Improvement and evaluation of thermal, electrical, sealing and mechanical contacts, and their interface materials

NASA Astrophysics Data System (ADS)

Luo, Xiangcheng

Material contacts, including thermal, electrical, seating (fluid sealing and electromagnetic sealing) and mechanical (pressure) contacts, together with their interface materials, were, evaluated, and in some cases, improved beyond the state of the art. The evaluation involved the use of thermal, electrical and mechanical methods. For thermal contacts, this work evaluated and improved the heat transfer efficiency between two contacting components by developing various thermal interface pastes. Sodium silicate based thermal pastes (with boron nitride particles as the thermally conductive filler) as well as polyethylene glycol (PEG) based thermal pastes were developed and evaluated. The optimum volume fractions of BN in sodium silicate based pastes and PEG based pastes were 16% and 18% respectively. The contribution of Li+ ions to the thermal contact conductance in the PEG-based paste was confirmed. For electrical contacts, the relationship between the mechanical reliability and electrical reliability of solder/copper and silver-epoxy/copper joints was addressed. Mechanical pull-out testing was conducted on solder/copper and silver-epoxy/copper joints, while the contact electrical resistivity was measured. Cleansing of the copper surface was more effective for the reliability of silver-epoxy/copper joint than that of solder/copper joint. For sealing contacts, this work evaluated flexible graphite as an electromagnetic shielding gasket material. Flexible graphite was found to be at least comparable to conductive filled silicone (the state of the art) in terms of the shielding effectiveness. The conformability of flexible graphite with its mating metal surface under repeated compression was characterized by monitoring the contact electrical resistance, as the conformability is important to both electromagnetic scaling and fluid waling using flexible graphite. For mechanical contacts, this work focused on the correlation of the interface structure (such as elastic/plastic deformation, oxidation, strain hardening, passive layer damage, fracture, etc.) with the electrical contact resistance, which was measured in real time for contacts under dynamic compression, thus allowing both reversible and irreversible changes to be observed. The materials studied included metals (carbon steel, stainless steel, aluminum and copper), carbon fiber reinforced polymer-matrix composite (nylon-6), ceramic (mortar) and graphite, due to their relevance to fastening, concrete structures, electric brushes and electrical pressure contacts.

Status of Understanding for Seal Materials

NASA Technical Reports Server (NTRS)

Brown, P. F.

1984-01-01

Material selection for mainshaft face and ring seals, labyrinth seals, accessory gearbox face seals, and lip seals are discussed in light of tribology requirements and a given seal application. Carbon graphite has been found to be one of the best sealing materials and it is widely used in current gas turbine mainshaft and accessory gearbox seals. Its popularity is due to its unique combination of properties which consists of dimensional stability, corrosion resistance, low friction, good self lubricating characteristics, high thermal conductivity and low thermal expansion, the latter two properties combining to provide good thermal shock resistance. A brief description of the seals and the requirements they must meet are discussed to provide insight into the limitations and advantages of the seals in containing the lubricant. A forecast is made of the operational requirements of main shaft and gearbox seals for advanced engines and candidate materials and coatings that may satisfy these advanced engine requirements.

Closed tubes preparation of graphite for high-precision AMS radiocarbon analysis

NASA Astrophysics Data System (ADS)

Hajdas, I.; Michczynska, D.; Bonani, G.; Maurer, M.; Wacker, L.

2009-04-01

Radiocarbon dating is an established tool applied in Geochronology. Technical developments of Accelerator Mass Spectrometry AMS, which allow measurements of samples containing less than 1 mg of carbon, opened opportunities for new applications. Moreover, high resolution records of the past changes require high-resolution chronologies i.e. sampling for 14C dating. In result, the field of applications is rapidly expanding and number of radiocarbon analysis is growing rapidly. Nowadays dedicated 14C AMS machines have great capacity for analysis but in order to keep up with the demand for analysis and provide the results as fast as possible a very efficient way of sample preparation is required. Sample preparation for 14C AMS analysis consists of two steps: separation of relevant carbon from the sample material (removing contamination) and preparation of graphite for AMS analysis. The last step usually involves reaction of CO2 with H2, in the presence of metal catalyst (Fe or Co) of specific mesh size heated to 550-625°C, as originally suggested by Vogel et al. (1984). Various graphitization systems have been built in order to fulfil the requirement of sample quality needed for high-precision radiocarbon data. In the early 90ties another method has been proposed (Vogel 1992) and applied by few laboratories mainly for environmental or biomedical samples. This method uses TiH2 as a source of H2 and can be easily and flexibly applied to produce graphite. Sample of CO2 is frozen in to the tube containing pre-conditioned Zn/TiH2 and Fe catalyst. Torch sealed tubes are then placed in the stepwise heated oven at 500/550°C and left to react for several hours. The greatest problem is the lack of control of the reaction completeness and considerable fractionation. However, recently reported results (Xu et al. 2007) suggest that high precision dating using graphite produced in closed tubes might be possible. We will present results of radiocarbon dating of the set of standards and secondary IAEA standards to demonstrate to what level this method can be used for high precision radiocarbon dating. References Vogel JS. 1992. Rapid Production of Graphite without Contamination for Biomedical Ams. Radiocarbon 34: 344-350. Vogel JS, Southon JR, Nelson DE, and Brown TA. 1984. Performance of Catalytically Condensed Carbon for Use in Accelerator Mass-Spectrometry. Nuclear Instruments & Methods in Physics Research Section B-Beam Interactions with Materials and Atoms 233: 289-293. Xu X, Trumbore SE, Zheng S, Southon JR, McDuffee KE, Luttgen M, and Liu JC. 2007. Modifying a sealed tube zinc reduction method for preparation of AMS graphite targets: Reducing background and attaining high precision. Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms Accelerator Mass Spectrometry - Proceedings of the Tenth International Conference on Accelerator Mass Spectrometry 259: 320-329.

Effect of filler content on the properties of expanded- graphite-based composite bipolar plates for application in polymer electrolyte membrane fuel cells

NASA Astrophysics Data System (ADS)

Masand, Aakash; Borah, Munu; Pathak, Abhishek K.; Dhakate, Sanjay R.

2017-09-01

Minimization of the weight and volume of a hydrogen-based PEM fuel cell stack is an essential area of research for the development and commercialization of PEMFCs for various applications. Graphite-based composite bipolar plates have significant advantages over conventional metallic bipolar plates due to their corrosion resistivity and low cost. On the other hand, expanded graphite is seen to be a potential candidate for facilitating the required electrical, thermal and mechanical properties of bipolar plates with a low density. Therefore, in the present study, the focus is on minimization of the high loading of graphite and optimizes its composition to meet the target properties of bipolar plates as per the USDOE target. Three types of expanded graphite (EG)-phenolic-resin-based composite bipolar plates were developed by partially replacing the expanded graphite content with natural graphite (NG) and carbon black as an additional filler. The three types of composite plate with the reinforcing constituent ratio EG:NG:R (25:25:50) give a bending strength of 49 MPa, a modulus of ~6 GPa, electrical conductivity  >100 S cm-1, a shore hardness of 55 and a bulk density of 1.55 g/cc. The 50 wt% loading of resin is sufficient to wet the 50 wt% filler content in the composite plate. This study gives an insight into using hybrid reinforcements in order to achieve the desired properties of bipolar plates.

14C sample preparation for AMS microdosing studies at Lund University using online combustion and septa-sealed vials

NASA Astrophysics Data System (ADS)

Sydoff, Marie; Stenström, Kristina

2010-04-01

The Department of Physics at Lund University is participating in a European Union project called EUMAPP (European Union Microdose AMS Partnership Programme), in which sample preparation and accelerator mass spectrometry (AMS) measurements of biological samples from microdosing studies have been made. This paper describes a simplified method of converting biological samples to solid graphite for 14C analysis with AMS. The method is based on online combustion of the samples, and reduction of CO 2 in septa-sealed vials. The septa-sealed vials and disposable materials are used to eliminate sample cross-contamination. Measurements of ANU and Ox I standards show deviations of 2% and 3%, respectively, relative to reference values. This level of accuracy is sufficient for biological samples from microdosing studies. Since the method has very few handling steps from sample to graphite, the risk of failure during the sample preparation process is minimized, making the method easy to use in routine preparation of samples.

Turbine with radial acting seal

DOEpatents

Eng, Darryl S; Ebert, Todd A

2016-11-22

A floating brush seal in a rim cavity of a turbine in a gas turbine engine, where the floating brush seal includes a seal holder in which the floating brush seal floats, and a expandable seal that fits within two radial extending seal slots that maintains a seal with radial displacement of the floating brush seal and the seal holder.

Status of Seal Development at Technetics

NASA Astrophysics Data System (ADS)

Chappel, Doug

2002-10-01

Technetics has recently reported results for blade tip seal rub characteristics. Expanding on this work, Technetics will share rub characteristics for knife edge abradable seal systems typical of those found at vane inner air seal and shaft seal locations.

Sealing ceramic material in low melting point glass

NASA Technical Reports Server (NTRS)

Moritoki, M.; Fujikawa, T.; Miyanaga, J.

1984-01-01

A structured device placed in an aerated crucible to pack ceramics molding substance that is to be processed was designed. The structure is wrapped by sealing material made of pyrex glass and graphite foil or sheet with a weight attached on top of it. The crucible is made of carbon; the ceramics material to be treated through heat intervenient press process is molding substance consisting mainly of silicon nitride.

Mechanically expandable annular seal

DOEpatents

Gilmore, R.F.

1983-07-19

A mechanically expandable annular reusable seal assembly to form an annular hermetic barrier between two stationary, parallel, and planar containment surfaces is described. A rotatable ring, attached to the first surface, has ring wedges resembling the saw-tooth array of a hole saw. Matching seal wedges are slidably attached to the ring wedges and have their motion restricted to be perpendicular to the second surface. Each seal wedge has a face parallel to the second surface. An annular elastomer seal has a central annular region attached to the seal wedges' parallel faces and has its inner and outer circumferences attached to the first surface. A rotation of the ring extends the elastomer seal's central region perpendicularly towards the second surface to create the fluid tight barrier. A counter rotation removes the barrier. 6 figs.

Method of making a sodium sulfur battery

DOEpatents

Elkins, Perry E.

1981-01-01

A method of making a portion of a sodium sulfur battery is disclosed. The battery portion made is a portion of the container which defines the volume for the cathodic reactant materials which are sulfur and sodium polysulfide materials. The container portion is defined by an outer metal casing with a graphite liner contained therein, the graphite liner having a coating on its internal diameter for sealing off the porosity thereof. The steel outer container and graphite pipe are united by a method which insures that at the operating temperature of the battery, relatively low electrical resistance exists between the two materials because they are in intimate contact with one another.

CALANDRIA TYPE SODIUM GRAPHITE REACTOR

DOEpatents

Peterson, R.M.; Mahlmeister, J.E.; Vaughn, N.E.; Sanders, W.J.; Williams, A.C.

1964-02-11

A sodium graphite power reactor in which the unclad graphite moderator and fuel elements are contained within a core tank is described. The core tank is submersed in sodium within the reactor vessel. Extending longitudinally through the core thnk are process tubes with fuel elements positioned therein. A bellows sealing means allows axial expansion and construction of the tubes. Within the core tank, a leakage plenum is located below the graphite, and above the graphite is a gas space. A vent line regulates the gas pressure in the space, and another line removes sodium from the plenum. The sodium coolant flows from the lower reactor vessel through the annular space between the fuel elements and process tubes and out into the reactor vessel space above the core tank. From there, the heated coolant is drawn off through an outlet line and sent to the heat exchange. (AEC)

Collapsable seal member

DOEpatents

Sherrell, Dennis L.

1990-01-01

A hollow, collapsable seal member normally disposed in a natural expanded state offering fail-safe pressure sealing against a seating surface and adapted to be evacuated by a vacuum force for collapsing the seal member to disengage the same from said seating surface.

Collapsable seal member

DOEpatents

Sherrell, D.L.

1983-12-08

A hollow, collapsable seal member normally disposed in a natural expanded state offering fail-safe pressure sealing against a seating surface and adapted to be evacuated by a vacuum force for collapsing the seal member to disengage the same from said seating surface.

Thermal charging study of compressed expanded natural graphite/phase change material composites

DOE PAGES

Mallow, Anne; Abdelaziz, Omar; Graham, Jr., Samuel

2016-08-12

The thermal charging performance of paraffin wax combined with compressed expanded natural graphite foam was studied for different graphite bulk densities. Constant heat fluxes between 0.39 W/cm 2 and 1.55 W/cm 2 were applied, as well as a constant boundary temperature of 60 °C. Thermal charging experiments indicate that, in the design of thermal batteries, thermal conductivity of the composite alone is an insufficient metric to determine the influence of the graphite foam on the thermal energy storage. By dividing the latent heat of the composite by the time to end of melt for each applied boundary condition, the energymore » storage performance was calculated to show the effects of composite thermal conductivity, graphite bulk density, and latent heat capacity. For the experimental volume, the addition of graphite beyond a graphite bulk density of 100 kg/m 3 showed limited benefit on the energy storage performance due to the decrease in latent heat storage capacity. These experimental results are used to validate a numerical model to predict the time to melt and for future use in the design of heat exchangers with graphite-foam based phase change material composites. As a result, size scale effects are explored parametrically with the validated model.« less

Method of making a sodium sulfur battery

DOEpatents

Elkins, P. E.

1981-09-22

A method of making a portion of a sodium sulfur battery is disclosed. The battery portion made is a portion of the container which defines the volume for the cathodic reactant materials which are sulfur and sodium polysulfide materials. The container portion is defined by an outer metal casing with a graphite liner contained therein, the graphite liner having a coating on its internal diameter for sealing off the porosity thereof. The steel outer container and graphite pipe are united by a method which insures that at the operating temperature of the battery, relatively low electrical resistance exists between the two materials because they are in intimate contact with one another. 3 figs.

Expanding hollow metal rings

DOEpatents

Peacock, Harold B [Evans, GA; Imrich, Kenneth J [Grovetown, GA

2009-03-17

A sealing device that may expand more planar dimensions due to internal thermal expansion of a filler material. The sealing material is of a composition such that when desired environment temperatures and internal actuating pressures are reached, the sealing materials undergoes a permanent deformation. For metallic compounds, this permanent deformation occurs when the material enters the plastic deformation phase. Polymers, and other materials, may be using a sealing mechanism depending on the temperatures and corrosivity of the use. Internal pressures are generated by either rapid thermal expansion or material phase change and may include either liquid or solid to gas phase change, or in the gaseous state with significant pressure generation in accordance with the gas laws. Sealing material thickness and material composition may be used to selectively control geometric expansion of the seal such that expansion is limited to a specific facing and or geometric plane.

Collar nut and thrust ring

DOEpatents

Lowery, Guy B.

1991-01-01

A collar nut comprises a hollow cylinder having fine interior threads at one end for threadably engaging a pump mechanical seal assembly and an inwardly depending flange at the other end. The flange has an enlarged portion with a groove for receiving an O-ring for sealing against the intrusion of pumpage from the exterior. The enlarged portion engages a thrust ring about the pump shaft for crushing a hard O-ring, such as a graphite O-ring. The hard O-ring seals the interior of the mechanical seal assembly and pump housing against the loss of lubricants or leakage of pumpage. The fine threads of the hollow cylinder provide the mechanical advantage for crushing the hard O-ring evenly and easily with a hand tool from the side of the collar nut rather than by tightening a plurality of bolts from the end and streamlines the exterior surface of the mechanical seal. The collar nut avoids the spatial requirements of bolt heads at the end of a seal and associated bolt head turbulence.

Non-activated high surface area expanded graphite oxide for supercapacitors

NASA Astrophysics Data System (ADS)

Vermisoglou, E. C.; Giannakopoulou, T.; Romanos, G. E.; Boukos, N.; Giannouri, M.; Lei, C.; Lekakou, C.; Trapalis, C.

2015-12-01

Microwave irradiation of graphite oxide constitutes a facile route toward production of reduced graphene oxide, since during this treatment both exfoliation and reduction of graphite oxide occurs. In this work, the effect of pristine graphite (type, size of flakes), pretreatment and oxidation cycles on the finally produced expanded material was examined. All the types of graphite that were tested afforded materials with high BET surface areas ranging from 940 m2/g to 2490 m2/g, without intervening an activation stage at elevated temperature. SEM and TEM images displayed exfoliated structures, where the flakes were significantly detached and curved. The quality of the reduced graphene oxide sheets was evidenced both by X-ray photoelectron spectroscopy and Raman spectroscopy. The electrode material capacitance was determined via electrochemical impedance spectroscopy and cyclic voltammetry. The materials with PEDOT binder had better performance (∼97 F/g) at low operation rates while those with PVDF binder performed better (∼20 F/g) at higher rates, opening up perspectives for their application in supercapacitors.

Corrosion-Resistant Ball Bearings

NASA Technical Reports Server (NTRS)

Zdankiewicz, E. M.; Linaburg, E. L.; Lytle, L. J.

1990-01-01

Self-lubricating bearing system withstands highly corrosive environment of wastewater-recycling unit. New bearings contain cobalt-based-alloy balls and races, graphite/polyimide polymer ball cages, and single integral polytetrafluoroethylene seals on wet sides. Materials and design prevent corrosion by acids and provide lubrication.

EXPERIMENTAL LIQUID METAL FUEL REACTOR

DOEpatents

Happell, J.J.; Thomas, G.R.; Denise, R.P.; Bunts, J.L. Jr.

1962-01-23

A liquid metal fuel nuclear fission reactor is designed in which the fissionable material is dissolved or suspended in a liquid metal moderator and coolant. The liquid suspension flows into a chamber in which a critical amount of fissionable material is obtained. The fluid leaves the chamber and the heat of fission is extracted for power or other utilization. The improvement is in the support arrangement for a segrnented graphite core to permit dif ferential thermal expansion, effective sealing between main and blanket liquid metal flows, and avoidance of excessive stress development in the graphite segments. (AEC)

JACKETED FUEL ELEMENTS FOR GRAPHITE MODERATED REACTORS

DOEpatents

Szilard, L.; Wigner, E.P.; Creutz, E.C.

1959-05-12

Fuel elements for a heterogeneous, fluid cooled, graphite moderated reactor are described. The fuel elements are comprised of a body of natural uranium hermetically sealed in a jacket of corrosion resistant material. The jacket, which may be aluminum or some other material which is non-fissionable and of a type having a low neutron capture cross-section, acts as a barrier between the fissioning isotope and the coolant or moderator or both. The jacket minimizes the tendency of the moderator and coolant to become radioactive and/or contaminated by fission fragments from the fissioning isotope.

Graphite Sheet Coating for Improved Thermal Oxidative Stability of Carbon Fiber Reinforced/PMR-15 Composites

NASA Technical Reports Server (NTRS)

Campbell, Sandi; Papadopoulos, Demetrios; Heimann, Paula; Inghram, Linda; McCorkle, Linda

2005-01-01

Expanded graphite was compressed into graphite sheets and used as a coating for carbon fiber reinforced PMR-15 composites. BET analysis of the graphite indicated an increase in graphite pore size on compression, however the material was proven to be an effective barrier to oxygen when prepegged with PMR-15 resin. Oxygen permeability of the PMR-15/graphite was an order of magnitude lower than the compressed graphite sheet. By providing a barrier to oxygen permeation, the rate of oxidative degradation of PMR-15 was decreased. As a result, the composite thermo-oxidative stability increased by up to 25%. The addition of a graphite sheet as a top ply on the composites yielded little change in the material's flexural strength or interlaminar shear strength.

Friction and wear of several compressor gas-path seal movements

NASA Technical Reports Server (NTRS)

Bill, R. C.; Wisander, D. W.

1978-01-01

Rub interaction experiments were conducted on a series of sintered and plasma sprayed compressor gas path seal materials in contact with Ti-6Al-4V blade tip and knife edge rotors. The most rub tolerant materials investigated were sintered Nichrome and plasma sprayed nickel 25 percent graphite. The effectiveness of providing a compliant substrate for dense seal material coatings was also demonstrated. In general, it was observed that rotor wear and high frictional energy generation rates accompanied smearing or surface densification of the materials investigated. The onset of smearing was sensitive to rub interaction parameters and seal geometry. Two complementary models were proposed to account for the smearing trends. One is based on thermal effects, the other on particulate escape effects. They were shown to be consistent with the experimental evidence at hand, and together they predict that smearing, with the onset of high energy rub conditions, is favored when incursion rates (radial motion) are low, incursion depths are high, the seal geometry is of a knife-edge character, and the seal particle size is small.

Laser induced periodic surface structures formation by nanosecond laser irradiation of poly (ethylene terephthalate) reinforced with Expanded Graphite

NASA Astrophysics Data System (ADS)

Rodríguez-Beltrán, René I.; Hernandez, Margarita; Paszkiewicz, Sandra; Szymczyk, Anna; Rosłaniec, Zbigniew; Ezquerra, Tiberio A.; Castillejo, Marta; Moreno, Pablo; Rebollar, Esther

2018-04-01

We report on the formation of Laser Induced Periodic Surface Structures in poly (ethylene terephthalate) and poly (ethylene terephthalate)/Expanded Graphite films by laser irradiation with nanosecond pulses at 266 nm. The characterization studies show that the quality of the ripples depends strongly on the irradiation time and fluence and the optimal conditions for obtaining LIPSS are affected by the amount of the expanded graphite present in the film due to the differences in crystallinity, thermal conductivity and thermal diffusivity of the nanocomposites. Physicochemical modifications in the materials were inspected by Raman spectroscopy, the colloidal probe technique and contact angle measurements using different liquids. Results show that there is an increase of the hydrophilicity of the surfaces after laser irradiation together with an increase of the surface free energy and in particular of its polar component. Additionally, the adhesion force estimated by the colloidal probe technique increases after laser nanostructuring.

Sample Containerization and Sealing Techniques for Contamination Prevention and Preservation of Science Value for Mars Sample Return

NASA Astrophysics Data System (ADS)

Younse, Paulo

Four sealing methods for encapsulating samples in 1 cm diameter thin-walled sample tubes were designed, along with a set of tests for characterization and evaluation of contamination prevention and sample preservation capability for the proposed Mars Sample Return (MSR) campaign. The sealing methods include a finned shape memory alloy (SMA) plug, expanding torque plug, contracting SMA ring cap, and expanding SMA ring plug. Mechanical strength and hermeticity of the seal were measured using a helium leak detector. Robustness of the seal to Mars simulant dust, surface abrasion, and pressure differentials were tested. Survivability tests were run to simulate thermal cycles on Mars, vibration from a Mars Ascent Vehicle (MAV), and shock from Earth Entry Vehicle (EEV) landing. Material compatibility with potential sample minerals and organic molecules were studied to select proper tube and seal materials that would not lead to adverse reactions nor contaminate the sample. Cleaning and sterilization techniques were executed on coupons made from the seal materials to assess compliance with planetary protection and contamination control. Finally, a method to cut a sealed tube for sample removal was designed and tested.

Expanded graphite embedded with aluminum nanoparticles as superior thermal conductivity anodes for high-performance lithium-ion batteries

PubMed Central

Zhao, Tingkai; She, Shengfei; Ji, Xianglin; Guo, Xinai; Jin, Wenbo; Zhu, Ruoxing; Dang, Alei; Li, Hao; Li, Tiehu; Wei, Bingqing

2016-01-01

The development of high capacity and long-life lithium-ion batteries is a long-term pursuing and under a close scrutiny. Most of the researches have been focused on exploring electrode materials and structures with high store capability of lithium ions and at the same time with a good electrical conductivity. Thermal conductivity of an electrode material will also have significant impacts on boosting battery capacity and prolonging battery lifetime, which is, however, underestimated. Here, we present the development of an expanded graphite embedded with Al metal nanoparticles (EG-MNPs-Al) synthesized by an oxidation-expansion process. The synthesized EG-MNPs-Al material exhibited a typical hierarchical structure with embedded Al metal nanoparticles into the interspaces of expanded graphite. The parallel thermal conductivity was up to 11.6 W·m−1·K−1 with a bulk density of 453 kg·m−3 at room temperature, a 150% improvement compared to expanded graphite (4.6 W·m−1·K−1) owing to the existence of Al metal nanoparticles. The first reversible capacity of EG-MNPs-Al as anode material for lithium ion battery was 480 mAh·g−1 at a current density of 100 mA·g−1, and retained 84% capacity after 300 cycles. The improved cycling stability and system security of lithium ion batteries is attributed to the excellent thermal conductivity of the EG-MNPs-Al anodes. PMID:27671848

Expanded graphite embedded with aluminum nanoparticles as superior thermal conductivity anodes for high-performance lithium-ion batteries.

PubMed

Zhao, Tingkai; She, Shengfei; Ji, Xianglin; Guo, Xinai; Jin, Wenbo; Zhu, Ruoxing; Dang, Alei; Li, Hao; Li, Tiehu; Wei, Bingqing

2016-09-27

The development of high capacity and long-life lithium-ion batteries is a long-term pursuing and under a close scrutiny. Most of the researches have been focused on exploring electrode materials and structures with high store capability of lithium ions and at the same time with a good electrical conductivity. Thermal conductivity of an electrode material will also have significant impacts on boosting battery capacity and prolonging battery lifetime, which is, however, underestimated. Here, we present the development of an expanded graphite embedded with Al metal nanoparticles (EG-MNPs-Al) synthesized by an oxidation-expansion process. The synthesized EG-MNPs-Al material exhibited a typical hierarchical structure with embedded Al metal nanoparticles into the interspaces of expanded graphite. The parallel thermal conductivity was up to 11.6 W·m -1 ·K -1 with a bulk density of 453 kg·m -3 at room temperature, a 150% improvement compared to expanded graphite (4.6 W·m -1 ·K -1 ) owing to the existence of Al metal nanoparticles. The first reversible capacity of EG-MNPs-Al as anode material for lithium ion battery was 480 mAh·g -1 at a current density of 100 mA·g -1 , and retained 84% capacity after 300 cycles. The improved cycling stability and system security of lithium ion batteries is attributed to the excellent thermal conductivity of the EG-MNPs-Al anodes.

Two-stage preparation of magnetic sorbent based on exfoliated graphite with ferrite phases for sorption of oil and liquid hydrocarbons from the water surface

NASA Astrophysics Data System (ADS)

Pavlova, Julia A.; Ivanov, Andrei V.; Maksimova, Natalia V.; Pokholok, Konstantin V.; Vasiliev, Alexander V.; Malakho, Artem P.; Avdeev, Victor V.

2018-05-01

Due to the macropore structure and the hydrophobic properties, exfoliated graphite (EG) is considered as a perspective sorbent for oil and liquid hydrocarbons from the water surface. However, there is the problem of EG collection from the water surface. One of the solutions is the modification of EG by a magnetic compound and the collection of EG with sorbed oil using the magnetic field. In this work, the method of the two-stage preparation of exfoliated graphite with ferrite phases is proposed. This method includes the impregnation of expandable graphite in the mixed solution of iron (III) chloride and cobalt (II) or nickel (II) nitrate in the first stage and the thermal exfoliation of impregnated expandable graphite with the formation of exfoliated graphite containing cobalt and nickel ferrites in the second stage. Such two-stage method makes it possible to obtain the sorbent based on EG modified by ferrimagnetic phases with high sorption capacity toward oil (up to 45-51 g/g) and high saturation magnetization (up to 42 emu/g). On the other hand, this method allows to produce the magnetic sorbent in a short period of time (up to 10 s) during which the thermal exfoliation is carried out in the air atmosphere.

A Highly Efficient and Facile Approach for Fabricating Graphite Nanoplatelets

NASA Astrophysics Data System (ADS)

Van Thanh, Dang; Van Thien, Nguyen; Thang, Bui Hung; Van Chuc, Nguyen; Hong, Nguyen Manh; Trang, Bui Thi; Lam, Tran Dai; Huyen, Dang Thi Thu; Hong, Phan Ngoc; Minh, Phan Ngoc

2016-05-01

In this study, we report a highly efficient, convenient, and cost-effective technique for producing graphite nanoplatelets (GNPs) from plasma-expanded graphite oxides (PEGOs) obtained directly from low-cost, recycled graphite electrodes of used batteries, x-ray diffraction, Raman spectroscopy, and x-ray photoelectron spectroscopy confirmed the successful preparation of GNPs. Scanning electron microscopy revealed that the GNPs have lateral width from several hundreds of nanometers to 1.5 μm with an approximate thickness of 20-50 nm. These GNPs can serve as a precursor for the preparation of GNPs-based nanocomposite.

Production of graphene quantum dots by ultrasound-assisted exfoliation in supercritical CO2/H2O medium.

PubMed

Gao, Hanyang; Xue, Chen; Hu, Guoxin; Zhu, Kunxu

2017-07-01

In this research, three kinds of graphene quantum dots (GQDs)-pristine graphene quantum dots (PGQDs), expanded graphene quantum dots (EGQDs) and graphene oxide quantum dots (GOQDs)-were produced from natural graphite, expanded graphite, and oxide graphite respectively in an ultrasound-assisted supercritical CO 2 (scCO 2 )/H 2 O system. The effects of aqueous solution content ratio, system pressure, and ultrasonic power on the yields of different kinds of GQDs were investigated. According to these experiment results, the combination of the intense knocking force generated from high-pressure acoustic cavitation in a scCO 2 /H 2 O system and the superior penetration ability of scCO 2 was considered to be the key to the successful exfoliation of such tiny pieces from bulk graphite. An interesting result was found that, contrary to common experience, the yield of PGQDs from natural graphite was much higher than that of GOQDs from graphite oxide. Based on the experimental analysis, the larger interlayer resistance of natural graphite, which hindered the insertion of scCO 2 molecules, and the hydrophobic property of natural graphite surface, which made the planar more susceptible to the attack of ultrasonic collapsing bubbles, were deduced to be the two main reasons for this result. The differences in characteristics among the three kinds of GQDs were also studied and compared in this research. In our opinion, this low-cost and time-saving method may provide an alternative green route for the production of various kinds of GQDs, especially PGQDs. Copyright © 2017 Elsevier B.V. All rights reserved.

Inert gas rejection device for zinc-halogen battery systems

DOEpatents

Hammond, Michael J.; Arendell, Mark W.

1981-01-01

An electrolytic cell for separating chlorine gas from other (foreign) gases, having an anode, a cathode assembly, an aqueous electrolyte, a housing, and a constant voltage power supply. The cathode assembly is generally comprised of a dense graphite electrode having a winding channel formed in the face opposing the anode, a gas impermeable (but liquid permeable) membrane sealed into the side of the cathode electrode over the channel, and a packing of graphite particles contained in the channel of the cathode electrode. The housing separates and parallelly aligns the anode and cathode assembly, and provides a hermetic seal for the cell. In operation, a stream of chlorine and foreign gases enters the cell at the beginning of the cathode electrode channel. The chlorine gas is dissolved into the electrolyte and electrochemically reduced into chloride ions. The chloride ions disfuse through the gas impermeable membrane, and are electrochemically oxidized at the anode into purified chlorine gas. The foreign gases do not participate in the above electrochemical reactions, and are vented from the cell at the end of the cathode electrode channel.

Low-temperature method of producing nano-scaled graphene platelets and their nanocomposites

DOEpatents

Zhamu, Aruna [Centerville, OH; Shi, Jinjun [Columbus, OH; Guo, Jiusheng [Centerville, OH; Jang, Bor Z [Centerville, OH

2012-03-13

A method of exfoliating a layered material to produce separated nano-scaled platelets having a thickness smaller than 100 nm. The method comprises: (a) providing a graphite intercalation compound comprising a layered graphite containing expandable species residing in an interlayer space of the layered graphite; (b) exposing the graphite intercalation compound to an exfoliation temperature lower than 650.degree. C. for a duration of time sufficient to at least partially exfoliate the layered graphite without incurring a significant level of oxidation; and (c) subjecting the at least partially exfoliated graphite to a mechanical shearing treatment to produce separated platelets. The method can further include a step of dispersing the platelets in a polymer or monomer solution or suspension as a precursor step to nanocomposite fabrication.

An experimental investigation of rubbing interaction in labyrinth seals at cryogenic temperature

NASA Technical Reports Server (NTRS)

Dolan, F. X.; Kennedy, F. E.; Schulson, E. M.

1985-01-01

An experimental program was carried out to address issues related to the observed cracking of the titanium knife edges on the labyrinth seals of the high pressure fuel pump (HPFP) in the Space Shuttle main engine (SSME). Thermal shock experiments were carried out using a jet specimen with geometry similar to the knife edge geometry. These tests demonstrate that cracking of the titanium alloy is possible in a situation involving repeated thermal cycles over a wide temperature range, as might be realized during a rub in the liquid hydrogen fuel pump. High speed rub interaction tests were conducted using a representative knife edge and seal geometry over a broad range of interaction rates. Alternative materials were also experimentally evaluated. These tests provide information which can be used to design improved labyrinth seals for the HPFP of the SSME. In particular, plasma-sprayed aluminum-graphite was found to be significantly better than aluminum alloy seals used at present from the standpoint of rub performance. Ion nitriding of the titanium alloy knife edges was also found to improve rub performance compared with the untreated baseline knife edge material.

O-Ring sealing arrangements for ultra-high vacuum systems

DOEpatents

Kim, Chang-Kyo; Flaherty, Robert

1981-01-01

An all metal reusable O-ring sealing arrangement for sealing two concentric tubes in an ultra-high vacuum system. An O-ring of a heat recoverable alloy such as Nitinol is concentrically positioned between protruding sealing rings of the concentric tubes. The O-ring is installed between the tubes while in a stressed martensitic state and is made to undergo a thermally induced transformation to an austenitic state. During the transformation the O-ring expands outwardly and contracts inwardly toward a previously sized austenitic configuration, thereby sealing against the protruding sealing rings of the concentric tubes.

Powder, paper and foam of few-layer graphene prepared in high yield by electrochemical intercalation exfoliation of expanded graphite.

PubMed

Wu, Liqiong; Li, Weiwei; Li, Peng; Liao, Shutian; Qiu, Shengqiang; Chen, Mingliang; Guo, Yufen; Li, Qi; Zhu, Chao; Liu, Liwei

2014-04-09

A facile and high-yield approach to the preparation of few-layer graphene (FLG) by electrochemical intercalation exfoliation (EIE) of expanded graphite in sulfuric acid electrolyte is reported. Stage-1 H2SO4-graphite intercalation compound is used as a key intermediate in EIE to realize the efficient exfoliation. The yield of the FLG sheets (<7 layers) with large lateral sizes (tens of microns) is more than 75% relative to the total amount of starting expanded graphite. A low degree of oxygen functionalization existing in the prepared FLG flakes enables them to disperse effectively, which contributes to the film-forming characteristics of the FLG flakes. These electrochemically exfoliated FLG flakes are integrated into several kinds of macroscopic graphene structures. Flexible and freestanding graphene papers made of the FLG flakes retain excellent conductivity (≈24,500 S m(-1)). Three-dimensional (3D) graphene foams with light weight are fabricated from the FLG flakes by the use of Ni foams as self-sacrifice templates. Furthermore, 3D graphene/Ni foams without any binders, which are used as supercapacitor electrodes in aqueous electrolyte, provide the specific capacitance of 113.2 F g(-1) at a current density of 0.5 A g(-1), retaining 90% capacitance after 1000 cycles. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Dispersion of iron nano-particles on expanded graphite for the shielding of electromagnetic radiation

NASA Astrophysics Data System (ADS)

Xu, Zheng; Huang, Yu'an; Yang, Yang; Shen, Jianyi; Tang, Tao; Huang, Runsheng

2010-10-01

Composite materials containing electrically conductive expanded graphite (EG) and magnetic iron nano-particles for electromagnetic shielding were prepared by impregnating EG with an ethanol solution containing iron nitrate and acetic acid, followed by drying and reduction in H 2. Magnetic nano-iron particles were found to be highly dispersed on the surface of EG in the Fe/EG composites, and played the role of enhancing the electromagnetic shielding effectiveness (SE) at low frequencies (0.3-10 MHz), which seemed to depend proportionally on magnetic hysteresis loss of loaded iron nano-particles.

Emergency sacrificial sealing method in filters, equipment, or systems

DOEpatents

Brown, Erik P

2014-09-30

A system seals a filter or equipment component to a base and will continue to seal the filter or equipment component to the base in the event of hot air or fire. The system includes a first sealing material between the filter or equipment component and the base; and a second sealing material between the filter or equipment component and the base and proximate the first sealing material. The first sealing material and the second seal material are positioned relative to each other and relative to the filter or equipment component and the base to seal the filter or equipment component to the base and upon the event of fire the second sealing material will be activated and expand to continue to seal the filter or equipment component to the base in the event of hot air or fire.

Method of forming shrink-fit compression seal

NASA Technical Reports Server (NTRS)

Podgorski, T. J. (Inventor)

1977-01-01

A method for making a glass-to-metal seal is described. A domed metal enclosure having a machined seal ring is fitted to a glass post machined to a slight taper and to a desired surface finish. The metal part is then heated by induction in a vacuum. As the metal part heats and expands relative to the glass post, the metal seal ring, possessing a higher coefficient of expansion than the glass post, slides down the tapered post. Upon cooling, the seal ring crushes against the glass post forming the seal. The method results in a glass-to-metal seal possessing extremely good leak resistance, while the parts are kept clean and free of the contaminants.

Preliminary Results of IS Plasma Focus as a Breeder of Short-Lived Radioisotopes 12C(d,n)13N

NASA Astrophysics Data System (ADS)

Sadat Kiai, S. M.; Elahi, M.; Adlparvar, S.; Shahhoseini, E.; Sheibani, S.; Ranjber akivaj, H.; Alhooie, S.; Safarien, A.; Farhangi, S.; Aghaei, N.; Amini, S.; Khalaj, M. M.; Zirak, A. R.; Dabirzadeh, A. A.; Soleimani, J.; Torkzadeh, F.; Mousazadeh, M. M.; Moradi, K.; Abdollahzadeh, M.; Talaei, A.; Zaeem, A. A.; Moslehi, A.; Kashani, A.; Babazadeh, A. R.; Bagiyan, F.; Ardestani, M.; Roozbahani, A.; Pourbeigi, H.; Tajik Ahmadi, H.; Ahmadifaghih, M. A.; Mahlooji, M. S.; Mortazavi, B. N.; Zahedi, F.

2011-04-01

Modified IS (Iranian Sun) plasma focus (10 kJ,15 kV, 94 μF, 0.1 Hz) has been used to produce the short-lived radioisotope 13N (half-life of 9.97 min) through 12C(d,n)13N nuclear reaction. The filling gas was 1.5-3 torr of hydrogen (60%) deuterium (40%) mixture. The target was solid nuclear grade graphite with 5 mm thick, 9 cm width and 13 in length. The activations of the exogenous target on average of 20 shots (only one-third acceptable) through 10-13 kV produced the 511 keV gamma rays. Another peak found at the 570 keV gamma of which both was measured by a NaI portable gamma spectrometer calibrated by a 137Cs 0.25 μCi sealed reference source with its single line at 661.65 keV and 22Na 0.1 μCi at 511 keV. To measure the gamma rays, the graphite target converts to three different phases; solid graphite, powder graphite, and powder graphite in water solution. The later phase approximately has a doubled activity with respect to the solid graphite target up to 0.5 μCi of 511 keV and 1.1 μCi of 570 keV gamma lines were produced. This increment in activity was perhaps due to structural transformation of graphite powder to nano-particles characteristic in liquid water.

Emergency sacrificial sealing method in filters, equipment, or systems

DOE Office of Scientific and Technical Information (OSTI.GOV)

Brown, Erik P.

A system seals a filter or equipment component to abase and will continue to seal the filter or equipment component to the base in the event of hot air or fire. The system includes a first sealing material between the filter or equipment component and the base; and a second sealing material between the filter or equipment component and the base and proximate the first sealing material. The first sealing material and the second seal material are positioned relative to each other and relative to the filter or equipment component and the base to seal the filter or equipment componentmore » to the base and upon the event of fire the second sealing material will be activated and expand to continue to seal the filter or equipment component to the base in the event of hot air or fire.« less

Bellow seal and anchor

DOEpatents

Mansure, Arthur J.

2001-01-01

An annular seal is made of a collapsible bellows. The bellows can function as an anchor or a seal and is easily set into position using relative component movement. The bellows folds can be slanted and their outer sealing edges can have different profiles to meet expected conditions. The bellows is expanded for insertion to reduce its outer dimension and sets by compaction as a result of relative movement. The bellows can be straight or tapered and is settable with a minimal axial force.

Implementation of transverse variable asphalt rate seal coat practices in Texas.

DOT National Transportation Integrated Search

2011-01-01

An implementation project was performed to expand use of transversely varied asphalt rate (TVAR) seal : coat practices in all districts. The project included nine regional workshops, continued field texture testing of : test sites, provided one set o...

Leaf seal for inner and outer casings of a turbine

DOEpatents

Schroder, Mark Stewart; Leach, David

2002-01-01

A plurality of arcuate, circumferentially extending leaf seal segments form an annular seal spanning between annular sealing surfaces of inner and outer casings of a turbine. The ends of the adjoining seal segments have circumferential gaps to enable circumferential expansion and contraction of the segments. The end of a first segment includes a tab projecting into a recess of a second end of a second segment. Edges of the tab seal against the sealing surfaces of the inner and outer casings have a narrow clearance with opposed edges of the recess. An overlying cover plate spans the joint. Leakage flow is maintained at a minimum because of the reduced gap between the radially spaced edges of the tab and recess, while the seal segments retain the capacity to expand and contract circumferentially.

Ferric chloride-graphite intercalation compounds as anode materials for Li-ion batteries.

PubMed

Wang, Lili; Zhu, Yongchun; Guo, Cong; Zhu, Xiaobo; Liang, Jianwen; Qian, Yitai

2014-01-01

Ferric chloride-graphite intercalation compounds (FeCl3 -GICs) with stage 1 and stage 2 structures were synthesized by reacting FeCl3 and expanded graphite (EG) in air in a stainless-steel autoclave. As rechargeable Li-ion batteries, these FeCl3 -GICs exhibit high capacity, excellent cycling stability, and superior rate capability, which could be attributed to their unique intercalation features. This work may enable new possibilities for the fabrication of Li-ion batteries. Copyright © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Lightweight bladder lined pressure vessels

DOEpatents

Mitlitsky, F.; Myers, B.; Magnotta, F.

1998-08-25

A lightweight, low permeability liner is described for graphite epoxy composite compressed gas storage vessels. The liner is composed of polymers that may or may not be coated with a thin layer of a low permeability material, such as silver, gold, or aluminum, deposited on a thin polymeric layer or substrate which is formed into a closed bladder using tori spherical or near tori spherical end caps, with or without bosses therein, about which a high strength to weight material, such as graphite epoxy composite shell, is formed to withstand the storage pressure forces. The polymeric substrate may be laminated on one or both sides with additional layers of polymeric film. The liner may be formed to a desired configuration using a dissolvable mandrel or by inflation techniques and the edges of the film sealed by heat sealing. The liner may be utilized in most any type of gas storage system, and is particularly applicable for hydrogen, gas mixtures, and oxygen used for vehicles, fuel cells or regenerative fuel cell applications, high altitude solar powered aircraft, hybrid energy storage/propulsion systems, and lunar/Mars space applications, and other applications requiring high cycle life. 19 figs.

Seal Apparatus and Methods to Manufacture Thereof

NASA Technical Reports Server (NTRS)

Richard, James A. (Inventor)

2013-01-01

In some implementations, apparatus and methods are provided through which a dynamic cryogenic seal is manufactured. In some implementations, the seal includes a retainer and a spring-seal assembly, the assembly being comprised of a main spring housing and fluorine-containing polymer seals. In some implementations, either a radial seal, or an axial (or "piston seal") is provided. In some implementations, methods of manufacturing the dynamic cryogenic seal are also provided. In some implementations, the methods include assembling the components while either heated or cooled, taking advantage of thermal expansion and contraction, such that there is a strong interference fit between the components at room temperature. In some implementations, this process ensures that the weaker fluorine-containing polymer seal is forced to expand and contract with the stronger retainer and spring and is under constant preload. In some implementations, the fluorine-containing polymer is therefore fluidized and retained, and can not lift off.

Analytical and experimental investigation of rubbing interaction in labyrinth seals for a liquid hydrogen fuel pump. [space shuttle main engine

NASA Technical Reports Server (NTRS)

Dolan, F. X.; Kennedy, F. E.; Schulson, E. M.

1984-01-01

Cracking of the titanium knife edges on the labyrinth seals of the liquid hydrogen fuel pump in the Space Shuttle main engine is considered. Finite element analysis of the thermal response of the knife edge in sliding contact with the wear ring surface shows that interfacial temperatures can be quite high and they are significantly influenced by the thermal conductivity of the surfaces in rubbing contact. Thermal shock experiments on a test specimen similar to the knife edge geometry demonstrate that cracking of the titanium alloy is possible in a situation involving repeated thermal cycles over a wide temperature range, as might be realized during a rub in the liquid hydrogen fuel pump. High-speed rub interaction tests were conducted using a representative knife edge and seal geometry over a broad range of interaction rates and alternate materials were experimentally evaluated. Plasma-sprayed aluminum-graphite was found to be significantly better than presently used aluminum alloy seals from the standpoint of rub performance. Ion nitriding the titanium alloy knife-edges also improved rub performance compared to the untreated baseline.

Large scale production of highly-qualified graphene by ultrasonic exfoliation of expanded graphite under the promotion of (NH4)2CO3 decomposition.

PubMed

Wang, Yunwei; Tong, Xili; Guo, Xiaoning; Wang, Yingyong; Jin, Guoqiang; Guo, Xiangyun

2013-11-29

Highly-qualified graphene was prepared by the ultrasonic exfoliation of commercial expanded graphite (EG) under the promotion of (NH4)2CO3 decomposition. The yield of graphene from the first exfoliation is 7 wt%, and it can be increased to more than 65 wt% by repeated exfoliations. Atomic force microscopy, x-ray photoelectron spectroscopy and Raman analysis show that the as-prepared graphene only has a few defects or oxides, and more than 95% of the graphene flakes have a thickness of ~1 nm. The electrochemical performance of the as-prepared graphene is comparable to reduced graphene oxide in the determination of dopamine (DA) from the mixed solution of ascorbic acid, uric acid and DA. These results show that the decomposition of (NH4)2CO3 molecules in the EG layers under ultrasonication promotes the exfoliation of graphite and provides a low-priced route for large scale production of highly-quality graphene.

Large scale production of highly-qualified graphene by ultrasonic exfoliation of expanded graphite under the promotion of (NH4)2CO3 decomposition

NASA Astrophysics Data System (ADS)

Wang, Yunwei; Tong, Xili; Guo, Xiaoning; Wang, Yingyong; Jin, Guoqiang; Guo, Xiangyun

2013-11-01

Highly-qualified graphene was prepared by the ultrasonic exfoliation of commercial expanded graphite (EG) under the promotion of (NH4)2CO3 decomposition. The yield of graphene from the first exfoliation is 7 wt%, and it can be increased to more than 65 wt% by repeated exfoliations. Atomic force microscopy, x-ray photoelectron spectroscopy and Raman analysis show that the as-prepared graphene only has a few defects or oxides, and more than 95% of the graphene flakes have a thickness of ˜1 nm. The electrochemical performance of the as-prepared graphene is comparable to reduced graphene oxide in the determination of dopamine (DA) from the mixed solution of ascorbic acid, uric acid and DA. These results show that the decomposition of (NH4)2CO3 molecules in the EG layers under ultrasonication promotes the exfoliation of graphite and provides a low-priced route for large scale production of highly-quality graphene.

The effect of 150μm expandable graphite on char expansion of intumescent fire retardant coating

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ullah, Sami, E-mail: samichemist1@gmail.com; Shariff, A. M., E-mail: azmish@petronas.com.my, E-mail: azmibustam@petronas.com.my; Bustam, M. A., E-mail: azmish@petronas.com.my, E-mail: azmibustam@petronas.com.my

2014-10-24

Intumescent is defined as the swelling of certain substances to insulate the underlying substrate when they are heated. In this research work the effect of 150μm expandable graphite (EG) was studied on char expansion, char morphology and char composition of intumescent coating formulations (ICFs). To study the expansion and thermal properties of the coating, nine different formulations were prepared. The coatings were tested at 500 °C for one hour and physically were found very stable and well bound with the steel substrate. The morphology was studied by Scanning Electron Microscopy (SEM). The char composition was analysed by X-ray Diffraction (XRD)more » and Fourier transform infrared spectroscopy (FTIR) techniques. EG above than 10.8wt% expands the char abruptly with uniform network structure and affect the outer surface of the char.« less

Solid Lubricants for Space Structures

DTIC Science & Technology

1993-04-17

will utilize mechanically interlocked hardware (caged bearings or bearings for ultra precision gimbals pointing mechanisms) controlled through precision...structure unless the lubricant were of low vapor pressure and/or suitably sealed to I prevent molecular effusion . While temperatures within spacecraft or...incorporation in the continuous cast system. The die made of graphite, consists of a plurality of openings or holes located in the die and positioned (unlined

Feasibility investigation of growing gallium arsenide single crystals in ribbon form

NASA Technical Reports Server (NTRS)

Richardson, D. L.

1975-01-01

Polycrystalline GaAs ribbons have been grown in graphite boats by passage of a wide zone through B2O3 encapsulated feed stock, confined by a quartz cover plate. By controlling the heat flow in the graphite boat and controlling the zoning rate, large grained, single phase polycrystalline samples with directional solidification and good thickness control were achieved. Arsenic vaporization was effectively suppressed at the melting point of GaAs by the B2O3 moat and 3 atmospheres of pressure. A vertical constrained-zone-melting apparatus with a B2O3 moat seal, rf heating, and water cooling on the bottom will be used to control the heat flow and temperature patterns required for growth of single crystal ribbons.

Thulium-170 heat source

DOEpatents

Walter, Carl E.; Van Konynenburg, Richard; VanSant, James H.

1992-01-01

An isotopic heat source is formed using stacks of thin individual layers of a refractory isotopic fuel, preferably thulium oxide, alternating with layers of a low atomic weight diluent, preferably graphite. The graphite serves several functions: to act as a moderator during neutron irradiation, to minimize bremsstrahlung radiation, and to facilitate heat transfer. The fuel stacks are inserted into a heat block, which is encased in a sealed, insulated and shielded structural container. Heat pipes are inserted in the heat block and contain a working fluid. The heat pipe working fluid transfers heat from the heat block to a heat exchanger for power conversion. Single phase gas pressure controls the flow of the working fluid for maximum heat exchange and to provide passive cooling.

Seal assembly

DOEpatents

Johnson, Roger Neal; Longfritz, William David

2001-01-01

A seal assembly that seals a gap formed by a groove comprises a seal body, a biasing element, and a connection that connects the seal body to the biasing element to form the seal assembly. The seal assembly further comprises a concave-shaped center section and convex-shaped contact portions at each end of the seal body. The biasing element is formed from an elastic material and comprises a convex-shaped center section and concave-shaped biasing zones that are opposed to the convex-shaped contact portions. The biasing element is adapted to be compressed to change a width of the seal assembly from a first width to a second width that is smaller than the first width. In the compressed state, the seal assembly can be disposed in the groove. After release of the compressing force, the seal assembly expands. The contact portions will move toward a surface of the groove and the biasing zones will move into contact with another surface of the groove. The biasing zones will bias the contact portions of the seal body against the surface of the groove.

Inflatable containment diaphragm for sealing and removing stacks

DOEpatents

Meskanick, G.R.; Rosso, D.T.

1993-04-13

A diaphragm with an inflatable torus-shaped perimeter is used to seal at least one end of a stack so that debris that might be hazardous will not be released during removal of the stack. A diaphragm is inserted and inflated in the lower portion of a stack just above where the stack is to be cut such that the perimeter of the diaphragm expands and forms a seal against the interior surface of the stack.

Inflatable containment diaphragm for sealing and removing stacks

DOEpatents

Meskanick, Gerald R.; Rosso, David T.

1993-01-01

A diaphragm with an inflatable torus-shaped perimeter is used to seal at least one end of a stack so that debris that might be hazardous will not be released during removal of the stack. A diaphragm is inserted and inflated in the lower portion of a stack just above where the stack is to be cut such that the perimeter of the diaphragm expands and forms a seal against the interior surface of the stack.

In-Situ Leak Testing And Replacement Of Glovebox Isolator, Or Containment Unit Gloves

DOEpatents

Castro, Julio M.; Macdonald, John M.; Steckle, Jr., Warren P.

2004-11-02

A test plug for in-situ testing a glove installed in a glovebox is provided that uses a top plate and a base plate, and a diametrically expandable sealing mechanism fitting between the two plates. The sealing mechanism engages the base plate to diametrically expand when the variable distance between the top plate and the bottom plate is reduced. An inlet valve included on the top plate is used to introducing a pressurized gas to the interior of the glove, and a pressure gauge located on the top plate is used to monitor the interior glove pressure.

Low thermal expansion seal ring support

DOEpatents

Dewis, David W.; Glezer, Boris

2000-01-01

Today, the trend is to increase the temperature of operation of gas turbine engines. To cool the components with compressor discharge air, robs air which could otherwise be used for combustion and creates a less efficient gas turbine engine. The present low thermal expansion sealing ring support system reduces the quantity of cooling air required while maintaining life and longevity of the components. Additionally, the low thermal expansion sealing ring reduces the clearance "C","C'" demanded between the interface between the sealing surface and the tip of the plurality of turbine blades. The sealing ring is supported by a plurality of support members in a manner in which the sealing ring and the plurality of support members independently expand and contract relative to each other and to other gas turbine engine components.

Electrochemical to Mechanical Energy Conversion

DTIC Science & Technology

2010-02-01

advantage of these properties . Metal alloys fit these requirements as many of them dilate in excess of 100% when alloyed with lithium. Aluminum, in...3. Woo KC, Kamitakahara WA, DiVincenzo DP, et al . Effect of In-Plane Density on the Structural and Elastic Properties of Graphite Intercalation...Further, free volume associated with the powder packing of the electrodes or the sealing process will aid in stress relaxation and creep strain. (a) (b) 35

Best Practices for Fuel System Contamination Detection and Remediation

DTIC Science & Technology

2015-12-14

Valve Fyre Ring GR DBB Style Plug Valve Gasket SS graphite Spiral DBB Style Plug Valve O- rings & slip seals VI DBB Style Plug Valve Packing gland...Pumps Impeller Key SS Vertical Turbine Pumps Impeller Retaining Ring SS Vertical Turbine Pumps Impellers (Electroless Nickel Plating) DI Vertical... Turbine Pumps Line Shaft SS Vertical Turbine Pumps Lineshaft Bearing CA Vertical Turbine Pumps Mating Ring Si-C Vertical Turbine Pumps Mechanical

Best Practices for Fuel System Contamination Detection and Remediation

DTIC Science & Technology

2016-01-15

Valve Fyre Ring GR DBB Style Plug Valve Gasket SS graphite Spiral DBB Style Plug Valve O- rings & slip seals VI DBB Style Plug Valve Packing gland...Pumps Impeller Key SS Vertical Turbine Pumps Impeller Retaining Ring SS Vertical Turbine Pumps Impellers (Electroless Nickel Plating) DI Vertical... Turbine Pumps Line Shaft SS Vertical Turbine Pumps Lineshaft Bearing CA Vertical Turbine Pumps Mating Ring Si-C Vertical Turbine Pumps Mechanical

The preparation of polytrifluorochloroethylene (PCTFE) micro-particles and application on treating bearing steel surfaces to improve the lubrication effect for copper-graphite (Cu/C)

NASA Astrophysics Data System (ADS)

Lu, Hailin; Zhang, Pengpeng; Ren, Shanshan; Guo, Junde; Li, Xing; Dong, Guangneng

2018-01-01

Contact mechanical seal is a normal technology applied on middle axis of liquid rocket turbo pump, and the kinetic and static seal rings contact low temperature rocket propellant. Copper-graphite (Cu/C) composite as an excellent self-lubrication material was widely used in aerospace industry, this study took Cu/C as ball and bearing steel as disk to investigate the tribology properties, and distilled water were used to simulate the lox tribology performances. This study prepared polytrifluorochloroethylene (PCTFE) micro-particles which were coated on the oxide surfaces of bearing steel disk at temperature of 150 °C. The tribology results showed that the oxide surfaces treated with micro PCTFE particles have lower fiction coefficient and lower wear rate than original disk in water, and the wear morphology revealed that the treated surfaces obviously had less Cu/C composite transfer film than original disk. Meanwhile SEM, EDS, XRD, XPS and light microscope etc revealed that PCTFE micro-particles could associate with the oxide surfaces and caused higher water contact angle, due to the properties of the fluorine-containing composite may cause the good lubrication effect in water. Thus this technology shows great potential to enhance tribological performances for aerospace industry on a large scale.

Apparatus and method for maintaining an article at a temperature that is less than the temperature of the ambient air

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klett, James; Klett, Lynn

An apparatus for maintaining the temperature of an article at a temperature that is below the ambient air temperature includes an enclosure having an outer wall that defines an interior chamber for holding a volume of sealed air. An insert is disposed inside of the chamber and has a body that is made of a porous graphite foam material. A vacuum pump penetrates the outer wall and fluidly connects the sealed air in the interior chamber with the ambient air outside of the enclosure. The temperatures of the insert and article is maintained at temperatures that are below the ambientmore » air temperature when a volume of a liquid is wicked into the pores of the porous insert and the vacuum pump is activated to reduce the pressure of a volume of sealed air within the interior chamber to a pressure that is below the vapor pressure of the liquid.« less

Non-graphite crucible for high temperature applications

DOEpatents

Holcombe, C.E.; Pfeiler, W.A.

1994-08-02

A multi-piece crucible for high temperature applications comprises a tubular side wall member having a lip on the inside surface and a bottom member or members forming a container for containing a melt of a material during a high temperature melt-casting operations. The multi-piece design prevents cracking of the crucible or leakage of the melt from the crucible during the melt-casting operation. The lip of the tubular member supports the bottom member. The contacting surfaces where the lip of the tubular side wall member contacts the bottom member of the multi-piece crucible contains a ceramic sealing material. The ceramic sealing material forms a seal sufficient to prevent the melt of the material from leaking out of the multi-piece crucible during the melt-casting process. The multi-piece crucible is made of a material which is chemically inert to the melt and has structural integrity at the melting point temperature of the melt, or of a material coated with such a material. 6 figs.

Non-graphite crucible for high temperature applications

DOEpatents

Holcombe, Cressie E.; Pfeiler, William A.

1994-01-01

A multi-piece crucible for high temperature applications comprises a tubular side wall member having a lip on the inside surface and a bottom member or members forming a container for containing a melt of a material during a high temperature melt-casting operations. The multi-piece design prevents cracking of the crucible or leakage of the melt from the crucible during the melt-casting operation. The lip of the tubular member supports the bottom member. The contacting surfaces where the lip of the tubular side wall member contacts the bottom member of the multi-piece crucible contains a ceramic sealing material. The ceramic sealing material forms a seal sufficient to prevent the melt of the material from leaking out of the multi-piece crucible during the melt-casting process. The multi-piece crucible is made of a material which is chemically inert to the melt and has structural integrity at the melting point temperature of the melt, or of a material coated with such a material.

Solid handling valve

DOEpatents

Williams, William R.

1979-01-01

The present invention is directed to a solids handling valve for use in combination with lock hoppers utilized for conveying pulverized coal to a coal gasifier. The valve comprises a fluid-actuated flow control piston disposed within a housing and provided with a tapered primary seal having a recessed seat on the housing and a radially expandable fluid-actuated secondary seal. The valve seals are highly resistive to corrosion, erosion and abrasion by the solids, liquids, and gases associated with the gasification process so as to minimize valve failure.

AGC-2 Irradiation Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rohrbaugh, David Thomas; Windes, William; Swank, W. David

The Next Generation Nuclear Plant (NGNP) will be a helium-cooled, very high temperature reactor (VHTR) with a large graphite core. In past applications, graphite has been used effectively as a structural and moderator material in both research and commercial high temperature gas cooled reactor (HTGR) designs.[ , ] Nuclear graphite H 451, used previously in the United States for nuclear reactor graphite components, is no longer available. New nuclear graphites have been developed and are considered suitable candidates for the new NGNP reactor design. To support the design and licensing of NGNP core components within a commercial reactor, a completemore » properties database must be developed for these current grades of graphite. Quantitative data on in service material performance are required for the physical, mechanical, and thermal properties of each graphite grade with a specific emphasis on data related to the life limiting effects of irradiation creep on key physical properties of the NGNP candidate graphites. Based on experience with previous graphite core components, the phenomenon of irradiation induced creep within the graphite has been shown to be critical to the total useful lifetime of graphite components. Irradiation induced creep occurs under the simultaneous application of high temperatures, neutron irradiation, and applied stresses within the graphite components. Significant internal stresses within the graphite components can result from a second phenomenon—irradiation induced dimensional change. In this case, the graphite physically changes i.e., first shrinking and then expanding with increasing neutron dose. This disparity in material volume change can induce significant internal stresses within graphite components. Irradiation induced creep relaxes these large internal stresses, thus reducing the risk of crack formation and component failure. Obviously, higher irradiation creep levels tend to relieve more internal stress, thus allowing the components longer useful lifetimes within the core. Determining the irradiation creep rates of nuclear grade graphites is critical for determining the useful lifetime of graphite components and is a major component of the Advanced Graphite Creep (AGC) experiment.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mallow, Anne; Abdelaziz, Omar; Graham, Jr., Samuel

The thermal charging performance of paraffin wax combined with compressed expanded natural graphite foam was studied for different graphite bulk densities. Constant heat fluxes between 0.39 W/cm 2 and 1.55 W/cm 2 were applied, as well as a constant boundary temperature of 60 °C. Thermal charging experiments indicate that, in the design of thermal batteries, thermal conductivity of the composite alone is an insufficient metric to determine the influence of the graphite foam on the thermal energy storage. By dividing the latent heat of the composite by the time to end of melt for each applied boundary condition, the energymore » storage performance was calculated to show the effects of composite thermal conductivity, graphite bulk density, and latent heat capacity. For the experimental volume, the addition of graphite beyond a graphite bulk density of 100 kg/m 3 showed limited benefit on the energy storage performance due to the decrease in latent heat storage capacity. These experimental results are used to validate a numerical model to predict the time to melt and for future use in the design of heat exchangers with graphite-foam based phase change material composites. As a result, size scale effects are explored parametrically with the validated model.« less

Use of self-expandable plastic stents for the treatment of esophageal perforations and symptomatic anastomotic leaks.

PubMed

Gelbmann, C M; Ratiu, N L; Rath, H C; Rogler, G; Lock, G; Schölmerich, J; Kullmann, F

2004-08-01

Extensive anastomotic leaks after esophageal resection and esophageal perforations are a therapeutic challenge. The aim of the present study was to assess the potential of the self-expandable Polyflex plastic stent for the treatment of these conditions. Between January 2002 and March 2003, nine patients were treated with a self-expandable Polyflex plastic stent for sealing of thoracic esophagoenteric anastomotic leaks following surgical resection (n = 5) or esophageal perforation (n = 4). In all patients the stents were inserted successfully without technical problems. In all but two patients complete sealing of the leak was achieved as demonstrated by radiography with water-soluble contrast media. The stent migration rate was 30 % and repositioning of the migrated stents was possible in all cases. Complete mucosal healing of the esophageal leaks and stent extraction was achieved in six patients. The stents were in situ for an average period of 135 +/- 78 days. Two critically ill patients with anastomotic leaks died in spite of stent insertion due to sepsis and one patient with esophageal perforation died due to the underlying malignant disease. Our preliminary experience with the self-expanding and removable Polyflex plastic stent for the sealing of anastomotic leaks and esophageal perforations suggests that this stent is a feasible treatment option, in particular, for more extensive esophageal defects, patients with co-morbid conditions, and critically ill patients.

Formation of NiFe2O4/Expanded Graphite Nanocomposites with Superior Lithium Storage Properties

NASA Astrophysics Data System (ADS)

Xiao, Yinglin; Zai, Jiantao; Tian, Bingbing; Qian, Xuefeng

2017-07-01

A NiFe2O4/expanded graphite (NiFe2O4/EG) nanocomposite was prepared via a simple and inexpensive synthesis method. Its lithium storage properties were studied with the goal of applying it as an anode in a lithium-ion battery. The obtained nanocomposite exhibited a good cycle performance, with a capacity of 601 mAh g-1 at a current of 1 A g-1 after 800 cycles. This good performance may be attributed to the enhanced electrical conductivity and layered structure of the EG. Its high mechanical strength could postpone the disintegration of the nanocomposite structure, efficiently accommodate volume changes in the NiFe2O4-based anodes, and alleviate aggregation of NiFe2O4 nanoparticles.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ganesh, Panchapakesan; Kent, Paul R; Mochalin, Vadym N

We simulate the experimentally observed graphitization of nanodiamonds into multi-shell onion-like carbon nanostructures, also called carbon onions, at different temperatures, using reactive force fields. The simulations include long-range Coulomb and van der Waals interactions. Our results suggest that long-range interactions play a crucial role in the phase-stability and the graphitization process. Graphitization is both enthalpically and entropically driven and can hence be controlled with temperature. The outer layers of the nanodiamond have a lower kinetic barrier toward graphitization irrespective of the size of the nanodiamond and graphitize within a few-hundred picoseconds, with a large volume increase. The inner core ofmore » the nanodiamonds displays a large size-dependent kinetic barrier, and graphitizes much more slowly with abrupt jumps in the internal energy. It eventually graphitizes by releasing pressure and expands once the outer shells have graphitized. The degree of transformation at a particular temperature is thereby determined by a delicate balance between the thermal energy, long-range interactions, and the entropic/enthalpic free energy gained by graphitization. Upon full graphitization, a multi-shell carbon nanostructure appears, with a shell-shell spacing of about {approx}3.4 {angstrom} for all sizes. The shells are highly defective with predominantly five- and seven-membered rings to curve space. Larger nanodiamonds with a diameter of 4 nm can graphitize into spiral structures with a large ({approx}29-atom carbon ring) pore opening on the outermost shell. Such a large one-way channel is most attractive for a controlled insertion of molecules/ions such as Li ions, water, or ionic liquids, for increased electrochemical capacitor or battery electrode applications.« less

Fuel containment, lightning protection and damage tolerance in large composite primary aircraft structures

NASA Technical Reports Server (NTRS)

Griffin, Charles F.; James, Arthur M.

