Predicting Fatigue Lives Of Metal-Matrix/Fiber Composites

NASA Technical Reports Server (NTRS)

Bartolotta, Paul A.

1994-01-01

Method of prediction of fatigue lives of intermetallic-matrix/fiber composite parts at high temperatures styled after method of universal slopes. It suffices to perform relatively small numbers of fatigue tests. Data from fatigue tests correlated with tensile-test data by fitting universal-slopes equation to both sets of data. Thereafter, universal-slopes equation used to predict fatigue lives from tensile properties.

Experimental and modeling results of creep fatigue life of Inconel 617 and Haynes 230 at 850 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xiang; Sokolov, Mikhail A; Sham, Sam

Creep fatigue testing of Ni-based superalloy Inconel 617 and Haynes 230 were conducted in the air at 850 C. Tests were performed with fully reversed axial strain control at a total strain range of 0.5%, 1.0% or 1.5% and hold time at maximum tensile strain for 3, 10 or 30 min. In addition, two creep fatigue life prediction methods, i.e. linear damage summation and frequency-modified tensile hysteresis energy modeling, were evaluated and compared with experimental results. Under all creep fatigue tests, Haynes 230 performed better than Inconel 617. Compared to the low cycle fatigue life, the cycles to failure formore » both materials decreased under creep fatigue test conditions. Longer hold time at maximum tensile strain would cause a further reduction in both material creep fatigue life. The linear damage summation could predict the creep fatigue life of Inconel 617 for limited test conditions, but considerably underestimated the creep fatigue life of Haynes 230. In contrast, frequency-modified tensile hysteresis energy modeling showed promising creep fatigue life prediction results for both materials.« less

Evaluation of fatigue life of CRM-reinforced SMA and its relationship to dynamic stiffness.

PubMed

Mashaan, Nuha Salim; Karim, Mohamed Rehan; Abdel Aziz, Mahrez; Ibrahim, Mohd Rasdan; Katman, Herda Yati; Koting, Suhana

2014-01-01

Fatigue cracking is an essential problem of asphalt concrete that contributes to pavement damage. Although stone matrix asphalt (SMA) has significantly provided resistance to rutting failure, its resistance to fatigue failure is yet to be fully addressed. The aim of this study is to evaluate the effect of crumb rubber modifier (CRM) on stiffness and fatigue properties of SMA mixtures at optimum binder content, using four different modification levels, namely, 6%, 8%, 10%, and 12% CRM by weight of the bitumen. The testing undertaken on the asphalt mix comprises the dynamic stiffness (indirect tensile test), dynamic creep (repeated load creep), and fatigue test (indirect tensile fatigue test) at temperature of 25°C. The indirect tensile fatigue test was conducted at three different stress levels (200, 300, and 400 kPa). Experimental results indicate that CRM-reinforced SMA mixtures exhibit significantly higher fatigue life compared to the mixtures without CRM. Further, higher correlation coefficient was obtained between the fatigue life and resilient modulus as compared to permanent strain; thus resilient modulus might be a more reliable indicator in evaluating the fatigue life of asphalt mixture.

Experimental and modeling results of creep-fatigue life of Inconel 617 and Haynes 230 at 850 °C

NASA Astrophysics Data System (ADS)

Chen, Xiang; Sokolov, Mikhail A.; Sham, Sam; Erdman, Donald L., III; Busby, Jeremy T.; Mo, Kun; Stubbins, James F.

2013-01-01

Creep-fatigue testing of Ni-based superalloy Inconel 617 and Haynes 230 were conducted in the air at 850 °C. Tests were performed with fully reversed axial strain control at a total strain range of 0.5%, 1.0% or 1.5% and hold time at maximum tensile strain for 3, 10 or 30 min. In addition, two creep-fatigue life prediction methods, i.e. linear damage summation and frequency-modified tensile hysteresis energy modeling, were evaluated and compared with experimental results. Under all creep-fatigue tests, Haynes 230 performed better than Inconel 617. Compared to the low cycle fatigue life, the cycles to failure for both materials decreased under creep-fatigue test conditions. Longer hold time at maximum tensile strain would cause a further reduction in both material creep-fatigue life. The linear damage summation could predict the creep-fatigue life of Inconel 617 for limited test conditions, but considerably underestimated the creep-fatigue life of Haynes 230. In contrast, frequency-modified tensile hysteresis energy modeling showed promising creep-fatigue life prediction results for both materials.

Fatigue crack identification method based on strain amplitude changing

NASA Astrophysics Data System (ADS)

Guo, Tiancai; Gao, Jun; Wang, Yonghong; Xu, Youliang

2017-09-01

Aiming at the difficulties in identifying the location and time of crack initiation in the castings of helicopter transmission system during fatigue tests, by introducing the classification diagnostic criteria of similar failure mode to find out the similarity of fatigue crack initiation among castings, an engineering method and quantitative criterion for detecting fatigue cracks based on strain amplitude changing is proposed. This method is applied on the fatigue test of a gearbox housing, whose results indicates: during the fatigue test, the system alarms when SC strain meter reaches the quantitative criterion. The afterwards check shows that a fatigue crack less than 5mm is found at the corresponding location of SC strain meter. The test result proves that the method can provide accurate test data for strength life analysis.

Effects of Acute Fatigue of the Hip Flexor Muscles on Hamstring Muscle Extensibility.

PubMed

Muyor, José M; Arrabal-Campos, Francisco M

2016-12-01

The purpose of the present study was to evaluate the influence of acute fatigue of the hip flexor muscles on scores attained in tests frequently used in literature to measure hamstring muscle extensibility, namely the passive straight leg raise (PSLR), active straight leg raise (ASLR), passive knee extension (PKE), active knee extension (AKE), sit-and-reach (SR) and toe-touch (TT) tests. A total of seventy-five healthy and recreationally active adults voluntarily participated in this study. To reach fatigue, the participants actively lifted their legs alternately as many times as possible. In the passive tests, the results were 7.10 ± 5.21° and 5.68 ± 4.54° higher (p < 0.01) for PSLR and PKE tests, respectively, after acute fatigue. However, in the ASLR test, the results were lower post-fatigue than pre-fatigue (mean difference = -5.30° ± 9.51°; p < 0.01). The AKE, SR and TT tests did not show significant differences between pre- and post-fatigue (p > 0.05). Moderate (r = 0.40) to high (r = 0.97) correlation coefficients were found, which were statistically significant among all the measured flexibility tests both pre- and post-fatigue. In conclusion, the active implication of the hip flexor muscles until reaching fatigue had acute influences on the results of the PSLR, PKE and ASLR tests, but not on the results of the AKE, SR and TT tests. It is recommended to use the AKE test to assess hamstring muscle extensibility in situations where athletes show fatigue in their hip flexor muscles.

Strain energy release rate as a function of temperature and preloading history utilizing the edge delamination fatique test method

NASA Technical Reports Server (NTRS)

Zimmerman, Richard S.; Adams, Donald F.

1989-01-01

Static laminate and tension-tension fatigue tests of IM7/8551-7 composite materials was performed. The Edge Delamination Test (EDT) was utilized to evaluate the temperature and preloading history effect on the critical strain energy release rate. Static and fatigue testing was performed at room temperature and 180 F (82 C). Three preloading schemes were used to precondition fatigue test specimens prior to performing the normal tension-tension fatigue EDT testing. Computer software was written to perform all fatigue testing while monitoring the dynamic modulus to detect the onset of delamination and record the test information for later retrieval and reduction.

Is the Sørensen test valid to assess muscle fatigue of the trunk extensor muscles?

