomedical engineering and biosensing. Ferrogels (FG) are magnetic composites capable of functioning as magnetic field sensitive transformers and field assisted drug deliverers. FG can be prepared by incorporating magnetic nanoparticles (MNPs) into chemically crosslinked hydrogels. The properties of biomimetic ferrogels for multifunctional biosensor applications can be set up by synthesis. The properties of these biomimetic ferrogels can be thoroughly controlled in a physical experiment environment which is much less demanding than biotests. Two series of ferrogels (soft and dense) based on polyacrylamide (PAAm) with different chemical network densities were synthesized by free-radical polymerization in aqueous solution with N , N '-methylene-diacrylamide as a cross-linker and maghemite Fe₂O₃ MNPs fabricated by laser target evaporation as a filler. Their mechanical, electrical and magnetic properties were comparatively analyzed. We developed a giant magnetoimpedance (MI) sensor prototype with multilayered FeNi-based sensitive elements deposited onto glass or polymer substrates adapted for FG studies. The MI measurements in the initial state and in the presence of FG with different concentrations of MNPs at a frequency range of 1-300 MHz allowed a precise characterization of the stray fields of the MNPs present in the FG. We proposed an electrodynamic model to describe the MI in multilayered film with a FG layer based on the solution of linearized Maxwell equations for the electromagnetic fields coupled with the Landau-Lifshitz equation for the magnetization dynamics.

[Mechanical properties of weld area soldered by lasers and structural changes in hot reaction zone].

PubMed

Wu, H; Cui, Y; Mu, W

2001-05-01

To analyse and measure the welding depths and strengths of three kinds of welding materials under different laser welding conditions as well as the structural changes of the heat affected zone. Under different voltages and pulse duration three kinds of measuring sticks, including Co-Cr alloy, Ni-Cr alloy and pure titanium were welded and their strengths were compared with that of control group. At the same time, the structure of the heat-affected zone was analysed by means of the gold-phase method. The welding depth and strength of Co-Cr alloy were in direct proportion to the setting voltage, with averages of 335MPa (250V) to 573MPa(330V). At the heat-affected zone, the crystal particle was small and the end point of welding by laser bean presented the shape of the mountain peak and the interval of finger shape. The center of measuring sticks had a black zone with the circle shape. The setting voltage was in direct proportion to the welding depth of pure titanium and in inverse proportion to the welding strength with averages of 221MPa(250V) to 154MPa (330V). The crystal particle in the heat affected zone grew large and the solid phase expanded, the interval of the crystal oxidised, and the structure showed honeycomb changes. The laser welding is favourable to the welding properties of Co-Cr and Ni-Cr alloys, but its effect on the welding properties of pure titanium needs further discussion.

Impedance spectroscopy of the oxide films formed during high temperature oxidation of a cobalt-plated ferritic alloy

NASA Astrophysics Data System (ADS)

Velraj, S.; Zhu, J. H.; Painter, A. S.; Du, S. W.; Li, Y. T.

2014-02-01

Impedance spectroscopy was used to evaluate the oxide films formed on cobalt-coated Crofer 22 APU ferritic stainless steel after thermal oxidation at 800 °C in air for different times (i.e. 2, 50, 100 and 500 h). Impedance spectra of the oxide films exhibited two or three semicircles depending on the oxidation time, which correspond to the presence of two or three individual oxide layers. Coupled with scanning electron microscopy/energy-dispersive spectroscopy (SEM/EDS) and X-ray diffraction (XRD), the individual oxide layer corresponding to each semicircle was determined unambiguously. Impedance spectrum analysis of the oxide films formed on the sample after thermal exposure at 800 °C in air for 2 h led to the identification of the low-frequency and high-frequency semicircles as being from Cr2O3 and Co3O4, respectively. SEM/EDS and XRD analysis of the 500-h sample clearly revealed the presence of three oxide layers, analyzed to be Co3-xCrxO4, CoCr2O4, and Cr2O3. Although the SEM images of the 50-h and 100-h samples did not clearly show the CoCr2O4 layer, impedance plots implied their presence. The oxide scales were assigned to their respective semicircles and the electrical properties of Co3-xCrxO4, CoCr2O4 and Cr2O3 were determined from the impedance data.

[Determination of the dynamic levels of interleukin-8 in gingival crevicular fluid of porcelain teeth with three different alloys].

PubMed

Xu, Weixing; Su, Jiansheng

2012-06-01

To study the interleukin-8 (IL-8) levels in gingival crevicular fluid (GCF) of porcelain teeth coated with Ni-Cr, Co-Cr or gold alloy at different time periods, and to uncover the degree of stimulation by these alloys on gingiva at different time periods. 45 cases of porcelain teeth coated with Ni-Cr, Co-Cr or gold alloy were selected randomly, with 15 cases in each group. Sandwich enzyme-linked immunosorbent assay (ELISA) was used to determine the concentration and total amount of IL-8 in GCF. The assay was done before treatment, as well as at 1, 3 and 6 months post-treatment. The total amounts of IL-8 and GCF volume in the Ni-Cr alloy coated porcelain teeth were higher in different time period than those before treatment (P<0.05). However, the IL-8 levels in Co-Cr and gold alloy coated porcelain teeth returned to pre-dental restoration after 3 months. Otherwise, the levels of IL-8 concentration in GCF showed no significant difference among the three different alloys coating at different time periods. IL-8 is an important cytokine during tissue inflammation. Therefore, the level of IL-8 in GCF is a useful criteria for the evaluation of stimulation degree on gingiva by different alloy coating materials in porcelain teeth. The clinical choice of different alloy coating for porcelain teeth should be considered accordingly.

Macrophage Biocompatibility of CoCr Wear Particles Produced under Polarization in Hyaluronic Acid Aqueous Solution

PubMed Central

Perez-Maceda, Blanca Teresa; López-Fernández, María Encarnación; Díaz, Iván; Kavanaugh, Aaron; Billi, Fabrizio; Escudero, María Lorenza; García-Alonso, María Cristina; Lozano, Rosa María

2018-01-01

Macrophages are the main cells involved in inflammatory processes and in the primary response to debris derived from wear of implanted CoCr alloys. The biocompatibility of wear particles from a high carbon CoCr alloy produced under polarization in hyaluronic acid (HA) aqueous solution was evaluated in J774A.1 mouse macrophages cultures. Polarization was applied to mimic the electrical interactions observed in living tissues. Wear tests were performed in a pin-on-disk tribometer integrating an electrochemical cell in phosphate buffer solution (PBS) and in PBS supplemented with 3 g/L HA, an average concentration that is generally found in synovial fluid, used as lubricant solution. Wear particles produced in 3 g/L HA solution showed a higher biocompatibility in J774A.1 macrophages in comparison to those elicited by particles obtained in PBS. A considerable enhancement in macrophages biocompatibility in the presence of 3 g/L of HA was further observed by the application of polarization at potentials having current densities typical of injured tissues suggesting that polarization produces an effect on the surface of the metallic material that leads to the production of wear particles that seem to be macrophage-biocompatible and less cytotoxic. The results showed the convenience of considering the influence of the electric interactions in the chemical composition of debris detached from metallic surfaces under wear corrosion to get a better understanding of the biological effects caused by the wear products. PMID:29738506

Evaluation of marginal/internal fit of chrome-cobalt crowns: Direct laser metal sintering versus computer-aided design and computer-aided manufacturing.

PubMed

Gunsoy, S; Ulusoy, M

2016-01-01

The purpose of this study was to evaluate the internal and marginal fit of chrome cobalt (Co-Cr) crowns were fabricated with laser sintering, computer-aided design (CAD) and computer-aided manufacturing, and conventional methods. Polyamide master and working models were designed and fabricated. The models were initially designed with a software application for three-dimensional (3D) CAD (Maya, Autodesk Inc.). All models were fabricated models were produced by a 3D printer (EOSINT P380 SLS, EOS). 128 1-unit Co-Cr fixed dental prostheses were fabricated with four different techniques: Conventional lost wax method, milled wax with lost-wax method (MWLW), direct laser metal sintering (DLMS), and milled Co-Cr (MCo-Cr). The cement film thickness of the marginal and internal gaps was measured by an observer using a stereomicroscope after taking digital photos in ×24. Best fit rates according to mean and standard deviations of all measurements was in DLMS both in premolar (65.84) and molar (58.38) models in μm. A significant difference was found DLMS and the rest of fabrication techniques (P < 0.05). No significant difference was found between MCo-CR and MWLW in all fabrication techniques both in premolar and molar models (P > 0.05). DMLS was best fitting fabrication techniques for single crown based on the results.The best fit was found in marginal; the larger gap was found in occlusal.All groups were within the clinically acceptable misfit range.

A study on 100 MeV O7+ irradiated SnO2/Ag/SnO2 multilayer as transparent electrode for flat panel display application

NASA Astrophysics Data System (ADS)

Sharma, Vikas; Singh, Satyavir; Asokan, K.; Sachdev, Kanupriya

2016-07-01

The multilayer thin films of SnO2/Ag/SnO2 were deposited using electron-beam and thermal evaporation for flat panel display application. The as-prepared SnO2/Ag/SnO2 specimen was irradiated with 100 MeV O7+ ions by varying the fluences 1 × 1012 and 5 × 1012 ions/cm2. The pristine and irradiated films were investigated using XRD, SEM, AFM and Raman to find out modification in the structure and surface morphology of the films. UV-Vis and Hall measurement techniques were used to investigate the optical and electrical properties respectively. It was observed that the roughness of the film after irradiation (for the fluence of 1 × 1012 ions/cm2) ​ decreased to 0.68 nm from 1.6 nm and showed an increase in roughness to 1.35 nm on increasing the fluence to 5 × 1012 ions/cm2. This oxide/metal/oxide structure fulfills the basic requirements of a TCE, like high-transmittance >75% for pristine and >80% for the fluence of 1 × 1012 ions/cm2 over a broad spectrum of visible light for practical applications. The multilayer structure shows change in the electrical resistivity from 1.6 × 10-3 Ω cm to 6.3 × 10-3 Ω cm after irradiation.

Fretting corrosion of CoCr alloy: Effect of load and displacement on the degradation mechanisms.

PubMed

Bryant, Michael; Neville, Anne

2017-02-01

Fretting corrosion of medical devices is of growing concern, yet, the interactions between tribological and electrochemical parameters are not fully understood. Fretting corrosion of CoCr alloy was simulated, and the components of damage were monitored as a function of displacement and contact pressure. Free corrosion potential (E corr ), intermittent linear polarisation resistance and cathodic potentiostatic methods were used to characterise the system. Interferometry was used to estimate material loss post rubbing. The fretting regime influenced the total material lost and the dominant degradation mechanism. At high contact pressures and low displacements, pure corrosion was dominant with wear and its synergies becoming more important as the contact pressure and displacement decreased and increased, respectively. In some cases, an antagonistic effect from the corrosion-enhanced wear contributor was observed suggesting that film formation and removal may be present. The relationship between slip mechanism and the contributors to tribocorrosion degradation is presented.

Initial tension loss in cerclage cables.

PubMed

Ménard, Jérémie; Émard, Maxime; Canet, Fanny; Brailovski, Vladimir; Petit, Yvan; Laflamme, George Y

2013-10-01

Cerclage cables, frequently used in the management of fractures and osteotomies, are associated with a high failure rate and significant loosening during surgery. This study compared the capacity to maintain tension of different types of orthopaedic cable systems. Multifilament Cobalt-Chrome (CoCr) cables with four different crimp/clamp devices (DePuy, Stryker, Zimmer and Smith&Nephew) and one non-metallic Nylon (Ny) cable from Kinamed were instrumented with a load cell to measure tension during insertion. Significant tension loss was observed with crimping for all cables (P<0.05). Removing the tensioner led to an additional unexpected tension loss (CoCr-DePuy: 18%, CoCr-Stryker: 29%, CoCr-Smith&Nephew: 33%, Ny: 46%, and CoCr-Zimmer: 52%). The simple CoCr (DePuy) cable system outperformed the more sophisticated locking devices due to its significantly better ability to prevent tension loss. Copyright © 2013 Elsevier Inc. All rights reserved.

Infiltration of trace metal ions in the oral mucosa of a rat analyzed using SRXRF, XAFS, and ICP-MS.

PubMed

Imamura, Toshihiro; Kanno, Zuisei; Imai, Haruki; Sugiyama, Tomoko; Wada, Takahiro; Yoshida, Midori; Sakama, Minoru; Ono, Takashi; Honda, Eiichi; Uo, Motohiro

2015-01-01

Although the accumulation and distribution of metals from metallic orthodontic appliances in the oral mucosa have been studied extensively, they remain unclear because their concentration is quite low. In this study, metal specimens (Ni, Ni-Ti, and Co-Cr) were sutured in the unilateral oral mucosa of rats, and the distribution of the eluted elements in the mucosal tissue was estimated using inductively coupled plasma mass spectrometry (ICP-MS) and synchrotron radiation X-ray fluorescence analysis (SR-XRF). While the infiltrations of Ni, Co, and Cr into the oral mucosal connective tissue were observed with SR-XRF, significant increases were only found in Ni from the pure Ni group and Cr from the Co-Cr group. Furthermore, Ni and Co were estimated as hydrated ions while Cr was estimated in oxide form through X-ray absorption fine structure (XAFS) analysis.

MOVPE of GaSb/InGaAsSb Multilayers and Fabrication of Dual Band Photodetectors

NASA Technical Reports Server (NTRS)

Xiao, Ye-Gao; Bhat, Ishwara; Refaat, Tamer F.; Abedin, M. Nurul; Shao, Qing-Hui

2005-01-01

Metalorganic vapor phase epitaxy (MOVPE) of GaSb/InGaAsSb multilayer thin films and fabrication of bias-selectable dual band photodetectors are reported. For the dual band photodetectors the short wavelength detector, or the upper p- GaSb/n-GaSb junction photodiode, is placed optically ahead of the long wavelength one, or the lower photodiode. The latter is based on latticed-matched In0.13Ga0.87As0.11Sb0.89 with bandgap near 0.6 eV. Specifically, high quality multilayer thin films are grown sequentially from top to bottom as p+-GaSb/p-GaSb/n-GaSb/n-InGaAsSb/p-InGaAsSb/p-GaSb on undoped p-type GaSb substrate, and as n-GaSb/p-GaSb/p-InGaAsSb/n-InGaAsSb/n-GaSb on Te-doped n-type GaSb substrate respectively. The multilayer thin films are characterized by optical microscope, atomic force microscope (AFM), electron microprobe analyses etc. The photodiode mesa steps are patterned by photolithography with wet chemical etching and the front metallization is carried out by e-beam evaporation with Pd/Ge/Au/Ti/Au to give ohmic contact on both n- and p-type Sb based layer surfaces. Dark I-V measurements show typical diode behavior for both the upper and lower photodiodes. The photoresponsivity measurements indicate that both the upper and lower photodiodes can sense the infrared illumination corresponding to their cutoff wavelengths respectively, comparable with the simulation results. More work is underway to bring the long wavelength band to the medium infrared wavelength region near 4 micrometers.

Comparison of joint designs for laser welding of cast metal plates and wrought wires.

PubMed

Takayama, Yasuko; Nomoto, Rie; Nakajima, Hiroyuki; Ohkubo, Chikahiro

2013-01-01

The purpose of the present study was to compare joint designs for the laser welding of cast metal plates and wrought wire, and to evaluate the welded area internally using X-ray micro-focus computerized tomography (micro-CT). Cast metal plates (Ti, Co-Cr) and wrought wires (Ti, Co-Cr) were welded using similar metals. The specimens were welded using four joint designs in which the wrought wires and the parent metals were welded directly (two designs) or the wrought wires were welded to the groove of the parent metal from one or both sides (n = 5). The porosity and gap in the welded area were evaluated by micro-CT, and the maximum tensile load of the welded specimens was measured with a universal testing machine. An element analysis was conducted using an electron probe X-ray microanalyzer. The statistical analysis of the results was performed using Bonferroni's multiple comparisons (α = 0.05). The results included that all the specimens fractured at the wrought wire when subjected to tensile testing, although there were specimens that exhibited gaps due to the joint design. The wrought wires were affected by laser irradiation and observed to melt together and onto the filler metal. Both Mo and Sn elements found in the wrought wire were detected in the filler metal of the Ti specimens, and Ni was detected in the filler metal of the Co-Cr specimens. The four joint designs simulating the designs used clinically were confirmed to have adequate joint strength provided by laser welding.

Influence of low concentration acid treatment on lithium disilicate core/veneer ceramic bond strength

PubMed Central

Garcia, Rudan P.; Conti, Paulo CR.; Pereira, Jefferson R.; Valle, Accácio Ld.

2013-01-01

Objective: This study evaluated the influence of low concentration acid treatment on the shear bond strength between lithium disilicate (LD) infrastructure and veneering porcelain. The surface morphology characteristic after this acid treatment was also examined. Study Design: LD reinforced ceramic cylinders (n=10) (IPS e.max Press, Ivoclar-Vivadent, Schaan, Liechtenstein) were treated (LD-treated) with a low concentration acid solution (Invex Liquid – Ivoclar-Vivadent, Schaan, Liechtenstein) or not treated with the acid solution (LD-untreated). They were veneered with a glass ceramic (IPS e.max Ceram, Ivoclar-Vivadent, Schaan, Liechtenstein). A metal ceramic group (CoCr) was tested as control. Shear bond strength (SBS) was conducted using a universal testing machine at 0.5 mm/min. Surface morphology characteristics after acid treatment were analyzed using scanning electron microscopy. Results: The acid treatment at low concentrations did not influence the SBS of the LD/veneering porcelain interface. The CoCr group showed the significant higher SBS value (35.59 ± 5.97 MPa), followed by LD-untreated group (27.76 ± 3.59 MPa) and LD-treated (27.02 ± 4.79 MPa). The fracture modes were predominantly adhesive for CoCr group and cohesive within the infrastructure for DL groups. Scanning Electron Microscopy (SEM) analysis showed no morphological differences between treated and untreated LD surfaces. Conclusions: Low concentration acid treatment did not improved SBS of veneering ceramic to LD and did not cause morphological changes on the LD surface. Key words:Lithium disilicate, glass ceramics, acid etching, shear bond strength, scanning electron microscopy. PMID:24455073

Effect of surface reaction layer on grindability of cast titanium alloys.

PubMed

Ohkubo, Chikahiro; Hosoi, Toshio; Ford, J Phillip; Watanabe, Ikuya

2006-03-01

The purpose of this study was to investigate the effect of the cast surface reaction layer on the grindability of titanium alloys, including free-machining titanium alloy (DT2F), and to compare the results with the grindability of two dental casting alloys (gold and Co-Cr). All titanium specimens (pure Ti, Ti-6Al-4V and DT2F) were cast using a centrifugal casting machine in magnesia-based investment molds. Two specimen sizes were used to cast the titanium metals so that the larger castings would be the same size as the smaller gold and Co-Cr alloy specimens after removal of the surface reaction layer (alpha-case). Grindability was measured as volume loss ground from a specimen for 1 min using a handpiece engine with a SiC abrasive wheel at 0.1 kgf and four circumferential wheel speeds. For the titanium and gold alloys, grindability increased as the rotational speed increased. There was no statistical difference (p>0.05) in grindability for all titanium specimens either with or without the alpha-case. Of the titanium metals tested, Ti-6 Al-4V had the greatest grindability at higher speeds, followed by DT2F and CP Ti. The grindability of the gold alloy was similar to that of Ti-6 Al-4V, whereas the Co-Cr alloy had the lowest grindability. The results of this study indicated that the alpha-case did not significantly affect the grindability of the titanium alloys. The free-machining titanium alloy had improved grindability compared to CP Ti.

A quantitative experimental phantom study on MRI image uniformity.

PubMed

Felemban, Doaa; Verdonschot, Rinus G; Iwamoto, Yuri; Uchiyama, Yuka; Kakimoto, Naoya; Kreiborg, Sven; Murakami, Shumei

2018-05-23

Our goal was to assess MR image uniformity by investigating aspects influencing said uniformity via a method laid out by the National Electrical Manufacturers Association (NEMA). Six metallic materials embedded in a glass phantom were scanned (i.e. Au, Ag, Al, Au-Ag-Pd alloy, Ti and Co-Cr alloy) as well as a reference image. Sequences included spin echo (SE) and gradient echo (GRE) scanned in three planes (i.e. axial, coronal, and sagittal). Moreover, three surface coil types (i.e. head and neck, Brain, and temporomandibular joint coils) and two image correction methods (i.e. surface coil intensity correction or SCIC, phased array uniformity enhancement or PURE) were employed to evaluate their effectiveness on image uniformity. Image uniformity was assessed using the National Electrical Manufacturers Association peak-deviation non-uniformity method. Results showed that temporomandibular joint coils elicited the least uniform image and brain coils outperformed head and neck coils when metallic materials were present. Additionally, when metallic materials were present, spin echo outperformed gradient echo especially for Co-Cr (particularly in the axial plane). Furthermore, both SCIC and PURE improved image uniformity compared to uncorrected images, and SCIC slightly surpassed PURE when metallic metals were present. Lastly, Co-Cr elicited the least uniform image while other metallic materials generally showed similar patterns (i.e. no significant deviation from images without metallic metals). Overall, a quantitative understanding of the factors influencing MR image uniformity (e.g. coil type, imaging method, metal susceptibility, and post-hoc correction method) is advantageous to optimize image quality, assists clinical interpretation, and may result in improved medical and dental care.

Characterization of ZrO2 buffer layers for sequentially evaporated Y-Ba-CuO on Si and Al2O3 substrates

NASA Technical Reports Server (NTRS)

Valco, George J.; Rohrer, Norman J.; Pouch, John J.; Warner, Joseph D.; Bhasin, Kul B.

1988-01-01

Thin film high temperature superconductors have the potential to change the microwave technology for space communications systems. For such applications it is desirable that the films be formed on substrates such as Al2O3 which have good microwave properties. The use of ZrO2 buffer layers between Y-Ba-Cu-O and the substrate has been investigated. These superconducting films have been formed by multilayer sequential electron beam evaporation of Cu, BaF2 and Y with subsequent annealing. The three layer sequence of Y/BaF2/Cu is repeated four times for a total of twelve layers. Such a multilayer film, approximately 1 micron thick, deposited directly on SrTiO3 and annealed at 900 C for 45 min produces a film with a superconducting onset of 93 K and critical temperature of 85 K. Auger electron spectroscopy in conjunction with argon ion sputtering was used to obtain the distribution of each element as a function of depth for an unannealed film, the annealed film on SrTiO3 and annealed films on ZrO2 buffer layers. The individual layers were apparent. After annealing, the bulk of the film on SrTiO3 is observed to be fairly uniform while films on the substrates with buffer layers are less uniform. The Y-Ba-Cu-O/ZrO2 interface is broad with a long Ba tail into the ZrO2, suggesting interaction between the film and the buffer layer. The underlying ZrO2/Si interface is sharper. The detailed Auger results are presented and compared with samples annealed at different temperatures and durations.

Dual-energy CT and ceramic or titanium prostheses material reduce CT artifacts and provide superior image quality of total knee arthroplasty.

PubMed

Kasparek, Maximilian F; Töpker, Michael; Lazar, Mathias; Weber, Michael; Kasparek, Michael; Mang, Thomas; Apfaltrer, Paul; Kubista, Bernd; Windhager, Reinhard; Ringl, Helmut

2018-06-07

To evaluate the influence of different scan parameters for single-energy CT and dual-energy CT, as well as the impact of different material used in a TKA prosthesis on image quality and the extent of metal artifacts. Eight pairs of TKA prostheses from different vendors were examined in a phantom set-up. Each pair consisted of a conventional CoCr prosthesis and the corresponding anti-allergic prosthesis (full titanium, ceramic, or ceramic-coated) from the same vendor. Nine different (seven dual-energy CT and two single-energy CT) scan protocols with different characteristics were used to determine the most suitable CT protocol for TKA imaging. Quantitative image analysis included assessment of blooming artifacts (metal implants appear thicker on CT than they are, given as virtual growth in mm in this paper) and streak artifacts (thick dark lines around metal). Qualitative image analysis was used to investigate the bone-prosthesis interface. The full titanium prosthesis and full ceramic knee showed significantly fewer blooming artifacts compared to the standard CoCr prosthesis (mean virtual growth 0.6-2.2 mm compared to 2.9-4.6 mm, p < 0.001). Dual-energy CT protocols showed less blooming (range 3.3-3.8 mm) compared to single-energy protocols (4.6-5.5 mm). The full titanium and full ceramic prostheses showed significantly fewer streak artifacts (mean standard deviation 77-86 Hounsfield unit (HU)) compared to the standard CoCr prosthesis (277-334 HU, p < 0.001). All dual-energy CT protocols had fewer metal streak artifacts (215-296 HU compared to single-energy CT protocols (392-497 HU)). Full titanium and ceramic prostheses were ranked superior with regard to the image quality at the bone/prosthesis interface compared to a standard CoCr prosthesis, and all dual-energy CT protocols were ranked better than single-energy protocols. Dual-energy CT and ceramic or titanium prostheses reduce CT artifacts and provide superior image quality of total knee arthroplasty at the bone/prosthesis interface. These findings support the use of dual-energy CT as a solid imaging base for clinical decision-making and the use of full-titanium or ceramic prostheses to allow for better CT visualization of the bone-prosthesis interface.

Comparative study of circumferential clasp retention force for titanium and cobalt-chromium removable partial dentures.

PubMed

Rodrigues, Renata Cristina Silveira; Ribeiro, Ricardo Faria; de Mattos, Maria da Gloria Chiarello; Bezzon, Osvaldo Luiz

2002-09-01

The interest in using titanium to fabricate removable partial denture (RPD) frameworks has increased, but there are few studies to support its use. The objective of this study was to compare circumferential RPD clasps made of commercially pure titanium and identical clasps made of 2 different cobalt (Co)-chromium (Cr) alloys by testing insertion/removal and radiographically inspecting the casts for defects. On refractory casts that represent a partially edentulous mandibular right hemi-arch segment, 36 frameworks were cast from commercially pure titanium (n = 12) and 2 Co-Cr alloys (n = 12 each) with identical prefabricated patterns and the manufacturer-designated investment and casting technique. Each group was divided into 2 subgroups, corresponding to .25-mm and .50-mm undercuts, respectively. No polishing procedures were performed to ensure uniformity. Only nodules and burs were carefully removed with tungsten burs under magnification when necessary. The specimens were radiographed and subjected to an insertion/removal test simulating 5 years of framework use. The data were subjected to analysis of variance and the Tukey complementary test (P<.01) to compare the retentive forces of RPDs made with the different materials. The Student t test (P<.01) was used to compare the retentive forces of RPDs fabricated with the same alloy with different undercuts. A total of 20% of the titanium specimens demonstrated porosity, showing casting difficulties, and any defect detected on the clasps determined the sample replacement. For Co-Cr alloys, casting difficulties were not found. The data were subjected to analysis of variance and the Tukey complementary test to compare materials for the same undercut. For the .25-mm undercut, no significant difference was found between Magnum and Rematitan alloys; they were both different from the Remanium alloy (P<.01). For the.50-mm undercut, no significant difference was found between Co-Cr alloys; they were both different from Rematitan alloy (P<.01). The Student t test used to compare the same alloys with different undercuts showed no significant difference between Remanium with .25-mm and .50-mm undercuts. For Magnum and Rematitan alloys, there was a significant difference between different undercuts (P=.01). Within the limitations of this simulation study, the results suggest that commercially pure titanium clasps maintained retention over a simulated 5-year period, with lower retention force than identical Co-Cr clasps.

Design and development of multilayer wideband antireflection coating and its annealing study

NASA Astrophysics Data System (ADS)

Jena, S.; Tokas, R. B.; Udupa, D. V.; Thakur, S.; Sahoo, N. K.

2018-04-01

Reflection loss occurs at the glass-air interface, limits performance of many optical devices such as eyeglass, camera lenses, and photovoltaic solar cells. Antireflection (AR) coating on the glass reduces the reflection loss and improves efficiency of such devices. In this paper, wideband AR coating in the visible region has been designed and developed using ZrO2-MgO/SiO2 multilayer. The thicknesses of individual thin layers are numerically optimized to get maximum transmission of the visible light. The optimized four thin layers have been deposited on BK7 glass substrate using electron beam evaporation technique. The measured transmission spectrum of the 4-layer AR coating is compared with that of simulated spectrum. The transmission of the single side AR coating increases by more than 3% as compared to that of bare glass substrate in the wavelength region of 470 nm - 810 nm. The wideband AR coating has been annealed at 200°C for 4 hours in ambient condition. The transmission of the AR coating decreases after the annealing, resulting degradation in its wideband AR characteristics.

Measurement of Two-Phase Flow and Heat Transfer Parameters using Infrared Thermometry

NASA Technical Reports Server (NTRS)

Kim, Tae-Hoon; Kommer, Eric; Dessiatoun, Serguei; Kim, Jungho

2012-01-01

A novel technique to measure heat transfer and liquid film thickness distributions over relatively large areas for two-phase flow and heat transfer phenomena using infrared (IR)thermometry is described. IR thermometry is an established technology that can be used to measure temperatures when optical access to the surface is available in the wavelengths of interest. In this work, a midwave IR camera (3.6-5.1 microns) is used to determine the temperature distribution within a multilayer consisting of a silicon substrate coated with a thin insulator. Since silicon is largely transparent to IR radiation, the temperature of the inner and outer walls of the multilayer can be measured by coating selected areas with a thin, IR opaque film. If the fluid used is also partially transparent to IR, the flow can be visualized and the liquid film thickness can be measured. The theoretical basis for the technique is given along with a description of the test apparatus and data reduction procedure. The technique is demonstrated by determining the heat transfer coefficient distributions produced by droplet evaporation and flow boiling heat transfer.

Assessment of hydrochemical processes and groundwater hydrodynamics in a multilayer aquifer system under long-term irrigation condition: A case study of Nefzaoua basin, southern Tunisia.

PubMed

Tarki, M; Ben Hammadi, M; El Mejri, H; Dassi, L

2016-04-01

The hydrochemical and isotopic investigation of the Nefzaoua aquifer system demonstrates that groundwater mineralization in is controlled by natural and anthropogenic processes including water-rock interaction and irrigation return flow. It identifies all of the water bodies that flow within the aquifer system and their circulation patterns. The isotopically depleted paleowaters, identified within the deep and intermediate aquifers, undergo significant enrichment by evaporation during irrigation and recharged the shallow aquifer by return flow. Subsequently, they infiltrate to the intermediate aquifer which receives also rainfall modern recharge. Copyright © 2016 Elsevier Ltd. All rights reserved.

Microstructural Investigation of a Wark-Lovering Rim on a Vigarano CAI

NASA Technical Reports Server (NTRS)

Han, J.; Keller, L. P.; Needham, A. W.; Messenger, S.; Simon, J. I.

2015-01-01

Wark-Lovering (WL) rims are thin multi-layered mineral sequences that surround many CAIs. These rim layers consist of the primary minerals found in the CAI interiors, but vary in their mineralogy. Several models for their origin have been proposed including condensation, reaction with a nebular gas, evaporation, or combinations of these. However, there still is little consensus on how and when the rims formed. Here, we describe the microstructure and mineralogy of a WL rim on a type B CAI from the Vigarano CV(sub red) chondrite using FIB/TEM to better understand the astrophysical significance of WL rim formation.

Measurements of the apparent thermal conductivity of multi-layer insulation between 20 K and 90 K

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hurd, Joseph A.; Van Sciver, Steven W.

NASA has the need to efficiently store cryogenic propellants in space for long periods of time. One method to improve storage efficiency is to use multi-layer insulation (MLI), a technique that minimizes the boiling rate due to radiation heat transfer. Typically, the thermal performance of MLI is determined by measuring the rate of evaporation of liquid nitrogen from a calibrated cryostat. The main limitation with this method is that testing conditions are restricted by the boiling temperature of the LN{sub 2}, which may not match the requirements of the application. The Multi-Layer Insulation Thermal Conductivity Experiment (MIKE) at the Nationalmore » High Magnetic Field Laboratory is capable of measuring the effective thermal conductivity of MLI at variable boundary temperatures. MIKE uses cryo-refrigerators to control boundary temperatures in the calorimeter and a calibrated thermal link to measure the heat load. To make the measurements requested by NASA, MIKE needed to be recalibrated for the 20 K to 90 K range. Also, due to the expectation of a lower heat transfer rate, the heat load support rod material was changed to one with a lower thermal conductivity to ensure the temperature difference seen on the cold rod could be measurable at the estimated heat load. Presented are the alterations to MIKE including calibration data and heat load measurements on new load-bearing MLI supplied by NASA.« less

An analytical model to design circumferential clasps for laser-sintered removable partial dentures.

PubMed

Alsheghri, Ammar A; Alageel, Omar; Caron, Eric; Ciobanu, Ovidiu; Tamimi, Faleh; Song, Jun

2018-06-21

Clasps of removable partial dentures (RPDs) often suffer from plastic deformation and failure by fatigue; a common complication of RPDs. A new technology for processing metal frameworks for dental prostheses based on laser-sintering, which allows for precise fabrication of clasp geometry, has been recently developed. This study sought to propose a novel method for designing circumferential clasps for laser-sintered RPDs to avoid plastic deformation or fatigue failure. An analytical model for designing clasps with semicircular cross-sections was derived based on mechanics. The Euler-Bernoulli elastic curved beam theory and Castigliano's energy method were used to relate the stress and undercut with the clasp length, cross-sectional radius, alloy properties, tooth type, and retention force. Finite element analysis (FEA) was conducted on a case study and the resultant tensile stress and undercut were compared with the analytical model predictions. Pull-out experiments were conducted on laser-sintered cobalt-chromium (Co-Cr) dental prostheses to validate the analytical model results. The proposed circumferential clasp design model yields results in good agreement with FEA and experiments. The results indicate that Co-Cr circumferential clasps in molars that are 13mm long engaging undercuts of 0.25mm should have a cross-section radius of 1.2mm to provide a retention of 10N and to avoid plastic deformation or fatigue failure. However, shorter circumferential clasps such as those in premolars present high stresses and cannot avoid plastic deformation or fatigue failure. Laser-sintered Co-Cr circumferential clasps in molars are safe, whereas they are susceptible to failure in premolars. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

[Effect of different heat treatment on the bonding strength of porcelain and Co-Cr alloy].

PubMed

Liao, Juan-kun; Ye, Jian-tao; Zhu, Feng; Zhang, Cui-cui; Wen, Xiao-shan; Zhang, Yi-ping; Li, Bo-hua

2011-12-01

To investigate and compare the effect of different heat treatment on the metal- ceramic bonding strength and the interfacial microstructure of the Co-Cr alloy. Thirty specimens were made according to ISO 9693,and then divided into 3 groups (n=10) through the measurements .Group A(degassed 60s):degassed and then maintained 60s in 980 degrees centigrade Group B(degassed 60s and preoxidation 60s): degassed and maintained 60s in 980 degrees centigrade, then were maintained continuously for 60s in 980 degrees centigrade after re-gassed,Group C(degassed 120s): degassed and maintained 120s in 980 degrees centigrade. The bonding strengths of the three groups were evaluated through three point bending test. Six specimens divided into 3 group were made in the same method to observe the metal-ceramic interface through scanning electronic microscope(SEM) and energy dispersive spectrum(EDS).The bonding strength data were analyzed using ANOVA and Bonferroni's test by SPSS13.0 software package. The mean value of bonding strength was (39.03±2.70)MPa for group A, (34.43±2.36)MPa for group B, (31.65±1.49)MPa for group C, respectively. There were significant difference between every two groups (P<0.05). SEM demonstrated that the width of interfacial transition layer was 12.3-16.4μm in group A, 15.2-21.8μm in group B and 26.3-32.2μm in group C. Higher metal-ceramic bonding strength for Co-Cr alloy will be formed under the situation of degassed,and maintained 60s in 980 degrees centigrade ; while extending degassed time, prolonging the heat maintained time and preoxidation after degassing will reduce metal-ceramic bonding strength.

Assessment of Corrosion, Fretting, and Material Loss of Retrieved Modular Total Knee Arthroplasties.

PubMed

Martin, Audrey J; Seagers, Kirsten A; Van Citters, Douglas W

2017-07-01

Modular junctions in total hip arthroplasties have been associated with fretting, corrosion, and debris release. The purpose of this study is to analyze damage severity in total knee arthroplasties of a single design by qualitative visual assessment and quantitative material loss measurements to evaluate implant performance and patient impact via material loss. Twenty-two modular knee retrievals of the same manufacturer were identified from an institutional review board-approved database. Junction designs included tapers with an axial screw and tapers with a radial screw. Constructs consisted of 2 metal alloys: CoCr and Ti6Al4V. Components were qualitatively scored and quantitatively measured for corrosion and fretting. Negative values represent adhered material. Statistical differences were analyzed using sign tests. Correlations were tested with a Spearman rank order test (P < .05). The median volumetric material loss and the maximum linear depth for the total population were -0.23 mm 3 and 5.84 μm, respectively. CoCr components in mixed metal junctions had higher maximum linear depth (P = .007) than corresponding Ti components. Fretting scores of Ti6Al4V alloy components in mixed metal junctions were statistically higher than the remaining groups. Taper angle did not correlate with material loss. Results suggest that CoCr components in mixed metal junctions are more vulnerable to corrosion than other components, suggesting preferential corrosion when interfacing with Ti6Al4V. Overall, although corrosion was noted in this series, material loss was low, and none were revised for clinical metal-related reaction. This suggests the clinical impact from corrosion in total knee arthroplasty is low. Copyright © 2017 Elsevier Inc. All rights reserved.

What is the changing frequency of diamond burs?

PubMed

Emir, Faruk; Ayyildiz, Simel; Sahin, Cem

2018-04-01

The purpose of this study was to determine the changing frequency of a diamond bur after multiple usages on 3 different surfaces. Human premolar teeth (N = 26), disc shaped direct metal laser sintered CoCr (N = 3) and zirconia specimens (N = 3) were used in this study. Groups named basically as Group T for teeth, Group M for CoCr, and Group Z for zirconia. Round tapered black-band diamond bur was used. The specimens were randomly divided into three groups and placed with a special assembly onto the surveyor. 1, 5, and 10 preparation protocols were performed to the first, second, and third sub-groups, respectively. The subgroups were named according to preparation numbers (1, 5, 10). The mentioned bur of each group was then used at another horizontal preparation on a new tooth sample. The same procedure was used for CoCr and zirconia disc specimens. All of the bur surfaces were evaluated using roughness analysis. Then, horizontal tooth preparation surfaces were examined under both stereomicroscope and SEM. The depth maps of tooth surfaces were also obtained from digital stereomicroscopic images. The results were statistically analyzed using One-Way ANOVA, and the Tukey HSD post-hoc tests (α=.05). All of the groups were significantly different from the control group ( P <.001). There was no significant difference between groups Z5 and Z10 ( P =.928). Significant differences were found among groups T5, M5, and Z5 ( P <.001). Diamond burs wear after multiple use and they should be changed after 5 teeth preparations at most. A diamond bur should not be used for teeth preparation after try-in procedures of metal or zirconia substructures.

The fit of cobalt-chromium three-unit fixed dental prostheses fabricated with four different techniques: a comparative in vitro study.

PubMed

Örtorp, Anders; Jönsson, David; Mouhsen, Alaa; Vult von Steyern, Per

2011-04-01

This study sought to evaluate and compare the marginal and internal fit in vitro of three-unit FDPs in Co-Cr made using four fabrication techniques, and to conclude in which area the largest misfit is present. An epoxy resin master model was produced. The impression was first made with silicone, and master and working models were then produced. A total of 32 three-unit Co-Cr FDPs were fabricated with four different production techniques: conventional lost-wax method (LW), milled wax with lost-wax method (MW), milled Co-Cr (MC), and direct laser metal sintering (DLMS). Each of the four groups consisted of eight FDPs (test groups). The FDPs were cemented on their cast and standardised-sectioned. The cement film thickness of the marginal and internal gaps was measured in a stereomicroscope, digital photos were taken at 12× magnification and then analyzed using measurement software. Statistical analyses were performed with one-way ANOVA and Tukey's test. Best fit based on the means (SDs) in μm for all measurement points was in the DLMS group 84 (60) followed by MW 117 (89), LW 133 (89) and MC 166 (135). Significant differences were present between MC and DLMS (p<0.05). The regression analyses presented differences within the parameters: production technique, tooth size, position and measurement point (p < 0.05). Best fit was found in the DLMS group followed by MW, LW and MC. In all four groups, best fit in both abutments was along the axial walls and in the deepest part of the chamfer preparation. The greatest misfit was present occlusally in all specimens. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Wear resistance of a pressable low-fusing ceramic opposed by dental alloys.

PubMed

Faria, Adriana Cláudia Lapria; de Oliveira, André Almeida; Alves Gomes, Érica; Silveira Rodrigues, Renata Cristina; Faria Ribeiro, Ricardo

2014-04-01

Dental alloys have increasingly replaced by dental ceramics in dentistry because of aesthetics. As both dental alloys and ceramics can be present in the oral cavity, the evaluation of the wear resistance of ceramics opposed by dental alloys is important. The aim of the present study was to evaluate wear resistance of a pressable low-fusing ceramic opposed by dental alloys as well as the microhardness of the alloys and the possible correlation of wear and antagonist microhardness. Fifteen stylus tips samples of pressable low-fusing ceramic were obtained, polished and glazed. Samples were divided into three groups according to the disk of alloy/metal to be used as antagonist: Nickel-Chromium (Ni-Cr), Cobalt-Chromium (Co-Cr) and commercially pure titanium (cp Ti). Vickers microhardness of antagonist disks was evaluated before wear tests. Then, antagonist disks were sandblasted until surface roughness was adjusted to 0.75μm. Wear tests were performed at a speed of 60 cycles/min and distance of 10mm, in a total of 300,000 cycles. Before and after wear tests, samples were weighted and had their profile designed in an optical comparator to evaluate weight and height loss, respectively. Ni-Cr and cp Ti caused greater wear than Co-Cr, presenting greater weight (p=.009) and height (p=.002) loss. Cp Ti microhardness was lower than Ni-Cr and Co-Cr (p<.05). There is a positive correlation between weight and height loss (p<.05), but weight (p=.204) and height (p=.05) loss are not correlated to microhardness. The results suggest that pressable low-fusing ceramic presents different wear according to the dental alloy used as antagonist and the wear is not affected by antagonist microhardness. Copyright © 2013 Elsevier Ltd. All rights reserved.

Misfit and microleakage of implant-supported crown copings obtained by laser sintering and casting techniques, luted with glass-ionomer, resin cements and acrylic/urethane-based agents.

PubMed

Castillo-Oyagüe, Raquel; Lynch, Christopher D; Turrión, Andrés S; López-Lozano, José F; Torres-Lagares, Daniel; Suárez-García, María-Jesús

2013-01-01

This study evaluated the marginal misfit and microleakage of cement-retained implant-supported crown copings. Single crown structures were constructed with: (1) laser-sintered Co-Cr (LS); (2) vacuum-cast Co-Cr (CC) and (3) vacuum-cast Ni-Cr-Ti (CN). Samples of each alloy group were randomly luted in standard fashion onto machined titanium abutments using: (1) GC Fuji PLUS (FP); (2) Clearfil Esthetic Cement (CEC); (3) RelyX Unicem 2 Automix (RXU) and (4) DentoTemp (DT) (n=15 each). After 60 days of water ageing, vertical discrepancy was SEM-measured and cement microleakage was scored using a digital microscope. Misfit data were subjected to two-way ANOVA and Student-Newman-Keuls multiple comparisons tests. Kruskal-Wallis and Dunn's tests were run for microleakage analysis (α=0.05). Regardless of the cement type, LS samples exhibited the best fit, whilst CC and CN performed equally well. Despite the framework alloy and manufacturing technique, FP and DT provide comparably better fit and greater microleakage scores than did CEC and RXU, which showed no differences. DMLS of Co-Cr may be a reliable alternative to the casting of base metal alloys to obtain well-fitted implant-supported crowns, although all the groups tested were within the clinically acceptable range of vertical discrepancy. No strong correlations were found between misfit and microleakage. Notwithstanding the framework alloy, definitive resin-modified glass-ionomer (FP) and temporary acrylic/urethane-based (DT) cements demonstrated comparably better marginal fit and greater microleakage scores than did 10-methacryloxydecyl-dihydrogen phosphate-based (CEC) and self-adhesive (RXU) dual-cure resin agents. Copyright © 2012 Elsevier Ltd. All rights reserved.

Bio-inspired Structural Colors from Deposition of Synthetic Melanin Nanoparticles by Evaporative Self-assembly

NASA Astrophysics Data System (ADS)

Xiao, Ming; Li, Yiwen; Deheyn, Dimitri; Yue, Xiujun; Gianneschi, Nathan; Shawkey, Matthew; Dhinojwala, Ali

2015-03-01

Melanin, a ubiquitous black or brown pigment in the animal kingdom, is a unique but poorly understood biomaterial. Many bird feathers contain melanosomes (melanin-containing organelles), which pack into ordered nanostructures, like multilayer or two-dimensional photonic crystal structures, to produce structural colors. To understand the optical properties of melanin and how melanosomes assemble into certain structures to produce colors, we prepared synthetic melanin (polydopamine) particles with variable sizes and aspect ratios. We have characterized the absorption and refractive index of the synthetic melanin particles. We have also shown that we can use an evaporative process to self-assemble melanin films with a wide range of colors. The colors obtained using this technique is modeled using a thin-film interference model and the optical properties of the synthetic melanin nanoparticles. Our results on self-assembly of synthetic melanin nanoparticles provide an explanation as why the use of melanosomes to produce colors is prevalent in the animal kingdom. National science foundation, air force office of scientific research, human frontier science program.

Metal thin-film optical polarizers for space applications, phase 2

NASA Technical Reports Server (NTRS)

Slocum, Robert E.

1991-01-01

A light polarizing material was developed for wavelengths in the visible and near infrared spectral band (400 to 3,000 nm). The material is comprised of ellipsoidal silver particles uniformly distributed and aligned on the surface of an optical material. A method is set forth for making polarizing material by evaporatively coating a smooth glass surface with ellipsoidal silver particles. The wavelength of peak absorption is chosen by selecting the aspect ratio of the ellipsoidal metal particles and the refractive index of the material surrounding the metal particles. The wavelength of peak absorption can be selected to fall at a desired wavelength in the range from 400 to 3,000 nm by control of the deposition process. This method is demonstrated by evaporative deposition of silver particles directly on to a smooth optical surface. By applying a multilayer silver coating of a glass disc, a contrast of greater than 40,000 was achieved at 590 nm. A polarizing filter was designed, fabricated, and assembled which achieved contrast of 100,00 at 59 nm and can serve as a replacement for crystal polarizers.

Reactive ion-beam-sputtering of fluoride coatings for the UV/VUV range

NASA Astrophysics Data System (ADS)

Schink, Harald; Kolbe, Jurgen; Zimmermann, F.; Ristau, Detlev; Welling, Herbert

1991-06-01

Fluoride coatings produced by thermal evaporation suffer from high scatter losses ageing and cracking due to high tensile stress. These problems impose severe limitations to the production of low loss multilayer coatings for the VUV range. A key position for improved performance is the microstructure of the layers. The aim of our investigations is to improve the microstructure of A1F3- and LaF3-'' films by ionbeamsputtering. Scatter measurements of single layers revealed lower values for lBS than for boat evaporation. Unfortunately sputtered fluoride films nave high absorption losses caused by decomposition of the coating material. By sputtering in reactive atmospheres and annealing we were able to reduce the absorption losses significantly. Antireflective as well as high reflective coatings were produced. Reflection and transmission values were obtained with a VUV-spectrophotometer. Damage tests at the 193 mu ArF laser wavelength were performed at the Laser-Laboratorium Gttingen. Key words: ion-beamsputtering fluoride films UVcoatings VUV-coatings color-center laser damage A]. F3 MgF2 LaF3. 1.

Poor short term outcome with a metal-on-metal total hip arthroplasty.