1985-01-01

The damage-tolerance characteristics of high strain-to-failure graphite fibers and toughened resins were evaluated. Test results show that conventional fuel tank sealing techniques are applicable to composite structures. Techniques were developed to prevent fuel leaks due to low-energy impact damage. For wing panels subjected to swept stroke lightning strikes, a surface protection of graphite/aluminum wire fabric and a fastener treatment proved effective in eliminating internal sparking and reducing structural damage. The technology features developed were incorporated and demonstrated in a test panel designed to meet the strength, stiffness, and damage tolerance requirements of a large commercial transport aircraft. The panel test results exceeded design requirements for all test conditions. Wing surfaces constructed with composites offer large weight savings if design allowable strains for compression can be increased from current levels.

Influence of carbon additives on operational properties of the intumescent coatings for the fire protection of building constructions

NASA Astrophysics Data System (ADS)

Zybina, Olga; Gravit, Marina; Stein, Yelena

2017-10-01

In work ability of the intercalated graphite entered into the fireproof intumescent compositions to act as catalytically active additive raising operational characteristics of the classical distending coverings intended for fire protection of building constructions. It is established that thermal expanded graphite, as well as nano-additives, increase frequency rate, durability, elasticity, density and uniformity of a coke layer of a fireproof covering for increase of fire resistance of a building construction.

FUEL ELEMENT FOR A NUCLEAR REACTOR

DOEpatents

Davidson, J.K.

1963-11-19

A fuel element structure particularly useful in high temperature nuclear reactors is presented. Basically, the structure comprises two coaxial graphite sleeves integrally joined together by radial fins. Due to the high structural strength of graphite at high temperatures and the rigidity of this structure, nuclear fuel encased within the inner sleeve in contiguous relation therewith is supported and prevented from expanding radially at high temperatures. Thus, the necessity of relying on the usual cladding materials with relatively low temperature limitations for structural strength is removed. (AEC)

Characterization of Epoxy Functionalized Graphite Nanoparticles and the Physical Properties of Epoxy Matrix Nanocomposites

NASA Technical Reports Server (NTRS)

Miller, Sandi G.; Bauer, Jonathan L.; Maryanski, Michael J.; Heimann, Paula J.; Barlow, Jeremy P.; Gosau, Jan-Michael; Allred, Ronald E.

2010-01-01

This work presents a novel approach to the functionalization of graphite nanoparticles. The technique provides a mechanism for covalent bonding between the filler and matrix, with minimal disruption to the sp2 hybridization of the pristine graphene sheet. Functionalization proceeded by covalently bonding an epoxy monomer to the surface of expanded graphite, via a coupling agent, such that the epoxy concentration was measured as approximately 4 wt.%. The impact of dispersing this material into an epoxy resin was evaluated with respect to the mechanical properties and electrical conductivity of the graphite-epoxy nanocomposite. At a loading as low as 0.5 wt.%, the electrical conductivity was increased by five orders of magnitude relative to the base resin. The material yield strength was increased by 30% and Young s modulus by 50%. These results were realized without compromise to the resin toughness.

Mussel-Inspired Polydopamine Coating for Enhanced Thermal Stability and Rate Performance of Graphite Anodes in Li-Ion Batteries.

PubMed

Park, Seong-Hyo; Kim, Hyeon Jin; Lee, Junmin; Jeong, You Kyeong; Choi, Jang Wook; Lee, Hochun

2016-06-08

Despite two decades of commercial history, it remains very difficult to simultaneously achieve both high rate capability and thermal stability in the graphite anodes of Li-ion batteries because the stable solid electrolyte interphase (SEI) layer, which is essential for thermal stability, impedes facile Li(+) ion transport at the interface. Here, we resolve this longstanding challenge using a mussel-inspired polydopamine (PD) coating via a simple immersion process. The nanometer-thick PD coating layer allows the formation of an SEI layer on the coating surface without perturbing the intrinsic properties of the SEI layer of the graphite anodes. PD-coated graphite exhibits far better performances in cycling test at 60 °C and storage test at 90 °C than bare graphite. The PD-coated graphite also displays superior rate capability during both lithiation and delithiation. As evidenced by surface free energy analysis, the enhanced performance of the PD-coated graphite can be ascribed to the Lewis basicity of the PD, which scavenges harmful hydrofluoric acid and forms an intermediate triple-body complex among a Li(+) ion, solvent molecules, and the PD's basic site. The usefulness of the proposed PD coating can be expanded to various electrodes in rechargeable batteries that suffer from poor thermal stability and interfacial kinetics.

Formation, characterization, and dynamics of onion-like carbon structures for electrical energy storage from nanodiamonds using reactive force fields

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ganesh, P.; Kent, P. R. C.; Mochalin, V.

We simulate the experimentally observed graphitization of nanodiamonds into multi-shell onion-like carbonnanostructures, also called carbon onions, at different temperatures, using reactive force fields. The simulations include long-range Coulomb and van der Waals interactions. Our results suggest that long-range interactions play a crucial role in the phase-stability and the graphitization process. Graphitization is both enthalpically and entropically driven and can hence be controlled with temperature. The outer layers of the nanodiamond have a lower kinetic barrier toward graphitization irrespective of the size of the nanodiamond and graphitize within a few-hundred picoseconds, with a large volume increase. The inner core of themore » nanodiamonds displays a large size-dependent kinetic barrier, and graphitizes much more slowly with abrupt jumps in the internal energy. It eventually graphitizes by releasing pressure and expands once the outer shells have graphitized. The degree of transformation at a particular temperature is thereby determined by a delicate balance between the thermal energy, long-range interactions, and the entropic/enthalpic free energy gained by graphitization. Upon full graphitization, a multi-shell carbonnanostructure appears, with a shell-shell spacing of about ~3.4 Å for all sizes. The shells are highly defective with predominantly five- and seven-membered rings to curve space. Larger nanodiamonds with a diameter of 4 nm can graphitize into spiral structures with a large (~29-atom carbon ring) pore opening on the outermost shell. Such a large one-way channel is most attractive for a controlled insertion of molecules/ions such as Li ions, water, or ionic liquids, for increased electrochemical capacitor or battery electrode applications.« less

Formation, characterization and dynamics of onion like carbon structures from nanodiamonds using reactive force-fields for electrical energy storage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kent, Paul R

We simulate the experimentally observed graphitization of nanodiamonds into multi-shell onion-like carbon nanostructures, also called carbon onions, at different temperatures, using reactive force fields. The simulations include long-range Coulomb and van der Waals interactions. Our results suggest that long-range interactions play a crucial role in the phase-stability and the graphitization process. Graphitization is both enthalpically and entropically driven and can hence be controlled with temperature. The outer layers of the nanodiamond have a lower kinetic barrier toward graphitization irrespective of the size of the nanodiamond and graphitize within a few-hundred picoseconds, with a large volume increase. The inner core ofmore » the nanodiamonds displays a large size-dependent kinetic barrier, and graphitizes much more slowly with abrupt jumps in the internal energy. It eventually graphitizes by releasing pressure and expands once the outer shells have graphitized. The degree of transformation at a particular temperature is thereby determined by a delicate balance between the thermal energy, long-range interactions, and the entropic/enthalpic free energy gained by graphitization. Upon full graphitization, a multi-shell carbon nanostructure appears, with a shell-shell spacing of about {approx}3.4 {angstrom} for all sizes. The shells are highly defective with predominantly five- and seven-membered rings to curve space. Larger nanodiamonds with a diameter of 4 nm can graphitize into spiral structures with a large ({approx}29-atom carbon ring) pore opening on the outermost shell. Such a large one-way channel is most attractive for a controlled insertion of molecules/ions such as Li ions, water, or ionic liquids, for increased electrochemical capacitor or battery electrode applications.« less

Dry compliant seal for phosphoric acid fuel cell

DOEpatents

Granata, Jr., Samuel J.; Woodle, Boyd M.

1990-01-01

A dry compliant overlapping seal for a phosphoric acid fuel cell preformed f non-compliant Teflon to make an anode seal frame that encircles an anode assembly, a cathode seal frame that encircles a cathode assembly and a compliant seal frame made of expanded Teflon, generally encircling a matrix assembly. Each frame has a thickness selected to accommodate various tolerances of the fuel cell elements and are either bonded to one of the other frames or to a bipolar or end plate. One of the non-compliant frames is wider than the other frames forming an overlap of the matrix over the wider seal frame, which cooperates with electrolyte permeating the matrix to form a wet seal within the fuel cell that prevents process gases from intermixing at the periphery of the fuel cell and a dry seal surrounding the cell to keep electrolyte from the periphery thereof. The frames may be made in one piece, in L-shaped portions or in strips and have an outer perimeter which registers with the outer perimeter of bipolar or end plates to form surfaces upon which flanges of pan shaped, gas manifolds can be sealed.

Adsorption and regeneration of expanded graphite modified by CTAB-KBr/H3PO4 for marine oil pollution.

PubMed

Xu, Congbin; Jiao, Chunlei; Yao, Ruihua; Lin, Aijun; Jiao, Wentao

2018-02-01

The cleaning-up of viscous oil spilled in ocean is a global challenge, especially in Bohai, due to its slow current movement and poor self-purification capacity. Frequent oil-spill accidents not only cause severe and long-term damages to marine ecosystems, but also lead to a great loss of valuable resources. To eliminate the environmental pollution of oil spills, an efficient and environment-friendly oil-recovery approach is necessary. In this study, 1 expanded graphite (EG) modified by CTAB-KBr/H 3 PO 4 was synthesized via composite intercalation agents of CTAB-KBr and natural flake graphite, followed by the activation of phosphoric acid at low temperature. The resultant modified expanded graphite (M-EG) obtained an interconnected and continuous open microstructure with lower polarity surface, more and larger pores, and increased surface hydrophobicity. Due to these characteristics, M-EG exhibited a superior adsorption capacity towards marine oil. The saturated adsorption capacities of M-EG were as large as 7.44  g/g for engine oil, 6.12 g/g for crude oil, 5.34 g/g for diesel oil and 4.10 g/g for gasoline oil in 120min, exceeding the capacity of pristine EG. Furthermore, M-EG maintained good removal efficiency under different adsorption conditions, such as temperature, oil types, and sodium salt concentration. In addition, oils sorbed into M-EG could be recovered either by a simple compression or filtration-drying treatment with a recovery ratio of 58-83%. However, filtration-drying treatment shows better performance in preserving microstructures of M-EG, which ensures the adsorbents can be recycled several times. High removal capability, fast adsorption efficiency, excellent stability and good recycling performance make M-EG an ideal candidate for treating marine oil pollution in practical application. Copyright © 2017 Elsevier Ltd. All rights reserved.

Fuel containment and damage tolerance for large composite primary aircraft structures. Phase 1: Testing

NASA Technical Reports Server (NTRS)

Sandifer, J. P.

1983-01-01

Technical problems associated with fuel containment and damage tolerance of composite material wings for transport aircraft were identified. The major tasks are the following: (1) the preliminary design of damage tolerant wing surface using composite materials; (2) the evaluation of fuel sealing and lightning protection methods for a composite material wing; and (3) an experimental investigation of the damage tolerant characteristics of toughened resin graphite/epoxy materials. The test results, the test techniques, and the test data are presented.

In-situ confined formation of NiFe layered double hydroxide quantum dots in expanded graphite for active electrocatalytic oxygen evolution

NASA Astrophysics Data System (ADS)

Guo, Jinxue; Li, Xiaoyan; Sun, Yanfang; Liu, Qingyun; Quan, Zhenlan; Zhang, Xiao

2018-06-01

Development of noble-metal-free catalysts towards highly efficient electrochemical oxygen evolution reaction (OER) is critical but challenging in the renewable energy area. Herein, we firstly embed NiFe LDHs quantum dots (QDs) into expanded graphite (NiFe LDHs/EG) via in-situ confined formation process. The interlayer spacing of EG layers acts as nanoreactors for spatially confined formation of NiFe LDHs QDs. The QDs supply huge catalytic sites for OER. The in-situ decoration endows the strong affinity between QDs with EG, thus inducing fast charge transfer. Based on the aforementioned benefits, the designed catalyst exhibits outstanding OER properties, in terms of small overpotential (220 mV required to generate 10 mA cm-2), low Tafel slope, and good durable stability, making it a promising candidate for inexpensive OER catalyst.

In Situ Raman Microscopy of a Single Graphite Microflake Electrode in a Li(+)-containing Electrolyte

NASA Technical Reports Server (NTRS)

Shi, Qing-Fang; Dokko, Kaoru; Scherson, Daniel A.

2003-01-01

Highly detailed Raman spectra from a single KS-44 graphite microflake electrode as a function of the applied potential have been collected in situ using a Raman microscope and a sealed spectroelectrochemical cell isolated from the laboratory environment. Correlations were found between the Raman spectral features and the various Li(+) intercalation stages while recording in real time Raman spectra during a linear potential scan from 0.7 down ca. 0.0V vs Li/Li(+) at a rate of 0.1 mV/s in a 1M LiClO4 solution in a 1:l (by volume) ethylene carbonate (EC):diethyl carbonate (DEC) mixture. In particular, clearly defined isosbestic points were observed for data collected in the potential range where the transition between dilute phase 1 and phase 4 of lithiated graphite is known to occur, i.e. 0.157 < E < 0.215 vs Li/Li(+). Statistical analysis of the spectroscopic data within this region made it possible to determine independently the fraction of each of the two phases present as a function of potential without relying on coulometric information and then predict, based on the proposed stoichiometry for the transition, a spectrally-derived voltammetric feature.

Non-graphite crucible for high temperature applications

DOEpatents

Holcombe, Cressie E.; Pfeiler, William A.

1996-01-01

A multi-piece crucible for high temperature applications comprises a tubular side wall member having a lip on the inside surface and a bottom member or members forming a container for containing a melt of a material during a high temperature melt-casting operations. The multi-piece design prevents cracking of the crucible or leakage of the melt from the crucible during the melt-casting operation. The lip of the tubular member supports the bottom member. The contacting surfaces where the lip of the tubular side wall member contacts the bottom member of the multi-piece crucible contains a ceramic sealing material. The ceramic sealing material forms a seal sufficient to prevent the melt of the material from leaking out of the multi-piece crucible during the melt-casting process. The multi-piece crucible is made of a material which is chemically inert to the melt and has structural integrity at the melting point temperature of the melt, or of a material coated with such a material. The multi-piece crucible is contained in a thermal can assembly of a high temperature induction furnace during a high temperature melt-casting operation. One embodiment of the multi-piece crucible comprises a tubular member having a vertical slot filled with a ceramic sealing material to provide expansion of the tubular member without cracking during the high temperature melt-casting operation.

Non-graphite crucible for high temperature applications

DOEpatents

Holcombe, C.E.; Pfeiler, W.A.

1996-01-09

A multi-piece crucible for high temperature applications comprises a tubular side wall member having a lip on the inside surface and a bottom member or members forming a container for containing a melt of a material during a high temperature melt-casting operations. The multi-piece design prevents cracking of the crucible or leakage of the melt from the crucible during the melt-casting operation. The lip of the tubular member supports the bottom member. The contacting surfaces where the lip of the tubular side wall member contacts the bottom member of the multi-piece crucible contains a ceramic sealing material. The ceramic sealing material forms a seal sufficient to prevent the melt of the material from leaking out of the multi-piece crucible during the melt-casting process. The multi-piece crucible is made of a material which is chemically inert to the melt and has structural integrity at the melting point temperature of the melt, or of a material coated with such a material. The multi-piece crucible is contained in a thermal can assembly of a high temperature induction furnace during a high temperature melt-casting operation. One embodiment of the multi-piece crucible comprises a tubular member having a vertical slot filled with a ceramic sealing material to provide expansion of the tubular member without cracking during the high temperature melt-casting operation. 9 figs.

The staging mechanism of AlCl4 intercalation in a graphite electrode for an aluminium-ion battery.

PubMed

Bhauriyal, Preeti; Mahata, Arup; Pathak, Biswarup

2017-03-15

Identifying a suitable electrode material with desirable electrochemical properties remains a primary challenge for rechargeable Al-ion batteries. Recently an ultrafast rechargeable Al-ion battery was reported with high charge/discharge rate, (relatively) high discharge voltage and high capacity that uses a graphite-based cathode. Using calculations from first-principles, we have investigated the staging mechanism of AlCl 4 intercalation into bulk graphite and evaluated the stability, specific capacity and voltage profile of AlCl 4 intercalated compounds. Ab initio molecular dynamics is performed to investigate the thermal stability of AlCl 4 intercalated graphite structures. Our voltage profiles show that the first AlCl 4 intercalation step could be a more sluggish step than the successive intercalation steps. However, the diffusion of AlCl 4 is very fast in the expanded graphite host layers with a diffusion barrier of ∼0.01 eV, which justifies the ultrafast charging rate of a graphite based Al-ion battery. And such an AlCl 4 intercalated battery provides an average voltage of 2.01-2.3 V with a maximum specific capacity of 69.62 mA h g -1 , which is excellent for anion intercalated batteries. Our density of states and Bader charge analysis shows that the AlCl 4 intercalation into the bulk graphite is a charging process. Hence, we believe that our present study will be helpful in understanding the staging mechanism of AlCl 4 intercalation into graphite-like layered electrodes for Al-ion batteries, thus encouraging further experimental work.

They Came from the Deep in the Supernova: The Origin of TiC and Metal Subgrains in Presolar Graphite Grains

NASA Astrophysics Data System (ADS)

Lodders, Katharina

2006-08-01

A new formation scenario for TiC and Fe-Ni metal inclusions in presolar graphite grains of supernova origin is described. The mineralogy and chemistry require condensation of Fe-Ni titanides from Fe-, Ni-, and Ti-rich gaseous ejecta, subsequent carburization to make TiC and metal, and encapsulation into graphite. Titanides only condense if Si is depleted relative to heavier elements, which requires α-rich freeze-out and a deep mass cut for the supernova ejecta. This Si-poor core material must remain unmixed with other supernova zones until the titanides condense. This can be accomplished by transport of core ejecta in bipolar jets through the major expanding supernova zone ejecta. If the jets stall in regions dominated by C-rich ejecta such as the C-He zone, where graphite condenses, thermochemically favored in situ carburization of the titanides-either before or during encapsulation into condensing graphite-leads to a TiC-and-metal composite. This scenario agrees with theoretical models and observations of asymmetric core collapse in supernovae that are associated with bipolar jets loaded with iron-peak elements.

Improved adaptability of polyaryl-ether-ether-ketone with texture pattern and graphite-like carbon film for bio-tribological applications

NASA Astrophysics Data System (ADS)

Ren, Siming; Huang, Jinxia; Cui, Mingjun; Pu, Jibin; Wang, Liping

2017-04-01

With the development of surface treatment technology, an increasing number of bearings, seals, dynamic friction drive or even biomedical devices involve a textured surface to improve lubrication and anti-wear. The present investigation has been conducted in order to evaluate the friction and wear behaviours of textured polyaryl-ether-ether-ketone (PEEK) coated with a graphite-like carbon (GLC) film sliding against stainless steel pin in biological medium. Compared with pure PEEK, the PEEK coated with GLC film shows excellent tribological performance with a low friction of 0.08 and long lifetime (wear volumes are about 3.78 × 10-4 mm3 for un-textured one and 2.60 × 10-4 mm3 for textured GLC film after 36,000 s of sliding) under physiological saline solution. In particular, the GLC film with appropriate dimple area density is effective to improve friction reduction and wear resistance properties of PEEK substrate under biological solution, which is attributed to the entrapment of wear debris in the dimples to inhibit the graphitization and the fluid dynamic pressure effect derived from the texture surface to increase the thickness in elastohydrodynamic lubrication (EHL) film during sliding motions. Moreover, the friction coefficient of GLC film under physiological saline solution decreases with the increase in the applied load. With the increasing applied load, the texture surface is responsible for accounting the improved wear resistance and a much lower graphitization of the GLC film during whole test.

Performance of Oil Pumping Rings: An Analytical and Experimental Study

NASA Technical Reports Server (NTRS)

Eusepi, M. W.; Walowit, J. A.; Pinkus, O.; Holmes, P.

1986-01-01

A steady-state design computer program was developed to predict the performance of pumping rings as functions of geometry, applied loading, speed, ring modulus, and fluid viscosity. Additional analyses were developed to predict transient behavior of the ring and the effects of temperature rises occurring in the hydrodynamic film between the ring and shaft. The analysis was initially compared with previous experimental data and then used to design additional rings for further testing. Tests were performed with Rulon, carbon-graphite, and babbit rings. The design analysis was used to size all of the rings and to select the ranges of clearances, thickness, and loading. Although full quantitative agreement was lacking, relative agreement existed in that rings that were predicted to perform well theoretically, generally performed well experimentally. Some causes for discrepanices between theory and experiment are believed to be due to starvation, leakage past the secondary seal at high pressures, and uncertainties in the small clearances and local inlet temperatures to the pumping ring. A separate preliminary analysis was performed for a pumping Leningrader seal. This anlaysis can be used to predict the film thickness and flow rate thr ough the seal as a function of pressure, speed, loading, and geometry.

Activated graphene as a cathode material for Li-ion hybrid supercapacitors.

PubMed

Stoller, Meryl D; Murali, Shanthi; Quarles, Neil; Zhu, Yanwu; Potts, Jeffrey R; Zhu, Xianjun; Ha, Hyung-Wook; Ruoff, Rodney S

2012-03-14

Chemically activated graphene ('activated microwave expanded graphite oxide', a-MEGO) was used as a cathode material for Li-ion hybrid supercapacitors. The performance of a-MEGO was first verified with Li-ion electrolyte in a symmetrical supercapacitor cell. Hybrid supercapacitors were then constructed with a-MEGO as the cathode and with either graphite or Li(4)Ti(5)O(12) (LTO) for the anode materials. The results show that the activated graphene material works well in a symmetrical cell with the Li-ion electrolyte with specific capacitances as high as 182 F g(-1). In a full a-MEGO/graphite hybrid cell, specific capacitances as high as 266 F g(-1) for the active materials at operating potentials of 4 V yielded gravimetric energy densities for a packaged cell of 53.2 W h kg(-1).

Method of fabricating composite structures

NASA Technical Reports Server (NTRS)

Sigur, W. A. (Inventor)

1990-01-01

A method of fabricating structures formed from composite materials by positioning the structure about a high coefficient of thermal expansion material, wrapping a graphite fiber overwrap about the structure, and thereafter heating the assembly to expand the high coefficient of thermal expansion material to forcibly compress the composite structure against the restraint provided by the graphite overwrap. The high coefficient of thermal expansion material is disposed about a mandrel with a release system therebetween, and with a release system between the material having the high coefficient of thermal expansion and the composite material, and between the graphite fibers and the composite structure. The heating may occur by inducing heat into the assembly by a magnetic field created by coils disposed about the assembly through which alternating current flows. The method permits structures to be formed without the use of an autoclave.

Method of fabricating composite structures

NASA Technical Reports Server (NTRS)

Sigur, Wanda A. (Inventor)

1992-01-01

A method of fabricating structures formed from composite materials by positioning the structure about a high coefficient of thermal expansion material, wrapping a graphite fiber overwrap about the structure, and thereafter heating the assembly to expand the high coefficient of thermal expansion material to forcibly compress the composite structure against the restraint provided by the graphite overwrap. The high coefficient of thermal expansion material is disposed about a mandrel with a release system therebetween, and with a release system between the material having the high coefficient of thermal expansion and the composite material, and between the graphite fibers and the composite structure. The heating may occur by inducing heat into the assembly by a magnetic field created by coils disposed about the assembly through which alternating current flows. The method permits structures to be formed without the use of an autoclave.

Single-Step, Solvent-Free, Catalyst-Free Preparation of Holey Carbon Allotropes

NASA Technical Reports Server (NTRS)

Lin, Yi (Inventor); Funk, Michael R. (Inventor); Kim, Jae-Woo (Inventor); Connell, John W. (Inventor); Campbell, Caroline J. (Inventor)

2017-01-01

Methods for forming holey carbon allotropes and graphene nanomeshes are provided by the various embodiments. The various embodiments may be applicable to a variety of carbon allotropes, such as graphene, graphene oxide, reduced graphene oxide, thermal exfoliated graphene, graphene nanoribbons, graphite, exfoliated graphite, expanded graphite, carbon nanotubes (e.g., single-walled carbon nanotubes, double-walled carbon nanotubes, few-walled carbon nanotubes, multi-walled carbon nanotubes, etc.), carbon nanofibers, carbon fibers, carbon black, amorphous carbon, fullerenes, etc. The methods may produce holey carbon allotropes without the use of solvents, catalysts, flammable gas, additional chemical agents, or electrolysis to produce the pores (e.g., holes, etc.) in the carbon allotropes. In an embodiment, a carbon allotrope may be heated at a working window temperature for a working period of time to create holes in the carbon allotrope.

Coping with Physiological Oxidative Stress: A Review of Antioxidant Strategies in Seals

PubMed Central

Vázquez-Medina, José Pablo; Zenteno-Savín, Tania; Elsner, Robert; Ortiz, Rudy M.

2012-01-01

While diving, seals are exposed to apnea-induced hypoxemia and repetitive cycles of ischemia/reperfusion. While on land, seals experience sleep apnea, as well as prolonged periods of food and water deprivation. Prolonged fasting, sleep apnea, hypoxemia and ischemia/reperfusion increase oxidant production and oxidative stress in terrestrial mammals. In seals, however, neither prolonged fasting nor apnea-induced hypoxemia or ischemia/reperfusion increase systemic or local oxidative damage. The strategies seals evolved to cope with increased oxidant production are reviewed in the present manuscript. Among these strategies, high antioxidant capacity and the oxidant-mediated activation of hormetic responses against hypoxia and oxidative stress are discussed. In addition to expanding our knowledge of the evolution of antioxidant defenses and adaptive responses to oxidative stress, understanding the mechanisms that allow adapted mammals to avoid oxidative damage has the potential to advance our knowledge of oxidative stress-induced pathologies and to enhance the translative value of biomedical therapies in the long term. PMID:22327141

Long-life, space-maintainable nuclear stage regulators and shutoff valves

NASA Technical Reports Server (NTRS)

1972-01-01

The six most promising valve, regulator, and remote coupling concepts, representing the more radical designs from twenty concepts generated, were investigated. Of the three valves, one has no moving parts because shutoff sealing is accomplished by an electromagnetic field which ionized the flowing fluid. Another valve uses liquid metal to obtain sealing. In the third valve, high sealing forces are generated by heating and expanding trapped hydrogen. The pressure regulator is an electronically controlled, electromechanically operated, single state valve. Its complexity is in electronic circuitry, and the design results in less weight, increased reliability and performance flexibility, and multipurpose application. The two remote couplings feature the minimization of weight and mechanical complexity. One concept uses a low melting temperature metal alloy which is injected into the joint cavity; upon solidification, the alloy provides a seal and a structural joint. The second concept is based on the differential thermal expansion of the coupling mating parts. At thermal equilibrium there is a predetermined interference between the parts, and sealing is achieved by interference loading.

Production of an impermeable composite of irradiated graphite and glass by hot isostatic pressing as a long term leach resistant waste form

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fachinger, Johannes; Muller, Walter; Marsat, Eric

2013-07-01

Around 250,000 tons of irradiated graphite (i-graphite) exists worldwide and can be considered as a current waste or future waste stream. The largest national i-graphite inventory is located in UK (∼ 100,000 tons) with significant quantities also in Russia and France [5]. Most of the i-graphite remains in the cores of shutdown nuclear reactors including the MAGNOX type in UK and the UNGG in France. Whilst there are still operational power reactors with graphite cores, such as the Russian RBMKs and the AGRs in UK, all of them will reach their end of life during the next two decades. Themore » most common reference waste management option of i-graphite is a wet or dry retrieval of the graphite blocks from the reactor core and the grouting of these blocks in a container without further conditioning. This produces large waste package volumes because the encapsulation capacity of the grout is limited and large cavities in the graphite blocks could reduce the packing densities. Packing densities from 0.5 to 1 tons per cubic meter have been assumed for grouting solutions. Furthermore the grout is permeable. This could over time allow the penetration of aqueous phases into the waste block and a potential dissolution and release of radionuclides. As a result particularly highly soluble radionuclides may not be retained by the grout. Vitrification could present an alternative, however a similar waste package volume increase may be expected since the encapsulation capacity of glass is potentially similar to or worse than that of grout. FNAG has developed a process for the production of a graphite-glass composite material called Impermeable Graphite Matrix (IGM) [3]. This process is also applicable to irradiated graphite which allows the manufacturing of an impermeable material without volume increase. Crushed i-graphite is mixed with 20 vol.% of glass and then pressed under vacuum at an elevated temperature in an axial hot vacuum press (HVP). The obtained product has zero or negligible porosity and a water impermeable structure. Structural analysis shows that the glass in the composite has replaced the pores in the graphite structure. The typical pore volume of a graphite material is in the range of 20 vol.%. Therefore no volume increase will occur in comparison with the former graphite material. This IGM material will allow the encapsulation of graphite with package densities larger than 1.5 ton per cubic meter. Therefore a huge volume saving can be achieved by such an alternative encapsulation method. Disposal performance is also enhanced since little or no leaching of radionuclides is observed due to the impermeability of the material NNL and FNAG have proved that IGM can be produced by hot isostatic pressing (HIP) which has several advantages for radioactive materials over the HVP process. - The sealed HIP container avoids the release of any radionuclides. - The outside of the waste package is not contaminated. - The HIP process time is shorter than the HVP process time. The isostatic press avoids anisotropic density distributions. - Simple filling of the HIP container has advantages over the filling of an axial die. (authors)« less

SIMPLIFIED SODIUM GRAPHITE REACTOR SYSTEM

DOEpatents

Dickinson, R.W.

1963-03-01

This patent relates to a nuclear power reactor comprising a reactor vessel, shielding means positioned at the top of said vessel, means sealing said reactor vessel to said shielding means, said vessel containing a quantity of sodium, a core tank, unclad graphite moderator disposed in said tank, means including a plurality of process tubes traversing said tank for isolating said graphite from said sodium, fuel elements positioned in said process tubes, said core tank being supported in spaced relation to the walls and bottom of said reactor vessel and below the level of said sodium, neutron shielding means positioned adjacent said core tank between said core tank and the walls of said vessel, said neutron shielding means defining an annuiar volume adjacent the inside wall of said reactor vessel, inlet plenum means below said core tank for providing a passage between said annular volume and said process tubes, heat exchanger means removably supported from the first-named shielding means and positioned in said annular volume, and means for circulating said sodium over said neutron shielding means down through said heat exchanger, across said inlet plenum and upward through said process tubes, said last-named means including electromagnetic pumps located outside said vessel and supported on said vessel wall between said heat exchanger means and said inlet plenum means. (AEC)

Double-ended ceramic helical-rotor expander

DOEpatents

Mohr, Peter B.; Myers, Wendell B.

1995-01-01

A ceramic helical rotor expander using a double-ended or tandem herringbone type rotor arrangement with bearing and seal assemblies remote from the hot gas inlets and especially capable of operating at an inlet temperature of above 1100.degree. C. The rotors are solid or hollow and bonded to hollow metal shafts, and mounted in a composite or simple prismatic casing. The rotors, casing and shafts are constructed from low expansivity materials. In the preferred embodiment the rotors are constructed of silicon nitride and the shafts constructed of an molybdenum alloy, with the metal shafts being supported in bearings and secured to synchronizing gears. The rotors and casing may be provided with coolant channels therein, and are constructed to eliminate the problem of end leakages at inlet temperature and pressure, and the need for high temperature bearings and seals.

Double-ended ceramic helical-rotor expander

DOEpatents

Mohr, P.B.; Myers, W.B.

1995-02-28

A ceramic helical rotor expander is disclosed using a double-ended or tandem herringbone type rotor arrangement with bearing and seal assemblies remote from the hot gas inlets and especially capable of operating at an inlet temperature of above 1,100 C. The rotors are solid or hollow and bonded to hollow metal shafts, and mounted in a composite or simple prismatic casing. The rotors, casing and shafts are constructed from low expansivity materials. In the preferred embodiment the rotors are constructed of silicon nitride and the shafts constructed of an molybdenum alloy, with the metal shafts being supported in bearings and secured to synchronizing gears. The rotors and casing may be provided with coolant channels therein, and are constructed to eliminate the problem of end leakages at inlet temperature and pressure, and the need for high temperature bearings and seals. 3 figs.

Synergistic effect between ammonium polyphosphate and expandable graphite on flame-retarded poly(butylene terephthalate)

NASA Astrophysics Data System (ADS)

Zhang, Weizhou; Ren, Jiawei; Wei, Ting; Guo, Weihong

2018-02-01

In this paper, the synergistic effect of ammonium polyphosphate (APP) and expandable graphite (EG) on flame-retarded poly(butylene terephthalate) (PBT) was systermically investigated using limiting oxygen index (LOI), UL-94 testing, microscale combustion calorimetry (MCC), thermal-gravimetric analysis (TGA) and scanning electronic microscopy (SEM). PBT composites containing 20 wt% of APP: EG (1:3) combinations exhibits a high LOI value of 29.8 and reaches V-0 rating in UL-94 testing, indicating that the flame retardant property is greatly enhanced compared to the composites solely with APP or EG. SEM images show that the combination of APP and EG could promote the formation of a compact char layer. The compact char layer protects the PBT resin efficiently by preventing penetration of heat flux inside the matrix and retards the decomposition of PBT, consequently improves the thermal stability of PBT materials as revealed by TGA. All of the results demonstrate that APP and EG are high efficiency synergists for improving the flame retardation of PBT materials.

Thermal Conductivity of Eutectic Nitrates and Nitrates/Expanded Graphite Composite as Phase Change Materials.

PubMed

Xiao, Xin; Zhang, Peng; Meng, Zhao-Nan; Li, Ming

2015-04-01

Nitrates and eutectic nitrate mixtures are considered as potential phase change materials (PCMs) for the middle-temperature-range solar energy storage applications. But the extensive utilization is restricted by the poor thermal conductivity and thermal stability. In the present study, sodium nitrate-potassium nitrate eutectic mixture was used as the base PCM, and expanded graphite (EG) was added to the mixture so as to improve the thermal conductivities. The elaboration method consists of a physically mixing of salt powders with or without EG, and the composite PCMs were cold-compressed to form shape-stabilized PCMs at room temperature. The thermal conductivities of the composite PCMs fabricated by cold-compression were investigated at different temperatures by the steady state method. The results showed that the addition of EG significantly enhanced the thermal conductivities. The thermal conductivities of pure nitrates and nitrates/EG composite PCMs in solid state showed the behavior of temperature dependant, and they slightly decreased with the increase of the temperature.

Method and technique for installing light-weight, fragile, high-temperature fiber insulation

NASA Technical Reports Server (NTRS)

Patel, B. C. (Inventor)

1983-01-01

A method of installing fragile, light weight, high temperature fiber insulation, particularly where the insulation is to be used as a seal strip providing a high order of thermal barrier insulation is discussed. The process is based on provision of a strip of the mineral batting cut oversize by a predetermined amount, saturated in a fugitive polymer solution, compressed in a mold, dried and cured to form a rigidized batting material which is machined to required shape. The machine dimensions would normally be at least nominally less than the dimensions of the cavity to be sealed. After insertion in the cavity, which may be a wire-mesh seal enclosure, the apparatus is subjected to baking at a temperature sufficiently high to cause the resin to burn off cleanly, leaving the batting substantially in its original condition and expanded into the cavity or seal enclosure.

A method and technique for installing light-weight fragile, high-temperature fiber insulation

NASA Technical Reports Server (NTRS)

Ballantine, T. J. (Inventor)

1982-01-01

A method of installing fragile, light-weight, high-temperature fiber insulation, particularly where the insulation is to be used as a seal strip providing a high order of thermal barrier insulation is described. The process is based on provision of a strip of the mineral batting cut oversize by a predetermined amount, saturated in a fugitive polymer solution, compressed in a mold, dried and cured to form a rigidized batting material which may be machined to required shape. The machined dimensions would normally be at least nominally less than the dimensions of the cavity to be sealed. After insertion in the cavity, which may be a wire-mesh seal enclosure, the apparatus is subjected to baking at a temperature sufficiently high to cause the resin to burn off cleanly, leaving the batting substantially in its original condition and expanded into the cavity or seal enclosure.

Enhanced adsorption of Eu(III) on mesoporous Al2O3/expanded graphite composites investigated by macroscopic and microscopic techniques.

PubMed

Sun, Yubing; Chen, Changlun; Tan, Xiaoli; Shao, Dadong; Li, Jiaxing; Zhao, Guixia; Yang, Shubin; Wang, Qi; Wang, Xiangke

2012-11-21

Mesoporous Al(2)O(3) was intercalated into an expanded graphite (EG) interlayer to prepare mesoporous Al(2)O(3)/EG composites. The basal spacing of mesoporous Al(2)O(3)/EG composites was enlarged as compared to raw graphite from the X-ray diffraction analysis. The massive surface functional groups and wedge-shaped pores were observed in terms of potentiometric acid-base titration analysis and scanning electron microscope, respectively. The pH-dependent adsorption of Eu(III) on mesoporous Al(2)O(3)/EG composites was evidently independent of ionic strength. The maximum adsorption capacity of Eu(III) on mesoporous Al(2)O(3)/EG composites at pH 6.0 and T = 293 K was calculated to be 5.14 mg g(-1). Desorption kinetics and cyclic operation results showed that mesoporous Al(2)O(3)/EG composites presented high hydrothermal stability in aqueous solution. The thermodynamic parameters suggested that Eu(III) adsorption on mesoporous Al(2)O(3)/EG composites is an endothermic and a spontaneous process. The decrease of Eu-O bond distance with the increasing pH demonstrated that the adsorption mechanism between Eu(III) and mesoporous Al(2)O(3)/EG composites would shift from outer-sphere surface complexation to inner-sphere surface complexation in terms of extended X-ray absorption fine structure spectroscopy analysis.

Spine-like Nanostructured Carbon Interconnected by Graphene for High-performance Supercapacitors

NASA Astrophysics Data System (ADS)

Park, Sang-Hoon; Yoon, Seung-Beom; Kim, Hyun-Kyung; Han, Joong Tark; Park, Hae-Woong; Han, Joah; Yun, Seok-Min; Jeong, Han Gi; Roh, Kwang Chul; Kim, Kwang-Bum

2014-08-01

Recent studies on supercapacitors have focused on the development of hierarchical nanostructured carbons by combining two-dimensional graphene and other conductive sp2 carbons, which differ in dimensionality, to improve their electrochemical performance. Herein, we report a strategy for synthesizing a hierarchical graphene-based carbon material, which we shall refer to as spine-like nanostructured carbon, from a one-dimensional graphitic carbon nanofiber by controlling the local graphene/graphitic structure via an expanding process and a co-solvent exfoliation method. Spine-like nanostructured carbon has a unique hierarchical structure of partially exfoliated graphitic blocks interconnected by thin graphene sheets in the same manner as in the case of ligaments. Owing to the exposed graphene layers and interconnected sp2 carbon structure, this hierarchical nanostructured carbon possesses a large, electrochemically accessible surface area with high electrical conductivity and exhibits high electrochemical performance.

Spine-like nanostructured carbon interconnected by graphene for high-performance supercapacitors.

PubMed

Park, Sang-Hoon; Yoon, Seung-Beom; Kim, Hyun-Kyung; Han, Joong Tark; Park, Hae-Woong; Han, Joah; Yun, Seok-Min; Jeong, Han Gi; Roh, Kwang Chul; Kim, Kwang-Bum

2014-08-19

Recent studies on supercapacitors have focused on the development of hierarchical nanostructured carbons by combining two-dimensional graphene and other conductive sp(2) carbons, which differ in dimensionality, to improve their electrochemical performance. Herein, we report a strategy for synthesizing a hierarchical graphene-based carbon material, which we shall refer to as spine-like nanostructured carbon, from a one-dimensional graphitic carbon nanofiber by controlling the local graphene/graphitic structure via an expanding process and a co-solvent exfoliation method. Spine-like nanostructured carbon has a unique hierarchical structure of partially exfoliated graphitic blocks interconnected by thin graphene sheets in the same manner as in the case of ligaments. Owing to the exposed graphene layers and interconnected sp(2) carbon structure, this hierarchical nanostructured carbon possesses a large, electrochemically accessible surface area with high electrical conductivity and exhibits high electrochemical performance.

Spine-like Nanostructured Carbon Interconnected by Graphene for High-performance Supercapacitors

PubMed Central

Park, Sang-Hoon; Yoon, Seung-Beom; Kim, Hyun-Kyung; Han, Joong Tark; Park, Hae-Woong; Han, Joah; Yun, Seok-Min; Jeong, Han Gi; Roh, Kwang Chul; Kim, Kwang-Bum

2014-01-01

Recent studies on supercapacitors have focused on the development of hierarchical nanostructured carbons by combining two-dimensional graphene and other conductive sp2 carbons, which differ in dimensionality, to improve their electrochemical performance. Herein, we report a strategy for synthesizing a hierarchical graphene-based carbon material, which we shall refer to as spine-like nanostructured carbon, from a one-dimensional graphitic carbon nanofiber by controlling the local graphene/graphitic structure via an expanding process and a co-solvent exfoliation method. Spine-like nanostructured carbon has a unique hierarchical structure of partially exfoliated graphitic blocks interconnected by thin graphene sheets in the same manner as in the case of ligaments. Owing to the exposed graphene layers and interconnected sp2 carbon structure, this hierarchical nanostructured carbon possesses a large, electrochemically accessible surface area with high electrical conductivity and exhibits high electrochemical performance. PMID:25134517

DNA Origami Reorganizes upon Interaction with Graphite: Implications for High-Resolution DNA Directed Protein Patterning

PubMed Central

Rahman, Masudur; Neff, David; Green, Nathaniel; Norton, Michael L.

2016-01-01

Although there is a long history of the study of the interaction of DNA with carbon surfaces, limited information exists regarding the interaction of complex DNA-based nanostructures with the important material graphite, which is closely related to graphene. In view of the capacity of DNA to direct the assembly of proteins and optical and electronic nanoparticles, the potential for combining DNA-based materials with graphite, which is an ultra-flat, conductive carbon substrate, requires evaluation. A series of imaging studies utilizing Atomic Force Microscopy has been applied in order to provide a unified picture of this important interaction of structured DNA and graphite. For the test structure examined, we observe a rapid destabilization of the complex DNA origami structure, consistent with a strong interaction of single-stranded DNA with the carbon surface. This destabilizing interaction can be obscured by an intentional or unintentional primary intervening layer of single-stranded DNA. Because the interaction of origami with graphite is not completely dissociative, and because the frustrated, expanded structure is relatively stable over time in solution, it is demonstrated that organized structures of pairs of the model protein streptavidin can be produced on carbon surfaces using DNA origami as the directing material. PMID:28335324

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mallow, Anne M; Abdelaziz, Omar; Graham, Samuel

The thermal charging performance of phase change materials, specifically paraffin wax, combined with compressed expanded natural graphite foam is studied under constant heat flux and constant temperature conditions. By varying the heat flux between 0.39 W/cm2 and 1.55 W/cm2 or maintaining a boundary temperature of 60 C for four graphite foam bulk densities, the impact on the rate of thermal energy storage is discussed. Thermal charging experiments indicate that thermal conductivity of the composite is an insufficient metric to compare the influence of graphite foam on the rate of thermal energy storage of the PCM composite. By dividing the latentmore » heat of the composite by the time to melt for various boundary conditions and graphite foam bulk densities, it is determined that bulk density selection is dependent on the applied boundary condition. A greater bulk density is advantageous for samples exposed to a constant temperature near the melting temperature as compared to constant heat flux conditions where a lower bulk density is adequate. Furthermore, the anisotropic nature of graphite foam bulk densities greater than 50 kg/m3 is shown to have an insignificant impact on the rate of thermal charging. These experimental results are used to validate a computational model for future use in the design of thermal batteries for waste heat recovery.« less

FRACTIONAL DISTILLATION SEPARATION OF PLUTONIUM VALUES FROM LIGHT ELEMENT VALUES

DOEpatents

Cunningham, B.B.

1957-12-17

A process is described for removing light element impurities from plutonium. It has been found that plutonium contaminated with impurities may be purified by converting the plutonium to a halide and purifying the halide by a fractional distillation whereby impurities may be distilled from the plutonium halide. A particularly effective method includes the step of forming a lower halide such as the trior tetrahalide and distilling the halide under conditions such that no decomposition of the halide occurs. Molecular distillation methods are particularly suitable for this process. The apparatus may comprise an evaporation plate with means for heating it and a condenser surface with means for cooling it. The condenser surface is placed at a distance from the evaporating surface less than the mean free path of molecular travel of the material being distilled at the pressure and temperature used. The entire evaporating system is evacuated until the pressure is about 10/sup -4/ millimeters of mercury. A high temperuture method is presented for sealing porous materials such as carbon or graphite that may be used as a support or a moderator in a nuclear reactor. The carbon body is subjected to two surface heats simultaneously in an inert atmosphere; the surface to be sealed is heated to 1500 degrees centigrade; and another surface is heated to 300 degrees centigrade, whereupon the carbon vaporizes and flows to the cooler surface where it is deposited to seal that surface. This method may be used to seal a nuclear fuel in the carbon structure.

Technological progress in sealed lead/acid batteries

NASA Astrophysics Data System (ADS)

Yamashita, J.; Nakashima, H.; Kasai, Y.

A brief review is given of the history of the research and development of sealed lead/acid batteries during the 30 years since, in 1959, the Yuasa Battery Co. introduced a small-sized sealed battery as the power supply for portable television sets. In 1965, Yuasa began the full-scale mass production and sale of a small-sized sealed lead/acid battery under the NOYPER brand. In 1970, the use of a PbCa alloy grid was adopted, and there followed the successful development of a sealed battery with an oxygen-recombination facility. In 1976, Yuasa more or less established the basic technology for the valve-regulated sealed lead/acid battery — the NP battery — which is now the type in general use. Throughout the 1980s, Yuasa, has continued development in order to expand the sphere of application for the production technology of valve-regulated batteries for motorcycles, as well as for stationary duties with large capacities of 100 to 3000 A h. Recently, in order to improve the reliability and boost the output of sealed lead/acid batteries for employment in UPS power sources, Yuasa has been working intently on the design of a valve-regulated lead/acid battery with outstanding characteristics for high-rate discharge and resistance to high temperatures.

Experimental high temperature carbon isotope fractionation involving graphite

NASA Astrophysics Data System (ADS)

Kueter, N.; Schmidt, M. W.; Lilley, M. D.; Bernasconi, S. M.

2016-12-01

Graphite/carbonate carbon isotope fractionation was mainly investigated at 400- 800°C and is based on empirical calibrations, theoretical calculations and few experiments [1,2]. Own work on COH-fluid/graphite isotope fractionation shows that in experiments up to 1000oC a fluid phase is always enriched in 13C compared to coexisting graphitic carbon. The eventual kinetic isotope effect in these experiments is best displayed by the graphitic carbon being at least 3 ‰ lighter than methane. Only few experiments done in the graphite/carbonate pair dealt with higher temperatures reaching 1400°C, indicating a fractionation of up to 2 ‰ at temperatures of the Earth's mantle [2-4]. To better understand carbon isotope fractionation in crustal systems and still overcome kinetic effects, we study the graphite/carbonatite pair with piston cylinder experiments in the Na2CO3-CaCO3-CaO-COH system. Tartaric acid (C4H6O6) supplies reduced carbon, time series are performed at 10 kbar, 1300-1800°C. Initial experiments at 1300°C produce well-ordered, micron-sized graphite flakes growing attached to the capsule walls while the Na-Ca-carbonatite-melt quenches to dendritic textures. No gaseous phase was observed. Conditions well above the liquidus of the Na2CO3-CaCO3-binary lead to dissolution of the H2O from tartaric acid decomposition in the melt, any CO2-component is bound by the excess CaO to CaCO3melt while in the relatively oxidizing capsule environment any CH4-component reacts with CO2 to carbon and H2O. The graphite and the carbonatite quench are measured for their δ13C composition using a GasBench II (carbonate-dissolution in phosphoric acid) and TC/EA (residual graphite combusted in oxygen atmosphere) system coupled to a Thermo Fischer IRMS. Our results expand from the graphite-carbonate system to graphite-fluid system when adding available fluid-carbonate fractionation factors, but are also directly applicable to diamond synthesis as graphite is often found as a precursor phase in diamond-growth experiments in carbonatite systems and natural diamonds. [1] Chacko et al. (2001) Rev Min Geochem; Deines & Eggler (2009) GCA; [3] Scheele & Hoefs (1992) CMP; [4] Chacko et al. (1991) GCA

ChEVAS: Combining Suprarenal EVAS with Chimney Technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Torella, Francesco, E-mail: f.torella@liverpool.ac.uk; Chan, Tze Y., E-mail: tze.chan@rlbuht.nhs.uk; Shaikh, Usman, E-mail: usman.shaikh@rlbuht.nhs.uk

2015-10-15

Endovascular sealing with the Nellix{sup ®} endoprosthesis (EVAS) is a new technique to treat infrarenal abdominal aortic aneurysms. We describe the use of endovascular sealing in conjunction with chimney stents for the renal arteries (chEVAS) in two patients, one with a refractory type Ia endoleak and an expanding aneurysm, and one with a large juxtarenal aneurysm unsuitable for fenestrated endovascular repair (EVAR). Both aneurysms were successfully excluded. Our report confirms the utility of chEVAS in challenging cases, where suprarenal seal is necessary. We suggest that, due to lack of knowledge on its durability, chEVAS should only been considered when moremore » conventional treatment modalities (open repair and fenestrated EVAR) are deemed difficult or unfeasible.« less

Respiratory Distress

NASA Technical Reports Server (NTRS)

1976-01-01

The University of Miami School of Medicine asked the Research Triangle Institute for assistance in improvising the negative pressure technique to relieve respiratory distress in infants. Marshall Space Flight Center and Johnson Space Center engineers adapted this idea to the lower-body negative-pressure system seals used during the Skylab missions. Some 20,000 babies succumb to respiratory distress in the U.S. each year, a condition in which lungs progressively lose their ability to oxygenate blood. Both positive and negative pressure techniques have been used - the first to force air into lungs, the second to keep infant's lungs expanded. Negative pressure around chest helps the baby expand his lungs and maintain proper volume of air. If doctors can keep the infant alive for four days, the missing substance in the lungs will usually form in sufficient quantity to permit normal breathing. The Skylab chamber and its leakproof seals were adapted for medical use.

Support services for the automative gas turbine project

NASA Technical Reports Server (NTRS)

Golec, T. (Editor)

1981-01-01

Support was provided to DOE and NASA in their efforts to inform industry, the public, and Government on the benefits and purpose of the gas turbine programs through demonstrations and exhibits. Tasks were carried out for maintenance, repair, and retrofit of the experimental gas turbine engines being used by NASA in their gas turbine technology programs and in program demonstrations. Limited support testing was conducted at Chrysler in which data were generated on air bearing rotor shaft dynamics, heavy duty variable sheave rubber belts, high temperature elastomer regenerator drive mounting and graphite regenerator seal friction characteristics.

Dynamics of face and annular seals with two-phase flow

NASA Technical Reports Server (NTRS)

Hughes, William F.; Basu, Prithwish; Beatty, Paul A.; Beeler, Richard M.; Lau, Stephen

1989-01-01

A detailed study was made of face and annular seals under conditions where boiling, i.e., phase change of the leaking fluid, occurs within the seal. Many seals operate in this mode because of flashing due to pressure drop and/or heat input from frictional heating. High pressure, water pumps, industrial chemical pumps, and cryogenic pumps are mentioned as a few of many applications. The initial motivation was the LOX-GOX seals for the space shuttle main engine, but the study was expanded to include any face or annular seal where boiling occurs. Some of the distinctive behavior characteristics of two-phase seals were discussed, particularly their axial stability. While two-phase seals probably exhibit instability to disturbances of other degrees of freedom such as wobble, etc., under certain conditions, such analyses are too complex to be treated at present. Since an all liquid seal (with parallel faces) has a neutral axial stiffness curve, and is stabilized axially by convergent coning, other degrees of freedom stability analyses are necessary. However, the axial stability behavior of the two-phase seal is always a consideration no matter how well the seal is aligned and regardless of the speed. Hence, axial stability is thought of as the primary design consideration for two-phase seals and indeed the stability behavior under sub-cooling variations probably overshadows other concerns. The main thrust was the dynamic analysis of axial motion of two-phase face seals, principally the determination of axial stiffness, and the steady behavior of two-phase annular seals. The main conclusions are that seals with two-phase flow may be unstable if improperly balanced. Detailed theoretical analyses of low (laminar) and high (turbulent) leakage seals are presented along with computer codes, parametric studies, and in particular a simplified PC based code that allows for rapid performance prediction. A simplified combined computer code for the performance prediction over the laminar and turbulent ranges of a two-phase seal is described and documented. The analyses, results, and computer codes are summarized.

A graphite calorimeter for absolute measurements of absorbed dose to water: application in medium-energy x-ray filtered beams.

PubMed

Pinto, M; Pimpinella, M; Quini, M; D'Arienzo, M; Astefanoaei, I; Loreti, S; Guerra, A S

2016-02-21

The Italian National Institute of Ionizing Radiation Metrology (ENEA-INMRI) has designed and built a graphite calorimeter that, in a water phantom, has allowed the determination of the absorbed dose to water in medium-energy x-rays with generating voltages from 180 to 250 kV. The new standard is a miniaturized three-bodies calorimeter, with a disc-shaped core of 21 mm diameter and 2 mm thickness weighing 1.134 g, sealed in a PMMA waterproof envelope with air-evacuated gaps. The measured absorbed dose to graphite is converted into absorbed dose to water by means of an energy-dependent conversion factor obtained from Monte Carlo simulations. Heat-transfer correction factors were determined by FEM calculations. At a source-to-detector distance of 100 cm, a depth in water of 2 g cm(-2), and at a dose rate of about 0.15 Gy min(-1), results of calorimetric measurements of absorbed dose to water, D(w), were compared to experimental determinations, D wK, obtained via an ionization chamber calibrated in terms of air kerma, according to established dosimetry protocols. The combined standard uncertainty of D(w) and D(wK) were estimated as 1.9% and 1.7%, respectively. The two absorbed dose to water determinations were in agreement within 1%, well below the stated measurement uncertainties. Advancements are in progress to extend the measurement capability of the new in-water-phantom graphite calorimeter to other filtered medium-energy x-ray qualities and to reduce the D(w) uncertainty to around 1%. The new calorimeter represents the first implementation of in-water-phantom graphite calorimetry in the kilovoltage range and, allowing independent determinations of D(w), it will contribute to establish a robust system of absorbed dose to water primary standards for medium-energy x-ray beams.

Polybenzimidazole (PBI) functionalized nanographene as highly stable catalyst support for polymer Electrolyte membrane fuel cells (PEMFCs)

DOE PAGES

Xin, Le; Yang, Fan; Qiu, Yang; ...

2016-08-25

Nanoscale graphenes were used as cathode catalyst supports in proton exchange membrane fuel cells (PEMFCs). Surface-initiated polymerization that covalently bonds polybenzimidazole (PBI) polymer on the surface of graphene supports enables the uniform distribution of the Pt nanoparticles, as well as allows the sealing of the unterminated carbon bonds usually present on the edge of graphene from the chemical reduction of graphene oxide. The nanographene effectively shortens the length of channels and pores for O 2 diffusion/water dissipation and significantly increases the primary pore volume. Further addition of p-phenyl sulfonic functional graphitic carbon particles as spacers, increases the specific volume ofmore » the secondary pores and greatly improves O 2 mass transport within the catalyst layers. The developed composite cathode catalyst of Pt/PBI-nanographene (50 wt%) + SO 3H-graphitic carbon black demonstrates a higher beginning of life (BOL) PEMFC performance as compared to both Pt/PBI-nanographene (50 wt%) and Pt/PBI-graphene (50 wt%) + SO 3H-graphitic carbon black (GCB). Accelerated stress tests show excellent support durability compared to that of traditional Pt/Vulcan XC72 catalysts, when subjected to 10,000 cycles from 1.0 V to 1.5 V. As a result, this study suggests the promise of using PBI-nanographene + SO 3H-GCB hybrid supports in fuel cells to achieve the 2020 DOE targets for transportation applications.« less

Theoretical Limits of Energy Density in Silicon-Carbon Composite Anode Based Lithium Ion Batteries.

PubMed

Dash, Ranjan; Pannala, Sreekanth

2016-06-17

Silicon (Si) is under consideration as a potential next-generation anode material for the lithium ion battery (LIB). Experimental reports of up to 40% increase in energy density of Si anode based LIBs (Si-LIBs) have been reported in literature. However, this increase in energy density is achieved when the Si-LIB is allowed to swell (volumetrically expand) more than graphite based LIB (graphite-LIB) and beyond practical limits. The volume expansion of LIB electrodes should be negligible for applications such as automotive or mobile devices. We determine the theoretical bounds of Si composition in a Si-carbon composite (SCC) based anode to maximize the volumetric energy density of a LIB by constraining the external dimensions of the anode during charging. The porosity of the SCC anode is adjusted to accommodate the volume expansion during lithiation. The calculated threshold value of Si was then used to determine the possible volumetric energy densities of LIBs with SCC anode (SCC-LIBs) and the potential improvement over graphite-LIBs. The level of improvement in volumetric and gravimetric energy density of SCC-LIBs with constrained volume is predicted to be less than 10% to ensure the battery has similar power characteristics of graphite-LIBs.

Unique Tuft Test Facility Dramatically Reduces Brush Seal Development Costs

NASA Technical Reports Server (NTRS)

Fellenstein, James A.

1997-01-01

Brush seals have been incorporated in the latest turbine engines to reduce leakage and improve efficiency. However, the life of these seals is limited by wear. Studies have shown that optimal sealing characteristics for a brush seal occur before the interference fit between the brush and shaft is excessively worn. Research to develop improved tribopairs (brush and coating) with reduced wear and lower friction has been hindered by the lack of an accurate, low-cost, efficient test methodology. Estimated costs for evaluating a new material combination in an engine company seal test program are on the order of $100,000. To address this need, the NASA Lewis Research Center designed, built, and validated a unique, innovative brush seal tuft tester that slides a single tuft of brush seal wire against a rotating shaft under controlled loads, speeds, and temperatures comparable to those in turbine engines. As an initial screening tool, the brush seal tuft tester can tribologicaly evaluate candidate seal materials for 1/10th the cost of full-scale seal tests. Previous to the development of the brush seal tuft tester facility, most relevant tribological data had been obtained from full-scale seal tests conducted primarily to determine seal leakage characteristics. However, from a tribological point of view, these tests included the confounding effects of varying contact pressures, bristle flaring, high-temperature oxidation, and varying bristle contact angles. These confounding effects are overcome in tuft testing. The interface contact pressures can be either constant or varying depending on the tuft mounting device, and bristle wear can be measured optically with inscribed witness marks. In a recent cooperative program with a U.S. turbine engine manufacturer, five metallic wire candidates were tested against a plasma-sprayed Nichrome-bonded chrome carbide. The wire materials used during this collaboration were either nickel-chrome- or cobaltchrome-based superalloys. These tests corroborated full-scale seal test results and provided insight into previously untested combinations. As the cycle temperature for improved efficiency turbine engines increases, new brush seal materials combinations must be considered. Future brush seal tuft testing will include both metallic and ceramic bristles versus commercial and NASA-developed shaft coatings. The ultimate goal of this work is to expand the current data base so that seal designers can tailor brush seal materials to specific applications.

Si@SiOx/Graphene nanosheet anode materials for lithium-ion batteries synthesized by ball milling process

NASA Astrophysics Data System (ADS)

Tie, Xiaoyong; Han, Qianyan; Liang, Chunyan; Li, Bo; Zai, Jiantao; Qian, Xuefeng

2017-12-01

Si@SiOx/Graphene nanosheet (GNS) nanocomposites as high performance anode materials for lithium-ion batteries are synthesized by mechanically blending the mixture of expanded graphite with Si nanoparticles, and characterized by X-ray diffraction, Raman spectrum, field emission scanning electron microscopy and transmission electron microscopy. During the ball milling process, the size of Si nanoparticles will decrease, and the layer of expanded graphite can be peeled off to thin multilayers. Electrochemical performances reveal that the obtained Si@SiOx/GNS nanocomposites exhibit improved cycling stability, high reversible lithium storage capacity and superior rate capability, e.g. the discharge capacity is kept as high as 1055 mAh g-1 within 50 cycles at a current density of 200 mA g-1, retaining 63.6% of the initial value. The high performance of the obtained nanocomposites can be ascribed to GNS prepared through heat-treat and ball-milling methods, the decrease in the size of Si nanoparticles and SiOx layer on Si surface, which enhance the interactions between Si and GNS.

High performance asymmetric supercapacitor based on molybdenum disulphide/graphene foam and activated carbon from expanded graphite.

PubMed

Masikhwa, Tshifhiwa M; Madito, Moshawe J; Bello, Abdulhakeem; Dangbegnon, Julien K; Manyala, Ncholu

2017-02-15

Molybdenum disulphide which has a graphene-like single layer structure has excellent mechanical and electrical properties and unique morphology, which might be used with graphene foam as composite in supercapacitor applications. In this work, Molybdenum disulphide (MoS 2 )/graphene foam (GF) composites with different graphene foam loading were synthesized by the hydrothermal process to improve on specific capacitance of the composites. Asymmetric supercapacitor device was fabricated using the best performing MoS 2 /GF composite and activated carbon derived from expanded graphite (AEG) as positive and negative electrodes, respectively, in 6M KOH electrolyte. The asymmetric MoS 2 /GF//AEG device exhibited a maximum specific capacitance of 59Fg -1 at a current density of 1Ag -1 with maximum energy and power densities of 16Whkg -1 and 758Wkg -1 , respectively. The supercapacitor also exhibited a good cyclic stability with 95% capacitance retention over 2000 constant charge-discharge cycles. The results obtained demonstrate the potential of MoS 2 /GF//AEG as a promising material for electrochemical energy storage application. Copyright © 2016 Elsevier Inc. All rights reserved.

Thermal Characterization of Lauric-Stearic Acid/Expanded Graphite Eutectic Mixture as Phase Change Materials.

PubMed

Zhu, Hua; Zhang, Peng; Meng, Zhaonan; Li, Ming

2015-04-01

The eutectic mixture of lauric acid (LA) and stearic acid (SA) is a desirable phase change material (PCM) due to the constant melting temperature and large latent heat. However, its poor thermal conductivity has hampered its broad utilization. In the present study, pure LA, SA and the mixtures with various mass fractions of LA-SA were used as the basic PCMs, and 10 wt% expanded graphite (EG) was added to enhance the thermal conductivities. The phase change behaviors, microstructural analysis, thermal conductivities and thermal stabilities of the mixtures of PCMs were investigated by differential scanning calorimetry (DSC), scanning electronic microscope (SEM), transient plane source (TPS) and thermogravimetric analysis (TGA), respectively. The results show that the LA-SA binary mixture of mixture ratio of 76.3 wt%: 23.7 wt% forms an eutectic mixture, which melts at 38.99 °C and has a latent heat of 159.94 J/g. The melted fatty acids are well absorbed by the porous network of EG and they have a good thermal stability. Furthermore, poor thermal conductivities can be well enhanced by the addition of EG.

Novel application of thermally expanded graphite as the support of catalysts for direct synthesis of DMC from CH3OH and CO2.

PubMed

Bian, J; Xiao, M; Wang, S J; Lu, Y X; Meng, Y Z

2009-06-01

Novel Cu-Ni bimetallic catalysts supported on thermally expanded graphite (TEG) were prepared as an example to show the particular characteristics of TEG as a carbon support material. The structures of TEG and the synthesized Cu-Ni/TEG catalysts were characterized using BET, FTIR, TG, SEM, TEM, XRD and TPR techniques. The catalytic activities of the prepared catalysts were investigated by performing micro-reaction in the direct synthesis of dimethyl carbonate (DMC) from CH3OH and CO2. The experimental results indicated that the prepared Cu-Ni/TEG catalysts exhibited highly catalytic activity. Under the optimal catalytic conditions at 100 degrees C and under 1.2 MPa, the highest conversion of CH3OH of 4.97% and high selectivity of DMC of 89.3% can be achieved. The highly catalytic activity of Cu-Ni/TEG in DMC synthesis can be attributed to the synergetic effects of metal Cu, Ni and Cu-Ni alloy in the activation of CH3OH and CO2 and the particular characteristics of TEG as a carbon support material.

Microrobot with passive diamagnetic levitation for microparticle manipulations

NASA Astrophysics Data System (ADS)

Feng, Lin; Zhang, Shengyuan; Jiang, Yonggang; Zhang, Deyuan; Arai, Fumihito

2017-12-01

In this paper, an innovative microrobot with passive diamagnetic levitation is presented. Based on theoretical analysis, finite element method simulation, and experiments, the shape of pyrolytic graphite is redesigned, which improves the stability of passive diamagnetic levitation significantly. Therefore, passive diamagnetic levitation is able to be applied for 3-D control of the microrobot. Compared with the traditional microrobots driven by permanent magnets in a microfluidic chip, the microrobot made of pyrolytic graphite and driven by magnetic force has two advantages, no friction and 3-D control, which is able to expand the scope of the microrobot applications. Finally, the microrobot with passive diamagnetic levitation was demonstrated by being encapsulated in a microfluidic chip for microparticle manipulations.

Trapped rubber processing for advanced composites

NASA Technical Reports Server (NTRS)

Marra, P. J.

1976-01-01

Trapped rubber processing is a molding technique for composites in which precast silicone rubber is placed within a closed cavity where it thermally expands against the composite's surface supported by the vessel walls. The method has been applied by the Douglas Aircraft Company, under contract to NASA-Langley, to the design and fabrication of 10 DC-10 graphite/epoxy upper aft rudder assemblies. A three-bay development tool form mold die has been designed and manufactured, and tooling parameters have been established. Fabrication procedures include graphite layup, assembly of details in the tool, and a cure cycle. The technique has made it possible for the cocured fabrication of complex primary box structures otherwise impracticable via standard composite material processes.

Solidification Using a Baffle in Sealed Ampoules (SUBSA)

NASA Technical Reports Server (NTRS)

Marin, C.; Ostrogorsky, A. G.; Volz, M.; Luz, P.; Jeter, L.; Spivey, R.; Burton, H.; Smith, G.; Knowles, T. R.; Bonner, W. A.