PubMed

Demoulin, Christophe; Boyer, Mathieu; Duchateau, Jacques; Grosdent, Stéphanie; Jidovtseff, Boris; Crielaard, Jean-Michel; Vanderthommen, Marc

2016-01-01

Very few studies have quantified the degree of fatigue characterized by the decline in the maximal voluntary contraction (MVC) force of the trunk extensors induced by the widely used Sørensen test. Measure the degree of fatigue of the trunk extensor muscles induced by the Sørensen test. Eighty young healthy subjects were randomly divided into a control group (CG) and an experimental group (EG), each including 50% of the two genders. The EG performed an isometric MVC of the trunk extensors (pre-fatigue test) followed by the Sørensen test, the latter being immediately followed by another MVC (post-fatigue test). The CG performed only the pre- and post-fatigue tests without any exertion in between. The comparison of the pre- and post-fatigue tests revealed a significant (P< 0.05) decrease in MVC force normalized by body mass (-13%) in the EG, whereas a small increase occurred in the CG (+2.7%, P= 0.001). This study shows that the Sørensen test performed until failure in a young healthy population results in a reduced ability of the trunk extensor muscles to generate maximal force, and indicates that this test is valid for the assessment of fatigue in trunk extensor muscles.

Evaluation of Fatigue Life of CRM-Reinforced SMA and Its Relationship to Dynamic Stiffness

PubMed Central

Mashaan, Nuha Salim; Karim, Mohamed Rehan; Abdel Aziz, Mahrez; Ibrahim, Mohd Rasdan; Katman, Herda Yati

2014-01-01

Fatigue cracking is an essential problem of asphalt concrete that contributes to pavement damage. Although stone matrix asphalt (SMA) has significantly provided resistance to rutting failure, its resistance to fatigue failure is yet to be fully addressed. The aim of this study is to evaluate the effect of crumb rubber modifier (CRM) on stiffness and fatigue properties of SMA mixtures at optimum binder content, using four different modification levels, namely, 6%, 8%, 10%, and 12% CRM by weight of the bitumen. The testing undertaken on the asphalt mix comprises the dynamic stiffness (indirect tensile test), dynamic creep (repeated load creep), and fatigue test (indirect tensile fatigue test) at temperature of 25°C. The indirect tensile fatigue test was conducted at three different stress levels (200, 300, and 400 kPa). Experimental results indicate that CRM-reinforced SMA mixtures exhibit significantly higher fatigue life compared to the mixtures without CRM. Further, higher correlation coefficient was obtained between the fatigue life and resilient modulus as compared to permanent strain; thus resilient modulus might be a more reliable indicator in evaluating the fatigue life of asphalt mixture. PMID:25050406

Fatigue Strength and Related Characteristics of Aircraft Joints I : Comparison of Spot-Weld and Rivet Patterns in 24s-t Alclad and 75s-t Alclad

NASA Technical Reports Server (NTRS)

Russell, H W; Jackson, L R; Grover, H J; Beaver, W W

1944-01-01

Report contains detailed results of a number of fatigue tests on spot-welded joints in aluminum alloys. The tests described include: (1) fatigue tests on spot-welded lap joints in sheets of unequal thickness of alclad 24s-t. These tests indicate that the fatigue strength of a spot-welded joint in sheets of two different gages is slightly higher than that of a similar joint in two sheets of the thinner gage but definitely lower than that of a similar joint in two sheets of the thicker gage. (2) Fatigue tests on spot-welded alclad 75s-t spot-welded lap-joint specimens of alclad 75s-t were not any stronger in fatigue than similar specimens of alclad 24s-t. (3) Fatigue tests on lap-joint specimens spot -welded after various surface preparations--these included ac welding wire-brushed surfaces, dc welding wire-brushed surfaces, and dc welding chemically cleaned surfaces. While the ac welds were strongest statically, the dc welds on wire-brushed surfaces were strongest in fatigue. Specimens prepared in this way were very nearly as strong as the best riveted specimens tested for comparison. (4) Fatigue tests on specimens spot-welded with varying voltage so as to include a wide range of static spot-weld strengths. The fatigue strengths were in the same order as the static strengths but showed less range. (author)

Simulation of Fatigue Crack Initiation at Corrosion Pits With EDM Notches

NASA Technical Reports Server (NTRS)

Smith, Stephen W.; Newman, John A.; Piascik, Robert S.

2003-01-01

Uniaxial fatigue tests were conducted to compare the fatigue life of laboratory produced corrosion pits, similar to those observed in the shuttle main landing gear wheel bolt-hole, and an electro-discharged-machined (EDM) flaw. EDM Jaws are used to simulate corrosion pits during shuttle wheel (dynamometer) testing. The aluminum alloy, (AA 7050) laboratory fatigue tests were conducted to simulate the local stress level contained in the wheel bolt-hole. Under this high local stress condition, the EDM notch produced a fatigue life similar to test specimens containing corrosion pits of similar size. Based on the laboratory fatigue test results, the EDM Jaw (semi-circular disc shaped) produces a local stress state similar to corrosion pits and can be used to simulate a corrosion pit during the shuttle wheel dynamometer tests.

High temperature, low-cycle fatigue of copper-base alloys for rocket nozzles. Part 2: Strainrange partitioning and low-cycle fatigue results at 538 deg C

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1976-01-01

Low-cycle fatigue tests of 1/2 Hard AMZIRC Copper and NARloy Z were performed in argon at 538 C to determine partitioned strain range versus life relationships. Strain-controlled low-cycle fatigue tests of a Zr-Cr-Mg copper-base alloy were also performed. Strain ranges, lower than those employed in previous tests, were imposed in order to extend the fatigue life curve out to approximately 400,000 cycles. An experimental copper alloy and an experimental silver alloy were also studied. Tensile tests were performed in air at room temperature and in argon at 538 C. Strain-controlled low-cycle fatigue tests were performed at 538 C in argon to define the fatigue life over the regime from 300 to 3,000 cycles. For the silver alloy, three additional heat treatments were introduced, and a limited evaluation of the short-term tensile and low-cycle fatigue behavior at 538 C was performed.

Notched fatigue of single crystal PWA 1480 at turbine attachment temperatures

NASA Technical Reports Server (NTRS)

Meyer, T. G.; Nissley, D. M.; Swanson, G. A.

1989-01-01

The focus is on the lower temperature, uncoated and notched features of gas turbine blades. Constitutive and fatigue life prediction models applicable to these regions are being developed. Fatigue results are presented which were obtained thus far. Fatigue tests are being conducted on PWA 1480 single crystal material using smooth strain controlled specimens and three different notched specimens. Isothermal fatigue tests were conducted at 1200, 1400, and 1600 F. The bulk of the tests were conducted at 1200 F. The strain controlled tests were conducted at 0.4 percent per second strain rate and the notched tests were cycled at 1.0 cycle per second. A clear orientation dependence is observed in the smooth strain controlled fatigue results. The fatigue lifes of the thin, mild notched specimens agree fairly well with this smooth data when elastic stress range is used as a correlating parameter. Finite element analyses were used to calculate notch stresses. Fatigue testing will continue to further explore the trends observed thus far. Constitutive and life prediction models are being developed.

Prediction of Mean and Design Fatigue Lives of Self Compacting Concrete Beams in Flexure

NASA Astrophysics Data System (ADS)

Goel, S.; Singh, S. P.; Singh, P.; Kaushik, S. K.

