Reflow-oven-processing of pressureless sintered-silver interconnects

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wereszczak, Andrew A.; Chen, Branndon R.; Oistad, Brian A.

Here, a method was developed to pressurelessly fabricate strong and consistent sinterable-silver joints or interconnects using reflow oven heating. Circular sinterable-silver interconnects, having nominal diameter of 5 mm and 0.1 mm thickness were stencil printed, contact-dried, and then pressurelessly sinter-bonded to Au-plated direct copper bonded ceramic substrates at 250 °C in ambient air. That sintering was done in either a reflow oven or a convective oven (latter being a conventional heating source for processing sinterable-silver). Consistently strong (>40 MPa) interconnects were produced with reflow oven heating and were as strong as those produced with convective oven heating. This is significantmore » because reflow oven technology affords better potential for continuous mass production and it was shown that strong sintered-silver bonds can indeed be achieved with its use.« less

Reflow-oven-processing of pressureless sintered-silver interconnects

DOE PAGES

Wereszczak, Andrew A.; Chen, Branndon R.; Oistad, Brian A.

2018-01-04

Here, a method was developed to pressurelessly fabricate strong and consistent sinterable-silver joints or interconnects using reflow oven heating. Circular sinterable-silver interconnects, having nominal diameter of 5 mm and 0.1 mm thickness were stencil printed, contact-dried, and then pressurelessly sinter-bonded to Au-plated direct copper bonded ceramic substrates at 250 °C in ambient air. That sintering was done in either a reflow oven or a convective oven (latter being a conventional heating source for processing sinterable-silver). Consistently strong (>40 MPa) interconnects were produced with reflow oven heating and were as strong as those produced with convective oven heating. This is significantmore » because reflow oven technology affords better potential for continuous mass production and it was shown that strong sintered-silver bonds can indeed be achieved with its use.« less

Improvements to Zirconia Thick-Film Oxygen Sensors

NASA Astrophysics Data System (ADS)

Maskell, William C.; Brett, Daniel J. L.; Brandon, Nigel P.

2013-06-01

Thick-film zirconia gas sensors are normally screen-printed onto a planar substrate. A sandwich of electrode-electrolyte-electrode is fired at a temperature sufficient to instigate sintering of the zirconia electrolyte. The resulting porous zirconia film acts as both the electrolyte and as the diffusion barrier through which oxygen diffuses. The high sintering temperature results in de-activation of the electrodes so that sensors must be operated at around 800 °C for measurements in the percentage range of oxygen concentration. This work shows that the use of cobalt oxide as a sintering aid allows reduction of the sensor operating temperature by 100-200 °C with clear benefits. Furthermore, an interesting and new technique is presented for the investigation of the influence of dopants and of the through-porosity of ionically-conducting materials.

Mechanical characterization and durability of sintered porous transport layers for polymer electrolyte membrane electrolysis

NASA Astrophysics Data System (ADS)

Borgardt, Elena; Panchenko, Olha; Hackemüller, Franz Josef; Giffin, Jürgen; Bram, Martin; Müller, Martin; Lehnert, Werner; Stolten, Detlef

2018-01-01

Differential pressure electrolysis offers the potential for more efficient hydrogen compression. Due to the differential pressures acting within the electrolytic cell, the porous transport layer (PTL) is subjected to high stress. For safety reasons, the PTL's mechanical stability must be ensured. However, the requirements for high porosity and low thickness stand in contrast to that for mechanical stability. Porous transport layers for polymer electrolyte membrane (PEM) electrolysis are typically prepared by means of the thermal sintering of titanium powder. Thus far, the factors that influence the mechanical strength of the sintered bodies and how all requirements can be simultaneously fulfilled have not been investigated. Here, the static and dynamic mechanical properties of thin sintered titanium sheets are investigated ex-situ via tensile tests and periodic loading in a test cell, respectively. In order for a sintered PTL with a thickness of 500 μm and porosities above 25% to be able to withstand 50 bar differential pressure in the cell, the maximum flow field width should be limited to 3 mm. Thus, a method was developed to test the suitability of PTL materials for use in electrolysis for various differential pressures and flow field widths.

[Effect of repeated sintering and variations in thickness on the color and microstructure of dental lithium disilicate-based glass ceramic veneers].

PubMed

Cui, Huang; Jia, Yu; Shaofeng, Meng; Biyun, Gao

2017-08-01

Objective The aim of this study is to evaluate the effect of repeated sintering and variation in thickness on the color and microstructure of dental lithium disilicate-based glass ceramic veneers. Methods A total of 24 computer aided design and computer aided manufacturing (CAD/CAM) veneers was fabricated using the IPS e.max-CAD LS2 and then randomly divided into four groups (S0, S1, S2, S3; n=6). Each group was sintered 0, 1, 2, 3 times individually according to the manufacturer's recommendation. The color parameters (L, C, H, a, b values) of all the specimens were measured by a Vita easyshade dental colorimeter. The results were statistically analyzed using the SAS 9.1.3 software for MANOVA and LSD. Subsequently, the microstructures of the intersecting surfaces of the specimens were observed by scanning electron microscopy (SEM). Results After repeated sintering, the L value significantly decreased (P<0.05). For the C and b values, statistical differences were observed among the groups except between S2 and S3. SEM results showed that the interlocking microstructures of rod-shaped Li₂Si₂O₅ crystals became more compact when the number of sintering times was increased. Conclusion Repeated sintering exhibited significant influence on the color of the IPS e.max-CAD LS2 veneers.

Synthesis of Nano-Scale Fast Ion Conducting Cubic Li7La3Zr2O12

DTIC Science & Technology

2013-09-25

offer the flexibility to make nano-dimensional particles with high sinterability nor the ability to coat/protect electrode powders. By developing a...sintering temperature are needed. One possible approach is to use small particles , such as nano-scale particles , that can be sintered at lower temperatures...matrix to suppress Li dendrite penetration. By developing a sol–gel process, the LLZO particle size can be precisely tuned, from the nanometer to the

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hanc, Emil; Zając, Wojciech, E-mail: wojciech.zajac@agh.edu.pl; Lu, Li

Ceramic oxides exhibiting high lithium-ion mobility at room temperature receive broad attention as candidate electrolytes for lithium batteries. Lithium-stuffed garnets from the Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} group seem to be especially promising because of their high ionic conductivity at room temperature and their electrochemical stability. In this work, we discuss factors that affect formation of the garnet in its bulk form or in the form of thick and thin films. We demonstrate that zinc oxide can be applied as a sintering aid that facilitate the formation of the highly conducting cubic Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} garnet phase inmore » a single-step sintering procedure. Based on our experience with the single-step sintering experiments, we successfully fabricated a thick-film membrane consisting of a garnet solid electrolyte using the tape casting technique. In order to reduce the thickness of the electrolyte even further we investigated the fabrication of a thin-film Li{sub 7}La{sub 3}Zr{sub 2}O{sub 12} electrolyte by means of the pulsed laser deposition technique.« less

On fabrication procedures of Li-ion conducting garnets

NASA Astrophysics Data System (ADS)

Hanc, Emil; Zając, Wojciech; Lu, Li; Yan, Binggong; Kotobuki, Masashi; Ziąbka, Magdalena; Molenda, Janina

2017-04-01

Ceramic oxides exhibiting high lithium-ion mobility at room temperature receive broad attention as candidate electrolytes for lithium batteries. Lithium-stuffed garnets from the Li7La3Zr2O12 group seem to be especially promising because of their high ionic conductivity at room temperature and their electrochemical stability. In this work, we discuss factors that affect formation of the garnet in its bulk form or in the form of thick and thin films. We demonstrate that zinc oxide can be applied as a sintering aid that facilitate the formation of the highly conducting cubic Li7La3Zr2O12 garnet phase in a single-step sintering procedure. Based on our experience with the single-step sintering experiments, we successfully fabricated a thick-film membrane consisting of a garnet solid electrolyte using the tape casting technique. In order to reduce the thickness of the electrolyte even further we investigated the fabrication of a thin-film Li7La3Zr2O12 electrolyte by means of the pulsed laser deposition technique.

Large size crystalline vs. co-sintered ceramic Yb(3+):YAG disk performance in diode pumped amplifiers.

PubMed

Albach, Daniel; Chanteloup, Jean-Christophe

2015-01-12

A comprehensive experimental benchmarking of Yb(3+):YAG crystalline and co-sintered ceramic disks of similar thickness and doping level is presented in the context of high average power laser amplifier operation. Comparison is performed considering gain, depolarization and wave front deformation quantitative measurements and analysis.

Rapidly sintering of interconnected porous Ti-HA biocomposite with high strength and enhanced bioactivity.

PubMed

Zhang, L; He, Z Y; Zhang, Y Q; Jiang, Y H; Zhou, R

2016-10-01

In this work, interconnected porous Ti-HA biocomposites with enhanced bioactivity, high porosity and compressive strength were prepared by spark plasma sintering (SPS) and space holder method. Pore characteristics, mechanical properties, corrosion behaviors and in vitro bioactivity of the porous Ti-HA were investigated. Results showed that porous Ti-HA with 5-30wt% HA contents possessed not only low elastic modulus of 8.2-15.8GPa (close to that of human bone) but also high compressive strength (86-388MPa). Although the HA partially decomposed and formed secondary phases, the sintered porous Ti-HA can still be good bioactivity. The homogeneity and the thickness of apatite layer increased significantly with the increase of HA. But with the thickness of apatite layer increased, micro-cracks appeared on the surface of porous Ti-30%HA. A model was built to discuss the current distribution and sintering mechanism of HA on Ti matrix during SPS process. It indicated that the excessive addition of HA would deteriorate the sintering quality, thus decreasing the mechanical properties and corrosion resistance. However, the combination of interconnected pore characteristics, low elastic modulus, high compressive strength and enhanced bioactivity might make porous Ti-HA biocomposites prepared by SPS a promising candidate for hard tissue implants. Copyright © 2016 Elsevier B.V. All rights reserved.

Preparation of functional layers for anode-supported solid oxide fuel cells by the reverse roll coating process

NASA Astrophysics Data System (ADS)

Mücke, R.; Büchler, O.; Bram, M.; Leonide, A.; Ivers-Tiffée, E.; Buchkremer, H. P.

The roll coating technique represents a novel method for applying functional layers to solid oxide fuel cells (SOFCs). This fast process is already used for mass production in other branches of industry and offers a high degree of automation. It was utilized for coating specially developed anode (NiO + 8YSZ, 8YSZ: 8 mol% yttria-stabilized zirconia) and electrolyte (8YSZ) suspensions on green and pre-sintered tape-cast anode supports (NiO + 8YSZ). The layers formed were co-fired in a single step at 1400 °C for 5 h. As a result, the electrolyte exhibited a thickness of 14-18 μm and sufficient gas tightness. Complete cells with a screen-printed and sintered La 0.65Sr 0.3MnO 3- δ (LSM)/8YSZ cathode yielded a current density of 0.9-1.1 A cm -2 at 800 °C and 0.7 V, which is lower than the performance of non-co-fired slip-cast or screen-printed Jülich standard cells with thinner anode and electrolyte layers. The contribution of the cell components to the total area-specific resistance (ASR) was calculated by analyzing the distribution function of the relaxation times (DRTs) of measured electrochemical impedance spectra (EIS) and indicates the potential improvement in the cell performance achievable by reducing the thickness of the roll-coated layers. The results show that the anode-supported planar half-cells can be fabricated cost-effectively by combining roll coating with subsequent co-firing.

[Application of sintered Ti powder to dental prostheses].

PubMed

Hikosaka, Tatsuya; Tanaka, Yoshinobu; Hoshiai, Kazumoto; Kanazawa, Takeshi; Nakamura, Yoshinori; Tsuda, Kenji; Ohasi, Hideya

2005-04-01

Powder metallurgy is a metal processing technology. Porous titanium produced from powder is widely used. The method is applied to titanium, which is not easy to cast as it sinters under melting point. In prosthetic dentistry, powder metallurgy can be applied to high fusing metal that is biocompatible. In this study, we examined the mechanical characteristics of the Ti sheet produced by sintering and discussed its application to dental prosthesis manufacturing. Ti sheets of 1-mm thickness, in which a binder was added to spherical Ti powder, were produced with the Doctor Blade Method. The sintering was carried out between 900-1150 degrees C at 6 temperatures. The sintered compact was evaluated by dimensional change rate, hardness test, bending strength, tensile strength and SEM observation. Another compact was sintered on the refractory cast. Mechanical strength significantly increased with sintering temperature. In addition, excellent mechanical strength was acquired by adding crushed powder and performing the de-binder process. In the sintering on the refractory cast, pre-baking for more than 100 minutes and sintering at over 1050 degrees C was needed for practical application. It thus seems possible to apply sintered titanium to dental prostheses. However, it will be necessary to examine the control of the shrinkage of the sintered compact in the future too.

Scanning pattern angle effect on the resulting properties of selective laser sintered monolayers of Cu-Sn-Ni powder

NASA Astrophysics Data System (ADS)

Sabelle, Matías; Walczak, Magdalena; Ramos-Grez, Jorge

2018-01-01

Laser-based layer manufacturing of metals, also known as additive manufacturing, is a growing research field of academic and industrial interest. However, in the associated laser-driven processes (i.e. selective laser sintering (SLS) or melting (SLM)), optimization of some parameters has not been fully explored. This research aims at determining how the angle of laser scanning pattern (i.e. build orientation) in SLS affects the mechanical properties and structure of an individual Cu-Sn-Ni alloy metallic layer sintered in the process. Experiments consist in varying the angle of the scanning pattern (0°, 30°, 45° 60° and 90° relative to the transverse dimension of the piece), at constant scanning speed and laser beam power, producing specimens of different thicknesses. A noticeable effect of the scan angle on the mechanical strength and degree of densification of the sintered specimens is found. Thickness of the resulting monolayer correlates negatively with increasing scan angle, whereas relative density correlates positively. A minimum porosity and maximum UTS are found at the angle of 60°. It is concluded that angle of the scanning pattern angle plays a significant role in SLS of metallic monolayers.

Influence of the sintering temperature on the electrical properties of Ce-doped WO3 ceramics prepared from nano-powders

NASA Astrophysics Data System (ADS)

Dong, Liang; Chen, Han-Jun; Wang, Yu; Li, De-Zhu; Li, Tong-Ye; Zhao, Yong

2007-04-01

Using a nm-level powder fabricated by a wet chemical method as precursor, the CeO2-doped WO3 ceramics were prepared by the conventional solid state reaction at sintering temperatures from 600 to 1100 °C. The x-ray diffraction analysis reveals the coexistence of different WO3 phases in the samples sintered at temperatures below 900 °C, whereas a single phase appears in the samples sintered above 1000 °C. No new Ce-W compound appears. As the sintering temperature increases, the electrical properties of the samples display an interesting transformation from linear to nonlinear behaviour. The measurements of scanning electron microscope, complex impedance and electrical stability indicate that a lot of grain boundary regions in the samples sintered at low temperatures strongly influences the electrical transportation. Therefore, the electrical nonlinearity is due to a basic process controlled by the back-to-back Schottky barriers at grain boundaries with suitable thickness as well as the coexistence of phases.

Luminescence Characteristics of ZnGa2O4 Thick Film Doped with Mn2+ and Cr3+ at Various Sintering Temperatures

NASA Astrophysics Data System (ADS)

Cha, Jae Hyeok; Kim, Kyung Hwan; Park, Yong Seo; Kwon, Sang Jik; Choi, Hyung Wook

2007-10-01

ZnGa2O4 phosphor separately doped with Mn2+ and Cr3+ was synthesized by solid-state reaction, and thick films were deposited by screen printing. The X-ray diffraction (XRD) patterns of ZnGa2O4 phosphor thick films show a (311) main peak and a spinal phase. Uniform distribution and filled morphology of the doped ZnGa2O4 phosphor thick films were formed at the sintering temperature of 1100 °C. The CL spectrum of Mn2+-doped ZnGa2O4 shows the main peak of 512 nm green emission with the 4T1→6A1 transition of Mn2+ ions and the CL spectrum of Cr3+-doped ZnGa2O4 shows the main peak of 716 nm red emission with the 2E→4A2 transition of Cr3+ ions.

Development of Economical Improved Thick Film Solar Cell Contact

NASA Technical Reports Server (NTRS)

Ross, B.

1979-01-01

Materials were surveyed to provide candidates for an all metal electrode paste system. These consisted of a major constituent metal powder, a low melting metal powder suitable for a liquid phase sintering medium, and a powder material suitable as an etchant for silicon dioxide at sintering temperatures. By means of thermal gravimetric analysis a suitable binder was identified for low temperature fired inks.

Twin defects in thick stoichiometric lithium tantalate crystals prepared by a vapor transport equilibration method

NASA Astrophysics Data System (ADS)

Yang, Jinfeng; Sun, Jun; Xu, Jingjun; Li, Qinglian; Shang, Jifang; Zhang, Ling; Liu, Shiguo; Huang, Cunxin

2016-01-01

The twins were observed and investigated in vapor transport equilibration (VTE) treated lithium tantalate crystals by burying congruent lithium tantalate crystals (CLT) in a Li-rich polycrystalline powder. Twins and their etched patterns were observed under an optical polarizing microscope, and the geometry of the twins was discussed. Twin composition planes were the { 01 1 bar 2 } planes. The cause of twinning was analyzed and verified by experiment. The results indicate that the emergence of twins is due to sintering stress, which arises from sintered Li-rich polycrystalline powders at high temperature. 3.2 mm thick stoichiometric lithium tantalate (SLT) crystals without twins were obtained by setting corundum crucibles over the top of the crystals to make crystals free from the sintering stress. In addition, cracks were observed at the intersection of twin bands, and the stress caused by the dislocation pile-up was considered to be the reason for the formation of cracks.

Terahertz thickness measurements for real industrial applications: from automotive paints to aerospace industry (Conference Presentation)

NASA Astrophysics Data System (ADS)

Krimi, Soufiene; Beigang, René

2017-02-01

In this contribution, we present a highly accurate approach for real-time thickness measurements of multilayered coatings using terahertz time domain spectroscopy in reflection geometry. The proposed approach combines the benefits of a model-based material parameters extraction method to calibrate the specimen under test, a generalized modeling method to simulate the terahertz radiation behavior within arbitrary thin films, and the robustness of a powerful evolutionary optimization algorithm to increase the sensitivity and the precision of the minimum thickness measurement limit. Furthermore, a novel self-calibration model is introduced, which takes into consideration the real industrial challenges such as the effect of wet-on-wet spray in the car painting process and the influence of the spraying conditions and the sintering process on ceramic thermal barrier coatings (TBCs) in aircraft industry. In addition, the developed approach enables for some applications the simultaneous determination of the complex refractive index and the coating thickness. Hence, a pre-calibration of the specimen under test is not required for such cases. Due to the high robustness of the self-calibration method and the genetic optimization algorithms, the approach has been successfully applied to resolve individual layer thicknesses within multi-layered coated samples down to less than 10 µm. The regression method can be applied in time-domain, frequency-domain or in both the time and frequency-domain simultaneously. The data evaluation uses general-purpose computing on graphics processing units and thanks to the developed highly parallelized algorithm lasts less than 300 ms. Thus, industrial requirements for fast thickness measurements with an "every-second-cycle" can be fulfilled.

Assesment of (Mn,Co)33O4 powders for possible coating material for SOFC/SOEC interconnects

NASA Astrophysics Data System (ADS)

Szymczewska, D.; Molin, S.; Venkatachalam, V.; Chen, M.; Jasinski, P.; Hendriksen, P. V.

2016-01-01

In this work (Mn,Co)3O4 spinel powders with different Mn:Co ratio (1:1 and 1:2) and from different commercial suppliers are evaluated for possible powder for production of interconnect coatings. Sinterability of the powders is evaluated on pressed pellets sintered in oxidizing and in reducing/oxidizing atmospheres. For selected powder, coatings are then prepared by the electrophoretic deposition method on Crofer 22 APU stainless steel coupons. Effects of dispersant/iodine content and deposition voltage and times are evaluated. Thickness as a function of deposition parameters is described. Results show that with appropriate powder it is possible to produce adherent protective coating with a well-controlled thickness.

Special Test Methods for Batteries

NASA Technical Reports Server (NTRS)

Gross, S.

1984-01-01

Various methods are described for measuring heat generation in primary and secondary batteries as well as the specific heat of batteries and cell thermal conductance. Problems associated with determining heat generation in large batteries are examined. Special attention is given to monitoring temperature gradients in nickel cadmium cells, the use of auxiliary electrodes for conducting tests on battery charge control, evaluating the linear sweep of current from charge to discharge, and determining zero current voltage. The fast transient behavior of batteries in the microsecond range, and the electrical conductance of nickel sinters in the thickness direction are also considered. Mechanical problems experienced in the vibration of Ni-Cd batteries and tests to simulate cyclic fatigue of the steel table connecting the plates to the comb are considered. Methods of defining the distribution of forces when cells are compressed during battery packaging are also explored.

Special test methods for batteries

NASA Astrophysics Data System (ADS)

Gross, S.

1984-09-01

Various methods are described for measuring heat generation in primary and secondary batteries as well as the specific heat of batteries and cell thermal conductance. Problems associated with determining heat generation in large batteries are examined. Special attention is given to monitoring temperature gradients in nickel cadmium cells, the use of auxiliary electrodes for conducting tests on battery charge control, evaluating the linear sweep of current from charge to discharge, and determining zero current voltage. The fast transient behavior of batteries in the microsecond range, and the electrical conductance of nickel sinters in the thickness direction are also considered. Mechanical problems experienced in the vibration of Ni-Cd batteries and tests to simulate cyclic fatigue of the steel table connecting the plates to the comb are considered. Methods of defining the distribution of forces when cells are compressed during battery packaging are also explored.

Cryomilled and spark plasma sintered titanium: the evolution of microstructure

NASA Astrophysics Data System (ADS)

Kozlík, Jiří; Becker, Hanka; Harcuba, Petr; Stráský, Josef; Janeček, Milos

2017-05-01

Bulk ultra-fine grained (UFG) commercially pure Ti was prepared by cryogenic milling in liquid argon and subsequent spark plasma sintering (SPS). During cryogenic milling, individual powder particles are repetitively severely deformed by attrition forces. Powder particles were not significantly refined, but due to severe repetitive plastic deformation, ultra-fine grained microstructure emerges within each powder particle. Cryogenic milling can be therefore considered as a specific severe plastic deformation (SPD) method. Compactization of cryomilled powder by SPS technique (also referred to as field assisted sintering technique - FAST) requires significantly lower sintering temperatures and shorter sintering times for successful compaction when compared to any other sintering technique. This is crucial for maintaining the UFG microstructure due to its limited thermal stability. Several specimens were prepared by varying processing parameters, in particular the sintering temperature. The microstructure of powders and compacted samples was observed by scanning electron microscopy (SEM). Increased sintering temperature results in recrystallization and grain growth. A trade-off relationship between the density of compacted material and grain size was identified. Microhardness of the material was found to depend on residual porosity rather than grain size. This contribution presents cryogenic milling and spark plasma sintering as a viable alternative for achieving UFG microstructure in commercially pure Ti.

Anti-aging Friction of Carbonate Fault Mirror and its Microstructural Interpretation

NASA Astrophysics Data System (ADS)

Park, Y.; Ree, J. H.; Hirose, T.

2017-12-01

In our slide-hold-slide (SHS) friction tests on carbonate fault rocks, fault mirror (FM), light reflective mirror-like fault surface, shows almost zero or slightly negative aging rate of friction (`anti-aging' friction), whereas carbonate faults without FM exhibit a positive aging rate. We analyzed microstructures from three types of carbonate faults to explore the cause of the anti-aging friction of FM. The three types of fault rocks before SHS tests were made from Carrara marble; (i) FM, (ii) crushed gouge of former FM (CF), and (iii) gouge produced by pre-shearing of Carrara marble (PR). The fault zone of FM before SHS tests consists of sintered nanograin patches smeared into negative asperities of wall rocks (thickness up to 150 μm) and a sintered gouge layer between wall rocks (thickness up to 200 μm) that is composed of tightly-packed nanograins (50-500 nm in size) with triple junctions and angular-subangular fragments (a few-100 μm) of sintered nanograin aggregates. A straight and discrete Y-shear surface defines a boundary between the gouge layer and the nanograin patches or between the layer and wall rock. CF specimens before SHS tests are composed of patches of sintered nanograins as in FM specimens and a porous gouge layer with finer nanograins (a few-20 nm in size) and angular fragments of former FM. PR specimens before SHS tests are composed of damaged wall rocks and porous gouge with finer nanograins (a few-tens of μm). After SHS tests, sintered appearance of grains within the fault zones of CF and PR indicates the increase in interparticle bonding and also in contact area by grain aggregation. In contrast, the gouge layer of FM specimens after SHS tests consists mostly of angular fragments of sintered nanograin aggregates. The angular shape of the fragments indicates little increase in bonding and contact area between the fragments. Tightly sintered nanograins in FM specimens would have a lower chemical reactivity with their size coarser and sintering stronger than those of CF and PR. Furthermore, a high wear resistance of sintered nanograins of FM would prohibit generation of fine wear debris which may have led to the strenghtened interparticle bonding. Our results imply that anti-aging friction may be a common behavior other rocks' FM too, once they are composed of tightly sintered nanograins.

Low-Temperature Oxidation-Free Selective Laser Sintering of Cu Nanoparticle Paste on a Polymer Substrate for the Flexible Touch Panel Applications.

PubMed

Kwon, Jinhyeong; Cho, Hyunmin; Eom, Hyeonjin; Lee, Habeom; Suh, Young Duk; Moon, Hyunjin; Shin, Jaeho; Hong, Sukjoon; Ko, Seung Hwan

2016-05-11

Copper nanomaterials suffer from severe oxidation problem despite the huge cost effectiveness. The effect of two different processes for conventional tube furnace heating and selective laser sintering on copper nanoparticle paste is compared in the aspects of chemical, electrical and surface morphology. The thermal behavior of the copper thin films by furnace and laser is compared by SEM, XRD, FT-IR, and XPS analysis. The selective laser sintering process ensures low annealing temperature, fast processing speed with remarkable oxidation suppression even in air environment while conventional tube furnace heating experiences moderate oxidation even in Ar environment. Moreover, the laser-sintered copper nanoparticle thin film shows good electrical property and reduced oxidation than conventional thermal heating process. Consequently, the proposed selective laser sintering process can be compatible with plastic substrate for copper based flexible electronics applications.

Thermal and Electrical Characterization of Alumina Substrate for Microelectronic Applications

NASA Astrophysics Data System (ADS)

Ahmad, S.; Ibrahim, A.; Alias, R.; Shapee, S. M.; Ambak, Z.; Zakaria, S. Z.; Yahya, M. R.; Mat, A. F. A.

2010-03-01

This paper reports the effect of sintering temperature on thermal and electrical properties of alumina material as substrate for microelectronic devices. Alumina materials in the form of green sheet with 1 mm thickness were sintered at 1100° C, 1300° C and 1500° C for about 20 hours using heating and cooling rates of 2° C/min. The densities were measured using densitometer and the microstructures of the samples were analyzed using SEM micrographs. Meanwhile thermal and electrical properties of the samples were measured using flash method and impedance analyzer respectively. It was found that thermal conductivity and thermal diffusivity of the substrate increases as sintering temperature increases. It was found also that the dielectric constant of alumina substrate increases as the sintering temperature increases.

NT-SiC (new-technology silicon carbide) : Φ 650mm optical space mirror substrate of high-strength reaction-sintered silicon carbide

NASA Astrophysics Data System (ADS)

Suyama, Shoko; Itoh, Yoshiyasu; Tsuno, Katsuhiko; Ohno, Kazuhiko

2005-08-01

Silicon carbide (SiC) is the most advantageous as the material of various telescope mirrors, because of high stiffness, low density, low coefficient of thermal expansion, high thermal conductivity and thermal stability. Newly developed high-strength reaction-sintered silicon carbide (NTSIC), which has two times higher strength than sintered SiC, is one of the most promising candidates for lightweight optical mirror substrate, because of fully dense, lightweight, small sintering shrinkage (+/-1 %), good shape capability and low processing temperature. In this study, 650mm in diameter mirror substrate of NTSIC was developed for space telescope applications. Three developed points describe below. The first point was to realize the lightweight to thin the thickness of green bodies. Ribs down to 3mm thickness can be obtained by strengthen the green body. The second point was to enlarge the mirror size. 650mm in diameter of mirror substrate can be fabricated with enlarging the diameter in order. The final point was to realize the homogeneity of mirror substrate. Some properties, such as density, bending strength, coefficient of thermal expansion, Young's modulus, Poisson's ratio, fracture toughness, were measured by the test pieces cutting from the fabricated mirror substrates.

Monolithic Pellets, Composites and Thick Films of Hydroxyapatite: Correlation of Mechanical Properties with Microstructure.

NASA Astrophysics Data System (ADS)

Wang, Pauchiu Either

Hydroxyapatite Ca_{10}(PO _4)_6(OH)_2 (abbreviated as HA) has great biocompatibility. Poor mechanical properties of HA implants and decomposition of HA during processing are the major obstacles for widespread uses of HA. In the present thesis we have attempted to understand the sintering behavior of monolithic HA and metal-reinforced HA-matrix composites, and the mechanism of formation of HA coating in the solutions at the normal temperature. The powders of two calcium phosphates, namely hydroxyapatite and dicalcium phosphate (DCP: chemical formula Ca_2P_2O_7), were sintered at various temperatures and in various environments. The density, flexural strength and knoop hardness of both phosphates sintered in air for 4 h initially increased with the sintering temperature, reaching maxima at around 1000-1150 ^circC, and then decreased due to decomposition. To reduce dehydroxylation, HA powder was sintered in moisture at various temperatures up to 1350^circ C and X-ray diffraction study did not indicate any decomposition at the highest sintering temperature. It is seen that dehydroxylation did not hinder sintering, but decomposition obstructed sintering of both HA and DCP. Ductile-phase reinforcement of hydroxyapatite was achieved by addition of silver particulates (5-30 vol.%) in HA powder compacts. A composite made by sintering 10 vol.% Ag and balance HA at 1200^circ C for 1 h in air had flexural strength of 75 +/- 7 MPa, which was almost double that of pure HA sintered under an identical condition. Silver in the composite melted during sintering, but due to poor wetting, did not spread in between HA particles. The increase in the flexural strength of the composites was thought to be due to crack-bridging and crack-arrest by silver inclusions. Thick films (several μm) of hydroxyapatite were deposited on silicon single crystal placed in close proximity to a plate of apatite- and wollastonite -containing glass and dipped into a simulated body fluid (SBF) at 36^circC. Amorphous calcium phosphate phase present in the glass leached into the SBF, causing supersaturation of Ca^ {2+} and (PO_4)^ {3-} ions. HA films grown on Si(111) showed strong (102) texture. As a contrast hardly any HA film could be grown on Si(100) surface. Our results suggest that the driving force for formation of apatite films arises from lowering of free energy of the supersatured solution by deposition of ions in certain crystallographic arrangements on suitable substrates with low interface energies.

The effect of air-abrasion and heat treatment on the fracture behavior of Y-TZP.

PubMed

Passos, Sheila P; Linke, Bernie; Major, Paul W; Nychka, John A

2015-09-01

This study evaluated how the flexural strength and fracture behavior of a zirconia-based ceramic (Y-TZP) were affected by pre- and post-sintering mechanical and thermal treatments. Treatments included sandblasting with different particle size and type (30μm SiO2; 50 and 110μm Al2O3) and thermal conditioning. Two hundred bar-shaped specimens of pre-sintered Y-TZP ceramic (Lava Frame, 3M) were prepared (specimen dimensions: 25mm length×4mm width×0.7mm thickness) and divided into three groups (before sintering, after sintering and after sintering with heating treatment). The before sintering group specimens were airborne-particle abraded prior to dense sintering. Specimens from the after sintering group were airborne-particle abraded after sintering. The after sintering with heating treatment group specimens were submitted to a heating procedure after airborne-particle abrasion. The controls were the specimens that were sintered and not treated with any conditioning procedures. The specimens from all experimental conditions were analyzed by SEM, CLSM and XRD. All specimens were tested in four-point bending. Data were statistically analyzed using one-way ANOVA and Post Hoc tests (α=0.05). A Weibull analysis was used to analyze the strength reliability. Sandblasting pre-sintered zirconia before sintering significantly decreased the flexural strength, except when the smallest blasting particles were used (30μm SiO2). Phase transformation (t-m) was observed after sandblasting and reverse transformation (m-t) was observed after heating. Sandblasting with 30μm SiO2 and 50μm Al2O3 allowed lower phase transformation. However, 30mm SiO2 presented better reliability. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

On the Mechanism of Microwave Flash Sintering of Ceramics

PubMed Central

Bykov, Yury V.; Egorov, Sergei V.; Eremeev, Anatoly G.; Kholoptsev, Vladislav V.; Plotnikov, Ivan V.; Rybakov, Kirill I.; Sorokin, Andrei A.

2016-01-01

The results of a study of ultra-rapid (flash) sintering of oxide ceramic materials under microwave heating with high absorbed power per unit volume of material (10–500 W/cm3) are presented. Ceramic samples of various compositions—Al2O3; Y2O3; MgAl2O4; and Yb(LaO)2O3—were sintered using a 24 GHz gyrotron system to a density above 0.98–0.99 of the theoretical value in 0.5–5 min without isothermal hold. An analysis of the experimental data (microwave power; heating and cooling rates) along with microstructure characterization provided an insight into the mechanism of flash sintering. Flash sintering occurs when the processing conditions—including the temperature of the sample; the properties of thermal insulation; and the intensity of microwave radiation—facilitate the development of thermal runaway due to an Arrhenius-type dependency of the material’s effective conductivity on temperature. The proper control over the thermal runaway effect is provided by fast regulation of the microwave power. The elevated concentration of defects and impurities in the boundary regions of the grains leads to localized preferential absorption of microwave radiation and results in grain boundary softening/pre-melting. The rapid densification of the granular medium with a reduced viscosity of the grain boundary phase occurs via rotation and sliding of the grains which accommodate their shape due to fast diffusion mass transport through the (quasi-)liquid phase. The same mechanism based on a thermal runaway under volumetric heating can be relevant for the effect of flash sintering of various oxide ceramics under a dc/ac voltage applied to the sample. PMID:28773807

Removal of glass adhered to sintered ceramics in hot isostatic pressing

NASA Technical Reports Server (NTRS)

1985-01-01

In the hot isostatic pressing of ceramic materials in molten glass using an inert gas as a pressing medium, glass adhered to the sintered ceramics is heated to convert it to a porous glass and removed. Thus, Si3N4 powder was compacted at 5000 kg/sq cm, coated with a 0.5 mm thick BN, embedded in Pyrex glass in a graphite crucible, put inside a hot isostatic press containing Argon, hot pressed at 1750 C and 100 kg/sq cm; cooled, taken out from the crucible, heated at 1100 C for 30 minutes, cooled, and then glass adhered to the sintered body was removed.

FABRICATION DEVELOPMENT OF UO$sub 2$-STAINLESS STEEL COMPOSITE FUEL PLATES FOR CORE B OF THE ENRICO FERMI FAST BREEDER REACTOR

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cherubini, J.H.; Beaver, R.J.; Leitten, C.F. Jr.

1961-04-18

The development of an inexpensive composite fuel plate with a high burnup potential for application in a 500 deg C sodium environment as Core B of the Enrico Fermi Fast Breeder Reactor is described. The dispersion fuel product consists of 35 wt.% spheroidal UO/sub 2/ dispersed in type 347B stainless steel powder and clad with wrought type 347 stainless steel. Nominal over-all dimensions of Type II design fuel plates are 18.97 in. long x 2.406 in. wide x 0.112 in. thick with 0.005-in. cladding. Reliable processing methods for achieving a uniform distribution of spheroidal UO/sub 2/ in the matrix powdermore » and cladding the sintered powder compact by roll bonding are described. Examination of experimental plates reveals that the degree of UO/sub 2/ fragmentation and stringering encountered during processing is primarily a function of the degree of cold work employed in the finishing operation snd the starting quality of the UO/sub 2/ powder. Cladding studies indicate that a sound metallurgical bond can be achieved with an 87.5% reduction in thickness at 1200 deg C and that close processing control is required to meet the stringent tolerances specified. The developed process meets all criteria except possibly the surface finish requirement; occasionally, pitting occurs due to scale embedded during hot working. Detailed procedures covering composite plate manufacture are presented. (auth)« less

Surface hardening of Al alloys through controlled ball-milling and sintering.

PubMed

Kim, Seek Hyeoun; Kim, Yong Jin; Ahn, Jung-Ho

2012-07-01

One of the drawbacks of aluminum and its alloys is the lack of proper heat-treatment for surface-hardening. In the present work, a new and simple method of hardening the surface of aluminum and its alloys was developed. Low-energy ball-milling using specific process control agents (PCAs) was employed, using subsequent sintering in a controlled atmosphere. The PCAs in the present work were very effective both for milling and the formation of hard nanocrystalline dispersoids during sintering. The residual oxygen in a sintering atmosphere also played an important role in the formation of AIN or Al-O-N dispersoids. Through the proper control of the processing atmosphere and PCAs, the hardness and thickness of the hardened layers could be adjusted. The results of the wear test showed that the present aluminum alloys can be effectively utilized as light-weight components with a good wear resistance. Furthermore, the present method involves a simple forming process of die-compaction and sintering.

Size Dependence of Residual Thermal Stresses in Micro Multilayer Ceramic Capacitors by Using Finite Element Unit Cell Model Including Strain Gradient Effect

NASA Astrophysics Data System (ADS)

Jiang, W. G.; Xiong, C. A.; Wu, X. G.

2013-11-01

The residual thermal stresses induced by the high-temperature sintering process in multilayer ceramic capacitors (MLCCs) are investigated by using a finite-element unit cell model, in which the strain gradient effect is considered. The numerical results show that the residual thermal stresses depend on the lateral margin length, the thickness ratio of the dielectrics layer to the electrode layer, and the MLCC size. At a given thickness ratio, as the MLCC size is scaled down, the peak shear stress reduces significantly and the normal stresses along the length and thickness directions change slightly with the decrease in the ceramic layer thickness t d as t d > 1 μm, but as t d < 1 μm, the normal stress components increase sharply with the increase in t d. Thus, the residual thermal stresses induced by the sintering process exhibit strong size effects and, therefore, the strain gradient effect should be taken into account in the design and evaluation of MLCC devices

Development of electrophoretically deposited hydroxyapatite coatings on anodized nanotubular TiO2 structures: Corrosion and sintering temperature

NASA Astrophysics Data System (ADS)

Goudarzi, Mona; Batmanghelich, Farhad; Afshar, Abdollah; Dolati, Abolghasem; Mortazavi, Golsa

2014-05-01

Hydroxyapatite (HA) coatings in and onto anodized TiO2 nanotube arrays were presented and prepared by electrophoretic deposition technique (EPD). Coatings were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). EPD proved to be an innovative and versatile technique to coat HA on and into nanotubular structures of TiO2 with enhanced adhesion between nanotubes and HA particles provided by mechanical interlocking. After EPD of HA on TiO2 layer, samples were sintered at 400 °C, 600 °C and 800 °C for 2 h in an Ar atmosphere. Effect of EPD processing parameters on thickness of the deposits and rate of deposition was elucidated for HA coatings on the nanotubular TiO2 structures. It was shown that higher applied voltages increase deposition rate and thickness of the coatings. Potentiodynamic polarization measurements proved corrosion protection caused by both HA coating and nanotubular TiO2 structure in simulated body fluid (SBF). Effect of sintering temperature on adhesion strength of HA coatings on TiO2 nanotubes and their composition were also studied.

Braze Process Optimization Involving Conventional Metal/Ceramic Brazing with 50Au-50Cu Alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

MALIZIA JR.,LOUIS A.; MEREDITH,KEITH W.; APPEL,DANIEL B.

1999-12-15

Numerous process variables can influence the robustness of conventional metal/ceramic brazing processes. Experience with brazing of hermetic vacuum components has identified the following parameters as influencing the outcome of hydrogen furnace brazed Kovar{trademark} to metallized alumina braze joints: (a) Mo-Mn metallization thickness, sinter fire temperature and porosity (b) Nil plate purity, thickness, and sinter firing conditions (c) peak process temperature, time above liquidus and (d) braze alloy washer thickness. ASTM F19 tensile buttons are being used to investigate the above parameters. The F19 geometry permits determination of both joint hermeticity and tensile strength. This presentation will focus on important lessonsmore » learned from the tensile button study: (A) the position of the Kovar{trademark} interlayer can influence the joint tensile strength achieved--namely, off-center interlayers can lead to residual stress development in the ceramic and degrade tensile strength values. Finite element analysis has been used to demonstrate the expected magnitude in strength degradation as a function of misalignment. (B) Time above liquidus (TAL) and peak temperature can influence the strength and alloying level of the resulting braze joint. Excessive TAL or peak temperatures can lead to overbraze conditions where all of the Ni plate is dissolved. (C) Metallize sinter fire processes can influence the morphology and strength obtained from the braze joints.« less

Magnetic properties of the surface layer and its magnetic interaction with the interior of Nd-Fe-B sintered magnets

NASA Astrophysics Data System (ADS)

Kobayashi, Kurima; Nakamura, Michi-hide; Urushibata, Kimiko

2015-05-01

The magnetization and demagnetization mechanisms in the mechanically polished surface layers (SL) of the c-plane and a-b plane of Nd-Fe-B sintered magnets were investigated. The magnetic interaction between the SL and the interior of the magnet was clarified by using vibrating sample magnetometer measurements of a whole sample and magneto-force microscopy observations of the domain structure of the SL layer. The polishing eliminated the Nd-rich grain boundary phases, which was only about 2 nm thick, from the SL crystal grains in the sintered magnets. The a-b plane polishing caused the independent magnetic reversal of the a-b plane SL, which was about 5.5 μm thick, as in the platy samples. The coercivities (μ0Hc) of the SL were less than 0.3 T. In contrast, the c-plane polishing did not produce independent magnetic reversal of the SL, although the coercivity of bulk samples was clearly decreased by the formation of the c-plane SL. The grains in the SL should form clusters that alter the demagnetizing factors, depending on the shape of cluster as a magnetic unit. The magnetic interaction among the SL crystal grains is expected to play an important role in the coercivity mechanism of Nd-Fe-B sintered magnets.

Composite uranium carbide targets at TRIUMF: Development and characterization with SEM, XRD, XRF and L-edge densitometry

NASA Astrophysics Data System (ADS)

Kunz, Peter; Bricault, Pierre; Dombsky, Marik; Erdmann, Nicole; Hanemaayer, Vicky; Wong, John; Lützenkirchen, Klaus

2013-09-01

The production of radioactive ion beams (RIB) from spallation targets by irradiation with a continuous 500 MeV proton beam, has been routine at TRIUMF for several years. Based on the experience with composite refractory carbide targets a procedure for the fabrication of UC2/C targets was developed. It includes the preparation of UC2 by carbothermal reduction of UO2, the slip-casting of fine-grained UC2/C slurry on graphite foil under inert gas atmosphere and the cutting of composite target discs which are stacked up to a lamellar structure. The thermal properties of such an arrangement are adequate to withstand the high power deposition of an intense, continuous proton beam and also beneficial for the fast release of short-lived radioactive isotopes. Molecular structure, particle size and the impact of sintering of the target discs were investigated via XRD and SEM. Thickness and mass distribution were measured with position-sensitive LIII-edge densitometry. The results confirm that the properties of the UC2/C target material are well suited for RIB production at TRIUMF while there is still room for improvement with regard to uniformity of mass distribution in target disc thickness.

Influence of Microstructure and Surface Activation of Dual-Phase Membrane Ce 0.8 Gd 0.2 O 2-δ -FeCo 2 O 4 on Oxygen Permeation

DOE PAGES

Ramasamy, Madhumidha; Baumann, Stefan; Palisaitis, Justinas; ...

2015-09-24

In dual-phase oxygen transport membranes we noticed that there is fast-growing interest in research for oxyfuel combustion process application. One such potential candidate is CGO-FCO (60wt% Ce 0.8Gd 0.2O 2-δ-40wt% FeCo 2O4) identified to provide good oxygen permeation flux with substantial stability in harsh atmosphere. Dense CGO-FCO membranes of 1mm thickness were fabricated by sintering dry pellets pressed from powders synthesized by one-pot method (modified Pechini process) at 1200 degrees C for 10h. Microstructure analysis indicates presence of a third orthorhombic perovskite phase in the sintered composite. We also identified that the spinel phase tends to form an oxygen deficientmore » phase at the grain boundary of spinel and CGO phases. Surface exchange limitation of the membranes was overcome by La 0.6Sr 0.4Co 0.2Fe 0.8O 3-δ (LSCF) porous layer coating over the composite. Moreover, the oxygen permeation flux of the CGO-FCO screen printed with a porous layer of 10mthick LSCF is 0.11mL/cm 2 per minute at 850 degrees C with argon as sweep and air as feed gas at the rates of 50 and 250mL/min.« less

Production of ZrC Matrix for Use in Gas Fast Reactor Composite Fuels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vasudevamurthy, Gokul; Knight, Travis W.; Roberts, Elwyn

2007-07-01

Zirconium carbide is being considered as a candidate for inert matrix material in composite nuclear fuel for Gas fast reactors due to its favorable characteristics. ZrC can be produced by the direct reaction of pure zirconium and graphite powders. Such a reaction is exothermic in nature. The reaction is self sustaining once initial ignition has been achieved. The heat released during the reaction is high enough to complete the reaction and achieve partial sintering without any external pressure applied. External heat source is required to achieve ignition of the reactants and maintain the temperature close to the adiabatic temperature tomore » achieve higher levels of sintering. External pressure is also a driving force for sintering. In the experiments described, cylindrical compacts of ZrC were produced by direct combustion reaction. External induction heating combined with varying amounts of external applied pressure was employed to achieve varying degrees of density/porosity. The effect of reactant particle size on the product characteristics was also studied. The samples were characterized for density/porosity, composition and microstructure. (authors)« less

Evaluation of Computed Tomography of Mock Uranium Fuel Rods at the Advanced Photon Source

DOE PAGES

Hunter, James F.; Brown, Donald William; Okuniewski, Maria

2015-06-01

This study discusses a multi-year effort to evaluate the utility of computed tomography at the Advanced Photon Source (APS) as a tool for non-destructive evaluation of uranium based fuel rods. The majority of the data presented is on mock material made with depleted uranium which mimics the x-ray attenuation characteristics of fuel rods while allowing for simpler handling. A range of data is presented including full thickness (5mm diameter) fuel rodlets, reduced thickness (1.8mm) sintering test samples, and pre/post irradiation samples (< 1mm thick). These data were taken on both a white beam (bending magnet) beamline and a high energy,more » monochromatic beamline. This data shows the utility of a synchrotron type source in the evealuation of manufacturing defects (pre-irradiation) and lays out the case for in situ CT of fuel pellet sintering. Finally, in addition data is shown from small post-irradiation samples and a case is made for post-irradiation CT of larger samples.« less

Research Progresses and Suggestions of Manufacturing Technologies of Engine Bearing Bushes

NASA Astrophysics Data System (ADS)

Cao, J.; Yin, Z. W.; Li, H. L.; Y Gao, G.

2017-12-01

Bearing bush is a key part of diesel engine, and its performance directly influences the life of whole machine. Several manufacturing technologies of bearing bush such as centrifugal casting, sintering, electroplating and magnetron sputtering have been overviewed. Their bond strength, porosity, production efficient, layer thickness, frictional coefficient and corresponding materials analyzed and compared. Results show that the porosity and oxidation of sintering and centrifugal casting are higher than that of other two methods. However, the production efficiency and coating thickness are better than that of electroplating and magnetron sputtering. Based on above comparisons and discussions, the improvements of all manufacturing technologies are suggested and supersonic cold spraying is suggested. It is proved that cold spraying technology is the best choice in the future with the developing of low frictional materials.

Process for making dense thin films

DOEpatents

Jacobson, Craig P.; Visco, Steven J.; DeJonghe, Lutgard C.

2005-07-26

Provided are low-cost, mechanically strong, highly electronically conductive porous substrates and associated structures for solid-state electrochemical devices, techniques for forming these structures, and devices incorporating the structures. The invention provides solid state electrochemical device substrates of novel composition and techniques for forming thin electrode/membrane/electrolyte coatings on the novel or more conventional substrates. In particular, in one embodiment the invention provides techniques for firing of device substrate to form densified electrolyte/membrane films 5 to 20 microns thick. In another embodiment, densified electrolyte/membrane films 5 to 20 microns thick may be formed on a pre-sintered substrate by a constrained sintering process. In some cases, the substrate may be a porous metal, alloy, or non-nickel cermet incorporating one or more of the transition metals Cr, Fe, Cu and Ag, or alloys thereof.

Processing conditions and microstructural features of porous 316L stainless steel components by DMLS

NASA Astrophysics Data System (ADS)

Gu, Dongdong; Shen, Yifu

2008-12-01

Direct metal laser sintering (DMLS), due to its flexibility in materials and shapes, would be especially interesting to produce complex shaped porous metallic components. In the present work, processing conditions and microstructural characteristics of direct laser sintered porous 316L stainless steel components were studied. It was found that a partial melting mechanism of powders gave a high feasibility in obtaining porous sintered structures possessing porosities of ˜21-˜55%. Linear energy density (LED), which was defined by the ratio of laser power to scan speed, was used to tailor the laser sintering mechanism. A moderate LED of ˜3400-˜6000 J/m and a lower scan speed less than 0.06 m/s proved to be feasible. With the favorable sintering mechanism prevailed, lowering laser power or increasing scan speed, scan line spacing, and powder layer thickness generally led to a higher porosity. Metallurgical mechanisms of pore formation during DMLS were addressed. It showed that the presence of pores was through: (i) the formation of liquid bridges between partially melted particles during laser irradiation; and (ii) the growth of sintering necks during solidification, leaving residual pores between solidified metallic agglomerates.

The strength of sintered and adhesively bonded zirconia/veneer-ceramic bilayers.

PubMed

Costa, Anna Karina F; Borges, Alexandre Luiz S; Fleming, Garry James P; Addison, Owen

2014-10-01

Recently all-ceramic restorative systems have been introduced that use CAD/CAM technology to fabricate both the Y-TZP core and veneer-ceramic layers. The aim was to identify whether the CAD/CAM approach resulted in more favourable stressing patterns in the veneer-ceramic when compared with a conventionally sintered Y-TZP core/veneer-ceramic. Nominally identical Vita VM9 veneer-ceramic disc-shaped specimens (0.7mm thickness, 12mm diameter) were fabricated. 20 specimens received a surface coating of resin-cement (Panavia 21); 20 specimens were bonded with the resin-cement to fully sintered Y-TZP (YZ Vita Inceram Vita) discs (0.27mm thickness, 12mm diameter). A final series of 20 Y-TZP core/veneer-ceramic specimens were manufactured using a conventional sintering route. Biaxial flexure strength was determined in a ball-on-ring configuration and stress at the fracture origin calculated using multilayer closed-form analytical solutions. Fractography was undertaken using scanning electron microscopy. The experimental test was simulated using Finite Element Analysis. Group mean BFS were compared using a one-way ANOVA and post hoc Tukey tests at a 95% significance level. Resin cement application resulted in significant strengthening of the veneer-ceramic and further significant strengthening of the veneer-ceramic (p<0.01) occurred following bonding to the Y-TZP core. The BFS calculated at the failure origin for conventionally sintered specimens was significantly reduced when compared with the adhesively bonded Y-TZP/veneer-ceramic. Under the test conditions employed adhesive cementation between CAD/CAM produced Y-TZP/veneer-ceramic layers appears to offer the potential to induce more favourable stress states within the veneer-ceramic when compared with conventional sintered manufacturing routes. The current investigation suggests that the stressing patterns that arise in all-ceramic restorations fabricated using CAD/CAM for both the core and veneer-ceramic layers differ from those that occur in conventionally sintered bilayer restorations. Further work is required to ascertain whether such differences will translate into improved clinical outcomes. Copyright © 2014 Elsevier Ltd. All rights reserved.

Microwave-assisted reactive sintering and lithium ion conductivity of Li1.3Al0.3Ti1.7(PO4)3 solid electrolyte

NASA Astrophysics Data System (ADS)

Hallopeau, Leopold; Bregiroux, Damien; Rousse, Gwenaëlle; Portehault, David; Stevens, Philippe; Toussaint, Gwenaëlle; Laberty-Robert, Christel

2018-02-01

Li1.3Al0.3Ti1.7(PO4)3 (LATP) materials are made of a three-dimensional framework of TiO6 octahedra and PO4 tetrahedra, which provides several positions for Li+ ions. The resulting high ionic conductivity is promising to yield electrolytes for all-solid-state Li-ion batteries. In order to elaborate dense ceramics, conventional sintering methods often use high temperature (≥1000 °C) with long dwelling times (several hours) to achieve high relative density (∼90%). In this work, an innovative synthesis and processing approach is proposed. A fast and easy processing technique called microwave-assisted reactive sintering is used to both synthesize and sinter LATP ceramics with suitable properties in one single step. Pure and crystalline LATP ceramics can be achieved in only 10 min at 890 °C starting from amorphous, compacted LATP's precursors powders. Despite a relative density of 88%, the ionic conductivity measured at ambient temperature (3.15 × 10-4 S cm-1) is among the best reported so far. The study of the activation energy for Li+ conduction confirms the high quality of the ceramic (purity and crystallinity) achieved by using this new approach, thus emphasizing its interest for making ion-conducting ceramics in a simple and fast way.

Long Life Nickel Electrodes for Nickel-Hydrogen Cells: Fiber Substrates Nickel Electrodes

NASA Technical Reports Server (NTRS)

Rogers, Howard H.

2000-01-01

Samples of nickel fiber mat electrodes were investigated over a wide range of fiber diameters, electrode thickness, porosity and active material loading levels. Thickness' were 0.040, 0.060 and 0.080 inches for the plaque: fiber diameters were primarily 2, 4, and 8 micron and porosity was 85, 90, and 95%. Capacities of 3.5 in. diameter electrodes were determined in the flooded condition with both 26 and 31% potassium hydroxide solution. These capacity tests indicated that the highest capacities per unit weight were obtained at the 90% porosity level with a 4 micron diameter fiber plaque. It appeared that the thinner electrodes had somewhat better performance, consistent with sintered electrode history. Limited testing with two-positive-electrode boiler plate cells was also carried out. Considerable difficulty with constructing the cells was encountered with short circuits the major problem. Nevertheless, four cells were tested. The cell with 95% porosity electrodes failed during conditioning cycling due to high voltage during charge. Discharge showed that this cell had lost nearly all of its capacity. The other three cells after 20 conditioning cycles showed capacities consistent with the flooded capacities of the electrodes. Positive electrodes made from fiber substrates may well show a weight advantage of standard sintered electrodes, but need considerably more work to prove this statement. A major problem to be investigated is the lower strength of the substrate compared to standard sintered electrodes. Problems with welding of leads were significant and implications that the electrodes would expand more than sintered electrodes need to be investigated. Loading levels were lower than had been expected based on sintered electrode experiences and the lower loading led to lower capacity values. However, lower loading causes less expansion and contraction during cycling so that stress on the substrate is reduced.

Ceramic Spheres—A Novel Solution to Deep Sea Buoyancy Modules

PubMed Central

Jiang, Bo; Blugan, Gurdial; Sturzenegger, Philip N.; Gonzenbach, Urs T.; Misson, Michael; Thornberry, John; Stenerud, Runar; Cartlidge, David; Kuebler, Jakob

2016-01-01

Ceramic-based hollow spheres are considered a great driving force for many applications such as offshore buoyancy modules due to their large diameter to wall thickness ratio and uniform wall thickness geometric features. We have developed such thin-walled hollow spheres made of alumina using slip casting and sintering processes. A diameter as large as 50 mm with a wall thickness of 0.5–1.0 mm has been successfully achieved in these spheres. Their material and structural properties were examined by a series of characterization tools. Particularly, the feasibility of these spheres was investigated with respect to its application for deep sea (>3000 m) buoyancy modules. These spheres, sintered at 1600 °C and with 1.0 mm of wall thickness, have achieved buoyancy of more than 54%. As the sphere’s wall thickness was reduced (e.g., 0.5 mm), their buoyancy reached 72%. The mechanical performance of such spheres has shown a hydrostatic failure pressure above 150 MPa, corresponding to a rating depth below sea level of 5000 m considering a safety factor of 3. The developed alumina-based ceramic spheres are feasible for low cost and scaled-up production and show great potential at depths greater than those achievable by the current deep-sea buoyancy module technologies. PMID:28773651

Sinter of uniform, predictable, blemish-free nickel plaque for large aerospace nickel cadmium cells

NASA Technical Reports Server (NTRS)

Seiger, H. N.

1975-01-01

A series of nickel slurry compositions were tested. Important slurry parameters were found to be the nature of the binder, a pore former and the method of mixing. A slow roll mixing which is non-turbulent successfully eliminated entrapped air so that bubbles and pockets were avoided in the sinter. A slurry applicator was developed which enabled an equal quantity of slurry to be applied to both sides of the grid. Sintering in a furnace having a graded atmosphere characteristic, ranging from oxidizing to strongly reducing, improved adhesion of porous sinter to grid and resulted in a uniform welding of nickel particles to each other throughout the plaque. Sintering was carried out in a horizontal furnace having three heating zones and 16 heating control circuits. Tests used for plaque evaluation include (1) appearance, (2) grid location and adhesion, (3) mechanical strength, (4) thickness, (5) weight per unit area, (6) void volume per unit area, (7) surface area and (8) electrical resistance. Plaque material was impregnated using Heliotek proprietary processes and 100 AH cells were fabricated.

Analysis of key factors influencing the evaporation performances of an oriented linear cutting copper fiber sintered felt

NASA Astrophysics Data System (ADS)

Pan, Minqiang; Zhong, Yujian

2018-01-01

Porous structure can effectively enhance the heat transfer efficiency. A kind of micro vaporizer using the oriented linear cutting copper fiber sintered felt is proposed in this work. Multiple long cutting copper fibers are firstly fabricated with a multi-tooth tool and then sintered together in parallel to form uniform thickness metal fiber sintered felts that provided a characteristic of oriented microchannels. The temperature rise response and thermal conversion efficiency are experimentally investigated to evaluate the influences of porosity, surface structure, feed flow rate and input power on the evaporation characteristics. It is indicated that the temperature rise response of water is mainly affected by input power and feed flow rate. High input power and low feed flow rate present better temperature rise response of water. Porosity rather than surface structure plays an important role in the temperature rise response of water at a relatively high input power. The thermal conversion efficiency is dominated by the input power and surface structure. The oriented linear cutting copper fiber sintered felts for three kinds of porosities show better thermal conversion efficiency than that of the oriented linear copper wire sintered felt when the input power is less than 115 W. All the sintered felts have almost the same performance of thermal conversion at a high input power.

Multiwalled carbon nanotube monoliths prepared by spark plasma sintering (SPS) and their mechanical properties.

PubMed

Uo, Motohiro; Hasegawa, Tomoka; Akasaka, Tsukasa; Tanaka, Isao; Munekane, Fuminori; Omori, Mamoru; Kimura, Hisamichi; Nakatomi, Reiko; Soga, Kohei; Kogo, Yasuo; Watari, Fumio

2009-01-01

Three types of multiwalled carbon nanotube (MWCNT) monoliths without any binders were obtained by spark plasma sintering (SPS) treatment at 2000 degrees C under 80 MPa sintering pressure. Three MWCNTs with different diameters: thin (slashed circle20-30 nm, CNT Co., Ltd., Korea), thick (slashed circle100 nm, Nano Carbon Technologies Co., Ltd., Japan) and spherical thin (slashed circle20-30 nm, granulated diameter = 1-3 microm, Shimizu Corporation, Japan) were employed for SPS. SEM observation confirmed that these materials maintained the nanosized tube microstructure of raw CNT powder after SPS treatment. The densest monolith was prepared with the spherical MWCNTs. The mechanical properties of this material were estimated by the dynamic hardness test. The elastic modulus of the monolith did not depend on the difference of MWCNTs, but the hardness of spherical MWCNTs was higher than that of thick MWCNTs. The high density and hardness of the spherical MWCNTs were caused by the high packing density during the SPS process because of its spherical granulation. Thus, the spherical MWCNTs were most useful for the MWCNT monolith preparation with the SPS process and its application as a bone substitute material and a bone tissue engineering scaffold material was suggested.

Rapid vacuum sintering: A novel technique for fabricating fluorapatite ceramic scaffolds for bone tissue engineering.

PubMed

Denry, Isabelle; Goudouri, Ourania-Menti; Harless, Jeffrey; Holloway, Julie A

2018-01-01

Macroporous bioceramic scaffolds are often fabricated via the foam replica technique, based on polymeric foam impregnation with a glass slurry, followed by slow heat treatment to allow for drying, polymeric burnout, and sintering of the glass particles. As a consequence, the process is time consuming and complicated by concurrent crystallization of the glass, often leading to incomplete sintering. Our goal was to investigate the effect of heating rate on sintering behavior, architecture, and mechanical properties of fluorapatite-based glass and glass-ceramic scaffolds. Glass scaffolds were prepared and sintered by rapid vacuum sintering (RVS) at 785°C under vacuum at a fast heating rate (55°C/min.) or without vacuum at a slow heating rate (2°C/min.). Two additional groups were further crystallized at 775°C/1 h. XRD confirmed the presence of fluorapatite for crystallized scaffolds. All groups presented interconnected porosity with a pore size in the 500 μm range. Scaffolds produced by RVS exhibited an excellent degree of sintering while scaffolds produced by slow sintering were incompletely sintered. The mean compressive strength was significantly higher for the RVS groups (1.52 ± 0.55 and 1.72 ± 0.61 MPa) compared to the slow-sintered groups (0.54 ± 0.30 and 0.45 ± 0.26 MPa). Meanwhile, the total production time was reduced by more than 12 h by using the RVS technique. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 291-299, 2018. © 2017 Wiley Periodicals, Inc.

Structures and fabrication techniques for solid state electrochemical devices

DOEpatents

Visco, Steven J.; Jacobson, Craig P.; DeJonghe, Lutgard C.

2006-10-10

Low-cost, mechanically strong, highly electronically conductive porous substrates and associated structures for solid-state electrochemical devices, techniques for forming these structures, and devices incorporating the structures provide solid state electrochemical device substrates of novel composition and techniques for forming thin electrode/membrane/electrolyte coatings on the novel or more conventional substrates. In particular, in one aspect the invention provides techniques for co-firing of device substrate (often an electrode) with an electrolyte or membrane layer to form densified electrolyte/membrane films 5 to 20 microns thick. In another aspect, densified electrolyte/membrane films 5 to 20 microns thick may be formed on a pre-sintered substrate by a constrained sintering process. In some cases, the substrate may be a porous metal, alloy, or non-nickel cermet incorporating one or more of the transition metals Cr, Fe and Cu, or alloys thereof.

Pulsed Laser Deposition of BaCe(sub 0.85)Y(sub 0.15)0(sub 3) FILMS

NASA Technical Reports Server (NTRS)

Dynys, F. W.; Sayir, A.

2006-01-01

Pulsed laser deposition has been used to grow nanostructured BaCe(sub 0.85)Y(sub 0.15)0(sub 3) films. The objective is to enhance protonic conduction by reduction of membrane thickness. Sintered samples and laser targets were prepared by sintering BaCe(sub 0.85)Y(sub 0.15)O(sub 3) powders derived by solid state synthesis. Films 2 to 6 m thick were deposited by KrF excimer laser on Si and porous Al2O3 substrates. Nanocrystalline films were fabricated at deposition temperatures of 600-800 C deg at O2 pressure of 30 mTorr and laser fluence of 1.2 J/cm square. Films were characterized by x-ray diffraction, scanning electron microscopy and electrical impedance spectroscopy. Dense single phase BaCe(sub 0.85)Y((sub 0.15) 0(sub 3) films with a columnar growth morphology is observed, preferred crystal growth was found to be dependent upon deposition temperature and substrate type. Electrical conductivity of bulk samples produced by solid state sintering and thin film samples were measured over a temperature range of 100 C deg to 900 C deg in moist argon. Electrical conduction of the fabricated films was 1 to 4 orders of magnitude lower than the sintered bulk samples. With respect to the film growth direction, activation energy for electrical conduction is 3 times higher in the perpendicular direction than the parallel direction.

High Temperature Tolerant Ceramic Composites Having Porous Interphases

DOEpatents

Kriven, Waltraud M.; Lee, Sang-Jin

2005-05-03

In general, this invention relates to a ceramic composite exhibiting enhanced toughness and decreased brittleness, and to a process of preparing the ceramic composite. The ceramic composite comprises a first matrix that includes a first ceramic material, preferably selected from the group including alumina (Al2O3), mullite (3Al2O3.2SiO2), yttrium aluminate garnet (YAG), yttria stabilized zirconia (YSZ), celsian (BaAl2Si2O8) and nickel aluminate (NiAl2O4). The ceramic composite also includes a porous interphase region that includes a substantially non-sinterable material. The non-sinterable material can be selected to include, for example, alumina platelets. The platelets lie in random 3-D orientation and provide a debonding mechanism, which is independent of temperature in chemically compatible matrices. The non-sinterable material induces constrained sintering of a ceramic powder resulting in permanent porosity in the interphase region. For high temperature properties, addition of a sinterable ceramic powder to the non-sinterable material provides sufficiently weak debonding interphases. The ceramic composite can be provided in a variety of forms including a laminate, a fibrous monolith, and a fiber-reinforced ceramic matrix. In the laminated systems, intimate mixing of strong versus tough microstructures were tailored by alternating various matrix-to-interphase thickness ratios to provide the bimodal laminate.

Copper-polydopamine composite derived from bioinspired polymer coating

DOE PAGES

Zhao, Yao; Wang, Hsin; Qian, Bosen; ...

2018-04-01

Metal matrix composites with nanocarbon phases, such carbon nanotube (CNT) and graphene, have shown potentials to achieve improved mechanical, thermal, and electrical properties. However, incorporation of these nanocarbons into the metal matrix usually involves complicated processes. Here, this study explored a new processing method to fabricate copper (Cu) matrix composite by coating Cu powder particles with nanometer-thick polydopamine (PDA) thin films and sintering of the powder compacts. For sintering temperatures between 300°C and 750°C, the Cu-PDA composite samples showed higher electrical conductivity and thermal conductivity than the uncoated Cu samples, which is likely related to the higher mass densities ofmore » the composite samples. After being sintered at 950°C, the thermal conductivity of the Cu-PDA sample was approximately 12% higher than the Cu sample, while the electrical conductivity did not show significant difference. On the other hand, Knoop micro-hardness values were comparable between the Cu-PDA and Cu samples sintered at the same temperatures.« less

Copper-polydopamine composite derived from bioinspired polymer coating

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhao, Yao; Wang, Hsin; Qian, Bosen

Metal matrix composites with nanocarbon phases, such carbon nanotube (CNT) and graphene, have shown potentials to achieve improved mechanical, thermal, and electrical properties. However, incorporation of these nanocarbons into the metal matrix usually involves complicated processes. Here, this study explored a new processing method to fabricate copper (Cu) matrix composite by coating Cu powder particles with nanometer-thick polydopamine (PDA) thin films and sintering of the powder compacts. For sintering temperatures between 300°C and 750°C, the Cu-PDA composite samples showed higher electrical conductivity and thermal conductivity than the uncoated Cu samples, which is likely related to the higher mass densities ofmore » the composite samples. After being sintered at 950°C, the thermal conductivity of the Cu-PDA sample was approximately 12% higher than the Cu sample, while the electrical conductivity did not show significant difference. On the other hand, Knoop micro-hardness values were comparable between the Cu-PDA and Cu samples sintered at the same temperatures.« less

High Thermal Conductivity NARloy-Z-Diamond Composite Combustion Chamber Liner For Advanced Rocket Engines

NASA Technical Reports Server (NTRS)

Bhat, Biliyar N.; Ellis, David; Singh, Jogender

2014-01-01

Advanced high thermal conductivity materials research conducted at NASA Marshall Space Flight Center (MSFC) with state of the art combustion chamber liner material NARloy-Z showed that its thermal conductivity can be increased significantly by adding diamond particles and sintering it at high temperatures. For instance, NARloy-Z containing 40 vol. percent diamond particles, sintered at 975C to full density by using the Field assisted Sintering Technology (FAST) showed 69 percent higher thermal conductivity than baseline NARloy-Z. Furthermore, NARloy-Z-40vol. percent D is 30 percent lighter than NARloy-Z and hence the density normalized thermal conductivity is 140 percent better. These attributes will improve the performance and life of the advanced rocket engines significantly. By one estimate, increased thermal conductivity will directly translate into increased turbopump power up to 2X and increased chamber pressure for improved thrust and ISP, resulting in an expected 20 percent improvement in engine performance. Follow on research is now being conducted to demonstrate the benefits of this high thermal conductivity NARloy-Z-D composite for combustion chamber liner applications in advanced rocket engines. The work consists of a) Optimizing the chemistry and heat treatment for NARloy-Z-D composite, b) Developing design properties (thermal and mechanical) for the optimized NARloy-Z-D, c) Fabrication of net shape subscale combustion chamber liner, and d) Hot fire testing of the liner for performance. FAST is used for consolidating and sintering NARlo-Z-D. The subscale cylindrical liner with built in channels for coolant flow is also fabricated near net shape using the FAST process. The liner will be assembled into a test rig and hot fire tested in the MSFC test facility to determine performance. This paper describes the development of this novel high thermal conductivity NARloy-Z-D composite material, and the advanced net shape technology to fabricate the combustion chamber liner. Properties of optimized NARloy-Z-D composite material will also be presented.

Powder Metallurgy Fabrication of Molybdenum Accelerator Target Disks

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lowden, Richard Andrew; Kiggans Jr., James O.; Nunn, Stephen D.

2015-07-01

Powder metallurgy approaches for the fabrication of accelerator target disks are being examined to support the development of Mo-99 production by NorthStar Medical Technologies, LLC. An advantage of powder metallurgy is that very little material is wasted and, at present, dense, quality parts are routinely produced from molybdenum powder. The proposed targets, however, are thin wafers, 29 mm in diameter with a thickness of 0.5 mm, with very stringent dimensional tolerances. Although tooling can be machined to very high tolerance levels, the operations of powder feed, pressing and sintering involve complicated mechanisms, each of which affects green density and shrinkage,more » and therefore the dimensions and shape of the final product. Combinations of powder morphology, lubricants and pressing technique have been explored to produce target disks with minimal variations in thickness and little or no distortion. In addition, sintering conditions that produce densities for optimum target dissolvability are being determined.« less

Examining Mechanical Strength Characteristics of Selective Inhibition Sintered HDPE Specimens Using RSM and Desirability Approach

NASA Astrophysics Data System (ADS)

Rajamani, D.; Esakki, Balasubramanian

2017-09-01

Selective inhibition sintering (SIS) is a powder based additive manufacturing (AM) technique to produce functional parts with an inexpensive system compared with other AM processes. Mechanical properties of SIS fabricated parts are of high dependence on various process parameters importantly layer thickness, heat energy, heater feedrate, and printer feedrate. In this paper, examining the influence of these process parameters on evaluating mechanical properties such as tensile and flexural strength using Response Surface Methodology (RSM) is carried out. The test specimens are fabricated using high density polyethylene (HDPE) and mathematical models are developed to correlate the control factors to the respective experimental design response. Further, optimal SIS process parameters are determined using desirability approach to enhance the mechanical properties of HDPE specimens. Optimization studies reveal that, combination of high heat energy, low layer thickness, medium heater feedrate and printer feedrate yielded superior mechanical strength characteristics.

Structures And Fabrication Techniques For Solid State Electrochemical Devices

DOEpatents

Visco, Steven J.; Jacobson, Craig P.; DeJonghe, Lutgard C.

2005-12-27

Provided are low-cost, mechanically strong, highly electronically conductive porous substrates and associated structures for solid-state electrochemical devices, techniques for forming these structures, and devices incorporating the structures. The invention provides solid state electrochemical device substrates of novel composition and techniques for forming thin electrode/membrane/electrolyte coatings on the novel or more conventional substrates. In particular, in one embodiment the invention provides techniques for co-firing of device substrate (often an electrode) with an electrolyte or membrane layer to form densified electrolyte/membrane films 5 to 20 microns thick. In another embodiment, densified electrolyte/membrane films 5 to 20 microns thick may be formed on a pre-sintered substrate by a constrained sintering process. In some cases, the substrate may be a porous metal, alloy, or non-nickel cermet incorporating one or more of the transition metals Cr, Fe, Cu and Ag, or alloys thereof.

Structures and fabrication techniques for solid state electrochemical devices

DOEpatents

Visco, Steven J.; Jacobson, Craig P.; DeJonghe, Lutgard C.

2003-08-12

Provided are low-cost, mechanically strong, highly electronically conductive porous substrates and associated structures for solid-state electrochemical devices, techniques for forming these structures, and devices incorporating the structures. The invention provides solid state electrochemical device substrates of novel composition and techniques for forming thin electrode/membrane/electrolyte coatings on the novel or more conventional substrates. In particular, in one embodiment the invention provides techniques for co-firing of device substrate (often an electrode) with an electrolyte or membrane layer to form densified electrolyte/membrane films 5 to 20 microns thick. In another embodiment, densified electrolyte/membrane films 5 to 20 microns thick may be formed on a pre-sintered substrate by a constrained sintering process. In some cases, the substrate may be a porous metal, alloy, or non-nickel cermet incorporating one or more of the transition metals Cr, Fe, Cu and Ag, or alloys thereof.

Effect of Reduced Meal Frequency during Ramadan Fasting on Retinal and Choroidal Thickness.

PubMed

Ersan, Ismail; Tufan, Hasan Ali; Arikan, Sedat; Kara, Selcuk; Gencer, Baran; Hondur, Ahmet Murat

2017-01-01

To evaluate the effects of Ramadan fasting on central foveal thickness (CFT) and subfoveal choroidal thickness (SFCT) in healthy individuals using enhanced depth imaging optical coherence tomography (EDI-OCT). The EDI-OCT scans of 42 healthy individuals obtained after about 12 hours of fasting on at least the twenty-first consecutive day of fasting were compared to scans of the same patients taken one month after the last day they had fasted. CFT values were similar for both time periods (p > 0.05). The SFCT was significantly higher after consecutive fasting days towards the end of Ramadan, compared to the SFCT after one month of no fasting (one month after Ramadan ended) (p < 0.001). Ramadan fasting may lead to a significant increase in subfoveal choroidal thickness without affecting the central foveal thickness.

Ceramic Life Prediction Methodology.

DTIC Science & Technology

1986-03-01

stress rupture data were collected on two materials, a sintered silicon nitride and a lithium-aluminum-silicate. The fast fracture data was presented...graphically in the form of Weibull plots of percent failed versus failure stress . The stress rupture results were presented in tabular form. Photo...micrographs were presented to illustrate the fracture surfaces of fast fracture and stress rupture failures. A program of specimen development was coaducted

Direct metal laser sintering (DMLS) of a customized titanium mesh for prosthetically guided bone regeneration of atrophic maxillary arches.