2003-01-01

Solidification Using a Baffle in Sealed Ampoules (SUBSA) will be the first materials science experiment conducted in the Microgravity Science Glovebox (MSG) Facility at the International Space Station (ISS) Alpha. The launch is schedule for May 31, 2002. Using the specially developed furnace, 10 Te and Zn-doped single crystals of InSb will be directionally solidified in microgravity. A key goal of the SUBSA investigation is to (i) clarify the origin of the melt motion in space laboratories and (ii) to reduce the magnitude of the melt motion to the point that it does not interfere with the transport phenomena. These goals will be accomplished through a special ampoule and furnace design. A disk-shaped baffle, positioned close to the freezing front, is used to reduce melt motion. Furthermore, the solidification will be visualized by using a transparent furnace, with a video camera, continuously sending images to the earth. This allows detection of bubbles and melt de-wetting that could cause surface tension driven convection. In preparation for the space experiments, 30 ground-based experiments were conducted. The results of ground based tests and numerical modeling will be presented. Based on numerical modeling, 12 mm 1D silica ampoules were selected. The small diameter ampoule favors closer placement of the baffle to the interface, without excessive radial segregation caused by forced convection while providing more damping of natural convection. The parts in the silica ampoule include 2 carbon springs made by Energy Science Laboratories, Inc., a pyrocarbon-coated graphite cylinder, pyrocarbon-coated graphite a baffle with the shaft and the InSb charge with the seed crystal grown by W.A. Bonner of Crystallod Inc.

Lightweight bladder lined pressure vessels

DOEpatents

Mitlitsky, Fred; Myers, Blake; Magnotta, Frank

1998-01-01

A lightweight, low permeability liner for graphite epoxy composite compressed gas storage vessels. The liner is composed of polymers that may or may not be coated with a thin layer of a low permeability material, such as silver, gold, or aluminum, deposited on a thin polymeric layer or substrate which is formed into a closed bladder using torispherical or near torispherical end caps, with or without bosses therein, about which a high strength to weight material, such as graphite epoxy composite shell, is formed to withstand the storage pressure forces. The polymeric substrate may be laminated on one or both sides with additional layers of polymeric film. The liner may be formed to a desired configuration using a dissolvable mandrel or by inflation techniques and the edges of the film seamed by heat sealing. The liner may be utilized in most any type of gas storage system, and is particularly applicable for hydrogen, gas mixtures, and oxygen used for vehicles, fuel cells or regenerative fuel cell applications, high altitude solar powered aircraft, hybrid energy storage/propulsion systems, and lunar/Mars space applications, and other applications requiring high cycle life.

Method for forming a bladder for fluid storage vessels

DOEpatents

Mitlitsky, Fred; Myers, Blake; Magnotta, Frank

2000-01-01

A lightweight, low permeability liner for graphite epoxy composite compressed gas storage vessels. The liner is composed of polymers that may or may not be coated with a thin layer of a low permeability material, such as silver, gold, or aluminum, deposited on a thin polymeric layer or substrate which is formed into a closed bladder using torispherical or near torispherical end caps, with or without bosses therein, about which a high strength to weight material, such as graphite epoxy composite shell, is formed to withstand the storage pressure forces. The polymeric substrate may be laminated on one or both sides with additional layers of polymeric film. The liner may be formed to a desired configuration using a dissolvable mandrel or by inflation techniques and the edges of the film seamed by heat sealing. The liner may be utilized in most any type of gas storage system, and is particularly applicable for hydrogen, gas mixtures, and oxygen used for vehicles, fuel cells or regenerative fuel cell applications, high altitude solar powered aircraft, hybrid energy storage/propulsion systems, and lunar/Mars space applications, and other applications requiring high cycle life.

Well sealing via thermite reactions

DOEpatents

Lowry, William Edward; Dunn, Sandra Dalvit

2016-11-15

A platform is formed in a well below a target plug zone by lowering a thermite reaction charge into the well and igniting it, whereby the products of the reaction are allowed to cool and expand to form a platform or support in the well. A main thermite reaction charge is placed above the platform and ignited to form a main sealing plug for the well. In some embodiments an upper plug is formed by igniting an upper thermite reaction charge above the main thermite reaction charge. The upper plug confines the products of ignition of the main thermite reaction charge.

Ultra low friction carbon/carbon composites for extreme temperature applications

DOEpatents

Erdemir, Ali; Busch, Donald E.; Fenske, George R.; Lee, Sam; Shepherd, Gary; Pruett, Gary J.

2001-01-01

A carbon/carbon composite in which a carbon matrix containing a controlled amount of boron or a boron compound is reinforced with carbon fiber exhibits a low coefficient of friction, i.e., on the order of 0.04 to 0.1 at temperatures up to 600.degree. C., which is one of the lowest frictional coefficients for any type of carbonaceous material, including graphite, glassy carbon, diamond, diamond-like carbon and other forms of carbon material. The high degree of slipperiness of the carbon composite renders it particularly adapted for limiting friction and wear at elevated temperatures such as in seals, bearings, shafts, and flexible joints

Frangible electrochemical cell and sealing technique

NASA Technical Reports Server (NTRS)

Halpert, G.; Haynos, J.; Sherfey, J.

1969-01-01

Electrochemical cell assembly, which includes a positive electrode plate between two negative electrode plates, is both flexible and compact, and frangible under severe shock conditions. Leak-tight integrity of the housing is maintained by polymer-to-polymer fusion bonds through holes in the expanded metal electrode terminals.

Expanding Actin Rings Zipper the Mouse Embryo for Blastocyst Formation.

PubMed

Zenker, Jennifer; White, Melanie D; Gasnier, Maxime; Alvarez, Yanina D; Lim, Hui Yi Grace; Bissiere, Stephanie; Biro, Maté; Plachta, Nicolas

2018-04-19

Transformation from morula to blastocyst is a defining event of preimplantation embryo development. During this transition, the embryo must establish a paracellular permeability barrier to enable expansion of the blastocyst cavity. Here, using live imaging of mouse embryos, we reveal an actin-zippering mechanism driving this embryo sealing. Preceding blastocyst stage, a cortical F-actin ring assembles at the apical pole of the embryo's outer cells. The ring structure forms when cortical actin flows encounter a network of polar microtubules that exclude F-actin. Unlike stereotypical actin rings, the actin rings of the mouse embryo are not contractile, but instead, they expand to the cell-cell junctions. Here, they couple to the junctions by recruiting and stabilizing adherens and tight junction components. Coupling of the actin rings triggers localized myosin II accumulation, and it initiates a tension-dependent zippering mechanism along the junctions that is required to seal the embryo for blastocyst formation. Copyright © 2018 Elsevier Inc. All rights reserved.

Highly Thermal Conductive Nanocomposites

NASA Technical Reports Server (NTRS)

Sun, Ya-Ping (Inventor); Connell, John W. (Inventor); Veca, Lucia Monica (Inventor)

2015-01-01

Disclosed are methods for forming carbon-based fillers as may be utilized in forming highly thermal conductive nanocomposite materials. Formation methods include treatment of an expanded graphite with an alcohol/water mixture followed by further exfoliation of the graphite to form extremely thin carbon nanosheets that are on the order of between about 2 and about 10 nanometers in thickness. Disclosed carbon nanosheets can be functionalized and/or can be incorporated in nanocomposites with extremely high thermal conductivities. Disclosed methods and materials can prove highly valuable in many technological applications including, for instance, in formation of heat management materials for protective clothing and as may be useful in space exploration or in others that require efficient yet light-weight and flexible thermal management solutions.

Highly Thermal Conductive Nanocomposites

NASA Technical Reports Server (NTRS)

Sun, Ya-Ping (Inventor); Connell, John W. (Inventor); Veca, Lucia Monica (Inventor)

2017-01-01

Disclosed are methods for forming carbon-based fillers as may be utilized in forming highly thermal conductive nanocomposite materials. Formation methods include treatment of an expanded graphite with an alcohol/water mixture followed by further exfoliation of the graphite to form extremely thin carbon nanosheets that are on the order of between about 2 and about 10 nanometers in thickness. Disclosed carbon nanosheets can be functionalized and/or can be incorporated in nanocomposites with extremely high thermal conductivities. Disclosed methods and materials can prove highly valuable in many technological applications including, for instance, in formation of heat management materials for protective clothing and as may be useful in space exploration or in others that require efficient yet light-weight and flexible thermal management solutions.

Theoretical Limits of Energy Density in Silicon-Carbon Composite Anode Based Lithium Ion Batteries

PubMed Central

Dash, Ranjan; Pannala, Sreekanth

2016-01-01

Silicon (Si) is under consideration as a potential next-generation anode material for the lithium ion battery (LIB). Experimental reports of up to 40% increase in energy density of Si anode based LIBs (Si-LIBs) have been reported in literature. However, this increase in energy density is achieved when the Si-LIB is allowed to swell (volumetrically expand) more than graphite based LIB (graphite-LIB) and beyond practical limits. The volume expansion of LIB electrodes should be negligible for applications such as automotive or mobile devices. We determine the theoretical bounds of Si composition in a Si–carbon composite (SCC) based anode to maximize the volumetric energy density of a LIB by constraining the external dimensions of the anode during charging. The porosity of the SCC anode is adjusted to accommodate the volume expansion during lithiation. The calculated threshold value of Si was then used to determine the possible volumetric energy densities of LIBs with SCC anode (SCC-LIBs) and the potential improvement over graphite-LIBs. The level of improvement in volumetric and gravimetric energy density of SCC-LIBs with constrained volume is predicted to be less than 10% to ensure the battery has similar power characteristics of graphite-LIBs. PMID:27311811

Pinniped Hearing in Complex Acoustic Environments

DTIC Science & Technology

2012-09-30

Piedras Blancas, is located just north of Cambria, California and is quickly expanding as one of the largest northern elephant seal colonies along the...acoustically sampled at the Año Nuevo breeding colony, and 46 individuals were similarly studied at the Piedras Blancas breeding colony during the 2011-12

How Many Seals Were There? The Global Shelf Loss during the Last Glacial Maximum and Its Effect on the Size and Distribution of Grey Seal Populations

PubMed Central

Boehme, Lars; Thompson, Dave; Fedak, Mike; Bowen, Don; Hammill, Mike O.; Stenson, Garry B.

2012-01-01

Predicting how marine mammal populations respond to habitat changes will be essential for developing conservation management strategies in the 21st century. Responses to previous environmental change may be informative in the development of predictive models. Here we describe the likely effects of the last ice age on grey seal population size and distribution. We use satellite telemetry data to define grey seal foraging habitat in terms of the temperature and depth ranges exploited by the contemporary populations. We estimate the available extent of such habitat in the North Atlantic at present (between 1.42·106 km2 and 2.07·106 km2) and at the last glacial maximum (between 4.74·104 km2 and 2.11·105 km2); taking account of glacial and seasonal sea-ice coverage, estimated reductions of sea-level (123 m) and sea surface temperature hind-casts. Most of the extensive continental shelf waters (North Sea, Baltic Sea and Scotian Shelf), currently supporting >95% of grey seals, were unavailable during the last glacial maximum. A combination of lower sea-level and extensive ice-sheets, massively increased seasonal sea-ice coverage and southerly extent of cold water would have pushed grey seals into areas with no significant shelf waters. The habitat during the last glacial maximum might have been as small as 3% of today's extent and grey seal populations may have fallen to similarly low numbers. An alternative scenario involving a major change to a pelagic or bathy-pelagic foraging niche cannot be discounted. However, hooded seals currently dominate that niche and may have excluded grey seals from such habitat. If as seems likely, the grey seal population fell to very low levels it would have remained low for several thousand years before expanding into current habitats over the past 12,000 years or so. PMID:23300843

Grease-Resistant O Rings for Joints in Solid Rocket Motors

NASA Technical Reports Server (NTRS)

Harvey, Albert R.; Feldman, Harold

2003-01-01

There is a continuing effort to develop improved O rings for sealing joints in solid-fuel rocket motors. Following an approach based on the lessons learned in the explosion of the space shuttle Challenger, investigators have been seeking O-ring materials that exhibit adequate resilience for effective sealing over a broad temperature range: What are desired are O rings that expand far and fast enough to maintain seals, even when metal sealing surfaces at a joint move slightly away from each other shortly after ignition and the motor was exposed to cold weather before ignition. Other qualities desired of the improved O rings include adequate resistance to ablation by hot rocket gases and resistance to swelling when exposed to hydrocarbon-based greases used to protect some motor components against corrosion. Five rubber formulations two based on a fluorosilicone polymer and three based on copolymers of epichlorohydrin with ethylene oxide were tested as candidate O-ring materials. Of these, one of the epichlorohydrin/ethylene oxide formulations was found to offer the closest to the desired combination of properties and was selected for further evaluation.

Collaboration and Commitment to Sealed Source Safety, Security, and Disposition - 13627

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jennison, Meaghan; Martin, David W.

2013-07-01

EnergySolutions, the Division of Radiation Control at the Utah Department of Environmental Quality (UDEQ), the Conference of Radiation Control Program Directors (CRCPD), and the Department of Energy's Global Threat Reduction Initiative (GTRI) are collaborating on a truly innovative effort to expand opportunities for cost-effective sealed source disposal. These entities have developed a first-of-its-kind initiative to dispose of certain sealed sources at the EnergySolutions disposal facility near Clive, Utah, which normally cannot accept sealed sources of any type. This creative and collaborative effort to improve radiation health, safety, and security exemplifies the spirit and commitment represented by the Richard S. Hodes,more » M.D. Honor Lecture Award, which is presented annually at the Waste Management Symposia by the Southeast Compact Commission to encourage environmental professionals and political leaders to develop innovative approaches to waste management in the United States. The participants in the collaborative initiative are honored to receive special recognition for their efforts thus far. They also recognize that the hard work remains to be done. (authors)« less

Underground gas storage in the Leyden lignite mine

DOE Office of Scientific and Technical Information (OSTI.GOV)

Meddles, R.M.

1978-01-01

Underground gas storage in the Leyden lignite mine by Public Service Co. of Colorado was preceded by careful studies of mine records with respect to geologic conditions and investigation of the gas-sealing potential of the rocks surrounding the cavern. The water level in shaft No. 3 in Sept. 1958 was about 100 ft above the coal seam at that point. Wells were drilled into the mine up-dip (east) of the structurally highest point that a mine shaft intersected the coal seams, and gas was injected into the mine, using the mine water as a seal. At least the up-dip partmore » of the mine was gas-tight, and tests were expanded to the rest of the mine, which also proved to be gas-tight. All that remained to complete the preparation of the mine for permanent gas storage was sealing of the old mine shafts.« less

Effects of nano-sized boron nitride (BN) reinforcement in expandable graphite based in-tumescent fire retardant coating

NASA Astrophysics Data System (ADS)

Zulkurnain, E. S.; Ahmad, F.; Gillani, Q. F.

2016-08-01

The purpose of in-tumescent fire retardant coating (IFRC) is to protect substrate from fire attack by limiting heat transfer. A range of coating formulations have been prepared using Bisphenol A epoxy resin BE-188 and polyamide solidifier H-2310 as two-part binder, ammonium polyphosphate (APP) as acid source, melamine (MEL) as the blowing agent, expandable graphite (EG) as carbon source and nano-boron nitride (BN) as inorganic nano filler. The filler was used to improve the performances of the APP-EG-MEL coating. The effects of nano-BN on the char morphology and thermal degradation were investigated by fire test, thermo gravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), X- ray photoelectron spectroscopy (XPS) and field emission scanning electron microscopy (FESEM). The results showed that by substituting or reinforcing of 4% weight percentage of nano-BN, residual weight of the char increases by 23.82% compared to APP-EG-MEL coating without filler. Higher carbon content was obtained in the char and a more compact char was produced. The results indicated that nano-BN could be used as a filler to improve thermal stability of the APP-EG-MEL coating.

Adsorption isotherm, kinetic and mechanism of expanded graphite for sulfadiazine antibiotics removal from aqueous solutions.

PubMed

Zhang, Ling; Wang, Yong; Jin, SuWan; Lu, QunZan; Ji, Jiang

2017-10-01

The adsorption of sulfadiazine from water by expanded graphite (EG), a low cost and environmental-friendly adsorbent, was investigated. Several adsorption parameters (including the initial sulfadiazine concentration, contact time, pH of solution, ionic strength and temperature) were studied. Results of equilibrium experiments indicated that adsorption of sulfadiazine onto EG were better described by the Langmuir and Tempkin models than by the Freundlich model. The maximum adsorption capacity is calculated to be 16.586 mg/g at 298 K. The kinetic data were analyzed by pseudo-first-order, pseudo-second-order and intraparticle models. The results indicated that the adsorption process followed pseudo-second-order kinetics and may be controlled by two steps. Moreover, the pH significantly influenced the adsorption process, with the relatively high adsorption capacity at pH 2-10. The electrostatic and hydrophobic interactions are manifested to be two main mechanisms for sulfadiazine adsorption of EG. Meanwhile, the ionic concentration of Cl - slightly impacted the removal of sulfadiazine. Results of thermodynamics analysis showed spontaneous and exothermic nature of sulfadiazine adsorption on EG. In addition, regeneration experiments imply that the saturated EG could be reused for sulfadiazine removal by immersing sodium hydroxide.

Rotordynamic Instability Problems in High-Performance Turbomachinery, 1990

NASA Technical Reports Server (NTRS)

1991-01-01

The present workshop continues to report field experience and experimental results, and it expands the use of computational and control techniques with the integration of damper, bearing, and eccentric seal operation results. The intent of the workshop was to provide a continuing impetus for an understanding and resolution of these problems.

Cost-effective use of liquid nitrogen in cryogenic wind tunnels, phase 2

NASA Technical Reports Server (NTRS)

Mcintosh, Glen E.; Lombard, David S.; Leonard, Kenneth R.; Morhorst, Gerald D.

1990-01-01

Cryogenic seal tests were performed and Rulon A was selected for the subject nutating positive displacement expander. A four-chamber expander was designed and fabricated. A nitrogen reliquefier flow system was also designed and constructed for testing the cold expander. Initial tests were unsatisfactory because of high internal friction attributed to nutating Rulon inlet and outlet valve plates. Replacement of the nutating valves with cam-actuated poppet valves improved performance. However, no net nitrogen reliquefaction was achieved due to high internal friction. Computer software was developed for accurate calculation of nitrogen reliquefaction from a system such as that proposed. These calculations indicated that practical reliquefaction rates of 15 to 19 percent could be obtained. Due to mechanical problems, the nutating expander did not demonstrate its feasibility nor that of the system. It was concluded that redesign and testing of a smaller nutating expander was required to prove concept feasibility.

Internally folded expanded metal electrode for battery construction

NASA Technical Reports Server (NTRS)

Pierce, Doug C. (Inventor); Korinek, Paul D. (Inventor); Morgan, Maurice C. (Inventor)

1993-01-01

A battery system is disclosed which includes folded grids of expanded metal inserted through non-conductive substrates and pasted with electrochemically active materials. In the most preferred embodiment, a frame is provided with a plastic insert, and slots are provided in the latter to receive the expanded metal grid. After suitable coinage of the grid and insertion through the plastic film, the grid is sealed and pasted on opposite sides with positive and negative active material. A battery is assembled using one or a plurality of the resulting electrode elements, with separators, to produce a high-power, lead-acid battery. The folded grid provides many of the design benefits of standard bipolar construction.

Heat transfer device

NASA Technical Reports Server (NTRS)

Kalkbrenner, R. W. (Inventor)

1974-01-01

A heat transfer device is characterized by an hermetically sealed tubular housing including a tubular shell terminating in spaced end plates, and a tubular mesh wick concentrically arranged and operatively supported within said housing. The invention provides an improved wicking restraint formed as an elongated and radially expanded tubular helix concentrically related to the wick and adapted to be axially foreshortened and radially expanded into engagement with the wick in response to an axially applied compressive load. The wick is continuously supported in a contiguous relationship with the internal surfaces of the shell.

Pre-conceptual Development and characterization of an extruded graphite composite fuel for the TREAT Reactor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Luther, Erik; Rooyen, Isabella van; Leckie, Rafael

2015-03-01

In an effort to explore fuel systems that are more robust under accident scenarios, the DOE-NE has identified the need to resume transient testing. The Transient Reactor Test (TREAT) facility has been identified as the preferred option for the resumption of transient testing of nuclear fuel in the United States. In parallel, NNSA’s Global Threat Reduction Initiative (GTRI) Convert program is exploring the needs to replace the existing highly enriched uranium (HEU) core with low enriched uranium (LEU) core. In order to construct a new LEU core, materials and fabrication processes similar to those used in the initial core fabricationmore » must be identified, developed and characterized. In this research, graphite matrix fuel blocks were extruded and materials properties of were measured. Initially the extrusion process followed the historic route; however, the project was expanded to explore methods to increase the graphite content of the fuel blocks and explore modern resins. Materials properties relevant to fuel performance including density, heat capacity and thermal diffusivity were measured. The relationship between process defects and materials properties will be discussed.« less

An investigation of lithium-ion battery thermal management using paraffin/porous-graphite-matrix composite

NASA Astrophysics Data System (ADS)

Greco, Angelo; Jiang, Xi; Cao, Dongpu

2015-03-01

The thermal management of a cylindrical battery cell by a phase change material (PCM)/compressed expanded natural graphite (CENG) is investigated in this study. The transient thermal behaviour of both the battery and the PCM/CENG is described with a simplified one-dimensional model taking into account the physical and phase change properties of the PCM/CENG composite. The 1D analytical/computational model yielded nearly identical results to the three-dimensional simulation results for various cooling strategies. Therefore, the 1D model is sufficient to describe the transient behaviour of the battery cooled by a PCM/CENG composite. Moreover, the maximum temperature reached by the PCM/CENG cooling strategy is much lower than that by the forced convection in the same configuration. In the test case studied, the PCM showed superior transient characteristics to forced convection cooling. The PCM cooling is able to maintain a lower maximum temperature during the melting process and to extend the transient time for temperature rise. Furthermore, the graphite-matrix bulk density is identified as an important parameter for optimising the PCM/CENG cooling strategy.

Development of a high temperature storage unit for integration with solar dynamic systems

NASA Astrophysics Data System (ADS)

Staehle, H. J.; Lindner, F.

1989-08-01

Lithium fluoride in its capacity as a suitable energy storage material is investigated. Energy is stored as latent heat by melting the LiF. The energy is later released during recrystallization of the salt. Drawbacks to this system are described. The high corrosivity in molten state may lead to container failure in long term use. In order to avoid destruction of canisters, a graphite container is developed as graphite is not wetted by liquid LiF and thus does not suffer any corrosion. In order to match the mechanical forces caused by the volume increase during melting, a channel-like internal structure is tested. The melt formed first can expand into these channels and no pressure is built up. The results of these tests are presented.

Enhanced low-temperature lithium storage performance of multilayer graphene made through an improved ionic liquid-assisted synthesis

NASA Astrophysics Data System (ADS)

Raccichini, Rinaldo; Varzi, Alberto; Chakravadhanula, Venkata Sai Kiran; Kübel, Christian; Balducci, Andrea; Passerini, Stefano

2015-05-01

The electrochemical properties of graphene are strongly depending on its synthesis. Between the different methods proposed so far, liquid phase exfoliation turns out to be a promising method for the production of graphene. Unfortunately, the low yield of this technique, in term of solid material obtained, still limit its use to small scale applications. In this article we propose a low cost and environmentally friendly method for producing multilayer crystalline graphene with high yield. Such innovative approach, involving an improved ionic liquid assisted, microwave exfoliation of expanded graphite, allows the production of graphene with advanced lithium ion storage performance, for the first time, at low temperatures (<0 °C), as low as -30 °C, with respect to commercially available graphite.

Microfabricated triggered vacuum switch

DOEpatents

Roesler, Alexander W [Tijeras, NM; Schare, Joshua M [Albuquerque, NM; Bunch, Kyle [Albuquerque, NM

2010-05-11

A microfabricated vacuum switch is disclosed which includes a substrate upon which an anode, cathode and trigger electrode are located. A cover is sealed over the substrate under vacuum to complete the vacuum switch. In some embodiments of the present invention, a metal cover can be used in place of the trigger electrode on the substrate. Materials used for the vacuum switch are compatible with high vacuum, relatively high temperature processing. These materials include molybdenum, niobium, copper, tungsten, aluminum and alloys thereof for the anode and cathode. Carbon in the form of graphitic carbon, a diamond-like material, or carbon nanotubes can be used in the trigger electrode. Channels can be optionally formed in the substrate to mitigate against surface breakdown.

Harbor seals (Phoca vitulina) can perceive optic flow under water.

PubMed

Gläser, Nele; Mauck, Björn; Kandil, Farid I; Lappe, Markus; Dehnhardt, Guido; Hanke, Frederike D

2014-01-01

Optic flow, the pattern of apparent motion elicited on the retina during movement, has been demonstrated to be widely used by animals living in the aerial habitat, whereas underwater optic flow has not been intensively studied so far. However optic flow would also provide aquatic animals with valuable information about their own movement relative to the environment; even under conditions in which vision is generally thought to be drastically impaired, e. g. in turbid waters. Here, we tested underwater optic flow perception for the first time in a semi-aquatic mammal, the harbor seal, by simulating a forward movement on a straight path through a cloud of dots on an underwater projection. The translatory motion pattern expanded radially out of a singular point along the direction of heading, the focus of expansion. We assessed the seal's accuracy in determining the simulated heading in a task, in which the seal had to judge whether a cross superimposed on the flow field was deviating from or congruent with the actual focus of expansion. The seal perceived optic flow and determined deviations from the simulated heading with a threshold of 0.6 deg of visual angle. Optic flow is thus a source of information seals, fish and most likely aquatic species in general may rely on for e. g. controlling locomotion and orientation under water. This leads to the notion that optic flow seems to be a tool universally used by any moving organism possessing eyes.

Harbor Seals (Phoca vitulina) Can Perceive Optic Flow under Water

PubMed Central

Gläser, Nele; Mauck, Björn; Kandil, Farid I.; Lappe, Markus; Dehnhardt, Guido; Hanke, Frederike D.

2014-01-01

Optic flow, the pattern of apparent motion elicited on the retina during movement, has been demonstrated to be widely used by animals living in the aerial habitat, whereas underwater optic flow has not been intensively studied so far. However optic flow would also provide aquatic animals with valuable information about their own movement relative to the environment; even under conditions in which vision is generally thought to be drastically impaired, e. g. in turbid waters. Here, we tested underwater optic flow perception for the first time in a semi-aquatic mammal, the harbor seal, by simulating a forward movement on a straight path through a cloud of dots on an underwater projection. The translatory motion pattern expanded radially out of a singular point along the direction of heading, the focus of expansion. We assessed the seal's accuracy in determining the simulated heading in a task, in which the seal had to judge whether a cross superimposed on the flow field was deviating from or congruent with the actual focus of expansion. The seal perceived optic flow and determined deviations from the simulated heading with a threshold of 0.6 deg of visual angle. Optic flow is thus a source of information seals, fish and most likely aquatic species in general may rely on for e. g. controlling locomotion and orientation under water. This leads to the notion that optic flow seems to be a tool universally used by any moving organism possessing eyes. PMID:25058490

In-SITU, Time-resolved Raman Spectro-micro-topography of an Operating Lithium Ion Battery

NASA Technical Reports Server (NTRS)

Luo, Yu; Cai, Wen-Bin; Xing, Xue-Kun; Scherson, Daniel A.

2003-01-01

A Raman microscope has been coupled to a computer-controlled, two-dimensional linear translator attached to a custom-designed, sealed optical chamber to allow in situ acquisition of space-, and time-resolved spectra of an operating thin graphite/LiCoO2 Li-ion battery. This unique arrangement made it possible to collect continuously series of Raman spectra from a sharply defined edge of the battery exposing the anode (A), separator (S), and cathode (C), during charge and discharge, while the device was moved back and forth under the fixed focused laser beam along an axis normal to the layered A/S/C plane. Clear spectral evidence was obtained for changes in the amount of Li(+) within particles of graphite in the anode, and, to a lesser extent, of LiCoO2 in the cathode, during battery discharge both as a function of position and time. Analysis of time-resolved Raman spectro-micro-topography (SMT) measurements of the type described in this work are expected to open new prospects for assessing the validity of theoretical models aimed at simulating the flow of Li(+) within Li-ion batteries under operating conditions.

Researching Society and Culture. Third Edition

ERIC Educational Resources Information Center

Seale, Clive, Ed.

2012-01-01

Clear, coherent and trusted, this book is the perfect guide to the main social research methods in use today. The much anticipated Third Edition of Clive Seale's bestselling title further expands its coverage to provide an authoritative introduction to all of the social research methods used to analyze qualitative and quantitative data. Written by…

76 FR 67419 - Takes of Marine Mammals Incidental to Specified Activities; Piling and Structure Removal in...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-11-01

... unclear how expanded monitoring, in the absence of specific experimental design, would empirically verify..., designed to minimize disturbance to harbor seals within the action area in consideration of timing... February (i.e., within the designated in-water work window designed to reduce impacts to fish species in...

Undisturbed soil columns for lysimetry II. Miscible displacement and field evaluation

USDA-ARS?s Scientific Manuscript database

Concerns about agriculture's effect on water quality and the expanding use of no-tillage, has produced a crucial need for in situ solute transport research of mobile nutrients as affected by tillage system. Eight undisturbed soil columns (41 cm diameter by 100 cm long) were sealed into PVC cylinder...

Taking Impressions of Hidden Cavity Walls

NASA Technical Reports Server (NTRS)

Burley, D.; Mayer, W.

1987-01-01

Lightweight, portable internal-molding device makes it possible to measure radii of, or examine contours of, passageways in hidden or complicated cavities. With device, measurements made in field, without returning assemblies to shop or laboratory for inspection. Molding head expands when compressed air applied. Inflatable tubes around head perform dual sealing and aligning function.

Enhanced Thermal Diffusion of Li in Graphite by Alternating Vertical Electric Field: A Hybrid Quantum-Classical Simulation Study

NASA Astrophysics Data System (ADS)

Ohba, Nobuko; Ogata, Shuji; Tamura, Tomoyuki; Kobayashi, Ryo; Yamakawa, Shunsuke; Asahi, Ryoji

2012-02-01

Enhancing the diffusivity of the Li ion in a Li-graphite intercalation compound that has been used as a negative electrode in the Li-ion rechargeable battery, is important in improving both the recharging speed and power of the battery. In the compound, the Li ion creates a long-range stress field around itself by expanding the interlayer spacing of graphite. We advance the hybrid quantum-classical simulation code to include the external electric field in addition to the long-range stress field by first-principles simulation. In the hybrid code, the quantum region selected adaptively around the Li ion is treated using the real-space density-functional theory for electrons. The rest of the system is described with an empirical interatomic potential that includes the term relating to the dispersion force between the C atoms in different layers. Hybrid simulation runs for Li dynamics in graphite are performed at 423 K under various settings of the amplitude and frequency of alternating electric fields perpendicular to C-layers. We find that the in-plane diffusivity of the Li ion is enhanced significantly by the electric field if the amplitude is larger than 0.2 V/Å within its order and the frequency is as high as 1.7 THz. The microscopic mechanisms of the enhancement are explained.

Evolution of the Proximal Sealing Rings of the Anaconda Stent-Graft After Endovascular Aneurysm Repair.

PubMed

Koenrades, Maaike A; Klein, Almar; Leferink, Anne M; Slump, Cornelis H; Geelkerken, Robert H

2018-04-01

To provide insight into the evolution of the saddle-shaped proximal sealing rings of the Anaconda stent-graft after endovascular aneurysm repair (EVAR). Eighteen abdominal aortic aneurysm patients were consecutively enrolled in a single-center, prospective, observational cohort study (LSPEAS; Trialregister.nl identifier NTR4276). The patients were treated electively using an Anaconda stent-graft with a mean 31% oversizing (range 17-47). According to protocol, participants were to be followed for 2 years, during which 5 noncontrast electrocardiogram-gated computed tomography scans would be conducted. Three patients were eliminated within 30 days (1 withdrew, 1 died, and a third was converted before stent-graft deployment), leaving 15 patients (mean age 72.8±3.7 years; 14 men) for this analysis. Evolution in size and shape (symmetry) of both proximal infrarenal sealing rings were assessed from discharge to 24 months using dedicated postprocessing algorithms. At 24 months, the mean diameters of the first and second ring stents had increased significantly (first ring: 2.2±1.0 mm, p<0.001; second ring: 2.7±1.1 mm, p<0.001). At 6 months, the first and second rings had expanded to a mean 96.6%±2.1% and 94.8%±2.7%, respectively, of their nominal diameter, after which the rings expanded slowly; ring diameters stabilized to near nominal size (first ring, 98.3%±1.1%; second ring, 97.2%±1.4%) at 24 months irrespective of initial oversizing. No type I or III endoleaks or aneurysm-, device-, or procedure-related adverse events were noted in follow-up. The difference in the diametric distances between the peaks and valleys of the saddle-shaped rings was marked at discharge but became smaller after 24 months for both rings (first ring: median 2.0 vs 1.2 mm, p=0.191; second ring: median 2.8 vs 0.8 mm; p=0.013). Irrespective of initial oversizing, the Anaconda proximal sealing rings radially expanded to near nominal size within 6 months after EVAR. Initial oval-shaped rings conformed symmetrically and became nearly circular through 24 months. These findings should be taken into account in planning and follow-up.

Nozzle and shroud assembly mounting structure

DOEpatents

Faulder, Leslie J.; Frey, deceased, Gary A.; Nielsen, Engward W.; Ridler, Kenneth J.

1997-01-01

The present nozzle and shroud assembly mounting structure configuration increases component life and reduces maintenance by reducing internal stress between the mounting structure having a preestablished rate of thermal expansion and the nozzle and shroud assembly having a preestablished rate of thermal expansion being less than that of the mounting structure. The mounting structure includes an outer sealing portion forming a cradling member in which an annular ring member is slidably positioned. The mounting structure further includes an inner mounting portion to which a hooked end of the nozzle and shroud assembly is attached. As the inner mounting portion expands and contracts, the nozzle and shroud assembly slidably moves within the outer sealing portion.

Nozzle and shroud assembly mounting structure

DOEpatents

Faulder, L.J.; Frey, G.A.; Nielsen, E.W.; Ridler, K.J.

1997-08-05

The present nozzle and shroud assembly mounting structure configuration increases component life and reduces maintenance by reducing internal stress between the mounting structure having a preestablished rate of thermal expansion and the nozzle and shroud assembly having a preestablished rate of thermal expansion being less than that of the mounting structure. The mounting structure includes an outer sealing portion forming a cradling member in which an annular ring member is slidably positioned. The mounting structure further includes an inner mounting portion to which a hooked end of the nozzle and shroud assembly is attached. As the inner mounting portion expands and contracts, the nozzle and shroud assembly slidably moves within the outer sealing portion. 3 figs.

Haul-Out Behavior of Harbor Seals (Phoca vitulina) in Hood Canal, Washington

PubMed Central

London, Josh M.; Ver Hoef, Jay M.; Jeffries, Steven J.; Lance, Monique M.; Boveng, Peter L.

2012-01-01

The goal of this study was to model haul-out behavior of harbor seals (Phoca vitulina) in the Hood Canal region of Washington State with respect to changes in physiological, environmental, and temporal covariates. Previous research has provided a solid understanding of seal haul-out behavior. Here, we expand on that work using a generalized linear mixed model (GLMM) with temporal autocorrelation and a large dataset. Our dataset included behavioral haul-out records from archival and VHF radio tag deployments on 25 individual seals representing 61,430 seal hours. A novel application for increased computational efficiency allowed us to examine this large dataset with a GLMM that appropriately accounts for temporal autocorellation. We found significant relationships with the covariates hour of day, day of year, minutes from high tide and year. Additionally, there was a significant effect of the interaction term hour of day : day of year. This interaction term demonstrated that seals are more likely to haul out during nighttime hours in August and September, but then switch to predominantly daylight haul-out patterns in October and November. We attribute this change in behavior to an effect of human disturbance levels. This study also examined a unique ecological event to determine the role of increased killer whale (Orcinus orca) predation on haul-out behavior. In 2003 and 2005 these harbor seals were exposed to unprecedented levels of killer whale predation and results show an overall increase in haul-out probability after exposure to killer whales. The outcome of this study will be integral to understanding any changes in population abundance as a result of increased killer whale predation. PMID:22723851

Numerical modelling of multi-vane expander operating conditions in ORC system

NASA Astrophysics Data System (ADS)

Rak, Józef; Błasiak, Przemysław; Kolasiński, Piotr

2017-11-01

Multi-vane expanders are positive displacement volumetric machines which are nowadays considered for application in micro-power domestic ORC systems as promising alternative to micro turbines and other volumetric expanders. The multi-vane expander features very simple design, low gas flow capacity, low expansion ratios, an advantageous ratio of the power output to the external dimensions and are insensitive to the negative influence of the gas-liquid mixture expansion. Moreover, the multi-vane expander can be easily hermetically sealed, which is one of the key issues in the ORC system design. A literature review indicates that issues concerning the application of multi-vane expanders in such systems, especially related to operating of multi-vane expander with different low-boiling working fluids, are innovative, not fully scientifically described and have the potential for practical implementation. In this paper the results of numerical investigations on multi-vane expander operating conditions are presented. The analyses were performed on three-dimensional numerical model of the expander in ANSYS CFX software. The numerical model of the expander was validated using the data obtained from the experiment carried out on a lab test-stand. Then a series of computational analysis were performed using expanders' numerical model in order to determine its operating conditions under various flow conditions of different working fluids.

Shape Fixing via Salt Recrystallization: A Morphology-Controlled Approach To Convert Nanostructured Polymer to Carbon Nanomaterial as a Highly Active Catalyst for Oxygen Reduction Reaction.

PubMed

Ding, Wei; Li, Li; Xiong, Kun; Wang, Yao; Li, Wei; Nie, Yao; Chen, Siguo; Qi, Xueqiang; Wei, Zidong

2015-04-29

Herein, we report a "shape fixing via salt recrystallization" method to efficiently synthesize nitrogen-doped carbon material with a large number of active sites exposed to the three-phase zones, for use as an ORR catalyst. Self-assembled polyaniline with a 3D network structure was fixed and fully sealed inside NaCl via recrystallization of NaCl solution. During pyrolysis, the NaCl crystal functions as a fully sealed nanoreactor, which facilitates nitrogen incorporation and graphitization. The gasification in such a closed nanoreactor creates a large number of pores in the resultant samples. The 3D network structure, which is conducive to mass transport and high utilization of active sites, was found to have been accurately transferred to the final N-doped carbon materials, after dissolution of the NaCl. Use of the invented cathode catalyst in a proton exchange membrane fuel cell produces a peak power of 600 mW cm(-2), making this among the best nonprecious metal catalysts for the ORR reported so far. Furthermore, N-doped carbon materials with a nanotube or nanoshell morphology can be realized by the invented method.

Structure and phase transitions of monolayers of intermediate-length n-alkanes on graphite studied by neutron diffraction and molecular dynamics simulation

NASA Astrophysics Data System (ADS)

Diama, A.; Matthies, B.; Herwig, K. W.; Hansen, F. Y.; Criswell, L.; Mo, H.; Bai, M.; Taub, H.

2009-08-01

We present evidence from neutron diffraction measurements and molecular dynamics (MD) simulations of three different monolayer phases of the intermediate-length alkanes tetracosane (n-C24H50 denoted as C24) and dotriacontane (n-C32H66 denoted as C32) adsorbed on a graphite basal-plane surface. Our measurements indicate that the two monolayer films differ principally in the transition temperatures between phases. At the lowest temperatures, both C24 and C32 form a crystalline monolayer phase with a rectangular-centered (RC) structure. The two sublattices of the RC structure each consists of parallel rows of molecules in their all-trans conformation aligned with their long axis parallel to the surface and forming so-called lamellas of width approximately equal to the all-trans length of the molecule. The RC structure is uniaxially commensurate with the graphite surface in its [110] direction such that the distance between molecular rows in a lamella is 4.26 Å=√3 ag, where ag=2.46 Å is the lattice constant of the graphite basal plane. Molecules in adjacent rows of a lamella alternate in orientation between the carbon skeletal plane being parallel and perpendicular to the graphite surface. Upon heating, the crystalline monolayers transform to a "smectic" phase in which the inter-row spacing within a lamella expands by ˜10% and the molecules are predominantly oriented with the carbon skeletal plane parallel to the graphite surface. In the smectic phase, the MD simulations show evidence of broadening of the lamella boundaries as a result of molecules diffusing parallel to their long axis. At still higher temperatures, they indicate that the introduction of gauche defects into the alkane chains drives a melting transition to a monolayer fluid phase as reported previously.

Structure and phase transitions of monolayers of intermediate-length n-alkanes on graphite studied by neutron diffraction and molecular dynamics simulation.

PubMed

Diama, A; Matthies, B; Herwig, K W; Hansen, F Y; Criswell, L; Mo, H; Bai, M; Taub, H

2009-08-28

We present evidence from neutron diffraction measurements and molecular dynamics (MD) simulations of three different monolayer phases of the intermediate-length alkanes tetracosane (n-C(24)H(50) denoted as C24) and dotriacontane (n-C(32)H(66) denoted as C32) adsorbed on a graphite basal-plane surface. Our measurements indicate that the two monolayer films differ principally in the transition temperatures between phases. At the lowest temperatures, both C24 and C32 form a crystalline monolayer phase with a rectangular-centered (RC) structure. The two sublattices of the RC structure each consists of parallel rows of molecules in their all-trans conformation aligned with their long axis parallel to the surface and forming so-called lamellas of width approximately equal to the all-trans length of the molecule. The RC structure is uniaxially commensurate with the graphite surface in its [110] direction such that the distance between molecular rows in a lamella is 4.26 A=sqrt[3a(g)], where a(g)=2.46 A is the lattice constant of the graphite basal plane. Molecules in adjacent rows of a lamella alternate in orientation between the carbon skeletal plane being parallel and perpendicular to the graphite surface. Upon heating, the crystalline monolayers transform to a "smectic" phase in which the inter-row spacing within a lamella expands by approximately 10% and the molecules are predominantly oriented with the carbon skeletal plane parallel to the graphite surface. In the smectic phase, the MD simulations show evidence of broadening of the lamella boundaries as a result of molecules diffusing parallel to their long axis. At still higher temperatures, they indicate that the introduction of gauche defects into the alkane chains drives a melting transition to a monolayer fluid phase as reported previously.

A field study setup of four homes having non-ventilated and semi-conditioned sealed attics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Miller, William A.; Boudreaux, Philip R.; Pallin, Simon B.

During the 2015-2016 fiscal year and with financial support from the Florida Building Commission (FBC) and the Florida Roofing and Sheet Metal Contractors Association (FRSA ), the University of Florida (UF) and the Oak Ridge National Laboratory (ORNL) completed Phase I of a study that setup four residential home demonstrations in Florida climate zones CZ-1A and CZ-2A. UF and ORNL are evaluating the hygrothermal (heat and moisture flow) performance and durability of sealed attic construction where expanded foam insulation is applied directly to the underside of the roof deck. The four homes are instrumented for measuring temperature and relative humiditymore » of the indoor living space, the outdoor air and the attic air. In addition, the temperature, relative humidity and moisture content of the roof sheathing are being monitored and recorded by remotely-accessible data acquisition equipment. Here, air leakage tests on the whole house, on the sealed attic and in the HVAC ducts were conducted on all four homes.« less

A field study setup of four homes having non-ventilated and semi-conditioned sealed attics

DOE PAGES

Miller, William A.; Boudreaux, Philip R.; Pallin, Simon B.; ...

2016-06-01

During the 2015-2016 fiscal year and with financial support from the Florida Building Commission (FBC) and the Florida Roofing and Sheet Metal Contractors Association (FRSA ), the University of Florida (UF) and the Oak Ridge National Laboratory (ORNL) completed Phase I of a study that setup four residential home demonstrations in Florida climate zones CZ-1A and CZ-2A. UF and ORNL are evaluating the hygrothermal (heat and moisture flow) performance and durability of sealed attic construction where expanded foam insulation is applied directly to the underside of the roof deck. The four homes are instrumented for measuring temperature and relative humiditymore » of the indoor living space, the outdoor air and the attic air. In addition, the temperature, relative humidity and moisture content of the roof sheathing are being monitored and recorded by remotely-accessible data acquisition equipment. Here, air leakage tests on the whole house, on the sealed attic and in the HVAC ducts were conducted on all four homes.« less

Design and Test of an Event Detector for the ReflectoActive Seals System

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stinson, Brad J

2006-05-01

The purpose of this thesis was to research, design, develop and test a novel instrument for detecting fiber optic loop continuity and spatially locating fiber optic breaches. The work is for an active seal system called ReflectoActive Seals whose purpose is to provide real time container tamper indication. A Field Programmable Gate Array was used to implement a loop continuity detector and a spatial breach locator based on a high acquisition speed single photon counting optical time domain reflectometer. Communication and other control features were added in order to create a usable instrument that met defined requirements. A host graphicalmore » user interface was developed to illustrate system use and performance. The resulting device meets performance specifications by exhibiting a dynamic range of 27dB and a spatial resolution of 1.5 ft. The communication scheme used expands installation options and allows the device to communicate to a central host via existing Local Area Networks and/or the Internet.« less

Design and Test of an Event Detector and Locator for the ReflectoActive Seals System

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stinson, Brad J

2006-06-01

The purpose of this work was to research, design, develop and test a novel instrument for detecting fiber optic loop continuity and spatially locating fiber optic breaches. The work is for an active seal system called ReflectoActive{trademark} Seals whose purpose is to provide real time container tamper indication. A Field Programmable Gate Array was used to implement a loop continuity detector and a spatial breach locator based on a high acquisition speed single photon counting optical time domain reflectometer. Communication and other control features were added in order to create a usable instrument that met defined requirements. A host graphicalmore » user interface was developed to illustrate system use and performance. The resulting device meets performance specifications by exhibiting a dynamic range of 27dB and a spatial resolution of 1.5 ft. The communication scheme used expands installation options and allows the device to communicate to a central host via existing Local Area Networks and/or the Internet.« less

Determination of the Apical Sealing Abilities of Mineral Trioxide Aggregate, Portland Cement, and Bioaggregate After Irrigation with Different Solutions.

PubMed

Bayram, H Melike; Saklar, Feridun; Bayram, Emre; Orucoglu, Hasan; Bozkurt, Alperen

2015-06-01

The purpose of this study was to investigate the sealing ability of root-end filling materials such as mineral trioxide aggregate (MTA), Portland cement, and bioaggregate (BA) after irrigation with different solutions. We examined 130 human maxillar central teeth. After cutting the teeth at the cementoenamel junction, the root canals were expanded using nickel-titanium rotary instruments. Root canals were filled with AH-plus and gutta-percha. Then, the roots were cut apically, and 3 mm deep retrograde cavities were prepared. The roots were divided 12 experimental groups, consisting 10 teeth each; the positive and negative control groups contained five teeth each. The retrograde cavities were rinsed using ethylenediaminetetraacetic acid (EDTA), chlorhexidine (CHX), BioPure(™) mixture of a tetracycline isomer, an acid, and a detergent (MTAD), or distilled water. Next, groups 1, 2, 3, and 4 were sealed with MTA; groups 5, 6, 7, and 8 were sealed with Portland cement; and groups 9, 10, 11, and 12 were sealed with BA. Then, apical microleakage was evaluated by using a computerized fluid filtration method. The results of the leakage test were statistically evaluated by the post-hoc Tukey's test. MTA, Portland cement, and BA root-end filling materials showed the least leakage in the CHX and distilled water groups. The highest leakage was observed in the EDTA and MTAD groups. The sealing ability of BA was as good as that of MTA. EDTA and MTAD increased the apical leakage and CHX and distilled water decreased the leakage of the root-end filling materials examined in this study.

An implantable centrifugal blood pump with a recirculating purge system (Cool-Seal system).

PubMed

Yamazaki, K; Litwak, P; Tagusari, O; Mori, T; Kono, K; Kameneva, M; Watach, M; Gordon, L; Miyagishima, M; Tomioka, J; Umezu, M; Outa, E; Antaki, J F; Kormos, R L; Koyanagi, H; Griffith, B P

1998-06-01

A compact centrifugal blood pump has been developed as an implantable left ventricular assist system. The impeller diameter is 40 mm, and pump dimensions are 55 x 64 mm. This first prototype, fabricated from titanium alloy, resulted in a pump weight of 400 g including a brushless DC motor. The weight of a second prototype pump was reduced to 280 g. The entire blood contacting surface is coated with diamond like carbon (DLC) to improve blood compatibility. Flow rates of over 7 L/min against 100 mm Hg pressure at 2,500 rpm with 9 W total power consumption have been measured. A newly designed mechanical seal with a recirculating purge system (Cool-Seal) is used for the shaft seal. In this seal system, the seal temperature is kept under 40 degrees C to prevent heat denaturation of blood proteins. Purge fluid also cools the pump motor coil and journal bearing. Purge fluid is continuously purified and sterilized by an ultrafiltration unit which is incorporated in the paracorporeal drive console. In vitro experiments with bovine blood demonstrated an acceptably low hemolysis rate (normalized index of hemolysis = 0.005 +/- 0.002 g/100 L). In vivo experiments are currently ongoing using calves. Via left thoracotomy, left ventricular (LV) apex descending aorta bypass was performed utilizing an expanded polytetrafluoroethylene (ePTFE) vascular graft with the pump placed in the left thoracic cavity. In 2 in vivo experiments, the pump flow rate was maintained at 5-9 L/min, and pump power consumption remained stable at 9-10 W. All plasma free Hb levels were measured at less than 15 mg/dl. The seal system has demonstrated good seal capability with negligible purge fluid consumption (<0.5 ml/day). In both calves, the pumps demonstrated trouble free continuous function over 6 month (200 days and 222 days).

Hydrogen storage in graphite nanofibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Park, C.; Tan, C.D.; Hidalgo, R.

1998-08-01

Graphite nanofibers (GNF) are a type of material that is produced by the decomposition of carbon containing gases over metal catalyst particles at temperatures around 600 C. These molecularly engineered structures consist of graphene sheets perfectly arranged in a parallel, perpendicular or at angle orientation with respect to the fiber axis. The most important feature of the material is that only edges are exposed. Such an arrangement imparts the material with unique properties for gas adsorption because the evenly separated layers constitute the most ordered set of nanopores that can accommodate an adsorbate in the most efficient manner. In addition,more » the non-rigid pore walls can also expand so as to accommodate hydrogen in a multilayer conformation. Of the many varieties of structures that can be produced the authors have discovered that when gram quantities of a selected number of GNF are exposed to hydrogen at pressures of {approximately} 2,000 psi, they are capable of adsorbing and storing up to 40 wt% of hydrogen. It is believed that a strong interaction is established between hydrogen and the delocalized p-electrons present in the graphite layers and therefore a new type of chemistry is occurring within these confined structures.« less

Statistical Models of Fracture Relevant to Nuclear-Grade Graphite: Review and Recommendations

NASA Technical Reports Server (NTRS)

Nemeth, Noel N.; Bratton, Robert L.

2011-01-01

The nuclear-grade (low-impurity) graphite needed for the fuel element and moderator material for next-generation (Gen IV) reactors displays large scatter in strength and a nonlinear stress-strain response from damage accumulation. This response can be characterized as quasi-brittle. In this expanded review, relevant statistical failure models for various brittle and quasi-brittle material systems are discussed with regard to strength distribution, size effect, multiaxial strength, and damage accumulation. This includes descriptions of the Weibull, Batdorf, and Burchell models as well as models that describe the strength response of composite materials, which involves distributed damage. Results from lattice simulations are included for a physics-based description of material breakdown. Consideration is given to the predicted transition between brittle and quasi-brittle damage behavior versus the density of damage (level of disorder) within the material system. The literature indicates that weakest-link-based failure modeling approaches appear to be reasonably robust in that they can be applied to materials that display distributed damage, provided that the level of disorder in the material is not too large. The Weibull distribution is argued to be the most appropriate statistical distribution to model the stochastic-strength response of graphite.

Basic Study on Engine with Scroll Compressor and Expander

NASA Astrophysics Data System (ADS)

Morishita, Etsuo; Kitora, Yoshihisa; Nishida, Mitsuhiro

Scroll compressors are becoming popular in air conditioning and refrigeration. This is primarily due to their higher efficiency and low noise/vibration characteristics. The scroll principle can be applied also to the steam expander and the Brayton cycle engine,as shown in the past literature. The Otto cycle spark-ignition engine with a scroll compressor and expander is studied in this report. The principle and basic structure of the scroll engine are explained,and the engine characteristic are calculated based on the idealized cycles and processes. A prototype model has been proposed and constructed. The rotary type engine has always had a problem with sealing. The scroll engine might overcome this shortcoming with its much lower rubbing speed compared to its previous counterparts,and is therefore worth investigating.

76 FR 78138 - Airworthiness Directives; The Boeing Company Model 777-200, -200LR, -300, and -300ER Series...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-12-16

... routed along the fuel tank boundary structure, and cap sealing certain penetrating fasteners of the main and center fuel tanks. This AD expands the applicability in the existing AD. This AD was prompted by... tank boundary structure or inside the fuel tanks could result in a fire or explosion. We are issuing...

Vibration Control by a Shear Type Semi-active Damper Using Magnetorheological Grease

NASA Astrophysics Data System (ADS)

Shiraishi, Toshihiko; Misaki, Hirotaka

2016-09-01

This paper describes semi-active vibration control by a controllable damper with high reliability and wide dynamic range using magnetorheological (MR) grease. Some types of cylindrical controllable dampers based on pressure difference between chambers in the dampers using “MR fluid”, whose rheological properties can be varied by applying a magnetic field, have been reported as a semi-active device. However, there are some challenging issues of them. One is to improve dispersion stability. The particles dispersed in MR fluid would make sedimentation after a period. Another is to expand dynamic range. Since cylindrical dampers require sealing elements because of pressure difference in the dampers, the dynamic range between the maximum and minimum damping force according to a magnetic field is reduced. In this study, a controllable damper using the MR effect was proposed and its performance was experimentally verified to improve the dispersion stability by using “MR grease”, which includes grease as the carrier of magnetic particles, and to expand the dynamic range by adopting a shear type structure not requiring sealing elements. Furthermore, semiactive vibration control experiments by the MR grease damper using a simple algorithm based on the skyhook damper scheme were conducted and its performance was investigated.

Thermal Properties of Cement-Based Composites for Geothermal Energy Applications.

PubMed

Bao, Xiaohua; Memon, Shazim Ali; Yang, Haibin; Dong, Zhijun; Cui, Hongzhi

2017-04-27

Geothermal energy piles are a quite recent renewable energy technique where geothermal energy in the foundation of a building is used to transport and store geothermal energy. In this paper, a structural-functional integrated cement-based composite, which can be used for energy piles, was developed using expanded graphite and graphite nanoplatelet-based composite phase change materials (CPCMs). Its mechanical properties, thermal-regulatory performance, and heat of hydration were evaluated. Test results showed that the compressive strength of GNP-Paraffin cement-based composites at 28 days was more than 25 MPa. The flexural strength and density of thermal energy storage cement paste composite decreased with increases in the percentage of CPCM in the cement paste. The infrared thermal image analysis results showed superior thermal control capability of cement based materials with CPCMs. Hence, the carbon-based CPCMs are promising thermal energy storage materials and can be used to improve the durability of energy piles.

Research Technology

NASA Image and Video Library

1998-01-01

Engineers at Marshall Space Flight Center (MSFC) in Huntsville, Alabama, are working with industry partners to develop a new generation of more cost-efficient space vehicles. Lightweight fuel tanks and components under development will be the critical elements in tomorrow's reusable launch vehicles and will tremendously curb the costs of getting to space. In this photo, Tom DeLay, a materials processes engineer for MSFC, uses a new graphite epoxy technology to create lightweight cryogenic fuel lines for futuristic reusable launch vehicles. He is wrapping a water-soluble mandrel, or mold, with a graphite fabric coated with an epoxy resin. Once wrapped, the pipe will be vacuum-bagged and autoclave-cured. The disposable mold will be removed to reveal a thin-walled fuel line. In addition to being much lighter and stronger than metal, this material won't expand or contract as much in the extreme temperatures encountered by launch vehicles.

Effect of heat treatment on CO2 adsorption of KOH-activated graphite nanofibers.

PubMed

Meng, Long-Yue; Park, Soo-Jin

2010-12-15

In this work, graphite nanofibers (GNFs) were successfully expanded intercalating KOH followed by heat treatment in the temperature range of 700-1000 °C. The aim was to improve the CO(2) adsorption capacity of the GNFs by increasing the porosity of GNFs. The effects of heat treatment on the pore structures of GNFs were investigated by N(2) full isotherms, XRD, SEM, and TEM. The CO(2) adsorption capacity was measured by CO(2) isothermal adsorption at 25 °C and 1 atm. From the results, it was found that the activation temperature had a major influence on CO(2) adsorption capacity and textural properties of GNFs. The specific surface area, total pore volume, and mesopore volume of the GNFs increased after heat treatment. The CO(2) adsorption isotherms showed that G-900 exhibited the best CO(2) adsorption capacity with 59.2 mg/g. Copyright © 2010 Elsevier Inc. All rights reserved.

Highly conductive composites for fuel cell flow field plates and bipolar plates

DOEpatents

Jang, Bor Z; Zhamu, Aruna; Song, Lulu

2014-10-21

This invention provides a fuel cell flow field plate or bipolar plate having flow channels on faces of the plate, comprising an electrically conductive polymer composite. The composite is composed of (A) at least 50% by weight of a conductive filler, comprising at least 5% by weight reinforcement fibers, expanded graphite platelets, graphitic nano-fibers, and/or carbon nano-tubes; (B) polymer matrix material at 1 to 49.9% by weight; and (C) a polymer binder at 0.1 to 10% by weight; wherein the sum of the conductive filler weight %, polymer matrix weight % and polymer binder weight % equals 100% and the bulk electrical conductivity of the flow field or bipolar plate is at least 100 S/cm. The invention also provides a continuous process for cost-effective mass production of the conductive composite-based flow field or bipolar plate.

Thermal Properties of Cement-Based Composites for Geothermal Energy Applications

PubMed Central

Bao, Xiaohua; Memon, Shazim Ali; Yang, Haibin; Dong, Zhijun; Cui, Hongzhi

2017-01-01

Geothermal energy piles are a quite recent renewable energy technique where geothermal energy in the foundation of a building is used to transport and store geothermal energy. In this paper, a structural–functional integrated cement-based composite, which can be used for energy piles, was developed using expanded graphite and graphite nanoplatelet-based composite phase change materials (CPCMs). Its mechanical properties, thermal-regulatory performance, and heat of hydration were evaluated. Test results showed that the compressive strength of GNP-Paraffin cement-based composites at 28 days was more than 25 MPa. The flexural strength and density of thermal energy storage cement paste composite decreased with increases in the percentage of CPCM in the cement paste. The infrared thermal image analysis results showed superior thermal control capability of cement based materials with CPCMs. Hence, the carbon-based CPCMs are promising thermal energy storage materials and can be used to improve the durability of energy piles. PMID:28772823

Method for creating ideal tissue fusion in soft-tissue structures using radio frequency (RF) energy.

PubMed

Shields, Chelsea A; Schechter, David A; Tetzlaff, Phillip; Baily, Ali L; Dycus, Sean; Cosgriff, Ned

2004-01-01

Bipolar radiofrequency (RF) energy can successfully seal vascular structures up to 7 mm by fusing collagen and elastin in the lumen. Valleylab has created a system to expand this technology beyond vessel sealing with the development of a closed-loop, feedback-control RF generator that closely monitors tissue fusion. This generator, operating with a loop time of approximately 250 micros, continuously adjusts energy output, creating optimized soft-tissue fusion through structural protein amalgamation. In the first study, RF energy was applied to canine lung using the new-generation generator and lung-prototype device. A lobectomy was completed, sealing the lobar bronchus, parenchyma, and pulmonary vasculature. Chronic performance of the seals was evaluated at necropsy on postoperative days 7 and 14. In a second study, RF energy was applied to porcine small intestine using the same closed-loop generator and anastomosis prototype device. Acute tissue fusion was assessed qualitatively for hemostasis and seal quality. Terminal tissue evaluation was completed on postoperative day 7 and analyzed histopathologically. Histopathology confirmed acute and chronic tissue fusion in both the lung and intestine. Normal pathological healing was substantiated by angiogenesis, granulation, and proliferation of fibroblasts. Preliminary studies using canine lung and porcine small intestine demonstrate the potential of this closed-loop generator for soft-tissue amalgamation. Advanced monitoring capabilities make this fusion system applicable in many soft-tissue structures with adequate collagen and elastin. Further investigation of potential surgical applications needs to be completed.

Corrosion Behavior of an Abradable Seal Coating System

NASA Astrophysics Data System (ADS)

Zhang, Feng; Xu, Cunguan; Lan, Hao; Huang, Chuanbing; Zhou, Yang; Du, Lingzhong; Zhang, Weigang

2014-08-01

A novel NiTi/BN composite abradable coating and two traditional Ni/C and Ni/BN coatings were manufactured with NiAl as the bond layer using thermal spray technology and their corrosion behaviors were investigated. In salt spray corrosion testing of the Ni/BN coating, defective sites of the metal matrix were corroded preferentially. Simulated occlusion experiments and electrochemical tests indicated that migration of ions resulted in pH decrease and Cl- enrichment in defects, and a more aggressive electrolyte led to a decrease of the corrosion potential of the metal inside defects but an increase of the corrosion current density, representing an autocatalytic corrosion process. Moreover, galvanic corrosion between the top and bond coatings of the abradable system was studied via the electrochemical technique. The results showed that, for the NiTi/BN, Ni/BN, and Ni/graphite coatings with a NiAl bond coating, current flow was generated between the anode and cathode. The NiTi/BN coating acted as the cathode due to its passivation, while the Ni/BN and Ni/graphite coatings acted as the anode because of their lower corrosion potential compared with the NiAl coating. The anode suffered serious corrosion damage due to galvanic corrosion, while the cathode corroded only slightly.

Investigation of the characteristics of a stacked direct borohydride fuel cell for portable applications

NASA Astrophysics Data System (ADS)

Kim, Cheolhwan; Kim, Kyu-Jung; Ha, Man Yeong

To investigate the possibility of the portable application of a direct borohydride fuel cell (DBFC), weight reduction of the stack and high stacking of the cells are investigated for practical running conditions. For weight reduction, carbon graphite is adopted as the bipolar plate material even though it has disadvantages in tight stacking, which results in stacking loss from insufficient material strength. For high stacking, it is essential to have a uniform fuel distribution among cells and channels to maintain equal electric load on each cell. In particular, the design of the anode channel is important because active hydrogen generation causes non-uniformity in the fuel flow-field of the cells and channels. To reduce the disadvantages of stacking force margin and fuel maldistribution, an O-ring type-sealing system with an internal manifold and a parallel anode channel design is adopted, and the characteristics of a single and a five-cell fuel cell stack are analyzed. By adopting carbon graphite, the stack weight can be reduced by 4.2 times with 12% of performance degradation from the insufficient stacking force. When cells are stacked, the performance exceeds the single-cell performance because of the stack temperature increase from the reduction of the radiation area from the narrow stacking of cells.

Test Report: Direct and Indirect Lightning Effects on Composite Materials

NASA Technical Reports Server (NTRS)

Evans, R. W.

1997-01-01

Lightning tests were performed on composite materials as a part of an investigation of electromagnetic effects on the materials. Samples were subjected to direct and remote simulated lightning strikes. Samples included various thicknesses of graphite filament reinforced plastic (GFRP), material enhanced by expanded aluminum foil layers, and material with an aluminum honeycomb core. Shielding properties of the material and damage to the sample surfaces and joints were investigated. Adding expanded aluminum foil layers and increasing the thickness of GFRP improves the shielding effectiveness against lightning induced fields and the ability to withstand lightning strikes. A report describing the lightning strike tests performed by the U.S. Army Redstone Technical Test Center, Redstone Arsenal, AL, STERT-TE-E-EM, is included as an appendix.

Highly Stretchable Conductors Based on Expanded Graphite Macroconfined in Tubular Rubber.

PubMed

Luo, Wei; Wu, Tongfei; Chen, Biqiong; Liang, Mei; Zou, Huawei

2017-12-13

Highly stretchable and durable conductors are significant to the development of wearable devices, robots, human-machine interfaces, and other artificial intelligence products. Although many respectable methods have been reported, it is still a challenge to fabricate stretchable conductors with a large elastic limit, high conductivity, and excellent reliability in rapid, effective, and economic ways. Herein, a facile method is offered to fabricate high-performance stretchable tubular conductors (TCs) based on a macroconfined structure of expanded graphite (EG) in rubber tubing by simply physical packing. The maximum original electrical conductivity of TCs reached a high value of 160.6 S/cm. Meanwhile, TCs showed more insensitive response of conductivity to increasing tensile strain compared to the TCs encapsulated with liquid metal or ionic liquid. The conductivity and effective stretchability of TCs can be adjusted by varying the packing density of EG. A low gauge factor below 3 was reached even under 400% stretching for TCs with a packing density of 1.233 g/cm 3 . The excellent resilience and good stability of conductivity of TCs during dynamic stretching-releasing cycles are attributed to the stable and rapid reconstruction of the percolation network of EG particles. The combination of high conductivity, tunable stretchability, and good reliability renders potential applications to TCs, such as highly stretchable interconnects or strain sensors, in human motion detection.