PubMed

Levy, Yadin D; Ezzet, Kace A

2013-08-01

Metal-on-metal (MoM) bearings for total hip arthroplasty (THA) have come under scrutiny with reports of high failure rates. Clinical outcome studies with several commercially available MoM THA bearings remain unreported. We evaluated 78 consecutive MoM THAs from a single manufacturer in 68 patients. Sixty-six received cobalt-chrome (CoCr) monoblock and 12 received modular titanium acetabular cups with internal CoCr liners. Femoral components were titanium with modular necks. At average 2.1 years postoperatively, 12 THAs (15.4%) demonstrated aseptic failure (10 revisions, 2 revision recommended). All revised hips demonstrated capsular necrosis with positive histology reaction for aseptic lymphocytic vasculitis-associated lesions/adverse local tissue reactions. Prosthetic instability following revision surgery was relatively common. Female gender was a strong risk factor for failure, though smaller cups were not. Both monoblock and modular components fared poorly. Corrosion was frequently observed around the proximal and distal end of the modular femoral necks. Copyright © 2013 Elsevier Inc. All rights reserved.

[Corrosion property and oxide film of dental casting alloys before and after porcelain firing].

PubMed

Ma, Qian; Wu, Feng-ming

2011-03-01

To evaluate the types and compositions of oxide films formed during porcelain-fused-to-metal (PFM) firing on three kinds of dental casting alloys, and to investigate the corrosion property of these alloys in Dulbecco's modification of Eagle's medium (DMEM) cell culture fluid, before and after PFM firing. Specimens of three dental casting alloys (Ni-Cr, Co-Cr and Ni-Ti) before and after PFM firing were prepared, and were immersed in DMEM cell culture fluid. After 30 days, the type and concentration of released metal ions were measured using inductively coupled plasma atomic emission spectroscopy (ICP-AES). X-ray photoelectron spectroscopy (XPS) and scanning electron microscope (SEM) were used for analysis of oxide film on the alloys. One way-ANOVA was adopted in data analysis. The total amount of metal ions released from the three dental alloys was found to be highest in Ni-Cr alloy [(2.829 ± 0.694) mg/L], followed by Co-Cr [(2.120 ± 0.418) mg/L] and Ni-Ti alloy [(1.211 ± 0.101) mg/L]. The amount of Ni ions released from Ni-Cr alloys [(1.531 ± 0.392) mg/L] was higher than that from Ni-Ti alloys [(0.830 ± 0.052) mg/L]. The amount of Cr, Mo ions released from Co-Cr alloy [Cr: (0.048 ± 0.011) mg/L, Mo: (1.562 ± 0.333) mg/L] was higher than that from Ni-Cr alloy [Cr: (0.034 ± 0.002) mg/L, Mo: (1.264 ± 0.302) mg/L] and Ni-Ti alloy [Cr: (0.013 ± 0.006) mg/L, Mo: (0.151 ± 0.026) mg/L] (P < 0.05). After PFM firing, the total amount of metal irons released from the three dental alloys decreased [Ni-Cr: (0.861 ± 0.054) mg/L, Co-Cr: (0.695 ± 0.327) mg/L, Ni-Ti: (0.892 ± 0.115) mg/L] (P < 0.05). In addition, XPS showed increase of Cr(2)O(3) and Mo-Ni oxide on the surface of all the alloys after PFM firing. The amount of ions released from Ni-Cr alloy was the highest among the three dental casting alloys, this means Ni-Cr alloy is prone to corrode. The PFM firing process changed the alloys' surface composition. Increased Ni, Cr and Mo were found in oxide film, and the increase in Cr(2)O(3) can improve the corrosion-resistance of alloys.

Depth distribution of secondary phases in kesterite Cu 2ZnSnS 4 by angle-resolved X-ray absorption spectroscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Just, J.; Lützenkirchen-Hecht, D.; Müller, O.

The depth distribution of secondary phases in the solar cell absorber material Cu 2ZnSnS 4 (CZTS) is quantitatively investigated using X-ray Absorption Near Edge Structure (XANES) analysis at the K-edge of sulfur at varying incidence angles. Varying information depths from several nanometers up to the full thickness is achieved. A quantitative profile of the phase distribution is obtained by a self-consistent fit of a multilayer model to the XANES spectra for different angles. Single step co-evaporated CZTS thin-films are found to exhibit zinc and copper sulfide secondary phases preferentially at the front or back interfaces of the film.

Depth distribution of secondary phases in kesterite Cu 2ZnSnS 4 by angle-resolved X-ray absorption spectroscopy

DOE PAGES

Just, J.; Lützenkirchen-Hecht, D.; Müller, O.; ...

2017-12-12

The depth distribution of secondary phases in the solar cell absorber material Cu 2ZnSnS 4 (CZTS) is quantitatively investigated using X-ray Absorption Near Edge Structure (XANES) analysis at the K-edge of sulfur at varying incidence angles. Varying information depths from several nanometers up to the full thickness is achieved. A quantitative profile of the phase distribution is obtained by a self-consistent fit of a multilayer model to the XANES spectra for different angles. Single step co-evaporated CZTS thin-films are found to exhibit zinc and copper sulfide secondary phases preferentially at the front or back interfaces of the film.

Hybrid organic–inorganic porous semiconductor transducer for multi-parameters sensing

PubMed Central

Caliò, Alessandro; Cassinese, Antonio; Casalino, Maurizio; Rea, Ilaria; Barra, Mario; Chiarella, Fabio; De Stefano, Luca

2015-01-01

Porous silicon (PSi) non-symmetric multi-layers are modified by organic molecular beam deposition of an organic semiconductor, namely the N,N′-1H,1H-perfluorobutyldicyanoperylene-carboxydi-imide (PDIF-CN2). Joule evaporation of PDIF-CN2 into the PSi sponge-like matrix not only improves but also adds transducing skills, making this solid-state device a dual signal sensor for chemical monitoring. PDIF-CN2 modified PSi optical microcavities show an increase of about five orders of magnitude in electric current with respect to the same bare device. This feature can be used to sense volatile substances. PDIF-CN2 also improves chemical resistance of PSi against alkaline and acid corrosion. PMID:26063814

Solution Coating of Pharmaceutical Nanothin Films and Multilayer Nanocomposites with Controlled Morphology and Polymorphism.

PubMed

Horstman, Elizabeth M; Kafle, Prapti; Zhang, Fengjiao; Zhang, Yifu; Kenis, Paul J A; Diao, Ying

2018-03-28

Nanosizing is rapidly emerging as an alternative approach to enhance solubility and thus the bioavailability of poorly aqueous soluble active pharmaceutical ingredients (APIs). Although numerous techniques have been developed to perform nanosizing of API crystals, precise control and modulation of their size in an energy and material efficient manner remains challenging. In this study, we present meniscus-guided solution coating as a new technique to produce pharmaceutical thin films of nanoscale thickness with controlled morphology. We demonstrate control of aspirin film thickness over more than 2 orders of magnitude, from 30 nm to 1.5 μm. By varying simple process parameters such as the coating speed and the solution concentration, the aspirin film morphology can also be modulated by accessing different coating regimes, namely the evaporation regime and the Landau-Levich regime. Using ellipticine-a poorly water-soluble anticancer drug-as another model compound, we discovered a new polymorph kinetically trapped during solution coating. Furthermore, the polymorphic outcome can be controlled by varying coating conditions. We further performed layer-by-layer coating of multilayer nanocomposites, with alternating thin films of ellipticine and a biocompatible polymer, which demonstrate the potential of additive manufacturing of multidrug-personalized dosage forms using this approach.

Work function measurement of multilayer electrodes using Kelvin probe force microscopy

NASA Astrophysics Data System (ADS)

Peres, L.; Bou, A.; Cornille, C.; Barakel, D.; Torchio, P.

2017-04-01

The workfunction of dielectric|metal|dielectric transparent and conductive electrodes, promising candidates for replacing ITO in thin film solar cells, is measured by Kelvin probe force microscopy (KPFM). Measurement on commercial ITO gives a workfunction of 4.74 eV, which is in agreement with the values reported in the literature. Measurements are then performed on optically optimised multilayer electrodes fabricated on glass by e-beam evaporation, using three different dielectrics. For TiO2(37 nm)|Ag(13 nm)|TiO2(42 nm), SnO x (45 nm)|Ag(10 nm)|SnO x (45 nm), and ZnS(47 nm)|Ag(12 nm)|ZnS(42 nm), workfunctions of 4.83 eV, 4.75 eV, and 4.48 eV are measured respectively. These values suggest that these transparent and conductive electrodes are well adapted to extract photo-generated charge carriers in photovoltaic devices in which ITO is normally used. Furthermore, the KPFM technique proves to be an efficient and relatively fast way to determine the work function values of such electrodes.

Biophysical characterization of monofilm model systems composed of selected tear film phospholipids.

PubMed

Patterson, Matthew; Vogel, Hans J; Prenner, Elmar J

2016-02-01

The tear film protects the eye from foreign particles and pathogens, prevents excess evaporation, provides lubrication, and maintains a high quality optical surface necessary for vision. The anterior layer of tear film consists of polar and non-polar lipid layers. The polar lipids form a monolayer on the aqueous subphase, acting as surfactants for the non-polar lipid multilayer. A tear film polar lipid biomimetic consisting of dipalmitoyl phosphatidylcholine (DPPC), dipalmitoyl phosphatidylethanolamine (DPPE), palmitoyl glucosylceramide (PGC), and palmitoyl sphingomyelin (PSM) was characterized using Langmuir monolayers and Brewster angle microscopy (BAM). Lipid combinations formed very stable monolayers, especially those containing DPPC or PSM. Surface experiments and elasticity analyses revealed that PGC resulted in more condensed and rigid mixed monolayers. DPPE provided resistance to large changes in lipid ordering over a wide surface pressure range. Ternary mixtures containing DPPE and PGC with either DPPC or PSM experienced the greatest lipid ordering within the natural tear film surface pressure range suggesting that these lipids are important to maintain tear film integrity during the inter-blink period. Finally, BAM images revealed unique structures within monolayers of DPPC, DPPE, and PGC at the natural tear film surface pressure. 3D analysis of these domains suggested either the formation of multilayers or outward protrusions at surface pressures far below the point of irreversible collapse as seen on the isotherm. This entails that the polar lipids of tear film may be capable of multilayer formation or outward folding as a mechanism to prevent rupture of the tear film during a blink. Copyright © 2015 Elsevier B.V. All rights reserved.

Smooth e-beam-deposited tin-doped indium oxide for III-nitride vertical-cavity surface-emitting laser intracavity contacts

NASA Astrophysics Data System (ADS)

Leonard, J. T.; Cohen, D. A.; Yonkee, B. P.; Farrell, R. M.; DenBaars, S. P.; Speck, J. S.; Nakamura, S.

2015-10-01

We carried out a series of simulations analyzing the dependence of mirror reflectance, threshold current density, and differential efficiency on the scattering loss caused by the roughness of tin-doped indium oxide (ITO) intracavity contacts for 405 nm flip-chip III-nitride vertical-cavity surface-emitting lasers (VCSELs). From these results, we determined that the ITO root-mean-square (RMS) roughness should be <1 nm to minimize scattering losses in VCSELs. Motivated by this requirement, we investigated the surface morphology and optoelectronic properties of electron-beam (e-beam) evaporated ITO films, as a function of substrate temperature and oxygen flow and pressure. The transparency and conductivity were seen to increase with increasing temperature. Decreasing the oxygen flow and pressure resulted in an increase in the transparency and resistivity. Neither the temperature, nor oxygen flow and pressure series on single-layer ITO films resulted in highly transparent and conductive films with <1 nm RMS roughness. To achieve <1 nm RMS roughness with good optoelectronic properties, a multi-layer ITO film was developed, utilizing a two-step temperature scheme. The optimized multi-layer ITO films had an RMS roughness of <1 nm, along with a high transparency (˜90% at 405 nm) and low resistivity (˜2 × 10-4 Ω-cm). This multi-layer ITO e-beam deposition technique is expected to prevent p-GaN plasma damage, typically observed in sputtered ITO films on p-GaN, while simultaneously reducing the threshold current density and increasing the differential efficiency of III-nitride VCSELs.

Microscopical analysis of synovial fluid wear debris from failing CoCr hip prostheses

NASA Astrophysics Data System (ADS)

Ward, M. B.; Brown, A. P.; Cox, A.; Curry, A.; Denton, J.

2010-07-01

Metal on metal hip joint prostheses are now commonly implanted in patients with hip problems. Although hip replacements largely go ahead problem free, some complications can arise such as infection immediately after surgery and aseptic necrosis caused by vascular complications due to surgery. A recent observation that has been made at Manchester is that some Cobalt Chromium (CoCr) implants are causing chronic pain, with the source being as yet unidentified. This form of replacement failure is independent of surgeon or hospital and so some underlying body/implant interface process is thought to be the problem. When the synovial fluid from a failed joint is examined particles of metal (wear debris) can be found. Transmission Electron Microscopy (TEM) has been used to look at fixed and sectioned samples of the synovial fluid and this has identified fine (< 100 nm) metal and metal oxide particles within the fluid. TEM EDX and Electron Energy Loss Spectroscopy (EELS) have been employed to examine the composition of the particles, showing them to be chromium rich. This gives rise to concern that the failure mechanism may be associated with the debris.

Mechanical strength of laser-welded cobalt-chromium alloy.

PubMed

Baba, N; Watanabe, I; Liu, J; Atsuta, M

2004-05-15

The purpose of this study was to investigate the effect of the output energy of laser welding and welding methods on the joint strength of cobalt-chromium (Co-Cr) alloy. Two types of cast Co-Cr plates were prepared, and transverse sections were made at the center of the plate. The cut surfaces were butted against one another, and the joints welded with a laser-welding machine at several levels of output energy with the use of two methods. The fracture force required to break specimens was determined by means of tensile testing. For the 0.5-mm-thick specimens, the force required to break the 0.5-mm laser-welded specimens at currents of 270 and 300 A was not statistically different (p > 0.05) from the results for the nonwelded control specimens. The force required to break the 1.0-mm specimens double-welded at a current of 270 A was the highest value among the 1.0-mm laser-welded specimens. The results suggested that laser welding under the appropriate conditions improved the joint strength of cobalt- chromium alloy. Copyright 2004 Wiley Periodicals, Inc.

Quarterly Technical Progress Report - Investigation of Syngas Interaction in Alcohol Synthesis Catalysts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Murty A. Akundi

This report presents the work done on " Investigation of Syngas Interaction in Alcohol Synthesis Catalysts" during the last quarter. The major activity during this period is on FTIR absorption studies of Co/Cr catalysts using CO as a probe molecule. Transition metals cobalt and copper play significant roles in the conversion of syngas (CO + H2 ) to liquid fuels. With a view to examine the nature of interaction between CO and metal, the FTIR spectra of CO adsorbed on Co-Cr2 O3 composites were investigated. The results indicate that as cobalt loading increases, the intensity of the CO adsorption bandsmore » increase and several vibrational modes seem to be promoted. Heat treatment of the sample revealed two distinct processes of adsorption. Bands due to physisorption disappeared while bands due to chemisorption not only increased in intensity but persisted even after desorption. It seems that the physisorption process is more active when the catalyst is fresh and is hindered when carbidic/carbonyl formations occur on the metal surfaces.« less

Oral rehabilitation of a patient with amelogenesis imperfecta using removable overlay denture: a clinical report.

PubMed

Ghodsi, S; Rasaeipour, S; Vojdani, M

2012-03-01

The aim of this study was oral rehabilitation of 17-year old patient with amelogenesis imperfecta using removable overlay denture in order to satisfy her esthetic and functional expectations and enhance her self-image. Amelogenesis imperfecta (AI) is a group of genetic disorders that primarily affect the quality and quantity of amelogenesis in both primary and permanent dentitions. The main clinical characteristics are severe attrition, tooth sensitivity and unesthetic appearance. This clinical report illustrates the oral rehabilitation of a 17-year-old girl with hypoplastic-hypomature type of AI with cobalt-chromium (Co-Cr) overlay removable partial denture (ORPD) that is one of the most economical and biocompatible replacements for noble metal and nickel-chromium (Ni-Cr) alloy. The presented case report suggests that Co-Cr ORPD can be a good temporary or even permanent treatment option for AI patients with limited budget, low esthetic concerns or medical limitations. There are major advantages in cast metal ORPDs; they are simpler, less traumatic and less expensive than fixed prosthetic options. This case report supports their use in patients with amelogenesis imperfecta.

Temperature Dependent Electrical Transport Properties of Ni-Cr and Co-Cr Binary Alloys

NASA Astrophysics Data System (ADS)

Thakore, B. Y.; Suthar, P. H.; Khambholja, S. G.; Gajjar, P. N.; Bhatt, N. K.; Jani, A. R.

2011-12-01

The temperature dependent electrical transport properties viz. electrical resistivity and thermal conductivity of Ni10Cr90 and Co20Cr80 alloys are computed at various temperatures. The electrical resistivity has been calculated according to Faber-Ziman model combined with Ashcroft-Langreth partial structure factors. In the present work, to include the ion-electron interaction, we have used a well tested local model potential. For exchange-correlation effects, five different forms of local field correction functions due to Hartree (H), Taylor (T), Ichimaru and Utsumi (IU), Farid et al (F) and Sarkar et al (S) are used. The present results due to S function are in good agreement with the experimental data as compared to results obtained using other four functions. The S functions satisfy compressibility sum rule in long wave length limit more accurately as compared to T, IU and F functions, which may be responsible for better agreement of results, obtained using S function. Also, present result confirms the validity of present approach in determining the transport properties of alloys like Ni-Cr and Co-Cr.

Simulation and optimization of a pulsating heat pipe using artificial neural network and genetic algorithm

NASA Astrophysics Data System (ADS)

Jokar, Ali; Godarzi, Ali Abbasi; Saber, Mohammad; Shafii, Mohammad Behshad

2016-11-01

In this paper, a novel approach has been presented to simulate and optimize the pulsating heat pipes (PHPs). The used pulsating heat pipe setup was designed and constructed for this study. Due to the lack of a general mathematical model for exact analysis of the PHPs, a method has been applied for simulation and optimization using the natural algorithms. In this way, the simulator consists of a kind of multilayer perceptron neural network, which is trained by experimental results obtained from our PHP setup. The results show that the complex behavior of PHPs can be successfully described by the non-linear structure of this simulator. The input variables of the neural network are input heat flux to evaporator (q″), filling ratio (FR) and inclined angle (IA) and its output is thermal resistance of PHP. Finally, based upon the simulation results and considering the heat pipe's operating constraints, the optimum operating point of the system is obtained by using genetic algorithm (GA). The experimental results show that the optimum FR (38.25 %), input heat flux to evaporator (39.93 W) and IA (55°) that obtained from GA are acceptable.

Non-destructive three-dimensional evaluation of pores at different welded joints and their effects on joints strength.

PubMed

Nomoto, Rie; Takayama, Yasuko; Tsuchida, Fujio; Nakajima, Hiroyuki

2010-12-01

The purpose of this study was to measure the porosity in different laser welded cast alloys non-destructively using X-ray micro-focus computerized tomography (micro-CT) and to evaluate the effect of porosity on the tensile strength of the welded joints. The welding procedure was conducted in rectangular cast metals, CoCr, Ti and platinum added gold alloy (AuPt). The metal plates were butted CoCr to CoCr (CoCr/CoCr) or Ti to Ti (Ti/Ti) for welding of similar metals and Ti to AuPt (Ti/AuPt) for welding of dissimilar metals. Specimens were welded under several laser-welding conditions; with groove (normal), without groove (no groove), spatter, crack, or no overlapped welding (no overlap) (n=5). Porosity in the welded area was evaluated using a micro-CT. Tensile strength of the welded specimens was measured at a crosshead speed of 1mm/min. Multiple comparisons of the group means were performed using ANOVA and Fisher's multiple comparisons test (α=.05). The relationship between the porosity and the tensile strength was investigated with a regression analysis. Three-dimensional images of Ti/AuPt could not be obtained due to metal artifacts and the tensile specimens of Ti/AuPt were debonded prior to the tensile test. All other welded specimens had porosity in the welded area and the porosities ranged from 0.01% to 0.17%. The fractures of most of the CoCr/CoCr and Ti/Ti specimens occurred in the parent metals. Joint strength had no relationship with the porosity in the welded area (R(2)=0.148 for CoCr/CoCr, R(2)=0.088 for Ti/Ti, respectively). The small amount of porosity caused by the laser-welding procedures did not affect the joint strength. The joint strength of Ti/AuPt was too weak to be used clinically. Copyright © 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Development of a discriminatory biocompatibility testing model for non-precious dental casting alloys.

PubMed

McGinley, Emma Louise; Fleming, Garry J P; Moran, Gary P

2011-12-01

To develop an enhanced, reproducible and discriminatory biocompatibility testing model for non-precious dental casting alloys, prepared to a clinically relevant surface finishing condition, using TR146 oral keratinocyte cells. Comparative biocompatibility was determined following direct and indirect exposure of TR146 cells to two nickel-chromium (Ni-Cr) and a cobalt-chromium (Co-Cr) alloy-discs. The surface roughness of the discs was determined using a contact stylus profilometer and the elemental ion release by inductively coupled plasma mass spectrometry (ICP-MS). Subsequent biocompatibility analysis included cell morphology, cell density measurements with Trypan blue exclusion assay, inflammatory cytokine expression with ELISAs, cellular metabolic activity using XTT and cellular toxicity using lactate dehydrogenase (LDH) release assay. TR146 cell morphology was altered following direct and indirect exposure to the Ni-Cr alloys but not the Co-Cr alloy. Significant reductions (all P<0.001) in viable cell density measurements, cellular metabolic activity, significant increases inflammatory cytokine expression and cellular toxicity were observed when TR146 cells were exposed to the Ni-Cr alloys. Significant decreases in cell density measurements, cellular metabolic activity, significant increases inflammatory cytokine expression and cellular toxicity for the Ni-Cr d.Sign(®)15 alloy compared with d.Sign(®)10 alloy were identifiable (all P<0.001). Cellular toxicity was attributed to nickel ion release levels in solution detected by ICP-MS analysis. Nickel ions from the Ni-Cr alloys permeated the epithelial cells and activated a proinflammatory response, namely IL-1a, IL-8 and PGE2 expression. Further evidence of nickel ioninduced cell death was supported by the decreased biocompatibility of the highest nickel ion releasing alloy (d.Sign(®)15 compared with d.Sign(®)10) and the increased biocompatibility of the Co-Cr (d.Sign(®)30) alloy where nickel ions were absent. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Size-dependent magnetic transitions in CoFe0.1Cr1.9O4 nanoparticles studied by magnetic and neutron-polarization analysis.

PubMed

Kumar, D; Galivarapu, J K; Banerjee, A; Nemkovski, K S; Su, Y; Rath, Chandana

2016-04-29

Multiferroic, CoCr2O4 bulk material undergoes successive magnetic transitions such as a paramagnetic to collinear and non-collinear ferrimagnetic state at the Curie temperature (TC) and spiral ordering temperature (TS) respectively and finally to a lock-in-transition temperature (Tl). In this paper, the rich sequence of magnetic transitions in CoCr2O4 after mixing the octahedral site with 10% of iron are investigated by varying the size of the particle from 10 to 50 nm. With the increasing size, while the TC increases from 110 to 119 K which is higher than the TC (95 K) of pure CoCr2O4, the TS remains unaffected. In addition, a compensation of magnetization at 34 K and a lock-in transition at 10 K are also monitored in 50 nm particles. Further, we have examined the magnetic-ordering temperatures through neutron scattering using a polarized neutron beam along three orthogonal directions after separating the magnetic scattering from nuclear-coherent and spin-incoherent contributions. While a sharp long-range ferrimagnetic ordering down to 110 K and a short-range spiral ordering down to 50 K are obtained in 50 nm particles, in 10 nm particles, the para to ferrimagnetic transition is found to be continuous and spiral ordering is diffused in nature. Frequency-dependent ac susceptibility (χ) data fitted with different phenomenological models such as the Neel-Arrhenius, Vogel-Fulcher and power law, while ruling out the canonical spin-glass, cluster-glass and interacting superparamagnetism, reveal that both particles show spin-glass behavior with a higher relaxation time in 10 nm particles than in 50 nm. The smaller spin flip time in 50 nm particles confirms that spin dynamics does not slow down on approaching the glass transition temperature (Tg).

Biomechanical evaluation of a spherical lumbar interbody device at varying levels of subsidence.

PubMed

Rundell, Steven A; Isaza, Jorge E; Kurtz, Steven M

2011-01-01

Ulf Fernström implanted stainless steel ball bearings following discectomy, or for painful disc disease, and termed this procedure disc arthroplasty. Today, spherical interbody spacers are clinically available, but there is a paucity of associated biomechanical testing. The primary objective of the current study was to evaluate the biomechanics of a spherical interbody implant. It was hypothesized that implantation of a spherical interbody implant, with combined subsidence into the vertebral bodies, would result in similar ranges of motion (RoM) and facet contact forces (FCFs) when compared with an intact condition. A secondary objective of this study was to determine the effect of using a polyetheretherketone (PEEK) versus a cobalt chrome (CoCr) implant on vertebral body strains. We hypothesized that the material selection would have a negligible effect on vertebral body strains since both materials have elastic moduli substantially greater than the annulus. A finite element model of L3-L4 was created and validated by use of ROM, disc pressure, and bony strain from previously published data. Virtual implantation of a spherical interbody device was performed with 0, 2, and 4 mm of subsidence. The model was exercised in compression, flexion, extension, axial rotation, and lateral bending. The ROM, vertebral body effective (von Mises) strain, and FCFs were reported. Implantation of a PEEK implant resulted in slightly lower strain maxima when compared with a CoCr implant. For both materials, the peak strain experienced by the underlying bone was reduced with increasing subsidence. All levels of subsidence resulted in ROM and FCFs similar to the intact model. The results suggest that a simple spherical implant design is able to maintain segmental ROM and provide minimal differences in FCFs. Large areas of von Mises strain maxima were generated in the bone adjacent to the implant regardless of whether the implant was PEEK or CoCr.

Vertical misfit of laser-sintered and vacuum-cast implant-supported crown copings luted with definitive and temporary luting agents.

PubMed

Castillo-de-Oyagüe, Raquel; Sánchez-Turrión, Andrés; López-Lozano, José-Francisco; Albaladejo, Alberto; Torres-Lagares, Daniel; Montero, Javier; Suárez-García, Maria-Jesús

2012-07-01

This study aimed to evaluate the vertical discrepancy of implant-supported crown structures constructed with vacuum-casting and Direct Metal Laser Sintering (DMLS) technologies, and luted with different cement types. Crown copings were fabricated using: (1) direct metal laser sintered Co-Cr (LS); (2) vacuum-cast Co-Cr (CC); and (3) vacuum-cast Ti (CT). Frameworks were luted onto machined implant abutments under constant seating pressure. Each alloy group was randomly divided into 5 subgroups (n = 10 each) according to the cement system utilized: Subgroup 1 (KC) used resin-modified glass-ionomer Ketac Cem Plus; Subgroup 2 (PF) used Panavia F 2.0 dual-cure resin cement; Subgroup 3 (RXU) used RelyX Unicem 2 Automix self-adhesive dual-cure resin cement; Subgroup 4 (PIC) used acrylic/urethane-based temporary Premier Implant Cement; and Subgroup 5 (DT) used acrylic/urethane-based temporary DentoTemp cement. Vertical misfit was measured by scanning electron microscopy (SEM). Two-way ANOVA and Student-Newman-Keuls tests were run to investigate the effect of alloy/fabrication technique, and cement type on vertical misfit. The statistical significance was set at α = 0.05. The alloy/manufacturing technique and the luting cement affected the vertical discrepancy (p < 0.001). For each cement type, LS samples exhibited the best fit (p < 0.01) whereas CC and CT frames were statistically similar. Within each alloy group, PF and RXU provided comparably greater discrepancies than KC, PIC, and DT, which showed no differences. Laser sintering may be an alternative to vacuum-casting of base metals to obtain passive-fitting implant-supported crown copings. The best marginal adaptation corresponded to laser sintered structures luted with glass-ionomer KC, or temporary PIC or DT cements. The highest discrepancies were recorded for Co-Cr and Ti cast frameworks bonded with PF or RXU resinous agents. All groups were within the clinically acceptable misfit range.

Center for dielectric studies

NASA Astrophysics Data System (ADS)

Cross, L. E.; Newnham, R. E.; Biggers, J. V.

1984-05-01

This report focuses upon the parts of the Center program which have drawn most extensively upon Navy funds. In the basic study of polarization processes in high K dielectrics, major progress has been made in understanding the mechanisms in relaxor ferroelectric in the perovskite structure families. A new effort is also being mounted to obtain more precise evaluation of the internal stress effects in fine grained barium titanate. Related to reliability, studies of the effects of induced macro-defects are described, and preparation for the evaluation of space charge by internal potential distribution measurements discussed. To develop new processing methods for very thin dielectric layers, a new type of single barrier layer multilayer is discussed, and work on the thermal evaporation of oriented crystalline antimony sulphur iodide describe.

The properties of RE-TM magneto-optical films

NASA Astrophysics Data System (ADS)

Lee, Z. Y.; Miao, X. S.; Zhu, P.; Hu, Y. S.; Wan, D. F.; Dai, D. W.; Chen, S. B.; Lin, G. Q.

1992-09-01

In this paper, the magnetic, magneto-optical and galvonomagnetic properties, and their temperature dependence for LRE-TM SmCo, SmCoDy and HRE-TM TbFeCo magneto-optical films as high density recording media prepared by rf magnetron sputtering or evaporation are reported. By adding Dy to SmCo thin film, the SmCoDy thin film is more suitable for magneto-optical recording, its domain size being below 0.63 μm. The Kerr enhancement and corrosion protective effects of AIN and AlSiN for optimum design of the multi-layer structure of magneto-optical disk are described. The instruments of measuring the magneto-optical Kerr effect and magneto-optical recording domain characteristics of thin films are reviewed.

Maple prepared organic heterostructures for photovoltaic applications

NASA Astrophysics Data System (ADS)

Stanculescu, A.; Socol, M.; Socol, G.; Mihailescu, I. N.; Girtan, M.; Stanculescu, F.

2011-09-01

In this study, we present the deposition of ZnPc, Alq3, and PTCDA thin films using Matrix Assisted Pulsed Laser Evaporation (MAPLE) technique. We also report the realisation of multilayer structures, made by the successive application of MAPLE. The films have been characterized by spectroscopic (UV-VIS and Photoluminescence) and microscopic (SEM and AFM) methods, and the effect of different deposition conditions such as fluence, number of pulses, and target concentration on the properties has been analysed. This paper also presents some investigations on the electrical conduction in sandwich type structures ITO or Si/organic layer/Au or Cu and ITO/double organic layer/Cu, emphasising the dominant effect of the height of the energetic barriers at the inorganic/organic and organic/organic interfaces.

Computational method for determining n and k for a thin film from the measured reflectance, transmittance, and film thickness.

PubMed

Bennett, J M; Booty, M J

1966-01-01

A computational method of determining n and k for an evaporated film from the measured reflectance, transmittance, and film thickness has been programmed for an IBM 7094 computer. The method consists of modifications to the NOTS multilayer film program. The basic program computes normal incidence reflectance, transmittance, phase change on reflection, and other parameters from the optical constants and thicknesses of all materials. In the modification, n and k for the film are varied in a prescribed manner, and the computer picks from among these values one n and one k which yield reflectance and transmittance values almost equalling the measured values. Results are given for films of silicon and aluminum.

77 FR 60704 - Medical Devices; Availability of Safety and Effectiveness Summaries for Premarket Approval...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-10-04

...] Fenestrated April 4, 2012. AAA Endovascular Graft (with the adjunctive Zenith Alignment Stent). P110029, FDA...\\ plus CoCr April 12, 2012. Coronary Stent on RX System. P110035, FDA-2012-M-0373 Boston Scientific Epic\\TM\\ Vascular Self- April 13, 2012. Corp. Expanding Stent System. P090015, FDA-2012-M-0390 Leica...

Sequentially evaporated thin Y-Ba-Co-O superconducting films on microwave substrates

NASA Technical Reports Server (NTRS)

Valco, G. J.; Rohrer, N. J.; Warner, J. D.; Bhasin, K. B.

1989-01-01

The development of high T sub c superconducting thin films on various microwave substrates is of major interest in space electronic systems. Thin films of YBa2Cu3O(7-Delta) were formed on SrTiO3, MgO, ZrO2 coated Al2O3, and LaAlO3 substrates by multi-layer sequential evaporation and subsequent annealing in oxygen. The technique allows controlled deposition of Cu, BaF2 and Y layers, as well as the ZrO buffer layers, to achieve reproducibility for microwave circuit fabrication. The three layer structure of Cu/BaF2/Y is repeated a minimum of four times. The films were annealed in an ambient of oxygen bubbled through water at temperatures between 850 C and 900 C followed by slow cooling (-2 C/minute) to 450 C, a low temperature anneal, and slow cooling to room temperature. Annealing times ranged from 15 minutes to 5 hrs. at high temperature and 0 to 6 hr. at 450 C. Silver contacts for four probe electrical measurements were formed by evaporation followed with an anneal at 500 C. The films were characterized by resistance-temperature measurements, energy dispersive X-ray spectroscopy, X-ray diffraction, and scanning electron microscopy. Critical transition temperatures ranged from 30 K to 87 K as a function of the substrate, composition of the film, thicknesses of the layers, and annealing conditions. Microwave ring resonator circuits were also patterned on these MgO and LaAlO3 substrates.

Next-generation all-silica coatings for UV applications

NASA Astrophysics Data System (ADS)

Melninkaitis, A.; Grinevičiūtė, L.; Abromavičius, G.; Mažulė, L.; Smalakys, L.; Pupka, E.; Š čiuka, M.; Buzelis, R.; Kičas, S.

2017-11-01

Band-gap and refractive index are known as fundamental properties determining intrinsic optical resistance of multilayer dielectric coatings. By considering this fact we propose novel approach to manufacturing of interference thin films, based on artificial nano-structures of modulated porosity embedded in high band-gap matrix. Next generation all-silica mirrors were prepared by GLancing Angle Deposition (GLAD) using electron beam evaporation. High reflectivity (HR) was achieved by tailoring the porosity of highly resistant silica material during the thin film deposition process. Furthermore, the proposed approach was also demonstrated to work well in case of anti-reflection (AR) coatings. Conventional HR HfO2 and SiO2 as well as AR Al2O3 and SiO2 multilayers produced by Ion Beam Sputtering (IBS) were used as reference coatings. Damage performance of experimental coatings was also analyzed. All-silica based GLAD approach resulted in significant improvement of intrinsic laser damage resistance properties if compared to conventional coatings. Besides laser damage testing, other characteristics of experimental coatings are analyzed and discussed - reflectance, surface roughness and optical scattering. We believe that reported concept can be expanded to virtually any design of thin film coatings thus opening a new way of next generation highly resistant thin films well suited for high power and UV laser applications.

CAD-FEA modeling and analysis of different full crown monolithic restorations.

PubMed

Dal Piva, Amanda Maria de Oliveira; Tribst, João Paulo Mendes; Borges, Alexandre Luiz Souto; Souza, Rodrigo Othávio de Assunção E; Bottino, Marco Antonio

2018-06-19

To investigate the influence of different materials for monolithic full posterior crowns using 3D-Finite Element Analysis (FEA). Twelve (12) 3D models of adhesively-restored teeth with different crowns according to the material and its elastic modulus were analysed: Acrylic resin, Polyetheretherketone, Composite resin, Hybrid ceramic, pressable and machinable Zirconia reinforced lithium silicate, Feldspathic, Lithium disilicate, Gold alloy, Cobalt-Chromium alloy (Co-Cr), Zirconia tetragonal partially stabilized with yttria, and Alumina. All materials were assumed to behave elastically throughout the entire deformation. Results in restoration and cementing line were obtained using maximum principal stress. In addition, maximum shear stress criteria was used for the cementing line. Restorative materials with higher elastic modulus present higher stress concentration inside the crown, mainly tensile stress on an intaglio surface. On the other hand, materials with lower elastic modulus allow stress passage for cement, increasing shear stress on this layer. Stiffer materials promote higher stress peak values. Materials with higher elastic modulus such as Co-Cr, zirconia and alumina enable higher tensile stress concentration on the crown intaglio surface and higher shear stress on the cement layer, facilitating crown debonding. Copyright © 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.

Stress distribution in Co-Cr implant frameworks after laser or TIG welding.

PubMed

de Castro, Gabriela Cassaro; de Araújo, Cleudmar Amaral; Mesquita, Marcelo Ferraz; Consani, Rafael Leonardo Xediek; Nóbilo, Mauro Antônio de Arruda

2013-01-01

Lack of passivity has been associated with biomechanical problems in implant-supported prosthesis. The aim of this study was to evaluate the passivity of three techniques to fabricate an implant framework from a Co-Cr alloy by photoelasticity. The model was obtained from a steel die simulating an edentulous mandible with 4 external hexagon analog implants with a standard platform. On this model, five frameworks were fabricated for each group: a monoblock framework (control), laser and TIG welding frameworks. The photoelastic model was made from a flexible epoxy resin. On the photoelastic analysis, the frameworks were bolted onto the model for the verification of maximum shear stress at 34 selected points around the implants and 5 points in the middle of the model. The stresses were compared all over the photoelastic model, between the right, left, and center regions and between the cervical and apical regions. The values were subjected to two-way ANOVA, and Tukey's test (α=0.05). There was no significant difference among the groups and studied areas (p>0.05). It was concluded that the stresses generated around the implants were similar for all techniques.

[Comparative adaptation of crowns of selective laser melting and wax-lost-casting method].

PubMed

Li, Guo-qiang; Shen, Qing-yi; Gao, Jian-hua; Wu, Xue-ying; Chen, Li; Dai, Wen-an

2012-07-01

To investigate the marginal adaptation of crowns fabricated by selective laser melting (SLM) and wax-lost-casting method, so as to provide an experimental basis for clinic. Co-Cr alloy full crown were fabricated by SLM and wax-lost-casting for 24 samples in each group. All crowns were cemented with zinc phosphate cement and cut along longitudinal axis by line cutting machine. The gap between crown tissue surface and die was measured by 6-point measuring method with scanning electron microscope (SEM). The marginal adaptation of crowns fabricated by SLM and wax-lost-casting were compared statistically. The gap between SLM crowns were (36.51 ± 2.94), (49.36 ± 3.31), (56.48 ± 3.35), (42.20 ± 3.60) µm, and wax-lost-casting crowns were (68.86 ± 5.41), (58.86 ± 6.10), (70.62 ± 5.79), (69.90 ± 6.00) µm. There were significant difference between two groups (P < 0.05). Co-Cr alloy full crown fabricated by wax-lost-casting method and SLM method provide acceptable marginal adaptation in clinic, and the marginal adaptation of SLM is better than that of wax-lost-casting method.

A patterned microtexture to reduce friction and increase longevity of prosthetic hip joints

PubMed Central

Chyr, Anthony; Qiu, Mingfeng; Speltz, Jared; Jacobsen, Ronald L.; Sanders, Anthony P.; Raeymaekers, Bart

2014-01-01

More than 285,000 total hip replacement surgeries are performed in the US each year. Most prosthetic hip joints consist of a cobalt-chromium (CoCr) femoral head that articulates with a polyethylene acetabular component, lubricated with synovial fluid. The statistical survivorship of these metal-on-polyethylene prosthetic hip joints declines significantly after 10 to 15 years of use, primarily as a result of polyethylene wear and wear debris incited disease. The current engineering paradigm to increase the longevity of prosthetic hip joints is to improve the mechanical properties of the polyethylene component, and to manufacture ultra-smooth articulating surfaces. In contrast, we show that adding a patterned microtexture to the ultra-smooth CoCr femoral head reduces friction when articulating with the polyethylene acetabular liner. The microtexture increases the load-carrying capacity and the thickness of the joint lubricant film, which reduces contact between the articulating surfaces. As a result, friction and wear is reduced. We have used a lubrication model to design the geometry of the patterned microtexture, and experimentally demonstrate reduced friction for the microtextured compared to conventional smooth surrogate prosthetic hip joints. PMID:25013240

Hybrid organic-inorganic porous semiconductor transducer for multi-parameters sensing.

PubMed

Caliò, Alessandro; Cassinese, Antonio; Casalino, Maurizio; Rea, Ilaria; Barra, Mario; Chiarella, Fabio; De Stefano, Luca

2015-07-06

Porous silicon (PSi) non-symmetric multi-layers are modified by organic molecular beam deposition of an organic semiconductor, namely the N,N'-1H,1H-perfluorobutyldicyanoperylene-carboxydi-imide (PDIF-CN2). Joule evaporation of PDIF-CN2 into the PSi sponge-like matrix not only improves but also adds transducing skills, making this solid-state device a dual signal sensor for chemical monitoring. PDIF-CN2 modified PSi optical microcavities show an increase of about five orders of magnitude in electric current with respect to the same bare device. This feature can be used to sense volatile substances. PDIF-CN2 also improves chemical resistance of PSi against alkaline and acid corrosion. © 2015 The Author(s) Published by the Royal Society. All rights reserved.

Correlation of Predicted and Observed Optical Properties of Multilayer Thermal Control Coatings

NASA Technical Reports Server (NTRS)

Jaworske, Donald A.

1998-01-01

Thermal control coatings on spacecraft will be increasingly important, as spacecraft grow smaller and more compact. New thermal control coatings will be needed to meet the demanding requirements of next generation spacecraft. Computer programs are now available to design optical coatings and one such program was used to design several thermal control coatings consisting of alternating layers of WO3 and SiO2. The coatings were subsequently manufactured with electron beam evaporation and characterized with both optical and thermal techniques. Optical data were collected in both the visible region of the spectrum and the infrared. Predictions of solar absorptance and infrared emittance were successfully correlated to the observed thermal control properties. Functional performance of the coatings was verified in a bench top thermal vacuum chamber.

Technique for forming ITO films with a controlled refractive index

DOE Office of Scientific and Technical Information (OSTI.GOV)

Markov, L. K., E-mail: l.markov@mail.ioffe.ru; Smirnova, I. P.; Pavluchenko, A. S.

2016-07-15

A new method for fabricating transparent conducting coatings based on indium-tin oxide (ITO) with a controlled refractive index is proposed. This method implies the successive deposition of material by electron-beam evaporation and magnetron sputtering. Sputtered coatings with different densities (and, correspondingly, different refractive indices) can be obtained by varying the ratio of the mass fractions of material deposited by different methods. As an example, films with effective refractive indices of 1.2, 1.4, and 1.7 in the wavelength range of 440–460 nm are fabricated. Two-layer ITO coatings with controlled refractive indices of the layers are also formed by the proposed method.more » Thus, multilayer transparent conducting coatings with desired optical parameters can be produced.« less

Structural, magnetic, and dielectric properties of multiferroic Co1-xMgxCr2O4 nanoparticles

NASA Astrophysics Data System (ADS)

Kamran, M.; Ullah, A.; Rahman, S.; Tahir, A.; Nadeem, K.; Anis ur Rehman, M.; Hussain, S.

2017-07-01

We examined the structural, magnetic, and dielectric properties of Co1-xMgxCr2O4 nanoparticles with composition x = 0, 0.2, 0.4, 0.5, 0.6, 0.8 and 1 in detail. X-ray diffraction (XRD) revealed normal spinel structure for all the samples. Rietveld refinement fitting results of the XRD showed no impurity phases which signifies the formation of single phase Co1-xMgxCr2O4 nanoparticles. The average crystallite size showed a peak behaviour with maxima at x = 0.6. Raman and Fourier transform infrared (FTIR) spectroscopy also confirmed the formation of single phase normal spinel for all the samples and exhibited dominant vibrational changes for x ≥ 0.6. For x = 0 (CoCr2O4), zero field cooled/field cooled (ZFC/FC) magnetization curves showed paramagnetic (PM) to ferrimagnetic (FiM) transition at Tc = 97 K and a conical spiral magnetic order at Ts = 30 K. The end members CoCr2O4 (x = 0) and MgCr2O4 (x = 1) are FiM and antiferromagnetic (AFM), respectively. Tc and Ts showed decreasing trend with increasing x, followed by an additional AFM transition at TN = 15 K for x = 0.6. The system finally stabilized and changed to highly frustrated AFM structure at x = 1 due to formation of pure MgCr2O4. High field FC curves (5T) depicted nearly no effect on spiral magnetic state, which is attributed to strong exchange B-B magnetic interactions at low temperatures. Dielectric parameters showed a non-monotonous behaviour with Mg concentration and were explained with the help of Maxwell-Wagner model and Koop's theory. Dielectric properties were improved for nanoparticles with x = 0.6 and is attributed to their larger average crystallite size. In summary, Mg doping has significantly affects the structural, magnetic, and dielectric properties of CoCr2O4 nanoparticles, which can be attributed to variations in local magnetic exchange interactions and variation in average crystallite size of these chromite nanoparticles.

Fretting corrosion behavior of nitinol spinal rods in conjunction with titanium pedicle screws.

PubMed

Lukina, Elena; Kollerov, Mikhail; Meswania, Jay; Khon, Alla; Panin, Pavel; Blunn, Gordon W

2017-03-01

Untypical corrosion damage including erosions combined with the build-up of titanium oxide as a corrosion product on the surface of explanted Nitinol spinal rods in the areas where it was in contact with titanium pedicle screw head is reported. It was suggested that Nitinol rods might have inferior fretting corrosion resistance compared with that made of titanium or CoCr. Fretting corrosion of Nitinol spinal rods with titanium (Ti6Al4V) pedicle screws were tested in-vitro by conducting a series of potentiostatic measurements of the peak-to-peak values of fretting corrosion current under bending in a 10% solution of calf serum in PBS. The test included Nitinol rods locked in titanium pedicle screws of different designs. Performance of commercially available titanium (Ti6Al4V) and CoCr spinal rods was also investigated for a comparison. Corrosion damage observed after the in-vitro tests was studied using SEM and EDAX analysis and was compared with patterns on Nitinol rods retrieved 12months after initial surgery. Metal ions level was measured in the test media after in-vitro experiments and in the blood and tissues of the patients who had the rods explanted. The results of this study revealed that Nitinol spinal rods locked in Ti pedicle screws are susceptible to fretting corrosion demonstrating higher fretting corrosion current compared with commercially used Ti6Al4V and CoCr rods. On the surface of Nitinol rods after in-vitro tests and on those retrieved from the patients similar corrosion patterns were observed. Improved resistance to fretting corrosion was observed with Nitinol rods in the in-vitro tests where pedicle screws were used with a stiffer locking mechanism. Since the development of the localized corrosion damage might increase the risk of premature fatigue failure of the rods and result in leaching of Ni ions, it is concluded that Nitinol rods should not be used in conjunction with Ti pedicle screws without special protection especially where the design provides a high degree of mobility to the rods. Copyright © 2016 Elsevier B.V. All rights reserved.

Trunnion Failure of the Recalled Low Friction Ion Treatment Cobalt Chromium Alloy Femoral Head.

PubMed

Urish, Kenneth L; Hamlin, Brian R; Plakseychuk, Anton Y; Levison, Timothy J; Higgs, Genymphas B; Kurtz, Steven M; DiGioia, Anthony M

2017-09-01

Gross trunnion failure (GTF) is a rare complication in total hip arthroplasty (THA) reported across a range of manufacturers. Specific lots of the Stryker low friction ion treatment (LFIT) anatomic cobalt chromium alloy (CoCr) V40 femoral head were recalled in August 2016. In part, the recall was based out of concerns for disassociation of the femoral head from the stem and GTF. We report on 28 patients (30 implants) with either GTF (n = 18) or head-neck taper corrosion (n = 12) of the LFIT CoCr femoral head and the Accolade titanium-molybdenum-zirconium-iron alloy femoral stems. All these cases were associated with adverse local tissue reactions requiring revision of the THA. In our series, a conservative estimate of the incidence of failure was 4.7% (n = 636 total implanted) at 8.0 ± 1.4 years from the index procedure. Failures were associated with a high-offset 127° femoral stem neck angle and increased neck lengths; 43.3% (13 of 30) of the observed failures included implant sizes outside the voluntary recall (27.8% [5 of 18] of the GTF and 75.0% [8 of 12] of the taper corrosion cases). Serum cobalt and chromium levels were elevated (cobalt: 8.4 ± 7.0 μg/mL; chromium: 3.4 ± 3.3 μ/L; cobalt/chromium ratio: 3.7). The metal artifact reduction sequence magnetic resonance imaging demonstrated large cystic fluid collections typical with adverse local tissue reactions. During revision, a pseudotumor was observed in all cases. Pathology suggested a chronic inflammatory response. Impending GTF could be diagnosed based on aspiration of black synovial fluid and an oblique femoral head as compared with the neck taper on radiographs. In our series of the recalled LFIT CoCr femoral head, the risk of impending GTF or head-neck taper corrosion should be considered as a potential diagnosis in a painful LFIT femoral head and Accolade titanium-molybdenum-zirconium-iron alloy THA with unknown etiology. Almost half of the failures we observed included sizes outside of the voluntary recall. Copyright © 2017 Elsevier Inc. All rights reserved.