PubMed

Ciocca, L; Fantini, M; De Crescenzio, F; Corinaldesi, G; Scotti, R

2011-11-01

This study describes a protocol for the direct manufacturing of a customized titanium mesh using CAD-CAM procedures and rapid prototyping to augment maxillary bone and minimize surgery when severe atrophy or post-oncological deformities are present. Titanium mesh and particulate autogenous plus bovine demineralised bone were planned for patient rehabilitation. Bone augmentation planning was performed using the pre-op CT data set in relation to the prosthetic demands, minimizing the bone volume to augment at the minimum necessary for implants. The containment mesh design was used to prototype the 0.6 mm thickness customized titanium mesh, by direct metal laser sintering. The levels of regenerated bone were calculated using the post-op CT data set, through comparison with the pre-op CT data set. The mean vertical height difference of the crestal bone was 2.57 mm, while the mean buccal-palatal dimension of thickness difference was 3.41 mm. All planned implants were positioned after an 8 month healing period using two-step implant surgery, and finally restored with a partial fixed prosthesis. We present a viable and reproducible method to determine the correct bone augmentation prior to implant placement and CAD-CAM to produce a customized direct laser-sintered titanium mesh that can be used for bone regeneration.

Oxidation resistant slurry coating for carbon-based materials

NASA Technical Reports Server (NTRS)

Smialek, J. L.; Rybicki, G. C. (Inventor)

1985-01-01

An oxidation resistant coating is produced on carbon-base materials, and the same processing step effects an infiltration of the substrate with silicon containing material. The process comprises making a slurry of nickel and silicon powders in a nitrocellulose lacquer, spraying onto the graphite or carbon-carbon substrate, and sintering in vacuum to form a fused coating that wets and covers the surface as well as penetrates into the pores of the substrate. Optimum wetting and infiltration occurs in the range of Ni-60 w/o Si to Ni-90 w/o Si with deposited thicknesses of 25-100 mg/sq. cm. Sintering temperatures of about 1200 C to about 1400 C are used, depending on the melting point of the specific coating composition. The sintered coating results in Ni-Si intermetallic phases and SiC, both of which are highly oxidation resistant.

The observation of resistivity change on the ultrasonic treated Fe-Cr ODS sinter alloy under magnetic field influence

NASA Astrophysics Data System (ADS)

Silalahi, Marzuki; Purwanto, Setyo; Mujamilah; Dimyati, Arbi

2018-03-01

About the observation of resistivity change on the ultrasonic treated Fe-Cr ODS sinter alloy under magnetic field influence. This paper reported about the observation of the resistivity change in the ultrasonic pre-treated Fe-Cr ODS sinter alloy under the influence of magnetic field at the Center for Science and Technology of Advanced Material, Nuclear Energy Agency of Indonesia. Fe-Cr ODS alloy were sinthesized by vacuum sintering of Fe- and Cr-powder dispersed Y2O3. However, before sintering the powder mixture was subjected to the irradiation process by ultrasonic for 50 hours at 20 kHz and then isostatic pressed up to 50.91 MPa to form a coin of 10 mm in diameter. LCR meassurement revealed the decreasing of resistivity about 3 times by increasing of applied magnetic field from 0 to 70 mT. In addition, VSM meassurement was performed on both as powder material and as sintered sample. The results showed increasing the magnetization with increasing magnetic field and the curve exhibits almost exact symmetry S-form with small hysterese indicating fast changing magnetization and demagnetization capability without energy loss. This opens strong speculations about the existence of magnetoresistant property of the material which is important for many application in field of sensors or electro magnetic valves.

Development of an in-situ multi-component reinforced Al-based metal matrix composite by direct metal laser sintering technique — Optimization of process parameters

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ghosh, Subrata Kumar, E-mail: subratagh82@gmail.com; Bandyopadhyay, Kaushik; Saha, Partha

2014-07-01

In the present investigation, an in-situ multi-component reinforced aluminum based metal matrix composite was fabricated by the combination of self-propagating high-temperature synthesis and direct metal laser sintering process. The different mixtures of Al, TiO{sub 2} and B{sub 4}C powders were used to initiate and maintain the self-propagating high-temperature synthesis by laser during the sintering process. It was found from the X-ray diffraction analysis and scanning electron microscopy that the reinforcements like Al{sub 2}O{sub 3}, TiC, and TiB{sub 2} were formed in the composite. The scanning electron microscopy revealed the distribution of the reinforcement phases in the composite and phase identities.more » The variable parameters such as powder layer thickness, laser power, scanning speed, hatching distance and composition of the powder mixture were optimized for higher density, lower porosity and higher microhardness using Taguchi method. Experimental investigation shows that the density of the specimen mainly depends upon the hatching distance, composition and layer thickness. On the other hand, hatching distance, layer thickness and laser power are the significant parameters which influence the porosity. The composition, laser power and layer thickness are the key influencing parameters for microhardness. - Highlights: • The reinforcements such as Al{sub 2}O{sub 3}, TiC, and TiB{sub 2} were produced in Al-MMC through SHS. • The density is mainly influenced by the material composition and hatching distance. • Hatching distance is the major influencing parameter on porosity. • The material composition is the significant parameter to enhance the microhardness. • The SEM micrographs reveal the distribution of TiC, TiB{sub 2} and Al{sub 2}O{sub 3} in the composite.« less

Characterization of the porous structures of the green body and sintered biomedical titanium scaffolds with micro-computed tomography

DOE Office of Scientific and Technical Information (OSTI.GOV)

Arifvianto, B., E-mail: b.arifvianto@tudelft.nl; L

The present research was aimed at gaining an understanding of the porous structure changes from the green body through water leaching and sintering to titanium scaffolds. Micro-computed tomography (micro-CT) was performed to generate 3D models of titanium scaffold preforms containing carbamide space-holding particles and sintered scaffolds containing macro- and micro-pores. The porosity values and structural parameters were determined by means of image analysis. The result showed that the porosity values, macro-pore sizes, connectivity densities and specific surface areas of the titanium scaffolds sintered at 1200 °C for 3 h did not significantly deviate from those of the green structures withmore » various volume fractions of the space holder. Titanium scaffolds with a maximum specific surface area could be produced with an addition of 60–65 vol% carbamide particles to the matrix powder. The connectivity of pores inside the scaffold increased with rising volume fraction of the space holder. The shrinkage of the scaffolds prepared with > 50 vol% carbamide space holder, occurring during sintering, was caused by the reductions of macro-pore sizes and micro-pore sizes as well as the thickness of struts. In conclusion, the final porous structural characteristics of titanium scaffolds could be estimated from those of the green body. - Highlights: •Porous structures of green body and sintered titanium scaffolds was studied. •Porous structures of both samples were quantitatively characterized with micro-CT. •Porous structures of scaffolds could be controlled from the green body. •Shrinkage mechanisms of titanium scaffolds during sintering was established.« less

Sintering and Microstructure of BaTiO3 Nano Particles Synthesized by Molten Salt Method.

PubMed

Lee, Chang-Hyun; Shin, Hyo-Soon; Yeo, Dong-Hun; Ha, Gook-Hyun; Nahm, Sahn

2016-05-01

In order to establish thinner dielectric layers in thick film electronic components such as MLCC (Multilayer ceramic capacitor), BaTiO3 nanoparticles have been utilized. However, studies on the synthesis of nanoparticles smaller than 20 nm, the characteristics of the BaTiO3 powder, and the powder's sintering are lacking. Therefore, this paper aims to synthesize BaTiO3 particles smaller than 20 nm by using the molten salt method and evaluate the microstructure and dielectric properties by varying the sintering temperature from 750 degrees C to 1200 degrees C. Through the molten salt method and by using KOH-KCl mixed salt, 20 nm BaTiO3 powder was synthesized at a low temperature of 150 degrees C. Sintering the pellets formed from the synthesized 20 nm BaTiO3 nano powder led to the observation of an unusual phenomenon where the particles grew to approximate sizes below 850 degrees C where densification progressed. At sintering temperatures above 950 degrees C, particles that expanded into rod shapes were observed and these particles were identified to be unreacted TiO2 based on the results of the EDX (Energy Dispersive X-ray Spectroscopy) analysis and phase analysis results.

The Influence of Sintering Temperature on the Microstructure and Thermoelectric Properties of n-Type Bi2Te3- x Se x Nanomaterials

NASA Astrophysics Data System (ADS)

Du, Y.; Cai, K. F.; Li, H.; An, B. J.

2011-05-01

Pure Bi2Te3 and Bi2Se3 nanopowders were hydrothermally synthesized, and n-type Bi2Te3- x Se x bulk samples were prepared by hot pressing a mixture of Bi2Te3 and Bi2Se3 nanopowders at 623 K, 648 K or 673 K and 80 MPa in vacuum. The phase composition of the powders and bulk samples were characterized by x-ray diffraction. The morphology of the powders was examined by transmission electron microscopy. The microstructure and composition of the bulk samples were characterized by field-emission scanning electron microscopy and energy-dispersive x-ray spectroscopy, respectively. The density of the samples increased with sintering temperature. The samples were somewhat oxidized, and the amount of oxide (Bi2TeO5) present increased with sintering temperature. The samples consisted of sheet-like grains with a thickness less than 100 nm. Seebeck coefficient, electrical conductivity, and thermal conductivity of the samples were measured from room temperature up to 573 K. Throughout the temperature range investigated, the sample sintered at 623 K had a higher power factor than the samples sintered at 648 K or 673 K.

Experimental sintering of ash at conduit conditions and implications for the longevity of tuffisites

NASA Astrophysics Data System (ADS)

Gardner, James E.; Wadsworth, Fabian B.; Llewellin, Edward W.; Watkins, James M.; Coumans, Jason P.

2018-03-01

Escape of gas from magma in the conduit plays a crucial role in mitigating explosivity. Tuffisite veins—ash-filled cracks that form in and around volcanic conduits—represent important gas escape pathways. Sintering of the ash infill decreases its porosity, eventually forming dense glass that is impermeable to gas. We present an experimental investigation of surface tension-driven sintering and associated densification of rhyolitic ash under shallow conduit conditions. Suites of isothermal (700-800 °C) and isobaric H2O pressure (20 and 40 MPa) experiments were run for durations of 5-90 min. Obsidian powders with two different size distributions were used: 1-1600 μm (mean size = 89 μm), and 63-400 μm (mean size = 185 μm). All samples evolved similarly through four textural phases: phase 1—loose and cohesion-less particles; phase 2—particles sintered at contacts and surrounded by fully connected tortuous pore space of up to 40% porosity; phase 3—continuous matrix of partially coalesced particles that contain both isolated spherical vesicles and connected networks of larger, contorted vesicles; phase 4—dense glass with 2-5% fully isolated vesicles that are mainly spherical. Textures evolve faster at higher temperature and higher H2O pressure. Coarse samples sinter more slowly and contain fewer, larger vesicles when fully sintered. We quantify the sintering progress by measuring porosity as a function of experimental run-time, and find an excellent collapse of data when run-time is normalized by the sintering timescale {λ}_s=η \\overline{R}/σ , where η is melt viscosity, \\overline{R} is mean particle radius, and σ is melt-gas surface tension. Because timescales of diffusive H2O equilibration are generally fast compared to those of sintering, the relevant melt viscosity is calculated from the solubility H2O content at experimental temperature and pressure. We use our results to develop a framework for estimating ash sintering rates under shallow conduit conditions, and predict that sintering of ash to dense glass can seal tuffisites in minutes to hours, depending on pressure (i.e., depth), temperature, and ash size.

Additive manufacturing technology (direct metal laser sintering) as a novel approach to fabricate functionally graded titanium implants: preliminary investigation of fabrication parameters.

PubMed

Lin, Wei-Shao; Starr, Thomas L; Harris, Bryan T; Zandinejad, Amirali; Morton, Dean

2013-01-01

This article describes the preliminary findings of the mechanical properties of functionally graded titanium with controlled distribution of porosity and a reduced Young's modulus on the basis of a computeraided design (CAD) file, using the rapid-prototyping, direct metal laser sintering (DMLS) technique. Sixty specimens of Ti-6Al-4V were created using a DMLS machine (M270) following the standard for tensile testing of metals. One group was fabricated with only 170 W of laser energy to create fully dense specimens (control group). The remaining specimens all featured an outer fully dense "skin" layer and a partially sintered porous inner "core" region. The outer "skin" of each specimen was scanned at 170 W and set at a thickness of 0.35, 1.00, or 1.50 mm for different specimen groups. The inner "core" of each specimen was scanned at a lower laser power (43 or 85 W). The partially sintered core was clearly visible in all specimens, with somewhat greater porosity with the lower laser power. However, the amount of porosity in the core region was not related to the laser power alone; thinner skin layers resulted in higher porosity for the same power values in the core structure. The lowest Young's modulus achieved, 35 GPa, is close to that of bone and was achieved with a laser power of 43 W and a skin thickness of 0.35 mm, producing a core that comprised 74% of the total volume. Additive manufacturing technology may provide an efficient alternative way to fabricate customized dental implants based on a CAD file with a functionally graded structure that may minimize stress shielding and improve the long-term performance of dental implants.

Perovskite solar cell with an efficient TiO₂ compact film.

PubMed

Ke, Weijun; Fang, Guojia; Wang, Jing; Qin, Pingli; Tao, Hong; Lei, Hongwei; Liu, Qin; Dai, Xin; Zhao, Xingzhong

2014-09-24

A perovskite solar cell with a thin TiO2 compact film prepared by thermal oxidation of sputtered Ti film achieved a high efficiency of 15.07%. The thin TiO2 film prepared by thermal oxidation is very dense and inhibits the recombination process at the interface. The optimum thickness of the TiO2 compact film prepared by thermal oxidation is thinner than that prepared by spin-coating method. Also, the TiO2 compact film and the TiO2 porous film can be sintered at the same time. This one-step sintering process leads to a lower dark current density, a lower series resistance, and a higher recombination resistance than those of two-step sintering. Therefore, the perovskite solar cell with the TiO2 compact film prepared by thermal oxidation has a higher short-circuit current density and a higher fill factor.

Vacuum Compatibility of Laser-Sintered Metals

NASA Astrophysics Data System (ADS)

Rivera, W. F.; Romero-Talamas, C. A.; Bates, E. M.; Birmingham, W. J.; Quinley, M.; Woodruff, S.; Stuber, J. E.; Sieck, P. E.; Melnik, P. A.

2016-10-01

We present the design and results of a mass spectrometry system used to assess vacuum compatibility of selective laser-sintered parts. The parts are disks with a thickness of 0.20 cm and a diameter of 8.25 cm, and are made of aluminum, stainless steel, inconel, and titanium. From preliminary results, titanium had the lowest partial pressure for hydrogen. Outgassing from laser-sintered parts is compared against parts with similar surface area that are manufactured with traditional methods. Outgassing is also measured while the part is heated, emulating the conditions at the edge of high temperature plasma confinement chambers. Each part is placed on a heated container that can vary in temperature inside the mass spectrometer's vacuum chamber. The partial pressures of elements up to 200 atomic mass units are analyzed to obtain outgassing data from each sample. This work supported under DOE SBIR Grant DE SC0011858.

ALD coating of nuclear fuel actinides materials

DOEpatents

Yacout, A. M.; Pellin, Michael J.; Yun, Di; Billone, Mike

2017-09-05

The invention provides a method of forming a nuclear fuel pellet of a uranium containing fuel alternative to UO.sub.2, with the steps of obtaining a fuel form in a powdered state; coating the fuel form in a powdered state with at least one layer of a material; and sintering the powdered fuel form into a fuel pellet. Also provided is a sintered nuclear fuel pellet of a uranium containing fuel alternative to UO.sub.2, wherein the pellet is made from particles of fuel, wherein the particles of fuel are particles of a uranium containing moiety, and wherein the fuel particles are coated with at least one layer between about 1 nm to about 4 nm thick of a material using atomic layer deposition, and wherein the at least one layer of the material substantially surrounds each interfacial grain barrier after the powdered fuel form has been sintered.

Pulsed Laser Deposition of High Temperature Protonic Films

NASA Technical Reports Server (NTRS)

Dynys, Fred W.; Berger, M. H.; Sayir, Ali

2006-01-01

Pulsed laser deposition has been used to fabricate nanostructured BaCe(0.85)Y(0.15)O3- sigma) films. Protonic conduction of fabricated BaCe(0.85)Y(0.15)O(3-sigma) films was compared to sintered BaCe(0.85)Y(0.15)O(3-sigma). Sintered samples and laser targets were prepared by sintering BaCe(0.85)Y(0.15)O(3-sigma) powders derived by solid state synthesis. Films 1 to 8 micron thick were deposited by KrF excimer laser on porous Al2O3 substrates. Thin films were fabricated at deposition temperatures of 700 to 950 C at O2 pressures up to 200 mTorr using laser pulse energies of 0.45 - 0.95 J. Fabricated films were characterized by X-ray diffraction, electron microscopy and electrical impedance spectroscopy. Single phase BaCe(0.85)Y(0.15)O(3-sigma) films with a columnar growth morphology are observed with preferred crystal growth along the [100] or [001] direction. Results indicate [100] growth dependence upon laser pulse energy. Electrical conductivity of bulk samples produced by solid state sintering and thin film samples were measured over a temperature range of 100 C to 900 C. Electrical conduction behavior was dependent upon film deposition temperature. Maximum conductivity occurs at deposition temperature of 900 oC; the electrical conductivity exceeds the sintered specimen. All other deposited films exhibit a lower electrical conductivity than the sintered specimen. Activation energy for electrical conduction showed dependence upon deposition temperature, it varied

2D all-solid state fabric supercapacitor fabricated via an all solution process for use in smart textiles

NASA Astrophysics Data System (ADS)

Jang, Yunseok; Jo, Jeongdai; Woo, Kyoohee; Lee, Seung-Hyun; Kwon, Sin; Kim, Kwang-Young; Kang, Dongwoo

2017-05-01

We propose a method to fabricate a supercapacitor for smart textiles using silver (Ag) nanoparticle (NP) ink, simple spray patterning systems, and intense pulsed light (IPL) sintering systems. The Ag NP current collectors provided as high conductivity as the metal current collectors. The spray patterning technique is useful for fabricating supercapacitors because it is simple, fast, and cheap. IPL systems reduced the sintering temperature of Ag NPs and prevented thermal damage to the textiles during the Ag NP sintering process. The two-dimensional (2D) all-solid state fabric supercapacitor with an interdigitated configuration, developed here, exhibited a specific capacitance of 25.7 F/g and an energy density of 1.5 Wh/kg at a power density of 64.3 W/kg. These results support the utility of our proposed method in the development of energy textiles.

Improved Tubulars for Better Economics in Deep Gas Well Drilling Using Microwave Technology

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dinesh Agrawal

2006-09-30

The main objective of the entire research program has been to improve the rate-of-penetration in deep hostile environments by improving the life cycle and performance of coiled-tubing, an important component of a deep well drilling system for oil and gas exploration, by utilizing the latest developments in the microwave materials technology. Based on the results of the Phase I and insurmountable difficulties faced in the extrusion and de-waxing processes, the approach of achieving the goals of the program was slightly changed in the Phase II in which an approach of microwave sintering combined with Cold Isostatic Press (CIP) and joiningmore » (by induction or microwave) has been adopted. This process can be developed into a semicontinuous sintering process if the CIP can produce parts fast enough to match the microwave sintering rates. The main objective of the Phase II research program is to demonstrate the potential to economically manufacture microwave processed coiled tubing with improved performance for extended useful life under hostile coiled tubing drilling conditions. After the completion of the Phase II, it is concluded that scale up and sintering of a thin wall common O.D. size tubing that is widely used in the market is still to be proved and further experimentation and refinement of the sintering process is needed in Phase III. Actual manufacturing capability of microwave sintered, industrial quality, full length tubing will most likely require several million dollars of investment.« less

Improved Tubulars for Better Economics in Deep Gas Well Drilling using Microwave Technology

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dinesh Agrawal; Paul Gigl; Mark Hunt

2007-07-31

The main objective of the entire research program has been to improve the rate-of-penetration in deep hostile environments by improving the life cycle and performance of coiled-tubing, an important component of a deep well drilling system for oil and gas exploration, by utilizing the latest developments in the microwave materials technology. Based on the results of the Phase I and insurmountable difficulties faced in the extrusion and de-waxing processes, the approach of achieving the goals of the program was slightly changed in the Phase II in which an approach of microwave sintering combined with Cold Isostatic Press (CIP) and joiningmore » (by induction or microwave) has been adopted. This process can be developed into a semicontinuous sintering process if the CIP can produce parts fast enough to match the microwave sintering rates. The main objective of the Phase II research program is to demonstrate the potential to economically manufacture microwave processed coiled tubing with improved performance for extended useful life under hostile coiled tubing drilling conditions. After the completion of the Phase II, it is concluded that scale up and sintering of a thin wall common O.D. size tubing that is widely used in the market is still to be proved and further experimentation and refinement of the sintering process is needed in Phase III. Actual manufacturing capability of microwave sintered, industrial quality, full length tubing will most likely require several million dollars of investment.« less

Effect of Mg(2+) doping on beta-alpha phase transition in tricalcium phosphate (TCP) bioceramics.

PubMed

Frasnelli, Matteo; Sglavo, Vincenzo M

2016-03-01

The beta to alpha transition in tricalcium phosphate (TCP) bioceramics containing different amount of magnesium was studied in the present work. Mg-doped TCP powder was obtained by solid-state reaction starting from pure calcium carbonate, ammonium phosphate dibasic and magnesium oxide powders. The β to α transformation temperature was identified by dilatometric and thermo-differential analyses. Small pellets produced by uniaxial pressing samples were employed to study the influence of Mg(2+) on the transition kinetic, after sintering at 1550°C and subsequent slow or fast cooling down to room temperature. The evolution of β- and α-TCP crystalline phases during each thermal treatment was determined by X-ray powder diffraction analysis combined with Rietveld method-based software An annealing treatment, suitable to reconvert metastable α phase to the more clinically suitable β phase, was also investigated. It is shown that the presence of magnesium within the TCP lattice strongly influences the kinetic of the β⇆α phase transition, promoting the spontaneous α→β reconversion even upon fast cooling, or slowing down the β→α transition during heating. Similarly, it allows the α→β transformation in TCP sintered components by optimized annealing treatment at 850°C. This work concerns the effect of Mg(2+) doping on the β→α phase reconstructive transition in tricalcium phosphate (TCP), one of the most important bio-resorbable materials for bone tissue regeneration. The transition occurs upon the sintering process and is has been shown to be strongly irreversible upon cooling, leading to technological issues such as poor mechanical properties and excessive solubility due to the presence of metastable α-phase. This paper points out the kinetic contribution of Mg(2+) on the spontaneous α→β reconversion also upon fast cooling (i.e. quenching). Moreover, an annealing treatment has been shown to be beneficial to remove the retained α-phase in sintered TCP components, the presence of Mg promoting the reconversion process. Copyright © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Combustion chamber struts can be effectively transpiration cooled

NASA Technical Reports Server (NTRS)

Palmer, G. H.

1966-01-01

Vapor-deposited sintering technique increases the feasible temperature range of transpiration-cooled structural members in combustion chambers. This technique produces a porous mass of refractory metal wires around a combustion chamber structural member. This mass acts as a transpiration-cooled surface for a thick-walled tube.

Scientific Research Program for Power, Energy, and Thermal Technologies. Task Order 0001: Power, Thermal and Control Technologies and Processes Experimental Research

DTIC Science & Technology

2015-08-01

and (b) physical property data collection Following film deposition (via PLD or radio frequency magnetron sputtering), to prevent unwanted...carried out using an in-house radio frequency induction hot press under vacuum at ~1 mTorr and temperatures of 650, 750 and 850 °C. Sintering time was 2...tape thickness 23 µm, lamination stack thickness 11 mm). Simulated magnetic flux density inside the core was ~0.1 T, and operating frequency was

Fast femtosecond laser ablation for efficient cutting of sintered alumina substrates

NASA Astrophysics Data System (ADS)

Oosterbeek, Reece N.; Ward, Thomas; Ashforth, Simon; Bodley, Owen; Rodda, Andrew E.; Simpson, M. Cather

2016-09-01

Fast, accurate cutting of technical ceramics is a significant technological challenge because of these materials' typical high mechanical strength and thermal resistance. Femtosecond pulsed lasers offer significant promise for meeting this challenge. Femtosecond pulses can machine nearly any material with small kerf and little to no collateral damage to the surrounding material. The main drawback to femtosecond laser machining of ceramics is slow processing speed. In this work we report on the improvement of femtosecond laser cutting of sintered alumina substrates through optimisation of laser processing parameters. The femtosecond laser ablation thresholds for sintered alumina were measured using the diagonal scan method. Incubation effects were found to fit a defect accumulation model, with Fth,1=6.0 J/cm2 (±0.3) and Fth,∞=2.5 J/cm2 (±0.2). The focal length and depth, laser power, number of passes, and material translation speed were optimised for ablation speed and high quality. Optimal conditions of 500 mW power, 100 mm focal length, 2000 μm/s material translation speed, with 14 passes, produced complete cutting of the alumina substrate at an overall processing speed of 143 μm/s - more than 4 times faster than the maximum reported overall processing speed previously achieved by Wang et al. [1]. This process significantly increases processing speeds of alumina substrates, thereby reducing costs, making femtosecond laser machining a more viable option for industrial users.

Fabrication of Lightweight Radiation Shielding Composite Materials by Field Assisted Sintering Technique (FAST)

NASA Technical Reports Server (NTRS)

Prasad, Narasimha; Trivedi, Sudhir; Chen, Henry; Kutcher, Susan; Zhang, Dajie; Singh, Jogender

2017-01-01

Advances in radiation shielding technologies are needed to protect humans and electronic components from all threats of space radiation over long durations. In this paper, we report on the use of the innovative and novel fabrication technology known as Field Assisted Sintering Technology (FAST) to fabricate lightweight material with enhanced radiation shielding strength to safeguard humans and electronics suitable for next generation space exploration missions. The base materials we investigated were aluminum (Al), the current standard material for space hardware, and Ultra-High Molecular Weight Polyethylene (UHMWPE), which has high hydrogen content and resistance to nuclear reaction from neutrons, making it a good shielding material for both gamma radiation and particles. UHMWPE also has high resistance to corrosive chemicals, extremely low moisture sensitivity, very low coefficient of friction, and high resistance to abrasion. We reinforced the base materials by adding high density (ie, high atomic weight) metallic material into the composite. These filler materials included: boron carbide (B4C), tungsten (W), tungsten carbide (WC) and gadolinium (Gd).

Process Parameter Optimization of Extrusion-Based 3D Metal Printing Utilizing PW-LDPE-SA Binder System.

PubMed

Ren, Luquan; Zhou, Xueli; Song, Zhengyi; Zhao, Che; Liu, Qingping; Xue, Jingze; Li, Xiujuan

2017-03-16

Recently, with a broadening range of available materials and alteration of feeding processes, several extrusion-based 3D printing processes for metal materials have been developed. An emerging process is applicable for the fabrication of metal parts into electronics and composites. In this paper, some critical parameters of extrusion-based 3D printing processes were optimized by a series of experiments with a melting extrusion printer. The raw materials were copper powder and a thermoplastic organic binder system and the system included paraffin wax, low density polyethylene, and stearic acid (PW-LDPE-SA). The homogeneity and rheological behaviour of the raw materials, the strength of the green samples, and the hardness of the sintered samples were investigated. Moreover, the printing and sintering parameters were optimized with an orthogonal design method. The influence factors in regard to the ultimate tensile strength of the green samples can be described as follows: infill degree > raster angle > layer thickness. As for the sintering process, the major factor on hardness is sintering temperature, followed by holding time and heating rate. The highest hardness of the sintered samples was very close to the average hardness of commercially pure copper material. Generally, the extrusion-based printing process for producing metal materials is a promising strategy because it has some advantages over traditional approaches for cost, efficiency, and simplicity.

Process Parameter Optimization of Extrusion-Based 3D Metal Printing Utilizing PW–LDPE–SA Binder System

PubMed Central

Ren, Luquan; Zhou, Xueli; Song, Zhengyi; Zhao, Che; Liu, Qingping; Xue, Jingze; Li, Xiujuan

2017-01-01

Recently, with a broadening range of available materials and alteration of feeding processes, several extrusion-based 3D printing processes for metal materials have been developed. An emerging process is applicable for the fabrication of metal parts into electronics and composites. In this paper, some critical parameters of extrusion-based 3D printing processes were optimized by a series of experiments with a melting extrusion printer. The raw materials were copper powder and a thermoplastic organic binder system and the system included paraffin wax, low density polyethylene, and stearic acid (PW–LDPE–SA). The homogeneity and rheological behaviour of the raw materials, the strength of the green samples, and the hardness of the sintered samples were investigated. Moreover, the printing and sintering parameters were optimized with an orthogonal design method. The influence factors in regard to the ultimate tensile strength of the green samples can be described as follows: infill degree > raster angle > layer thickness. As for the sintering process, the major factor on hardness is sintering temperature, followed by holding time and heating rate. The highest hardness of the sintered samples was very close to the average hardness of commercially pure copper material. Generally, the extrusion-based printing process for producing metal materials is a promising strategy because it has some advantages over traditional approaches for cost, efficiency, and simplicity. PMID:28772665

Constrained Sintering in Fabrication of Solid Oxide Fuel Cells

PubMed Central

Lee, Hae-Weon; Park, Mansoo; Hong, Jongsup; Kim, Hyoungchul; Yoon, Kyung Joong; Son, Ji-Won; Lee, Jong-Ho; Kim, Byung-Kook

2016-01-01

Solid oxide fuel cells (SOFCs) are inevitably affected by the tensile stress field imposed by the rigid substrate during constrained sintering, which strongly affects microstructural evolution and flaw generation in the fabrication process and subsequent operation. In the case of sintering a composite cathode, one component acts as a continuous matrix phase while the other acts as a dispersed phase depending upon the initial composition and packing structure. The clustering of dispersed particles in the matrix has significant effects on the final microstructure, and strong rigidity of the clusters covering the entire cathode volume is desirable to obtain stable pore structure. The local constraints developed around the dispersed particles and their clusters effectively suppress generation of major process flaws, and microstructural features such as triple phase boundary and porosity could be readily controlled by adjusting the content and size of the dispersed particles. However, in the fabrication of the dense electrolyte layer via the chemical solution deposition route using slow-sintering nanoparticles dispersed in a sol matrix, the rigidity of the cluster should be minimized for the fine matrix to continuously densify, and special care should be taken in selecting the size of the dispersed particles to optimize the thermodynamic stability criteria of the grain size and film thickness. The principles of constrained sintering presented in this paper could be used as basic guidelines for realizing the ideal microstructure of SOFCs. PMID:28773795

Modeling of submicrometer aerosol penetration through sintered granular membrane filters.

PubMed

Marre, Sonia; Palmeri, John; Larbot, André; Bertrand, Marielle

2004-06-01

We present a deep-bed aerosol filtration model that can be used to estimate the efficiency of sintered granular membrane filters in the region of the most penetrating particle size. In this region the capture of submicrometer aerosols, much smaller than the filter pore size, takes place mainly via Brownian diffusion and direct interception acting in synergy. By modeling the disordered sintered grain packing of such filters as a simple cubic lattice, and mapping the corresponding 3D connected pore volume onto a discrete cylindrical pore network, the efficiency of a granular filter can be estimated, using new analytical results for the efficiency of cylindrical pores. This model for aerosol penetration in sintered granular filters includes flow slip and the kinetics of particle capture by the pore surface. With a unique choice for two parameters, namely the structural tortuosity and effective kinetic coefficient of particle adsorption, this semiempirical model can account for the experimental efficiency of a new class of "high-efficiency particulate air" ceramic membrane filters as a function of particle size over a wide range of filter thickness and texture (pore size and porosity) and operating conditions (face velocity).

DOE Office of Scientific and Technical Information (OSTI.GOV)

None

Films of cadmium sulfide and cadmium telluride have been produced by screen printing and sintering. Cadmium sulfide films ten microns thick had a resistivity in the 10 ohm-cm range. A technique was developed for forming a cadmium telluride layer on top of a cadmium sulfide layer. Process control and device preparation are areas requiring further study.

Heat Transfer Measurements for a Film Cooled Turbine Vane Cascade

DTIC Science & Technology

2008-05-01

were made of 0.75 in (1.91 cm) thick clear acrylic. The test vanes were made by rapid prototyping technique of a Duraform polyamide sintering material...conditions using the following definition: pVc hSt ρ = (4) We acquired pressure survey measurements under steady state conditions. Total pressure

Results of thermal test of metallic molybdenum disk target and fast-acting valve testing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Virgo, M.; Chemerisov, S.; Gromov, R.

2016-12-01

This report describes the irradiation conditions for thermal testing of helium-cooled metallic disk targets that was conducted on March 9, 2016, at the Argonne National Laboratory electron linac. The four disks in this irradiation were pressed and sintered by Oak Ridge National Laboratory from molybdenum metal powder. Two of those disks were instrumented with thermocouples. Also reported are results of testing a fast-acting-valve system, which was designed to protect the accelerator in case of a target-window failure.

Gas response properties of citrate gel synthesized nanocrystalline MgFe{sub 2}O{sub 4}: Effect of sintering temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Patil, J.Y.; Mulla, I.S.; Suryavanshi, S.S., E-mail: sssuryavanshi@rediffmail.com

2013-02-15

Graphical abstract: Display Omitted Highlights: ► Synthesis of nanocrystalline MgFe{sub 2}O{sub 4} by economical citrate gel combustion method. ► Structural, morphological, and gas response properties of MgFe{sub 2}O{sub 4}. ► Enhancement in selectivity of MgFe{sub 2}O{sub 4} towards LPG with sintering temperature. ► Use of MgFe{sub 2}O{sub 4} to detect different gases at different operating temperatures. -- Abstract: Spinel type MgFe{sub 2}O{sub 4} material was synthesized by citrate gel combustion method. The effect of sintering temperature on structural, morphological, and gas response properties was studied. The powder X-ray diffraction pattern and transmission electron microscope study confirms nanocrystalline spinel structure ofmore » the synthesized powder. The material was tested for response properties to various reducing gases like liquid petroleum gas (LPG), acetone, ethanol, and ammonia. The results demonstrated n-type semiconducting behavior of MgFe{sub 2}O{sub 4} material. It was revealed that MgFe{sub 2}O{sub 4} sintered at 973 K was most sensitive to LPG at 648 K and to acetone at 498 K. However MgFe{sub 2}O{sub 4} sintered at 1173 K exhibited higher response and selectivity to LPG with marginal increase in the operating temperature. Furthermore, the sensor exhibited a fast response and a good recovery. It was observed that the particles size, porosity, and surface activity of the sensor material is affected by the sintering temperature.« less

A comparative study on NbOx films reactively sputtered from sintered and cold gas sprayed targets

NASA Astrophysics Data System (ADS)

Lorenz, Roland; O'Sullivan, Michael; Fian, Alexander; Sprenger, Dietmar; Lang, Bernhard; Mitterer, Christian

2018-04-01

The aim of this work is to evaluate novel cold gas sprayed Nb targets in a reactive sputter deposition process of thin films with respect to the widely used sintered Nb targets. With the exception of a higher target discharge voltage of ∼100 V for the cold gas sprayed targets and the thus higher film growth rate compared to sintered targets, NbOx films with comparable microstructure and properties were obtained for both target variants. The amorphous films with thicknesses between 2.9 and 4.9 μm present an optical shift from dark and non-transparent towards transparent properties, as the oxygen partial pressure increases. X-ray photoelectron spectroscopy confirms the occurrence of the Nb5+ oxidation state for the highest oxygen partial pressure, while Nb4+ is additionally present at lower oxygen partial pressure settings. With a maximal transparency of ∼80% and a refractive index of ∼2.5, the transparent films show characteristics similar to Nb2O5.

A study of degradation of plates for nickel-cadmium spacecraft cells

NASA Technical Reports Server (NTRS)

Scott, W. R.

1974-01-01

The relative merits of coining and not coining of sintered nickel oxide and cadmium plates was investigated. Sample plate materials from most commercial cell suppliers were obtained and characterized for properties that may correlate with the tendency toward physical disintegration during handling and over long periods of time in the cell. Special test methods were developed to obtain comparative data in a short time. A wide range of physical properties and coining thickness was observed, resulting in a range of responses. The stronger materials resisted loss of sinter better than weaker materials whether or not coined. Coining improved handling and resistance to electrochemical cycling of weaker materials. The mechanism of break-down of positive plate edges under cycling appears to be the same as that of thickening and blistering. Brittle, nonadherent sinter, resulting from certain impregnation processes, is the most vulnerable to degradation. It is concluded that the latter type of materials should be coined, but coining of strong materials is optional.

Powder Metallurgy of Uranium Alloy Fuels for TRU-Burning Reactors Final Technical Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

McDeavitt, Sean M

2011-04-29

Overview Fast reactors were evaluated to enable the transmutation of transuranic isotopes generated by nuclear energy systems. The motivation for this was that TRU isotopes have high radiotoxicity and relatively long half-lives, making them unattractive for disposal in a long-term geologic repository. Fast reactors provide an efficient means to utilize the energy content of the TRUs while destroying them. An enabling technology that requires research and development is the fabrication metallic fuel containing TRU isotopes using powder metallurgy methods. This project focused upon developing a powder metallurgical fabrication method to produce U-Zr-transuranic (TRU) alloys at relatively low processing temperatures (500ºCmore » to 600ºC) using either hot extrusion or alpha-phase sintering for charecterization. Researchers quantified the fundamental aspects of both processing methods using surrogate metals to simulate the TRU elements. The process produced novel solutions to some of the issues relating to metallic fuels, such as fuel-cladding chemical interactions, fuel swelling, volatility losses during casting, and casting mold material losses. Workscope There were two primary tasks associated with this project: 1. Hot working fabrication using mechanical alloying and extrusion • Design, fabricate, and assemble extrusion equipment • Extrusion database on DU metal • Extrusion database on U-10Zr alloys • Extrusion database on U-20xx-10Zr alloys • Evaluation and testing of tube sheath metals 2. Low-temperature sintering of U alloys • Design, fabricate, and assemble equipment • Sintering database on DU metal • Sintering database on U-10Zr alloys • Liquid assisted phase sintering on U-20xx-10Zr alloys Appendices Outline Appendix A contains a Fuel Cycle Research & Development (FCR&D) poster and contact presentation where TAMU made primary contributions. Appendix B contains MSNE theses and final defense presentations by David Garnetti and Grant Helmreich outlining the beginning of the materials processing setup. Also included within this section is a thesis proposal by Jeff Hausaman. Appendix C contains the public papers and presentations introduced at the 2010 American Nuclear Society Winter Meeting. Appendix A—MSNE theses of David Garnetti and Grant Helmreich and proposal by Jeff Hausaman A.1 December 2009 Thesis by David Garnetti entitled “Uranium Powder Production Via Hydride Formation and Alpha Phase Sintering of Uranium and Uranium-Zirconium Alloys for Advanced Nuclear Fuel Applications” A.2 September 2009 Presentation by David Garnetti (same title as document in Appendix B.1) A.3 December 2010 Thesis by Grant Helmreich entitled “Characterization of Alpha-Phase Sintering of Uranium and Uranium-Zirconium Alloys for Advanced Nuclear Fuel Applications” A.4 October 2010 Presentation by Grant Helmreich (same title as document in Appendix B.3) A.5 Thesis Proposal by Jeffrey Hausaman entitled “Hot Extrusion of Alpha Phase Uranium-Zirconium Alloys for TRU Burning Fast Reactors” Appendix B—External presentations introduced at the 2010 ANS Winter Meeting B.1 J.S. Hausaman, D.J. Garnetti, and S.M. McDeavitt, “Powder Metallurgy of Alpha Phase Uranium Alloys for TRU Burning Fast Reactors,” Proceedings of 2010 ANS Winter Meeting, Las Vegas, Nevada, USA, November 7-10, 2010 B.2 PowerPoint Presentation Slides from C.1 B.3 G.W. Helmreich, W.J. Sames, D.J. Garnetti, and S.M. McDeavitt, “Uranium Powder Production Using a Hydride-Dehydride Process,” Proceedings of 2010 ANS Winter Meeting, Las Vegas, Nevada, USA, November 7-10, 2010 B.4. PowerPoint Presentation Slides from C.3 B.5 Poster Presentation from C.3 Appendix C—Fuel cycle research and development undergraduate materials and poster presentation C.1 Poster entitled “Characterization of Alpha-Phase Sintering of Uranium and Uranium-Zirconium Alloys” presented at the Fuel Cycle Technologies Program Annual Meeting C.2 April 2011 Honors Undergraduate Thesis by William Sames, Research Fellow, entitled “Uranium Metal Powder Production, Particle Distribution Analysis, and Reaction Rate Studies of a Hydride-Dehydride Process"« less

Global variations in gravity-derived oceanic crustal thickness: Implications on oceanic crustal accretion and hotspot-lithosphere interactions

NASA Astrophysics Data System (ADS)

Lin, J.; Zhu, J.

2012-12-01

We present a new global model of oceanic crustal thickness based on inversion of global oceanic gravity anomaly with constrains from seismic crustal thickness profiles. We first removed from the observed marine free-air gravity anomaly all gravitational effects that can be estimated and removed using independent constraints, including the effects of seafloor topography, marine sediment thickness, and the age-dependent thermal structure of the oceanic lithosphere. We then calculated models of gravity-derived crustal thickness through inversion of the residual mantle Bouguer anomaly using best-fitting gravity-modeling parameters obtained from comparison with seismically determined crustal thickness profiles. Modeling results show that about 5% of the global crustal volume (or 9% of the global oceanic surface area) is associated with model crustal thickness <5.2 km (designated as "thin" crust), while 56% of the crustal volume (or 65% of the surface area) is associated with crustal thickness of 5.2-8.6 km thick (designated as "normal" crust). The remaining 39% of the crustal volume (or 26% of the surface area) is associated with crustal thickness >8.6 km and is interpreted to have been affected by excess magmatism. The percentage of oceanic crustal volume that is associated with thick crustal thickness (>8.6 km) varies greatly among tectonic plates: Pacific (33%), Africa (50%), Antarctic (33%), Australia (30%), South America (34%), Nazca (23%), North America (47%), India (74%), Eurasia (68%), Cocos (20%), Philippine (26%), Scotia (41%), Caribbean (89%), Arabian (82%), and Juan de Fuca (21%). We also found that distribution of thickened oceanic crust (>8.6 km) seems to depend on spreading rate and lithospheric age: (1) On ocean basins younger than 5 Ma, regions of thickened crust are predominantly associated with slow and ultraslow spreading ridges. The relatively strong lithospheric plate at slow and ultraslow ridges might facilitate the loading of large magmatic emplacements on the plate. (2) In contrast, crustal thickness near fast and intermediately fast spreading ridges typically does not exceed 7-8 km. The relatively weak lithosphere at fast and intermediately fast ridges might make it harder for excess magmatism to accrete. We further speculate that the relatively wide partial melting zones in the upper mantle beneath the fast and intermediately fast ridges might act as "buffer" zones, thus diluting the melt anomalies from the underlying hotspots or regions of mantle heterogeneities. (3) As the crustal age increases and the lithospheric plate thickens, regions of thickened crust start to develop on ocean basins that were originally created at fast and intermediately fast ridges. The integrated crustal volume for fast and intermediately fast ocean crust appears to reach peak values for certain geological periods, such as 40-50 Ma and 70-80 Ma. The newly constructed global models of gravity-derived crustal thickness, combining with geochemical and other constraints, can be used to investigate the processes of oceanic crustal accretion and hotspot-lithosphere interactions.

Preparation and Properties of High-T(sub c) Bi-Pb-Sr-Ca-Cu-O Thick Film Superconductors on YSZ Substrates

NASA Technical Reports Server (NTRS)

Hooker, Matthew W.

1996-01-01

An evaluation of four firing profiles was performed to determine the optimum processing conditions for producing high-T(sub c) Bi-Pb-Sr-Ca-Cu-O thick films on yttria-stabilized zirconia substrates. Using these four profiles, the effects of sintering temperatures of 830-850 C and soak times of 0.5 to 12 hours were examined. In this study, T-c, zero values of 100 K were obtained using a firing profile in which the films were sintered for 1.5 to 2 hours at 840 to 845 C and then quenched to room temperature. X-ray diffraction analyses of these specimens confirmed the presence of the high-T(sub c) phase. Films which were similarly fired and furnace cooled from the peak processing temperature exhibited a two-step superconductive transition to zero resistance, with T-c,zero values ranging from 85 to 92 K. The other firing profiles evaluated in this investigation yielded specimens which either exhibited critical transition temperatures below 90 K or did not exhibit a superconductive transition above 77 K.

[In vitro study on shear bond strength of veneering ceramics to zirconia].

PubMed

Hu, Xiaoping; Zhu, Hongshui; Zeng, Liwei

2012-12-01

To investigate the shear bond strength between veneering ceramic and zirconia core in different all-ceramic systems. Twenty disk-shaped specimens with 8 mm in diameter and 3 mm in height for each zirconia system (Lava, Cercon, IPS e.max ZirCAD, Procera) were fabricated respectively and divided into four groups: Lava group, Cercon group, IPS e.max ZirCAD group, Procera group. For each group, 10 specimens were sintered with 1 mm corresponding veneering ceramic, while the other were sintered with 2 mm corresponding veneering ceramic respectively. The shear bond strength and fracture mode of specimens were observed and determined. The values of shear bond strength for Lava, Cercon, IPS e.max ZirCAD and Procera were (13.82 +/- 3.71), (13.24 +/- 2.09), (6.37 +/- 4.15), (5.19 +/- 5.31) MPa in the group of 1 mm thicked veneering ceramics, respectively, while the values in the group of 2mm thicked veneering ceramics were (38.77 +/- 1.69), (21.67 +/- 3.34), (12.70 +/- 4.24), (9.94 +/- 6.67) MPa. The values of Lava and Cercon groups were significantly higher than that of IPS e.max ZirCAD and Procera groups (P < 0.05). And the values of 2 mm thicked veneering ceramic group were significantly higher than that in 1 mm thicked groups (P < 0.05). Adhesive fracture between core and veneering ceramics were observed in the fracture modes of most specimens. The shear bond strength of veneering ceramic to the zirconia framework are different from the zirconia system we chose, and the thickness of veneering ceramic has a great impact on its shear bond strength.

Development of TiN particulates reinforced SS316 based metal matrix composite by direct metal laser sintering technique and its characterization

NASA Astrophysics Data System (ADS)

Hussain, Manowar; Mandal, Vijay; Kumar, Vikas; Das, A. K.; Ghosh, S. K.

2017-12-01

The present study describes the fabrication of TiN particulates reinforced SS316 based Metal Matrix Composites (MMCs) in nitrogen and argon atmosphere. The influence of sintering process parameters on microstructure, density, porosity, wear rate and microhardness of the fabricated samples has been analyzed. The input variable process parameters, such as, laser power density (range: 4.13-5.57 W/cm2 (× 104)), scanning speed (range: 3500-4500 mm/min) and the constant parameters, such as, laser beam diameter (0.4 mm), hatching distance (0.2 mm) and layer thickness (0.4 mm) have been considered in the process. It has been observed from Field Emission Scanning Electron Microscopy (FESEM) analysis that TiN and SS316 powder mixture can be sintered in which chromium acts as a binder. Fine gaps are not found at the interface between TiN and SS316 when the mixture is sintered in nitrogen atmosphere. With an increase in the percentage of TiN, the density and wear rate decreases. However, when the reinforcement is taken beyond 18% by weight, the wear rate starts increasing. The microhardness also increases with an increase in the percentage of TiN. The microstructure, elemental compositions and phase characterization of the developed sintered MMCs have been examined by FESEM, EDX (Energy-dispersive X-ray spectroscopy) and XRD (X-ray diffractometer) analysis, respectively. The results have demonstrated the suitability of the TiN reinforced SS316 MMCs for industrial applications.

X-ray photoelectron spectroscopy (XPS) investigation of the surface film on magnesium powders.

PubMed

Burke, Paul J; Bayindir, Zeynel; Kipouros, Georges J

2012-05-01

Magnesium (Mg) and its alloys are attractive for use in automotive and aerospace applications because of their low density and good mechanical properties. However, difficulty in forming magnesium and the limited number of available commercial alloys limit their use. Powder metallurgy may be a suitable solution for forming near-net-shape parts. However, sintering pure magnesium presents difficulties due to surface film that forms on the magnesium powder particles. The present work investigates the composition of the surface film that forms on the surface of pure magnesium powders exposed to atmospheric conditions and on pure magnesium powders after compaction under uniaxial pressing at a pressure of 500 MPa and sintering under argon at 600 °C for 40 minutes. Initially, focused ion beam microscopy was utilized to determine the thickness of the surface layer of the magnesium powder and found it to be ~10 nm. The X-ray photoelectron analysis of the green magnesium sample prior to sintering confirmed the presence of MgO, MgCO(3)·3H(2)O, and Mg(OH)(2) in the surface layer of the powder with a core of pure magnesium. The outer portion of the surface layer was found to contain MgCO(3)·3H(2)O and Mg(OH)(2), while the inner portion of the layer is primarily MgO. After sintering, the MgCO(3)·3H(2)O was found to be almost completely absent, and the amount of Mg(OH)(2) was also decreased significantly. This is postulated to occur by decomposition of the compounds to MgO and gases during the high temperature of sintering. An increase in the MgO content after sintering supports this theory.

Sinter-vein correlations at Buckskin Mountain, National district, Humboldt County, Nevada

USGS Publications Warehouse

Vikre, P.G.

2007-01-01

At Buckskin Mountain (elev 2,650 m, 8,743 ft), Humboldt County, Nevada, a hydrothermal system, imposed on a middle Miocene volcanic sequence with contrasting permeabilities and tensile strengths, produced alteration assemblages controlled by elevation, from Hg-mineralized sinter to subjacent precious metal veins over a vertical distance exceeding 790 m. Sinter and epiclastic deposits, interpreted to be remnant paleosurface basinal strata enclosed by 16.6 to 16.1 Ma rhyolites, overlie older volcaniclastic basinal deposits and were part of a regional fluvial-lacustrine system developed among ca. 16 to 12 Ma basalt-rhyolite eruptive centers throughout the northern Great Basin. Because of contrasting erosional resistance among altered and unaltered rocks, Buckskin Mountain represents inverse topography with sinter and silicified epiclastic deposits at the summit. Sinter and veins, correlated by common elements, similar mineralogy, age constraints, textures, S isotope compositions, and fluid inclusion microthermometry, were deposited by sinter-vein fluid, the first of two sequential hydrothermal fluid regimes that evolved in response to magmatism, tectonism, hydrology, and topography. Thermal quenching of distally derived sinter-vein fluid in planar conduits caused deposition of banded quartz-silicate-selenide-sulfide veins ???270 to > 440 m below sinter at 16.1 Ma; vei??ns were initially enveloped by zoned selvages of proximal K-feldspar + K-mica + quartz + pyrite and distal illite + chlorite + calcite + pyrite. Mixing of sinter-vein fluid with local meteoric water in saturated basinal deposits caused deposition of silica, Hg-Se-S-Cl minerals, and precious metals in sinter and epiclastic deposits. Elevated ???Se/???S in sinter-vein fluid, and the relatively large stability fields of reduced aqueous selenide species in the temperature range of 250?? to <100??C, enabled (but was not the cause of) codeposition of selenide-sulfide minerals and common element associations in veins and sinter. Acid-sulfate fluid of the second fluid regime was derived from oxidation of H2S and other volatiles exsolved from sinter-vein fluid. Acid-sulfate fluid produced (1) a subhorizontal zone of partially leached basinal deposits and rhyolite from the paleosurface to a depth of ???60 m, and (2) laterally pervasive zones, ???100 to 200 m thick, of quartz + alunite ?? hematite and quartz + kaolinite + pyrite in volcaniclastic deposits immediately beneath partially leached rocks, but this fluid did not decompose selenide-sulfide-precious metal phases in sinter. Paragenetically late vein and wall-rock assemblages, including marcasite + pyrite, calcite, and kaolinite-replaced K minerals, record deeper transition of sinter-vein fluid into acid-sulfate fluid in vein conduits. This transition occurred as regional subsidence, manifested by the Goosey Lake depression immediately east of Buckskin Mountain, lowered the pieziometric surface at Buckskin Mountain, terminated sinter deposition, and caused boiling and/or degassing of sinter-vein fluid. The timing of subsidence is recorded by a decrease in alunite ages, from ca. 15.8 to 15.6 Ma, with depth below sinter. Lateral replacement of sinter and partially leached epiclastic deposits and rhyolite by opal-A marks the termination of the two hydrothermal regimes that lasted ???0.5 m.y. and followed rhyolitic volcanism of similar duration. Veins and sinter display textures that attest to plastic deformation, spalling, and gravitational settling, and indicate fluid-flow direction, velocity, and density stratification which, with conduit topology, may have influenced precious metal tenor in the veins. Components of sinter and veins were transported as colloids, formed in supersaturated sinter-vein fluid, that aggregated or coagulated as incompetent gelatinous layers in shallow pools and in underlying, near-vertical conduits in rhyolite and initially crystallized as opal and chalcedony. The low thermal conductivity of ho

IMPROVED TUBULARS FOR BETTER ECONOMICS IN DEEP GAS WELL DRILLING USING MICROWAVE TECHNOLOGY

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dinesh Agrawal; Paul Gigl; Mahlon Dennis

2005-03-01

The main objective of the research program has been to improve the rate-of-penetration in deep hostile environments by improving the life cycle and performance of coiled-tubing, an important component of a deep well drilling system for oil and gas exploration, by utilizing the latest developments in the microwave materials technology. Originally, it was proposed to accomplish this by developing an efficient and economically viable continuous microwave process to sinter continuously formed/extruded steel powder for the manufacture of seamless coiled tubing and other tubular products. However, based on the results and faced with insurmountable difficulties in the extrusion and de-waxing processes,more » the approach of achieving the goals of the program has been slightly changed. In the continuation proposal an approach of microwave sintering combined with Cold Isostatic Press (CIP) and joining (by induction or microwave) is adopted. This process can be developed into a semi-continuous sintering process if the CIP can produce parts fast enough to match the microwave sintering rates. Originally, the entire program was spread over three phases with the following goals: Phase I: Demonstration of the feasibility concept of continuous microwave sintering process for tubular steel products. Phase II: Design, building and testing of a prototype microwave system which shall be combined with a continuous extruder for steel tubular objects. Phase III: Execution of the plan for commercialization of the technology by one of the industrial partners. However, since some of the goals of the phase I were not completed, an extension of nine months was granted and we continued extrusion experiments, designed and built semicontinuous microwave sintering unit.« less

Optimization of the dissolution of molybdenum disks. FY-16 results

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tkac, Peter; Rotsch, David A.; Chemerisov, Sergey D.

2016-09-01

Argonne National Laboratory is providing technical development assistance to NorthStar Medical Technologies LLC in its pursuit of two pathways for production of molybdenum-99: the 98Mo(n,γ) 99Mo reaction and the photonuclear reaction, 100Mo(γ,n) 99Mo. Processing of irradiated targets, from either production mode, requires dissolution of the target material in H 2O 2 followed by a concentration step, addition of ferric ion to precipitate impurities, and conversion of the final solution to 5M potassium hydroxide solution of potassium molybdate. Currently, NorthStar is using pressed and sintered Mo disks as targets. Several options are being considered for the design of Mo targets formore » the production of 99Mo using the (γ,n) reaction. In the current design, the target holder contains a series of sintered Mo disks lined up perpendicular to two incident electron beams, one entering from each side of the target stack. In this configuration, the front-most disks absorb most of the heat from the electron beam and need to be thinner to allow for better cooling, while the middle of the target can be thicker. Distribution of the total mass of Mo allows for larger masses of Mo material and thus larger production batches of 99Mo. A limitation of the sintering approach is the production of very thin disks. Recent advances in 3D printing allow for much thinner target components can be achieved than when the traditional press-and-sinter approach is used. We have demonstrated that several factors can play important roles in dissolution behavior: particle size of Mo metal used for production of targets, sintering conditions, degree of open porosity, and thickness of the sintered Mo targets. Here we report experimental results from studies of small-scale dissolution of sintered Mo disks fabricated from various recycled and commercial Mo materials, and dissolution of 3D-printed Mo disks that were fabricated by Oak Ridge National Laboratory (ORNL). We also report on large-scale dissolution studies with 600 g batches of sintered Mo disks.« less

Structural, Optical and Ethanol Sensing Properties of Dy-Doped SnO2 Nanoparticles

NASA Astrophysics Data System (ADS)

Shaikh, F. I.; Chikhale, L. P.; Nadargi, D. Y.; Mulla, I. S.; Suryavanshi, S. S.

2018-04-01

We report a facile co-precipitation synthesis of dysprosium (Dy3+) doped tin oxide (SnO2) thick films and their use as gas sensors. The doping percentage (Dy3+) was varied from 1 mol.% to 4 mol.% with the step of 1 mol.%. As-produced material with varying doping levels were sintered in air; and by using a screen printing technique, their thick films were developed. Prior to sensing performance investigations, the films were examined for structural, morphological and compositional properties using x-ray diffraction, a field emission scanning electron microscope, a transmission electron microscope, selected area electron diffraction, energy dispersive analysis by x-rays, Fourier transform infrared spectroscopy and Raman spectroscopic techniques. The structural analyses revealed formation of single phase nanocrystalline material with tetragonal rutile structure of SnO2. The morphological analyses confirmed the nanocrystalline porous morphology of as-developed material. Elemental analysis defined the composition of material in accordance with the doping concentration. The produced sensor material exhibited good response towards different reducing gases (acetone, ethanol, LPG, and ammonia) at different operating temperatures. The present study confirms that the Dy3+ doping in SnO2 enhances the response towards ethanol with reduction in operating temperature. Particularly, 3 mol.% Dy3+ doped sensor exhibited the highest response (˜ 92%) at an operating temperature of 300°C with better selectivity, fast response (˜ 13 s) and recovery (˜ 22 s) towards ethanol.

[The effect of core veneer thickness ratio on the flexural strength of diatomite-based dental ceramic].

PubMed

Jiang, Jie; Zhang, Xin; Gao, Mei-qin; Zhang, Fei-min; Lu, Xiao-li

2015-06-01

To evaluate the effect of different core veneer thickness ratios on the flexural strength and failure mode of bilayered diatomite-based dental ceramics. Diatomite-based dental ceramics blocks (16 mm×5.4 mm×1 mm) were sintered with different thickness of veneer porcelains: 0 mm (group A), 0.6 mm (group B), 0.8 mm (group C) and 1.0 mm (group D). Flexural strength was detected and scanning electron microscope was used to observe the interface microstructure. Statistical analysis was performed using SPSS 17.0 software package. With the increase of the thickness of the veneer porcelain, flexural strength of group C showed highest flexural strength up to (277.24±5.47) MPa. Different core veneer thickness ratios can significantly influence the flexural strength of bilayered diatomite-based dental ceramics. Supported by Science and Technology Projects of Nantong City (HS2013010).

Electric-Loading Enhanced Kinetics in Oxide Ceramics: Pore Migration, Sintering and Grain Growth: Final Report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, I-Wei

Solid oxide fuel cells and solid oxide electrolysis cells rely on solid electrolytes in which a large ionic current dominates. This project was initiated to investigate microstructural changes in such devices under electrochemical forces, because nominally insignificant processes may couple to the large ionic current to yield non-equilibrium phenomena that alter the microstructure. Our studies had focused on yttria-stabilized cubic zirconia (YSZ) widely used in these devices. The experiments have revealed enhanced grain growth at higher temperatures, pore and gas bubble migration at all temperatures, and the latter also lead to enhanced sintering of highly porous ceramics into fully densemore » ceramics at unprecedentedly low temperatures. These results have shed light on kinetic processes that fall completely outside the realm of classical ceramic processing. Other fast-oxygen oxide ceramics closely related to, and often used in conjunction with zirconia ceramics, have also be investigated, as are closely related scientific problems in zirconia ceramics. These include crystal structures, defects, diffusion kinetics, oxygen potentials, low temperature sintering, flash sintering, and coarsening theory, and all have resulted in greater clarity in scientific understanding. The knowledge is leveraged to provide new insight to electrode kinetics and near-electrode mixed conductivity and to new materials. In the following areas, our research has resulted in completely new knowledge that defines the state-of-the-art of the field. (a) Electrical current driven non-equilibrium phenomena, (b) Enhanced grain growth under electrochemically reducing conditions, (c) Development of oxygen potential polarization in electrically loaded electrolyte, (d) Low temperature sintering and grain growth, and (e) Structure, defects and cation kinetics of fluorite-structured oxides. Our research has also contributed to synthesis of new energy-relevant electrochemical materials and new understanding of flash sintering, which is a rapid sintering process initiated by a large electrical loading.« less

Bismuth Titanate Fabricated by Spray-on Deposition and Microwave Sintering For High-Temperature Ultrasonic Transducers.

PubMed

Searfass, Clifford T; Pheil, C; Sinding, K; Tittmann, B R; Baba, A; Agrawal, D K

2016-01-01

Thick films of ferroelectric bismuth titanate (Bi4Ti3O12) have been fabricated by spray-on deposition in conjunction with microwave sintering for use as high-temperature ultrasonic transducers. The elastic modulus, density, permittivity, and conductivity of the films were characterized. Electro-mechanical properties of the films were estimated with a commercial d33 meter which gave 16 pC/N. This value is higher than typically reported for bulk bismuth titanate; however, these films withstand higher field strengths during poling which is correlated with higher d33 values. Films were capable of operating at 650 °C for roughly 5 min before depoling and can operate at 600 °C for at least 7 days.

Method of preparing porous, rigid ceramic separators for an electrochemical cell

DOEpatents

Bandyopadhyay, Gautam; Dusek, Joseph T.

1981-01-01

Porous, rigid separators for electrochemical cells are prepared by first calcining particles of ceramic material at temperatures above about 1200.degree. C. for a sufficient period of time to reduce the sinterability of the particles. A ceramic powder that has not been calcined is blended with the original powder to control the porosity of the completed separator. The ceramic blend is then pressed into a sheet of the desired shape and sintered at a temperature somewhat lower than the calcination temperature. Separator sheets of about 1 to 2.5 mm thickness and 30 to 70% porosity can be prepared by this technique. Ceramics such as yttria, magnesium oxide and magnesium-aluminum oxide have advantageously been used to form separators by this method.

Silicon nitride ceramic having high fatigue life and high toughness

DOEpatents

Yeckley, Russell L.

1996-01-01

A sintered silicon nitride ceramic comprising between about 0.6 mol % and about 3.2 mol % rare earth as rare earth oxide, and between about 85 w/o and about 95 w/o beta silicon nitride grains, wherein at least about 20% of the beta silicon nitride grains have a thickness of greater than about 1 micron.

Design of Aerosol Particle Coating: Thickness, Texture and Efficiency

PubMed Central

Buesser, B.; Pratsinis, S.E.

2013-01-01

Core-shell particles preserve the performance (e.g. magnetic, plasmonic or opacifying) of a core material while modifying its surface with a shell that facilitates (e.g. by blocking its reactivity) their incorporation into a host liquid or polymer matrix. Here coating of titania (core) aerosol particles with thin silica shells (films or layers) is investigated at non-isothermal conditions by a trimodal aerosol dynamics model, accounting for SiO2 generation by gas phase and surface oxidation of hexamethyldisiloxane (HMDSO) vapor, coagulation and sintering. After TiO2 particles have reached their final primary particle size (e.g. upon completion of sintering during their flame synthesis), coating starts by uniformly mixing them with HMDSO vapor that is oxidized either in the gas phase or on the particles’ surface resulting in SiO2 aerosols or deposits, respectively. Sintering of SiO2 deposited onto the core TiO2 particles takes place transforming rough into smooth coating shells depending on process conditions. The core-shell characteristics (thickness, texture and efficiency) are calculated for two limiting cases of coating shells: perfectly smooth (e.g. hermetic) and fractal-like. At constant TiO2 core particle production rate, the influence of coating weight fraction, surface oxidation and core particle size on coating shell characteristics is investigated and compared to pertinent experimental data through coating diagrams. With an optimal temperature profile for complete precursor conversion, the TiO2 aerosol and SiO2-precursor (HMDSO) vapor concentrations have the strongest influence on product coating shell characteristics. PMID:23729833

Effect of fabrication parameters on coating properties of tubular solid oxide fuel cell electrolyte prepared by vacuum slurry coating

NASA Astrophysics Data System (ADS)

Son, Hui-Jeong; Song, Rak-Hyun; Lim, Tak-Hyoung; Lee, Seung-Bok; Kim, Sung-Hyun; Shin, Dong-Ryul

The process of vacuum slurry coating for the fabrication of a dense and thin electrolyte film on a porous anode tube is investigated for application in solid oxide fuel cells. 8 mol% yttria stabilized zirconia is coated on an anode tube by vacuum slurry-coating process as a function of pre-sintering temperature of the anode tube, vacuum pressure, slurry concentration, number of coats, and immersion time. A dense electrolyte layer is formed on the anode tube after final sintering at 1400 °C. With decrease in the pre-sintering temperature of the anode tube, the grain size of the coated electrolyte layer increases and the number of surface pores in the coating layer decreases. This is attributed to a reduced difference in the respective shrinkage of the anode tube and the electrolyte layer. The thickness of the coated electrolyte layer increases with the content of solid powder in the slurry, the number of dip-coats, and the immersion time. Although vacuum pressure has no great influence on the electrolyte thickness, higher vacuum produces a denser coating layer, as confirmed by low gas permeability and a reduced number of defects in the coating layer. A single cell with the vacuum slurry coated electrolyte shows a good performance of 620 mW cm -2 (0.7 V) at 750 °C. These experimental results indicate that the vacuum slurry-coating process is an effective method to fabricate a dense thin film on a porous anode support.

Fabrication and ferroelectric properties of highly dense lead-free piezoelectric (K0.5Na0.5)NbO3 thick films by aerosol deposition

NASA Astrophysics Data System (ADS)

Ryu, Jungho; Choi, Jong-Jin; Hahn, Byung-Dong; Park, Dong-Soo; Yoon, Woon-Ha; Kim, Ki-Hoon

2007-04-01

Lead-free piezoelectric thick films of (K0.5Na0.5)NbO3 were fabricated by aerosol-deposition method. The thickness of KNN film was 7.1μm and fully dense films were obtained. The dielectric constants ɛ3T/ɛ0 of the as-deposited and annealed films at 1kHz were 116 and 545, respectively, which are higher than any previously reported values for lead-free piezoelectric thin/thick films, either without or with heat treatment. The ferroelectric properties were improved after annealing and the maximum values of Pr=8.1μC/cm3 and Ec=100kV/cm were achieved. These values are markedly superior to those of sintered KNN ceramic counterparts.

High pressure FAST of nanocrystalline barium titanate

DOE PAGES

Fraga, Martin B.; Delplanque, Jean -Pierre; Yang, Nancy; ...

2016-06-01

Here, this work studies the microstructural evolution of nanocrystalline (<1 µm) barium titanate (BaTiO 3), and presents high pressure in field-assisted sintering (FAST) as a robust methodology to obtain >100 nm BaTiO 3 compacts. Using FAST, two commercial ~50 nm powders were consolidated into compacts of varying densities and grain sizes. Microstructural inhomogeneities were investigated for each case, and an interpretation is developed using a modified Monte Carlo Potts (MCP) simulation. Two recurrent microstructural inhomogeneities are highlighted, heterogeneous grain growth and low-density regions, both ubiqutously present in all samples to varying degrees. In the worst cases, HGG presents an areamore » coverage of 52%. Because HGG is sporadic but homogenous throughout a sample, the catalyst (e.g., the local segregation of species) must be, correspondingly, distributed in a homogenous manner. MCP demonstrates that in such a case, a large distance between nucleating abnormal grains is required—otherwise abnormal grains prematurely impinge on each other, and their size is not distinguishable from that of normal grains. Compacts sintered with a pressure of 300 MPa and temperatures of 900 °C, were 99.5% dense and had a grain size of 90±24 nm. These are unprecedented results for commercial BaTiO 3 powders or any starting powder of 50 nm particle size—other authors have used 16 nm lab-produced powder to obtain similar results.« less

Fabrication of High Thermal Conductivity NARloy-Z-Diamond Composite Combustion Chamber Liner for Advanced Rocket Engines

NASA Technical Reports Server (NTRS)

Bhat, Biliyar N.; Greene, Sandra E.; Singh, Jogender

2016-01-01

NARloy-Z alloy (Cu-3 percent, Ag-0.5 percent, Zr) is a state of the art alloy currently used for fabricating rocket engine combustion chamber liners. Research conducted at NASA-MSFC and Penn State – Applied Research Laboratory has shown that thermal conductivity of NARloy-Z can be increased significantly by adding diamonds to form a composite (NARloy-Z-D). NARloy-Z-D is also lighter than NARloy-Z. These attributes make this advanced composite material an ideal candidate for fabricating combustion chamber liner for an advanced rocket engine. Increased thermal conductivity will directly translate into increased turbopump power and increased chamber pressure for improved thrust and specific impulse. This paper describes the process development for fabricating a subscale high thermal conductivity NARloy-Z-D combustion chamber liner using Field Assisted Sintering Technology (FAST). The FAST process uses a mixture of NARloy-Z and diamond powders which is sintered under pressure at elevated temperatures. Several challenges were encountered, i.e., segregation of diamonds, machining the super hard NARloy-Z-D composite, net shape fabrication and nondestructive examination. The paper describes how these challenges were addressed. Diamonds coated with copper (CuD) appear to give the best results. A near net shape subscale combustion chamber liner is being fabricated by diffusion bonding cylindrical rings of NARloy-Z-CuD using the FAST process.

Method of forming a relatively stable slip of silicon metal particles and yttrium containing particles

DOEpatents

Dickie, Ray A.; Mangels, John A.

1984-01-01

The method concerns forming a relatively stable slip of silicon metal particles and yttrium containing particles. In one embodiment, a casting slip of silicon metal particles is formed in water. Particles of a yttrium containing sintering aid are added to the casting slip. The yttrium containing sintering aid is a compound which has at least some solubility in water to form Y.sup.+3 ions which have a high potential for totally flocculating the silicon metal particles into a semiporous solid. A small amount of a fluoride salt is added to the casting slip which contains the yttrium containing sintering aid. The fluoride salt is one which will produce fluoride anions when dissolved in water. The small amount of the fluoride anions produced are effective to suppress the flocculation of the silicon metal particles by the Y.sup.+3 ions so that all particles remain in suspension in the casting slip and the casting slip has both an increased shelf life and can be used to cast articles having a relatively thick cross-section. The pH of the casting slip is maintained in a range from 7.5 to 9. Preferably, the fluoride salt used is one which is based on a monovalent cation such as sodium or ammonia. The steps of adding the yttrium containing sintering aid and the fluoride salt may be interchanged if desired, and the salt may be added to a solution containing the sintering aid prior to addition of the silicon metal particles.

Analysis of thermoelastic characteristics in a thick walled FGM cylinder

NASA Astrophysics Data System (ADS)

Tanvir, A. N. M.; Islam, Md. Didarul; Ahmed, Faisal

2017-12-01

This study is concerned with the behavior of stress and strain in a thick walled functionally graded material (FGM) cylinder under internal pressure. The incompatible eigenstrain and equivalent eigenstrain developed in the cylinder, are taken into account. As a demonstration, a TiC/Al2O3 FGM cylinder is considered and different components of stress and strain are presented in order to study the effects of internal pressure, temperature difference (between room and sintering temperature), cylinder wall thickness and material distribution. The numerical result presented here shows that the thermoelastic characteristic like stress and strain of an FGM cylinder is significantly influenced by some of the above-mentioned parameters and can be controlled by properly controlling these parameters.

Manufacturing issues and optical properties of rare-earth (Y, Lu, Sc, Nd) aluminate garnets composite transparent ceramics

NASA Astrophysics Data System (ADS)

Bonnet, Loïck; Boulesteix, Rémy; Maître, Alexandre; Sallé, Christian; Couderc, Vincent; Brenier, Alain

2015-12-01

In this work, a comparative study of reactive sintering and optical properties of three laser composite transparent ceramics doped with neodymium: Nd:YAG/Nd:YS1AG, Nd:YAG/Nd:LuAG and Nd:YS1AG/Nd:LuAG has been achieved. Samples were manufactured thanks to pressureless co-sintering under vacuum of bilayer powder compacts. The reaction sequence from primary oxides to final garnet phases has been investigated. Similar dilatometric behavior was observed during reactive-sintering for each composition. Differential shrinkage can be thus accommodated to some extent. Second, this work has shown that the intermediate zone at composites interface is composed of single-phased garnet solid-solution with continuous evolution from one side to the other. The thickness of the interdiffusion zone was found to be limited to about 100 μm in all cases and appeared to be well described by classical diffusion laws of Fick and Whipple-Le Claire. The analyses of spectroscopic properties of transparent ceramics composites have finally shown that composite ceramics should be suitable to produce dual wavelength emission for terahertz generation.

Crack Driving Forces in a Multilayered Coating System for Ceramic Matrix Composite Substrates

NASA Technical Reports Server (NTRS)

Ghosn, Louis J.; Zhu, Dongming; Miller, Robert A.

2005-01-01

The effects of the top coating thickness, modulus and shrinkage strains on the crack driving forces for a baseline multilayer Yttria-Stabilized-Zirconia/Mullite/Si thermal and environment barrier coating (TEBC) system for SiC/SiC ceramic matrix composite substrates are determined for gas turbine applications. The crack driving forces increase with increasing modulus, and a low modulus thermal barrier coating material (below 10 GPa) will have no cracking issues under the thermal gradient condition analyzed. Since top coating sintering increases the crack driving forces with time, highly sintering resistant coatings are desirable to maintain a low tensile modulus and maintain a low crack driving force with time. Finite element results demonstrated that an advanced TEBC system, such as ZrO2/HfO2, which possesses improved sintering resistance and high temperature stability, exhibited excellent durability. A multi-vertical cracked structure with fine columnar spacing is an ideal strain tolerant coating capable of reducing the crack driving forces to an acceptable level even with a high modulus of 50 GPa.

Nondestructive evaluation of structural ceramics by photoacoustic microscopy

NASA Technical Reports Server (NTRS)

Khandelwal, Pramod K.

1987-01-01

A photoacoustic microscopy (PAM) digital imaging system was developed and utilized to characterize silicon nitride material at the various stages of the ceramic fabrication process. Correlation studies revealed that photoacoustic microscopy detected failure initiating defects in substantially more specimens than microradiography and ultrasonic techniques. Photoacoustic microscopy detected 10 to 100 micron size surface and subsurface pores and inclusions, respectively, up to 80 microns below the interrogating surface in machined sintered silicon nitride. Microradiography detected 50 micron diameter fracture controlling pores and inclusions. Subsurface holes were detected up to a depth of 570 microns and 1.00 mm in sintered silicon nitride and silicon carbide, respectively. Seeded voids of 20 to 30 micron diameters at the surface and 50 microns below the interrogating surface were detected by photoacoustic microscopy and microradiography with 1 percent X-ray thickness sensitivity. Tight surface cracks of 96 micron length x 48 micron depth were detected by photoacoustic microscopy. PAM volatilized and removed material in the green state which resulted in linear shallow microcracks after sintering. This significantly limits the use of PAM as an in-process NDE technique.