Synthesis and CO{sub 2} adsorption study of modified MOF-5 with multi-wall carbon nanotubes and expandable graphite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ullah, Sami, E-mail: samichemist1@gmail.com, E-mail: azmibustam@petronas.com.my, E-mail: azmish@petronas.com.my, E-mail: lkhlfh@gmail.com, E-mail: hmurshid@gmail.com, E-mail: nadiariazz@gmail.com; Bustam, M. A., E-mail: samichemist1@gmail.com, E-mail: azmibustam@petronas.com.my, E-mail: azmish@petronas.com.my, E-mail: lkhlfh@gmail.com, E-mail: hmurshid@gmail.com, E-mail: nadiariazz@gmail.com; Shariff, A. M., E-mail: samichemist1@gmail.com, E-mail: azmibustam@petronas.com.my, E-mail: azmish@petronas.com.my, E-mail: lkhlfh@gmail.com, E-mail: hmurshid@gmail.com, E-mail: nadiariazz@gmail.com

2014-10-24

MOF-5 was synthesized by solvothermal method and its reactivation under anhydrous conditions. This research is conducted to investigate the effect of MOF-5 and MOF-5 modified with multi-wall carbon nanotubes (MWCNTs) and expandable graphite (EG) on the performance of CO{sub 2} adsorption. The synthesized MOFs were characterized using Field emission scanning electron microscopy (FESEM) for surface morphology, Thermogravimetric analysis (TGA) for thermal stability, X-ray diffraction (XRD) for crystals plane, Brunauer-Emmet-Teller (BET) for surface area and CO{sub 2} adsorption. The result had showed that the modified MOF-5 enhanced the CO{sub 2} adsorption compared to the pure MOF-5. The increment in the CO{submore » 2} uptake capacities of MOF materials was attributed to the decrease in the pore size and enhancement of micropore volume of MOF-5 by multi-walled carbon nanotube and EG incorporation. The BET surface area of the synthesized MOF-5@MWCNTs is more than MOF-5. The CO{sub 2} sorption capacities of MOF-5 and MOF-5@MWCNTs were observed to increase from 0.00008 to 0.00048 mol g-1 at 298 K and 1 bar. The modified MOF-5@MWCNTs resulted in the highest CO{sub 2} adsorption followed by the modified MOF-5@ EG and lastly, MOF-5.« less

Preparation and characterization of expanded graphite/metal oxides for antimicrobial application.

PubMed

Hung, Wei-Che; Wu, Kuo-Hui; Lyu, Dong-Yi; Cheng, Ken-Fa; Huang, Wen-Chien

2017-06-01

Composite materials based on expanded graphite (EG) and metal oxide (MO) particles was prepared by an explosive combustion and blending method. The objective of the study was to develop EG impregnated with metal oxide particulates (Ag 2 O, CuO and ZnO) and evaluate the level of protection the materials conferred against biological agents. The physical properties of the EG/MO composites were examined using SEM, EDX and XRD spectroscopy, and the results indicated that the MO particles were incorporated into the EG matrix after impregnation. The antimicrobial activities of the EG/MO composites against Gram-positive bacteria, Gram-negative bacteria and Bacillus anthracis were investigated using zone of inhibition, minimum inhibitory concentration (MIC), minimum bactericidal concentration (MBC) and plate-counting methods. EG/Ag 2 O exhibited a stronger antibacterial activity than EG/CuO and EG/ZnO, with a MIC of 0.3mg/mL and a MBC of 0.5mg/mL. To the best of our knowledge, few studies have demonstrated that EG/MO composites can inhibit the growth of Bacillus anthracis-adhered cells, thus preventing the process of biofilm formation. Nanoscale metal oxides display enhanced reactive properties toward bacteria due to their high surface area, large number of highly reactive edges, corner defect sites and high surface to volume ratio. Copyright © 2017 Elsevier B.V. All rights reserved.

Composite structures for optical mirror applications

NASA Astrophysics Data System (ADS)

Brand, Richard A.; Marks, John E.

1990-10-01

The employment of composites in RF structures such as antennas, feedhorns, and waveguides is outlined, and focus is placed on the parameters of a composite mirror operating in the 3-5- and 8-12-micron areas. A large beam-steering composite mirror fabricated from ultrahigh-modulus graphite/epoxy is described, including its three subassemblies: the core subassembly and two facesheet subassemblies. Attention is given to an alternative approach in which a gel coat resin is applied to the glass surface and the mirror substrate is pressed to the tool to cover the mirror with the resin. Another method is to seal the composite from the effects of moisture expansion by applying a eutectic coating; voids and crystal-grain growth are the main sources of surface perturbation on such mirror surfaces.

Development of a hermetically sealed brushless DC motor for a J-T cryocooler

NASA Technical Reports Server (NTRS)

Joscelyn, Edwin; Hochler, Irwin; Ferri, Andrew; Rott, Heinz; Soukaris, Ted

1996-01-01

This development was sponsored by Ball Aerospace for the Cryogenic On-Orbit LongLife Active Refrigerator (COOLLAR) program. The cryocooler is designed to cool objects to 65 K and operate in space for at least 7 years. The system also imports minimal impact to the spacecraft in terms of vibration and heat. The basic Joule-Thompson cycle involves compressing a working fluid, nitrogen in this case, at near-constant temperature from 17.2 KPa to 6.89 MPa. The nitrogen is then expanded through a Joule-Thompson valve. The pure nitrogen gas must be kept clean; therefore, any contamination from motor organic materials must be eliminated. This requirement drove the design towards sealing of the motor within a titanium housing without sacrificing motor performance. It is estimated that an unsealed motor would have contributed 1.65 g of contaminants, due to the organic insulation and potting materials, over the 7-year life. This paper describes the motor electrical and mechanical design, as well as the sealing difficulties encountered, along with their solutions.

Comparative assessment of amphibious hearing in pinnipeds.

PubMed

Reichmuth, Colleen; Holt, Marla M; Mulsow, Jason; Sills, Jillian M; Southall, Brandon L

2013-06-01

Auditory sensitivity in pinnipeds is influenced by the need to balance efficient sound detection in two vastly different physical environments. Previous comparisons between aerial and underwater hearing capabilities have considered media-dependent differences relative to auditory anatomy, acoustic communication, ecology, and amphibious life history. New data for several species, including recently published audiograms and previously unreported measurements obtained in quiet conditions, necessitate a re-evaluation of amphibious hearing in pinnipeds. Several findings related to underwater hearing are consistent with earlier assessments, including an expanded frequency range of best hearing in true seals that spans at least six octaves. The most notable new results indicate markedly better aerial sensitivity in two seals (Phoca vitulina and Mirounga angustirostris) and one sea lion (Zalophus californianus), likely attributable to improved ambient noise control in test enclosures. An updated comparative analysis alters conventional views and demonstrates that these amphibious pinnipeds have not necessarily sacrificed aerial hearing capabilities in favor of enhanced underwater sound reception. Despite possessing underwater hearing that is nearly as sensitive as fully aquatic cetaceans and sirenians, many seals and sea lions have retained acute aerial hearing capabilities rivaling those of terrestrial carnivores.

Self-Passivating Lithium/Solid Electrolyte/Iodine Cells

NASA Technical Reports Server (NTRS)

Bugga, Ratnakumar; Whitcare, Jay; Narayanan, Sekharipuram; West, William

2006-01-01

Robust lithium/solid electrolyte/iodine electrochemical cells that offer significant advantages over commercial lithium/ iodine cells have been developed. At room temperature, these cells can be discharged at current densities 10 to 30 times those of commercial lithium/iodine cells. Moreover, from room temperature up to 80 C, the maximum discharge-current densities of these cells exceed those of all other solid-electrolyte-based cells. A cell of this type includes a metallic lithium anode in contact with a commercial flexible solid electrolyte film that, in turn, is in contact with an iodine/ graphite cathode. The solid electrolyte (the chemical composition of which has not been reported) offers the high ionic conductivity needed for high cell performance. However, the solid electrolyte exhibits an undesirable chemical reactivity to lithium that, if not mitigated, would render the solid electrolyte unsuitable for use in a lithium cell. In this cell, such mitigation is affected by the formation of a thin passivating layer of lithium iodide at the anode/electrolyte interface. Test cells of this type were fabricated from iodine/graphite cathode pellets, free-standing solid-electrolyte films, and lithium-foil anodes. The cathode mixtures were made by grinding together blends of nominally 10 weight percent graphite and 90 weight percent iodine. The cathode mixtures were then pressed into pellets at 36 kpsi (248 MPa) and inserted into coin-shaped stainless-steel cell cases that were coated with graphite paste to minimize corrosion. The solid-electrolyte film material was stamped to form circular pieces to fit in the coin cell cases, inserted in the cases, and pressed against the cathode pellets with polyethylene gaskets. Lithium-foil anodes were placed directly onto the electrolyte films. The layers described thus far were pressed and held together by stainless- steel shims, wave springs, and coin cell caps. The assembled cells were then crimped to form hermetic seals. It was found that the solid electrolyte films became discolored within seconds after they were placed in contact with the cathodes - a result of facile diffusion of iodine through the solid electrolyte material (see figure).

Influences of graphene oxide support on the electrochemical performances of graphene oxide-MnO2 nanocomposites

PubMed Central

2011-01-01

MnO2 supported on graphene oxide (GO) made from different graphite materials has been synthesized and further investigated as electrode materials for supercapacitors. The structure and morphology of MnO2-GO nanocomposites are characterized by X-ray diffraction, X-ray photoemission spectroscopy, scanning electron microscopy, transmission electron microscopy, Raman spectroscopy, and Nitrogen adsorption-desorption. As demonstrated, the GO fabricated from commercial expanded graphite (denoted as GO(1)) possesses more functional groups and larger interplane gap compared to the GO from commercial graphite powder (denoted as GO(2)). The surface area and functionalities of GO have significant effects on the morphology and electrochemical activity of MnO2, which lead to the fact that the loading amount of MnO2 on GO(1) is much higher than that on GO(2). Elemental analysis performed via inductively coupled plasma optical emission spectroscopy confirmed higher amounts of MnO2 loading on GO(1). As the electrode of supercapacitor, MnO2-GO(1) nanocomposites show larger capacitance (307.7 F g-1) and better electrochemical activity than MnO2-GO(2) possibly due to the high loading, good uniformity, and homogeneous distribution of MnO2 on GO(1) support. PMID:21951643

Small drill-hole, gas mini-permeameter probe

DOEpatents

Molz, III, Fred J.; Murdoch, Lawrence C.; Dinwiddie, Cynthia L.; Castle, James W.

2002-12-03

The distal end of a basic tube element including a stopper device with an expandable plug is positioned in a pre-drilled hole in a rock face. Rotating a force control wheel threaded on the tube element exerts force on a sleeve that in turn causes the plug component of the stopper means to expand and seal the distal end of the tube in the hole. Gas under known pressure is introduced through the tube element. A thin capillary tube positioned in the tube element connects the distal end of the tube element to means to detect and display pressure changes and data that allow the permeability of the rock to be determined.

Small drill-hole, gas mini-permeameter probe

DOEpatents

Molz, III, Fred J.; Murdoch, Lawrence C.; Dinwiddie, Cynthia L.; Castle, James W.

2002-01-01

The distal end of a basic tube element including a stopper device with an expandable plug is positioned in a pre-drilled hole in a rock face. Rotating a force control wheel threaded on the tube element exerts force on a sleeve that in turn causes the plug component of the stopper means to expand and seal the distal end of the tube in the hole. Gas under known pressure is introduced through the tube element. A thin capillary tube positioned in the tube element connects the distal end of the tube element to means to detect and display pressure changes and data that allow the permeability of the rock to be determined.

Recent advances in the treatment of air leaks.

PubMed

Cerfolio, Robert James

2005-07-01

Alveolar-pleural fistulas (air leaks) are an extremely common clinical problem and remain the most common complication after elective pulmonary resection and video-assisted procedures. The decision making process used to manage air leaks and chest tubes that control them has been, until very recently, based on opinions and training preferences as opposed to facts derived from randomized clinical trials. Recently, several prospective randomized trials have studied air leaks. An objective, reproducible classification system has also been designed and clinically validated to help study air leaks. This system and these studies have shown that water seal is superior to wall suction to help stop most leaks. Even in patients with a pneumothorax and an air leak, water seal is safe and best; however, if a patient has a large leak (greater than an expiratory 3 on the classification system) or experiences subcutaneous emphysema or an expanding pneumothorax that causes hypoxia, then some suction (-10 cm of water) should be applied to the chest tubes. Air leaks were a poorly understood yet extremely common clinical problem that had never been scientifically studied. Over the past 5 years, prospective randomized studies have shown that water seal is the best setting for chest tubes and that a pneumothorax is not a contraindication to leaving tubes on seal. Further studies are needed to investigate the ideal management of alveolar-pleural fistulas (air leaks) in different clinical scenarios besides those that occur postoperatively.

Effect of volatile metabolites of dill, radish and garlic on growth of bacteria

NASA Astrophysics Data System (ADS)

Tirranen, L. S.; Borodina, E. V.; Ushakova, S. A.; Rygalov, V. Ye; Gitelson, J. I.

2001-07-01

In a model experiment plants were grown in sealed chambers on expanded clay aggregate under the luminance of 150 W/m 2 PAR and the temperature of 24°C. Seven bacterial strains under investigation, replicated on nutrient medium surface in Petri dishes, were grown in the atmosphere of cultivated plants. Microbial response was evaluated by the difference between colony size in experiment and in control. In control, bacteria grew in the atmosphere of clean air. To study the effect of volatile metabolites of various plant on microbial growth, the experimental data were compared with the background values defined for each individual experiment. Expanded clay aggregate, luminance, temperature and sealed chamber (without plants) for the background were the same. Volatile metabolites from 28-days old radish plants have been reliably established to have no effect on the growth of microbes under investigation. Metabolites of 30-days old dill and 50-days old garlic have been established to have reliable bacteriostatic effect on the growth of three bacterial strains. Dill and garlic have been found to have different range of effects of volatile substances on bacterial growth. Volatile metabolites of dill and garlic differed in their effect on the sensitivity spectrum of bacteria. An attempt has been made to describe the obtained data mathematically.

Rock Melt Borehole Sealing System, Final Technical Report for SBIR Phase I Grant No. DE-SC0011888

DOE Office of Scientific and Technical Information (OSTI.GOV)

Osnes, John D.; Vining, Cody A.; Nopola, Jay R.

Purpose of Research Deep borehole disposal is one option that has received attention in recent years as a possible strategy for long-term disposal of the tens of thousands of tons of spent nuclear fuel. The feasibility of the deep borehole option relies upon designing and constructing an effective seal within the borehole to ensure that the waste package does not communicate with the shallow subsurface biosphere through the borehole itself. Some of the uncertainty associated with the long-term suitability of the deep borehole option is related to (1) the degradation of traditional sealing materials over time and (2) the inabilitymore » of traditional sealing methods to adequately seal a Disturbed Rock Zone surrounding the borehole. One possible system to address these concerns consists of encapsulating the waste in a melt generated from either the waste itself or a plug above the waste. This current project expanded on previous work to further advance the deep borehole disposal concept. Research Objectives & Findings The overarching objective of the study was to evaluate the feasibility of constructing a downhole heater that is capable of meeting the technical and logistical requirements to melt rock. This ultimate objective was accomplished by two primary approaches. The first approach was to define the heater requirements and conceptually design a system that is capable of melting rock. The second approach was to determine the feasibility of conducting an in situ, field-scale melting experiment to validate the suitability of the rock melt seal concept. The evaluation and conceptual design of the heater system resulted in the following primary findings: • Borehole wall temperatures capable of producing a partial melt are achievable under most expected thermal conductivities with a 12-kilowatt heater. • Commercially available components have been identified that meet the requirements of the heater system, including resistive elements that are capable of providing the required heat generation, container materials that can withstand the anticipated temperatures, and a system capable of providing power to the heater. Evaluating the feasibility of performing field-scale experiments resulted in the following major findings: • The Sanford Underground Research Facility (SURF) has been identified as a host site for field testing of prototype heaters. The technical and logistical requirements for performing the rock melt tests can be met by using or expanding the existing infrastructure at SURF with on-site personnel and contractors. • In situ hydraulic conductivity test using packers can test the effectiveness of the rock melt seal, while a mine back performed from a lower level can further evaluate the recrystallized melt. • Preliminary costing indicates that a field-scale melting experiment at SURF is feasible within a Phase II Small Business Innovation Research budget while allowing sufficient budget for refining the heater design, coordinating the test program, and interpreting the results. Application of Research The rock melt sealing concept has the potential to reduce uncertainty associated with the long-term storage of nuclear waste. Preliminary efforts of this study defined the requirements of a downhole heater system capable of melting rock and indicated that developing such a system is feasible using available technology. The next logical step is designing and manufacturing prototype heaters. Concurrent with prototype development is coordinating robust field-scale experiments that are capable of validating the design for marketing to potential users.« less

Thermal energy storage for low grade heat in the organic Rankine cycle

NASA Astrophysics Data System (ADS)

Soda, Michael John

Limits of efficiencies cause immense amounts of thermal energy in the form of waste heat to be vented to the atmosphere. Up to 60% of unrecovered waste heat is classified as low or ultra-low quality, making recovery difficult or inefficient. The organic Rankine cycle can be used to generate mechanical power and electricity from these low temperatures where other thermal cycles are impractical. A variety of organic working fluids are available to optimize the ORC for any target temperature range. San Diego State University has one such experimental ORC using R245fa, and has been experimenting with multiple expanders. One limitation of recovering waste heat is the sporadic or cyclical nature common to its production. This inconsistency makes sizing heat recovery ORC systems difficult for a variety of reasons including off-design-point efficiency loss, increased attrition from varying loads, unreliable outputs, and overall system costs. Thermal energy storage systems can address all of these issues by smoothing the thermal input to a constant and reliable level and providing back-up capacity for times when the thermal input is deactivated. Multiple types of thermal energy storage have been explored including sensible, latent, and thermochemical. Latent heat storage involves storing thermal energy in the reversible phase change of a phase change material, or PCM, and can have several advantages over other modalities including energy storage density, cost, simplicity, reliability, relatively constant temperature output, and temperature customizability. The largest obstacles to using latent heat storage include heat transfer rates, thermal cycling stability, and potentially corrosive PCMs. Targeting 86°C, the operating temperature of SDSU's experimental ORC, multiple potential materials were explored and tested as potential PCMs including Magnesium Chloride Hexahydrate (MgCl2˙6H2O), Magnesium Nitrate Hexahydrate (Mg(NO3)2˙6H 2O), montan wax, and carnauba wax. The addition of graphite to augment heat transfer rates was also tested. Melting and solidification temperatures largely matched predictions. The magnesium salts were found to be less stable under thermal cycling than the waxes. Graphite was only soluble in the waxes. Mixtures of magnesium salts and waxes yielded a layered composite with the less dense waxes creating a sealing layer over the salt layer that significantly increased the stability of the magnesium salts. Research into optimum heat exchangers and storage vessels for these applications indicates that horizontally oriented aluminum pipes with vertically oriented aluminum fins would be the best method of storing and retrieving energy. Fin spacing can be predicted by an equation based on target temperatures and PCM characteristics.

Development and characterization of a rechargeable carbon foam electrode containing nickel oxyhydroxide active mass

NASA Astrophysics Data System (ADS)

Chye, Matthew B.

2011-12-01

Batteries and asymmetric electrochemical capacitors using nickel-based positive electrodes can provide high currents due to their defect structure and low internal resistance. Nickel-based positive electrodes, therefore, are ideal for high current applications such as power tools and electric vehicles (EVs). The positive electrodes prepared in this research are monolithic graphitic foams electrochemically impregnated with nickel oxyhydroxide active mass and select additives that enhance electrode performance. Carbon foam is a good current collector due to its light-weight, porous, and graphitic nature, which give its good electrical properties and the ability to be used as a current collector. Replacing sintered nickel current collectors in nickel-based batteries with a low cost, readily available material, carbon foam, can reduce the mass of a rechargeable battery. The goal of this research has been to contribute to fundamental science through better understanding of optimizing the deposition and formation processes of the active mass onto carbon foams as well as investigating the active mass behavior under deposition, formation, and cycling conditions. Flooded cells and a PFA sealed asymmetric capacitor have been used. The effects of carbon foam surface pretreatments and how they affect the active material/carbon foam performance are demonstrated. Also the feasibility of this positive electrode as a component in nickel-based batteries, a Ni-Zn cells and an asymmetric capacitor pouch cell, is demonstrated.

Design and Preparation of Carbon Based Composite Phase Change Material for Energy Piles.

PubMed

Yang, Haibin; Memon, Shazim Ali; Bao, Xiaohua; Cui, Hongzhi; Li, Dongxu

2017-04-07

Energy piles-A fairly new renewable energy concept-Use a ground heat exchanger (GHE) in the foundation piles to supply heating and cooling loads to the supported building. Applying phase change materials (PCMs) to piles can help in maintaining a stable temperature within the piles and can then influence the axial load acting on the piles. In this study, two kinds of carbon-based composite PCMs (expanded graphite-based PCM and graphite nanoplatelet-based PCM) were prepared by vacuum impregnation for potential application in energy piles. Thereafter, a systematic study was performed and different characterization tests were carried out on two composite PCMs. The composite PCMs retained up to 93.1% of paraffin and were chemically compatible, thermally stable and reliable. The latent heat of the composite PCM was up to 152.8 J/g while the compressive strength of cement paste containing 10 wt % GNP-PCM was found to be 37 MPa. Hence, the developed composite PCM has potential for thermal energy storage applications.

Design and Preparation of Carbon Based Composite Phase Change Material for Energy Piles

PubMed Central

Yang, Haibin; Memon, Shazim Ali; Bao, Xiaohua; Cui, Hongzhi; Li, Dongxu

2017-01-01

Energy piles—A fairly new renewable energy concept—Use a ground heat exchanger (GHE) in the foundation piles to supply heating and cooling loads to the supported building. Applying phase change materials (PCMs) to piles can help in maintaining a stable temperature within the piles and can then influence the axial load acting on the piles. In this study, two kinds of carbon-based composite PCMs (expanded graphite-based PCM and graphite nanoplatelet-based PCM) were prepared by vacuum impregnation for potential application in energy piles. Thereafter, a systematic study was performed and different characterization tests were carried out on two composite PCMs. The composite PCMs retained up to 93.1% of paraffin and were chemically compatible, thermally stable and reliable. The latent heat of the composite PCM was up to 152.8 J/g while the compressive strength of cement paste containing 10 wt % GNP-PCM was found to be 37 MPa. Hence, the developed composite PCM has potential for thermal energy storage applications. PMID:28772752

Shunt attachment and method for interfacing current collection systems

DOEpatents

Denney, P.E.; Iyer, N.C.; Hannan, W.F. III.

1992-12-08

A composite brush to shunt attachment wherein a volatile component of a composite but mostly metallic brush, used for current collection purposes, does not upon welding or brazing, adversely affect the formation of the interfacial bond with a conductive shunt which carries the current from the zone of the brush. The brush to shunt attachment for a brush material of copper-graphite composite and a shunt of copper, or substituting silver for copper as an alternative, is made through a hot isostatic pressing (HIP). The HIP process includes applying high pressure and temperature simultaneously at the brush to shunt interface, after it has been isolated or canned in a metal casing in which the air adjacent to the interface has been evacuated and the interfacial area has been sealed before the application of pressure and temperature. 6 figs.

Shunt attachment and method for interfacing current collection systems

DOEpatents

Denney, Paul E.; Iyer, Natraj C.; Hannan, III, William F.

1992-01-01

A composite brush to shunt attachment wherein a volatile component of a composite but mostly metallic brush, used for current collection purposes, does not upon welding or brazing, adversely affect the formation of the interfacial bond with a conductive shunt which carries the current from the zone of the brush. The brush to shunt attachment for a brush material of copper-graphite composite and a shunt of copper, or substituting silver for copper as an alternative, is made through a hot isostatic pressing (HIP). The HIP process includes applying high pressure and temperature simultaneously at the brush to shunt interface, after it has been isolated or canned in a metal casing in which the air adjacent to the interface has been evacuated and the interfacial area has been sealed before the application of pressure and temperature.

Preparation and Thermal Properties of Molecular-Bridged Expanded Graphite/Polyethylene Glycol Composite Phase Change Materials for Building Energy Conservation.

PubMed

Zhang, Dong; Chen, Meizhu; Liu, Quantao; Wan, Jiuming; Hu, Jinxuan

2018-05-16

Using phase change materials (PCMs) in building envelopes became a reliable method to improve indoor comfort and reduce buildings' energy consumption. This research developed molecular-bridged expanded graphite (EG)/polyethylene glycol (PEG) composite PCMs (m-EPs) to conserve energy in buildings. The m-EPs were prepared through a vacuum absorption technique, and a titanate coupling agent was used to build a molecular bridge between EG and PEG. SEM, mercury intrusion porosimetry (MIP), the leakage test, microcalorimetry, X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy (FT-IR) were conducted to characterize the morphology, pore structure, absorbability, and modifying effects of the m-EPs. The phase change temperature, latent heat, thermal stability, and thermal conductivity of the m-EPs were determined by a differential scanning calorimeter (DSC), TGA, and a thermal constants analyzer. Results showed that the maximum mass ratio of PEG to EG without leakage was 1:7, and a stable connection was established in the m-EPs after modification. Compared with the unmodified EPs, the supercooling degree of the m-EPs reduced by about 3 °C, but the latent heats and initial decomposition temperatures increased by approximately 10% and 20 °C, respectively, which indicated an improvement in the thermal energy storage efficiency. The thermal conductivities of the m-EPs were 10 times higher than those of the pristine PEGs, which ensured a rapid responding to building temperature fluctuations.

Preparation and Thermal Properties of Molecular-Bridged Expanded Graphite/Polyethylene Glycol Composite Phase Change Materials for Building Energy Conservation

PubMed Central

Zhang, Dong; Chen, Meizhu; Liu, Quantao; Hu, Jinxuan

2018-01-01

Using phase change materials (PCMs) in building envelopes became a reliable method to improve indoor comfort and reduce buildings’ energy consumption. This research developed molecular-bridged expanded graphite (EG)/polyethylene glycol (PEG) composite PCMs (m-EPs) to conserve energy in buildings. The m-EPs were prepared through a vacuum absorption technique, and a titanate coupling agent was used to build a molecular bridge between EG and PEG. SEM, mercury intrusion porosimetry (MIP), the leakage test, microcalorimetry, X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared spectroscopy (FT-IR) were conducted to characterize the morphology, pore structure, absorbability, and modifying effects of the m-EPs. The phase change temperature, latent heat, thermal stability, and thermal conductivity of the m-EPs were determined by a differential scanning calorimeter (DSC), TGA, and a thermal constants analyzer. Results showed that the maximum mass ratio of PEG to EG without leakage was 1:7, and a stable connection was established in the m-EPs after modification. Compared with the unmodified EPs, the supercooling degree of the m-EPs reduced by about 3 °C, but the latent heats and initial decomposition temperatures increased by approximately 10% and 20 °C, respectively, which indicated an improvement in the thermal energy storage efficiency. The thermal conductivities of the m-EPs were 10 times higher than those of the pristine PEGs, which ensured a rapid responding to building temperature fluctuations. PMID:29772728

Adsorption and decomposition of dimethyl methylphosphonate (DMMP) on expanded graphite/metal oxides

NASA Astrophysics Data System (ADS)

Hung, Wei-Che; Wang, Je-Chuang; Wu, Kuo-Hui

2018-06-01

Composites based on expanded graphite (EG) and metal oxides (MOs) were prepared by an explosive combustion and blending method. A metal oxide (Ag2O, CuO or ZnO)-containing phase was employed as a component with reactive functionality, which was supported on EG as a component with adsorptive functionality. The physical properties of the EG/MO composites were examined using SEM and FTIR spectroscopy, the results of which indicated that the MOs were incorporated in the EG matrix after impregnation. Solid state magic angle spinning (MAS) 1H, 31P and cross polarization (CP) MAS 13C NMR studies of the EG/MO composites were performed after adsorption of dimethyl methylphosphonate (DMMP). The FTIR and NMR data showed that the initial uptake occurred through both molecular and reactive adsorption. Molecular adsorption occurred by van der Waals interaction of M(Zn, Cu, Ag)⋯Odbnd P and hydrogen-bond formation to isolated hydroxyl groups. Reactive chemisorption appeared to occur through interaction with both Lewis acid sites and active oxygen species present on the MO surface. The FTIR and NMR results exhibited a trend of reactivity towards DMMP in the order Ag2O > ZnO > CuO, which indicated stronger interaction between the Lewis acid sites and the phosphoryl O atom of DMMP for Ag2O as compared with ZnO and CuO, with concomitant formation of surface-coordinated DMMP and bridge-bonded Osbnd Psbnd O phosphorus oxide species.

Correlated NanoSIMS, TEM, and XANES Studies of Presolar Grains

NASA Astrophysics Data System (ADS)

Groopman, Evan Edward

The objective of this thesis is to describe the correlated study of individual presolar grains via Nano-scale Secondary Ion Mass Spectrometry (NanoSIMS), Transmission Electron Microscopy (TEM), and Scanning Transmission X-ray Microscopy (STXM) utilizing X-ray Absorption Near Edge Structure (XANES), with a focus on connecting these correlated laboratory studies to astrophysical phenomena. The correlated isotopic, chemical, and microstructural studies of individual presolar grains provide the most detailed description of their formation environments, and help to inform astrophysical models and observations of stellar objects. As a part of this thesis I have developed and improved upon laboratory techniques for micromanipulating presolar grains and embedding them in resin for ultramicrotomy after NanoSIMS analyses and prior to TEM characterization. The new methods have yielded a 100% success rate and allow for the specific correlation of microstructural and isotopic properties of individual grains. Knowing these properties allows for inferences to be made regarding the condensation sequences and the origins of the stellar material that condensed to form these grains. NanoSIMS studies of ultramicrotomed sections of presolar graphite grains have revealed complex isotopic heterogeneities that appear to be primary products of the grains' formation environments and not secondary processing during the grains' lifetimes. Correlated excesses in 15N and 18O were identified as being carried by TiC subgrains within presolar graphite grains from supernovae (SNe). These spatially-correlated isotopic anomalies pinpoint the origin of the material that formed these grains: the inner He/C zone. Complex microstructures and isotopic heterogeneities also provide evidence for mixing in globular SN ejecta, which is corroborated by models and telescopic observations. In addition to these significant isotopic discoveries, I have also observed the first reported nanocrystalline core surrounded by turbostratic graphite within a low-density SN graphite grain. Nanocrystalline cores consisting of randomly-oriented 2-4 nm sheets of graphene and surrounded by concentric shells of graphite have been observed in high-density presolar graphite grains from Asymptotic Giant Branch stars, whose grains are typically microstructurally distinct from SN graphite grains. These vastly different stellar environments briefly formed similar nanocrystalline structures before diverging in the structure of their mantling graphite to be typical of AGB and SN grains. While relatively few correlated NanoSIMS and TEM studies have been performed previously, which this research thesis aims to expand, my collaborators and I also endeavored to add a third correlated technique, STXM/XANES, which had previously not been applied to presolar grains. XANES allows for the investigation of molecular bonds, which we used to help infer physical and chemical properties of stellar ejecta. I investigated the C K-edge and Ti L-edge of molecular bonds in both presolar graphite grains and their TiC subgrains. The presolar graphite grains, while overwhelmingly composed of aromatic C molecules, host a wide variety of minor organic molecules. Considering the large isotopic anomalies in the grains, these minor components are not likely due to contamination. I also investigated the valence state of Ti in Ti-rich subgrains and plan to work towards illuminating the effect that V in solid solution has upon the TiC bonds.

Graphite grain-size spectrum and molecules from core-collapse supernovae

NASA Astrophysics Data System (ADS)

Clayton, Donald D.; Meyer, Bradley S.

2018-01-01

Our goal is to compute the abundances of carbon atomic complexes that emerge from the C + O cores of core-collapse supernovae. We utilize our chemical reaction network in which every atomic step of growth employs a quantum-mechanically guided reaction rate. This tool follows step-by-step the growth of linear carbon chain molecules from C atoms in the oxygen-rich C + O cores. We postulate that once linear chain molecules reach a sufficiently large size, they isomerize to ringed molecules, which serve as seeds for graphite grain growth. We demonstrate our technique for merging the molecular reaction network with a parallel program that can follow 1017 steps of C addition onto the rare seed species. Due to radioactivity within the C + O core, abundant ambient oxygen is unable to convert C to CO, except to a limited degree that actually facilitates carbon molecular ejecta. But oxygen severely minimizes the linear-carbon-chain abundances. Despite the tiny abundances of these linear-carbon-chain molecules, they can give rise to a small abundance of ringed-carbon molecules that serve as the nucleations on which graphite grain growth builds. We expand the C + O-core gas adiabatically from 6000 K for 109 s when reactions have essentially stopped. These adiabatic tracks emulate the actual expansions of the supernova cores. Using a standard model of 1056 atoms of C + O core ejecta having O/C = 3, we calculate standard ejection yields of graphite grains of all sizes produced, of the CO molecular abundance, of the abundances of linear-carbon molecules, and of Buckminsterfullerene. None of these except CO was expected from the C + O cores just a few years past.

Hypervelocity impact survivability experiments for carbonaceous impactors

NASA Technical Reports Server (NTRS)

Bunch, T. E.; Becker, Luann; Bada, Jeffrey; Macklin, John; Radicatidibrozolo, Filippo; Fleming, R. H.; Erlichman, Jozef

1993-01-01

We performed a series of hypervelocity impact experiments using carbon-bearing impactors (diamond, graphite, fullerenes, phthalic acid crystals, and Murchison meteorite) into Al plate at velocities between 4.2 and 6.1 km/s. These tests were made to do the following: (1) determine the survivability of carbon forms and organize molecules in low hypervelocity impact; (2) characterize carbonaceous impactor residues; and (3) determine whether or not fullerenes could form from carbonaceous impactors, under our experimental conditions, or survive as impactors. An analytical protocol of field emission SEM imagery, SEM-EDX, laser Raman spectroscopy, single and 2-stage laser mass spectrometry, and laser induced fluorescence (LIF) found the following: (1) diamonds did not survive impact at 4.8 km/s, but were transformed into various forms of disordered graphite; (2) intact, well-ordered graphite impactors did survive impact at 5.9 km/sec, but were only found in the crater bottom centers; the degree of impact-induced disorder in the graphite increases outward (walls, rims, ejecta); (3) phthalic acid crystals were destroyed on impact (at 4.2 km/s, although a large proportion of phthalic acid molecules did survive impact); (4) fullerenes did not form as products of carbonaceous impactors (5.9 - 6.1 km/s, fullerene impactor molecules mostly survived impact at 5.9 km/s; and (5) two Murchison meteorite samples (launched at 4.8 and 5.9 km/s) show preservation of some higher mass polycyclic aromatic hydrocarbons (PAHs) compared with the non-impacted sample. Each impactor type shows unique impactor residue morphologies produced at a given impact velocity. An expanded methodology is presented to announce relatively new analytical techniques together with innovative modifications to other methods that can be used to characterize small impact residues in LDEF craters, in addition to other acquired extraterrestrial samples.

Ionic Liquid-Modified Thermosets and Their Nanocomposites: Dispersion, Exfoliation, Degradation, and Cure

NASA Astrophysics Data System (ADS)

Throckmorton, James A.

This dissertation explores the application of a room temperature ionic liquid (RTIL) to problems in the chemistry, processing, and modification of thermosetting polymers. In particular, the solution properties and reaction chemistry of 1-ethyl-3-methyl imidazolium dicyanamide (EMIM-DCN) are applied to problems of nanoparticle dispersion and processing, graphite exfoliation, cyanate ester (CE) cure, and the environmental degradation of CEs. Nanoparticle Dispersion: Nanocomposite processing can be simplified by using the same compound as both a nanoparticle solvent and an initiator for polymerization. This dual-function molecule can be designed both for solvent potential and reaction chemistry. EMIM-DCN, previously shown by our lab to act as an epoxy initiator, is used in the synthesis of silica and acid expanded graphite composites. These composites are then characterized for particle dispersion and physical properties. Individual particle dispersion of silica nanocomposites is shown, and silica nanocomposites at low loading show individual particle dispersion and improved modulus and fracture toughness. GNP nanocomposites show a 70% increase in modulus along with a 10-order of magnitude increase in electrical conductivity at 6.5 vol%, and an electrical percolation threshold of 1.7 vol%. Direct Graphite Exfoliation By Laminar Shear: This work presents a laminar-shear alternative to chemical processing and chaotic flow-fields for the direct exfoliation of graphite and the single-pot preparation of nanocomposites. Additionally, we develop the theory of laminar flow through a 3-roll mill, and apply that theory to the latest developments in the theory of graphite interlayer shear. The resulting nanocomposite shows low electrical percolation (0.5 vol%) and low thickness (1-3 layer) graphite/graphene flakes. Additionally, the effect of processing conditions by rheometry and comparison with solvent-free conditions reveal the interactions between processing and matrix properties and provide insight into the theory of the chemical and physical exfoliation of graphite crystals and the resulting polymer matrix dispersion. Cyanate Ester Cure: Dicyanamide-containing ionic liquids decrease the cure temperature of bi- and tri-functional CEs. During the cure reaction, the dicyanamide anion completely reacts and is incorporated into the triazine network. The cure effect was found in many dicyanamide-containing ionic liquids with diverse cations. This invention creates a novel, ionic thermoset polymer. The dicyanamide initiator provides an alternative to metal and hydroxyl catalysts (which have been shown to accelerate degradation and possess human and environmental toxicity). Additionally, the ionic character of the new polymer, rare among thermosets, lends itself to future research and novel applications. RTIL initiation also paves the way to new CE technologies, including RTIL-CE nanocomposites, prepared by graphite exfoliation and nanocomposite dispersion techniques developed herin.

Prototype Rechargeable Lithium Batteries. Phase 1

DTIC Science & Technology

1987-06-01

pentoxide [ V2o5 ], titanium disulfide [TiS ], vanadium V) sulfide [V2S 5 ], and lithium cobalt oxide [Li Co02]) witi high conductivity, ester-Eased...2400 envelope while the cathodes were supported with porous glass disks to maintain good electrical contact with the expanded metal current collectors...cells consisted of an electrode stack mounted between two glass slides held together with stainless steel wire and sealed in a Fisher & Porter 3-ounce

A systems approach to hemostasis: 4. How hemostatic thrombi limit the loss of plasma-borne molecules from the microvasculature

PubMed Central

Welsh, John D.; Muthard, Ryan W.; Stalker, Timothy J.; Taliaferro, Joshua P.; Diamond, Scott L.

2016-01-01

Previous studies have shown that hemostatic thrombi formed in response to penetrating injuries have a core of densely packed, fibrin-associated platelets overlaid by a shell of less-activated, loosely packed platelets. Here we asked, first, how the diverse elements of this structure combine to stem the loss of plasma-borne molecules and, second, whether antiplatelet agents and anticoagulants that perturb thrombus structure affect the re-establishment of a tight vascular seal. The studies combined high-resolution intravital microscopy with a photo-activatable fluorescent albumin marker to simultaneously track thrombus formation and protein transport following injuries to mouse cremaster muscle venules. The results show that protein loss persists after red cell loss has ceased. Blocking platelet deposition with an αIIbβ3 antagonist delays vessel sealing and increases extravascular protein accumulation, as does either inhibiting adenosine 5′-diphosphate (ADP) P2Y12 receptors or reducing integrin-dependent signaling and retraction. In contrast, sealing was unaffected by introducing hirudin to block fibrin accumulation or a Gi2α gain-of-function mutation to expand the thrombus shell. Collectively, these observations describe a novel approach for studying vessel sealing after injury in real time in vivo and show that (1) the core/shell architecture previously observed in arterioles also occurs in venules, (2) plasma leakage persists well beyond red cell escape and mature thrombus formation, (3) the most critical events for limiting plasma extravasation are the stable accumulation of platelets, ADP-dependent signaling, and the emergence of a densely packed core, not the accumulation of fibrin, and (4) drugs that affect platelet accumulation and packing can delay vessel sealing, permitting protein escape to continue. PMID:26738537

Female harbor seal (Phoca vitulina) behavioral response to playbacks of underwater male acoustic advertisement displays

PubMed Central

Blades, Brittany; Parks, Susan E.

2018-01-01

During the breeding season, male harbor seals (Phoca vitulina) make underwater acoustic displays using vocalizations known as roars. These roars have been shown to function in territory establishment in some breeding areas and have been hypothesized to be important for female choice, but the function of these sounds remains unresolved. This study consisted of a series of playback experiments in which captive female harbor seals were exposed to recordings of male roars to determine if females respond to recordings of male vocalizations and whether or not they respond differently to roars from categories with different acoustic characteristics. The categories included roars with characteristics of dominant males (longest duration, lowest frequency), subordinate males (shortest duration, highest frequency), combinations of call parameters from dominant and subordinate males (long duration, high frequency and short duration, low frequency), and control playbacks of water noise and water noise with tonal signals in the same frequency range as male signals. Results indicate that overall females have a significantly higher level of response to playbacks that imitate male vocalizations when compared to control playbacks of water noise. Specifically, there was a higher level of response to playbacks representing dominant male vocalization when compared to the control playbacks. For most individuals, there was a greater response to playbacks representing dominant male vocalizations compared to playbacks representing subordinate male vocalizations; however, there was no statistical difference between those two playback types. Additionally, there was no difference between the playbacks of call parameter combinations and the controls. Investigating female preference for male harbor seal vocalizations is a critical step in understanding the harbor seal mating system and further studies expanding on this captive study will help shed light on this important issue. PMID:29607261

Female harbor seal (Phoca vitulina) behavioral response to playbacks of underwater male acoustic advertisement displays.

PubMed

Matthews, Leanna P; Blades, Brittany; Parks, Susan E

2018-01-01

During the breeding season, male harbor seals ( Phoca vitulina ) make underwater acoustic displays using vocalizations known as roars. These roars have been shown to function in territory establishment in some breeding areas and have been hypothesized to be important for female choice, but the function of these sounds remains unresolved. This study consisted of a series of playback experiments in which captive female harbor seals were exposed to recordings of male roars to determine if females respond to recordings of male vocalizations and whether or not they respond differently to roars from categories with different acoustic characteristics. The categories included roars with characteristics of dominant males (longest duration, lowest frequency), subordinate males (shortest duration, highest frequency), combinations of call parameters from dominant and subordinate males (long duration, high frequency and short duration, low frequency), and control playbacks of water noise and water noise with tonal signals in the same frequency range as male signals. Results indicate that overall females have a significantly higher level of response to playbacks that imitate male vocalizations when compared to control playbacks of water noise. Specifically, there was a higher level of response to playbacks representing dominant male vocalization when compared to the control playbacks. For most individuals, there was a greater response to playbacks representing dominant male vocalizations compared to playbacks representing subordinate male vocalizations; however, there was no statistical difference between those two playback types. Additionally, there was no difference between the playbacks of call parameter combinations and the controls. Investigating female preference for male harbor seal vocalizations is a critical step in understanding the harbor seal mating system and further studies expanding on this captive study will help shed light on this important issue.

Experiment and simulation of a LiFePO4 battery pack with a passive thermal management system using composite phase change material and graphite sheets

NASA Astrophysics Data System (ADS)

Lin, Chunjing; Xu, Sichuan; Chang, Guofeng; Liu, Jinling

2015-02-01

A passive thermal management system (TMS) for LiFePO4 battery modules using phase change material (PCM) as the heat dissipation source to control battery temperature rise is developed. Expanded graphite matrix and graphite sheets are applied to compensate low thermal conductivity of PCM and improve temperature uniformity of the batteries. Constant current discharge and mixed charge-discharge duties were applied on battery modules with and without PCM on a battery thermal characteristics test platform. Experimental results show that PCM cooling significantly reduces the battery temperature rise during short-time intense use. It is also found that temperature uniformity across the module deteriorates with the increasing of both discharge time and current rates. The maximum temperature differences at the end of 1C and 2C-rate discharges are both less than 5 °C, indicating a good performance in battery thermal uniformity of the passive TMS. Experiments on warm-keeping performance show that the passive TMS can effectively keep the battery within its optimum operating temperature for a long time during cold weather uses. A three dimensional numerical model of the battery pack with the passive TMS was conducted using ANSYS Fluent. Temperature profiles with respect to discharging time reveal that simulation shows good agreement with experiment at 1C-discharge rate.

Smaller-lateral-size graphene oxide hydrosols sealed in dialysis bags for enhanced trace Pb(II) removal from water without re-pollution

NASA Astrophysics Data System (ADS)

Guo, Lanyu; Liu, Liyun; Zhuo, Mingpeng; Fu, Shulei; Xu, Yunpeng; Zhou, Wenwei; Shi, Ce; Ye, Bin; Li, Yongxiu; Chen, Weifan

2018-07-01

In this work, presented is a novel and facile strategy to enhance Pb(II) adsorption capacity of graphene oxide (GO) hydrosols via the modified Hummers' method, using the smaller-sized natural flake graphite as starting materials. The as-prepared micron GO (MGO) and submicron GO (SMGO) hydrosols were sealed in dialysis bags for adsorptive separation of Pb(II) from water to avoid secondary pollution. The effects of pH and contact duration on Pb(II) adsorption on MGO and SMGO as well as their thermodynamics and kinetics were investigated comparatively. Their performances for recycling and regeneration were also evaluated. The results indicated that SMGO exhibited an enhanced maximum sorption capacity for Pb(II) up to 1162.60 mg·g-1 higher than MGO by 25.75% and achieved adsorption equilibrium faster, which can be attributed to the fact that SMGO has more oxygen-containing functional groups on the sheet basal planes and especially at the sheet edges than SMGO. The adsorption of Pb(II) on MGO and SMGO was a spontaneous and endothermic process and well fitted the pseudo-second-order kinetics and the Langmuir sorption model. Significantly, MGO and SMGO nanosheets still kept the high sorption capacities of 514.26 mg·g-1 and 700.35 mg·g-1 after the 5 cycles, respectively, promising of enormous potential applications.

Chlorinated hydrocarbon contaminants in arctic marine mammals.

PubMed

Norstrom, R J; Muir, D C

1994-09-16

By 1976, the presence of chlorinated hydrocarbon contaminants (CHCs) had been demonstrated in fur seal (Callorhinus ursinus), ringed seal (Phoca hispida), hooded seal (Cystophora cristata), bearded seal (Erignathus barbatus), walrus (Obdobenus rosmarus divergens), beluga (Delphinapterus leucas), porpoise (Phocoena phocoena) and polar bear (Ursus maritimus) in various parts of the Arctic. In spite of this early interest, very little subsequent research on contaminants in Arctic marine mammals was undertaken until the mid-1980s. Since that time, there has been an explosion of interest, resulting in a much expanded data base on contaminants in Arctic marine mammals. Except in the Russian Arctic, data have now been obtained on the temporospatial distribution of PCBs and other contaminants in ringed seal, beluga and polar bear. Contaminants in narwhal (Monodon monoceros) have also now been measured. On a fat weight basis, the sum of DDT-related compounds (S-DDT) and PCB levels are lowest in walrus (< 0.1 microgram/g), followed by ringed seal, (0.1-1 microgram/g range). Levels are an order of magnitude higher in beluga and narwhal (1-10 micrograms/g range). It appears that metabolism and excretion of S-DDT and PCBs may be less efficient in cetaceans, leading to greater biomagnification. Polar bears have similar levels of PCBs as cetaceans (1-10 micrograms/g), but with a much simpler congener pattern. DDE levels are lowest in polar bear, indicating rapid metabolism. Effects of age and sex on residue levels are found for all species where this was measured. Among cetaceans and ringed seal, sexually mature females have lower levels than males due to lactation. Although PCB levels in adult male polar bears are about twice as high as females, there is only a trivial age effect in either sex apart from an initial decrease from birth to sexual maturity (age 0-5). Comparison of levels of S-DDT and PCBs in Arctic beluga and ringed seal with those in beluga in the Gulf of St. Lawrence and ringed seal in the Baltic Sea, indicate that overall contamination of the Arctic marine ecosystem is 10-50 times less than the most highly contaminated areas in the northern hemisphere temperate latitude marine environment. Geographic distribution of residue levels in polar bears indicates a gradual increase from Alaska east to Svalbard, except PCB levels are significantly higher in eastern Greenland and Svalbard. Information on temporal trends is somewhat contradictory.(ABSTRACT TRUNCATED AT 400 WORDS)

In Vitro Hydrodynamic Assessment of a New Transcatheter Heart Valve Concept (the TRISKELE).

PubMed

Rahmani, Benyamin; Tzamtzis, Spyros; Sheridan, Rose; Mullen, Michael J; Yap, John; Seifalian, Alexander M; Burriesci, Gaetano

2017-04-01

This study presents the in vitro hydrodynamic assessment of the TRISKELE, a new system suitable for transcatheter aortic valve implantation (TAVI), aiming to mitigate the procedural challenges experienced with current technologies. The TRISKELE valve comprises three polymeric leaflet and an adaptive sealing cuff, supported by a novel fully retrievable self-expanding nitinol wire frame. Valve prototypes were manufactured in three sizes of 23, 26, and 29 mm by automated dip-coating of a biostable polymer, and tested in a hydrodynamic bench setup in mock aortic roots of 21, 23, 25, and 27 mm annulus, and compared to two reference valves suitable for equivalent implantation ranges: Edwards SAPIEN XT and Medtronic CoreValve. The TRISKELE valves demonstrated a global hydrodynamic performance comparable or superior to the controls with significant reduction in paravalvular leakage. The TRISKELE valve exhibits enhanced anchoring and improved sealing. The valve is currently under preclinical investigation.

Fibrin sealant: past, present, and future: a brief review.

PubMed

Spotnitz, William D

2010-04-01

Fibrin sealant is a two-component topical hemostat, sealant, and tissue adhesive consisting of fibrinogen and thrombin that has been used in the United States as a blood bank- or laboratory-derived product since the 1980s and has been commercially available since 1998. Initially, surgeons employed hospital-based materials because of the lack of availability of a commercially produced agent. At present, there are five U.S. Food and Drug Administration (FDA)-approved forms including products derived from pooled or autologous human plasma as well as bovine plasma. On-label indications include hemostasis, colonic sealing, and skin graft attachment. Recent clinical and experimental uses include tissue or mesh attachment, fistula closure, lymphatic sealing, adhesion prevention, drug delivery, and tissue engineering. The modern literature on fibrin sealant now exceeds 3000 articles and continues to expand. This brief review presents the history of this material, its present clinical use, and its future applications.

Electrochemical power-producing cell. [Li/Se

DOEpatents

Cairns, E.J.; Chilenskas, A.A.; Steunenberg, R.K.; Shimotake, H.

1972-05-30

An electrochemical power-producing cell including a molten lithium metal anode, a molten selenium metal cathode, a paste electrolyte separating the anode from the cathode, an anode current collector, and a single layer of niobium expanded metal formed in corrugated shape as cathode current collector is described. In addition, means are provided for sealing the anode and the cathode from loss of lithium and selenium, respectively, and an insulator is provided between the anode housing and the paste electrolyte disk.

Solar Thermochemical Fuel Production via a Novel Low Pressure, Magnetically Stabilized, Non-volatile Iron Oxide Looping Process (University of Florida)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hahn, David W.

The UF Solar Fuels team has developed a modular reactor at the 10kW scale for the thermochemical conversion of H2O and CO2 to H2 and CO, respectively, using concentrated solar energy to drive high-temperature redox reactions. Various materials, including ferrites, doped and mixed metal ferrites, and ceria, were investigated and reported on. Ceria was chosen as the reactive material, with thermogravimetric and bench-scale analysis concurring with literature review and pointing towards reasonable kinetics and stability at temperatures on the order of 1500 °C. A combined radiation, conduction, and species reaction/mass transport model was developed, utilizing Monte Carlo ray tracing, Latticemore » Boltzmann, and random walk particle tracking for the respective components to direct development and optimization of the reactor. With experimental data used for reaction rates, the model showed a path to efficiencies >20%, which could be market competitive with current PV-hydrolysis hydrogen generation systems. Economic analysis of a larger-scale plant (100kW modular system with cost performed at 500 modules) has been performed, assuming 0.5% and 10% internal rate of return. Without compression costs, H2 production cost using this is technology at $12/kg H2 and $17/kg H2 for realized efficiencies of 20% and 15%, respectively. An interaction of ceria and alumina, with the formation of CeAlO3 occurring at ~1700 °C, had been reported in the literature, but the UF Solar Fuels team observed and reported on it at a large scale, confirming its presence as an engineering consideration when working ceria and alumina at extreme temperatures. CeAlO3 could be being produced at lower temperatures due to the oxidation and reducing environments or due to local hotspots in the reactor. A solar thermogravimeter was developed, to take advantage of the high heating rates available at the UF Solar Simulator Facility to allow investigation of species evolution and material stability in extreme heating rate scenarios. A novel flash-boiling centrifugal-separation steam generator was developed to provide inexpensive, identical steam flows to modular systems, using water-metering and generating the steam for each flow in separate chambers. Several novel methods of reactant material preparation were developed, including: • Sacrificial Pore Formation - Uses a component, such as graphite, designed to be carried away in gaseous form at some point in the preparation process to aid in the formation of pathways and porosity for the enhancement of fluid flow and radiative heat transport at elevated temperatures. • Particle stacking and sintering – Using material that has been pre-sintered (at the temperatures expected for reaction) and mechanically broken apart. The particles are then separated by size to allow the process to be repeated several times with a given particle size range. The resulting stacked and sintered structure maintains micro- to millimeter size pore structure for fluid transport at temperatures that previously demonstrated some contraction or collapse of the reactive material due to porosity reduction due to sintering. In addition, novel seals utilizing graphite and boron nitride particle filler as an internally compressed seal were developed. These seals allow sealing of a ceramic Efficiencies of >4% solar-to-fuel were demonstrated, which at the time of demonstration was the highest yet reported. Hydrogen and CO production rates targets that averaged ~3 cc/gram of reactive material were achieved.« less

Process and targets for production of no-carrier-added radiotin

DOEpatents

Srivastava, Suresh C; Zhuikov, Boris Leonidovich; Ermolaev, Stanislav Victorovich; Konyakhin, Nikolay Alexandrovich; Kokhanyuk, Vladimir Mikhailovich; Khamyanov, Stepan Vladimirovich; Togaeva, Natalya Roaldovna

2014-04-22

One embodiment of the present invention includes a process for production and recovery of no-carrier-added radioactive tin (NCA radiotin). An antimony target can be irradiated with a beam of accelerated particles forming NCA radiotin, followed by separation of the NCA radiotin from the irradiated target. The target is metallic Sb in a hermetically sealed shell. The shell can be graphite, molybdenum, or stainless steel. The irradiated target can be removed from the shell by chemical or mechanical means, and dissolved in an acidic solution. Sb can be removed from the dissolved irradiated target by extraction. NCA radiotin can be separated from the remaining Sb and other impurities using chromatography on silica gel sorbent. NCA tin-117m can be obtained from this process. NCA tin-117m can be used for labeling organic compounds and biological objects to be applied in medicine for imaging and therapy of various diseases.

Bronchobiliary Fistula Treated by Self-expanding ePTFE-Covered Nitinol Stent-Graft

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gandini, Roberto; Konda, Daniel; Tisone, Giuseppe

A 71-year-old man, who had undergone right hepatectomy extended to the caudate lobe with terminolateral Roux-en-Y left hepatojejunostomy for a Klatskin tumor, developed bilioptysis 3 weeks postoperatively due to bronchobiliary fistula. Percutaneous transhepatic cholangiography revealed a non-dilated biliary system with contrast medium extravasation to the right subphrenic space through a resected anomalous right posterior segmental duct. After initial unsuccessful internal-external biliary drainage, the fistula was sealed with a VIATORR covered self-expanding nitinol stent-graft placed with its distal uncovered region in the hepatojejunal anastomosis and the proximal ePTFE-lined region in the left hepatic duct. A 10-month follow-up revealed no recurrence ofmore » bilioptysis and confirmed the complete exclusion of the bronchobiliary fistula.« less

In situ growth of TiO2 in interlayers of expanded graphite for the fabrication of TiO2-graphene with enhanced photocatalytic activity.

PubMed

Jiang, Baojiang; Tian, Chungui; Zhou, Wei; Wang, Jianqiang; Xie, Ying; Pan, Qingjiang; Ren, Zhiyu; Dong, Youzhen; Fu, Dan; Han, Jiale; Fu, Honggang

2011-07-18

We present a facile route for the preparation of TiO(2)-graphene composites by in situ growth of TiO(2) in the interlayer of inexpensive expanded graphite (EG) under solvothermal conditions. A vacuum-assisted technique combined with the use of a surfactant (cetyltrimethylammonium bromide) plays a key role in the fabrication of such composites. Firstly, the vacuum environment promotes full infusion of the initial solution containing Ti(OBu)(4) and the surfactant into the interlayers of EG. Subsequently, numerous TiO(2) nanoparticles uniformly grow in situ in the interlayers with the help of the surfactant, which facilitates the exfoliation of EG under the solvothermal conditions in ethanol, eventually forming TiO(2)-graphene composites. The as-prepared samples have been characterized by Raman and FTIR spectroscopies, SEM, TEM, AFM, and thermogravimetic analysis. It is shown that a large number of TiO(2) nanoparticles homogeneously cover the surface of high-quality graphene sheets. The graphene exhibits a multi-layered structure (5-7 layers). Notably, the TiO(2)-graphene composite (only 30 wt % of which is TiO(2)) synthesized by subsequent thermal treatment at high temperature under nitrogen shows high photocatalytic activity in the degradation of phenol under visible and UV lights in comparison with bare Degussa P25. The enhanced photocatalytic performance is attributed to increased charge separation, improved light absorbance and light absorption width, and high adsorptivity for pollutants. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Visible-light-driven, water-surface-floating antimicrobials developed from graphitic carbon nitride and expanded perlite for water disinfection.

PubMed

Zhang, Chi; Li, Yi; Shuai, Danmeng; Zhang, Wenlong; Niu, Lihua; Wang, Longfei; Zhang, Huanjun

2018-05-28

Waterborne pathogens, especially bacteria and viruses, pose significant health risks to the public, calling for the development of a sustainable, efficient, and robust disinfection strategy with reduced energy footprint and minimized byproduct formation. Here, we developed a sustainable photocatalytic composite for antimicrobial applications by integrating visible-light-responsive graphitic carbon nitride (g-C 3 N 4 ) with low-density porous expanded perlite (EP) mineral, and g-C 3 N 4 /EP-520 showed a high specific surface area of 45.3 m 2 /g and optimum performance for disinfection. g-C 3 N 4 /EP-520 achieved 8-log inactivation of E. coli and MS2 under 180 and 240 min visible-light irradiation without stirring, respectively. Water quality parameters were found to influence the disinfection performance of g-C 3 N 4 /EP-520: MS2 inactivation was promoted with the increase of dissolved oxygen (DO), proton concentration, salinity (NaCl), and hardness (Ca 2+ ). Importantly, g-C 3 N 4 /EP-520 could fully inactivate MS2 in a real source water sample with prolonged light irradiation, and negligible activity loss was observed in recycle use, demonstrating its viability and robustness for waterborne pathogen removal. Antimicrobial mechanisms of g-C 3 N 4 /EP-520 were systemically evaluated by radical scavenger addition, and revealed that the inactivation behavior was dependent on the type of microorganisms. Microscopic analyses confirmed that the destruction of bacterial cells and viral particles, leading to the inactivation of microorganisms. Copyright © 2018 Elsevier Ltd. All rights reserved.

Sodern development of a high LIDT laser beam expander for ATLID

NASA Astrophysics Data System (ADS)

Battarel, Denis C.; Barnasson, Elodie

2017-11-01

Sodern has been contracted for the development of the laser beam expander used on the lidar of the ATLID instrument developed by Airbus Defence & Space France and Germany (Formerly ASTRIUM) embarked on the EathCARE satellite, element of the ESA (European Space Agency) Living Planet Programme. The ATLID emission beam expander (E-BEX) has two functions: one is to reduce the divergence of the laser in order to achieve a high spatial resolution and the other is to enlarge the laser beam to reduce the power density and thus reduce Laser Induced Contamination (LIC) and Laser Induced Damage Threshold (LIDT) effects on the outer surface exposed to vacuum. This paper exposes the design drivers of the beam expander which are: having optical components withstanding very high laser fluence at a wavelength of 355nm and exhibiting a very low depolarization ratio., hermetically sealing the cavity with metallic gaskets in order to keep the pressure constant so that beam collimation is not affected, choosing housing material compatible with both hermiticity requirements and thermal control. To obtain a high spatial resolution on Earth, ATLID requires a means for controlling beam collimation. This is ensured by an active thermal control on the beam expander in order to change its Wavefront Error (WFE) by a few tens of nanometers.

Study on the cutting mechanism and the brittle ductile transition model of isotropic pyrolyric graphite

NASA Astrophysics Data System (ADS)

Wang, Minghai; Wang, Hujun; Liu, Zhonghai

2011-05-01

Isotropic pyrolyric graphite (IPG) is a new kind of brittle material, it can be used for sealing the aero-engine turbine shaft and the ethylene high-temperature equipment. It not only has the general advantages of ordinal carbonaceous materials such as high temperature resistance, lubrication and abrasion resistance, but also has the advantages of impermeability and machinability that carbon/carbon composite doesn't have. Therefore, it has broad prospects for development. Mechanism of brittle-ductile transition of IPG is the foundation of precision cutting while the plastic deformation of IPG is the essential and the most important mechanical behavior of precision cutting. Using the theory of strain gradient, the mechanism of this material removal during the precision cutting is analyzed. The critical cutting thickness of IPG is calculated for the first time. Furthermore, the cutting process parameters such as cutting depth, feed rate which corresponding to the scale of brittle-ductile transition deformation of IPG are calculated. In the end, based on the theory of micromechanics, the deformation behaviors of IPG such as brittle fracture, plastic deformation and mutual transformation process are all simulated under the Sih.G.C fracture criterion. The condition of the simulation is that the material under the pressure-shear loading conditions .The result shows that the best angle during the IPG precision cutting is -30°. The theoretical analysis and the simulation result are validated by precision cutting experiments.

Novel approach to microwave-assisted extraction and micro-solid-phase extraction from soil using graphite fibers as sorbent.

PubMed

Xu, Li; Lee, Hian Kee

2008-05-30

A single-step extraction-cleanup procedure involving microwave-assisted extraction (MAE) and micro-solid-phase extraction (micro-SPE) has been developed for the analysis of polycyclic aromatic hydrocarbons (PAHs) from soil samples. Micro-SPE is a relatively new extraction procedure that makes use of a sorbent enclosed within a sealed polypropylene membrane envelope. In the present work, for the first time, graphite fiber was used as a sorbent material for extraction. MAE-micro-SPE was used to cleanup sediment samples and to extract and preconcentrate five PAHs in sediment samples prepared as slurries with addition of water. The best extraction conditions comprised of microwave heating at 50 degrees C for a duration of 20 min, and an elution (desorption) time of 5 min using acetonitrile with sonication. Using gas chromatography (GC)-flame ionization detection (FID), the limits of detection (LODs) of the PAHs ranged between 2.2 and 3.6 ng/g. With GC-mass spectrometry (MS), LODs were between 0.0017 and 0.0057 ng/g. The linear ranges were between 0.1 and 50 or 100 microg/g for GC-FID analysis, and 1 and 500 or 1000 ng/g for GC-MS analysis. Granular activated carbon was also used for the micro-SPE device but was found to be not as efficient in the PAH extraction. The MAE-micro-SPE method was successfully used for the extraction of PAHs in river and marine sediments, demonstrating its applicability to real environmental solid matrixes.

Orbit Transfer Vehicle (OTV) advanced expander cycle engine point design study. Volume 2: Study results

NASA Technical Reports Server (NTRS)

1980-01-01

Detailed computer models of the engine were developed to predict both the steady state and transient operation of the engine system. Mechanical design layout drawings were prepared for the following components: thrust chamber and nozzle; extendible nozzle actuating mechanism and seal; LOX turbopump and boost pump; hydrogen turbopump and boost pump; and the propellant control valves. The necessary heat transfer, stress, fluid flow, dynamic, and performance analyses were performed to support the mechanical design.

Packer arrangements for oil wells and the like

DOEpatents

Harvey, Andrew C.; McFadden, David H.

1981-11-24

The packer includes an elongated tubular casing, and a metal ring is disposed in its entirety within an annular recess in the casing. The recess has a circumferential opening extending entirely around the peripheral outer surface of the casing. Hydraulic fluid is flowed into the recess to apply pressure to the inner peripheral surface of the metal ring to expand the ring radially outwardly and force its outer peripheral surface through the circumferential opening and into annular sealing engagement with the opposed surface of the well casing.

The design of a small linear-resonant, split Stirling cryogenic refrigerator compressor

NASA Technical Reports Server (NTRS)

Ackermann, R. A.

1985-01-01

The development of a small linear-resonant compressor for use in a 1/4-watt, 78K, split Stirling cryogenic refrigerator is discussed. The compressor contains the following special features: (1) a permanent-magnet linear motor; (2) resonant dynamics; (3) dynamic balancing; and (4) a close-clearance seal between the compressor piston and cylinder. This paper describes the design of the compressor, and presents component test data and system test data for the compressor driving a 1/4-watt expander.

Structures and electrochemical performances of pyrolized carbons from graphite oxides for electric double-layer capacitor

NASA Astrophysics Data System (ADS)

Kim, Ick-Jun; Yang, Sunhye; Jeon, Min-Je; Moon, Seong-In; Kim, Hyun-Soo; Lee, Yoon-Pyo; An, Kye-Hyeok; Lee, Young-Hee

The structural features and the electrochemical performances of pyrolized needle cokes from oxidized cokes are examined and compared with those of KOH-activated needle coke. The structure of needle coke is changed to a single phase of graphite oxide after oxidation treatment with an acidic solution having an NaClO 3/needle coke composition ratio of above 7.5, and the inter-layer distance of the oxidized needle coke is expanded to 6.9 Å with increasing oxygen content. After heating at 200 °C, the oxidized needle coke is reduced to a graphite structure with an inter-layer distance of 3.6 Å. By contrast, a change in the inter-layer distance in KOH-activated needle coke is not observed. An intercalation of pyrolized needle coke, observed on first charge, occurs at 1.0 V. This value is lower than that of KOH-activation needle coke. A capacitor using pyrolized needle coke exhibits a lower internal resistance of 0.57 Ω in 1 kHz, and a larger capacitance per weight and volume of 30.3 F g -1 and 26.9 F ml -1, in the two-electrode system over the potential range 0-2.5 V compared with those of a capacitor using KOH-activation of needle coke. This better electrochemical performance is attributed to a distorted graphene layer structure derived from the process of the inter-layer expansion and shrinkage.

Bioinspired Mesoporous Chiral Nematic Graphitic Carbon Nitride Photocatalysts modulated by Polarized Light.