2012-02-01

In this paper, result of an investigation conducted to study the flexural fatigue characteristics of self compacting concrete (SCC) beams in flexure are presented. An experimental programme was planned in which approximately 60 SCC beam specimens of size 100 × 100 × 500 mm were tested under flexural fatigue loading. Approximately 45 static flexural tests were also conducted to facilitate fatigue testing. The flexural fatigue and static flexural strength tests were conducted on a 100 kN servo-controlled actuator. The fatigue life data thus obtained have been used to establish the probability distributions of fatigue life of SCC using two-parameter Weibull distribution. The parameters of the Weibull distribution have been obtained by different methods of analysis. Using the distribution parameters, the mean and design fatigue lives of SCC have been estimated and compared with Normally vibrated concrete (NVC), the data for which have been taken from literature. It has been observed that SCC exhibits higher mean and design fatigue lives compared to NVC.

Detecting Gear Tooth Fatigue Cracks in Advance of Complete Fracture

NASA Technical Reports Server (NTRS)

Zakrajsek, James J.; Lewicki, David G.

1996-01-01

Results of using vibration-based methods to detect gear tooth fatigue cracks are presented. An experimental test rig was used to fail a number of spur gear specimens through bending fatigue. The gear tooth fatigue crack in each test was initiated through a small notch in the fillet area of a tooth on the gear. The primary purpose of these tests was to verify analytical predictions of fatigue crack propagation direction and rate as a function of gear rim thickness. The vibration signal from a total of three tests was monitored and recorded for gear fault detection research. The damage consisted of complete rim fracture on the two thin rim gears and single tooth fracture on the standard full rim test gear. Vibration-based fault detection methods were applied to the vibration signal both on-line and after the tests were completed. The objectives of this effort were to identify methods capable of detecting the fatigue crack and to determine how far in advance of total failure positive detection was given. Results show that the fault detection methods failed to respond to the fatigue crack prior to complete rim fracture in the thin rim gear tests. In the standard full rim gear test all of the methods responded to the fatigue crack in advance of tooth fracture; however, only three of the methods responded to the fatigue crack in the early stages of crack propagation.

Investigating the effects of maximal anaerobic fatigue on dynamic postural control using the Y-Balance Test.

PubMed

Johnston, William; Dolan, Kara; Reid, Niamh; Coughlan, Garrett F; Caulfield, Brian

2018-01-01

The Y Balance Test is one of the most commonly used dynamic balance assessments, providing an insight into the integration of the sensorimotor subsystems. In recent times, there has been an increase in interest surrounding it's use in various clinical populations demonstrating alterations in motor function. Therefore, it is important to examine the effect physiological influences such as fatigue play in dynamic postural control, and establish a timeframe for its recovery. Descriptive laboratory study. Twenty male and female (age 23.75±4.79years, height 174.12±8.45cm, mass 69.32±8.76kg) partaking in competitive sport, completed the Y Balance Test protocol at 0, 10 and 20min, prior to a modified 60s Wingate fatiguing protocol. Post-fatigue assessments were then completed at 0, 10 and 20 min post-fatiguing intervention. Intraclass correlation coefficients demonstrated excellent intra-session reliability (0.976-0.982) across the three pre-fatigue YBT tests. Post-hoc paired sample t-tests demonstrated that all three reach directions demonstrated statistically significant differences between pre-fatigue and the first post-fatigue measurement (anterior; p=0.019, posteromedial; p=0.019 & posterolateral; p=0.003). The anterior reach direction returned to pre-fatigue levels within 10min (p=0.632). The posteromedial reach direction returned to pre-fatigue levels within 20min (p=0.236), while the posterolateral direction maintained a statistically significant difference at 20min (p=0.023). Maximal anaerobic fatigue has a negative effect on normalised Y balance test scores in all three directions. Following the fatiguing protocol, dynamic postural control returns to pre-fatigue levels for the anterior (<10min), posteromedial (<20min) and posterolateral (>20min). Copyright © 2017 Sports Medicine Australia. Published by Elsevier Ltd. All rights reserved.

Comments on the origin of acoustic emission in fatigue testing of aluminum alloys

NASA Astrophysics Data System (ADS)

Heiple, C. R.; Carpenter, S. H.; Armentrout, D. L.

The size of acoustic emission (AE) signals expected from inclusion fracture during fatigue testing of 7075 aluminum has been estimated on the basis of previous measurements of AE produced by the fracture of boron particles incorporated into 2219 aluminum. The AF signal size expected from deformation in the plastic zone ahead of the fatigue crack was estimated from the results of tensile tests on 7075 aluminum. The signals predicted from both processes are near or below the noise level in the fatigue experiments and are therefore far too small to account for the signals actually observed. Nearly simultaneous fracture of multiple inclusions could produce signals as large as those observed in fatigue tests of 7075 aluminum, however, fatigue tests of 7050 aluminum produced signals as large or larger than in 7075. Since 7050 has substantially fewer inclusions than 7075, the simultaneous failure of multiple inclusions is unlikely to be a major AE source in fatigue testing of either aluminum alloy. Thus, the most probable source of acoustic emission during fatigue testing of 7075 and 7050 aluminum is the crack advance itself. The measured crack advance per cycle is large enough to release sufficient elastic energy to account for the AE signals observed.

Development of a remote-controlled fatigue test machine using a laser extensometer for investigation of irradiation effect on fatigue properties

NASA Astrophysics Data System (ADS)

Yonekawa, M.; Ishii, T.; Ohmi, M.; Takada, F.; Hoshiya, T.; Niimi, M.; Ioka, I.; Miwa, Y.; Tsuji, H.

2002-12-01

In order to investigate effects of neutron irradiation on fatigue properties of nuclear materials, a remote-controlled high temperature fatigue test machine was developed at the hot laboratory of the Japan Materials Testing Reactor (JMTR) in the Japan Atomic Energy Research Institute (JAERI). A small-sized fatigue specimen having double blades to measure strain with a laser extensometer was designed for this machine. A strain amplitude in fatigue tests of a completely reversed push-pull type using a triangular wave was controlled with an accuracy of ±3% of the total strain range during test. Low cycle fatigue tests of type 304 stainless steel irradiated in JMTR at 823 K up to a fast neutron fluence of 1×10 25 n/m 2 ( E>1 MeV) were performed in total strain ranges of 0.7-1.4% at 823 K using the designed small-sized specimens.

75 FR 75882 - Airworthiness Directives; British Aerospace Regional Aircraft Models Jetstream Series 3101 and...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-12-07

... describes the unsafe condition as: As a result of the fatigue-testing programme on the Jetstream fatigue... result of the fatigue-testing programme on the Jetstream fatigue test specimen, it has been identified....S. registry. We also estimate that it will take about 15 work-hours per product to comply with the...

A literature review and inventory of the effects of environment on the fatigue behavior of metals

NASA Technical Reports Server (NTRS)

Hudson, C. M.; Seward, S. K.

1976-01-01

The current state of knowledge of the effects of gas environments (at atmospheric pressure and below) on the fatigue behavior of metals is reviewed. Among the topics considered are the mechanisms proposed to explain the differences observed in the fatigue behavior of vacuum- and air-tested specimens, the effects of environment on the surface topography of fatigue cycled specimens, the effect of environment on the various phases of the fatigue phenomenon, the effect of prolonged exposure to vacuum on fatigue life, the variation of fatigue life with decreasing gas pressure, and gas evolution during fatigue cycling. Analysis of the findings of this review indicates that hydrogen embrittlement is primarily responsible for decreased fatigue resistance in humid environments, and that dislocations move more easily during tests in vacuum than during test in air. It was found that fatigue cracks generally initiated and propagated more rapidly in air than in vacuum. Prolonged exposure to vacuum does not adversely affect fatigue resistance. The variation of fatigue life with decreasing gas pressure is sometimes stepped and sometimes continuous.