Vertical misfit of laser-sintered and vacuum-cast implant-supported crown copings luted with definitive and temporary luting agents

PubMed Central

Sánchez-Turrión, Andrés; López-Lozano, José F.; Albaladejo, Alberto; Torres-Lagares, Daniel; Montero, Javier; Suárez-García, Maria J.

2012-01-01

Objectives. This study aimed to evaluate the vertical discrepancy of implant-supported crown structures constructed with vacuum-casting and Direct Metal Laser Sintering (DMLS) technologies, and luted with different cement types. Study Design. Crown copings were fabricated using: (1) direct metal laser sintered Co-Cr (LS); (2) vacuum-cast Co-Cr (CC); and (3) vacuum-cast Ti (CT). Frameworks were luted onto machined implant abutments under constant seating pressure. Each alloy group was randomly divided into 5 subgroups (n = 10 each) according to the cement system utilized: Subgroup 1 (KC) used resin-modified glass-ionomer Ketac Cem Plus; Subgroup 2 (PF) used Panavia F 2.0 dual-cure resin cement; Subgroup 3 (RXU) used RelyX Unicem 2 Automix self-adhesive dual-cure resin cement; Subgroup 4 (PIC) used acrylic/urethane-based temporary Premier Implant Cement; and Subgroup 5 (DT) used acrylic/urethane-based temporary DentoTemp cement. Vertical misfit was measured by scanning electron microscopy (SEM). Two-way ANOVA and Student-Newman-Keuls tests were run to investigate the effect of alloy/fabrication technique, and cement type on vertical misfit. The statistical significance was set at α = 0.05. Results. The alloy/manufacturing technique and the luting cement affected the vertical discrepancy (p < 0.001). For each cement type, LS samples exhibited the best fit (p < 0.01) whereas CC and CT frames were statistically similar. Within each alloy group, PF and RXU provided comparably greater discrepancies than KC, PIC, and DT, which showed no differences. Conclusions. Laser sintering may be an alternative to vacuum-casting of base metals to obtain passive-fitting implant-supported crown copings. The best marginal adaptation corresponded to laser sintered structures luted with glass-ionomer KC, or temporary PIC or DT cements. The highest discrepancies were recorded for Co-Cr and Ti cast frameworks bonded with PF or RXU resinous agents. All groups were within the clinically acceptable misfit range. Key words:Dental alloy, laser sintering, implant-supported prostheses, vertical discrepancy, vertical misfit. PMID:22322524

Retention Load Values of Telescopic Crowns Made of Y-TZP and CoCr with Y-TZP Secondary Crowns: Impact of Different Taper Angles

PubMed Central

Merk, Susanne; Wagner, Christina; Stock, Veronika; Schmidlin, Patrick R.; Roos, Malgorzata; Eichberger, Marlis; Stawarczyk, Bogna

2016-01-01

This study aimed to examine and compare the retention load values (RL) of different telescopic crown assemblies (Y-TZP and CoCr primary crowns with electroformed and Y-TZP secondary crowns each) with three different taper angles (0°, 1° and 2°). Thirty Y-TZP primary crowns with electroformed gold copings (Z/G group) and Y-TZP secondary crowns (Z/Z group) and 30 CoCr primary crowns with electroformed gold copings (C/G group) and Y-TZP secondary crowns (C/Z group), each with taper angles of 0°, 1° and 2°, were fabricated, respectively. With the exception of the electroformed gold copings, all specimens were Computer-Aided-Design/Computer-Aided-Manufacturing (CAD/CAM)-milled, then sintered and afterwards manually adapted. In order to stabilize the gold copings, they were fixed in a tertiary structure. The secondary crowns were constructed with a hook, which ensured self-alignment with an upper chain. Afterwards, 20 pull-off test cycles were performed in a universal testing machine under artificial saliva and after weighing the secondary crowns with a 5 kg object for 20 s. Data were analyzed by one-way and two-way Analysis of Variance (ANOVA). C/Z with 1° showed higher (p = 0.009) RL than 0° and 2° tapers. C/G at 1° also showed higher (p = 0.001) RL than at tapers of 0° and 2°. Z/G and C/G at 0° showed lower RL than Z/Z and C/Z (p < 0.001). Primary crowns had no impact on the 0° group. Z/G showed lower RL as compared to C/Z within the 1° group (p = 0.007) and Z/Z in the 2° group (p = 0.006). The primary crown material had no influence on RL. Electroformed copings showed lower RL. Further investigations for 1° as well as for the long-term performance after thermomechanical aging are necessary. PMID:28773477

Pan evaporation modeling using six different heuristic computing methods in different climates of China

NASA Astrophysics Data System (ADS)

Wang, Lunche; Kisi, Ozgur; Zounemat-Kermani, Mohammad; Li, Hui

2017-01-01

Pan evaporation (Ep) plays important roles in agricultural water resources management. One of the basic challenges is modeling Ep using limited climatic parameters because there are a number of factors affecting the evaporation rate. This study investigated the abilities of six different soft computing methods, multi-layer perceptron (MLP), generalized regression neural network (GRNN), fuzzy genetic (FG), least square support vector machine (LSSVM), multivariate adaptive regression spline (MARS), adaptive neuro-fuzzy inference systems with grid partition (ANFIS-GP), and two regression methods, multiple linear regression (MLR) and Stephens and Stewart model (SS) in predicting monthly Ep. Long-term climatic data at various sites crossing a wide range of climates during 1961-2000 are used for model development and validation. The results showed that the models have different accuracies in different climates and the MLP model performed superior to the other models in predicting monthly Ep at most stations using local input combinations (for example, the MAE (mean absolute errors), RMSE (root mean square errors), and determination coefficient (R2) are 0.314 mm/day, 0.405 mm/day and 0.988, respectively for HEB station), while GRNN model performed better in Tibetan Plateau (MAE, RMSE and R2 are 0.459 mm/day, 0.592 mm/day and 0.932, respectively). The accuracies of above models ranked as: MLP, GRNN, LSSVM, FG, ANFIS-GP, MARS and MLR. The overall results indicated that the soft computing techniques generally performed better than the regression methods, but MLR and SS models can be more preferred at some climatic zones instead of complex nonlinear models, for example, the BJ (Beijing), CQ (Chongqing) and HK (Haikou) stations. Therefore, it can be concluded that Ep could be successfully predicted using above models in hydrological modeling studies.

Multilayer Ni/Fe thin films as oxygen evolution catalysts for solar fuel production

NASA Astrophysics Data System (ADS)

Biset-Peiró, M.; Murcia-López, S.; Fàbrega, C.; Morante, J. R.; Andreu, T.

2017-03-01

The slow kinetics and high overpotential of the oxygen evolution reaction is one of the main limiting factors to achieve the minimum required performances of the so-called photoelectrochemical water splitting systems. An oxygen evolution catalyst (OEC) becomes essential in order to perform this process with higher efficiency. Herein, we report the physical, optical and electrochemical characterization of multilayer Ni/Fe thin films as earth-abundant OEC, to avoid the use of platinum group metals (PGM). Uniform films of thicknesses ranging from 1 to 10 nm were fabricated by sequential and alternate thermal evaporation of Ni and Fe. It was found that the successive deposition allows the fabrication of a Ni terminated surface that does not need activation due to the Fe underlayer. The lowest overpotential achieved for NiFe was 370 mV at 10 mA cm-2 and a Tafel slope of 37 mV dec-1 with 1 nm thickness and 95% transmittance. Finally, NiFe OEC was implemented on top of Mo:BiVO4 photoanodes which resulted in a reduction of the open circuit potential of 0.2 V and up to five fold increase of the oxidation efficiency at 0.7 VRHE. The results presented facilitate the practical implementation of BiVO4 photoanodes in tandem configuration for bias free photoassisted water splitting.

Iron silicide formation at different layers of (Fe/Si)3 multilayered structures determined by conversion electron Mössbauer spectroscopy

NASA Astrophysics Data System (ADS)

Badía-Romano, L.; Rubín, J.; Magén, C.; Bürgler, D. E.; Bartolomé, J.

2014-07-01

The morphology and the quantitative composition of the Fe-Si interface layer forming at each Fe layer of a (Fe/Si)3 multilayer have been determined by means of conversion electron Mössbauer spectroscopy (CEMS) and high-resolution transmission electron microscopy (HRTEM). For the CEMS measurements, each layer was selected by depositing the Mössbauer active 57Fe isotope with 95% enrichment. Samples with Fe layers of nominal thickness dFe = 2.6 nm and Si spacers of dSi = 1.5 nm were prepared by thermal evaporation onto a GaAs(001) substrate with an intermediate Ag(001) buffer layer. HRTEM images showed that Si layers grow amorphous and the epitaxial growth of the Fe is good only for the first deposited layer. The CEMS spectra show that at all Fe/Si and Si/Fe interfaces a paramagnetic c-Fe1-xSi phase is formed, which contains 16% of the nominal Fe deposited in the Fe layer. The bottom Fe layer, which is in contact with the Ag buffer, also contains α-Fe and an Fe1-xSix alloy that cannot be attributed to a single phase. In contrast, the other two layers only comprise an Fe1-xSix alloy with a Si concentration of ≃0.15, but no α-Fe.

Second harmonic generation from metallo-dielectric multilayered structures in the plasmonic regime.

PubMed

Mattiucci, Nadia; D'Aguanno, Giuseppe; Bloemer, Mark J

2010-11-08

We present a theoretical study on second harmonic generation from metallo-dielectric multilayered structures in the plasmonic regime. In particular we analyze the behavior of structures made of Ag (silver) and MgF2 (magnesium-fluoride) due to the straightforward procedure to grow these materials with standard sputtering or thermal evaporation techniques. A systematic study is performed which analyzes four different kinds of elementary cells--namely (Ag/MgF2)N, (MgF2/Ag)N, (Ag/MgF2/Ag)N and (MgF2/Ag/MgF2)N--as function of the number of periods (N) and the thickness of the layers. We predict the conversion efficiency to be up to three orders of magnitude greater than the conversion efficiency found in the non-plasmonic regime and we point out the best geometries to achieve these conversion efficiencies. We also underline the role played by the short-range/long-range plasmons and leaky waves in the generation process. We perform a statistical study to demonstrate the robustness of the SH process in the plasmonic regime against the inevitable variations in the thickness of the layers. Finally, we show that a proper choice of the output medium can further improve the conversion efficiency reaching an enhancement of almost five orders of magnitude with respect to the non plasmonic regime.

Relationship between open-circuit voltage in Cu(In,Ga)Se{sub 2} solar cell and peak position of (220/204) preferred orientation near its absorber surface

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chantana, J., E-mail: jakapan@fc.ritsumei.ac.jp; Minemoto, T.; Watanabe, T.

2013-11-25

Cu(In,Ga)Se{sub 2} (CIGS) absorbers with various Ga/III, Ga/(In+Ga), profiles are prepared by the so-called “multi-layer precursor method” using multi-layer co-evaporation of material sources. It is revealed that open-circuit voltage (V{sub OC}) of CIGS solar cell is primarily dependent on averaged Ga/III near the surface of its absorber. This averaged Ga/III is well predicted by peak position of (220/204) preferred orientation of CIGS film near its surface investigated by glancing-incidence X-ray diffraction with 0.1° incident angle. Finally, the peak position of (220/204) preferred orientation is proposed as a measure of V{sub OC} before solar cell fabrication.

Physical, electrical and magnetic properties of nano-sized Co-Cr substituted magnesium ferrites

NASA Astrophysics Data System (ADS)

Javed Iqbal, Muhammad; Ahmad, Zahoor; Meydan, Turgut; Melikhov, Yevgen

2012-02-01

Co-Cr substituted magnesium ferrite nanomaterials (Mg1-xCoxCrxFe2-xO4 with x = 0.0-0.5) have been prepared by the polyethylene glycol assisted micro emulsion method. X-ray diffraction analysis confirms the single-phase cubic close-packed lattice formation of synthesized materials. Hysteresis loops are measured up to field of 4 MA/m and high field region of these loops are modeled using the Law of Approach to saturation to calculate the magnetocrystalline anisotropy constant. The saturation magnetization of the samples increases initially from 148 kA/m for x = 0.0 to 299 kA/m (x = 0.3) and then decreases to 187 kA/m (x = 0.5). Curie temperature for this series is found to be in the range of 618-766 K. Room temperature resistivity increases gradually from 7.5 × 108 Ω cm (x = 0.0) to 3.47 × 109 Ω cm (x = 0.5). Additionally, dielectric measurements are carried out at room temperature in a frequency range of 100 Hz to 3 MHz. With improvement in the values of the above-mentioned properties, the synthesized materials could be suitable for potential application in some magnetic and microwave devices.

[Effect of vacuum deposition technology on the metal-porcelain bond strength of a new type of CO-CR ceramic and framework dental alloy].

PubMed

Wu, Jun-ling; Chao, Yong-lie; Ji, Ping; Gao, Xu

2007-10-01

To investigate the effect of a new engineering technique of vacuum deposition-plasma magnetron reactive sputter deposition technique on the metal-porcelain bond strength of a new type of Co-Cr ceramic and framework dental alloy. Before porcelain painted on the specimens, the standardized metal strips made from DA9-4 dental alloy were coated with a thin Al2O3 ceramic film by plasma magnetron reactive sputter deposition technique. The conformation, structure and thickness of the ceramic film were analyzed. The specimens for three-point bending test made from DA9-4 alloy and VMK95 porcelain were used for metal-porcelain bond strength measurement, in the same time the interface of metal-porcelain and element distribution were also observed. The flexural bonding strength of metal-porcelain of sputtering group and control group were (180.55+/-16.45) MPa and (143.80+/-24.49) MPa. The flexural bonding strength of metal-porcelain of sputtering group was higher than control group significantly through statistical analysis (P<0.01). The plasma magnetron reactive sputter deposition technique has a positive effect in improving the bonding strength of DA9-4 dental alloy and ceramic.

Toxicity of porcelain-fused-to-metal substrate to zebrafish (Danio rerio) embryos and larvae.

PubMed

Zhao, Libo; Si, Jing; Wei, Yuan; Li, Sirui; Jiang, Yanjiao; Zhou, Rong; Liu, Bin; Zhang, Hong

2018-06-15

Porcelain-fused-to-metal (PFM) crowns are a standard restoration technique in dentistry, but toxicity of PFM in vivo has not been systematically evaluated. The present study evaluated the effects of various metal alloy shells of PFM crowns on the development of zebrafish embryos and larvae in order to determine the safety of these materials. Gold palladium (Au-Pd), silver palladium (Ag-Pd), Nickel chromium (Ni-Cr), cobalt chromium (Co-Cr), titanium (Ti) alloy porcelain crowns were immersed in artificial saliva for 1, 4, and 7 weeks, and the leach solution was collected and used to treat zebrafish embryos at 4-144 h PFM. Toxicity was assessed based on mortality, spontaneous movement, heart rate, hatchability, malformation, and swimming behavior. The 1-week leachates of the five PFMs were not toxic to zebrafish. The rates of mortality and malformation of zebrafish in the Ni-Cr alloy group were increased whereas spontaneous movement, heart rate, and swimming behavior were decreased for 4- and 7-week leachates. Among metal substrates commonly used in dental work, Ni-Cr alloy was most toxic, followed by Co-Cr and Ag-Pd alloys. Ti and Au-Pd alloys showed good biocompatibility and are therefore the most suitable materials for clinical applications. Copyright © 2018 Elsevier Inc. All rights reserved.

Comparison of Conventional Methods and Laser-Assisted Rapid Prototyping for Manufacturing Fixed Dental Prostheses: An In Vitro Study.

PubMed

Pompa, Giorgio; Di Carlo, Stefano; De Angelis, Francesca; Cristalli, Maria Paola; Annibali, Susanna

2015-01-01

This study assessed whether there are differences in marginal fit between laser-fusion and conventional techniques to produce fixed dental prostheses (FDPs). A master steel die with 2 abutments was produced to receive a posterior 4-unit FDPs and single copings. These experimental models were divided into three groups (n = 20/group) manufactured: group 1, Ni-Cr alloy, with a lost-wax casting technique; group 2, Co-Cr alloy, with selective laser melting (SLM); and group 3, yttria-tetragonal zirconia polycrystal (Y-TZP), with a milling system. All specimens were cut along the longitudinal axis and their adaptation was measured at the marginal and shoulder areas on the right and left sides of each abutment. Measurements were made using a stereomicroscope (×60 magnification) and a scanning electron microscope (×800 magnification). The data were analyzed using one-way analysis of variance and the Bonferroni post hoc test, with a significance cutoff of 5%. Significant differences (P < 0.05) were observed between group 3 and the other groups. The marginal opening was smallest with Co-Cr alloy substructures, while the shoulder opening was smallest with Ni-Cr alloy substructures. Within the limitations of this study, the marginal fit of an FDP is better with rapid prototyping (RP) via SLM than conventional manufacturing systems.

Nested potassium hydroxide etching and protective coatings for silicon-based microreactors

NASA Astrophysics Data System (ADS)

de Mas, Nuria; Schmidt, Martin A.; Jensen, Klavs F.

2014-03-01

We have developed a multilayer, multichannel silicon-based microreactor that uses elemental fluorine as a reagent and generates hydrogen fluoride as a byproduct. Nested potassium hydroxide etching (using silicon nitride and silicon oxide as masking materials) was developed to create a large number of channels (60 reaction channels connected to individual gas and liquid distributors) of significantly different depths (50-650 µm) with sloped walls (54.7° with respect to the (1 0 0) wafer surface) and precise control over their geometry. The wetted areas were coated with thermally grown silicon oxide and electron-beam evaporated nickel films to protect them from the corrosive fluorination environment. Up to four Pyrex layers were anodically bonded to three silicon layers in a total of six bonding steps to cap the microchannels and stack the reaction layers. The average pinhole density in as-evaporated films was 3 holes cm-2. Heating during anodic bonding (up to 350 °C for 4 min) did not significantly alter the film composition. Upon fluorine exposure, nickel films (160 nm thick) deposited on an adhesion layer of Cr (10 nm) over an oxidized silicon substrate (up to 500 nm thick SiO2) led to the formation of a nickel fluoride passivation layer. This microreactor was used to investigate direct fluorinations at room temperature over several hours without visible signs of film erosion.

Multi-spectral antireflection coating on zinc sulphide simultaneously effective in visible, eye safe laser wave length and MWIR region

NASA Astrophysics Data System (ADS)

Awasthi, Suman; Nautiyal, B. B.; Kumar, Rajiv; Bandyopadhyay, P. K.

2012-09-01

In recent years multi-spectral device is steadily growing popularity. Multi-spectral antireflection coating effective in visible region for sighting system, laser wavelength for ranging and MWIR region for thermal system can use common objective/receiver optics highly useful for state of art thermal instrumentation. In this paper, design and fabrication of antireflection coating simultaneously effective in visible region (450-650 nm), Eye safe laser wave length (1540 nm) and MWIR region (3.6-4.9 μm) has been reported. Comprehensive search method of design was used and the number of layers in the design was optimised with lowest evaluated merit function studied with respect to various layers. Finally eight-layer design stack was established using hafnium oxide as high index layer and silicon-di-oxide as low index coating material combination. The multilayer stack had been fabricated by using electron beam gun evaporation system in Symphony 9 vacuum coating unit. During layer deposition the substrate was irradiated with End-Hall ion gun. The evaporation was carried out in presence of oxygen and layer thicknesses were measured with crystal monitor. The result achieved for the antireflection coating was 85% average transmission from 450 to 650 nm in visible region, 95% transmission at 1540 nm and 96% average transmission from 3.6 to 4.9 μm in MWIR region.

Effects of a pre-moistened multilayered breathable fabric in promoting heat loss during recovery after exercise under hot conditions.

PubMed

Foreman, J H; Benson, G J; Foreman, M H

2006-08-01

Horses generate considerable internal heat burdens when exercising. Although common practice for a trainer or groom to place a wet blanket or towel on the dorsum of a hot horse post exercise, there are no data supporting the efficacy of this cooling method. To test the hypothesis that a pre-moistened blanket designed with a multilayered breathable fabric would enhance heat loss in horses post exercise. Eight treadmill-trained horses performed a standardised exercise test (SET) weekly for 3 weeks, with 3 different recovery treatments administered randomly. Pulmonary artery temperature (PAT) was measured via Swan-Ganz catheter. The SET consisted of 10 min at 3.7 m/sec, 3 min at 11.0 m/sec, 25 min at 3.7 m/sec and 20 min of recovery walking at 2.0 m/sec (58 min exercise and recovery under laboratory conditions of 35.0-40.6 degrees C and 27-49% RH). From 3-7 min during recovery, the treadmill was stopped and horses randomly received either: (a) no bath (negative control); (b) a bath consisting of 32 l of 1-4 degrees C water split into 3-4 cycles of bilateral water application (positive control) followed by water removal ('scraping'); or (c) application of a multilayered fabric blanket soaked in 16-19 degrees C water, wrung out, and placed over the dorsum and sides of the horse. PAT was compared using RM ANOVA with the Student Neuman-Keul's test used post hoc to discriminate between treatments at specific points in time. Mean PAT rose with each phase of exercise (P<0.001) and peaked at a mean of 40.2 +/- 0.2 degrees C. During recovery, the cold bath decreased HR and PAT for 9 min after walking resumed (P<0.001-P<0.05). The blanket did not decrease HR or PAT compared to negative control (P>0.05), and both were hotter than the cold bath treatment through 16 min of recovery (P<0.05). A specially-designed cooling blanket failed to reduce PAT when compared to negative control. Cold water bathing decreased HR and PAT but was not effective throughout all of recovery. A specially-designed, pre-moistened multilayered breathable fabric failed to promote evaporative cooling compared to negative control. Cold water baths may need to be repeated throughout recovery to optimise their effect.

Process-Parameter-Dependent Optical and Structural Properties of ZrO2MgO Mixed-Composite Films Evaporated from the solid Solution

NASA Technical Reports Server (NTRS)

Sahoo, N. K.; Shapiro, A. P.

1998-01-01

The process-parameter-dependent optical and structural properties of ZrO2MgO mixed-composite material have been investigated. Optical properties were derived from spectrophotometric measurements. By use of atomic force microscopy, x-ray diffraction analysis, and energy-dispersive x-ray (EDX) analysis, the surface morphology, grain size distributions, crystallographic phases, and process-dependent material composition of films have been investigated. EDX analysis made evident the correlation between the oxygen enrichment in the films prepared at a high level of oxygen pressure and the very low refractive index. Since oxygen pressure can be dynamically varied during a deposition process, coatings constructed of suitable mixed-composite thin films can benefit from continuous modulation of the index of refraction. A step modulation approach is used to develop various multilayer-equivalent thin-film devices.

Thermoelectric Measurements of Magnetic Nanostructures Using Thermal Isolation Platforms

NASA Astrophysics Data System (ADS)

Avery, A. D.; Sultan, R.; Bassett, D.; Pufall, M. R.; Zink, B. L.

2010-03-01

The effective design of next-generation memory storage and logic devices based on spin necessitates a thorough understanding of transport properties of their potential components. Although electrical transport in magnetic materials is well-understood, thermal transport is historically difficult to measure. Using micromachined thermal isolation structures, we make direct measurements of thermal and electrical transport in these systems. Our technique offers a method for accurately measuring films and other low-dimensional geometries from the microscale down to the nano regime. We will present in-plane thermal conductivity, resistivity, and thermopower results, as well as direct comparisons with the Wiedemann-Franz law for films of various thicknesses and preparation techniques. We will also present the extension of our technique to explore an evaporated multilayer film. Finally, we discuss the application of our method to examining the fundamental physics underlying thermoelectric effects, such as thermally driven spin currents, to further the emerging sub-field of spin caloritronics.

Influence of substrate temperatures on the properties of GdF(3) thin films with quarter-wave thickness in the ultraviolet region.

PubMed

Jin, Jingcheng; Jin, Chunshui; Li, Chun; Deng, Wenyuan; Yao, Shun

2015-06-01

High-quality coatings of fluoride materials are in extraordinary demand for use in deep ultraviolet (DUV) lithography. Gadolinium fluoride (GdF₃) thin films were prepared by a thermal boat evaporation process at different substrate temperatures. GdF₃ thin film was set at quarter-wave thickness (∼27  nm) with regard to their common use in DUV/vacuum ultraviolet optical stacks; these thin films may significantly differ in nanostructural properties at corresponding depositing temperatures, which would crucially influence the performance of the multilayers. The measurement and analysis of optical, structural, and mechanical properties of GdF₃ thin films have been performed in a comprehensive characterization cycle. It was found that depositing GdF₃ thin films at relative higher temperature would form a rather dense, smooth, homogeneous structure within this film thickness scale.

Interface Optoelectronics Engineering for Mechanically Stacked Tandem Solar Cells Based on Perovskite and Silicon.

PubMed

Kanda, Hiroyuki; Uzum, Abdullah; Nishino, Hitoshi; Umeyama, Tomokazu; Imahori, Hiroshi; Ishikawa, Yasuaki; Uraoka, Yukiharu; Ito, Seigo

2016-12-14

Engineering of photonics for antireflection and electronics for extraction of the hole using 2.5 nm of a thin Au layer have been performed for two- and four-terminal tandem solar cells using CH 3 NH 3 PbI 3 perovskite (top cell) and p-type single crystal silicon (c-Si) (bottom cell) by mechanically stacking. Highly transparent connection multilayers of evaporated-Au and sputtered-ITO films were fabricated at the interface to be a point-contact tunneling junction between the rough perovskite and flat silicon solar cells. The mechanically stacked tandem solar cell with an optimized tunneling junction structure was ⟨perovskite for the top cell/Au (2.5 nm)/ITO (154 nm) stacked-on ITO (108 nm)/c-Si for the bottom cell⟩. It was confirmed the best efficiency of 13.7% and 14.4% as two- and four-terminal devices, respectively.

Sb2O3/Ag/Sb2O3 Multilayer Transparent Conducting Films For Ultraviolet Organic Light-emitting Diode

NASA Astrophysics Data System (ADS)

Song, Chunyan; Zhang, Nan; Lin, Jie; Guo, Xiaoyang; Liu, Xingyuan

2017-01-01

A novel UV transparent conducting films based on Sb2O3/Ag/Sb2O3 (SAS) structure, which were prepared by an electron-beam thermal evaporation at room temperature. This SAS exhibits excellent electrical, optical and stable properties. Especially for UV region, the SAS has high transmittance of 80% at 306 nm and 92% at 335 nm, meanwhile achieving low sheet resistance ( ≤ 10 Ω sq-1). The UV OLED based on the SAS show competitive device performance. The UV OLED obtains the peak of UV electroluminescence at 376 nm and shows a very high maximum EQE of 4.1% with the maximum output power density of 5.18 mW cm-2. These results indicate that the potential of SAS applications in deep UV transparent electrodes and large-scale flexible transparent electronics.

Sb2O3/Ag/Sb2O3 Multilayer Transparent Conducting Films For Ultraviolet Organic Light-emitting Diode.

PubMed

Song, Chunyan; Zhang, Nan; Lin, Jie; Guo, Xiaoyang; Liu, Xingyuan

2017-01-25

A novel UV transparent conducting films based on Sb 2 O 3 /Ag/Sb 2 O 3 (SAS) structure, which were prepared by an electron-beam thermal evaporation at room temperature. This SAS exhibits excellent electrical, optical and stable properties. Especially for UV region, the SAS has high transmittance of 80% at 306 nm and 92% at 335 nm, meanwhile achieving low sheet resistance ( ≤ 10 Ω sq -1 ). The UV OLED based on the SAS show competitive device performance. The UV OLED obtains the peak of UV electroluminescence at 376 nm and shows a very high maximum EQE of 4.1% with the maximum output power density of 5.18 mW cm -2 . These results indicate that the potential of SAS applications in deep UV transparent electrodes and large-scale flexible transparent electronics.

Sb2O3/Ag/Sb2O3 Multilayer Transparent Conducting Films For Ultraviolet Organic Light-emitting Diode

PubMed Central

Song, Chunyan; Zhang, Nan; Lin, Jie; Guo, Xiaoyang; Liu, Xingyuan

2017-01-01

A novel UV transparent conducting films based on Sb2O3/Ag/Sb2O3 (SAS) structure, which were prepared by an electron-beam thermal evaporation at room temperature. This SAS exhibits excellent electrical, optical and stable properties. Especially for UV region, the SAS has high transmittance of 80% at 306 nm and 92% at 335 nm, meanwhile achieving low sheet resistance ( ≤ 10 Ω sq−1). The UV OLED based on the SAS show competitive device performance. The UV OLED obtains the peak of UV electroluminescence at 376 nm and shows a very high maximum EQE of 4.1% with the maximum output power density of 5.18 mW cm−2. These results indicate that the potential of SAS applications in deep UV transparent electrodes and large-scale flexible transparent electronics. PMID:28120888

Transparent ambipolar organic thin film transistors based on multilayer transparent source-drain electrodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhang, Nan; Hu, Yongsheng, E-mail: huyongsheng@ciomp.ac.cn, E-mail: liuxy@ciomp.ac.cn; Lin, Jie

A fabrication method for transparent ambipolar organic thin film transistors with transparent Sb{sub 2}O{sub 3}/Ag/Sb{sub 2}O{sub 3} (SAS) source and drain electrodes has been developed. A pentacene/N,N′-ditridecylperylene-3,4,9,10-tetracarboxylic di-imide (PTCDI-C13) bilayer heterojunction is used as the active semiconductor. The electrodes are deposited by room temperature electron beam evaporation. The devices are fabricated without damaging the active layers. The SAS electrodes have high transmittance (82.5%) and low sheet resistance (8 Ω/sq). High performance devices with hole and electron mobilities of 0.3 cm{sup 2}/V s and 0.027 cm{sup 2}/V s, respectively, and average visible range transmittance of 72% were obtained. These transistors have potential for transparent logicmore » integrated circuit applications.« less

Magnetoimpedance biosensor prototype for ferrogel detection

NASA Astrophysics Data System (ADS)

Kurlyandskaya, G. V.; Fernández, E.; Safronov, A. P.; Blyakhman, F. A.; Svalov, A. V.; Burgoa Beitia, A.; Beketov, I. V.

2017-11-01

Ferrogels are composite materials widely introduced in the area of biomedical engineering as magnetic field sensitive transformers. These biomimetic materials can be prepared by incorporating monodomain magnetic nanoparticles into chemically crosslinked hydrogels. The properties of a biomimetic ferrogels taken for the study unlike that of the biological prototype might be set up by the synthesis and can be thoroughly controlled in a physical experiment. In this work we developed a giant magnetoimpedance sensor with a multilayered FeNi/Ti-based sensitive element adapted for ferrogel studies. Ferrogels were synthesized by radical polymerization of acrylamide in a stable aqueous suspension of γ-Fe2O3 MNPs fabricated by laser target evaporation. The magnetoimpedance measurements in initial state and in the presence of ferrogels with concentrations of nanoparticles from 0 to 2.4 wt% in a frequency range of 1-300 MHz allowed a precise characterization of the stray fields of the nanoparticles present in the ferrogel.

Effect of hydrogen concentration in conventional and IAD coatings on the absorption and laser-induced damage at 10.6 μm

NASA Astrophysics Data System (ADS)

Rahe, Manfred; Ristau, Detlev; Schmidt, Holger

1993-06-01

In this paper, data of single layers of YbF3, BaF2, YF3, and NaF and multilayer coatings produced by conventional thermal evaporation (boat, e-beam) and ion assisted deposition (IAD) are compared. Hydrogen concentration depth profiling was performed using nuclear reaction analysis based on the reaction 1H(15N, (alpha) (gamma) )12C. Absorption was measured with the aid of a laser calorimeter and a cw CO2 laser. A computer-controlled test facility with a TEA CO2 laser was used for determining the 1-on-1 damage thresholds of the coatings. The results point out that the absorption and damage behavior of coatings for the CO2 laser wavelength are related to the total amount of species containing hydrogen. Most of the IAD coatings exhibit a lower hydrogen contamination than conventional thin films.

Silicon solar cell process development, fabrication, and analysis

NASA Technical Reports Server (NTRS)

Yoo, H. I.; Iles, P. A.; Leung, D. C.

1981-01-01

Work has progressed in fabrication and characterization of solar cells from ubiquitous crystallization process (UCP) wafers and LASS ribbons. Gettering tests applied to UCP wafers made little change on their performance compared with corresponding baseline data. Advanced processes such as shallow junction (SJ), back surface field (BSF), and multilayer antireflection (MLAR) were also applied. While BSF by Al paste had shunting problems, cells with SJ and BSF by evaporated Al, and MLAR did achieve 14.1% AMI on UCP silicon. The study of LASS material was very preliminary. Only a few cells with SJ, BSR, (no BSF) and MLAR were completed due to mechanical yield problems after lapping the material. Average efficiency was 10.7% AMI with 13.4% AMI for CZ controls. Relatively high minority carrier diffusion lengths were obtained. The lower than expected Jsc could be partially explained by low active area due to irregular sizes.

Three-dimensionally ordered array of air bubbles in a polymer film

NASA Technical Reports Server (NTRS)

Srinivasarao, M.; Collings, D.; Philips, A.; Patel, S.; Brown, C. S. (Principal Investigator)

2001-01-01

We report the formation of a three-dimensionally ordered array of air bubbles of monodisperse pore size in a polymer film through a templating mechanism based on thermocapillary convection. Dilute solutions of a simple, coil-like polymer in a volatile solvent are cast on a glass slide in the presence of moist air flowing across the surface. Evaporative cooling and the generation of an ordered array of breath figures leads to the formation of multilayers of hexagonally packed water droplets that are preserved in the final, solid polymer film as spherical air bubbles. The dimensions of these bubbles can be controlled simply by changing the velocity of the airflow across the surface. When these three-dimensionally ordered macroporous materials have pore dimensions comparable to the wavelength of visible light, they are of interest as photonic band gaps and optical stop-bands.

Surface studies on scandate cathodes and synthesized scandates

NASA Technical Reports Server (NTRS)

Lesny, Gary; Forman, Ralph

1990-01-01

Auger, ESCA, electron emission, evaporation, and desorption measurements were made on three different types of scandate surfaces. They are: (1) an impregnated top layer scandate cathode, (2) an unimpregnated top layer scandate cathode with a deposited barium or barium oxide adsorbate surface layer, and (3) a synthesized scandate surface, which replicates a scandate cathode surface. The purpose of these experiments was to determine the role that Sc2O3 plays in making the scandate cathode a more copious electron emitter than the conventional impregnated-type cathode. The synthesized scandate surface experiments consisted of depositing multilayer scandium on a tungsten surface, oxidizing the scandium, and then depositing either Ba or BaO on the scandium oxide surface. The results of these measurements showed that the low work function portions of the thin-film scandate cathode are where the Sc2O3 is the substrate and BaO is the adsorbate.

Macro-structural effect of metal surfaces treated using computer-assisted yttrium-aluminum-garnet laser scanning on bone-implant fixation.

PubMed

Hirao, Makoto; Sugamoto, Kazuomi; Tamai, Noriyuki; Oka, Kunihiro; Yoshikawa, Hideki; Mori, Yusuke; Sasaki, Takatomo

2005-05-01

Porous coatings have been applied to the surface of prosthetic devices to foster stable device fixation. The coating serves as a source of mechanical interlocking and may stimulate healthy bone growth through osseointegrated load transfer in cementless arthroplasty. Joint arthroplasty by porous-coated prostheses is one of the most common surgical treatments, and has provided painless and successful joint mobility. However, long-term success is often impaired by the loss of fixation between the prosthesis and bone. Porous-coated prostheses are associated with several disadvantages, including metal debris from porous coatings (third body wear particles) and irregular micro-texture of metal surfaces. Consequently, quantitative histological analysis has been very difficult. These issues arise because the porous coating treatment is based on addition of material and is not precisely controllable. We recently developed a precisely controllable porous texture technique based on material removal by yttrium-aluminum-garnet laser. Free shapes can be applied to complex, three-dimensional hard metal surfaces using this technique. In this study, tartan check shapes made by crossing grooves and dot shapes made by forming holes were produced on titanium (Ti6A14V) or cobalt chrome (CoCr) and evaluated with computer-assisted histological analysis and measurement of bone-metal interface shear strength. Width of grooves or holes ranged from 100 to 800 mum (100, 200, 500, and 800 microm), with a depth of 500 microm. When the cylindrical porous-texture-treated metal samples (diameter, 5 mm; height, 15 mm) were implanted into a rabbit femoral condyle, bone tissue with bone trabeculae formed in the grooves and holes after 2 or 4 weeks, especially in 500-microm-wide grooves. Abundant osteoconduction was consistently observed throughout 500-microm-wide grooves in both Ti6A14V and CoCr. Speed of osteoconduction was faster in Ti6A14V than in CoCr, especially in the tartan check shape made of 500-microm-wide grooves. In pushout testing, the tartan check shape made of 500-microm-wide grooves had significantly higher bone-metal interface shear strength than the dot shape or commercial porous coating. These results indicate that the tartan check shape made of 500-microm-wide grooves on metal surfaces has potential for clinical application in artificial prosthesis design.

Evaluation of the mechanical properties and porcelain bond strength of cobalt-chromium dental alloy fabricated by selective laser melting.

PubMed

Wu, Lin; Zhu, Haiting; Gai, Xiuying; Wang, Yanyan

2014-01-01

Limited information is available regarding the microstructure and mechanical properties of dental alloy fabricated by selective laser melting (SLM). The purpose of this study was to evaluate the mechanical properties of a cobalt-chromium (Co-Cr) dental alloy fabricated by SLM and to determine the correlation between its microstructure and mechanical properties and its porcelain bond strength. Five metal specimens and 10 metal ceramic specimens were fabricated to evaluate the mechanical properties of SLM Co-Cr dental alloy (SLM alloy) with a tensile test and its porcelain bond strength with a 3-point bending test. The relevant properties of the SLM alloy were compared with those of the currently used Co-Cr dental alloy fabricated with conventional cast technology (cast alloy). The Student t test was used to compare the results of the SLM alloy and the cast alloy (α=.05). The microstructure of the SLM alloy was analyzed with a metallographic microscope; the metal ceramic interface of the SLM porcelain bonded alloy was studied with scanning electron microscopy, energy dispersive x-ray spectroscopy, and an electron probe microanalyzer. Both the mean (standard deviation) yield strength (884.37 ± 8.96 MPa) and tensile strength (1307.50 ±10.65 MPa) of the SLM alloy were notably higher than yield strength (568.10 ± 30.94 MPa) and tensile strength (758.73 ± 25.85 MPa) of the currently used cast alloy, and the differences were significant (P<.05). The porcelain bond strength of the SLM alloy was 55.78 ± 3.02 MPa, which was similar to that of the cast alloy, 54.17 ± 4.96 MPa (P>.05). Microstructure analysis suggested that the SLM alloy had a dense and obviously orientated microstructure, which led to excellent mechanical properties. Analysis from scanning electron microscopy, energy dispersive x-ray spectroscopy, and the electron probe microanalyzer indicated that the SLM alloy had an intermediate layer with elemental interpenetration between the alloy and the porcelain, which resulted in an improved bonding interface. Compared with the currently used cast alloy, SLM alloy possessed improved mechanical properties and similar porcelain bond strength. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

A microcomputed tomography evaluation of the marginal fit of cobalt-chromium alloy copings fabricated by new manufacturing techniques and alloy systems.

PubMed

Kim, Eun-Ha; Lee, Du-Hyeong; Kwon, Sung-Min; Kwon, Tae-Yub

2017-03-01

Although new digital manufacturing techniques are attracting interest in dentistry, few studies have comprehensively investigated the marginal fit of fixed dental prostheses fabricated with such techniques. The purpose of this in vitro microcomputed tomography (μCT) study was to evaluate the marginal fit of cobalt-chromium (Co-Cr) alloy copings fabricated by casting and 3 different computer-aided design and computer-aided manufacturing (CAD-CAM)-based processing techniques and alloy systems. Single Co-Cr metal crowns were fabricated using 4 different manufacturing techniques: casting (control), milling, selective laser melting, and milling/sintering. Two different commercial alloy systems were used for each fabrication technique (a total of 8 groups; n=10 for each group). The marginal discrepancy and absolute marginal discrepancy of the crowns were determined with μCT. For each specimen, the values were determined from 4 different regions (sagittal buccal, sagittal lingual, coronal mesial, and coronal distal) by using imaging software and recorded as the average of the 4 readings. For each parameter, the results were statistically compared with 2-way analysis of variance and appropriate post hoc analysis (using Tukey or Student t test) (α=.05). The milling and selective laser melting groups showed significantly larger marginal discrepancies than the control groups (70.4 ±12.0 and 65.3 ±10.1 μm, respectively; P<.001), whereas the milling/sintering groups exhibited significantly smaller values than the controls (P=.004). The milling groups showed significantly larger absolute marginal discrepancy than the control groups (137.4 ±29.0 and 139.2 ±18.9 μm, respectively; P<.05). In the selective laser melting and milling/sintering groups, the absolute marginal discrepancy values were material-specific (P<.05). Nonetheless, the milling/sintering groups yielded statistically comparable (P=.935) or smaller (P<.001) absolute marginal discrepancies to the control groups. The findings of this in vitro μCT study showed that the marginal fit values of the Co-Cr alloy greatly depended on the fabrication methods and, occasionally, the alloy systems. Fixed dental prostheses produced by using the milling/sintering technique can be considered clinically acceptable in terms of marginal fit. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Assembly of large-area, highly ordered, crack-free inverse opal films

PubMed Central

Hatton, Benjamin; Mishchenko, Lidiya; Davis, Stan; Sandhage, Kenneth H.; Aizenberg, Joanna

2010-01-01

Whereas considerable interest exists in self-assembly of well-ordered, porous “inverse opal” structures for optical, electronic, and (bio)chemical applications, uncontrolled defect formation has limited the scale-up and practicality of such approaches. Here we demonstrate a new method for assembling highly ordered, crack-free inverse opal films over a centimeter scale. Multilayered composite colloidal crystal films have been generated via evaporative deposition of polymeric colloidal spheres suspended within a hydrolyzed silicate sol-gel precursor solution. The coassembly of a sacrificial colloidal template with a matrix material avoids the need for liquid infiltration into the preassembled colloidal crystal and minimizes the associated cracking and inhomogeneities of the resulting inverse opal films. We discuss the underlying mechanisms that may account for the formation of large-area defect-free films, their unique preferential growth along the 〈110〉 direction and unusual fracture behavior. We demonstrate that this coassembly approach allows the fabrication of hierarchical structures not achievable by conventional methods, such as multilayered films and deposition onto patterned or curved surfaces. These robust SiO2 inverse opals can be transformed into various materials that retain the morphology and order of the original films, as exemplified by the reactive conversion into Si or TiO2 replicas. We show that colloidal coassembly is available for a range of organometallic sol-gel and polymer matrix precursors, and represents a simple, low-cost, scalable method for generating high-quality, chemically tailorable inverse opal films for a variety of applications. PMID:20484675

Corrosion of dental alloys in artificial saliva with Streptococcus mutans.

PubMed

Lu, Chunhui; Zheng, Yuanli; Zhong, Qun

2017-01-01

A comparative study of the corrosion resistance of CoCr and NiCr alloys in artificial saliva (AS) containing tryptic soy broth (Solution 1) and Streptococcus mutans (S. mutans) species (Solution 2) was performed by electrochemical methods, including open circuit potential measurements, impedance spectroscopy, and potentiodynamic polarization. The adherence of S. mutans to the NiCr and CoCr alloy surfaces immersed in Solution 2 for 24 h was verified by scanning electron microscopy, while the results of electrochemical impedance spectroscopy confirmed the importance of biofilm formation for the corrosion process. The R(QR) equivalent circuit was successfully used to fit the data obtained for the AS mixture without S. mutans, while the R(Q(R(QR))) circuit was found to be more suitable for describing the biofilm properties after treatment with the AS containing S. mutans species. In addition, a negative shift of the open circuit potential with immersion time was observed for all samples regardless of the solution type. Both alloys exhibited higher charge transfer resistance after treatment with Solution 2, and lower corrosion current densities were detected for all samples in the presence of S. mutans. The obtained results suggest that the biofilm formation observed after 24 h of exposure to S. mutans bacteria might enhance the corrosion resistance of the studied samples by creating physical barriers that prevented oxygen interactions with the metal surfaces.

Comparative Evaluation of Marginal and Internal Gap of Co-Cr Copings Fabricated from Conventional Wax Pattern, 3D Printed Resin Pattern and DMLS Tech: An In Vitro Study.

PubMed

Bhaskaran, Eswaran; Azhagarasan, N S; Miglani, Saket; Ilango, T; Krishna, G Phani; Gajapathi, B

2013-09-01

Accuracy of the fit of the restoration has always remained as one of the primary factors in determining success of the restoration. A well fitting restoration needs to be accurate both along its margins and internal surface. This study was conducted to comparatively evaluate the marginal gap and internal gap of cobalt-chromium (Co-Cr) copings fabricated by conventional casting procedures and with direct metal laser sintering (DMLS) technique. Among the total of 30 test samples 10 cast copings were made from inlay casting wax and 10 from 3D printed resin pattern. 10 copings were obtained from DMLS technique. All the 30 test samples were then cemented sequentially on stainless steel model using pressure indicating paste and evaluated for vertical marginal gap in 8 predetermined reference areas. All copings were then removed and partially sectioned and cemented sequentially on same master model for evaluation of internal gap at 4 predetermined reference areas. Both marginal gap and internal gap were measured in microns using video measuring system (VMS2010F). The results obtained for both marginal and internal gap were statistically analyzed and the values fall within the clinically acceptable range. The DMLS technique had an edge over the other two techniques used, as it exhibited minimal gap in the marginal region which is an area of chief concern.

Negative magnetization and the sign reversal of exchange bias field in Co(Cr1-xMnx)2O4 (0≤x≤0.6)

NASA Astrophysics Data System (ADS)

Li, Canglong; Yan, Tengyun; Chakrabarti, Chiranjib; Zhang, Run; Chen, Xinghan; Fu, Qingshan; Yuan, Songliu; Barasa, Godfrey Okumu

2018-03-01

A series of Co(Cr1-xMnx)2O4 (0 ≤ x ≤ 0.6) ceramic samples have been synthesized by using the sol-gel method. The magnetic properties of the ceramics are experimentally studied through different protocols of dc magnetization measurements. It is found that Mn-doping continuously decreases the total magnetization for x in the range of 0 ≤ x ≤ 0.2 and the net magnetization becomes negative in the range of 0.3 ≤ x ≤ 0.5. The net magnetization reverses and becomes positive upon further increasing x to 0.6. This unusual magnetic phenomenon in the system for x = 0.3-0.5 can be called as negative magnetization. It is regarded as arising from the competition of the two magnetic sublattices at different crystallographic sites. For the sample x = 0.3, the magnetic switching effect near the compensation temperature Tcomp has been studied, and it shows potential applications in the spintronic devices. The magnetic configuration of the sample could be changed under a high magnetic field, and the spin is reoriented at TSR. Both positive and negative exchange bias effects are observed, which are ascribed to the pinning force of uncompensated spins on ferromagnetic moments and the magneto-structural transition, respectively.

Oxidized zirconium versus cobalt-chromium against the native patella in total knee arthroplasty: Patellofemoral outcomes.