Lightweight Electrode For Nickel/Hydrogen Cell

NASA Technical Reports Server (NTRS)

Britton, Doris L.

1994-01-01

Improved substrate for nickel electrode increases specific energy of nickel/hydrogen cell. Consists of 50 percent by weight nickel fiber, 35 percent nickel powder, and 15 percent cobalt powder. Porosity and thickness of nickel electrodes affect specific energy, initial performance, and cycle life of cell. Substrate easily manufactured with much larger porosities than those of heavy-sintered state-of-art nickel substrate.

Method of preparing porous, rigid ceramic separators for an electrochemical cell. [Patent application

DOEpatents

Bandyopadhyay, G.; Dusek, J.T.

Porous, rigid separators for electrochemical cells are prepared by first calcining particles of ceramic material at temperatures above about 1200/sup 0/C for a sufficient period of time to reduce the sinterability of the particles. A ceramic powder that has not been calcined is blended with the original powder to control the porosity of the completed separator. The ceramic blend is then pressed into a sheet of the desired shape and sintered at a temperature somewhat lower than the calcination temperature. Separator sheets of about 1 to 2.5 mm thickness and 30 to 70% porosity can be prepared by this technique. Ceramics such as yttria, magnesium oxide, and magnesium-aluminium oxide have advantageously been used to form separators by this method.

High temperature strain gages

NASA Technical Reports Server (NTRS)

Gregory, Otto J. (Inventor); You, Tao (Inventor)

2011-01-01

A ceramic strain gage based on reactively sputtered indium-tin-oxide (ITO) thin films is used to monitor the structural integrity of components employed in aerospace propulsion systems operating at temperatures in excess of 1500.degree. C. A scanning electron microscopy (SEM) of the thick ITO sensors reveals a partially sintered microstructure comprising a contiguous network of submicron ITO particles with well defined necks and isolated nanoporosity. Densification of the ITO particles was retarded during high temperature exposure with nitrogen thus stabilizing the nanoporosity. ITO strain sensors were prepared by reactive sputtering in various nitrogen/oxygen/argon partial pressures to incorporate more nitrogen into the films. Under these conditions, sintering and densification of the ITO particles containing these nitrogen rich grain boundaries was retarded and a contiguous network of nano-sized ITO particles was established.

The Achievement of Near-Theoretical-Minimum Contact Resistance to InP

NASA Technical Reports Server (NTRS)

Fatemi, Navid S.; Weizer, Victor G.

1993-01-01

We have investigated the electrical and metallurgical behavior of the InP/Au/Ni contact system. We show that when a layer of Au, 100 A or more in thickness, is introduced between n-InP and Ni contact metallization, specific contact resistivity R, values in the low 10(exp -8) Omega cm(exp 2) range are achieved after sintering. It is suggested that these ultralow values of R(sub c) are due to the presence, at the metal-InP interface, of a Ni3P layer combined with a stoichiometry change in the InP surface. We show, in addition, that it is possible to achieve very low R(sub c) values with this system without incurring device destroying sinter-induced metallurgical interdiffusion.

An Evaluation of the Gap Sizes of 3-Unit Fixed Dental Prostheses Milled from Sintering Metal Blocks.

PubMed

Jung, Jae-Kwan

2017-01-01

This study assessed the clinical acceptability of sintering metal-fabricated 3-unit fixed dental prostheses (FDPs) based on gap sizes. Ten specimens were prepared on research models by milling sintering metal blocks or by the lost-wax technique (LWC group). Gap sizes were assessed at 12 points per abutment (premolar and molar), 24 points per specimen (480 points in a total in 20 specimens). The measured points were categorized as marginal, axial wall, and occlusal for assessment in a silicone replica. The silicone replica was cut through the mesiodistal and buccolingual center. The four sections were magnified at 160x, and the thickness of the light body silicone was measured to determine the gap size, and gap size means were compared. For the premolar part, the mean (standard deviation) gap size was nonsignificantly ( p = 0.139) smaller in the SMB group (68.6 ± 35.6  μ m) than in the LWC group (69.6 ± 16.9  μ m). The mean molar gap was nonsignificantly smaller ( p = 0.852) in the LWC (73.9 ± 25.6  μ m) than in the SMB (78.1 ± 37.4  μ m) group. The gap sizes were similar between the two groups. Because the gap sizes were within the previously proposed clinically accepted limit, FDPs prepared by sintered metal block milling are clinically acceptable.

An Evaluation of the Gap Sizes of 3-Unit Fixed Dental Prostheses Milled from Sintering Metal Blocks

PubMed Central

2017-01-01

This study assessed the clinical acceptability of sintering metal-fabricated 3-unit fixed dental prostheses (FDPs) based on gap sizes. Ten specimens were prepared on research models by milling sintering metal blocks or by the lost-wax technique (LWC group). Gap sizes were assessed at 12 points per abutment (premolar and molar), 24 points per specimen (480 points in a total in 20 specimens). The measured points were categorized as marginal, axial wall, and occlusal for assessment in a silicone replica. The silicone replica was cut through the mesiodistal and buccolingual center. The four sections were magnified at 160x, and the thickness of the light body silicone was measured to determine the gap size, and gap size means were compared. For the premolar part, the mean (standard deviation) gap size was nonsignificantly (p = 0.139) smaller in the SMB group (68.6 ± 35.6 μm) than in the LWC group (69.6 ± 16.9 μm). The mean molar gap was nonsignificantly smaller (p = 0.852) in the LWC (73.9 ± 25.6 μm) than in the SMB (78.1 ± 37.4 μm) group. The gap sizes were similar between the two groups. Because the gap sizes were within the previously proposed clinically accepted limit, FDPs prepared by sintered metal block milling are clinically acceptable. PMID:28246605

Effect of Silver Flakes in Silver Paste on the Joining Process and Properties of Sandwich Power Modules (IGBTs Chip/Silver Paste/Bare Cu)

NASA Astrophysics Data System (ADS)

Zhao, Su-Yan; Li, Xin; Mei, Yun-Hui; Lu, Guo-Quan

2016-11-01

In this study, a silver paste has been introduced for attaching chips onto bare Cu substrates (without coating) without applying pressure. Small nano-thickness Ag flakes, measuring 1 μm-5 μm length, were embedded uniformly in Ag nanoparticles for improving the density of the material. The presence of silver flakes in the silver paste affected the joining process and its microstructure. Microstructure characterization revealed that densification of the silver layer was affected by the presence of silver flakes as the flakes coarsened and formed reactive in situ nanoparticles, which facilitated the sintering between the flakes and the incorporated nanoparticles. Coarsening of silver flakes depended on the sintering temperature, time, and the atmosphere, which affected the decomposition and burning out of organics presented on the surface of the flakes. A high-density silver layer was obtained due to the presence of compact silver flakes. With an increase in the microstructure density, a higher bonding strength and a lower thermal impedance of the sintered joints were achieved. On performing pressureless sintering at 270°C for 30 min under 99.99% N2 or 4% H2/N2, the bonding strength and thermal impedance for 11 × 11 mm2 chips were excellent, measuring approximately 21.9 MPa and 0.077°C/W, respectively.

Ceramic components manufacturing by selective laser sintering

NASA Astrophysics Data System (ADS)

Bertrand, Ph.; Bayle, F.; Combe, C.; Goeuriot, P.; Smurov, I.

2007-12-01

In the present paper, technology of selective laser sintering/melting is applied to manufacture net shaped objects from pure yttria-zirconia powders. Experiments are carried out on Phenix Systems PM100 machine with 50 W fibre laser. Powder is spread by a roller over the surface of 100 mm diameter alumina cylinder. Design of experiments is applied to identify influent process parameters (powder characteristics, powder layering and laser manufacturing strategy) to obtain high-quality ceramic components (density and micro-structure). The influence of the yttria-zirconia particle size and morphology onto powder layering process is analysed. The influence of the powder layer thickness on laser sintering/melting is studied for different laser beam velocity V ( V = 1250-2000 mm/s), defocalisation (-6 to 12 mm), distance between two neighbour melted lines (so-called "vectors") (20-40 μm), vector length and temperature in the furnace. The powder bed density before laser sintering/melting also has significant influence on the manufactured samples density. Different manufacturing strategies are applied and compared: (a) different laser beam scanning paths to fill the sliced surfaces of the manufactured object, (b) variation of vector length (c) different strategies of powder layering, (d) temperature in the furnace and (e) post heat treatment in conventional furnace. Performance and limitations of different strategies are analysed applying the following criteria: geometrical accuracy of the manufactured samples, porosity. The process stability is proved by fabrication of 1 cm 3 volume cube.

Post-Plasma SiOx Coatings of Metal and Metal Oxide Nanoparticles for Enhanced Thermal Stability and Tunable Photoactivity Applications

PubMed Central

Post, Patrick; Jidenko, Nicolas; Weber, Alfred P.; Borra, Jean-Pascal

2016-01-01

The plasma-based aerosol process developed for the direct coating of particles in gases with silicon oxide in a continuous chemical vapor deposition (CVD) process is presented. It is shown that non-thermal plasma filaments induced in a dielectric barrier discharge (DBD) at atmospheric pressure trigger post-DBD gas phase reactions. DBD operating conditions are first scanned to produce ozone and dinitrogen pentoxide. In the selected conditions, these plasma species react with gaseous tetraethyl orthosilicate (TEOS) precursor downstream of the DBD. The gaseous intermediates then condense on the surface of nanoparticles and self-reactions lead to homogeneous solid SiOx coatings, with thickness from nanometer to micrometer. This confirms the interest of post-DBD injection of the organo-silicon precursor to achieve stable production of actives species with subsequent controlled thickness of SiOx coatings. SiOx coatings of spherical and agglomerated metal and metal oxide nanoparticles (Pt, CuO, TiO2) are achieved. In the selected DBD operating conditions, the thickness of homogeneous nanometer sized coatings of spherical nanoparticles depends on the reaction duration and on the precursor concentration. For agglomerates, operating conditions can be tuned to cover preferentially the interparticle contact zones between primary particles, shifting the sintering of platinum agglomerates to much higher temperatures than the usual sintering temperature. Potential applications for enhanced thermal stability and tunable photoactivity of coated agglomerates are presented. PMID:28335219

Synthesis of Highly Uniform and Compact Lithium Zinc Ferrite Ceramics via an Efficient Low Temperature Approach.

PubMed

Xu, Fang; Liao, Yulong; Zhang, Dainan; Zhou, Tingchuan; Li, Jie; Gan, Gongwen; Zhang, Huaiwu

2017-04-17

LiZn ferrite ceramics with high saturation magnetization (4πM s ) and low ferromagnetic resonance line widths (ΔH) represent a very critical class of material for microwave ferrite devices. Many existing approaches emphasize promotion of the grain growth (average size is 10-50 μm) of ferrite ceramics to improve the gyromagnetic properties at relatively low sintering temperatures. This paper describes a new strategy for obtaining uniform and compact LiZn ferrite ceramics (average grains size is ∼2 μm) with enhanced magnetic performance by suppressing grain growth in great detail. The LiZn ferrites with a formula of Li 0.415 Zn 0.27 Mn 0.06 Ti 0.1 Fe 2.155 O 4 were prepared by solid reaction routes with two new sintering strategies. Interestingly, results show that uniform, compact, and pure spinel ferrite ceramics were synthesized at a low temperature (∼850 °C) without obvious grain growth. We also find that a fast second sintering treatment (FSST) can further improve their gyromagnetic properties, such as higher 4πM s and lower ΔH. The two new strategies are facile and efficient for densification of LiZn ferrite ceramics via suppressing grain growth at low temperatures. The sintering strategy reported in this study also provides a referential experience for other ceramics, such as soft magnetism ferrite ceramics or dielectric ceramics.

One-Step Fabrication of Stretchable Copper Nanowire Conductors by a Fast Photonic Sintering Technique and Its Application in Wearable Devices.

PubMed

Ding, Su; Jiu, Jinting; Gao, Yue; Tian, Yanhong; Araki, Teppei; Sugahara, Tohru; Nagao, Shijo; Nogi, Masaya; Koga, Hirotaka; Suganuma, Katsuaki; Uchida, Hiroshi

2016-03-09

Copper nanowire (CuNW) conductors have been considered to have a promising perspective in the area of stretchable electronics due to the low price and high conductivity. However, the fabrication of CuNW conductors suffers from harsh conditions, such as high temperature, reducing atmosphere, and time-consuming transfer step. Here, a simple and rapid one-step photonic sintering technique was developed to fabricate stretchable CuNW conductors on polyurethane (PU) at room temperature in air environment. It was observed that CuNWs were instantaneously deoxidized, welded and simultaneously embedded into the soft surface of PU through the one-step photonic sintering technique, after which highly conductive network and strong adhesion between CuNWs and PU substrates were achieved. The CuNW/PU conductor with sheet resistance of 22.1 Ohm/sq and transmittance of 78% was achieved by the one-step photonic sintering technique within only 20 μs in air. Besides, the CuNW/PU conductor could remain a low sheet resistance even after 1000 cycles of stretching/releasing under 10% strain. Two flexible electronic devices, wearable sensor and glove-shaped heater, were fabricated using the stretchable CuNW/PU conductor, demonstrating that our CuNW/PU conductor could be integrated into various wearable electronic devices for applications in food, clothes, and medical supplies fields.

Fabrication, Structural Characterization and Uniaxial Tensile Properties of Novel Sintered Multi-Layer Wire Mesh Porous Plates

PubMed Central

Duan, Liuyang; Zhou, Zhaoyao; Yao, Bibo

2018-01-01

There is an increasing interest in developing porous metals or metallic foams for functional and structural applications. The study of the physical and mechanical properties of porous metals is very important and helpful for their application. In this paper, a novel sintered multilayer wire mesh porous plate material (WMPPs) with a thickness of 0.5 mm–3 mm and a porosity of 10–35% was prepared by winding, pressing, rolling, and subsequently vacuum sintering them. The pore size and total size distribution in the as-prepared samples were investigated using the bubble point method. The uniaxial tensile behavior of the WMPPs was investigated in terms of the sintering temperature, porosity, wire diameter, and manufacturing technology. The deformation process and the failure mechanism under the tensile press was also discussed based on the appearance of the fractures (SEM figures). The results indicated that the pore size and total size distribution were closely related to the raw material used and the sintering temperature. For the WMPPs prepared by the wire mesh, the pore structures were inerratic and the vast majority of pore size was less than 10 μm. On the other hand, for the WMPPs that were prepared by wire mesh and powder, the pore structures were irregular and the pore size ranged from 0 μm–50 μm. The experimental data showed that the tensile strength of WMPPs is much higher than any other porous metals or metallic foams. Higher sintering temperatures led to coarser joints between wires and resulted in higher tensile strength. The sintering temperature decreased from 1330 °C to 1130 °C and the tensile strength decreased from 296 MPa to 164 MPa. Lower porosity means that there are more metallurgical joints and metallic frameworks resisting deformation per unit volume. Therefore, lower porosities exhibit higher tensile strength. An increase of porosity from 17.14% to 32.5% led to the decrease of the tensile strength by 90 MPa. The coarser wires led to a bigger contact area between the interconnecting wires, resulting in a stronger sintering neck that exhibited higher tensile strength. The wire diameter increased from 81 μm to 122 μm and the tensile strength increased from 296 MPa to 362 MPa. The fracture morphology showed that the wires experience necking deformation and ductile fracture. PMID:29342129

Fabrication, Structural Characterization and Uniaxial Tensile Properties of Novel Sintered Multi-Layer Wire Mesh Porous Plates.

PubMed

Duan, Liuyang; Zhou, Zhaoyao; Yao, Bibo

2018-01-17

There is an increasing interest in developing porous metals or metallic foams for functional and structural applications. The study of the physical and mechanical properties of porous metals is very important and helpful for their application. In this paper, a novel sintered multilayer wire mesh porous plate material (WMPPs) with a thickness of 0.5 mm-3 mm and a porosity of 10-35% was prepared by winding, pressing, rolling, and subsequently vacuum sintering them. The pore size and total size distribution in the as-prepared samples were investigated using the bubble point method. The uniaxial tensile behavior of the WMPPs was investigated in terms of the sintering temperature, porosity, wire diameter, and manufacturing technology. The deformation process and the failure mechanism under the tensile press was also discussed based on the appearance of the fractures (SEM figures). The results indicated that the pore size and total size distribution were closely related to the raw material used and the sintering temperature. For the WMPPs prepared by the wire mesh, the pore structures were inerratic and the vast majority of pore size was less than 10 μm. On the other hand, for the WMPPs that were prepared by wire mesh and powder, the pore structures were irregular and the pore size ranged from 0 μm-50 μm. The experimental data showed that the tensile strength of WMPPs is much higher than any other porous metals or metallic foams. Higher sintering temperatures led to coarser joints between wires and resulted in higher tensile strength. The sintering temperature decreased from 1330 °C to 1130 °C and the tensile strength decreased from 296 MPa to 164 MPa. Lower porosity means that there are more metallurgical joints and metallic frameworks resisting deformation per unit volume. Therefore, lower porosities exhibit higher tensile strength. An increase of porosity from 17.14% to 32.5% led to the decrease of the tensile strength by 90 MPa. The coarser wires led to a bigger contact area between the interconnecting wires, resulting in a stronger sintering neck that exhibited higher tensile strength. The wire diameter increased from 81 μm to 122 μm and the tensile strength increased from 296 MPa to 362 MPa. The fracture morphology showed that the wires experience necking deformation and ductile fracture.

Large-Scale Surfactant-Free Synthesis of p-Type SnTe Nanoparticles for Thermoelectric Applications

PubMed Central

Han, Guang; Zhang, Ruizhi; Popuri, Srinivas R.; Greer, Heather F.; Reece, Michael J.; Bos, Jan-Willem G.; Zhou, Wuzong; Knox, Andrew R.; Gregory, Duncan H.

2017-01-01

A facile one-pot aqueous solution method has been developed for the fast and straightforward synthesis of SnTe nanoparticles in more than ten gram quantities per batch. The synthesis involves boiling an alkaline Na2SnO2 solution and a NaHTe solution for short time scales, in which the NaOH concentration and reaction duration play vital roles in controlling the phase purity and particle size, respectively. Spark plasma sintering of the SnTe nanoparticles produces nanostructured compacts that have a comparable thermoelectric performance to bulk counterparts synthesised by more time- and energy-intensive methods. This approach, combining an energy-efficient, surfactant-free solution synthesis with spark plasma sintering, provides a simple, rapid, and inexpensive route to p-type SnTe nanostructured materials. PMID:28772593

Highly Dispersed and Active ReOx on Alumina-Modified SBA-15 Silica for 2-Butanol Dehydration

DOE Office of Scientific and Technical Information (OSTI.GOV)

She, Xiaoyan; Kwak, Ja Hun; Sun, Junming

2012-05-23

SBA-15 silica supported rhenium catalysts were synthesized using solution-based atomic layer deposition method, and their activity and stability were studied in the acid-catalyzed 2-butanol dehydration. We find that ReOx/SBA-15 exhibited an extremely high initial activity but a fast deactivation for 2-butanol dehydration at 90-105 C. Fast deactivation was likely due to the sintering, sublimation, and reduction of rhenia as confirmed by TEM, elemental analysis, and in situ UV vis (DRS) measurements. To overcome these issues, ReOx/AlOx/SBA-15 catalysts with significantly improved stability were prepared by first modifying the surface identity of SBA-15 with alumina followed by dispersion of rhenia using atomicmore » layer deposition. The AlOx phase stabilizes the dispersion of small and uniform rhenia clusters (<2 nm) as as confirmed by TEM, STEM and UV-vis (DRS) characterizations. Additional 27Al MAS NMR characterization revealed that modification of the SBA-15 surface with alumina introduces a strong interaction between rhenia and alumina, which consequently improves the stability of supported rhenia catalysts by suppressing the sintering, sublimation, and reduction of rhenia albeit at a moderately reduced initial catalytic dehydration activity« less

Synthesis of nano-scale fast ion conducting cubic Li7La3Zr2O12.

PubMed

Sakamoto, Jeff; Rangasamy, Ezhiylmurugan; Kim, Hyunjoung; Kim, Yunsung; Wolfenstine, Jeff

2013-10-25

A solution-based process was investigated for synthesizing cubic Li7La3Zr2O12 (LLZO), which is known to exhibit the unprecedented combination of fast ionic conductivity, and stability in air and against Li. Sol-gel chemistry was developed to prepare solid metal-oxide networks consisting of 10 nm cross-links that formed the cubic LLZO phase at 600 ° C. Sol-gel LLZO powders were sintered into 96% dense pellets using an induction hot press that applied pressure while heating. After sintering, the average LLZO grain size was 260 nm, which is 13 times smaller compared to LLZO prepared using a solid-state technique. The total ionic conductivity was 0.4 mS cm(-1) at 298 K, which is the same as solid-state synthesized LLZO. Interestingly, despite the same room temperature conductivity, the sol-gel LLZO total activation energy is 0.41 eV, which 1.6 times higher than that observed in solid-state LLZO (0.26 eV). We believe the nano-scale grain boundaries give rise to unique transport phenomena that are more sensitive to temperature when compared to the conventional solid-state LLZO.

New horizons in selective laser sintering surface roughness characterization

NASA Astrophysics Data System (ADS)

Vetterli, M.; Schmid, M.; Knapp, W.; Wegener, K.

2017-12-01

Powder-based additive manufacturing of polymers and metals has evolved from a prototyping technology to an industrial process for the fabrication of small to medium series of complex geometry parts. Unfortunately due to the processing of powder as a basis material and the successive addition of layers to produce components, a significant surface roughness inherent to the process has been observed since the first use of such technologies. A novel characterization method based on an elastomeric pad coated with a reflective layer, the Gelsight, was found to be reliable and fast to characterize surfaces processed by selective laser sintering (SLS) of polymers. With help of this method, a qualitative and quantitative investigation of SLS surfaces is feasible. Repeatability and reproducibility investigations are performed for both 2D and 3D areal roughness parameters. Based on the good results, the Gelsight is used for the optimization of vertical SLS surfaces. A model built on laser scanning parameters is proposed and after confirmation could achieve a roughness reduction of 10% based on the S q parameter. The Gelsight could be successfully identified as a fast, reliable and versatile surface topography characterization method as it applies to all kind of surfaces.

Forming a single layer of a composite powder based on the Ti-Nb system via selective laser melting (SLM)

NASA Astrophysics Data System (ADS)

Saprykin, A. A.; Sharkeev, Yu P.; Ibragimov, E. A.; Babakova, E. V.; Dudikhin, D. V.

2016-07-01

Alloys based on the titanium-niobium system are widely used in implant production. It is conditional, first of all, on the low modulus of elasticity and bio-inert properties of an alloy. These alloys are especially important for tooth replacement and orthopedic surgery. At present alloys based on the titanium-niobium system are produced mainly using conventional metallurgical methods. The further subtractive manufacturing an end product results in a lot of wastes, increasing, therefore, its cost. The alternative of these processes is additive manufacturing. Selective laser melting is a technology, which makes it possible to synthesize products of metal powders and their blends. The point of this technology is laser melting a layer of a powdered material; then a sintered layer is coated with the next layer of powder etc. Complex products and working prototypes are made on the base of this technology. The authors of this paper address to the issue of applying selective laser melting in order to synthesize a binary alloy of a composite powder based on the titanium-niobium system. A set of 10x10 mm samples is made in various process conditions. The samples are made by an experimental selective laser synthesis machine «VARISKAF-100MB». The machine provides adjustment of the following process variables: laser emission power, scanning rate and pitch, temperature of powder pre-heating, thickness of the layer to be sprinkled, and diameter of laser spot focusing. All samples are made in the preliminary vacuumized shielding atmosphere of argon. The porosity and thickness of the sintered layer related to the laser emission power are shown at various scanning rates. It is revealed that scanning rate and laser emission power are adjustable process variables, having the greatest effect on forming the sintered layer.

Structural and Chemical Analysis of the Zirconia-Veneering Ceramic Interface.

PubMed

Inokoshi, M; Yoshihara, K; Nagaoka, N; Nakanishi, M; De Munck, J; Minakuchi, S; Vanmeensel, K; Zhang, F; Yoshida, Y; Vleugels, J; Naert, I; Van Meerbeek, B

2016-01-01

The interfacial interaction of veneering ceramic with zirconia is still not fully understood. This study aimed to characterize morphologically and chemically the zirconia-veneering ceramic interface. Three zirconia-veneering conditions were investigated: 1) zirconia-veneering ceramic fired on sandblasted zirconia, 2) zirconia-veneering ceramic on as-sintered zirconia, and 3) alumina-veneering ceramic (lower coefficient of thermal expansion [CTE]) on as-sintered zirconia. Polished cross-sectioned ceramic-veneered zirconia specimens were examined using field emission gun scanning electron microscopy (Feg-SEM). In addition, argon-ion thinned zirconia-veneering ceramic interface cross sections were examined using scanning transmission electron microscopy (STEM)-energy dispersive X-ray spectrometry (EDS) at high resolution. Finally, the zirconia-veneering ceramic interface was quantitatively analyzed for tetragonal-to-monoclinic phase transformation and residual stress using micro-Raman spectroscopy (µRaman). Feg-SEM revealed tight interfaces for all 3 veneering conditions. High-resolution transmission electron microscopy (HRTEM) disclosed an approximately 1.0-µm transformed zone at sandblasted zirconia, in which distinct zirconia grains were no longer observable. Straight grain boundaries and angular grain corners were detected up to the interface of zirconia- and alumina-veneering ceramic with as-sintered zirconia. EDS mapping disclosed within the zirconia-veneering ceramic a few nanometers thick calcium/aluminum-rich layer, touching the as-sintered zirconia base, with an equally thick silicon-rich/aluminum-poor layer on top. µRaman revealed t-ZrO2-to-m-ZrO2 phase transformation and residual compressive stress at the sandblasted zirconia surface. The difference in CTE between zirconia- and the alumina-veneering ceramic resulted in residual tensile stress within the zirconia immediately adjacent to its interface with the veneering ceramic. The rather minor chemical elemental shifts recorded in the veneering ceramic did not suffice to draw definitive conclusions regarding potential chemical interaction of the veneering ceramic with zirconia. Sandblasting damaged the zirconia surface and induced phase transformation that also resulted in residual compressive stress. Difference in CTE of zirconia versus that of the veneering ceramic resulted in an unfavorable residual tensile stress at the zirconia-veneering ceramic interface. © International & American Associations for Dental Research 2015.

Polarization of fast particle beams by collisional pumping

DOEpatents

Stearns, J. Warren; Kaplan, Selig N.; Pyle, Robert V.; Anderson, L. Wilmer; Ruby, Lawrence; Schlachter, Alfred S.

1988-01-01

Method and apparatus for highly polarizing a fast beam of particles by collisional pumping, including generating a fast beam of particles, and also generating a thick electron-spin-polarized medium positioned as a target for the beam. The target is made sufficiently thick to allow the beam to interact with the medium to produce collisional pumping whereby the beam becomes highly polarized.

Young Investigator Program: Quasi-Liquid Grain Boundary Films in Refractory Metals

DTIC Science & Technology

2010-01-15

have been conducted for W using various dopants with significantly different effectiveness [48, 52], enabling a critical test of the hypothesized...thickness vs. temperature for dopant -saturated W specimens. (b) The experimental sintering (densification) rates. Reprinted from an AFOSR supported...the colloidal theory (Fig. 16b). The basic concepts can be explained as follows. By reducing the temperature, or dopant activity, a quasi-liquid

The development of manganese oxide coated ceramic membranes for combined catalytic ozonation and ultrafiltration of drinking water

NASA Astrophysics Data System (ADS)

Corneal, Lindsay Marie

A novel method for the preparation of hydrated MnO2 by the ozonation of MnCl2 in water is described. The hydrated MnO 2 was used to coat titania water filtration membranes using a layer-by-layer technique. The coated membranes were then sintered in air at 500°C for 45 minutes. Upon sintering, the MnO2 is converted to alpha-Mn 2O3 (as characterized by x-ray and electron diffraction). Atomic force microscopy (AFM) imaging showed no significant change in the roughness or height of the surface features of coated membranes, while scanning electron microscopy (SEM) imaging showed an increase in grain size with increasing number of coating layers. Energy dispersive x-ray spectroscopy (EDS) mapping and line scans revealed manganese present throughout the membrane, indicating that manganese dispersed into the porous membrane during the coating process and diffused into the titania grains during sintering. Selected area diffraction (SAD) of the coated and sintered membrane was used to index the surface layer as alpha-Mn2O3. The surface layer was uneven, although there was a trend of increasing thickness with increasing coating layers. The coating acts as a catalyst for the oxidation of organic matter when coated membranes are used in a hybrid ozonation-membrane filtration system. A trend of decreasing total organic carbon (TOC) in the permeate water was observed with increasing number of coating layers. The catalytic activity also manifests itself as improved recovery of the water flux due to oxidation of foulants on the membrane surface. Ceramic nanoparticle coatings on ceramic water filtration membranes must undergo high temperature sintering. However, this means that the underlying membrane, which has been engineered for a given molecular weight cut-off (MWCO), also undergoes a high temperature heat treatment that serves to increase pore size that have resulted in increases in permeability of titania membranes. Coating the titania membrane with manganese oxide followed by sintering in air at 500°C maintains the MWCO of the membranes, with high DI water permeability, which may be favorable in terms of membrane use. SEM micrographs of titania membrane samples sintered between 500°C to 900°C were analyzed to identify a statistically significant increase in grain size with increasing sintering temperature. The grains however, generally retain a uniform shape until the 900°C sintering temperature, where large, irregularly shaped grains were observed. AFM analysis showed a corresponding increase in the surface roughness of the membrane for the sample sintered at 900°C.

Estimation of Antarctic Land-Fast Sea Ice Algal Biomass and Snow Thickness From Under-Ice Radiance Spectra in Two Contrasting Areas

NASA Astrophysics Data System (ADS)

Wongpan, P.; Meiners, K. M.; Langhorne, P. J.; Heil, P.; Smith, I. J.; Leonard, G. H.; Massom, R. A.; Clementson, L. A.; Haskell, T. G.

2018-03-01

Fast ice is an important component of Antarctic coastal marine ecosystems, providing a prolific habitat for ice algal communities. This work examines the relationships between normalized difference indices (NDI) calculated from under-ice radiance measurements and sea ice algal biomass and snow thickness for Antarctic fast ice. While this technique has been calibrated to assess biomass in Arctic fast ice and pack ice, as well as Antarctic pack ice, relationships are currently lacking for Antarctic fast ice characterized by bottom ice algae communities with high algal biomass. We analyze measurements along transects at two contrasting Antarctic fast ice sites in terms of platelet ice presence: near and distant from an ice shelf, i.e., in McMurdo Sound and off Davis Station, respectively. Snow and ice thickness, and ice salinity and temperature measurements support our paired in situ optical and biological measurements. Analyses show that NDI wavelength pairs near the first chlorophyll a (chl a) absorption peak (≈440 nm) explain up to 70% of the total variability in algal biomass. Eighty-eight percent of snow thickness variability is explained using an NDI with a wavelength pair of 648 and 567 nm. Accounting for pigment packaging effects by including the ratio of chl a-specific absorption coefficients improved the NDI-based algal biomass estimation only slightly. Our new observation-based algorithms can be used to estimate Antarctic fast ice algal biomass and snow thickness noninvasively, for example, by using moored sensors (time series) or mapping their spatial distributions using underwater vehicles.

Copper sludge from printed circuit board production/recycling for ceramic materials: a quantitative analysis of copper transformation and immobilization.

PubMed

Tang, Yuanyuan; Lee, Po-Heng; Shih, Kaimin

2013-08-06

The fast development of electronic industries and stringent requirement of recycling waste electronics have produced a large amount of metal-containing waste sludge. This study developed a waste-to-resource strategy to beneficially use such metal-containing sludge from the production and recycling processes of printed circuit board (PCBs). To observe the metal incorporation mechanisms and phase transformation processes, mixtures of copper industrial waste sludge and kaolinite-based materials (kaolinite and mullite) were fired between 650 and 1250 °C for 3 h. The different copper-hosting phases were identified by powder X-ray diffraction (XRD) in the sintered products, and CuAl2O4 was found to be the predominant hosting phase throughout the reactions, regardless of the strong reduction potential of copper expected at high temperatures. The experimental results indicated that CuAl2O4 was generated more easily and in larger quantities at low-temperature processing when using the kaolinite precursor. Maximum copper transformations reached 86% and 97% for kaolinite and mullite systems, respectively, when sintering at 1000 °C. To monitor the stabilization effect after thermal process, prolonged leaching tests were carried out using acetic acid with an initial pH value of 2.9 to leach the sintered products for 20 days. The results demonstrated the decrease of copper leachability with the formation of CuAl2O4, despite different sintering behavior in kaolinite and mullite systems. This study clearly indicates spinel formation as the most crucial metal stabilization mechanism when sintering copper sludge with aluminosilicate materials, and suggests a promising and reliable technique for reusing metal-containing sludge as ceramic materials.

Polarization of fast particle beams by collisional pumping

DOEpatents

Stearns, J.W.; Kaplan, S.N.; Pyle, R.V.; Anderson, L.W.; Schlachter, A.S.; Ruby, L.

1984-10-19

The invention relates to method and apparatus for polarizing a fast beam of particles by collisional pumping, including generating a fast beam of particles, and generating a thick electron-spin-polarized medium positioned as a target for said beam, said medium being sufficiently thick to allow said beam to interact with said medium to produce collisional pumping whereby said particle beam becomes highly polarized.

Mechanical characterization of injection-molded macro porous bioceramic bone scaffolds.

PubMed

Vivanco, Juan; Aiyangar, Ameet; Araneda, Aldo; Ploeg, Heidi-Lynn

2012-05-01

Bioactive ceramic materials like tricalcium phosphate (TCP) have been emerging as viable material alternatives to the current therapies of bone scaffolding to target fracture healing and osteoporosis. Both material and architectural characteristics play a critical role in the osteoconductive capacity and strength of bone scaffolds. Thus, the objective of this research was to investigate the sintering temperature effect of a cost-effective manufacturing process on the architecture and mechanical properties of a controlled macro porous bioceramic bone scaffold. In this study the physical and mechanical properties of β-TCP bioceramic scaffolds were investigated as a function of the sintering temperature in the range of 950-1150 °C. Physical properties investigated included bulk dimensions, pore size, and strut thickness; and, compressive mechanical properties were evaluated in air at room temperature and in saline solution at body temperature. Statistically significant increases in apparent elastic modulus were measured for scaffolds sintered at higher temperatures. Structural stiffness for all the specimens was significantly reduced when tested at body temperature in saline solution. These findings support the development of clinically successful bioceramic scaffolds that may stimulate bone regeneration and scaffold integration while providing structural integrity. Copyright © 2012 Elsevier Ltd. All rights reserved.

Highly Enhanced Thermoelectric Properties of Bi/Bi2S3 Nanocomposites.

PubMed

Ge, Zhen-Hua; Qin, Peng; He, DongSheng; Chong, Xiaoyu; Feng, Dan; Ji, Yi-Hong; Feng, Jing; He, Jiaqing

2017-02-08

Bismuth sulfide (Bi 2 S 3 ) has been of high interest for thermoelectric applications due to the high abundance of sulfur on Earth. However, the low electrical conductivity of pristine Bi 2 S 3 results in a low figure of merit (ZT). In this work, Bi 2 S 3 @Bi core-shell nanowires with different Bi shell thicknesses were prepared by a hydrothermal method. The core-shell nanowires were densified to Bi/Bi 2 S 3 nanocomposite by spark plasma sintering (SPS), and the structure of the nanowire was maintained as the nanocomposite due to rapid SPS processing and low sintering temperature. The thermoelectric properties of bulk samples were investigated. The electrical conductivity of a bulk sample after sintering at 673 K for 5 min using Bi 2 S 3 @Bi nanowire powders prepared by treating Bi 2 S 3 nanowires in a hydrazine solution for 3 h is 3 orders of magnitude greater than that of a pristine Bi 2 S 3 sample. The nanocomposite possessed the highest ZT value of 0.36 at 623 K. This represents a new strategy for densifying core-shell powders to enhance their thermoelectric properties.

Low modulus and bioactive Ti/α-TCP/Ti-mesh composite prepared by spark plasma sintering.

PubMed

Guo, Yu; Tan, Yanni; Liu, Yong; Liu, Shifeng; Zhou, Rui; Tang, Hanchun

2017-11-01

A titanium mesh scaffold composite filled with Ti/α-TCP particles was prepared by spark plasma sintering (SPS). The microstructures and interfacial reactions of the composites were investigated by scanning electron microscopy (SEM), Energy Dispersive Spectroscopy (EDS) and X-ray diffraction (XRD) analyses. The compressive strength and elastic modulus were also measured. In vitro bioactivity and biocompatibility was evaluated by using simulated body fluid and cells culture, respectively. After high temperature sintering, Ti oxides, Ti x P y and CaTiO 3 were formed. The formation of Ti oxides and Ti x P y were resulted from the diffusion of O and P elements from α-TCP to Ti. CaTiO 3 was the reaction product of Ti and α-TCP. The composite of 70Ti/α-TCP incorporated with Ti mesh showed a high compressive strength of 589MPa and a low compressive modulus of 30GPa. The bioactivity test showed the formation of a thick apatite layer on the composite and well-spread cells attachment. A good combination of mechanical properties and bioactivity indicated a high potential application of Ti/α-TCP/Ti-mesh composite for orthopedic implants. Copyright © 2017. Published by Elsevier B.V.

Study of micropart fabrication via 17-4 PH stainless nanopowder injection molding.

PubMed

Tirta, Andy; Prasetyo, Yus; Baek, Eung-Ryul; Choi, Chul-Jin

2011-01-01

Micropart fabrication via 17-4 PH stainless nanopowder injection molding was investigated. The nanopowder was mixed with a binder that was based on wax to produce a feedstock composed of 45% powder and binder (the powder load). Initially, the fit and proper test was done before the micropart was made by making some bars of green samples, which the properties were examined after the sintering process. The examination involved the mechanical properties such as the porosity, hardness, and some of metallurgical aspects, such as the second-phase formation and the final compound after the sintering. The results showed that utilizing 17-4 PH stainless nanopowder is promising for micropart fabrication since it can form a nearly full-density sintered sample with a low porosity and good toughness, and can provide a smooth surface finish. After this, the investigations followed with the injection of the feedstock into the PDMS micromold that was formed by the nickel pattern from the X-Ray LIGA process. The green samples successfully produced a high-aspect-ratio sample with a thickness of up to 1 mm and an aspect ratio of 15 in the microchannel part. Then the green samples were sintered at 1,300 degrees C for 2 h, since from the initial test, they showed optimum parameters with nearly full density, low porosity, and a high degree of hardness. The research shows the excellent results of the application of the 17-4 PH stainless nanopowder to micropart fabrication.

Manufacturing of prestressed piezoelectric unimorphs using a postfired biasing layer.

PubMed

Juuti, Jari A; Jantunen, Heli; Moilanen, Veli-Pekka; Leppävuori, Seppo

2006-05-01

A novel manufacturing method for prestressed piezoelectric unimorphs is introduced and the actuator properties are examined. Prestressed PZT 5A and PZT 5H unimorphs with piezo material thickness of 250 microm and 375 microm were manufactured by using sintering and thermal shrinkage of the prestressing material. The process was carried out by screen printing a layer of AgPd paste on one side of the sintered bulk ceramic. As an alternative method, dielectric low temperature co-fired ceramic (LTCC) tape was used as the prestressing material. Different configurations were tested to obtain high displacements and to make a comparison between materials. After firing, the samples were poled, and the displacement versus load characteristics of the resulting actuators were investigated. A maximum displacement of 118 microm was obtained from a 250 microm thick, prestressed PZT 5H actuator with a diameter of 25 mm, in which LTCC tape was used as the prestressing layer. Similarly, the PZT 5H material provided a maximum displacement of 63 microm with a screen-printed AgPd prestressing layer. The manufacturing method described offers a novel approach for the production of a wide range of integrated active structures on, for instance, an LTCC circuit board. This is especially important because piezoelectric bulk materials with high piezoelectric coefficients can be used to produce high displacements.

Modeling the interface of platinum and α-quartz(001): Implications for sintering

DOE PAGES

Plessow, Philipp N.; Sánchez-Carrera, Roel S.; Li, Lin; ...

2016-05-04

We present a first-principles study which aims to understand the metal–support interaction of platinum nanoparticles on α-quartz(001) and, more generally, silica. The thermodynamic stability of the α-quartz(001) surface and its interface with Pt(111) are investigated as a function of temperature and partial pressure of H 2O and O 2. Potential defects in the α-quartz(001) surface as well as the adsorption energies of the Pt atom are also studied. This allows us to draw conclusions concerning nanoparticle shape and the resistance toward particle migration based on the interface free energies. We find that, as for the clean α-quartz(001) surface, a dry,more » reconstructed interface is expected at temperatures that are high but within experimentally relevant ranges. On an ideal, dry, reconstructed surface, particle migration is predicted to be a fast sintering mechanism. On real surfaces, defects may locally prevent reconstruction and act as anchoring points. Finally, the energetics of the adsorption of platinum atoms on α-quartz(001) do not support surface-mediated single-atom migration as a viable path for sintering on the investigated surfaces.« less

FAST TRACK COMMUNICATION: Mechanical, electrical and micro-structural properties of La0.6Sr0.4Co0.2Fe0.8O3 perovskite-based ceramic foams

NASA Astrophysics Data System (ADS)

Gupta, Ravindra K.; Kim, Eun Yi; Noh, Ho Sung; Whang, Chin Myung

2008-02-01

Mechanical, electrical and micro-structural properties of new electronic conducting ceramic foams are reported. Ceramic foams are prepared using the slurry of La0.6Sr0.4Co0.2Fe0.8O3 (LSCF) by the polymeric sponge method, which is followed by spray coating for increasing the number of coatings-sinterings on polyurethane foams of 30, 45 and 60 ppi (pores per linear inch). An increase in the number of coatings-sinterings and ppi improved the compressive strength, density and electrical conductivity by decreasing the porosity to ~76%, as also observed by the SEM study. The three-times coated-sintered ceramic foams (60 ppi) exhibited optimum values of compressive strength of ~1.79 MPa and relative density of ~0.24 at 25 °C and electrical conductivity of ~22 S cm-1 at 600 °C with an activation energy of ~0.22 eV indicating its suitability as a solid oxide fuel cell current collector. The experimental results are discussed in terms of the Gibson and Ashby theoretical model.

TOPICAL REVIEW: Electric current activated/assisted sintering (ECAS): a review of patents 1906-2008

NASA Astrophysics Data System (ADS)

Grasso, Salvatore; Sakka, Yoshio; Maizza, Giovanni

2009-10-01

The electric current activated/assisted sintering (ECAS) is an ever growing class of versatile techniques for sintering particulate materials. Despite the tremendous advances over the last two decades in ECASed materials and products there is a lack of comprehensive reviews on ECAS apparatuses and methods. This paper fills the gap by tracing the progress of ECAS technology from 1906 to 2008 and surveys 642 ECAS patents published over more than a century. It is found that the ECAS technology was pioneered by Bloxam (1906 GB Patent No. 9020) who developed the first resistive sintering apparatus. The patents were searched by keywords or by cross-links and were withdrawn from the Japanese Patent Office (342 patents), the United States Patent and Trademark Office (175 patents), the Chinese State Intellectual Property Office of P.R.C. (69 patents) and the World Intellectual Property Organization (12 patents). A subset of 119 (out of 642) ECAS patents on methods and apparatuses was selected and described in detail with respect to their fundamental concepts, physical principles and importance in either present ECAS apparatuses or future ECAS technologies for enhancing efficiency, reliability, repeatability, controllability and productivity. The paper is divided into two parts, the first deals with the basic concepts, features and definitions of basic ECAS and the second analyzes the auxiliary devices/peripherals. The basic ECAS is classified with reference to discharge time (fast and ultrafast ECAS). The fundamental principles and definitions of ECAS are outlined in accordance with the scientific and patent literature.

Fasting glucose levels, incident diabetes, subclinical atherosclerosis and cardiovascular events in apparently healthy adults: A 12-year longitudinal study.

PubMed

Sitnik, Debora; Santos, Itamar S; Goulart, Alessandra C; Staniak, Henrique L; Manson, JoAnn E; Lotufo, Paulo A; Bensenor, Isabela M

2016-11-01

We aimed to study the association between fasting plasma glucose, diabetes incidence and cardiovascular burden after 10-12 years. We evaluated diabetes and cardiovascular events incidences, carotid intima-media thickness and coronary artery calcium scores in ELSA-Brasil (the Brazilian Longitudinal Study of Adult Health) baseline (2008-2010) of 1536 adults without diabetes in 1998. We used regression models to estimate association with carotid intima-media thickness (in mm), coronary artery calcium scores (in Agatston points) and cardiovascular events according to fasting plasma glucose in 1998. Adjusted diabetes incidence rate was 9.8/1000 person-years (95% confidence interval: 7.7-13.6/1000 person-years). Incident diabetes was positively associated with higher fasting plasma glucose. Fasting plasma glucose levels 110-125 mg/dL were associated with higher carotid intima-media thickness (β = 0.028; 95% confidence interval: 0.003-0.053). Excluding those with incident diabetes, there was a borderline association between higher carotid intima-media thickness and fasting plasma glucose 110-125 mg/dL (β = 0.030; 95% confidence interval: -0.005 to 0.065). Incident diabetes was associated with higher carotid intima-media thickness (β = 0.034; 95% confidence interval: 0.015-0.053), coronary artery calcium scores ⩾400 (odds ratio = 2.84; 95% confidence interval: 1.17-6.91) and the combined outcome of a coronary artery calcium scores ⩾400 or incident cardiovascular event (odds ratio = 3.50; 95% confidence interval: 1.60-7.65). In conclusion, fasting plasma glucose in 1998 and incident diabetes were associated with higher cardiovascular burden. © The Author(s) 2016.

Fabrication of fuel cell electrodes and other catalytic structures

DOEpatents

Smith, J.L.

1987-02-11

A porous layer of catalyst material suitable for use as an electrode in a molten carbonate fuel cell includes elongated pores substantially extending across the layer thickness. The catalyst layer is prepared by depositing particulate catalyst material into polymeric flocking on a substrate surface by a procedure such as tape casting. The loaded substrate is heated in a series of steps with rising temperatures to set the tape, thermally decompose the substrate with flocking and sinter bond the catalyst particles into a porous catalytic layer with elongated pores across its thickness. Employed as an electrode, the elongated pores provide distribution of reactant gas into contact with catalyst particles wetted by molten electrolyte. 1 fig.

Fabrication of catalytic electrodes for molten carbonate fuel cells

DOEpatents

Smith, James L.

1988-01-01

A porous layer of catalyst material suitable for use as an electrode in a molten carbonate fuel cell includes elongated pores substantially extending across the layer thickness. The catalyst layer is prepared by depositing particulate catalyst material into polymeric flocking on a substrate surface by a procedure such as tape casting. The loaded substrate is heated in a series of steps with rising temperatures to set the tape, thermally decompose the substrate with flocking and sinter bond the catalyst particles into a porous catalytic layer with elongated pores across its thickness. Employed as an electrode, the elongated pores provide distribution of reactant gas into contact with catalyst particles wetted by molten electrolyte.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ayala, Alicia; Corral, Erica L.; Loehman, Ronald E.

A tape casting procedure for fabricating ceramic magnesium oxide tapes has been developed as a method to produce flat sheets of sintered MgO that are thin and porous. Thickness of single layer tapes is in the range of 200-400 {micro}m with corresponding surface roughness values in the range of 10-20 {micro}m as measured by laser profilometry. Development of the tape casting technique required optimization of pretreatment for the starting magnesium oxide (MgO) powder as well as a detailed study of the casting slurry preparation and subsequent heat treatments for sintering and final tape flattening. Milling time of the ceramic powder,more » plasticizer, and binder mixture was identified as a primary factor affecting surface morphology of the tapes. In general, longer milling times resulted in green tapes with a noticeably smoother surface. This work demonstrates that meticulous control of the entire tape casting operation is necessary to obtain high-quality MgO tapes.« less

A study of degradation of plates for nickel-cadmium spacecraft cells. [feasibility of coining

NASA Technical Reports Server (NTRS)

Scott, W. R.

1973-01-01

The relative merits of coining and not coining of sintered nickel-oxide and cadmium plates was investigated. A survey of the industry including cell manufactures and users was made and results summarized. Sample plate materials from most commercial cell suppliers were obtained and characterized for properties that may correlate with the tendency toward physical disintegration during handling and over long periods of time in the cell. Special test methods were developed to obtain comparative data in a short time. A wide range of physical properties and coining thicknesses was observed, resulting in a range of responses. The stronger, less brittle materials resisted loss of sinter better than weaker materials whether or not coined. Coining improved handling and resistance to electrochemical cycling in all materials tested. An apparent exception was found to be due to improper coining of a tapered edge.

Influence of residual thermal stresses and geometric parameters on stress and electric fields in multilayer ceramic capacitors under electric bias

NASA Astrophysics Data System (ADS)

Jiang, Wu-Gui; Feng, Xi-Qiao; Nan, Ce-Wen

2008-07-01

The stress and electric fields in multilayer ceramic capacitors (MLCCs) under an applied electric bias were investigated by using a three-dimensional finite element model of ferroelectric ceramics. A coupled thermal-mechanical analysis was first made to calculate the residual thermal stress induced by the sintering process, and then a coupled electrical-mechanical analysis was performed to predict the total stress distribution in the MLCCs under a representative applied electric bias. The effects of the number of dielectric layers, the single layer thickness as well as the residual thermal stresses on the total stresses were all examined. The numerical results show that the residual thermal stress induced by the sintering process has a significant influence on the contribution of the total stresses and, therefore, should be taken into account in the design and evaluation of MLCC devices.

Combustion Joining of Regolith Tiles for In-Situ Fabrication of Launch/Landing Pads on the Moon and Mars

NASA Technical Reports Server (NTRS)

Ferguson, Robert E.; Shafirovich, Evgeny; Mantovani, James G.

2017-01-01

To mitigate dust problems during launch/landing operations in lunar and Mars missions, it is desired to build solid pads on the surface. Recently, strong tiles have been fabricated from lunar regolith simulants using high-temperature sintering. The present work investigates combustion joining of these tiles through the use of exothermic intermetallic reactions. Specifically, nickel/aluminum (1:1 mole ratio) mixture was placed in a gap between the tiles sintered from JSC-1A lunar regolith simulant. Upon ignition by a laser, a self-sustained propagation of the combustion front over the mixture occurred. Joining was improved with increasing the tile thickness from 6.3 mm to 12.7 mm. The temperatures sufficient for melting the glass phase of JSC-1A were recorded for 12.7-mm tiles, which explains the observed better joining.

Combustion Joining of Regolith Tiles for In-Situ Fabrication of Launch/Landing Pads on the Moon and Mars

NASA Technical Reports Server (NTRS)

Ferguson, Robert E.; Mantovani, James G.; Shafirovich, Evgeny

2017-01-01

To mitigate dust problems during launch-landing operations in lunar and Mars missions, it is desired to build solid pads on the surface. Recently, strong tiles have been fabricated from lunar regolith simulants using high-temperature sintering. The present work investigates combustion joining of these tiles through the use of exothermic intermetallic reactions. Specifically, nickel aluminum (1:1 mole ratio) mixture was placed in a gap between the tiles sintered from JSC-1A lunar regolith simulant. Upon ignition by a laser, a self-sustained propagation of the combustion front over the mixture occurred. Joining was improved with increasing the tile thickness from 6.3 mm to 12.7 mm. The temperatures sufficient for melting the glass phase of JSC-1A were recorded for 12.7-mm tiles, which explains the observed better joining.

Catastrophic onset of fast magnetic reconnection with a guide field

NASA Astrophysics Data System (ADS)

Cassak, P. A.; Drake, J. F.; Shay, M. A.

2007-05-01

It was recently shown that the slow (collisional) Sweet-Parker and the fast (collisionless) Hall magnetic reconnection solutions simultaneously exist for a wide range of resistivities; reconnection is bistable [Cassak, Shay, and Drake, Phys. Rev. Lett., 95, 235002 (2005)]. When the thickness of the dissipation region becomes smaller than a critical value, the Sweet-Parker solution disappears and fast reconnection ensues, potentially explaining how large amounts of magnetic free energy can accrue without significant release before the onset of fast reconnection. Two-fluid numerical simulations extending the previous results for anti-parallel reconnection (where the critical thickness is the ion skin depth) to component reconnection with a large guide field (where the critical thickness is the thermal ion Larmor radius) are presented. Applications to laboratory experiments of magnetic reconnection and the sawtooth crash are discussed.

Array automated assembly task low cost silicon solar array project, phase 2

NASA Technical Reports Server (NTRS)

Olson, C.

1980-01-01

Analyses of solar cell and module process steps for throughput rate, cost effectiveness, and reproductibility are reported. In addition to the concentration on cell and module processing sequences, an investigation was made into the capability of using microwave energy in the diffusion, sintering, and thick film firing steps of cell processing. Although the entire process sequence was integrated, the steps are treated individually with test and experimental data, conclusions, and recommendations.

Low temperature solid oxide electrolytes (LT-SOE): A review

NASA Astrophysics Data System (ADS)

Singh, B.; Ghosh, S.; Aich, S.; Roy, B.

2017-01-01

Low temperature solid oxide fuel cell (LT-SOFC) can be a source of power for vehicles, online grid, and at the same time reduce system cost, offer high reliability, and fast start-up. A huge amount of research work, as evident from the literature has been conducted for the enhancement of the ionic conductivity of LT electrolytes in the last few years. The basic conduction mechanisms, advantages and disadvantages of different LT oxide ion conducting electrolytes {BIMEVOX systems, bilayer systems including doped cerium oxide/stabilised bismuth oxide and YSZ/DCO}, mixed ion conducting electrolytes {doped cerium oxides/alkali metal carbonate composites}, and proton conducting electrolytes {doped and undoped BaCeO3, BaZrO3, etc.} are discussed here based on the recent research articles. Effect of various material aspects (composition, doping, layer thickness, etc.), fabrication methods (to achieve different microstructures and particle size), design related strategies (interlayer, sintering aid etc.), characterization temperature & environment on the conductivity of the electrolytes and performance of the fuel cells made from these electrolytes are shown in tabular form and discussed. The conductivity of the electrolytes and performance of the corresponding fuel cells are compared. Other applications of the electrolytes are mentioned. A few considerations regarding the future prospects are pointed.

Modeling Ultra-fast assembly and sintering of gold nanostructures

NASA Astrophysics Data System (ADS)

Lane, J. Matthew D.; Salerno, K. Michael; Grest, Gary S.; Fan, Hongyou

We use fully atomistic simulations to understand the role of extreme pressure in the assembly and sintering of fcc superlattices of alkanethiol-coated gold nanocrystals into larger nanostructures. Recent quasi-isentropic experiments have shown that 1D, 2D and 3D nanostructures can be formed and recovered from dynamic compression experiments on Sandia's Veloce pulsed power accelerator. Here, we describe the role of coating properties, such as ligand length and grafting density, on ligand migration and deformation processes during pressure-driven coalescence of metal nano cores into permanent nanowires, nanosheets and 3D structures. The role of uniaxial vs isotropic pressure and the effects of compression along various superlattice orientations will be discussed. Sandia National Laboratories is a multi-mission laboratory managed and operated by Sandia Corporation, a wholly owned subsidiary of Lockheed Martin Corporation, for the U.S. Department of Energy's National Nuclear Security Administration under contract DE-AC04-94AL85000.

'Beautiful' unconventional synthesis and processing technologies of superconductors and some other materials.

PubMed

Badica, Petre; Crisan, Adrian; Aldica, Gheorghe; Endo, Kazuhiro; Borodianska, Hanna; Togano, Kazumasa; Awaji, Satoshi; Watanabe, Kazuo; Sakka, Yoshio; Vasylkiv, Oleg

2011-02-01

Superconducting materials have contributed significantly to the development of modern materials science and engineering. Specific technological solutions for their synthesis and processing helped in understanding the principles and approaches to the design, fabrication and application of many other materials. In this review, we explore the bidirectional relationship between the general and particular synthesis concepts. The analysis is mostly based on our studies where some unconventional technologies were applied to different superconductors and some other materials. These technologies include spray-frozen freeze-drying, fast pyrolysis, field-assisted sintering (or spark plasma sintering), nanoblasting, processing in high magnetic fields, methods of control of supersaturation and migration during film growth, and mechanical treatments of composite wires. The analysis provides future research directions and some key elements to define the concept of 'beautiful' technology in materials science. It also reconfirms the key position and importance of superconductors in the development of new materials and unconventional synthesis approaches.

Dental implant customization using numerical optimization design and 3-dimensional printing fabrication of zirconia ceramic.

PubMed

Cheng, Yung-Chang; Lin, Deng-Huei; Jiang, Cho-Pei; Lin, Yuan-Min

2017-05-01

This study proposes a new methodology for dental implant customization consisting of numerical geometric optimization and 3-dimensional printing fabrication of zirconia ceramic. In the numerical modeling, exogenous factors for implant shape include the thread pitch, thread depth, maximal diameter of implant neck, and body size. Endogenous factors are bone density, cortical bone thickness, and non-osseointegration. An integration procedure, including uniform design method, Kriging interpolation and genetic algorithm, is applied to optimize the geometry of dental implants. The threshold of minimal micromotion for optimization evaluation was 100 μm. The optimized model is imported to the 3-dimensional slurry printer to fabricate the zirconia green body (powder is bonded by polymer weakly) of the implant. The sintered implant is obtained using a 2-stage sintering process. Twelve models are constructed according to uniform design method and simulated the micromotion behavior using finite element modeling. The result of uniform design models yields a set of exogenous factors that can provide the minimal micromotion (30.61 μm), as a suitable model. Kriging interpolation and genetic algorithm modified the exogenous factor of the suitable model, resulting in 27.11 μm as an optimization model. Experimental results show that the 3-dimensional slurry printer successfully fabricated the green body of the optimization model, but the accuracy of sintered part still needs to be improved. In addition, the scanning electron microscopy morphology is a stabilized t-phase microstructure, and the average compressive strength of the sintered part is 632.1 MPa. Copyright © 2016 John Wiley & Sons, Ltd.

Influence of the Oxygen content on the thermal migration of Xenon in ZrCxO1-x

NASA Astrophysics Data System (ADS)

Pipon, Y.; Toulhoat, N.; Moncoffre, N.; Gutierrez, G.; Maître, A.; Gendre, M.

2013-09-01

Zirconium carbide (ZrC) is a refractory ceramic presenting interesting properties such as a high melting point, a very high hardness and a good thermal stability. For these reasons, this material is considered as a candidate for fuel coating for fourth-generation reactors in particular for the Gas cooled Fast Reactors (GFR). The ceramic temperature could reach 1200 °C in normal reactor operation and reach 1700 °C in accidental conditions. It is therefore important to assess the ZrC thermal retention capacity regarding abundant and/or volatile fission products. This paper deals with the behavior of Xenon which is the major gaseous fission product created during fission. Previous studies have shown that Xenon remained motionless in an "Oxygen-poor" matrix such as ZrC0.95O0.05, up to temperatures of 1800 °C. However, Zirconium oxycarbides are known to be very sensitive to oxidation. This study aims therefore at studying the behavior of Xenon in Zirconium oxycarbide samples with different Oxygen contents. Xenon is introduced by ion implantation and the samples are annealed in secondary vacuum in the temperature range 1400 °C-1800 °C. The Oxygen profiles are determined by using the 16O(4He, 4He)16O nuclear reaction at 7.5 MeV and the concentration profiles of Xenon are measured by Rutherford Backscattering Spectrometry at each step of the treatment. The results show that the behavior of the material during annealing with respect to oxidation is strongly related to its initial Oxygen content. More generally, the higher the initial Oxygen content, the more important is the oxidation. Consequently, the Xenon migration is enhanced in Oxygen rich Zirconium carbides. at 1950 °C under vacuum with an applied load of 100 MPa by Spark Plasma Sintering (SPS) at the University of Toulouse (CNRS PNF2 platform) [22]. at 1845 °C under an Ar gas flow with an applied load of 40 MPa by Hot Pressing (HP) at Limoges. Sintered pellets were divided into two batches: (i) a batch of sintered pellets cut in the middle to analyze the centre of the pellet and named "Pellet Centre" in the following, and (ii) a batch of intact sintered pellets to analyze the edge of the pellets called "Pellet Edge". The pellet density was measured using Archimedes's method and the grain size was controlled after a 7 min annealing at 1800 °C by SEM.Each pellet was cut into several samples of 7 × 7 × 2 mm3 and polished to micron with a diamond paste. Fig. 1 illustrates the whole cutting process and the characteristics of each type of sample are summarized in Table 1 and are classified in four batches. The stoichiometry strongly influences the Xenon behavior at high temperature. The confinement of Xenon is excellent for the ZrC0.95O0.05 stoichiometry. Gutierrez et al. have already presented these results in previous papers [13,14] and shown that the stability of Xenon is related to the formation of nanometric sized bubbles that are trapped in the dislocation walls. The Xenon confinement is worse for the ZrC0.80O0.20 stoichiometry but, in a first approach, the sintering process does not seem to influence the Xenon behavior. In order to get more insight into the differences observed for this stoichiometry between the "Pellet Edge" and "Pellet Centre" samples, it was mandatory to check the Oxygen content in the Xenon implanted zones of the pellets. For the ZrC0.95O0.05 stoichiometry (Fig. 3a), the general trend for all profiles corresponds to an Oxygen enrichment at the sample surface on a thickness around 20 nm (corresponding to the resolution of the technique) followed by a drop and then a linearity of the Oxygen content in the depth of the samples. The polishing process and the pre annealing at 1400 °C for the "Polished sample" and the "As-Implanted" sample results in a rather strong oxidation of the sample surface but the amount of Oxygen remains lower than 20 at.%, whereas the Oxygen content at depth is similar to the powder's one. For increasing annealing temperatures, the Oxygen content drops at the sample surface as well as in the depth. For the samples annealed at 1800 °C, the Oxygen content in the implanted zone (˜50 nm and 300 nm) is even lower (around 1 at.%) than for the original powder. On the contrary, for all the samples corresponding to the ZrC0.80O0.20 stoichiometry, the Oxygen content is always higher than that of the original powder before sintering. Moreover, for all of these samples, the surface Oxygen contents of the annealed samples are always higher than that of the "Polished samples". The "As-Implanted" samples display heterogeneous Oxygen enrichment levels in the first 50 nm ("Pellet Centre" samples) or even 150 nm ("Pellet edge" samples). The amount of Oxygen enrichment and the enriched thickness are always higher for the "Pellet Edge" samples than for the "Pellet Centre" samples. For the "Pellet Centre" samples, the maximum Oxygen enrichment does not exceed 35 at.% at the very surface and the oxidized thickness does not exceed 150 nm and it decreases with the annealing time. For the "Pellet Edge" samples, maximum Oxygen enrichment reaches 62 at.% at the very surface and the oxidized thickness grows with the annealing time.

A High-Performance Sintered Iron Electrode for Rechargeable Alkaline Batteries to Enable Large-Scale Energy Storage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yang, Chenguang; Manohar, Aswin K.; Narayanan, S. R.

Iron-based alkaline rechargeable batteries such as iron-air and nickel-iron batteries are particularly attractive for large-scale energy storage because these batteries can be relatively inexpensive, environment- friendly, and also safe. Therefore, our study has focused on achieving the essential electrical performance and cycling properties needed for the widespread use of iron-based alkaline batteries in stationary and distributed energy storage applications.We have demonstrated for the first time, an advanced sintered iron electrode capable of 3500 cycles of repeated charge and discharge at the 1-hour rate and 100% depth of discharge in each cycle, and an average Coulombic efficiency of over 97%. Suchmore » a robust and efficient rechargeable iron electrode is also capable of continuous discharge at rates as high as 3C with no noticeable loss in utilization. We have shown that the porosity, pore size and thickness of the sintered electrode can be selected rationally to optimize specific capacity, rate capability and robustness. As a result, these advances in the electrical performance and durability of the iron electrode enables iron-based alkaline batteries to be a viable technology solution for meeting the dire need for large-scale electrical energy storage.« less

Rapid fabrication of mesoporous TiO2 thin films by pulsed fibre laser for dye sensitized solar cells

NASA Astrophysics Data System (ADS)

Hadi, Aseel; Alhabradi, Mansour; Chen, Qian; Liu, Hong; Guo, Wei; Curioni, Michele; Cernik, Robert; Liu, Zhu

2018-01-01

In this paper we demonstrate for the first time that a fibre laser with a wavelength of 1070 nm and a pulse width of milliseconds can be applied to generate mesoporous nanocrystalline (nc) TiO2 thin films on ITO coated glass in ambient atmosphere, by complete vaporisation of organic binder and inter-connection of TiO2 nanoparticles, without thermally damaging the ITO layer and the glass substrate. The fabrication of the mesoporous TiO2 thin films was achieved by stationary laser beam irradiation of 1 min. The dye sensitized solar cell (DSSC) with the laser-sintered TiO2 photoanode reached higher power conversion efficiency (PCE) of 3.20% for the TiO2 film thickness of 6 μm compared with 2.99% for the furnace-sintered. Electrochemical impedance spectroscopy studies revealed that the laser sintering under the optimised condition effectively decreased charge transfer resistance and increased electron lifetime of the TiO2 thin films. The use of the fibre laser with over 40% wall-plug efficiency offers an economically-feasible, industrial viable solution to the major challenge of rapid fabrication of large scale, mass production of mesoporous metal oxide thin film based solar energy systems, potentially for perovskite and monolithic tandem solar cells, in the future.

A High-Performance Sintered Iron Electrode for Rechargeable Alkaline Batteries to Enable Large-Scale Energy Storage

DOE PAGES

Yang, Chenguang; Manohar, Aswin K.; Narayanan, S. R.

2017-01-07

Iron-based alkaline rechargeable batteries such as iron-air and nickel-iron batteries are particularly attractive for large-scale energy storage because these batteries can be relatively inexpensive, environment- friendly, and also safe. Therefore, our study has focused on achieving the essential electrical performance and cycling properties needed for the widespread use of iron-based alkaline batteries in stationary and distributed energy storage applications.We have demonstrated for the first time, an advanced sintered iron electrode capable of 3500 cycles of repeated charge and discharge at the 1-hour rate and 100% depth of discharge in each cycle, and an average Coulombic efficiency of over 97%. Suchmore » a robust and efficient rechargeable iron electrode is also capable of continuous discharge at rates as high as 3C with no noticeable loss in utilization. We have shown that the porosity, pore size and thickness of the sintered electrode can be selected rationally to optimize specific capacity, rate capability and robustness. As a result, these advances in the electrical performance and durability of the iron electrode enables iron-based alkaline batteries to be a viable technology solution for meeting the dire need for large-scale electrical energy storage.« less

Electric current activated/assisted sintering (ECAS): a review of patents 1906–2008

PubMed Central

Grasso, Salvatore; Sakka, Yoshio; Maizza, Giovanni

2009-01-01

The electric current activated/assisted sintering (ECAS) is an ever growing class of versatile techniques for sintering particulate materials. Despite the tremendous advances over the last two decades in ECASed materials and products there is a lack of comprehensive reviews on ECAS apparatuses and methods. This paper fills the gap by tracing the progress of ECAS technology from 1906 to 2008 and surveys 642 ECAS patents published over more than a century. It is found that the ECAS technology was pioneered by Bloxam (1906 GB Patent No. 9020) who developed the first resistive sintering apparatus. The patents were searched by keywords or by cross-links and were withdrawn from the Japanese Patent Office (342 patents), the United States Patent and Trademark Office (175 patents), the Chinese State Intellectual Property Office of P.R.C. (69 patents) and the World Intellectual Property Organization (12 patents). A subset of 119 (out of 642) ECAS patents on methods and apparatuses was selected and described in detail with respect to their fundamental concepts, physical principles and importance in either present ECAS apparatuses or future ECAS technologies for enhancing efficiency, reliability, repeatability, controllability and productivity. The paper is divided into two parts, the first deals with the basic concepts, features and definitions of basic ECAS and the second analyzes the auxiliary devices/peripherals. The basic ECAS is classified with reference to discharge time (fast and ultrafast ECAS). The fundamental principles and definitions of ECAS are outlined in accordance with the scientific and patent literature. PMID:27877308

Aerosol Combustion Synthesis of Nanopowders and Processing to Functional Thin Films

NASA Astrophysics Data System (ADS)

Yi, Eongyu

In this dissertation, the advantages of liquid-feed flame spray pyrolysis (LF-FSP) process in producing nanoparticles (NPs) as well as processing the produced NPs to ceramic/polymer nanocomposite films and high density polycrystalline ceramic films are demonstrated. The LF-FSP process aerosolizes alcohol solutions of metalloorganic precursors by oxygen and combusts them at > 1500 °C. The combustion products are rapidly quenched ( 10s of ms) to < 400 °C, producing NPs with the same compositions as those of the precursor solutions. The high specific surface areas of NPs enable formulation of ceramic/polymer/interface(phase) ternary nanocomposites in which the interphase can be the determining factor of the final net properties. In ceramic processing, NPs show increased sinterability and provide access to small average grain sizes with fine control of microstructures, compared to when micron sized powders are used. Therefore, synthesis, processing, and characterization of NPs, NP derived nanocomposites and ceramic monoliths are of great interest. We first compare the LF-FSP to commercial FSP process by producing fumed silica. Combusting spirocyclic alkoxysilanes or Si(OEt)4 by LF-FSP process produced fumed silica very similar to SiCl4 derived products. Given LF-FSP approach does not require the containment constraints of the SiCl4 process and precursors are synthesized from rice hull ash, the reported approach represents a sustainable, green and potentially lower cost alternative. We then show the versatility of NPs in formulating flexible ceramic/polymer nanocomposites (BaTiO3/epoxy) with superior properties. Volume fractions of the BaTiO3 filler and composite film thicknesses were controlled to adjust the net dielectric constant and the capacitance. Measured net dielectric constants further deviated from theory, with increasing solids loadings, due to NP agglomeration. Wound nanocomposite capacitors showed ten times higher capacitance compared to the commercial counterpart. Following series of studies explore the use of flame made NPs in processing Li+ conducting membranes. Systematic doping studies were conducted in the LiTi2(PO4)3 system to modify the lattice constant, conduction channel width, and sintering behavior by introducing Al3+ and Si4+ dopants. Excess Li2O content was also adjusted to observe its effect on final microstructures and phase compositions. Improved densification rates were found in Li1.7 Al0.3Ti1.7Si0.4P2.6O 12 composition and thin films (52+/-1 microm) with conductivities of 0.3-0.5 mS cm-1 were achieved. Li6.25M0.25La3Zr2O12 (M = Al3+, Ga3+) thin films (25-28 microm) with conductivities of 0.2-1.3 mS cm-1 were also successfully processed using flame made NPs, overcoming processing challenges extant, resulting in significantly reduced energy input required for densification. Heating schedules, sintering atmospheres, and types of substrates were controlled to observe their effect on the sintering behavior. Furthermore, green film thicknesses were found to be a crucial variable determining the final microstructures and phase compositions due to the varying Li2O loss rates with change in thicknesses (surface/volume ratios). Using fully decomposed NP mixtures (Li2CO3/off-stoichiometric La2Zr2O 7), as obtained by LF-FSP, provides an ideal approach to use high surface/reaction energy and liquid phase sintering to drive densification.

The microwave properties of Ag(Ta0.8Nb0.2)O3 thick film interdigital capacitors on alumina substrates

NASA Astrophysics Data System (ADS)

Lee, Ku-Tak; Koh, Jung-Hyuk

2012-01-01

In this paper, we will introduce the microwave properties of Ag(Ta0.8Nb0.2)O3 thick film planar type interdigital capacitors fabricated on alumina substrates. The tailored paraelectric state of Ag(Ta,Nb)O3 allows the material to be regarded as a part of the family of microwave materials. As thick films formed in our experiment, Ag(Ta,Nb)O3 exhibited extremely low dielectric loss with relatively high dielectric permittivity. This low dielectric loss is a very important issue for microwave applications. Therefore, we investigated the microwave properties of Ag(Ta0.8Nb0.2)O3 thick film planar type interdigital capacitors. Ag(Ta0.8Nb0.2)O3 thick films were prepared by a screen-printing method on alumina substrates and were sintered at 1140 °C for 2 hrs. The XRD analysis results showed that the Ag(Ta0.8Nb0.2)O3 thick film has the perovskite structure. The frequency dependent dielectric permittivity showed that these Ag(Ta0.8Nb0.2)O3 thick film planar type interdigital capacitors have very weak frequency dispersions with low loss tangents in the microwave range.

Department of Defense Advisory Group on Electron Devices. Special Technology Area Review on Microwave Packaging Technology. Appendix

DTIC Science & Technology

1993-02-01

sintered in hydrogen furnace at very high temperatures . Multiple furnace firing occurs until the binders are removed and part density is achieved "* Process...and base Low temperature co-fired ceramic - Metallized for shielding and grounding - Low resistance thick-film metallization - High thermal resistance...ESPECIALLY LOW TEMPERATURE COFIRED CERAMIC CERAMICS HIGH THERMAL CONDUCTIVITY,MATCHED GaAS AND SILICON SUBSTRATE MATERIALS I I,1Z#A,17Mr1 J, TI

Lower-Conductivity Ceramic Materials for Thermal-Barrier Coatings

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.; Zhu, Dongming

2006-01-01

Doped pyrochlore oxides of a type described below are under consideration as alternative materials for high-temperature thermal-barrier coatings (TBCs). In comparison with partially-yttria-stabilized zirconia (YSZ), which is the state-of-the-art TBC material now in commercial use, these doped pyrochlore oxides exhibit lower thermal conductivities, which could be exploited to obtain the following advantages: For a given difference in temperature between an outer coating surface and the coating/substrate interface, the coating could be thinner. Reductions in coating thicknesses could translate to reductions in weight of hot-section components of turbine engines (e.g., combustor liners, blades, and vanes) to which TBCs are typically applied. For a given coating thickness, the difference in temperature between the outer coating surface and the coating/substrate interface could be greater. For turbine engines, this could translate to higher operating temperatures, with consequent increases in efficiency and reductions in polluting emissions. TBCs are needed because the temperatures in some turbine-engine hot sections exceed the maximum temperatures that the substrate materials (superalloys, Si-based ceramics, and others) can withstand. YSZ TBCs are applied to engine components as thin layers by plasma spraying or electron-beam physical vapor deposition. During operation at higher temperatures, YSZ layers undergo sintering, which increases their thermal conductivities and thereby renders them less effective as TBCs. Moreover, the sintered YSZ TBCs are less tolerant of stress and strain and, hence, are less durable.