Fatigue Behavior of Steel Fiber Reinforced High-Strength Concrete under Different Stress Levels

NASA Astrophysics Data System (ADS)

Zhang, Chong; Gao, Danying; Gu, Zhiqiang

2017-12-01

The investigation was conducted to study the fatigue behavior of steel fiber reinforced high-strength concrete (SFRHSC) beams. A series of 5 SFRHSC beams was conducted flexural fatigue tests at different stress level S of 0.5, 0.55, 0.6, 0.7 and 0.8 respectively. Static test was conducted to determine the ultimate static capacity prior to fatigue tests. Fatigue modes and S-N curves were analyzed. Besides, two fatige life prediction model were analyzed and compared. It was found that stress level S significantly influenced the fatigue life of SFRHSC beams and the fatigue behavior of SFRHSC beams was mainly determined by the tensile reinforcement.

Tension and fatigue behavior of 316LVM 1x7 multi-strand cables used as implantable electrodes.

PubMed

Lewandowski, John J; Varadarajan, Ravikumar; Smith, Brian; Tuma, Chris; Shazly, Mostafa; Vatamanu, Luciano O

2008-07-15

The mechanical behavior of 316LVM 1x7 cables were evaluated in uniaxial tension, and in cyclic strain-controlled fatigue with the use of a Flex tester operated to provide fully reversed bending fatigue. The magnitude of cyclic strains imparted to each cable tested was controlled via the use of different diameter mandrels. Smaller diameter mandrels produced higher values of cyclic strain and lower fatigue life. Multiple samples were tested and analyzed via scanning electron microscopy. The fatigue results were analyzed via a Coffin-Manson-Basquin approach and compared to fatigue data obtained from the literature where testing was conducted on similar materials, but under rotating bending fatigue conditions.

Fatigue Life Methodology for Bonded Composite Skin/Stringer Configurations

NASA Technical Reports Server (NTRS)

Krueger, Ronald; Paris, Isabelle L.; OBrien, T. Kevin; Minguet, Pierre J.

2001-01-01

A methodology is presented for determining the fatigue life of composite structures based on fatigue characterization data and geometric nonlinear finite element (FE) analyses. To demonstrate the approach, predicted results were compared to fatigue tests performed on specimens which represented a tapered composite flange bonded onto a composite skin. In a first step, tension tests were performed to evaluate the debonding mechanisms between the flange and the skin. In a second step, a 2D FE model was developed to analyze the tests. To predict matrix cracking onset, the relationship between the tension load and the maximum principal stresses transverse to the fiber direction was determined through FE analysis. Transverse tension fatigue life data were used to -enerate an onset fatigue life P-N curve for matrix cracking. The resulting prediction was in good agreement with data from the fatigue tests. In a third step, a fracture mechanics approach based on FE analysis was used to determine the relationship between the tension load and the critical energy release rate. Mixed mode energy release rate fatigue life data were used to create a fatigue life onset G-N curve for delamination. The resulting prediction was in good agreement with data from the fatigue tests. Further, the prediction curve for cumulative life to failure was generated from the previous onset fatigue life curves. The results showed that the methodology offers a significant potential to Predict cumulative fatigue life of composite structures.

Energy-based fatigue model for shape memory alloys including thermomechanical coupling

NASA Astrophysics Data System (ADS)

Zhang, Yahui; Zhu, Jihong; Moumni, Ziad; Van Herpen, Alain; Zhang, Weihong

2016-03-01

This paper is aimed at developing a low cycle fatigue criterion for pseudoelastic shape memory alloys to take into account thermomechanical coupling. To this end, fatigue tests are carried out at different loading rates under strain control at room temperature using NiTi wires. Temperature distribution on the specimen is measured using a high speed thermal camera. Specimens are tested to failure and fatigue lifetimes of specimens are measured. Test results show that the fatigue lifetime is greatly influenced by the loading rate: as the strain rate increases, the fatigue lifetime decreases. Furthermore, it is shown that the fatigue cracks initiate when the stored energy inside the material reaches a critical value. An energy-based fatigue criterion is thus proposed as a function of the irreversible hysteresis energy of the stabilized cycle and the loading rate. Fatigue life is calculated using the proposed model. The experimental and computational results compare well.

Spectrum Fatigue of 7075-T651 Aluminum Alloy under Overloading and Underloading

DTIC Science & Technology

2016-03-15

underload, stress ratio, and environment on fatigue crack growth. Fatigue crack growth tests were conducted with a 7075-T651 aluminum alloy under constant...the UniGrow equation, the variation of crack length with number of loading cycle was predicted. The prediction and the fatigue test life were found to...Standard Form 298 (Rev. 8-98) Prescribed by ANSI Std. Z39-18 REPORT NO. NAWCADPAX/TIM-2015/282 ii SUMMARY Fatigue tests of 7075-T651

Investigation of Gear and Bearing Fatigue Damage Using Debris Particle Distributions

NASA Technical Reports Server (NTRS)

Dempsey, Paula J.; Lewicki, David G.; Decker, Harry J.

2004-01-01

A diagnostic tool was developed for detecting fatigue damage to spur gears, spiral bevel gears, and rolling element bearings. This diagnostic tool was developed and evaluated experimentally by collecting oil debris data from fatigue tests performed in the NASA Glenn Spur Gear Fatigue Rig, Spiral Bevel Gear Test Facility, and the 500hp Helicopter Transmission Test Stand. During each test, data from an online, in-line, inductance type oil debris sensor was monitored and recorded for the occurrence of pitting damage. Results indicate oil debris alone cannot discriminate between bearing and gear fatigue damage.

Influence of sustained submaximal clenching fatigue test on electromyographic activity and maximum voluntary bite forces in healthy subjects and patients with temporomandibular disorders.

PubMed

Xu, L; Fan, S; Cai, B; Fang, Z; Jiang, X

2017-05-01

This study aimed to investigate whether the fatigue induced by sustained motor task in the jaw elevator muscles differed between healthy subjects and patients with temporomandibular disorder (TMD). Fifteen patients with TMD and thirteen age- and sex-matched healthy controls performed a fatigue test consisting of sustained clenching contractions at 30% maximal voluntary clenching intensity until test failure (the criterion for terminating the fatigue test was when the biting force decreased by 10% or more from the target force consecutively for >3 s). The pre- and post-maximal bite forces (MBFs) were measured. Surface electromyographic signals were recorded from the superficial masseter muscles and anterior temporal muscles bilaterally, and the median frequency at the beginning, middle and end of the fatigue test was calculated. The duration of the fatigue test was also quantified. Both pre- and post-MBFs were lower in patients with TMD than in controls (P < 0·01). No significant difference was found in the percentage change in MBF between groups. The duration of the fatigue test in TMD patients was significantly shorter than that of the controls (P < 0·05). Our results suggest that, compared to healthy subjects, patients with TMD become more easily fatigued, but the electromyographic activation process during the fatigue test is similar between healthy subjects and patients with TMD. However, the mechanisms involved in this process remain unclear, and further research is warranted. © 2017 John Wiley & Sons Ltd.

Thermal-Mechanical Fatigue Testing of a Titanium-Aluminide Alloy.

DTIC Science & Technology

1987-12-01

DIMSTRIBUTION STA Approved for pubi robing e% dQ *- AFIT/GAB/AA/87D-18 THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS John J...THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS Presented to the Faculty of the School of Engineering of the Air Force Institute...develop a Thermal-Mechanical Fatigue (TMF) testing system for titanium - aluminide compact tension specimens. I could not have accomplished this without the

Single-leg hop testing following fatiguing exercise: reliability and biomechanical analysis.