PubMed

Matassi, Fabrizio; Paoli, Tommaso; Civinini, Roberto; Carulli, Christian; Innocenti, Massimo

2017-10-01

Oxidized zirconium (OxZr) has demonstrated excellent mechanical properties in vitro when used against articular cartilage; less coefficient of friction and less chondral damage have been found when compared with cobalt-chromium (CoCr) implants. However, controversy exists as to whether implants with a zirconium femoral component articulate safely with a native patella in total knee arthroplasty (TKA). To answer this question, the clinical and radiographic results were analysed from a group of patients who underwent a TKA with patella retention; the OxZr versus CoCr femoral components were compared. The present study prospectively evaluated 83 knees of 74 patients from 2009 to 2010. Each patient was evaluated clinically (visual analogue scale, Knee Society score, patellar score) and radiographically (long leg standing radiograph, anterior-posterior and latero-lateral projections, axial view of the patella) pre-operatively and postoperatively with a mean follow-up of 4.47years. The patellar tilt and shift, and progression of patellofemoral osteoarthritis were calculated with the axial view. There were no patient reported adverse reactions and none of the evaluated prostheses failed. Both the clinical and radiographic evaluations showed no statistically significant between-group differences. No adverse events were observed clinically or radiologically. These results justify pursuing the use of oxidized zirconium as an alternative bearing surface for a femoral component associated with patellar retention in TKA. Published by Elsevier B.V.

Corrosion of dental alloys in artificial saliva with Streptococcus mutans

PubMed Central

Lu, Chunhui; Zheng, Yuanli; Zhong, Qun

2017-01-01

A comparative study of the corrosion resistance of CoCr and NiCr alloys in artificial saliva (AS) containing tryptic soy broth (Solution 1) and Streptococcus mutans (S. mutans) species (Solution 2) was performed by electrochemical methods, including open circuit potential measurements, impedance spectroscopy, and potentiodynamic polarization. The adherence of S. mutans to the NiCr and CoCr alloy surfaces immersed in Solution 2 for 24 h was verified by scanning electron microscopy, while the results of electrochemical impedance spectroscopy confirmed the importance of biofilm formation for the corrosion process. The R(QR) equivalent circuit was successfully used to fit the data obtained for the AS mixture without S. mutans, while the R(Q(R(QR))) circuit was found to be more suitable for describing the biofilm properties after treatment with the AS containing S. mutans species. In addition, a negative shift of the open circuit potential with immersion time was observed for all samples regardless of the solution type. Both alloys exhibited higher charge transfer resistance after treatment with Solution 2, and lower corrosion current densities were detected for all samples in the presence of S. mutans. The obtained results suggest that the biofilm formation observed after 24 h of exposure to S. mutans bacteria might enhance the corrosion resistance of the studied samples by creating physical barriers that prevented oxygen interactions with the metal surfaces. PMID:28350880

Comparison of Conventional Methods and Laser-Assisted Rapid Prototyping for Manufacturing Fixed Dental Prostheses: An In Vitro Study

PubMed Central

Pompa, Giorgio; Di Carlo, Stefano; De Angelis, Francesca; Cristalli, Maria Paola; Annibali, Susanna

2015-01-01

This study assessed whether there are differences in marginal fit between laser-fusion and conventional techniques to produce fixed dental prostheses (FDPs). A master steel die with 2 abutments was produced to receive a posterior 4-unit FDPs and single copings. These experimental models were divided into three groups (n = 20/group) manufactured: group 1, Ni-Cr alloy, with a lost-wax casting technique; group 2, Co-Cr alloy, with selective laser melting (SLM); and group 3, yttria-tetragonal zirconia polycrystal (Y-TZP), with a milling system. All specimens were cut along the longitudinal axis and their adaptation was measured at the marginal and shoulder areas on the right and left sides of each abutment. Measurements were made using a stereomicroscope (×60 magnification) and a scanning electron microscope (×800 magnification). The data were analyzed using one-way analysis of variance and the Bonferroni post hoc test, with a significance cutoff of 5%. Significant differences (P < 0.05) were observed between group 3 and the other groups. The marginal opening was smallest with Co-Cr alloy substructures, while the shoulder opening was smallest with Ni-Cr alloy substructures. Within the limitations of this study, the marginal fit of an FDP is better with rapid prototyping (RP) via SLM than conventional manufacturing systems. PMID:26576419

The potential of different artificial neural network (ANN) techniques in daily global solar radiation modeling based on meteorological data

DOE Office of Scientific and Technical Information (OSTI.GOV)

Behrang, M.A.; Assareh, E.; Ghanbarzadeh, A.

2010-08-15

The main objective of present study is to predict daily global solar radiation (GSR) on a horizontal surface, based on meteorological variables, using different artificial neural network (ANN) techniques. Daily mean air temperature, relative humidity, sunshine hours, evaporation, and wind speed values between 2002 and 2006 for Dezful city in Iran (32 16'N, 48 25'E), are used in this study. In order to consider the effect of each meteorological variable on daily GSR prediction, six following combinations of input variables are considered: (I)Day of the year, daily mean air temperature and relative humidity as inputs and daily GSR as output.more » (II)Day of the year, daily mean air temperature and sunshine hours as inputs and daily GSR as output. (III)Day of the year, daily mean air temperature, relative humidity and sunshine hours as inputs and daily GSR as output. (IV)Day of the year, daily mean air temperature, relative humidity, sunshine hours and evaporation as inputs and daily GSR as output. (V)Day of the year, daily mean air temperature, relative humidity, sunshine hours and wind speed as inputs and daily GSR as output. (VI)Day of the year, daily mean air temperature, relative humidity, sunshine hours, evaporation and wind speed as inputs and daily GSR as output. Multi-layer perceptron (MLP) and radial basis function (RBF) neural networks are applied for daily GSR modeling based on six proposed combinations. The measured data between 2002 and 2005 are used to train the neural networks while the data for 214 days from 2006 are used as testing data. The comparison of obtained results from ANNs and different conventional GSR prediction (CGSRP) models shows very good improvements (i.e. the predicted values of best ANN model (MLP-V) has a mean absolute percentage error (MAPE) about 5.21% versus 10.02% for best CGSRP model (CGSRP 5)). (author)« less

Room-Temperature Deformation and Martensitic Transformation of Two Co-Cr-Based Alloys

NASA Astrophysics Data System (ADS)

Cai, S.; Schaffer, J. E.; Huang, D.; Gao, J.; Ren, Y.

2018-05-01

Deformation of two Co-Cr alloys was studied by in situ synchrotron X-ray diffraction. Both alloys show stress-induced martensite transformation, which is affected by phase stabilities and transformation strains. Crystal structure of WC in Co-20Cr-15W-10Ni is identified. Compared with other phases present, it is elastically isotropic, exhibits high strength, and can elastically withstand strains exceeding 1 pct. Texture change during phase transformation is explained based on the crystal orientation relationship between γ- and ɛ-phases.

Room-Temperature Deformation and Martensitic Transformation of Two Co-Cr-Based Alloys

NASA Astrophysics Data System (ADS)

Cai, S.; Schaffer, J. E.; Huang, D.; Gao, J.; Ren, Y.

2018-07-01

Deformation of two Co-Cr alloys was studied by in situ synchrotron X-ray diffraction. Both alloys show stress-induced martensite transformation, which is affected by phase stabilities and transformation strains. Crystal structure of WC in Co-20Cr-15W-10Ni is identified. Compared with other phases present, it is elastically isotropic, exhibits high strength, and can elastically withstand strains exceeding 1 pct. Texture change during phase transformation is explained based on the crystal orientation relationship between γ- and ɛ-phases.

NASA Tech Briefs, June 2004

NASA Technical Reports Server (NTRS)

2004-01-01

Topics covered include: COTS MEMS Flow-Measurement Probes; Measurement of an Evaporating Drop on a Reflective Substrate; Airplane Ice Detector Based on a Microwave Transmission Line; Microwave/Sonic Apparatus Measures Flow and Density in Pipe; Reducing Errors by Use of Redundancy in Gravity Measurements; Membrane-Based Water Evaporator for a Space Suit; Compact Microscope Imaging System with Intelligent Controls; Chirped-Superlattice, Blocked-Intersubband QWIP; Charge-Dissipative Electrical Cables; Deep-Sea Video Cameras Without Pressure Housings; RFID and Memory Devices Fabricated Integrally on Substrates; Analyzing Dynamics of Cooperating Spacecraft; Spacecraft Attitude Maneuver Planning Using Genetic Algorithms; Forensic Analysis of Compromised Computers; Document Concurrence System; Managing an Archive of Images; MPT Prediction of Aircraft-Engine Fan Noise; Improving Control of Two Motor Controllers; Electro-deionization Using Micro-separated Bipolar Membranes; Safer Electrolytes for Lithium-Ion Cells; Rotating Reverse-Osmosis for Water Purification; Making Precise Resonators for Mesoscale Vibratory Gyroscopes; Robotic End Effectors for Hard-Rock Climbing; Improved Nutation Damper for a Spin-Stabilized Spacecraft; Exhaust Nozzle for a Multitube Detonative Combustion Engine; Arc-Second Pointer for Balloon-Borne Astronomical Instrument; Compact, Automated Centrifugal Slide-Staining System; Two-Armed, Mobile, Sensate Research Robot; Compensating for Effects of Humidity on Electronic Noses; Brush/Fin Thermal Interfaces; Multispectral Scanner for Monitoring Plants; Coding for Communication Channels with Dead-Time Constraints; System for Better Spacing of Airplanes En Route; Algorithm for Training a Recurrent Multilayer Perceptron; Orbiter Interface Unit and Early Communication System; White-Light Nulling Interferometers for Detecting Planets; and Development of Methodology for Programming Autonomous Agents.

A study of metalized electrode self-clearing in electroactive polymer (EAP) based actuators

NASA Astrophysics Data System (ADS)

Ahmed, Saad; Ounaies, Zoubeida

2016-04-01

Electroactive polymer (EAP) based technologies have shown promise in areas such as artificial muscles, actuator, aerospace, medical and soft robotics. Still challenges remain such as low induced forces and defects-driven electrical breakdown, which impede the practical implementation of this technology. Multilayered or stacked configuration can address the low induced force issue whereas self-clearing can be a technique to improve breakdown limit of EAP based actuators. Self-clearing refers to the partial local breakdown of dielectric medium due to the presence of impurities, which in turn results in the evaporation of some of the metalized electrode. After this evaporation, the impurity is cleared and any current path would be safely cut off, which means the actuator continues to perform. It is a widely studied concept in the capacitor community, while it has not been studied much for EAP technologies. In this paper we report a systematic approach to precondition a silver-metalized electroactive polymer (EAP), more specifically P(VDF-TrFE-CTFE) terpolymer, using self-clearing concept. First, we show improvement in the dielectric breakdown strength of EAP based unimorph actuators after pre-clearing the impurities using low electric field (lower than dielectric breakdown of the terpolymer). Inspired by this improvement, we used Weibull statistics to systematically estimate the self-clearing/ preconditioning field needed to clear the defects. Then electrical breakdown experiments are conducted with and without preconditioning the samples to investigate its effect on the breakdown strength of the sample.

Phase and microstructural development in alumina sol-gel coatings on CoCr alloy.

PubMed

Bae, I J; Standard, O C; Roger, G J; Brazil, D

2004-09-01

Phase transformation of gamma-Al(2)O(3) to alpha-Al(2)O(3) in alumina sol gel coatings on biomedical CoCr alloy was studied as function of heat treatment temperature and time. Transformation in unseeded coatings was significant only above approximately 1200 degrees C. Addition of alpha-Al(2)O(3) seed particles having an average size of approximately 40 nm lowered the phase transformation temperature to around 800 degrees C. These particles were considered to act as heterogeneous nucleation sites for epitaxial growth of the alpha-Al(2)O(3) phase. The kinetics and activation energy (420 kJ/mol) for the phase transformation in the seeded coatings were similar to those reported for seeded monolithic alumina gels indicating that the transformation mechanism is the same in the two material configurations. Avrami growth parameters indicated that the mechanism was diffusion controlled and invariant over the temperature range studied but that growth was possibly constrained by the finite size of the seed particles and/or coating thickness. The phase transformation occurred by the growth of alpha-Al(2)O(3) grains at the expense of the precursor fine-grained gamma-Al(2)O(3) matrix and near-complete transformation coincided with physical impingement of the growing grains. The grain size at impingement was approximately 100 nm which agreed well with that predicted from the theoretical linear spacing of seed particles in the initial sol.

Highly crosslinked polyethylene: a safe alternative to conventional polyethylene for dual mobility cup mobile component. A biomechanical validation.

PubMed

Malatray, Matthieu; Roux, Jean-Paul; Gunst, Stanislas; Pibarot, Vincent; Wegrzyn, Julien

2017-03-01

Dual mobility cup (DMC) consists of a cobalt-chromium (CoCr) alloy cup articulated with a polyethylene (PE) mobile component capturing the femoral head in force using a snap-fit technique. This biomechanical study was the first to evaluate and compare the generation of cracks in the retentive area of DMC mobile components made of highly crosslinked PE (XLPE) or conventional ultra-high molecular weight PE (UHMWPE). Eighty mobile components designed for a 52-mm diameter Symbol® DMC (Dedienne Santé, Mauguio, France) and a 28-mm diameter femoral head were analyzed. Four groups of 20 mobile components were constituted according to the PE material: raw UHMWPE, sterilized UHMWPE, annealed XLPE and remelted XLPE. Ten mobile components in each group were impacted with a 28-mm diameter CoCr femoral head using a snap-fit technique. The occurrence, location and area of the cracks in the retentive area were investigated using micro-CT (Skyscan 1176®, Bruker, Aarsellar, Belgium) with a 35 μm nominal isotropic voxel size by two observers blinded to the PE material and impaction or not of the mobile components. Compared to conventional UHMWPE, the femoral head snap-fit did not generate more or wider cracks in the retentive area of annealed or remelted XLPE mobile components. This biomechanical study suggests that XLPE in DMC could be a safe alternative to conventional UHMWPE regarding the generation of cracks in the retentive area related to the femoral head snap-fit.

In vitro study of biodegradation of a Co-Cr alloy using a human cell culture model.

PubMed

Harmand, M F

1995-01-01

The evaluation of a potential biomaterial is based on two approaches: firstly, the study of the local and systemic effects of the biomaterial implanted in the host; and secondly the study of the behaviour of the biomaterial itself with increasing time. The progress achieved in human cell culturing allows in vitro evaluation of a new biomaterial using the human cell(s) system(s) characteristic of the tissue which it will be exposed to in vivo. This kind of approach permits the assessment of the biodegradation of a biomaterial whatever it is: metal; alloy; ceramic; glass; polymer; with or without specialized coating.... The experimental approach is as follows: discs representative of the biomaterial (surface state, cleaning, sterilization process) are manufactured in order to cover the bottom of the culture wells. Thereafter, they are either brought in the presence of complete culture medium alone, or in the presence of a subconfluent cell layer. A kinetic analysis is performed using various incubation periods at 37 degrees C. Released biodegradation products are identified and quantified, in both the medium and cell compartment, and on the other hand cytotoxicity is assessed. A Co-Cr alloy was studied over a 9-day period according to the experimental schedule, and showed a higher corrosion rate in the presence of osteoblasts in the range of 25-30%. Moreover, an intracellular uptake of both Cr and Co was detected, which will have physiological importance.

Effect of cantilever length and alloy framework on the stress distribution in peri-implant area of cantilevered implant-supported fixed partial dentures

PubMed Central

SUEDAM, Valdey; MORETTI, Rafael Tobias; SOUSA, Edson Antonio Capello; RUBO, José Henrique

2016-01-01

ABSTRACT Because many mechanical variables are present in the oral cavity, the proper load transfer between the prosthesis and the bone is important for treatment planning and for the longevity of the implant-supported fixed partial denture. Objectives To verify the stress generated on the peri-implant area of cantilevered implant-supported fixed partial dentures and the potential effects of such variable. Material and Methods A U-shaped polyurethane model simulating the mandibular bone containing two implants (Ø 3.75 mm) was used. Six groups were formed according to the alloy’s framework (CoCr or PdAg) and the point of load application (5 mm, 10 mm and 15 mm of cantilever arm). A 300 N load was applied in pre-determined reference points. The tension generated on the mesial, lingual, distal and buccal sides of the peri-implant regions was assessed using strain gauges. Results Two-way ANOVA and Tukey statistical tests were applied showing significant differences (p<0.05) between the groups. Pearson correlation test (p<0.05) was applied showing positive correlations between the increase of the cantilever arm and the deformation of the peri-implant area. Conclusions This report demonstrated the CoCr alloy shows larger compression values compared to the PdAg alloy for the same distances of cantilever. The point of load application influences the deformation on the peri-implant area, increasing in accordance with the increase of the lever arm. PMID:27119758

Large area and structured epitaxial graphene produced by confinement controlled sublimation of silicon carbide

PubMed Central

de Heer, Walt A.; Berger, Claire; Ruan, Ming; Sprinkle, Mike; Li, Xuebin; Hu, Yike; Zhang, Baiqian; Hankinson, John; Conrad, Edward

2011-01-01

After the pioneering investigations into graphene-based electronics at Georgia Tech, great strides have been made developing epitaxial graphene on silicon carbide (EG) as a new electronic material. EG has not only demonstrated its potential for large scale applications, it also has become an important material for fundamental two-dimensional electron gas physics. It was long known that graphene mono and multilayers grow on SiC crystals at high temperatures in ultrahigh vacuum. At these temperatures, silicon sublimes from the surface and the carbon rich surface layer transforms to graphene. However the quality of the graphene produced in ultrahigh vacuum is poor due to the high sublimation rates at relatively low temperatures. The Georgia Tech team developed growth methods involving encapsulating the SiC crystals in graphite enclosures, thereby sequestering the evaporated silicon and bringing growth process closer to equilibrium. In this confinement controlled sublimation (CCS) process, very high-quality graphene is grown on both polar faces of the SiC crystals. Since 2003, over 50 publications used CCS grown graphene, where it is known as the “furnace grown” graphene. Graphene multilayers grown on the carbon-terminated face of SiC, using the CCS method, were shown to consist of decoupled high mobility graphene layers. The CCS method is now applied on structured silicon carbide surfaces to produce high mobility nano-patterned graphene structures thereby demonstrating that EG is a viable contender for next-generation electronics. Here we present for the first time the CCS method that outperforms other epitaxial graphene production methods. PMID:21960446

Ultra-fast vapor generation by a graphene nano-ratchet: a theoretical and simulation study.

PubMed

Ding, Hongru; Peng, Guilong; Mo, Shenqiu; Ma, Dengke; Sharshir, Swellam Wafa; Yang, Nuo

2017-12-14

Vapor generation is of prime importance for a broad range of applications: domestic water heating, desalination and wastewater treatment, etc. However, slow and inefficient evaporation limits its development. In this study, a nano-ratchet, a multilayer graphene with cone-shaped nanopores (MGCN), to accelerate vapor generation has been proposed. By performing molecular dynamics simulation, we found that air molecules were spontaneously transported across MGCN and resulted in a remarkable pressure difference, 21 kPa, between the two sides of MGCN. We studied the dependence of the pressure difference on the ambient temperature and geometry of MGCN in detail. Through further analysis of the diffusive transport, we found that pressure difference depended on the competition between ratchet transport and Knudsen diffusion and it was further found that ratchet transport is dominant. The significant pressure difference could lead to a 15-fold or greater enhancement of vapor generation, which shows the wide applications of this nano-ratchet.

Highly Efficient White Organic Light Emitting Diodes Using New Blue Fluorescence Emitter.

PubMed

Kim, Seungho; Kim, Beomjin; Lee, Jaehyun; Yu, Young-Jun; Park, Jongwook

2015-07-01

Two different emitting compounds, 1-[1,1';3',1"]Terphenyl-5'-yl-6-(10-[1,1';3',1"]terpheny-5'-yl- anthracen-9-yl)-pyrene (TP-AP-TP) and Poly-phenylene vinylene derivative (PDY 132) were used to white OLED device. By incorporating adjacent blue and yellow emitting layers in a multi-layered structure, highly efficient white emission has been attained. The device was fabricated with a hybrid configuration structure: ITO/PEDOT (40 nm)/PDY-132 (8-50 nm)/ NPB (10 nm)/TP-AP-TP (30 nm)/Alq3 (20 nm)/LiF (1 nm)/Al (200 nm). After fixing TP-AP-TP thickness of 30 nm by evaporation, PDY-132 thickness varied with 8, 15, 35, and 50 nm by spin coating in device. The luminance efficiency of the white devices at 10 mA/cm2 were 2.93 cd/A-6.55 cd/A. One of white devices showed 6.55 cd/A and white color of (0.290, 0.331).

A Filmy Black-Phosphorus Polyimide Saturable Absorber for Q-Switched Operation in an Erbium-Doped Fiber Laser.

PubMed

Feng, Tianxian; Mao, Dong; Cui, Xiaoqi; Li, Mingkun; Song, Kun; Jiang, Biqiang; Lu, Hua; Quan, Wangmin

2016-11-11

We demonstrate an erbium-doped fiber laser passively Q-switched by a black-phosphorus polyimide film. The multi-layer black-phosphorus (BP) nanosheets were prepared via a liquid exfoliation approach exploiting N -methylpyrrolidone as the dispersion liquid. By mixing the BP nanosheets with polyimide (PI), a piece of BP-PI film was obtained after evaporating the mixture in a petri dish. The BP-PI saturable absorber had a modulation depth of 0.47% and was inserted into an erbium-doped fiber laser to realize passive Q-switched operations. The repetition rate of the Q-switched laser increased from 5.73 kHz to 31.07 kHz when the laser pump was enhanced from 31.78 mW to 231.46 mW. Our results show that PI is an excellent host material to protect BP from oxidation, and the BP-PI film can act as a promising nonlinear optical device for laser applications.

Fabrication and Characterization of Thin Film Nickel Hydroxide Electrodes for Micropower Applications.

PubMed

Falahati, Hamid; Kim, Edward; Barz, Dominik P J

2015-06-17

The utilization of micropower sources is attractive in portable microfluidic devices where only low-power densities and energy contents are required. In this work, we report on the microfabrication of patterned α-Ni(OH)2 films on glass substrates which can be used for rechargeable microbatteries as well as for microcapacitors. A multilayer deposition technique is developed based on e-beam evaporation, ultraviolet lithography, and electroplating/electrodeposition which creates thin-film electrodes that are patterned with arrays of micropillars. The morphology and the structure of the patterned electrode films are characterized by employing field emission scanning electron microscopy. The chemical (elemental) composition is investigated by using X-ray diffraction and X-ray photoelectron spectroscopy. Finally, cyclic voltammetry, electrochemical impedance spectroscopy, and galvanostatic charge/discharge measurements are used to evaluate the electrochemical performance of the patterned thin film electrodes compared to patternless electrodes. We observe that patterning of the electrodes results in significantly improved stability and, thus, longer endurance while good electrochemical performance is maintained.

Surface studies of thermionic cathodes and the mechanism of operation of an impregnated tungsten cathode

NASA Technical Reports Server (NTRS)

Forman, R.

1976-01-01

The surface properties of conventional impregnated cathodes were investigated by the use of Auger spectroscopy and work function measurements, and these were compared with a synthesized barium or barium oxide coated tungsten surface. The barium and barium oxide coated surfaces were prepared by evaporating barium onto a tungsten surface that can be heated to elevated temperatures. Multilayer or monolayer coverages can be investigated using this technique. The results of this study show that the surface of an impregnated tungsten cathode is identical to that observed for a synthesized monolayer or partial monolayer of barium on partially oxidized tungsten, using the criteria of identical Auger patterns and work functions. Desorption measurements of barium from a tungsten surface were also made. These results in conjunction with Auger and work function data were interpreted to show that throughout most of its life an impregnated cathode operating in the range of 1100 C has a partial monolayer rather than a monolayer of barium on its surface.

Spectral tailoring of nanoscale EUV and soft x-ray multilayer optics

NASA Astrophysics Data System (ADS)

Huang, Qiushi; Medvedev, Viacheslav; van de Kruijs, Robbert; Yakshin, Andrey; Louis, Eric; Bijkerk, Fred

2017-03-01

Extreme ultraviolet and soft X-ray (XUV) multilayer optics have experienced significant development over the past few years, particularly on controlling the spectral characteristics of light for advanced applications like EUV photolithography, space observation, and accelerator- or lab-based XUV experiments. Both planar and three dimensional multilayer structures have been developed to tailor the spectral response in a wide wavelength range. For the planar multilayer optics, different layered schemes are explored. Stacks of periodic multilayers and capping layers are demonstrated to achieve multi-channel reflection or suppression of the reflective properties. Aperiodic multilayer structures enable broadband reflection both in angles and wavelengths, with the possibility of polarization control. The broad wavelength band multilayer is also used to shape attosecond pulses for the study of ultrafast phenomena. Narrowband multilayer monochromators are delivered to bridge the resolution gap between crystals and regular multilayers. High spectral purity multilayers with innovated anti-reflection structures are shown to select spectrally clean XUV radiation from broadband X-ray sources, especially the plasma sources for EUV lithography. Significant progress is also made in the three dimensional multilayer optics, i.e., combining micro- and nanostructures with multilayers, in order to provide new freedom to tune the spectral response. Several kinds of multilayer gratings, including multilayer coated gratings, sliced multilayer gratings, and lamellar multilayer gratings are being pursued for high resolution and high efficiency XUV spectrometers/monochromators, with their advantages and disadvantages, respectively. Multilayer diffraction optics are also developed for spectral purity enhancement. New structures like gratings, zone plates, and pyramids that obtain full suppression of the unwanted radiation and high XUV reflectance are reviewed. Based on the present achievement of the spectral tailoring multilayer optics, the remaining challenges and opportunities for future researches are discussed.

Structural and magnetic properties and superconductivity in Ba(Fe 1-xTM x) 2As 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Thaler, Alexander

2012-01-01

We studied the effects on structural and magnetic phase transitions and the emergence of superconductivity in transition metal substituted BaFe 2As 2. We grew four series of Ba(Fe 1-xTM 2) 2As 2 (TM=Ru, Mn, Co+Cr and Co+Mn) and characterized them by crystallographic, magnetic and transport measurements. We also subjected Ba(Fe 1-xCr x) 2As 2 and Ba(Fe 1-xCo x) 2As 2 to heat treatment to explore what changes might be induced.

Distributed Computer Systems for the Republic of Turkish Navy.

DTIC Science & Technology

1985-12-01

and the entire medium spectrum is consumed by the signal. Baseband LAN’s are typically accessed via a carrier sensed multi-access collision detect...Process IPrcoess 2 Cocr~un i cat i Ots B uffer Buffer 6.:,e~2er 1. t -s cessage c~.ur2:s I.essage okul.ks "r, Prcesse eroes pac: et 5packet S et t4Qet...control. a. Routing Routing is the decision process which determines the path a message follows from its source to its destina- tion. Some routing

Novel materials as potential infrared laser hosts

NASA Astrophysics Data System (ADS)

Sarkies, Julian Richard

The work presented in this thesis has concentrated on an assessment and characterisation of potential laser host media which will only support low phonon or vibrational modes. This is a necessary criterion if systems in which the active ions are lanthanides are to be made to lase in the mid-infrared, as in conventional host media non- radiative processes dominate transitions in this region. Research has concentrated upon two main areas. Firstly a spectroscopic study of lanthanide doped PBr3/AlBr3/SbBr3 was undertaken. A detailed investigation and characterisation of the stable solution formation region was carried out. The doping levels achievable were seen to vary across the lanthanide series from a maximum 0.24mol% for praesodymium to a minimum 0.15mol% for ytterbium. Energies of the characteristic 4 f absorptions of the trivalent lanthanides were measured, along with their oscillator strengths. Judd-Ofelt parameters were found for several rare earths. Stimulated emission cross sections were found to be higher than in conventional glass hosts for certain transitions, such as 6.83 × 10 -20 cm2 for the 4F3/2 --> 4I11/2 transition in the Nd3+ doped liquid. This was verified both experimentally and by the Ladenburg-Fuchtbauer relation when compared to a standard silicate glass. The behaviour, both spectroscopic and physical, of the doped solutions was seen to change dramatically upon heating. Heating the solutions gave rise to higher crystallisation rates, but lower non-radiative relaxation rates. Waveguide and laser experiments were attempted in both bulk and capillary geometries, however material factors such as crystallisation and thermal lensing prevented laser action. Secondly, rare earth doped planar waveguides of zinc sulphide were prepared. A full characterisation of the way in which waveguide loss was affected by factors such as deposition rate, doping level and waveguide masking during evaporation was performed. Waveguide losses as low as 1.5dB/cm at 980nm were measured. The loss was seen to have a strong λ-4 dependence, indicating it was predominantly due to Rayleigh scattering. Deposition onto heated substrates and post deposition annealing increased the loss significantly. Shielding the substrate from the radiant heating of the evaporation boat by partial masking of the substrate reduced the loss significantly. Doping the films caused a large increase in the loss for dopant concentrations of above 0.8mol%. Emission was observed from both Er3+ and Nd 3+ doped waveguides, and fluorescent lifetimes measured. The emission cross sections were measured for the 4F3/2 --> 4I11/2 transition in the Nd3+ doped waveguide, and for the 4I13/2 --> 4I 15/2 transition in the Er3+ doped waveguide. Multilayer dielectric mirrors were deposited onto the ends of a Nd3+ doped waveguide, forming a fully integrated resonator. The low damage threshold of the multilayer coatings precluded laser action. These results are believed to be the first ever reported for thermally evaporated doped zinc sulphide waveguides. This system has shown considerable promise as an infrared laser host, the future implications of this work are discussed and possible directions for future research suggested.

Directing the assembly of nanostructured films with living cells

NASA Astrophysics Data System (ADS)

Brinker, C. Jeffrey

2007-03-01

This talk describes our recent discovery of the ability of living cells to organize extended nanostructures and nano-objects in a manner that creates a unique, highly biocompatible nano//bio interface (Science 313, 337-340, 2006). We find that, using short chain phospholipids to direct the formation of thin film silica mesophases during evaporation-induced self-assembly, the introduction of cells (so far yeast and bacteria) alters profoundly the inorganic self-assembly pathway. Cells actively organize around themselves an ordered, multilayered lipid-membrane that interfaces coherently with a lipid-templated silica mesophase. This bio/nano interface is unique in that it withstands drying (even evacuation) without cracking or the development of tensile stresses -- yet it maintains accessibility to molecules, proteins/antibodies, plasmids, etc - introduced into the 3D silica host. Additionally cell viability is preserved for weeks to months in the absence of buffer, making these constructs useful as standalone cell-based sensors. The bio/nano interfaces we describe do not form `passively' -- rather they are a consequence of the cell's ability to sense and actively respond to external stimuli. During EISA, solvent evaporation concentrates the extracellular environment in osmolytes. In response to this hyperosmotic stress, the cells release water, creating a gradient in pH, which is maintained within the adjoining nanostructured host and serves to localize lipids, proteins, plasmids, lipidized nanocrystals, and a variety of other components at the cellular surface. This active organization of the bio/nano interface can be accomplished during ink-jet printing or selective wetting -- processes allowing patterning of cellular arrays - and even spatially-defined genetic modification.

NASA Tech Briefs, May 2007

NASA Technical Reports Server (NTRS)

2007-01-01

Topics include: Noise-Canceling Helmet Audio System; Program Analyzes Spacecraft/Ground Radio Links; Two-Way Communication Using RFID Equipment and Techniques; Six-Message Electromechanical Display System; Scanning Terahertz Heterodyne Imaging Systems; Master Clock and Time-Signal-Distribution System; Synchronous Phase-Resolving Flash Range Imaging; Integrated Radial Probe Transition From MMIC to Waveguide; Bar-Code System for a Microbiological Laboratory; MMIC Amplifier Produces Gain of 10 dB at 235 GHz; Mapping Nearby Terrain in 3D by Use of a Grid of Laser Spots; Digital Beam Deflectors Based Partly on Liquid Crystals; Narrow-Band WGM Optical Filters With Tunable FSRs; Better Finite-Element Analysis of Composite Shell Structures; Computing Spacecraft-Pointing Vectors for Limb Tracking; Enhanced Master Controller Unit Tester; Rover Graphical Simulator; Increasing Durability of Flame-Sprayed Strain Gauges; Multifunctional, High-Temperature Nanocomposites; Multilayer Impregnated Fibrous Thermal Insulation Tiles; Radiation-Shielding Polymer/Soil Composites; Film/Adhesive Processing Module for Fiber-Placement Processing of Composites; Fabrication of Submillimeter Axisymmetric Optical Components; Electrochemical Disposal of Hydrazines in Water; Statistical Model of Evaporating Multicomponent Fuel Drops; Resistively Heated SiC Nozzle for Generating Molecular Beams; Compact Packaging of Photonic Millimeter-Wave Receiver; Diffractive Combiner of Single-Mode Pump Laser-Diode Beams; Wide-Band, High-Quantum-Efficiency Photodetector; A Robustly Stabilizing Model Predictive Control Algorithm; Modeling Evaporation of Drops of Different Kerosenes; Development of Vapor-Phase Catalytic Ammonia Removal System; Several Developments in Space Tethers; Design Concept for a Nuclear Reactor-Powered Mars Rover; Formation-Initialization Algorithm for N Spacecraft; and DNSs of Multicomponent Gaseous and Drop-Laden Mixing Layers Achieving Transition to Turbulence.

In-stent neoatherosclerosis and tissue characteristics of restenotic lesions following implantation of second generation drug-eluting stents in unrestricted coronary lesions: Optical frequency domain imaging study.

PubMed

Sabbah, Mahmoud; Kadota, Kazushige; El-Eraky, Azza; Kamal, Hanan M; Abdellah, Ahmed-Tageldien; El Hawary, Ahmed

2017-06-01

Differences in stent platform, polymer coatings, and antirestenotic drugs among the current in use second-generation drug-eluting stents (G2-DESs) may induce significant variations in neointimal response and vascular healing, which may impact the prevalence of neoatherosclerosis (NA) and morphological appearance of the restenotic tissue. Utilizing Optical frequency domain imaging, two independent reviewers, retrospectively compared the prevalence of neoatherosclerosis (NA), and the morphological differences, and tissue characteristics of 50 G2-DESs in-stent restenosis (ISR) lesions (35 everolimus-eluting stent [22 cobalt-chromium (CoCr), 13 platinum-chromium (PtCr)], and 15 biolimus-eluting stent [BES]) implanted liberally in unrestricted coronary lesions. More than half of the stents were implanted in type C lesions, while 40% of the stents were implanted primarily in lesions with recanalized chronic total occlusion. NA, defined as a neointima formation with the presence of lipids or calcification, was observed in fewer than half (24/50) of all ISR lesions with no significant in-between group differences (41%, 69%, and 40% in CoCr, PtCr, and BES respectively, P = 0.22), nor were there any significant differences in the morphological appearance or tissue characteristics between all G2-DESs subtypes. Acknowledging some limitations, our results may suggest that the prevalence of NA and the morphological appearance of restenotic lesions might not differ when G2-DESs are implanted in unrestricted, rather complex, coronary lesions. © 2017, Wiley Periodicals, Inc.

[The effects of different welding wires on the mechanical properties of laser welding joints].

PubMed

Huang, Qing-feng; Zhang, Jian-zhong; Jiang, Wei-dong; Li, Quan; Yu, Jin-xing

2006-08-01

To evaluate the mechanical properties and microstructure of laser-welded joints with different welding wires for clinical use of welding wire. The standard tensile test and three-point bending test rods were made from Co-Cr and Ni-Cr alloy, and were laser-welded with different welding wire (commercially welding wire and casting wire). Then the tensile rods were tested for the ultimate tensile strength (UTS), and the bending rods for the ultimate bending strength (UBS). The results was analyzed by one-way ANOVA. The tensile fracture surface were examined by scanning electron microscopy (SEM). Metallurgical analysis were also performed on polished longitudinal sectioned samples. For Co-Cr alloy, the UTS of casting wire group and commercially welding wire group was respectively (606.40+/-82.53)MPa and (693.61+/-47.68)MPa; the UBS was respectively (997.95+/-88.89)MPa and (1160.76+/-91.59)MPa. ANOVA showed a significant difference of UTS and UBS between the two groups at the 0.05 level (P<0.05). For Ni-Cr alloy, the UTS of casting wire group and commercially welding wire group was respectively (558.14+/-46.75)MPa and (582.32+/-35.43)MPa; the UBS was respectively (1084.75+/-46.02)MPa and (1078.29+/-36.25)MPa. There was no significant difference between the two groups (P>0.05). SEM and metallurgical examination showed the welded zone exhibiting more cracks in the casting wire group than in the commercially welding wire group. It would be advisable to work with commercially welding wire for the joints that need better strength.

[The study of the colorimetric characteristics of the cobalt-chrome alloys abutments covered by four different all-ceramic crowns by using dental spectrophotometer].

PubMed

Chen, Yifan; Liu, Hongchun; Meng, Yukun; Chao, Yonglie; Liu, Changhong

2015-06-01

This study aims to evaluate the optical data of the different sites of the cobalt-chrome (Co-Cr) alloy abutments covered by four different all-ceramic crowns and the color difference between the crowns and target tab using a digital dental spectrophotometer. Ten Co-Cr alloy abutments were made and tried in four different groups of all-ceramic crowns, namely, Procera aluminia, Procera zirconia, Lava zirconia (Lava-Zir), and IPS E.max glass-ceramic lithium disilicate-reinforced monolithic. The color data of the cervical, body, and incisal sites of the samples were recorded and analyzed by dental spectrophotometer. The CIE L*, a*, b* values were again measured after veneering. The color difference between the abutments covered by all-ceramic crowns and A2 dentine shade tab was evaluated. The L* and b* values of the abutments can be increased by all of the four groups of all-ceramic copings, but a* values were decreased in most groups. A statistical difference was observed among four groups. After being veneered, the L* values of all the copings declined slightly, and the values of a*, b* increased significantly. When compared with A2 dentine shade tab, the ΔE of the crowns was below 4. Four ceramic copings were demonstrated to promote the lightness and hue of the alloy abutments effecttively. Though the colorimetric baseline of these copings was uneven, veneer porcelain can efficiently decrease the color difference between the samples and thee target.

Mechanical and interfacial characterization of laser welded Co-Cr alloy with different joint configurations

PubMed Central

Kokolis, John; Chakmakchi, Makdad; Theocharopoulos, Antonios; Prombonas, Anthony

2015-01-01

PURPOSE The mechanical and interfacial characterization of laser welded Co-Cr alloy with two different joint designs. MATERIALS AND METHODS Dumbbell cast specimens (n=30) were divided into 3 groups (R, I, K, n=10). Group R consisted of intact specimens, group I of specimens sectioned with a straight cut, and group K of specimens with a 45° bevel made at the one welding edge. The microstructure and the elemental distributions of alloy and welding regions were examined by an SEM/EDX analysis and then specimens were loaded in tension up to fracture. The tensile strength (TS) and elongation (ε) were determined and statistically compared among groups employing 1-way ANOVA, SNK multiple comparison test (α=.05) and Weibull analysis where Weibull modulus m and characteristic strength σο were identified. Fractured surfaces were imaged by a SEM. RESULTS SEM/EDX analysis showed that cast alloy consists of two phases with differences in mean atomic number contrast, while no mean atomic number was identified for welded regions. EDX analysis revealed an increased Cr and Mo content at the alloy-joint interface. All mechanical properties of group I (TS, ε, m and σο) were found inferior to R while group K showed intermediated values without significant differences to R and I, apart from elongation with group R. The fractured surfaces of all groups showed extensive dendritic pattern although with a finer structure in the case of welded groups. CONCLUSION The K shape joint configuration should be preferred over the I, as it demonstrates improved mechanical strength and survival probability. PMID:25722836

Design and development of novel MRI compatible zirconium- ruthenium alloys with ultralow magnetic susceptibility.

PubMed

Li, H F; Zhou, F Y; Li, L; Zheng, Y F

2016-04-19

In the present study, novel MRI compatible zirconium-ruthenium alloys with ultralow magnetic susceptibility were developed for biomedical and therapeutic devices under MRI diagnostics environments. The results demonstrated that alloying with ruthenium into pure zirconium would significantly increase the strength and hardness properties. The corrosion resistance of zirconium-ruthenium alloys increased significantly. High cell viability could be found and healthy cell morphology observed when culturing MG 63 osteoblast-like cells and L-929 fibroblast cells with zirconium-ruthenium alloys, whereas the hemolysis rates of zirconium-ruthenium alloys are <1%, much lower than 5%, the safe value for biomaterials according to ISO 10993-4 standard. Compared with conventional biomedical 316L stainless steel, Co-Cr alloys and Ti-based alloys, the magnetic susceptibilities of the zirconium-ruthenium alloys (1.25 × 10(-6) cm(3)·g(-1)-1.29 × 10(-6) cm(3)·g(-1) for zirconium-ruthenium alloys) are ultralow, about one-third that of Ti-based alloys (Ti-6Al-4V, ~3.5 × 10(-6) cm(3)·g(-1), CP Ti and Ti-6Al-7Nb, ~3.0 × 10(-6) cm(3)·g(-1)), and one-sixth that of Co-Cr alloys (Co-Cr-Mo, ~7.7 × 10(-6) cm(3)·g(-1)). Among the Zr-Ru alloy series, Zr-1Ru demonstrates enhanced mechanical properties, excellent corrosion resistance and cell viability with lowest magnetic susceptibility, and thus is the optimal Zr-Ru alloy system as therapeutic devices under MRI diagnostics environments.

Film growth, adsorption and desorption kinetics of indigo on SiO2

PubMed Central

Scherwitzl, Boris; Resel, Roland; Winkler, Adolf

2015-01-01

Organic dyes have recently been discovered as promising semiconducting materials, attributable to the formation of hydrogen bonds. In this work, the adsorption and desorption behavior, as well as thin film growth was studied in detail for indigo molecules on silicon dioxide with different substrate treatments. The material was evaporated onto the substrate by means of physical vapor deposition under ultra-high vacuum conditions and was subsequently studied by Thermal Desorption Spectroscopy (TDS), Auger Electron Spectroscopy, X-Ray Diffraction, and Atomic Force Microscopy. TDS revealed initially adsorbed molecules to be strongly bonded on a sputter cleaned surface. After further deposition a formation of dimers is suggested, which de-stabilizes the bonding mechanism to the substrate and leads to a weakly bonded adsorbate. The dimers are highly mobile on the surface until they get incorporated into energetically favourable three-dimensional islands in a dewetting process. The stronger bonding of molecules within those islands could be shown by a higher desorption temperature. On a carbon contaminated surface no strongly bonded molecules appeared initially, weakly bonded monomers rather rearrange into islands at a surface coverage that is equivalent to one third of a monolayer of flat-lying molecules. The sticking coefficient was found to be unity on both substrates. The desorption energies from carbon covered silicon dioxide calculated to 1.67 ± 0.05 eV for multilayer desorption from the islands and 0.84 ± 0.05 eV for monolayer des orption. Corresponding values for desorption from a sputter cleaned surface are 1.53 ± 0.05 eV for multilayer and 0.83 ± 0.05 eV for monolayer desorption. PMID:24832297

Film growth, adsorption and desorption kinetics of indigo on SiO{sub 2}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Scherwitzl, Boris, E-mail: b.scherwitzl@tugraz.at; Resel, Roland; Winkler, Adolf

2014-05-14

Organic dyes have recently been discovered as promising semiconducting materials, attributable to the formation of hydrogen bonds. In this work, the adsorption and desorption behavior, as well as thin film growth was studied in detail for indigo molecules on silicon dioxide with different substrate treatments. The material was evaporated onto the substrate by means of physical vapor deposition under ultra-high vacuum conditions and was subsequently studied by Thermal Desorption Spectroscopy (TDS), Auger Electron Spectroscopy, X-Ray Diffraction, and Atomic Force Microscopy. TDS revealed initially adsorbed molecules to be strongly bonded on a sputter cleaned surface. After further deposition a formation ofmore » dimers is suggested, which de-stabilizes the bonding mechanism to the substrate and leads to a weakly bonded adsorbate. The dimers are highly mobile on the surface until they get incorporated into energetically favourable three-dimensional islands in a dewetting process. The stronger bonding of molecules within those islands could be shown by a higher desorption temperature. On a carbon contaminated surface no strongly bonded molecules appeared initially, weakly bonded monomers rather rearrange into islands at a surface coverage that is equivalent to one third of a monolayer of flat-lying molecules. The sticking coefficient was found to be unity on both substrates. The desorption energies from carbon covered silicon dioxide calculated to 1.67 ± 0.05 eV for multilayer desorption from the islands and 0.84 ± 0.05 eV for monolayer desorption. Corresponding values for desorption from a sputter cleaned surface are 1.53 ± 0.05 eV for multilayer and 0.83 ± 0.05 eV for monolayer desorption.« less

Film growth, adsorption and desorption kinetics of indigo on SiO2.

PubMed

Scherwitzl, Boris; Resel, Roland; Winkler, Adolf

2014-05-14

Organic dyes have recently been discovered as promising semiconducting materials, attributable to the formation of hydrogen bonds. In this work, the adsorption and desorption behavior, as well as thin film growth was studied in detail for indigo molecules on silicon dioxide with different substrate treatments. The material was evaporated onto the substrate by means of physical vapor deposition under ultra-high vacuum conditions and was subsequently studied by Thermal Desorption Spectroscopy (TDS), Auger Electron Spectroscopy, X-Ray Diffraction, and Atomic Force Microscopy. TDS revealed initially adsorbed molecules to be strongly bonded on a sputter cleaned surface. After further deposition a formation of dimers is suggested, which de-stabilizes the bonding mechanism to the substrate and leads to a weakly bonded adsorbate. The dimers are highly mobile on the surface until they get incorporated into energetically favourable three-dimensional islands in a dewetting process. The stronger bonding of molecules within those islands could be shown by a higher desorption temperature. On a carbon contaminated surface no strongly bonded molecules appeared initially, weakly bonded monomers rather rearrange into islands at a surface coverage that is equivalent to one third of a monolayer of flat-lying molecules. The sticking coefficient was found to be unity on both substrates. The desorption energies from carbon covered silicon dioxide calculated to 1.67 ± 0.05 eV for multilayer desorption from the islands and 0.84 ± 0.05 eV for monolayer desorption. Corresponding values for desorption from a sputter cleaned surface are 1.53 ± 0.05 eV for multilayer and 0.83 ± 0.05 eV for monolayer desorption.

The effect of repeated lateral compression and expansions mimicking blinking on selected tear film polar lipid monofilms.

PubMed

Patterson, Matthew; Vogel, Hans J; Prenner, Elmar J

2017-03-01

The tear film lipid layer is formed on the anterior surface of the eye, functioning as a barrier to excess evaporation and foreign particles, while also providing stability to the tear film. The lipid layer is organized into a polar lipid layer consisting of phospholipids, ceramides, and free fatty acids that act as a surfactant to a non-polar multilayer of wax and cholesterol esters. Due to shear forces from eye movement and the compression and expansion of blinking, the tear lipids are under constant stress. However, tear film is able to resist immediate rupture and remains intact over multiple blinks. This work aimed to better understand the lateral organization of selected tear film polar lipids. The polar lipid biomimetic studied here consisted of dipalmitoyl phosphatidylcholine (DPPC), dipalmitoyl phosphatidylethanolamine (DPPE), palmitoyl glucosylceramide (PGC), and palmitoyl sphingomyelin (PSM). Surface pressure-area isocycles mimicked blinking and films were visualized by Brewster angle microscopy (BAM). All lipid systems formed relatively reversible films as indicated by limited hysteresis. However, pure DPPC and PSM films experienced greater changes in lipid packing upon compression and expansion compared to pure PGC and DPPE. This suggests that the driving force behind maintaining the lateral organization of the polar lipids from tear film may be the hydrogen bonding propensities of the head groups. Additionally, isocycles of films containing DPPC, DPPE, and PGC mixtures exhibited evidence for reversible multilayer formation or folding. This was supported by 3D analysis of structures that formed during compression but reintegrated back into the bulk lipid film during expansion near the in vitro tear film surface pressure of the open eye. Therefore, the polar lipids of tear film may be directly involved in preventing film rupture during a blink. Copyright © 2016 Elsevier B.V. All rights reserved.