PubMed

Lin, Wensheng; Hong, Wei; Sun, Lu; Yu, Di; Yu, Dingshan; Chen, Xudong

2018-01-10

Endowing materials with chirality and exploring the responses of the material under circularly polarized light (CPL) can enable further insight into the physical and chemical properties of the semiconductors to be gained, thus expanding on optoelectronic applications. Herein a bioinspired mesoporous chiral nematic graphitic carbon nitride (g-C 3 N 4 ) for efficient hydrogen evolution with polarized light modulation based on chiral nematic cellulose nanocrystal films prepared through silica templating is described. The mesoporous nematic chiral g-C 3 N 4 exhibits an ultrahigh hydrogen evolution rate of 219.9 μmol h -1 (for 20 mg catalyst), corresponding to a high enhancement factor of 55 when compared to the bulk g-C 3 N 4 under λ>420 nm irradiation. Furthermore, the chiral g-C 3 N 4 material exhibits unique photocatalytic activity modulated by CPL within the absorption region. This CPL-assisted photocatalytic regulation strategy holds great promise for a wide range of applications including optical devices, asymmetric photocatalysis, and chiral recognition/separation. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Bending fracture in carbon nanotubes.

PubMed

Kuo, Wen-Shyong; Lu, Hsin-Fang

2008-12-10

A novel approach was adopted to incur bending fracture in carbon nanotubes (CNTs). Expanded graphite (EG) was made by intercalating and exfoliating natural graphite flakes. The EG was deposited with nickel particles, from which CNTs were grown by chemical vapor deposition. The CNTs were tip-grown, and their roots were fixed on the EG flakes. The EG flakes were compressed, and many CNTs on the surface were fragmented due to the compression-induced bending. Two major modes of the bending fracture were observed: cone-shaped and shear-cut. High-resolution scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to examine the crack growth within the graphene layers. The bending fracture is characterized by two-region crack growth. An opening crack first appears around the outer-tube due to the bending-induced tensile stress. The crack then branches to grow along an inclined direction toward the inner-tube due to the presence of the shear stress in between graphene layers. An inner-tube pullout with inclined side surface is formed. The onset and development of the crack in these two regions are discussed.

Non-Pyrotechnic Zero-Leak Normally Closed Valve

NASA Technical Reports Server (NTRS)

Gillespie, Rebecca

2010-01-01

This valve is designed to create a zero-leak seal in a liquid propulsion system that is a functional replacement for the normally closed pyrovalve. Unlike pyrovalves, Nitinol is actuated by simply heating the material to a certain temperature, called the transition temperature. Like a pyrovalve, before actuation, the upstream and downstream sections are separated from one another and from the external environment by closed welded seals. Also like pyrovalves, after actuation, the propellant or pressurant gas can flow without a significant pressure drop but are still separated from the external environment by a closed welded seal. During manufacture, a Nitinol bar is compressed to 93 percent of its original length and fitted tightly into the valve. During operation, the valve is heated until the Nitinol reaches the transition temperature of 95 C; the Nitinol "remembers" its previous longer shape with a very large recovery force causing it to expand and break the titanium parent metal seal to allow flow. Once open, the valve forever remains open. The first prototype valve was designed for high pressure [5,000 psi (=34.5 MPa)] and low flow, typical requirements for pressurant gas valves in liquid propulsion systems. It is possible to modify the dimensions to make low-pressure models or high-flow models, for use downstream of the propellant tanks. This design is simpler, lower risk, and less expensive than the pyrovalve. Although the valve must be in a thermally controlled state (kept below 80 C) to prevent premature actuation, the pyrovalves and electrically actuated initiators have far more taxing handling requirements.

Rotordynamic Instability Problems in High-Performance Turbomachinery 1996

NASA Technical Reports Server (NTRS)

1997-01-01

The first rotordynamics workshop proceedings emphasized a feeling of uncertainty in predicting the stability of characteristics of high-performance turbomachinery. In the second workshop proceedings these uncertainties were reduced through programs established to systematically resolve problems, with emphasis on experimental validation of the forces that influence rotordynamics. In the third proceedings many programs for predicting or measuring forces and force coefficients in high-performance turbomachinery produced results. Data became available for designing new machines with enhanced stability characteristics or for upgrading existing machines. In the fourth proceedings there emerged trends towards a more unified view of rotordynamic instability problems and several encouraging new analytical developments. The fifth workshop supported the continuing trend toward a unified view with several new developments in the design and manufacture of new turbomachineries with enhanced stability characteristics along with new data and associated numerical/theoretical results. The sixth workshop report provided field experience and experimental results, and expanded the use of computational and control techniques with integration of damper, bearing, and eccentric seal operation results. The seventh workshop report provided field experiences, numerical, theoretical, and experimental results and control methods for seals, bearings, and dampers with some attention given to variable thermophysical properties and turbulence measurements, and introduction of two-phase flow results. In the present workshop, active magnetic bearings (AMB's) evolve into a new method of measuring rotordynamic coefficients with discussions on honeycomb seals, drop of magnetically supported rotors, seals, bearings and dampers with new data being reported. The intent of the workshop and this proceedings is to provide a continuing impetus for an understanding and resolution of these problems.

Anode materials for electrochemical waste destruction

NASA Technical Reports Server (NTRS)

Molton, Peter M.; Clarke, Clayton

1990-01-01

Electrochemical Oxidation (ECO) offers promise as a low-temperature, atmospheric pressure method for safe destruction of hazardous organic chemical wastes in water. Anode materials tend to suffer corrosion in the intensely oxidizing environment of the ECO cell. There is a need for cheaper, more resistant materials. In this experiment, a system is described for testing anode materials, with examples of several common anodes such as stainless steel, graphite, and platinized titanium. The ECO system is simple and safe to operate and the experiment can easily be expanded in scope to study the effects of different solutions, temperatures, and organic materials.

Resistence seam welding thin copper foils

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hollar, D.L. Jr.

1991-02-01

Use of flat flexible circuits in the electronics industry is expanding. The term flexible circuits'' is defined here as copper foil which has been bonded to an insulating film such as Kapton film. The foil is photo processed to produce individual circuit paths similar to printed circuit boards. Another insulating film is laminated over the conductors to complete the flexible circuit. Flexible circuits, like multiwire cables, are susceptible to electromagnetic radiation (EMR) interference. On multiwire cables the interference problem is mitigated by adding a woven wire braid shielding over the conductors. Shielding on flexible circuits is accomplished by enclosing themore » circuits in a copper foil envelope. However, the copper foil must be electrically sealed around the flexcircuit to be effective. Ultimately, a resistance seam welding process and appropriate equipment were developed which would provide the required electrical seal between two layers of 2-oz (0.0028-inch thick) copper foil on a 1.1-inch wide, 30-inch long, 0.040-inch thick flexible circuit. 4 refs., 19 figs.« less

Actuator device utilizing a conductive polymer gel

DOEpatents

Chinn, Douglas A.; Irvin, David J.

2004-02-03

A valve actuator based on a conductive polymer gel is disclosed. A nonconductive housing is provided having two separate chambers separated by a porous frit. The conductive polymer is held in one chamber and an electrolyte solution, used as a source of charged ions, is held in the second chamber. The ends of the housing a sealed with a flexible elastomer. The polymer gel is further provide with electrodes with which to apply an electrical potential across the gel in order to initiate an oxidation reaction which in turn drives anions across the porous frit and into the polymer gel, swelling the volume of the gel and simultaneously contracting the volume of the electrolyte solution. Because the two end chambers are sealed the flexible elastomer expands or contracts with the chamber volume change. By manipulating the potential across the gel the motion of the elastomer can be controlled to act as a "gate" to open or close a fluid channel and thereby control flow through that channel.

Vaccine vial stopper performance for fractional dose delivery of vaccines.

PubMed

Jarrahian, Courtney; Myers, Daniel; Creelman, Ben; Saxon, Eugene; Zehrung, Darin

2017-07-03

Shortages of vaccines such as inactivated poliovirus and yellow fever vaccines have been addressed by administering reduced-or fractional-doses, as recommended by the World Health Organization Strategic Advisory Group of Experts on Immunization, to expand population coverage in countries at risk. We evaluated 3 kinds of vaccine vial stoppers to assess their performance after increased piercing from repeated withdrawal of doses needed when using fractional doses (0.1 mL) from presentations intended for full-dose (0.5 mL) delivery. Self-sealing capacity and fragmentation of the stopper were assessed via modified versions of international standard protocols. All stoppers maintained self-sealing capacity after 100 punctures. The damage to stoppers measured as the fragmentation rate was within the target of ≤ 10% of punctures resulting in a fragment after as many as 50 punctures. We concluded that stopper failure is not likely to be a concern if existing vaccine vials containing up to 10 regular doses are used up to 50 times for fractional dose delivery.

Ceramic tile expansion engine housing

DOEpatents

Myers, Blake

1995-01-01

An expandable ceramic tile housing for a high temperature engine is disclosed wherein each tile is independently supported in place in an interlocking matrix by retention mechanisms which mechanically couple the individual ceramic tiles to an outer metal support housing while maintaining thermal isolation of the metal housing from the ceramic tiles. The ceramic tiles are formed with either an octagonal front face portion and a square shank portion or a square front face portion with an octagonal shank portion. The length of the sides of the octagonal front face portion on one tile is equal to the length of the sides of the square front face portion of adjoining tiles to permit formation of an interlocking matrix. Fibrous ceramic sealing material may be placed between radial and tangential facing surfaces of adjacent tiles to limit radial gas flow therebetween. Labyrinth-sealed pressure-controlled compartments may be established between the tile housing and the outer metal support housing to control radial gas flow.

Ceramic tile expansion engine housing

DOEpatents

Myers, B.

1995-04-11

An expandable ceramic tile housing for a high temperature engine is disclosed wherein each tile is independently supported in place in an interlocking matrix by retention mechanisms which mechanically couple the individual ceramic tiles to an outer metal support housing while maintaining thermal isolation of the metal housing from the ceramic tiles. The ceramic tiles are formed with either an octagonal front face portion and a square shank portion or a square front face portion with an octagonal shank portion. The length of the sides of the octagonal front face portion on one tile is equal to the length of the sides of the square front face portion of adjoining tiles to permit formation of an interlocking matrix. Fibrous ceramic sealing material may be placed between radial and tangential facing surfaces of adjacent tiles to limit radial gas flow there between. Labyrinth-sealed pressure-controlled compartments may be established between the tile housing and the outer metal support housing to control radial gas flow. 8 figures.

Seal Technology Development for Advanced Component for Airbreathing Engines

NASA Technical Reports Server (NTRS)

Snyder, Philip H.

2008-01-01

Key aspects of the design of sealing systems for On Rotor Combustion/Wave Rotor (ORC/WR) systems were addressed. ORC/WR systems generally fit within a broad class of pressure gain Constant Volume Combustors (CVCs) or Pulse Detonation Combustors (PDCs) which are currently being considered for use in many classes of turbine engines for dramatic efficiency improvement. Technology readiness level of this ORC/WR approaches are presently at 2.0. The results of detailed modeling of an ORC/WR system as applied to a regional jet engine application were shown to capture a high degree of pressure gain capabilities. The results of engine cycle analysis indicated the level of specific fuel consumption (SFC) benefits to be 17 percent. The potential losses in pressure gain due to leakage were found to be closely coupled to the wave processes at the rotor endpoints of the ORC/WR system. Extensive investigation into the sealing approaches is reported. Sensitivity studies show that SFC gains of 10 percent remain available even when pressure gain levels are highly penalized. This indicates ORC/WR systems to have a high degree of tolerance to rotor leakage effects but also emphasizes their importance. An engine demonstration of an ORC/WR system is seen as key to progressing the TRL of this technology. An industrial engine was judged to be a highly advantageous platform for demonstration of a first generation ORC/WR system. Prior to such a demonstration, the existing NASA pressure exchanger wave rotor rig was identified as an opportunity to apply both expanded analytical modeling capabilities developed within this program and to identify and fix identified leakage issues existing within this rig. Extensive leakage analysis of the rig was performed and a detailed design of additional sealing strategies for this rig was generated.

A novel approach to quantifying the spatiotemporal behavior of instrumented grey seals used to sample the environment.

PubMed

Baker, Laurie L; Mills Flemming, Joanna E; Jonsen, Ian D; Lidgard, Damian C; Iverson, Sara J; Bowen, W Don

2015-01-01

Paired with satellite location telemetry, animal-borne instruments can collect spatiotemporal data describing the animal's movement and environment at a scale relevant to its behavior. Ecologists have developed methods for identifying the area(s) used by an animal (e.g., home range) and those used most intensely (utilization distribution) based on location data. However, few have extended these models beyond their traditional roles as descriptive 2D summaries of point data. Here we demonstrate how the home range method, T-LoCoH, can be expanded to quantify collective sampling coverage by multiple instrumented animals using grey seals (Halichoerus grypus) equipped with GPS tags and acoustic transceivers on the Scotian Shelf (Atlantic Canada) as a case study. At the individual level, we illustrate how time and space-use metrics quantifying individual sampling coverage may be used to determine the rate of acoustic transmissions received. Grey seals collectively sampled an area of 11,308 km (2) and intensely sampled an area of 31 km (2) from June-December. The largest area sampled was in July (2094.56 km (2)) and the smallest area sampled occurred in August (1259.80 km (2)), with changes in sampling coverage observed through time. T-LoCoH provides an effective means to quantify changes in collective sampling effort by multiple instrumented animals and to compare these changes across time. We also illustrate how time and space-use metrics of individual instrumented seal movement calculated using T-LoCoH can be used to account for differences in the amount of time a bioprobe (biological sampling platform) spends in an area.

Water-level sensor and temperature-profile detector

DOEpatents

Not Available

1981-01-29

A temperature profile detector is described which comprises a surrounding length of metal tubing and an interior electrical conductor both constructed of high temperature high electrical resistance materials. A plurality of gas-filled expandable bellows made of electrically conductive material are positioned at spaced locations along a length of the conductors. The bellows are sealed and contain a predetermined volume of a gas designed to effect movement of the bellows from an open circuit condition to a closed circuit condition in response to monitored temperature changes sensed by each bellows.

Water level sensor and temperature profile detector

DOEpatents

Tokarz, Richard D.

1983-01-01

A temperature profile detector comprising a surrounding length of metal tubing and an interior electrical conductor both constructed of high temperature high electrical resistance materials. A plurality of gas-filled expandable bellows made of electrically conductive material is electrically connected to the interior electrical conductor and positioned within the length of metal tubing. The bellows are sealed and contain a predetermined volume of a gas designed to effect movement of the bellows from an open circuit condition to a closed circuit condition in response to monitored temperature changes sensed by each bellows.

Laser excited atomic fluorescence spectrometry as a powerful tool for analytical applications and spectroscopic studies

NASA Astrophysics Data System (ADS)

Gornushkin, Igor B.

1997-12-01

Laser-excited atomic fluorescence spectrometry (LEAFS) with a novel diffusive tube electrothermal atomizer (ETA) has been used for the study of atomization and diffusion processes and for the direct trace analysis of complex matrices. A novel ETA was a graphite tube sealed by two graphite electrodes. A sample was introduced into the tube and the furnace assembly was heated. The vaporized sample diffused through the hot graphite and the atomic fraction of the vapor was excited by a tunable dye laser above the tube. Temporal behavior of atomic fluorescence of Cu, Ag, and Ni atoms, diffused through the furnace tube, was studied at different temperatures; the values for activation energies and diffusion coefficients were derived on the basis of the diffusion/vaporization kinetic model. The femtogram/nanogram concentrations of silver were determined in coastal Atlantic water and soil samples. Use of the new ETA resulted in significant reduction of matrix interferences, ultra-low limits of detection, good accuracy and precision. LEAFS coupled with laser ablation (LA) was studied in terms of its analytical and spectroscopic potential. Low concentrations of lead (0.15 ppm-750 ppm) in metallic matrices (copper, brass, steel, and zinc) were measured in a low pressure argon atmosphere. No matrix effect was observed, providing a universal calibration curve for all samples. A limit of detection of 22 ppb (0.5 fg) was achieved. Also, the lifetime of the metastable 6p21D level of lead was measured and found to be in good agreement with the literature data. A simple open-air LA-LEAFS system was used for the determination of cobalt in solid matrices (graphite, soil, and steel). The fluorescence of cobalt was excited from a level which was already populated in the ablation plasma and was monitored at the Stokes-shifted wavelength. Detection limits in the ppb to ppm range and linearity over four orders of magnitude were achieved. The resonance shadowgraph technique has been developed for time-resolved imaging of laser-produced plasmas. The shadowgraphs were obtained by igniting the plasma on the lead or tin surface and by illuminating the plasma by a laser tuned in resonance with a strong atomic transition. UV-photodecomposition of lead and tin clusters was visualized. The evolution of the plasmas was studied at different pressures of argon. A shock wave produced by the laser ablation was monitored and its speed was measured.

Expanded study of feasibility of measuring in-flight 747/JT9D loads, performance, clearance, and thermal data

NASA Technical Reports Server (NTRS)

Sallee, G. P.; Martin, R. L.

1980-01-01

The JT9D jet engine exhibits a TSFC loss of about 1 percent in the initial 50 flight cycles of a new engine. These early losses are caused by seal-wear induced opening of running clearances in the engine gas path. The causes of this seal wear have been identified as flight induced loads which deflect the engine cases and rotors, causing the rotating blades to rub against the seal surfaces, producing permanent clearance changes. The real level of flight loads encountered during airplane acceptance testing and revenue service and the engine's response in the dynamic flight environment were investigated. The feasibility of direct measurement of these flight loads and their effects by concurrent measurement of 747/JT9D propulsion system aerodynamic and inertia loads and the critical engine clearance and performance changes during 747 flight and ground operations was evaluated. A number of technical options were examined in relation to the total estimated program cost to facilitate selection of the most cost effective option. It is concluded that a flight test program meeting the overall objective of determining the levels of aerodynamic and inertia load levels to which the engine is exposed during the initial flight acceptance test and normal flight maneuvers is feasible and desirable. A specific recommended flight test program, based on the evaluation of cost effectiveness, is defined.

Shock Initiation of Thermally Expanded TATB

NASA Astrophysics Data System (ADS)

Mulford, Roberta; Swift, Damian

2011-06-01

The plastic-bonded explosive PBX-9502 undergoes unusual hysteretic thermal expansion, or ``ratchet growth'' as a consequence of the uniaxial thermal expansion of the graphitic structure of the major component, TATB explosive. Upon thermal cycling, the density of the material can be reduced by as much as 9%, resulting in a distinct increase in the shock sensitivity of the solid. Run distances to detonation have been measured in thermally expanded samples of PBX-9502, using embedded particle velocity gauges and shock tracker gauges. Uniaxial shocks were generated using a light gas gun, to provide a repeatable stimulus for initiation of detonation. We have applied a porosity model to adjust standard Pop plot data to the reduced density of our samples, to investigate whether the sensitivity of the PBX 9502 increases ideally with the decreasing density, or whether the microscopically non-uniform expansion that occurs during ``ratchet growth'' leads to abnormal sensitivity, possibly as a result of cracking or debonding from the binder, as observed in micrographs of the sample.

Prevalence of algal toxins in Alaskan marine mammals foraging in a changing arctic and subarctic environment.

PubMed

Lefebvre, Kathi A; Quakenbush, Lori; Frame, Elizabeth; Huntington, Kathy Burek; Sheffield, Gay; Stimmelmayr, Raphaela; Bryan, Anna; Kendrick, Preston; Ziel, Heather; Goldstein, Tracey; Snyder, Jonathan A; Gelatt, Tom; Gulland, Frances; Dickerson, Bobette; Gill, Verena

2016-05-01

Current climate trends resulting in rapid declines in sea ice and increasing water temperatures are likely to expand the northern geographic range and duration of favorable conditions for harmful algal blooms (HABs), making algal toxins a growing concern in Alaskan marine food webs. Two of the most common HAB toxins along the west coast of North America are the neurotoxins domoic acid (DA) and saxitoxin (STX). Over the last 20 years, DA toxicosis has caused significant illness and mortality in marine mammals along the west coast of the USA, but has not been reported to impact marine mammals foraging in Alaskan waters. Saxitoxin, the most potent of the paralytic shellfish poisoning toxins, has been well-documented in shellfish in the Aleutians and Gulf of Alaska for decades and associated with human illnesses and deaths due to consumption of toxic clams. There is little information regarding exposure of Alaskan marine mammals. Here, the spatial patterns and prevalence of DA and STX exposure in Alaskan marine mammals are documented in order to assess health risks to northern populations including those species that are important to the nutritional, cultural, and economic well-being of Alaskan coastal communities. In this study, 905 marine mammals from 13 species were sampled including; humpback whales, bowhead whales, beluga whales, harbor porpoises, northern fur seals, Steller sea lions, harbor seals, ringed seals, bearded seals, spotted seals, ribbon seals, Pacific walruses, and northern sea otters. Domoic acid was detected in all 13 species examined and had the greatest prevalence in bowhead whales (68%) and harbor seals (67%). Saxitoxin was detected in 10 of the 13 species, with the highest prevalence in humpback whales (50%) and bowhead whales (32%). Pacific walruses contained the highest concentrations of both STX and DA, with DA concentrations similar to those detected in California sea lions exhibiting clinical signs of DA toxicosis (seizures) off the coast of Central California, USA. Forty-six individual marine mammals contained detectable concentrations of both toxins emphasizing the potential for combined exposure risks. Additionally, fetuses from a beluga whale, a harbor porpoise and a Steller sea lion contained detectable concentrations of DA documenting maternal toxin transfer in these species. These results provide evidence that HAB toxins are present throughout Alaska waters at levels high enough to be detected in marine mammals and have the potential to impact marine mammal health in the Arctic marine environment. Published by Elsevier B.V.

A New Merit Function for Evaluating the Flaw Tolerance of Composite Laminates. Pt. 2; Arbitrary Size Holes and Center Cracks

NASA Technical Reports Server (NTRS)

Mikulas, Martin M., Jr.; Sumpter, Rod

1999-01-01

In a previous paper, a new merit function for determining the strength performance of flawed composite laminates was presented. This previous analysis was restricted to circular hole flaws that were large enough that failure could be predicted using the laminate stress concentration factor. In this paper, the merit function is expanded to include the flaw cases of an arbitrary size circular hole or a center crack. Failure prediction for these cases is determined using the point stress criterion. An example application of the merit function is included for a wide range of graphite/epoxy laminates.

A New Merit Function for Evaluating the Flaw Tolerance of Composite Laminates. Part 2; Arbitrary Size Holes and Center Cracks

NASA Technical Reports Server (NTRS)

Martin, Mikulas M., Jr.; Sumpter, Rod

2000-01-01

In a previous paper, a new merit function for determining the strength performance of flawed composite laminates was presented. This previous analysis was restricted to circular hole flaws that were large enough that failure could be predicted using the laminate stress concentration factor. In this paper, the merit function is expanded to include the flaw cases of an arbitrary size circular hole or center crack. Failure prediction for these cases is determined using the point stress criterion. An example application of the merit function is included for a wide range of graphite/epoxy laminates.

A New Merit Function for Evaluating the Flaw Tolerance of Composite Laminates. Part 2; Arbitrary Size Holes and Center Cracks

NASA Technical Reports Server (NTRS)

Mikulas, Martin M., Jr.; Sumpter, Rod

1997-01-01

In a previous paper, a new merit function for determining the strength performance of flawed composite laminates was presented. This previous analysis was restricted to circular hole flaws that were large enough that failure could be predicted using the laminate stress concentration factor. In this paper, the merit function is expanded to include the flaw cases of an arbitrary size circular hole or a center crack. Failure prediction for these cases is determined using the point stress criterion. An example application of the merit function is included for a wide range of graphite/epoxy laminates.

Method of preparing graphene-sulfur nanocomposites for rechargeable lithium-sulfur battery electrodes

DOEpatents

Liu, Jun; Lemmon, John P; Yang, Zhenguo; Cao, Yuliang; Li, Xiaolin

2015-04-07

A method of preparing a graphene-sulfur nanocomposite for a cathode in a rechargeable lithium-sulfur battery comprising thermally expanding graphite oxide to yield graphene layers, mixing the graphene layers with a first solution comprising sulfur and carbon disulfide, evaporating the carbon disulfide to yield a solid nanocomposite, and grinding the solid nanocomposite to yield the graphene-sulfur nanocomposite. Rechargeable-lithium-sulfur batteries having a cathode that includes a graphene-sulfur nanocomposite can exhibit improved characteristics. The graphene-sulfur nanocomposite can be characterized by graphene sheets with particles of sulfur adsorbed to the graphene sheets. The sulfur particles have an average diameter of less than 50 nm.

Accelerated testing of composites

NASA Technical Reports Server (NTRS)

Papazian, H. A.

1983-01-01

It is shown that the Zhurkov method for testing the strength of solids can be applied to dynamic tension and to cyclic loading and provides a viable approach to accelerated testing of composites. Data from the literature are used to demonstrate a straightforward application of the method to dynamic tension of glass fiber and cyclic loading for glass/polymer, metal matrix, and graphite/epoxy composites. Zhurkov's equation can be used at relatively high loads to obtain failure times at any temperature of interest. By taking a few data points at one or two other temperatures the spectrum of failure times can be expanded to temperatures not easily accessible.

An update of the JPL program to develop Li-SOCl2 cells

NASA Technical Reports Server (NTRS)

Halpert, S.; Ang, V.; Banes, R.; Dawson, S.; Frank, H.; Subbarao, S.; Whitcanack, L.

1985-01-01

The goal of producing spiral wound D cell was met. The cell design and electrodes, particularly the carbon cathodes were produced in-house. Also all parts were assembled, the welding performed, the electrolyte aided and the cells sealed in-house. The lithium capacity (theoretical) was 19.3 Ah and that of the SOCl2 in the 1.8 m LiAlCl4 electrolyte, 16.4 Ah (a greater excess of SOCl2 is necessary for safe high rate operation). The electrode surface area was 452 sq cm. The carbon electrode comprised Shawinigen Black/Teflon -30 (90/10 by weight) mixture 0.020 inches thick on an expanded metal screen prepared in the JPL laboratory. There were two tab connections to the cathode. The 0.0078 inch thick lithium foil was rolled into an expanded nickel screen. The separator was Mead 934-5 fiberglass material.

Stirling cryocooler test results and design model verification

NASA Astrophysics Data System (ADS)

Shimko, Martin A.; Stacy, W. D.; McCormick, John A.

A long-life Stirling cycle cryocooler being developed for spaceborne applications is described. The results from tests on a preliminary breadboard version of the cryocooler used to demonstrate the feasibility of the technology and to validate the generator design code used in its development are presented. This machine achieved a cold-end temperature of 65 K while carrying a 1/2-W cooling load. The basic machine is a double-acting, flexure-bearing, split Stirling design with linear electromagnetic drives for the expander and compressors. Flat metal diaphragms replace pistons for sweeping and sealing the machine working volumes. The double-acting expander couples to a laminar-channel counterflow recuperative heat exchanger for regeneration. The PC-compatible design code developed for this design approach calculates regenerator loss, including heat transfer irreversibilities, pressure drop, and axial conduction in the regenerator walls. The code accurately predicted cooler performance and assisted in diagnosing breadboard machine flaws during shakedown and development testing.

Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene

PubMed Central

Shepelev, Olga; Kenig, Samuel

2017-01-01

Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called “stacked” graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior. PMID:29046838

Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene.

PubMed

Naveh, Naum; Shepelev, Olga; Kenig, Samuel

2017-01-01

Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called "stacked" graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior.

Influence of electrolytes (TEABF4 and TEMABF4) on electrochemical performance of graphite oxide derived from needle coke.

PubMed

Yang, Sunhye; Kim, Ick-Jun; Choi, In-Sik; Bae, Mi-Kyeong; Kim, Hyun-Soo

2013-05-01

The structure of needle coke was changed to graphite oxide structure after oxidation treatment with 70 wt.% of nitric acid and sodium chlorate (NaClO3), and the inter-layer distance of the oxidized needle coke was expanded to 6.9 angstroms. The first charge profile of the oxidized needle coke-cell with 1.2 M TEMABF4/acetonitrile solution displayed that the intercalation of electrolyte ions into the inter-layer occurred at 1.0 V, which value is lower than 1.3 V of the oxidized needle coke-cell with 1.2 M TEABF4/acetonitrile solution. After first charge/discharge, the cell using TEMABF4 electrolyte exhibited smaller electrode resistance of 0.05 omega, and larger specific volume capacitance of 25.5 F/ml at the two-electrode system in the potential range 0-2.5 V than those of the cell using TEABF4 electrolyte. Compared to the TEABF4 electrolyte, better electrochemical performance of the TEMABF4 electrolyte in the oxidized needle coke may be caused by the smaller cation (TEMA+) size and better ion mobility in the nanopores between inter-layers.

Preparation and Characterization of Graphene Oxide Paper

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dikin,D.; Stankovich, S.; Zimney, E.

2007-01-01

Free-standing paper-like or foil-like materials are an integral part of our technological society. Their uses include protective layers, chemical filters, components of electrical batteries or supercapacitors, adhesive layers, electronic or optoelectronic components, and molecular storage. Inorganic 'paper-like' materials based on nanoscale components such as exfoliated vermiculite or mica platelets have been intensively studied and commercialized as protective coatings, high-temperature binders, dielectric barriers and gas-impermeable membranes. Carbon-based flexible graphite foils composed of stacked platelets of expanded graphite have long been used in packing and gasketing applications because of their chemical resistivity against most media, superior sealability over a wide temperature range,more » and impermeability to fluids. The discovery of carbon nanotubes brought about bucky paper, which displays excellent mechanical and electrical properties that make it potentially suitable for fuel cell and structural composite applications. Here we report the preparation and characterization of graphene oxide paper, a free-standing carbon-based membrane material made by flow-directed assembly of individual graphene oxide sheets. This new material outperforms many other paper-like materials in stiffness and strength. Its combination of macroscopic flexibility and stiffness is a result of a unique interlocking-tile arrangement of the nanoscale graphene oxide sheets.« less

Preparation and characterization of graphene oxide paper.

PubMed

Dikin, Dmitriy A; Stankovich, Sasha; Zimney, Eric J; Piner, Richard D; Dommett, Geoffrey H B; Evmenenko, Guennadi; Nguyen, SonBinh T; Ruoff, Rodney S

2007-07-26

Free-standing paper-like or foil-like materials are an integral part of our technological society. Their uses include protective layers, chemical filters, components of electrical batteries or supercapacitors, adhesive layers, electronic or optoelectronic components, and molecular storage. Inorganic 'paper-like' materials based on nanoscale components such as exfoliated vermiculite or mica platelets have been intensively studied and commercialized as protective coatings, high-temperature binders, dielectric barriers and gas-impermeable membranes. Carbon-based flexible graphite foils composed of stacked platelets of expanded graphite have long been used in packing and gasketing applications because of their chemical resistivity against most media, superior sealability over a wide temperature range, and impermeability to fluids. The discovery of carbon nanotubes brought about bucky paper, which displays excellent mechanical and electrical properties that make it potentially suitable for fuel cell and structural composite applications. Here we report the preparation and characterization of graphene oxide paper, a free-standing carbon-based membrane material made by flow-directed assembly of individual graphene oxide sheets. This new material outperforms many other paper-like materials in stiffness and strength. Its combination of macroscopic flexibility and stiffness is a result of a unique interlocking-tile arrangement of the nanoscale graphene oxide sheets.

An extended life and performance test of a low-power arcjet

NASA Technical Reports Server (NTRS)

Curran, Francis M.; Haag, Thomas W.

1988-01-01

An automated, cyclic life test was performed to demonstrate the reliability and endurance of a low power dc cycle arcjet thruster. Over 1000 hr and 500 on-off cycles were accumulated which would represent the requirements for about 15 years of on-orbit lifetime. A hydrogen/nitrogen propellant mixture was used to simulate decomposed hydrazine propellant and the power level was nominally 1.2 kW after the burn-in period. The arcjet operated in a very repeatable fashion from cycle to cycle. The steady state voltage increased by approximately 6 V over the first 300 hr, and then by only 3 V through the remainder of the test. Thrust measurements taken before, during, and after the test verified that the thruster performed in a consistent fashion throughout the tests at a specific impulse of 450 to 460 sec. Post-test component evaluation revealed limited erosion on both the anode and cathode. Other thruster components, including graphite seals, appeared undamaged.

Online Oxide Contamination Measurement and Purification Demonstration

NASA Technical Reports Server (NTRS)

Bradley, D. E.; Godfroy, T. J.; Webster, K. L.; Garber, A. E.; Polzin, K. A.; Childers, D. J.

2011-01-01

Liquid metal sodium-potassium (NaK) has advantageous thermodynamic properties indicating its use as a fission reactor coolant for a surface (lunar, martian) power system. A major area of concern for fission reactor cooling systems is system corrosion due to oxygen contaminants at the high operating temperatures experienced. A small-scale, approximately 4-L capacity, simulated fission reactor cooling system employing NaK as a coolant was fabricated and tested with the goal of demonstrating a noninvasive oxygen detection and purification system. In order to generate prototypical conditions in the simulated cooling system, several system components were designed, fabricated, and tested. These major components were a fully-sealed, magnetically-coupled mechanical NaK pump, a graphite element heated reservoir, a plugging indicator system, and a cold trap. All system components were successfully demonstrated at a maximum system flow rate of approximately 150 cc/s at temperatures up to 550 C. Coolant purification was accomplished using a cold trap before and after plugging operations which showed a relative reduction in oxygen content.

Seal welded cast iron nuclear waste container

DOEpatents

Filippi, Arthur M.; Sprecace, Richard P.

1987-01-01

This invention identifies methods and articles designed to circumvent metallurgical problems associated with hermetically closing an all cast iron nuclear waste package by welding. It involves welding nickel-carbon alloy inserts which are bonded to the mating plug and main body components of the package. The welding inserts might be bonded in place during casting of the package components. When the waste package closure weld is made, the most severe thermal effects of the process are restricted to the nickel-carbon insert material which is far better able to accommodate them than is cast iron. Use of nickel-carbon weld inserts should eliminate any need for pre-weld and post-weld heat treatments which are a problem to apply to nuclear waste packages. Although the waste package closure weld approach described results in a dissimilar metal combination, the relative surface area of nickel-to-iron, their electrochemical relationship, and the presence of graphite in both materials will act to prevent any galvanic corrosion problem.

Fluid flow monitoring device

DOEpatents

McKay, M.D.; Sweeney, C.E.; Spangler, B.S. Jr.

1993-11-30

A flow meter and temperature measuring device are described comprising a tube with a body centered therein for restricting flow and a sleeve at the upper end of the tube to carry several channels formed longitudinally in the sleeve to the appropriate axial location where they penetrate the tube to allow pressure measurements and temperature measurements with thermocouples. The high pressure measurement is made using a channel penetrating the tube away from the body and the low pressure measurement is made at a location at the widest part of the body. An end plug seals the end of the device and holes at its upper end allow fluid to pass from the interior of the tube into a plenum. The channels are made by cutting grooves in the sleeve, the grooves widened at the surface of the sleeve and then a strip of sleeve material is welded to the grooves closing the channels. Preferably the sleeve is packed with powdered graphite before cutting the grooves and welding the strips. 7 figures.

Construction material processed using lunar simulant in various environments

NASA Technical Reports Server (NTRS)

Chase, Stan; Ocallaghan-Hay, Bridget; Housman, Ralph; Kindig, Michael; King, John; Montegrande, Kevin; Norris, Raymond; Vanscotter, Ryan; Willenborg, Jonathan; Staubs, Harry

1995-01-01

The manufacture of construction materials from locally available resources in space is an important first step in the establishment of lunar and planetary bases. The objective of the CoMPULSIVE (Construction Material Processed Using Lunar Simulant In Various Environments) experiment is to develop a procedure to produce construction materials by sintering or melting Johnson Space Center Simulant 1 (JSC-1) lunar soil simulant in both earth-based (1-g) and microgravity (approximately 0-g) environments. The characteristics of the resultant materials will be tested to determine its physical and mechanical properties. The physical characteristics include: crystalline, thermal, and electrical properties. The mechanical properties include: compressive tensile, and flexural strengths. The simulant, placed in a sealed graphite crucible, will be heated using a high temperature furnace. The crucible will then be cooled by radiative and forced convective means. The core furnace element consists of space qualified quartz-halogen incandescent lamps with focusing mirrors. Sample temperatures of up to 2200 C are attainable using this heating method.

NASA Tech Briefs, February 2008

NASA Technical Reports Server (NTRS)

2008-01-01

Topics discussed include: Optical Measurement of Mass Flow of a Two-Phase Fluid; Selectable-Tip Corrosion-Testing Electrochemical Cell; Piezoelectric Bolt Breakers and Bolt Fatigue Testers; Improved Measurement of B(sub 22) of Macromolecules in a Flow Cell; Measurements by a Vector Network Analyzer at 325 to 508 GHz; Using Light to Treat Mucositis and Help Wounds Heal; Increasing Discharge Capacities of Li-(CF)(sub n) Cells; Dot-in-Well Quantum-Dot Infrared Photodetectors; Integrated Microbatteries for Implantable Medical Devices; Oxidation Behavior of Carbon Fiber-Reinforced Composites; GIDEP Batching Tool; Generic Spacecraft Model for Real-Time Simulation; Parallel-Processing Software for Creating Mosaic Images; Software for Verifying Image-Correlation Tie Points; Flexcam Image Capture Viewing and Spot Tracking; Low-Pt-Content Anode Catalyst for Direct Methanol Fuel Cells; Graphite/Cyanate Ester Face Sheets for Adaptive Optics; Atomized BaF2-CaF7 for Better-Flowing Plasma-Spray Feedstock; Nanophase Nickel-Zirconium Alloys for Fuel Cells; Vacuum Packaging of MEMS With Multiple Internal Seal Rings; Compact Two-Dimensional Spectrometer Optics; and Fault-Tolerant Coding for State Machines.

Synthesis and characterization of magnetic poly(divinyl benzene)/Fe3O4, C/Fe3O4/Fe, and C/Fe onionlike fullerene micrometer-sized particles with a narrow size distribution.

PubMed

Snovski, Ron; Grinblat, Judith; Margel, Shlomo

2011-09-06

Magnetic poly(divinyl benzene)/Fe(3)O(4) microspheres with a narrow size distribution were produced by entrapping the iron pentacarbonyl precursor within the pores of uniform porous poly(divinyl benzene) microspheres prepared in our laboratory, followed by the decomposition in a sealed cell of the entrapped Fe(CO)(5) particles at 300 °C under an inert atmosphere. Magnetic onionlike fullerene microspheres with a narrow size distribution were produced by annealing the obtained PDVB/Fe(3)O(4) particles at 500, 600, 800, and 1100 °C, respectively, under an inert atmosphere. The formation of carbon graphitic layers at low temperatures such as 500 °C is unique and probably obtained because of the presence of the magnetic iron nanoparticles. The annealing temperature allowed control of the composition, size, size distribution, crystallinity, porosity, and magnetic properties of the produced magnetic microspheres. © 2011 American Chemical Society

Method for producing dustless graphite spheres from waste graphite fines

DOEpatents

Pappano, Peter J [Oak Ridge, TN; Rogers, Michael R [Clinton, TN

2012-05-08

A method for producing graphite spheres from graphite fines by charging a quantity of spherical media into a rotatable cylindrical overcoater, charging a quantity of graphite fines into the overcoater thereby forming a first mixture of spherical media and graphite fines, rotating the overcoater at a speed such that the first mixture climbs the wall of the overcoater before rolling back down to the bottom thereby forming a second mixture of spherical media, graphite fines, and graphite spheres, removing the second mixture from the overcoater, sieving the second mixture to separate graphite spheres, charging the first mixture back into the overcoater, charging an additional quantity of graphite fines into the overcoater, adjusting processing parameters like overcoater dimensions, graphite fines charge, overcoater rotation speed, overcoater angle of rotation, and overcoater time of rotation, before repeating the steps until graphite fines are converted to graphite spheres.

Photonic crystal fiber refractive-index sensor based on multimode interferometry

NASA Astrophysics Data System (ADS)

Gong, Zhenfeng; Zhang, Xinpu; Liu, Yun; Liu, Zigeng; Peng, Wei

2014-11-01

We report a type of multimode fiber interferometers (MMI) formed in photonic crystal fiber (PCF). To excite the cladding modes from the fundamental core mode of a PCF, a coupling point is formed. To form the coupling point, we used the method that is blowing compressed gas into the air-holes and discharging at one point, and the air-holes in this point will expand due to gas expansion in the discharge process. By placing two coupling points in series, a very simple all-fiber MMI can be implemented. The detailed fabrication process is that the one end of the PCF is tightly sealed by a short section of single mode fiber (SMF) spliced to the PCF. The other end of the PCF is sealed into a gas chamber and the opened air holes are pressurized. The PCF is then heated locally by the fusion splicer and the holes with higher gas pressure will expand locally where two bubbles formed. We tested the RI responses of fabricated sensors at room temperature by immersing the sensor into solutions with different NaCl concentration. Experimental results show that as refractive-index (RI) increases, the resonance wavelength of the MMI moves toward longer wavelengths. The sensitivity coefficients are estimated by the linear fitting line, which is 46nm/RIU, 154mn/RIU with the interferometer lengths (IL) of 3mm and 6mm. The interferometer with larger IL has higher RI sensitivity. The temperature cross-sensitivity of the sensor is also tested. The temperature sensitivity can be as low as -16.0pm/°C.

FennoFlakes: a project for identifying flake graphite ores in the Fennoscandian shield and utilizing graphite in different applications

NASA Astrophysics Data System (ADS)

Palosaari, Jenny; Eklund, O.; Raunio, S.; Lindfors, T.; Latonen, R.-M.; Peltonen, J.; Smått, J.-H.; Kauppila, J.; Lund, S.; Sjöberg-Eerola, P.; Blomqvist, R.; Marmo, J.

2016-04-01

Natural graphite is a strategic mineral, since the European Commission stated (Report on critical raw materials for the EU (2014)) that graphite is one of the 20 most critical materials for the European Union. The EU consumed 13% of all flake graphite in the world but produced only 3%, which stresses the demand of the material. Flake graphite, which is a flaky version of graphite, forms under high metamorphic conditions. Flake graphite is important in different applications like batteries, carbon brushes, heat sinks etc. Graphene (a single layer of graphite) can be produced from graphite and is commonly used in many nanotechnological applications, e.g. in electronics and sensors. The steps to obtain pure graphene from graphite ore include fragmentation, flotation and exfoliation, which can be cumbersome and resulting in damaging the graphene layers. We have started a project named FennoFlakes, which is a co-operation between geologists and chemists to fill the whole value chain from graphite to graphene: 1. Exploration of graphite ores (geological and geophysical methods). 2. Petrological and geochemical analyses on the ores. 3. Development of fragmentation methods for graphite ores. 4. Chemical exfoliation of the enriched flake graphite to separate flake graphite into single and multilayer graphene. 5. Test the quality of the produced material in several high-end applications with totally environmental friendly and disposable material combinations. Preliminary results show that flake graphite in high metamorphic areas has better qualities compared to synthetic graphite produced in laboratories.

Benchtop quantification of gutter formation and compression of chimney stent grafts in relation to renal flow in chimney endovascular aneurysm repair and endovascular aneurysm sealing configurations.

PubMed

Boersen, Johannes T; Donselaar, Esme J; Groot Jebbink, Erik; Starreveld, Roeliene; Overeem, Simon P; Slump, Cornelis H; de Vries, Jean-Paul P M; Reijnen, Michel M P J

2017-11-01

The chimney technique has been successfully used to treat juxtarenal aortic aneurysms. The two main issues with this technique are gutter formation and chimney graft (CG) compression, which induce a risk for type Ia endoleaks and stent thrombosis, respectively. In this benchtop study, the geometry and renal artery flow of chimney endovascular aneurysm repair configurations were compared with chimney configurations with endovascular aneurysm sealing (ch-EVAS). Seven flow phantoms were constructed, including one control and six chimney endovascular aneurysm repairs (Endurant [Medtronic Inc, Minneapolis, Minn] and AFX [Endologix Inc, Irvine, Calif]) or ch-EVAS (Nellix, Endologix) configurations, combined with either balloon-expandable or self-expanding CGs with an intended higher positioning of the right CG in comparison to the left CG. Geometric analysis was based on measurements at three-dimensional computed tomography angiography and included gutter volume and CG compression, quantified by the ratio between maximal and minimal diameter (D-ratio). In addition, renal artery flow was studied in a physiologic flow model and compared with the control. The average gutter volume was 343.5 ± 142.0 mm 3 , with the lowest gutter volume in the EVAS-Viabahn (W. L. Gore & Associates, Flagstaff, Ariz) combination (102.6 mm 3 ) and the largest in the AFX-Advanta V12 (Atrium Medical Corporation, Hudson, NH) configuration (559.6 mm 3 ). The maximum D-ratio was larger in self-expanding CGs than in balloon-expandable CGs in all configurations (2.02 ± 0.34 vs 1.39 ± 0.13). The CG compression had minimal influence on renal volumetric flow (right, 390.7 ± 29.4 mL/min vs 455.1 mL/min; left, 423.9 ± 28.3 mL/min vs 410.0 mL/min in the control). This study showed that gutter volume was lowest in ch-EVAS in combination with a Viabahn CG. CG compression was lower in configurations with the Advanta V12 than with Viabahn. Renal flow is unrestricted by CG compression. Copyright © 2016 Society for Vascular Surgery. Published by Elsevier Inc. All rights reserved.

Graphite Black shale of Vendas de Ceira, Coimbra, Portugal

NASA Astrophysics Data System (ADS)

Quinta-Ferreira, Mário; Silva, Daniela; Coelho, Nuno; Gomes, Ruben; Santos, Ana; Piedade, Aldina

2017-04-01

The graphite black shale of Vendas de Ceira located in south of Coimbra (Portugal), caused serious instability problems in recent road excavation slopes. The problems increased with the rain, transforming shales into a dark mud that acquires a metallic hue when dried. The black shales are attributed to the Devonian or eventually, to the Silurian. At the base of the slope is observed graphite black shale and on the topbrown schist. Samples were collected during the slope excavation works. Undisturbed and less altered materials were selected. Further, sampling was made difficult as the graphite shale was covered by a thick layer of reinforced concrete, which was used to stabilize the excavated surfaces. The mineralogy is mainly constituted by quartz, muscovite, ilite, ilmenite and feldspar without the presence of expansive minerals. The organic matter content is 0.3 to 0.4%. The durability evaluated by the Slake Durability Test varies from very low (Id2 of 6% for sample A) to high (98% for sample C). The grain size distribution of the shale particles, was determined after disaggregation with water, which allowed verifying that sample A has 37% of fines (5% of clay and 32% of silt) and 63% of sand, while sample C has only 14% of fines (2% clay and 12% silt) and 86% sand, showing that the decrease in particle size contributes to reduce durability. The unconfined linear expansion confirms the higher expandability (13.4%) for sample A, reducing to 12.1% for sample B and 10.5% for sample C. Due the shale material degradated with water, mercury porosimetry was used. While the dry weight of the three samples does not change significantly, around 26 kN/m3, the porosity is much higher in sample A with 7.9% of pores, reducing to 1.4% in sample C. The pores size vary between 0.06 to 0.26 microns, does not seem to have any significant influence in the shale behaviour. In order to have a comparison term, a porosity test was carried out on the low weatherable brown shale, which is quite abundant at the site. The main difference to the graphite shale is the high porosity of the brown shale with 14.7% and the low volume weight of 23 kN/m3, evidencing the distinct characteristics of the graphite schists. The maximum strength was evaluated by the Schmidt hammer, as the point load test could not be performed as the rock was very soft. The maximum estimated values on dry samples were 32 MPa for sample A and 85 MPa for sample C. The results show a singular material characterized by significant heterogeneity. It can be concluded that for the graphite schists the smaller particle size and higher porosity make the soft rock extremely weatherable when decompressed and exposed to water, as a result of high capillary tension and reduced cohesion. They also exhibit high expansion and an enormous degradation of the rock presenting a behaviour close to a soil. The graphite black schist is a highly weatherable soft rock, without expansive minerals, with small pores, in which the porosity, low strength and low cohesion allow their rapid degradation when decompressed and exposed to the action of Water.

Voronoi-Tessellated Graphite Produced by Low-Temperature Catalytic Graphitization from Renewable Resources.

PubMed

Zhao, Leyi; Zhao, Xiuyun; Burke, Luke T; Bennett, J Craig; Dunlap, Richard A; Obrovac, Mark N

2017-09-11

A highly crystalline graphite powder was prepared from the low temperature (800-1000 °C) graphitization of renewable hard carbon precursors using a magnesium catalyst. The resulting graphite particles are composed of Voronoi-tessellated regions comprising irregular sheets; each Voronoi-tessellated region having a small "seed" particle located near their centroid on the surface. This suggests nucleated outward growth of graphitic carbon, which has not been previously observed. Each seed particle consists of a spheroidal graphite shell on the inside of which hexagonal graphite platelets are perpendicularly affixed. This results in a unique high surface area graphite with a high degree of graphitization that is made with renewable feedstocks at temperatures far below that conventionally used for artificial graphites. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Influence of Metal-Coated Graphite Powders on Microstructure and Properties of the Bronze-Matrix/Graphite Composites

NASA Astrophysics Data System (ADS)

Zhao, Jian-hua; Li, Pu; Tang, Qi; Zhang, Yan-qing; He, Jian-sheng; He, Ke

2017-02-01

In this study, the bronze-matrix/x-graphite (x = 0, 1, 3 and 5%) composites were fabricated by powder metallurgy route by using Cu-coated graphite, Ni-coated graphite and pure graphite, respectively. The microstructure, mechanical properties and corrosive behaviors of bronze/Cu-coated-graphite (BCG), bronze/Ni-coated-graphite (BNG) and bronze/pure-graphite (BPG) were characterized and investigated. Results show that the Cu-coated and Ni-coated graphite could definitely increase the bonding quality between the bronze matrix and graphite. In general, with the increase in graphite content in bronze-matrix/graphite composites, the friction coefficients, ultimate density and wear rates of BPG, BCG and BNG composites all went down. However, the Vickers microhardness of the BNG composite would increase as the graphite content increased, which was contrary to the BPG and BCG composites. When the graphite content was 3%, the friction coefficient of BNG composite was more stable than that of BCG and BPG composites, indicating that BNG composite had a better tribological performance than the others. Under all the values of applied loads (10, 20, 40 and 60N), the BCG and BNG composites exhibited a lower wear rate than BPG composite. What is more, the existence of nickel in graphite powders could effectively improve the corrosion resistance of the BNG composite.

Producing graphite with desired properties

NASA Technical Reports Server (NTRS)

Dickinson, J. M.; Imprescia, R. J.; Reiswig, R. D.; Smith, M. C.

1971-01-01

Isotropic or anisotropic graphite is synthesized with precise control of particle size, distribution, and shape. The isotropic graphites are nearly perfectly isotropic, with thermal expansion coefficients two or three times those of ordinary graphites. The anisotropic graphites approach the anisotropy of pyrolytic graphite.

Brazing graphite to graphite

DOEpatents

Peterson, George R.

1976-01-01

Graphite is joined to graphite by employing both fine molybdenum powder as the brazing material and an annealing step that together produce a virtually metal-free joint exhibiting properties similar to those found in the parent graphite. Molybdenum powder is placed between the faying surfaces of two graphite parts and melted to form molybdenum carbide. The joint area is thereafter subjected to an annealing operation which diffuses the carbide away from the joint and into the graphite parts. Graphite dissolved by the dispersed molybdenum carbide precipitates into the joint area, replacing the molybdenum carbide to provide a joint of virtually graphite.

Method of Joining Graphite Fibers to a Substrate

NASA Technical Reports Server (NTRS)

Beringer, Durwood M. (Inventor); Caron, Mark E. (Inventor); Taddey, Edmund P. (Inventor); Gleason, Brian P. (Inventor)

2014-01-01

A method of assembling a metallic-graphite structure includes forming a wetted graphite subassembly by arranging one or more layers of graphite fiber material including a plurality of graphite fibers and applying a layer of metallization material to ends of the plurality of graphite fibers. At least one metallic substrate is secured to the wetted graphite subassembly via the layer of metallization material.

COMPARTMENTED REACTOR FUEL ELEMENT

DOEpatents

Cain, F.M. Jr.

1962-09-11

A method of making a nuclear reactor fuel element of the elongated red type is given wherein the fissionable fuel material is enclosed within a tubular metal cladding. The method comprises coating the metal cladding tube on its inside wall with a brazing alloy, inserting groups of cylindrical pellets of fissionable fuel material into the tube with spacing members between adjacent groups of pellets, sealing the ends of the tubes to leave a void space therewithin, heating the tube and its contents to an elevated temperature to melt the brazing alloy and to expand the pellets to their maximum dimensions under predetermined operating conditions thereby automatically positioning the spacing members along the tube, and finally cooling the tube to room temperature whereby the spacing disks become permanently fixed at their edges in the brazing alloy and define a hermetically sealed compartment for each fl group of fuel pellets. Upon cooling, the pellets contract thus leaving a space to accommodate thermal expansion of the pellets when in use in a reactor. The spacing members also provide lateral support for the tubular cladding to prevent collapse thereof when subjected to a reactor environment. (AEC)

Vaccine vial stopper performance for fractional dose delivery of vaccines

PubMed Central

Jarrahian, Courtney; Myers, Daniel; Creelman, Ben; Saxon, Eugene; Zehrung, Darin

2017-01-01

ABSTRACT Shortages of vaccines such as inactivated poliovirus and yellow fever vaccines have been addressed by administering reduced—or fractional—doses, as recommended by the World Health Organization Strategic Advisory Group of Experts on Immunization, to expand population coverage in countries at risk. We evaluated 3 kinds of vaccine vial stoppers to assess their performance after increased piercing from repeated withdrawal of doses needed when using fractional doses (0.1 mL) from presentations intended for full-dose (0.5 mL) delivery. Self-sealing capacity and fragmentation of the stopper were assessed via modified versions of international standard protocols. All stoppers maintained self-sealing capacity after 100 punctures. The damage to stoppers measured as the fragmentation rate was within the target of ≤ 10% of punctures resulting in a fragment after as many as 50 punctures. We concluded that stopper failure is not likely to be a concern if existing vaccine vials containing up to 10 regular doses are used up to 50 times for fractional dose delivery. PMID:28463054

The Zagora cryptograph

NASA Astrophysics Data System (ADS)

Coucouzeli, A.

A unique lead seal from the well-known eighth century B.C. settlement of Zagora on the island of Andros dramatically confirms and expands our knowledge of the town planning identified at the site and constituting the earliest example of an orthogonal grid plan in the Greek world. The seal in question is decorated with a symbolic design that constitutes a rare representation of the Dioskouroi as part of the constellation Gemini. This design appears to have acted as a cryptograph enciphering the basic mathematical and astronomical principles behind the planning of Zagora. Besides offering us new insights into early Greek settlement planning, the cryptograph seems to reveal an advanced practical competence in mathematics and celestial observation, which was hitherto unsuspected for such an early period. The Zagora cryptograph also suggests that astronomy and mathematics played a crucial role in the strengthening of the ruling elite's power at Zagora in the framework of the rising city-state or polis. The tight interweaving of astronomical, mathematical, architectural and social considerations in the planning of Zagora is an entirely new discovery for Greece, whose implications are far-reaching.

DESIGN CHARACTERISTICS OF THE IDAHO NATIONAL LABORATORY HIGH-[TEMPERATURE GAS-COOLED TEST REACTOR

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sterbentz, James; Bayless, Paul; Strydom, Gerhard

A point design for a graphite-moderated, high-temperature, gas-cooled test reactor (HTG TR) has been developed by Idaho National Laboratory (INL) as part of a United States (U.S.) Department of Energy (DOE) initiative to explore and potentially expand the existing U.S. test reactor capabilities. This paper provides a summary of the design and its main attributes. The 200 MW HTG TR is a thermal-neutron spectrum reactor composed of hexagonal prismatic fuel and graphite reflector blocks. Twelve fuel columns (96 fuel blocks total and 6.34 m active core height) are arranged in two hexagonal rings to form a relatively compact, high-power density,more » annular core sandwiched between inner, outer, top, and bottom graphite reflectors. The HTG-TR is designed to operate at 7 MPa with a coolant inlet/outlet temperature of 325°C/650°C, and utilizes TRISO particle fuel from the DOE AGR Program with 425 ?m uranium oxycarbide (UCO) kernels and an enrichment of 15.5 wt% 235U. The primary mission of the HTG TR is material irradiation and therefore the core has been specifically designed and optimized to provide the highest possible thermal and fast neutron fluxes. The highest thermal neutron flux (3.90E+14 n/cm2s) occurs in the outer reflector, and the maximum fast flux levels (1.17E+14 n/cm2s) are produced in the central reflector column where most of the graphite has been removed. Due to high core temperatures under accident conditions, all the irradiation test facilities have been located in the inner and outer reflectors where fast flux levels decline. The core features a large number of irradiation positions with large test volumes and long test lengths, ideal for thermal neutron irradiation of large test articles. The total available test volume is more than 1100 liters. Up to four test loop facilities can be accommodated with pressure tube boundaries to isolate test articles and test fluids (e.g., liquid metal, liquid salt, light water) from the helium primary coolant system.« less

A structural study of solid electrolyte interface on negative electrode of lithium-Ion battery by electron microscopy.

PubMed

Matsushita, Tadashi; Watanabe, Jiro; Nakao, Tatsuya; Yamashita, Seiichi

2014-11-01

For the last decades, the performance of the lithium-ion battery (LIB) has been significantly improved and its applications have been expanding rapidly. However, its performance has yet to be enhanced.In the lithium-ion battery development, it is important to elucidate the electrode structure change in detail during the charge and discharge cycling. In particular, solid electrolyte interface (SEI) formed by decomposition of the electrolytes on the graphite negative electrode surface should play an important role for battery properties. Therefore, it is essential to control the structure and composition of SEI to improve the battery performance. Here, we conducted a scanning electron microscope (SEM) and transmission electron microscope (TEM) study to elucidate the structures of the SEI during the charge and discharge process using LiNi1/3Co1/3Mn1/3O2 [1] cathode and graphite anode. [2] Since SEI is a lithium-containing compound with high activity, it was observed without being exposed to the atmosphere. The electrodes including SEI were sampled after dismantling batteries with cutoff voltages of 3V and 4.2V for the charge process and 3V for the discharge process. Fig.1 shows SEM images of the graphite electrode surface during the charge and discharge process. The change of the SEI structure during the process was clearly observed. Further, TEM images showed that the SEI grew thicker during the charge process and becomes thinner when discharged. These results with regard to the reversible SEI structure could give a new insight for the battery development.jmicro;63/suppl_1/i21/DFU056F1F1DFU056F1Fig. 1.SEM images of the graphite electrode surface:(a) before charge process;(b) with charge-cutoff voltage of 3.0V; (c) with charge-cutoff voltage of 4.2V; (d) with discharge-cutoff voltage of 3.0V. © The Author 2014. Published by Oxford University Press on behalf of The Japanese Society of Microscopy. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

Thermally exfoliated graphite oxide

NASA Technical Reports Server (NTRS)

Prud'Homme, Robert K. (Inventor); Aksay, Ilhan A. (Inventor); Abdala, Ahmed (Inventor)

2011-01-01

A modified graphite oxide material contains a thermally exfoliated graphite oxide with a surface area of from about 300 sq m/g to 2600 sq m/g, wherein the thermally exfoliated graphite oxide displays no signature of the original graphite and/or graphite oxide, as determined by X-ray diffraction.

The action of macrosounds on graphite ore and derived products

NASA Technical Reports Server (NTRS)

Bradeteanu, C.; Dragan, O.

1974-01-01

A suspension of graphite ore, floated graphite, and the gangue left over from flotation were subjected to the action of macrosounds under determinant conditions. The following was found: (1) The graphite ore undergoes an efficient settling action. (2) The floated graphite is strongly crushed down to the dimensions of colloidal graphite. (3) The gangue left over from flotation can be further processed to recuperate graphite from its nuclei.

Graphene prepared by thermal reduction–exfoliation of graphite oxide: Effect of raw graphite particle size on the properties of graphite oxide and graphene

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dao, Trung Dung; Jeong, Han Mo, E-mail: hmjeong@mail.ulsan.ac.kr

Highlights: • Effect of raw graphite particle size on properties of GO and graphene is reported. • Size of raw graphite affects oxidation degree and chemical structure of GO. • Highly oxidized GO results in small-sized but well-exfoliated graphene. • GO properties affect reduction degree, structure, and conductivity of graphene. - Abstract: We report the effect of raw graphite size on the properties of graphite oxide and graphene prepared by thermal reduction–exfoliation of graphite oxide. Transmission electron microscope analysis shows that the lateral size of graphene becomes smaller when smaller size graphite is used. X-ray diffraction analysis confirms that graphitemore » with smaller size is more effectively oxidized, resulting in a more effective subsequent exfoliation of the obtained graphite oxide toward graphene. X-ray photoelectron spectroscopy demonstrates that reduction of the graphite oxide derived from smaller size graphite into graphene is more efficient. However, Raman analysis suggests that the average size of the in-plane sp{sup 2}-carbon domains on graphene is smaller when smaller size graphite is used. The enhanced reduction degree and the reduced size of sp{sup 2}-carbon domains contribute contradictively to the electrical conductivity of graphene when the particle size of raw graphite reduces.« less

Enhanced performance of graphite anode materials by AlF3 coating for lithium-ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ding, Fei; Xu, Wu; Choi, Daiwon

2012-04-27

In order to form the stable surface film and to further enhance the long-term cycling stability of the graphite anodes of lithium-ion batteries, the surface of graphite powders has been modified by AlF3 coating through chemical precipitation method. The AlF3-coated graphite shows no evident changes in the bulk structure and a thin AlF3-coating layer of about 2 nm thick is found to uniformly cover the graphite particles with 2 wt% AlF3 content. However, it delivers a higher initial discharge capacity and largely improved rate performances compared to the pristine graphite. Remarkably, AlF3 coated graphite demonstrated a much better cycle life.more » After 300 cycles, AlF3 coated graphite and uncoated graphite show capacity retention of 92% and 81%, respectively. XPS measurement shows that a more conductive solid electrode interface (SEI) layer was formed on AlF3 coated graphite as compared to uncoated graphite. SEM monograph also reveals that the AlF3-coated graphite particles have a much more stable surface morphology after long-term cycling. Therefore, the improved electrochemical performance of AlF3 coated graphite can be attributed to a more stable and conductive SEI formed on coated graphite anode during cycling process.« less

Graphite

USGS Publications Warehouse

Robinson, Gilpin R.; Hammarstrom, Jane M.; Olson, Donald W.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

2017-12-19

Graphite is a form of pure carbon that normally occurs as black crystal flakes and masses. It has important properties, such as chemical inertness, thermal stability, high electrical conductivity, and lubricity (slipperiness) that make it suitable for many industrial applications, including electronics, lubricants, metallurgy, and steelmaking. For some of these uses, no suitable substitutes are available. Steelmaking and refractory applications in metallurgy use the largest amount of produced graphite; however, emerging technology uses in large-scale fuel cell, battery, and lightweight high-strength composite applications could substantially increase world demand for graphite.Graphite ores are classified as “amorphous” (microcrystalline), and “crystalline” (“flake” or “lump or chip”) based on the ore’s crystallinity, grain-size, and morphology. All graphite deposits mined today formed from metamorphism of carbonaceous sedimentary rocks, and the ore type is determined by the geologic setting. Thermally metamorphosed coal is the usual source of amorphous graphite. Disseminated crystalline flake graphite is mined from carbonaceous metamorphic rocks, and lump or chip graphite is mined from veins in high-grade metamorphic regions. Because graphite is chemically inert and nontoxic, the main environmental concerns associated with graphite mining are inhalation of fine-grained dusts, including silicate and sulfide mineral particles, and hydrocarbon vapors produced during the mining and processing of ore. Synthetic graphite is manufactured from hydrocarbon sources using high-temperature heat treatment, and it is more expensive to produce than natural graphite.Production of natural graphite is dominated by China, India, and Brazil, which export graphite worldwide. China provides approximately 67 percent of worldwide output of natural graphite, and, as the dominant exporter, has the ability to set world prices. China has significant graphite reserves, and China’s graphite production is expected to increase, although rising labor costs and some mine production problems are developing. China is expected to continue to be the dominant exporter for the near future. Mexico and Canada export graphite mainly to the United States, which has not had domestic production of natural graphite since the 1950s. Most graphite deposits in the United States are too small, low-grade, or remote to be of commercial value in the near future, and the likelihood of discovering larger, higher-grade, or favorably located domestic deposits is unlikely. The United States is a major producer of synthetic graphite.

Strategic graphite, a survey

USGS Publications Warehouse

Cameron, Eugene N.; Weis, Paul L.