PubMed

Augustsson, J; Thomeé, R; Lindén, C; Folkesson, M; Tranberg, R; Karlsson, J

2006-04-01

A fatiguing exercise protocol was combined with single-leg hop testing to improve the possibilities of evaluating the effects of training or rehabilitation interventions. In the first test-retest experiment, 11 healthy male subjects performed two trials of single-leg hops under three different test conditions: non-fatigued and following fatiguing exercise, which consisted of unilateral weight machine knee extensions at 80% and 50%, respectively, of 1 repetition maximum (1 RM) strength. Intraclass correlation coefficients ranged from 0.75 to 0.98 for different hop test conditions, indicating that all tests were reliable. For the second experiment, eight healthy male subjects performed the fatiguing exercise protocol to investigate how fatigue influences lower-extremity joint kinematics and kinetics during single-leg hops. Hip, knee and ankle joint angles, moments and powers, as well as ground-reaction forces were recorded with a six-camera, motion-capture system and a force platform. Recovery of hop performance following the fatiguing exercise was also measured. During the take-off for the single-leg hops, hip and knee flexion angles, generated powers for the knee and ankle joints, and ground-reaction forces decreased for the fatigued hop conditions compared with the non-fatigued condition (P<0.05). Compared with landing during the non-fatigued condition, hip moments and ground-reaction forces were lower for the fatigued hop conditions (P<0.05). The negative joint power was two to three times greater for the knee than for the hip and five to 10 times greater for the knee than for the ankle during landing for all test conditions (P<0.05). Most measured variables had recovered three minutes post-exercise. It is concluded that the fatiguing exercise protocol combined with single-leg hop testing was a reliable method for investigating functional performance under fatigued test conditions. Further, subjects utilized an adapted hop strategy, which employed less hip and knee flexion and generated powers for the knee and ankle joints during take-off, and less hip joint moments during landing under fatigued conditions. The large negative power values observed at the knee joint during the landing phase of the single-leg hop, during which the quadriceps muscle activates eccentrically, indicate that not only hop distance but also the ability to perform successful landings should be investigated when assessing dynamic knee function.

Experimental Investigation and Finite Element Analysis on Fatigue Behavior of Aluminum Alloy 7050 Single-Lap Joints

NASA Astrophysics Data System (ADS)

Zhou, Bing; Cui, Hao; Liu, Haibo; Li, Yang; Liu, Gaofeng; Li, Shujun; Zhang, Shangzhou

2018-03-01

The fatigue behavior of single-lap four-riveted aluminum alloy 7050 joints was investigated by using high-frequency fatigue test and scanning electron microscope (SEM). Stress distributions obtained by finite element (FE) analysis help explain the fatigue performance. The fatigue test results showed that the fatigue lives of the joints depend on cold expansion and applied cyclic loads. FE analysis and fractography indicated that the improved fatigue lives can be attributed to the reduction in maximum stress and evolution of fatigue damage at the critical location. The beneficial effects of strengthening techniques result in tearing ridges or lamellar structure on fracture surface, decrease in fatigue striations spacing, delay of fatigue crack initiation, crack deflection in fatigue crack propagation and plasticity-induced crack closure.

Fatigue Lives Of Laser-Cut Metals

NASA Technical Reports Server (NTRS)

Martin, Michael R.

1988-01-01

Fatigue lives made to approach those attainable by traditional grinding methods. Fatigue-test specimens prepared from four metallic alloys, and material removed from specimens by manual grinding, by Nd:glass laser, and by Nd:YAG laser. Results of fatigue tests of all specimens indicated reduction of fatigue strengths of laser-fired specimens. Laser machining holds promise for improved balancing of components of gas turbines.

Cumulative Axial and Torsional Fatigue: An Investigation of Load-Type Sequencing Effects

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Bonacuse, Peter J.

2000-01-01

Cumulative fatigue behavior of a wrought cobalt-base superalloy, Haynes 188 was investigated at 538 C under various single-step sequences of axial and torsional loading conditions. Initially, fully-reversed, axial and torsional fatigue tests were conducted under strain control at 538 C on thin-walled tubular specimens to establish baseline fatigue life relationships. Subsequently, four sequences (axial/axial, torsional/torsional, axial/torsional, and torsional/axial) of two load-level fatigue tests were conducted to characterize both the load-order (high/low) and load-type sequencing effects. For the two load-level tests, summations of life fractions and the remaining fatigue lives at the second load-level were computed by the Miner's Linear Damage Rule (LDR) and a nonlinear Damage Curve Approach (DCA). In general, for all four cases predictions by LDR were unconservative. Predictions by the DCA were within a factor of two of the experimentally observed fatigue lives for a majority of the cumulative axial and torsional fatigue tests.

Rolling-element fatigue life of AMS 5749 corrosion resistant, high temperature bearing steel

NASA Technical Reports Server (NTRS)

Parker, R. J.; Hodder, R. S.

1977-01-01

The rolling element fatigue lives of AMS 5749 and AISI M-50 were compared in tests run in the five ball fatigue tester and the rolling contact fatigue tester. The effects of double vacuum melting and retained austenite on the life of AMS 5749 were determined in five ball fatigue tests. The double vacuum melting process consisted of induction vacuum melting followed by vacuum arc remelting (VIM-VAR). In the five ball tests, VIM-VAR AMS 5749 gave lives at least six times that of VIM-VAR AISI M-50. Similar tests in the rolling contact fatigue tester showed no significant difference in the lives of the two materials. The rolling element fatigue life of VIM-VAR AMS 5749 was at least 14 times that of vacuum induction melted AMS 5749. A trend toward increased rolling element fatigue life with decreased retained austenite is apparent, but the confidence that all experimental differences are significant is not great.

Fatigue and physical fitness of mildly disabled persons with multiple sclerosis: a cross-sectional study.

PubMed

Valet, Maxime; Lejeune, Thierry; Glibert, Yumiko; Hakizimana, Jean C; Van Pesch, Vincent; El Sankari, Souraya; Detrembleur, Christine; Stoquart, Gaëtan

2017-09-01

Fatigue is frequent and disabling in persons with multiple sclerosis (pwMS) with mild neurological disability. These patients also have impaired physical fitness. Whether mildly disabled pwMS are deconditioned, and this deconditioning is linked to fatigue, remains unknown. Our aim is to determine the physical fitness of mildly disabled patients with multiple sclerosis and study its relationship with perceived fatigue and to link perceived fatigue with other parameters. Twenty patients (14 women; mean age: 45.5 years) with mild disability (Expanded Disability Status Scale 0-4) underwent a 2-min walking test, Timed Up-and-Go test, aerobic capacity testing, and isometric knee extension testing to assess strength and neuromuscular fatigability. They completed questionnaires assessing perceived fatigue, psychological status, and physical activity. Correlation coefficients and multivariate regression were used to analyze the relationships among variables. Seventeen (85%) patients reported a high level of fatigue. Thirteen (65%) patients had subnormal aerobic capacity. Fatigue was weakly to moderately associated with aerobic capacity, mobility, walking capacity, depression, and neuromuscular fatigability. An association of disease duration, aerobic capacity, and the neuromuscular fatigability index explained 65.1% of fatigue. A high proportion of pwMS with mild neurological disability are fatigued and deconditioned. Perceived fatigue is linked to aerobic capacity, neuromuscular fatigability, depression, mobility, and walking capacity. Focusing on these parameters could help in the management of fatigue.

Probabilistic Flexural Fatigue in Plain and Fiber-Reinforced Concrete

PubMed Central

Ríos, José D.