Fracture resistance and marginal discrepancy of porcelain laminate veneers influenced by preparation design and restorative material in vitro.

PubMed

Lin, Tai-Min; Liu, Perng-Ru; Ramp, Lance C; Essig, Milton E; Givan, Daniel A; Pan, Yu-Hwa

2012-03-01

The purpose of this investigation is to evaluate marginal discrepancy and fracture resistance of two veneering materials using two preparation designs. Two veneer preparation designs (full and traditional) were restored with leucite-reinforced ceramic (ProCAD, Ivoclar Vivadent, Amherst, NY) milled by CAD/CAM (Cerec 3D milling system, Serona Dental Systems), and conventional sintered feldspathic porcelain (Noritake Super Porcelain EX3, Noritake Dental Supply Co). Forty-eight specimens were analysed with a sample size of n=12 per group. The thickness of each veneer was measured on four specific surfaces. Marginal discrepancy was evaluated with a replica technique and cross-sectional view using a digital microscope. The fracture resistance of veneers cemented on standardised composite resin dies was evaluated using a universal testing machine. Results were analysed with ANOVA, Tukey-Kramer post hoc testing, and linear regression. The results of this investigation revealed no correlation between the thickness and marginal discrepancy of the veneers. The full preparation design with ProCAD and the traditional preparation design with feldspathic porcelain manifested smaller gap. Fracture resistance was decreased for the full preparation design with feldspathic porcelain. In terms of marginal discrepancy and fracture resistance, the most favourable combination was a traditional veneer preparation design with conventional sintered feldspathic porcelain. For the full veneer preparation, a stronger ceramic material such as ProCAD is suggested. Published by Elsevier Ltd.

Invisible polynyas: Modulation of fast ice thickness by ocean heat flux on the Canadian polar shelf

NASA Astrophysics Data System (ADS)

Melling, Humfrey; Haas, Christian; Brossier, Eric

2015-02-01

Although the Canadian polar shelf is dominated by thick fast ice in winter, areas of young ice or open water do recur annually at locations within and adjacent to the fast ice. These polynyas are detectable by eye and sustained by wind or tide-driven ice divergence and ocean heat flux. Our ice-thickness surveys by drilling and towed electromagnetic sounder reveal that visible polynyas comprise only a subset of thin-ice coverage. Additional area in the coastal zone, in shallow channels and in fjords is covered by thin ice which is too thick to be discerned by eye. Our concurrent surveys by CTD reveal correlation between thin fast ice and above-freezing seawater beneath it. We use winter time series of air and ocean temperatures and ice and snow thicknesses to calculate the ocean-to-ice heat flux as 15 and 22 W/m2 at locations with thin ice in Penny Strait and South Cape Fjord, respectively. Near-surface seawater above freezing is not a sufficient condition for ocean heat to reach the ice; kinetic energy is needed to overcome density stratification. The ocean's isolation from wind under fast ice in winter leaves tides as the only source. Two tidal mechanisms driving ocean heat flux are discussed: diffusion via turbulence generated by shear at the under-ice and benthic boundaries, and the internal hydraulics of flow over topography. The former appears dominant in channels and the coastal zone and the latter in some silled fjords where and when the layering of seawater density permits hydraulically critical flow.

Self-Poling of BiFeO3 Thick Films.

PubMed

Khomyakova, Evgeniya; Sadl, Matej; Ursic, Hana; Daniels, John; Malic, Barbara; Bencan, Andreja; Damjanovic, Dragan; Rojac, Tadej

2016-08-03

Bismuth ferrite (BiFeO3) is difficult to pole because of the combination of its high coercive field and high electrical conductivity. This problem is particularly pronounced in thick films. The poling, however, must be performed to achieve a large macroscopic piezoelectric response. This study presents evidence of a prominent and reproducible self-poling effect in few-tens-of-micrometer-thick BiFeO3 films. Direct and converse piezoelectric measurements confirmed that the as-sintered BiFeO3 thick films yield d33 values of up to ∼20 pC/N. It was observed that a significant self-poling effect only appears in cases when the films are heated and cooled through the ferroelectric-paraelectric phase transition (Curie temperature TC ∼ 820 °C). These self-poled films exhibit a microstructure with randomly oriented columnar grains. The presence of a compressive strain gradient across the film thickness cooled from above the TC was experimentally confirmed and is suggested to be responsible for the self-poling effect. Finally, the macroscopic d33 response of the self-poled BiFeO3 film was characterized as a function of the driving-field frequency and amplitude.

Method of manufacturing a heat pipe wick with structural enhancement

DOEpatents

Andraka, Charles E [Albuquerque, NM; Adkins, Douglas R [Albuquerque, NM; Moreno, James B [Albuquerque, NM; Rawlinson, K Scott [Albuquerque, NM; Showalter, Steven K [Albuquerque, NM; Moss, Timothy A [Albuquerque, NM

2006-10-24

Heat pipe wick structure wherein a stout sheet of perforated material overlays a high performance wick material such as stainless steel felt affixed to a substrate. The inventive structure provides a good flow path for working fluid while maintaining durability and structural stability independent of the structure (or lack of structure) associated with the wick material. In one described embodiment, a wick of randomly laid .about.8 micron thickness stainless steel fibers is sintered to a metal substrate and a perforated metal overlay.

Heat pipe wick with structural enhancement

DOEpatents

Andraka, Charles E.; Adkins, Douglas R.; Moreno, James B.; Rawlinson, K. Scott; Showalter, Steven K.; Moss, Timothy A.

2003-11-18

Heat pipe wick structure wherein a stout sheet of perforated material overlays a high performance wick material such as stainless steel felt affixed to a substrate. The inventive structure provides a good flow path for working fluid while maintaining durability and structural stability independent of the structure (or lack of structure) associated with the wick material. In one described embodiment, a wick of randomly laid .about.8 micron thickness stainless steel fibers is sintered to a metal substrate and a perforated metal overlay.

CdZnO coated film: A material for photovoltaic applications

NASA Astrophysics Data System (ADS)

Zargar, R. A.; Bhat, M. A.; Reshi, H. A.; Khan, S. D.

2018-06-01

The present study reports structural and optical parameters of wide band gap oxide thick film prepared by screen-printing followed by sintering route. Characterization of the samples was carried out with UV-spectroscopy, XRD, SEM, and Photoluminous study. The XRD and SEM studies reveal that the film deposited is polycrystalline, double phase, and porous with unsymmetrical grain distributions. Optical diffused reflection spectroscopy and Pl measurements give optical band gap of 2.87 eV and near band edge emission at 430 nm.

Conventional, Bayesian, and Modified Prony's methods for characterizing fast and slow waves in equine cancellous bone

PubMed Central

Groopman, Amber M.; Katz, Jonathan I.; Holland, Mark R.; Fujita, Fuminori; Matsukawa, Mami; Mizuno, Katsunori; Wear, Keith A.; Miller, James G.

2015-01-01

Conventional, Bayesian, and the modified least-squares Prony's plus curve-fitting (MLSP + CF) methods were applied to data acquired using 1 MHz center frequency, broadband transducers on a single equine cancellous bone specimen that was systematically shortened from 11.8 mm down to 0.5 mm for a total of 24 sample thicknesses. Due to overlapping fast and slow waves, conventional analysis methods were restricted to data from sample thicknesses ranging from 11.8 mm to 6.0 mm. In contrast, Bayesian and MLSP + CF methods successfully separated fast and slow waves and provided reliable estimates of the ultrasonic properties of fast and slow waves for sample thicknesses ranging from 11.8 mm down to 3.5 mm. Comparisons of the three methods were carried out for phase velocity at the center frequency and the slope of the attenuation coefficient for the fast and slow waves. Good agreement among the three methods was also observed for average signal loss at the center frequency. The Bayesian and MLSP + CF approaches were able to separate the fast and slow waves and provide good estimates of the fast and slow wave properties even when the two wave modes overlapped in both time and frequency domains making conventional analysis methods unreliable. PMID:26328678

Halloysite nanotube-based electrospun ceramic nanofibre mat: a novel support for zeolite membranes

PubMed Central

Chen, Zhuwen; Zeng, Jiaying; Lv, Dong; Gao, Jinqiang; Zhang, Jian; Bai, Shan; Li, Ruili; Wu, Jingshen

2016-01-01

Some key parameters of supports such as porosity, pore shape and size are of great importance for fabrication and performance of zeolite membranes. In this study, we fabricated millimetre-thick, self-standing electrospun ceramic nanofibre mats and employed them as a novel support for zeolite membranes. The nanofibre mats were prepared by electrospinning a halloysite nanotubes/polyvinyl pyrrolidone composite followed by a programmed sintering process. The interwoven nanofibre mats possess up to 80% porosity, narrow pore size distribution, low pore tortuosity and highly interconnected pore structure. Compared with the commercial α-Al2O3 supports prepared by powder compaction and sintering, the halloysite nanotube-based mats (HNMs) show higher flux, better adsorption of zeolite seeds, adhesion of zeolite membranes and lower Al leaching. Four types of zeolite membranes supported on HNMs have been successfully synthesized with either in situ crystallization or a secondary growth method, demonstrating good universality of HNMs for supporting zeolite membranes. PMID:28083098

Study on AN Intermediate Temperature Planar Sofc

NASA Astrophysics Data System (ADS)

Wang, Shaorong; Cao, Jiadi; Chen, Wenxia; Lu, Zhiyi; Wang, Daqian; Wen, Ting-Lian

An ITSOFC consisted of Ni/YSZ anode supported YSZ composite thin film and La0.6Sr0.4CoO3 (LSCO) cathode combined with a Ce0.8Sm0.2O1.9 (CSO) interlayer was studied. Tape cast method was applied to prepare green sheets of Ni/YSZ anode supported YSZ composite thin film. After isostatic pressing and cosintering, the YSZ film on the Ni/YSZ anode was gas-tight dense, and 15-30μm thick. The area of the composite film was over 100 cm2. A CSO interlayer was sintered on to the YSZ electrolyte film to protect LSCO cathode from reaction with YSZ at high temperatures. The LSCO cathode layer was screen printed onto the CSO interlayer and sintered at 1200°C for 3h to form a single cell. The obtained single cell was operated with H2 as fuel and O2 as oxidant. The cell performance and impedance were measured and discussed relating with the component contributions.

Microstructure and mechanical properties of a hot-extruded Al-based composite reinforced with core-shell-structured Ti/Al3Ti

NASA Astrophysics Data System (ADS)

Zhang, Li; Wu, Bao-lin; Liu, Yu-lin

2017-12-01

An Al-based composite reinforced with core-shell-structured Ti/Al3Ti was fabricated through a powder metallurgy route followed by hot extrusion and was found to exhibit promising mechanical properties. The ultimate tensile strength and elongation of the composite sintered at 620°C for 5 h and extruded at a mass ratio of 12.75:1 reached 304 MPa and 14%, respectively, and its compressive deformation reached 60%. The promising mechanical properties are due to the core-shell-structured reinforcement, which is mainly composed of Al3Ti and Ti and is bonded strongly with the Al matrix, and to the reduced crack sensitivity of Al3Ti. The refined grains after hot extrusion also contribute to the mechanical properties of this composite. The mechanical properties might be further improved through regulating the relative thickness of Al-Ti intermetallics and Ti metal layers by adjusting the sintering time and the subsequent extrusion process.

Phase Structures and Magnetic Properties of Graphite Nanosheets and Ni-Graphite Nanocomposite Synthesized by Electrical Explosion of Wire in Liquid

NASA Astrophysics Data System (ADS)

Nguyen, Minh-Thuyet; Kim, Jin-Hyung; Lee, Jung-Goo; Kim, Jin-Chun

2018-03-01

The present work studied on phases and magnetic properties of graphite nanosheets and Ni-graphite nanocomposite synthesized using the electrical explosion of wire (EEW) in ethanol. X-ray diffraction and field emission scanning electron microscope were used to investigate the phases and the morphology of the nanopowders obtained. It was found that graphite nanosheets were absolutely fabricated by EEW with a thickness of 29 nm and 3 μm diameter. The as-synthesized Ni-graphite composite powders had a Ni-coating on the surfaces of graphite sheets. The hysteresis loop of the as-exploded, the hydrogen-treated composite nanopowders and the sintered samples were examined with a vibrating sample magnetometer at room temperature. The Ni-graphite composite exposed the magnetic behaviors which are attributed to Ni component. The magnetic properties of composite had the improvement from 10.2 emu/g for the as-exploded powders to 15.8 emu/g for heat-treated powders and 49.16 emu/g for sintered samples.

Coercivity enhancement of sintered Nd-Fe-B magnets by chemical bath deposition of TbCl{sub 3}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Guo, Shuai, E-mail: gshuai@nimte.ac.cn; Zhang, Xiaofeng; Ding, Guangfei

2014-05-07

The chemical bath deposition (CBD) and the grain boundary diffusion method were combined to diffuse the heavy rare earth for obtain the thick magnets with high coercivity and low heavy rare earth. The jet mill powders were soaked into the alcohol solution of 0.2 wt. % TbCl{sub 3}. A thin layer of TbCl{sub 3} was wrapped to the surface of (PrNd){sub 2}Fe{sub 14}B powder particles. The coercivity of magnet is increased from 11.89 kOe to 14.72 kOe without significant reduction of remanence after grain boundary diffusion in the sintering and the annealing processes. The temperature coefficients of the remanence and themore » coercivity are improved by the substitution of PrNd by Tb in the surface of grains. The highly accelerated temperature/humidity stress test (HAST) results indicate that the CBD magnet has poor corrosion resistance, attributing to the present of Cl atoms in the grain boundaries.« less

Effect of the co-spun anode functional layer on the performance of the direct-methane microtubular solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Meng, Xiuxia; Gong, Xun; Yin, Yimei; Yang, Naitao; Tan, Xiaoyao; Ma, Zi-Feng

2014-02-01

NiO-YSZ/porous YSZ (NiO-YSZ/p-YSZ) dual-layer hollow fibers have been fabricated by a co-spinning-sintering method, on which a dense YSZ films has been formed by a dip-coating and sintering process. A LSM-YSZ ink has been dip-coated on the dense YSZ films as cathode, while the Cu-CeO2 carbon-resistant catalyst has been impregnated in the p-YSZ layer to form double-anode supported micro tubular fuel cells (MT-SOFCs). The thickness of the Ni-YSZ layer, so called anode functional layer (AFL), is controlled from 74 μm to 13 μm by varying the spinning rates of the NiO-YSZ dopes. The maximum power density of an MT-SOFC, which is fabricated based on a thin co-spun AFL, reaches 566 mW cm-2 operated at 850 °C fed with dry methane, and is stably operated for 85 h without power declination.

Halloysite nanotube-based electrospun ceramic nanofibre mat: a novel support for zeolite membranes

NASA Astrophysics Data System (ADS)

Chen, Zhuwen; Zeng, Jiaying; Lv, Dong; Gao, Jinqiang; Zhang, Jian; Bai, Shan; Li, Ruili; Hong, Mei; Wu, Jingshen

2016-12-01

Some key parameters of supports such as porosity, pore shape and size are of great importance for fabrication and performance of zeolite membranes. In this study, we fabricated millimetre-thick, self-standing electrospun ceramic nanofibre mats and employed them as a novel support for zeolite membranes. The nanofibre mats were prepared by electrospinning a halloysite nanotubes/polyvinyl pyrrolidone composite followed by a programmed sintering process. The interwoven nanofibre mats possess up to 80% porosity, narrow pore size distribution, low pore tortuosity and highly interconnected pore structure. Compared with the commercial α-Al2O3 supports prepared by powder compaction and sintering, the halloysite nanotube-based mats (HNMs) show higher flux, better adsorption of zeolite seeds, adhesion of zeolite membranes and lower Al leaching. Four types of zeolite membranes supported on HNMs have been successfully synthesized with either in situ crystallization or a secondary growth method, demonstrating good universality of HNMs for supporting zeolite membranes.

Low-temperature fabrication of dye-sensitized solar cells by transfer of composite porous layers

NASA Astrophysics Data System (ADS)

Dürr, Michael; Schmid, Andreas; Obermaier, Markus; Rosselli, Silvia; Yasuda, Akio; Nelles, Gabriele

2005-08-01

Dye-sensitized solar cells have established themselves as a potential low-cost alternative to conventional solar cells owing to their remarkably high power-conversion efficiency combined with `low-tech' fabrication processes. As a further advantage, the active layers consisting of nanoporous TiO2 are only some tens of micrometres thick and are therefore in principle suited for flexible applications. However, typical flexible plastic substrates cannot withstand the process temperatures of up to 500 ∘C commonly used for sintering the TiO2 nanoparticles together. Even though some promising routes for low-temperature sintering have been proposed, those layers cannot compete as regards electrical properties with layers obtained with the standard high-temperature process. Here we show that by a lift-off technique, presintered porous layers can be transferred to an arbitrary second substrate, and the original electrical properties of the transferred porous layers are maintained. The transfer process is greatly assisted by the application of composite layers comprising nanoparticles and nanorods.

Glass-ceramic coating material for the CO2 laser based sintering of thin films as caries and erosion protection.

PubMed

Bilandžić, Marin Dean; Wollgarten, Susanne; Stollenwerk, Jochen; Poprawe, Reinhart; Esteves-Oliveira, Marcella; Fischer, Horst

2017-09-01

The established method of fissure-sealing using polymeric coating materials exhibits limitations on the long-term. Here, we present a novel technique with the potential to protect susceptible teeth against caries and erosion. We hypothesized that a tailored glass-ceramic material could be sprayed onto enamel-like substrates to create superior adhesion properties after sintering by a CO 2 laser beam. A powdered dental glass-ceramic material from the system SiO 2 -Na 2 O-K 2 O-CaO-Al 2 O 3 -MgO was adjusted with individual properties suitable for a spray coating process. The material was characterized using X-ray fluorescence analysis (XRF), heating microscopy, dilatometry, scanning electron microscopy (SEM), grain size analysis, biaxial flexural strength measurements, fourier transform infrared spectroscopy (FTIR), and gas pycnometry. Three different groups of samples (each n=10) where prepared: Group A, powder pressed glass-ceramic coating material; Group B, sintered hydroxyapatite specimens; and Group C, enamel specimens (prepared from bovine teeth). Group B and C where spray coated with glass-ceramic powder. All specimens were heat treated using a CO 2 laser beam process. Cross-sections of the laser-sintered specimens were analyzed using laser scanning microscopy (LSM), energy dispersive X-ray analysis (EDX), and SEM. The developed glass-ceramic material (grain size d50=13.1mm, coefficient of thermal expansion (CTE)=13.310 -6 /K) could be spray coated on all tested substrates (mean thickness=160μm). FTIR analysis confirmed an absorption of the laser energy up to 95%. The powdered glass-ceramic material was successfully densely sintered in all sample groups. The coating interface investigation by SEM and EDX proved atomic diffusion and adhesion of the glass-ceramic material to hydroxyapatite and to dental enamel. A glass-ceramic material with suitable absorption properties was successfully sprayed and laser-sintered in thin films on hydroxyapatite as well as on bovine enamel. The presented novel technique of tooth coating with a dental glass-ceramic using a CO 2 -laser holds a great potential as a possible method to protect susceptible teeth against caries and erosion. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Spark plasma sintering synthesis of porous nanocrystalline titanium alloys for biomedical applications.

PubMed

Nicula, R; Lüthen, F; Stir, M; Nebe, B; Burkel, E

2007-11-01

The reason for the extended use of titanium and its alloys as implant biomaterials stems from their lower elastic modulus, their superior biocompatibility and improved corrosion resistance compared to the more conventional stainless steel and cobalt-based alloys [Niinomi, M., Hattori, T., Niwa, S., 2004. Material characteristics and biocompatibility of low rigidity titanium alloys for biomedical applications. In: Jaszemski, M.J., Trantolo, D.J., Lewandrowski, K.U., Hasirci, V., Altobelli, D.E., Wise, D.L. (Eds.), Biomaterials in Orthopedics. Marcel Dekker Inc., New York, pp. 41-62]. Nanostructured titanium-based biomaterials with tailored porosity are important for cell-adhesion, viability, differentiation and growth. Newer technologies like foaming or low-density core processing were recently used for the surface modification of titanium alloy implant bodies to stimulate bone in-growth and improve osseointegration and cell-adhesion, which in turn play a key role in the acceptance of the implants. We here report preliminary results concerning the synthesis of mesoporous titanium alloy bodies by spark plasma sintering. Nanocrystalline cp Ti, Ti-6Al-4V, Ti-Al-V-Cr and Ti-Mn-V-Cr-Al alloy powders were prepared by high-energy wet-milling and sintered to either full-density (cp Ti, Ti-Al-V) or uniform porous (Ti-Al-V-Cr, Ti-Mn-V-Cr-Al) bulk specimens by field-assisted spark plasma sintering (FAST/SPS). Cellular interactions with the porous titanium alloy surfaces were tested with osteoblast-like human MG-63 cells. Cell morphology was investigated by scanning electron microscopy (SEM). The SEM analysis results were correlated with the alloy chemistry and the topographic features of the surface, namely porosity and roughness.

Soft ferrite cores characterization for integrated micro-inductors

NASA Astrophysics Data System (ADS)

Nguyen, Yen Mai; Lopez, Thomas; Laur, Jean-Pierre; Bourrier, David; Charlot, Samuel; Valdez-Nava, Zarel; Bley, Vincent; Combettes, Céline; Brunet, Magali

2013-12-01

Ferrite-based micro-inductors are proposed for hybrid integration on silicon for low-power medium frequency DC-DC converters. Due to their small coercive field and their high resistivity, soft ferrites are good candidates for a magnetic core working at moderate frequencies in the range of 5-10 MHz. We have studied several soft ferrites including commercial ferrite film and U70 and U200 homemade ferrites. The inductors are fabricated at wafer level using micromachining and assembling techniques. The proposed process is based on a sintered ferrite core placed in between thick electroplated copper windings. The low profile ferrite cores of 1.2 × 2.6 × 0.2 mm3 are produced by two methods from green tape-casted films and ferrite powder. This paper presents the magnetic characterization of the sintered ferrite films cut and printed in rectangular shape and sintered at different temperatures. The comparison is made in order to find out the best material for the core that can reach the required inductance (470 nH at 6 MHz) under 0.6A current DC bias and that generate the smallest losses. An inductance density of 285 nH/ mm2 up to 6 MHz was obtained for ESL 40011 cores that is much higher than the previously reported devices. The small size of our devices is also a prominent point.

A screen-printed Ce 0.8Sm 0.2O 1.9 film solid oxide fuel cell with a Ba 0.5Sr 0.5Co 0.8Fe 0.2O 3- δ cathode

NASA Astrophysics Data System (ADS)

Zhang, Yaohui; Huang, Xiqiang; Lu, Zhe; Liu, Zhiguo; Ge, Xiaodong; Xu, Jiahuan; Xin, Xianshuang; Sha, Xueqing; Su, Wenhui

Screen-printing technology was developed to fabricate Ce 0.8Sm 0.2O 1.9 (SDC) electrolyte films onto porous NiO-SDC green anode substrates. After sintering at 1400 °C for 4 h, a gas-tight SDC film with a thickness of 12 μm was obtained. A novel cathode material of Ba 0.5Sr 0.5Co 0.8Fe 0.2O 3- δ was subsequently applied onto the sintered SDC electrolyte film also by screen-printing and sintered at 970 °C for 3 h to get a single cell. A fuel cell of Ni-SDC/SDC (12 μm)/Ba 0.5Sr 0.5Co 0.8Fe 0.2O 3- δ provides the maximum power densities of 1280, 1080, 670, 370, 180 and 73 mW cm -2 at 650, 600, 555, 505, 455 and 405 °C, respectively, using hydrogen as fuel and stationary air as oxidant. When dry methane was used as fuel, the maximum power densities are 876, 568, 346 and 114 mW cm -2 at 650, 600, 555 and 505 °C, respectively. The present fuel cell shows excellent performance at lowered temperatures.

Infiltrated W–Cu composites with combined architecture of hierarchical particulate tungsten and tungsten fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liang, Shuhua, E-mail: liangsh@xaut.edu.cn; Shaanxi Province Key Laboratory for Electrical Materials and Infiltration Technology, Xi'an 710048; Chen, Long

In this article, novel W–Cu composites reinforced with topologically-inserted tungsten fibers (W{sub f}) have been fabricated by hot-press sintering and infiltration method. By pre-sputtering of ~ 100 nm thick chromium layer onto the surface of W{sub f}, the contiguity or connectivity between W{sub f} and neighboring tungsten particles (W{sub p}) or Cu after sintering and infiltration was enhanced. Combined SEM, TEM and STEM techniques confirmed that the intact interfaces of W{sub f}/W{sub p} and W{sub f}/Cu free from precipitates, impurities and porosities would provide desirable strength and ductility. Further mechanical tests also validated its superior compressive strength and plasticity atmore » various temperatures, together with significantly improved tensile strength (by 23.6%) and hardness (by 9.3%) for the W–Cu composite after reinforcement with Cr-coated W{sub f}, which promotes the engineering application of the composite greatly. - Highlights: • W-fibers reinforced W–Cu composites were fabricated by sintering and infiltration. • The sputtered Cr onto W{sub f} has dissolved into adjacent W{sub f} and W{sub p} during fabrication. • The intact interfaces of W{sub f}/W{sub p} and W{sub f}/Cu confer enhanced strength and ductility. • Tensile strength and hardness improve by 23.6% and 9.3% after interface tuning.« less

Strength, Fracture Toughness, Fatigue, and Standardization Issues of Free-standing Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Zhu, Dong-Ming; Miller, Robert A.

2003-01-01

Strength, fracture toughness and fatigue behavior of free-standing thick thermal barrier coatings of plasma-sprayed ZrO2-8wt % Y2O3 were determined at ambient and elevated temperatures in an attempt to establish a database for design. Strength, in conjunction with deformation (stress-strain behavior), was evaluated in tension (uniaxial and trans-thickness), compression, and uniaxial and biaxial flexure; fracture toughness was determined in various load conditions including mode I, mode II, and mixed modes I and II; fatigue or slow crack growth behavior was estimated in cyclic tension and dynamic flexure loading. Effect of sintering was quantified through approaches using strength, fracture toughness, and modulus (constitutive relations) measurements. Standardization issues on test methodology also was presented with a special regard to material's unique constitutive relations.

Overview of the production of sintered SiC optics and optical sub-assemblies

NASA Astrophysics Data System (ADS)

Williams, S.; Deny, P.

2005-08-01

The following is an overview on sintered silicon carbide (SSiC) material properties and processing requirements for the manufacturing of components for advanced technology optical systems. The overview will compare SSiC material properties to typical materials used for optics and optical structures. In addition, it will review manufacturing processes required to produce optical components in detail by process step. The process overview will illustrate current manufacturing process and concepts to expand the process size capability. The overview will include information on the substantial capital equipment employed in the manufacturing of SSIC. This paper will also review common in-process inspection methodology and design rules. The design rules are used to improve production yield, minimize cost, and maximize the inherent benefits of SSiC for optical systems. Optimizing optical system designs for a SSiC manufacturing process will allow systems designers to utilize SSiC as a low risk, cost competitive, and fast cycle time technology for next generation optical systems.

Ultra-high aspect ratio titania nanoflakes for dye-sensitized solar cells

NASA Astrophysics Data System (ADS)

Lee, Yang-Yao; El-Shall, Hassan

2017-12-01

Micron sized titania flakes with thickness about 40 nm were used in the titania pastes to assemble dye-sensitized solar cells (DSSCs). Using the same deposition method, better particle dispersion of titania flakes resulted in well bonded and integral films comparing to cracking of Degussa P25 nanoparticle films during the evaporation and sintering processes. There are two features of titania flakes which leads to improved conversion efficiency of DSSC: (1) Higher and stronger adsorption of N-719 dyes due to high specific surface area (2) Stronger light scattering of visible light spectrum because of micron scale wide in two dimensions of the flakes. The thickness of the conducting TiO2 was critical to the IV characteristics of DSSC such as the short-circuit current density (Isc) and open-circuit voltage (Voc). Under the same thickness basis, calcined titania flakes provided 5 times higher efficiency than the photoelectrodes consisted of Degussa P25 nanoparticles (7.4% vs. 1.2%).

Magnetic force microscopy study of domain walls in Co{sub 2}Z ferrite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Qin, Lang; Verweij, Henk, E-mail: verweij.1@osu.edu

2014-03-01

Graphical abstract: - Highlights: • Hexaferrite Co{sub 2}Z is synthesized through the modified Pechini method. • Magnetic domains are observed in anisotropic Co{sub 2}Z single grain using MFM. • Observed single grain domain thickness is in good agreement with Dotsh model. - Abstract: Hexaferrite Co{sub 2}Z was synthesized through the modified Pechini method. Partially oriented samples were obtained after consolidation with uniaxial pressing and calcination/sintering at 1300 °C/1330 °C. The sample composition and morphology was identified with X-ray diffractometry (XRD) and scanning electron microscopy (SEM) with energy-dispersive X-ray spectrometry (EDS). MFM studies of the single grains revealed a domain structuremore » with 0.7 μm wide. The Co{sub 2}Z static magnetization was measured with a vibrating sample magnetometer (VSM), and was used to calculate a single grain domain with a thickness of 4.8 μm. This result is in good agreement with SEM observations of the single grain thickness.« less

Grain growth in uranium nitride prepared by spark plasma sintering

NASA Astrophysics Data System (ADS)

Johnson, Kyle D.; Lopes, Denise Adorno

2018-05-01

Uranium mononitride (UN) has long been considered a potential high density, high performance fuel candidate for light water reactor (LWR) and fast reactor (FR) applications. However, deployability of this fuel has been limited by the notable resistance to sintering and subsequent difficulty in producing a desirable microstructure, the high costs associated with 15N enrichment, as well as the known proclivity to oxidation and interaction with steam. In this study, the stimulation of grain growth in UN pellets sintered using SPS has been investigated. The results reveal that by using SPS and controlling temperature, time, and holding pressure, grain growth can be stimulated and controlled to produce a material featuring both a desired porosity and grain size, at least within the range of interest for nuclear fuel candidates. Grain sizes up to 31 μm were obtained using temperatures of 1650 °C and hold times of 15 min. Evaluation by EBSD reveal grain rotation and coalescence as the dominant mechanism in grain growth, which is suppressed by the application of higher external pressure. Moreover, complete closure of the porosity of the material was observed at relative densities of 96% TD, resulting in a material with sufficient porosity to accommodate LWR burnup. These results indicate that a method exists for the economic fabrication of an 15N-bearing uranium mononitride fuel with favorable microstructural characteristics compatible with use in a light water-cooled nuclear reactor.

Fabrication of Bi–Sb–Te Thermoelectric by Cold-Pressed Sintering for Motorcycle Exhaust.

PubMed

Kao, Mu-Jung; Chen, Ming-Jing

2017-04-01

This study was conducted on the Bi–Sb–Te thermoelectric material which is cold-pressed Sintering under 750 Mpa to make square thermoelectric pairs with size 8.2 mm × 8.2 mm and thicknesses 0.8 mm and 1.5 mm. The zone melting method was used to acquire P-type thermoelectric material Bi0.4Sb1.6Te3 and N-type thermoelectric material Bi2Te2.5Se0.5. At temperature 383 K, the measured Seebeck coefficient of Bi0.4Sb1.6Te3 is 222 μV/K, and its thermoelectric figure of merit ZT is 1.35. At temperature 400 K, the measured Seebeck coefficient of Bi2Te2.5Se0.5 is 210 μV/K, and its thermoelectric figure of merit ZT is 1.13. Using Solder paste Sn42Bi58 and copper electrode plate are in series connection with 16 pieces of P/N thermoelectric material to form thermoelectric modules. The thermoelectric module is actually pasted on the motorcycle waste heat source to be evaluated the performance, making the cold-end temperature dissipation heat can enhance the temperature difference between it so as to increase the output power. Increasing the leg thickness of thermoelectric module and making the about 35 °C temperature-difference of those can obviously enhance the performance of in terms of its voltage, its thermoelectric figure of merit ZT and output power of the thermoelectric modules.

Influence of cement film thickness on the retention of implant-retained crowns.

PubMed

Mehl, Christian; Harder, Sönke; Steiner, Martin; Vollrath, Oliver; Kern, Matthias

2013-12-01

The main goal of this study was to establish a new, high precision procedure to evaluate the influence of cement film thickness on the retention of cemented implant-retained crowns. Ninety-six tapered titanium abutments (6° taper, 4.3 mm diameter, Camlog) were shortened to 4 mm. Computer-aided design was used to design the crowns, and selective laser sintering, using a cobalt-chromium alloy, was used to produce the crowns. This method used a focused high-energy laser beam to fuse a localized region of metal powder to build up the crowns gradually. Before cementing, preset cement film thicknesses of 15, 50, 80, or 110 μm were established. Glass ionomer, polycarboxylate, or resin cements were used for cementation. After 3 days storage in demineralized water, the retention of the crowns was measured in tension using a universal testing machine. The cement film thicknesses could be achieved with a high level of precision. Interactions between the factors cement and cement film thickness could be found (p ≤ 0.001). For all cements, crown retention decreased significantly between a cement film thickness of 15 and 50 μm (p ≤ 0.001). At 15 μm cement film thickness, the resin cement was the most retentive cement, followed by the polycarboxylate and then the glass ionomer cement (p ≤ 0.05). The results suggest that cement film thickness has an influence on the retentive strength of cemented implant-retained crowns. © 2013 by the American College of Prosthodontists.

Final Report on Initial Samples Supplied by LLNL for Task 3.3 Binder Burnout and Sintering Schedule Optimisation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Walls, P

Sixteen of the twenty-one samples have been investigated using the scanning laser dilatometer. This includes all three types of samples with different preparation routes and organic content. Cracks were observed in all samples, even those only heated to 300 C. It was concluded that the cracking was occurring in the early part of the heat treatment before the samples reached 300 C. Increase in the rate of dilation of the samples occurred above 170 C which coincided with the decomposition of the binder/wax additives as determined by differential thermal analysis. A comparison was made with SYNROC C material (Powder Runmore » 143), samples of which had been CIPed and green machined to a similar diameter and thickness as the 089mm SRTC pucks. These samples contained neither binder nor other organic processing aids and had been kept in the same desiccator as the SRTC samples. The CIPed Synroc C samples sintered to high density with zero cracks. As the cracks made up only a small contribution to the change in diameter of the sample compared to the sintering shrinkage, useful information could still be gained from the runs. The sintering curves showed that there was much greater shrinkage of the Type III samples containing only the 5% PEG binder compared to the Type I which contained polyolefin wax as processing aid. Slight changes in gradient of the sintering curve were observed, however, due to the masking effect of the cracking, full analysis of the sintering kinetics cannot be conducted. Even heating the samples to 300 C at 1.0 or 0.5 C/min could not prevent crack formation. This indicated that heating rate was not the critical parameter causing cracking of the samples. Sectioning of green bodies revealed the inhomogeneous nature of the binder/lubricant distribution in the samples. Increased homogeneity would reduce the amount of binder/lubricant required, which should in turn, reduce the degree of cracking observed during heating to the binder burnout temperature. A combination of: (1) use of a higher forming pressure, (2) reduction of organics content, (3) improvement in the distribution of the organic wax and binder components throughout the green body, could possibly alleviate cracking. Ultrasonic emulsification of the binder and wax with a small quantity of water prior to adding to the ball or attrition mill is advised to ensure more even distribution of the wax/binder system. This would also reduce the proportion of organic additives required. The binder burnout stage of the operation must first be optimized (i.e. production of pucks with no cracks) prior to optimization of the sintering stage.« less

Aluminum powder metallurgy processing

NASA Astrophysics Data System (ADS)

Flumerfelt, Joel Fredrick

In recent years, the aluminum powder industry has expanded into non-aerospace applications. However, the alumina and aluminum hydroxide in the surface oxide film on aluminum powder require high cost powder processing routes. A driving force for this research is to broaden the knowledge base about aluminum powder metallurgy to provide ideas for fabricating low cost aluminum powder components. The objective of this dissertation is to explore the hypothesis that there is a strong linkage between gas atomization processing conditions, as-atomized aluminum powder characteristics, and the consolidation methodology required to make components from aluminum powder. The hypothesis was tested with pure aluminum powders produced by commercial air atomization commercial inert gas atomization and gas atomization reaction synthesis (GARS). The commercial atomization methods are bench marks of current aluminum powder technology. The GARS process is a laboratory scale inert gas atomization facility. A benefit of using pure aluminum powders is an unambiguous interpretation of the results without considering the effects of alloy elements. A comparison of the GARS aluminum powders with the commercial aluminum powders showed the former to exhibit superior powder characteristics. The powders were compared in terms of size and shape, bulk chemistry, surface oxide chemistry and structure, and oxide film thickness. Minimum explosive concentration measurements assessed the dependence of explosibility hazard on surface area, oxide film thickness, and gas atomization processing conditions. The GARS aluminum powders were exposed to different relative humidity levels, demonstrating the effect of atmospheric conditions on post-atomization oxidation of aluminum powder. An Al-Ti-Y GARS alloy exposed in ambient air at different temperatures revealed the effect of reactive alloy elements on post-atomization powder oxidation. The pure aluminum powders were consolidated by two different routes, a conventional consolidation process for fabricating aerospace components with aluminum powder and a proposed alternative. The consolidation procedures were compared by evaluating the consolidated microstructures and the corresponding mechanical properties. A low temperature solid state sintering experiment demonstrated that tap densified GARS aluminum powders can form sintering necks between contacting powder particles, unlike the total resistance to sintering of commercial air atomization aluminum powder.

The effect of nano-structured alumina coating on resin-bond strength to zirconia ceramics.

PubMed

Jevnikar, Peter; Krnel, Kristoffer; Kocjan, Andraz; Funduk, Nenad; Kosmac, Tomaz

2010-07-01

The aim of this study was to functionalize the surface of yttria partially stabilized tetragonal zirconia ceramics (Y-TZP) with a nano-structured alumina coating to improve resin bonding. A total of 120 densely sintered disc-shaped specimens (15.5+/-0.03 mm in diameter and 2.6+/-0.03 mm thick) were produced from biomedical-grade TZ-3YB-E zirconia powder (Tosoh, Tokyo, Japan), randomly divided into three groups of 40 and subjected to the following surface treatments: AS - as-sintered; APA - airborne-particle abraded; POL - polished. Half of the discs in each group received an alumina coating that was fabricated by exploiting the hydrolysis of aluminium nitride (AlN) powder (groups AS-C, APA-C, POL-C). The coating was characterized using scanning electron microscopy (SEM), atomic force microscopy (AFM), and transmission electron microscopy (TEM). The shear-bond strength of the self-etching composite resin (RelyX Unicem, 3M ESPE, USA) was then studied for the coated and uncoated surfaces of the as-sintered, polished and airborne-particle abraded specimens before and after thermocycling (TC). The SEM/TEM analyses revealed that the application of an alumina coating to Y-TZP ceramics created a highly retentive surface for resin penetration. The coating showed good surface coverage and a uniform thickness of 240 nm. The resin-bond strength to the groups AS-C, APA-C, POL-C was significantly higher than to the groups AS, APA and POL, both before and after TC (p< or =0.05). During TC all the specimens in the POL and AS groups debonded spontaneously. In contrast, the TC did not affect the bond strength of the AS-C, POL-C and APA-C groups. A non-invasive method has been developed that significantly improves resin-bond strength to Y-TZP ceramics. After surface functionalization the bond survives thermocycling without reduction in strength. The method is relatively simple and has the potential to become an effective conditioning method for zirconia ceramics. Copyright 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

A Simple Transmission Electron Microscopy Method for Fast Thickness Characterization of Suspended Graphene and Graphite Flakes.

PubMed

Rubino, Stefano; Akhtar, Sultan; Leifer, Klaus

2016-02-01

We present a simple, fast method for thickness characterization of suspended graphene/graphite flakes that is based on transmission electron microscopy (TEM). We derive an analytical expression for the intensity of the transmitted electron beam I 0(t), as a function of the specimen thickness t (t<λ; where λ is the absorption constant for graphite). We show that in thin graphite crystals the transmitted intensity is a linear function of t. Furthermore, high-resolution (HR) TEM simulations are performed to obtain λ for a 001 zone axis orientation, in a two-beam case and in a low symmetry orientation. Subsequently, HR (used to determine t) and bright-field (to measure I 0(0) and I 0(t)) images were acquired to experimentally determine λ. The experimental value measured in low symmetry orientation matches the calculated value (i.e., λ=225±9 nm). The simulations also show that the linear approximation is valid up to a sample thickness of 3-4 nm regardless of the orientation and up to several ten nanometers for a low symmetry orientation. When compared with standard techniques for thickness determination of graphene/graphite, the method we propose has the advantage of being simple and fast, requiring only the acquisition of bright-field images.

Highly sensitive graphene biosensor by monomolecular self-assembly of receptors on graphene surface

NASA Astrophysics Data System (ADS)

Kim, Ji Eun; No, Young Hyun; Kim, Joo Nam; Shin, Yong Seon; Kang, Won Tae; Kim, Young Rae; Kim, Kun Nyun; Kim, Yong Ho; Yu, Woo Jong

2017-05-01

Graphene has attracted a great deal of interest for applications in bio-sensing devices because of its ultra-thin structure, which enables strong electrostatic coupling with target molecules, and its excellent electrical mobility promising for ultra-fast sensing speeds. However, thickly stacked receptors on the graphene's surface interrupts electrostatic coupling between graphene and charged biomolecules, which can reduce the sensitivity of graphene biosensors. Here, we report a highly sensitive graphene biosensor by the monomolecular self-assembly of designed peptide protein receptors. The graphene channel was non-covalently functionalized using peptide protein receptors via the π-π interaction along the graphene's Bravais lattice, allowing ultra-thin monomolecular self-assembly through the graphene lattice. In thickness dependent characterization, a graphene sensor with a monomolecular receptor (thickness less than 3 nm) showed five times higher sensitivity and three times higher voltage shifts than graphene sensors with thick receptor stacks (thicknesses greater than 20 nm), which is attributed to excellent gate coupling between graphene and streptavidin via an ultrathin receptor insulator. In addition to having a fast-inherent response time (less than 0.6 s) based on fast binding speed between biotin and streptavidin, our graphene biosensor is a promising platform for highly sensitive real-time monitoring of biomolecules with high spatiotemporal resolution.

Interfacial contribution to the dielectric response in semiconducting LaBiMn4/3Co2/3O6

NASA Astrophysics Data System (ADS)

Filippi, M.; Kundys, B.; Ranjith, R.; Kundu, Asish K.; Prellier, W.

2008-05-01

Impedance measurements have been performed on a sintered polycrystalline sample of the perovskite LaBiMn4/3Co2/3O6. Colossal dielectric permittivity is often measured in this class of semiconducting materials as a result of extrinsic factors. Our results show that a large offset in the capacitance, measured on a series of samples with different thickness, is due to the interfacial polarization. This contribution can then be removed from the data, creating a general procedure for dielectric measurements in semiconducting samples.

Powder Metallurgy Reconditioning of Food and Processing Equipment Components

NASA Astrophysics Data System (ADS)

Nafikov, M. Z.; Aipov, R. S.; Konnov, A. Yu.

2017-12-01

A powder metallurgy method is developed to recondition the worn surfaces of food and processing equipment components. A combined additive is composed to minimize the powder losses in sintering. A technique is constructed to determine the powder consumption as a function of the required metallic coating thickness. A rapid method is developed to determine the porosity of the coating. The proposed technology is used to fabricate a wear-resistant defectless metallic coating with favorable residual stresses, and the adhesive strength of this coating is equal to the strength of the base metal.

Microscale 1-3-Type (Na,K)NbO(3)-Based Pb-Free Piezocomposites for High-Frequency Ultrasonic Transducer Applications.

PubMed

Shen, Zong-Yang; Li, Jing-Feng; Chen, Ruimin; Zhou, Qifa; Shung, K Kirk

2011-05-01

Fine-grained Pb-free (Na(0.535)K(0.485))(0.95)Li(0.05)(Nb(0.8)Ta(0.2))O(3) (NKLNT) piezoceramics prepared by spark plasma sintering (SPS) technique was used to fabricate NKLNT/epoxy 1-3 composites with a modified dice-fill method. Because of its good machinability, SPSed NKLNT ceramic rods could be miniaturized to a lateral width of 50 µm. After lapping down to 56 µm in thickness, the composite was used to fabricate an ultrasonic transducer as the active piezoelectric element. This composite transducer showed a bandwidth at -6 dB nearly 90%at a center frequency of 29 MHz, demonstrating that this Pb-free composite thick film is very promising for the fabrication of high-frequency ultrasonic transducers in medical imaging applications.

Mechanical Properties Optimization of Poly-Ether-Ether-Ketone via Fused Deposition Modeling.

PubMed

Deng, Xiaohu; Zeng, Zhi; Peng, Bei; Yan, Shuo; Ke, Wenchao

2018-01-30

Compared to the common selective laser sintering (SLS) manufacturing method, fused deposition modeling (FDM) seems to be an economical and efficient three-dimensional (3D) printing method for high temperature polymer materials in medical applications. In this work, a customized FDM system was developed for polyether-ether-ketone (PEEK) materials printing. The effects of printing speed, layer thickness, printing temperature and filling ratio on tensile properties were analyzed by the orthogonal test of four factors and three levels. Optimal tensile properties of the PEEK specimens were observed at a printing speed of 60 mm/s, layer thickness of 0.2 mm, temperature of 370 °C and filling ratio of 40%. Furthermore, the impact and bending tests were conducted under optimized conditions and the results demonstrated that the printed PEEK specimens have appropriate mechanical properties.

Effect of grinding and aging on subcritical crack growth of a Y-TZP ceramic.

PubMed

Amaral, Marina; Weitzel, Isabela Sandim Souza Leite; Silvestri, Tais; Guilardi, Luis Felipe; Pereira, Gabriel Kalil Rocha; Valandro, Luiz Felipe

2018-01-01

This study aimed to investigate slow crack growth (SCG) behavior of a zirconia ceramic after grinding and simulated aging with low-temperature degradation (LTD). Complementary analysis of hardness, surface topography, crystalline phase transformation, and roughness were also measured. Disc-shaped specimens (15 mm Ø × 1.2 mm thick, n = 42) of a full-contour Y-TZP ceramic (Zirlux FC, Amherst) were manufactured according to ISO:6872-2008, and then divided into: Ctrl - as-sintered condition; Ctrl LTD - as-sintered after aging in autoclave (134°C, 2 bar, 20 h); G - ground with coarse diamond bur (grit size 181 μm); G LTD - ground and aged. The SCG parameters were measured by a dynamic biaxial flexural test, which determines the tensile stress versus stress rate under four different rates: 100, 10, 1 and 0.1 MPa/s. LTD led to m-phase content increase, as well as grinding (m-phase content: Ctrl - 0%; G - 12.3%; G LTD - 59.9%; Ctrl LTD - 81%). Surface topography and roughness analyses showed that grinding created an irregular surface (increased roughness) and aging did not promote any relevant surface change. There was no statistical difference on surface hardness among different conditions. The control group presented the lowest strength values in all tested rates. Regarding SCG, ground conditions were less susceptible to SCG, delaying its occurrence. Aging (LTD) caused an increase in SCG susceptibility for the as-sintered condition (i.e. G < G LTD < Ctrl < Ctrl LTD).

Thermal Test on Target with Pressed Disks

DOE Office of Scientific and Technical Information (OSTI.GOV)

Woloshun, Keith Albert; Dale, Gregory E.; Olivas, Eric Richard

A thorough test of the thermal performance of a target for Mo 99 production using solid Mo 100 target to produce the Mo 99 via a gamma-n reaction has previously been conducted at Argonne National Laboratory (ANL). The results are reported in “Zero Degree Line Mo Target Thermal Test Results and Analysis,” LANL report Number LA-UR-15-23134 dated 3/27/15. This target was comprised of 25 disks 1 mm thick and 12 mm in diameter, separated by helium coolant gaps 0.5 mm wide. The test reported in the above referenced report was conducted with natural Mo disks all cut from commercial rod.more » The production plant will have Mo 100 disks pressed and sintered using a process being developed at Oak Ridge National Laboratory (ORNL). The structural integrity of press-and-sinter disks is of some concern. The test reported herein included 4 disks made by the ORNL process and placed in the high heat, and therefore high thermal stress, region of the target. The electron beam energy was 23 MeV for these tests. Beam spot size was 3.5 mm horizontal and 3 mm vertical, FWHM. The thermal stress test of pressed-and-sintered disks resulted in no mechanical failures. The induced thermal stresses were below yield stress for natural Mo, indicating that up to that stress state no inherent deficiencies in the mechanical properties of the fabricated disks were evident.« less

Evaluation of marginal/internal fit of chrome-cobalt crowns: Direct laser metal sintering versus computer-aided design and computer-aided manufacturing.

PubMed

Gunsoy, S; Ulusoy, M

2016-01-01

The purpose of this study was to evaluate the internal and marginal fit of chrome cobalt (Co-Cr) crowns were fabricated with laser sintering, computer-aided design (CAD) and computer-aided manufacturing, and conventional methods. Polyamide master and working models were designed and fabricated. The models were initially designed with a software application for three-dimensional (3D) CAD (Maya, Autodesk Inc.). All models were fabricated models were produced by a 3D printer (EOSINT P380 SLS, EOS). 128 1-unit Co-Cr fixed dental prostheses were fabricated with four different techniques: Conventional lost wax method, milled wax with lost-wax method (MWLW), direct laser metal sintering (DLMS), and milled Co-Cr (MCo-Cr). The cement film thickness of the marginal and internal gaps was measured by an observer using a stereomicroscope after taking digital photos in ×24. Best fit rates according to mean and standard deviations of all measurements was in DLMS both in premolar (65.84) and molar (58.38) models in μm. A significant difference was found DLMS and the rest of fabrication techniques (P < 0.05). No significant difference was found between MCo-CR and MWLW in all fabrication techniques both in premolar and molar models (P > 0.05). DMLS was best fitting fabrication techniques for single crown based on the results.The best fit was found in marginal; the larger gap was found in occlusal.All groups were within the clinically acceptable misfit range.

Diurnal Alterations of Refraction, Anterior Segment Biometrics, and Intraocular Pressure in Long-Time Dehydration due to Religious Fasting.

PubMed

Baser, Gonen; Cengiz, Hakan; Uyar, Murat; Seker Un, Emine

2016-01-01

To investigate the effects of dehydration due to fasting on diurnal changes of intraocular pressure, anterior segment biometrics, and refraction. The intraocular pressures, anterior segment biometrics (axial length: AL; Central corneal thickness: CCT; Lens thickness: LT; Anterior chamber depth: ACD), and refractive measurements of 30 eyes of 15 fasting healthy male volunteers were recorded at 8:00 in the morning and 17:00 in the evening in the Ramadan of 2013 and two months later. The results were compared and the statistical analyses were performed using the Rstudio software version 0.98.501. The variables were investigated using visual (histograms, probability plots) and analytical methods (Kolmogorov-Smirnov/Shapiro-Wilk test) to determine whether or not they were normally distributed. The refractive values remained stable in the fasting as well as in the control period (p = 0.384). The axial length measured slightly shorter in the fasting period (p = 0.001). The corneal thickness presented a diurnal variation, in which the cornea measured thinner in the evening. The difference between the fasting and control period was not statistically significant (p = 0.359). The major differences were observed in the anterior chamber depth and IOP. The ACD was shallower in the evening during the fasting period, where it was deeper in the control period. The diurnal IOP difference was greater in the fasting period than the control period. Both were statistically significant (p = 0.001). The LT remained unchanged in both periods. The major difference was shown in the anterior chamber shallowing in the evening hours and IOP. Our study contributes the hypothesis that the posterior segment of the eye is more responsible for the axial length alterations and normovolemia has a more dominant influence on diurnal IOP changes.

Elaboration and characterization of a free standing LiSICON membrane for aqueous lithium-air battery

NASA Astrophysics Data System (ADS)

Puech, Laurent; Cantau, Christophe; Vinatier, Philippe; Toussaint, Gwenaëlle; Stevens, Philippe

2012-09-01

In order to develop a LISICON separator for an aqueous lithium-air battery, a thin membrane was prepared by a tape-casting of a Li1.3Al0.3Ti1.7 (PO4)3-AlPO4 based slip followed by a sintering step. By optimizing the grain sizes, the slip composition and the sintering treatment, the mechanical properties were improved and the membrane was reduced to a thickness of down to 40 μm. As a result, the ionic resistance is relatively low, around 38 Ω for a 55 μm membrane of 1 cm2. One side of the membrane was coated with a lithium oxynitrured phosphorous (LiPON) thin film to prevent lithium metal attack. Lithium metal was electrochemically deposited on the LiPON surface from a saturated aqueous solution of LiOH. However, the ionic resistance of the LiPON film, around 67 Ω for a 1.2 μm film of 1 cm2, still causes an important ohmic loss contribution which limits the power performance of a lithium-air battery.

Synthesis of transparent Lu3Al5O12 ceramic by solid-state reaction method

NASA Astrophysics Data System (ADS)

Basyrova, L. R.; Maksimov, R. N.; Shitov, V. A.; Aleksandrov, E. O.

2017-09-01

Transparent polycrystalline Lu3Al5O12 (LuAG) ceramic was fabricated by solid-state reactive sintering a mixture of Lu2O3 nanoparticles synthesized by laser ablation and commercial Al2O3 powder. The obtained Lu2O3 nanoparticles exhibited a metastable monoclinic phase and were fully converted into a main cubic phase after calcination at 1100 °C for 1 h in air. The powders were mixed in ethanol with the addition of 0.5 wt% tetraethoxysilane (TEOS), dried in a rotary evaporator, and uniaxially pressed into pellet at 200 MPa. Transparent 2 mm thick LuAG ceramic sample with an average grain size of 9.6 µm and an optical transmittance of 30 % at a wavelength of 1080 nm was obtained after sintering at 1780 °C for 20 h under vacuum. The average volume of the scattering centers (380 ppm) in the obtained LuAG ceramic and their distribution along the sample depth was evaluated by the direct count method using an optical microscope.

Isolated Mesoporous Microstructures Prepared by Stress Localization-Induced Crack Manipulation.

PubMed

Wooh, Sanghyuk; Lee, Soojin; Lee, Yunchan; Ryu, Ji Ho; Lee, Won Bo; Yoon, Hyunsik; Char, Kookheon

2016-09-22

Cracks observed in brittle materials are mostly regarded as defects or failures. However, they can be a valuable tool when implemented in a controlled way. Here, we introduce a strategy to control the crack propagation of mesoporous micropatterns (prisms and pyramids), which leads to the isolation of well-defined microstructures. Mesoporous micropatterns were fabricated by the soft imprinting technique with wet TiO 2 nanoparticle (NP) pastes, followed by sintering to remove organic components. Since the volume of the paste significantly shrinks during the sintering step, stress is localized at the edge of micropatterns, in good agreement with finite element method simulations, creating well-defined cracks and their propagation. It was demonstrated that the degree of stress localization is determined by the thickness of residual layers, NP size, and heating rate. After controlled crack propagation and delamination of microparticles from the substrates, mesoporous microwires and microparticles were successfully produced and functionalized from the isolated mesoporous prisms and pyramids. The method proposed in this study for controlled crack manipulation and delamination opens a door for straightforward and economical fabrication of well-defined mesoporous microparticles.

Extrusion of metal oxide superconducting wire, tube or ribbon

DOEpatents

Dusek, Joseph T.

1993-10-05

A process for extruding a superconducting metal oxide composition YBa.sub.2 Cu.sub.3 O.sub.7-x provides a wire (tube or ribbon) having a cohesive mass and a degree of flexibility together with enhanced electrical properties. Wire diameters in the range of 6-85 mils have been produced with smaller wires on the order of 10 mils in diameter exhibiting enhanced flexibility for forming braided, or multistrand, configurations for greater current carrying capacity. The composition for extrusion contains a polymeric binder to provide a cohesive mass to bind the particles together during the extrusion process with the binder subsequently removed at lower temperatures during sintering. The composition for extrusion further includes a deflocculent, an organic plasticizer and a solvent which also are subsequently removed during sintering. Electrically conductive tubing with an inner diameter of 52 mil and an outer diameter of 87-355 mil has also been produced. Flat ribbons have been produced in the range of 10-125 mil thick by 100-500 mil wide. The superconducting wire, tube or ribbon may include an outer ceramic insulating sheath co-extruded with the wire, tubing or ribbon.

Extrusion of metal oxide superconducting wire, tube or ribbon

DOEpatents

Dusek, Joseph T.

1993-01-01

A process for extruding a superconducting metal oxide composition YBa.sub.2 Cu.sub.3 O.sub.7-x provides a wire (tube or ribbon) having a cohesive mass and a degree of flexibility together with enhanced electrical properties. Wire diameters in the range of 6-85 mils have been produced with smaller wires on the order of 10 mils in diameter exhibiting enhanced flexibility for forming braided, or multistrand, configurations for greater current carrying capacity. The composition for extrusion contains a polymeric binder to provide a cohesive mass to bind the particles together during the extrusion process with the binder subsequently removed at lower temperatures during sintering. The composition for extrusion further includes a deflocculent, an organic plasticizer and a solvent which also are subsequently removed during sintering. Electrically conductive tubing with an inner diameter of 52 mil and an outer diameter of 87-355 mil has also been produced. Flat ribbons have been produced in the range of 10-125 mil thick by 100-500 mil wide. The superconducting wire, tube or ribbon may include an outer ceramic insulating sheath co-extruded with the wire, tubing or ribbon.

Development of silicon nitride of improved toughness

NASA Technical Reports Server (NTRS)

Brennan, J. J.

1979-01-01

The application of reaction sintered Si2N4 energy absorbing surface layers to hot-pressed Si3N4 was investigated. The surface layer was formed by in-place nitridation of silicon powder. It was found that reaction sintered Si3N4 layers of 1 mm thickness, fabricated from either -100, +200, -200, or -325 mesh Si powder and nitrided in 96% N2/4% H2 so that approximately 20-25 vol % unnitrided Si remained in the layer, resulted in a sevenfold increase in ballistic impact resistance of a 0.64 cm thick hot-pressed SI3N4 substrate from RT 1370 C. Both NC-132 SI3N4, with MgO additive, and NCX-34 Si3N4, with Y2O3 additive, were evaluated as substrate material. The finer grain size -200 and -325 mesh nitrided Si layers were for their smoothness and relatively high density. It was found that nitriding in N2/H2 mixtures, rather than pure N2, resulted in a microstructure that did not substantially degrade the strength of the hot-pressed Si3N4 substrate. Thermal cycling tests on the RSSN/HPSN combinations from 200 C to 1370 C for 75 cycles in air did not degrade the impact resistance nor the interfacial bonding, although a large amount of internal silica formation occurred within the RSSN layer. Mach 0.8, 5 hr, hot gas erosion tests showed no surface recession of RSSN layers at 1200 C and slight surface recession at 1370 C.

Processing and characterization of laser sintered hybrid B4C/cBN reinforced Ti-based metal matrix composite

NASA Astrophysics Data System (ADS)

Gupta, Ankit; Hussain, Manowar; Misra, Saurav; Das, Alok Kumar; Mandal, Amitava

2018-06-01

The purpose of this study is to make a boron carbide (B4C) and cubic boron nitride (cBN) reinforced Ti6Al4V metal matrix composites (MMC's) by direct metal laser sintering (DMLS) technique using the continuous wave (CW) SPI fiber laser and to check the feasibility of the formation of three dimensional objects by this process. For this study, the process parameters like laser power density (3.528-5.172 W/cm2 (×104), scanning speed (3500-4500 mm/min), composition of the reinforced materials B4C (5-25% by volume) and cBN (3% by volume) were taken as input variables and hatching gap (0.2 mm), spot diameter (0.4 mm), layer thickness (0.4 mm) were taken as constant. It was analyzed that surface characteristic, density and the mechanical properties of sintered samples were greatly influenced by varying the input process parameters. Field emission scanning electron microscopy (FESEM), Energy dispersive X-ray spectroscopy (EDX) and X-Ray diffraction (XRD) were performed for microstructural analysis, elemental analysis, and recognition of intermetallic compounds respectively. Mechanical properties like micro-hardness & wear rate were examined by Vickers micro-hardness tester & pin on disc arrangement respectively. From hardness tests, it was observed that hardness property of the sintered specimens was increased as compared to the parent material. The XRD results show that there is a good affinity between Ti6Al4V-B4C-cBN to produce various intermetallic compounds which themselves enhance the mechanical properties of the samples. From FESEM analysis, we can conclude that there is a uniform distribution of reinforcements in the titanium alloy matrix. Furthermore, the coefficient of friction (COF) was characterized by the irregular pattern and it tends to decrease with an increase in the volume % of reinforcement. The results obtained in this work may be useful in preparing the MMC's with improved mechanical properties and overall characteristics.

A new measurement method of coatings thickness based on lock-in thermography

NASA Astrophysics Data System (ADS)

Zhang, Jin-Yu; Meng, Xiang-bin; Ma, Yong-chao

2016-05-01

Coatings have been widely used in modern industry and it plays an important role. Coatings thickness is directly related to the performance of the functional coatings, therefore, rapid and accurate coatings thickness inspection has great significance. Existing coatings thickness measurement method is difficult to achieve fast and accurate on-site non-destructive coatings inspection due to cost, accuracy, destruction during inspection and other reasons. This paper starts from the introduction of the principle of lock-in thermography, and then performs an in-depth study on the application of lock-in thermography in coatings inspection through numerical modeling and analysis. The numerical analysis helps explore the relationship between coatings thickness and phase, and the relationship lays the foundation for accurate calculation of coatings thickness. The author sets up a lock-in thermography inspection system and uses thermal barrier coatings specimens to conduct an experiment. The specimen coatings thickness is measured and calibrated to verify the quantitative inspection. Experiment results show that the lock-in thermography method can perform fast coatings inspection and the inspection accuracy is about 95%. Therefore, the method can meet the field testing requirements for engineering projects.

The relationship of periaortic fat thickness and cardiovascular risk factors in children with Turner syndrome.

PubMed

Akyürek, Nesibe; Atabek, Mehmet Emre; Eklioglu, Beray Selver; Alp, Hayrullah

2015-06-01

Children with Turner syndrome (TS) have a broad range of later health problems, including an increased risk of cardiovascular morbidity and mortality. The aim of this study was to evaluate the relationship between periaortic fat thickness (PAFT) and metabolic and cardiovascular profiles in children with TS. Twenty-nine TS and 29 healthy children and adolescents were enrolled in the study. Anthropometric measurements, pubertal staging, and blood pressure measurements were performed. Fasting serum glucose, insulin, and lipid profile were measured. Periaortic fat thickness was measured using an echocardiography method, which has not previously been applied in children with TS. No difference was found between TS and control subject (CS) in age, weight, waist/hip ratio, HDL cholesterol and LDL cholesterol levels. However, in TS subjects, total cholesterol (p = 0.045) was greater than that in controls. It was determined that 13.7 % (N: 4) of TS subjects had dyslipidemia. Mean fasting glucose, fasting insulin, QUICK-I, HOMA, and FGIR index were similar in TS and in CS, whereas 17.2 % (N: 5) of TS subjects had insulin resistance (IR) and 13.7 % (N: 4) had impaired glucose tolerance. Six subjects (20.6 %) were diagnosed as hypertensive. Periaortic fat thickness was significantly higher in the TS group (p < 0.001) (0.1694 ± 0.025 mm in the TS group and 0.1416 ± 0.014 mm in the CS group) In children with TS, PAFT was positively correlated with fasting insulin, body mass index, and diastolic blood pressure. Our results provide additional evidence for the presence of subclinical cardiovascular disease in TS. In addition to existing methods, we recommend the measurement of periaortic fat thickness in children with TS to reveal the presence of early atherosclerosis.

Development of a Novel Melt Spinning-Based Processing Route for Oxide Dispersion-Strengthened Steels

NASA Astrophysics Data System (ADS)

Hong, Zuliang; Morrison, Alasdair P. C.; Zhang, Hongtao; Roberts, Steve G.; Grant, Patrick S.

2018-02-01

Melt spinning of an Fe-5Y and Fe-1Y-1Ti (wt pct) alloy produced a relatively uniform spatial distribution of Y and Ti in solid solution and ribbons with consistent yield (> 60 pct by weight), fast processing time (< 10 seconds), good scalability (up to > 100 g feedstock material), and repeatability. Heat treatment in the presence of Fe2O3 as an oxygen source (Rhines pack method) at 973 K validated the potential of forming < 20 nm Y-rich oxides in the Fe-5Y ribbons. Pulverized Fe-1Y-1Y ribbons were consolidated to bulk using the field-assisted sintering technique (FAST) incorporating nano-sized Fe3O4 powder as the oxygen source. After FAST at 1273 K, 50 MPa, and 30 minutes, a comparatively high number density of sub-micron Y and/or Ti-rich oxides were developed. Further formation of fine-scale oxides took place during post-FAST annealing, resulting in an approximate 20 pct increase in hardness at temperatures below 573 K, but with a reduced hardening effect above 673 K due to a small fraction of persistent porosity and mechanically weak prior ribbon boundaries that were decorated with Ti-rich oxides.

Development of UO2/PuO2 dispersed in uranium matrix CERMET fuel system for fast reactors

NASA Astrophysics Data System (ADS)

Sinha, V. P.; Hegde, P. V.; Prasad, G. J.; Pal, S.; Mishra, G. P.

2012-08-01

CERMET fuel with either PuO2 or enriched UO2 dispersed in uranium metal matrix has a strong potential of becoming a fuel for the liquid metal cooled fast breeder reactors (LMR's). In fact it may act as a bridge between the advantages and disadvantages associated with the two extremes of fuel systems (i.e. ceramic fuel and metallic fuel) for fast reactors. At Bhabha Atomic Research Centre (BARC), R & D efforts are on to develop this CERMET fuel by powder metallurgy route. This paper describes the development of flow sheet for preparation of UO2 dispersed in uranium metal matrix pellets for three different compositions i.e. U-20 wt%UO2, U-25 wt%UO2 and U-30 wt%UO2. It was found that the sintered pellets were having excellent integrity and their linear mass was higher than that of carbide fuel pellets used in Fast Breeder Test Reactor programme (FBTR) in India. The pellets were characterized by X-ray diffraction (XRD) technique for phase analysis and lattice parameter determination. The optical microstructures were developed and reported for all the three different U-UO2 compositions.

Structure and short time degradation studies of sodium zirconium phosphate ceramics loaded with simulated fast breeder (FBR) waste

NASA Astrophysics Data System (ADS)

Ananthanarayanan, A.; Ambashta, R. D.; Sudarsan, V.; Ajithkumar, T.; Sen, D.; Mazumder, S.; Wattal, P. K.

2017-04-01

Sodium zirconium phosphate (NZP) ceramics have been prepared using conventional sintering and hot isostatic pressing (HIP) routes. The structure of NZP ceramics, prepared using the HIP route, has been compared with conventionally sintered NZP using a combination of X-ray diffraction (XRD) and (31P and 23Na) nuclear magnetic resonance (NMR) spectroscopy techniques. It is observed that NZP with no waste loading is aggressive toward the steel HIP-can during hot isostatic compaction and significant fraction of cations from the steel enter the ceramic material. Waste loaded NZP samples (10 wt% simulated FBR waste) show significantly low can-interaction and primary NZP phase is evident in this material. Upon exposure of can-interacted and waste loaded NZP to boiling water and steam, 31P NMR does not detect any major modifications in the network structure. However, the 23Na NMR spectra indicate migration of Na+ ions from the surface and possible re-crystallization. This is corroborated by Small-Angle Neutron Scattering (SANS) data and Scanning Electron Microscopy (SEM) measurements carried out on these samples.

Efficacy of a Solution-Based Approach for Making Sodalite Waste Forms for an Oxide Reduction Salt Utilized in the Reprocessing of Used Uranium Oxide Fuel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Riley, Brian J.; Pierce, David A.; Frank, Steven M.

2015-04-01

This paper describes various approaches for making sodalite with a LiCl-Li2O oxide reduction salt used to recover uranium from used oxide fuel. The approaches include sol-gel and solution-based synthesis processes. As-made products were mixed with 5 and 10 mass% of a Na2O-B2O3-SiO2 glass binder and these, along with product without a binder, were heated using either a cold-press-and-sinter method or hot uniaxial pressing. The results demonstrate the limitation of sodalite yield due to the fast intermediate reactions between Na+ and Cl- to form halite in solution and Li2O and SiO2 to form lithium silicates (e.g., Li2SiO3 or Li2Si2O5) in themore » calcined and sintered pellets. The results show that pellets can be made with high sodalite fractions (~92 mass%) and low porosities using a solution-based approach and this LiCl-Li2O salt.« less

Macroporous Silica with Thick Framework for Steam-Stable and High-Performance Poly(ethyleneimine)/Silica CO2 Adsorbent.

PubMed

Min, Kyungmin; Choi, Woosung; Choi, Minkee

2017-06-09

Poly(ethyleneimine) (PEI)/silica has been widely studied as a solid adsorbent for post-combustion CO 2 capture. In this work, a highly macroporous silica (MacS), synthesized by secondary sintering of fumed silica, is compared with various mesoporous silicas with different pore structures as a support for PEI. The silicas with large pore diameter and volume enabled high CO 2 adsorption kinetics and capacity, because pore occlusion by the supported PEI was minimized. The steam stability of the silica structures increased with the silica wall thickness owing to suppressed framework ripening. The silicas with low steam stability showed rapid leaching of PEI, which indicated that the PEI squeezed out of the collapsed silica pores leached more readily. Consequently, MacS that had an extra-large pore volume (1.80 cm 3  g -1 ) and pore diameter (56.0 nm), and a thick wall (>10 nm), showed the most promising CO 2 adsorption kinetics and capacity as well as steam stability. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Variability of the volume and thickness of sea ice in the Bay of Bothnia

NASA Astrophysics Data System (ADS)

Ronkainen, Iina; Lehtiranta, Jonni; Lensu, Mikko; Rinne, Eero; Hordoir, Robinson; Haapala, Jari

2017-04-01

Variability of the volume and thickness of sea ice in the Bay of Bothnia In our study, we want to quantify the variability of sea ice volume and thickness in the Bay of Bothnia and to introduce the drivers of the observed variability. There has been similar studies, but only for fast ice. We use various different data sets: in-situ ice thickness data, remote sensing data, model data and ice charts. In-situ data is from the regular monitoring stations in the coastal fast ice zone and from field campaigns. The remote sensing data is helicopter-borne and ship-borne electromagnetic data. The models we use are HELMI and NEMO-Nordic. We analyze the different data sets and compare them to each other to solve the inter-annual variability and to discuss the ratio of level and deformed ice.

Sintering behavior of U 80 at.%Zr powder compacts in a vacuum environment

NASA Astrophysics Data System (ADS)

Kim, Tae-Kyu; Lee, Chong-Tak; Sohn, Dong-Seong

2008-01-01

Sintering behavior of U-80 at.%Zr powder compacts in a temperature range from 1100 to 1500 °C in a vacuum of 1 × 10 -4 Pa was evaluated. The sintered density depended more on the sintering temperature than on the sintering time. The sintered specimens consisted of the δ-UZr 2 matrix with acicular α-Zr precipitates, but it still had un-reacted zirconium when the sintering temperature was 1100 °C. The uranium depletion near the surface of the specimens sintered at temperatures above 1300 °C was detected. Massive Zr(O) grains in the sintered specimen were found, and their formation was restrained when the cooling rate from the sintering temperature was increased.

[Translucency of dental zirconia ceramics sintered in conventional and microwave ovens].

PubMed

Yuemei, Jiang; Ying, Yang; Wenhui, Zhan; Guoxin, Hu; Qiuxia, Yang

2015-12-01

To evaluate the effect of microwave sintering on the translucency of zirconia and to compare these effect with those of conventional sintering. The relationship between the microstructure of specimens and translucency was investigated. A total of 10 disc-shaped specimens were fabricated from 2 commercial brands of zirconia, namely, Zenostar and Lava. Each group included 5 discs. Conventional sintering was performed according to the manufacturers' specifications. The maximum temperature for Zenostar was 1,490 °C, whereas that for Lava was 1,500 °C. The dwelling time was 2 h. The sintering temperature for microwave sintering was 1,420 °C, heating rate was 15 °C · min⁻¹, and dwelling time was 30 min. After sintering, the translucency parameter (TP) of the specimens were measured with ShadeEye NCC. The sintered density of the specimens was determined by Archimedes' method. The grain size and microstructure of the specimens were investigated by scanning electron microscopy. Density and translucency slightly increased by microwave sintering, but no significant difference was found between microwave and conventional sintering (P > 0.05). Small and uniform microstructure were obtained from microwave sintering. The mean TP of Lava was significantly higher than that of Zenostar (P < 0.001). The translucency of zirconia sintered by microwave sintering is similar to that of the zirconia sintered by conventional sintering.

[Effect of two-step sintering method on properties of zirconia ceramic].

PubMed

Huang, Hui; Wei, Bin; Zhang, Fu-Qiang; Sun, Jing; Gao, Lian

2008-04-01

To study the influence of two-step sintering method on the sintering property, mechanical properties and microstructure of zirconia ceramic. The nano-size zirconia powder were compacted and divided into two groups, one group for one-step sintering method, another group for two-step sintering method. All samples sintered at different temperature. The relative density, three-bend strength, HV hardness, fracture toughness and microstructure of sintered block were investigated. Two-step sintering method influenced the sintering property and mechanical properties of zirconia ceramic. The maximal relative density was 98.49% at 900 degrees C/1,450 degrees C sintering temperature. There were significant difference of mechanical properties between one-step sintering and two-step sintering, the three-bend strength and fracture toughness declined, hardness increased at two-step sintering. The three-bend strength, HV hardness and fracture toughness reached to maximum value as 1,059.08 MPa +/- 75.24 MPa, 1,377.00 MPa +/- 16.37 MPa and 5.92 MPa x m1/2 +/- 0.37 MPa x m1/2 at 900 degrees C/1,450 degrees C sintering temperature respectively. Microscopy revealed the relationship between the porosity and shapes of grains was correlated to strength of the zirconia ceramics. Despite of the two-step sintering method influences the properties of zirconia, it also is a promising esthetic all-ceramic dental material.

Ultrasonically spray coated silver layers from designed precursor inks for flexible electronics.