1960-01-01

Strategic graphite consists of certain grades of lump and flake graphite for which the United States is largely or entirely dependent on sources abroad. Lump graphite of high purity, necessary in the manufacture of carbon brushes, is imported from Ceylon, where it occurs in vein deposits. Flake graphite, obtained from deposits consisting of graphite disseminated in schists and other metamorphic rocks, is an essential ingredient of crucibles used in the nonferrous metal industries and in the manufacture of lubricants and packings. High-quality flake graphite for these uses has been obtained mostly from Madagascar since World War I. Some flake graphite of strategic grade has been produced, however, from deposits in Texas, Alabama, and Pennsylvania. The development of the carbon-bonded crucible, which does not require coarse flake, should lessen the competitive advantage of the Madagascar producers of crucible flake. Graphite of various grades has been produced intermittently in the United States since 1644. The principal domestic deposits of flake graphite are in Texas, Alabama, Pennsylvania, and New York. Reserves of flake graphite in these four States are very large, but production has been sporadic and on the whole unprofitable since World War I, owing principally to competition from producers in Madagascar. Deposits in Madagascar are large and relatively high in content of flake graphite. Production costs are low and the flake produced is of high quality. Coarseness of flake and uniformity of the graphite products marketed are cited as major advantages of Madagascar flake. In addition, the usability of Madagascar flake for various purposes has been thoroughly demonstrated, whereas the usability of domestic flake for strategic purposes is still in question. Domestic graphite deposits are of five kinds: deposits consisting of graphite disseminated in metamorphosed siliceous sediments, deposits consisting of graphite disseminated in marble, deposits formed by thermal or dynamothermal metamorphism of coal beds or other highly carbonaceous sediments, vein deposits, and contact metasomatic deposits in marble. Only the first kind comprises deposits sufficiently large and rich in flake graphite to be significant potential sources of strategic grades of graphite. Vein deposits in several localities are known, but none is known to contain substantial reserves of graphite of strategic quality.Large resources of flake graphite exist in central Texas, in northeastern Alabama, in eastern Pennsylvania, and in the eastern Adirondack Mountains of New York. Tonnages available, compared with the tonnages of flake graphite consumed annually in the United States, are very large. There have been indications that flake graphite from Texas, Alabama, and Pennsylvania can be used in clay-graphite crucibles as a substitute for Madagascar flake, and one producer has made progress in establishing markets for his flake products as ingredients of lubricants. The tonnages of various commercial grades of graphite recoverable from various domestic deposits, however, have not been established; hence, the adequacy of domestic resources of graphite in a time of emergency is not known.The only vein deposits from which significant quantities of lump graphite have been produced are those of the Crystal Graphite mine, Beaverhead County, Mont. The deposits are fracture fillings in Precambrian gneiss and pegmatite. Known reserves in the deposits are small. In Texas, numerous flake-graphite deposits occur in the Precambrian Packsaddle schist in Llano and Burnet Counties. Graphite disseminated in certain parts of this formation ranges from extremely fine to medium grained. The principal producer has been the mine of the Southwestern Graphite Co., west of the town of Burnet. Substantial reserves of medium-grained graphite are present in the deposit mined by the company. In northeastern Alabama, flake-graphite deposits occur in the Ashland mica schist in two belts that trend northeastward across Clay, Goosa, and Chilton Counties. The northeastern belt has been the most productive. About 40 mines have been operated at one time or another, but only a few have been active during or since World War I. The deposits consist of flake graphite disseminated in certain zones or "leads" consisting of quartz-mica-feldspar schists and mica quartzite. Most of past production has come from the weathered upper parts of the deposits, but unweathered rock has been mined at several localities. Reserves of weathered rock containing 3 to 5 percent graphite are very large, and reserves of unweathered rock are even greater. Flake graphite deposits in Chester County, Pa., have been worked intermittently since about 1890. The deposits consist of medium- to coarse-grained graphite disseminated in certain belts of the Pickering gneiss. The most promising deposit is one worked in the Benjamin Franklin and the Eynon Just mines. Reserves of weathered rock containing 1.5 percent graphite are of moderate size; reserves of unweathered rock are large. In the eastern Adirondack Mountains in New York there are two principal kinds of flake-graphite deposits: contact-metasomatic deposits and those consisting of flake graphite disseminated in quartz schist. The contact-metasomatic deposits are small, irregular, and very erratic in graphite content. The deposits in quartz schist are very large, persistent, and uniform in grade. There are large reserves of schist containing 3 to 5 percent graphite, but the graphite is relatively fine grained.

Solar-powered turbocompressor heat pump system

DOEpatents

Landerman, A.M.; Biancardi, F.R.; Melikian, G.; Meader, M.D.; Kepler, C.E.; Anderson, T.J.; Sitler, J.W.

1982-08-12

The turbocompressor comprises a power turbine and a compressor turbine having respective rotors and on a common shaft, rotatably supported by bearings. A first working fluid is supplied by a power loop and is expanded in the turbine. A second working fluid is compressed in the turbine and is circulated in a heat pump loop. A lubricant is mixed with the second working fluid but is excluded from the first working fluid. The bearings are cooled and lubricated by a system which circulates the second working fluid and the intermixed lubricant through the bearings. Such system includes a pump, a thermostatic expansion valve for expanding the working fluid into the space between the bearings, and a return conduit system for withdrawing the expanded working fluid after it passes through the bearings and for returning the working fluid to the evaporator. A shaft seal excludes the lubricant from the power turbine. The power loop includes a float operable by liquid working fluid in the condenser for controlling a recirculation valve so as to maintain a minimum liquid level in the condenser, while causing a feed pump to pump most of the working fluid into the vapor generator. The heat pump compressor loop includes a float in the condenser for operating and expansion valve to maintain a minimum liquid working fluid level in the condenser while causing most of the working fluid to be expanded into the evaporator.

Novel Composites for Wing and Fuselage Applications

NASA Technical Reports Server (NTRS)

Suarez, J. A.; Buttitta, C.

1996-01-01

Design development was successfully completed for textile preforms with continuous cross-stiffened epoxy panels with cut-outs. The preforms developed included 3-D angle interlock weaving of graphite structural fibers impregnated by resin film infiltration (RFI) and shown to be structurally suitable under conditions requiring minimum acquisition costs. Design guidelines/analysis methodology for such textile structures are given. The development was expanded to a fuselage side-panel component of a subsonic commercial airframe and found to be readily scalable. The successfully manufactured panel was delivered to NASA Langley for biaxial testing. This report covers the work performed under Task 3 -- Cross-Stiffened Subcomponent; Task 4 -- Design Guidelines/Analysis of Textile-Reinforced Composites; and Task 5 -- Integrally Woven Fuselage Panel.

CMB-13 research on carbon and graphite

NASA Technical Reports Server (NTRS)

Smith, M. C.

1972-01-01

Preliminary results of the research on carbon and graphite accomplished during this report period are presented. Included are: particle characteristics of Santa Maria fillers, compositions and density data for hot-molded Santa Maria graphites, properties of hot-molded Santa Maria graphites, and properties of hot-molded anisotropic graphites. Ablation-resistant graphites are also discussed.

METHOD OF FABRICATING A GRAPHITE MODERATED REACTOR

DOEpatents

Kratz, H.R.

1963-05-01

S>A nuclear reactor formed of spaced bodies of uranium and graphite blocks is improved by diffusing helium through the graphite blocks in order to replace the air in the pores of the graphite with helium. The helium-impregnated graphite conducts heat better, and absorbs neutrons less, than the original air- impregnated graphite. (AEC)

Stable dispersions of polymer-coated graphitic nanoplatelets

NASA Technical Reports Server (NTRS)

Nguyen, Sonbinh T. (Inventor); Stankovich, Sasha (Inventor); Ruoff, Rodney S. (Inventor)

2011-01-01

A method of making a dispersion of reduced graphite oxide nanoplatelets involves providing a dispersion of graphite oxide nanoplatelets and reducing the graphite oxide nanoplatelets in the dispersion in the presence of a reducing agent and a polymer. The reduced graphite oxide nanoplatelets are reduced to an extent to provide a higher C/O ratio than graphite oxide. A stable dispersion having polymer-treated reduced graphite oxide nanoplatelets dispersed in a dispersing medium, such as water or organic liquid is provided. The polymer-treated, reduced graphite oxide nanoplatelets can be distributed in a polymer matrix to provide a composite material.

Structural disorder of graphite and implications for graphite thermometry

NASA Astrophysics Data System (ADS)

Kirilova, Martina; Toy, Virginia; Rooney, Jeremy S.; Giorgetti, Carolina; Gordon, Keith C.; Collettini, Cristiano; Takeshita, Toru

2018-02-01

Graphitization, or the progressive maturation of carbonaceous material, is considered an irreversible process. Thus, the degree of graphite crystallinity, or its structural order, has been calibrated as an indicator of the peak metamorphic temperatures experienced by the host rocks. However, discrepancies between temperatures indicated by graphite crystallinity versus other thermometers have been documented in deformed rocks. To examine the possibility of mechanical modifications of graphite structure and the potential impacts on graphite thermometry, we performed laboratory deformation experiments. We sheared highly crystalline graphite powder at normal stresses of 5 and 25 megapascal (MPa) and aseismic velocities of 1, 10 and 100 µm s-1. The degree of structural order both in the starting and resulting materials was analyzed by Raman microspectroscopy. Our results demonstrate structural disorder of graphite, manifested as changes in the Raman spectra. Microstructural observations show that brittle processes caused the documented mechanical modifications of the aggregate graphite crystallinity. We conclude that the calibrated graphite thermometer is ambiguous in active tectonic settings.

International strategic minerals inventory summary report; natural graphite

USGS Publications Warehouse

Krauss, U.H.; Schmidt, H.W.; Taylor, H.A.; Sutphin, D.M.

1989-01-01

Natural graphite is a crystalline mineral of pure carbon which normally occurs in the form of platelet-shaped crystals. It has important properties, such as chemical inertness, low thermal expansion, and lubricity, that make it almost irreplaceable for certain uses such as refractories and steelmaking. Graphite ore types are crystalline (flake and lump} or 'amorphous' (cryptocrystalline}. Refractory applications use the largest total amount of natural graphite, while the most important use of crystalline graphite is in crucibles for handling molten metals. All graphite deposits being mined today are found in the following metamorphic environments: (1) contact metamorphosed coal generally is a source of amorphous graphite; (2)disseminated crystalline flake graphite comes from syngenetic metasediments; and (3) crystalline lump graphite is found in epigenetic veins in high-grade metamorphic regions. Graphite may also occur as a trace mineral in ultrabasic rocks and pegmatites, but these are economically insignificant. The world's identified economically exploitable resources of crystalline graphite in major deposits are estimated to be about 9.7 million metric tons of concentrate. In-place resources of amorphous graphite are about 11.5 million metric tons. Of these, less than 2 percent of the crystalline ore and less than 1 percent of the amorphous ore are in western industrial countries. World mining production of natural graphite rose from 347,000 metric tons in 1973 to 659,000 metric tons in 1986, while the proportion produced by central economy countries increased from about 50 percent for the period from 1973 to 1978 to more than 64 percent in 1979 to 1986. It is estimated that crystalline flake graphite accounts for at least 180,000 metric tons of total annual world mining production of natural graphite, and amorphous graphite makes up the rest.

Transformation of graphite by tectonic and hydrothermal processes in an active plate boundary fault zone, Alpine Fault, New Zealand

NASA Astrophysics Data System (ADS)

Kirilova, Matina; Toy, Virginia; Timms, Nicholas; Halfpenny, Angela; Menzies, Catriona; Craw, Dave; Rooney, Jeremy; Giorgetti, Carolina

2017-04-01

Graphite is a material with one of the lowest frictional strengths, with coefficient of friction of 0.1 and thus in natural fault zones it may act as a natural solid lubricant. Graphitization, or the transformation of organic matter (carbonaceous material, or CM) into crystalline graphite, is induced by compositional and structural changes during diagenesis and metamorphism. The supposed irreversible nature of this process has allowed the degree of graphite crystallinity to be calibrated as an indicator of the peak temperatures reached during progressive metamorphism. We examine processes of graphite emplacement and deformation in the Alpine Fault Zone, New Zealand's active continental tectonic plate boundary. Raman spectrometry indicates that graphite in the distal, amphibolite-facies Alpine Schist, which experienced peak metamorphic temperatures up to 640 ◦C, is highly crystalline and occurs mainly along grain boundaries within quartzo-feldspathic domains. The subsequent mylonitisation in the Alpine Fault Zone resulted in progressive reworking of CM under lower temperature conditions (500◦C-600◦C) in a structurally controlled environment, resulting in spatial clustering in lower-strain protomylonites, and further foliation-alignment in higher-strain mylonites. Subsequent brittle deformation of the mylonitised schists resulted in cataclasites that contain over three-fold increase in the abundance of graphite than mylonites. Furthermore, cataclasites contain graphite with two different habits: highly-crystalline, foliated forms that are inherited mylonitic graphite; and lower-crystallinity, less mature patches of finer-grained graphite. The observed graphite enrichment and the occurrence of poorly-organised graphite in the Alpine Fault cataclasites could result from: i) hydrothermal precipitation from carbon-supersaturated fluids; and/or ii) mechanical degradation by structural disordering of mylonitic graphite combined with strain-induced graphite localisation. The lack of published systematic studies of mechanical modification of the structure of graphite inhibits further conclusion to be drawn. Thus, we performed laboratory deformation experiments during which we sheared highly crystalline graphite powder at room temperature, normal stresses of 5 MPa and 25 MPa and sliding velocities of 1 µm/s, 10 µm/s and 100 µm/s. The degree of graphite crystallinity, both in the starting and resulting materials, was analysed by Raman microspectroscopy. Our results demonstrate consistent decrease of graphite crystallinity with increasing shear strain. We conclude that: i) graphite 'thermometers' are unreliable in brittely deformed rocks; ii) a shear strain calibration of graphite 'thermometers' is needed; iii) fault creep is very likely responsible for the observed structural and textural characteristics of graphite in the Alpine Fault cataclasites. Finally, to investigate the possibility of hydrothermal origin for at least some of the graphite in the Alpine Fault cataclasites we will also present synchrotron FTIR and carbon isotope analysis of the Alpine fault rocks.

Efficacy and safety of a new fully covered self-expandable non-foreshortening metal esophageal stent.

PubMed

Dua, Kulwinder S; Latif, Sahibzada U; Yang, Juliana F; Fang, Tom C; Khan, Abdul; Oh, Young

2014-10-01

Fully covered esophageal self-expandable metal stents (SEMSs) are potentially removable but can be associated with high migration rates. For precise positioning, non-foreshortening SEMSs are preferred. Recently, a new fully covered non-foreshortening SEMS with anti-migration features was introduced. To evaluate the efficacy and safety of this new esophageal SEMS. Retrospective study. Single, tertiary-care center. Consecutive patients with malignant and benign strictures with dysphagia grade of ≥3 and patients with fistulas/leaks were studied. Stent placement and removal. Technical success in stent deployment/removal, efficacy in relieving dysphagia and sealing fistulas/leaks, and adverse events. Forty-three stents were placed in 35 patients (mean [± standard deviation] age 65 ± 11 years; 31 male), 24 for malignant and 11 for benign (5 strictures, 6 leaks) indications. Technical success in precise SEMS placement was 100%. The after-stent dysphagia grade improved significantly (at 1 week: 1.5 ± 0.7; at 4 weeks: 1.2 ± 0.4; baseline: 3.8 ± 0.4; P < .0001). Twenty stents were removed for clinical indications, with technical success of 100%. All leaks sealed after SEMS placement and did not recur after stent removal. All benign strictures recurred after stent removal. Adverse events included migration (14%), chest pain (11%), and dysphagia from tissue hyperplasia (6%). There was no stent-related mortality. Nonrandomized, single-center study. The new esophageal SEMS was effective in relieving malignant dysphagia, allowed for precise placement, and was easily removable. It was effective in treating benign esophageal fistulas and leaks. Stent-related adverse events were acceptable. Copyright © 2014 American Society for Gastrointestinal Endoscopy. Published by Elsevier Inc. All rights reserved.

Evaluation of co-cokes from bituminous coal with vacuum resid or decant oil, and evaluation of anthracites, as precursors to graphite

NASA Astrophysics Data System (ADS)

Nyathi, Mhlwazi S.

2011-12-01

Graphite is utilized as a neutron moderator and structural component in some nuclear reactor designs. During the reactor operaction the structure of graphite is damaged by collision with fast neutrons. Graphite's resistance to this damage determines its lifetime in the reactor. On neutron irradiation, isotropic or near-isotropic graphite experiences less structural damage than anisotropic graphite. The degree of anisotropy in a graphite artifact is dependent on the structure of its precursor coke. Currently, there exist concerns over a short supply of traditional precursor coke, primarily due to a steadily increasing price of petroleum. The main goal of this study was to study the anisotropic and isotropic properties of graphitized co-cokes and anthracites as a way of investigating the possibility of synthesizing isotropic or near-isotropic graphite from co-cokes and anthracites. Demonstrating the ability to form isotropic or near-isotropic graphite would mean that co-cokes and anthracites have a potential use as filler material in the synthesis of nuclear graphite. The approach used to control the co-coke structure was to vary the reaction conditions. Co-cokes were produced by coking 4:1 blends of vacuum resid/coal and decant oil/coal at temperatures of 465 and 500 °C for reaction times of 12 and 18 hours under autogenous pressure. Co-cokes obtained were calcined at 1420 °C and graphitized at 3000 °C for 24 hours. Optical microscopy, X-ray diffraction, temperature-programmed oxidation and Raman spectroscopy were used to characterize the products. It was found that higher reaction temperature (500 °C) or shorter reaction time (12 hours) leads to an increase in co-coke structural disorder and an increase in the amount of mosaic carbon at the expense of textural components that are necessary for the formation of anisotropic structure, namely, domains and flow domains. Characterization of graphitized co-cokes showed that the quality, as expressed by the degree of graphitization and crystallite dimensions, of the final product is dependent on the nature of the precursor co-coke. The methodology for studying anthracites was to select two anthracites on basis of rank, PSOC1515 being semi-anthracite and DECS21 anthracite. The selected anthracites were graphitized, in both native and demineralized states, under the same conditions as co-cokes. Products obtained from DECS21 showed higher degrees of graphitization and larger crystallite dimensions than products obtained from PSOC1515. Demineralization of anthracites served to increase the degree of graphitization, indicating that the minerals contained in these anthracites have no graphitization-enhancing ability. A larger crystallite length for products obtained from native versions, compared to demineralized versions, was attributed to a formation and decomposition of a silicon carbide during graphitization of native versions. In order to examine the anisotropic and isotropic properties, nuclear-grade graphite samples obtained from Oak Ridge National Laboratory (ORNL) and commercial graphite purchased from Fluka were characterized under similar conditions as graphitized co-cokes and anthracites. These samples served as representatives of "two extremes", with ORNL samples being the isotropic end and commercial graphite being the anisotropic end. Through evaluating relationships between structural parameters, it was observed that graphitized co-cokes are situated, structurally, somewhere between the "two extremes", whereas graphitized anthracites are closer to the anisotropic end. Basically, co-cokes have a better potential than anthracites to transform to isotropic or near-isotropic graphite upon graphitization. By co-coking vacuum resid/coal instead of decant oil/coal or using 500 °C instead of 465 °C, a shift away from commercial graphite towards ORNL samples was attained. Graphitizing a semi-anthracite or demineralizing anthracites before graphitization also caused a shift towards ORNL samples.

Diamonds in detonation soot

NASA Technical Reports Server (NTRS)

Greiner, N. Roy; Phillips, Dave; Johnson, J. D.; Volk, Fred

1990-01-01

Diamonds 4 to 7 nm in diameter have been identified and partially isolated from soot formed in detonations of carbon-forming composite explosives. The morphology of the soot has been examined by transmission electron microscopy (TEM), and the identity of the diamond has been established by the electron diffraction pattern of the TEM samples and by the X-ray diffraction (XRD) pattern of the isolated solid. Graphite is also present in the form of ribbons of turbostatic structure with a thickness of 2 to 4 nm. A fraction, about 25 percent of the soot by weight, was recovered from the crude soot after oxidation of the graphite with fuming perchloric acid. This fraction showed a distinct XRD pattern of diamond and the diffuse band of amorphous carbon. The IR spectrum of these diamonds closely matches that of diamonds recovered from meteorites (Lewis et al., 1987), perhaps indicating similar surface properties after the oxidation. If these diamonds are produced in the detonation itself or during the initial expansion, they exhibit a phenomenal crystal growth rate (5 nm/0.00001 s equal 1.8 m/hr) in a medium with a very low hydrogen/carbon ratio. Because the diamonds will be carried along with the expanding gases, they will be accelerated to velocities approaching 8 km/s.

EXPLORATORY DEVELOPMENT OF GRAPHITE MATERIALS.

DTIC Science & Technology

COMPOSITE MATERIALS), (* GRAPHITE , (*FIBERS, GRAPHITE ), (*LAMINATED PLASTICS, GRAPHITE ), MOLDINGS, EXTRUSION, VACUUM, EPOXY RESINS, FILAMENTS, STRESSES, TENSILE PROPERTIES, OXIDATION, PHYSICAL PROPERTIES.

Seals Having Textured Portions for Protection in Space Environments

NASA Technical Reports Server (NTRS)

Daniels, Christopher (Inventor); Garafolo, Nicholas (Inventor)

2016-01-01

A sealing construct for a space environment includes a seal-bearing object, a seal on the seal-bearing object, and a seal-engaging object. The seal includes a seal body having a sealing surface, and a textured pattern at the sealing surface, the textured pattern defining at least one shaded channel surface. The seal-engaging object is selectively engaged with the seal-bearing object through the seal. The seal-engaging object has a sealing surface, wherein, when the seal-engaging object is selectively engaged with the seal-bearing object, the sealing surface of the seal-engaging object engages the sealing surface of the seal, and the seal is compressed between the seal-bearing object and the seal-engaging object such that at least one shaded channel surface engages the sealing surface of the seal-engaging object.

Apical closure device for full-percutaneous transapical valve implantation: stress-test in an animal model†.

PubMed

Ferrari, Enrico; Demertzis, Stefanos; Angelella, Jennifer; Berdajs, Denis; Tozzi, Piergiorgio; Moccetti, Tiziano; Maisano, Francesco; von Segesser, Ludwig K

2017-05-01

Transapical valve implantation is traditionally performed through a left antero-lateral mini-thoracotomy. A self-expandable apical closure device has recently been developed for full-percutaneous transapical valve implantation. We performed haemodynamics stress-tests on an animal model to evaluate the sealing properties. Under general anaesthesia 5 pigs (mean weight: 67 ± 6 Kg) received full heparinization (100 IU/Kg; activated clotting time >250 s and, through inferior mini-sternotomies, 21-Fr introducer sheaths for transapical aortic valve implantation (outer diameter: 25-Fr) were placed over-the-wire in the apexes. Delivery-catheters carrying folded occluders (SAFEX TM final design) were inserted in the introducer sheaths and plugs were then deployed under fluoroscopic guidance. Phase 1: after protamine injection, apical bleeding was monitored for 1 h with standard haemodynamics condition. Phase 2: we induced systemic hypertension with adrenaline infusion to test the sealing properties under stress. Animals were sacrificed after Phase 2 and hearts were removed and inspected. Five plugs were successfully introduced and deployed in 5 pig hearts. Plugs provided good apical sealing in each animal and a mean of 7 ± 4 ml of blood lost per animal was collected during Phase 1: haemodynamics remained stable and no plug dislodgement was detected (mean blood pressure: 52 ± 9 mmHg). During Phase 2, mean systolic and diastolic peak levels reached 268 ± 24 mmHg and 175 ± 17 mmHg, respectively, without plug dislodgment or bleeding. Post-mortem inspection showed good plug deployment and fixation without myocardial damage. The new apical occluder seals large-sized apical access sites in animal models also during induced systemic hypertension. This pilot study is a further step towards full-percutaneous transapical valve procedures in the clinical setting. © The Author 2017. Published by Oxford University Press on behalf of the European Association for Cardio-Thoracic Surgery. All rights reserved.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gao, J.X.; Wei, B.Q.; Li, D.D.

The evolution of microstructure in bainite during graphitization annealing at 680 °C of Jominy-quenched bars of an Al-Si bearing medium carbon (0.4C wt%) steel has been studied and compared with that in martensite by using light, scanning and transmission electron microscopy. The results show that the graphitization process in bainite is different from that in martensite in many aspects such as the initial carbon state, the behavior of cementite, the nucleation-growth feature and kinetics of formation of graphite spheroids during graphitization annealing, and the shape, size and distribution of these graphite spheroids. The fact that the graphitization in bainite canmore » produce more homogeneous graphite spheroids with more spherical shape and finer size in a shorter annealing time without the help of preexisting coring particles implies that bainite should be a better starting structure than martensite for making graphitic steel. - Highlights: • This article presents a microstructural characterization of formation of graphite spheroids in bainite. • Nucleation and growth characteristics of graphite spheroids formed in bainite and martensite are compared. • Bainite should be a better starting structure for making graphitic steel as results show.« less

Adsorption-synergic biodegradation of diesel oil in synthetic seawater by acclimated strains immobilized on multifunctional materials.

PubMed

Wang, Xin; Wang, Xuejiang; Liu, Mian; Bu, Yunjie; Zhang, Jing; Chen, Jie; Zhao, Jianfu

2015-03-15

Using enrichment culture technique, three isolates marked as ODB-1, ODB-2 and ODB-3, were selected from oil contaminated seawater. 16S rDNA gene sequencing indicated that ODB-1 affiliated with Pseudomonas sp. while ODB-2 and ODB-3 affiliated with Brevundimonas sp. Subsequently, the bacterial cells were immobilized on the surface of expanded graphite (EG), expanded perlite (EP) and bamboo charcoal (BC). Among the three isolates, ODB-1 showed a strong binding to the bio-carriers through extracellular polysaccharides, while ODB-2 and ODB-3 made the adhesion to bio-carrier through direct physical adsorption. The immobilized bacteria exhibited good salinity tolerance compared with the planktonic bacteria. Their total diesel oil removal rates were more than 85% after 6 days' incubation. Adsorption-biodegradation process played an important role in the oil-pollution remediation. EG-bacteria system was treated as a promising remediation method, which achieved nearly 100% removal of diesel oil. Thereinto, over 83% removal of diesel oil owed to biodegradation. Copyright © 2014 Elsevier Ltd. All rights reserved.

40 CFR 436.380 - Applicability; description of the graphite subcategory.

Code of Federal Regulations, 2012 CFR

2012-07-01

... graphite subcategory. 436.380 Section 436.380 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY... Graphite Subcategory § 436.380 Applicability; description of the graphite subcategory. The provisions of this subpart are applicable to the mining and processing of naturally occurring graphite. ...

Method for producing thin graphite flakes with large aspect ratios

DOEpatents

Bunnell, L. Roy

1993-01-01

A method for making graphite flakes of high aspect ratio by the steps of providing a strong concentrated acid and heating the graphite in the presence of the acid for a time and at a temperature effective to intercalate the acid in the graphite; heating the intercalated graphite at a rate and to a temperature effective to exfoliate the graphite in discrete layers; subjecting the graphite layers to ultrasonic energy, mechanical shear forces, or freezing in an amount effective to separate the layes into discrete flakes.

State-of-the-art of alkaline rechargeable batteries

NASA Astrophysics Data System (ADS)

Morioka, Y.; Narukawa, S.; Itou, T.

Alkaline rechargeable batteries represented by Ni-Cd and Ni-MH batteries are expanding their market, continuously meeting an increasing demand. Approximately 30 years have elapsed since the first sealed Ni-Cd battery was commercialized for consumer use, and the production of these alkaline batteries is still expanding. The high power performance and good cost performance of these batteries are the outstanding features, which are leading to new battery applications. Continuous R&D of many researchers and engineers has improved these features. Since first coming to the market in 1990, Ni-MH batteries have been extending their application as power sources for portable advanced information and communication equipment. Improvements in electrode materials and other components have increased the energy density of current Ni-MH batteries to values of 91 Wh/kg and 340 Wh/l. Recently, novel metallic alloys for hydrogen storage have been proposed to increase their capacity further, and further improvement in the performance of these batteries is expected.

EFFECTS OF ONE WEEK TRITIUM EXPOSURE ON EPDM ELASTOMER

DOE Office of Scientific and Technical Information (OSTI.GOV)

Clark, E

This report documents test results for the exposure of four formulations of EPDM (ethylene-propylene diene monomer) elastomer to tritium gas at one atmosphere for approximately one week and characterization of material property changes and changes to the exposure gas during exposure. All EPDM samples were provided by Los Alamos National Laboratory (LANL). Material properties that were characterized include mass, sample dimensions, appearance, flexibility, and dynamic mechanical properties. The glass transition temperature was determined by analysis of the dynamic mechanical property data per ASTM standards. No change of glass transition temperature due to the short tritium gas exposure was observed. Filledmore » and unfilled formulations of Dupont{reg_sign} Nordel{trademark} 1440 had a slightly higher glass transition temperature than filled and unfilled formulations of Uniroyal{reg_sign} Royalene{reg_sign} 580H; filled formulations had the same glass transition as unfilled. The exposed samples appeared the same as before exposure--there was no evidence of discoloration, and no residue on stainless steel spacers contacting the samples during exposure was observed. The exposed samples remained flexible--all formulations passed a break test without failing. The unique properties of polymers make them ideal for certain components in gas handling systems. Specifically, the resiliency of elastomers is ideal for sealing surfaces, for example in valves. EPDM, initially developed in the 1960s, is a hydrocarbon polymer used extensively for sealing applications. EPDM is used for its excellent combination of properties including high/low-temperature resistance, radiation resistance, aging resistance, and good mechanical properties. This report summarizes initial work to characterize effects of tritium gas exposure on samples of four types of EPDM elastomer: graphite filled and unfilled formulations of Nordel{trademark} 1440 and Royalene{reg_sign} 580H.« less

Physical, electrochemical, and thermal properties of granulated natural graphite as anodes for Li-ion batteries.

PubMed

Jo, Yong Nam; Park, Min-Sik; Kim, Jae-Hun; Kim, Young-Jun

2013-05-01

Two different types of granulated graphites were synthesized by blending and kneading of natural graphite with pitch followed by sintering methods. The electrochemical performances of granulated graphites were investigated as anode materials for use in Li-ion batteries. The blending type granulated graphite possesses a large amount of cavities and voids, while the kneading type granulated graphite has a relatively compact microstructure, which is responsible for a high tap density. Both granulated graphites show improved the initial coulombic efficiencies as a result of decrease of surface area by the granulations. In particular, the kneading type granulated graphite exhibits an excellent rate-capability without significant capacity loss. In addition, the thermal stabilities of both granulated graphites were also improved, which could be attributed to the decrease of active surface area due to pitch coating.

Effect of Reacting Surface Density on the Overall Graphite Oxidation Rate

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang H. Oh; Eung Kim; Jong Lim

2009-05-01

Graphite oxidation in an air-ingress accident is presently a very important issue for the reactor safety of the very high temperature gas cooled-reactor (VHTR), the concept of the next generation nuclear plant (NGNP) because of its potential problems such as mechanical degradation of the supporting graphite in the lower plenum of the VHTR might lead to core collapse if the countermeasure is taken carefully. The oxidation process of graphite has known to be affected by various factors, including temperature, pressure, oxygen concentration, types of graphite, graphite shape and size, flow distribution, etc. However, our recent study reveals that the internalmore » pore characteristics play very important roles in the overall graphite oxidation rate. One of the main issues regarding graphite oxidation is the potential core collapse problem that may occur following the degradation of graphite mechanical strength. In analyzing this phenomenon, it is very important to understand the relationship between the degree of oxidization and strength degradation. In addition, the change of oxidation rate by graphite oxidation degree characterization by burn-off (ratio of the oxidized graphite density to the original density) should be quantified because graphite strength degradation is followed by graphite density decrease, which highly affects oxidation rates and patterns. Because the density change is proportional to the internal pore surface area, they should be quantified in advance. In order to understand the above issues, the following experiments were performed: (1)Experiment on the fracture of the oxidized graphite and validation of the previous correlations, (2) Experiment on the change of oxidation rate using graphite density and data collection, (3) Measure the BET surface area of the graphite. The experiments were performed using H451 (Great Lakes Carbon Corporation) and IG-110 (Toyo Tanso Co., Ltd) graphite. The reason for the use of those graphite materials is because their chemical and mechanical characteristics are well identified by the previous investigations, and therefore it was convenient for us to access the published data, and to apply and validate our new methodologies. This paper presents preliminary results of compressive strength vs. burn-off and surface area density vs. burn-off, which can be used for the nuclear graphite selection for the NGNP.« less

Systems and methods for forming defects on graphitic materials and curing radiation-damaged graphitic materials

DOEpatents

Ryu, Sunmin; Brus, Louis E.; Steigerwald, Michael L.; Liu, Haitao

2012-09-25

Systems and methods are disclosed herein for forming defects on graphitic materials. The methods for forming defects include applying a radiation reactive material on a graphitic material, irradiating the applied radiation reactive material to produce a reactive species, and permitting the reactive species to react with the graphitic material to form defects. Additionally, disclosed are methods for removing defects on graphitic materials.

Faulting, fracturing and in situ stress prediction in the Ahnet Basin, Algeria — a finite element approach

NASA Astrophysics Data System (ADS)

Beekman, Fred; Badsi, Madjid; van Wees, Jan-Diederik

2000-05-01

Many low-efficiency hydrocarbon reservoirs are productive largely because effective reservoir permeability is controlled by faults and natural fractures. Accurate and low-cost information on basic fault and fracture properties, orientation in particular, is critical in reducing well costs and increasing well recoveries. This paper describes how we used an advanced numerical modelling technique, the finite element method (FEM), to compute site-specific in situ stresses and rock deformation and to predict fracture attributes as a function of material properties, structural position and tectonic stress. Presented are the numerical results of two-dimensional, plane-strain end-member FEM models of a hydrocarbon-bearing fault-propagation-fold structure. Interpretation of the modelling results remains qualitative because of the intrinsic limitations of numerical modelling; however, it still allows comparisons with (the little available) geological and geophysical data. In all models, the weak mechanical strength and flow properties of a thick shale layer (the main seal) leads to a decoupling of the structural deformation of the shallower sediments from the underlying sediments and basement, and results in flexural slip across the shale layer. All models predict rock fracturing to initiate at the surface and to expand with depth under increasing horizontal tectonic compression. The stress regime for the formation of new fractures changes from compressional to shear with depth. If pre-existing fractures exist, only (sub)horizontal fractures are predicted to open, thus defining the principal orientation of effective reservoir permeability. In models that do not include a blind thrust fault in the basement, flexural amplification of the initial fold structure generates additional fracturing in the crest of the anticline controlled by the material properties of the rocks. The folding-induced fracturing expands laterally along the stratigraphic boundaries under enhanced tectonic loading. Models incorporating a blind thrust fault correctly predict the formation of secondary syn- and anti-thetic mesoscale faults in the basement and sediments of the hanging wall. Some of these faults cut reservoir and/or seal layers, and thus may influence effective reservoir permeability and affect seal integrity. The predicted faults divide the sediments across the anticline in several compartments with different stress levels and different rock failure (and proximity to failure). These numerical model outcomes can assist classic interpretation of seismic and well bore data in search of fractured and overpressured hydrocarbon reservoirs.

Effect of graphite target power density on tribological properties of graphite-like carbon films

NASA Astrophysics Data System (ADS)

Dong, Dan; Jiang, Bailing; Li, Hongtao; Du, Yuzhou; Yang, Chao

2018-05-01

In order to improve the tribological performance, a series of graphite-like carbon (GLC) films with different graphite target power densities were prepared by magnetron sputtering. The valence bond and microstructure of films were characterized by AFM, TEM, XPS and Raman spectra. The variation of mechanical and tribological properties with graphite target power density was analyzed. The results showed that with the increase of graphite target power density, the deposition rate and the ratio of sp2 bond increased obviously. The hardness firstly increased and then decreased with the increase of graphite target power density, whilst the friction coefficient and the specific wear rate increased slightly after a decrease with the increasing graphite target power density. The friction coefficient and the specific wear rate were the lowest when the graphite target power density was 23.3 W/cm2.

AGC 2 Irradiated Material Properties Analysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Rohrbaugh, David Thomas

2017-05-01

The Advanced Reactor Technologies Graphite Research and Development Program is conducting an extensive graphite irradiation experiment to provide data for licensing of a high temperature reactor (HTR) design. In past applications, graphite has been used effectively as a structural and moderator material in both research and commercial high temperature gas cooled reactor designs. , Nuclear graphite H 451, used previously in the United States for nuclear reactor graphite components, is no longer available. New nuclear graphite grades have been developed and are considered suitable candidates for new HTR reactor designs. To support the design and licensing of HTR core componentsmore » within a commercial reactor, a complete properties database must be developed for these current grades of graphite. Quantitative data on in service material performance are required for the physical, mechanical, and thermal properties of each graphite grade, with a specific emphasis on data accounting for the life limiting effects of irradiation creep on key physical properties of the HTR candidate graphite grades. Further details on the research and development activities and associated rationale required to qualify nuclear grade graphite for use within the HTR are documented in the graphite technology research and development plan.« less

AGC 2 Irradiation Creep Strain Data Analysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Windes, William E.; Rohrbaugh, David T.; Swank, W. David

2016-08-01

The Advanced Reactor Technologies Graphite Research and Development Program is conducting an extensive graphite irradiation experiment to provide data for licensing of a high temperature reactor (HTR) design. In past applications, graphite has been used effectively as a structural and moderator material in both research and commercial high temperature gas cooled reactor designs. Nuclear graphite H-451, used previously in the United States for nuclear reactor graphite components, is no longer available. New nuclear graphite grades have been developed and are considered suitable candidates for new HTR reactor designs. To support the design and licensing of HTR core components within amore » commercial reactor, a complete properties database must be developed for these current grades of graphite. Quantitative data on in service material performance are required for the physical, mechanical, and thermal properties of each graphite grade, with a specific emphasis on data accounting for the life limiting effects of irradiation creep on key physical properties of the HTR candidate graphite grades. Further details on the research and development activities and associated rationale required to qualify nuclear grade graphite for use within the HTR are documented in the graphite technology research and development plan.« less

The impact of LDEF results on the space application of metal matrix composites

NASA Technical Reports Server (NTRS)

Steckel, Gary L.; Le, Tuyen D.

1993-01-01

Over 200 graphite/aluminum and graphite/magnesium composites were flown on the leading and trailing edges of LDEF on the Advanced Composites Experiment. The performance of these composites was evaluated by performing scanning electron microscopy and x-ray photoelectron spectroscopy of exposed surfaces, optical microscopy of cross sections, and on-orbit and postflight thermal expansion measurements. Graphite/aluminum and graphite/magnesium were found to be superior to graphite/polymer matrix composites in that they are inherently resistant to atomic oxygen and are less susceptible to thermal cycling induced microcracking. The surface foils on graphite/aluminum and graphite/magnesium protect the graphite fibers from atomic oxygen and from impact damage from small micrometeoroid or space debris particles. However, the surface foils were found to be susceptible to thermal fatigue cracking arising from contamination embrittlement, surface oxidation, or stress risers. Thus, the experiment reinforced requirements for carefully protecting these composites from prelaunch oxidation or corrosion, avoiding spacecraft contamination, and designing composite structures to minimize stress concentrations. On-orbit strain measurements demonstrated the importance of through-thickness thermal conductivity in composites to minimize thermal distortions arising from thermal gradients. Because of the high thermal conductivity of aluminum, thermal distortions were greatly reduced in the LDEF thermal environment for graphite/aluminum as compared to graphite/magnesium and graphite/polymer composites. The thermal expansion behavior of graphite/aluminum and graphite/magnesium was stabilized by on-orbit thermal cycling in the same manner as observed in laboratory tests.

Natural graphite demand and supply - Implications for electric vehicle battery requirements

USGS Publications Warehouse

Olson, Donald W.; Virta, Robert L.; Mahdavi, Mahbood; Sangine, Elizabeth S.; Fortier, Steven M.

2016-01-01

Electric vehicles have been promoted to reduce greenhouse gas emissions and lessen U.S. dependence on petroleum for transportation. Growth in U.S. sales of electric vehicles has been hindered by technical difficulties and the high cost of the lithium-ion batteries used to power many electric vehicles (more than 50% of the vehicle cost). Groundbreaking has begun for a lithium-ion battery factory in Nevada that, at capacity, could manufacture enough batteries to power 500,000 electric vehicles of various types and provide economies of scale to reduce the cost of batteries. Currently, primary synthetic graphite derived from petroleum coke is used in the anode of most lithium-ion batteries. An alternate may be the use of natural flake graphite, which would result in estimated graphite cost reductions of more than US$400 per vehicle at 2013 prices. Most natural flake graphite is sourced from China, the world's leading graphite producer. Sourcing natural flake graphite from deposits in North America could reduce raw material transportation costs and, given China's growing internal demand for flake graphite for its industries and ongoing environmental, labor, and mining issues, may ensure a more reliable and environmentally conscious supply of graphite. North America has flake graphite resources, and Canada is currently a producer, but most new mining projects in the United States require more than 10 yr to reach production, and demand could exceed supplies of flake graphite. Natural flake graphite may serve only to supplement synthetic graphite, at least for the short-term outlook.

NASA Orbit Transfer Rocket Engine Technology Program

NASA Technical Reports Server (NTRS)

1984-01-01

The advanced expander cycle engine with a 15,000 lb thrust level and a 6:1 mixture ratio and optimized performance was used as the baseline for a design study of the hydrogen/oxgyen propulsion system for the orbit transfer vehicle. The critical components of this engine are the thrust chamber, the turbomachinery, the extendible nozzle system, and the engine throttling system. Turbomachinery technology is examined for gears, bearing, seals, and rapid solidification rate turbopump shafts. Continuous throttling concepts are discussed. Components of the OTV engine described include the thrust chamber/nozzle assembly design, nozzles, the hydrogen regenerator, the gaseous oxygen heat exchanger, turbopumps, and the engine control valves.

An approach to the implementation of ISO 14000 at a shipping company

NASA Astrophysics Data System (ADS)

Panaitescu, F. V.; Panaitescu, M.

2015-11-01

We present here a successful implementation of the Environmental Management System (EMS) in a shipping company. The EMS of the each company must be revised and expanded and new analytical requirements included in it. This new EMS concept is available to everyone on board and must be studied by every seafarer. All environmental requirements to be strictly followed all over the world. The main points of new EMS are: new open reporting system, environmental tag system (ETS) which introduce non re-usable numbered seals, pollution prevention equipment (OWS, OCM, Incinerator and Sewage Treatment Plant), the environmental defect reports system - extraordinary E/R operations and leakages log book.

Treatment of irradiated graphite from French Bugey reactor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stevens, Howard; Laurent, Gerard

In 2008, following the general French plan for nuclear waste management, Electricite de France attempted to find for irradiated graphite an alternative solution to direct storage at the low-activity long-life storage center in France managed by the national agency for wastes (ANDRA). EDF management requested that its engineering arm, EDF CIDEN, study the graphite treatment alternatives to direct storage. In mid-2008, this study revealed the potential advantage for EDF to use a steam reforming process known as Thermal Organic Reduction, 'THOR' (owned by Studsvik, Inc., USA), to treat or destroy the graphite matrix and limit the quantity of secondary wastemore » to be stored. In late 2009, EDF began a test program with Studsvik to determine if the THOR steam reforming process could be used to destroy the graphite. The program also sought to determine if the graphite could be treated to release the bulk of activity while minimizing the gasification of the bulk mass of the graphite. In October 2009, tests with non-irradiated graphite were completed and demonstrated destruction of a graphite matrix by the THOR process at satisfactory rates. After gasifying the graphite, focus shifted to the effect of roasting graphite at high temperatures in inert gases with low concentrations of oxidizing gases to preferentially remove volatile radionuclides while minimizing the graphite mass loss to 5%. A radioactive graphite sleeve was imported from France to the US for these tests. Completed in April 2010, 'Phase I' of testing showed that the process removed >99% of H-3 and 46% of C-14 with <6% mass loss. Completed in September 2011, 'Phase II' testing achieved increased removals as high as 80% C-14. During Phase II, it was also discovered that roasting in a reducing atmosphere helped to limit the oxidation of the graphite. Future work seeks to explore the effects of reducing gases to limit the bulk oxidation of graphite. If the graphite could be decontaminated of long-lived radionuclides up to 95% for C-14 while minimizing mass loss to <5%, this would minimize the volume of any secondary waste streams and potentially lower the waste class of the larger bulk of graphite. Alternatively, if up to 95% decontamination of C-14 is achieved, the graphite may be completely gasified which could result in lower disposal. (authors)« less

High-temperature, high-pressure bonding of nested tubular metallic components

DOEpatents

Quinby, T.C.

A tool is described for effecting high-temperature, high-compression bonding between the confronting faces of nested, tubular, metallic components. In a typical application, the tool is used to produce tubular target assemblies for irradiation in nuclear reactors or particle accelerators. The target assembly comprising a uranum foil and an aluninum-alloy substrate. The tool is composed of graphite. It comprises a tubular restraining member in which a mechanically expandable tubular core is mounted to form an annulus. The components to be bonded are mounted in nested relation in the annulus. The expandable core is formed of individually movable, axially elongated segments whose outer faces cooperatively define a cylindrical pressing surface and whose inner faces cooperatively define two opposed, inwardly tapered, axial bores. Tapered rams extend into the bores. The loaded tool is mounted in a conventional hot-press provided with evacuation means, heaters for maintaining its interior at bonding temperature, and hydraulic cylinders for maintaining a selected inwardly directed pressure on the tapered rams. With the hot-press evacuated and the loaded tool at the desired temperature, the cylinders are actuated to apply the selected pressure to the rams. The rams in turn expand the segmented core to maintain the nested components in compression against the restraining member. These conditions are maintained until the confronting faces of the nested components are joined in a continuous, uniform bond characterized by high thermal conductivity.

Fuel Cell Thermal Management Through Conductive Cooling Plates

NASA Technical Reports Server (NTRS)

Colozza, Anthony J.; Burke, Kenneth A.

2008-01-01

An analysis was performed to evaluate the concept of utilizing conductive cooling plates to remove heat from a fuel cell stack, as opposed to a conventional internal cooling loop. The potential advantages of this type of cooling system are reduced stack complexity and weight and increased reliability through the reduction of the number of internal fluid seals. The conductive cooling plates would extract heat from the stack transferring it to an external coolant loop. The analysis was performed to determine the required thickness of these plates. The analysis was based on an energy balance between the thermal energy produced within the stack and the heat removal from the cooling plates. To accomplish the energy balance, the heat flow into and along the plates to the cooling fluid was modeled. Results were generated for various numbers of cells being cooled by a single cooling plate. The results provided cooling plate thickness, mass, and operating temperature of the plates. It was determined that utilizing high-conductivity pyrolitic graphite cooling plates can provide a specific cooling capacity (W/kg) equivalent to or potentially greater than a conventional internal cooling loop system.

Microstructures of Pd-containing dispersants for admixed dental amalgams.

PubMed

Chern Lin, J H; Greener, E H

1991-10-01

Blended Pd-containing dispersants were developed by the utilization of a Ag-Cu eutectic into which Pd was substituted for Ag or Cu in concentrations of up to 20 wt%. Compositions were melted either in argon-filled sealed vycor tubes or in a graphite-linked carbon crucible of an induction furnace with an argon blanket. Ingots of approximately 1.5 cm in diameter were sectioned to 0.2 cm in thickness and polished through standard metallographic polishing procedures. The possible compounds were identified by XRD. The microstructures of the alloys were examined by SEM/EDS. XRD analysis of the alloys revealed the preferential dissolution of Pd in Cu when the Pd concentration was less than or equal to 10 wt%. When the Pd concentration exceeded 20 wt%, Pd was found to be dissolved in both Ag and Pd. No Cu3Pd x-ray diffraction peaks were found for alloys with Pd concentration of up to 20 wt%. SEM/EDS analysis confirmed XRD results; lamellae of Ag and Cu-Pd were found in alloys with Pd concentration less than or equal to 10 wt%.

Bridged graphite oxide materials

NASA Technical Reports Server (NTRS)

Herrera-Alonso, Margarita (Inventor); McAllister, Michael J. (Inventor); Aksay, Ilhan A. (Inventor); Prud'homme, Robert K. (Inventor)

2010-01-01

Bridged graphite oxide material comprising graphite sheets bridged by at least one diamine bridging group. The bridged graphite oxide material may be incorporated in polymer composites or used in adsorption media.

Preparation of graphitic articles

DOEpatents

Phillips, Jonathan; Nemer, Martin; Weigle, John C.

2010-05-11

Graphitic structures have been prepared by exposing templates (metal, metal-coated ceramic, graphite, for example) to a gaseous mixture that includes hydrocarbons and oxygen. When the template is metal, subsequent acid treatment removes the metal to yield monoliths, hollow graphitic structures, and other products. The shapes of the coated and hollow graphitic structures mimic the shapes of the templates.

Method of Obtaining Uniform Coatings on Graphite

DOEpatents

Campbell, I. E.

1961-04-01

A method is given for obtaining uniform carbide coatings on graphite bodies. According to the invention a metallic halide in vapor form is passed over the graphite body under such conditions of temperature and pressure that the halide reacts with the graphite to form a coating of the metal carbide on the surface of the graphite.

METHOD OF OBTAINING UNIFORM COATINGS ON GRAPHITE

DOEpatents

Campbell, I.E.

1961-04-01

A method is given for obtaining uniform carbide coatings on graphite bodies. According to the invention a metallic halide in vapor form is passed over the graphite body under such conditions of temperature and pressure that the halide reacts with the graphite to form a coating of the metal carbide on the surface of the graphite.

Morphological and optoelectronic characteristics of nanocomposites comprising graphene nanosheets and poly(3-hexylthiophene).

PubMed

Chang, Yo-Wei; Yu, Shiau-Wei; Liu, Cheng-Hao; Tsiang, Raymond Chien-Chao

2010-10-01

P3HT/graphene nanocomposite was prepared via in-situ reduction of exfoliated graphite oxide in the P3HT polymer matrix, where the exfoliated graphite oxide was formed beforehand via the oxidation of graphite via the Hummers method. The oxidation reaction not only imparts functional groups, such as C=O, C-OH, and C-O-C, to graphite but also causes exfoliation of the resulting graphite oxide. The functional groups render graphite oxide an additional, lower thermal degradation temperature (T(d)) and the exfoliation shifts the XRD pattern towards a much smaller angle. The oxidation of graphite into graphite oxide creates a pleated flaking morphology for graphite oxide as opposed to that of graphite. UV/Vis and photoluminescence (PL) spectra of P3HT/graphene nanocomposite indicate that the existence of graphene does not alter the UV/Vis and PL excitation characteristics of P3HT, and the P3HT/graphene composite has higher electron mobility, a smaller band gap and higher conductivity than the pristine P3HT.

Increasing Patient Safety by Closing the Sterile Production Gap-Part 1. Introduction.

PubMed

Agalloco, James P

2017-01-01

Terminal sterilization is considered the preferred means for the production of sterile drug products because it affords enhanced safety for the patient as the formulation is filled into its final container, sealed, and sterilized. Despite the obvious patient benefits, the use of terminal sterilization is artificially constrained by unreasonable expectations for the minimum time-temperature process to be used. The core misunderstanding with terminal sterilization is a fixation that destruction of a high population of a resistant biological indicator is required. The origin of this misconception is unclear, but it has resulted in sterilization conditions that are extremely harsh (15 min at 121 °C, of F 0 > 8 min), which limit the use of terminal sterilization to extremely heat-stable formulations. These articles outline the artificial nature of the process constraints and describe a scientifically sound means to expand the use of terminal sterilization by identifying the correct process goal-destruction of the bioburden present in the container prior to sterilization. Recognition that the true intention is bioburden destruction in routine products allows for the use of reduced conditions (lower temperatures, shorter process dwell, or both) without added patient risk. By focusing attention on the correct process target, lower time-temperature conditions can be used to expand the use of terminal sterilization to products unable to withstand the harsh conditions that have been mistakenly applied. The first article provides the background and describes the benefits to patient, producer, and regulator. The second article includes validation and operational advice that can be used in the implementation. LAY ABSTRACT: Terminal sterilization is considered the preferred means for the production of sterile drug products because it affords enhanced safety for the patient as the formulation is filled into its final container, sealed, and sterilized. Despite the obvious patient benefits, the use of terminal sterilization is artificially constrained by unreasonable expectations for the minimum time-temperature process to be used. These articles outline the artificial nature of the process constraints and describe a scientifically sound means to expand the use of terminal sterilization by identifying the correct process goal-destruction of the bioburden present in the container prior to sterilization. By focusing attention on the correct process target, lower time-temperature conditions can be used to expand the use of terminal sterilization to products unable to withstand the harsh conditions that have been mistakenly applied. The first article provides the background, and describes the benefits to patient, producer, and regulator. The second article includes validation and operational advice that can be used in the implementation. © PDA, Inc. 2017.

GRAFEC: A New Spanish Program to Investigate Waste Management Options for Radioactive Graphite - 12399

DOE Office of Scientific and Technical Information (OSTI.GOV)

Marquez, Eva; Pina, Gabriel; Rodriguez, Marina

Spain has to manage about 3700 tons of irradiated graphite from the reactor Vandellos I as radioactive waste. 2700 tons are the stack of the reactor and are still in the reactor core waiting for retrieval. The rest of the quantities, 1000 tons, are the graphite sleeves which have been already retrieved from the reactor. During operation the graphite sleeves were stored in a silo and during the dismantling stage a retrieval process was carried out separating the wires from the graphite, which were crushed and introduced into 220 cubic containers of 6 m{sup 3} each and placed in interimmore » storage. The graphite is an intermediate level radioactive waste but it contains long lived radionuclides like {sup 14}C which disqualifies disposal at the low level waste repository of El Cabril. Therefore, a new project has been started in order to investigate two new options for the management of this waste type. The first one is based on a selective decontamination of {sup 14}C by thermal methods. This method is based on results obtained at the Research Centre Juelich (FZJ) in the Frame of the EC programs 'Raphael' and 'Carbowaste'. The process developed at FZJ is based on a preferential oxidation of {sup 14}C in comparison to the bulk {sup 12}C. Explanations for this effect are the inhomogeneous distribution and a weaker bounding of {sup 14}C which is not incorporated in the graphite lattice. However these investigations have only been performed with graphite from the high temperature reactor Arbeitsgemeinschaft Versuchsreaktor Juelich AVR which has been operated in a non-oxidising condition or research reactor graphite operated at room temperature. The reactor Vandellos I has been operated with CO{sub 2} as coolant and significant amounts of graphite have been already oxidised. The aim of the project is to validate whether a {sup 14}C decontamination can also been achieved with graphite from Vandellos I. A second possibility under investigation is the encapsulation of the graphite in a long term stable glass matrix. The principal applicability has been already proved by FNAG. Crushed graphite mixed with a suitable glass powder has been pressed at elevated temperature under vacuum. The vacuum is required to avoid gas enclosures in the obtained product. The obtained products, named IGM for 'Impermeable Graphite Matrix', have densities above 99% of theoretical density. The amount of glass has been chosen with respect to the pore volume of the former graphite parts. The method allows the production of encapsulated graphite without increasing the disposal volume. This paper will give a short overview of characterisation results of different irradiated graphite materials obtained at CIEMAT and in the Carbowaste project as well as the proposed methods and the actual status of the program including first results about leaching of non-radioactive IGM samples and hopefully first tendencies concerning the C-14 separation from graphite of Vandellos I by thermal treatment. Both processes, the thermal treatment as well as the IGM, have the potential to solve problems related to the management of irradiated graphite in Spain. However the methods have only been tested with different types of i-graphite and virgin graphite, respectively. Only investigations with real i-graphite from Spain will reveal whether the described methods are applicable to graphite from Vandellos I. However all partners are convinced that one of these new methods or a combination of them will lead to a feasible option to manage i-graphite in Spain on an industrial scale. (authors)« less

Substitutional doping of carbon nanotubes with heteroatoms and their chemical applications.

PubMed

Zhang, Yexin; Zhang, Jian; Su, Dang Sheng

2014-05-01

The electronic properties of carbon nanotubes (CNTs) can be tuned by substitutional doping with heteroatoms (mainly B and N) to expand the applications of CNTs. Based on the comprehensive understanding of the substitutional doping of CNTs, it should be possible to deliberately design doped CNTs for specific purposes. Thus, relevant experimental and theoretical works are reviewed herein in an attempt to correlate the synthetic methods, electronic properties, and applications of heteroatom-doped CNTs. The distribution and arrangement of heteroatoms in the graphitic lattice of CNTs can be modulated through the choice of synthetic conditions, which would further lead to different electronic properties of CNTs for their chemical applications. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Environmental exposure effects on composite materials for commercial aircraft

NASA Technical Reports Server (NTRS)

Gibbons, M. N.

1982-01-01

The data base for composite materials' properties as they are affected by the environments encountered in operating conditions, both in flight and at ground terminals is expanded. Absorbed moisture degrades the mechanical properties of graphite/epoxy laminates at elevated temperatures. Since airplane components are frequently exposed to atmospheric moisture, rain, and accumulated water, quantitative data are required to evaluate the amount of fluids absorbed under various environmental conditions and the subsequent effects on material properties. In addition, accelerated laboratory test techniques are developed are reliably capable of predicting long term behavior. An accelerated environmental exposure testing procedure is developed, and experimental results are correlated and compared with analytical results to establish the level of confidence for predicting composite material properties.

Research on graphite reinforced glass matrix composites

NASA Technical Reports Server (NTRS)

Bacon, J. F.; Prewo, K. M.

1977-01-01

The results of research for the origination of graphite-fiber reinforced glass matrix composites are presented. The method selected to form the composites consisted of pulling the graphite fiber through a slurry containing powdered glass, winding up the graphite fiber and the glass it picks up on a drum, drying, cutting into segments, loading the tape segment into a graphite die, and hot pressing. During the course of the work, composites were made with a variety of graphite fibers in a glass matrix.

Research on the transformation mechanism of graphite phase and microstructure in the heated region of gray cast iron by laser cladding

NASA Astrophysics Data System (ADS)

Liu, Yancong; Zhan, Xianghua; Yi, Peng; Liu, Tuo; Liu, Benliang; Wu, Qiong

2018-03-01

A double-track lap cladding experiment involving gray cast iron was established to investigate the transformation mechanism of graphite phase and microstructure in a laser cladding heated region. The graphite phase and microstructure in different heated regions were observed under a microscope, and the distribution of elements in various heated regions was analyzed using an electron probe. Results show that no graphite existed in the cladding layer and in the middle and upper parts of the binding region. Only some of the undissolved small graphite were observed at the bottom of the binding region. Except the refined graphite size, the morphological characteristics of substrate graphite and graphite in the heat-affected zone were similar. Some eutectic clusters, which grew along the direction of heat flux, were observed in the heat-affected zone whose microstructure was transformed into a mixture of austenite, needle-like martensite, and flake graphite. Needle-like martensite around graphite was fine, but this martensite became sparse and coarse when it was away from graphite. Some martensite clusters appeared in the local area near the binding region, and the carbon atoms in the substrate did not diffuse into the cladding layer through laser cladding, which only affected the bonding area and the bottom of the cladding layer.

NEW METHOD OF GRAPHITE PREPARATION

DOEpatents

Stoddard, S.D.; Harper, W.T.

1961-08-29

BS>A method is described for producing graphite objects comprising mixing coal tar pitch, carbon black, and a material selected from the class comprising raw coke, calcined coke, and graphite flour. The mixture is placed in a graphite mold, pressurized to at least 1200 psi, and baked and graphitized by heating to about 2500 deg C while maintaining such pressure. (AEC)

Uncertainty analysis of gas flow measurements using clearance-sealed piston provers in the range from 0.0012 g min-1 to 60 g min-1

NASA Astrophysics Data System (ADS)

Bobovnik, G.; Kutin, J.; Bajsić, I.

2016-08-01

This paper deals with an uncertainty analysis of gas flow measurements using a compact, high-speed, clearance-sealed realization of a piston prover. A detailed methodology for the uncertainty analysis, covering the components due to the gas density, dimensional and time measurements, the leakage flow, the density correction factor and the repeatability, is presented. The paper also deals with the selection of the isothermal and adiabatic measurement models, the treatment of the leakage flow and discusses the need for averaging multiple consecutive readings of the piston prover. The analysis is prepared for the flow range (50 000:1) covered by the three interchangeable flow cells. The results show that using the adiabatic measurement model and averaging the multiple readings, the estimated expanded measurement uncertainty of the gas mass flow rate is less than 0.15% in the flow range above 0.012 g min-1, whereas it increases for lower mass flow rates due to the leakage flow related effects. At the upper end of the measuring range, using the adiabatic instead of the isothermal measurement model, as well as averaging multiple readings, proves important.

Endoscopic-assisted resection of a pedunculated uterine leiomyoma with maximal tissue preservation in a cow and a mare.

PubMed

Schneeweiss, Wilfried; Krump, Lea; Metcalfe, Lucy; Ryan, Eoin; Beltman, Marijke; Jahns, Hanne; David, Florent

2015-02-01

To report successful minimally invasive treatment of a uterine leiomyoma in a cow and a mare. Clinical report. Limousine cow (n = 1), Thoroughbred mare (n = 1). A 10-year-old cow and an 18-year-old mare were presented for difficulties in breeding and infertility, respectively. Examination of the reproductive tract revealed the presence of a large mass attached to the uterine wall via a wide and short peduncle in both cases. The mass expanded into the uterine lumen in the mare and into the abdomen in the cow. Both masses were removed using a minimally invasive endoscopic approach and a vessel-sealing and dividing device. Minimally invasive surgical resection of a subserosal and a submucosal leiomyoma with maximal sparing of uterine tissue resulted in a short convalescence period and apparent return to breeding function in a cow and a mare. Use of a vessel-sealing and dividing device provided excellent hemostasis and decreased tissue handling. Leiomyoma with short, wide, and thick peduncles were treated successfully in a cow and a mare with minimally invasive endoscopic approaches aiming at maximal uterine tissue preservation. © Copyright 2014 by The American College of Veterinary Surgeons.

Are the ghosts of nature's past haunting ecology today?

PubMed

Silliman, Brian R; Hughes, Brent B; Gaskins, Lindsay C; He, Qiang; Tinker, M Tim; Read, Andrew; Nifong, James; Stepp, Rick

2018-05-07

Humans have decimated populations of large-bodied consumers and their functions in most of the world's ecosystems. It is less clear how human activities have affected the diversity of habitats these consumers occupy. Rebounding populations of some predators after conservation provides an opportunity to begin to investigate this question. Recent research shows that following long-term protection, sea otters along the northeast Pacific coast have expanded into estuarine marshes and seagrasses, and alligators on the southeast US coast have expanded into saltwater ecosystems, habitats presently thought beyond their niche space. There is also evidence that seals have expanded into subtropical climates, mountain lions into grasslands, orangutans into disturbed forests and wolves into coastal marine ecosystems. Historical records, surveys of protected areas and patterns of animals moving into habitats that were former hunting hotspots indicate that - rather than occupying them for the first time - many of these animals are in fact recolonizing ecosystems. Recognizing that many large consumers naturally live and thrive across a greater diversity of ecosystems has implications for setting historical baselines for predator diversity within specific habitats, enhancing the resilience of newly colonized ecosystems and for plans to recover endangered species, as a greater range of habitats is available for large consumers as refugia from climate-induced threats. Copyright © 2018 Elsevier Ltd. All rights reserved.

Malignant esophageal-tracheobronchial strictures: parallel placement of covered retrievable expandable nitinol stents.

PubMed

Nam, D H; Shin, J H; Song, H Y; Jung, G S; Han, Y M

2006-02-01

To assess the safety and clinical effectiveness of the parallel placement of covered retrievable expandable metallic stents in the palliative treatment of malignant esophageal and tracheobronchial strictures. Under fluoroscopic guidance, parallel stents were placed in 12 symptomatic patients with both malignant esophageal and tracheobronchial strictures. Seven of these 12 patients also had an esophagorespiratory fistula (ERF) and one patient had an esophagocutaneous fistula. Technical success, clinical improvement, complications, and survival rates were evaluated. A total of 28 esophageal and airway stents were successfully placed. The grade of dysphagia and dyspnea score significantly decreased after stent placement (P=0.002 and 0.003, respectively). ERF and esophagocutaneous fistula were sealed off in all eight patients after esophageal stent placement; however, the esophagocutaneous fistula reopened 1 month later. Complications included stent migration or expectoration (n=3), tracheal compression by the esophageal stent (n=3), new fistula development due to covering membrane degradation of the esophageal stent (n=1), and symptomatic sputum retention (n=1). Stent removal was easily performed for two stents; one migrated stent and the other with covering membrane degradation. All 12 patients died within the mean survival period of 72.50 days (range 7-375 days). Parallel placement of covered retrievable expandable metallic stents is safe and effective for the palliative treatment of malignant esophageal and tracheobronchial strictures.

Electronic and total energy properties of ternary and quaternary semiconductor compounds, alloys, and superlattices: Theoretical study of Cu/graphite bonding

NASA Technical Reports Server (NTRS)

Lambrecht, Walter R. L.

1992-01-01

The goals of the research were to provide a fundamental science basis for why the bonding of Cu to graphite is weak, to critically evaluate the previous analysis of the wetting studies with particular regard to the values used for the surface energies of Cu and graphite, and to make recommendations for future experiments or other studies which could advance the understanding and solution of this technological problem. First principles electronic structure calculations were used to study the problem. These are based on density functional theory in the local density approximation and the use of the linear muffin-tin orbital band structure method. Calculations were performed for graphite monolayers, single crystal graphite with the hexagonal AB stacking, bulk Cu, Cu(111) surface, and Cu/graphite superlattices. The study is limited to the basal plane of graphite because this is the graphite plane exposed to Cu and graphite surface energies and combined with the measured contact angles to evaluate the experimental adhesion energy.

Low-energy electron diffraction study of potassium adsorbed on single-crystal graphite and highly oriented pyrolytic graphite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ferralis, N.; Diehl, R.D.; Pussi, K.

2004-12-15

Potassium adsorption on graphite has been a model system for the understanding of the interaction of alkali metals with surfaces. The geometries of the (2x2) structure of potassium on both single-crystal graphite (SCG) and highly oriented pyrolytic graphite (HOPG) were investigated for various preparation conditions for graphite temperatures between 55 and 140 K. In all cases, the geometry was found to consist of K atoms in the hollow sites on top of the surface. The K-graphite average perpendicular spacing is 2.79{+-}0.03 A , corresponding to an average C-K distance of 3.13{+-}0.03 A , and the spacing between graphite planes ismore » consistent with the bulk spacing of 3.35 A. No evidence was observed for a sublayer of potassium. The results of dynamical LEED studies for the clean SCG and HOPG surfaces indicate that the surface structures of both are consistent with the truncated bulk structure of graphite.« less

An Electron Microscopy Study of Graphite Growth in Nodular Cast Irons

NASA Astrophysics Data System (ADS)

Laffont, L.; Jday, R.; Lacaze, J.

2018-04-01

Growth of graphite during solidification and high-temperature solid-state transformation has been investigated in samples cut out from a thin-wall casting which solidified partly in the stable (iron-graphite) and partly in the metastable (iron-cementite) systems. Transmission electron microscopy has been used to characterize graphite nodules in as-cast state and in samples having been fully graphitized at various temperatures in the austenite field. Nodules in the as-cast material show a twofold structure characterized by an inner zone where graphite is disoriented and an outer zone where it is well crystallized. In heat-treated samples, graphite nodules consist of well-crystallized sectors radiating from the nucleus. These observations suggest that the disoriented zone appears because of mechanical deformation when the liquid contracts during its solidification in the metastable system. During heat-treatment, the graphite in this zone recrystallizes. In turn, it can be concluded that nodular graphite growth mechanism is the same during solidification and solid-state transformation.