Properties of AlF3 and LaF3 films at 193nm

NASA Astrophysics Data System (ADS)

Xue, Chunrong; Shao, Jianda

2010-10-01

In order to develop low loss, high-performance 193nm Fluoride HR mirrors and anti-reflection coatings, LaF3 and AlF3 materials, used for a single-layer coating, were deposited by a molybdenum boat evaporation process. Various microstructures that formed under different substrate temperatures and with deposition rates were investigated. The relation between these microstructures (including cross section morphology, surface roughness and crystalline structure), the optical properties (including refractive index and optical loss) and mechanical properties (stress) were investigated. Furthermore, AlF3 used as a low-index material and LaF3 used as a high-index material were designed and deposited for multilayer coatings. Transmittance, reflectance, stress, and the laser-induced damage threshold (LIDT) were studied. It is shown that AlF3 and LaF3 thin films, deposited on the substrate at a temperature of 300 °C, obtained good quality thin films with high transmittance and little optical loss at 193 nm. For multilayer coatings, the absorption mainly comes from LaF3. Based on these studies, The thickness of 193nm films was controled by a 1/3 baffle with pre-coating technology. the LaF3/AlF3 AR coantings and HR mirrors at 193nm were designed and deposited. Under the present experimental conditions, the reflectance of LaF3/AlF3 HR mirror is up to 96%, and its transmittance is 1.5%. the LaF3/AlF3 AR coanting's residual reflectance is less than 0.14%, and single-sided transmittance is 93.85%. To get a high-performance 193nm AR coating, super-polished substrate is the best choice.

Zone compensated multilayer laue lens and apparatus and method of fabricating the same

DOEpatents

Conley, Raymond P.; Liu, Chian Qian; Macrander, Albert T.; Yan, Hanfei; Maser, Jorg; Kang, Hyon Chol; Stephenson, Gregory Brian

2015-07-14

A multilayer Laue Lens includes a compensation layer formed in between a first multilayer section and a second multilayer section. Each of the first and second multilayer sections includes a plurality of alternating layers made of a pair of different materials. Also, the thickness of layers of the first multilayer section is monotonically increased so that a layer adjacent the substrate has a minimum thickness, and the thickness of layers of the second multilayer section is monotonically decreased so that a layer adjacent the compensation layer has a maximum thickness. In particular, the compensation layer of the multilayer Laue lens has an in-plane thickness gradient laterally offset by 90.degree. as compared to other layers in the first and second multilayer sections, thereby eliminating the strict requirement of the placement error.

Micromechanical Properties of Nanostructured Clay-Oxide Multilayers Synthesized by Layer-by-Layer Self-Assembly.

PubMed

Hou, Dongwei; Zhang, Guoping; Pant, Rohit Raj; Wei, Zhongxin; Shen, Shuilong

2016-11-08

Clay-based nanostructured multilayers, such as clay-polymer multilayers and clay-oxide multilayers, have attracted growing attention owing to their remarkable mechanical properties and promising application in various fields. In this paper, synthesis of a new kind of nanostructured clay-oxide multilayers by layer-by-layer self-assembly was explored. Nano-mechanical characterization of 18 clay-based multilayer samples, prepared under as-deposited (i.e., air-dried) and annealing conditions at 400 °C/600 °C with different precursor cations and multilayer structure, were carried out using nanoindentation testing, atomic force microscopy (AFM), and X-ray diffraction (XRD). The influencing factors, including as-deposited and annealing conditions and clay concentrations on the mechanical properties were analyzed. Results show that all of the multilayers exhibit high bonding strength between interlayers. Higher modulus and hardness of clay-based multilayers were obtained with lower clay concentrations than that with higher clay concentrations. Different relationships between the modulus and hardness and the annealing temperature exist for a specific type of clay-oxide multilayer. This work offers the basic and essential knowledge on design of clay-based nanostructured multilayers by layer-by-layer self-assembly.

Identification of ground-state spin ordering in antiferromagnetic transition metal oxides using the Ising model and a genetic algorithm

PubMed Central

Lee, Kyuhyun; Youn, Yong; Han, Seungwu

2017-01-01

Abstract We identify ground-state collinear spin ordering in various antiferromagnetic transition metal oxides by constructing the Ising model from first-principles results and applying a genetic algorithm to find its minimum energy state. The present method can correctly reproduce the ground state of well-known antiferromagnetic oxides such as NiO, Fe2O3, Cr2O3 and MnO2. Furthermore, we identify the ground-state spin ordering in more complicated materials such as Mn3O4 and CoCr2O4. PMID:28458746

Cemented fixation with PMMA or Bis-GMA resin hydroxyapatite cement: effect of implant surface roughness.

PubMed

Walsh, W R; Svehla, M J; Russell, J; Saito, M; Nakashima, T; Gillies, R M; Bruce, W; Hori, R

2004-09-01

Implant surface roughness is an important parameter governing the overall mechanical properties at the implant-cement interface. This study investigated the influence of surface roughness using polymethylmethcrylate (PMMA) and a Bisphenol-a-glycidylmethacyrlate resin-hydroxyapatite cement (CAP). Mechanical fixation at the implant-cement interface was evaluated in vitro using static shear and fatigue loading with cobalt chrome alloy (CoCr) dowels with different surface roughness preparations. Increasing surface roughness improved the mechanical properties at the implant-cement interface for both types of cement. CAP cement fixation was superior to PMMA under static and dynamic loading.

Method to adjust multilayer film stress induced deformation of optics

DOEpatents

Spiller, Eberhard A.; Mirkarimi, Paul B.; Montcalm, Claude; Bajt, Sasa; Folta, James A.

2000-01-01

Stress compensating systems that reduces/compensates stress in a multilayer without loss in reflectivity, while reducing total film thickness compared to the earlier buffer-layer approach. The stress free multilayer systems contain multilayer systems with two different material combinations of opposite stress, where both systems give good reflectivity at the design wavelengths. The main advantage of the multilayer system design is that stress reduction does not require the deposition of any additional layers, as in the buffer layer approach. If the optical performance of the two systems at the design wavelength differ, the system with the poorer performance is deposited first, and then the system with better performance last, thus forming the top of the multilayer system. The components for the stress reducing layer are chosen among materials that have opposite stress to that of the preferred multilayer reflecting stack and simultaneously have optical constants that allow one to get good reflectivity at the design wavelength. For a wavelength of 13.4 nm, the wavelength presently used for extreme ultraviolet (EUV) lithography, Si and Be have practically the same optical constants, but the Mo/Si multilayer has opposite stress than the Mo/Be multilayer. Multilayer systems of these materials have practically identical reflectivity curves. For example, stress free multilayers can be formed on a substrate using Mo/Be multilayers in the bottom of the stack and Mo/Si multilayers at the top of the stack, with the switch-over point selected to obtain zero stress. In this multilayer system, the switch-over point is at about the half point of the total thickness of the stack, and for the Mo/Be--Mo/Si system, there may be 25 deposition periods Mo/Be to 20 deposition periods Mo/Si.

Magnetic multilayer structure

DOEpatents

Herget, Philipp; O'Sullivan, Eugene J.; Romankiw, Lubomyr T.; Wang, Naigang; Webb, Bucknell C.

2016-07-05

A mechanism is provided for an integrated laminated magnetic device. A substrate and a multilayer stack structure form the device. The multilayer stack structure includes alternating magnetic layers and diode structures formed on the substrate. Each magnetic layer in the multilayer stack structure is separated from another magnetic layer in the multilayer stack structure by a diode structure.

Magnetic multilayer structure

DOEpatents

Herget, Philipp; O'Sullivan, Eugene J.; Romankiw, Lubomyr T.; Wang, Naigang; Webb, Bucknell C.

2017-03-21

A mechanism is provided for an integrated laminated magnetic device. A substrate and a multilayer stack structure form the device. The multilayer stack structure includes alternating magnetic layers and diode structures formed on the substrate. Each magnetic layer in the multilayer stack structure is separated from another magnetic layer in the multilayer stack structure by a diode structure.

Numerical simulation and experiment on multilayer stagger-split die.

PubMed

Liu, Zhiwei; Li, Mingzhe; Han, Qigang; Yang, Yunfei; Wang, Bolong; Sui, Zhou

2013-05-01

A novel ultra-high pressure device, multilayer stagger-split die, has been constructed based on the principle of "dividing dies before cracking." Multilayer stagger-split die includes an encircling ring and multilayer assemblages, and the mating surfaces of the multilayer assemblages are mutually staggered between adjacent layers. In this paper, we investigated the stressing features of this structure through finite element techniques, and the results were compared with those of the belt type die and single split die. The contrast experiments were also carried out to test the bearing pressure performance of multilayer stagger-split die. It is concluded that the stress distributions are reasonable and the materials are utilized effectively for multilayer stagger-split die. And experiments indicate that the multilayer stagger-split die can bear the greatest pressure.

MoRu/Be multilayers for extreme ultraviolet applications

DOEpatents

Bajt, Sasa C.; Wall, Mark A.

2001-01-01

High reflectance, low intrinsic roughness and low stress multilayer systems for extreme ultraviolet (EUV) lithography comprise amorphous layers MoRu and crystalline Be layers. Reflectance greater than 70% has been demonstrated for MoRu/Be multilayers with 50 bilayer pairs. Optical throughput of MoRu/Be multilayers can be 30-40% higher than that of Mo/Be multilayer coatings. The throughput can be improved using a diffusion barrier to make sharper interfaces. A capping layer on the top surface of the multilayer improves the long-term reflectance and EUV radiation stability of the multilayer by forming a very thin native oxide that is water resistant.

Piezoelectric polymer multilayer on flexible substrate for energy harvesting.

PubMed

Zhang, Lei; Oh, Sharon Roslyn; Wong, Ting Chong; Tan, Chin Yaw; Yao, Kui

2013-09-01

A piezoelectric polymer multilayer structure formed on a flexible substrate is investigated for mechanical energy harvesting under bending mode. Analytical and numerical models are developed to clarify the effect of material parameters critical to the energy harvesting performance of the bending multilayer structure. It is shown that the maximum power is proportional to the square of the piezoelectric stress coefficient and the inverse of dielectric permittivity of the piezoelectric polymer. It is further found that a piezoelectric multilayer with thinner electrodes can generate more electric energy in bending mode. The effect of improved impedance matching in the multilayer polymer on energy output is remarkable. Comparisons between piezoelectric ceramic multilayers and polymer multilayers on flexible substrate are discussed. The fabrication of a P(VDF-TrFE) multilayer structure with a thin Al electrode layer is experimentally demonstrated by a scalable dip-coating process on a flexible aluminum substrate. The results indicate that it is feasible to produce a piezoelectric polymer multilayer structure on flexible substrate for harvesting mechanical energy applicable for many low-power electronics.

Stress Compensating Multilayers

NASA Technical Reports Server (NTRS)

Broadway, David M.; Ramsey, Brian D.; O'dell, Stephen; Gurgew, Danielle

2017-01-01

We present in-situ stress measurement results for single and multilayer thin-films deposited by magnetron sputtering. In particular, we report on the influence of the material interfaces on the ensuing stress in both the transient and steady-state regimes of film growth. This behavior is used to determine the appropriate thicknesses of the constituent layers that will result in a net tensile stress in multilayers composed of various material combinations. These multilayers can then be used to compensate the compressive integrated stress in single and multilayer EUV and x-ray optical coatings. The use of multilayers to compensate the integrated stress might be advantageous because, unlike single layers of chromium, the roughness is not expected to increase with the total thickness of the multilayer. In this paper, we demonstrate the technique for W/Si and Mo/Si multilayers and discuss its application to other material combinations.

Investigation of cross-linking characteristics of novel hole-transporting materials for solution-processed phosphorescent OLEDs

NASA Astrophysics Data System (ADS)

Lee, Jaemin; Ameen, Shahid; Lee, Changjin

2016-04-01

After the success of commercialization of the vacuum-evaporated organic light-emitting diodes (OLEDs), solutionprocessing or printing of OLEDs are currently attracting much research interests. However, contrary to various kinds of readily available vacuum-evaporable OLED materials, the solution-processable OLED materials are still relatively rare. Hole-transporting layer (HTL) materials for solution-processed OLEDs are especially limited, because they need additional characteristics such as cross-linking to realize multilayer structures in solution-processed OLEDs, as well as their own electrically hole-transporting characteristics. The presence of such cross-linking characteristics of solutionprocessable HTL materials therefore makes them more challenging in the development stage, and also makes them essence of solution-processable OLED materials. In this work, the structure-property relationships of thermally crosslinkable HTL materials were systematically investigated by changing styrene-based cross-linking functionalities and modifying the carbazole-based hole-transporting core structures. The temperature dependency of the cross-linking characteristics of the HTL materials was systematically investigated by the UV-vis. absorption spectroscopy. The new HTL materials were also applied to green phosphorescent OLEDs, and their device characteristics were also investigated based on the chemical structures of the HTL materials. The device configuration was [ITO / PEDOT:PSS / HTL / EML / ETL / CsF / Al]. We found out that the chemical structures of the cross-linking functionalities greatly affect not only the cross-linking characteristics of the resultant HTL materials, but also the resultant OLED device characteristics. The increase of the maximum luminance and efficiency of OLEDs was evident as the cross-linking temperature decreases from higher than 200°C to at around 150°C.

Process for fabricating high reflectance-low stress Mo--Si multilayer reflective coatings

DOEpatents

Montcalm, Claude; Mirkarimi, Paul B.

2001-01-01

A high reflectance-low stress Mo--Si multilayer reflective coating particularly useful for the extreme ultraviolet (EUV) wavelength region. While the multilayer reflective coating has particular application for EUV lithography, it has numerous other applications where high reflectance and low stress multilayer coatings are utilized. Multilayer coatings having high near-normal incidence reflectance (R.gtoreq.65%) and low residual stress (.ltoreq.100 MPa) have been produced using thermal and non-thermal approaches. The thermal approach involves heating the multilayer coating to a given temperature for a given time after deposition in order to induce structural changes in the multilayer coating that will have an overall "relaxation" effect without reducing the reflectance significantly.

High reflectance-low stress Mo-Si multilayer reflective coatings

DOEpatents

Montcalm, Claude; Mirkarimi, Paul B.

2000-01-01

A high reflectance-low stress Mo-Si multilayer reflective coating particularly useful for the extreme ultraviolet (EUV) wavelength region. While the multilayer reflective coating has particular application for EUV lithography, it has numerous other applications where high reflectance and low stress multilayer coatings are utilized. Multilayer coatings having high near-normal incidence reflectance (R.gtoreq.65%) and low residual stress (.ltoreq.100 MPa) have been produced using thermal and non-thermal approaches. The thermal approach involves heating the multilayer coating to a given temperature for a given time after deposition in order to induce structural changes in the multilayer coating that will have an overall "relaxation" effect without reducing the reflectance significantly.

Design challenges for matrix assisted pulsed laser evaporation and infrared resonant laser evaporation equipment

NASA Astrophysics Data System (ADS)

Greer, James A.

2011-11-01

Since the development of the Matrix Assisted Pulsed Laser Evaporation (MAPLE) process by the Naval Research Laboratory (NRL) in the late 1990s, MAPLE has become an active area of research for the deposition of a variety of polymer, biological, and organic thin films. As is often the case with advancements in thin-film deposition techniques new technology sometimes evolves by making minor or major adjustments to existing deposition process equipment and techniques. This is usually the quickest and least expensive way to try out new ideas and to "push the envelope" in order to obtain new and unique scientific results as quickly as possible. This process of "tweaking" current equipment usually works to some degree, but once the new process is further refined overall designs for a new deposition tool based on the critical attributes of the new process typically help capitalize more fully on the all the salient features of the new and improved process. This certainly has been true for the MAPLE process. In fact the first MAPLE experiments the polymer/solvent matrix was mixed and poured into a copper holder held at LN2 temperature on a laboratory counter top. The holder was then quickly placed onto a LN2 cooled reservoir in a vacuum deposition chamber and placed in a vertical position on a LN2 cooled stage and pumped down as quickly as possible. If the sample was not placed into the chamber quickly enough the frozen matrix would melt and drip into the bottom of the chamber onto the chambers main gate valve making a bit of a mess. However, skilled and motivated scientists usually worked quickly enough to make this process work most of the time. The initial results from these experiments were encouraging and led to several publications which sparked considerable interest in this newly developed technique Clearly this approach provided the vision that MAPLE was a viable deposition process, but the equipment was not optimal for conducting MAPLE experiments on a regular basis for several reasons. The first reason is that the polymer/solvent mix as well as the sample holder are both exposed to the humidity in the air which will coat the entire surface of the holder and target with water vapor. Some polymer and/or solvent materials may not react well with water vapor. Also, the layer of water vapor absorbed on the target surface may then absorb the incident laser radiation until it is removed from the surface. Thus, it may be unclear when the water vapor is fully removed from the polymer/solvent surface and the MAPLE deposition process actually occurs. This makes deposition of specific polymer thickness difficult to calculate. While it is well known that Quartz crystal microbalances do not work well for PLD of oxide materials it can be used for the deposition of MAPLE materials. However, with rastered laser beams the tooling factor becomes a dynamic number making interpretation of final thickness potentially difficult without careful pre-calibration. Another serious issue with the initial MAPLE process was related to the use of UV lasers such as an excimer operating at 193- or 248-nm or frequency tripled, Nd:YAG lasers at 355 nm. These lasers have high energy per photon (between about 6.4 to 3.5 eV) which can lead to a variety of deleterious photochemical mechanisms that can damage the polymer chains or organic structure. Such mechanisms can be direct photo-decomposition by photochemical bond breaking and photothermal effects. Alternative lasers, such as a Er:YAG laser operating at 2.9 microns produce photons with energy of ˜0.43 eV. Such longer wavelength lasers have been used for the IR-MAPLE process and may be very useful for future MAPLE systems. A third issue with the initial approach to MAPLE was that the process did not lend itself easily to growing multilayer films. Most standard pulsed laser deposition tools have "multi-target" carousels that allow for easy target changes and multilayer film growth. This is true for sputtering, MBE, and evaporation equipment as well. This multilayer feature would certainly benefit the MAPLE process for the growth of multilayer organic materials. Another more recent advancement in thin-film laser deposition is that of Resonant Infra Red Pulsed Laser Deposition (RIRPLD) of polymer materials. This process is more akin to standard PLD but uses tunable lasers with which to select the proper wavelength to couple to vibration bands of a solid polymer, or in some cases a polymer/solvent MAPLE mixture. This technique was developed under a collaboration of researchers at the Naval Research Labs and the Free Electron Laser (FEL) at Vanderbilt University. The wide tuning range of the FEL and its relatively high power make it a very attractive source for RIRPLD. However, the price of such lasers—of order several million dollars in capital costs alone—is very high and well beyond the budgets of most research institutions. Advances in RIRPLD are currently limited due to the scarcity of tunable lasers with sufficient power in the IR range of interest to obtain reasonable deposition rates. Over the past nine years commercial equipment for MAPLE has been on the market and new lasers are being developed that may significantly improve MAPLE and RIRPLD capabilities. Examples of basic single-target MAPLE equipment, as well as multiple target MAPLE systems are described. Discussion of current lasers for MAPLE and RIRPLD are given. Finally, even though these processes have been around for a significant amount of time there are still many unknowns associated with these techniques that still should be explored before these processes can be used for production of useful products. Some of these issues which need to be addressed will be discussed.

Electrochemical Behaviour and Galvanic Effects of Titanium Implants Coupled to Metallic Suprastructures in Artificial Saliva

PubMed Central

Mellado-Valero, Ana; Igual Muñoz, Anna; Guiñón Pina, Virginia

2018-01-01

The aim of the present study is to analyze the electrochemical behavior of five different dental alloys: two cobalt-chromium alloys (CoCr and CoCr-c), one nickel-chromium-titanium alloy (NiCrTi), one gold-palladium alloy (Au), and one titanium alloy (Ti6Al4V), and the galvanic effect when they are coupled to titanium implants (TiG2). It was carried out by electrochemical techniques (open circuit measurements, potentiodynamic curves and Zero-Resistance Ammetry) in artificial saliva (AS), with and without fluorides in different acidic conditions. The studied alloys are spontaneously passivated, but NiCrTi alloy has a very narrow passive domain and losses its passivity in presence of fluorides, so is not considered as a good option for implant superstructures. Variations of pH from 6.5 to 3 in artificial saliva do not change the electrochemical behavior of Ti, Ti6Al4V, and CoCr alloys, and couples, but when the pH of the artificial saliva is below 3.5 and the fluoride content is 1000 ppm Ti and Ti6Al4V starts actively dissolving, and CoCr-c superstructures coupled to Ti show acceleration of corrosion due to galvanic effects. Thus, NiCrTi is not recommended for implant superstructures because of risk of Ni ion release to the body, and fluorides should be avoided in acidic media because Ti, Ti6Al4V, and CoCr-c superstructures show galvanic corrosion. The best combinations are Ti/Ti6Al4V and Ti/CoCr as alternative of noble gold alloys. PMID:29361767

Trend of change in retentive force for bar attachments with different materials.

PubMed

Saito, Marie; Kanazawa, Manabu; Takahashi, Hidekazu; Uo, Motohiro; Minakuchi, Shunsuke

2014-12-01

Attachment wear can decrease the retentive force of 2-implant overdentures (2-IODs). The purpose of this in vitro study was to investigate the trend of change in retentive force for 6 different bar attachments during dislodgement. Round and Dolder bars were made of platinum-added gold alloy (PGA), cobalt chromium alloy (Co-Cr), and commercially pure titanium grade IV (Ti). Clips were made of PGA. Retentive force was measured during 7200 dislodging cycles. Simple linear regression analysis was performed in order to investigate the relationship between number of cycles and retentive force (P<.05). Subsequently, wear debris was analyzed, and the surface of the attachments was observed. The retentive force of the Co-Cr round bar attachment (CoCr-R) increased from 57.5 N to 68.3 N and the Ti round bar attachment (Ti-R) from 54.8 N to 59.7 N. However, the retentive force of the PGA round bar attachment (PGA-R) decreased from 69.3 N to 64.0 N. A positive relationship was found between the number of cycles and the retentive force of both CoCr-R and Ti-R. The composition of the wear debris was almost the same as for PGA. For the Dolder bar attachment, no changes were seen in retentive force (between 7.0 N to 12.0 N). For the round bar attachment, the PGA clip and PGA bar showed wear. The retentive force of PGA-R slightly decreased. The retentive force of CoCr-R and Ti-R tended to increase. For the Dolder bar attachment, all 3 types of bar attachment showed no wear. Copyright © 2014 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

Self-organization in complex oxide thin films: from 2D to 0D nanostructures of SrRuO3 and CoCr2O4

NASA Astrophysics Data System (ADS)

Sánchez, F.; Lüders, U.; Herranz, G.; Infante, I. C.; Fontcuberta, J.; García-Cuenca, M. V.; Ferrater, C.; Varela, M.

2005-05-01

We report here on the controlled fabrication of nanostructures of varied dimensionality by self-organization processes in the heteroepitaxial growth of SrRuO3 (SRO) and CoCr2O4 (CCO) films. The surface of SRO films on SrTiO3(001) substrates can show extremely smooth terraces (2D objects) separated by atomic steps, a structure of faceted islands (0D objects), a cross-hatch morphology (1D objects), an array of finger-like units (1D objects), or an array of giant bunched steps (1D objects). The surface can be tailored to a particular structure by controlling the vicinality of the substrate and the growth rate and nominal thickness of the film. In the case of CCO films, grown on (001)-oriented MgAl2O4 or MgO substrates, high aspect ratio {111}-faceted pyramids and hut clusters (0D objects), highly oriented and having a similar size, appear above a critical thickness. The size and spatial density can be tuned by varying deposition temperature, nominal thickness, and substrate. This dependence allows the fabrication of surfaces being fully faceted (2D objects), or having arrays of dislocated pyramids of up to micrometric size, or small coherently lattice strained pyramids having a nanometric size. We discuss the driving forces that originate the peculiar SRO and CCO nanostructures. The findings illustrate that the growth of complex oxides can promote a variety of novel self-organized morphologies, and suggest original strategies to fabricate templates or hybrid structures of oxides combining varied functionalities.

Dynamic simulation of stent deployment - effects of design, material and coating

NASA Astrophysics Data System (ADS)

Schiavone, A.; Zhao, L. G.; Abdel-Wahab, A. A.

2013-07-01

Dynamic finite-element simulations have been carried out to study the effects of cell design, material choice and drug eluting coating on the mechanical behaviour of stents during deployment. Four representative stent designs have been considered, i.e., Palmaz-Schatz, Cypher, Xience and Endeavor. The former two are made of stainless steel while the latter two made of Co-Cr alloy. Geometric model for each design was created using ProEngineer software, and then imported into Abaqus for simulation of the full process of stent deployment within a diseased artery. In all cases, the delivery system was based on the dynamic expansion of a polyurethane balloon under applied internal pressure. Results showed that the expansion is mainly governed by the design, in particular open-cell design (e.g. Endeavor) tends to have greater expansion than closed-cell design (e.g. Cypher). Dogboning effect was strong for slotted tube design (e.g. Palmaz-Schatz) but reduced significantly for sinusoidal design (e.g. Cypher). Under the same pressure, the maximum von Mises stress in the stent was higher for the open-cell designs and located mostly at the inner corners of each cell. For given deformation, stents made of Co-Cr alloys tend to experience higher stress level than those made of stainless steels, mainly due to the difference in material properties. For artery-plaque system, the maximum stress occurred on the stenosis and dogboning led to stress concentration at the ends of the plaque. The drug eluting coating affected the stent expansion by reducing the recoiling phenomenon considerably, but also raised the stress level on the stent due to property mismatch.

Electrochemical Behaviour and Galvanic Effects of Titanium Implants Coupled to Metallic Suprastructures in Artificial Saliva.

PubMed

Mellado-Valero, Ana; Muñoz, Anna Igual; Pina, Virginia Guiñón; Sola-Ruiz, Ma Fernanda

2018-01-22

The aim of the present study is to analyze the electrochemical behavior of five different dental alloys: two cobalt-chromium alloys (CoCr and CoCr-c), one nickel-chromium-titanium alloy (NiCrTi), one gold-palladium alloy (Au), and one titanium alloy (Ti6Al4V), and the galvanic effect when they are coupled to titanium implants (TiG2). It was carried out by electrochemical techniques (open circuit measurements, potentiodynamic curves and Zero-Resistance Ammetry) in artificial saliva (AS), with and without fluorides in different acidic conditions. The studied alloys are spontaneously passivated, but NiCrTi alloy has a very narrow passive domain and losses its passivity in presence of fluorides, so is not considered as a good option for implant superstructures. Variations of pH from 6.5 to 3 in artificial saliva do not change the electrochemical behavior of Ti, Ti6Al4V, and CoCr alloys, and couples, but when the pH of the artificial saliva is below 3.5 and the fluoride content is 1000 ppm Ti and Ti6Al4V starts actively dissolving, and CoCr-c superstructures coupled to Ti show acceleration of corrosion due to galvanic effects. Thus, NiCrTi is not recommended for implant superstructures because of risk of Ni ion release to the body, and fluorides should be avoided in acidic media because Ti, Ti6Al4V, and CoCr-c superstructures show galvanic corrosion. The best combinations are Ti/Ti6Al4V and Ti/CoCr as alternative of noble gold alloys.

The Survival of Total Knee Arthroplasty: Current Data from Registries on Tribology: Review Article.

PubMed

Civinini, Roberto; Carulli, Christian; Matassi, Fabrizio; Lepri, Andrea Cozzi; Sirleo, Luigi; Innocenti, Massimo

2017-02-01

Polyethylene (PE) wear is a major contributor to implant loosening following total knee arthroplasty (TKA), and advanced bearings in TKA are being investigated with hopes of reducing or eliminate wear-related loosening. Currently, information on knee tribology is available from national joint registries and may be the best tools to evaluate the efficacy and safety of design innovations in joint arthroplasty. We performed a review of national joint registries trying to answer the following questions: "Which is the main factor directly related to revisions rate in TKA?" and "Are there new bearing options better than conventional ones?" A review was performed of all published annual reports of National Joint Registers, as well as of the literature. The search was carried out using and comparing the National Joint Registers. Current data from registries for total knee arthroplasty indicates that age is the major factor affecting the outcome of primary total knee replacement. The 10-year cumulative revision rate for non-cross-linked PE was 5.8% and for XLPE it was 3.5%. The effect of cross-linked polyethylene was more evident in the younger patients. The survival of the oxidized zirconium (OxZr) femoral component appears better when compared to a similar age group of patients with conventional group of prostheses. Our review suggests that the revision rates are half for the OxZr components compared to conventional CoCr femoral components. Age is the most relevant single factor related to revision rate. Cross-linked PE has a statistical lower revision rate at 10 years compared to conventional PE and, in the OxZr group, the revision rate is 2 times lower than Co-Cr in the same group of age.

Necrotic and inflammatory changes in metal-on-metal resurfacing hip arthroplasties

PubMed Central

2009-01-01

Background Necrosis and inflammation in peri-implant soft tissues have been described in failed second-generation metal-on-metal (MoM) resurfacing hip arthroplasties and in the pseudotumors associated with these implants. The precise frequency and significance of these tissue changes is unknown. Method We analyzed morphological and immunophenotypic changes in the periprosthetic soft tissues and femoral heads of 52 revised MoM arthroplasties (fracture in 21, pseudotumor in 13, component loosening in 9, and other causes in 9 cases). Results Substantial necrosis was observed in the periprosthetic connective tissue in 28 of the cases, including all pseudotumors, and 5 cases of component loosening. A heavy, diffuse inflammatory cell infiltrate composed mainly of HLA-DR+/CD14+/CD68+ macrophages and CD3+ T cells was seen in 45 of the cases. Perivascular lymphoid aggregates composed of CD3+ cells and CD20+ B cells were noted in 27 of the cases, but they were not seen in all cases of component loosening or pseudotumors. Plasma cells were noted in 30 cases. Macrophage granulomas were noted in 6 cases of component loosening. In the bone marrow of the femoral head, a macrophage and T cell response was seen in 31 of the cases; lymphoid aggregates were noted in 19 of the cases and discrete granulomas in 1 case. Interpretation Our findings indicate that there is a spectrum of necrotic and inflammatory changes in response to the deposition of cobalt-chrome (Co-Cr) wear particles in periprosthetic tissues. Areas of extensive coagulative necrosis and a macrophage and T lymphocyte response occur in implant failure and pseudotumors, in which there is also granuloma formation. The pathogenesis of these changes is uncertain but it may involve both a cytotoxic response and a delayed hypersensitivity (type IV) response to Co-Cr particles. PMID:19995315

Evaluation of tensile strength and surface topography of orthodontic wires after infection control procedures: An in vitro study

PubMed Central

Brindha, M.; Kumaran, N. Kurunji; Rajasigamani, K.

2014-01-01

Aim: The aim of this study is to evaluate, the influence of four types of sterilization/disinfection procedures (autoclave, hot air oven, glutaraldehyde, and ultraviolet [UV] light) on the tensile strength and surface topography of three orthodontic wires (stainless steel (SS), titanium - molybdenum alloy [TMA], and cobalt chromium (CoCr)). Materials and Methods: Sample comprised of three types of 8 inches straight length segments of orthodontic wires. They were divided into three groups according to wire composition comprising of 50 samples each. Totally 50 samples of each group were then equally divided into five subgroups according to sterilization method. After sterilization and disinfection of the experimental group, surface topography was examined with scanning electron microscope (SEM) and tensile strength was tested using universal testing machine. Result: The results of this study show that the mean ultimate tensile strength (UTS) of SS wire after four sterilization procedures were similar to the control group (1845.815 ± 142.29 MPa). The mean UTS of TMA wire increases after four sterilization procedures when compared with the control group (874.107 ± 275.939 MPa). The mean UTS of CoCr wire remains same after UV light disinfection, but increases after other three sterilization procedures when compared with the control group (1449.759 ± 156.586 MPa). SEM photographs of the present study shows gross increase in pitting roughness of the surface topography of all the three types of wires after four types of sterilization. Conclusion: Orthodontists who want to offer maximum safety for their patients can sterilize orthodontic wires before placement, as it does not deteriorate the tensile strength and surface roughness of the alloys. PMID:25210383

Evaluation of tensile strength and surface topography of orthodontic wires after infection control procedures: An in vitro study.

PubMed

Brindha, M; Kumaran, N Kurunji; Rajasigamani, K

2014-07-01

The aim of this study is to evaluate, the influence of four types of sterilization/disinfection procedures (autoclave, hot air oven, glutaraldehyde, and ultraviolet [UV] light) on the tensile strength and surface topography of three orthodontic wires (stainless steel (SS), titanium - molybdenum alloy [TMA], and cobalt chromium (CoCr)). Sample comprised of three types of 8 inches straight length segments of orthodontic wires. They were divided into three groups according to wire composition comprising of 50 samples each. Totally 50 samples of each group were then equally divided into five subgroups according to sterilization method. After sterilization and disinfection of the experimental group, surface topography was examined with scanning electron microscope (SEM) and tensile strength was tested using universal testing machine. The results of this study show that the mean ultimate tensile strength (UTS) of SS wire after four sterilization procedures were similar to the control group (1845.815 ± 142.29 MPa). The mean UTS of TMA wire increases after four sterilization procedures when compared with the control group (874.107 ± 275.939 MPa). The mean UTS of CoCr wire remains same after UV light disinfection, but increases after other three sterilization procedures when compared with the control group (1449.759 ± 156.586 MPa). SEM photographs of the present study shows gross increase in pitting roughness of the surface topography of all the three types of wires after four types of sterilization. Orthodontists who want to offer maximum safety for their patients can sterilize orthodontic wires before placement, as it does not deteriorate the tensile strength and surface roughness of the alloys.

Characterization of wear debris from metal-on-metal hip implants during normal wear versus edge-loading conditions.

PubMed

Kovochich, Michael; Fung, Ernest S; Donovan, Ellen; Unice, Kenneth M; Paustenbach, Dennis J; Finley, Brent L

2018-04-01

Advantages of second-generation metal-on-metal (MoM) hip implants include low volumetric wear rates and the release of nanosized wear particles that are chemically inert and readily cleared from local tissue. In some patients, edge loading conditions occur, which result in higher volumetric wear. The objective of this study was to characterize the size, morphology, and chemistry of wear particles released from MoM hip implants during normal (40° angle) and edge-loading (65° angle with microseparation) conditions. The mean primary particle size by volume under normal wear was 35 nm (range: 9-152 nm) compared with 95 nm (range: 6-573 nm) under edge-loading conditions. Hydrodynamic diameter analysis by volume showed that particles from normal wear were in the nano- (<100 nm) to submicron (<1000 nm) size range, whereas edge-loading conditions generated particles that ranged from <100 nm up to 3000-6000 nm in size. Particles isolated from normal wear were primarily chromium (98.5%) and round to oval in shape. Edge-loading conditions generated more elongated particles (4.5%) (aspect ratio ≥ 2.5) and more CoCr alloy particles (9.3%) compared with normal wear conditions (1.3% CoCr particles). By total mass, edge-loading particles contained approximately 640-fold more cobalt than normal wear particles. Our findings suggest that high wear conditions are a potential risk factor for adverse local tissue effects in MoM patients who experience edge loading. This study is the first to characterize both the physical and chemical characteristics of MoM wear particles collected under normal and edge-loading conditions. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 986-996, 2018. © 2017 Wiley Periodicals, Inc.

Fast plasma sintering delivers functional graded materials components with macroporous structures and osseointegration properties.

PubMed

Godoy, R F; Coathup, M J; Blunn, G W; Alves, A L; Robotti, P; Goodship, A E

2016-04-13

We explored the osseointegration potential of two macroporous titanium surfaces obtained using fast plasma sintering (FPS): Ti macroporous structures with 400-600 µmØ pores (TiMac400) and 850-1000 µmØ pores (TiMac850). They were compared against two surfaces currently in clinical use: Ti-Growth® and air plasma spray (Ti-Y367). Each surface was tested, once placed over a Ti-alloy and once onto a CoCr bulk substrate. Implants were placed in medial femoral condyles in 24 sheep. Samples were explanted at four and eight weeks after surgery. Push-out loads were measured using a material-testing system. Bone contact and ingrowth were assessed by histomorphometry and SEM and EDX analyses. Histology showed early osseointegration for all the surfaces tested. At 8 weeks, TiMac400, TiMac850 and Ti-Growth® showed deep bone ingrowth and extended colonisation with newly formed bone. The mechanical push-out force was equal in all tested surfaces. Plasma spray surfaces showed greater bone-implant contact and higher level of pores colonisation with new bone than FPS produced surfaces. However, the void pore area in FPS specimens was significantly higher, yet the FPS porous surfaces allowed a deeper osseointegration of bone to implant. FPS manufactured specimens showed similar osseointegration potential to the plasma spray surfaces for orthopaedic implants. FPS is a useful technology for manufacturing macroporous titanium surfaces. Furthermore, its capability to combine two implantable materials, using bulk CoCr with macroporous titanium surfaces, could be of interest as it enables designers to conceive and manufacture innovative components. FPS delivers functional graded materials components with macroporous structures optimised for osseointegration.

Optimal conjugation of catechol group onto hyaluronic acid in coronary stent substrate coating for the prevention of restenosis.

PubMed

Lih, Eugene; Choi, Seul Gi; Ahn, Dong June; Joung, Yoon Ki; Han, Dong Keun

2016-01-01

Although endovascular stenting has been used as an interventional therapy to treat cardio- and cerebro-vascular diseases, it is associated with recurrent vascular diseases following stent thrombosis and in-stent restenosis. In this study, a metallic stent was coated with dopamine-conjugated hyaluronic acid with different ratios of catechol group to improve hemocompatibility and re-endothelialization. Especially, we were interested in how much amount of catechol group is appropriate for the above-mentioned purposes. Therefore, a series of dopamine-conjugated hyaluronic acid conjugates with different ratios of catechol group were synthesized via a carbodiimide coupling reaction. Dopamine-conjugated hyaluronic acid conjugates were characterized with 1 H-nuclear magnetic resonance and Fourier transform infrared spectroscopy, and the amount of catechol group in dopamine-conjugated hyaluronic acid was measured by ultraviolet spectrometer. Co-Cr substrates were polished and coated with various dopamine-conjugated hyaluronic acid conjugates under pH 8.5. Dopamine-conjugated hyaluronic acid amounts on the substrate were quantified by micro-bicinchoninic acid assay. Surface characteristics of dopamine-conjugated hyaluronic-acid-coated Co-Cr were evaluated by water contact angle, scanning electron microscopy, and atomic force microscopy. The hemocompatibility of the surface-modified substrates was assessed by protein adsorption and platelet adhesion tests. Adhesion and activation of platelets were confirmed with scanning electron microscopy and lactate dehydrogenase assay. Human umbilical vein endothelial cells were cultured on the substrates, and the viability, adhesion, and proliferation were investigated through cell counting kit-8 assay and fluorescent images. Obtained results demonstrated that optimal amounts of catechol group (100 µmol) in the dopamine-conjugated hyaluronic acid existed in terms of various properties such as hemocompatibility and cellular responses.

Grindability of cast Ti-6Al-4V alloyed with copper.

PubMed

Watanabe, Ikuya; Aoki, Takayuki; Okabe, Toru

2009-02-01

This study investigated the grindability of cast Ti-6Al-4V alloyed with copper. The metals tested were commercially pure titanium (CP Ti), Ti-6Al-4V, experimental Ti-6Al-4V-Cu (1, 4, and 10 wt% Cu), and Co-Cr alloy. Each metal was cast into five blocks (3.0 x 8.0 x 30.0 mm(3)). The 3.0-mm wide surface of each block was ground using a hand-piece engine with an SiC wheel at four circumferential speeds (500, 750, 1000, and 1250 m/min) at a grinding force of 100 g. The grindability index (G-index) was determined as volume loss (mm(3)) calculated from the weight loss after 1 minute of grinding and the density of each metal. The ratio of the metal volume loss and the wheel volume loss was also calculated (G-ratio, %). Data (n = 5) were statistically analyzed using ANOVA (alpha= 0.05). Ti-6Al-4V and the experimental Ti-6Al-4V-Cu alloys exhibited significantly (p < 0.05) higher G-indexes compared with CP Ti and Co-Cr at any rotational speed except for the lowest speed (500 m/min). At 500 m/min, the G-index of Ti-6Al-4V-Cu increased as the amount of alloyed copper increased. The 4% Cu and 10% Cu alloys had significantly greater G-indexes than did 1% Cu and Ti-6Al-4V at the highest rotational speed (1250 m/min). Increasing the percentage of alloyed copper and the circumferential speed also increased the G-ratio. A slight reduction in ductility due to alloying Ti-6Al-4V with copper improved the grindability of some of the resultant Ti-6Al-4V-Cu alloys.

Development of extreme ultraviolet and soft x-ray multilayer optics for scientific studies with femtosecond/attosecond sources

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aquila, Andrew Lee

The development of multilayer optics for extreme ultraviolet (EUV) radiation has led to advancements in many areas of science and technology, including materials studies, EUV lithography, water window microscopy, plasma imaging, and orbiting solar physics imaging. Recent developments in femtosecond and attosecond EUV pulse generation from sources such as high harmonic generation lasers, combined with the elemental and chemical specificity provided by EUV radiation, are opening new opportunities to study fundamental dynamic processes in materials. Critical to these efforts is the design and fabrication of multilayer optics to transport, focus, shape and image these ultra-fast pulses This thesis describes themore » design, fabrication, characterization, and application of multilayer optics for EUV femtosecond and attosecond scientific studies. Multilayer mirrors for bandwidth control, pulse shaping and compression, tri-material multilayers, and multilayers for polarization control are described. Characterization of multilayer optics, including measurement of material optical constants, reflectivity of multilayer mirrors, and metrology of reflected phases of the multilayer, which is critical to maintaining pulse size and shape, were performed. Two applications of these multilayer mirrors are detailed in the thesis. In the first application, broad bandwidth multilayers were used to characterize and measure sub-100 attosecond pulses from a high harmonic generation source and was performed in collaboration with the Max-Planck institute for Quantum Optics and Ludwig- Maximilians University in Garching, Germany, with Professors Krausz and Kleineberg. In the second application, multilayer mirrors with polarization control are useful to study femtosecond spin dynamics in an ongoing collaboration with the T-REX group of Professor Parmigiani at Elettra in Trieste, Italy. As new ultrafast x-ray sources become available, for example free electron lasers, the multilayer designs described in this thesis can be extended to higher photon energies, and such designs can be used with those sources to enable new scientific studies, such as molecular bonding, phonon, and spin dynamics.« less

In-situ stress measurement of single and multilayer thin-films used in x-ray astronomy optics applications

NASA Astrophysics Data System (ADS)

Broadway, David M.; Ramsey, Brian D.; O'Dell, Stephen L.; Gurgew, Danielle

2017-09-01

We present in-situ stress measurement results for single and multilayer thin-films deposited by magnetron sputtering. In particular, we report on the influence of the material interfaces on the ensuing stress in both the transient and steady-state regimes of film growth. This behavior is used to determine the appropriate thicknesses of the constituent layers that will result in a net tensile stress in multilayers composed of various material combinations. These multilayers can then be used to compensate the compressive integrated stress in single and multilayer EUV and x-ray optical coatings. The use of multilayers to compensate the integrated stress might be advantageous because, unlike single layers of chromium, the roughness is not expected to increase with the total thickness of the multilayer. In this paper, we demonstrate the technique for W/Si and Mo/Si multilayers and discuss its application to other material combinations.

Synthesis of lithium nitride for neutron production target of BNCT by in situ lithium deposition and ion implantation

NASA Astrophysics Data System (ADS)

Ishiyama, S.; Baba, Y.; Fujii, R.; Nakamura, M.; Imahori, Y.

2012-12-01

To achieve high performance of BNCT (Boron Neutron Capture Therapy) device, Li3N/Li/Pd/Cu four layered Li target was designed and the structures of the synthesized four layered target were characterized by X-ray photoelectron spectroscopy. For the purpose of avoiding the radiation blistering and lithium evaporation, in situ vacuum deposition and nitridation techniques were established for in situ production and repairing maintenance of the lithium target. Following conclusions were derived: Uniform lithium layer of a few hundreds nanometer was formed on Pd/Cu multilayer surface by in situ vacuum deposition technique using metallic lithium as a source material. Lithium nitrides were formed by in situ nitridation reaction by the implantation of low-energy nitrogen ions on the deposited lithium layer surface. The chemical states of the nitridated zone were close to the stoichiometric lithium nitride, Li3N. This nitridated zone formed on surface of four layered lithium target is stable for a long time in air condition. The in situ nitridation is effective to protect lithium target from degradation by unfavorable reactions.

Soft x ray optics by pulsed laser deposition

NASA Technical Reports Server (NTRS)

Fernandez, Felix E.

1994-01-01

A series of molybdenum thin film depositions by PLD (Pulsed Laser Deposition) have been carried out, seeking appropriate conditions for multilayer fabrication. Green (532 nm) and UV (355 nm) light pulses, in a wide range of fluences, were used. Relatively large fluences (in comparison with Si) are required to cause evaporation of molybdenum. The optical penetration depths and reflectivities for Mo at these two wavelengths are comparable, which means that results should be, and do appear to be similar for equal fluences. For all fluences above threshold used, a large number of incandescent particles is ejected by the target (either a standard Mo sputtering target or a Mo sheet were tried), together with the plasma plume. Most of these particles are clearly seen to bounce off the substrate. The films were observed with light microscopy using Nomarski and darkfield techniques. There is no evidence of large debris. Smooth films plus micron-sized droplets are usually seen. The concentration of these droplets embedded in the film appears not to vary strongly with the laser fluence employed. Additional characterization with SEM and XRD is under way.

Improved optoelectronics properties of ITO-based transparent conductive electrodes with the insertion of Ag/Ni under-layer

NASA Astrophysics Data System (ADS)

Ali, Ahmad Hadi; Abu Bakar, Ahmad Shuhaimi; Hassan, Zainuriah

2014-10-01

ITO-based transparent conductive electrodes (TCE) with Ag/Ni thin metal under-layer were deposited on Si and glass substrates by thermal evaporator and RF magnetron sputtering system. Ceramic ITO with purity of 99.99% and In2O3:SnO2 weight ratio of 90:10 was used as a target at room temperature. Post-deposition annealing was performed on the TCE at moderate temperature of 500 °C, 600 °C and 700 °C under N2 ambient. It was observed that the structural properties, optical transmittance, electrical characteristics and surface morphology were improved significantly after the post-annealing process. Post-annealed ITO/Ag/Ni at 600 °C shows the best quality of TCE with figure-of-merit (FOM) of 1.5 × 10-2 Ω-1 and high optical transmittance of 83% at 470 nm as well as very low electrical resistivity of 4.3 × 10-5 Ω-cm. The crystalline quality and surface morphological plays an important role in determining the quality of the TCE multilayer thin films properties.

Topical meeting on optical interference coatings (OIC'2001): manufacturing problem.

PubMed

Dobrowolski, J A; Browning, Stephen; Jacobson, Michael; Nadal, Maria

2002-06-01

Measurements are presented of the experimental filters submitted to the first optical thin-film manufacturing problem posed in conjunction with the Topical Meeting on Optical Interference Coatings, in which the object was to produce multilayers with spectral transmittance and reflectance curves that were as close as possible to the target values that were specified in the 400- to 600-nm spectral region. No limit was set on the overall thickness of the solutions or the number of layers used in their construction. The participants were free to use the coating materials of their choice. Six different groups submitted a total of 11 different filters for evaluation. Three different physical vapor deposition processes were used for the manufacture of the coatings: magnetron sputtering, ion-beam sputtering, and plasma-ion-assisted, electron-beam gun evaporation. The solutions ranged in metric thickness from 758 to 4226 nm and consisted of between 8 and 27 layers. For all but two of the samples submitted, the average rms departure of the measured transmittances and reflectances from the target values in the spectral region of interest was between 0.98% and 1.55%.

Diffusion-controlled growth of molecular heterostructures: fabrication of two-, one-, and zero-dimensional C(60) nanostructures on pentacene substrates.

PubMed

Breuer, Tobias; Witte, Gregor

2013-10-09

A variety of low dimensional C60 structures has been grown on supporting pentacene multilayers. By choice of substrate temperature during growth the effective diffusion length of evaporated fullerenes and their nucleation at terraces or step edges can be precisely controlled. AFM and SEM measurements show that this enables the fabrication of either 2D adlayers or solely 1D chains decorating substrate steps, while at elevated growth temperature continuous wetting of step edges is prohibited and instead the formation of separated C60 clusters pinned at the pentacene step edges occurs. Remarkably, all structures remain thermally stable at room temperature once they are formed. In addition the various fullerene structures have been overgrown by an additional pentacene capping layer. Utilizing the different probe depth of XRD and NEXAFS, we found that no contiguous pentacene film is formed on the 2D C60 structure, whereas an encapsulation of the 1D and 0D structures with uniformly upright oriented pentacene is achieved, hence allowing the fabrication of low dimensional buried organic heterostructures.