2017-01-01

The objective of this work is two-fold. First, we attempt to fit the experimental data on the flexural fatigue of plain and fiber-reinforced concrete with a probabilistic model (Saucedo, Yu, Medeiros, Zhang and Ruiz, Int. J. Fatigue, 2013, 48, 308–318). This model was validated for compressive fatigue at various loading frequencies, but not for flexural fatigue. Since the model is probabilistic, it is not necessarily related to the specific mechanism of fatigue damage, but rather generically explains the fatigue distribution in concrete (plain or reinforced with fibers) for damage under compression, tension or flexion. In this work, more than 100 series of flexural fatigue tests in the literature are fit with excellent results. Since the distribution of monotonic tests was not available in the majority of cases, a two-step procedure is established to estimate the model parameters based solely on fatigue tests. The coefficient of regression was more than 0.90 except for particular cases where not all tests were strictly performed under the same loading conditions, which confirms the applicability of the model to flexural fatigue data analysis. Moreover, the model parameters are closely related to fatigue performance, which demonstrates the predictive capacity of the model. For instance, the scale parameter is related to flexural strength, which improves with the addition of fibers. Similarly, fiber increases the scattering of fatigue life, which is reflected by the decreasing shape parameter. PMID:28773123

Probabilistic Flexural Fatigue in Plain and Fiber-Reinforced Concrete.

PubMed

Ríos, José D; Cifuentes, Héctor; Yu, Rena C; Ruiz, Gonzalo

2017-07-07

The objective of this work is two-fold. First, we attempt to fit the experimental data on the flexural fatigue of plain and fiber-reinforced concrete with a probabilistic model (Saucedo, Yu, Medeiros, Zhang and Ruiz, Int. J. Fatigue, 2013, 48, 308-318). This model was validated for compressive fatigue at various loading frequencies, but not for flexural fatigue. Since the model is probabilistic, it is not necessarily related to the specific mechanism of fatigue damage, but rather generically explains the fatigue distribution in concrete (plain or reinforced with fibers) for damage under compression, tension or flexion. In this work, more than 100 series of flexural fatigue tests in the literature are fit with excellent results. Since the distribution of monotonic tests was not available in the majority of cases, a two-step procedure is established to estimate the model parameters based solely on fatigue tests. The coefficient of regression was more than 0.90 except for particular cases where not all tests were strictly performed under the same loading conditions, which confirms the applicability of the model to flexural fatigue data analysis. Moreover, the model parameters are closely related to fatigue performance, which demonstrates the predictive capacity of the model. For instance, the scale parameter is related to flexural strength, which improves with the addition of fibers. Similarly, fiber increases the scattering of fatigue life, which is reflected by the decreasing shape parameter.

Research on the Fatigue Flexural Performance of RC Beams Attacked by Salt Spray

NASA Astrophysics Data System (ADS)

Mao, Jiang-hong; Xu, Fang-yuan; Jin, Wei-liang; Zhang, Jun; Wu, Xi-xi; Chen, Cai-sheng

2018-04-01

The fatigue flexural performance of RC beams attacked by salt spray was studied. A testing method involving electro osmosis, electrical accelerated corrosion and salt spray was proposed. This corrosion process method effectively simulates real-world salt spray and fatigue loading exerted by RC components on sea bridges. Four RC beams that have different stress amplitudes were tested. It is found that deterioration by corrosion and fatigue loading reduces the fatigue life of the RC and decreases the ability of deformation. The fatigue life and deflection ability could be reduced by increasing the stress amplitude and the corrosion duration time. The test result demonstrates that this experimental method can couple corrosion deterioration and fatigue loading reasonably. This procedure may be applied to evaluate the fatigue life and concrete durability of RC components located in a natural salt spray environment.

Assessment of corrosion fatigue damage by acoustic emission and periodic proof tests

NASA Astrophysics Data System (ADS)

Mehdizadeh, P.

1976-03-01

The development of a better nondestructive inspection method for detecting corrosion fatigue damage based on acoustic emission (AE) and periodic proof testing (PPT) is studied for corrosion fatigue tests in salt water solution under tension-tension loading. It is shown that PPT combined with AE monitoring can be a sensitive method for assessing the progress of corrosion fatigue damage as the continuous AE monitoring method. The AE-PPT technique is shown to be dependent on the geometry and size of the crack relative to the test specimen. A qualitative method based on plateauing of acoustic emission counts during proof tests due to changes in the fracture mode is used to predict the remaining fatigue life up to 70% of the actual values. PPT is shown to have no adverse effect on fatigue performance in salt water.

Conducting High Cycle Fatigue Strength Step Tests on Gamma TiAl

NASA Technical Reports Server (NTRS)

Lerch, Brad; Draper, Sue; Pereira, J. Mike

2002-01-01

High cycle fatigue strength testing of gamma TiAl by the step test method is investigated. A design of experiments was implemented to determine if the coaxing effect occurred during testing. Since coaxing was not observed, step testing was deemed a suitable method to define the fatigue strength at 106 cycles.

Oxygen uptake during peak graded exercise and single-stage fatigue tests of wheelchair propulsion in manual wheelchair users and the able-bodied.

PubMed

Keyser, R E; Rodgers, M M; Gardner, E R; Russell, P J

1999-10-01

To determine if a single-stage, submaximal fatigue test on a wheelchair ergometer would result in higher than expected energy expenditure. An experimental survey design contrasting physiologic responses during peak graded exercise tests and fatigue tests. A rehabilitation science laboratory that included a prototypical wheelchair ergometer, open-circuit spirometry system, and heart rate monitor. Nine able-bodied non-wheelchair users (the NWC group: 6 men and 3 women, mean +/- SD age 30 +/- 7yrs) and 15 manual wheelchair users (the WC group: 12 men and 3 women, age 40 +/- 9yrs, time in wheelchair 16 +/- 9yrs). No subject had any disease, medication regimen, or upper body neurologic, orthopedic, or other condition that would limit wheelchair exercise. Peak oxygen uptake (VO2) for graded exercise testing and during fatigue testing, using a power output corresponding to 75% peak aerobic capacity on graded exercise test. In the WC group, VO2 at 6 minutes of fatigue testing was not significantly different from peak VO2. In the NWC group, VO2 was similar to the expected level throughout fatigue testing. Energy expenditure was higher than expected in the WC group but not in the NWC group. Fatigue testing may provide a useful evaluation of cardiorespiratory status in manual wheelchair users.

Repeatability of testing procedures for resilient modulus and fatigue : appendices.

DOT National Transportation Integrated Search

1989-04-01

The article is the appendices of "Repeatability of testing procedures for resilient modulus and fatigue". : Extensive use of diametral resilient modulus and fatigue testing is made by the Oregon State Highway Division to evaluate asphaltic concrete m...

Three-dimensional measurements of fatigue crack closure

NASA Technical Reports Server (NTRS)

Ray, S. K.; Grandt, A. F., Jr.

1984-01-01

Fatigue crack growth and retardation experiments conducted in polycarbonate test specimen are described. The transparent test material allows optical interferometry measurements of the fatigue crack opening (and closing) profiles. Crack surface displacements are obtained through the specimen thickness and three dimensional aspects of fatigue crack closure are discussed.

High Frequency Vibration Based Fatigue Testing of Developmental Alloys

NASA Astrophysics Data System (ADS)

Holycross, Casey M.; Srinivasan, Raghavan; George, Tommy J.; Tamirisakandala, Seshacharyulu; Russ, Stephan M.