PubMed

Marchal, W; Vandevenne, G; D'Haen, J; Calmont de Andrade Almeida, A; Durand Sola, M A; van den Ham, E J; Drijkoningen, J; Elen, K; Deferme, W; Van Bael, M K; Hardy, A

2017-05-26

Integration of electronic circuit components onto flexible materials such as plastic foils, paper and textiles is a key challenge for the development of future smart applications. Therefore, conductive metal features need to be deposited on temperature sensitive substrates in a fast and straightforward way. The feasibility of these emerging (nano-) electronic technologies depends on the availability of well-designed deposition techniques and on novel functional metal inks. As ultrasonic spray coating (USSC) is one of the most promising techniques to meet the above requirements, innovative metal organic decomposition (MOD) inks are designed to deposit silver features on plastic foils. Various amine ligands were screened and their influence on the ink stability and the characteristics of the resulting metal depositions were evaluated to determine the optimal formulation. Eventually, silver layers with excellent performance in terms of conductivity (15% bulk silver conductivity), stability, morphology and adhesion could be obtained, while operating in a very low temperature window of 70 °C-120 °C. Moreover, the optimal deposition conditions were determined via an in-depth analysis of the ultrasonically sprayed silver layers. Applying these tailored MOD inks, the USSC technique enabled smooth, semi-transparent silver layers with a tunable thickness on large areas without time-consuming additional sintering steps after deposition. Therefore, this novel combination of nanoparticle-free Ag-inks and the USSC process holds promise for high throughput deposition of highly conductive silver features on heat sensitive substrates and even 3D objects.

Ultrasonically spray coated silver layers from designed precursor inks for flexible electronics

NASA Astrophysics Data System (ADS)

Marchal, W.; Vandevenne, G.; D'Haen, J.; Almeida, A. Calmont de Andrade; Durand Sola, M. A., Jr.; van den Ham, E. J.; Drijkoningen, J.; Elen, K.; Deferme, W.; Van Bael, M. K.; Hardy, A.

2017-05-01

Integration of electronic circuit components onto flexible materials such as plastic foils, paper and textiles is a key challenge for the development of future smart applications. Therefore, conductive metal features need to be deposited on temperature sensitive substrates in a fast and straightforward way. The feasibility of these emerging (nano-) electronic technologies depends on the availability of well-designed deposition techniques and on novel functional metal inks. As ultrasonic spray coating (USSC) is one of the most promising techniques to meet the above requirements, innovative metal organic decomposition (MOD) inks are designed to deposit silver features on plastic foils. Various amine ligands were screened and their influence on the ink stability and the characteristics of the resulting metal depositions were evaluated to determine the optimal formulation. Eventually, silver layers with excellent performance in terms of conductivity (15% bulk silver conductivity), stability, morphology and adhesion could be obtained, while operating in a very low temperature window of 70 °C-120 °C. Moreover, the optimal deposition conditions were determined via an in-depth analysis of the ultrasonically sprayed silver layers. Applying these tailored MOD inks, the USSC technique enabled smooth, semi-transparent silver layers with a tunable thickness on large areas without time-consuming additional sintering steps after deposition. Therefore, this novel combination of nanoparticle-free Ag-inks and the USSC process holds promise for high throughput deposition of highly conductive silver features on heat sensitive substrates and even 3D objects.

[Influence on microstructure of dental zirconia ceramics prepared by two-step sintering].

PubMed

Jian, Chao; Li, Ning; Wu, Zhikai; Teng, Jing; Yan, Jiazhen

2013-10-01

To investigate the microstructure of dental zirconia ceramics prepared by two-step sintering. Nanostructured zirconia powder was dry compacted, cold isostatic pressed, and pre-sintered. The pre-sintered discs were cut processed into samples. Conventional sintering, single-step sintering, and two-step sintering were carried out, and density and grain size of the samples were measured. Afterward, T1 and/or T2 of two-step sintering ranges were measured. Effects on microstructure of different routes, which consisted of two-step sintering and conventional sintering were discussed. The influence of T1 and/or T2 on density and grain size were analyzed as well. The range of T1 was between 1450 degrees C and 1550 degrees C, and the range of T2 was between 1250 degrees C and 1350 degrees C. Compared with conventional sintering, finer microstructure of higher density and smaller grain could be obtained by two-step sintering. Grain growth was dependent on T1, whereas density was not much related with T1. However, density was dependent on T2, and grain size was minimally influenced. Two-step sintering could ensure a sintering body with high density and small grain, which is good for optimizing the microstructure of dental zirconia ceramics.

Carbon-based nanostructured surfaces for enhanced phase-change cooling

NASA Astrophysics Data System (ADS)

Selvaraj Kousalya, Arun

To maintain acceptable device temperatures in the new generation of electronic devices under development for high-power applications, conventional liquid cooling schemes will likely be superseded by multi-phase cooling solutions to provide substantial enhancement to the cooling capability. The central theme of the current work is to investigate the two-phase thermal performance of carbon-based nanostructured coatings in passive and pumped liquid-vapor phase-change cooling schemes. Quantification of the critical parameters that influence thermal performance of the carbon nanostructured boiling surfaces presented herein will lead to improved understanding of the underlying evaporative and boiling mechanisms in such surfaces. A flow boiling experimental facility is developed to generate consistent and accurate heat transfer performance curves with degassed and deionized water as the working fluid. New means of boiling heat transfer enhancement by altering surface characteristics such as surface energy and wettability through light-surface interactions is explored in this work. In this regard, carbon nanotube (CNT) coatings are exposed to low-intensity irradiation emitted from a light emitting diode and the subcooled flow boiling performance is compared against a non-irradiated CNT-coated copper surface. A considerable reduction in surface superheat and enhancement in average heat transfer coefficient is observed. In another work involving CNTs, the thermal performance of CNT-integrated sintered wick structures is evaluated in a passively cooled vapor chamber. A physical vapor deposition process is used to coat the CNTs with varying thicknesses of copper to promote surface wetting with the working fluid, water. Thermal performance of the bare sintered copper powder sample and the copper-functionalized CNT-coated sintered copper powder wick samples is compared using an experimental facility that simulates the capillary fluid feeding conditions of a vapor chamber. Nanostructured samples having a thicker copper coating provided a considerable increase in dryout heat flux while maintaining lower surface superheat temperatures compared to a bare sintered powder sample; this enhancement is attributed primarily to the improved surface wettability. Dynamic contact angle measurements are conducted to quantitatively compare the surface wetting trends for varying copper coating thicknesses and confirm the increase in hydrophilicity with increasing coating thickness. The second and relatively new carbon nanostructured coating, carbon nanotubes decorated with graphitic nanopetals, are used as a template to manufacture boiling surfaces with heterogeneous wettability. Heat transfer surfaces with parallel alternating superhydrophobic and superhydrophilic stripes are fabricated by a combination of oxygen plasma treatment, Teflon coating and shadow masking. Such composite wetting surfaces exhibit enhanced flow-boiling performance compared to homogeneous wetting surfaces. Flow visualization studies elucidate the physical differences in nucleate boiling mechanisms between the different heterogeneous wetting surfaces. The third and the final carbon nanomaterial, graphene, is examined as an oxidation barrier coating for liquid and liquid-vapor phase-change cooling systems. Forced convection heat transfer experiments on bare and graphene-coated copper surfaces reveal nearly identical liquid-phase and two-phase thermal performance for the two surfaces. Surface analysis after thermal testing indicates significant oxide formation on the entire surface of the bare copper substrate; however, oxidation is observed only along the grain boundaries of the graphene-coated substrate. Results suggest that few-layer graphene can act as a protective layer even under vigorous flow boiling conditions, indicating a broad application space of few-layer graphene as an ultra-thin oxidation barrier coating.

Hydrothermal Cold Sintering

NASA Astrophysics Data System (ADS)

Kang, Xiaoyu

Solid state sintering transforms particle compact to a physically robust and dense polycrystalline monolith driven by reduction of surface energy and curvature. Since bulk diffusion is required for neck formation and pore elimination, sintering temperature about 2/3 of melting point is needed. It thus places limitations for materials synthesis and integration, and contributes to significant energy consumption in ceramic processing. Furthermore, since surface transport requires lower temperature than bulk processes, grain growth is often rapid and can be undesired for physical properties. For these reasons, several techniques have been developed including Liquid Phase Sintering (LPS), Hot Pressing (HP) and Field Assisted Sintering Technique (FAST), which introduce either viscous melt, external pressure or electric field to speed up densification rates at lower temperature. However, because of their inherent reliability on bulk diffusion, temperatures required are often too high for integrating polymers and non-noble metals. Reduction of sintering temperature below 400 °C would require a different densification mechanism that is based on surface transport with external forces to drive volume shrinkage. Densification method combining uniaxial pressure and solution under hydrothermal condition was first demonstrated by Kanahara's group at Kochi University in 1986 and was brought to our attention by the work of Kahari, etc, from University of Oulu on densification of Li2MoO 4 in 2015. This relatively new process showed promising ultra-low densification temperature below 300 °C, however little was known about its fundamental mechanism and scope of applications, which became the main focus of this dissertation. In this work, a uniaxial hydraulic press, a standard stainless steel 1/2 inch diameter die with heating band were utilized in densifying metal oxides. Applied pressure and sintering temperature were between 100 MPa and 700 MPa and from room temperature to 300 °C, respectively. Process variables were defined and effects of individual parameters were studied systematically through control variable method with Li2MoO4-water system. Crystalline structure, fractured surface morphology and chemical bonding information of the cold sintered pellets were studied with X-ray diffraction (XRD), field effect scanning electron microscopy (FE-SEM) and Raman spectroscopy, etc. Densification mechanism studies were conducted on ZnO. Through comparison experiments, it was found that the Zn2+ concentration in the solution is critical for densification, while dissolution of grains only serves as a means to the former. Through pressure dependent studies, a critical value was found, which correlated well with the hydrostatic pressure keeping liquid water from thermal expansion. These results confirmed establishment of hydrothermal condition that would be important for mass transport in densification. Densification rate variations with process time was estimated and similar time dependence to Kingery's model was found. The densification process was proposed to be consist of three consecutive stages, which are quick initial compaction, grain rearrangement and dissolution-reprecipitation events. Binary metal oxides with different acidities were subjected to cold sintering with various aqueous solutions in establishing a criteria for material selection. It was found that in general materials with high solubility at around neutral pH, high dissolution kinetics and similar free energy to their hydroxides or hydrates at ambient would be more likely for full densification with high phase purity. The anions in solution should also be wisely selected to avoid stable compound or complex formation. To extend the applicable material list for full densification, non-aqueous solvent of dimethyl sulfoxide (DMSO) based solution was studied for cold sintering. Both improvement of pellet density and suppression of hydroxide formation were achieved for MnO by using DMSO-HOAc solution. With this strategy, densification of other metal oxides with strong hydroxide formation may also be improved, for example oxides of alkaline earth and many transition metals. Finally, the author's previous work on Zn1-xMg xO thin films is included in Chapter 7.

Laser Cutting of Thin Nickel Bellows

NASA Technical Reports Server (NTRS)

Butler, C. L.

1986-01-01

Laser cutting technique produces narrow, precise, fast, and repeatable cuts in thin nickel-allow bellows material. Laser cutting operation uses intense focused beam to melt material and assisting gas to force melted material through part thickness, creating void. When part rotated or moved longitudinally, melting and material removal continuous and creates narrow, fast, precise, and repeatable cut. Technique used to produce cuts of specified depths less than material thickness. Avoids distortion, dents, and nicks produced in delicate materials during lathe trimming operations, which require high cutting-tool pressure and holding-fixture forces.

Improved Tubulars for Better Economics in Deep Gas Well Drilling using Microwave Technology

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dinesh Agrawal; Paul Gigl; Mahlon Dennis

2006-02-01

The objective of the research program has been to improve the rate-of-penetration in deep hostile environments by improving the life cycle and performance of coiled-tubing, an important component of a deep well drilling system for oil and gas exploration. The current process of the manufacture long tubular steel products consists of shaping the tube from flat strip, welding the seam and sections into lengths that can be miles long, and coiling onto reels. However, the welds, that are a weak point, now limit the performance of the coil tubing. This is not only from a toughness standpoint but also frommore » a corrosion standpoint. By utilizing the latest developments in the sintering of materials with microwave energy and powder metal extrusion technology for the manufacture of seamless coiled tubing and other tubular products, these problems can be eliminated. The project is therefore to develop a continuous microwave process to sinter continuously steel tubulars and butt-join them using microwave/induction process. The program started about three years ago and now we are in the middle of Phase II. In Phase I (which ended in February 2005) a feasibility study of the extrusion process of steel powder and continuously sinter the extruded tubing was conducted. The research program has been based on the development of microwave technology to process tubular specimens of powder metals, especially steels. The existing microwave systems at the Materials Research Laboratory (MRL) and Dennis Tool Company (DTC) were suitably modified to process tubular small specimens. The precursor powder metals were either extruded or cold isostatically pressed (CIP) to form tubular specimens. After conducting an extensive and systematic investigation of extrusion process for producing long tubes, it was determined that there were several difficulties in adopting extrusion process and it cannot be economically used for producing thousands of feet long green tubing. Therefore, in the Phase II the approach was modified to the microwave sintering combined with Cold Isostatic Press (CIP) and joining (by induction or microwave). This process can be developed into a semi-continuous sintering process if the CIP can produce parts fast enough to match the microwave sintering rates. This report summarizes the progress made to-date in this new approach. The final steel composition matching with the Quality tubing's QT-16Cr80 was short listed and used for all experiments. Bonding experiments using 4 different braze powders were conducted and the process optimized to obtain high degree of bonding strength. For fabrication of green tubulars a large CIP unit was acquired and tested. This equipment is located at the Dennis Tool facility in Houston. Microwave sintering experiments for continuous processing of the CIPed tubes are under progress in order to identify the optimum conditions. There have been some reproducibility problems and we are at present working to resolve these problems.« less

Recent Advances and Research Status in Energy Conservation of Iron Ore Sintering in China

NASA Astrophysics Data System (ADS)

Wang, Yao-Zu; Zhang, Jian-Liang; Liu, Zheng-Jian; Du, Cheng-Bo

2017-11-01

For the ferrous burden of blast furnaces in China, sinter generally accounts for more than 70% and the sintering process accounts for approximately 6-10% of the total energy consumption of the iron and steel enterprise. Therefore, saving energy during the sintering process is important to reduce the energy consumption in the iron and steel industry. This paper aims to illustrate recent advances and the research status of energy conservation of iron ore sintering in China. It focuses on the development and application of energy-saving technologies such as the composite agglomeration process, sintering with high-proportion flue gas recirculation sintering, recovery of sensible heat from the sinter cooling process, homogeneous deep-bed sintering technology, and comprehensive treatment technology of leakage of sintering. Moreover, some suggestions for the future development of energy-saving technologies are put forward.

Sintered tantalum carbide coatings on graphite substrates: Highly reliable protective coatings for bulk and epitaxial growth

DOE Office of Scientific and Technical Information (OSTI.GOV)

Nakamura, Daisuke; Suzumura, Akitoshi; Shigetoh, Keisuke

2015-02-23

Highly reliable low-cost protective coatings have been sought after for use in crucibles and susceptors for bulk and epitaxial film growth processes involving wide bandgap materials. Here, we propose a production technique for ultra-thick (50–200 μmt) tantalum carbide (TaC) protective coatings on graphite substrates, which consists of TaC slurry application and subsequent sintering processes, i.e., a wet ceramic process. Structural analysis of the sintered TaC layers indicated that they have a dense granular structure containing coarse grain with sizes of 10–50 μm. Furthermore, no cracks or pinholes penetrated through the layers, i.e., the TaC layers are highly reliable protective coatings. The analysismore » also indicated that no plastic deformation occurred during the production process, and the non-textured crystalline orientation of the TaC layers is the origin of their high reliability and durability. The TaC-coated graphite crucibles were tested in an aluminum nitride (AlN) sublimation growth process, which involves extremely corrosive conditions, and demonstrated their practical reliability and durability in the AlN growth process as a TaC-coated graphite. The application of the TaC-coated graphite materials to crucibles and susceptors for use in bulk AlN single crystal growth, bulk silicon carbide (SiC) single crystal growth, chemical vapor deposition of epitaxial SiC films, and metal-organic vapor phase epitaxy of group-III nitrides will lead to further improvements in crystal quality and reduced processing costs.« less

Effect of sintering process on the magnetic and mechanical properties of sintered Nd-Fe-B magnets

NASA Astrophysics Data System (ADS)

Hu, Z. H.; Qu, H. J.; Zhao, J. Q.; Yan, C. J.; Liu, X. M.

2014-11-01

The magnetic and mechanical properties of sintered Nd-Fe-B magnets prepared by different sintering processes were investigated. The results showed that the intrinsic coercivity and fracture toughness of sintered Nd-Fe-B magnets first increased, and then declined with increasing annealing temperature. The optimum magnetic properties and fracture toughness of sintered Nd-Fe-B magnets were obtained at the annealing temperature of 540 °C. Sintering temperature increasing from 1047 °C to 1071 °C had hardly effect on the magnetic properties of sintered Nd-Fe-B magnets. The variation of Vickers hardness and fracture toughness was not the same with increasing sintering temperature, and the effect of sintering temperature on the mechanical properties was complex and irregular. The reasons for the variation on magnetic and mechanical properties were analyzed, and we presumed that the effect of microstructure on the mechanical properties was more sensitive than the magnetic properties through analyzing the microstructure of sintered Nd-Fe-B magnets.

New materials through a variety of sintering methods

NASA Astrophysics Data System (ADS)

Jaworska, L.; Cyboroń, J.; Cygan, S.; Laszkiewicz-Łukasik, J.; Podsiadło, M.; Novak, P.; Holovenko, Y.

2018-03-01

New sintering techniques make it possible to obtain materials with special properties that are impossible to obtain by conventional sintering techniques. This issue is especially important for ceramic materials for application under extreme conditions. Following the tendency to limit critical materials in manufacturing processes, the use of W, Si, B, Co, Cr should be limited, also. One of the cheapest and widely available materials is aluminum oxide, which shows differences in phase composition, grain size, hardness, strain and fracture toughness of the same type of powder, sintered via various methods. In this paper the alumina was sintered using the conventional free sintering process, microwave sintering, Spark Plasma Sintering (SPS), high pressure-high temperature method (HP-HT) and High Pressure Spark Plasma Sintering (HP SPS). Phase composition analysis, by X-ray diffraction of the alumina materials sintered using various methods, was carried out. For the conventional sintering method, compacts are composed of α-Al2O3 and θ-Al2O3. For compacts sintered using SPS, microwave and HP-HT methods, χ-Al2O3 and γ-Al2O3 phases were additionally present. Mechanical and physical properties of the obtained materials were compared between the methods of sintering. On the basis of images from scanning electron microscope quantitative analysis was performed to determine the degree of grain growth of alumina after sintering.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Perriot, Romain; Uberuaga, Blas P.; Zamora, Richard J.

Diffusion in complex oxides is critical to ionic transport, radiation damage evolution, sintering, and aging. In complex oxides such as pyrochlores, anionic diffusion is dramatically affected by cation disorder. However, little is known about how disorder influences cation transport. Here, we report results from classical and accelerated molecular dynamics simulations of vacancy-mediated cation diffusion in Gd 2Ti 2O 7 pyrochlore, on the microsecond timescale. We find that diffusion is slow at low levels of disorder, while higher disorder allows for fast diffusion, which is then accompanied by antisite annihilation and reordering, and thus a slowing of cation transport. Cation diffusivitymore » is therefore not constant, but decreases as the material reorders. We also show that fast cation diffusion is triggered by the formation of a percolation network of antisites. This is in contrast with observations from other complex oxides and disordered media models, suggesting a fundamentally different relation between disorder and mass transport.« less

Sintering in Ceramics and Solid Oxide Fuel Cells

NASA Astrophysics Data System (ADS)

Hunt, Clay Dale

Nature's propensity to minimize energy, and the change in energy with respect to position, drives diffusion. Diffusion is a means by which mass transport resulting in the bonding of the particles of a powder compact can be achieved without melting. This phenomenon occurs in powdered materials near their melting temperature, and is referred to as "sintering". Because of the extreme melting temperature of some materials, sintering might be the only practical means of processing. The complexity and subtlety of sintering ceramics motivated the evaluation of empirical data and existing sintering models. This project examined polycrystalline cubic-zirconia sintering with and without transition-metal oxide additions that change sintering behavior. This study was undertaken to determine how sintering aids affect the driving force, and activation energy, the energy barrier that must be overcome in order for an atom or ion to diffuse, of the densification occurring during sintering. Examination of commercially-available cubic-zirconia powder sintering behavior was undertaken with dilatometry, which allows monitoring of the length change a material undergoes as it sinters, and with scanning electron microscopy, which facilitates the study of sintered-sample microstructure. MATLAB algorithms quantifying sintering results were developed. Results from this work include proposed definitions of a 26-year-old undefined function of density factor in a well-accepted mathematical model of sintering. These findings suggest activation energy is not changing with density, as is suggested by recent published results. The first numerical integration of the studied sintering model has been performed. With these tools, a measure of the activation energy of densification of cubic-zirconia with and without the addition of cobalt-oxide as a sintering aid has been performed. The resulting MATLAB algorithms can be used in future sintering studies. It is concluded that sintering enhancement achieved with cobalt-oxide addition comes from reduction in activation energy of densification of cubic-zirconia. Further, it is suggested that the activation energy of densification does not change with material density. This conclusion is supported by the sensitivity of the numerical integration of the aforementioned sintering model to changes in activation energy.

Rare earth elements in sinters from the geothermal waters (hot springs) on the Tibetan Plateau, China

NASA Astrophysics Data System (ADS)

Feng, Jin-Liang; Zhao, Zhen-Hong; Chen, Feng; Hu, Hai-Ping

2014-10-01

The mineralogical and geochemical composition of sinters from the geothermal areas on the Tibetan Plateau was determined. They occur as siliceous, salty and calcareous sinters but biogenic siliceous sinters were also found. The analyses indicate that there are no distinct inter -element relationships between individual rare earth elements (REEs) and other elements. Formed from the same geothermal water, the mineralogical and chemical composition of the sinters is influenced by their genesis and formation conditions. The REE distributions depend on the origin of the sinters. Fe-Mn phases in sinters tend to scavenge more REEs from geothermal water. Neither the REE fractionation nor the Ce anomaly seems to be associated with Fe-Mn phases in the sinters. The fourth tetrads of some sinters display weak W-type (concave) effects. In contrast, the third tetrads present large effects in some sinters due to positive Gd anomalies. The origin of the positive Eu anomalies in some sinters seems to be caused by preferential dissolution of feldspars during water-rock interaction. The complexing ligands in geothermal water may contribute significantly to the fractionation of REEs in sinters. The dominant CO32- and HCO3- complexing in geothermal water favors enrichment of heavy REEs in calcareous sinters.

Double-HE-Layer Detonation-Confinement Sandwich Tests: The Effect of Slow-Layer Density

NASA Astrophysics Data System (ADS)

Hill, Larry

2013-06-01

Over a period of several years, we have explored the phenomenon in which slabs of high explosives (HEs) with differing detonation speeds are joined along one of their faces. Both are initiated (usually by a line-wave generator) at one edge. If there were no coupling between the layers, the detonation in the fast HE would outrun that in the slow HE. In reality, the detonation in the fast HE transmits an oblique shock into the slow HE, the phase speed of which is equal to the speed of the fast HE. This has one of two effects depending on the particulars. First, the oblique shock transmitted to the slow HE can pre-shock and deaden it, extinguishing the detonation in the slow HE. Second, the oblique shock can transversely initiate the slow layer, pulling its detonation along at the fast HE speed. When the second occurs, it does so at the ``penalty'' of a nominally dead layer, which forms in the slow HE adjacent to the material interface. We present the results of tests in which the fast layer was 3-mm-thick PBX 9501 (95 wt% HMX), and the slow layer was 8-mm-thick PBX 9502 (95 wt% TATB). The purpose was to observe the effect of slow layer density on the ``dead'' layer thickness. Very little effect was observed across the nominal PBX 9502 density range, 1.885-1.895 g/cc.

Processing, Microstructure, and Properties of Engineered Diboride Structures

NASA Astrophysics Data System (ADS)

Wittmaier, Connor Charles

The mechanical properties and processing parameters of boride ceramics in foam and laminate architectures were evaluated. The ceramic reticulated foam was produced through a polymer substrate replication technique and the hardness and compressive strength were tested. The laminate structure was tested to evaluate the flexure strength and work of fracture as a function of temperature. The foam architecture was produced using a TiB2 slurry coating on a polyurethane reticulated foam preform. Foams sintered to 2150°C displayed an average grain size of 8.9 +/- 7.3 microm, and a hardness of 17.3 +/- 2.4 GPa. Crush testing foams were sintered at 1975°C, and displayed a specific strength of 208 +/- 63 kPa with an overall porosity of 97%. For these specimens, it is likely that microcracking lowered the hardness, but the overall strength was controlled by the bulk density. The laminate structures were fabricated using alternating layers of ZrB 2 and C-10 vol% ZrB2. The structures were fabricated through the shaping of ceramic loaded thermoplastic polymers that underwent burnout and hot pressing cycles. These specimens had strong phase ZrB2 layers that were about 150 mum thick alternating with weak phase layers that were about 20 mum thick. Specimens exhibited a maximum flexure strength of 311 +/- 10 MPa at 1600°C, and an increased work of fracture compared to conventional ZrB2 ceramics. The maximum fraction of inelastic work of fracture occurred at room temperature, and decreased as temperature increased. This was reflected in the length of the crack path through the specimen. Deflected cracks travelled through the center of the C-ZrB2 layers in the material in Mode II fracture.

Preparation and characterization of ceramic sensors for use at elevated temperatures

NASA Astrophysics Data System (ADS)

You, Tao

Ceramic ITO strain sensors were prepared by reactive sputtering in various nitrogen/oxygen/argon partial pressures. The thickness of the active ITO strain elements played a significant role in the high temperature stability and piezoresistive properties, specifically, these results indicated that both gauge factor and drift rate were affected by the thickness of ITO films comprising the active strain elements. The influence of nitrogen in the reactive sputtered ITO films on the microstructure and the high temperature piezoresistive properties was also investigated. Scanning electron microscopy (SEM) revealed a partially sintered microstructure consisting of a contiguous network of sub-micron ITO particles with well-defined necks and isolated nanoporosity. Sintering and densification of the ITO particles containing these nitrogen rich grain boundaries was retarded and a contiguous network of nano-sized ITO particles was established. Aluminum doped indium tin oxide thin film exhibited an enhanced high temperature stability compared with undoped ITO thin film. The effect of aluminum doped ITO was investigated under various preparation and testing environments. Electron spectroscopy for chemical analysis (ESCA) studies indicated that interfacial reactions between ITO and aluminum increased the stability of ITO at elevated temperatures. These binding energies of indium-indium are significantly higher than those associated with stoichiometric indium oxide. A robust ceramic temperature sensor was fabricated by two different ITO elements, each with substantially different charge carrier concentrations. Thermal cycling of ITO thin films in a varied of partial oxygen pressures conditions showed that temperature coefficient of resistance (TCR) was nearly independent of oxygen partial pressure. A thermoelectric power of 6.0muV/°C and a linear voltage-temperature response were measured for an ITO thin film ceramic thermocouple over the temperature range 25--1250°C.

Thermal Conductivity and Elastic Modulus Evolution of Thermal Barrier Coatings under High Heat Flux Conditions

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Miller, Robert A.

1999-01-01

Laser high heat flux test approaches have been established to obtain critical properties of ceramic thermal barrier coatings (TBCs) under near-realistic temperature and thermal gradients that may he encountered in advanced engine systems. Thermal conductivity change kinetics of a thin ceramic coating were continuously monitored in real time at various test temperatures. A significant thermal conductivity increase was observed during the laser simulated engine heat flux tests. For a 0.25 mm thick ZrO2-8%Y2O3 coating system, the overall thermal conductivity increased from the initial value of 1.0 W/m-K to 1. 15 W/m-K, 1. 19 W/m-K and 1.5 W/m-K after 30 hour testing at surface temperatures of 990C, 1100C, and 1320C. respectively. Hardness and modulus gradients across a 1.5 mm thick TBC system were also determined as a function of laser testing time using the laser sintering/creep and micro-indentation techniques. The coating Knoop hardness values increased from the initial hardness value of 4 GPa to 5 GPa near the ceramic/bond coat interface, and to 7.5 GPa at the ceramic coating surface after 120 hour testing. The ceramic surface modulus increased from an initial value of about 70 GPa to a final value of 125 GPa. The increase in thermal conductivity and the evolution of significant hardness and modulus gradients in the TBC systems are attributed to sintering-induced micro-porosity gradients under the laser-imposed high thermal gradient conditions. The test techniques provide a viable means for obtaining coating data for use in design, development, stress modeling, and life prediction for various thermal barrier coating applications.

Mechanical properties of ZrB2- and HfB2-based ultra-high temperature ceramics fabricated by spark plasma sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zapata-Solvas, E.; Jayaseelan, D.; Lin, Hua-Tay

2013-01-01

Flexural strengths at room temperature, at 1400 C in air and at room temperature after 1 h oxidation at 1400 C were determined for ZrB2- and HfB2-based ultra-high temperature ceramics (UHTCs). Defects caused by electrical discharge machining (EDM) lowered measured strengths significantly and were used to calculate fracture toughness via a fracture mechanics approach. ZrB2 with 20 vol.% SiC had room temperature strength of 700 90 MPa, fracture toughness of 6.4 0.6 MPa, Vickers hardness at 9.8 N load of 21.1 0.6 GPa, 1400 C strength of 400 30 MPa and room temperature strength after 1 h oxidation at 1400more » C of 678 15 MPa with an oxide layer thickness of 45 5 m. HfB2 with 20 vol.% SiC showed room temperature strength of 620 50 MPa, fracture toughness of 5.0 0.4 MPa, Vickers hardness at 9.8 N load of 27.0 0.6 GPa, 1400 C strength of 590 150 MPa and room temperature strength after 1 h oxidation at 1400 C of 660 25 MPa with an oxide layer thickness of 12 1 m. 2 wt.% La2O3 addition to UHTCs slightly reduced mechanical performance while increasing tolerance to property degradation after oxidation and effectively aided internal stress relaxation during spark plasma sintering (SPS) cooling, as quantified by X-ray diffraction (XRD). Slow crack growth was suggested as the failure mechanism at high temperatures as a consequence of sharp cracks formation during oxidation.« less

Flash sintering of stoichiometric and hyper-stoichiometric urania

DOE PAGES

Valdez, James Anthony; Byler, Darrin David; Kardoulaki, Erofili; ...

2018-03-29

Flash sintering (FS), a novel fabrication technique belonging to the family of field assisted sintering (FAS) techniques, has been utilized in this study to fabricate uranium dioxide (UO 2) pellets. Stoichiometric (UO 2.00) and hyper-stoichiometric (UO 2.16) pellets were flash sintered at 600 °C within a few (2–3) minutes. This is in sharp contrast to conventional sintering where temperatures hundreds of degrees higher are necessary and the sintering time extends to hours. Relating this in terms of the homologous temperature ratio (T H) for both conditions shows that in the case of flash sintering at 600 °C, T H =more » 0.3 versus T H = 0.6 for conventional sintering at 1600 °C. The highest density achieved for a UO 2.00 pellet was 81% theoretical density (TD) when flash sintered at 600 °C for 184 s at a field of 188 V/cm and a current density of 442 mA/mm 2. For the UO 2.16 pellet, the highest achieved density was 92% TD when flash sintered at 600 °C for 140 s at a field of 188 V/cm and a current density of 632 mA/mm 2. X-ray diffraction (XRD) characterization of the sintered pellets showed the final sintered material to be single cubic fluorite phase. Scanning electron microscopy (SEM) of longitudinal sections revealed non-uniform microstructures with regions of high density where the grain size ranged from 1 to 15 μm. Comparisons between conventionally and flash sintered pellets that achieved equivalent shrinkage strains were also conducted. Lastly, in all cases, the flash sintered pellets achieved similar densification to the conventionally sintered pellets at much lower furnace temperatures and shorter times.« less

Flash sintering of stoichiometric and hyper-stoichiometric urania

DOE Office of Scientific and Technical Information (OSTI.GOV)

Valdez, James Anthony; Byler, Darrin David; Kardoulaki, Erofili

Flash sintering (FS), a novel fabrication technique belonging to the family of field assisted sintering (FAS) techniques, has been utilized in this study to fabricate uranium dioxide (UO 2) pellets. Stoichiometric (UO 2.00) and hyper-stoichiometric (UO 2.16) pellets were flash sintered at 600 °C within a few (2–3) minutes. This is in sharp contrast to conventional sintering where temperatures hundreds of degrees higher are necessary and the sintering time extends to hours. Relating this in terms of the homologous temperature ratio (T H) for both conditions shows that in the case of flash sintering at 600 °C, T H =more » 0.3 versus T H = 0.6 for conventional sintering at 1600 °C. The highest density achieved for a UO 2.00 pellet was 81% theoretical density (TD) when flash sintered at 600 °C for 184 s at a field of 188 V/cm and a current density of 442 mA/mm 2. For the UO 2.16 pellet, the highest achieved density was 92% TD when flash sintered at 600 °C for 140 s at a field of 188 V/cm and a current density of 632 mA/mm 2. X-ray diffraction (XRD) characterization of the sintered pellets showed the final sintered material to be single cubic fluorite phase. Scanning electron microscopy (SEM) of longitudinal sections revealed non-uniform microstructures with regions of high density where the grain size ranged from 1 to 15 μm. Comparisons between conventionally and flash sintered pellets that achieved equivalent shrinkage strains were also conducted. Lastly, in all cases, the flash sintered pellets achieved similar densification to the conventionally sintered pellets at much lower furnace temperatures and shorter times.« less

Flash sintering of stoichiometric and hyper-stoichiometric urania

NASA Astrophysics Data System (ADS)

Valdez, J. A.; Byler, D. D.; Kardoulaki, E.; Francis, J. S. C.; McClellan, K. J.

2018-07-01

Flash sintering (FS), a novel fabrication technique belonging to the family of field assisted sintering (FAS) techniques, has been utilized in this study to fabricate uranium dioxide (UO2) pellets. Stoichiometric (UO2.00) and hyper-stoichiometric (UO2.16) pellets were flash sintered at 600 °C within a few (2-3) minutes. This is in sharp contrast to conventional sintering where temperatures hundreds of degrees higher are necessary and the sintering time extends to hours. Relating this in terms of the homologous temperature ratio (TH) for both conditions shows that in the case of flash sintering at 600 °C, TH = 0.3 versus TH = 0.6 for conventional sintering at 1600 °C. The highest density achieved for a UO2.00 pellet was 81% theoretical density (TD) when flash sintered at 600 °C for 185 s at a field of 188 V/cm and a current density of 442 mA/mm2. For the UO2.16 pellet, the highest achieved density was 91% TD when flash sintered at 600 °C for 123 s at a field of 188 V/cm and a current density of 632 mA/mm2. X-ray diffraction (XRD) characterization of the sintered pellets showed the final sintered material to be single cubic fluorite phase. Scanning electron microscopy (SEM) of longitudinal sections revealed non-uniform microstructures with regions of high density where the grain size ranged from 1 to 15 μm. Comparisons between conventionally and flash sintered pellets that achieved equivalent shrinkage strains were also conducted. In all cases, the flash sintered pellets achieved similar densification to the conventionally sintered pellets at much lower furnace temperatures and shorter times.

Parallel Large-Scale Molecular Dynamics Simulation Opens New Perspective to Clarify the Effect of a Porous Structure on the Sintering Process of Ni/YSZ Multiparticles.

PubMed

Xu, Jingxiang; Higuchi, Yuji; Ozawa, Nobuki; Sato, Kazuhisa; Hashida, Toshiyuki; Kubo, Momoji

2017-09-20

Ni sintering in the Ni/YSZ porous anode of a solid oxide fuel cell changes the porous structure, leading to degradation. Preventing sintering and degradation during operation is a great challenge. Usually, a sintering molecular dynamics (MD) simulation model consisting of two particles on a substrate is used; however, the model cannot reflect the porous structure effect on sintering. In our previous study, a multi-nanoparticle sintering modeling method with tens of thousands of atoms revealed the effect of the particle framework and porosity on sintering. However, the method cannot reveal the effect of the particle size on sintering and the effect of sintering on the change in the porous structure. In the present study, we report a strategy to reveal them in the porous structure by using our multi-nanoparticle modeling method and a parallel large-scale multimillion-atom MD simulator. We used this method to investigate the effect of YSZ particle size and tortuosity on sintering and degradation in the Ni/YSZ anodes. Our parallel large-scale MD simulation showed that the sintering degree decreased as the YSZ particle size decreased. The gas fuel diffusion path, which reflects the overpotential, was blocked by pore coalescence during sintering. The degradation of gas diffusion performance increased as the YSZ particle size increased. Furthermore, the gas diffusion performance was quantified by a tortuosity parameter and an optimal YSZ particle size, which is equal to that of Ni, was found for good diffusion after sintering. These findings cannot be obtained by previous MD sintering studies with tens of thousands of atoms. The present parallel large-scale multimillion-atom MD simulation makes it possible to clarify the effects of the particle size and tortuosity on sintering and degradation.

Preparation of Ti3Al intermetallic compound by spark plasma sintering

NASA Astrophysics Data System (ADS)

Ito, Tsutomu; Fukui, Takahiro

2018-04-01

Sintered compacts of single phase Ti3Al intermetallic compound, which have excellent potential as refractory materials, were prepared by spark plasma sintering (SPS). A raw powder of Ti3Al intermetallic compound with an average powder diameter of 176 ± 56 μm was used in this study; this large powder diameter is disadvantageous for sintering because of the small surface area. The samples were prepared at sintering temperatures (Ts) of 1088, 1203, and 1323 K, sintering stresses (σs) of 16, 32, and 48 MPa, and a sintering time (ts) of 10 min. The calculated relative densities based on the apparent density of Ti3Al provided by the supplier were approximately 100% under all sintering conditions. From the experimental results, it was evident that SPS is an effective technique for dense sintering of Ti3Al intermetallic compounds in a short time interval. In this report, the sintering characteristics of Ti3Al intermetallic compacts are briefly discussed and compared with those of pure titanium compacts.

Mineral Phases and Release Behaviors of As in the Process of Sintering Residues Containing As at High Temperature

PubMed Central

Wang, Xingrun; Zhang, Fengsong; Nong, Zexi

2014-01-01

To investigate the effect of sintering temperature and sintering time on arsenic volatility and arsenic leaching in the sinter, we carried out experimental works and studied the structural changes of mineral phases and microstructure observation of the sinter at different sintering temperatures. Raw materials were shaped under the pressure of 10 MPa and sintered at 1000~1350°C for 45 min with air flow rate of 2000 mL/min. The results showed that different sintering temperatures and different sintering times had little impact on the volatilization of arsenic, and the arsenic fixed rate remained above 90%; however, both factors greatly influenced the leaching concentration of arsenic. Considering the product's environmental safety, the best sintering temperature was 1200°C and the best sintering time was 45 min. When sintering temperature was lower than 1000°C, FeAsS was oxidized into calcium, aluminum, and iron arsenide, mainly Ca3(AsO4)2 and AlAsO4, and the arsenic leaching was high. When it increased to 1200°C, arsenic was surrounded by a glass matrix and became chemically bonded inside the matrix, which lead to significantly lower arsenic leaching. PMID:24723798

Development of radon sources with a high stability and a wide range

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukutsu, K.; Yamada, Y.

A solid {sup 222}Rn (radon) source using a fibrous and porous SiC ceramic disk was developed. The emission rate of radon emanated from the disk depended on the content of {sup 226}Ra and the sintering temperature. A {sup 226}Ra sulfate ({sup 226}RaSO{sub 4}) solution was dropped on a fibrous SiC ceramic disk (33 mmφ) of 1 mm in thickness, and sintered at 400 °C. The radon concentration from a disk containing {sup 226}Ra of 1.85 MBq was measured to be 38 kBq m{sup −3} at a carrier airflow rate of 0.5 L min{sup −1}. By adjusting the {sup 226}Ra contentmore » or the sweep airflow rate, the radon concentrations were easily controlled over a wide range of over three orders of magnitude. The concentration was very stable for a long term. The compactness of the source disk made is easy for handling the source container and the shielding of gamma radiation from {sup 226}Ra and its decay products. Such advantages in a radon generation system are desirable for experiments of high-level, large-scale radon exposure.« less

Evolution de films de cuivre sur un substrat de cordiérite au cours de traitements thermiques

NASA Astrophysics Data System (ADS)

Guille, Jean-Louis; Gondolf, Marc

1993-04-01

Copper films were applied on low sintering temperature cordierite substrates either by sputtering or screen printing. Their behaviour during thermal treatments was studied as a function of various parameters : deposition technique, thickness, firing atmosphere, physical state of the substrate (green or sintered). Films were most often broken during the treatment. In the case of screen printed films the effects of an oxydation-reduction cycle of copper are pointed out. Des films de cuivre ont été déposés sur un substrat de cordiérite à basse température de frittage par deux techniques, pulvérisation cathodique et sérigraphie. On étudie leur comportement au cours de traitements thermiques en fonction de différents paramètres : technique de déposition, épaisseur, atmosphère de traitement, état physique du substrat (cru ou fritté). On constate le plus souvent une fragmentation du film. Dans le cas des films sérigraphiés on met en évidence les effets dus à l'oxydation et à la réduction du cuivre.

Corrosion Behavior and Strength of Dissimilar Bonding Material between Ti and Mg Alloys Fabricated by Spark Plasma Sintering

PubMed Central

Pripanapong, Patchara; Kariya, Shota; Luangvaranunt, Tachai; Umeda, Junko; Tsutsumi, Seiichiro; Takahashi, Makoto; Kondoh, Katsuyoshi

2016-01-01

Ti and solution treated Mg alloys such as AZ31B (ST), AZ61 (ST), AZ80 (ST) and AZ91 (ST) were successfully bonded at 475 °C by spark plasma sintering, which is a promising new method in welding field. The formation of Ti3Al intermetallic compound was found to be an important factor in controlling the bonding strength and galvanic corrosion resistance of dissimilar materials. The maximum bonding strength and bonding efficiency at 193 MPa and 96% were obtained from Ti/AZ91 (ST), in which a thick and uniform nano-level Ti3Al layer was observed. This sample also shows the highest galvanic corrosion resistance with a measured galvanic width and depth of 281 and 19 µm, respectively. The corrosion resistance of the matrix on Mg alloy side was controlled by its Al content. AZ91 (ST) exhibited the highest corrosion resistance considered from its corrode surface after corrosion test in Kroll’s etchant. The effect of Al content in Mg alloy on bonding strength and corrosion behavior of Ti/Mg alloy (ST) dissimilar materials is discussed in this work. PMID:28773788

Influence of CeO2 addition on the preparation of foamed glass-ceramics from high-titanium blast furnace slag

NASA Astrophysics Data System (ADS)

Zhou, Hong-ling; Feng, Ke-qin; Chen, Chang-hong; Yan, Zi-di

2018-06-01

Foamed glass-ceramics doped with cerium oxide (CeO2) were successfully prepared from high-titanium blast furnace slag by one-step sintering. The influence of CeO2 addition (1.5wt%-3.5wt%) on the crystalline phases, microstructure, and properties of foamed glass-ceramics was studied. Results show that CeO2 improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one. XRD analysis indicates the presence of Ca(Mg, Fe)Si2O6 and Ca(Ti, Mg, Al)(Si, Al)2O6 in all sintered samples. Added with CeO2, TiCeO4 precipitates, and crystallinity increases, leading to increased thickness of pore walls and uniform pores. The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO2. In particular, the sample added with a suitable amount of CeO2 (2.5wt%) exhibits bulk density that is similar to and compressive strength (14.9 MPa) that is more than twice of foamed glass-ceramics without CeO2.

Preparation and Characterization of Anode-Supported YSZ Thin Film Electrolyte by Co-Tape Casting and Co-Sintering Process

NASA Astrophysics Data System (ADS)

Liu, Q. L.; Fu, C. J.; Chan, S. H.; Pasciak, G.

2011-06-01

In this study, a co-tape casting and co-sintering process has been developed to prepare yttria-stabilized zirconia (YSZ) electrolyte films supported on Ni-YSZ anode substrates in order to substantially reduce the fabrication cost of solid oxide fuel cells (SOFC). Through proper control of the process, the anode/electrolyte bilayer structures with a size of 7.8cm × 7.8cm were achieved with good flatness. Scanning electron microscopy (SEM) observation indicated that the YSZ electrolyte film was about 16 μm in thickness, highly dense, crack free and well-bonded to the anode support. The electrochemical properties of the prepared anode-supported electrolyte film was evaluated in a button cell mode incorporating a (LaSr)MnO3-YSZ composite cathode. With humidified hydrogen as the fuel and stationary air as the oxidant, the cell demonstrated an open-circuit voltage of 1.081 V and a maximum power density of 1.01 W/cm2 at 800°C. The obtained results represent the important progress in the development of anode-supported intermediate temperature SOFC with reduced fabrication cost.

INVESTIGATION OF THE EFFECTS OF PROCESSING VARIABLES AND FABRICATION TECHNIQUES UPON THE PROPERTIES OF INTERMETALLIC COMPOUNDS. Technical Report No. 190-229. Progress Report No. 2 for July 1, 1960 to September 30, 1960

DOE Office of Scientific and Technical Information (OSTI.GOV)

Truesdale, R.; Lympany, B.; Klein, J.

1960-10-15

The optimum sintering temperatures of cold pressed NbBe/sub 12/, Nb/sub 2/Be/sub 17/ and Nb/sub 2/Be/sub 19/ were established as 3090. and 3090 deg F, respectively. The compound Nb/sub 2/Be/sub 17/ sintered to 97.5% of theoretical density. Sound 4-in.-square by l-in.-thick blocks of Nb/sub 2/Be/sub 17/ were fabricated and cut into transverse-rupture bars. A modulus of rupture strength of over 46.000 psi was measured at 2500 deg F. In the metallurgical phase. tungsten was found to be a suitable jacket material for the mechanical working of the niobium beryllides at 3000 deg F if protected from oxidation. Cera-kote. a refractory coating,more » sufficiently reduced tungsten oxidation for periods up to 1- hr. Two Nb/sub 2/Be/sub 17/ specimens were upset at 2750 deg F and 7500 psi. An upset of 48% was achieved. causing a slight increase in density and grain size. (auth)« less

B{sub 4}C-SiC reaction-sintered coatings on graphite plasma facing components

DOE Office of Scientific and Technical Information (OSTI.GOV)

Valentine, P.G.; Trester, P.W.; Winter, J.

1994-05-01

Boron carbide plus silicon carbide (B{sub 4}C-SiC) reaction-sintered coatings for use on graphite plasma-facing components were developed. Such coatings are of interest in TEXTOR tokamak limiter-plasma interactions as a means of reducing carbon erosion, of providing a preferred release of boron for oxygen gettering, and of investigating silicon`s effect on radiative edge phenomena. Specimens evaluated had (a) either Ringsdorfwerke EK 98 graphite or Le Carbon Lorraine felt-type AEROLOR A05 CFC substrates; (b) multiphase coatings, comprised of B{sub 4}C, Sic, and graphite; (c) nominal coating compositions of 69 wt.-% B{sub 4}C + 31 wt.-% SiC; and (d) nominal coating thicknesses betweenmore » 250 and 775 {mu}m. Coated coupons were evaluated by high heat flux experiments in the JUDITH (electron beam) test facility at KFA. Simulated disruptions, with energy densities up to 10 MJm{sup {minus}2}, and normal operation simulations, with power densities up to 12 MWm{sup {minus}2}, were conducted. The coatings remained adherent; at the highest levels tested, minor changes occurred, including localized remelting, modification of the crystallographic phases, occasional microcracking, and erosion.« less

40 CFR 63.1543 - Standards for process and process fugitive sources.

Code of Federal Regulations, 2011 CFR

2011-07-01

... section. (1) Sinter machine; (2) Blast furnace; (3) Dross furnace; (4) Dross furnace charging location; (5) Blast furnace and dross furnace tapping location; (6) Sinter machine charging location; (7) Sinter machine discharge end; (8) Sinter crushing and sizing equipment; and (9) Sinter machine area. (b) The...

Sintering and microstructure of silicon carbide ceramic with Y3Al5O12 added by sol-gel method*

PubMed Central

Guo, Xing-zhong; Yang, Hui

2005-01-01

Silicon carbide (SiC) ceramic with YAG (Y3Al5O12) additive added by sol-gel method was liquid-phase sintered at different sintering temperatures, and the sintering mechanism and microstructural characteristics of resulting silicon carbide ceramics were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and elemental distribution of surface (EDS). YAG (yttrium aluminum garnet) phase formed before the sintering and its uniform distribution in the SiC/YAG composite powder decreased the sintering temperature and improved the densification of SiC ceramic. The suitable sintering temperature was 1860 °C with the specimen sintered at this temperature having superior sintering and mechanical properties, smaller crystal size and fewer microstructure defects. Three characteristics of improved toughness of SiC ceramic with YAG added by sol-gel method were microstructural densification, main-crack deflection and crystal ‘bridging’. PMID:15682507

Effect of Process Parameter on Barium Titanate Stannate (BTS) Materials Sintered at Low Sintering

NASA Astrophysics Data System (ADS)

Shukla, Alok; Bajpai, P. K.

2011-11-01

Ba(Ti1-xSnx)O3 solid solutions with (x = 0.15, 0.20, 0.30 and 0.40) are synthesized using conventional solid state reaction method. Formation of solid solutions in the range 0 ≤ x ≤0.40 is confirmed using X-ray diffraction technique. Single phase solid solutions with homogeneous grain distribution are observed at relatively low sintering by controlling process parameters viz. sintering time. Composition at optimized temperature (1150 °C) sintered by varying the sintering time, stabilize in cubic perovskite phase. The % experimental density increase with increasing the time of sintering instead of increasing sintering temperature. The lattice parameter increases by increasing the tin composition in the material. This demonstrates that process parameter optimization can lead to single phase at relatively lower sintering-a major advantage for the materials used as capacitor element in MLCC.

Sintering behavior and mechanical properties of zirconia compacts fabricated by uniaxial press forming.

PubMed

Oh, Gye-Jeong; Yun, Kwi-Dug; Lee, Kwang-Min; Lim, Hyun-Pil; Park, Sang-Won

2010-09-01

The purpose of this study was to compare the linear sintering behavior of presintered zirconia blocks of various densities. The mechanical properties of the resulting sintered zirconia blocks were then analyzed. Three experimental groups of dental zirconia blocks, with a different presintering density each, were designed in the present study. Kavo Everest® ZS blanks (Kavo, Biberach, Germany) were used as a control group. The experimental group blocks were fabricated from commercial yttria-stabilized tetragonal zirconia powder (KZ-3YF (SD) Type A, KCM. Corporation, Nagoya, Japan). The biaxial flexural strengths, microhardnesses, and microstructures of the sintered blocks were then investigated. The linear sintering shrinkages of blocks were calculated and compared. Despite their different presintered densities, the sintered blocks of the control and experimental groups showed similar mechanical properties. However, the sintered block had different linear sintering shrinkage rate depending on the density of the presintered block. As the density of the presintered block increased, the linear sintering shrinkage decreased. In the experimental blocks, the three sectioned pieces of each block showed the different linear shrinkage depending on the area. The tops of the experimental blocks showed the lowest linear sintering shrinkage, whereas the bottoms of the experimental blocks showed the highest linear sintering shrinkage. Within the limitations of this study, the density difference of the presintered zirconia block did not affect the mechanical properties of the sintered zirconia block, but affected the linear sintering shrinkage of the zirconia block.

Sintering behavior and mechanical properties of zirconia compacts fabricated by uniaxial press forming

PubMed Central

Oh, Gye-Jeong; Yun, Kwi-Dug; Lee, Kwang-Min; Lim, Hyun-Pil

2010-01-01

PURPOSE The purpose of this study was to compare the linear sintering behavior of presintered zirconia blocks of various densities. The mechanical properties of the resulting sintered zirconia blocks were then analyzed. MATERIALS AND METHODS Three experimental groups of dental zirconia blocks, with a different presintering density each, were designed in the present study. Kavo Everest® ZS blanks (Kavo, Biberach, Germany) were used as a control group. The experimental group blocks were fabricated from commercial yttria-stabilized tetragonal zirconia powder (KZ-3YF (SD) Type A, KCM. Corporation, Nagoya, Japan). The biaxial flexural strengths, microhardnesses, and microstructures of the sintered blocks were then investigated. The linear sintering shrinkages of blocks were calculated and compared. RESULTS Despite their different presintered densities, the sintered blocks of the control and experimental groups showed similar mechanical properties. However, the sintered block had different linear sintering shrinkage rate depending on the density of the presintered block. As the density of the presintered block increased, the linear sintering shrinkage decreased. In the experimental blocks, the three sectioned pieces of each block showed the different linear shrinkage depending on the area. The tops of the experimental blocks showed the lowest linear sintering shrinkage, whereas the bottoms of the experimental blocks showed the highest linear sintering shrinkage. CONCLUSION Within the limitations of this study, the density difference of the presintered zirconia block did not affect the mechanical properties of the sintered zirconia block, but affected the linear sintering shrinkage of the zirconia block. PMID:21165274

Sintering of MSW fly ash for reuse as a concrete aggregate.

PubMed

Mangialardi, T

2001-10-12

The sintering process of municipal solid waste (MSW) fly ash was investigated in order to manufacture sintered products for reuse as concrete aggregates. Four types of fly ash resulting from different Italian MSW incineration plants were tested in this study. A modification of the chemical composition of MSW fly ash--through a preliminary four-stage washing treatment of this material with water--was attempted to improve the chemical and mechanical characteristics of sintered products.The sintering treatment of untreated or washed fly ash was performed on cylindrical compact specimens (15 mm in diameter and 20mm in height) at different compact pressures, sintering temperatures and times.The sintering process of untreated MSW fly ashes proved to be ineffective for manufacturing sintered products for reuse as a construction material, because of the adverse chemical characteristics of these fly ashes in terms of sulfate, chloride, and vitrifying oxide contents.A preliminary washing treatment of MSW fly ash with water greatly improved the chemical and mechanical characteristics of sintered products and, for all the types of fly ash tested, the sintered products satisfied the Italian requirements for normal weight aggregates for use in concretes having a specified strength not greater than 12 and 15N/mm(2), when measured on cylindrical and cubic specimens, respectively.A compact pressure of 28 N/mm(2), a sintering temperature of 1140 degrees C, and a sintering time of 60 min were the best operating conditions for manufacturing sintered products of washed MSW fly ash.

Transmission of Er:YAG laser through different dental ceramics.

PubMed

Sari, Tugrul; Tuncel, Ilkin; Usumez, Aslihan; Gutknecht, Norbert

2014-01-01

The aim of this study was to determine the erbium-doped yttrium aluminum garnet (Er:YAG) laser transmission ratio through different dental ceramics with different thicknesses. Laser debonding procedure of adhesively luted all-ceramic restorations is based on the transmission of laser energy through the ceramic and the ablation of resin cement, because of the transmitted laser energy. Five different dental ceramics were evaluated in this study: sintered zirconium-oxide core ceramic, monolithic zirconium-oxide ceramic, feldspathic ceramic, leucite-reinforced glass ceramic, and lithium disilicate-reinforced glass ceramic. Two ceramic discs with different thicknesses (0.5 and 1 mm) were fabricated for each group. Ceramic discs were placed between the sensor membrane of the laser power meter and the tip of the contact handpiece of an Er:YAG laser device with the aid of a custom- made acrylic holder. The transmission ratio of Er:YAG laser energy (500 mJ, 2 Hz, 1 W, 1000 μs) through different ceramic discs was measured with the power meter. Ten measurements were made for each group and the results were analyzed with two way analysis of variance (ANOVA) and Tukey honestly significant difference (HSD) tests. The highest transmission ratio was determined for lithium disilicate-reinforced ceramic with 0.5 mm thickness (88%) and the lowest was determined for feldspathic ceramic with 1 mm thickness (44%). The differences among the different ceramics and between the different thicknesses were significant (p<0.05). Ceramic type and thickness should be taken into consideration to adjust the laser irradiation parameters during laser debonding of adhesively luted all-ceramic restorations.

Effect of the application of surface treatments before and after sintering on the flexural strength, phase transformation and surface topography of zirconia.

PubMed

Kurtulmus-Yilmaz, Sevcan; Aktore, Huseyin

2018-05-01

To evaluate the effects of airborne-particle abrasion (APA) and Er,Cr:YSGG laser irradiation on 4-point-flexural strength, phase transformation and morphologic changes of zirconia ceramics treated at pre-sintered or post-sintered stage. Three hundred and forty-two bar shaped zirconia specimens were milled with different sizes according to the flexural strength test (n = 10), X-ray diffraction (XRD) (n = 4) and field emission scanning electron microscope (FE-SEM) (n = 4) analyses. For each test protocol, specimens were divided into 4 main groups whether the surface treatments applied before or after sintering and whether the specimens received heat treatment or not as pre-sintered, post-sintered no-heat and post-sintered heat-treated groups, and a group was served as control. Main groups were further divided into 6 equal subgroups according to surface treatment method applied (2 W-, 3 W-, 4 W-, 5 W-, 6 W-laser irradiations and APA). Surface treatments were applied to pre-sintered groups before sintering and to post-sintered groups after sintering. Post-sintered heat-treated groups were subjected to veneer ceramic firing simulation after surface treatments. Flexural strength and flexural modulus values were statistically analysed and monoclinic phase content was calculated. Weibull analysis was used to evaluate strength reliability and fractographic analysis was conducted. Highest flexural strength values were detected at post-sintered no-heat APA and 4W-laser groups (P < 0.05). Pre-sintered groups showed statistically lower flexural strength values. Heat treatment decreased the strength of the specimens. Monoclinic phase content was only detected at post-sintered no-heat groups and the highest amount was detected at APA group. Rougher surfaces and deeper irregularities were detected at FE-SEM images pre-sintered groups. Application of surface treatments at pre-sintered stage may be detrimental for zirconia ceramics in terms of flexural strength. Treating the surface of zirconia ceramic before sintering process is not recommended due to significant decrease in flexural strength values. 2 W-4 W Er,Cr:YSGG laser irradiations can be regarded as alternative surface treatment methods when zirconia restoration would be subjected to veneer ceramic firing procedures. Copyright © 2018 Elsevier Ltd. All rights reserved.

Fast plasma sintering delivers functional graded materials components with macroporous structures and osseointegration properties.

PubMed

Godoy, R F; Coathup, M J; Blunn, G W; Alves, A L; Robotti, P; Goodship, A E

2016-04-13

We explored the osseointegration potential of two macroporous titanium surfaces obtained using fast plasma sintering (FPS): Ti macroporous structures with 400-600 µmØ pores (TiMac400) and 850-1000 µmØ pores (TiMac850). They were compared against two surfaces currently in clinical use: Ti-Growth® and air plasma spray (Ti-Y367). Each surface was tested, once placed over a Ti-alloy and once onto a CoCr bulk substrate. Implants were placed in medial femoral condyles in 24 sheep. Samples were explanted at four and eight weeks after surgery. Push-out loads were measured using a material-testing system. Bone contact and ingrowth were assessed by histomorphometry and SEM and EDX analyses. Histology showed early osseointegration for all the surfaces tested. At 8 weeks, TiMac400, TiMac850 and Ti-Growth® showed deep bone ingrowth and extended colonisation with newly formed bone. The mechanical push-out force was equal in all tested surfaces. Plasma spray surfaces showed greater bone-implant contact and higher level of pores colonisation with new bone than FPS produced surfaces. However, the void pore area in FPS specimens was significantly higher, yet the FPS porous surfaces allowed a deeper osseointegration of bone to implant. FPS manufactured specimens showed similar osseointegration potential to the plasma spray surfaces for orthopaedic implants. FPS is a useful technology for manufacturing macroporous titanium surfaces. Furthermore, its capability to combine two implantable materials, using bulk CoCr with macroporous titanium surfaces, could be of interest as it enables designers to conceive and manufacture innovative components. FPS delivers functional graded materials components with macroporous structures optimised for osseointegration.

Pressureless sintering of whisker-toughened ceramic composites

DOEpatents

Tiegs, T.N.

1993-05-04

A pressureless sintering method is disclosed for use in the production of whisker-toughened ceramic composites wherein the sintered density of composites containing up to about 20 vol. % SiC whiskers is improved by reducing the average aspect ratio of the whiskers to from about 10 to about 20. Sintering aids further improve the density, permitting the production of composites containing 20 vol. % SiC with sintered densities of 94% or better of theoretical density by a pressureless sintering method.

Pressureless sintering of whiskered-toughened ceramic composites

DOEpatents

Tiegs, Terry N.

1994-01-01

A pressureless sintering method is disclosed for use in the production of whisker-toughened ceramic composites wherein the sintered density of composites containing up to about 20 vol. % SiC whiskers is improved by reducing the average aspect ratio of the whiskers to from about 10 to about 20. Sintering aids further improve the density, permitting the production of composites containing 20 vol. % SiC with sintered densities of 94% or better of theoretical density by a pressureless sintering method.

Pressureless sintering of whisker-toughened ceramic composites

DOEpatents

Tiegs, Terry N.

1993-01-01

A pressureless sintering method is disclosed for use in the production of whisker-toughened ceramic composites wherein the sintered density of composites containing up to about 20 vol. % SiC whiskers is improved by reducing the average aspect ratio of the whiskers to from about 10 to about 20. Sintering aids further improve the density, permitting the production of composites containing 20 vol. % SiC with sintered densities of 94% or better of theoretical density by a pressureless sintering method.

Behavior of New Zealand Ironsand During Iron Ore Sintering

NASA Astrophysics Data System (ADS)

Wang, Zhe; Pinson, David; Chew, Sheng; Rogers, Harold; Monaghan, Brian J.; Pownceby, Mark I.; Webster, Nathan A. S.; Zhang, Guangqing

2016-02-01

A New Zealand ironsand sample was characterized by scanning electron microscopy (SEM), X-ray fluorescence spectroscopy, qualitative and quantitative X-ray diffraction, and electron probe microanalysis. The titanomagnetite-rich ironsand was added into an industrial sinter blend in the proportion of 5 wt pct, and the mixture was uniaxially pressed into cylindrical tablets and sintered in a tube furnace under flowing gas with various oxygen potentials and temperatures to develop knowledge and understanding of the behavior of titanium during sintering. An industrial sinter with the addition of 3 wt pct ironsand was also examined. Both the laboratory and industrial sinters were characterized by optical and SEM. Various morphologies of relict ironsand particles were present in the industrial sinter due to the heterogeneity of sintering conditions, which could be well simulated by the bench-scale sintering experiments. The assimilation of ironsand during sintering in a reducing atmosphere started with the diffusion of calcium into the lattice of the ironsand matrix, and a reaction zone was formed near the boundary within individual ironsand particles where a perovskite phase was generated. With increasing sintering temperature, in a reducing atmosphere, ironsand particles underwent further assimilation and most of the titanium moved from the ironsand particles into a glass phase. In comparison, more titanium remained in the original ironsand particles when sintered in air. Ironsand particles are more resistant to assimilation in an oxidizing atmosphere.

The effect of noble metal additives on the optimum operating temperature of SnO2 gas sensors

NASA Astrophysics Data System (ADS)

Mohammad-Yousefi, S.; Rahbarpour, S.; Ghafoorifard, H.

2017-12-01

The effect of Pd and Au additives on gas sensing properties of SnO2 was investigated. SnO2 pallets were fabricated and sintered at 900 °C for 90 minutes. Several nanometer layers of Pd and Au were deposited on separate SnO2 pallets and were intentionally dispersed into the SnO2 pallets by long heat treatment (400 °C for 1 Day). All metal loaded samples showed significant enhancement in response level and optimum operating temperature compare to pure SnO2 gas sensors. The amount of enhancement was strongly dependent on the material and the thickness of deposited metal layer. Studying butanol response showed that increasing the thickness of metal causes the response level to increase. Further thickness increase caused contrary effect and decreased the performance of sensors. Best results were achieved at 10 nm-thick Au and 7 nm-thick Pd. Generally, Pd-SnO2 samples demonstrated better performance than Au-SnO2 ones, however, Au-SnO2 samples were proved to be good candidate to sense reducing gases with lower hydrogen atoms in their formula. Given experimental results were also good evidence of chemical activity of gold and simply confirms the relation between chemical activity and gold particle size. Results were qualitatively described by gas diffusion theory and surface reactions take place on metal particles.The first section in your paper

A comparative study of conventionally sintered and microwave sintered nickel zinc ferrite

NASA Astrophysics Data System (ADS)

Rani, Rekha; Juneja, J. K.; Raina, K. K.; Kotnala, R. K.; Prakash, Chandra

2014-04-01

For the present work, nickel zinc ferrite having compositional formula Ni0.8Zn0.2Fe2O4 was synthesized by conventional solid state method and sintered in conventional and microwave furnaces. Pellets were sintered with very short soaking time of 10 min at 1150 °C in microwave furnace whereas 4 hrs of soaking time was selected for conventional sintering at 1200 °C. Phase formation was confirmed by X-ray diffraction analysis technique. Scanning electron micrographs were taken for microstructural study. Dielectric properties were studied as a function of temperature. To study magnetic behavior, M-H hysteresis loops were recorded for both samples. It is observed that microwave sintered sample could obtain comparable properties to the conventionally sintered one in lesser soaking time at lower sintering temperature.

Formation and decay of charge carriers in aggregate nanofibers consisting of poly(3-hexylthiophene)-coated gold nanoparticles.

PubMed

Lee, Dongki; Lee, Jaewon; Song, Ki-Hee; Rhee, Hanju; Jang, Du-Jeon

2016-01-21

Thin nanofibers (NFs) of J-dominant aggregates with a thickness of 15 nm and thick NFs of H-dominant aggregates with a thickness of 25 nm were fabricated by the self-assembly of poly(3-hexylthiophene)-coated gold nanoparticles. The formation and decay dynamics of the charge carriers, which are dependent on the aggregate types of NFs, was investigated by time-resolved emission and transient-absorption spectroscopy. With increasing excitation energy, the fraction of the fast emission decay component decreased, suggesting that the fast formation of polaron pairs (PP), localized (LP), and delocalized polarons (DP) results from higher singlet exciton states produced by the singlet fusion. The faster decay dynamics of DP and LP in the thick NFs than in thin NFs is due to the increased delocalization of DP and LP. As the interchain aggregation is weaker than intrachain aggregation, PP decays faster in thin NFs than in thick NFs. In both thin and thick NFs, although triplet (T1) excitons were barely observed with excitation at 532 nm on a nanosecond time scale, they were observed with excitation at 355 nm, showing that T1 excitons within NFs are generated mainly through the singlet fission from a higher singlet exciton state rather than through intersystem crossing.

Multilayer Black Phosphorus Near-Infrared Photodetectors.

PubMed

Hou, Chaojian; Yang, Lijun; Li, Bo; Zhang, Qihan; Li, Yuefeng; Yue, Qiuyang; Wang, Yang; Yang, Zhan; Dong, Lixin

2018-05-23

Black phosphorus (BP), owing to its distinguished properties, has become one of the most competitive candidates for photodetectors. However, there has been little attention paid on photo-response performance of multilayer BP nanoflakes with large layer thickness. In fact, multilayer BP nanoflakes with large layer thickness have greater potential from the fabrication viewpoint as well as due to the physical properties than single or few layer ones. In this report, the thickness-dependence of the intrinsic property of BP photodetectors in the dark was initially investigated. Then the photo-response performance (including responsivity, photo-gain, photo-switching time, noise equivalent power, and specific detectivity) of BP photodetectors with relative thicker thickness was explored under a near-infrared laser beam ( λ IR = 830 nm). Our experimental results reveal the impact of BP's thickness on the current intensity of the channel and show degenerated p-type BP is beneficial for larger current intensity. More importantly, the photo-response of our thicker BP photodetectors exhibited a larger responsivity up to 2.42 A/W than the few-layer ones and a fast response photo-switching speed (response time is ~2.5 ms) comparable to thinner BP nanoflakes was obtained, indicating BP nanoflakes with larger layer thickness are also promising for application for ultra-fast and ultra-high near-infrared photodetectors.

Corrigendum to "Extra-terrestrial construction processes - Advancements, opportunities and challenges" [Adv. Space Res. 60 (2017) 1413-1429

NASA Astrophysics Data System (ADS)

Lim, Sungwoo; Prabhu, Vibha Levin; Anand, Mahesh; Taylor, Lawrence A.

2018-05-01

The authors regret that because of an oversight, the published manuscript contained following errors (i) the estimated energy consumption for laser sintering was ten times larger than the real value as a result of incorrect unit conversion from J/mm2 ∗ thickness (μm) to kW h/m3; (ii) an inappropriate comparison with Benaroya (2010) as the estimation for energy consumption in Benaroya (2010) was based on a conventional furnace and NOT microwave heating. The revised text pertaining to paragraph 2 of Section 2.2.1, the last paragraph of Section 3.3 and Table 1 are provided below.

Thermal shock and erosion resistant tantalum carbide ceramic material

NASA Technical Reports Server (NTRS)

Honeycutt, L., III; Manning, C. R. (Inventor)

1978-01-01

Ceramic tantalum carbide artifacts with high thermal shock and mechanical erosion resistance are provided by incorporating tungsten-rhenium and carbon particles in a tantalum carbide matrix. The mix is sintered by hot pressing to form the ceramic article which has a high fracture strength relative to its elastic modulus and thus has an improved thermal shock and mechanical erosion resistance. The tantalum carbide is preferable less than minus 100 mesh, the carbon particles are preferable less than minus 100 mesh, and the tungsten-rhenium particles are preferable elongate, having a length to thickness ratio of at least 2/1. Tungsten-rhenium wire pieces are suitable as well as graphite particles.

Flexural strength of proof-tested and neutron-irradiated silicon carbide

NASA Astrophysics Data System (ADS)

Price, R. J.; Hopkins, G. R.

1982-08-01

Proof testing before service is a valuable method for ensuring the reliability of ceramic structures. Silicon carbide has been proposed as a very low activation first-wall and blanket structural material for fusion devices, where it would experience a high flux of fast neutrons. Strips of three types of silicon carbide were loaded in four-point bending to a stress sufficient to break about a third of the specimens. Groups of 16 survivors were irradiated to 2 × 10 26n/ m2 ( E>0.05 MeV) at 740°C and bend tested to failure. The strength distribution of chemically vapor-deposited silicon carbide (Texas Instruments) was virtually unchanged by irradiation. The mean strength of sintered silicon carbide (Carborundum Alpha) was reduced 34% by irradiation, while the Weibull modulus and the truncated strength distribution characteristic of proof-tested material were retained. Irradiation reduced the mean strength of reaction-bonded silicon carbide (Norton NC-430) by 58%, and the spread in strength values was increased. We conclude that for the chemically vapor-deposited and the sintered silicon carbide the benefits of proof testing to eliminate low strength material are retained after high neutron exposures.

The influence of sintering temperature on the proliferation of fibroblastic cells in contact with HA-bioceramics.

PubMed

Frayssinet, P; Rouquet, N; Fages, J; Durand, M; Vidalain, P O; Bonel, G

1997-06-05

HA-ceramics used in human surgery as osteoconductive surfaces show a great variety of characteristics. Certain characteristics such as grain size, porosity, and surface area, are controlled by the sintering temperature of the slurry. We grew L-929 fibroblast cells on HA-ceramic disks that had been sintered at different temperatures ranging from 850 degrees-1350 degrees C. The cell line growth rate was lower on ceramic disks than on the culture-grade polystyrene used as a negative control. Cell growth correlated with the ceramic sintering temperature although no significant difference in the cell adhesion to the different ceramics was shown. Growth rate on ceramics sintered at low temperatures (850 degrees and 950 degrees C) was negative whereas it was positive on disks sintered at higher temperatures. When the cells were separated from the disks by a polycarbonate membrane, the growth rate was negative on those membranes in contact with low-temperature sintered disks and positive on the high-temperature sintered disks. The calcium and phosphorus concentration in the culture medium in contact with ceramics sintered below 1050 degrees C decreased during the culture period. Ceramics sintered between 1100 degrees and 1250 degrees C brought about an increase in Ca and P concentrations while ceramics sintered at higher temperatures did not induce any changes. SEM examination of the 850 degrees and 1200 degrees C sintered ceramics showed that the 850 degrees C sintered ceramics consisted of small grains with pores between them and the 1200 degrees C sintered ceramics were made of larger grains without any visible pores, thereby decreasing the surface of material in contact with the culture medium. This difference in surface area was confirmed by the fact that the amount of albumin absorbed onto the ceramic was dependent on the sintering temperature. In conclusion, the modification of the culture medium brought about by high-surfaced ceramics could influence the growth of cells with which such ceramics come in contact.

Pressureless sintering of whiskered-toughened ceramic composites

DOEpatents

Tiegs, T.N.

1994-12-27

A pressureless sintering method is disclosed for use in the production of whisker-toughened ceramic composites wherein the sintered density of composites containing up to about 20 vol. % SiC whiskers is improved by reducing the average aspect ratio of the whiskers to from about 10 to about 20. Sintering aids further improve the density, permitting the production of composites containing 20 vol. % SiC with sintered densities of 94% or better of theoretical density by a pressureless sintering method. 6 figures.

Graphene addition to MgB{sub 2} superconductor obtained by ex-situ spark plasma sintering technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Aldica, G.; Burdusel, M.; Popa, S.

Highlights: • Graphene-added dense MgB{sub 2} was prepared by ex-situ spark plasma sintering. • There is a limited interaction between graphene and MgB{sub 2}. • Addition of graphene (G) shows a small enhancement of J{sub c} and μ{sub 0}H{sub irr}. • G is one of the least effective C-containing additions. - Abstract: Graphene nanopowder (G) with average thickness particle size of about 6–8 nm was added to MgB{sub 2} commercial powder. Starting composition was (MgB{sub 2}){sub (1−x)}(G){sub x}, x = 0.0125, 0.025, 0.05. Processing was performed by Spark Plasma Sintering (SPS) technique. All added samples have high density (above 95%).more » The critical temperature (T{sub c}) and the lattice parameter a (c-axis lattice parameter is constant) show a small variation suggesting that carbon substitution for boron is low. TEM observations show the presence of un-reacted graphene plates supporting the T{sub c} and structural results. It also indicates that G-addition does not modify the MgB{sub 2} microstructure. Despite this, there is an optimum doped sample (MgB{sub 2}){sub 0.9875}(G){sub 0.0125} for which the critical current density at temperatures below 25 K is slightly higher at high magnetic fields than for the pristine sample. The addition of G is found as one of the least effective C-source additions enhancing J{sub c}. We discuss results as being strongly related to variation of the residual stress.« less

Effect of Ceramic Surface Treatments After Machine Grinding on the Biaxial Flexural Strength of Different CAD/CAM Dental Ceramics.