Understanding the crack formation of graphite particles in cycled commercial lithium-ion batteries by focused ion beam - scanning electron microscopy

NASA Astrophysics Data System (ADS)

Lin, Na; Jia, Zhe; Wang, Zhihui; Zhao, Hui; Ai, Guo; Song, Xiangyun; Bai, Ying; Battaglia, Vincent; Sun, Chengdong; Qiao, Juan; Wu, Kai; Liu, Gao

2017-10-01

The structure degradation of commercial Lithium-ion battery (LIB) graphite anodes with different cycling numbers and charge rates was investigated by focused ion beam (FIB) and scanning electron microscopy (SEM). The cross-section image of graphite anode by FIB milling shows that cracks, resulted in the volume expansion of graphite electrode during long-term cycling, were formed in parallel with the current collector. The crack occurs in the bulk of graphite particles near the lithium insertion surface, which might derive from the stress induced during lithiation and de-lithiation cycles. Subsequently, crack takes place along grain boundaries of the polycrystalline graphite, but only in the direction parallel with the current collector. Furthermore, fast charge graphite electrodes are more prone to form cracks since the tensile strength of graphite is more likely to be surpassed at higher charge rates. Therefore, for LIBs long-term or high charge rate applications, the tensile strength of graphite anode should be taken into account.

Friction and wear of carbon-graphite materials for high-energy brakes

NASA Technical Reports Server (NTRS)

Bill, R. C.

1978-01-01

Caliper type brake simulation experiments were conducted on seven different carbon graphite materials formulations against a steel disk material and against a carbon graphite disk material. The effects of binder level, boron carbide (B4C) additions, SiC additions, graphite fiber additions, and graphite cloth reinforcement on friction and wear behavior were investigated. Reductions in binder level, additions of B4C, and additions of SiC each resulted in increased wear. The wear rate was not affected by the addition of graphite fibers. Transition to severe wear and high friction was observed in the case of graphite-cloth-reinforced carbon sliding against a disk of similar composition. The transition was related to the disruption of a continuous graphite shear film that must form on the sliding surfaces if low wear is to occur.

Fluid-deposited graphitic inclusions in quartz: Comparison between KTB (German Continental Deep-Drilling) core samples and artificially reequilibrated natural inclusions

USGS Publications Warehouse

Pasteris, J.D.; Chou, I.-Ming

1998-01-01

We used Raman microsampling spectroscopy (RMS) to determine the degree of crystallinity of minute (2-15 ??m) graphite inclusions in quartz in two sets of samples: experimentally reequilibrated fluid inclusions in a natural quartz grain and biotite-bearing paragneisses from the KTB deep drillhole in SE Germany. Our sequential reequilibration experiments at 725??C on initially pure CO2 inclusions in a quartz wafer and the J. Krautheim (1993) experiments at 900-1100??C on organic compounds heated in gold or platinum capsules suggest that, at a given temperature, (1) fluid-deposited graphite will have a lower crystallinity than metamorphosed organic matter and (2) that the crystallinity of fluid-deposited graphite is affected by the composition of the fluid from which it was deposited. We determined that the precipitation of more-crystalline graphite is favored by lower fH2 (higher fO2), and that the crystallinity of graphite is established by the conditions (including gas fugacities) that pertain as the fluid first reaches graphite saturation. Graphite inclusions within quartz grains in the KTB rocks show a wide range in crystallinity index, reflecting three episodes of carbon entrapment under different metamorphic conditions. Isolated graphite inclusions have the spectral properties of totally ordered, completely crystalline graphite. Such crystallinity suggests that the graphite was incorporated from the surrounding metasedimentary rocks, which underwent metamorphism at upper amphibolite-facies conditions. Much of the fluid-deposited graphite in fluid inclusions, however, shows some spectral disorder. The properties of that graphite resemble those of experimental precipitates at temperatures in excess of 700??C and at elevated pressures, suggesting that the inclusions represent precipitates from C-O-H fluids trapped under conditions near those of peak metamorphism at the KTB site. In contrast, graphite that is intimately associated with chlorite and other (presumably low-temperature) silicates in inclusions is highly disordered and spectrally resembles kerogens. This graphite probably was deposited during later greenschist-facies retrograde metamorphism at about 400-500??C. The degree of crystallinity of fluid-deposited graphite is shown to be a much more complex function of temperature than is the crystallinity of metamorphic graphite. To some extent, experiments can provide temperature-calibration of the crystallinity index. However, the difference in time scales between experimental runs and geologic processes makes it difficult to infer specific temperatures for naturally precipitated graphite. Copyright ?? 1998 Elsevier Science Ltd.

Tubular graphite cones.

PubMed

Zhang, Guangyu; Jiang, Xin; Wang, Enge

2003-04-18

We report the synthesis of tubular graphite cones using a chemical vapor deposition method. The cones have nanometer-sized tips, micrometer-sized roots, and hollow interiors with a diameter ranging from about 2 to several tens of nanometers. The cones are composed of cylindrical graphite sheets; a continuous shortening of the graphite layers from the interior to the exterior makes them cone-shaped. All of the tubular graphite cones have a faceted morphology. The constituent graphite sheets have identical chiralities of a zigzag type across the entire diameter, imparting structural control to tubular-based carbon structures. The tubular graphite cones have potential for use as tips for scanning probe microscopy, but with greater rigidity and easier mounting than currently used carbon nanotubes.

Process for the fabrication of aluminum metallized pyrolytic graphite sputtering targets

DOEpatents

Makowiecki, D.M.; Ramsey, P.B.; Juntz, R.S.

1995-07-04

An improved method is disclosed for fabricating pyrolytic graphite sputtering targets with superior heat transfer ability, longer life, and maximum energy transmission. Anisotropic pyrolytic graphite is contoured and/or segmented to match the erosion profile of the sputter target and then oriented such that the graphite`s high thermal conductivity planes are in maximum contact with a thermally conductive metal backing. The graphite contact surface is metallized, using high rate physical vapor deposition (HRPVD), with an aluminum coating and the thermally conductive metal backing is joined to the metallized graphite target by one of four low-temperature bonding methods; liquid-metal casting, powder metallurgy compaction, eutectic brazing, and laser welding. 11 figs.

Environmentally benign graphite intercalation compound composition for exfoliated graphite, flexible graphite, and nano-scaled graphene platelets

DOEpatents

Zhamu, Aruna; Jang, Bor Z.

2014-06-17

A carboxylic-intercalated graphite compound composition for the production of exfoliated graphite, flexible graphite, or nano-scaled graphene platelets. The composition comprises a layered graphite with interlayer spaces or interstices and a carboxylic acid residing in at least one of the interstices, wherein the composition is prepared by a chemical oxidation reaction which uses a combination of a carboxylic acid and hydrogen peroxide as an intercalate source. Alternatively, the composition may be prepared by an electrochemical reaction, which uses a carboxylic acid as both an electrolyte and an intercalate source. Exfoliation of the invented composition does not release undesirable chemical contaminants into air or drainage.

Mineral resource of the month: graphite

USGS Publications Warehouse

,

2008-01-01

The article presents facts about graphite ideal for industrial applications. Among the characteristics of graphite are its metallic luster, softness, perfect basal cleavage and electrical conductivity. Batteries, brake linings and powdered metals are some of the products that make use of graphite. It attributes the potential applications for graphite in high-technology fields to innovations in thermal technology and acid-leaching techniques.

Nucleation and Growth of Graphite in Eutectic Spheroidal Cast Iron: Modeling and Testing

NASA Astrophysics Data System (ADS)

Carazo, Fernando D.; Dardati, Patricia M.; Celentano, Diego J.; Godoy, Luis A.

2016-06-01

A new model of graphite growth during the continuous cooling of eutectic spheroidal cast iron is presented in this paper. The model considers the nucleation and growth of graphite from pouring to room temperature. The microstructural model of solidification accounts for the eutectic as divorced and graphite growth rate as a function of carbon gradient at the liquid in contact with the graphite. In the solid state, the microstructural model takes into account three stages for graphite growth, namely (1) from the end of solidification to the upper bound of intercritical stable eutectoid, (2) during the intercritical stable eutectoid, and (3) from the lower bound of intercritical stable eutectoid to room temperature. The micro- and macrostructural models are coupled using a sequential multiscale approach. Numerical results for graphite fraction and size distribution are compared with experimental results obtained from a cylindrical cup, in which the graphite volumetric fraction and size distribution were obtained using the Schwartz-Saltykov approach. The agreements between the experimental and numerical results for the fraction of graphite and the size distribution of spheroids reveal the importance of numerical models in the prediction of the main aspects of graphite in spheroidal cast iron.

Graphitized-carbon fiber/carbon char fuel

DOEpatents

Cooper, John F [Oakland, CA

2007-08-28

A method for recovery of intact graphitic fibers from fiber/polymer composites is described. The method comprises first pyrolyzing the graphite fiber/polymer composite mixture and then separating the graphite fibers by molten salt electrochemical oxidation.

Seal assembly with anti-rotation pin for high pressure supercritical fluids

DOEpatents

Wright, Steven A.; Fuller, Robert L.

2014-08-05

A seal assembly for sealing a machine with a first chamber and a second chamber is provided. A rotating shaft extends through the first and second chambers, and rotates therein. The seal assembly has a seal housing, a seal ring and a seal pin. The seal housing is positionable in the machine housing. The seal housing has a seal pocket extending into a fluid side thereof, and a housing receptacle extending into an inner diameter thereof at the seal pocket. The seal ring is positionable in the seal pocket of the seal housing for forming a seal therewith. The seal ring has a ring receptacle extending into an outer diameter thereof. The ring receptacle is positionable adjacent to the housing receptacle for defining a pin hole therebetween. The seal pin is loosely positionable in the pin hole whereby movement about the seal ring is accommodated while preventing rotation thereof.

Design guide for helicopter transmission seals

NASA Technical Reports Server (NTRS)

Hayden, T. S.; Keller, C. H., Jr.

1974-01-01

A detailed approach for the selection and design of seals for helicopter transmissions is presented. There are two major types of seals presently being used and they are lip type seals and mechanical type seals. Lip type seals can be divided in conventional lip seals and hydrodynamic lip seals. Conventional lip seals can be used for slow-speed, low-pressure, low-temperature sealing. Hydrodynamic lip seals although they are as pressure and temperature limited as conventional lip seals, can operate at a higher speed. Mechanical types seals are comprised of face seals and circumferential seals. Face seals are capable of high speed, high pressure, and high temperature. Circumferential seals can be used in high-speed and high-temperature applications, but will leak excessively at moderate pressures. The performance goals of transmission seals are a life that is at least equal to the scheduled overhaul interval of the gearbox component and a leakage rate of near zero.

Thermodynamic Simulation of Equilibrium Composition of Reaction Products at Dehydration of a Technological Channel in a Uranium-Graphite Reactor

NASA Astrophysics Data System (ADS)

Pavliuk, A. O.; Zagumennov, V. S.; Kotlyarevskiy, S. G.; Bespala, E. V.

2018-01-01

The problems of accumulation of nuclear fuel spills in the graphite stack in the course of operation of uranium-graphite nuclear reactors are considered. The results of thermodynamic analysis of the processes in the graphite stack at dehydration of a technological channel, fuel element shell unsealing and migration of fission products, and activation of stable nuclides in structural elements of the reactor and actinides inside the graphite moderator are given. The main chemical reactions and compounds that are produced in these modes in the reactor channel during its operation and that may be hazardous after its shutdown and decommissioning are presented. Thermodynamic simulation of the equilibrium composition is performed using the specialized code TERRA. The results of thermodynamic simulation of the equilibrium composition in different cases of technological channel dehydration in the course of the reactor operation show that, if the temperature inside the active core of the nuclear reactor increases to the melting temperature of the fuel element, oxides and carbides of nuclear fuel are produced. The mathematical model of the nonstationary heat transfer in a graphite stack of a uranium-graphite reactor in the case of the technological channel dehydration is presented. The results of calculated temperature evolution at the center of the fuel element, the replaceable graphite element, the air gap, and in the surface layer of the block graphite are given. The numerical results show that, in the case of dehydration of the technological channel in the uranium-graphite reactor with metallic uranium, the main reaction product is uranium dioxide UO2 in the condensed phase. Low probability of production of pyrophoric uranium compounds (UH3) in the graphite stack is proven, which allows one to disassemble the graphite stack without the risk of spontaneous graphite ignition in the course of decommissioning of the uranium-graphite nuclear reactor.

Electrochemical treatment of evaporated residue of soak liquor generated from leather industry.

PubMed

Boopathy, R; Sekaran, G

2013-09-15

The organic and suspended solids present in soak liquor, generated from leather industry, demands treatment. The soak liquor is being segregated and evaporated in solar evaporation pans/multiple effect evaporator due to non availability of viable technology for its treatment. The residue left behind in the pans/evaporator does not carry any reuse value and also faces disposal threat due to the presence of high concentration of sodium chloride, organic and bacterial impurities. In the present investigation, the aqueous evaporated residue of soak liquor (ERSL) was treated by electrochemical oxidation. Graphite/graphite and SS304/graphite systems were used in electrochemical oxidation of organics in ERSL. Among these, graphite/graphite system was found to be effective over SS304/graphite system. Hence, the optimised conditions for the electrochemical oxidation of organics in ERSL using graphite/graphite system was evaluated by response surface methodology (RSM). The mass transport coefficient (km) was calculated based on pseudo-first order rate kinetics for both the electrode systems (graphite/graphite and SS304/graphite). The thermodynamic properties illustrated the electrochemical oxidation was exothermic and non-spontaneous in nature. The calculated specific energy consumption at the optimum current density of 50 mA cm(-2) was 0.41 kWh m(-3) for the removal of COD and 2.57 kWh m(-3) for the removal of TKN. Copyright © 2013 Elsevier B.V. All rights reserved.

AGC-2 Graphite Pre-irradiation Data Package

DOE Office of Scientific and Technical Information (OSTI.GOV)

David Swank; Joseph Lord; David Rohrbaugh

2010-08-01

The NGNP Graphite R&D program is currently establishing the safe operating envelope of graphite core components for a Very High Temperature Reactor (VHTR) design. The program is generating quantitative data necessary for predicting the behavior and operating performance of the new nuclear graphite grades. To determine the in-service behavior of the graphite for pebble bed and prismatic designs, the Advanced Graphite Creep (AGC) experiment is underway. This experiment is examining the properties and behavior of nuclear grade graphite over a large spectrum of temperatures, neutron fluences and compressive loads. Each experiment consists of over 400 graphite specimens that are characterizedmore » prior to irradiation and following irradiation. Six experiments are planned with the first, AGC-1, currently being irradiated in the Advanced Test Reactor (ATR) and pre-irradiation characterization of the second, AGC-2, completed. This data package establishes the readiness of 512 specimens for assembly into the AGC-2 capsule.« less

Preparation and Characterization of Graphite Waste/CeO2 Composites

NASA Astrophysics Data System (ADS)

Kusrini, E.; Utami, C. S.; Nasruddin; Prasetyanto, E. A.; Bawono, Aji A.

2018-03-01

In this research, the chemical modification of graphite waste with CeO2 was developed and characterized. Graphite waste was pretreated with mechanical to obtain the size 200 mesh (75 μm), and thermal methods at 110°C oven for 6 hours. Here, we demonstrate final properties of graphite before modification (GBM), activated graphite (GA) and graphite/CeO2 composite with variation of 0.5, 1 and 2 g of CeO2 (G0.5; G1; G2). The effect of CeO2 concentration was observed. The presence of cerium in modified graphite samples (G0.5; G1; G2) were analyzed using SEM-EDX. The results show that the best surface area was found in G2 is 26.82 m2/g. The presence of CeO2 onto graphite surface does not significantly increase the surface area of composites.

Monolithic porous graphitic carbons obtained through catalytic graphitization of carbon xerogels

NASA Astrophysics Data System (ADS)

Kiciński, Wojciech; Norek, Małgorzata; Bystrzejewski, Michał

2013-01-01

Pyrolysis of organic xerogels accompanied by catalytic graphitization and followed by selective-combustion purification was used to produce porous graphitic carbons. Organic gels impregnated with iron(III) chloride or nickel(II) acetate were obtained through polymerization of resorcinol and furfural. During the pyrolysis stage graphitization of the gel matrix occurs, which in turn develops mesoporosity of the obtained carbons. The evolution of the carbon into graphitic structures is strongly dependent on the concentrations of the transition metal. Pyrolysis leads to monoliths of carbon xerogel characterized by substantially enhanced mesoporosity resulting in specific surface areas up to 400 m2/g. Removal of the amorphous carbon by selective-combustion purification reduces the xerogels' mesoporosity, occasionally causing loss of their mechanical strength. The graphitized carbon xerogels were investigated by means of SEM, XRD, Raman scattering, TG-DTA and N2 physisorption. Through this procedure well graphitized carbonaceous materials can be obtained as bulk pieces.

Friction and wear of carbon-graphite materials for high energy brakes

NASA Technical Reports Server (NTRS)

Bill, R. C.

1975-01-01

Caliper-type brakes simulation experiments were conducted on seven different carbon-graphite material formulations against a steel disk material and against a carbon-graphite disk material. The effects of binder level, boron carbide (B4C) additions, graphite fiber additions, and graphite cloth reinforcement on friction and wear behavior were investigated. Reductions in binder level and additions of B4C each resulted in increased wear. The wear rate was not affected by the addition of graphite fibers. Transition to severe wear and high friction was observed in the case of graphite-cloth-reinforced carbon sliding against a disk of similar composition. This transition was related to the disruption of a continuous graphite shear film that must form on the sliding surfaces if low wear is to occur. The exposure of the fiber structure of the cloth constituent is believed to play a role in the shear film disruption.

Porous carbon-coated graphite electrodes for energy production from salinity gradient using reverse electrodialysis

NASA Astrophysics Data System (ADS)

Lee, Su-Yoon; Jeong, Ye-Jin; Chae, So-Ryong; Yeon, Kyeong-Ho; Lee, Yunkyu; Kim, Chan-Soo; Jeong, Nam-Jo; Park, Jin-Soo

2016-04-01

Performance of graphite foil electrodes coated by porous carbon black (i.e., Vulcan) was investigated in comparison with metal electrodes for reverse electrodialysis (RED) application. The electrode slurry that was used for fabrication of the porous carbon-coated graphite foil is composed of 7.2 wt% of carbon black (Vulcan X-72), 0.8 wt% of a polymer binder (polyvinylidene fluoride, PVdF), and 92.0 wt% of a mixing solvent (dimethylacetamide, DMAc). Cyclic voltammograms of both the porous carbon (i.e., Vulcan)-coated graphite foil electrode and the graphite foil electrode without Vulcan showed good reversibility in the hexacyanoferrate(III) (i.e., Fe(CN)63-) and hexacyanoferrate(II) (i.e., Fe(CN)64-) redox couple and 1 M Na2SO4 at room temperature. However, anodic and cathodic current of the Vulcan-coated graphite foil electrode was much higher than those of the graphite foil electrode. Using a bench-scale RED stack, the current-voltage polarization curve of the Vulcan-coated graphite electrode was compared to that of metal electrodes such as iridium (Ir) and platinum (Pt). From the results, it was confirmed that resistance of four different electrodes increased with the following order: the Vulcan-coated graphite foil

Comparison between the Strength Levels of Baseline Nuclear-Grade Graphite and Graphite Irradiated in AGC-2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carroll, Mark Christopher

2015-07-01

This report details the initial comparison of mechanical strength properties between the cylindrical nuclear-grade graphite specimens irradiated in the second Advanced Graphite Creep (AGC-2) experiment with the established baseline, or unirradiated, mechanical properties compiled in the Baseline Graphite Characterization program. The overall comparative analysis will describe the development of an appropriate test protocol for irradiated specimens, the execution of the mechanical tests on the AGC-2 sample population, and will further discuss the data in terms of developing an accurate irradiated property distribution in the limited amount of irradiated data by leveraging the considerably larger property datasets being captured in themore » Baseline Graphite Characterization program. Integrating information on the inherent variability in nuclear-grade graphite with more complete datasets is one of the goals of the VHTR Graphite Materials program. Between “sister” specimens, or specimens with the same geometry machined from the same sub-block of graphite from which the irradiated AGC specimens were extracted, and the Baseline datasets, a comprehensive body of data will exist that can provide both a direct and indirect indication of the full irradiated property distributions that can be expected of irradiated nuclear-grade graphite while in service in a VHTR system. While the most critical data will remain the actual irradiated property measurements, expansion of this data into accurate distributions based on the inherent variability in graphite properties will be a crucial step in qualifying graphite for nuclear use as a structural material in a VHTR environment.« less

Surface conforming thermal/pressure seal. [tail assemblies of space shuttle orbiters

NASA Technical Reports Server (NTRS)

Stevens, M. L. (Inventor)

1981-01-01

An assembly is disclosed for sealing a variable gap between the surface of element and a second element in movable relation to it. A seal housing is attached to the second element for movement therewith and has a sealing surface. At least one elongated seal member carried by the housing has first and second conjugate sealing surfaces. The first sealing surface is for rubbing and sealing engagement with the first element surface and the second sealing surface is for sliding and sealing engagement with the housing sealing surface. A biasing assembly may be carried by the housing for biasing the first and second conjugate sealing surfaces of the sealing member toward sealing engagement with the first element surface and housing sealing surface, respectively.

Influence of graphite-alloy interactions on corrosion of Ni-Mo-Cr alloy in molten fluorides

NASA Astrophysics Data System (ADS)

Ai, Hua; Hou, Juan; Ye, Xiang-Xi; Zeng, Chao Liu; Sun, Hua; Li, Xiaoyun; Yu, Guojun; Zhou, Xingtai; Wang, Jian-Qiang

2018-05-01

In this study, the effects of graphite-alloy interaction on corrosion of Ni-Mo-Cr alloy in molten FLiNaK salt were investigated. The corrosion tests of Ni-Mo-Cr alloys were conducted in graphite crucibles, to examine the differences of test specimens in conditions of electric contact and isolated with graphite, respectively. The corrosion attack is severer with more weight loss and deeper Cr depletion layer in samples electric contact with graphite than those isolated with graphite. The occurrence of galvanic corrosion between alloy specimens and graphite container was confirmed by electrochemical measurement. The corrosion is controlled by nonelectric transfer in isolated test while electrochemical reaction accelerated corrosion in electric contact test.

The origin of epigenetic graphite: evidence from isotopes

USGS Publications Warehouse

Weis, P.L.; Friedman, I.; Gleason, J.P.

1981-01-01

Stable carbon isotope ratios measured in syngenetic graphite, epigenetic graphite, and graphitic marble suggests that syngenetic graphite forms only by the metamorphism of carbonaceous detritus. Metamorphism of calcareous rocks with carbonaceous detritus is accompanied by an exchange of carbon between the two, which may result in large changes in isotopic composition of the non-carbonate phase but does not affect the relative proportions of the two reactants in the rock. Epigenetic graphite forms only from carbonaceous material or preexisting graphite. The reactions involved are the water gas reaction (C + H2O ??? CO + H2) at 800-900??C, and the Boudouard reaction (2CO ??? C + CO2), which probably takes place at temperatures about 50-100??C lower. ?? 1982.

Method of producing exfoliated graphite, flexible graphite, and nano-scaled graphene platelets

DOEpatents

Zhamu, Aruna; Shi, Jinjun; Guo, Jiusheng; Jang, Bor Z.

2010-11-02

The present invention provides a method of exfoliating a layered material (e.g., graphite and graphite oxide) to produce nano-scaled platelets having a thickness smaller than 100 nm, typically smaller than 10 nm. The method comprises (a) dispersing particles of graphite, graphite oxide, or a non-graphite laminar compound in a liquid medium containing therein a surfactant or dispersing agent to obtain a stable suspension or slurry; and (b) exposing the suspension or slurry to ultrasonic waves at an energy level for a sufficient length of time to produce separated nano-scaled platelets. The nano-scaled platelets are candidate reinforcement fillers for polymer nanocomposites. Nano-scaled graphene platelets are much lower-cost alternatives to carbon nano-tubes or carbon nano-fibers.

METHOD FOR COATING GRAPHITE WITH METALLIC CARBIDES

DOEpatents

Steinberg, M.A.

1960-03-22

A method for producing refractory coatings of metallic carbides on graphite was developed. In particular, the graphite piece to be coated is immersed in a molten solution of 4 to 5% by weight of zirconium, titanium, or niobium dissolved in tin. The solution is heated in an argon atmosphere to above 1400 deg C, whereby the refractory metal reacts with the surface of the graphite to form a layer of metalic carbide. The molten solution is cooled to 300 to 400 deg C, and the graphite piece is removed. Excess tin is wiped from the graphite, which is then heated in vacuum to above 2300 deg C. The tin vaporizes from the graphite surface, leaving the surface coated with a tenacious layer of refractory metallic carbide.

Recent Advances in Preparation, Structure, Properties and Applications of Graphite Oxide.

PubMed

Srivastava, Suneel Kumar; Pionteck, Jürgen

2015-03-01

Graphite oxide, also referred as graphitic oxide or graphitic acid, is an oxidized bulk product of graphite with a variable composition. However, it did not receive immense attention until it was identified as an important and easily obtainable precursor for the preparation of graphene. This inspired many researchers to explore facts related to graphite oxide in exploiting its fascinating features. The present article culminates up-dated review on different preparative methods, morphology and characterization of physical/chemical properties of graphite oxide by XRD, XPS, FTIR, Raman, NMR, UV-visible, and DRIFT analyses. Finally, recent developments on intercalation and applications of GO in multifaceted areas of catalysis, sensor, supercapacitors, water purification, hydrogen storage and magnetic shielding etc. has also been reviewed.

CMB-13 research on carbon and graphite

NASA Technical Reports Server (NTRS)

Smith, M. C.

1972-01-01

The research on graphite and carbon for this period is reported. Topics discussed include: effects of grinding on the Santa Marie graphites, properties and purities of coal-tar, resin-bonded graphite, carbonization of resin components, and glass-like carbon filler.

Tribological Analysis of Copper-Coated Graphite Particle-Reinforced A359 Al/5 wt.% SiC Composites

NASA Astrophysics Data System (ADS)

Lin, C. B.; Wang, T. C.; Chang, Z. C.; Chu, H. Y.

2013-01-01

Copper-coated graphite particles can be mass-produced by the cementation process using simple equipment. Graphite particulates that were coated with electroless copper and 5 wt.% SiC particulates were introduced into an aluminum alloy by compocasting to make A359 Al/5 wt.% SiC(p) composite that contained 2, 4, 6, and 8 wt.% graphite particulate composite. The effects of SiC particles, quantity of graphite particles, normal loading, sliding speed and wear debris on the coefficient of friction, and the wear rate were investigated. The results thus obtained indicate that the wear properties were improved by adding small amounts of SiC and graphite particles into the A359 Al alloy. The coefficient of friction of the A359 Al/5 wt.% SiC(p) composite that contained 6.0 wt.% graphite particulates was reduced to 0.246 and the amount of graphite film that was released on the worn surface increased with the graphite particulate content. The coefficient of friction and the wear rate were insensitive to the variation in the sliding speed and normal loading.

Preparation and characterization of copper-graphite composites by electrical explosion of wire in liquid.

PubMed

Bien, T N; Gul, W H; Bac, L H; Kim, J C

2014-11-01

Copper-graphite nanocomposites containing 5 vol.% graphite were prepared by a powder metallurgy route using an electrical wire explosion (EEW) in liquid method and spark plasma sintering (SPS) process. Graphite rods with a 0.3 mm diameter and copper wire with a 0.2 mm diameter were used as raw materials for EEWin liquid. To compare, a pure copper and copper-graphite mixture was also prepared. The fabricated graphite was in the form of a nanosheet, onto which copper particles were coated. Sintering was performed at 900 degrees C at a heating rate of 30 degrees C/min for 10 min and under a pressure of 70 MPa. The density of the sintered composite samples was measured by the Archimedes method. A wear test was performed by a ball-on-disc tribometer under dry conditions at room temperature in air. The presence of graphite effectively reduced the wear of composites. The copper-graphite nanocomposites prepared by EEW had lower wear rates than pure copper material and simple mixed copper-graphite.

Understanding the crack formation of graphite particles in cycled commercial lithium-ion batteries by focused ion beam - scanning electron microscopy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lin, Na; Jia, Zhe; Wang, Zhihui

Here in this paper, the structure degradation of commercial Lithium-ion battery (LIB) graphite anodes with different cycling numbers and charge rates was investigated by focused ion beam (FIB) and scanning electron microscopy (SEM). The cross-section image of graphite anode by FIB milling shows that cracks, resulted in the volume expansion of graphite electrode during long-term cycling, were formed in parallel with the current collector. The crack occurs in the bulk of graphite particles near the lithium insertion surface, which might derive from the stress induced during lithiation and de-lithiation cycles. Subsequently, crack takes place along grain boundaries of the polycrystallinemore » graphite, but only in the direction parallel with the current collector. Furthermore, fast charge graphite electrodes are more prone to form cracks since the tensile strength of graphite is more likely to be surpassed at higher charge rates. Therefore, for LIBs long-term or high charge rate applications, the tensile strength of graphite anode should be taken into account.« less

Understanding the crack formation of graphite particles in cycled commercial lithium-ion batteries by focused ion beam - scanning electron microscopy

DOE PAGES

Lin, Na; Jia, Zhe; Wang, Zhihui; ...

2017-10-01

Here in this paper, the structure degradation of commercial Lithium-ion battery (LIB) graphite anodes with different cycling numbers and charge rates was investigated by focused ion beam (FIB) and scanning electron microscopy (SEM). The cross-section image of graphite anode by FIB milling shows that cracks, resulted in the volume expansion of graphite electrode during long-term cycling, were formed in parallel with the current collector. The crack occurs in the bulk of graphite particles near the lithium insertion surface, which might derive from the stress induced during lithiation and de-lithiation cycles. Subsequently, crack takes place along grain boundaries of the polycrystallinemore » graphite, but only in the direction parallel with the current collector. Furthermore, fast charge graphite electrodes are more prone to form cracks since the tensile strength of graphite is more likely to be surpassed at higher charge rates. Therefore, for LIBs long-term or high charge rate applications, the tensile strength of graphite anode should be taken into account.« less

Study of evaporating the irradiated graphite in equilibrium low-temperature plasma

NASA Astrophysics Data System (ADS)

Bespala, E. V.; Novoselov, I. Yu.; Pavlyuk, A. O.; Kotlyarevskiy, S. G.

2018-01-01

The paper describes a problem of accumulation of irradiated graphite due to operation of uranium-graphite nuclear reactors. The main noncarbon contaminants that contribute to the overall activity of graphite elements are iso-topes 137Cs, 60Co, 90Sr, 36Cl, and 3H. A method was developed for processing of irradiated graphite ensuring the volu-metric decontamination of samples. The calculation results are presented for equilibrium composition of plasma-chemical reactions in systems "irradiated graphite-argon" and "irradiated graphite-helium" for a wide range of tem-peratures. The paper describes a developed mathematical model for the process of purification of a porous graphite surface treated by equilibrium low-temperature plasma. The simulation results are presented for the rate of sublimation of radioactive contaminants as a function of plasma temperature and plasma flow velocity when different plasma-forming gases are used. The extraction coefficient for the contaminant 137Cs from the outer side of graphite pores was calculated. The calculations demonstrated the advantages of using a lighter plasma forming gas, i.e., helium.

Hybridized polymer matrix composites

NASA Technical Reports Server (NTRS)

House, E. E.; Hoggatt, J. T.; Symonds, W. A.

1980-01-01

The extent to which graphite fibers are released from resin matrix composites that are exposed to fire and impact conditions was determined. Laboratory simulations of those conditions that could exist in the event of an aircraft crash and burn situation were evaluated. The effectiveness of various hybridizing concepts in preventing this release of graphite fibers were also evaluated. The baseline (i.e., unhybridized) laminates examined were prepared from commercially available graphite/epoxy, graphite/polyimide, and graphite/phenolic materials. Hybridizing concepts investigated included resin fillers, laminate coatings, resin blending, and mechanical interlocking of the graphite reinforcement. The baseline and hybridized laminates' mechanical properties, before and after isothermal and humidity aging, were also compared. It was found that a small amount of graphite fiber was released from the graphite/epoxy laminates during the burn and impact conditions used in this program. However, the extent to which the fibers were released is not considered a severe enough problem to preclude the use of graphite reinforced composites in civil aircraft structure. It also was found that several hybrid concepts eliminated this fiber release. Isothermal and humidity aging did not appear to alter the fiber release tendencies.

Fuel cell manifold sealing system

DOEpatents

Grevstad, Paul E.; Johnson, Carl K.; Mientek, Anthony P.

1980-01-01

A manifold-to-stack seal and sealing method for fuel cell stacks. This seal system solves the problem of maintaining a low leak rate manifold seal as the fuel cell stack undergoes compressive creep. The seal system eliminates the problem of the manifold-to-stack seal sliding against the rough stack surface as the stack becomes shorter because of cell creep, which relative motion destroys the seal. The seal system described herein utilizes a polymer seal frame firmly clamped between the manifold and the stack such that the seal frame moves with the stack. Thus, as the stack creeps, the seal frame creeps with it, and there is no sliding at the rough, tough to seal, stack-to-seal frame interface. Here the sliding is on a smooth easy to seal location between the seal frame and the manifold.

Method for producing a fuel cell manifold seal

DOEpatents

Grevstad, Paul E.; Johnson, Carl K.; Mientek, Anthony P.

1982-01-01

A manifold-to-stack seal and sealing method for fuel cell stacks. This seal system solves the problem of maintaining a low leak rate manifold seal as the fuel cell stack undergoes compressive creep. The seal system eliminates the problem of the manifold-to-stack seal sliding against the rough stack surface as the stack becomes shorter because of cell creep, which relative motion destroys the seal. The seal system described herein utilizes a polymer seal frame firmly clamped between the manifold and the stack such that the seal frame moves with the stack. Thus, as the stack creeps, the seal frame creeps with it, and there is no sliding at the rough, tough to seal, stack-to-seal frame interface. Here the sliding is on a smooth easy to seal location between the seal frame and the manifold.

Chemical Characterization and Removal of C-14 from Irradiated Graphite-12010

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cleaver, James; McCrory, Shilo; Smith, Tara E.

2012-07-01

Quantities of irradiated graphite waste are expected to drastically increase, which indicates the need for a graphite waste management strategy. Of greatest concern for long-term disposal of irradiated graphite is carbon-14 (C-14), with a half-life of 5730 years. Study of irradiated graphite from nuclear reactors indicates C-14 is concentrated on the outer 5 mm of the graphite structure. The aim of the research described here is to identify the chemical form of C-14 in irradiated graphite and develop a practical method by which C-14 can be removed. Characterization of pre- and post-irradiation graphite was conducted to determine bond type, functionalmore » groups, location and concentration of C-14 and its precursors via the use of surface sensitive characterization techniques. Because most surface C-14 originates from neutron activation of nitrogen, an understanding of nitrogen bonding to graphite may lead to a greater understanding of the formation pathway of C-14. However, no single technique provides a complete picture. Therefore, a portfolio of techniques has been developed, with each technique providing another piece to the puzzle that is the chemical nature of the C-14. Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), and Raman Spectroscopy were used to evaluate the morphological features of graphite samples. The concentration, chemical composition, and bonding characteristics of C-14 and its precursors were determined through X-ray Photoelectron Spectroscopy (XPS), Time-of-Flight Secondary Ion Mass Spectrometry (SIMS), and Auger and Energy Dispersive X-ray Analysis Spectroscopy (EDX). High-surface-area graphite foam, POCOFoam{sup R}, was exposed to liquid nitrogen and irradiated. Characterization of this material has shown C-14 to C-12 ratios of 0.035. This information was used to optimize the thermal treatment of graphite. Thermal treatment of irradiated graphite as reported by Fachinger et al. (2007) uses naturally adsorbed oxygen complexes to gasify graphite, thus its effectiveness is highly dependent on the availability of adsorbed oxygen compounds. In research presented, the quantity and form of adsorbed oxygen complexes in pre- and post irradiated graphite was studied using SIMS and XPS. SIMS and XPS detected adsorbed oxygen compounds on both irradiated and unirradiated graphite. During thermal treatment graphite samples are heated in the presence of inert argon gas, which carries off gaseous products released during treatment. Experiments were performed at 900 deg. C and 1400 deg. C to evaluate the selective removal of C-14. (authors)« less

High speed hydrogen/graphite interaction

NASA Technical Reports Server (NTRS)

Kelly, A. J.; Hamman, R.; Sharma, O. P.; Harrje, D. T.

1974-01-01

Various aspects of a research program on high speed hydrogen/graphite interaction are presented. Major areas discussed are: (1) theoretical predictions of hydrogen/graphite erosion rates; (2) high temperature, nonequilibrium hydrogen flow in a nozzle; and (3) molecular beam studies of hydrogen/graphite erosion.

RECOVERY OF VALUABLE MATERIAL FROM GRAPHITE BODIES

DOEpatents

Fromm, L.W. Jr.

1959-09-01

An electrolytic process for recovering uranium from a graphite fuel element is described. The uraniumcontaining graphite body is disposed as the anode of a cell containing a nitric acid electrolyte and a 5 amp/cm/sup 2/ current passed to induce a progressive disintegration of the graphite body. The dissolved uranium is quickly and easily separated from the resulting graphite particles by simple mechanical means, such as centrifugation, filtration, and decontamination.

Interface Character of Aluminum-Graphite Metal Matrix Composites.

DTIC Science & Technology

1983-01-27

studied included the commer- cial A/graphite composites; layered model systems on single crystal and poly- crystalline graphite substrates as well as...composition and thickness of the composite interface, and graphite crystal orientation. 3 For the model systems in this study , single crystal graphite...been reviewed by Kingcry. Segregation at surfaces in single- crystal MgO of Fe, Cr and Sc, which were Dresent in concentrations within the single- 3phase

Structure and Performance of Epoxy Resin Cladded Graphite Used as Anode

NASA Astrophysics Data System (ADS)

Zhou, Zhentao; Li, Haijun

This paper is concerning to prepare modified natural graphite which is low-cost and advanced materials used as lithium ion battery anode using the way of cladding natural graphite with epoxy resin. The results shows that the specific capacity and circular performance of the modified natural graphite, which is prepared in the range of 600°C and 1000°C, have been apparently improved compare with the not-modified natural graphite. The first reversible capacity of the modified natural graphite is 338mAh/g and maintain more than 330mAh/g after 20 charge/discharge circles.

Artificially-built solid electrolyte interphase via surface-bonded vinylene carbonate derivative on graphite by molecular layer deposition

NASA Astrophysics Data System (ADS)

Chae, Seulki; Lee, Jeong Beom; Lee, Jae Gil; Lee, Tae-jin; Soon, Jiyong; Ryu, Ji Heon; Lee, Jin Seok; Oh, Seung M.

2017-12-01

Vinylene carbonate (VC) is attached in a ring-opened form on a graphite surface by molecular layer deposition (MLD) method, and its role as a solid electrolyte interphase (SEI) former is studied. When VC is added into the electrolyte solution of a graphite/LiNi0.5Mn1.5O4 (LNMO) full-cell, it is reductively decomposed to form an effective SEI on the graphite electrode. However, VC in the electrolyte solution has serious adverse effects due to its poor stability against electrochemical oxidation on the LNMO positive electrode. A excessive acid generation as a result of VC oxidation is observed, causing metal dissolution from the LNMO electrode. The dissolved metal ions are plated on the graphite electrode to destroy the SEI layer, eventually causing serious capacity fading and poor Coulombic efficiency. The VC derivative on the graphite surface also forms an effective SEI layer on the graphite negative electrode via reductive decomposition. The detrimental effects on the LNMO positive electrode, however, can be avoided because the bonded VC derivative on the graphite surface cannot move to the LNMO electrode. Consequently, the graphite/LNMO full-cell fabricated with the VC-attached graphite outperforms the cells without VC or with VC in the electrolyte, in terms of Coulombic efficiency and capacity retention.

Micro-fabrication method of graphite mesa microdevices based on optical lithography technology

NASA Astrophysics Data System (ADS)

Zhang, Cheng; Wen, Donghui; Zhu, Huamin; Zhang, Xiaorui; Yang, Xing; Shi, Yunsheng; Zheng, Tianxiang

2017-12-01

Graphite mesa microdevices have incommensurate contact nanometer interfaces, superlubricity, high-speed self-retraction, and other characteristics, which have potential applications in high-performance oscillators and micro-scale switches, memory devices, and gyroscopes. However, the current method of fabricating graphite mesa microdevices is mainly based on high-cost, low efficiency electron beam lithography technology. In this paper, the processing technologies of graphite mesa microdevices with various shapes and sizes were investigated by a low-cost micro-fabrication method, which was mainly based on optical lithography technology. The characterization results showed that the optical lithography technology could realize a large-area of patterning on the graphite surface, and the graphite mesa microdevices, which have a regular shape, neat arrangement, and high verticality could be fabricated in large batches through optical lithography technology. The experiments and analyses showed that the graphite mesa microdevices fabricated through optical lithography technology basically have the same self-retracting characteristics as those fabricated through electron beam lithography technology, and the maximum size of the graphite mesa microdevices with self-retracting phenomenon can reach 10 µm  ×  10 µm. Therefore, the proposed method of this paper can realize the high-efficiency and low-cost processing of graphite mesa microdevices, which is significant for batch fabrication and application of graphite mesa microdevices.

A magnetic fluid seal for rotary blood pumps: effects of seal structure on long-term performance in liquid.

PubMed

Mitamura, Yoshinori; Takahashi, Sayaka; Amari, Shuichi; Okamoto, Eiji; Murabayashi, Shun; Nishimura, Ikuya

2011-03-01

A magnetic fluid (MF) seal enables mechanical contact-free rotation of the shaft and hence has excellent durability. The performance of an MF seal, however, has been reported to decrease in liquids. We developed an MF seal that has a "shield" mechanism, and a new MF with a higher magnetization of 47.9 kA/m. The sealing performance of the MF seal installed in a rotary blood pump was studied. Three types of MF seals were used. Seal A was a conventional seal without a shield. Seal B had the same structure as that of Seal A, but the seal was installed at 1 mm below liquid level. Seal C was a seal with a shield and the MF was set at 1 mm below liquid level. Seal A failed after 6 and 11 days. Seal B showed better results (20 and 73 days). Seal C showed long-term durability (217 and 275 days). The reason for different results in different seal structures was considered to be different flow conditions near the magnetic fluid. Fluid dynamics near the MF in the pump were analyzed using computational fluid dynamics (CFD) software. We have developed an MF seal with a shield that works in liquid for >275 days. The MF seal is promising as a shaft seal for rotary blood pumps.

Comet Impacts as a Source of Methane on Titan

NASA Astrophysics Data System (ADS)

Howard, Michael; Goldman, N.; Vitello, P. A.

2006-12-01

We model comet impacts on Titan as a possible source of atmospheric methane. That is, we study the formation of methane in comet impacts using chemical equilibrium calculations coupled with arbitrary Lagrange-Eulerian (ALE) hydrodynamics. That is, we study the chemical transformation of comet material under high pressure and temperature conditions as it impacts Titan. We assume that the comet is composed of ice, graphite, nitrogen and some hydrocarbons. For certain pressure and temperature regimes, in chemical equilibrium, a significant amount of ice and graphite can be transformed into methane. As a result, we find that a significant amount of methane can be formed in comet collisions on Titan. The methane is formed in the post-impact vapor clouds that form as the comet material expands and cools. We use molecular dynamics to construct an equation of state for the ice surface structures and the comet material. We also study kinetic processes for methane formation during the expansion and cooling phase. We discuss the implication of our results for comets as a possible source of abiotic methane on Titan and its implications on the origin of life. We also discuss the various uncertainties in our model. * This work was performed under the auspices of the U.S. Department of Energy by University of California, Lawrence Livermore National Laboratory under Contract W-7405-Eng-48.

Thermal protection system (TPS) monitoring using acoustic emission

NASA Astrophysics Data System (ADS)

Hurley, D. A.; Huston, D. R.; Fletcher, D. G.; Owens, W. P.

2011-04-01

This project investigates acoustic emission (AE) as a tool for monitoring the degradation of thermal protection systems (TPS). The AE sensors are part of an array of instrumentation on an inductively coupled plasma (ICP) torch designed for testing advanced thermal protection aerospace materials used for hypervelocity vehicles. AE are generated by stresses within the material, propagate as elastic stress waves, and can be detected with sensitive instrumentation. Graphite (POCO DFP-2) is used to study gas-surface interaction during degradation of thermal protection materials. The plasma is produced by a RF magnetic field driven by a 30kW power supply at 3.5 MHz, which creates a noisy environment with large spikes when powered on or off. AE are waveguided from source to sensor by a liquid-cooled copper probe used to position the graphite sample in the plasma stream. Preliminary testing was used to set filters and thresholds on the AE detection system (Physical Acoustics PCI-2) to minimize the impact of considerable operating noise. Testing results show good correlation between AE data and testing environment, which dictates the physics and chemistry of the thermal breakdown of the sample. Current efforts for the project are expanding the dataset and developing statistical analysis tools. This study shows the potential of AE as a powerful tool for analysis of thermal protection material thermal degradations with the unique capability of real-time, in-situ monitoring.

Graphite tail powder and liquid biofertilizer as trace elements source for ground nut

NASA Astrophysics Data System (ADS)

Hindersah, Reginawanti; Setiawati, M. Rochimi; Fitriatin, B. Natalie; Suryatama, Pujawati; Asmiran, Priyanka; Panatarani, Camellia; Joni, I. Made

2018-02-01

Utilization of graphite tail waste from the mineral beneficiation processing is very important since it contain significant amount of essential minerals which are necessary for plant growth. These mineral are required in biochemical processes and mainly play an important role as cofactor in enzymatic reaction. The objective of this research is to investigate the performance of graphite tail on supporting plant growth and yield of ground nut (Arachishypogeae L.). A field experiment has been performed to test the performance of mixed graphite tail and reduced organic matter dose. The graphite tail size were reduced to various sieved size, -80 mesh, -100 mesh and -200 mesh. The experiment was setup in randomized block design with 4 treatments and 6 replications for each treatment, while the control plot is received without graphite tail. The results demonstrated that reduced organic matter along with -200 mesh tail has potentially decreased plant height at the end of vegetative growth stage, in contrast for to -80 mesh tail amendment increased individual fresh plant biomass. Statistically, there was no change of plant nodule, individual shoot fresh and dry weight, root nodule, number of pod following any mesh of graphite tail amendment. Reducing organic matter while adding graphite tail of 5% did not change bean weight in all plot. In contrast, reduced organic matter along with 80-mesh graphite tail amendment improved the nut yield per plot. This experiment suggests that graphite tail, mainly -80 mesh graphite tail can be possibly used in legume production.

40 CFR 436.380 - Applicability; description of the graphite subcategory.

Code of Federal Regulations, 2011 CFR

2011-07-01

... graphite subcategory. 436.380 Section 436.380 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) EFFLUENT GUIDELINES AND STANDARDS MINERAL MINING AND PROCESSING POINT SOURCE CATEGORY Graphite Subcategory § 436.380 Applicability; description of the graphite subcategory. The provisions of this subpart...

40 CFR 436.380 - Applicability; description of the graphite subcategory.

Code of Federal Regulations, 2010 CFR

2010-07-01

... graphite subcategory. 436.380 Section 436.380 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY (CONTINUED) EFFLUENT GUIDELINES AND STANDARDS MINERAL MINING AND PROCESSING POINT SOURCE CATEGORY Graphite Subcategory § 436.380 Applicability; description of the graphite subcategory. The provisions of this subpart...

Continued Investigation of Leakage and Power Loss Test Results for Competing Turbine Engine Seals

NASA Technical Reports Server (NTRS)

Delgado, Irebert R.; Proctor, Margaret P.

2007-01-01

Seal leakage decreases with increasing surface speed due to reduced clearances from disk centrifugal growth. Annular and labyrinth seal leakage are 2-3 times greater than brush and finger seal leakage. Seal leakage rates increase with increasing temperature because of seal clearance growth due to different coefficients of thermal expansion between the seal and test disk. Seal power loss is not strongly affected by inlet temperature. Seal power loss increases with increasing surface speed, seal pressure differential, mass flow rate or flow factor, and radial clearance. The brush and finger seals had nearly the same power loss. Annular and labyrinth seal power loss were higher than finger or brush seal power loss. The brush seal power loss was the lowest and 15-30% lower than annular and labyrinth seal power loss.

Fabrication and testing of non-graphitic superhybrid composites

NASA Technical Reports Server (NTRS)

Lark, R. F.; Sinclair, J. H.; Chamis, C. C.

1979-01-01

A study was conducted to determine the fabrication feasibility and the mechanical properties of adhesively-bonded boron aluminum/titanium and non-graphitic fiber/epoxy resin superhybrid (NGSH) composite laminates for potential aerospace applications. The major driver for this study was the elimination of a potential graphite fiber release problem in the event of a fire. The results of the study show that non-graphitic fibers, such as S-glass and Kevlar 49, may be substituted for the graphite fibers used in superhybrid (SH) composites for some applications. As is to be expected, however, the non-graphitic superhybrids have lower stiffness properties than the graphitic superhybrids. In-plane and flexural moduli of the laminates studied in this program can be predicted reasonably well using linear laminate theory while nonlinear laminate theory is required for strength predictions.

Status of Initial Assessment of Physical and Mechanical Properties of Graphite Grades for NGNP Appkications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Strizak, Joe P; Burchell, Timothy D; Windes, Will

2011-12-01

Current candidate graphite grades for the core structures of NGNP include grades NBG-17, NBG-18, PCEA and IG-430. Both NBG-17 and NBG-18 are manufactured using pitch coke, and are vibrationally molded. These medium grain products are produced by SGL Carbon SAS (France). Tayo Tanso (Japan) produces IG-430 which is a petroleum coke, isostatically molded, nuclear grade graphite. And PCEA is a medium grain, extruded graphite produced by UCAR Carbon Co. (USA) from petroleum coke. An experimental program has been initiated to develop physical and mechanical properties data for these current candidate graphites. The results will be judged against the requirements formore » nuclear grade graphites set forth in ASTM standard D 7219-05 "Standard Specification for Isotropic and Near-isotropic Nuclear Graphites". Physical properties data including thermal conductivity and coefficient of thermal expansion, and mechanical properties data including tensile, compressive and flexural strengths will be obtained using the established test methods covered in D-7219 and ASTM C 781-02 "Standard Practice for Testing Graphite and Boronated Graphite Components for High-Temperature Gas-Cooled Nuclear Reactors". Various factors known to effect the properties of graphites will be investigated. These include specimen size, spatial location within a graphite billet, specimen orientation (ag and wg) within a billet, and billet-to-billet variations. The current status of the materials characterization program is reported herein. To date billets of the four graphite grades have been procured, and detailed cut up plans for obtaining the various specimens have been prepared. Particular attention has been given to the traceability of each specimen to its spatial location and orientation within a billet.« less

Turbine interstage seal with self-balancing capability

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mills, Jacob A; Jones, Russell B; Sexton, Thomas D

An interstage seal for a turbine of a gas turbine engine, the interstage seal having a seal carrier with an axial extending seal tooth movable with a stator of the engine, and a rotor with a seal surface that forms the interstage seal with the seal tooth, where a magnetic force produced by two magnets and a gas force produced by a gas pressure acting on the seal carrier forms a balancing force to maintain a close clearance of the seal without the seal tooth contacting the rotor seal surfaces during engine operation. In other embodiments, two pairs of magnetsmore » produce first and second magnetic forces that balance the seal in the engine.« less

A contrastive study of three graphite anodes in the piperidinium based electrolytes for lithium ion batteries

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jiang, Xiao-Tao; Wang, Chen-Yi; Gao, Kun, E-mail: gaokun0451@163.com

Graphical abstract: The fitting results of R{sub sei} and R{sub ct} of three graphite/Li cells. Besides three graphite/Li cells show the similar R{sub sei}, the NG198/Li cell demonstrates a higher R{sub ct} value in all test temperatures. Especially, the R{sub ct} at 333 K is even up to 355.8 Ω cm{sup 2}. Obviously, the narrow distribution of edge plane for NG198 caused this result, and then greatly restricts its cell capacity. By contrast, CMB with bigger specific surface area and more Li{sup +} insertion points shows lower resistance at room temperature, which should help to improve its capacity. - Highlights:more » • SEI film is closely related to graphite structures and formation temperature. • The graphite with bigger surface area and more Li{sup +} insertion points behaves better. • The graphite with narrow edge plane is uncompetitive for ionic liquid electrolyte. - Abstract: The electrochemical behaviors of natural graphite (NG198), artificial graphite (AG360) and carbon microbeads (CMB) in an ionic liquid based electrolyte are investigated by cyclic voltammetry (CV). The surface and structure of three graphite materials are characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD) before and after cycling. It is found that solid electrolyte interface (SEI) is closely related to graphite structure. Benefiting from larger specific surface area and more dispersed Li{sup +} insertion points, CMB shows a better Li{sup +} insertion/de-insertion behavior than NG198 and AG360. Furthermore, electrochemical impedance spectra (EIS) prove that the SEI of different graphite electrodes has different intrinsic resistance and Li{sup +} penetrability. By comparison, CMB behaves better cell performances than AG360, while the narrow edge plane makes NG198 uncompetitive as a potential anode for the ionic liquids (ILs)-type Li-ion battery.« less

Is Water at the Graphite Interface Vapor-like or Ice-like?

PubMed

Qiu, Yuqing; Lupi, Laura; Molinero, Valeria

2018-04-05

Graphitic surfaces are the main component of soot, a major constituent of atmospheric aerosols. Experiments indicate that soots of different origins display a wide range of abilities to heterogeneously nucleate ice. The ability of pure graphite to nucleate ice in experiments, however, seems to be almost negligible. Nevertheless, molecular simulations with the monatomic water model mW with water-carbon interactions parameterized to reproduce the experimental contact angle of water on graphite predict that pure graphite nucleates ice. According to classical nucleation theory, the ability of a surface to nucleate ice is controlled by the binding free energy between ice immersed in liquid water and the surface. To establish whether the discrepancy in freezing efficiencies of graphite in mW simulations and experiments arises from the coarse resolution of the model or can be fixed by reparameterization, it is important to elucidate the contributions of the water-graphite, water-ice, and ice-water interfaces to the free energy, enthalpy, and entropy of binding for both water and the model. Here we use thermodynamic analysis and free energy calculations to determine these interfacial properties. We demonstrate that liquid water at the graphite interface is not ice-like or vapor-like: it has similar free energy, entropy, and enthalpy as water in the bulk. The thermodynamics of the water-graphite interface is well reproduced by the mW model. We find that the entropy of binding between graphite and ice is positive and dominated, in both experiments and simulations, by the favorable entropy of reducing the ice-water interface. Our analysis indicates that the discrepancy in freezing efficiencies of graphite in experiments and the simulations with mW arises from the inability of the model to simultaneously reproduce the contact angle of liquid water on graphite and the free energy of the ice-graphite interface. This transferability issue is intrinsic to the resolution of the model, and arises from its lack of rotational degrees of freedom.

Effects of Compression, Staging, and Braid Angle on Braided Rope Seal Performance

NASA Technical Reports Server (NTRS)

Steinetz, Bruce M.; Adams, Michael L.

1997-01-01

Future turbine engines and industrial systems will be operating at increased temperatures to achieve more demanding efficiency and performance goals. In the highest temperature sections of the engine new material systems such as ceramics and intermetallics are being considered to withstand the harsh thermal environment. Components constructed of these low expansion-rate materials experience thermal strains and a resulting reduction of life when rigidly attached to high expansion-rate, superalloy support structures. Seals are being designed to both seal and to serve as compliant mounts allowing for relative thermal growths between high temperature but brittle primary structures and the surrounding support structures. Previous seal research yielded several braided rope seal designs which demonstrated the ability to both seal and serve as a compliant mount. The hybrid seal was constructed of an all-ceramic (alumina-silica) core overbraided with a superalloy wire sheath (cobalt based superalloy). The all ceramic seal was constructed of an all-ceramic (alumina-silica) core overbraided with multiple ceramic (alumina-silica) sheath layers. Program goals for braided rope seals are to improve flow resistance and/or seal resilience. To that end, the current report studies the test results of: baseline and modified hybrid seals; two stage hybrid and two stage all-ceramic seal configurations; and single stage hybrid and single stage all-ceramic seal configurations for a range of seal crush conditions. Hybrid seal modifications include increasing the sheath braid angle and core coverage. For the same percent seal cross-sectional crush, results show that increasing the hybrid seal braid angle increased seal stiffness and seal unit load, resulting in flows approximately one third of the baseline hybrid seal flows. For both hybrid and all-ceramic seals, two stage seal configurations significantly outperformed single stage configurations. Two stage seal flows were at least 30% less than the single stage seal flows for the same seal crush. Furthermore, test results of single stage seals indicate that for both all-ceramic and hybrid seals, a specific seal crush condition exists at which minimum flows are achieved (i.e. increasing seal crush beyond a certain point does not result in better flow performance). Flow results are presented for a range of pressures and temperatures from ambient to 1300 F, before and after scrubbing. Compression tests results show that for both all-ceramic and hybrid seals, seal preload and stiffness increase with seal crush, but residual seal interference remains constant.

Effect of friction on oxidative graphite intercalation and high-quality graphene formation.

PubMed

Seiler, Steffen; Halbig, Christian E; Grote, Fabian; Rietsch, Philipp; Börrnert, Felix; Kaiser, Ute; Meyer, Bernd; Eigler, Siegfried

2018-02-26

Oxidative wet-chemical delamination of graphene from graphite is expected to become a scalable production method. However, the formation process of the intermediate stage-1 graphite sulfate by sulfuric acid intercalation and its subsequent oxidation are poorly understood and lattice defect formation must be avoided. Here, we demonstrate film formation of micrometer-sized graphene flakes with lattice defects down to 0.02% and visualize the carbon lattice by transmission electron microscopy at atomic resolution. Interestingly, we find that only well-ordered, highly crystalline graphite delaminates into oxo-functionalized graphene, whereas other graphite grades do not form a proper stage-1 intercalate and revert back to graphite upon hydrolysis. Ab initio molecular dynamics simulations show that ideal stacking and electronic oxidation of the graphite layers significantly reduce the friction of the moving sulfuric acid molecules, thereby facilitating intercalation. Furthermore, the evaluation of the stability of oxo-species in graphite sulfate supports an oxidation mechanism that obviates intercalation of the oxidant.

Direct Preparation of Few Layer Graphene Epoxy Nanocomposites from Untreated Flake Graphite.

PubMed

Throckmorton, James; Palmese, Giuseppe

2015-07-15

The natural availability of flake graphite and the exceptional properties of graphene and graphene-polymer composites create a demand for simple, cost-effective, and scalable methods for top-down graphite exfoliation. This work presents a novel method of few layer graphite nanocomposite preparation directly from untreated flake graphite using a room temperature ionic liquid and laminar shear processing regimen. The ionic liquid serves both as a solvent and initiator for epoxy polymerization and is incorporated chemically into the matrix. This nanocomposite shows low electrical percolation (0.005 v/v) and low thickness (1-3 layers) graphite/graphene flakes by TEM. Additionally, the effect of processing conditions by rheometry and comparison with solvent-free conditions reveal the interactions between processing and matrix properties and provide insight into the theory of the chemical and physical exfoliation of graphite crystals and the resulting polymer matrix dispersion. An interaction model that correlates the interlayer shear physics of graphite flakes and processing parameters is proposed and tested.

New insights into canted spiro carbon interstitial in graphite

NASA Astrophysics Data System (ADS)

EL-Barbary, A. A.

2017-12-01

The self-interstitial carbon is the key to radiation damage in graphite moderator nuclear reactor, so an understanding of its behavior is essential for plant safety and maximized reactor lifetime. The density functional theory is applied on four different graphite unit cells, starting from of 64 carbon atoms up to 256 carbon atoms, using AIMPRO code to obtain the energetic, athermal and mechanical properties of carbon interstitial in graphite. This study presents first principles calculations of the energy of formation that prove its high barrier to athermal diffusion (1.1 eV) and the consequent large critical shear stress (39 eV-50 eV) necessary to shear graphite planes in its presence. Also, for the first time, the gamma surface of graphite in two dimensions is calculated and found to yield the critical shear stress for perfect graphite. Finally, in contrast to the extensive literature describing the interstitial of carbon in graphite as spiro interstitial, in this work the ground state of interstitial carbon is found to be canted spiro interstitial.

Adsorption behavior of bisphenol A on CTAB-modified graphite

NASA Astrophysics Data System (ADS)

Wang, Li-Cong; Ni, Xin-jiong; Cao, Yu-Hua; Cao, Guang-qun

2018-01-01

In this work, the adsorption behavior of BPA on CTAB-modified graphite was investigated thoroughly to develop a novel absorbent material. Atomic force microscopy revealed that conical admicelles formed on the surface of graphite. The surface area of graphite decreased significantly from 1.46 to 0.95 m2 g-1, which confirmed the formation of the larger size admicelle instead of the original smaller particle on the surface. CTAB concentration and incubation time affected the progress of admicelle formation on the surface of graphite. Adsolubilization is key in BPA adsorption by CTAB-modified graphite. An extraordinary cation-π electron interaction between CTAB and BPA, revealed by a red-shift in the ultraviolet spectrum, as well as a hydrophobic interaction contribute substantially to BPA adsolubilization. The equilibrium adsorption capacity of the modified graphite for BPA was 125.01 mg g-1. The adsorption kinetic curves of BPA on modified graphite were shown to follow a pseudosecond-order rate. The adsorption process was observed to be both spontaneous and exothermic complied with the Freundlich model.

Phase Structures and Magnetic Properties of Graphite Nanosheets and Ni-Graphite Nanocomposite Synthesized by Electrical Explosion of Wire in Liquid

NASA Astrophysics Data System (ADS)

Nguyen, Minh-Thuyet; Kim, Jin-Hyung; Lee, Jung-Goo; Kim, Jin-Chun

2018-03-01

The present work studied on phases and magnetic properties of graphite nanosheets and Ni-graphite nanocomposite synthesized using the electrical explosion of wire (EEW) in ethanol. X-ray diffraction and field emission scanning electron microscope were used to investigate the phases and the morphology of the nanopowders obtained. It was found that graphite nanosheets were absolutely fabricated by EEW with a thickness of 29 nm and 3 μm diameter. The as-synthesized Ni-graphite composite powders had a Ni-coating on the surfaces of graphite sheets. The hysteresis loop of the as-exploded, the hydrogen-treated composite nanopowders and the sintered samples were examined with a vibrating sample magnetometer at room temperature. The Ni-graphite composite exposed the magnetic behaviors which are attributed to Ni component. The magnetic properties of composite had the improvement from 10.2 emu/g for the as-exploded powders to 15.8 emu/g for heat-treated powders and 49.16 emu/g for sintered samples.

Quantifying microstructural dynamics and electrochemical activity of graphite and silicon-graphite lithium ion battery anodes

NASA Astrophysics Data System (ADS)

Pietsch, Patrick; Westhoff, Daniel; Feinauer, Julian; Eller, Jens; Marone, Federica; Stampanoni, Marco; Schmidt, Volker; Wood, Vanessa

2016-09-01

Despite numerous studies presenting advances in tomographic imaging and analysis of lithium ion batteries, graphite-based anodes have received little attention. Weak X-ray attenuation of graphite and, as a result, poor contrast between graphite and the other carbon-based components in an electrode pore space renders data analysis challenging. Here we demonstrate operando tomography of weakly attenuating electrodes during electrochemical (de)lithiation. We use propagation-based phase contrast tomography to facilitate the differentiation between weakly attenuating materials and apply digital volume correlation to capture the dynamics of the electrodes during operation. After validating that we can quantify the local electrochemical activity and microstructural changes throughout graphite electrodes, we apply our technique to graphite-silicon composite electrodes. We show that microstructural changes that occur during (de)lithiation of a pure graphite electrode are of the same order of magnitude as spatial inhomogeneities within it, while strain in composite electrodes is locally pronounced and introduces significant microstructural changes.

Overview of LIDS Docking and Berthing System Seals

NASA Technical Reports Server (NTRS)

Daniels, Christopher C.; Dunlap, Patrick H., Jr.; deGroh, Henry C., III; Steinetz, Bruce M.; Oswald, Jay J.; Smith, Ian

2007-01-01

This viewgraph presentation describes the Low Impact Docking System (LIDS) docking and berthing system seals. The contents include: 1) Description of the Application: Low Impact Docking System (LIDS); 2) LIDS Seal Locations: Vehicle Undocked (Hatch Closed); 3) LIDS Seal Locations: Mechanical Pass Thru; 4) LIDS Seal Locations: Electrical and Pyro Connectors; 5) LIDS Seal Locations: Vehicle Docked (Hatches Open); 6) LIDS Seal Locations: Main Interface Seal; 7) Main Interface Seal Challenges and Specifications; 8) Approach; 9) Seal Concepts Under Development/Evaluation; 10) Elastomer Material Evaluations; 11) Evaluation of Relevant Seal Properties; 12) Medium-Scale (12") Gask-O-Seal Compression Tests; 13) Medium-Scale Compression Results; 14) Adhesion Forces of Elliptical Top Gask-o-seals; 15) Medium-Scale Seals; 16) Medium-Scale Leakage Results: Effect of Configuration; 17) Full Scale LIDS Seal Test Rig Development; 18) Materials International Space Station Experiment (MISSE 6A and 6B); and 19) Schedule.

Overview of NASA Glenn Seal Program

NASA Technical Reports Server (NTRS)

Steinetz, Bruce M.; Proctor, Margaret P.; Dunlap, Patrick H., Jr.; Delgado, Irebert; DeMange, Jeffrey J.; Daniels, Christopher C.; Lattime, Scott B.

2003-01-01

The Seal Team is divided into four primary areas. These areas include turbine engine seal development, structural seal development, acoustic seal development, and adaptive seal development. The turbine seal area focuses on high temperature, high speed shaft seals for secondary air system flow management. The structural seal area focuses on high temperature, resilient structural seals required to accommodate large structural distortions for both space- and aero-applications. Our goal in the acoustic seal project is to develop non-contacting, low leakage seals exploiting the principles of advanced acoustics. We are currently investigating a new acoustic field known as Resonant Macrosonic Synthesis (RMS) to see if we can harness the large acoustic standing pressure waves to form an effective air-barrier/seal. Our goal in the adaptive seal project is to develop advanced sealing approaches for minimizing blade-tip (shroud) or interstage seal leakage. We are planning on applying either rub-avoidance or regeneration clearance control concepts (including smart structures and materials) to promote higher turbine engine efficiency and longer service lives.