Many fatigue test methods have been previously developed to rapidly evaluate fatigue behavior. This increased test speed can come at some expense, since these methods may require non-standard specimen geometry or increased facility and equipment capability. One such method, developed by George et al, involves a base-excited plate specimen driven into a high frequency bending resonant mode. This resonant mode is of sufficient frequency (typically 1200 to 1700 Hertz) to accumulate 107 cycles in a few hours. One of the main limitations of this test method is that fatigue cracking is almost certainly guaranteed to be surface initiated at regions of high stress. This brings into question the validity of the fatigue test results, as compared to more traditional uniaxial, smooth-bar testing, since high stresses are subjecting only a small volume to fatigue damage. This limitation also brings into question the suitability of this method to screen developmental alloys, should their initiation life be governed by subsurface flaws. However, if applicable, the rapid generation of fatigue data using this method would facilitate faster design iterations, identifying more quickly, material and manufacturing process deficiencies. The developmental alloy used in this study was a powder metallurgy boron-modified Ti-6Al-4V, a new alloy currently being considered for gas turbine engine fan blades. Plate specimens were subjected to fully reversed bending fatigue. Results are compared with existing data from commercially available Ti-6Al-4V using both vibration based and more traditional fatigue test methods.

Effect of fatigue loading on critical current in stainless steel-laminated DI-BSCCO superconducting composite tape

NASA Astrophysics Data System (ADS)

Hojo, M.; Osawa, K.; Adachi, T.; Inoue, Y.; Osamura, K.; Ochiai, S.; Ayai, N.; Hayashi, K.

2010-11-01

Tensile strain tolerance of the critical current in (Bi,Pb)2Sr2Ca2Cu3Ox (Bi2223) composite superconductor is dramatically improved when the tape is laminated with stainless steel. For practical applications, it is important to understand whether this reinforcement by lamination is effective under fatigue loading. In the present study, we carried out fatigue tests in LN2 and measured the critical current at the specific fatigue cycles to clarify the strain tolerance of the critical current in stainless steel-laminated drastically innovative Bi2223 (DI-BSCCO®) tapes. The fatigue tests were carried out using a computer-controlled 10 kN servo-hydraulic fatigue testing machine with a load cell capacity of 2.5 kN. Tests under static loading showed that the irreversible stress at which the critical current is reduced by 1% from the original value (tensile stress at Ic/Ic0 = 0.99) was 315 MPa when measured at unloading state. The present fatigue tests results indicated that the critical current was maintained at over 98% of the original value at unloading state after stress cycles of 106 when the static irreversible stress was selected as the maximum stress under fatigue loading. Thus, laminated DI-BSCCO tapes showed excellent mechanical properties even under fatigue loading.

Axial-Load Fatigue Tests on 17-7 PH Stainless Steel Under Constant-Amplitude Loading

NASA Technical Reports Server (NTRS)

Leybold, Herbert A.

1960-01-01

Axial-load fatigue tests were conducted at room temperature on notched and unnotched sheet specimens of 17-7 PH stainless steel in Condition TH 1050. The notched specimens had theoretical stress-concentration factors of 2.32, 4.00, and 5.00. All specimens were tested under completely reversed loading. S-N curves are presented for each specimen configuration and ratios of fatigue strengths of unnotched specimens to those of notched specimens are given. Predictions of the fatigue behavior of notched specimens near the fatigue limit were made.

Strain-controlled fatigue of acrylic bone cement.

PubMed

Carter, D R; Gates, E I; Harris, W H

1982-09-01

Monotonic tensile tests and tension-compression fatigue tests were conducted of wet acrylic bone cement specimens at 37 degrees C. All testing was conducted in strain control at a strain rate of 0.02/s. Weibull analysis of the tensile tests indicated that monotonic fracture was governed more strongly by strain than stress. The number of cycles to fatigue failure was also more strongly controlled by strain amplitude than stress amplitude. Specimen porosity distribution played a major role in determining the tensile and fatigue strengths. The degree of data scatter suggests that Weibull analysis of fatigue data may be useful in developing design criteria for the surgical use of bone cement.

Characterization of fatigue behavior of 2-D woven fabric reinforced ceramic matrix composite at elevated temperature. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Groner, D.J.

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced SiC/SiC ceramic matrix composite specimens at 1100 deg C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle/low stress fatigue tests, far less fiber/matrix interface debond was evident than in low cycle/high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.

Comparison of Mode II and III Monotonic and Fatigue Delamination Onset Behavior for Carbon/Toughened Epoxy Composites

NASA Technical Reports Server (NTRS)

Li, Jian; OBrien, T. Kevin; Lee, Shaw Ming

1997-01-01

Monotonic and fatigue tests were performed to compare the Mode II and III interlaminar fracture toughness and fatigue delamination onset for Tenax-HTA/R6376 carbon/toughened epoxy composites. The Mode II interlaminar fracture toughness and fatigue delamination onset were characterized using the end-notched flexure (ENF) test while the Mode III interlaminar fracture toughness and fatigue delamination onset were characterized by using the edge crack torsion (ECT) test. Monotonic tests show that the Mode III fracture toughness is higher than the Mode II fracture toughness. Both Mode II and III cyclic loading greatly increases the tendency for a delamination to grow relative to a single monotonically increasing load. Under fatigue loading, the Mode III specimen also has a longer life than the Mode II specimen.

Analysis of methods for determining high cycle fatigue strength of a material with investigation of titanium-aluminum-vanadium gigacycle fatigue behavior

NASA Astrophysics Data System (ADS)

Pollak, Randall D.

Today, aerospace engineers still grapple with the qualitative and quantitative understanding of fatigue behavior in the design and testing of turbine-driven jet engines. The Department of Defense has taken a very active role in addressing this problem with the formation of the National High Cycle Fatigue Science & Technology Program in 1994. The primary goal of this program is to further the understanding of high cycle fatigue (HCF) behavior and develop methods in order to mitigate the negative impact of HCF on aerospace operations. This research supports this program by addressing the fatigue strength testing guidance currently provided by the DoD to engine manufacturers, with the primary goal to investigate current methods and recommend a test strategy to characterize the fatigue strength of a material at a specified number of cycles, such as the 109 design goal specified by MIL-HDBK-1783B, or range of cycles. The research utilized the benefits of numerical simulation to initially investigate the staircase method for use in fatigue strength testing. The staircase method is a commonly used fatigue strength test, but its ability to characterize fatigue strength variability is extremely suspect. A modified staircase approach was developed and shown to significantly reduce bias and scatter in estimates for fatigue strength variance. Experimental validation of this proposed test strategy was accomplished using a dual-phase Ti-6Al-4V alloy. The HCF behavior of a second material with a very different microstructure (beta annealed Ti-6Al-4V) was also investigated. The random fatigue limit (RFL) model, a recently developed analysis tool, was investigated to characterize stress-life behavior but found to have difficulty representing fatigue life curves with sharp transitions. Two alternative models (bilinear and hyperbolic) were developed based on maximum likelihood methods to better characterize the Ti-6Al-4V fatigue life behavior. These models provided a good fit to the experimental data for the dual-phase Ti-6Al-4V and were applied to the beta annealed variant in order to estimate stress-life behavior using a small-sample approach. Based on this research, designers should be better able to make reliable estimates of fatigue strength parameters using small-sample testing.

Fatigue-environment interactions in a SiC/Ti-15-3 composite

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Lerch, B. A.