PubMed

Bagheri, Hossein; Hooshmand, Tabassom; Aghajani, Farzaneh

2015-09-01

This study aimed to evaluate the effect of different ceramic surface treatments after machining grinding on the biaxial flexural strength (BFS) of machinable dental ceramics with different crystalline phases. Disk-shape specimens (10mm in diameter and 1.3mm in thickness) of machinable ceramic cores (two silica-based and one zirconia-based ceramics) were prepared. Each type of the ceramic surfaces was then randomly treated (n=15) with different treatments as follows: 1) machined finish as control, 2) machined finish and sandblasting with alumina, and 3) machined finish and hydrofluoric acid etching for the leucite and lithium disilicate-based ceramics, and for the zirconia; 1) machined finish and post-sintered as control, 2) machined finish, post-sintered, and sandblasting, and 3) machined finish, post-sintered, and Nd;YAG laser irradiation. The BFS were measured in a universal testing machine. Data based were analyzed by ANOVA and Tukey's multiple comparisons post-hoc test (α=0.05). The mean BFS of machined finish only surfaces for leucite ceramic was significantly higher than that of sandblasted (P=0.001) and acid etched surfaces (P=0.005). A significantly lower BFS was found after sandblasting for lithium disilicate compared with that of other groups (P<0.05). Sandblasting significantly increased the BFS for the zirconia (P<0.05), but the BFS was significantly decreased after laser irradiation (P<0.05). The BFS of the machinable ceramics was affected by the type of ceramic material and surface treatment method. Sandblasting with alumina was detrimental to the strength of only silica-based ceramics. Nd:YAG laser irradiation may lead to substantial strength degradation of zirconia.

Improved thermoelectric properties of Bi2Te3-xSex alloys by melt spinning and resistance pressing sintering

NASA Astrophysics Data System (ADS)

Cai, Xinzhi; Fan, Xi'an; Rong, Zhenzhou; Yang, Fan; Gan, Zhanghua; Li, Guangqiang

2014-03-01

Starting from bismuth, tellurium and selenium chunks, n-type Bi2Te3-xSex (x ⩽ 0.3) alloys were obtained by melt spinning (MS) combined with a resistance pressing sintering (RPS) process. The phases, microstructures and compositions of the samples were evaluated by x-ray diffraction, field emission scanning electron microscopy, and energy dispersive x-ray spectroscopy during each step in the preparation process, respectively. The influences of Se doping, MS and RPS processes on the thermoelectric (TE) properties of Bi2Te3-xSex alloys were investigated in detail. The Bi2Te3-xSex powders could be well compacted by the RPS process and the relative densities of the bulks prepared by RPS were all higher than 96%. The partially oriented lamellar structure could be observed at some regions of the samples prepared by RPS, and the monolayer thickness of the lamellar structure in the MS-RPS samples was smaller than that in the smelting-RPS sample. The MS process was confirmed as an excellent method to obtain fine microstructures and low lattice thermal conductivity for the TE materials. All evidence about electrical and thermal transport properties suggested that suitably increasing the Se content could effectively improve the ZT value. The maximum ZT value of 0.84 was obtained for the Bi2Te2.7Se0.3 prepared by MS-RPS at 423 K. As opposed to the conventional hot pressing and spark plasma sintering, the RPS method introduced here is more suitable for practical industrial application due to its cost saving and high efficiency.

Effect of Ceramic Surface Treatments After Machine Grinding on the Biaxial Flexural Strength of Different CAD/CAM Dental Ceramics

PubMed Central

Bagheri, Hossein; Aghajani, Farzaneh

2015-01-01

Objectives: This study aimed to evaluate the effect of different ceramic surface treatments after machining grinding on the biaxial flexural strength (BFS) of machinable dental ceramics with different crystalline phases. Materials and Methods: Disk-shape specimens (10mm in diameter and 1.3mm in thickness) of machinable ceramic cores (two silica-based and one zirconia-based ceramics) were prepared. Each type of the ceramic surfaces was then randomly treated (n=15) with different treatments as follows: 1) machined finish as control, 2) machined finish and sandblasting with alumina, and 3) machined finish and hydrofluoric acid etching for the leucite and lithium disilicate-based ceramics, and for the zirconia; 1) machined finish and post-sintered as control, 2) machined finish, post-sintered, and sandblasting, and 3) machined finish, post-sintered, and Nd;YAG laser irradiation. The BFS were measured in a universal testing machine. Data based were analyzed by ANOVA and Tukey’s multiple comparisons post-hoc test (α=0.05). Results: The mean BFS of machined finish only surfaces for leucite ceramic was significantly higher than that of sandblasted (P=0.001) and acid etched surfaces (P=0.005). A significantly lower BFS was found after sandblasting for lithium disilicate compared with that of other groups (P<0.05). Sandblasting significantly increased the BFS for the zirconia (P<0.05), but the BFS was significantly decreased after laser irradiation (P<0.05). Conclusions: The BFS of the machinable ceramics was affected by the type of ceramic material and surface treatment method. Sandblasting with alumina was detrimental to the strength of only silica-based ceramics. Nd:YAG laser irradiation may lead to substantial strength degradation of zirconia. PMID:27148372

Behavior of oxide film at the interface between particles in sintered Al powders by pulse electric-current sintering

NASA Astrophysics Data System (ADS)

Xie, Guoqiang; Ohashi, Osamu; Song, Minghui; Furuya, Kazuo; Noda, Tetsuji

2003-03-01

The microstructure of the bonding interfaces between particles in aluminum (Al) powder sintered specimens by the pulse electric-current sintering (PECS) process was observed, using conventional transmission electron microscopy (CTEM) and high-resolution transmission electron microscopy (HRTEM). The behavior of oxide film at the interface between Al particles and its effect on properties of the sintered specimens were investigated. The results showed there were two kinds of bonding interfaces in the sintered specimens, namely, the direct metal/metal bonding and the metal/oxide film layer/metal bonding interface. By increasing the fraction of the direct metal/metal bonding interfaces, the tensile strength of the sintered specimens increased, and the electrical resistivity decreased. By increasing the loading pressure at higher sintering temperatures or increasing the sintering temperature under loading pressure, the breakdown of oxide film was promoted. The broken oxide film debris was dispersed in aluminum metal near the bonding interfaces between particles.

Effect of sintering atmosphere on properties of porous stainless steel for biomedical applications.

PubMed

Dudek, Agata; Włodarczyk, Renata

2013-01-01

This study discusses manufacturing of metallic biomaterials by means of powder metallurgy with consideration for their unquestionable advantages, i.e. opportunities of obtaining materials with controllable porosity. The paper focuses on properties of 316 L stainless steel obtained using the method of powder metallurgy with respect to compacting pressure and sintering atmosphere. All the specimens were compacted at 700, 400 and 225 MPa, and sintered at 1250 °C. In order to analyze the sintering atmosphere, three different media were used: dissociated ammonia, hydrogen and vacuum. The study covered sintering density, porosity, microstructure analysis and corrosion resistance. The proposed method of powder metallurgy allowed for obtaining materials with predictable size and distribution of pores, depending on the parameters of sinter preparation (compaction force, sinter atmosphere). High corrosion resistance of the materials (sintering in the atmosphere of hydrogen and in vacuum) and high porosity in the sinters studied offer opportunities for using them for medical purposes. Copyright © 2012 Elsevier B.V. All rights reserved.

[Effect of compaction pressure on the properties of dental machinable zirconia ceramic].

PubMed

Huang, Hui; Wei, Bin; Zhang, Fu-qiang; Sun, Jing; Gao, Lian

2010-10-01

To investigate the effect of compaction pressure on the linear shrinkage, sintering property and machinability of the dental zirconia ceramic. The nano-size zirconia powder was compacted at different isostatic pressure and sintered at different temperature. The linear shrinkage of sintered body was measured and the relative density was tested using the Archimedes method. The cylindrical surface of pre-sintering blanks was traversed using a hard metal tool. Surface and edge quality were checked visually using light stereo microscopy. The sintering behaviour depended on the compaction pressure. Increasing compaction pressure led to higher sintering rate and lower sintering temperature. Increasing compaction pressure also led to decreasing linear shrinkage of the sintered bodies, from 24.54% of 50 MPa to 20.9% of 400 MPa. Compaction pressure showed only a weak influence on machinability of zirconia blanks, but the higher compaction pressure resulted in the poor surface quality. The better sintering property and machinability of dental zirconia ceramic is found for 200-300 MPa compaction pressure.

Infiltration sintering properties of Ni-4B-4Si(wt.%) alloy powders

NASA Astrophysics Data System (ADS)

Yang, Q.; Zhang, X. C.; Wang, F. L.; Zou, J. T.

2018-01-01

The Ni-4B-4Si(wt.%) alloy powders were infiltrated into the nickel skeletons, the effects of sintering temperatures (1050-1150 °C) and skeletons (loose and compact nickel powders) on the microstructures and hardness of the sintered alloys were investigated. The Ni-B-Si alloy sintered at 1100 °C consisted of γ-Ni and Ni3B, and Si mainly solid soluted in the γ-Ni. The loose nickel powders favored to the infiltration of Ni-B-Si liquid alloy into the nickel skeletons, the sintered alloys exhibited dense microstructures and good interfacial bonding with Ni substrates. The interfacial hardness was equal to that of the sintered alloys and Ni substrates. Loose nickel powders ensured the density and interfacial bonding of the sintered alloys, the infiltration sintering process can be simplified and easily applied to practice.

Factors contributing to the temperature beneath plaster or fiberglass cast material

PubMed Central

Hutchinson, Michael J; Hutchinson, Mark R

2008-01-01

Background Most cast materials mature and harden via an exothermic reaction. Although rare, thermal injuries secondary to casting can occur. The purpose of this study was to evaluate factors that contribute to the elevated temperature beneath a cast and, more specifically, evaluate the differences of modern casting materials including fiberglass and prefabricated splints. Methods The temperature beneath various types (plaster, fiberglass, and fiberglass splints), brands, and thickness of cast material were measured after they were applied over thermometer which was on the surface of a single diameter and thickness PVC tube. A single layer of cotton stockinette with variable layers and types of cast padding were placed prior to application of the cast. Serial temperature measurements were made as the cast matured and reached peak temperature. Time to peak, duration of peak, and peak temperature were noted. Additional tests included varying the dip water temperature and assessing external insulating factors. Ambient temperature, ambient humidity and dip water freshness were controlled. Results Outcomes revealed that material type, cast thickness, and dip water temperature played key roles regarding the temperature beneath the cast. Faster setting plasters achieved peak temperature quicker and at a higher level than slower setting plasters. Thicker fiberglass and plaster casts led to greater peak temperature levels. Likewise increasing dip-water temperature led to elevated temperatures. The thickness and type of cast padding had less of an effect for all materials. With a definition of thermal injury risk of skin injury being greater than 49 degrees Celsius, we found that thick casts of extra fast setting plaster consistently approached dangerous levels (greater than 49 degrees for an extended period). Indeed a cast of extra-fast setting plaster, 20 layers thick, placed on a pillow during maturation maintained temperatures over 50 degrees of Celsius for over 20 minutes. Conclusion Clinicians should be cautious when applying thick casts with warm dip water. Fast setting plasters have increased risk of thermal injury while brand does not appear to play a significant role. Prefabricated fiberglass splints appear to be safer than circumferential casts. The greatest risk of thermal injury occurs when thick casts are allowed to mature while resting on pillow. PMID:18298851

Characteristics of iron ore sinter with EFB addition

NASA Astrophysics Data System (ADS)

Purwanto, H.; Rozhan, A. N.; Mohamad, A. S.; Zakiyuddin, A.

2018-04-01

Utilization of EFB-derived biochar in sintering of iron ore has been conducted in this work with regards to the porosity of iron sinter. EFB has been heated up in argon atmosphere to 450°C in order to produce biochar. In the present work, the sintering process was conducted at 1150°C with variations of biochar content from 5% to 10%. In this case, the apparent density for iron sinter shows significant decrease as the biochar addition increase. The porosity of iron sinter showed a gradual increment from 5% to 7.5% and escalated at 10% biochar content. The results of porosity and apparent density were in line with the micrograph of iron sinter.

Apparatus and method for direct measurement of coal ash sintering and fusion properties at elevated temperatures and pressures

DOEpatents

Khan, M. Rashid

1990-01-01

A high-pressure microdilatometer is provided for measuring the sintering and fusion properties of various coal ashes under the influence of elevated pressures and temperatures in various atmospheres. Electrical resistivity measurements across a sample of coal ash provide a measurement of the onset of the sintering and fusion of the ash particulates while the contraction of the sample during sintering is measured with a linear variable displacement transducer for detecting the initiation of sintering. These measurements of sintering in coal ash at different pressures provide a mechanism by which deleterious problems due to the sintering and fusion of ash in various combustion systems can be minimized or obviated.

Sintered Lining for Heat-Pipe Evaporator

NASA Technical Reports Server (NTRS)

Ernst, D. M.; Eastman, G. Y.

1985-01-01

Hotspots eliminated by lining inner wall. Distribution of heat transfer liquid in heat-pipe evaporator improved by lining inner wall with layer of sintered metal. Sintered layer takes place of layer of screen wick formerly sintered or bonded to wall. Since sintered layer always full of liquid, no hotspot of type that previously arose where former screen wick did not fit properly against wall.

Effect of surface oxide films on the properties of pulse electric-current sintered metal powders

NASA Astrophysics Data System (ADS)

Xie, Guoqiang; Ohashi, Osamu; Yamaguchi, Norio; Wang, Airu

2003-11-01

Metallic powders with various thermodynamic stability oxide films (Ag, Cu, and Al powders) were sintered using a pulse electric-current sintering (PECS) process. Behavior of oxide films at powder surfaces and their effect on the sintering properties were investigated. The results showed that the sintering properties of metallic powders in the PECS process were subject to the thermodynamic stability of oxide films at particles surfaces. The oxide films at Ag powder surfaces are decomposed during sintering with the contact region between the particles being metal/metal bond. The oxide films at Cu powder surfaces are mainly broken via loading pressure at a low sintering temperature. At a high sintering temperature, they are mainly dissolved in the parent metal, and the contact regions turn into the direct metal/metal bonding. Excellent sintering properties can be received. The oxide films at Al powder surfaces are very stable, and cannot be decomposed and dissolved, but broken by plastic deformation of particles under loading pressure at experimental temperatures. The interface between particles is partially bonded via the direct metal/metal bonding making it difficult to achieve good sintered properties.

[Influence of manufacture technique on translucency and color of dental porcelain].

PubMed

Xiong, Fang; Chao, Yong-Lie; Zhu, Zhi-Min

2007-12-01

To study the influence of manufacture technique on the translucency and color of dental porcelain. Specimens were made of VITA VMK 95 dentin porcelain and enamel porcelain and divided into 3 groups: Sintering times group (1, 2, 4, 6, 8 and 10 times), sintering temperature group (910, 920, 930, 940 and 950 degrees C), sintering vacuum group (95, 65, 35 and 0 kPa). Transmittance, Y, dominant wavelength and saturation were measured by PR-650 spectra scan spectrocolorimeter. Transmittance of dentin porcelain increased after 6 times repeated sintering. Transmittance of enamel porcelain increased first after the second sintering, and then became decreasing when sintering more than 2 times. Transmittance of enamel porcelain deceased when sintering temperature was lower than standard. Decrease of sintering vacuum caused the transmittance of dentin and enamel porcelain decreased. The changing of value was coordinated with transmittance. Dominant wavelength and saturation had negative correlation with sintering times and temperature, and positive correlation with vacuum. Sintering times, temperature and vacuum all had prominent effects on the translucency and color of dental porcelain. Comparing with dentin porcelain, enamel porcelain was more sensitive with the modification of manufacture technique.

Exothermic low temperature sintering of Cu nanoparticles

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mittal, Jagjiwan; Lin, Kwang-Lung, E-mail: matkllin@mail.ncku.edu.tw

2015-11-15

Sintering of the Cu nanoparticle at low temperatures resulted in exothermic behavior after its initiation. The calorimetry study of the heating of a 20 nm copper nanoparticles agglomerate revealed the evolution of 41.17 J/g of heat between 170 °C and 270 °C. High resolution transmission electron microscopy (HRTEM) images indicated that the heat generation was accompanied by sintering. The surface energy of the 20 nm copper nanoparticles was estimated to be 1.23 × 10{sup 3} erg/cm{sup 2} based on the heat released during sintering. The in situ high resolution transmission electron microscope (HRTEM) investigation showed that vigorous sintering occurred betweenmore » 217 and 234 °C, which took place through the dislocation sintering mechanism. - Highlights: • Calorimetry showed exothermic behavior during heating of Cu nanoparticles between 170 and 270 °C. • Heat released due to the sintering of Cu nanoparticles was demonstrated by HRTEM. • Surface energy of 20 nm copper nanoparticles was estimated to be 1.23 × 10{sup 3} erg/cm{sup 2} during sintering. • Growth in crystallite sizes during sintering is disclosed by X-ray diffraction. • In situ HRTEM heating study showed occurrence of sintering through dislocation mechanism.« less

Effect of Sintering Temperature on Magnetic Core-Loss Properties of a NiCuZn Ferrite for High-Frequency Power Converters

NASA Astrophysics Data System (ADS)

Yan, Yi; Ngo, Khai D. T.; Hou, Dongbin; Mu, Mingkai; Mei, Yunhui; Lu, Guo-Quan

2015-10-01

In an effort to find a magnetic material for making low-loss magnetic components for high-power-density converters, we investigated the magnetic core-loss characteristics of a commercial NiCuZn ferrite (LSF 50) at 5 MHz as a function of the sintering temperature of the ferrite powder. The ferrite powder was compacted into toroid cores and then sintered at 850°C, 900°C, 950°C, 1000°C, and 1050°C for 2 h. The sintered densities of the cores increased at higher sintering temperatures. The magnetic properties of the sintered cores—complex permeability and core-loss density—were measured. We found that both the real and imaginary parts of the relative permeability increased with sintering temperature. The core-loss results at 5 MHz showed that the cores sintered at 950°C and 1000°C had the lowest core-loss densities, being two to three times lower than that of a commercial NiZn ferrite (4F1) core. Microstructures of the sintered cores were examined by scanning electron microscopy; the grains grew significantly at higher sintering temperatures.

Enhanced thermal conductivity of uranium dioxide-silicon carbide composite fuel pellets prepared by Spark Plasma Sintering (SPS)

NASA Astrophysics Data System (ADS)

Yeo, S.; Mckenna, E.; Baney, R.; Subhash, G.; Tulenko, J.

2013-02-01

Uranium dioxide (UO2)-10 vol% silicon carbide (SiC) composite fuel pellets were produced by oxidative sintering and Spark Plasma Sintering (SPS) at a range of temperatures from 1400 to 1600 °C. Both SiC whiskers and SiC powder particles were utilized. Oxidative sintering was employed over 4 h and the SPS sintering was employed only for 5 min at the highest hold temperature. It was noted that composite pellets sintered by SPS process revealed smaller grain size, reduced formation of chemical products, higher density, and enhanced interfacial contact compared to the pellets made by oxidative sintering. For given volume of SiC, the pellets with powder particles yielded a smaller grain size than pellets with SiC whiskers. Finally thermal conductivity measurements at 100 °C, 500 °C, and 900 °C revealed that SPS sintered UO2-SiC composites exhibited an increase of up to 62% in thermal conductivity compared to UO2 pellets, while the oxidative sintered composite pellets revealed significantly inferior thermal conductivity values. The current study points to the improved processing capabilities of SPS compared to oxidative sintering of UO2-SiC composites.

On the self-damping nature of densification in photonic sintering of nanoparticles

PubMed Central

MacNeill, William; Choi, Chang-Ho; Chang, Chih-Hung; Malhotra, Rajiv

2015-01-01

Sintering of nanoparticle inks over large area-substrates is a key enabler for scalable fabrication of patterned and continuous films, with multiple emerging applications. The high speed and ambient condition operation of photonic sintering has elicited significant interest for this purpose. In this work, we experimentally characterize the temperature evolution and densification in photonic sintering of silver nanoparticle inks, as a function of nanoparticle size. It is shown that smaller nanoparticles result in faster densification, with lower temperatures during sintering, as compared to larger nanoparticles. Further, high densification can be achieved even without nanoparticle melting. Electromagnetic Finite Element Analysis of photonic heating is coupled to an analytical sintering model, to examine the role of interparticle neck growth in photonic sintering. It is shown that photonic sintering is an inherently self-damping process, i.e., the progress of densification reduces the magnitude of subsequent photonic heating even before full density is reached. By accounting for this phenomenon, the developed coupled model better captures the experimentally observed sintering temperature and densification as compared to conventional photonic sintering models. Further, this model is used to uncover the reason behind the experimentally observed increase in densification with increasing weight ratio of smaller to larger nanoparticles. PMID:26443492

Determining optimal operation parameters for reducing PCDD/F emissions (I-TEQ values) from the iron ore sintering process by using the Taguchi experimental design.

PubMed

Chen, Yu-Cheng; Tsai, Perng-Jy; Mou, Jin-Luh

2008-07-15

This study is the first one using the Taguchi experimental design to identify the optimal operating condition for reducing polychlorinated dibenzo-p-dioxins and dibenzofurans (PCDD/ Fs) formations during the iron ore sintering process. Four operating parameters, including the water content (Wc; range = 6.0-7.0 wt %), suction pressure (Ps; range = 1000-1400 mmH2O), bed height (Hb; range = 500-600 mm), and type of hearth layer (including sinter, hematite, and limonite), were selected for conducting experiments in a pilot scale sinter pot to simulate various sintering operating conditions of a real-scale sinter plant We found that the resultant optimal combination (Wc = 6.5 wt%, Hb = 500 mm, Ps = 1000 mmH2O, and hearth layer = hematite) could decrease the emission factor of total PCDD/Fs (total EF(PCDD/Fs)) up to 62.8% by reference to the current operating condition of the real-scale sinter plant (Wc = 6.5 wt %, Hb = 550 mm, Ps = 1200 mmH2O, and hearth layer = sinter). Through the ANOVA analysis, we found that Wc was the most significant parameter in determining total EF(PCDD/Fs (accounting for 74.7% of the total contribution of the four selected parameters). The resultant optimal combination could also enhance slightly in both sinter productivity and sinter strength (30.3 t/m2/day and 72.4%, respectively) by reference to those obtained from the reference operating condition (29.9 t/m (2)/day and 72.2%, respectively). The above results further ensure the applicability of the obtained optimal combination for the real-scale sinter production without interfering its sinter productivity and sinter strength.

Effect on the grain size of single-mode microwave sintered NiCuZn ferrite and zinc titanate dielectric resonator ceramics.

PubMed

Sirugudu, Roopas Kiran; Vemuri, Rama Krishna Murthy; Venkatachalam, Subramanian; Gopalakrishnan, Anisha; Budaraju, Srinivasa Murty

2011-01-01

Microwave sintering of materials significantly depends on dielectric, magnetic and conductive Losses. Samples with high dielectric and magnetic loss such as ferrites could be sintered easily. But low dielectric loss material such as dielectric resonators (paraelectrics) finds difficulty in generation of heat during microwave interaction. Microwave sintering of materials of these two classes helps in understanding the variation in dielectric and magnetic characteristics with respect to the change in grain size. High-energy ball milled Ni0.6Cu0.2Zn0.2Fe1.98O4-delta and ZnTiO3 are sintered in conventional and microwave methods and characterized for respective dielectric and magnetic characteristics. The grain size variation with higher copper content is also observed with conventional and microwave sintering. The grain size in microwave sintered Ni0.6Cu0.2Zn0.2Fe1.98O4-delta is found to be much small and uniform in comparison with conventional sintered sample. However, the grain size of microwave sintered sample is almost equal to that of conventional sintered sample of Ni0.3Cu0.5Zn0.2Fe1.98O4-delta. In contrast to these high dielectric and magnetic loss ferrites, the paraelectric materials are observed to sinter in presence of microwaves. Although microwave sintered zinc titanate sample showed finer and uniform grains with respect to conventional samples, the dielectric characteristics of microwave sintered sample are found to be less than that of conventional sample. Low dielectric constant is attributed to the low density. Smaller grain size is found to be responsible for low quality factor and the presence of small percentage of TiO2 is observed to achieve the temperature stable resonant frequency.

Synchrotron X-ray studies of model SOFC cathodes, part II: Porous powder cathodes

DOE PAGES

Chang, Kee-Chul; Ingram, Brian; Ilavsky, Jan; ...

2017-10-28

Infiltrated La 0.6Sr 0.4Co 0.2Fe 0.8O 3-δ (LSCF) sintered porous powder cathodes for solid oxide fuel cells have been investigated by synchrotron ultra-small angle x-ray scattering (USAXS). Here, we demonstrated that atomic layer deposition (ALD) is the method for a uniform coating and liquid-phase infiltration for growing nanoscale particles on the porous LSCF surfaces. The MnO infiltrate, grown by ALD, forms a conformal layer with a uniform thickness throughout the pores evidenced by USAXS thickness fringes. The La 0.6Sr 0.4CoO 3 (LSC) and La 2Zr 2O 7 (LZO) infiltrates, grown by liquid-phase infiltration, were found to form nanoscale particles onmore » the surfaces of LSCF particles resulting in increased surface areas. In conclusion, impedance measurements suggest that the catalytic property of LSC infiltrate, not the increased surface area of LZO, is important for increasing oxygen reduction activities.« less

Synchrotron X-ray studies of model SOFC cathodes, part II: Porous powder cathodes

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chang, Kee-Chul; Ingram, Brian; Ilavsky, Jan

Infiltrated La 0.6Sr 0.4Co 0.2Fe 0.8O 3-δ (LSCF) sintered porous powder cathodes for solid oxide fuel cells have been investigated by synchrotron ultra-small angle x-ray scattering (USAXS). Here, we demonstrated that atomic layer deposition (ALD) is the method for a uniform coating and liquid-phase infiltration for growing nanoscale particles on the porous LSCF surfaces. The MnO infiltrate, grown by ALD, forms a conformal layer with a uniform thickness throughout the pores evidenced by USAXS thickness fringes. The La 0.6Sr 0.4CoO 3 (LSC) and La 2Zr 2O 7 (LZO) infiltrates, grown by liquid-phase infiltration, were found to form nanoscale particles onmore » the surfaces of LSCF particles resulting in increased surface areas. In conclusion, impedance measurements suggest that the catalytic property of LSC infiltrate, not the increased surface area of LZO, is important for increasing oxygen reduction activities.« less

Suppressing Crack Formation in Particulate Systems by Utilizing Capillary Forces

PubMed Central

Schneider, Monica; Maurath, Johannes; Fischer, Steffen B.; Weiß, Moritz; Willenbacher, Norbert; Koos, Erin

2017-01-01

Cracks, formed during the drying of particulate films, can reduce the effectiveness or even render products useless. We present a novel, generic approach to suppress crack formation in thin films made from hard particle suspensions, which are otherwise highly susceptible to cracking, using the capillary force between particles present when a trace amount of an immiscible liquid is added to a suspension. This secondary liquid preserves the particle cohesion, modifying the structure and increasing the drying rate. Crack-free films can be produced at thicknesses much greater than the critical cracking thickness for a suspension without capillary interactions, and even persists after sintering. This capillary suspension strategy is applicable to a broad range of materials including suspensions of metals, semiconductive and ceramic oxides or glassy polymeric particles and can be easily implemented in many industrial processes since it is based on well-established unit operations. Promising fields of application include ceramic foils and printed electronic devices. PMID:28263554

Oxygen ingress study of 3D printed gaseous radiation detector enclosures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Steer, Christopher A.; Durose, Aaron

2015-07-01

As part of our ongoing studies into the potential application of 3D printing techniques to gaseous radiation detectors, we have studied the ability of 3D printed enclosures to resist environmental oxygen ingress. A set of cuboid and hexagonal prism shaped enclosures with wall thicknesses of 4 mm, 6 mm, 8 mm and 10 mm were designed and printed in nylon using a EOSINT P 730 Selective Laser Sintering 3D printer system These test enclosures provide a comparison of different environmental gas ingress for different 3D printing techniques. The rate of change of oxygen concentration was found to be linear, decreasingmore » as the wall thickness increases. It was also found that the hexagonal prism geometry produced a lower rate of change of oxygen concentration compared with the cuboid shaped enclosures. Possible reasons as to why these results were obtained are discussed The implications for the this study for deployable systems are also discussed (authors)« less

Characterization of M-type barium hexagonal ferrite-based wide band microwave absorber

NASA Astrophysics Data System (ADS)

Meshram, M. R.; Agrawal, Nawal K.; Sinha, Bharoti; Misra, P. S.

2004-05-01

This paper present the design, development and characterization of the hexagonal ferrite powder [BaCo 0.5δTi 0.5δMn 0.1Fe (11.87-δ)O 19] and [Ba(MnTi) δFe (12-2δ)O 19] at δ=1.6 as a microwave absorber. The hexagonal ferrite powder has been developed by dry attrition and sintering procedure. The developed ferrite powder 60% by weight has been mixed in epoxy resin to form a microwave-absorbing paint. This paint was coated on a conducting aluminum sheet to study the absorption characteristics of a linearly polarized TE wave at X band. The results for single- and two-layer microwave absorbers for different coating thicknesses have been reported. It has been found that it shows the broadband characteristics with minimum absorption of 8 dB from 8 to 12 GHz for a coating thickness of 2 mm.These paints are very useful in military applications such as RCS reduction, camouflaging of the target and prevention of EMI, etc.

Critical current density and microstructure of screen-printed (Bi,Pb)2Sr2Ca2Cu3O(x) thick film sandwiched between Ag substrates

NASA Astrophysics Data System (ADS)

Oota, A.; Matsui, H.; Funakura, M.; Iwaya, J.; Maeda, J.

1993-07-01

A process of combined rolling and uniaxial pressing with intermediate sintering steps for fabrication of screen-printed (Bi,Pb)2Sr2Ca2Cu3O(x) thick films sandwiched between Ag substrates yields c-axis-oriented microstructures with a high critical current density (Jc) of 1.5 x 10 exp 4 A/sq cm (77 K, 0 T) and 9.0 x 10 exp 4 A/sq cm (23 K, 0 T). The measured Jc anisotropy at 77 K, as a function of the angle Theta between B and c axis, is pronounced. An increase in B sharpens a peak at Theta = 90 deg in the Jc vs Theta curve, together with enhancement of the anisotropy ratio. In high fields above 0.5 T, the half-height angular width of the peak approaches an average misalignment angle between the grains with increasing B.

The influence of anatase-rutile mixed phase and ZnO blocking layer on dye-sensitized solar cells based on TiO2nanofiberphotoanodes

PubMed Central

2013-01-01

High performance is expected in dye-sensitized solar cells (DSSCs) that utilize one-dimensional (1-D) TiO2 nanostructures owing to the effective electron transport. However, due to the low dye adsorption, mainly because of their smooth surfaces, 1-D TiO2 DSSCs show relatively lower efficiencies than nanoparticle-based ones. Herein, we demonstrate a very simple approach using thick TiO2 electrospun nanofiber films as photoanodes to obtain high conversion efficiency. To improve the performance of the DSCCs, anatase-rutile mixed-phase TiO2 nanofibers are achieved by increasing sintering temperature above 500°C, and very thin ZnO films are deposited by atomic layer deposition (ALD) method as blocking layers. With approximately 40-μm-thick mixed-phase (approximately 15.6 wt.% rutile) TiO2 nanofiber as photoanode and 15-nm-thick compact ZnO film as a blocking layer in DSSC, the photoelectric conversion efficiency and short-circuit current are measured as 8.01% and 17.3 mA cm−2, respectively. Intensity-modulated photocurrent spectroscopy and intensity-modulated photovoltage spectroscopy measurements reveal that extremely large electron diffusion length is the key point to support the usage of thick TiO2 nanofibers as photoanodes with very thin ZnO blocking layers to obtain high photocurrents and high conversion efficiencies. PMID:23286741

Effects of Rapid Solidification on Phase Formation and Microstructure Evolution of AgSbTe₂-Based Thermoelectric Compounds.

PubMed

Castellero, Alberto; Fiore, Gianluca; Evenstein, Eliran; Baricco, Marcello; Amouyal, Yaron

2017-03-01

We report on rapid solidification of an Ag(16.7)Sb(30.0)Te(53.3) compound using planar flow casting to stabilize the δ-AgSbTe₂ single phase and avoid precipitation of the interconnected Sb₂Te₃ phase, which leads to deterioration of thermoelectric properties. Rapidly solidified samples are in form of flakes with different thickness (60–400 μm). Precipitation of Sb2Te₃ phase is fully inhibited in thin flakes (thickness below 100 μm), which consist of an homogeneous δ-AgSbTe₂ matrix, whereas isolated Sb₂Te₃ precipitates, dispersed throughout the δ-AgSbTe₂ matrix, were found in thick flakes (thickness above 100 μm). The lattice parameter of the δ-AgSbTe₂ phase progressively increases with the cooling rate, indicating progressive supersaturation of the matrix for high degree of supercooling. Bulk specimens were prepared by hot pressing of the rapidly solidified flakes to evaluate thermoelectric properties. After sintering of the rapidly solidified flakes, the differential scanning calorimetry (DSC) traces indicates partial decomposition of the non equilibrium δ-AgSbTe₂ into the stable phases. Measurements of the thermoelectric transport properties indicate the positive effects of rapid solidification on thermal conductivity and Seebeck coefficient and its negative effect on electrical conductivity, suggesting an operative way to improve thermoelectric performance.

Processing effects on microstructure, percolation and resistive sensor properties of nickel-zirconium oxide cermet films on silicon substrates

NASA Astrophysics Data System (ADS)

Sundeen, John Edward, Jr.

Thin Ni-ZrO2 cermet films were developed on silicon substrates using solution based, metallo-organic deposition (MOD) technique. The nickel based cermet films on silicon are of interest for heater, temperature and flow sensor devices, particularly in automotive or aerospace applications at UP to 250°C. In this study, precursors for the NiO-ZrO2 composite films were derived from metal carboxylate and nitrate based solutions. Composition and heat treatment conditions were the main process variables for controlling the structure, particle size and morphology, on which the electrical properties depend. Electrical resistance behavior was studied for Ni-ZrO2 films with 25--78 vol.% Ni content. This Ni amount exceeds the percolation threshold for conduction. The dependence of the resistance on individual processing variables, including film thickness, ambient flow rate, sintering temperature and time, and specimen geometry was studied. Electrical characterization included establishing the percolative resistive behavior in the MOD Ni-ZrO2 films. A resistive percolation threshold (pc) at ˜25 vol.% Ni was found for 800°C sintered, 1mum thick Ni-ZrO2 films. Existing models including the general effective media (GEM) percolation equation, and mixture rules were used to develop a predictive expression for Ni-ZrO2 film resistance as a function of composition. Kinetic analysis of particle size in the 55 vol.% Ni cermet films was directly correlated to the sheet resistance (Rs) of the films. The temperature coefficient of resistance (TCR) was also correlated to R s, by the equation: (TCR)alpha = alphao - betaR s. These electrical characteristics make the films suitable for use as gas flow and temperature sensors. Calculated figure of merit (rho-TCR), values for the MOD Ni-ZrO2 films Compared favorably to commercial Pt and Ni based thin and thick film formulations used for heaters and thermal sensors. An added advantage of the MOD Ni-ZrO2, compared to the non-linear behavior of Ni, was that film resistance response to temperature is highly linear over the temperature range of 20--160°C. Select films could be heated to 45--100°C with a low (I2R) power input of 400mW-2W. Then films demonstrated stable hot resistance, high sensitivity and rapid response to gas flow. Significant accomplishments from this work included the development of: (a) MOD derived cermet films of 40--78 vol.% Ni, with high positive TCR of 2600--4250ppm/°C and Rs of 2.5--60%O/□/1mum which are highly suitable for thermal sensing applications, (b) A simple mixture rule rho = rhoo - m·VNi describing the film resistivity with composition; and (c) Expressions correlating film TCR and resistance to sintering time and temperature using particle growth kinetics.

Comparison of collagen fibre architecture between slow-twitch cranial and fast-twitch caudal parts of broiler M. latissimus dorsi.

PubMed

Nakamura, Y N; Iwamoto, H; Tabata, S; Ono, Y

2003-07-01

1. Collagen fibre architectures of perimysium and endomysium in the slow-twitch cranial and fast-twitch caudal parts of broiler M. latissimus dorsi were compared. 2. Type I and III collagens were distributed in both perimysium and endomysium as indicated by their positive immunohistochemical reactions to polyclonal antibodies. 3. Cells invested by endomysium with no myofibres were larger in the cranial part because of the presence of larger slow-twitch myofibres. The honeycomb structure of endomysium was divided into several parts by thick perimysium. 4. The thick perimysial collagen fibres with parallel fibrils, which were interconnected by the loose reticular fibrils and thin fibres, were more numerous and thicker in the cranial part than the caudal. 5. Thick endomysial sidewall of cells in the cranial part was composed of a rougher reticulum of slightly thicker collagen fibrils compared with the thin sidewall in the caudal part. 6. These results indicated that both perimysial constitutions of collagen fibres and endomysial collagen fibrils had attained much larger growth in the slow-twitch cranial part than the fast-twitch caudal in broiler latissimus dorsi muscle.

A fast and flexible method for manufacturing 3D molded interconnect devices by the use of a rapid prototyping technology

NASA Astrophysics Data System (ADS)

Amend, P.; Pscherer, C.; Rechtenwald, T.; Frick, T.; Schmidt, M.

This paper presents experimental results of manufacturing MID-prototypes by means of SLS, laser structuring and metallization. Therefore common SLS powder (PA12) doped with laser structuring additives is used. First of all the influence of the additives on the characteristic temperatures of melting and crystallization is analyzed by means of DSC. Afterwards the sintering process is carried out and optimized by experiments. Finally the generated components are qualified regarding their density, mechanical properties and surface roughness. Especially the surface quality is important for the metallization process. Therefore surface finishing techniques are investigated.

High energy X-ray diffraction study of a dental ceramics–titanium functional gradient material prepared by field assisted sintering technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Witte, K., E-mail: kerstin.witte@uni-rostock.de; Bodnar, W.; Schell, N.

A functional gradient material with eleven layers composed of a dental ceramics and titanium was successfully consolidated using field assisted sintering technique in a two-step sintering process. High energy X-ray diffraction studies on the gradient were performed at High Energy Material Science beamline at Desy in Hamburg. Phase composition, crystal unit edges and lattice mismatch along the gradient were determined applying Rietveld refinement procedure. Phase analysis revealed that the main crystalline phase present in the gradient is α-Ti. Crystallinity increases stepwisely along the gradient with a decreasing increment between every next layer, following rather the weight fraction of titanium. Themore » crystal unit edge a of titanium remains approximately constant with a value of 2.9686(1) Å, while c is reduced with increasing amount of titanium. In the layer with pure titanium the crystal unit edge c is constant with a value of 4.7174(2) Å. The lattice mismatch leading to an internal stress was calculated over the whole gradient. It was found that the maximal internal stress in titanium embedded in the studied gradient is significantly smaller than its yield strength, which implies that the structure of titanium along the whole gradient is mechanically stable. - Highlights: • High energy XRD studies of dental ceramics–Ti gradient material consolidated by FAST. • Phase composition, crystallinity and lattice parameters are determined. • Crystallinity increases stepwisely along the gradient following weight fraction of Ti. • Lattice mismatch leading to internal stress is calculated over the whole gradient. • Internal stress in α-Ti embedded in the gradient is smaller than its yield strength.« less

Al2O3-TiC Composite Prepared by Spark Plasma Sintering Process: Evaluation of Mechanical and Tribological Properties

NASA Astrophysics Data System (ADS)

Kumar, Rohit; Chaubey, A. K.; Bathula, Sivaiah; Prashanth, K. G.; Dhar, Ajay

2018-03-01

Al2O3-10TiC composites were synthesized by spark plasma sintering (SPS) process. Microstructural and mechanical properties of the composite reveal homogeneous distribution of the fine TiC particles in the matrix. The samples were produced with different sintering temperature, and it shows that the hardness and density gradually increases with increasing sintering temperature. Abrasion wear test result reveals that the composite sintered at 1500 °C shows high abrasion resistance (wt. loss 0.016 g) and the lowest abrasion resistance was observed for the composite sample sintered at 1100 °C (wt. loss 1.459 g). The profilometry surface roughness study shows that sample sintered at 1100 °C shows maximum roughness ( R a = 6.53 µm) compared to the sample sintered at 1500 °C ( R a = 0.66 µm) corroborating the abrasion wear test results.

The effects of surface finish and grain size on the strength of sintered silicon carbide

NASA Technical Reports Server (NTRS)

You, Y. H.; Kim, Y. W.; Lee, J. G.; Kim, C. H.

1985-01-01

The effects of surface treatment and microstructure, especially abnormal grain growth, on the strength of sintered SiC were studied. The surfaces of sintered SiC were treated with 400, 800 and 1200 grit diamond wheels. Grain growth was induced by increasing the sintering times at 2050 C. The beta to alpha transformation occurred during the sintering of beta-phase starting materials and was often accompanied by abnormal grain growth. The overall strength distributions were established using Weibull statistics. The strength of the sintered SiC is limited by extrinsic surface flaws in normal-sintered specimens. The finer the surface finish and grain size, the higher the strength. But the strength of abnormal sintering specimens is limited by the abnormally grown large tabular grains. The Weibull modulus increases with decreasing grain size and decreasing grit size for grinding.

Gravitational Role in Liquid Phase Sintering

NASA Technical Reports Server (NTRS)

Upadhyaya, Anish; Iacocca, Ronald G.; German, Randall M.

1998-01-01

To comprehensively understand the gravitational effects on the evolution of both the microstructure and the macrostructure during liquid phase sintering, W-Ni-Fe alloys with W content varying from 35 to 98 wt.% were sintered in microgravity. Compositions that slump during ground-based sintering also distort when sintered under microgravity. In ground-based sintering, low solid content alloys distort with a typical elephant-foot profile, while in microgravity, the compacts tend to spheroidize. This study shows that microstructural segregation occurs in both ground-based as well as microgravity sintering. In ground-based experiments, because of the density difference between the solid and the liquid phase, the solid content increases from top to the bottom of the sample. In microgravity, the solid content increases from periphery to the center of the samples. This study also shows that the pores during microgravity sintering act as a stable phase and attain anomalous shapes.

An application of powder metallurgy to dentistry.

PubMed

Oda, Y; Ueno, S; Kudoh, Y

1995-11-01

Generally, the dental casting method is used to fabricate dental prostheses made with metal. The method of fabricating dental prostheses from sintered titanium alloy has certain advantages: the elimination of casting defects, a sintering temperature that is lower than the melting point, and a shorter processing time. By examining (1) the properties of green, sintered compacts of titanium powder, (2) the effects of adding aluminum powder on the properties of green, sintered compacts of Ti-Al compound, and (3) the effects of adding copper powder on the properties of green, sintered compacts of Ti-Al-Cu compound, the authors developed a sintered titanium alloy on a trial basis. Because the properties satisfied the requirements of dental restorations, a powder metallurgical method of making dental restorations from this sintered titanium alloy was devised. Applications of such sintered titanium alloys for the metal coping of metal-ceramic crowns and denture base plates were discussed.

Structural and mechanical characterization of boron doped biphasic calcium phosphate produced by wet chemical method and subsequent thermal treatment

DOE Office of Scientific and Technical Information (OSTI.GOV)

Albayrak, Onder, E-mail: albayrakonder@mersin.edu.tr

In the current study, boron doped biphasic calcium phosphate bioceramics consisting of a mixture of boron doped hydroxyapatite (BHA) and beta tricalcium phosphate (β-TCP) of varying BHA/β-TCP ratios were obtained after sintering stage. The effects of varying boron contents and different sintering temperatures on the BHA/β-TCP ratios and on the sinterability of the final products were investigated. Particle sizes and morphologies of the obtained precipitates were determined using SEM. XRD and FTIR investigation were conducted to detect the boron formation in the structure of HA and quantitative analysis was performed to determine the BHA/β-TCP ratio before and after sintering stage.more » In order to determine the sinterability of the obtained powders, pellets were prepared and sintered; the rates of densification were calculated and obtained results were correlated by SEM images. Also Vickers microhardness values of the sintered samples were determined. The experimental results verified that boron doped hydroxyapatite powders were obtained after sintering stage and the structure consists of a mixture of BHA and β-TCP. As the boron content used in the precipitation stage increases, β-TCP content of the BHA/β-TCP ratio increases but sinterability, density and microhardness deteriorate. As the sintering temperature increases, β-TCP content, density and microhardness of the samples increase and sinterability improves. - Highlights: • This is the first paper about boron doped biphasic calcium phosphate bioceramics. • Boron doping affects the structural and mechanical properties. • BHA/β-TCP ratio can be adjustable with boron content and sintering temperature.« less

One step sintering of homogenized bauxite raw material and kinetic study

NASA Astrophysics Data System (ADS)

Gao, Chang-he; Jiang, Peng; Li, Yong; Sun, Jia-lin; Zhang, Jun-jie; Yang, Huan-ying

2016-10-01

A one-step sintering process of bauxite raw material from direct mining was completed, and the kinetics of this process was analyzed thoroughly. The results show that the sintering kinetics of bauxite raw material exhibits the liquid-phase sintering behavior. A small portion of impurities existed in the raw material act as a liquid phase. After X-ray diffraction analyses, scanning electron microscopy observations, and kinetics calculations, sintering temperature and heating duration were determined as the two major factors contributing to the sintering process and densification of bauxite ore. An elevated heating temperature and longer duration favor the densification process. The major obstacle for the densification of bauxite material is attributed to the formation of the enclosed blowhole during liquid-phase sintering.

Stress-dislocation interaction mechanism in low-temperature thermo-compression sintering of Ag NPs

NASA Astrophysics Data System (ADS)

Wang, Fuliang; Tang, Zikai; He, Hu

2018-04-01

The sintering of metal nanoparticles (NPs) has been widely studied in the field of nanotechnology, and low-temperature sintering has become the industry standard. In this study, a molecular dynamics (MD) model was established to study the sintering behaviour of silver NPs during low-temperature thermo-compression. Primarily, we studied the sintering process, in which the ratio of neck radius to particle radius (x/r) changes. Under a uniaxial pressure, the maximum ratio in the temperature range 420-425 K was 1. According to the change of x/r, the process can be broken down into three stages: the neck-formation stage, neck-growth stage, and neck-stability stage. In addition, the relationship between potential energy, internal stress, and dislocation density during sintering is discussed. The results showed that cycling internal stress played an important role in sintering. Under the uniaxial pressure, the stress-dislocation interaction was found to be the major mechanism for thermo-compression sintering because the plastic deformation product dislocation intensified the diffusion of atoms. Also, the displacement vector, the mean square displacement, and the changing crystal structure during sintering were studied.

[Study on preparation and physicochemical properties of surface modified sintered bone].

PubMed

Li, Jingfeng; Zheng, Qixin; Guo, Xiaodong

2012-06-01

The aim of this study is to investigate a new method for preparing a biomimetic bone material-surface modified sintered bovine cancellous bone, and to improve its bioactivity as a tissue engineering bone. The prepared sintered bovine cancellous bones with the same size were randomly divided into two groups, immersing in 1 and 1. 5 times simulated body fluid (SBF), respectively. The three time periods of soak time were 7, 14, and 21 days. After sintered bone was dried, the surface morphology of sintered bone and surface mineralization composition were observed under scanning electron microscopy (SEM). By comparing the effect of surface modification of sintered bone materials, we chose the most ideal material and studied its pore size, the rate of the porosity, the compress and bend intensity. And then the material and the sintered bone material without surface modification were compared. The study indicated that sintered bone material immersed in SBF (1.5 times) for 14 days showed the best effect of surface modification, retaining the original physico-chemical properties of sintered bone.

Sintered rare earth-iron Laves phase magnetostrictive alloy product and preparation thereof

DOEpatents

Malekzadeh, Manoochehr; Pickus, Milton R.

1979-01-01

A sintered rare earth-iron Laves phase magnetostrictive alloy product characterized by a grain oriented morphology. The grain oriented morphology is obtained by magnetically aligning powder particles of the magnetostrictive alloy prior to sintering. Specifically disclosed are grain oriented sintered compacts of Tb.sub.x Dy.sub.1-x Fe.sub.2 and their method of preparation. The present sintered products have enhanced magnetostrictive properties.

Influence of Hydrogen on Atomized Titanium Powders Sintering

NASA Astrophysics Data System (ADS)

Senkevich, K. S.

2018-07-01

The aim of this work is to study the effect of hydrogen reversible alloying (thermohydrogen processing, THP) on low-temperature sintering of atomized titanium powders. It is stated that alloying with 0.2 to 0.8 wt pct of hydrogen beneficially affects titanium powders sintering. The effect is caused by phase transformations occurring upon hydrogen saturation of powders and dehydrogenation, which substantially intensifies sintering at temperatures from 800 °C to 900 °C. The role of certain THP stages (sintering in hydrogenated state and upon dehydrogenation) on formation of sintered contacts in porous materials is shown.

Influence of Hydrogen on Atomized Titanium Powders Sintering

NASA Astrophysics Data System (ADS)

Senkevich, K. S.

2018-05-01

The aim of this work is to study the effect of hydrogen reversible alloying (thermohydrogen processing, THP) on low-temperature sintering of atomized titanium powders. It is stated that alloying with 0.2 to 0.8 wt pct of hydrogen beneficially affects titanium powders sintering. The effect is caused by phase transformations occurring upon hydrogen saturation of powders and dehydrogenation, which substantially intensifies sintering at temperatures from 800 °C to 900 °C. The role of certain THP stages (sintering in hydrogenated state and upon dehydrogenation) on formation of sintered contacts in porous materials is shown.

Sintering Kinetics of Inkjet Printed Conductive Silver Lines on Insulating Plastic Substrate

DOE PAGES

Zhou, Wenchao; List, III, Frederick Alyious; Duty, Chad E; ...

2015-01-24

This paper focuses on sintering kinetics of inkjet printed lines containing silver nanoparticles deposited on a plastic substrate. Upon heat treatment, the change of resistance in the printed lines was measured as a function of time and sintering temperatures from 150 to 200 C. A critical temperature was observed for the sintering process, beyond which there was no further reduction in resistance. Analysis shows the critical temperature correlates to the boiling point of the solvent, which is attributed to a liquid-mediated sintering mechanism. It is demonstrated that the sintering process shuts down after the solvent has completely evaporated.

Effects of the addition of municipal solid waste incineration fly ash on the behavior of polychlorinated dibenzo-p-dioxins and furans in the iron ore sintering process.

PubMed

Min, Yi; Liu, Chengjun; Shi, Peiyang; Qin, Chongda; Feng, Yutao; Liu, Baichen

2018-04-11

Raw materials were co-sintered with municipal solid waste incineration (MSWI) fly ash through iron ore sintering to promote the safe treatment and utilization of MSWI fly ash. To assess the feasibility of this co-sintering method, in this study, the effects of the addition of MSWI fly ash on the formation and emission of polychlorinated dibenzo-p-dioxins and furans (PCDD/Fs) were estimated via iron ore sintering pot experiments. During co-sintering, most of the PCDD/Fs in the added MSWI fly ash were decomposed and transformed into PCDD/Fs associated with iron sintering, and the concentrations of lower- and mid-chlorinated congeners increased. As there was a sufficient chlorine source and the sintering bed permeability was decreased by the addition of MSWI fly ash, the PCDD/F concentration in the exhaust gas increased. The mass emission of PCDD/Fs decreased; however, the emission of toxic PCDD/Fs increased beyond the total emissions from the independent MSW incineration and iron ore sintering processes due to the transformation of PCDD/F congeners. The co-sintering may be an important solution after technological improvements in the flue gas cleaning system and PCDD/F formation inhibition procedures. Copyright © 2018. Published by Elsevier Ltd.

Lightweight Aluminum/Nano composites for Automotive Drive Train Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chelluri, Bhanumathi; Knoth, Edward A.; Schumaker, Edward J.

2012-12-14

During Phase I, we successfully processed air atomized aluminum powders via Dynamic Magnetic Compaction (DMC) pressing and subsequent sintering to produce parts with properties similar to wrought aluminum. We have also showed for the first time that aluminum powders can be processed without lubes via press and sintering to 100 % density. This will preclude a delube cycle in sintering and promote environmentally friendly P/M processing. Processing aluminum powders via press and sintering with minimum shrinkage will enable net shape fabrication. Aluminum powders processed via a conventional powder metallurgy process produce too large a shrinkage. Because of this, sinter partsmore » have to be machined into specific net shape. This results in increased scrap and cost. Fully sintered aluminum alloy under this Phase I project has shown good particle-to-particle bonding and mechanical properties. We have also shown the feasibility of preparing nano composite powders and processing via pressing and sintering. This was accomplished by dispersing nano silicon carbide (SiC) powders into aluminum matrix comprising micron-sized powders (<100 microns) using a proprietary process. These composite powders of Al with nano SiC were processed using DMC press and sinter process to sinter density of 85-90%. The process optimization along with sintering needs to be carried out to produce full density composites.« less

Early and current physical activity: relationship with intima-media thickness and metabolic variables in adulthood

PubMed Central

Lima, Manoel C. S.; Barbosa, Maurício F.; Diniz, Tiego A.; Codogno, Jamile S.; Freitas, Ismael F.; Fernandes, Rômulo A.

2014-01-01

Background: It is unclear whether early physical activity has a greater influence on intima-media thickness and metabolic variables than current physical activity. Objective: To analyze the relationship between current and early physical activity, metabolic variables, and intima-media thickness measures in adults. Method: The sample was composed of 55 healthy subjects of both sexes (33 men and 22 women). Total body fat and trunk fat were estimated by dual-energy X-ray absorptiometry. Carotid and femoral intima-media thickness were measured using a Doppler ultrasound device. A 12-hour fasting blood sample collection was taken (fasting glucose and lipid profile). Early physical activity was assessed through face-to-face interview, and the current physical activity was assessed by pedometer (Digi-Walker Yamax, SW200), which was used for a period of seven days. Results: Current physical activity was negatively related to total cholesterol (rho=-0.31), while early physical activity was negatively related to triglycerides (rho=-0.42), total cholesterol (rho=-0.28), very low density lipoprotein (rho=-0.44), and carotid intima-media thickness (rho=-0.50). In the multivariate model, subjects engaged in sports activities during early life had lower values of very low density lipoprotein (b=-8.74 [b=-16.1; -1.47]) and carotid intima-media thickness (b=-0.17 [95%CI: -0.28; -0.05]). Conclusion: Early 95%CI physical activity has a significant influence on carotid intima-media thickness, regardless of the current physical activity. PMID:25372009

Early and current physical activity: relationship with intima-media thickness and metabolic variables in adulthood.

PubMed

Lima, Manoel C S; Barbosa, Maurício F; Diniz, Tiego A; Codogno, Jamile S; Freitas Júnior, Ismael F; Fernandes, Rômulo A

2014-01-01

It is unclear whether early physical activity has a greater influence on intima-media thickness and metabolic variables than current physical activity. To analyze the relationship between current and early physical activity, metabolic variables, and intima-media thickness measures in adults. The sample was composed of 55 healthy subjects of both sexes (33 men and 22 women). Total body fat and trunk fat were estimated by dual-energy X-ray absorptiometry. Carotid and femoral intima-media thickness were measured using a Doppler ultrasound device. A 12-hour fasting blood sample collection was taken (fasting glucose and lipid profile). Early physical activity was assessed through face-to-face interview, and the current physical activity was assessed by pedometer (Digi-Walker Yamax, SW200), which was used for a period of seven days. Current physical activity was negatively related to total cholesterol (rho=-0.31), while early physical activity was negatively related to triglycerides (rho=-0.42), total cholesterol (rho=-0.28), very low density lipoprotein (rho=-0.44), and carotid intima-media thickness (rho=-0.50). In the multivariate model, subjects engaged in sports activities during early life had lower values of very low density lipoprotein (b=-8.74 [b95%CI=-16.1; -1.47]) and carotid intima-media thickness (b=-0.17 [95%CI: -0.28; -0.05]). Early 95%CI physical activity has a significant influence on carotid intima-media thickness, regardless of the current physical activity.

[Influence of repeated sintering on the color of two brands of porcelain-fused-to-titanium].

PubMed

Shu, Cheng-jun; Luo, Xiao-ping; Wu, Lie

2007-08-01

To investigate the influence of repeated sintering on the color of two porcelain-fused-to-titanium, and the differences between the two porcelains. Thirty samples were prepared and sintered for 9 times. The color of samples were measured following sintering 1, 3, 5, 7, 9 times by ShadeEye NCC colorimeter according to two brands of porcelains with CIE1976L*a*b* color system, and calculated relevant chrome, chromatism and hue, and statistical analysis. When two brands of porcelains were sintered 5 times, the color parameters had no significant change and sintered continuely, the color parameters of L* and a* had obvious changes, but can't be observed by eyes. The color parameters of titanium-porcelains have no significant change after repeated sintering.

Sub-second carbon-nanotube-mediated microwave sintering for high-conductivity silver patterns on plastic substrates

NASA Astrophysics Data System (ADS)

Jung, Sunshin; Chun, Su Jin; Han, Joong Tark; Woo, Jong Seok; Shon, Cha-Hwa; Lee, Geon-Woong

2016-02-01

A method of microwave sintering that is mediated by carbon nanotubes (CNTs) has been developed to obtain high-conductivity Ag patterns on the top of heat-sensitive plastic substrates within a short time. The Ag patterns are printed on CNTs formed on plastic substrates and rapidly heated to a great extent by the heat transferred from the microwave-heated CNTs. The conductivity of the microwave-sintered Ag patterns reaches ~39% that of bulk Ag within 1 s without substrate deformation. Furthermore, microwave sintering enhances the adhesion of Ag patterns to the thermoplastic substrates because the sintering causes interfacial fusion between the Ag patterns and the substrates, and CNTs physically connect the patterns with the substrates.A method of microwave sintering that is mediated by carbon nanotubes (CNTs) has been developed to obtain high-conductivity Ag patterns on the top of heat-sensitive plastic substrates within a short time. The Ag patterns are printed on CNTs formed on plastic substrates and rapidly heated to a great extent by the heat transferred from the microwave-heated CNTs. The conductivity of the microwave-sintered Ag patterns reaches ~39% that of bulk Ag within 1 s without substrate deformation. Furthermore, microwave sintering enhances the adhesion of Ag patterns to the thermoplastic substrates because the sintering causes interfacial fusion between the Ag patterns and the substrates, and CNTs physically connect the patterns with the substrates. Electronic supplementary information (ESI) available: Temperature difference in Ag/CNT/PC samples; the carbon content and electrical performance after microwave sintering; microwave sintering of Ag/CNT patterns; physical connection between the substrate and sintered Ag lines; touch-piano (figure and movie). See DOI: 10.1039/c5nr08082g

Flash sintering of ceramic materials

NASA Astrophysics Data System (ADS)

Dancer, C. E. J.

2016-10-01

During flash sintering, ceramic materials can sinter to high density in a matter of seconds while subjected to electric field and elevated temperature. This process, which occurs at lower furnace temperatures and in shorter times than both conventional ceramic sintering and field-assisted methods such as spark plasma sintering, has the potential to radically reduce the power consumption required for the densification of ceramic materials. This paper reviews the experimental work on flash sintering methods carried out to date, and compares the properties of the materials obtained to those produced by conventional sintering. The flash sintering process is described for oxides of zirconium, yttrium, aluminium, tin, zinc, and titanium; silicon and boron carbide, zirconium diboride, materials for solid oxide fuel applications, ferroelectric materials, and composite materials. While experimental observations have been made on a wide range of materials, understanding of the underlying mechanisms responsible for the onset and latter stages of flash sintering is still elusive. Elements of the proposed theories to explain the observed behaviour include extensive Joule heating throughout the material causing thermal runaway, arrested by the current limitation in the power supply, and the formation of defect avalanches which rapidly and dramatically increase the sample conductivity. Undoubtedly, the flash sintering process is affected by the electric field strength, furnace temperature and current density limit, but also by microstructural features such as the presence of second phase particles or dopants and the particle size in the starting material. While further experimental work and modelling is still required to attain a full understanding capable of predicting the success of the flash sintering process in different materials, the technique non-etheless holds great potential for exceptional control of the ceramic sintering process.

Tear film measurement by optical reflectometry technique

PubMed Central

Lu, Hui; Wang, Michael R.; Wang, Jianhua; Shen, Meixiao

2014-01-01

Abstract. Evaluation of tear film is performed by an optical reflectometer system with alignment guided by a galvanometer scanner. The reflectometer system utilizes optical fibers to deliver illumination light to the tear film and collect the film reflectance as a function of wavelength. Film thickness is determined by best fitting the reflectance-wavelength curve. The spectral reflectance acquisition time is 15 ms, fast enough for detecting film thickness changes. Fast beam alignment of 1 s is achieved by the galvanometer scanner. The reflectometer was first used to evaluate artificial tear film on a model eye with and without a contact lens. The film thickness and thinning rate have been successfully quantified with the minimum measured thickness of about 0.3 μm. Tear films in human eyes, with and without a contact lens, have also been evaluated. A high-contrast spectral reflectance signal from the precontact lens tear film is clearly observed, and the thinning dynamics have been easily recorded from 3.69 to 1.31 μm with lipid layer thickness variation in the range of 41 to 67 nm. The accuracy of the measurement is better than ±0.58% of the film thickness at an estimated tear film refractive index error of ±0.001. The fiber-based reflectometer system is compact and easy to handle. PMID:24500519

Central macular thickness in patients with type 2 diabetes mellitus without clinical retinopathy.

PubMed

Demir, Mehmet; Oba, Ersin; Dirim, Burcu; Ozdal, Erhan; Can, Efe

2013-04-09

An increase in macular thickness due to fluid accumulation in the macula in patients with diabetes mellitus. Optical coherence tomography (OCT) has been shown to be highly reproducible in measuring macular thickness in normal individuals and diabetic patients. OCT can detect subtle changes of macular thickness. The aim of this study is to compare central macular thickness (CMT) of diabetic patients with type 2 diabetes without clinical retinopathy and normal controls, in order to assess possible increased macular thickness associated with diabetes mellitus. Optical coherence tomography (OCT) measurements were performed in 124 eyes of 62 subjects with diabetes mellitus without clinically retinopathy (study group: 39 female, 23 male, mean age: 55.06 ± 9.77 years) and in 120 eyes of 60 healthy subjects (control group: 35 female, 25 male, mean age: 55.78 ± 10.34 years). Blood biochemistry parameters were analyzed in all cases. The data for central macular thickness (at 1 mm) and the levels of the fasting plasma glucose and glycosylated hemoglobin (HbA1c) were compared in both groups. The mean central macular thickness was 232.12 ±24.41 μm in the study group and 227.19 ± 29.94 μm in the control group.The mean HbA1c level was 8.92 ± 2.58% in the study group and 5.07 ± 0.70% in the control group (p=0.001). No statistically significant relationship was found between CMT, HbA1c, and fasting plasma glucose level in either group (p=0.05). Central macular thickness was not significantly thicker in patients with type 2 diabetes without clinical retinopathy than in healthy subjects.

Processing and Characterization of Porous Ti2AlC with Controlled Porosity and Pore Size

DTIC Science & Technology

2012-09-11

fabricated by spark plasma sintering , were also characterized. The effects of porosity and/or pore size on the room temperature elastic moduli...pressureless- sintered without NaCl pore former, or fabricated by spark plasma sintering , were also characterized. The effects of porosity and/or pore size...as well as several samples sintered using spark plasma sintering (SPS). Furthermore, we demon- strate that the developed methodology can be implemented

Evidence for percolation diffusion of cations and reordering in disordered pyrochlore from accelerated molecular dynamics

DOE PAGES

Perriot, Romain; Uberuaga, Blas P.; Zamora, Richard J.; ...

2017-09-20

Diffusion in complex oxides is critical to ionic transport, radiation damage evolution, sintering, and aging. In complex oxides such as pyrochlores, anionic diffusion is dramatically affected by cation disorder. However, little is known about how disorder influences cation transport. Here, we report results from classical and accelerated molecular dynamics simulations of vacancy-mediated cation diffusion in Gd 2Ti 2O 7 pyrochlore, on the microsecond timescale. We find that diffusion is slow at low levels of disorder, while higher disorder allows for fast diffusion, which is then accompanied by antisite annihilation and reordering, and thus a slowing of cation transport. Cation diffusivitymore » is therefore not constant, but decreases as the material reorders. We also show that fast cation diffusion is triggered by the formation of a percolation network of antisites. This is in contrast with observations from other complex oxides and disordered media models, suggesting a fundamentally different relation between disorder and mass transport.« less

The effect of impurities elements on titanium alloy (Ti-6Al-4V) MIM sintered part properties

NASA Astrophysics Data System (ADS)

Ahmad, M. Azmirruddin; Jabir, M.; Johari, N.; Ibrahim, R.; Hamidi, N.

2017-12-01

The titanium alloys (Ti-6Al-4V) compact were fabricated by Metal Injection Molding (MIM). However, the real challenge of MIM processing for titanium alloy is its affinity to be contaminated by interstitial light elements such as oxygen and carbon which could degrade the mechanical properties of sintered titanium alloy such as its tensile strength and ductility. The sintering temperature effect on carbon and oxygen content that affects its physical and mechanical properties of the sintered titanium alloy was studied. The titanium MIM brown specimen was sintered at four different sintering temperatures which are 1100 °C, 1150 °C, 1200 °C and 1250 °C for 4 hours under furnace control atmosphere. The experimental result indicated that the specimen which has been made from 100% gas atomized powder have a relative density of 92.2 % - 97.6 %, the range of porosity percent around 2.38 %-3.84 %. Ultimate tensile strength of 873.11 MPa - 1007.19 MPa and ductility percent in range of 1.89 %-3.46 %. The titanium alloy MIM specimen which was sintered at 1150 °C contained 0.145 % of carbon and 0.143 % of oxygen possess the highest value of density and tensile strength, with value of 4.344 gcm-3 and 1007.2 MPa respectively. Meanwhile, the titanium alloy MIM specimen which was sintered at 1200 °C contains 0.130 % of carbon and 0.127 % of oxygen, has the highest percentage of ductility with 3.46 %. The carbon content level increased as the sintering temperature increased due to decomposition of high molecule weight of residue binder system which could not be eliminated during solvent extraction debinding process and sintered at low temperature. Contrarily, the oxygen content level indicates a decrease as the sintering temperature increased. Briefly, the sintering temperature could influence the physical and mechanical properties of titanium alloy MIM sintered specimen as it influences the oxygen and carbon content level in the alloys.

Debinding and Sintering of an Injection-Moulded Hypereutectic Al⁻Si Alloy.

PubMed

Ni, Jiaqi; Yu, Muhuo; Han, Keqing

2018-05-16

Hypereutectic Al⁻Si (20 wt.%) alloy parts were fabricated by employing a powder injection moulding (PIM) technique with a developed multi-component binder system composed of high-density polyethylene (35 wt.%), carnauba wax (62 wt.%) and stearic acid (3 wt.%). The feedstocks contained 83 wt.% metal powders. The debinding process was carried out by a combination of solvent extraction and thermal decomposition. The effects of solvent debinding variables such as kind of solvents, debinding temperatures and time, and the bulk surface area to volume ratios on the debinding process were investigated. Thermal debinding and the subsequent sintering process were carried out in a heating sequence under a nitrogen atmosphere. The influences of sintering temperature and sintering time on the mechanical properties and structure were considered. Under the optimal sintering condition, sintering at 550 °C for 3 h, the final sintering parts were free of distortion and exhibited good mechanical properties. Relative sintered density, Brinell hardness, and tensile strength were ~95.5%, 58 HBW and ~154, respectively.

Effect of starting powders on the sintering of nanostructured ZrO2 ceramics by colloidal processing

NASA Astrophysics Data System (ADS)

Suárez, Gustavo; Sakka, Yoshio; Suzuki, Tohru S.; Uchikoshi, Tetsuo; Zhu, Xinwen; Aglietti, Esteban F.

2009-04-01

The effect of starting powders on the sintering of nanostructured tetragonal zirconia was evaluated. Suspensions were prepared with a concentration of 10 vol.% by mixing a bicomponent mixture of commercial powders (97 mol.% monoclinic zirconia with 3 mol.% yttria) and by dispersing commercially available tetragonal zirconia (3YTZ, Tosoh). The preparation of the slurry by bead-milling was optimized. Colloidal processing using 50 μm zirconia beads at 4000 rpm generated a fully deagglomerated suspension leading to the formation of high-density consolidated compacts (62% of the theoretical density (TD) for the bicomponent suspension). Optimum colloidal processing of the bicomponent suspension followed by the sintering of yttria and zirconia allowed us to obtain nanostructured tetragonal zirconia. Three different sintering techniques were investigated: normal sintering, two-step sintering and spark plasma sintering. The inhibition of grain growth in the bicomponent mixed powders in comparison with 3YTZ was demonstrated. The inhibition of the grain growth may have been caused by inter-diffusion of cations during the sintering.

Borax as flux on sintering of iron Ancor Steel 1000® under glow discharge

NASA Astrophysics Data System (ADS)

Ariza Suarez, H. G.; Sarmiento Santos, A.; Ortiz Otálora, C. A.

2016-02-01

This work studies the flux effect of borax (di sodium tetraborate decahydrate) on sintering of iron Ancor Steel 1000® in abnormal glow discharge. The incidence of the percentage by weight of borax and the sintering temperature in the process were observed. Samples of powder metallurgical iron were prepared with proportions of 0.50%, 2.0%, 4.0% and 6.0% by weight of borax using the procedures of powder metallurgy. The samples were sintered at 800 and 1100°C for 30min, by glow discharge at low pressure in a reducing atmosphere composed of 20% H2+80% Ar. The samples in compact green-state were analyzed by TGA-DSC to determine the fusion process and mass loss during sintering. The analysis of microhardness and density, shows that at a sintering temperature of 800°C the sample density decreases and the sample microhardness increases with respect to sintered samples without borax. Sintered samples were analysed by DRX showing the absence of precipitates.

Chemical Sintering Generates Uniform Porous Hyaluronic Acid Hydrogels

PubMed Central

Cam, Cynthia; Segura, Tatiana

2014-01-01

Implantation of scaffolds for tissue repair has been met with limited success primarily due to the inability to achieve vascularization within the construct. Many strategies have shifted to incorporate pores into these scaffolds to encourage rapid cellular infiltration and subsequent vascular ingrowth. We utilized an efficient chemical sintering technique to create a uniform network of polymethyl methacrylate (PMMA) microspheres for porous hyaluronic acid hydrogel formation. The porous hydrogels generated from chemical sintering possessed comparable pore uniformity and interconnectivity as the commonly used non- and heat sintering techniques. Moreover, similar cell response to the porous hydrogels generated from each sintering approach was observed in cell viability, spreading, proliferation in vitro, as well as, cellular invasion in vivo. We propose chemical sintering of PMMA microspheres using a dilute acetone solution as an alternative method to generating porous hyaluronic acid hydrogels since it requires equal or ten-fold less processing time as the currently used non-sintering or heat sintering technique, respectively. PMID:24120847

Microwave processing of a dental ceramic used in computer-aided design/computer-aided manufacturing.

PubMed

Pendola, Martin; Saha, Subrata

2015-01-01

Because of their favorable mechanical properties and natural esthetics, ceramics are widely used in restorative dentistry. The conventional ceramic sintering process required for their use is usually slow, however, and the equipment has an elevated energy consumption. Sintering processes that use microwaves have several advantages compared to regular sintering: shorter processing times, lower energy consumption, and the capacity for volumetric heating. The objective of this study was to test the mechanical properties of a dental ceramic used in computer-aided design/computer-aided manufacturing (CAD/CAM) after the specimens were processed with microwave hybrid sintering. Density, hardness, and bending strength were measured. When ceramic specimens were sintered with microwaves, the processing times were reduced and protocols were simplified. Hardness was improved almost 20% compared to regular sintering, and flexural strength measurements suggested that specimens were approximately 50% stronger than specimens sintered in a conventional system. Microwave hybrid sintering may preserve or improve the mechanical properties of dental ceramics designed for CAD/CAM processing systems, reducing processing and waiting times.

The Effects of Atmosphere on the Sintering of Ultrafine-Grained Tungsten with Ti

NASA Astrophysics Data System (ADS)

Ren, Chai; Koopman, Mark; Fang, Z. Zak; Zhang, Huan

2016-11-01

Tungsten (W) is a brittle material at room temperature making it very difficult to fabricate. Although the lack of ductility remains a difficult challenge, nano-sized and ultrafine-grained (UFG) structures offer the potential to overcome tungsten's room-temperature brittleness. One way to manufacture UFG W is to compact and sinter nano-sized W powder. It is challenging, however, to control grain growth during sintering. As one method to inhibit grain growth, the effect of Ti-based additives on the densification and grain growth of nano-W powders was investigated in this study. Addition of 1% Ti into tungsten led to more than a 63% decrease in average grain size of sintered samples at comparable density levels. It was found that sintering in Ar yielded a finer grain size than sintering in H2 at similar densities. The active diffusion mechanisms during sintering were different for W-1% Ti nano powders sintered in Ar and H2.

EFFECT OF MICROWAVE SINTERING ON THE STRUCTURAL AND ELECTRICAL PROPERTIES OF Li0.51Zn0.2Ti0.2V0.01Fe2.08O4 FERRITE

NASA Astrophysics Data System (ADS)

Maisnam, Mamata; Phanjoubam, Sumitra

2013-07-01

Effect of microwave sintering on the structural and electrical properties of Li+0.51Zn2+0.2Ti4+0.2V5+0.01Fe3+2.08O2-4 is studied in comparison with that of conventionally sintered one. The technique is advantageous in terms of significantly reduced size of microwave kilns and rapid heating compared to the cumbersome and slow heating of conventional sintering technology. Microwave sintering produced enhanced densification and much finer microstructures. The DC resistivity is markedly increased. Microwave sintering reduces chances of evaporation of lithium and oxygen during sintering of lithium based ferrites resulting in formation of lesser ferrous ions. This has profound effect on the electrical properties of microwave sintered ferrites. The dielectric constant is significantly reduced possibly due to reduced space charge polarization and the temperature dependence of the dielectric properties are also studied.

Improved microstructure and thermoelectric properties of iodine doped indium selenide as a function of sintering temperature

NASA Astrophysics Data System (ADS)

Dhama, Pallavi; Kumar, Aparabal; Banerji, P.

2018-04-01

In this paper, we explored the effect of sintering temperature on the microstructure, thermal and electrical properties of iodine doped indium selenide in the temperature range 300 - 700 K. Samples were prepared by a collaborative process of vacuum melting, ball milling and spark plasma sintering at 570 K, 630 K and 690 K. Single phase samples were obtained at higher sintering temperature as InSe is stable only at lower temperature. With increasing sintering temperature, densities of the samples were found to improve with larger grain size formation. Negative values of Seebeck coefficient were observed which indicates n-type carrier transport. Seebeck coefficient increases with sintering temperature and found to be the highest for the sample sintered at 690 K. Thermal conductivity found to be lower in the samples sintered at lower temperatures. The maximum thermoelectric figure of merit found to be ˜ 1 at 700 K due to the enhanced power factor as a result of improved microstructure.

Reduction of FeO contents in sinter under high bed operation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fujii, K.; Hazama, K.; Hoshikuma, Y.