DOE Office of Scientific and Technical Information (OSTI.GOV)

McNally, J.J.

The effects on the properties of Ta/sub 2/O/sub 5/, Al/sub 2/O/sub 3/, SiO/sub 2/ and HfO/sub 2/ single- and multi-layer optical coatings deposited using ion-assisted deposition (IAD) were investigated. IAD is a novel deposition technique which utilizes a separate ion source to direct a beam of ions at the growing film. A Kaufman ion source was used to provide a monoenergetic, neutralized beam of oxygen ions independent of the material evaporation process. The optical and physical properties, as well as laser induced damage threshold (LIDT) values, were studied for coatings bombarded with 200, 300, 500 and 1000 eV oxygen ionsmore » at values of current density from 0 to 200 microAmp/sq cm. IAD was successfully applied to deposit coatings at low temperature on heavy metal fluoride (HMF) glass substrates. The coatings deposited using IAD were hard and dense. The IAD coatings improved the durability and abrasion resistance of the HMF glass substrates. The results of this investigation show that IAD can be used to improve the optical and physical properties of optical coatings.« less

Topological interface modes in graphene multilayer arrays

NASA Astrophysics Data System (ADS)

Wang, Feng; Ke, Shaolin; Qin, Chengzhi; Wang, Bing; Long, Hua; Wang, Kai; Lu, Peixiang

2018-07-01

We investigate the topological interface modes of surface plasmon polaritons in a multilayer system composed of graphene waveguide arrays. The topological interface modes emerge when two topologically distinct graphene multilayer arrays are connected. In such multilayer system, the non-trivial topological interface modes and trivial modes coexist. By tuning the configuration of the graphene multilayer arrays, the associated non-trivial interface modes present robust against structural disorder. The total number of topological modes is related to that of graphene layers in a unit cell of the graphene multilayer array. The results provide a new paradigm for topologically protected plasmonics in the graphene multilayer arrays. The study suggests a promising approach to realize light transport and optical switching on a deep-subwavelength scale.

The multilayer nanoparticles formed by layer by layer approach for cancer-targeting therapy.

PubMed

Oh, Keun Sang; Lee, Hwanbum; Kim, Jae Yeon; Koo, Eun Jin; Lee, Eun Hee; Park, Jae Hyung; Kim, Sang Yoon; Kim, Kwangmeyung; Kwon, Ick Chan; Yuk, Soon Hong

2013-01-10

The multilayer nanoparticles (NPs) were prepared for cancer-targeting therapy using the layer by layer approach. When drug-loaded Pluronic NPs were mixed with vesicles (liposomes) in the aqueous medium, Pluronic NPs were incorporated into the vesicles to form the vesicle NPs. Then, the multilayer NPs were formed by freeze-drying the vesicle NPs in a Pluronic aqueous solution. The morphology and size distribution of the multilayer NPs were observed using a TEM and a particle size analyzer. In order to apply the multilayer NPs as a delivery system for docetaxel (DTX), which is a model anticancer drug, the release pattern of the DTX was observed and the tumor growth was monitored by injecting the multilayer NPs into the tail veins of tumor (squamous cell carcinoma)-bearing mice. The cytotoxicity of free DTX (commercial DTX formulation (Taxotere®)) and the multilayer NPs was evaluated using MTT assay. We also evaluated the tumor targeting ability of the multilayer NPs using magnetic resonance imaging. The multilayer NPs showed excellent tumor targetability and antitumor efficacy in tumor-bearing mice, caused by the enhanced permeation and retention (EPR) effect. These results suggest that the multilayer NPs could be a potential drug delivery system for cancer-targeting therapy. Copyright © 2012 Elsevier B.V. All rights reserved.

75 FR 66126 - Multilayered Wood Flooring From China

Federal Register 2010, 2011, 2012, 2013, 2014

2010-10-27

...)] Multilayered Wood Flooring From China AGENCY: United States International Trade Commission. ACTION: Institution... the United States is materially retarded, by reason of imports from China of multilayered wood... multilayered wood flooring. The following companies are members of the CAHP: Anderson Hardwood Floors, LLC...

Advances in polyelectrolyte multilayer nanofilms as tunable drug delivery systems

PubMed Central

Jiang, Bingbing; Barnett, John B; Li, Bingyun

2009-01-01

There has been considerable interest in polyelectrolyte multilayer nanofilms, which have a variety of applications ranging from optical and electrochemical materials to biomedical devices. Polyelectrolyte multilayer nanofilms are constructed from aqueous solutions using electrostatic layer-by-layer self-assembly of oppositely-charged polyelectrolytes on a solid substrate. Multifunctional polyelectrolyte multilayer nanofilms have been studied using charged dyes, metal and inorganic nanoparticles, DNA, proteins, and viruses. In the past few years, there has been increasing attention to developing polyelectrolyte multilayer nanofilms as drug delivery vehicles. In this mini-review, we present recent developments in polyelectrolyte multilayer nanofilms with tunable drug delivery properties, with particular emphasis on the strategies in tuning the loading and release of drugs in polyelectrolyte multilayer nanofilms as well as their applications. PMID:24198464

Magneto-structural correlation in Co0.8Cu0.2Cr2O4 cubic spinel

NASA Astrophysics Data System (ADS)

Kumar, Ram; Rayaprol, S.; Siruguri, V.; Xiao, Y.; Ji, W.; Pal, D.

2018-05-01

Neutron and X-ray diffraction, magnetic susceptibility, and specific heat measurements have been used to investigate the magneto-structural phase transitions in 20% Cu substituted multiferroic CoCr2O4 spinel. The Jahn-Teller active Cu2+ ion in the tetrahedral A-site of the spinel configuration induces the Jahn-Teller distortion slightly above the Néel temperature. In this compound, we observe a Jahn-Teller distortion of the crystal structure at 90 K. It was further observed that the high temperature cubic (Fd 3 ‾ m) structure coexists with the low temperature orthorhombic (Fddd) structure till the lowest temperature of measurement.

Preparation and properties of the multi-layer aerogel thermal insulation composites

NASA Astrophysics Data System (ADS)

Wang, Miao; Feng, Junzong; Jiang, Yonggang; Zhang, Zhongming; Feng, Jian

2018-03-01

Multi-layer insulation materials possess low radiation thermal conductivity, and excellent thermal insulation property in a vacuum environment. However, the spacers of the traditional multi-layer insulation materials are mostly loose fibers, which lead to more sensitive to the vacuum environmental of serviced. With the vacuum degree declining, gas phases thermal convection increase obviously, and the reflective screen will be severe oxidation, all of these make the thermal insulation property of traditional multi-layer insulation deteriorate, thus limits its application scope. In this paper, traditional multi-layer insulation material is combined with aerogel and obtain a new multi-layer aerogel thermal insulation composite, and the effects of the number, thickness and type of the reflective screens on the thermal insulation properties of the multi-layer composites are also studied. The result is that the thermal insulation property of the new type multi-layer aerogel composites is better than the pure aerogel composites and the traditional multi-layer insulation composites. When the 0.01 mm stainless steel foil as the reflective screen, and the aluminum silicate fiber and silica aerogel as the spacer layer, the layer density of composite with the best thermal insulation property is one layer per millimeter at 1000 °C.

Controlled synthesis of MnOOH multilayer nanowires as anode materials for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wu, Yue; Yue, Kaiqiang; Wang, Yuanxin

MnOOH multilayer nanowires have been successfully synthesized by a hydrothermal method. It is found that the uniform multilayer structure of nanowires ran through the entire nanowire, which is formed via a layer by layer. The electrochemical properties of MnOOH multilayer nanowires as an anode material for Li-ion batteries (LIB) were investigated, and excellent capacity retention, superior cycling performance, and high rate capability were achieved. Specifically, the reversible capacity of MnOOH multilayer nanowires is 521 mAh/g after 500 cycles at 0.1 C, with excellent electrochemical stability. The multilayer nanowire electrodes exhibit short electron path lengths, high internal dislocation densities and largemore » surface to volume ratio, resulting in increased specific capacity, cycling stability and rate performance in the energy storage devices, which serves as an indication of their potential application in LIBs. - Highlights: •MnOOH multilayer nanowires were synthesized by a hydrothermal method. •The uniform multilayer structure of nanowires was formed via layer by layer. •The reversible capacity of product shows 521 mAh/g after 500 cycles at 0.1 C. •MnOOH multilayer nanowires showed higher property as anode material in LIB.« less

76 FR 92 - Multilayered Wood Flooring From the People's Republic of China: Postponement of Preliminary...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-01-03

... DEPARTMENT OF COMMERCE International Trade Administration [C-570-971] Multilayered Wood Flooring... Department'') initiated an investigation of multilayered wood flooring from the People's Republic of China (``PRC''). See Multilayered Wood Flooring From the People's Republic of China: Initiation of...

76 FR 76693 - Multilayered Wood Flooring From the People's Republic of China: Countervailing Duty Order

Federal Register 2010, 2011, 2012, 2013, 2014

2011-12-08

... DEPARTMENT OF COMMERCE International Trade Administration [C-570-971] Multilayered Wood Flooring...''), the Department is issuing a countervailing duty (``CVD'') order on multilayered wood flooring from the... that countervailable subsidies are being provided to producers and exporters of multilayered wood...

76 FR 76435 - Multilayered Wood Flooring From China

Federal Register 2010, 2011, 2012, 2013, 2014

2011-12-07

...)] Multilayered Wood Flooring From China Determinations On the basis of the record \\1\\ developed in the subject... multilayered wood flooring, provided for in subheadings 4409.10, 4409.29, 4412.31, 4412.32, 4412.39, 4412.94... American Hardwood Parity (``CAHP''), an ad hoc association of U.S. manufacturers of multilayered wood...

75 FR 79019 - Multilayered Wood Flooring From China

Federal Register 2010, 2011, 2012, 2013, 2014

2010-12-17

...)] Multilayered Wood Flooring From China Determinations On the basis of the record \\1\\ developed in the subject... imports from China of multilayered wood flooring, provided for in subheadings 4409.10, 4409.29, 4412.31... multilayered wood flooring. The following companies are members of the CAHP: Anderson Hardwood Floors, LLC...

75 FR 70714 - Multilayered Wood Flooring From the People's Republic of China: Initiation of Antidumping Duty...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-11-18

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... Commerce (``Department'') received a petition concerning imports of multilayered wood flooring from the...: Multilayered Wood Flooring from the People's Republic of China dated October 21, 2010 (``Petition''). On...

76 FR 76690 - Multilayered Wood Flooring From the People's Republic of China: Amended Final Determination of...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-12-08

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... is issuing an antidumping duty order on multilayered wood flooring (``wood flooring'') from the... antidumping duty investigation of wood flooring from the PRC. See Multilayered Wood Flooring From the People's...

78 FR 32367 - Multilayered Wood Flooring From the People's Republic of China; Preliminary Results of...

Federal Register 2010, 2011, 2012, 2013, 2014

2013-05-30

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... duty order on multilayered wood flooring (``MLWF'') from the People's Republic of China (``PRC''). The... Memorandum for Preliminary Results of Antidumping Duty New Shipper Review: Multilayered Wood Flooring from...

78 FR 52502 - Multilayered Wood Flooring From the People's Republic of China: Final Results of Antidumping Duty...

Federal Register 2010, 2011, 2012, 2013, 2014

2013-08-23

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... an antidumping duty new shipper review of multilayered wood flooring (``MLWF'') from the People's... of subject merchandise at less than normal value. \\1\\ See Multilayered Wood Flooring From the People...

77 FR 5484 - Multilayered Wood Flooring From the People's Republic of China: Amended Antidumping and...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-02-03

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970, C-570-971] Multilayered Wood... (``CVD'') orders on multilayered wood flooring from the People's Republic of China (``PRC'') to remove an... the International Trade Commission, the Department published AD and CVD orders on multilayered wood...

76 FR 13357 - Multilayered Wood Flooring from the People's Republic of China: Postponement of Preliminary...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-03-11

... DEPARTMENT OF COMMERCE. International Trade Administration [A-570-970] Multilayered Wood Flooring... multilayered wood flooring from the People's Republic of China.\\1\\ The notice of initiation stated that, unless... Multilayered Wood Flooring from the People's Republic of China: Initiation of Antidumping Duty Investigation...

Advances in far-ultraviolet reflective and transmissive coatings for space applications

NASA Astrophysics Data System (ADS)

Rodríguez-de Marcos, Luis; Aznárez, José A.; Méndez, José A.; Larruquert, Juan I.; Vidal-Dasilva, M.; Malvezzi, A. Marco; Giglia, Angelo; Capobianco, Gerardo; Massone, Giuseppe; Fineschi, Silvano; Nannarone, Stefano

2016-07-01

Exploitation of far ultraviolet (FUV, 100-200 nm) observations extends to most areas of modern astronomy, from detailed observations of Solar System objects, the interstellar medium, exoplanets, stars and galaxies, to studies of crucial cosmological relevance. Despite several developments in recent decades, yet many observations are not possible due to technical limitations, of which one of the most important is the lack of optical coatings with high throughput. Development and optimization of such efficient FUV coatings have been identified in several roadmap reports as a key goal for future missions. The success of this development will ultimately improve the performance of nowadays feasible optical instruments and will enable new scientific imaging capabilities. GOLD's research is devoted to developing novel coatings with enhanced performance for space optics. Several deposition systems are available for the deposition of multilayer coatings. A deposition system was developed to deposit FUV coatings to satisfy space requirements. It consists of a 75-cm-diameter deposition chamber pumped with a cryo-pump and placed in an ISO-6 clean room. This chamber is available for deposition by evaporation of top-requirement coatings such as Al/ MgF2 mirrors or (Al/MgF2)n multilayer coatings for transmittance filters. A plan to add an Ion-Beam-Sputtering system in this chamber is under way. In this and other chambers at GOLD the following FUV coatings can be prepared: Transmittance filters based on (Al/MgF2)n multilayer coatings. These filters can be designed to have a peak at the FUV spectral line or band of interest and a high peak-to-visible transmittance ratio. Filters can be designed with a peak transmittance at a wavelength as short as 120 nm and with a transmittance in the visible smaller than 10-5. Narrowband reflective coatings peaked close to H Lyman β (102.6 nm) with a reflectance at H Lyman α (121.6 nm) two orders of magnitude below the one at 102.6 nm. Other potential spectral lines at which these coatings could be peaked are the OVI doublet (103.2, 103.8 nm). Narrowband reflective mirrors based on (MgF2/LaF3)n multilayers peaked at a wavelength as short as 120 nm. Target wavelengths include lines of high interest for space observations, such as H Lyman α (121.6 nm), OI (130.4 and 135.6 nm), CIV (154.8, 155.1 nm), among others. Coating-based linear polarizers tuned at H Lyman α (121.6 nm) both based on reflectance or on transmittance. Reflective polarizers present a high efficiency. Transmissive polarizers have a more modest peak performance compared to reflective polarizers; however, they involve spectral filtering properties to reject the long FUV and even more the near UV to the IR, which turn them competitive compared to reflective polarizers. In this communication we present a summary of our research on the above FUV coatings developed at GOLD.

Multivalent-Counterion-Induced Surfactant Multilayer Formation at Hydrophobic and Hydrophilic Solid-Solution Interfaces.

PubMed

Penfold, Jeffrey; Thomas, Robert K; Li, Peixun; Xu, Hui; Tucker, Ian M; Petkov, Jordan T; Sivia, Devinderjit S

2015-06-23

Surface multilayer formation from the anionic-nonionic surfactant mixture of sodium dodecyl dioxyethylene sulfate, SLES, and monododecyl dodecaethylene glycol, C12E12, by the addition of multivalent Al(3+) counterions at the solid-solution interface is observed and characterized by neutron reflectivity, NR. The ability to form surface multilayer structures on hydrophobic and hydrophilic silica and cellulose surfaces is demonstrated. The surface multilayer formation is more pronounced and more well developed on the hydrophilic and hydrophobic silica surfaces than on the hydrophilic and hydrophobic cellulose surfaces. The less well developed multilayer formation on the cellulose surfaces is attributed to the greater surface inhomogeneities of the cellulose surface which partially inhibit lateral coherence and growth of the multilayer domains at the surface. The surface multilayer formation is associated with extreme wetting properties and offers the potential for the manipulation of the solid surfaces for enhanced adsorption and control of the wetting behavior.

A novel multilayer model with controllable mechanical properties for magnesium-based bone plates.

PubMed

Zhou, Juncen; Huang, Wanru; Li, Qing; She, Zuxin; Chen, Funan; Li, Longqin

2015-04-01

Proper mechanical properties are essential for the clinical application of magnesium-based implants. In the present work, a novel multilayer model composed of three layers with desirable features was developed. The modulus of the multilayer model can be adjusted by changing the thickness of each layer. To combine three layers and improve the corrosion resistance of the whole multilayer model, the polycaprolactone coating was employed. In the immersion test, pH values, the concentration of released magnesium ions, and weight loss indicate that the corrosion rate of multilayer models is considerable lower than that of the one-layer bare substrate. The three-point bending test, which is used to examine models' mechanical properties, shows that the flexural modulus of multilayer models is reduced effectively. In addition, the mechanical degradation of multilayer models is more stable, compared to the one-layer substrate.

77 FR 45336 - Multilayered Wood Flooring From the People's Republic of China: Initiation of Antidumping Duty...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-07-31

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... on multilayered wood flooring from the People's Republic of China (``PRC'') meets the statutory and... announcing the antidumping duty order on multilayered wood flooring from the PRC was published in the Federal...

78 FR 46318 - Multilayered Wood Flooring From the People's Republic of China: Initiation of Antidumping Duty...

Federal Register 2010, 2011, 2012, 2013, 2014

2013-07-31

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... antidumping duty order on multilayered wood flooring from the People's Republic of China (``PRC'') meet the...: Background The Department published the antidumping duty order on multilayered wood flooring from the PRC on...

76 FR 37316 - Multilayered Wood Flooring From the People's Republic of China: Notice of Amended Preliminary...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-06-27

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... less than fair value in the antidumping duty investigation of multilayered wood flooring from the... in this proceeding that multilayered wood flooring from the PRC is being, or is likely to be, sold in...

Strain and mechanical properties of the VCM multilayer sheet and their composites using the digital speckle correlation method.

PubMed

Zhang, Dehai; Xie, Guizhong; Li, Yanqin; Liu, Jianxiu

2015-09-01

The digital speckle correlation method (DSCM) is introduced to solve the challenging problems in the related geometric measurement. Theoretical calculations of strain are deduced using the DSCM. Corresponding strains along x and y directions are obtained from uniaxial tension experiments and digital speckle measurements, using the VCM nondeep drawing multilayer sheet, the VCM deep-drawing multilayer sheet, clad films, nondeep drawing substrate, and deep-drawing substrate sheet as the targeted experimental objects. The results show that the maximum strains along the x direction of the VCM nondeep drawing multilayer sheet, the VCM deep-drawing multilayer sheet, clad film, nondeep drawing substrate, and deep-drawing substrate sheet are 68.473%, 48.632%, 91.632%, 50.784% and 40.068%, respectively, while the maximum strains along the y direction are -2.657%, -15.381%, 2.826%, -9.780% and -7.783%, respectively. The mechanical properties of the VCM multilayer sheet are between those of the substrate and clad film, while mechanical properties of the VCM deep-drawing multilayer sheet are superior to those of the VCM nondeep drawing multi-layer sheet.

Flexible IZO/Ag/IZO/Ag multilayer electrode grown on a polyethylene terephthalate substrate using roll-to-roll sputtering

PubMed Central

2012-01-01

We investigated the optical, electrical, structural, and surface properties of roll-to-roll [R2R] sputter-grown flexible IZO/Ag/IZO/Ag [IAIA] multilayer films on polyethylene terephthalate substrates as a function of the top indium zinc oxide [IZO] thickness. It was found that the optical transmittance of the IAIA multilayer was significantly influenced by the top IZO layer thickness, which was grown on identical AIA multilayers. However, the sheet resistance of the IAIA multilayer was maintained between the range 5.01 to 5.1 Ω/square regardless of the top IZO thickness because the sheet resistance of the IAIA multilayer was mainly dependent on the thickness of the Ag layers. Notably, the optimized IAIA multilayer had a constant resistance change (ΔR/R0) under repeated outer bending tests with a radius of 10 mm. The mechanical integrity of the R2R-sputtered IAIA multilayer indicated that hybridization of an IZO and Ag metal layer is a promising flexible electrode scheme for the next-generation flexible optoelectronics. PMID:22222144

Multilayer Brain Networks

NASA Astrophysics Data System (ADS)

Vaiana, Michael; Muldoon, Sarah Feldt

2018-01-01

The field of neuroscience is facing an unprecedented expanse in the volume and diversity of available data. Traditionally, network models have provided key insights into the structure and function of the brain. With the advent of big data in neuroscience, both more sophisticated models capable of characterizing the increasing complexity of the data and novel methods of quantitative analysis are needed. Recently, multilayer networks, a mathematical extension of traditional networks, have gained increasing popularity in neuroscience due to their ability to capture the full information of multi-model, multi-scale, spatiotemporal data sets. Here, we review multilayer networks and their applications in neuroscience, showing how incorporating the multilayer framework into network neuroscience analysis has uncovered previously hidden features of brain networks. We specifically highlight the use of multilayer networks to model disease, structure-function relationships, network evolution, and link multi-scale data. Finally, we close with a discussion of promising new directions of multilayer network neuroscience research and propose a modified definition of multilayer networks designed to unite and clarify the use of the multilayer formalism in describing real-world systems.

Characterization of stable, electroactive protein cage/synthetic polymer multilayer thin films prepared by layer-by-layer assembly

NASA Astrophysics Data System (ADS)

Uto, Koichiro; Yamamoto, Kazuya; Kishimoto, Naoko; Muraoka, Masahiro; Aoyagi, Takao; Yamashita, Ichiro

2013-04-01

We have fabricated electroactive multilayer thin films containing ferritin protein cages. The multilayer thin films were prepared on a solid substrate by the alternate electrostatic adsorption of (apo)ferritin and poly( N-isopropylacrylamide- co-2-carboxyisopropylacrylamide) (NIPAAm- co-CIPAAm) in pH 3.5 acetate buffer solution. The assembly process was monitored using a quartz crystal microbalance. The (apo)ferritin/poly(NIPAAm- co-CIPAAm) multilayer thin films were then cross-linked using a water-soluble carbodiimide, 1-[3-(dimethylamino)propyl]-3-ethylcarbodiimide. The cross-linked films were stable under a variety of conditions. The surface morphology and thickness of the multilayer thin films were characterized by atomic force microscopy, and the ferritin iron cores were observed by scanning electron microscopy to confirm the assembly mechanism. Cyclic voltammetry measurements showed different electrochemical properties for the cross-linked ferritin and apoferritin multilayer thin films, and the effect of stability of the multilayer film on its electrochemical properties was also examined. Our method for constructing multilayer films containing protein cages is expected to be useful in building more complex functional inorganic nanostructures.

Fabrication, characterization, and biological assessment of multilayer laminin γ2 DNA coatings on titanium surfaces.

PubMed

Yang, Guoli; Zhang, Jing; Dong, Wenjing; Liu, Li; Shi, Jue; Wang, Huiming

2016-03-21

The purpose of this work was to fabricate a multilayer laminin γ2 DNA coating on a titanium surface and evaluate its biological properties. A multilayer laminin γ2 DNA coating was fabricated on titanium using a layer-by-layer assembly technique. The rate of coating degradation was evaluated by detecting the amount of cDNA remaining. Surface analysis using X-ray photoelectron spectroscopy, atomic force microscopy, and surface contact angle measurements revealed the multilayer structure to consist of cationic lipid and confirmed that a laminin γ2 DNA layer could be fabricated on titanium via the layer-by-layer assembly process. The transfection efficiency was highest for five layers in the multilayer structure. HEK293 cells cultured on the multilayer films displayed significantly higher adhesion activity than the control group. The expression of laminin γ2 and the co-localization of integrin β4 and plectin were more obvious in HN4 cells cultured on the multilayer laminin γ2 DNA coating, while weak immunoreactivities were observed in the control group. We concluded that the DNA-loaded multilayer provided a surface with good biocompatibility and that the multilayer laminin γ2 DNA coating might be effective in improving cell adhesion and the formation of hemidesmosomes on titanium surfaces.

Effect of multilayer substrate configuration in horizontal subsurface flow constructed wetlands: assessment of treatment performance, biofilm development, and solids accumulation.

PubMed

Ding, Yanli; Lyu, Tao; Bai, Shaoyuan; Li, Zhenling; Ding, Haijing; You, Shaohong; Xie, Qinglin

2018-01-01

This study investigates the influence of multilayer substrate configuration in horizontal subsurface flow constructed wetlands (HSCWs) on their treatment performance, biofilm development, and solids accumulation. Three pilot-scale HSCWs were built to treat campus sewage and have been operational for 3 years. The HSCWs included monolayer (CW1), three-layer (CW3), and six-layer (CW6) substrate configurations with hydraulic conductivity of the substrate increasing from the surface to bottom in the multilayer CWs. It was demonstrated the pollutant removal performance after a 3-year operation improved in the multilayer HSCWs (49-80%) compared to the monolayer HSCW (29-41%). Simultaneously, the multilayer HSCWs exhibited significant features that prevented clogging compared to the monolayer configuration. The amount of accumulated solids was notably higher in the monolayer CW compared to multilayer CWs. Further, multilayer HSCWs could delay clogging by providing higher biofilm development for organics removal and consequently, lesser solids accumulations. Principal component analysis strongly supported the visualization of the performance patterns in the present study and showed that multilayer substrate configuration, season, and sampling locations significantly influenced biofilm growth and solids accumulation. Finally, the present study provided important information to support the improved multilayer configured HSCW implication in the future.

Fabrication, characterization, and biological assessment of multilayer laminin γ2 DNA coatings on titanium surfaces

PubMed Central

Yang, Guoli; Zhang, Jing; Dong, Wenjing; Liu, Li; Shi, Jue; Wang, Huiming

2016-01-01

The purpose of this work was to fabricate a multilayer laminin γ2 DNA coating on a titanium surface and evaluate its biological properties. A multilayer laminin γ2 DNA coating was fabricated on titanium using a layer-by-layer assembly technique. The rate of coating degradation was evaluated by detecting the amount of cDNA remaining. Surface analysis using X-ray photoelectron spectroscopy, atomic force microscopy, and surface contact angle measurements revealed the multilayer structure to consist of cationic lipid and confirmed that a laminin γ2 DNA layer could be fabricated on titanium via the layer-by-layer assembly process. The transfection efficiency was highest for five layers in the multilayer structure. HEK293 cells cultured on the multilayer films displayed significantly higher adhesion activity than the control group. The expression of laminin γ2 and the co-localization of integrin β4 and plectin were more obvious in HN4 cells cultured on the multilayer laminin γ2 DNA coating, while weak immunoreactivities were observed in the control group. We concluded that the DNA-loaded multilayer provided a surface with good biocompatibility and that the multilayer laminin γ2 DNA coating might be effective in improving cell adhesion and the formation of hemidesmosomes on titanium surfaces. PMID:26996815

Fabrication, characterization, and biological assessment of multilayer laminin γ2 DNA coatings on titanium surfaces

NASA Astrophysics Data System (ADS)

Yang, Guoli; Zhang, Jing; Dong, Wenjing; Liu, Li; Shi, Jue; Wang, Huiming

2016-03-01

The purpose of this work was to fabricate a multilayer laminin γ2 DNA coating on a titanium surface and evaluate its biological properties. A multilayer laminin γ2 DNA coating was fabricated on titanium using a layer-by-layer assembly technique. The rate of coating degradation was evaluated by detecting the amount of cDNA remaining. Surface analysis using X-ray photoelectron spectroscopy, atomic force microscopy, and surface contact angle measurements revealed the multilayer structure to consist of cationic lipid and confirmed that a laminin γ2 DNA layer could be fabricated on titanium via the layer-by-layer assembly process. The transfection efficiency was highest for five layers in the multilayer structure. HEK293 cells cultured on the multilayer films displayed significantly higher adhesion activity than the control group. The expression of laminin γ2 and the co-localization of integrin β4 and plectin were more obvious in HN4 cells cultured on the multilayer laminin γ2 DNA coating, while weak immunoreactivities were observed in the control group. We concluded that the DNA-loaded multilayer provided a surface with good biocompatibility and that the multilayer laminin γ2 DNA coating might be effective in improving cell adhesion and the formation of hemidesmosomes on titanium surfaces.

Polypeptide multilayer film co-delivers oppositely-charged drug molecules in sustained manners.

PubMed

Jiang, Bingbing; Defusco, Elizabeth; Li, Bingyun

2010-12-13

The current state-of-the-art for drug-carrying biomedical devices is mostly limited to those that release a single drug. Yet there are many situations in which more than one therapeutic agent is needed. Also, most polyelectrolyte multilayer films intended for drug delivery are loaded with active molecules only during multilayer film preparation. In this paper, we present the integration of capsules as vehicles within polypeptide multilayer films for sustained release of multiple oppositely charged drug molecules using layer-by-layer nanoassembly technology. Calcium carbonate (CaCO(3)) particles were impregnated with polyelectrolytes, shelled with polyelectrolyte multilayers, and then assembled onto polypeptide multilayer films using glutaraldehyde. Capsule-integrated polypeptide multilayer films were obtained after decomposition of CaCO(3) templates. Two oppositely charged drugs were loaded into capsules within polypeptide multilayer films postpreparation based on electrostatic interactions between the drugs and the polyelectrolytes impregnated within capsules. We determined that the developed innovative capsule-integrated polypeptide multilayer films could be used to load multiple drugs of very different properties (e.g., opposite charges) any time postpreparation (e.g., minutes before surgical implantation inside an operating room), and such capsule-integrated films allowed simultaneous delivery of two oppositely charged drug molecules and a sustained (up to two weeks or longer) and sequential release was achieved.

Polypeptide Multilayer Film Co-Delivers Oppositely-Charged Drug Molecules in Sustained Manners

PubMed Central

Jiang, Bingbing; DeFusco, Elizabeth; Li, Bingyun

2010-01-01

The current state-of-the-art for drug-carrying biomedical devices is mostly limited to those that release a single drug. Yet there are many situations in which more than one therapeutic agent is needed. Also, most polyelectrolyte multilayer films intending for drug delivery are loaded with active molecules only during multilayer film preparation. In this paper, we present the integration of capsules as vehicles within polypeptide multilayer films for sustained release of multiple oppositely-charged drug molecules using layer-by-layer nanoassembly technology. Calcium carbonate (CaCO3) particles were impregnated with polyelectrolytes, shelled with polyelectrolyte multilayers, and then assembled onto polypeptide multilayer films using glutaraldehyde. Capsule-integrated polypeptide multilayer films were obtained after decomposition of CaCO3 templates. Two oppositely-charged drugs were loaded into capsules within polypeptide multilayer films post-preparation based on electrostatic interactions between the drugs and the polyelectrolytes impregnated within capsules. We determined that the developed innovative capsule-integrated polypeptide multilayer films could be used to load multiple drugs of very different properties (e.g. opposite charges) any time post-preparation (e.g. minutes before surgical implantation inside an operating room), and such capsule-integrated films allowed simultaneous delivery of two oppositely-charged drug molecules and a sustained (up to two weeks or longer) and sequential release was achieved. PMID:21058719

Multilayer Cloud Detection with the MODIS Near-Infrared Water Vapor Absorption Band

NASA Technical Reports Server (NTRS)

Wind, Galina; Platnick, Steven; King, Michael D.; Hubanks, Paul A,; Pavolonis, Michael J.; Heidinger, Andrew K.; Yang, Ping; Baum, Bryan A.

2009-01-01

Data Collection 5 processing for the Moderate Resolution Imaging Spectroradiometer (MODIS) onboard the NASA Earth Observing System EOS Terra and Aqua spacecraft includes an algorithm for detecting multilayered clouds in daytime. The main objective of this algorithm is to detect multilayered cloud scenes, specifically optically thin ice cloud overlying a lower-level water cloud, that presents difficulties for retrieving cloud effective radius using single layer plane-parallel cloud models. The algorithm uses the MODIS 0.94 micron water vapor band along with CO2 bands to obtain two above-cloud precipitable water retrievals, the difference of which, in conjunction with additional tests, provides a map of where multilayered clouds might potentially exist. The presence of a multilayered cloud results in a large difference in retrievals of above-cloud properties between the CO2 and the 0.94 micron methods. In this paper the MODIS multilayered cloud algorithm is described, results of using the algorithm over example scenes are shown, and global statistics for multilayered clouds as observed by MODIS are discussed. A theoretical study of the algorithm behavior for simulated multilayered clouds is also given. Results are compared to two other comparable passive imager methods. A set of standard cloudy atmospheric profiles developed during the course of this investigation is also presented. The results lead to the conclusion that the MODIS multilayer cloud detection algorithm has some skill in identifying multilayered clouds with different thermodynamic phases

Mo/Si multilayers with enhanced TiO II- and RuO II-capping layers

NASA Astrophysics Data System (ADS)

Yulin, Sergiy; Benoit, Nicolas; Feigl, Torsten; Kaiser, Norbert; Fang, Ming; Chandhok, Manish

2008-03-01

The lifetime of Mo/Si multilayer-coated projection optics is one of the outstanding issues on the road of commercialization of extreme-ultraviolet lithography (EUVL). The application of Mo/Si multilayer optics in EUVL requires both sufficient radiation stability and also the highest possible normal-incidence reflectivity. A serious problem of conventional high-reflective Mo/Si multilayers capped by silicon is the considerable degradation of reflective properties due to carbonization and oxidation of the silicon surface layer under exposure by EUV radiation. In this study, we focus on titanium dioxide (TiO II) and ruthenium dioxide (RuO II) as promising capping layer materials for EUVL multilayer coatings. The multilayer designs as well as the deposition parameters of the Mo/Si systems with different capping layers were optimized in terms of maximum peak reflectivity at the wavelength of 13.5 nm and longterm stability under high-intensive irradiation. Optimized TiO II-capped Mo/Si multilayer mirrors with an initial reflectivity of 67.0% presented a reflectivity drop of 0.6% after an irradiation dose of 760 J/mm2. The reflectivity drop was explained by the partial oxidation of the silicon sub-layer. No reflectivity loss after similar irradiation dose was found for RuO II-capped Mo/Si multilayer mirrors having initial peak reflectivity of 66%. In this paper we present data on improved reflectivity of interface-engineered TiO II- and RuO II-capped Mo/Si multilayer mirrors due to the minimization of both interdiffusion processes inside the multilayer stack and absorption loss in the oxide layer. Reflectivities of 68.5% at the wavelength of 13.4 nm were achieved for both TiO II- and RuO II-capped Mo/Si multilayer mirrors.

Reflectance, Optical Properties, and Stability of Molybdenum/Strontium and Molybdenum/Yttrium Multilayer Mirrors

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kjornrattanawanich, Benjawan

2002-09-01

The motivation of this work is to develop high reflectance normal-incidence multilayer mirrors in the 8-12 nm wavelength region for applications in astronomy and extreme ultraviolet lithography. To achieve this goal, Mo/Sr and Mo/Y multilayers were studied. These multilayers were deposited with a UHV magnetron sputtering system and their reflectances were measured with synchrotron radiation. High normal-incidence reflectances of 23% at 8.8 nm, 40.8% at 9.4 nm, and 48.3% at 10.5 nm were achieved. However, the reflectance of Mo/Sr multilayers decreased rapidly after exposure to air. Attempts to use thin layers of carbon to passivate the surface of Mo/Sr multilayers were unsuccessful. Experimental results on the refractive indexmore » $$\\tilde{n}$$ = 1-δ + iβ of yttrium and molybdenum in the 50-1300 eV energy region are reported in this work. This is the first time ever that values on the refractive index of yttrium are measured in this energy range. The absorption part β was determined through transmittance measurements. The dispersive part δ was calculated by means of the Kramers-Kronig formalism. The newly determined values of the refractive index of molybdenum are in excellent agreement with the published data. Those of yttrium are more accurate and contain fine structures around the yttrium M-absorption edges where Mo/Y multilayers operate. These improved sets of optical data lead to better design and modeling of the optical properties of Mo/Y multilayers. The reflectance quality of Mo/Y multilayers is dependent on their optical and structural properties. To correlate these properties with the multilayer reflectance, x-ray diffraction, Rutherford backscattering spectrometry, and transmission electron microscopy were used to analyze samples. Normal-incidence reflectances of 32.6% at 9.27 nm, 38.4% at 9.48 nm, and 29.6% at 9.46 nm were obtained from three representative Mo/Y multilayers which had about 0%, 25%, and 39% atomic oxygen assimilated in their yttrium layers, respectively. Based on the optical properties, multilayers with higher oxygen content should have higher absorption. However, the 25%-oxygen multilayer had less interface roughness and thus had higher reflectance than the 0%-oxygen sample. The 39%-oxygen multilayer had the highest absorption and roughness, thus had the lowest reflectance among three samples. The optical and structural properties of the multilayers are competing in the reflectance results.« less

76 FR 30656 - Multilayered Wood Flooring From the People's Republic of China: Preliminary Determination of...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-05-26

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-970] Multilayered Wood Flooring... multilayered wood flooring from the People's Republic of China (``PRC'') is being, or is likely to be, sold in... multilayered wood flooring from the PRC filed in proper form by the Coalition for American Hardwood Parity \\1...

Multilayer films with sharp, stable interfaces for use in EUV and soft X-ray application

DOEpatents

Barbee, Jr., Troy W.; Bajt, Sasa

2002-01-01

The reflectivity and thermal stability of Mo/Si (molybdenum/silicon) multilayer films, used in soft x-ray and extreme ultraviolet region, is enhanced by deposition of a thin layer of boron carbide (e.g., B.sub.4 C) between alternating layers of Mo and Si. The invention is useful for reflective coatings for soft X-ray and extreme ultraviolet optics, multilayer for masks, coatings for other wavelengths and multilayers for masks that are more thermally stable than pure Mo/Si multilayers

Multilayer Nanoporous Graphene Membranes for Water Desalination.

PubMed

Cohen-Tanugi, David; Lin, Li-Chiang; Grossman, Jeffrey C

2016-02-10

While single-layer nanoporous graphene (NPG) has shown promise as a reverse osmosis (RO) desalination membrane, multilayer graphene membranes can be synthesized more economically than the single-layer material. In this work, we build upon the knowledge gained to date toward single-layer graphene to explore how multilayer NPG might serve as a RO membrane in water desalination using classical molecular dynamic simulations. We show that, while multilayer NPG exhibits similarly promising desalination properties to single-layer membranes, their separation performance can be designed by manipulating various configurational variables in the multilayer case. This work establishes an atomic-level understanding of the effects of additional NPG layers, layer separation, and pore alignment on desalination performance, providing useful guidelines for the design of multilayer NPG membranes.

Comparison of Mg-based multilayers for solar He II radiation at 30.4 nm wavelength

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu Jingtao; Zhou Sika; Li Haochuan

2010-07-10

Mg-based multilayers, including SiC/Mg, Co/Mg, B4C/Mg, and Si/Mg, are investigated for solar imaging and a He II calibration lamp at a 30.4 nm wavelength. These multilayers were fabricated by a magnetron sputtering method and characterized by x-ray reflection. The reflectivities of these multilayers were measured by synchrotron radiation. Near-normal-incidence reflectivities of Co/Mg and SiC/Mg multilayer mirrors are as high as 40.3% and 44.6%, respectively, while those of B4C/Mg and Si/Mg mirrors are too low for application. The measured results suggest that SiC/Mg, Co/Mg multilayers are promising for a 30.4 nm wavelength.

Figure correction of multilayer coated optics

DOEpatents

Chapman; Henry N. , Taylor; John S.

2010-02-16

A process is provided for producing near-perfect optical surfaces, for EUV and soft-x-ray optics. The method involves polishing or otherwise figuring the multilayer coating that has been deposited on an optical substrate, in order to correct for errors in the figure of the substrate and coating. A method such as ion-beam milling is used to remove material from the multilayer coating by an amount that varies in a specified way across the substrate. The phase of the EUV light that is reflected from the multilayer will be affected by the amount of multilayer material removed, but this effect will be reduced by a factor of 1-n as compared with height variations of the substrate, where n is the average refractive index of the multilayer.

Swift heavy ion irradiation effects in Pt/C and Ni/C multilayers

NASA Astrophysics Data System (ADS)

Gupta, Ajay; Pandita, Suneel; Avasthi, D. K.; Lodha, G. S.; Nandedkar, R. V.

1998-12-01

Irradiation effects of 100 MeV Ag ion irradiation on Ni/C and Pt/C multilayers have been studied using X-ray reflectivity measurements. Modifications are observed in both the multilayers at (dE/dx)e values much below the threshold values for Ni and Pt. This effect is attributed to the discontinuous nature of the metal layers. In both the multilayers interfacial roughness increases with irradiation dose. While Ni/C multilayers exhibit large ion-beam induced intermixing, no observable intermixing is observed in the case of Pt/C multilayer. This difference in the behavior of the two systems suggests a significant role for chemically guided defect motion in the mixing process associated with swift heavy ion irradiation.

Microstructure, mechanical and tribological characterization of CrN/DLC/Cr-DLC multilayer coating with improved adhesive wear resistance

NASA Astrophysics Data System (ADS)

Sui, Xudong; Liu, Jinyu; Zhang, Shuaituo; Yang, Jun; Hao, Junying

2018-05-01

Adhesive wear is one of the major reasons for the failure of components during various tribological application, especially for rubbing with viscous materials. This study presents CrN/DLC/Cr-DLC multilayer composite coatings prepared on a plasma enhanced chemical vapor deposition (PECVD) device with the close field unbalanced magnetron sputtering ion plating (CFUBMSIP) technique. SEM, XRD and Raman spectroscopy were used to determine the structure of multilayer coatings. It was found that the multilayer coatings are composed by the alternating CrN and DLC layers. Compared with the single CrN coatings, the friction coefficient of the CrN/DLC/Cr-DLC multilayer coating decreases about more than seven times after sliding a distance of 500 m. This helps to reduce the adhesive wear of multilayer coatings. Compared with the single CrN and DLC coating, the wear rate of the CrN/DLC/Cr-DLC multilayer coating is reduced by an order of magnitude to 7.10 × 10-17 (sliding with AISI 440C) and 2.64 × 10-17 (sliding with TC4) m3/(N m). The improved tribological performance of multilayer coatings mainly attributes to the introduction of lubricant DLC and hard support CrN layers, the enhancement of crack propagation inhibition, and the increment of elastic recovery value We (71.49%) by multilayer design method.

High reflectance and low stress Mo2C/Be multilayers

DOEpatents

Bajt, Sasa; Barbee, Jr., Troy W.

2001-01-01

A material for extreme ultraviolet (EUV) multilayers that will reflect at about 11.3 nm, have a high reflectance, low stress, and high thermal and radiation stability. The material consists of alternating layers of Mo.sub.2 C and Be deposited by DC magnetron sputtering on a substrate, such as silicon. In one example a Mo.sub.2 C/Be multilayer gave 65.2% reflectance at 11.25 nm measured at 5 degrees off normal incidence angle, and consisted of 70 bilayers with a deposition period of 5.78 nm, and was deposited at 0.83 mTorr argon (Ar) sputtering pressure, with the first and last layers being Be. The stress of the multilayer is tensile and only +88 MPa, compared to +330 MPa of a Mo/Be multilayers of the same thickness. The Mo.sub.2 C/Be multilayer was capped with carbon which produced an increase in reflectivity of about 7% over a similar multilayer with no carbon capping material, thus raising the reflectivity from 58.3% to over 65%. The multilayers were formed using either Mo.sub.2 C or Be as the first and last layers, and initial testing has shown the formation of beryllium carbide at the interfaces between the layers which both stabilizes and has a smoothing effect, and appear to be smoother than the interfaces in Mo/Be multilayers.

Localization of multilayer networks by optimized single-layer rewiring.

PubMed

Jalan, Sarika; Pradhan, Priodyuti

2018-04-01

We study localization properties of principal eigenvectors (PEVs) of multilayer networks (MNs). Starting with a multilayer network corresponding to a delocalized PEV, we rewire the network edges using an optimization technique such that the PEV of the rewired multilayer network becomes more localized. The framework allows us to scrutinize structural and spectral properties of the networks at various localization points during the rewiring process. We show that rewiring only one layer is enough to attain a MN having a highly localized PEV. Our investigation reveals that a single edge rewiring of the optimized MN can lead to the complete delocalization of a highly localized PEV. This sensitivity in the localization behavior of PEVs is accompanied with the second largest eigenvalue lying very close to the largest one. This observation opens an avenue to gain a deeper insight into the origin of PEV localization of networks. Furthermore, analysis of multilayer networks constructed using real-world social and biological data shows that the localization properties of these real-world multilayer networks are in good agreement with the simulation results for the model multilayer network. This paper is relevant to applications that require understanding propagation of perturbation in multilayer networks.

Localization of multilayer networks by optimized single-layer rewiring

NASA Astrophysics Data System (ADS)

Jalan, Sarika; Pradhan, Priodyuti

2018-04-01

We study localization properties of principal eigenvectors (PEVs) of multilayer networks (MNs). Starting with a multilayer network corresponding to a delocalized PEV, we rewire the network edges using an optimization technique such that the PEV of the rewired multilayer network becomes more localized. The framework allows us to scrutinize structural and spectral properties of the networks at various localization points during the rewiring process. We show that rewiring only one layer is enough to attain a MN having a highly localized PEV. Our investigation reveals that a single edge rewiring of the optimized MN can lead to the complete delocalization of a highly localized PEV. This sensitivity in the localization behavior of PEVs is accompanied with the second largest eigenvalue lying very close to the largest one. This observation opens an avenue to gain a deeper insight into the origin of PEV localization of networks. Furthermore, analysis of multilayer networks constructed using real-world social and biological data shows that the localization properties of these real-world multilayer networks are in good agreement with the simulation results for the model multilayer network. This paper is relevant to applications that require understanding propagation of perturbation in multilayer networks.

Tuning cell adhesive properties via layer-by-layer assembly of chitosan and alginate

PubMed Central

Silva, Joana M.; García, José R.; Reis, Rui L.; García, Andrés J.; Mano, João F.

2017-01-01

Understanding the mechanisms controlling cell-multilayer film interactions is crucial to the successful engineering of these coatings for biotechnological and biomedical applications. Herein, we present a strategy to tune the cell adhesive properties of multilayers based on marine polysaccharides with and without cross-linking and/or coating with extracellular matrix proteins. Chemical cross-linking of multilayers improved mechanical properties of the coatings but also elicited changes in surface chemistry that alter the adhesion of human umbilical vein endothelial cells. We evaluated a strategy to decouple the mechanical and chemical properties of these films, enabling the transition from cell-adhesive to cell-resistant multilayers. Addition of chitosan/alginate multilayers on top of cross-linked films decreased endothelial cell adhesion, spreading, and proliferation to similar levels as uncross-linked films. Our findings highlight the key role of surface chemistry in cell-multilayer film interactions, and these engineered nanocoatings represent a tunable model of cell adhesive and non-adhesive multilayered films. PMID:28126597

POLYELECTROLYTE MULTILAYER STAMPING IN AQUEOUS PHASE AND NON-CONTACT MODE

PubMed Central

Mehrotra, Sumit; Lee, Ilsoon; Liu, Chun; Chan, Christina

2011-01-01

Polyelectrolyte multilayer (PEM) transfer printing has been previously achieved by stamping under dry conditions. Here, we show for the first time, that PEM can be transferred from a stamp to the base substrate under aqueous conditions whereby the two surfaces are in a non-contact mode. Degradable multilayers of (PAA/PEG)10.5 followed by non-degradable multilayers of (PDAC/SPS)80.5 were fabricated under acidic pH conditions on either PDMS or glass (stamp), and subsequently transferred over top of another multilayer prepared on a different substrate (base substrate), with a spacing of ~ 200 μm between the stamping surface and the base substrate. This multilayer transfer was performed under physiological pH conditions. This process is referred to herein as non-contact, aqueous-phase multilayer (NAM) transfer. NAM transfer can be useful for applications such as fabricating three-dimensional (3-D) cellular scaffolds. We attempted to create a 3-D cellular scaffold using NAM transfer, and characterized the scaffolds with conventional and fluorescence microscopy. PMID:21860540

Highly efficient blazed grating with multilayer coating for tender X-ray energies.