Rotary shaft sealing assembly

DOEpatents

Dietle, Lannie L; Schroeder, John E; Kalsi, Manmohan S; Alvarez, Patricio D

2013-08-13

A rotary shaft sealing assembly in which a first fluid is partitioned from a second fluid in a housing assembly having a rotary shaft located at least partially within. In one embodiment a lip seal is lubricated and flushed with a pressure-generating seal ring preferably having an angled diverting feature. The pressure-generating seal ring and a hydrodynamic seal may be used to define a lubricant-filled region with each of the seals having hydrodynamic inlets facing the lubricant-filled region. Another aspect of the sealing assembly is having a seal to contain pressurized lubricant while withstanding high rotary speeds. Another rotary shaft sealing assembly embodiment includes a lubricant supply providing a lubricant at an elevated pressure to a region between a lip seal and a hydrodynamic seal with a flow control regulating the flow of lubricant past the lip seal. The hydrodynamic seal may include an energizer element having a modulus of elasticity greater than the modulus of elasticity of a sealing lip of the hydrodynamic seal.

Rotary shaft sealing assembly

DOEpatents

Dietle, Lannie L.; Schroeder, John E.; Kalsi, Manmohan S.; Alvarez, Patricio D.

2010-09-21

A rotary shaft sealing assembly in which a first fluid is partitioned from a second fluid in a housing assembly having a rotary shaft located at least partially within. In one embodiment a lip seal is lubricated and flushed with a pressure-generating seal ring preferably having an angled diverting feature. The pressure-generating seal ring and a hydrodynamic seal may be used to define a lubricant-filled region with each of the seals having hydrodynamic inlets facing the lubricant-filled region. Another aspect of the sealing assembly is having a seal to contain pressurized lubricant while withstanding high rotary speeds. Another rotary shaft sealing assembly embodiment includes a lubricant supply providing a lubricant at an elevated pressure to a region between a lip seal and a hydrodynamic seal with a flow control regulating the flow of lubricant past the lip seal. The hydrodynamic seal may include an energizer element having a modulus of elasticity greater than the modulus of elasticity of a sealing lip of the hydrodynamic seal.

Industrial Code Development

NASA Technical Reports Server (NTRS)

Shapiro, Wilbur

1991-01-01

The industrial codes will consist of modules of 2-D and simplified 2-D or 1-D codes, intended for expeditious parametric studies, analysis, and design of a wide variety of seals. Integration into a unified system is accomplished by the industrial Knowledge Based System (KBS), which will also provide user friendly interaction, contact sensitive and hypertext help, design guidance, and an expandable database. The types of analysis to be included with the industrial codes are interfacial performance (leakage, load, stiffness, friction losses, etc.), thermoelastic distortions, and dynamic response to rotor excursions. The first three codes to be completed and which are presently being incorporated into the KBS are the incompressible cylindrical code, ICYL, and the compressible cylindrical code, GCYL.

Altitude release mechanism

DOEpatents

Kulhanek, Frank C.

1977-01-01

An altitude release mechanism for releasing a radiosonde or other measuring instrument from a balloon carrying it up into the atmosphere includes a bottle partially filled with water, a tube sealed into the bottle having one end submerged in the water in the bottle and the free end extending above the top of the bottle and a strip of water-disintegrable paper held within the free end of the tube linking the balloon to the remainder of the package. As the balloon ascends, the lowered atmospheric air pressure causes the air in the bottle to expand, forcing the water in the bottle up the tubing to wet and disintegrate the paper, releasing the package from the balloon.

Continued Investigation of Leakage and Power Loss Test Results for Competing Turbine Engine Seals

NASA Technical Reports Server (NTRS)

Delgado, Irebert R.; Proctor, Margaret P.

2006-01-01

Secondary seal leakage in jet engine applications results in power losses to the engine cycle. Likewise, seal power loss in jet engines not only result in efficiency loss but also increase the heat input into the engine resulting in reduced component lives. Experimental work on labyrinth and annular seals was performed at NASA Glenn Research Center to quantify seal leakage and power loss at various temperatures, seal pressure differentials, and surface speeds. Data from annular and labyrinth seals are compared with previous brush and finger seal test results. Data are also compared to literature. Annular and labyrinth seal leakage rates are 2 to 3 times greater than brush and finger seal rates. Seal leakage decreases with increasing speed but increases with increasing test temperature due to thermal expansion mismatch. Also seal power loss increases with surface speed, seal pressure differential, mass flow rate, and radial clearance. Annular and labyrinth seal power losses were higher than those of brush or finger seal data. The brush seal power loss was 15 to 30 percent lower than annular and labyrinth seal power loss.

Fire test method for graphite fiber reinforced plastics

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1980-01-01

A potential problem in the use of graphite fiber reinforced resin matrix composites is the dispersal of graphite fibers during accidential fires. Airborne, electrically conductive fibers originating from the burning composites could enter and cause shorting in electrical equipment located in surrounding areas. A test method for assessing the burning characteristics of graphite fiber reinforced composites and the effectiveness of the composites in retaining the graphite fibers has been developed. The method utilizes a modified rate of heat release apparatus. The equipment and the testing procedure are described. The application of the test method to the assessment of composite materials is illustrated for two resin matrix/graphite composite systems.

Process for the fabrication of aluminum metallized pyrolytic graphite sputtering targets

DOEpatents

Makowiecki, Daniel M.; Ramsey, Philip B.; Juntz, Robert S.

1995-01-01

An improved method for fabricating pyrolytic graphite sputtering targets with superior heat transfer ability, longer life, and maximum energy transmission. Anisotropic pyrolytic graphite is contoured and/or segmented to match the erosion profile of the sputter target and then oriented such that the graphite's high thermal conductivity planes are in maximum contact with a thermally conductive metal backing. The graphite contact surface is metallized, using high rate physical vapor deposition (HRPVD), with an aluminum coating and the thermally conductive metal backing is joined to the metallized graphite target by one of four low-temperature bonding methods; liquid-metal casting, powder metallurgy compaction, eutectic brazing, and laser welding.

Arsenic Removal from Water by Adsorption on Iron-Contaminated Cryptocrystalline Graphite

NASA Astrophysics Data System (ADS)

Yang, Qiang; Yang, Lang; Song, Shaoxian; Xia, Ling

This work aimed to study the feasibility of using iron-contaminated graphite as an adsorbent for As(V) removal from water. The adsorbent was prepared by grinding graphite concentrate with steel ball. The study was performed through the measurements of adsorption capacity, BET surface area and XPS analysis. The experimental results showed that the iron-contaminated graphite exhibited significantly high adsorption capacity of As(V). The higher the iron contaminated on the graphite surface, the higher the adsorption capacity of As(V) on the material obtained. It was suggested that the ion-contaminated graphite was a good adsorbent for As(V) removal.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Inam, A., E-mail: aqil.ceet@pu.edu.pk; Brydson, R., E-mail: mtlrmdb@leeds.ac.uk; Edmonds, D.V., E-mail: d.v.edmonds@leeds.ac.uk

The potential for using graphite particles as an internal lubricant during machining is considered. Graphite particles were found to form during graphitisation of experimental medium-carbon steel alloyed with Si and Al. The graphite nucleation sites were strongly influenced by the starting microstructure, whether ferrite–pearlite, bainite or martensite, as revealed by light and electron microscopy. Favourable nucleation sites in the ferrite–pearlite starting microstructure were, not unexpectedly, found to be located within pearlite colonies, no doubt due to the presence of abundant cementite as a source of carbon. In consequence, the final distribution of graphite nodules in ferrite–pearlite microstructures was less uniformmore » than for the bainite microstructure studied. In the case of martensite, this study found a predominance of nucleation at grain boundaries, again leading to less uniform graphite dispersions. - Highlights: • Metallography of formation of graphite particles in experimental carbon steel. • Potential for using graphite in steel as an internal lubricant during machining. • Microstructure features expected to influence improved machinability studied. • Influence of pre-anneal starting microstructure on graphite nucleation sites. • Influence of pre-anneal starting microstructure on graphite distribution. • Potential benefit is new free-cutting steel compositions without e.g. Pb alloying.« less

Understanding the reaction of nuclear graphite with molecular oxygen: Kinetics, transport, and structural evolution

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kane, Joshua J.; Contescu, Cristian I.; Smith, Rebecca E.

A thorough understanding of oxidation is important when considering the health and integrity of graphite components in graphite reactors. For the next generation of graphite reactors, HTGRs specifically, an unlikely air ingress has been deemed significant enough to have made its way into the licensing applications of many international licensing bodies. While a substantial body of literature exists on nuclear graphite oxidation in the presence of molecular oxygen and significant efforts have been made to characterize oxidation kinetics of various grades, the value of existing information is somewhat limited. Often, multiple competing processes, including reaction kinetics, mass transfer, and microstructuralmore » evolution, are lumped together into a single rate expression that limits the ability to translate this information to different conditions. This article reviews the reaction of graphite with molecular oxygen in terms of the reaction kinetics, gas transport, and microstructural evolution of graphite. It also presents the foundations of a model for the graphite-molecular oxygen reaction system that is kinetically independent of graphite grade, and is capable of describing both the bulk and local oxidation rates under a wide range of conditions applicable to air-ingress.« less

Understanding the reaction of nuclear graphite with molecular oxygen: Kinetics, transport, and structural evolution

DOE PAGES

Kane, Joshua J.; Contescu, Cristian I.; Smith, Rebecca E.; ...

2017-06-08

A thorough understanding of oxidation is important when considering the health and integrity of graphite components in graphite reactors. For the next generation of graphite reactors, HTGRs specifically, an unlikely air ingress has been deemed significant enough to have made its way into the licensing applications of many international licensing bodies. While a substantial body of literature exists on nuclear graphite oxidation in the presence of molecular oxygen and significant efforts have been made to characterize oxidation kinetics of various grades, the value of existing information is somewhat limited. Often, multiple competing processes, including reaction kinetics, mass transfer, and microstructuralmore » evolution, are lumped together into a single rate expression that limits the ability to translate this information to different conditions. This article reviews the reaction of graphite with molecular oxygen in terms of the reaction kinetics, gas transport, and microstructural evolution of graphite. It also presents the foundations of a model for the graphite-molecular oxygen reaction system that is kinetically independent of graphite grade, and is capable of describing both the bulk and local oxidation rates under a wide range of conditions applicable to air-ingress.« less

Triple acting radial seal

DOEpatents

Ebert, Todd A [West Palm Beach, FL; Carella, John A [Jupiter, FL

2012-03-13

A triple acting radial seal used as an interstage seal assembly in a gas turbine engine, where the seal assembly includes an interstage seal support extending from a stationary inner shroud of a vane ring, the interstage seal support includes a larger annular radial inward facing groove in which an outer annular floating seal assembly is secured for radial displacement, and the outer annular floating seal assembly includes a smaller annular radial inward facing groove in which an inner annular floating seal assembly is secured also for radial displacement. A compliant seal is secured to the inner annular floating seal assembly. The outer annular floating seal assembly encapsulates the inner annular floating seal assembly which is made from a very low alpha material in order to reduce thermal stress.

Fire performance, microstructure and thermal degradation of an epoxy based nano intumescent fire retardant coating for structural applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aziz, Hammad, E-mail: engr.hammad.aziz03@gmail.com; Ahmad, Faiz, E-mail: faizahmad@petronas.com.my; Yusoff, P. S. M. Megat

Intumescent fire retardant coating (IFRC) is a passive fire protection system which swells upon heating to form expanded multi-cellular char layer that protects the substrate from fire. In this research work, IFRC’s were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder and cured together using curing agent. IFRC was then reinforced with nano magnesium oxide and nano alumina as inorganic fillers to study their effect towards fire performance, microstructure and thermal degradation. Small scale fire test was conducted to investigate themore » thermal insulation of coating whereas fire performance was calculated using thermal margin value. Field emission scanning electron microscopy was used to examine the microstructure of char obtained after fire test. Thermogravimetric analysis was conducted to investigate the residual weight of coating. Results showed that the performance of the coating was enhanced by reinforcement with nano size fillers as compared to non-filler based coating. Comparing both nano size magnesium oxide and nano size alumina; nano size alumina gave better fire performance with improved microstructure of char and high residual weight.« less

Fire performance, microstructure and thermal degradation of an epoxy based nano intumescent fire retardant coating for structural applications

NASA Astrophysics Data System (ADS)

Aziz, Hammad; Ahmad, Faiz; Yusoff, P. S. M. Megat; Zia-ul-Mustafa, M.

2015-07-01

Intumescent fire retardant coating (IFRC) is a passive fire protection system which swells upon heating to form expanded multi-cellular char layer that protects the substrate from fire. In this research work, IFRC's were developed using different flame retardants such as ammonium polyphosphate, expandable graphite, melamine and boric acid. These flame retardants were bound together with the help of epoxy binder and cured together using curing agent. IFRC was then reinforced with nano magnesium oxide and nano alumina as inorganic fillers to study their effect towards fire performance, microstructure and thermal degradation. Small scale fire test was conducted to investigate the thermal insulation of coating whereas fire performance was calculated using thermal margin value. Field emission scanning electron microscopy was used to examine the microstructure of char obtained after fire test. Thermogravimetric analysis was conducted to investigate the residual weight of coating. Results showed that the performance of the coating was enhanced by reinforcement with nano size fillers as compared to non-filler based coating. Comparing both nano size magnesium oxide and nano size alumina; nano size alumina gave better fire performance with improved microstructure of char and high residual weight.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chuang, Chihpin; Singh, Dileep; Kenesei, Peter

The size and morphology of the graphite particles play a crucial role in determining various mechanical and thermal properties of cast iron. In the present study, we utilized high-energy synchrotron X-ray tomography to perform quantitative 3D-characterization of the distribution of graphite particles in high-strength compacted graphite iron (CGI). The size, shape, and spatial connectivity of graphite were examined. The analysis reveals that the compacted graphite can grow with a coral-tree-like morphology and span several hundred microns in the iron matrix.

Preparation of pyrolytic carbon coating on graphite for inhibiting liquid fluoride salt and Xe135 penetration for molten salt breeder reactor

NASA Astrophysics Data System (ADS)

Song, Jinliang; Zhao, Yanling; He, Xiujie; Zhang, Baoliang; Xu, Li; He, Zhoutong; Zhang, DongSheng; Gao, Lina; Xia, Huihao; Zhou, Xingtai; Huai, Ping; Bai, Shuo

2015-01-01

A fixed-bed deposition method was used to prepare rough laminar pyrolytic carbon coating (RLPyC) on graphite for inhibiting liquid fluoride salt and Xe135 penetration during use in molten salt breeder reactor. The RLPyC coating possessed a graphitization degree of 44% and had good contact with graphite substrate. A high-pressure reactor was constructed to evaluate the molten salt infiltration in the isostatic graphite (IG-110, TOYO TANSO CO., LTD.) and RLPyC coated graphite under 1.01, 1.52, 3.04, 5.07 and 10.13 × 105 Pa for 12 h. Mercury injection and molten-salt infiltration experiments indicated the porosity and the salt-infiltration amount of 18.4% and 13.5 wt% under 1.52 × 105 Pa of IG-110, which was much less than 1.2% and 0.06 wt% under 10.13 × 105 Pa of the RLPyC, respectively. A vacuum device was constructed to evaluate the Xe135 penetration in the graphite. The helium diffusion coefficient of RLPyC coated graphite was 2.16 × 10-12 m2/s, much less than 1.21 × 10-6 m2/s of the graphite. Thermal cycle experiment indicated the coatings possessed excellent thermal stability. The coated graphite could effectively inhibit the liquid fluoride salt and Xe135 penetration.

Kinetics of Chronic Oxidation of NBG-17 Nuclear Graphite by Water Vapor

DOE Office of Scientific and Technical Information (OSTI.GOV)

Contescu, Cristian I; Burchell, Timothy D; Mee, Robert

2015-05-01

This report presents the results of kinetic measurements during accelerated oxidation tests of NBG-17 nuclear graphite by low concentration of water vapor and hydrogen in ultra-high purity helium. The objective is to determine the parameters in the Langmuir-Hinshelwood (L-H) equation describing the oxidation kinetics of nuclear graphite in the helium coolant of high temperature gas-cooled reactors (HTGR). Although the helium coolant chemistry is strictly controlled during normal operating conditions, trace amounts of moisture (predictably < 0.2 ppm) cannot be avoided. Prolonged exposure of graphite components to water vapor at high temperature will cause very slow (chronic) oxidation over the lifetimemore » of graphite components. This behavior must be understood and predicted for the design and safe operation of gas-cooled nuclear reactors. The results reported here show that, in general, oxidation by water of graphite NBG-17 obeys the L-H mechanism, previously documented for other graphite grades. However, the characteristic kinetic parameters that best describe oxidation rates measured for graphite NBG-17 are different than those reported previously for grades H-451 (General Atomics, 1978) and PCEA (ORNL, 2013). In some specific conditions, certain deviations from the generally accepted L-H model were observed for graphite NBG-17. This graphite is manufactured in Germany by SGL Carbon Group and is a possible candidate for the fuel elements and reflector blocks of HTGR.« less

Through-thickness thermal conductivity enhancement of graphite film/epoxy composite via short duration acidizing modification

NASA Astrophysics Data System (ADS)

Wang, Han; Wang, Shaokai; Lu, Weibang; Li, Min; Gu, Yizhou; Zhang, Yongyi; Zhang, Zuoguang

2018-06-01

Graphite films have excellent in-plane thermal conductivity but extremely low through-thickness thermal conductivity because of their intrinsic inter-layer spaces. To improve the inter-layer heat transfer of graphite films, we developed a simple interfacial modification with a short duration mixed-acid treatment. The effects of the mixture ratio of sulfuric and nitric acids and treatment time on the through-thickness thermal properties of graphite films were studied. The modification increased the through-thickness thermal conductivity by 27% and 42% for the graphite film and its composite, respectively. X-ray photoelectron spectroscopy, X-ray powder diffraction, and scanning electron microscopy results indicated that the acidification process had two competing effects: the positive contribution made by the enhanced interaction between the graphite layers induced by the functional groups and the negative effect from the destruction of the graphite layers. As a result, an optimal acidification method was found to be sulfuric/nitric acid treatment with a mixture ratio of 3:1 for 15 min. The resultant through-thickness thermal conductivity of the graphite film could be improved to 0.674 W/mK, and the corresponding graphite/epoxy composite shows a through-thickness thermal conductivity of 0.587 W/mK. This method can be directly used for graphite films and their composite fabrication to improve through-thickness thermal conductivity.

Characterization of the Intrinsic Water Wettability of Graphite Using Contact Angle Measurements: Effect of Defects on Static and Dynamic Contact Angles.

PubMed

Kozbial, Andrew; Trouba, Charlie; Liu, Haitao; Li, Lei

2017-01-31

Elucidating the intrinsic water wettability of the graphitic surface has increasingly attracted research interests, triggered by the recent finding that the well-established hydrophobicity of graphitic surfaces actually results from airborne hydrocarbon contamination. Currently, static water contact angle (WCA) is often used to characterize the intrinsic water wettability of graphitic surfaces. In the current paper, we show that because of the existence of defects, static WCA does not necessarily characterize the intrinsic water wettability. Freshly exfoliated graphite of varying qualities, characterized using atomic force microscopy and Raman spectroscopy, was studied using static, advancing, and receding WCA measurements. The results showed that graphite of different qualities (i.e., defect density) always has a similar advancing WCA, but it could have very different static and receding WCAs. This finding indicates that defects play an important role in contact angle measurements, and the static contact angle does not always represent the intrinsic water wettability of pristine graphite. On the basis of the experimental results, a qualitative model is proposed to explain the effect of defects on static, advancing, and receding contact angles. The model suggests that the advancing WCA reflects the intrinsic water wettability of pristine (defect-free) graphite. Our results showed that the advancing WCA for pristine graphite is 68.6°, which indicates that graphitic carbon is intrinsically mildly hydrophilic.

Graphite fiber reinforced thermoplastic resins

NASA Technical Reports Server (NTRS)

Navak, R. C.

1977-01-01

The results of a program designed to optimize the fabrication procedures for graphite thermoplastic composites are described. The properties of the composites as a function of temperature were measured and graphite thermoplastic fan exit guide vanes were fabricated and tested. Three thermoplastics were included in the investigation: polysulfone, polyethersulfone, and polyarylsulfone. Type HMS graphite was used as the reinforcement. Bending fatigue tests of HMS graphite/polyethersulfone demonstrated a gradual shear failure mode which resulted in a loss of stiffness in the specimens. Preliminary curves were generated to show the loss in stiffness as a function of stress and number of cycles. Fan exit guide vanes of HMS graphite polyethersulfone were satisfactorily fabricated in the final phase of the program. These were found to have stiffness and better fatigue behavior than graphite epoxy vanes which were formerly bill of material.

High efficiency of CO2-activated graphite felt as electrode for vanadium redox flow battery application

NASA Astrophysics Data System (ADS)

Chang, Yu-Chung; Chen, Jian-Yu; Kabtamu, Daniel Manaye; Lin, Guan-Yi; Hsu, Ning-Yih; Chou, Yi-Sin; Wei, Hwa-Jou; Wang, Chen-Hao

2017-10-01

A simple method for preparing CO2-activated graphite felt as an electrode in a vanadium redox flow battery (VRFB) was employed by the direct treatment in a CO2 atmosphere at a high temperature for a short period. The CO2-activated graphite felt demonstrates excellent electrochemical activity and reversibility. The VRFB using the CO2-activated graphite felts in the electrodes has coulombic, voltage, and energy efficiencies of 94.52%, 88.97%, and 84.15%, respectively, which is much higher than VRFBs using the electrodes of untreated graphite felt and N2-activated graphite felt. The efficiency enhancement was attributed to the higher number of oxygen-containing functional groups on the graphite felt that are formed during the CO2-activation, leading to improving the electrochemical behaviour of the resultant VRFB.

Influence of the Interaction Between Graphite and Polar Surfaces of ZnO on the Formation of Schottky Contact

NASA Astrophysics Data System (ADS)

Yatskiv, R.; Grym, J.

2018-03-01

We show that the interaction between graphite and polar surfaces of ZnO affects electrical properties of graphite/ZnO Schottky junctions. A strong interaction of the Zn-face with the graphite contact causes interface imperfections and results in the formation of laterally inhomogeneous Schottky contacts. On the contrary, high quality Schottky junctions form on the O-face, where the interaction is significantly weaker. Charge transport through the O-face ZnO/graphite junctions is well described by the thermionic emission model in both forward and reverse directions. We further demonstrate that the parameters of the graphite/ZnO Schottky diodes can be significantly improved when a thin layer of ZnO2 forms at the interface between graphite and ZnO after hydrogen peroxide surface treatment.

Thermophysical properties of graphite HOPG and HAPG in the solid state and under melting (from 2000 K up to 5000 K)

NASA Astrophysics Data System (ADS)

Savvatimskiy, A. I.; Onufriev, S. V.; Konyukhov, S. A.

2017-11-01

Experiments with HOPG graphite grade showed that the melting temperature of graphite equals 4800-4900 K and that the melting of graphite is possible only at elevated pressures. The data were obtained for resistivity, specific heat and input (Joule) energy up to 5000 K. HAPG (Highly Annealing Pyrolytic Graphite) is a form of highly oriented pyrolytic graphite. HAPG specimens in the form of strips (thickness 30 microns) were placed in a cell (between two plates of glass-sapphire). The specimen temperature was measured by a high speed pyrometer. The heat of fusion for both graphite grades (heated in a confined volume) was less (and specific heat - higher) than for the case with nearly free expansion. A possible reason for the observed effects is discussed in the report.

Modelling deformation and fracture of Gilsocarbon graphite subject to service environments

NASA Astrophysics Data System (ADS)

Šavija, Branko; Smith, Gillian E.; Heard, Peter J.; Sarakinou, Eleni; Darnbrough, James E.; Hallam, Keith R.; Schlangen, Erik; Flewitt, Peter E. J.

2018-02-01

Commercial graphites are used for a wide range of applications. For example, Gilsocarbon graphite is used within the reactor core of advanced gas-cooled reactors (AGRs, UK) as a moderator. In service, the mechanical properties of the graphite are changed as a result of neutron irradiation induced defects and porosity arising from radiolytic oxidation. In this paper, we discuss measurements undertaken of mechanical properties at the micro-length-scale for virgin and irradiated graphite. These data provide the necessary inputs to an experimentally-informed model that predicts the deformation and fracture properties of Gilsocarbon graphite at the centimetre length-scale, which is commensurate with laboratory test specimen data. The model predictions provide an improved understanding of how the mechanical properties and fracture characteristics of this type of graphite change as a result of exposure to the reactor service environment.

Pyrolytic graphite gauge for measuring heat flux

NASA Technical Reports Server (NTRS)

Bunker, Robert C. (Inventor); Ewing, Mark E. (Inventor); Shipley, John L. (Inventor)

2002-01-01

A gauge for measuring heat flux, especially heat flux encountered in a high temperature environment, is provided. The gauge includes at least one thermocouple and an anisotropic pyrolytic graphite body that covers at least part of, and optionally encases the thermocouple. Heat flux is incident on the anisotropic pyrolytic graphite body by arranging the gauge so that the gauge surface on which convective and radiative fluxes are incident is perpendicular to the basal planes of the pyrolytic graphite. The conductivity of the pyrolytic graphite permits energy, transferred into the pyrolytic graphite body in the form of heat flux on the incident (or facing) surface, to be quickly distributed through the entire pyrolytic graphite body, resulting in small substantially instantaneous temperature gradients. Temperature changes to the body can thereby be measured by the thermocouple, and reduced to quantify the heat flux incident to the body.

The graphite deposit at Borrowdale (UK): A catastrophic mineralizing event associated with Ordovician magmatism

NASA Astrophysics Data System (ADS)

Ortega, L.; Millward, D.; Luque, F. J.; Barrenechea, J. F.; Beyssac, O.; Huizenga, J.-M.; Rodas, M.; Clarke, S. M.

2010-04-01

The volcanic-hosted graphite deposit at Borrowdale in Cumbria, UK, was formed through precipitation from C-O-H fluids. The δ 13C data indicate that carbon was incorporated into the mineralizing fluids by assimilation of carbonaceous metapelites of the Skiddaw Group by andesite magmas of the Borrowdale Volcanic Group. The graphite mineralization occurred as the fluids migrated upwards through normal conjugate fractures forming the main subvertical pipe-like bodies. The mineralizing fluids evolved from CO 2-CH 4-H 2O mixtures (XCO 2 = 0.6-0.8) to CH 4-H 2O mixtures. Coevally with graphite deposition, the andesite and dioritic wall rocks adjacent to the veins were intensely hydrothermally altered to a propylitic assemblage. The initial graphite precipitation was probably triggered by the earliest hydration reactions in the volcanic host rocks. During the main mineralization stage, graphite precipitated along the pipe-like bodies due to CO 2 → C + O 2. This agrees with the isotopic data which indicate that the first graphite morphologies crystallizing from the fluid (cryptocrystalline aggregates) are isotopically lighter than those crystallizing later (flakes). Late chlorite-graphite veins were formed from CH 4-enriched fluids following the reaction CH 4 + O 2 → C + 2H 2O, producing the successive precipitation of isotopically lighter graphite morphologies. Thus, as mineralization proceeded, water-generating reactions were involved in graphite precipitation, further favouring the propylitic alteration. The structural features of the pipe-like mineralized bodies as well as the isotopic homogeneity of graphite suggest that the mineralization occurred in a very short period of time.

Solid Fuel Burning in Steady, Strained, Premixed Flow Fields: The Graphite/Air/Methane System

NASA Technical Reports Server (NTRS)

Egolfopoulos, Fokion N.; Wu, Ming-Shin (Technical Monitor)

2000-01-01

A detailed numerical investigation was conducted on the simultaneous burning of laminar premixed CH4/air flames and solid graphite in a stagnation flow configuration. The graphite and methane were chosen for this model, given that they are practical fuels and their chemical kinetics are considered as the most reliable ones among solid and hydrocarbon fuels, respectively. The simulation was performed by solving the quasi-one-dimensional equations of mass, momentum, energy, and species. The GRI 2.1 scheme was used for the gas-phase kinetics, while the heterogeneous kinetics were described by a six-step mechanism including stable and radical species. The effects of the graphite surface temperature, the gas-phase equivalence ratio, and the aerodynamic strain rate on the graphite burning rate and NO, production and destruction mechanisms were assessed. Results indicate that as the graphite temperature increases, its burning rate as well as the NO, concentration increase. Furthermore, it was found that by increasing the strain rate, the graphite burning rate increases as a result of the augmented supply of the gas-phase reactants towards the surface, while the NO, concentration decreases as a result of the reduced residence time. The effect of the equivalence ratio on both the graphite burning rate and NO, concentration was found to be non-monotonic and strongly dependent on the graphite temperature. Comparisons between results obtained for a graphite and a chemically inert surface revealed that the chemical activity of the graphite surface can result to the reduction of NO through reactions of the CH3, CH2, CH, and N radicals with NO.

Reaction rates of graphite with ozone measured by etch decoration

NASA Technical Reports Server (NTRS)

Hennig, G. R.; Montet, G. L.

1968-01-01

Etch-decoration technique of detecting vacancies in graphite has been used to determine the reaction rates of graphite with ozone in the directions parallel and perpendicular to the layer planes. It consists essentially of peeling single atom layers off graphite crystals without affecting the remainder of the crystal.

Graphite-based photovoltaic cells

DOEpatents

Lagally, Max; Liu, Feng

2010-12-28

The present invention uses lithographically patterned graphite stacks as the basic building elements of an efficient and economical photovoltaic cell. The basic design of the graphite-based photovoltaic cells includes a plurality of spatially separated graphite stacks, each comprising a plurality of vertically stacked, semiconducting graphene sheets (carbon nanoribbons) bridging electrically conductive contacts.

78 FR 56864 - Small Diameter Graphite Electrodes From the People's Republic of China: Affirmative Final...

Federal Register 2010, 2011, 2012, 2013, 2014

2013-09-16

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-929] Small Diameter Graphite... (Department) determines that imports from the People's Republic of China (PRC) of graphite electrodes... Act of 1930, as amended (the Act).\\1\\ \\1\\ See Antidumping Duty Order: Small Diameter Graphite...

New Occurrence of Shocked Graphite Aggregates at Barringer Crater

NASA Astrophysics Data System (ADS)

Miura, Y.; Noma, Y.; Iancu, O. G.

1993-07-01

High-pressure carbon minera]s are considered to be formed by solid-solid transformation under static or impact high-pressure condition, but shocked quartz aggregates of impact craters are considered to be formed by quenched accretion of various aggregates by dynamic impact process [1-3]. The main purpose of this study is to elucidate new findings and occurrences of shocked graphite (SG) aggregates [2,3] at the Barringer meteorite crater. The graphite nodule block of Barringer Crater used in this study is collected near the rim. The sample is compared with standard graphite samples of Korea, Madagascar, and artificial impact graphites. There are four different mineral aggregates of the Barringer graphite nodule sample: (1) shocked graphite-1, (2) shocked graphite-2 and hexagonal diamond in the vein, (3) shocked quartz-1 (with kamacite) in the rim, and (4) calcite in the rim (Table 1). X-ray diffraction peaks of shocked graphite reveal low X-ray intensity, high Bragg-angle shift of X-ray diffraction peak, and multiple splitting of X-ray diffraction peaks. X-ray calculated density (rho) has been determined by X-ray diffractometer by the equation of density deviation Delta rho (%) = 100 x {(rho-rho(sub)0)/rho(sub)0}, where standard density rho(sub)0 is 2.255 g/cm^3 in Korean graphite [2,3]. The high-density value of shocked graphite grain obtained in Barringer is Delta rho = +0.6 +/- 0.1%. Shocked hexagonal diamonds (chaoite) show a high value of Delta rho = +0.6 +/- 0.9%. Analytical electron microscopy data reveal three different aggregates in the graphite nodule samples (Table 1): (1) shocked graphite-1 in the matrix, which contains uniformly Fe and Ca elements formed under gas state; (2) shocked graphite-2 in the vein, where crystallized shocked graphites and hexagonal diamonds are surrounded by kamacite-rich metals formed under gas-melt states of mixed compositions from iron meteorite and target rocks; and (3) shocked quartz-1 and kamacite in the rim, where coexisted elements are supplied from kamacite, sandstone, and limestone. The shocked quartz-1 grains with high density contain Fe and Ca elements that are different from the shocked quartz-2 of pure silica [1] formed at the final stage from the Coconino sandstone. (4) Limestone in the rim is attached from Kaibab limestone. The present shocked graphites with high density are the same as artificial fine-grained shocked graphites (Delta rho = +0.7%). Table 1, which appears here in the hard copy, shows formation stages with two shocked graphites in the Barringer Crater. Formation of shocked aggregates with chemical contamination indicate dynamic accretion processes of quenching and depression at impact. The existence of two shocked graphites indicates the two formation stages of the first gas-state and the second gas-melt states with quenching processes. The origin of carbon in the shocked graphites is considered in this study to be from Kaibab limestone. References: [1] Miura Y. (1991) Shock Waves, 1, 35-41. [2] Miura Y. (1992) Proc. Shock Waves (Japan), 2, 54-57. [3] Miura Y. et al. (1993) Symp. NIPR Antarctic Meteorite (Tokyo), in press. [4] Foote A. E. (1891) Am. J. Sci., 42, 413-417. [5] Hannemann R. E. et al. (1967) Science, 155, 995-997.

Thermal Conductivity of Polyimide/Carbon Nanofiller Blends

NASA Technical Reports Server (NTRS)

Ghose, S.; Watson, K. A.; Delozier, D. M.; Working, D. C.; Connell, J. W.; Smith, J. G.; Sun, Y. P.; Lin, Y.

2007-01-01

In efforts to improve the thermal conductivity (TC) of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

A "Tandem" Strategy to Fabricate Flexible Graphene/Polypyrrole Nanofiber Film Using the Surfactant-Exfoliated Graphene for Supercapacitors.

PubMed

Shu, Kewei; Chao, Yunfeng; Chou, Shulei; Wang, Caiyun; Zheng, Tian; Gambhir, Sanjeev; Wallace, Gordon G

2018-06-19

The surfactant-assisted liquid-phase exfoliation of expanded graphite can produce graphene sheets in large quantities with minimal defects. However, it is difficult to completely remove the surfactant from the final product, thus affecting the electrochemical properties of the produced graphene. In this article, a novel approach to fabricate flexible graphene/polypyrrole film was developed: using surfactant cetyltrimethylammonium bromide as a template for growth of polypyrrole nanofibers (PPyNFs) instead of removal after the exfoliation process; followed by a simple filtration method. The introduction of PPyNF not only increases the electrochemical performance, but also ensures flexibility. This composite film electrode offers a capacitance up to 161 F g -1 along with a capacitance retention rate of over 80% after 5000 cycles.

Thermal Conductivity of Polyimide/Nanofiller Blends

NASA Technical Reports Server (NTRS)

Ghose, S.; Watson, K. A.; Delozier, D. M.; Working, D. c.; Connell, J. W.; Smith, J. G.; Sun, Y. P.; Lin, Y.

2006-01-01

In efforts to improve the thermal conductivity of Ultem(TM) 1000, it was compounded with three carbon based nano-fillers. Multiwalled carbon nanotubes (MWCNT), vapor grown carbon nanofibers (CNF) and expanded graphite (EG) were investigated. Ribbons were extruded to form samples in which the nano-fillers were aligned. Samples were also fabricated by compression molding in which the nano-fillers were randomly oriented. The thermal properties were evaluated by DSC and TGA, and the mechanical properties of the aligned samples were determined by tensile testing. The degree of dispersion and alignment of the nanoparticles were investigated with high-resolution scanning electron microscopy. The thermal conductivity of the samples was measured in both the direction of alignment as well as perpendicular to that direction using the Nanoflash technique. The results of this study will be presented.

Compliant high temperature seals for dissimilar materials

DOEpatents

Rynders, Steven Walton; Minford, Eric; Tressler, Richard Ernest; Taylor, Dale M.

2001-01-01

A high temperature, gas-tight seal is formed by utilizing one or more compliant metallic toroidal ring sealing elements, where the applied pressure serves to activate the seal, thus improving the quality of the seal. The compliant nature of the sealing element compensates for differences in thermal expansion between the materials to be sealed, and is particularly useful in sealing a metallic member and a ceramic tube art elevated temperatures. The performance of the seal may be improved by coating the sealing element with a soft or flowable coating such as silver or gold and/or by backing the sealing element with a bed of fine powder. The material of the sealing element is chosen such that the element responds to stress elastically, even at elevated temperatures, permitting the seal to operate through multiple thermal cycles.

Seal Related Development Activities at EG/G

NASA Technical Reports Server (NTRS)

Greiner, Harold F.

1991-01-01

Seal related development activities including modeling, analysis, and performance testing are described for several current seal related projects. Among the current seal related projects are the following: high pressure gas sealing systems for turbomachinery; brush seals for gas path sealing in gas turbines; and tribological material evaluation for wear surfaces in sealing systems.

Pressure Actuated Leaf Seals for Improved Turbine Shaft Sealing

NASA Technical Reports Server (NTRS)

Grondahl, Clayton

2006-01-01

This presentation introduces a shaft seal in which leaf seal elements are constructed from slotted shim material formed and layered into a frusto-conical assembly. Limited elastic deflection of seal leaves with increasing system pressure close large startup clearance to a small, non-contacting, steady state running clearance. At shutdown seal elements resiliently retract as differential seal pressure diminishes. Large seal clearance during startup and shutdown provides a mechanism for rub avoidance. Minimum operating clearance improves performance and non-contacting operation promises long seal life. Design features of this seal, sample calculations at differential pressures up to 2400 psid and benefit comparison with brush and labyrinth seals is documented in paper, AIAA 2005 3985, presented at the Advanced Seal Technology session of the Joint Propulsion Conference in Tucson this past July. In this presentation use of bimetallic leaf material will be discussed. Frictional heating of bimetallic leaf seals during a seal rub can relieve the rub condition to some extent with a change in seal shape. Improved leaf seal rub tolerance is expected with bimetallic material.

High-temperature, high-pressure bonding of nested tubular metallic components

DOEpatents

Quinby, Thomas C.

1980-01-01

This invention is a tool for effecting high-temperature, high-compression bonding between the confronting faces of nested, tubular, metallic components. In a typical application, the tool is used to produce tubular target assemblies for irradiation in nuclear reactors or particle accelerators, the target assembly comprising a uranium foil and an aluminum-alloy substrate. The tool preferably is composed throughout of graphite. It comprises a tubular restraining member in which a mechanically expandable tubular core is mounted to form an annulus with the member. The components to be bonded are mounted in nested relation in the annulus. The expandable core is formed of individually movable, axially elongated segments whose outer faces cooperatively define a cylindrical pressing surface and whose inner faces cooperatively define two opposed, inwardly tapered, axial bores. Tapered rams extend respectively into the bores. The loaded tool is mounted in a conventional hot-press provided with evacuation means, heaters for maintaining its interior at bonding temperature, and hydraulic cylinders for maintaining a selected inwardly directed pressure on the tapered rams. With the hot-press evacuated and the loaded tool at the desired temperature, the cylinders are actuated to apply the selected pressure to the rams. The rams in turn expand the segmented core to maintain the nested components in compression against the restraining member. These conditions are maintained until the confronting faces of the nested components are joined in a continuous, uniform bond characterized by high thermal conductivity.

A Comparison of Candidate Seal Designs for Future Docking Systems

NASA Technical Reports Server (NTRS)

Dunlap, Patrick, H., Jr.; Steinetz, Bruce, M.

2012-01-01

NASA is developing a new docking system to support future space exploration missions to low Earth orbit, the Moon, and other destinations. A key component of this system is the seal at the main docking interface which inhibits the loss of cabin air once docking is complete. Depending on the mission, the seal must be able to dock in either a seal-on-flange or seal-on-seal configuration. Seal-on-flange mating would occur when a docking system equipped with a seal docks to a system with a flat metal flange. This would occur when a vehicle docks to a node on the International Space Station. Seal-on-seal mating would occur when two docking systems equipped with seals dock to each other. Two types of seal designs were identified for this application: Gask-O-seals and multi-piece seals. Both types of seals had a pair of seal bulbs to satisfy the redundancy requirement. A series of performance assessments and comparisons were made between the candidate seal designs indicating that they meet the requirements for leak rate and compression and adhesion loads under a range of operating conditions. Other design factors such as part count, integration into the docking system tunnel, seal-on-seal mating, and cost were also considered leading to the selection of the multi-piece seal design for the new docking system. The results of this study can be used by designers of future docking systems and other habitable volumes to select the seal design best-suited for their particular application.

Low temperature vapor phase digestion of graphite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pierce, Robert A.

2017-04-18

A method for digestion and gasification of graphite for removal from an underlying surface is described. The method can be utilized to remove graphite remnants of a formation process from the formed metal piece in a cleaning process. The method can be particularly beneficial in cleaning castings formed with graphite molding materials. The method can utilize vaporous nitric acid (HNO.sub.3) or vaporous HNO.sub.3 with air/oxygen to digest the graphite at conditions that can avoid damage to the underlying surface.

The Fracture Toughness of Nuclear Graphites Grades

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burchell, Timothy D.; Erdman, III, Donald L.; Lowden, Rick R.

2017-04-01

New measurements of graphite mode I critical stress intensity factor, KIc (commonly referred to as the fracture toughness) and the mode II critical shear stress intensity, KIIc, are reported and compared with prior data for KIc and KIIc. The new data are for graphite grades PCEA, IG-110 and 2114. Variations of KIc and acoustic emission (AE) data with graphite texture are reported and discussed. The Codes and Standards applications of fracture toughness, KIc, data are also discussed. A specified minimum value for nuclear graphite KIc is recommended.

AC induction field heating of graphite foam

DOE Office of Scientific and Technical Information (OSTI.GOV)

Klett, James W.; Rios, Orlando; Kisner, Roger

A magneto-energy apparatus includes an electromagnetic field source for generating a time-varying electromagnetic field. A graphite foam conductor is disposed within the electromagnetic field. The graphite foam when exposed to the time-varying electromagnetic field conducts an induced electric current, the electric current heating the graphite foam. An energy conversion device utilizes heat energy from the heated graphite foam to perform a heat energy consuming function. A device for heating a fluid and a method of converting energy are also disclosed.

PROCESS OF COATING GRAPHITE WITH NIOBIUM-TITANIUM CARBIDE

DOEpatents

Halden, F.A.; Smiley, W.D.; Hruz, F.M.

1961-07-01

A process of coating graphite with niobium - titanium carbide is described. It is found that the addition of more than ten percent by weight of titanium to niobium results in much greater wetting of the graphite by the niobium and a much more adherent coating. The preferred embodiment comprises contacting the graphite with a powdered alloy or mixture, degassing simultaneously the powder and the graphite, and then heating them to a high temperature to cause melting, wetting, spreading, and carburization of the niobium-titanium powder.

Design and fabrication of a long-life Stirling cycle cooler for space application. Phase 3: Prototype model. Final Report, Sep. 1981 - Sep. 1990

DOE Office of Scientific and Technical Information (OSTI.GOV)

Keung, C.; Patt, P.J.; Starr, M.

A second-generation, Stirling-cycle cryocooler (cryogenic refrigerator) for space applications, with a cooling capacity of 5 watts at 65 K, was recently completed. The refrigerator, called the Prototype Model, was designed with a goal of 5 year life with no degradation in cooling performance. The free displacer and free piston of the refrigerator are driven directly by moving-magnet linear motors with the moving elements supported by active magnetic bearings. The use of clearance seals and the absence of outgassing material in the working volume of the refrigerator enable long-life operation with no deterioration in performance. Fiber-optic sensors detect the radial positionmore » of the shafts and provide a control signal for the magnetic bearings. The frequency, phase, stroke, and offset of the compressor and expander are controlled by signals from precision linear position sensors (LVDTs). The vibration generated by the compressor and expander is cancelled by an active counter balance which also uses a moving-magnet linear motor and magnetic bearings. The driving signal for the counter balance is derived from the compressor and expander position sensors which have wide bandwidth for suppression of harmonic vibrations. The efficiency of the three active members, which operate in a resonant mode, is enhanced by a magnetic spring in the expander and by gas springs in the compressor and counterbalance. The cooling was achieved with a total motor input power of 139 watts. The magnetic-bearing stiffness was significantly increased from the first-generation cooler to accommodate shuttle launch vibrations.« less

Design and fabrication of a long-life Stirling cycle cooler for space application. Phase 3: Prototype model

NASA Technical Reports Server (NTRS)

Keung, C.; Patt, P. J.; Starr, M.; Sweet, R. C.; Bourdillon, L. A.; Figueroa, R.; Hartmann, M.; Mcfarlane, R.

1990-01-01

A second-generation, Stirling-cycle cryocooler (cryogenic refrigerator) for space applications, with a cooling capacity of 5 watts at 65 K, was recently completed. The refrigerator, called the Prototype Model, was designed with a goal of 5 year life with no degradation in cooling performance. The free displacer and free piston of the refrigerator are driven directly by moving-magnet linear motors with the moving elements supported by active magnetic bearings. The use of clearance seals and the absence of outgassing material in the working volume of the refrigerator enable long-life operation with no deterioration in performance. Fiber-optic sensors detect the radial position of the shafts and provide a control signal for the magnetic bearings. The frequency, phase, stroke, and offset of the compressor and expander are controlled by signals from precision linear position sensors (LVDTs). The vibration generated by the compressor and expander is cancelled by an active counter balance which also uses a moving-magnet linear motor and magnetic bearings. The driving signal for the counter balance is derived from the compressor and expander position sensors which have wide bandwidth for suppression of harmonic vibrations. The efficiency of the three active members, which operate in a resonant mode, is enhanced by a magnetic spring in the expander and by gas springs in the compressor and counterbalance. The cooling was achieved with a total motor input power of 139 watts. The magnetic-bearing stiffness was significantly increased from the first-generation cooler to accommodate shuttle launch vibrations.

Late-time particle emission from laser-produced graphite plasma

NASA Astrophysics Data System (ADS)

Harilal, S. S.; Hassanein, A.; Polek, M.

2011-09-01

We report a late-time "fireworks-like" particle emission from laser-produced graphite plasma during its evolution. Plasmas were produced using graphite targets excited with 1064 nm Nd: yttrium aluminum garnet (YAG) laser in vacuum. The time evolution of graphite plasma was investigated using fast gated imaging and visible emission spectroscopy. The emission dynamics of plasma is rapidly changing with time and the delayed firework-like emission from the graphite target followed a black-body curve. Our studies indicated that such firework-like emission is strongly depended on target material properties and explained due to material spallation caused by overheating the trapped gases through thermal diffusion along the layer structures of graphite.

Fire test method for graphite fiber reinforced plastics

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1980-01-01

A potential problem in the use of graphite fiber reinforced resin matrix composites is the dispersal of graphite fibers during accidental fires. Airborne, electrically conductive fibers originating from the burning composites could enter and cause shorting in electrical equipment located in surrounding areas. A test method for assessing the burning characteristics of graphite fiber reinforced composites and the effectiveness of the composites in retaining the graphite fibers has been developed. The method utilizes a modified Ohio State University Rate of Heat Release apparatus. The equipment and the testing procedure are described. The application of the test method to the assessment of composite materials is illustrated for two resin matrix/graphite composite systems.

Twist seal for high-pressure vessels such as space shuttle rocket motors

NASA Technical Reports Server (NTRS)

von Pragenau, George L. (Inventor)

1989-01-01

Seals for sealing clevis and flange joints (14) of a solid rocket booster motor, and more particularly to a seal (30) which is twisted upon application of expansion forces to an edge seal (36). This twisting motion initially causes a leading edge seal (44) to be urged into sealing engagement with a surface (48) of an adjacent member (20) and thereafter, increasing fluid pressure on a pressurized side (64) of a seal (30) drives a broad sealing region (46) into sealing engagement with a surface (48).

Hypersonic engine seal development at NASA Lewis Research Center

NASA Technical Reports Server (NTRS)

Steinetz, Bruce M.

1994-01-01

NASA Lewis Research Center is developing advanced seal concepts and sealing technology for advanced combined cycle ramjet/scramjet engines being designed for the National Aerospace Plane (NASP). Technologies are being developed for both the dynamic seals that seal the sliding interfaces between articulating engine panels and sidewalls, and for the static seals that seal the heat exchanger to back-up structure interfaces. This viewgraph presentation provides an overview of the candidate engine seal concepts, seal material assessments, and unique test facilities used to assess the leakage and thermal performance of the seal concepts.

Brush seals for turbine engine fuel conservation

NASA Astrophysics Data System (ADS)

Sousa, Mike

1994-07-01

The program objective is to demonstrate brush seals for replacing labyrinth seals in turboprop engines. The approach taken was to design and procure brush seals with assistance from Sealol, modify and instrument an existing T407 low pressure turbine test rig, replace inner balance piston and outer balance piston labyrinth seals with brush seals, conduct cyclic tests to evaluate seal leakage at operating pressures and temperatures, and evaluate effect of seal pack width and rotor eccentricity. Results are presented in viewgraph format and show that brush seals offer performance advantages over labyrinth seals.

Development of advanced seals for space propulsion turbomachinery

NASA Technical Reports Server (NTRS)

Hendricks, R. C.; Liang, A. D.; Childs, D. W.; Proctor, M. P.

1992-01-01

Current activities in seals for space propulsion turbomachinery that the NASA Lewis Research Center sponsors are surveyed. The overall objective is to provide the designer and researcher with the concepts and the data to control seal dynamics and leakage. Included in the program are low-leakage seals, such as the brush seal, the 'ceramic rope' seal, low-leakage seals for liquid oxygen turbopumps, face seals for two phase flow, and swirl brakes for stability. Two major efforts are summarized: a seal dynamics in rotating machinery and an effort in seal code development.

Hypersonic engine seal development at NASA Lewis Research Center

NASA Astrophysics Data System (ADS)

Steinetz, Bruce M.

1994-07-01

NASA Lewis Research Center is developing advanced seal concepts and sealing technology for advanced combined cycle ramjet/scramjet engines being designed for the National Aerospace Plane (NASP). Technologies are being developed for both the dynamic seals that seal the sliding interfaces between articulating engine panels and sidewalls, and for the static seals that seal the heat exchanger to back-up structure interfaces. This viewgraph presentation provides an overview of the candidate engine seal concepts, seal material assessments, and unique test facilities used to assess the leakage and thermal performance of the seal concepts.

Design and development of high efficiency 140W space TWT with graphite collector

NASA Astrophysics Data System (ADS)

Srivastava, V.; Purohit, G.; Sharma, R. K.; Sharma, S. M.; Bera, A.; Bhaskar, P. V.; Singh, R. R.; Prasad, K.; Kiran, V.

2008-05-01

4-stage graphite collector assembly has been designed and developed for a 140W Ku-band space TWT to achieve the collector efficiency more than 80%. The UHV compatible, high density, copper impregnated POCO graphite (DFP-1C) was used to fabricate the four collector electrodes of the 4-stage depressed collector. Copper impregnated graphite material is used for the collector electrodes because of its low secondary electron emission coefficient, high thermal and electrical conductivities, easy machining and brazing, low thermal expansion coefficient and low weight. The graphite material was characterized for the UHV compatibility. The collector electrodes were precisely fabricated by careful machining, and technology was developed for brazing of graphite electrodes with high voltage alumina insulators. Complete TWT with four-stage graphite collector was developed and 140W output power at gain more than 55 dB was achieved. The TWT was pumped from both the gun and the collector ends.

Development of design data for graphite reinforced epoxy and polyimide composites

NASA Technical Reports Server (NTRS)

Scheck, W. G.

1974-01-01

Processing techniques and design data were characterized for a graphite/epoxy composite system that is useful from 75 K to 450 K, and a graphite/polyimide composite system that is useful from 75 K to 589 K. The Monsanto 710 polyimide resin was selected as the resin to be characterized and used with the graphite fiber reinforcement. Material was purchased using the prepreg specification for the design data generation for both the HT-S/710 and HM-S/710 graphite/polyimide composite system. Lamina and laminate properties were determined at 75 K, 297 K, and 589 K. The test results obtained on the skin-stringer components proved that graphite/polyimide composites can be reliably designed and analyzed much like graphite/epoxy composites. The design data generated in the program includes the standard static mechanical properties, biaxial strain data, creep, fatigue, aging, and thick laminate data.

Chemical stabilization of graphite surfaces

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bistrika, Alexander A.; Lerner, Michael M.

Embodiments of a device, or a component of a device, including a stabilized graphite surface, methods of stabilizing graphite surfaces, and uses for the devices or components are disclosed. The device or component includes a surface comprising graphite, and a plurality of haloaryl ions and/or haloalkyl ions bound to at least a portion of the graphite. The ions may be perhaloaryl ions and/or perhaloalkyl ions. In certain embodiments, the ions are perfluorobenzenesulfonate anions. Embodiments of the device or component including stabilized graphite surfaces may maintain a steady-state oxidation or reduction surface current density after being exposed to continuous oxidation conditionsmore » for a period of at least 1-100 hours. The device or component is prepared by exposing a graphite-containing surface to an acidic aqueous solution of the ions under oxidizing conditions. The device or component can be exposed in situ to the solution.« less

Development of CIP/graphite composite additives for electromagnetic wave absorption applications

NASA Astrophysics Data System (ADS)

Woo, Soobin; Yoo, Chan-Sei; Kim, Hwijun; Lee, Mijung; Quevedo-Lopez, Manuel; Choi, Hyunjoo

2017-09-01

In this study, the electromagnetic (EM) wave absorption ability of carbonyl iron powder (CIP)/graphite composites produced by ball milling were studied in a range of 28.5 GHz to examine the effects of the morphology and volume fraction of graphite on EM wave absorption ability. The results indicated that a ball milling technique was effective in exfoliating the graphite and covering it with CIP, thereby markedly increasing the specific surface area of the hybrid powder. The increase in the surface area and hybridization with dielectric loss materials (i.e., graphite) improved EM absorbing properties of CIP in the range of S and X bands. Specifically, the CIP/graphite composite containing 3 wt% graphite exhibited electromagnetic wave absorption of -13 dB at 7 GHz, -21 dB at 5.8 GHz, and -29 dB at 4.3 GHz after 1 h, 8 h, and 16 h of milling, respectively. [Figure not available: see fulltext.

Friction and wear of metals in contact with pyrolytic graphite

NASA Technical Reports Server (NTRS)

Buckley, D. H.; Brainard, W. A.

1975-01-01

Sliding friction experiments were conducted with gold, iron, and tantalum single crystals sliding on prismatic and basal orientations of pyrolytic graphite in various environments, including vacuum, oxygen, water vapor, nitrogen, and hydrogen bromide. Surfaces were examined in the clean state and with various adsorbates present on the graphite surfaces. Auger and LEED spectroscopy, SEM, and EDXA were used to characterize the graphite surfaces. Results indicate that the prismatic and basal orientations do not contain nor do they chemisorb oxygen, water vapor, acetylene, or hydrogen bromide. All three metals exhibited higher friction on the prismatic than on the basal orientation and these metals transferred to the atomically clean prismatic orientation of pyrolytic graphite. No metal transfer to the graphite was observed in the presence of adsorbates at 760 torr. Ion bombardment of the graphite surface with nitrogen ions resulted in the adherence of nitrogen to the surface.

Formation mechanism of graphite hexagonal pyramids by argon plasma etching of graphite substrates

NASA Astrophysics Data System (ADS)

Glad, X.; de Poucques, L.; Bougdira, J.

2015-12-01

A new graphite crystal morphology has been recently reported, namely the graphite hexagonal pyramids (GHPs). They are hexagonally-shaped crystals with diameters ranging from 50 to 800 nm and a constant apex angle of 40°. These nanostructures are formed from graphite substrates (flexible graphite and highly ordered pyrolytic graphite) in low pressure helicon coupling radiofrequency argon plasma at 25 eV ion energy and, purportedly, due to a physical etching process. In this paper, the occurrence of peculiar crystals is shown, presenting two hexagonal orientations obtained on both types of samples, which confirms such a formation mechanism. Moreover, by applying a pretreatment step with different time durations of inductive coupling radiofrequency argon plasma, for which the incident ion energy decreases at 12 eV, uniform coverage of the surface can be achieved with an influence on the density and size of the GHPs.

Tuning graphitic oxide for initiator- and metal-free aerobic epoxidation of linear alkenes

NASA Astrophysics Data System (ADS)

Pattisson, Samuel; Nowicka, Ewa; Gupta, Upendra N.; Shaw, Greg; Jenkins, Robert L.; Morgan, David J.; Knight, David W.; Hutchings, Graham J.

2016-09-01

Graphitic oxide has potential as a carbocatalyst for a wide range of reactions. Interest in this material has risen enormously due to it being a precursor to graphene via the chemical oxidation of graphite. Despite some studies suggesting that the chosen method of graphite oxidation can influence the physical properties of the graphitic oxide, the preparation method and extent of oxidation remain unresolved for catalytic applications. Here we show that tuning the graphitic oxide surface can be achieved by varying the amount and type of oxidant. The resulting materials differ in level of oxidation, surface oxygen content and functionality. Most importantly, we show that these graphitic oxide materials are active as unique carbocatalysts for low-temperature aerobic epoxidation of linear alkenes in the absence of initiator or metal. An optimum level of oxidation is necessary and materials produced via conventional permanganate-based methods are far from optimal.

Construction and performance evaluation of mediator-less microbial fuel cell using carbon nanotubes as an anode material.

PubMed

Roh, Sung-Hee; Kim, Sun-Il

2012-05-01

A microbial fuel cell (MFC) is a device that converts chemical energy to electrical energy using the catalytic reaction of microorganisms. We investigated the performance of mediator-less MFC with carbon nanotubes (CNTs)/graphite felt composite electrodes. The addition of CNTs to a graphite felt electrode increases the specific surface area of the electrode and enhances the charge transfer capability so as to cause considerable improvement of the electrochemical activity for the anode reaction in a MFC. The performance of the MFC using CNTs/graphite felt electrode has been compared against a plain graphite felt electrode based MFC. A CNTs/graphite felt electrode showed as high as 15% increase in the power density (252 mW/m2) compared to graphite felt electrode (214 mW/m2). The CNTs/graphite felt anode therefore offers good prospects for application in MFCs.

Method of making segmented pyrolytic graphite sputtering targets

DOEpatents

McKernan, Mark A.; Alford, Craig S.; Makowiecki, Daniel M.; Chen, Chih-Wen

1994-01-01

Anisotropic pyrolytic graphite wafers are oriented and bonded together such that the graphite's high thermal conductivity planes are maximized along the back surface of the segmented pyrolytic graphite target to allow for optimum heat conduction away from the sputter target's sputtering surface and to allow for maximum energy transmission from the target's sputtering surface.

76 FR 36092 - Small Diameter Graphite Electrodes From the People's Republic of China: Extension of Time Limit...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-06-21

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-929] Small Diameter Graphite... antidumping duty order on small diameter graphite electrodes from the People's Republic of China (``PRC'') for... preliminary results of this review were published on March 7, 2011. See Small Diameter Graphite Electrodes...

77 FR 6060 - Small Diameter Graphite Electrodes from the People's Republic of China: Extension of Time Limit...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-02-07

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-929] Small Diameter Graphite... Department) initiated an administrative review of the antidumping duty order on small diameter graphite... preliminary results of this review by 95 days until February 3, 2012. See Small Diameter Graphite Electrodes...

76 FR 67411 - Small Diameter Graphite Electrodes From the People's Republic of China: Extension of Time Limit...

Federal Register 2010, 2011, 2012, 2013, 2014

2011-11-01

... DEPARTMENT OF COMMERCE International Trade Administration [A-570-929] Small Diameter Graphite... diameter graphite electrodes from the People's Republic of China (PRC) for the period February 1, 2010... Graphite, Co. The preliminary results of the review are currently due no later than October 31, 2011...

Quenchable compressed graphite synthesized from neutron-irradiated highly oriented pyrolytic graphite in high pressure treatment at 1500 °C

NASA Astrophysics Data System (ADS)

Niwase, Keisuke; Terasawa, Mititaka; Honda, Shin-ichi; Niibe, Masahito; Hisakuni, Tomohiko; Iwata, Tadao; Higo, Yuji; Hirai, Takeshi; Shinmei, Toru; Ohfuji, Hiroaki; Irifune, Tetsuo

2018-04-01

The super hard material of "compressed graphite" (CG) has been reported to be formed under compression of graphite at room temperature. However, it returns to graphite under decompression. Neutron-irradiated graphite, on the other hand, is a unique material for the synthesis of a new carbon phase, as reported by the formation of an amorphous diamond by shock compression. Here, we investigate the change of structure of highly oriented pyrolytic graphite (HOPG) irradiated with neutrons to a fluence of 1.4 × 1024 n/m2 under static pressure. The neutron-irradiated HOPG sample was compressed to 15 GPa at room temperature and then the temperature was increased up to 1500 °C. X-ray diffraction, high-resolution transmission electron microscopy on the recovered sample clearly showed the formation of a significant amount of quenchable-CG with ordinary graphite. Formation of hexagonal and cubic diamonds was also confirmed. The effect of irradiation-induced defects on the synthesis of quenchable-CG under high pressure and high temperature treatment was discussed.

A Study on Effect of Graphite Particles on Tensile, Hardness and Machinability of Aluminium 8011 Matrix Material

NASA Astrophysics Data System (ADS)

Latha Shankar, B.; Anil, K. C.; Karabasappagol, Prasann J.

2016-09-01

Industrial application point of view, metal matrix composites in general and Aluminium alloy matrix composites in particular are ideal candidates because of their favourable engineering properties. Being lightweight Aluminium matrix composites are widely used in aircraft, defence and automotive industries. In this work Aluminium 8011 metal matrix was reinforced with fine Graphite particles of 50 μm. developed by two-step Stir casting method. Graphite weight %was varied in the range 2, 4, 6 and 8%. Uniform dispersion of graphite particle is examined under optical microscope. Tensile test coupons were prepared as per standard to determine % of elongation and tensile strength for various % of graphite particle. Hardness of developed composite for various % of graphite particle and Machinability parameters were also studied for effect on surface finish. It was observed that with increase of weight percentage of Graphite particles up to 8% in Aluminium 8011 alloy matrix there was increase in tensile strength, decrease in % of elongation with increase in hardness. Machinability study revealed that, there was decrease in surface roughness with increase in Graphite content.

Enhancement of oxidation resistance of graphite foams by polymer derived-silicon carbide coating for concentrated solar power applications

DOE PAGES

Kim, T.; Singh, D.; Singh, M.

2015-05-01

Graphite foam with extremely high thermal conductivity has been investigated to enhance heat transfer of latent heat thermal energy storage (LHTES) systems. However, the use of graphite foam for elevated temperature applications (>600 °C) is limited due to poor oxidation resistance of graphite. In the present study, oxidation resistance of graphite foam coated with silicon carbide (SiC) was investigated. A pre-ceramic polymer derived coating (PDC) method was used to form a SiC coating on the graphite foams. Post coating deposition, the samples were analyzed by scanning electron microscopy and energy dispersive spectroscopy. The oxidation resistance of PDC-SiC coating was quantifiedmore » by measuring the weight of the samples at several measuring points. The experiments were conducted under static argon atmosphere in a furnace. After the experiments, oxidation rates (%/hour) were calculated to predict the lifetime of the graphite foams. The experimental results showed that the PDC-SiC coating could prevent the oxidation of graphite foam under static argon atmosphere up to 900 °C.« less

Effects of sequential treatment with fluorine and bromine on graphite fibers

NASA Technical Reports Server (NTRS)

Hung, Ching-Cheh; Stahl, Mark; Maciag, Carolyn; Slabe, Melissa

1987-01-01

Three pitch based graphite fibers with different degrees of graphitization and one polyacryonitrile (PAN) based carbon fiber from Amoco Corporation were treated with 1 atm, room temperature fluorine gas for 90 hrs. Fluorination resulted in higher electrical conductivity for all pitch fibers. Further bromination after ambient condition defluorination resulted in further increases in electrical defluorination conductivity for less graphitized, less structurally ordered pitch fibers (P-55) which contain about 3% fluorine by weight before bromination. This product can be stable in 200 C air, or 100% humidity at 60 C. Due to its low cost, this less graphitized fiber may be useful for industrial application, such as airfoil deicer materials. The same bromination process, however, resulted in conductivity decreases for fluorine rich, more graphitized, structurally oriented pitch fibers (P-100 and P-75). Such decreases in electrical conductivity were partially reversed by heating the fibers at 185 C in air. Differential scanning calorimetric (DSC) data indicated that the more graphitized fibers (P-100) contained BrF3, whereas the less graphitized fibers (P-55) did not.

Approaches to Deal with Irradiated Graphite in Russia - Proposal for New IAEA CRP on Graphite Waste Management - 12364

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kascheev, Vladimir; Poluektov, Pavel; Ustinov, Oleg

The problems of spent reactor graphite are being shown, the options of its disposal is considered. Burning method is selected as the most efficient and waste-free. It is made a comparison of amounts of {sup 14}C that entering the environment in a natural way during the operation of nuclear power plants (NPPs) and as a result of the proposed burning of spent reactor graphite. It is shown the possibility of burning graphite with the arrival of {sup 14}C into the atmosphere within the maximum allowable emissions. This paper analyzes the different ways of spent reactor graphite treatment. It is shownmore » the possibility of its reprocessing by burning method in the air flow. It is estimated the effect of this technology to the overall radiation environment and compared its contribution to the general background radiation due to cosmic radiation and NPPs emission. It is estimated the maximum permissible speeds of burning reactor graphite (for example, RBMK graphite) for areas with different conditions of agricultural activities. (authors)« less

76 FR 43266 - Marine Mammals; File No. 16472

Federal Register 2010, 2011, 2012, 2013, 2014

2011-07-20

... (Lobodon carcinophagus), leopard seals (Hydrurga leptonyx), Ross seals (Ommatophoca rossii), and Weddell... monitoring program established in 1986. The applicant also requests permission to import tissue samples... seals, 100 crabeater seals, 100 leopard seals, 200 Weddell seals, and 5 Ross seals would be taken...