1996-12-31

High-bed operation (bed height more than 700 mm) is currently being carried out at the Kure No. 1 sintering plant. Before initiating this high-bed operation, the authors conducted sinter pot tests at various bed heights to investigate the effect of bed height on sintering. The following results were obtained from these pot tests: Heightening of the sinter bed increased yield at the upper layer, but at the lower layer, the yield reached a maximum value at a certain bed height. From observation of the sinter cakes, the reduction in yield is attributed to uneven burn caused by surplus heat atmore » the lower layers. Therefore, when high-bed operation is carried out, reduction of the burning energy (reduction of the FeO content in the sinter) is required. This high-bed operation with lower FeO content has enabled the company to reduce fuel consumption and SiO{sub 2} content, while maintaining high yield and high sinter quality.« less

Manufacture of sintered silicon nitrides

NASA Technical Reports Server (NTRS)

Iwai, T.

1985-01-01

Sintered silicon nitrides are manufactured by sintering Si3N powder containing 2 to 15% in wt of a powder mixture composed of nitride powder of lanthanide or Y 100 parts and AIN powder less than 100 parts at 1500 to 1900 deg. temperature under a pressure of less than 200 Kg/sq. cm. The sintered Si3N has high mechanical strength in high temperature. Thus, Si3N4 93.0, Y 5.0 and AlN 2.0% in weight were wet mixed in acetone in N atom, molded and sintered at 1750 deg. and 1000 Kg/sq. cm. to give a sintered body having high hardness.

Enhanced Densification and Hardness of Titanium Bodies Sintered by Advanced Hydrogen Sintering Process

NASA Astrophysics Data System (ADS)

Oh, Jung-Min; Koo, Ja-Geon; Lim, Jae-Won

2018-05-01

A new sintering technique for enhancing a densification and hardness of sintered titanium body by supplying hydrogen was developed (Hydrogen Sintering Process, HSP). The HSP was developed by only injecting hydrogen into an argon atmosphere during the core time. As a result, sound titanium sintered bodies with high density and hardness were obtained by the HSP. In addition, a pore size and number of the HSP specimens were smaller than those of the argon atmosphere specimen. It was found that the injecting hydrogen into the argon atmosphere by HSP can prevent the formation of oxide layers, resulting in enhanced densification and hardness.

Rapid sintering of anisotropic, nanograined Nd-Fe-B by flash-spark plasma sintering

NASA Astrophysics Data System (ADS)

Castle, Elinor; Sheridan, Richard; Grasso, Salvatore; Walton, Allan; Reece, Mike

2016-11-01

A Spark Plasma Sintering (SPS) furnace was used to Flash-Sinter (FS) Nd-Fe-Dy-Co-B-Ga melt spun permanent magnetic material. During the 10 s "Flash" process (heating rate 2660 K min-1), sample sintering (to theoretical density) and deformation (54% height reduction) occurred. This produced texturing and significant magnetic anisotropy, comparable to conventional die-upset magnets; yet with much greater coercivities (>1600 kA m-1) due to the nanoscale characteristics of the plate-like sintered grains. These preliminary results suggest that Flash-SPS could provide a new processing route for the mass production of highly anisotropic, nanocrystalline magnetic materials with high coercivity.

Solvent/non-solvent sintering: a novel route to create porous microsphere scaffolds for tissue regeneration.

PubMed

Brown, Justin L; Nair, Lakshmi S; Laurencin, Cato T

2008-08-01

Solvent/non-solvent sintering creates porous polymeric microsphere scaffolds suitable for tissue engineering purposes with control over the resulting porosity, average pore diameter, and mechanical properties. Five different biodegradable biocompatible polyphosphazenes exhibiting glass transition temperatures from -8 to 41 degrees C and poly (lactide-co-glycolide), (PLAGA) a degradable polymer used in a number of biomedical settings, were examined to study the versatility of the process and benchmark the process to heat sintering. Parameters such as: solvent/non-solvent sintering solution composition and submersion time effect the sintering process. PLAGA microsphere scaffolds fabricated with solvent/non-solvent sintering exhibited an interconnected porosity and pore size of 31.9% and 179.1 mum, respectively which was analogous to that of conventional heat sintered PLAGA microsphere scaffolds. Biodegradable polyphosphazene microsphere scaffolds exhibited a maximum interconnected porosity of 37.6% and a maximum compressive modulus of 94.3 MPa. Solvent/non-solvent sintering is an effective strategy for sintering polymeric microspheres, with a broad spectrum of glass transition temperatures, under ambient conditions making it an excellent fabrication route for developing tissue engineering scaffolds and drug delivery vehicles. (c) 2007 Wiley Periodicals, Inc.

Solvent/Non-Solvent Sintering: A Novel Route to Create Porous Microsphere Scaffolds For Tissue Regeneration

PubMed Central

Brown, Justin L.; Nair, Lakshmi S.; Laurencin, Cato T.

2009-01-01

Solvent/non-solvent sintering creates porous polymeric microsphere scaffolds suitable for tissue engineering purposes with control over the resulting porosity, average pore diameter and mechanical properties. Five different biodegradable biocompatible polyphosphazenes exhibiting glass transition temperatures from −8°C to 41oC and poly(lactide-co-glycolide), (PLAGA) a degradable polymer used in a number of biomedical settings, were examined to study the versatility of the process and benchmark the process to heat sintering. Parameters such as: solvent/non-solvent sintering solution composition and submersion time effect the sintering process. PLAGA microsphere scaffolds fabricated with solvent/non-solvent sintering exhibited an interconnected porosity and pore size of 31.9% and 179.1µm respectively which was analogous to that of conventional heat sintered PLAGA microsphere scaffolds. Biodegradable polyphosphazene microsphere scaffolds exhibited a maximum interconnected porosity of 37.6% and a maximum compressive modulus of 94.3MPa. Solvent/non-solvent sintering is an effective strategy for sintering polymeric microspheres, with a broad spectrum of glass transition temperatures, under ambient conditions making it an excellent fabrication route for developing tissue engineering scaffolds and drug delivery vehicles. PMID:18161819

An Investigation of Sintering Parameters on Titanium Powder for Electron Beam Melting Processing Optimization.

PubMed

Drescher, Philipp; Sarhan, Mohamed; Seitz, Hermann

2016-12-01

Selective electron beam melting (SEBM) is a relatively new additive manufacturing technology for metallic materials. Specific to this technology is the sintering of the metal powder prior to the melting process. The sintering process has disadvantages for post-processing. The post-processing of parts produced by SEBM typically involves the removal of semi-sintered powder through the use of a powder blasting system. Furthermore, the sintering of large areas before melting decreases productivity. Current investigations are aimed at improving the sintering process in order to achieve better productivity, geometric accuracy, and resolution. In this study, the focus lies on the modification of the sintering process. In order to investigate and improve the sintering process, highly porous titanium test specimens with various scan speeds were built. The aim of this study was to decrease build time with comparable mechanical properties of the components and to remove the residual powder more easily after a build. By only sintering the area in which the melt pool for the components is created, an average productivity improvement of approx. 20% was achieved. Tensile tests were carried out, and the measured mechanical properties show comparatively or slightly improved values compared with the reference.

Deuteron irradiation of W and WO 3 for production of high specific activity 186Re: Challenges associated with thick target preparation

DOE PAGES

Balkin, Ethan R.; Gagnon, Katherine; Strong, Kevin T.; ...

2016-06-28

This investigation evaluated target fabrication and beam parameters for scale-up production of high specific activity 186Re using deuteron irradiation of enriched 186W via the 186W(d,2n) 186Re reaction. Thick W and WO 3 targets were prepared, characterized and evaluated in deuteron irradiations. Full-thickness targets, as determined using SRIM, were prepared by uniaxi-ally pressing powdered natural abundance W and WO 3, or 96.86% enriched 186W, into Al target supports. Alternatively, thick targets were prepared by pressing 186W between two layers of graphite powder or by placing pre-sintered (1105°C, 12 hours) natural abundance WO 3 pellets into an Al target support. Assessments ofmore » structural integrity were made on each target pre-pared. Prior to irradiation, material composition analyses were conducted using SEM, XRD, and Raman spectroscopy. With-in a minimum of 24 hours post irradiation, gamma-ray spectroscopy was performed on all targets to assess production yields and radionuclidic byproducts. Problems were encountered with the structural integrity of some pressed W and WO 3 pellets before and during irradiation, and target material characterization results could be correlated with the structural integrity of the pressed target pellets. Under the conditions studied, the findings suggest that all WO 3 targets prepared and studied were unacceptable. By contrast, 186W metal was found to be a viable target material for 186Re production. Lastly, thick targets prepared with powdered 186W pressed between layers of graphite provided a particularly robust target configuration.« less

Deuteron irradiation of W and WO3 for production of high specific activity (186)Re: Challenges associated with thick target preparation.

PubMed

Balkin, Ethan R; Gagnon, Katherine; Strong, Kevin T; Smith, Bennett E; Dorman, Eric F; Emery, Robert C; Pauzauskie, Peter J; Fassbender, Michael E; Cutler, Cathy S; Ketring, Alan R; Jurisson, Silvia S; Wilbur, D Scott

2016-09-01

This investigation evaluated target fabrication and beam parameters for scale-up production of high specific activity (186)Re using deuteron irradiation of enriched (186)W via the (186)W(d,2n)(186)Re reaction. Thick W and WO3 targets were prepared, characterized and evaluated in deuteron irradiations. Full-thickness targets, as determined using SRIM, were prepared by uniaxially pressing powdered natural abundance W and WO3, or 96.86% enriched (186)W, into Al target supports. Alternatively, thick targets were prepared by pressing (186)W between two layers of graphite powder or by placing pre-sintered (1105°C, 12h) natural abundance WO3 pellets into an Al target support. Assessments of structural integrity were made on each target prepared. Prior to irradiation, material composition analyses were conducted using SEM, XRD, and Raman spectroscopy. Within a minimum of 24h post irradiation, gamma-ray spectroscopy was performed on all targets to assess production yields and radionuclidic byproducts. Problems were encountered with the structural integrity of some pressed W and WO3 pellets before and during irradiation, and target material characterization results could be correlated with the structural integrity of the pressed target pellets. Under the conditions studied, the findings suggest that all WO3 targets prepared and studied were unacceptable. By contrast, (186)W metal was found to be a viable target material for (186)Re production. Thick targets prepared with powdered (186)W pressed between layers of graphite provided a particularly robust target configuration. Copyright © 2016 Elsevier Ltd. All rights reserved.

Influence of Basicity on High-Chromium Vanadium-Titanium Magnetite Sinter Properties, Productivity, and Mineralogy

NASA Astrophysics Data System (ADS)

Zhou, Mi; Yang, Songtao; Jiang, Tao; Xue, Xiangxin

2015-05-01

The effect of basicity on high-chromium vanadium-titanium magnetite (V-Ti-Cr) sintering was studied via sintering pot tests. The sinter rate, yield, and productivity were calculated before determining sinter strength (TI) and reduction degradation index (RDI). Furthermore, the effect of basicity on V-Ti-Cr sinter mineralogy was clarified using metallographic microscopy, x-ray diffraction, and scanning electron microscopy-energy-dispersive x-ray spectroscopy. The results indicate that increasing basicity quickly increases the sintering rate from 25.4 mm min-1 to 28.9 mm min-1, yield from 75.3% to 87.2%, TI from 55.4% to 64.8%, and productivity from 1.83 t (m2 h)-1 to 1.94 t (m2 h)-1 before experiencing a slight drop. The V-Ti-Cr sinter shows complex mineral composition, with main mineral phases such as magnetite, hematite, silicate (dicalcium silicate, Ca-Fe olivine, glass), calcium and aluminum silico-ferrite (SFCA/SFCAI) and perovskite. Perovskite is notable because it lowers the V-Ti sinter strength and RDI. The well intergrowths between magnetite and SFCA/SFCAI, and the decrease in perovskite and secondary skeletal hematite are the key for improving TI and RDI. Finally, a comprehensive index was calculated, and the optimal V-Ti-Cr sinter basicity also for industrial application was 2.55.

An Arrhenius-type viscosity function to model sintering using the Skorohod Olevsky viscous sintering model within a finite element code.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ewsuk, Kevin Gregory; Arguello, Jose Guadalupe, Jr.; Reiterer, Markus W.

2006-02-01

The ease and ability to predict sintering shrinkage and densification with the Skorohod-Olevsky viscous sintering (SOVS) model within a finite-element (FE) code have been improved with the use of an Arrhenius-type viscosity function. The need for a better viscosity function was identified by evaluating SOVS model predictions made using a previously published polynomial viscosity function. Predictions made using the original, polynomial viscosity function do not accurately reflect experimentally observed sintering behavior. To more easily and better predict sintering behavior using FE simulations, a thermally activated viscosity function based on creep theory was used with the SOVS model. In comparison withmore » the polynomial viscosity function, SOVS model predictions made using the Arrhenius-type viscosity function are more representative of experimentally observed viscosity and sintering behavior. Additionally, the effects of changes in heating rate on densification can easily be predicted with the Arrhenius-type viscosity function. Another attribute of the Arrhenius-type viscosity function is that it provides the potential to link different sintering models. For example, the apparent activation energy, Q, for densification used in the construction of the master sintering curve for a low-temperature cofire ceramic dielectric has been used as the apparent activation energy for material flow in the Arrhenius-type viscosity function to predict heating rate-dependent sintering behavior using the SOVS model.« less

SEM and TEM characterization of microstructure of stainless steel composites reinforced with TiB{sub 2}

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sulima, Iwona, E-mail: isulima@up.krakow.pl

Steel-8TiB{sub 2} composites were produced by two new sintering techniques, i.e. Spark Plasma Sintering (SPS) and High Pressure-High Temperature (HP-HT) sintering. This study discusses the impact of these sintering methods on the microstructure of steel composites reinforced with TiB{sub 2} particles. Scanning electron microscopy (SEM), wavelength dispersive spectroscopy (WDS), X-ray diffraction, electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) were used to analyze the microstructure evolution in steel matrix composites. The results of microscopic examinations revealed a close relationship between the composite microstructure and the methods and conditions of sintering. Substantial differences were observed in the grain size ofmore » materials sintered by HP-HT and SPS. It has been demonstrated that the composites sintered by HP-HT tend to form a chromium-iron-nickel phase in the steel matrix. In contrast, the microstructure of the composites sintered by SPS is characterized by the presence of complex borides and chromium-iron phase. - Highlights: •The steel-8TiB{sub 2} composites were fabricated by Spark Plasma Sintering (SPS) and High Pressure-High Temperature (HP-HT). •Sintering techniques has an important effect on changes in the microstructure of steel-8TiB{sub 2} composites. •New phases of different size and morphology were identified.« less

Sintering of Lead-Free Piezoelectric Sodium Potassium Niobate Ceramics

PubMed Central

Malič, Barbara; Koruza, Jurij; Hreščak, Jitka; Bernard, Janez; Wang, Ke; Fisher, John G.; Benčan, Andreja

2015-01-01

The potassium sodium niobate, K0.5Na0.5NbO3, solid solution (KNN) is considered as one of the most promising, environment-friendly, lead-free candidates to replace highly efficient, lead-based piezoelectrics. Since the first reports of KNN, it has been recognized that obtaining phase-pure materials with a high density and a uniform, fine-grained microstructure is a major challenge. For this reason the present paper reviews the different methods for consolidating KNN ceramics. The difficulties involved in the solid-state synthesis of KNN powder, i.e., obtaining phase purity, the stoichiometry of the perovskite phase, and the chemical homogeneity, are discussed. The solid-state sintering of stoichiometric KNN is characterized by poor densification and an extremely narrow sintering-temperature range, which is close to the solidus temperature. A study of the initial sintering stage revealed that coarsening of the microstructure without densification contributes to a reduction of the driving force for sintering. The influences of the (K + Na)/Nb molar ratio, the presence of a liquid phase, chemical modifications (doping, complex solid solutions) and different atmospheres (i.e., defect chemistry) on the sintering are discussed. Special sintering techniques, such as pressure-assisted sintering and spark-plasma sintering, can be effective methods for enhancing the density of KNN ceramics. The sintering behavior of KNN is compared to that of a representative piezoelectric lead zirconate titanate (PZT). PMID:28793702

Effect of temperature on porosity of iron ore sinter with biochar derived from EFB

NASA Astrophysics Data System (ADS)

Purwanto, H.; Rozhan, A. N.; Zakiyuddin, A.; Mohamad, A. S.

2018-01-01

In this research, the replacement of fossil fuel energy (coke) with oil palm empty fruit bunch as a potential energy in sintering of iron ore was investigated. Carbon derived biomass has been produced by using oil palm empty fruit bunch by heat treatment process. In the present investigation, sintering process was carried out by heating the mixed iron ore and biochar at various temperatures. The apparent density and porosity for iron sinter show a significant increase and gradual decrement as the temperature increase, respectively. The porosity of iron sinter shows a gradual decrement from 950 °C to 1050 °C but up to 1150 °C it shows a significant decrement about 44%. Inferring to the micrograph, the agglomeration and assimilation of sinter at high temperature is better compared with low sintering temperature.

The physical chemistry and materials science behind sinter-resistant catalysts.

PubMed

Dai, Yunqian; Lu, Ping; Cao, Zhenming; Campbell, Charles T; Xia, Younan

2018-06-18

Catalyst sintering, a main cause of the loss of catalytic activity and/or selectivity at high reaction temperatures, is a major concern and grand challenge in the general area of heterogeneous catalysis. Although all heterogeneous catalysts are inevitably subjected to sintering during their operation, the immediate and drastic consequences can be mitigated by carefully engineering the catalytic particles and their interactions with the supports. In this tutorial review, we highlight recent progress in understanding the physical chemistry and materials science involved in sintering, including the discussion of advanced techniques, such as in situ microscopy and spectroscopy, for investigating the sintering process and its rate. We also discuss strategies for the design and rational fabrication of sinter-resistant catalysts. Finally, we showcase recent success in improving the thermal stability and thus sinter resistance of supported catalytic systems.

Mechanical parameters of strontium doped hydroxyapatite sintered using microwave and conventional methods.

PubMed

Curran, Declan J; Fleming, Thomas J; Towler, Mark R; Hampshire, Stuart

2011-11-01

The effects of ion substitution in hydroxyapatite (HA) on crystal structure and lattice stability is investigated in the green state and post sintering. The effects of ion incorporation on the biaxial flexural strength and hardness are also investigated. Sintering is carried out at 1200 °C using comparative conventional and microwave regimes. Post sintering, the effects of ion incorporation manifest as an increase in the lattice d-spacings and a reduction of the crystallite size. Some HA decomposition occurs with β-TCP stabilisation in conventional sintering (CS), but this phase is destabilised during microwave sintering (MS), generating α-TCP. Conventional sintering (CS) allows higher densification in the undoped samples. Overall, for the Sr-doped compositions, the MS samples retain higher amounts of HA and experience higher density levels compared to the CS samples. Published by Elsevier Ltd.

Lanthanide (Nd, Gd) compounds with garnet and monazite structures. Powders synthesis by "wet" chemistry to sintering ceramics by Spark Plasma Sintering

NASA Astrophysics Data System (ADS)

Potanina, Ekaterina; Golovkina, Ludmila; Orlova, Albina; Nokhrin, Aleksey; Boldin, Maksim; Sakharov, Nikita

2016-05-01

Complex oxide Y2.5Nd0.5Al5O12 with garnet structure and phosphates NdPO4 and GdPO4 with monazite structure were obtained by using precipitation methods. Ceramics Y2.5Nd0.5Al5O12 and NdPO4 were processed by Spark Plasma Sintering (SPS). Relative density more 98%, sintering time did not exceed 8 min, sintering temperature 1330-1390 °C. Leaching rates of elements from ceramics were 10-6-10-7 g/(cm2 d). The process of ceramics sintering has two-stage character: the first step of sintering-compaction process is related to the plastic flow of the material, the second step-to the process of grain boundary diffusion and grain growth.

Dye-sensitized solar cells using laser processing techniques

NASA Astrophysics Data System (ADS)

Kim, Heungsoo; Pique, Alberto; Kushto, Gary P.; Auyeung, Raymond C. Y.; Lee, S. H.; Arnold, Craig B.; Kafafi, Zakia H.

2004-07-01

Laser processing techniques, such as laser direct-write (LDW) and laser sintering, have been used to deposit mesoporous nanocrystalline TiO2 (nc-TiO2) films for use in dye-sensitized solar cells. LDW enables the fabrication of conformal structures containing metals, ceramics, polymers and composites on rigid and flexible substrates without the use of masks or additional patterning techniques. The transferred material maintains a porous, high surface area structure that is ideally suited for dye-sensitized solar cells. In this experiment, a pulsed UV laser (355nm) is used to forward transfer a paste of commercial TiO2 nanopowder (P25) onto transparent conducting electrodes on flexible polyethyleneterephthalate (PET) and rigid glass substrates. For the cells based on flexible PET substrates, the transferred TiO2 layers were sintered using an in-situ laser to improve electron paths without damaging PET substrates. In this paper, we demonstrate the use of laser processing techniques to produce nc-TiO2 films (~10 μm thickness) on glass for use in dye-sensitized solar cells (Voc = 690 mV, Jsc = 8.7 mA/cm2, ff = 0.67, η = 4.0 % at 100 mW/cm2). This work was supported by the Office of Naval Research.

Fabrication of Multilayer-Type Mn-Si Thermoelectric Device

NASA Astrophysics Data System (ADS)

Kajitani, T.; Ueno, T.; Miyazaki, Y.; Hayashi, K.; Fujiwara, T.; Ihara, R.; Nakamura, T.; Takakura, M.

2014-06-01

This research aims to develop a direct-contact manganese silicon p/ n multilayer-type thermoelectric power generation block. p-type MnSi1.74 and n-type Mn0.7Fe0.3Si1.68 ball-milled powders with diameter of about 10 μm or less were mixed with polyvinyl butyl alcohol diluted with methylbenzene at pigment volume concentration of approximately 70%. The doctor-blade method produced 45- μm-thick p- and n-type pigment plates. The insulator, i.e., powdered glass, was mixed with cellulose to form insulator slurry. Lamination of manganese silicide pigment layers and screen-printed insulator layers was carried out to fabricate multilayer direct-contact thermoelectric devices. Hot pressing and spark plasma sintering were carried out at 450°C and 900°C, respectively. Four to 30 thermoelectric (TE) p/ n pairs were fabricated in a 10 mm × 10 mm × 10 mm sintered TE block. The maximum output was 11.7 mW/cm2 at a temperature difference between 20°C and 700°C, which was about 1/85 of the ideal power generation estimated from the thermoelectric data of the bulk MnSi1.74 and Mn0.7Fe0.3Si1.68 materials. A power generation test using an engine test bench was also carried out.

Optimization of sound absorbing performance for gradient multi-layer-assembled sintered fibrous absorbers

NASA Astrophysics Data System (ADS)

Zhang, Bo; Zhang, Weiyong; Zhu, Jian

2012-04-01

The transfer matrix method, based on plane wave theory, of multi-layer equivalent fluid is employed to evaluate the sound absorbing properties of two-layer-assembled and three-layer-assembled sintered fibrous sheets (generally regarded as a kind of compound absorber or structures). Two objective functions which are more suitable for the optimization of sound absorption properties of multi-layer absorbers within the wider frequency ranges are developed and the optimized results of using two objective functions are also compared with each other. It is found that using the two objective functions, especially the second one, may be more helpful to exert the sound absorbing properties of absorbers at lower frequencies to the best of their abilities. Then the calculation and optimization of sound absorption properties of multi-layer-assembled structures are performed by developing a simulated annealing genetic arithmetic program and using above-mentioned objective functions. Finally, based on the optimization in this work the thoughts of the gradient design over the acoustic parameters- the porosity, the tortuosity, the viscous and thermal characteristic lengths and the thickness of each samples- of porous metals are put forth and thereby some useful design criteria upon the acoustic parameters of each layer of porous fibrous metals are given while applying the multi-layer-assembled compound absorbers in noise control engineering.

Synthesis of functional ceramic supports by ice templating and atomic layer deposition

NASA Astrophysics Data System (ADS)

Klotz, Michaela; Weber, Matthieu; Deville, Sylvain; Oison, Didier; Iatsunskyi, Igor; Coy, Emerson; Bechelany, Mikhael

2018-05-01

In this work, we report an innovative route for the manufacturing of functional ceramic supports, by combining ice templating of yttria stabilized zirconia (YSZ) and atomic layer deposition (ALD) of Al2O3 processes. Ceramic YSZ monoliths are prepared using the ice-templating process, which is based on the controlled crystallization of water following a thermal gradient. Sublimation of the ice and the sintering of the material reveal the straight micrometer sized pores shaped by the ice crystal growth. The high temperature sintering allows for the ceramic materials to present excellent mechanical strength and porosities of 67%. Next, the conformality benefit of ALD is used to deposit an alumina coating at the surface of the YSZ pores, in order to obtain a functional material. The Al2O3 thin films obtained by ALD are 100 nm thick and conformally deposited within the macroporous ceramic supports, as shown by SEM and EDS analysis. Mercury intrusion experiments revealed a reduction of the entrance pore diameter, in line with the growth per cycle of 2 Å of the ALD process. In addition to the manufacture of the innovative ceramic nanomaterials, this article also describes the fine characterization of the coatings obtained using mercury intrusion, SEM and XRD analysis.

High-performance electrodes for reduced temperature solid oxide fuel cells with doped lanthanum gallate electrolyte. II. La(Sr)CoO 3 cathode

NASA Astrophysics Data System (ADS)

Inagaki, Toru; Miura, Kazuhiro; Yoshida, Hiroyuki; Maric, Radenka; Ohara, Satoshi; Zhang, Xinge; Mukai, Kazuo; Fukui, Takehisa

The reduced temperature solid oxide fuel cell (SOFC) with 0.5 mm thick La 0.9Sr 0.1Ga 0.8Mg 0.2O 3- α (LSGM) electrolyte, La 0.6Sr 0.4CoO 3- δ (LSCo) cathode, and Ni-(CeO 2) 0.8(SmO 1.5) 0.2 (SDC) cermet anode showed an excellent initial performance, and high maximum power density, 0.47 W/cm 2, at 800°C. The results were comparable to those for the conventional SOFC with yttria-stabilized zirconia (YSZ) electrolyte, La(Sr)MnO 3-YSZ cathode and Ni-YSZ cermet anode at 1000°C. Using an LSCo powder prepared by spray pyrolysis, and selecting appropriate sintering temperatures, the lowest cathodic polarization of about 25 mV at 300 mA/cm 2 was measured for a cathode prepared by sintering at 1000°C. Life time cell test results, however, showed that the polarization of the LSCo cathode increased with operating time. From EPMA results, this behavior was considered to be related to the interdiffusion of the elements at the cathode/electrolyte interface. Calcination of LSCo powder could be a possible way to suppress this interdiffusion at the interface.

Manufacturing of PZT-nickel functionally graded piezoelectric ceramics

NASA Astrophysics Data System (ADS)

Rubio, Wilfredo M.; Silva, Emílio C. N.; Buiochi, Flávio

2012-05-01

A recent approach for designing and manufacturing piezoelectric ceramics consists of using the functionally graded materials (FGM) concept. In this work, nickel (Ni) is used to generate a new PZT-Ni graded ceramic and its dynamic behavior is experimentally explored. The PZT-Ni graded ceramic is manufactured by using the technique of Spark Plasma Sintering (SPS). The ceramic is graded from the top to the bottom surface (along 6 mm of thickness). Specifically, five layers of green powders are sintered: 100 wt% PZT-5A, 90 wt% PZT-5A and 10 wt% Ni, 80 wt% PZT-5A and 20 wt% Ni, 70 wt% PZT-5A and 30 wt% Ni, 60 wt% PZT-5A and 40 wt% Ni. Thus, Ni is used as a second phase, which is added to a PZT-5A matrix, changing its concentration. No manufacturing defects or cracks or exfoliated layers are observed. However, graphite diffusion is observed from the graphite die into the graded ceramic, which does not affect its performance; hence, the ceramic contains enough piezoelectric properties, which allows its polarization and dynamic characterization by determining the impedance curve of the PZT-Ni graded ceramic. The PZT-Ni graded ceramic vibrates at 1.04 MHz, 1.55 MHz and 2.07 MHz.

[Preparation and chromaticity properties of colored dental 3Y-TZP ceramics].

PubMed

Yi, Yuan-fu; Wang, Chen; Tian, Jie-mo; Liu, Hong-chen; Wen, Ning

2008-10-01

To obtain and investigate the chromaticity properties of colored dental 3Y-TZP ceramics with different colorant combinations. Colorant combinations were mixed with TZ-3Y-S powder, then the mixtures were compacted at 200 MPa using cold isostatic pressure, densely sintered at 1500 degrees C for 2 h forming 5 graded colored dental zirconia ceramics. Specimen were sectioned into 10 mm x 10 mm x 0.5 mm and 10 mm x l0 mmx 1 mm slices from the sintered blocks. Color measurement was performed under black background using spectrophotometer. The chromaticity properties were compared with that of the VITA In-Ceram YZ shade guide. Five colored dental zirconia ceramics were obtained. The lightness decreased gradually, and the chroma value increased gradually. The color differences of the two thickness specimens were little. The parameters of the color space were L*: 67.76-77.78; a*: -2.19-3.80; b*: 12.13-25.01, which was similar with that of the VITA In-Ceram YZ shade guide, while the lowest value of lightness was relatively higher than that of the VITA In-Ceram YZ shade guide. Colored 3Y-TZP dental ceramics are suitable for clinical use. There is a need to develop more darkness shaded zirconia dental ceramics.

Low-energy plasma-cathode electron gun with a perforated emission electrode

NASA Astrophysics Data System (ADS)

Burdovitsin, Victor; Kazakov, Andrey; Medovnik, Alexander; Oks, Efim; Tyunkov, Andrey

2017-11-01

We describe research of influence of the geometric parameters of perforated electrode on emission parameters of a plasma cathode electron gun generating continuous electron beams at gas pressure 5-6 Pa. It is shown, that the emission current increases with increasing the hole diameters and decreasing the thickness of the perforated emission electrode. Plasma-cathode gun with perforated electron can provide electron extraction with an efficiency of up to 72 %. It is shown, that the current-voltage characteristic of the electron gun with a perforated emission electrode differs from that of similar guns with fine mesh grid electrode. The plasma-cathode electron gun with perforated emission electrode is used for electron beam welding and sintering.

Dielectric breakdown of additively manufactured polymeric materials

DOE PAGES

Monzel, W. Jacob; Hoff, Brad W.; Maestas, Sabrina S.; ...

2016-01-11

Dielectric strength testing of selected Polyjet-printed polymer plastics was performed in accordance with ASTM D149. This dielectric strength data is compared to manufacturer-provided dielectric strength data for selected plastics printed using the stereolithography (SLA), fused deposition modeling (FDM), and selective laser sintering (SLS) methods. Tested Polyjet samples demonstrated dielectric strengths as high as 47.5 kV/mm for a 0.5 mm thick sample and 32.1 kV/mm for a 1.0 mm sample. As a result, the dielectric strength of the additively manufactured plastics evaluated as part of this study was lower than the majority of non-printed plastics by at least 15% (with themore » exception of polycarbonate).« less

Dielectric breakdown of additively manufactured polymeric materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Monzel, W. Jacob; Hoff, Brad W.; Maestas, Sabrina S.

Dielectric strength testing of selected Polyjet-printed polymer plastics was performed in accordance with ASTM D149. This dielectric strength data is compared to manufacturer-provided dielectric strength data for selected plastics printed using the stereolithography (SLA), fused deposition modeling (FDM), and selective laser sintering (SLS) methods. Tested Polyjet samples demonstrated dielectric strengths as high as 47.5 kV/mm for a 0.5 mm thick sample and 32.1 kV/mm for a 1.0 mm sample. As a result, the dielectric strength of the additively manufactured plastics evaluated as part of this study was lower than the majority of non-printed plastics by at least 15% (with themore » exception of polycarbonate).« less

High temperature structural insulating material

DOEpatents

Chen, Wayne Y.

1987-01-06

A high temperature structural insulating material useful as a liner for cylinders of high temperature engines through the favorable combination of high service temperature (above about 800.degree. C.), low thermal conductivity (below about 0.2 W/m.degree. C.), and high compressive strength (above about 250 psi). The insulating material is produced by selecting hollow ceramic beads with a softening temperature above about 800.degree. C., a diameter within the range of 20-200 .mu.m, and a wall thickness in the range of about 2-4 .mu.m; compacting the beads and a compatible silicate binder composition under pressure and sintering conditions to provide the desired structural form with the structure having a closed-cell, compact array of bonded beads.

High temperature structural insulating material

DOEpatents

Chen, Wayne Y.

1987-01-01

A high temperature structural insulating material useful as a liner for cylinders of high temperature engines through the favorable combination of high service temperature (above about 800.degree. C.), low thermal conductivity (below about 0.2 W/m.degree. C.), and high compressive strength (above about 250 psi). The insulating material is produced by selecting hollow ceramic beads with a softening temperature above about 800.degree. C., a diameter within the range of 20-200 .mu.m, and a wall thickness in the range of about 2-4 .mu.m; compacting the beads and a compatible silicate binder composition under pressure and sintering conditions to provide the desired structural form with the structure having a closed-cell, compact array of bonded beads.

Synthesis of copper coated carbon nanotubes for aluminium matrix composites

NASA Astrophysics Data System (ADS)

Maqbool, Adnan; Khalid, F. Ahmad; Hussain, M. Asif; Bakhsh, Nabi

2014-06-01

In this investigation copper coated carbon nanotubes (CNTs) were prepared to enhance the interfacial bonding between CNTs and aluminum matrix by the molecular-level mixing process. In optimized plating bath of (1:1) by wt. CNT with Cu, thickness of coated CNTs is reduced to 100 nm to promote uniform distribution of Cu nanoparticle on the surface of pretreated CNTs. The mixing of CNTs was accomplished by ultrasonication and ball milling. Scanning electron microscope analysis revealed the homogenous dispersion of Cu-coated CNTs in nanocomposites samples compared to the uncoated CNTs. The samples were pressureless sintered under vacuum. The densification increased with the increase in the CNTs content and is more pronounced in Cu-coated CNT nanocomposites.

Construction of Uniform Cobalt-Based Nanoshells and Its Potential for Improving Li-Ion Battery Performance.

PubMed

Piao, Jun-Yu; Liu, Xiao-Chan; Wu, Jinpeng; Yang, Wanli; Wei, Zengxi; Ma, Jianmin; Duan, Shu-Yi; Lin, Xi-Jie; Xu, Yan-Song; Cao, An-Min; Wan, Li-Jun

2018-06-28

Surface cobalt doping is an effective and economic way to improve the electrochemical performance of cathode materials. Herein, by tuning the precipitation kinetics of Co 2+ , we demonstrate an aqueous-based protocol to grow uniform basic cobaltous carbonate coating layer onto different substrates, and the thickness of the coating layer can be adjusted precisely in nanometer accuracy. Accordingly, by sintering the cobalt-coated LiNi 0.5 Mn 1.5 O 4 cathode materials, an epitaxial cobalt-doped surface layer will be formed, which will act as a protective layer without hindering charge transfer. Consequently, improved battery performance is obtained because of the suppression of interfacial degradation.

Use of a bite registration vinyl polysiloxane material to identify denture flange overextension and/or excessive border thickness in removable prosthodontics.

PubMed

Haeberle, C Brent; Abreu, Amara; Metzler, Kurt

2015-01-01

Vinyl polysiloxane (VPS) has multiple applications in prosthodontics. This article describes how a bite registration fast-set VPS material was used to identify length overextension and/or excessive border thickness of denture flanges. In addition, the advantages of VPS over conventional materials are presented.

Ir-based refractory superalloys by pulse electric current sintering (PECS) process (II prealloyed powder)

NASA Astrophysics Data System (ADS)

Huang, C.; Yamabe-Mitarai, Y.; Harada, H.

2002-02-01

Five prealloyed powder samples prepared from binary Ir-based refractory superalloys were sintered at 1800 °C for 4 h by Pulse Electric Current Sintering (PECS). No metal loss was observed during sintering. The relative densities of the sintered specimens all exceeded 90% T.D. The best one was Ir-13% Hf with the density of 97.82% T.D. Phases detected in sintered samples were in accordance with the phase diagram as expected. Fractured surfaces were observed in two samples (Ir-13% Hf and Ir-15% Zr). Some improvements obtained by using prealloyed powders instead of elemental powders, which were investigated in the previous studies, were presented.

Powder metallurgy: Solid and liquid phase sintering of copper

NASA Technical Reports Server (NTRS)

Sheldon, Rex; Weiser, Martin W.

1993-01-01

Basic powder metallurgy (P/M) principles and techniques are presented in this laboratory experiment. A copper based system is used since it is relatively easy to work with and is commercially important. In addition to standard solid state sintering, small quantities of low melting metals such as tin, zinc, lead, and aluminum can be added to demonstrate liquid phase sintering and alloy formation. The Taguchi Method of experimental design was used to study the effect of particle size, pressing force, sintering temperature, and sintering time. These parameters can be easily changed to incorporate liquid phase sintering effects and some guidelines for such substitutions are presented. The experiment is typically carried out over a period of three weeks.

Densification kinetics of nanocrystalline zirconia powder using microwave and spark plasma sintering--a comparative study.

PubMed

Vasylkiv, Oleg; Demirskyi, Dmytro; Sakka, Yoshio; Ragulya, Andrey; Borodianska, Hanna

2012-06-01

Two-stage densification process of nanosized 3 mol% yttria-stabilized zirconia (3Y-SZ) polycrystalline compacts during consolidation via microwave and spark-plasma sintering have been observed. The values of activation energies obtained for microwave and spark-plasma sintering 260-275 kJ x mol(-1) are quite similar to that of conventional sintering of zirconia, suggesting that densification during initial stage is controlled by the grain-boundary diffusion mechanism. The sintering behavior during microwave sintering was significantly affected by preliminary pressing conditions, as the surface diffusion mechanism (230 kJ x mol(-1)) is active in case of cold-isostatic pressing procedure was applied.

Fabrication of Bi2223 bulks with high critical current properties sintered in Ag tubes

NASA Astrophysics Data System (ADS)

Takeda, Yasuaki; Shimoyama, Jun-ichi; Motoki, Takanori; Kishio, Kohji; Nakashima, Takayoshi; Kagiyama, Tomohiro; Kobayashi, Shin-ichi; Hayashi, Kazuhiko

2017-03-01

Randomly grain oriented Bi2223 sintered bulks are one of the representative superconducting materials having weak-link problem due to very short coherence length particularly along the c-axis, resulting in poor intergrain Jc properties. In our previous studies, sintering and/or post-annealing under moderately reducing atmospheres were found to be effective for improving grain coupling in Bi2223 sintered bulks. Further optimizations of the synthesis process for Bi2223 sintered bulks were attempted in the present study to enhance their intergrain Jc. Effects of applied pressure of uniaxial pressing and sintering conditions on microstructure and superconducting properties have been systematically investigated. The best sample showed intergrain Jc of 2.0 kA cm-2 at 77 K and 8.2 kA cm-2 at 20 K, while its relative density was low ∼65%. These values are quite high as for a randomly oriented sintered bulk of cuprate superconductors.

Effects of sintering temperature on electrical properties of sheep enamel hydroxyapatite

NASA Astrophysics Data System (ADS)

Dumludag, F.; Gunduz, O.; Kılıc, O.; Kılıc, B.; Ekren, N.; Kalkandelen, C.; Oktar, F. N.

2017-12-01

Bioceramics, especially calcium phosphate based bioceramics, whose examples are hydroxyapatite, and calcium phosphate powders have been widely used in the biomedical engineering applications. Hydroxyapatite (HA) is one of the most promising biomaterials, which are derived from natural sources, chemical method, animal like dental enamel and corals. The influence of sintering temperature on the electrical properties (i.e. DC conductivity, AC conductivity) of samples of sintered sheep enamel (SSSE) was studied in air and in vacuum ambient at room temperature. The sheep enamel were sintered at varying temperatures between 1000°C and 1300°C. DC conductivity results revealed that while dc conductivity of the SSSE decreases with increasing the sintering temperature in air ambient the values increased with increasing the sintering temperature in vacuum ambient. AC conductivity measurements were performed in the frequency range of 40 Hz - 105 Hz. The results showed that ac conductivity values decrease with increasing the sintering temperature.

Degradation resistance of 3Y-TZP ceramics sintered using spark plasma sintering

NASA Astrophysics Data System (ADS)

Chintapalli, R.; Marro, F. G.; Valle, J. A.; Yan, H.; Reece, M. J.; Anglada, M.

2009-09-01

Commercially available tetragonal zirconia powder doped with 3 mol% of yttria has been sintered using spark plasma sintering (SPS) and has been investigated for its resistance to hydrothermal degradation. Samples were sintered at 1100, 1150, 1175 and 1600 °C at constant pressure of 100 MPa and soaking for 5 minutes, and the grain sizes obtained were 65, 90, 120 and 800 nm, respectively. Samples sintered conventionally with a grain size of 300 nm were also compared with samples sintered using SPS. Finely polished samples were subjected to artificial degradation at 131 °C for 60 hours in vapour in auto clave under a pressure of 2 bars. The XRD studies show no phase transformation in samples with low density and small grain size (<200 nm), but significant phase transformation is seen in dense samples with larger grain size (>300 nm). Results are discussed in terms of present theories of hydrothermal degradation.

Accelerated sintering in phase-separating nanostructured alloys

PubMed Central

Park, Mansoo; Schuh, Christopher A.

2015-01-01

Sintering of powders is a common means of producing bulk materials when melt casting is impossible or does not achieve a desired microstructure, and has long been pursued for nanocrystalline materials in particular. Acceleration of sintering is desirable to lower processing temperatures and times, and thus to limit undesirable microstructure evolution. Here we show that markedly enhanced sintering is possible in some nanocrystalline alloys. In a nanostructured W–Cr alloy, sintering sets on at a very low temperature that is commensurate with phase separation to form a Cr-rich phase with a nanoscale arrangement that supports rapid diffusional transport. The method permits bulk full density specimens with nanoscale grains, produced during a sintering cycle involving no applied stress. We further show that such accelerated sintering can be evoked by design in other nanocrystalline alloys, opening the door to a variety of nanostructured bulk materials processed in arbitrary shapes from powder inputs. PMID:25901420

Microwave sintering of single plate-shaped articles

DOEpatents

Katz, Joel D.; Blake, Rodger D.

1995-01-01

Apparatus and method for high temperature sintering of plate-shaped articles of alumina, magnesia, silica, yttria, zirconia, and mixtures thereof using microwave radiation. An article is placed within a sintering structure located within a sintering container which is placed in a microwave cavity for heating. The rates at which heating and cooling take place is controlled.

40 CFR 63.1543 - Standards for process and process fugitive sources.

Code of Federal Regulations, 2012 CFR

2012-07-01

... paragraphs (a)(1) through (9) of this section. (1) Sinter machine; (2) Blast furnace; (3) Dross furnace; (4... machine charging location; (7) Sinter machine discharge end; (8) Sinter crushing and sizing equipment; and (9) Sinter machine area. (b) No owner or operator of any existing, new, or reconstructed primary lead...

40 CFR 63.1543 - Standards for process and process fugitive sources.

Code of Federal Regulations, 2014 CFR

2014-07-01

... paragraphs (a)(1) through (9) of this section. (1) Sinter machine; (2) Blast furnace; (3) Dross furnace; (4... machine charging location; (7) Sinter machine discharge end; (8) Sinter crushing and sizing equipment; and (9) Sinter machine area. (b) No owner or operator of any existing, new, or reconstructed primary lead...

40 CFR 63.1543 - Standards for process and process fugitive sources.

Code of Federal Regulations, 2013 CFR

2013-07-01

... paragraphs (a)(1) through (9) of this section. (1) Sinter machine; (2) Blast furnace; (3) Dross furnace; (4... machine charging location; (7) Sinter machine discharge end; (8) Sinter crushing and sizing equipment; and (9) Sinter machine area. (b) No owner or operator of any existing, new, or reconstructed primary lead...

77 FR 51046 - Certain Sintered Rare Earth Magnets, Methods of Making Same and Products Containing Same; Notice...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-08-23

... INTERNATIONAL TRADE COMMISSION [Docket No. 2908] Certain Sintered Rare Earth Magnets, Methods of... Certain Sintered Rare Earth Magnets, Methods of Making Same and Products Containing Same, DN 2908; the... importation, and the sale within the United States after importation of certain sintered rare earth magnets...

77 FR 58578 - Certain Sintered Rare Earth Magnets, Methods of Making Same and Products Containing Same...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-09-21

... INTERNATIONAL TRADE COMMISSION [Investigation No. 337-TA-855] Certain Sintered Rare Earth Magnets... importation of certain sintered rare earth magnets, methods of making same and products containing same by... importation of certain sintered rare earth magnets, methods of making same and products containing same that...

Effects of sintering atmosphere on the physical and mechanical properties of modified BOF slag glass

NASA Astrophysics Data System (ADS)

Dai, Wen-bin; Li, Yu; Cang, Da-qiang; Zhou, Yuan-yuan; Fan, Yong

2014-05-01

This study proposes an efficient way to utilize all the chemical components of the basic oxygen furnace (BOF) slag to prepare high value-added glass-ceramics. A molten modified BOF slag was converted from the melting BOF slag by reducing it and separating out iron component in it, and the modified BOF slag was then quenched in water to form glasses with different basicities. The glasses were subsequently sintered in the temperature range of 600-1000°C in air or nitrogen atmosphere for 1 h. The effects of different atmospheres on the physical and mechanical properties of sintered samples were studied by using differential scanning calorimetry (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM) and by conducting experiment on evaluating the sintering shrinkage, water absorption and bulk density. It is found that the kinetics of the sintering process is significantly affected by sintering atmosphere. In particular, compared with sintering in air atmosphere, sintering in N2 atmosphere promotes the synergistic growth of pyroxene and melilite crystalline phases, which can contribute to better mechanical properties and denser microstructure.

Evaluation of Sintering Behaviors of Saprolitic Nickeliferous Laterite Based on Quaternary Basicity

NASA Astrophysics Data System (ADS)

Luo, Jun; Li, Guanghui; Rao, Mingjun; Zhang, Yuanbo; Peng, Zhiwei; Zhi, Qian; Jiang, Tao

2015-09-01

The sintering behaviors of saprolitic nickeliferous laterite with various quaternary basicities [(CaO + MgO)/(SiO2 + Al2O3) mass ratio] in a reductive atmosphere are investigated by simulative sintering and validated by sintering pot tests. The simulative sintering results show that the generation of diopside (CaMgSi2O6) with low melting point is the key reason for the decrease in characteristic fusion temperatures when the quaternary basicity increases from 0.5 to 0.8-1.0. Continuous increase of basicity leads to transformation of diopside (CaMgSi2O6) into akermanite (Ca2MgSi2O7), which adversely increases the characteristic fusion temperatures. These findings are confirmed by the sinter pot tests, which demonstrate that the sintering indexes including vertical sintering velocity (VSV), yield ( Y), and productivity ( P), can be improved by optimizing quaternary basicity. At basicity of 1.0, the VSV, Y, P, and ISO tumbling index reach 49.2 mm/min, 80.5%, 1.0 t/(h m2), and 66.5%, respectively.

Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process

NASA Astrophysics Data System (ADS)

Yu, Yeon-Tae; Naik, Gautam Kumar; Lim, Young-Bin; Yoon, Jeong-Mo

2017-11-01

The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder was investigated. The mixing ratio of Si-SiC composite nanoparticle to micron-sized SiC was optimized to 10 wt%. Vicker's hardness and relative density was increased with increasing sintering temperature and holding time. The relative density and Vicker's hardness was further increased by reaction bonding using additional activated carbon to the mixture of micron-sized SiC and nano-sized Si-SiC. The maximum relative density (97.1%) and Vicker's hardness (31.4 GPa) were recorded at 1800 °C sintering temperature for 1 min holding time, when 0.2 wt% additional activated carbon was added to the mixture of SiC/Si-SiC.

Low-Temperature Sintering Behavior (≤ 400°C) of Micro-sized Silver Particles Decorated by Silver Nanoparticles Through Surface Iodination

NASA Astrophysics Data System (ADS)

Zhou, Jian; Tang, Hongbo

2018-05-01

This paper introduces a facile and effective route to decorate micro-sized silver particle surfaces with Ag/AgI nanoclusters through a wet chemical reaction at room temperature using iodine and ethanol as reactant and solvent, respectively. Photosensitivity of AgI is utilized in the route, and AgI decomposes into Ag upon contact with sunshine, forming Ag/AgI nanoclusters. The modified micro-sized Ag particles showed sinterability even at 200°C and formed rigid electrical conductive networks at 350°C. Moreover, sintered film containing the modified Ag particles reached the best conductivity, 9.35 mΩ/sq, after sintering at 350°C for 20 min, while the film with untreated control Ag particles obtained its best conductivity at 400°C. The excellent sinterability should be attributed to the nanoclusters which served as a sintering aid during the heating process. However, increase of sintering temperature and time destroyed densification and conductivity of the sintered film containing the modified particles.

Study of sintering behavior of vapor forms of 1-octanethiol coated copper nanoparticles for application to ink-jet printing technology.

PubMed

Kwon, Jinhyeong; Park, Shinyoung; Haque, Md Mominul; Kim, Young-Seok; Lee, Caroline Sunyong

2012-04-01

Sub-50 nm copper nanoparticles coated with sub-5 nm 1-octanethiol layer for oxidation inhibition were examined to confirm the 1-octanethiol removal temperature as the sub-50 nm copper nanoparticles are sintered. As a result, 1-octanethiol Self-Assembled Multi-layers (SAMs) on sub-50 nm copper nanoparticles were successfully removed before sintering of copper nanoparticles so that a high density of copper line could be obtained. Finally, the line resistivity was measured and compared to verify the effect of sintering in different atmospheres. As a result, electrical resistivity of the copper pattern sintered in hydrogen atmosphere was measured at 6.96 x 10(-6) ohm-cm whereas that of the copper pattern sintered in mixed gas atmosphere was measured at 2.62 x 10(-5) ohm-cm. Thus, sintering of copper patterns was successfully done to show low electrical resistivity values. Moreover, removal of 1-octanethiol coating after sintering process was confirmed using X-ray photoelectron spectroscopy (XPS) analysis. By showing no sulfur content, XPS results indicate that 1-octanethiol is completely removed. Therefore, the vapor form of 1-octanethiol coating layers can be safely used as an oxidation inhibition layer for low temperature sintering processes and ink-jet applications.

Vacuum Pressureless Sintering of Ti-6Al-4V Alloy with Full Densification and Forged-Like Mechanical Properties

NASA Astrophysics Data System (ADS)

Zhang, Ce; Lu, Boxin; Wang, Haiying; Guo, Zhimeng; Paley, Vladislav; Volinsky, Alex A.

2018-01-01

Ti-6Al-4V ingots with a nearly 100% density, fine and homogeneous basket-weave microstructure, and better comprehensive mechanical properties (UTS = 935 MPa, Y.S. = 865 MPa, El. = 15.8%), have been manufactured by vacuum pressureless sintering of blended elemental powders. Coarse TiH2 powder, Al powder (2, 20 μm), V powder, and Al-V master alloy powder were used as raw materials to produce different powder mixtures ( D 50 = 10 μm). Then, the compacts made by cold isostatic pressing were consolidated by different sintering curves. A detailed investigation of different as-sintered samples revealed that a higher density can be obtained by generating transient molten Al in the sintering process. Coarse Al powder and a rapid heating rate under the melting point of Al contribute to molten Al formation. The presence of temporary liquid phase changes the sintering mechanism, accelerating the sintering neck formation, improving sinterability of the powder mixtures. Density of 99.5% was achieved at 1150 °C, which is markedly lower than the sintering temperatures reported for conventional blended elemental powder metallurgy routes. In addition, low interstitial content, especially for oxygen (0.17 wt.%), is obtained by strict process control.

Flash (Ultra-Rapid) Spark-Plasma Sintering of Silicon Carbide

PubMed Central

Olevsky, Eugene A.; Rolfing, Stephen M.; Maximenko, Andrey L.

2016-01-01

A new ultra-rapid process of flash spark plasma sintering is developed. The idea of flash spark plasma sintering (or flash hot pressing - FHP) stems from the conducted theoretical analysis of the role of thermal runaway phenomena for material processing by flash sintering. The major purpose of the present study is to theoretically analyze the thermal runaway nature of flash sintering and to experimentally address the challenge of uncontrollable thermal conditions by the stabilization of the flash sintering process through the application of the external pressure. The effectiveness of the developed FHP technique is demonstrated by the few seconds–long consolidation of SiC powder in an industrial spark plasma sintering device. Specially designed sacrificial dies heat the pre-compacted SiC powder specimens to a critical temperature before applying any voltage to the powder volume and allowing the electrode-punches of the SPS device setup to contact the specimens and pass electric current through them under elevated temperatures. The experimental results demonstrate that flash sintering phenomena can be realized using conventional SPS devices. The usage of hybrid heating SPS devices is pointed out as the mainstream direction for the future studies and utilization of the new flash hot pressing (ultra-rapid spark plasma sintering) technique. PMID:27624641

Flash (Ultra-Rapid) Spark-Plasma Sintering of Silicon Carbide

DOE PAGES

Olevsky, Eugene A.; Rolfing, Stephen M.; Maximenko, Andrey L.

2016-09-14

A new ultra-rapid process of flash spark plasma sintering is developed. The idea of flash spark plasma sintering (or flash hot pressing - FHP) stems from the conducted theoretical analysis of the role of thermal runaway phenomena for material processing by flash sintering. The major purpose of the present study is to theoretically analyze the thermal runaway nature of flash sintering and to experimentally address the challenge of uncontrollable thermal conditions by the stabilization of the flash sintering process through the application of the external pressure. The effectiveness of the developed FHP technique is demonstrated by the few seconds–long consolidationmore » of SiC powder in an industrial spark plasma sintering device. Specially designed sacrificial dies heat the pre-compacted SiC powder specimens to a critical temperature before applying any voltage to the powder volume and allowing the electrode-punches of the SPS device setup to contact the specimens and pass electric current through them under elevated temperatures. The experimental results demonstrate that flash sintering phenomena can be realized using conventional SPS devices. The usage of hybrid heating SPS devices is pointed out as the mainstream direction for the future studies and utilization of the new flash hot pressing (ultra-rapid spark plasma sintering) technique.« less

Hot-spring sinter deposits in the Alvord-Pueblo Valley, Harney County, Oregon

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cummings, M.L.; St. John, A.M.

1993-04-01

Silica sinter deposits occur at Borax Lake, Alvord Hot Springs, and Mickey Springs in the Alvord-Pueblo Valley. Although the sinter deposits occur in areas of active hot springs, sinter is not being deposited. Hot springs are localized along faults that have been active since the Pleistocene. The sinter deposits formed after the drying of glacial Lake Alvord, but before and during extensive wind deflation of glacial-lacustrine sediments. At Mickey Springs, sinter rests directly on unaltered, unconsolidated lithic-rich sand. At Borax Lake, sinter overlies unaltered diatomite, but some armoring, presumably by silica, of the 30 m vent has developed. Field relationsmore » suggest rapid dumping of silica from solution without alteration of the country rock at the vent. Discharge of thermal fluids and cold groundwater along the same structure may have produced colloidal silica carried in a solution stripped of dissolved silica. Sinter is composed of opal-a, traces of detrital feldspar and quartz, and evaporation-related boracite. The concentration of Sb is similar among the three sinter deposits (20 to 70 ppm); however, As, Cs, and Br are highest at Borax Lake (5 to 560 ppm; 26 to 118 ppm; 5 to 1,040 ppm) while Hg is highest at Mickey Springs (1.0 to 5.2 ppm).« less

Pressure-assisted low-temperature sintering for paper-based writing electronics.

PubMed

Xu, L Y; Yang, G Y; Jing, H Y; Wei, J; Han, Y D

2013-09-06

With the aim of preparing paper-based writing electronics, a kind of conductive pen was made with nano-silver ink as the conductive component and a rollerball pen as the writing implement. This was used to direct-write conductive patterns on Epson photo paper. In order to decrease the sintering temperature, pressure was introduced to enhance the driving forces for sintering. Compared with hot sintering without pressure, hot-pressure can effectively improve the conductivity of silver coatings, reduce the sintering time and thus improve productivity. Importantly, pressure can achieve a more uniform and denser microstructure, which increases the connection strength of the silver coating. At the optimum hot-pressure condition (sintering temperature 120 ° C/sintering pressure 25 MPa/sintering time 15 min), a typical measured resistivity value was 1.43 × 10⁻⁷ Ω m, nine greater than that of bulk silver. This heat treatment process is compatible with paper and does not cause any damage to the paper substrates. Even after several thousand bending cycles, the resistivity values of writing tracks by hot-pressure sintering stay almost the same (from 1.43 × 10⁻⁷ to 1.57 × 10⁻⁷ Ω m). The stability and flexibility of the writing circuits are good, which demonstrates the promising future of writing electronics.

Preparation of Porous Stainless Steel Hollow-Fibers through Multi-Modal Particle Size Sintering towards Pore Engineering

PubMed Central

Allioux, Francois-Marie; Etxeberria Benavides, Miren

2017-01-01

The sintering of metal powders is an efficient and versatile technique to fabricate porous metal elements such as filters, diffusers, and membranes. Neck formation between particles is, however, critical to tune the porosity and optimize mass transfer in order to minimize the densification process. In this work, macro-porous stainless steel (SS) hollow-fibers (HFs) were fabricated by the extrusion and sintering of a dope comprised, for the first time, of a bimodal mixture of SS powders. The SS particles of different sizes and shapes were mixed to increase the neck formation between the particles and control the densification process of the structure during sintering. The sintered HFs from particles of two different sizes were shown to be more mechanically stable at lower sintering temperature due to the increased neck area of the small particles sintered to the large ones. In addition, the sintered HFs made from particles of 10 and 44 μm showed a smaller average pore size (<1 μm) as compared to the micron-size pores of sintered HFs made from particles of 10 μm only and those of 10 and 20 μm. The novel HFs could be used in a range of applications, from filtration modules to electrochemical membrane reactors. PMID:28777352

Effect of Sintering Atmosphere and Solution Treatment on Density, Microstructure and Tensile Properties of Duplex Stainless Steels Developed from Pre-alloyed Powders

NASA Astrophysics Data System (ADS)

Murali, Arun Prasad; Mahendran, Sudhahar; Ramajayam, Mariappan; Ganesan, Dharmalingam; Chinnaraj, Raj Kumar

2017-10-01

In this research, Powder Metallurgy (P/M) of Duplex Stainless Steels (DSS) of different compositions were prepared through pre-alloyed powders and elemental powders with and without addition of copper. The powder mix was developed by pot mill for 12 h to obtain the homogeneous mixture of pre-alloyed powder with elemental compositions. Cylindrical green compacts with the dimensions of 30 mm diameter and 12 mm height were compacted through universal testing machine at a pressure level of 560 ± 10 MPa. These green compacts were sintered at 1350 °C for 2 h in hydrogen and argon atmospheres. Some of the sintered stainless steel preforms were solution treated at 1050 °C followed by water quenching. The sintered as well as solution treated samples were analysed by metallography examination, Scanning Electron Microscopy and evaluation of mechanical properties. Ferrite content of sintered and solution treated DSS were measured by Fischer Ferritoscope. It is inferred that the hydrogen sintered DSS depicted better density (94% theoretical density) and tensile strength (695 MPa) than the argon sintered steels. Similarly the microstructure of solution treated DSS revealed existence of more volume of ferrite grains than its sintered condition. Solution treated hydrogen sintered DSS A (50 wt% 316L + 50 wt% 430L) exhibited higher tensile strength of 716 MPa and elongation of 17%, which are 10-13% increment than the sintered stainless steels.

Estimation of Sintering Kinetics of Oxidized Magnetite Pellet Using Optical Dilatometer

NASA Astrophysics Data System (ADS)

Sandeep Kumar, T. K.; Viswanathan, Neelakantan Nurni; Ahmed, Hesham M.; Andersson, Charlotte; Björkman, Bo

2015-04-01

The quality of magnetite pellet is primarily determined by the physico-chemical changes the pellet undergoes as it makes excursion through the gaseous and thermal environment in the induration furnace. Among these physico-chemical processes, the oxidation of magnetite phase and the sintering of oxidized magnetite (hematite) and magnetite (non-oxidized) phases are vital. Rates of these processes not only depend on the thermal and gaseous environment the pellet gets exposed in the induration reactor but also interdependent on each other. Therefore, a systematic study should involve understanding these processes in isolation to the extent possible and quantify them seeking the physics. With this motivation, the present paper focusses on investigating the sintering kinetics of oxidized magnetite pellet. For the current investigation, sintering experiments were carried out on pellets containing more than 95 pct magnetite concentrate from LKAB's mine, dried and oxidized to completion at sufficiently low temperature to avoid sintering. The sintering behavior of this oxidized pellet is quantified through shrinkage captured by Optical Dilatometer. The extent of sintering characterized by sintering ratio found to follow a power law with time i.e., Kt n . The rate constant K for sintering was determined for different temperatures from isothermal experiments. The rate constant, K, varies with temperature as and the activation energy ( Q) and reaction rate constant ( K') are estimated. Further, the sintering kinetic equation was also extended to a non-isothermal environment and validated using laboratory experiments.

Wettability of eutectic NaLiCO3 salt on magnesium oxide substrates at 778 K

NASA Astrophysics Data System (ADS)

Li, Chuan; Li, Qi; Cao, Hui; Leng, Guanghui; Li, Yongliang; Wang, Li; Zheng, Lifang; Ding, Yulong

2018-06-01

We investigated the wetting behavior of a eutectic carbonate salt of NaLiCO3 on MgO substrates at an elevated temperature of 778 K by measuring contact angle with a sessile drop method. Both sintered and non-sintered MgO were prepared and used as the substrates. The sintered substrates were obtained by sintering compacted MgO powders at 500-1300 °C. For comparison purposes, a single crystal MgO substrate was also used in the work. The different sintering temperatures provided MgO substrates with different structures, allowing their effects on salt penetration and hence wettability and surface energy to be investigated. A scanning electron microscope equipped with energy dispersive spectrometry and an atomic force microscope were used to observe the morphology and structures of the MgO substrates as well as the salt penetration. The results showed a good wettability of the carbonate salt on both the sintered and non-sintered MgO substrates and the wettability depended strongly on the structure of the substrates. The non-sintered MgO substrate has a loose surface particle packing with large pores and crevices, leading to significant salt infiltration, and the corresponding contact angle was measured to be ∼25°. The contact angle of the salt on the sintered MgO substrates increased with an increase in the sintering temperature of the MgO substrate, and the contact angle of the salt on the single crystal substrate was the highest at ∼40°. The effect of the sintering temperature for making the MgO substrate could be linked to the surface energy, and the linkage is validated by the AFM measurements of the adhesion forces of the MgO substrates.

COUPLED FAST-THERMAL POWER BREEDER REACTOR

DOEpatents

Avery, R.

1961-07-18

A nuclear reactor having a region operating predominantly on fast neutrons and another region operating predominantly on slow neutrons is described. The fast region is a plutonium core and the slow region is a natural uranium blanket around the core. Both of these regions are free of moderator. A moderating reflector surrounds the uranium blanket. The moderating material and thickness of the reflector are selected so that fissions in the uranium blanket make a substantial contribution to the reactivity of the reactor.

Efficacy of a solution-based approach for making sodalite waste forms for an oxide reduction salt utilized in the reprocessing of used uranium oxide fuel

NASA Astrophysics Data System (ADS)

Riley, Brian J.; Pierce, David A.; Frank, Steven M.; Matyáš, Josef; Burns, Carolyne A.

2015-04-01

This paper describes the various approaches evaluated for making solution-derived sodalite with a LiCl-Li2O oxide reduction salt selected to dissolve used uranium oxide fuel so the uranium can be recovered and recycled. The approaches include modified sol-gel and solution-based synthesis processes. As-made products were mixed with 5 and 10 mass% of a Na2O-B2O3-SiO2 glass binder and these, along with product without a binder, were heated using either a cold-press-and-sinter method or hot uniaxial pressing. The results demonstrate the limitation of sodalite yield due to the fast intermediate reactions between Na+ and Cl- to form halite in solution and Li2O and SiO2 to form lithium silicates (e.g., Li2SiO3 or Li2Si2O5) in the calcined and sintered pellets. The results show that pellets can be made with high sodalite fractions in the crystalline product (∼92 mass%) and low porosities using a solution-based approach and this LiCl-Li2O salt but that the incorporation of Li into the sodalite is low.

Biocorrosion properties of antibacterial Ti-10Cu sintered alloy in several simulated biological solutions.

PubMed

Liu, Cong; Zhang, Erlin

2015-03-01

Ti-10Cu sintered alloy has shown strong antibacterial properties against S. aureus and E. coli and good cell biocompatibility, which displays potential application in dental application. The corrosion behaviors of the alloy in five different simulated biological solutions have been investigated by electrochemical technology, surface observation, roughness measurement and immersion test. Five different simulated solutions were chosen to simulate oral condition, oral condition with F(-) ion, human body fluids with different pH values and blood system. It has been shown that Ti-10Cu alloy exhibits high corrosion rate in Saliva pH 3.5 solution and Saliva pH 6.8 + 0.2F solution but low corrosion rate in Hank's, Tyrode's and Saliva pH 6.8 solutions. The corrosion rate of Ti-10Cu alloy was in a order of Hank's, Tyrode's, Saliva pH 6.8, Saliva-pH 3.5 and Saliva pH 6.8 + 0.2F from slow to fast. All results indicated acid and F(-) containing conditions prompt the corrosion reaction of Ti-Cu alloy. It was suggested that the Cu ion release in the biological environments, especially in the acid and F(-) containing condition would lead to high antibacterial properties without any cell toxicity, displaying wide potential application of this alloy.

Efficacy of a solution-based approach for making sodalite waste forms for an oxide reduction salt utilized in the reprocessing of used uranium oxide fuel

DOE PAGES

Riley, Brian J.; Pierce, David A.; Frank, Steven M.; ...

2015-04-01

This paper describes the various approaches attempted to make solution-derived sodalite with a LiCl-Li 2O oxide reduction salt used to dissolve used uranium oxide fuel so the uranium can be recovered and recycled. The approaches include modified sol-gel and solutionbased synthesis processes. As-made products were mixed with 5 and 10 mass% of a Na 2O-B 2O 3- SiO 2 glass binder and these, along with product without a binder, were heated using either a cold-press-and-sinter method or hot uniaxial pressing. The results demonstrate the limitation of sodalite yield due to the fast intermediate reactions between Na+ and Cl- to formmore » halite in solution and Li 2O and SiO 2 to form lithium silicates (e.g., Li 2SiO 3 or Li 2Si 2O 5) in the calcined and sintered pellets. The results show that pellets can be made with high sodalite fractions in the crystalline product (~92 mass%) and low porosities using a solution-based approach and this LiCl-Li 2O salt but that the incorporation of Li into the sodalite is low.« less

Structural modifications induced by ion irradiation and temperature in boron carbide B4C

NASA Astrophysics Data System (ADS)

Victor, G.; Pipon, Y.; Bérerd, N.; Toulhoat, N.; Moncoffre, N.; Djourelov, N.; Miro, S.; Baillet, J.; Pradeilles, N.; Rapaud, O.; Maître, A.; Gosset, D.

2015-12-01

Already used as neutron absorber in the current French nuclear reactors, boron carbide (B4C) is also considered in the future Sodium Fast Reactors of the next generation (Gen IV). Due to severe irradiation conditions occurring in these reactors, it is of primary importance that this material presents a high structural resistance under irradiation, both in the ballistic and electronic damage regimes. Previous works have shown an important structural resistance of boron carbide even at high neutron fluences. Nevertheless, the structural modification mechanisms due to irradiation are not well understood. Therefore the aim of this paper is to study structural modifications induced in B4C samples in different damage regimes. The boron carbide pellets were shaped and sintered by using spark plasma sintering method. They were then irradiated in several conditions at room temperature or 800 °C, either by favoring the creation of ballistic damage (between 1 and 3 dpa), or by favoring the electronic excitations using 100 MeV swift iodine ions (Se ≈ 15 keV/nm). Ex situ micro-Raman spectroscopy and Doppler broadening of annihilation radiation technique with variable energy slow positrons were coupled to follow the evolution of the B4C structure under irradiation.

Caesium isothermal migration behaviour in sintered titanium nitride: New data and comparison with previous results on iodine and xenon

NASA Astrophysics Data System (ADS)

Gavarini, S.; Bès, R.; Peaucelle, C.; Martin, P.; Esnouf, C.; Toulhoat, N.; Cardinal, S.; Moncoffre, N.; Malchère, A.; Garnier, V.; Millard-Pinard, N.; Guipponi, C.

2009-06-01

Titanium nitride has been proposed as a fission product barrier in fuel structures for gas cooled fast reactor (GFR) systems. The thermal migration of Cs was studied by implanting 800 keV 133Cs ++ ions into sintered samples of TiN at an ion fluence of 5 × 10 15 cm -2. Thermal treatments at temperatures ranging from 1500 to 1650 °C were performed under a secondary vacuum. Concentration profiles were determined by 2.5 MeV 4He + elastic backscattering. The results reveal that the global mobility of caesium in the host matrix is low compared to xenon and iodine implanted in the same conditions. Nevertheless, the evolution of caesium depth profile during thermal treatment presents similarities with that of xenon. Both species are homogeneously transported towards the surface and the transport rate increases with the temperature. In comparison, iodine exhibits singular migration behaviour. Several assumptions are proposed to explain the better retention of caesium in comparison with both other species. The potential role played by the oxidation is underlined since even a slight modification of the surface stoichiometry may modify species mobility. More generally, the apparition of square-like shapes on the surface of the samples after implantations and thermal treatments is discussed.

Effect of sintering temperature on flexural properties of alumina fiber-reinforced, alumina-based ceramics prepared by tape casting technique.

PubMed

Tanimoto, Yasuhiro; Nemoto, Kimiya

2006-01-01

The purpose of this study was to investigate the effect of sintering temperature on flexural properties of an alumina fiber-reinforced, alumina-based ceramic (alumina-fiber/alumina composite) prepared by a tape casting technique. The alumina-based ceramic used a matrix consisting of 60 wt% Al(2)O(3) powder and 40 wt% SiO(2)-B(2)O(3) glass powder with the following composition in terms of wt%: 33 SiO(2), 32 B(2)O(3), 20 CaO, and 15 MgO. Prepreg sheets of alumina-fiber/alumina composite in which uniaxial aligned alumina fibers were infiltrated with the alumina-based matrix were fabricated continuously using a tape casting technique employing a doctor blade system. Four sintering temperatures were investigated: 900 degrees C, 1000 degrees C, 1100 degrees C, and 1200 degrees C, all for 4 hours under atmospheric pressure in a furnace. The surface of the alumina-fiber/alumina composite after sintering was observed with a field-emission scanning electron microscope (FE-SEM). A three-point bending test was carried out to measure the flexural strength and modulus of alumina-fiber/alumina composite specimens. In addition, sintered alumina fiber was characterized by X-ray diffraction (XRD). FE-SEM observation showed that alumina-fiber/alumina composite was confirmed to be densely sintered for all sintering temperatures. Three-point bending measurement revealed that alumina-fiber/alumina composite produced at sintering temperatures of 1100 degrees C and 1200 degrees C exhibit flexural strengths lower than those of alumina-fiber/alumina composite produced at sintering temperatures of 900 degrees C and 1000 degrees C; alumina-fiber/alumina composite produced at sintering temperatures of 1100 degrees C and 1200 degrees C exhibit flexural moduli lower than that of alumina-fiber/alumina composite produced at a sintering temperature of 1000 degrees C. Additional XRD pattern of alumina fiber indicated that with increasing sintering temperature, the crystallographic structure of gamma-alumina transformed to mullite. There were significant differences in the flexural properties between the alumina-fiber/alumina composite sintered at the four temperatures. This indicates that the choice of optimum sintering temperature is an important factor for successful dental applications of alumina-fiber/alumina composite developed by the tape casting system.

Report on in-situ studies of flash sintering of uranium dioxide

DOE Office of Scientific and Technical Information (OSTI.GOV)

Raftery, Alicia Marie

Flash sintering is a novel type of field assisted sintering that uses an electric field and current to provide densification of materials on very short time scales. The potential for field assisted sintering techniques to be used in producing nuclear fuel is gaining recognition due to the potential economic benefits and improvements in material properties. The flash sintering behavior has so far been linked to applied and material parameters, but the underlying mechanisms active during flash sintering have yet to be identified. This report summarizes the efforts to investigate flash sintering of uranium dioxide using dilatometer studies at Los Alamosmore » National Laboratory and two separate sets of in-situ studies at Brookhaven National Laboratory’s NSLS-II XPD-1 beamline. The purpose of the dilatometer studies was to understand individual parameter (applied and material) effects on the flash behavior and the purpose of the in-situ studies was to better understand the mechanisms active during flash sintering. As far as applied parameters, it was found that stoichiometry, or oxygen-to-metal ratio, has a significant effect on the flash behavior (time to flash and speed of flash). Composite systems were found to have degraded sintering behavior relative to pure UO 2. The critical field studies are complete for UO 2.00 and will be analyzed against an existing model for comparison. The in-situ studies showed that the strength of the field and current are directly related to the sample temperature, with temperature-driven phase changes occurring at high values. The existence of an ‘incubation time’ has been questioned, due to a continuous change in lattice parameter values from the moment that the field is applied. Some results from the in-situ experiments, which should provide evidence regarding ion migration, are still being analyzed. Some preliminary conclusions can be made from these results with regard to using field assisted sintering to fabricate nuclear fuel. First, the pure UO 2-based system shows promising behavior with flash sintering, but composite systems are likely to show better sintering behavior with spark plasma sintering. Efforts to develop these methods should therefore be tailored towards the likelihood of success. Additionally, modeling is a rapidly developing aspect of current flash sintering research and should be used in parallel with experiments. Ultimately, ongoing flash sintering studies on various materials, like those summarized in this report, are rapidly contributing to the feasibility of controlling this method for use in the future.« less

Microwave-assisted one-step patterning of aqueous colloidal silver.

PubMed

Yang, G; Zhou, Y W; Guo, Z R; Wan, Y; Ding, Q; Bai, T T; Wang, C L; Gu, N

2012-07-05

A new approach of utilizing microwave to pattern gradient concentric silver nanoparticle ring structures has been presented. The width and height of a single ring and the space between adjacent rings can be adjusted by changing the silver colloidal concentration and the microwave output power. By simply enhancing the ambient vapour pressure to the saturated value during microwave-assisted evaporation, sub-100 nm rings can be deposited in between adjacent micro-rings over a distance of millimetres. Combined with microwave sintering, this approach can also create conductive silver tracks in a single step, showing huge potential in fabricating micro- and nano-electronic devices in an ultra-fast and cost-effective fashion.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Balkin, Ethan R.; Gagnon, Katherine; Strong, Kevin T.