PubMed

Senf, F; Bijkerk, F; Eggenstein, F; Gwalt, G; Huang, Q; Kruijs, R; Kutz, O; Lemke, S; Louis, E; Mertin, M; Packe, I; Rudolph, I; Schäfers, F; Siewert, F; Sokolov, A; Sturm, J M; Waberski, Ch; Wang, Z; Wolf, J; Zeschke, T; Erko, A

2016-06-13

For photon energies of 1 - 5 keV, blazed gratings with multilayer coating are ideally suited for the suppression of stray and higher orders light in grating monochromators. We developed and characterized a blazed 2000 lines/mm grating coated with a 20 period Cr/C- multilayer. The multilayer d-spacing of 7.3 nm has been adapted to the line distance of 500 nm and the blaze angle of 0.84° in order to provide highest efficiency in the photon energy range between 1.5 keV and 3 keV. Efficiency of the multilayer grating as well as the reflectance of a witness multilayer which were coated simultaneously have been measured. An efficiency of 35% was measured at 2 keV while a maximum efficiency of 55% was achieved at 4 keV. In addition, a strong suppression of higher orders was observed which makes blazed multilayer gratings a favorable dispersing element also for the low X-ray energy range.

Artificial multilayers and nanomagnetic materials.

PubMed

Shinjo, Teruya

2013-01-01

The author has been actively engaged in research on nanomagnetic materials for about 50 years. Nanomagnetic materials are comprised of ferromagnetic systems for which the size and shape are controlled on a nanometer scale. Typical examples are ultrafine particles, ultrathin films, multilayered films and nano-patterned films. In this article, the following four areas of the author's studies are described.(1) Mössbauer spectroscopic studies of nanomagnetic materials and interface magnetism.(2) Preparation and characterization of metallic multilayers with artificial superstructures.(3) Giant magnetoresistance (GMR) effect in magnetic multilayers.(4) Novel properties of nanostructured ferromagnetic thin films (dots and wires).A subject of particular interest in the author's research was the artificially prepared multilayers consisting of metallic elements. The motivation to initiate the multilayer investigation is described and the physical properties observed in the artificial multilayers are introduced. The author's research was initially in the field of pure physical science and gradually extended into applied science. His achievements are highly regarded not only from the fundamental point of view but also from the technological viewpoint.

Infrared metamaterial by RF magnetron sputtered ZnO/Al:ZnO multilayers

NASA Astrophysics Data System (ADS)

Santiago, Kevin C.; Mundle, Rajeh; White, Curtis; Bahoura, Messaoud; Pradhan, Aswini K.

2018-03-01

Hyperbolic metamaterials create artificial anisotropy using metallic wires suspended in dielectric media or alternating layers of a metal and dielectric (Type I or Type II). In this study we fabricated ZnO/Al:ZnO (AZO) multilayers by the RF magnetron sputtering deposition technique. Our fabricated multilayers satisfy the requirements for a type II hyperbolic metamaterial. The optical response of individual AZO and ZnO films, as well as the multilayered film were investigated via UV-vis-IR transmittance and spectroscopic ellipsometry. The optical response of the multilayered system is calculated using the nonlocal-corrected Effective Medium Approximation (EMA). The spectroscopic ellipsometry data of the multilayered system was modeled using a uniaxial material model and EMA model. Both theoretical and experimental studies validate the fabricated multilayers undergo a hyperbolic transition at a wavelength of 2.2 μm. To our knowledge this is the first AZO/ZnO type II hyperbolic metamaterial system fabricated by magnetron sputtering deposition method.

Influences of layer thickness on the compatibility and physical properties of polycarbonate/polystyrene multilayered film via nanolayer coextrusion

NASA Astrophysics Data System (ADS)

Cheng, Junfeng; Chen, Zhiru; Zhou, Jiaqi; Cao, Zheng; Wu, Dun; Liu, Chunlin; Pu, Hongting

2018-05-01

The effects of layer thickness on the compatibility between polycarbonate (PC) and polystyrene (PS) and physical properties of PC/PS multilayered film via nanolayer coextrusion are studied. The morphology of multilayered structure is observed using a scanning electron microscope. This multilayered structure may have a negative impact on the transparency, but it can improve the water resistance and heat resistance of film. To characterize the compatibility between PC and PS, differential scanning calorimetry is used to measure the glass transition temperature. The compatibility is found to be improved with the decrease of layer thickness. Therefore, the viscosity of multilayered film is also reduced with the decrease of layer thickness. In addition, the multilayered structure can improve the tensile strength with the increase of layer numbers. Because of the complete and continuous layer structure of PC, the PC/PS multilayered film can retain its mechanical strength at the temperature above Tg of PS.

Multi-layer assemblies with predetermined stress profile and method for producing same

NASA Technical Reports Server (NTRS)

Heuer, Arthur H. (Inventor); Kahn, Harold (Inventor); Yang, Jie (Inventor); Phillips, Stephen M. (Inventor)

2003-01-01

Multi-layer assemblies of polysilicon thin films having predetermined stress characteristics and techniques for forming such assemblies are disclosed. In particular, a multi-layer assembly of polysilicon thin films may be produced that has a stress level of zero, or substantially so. The multi-layer assemblies comprise at least one constituent thin film having a tensile stress and at least one constituent thin film having a compressive stress. The thin films forming the multi-layer assemblies may be disposed immediately adjacent to one another without the use of intermediate layers between the thin films. Multi-layer assemblies exhibiting selectively determinable overall bending moments are also disclosed. Selective production of overall bending moments in microstructures enables manufacture of such structures with a wide array of geometrical configurations.

Design of a normal incidence multilayer imaging X-ray microscope

NASA Astrophysics Data System (ADS)

Shealy, David L.; Gabardi, David R.; Hoover, Richard B.; Walker, Arthur B. C., Jr.; Lindblom, Joakim F.

Normal incidence multilayer Cassegrain X-ray telescopes were flown on the Stanford/MSFC Rocket X-ray Spectroheliograph. These instruments produced high spatial resolution images of the sun and conclusively demonstrated that doubly reflecting multilayer X-ray optical systems are feasible. The images indicated that aplanatic imaging soft X-ray/EUV microscopes should be achievable using multilayer optics technology. A doubly reflecting normal incidence multilayer imaging X-ray microscope based on the Schwarzschild configuration has been designed. The design of the microscope and the results of the optical system ray trace analysis are discussed. High resolution aplanatic imaging X-ray microscopes using normal incidence multilayer X-ray mirrors should have many important applications in advanced X-ray astronomical instrumentation, X-ray lithography, biological, biomedical, metallurgical, and laser fusion research.

Modelling single shot damage thresholds of multilayer optics for high-intensity short-wavelength radiation sources.

PubMed

Loch, R A; Sobierajski, R; Louis, E; Bosgra, J; Bijkerk, F

2012-12-17

The single shot damage thresholds of multilayer optics for high-intensity short-wavelength radiation sources are theoretically investigated, using a model developed on the basis of experimental data obtained at the FLASH and LCLS free electron lasers. We compare the radiation hardness of commonly used multilayer optics and propose new material combinations selected for a high damage threshold. Our study demonstrates that the damage thresholds of multilayer optics can vary over a large range of incidence fluences and can be as high as several hundreds of mJ/cm(2). This strongly suggests that multilayer mirrors are serious candidates for damage resistant optics. Especially, multilayer optics based on Li(2)O spacers are very promising for use in current and future short-wavelength radiation sources.

Disintegration-controllable stimuli-responsive polyelectrolyte multilayer microcapsules via covalent layer-by-layer assembly.

PubMed

Mu, Bin; Lu, Chunyin; Liu, Peng

2011-02-01

The disintegration-controllable stimuli-responsive polyelectrolyte multilayer microcapsules have been fabricated via the covalent layer-by-layer assembly between the amino groups of chitosan (CS) and the aldehyde groups of the oxidized sodium alginate (OSA) onto the sacrificial templates (polystyrene sulfonate, PSS) which was removed by dialysis subsequently. The covalent crosslinking bonds of the multilayer microcapsules were confirmed by FTIR analysis. The TEM analysis showed that the diameter of the multilayer microcapsules was <200nm. The diameter of the multilayer microcapsules decreased with the increasing of the pH values or the ionic strength. The pH and ionic strength dual-responsive multilayer microcapsules were stable in acidic and neutral media while they could disintegrate only at strong basic media. Copyright © 2010 Elsevier B.V. All rights reserved.

Material optimization of multi-layered enhanced nanostructures

NASA Astrophysics Data System (ADS)

Strobbia, Pietro

The employment of surface enhanced Raman scattering (SERS)-based sensing in real-world scenarios will offer numerous advantages over current optical sensors. Examples of these advantages are the intrinsic and simultaneous detection of multiple analytes, among many others. To achieve such a goal, SERS substrates with throughput and reproducibility comparable to commonly used fluorescence sensors have to be developed. To this end, our lab has discovered a multi-layer geometry, based on alternating films of a metal and a dielectric, that amplifies the SERS signal (multi-layer enhancement). The advantage of these multi-layered structures is to amplify the SERS signal exploiting layer-to-layer interactions in the volume of the structures, rather than on its surface. This strategy permits an amplification of the signal without modifying the surface characteristics of a substrate, and therefore conserving its reproducibility. Multi-layered structures can therefore be used to amplify the sensitivity and throughput of potentially any previously developed SERS sensor. In this thesis, these multi-layered structures were optimized and applied to different SERS substrates. The role of the dielectric spacer layer in the multi-layer enhancement was elucidated by fabricating spacers with different characteristics and studying their effect on the overall enhancement. Thickness, surface coverage and physical properties of the spacer were studied. Additionally, the multi-layered structures were applied to commercial SERS substrates and to isolated SERS probes. Studies on the dependence of the multi-layer enhancement on the thickness of the spacer demonstrated that the enhancement increases as a function of surface coverage at sub-monolayer thicknesses, due to the increasing multi-layer nature of the substrates. For fully coalescent spacers the enhancement decreases as a function of thickness, due to the loss of interaction between proximal metallic films. The influence of the physical properties of the spacer on the multi-layer enhancement were also studied. The trends in Schottky barrier height, interfacial potential and dielectric constant were isolated by using different materials as spacers (i.e., TiO2, HfO2, Ag 2O and Al2O3). The results show that the bulk dielectric constant of the material can be used to predict the relative magnitude of the multi-layer enhancement, with low dielectric constant materials performing more efficiently as spacers. Optimal spacer layers were found to be ultrathin coalescent films (ideally a monolayer) of low dielectric constant materials. Finally, multi-layered structures were observed to be employable to amplify SERS in drastically different substrate geometries. The multi-layered structures were applied to disposable commercial SERS substrates (i.e., Klarite). This project involved the regeneration of the used substrates, by stripping and redepositing the gold coating layer, and their amplification, by using the multi-layer geometry. The latter was observed to amplify the sensitivity of the substrates. Additionally, the multi-layered structures were applied to probes dispersed in solution. Such probes were observed to yield stronger SERS signal when optically trapped and to reduce the background signal. The application of the multi-layered structures on trapped probes, not only further amplified the SERS signal, but also increased the maximum number of applicable layers for the structures.

Energetic composite and system with enhanced mechanical sensitivity to initiation of self-sustained reaction

DOEpatents

Gash, Alexander E [Brentwood, CA; Barbee, Jr., Troy W.

2012-05-29

An energetic composition and system using amassed energetic multilayer pieces which are formed from the division, such as for example by cutting, scoring, breaking, crushing, shearing, etc., of a mechanically activatable monolithic energetic multilayer(s) (e.g. macro-scale sheets of multilayer films), for enhancing the sensitivity of the energetic composite and system to mechanical initiation of self-sustained reaction. In particular, mechanical initiation of the energetic composition may be achieved with significantly lower mechanical energy inputs than that typically required for initiating the monolithic energetic multilayers from which it is derived.

Analytic theory of alternate multilayer gratings operating in single-order regime.

PubMed

Yang, Xiaowei; Kozhevnikov, Igor V; Huang, Qiushi; Wang, Hongchang; Hand, Matthew; Sawhney, Kawal; Wang, Zhanshan

2017-07-10

Using the coupled wave approach (CWA), we introduce the analytical theory for alternate multilayer grating (AMG) operating in the single-order regime, in which only one diffraction order is excited. Differing from previous study analogizing AMG to crystals, we conclude that symmetrical structure, or equal thickness of the two multilayer materials, is not the optimal design for AMG and may result in significant reduction in diffraction efficiency. The peculiarities of AMG compared with other multilayer gratings are analyzed. An influence of multilayer structure materials on diffraction efficiency is considered. The validity conditions of analytical theory are also discussed.

Yield stress and scaling of polyelectrolyte multilayer modified suspensions: effect of polyelectrolyte conformation during multilayer assembly.

PubMed

Hess, Andreas; Aksel, Nuri

2013-09-10

The yield stress of polyelectrolyte multilayer modified suspensions exhibits a surprising dependence on the polyelectrolyte conformation of multilayer films. The rheological data scale onto a universal master curve for each polyelectrolyte conformation as the particle volume fraction, φ, and the ionic strength of the background fluid, I, are varied. It is shown that rough films with highly coiled, brushy polyelectrolytes significantly enhance the yield stress. Moreover, via the ionic strength I of the background fluid, the dynamic yield stress of brushy polyelectrolyte multilayers can be finely adjusted over 2 decades.

Low-temperature interface reactions in layered Au/Sb films: In situ investigation of the formation of an amorphous phase

NASA Astrophysics Data System (ADS)

Boyen, H.-G.; Cossy-Favre, A.; Oelhafen, P.; Siber, A.; Ziemann, P.; Lauinger, C.; Moser, T.; Häussler, P.; Baumann, F.

1995-01-01

Photoelectron-spectroscopy methods combined with electrical-resistance measurements were employed to study the effects of intermixing at Au/Sb interfaces at low temperatures. For the purpose of characterizing the growth processes of the intermixed phase on a ML scale, Au/Sb bilayers (layer thicknesses DAu=0.5-75 ML and DSb=150 ML) were evaporated at 77 K and the different in situ techniques allowed a comparison to vapor-quenched amorphous AuxSb100-x alloys. For Au thicknesses between 0.5 and 0.9 ML, a change from a semiconducting to a metallic behavior of the samples has been detected, as indicated by the development of a steplike photoelectron intensity at the Fermi level. Evidence has been found that for Au coverages <= 6 ML chemical reactions at the Au/Sb interface occur, leading to the formation of a homogeneously intermixed amorphous layer with a maximum thickness of about 2.3 nm and Au concentrations as high as x~=80 at. %. This latter value corresponds to the limiting Au content where amorphous alloys can be prepared at low temperature (0 at. % <=x<= 80 at. %). For nominal coverages beyond 6 ML polycrystalline Au films were formed. Consequently, Au/Sb multilayers with sufficiently small modulation lengths, which were prepared at 130 K by ion-beam sputtering, were observed to grow as a homogeneous amorphous phase over a broad range of compositions, as evidenced by in situ resistance measurements and by comparing the obtained crystallization temperatures to those of vapor-quenched amorphous alloys. Variation of the deposition temperature Ts revealed that an amorphous interface layer is only formed for Ts<= 220 K. This is consistent with the fact that for multilayers with large modulation lengths containing unreacted polycrystalline Au and Sb layers, long-range interdiffusion is found to set in at temperatures above 230 K. This interdiffusion, however, results in the formation of polycrystalline Au-Sb alloys.

Direct leaf wetness measurements and its numerical analysis using a multi-layer atmosphere-soil-vegetation model at a grassland site in pre-alpine region in Germany

NASA Astrophysics Data System (ADS)

Katata, Genki; Held, Andreas; Mauder, Matthias

2014-05-01

The wetness of plant leaf surfaces (leaf wetness) is important in meteorological, agricultural, and environmental studies including plant disease management and the deposition process of atmospheric trace gases and particles. Although many models have been developed to predict leaf wetness, wetness data directly measured at the leaf surface for model validations are still limited. In the present study, the leaf wetness was monitored using seven electrical sensors directly clipped to living leaf surfaces of thin and broad-leaved grasses. The measurements were carried out at the pre-alpine grassland site in TERestrial ENvironmental Observatories (TERENO) networks in Germany from September 20 to November 8, 2013. Numerical simulations of a multi-layer atmosphere-SOiL-VEGetation model (SOLVEG) developed by the authors were carried out for analyzing the data. For numerical simulations, the additional routine meteorological data of wind speed, air temperature and humidity, radiation, rainfall, long-wave radiative surface temperature, surface fluxes, ceilometer backscatter, and canopy or snow depth were used. The model reproduced well the observed leaf wetness, net radiation, momentum and heat, water vapor, and CO2 fluxes, surface temperature, and soil temperature and moisture. In rain-free days, a typical diurnal cycle as a decrease and increase during the day- and night-time, respectively, was observed in leaf wetness data. The high wetness level was always monitored under rain, fog, and snowcover conditions. Leaf wetness was also often high in the early morning due to thawing of leaf surface water frozen during a cold night. In general, leaf wetness was well correlated with relative humidity (RH) in condensation process, while it rather depended on wind speed in evaporation process. The comparisons in RH-wetness relations between leaf characteristics showed that broad-leaved grasses tended to be wetter than thin grasses.

Multilayer Insulation Material Guidelines

NASA Technical Reports Server (NTRS)

Finckenor, M. M.; Dooling, D.

1999-01-01

Multilayer Insulation Material Guidelines provides data on multilayer insulation materials used by previous spacecraft such as Spacelab and the Long-Duration Exposure Facility and outlines other concerns. The data presented in the document are presented for information only. They can be used as guidelines for multilayer insulation design for future spacecraft provided the thermal requirements of each new design and the environmental effects on these materials are taken into account.

Multi-layer seal for electrochemical devices

DOEpatents

Chou, Yeong-Shyung [Richland, WA; Meinhardt, Kerry D [Kennewick, WA; Stevenson, Jeffry W [Richland, WA

2010-11-16

Multi-layer seals are provided that find advantageous use for reducing leakage of gases between adjacent components of electrochemical devices. Multi-layer seals of the invention include a gasket body defining first and second opposing surfaces and a compliant interlayer positioned adjacent each of the first and second surfaces. Also provided are methods for making and using the multi-layer seals, and electrochemical devices including said seals.

Multi-layer seal for electrochemical devices

DOEpatents

Chou, Yeong-Shyung [Richland, WA; Meinhardt, Kerry D [Kennewick, WA; Stevenson, Jeffry W [Richland, WA

2010-09-14

Multi-layer seals are provided that find advantageous use for reducing leakage of gases between adjacent components of electrochemical devices. Multi-layer seals of the invention include a gasket body defining first and second opposing surfaces and a compliant interlayer positioned adjacent each of the first and second surfaces. Also provided are methods for making and using the multi-layer seals, and electrochemical devices including said seals.

AC conductivity and dielectric properties of Ti-doped CoCr 1.2Fe 0.8O 4 spinel ferrite

NASA Astrophysics Data System (ADS)

Elkestawy, M. A.; Abdel kader, S.; Amer, M. A.

2010-01-01

Dielectric properties of spinel ferrite samples Co 1+xTi xCr 1.2-2xFe 0.8O 4 (0≤ x≤0.5) were investigated as a function of frequency at different temperatures using a complex impedance technique. Also Cole-Cole diagrams of both permittivity and electric modulus were investigated at different temperatures to have an insight into the electric nature of the studied solids. It has been found that the electric modulus M* is the dominating property clarifying the intrinsic picture of these polycrystalline ferrites. The low conductivity and loss factor values indicate that the studied compositions may be good candidates for practical applications.

Conformal growth of Mo/Si multilayers on grating substrates using collimated ion beam sputtering

NASA Astrophysics Data System (ADS)

Voronov, D. L.; Gawlitza, P.; Cambie, R.; Dhuey, S.; Gullikson, E. M.; Warwick, T.; Braun, S.; Yashchuk, V. V.; Padmore, H. A.

2012-05-01

Deposition of multilayers on saw-tooth substrates is a key step in the fabrication of multilayer blazed gratings (MBG) for extreme ultraviolet and soft x-rays. Growth of the multilayers can be perturbed by shadowing effects caused by the highly corrugated surface of the substrates, which results in distortion of the multilayer stack structure and degradation of performance of MBGs. To minimize the shadowing effects, we used an ion-beam sputtering machine with a highly collimated atomic flux to deposit Mo/Si multilayers on saw-tooth substrates. The sputtering conditions were optimized by finding a balance between smoothening and roughening processes in order to minimize degradation of the groove profile in the course of deposition and at the same time to keep the interfaces of a multilayer stack smooth enough for high efficiency. An optimal value of energy of 200 eV for sputtering Kr+ ions was found by deposition of test multilayers on flat substrates at a range of ion energies. Two saw-tooth substrates were deposited at energies of 200 eV and 700 eV for the sputtering ions. It was found that reduction of the ion energy improved the blazing performance of the MBG and resulted in a 40% gain in the diffraction efficiency due to better replication of the groove profile by the multilayer. As a result of the optimization performed, an absolute diffraction efficiency of 28.8% was achieved for the 2nd blaze order of the MBG with a groove density of 7350 lines/mm at a wavelength of 13.5 nm. Details of the growth behavior of the multilayers on flat and saw-tooth substrates are discussed in terms of the linear continuous model of film growth.

Conformal growth of Mo/Si multilayers on grating substrates using collimated ion beam sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Voronov, D. L.; Cambie, R.; Dhuey, S.

2012-05-01

Deposition of multilayers on saw-tooth substrates is a key step in the fabrication of multilayer blazed gratings (MBG) for extreme ultraviolet and soft x-rays. Growth of the multilayers can be perturbed by shadowing effects caused by the highly corrugated surface of the substrates, which results in distortion of the multilayer stack structure and degradation of performance of MBGs. To minimize the shadowing effects, we used an ion-beam sputtering machine with a highly collimated atomic flux to deposit Mo/Si multilayers on saw-tooth substrates. The sputtering conditions were optimized by finding a balance between smoothening and roughening processes in order to minimizemore » degradation of the groove profile in the course of deposition and at the same time to keep the interfaces of a multilayer stack smooth enough for high efficiency. An optimal value of energy of 200 eV for sputtering Kr{sup +} ions was found by deposition of test multilayers on flat substrates at a range of ion energies. Two saw-tooth substrates were deposited at energies of 200 eV and 700 eV for the sputtering ions. It was found that reduction of the ion energy improved the blazing performance of the MBG and resulted in a 40% gain in the diffraction efficiency due to better replication of the groove profile by the multilayer. As a result of the optimization performed, an absolute diffraction efficiency of 28.8% was achieved for the 2nd blaze order of the MBG with a groove density of 7350 lines/mm at a wavelength of 13.5 nm. Details of the growth behavior of the multilayers on flat and saw-tooth substrates are discussed in terms of the linear continuous model of film growth.« less

Conformal growth of Mo/Si multilayers on grating substrates using collimated ion beam sputtering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Voronov, D. L.; Gawlitza, Peter; Cambie, Rossana

2012-05-07

Deposition of multilayers on saw-tooth substrates is a key step in the fabrication of multilayer blazed gratings (MBG) for extreme ultraviolet and soft x-rays. Growth of the multilayers can be perturbed by shadowing effects caused by the highly corrugated surface of the substrates, which results in distortion of the multilayer stack structure and degradation of performance of MBGs. In this study, to minimize the shadowing effects, we used an ion-beamsputtering machine with a highly collimated atomic flux to deposit Mo/Si multilayers on saw-tooth substrates. The sputtering conditions were optimized by finding a balance between smoothening and roughening processes in ordermore » to minimize degradation of the groove profile in the course of deposition and at the same time to keep the interfaces of a multilayer stack smooth enough for high efficiency. An optimal value of energy of 200 eV for sputtering Kr + ions was found by deposition of test multilayers on flat substrates at a range of ion energies. Two saw-tooth substrates were deposited at energies of 200 eV and 700 eV for the sputtering ions. It was found that reduction of the ion energy improved the blazing performance of the MBG and resulted in a 40% gain in the diffraction efficiency due to better replication of the groove profile by the multilayer. As a result of the optimization performed, an absolute diffraction efficiency of 28.8% was achieved for the 2nd blaze order of the MBG with a groove density of 7350 lines/mm at a wavelength of 13.5 nm. Lastly, details of the growth behavior of the multilayers on flat and saw-tooth substrates are discussed in terms of the linear continuous model of film growth.« less

Magnetisation reversal in anisotropy graded Co/Pd multilayers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Barton, C. W., E-mail: craig.barton-2@postgrad.manchester.ac.uk; Thomson, T.

2015-08-14

We demonstrate high precision controllability of the magnetization reversal nucleation process in [Co/Pd]{sub 8} multilayer films consisting of two sets of bilayers with high and low perpendicular anisotropy, respectively. The anisotropy of the entire film is set by the degree of Co/Pd interfacial mixing during deposition which provides fine control of the anisotropy of an individual bilayer in the multilayer stack. The relative number of each type of bilayer is used to select the magnetisation reversal behavior such that changing one bilayer changes the properties of the entire multilayer through anisotropy averaging. A simple extension to the sputtering protocol wouldmore » provide multilayer films with fully graded anisotropy, while maintaining a constant saturation magnetization opening new possibilities for the creation of highly engineered multilayer structures for spin torque devices and future magnetic recording media.« less

Identifying key nodes in multilayer networks based on tensor decomposition.

PubMed

Wang, Dingjie; Wang, Haitao; Zou, Xiufen

2017-06-01

The identification of essential agents in multilayer networks characterized by different types of interactions is a crucial and challenging topic, one that is essential for understanding the topological structure and dynamic processes of multilayer networks. In this paper, we use the fourth-order tensor to represent multilayer networks and propose a novel method to identify essential nodes based on CANDECOMP/PARAFAC (CP) tensor decomposition, referred to as the EDCPTD centrality. This method is based on the perspective of multilayer networked structures, which integrate the information of edges among nodes and links between different layers to quantify the importance of nodes in multilayer networks. Three real-world multilayer biological networks are used to evaluate the performance of the EDCPTD centrality. The bar chart and ROC curves of these multilayer networks indicate that the proposed approach is a good alternative index to identify real important nodes. Meanwhile, by comparing the behavior of both the proposed method and the aggregated single-layer methods, we demonstrate that neglecting the multiple relationships between nodes may lead to incorrect identification of the most versatile nodes. Furthermore, the Gene Ontology functional annotation demonstrates that the identified top nodes based on the proposed approach play a significant role in many vital biological processes. Finally, we have implemented many centrality methods of multilayer networks (including our method and the published methods) and created a visual software based on the MATLAB GUI, called ENMNFinder, which can be used by other researchers.

Advanced materials for multilayer mirrors for extreme ultraviolet solar astronomy.

PubMed

Bogachev, S A; Chkhalo, N I; Kuzin, S V; Pariev, D E; Polkovnikov, V N; Salashchenko, N N; Shestov, S V; Zuev, S Y

2016-03-20

We provide an analysis of contemporary multilayer optics for extreme ultraviolet (EUV) solar astronomy in the wavelength ranges: λ=12.9-13.3  nm, λ=17-21  nm, λ=28-33  nm, and λ=58.4  nm. We found new material pairs, which will make new spaceborne experiments possible due to the high reflection efficiencies, spectral resolution, and long-term stabilities of the proposed multilayer coatings. In the spectral range λ=13  nm, Mo/Be multilayer mirrors were shown to demonstrate a better ratio of reflection efficiency and spectral resolution compared with the commonly used Mo/Si. In the spectral range λ=17-21  nm, a new multilayer structure Al/Si was proposed, which had higher spectral resolution along with comparable reflection efficiency compared with the commonly used Al/Zr multilayer structures. In the spectral range λ=30  nm, the Si/B₄C/Mg/Cr multilayer structure turned out to best obey reflection efficiency and long-term stability. The B₄C and Cr layers prevented mutual diffusion of the Si and Mg layers. For the spectral range λ=58  nm, a new multilayer Mo/Mg-based structure was developed; its reflection efficiency and long-term stability have been analyzed. We also investigated intrinsic stresses inherent for most of the multilayer structures and proposed possibilities for stress elimination.

Finite-element modelling of multilayer X-ray optics.

PubMed

Cheng, Xianchao; Zhang, Lin

2017-05-01

Multilayer optical elements for hard X-rays are an attractive alternative to crystals whenever high photon flux and moderate energy resolution are required. Prediction of the temperature, strain and stress distribution in the multilayer optics is essential in designing the cooling scheme and optimizing geometrical parameters for multilayer optics. The finite-element analysis (FEA) model of the multilayer optics is a well established tool for doing so. Multilayers used in X-ray optics typically consist of hundreds of periods of two types of materials. The thickness of one period is a few nanometers. Most multilayers are coated on silicon substrates of typical size 60 mm × 60 mm × 100-300 mm. The high aspect ratio between the size of the optics and the thickness of the multilayer (10 7 ) can lead to a huge number of elements for the finite-element model. For instance, meshing by the size of the layers will require more than 10 16 elements, which is an impossible task for present-day computers. Conversely, meshing by the size of the substrate will produce a too high element shape ratio (element geometry width/height > 10 6 ), which causes low solution accuracy; and the number of elements is still very large (10 6 ). In this work, by use of ANSYS layer-functioned elements, a thermal-structural FEA model has been implemented for multilayer X-ray optics. The possible number of layers that can be computed by presently available computers is increased considerably.

Identifying key nodes in multilayer networks based on tensor decomposition

NASA Astrophysics Data System (ADS)

Wang, Dingjie; Wang, Haitao; Zou, Xiufen

2017-06-01

The identification of essential agents in multilayer networks characterized by different types of interactions is a crucial and challenging topic, one that is essential for understanding the topological structure and dynamic processes of multilayer networks. In this paper, we use the fourth-order tensor to represent multilayer networks and propose a novel method to identify essential nodes based on CANDECOMP/PARAFAC (CP) tensor decomposition, referred to as the EDCPTD centrality. This method is based on the perspective of multilayer networked structures, which integrate the information of edges among nodes and links between different layers to quantify the importance of nodes in multilayer networks. Three real-world multilayer biological networks are used to evaluate the performance of the EDCPTD centrality. The bar chart and ROC curves of these multilayer networks indicate that the proposed approach is a good alternative index to identify real important nodes. Meanwhile, by comparing the behavior of both the proposed method and the aggregated single-layer methods, we demonstrate that neglecting the multiple relationships between nodes may lead to incorrect identification of the most versatile nodes. Furthermore, the Gene Ontology functional annotation demonstrates that the identified top nodes based on the proposed approach play a significant role in many vital biological processes. Finally, we have implemented many centrality methods of multilayer networks (including our method and the published methods) and created a visual software based on the MATLAB GUI, called ENMNFinder, which can be used by other researchers.

Finite-element modelling of multilayer X-ray optics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cheng, Xianchao; Zhang, Lin

Multilayer optical elements for hard X-rays are an attractive alternative to crystals whenever high photon flux and moderate energy resolution are required. Prediction of the temperature, strain and stress distribution in the multilayer optics is essential in designing the cooling scheme and optimizing geometrical parameters for multilayer optics. The finite-element analysis (FEA) model of the multilayer optics is a well established tool for doing so. Multilayers used in X-ray optics typically consist of hundreds of periods of two types of materials. The thickness of one period is a few nanometers. Most multilayers are coated on silicon substrates of typical sizemore » 60 mm × 60 mm × 100–300 mm. The high aspect ratio between the size of the optics and the thickness of the multilayer (10 7) can lead to a huge number of elements for the finite-element model. For instance, meshing by the size of the layers will require more than 10 16elements, which is an impossible task for present-day computers. Conversely, meshing by the size of the substrate will produce a too high element shape ratio (element geometry width/height > 10 6), which causes low solution accuracy; and the number of elements is still very large (10 6). In this work, by use of ANSYS layer-functioned elements, a thermal-structural FEA model has been implemented for multilayer X-ray optics. The possible number of layers that can be computed by presently available computers is increased considerably.« less

Etched-multilayer phase shifting masks for EUV lithography

DOEpatents

Chapman, Henry N.; Taylor, John S.

2005-04-05

A method is disclosed for the implementation of phase shifting masks for EUV lithography. The method involves directly etching material away from the multilayer coating of the mask, to cause a refractive phase shift in the mask. By etching into the multilayer (for example, by reactive ion etching), rather than depositing extra material on the top of the multilayer, there will be minimal absorption loss associated with the phase shift.

Methods for making a multi-layer seal for electrochemical devices

DOEpatents

Chou, Yeong-Shyung [Richland, WA; Meinhardt, Kerry D [Kennewick, WA; Stevenson, Jeffry W [Richland, WA

2007-05-29

Multi-layer seals are provided that find advantageous use for reducing leakage of gases between adjacent components of electrochemical devices. Multi-layer seals of the invention include a gasket body defining first and second opposing surfaces and a compliant interlayer positioned adjacent each of the first and second surfaces. Also provided are methods for making and using the multi-layer seals, and electrochemical devices including said seals.

Direct Loading and Tunable Release of Antibiotics from Polyelectrolyte Multilayers To Reduce Bacterial Adhesion and Biofilm Formation.

PubMed

Wang, Bailiang; Jin, Tingwei; Xu, Qingwen; Liu, Huihua; Ye, Zi; Chen, Hao

2016-05-18

Bacteria adhesion on the surface of biomaterials and following biofilm formation are important problems in biomedical applications. The charged antibiotics with small molar mass can hardly deposit alternately with polymers into multilayered films to load the drug. Herein, the (poly(acrylic acid)-gentamicin/poly(ethylenimine))n ((PAA-GS/PEI)n) multilayer film was designed and constructed via a layer-by-layer self-assembly method. Low molar mass GS cations were first combined with polyanion PAA and self-assembled with PEI to form multilayer films showing exponential growth behavior. The GS dosage could be adjusted by changing the layer number of films. Furthermore, the thermal cross-linking method was used to control the release rate of GS in PBS buffer. Owing to the diffusion of GS, a zone of inhibition of about 7.0 mm showed the efficient disinfection activity of the multilayer film. It could also be seen from the biofilm inhibition assay that the multilayer film effectively inhibited bacterial adhesion and biofilm formation. As the drug loading dosage was 160 μg/cm(2), the multilayer films showed very low cytotoxicity against human lens epithelial cells. The present work provides an easy way to load GS into multilayer films which can be applied to surface modification of implants and biomedical devices.

High proton conductivity in the molecular interlayer of a polymer nanosheet multilayer film.

PubMed

Sato, Takuma; Hayasaka, Yuta; Mitsuishi, Masaya; Miyashita, Tokuji; Nagano, Shusaku; Matsui, Jun

2015-05-12

High proton conductivity was achieved in a polymer multilayer film with a well-defined two-dimensional lamella structure. The multilayer film was prepared by deposition of poly(N-dodecylacryamide-co-acrylic acid) (p(DDA/AA)) monolayers onto a solid substrate using the Langmuir-Blodgett technique. Grazing-angle incidence X-ray diffraction measurement of a 30-layer film of p(DDA/AA) showed strong diffraction peaks in the out-of-plane direction at 2θ = 2.26° and 4.50°, revealing that the multilayer film had a highly uniform layered structure with a monolayer thickness of 2.0 nm. The proton conductivity of the p(DDA/AA) multilayer film parallel to the layer plane direction was 0.051 S/cm at 60 °C and 98% relative humidity with a low activation energy of 0.35 eV, which is comparable to perfluorosulfonic acid membranes. The high conductivity and low activation energy resulted from the formation of uniform two-dimensional proton-conductive nanochannels in the hydrophilic regions of the multilayer film. The proton conductivity of the multilayer film perpendicular to the layer plane was determined to be 2.1 × 10(-13) S/cm. Therefore, the multilayer film showed large anisotropic conductivity with an anisotropic ratio of 2.4 × 10(11).

The multilayer nanoparticles for deep penetration of docetaxel into tumor parenchyma to overcome tumor microenvironment.

PubMed

Khaliq, Nisar Ul; Park, Dal Yong; Lee, Jae Young; Joo, Yeonhee; Oh, Keun Sang; Kim, Jung Seok; Kim, Jin-Seok; Kim, In-San; Kwon, Ick Chan; Yuk, Soon Hong

2016-10-01

Deep penetration of the anticancer drug, docetaxel (DTX), into tumor parenchyma was demonstrated to achieve improved chemotherapy. For this purpose, a multistage nanostructure was designed and characterized using the multilayer nanoparticles (NPs). The multilayer NPs had a core/shell structure. The core was composed of the DTX-loaded Pluronic NPs (diameter: 12nm) that were transferred into the inner side of vesicles to form the vesicle NPs. Förster resonance energy transfer (FRET) in the NPs was observed to verify the incorporation of the DTX-loaded Pluronic NPs into the inner side of the vesicles during the formation of the vesicle NPs. Subsequently, the vesicle NPs were stabilized through Pluronic-lipid bilayer interaction to form the multilayer NPs. To examine the morphology and size distribution of the multilayer NPs, transmittance electron microscopy and dynamic light scattering were used. In vitro release behavior and toxicity were observed to verify the functionality of the multilayer NPs as nanocarriers for cancer therapy. Multistage functionality was evaluated by cellular uptake and tissue distribution behaviors of the multilayer NPs. The biodistribution of the multilayer NPs and their antitumor efficacy were also observed to understand the role of multistage functionality for improved chemotherapy. Copyright © 2016 Elsevier B.V. All rights reserved.

Extended asymmetric-cut multilayer X-ray gratings.

PubMed

Prasciolu, Mauro; Haase, Anton; Scholze, Frank; Chapman, Henry N; Bajt, Saša

2015-06-15

The fabrication and characterization of a large-area high-dispersion blazed grating for soft X-rays based on an asymmetric-cut multilayer structure is reported. An asymmetric-cut multilayer structure acts as a perfect blazed grating of high efficiency that exhibits a single diffracted order, as described by dynamical diffraction throughout the depth of the layered structure. The maximum number of grating periods created by cutting a multilayer deposited on a flat substrate is equal to the number of layers deposited, which limits the size of the grating. The size limitation was overcome by depositing the multilayer onto a substrate which itself is a coarse blazed grating and then polish it flat to reveal the uniformly spaced layers of the multilayer. The number of deposited layers required is such that the multilayer thickness exceeds the step height of the substrate structure. The method is demonstrated by fabricating a 27,060 line pairs per mm blazed grating (36.95 nm period) that is repeated every 3,200 periods by the 120-μm period substrate structure. This preparation technique also relaxes the requirements on stress control and interface roughness of the multilayer film. The dispersion and efficiency of the grating is demonstrated for soft X-rays of 13.2 nm wavelength.

Direct Magnetic Relief Recording Using As40S60: Mn-Se Nanocomposite Multilayer Structures.

PubMed

Stronski, A; Achimova, E; Paiuk, O; Meshalkin, A; Prisacar, A; Triduh, G; Oleksenko, P; Lytvyn, P

2017-12-01

Processes of holographic recording of surface relief structures using As 2 S 3 :Mn-Se multilayer nanostructures as registering media were studied in this paper. Optical properties of As 2 S 3 :Mn, Se layers, and As 2 S 3 :Mn-Se multilayer nanostructures were investigated. Values of optical bandgaps were obtained from Tauc dependencies. Surface relief diffraction gratings were recorded. Direct one-stage formation of surface relief using multilayer nanostructures is considered. For the first time, possibility of direct formation of magnetic relief simultaneous with surface relief formation under optical recording using As 2 S 3 :Mn-Se multilayer nanostructures is shown.

Self-assembled metal nano-multilayered film prepared by co-sputtering method

NASA Astrophysics Data System (ADS)

Xie, Tianle; Fu, Licai; Qin, Wen; Zhu, Jiajun; Yang, Wulin; Li, Deyi; Zhou, Lingping

2018-03-01

Nano-multilayered film is usually prepared by the arrangement deposition of different materials. In this paper, a self-assembled nano-multilayered film was deposited by simultaneous sputtering of Cu and W. The Cu/W nano-multilayered film was accumulated by W-rich layer and Cu-rich layer. Smooth interfaces with consecutive composition variation and semi-coherent even coherent relationship were identified, indicating that a spinodal-like structure with a modulation wavelength of about 20 nm formed during co-deposition process. The participation of diffusion barrier element, such as W, is believed the essential to obtain the nano-multilayered structure besides the technological parameters.

Artificial multilayers and nanomagnetic materials

PubMed Central

SHINJO, Teruya

2013-01-01

The author has been actively engaged in research on nanomagnetic materials for about 50 years. Nanomagnetic materials are comprised of ferromagnetic systems for which the size and shape are controlled on a nanometer scale. Typical examples are ultrafine particles, ultrathin films, multilayered films and nano-patterned films. In this article, the following four areas of the author’s studies are described. (1) Mössbauer spectroscopic studies of nanomagnetic materials and interface magnetism. (2) Preparation and characterization of metallic multilayers with artificial superstructures. (3) Giant magnetoresistance (GMR) effect in magnetic multilayers. (4) Novel properties of nanostructured ferromagnetic thin films (dots and wires). A subject of particular interest in the author’s research was the artificially prepared multilayers consisting of metallic elements. The motivation to initiate the multilayer investigation is described and the physical properties observed in the artificial multilayers are introduced. The author’s research was initially in the field of pure physical science and gradually extended into applied science. His achievements are highly regarded not only from the fundamental point of view but also from the technological viewpoint. PMID:23391605

Tuning the electronic properties of gated multilayer phosphorene: A self-consistent tight-binding study

NASA Astrophysics Data System (ADS)

Li, L. L.; Partoens, B.; Peeters, F. M.

2018-04-01

By taking account of the electric-field-induced charge screening, a self-consistent calculation within the framework of the tight-binding approach is employed to obtain the electronic band structure of gated multilayer phosphorene and the charge densities on the different phosphorene layers. We find charge density and screening anomalies in single-gated multilayer phosphorene and electron-hole bilayers in dual-gated multilayer phosphorene. Due to the unique puckered lattice structure, both intralayer and interlayer charge screenings are important in gated multilayer phosphorene. We find that the electric-field tuning of the band structure of multilayer phosphorene is distinctively different in the presence and absence of charge screening. For instance, it is shown that the unscreened band gap of multilayer phosphorene decreases dramatically with increasing electric-field strength. However, in the presence of charge screening, the magnitude of this band-gap decrease is significantly reduced and the reduction depends strongly on the number of phosphorene layers. Our theoretical results of the band-gap tuning are compared with recent experiments and good agreement is found.

X-ray/EUV optics for astronomy, microscopy, polarimetry, and projection lithography; Proceedings of the Meeting, San Diego, CA, July 9-13, 1990

NASA Technical Reports Server (NTRS)

Hoover, Richard B. (Editor); Walker, Arthur B. C., Jr. (Editor)

1991-01-01

Topics discussed in this issue include the fabrication of multilayer X-ray/EUV coatings; the design, characterization, and test of multilayer X-ray/EUV coatings; multilayer X-ray/EUV monochromators and imaging microscopes; X-ray/EUV telescopes; the test and calibration performance of X-ray/EUV instruments; XUV/soft X-ray projection lithography; X-ray/EUV space observatories and missions; X-ray/EUV telescopes for solar research; X-ray/EUV polarimetry; X-ray/EUV spectrographs; and X-ray/EUV filters and gratings. Papers are presented on the deposition-controlled uniformity of multilayer mirrors, interfaces in Mo/Si multilayers, the design and analysis of an aspherical multilayer imaging X-ray microscope, recent developments in the production of thin X-ray reflecting foils, and the ultraprecise scanning technology. Consideration is also given to an active sun telescope array, the fabrication and performance at 1.33 nm of a 0.24-micron-period multilayer grating, a cylindrical proportional counter for X-ray polarimetry, and the design and analysis of the reflection grating arrays for the X-Ray Multi-Mirror Mission.

Effect of frequency on fretting wear behavior of Ti/TiN multilayer film on depleted uranium

PubMed Central

Zhu, Sheng-Fa; Lu, Lei; Cai, Zhen-Bing

2017-01-01

The Ti/TiN multi-layer film was prepared on the depleted uranium (DU) substrate by cathodic arc ion plating equipment. The character of multi-layer film was studied by SEM, XRD and AES, revealed that the surface was composed of small compact particle and the cross-section had a multi-layer structure. The fretting wear performance under different frequencies was performed by a MFT-6000 machine with a ball-on-plate configuration. The wear morphology was analyzed by white light interferometer, OM and SEM with an EDX. The result shows the Ti/TiN multi-layer film could greatly improve the fretting wear performance compared to the DU substrate. The fretting wear running and damaged behavior are strongly dependent on the film and test frequency. The fretting region of DU substrate and Ti/TiN multi-layer under low test frequency is gross slip. With the increase of test frequency, the fretting region of Ti/TiN multi-layer change from gross slip to mixed fretting, then to partial slip. PMID:28384200

Effect of frequency on fretting wear behavior of Ti/TiN multilayer film on depleted uranium.

PubMed

Wu, Yan-Ping; Li, Zheng-Yang; Zhu, Sheng-Fa; Lu, Lei; Cai, Zhen-Bing

2017-01-01

The Ti/TiN multi-layer film was prepared on the depleted uranium (DU) substrate by cathodic arc ion plating equipment. The character of multi-layer film was studied by SEM, XRD and AES, revealed that the surface was composed of small compact particle and the cross-section had a multi-layer structure. The fretting wear performance under different frequencies was performed by a MFT-6000 machine with a ball-on-plate configuration. The wear morphology was analyzed by white light interferometer, OM and SEM with an EDX. The result shows the Ti/TiN multi-layer film could greatly improve the fretting wear performance compared to the DU substrate. The fretting wear running and damaged behavior are strongly dependent on the film and test frequency. The fretting region of DU substrate and Ti/TiN multi-layer under low test frequency is gross slip. With the increase of test frequency, the fretting region of Ti/TiN multi-layer change from gross slip to mixed fretting, then to partial slip.

A Solution Processed Flexible Nanocomposite Electrode with Efficient Light Extraction for Organic Light Emitting Diodes

NASA Astrophysics Data System (ADS)

Li, Lu; Liang, Jiajie; Chou, Shu-Yu; Zhu, Xiaodan; Niu, Xiaofan; Zhibinyu; Pei, Qibing

2014-03-01

Highly efficient organic light emitting diodes (OLEDs) based on multiple layers of vapor evaporated small molecules, indium tin oxide transparent electrode, and glass substrate have been extensively investigated and are being commercialized. The light extraction from the exciton radiative decay is limited to less than 30% due to plasmonic quenching on the metallic cathode and the waveguide in the multi-layer sandwich structure. Here we report a flexible nanocomposite electrode comprising single-walled carbon nanotubes and silver nanowires stacked and embedded in the surface of a polymer substrate. Nanoparticles of barium strontium titanate are dispersed within the substrate to enhance light extraction efficiency. Green polymer OLED (PLEDs) fabricated on the nanocomposite electrode exhibit a maximum current efficiency of 118 cd/A at 10,000 cd/m2 with the calculated external quantum efficiency being 38.9%. The efficiencies of white PLEDs are 46.7 cd/A and 30.5%, respectively. The devices can be bent to 3 mm radius repeatedly without significant loss of electroluminescent performance. The nanocomposite electrode could pave the way to high-efficiency flexible OLEDs with simplified device structure and low fabrication cost.

A solution processed flexible nanocomposite electrode with efficient light extraction for organic light emitting diodes.

PubMed

Li, Lu; Liang, Jiajie; Chou, Shu-Yu; Zhu, Xiaodan; Niu, Xiaofan; ZhibinYu; Pei, Qibing

2014-03-17

Highly efficient organic light emitting diodes (OLEDs) based on multiple layers of vapor evaporated small molecules, indium tin oxide transparent electrode, and glass substrate have been extensively investigated and are being commercialized. The light extraction from the exciton radiative decay is limited to less than 30% due to plasmonic quenching on the metallic cathode and the waveguide in the multi-layer sandwich structure. Here we report a flexible nanocomposite electrode comprising single-walled carbon nanotubes and silver nanowires stacked and embedded in the surface of a polymer substrate. Nanoparticles of barium strontium titanate are dispersed within the substrate to enhance light extraction efficiency. Green polymer OLED (PLEDs) fabricated on the nanocomposite electrode exhibit a maximum current efficiency of 118 cd/A at 10,000 cd/m(2) with the calculated external quantum efficiency being 38.9%. The efficiencies of white PLEDs are 46.7 cd/A and 30.5%, respectively. The devices can be bent to 3 mm radius repeatedly without significant loss of electroluminescent performance. The nanocomposite electrode could pave the way to high-efficiency flexible OLEDs with simplified device structure and low fabrication cost.