This investigation evaluated target fabrication and beam parameters for scale-up production of high specific activity 186Re using deuteron irradiation of enriched 186W via the 186W(d,2n) 186Re reaction. Thick W and WO 3 targets were prepared, characterized and evaluated in deuteron irradiations. Full-thickness targets, as determined using SRIM, were prepared by uniaxi-ally pressing powdered natural abundance W and WO 3, or 96.86% enriched 186W, into Al target supports. Alternatively, thick targets were prepared by pressing 186W between two layers of graphite powder or by placing pre-sintered (1105°C, 12 hours) natural abundance WO 3 pellets into an Al target support. Assessments ofmore » structural integrity were made on each target pre-pared. Prior to irradiation, material composition analyses were conducted using SEM, XRD, and Raman spectroscopy. With-in a minimum of 24 hours post irradiation, gamma-ray spectroscopy was performed on all targets to assess production yields and radionuclidic byproducts. Problems were encountered with the structural integrity of some pressed W and WO 3 pellets before and during irradiation, and target material characterization results could be correlated with the structural integrity of the pressed target pellets. Under the conditions studied, the findings suggest that all WO 3 targets prepared and studied were unacceptable. By contrast, 186W metal was found to be a viable target material for 186Re production. Lastly, thick targets prepared with powdered 186W pressed between layers of graphite provided a particularly robust target configuration.« less

Microwave sintering of single plate-shaped articles

DOEpatents

Katz, J.D.; Blake, R.D.

1995-07-11

Apparatus and method are disclosed for high temperature sintering of plate-shaped articles of alumina, magnesia, silica, yttria, zirconia, and mixtures thereof using microwave radiation. An article is placed within a sintering structure located within a sintering container which is placed in a microwave cavity for heating. The rates at which heating and cooling take place is controlled. 2 figs.

Energy-Saving Sintering of Electrically Conductive Powders by Modified Pulsed Electric Current Heating Using an Electrically Nonconductive Die

NASA Astrophysics Data System (ADS)

Ito, Mikio; Kawahara, Kenta; Araki, Keita

2014-04-01

Sintering of Cu and thermoelectric Ca3Co4O9 was tried using a modified pulsed electric current sintering (PECS) process, where an electrically nonconductive die was used instead of a conventional graphite die. The pulsed electric current flowed through graphite punches and sample powder, which caused the Joule heating of the powder compact itself, resulting in sintering under smaller power consumption. Especially for the Ca3Co4O9 powder, densification during sintering was also accelerated by this modified PECS process.

Comparison of laser and intense pulsed light sintering (IPL) for inkjet-printed copper nanoparticle layers

PubMed Central

Niittynen, Juha; Sowade, Enrico; Kang, Hyunkyoo; Baumann, Reinhard R.; Mäntysalo, Matti

2015-01-01

In this contribution we discuss the sintering of an inkjet-printed copper nanoparticle ink based on electrical performance and microstructure analysis. Laser and intense pulsed light (IPL) sintering are employed in order to compare the different techniques and their feasibility for electronics manufacturing. A conductivity of more than 20% of that of bulk copper material has been obtained with both sintering methods. Laser and IPL sintering techniques are considered to be complementary techniques and are highly suitable in different application fields. PMID:25743631

Numerical Simulation of Sintering Process in Ceramic Powder Injection Moulded Components

NASA Astrophysics Data System (ADS)

Song, J.; Barriere, T.; Liu, B.; Gelin, J. C.

2007-05-01

A phenomenological model based on viscoplastic constitutive law is presented to describe the sintering process of ceramic components obtained by powder injection moulding. The parameters entering in the model are identified through sintering experiments in dilatometer with the proposed optimization method. The finite element simulations are carried out to predict the density variations and dimensional changes of the components during sintering. A simulation example on the sintering process of hip implant in alumina has been conducted. The simulation results have been compared with the experimental ones. A good agreement is obtained.

Methods of flash sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

Raj, Rishi; Cologna, Marco; Francis, John S.

2016-05-10

This disclosure provides methods of flash sintering and compositions created by these methods. Methods for sintering multilayered bodies are provided in which a sintered body is produced in less than one minute. In one aspect, each layer is of a different composition, and may be constituted wholly from a ceramic or from a combination of ceramic and metallic particles. When the body includes a layer of an anode composition, a layer of an electrolyte composition and a layer of a cathode composition, the sintered body can be used to produce a solid oxide fuel cell.

Manufacture of high-density ceramic sinters

NASA Technical Reports Server (NTRS)

Hibata, Y.

1986-01-01

High density ceramic sinters are manufactured by coating premolded or presintered porous ceramics with a sealing material of high SiO2 porous glass or nitride glass and then sintering by hot isostatic pressing. The ceramics have excellent abrasion and corrosion resistances. Thus LC-10 (Si3N2 powder) and Y2O3-Al2O3 type sintering were mixed and molded to give a premolded porous ceramic (porosity 37%, relative bulk density 63%). The ceramic was dipped in a slurry containing high SiO2 porous glass and an alcohol solution of cellulose acetate and dried. The coated ceramic was treated in a nitrogen atmosphere and then sintered by hot isostatic pressing to give a dense ceramic sinter.

Improved toughness of silicon carbide

NASA Technical Reports Server (NTRS)

Palm, J. A.

1976-01-01

Impact energy absorbing layers (EALs) comprised of partially densified silicon carbide were formed in situ on fully sinterable silicon carbide substrates. After final sintering, duplex silicon carbide structures resulted which were comprised of a fully sintered, high density silicon carbide substrate or core, overlayed with an EAL of partially sintered silicon carbide integrally bonded to its core member. Thermal cycling tests proved such structures to be moderately resistant to oxidation and highly resistant to thermal shock stresses. The strength of the developed structures in some cases exceeded but essentially it remained the same as the fully sintered silicon carbide without the EAL. Ballistic impact tests indicated that substantial improvements in the toughness of sintered silicon carbide were achieved by the use of the partially densified silicon carbide EALs.

Effect of heat wave at the initial stage in spark plasma sintering.

PubMed

Zhang, Long; Zhang, Xiaomin; Chu, Zhongxiang; Peng, Song; Yan, Zimin; Liang, Yuan

2016-01-01

Thermal effects are important considerations at the initial stage in spark plasma sintering of non-conductive Al2O3 powders. The generalized thermo-elastic theory is introduced to describe the influence of the heat transport and thermal focusing caused by thermal wave propagation within a constrained space and transient time. Simulations show that low sintering temperature can realize high local temperature because of the superposition effect of heat waves. Thus, vacancy concentration differences between the sink and the cross section of the particles increase relative to that observed during pressure-less and hot-pressure sintering. Results show that vacancy concentration differences are significantly improved during spark plasma sintering, thereby decreasing the time required for sintering.

Evaluation of Arctic Sea Ice Thickness Simulated by Arctic Ocean Model Intercomparison Project Models

NASA Technical Reports Server (NTRS)

Johnson, Mark; Proshuntinsky, Andrew; Aksenov, Yevgeny; Nguyen, An T.; Lindsay, Ron; Haas, Christian; Zhang, Jinlun; Diansky, Nikolay; Kwok, Ron; Maslowski, Wieslaw;

Development of Experimental Setup of Metal Rapid Prototyping Machine using Selective Laser Sintering Technique

NASA Astrophysics Data System (ADS)

Patil, S. N.; Mulay, A. V.; Ahuja, B. B.

2018-04-01

Unlike in the traditional manufacturing processes, additive manufacturing as rapid prototyping, allows designers to produce parts that were previously considered too complex to make economically. The shift is taking place from plastic prototype to fully functional metallic parts by direct deposition of metallic powders as produced parts can be directly used for desired purpose. This work is directed towards the development of experimental setup of metal rapid prototyping machine using selective laser sintering and studies the various parameters, which plays important role in the metal rapid prototyping using SLS technique. The machine structure in mainly divided into three main categories namely, (1) Z-movement of bed and table, (2) X-Y movement arrangement for LASER movements and (3) feeder mechanism. Z-movement of bed is controlled by using lead screw, bevel gear pair and stepper motor, which will maintain the accuracy of layer thickness. X-Y movements are controlled using timing belt and stepper motors for precise movements of LASER source. Feeder mechanism is then developed to control uniformity of layer thickness metal powder. Simultaneously, the study is carried out for selection of material. Various types of metal powders can be used for metal RP as Single metal powder, mixture of two metals powder, and combination of metal and polymer powder. Conclusion leads to use of mixture of two metals powder to minimize the problems such as, balling effect and porosity. Developed System can be validated by conducting various experiments on manufactured part to check mechanical and metallurgical properties. After studying the results of these experiments, various process parameters as LASER properties (as power, speed etc.), and material properties (as grain size and structure etc.) will be optimized. This work is mainly focused on the design and development of cost effective experimental setup of metal rapid prototyping using SLS technique which will gives the feel of metal rapid prototyping process and its important parameters.

Physical properties and microstructure study of 316L SS fabricated by metal injection moulding process

NASA Astrophysics Data System (ADS)

Dandang, Nur Aidah Nabihah; Harun, Wan Sharuzi Wan; Khalil, Nur Zalikha; Ismail, Muhammad Hussain; Ibrahim, Rosdi

2017-12-01

Metal injection moulding (MIM) has been practised to process alloy powders to become components with significant physical and mechanical properties. Dissimilar than other methods, MIM focuses on the production of high volume, a small, and complex shape of products. The performance of the compacts depends on the suitable sintering parameters that governs their strengths in the final phase which determines the excellent properties of the sintered compacts. Three different sintering temperatures were utilised; 1100, 1200, and 1300 °C with two different soaking times; 1 and 3 hours at 10 °C/min heating rate to study their effect on the physical properties and microstructure analysis of 316L SS alloy compacts. The shrinkage measurement, surface roughness, and density measurement had been conducted for physical properties study. Different sintering temperatures give an effect to the physical properties of the sintered compacts. The shrinkage measurement at 1300 °C and 3-hour sintering condition demonstrated the highest percentage reading which was 10.1 % compared to the lowest percentage reading of 6.4 % at 1100 °C and 1-hour sintering conditions. Whereas, the minimum percentage of density measurement can be found at sintering conditions of 1100 °C and 1-hour which is 83.9 % and the highest percentage is at 1300 °C and 3-hour sintering condition which is about 89.51 %. Therefore, it has been determined that there could be a significant relationship between sintering temperature and physical properties in which it can be found from the porosity of the compact based on the microstructure studies.

Low-Temperature Sintering of AlN Ceramics by Sm2O3-Y2O3-CaO Sintering Additives Formed via Decomposition of Nitrate Solutions

NASA Astrophysics Data System (ADS)

Zhan, Jun; Cao, Ye; Zhang, Hao; Guo, Jun; Zhang, Jianhua; Geng, Chunlei; Shi, Changdong; Cui, Song; Tang, Wenming

2017-01-01

The Sm, Y and Ca anhydrous nitrates were mixed with the AlN powder in ethanol and then decomposed into the Sm2O3-Y2O3-CaO sintering additives via calcining. Low-temperature sintering of the AlN ceramics was carried out at temperature range from 1675 to 1750 °C. Effects of the composition and adding amount of the sintering additives on the phases, microstructures and properties of the AlN ceramics were investigated. During sintering the AlN ceramics, main secondary phases of CaYAl3O7 and CaSmAl3O7 form. The relative density, bending strength and thermal conductivity of the AlN ceramics increase with the increase in the rare-earth oxides in them. The thermal conductivity of the sintered AlN ceramics is also greatly affected by the distribution of the secondary phases. As sintered at 1750 °C, the AlN ceramics by adding the sintering additives of 2 wt.% Sm2O3, 2 wt.% Y2O3 and 1 wt.% CaO formed via decomposition of their nitrates is fully dense and have the optimal bending strength and thermal conductivity of 402.1 MPa and 153.7 W/(m K), respectively.

Development of nano-structured duplex and ferritic stainless steels by pulverisette planetary milling followed by pressureless sintering

DOE Office of Scientific and Technical Information (OSTI.GOV)

R, Shashanka, E-mail: shashankaic@gmail.com; Chaira, D., E-mail: chaira.debasis@gmail.com

Nano-structured duplex and ferritic stainless steel powders are prepared by planetary milling of elemental Fe, Cr and Ni powder for 40 h and then consolidated by conventional pressureless sintering. The progress of milling and the continuous refinement of stainless steel powders have been confirmed by means of X-ray diffraction and scanning electron microscopy. Activation energy for the formation of duplex and ferritic stainless steels is calculated by Kissinger method using differential scanning calorimetry and is found to be 159.24 and 90.17 KJ/mol respectively. Both duplex and ferritic stainless steel powders are consolidated at 1000, 1200 and 1400 °C in argonmore » atmosphere to study microstructure, density and hardness. Maximum sintered density of 90% and Vickers microhardness of 550 HV are achieved for duplex stainless steel sintered at 1400 °C for 1 h. Similarly, 92% sintered density and 263 HV microhardness are achieved for ferritic stainless steel sintered at 1400 °C. - Highlights: • Synthesized duplex and ferritic stainless steels by pulverisette planetary milling • Calculated activation energy for the formation of duplex and ferritic stainless steels • Studied the effect of sintering temperature on density, hardness and microstructure • Duplex stainless steel exhibits 90% sintered density and microhardness of 550 HV. • Ferritic stainless steel shows 92% sintered density and 263 HV microhardness.« less

Grain boundary premelting and activated sintering in binary refractory alloys

NASA Astrophysics Data System (ADS)

Shi, Xiaomeng

Quasi-liquid intergranular film (IGF) which has been widely observed in ceramic systems can persist into sub-solidus region whereby an analogy to Grain boundary (GB) premelting can be made. In this work, a grain boundary (GB) premelting/prewetting model in a metallic system was firstly built based on the Benedictus' model and computational thermodynamics, predicting that GB disordering can start at 60-85% of the bulk solidus temperatures in selected systems. This model quantitatively explains the long-standing mystery of subsolidus activated sintering in W-Pd, W-Ni, W-Co, W-Fe and W-Cu, and it has broad applications for understanding GB-controlled transport kinetics and physical properties. Furthermore, this study demonstrates the necessity of developing GB phase diagrams as a tool for materials design. Subsequently, Grain boundary (GB) wetting and prewetting in Ni-doped Mo are systematically evaluated via characterizing well-quenched specimens and thermodynamic modeling. In contrast to prior reports, the delta-NiMo phase does not wet Mo GBs in the solid state. In the solid-liquid two-phase region, the Ni-rich liquid wets Mo GBs completely. Furthermore, high-resolution transmission electron microscopy demonstrates that nanometer-thick quasi-liquid IGFs persist at GBs into the single-phase region where the bulk liquid phase is no longer stable; this is interpreted as a case of GB prewetting. An analytical thermodynamic model is developed and validated, and this model can be extended to other systems. Furthermore, the analytical model was refined based upon Beneditus' model with correction in determining interaction contribution of interfacial energy. A calculation-based GB phase diagram for Ni-Mo binary system was created and validated by comparing with GB diffusivities determined through a series of controlled sintering experiments. The dependence of GB diffusivity on doping level and temperature was examined and compared with model-predicted GB phase diagram. The consistency between GB phase diagram and GB diffusivity was evidently observed. This study revealed the existence of quasi-liquid IGF in Ni-Mo and re-confirmed our prior hypothesis proposed through work in Ni-W system. It also demonstrated further the necessity of a GB phase diagram as a new tool to guide the materials processing or design, such as selection of sintering aid and heat-treatment.

Sintering Behavior of Spark Plasma Sintered SiC with Si-SiC Composite Nanoparticles Prepared by Thermal DC Plasma Process.

PubMed

Yu, Yeon-Tae; Naik, Gautam Kumar; Lim, Young-Bin; Yoon, Jeong-Mo

2017-11-25

The Si-coated SiC (Si-SiC) composite nanoparticle was prepared by non-transferred arc thermal plasma processing of solid-state synthesized SiC powder and was used as a sintering additive for SiC ceramic formation. Sintered SiC pellet was prepared by spark plasma sintering (SPS) process, and the effect of nano-sized Si-SiC composite particles on the sintering behavior of micron-sized SiC powder was investigated. The mixing ratio of Si-SiC composite nanoparticle to micron-sized SiC was optimized to 10 wt%. Vicker's hardness and relative density was increased with increasing sintering temperature and holding time. The relative density and Vicker's hardness was further increased by reaction bonding using additional activated carbon to the mixture of micron-sized SiC and nano-sized Si-SiC. The maximum relative density (97.1%) and Vicker's hardness (31.4 GPa) were recorded at 1800 °C sintering temperature for 1 min holding time, when 0.2 wt% additional activated carbon was added to the mixture of SiC/Si-SiC.

Effect of sintering temperature on the electrolysis of TiO2

NASA Astrophysics Data System (ADS)

Li, Ze-quan; Ru, Li-yue; Bai, Cheng-guang; Zhang, Na; Wang, Hai-hua

2012-07-01

The effects of sintering temperature on the microstructure and the conductivity of TiO2 cathodes were studied by examining the phase composition, microstructure, and element contents of the sintered cathodes and the cathodic products using X-ray diffraction and scanning electronic microscopy-energy dispersive spectrometry. The oxygen vacancy, conductivity, average pore diameter, and specific surface area of the sintered cathodes were detected by X-ray photoelectron spectroscopy, four-point probe, and ASPA 2010. The results showed that TiO2 phase transformations occurred, and oxygen vacancies formed with the increase of sintering temperature. The cathodic conductivity improved, but the average pore diameter and the effective response area of the TiO2 cathode were reduced when the sintering temperature increased. These phenomena could weaken the contact between reaction ions and electrons and also had the same effect on the cathodes and the molten salt. Moreover, they were disadvantageous to ion migration, so a lower sintering temperature was favorable for the microstructure of electrolysis. Consequently, the cathodic conductivity may be improved, but the microstructure became compact with the increase of sintering temperature. The cathodic products at different temperatures indicated that the cathodic conductivity was more important for electrolysis.

Sintering of micro-trusses created by extrusion-3D-printing of lunar regolith inks

NASA Astrophysics Data System (ADS)

Taylor, Shannon L.; Jakus, Adam E.; Koube, Katie D.; Ibeh, Amaka J.; Geisendorfer, Nicholas R.; Shah, Ramille N.; Dunand, David C.

2018-02-01

The development of in situ fabrication methods for the infrastructure required to support human life on the Moon is necessary due to the prohibitive cost of transporting large quantities of materials from the Earth. Cellular structures, consisting of a regular network (truss) of micro-struts with ∼500 μm diameters, suitable for bricks, blocks, panels, and other load-bearing structural elements for habitats and other infrastructure are created by direct-extrusion 3D-printing of liquid inks containing JSC-1A lunar regolith simulant powders, followed by sintering. The effects of sintering time, temperature, and atmosphere (air or hydrogen) on the microstructures, mechanical properties, and magnetic properties of the sintered lunar regolith micro-trusses are investigated. The air-sintered micro-trusses have higher relative densities, linear shrinkages, and peak compressive strengths, due to the improved sintering of the struts within the micro-trusses achieved by a liquid or glassy phase. Whereas the hydrogen-sintered micro-trusses show no liquid-phase sintering or glassy phase, they contain metallic iron 0.1-2 μm particles from the reduction of ilmenite, which allows them to be lifted with magnets.

Optimization of the sintering atmosphere for high-density hydroxyapatite–carbon nanotube composites

PubMed Central

White, Ashley A.; Kinloch, Ian A.; Windle, Alan H.; Best, Serena M.

2010-01-01

Hydroxyapatite–carbon nanotube (HA–CNT) composites have the potential for improved mechanical properties over HA for use in bone graft applications. Finding an appropriate sintering atmosphere for this composite presents a dilemma, as HA requires water in the sintering atmosphere to remain phase pure and well hydroxylated, yet CNTs oxidize at the high temperatures required for sintering. The purpose of this study was to optimize the atmosphere for sintering these composites. While the reaction between carbon and water to form carbon monoxide and hydrogen at high temperatures (known as the ‘water–gas reaction’) would seem to present a problem for sintering these composites, Le Chatelier's principle suggests this reaction can be suppressed by increasing the concentration of carbon monoxide and hydrogen relative to the concentration of carbon and water, so as to retain the CNTs and keep the HA's structure intact. Eight sintering atmospheres were investigated, including standard atmospheres (such as air and wet Ar), as well as atmospheres based on the water–gas reaction. It was found that sintering in an atmosphere of carbon monoxide and hydrogen, with a small amount of water added, resulted in an optimal combination of phase purity, hydroxylation, CNT retention and density. PMID:20573629

Studying hardness, workability and minimum bending radius in selectively laser-sintered Ti–6Al–4V alloy samples

NASA Astrophysics Data System (ADS)

Galkina, N. V.; Nosova, Y. A.; Balyakin, A. V.

2018-03-01

This research is relevant as it tries to improve the mechanical and service performance of the Ti–6Al–4V titanium alloy obtained by selective laser sintering. For that purpose, sintered samples were annealed at 750 and 850°C for an hour. Sintered and annealed samples were tested for hardness, workability and microstructure. It was found that incomplete annealing of selectively laser-sintered Ti–6Al–4V samples results in an insignificant reduction in hardness and ductility. Sintered and incompletely annealed samples had a hardness of 32..33 HRC, which is lower than the value of annealed parts specified in standards. Complete annealing at temperature 850°C reduces the hardness to 25 HRC and ductility by 15...20%. Incomplete annealing lowers the ductility factor from 0.08 to 0.06. Complete annealing lowers that value to 0.025. Complete annealing probably results in the embrittlement of sintered samples, perhaps due to their oxidation and hydrogenation in the air. Optical metallography showed lateral fractures in both sintered and annealed samples, which might be the reason why they had lower hardness and ductility.

Atomic-level study of a thickness-dependent phase change in gold thin films heated by an ultrafast laser.

PubMed

Gan, Yong; Shi, Jixiang; Jiang, Shan

2012-08-20

An ultrafast laser-induced phase change in gold thin films with different thicknesses has been simulated by the method of coupling the two-temperature model and the molecular dynamics, including transient optical properties. Numerical results show that the decrease of film thickness leads to faster melting in the early nonequilibrium time and a larger melting depth. Moreover, earlier occurrence and a higher rate of resolidification are observed for the thicker film. Further analysis reveals that the mechanism for the thickness-dependent phase change in the films is the fast electron thermal conduction in the nonequilibrium state.

Behavior of Oxide Film at Interface between Particles of Al-Mg Alloy Powder Compacts Prepared by Pulse Electric Current Sintering

NASA Astrophysics Data System (ADS)

Xie, Guoqiang; Ohashi, Osamu; Yamaguchi, Norio; Song, Minghui; Mitsuishi, Kazutaka; Furuya, Kazuo; Noda, Tetsuji

2003-07-01

Al-1.0 mass% Mg alloy powders were sintered using the pulse electric current sintering (PECS) process at various temperatures. The microstructure at the interfaces between powder particles and the effect of sintering temperature on interface characteristics were investigated using transmission electron microscopy (TEM) and energy dispersive X-ray spectroscopy (EDS). The precipitates were observed at the interfaces between powder particles of the compacts. The amounts of the precipitates increased and the compositions changed with an increase in sintering temperature: MgO for the compact sintered at 613 K, MgAl2O4+MgO for those at 663 K and 713 K, and MgAl2O4 for those above 763 K. Comparing the results obtained by the PECS process with those of diffusion bonding experiments and thermodynamic calculation, it was suggested that the temperature at the interfaces between the particles was higher than that of the particles sintered by the PECS process.

Application of the Zero-Order Reaction Rate Model and Transition State Theory to predict porous Ti6Al4V bending strength.

PubMed

Reig, L; Amigó, V; Busquets, D; Calero, J A; Ortiz, J L

2012-08-01

Porous Ti6Al4V samples were produced by microsphere sintering. The Zero-Order Reaction Rate Model and Transition State Theory were used to model the sintering process and to estimate the bending strength of the porous samples developed. The evolution of the surface area during the sintering process was used to obtain sintering parameters (sintering constant, activation energy, frequency factor, constant of activation and Gibbs energy of activation). These were then correlated with the bending strength in order to obtain a simple model with which to estimate the evolution of the bending strength of the samples when the sintering temperature and time are modified: σY=P+B·[lnT·t-ΔGa/R·T]. Although the sintering parameters were obtained only for the microsphere sizes analysed here, the strength of intermediate sizes could easily be estimated following this model. Copyright © 2012 Elsevier B.V. All rights reserved.

Sintered Intermetallic Reinforced 434L Ferritic Stainless Steel Composites

NASA Astrophysics Data System (ADS)

Upadhyaya, A.; Balaji, S.

2009-03-01

The present study examines the effect of aluminide (Ni3Al, Fe3Al) additions on the sintering behavior of ferritic 434L stainless steels during solid-state sintering (SSS) and supersolidus liquid-phase sintering (SLPS). 434L stainless steel matrix composites containing 5 and 10 wt pct of each aluminide were consolidated at 1200 °C (SSS) and 1400 °C (SLPS). The effects of sintering and aluminide additions on the densification, microstructural evolution, mechanical, tribological, and corrosion behavior of sintered ferritic (434L) stainless steels were investigated. The performances of the 434L-aluminide composites were compared with the straight 434L stainless steels processed at similar conditions. Supersolidus sintering resulted in significant improvement in densification, mechanical, wear, and corrosion resistance in both straight 434L and 434L-aluminide composites. Fe3Al additions to 434L stainless steels result in improved wear resistance without significant degradation of corrosion resistance in 3.56 wt pct NaCl solution.

[Influence of compaction pressure and pre-sintering temperature on the machinability of zirconia ceramic].

PubMed

Huang, Huil; Li, Jing; Zhang, Fuqiang; Sun, Jing; Gao, Lian

2011-10-01

In order to make certain the compaction pressure as well as pre-sintering temperature on the machinability of the zirconia ceramic. 3 mol nano-size 3 mol yttria partially stabilized zirconia (3Y-TZP) powder were compacted at different isostatic pressure and sintered at different temperature. The cylindrical surface was traversed using a hard metal tool. Surface and edge quality were checked visually using light stereo microscopy. Pre-sintering temperature had the obviously influence on the machinability of 3Y-TZP. The cutting surface was smooth, and the integrality of edge was better when the pre-sintering temperature was chosen between 800 degrees C to 900 degrees C. Compaction pressure showed only a weak influence on machinability of 3Y-TZP blanks, but the higher compaction pressure result in the poor surface quality. The best machinability of pre-sintered zirconia body was found for 800-900 degrees C pre-sintering temperature, and 200-300 MPa compaction pressure.

Extension of the master sintering curve for constant heating rate modeling

NASA Astrophysics Data System (ADS)

McCoy, Tammy Michelle

The purpose of this work is to extend the functionality of the Master Sintering Curve (MSC) such that it can be used as a practical tool for predicting sintering schemes that combine both a constant heating rate and an isothermal hold. Rather than just being able to predict a final density for the object of interest, the extension to the MSC will actually be able to model a sintering run from start to finish. Because the Johnson model does not incorporate this capability, the work presented is an extension of what has already been shown in literature to be a valuable resource in many sintering situations. A predicted sintering curve that incorporates a combination of constant heating rate and an isothermal hold is more indicative of what is found in real-life sintering operations. This research offers the possibility of predicting the sintering schedule for a material, thereby having advanced information about the extent of sintering, the time schedule for sintering, and the sintering temperature with a high degree of accuracy and repeatability. The research conducted in this thesis focuses on the development of a working model for predicting the sintering schedules of several stabilized zirconia powders having the compositions YSZ (HSY8), 10Sc1CeSZ, 10Sc1YSZ, and 11ScSZ1A. The compositions of the four powders are first verified using x-ray diffraction (XRD) and the particle size and surface area are verified using a particle size analyzer and BET analysis, respectively. The sintering studies were conducted on powder compacts using a double pushrod dilatometer. Density measurements are obtained both geometrically and using the Archimedes method. Each of the four powders is pressed into ¼" diameter pellets using a manual press with no additives, such as a binder or lubricant. Using a double push-rod dilatometer, shrinkage data for the pellets is obtained over several different heating rates. The shrinkage data is then converted to reflect the change in relative density of the pellets based on the green density and the theoretical density of each of the compositions. The Master Sintering Curve (MSC) model is then utilized to generate data that can be utilized to predict the final density of the respective powder over a range of heating rates. The Elton Master Sintering Curve Extension (EMSCE) is developed to extend the functionality of the MSC tool. The parameters generated from the original MSC are used in tandem with the solution to the closed integral, theta ≡ 1cTo T1Texp -QRT dT, over a set range of temperatures. The EMSCE is used to generate a set of sintering curves having both constant heating rate and isothermal hold portions. The EMSCE extends the usefulness of the MSC by allowing this generation of a complete sintering schedule rather than just being able to predict the final relative density of a given material. The EMSCE is verified by generating a set of curves having both constant heating rate and an isothermal hold for the heat-treatment. The modeled curves are verified experimentally and a comparison of the model and experimental results are given for a selected composition. Porosity within the final product can hinder the product from sintering to full density. It is shown that some of the compositions studied did not sinter to full density because of the presence of large porosity that could not be eliminated in a reasonable amount of time. A statistical analysis of the volume fraction of porosity is completed to show the significance of the presence in the final product. The reason this is relevant to the MSC is that the model does not take into account the presence of porosity and assumes that the samples sinter to full density. When this does not happen, the model actually under-predicts the final density of the material.

Densification of LSGM electrolytes using activated microwave sintering

NASA Astrophysics Data System (ADS)

Kesapragada, S. V.; Bhaduri, S. B.; Bhaduri, S.; Singh, P.

Lanthanum gallate doped with alkaline rare earths (LSGM) powders were densified using an activated microwave sintering process for developing a dense stable electrolyte layer for applications in intermediate temperature-solid oxide fuel cells (IT-SOFCs). Due to heat generation in situ, the process of sintering gets activated with faster kinetics compared to a conventional sintering process. The effect of various microwave process parameters on the microstructure and phase formation was studied. The sintered pellets were characterized using scanning electron microscopy-energy dispersive analysis (SEM-EDAX), and X-ray diffraction (XRD). The density of LSGM pellets microwave sintered at 1350 °C for 20 min is greater than 95% theoretical density with a fine grained microstructure (˜2-3 μm) and without the presence of other phase(s).

Hybrid processing and anisotropic sintering shrinkage in textured ZnO ceramics

PubMed Central

Keskinbora, Kahraman; Suzuki, Tohru S; Ozgur Ozer, I; Sakka, Yoshio; Suvaci, Ender

2010-01-01

We have studied the combined effects of the templated grain growth and magnetic alignment processes on sintering, anisotropic sintering shrinkage, microstructure development and texture in ZnO ceramics. Suspensions of 0–10 vol % ZnO template particles were slip cast in a 12 T rotating magnetic field. Sintering and texture characteristics were investigated via thermomechanical analysis and electron backscatter diffraction, respectively. Sintering as well as texture characteristics depend on template concentration. For the studied ZnO system, there is a critical template concentration (2 vol % in this study) above which densification is limited by the templates owing to constrained sintering. Below this limit, the densification is enhanced and the anisotropic shrinkage is reduced, which is attributed to densifying characteristics of the templates. PMID:27877373

Effect of grain size on structural and dielectric properties of barium titanate piezoceramics synthesized by high energy ball milling

NASA Astrophysics Data System (ADS)

Verma, Narendra Kumar; Patel, Sandeep Kumar Singh; Kumar, Dinesh; Singh, Chandra Bhal; Singh, Akhilesh Kumar

2018-05-01

We have investigated the effect of sintering temperature on the densification behaviour, grain size, structural and dielectric properties of BaTiO3 ceramics, prepared by high energy ball milling method. The Powder x-ray diffraction reveals the tetragonal structure with space group P4mm for all the samples. The samples were sintered at four different temperatures, (T = 900°C, 1000°C, 1100°C, 1200°C and 1300°C). Density increased with increasing sintering temperature, reaching up to 97% at 1300°C. A grain growth was observed with increasing sintering temperature. Impedance analyses of the sintered samples at various temperatures were performed. Increase in dielectric constant and Curie temperature is observed with increasing sintering temperature.

Densification behavior, nanocrystallization, and mechanical properties of spark plasma sintered Fe-based bulk amorphous alloys

NASA Astrophysics Data System (ADS)

Singh, Ashish Kumar

Fe-based amorphous alloys are gaining increasing attention due to their exceptional wear and corrosion resistance for potential structural applications. Two major challenges that are hindering the commercialization of these amorphous alloys are difficulty in processing of bulk shapes (diameter > 10 mm) and lack of ductility. Spark plasma sintering (SPS) is evolving as a promising technique for processing bulk shapes of amorphous and nanocrystalline materials. The objective of this work is to investigate densification behavior, nanocrystallization, and mechanical properties of SPS sintered Fe-based amorphous alloys of composition Fe48Cr15Mo14Y2C15B6. SPS processing was performed in three distinct temperature ranges of amorphous alloys: (a) below glass transition temperature (Tg), (b) between Tg and crystallization temperature (Tx), and (c) above Tx. Punch displacement data obtained during SPS sintering was correlated with the SPS processing parameters such as temperature, pressure, and sintering time. Powder rearrangement, plastic deformation below T g, and viscous flow of the material between Tg and Tx were observed as the main densification stages during SPS sintering. Micro-scale temperature distributions at the point of contact and macro-scale temperature distribution throughout the sample during SPS of amorphous alloys were modeled. The bulk amorphous alloys are expected to undergo structural relaxation and nanocrystallization during SPS sintering. X-ray diffraction (XRD), small angle neutron scattering (SANS), and transmission electron microscopy (TEM) was performed to investigate the evolution of nanocrystallites in SPS sintered Fe-based bulk amorphous alloys. The SANS analysis showed significant scattering for the samples sintered in the supercooled region indicating local structural and compositional changes with the profuse nucleation of nano-clusters (~4 nm). Compression tests and microhardness were performed on the samples sintered at different temperatures ranging from 570 °C to 800 °C. Maximum compression strength (1.1+/-0.2 MPa) was obtained for the samples sintered in the supercooled region. Effects of crystallization on tribological behavior of sintered samples were also investigated where crystallization resulted in increase in wear resistance. Laser surface hardening of SPS sintered amorphous samples were performed. Depending on the processing parameters, the laser surface irradiation causes structural relaxation and nanocrystallization, resulting in surface hardening.

Effects of pressure and deposition time on the characteristics of In2Se3 films grown by magnetron sputtering

NASA Astrophysics Data System (ADS)

Yan, Yong; Li, Shasha; Ou, Yufeng; Ji, Yaxin; Yu, Zhou; Liu, Lian; Yan, Chuanpeng; Zhang, Yong; Zhao, Yong

2014-11-01

Crystalline In2Se3 films were fabricated by magnetron sputtering from a sintered In2Se3-compound target and the effects of the deposition parameters, including the working pressure and deposition time, on the phase composition, structure, morphology, and optical properties were clarified. Single-phase κ-In2Se3 was prepared at 4.0 Pa, but γ-In2Se3 was recognized when the working pressure was lower than 4.0 Pa. The optical transmittance of the films decreased to 45% and the optical band gap varied from 2.9 to 2.0 eV with increasing film thickness from 80 to 967 nm. Metal-semiconductor-metal (MSM) photodetectors based on γ-In2Se3 thin films with various thicknesses were also fabricated. The result of photosensitivity research on such MSM photodetectors suggests that it may be impossible to fabricate wide-absorption-range MSM devices by just using a single material ( γ-In2Se3) because of spatial potential fluctuations in the layers. [Figure not available: see fulltext.

Micro-architecture embedding ultra-thin interlayer to bond diamond and silicon via direct fusion

NASA Astrophysics Data System (ADS)

Kim, Jong Cheol; Kim, Jongsik; Xin, Yan; Lee, Jinhyung; Kim, Young-Gyun; Subhash, Ghatu; Singh, Rajiv K.; Arjunan, Arul C.; Lee, Haigun

2018-05-01

The continuous demand on miniaturized electronic circuits bearing high power density illuminates the need to modify the silicon-on-insulator-based chip architecture. This is because of the low thermal conductivity of the few hundred nanometer-thick insulator present between the silicon substrate and active layers. The thick insulator is notorious for releasing the heat generated from the active layers during the operation of devices, leading to degradation in their performance and thus reducing their lifetime. To avoid the heat accumulation, we propose a method to fabricate the silicon-on-diamond (SOD) microstructure featured by an exceptionally thin silicon oxycarbide interlayer (˜3 nm). While exploiting the diamond as an insulator, we employ spark plasma sintering to render the silicon directly fused to the diamond. Notably, this process can manufacture the SOD microarchitecture via a simple/rapid way and incorporates the ultra-thin interlayer for minute thermal resistance. The method invented herein expects to minimize the thermal interfacial resistance of the devices and is thus deemed as a breakthrough appealing to the current chip industry.

Effects of Impurity Content on the Sintering Characteristics of Plasma-Sprayed Zirconia

NASA Astrophysics Data System (ADS)

Paul, S.; Cipitria, A.; Golosnoy, I. O.; Xie, L.; Dorfman, M. R.; Clyne, T. W.

2007-12-01

Yttria-stabilized zirconia powders, containing different levels of SiO2 and Al2O3, have been plasma sprayed onto metallic substrates. The coatings were detached from their substrates and a dilatometer was used to monitor the dimensional changes they exhibited during prolonged heat treatments. It was found that specimens containing higher levels of silica and alumina exhibited higher rates of linear contraction, in both in-plane and through-thickness directions. The in-plane stiffness and the through-thickness thermal conductivity were also measured after different heat treatments and these were found to increase at a greater rate for specimens with higher impurity (silica and alumina) levels. Changes in the pore architecture during heat treatments were studied using Mercury Intrusion Porosimetry (MIP). Fine scale porosity (< ˜50 nm) was found to be sharply reduced even by relatively short heat treatments. This is correlated with improvements in inter-splat bonding and partial healing of intra-splat microcracks, which are responsible for the observed changes in stiffness and conductivity, as well as the dimensional changes.

Effects of particle packing on the sintered microstructure

NASA Astrophysics Data System (ADS)

Barringer, E. A.; Bowen, H. K.

1988-04-01

The sintering process is shown to be critically dependent on particle-packing density and porosity uniformity. Sintering experiments were conducted on compacts consisting of monodisperse, spherical TiO2 particles. Densification kinetics and microstructure evolution for two initial packing densities, 55% and 69% of theoretical, were investigated. The lower-density compacts sintered rapidly to theoretical density, yet improved particle-packing density and uniformity significantly enhanced densification.

Experimental studies on a novel roll-to-roll powder hot embossing for large-area fabrication of micropyramid arrays on polymers

NASA Astrophysics Data System (ADS)

Yi, Peiyun; Deng, Yujun; Shu, Yunyi; Peng, Linfa

2018-08-01

Roll-to-roll (R2R) hot embossing is regarded as a cost-effective replication technology to fabricate microstructures on polymer films. However, the characteristics of continuous and fast forming for the R2R hot embossing process limits material flow during the filling stage and results in significant springback during the demolding stage. To resolve this issue, this study proposed a novel R2R powder hot embossing process, which combines the merits of the continuous fabrication of R2R hot embossing and near-net-shape forming of powder sintering and also decreases the whole cycle of the fabrication from films to microstructures. First, the relation between the molten layer thickness and processing parameters was discussed and an analytical model was established to predict the feed of the polymeric powder during R2R powder hot embossing. Then, with the use of a micro-pyramid array mold, the impact of the process parameters including mold temperature, feeding speed and applied force on the geometrical dimension of the patterned microstructures was discussed. Last, based on the response surface analysis, a process window, in terms of the mold temperature of 132 °C –145 °C, feeding speed of 0.1–1.4 m min‑1 and applied force of 15–50 kgf was determined for the continuous fabrication of completely-filled micropyramid arrays with the R2R powder hot embossing process. This research demonstrated the feasibility and superiority of the proposed R2R powder hot embossing process in continuously fabricating micropatterned structures on polymeric films.

Nano-Hydroxyapatite/Fluoridated and Unfluoridated Bioactive Glass Composites: Structural Analysis and Bioactivity Evaluation

DOE Office of Scientific and Technical Information (OSTI.GOV)

Batra, Uma; Kapoor, Seema; Sharma, J. D.

2011-12-12

Biphasic bioceramic composites containing nano-hydroxyapatite (HAP) and nanosized bioactive glasses have been prepared in the form of pellets and have been examined for the effects of bioglass concentrations and sintering temperature on the structural transformations and bioactivity behavior. Pure stoichiometric nano-HAP was synthesized using sol-gel technique. Two bioglasses synthesized in this work--fluoridated bioglass (Cao-P{sub 2}O{sub 5}-Na{sub 2}O{sub 3}-CaF{sub 2}) and unfluoridated bioglass (Cao-P{sub 2}O{sub 5}-Na{sub 2}O{sub 3}) designated as FBG and UFBG respectively, were added to nano-HAP with concentrations of 5, 10, 12 and 15%. The average particle sizes of synthesized HAP and bioglasses were 23 nm and 35 nm,more » respectively. The pellets were sintered at four different temperatures i.e. 1000 deg. C, 1150 deg. C, 1250 deg. C and 1350 deg. C. The investigations involved study of structural and bioactivity behavior of green and sintered pellets and their deviations from original materials i.e. HAP, FBG and UFBG, using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The phase composition of the sintered pellets was found to be non-stoichiometric HAP with {alpha}-TCP (tricalcium phosphate) and {beta}-TCP. It was revealed from SEM images that bonding mechanism was mainly solid state sintering for all pellets sintered at 1000 deg. C and 1150 deg. C and also for pellets with lower concentrations of bioglass i.e. 5% and 10% sintered at 1250 deg. C. Partly liquid phase sintering was observed for pellets with higher bioglass concentrations of 12% and 15% sintered at 1250 deg. C and same behaviour was noted for pellets at all concentrations of bioglasses at 1350 deg. C. The sintered density, hardness and compression strength of pellets have been influenced both by the concentration of the bioglasses and sintering temperature. It was observed that the biological HAP layer formation was faster on the green pellets surface than on pure HAP and sintered pellets, showing higher bioactivity in the green pellets.« less

Improvement of mechanical strength of sintered Mo alloyed steel by optimization of sintering and cold-forging processes with densification

NASA Astrophysics Data System (ADS)

Kamakoshi, Y.; Shohji, I.; Inoue, Y.; Fukuda, S.

2017-10-01

Powder metallurgy (P/M) materials have been expected to be spread in automotive industry. Generally, since sintered materials using P/M ones contain many pores and voids, mechanical properties of them are inferior to those of conventional wrought materials. To improve mechanical properties of the sintered materials, densification is effective. The aim of this study is to improve mechanical strength of sintered Mo-alloyed steel by optimizing conditions in sintering and cold-forging processes. Mo-alloyed steel powder was compacted. Then, pre-sintering (PS) using a vacuum sintering furnace was conducted. Subsequently, coldforging (CF) by a backward extrusion method was conducted to the pre-sintered specimen. Moreover, the cold-forged specimen was heat treated by carburizing, tempering and quenching (CQT). Afterwards, mechanical properties were investigated. As a result, it was found that the density of the PS specimen is required to be more than 7.4 Mg/m3 to strengthen the specimen by heat treatment after CF. Furthermore, density and the microstructure of the PS specimen are most important factors to make the high density and strength material by CF. At the CF load of 1200 kN, the maximum density ratio reached approximately 99% by the use of the PS specimen with proper density and microstructure. At the CF load of 900 kN, although density ratio was high like more than 97.8%, transverse rupture strength decreased sharply. Since densification caused high shear stress and stress concentration in the surface layer, microcracks occurred by the damages of inter-particle sintered connection of the surface layer. On the contrary, in case of the CF load of 1200 kN, ultra-densification of the surface layer occurred by a sufficient plastic flow. Such sufficient compressed specimens regenerated the sintered connections by high temperature heat treatment and thus the high strength densified material was obtained. These processes can be applicable to near net shape manufacturing without surface machining.

Development of a sintering process for recycling oil shale fly ash and municipal solid waste incineration bottom ash into glass ceramic composite.

PubMed

Zhang, Zhikun; Zhang, Lei; Li, Aimin

2015-04-01

Oil shale fly ash and municipal solid waste incineration bottom ash are industrial and municipal by-products that require further treatment before disposal to avoid polluting the environment. In the study, they were mixed and vitrified into the slag by the melt-quench process. The obtained vitrified slag was then mixed with various percentages of oil shale fly ash and converted into glass ceramic composites by the subsequent sintering process. Differential thermal analysis was used to study the thermal characteristics and determine the sintering temperatures. X-ray diffraction analysis was used to analyze the crystalline phase compositions. Sintering shrinkage, weight loss on ignition, density and compressive strength were tested to determine the optimum preparation condition and study the co-sintering mechanism of vitrified amorphous slag and oil shale fly ash. The results showed the product performances increased with the increase of sintering temperatures and the proportion of vitrified slag to oil shale fly ash. Glass ceramic composite (vitrified slag content of 80%, oil shale fly ash content of 20%, sintering temperature of 1000 °C and sintering time of 2h) showed the properties of density of 1.92 ± 0.05 g/cm(3), weight loss on ignition of 6.14 ± 0.18%, sintering shrinkage of 22.06 ± 0.6% and compressive strength of 67 ± 14 MPa. The results indicated that it was a comparable waste-based material compared to previous researches. In particular, the energy consumption in the production process was reduced compared to conventional vitrification and sintering method. Chemical resistance and heavy metals leaching results of glass ceramic composites further confirmed the possibility of its engineering applications. Copyright © 2015 Elsevier Ltd. All rights reserved.

TOPICAL REVIEW: Sintering and microstructure of ice: a review

NASA Astrophysics Data System (ADS)

Blackford, Jane R.

2007-11-01

Sintering of ice is driven by the thermodynamic requirement to decrease surface energy. The structural morphology of ice in nature has many forms—from snowflakes to glaciers. These forms and their evolution depend critically on the balance between the thermodynamic and kinetic factors involved. Ice is a crystalline material so scientific understanding and approaches from more conventional materials can be applied to ice. The early models of solid state ice sintering are based on power law models originally developed in metallurgy. For pressure sintering of ice, these are based on work on hot isostatic pressing of metals and ceramics. Recent advances in recognizing the grain boundary groove geometry between sintering ice particles require models that use new approaches in materials science. The newer models of sintering in materials science are beginning to incorporate more realistic processing conditions and microstructural complexity, and so there is much to be gained from applying these to ice in the future. The vapour pressure of ice is high, which causes it to sublime readily. The main mechanism for isothermal sintering of ice particles is by vapour diffusion; however other transport mechanisms certainly contribute. Plastic deformation with power law creep combined with recrystallization become important mechanisms in sintering with external pressure. Modern experimental techniques, low temperature scanning electron microscopy and x-ray tomography, are providing new insights into the evolution of microstructures in ice. Sintering in the presence of a small volume fraction of the liquid phase causes much higher bond growth rates. This may be important in natural snow which contains impurities that form a liquid phase. Knowledge of ice microstructure and sintering is beneficial in understanding mechanical behaviour in ice friction and the stability of snow slopes prone to avalanches.

[Study on friction and wear properties of dental zirconia ceramics processed by microwave and conventional sintering methods].

PubMed

Guoxin, Hu; Ying, Yang; Yuemei, Jiang; Wenjing, Xia

2017-04-01

This study evaluated the wear of an antagonist and friction and wear properties of dental zirconia ceramic that was subjected to microwave and conventional sintering methods. Ten specimens were fabricated from Lava brand zirconia and randomly assigned to microwave and conventional sintering groups. A profile tester for surface roughness was used to measure roughness of the specimens. Wear test was performed, and steatite ceramic was used as antagonist. Friction coefficient curves were recorded, and wear volume were calculated. Finally, optical microscope was used to observe the surface morphology of zirconia and steatite ceramics. Field emission scanning electron microscopy was used to observe the microstructure of zirconia. Wear volumes of microwave and conventionally sintered zirconia were (6.940±1.382)×10⁻², (7.952±1.815) ×10⁻² mm³, respectively. Moreover, wear volumes of antagonist after sintering by the considered methods were (14.189±4.745)×10⁻², (15.813±3.481)×10⁻² mm³, correspondingly. Statistically significant difference was not observed in the wear resistance of zirconia and wear volume of steatite ceramic upon exposure to two kinds of sintering methods. Optical microscopy showed that ploughed surfaces were apparent in zirconia. The wear surface of steatite ceramic against had craze, accompanied by plough. Scanning electron microscopy showed that zirconia was sintered compactly when subjected to both conventional sintering and microwave methods, whereas grains of zirconia sintered by microwave alone were smaller and more uniform. Two kinds of sintering methods are successfully used to produce dental zirconia ceramics with similar friction and wear properties.
.

Effects of pressure and temperature on sintering of Cr-doped Al2O3 by pulsed electric current sintering process

NASA Astrophysics Data System (ADS)

Dang, K. Q.; Nanko, M.

2011-03-01

The aluminium oxide crystal, Al2O3, which contains a small amount of chromium, Cr, is called ruby. Pulsed electric current sintering (PECS) was applied to sinter ruby polycrystals. Cr2O3-Al2O3 powder mixture prepared by drying an aqueous slurry containing amounts of Al2O3 and Cr(NO3)3 was consolidated by PECS process. The PECS process was performed in vacuum at sintering temperature raging from 1100 to 1300°C with heating rate of 2 K/min under applied uniaxial pressure varied from 40 to 100 MPa. This study found that highly densified and transparent Cr-doped Al2O3 can be obtained by the PECS process with the high applied pressure at sintering temperature of 1200°C.

Effect of two-stage sintering on dielectric properties of BaTi0.9Zr0.1O3 ceramics

NASA Astrophysics Data System (ADS)

Rani, Rekha; Rani, Renu; Kumar, Parveen; Juneja, J. K.; Raina, K. K.; Prakash, Chandra

2011-09-01

The effect of two-stage sintering on the dielectric properties of BaTi0.9Zr0.1O3 ceramics prepared by solid state route was investigated and is presented here. It has been found that under suitable two-stage sintering conditions, dense BaTi0.9Zr0.1O3 ceramics with improved electrical properties can be synthesized. The density was found to have a value of 5.49 g cc-1 for normally sintered samples, whereas in the case of the two-stage sintered sample it was 5.85 g cc-1. Dielectric measurements were done as a function of frequency and temperature. A small decrease in the Curie temperature was observed with modification in dielectric loss for two-stage sintered ceramic samples.

Surface-selective laser sintering of thermolabile polymer particles using water as heating sensitizer

NASA Astrophysics Data System (ADS)

Antonov, E. N.; Krotova, L. I.; Minaev, N. V.; Minaeva, S. A.; Mironov, A. V.; Popov, V. K.; Bagratashvili, V. N.

2015-11-01

We report the implementation of a novel scheme for surface-selective laser sintering (SSLS) of polymer particles, based on using water as a sensitizer of laser heating and sintering of particles as well as laser radiation at a wavelength of 1.94 μm, corresponding to the strong absorption band of water. A method of sintering powders of poly(lactide-co-glycolide), a hydrophobic bioresorbable polymer, after modifying its surface with an aqueous solution of hyaluronic acid is developed. The sintering thresholds for wetted polymer are by 3 - 4 times lower than those for sintering in air. The presence of water restricts the temperature of the heated polymer, preventing its thermal destruction. Polymer matrices with a developed porous structure are obtained. The proposed SSLS method can be applied to produce bioresorbable polymer matrices for tissue engineering.

Mechanical Properties and Plasma Erosion Resistance of ZrO2p(3Y)/BN-SiO2 Ceramic Composites under Different Sintering Temperature

NASA Astrophysics Data System (ADS)

Zhou, Yu; Duan1, Xiaoming; Jia, Dechang; Yang, Zhihua; Meng, Qingchang; Yu, Yang; Yu, Daren; Ding, Yongjie

2011-10-01

ZrO2p(3Y)/BN-SiO2 ceramic composites were hot pressed under different sintering temperature. The ceramic composites were composed by BN, m-ZrO2, t-ZrO2 and SiO2. The relative density, bending strength, elastic modulus and fracture toughness increase with the sintering temperature increasing, the maximum value of which at the sintering temperature of 1800°C are 97.5%, 229.9MPa, 60.8GPa and 3.55MPam1/2, respectively. The erosion resistance ability of ZrO2p(3Y)/BN-SiO2 ceramic composites rise gradually with the sintering temperature increasing, and the erosion rate of the ceramic composite sintered at 1800°C is 8.03×10-3mm/h.

Effect of sintering conditions on the electrical-transport properties of the SrZrO3-based protonic ceramic electrolyser membrane

NASA Astrophysics Data System (ADS)

Heras-Juaristi, Gemma; Pérez-Coll, Domingo; Mather, Glenn C.

2016-11-01

The effects of sintering temperature and addition of 4 mol.% ZnO as sintering additive on the crystal structure, microstructure and electrical properties of SrZr0.9Y0.1O3-δ are reported. The presence of ZnO as sintering aid brings about high densification at 1300 °C (relative density ∼97%); gas-tightness is not achieved for ZnO-free samples sintered below 1600 °C. Bulk conductivity (σB) is considerably higher in wet and dry O2 on doping with ZnO, but only slight variations of σB with sintering temperature are observed for the Zn-containing phases. Similarly, the apparent grain-boundary conductivities are much greater for the Zn-doped samples. The grain-boundary volume and accompanying resistances are much reduced on sintering at 1500 °C with ZnO addition in comparison to Zn-modified samples sintered below 1500 °C, with only minor changes in grain-boundary relaxation frequency observed. Conversely, in comparison to the undoped sample with sintering temperature of 1600 °C, there is an enormous improvement in the specific grain-boundary conductivity of two orders of magnitude for the ZnO-containing samples. Analysis on the basis of the core space-charge-layer model relates the enhancement of the grain-boundary transport to a higher concentration of charge carriers in the space-charge layer and associated lower potential barrier heights.

Measured and calculated fast neutron spectra in a depleted uranium and lithium hydride shielded reactor

NASA Technical Reports Server (NTRS)

Lahti, G. P.; Mueller, R. A.

1973-01-01

Measurements of MeV neutron were made at the surface of a lithium hydride and depleted uranium shielded reactor. Four shield configurations were considered: these were assembled progressively with cylindrical shells of 5-centimeter-thick depleted uranium, 13-centimeter-thick lithium hydride, 5-centimeter-thick depleted uranium, 13-centimeter-thick lithium hydride, 5-centimeter-thick depleted uranium, and 3-centimeter-thick depleted uranium. Measurements were made with a NE-218 scintillation spectrometer; proton pulse height distributions were differentiated to obtain neutron spectra. Calculations were made using the two-dimensional discrete ordinates code DOT and ENDF/B (version 3) cross sections. Good agreement between measured and calculated spectral shape was observed. Absolute measured and calculated fluxes were within 50 percent of one another; observed discrepancies in absolute flux may be due to cross section errors.

Microcrystalline silicon growth for heterojunction solar cells

NASA Technical Reports Server (NTRS)

Iles, P. A.; Leung, D. C.; Fang, P. H.

1983-01-01

A total of sixteen runs of e-beam vacuum deposition of p type microcrystalline Si (m-Si) films were attempted on n type or p-n junction single crystalline Si (C-Si) substrates. The m-Si film thickness varied from .15 to .7 um and metal contacts were deposited after plasma hydrogenation. The p-m-Si on n-c-Si structure had a Voc of up to 490 m V while no Voc improvements were observed in the p-m-Si on p-n C-Si structure against p-n controls. Both CFF and Jsc were lower than control. Possible problem areas were interfaced between m-Si and C-si and the back contacts due to lack of sintering for fear of dehydrogenation.

High temperature structural insulating material

DOEpatents

Chen, W.Y.

1984-07-27

A high temperature structural insulating material useful as a liner for cylinders of high temperature engines through the favorable combination of high service temperature (above about 800/sup 0/C), low thermal conductivity (below about 0.2 W/m/sup 0/C), and high compressive strength (above about 250 psi). The insulating material is produced by selecting hollow ceramic beads with a softening temperature above about 800/sup 0/C, a diameter within the range of 20-200 ..mu..m, and a wall thickness in the range of about 2 to 4 ..mu..m; compacting the beads and a compatible silicate binder composition under pressure and sintering conditions to provide the desired structural form with the structure having a closed-cell, compact array of bonded beads.

Ion beam sputter target and method of manufacture

DOE Office of Scientific and Technical Information (OSTI.GOV)

Higdon, Clifton; Elmoursi, Alaa A.; Goldsmith, Jason

A target for use in an ion beam sputtering apparatus made of at least two target tiles where at least two of the target tiles are made of different chemical compositions and are mounted on a main tile and geometrically arranged on the main tile to yield a desired chemical composition on a sputtered substrate. In an alternate embodiment, the tiles are of varied thickness according to the desired chemical properties of the sputtered film. In yet another alternate embodiment, the target is comprised of plugs pressed in a green state which are disposed in cavities formed in a mainmore » tile also formed in a green state and the assembly can then be compacted and then sintered.« less

Alternate methods of applying diffusants to silicon solar cells. [screen printing of thick-film paste materials and vapor phase transport from solid sources

NASA Technical Reports Server (NTRS)

Brock, T. W.; Field, M. B.

1979-01-01

Low-melting phosphate and borate glasses were screen printed on silicon wafers and heated to form n and p junctions. Data on surface appearance, sheet resistance and junction depth are presented. Similar data are reported for vapor phase transport from sintered aluminum metaphosphate and boron-containing glass-ceramic solid sources. Simultaneous diffusion of an N(+) layer with screen-printed glass and a p(+) layer with screen-printed Al alloy paste was attempted. No p(+) back surface field formation was achieved. Some good cells were produced but the heating in an endless-belt furnace caused a large scatter in sheet resistance and junction depth for three separate lots of wafers.

Effect of lifestyle interventions with or without metformin therapy on serum levels of osteoprotegerin and receptor activator of nuclear factor kappa B ligand in patients with prediabetes.

PubMed

Arslan, Muyesser Sayki; Tutal, Esra; Sahin, Mustafa; Karakose, Melia; Ucan, Bekir; Ozturk, Gulfer; Cakal, Erman; Biyikli Gencturk, Zeynep; Ozbek, Mustafa; Delibasi, Tuncay

2017-02-01

Osteoprotegerin has been shown to be increased in cardiovascular disorders and type 2 diabetes mellitus. Prediabetes represents a high risk condition for diabetes and diabetic complications. Therefore, we aimed to find the relationship between prediabetes and osteoprotegerin with nuclear factor-B ligand, carotid intima media thickness, and metabolic markers. A total of 54 participants with prediabetes including impaired fasting glucose (n = 21), impaired glucose tolerance (n = 8), impaired fasting glucose and impaired glucose tolerance (n = 25), and 60 healthy individuals as a control were admitted to the study. Metabolic and anthropometric parameters, insulin resistance variables, osteoprotegerin, and nuclear factor-B ligand markers, carotid intima media thickness were examined at baseline for all participants. To evaluate the effect of therapy we determined the same parameters after the end of the study. Measurements of waist circumference, body mass index, body fat percentage and levels of fasting blood glucose, fasting insulin, homeostatic model assessment of insulin resistance, triglyceride levels and hsCRP and carotid intima media thickness were significantly higher in patients with prediabetes (p < 0.05). We also found higher osteoprotegerin and lower nuclear factor-B ligand levels in patients than in controls however, the value was non-significant (p > 0.05). Patients with prediabetes were under lifestyle interventions with (group 1, n = 33) or without metformin (group 2, n = 21) therapy. Baseline anthropometric and metabolic characteristics were not found statistically different in group 1 and group 2. Mean follow up period of the patients were 7.9 ± 2.2 month (min-max: 6-12 months). After the follow up period we evaluated the same parameters and found significant differences between waist circumference, body mass index, body fat percentage, fasting insulin, homeostatic model assessment of insulin resistance, and osteoprotegerin levels (p < 0.05). However, carotid intima media thickness, and nuclear factor-B ligand levels significantly different only in the group treated with metformin (p < 0.05). We also compared the variables after the treatment period with the control group and found significantly lower levels in terms of fasting insulin, homeostatic model assessment of insulin resistance, waist circumference, body mass index, body fat percentage, carotid intima media thickness, osteoprotegerin, and nuclear factor-B ligand values (p < 0.05). Correlation analysis revealed a negative relationship between nuclear factor-B ligand and body mass index, and body fat percentage in group 1 (p = 0.05, r = -0.646, p = 0.01, r = -0.585). Therapy of prediabetes was associated with a significant decrease in osteoprotegerin and certain metabolic variables together with an increase in nuclear factor-B ligand levels particularly in patients with under metformin therapy.

Integrated Airborne and In-Situ Measurements over Land-Fast Ice near Barrow, AK

NASA Astrophysics Data System (ADS)

Brozena, J. M.; Gardner, J. M.; Liang, R.; Vermillion, M.; Ball, D.; Stoudt, C. A.; Geiger, C. A.; Woods, J. E.; Samluk, J.; Deliberty, T. L.

2013-12-01

During March of 2013, the Naval Research Laboratory, the University of Delaware and the US Naval Academy collected an integrated set of measurements over the largely floating, but land-fast ice near the coast of Barrow, AK. The purpose of the collection was to compare airborne remote sensing methods of collection to in-situ ground-truth measurements. Airborne measurements include scanning LiDAR (Riegl Q 680i), digital photogrammetry (Applanix DSS-439) and a short-pulse (~ 1 nsec) 10 GHz radar altimeter. The LiDAR measures total freeboard (ice + snow) referenced to leads in the ice. The radar measures approximate ice freeboard with the difference with the LiDAR providing an estimate of snow thickness. The freeboard measurements are aimed at estimating ice thickness via estimates of densities and isostasy. The photogrammetry was used to measure ice motion over free-floating sea-ice, but provided only a velocity calibration and general situational awareness over the land-fast ice. Ground measurements were collected along a transect, and included boreholes, snow-thickness (Magnaprobe), and ice thickness (EM31). Airborne data were collected on six overflights of this transect over a three week period. LiDAR swath widths ranged from 200-300m (depending on altitude) and encompassed three grounded ridges which remained essentially stationary over the collection period, that together with the shoreline, provided fixed reference points to compare the heights of the floating ice that varied with the tide (and to some extent the snow conditions). Sampling size or 'footprint' plays a critical role in the attempt to compare in-situ measurements with airborne (or satellite) measurements. Boreholes are point measurements and are difficult enough to obtain, that only a limited number are practical during a survey period. EM31 and Magnaprobe instrumentation allows collection of snow and ice thickness along one-dimensional profiles, and several adjacent profiles can be collected to approximate a two-dimensional swath, assuming that the spacing between profiles does not lead to unacceptable aliasing. For this project we collected two em31 profiles roughly 3-5m apart and two profiles of Magnaprobe snow thickness with separation varying from 1-20 m. The radar footprint is ~ 10-15m at our survey altitudes, and at least somewhat comparable. The LiDAR had a ground point spacing of ~25 cm and so easily encompassed the EM31, Magnaprobe and radar data. Measured snow thickness was minimal, averaging 9 cm on the date of the first collection and 12 cm on the second. Airborne radar data were compared to the LiDAR by applying a circular, weighted kernel to the LiDAR measurements surrounding the radar profile and commensurate in diameter to the radar footprint. Estimated snow thickness is then obtained from the difference of the radar and averaged LiDAR. Ice thickness was then calculated from the freeboard measurements and compared to the boreholes. Using these data sets we hope to address important questions such as: How can we improve co-registration between ground and airborne campaigns by taking advantage of land-fast ice as a non-moving ice field? How can we improve co-registration on drift ice by building from such activities? Is there spatial aliasing of sea ice at different resolutions and if so, what is the impact on sea ice volume and ice thickness distribution?

A Fast and Accurate Method of Radiation Hydrodynamics Calculation in Spherical Symmetry

NASA Astrophysics Data System (ADS)

Stamer, Torsten; Inutsuka, Shu-ichiro

2018-06-01

We develop a new numerical scheme for solving the radiative transfer equation in a spherically symmetric system. This scheme does not rely on any kind of diffusion approximation, and it is accurate for optically thin, thick, and intermediate systems. In the limit of a homogeneously distributed extinction coefficient, our method is very accurate and exceptionally fast. We combine this fast method with a slower but more generally applicable method to describe realistic problems. We perform various test calculations, including a simplified protostellar collapse simulation. We also discuss possible future improvements.

FAST CHOPPER DETECTOR HOUSE, TRA665. FIRST FLOOR, PLAN AND SECTION, ...

Library of Congress Historic Buildings Survey, Historic Engineering Record, Historic Landscapes Survey

FAST CHOPPER DETECTOR HOUSE, TRA-665. FIRST FLOOR, PLAN AND SECTION, AS PROPOSED FOR MODIFICATION IN 1962. CONCRETE WALLS THREE FEET THICK. EXISTING WINDOWS IN MTR AND DETECTOR HOUSE WALLS WERE TO BE FILLED IN WITH HIGH-DENSITY BRICK. NOTE 20-METER MARK, WHERE THE FAST CHOPPER DETECTOR HAD BEEN LOCATED. F.C. TORKELSON 842-MTR-665-S-2, 4/1962. INL INDEX NO. 531-0665-60-851-150996, REV. 5. - Idaho National Engineering Laboratory, Test Reactor Area, Materials & Engineering Test Reactors, Scoville, Butte County, ID

Reactive Spark Plasma Sintering (SPS) of Nitride Reinforced Titanium Alloy Composites (Postprint)

DTIC Science & Technology

2014-08-15

AFRL-RX-WP-JA-2014-0177 REACTIVE SPARK PLASMA SINTERING (SPS) OF NITRIDE REINFORCED TITANIUM ALLOY COMPOSITES (POSTPRINT) Jaimie S...titanium–vanadium alloys, has been achieved by introducing reactive nitrogen gas during the spark plasma sintering (SPS) of blended titanium and...lcomReactive spark plasma sintering (SPS) of nitride reinforced titanium alloy compositeshttp://dx.doi.org/10.1016/j.jallcom.2014.08.049 0925-8388

The thermal stability of hydroxyapatite in biphasic calcium phosphate ceramics.

PubMed

Nilen, R W N; Richter, P W

2008-04-01

Biphasic calcium phosphate ceramics (BCP) comprising a mix of non-resorbable hydroxyapatite (HA) and resorbable beta-tricalcium phosphate (beta-TCP) are particularly suitable materials for synthetic bone substitute applications. In this study, HA synthesised by solid state reaction was mechanically mixed with beta-TCP, then sintered to form a suite of BCP materials with a wide range of HA/beta-TCP phase content ratios. The influence of sintering temperature and composition on the HA thermal stability was quantified by X-ray diffraction (XRD). The pre-sinter beta-TCP content was found to strongly affect the post-sinter HA/beta-TCP ratio by promoting the thermal decomposition of HA to beta-TCP, even at sintering temperatures as low as 850 degrees C. For BCP material with pre-sinter HA/beta-TCP = 40/60 wt%, approximately 80% of the HA decomposed to beta-TCP during sintering at 1000 degrees C. Furthermore, the HA content appeared to influence the reverse transformation of alpha-TCP to beta-TCP expected upon gradual cooling from sintering temperatures greater than 1125 degrees C. Because the HA/beta-TCP ratio dominantly determines the rate and extent of BCP resorption in vivo, the possible thermal decomposition of HA during BCP synthesis must be considered, particularly if high temperature treatments are involved.

Electrochemical corrosion and bioactivity of Ti-Nb-Sn-hydroxyapatite composites fabricated by pulse current activated sintering.

PubMed

Xiaopeng, Wang; Fantao, Kong; Biqing, Han; Yuyong, Chen

2017-11-01

Ti-Nb-Sn-hydroxyapatite (HA) composites were prepared by mechanical alloying for different times (unmilled, 4, 8 and 12h), followed by pulse current activated sintering. The effects of the milling time on the electrochemical corrosion resistance and bioactivity of the sintered Ti-35Nb-2.5Sn-15HA composites were investigated. Potentiodynamic polarization test results indicated that the sintered Ti-35Nb-2.5Sn-15HA composites exhibited higher corrosion resistance with increasing milling time. The corrosion potential and current of the Ti-35Nb-2.5Sn-15HA composite sintered by 12h milled powders were - 0.261V and 0.18μA/cm 2 , respectively, and this sintered composite showed a stable and wide passivation region. The hemolysis rate of the sintered Ti-35Nb-2.5Sn-15HA composites reduced with increasing milling time and the lowest hemolytic rate of the composites was 0.87%. In addition, the in vitro cell culture results indicated that the composite sintered by 12h milled powders had good biocompatibility. These results indicate the significant potential of Ti-35Nb-2.5Sn/xHA composites for biomedical implant applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Clean recycle and utilization of hazardous iron-bearing waste in iron ore sintering process.

PubMed

Gan, Min; Ji, Zhiyun; Fan, Xiaohui; Chen, Xuling; Zhou, Yang; Wang, Guojing; Tian, Ye; Jiang, Tao

2018-04-18

Applying recycled iron-bearing waste materials (RIM) into iron ore sintering process is the general disposal approach worldwide, while its use is still a thorny problem. Results showed that adding RIM increased contents of hazardous elements (K, Na, Pb, Zn, and Cl) in sinter product, and also enhanced emission concentration of PM 2.5 in flue gas; increasing reaction temperature, and contents of CaO & coke breeze in raw mixtures improved hazardous elements removal. Based on these features, a novel method through granulating natural iron ores and RIM separately and distributing granulated RIM in bottom sintering layers was proposed for clean RIM cycle. When recycling 5% RIM, granulating RIM separately with higher contents of CaO and coke breeze removed hazardous elements effectively, the contents of which in sinter were reduced to comparable level of the case without RIM. Moreover, distributing RIM in bottom sintering layer reached intensive release of hazardous elements and PM 2.5 during sintering, which reduced the flue gas volume needing purification by about 2/3. Through activated carbon purification, about 60% of PM 2.5 comprised high contents of hazardous elements was removed. Novel technique eliminated the negative impact of RIM and has the prospect to reach clean recycle in sinter-making plants. Copyright © 2018. Published by Elsevier B.V.

Research on High Temperature Ceramic Insulation for Electrical Conductors

NASA Technical Reports Server (NTRS)

Kreidler, Eric R.; Bhallamudi, Vidya Praveen

2001-01-01

Three methods for applying ceramic coatings to wires were examined in depth and a fourth (chemical vapor deposition) was studied briefly. CVD coatings were not reported in the thesis because it was realized early in the study that the deposition rate of the coatings was too slow to be used in a commercial process. Of the methods reported in the thesis, slurry coating was the most promising. This method consists of slowly drawing a platinum wire through a thixotropic slurry of alumina in a vehicle composed of polyvinyl butyral, methyl ethyl ketone, and toluene. The coatings produced by this method were continuous and free of cracks after sintering. The sintered coatings crack when the wire is bent around sharp corners, but most of the coating remains in place and still provides electrical insulation between the wire and any metallic structure to which the wire may be attached. The coating thickness was 0.61 mm (16 micrometers). The electrical resistivity of the intact coating was 340 M-Ohm-cm at 800 C and 23 M-Ohm-cm at 1050 C. Therefore, these coatings more than meet the electrical requirements for use in turbine engines. Although adherence of the coating to the wire was generally excellent, a problem was noted in localized areas where the coating flaked off. Further work will be needed to obtain good coating adherence along the entire length of the wire. The next most promising coatings were made by electrophoretic deposition (EPD) of Al2O3 onto platinum wires, using mixtures of ethanol and acetone as the suspending liquid. These EPD coatings were made only on short lengths of wire because the coating is too fragile to allow spooling of the wire. The worst coatings were those made by electrophoretic deposition from aqueous suspensions. Continuous slurry coating of wire was achieved, but due to lack of suitable equipment, the wire had to be cut into short lengths for sintering.

Transparent layered YAG ceramics with structured Yb doping produced via tape casting

NASA Astrophysics Data System (ADS)

Hostaša, Jan; Piancastelli, Andreana; Toci, Guido; Vannini, Matteo; Biasini, Valentina

2017-03-01

The flexibility of the ceramic production process, in particular in terms of shaping and spatial control of distribution of active ions, is one of the strong points in favor of transparent ceramics. In high power lasers in particular, where thermal management is a critical issue, the finely controlled design of spatial distribution of the doping ions within the laser gain media can reduce undesired thermally induced effects and large temperature gradients, and thus enhance the efficiency and laser beam quality especially under increased thermal load. In the present work transparent structured YAG ceramics with Yb doping were produced by tape casting followed by thermal compression of assembled tapes and sintered under high vacuum. The thermal compression of variously doped tape cast layers is a very promising method because it allows a high precision and good control over dopant distribution in the sintered material. After sintering, the distribution of Yb across the layers was characterized by SEM-EDX and the thickness of Yb diffusion zones between the layers with different Yb content was measured. Optical homogeneity was assessed by means of optical transmittance mapping of the samples and by 2D scanning of laser output. The effect of structured dopant distribution on laser performance was measured in quasi-CW and CW regime with different duty factors. Slope efficiency values higher than 50% were measured both in quasi-CW and in CW lasing conditions. The results are in good agreement with previously calculated predictions, confirming the beneficial effect of structured doping on laser performances and enlightening the impact of the residual scattering losses. Compared to other processing methods, such as the pressing of granulated powders, tape casting followed by thermal compression leads to straight and narrow interfaces between layers with different composition and allows to build structures composed of extremely thin layers with defined dopant content.

X-ray shielding behaviour of kaolin derived mullite-barites ceramic

NASA Astrophysics Data System (ADS)

Ripin, A.; Mohamed, F.; Choo, T. F.; Yusof, M. R.; Hashim, S.; Ghoshal, S. K.

2018-03-01

Mullite-barite ceramic (MBC) is an emergent material for effective shielding of redundant ionizing radiation exposure. The composition dependent mechanical, thermal, and microstructure properties of MBC that makes MBC a high performing novel radiation shielding candidate remained unexplored. This paper examines the possibility of exploiting Malaysian kaolin (AKIM-35) and barite (BaSO4) derived ceramic (MBC) system for X-ray shielding operation. Using conventional pressing and sintering method six ceramic samples are prepared by mixing AKIM-35 with barite at varying contents (0, 10, 20, 30, 40 and 50 wt%). Synthesized pressed mixtures are calcined at 400 °C for 30 min and then sintered to 1300 °C for 120 min at a heating rate of 10 °C/min. Sintered samples are characterized via X-ray Diffraction (XRD), Field Emission Scanning Electron Microscope (FESEM), lead equivalent (LE), uniformity and dose reduction analyses. XRD pattern of prepared ceramics revealed the presence of monoclinic barium alumino-silicate (BAS) and orthorhombic mullite as major shielding phases together with other minor phase of barite and hexagonal quartz (SiO2) structures. Furthermore, FESEM images of ceramics (between 0 and 30 wt%) displayed the existence of compacted monoclinic plate of BAS and acicular mullite morphology (ceramics at 40 and 50 wt%). Radiation tests displayed the capacity of ceramics (at 0 and 10 wt%) to shield the X-ray radiation emanated at tube potential range of 50-120 kV. The highest radiation attenuation is ascertained at 70 kV where the dose is reduced remarkably between 99.11% and 97.42%. Ceramics at 0 and 10 wt% demonstrated the highest lead (Pb) equivalent thickness (LE) of 0.44 mm and 0.34 mm, respectively. It is established that such MBC may contribute towards the development of shielding material against ionizing radiation in diagnostic radiology (X-ray) dose range.