A Solution Processed Flexible Nanocomposite Electrode with Efficient Light Extraction for Organic Light Emitting Diodes

PubMed Central

Li, Lu; Liang, Jiajie; Chou, Shu-Yu; Zhu, Xiaodan; Niu, Xiaofan; ZhibinYu; Pei, Qibing

2014-01-01

Highly efficient organic light emitting diodes (OLEDs) based on multiple layers of vapor evaporated small molecules, indium tin oxide transparent electrode, and glass substrate have been extensively investigated and are being commercialized. The light extraction from the exciton radiative decay is limited to less than 30% due to plasmonic quenching on the metallic cathode and the waveguide in the multi-layer sandwich structure. Here we report a flexible nanocomposite electrode comprising single-walled carbon nanotubes and silver nanowires stacked and embedded in the surface of a polymer substrate. Nanoparticles of barium strontium titanate are dispersed within the substrate to enhance light extraction efficiency. Green polymer OLED (PLEDs) fabricated on the nanocomposite electrode exhibit a maximum current efficiency of 118 cd/A at 10,000 cd/m2 with the calculated external quantum efficiency being 38.9%. The efficiencies of white PLEDs are 46.7 cd/A and 30.5%, respectively. The devices can be bent to 3 mm radius repeatedly without significant loss of electroluminescent performance. The nanocomposite electrode could pave the way to high-efficiency flexible OLEDs with simplified device structure and low fabrication cost. PMID:24632742

Composition of Radioactive Aerosols in the Shelter Construction of the Chernobyl Nuclear Power Plant in 2000-2015

NASA Astrophysics Data System (ADS)

Ogorodnikov, B. I.

2018-06-01

The results of the physicochemical studies of radioactive aerosols inside and outside the Shelter construction at the Arch construction stage of the Chernobyl Nuclear Power Plant (ChNPP) in 2000-2015 were presented. The dominant isotopes were shown to be cesium, strontium, americium, plutonium, and uranium. They are carried by disperse particles of 2-7 μm. In subreactor rooms, in particular, 012/7, the composition of aerosols is affected by the erosion of the fuel-containing mass formed in 1986. Submicron cesium carrier aerosols appear as a result of evaporation and condensation during fires and welding works. Radiocesium is a well-soluble component of aerosols, while plutonium isotopes are not readily soluble components. In several rooms, the contents of radon, thoron, and their daughter products exceeded the permissible values. In April-June 2011, the intake of radionuclides from the accident at the Japanese Fukushima-1 NPP, which had AMAD of 0.5 μm, was detected and tracked using Petryanov multilayer filters. The productivity of filtration units under the dusty conditions in the exclusion zone of ChNPP and in fogs and haze was investigated. Hydrophilic prefilters with 7-10 μm fibers were recommended.

Demonstration of Microsphere Insulation in Cryogenic Vessels

NASA Astrophysics Data System (ADS)

Baumgartner, R. G.; Myers, E. A.; Fesmire, J. E.; Morris, D. L.; Sokalski, E. R.

2006-04-01

While microspheres have been recognized as a legitimate insulation material for decades, actual use in full-scale cryogenic storage tanks has not been demonstrated until now. The performance and life-cycle-cost advantages previously predicted have now been proven. Most bulk cryogenic storage tanks are insulated with either multilayer insulation (MLI) or perlite. Microsphere insulation, consisting of hollow glass bubbles, combines in a single material the desirable properties that other insulations only have individually. The material has high crush strength, low density, is noncombustible, and performs well in soft vacuum. These properties were proven during recent field testing of two 22,700-L (6,000-gallon) liquid nitrogen tanks, one insulated with microsphere insulation and the other with perlite. Normal evaporation rates (NER) for both tanks were monitored with precision test equipment and insulation levels within the tanks were observed through view ports as an indication of insulation compaction. Specific industrial applications were evaluated based on the test results and beneficial properties of microsphere insulation. Over-the-road trailers previously insulated with perlite will benefit not only from the reduced heat leak, but also the reduced mass of microsphere insulation. Economic assessments for microsphere-insulated cryogenic vessels including life-cycle cost are also presented.

Modeling of laser welding of steel and titanium plates with a composite insert

NASA Astrophysics Data System (ADS)

Isaev, V. I.; Cherepanov, A. N.; Shapeev, V. P.

2017-10-01

A 3D model of laser welding proposed before by the authors was extended to the case of welding of metallic plates made of dissimilar materials with a composite multilayer intermediate insert. The model simulates heat transfer in the welded plates and takes into account phase transitions. It was proposed to select the composition of several metals and dimensions of the insert to avoid the formation of brittle intermetallic phases in the weld joint negatively affecting its strength properties. The model accounts for key physical phenomena occurring during the complex process of laser welding. It is capable to calculate temperature regimes at each point of the plates. The model can be used to select the welding parameters reducing the risk of formation of intermetallic plates. It can forecast the dimensions and crystalline structure of the solidified melt. Based on the proposed model a numerical algorithm was constructed. Simulations were carried out for the welding of titanium and steel plates with a composite insert comprising four different metals: copper and niobium (intermediate plates) with steel and titanium (outer plates). The insert is produced by explosion welding. Temperature fields and the processes of melting, evaporation, and solidification were studied.

BaTiO3/PVDF Nanocomposite Film with High Energy Storage Density

NASA Astrophysics Data System (ADS)

Wang, Xiaohui

2016-03-01

A gradated multilayer BaTiO3/poly(vinylidenefluoride) thin film structure is presented to achieve both a higher breakdown strength and a superior energy-storage capability. Key to the process is the sequential deposition of uniform dispersions of the single component source, which generate a blended PVDF-BTO-PVDF structure prior to full evaporation of solvent, and thermal treatment of the dielectric. The result is like sandwich structure with partial 0-3 character. The central layer designed to provide the high electric displacement, is composed of high volume fraction 6-10 nm BTO nanocrystals produced by a TEG-sol method. The outer layers of the structure are predominantly PVDF, with a significantly lower volume fraction of BTO, taking advantage of the higher dielectric strength for pure PVDF at the electrode-nanocomposite interface. The film is mechanically flexible, and can be removed from the substrate, with total thicknesses in the range 1.2 - 1.5 μm. Parallel plate capacitance devices improved dielectric performances, compared to reported values for BTO-PVDF 0-3 nanocomposites, with a maximal discharged energy density of 19.4J/cm3 and dielectric breakdown strengths of up to 495 kV/mm.

Oxide formation and anodic polarization behavior of thin films of amorphous and crystalline FeCrP alloys prepared by ion beam mixing

NASA Astrophysics Data System (ADS)

Demaree, J. D.; Was, G. S.; Sorensen, N. R.

1991-07-01

An experimental program has been conducted to determine the effect of phosphorus on the corrosion and passivation behavior of FeCrP alloys. Chemically homogeneous 60 nm films of Fe10Cr xP ( x from 0 to 35 at.%) were prepared by multilayer evaporation followed by ion beam mixing with Kr + ions. Films with a phosphorus content of at least 25 at.% were found to be entirely amorphous, while films with 15 at.% P consisted of both amorphous and bcc phases. Recrystallization of the amorphous phase was accomplished by heating the samples to 450°C in a purified argon flow furnace. Electrochemical polarization tests in an acid solution have shown the Fe10Cr xP films to be more corrosion resistant than Fe10Cr, with the corrosion resistance increasing with the amount of P present. The corrosion resistance is not significantly affected when the amorphous films are recrystallized, indicating that the behavior is chemically controlled and not a result of the amorphous structure. When examined by XPS, the phosphorus appears to enhance passivation by encouraging Cr enrichment in the oxide and by incorporating in the oxide as phosphate.

Multilayer manipulated diffraction in flower beetles Torynorrhina flammea: intraspecific structural colouration variation

NASA Astrophysics Data System (ADS)

Song, C. X.; Liu, F.; Hao, Y. H.; Hu, X. H.; Zhang, Y. F.; Liu, X. H.

2014-10-01

We report that the intraspecific structural colouration variation of the beetle Torynorrhina flammea is a result of diffraction shifting manipulated by a multilayer sub-structure contained in a three-dimensional (3D) photonic architecture. With a perpendicularly 2D quasiperiodic diffraction grating inserted into the multilayer, the 3D photonic structure gives rise to anticrossing bandgaps of diffraction from the coupling of grating and multilayer bands. The angular dispersion of diffraction induced by the multilayer band shift behaves normally, in contrast to the ‘ultranegative’ behaviour controlled by the quasiperiodic grating. In addition, the diffraction wavelength is more sensitive to the multilayer periodicity than the diffraction grating constant, which explains the ‘smart’ biological selection of T. flammea in its intraspecific colouration variation from red to green to blue. The elucidated mechanism could be advantageous for the potential exploration of novel dispersive optical elements.

The role of symmetry-breaking-induced interface anisotropy in [Fe/Pt]{sub n} multilayer films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li Zhenghua; Center for Geo-environment Science, Faculty of Engineering and Resource Science, Akita University, Tegatagakuen-machi 1-1, Akita 010-8502; Xie Hailong

2011-04-01

The FePt films were deposited with [Fe/Pt]{sub n} multilayer structure on preheated Corning 1737F glass substrate using pure Fe and Pt target in a CMS-18 sputtering system. The dependence of FePt's texture and magnetic properties on the multilayer structure was investigated. The XRD patterns indicate that (111) texture is dominant for all [Fe/Pt]{sub n} (n = 8, 16, 20, 32) multilayer films. However, the measured M-H loops show that the perpendicular anisotropy is greatly enhanced in samples with n = 16, 20, and 32. The origin of the increased perpendicular anisotropy of [Fe/Pt]{sub n} multilayer films is related to themore » contributions of the interfaces, which will be analyzed using the micromagnetic models, with careful discussions of the crystalline and interface anisotropies. Finally, it is confirmed that the Fe/Pt interfaces favor the perpendicular orientation in the multilayer structure.« less

Advanced coatings for next generation lithography

NASA Astrophysics Data System (ADS)

Naujok, P.; Yulin, S.; Kaiser, N.; Tünnermann, A.

2015-03-01

Beyond EUV lithography at 6.X nm wavelength has a potential to extend EUVL beyond the 11 nm node. To implement B-based mirrors and to enable their industrial application in lithography tools, a reflectivity level of > 70% has to be reached in near future. The authors will prove that transition from conventional La/B4C to promising LaN/B4C multilayer coatings leads to enhanced optical properties. Currently a near normal-incidence reflectivity of 58.1% @ 6.65 nm is achieved by LaN/B4C multilayer mirrors. The introduction of ultrathin diffusion barriers into the multilayer design to reach the targeted reflectivity of 70% was also tested. The optimization of multilayer design and deposition process for interface-engineered La/C/B4C multilayer mirrors resulted in peak reflectivity of 56.8% at the wavelength of 6.66 nm. In addition, the thermal stability of several selected multilayers was investigated and will be discussed.

Ag-Pd-Cu alloy inserted transparent indium tin oxide electrodes for organic solar cells

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, Hyo-Joong; Seo, Ki-Won; Kim, Han-Ki, E-mail: imdlhkkim@khu.ac.kr

2014-09-01

The authors report on the characteristics of Ag-Pd-Cu (APC) alloy-inserted indium tin oxide (ITO) films sputtered on a glass substrate at room temperature for application as transparent anodes in organic solar cells (OSCs). The effect of the APC interlayer thickness on the electrical, optical, structural, and morphological properties of the ITO/APC/ITO multilayer were investigated and compared to those of ITO/Ag/ITO multilayer electrodes. At the optimized APC thickness of 8 nm, the ITO/APC/ITO multilayer exhibited a resistivity of 8.55 × 10{sup −5} Ω cm, an optical transmittance of 82.63%, and a figure-of-merit value of 13.54 × 10{sup −3} Ω{sup −1}, comparable to those of the ITO/Ag/ITOmore » multilayer. Unlike the ITO/Ag/ITO multilayer, agglomeration of the metal interlayer was effectively relieved with APC interlayer due to existence of Pd and Cu elements in the thin region of the APC interlayer. The OSCs fabricated on the ITO/APC/ITO multilayer showed higher power conversion efficiency than that of OSCs prepared on the ITO/Ag/ITO multilayer below 10 nm due to the flatness of the APC layer. The improved performance of the OSCs with ITO/APC/ITO multilayer electrodes indicates that the APC alloy interlayer prevents the agglomeration of the Ag-based metal interlayer and can decrease the thickness of the metal interlayer in the oxide-metal-oxide multilayer of high-performance OSCs.« less

Adsorption of IgG on/in a PAH/PSS multilayer film: Layer structure and cell response.

PubMed

Feldötö, Zsombor; Lundin, Maria; Braesch-Andersen, Sten; Blomberg, Eva

2011-02-01

The binding of immunogloblulins (IgG) (mouse monoclonal recognizing IFNγ) on precoated polystyrene or silica surfaces by the layer-by-layer technique has been investigated with QCM-D and DPI. The aim of the work was to increase the sensitivity of the conventional enzyme-linked immunosorbent spot (ELISpot) assay. The polyelectrolytes used to build the multilayers were poly(allylamine hydrochloride) (PAH)/poly(sodium 4-styrenesulfonate) (PSS) alternately adsorbed from 150mM NaCl. The multilayer build up is linear and the internal structure of the PAH/PSS multilayer is compact and rigid as observed by low relative water content (20-25%) and high layer refractive index (n∼1.5) after the formation of five bilayers. Incorporation of IgG within the PAH/PSS multilayer did not give rise to overcharging and did not affect the linear build up. ELISpot test on PAH/PSS multilayer modified polystyrene wells showed that the cytokine response was significantly smaller than on the regular PVDF backed polystyrene wells. This may be due to the compact and rigid nature of the PAH/PSS multilayer, which does not allow formation of the kind of three dimensional support needed to achieve bioactive IgG binding to the surface. Immunological tests of the polyelectrolyte multilayers in the absence of IgG showed that PSS terminated PAH/PSS multilayer did not induce any cytokine response whereas PAH terminated did, which suggests that PSS totally covers the surface from the cells point of view. Copyright © 2010 Elsevier Inc. All rights reserved.

Effect of Alkaline Peroxides on the Surface of Cobalt Chrome Alloy: An In Vitro Study.

PubMed

Vasconcelos, Glenda Lara Lopes; Curylofo, Patricia Almeida; Raile, Priscilla Neves; Macedo, Ana Paula; Paranhos, Helena Freitas Oliveira; Pagnano, Valeria Oliveira

2018-03-24

Removable denture hygiene care is very important for the longevity of the rehabilitation treatment; however, it is necessary to analyze the effects that denture cleansers can cause on the surfaces of prostheses. Thus, this study evaluated the effect of alkaline peroxide-effervescent tablets on the surface of cobalt-chromium alloys (Co-Cr) used in removable partial dentures. Circular metallic specimens (12 × 3 mm) were fabricated and were immersed (n = 16) in: control, Polident 3 Minute (P3M), Steradent (S), Efferdent (E), Polident for Partials (PFP), and Corega Tabs (CT). The surface roughness (μm) (n = 10) was measured before and after periods of cleanser immersion corresponding to 0.5, 1, 2, 3, 4, and 5 years. Ion release was analyzed (n = 5) for Co, Cr, and molybdenum (Mo). Scanning electron microscopy (SEM) analysis and an Energy-dispersive X-ray spectroscopy (EDS) were conducted in one specimen. The surface roughness data were statistically analyzed (α = 0.05) with the Kruskal-Wallis test to compare the solutions, and the Friedman test compared the immersion durations. Ion release analysis was performed using 2-way ANOVA and Tukey's test. There was no significant surface roughness difference when comparing the solutions (p > 0.05) and the immersion durations (p = 0.137). Regarding ion release (μg/L), CT, E, and control produced a greater release of Co ions than S (p < 0.05). CT produced a greater release of Cr ions than control, S, and P3M (p < 0.05). Finally, E caused the greatest release of Mo ions (p < 0.05). SEM confirmed that the solutions did not damage the surfaces and EDS confirmed that there were no signs of oxidation. The various solutions tested did not have any deleterious effects on the Co-Cr alloy surface. Steradent, however, presented the smallest ionic release. © 2018 by the American College of Prosthodontists.

Corrosion behaviours of the dental magnetic keeper complexes made by different alloys and methods.

PubMed

Wu, Min-Ke; Song, Ning; Liu, Fei; Kou, Liang; Lu, Xiao-Wen; Wang, Min; Wang, Hang; Shen, Jie-Fei

2016-09-29

The keeper and cast dowel-coping, as a primary component for a magnetic attachment, is easily subjected to corrosion in a wet environment, such as the oral cavity, which contains electrolyte-rich saliva, complex microflora and chewing behaviour and so on. The objective of this in vitro study was to examine the corrosion resistance of a dowel and coping-keeper complex fabricated by finish keeper and three alloys (cobalt-chromium, CoCr; silver-palladium-gold, PdAu; gold-platinum, AuPt) using a laser-welding process and a casting technique. The surface morphology characteristics and microstructures of the samples were examined by means of metallographic microscope and scanning electron microscope (SEM). Energy-dispersive spectroscopy (EDS) with SEM provided elements analysis information for the test samples after 10% oxalic acid solution etching test. Tafel polarization curve recordings demonstrated parameter values indicating corrosion of the samples when subjected to electrochemical testing. This study has suggested that massive oxides are attached to the surface of the CoCr-keeper complex but not to the AuPt-keeper complex. Only the keeper area of cast CoCr-keeper complex displayed obvious intergranular corrosion and changes in the Fe and Co elements. Both cast and laser-welded AuPt-keeper complexes had the highest free corrosion potential, followed by the PdAu-keeper complex. We concluded that although the corrosion resistance of the CoCr-keeper complex was worst, the keeper surface passive film was actually preserved to its maximum extent. The laser-welded CoCr- and PdAu-keeper complexes possessed superior corrosion resistance as compared with their cast specimens, but no significant difference was found between the cast and laser-welded AuPt-keeper complexes. The Fe-poor and Cr-rich band, appearing on the edge of the keeper when casting, has been proven to be a corrosion-prone area.

Cutting efficiency of air-turbine burs on cast titanium and dental casting alloys.

PubMed

Watanabe, I; Ohkubo, C; Ford, J P; Atsuta, M; Okabe, T

2000-11-01

The purpose of this study was to investigate the cutting efficiency of air-turbine burs on cast free-machining titanium alloy (DT2F) and to compare the results with those for cast commercially pure (CP) Ti, Ti-6Al-4V alloy, and dental casting alloys. The cast metal (DT2F, CP Ti, Ti-6Al-4V, Type IV gold alloy and Co-Cr alloy) specimens were cut with air-turbine burs (carbide burs and diamond points) at air pressures of 138 or 207 kPa and a cutting force of 0.784 N. The cutting efficiency of each bur was evaluated as volume loss calculated from the weight loss cut for 5 s and the density of each metal. The bulk microhardness was measured to correlate the machinability and the hardness of each metal. The amounts of DT2F cut with the carbide burs were significantly (p < 0.05) greater than for the other titanium specimens at either 138 or 207 kPa. The diamond points exhibited similar machining efficiency among all metals except for Type IV gold alloy. The increase in the volume loss of Co-Cr alloy (Vitallium) cut with the diamond points showed a negative value (-29%) with an increase in air pressure from 138 to 207 kPa. There was a negative correlation between the amounts of metal removed (volume loss) and the hardness (r2 = 0.689) when the carbide burs were used. The results of this study indicated that a free-machining titanium alloy (DT2F) exhibited better machinability compared to CP Ti and Ti-6Al-4V alloy when using carbide fissure burs. When machining cast CP Ti and its alloys, carbide fissure burs possessed a greater machining efficiency than the diamond points and are recommended for titanium dental prostheses.

Effect of metal conditioner on bonding of porcelain to cobalt-chromium alloy

PubMed Central

Kajihara, Yutaro; Takenouchi, Yoshihisa; Tanaka, Takuo; Suzuki, Shiro; Minami, Hiroyuki

2016-01-01

PURPOSE The purpose of this study was to evaluate the efficacy of two different metal conditioners for non-precious metal alloys for the bonding of porcelain to a cobalt-chromium (Co-Cr) alloy. MATERIALS AND METHODS Disk-shaped specimens (2.5×10.0 mm) were cast with Co-Cr alloy and used as adherend materials. The bonding surfaces were polished with a 600-grid silicon carbide paper and airborne-particle abraded using 110 µm alumina particles. Bonding specimens were fabricated by applying and firing either of the metal conditioners on the airborne-particle abraded surface, followed by firing porcelain into 5 mm in diameter and 3 mm in height. Specimens without metal conditioner were also fabricated. Shear bond strength for each group (n=8) were measured and compared (α=.05). Sectional view of bonding interface was observed by SEM. EDS analysis was performed to determine the chemical elements of metal conditioners and to determine the failure modes after shear test. RESULTS There were significant differences among three groups, and two metal conditioner-applied groups showed significantly higher values compared to the non-metal conditioner group. The SEM observation of the sectional view at bonding interface revealed loose contact at porcelain-alloy surface for non-metal conditioner group, however, close contact at both alloy-metal conditioner and metal conditioner-porcelain interfaces for both metal conditioner-applied groups. All the specimens showed mixed failures. EDS analysis showed that one metal conditioner was Si-based material, and another was Ti-based material. Si-based metal conditioner showed higher bond strengths compared to the Ti-based metal conditioner, but exhibited more porous failure surface failure. CONCLUSION Based on the results of this study, it can be stated that the application of metal conditioner is recommended for the bonding of porcelain to cobalt-chromium alloys. PMID:26949481

Multi-layer laminate structure and manufacturing method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Keenihan, James R; Cleereman, Robert J; Eurich, Gerald

2012-04-24

The present invention is premised upon a multi-layer laminate structure and method of manufacture, more particularly to a method of constructing the multi-layer laminate structure utilizing a laminate frame and at least one energy activated flowable polymer.

Multi-layer laminate structure and manufacturing method

DOE Office of Scientific and Technical Information (OSTI.GOV)

Keenihan, James R.; Cleereman, Robert J.; Eurich, Gerald

2013-01-29

The present invention is premised upon a multi-layer laminate structure and method of manufacture, more particularly to a method of constructing the multi-layer laminate structure utilizing a laminate frame and at least one energy activated flowable polymer.

Multi-Layer E-Textile Circuits

NASA Technical Reports Server (NTRS)

Dunne, Lucy E.; Bibeau, Kaila; Mulligan, Lucie; Frith, Ashton; Simon, Cory

2012-01-01

Stitched e-textile circuits facilitate wearable, flexible, comfortable wearable technology. However, while stitched methods of e-textile circuits are common, multi-layer circuit creation remains a challenge. Here, we present methods of stitched multi-layer circuit creation using accessible tools and techniques.

Use of information technologies when designing multilayered plates and covers with filler of various types

NASA Astrophysics Data System (ADS)

Golova, T. A.; Magerramova, I. A.; Ivanov, S. A.

2018-05-01

Calculation of multilayered plates and covers does not consider anisotropic properties of a construction. Calculation comes down to uniform isotropic covers and definition of one of intense and deformation conditions of constructions. The existing techniques consider work of multilayered designs by means of various coefficients. The article describes the optimized algorithm of operations when designing multilayered plates and covers with filler of various types on the basis of the conducted researches. It is dealt with a development engineering algorithm of calculation of multi-layer constructions of walls. Software is created which allows one to carry out assessment of intense and deformation conditions of constructions of walls.

Magneto-optical properties of PdCo based multilayered films

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nakamura, K.; Tsunashima, S.; Iwata, S.

1989-09-01

Magneto-optical and magnetic properties of multilayered films composed of PdCo alloy and other noble metal (Pd, Pt or Cu) layers are investigated. Multilayered films were prepared by RF magnetron sputtering method. Kerr rotation spectra (275nm-800nm) of Pd/Co multilayered films resemble those of PdCo alloys. In the films composed of PdCo alloy and Pt bilayers, the Kerr rotation increases with increasing Pt content while the perpendicular anisotropy decreases.

EUV multilayer defect compensation (MDC) by absorber pattern modification: from theory to wafer validation

NASA Astrophysics Data System (ADS)

Pang, Linyong; Hu, Peter; Satake, Masaki; Tolani, Vikram; Peng, Danping; Li, Ying; Chen, Dongxue

2011-11-01

According to the ITRS roadmap, mask defects are among the top technical challenges to introduce extreme ultraviolet (EUV) lithography into production. Making a multilayer defect-free extreme ultraviolet (EUV) blank is not possible today, and is unlikely to happen in the next few years. This means that EUV must work with multilayer defects present on the mask. The method proposed by Luminescent is to compensate effects of multilayer defects on images by modifying the absorber patterns. The effect of a multilayer defect is to distort the images of adjacent absorber patterns. Although the defect cannot be repaired, the images may be restored to their desired targets by changing the absorber patterns. This method was first introduced in our paper at BACUS 2010, which described a simple pixel-based compensation algorithm using a fast multilayer model. The fast model made it possible to complete the compensation calculations in seconds, instead of days or weeks required for rigorous Finite Domain Time Difference (FDTD) simulations. Our SPIE 2011 paper introduced an advanced compensation algorithm using the Level Set Method for 2D absorber patterns. In this paper the method is extended to consider process window, and allow repair tool constraints, such as permitting etching but not deposition. The multilayer defect growth model is also enhanced so that the multilayer defect can be "inverted", or recovered from the top layer profile using a calibrated model.

Layer-by-layer strippable Ag multilayer films fabricated by modular assembly.

PubMed

Li, Yan; Chen, Xiaoyan; Li, Qianqian; Song, Kai; Wang, Shihui; Chen, Xiaoyan; Zhang, Kai; Fu, Yu; Jiao, Yong-Hua; Sun, Ting; Liu, Fu-Chun; Han, En-Hou

2014-01-21

We have developed a new method to fabricate multilayer films, which uses prepared thin films as modular blocks and transfer as operation mode to build up multilayer structures. In order to distinguish it from the in situ fabrication manner, this method is called modular assembly in this study. On the basis of such concept, we have fabricated a multilayer film using the silver mirror film as the modular block and poly(lactic acid) as the transfer tool. Due to the special double-layer structure of the silver mirror film, the resulting multilayer film had a well-defined stratified architecture with alternate porous/compact layers. As a consequence of the distinct structure, the interaction between the adjacent layers was so weak that the multilayer film could be layer-by-layer stripped. In addition, the top layer in the film could provide an effective protection on the morphology and surface property of the underlying layers. This suggests that if the surface of the film was deteriorated, the top layer could be peeled off and the freshly exposed surface would still maintain the original function. The successful preparation of the layer-by-layer strippable silver multilayer demonstrates that modular assembly is a feasible and effective method to build up multilayer films capable of creating novel and attractive micro/nanostructures, having great potential in the fabrication of nanodevices and coatings.

Desktop aligner for fabrication of multilayer microfluidic devices.

PubMed

Li, Xiang; Yu, Zeta Tak For; Geraldo, Dalton; Weng, Shinuo; Alve, Nitesh; Dun, Wu; Kini, Akshay; Patel, Karan; Shu, Roberto; Zhang, Feng; Li, Gang; Jin, Qinghui; Fu, Jianping

2015-07-01

Multilayer assembly is a commonly used technique to construct multilayer polydimethylsiloxane (PDMS)-based microfluidic devices with complex 3D architecture and connectivity for large-scale microfluidic integration. Accurate alignment of structure features on different PDMS layers before their permanent bonding is critical in determining the yield and quality of assembled multilayer microfluidic devices. Herein, we report a custom-built desktop aligner capable of both local and global alignments of PDMS layers covering a broad size range. Two digital microscopes were incorporated into the aligner design to allow accurate global alignment of PDMS structures up to 4 in. in diameter. Both local and global alignment accuracies of the desktop aligner were determined to be about 20 μm cm(-1). To demonstrate its utility for fabrication of integrated multilayer PDMS microfluidic devices, we applied the desktop aligner to achieve accurate alignment of different functional PDMS layers in multilayer microfluidics including an organs-on-chips device as well as a microfluidic device integrated with vertical passages connecting channels located in different PDMS layers. Owing to its convenient operation, high accuracy, low cost, light weight, and portability, the desktop aligner is useful for microfluidic researchers to achieve rapid and accurate alignment for generating multilayer PDMS microfluidic devices.

Oromucosal multilayer films for tailor-made, controlled drug delivery.

PubMed

Lindert, Sandra; Breitkreutz, Jörg

2017-11-01

The oral mucosa has recently become increasingly important as an alternative administration route for tailor-made, controlled drug delivery. Oromucosal multilayer films, assigned to the monograph oromucosal preparations in the Ph.Eur. may be a promising dosage form to overcome the requirements related to this drug delivery site. Areas covered: We provide an overview of multilayer films as drug delivery tools, and discuss manufacturing processes and characterization methods. We focus on the suitability of characterization methods for particular requirements of multilayer films. A classification was performed covering indication areas and APIs incorporated in multilayer film systems for oromucosal use in order to provide a summary of data published in this field. Expert opinion: The shift in drug development to high molecular weight drugs will influence the field of pharmaceutical development and delivery technologies. For a high number of indication areas, such as hormonal disorders, cardiovascular diseases or local treatment of infections, the flexible layer design of oromucosal multilayer films provides a promising option for tailor-made, controlled delivery of APIs to or through defined surfaces in the oral cavity. However, there is a lack of discriminating or standardized testing methods to assess the quality of multilayer films in a reliable way.

Asynchronous cracking with dissimilar paths in multilayer graphene.

PubMed

Jang, Bongkyun; Kim, Byungwoon; Kim, Jae-Hyun; Lee, Hak-Joo; Sumigawa, Takashi; Kitamura, Takayuki

2017-11-16

Multilayer graphene consists of a stack of single-atomic-thick monolayer graphene sheets bound with π-π interactions and is a fascinating model material opening up a new field of fracture mechanics. In this study, fracture behavior of single-crystalline multilayer graphene was investigated using an in situ mode I fracture test under a scanning electron microscope, and abnormal crack propagation in multilayer graphene was identified for the first time. The fracture toughness of graphene was determined from the measured load-displacement curves and the realistic finite element modelling of specimen geometries. Nonlinear fracture behavior of the multilayer graphene is discussed based on nonlinear elastic fracture mechanics. In situ scanning electron microscope images obtained during the fracture test showed asynchronous crack propagation along independent paths, causing interlayer shear stress and slippages. We also found that energy dissipation by interlayer slippages between the graphene layers is the reason for the enhanced fracture toughness of multilayer graphene. The asynchronous cracking with independent paths is a unique cracking and toughening mechanism for single-crystalline multilayer graphene, which is not observed for the monolayer graphene. This could provide a useful insight for the design and development of graphene-based composite materials for structural applications.

Finding overlapping communities in multilayer networks

PubMed Central

Liu, Weiyi; Suzumura, Toyotaro; Ji, Hongyu; Hu, Guangmin

2018-01-01

Finding communities in multilayer networks is a vital step in understanding the structure and dynamics of these layers, where each layer represents a particular type of relationship between nodes in the natural world. However, most community discovery methods for multilayer networks may ignore the interplay between layers or the unique topological structure in a layer. Moreover, most of them can only detect non-overlapping communities. In this paper, we propose a new community discovery method for multilayer networks, which leverages the interplay between layers and the unique topology in a layer to reveal overlapping communities. Through a comprehensive analysis of edge behaviors within and across layers, we first calculate the similarities for edges from the same layer and the cross layers. Then, by leveraging these similarities, we can construct a dendrogram for the multilayer networks that takes both the unique topological structure and the important interplay into consideration. Finally, by introducing a new community density metric for multilayer networks, we can cut the dendrogram to get the overlapping communities for these layers. By applying our method on both synthetic and real-world datasets, we demonstrate that our method has an accurate performance in discovering overlapping communities in multilayer networks. PMID:29694387

Finding overlapping communities in multilayer networks.

PubMed

Liu, Weiyi; Suzumura, Toyotaro; Ji, Hongyu; Hu, Guangmin

2018-01-01

Finding communities in multilayer networks is a vital step in understanding the structure and dynamics of these layers, where each layer represents a particular type of relationship between nodes in the natural world. However, most community discovery methods for multilayer networks may ignore the interplay between layers or the unique topological structure in a layer. Moreover, most of them can only detect non-overlapping communities. In this paper, we propose a new community discovery method for multilayer networks, which leverages the interplay between layers and the unique topology in a layer to reveal overlapping communities. Through a comprehensive analysis of edge behaviors within and across layers, we first calculate the similarities for edges from the same layer and the cross layers. Then, by leveraging these similarities, we can construct a dendrogram for the multilayer networks that takes both the unique topological structure and the important interplay into consideration. Finally, by introducing a new community density metric for multilayer networks, we can cut the dendrogram to get the overlapping communities for these layers. By applying our method on both synthetic and real-world datasets, we demonstrate that our method has an accurate performance in discovering overlapping communities in multilayer networks.

Structural, mechanical and tribocorrosion behaviour in artificial seawater of CrN/AlN nano-multilayer coatings on F690 steel substrates

NASA Astrophysics Data System (ADS)

Ma, Fuliang; Li, Jinlong; Zeng, Zhixiang; Gao, Yimin

2018-01-01

The CrN monolayer and CrN/AlN nano-multilayer coating were successfully fabricated by reactive magnetron sputtering on F690 steel. The results show that CrN monolayer exhibits a face centered cubic crystalline structure with (111) preferred orientation and CrN/AlN nano-multilayer coating has a (200) preferred orientation. This design of the nano-multilayer can interrupt the continuous growth of columnar crystals making the coating denser. The CrN/AlN nano-multilayer coating has a better wear resistance and corrosion resistance compared with the CrN monolayer coating. The tribocorrosion tests reveal that the evolution of potential and current density of F690 steel and CrN monolayer or CrN/AlN nano-multilayer coating see an opposite trend under the simultaneous action of wear and corrosion, which is attributed to that F690 steel is a non-passive material and PVD coatings is a passive material. The nano-multilayer structure has a good ;Pore Sealing Effect;, and the corrosive solution is difficult to pass through the coating to corrode the substrate.

Desktop aligner for fabrication of multilayer microfluidic devices

PubMed Central

Li, Xiang; Yu, Zeta Tak For; Geraldo, Dalton; Weng, Shinuo; Alve, Nitesh; Dun, Wu; Kini, Akshay; Patel, Karan; Shu, Roberto; Zhang, Feng; Li, Gang; Jin, Qinghui; Fu, Jianping

2015-01-01

Multilayer assembly is a commonly used technique to construct multilayer polydimethylsiloxane (PDMS)-based microfluidic devices with complex 3D architecture and connectivity for large-scale microfluidic integration. Accurate alignment of structure features on different PDMS layers before their permanent bonding is critical in determining the yield and quality of assembled multilayer microfluidic devices. Herein, we report a custom-built desktop aligner capable of both local and global alignments of PDMS layers covering a broad size range. Two digital microscopes were incorporated into the aligner design to allow accurate global alignment of PDMS structures up to 4 in. in diameter. Both local and global alignment accuracies of the desktop aligner were determined to be about 20 μm cm−1. To demonstrate its utility for fabrication of integrated multilayer PDMS microfluidic devices, we applied the desktop aligner to achieve accurate alignment of different functional PDMS layers in multilayer microfluidics including an organs-on-chips device as well as a microfluidic device integrated with vertical passages connecting channels located in different PDMS layers. Owing to its convenient operation, high accuracy, low cost, light weight, and portability, the desktop aligner is useful for microfluidic researchers to achieve rapid and accurate alignment for generating multilayer PDMS microfluidic devices. PMID:26233409

Effect of preparation technique on the properties and in vivo efficacy of benzocaine-loaded ethosomes.

PubMed

Maestrelli, Francesca; Capasso, Gaetano; González-Rodríguez, Maria L; Rabasco, Antonio M; Ghelardini, Carla; Mura, Paola

2009-01-01

This study aimed to investigate the influence of the preparation conditions on the performance of an ethosomal formulation for topical delivery of the local anesthetic agent, benzocaine (BZC). Ethosomes were prepared with different techniques, such as thin-layer evaporation, freezing and thawing, reverse-phase evaporation, extrusion and sonication, obtaining, respectively, multilayer vesicles (MLVs), frozen and thawed MLV (FATMLV), large unilamellar vesicles (LUVs), and small unilamellar vesicles (SUVs). The obtained vesicles were characterized for morphology, size, zeta potential, and entrapment efficiency (EE%), and their stability was monitored during storage at 4 degrees C. In vitro permeation properties from gels incorporating drug ethosomal dispersions were evaluated in vitro by using artificial lipophilic membranes, while their anesthetic effect was determined in vivo on rabbits. The results suggested that the vesicle preparation method plays an important role in affecting the properties and effectiveness of ethosomal formulations. MLVs and LUVs exhibited higher drug EE% and better stability than FATMLV and SUV vesicles. The In vitro drug permeation rate was directly related to the vesicle EE% and varied in the order MLV>LUV approximately FATMLV>SUV. The therapeutic efficacy of BZC ethosomal formulations was significantly improved with respect to the corresponding BZC solution. The best results, in terms of enhanced intensity of anesthetic effect, were given by formulations containing MLVs and LUVs, and the order of effectiveness was MLV approximately LUV>FATMLV approximately SUV, rather similar to that found in permeation studies. On the contrary, unexpectedly, the effectiveness order in increasing the duration of drug action was SUV> or =MLV>LUV approximately FATMLV. The highest efficacy of SUVs was probably due to the more intimate contact with the epithelium due to their greatest surface area, which allowed the longest extension of drug therapeutic action. The overall results suggest that a suitably developed ethosomal formulation of BZC can be of actual value for improving its clinical effectiveness in topical anesthesia.

A MULTILAYER BIOCHEMICAL DRY DEPOSITION MODEL 1. MODEL FORMULATION

EPA Science Inventory

A multilayer biochemical dry deposition model has been developed based on the NOAA Multilayer Model (MLM) to study gaseous exchanges between the soil, plants, and the atmosphere. Most of the parameterizations and submodels have been updated or replaced. The numerical integration ...

78 FR 30329 - Multilayered Wood Flooring from China

Federal Register 2010, 2011, 2012, 2013, 2014

2013-05-22

...)] Multilayered Wood Flooring from China AGENCY: United States International Trade Commission. ACTION: Notice of...-1179 (Final) concerning multilayered wood flooring (``MLWF'') from China. For further information... Hardwood Floors, Inc.; BR Custom Surface; Real Wood Floors, LLC; Galleher Corp.; and DPR International, LLC...

Optical multilayers with an amorphous fluoropolymer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chow, R.; Loomis, G.E.; Lindsey, E.F.

1994-07-01

Multilayered coatings were made by physical vapor deposition (PVD) of a perfluorinated amorphous polymer, Teflon AF2400, together with other optical materials. A high reflector at 1064 run was made with ZnS and AF2400. An all-organic 1064-nm reflector was made from AF2400 and polyethylene. Oxide (HfO{sub 2}, SiO{sub 2}) compatibility was also tested. Each multilayer system adhered to itself. The multilayers were influenced by coating stress and unintentional temperature rises during PVD deposition.

Expressions for the evaporation of sessile liquid droplets incorporating the evaporative cooling effect.

PubMed

Wang, Yilin; Ma, Liran; Xu, Xuefeng; Luo, Jianbin

2016-12-15

The evaporation along the surface of pinned, sessile droplets is investigated numerically by using the combined field approach. In the present model, the evaporative cooling at the droplet surface which leads to a reduction in the evaporation is taken into account. Simple, yet accurate analytical expressions for the local evaporation flux and for the total evaporation rate of sessile droplets are obtained. The theoretical analyses indicate that the reduction in the evaporation becomes more pronounced as the evaporative cooling number Ec increases. The results also reveal that the variation of total evaporation rate with contact angle will change its trend as the intensity of the evaporative cooling changes. For small values of Ec, the total evaporation rate increases with the contact angle, the same as predicted by Deegan et al. and by Hu and Larson in their isothermal models in which the evaporative cooling is neglected. Contrarily, when the evaporative cooling effect is strong enough, the total evaporation rate will decrease as the contact angle increases. The present theory is corroborated experimentally, and found in good agreement with the expressions proposed by Hu and Larson in the limiting isothermal case. Copyright © 2016 Elsevier Inc. All rights reserved.

A Magnetron Sputter Deposition System for the Development of Multilayer X-Ray Optics

NASA Technical Reports Server (NTRS)

Broadway, David; Ramsey, Brian; Gubarev, Mikhail

2014-01-01

The proposal objective is to establish the capability to deposit multilayer structures for x-ray, neutron, and EUV optic applications through the development of a magnetron sputtering deposition system. A specific goal of this endeavor is to combine multilayer deposition technology with the replication process in order to enhance the MSFC's position as a world leader in the design of innovative X-ray instrumentation through the development of full shell replicated multilayer optics. The development of multilayer structures is absolutely necessary in order to advance the field of X-ray astronomy by pushing the limit for observing the universe to ever increasing photon energies (i. e. up to 200 keV or higher); well beyond Chandra (approx. 10 keV) and NuStar's (approx. 75 keV) capability. The addition of multilayer technology would significantly enhance the X-ray optics capability at MSFC and allow NASA to maintain its world leadership position in the development, fabrication and design of innovative X-ray instrumentation which would be the first of its kind by combining multilayer technology with the mirror replication process. This marriage of these technologies would allow astronomers to see the universe in a new light by pushing to higher energies that are out of reach with today's instruments.To this aim, a magnetron vacum sputter deposition system for the deposition of novel multilayer thin film X-ray optics is proposed. A significant secondary use of the vacuum deposition system includes the capability to fabricate multilayers for applications in the field of EUV optics for solar physics, neutron optics, and X-ray optics for a broad range of applications including medical imaging.

A Magnetron Sputter Deposition System for the Development of X-Ray Multilayer Optics

NASA Technical Reports Server (NTRS)

Broadway, David

2015-01-01

The project objective is to establish the capability to deposit multilayer structures for x-ray, neutron, and extreme ultraviolet (EUV) optic applications through the development of a magnetron sputtering deposition system. A specific goal of this endeavor is to combine multilayer deposition technology with the replication process in order to enhance NASA Marshall Space Flight Center's (MSFC's) position as a world leader in the design of innovative x-ray instrumentation through the development of full shell replicated multilayer optics. The development of multilayer structures are absolutely necessary in order to advance the field of x-ray astronomy by pushing the limit for observing the universe to ever-increasing photon energies (i.e., up to 200 keV or higher), well beyond Chandra's (approx.10 keV) and NuStar's (approx.75 keV) capability. The addition of multilayer technology would significantly enhance the x-ray optics capability at MSFC and allow NASA to maintain its world leadership position in the development, fabrication, and design of innovative x-ray instrumentation, which would be the first of its kind by combining multilayer technology with the mirror replication process. This marriage of these technologies would allow astronomers to see the universe in a new light by pushing to higher energies that are out of reach with today's instruments. To this aim, a magnetron vacuum sputter deposition system for the deposition of novel multilayer thin film x-ray optics is proposed. A significant secondary use of the vacuum deposition system includes the capability to fabricate multilayers for applications in the field of EUV optics for solar physics, neutron optics, and x-ray optics for a broad range of applications including medical imaging.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Upadhyaya, Mihir; Jindal, Vibhu; Basavalingappa, Adarsh

The availability of defect-free masks is considered to be a critical issue for enabling extreme ultraviolet lithography (EUVL) as the next generation technology. Since completely defect-free masks will be hard to achieve, it is essential to have a good understanding of the printability of the native EUV mask defects. In this work, we performed a systematic study of native mask defects to understand the defect printability caused by them. The multilayer growth over native substrate mask blank defects was correlated to the multilayer growth over regular-shaped defects having similar profiles in terms of their width and height. To model themore » multilayer growth over the defects, a novel level-set multilayer growth model was used that took into account the tool deposition conditions of the Veeco Nexus ion beam deposition tool. The same tool was used for performing the actual deposition of the multilayer stack over the characterized native defects, thus ensuring a fair comparison between the actual multilayer growth over native defects, and modeled multilayer growth over regular-shaped defects. Further, the printability of the characterized native defects was studied with the SEMATECH-Berkeley Actinic Inspection Tool (AIT), an EUV mask-imaging microscope at Lawrence Berkeley National Laboratory (LBNL). Printability of the modeled regular-shaped defects, which were propagated up the multilayer stack using level-set growth model was studied using defect printability simulations implementing the waveguide algorithm. Good comparison was observed between AIT and the simulation results, thus demonstrating that multilayer growth over a defect is primarily a function of a defect’s width and height, irrespective of its shape. This would allow us to predict printability of the arbitrarily-shaped native EUV mask defects in a systematic and robust manner.« less

Formation of He-Rich Layers Observed by Neutron Reflectometry in the He-Ion-Irradiated Cr/W Multilayers: Effects of Cr/W Interfaces on the He-Trapping Behavior.

PubMed

Chen, Feida; Tang, Xiaobin; Huang, Hai; Li, Xinxi; Wang, Yan; Huang, Chaoqiang; Liu, Jian; Li, Huan; Chen, Da

2016-09-21

Cr/W multilayer nanocomposites were presented in the paper as potential candidate materials for the plasma facing components in fusion reactors. We used neutron reflectometry to measure the depth profile of helium in the multienergy He ions irradiated [Cr/W (50 nm)]3 multilayers. Results showed that He-rich layers with low neutron scattering potential energy form at the Cr/W interfaces, which is in great agreement with previous modeling results of other multilayers. This phenomenon provided a strong evidence for the He trapping effects of Cr/W interfaces and implied the possibility of using the Cr/W multilayer nanocomposites as great He-tolerant plasma facing materials.

An in vivo study on the effect of coating stability on osteointegration performance of collagen/hyaluronic acid multilayer modified titanium implants.

PubMed

Ao, Haiyong; Zong, Jiajia; Nie, Yanjiao; Wan, Yizao; Zheng, Xiebin

2018-03-01

Aseptic loosening of implant is one of the main causes of Ti-based implant failure. In our previous work, a novel stable collagen/hyaluronic acid (Col/HA) multilayer modified titanium coatings (TCs) was developed by layer-by-layer (LBL) covalent immobilization technique, which showed enhanced biological properties compared with TCs that were physically absorbed with Col/HA multilayer in vitro . In this study, a rabbit model with femur condyle defect was employed to compare the osteointegration performance of them. Results indicated that Col/HA multilayer with favourable stability could better facilitate osteogenesis around implants and bone-implant contact. The Col/HA multilayer covalent-immobilized TC may reduce aseptic loosening of implant.

RBS Depth Profiling Analysis of (Ti, Al)N/MoN and CrN/MoN Multilayers.

PubMed

Han, Bin; Wang, Zesong; Devi, Neena; Kondamareddy, K K; Wang, Zhenguo; Li, Na; Zuo, Wenbin; Fu, Dejun; Liu, Chuansheng

2017-12-01

(Ti, Al)N/MoN and CrN/MoN multilayered films were synthesized on Si (100) surface by multi-cathodic arc ion plating system with various bilayer periods. The elemental composition and depth profiling of the films were investigated by Rutherford backscattering spectroscopy (RBS) using 2.42 and 1.52 MeV Li 2+ ion beams and different incident angles (0°, 15°, 37°, and 53°). The microstructures of (Ti, Al)N/MoN multilayered films were evaluated by X-ray diffraction. The multilayer periods and thickness of the multilayered films were characterized by scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HR-TEM) and then compared with RBS results.

Preparation for B4C/Mo2C multilayer deposition of alternate multilayer gratings with high efficiency in the 0.5-2.5 keV energy range

NASA Astrophysics Data System (ADS)

Choueikani, Fadi; Delmotte, Franck; Bridou, Françoise; Lagarde, Bruno; Mercere, Pascal; Otero, Edwige; Ohresser, Philippe; Polack, François

2013-03-01

This paper presents a study of B4C/Mo2C multilayers mirrors with the aim of using it in the achievement of Alternate MultiLayer (AML) grating. Such component allows a high efficiency in the 500-2500 eV energy range for the DEIMOS beamline. Multilayers were deposited on silicon substrate. They are characterized by reflectometry under grazing incidence. Numerical adjustments were performed with a model of two layers in the period without any interfacial. A prototype of AML grating was fabricated and characterized. The efficiency of the first order of diffraction was worth 15% at 1700 eV.