1993-01-01

Load-controlled isothermal and nonisothermal fatigue lives of a (0-deg)s SiC/Ti-15-3 were evaluated at temperatures between 150 and 550 C and a target strain range of about 0.45 percent. In nonisothermal fatigue tests, load was first cycled at minimum temperature and then temperature was cycled at zero load. For fatigue tests with peak temperatures at or above 300 C, fatigue life was dramatically reduced compared to that at 150 C. The shortest life was produced by the nonisothermal test with the greatest temperature range (Delta T = 400 C) and highest peak temperature (T(max) = 550 C). Vacuum testing showed that much of the life reduction under isothermal and nonisothermal conditions was related to environmental effects, although the nature of the fatigue-environment interaction was decidedly different for the isothermal and nonisothermal test cycles which were studied.

Sonic fatigue testing of an advanced composite aileron

NASA Technical Reports Server (NTRS)

Soovere, J.

1982-01-01

The sonic fatigue test program to verify the design of the composite inboard aileron for the L-1011 airplane is described. The composite aileron is fabricated from graphite/epoxy minisandwich covers which are attached to graphite/epoxy front spar and ribs, and to an aluminum rear spar with fasteners. The program covers the development of random fatigue data by means of coupon testing and modal studies on a representative section of the composite aileron, culminating in the accelerated sonic fatigue proof test. The composite aileron sustained nonlinear panel vibration during the proof test without failure. Viscous damping coefficients as low as 0.4% were measured on the panels. The effects of moisture conditioning and elevated temperature on the random fatigue life of both undamaged and impact damaged coupons were investigated. The combination of impact damage, moisture, and a 180 F temperature could reduce the random fatigue life by 50%.

Isothermal and thermal-mechanical fatigue of VVER-440 reactor pressure vessel steels

NASA Astrophysics Data System (ADS)

Fekete, Balazs; Trampus, Peter

2015-09-01

The fatigue life of the structural materials 15Ch2MFA (CrMoV-alloyed ferritic steel) and 08Ch18N10T (CrNi-alloyed austenitic steel) of VVER-440 reactor pressure vessel under completely reserved total strain controlled low cycle fatigue tests were investigated. An advanced test facility was developed for GLEEBLE-3800 physical simulator which was able to perform thermomechanical fatigue experiments under in-service conditions of VVER nuclear reactors. The low cycle fatigue results were evaluated with the plastic strain based Coffin-Manson law, and plastic strain energy based model as well. It was shown that both methods are able to predict the fatigue life of reactor pressure vessel steels accurately. Interrupted fatigue tests were also carried out to investigate the kinetic of the fatigue evolution of the materials. On these samples microstructural evaluation by TEM was performed. The investigated low cycle fatigue behavior can provide reference for remaining life assessment and lifetime extension analysis.

Corrosion fatigue of high strength fastener materials in seawater. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Tipton, D.G.

1983-12-01

Environmental effects can significantly reduce the fatigue life of metals. As such, corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L40 high strength steel blade-to-hub attachment bolt at the MOD-0A 200 kW wind turbine generator in Oahu, Hawaii prompted the current test program. Tests were undertaken to confirm the dramatic reduction of fatigue strength of AISI 41L40 in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials. AISI 41L40, AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35Nmore » were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data were fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.« less

Fatigue limit and Hysteresis Behavior of Type 304L Stainless Steel in Air and PWR Water, at 150°C and 300°C

NASA Astrophysics Data System (ADS)

Solomon, H. D.; Amzallag, C.; Vallee, A. J.; DeLair, R. E.

This is a study of the 107 cycle fatigue limit of Type 304L Stainless Steel, as measured in fully reversed (R=-1) load-controlled tests, at 150°C and 300°C, in air and PWR water. The staircase method was used to determine the fatigue limit. The tests run here utilized a cycle frequency of 1.818Hz and are compared to other tests from the literature that were run at 30Hz. The fatigue limit measured in the tests run at the high frequency was higher than that measured here. This is explained by measurements of the strain developed during cycling, using the different cycle frequencies. The tests run at the higher frequencies yielded lower strains for a given stress and, as expected, this resulted in higher fatigue limits. Using 107 cycles to define a run-out also led to a lower fatigue limit. These results are important as most previous fatigue limit measurements utilized 106 cycles or less to define a run-out, and when lives as long as 107 cycles are used the tests are generally run at high cycle frequencies, thus leading to higher fatigue limits than those measured here.

Fatigue Crack Growth Behavior Evaluation of Grainex Mar-M 247 for NASA's High Temperature, High Speed Turbine Seal Test Rig

NASA Technical Reports Server (NTRS)

Delgado, Irebert R.; Steinetz, Bruce M.; Rimnac, Clare M.; Lewandowski, John J.

2008-01-01

The fatigue crack growth behavior of Grainex Mar-M 247 is evaluated for NASA s Turbine Seal Test Facility. The facility is used to test air-to-air seals primarily for use in advanced jet engine applications. Because of extreme seal test conditions of temperature, pressure, and surface speeds, surface cracks may develop over time in the disk bolt holes. An inspection interval is developed to preclude catastrophic disk failure by using experimental fatigue crack growth data. By combining current fatigue crack growth results with previous fatigue strain-life experimental work, an inspection interval is determined for the test disk. The fatigue crack growth life of the NASA disk bolt holes is found to be 367 cycles at a crack depth of 0.501 mm using a factor of 2 on life at maximum operating conditions. Combining this result with previous fatigue strain-life experimental work gives a total fatigue life of 1032 cycles at a crack depth of 0.501 mm. Eddy-current inspections are suggested starting at 665 cycles since eddy current detection thresholds are currently at 0.381 mm. Inspection intervals are recommended every 50 cycles when operated at maximum operating conditions.

Proof test and fatigue crack growth modeling on 2024-T3 aluminum alloy

NASA Technical Reports Server (NTRS)

Newman, J. C., Jr.; Poe, C. C., Jr.; Dawicke, D. S.

1990-01-01

Pressure proof testing of aircraft fuselage structures has been suggested as a means of screening critical crack sizes and of extending their useful life. The objective of this paper is to study the proof-test concept and to model the crack-growth process on a ductile material. Simulated proof and operational fatigue life tests have been conducted on cracked panels made of 2024-T3 aluminum alloy sheet material. A fatigue crack-closure model was modified to simulate the proof test and operational fatigue cycling. Using crack-growth rate and resistance-curve data, the model was able to predict crack growth during and after the proof load. These tests and analyses indicate that the proof test increases fatigue life; but the beneficial life, after a 1.33 or 1.5 proof, was less than a few hundred cycles.

Improved High-Cycle Fatigue (HCF) Life Prediction

DTIC Science & Technology

2001-01-01

fatigue in 2024 - T351 aluminum alloy ’, Wear 221, 24-36. Appendix 6C CHARACTERIZATION OF FRETTING FATIGUE INITIATED CRACKS P.J. Golden A.F...0.8. To evaluate the effects of surface residual stresses on notch fatigue life , shot peened specimens were tested at R = -1.0 and 0.1. Data in...Behavior - Response • The undamaged fatigue test program demonstrates the sensitivity of surface effects (for different

Factors Influencing Dwell Fatigue Cracking in Notches of Powder Metallurgy Superalloys

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Telesman, J.; Ghosn, L.; Garg, A.; Gayda, J.

2011-01-01

The influences of heat treatment and cyclic dwells on the notch fatigue resistance of powder metallurgy disk superalloys were investigated for low solvus high refractory (LSHR) and ME3 disk alloys. Disks were processed to produce material conditions with varied microstructures and associated mechanical properties. Notched specimens were first subjected to baseline dwell fatigue cycles having a dwell at maximum load, as well as tensile, stress relaxation, creep rupture, and dwell fatigue crack growth tests at 704 C. Several material heat treatments displayed a bimodal distribution of fatigue life with the lives varying by two orders-of-magnitude, while others had more consistent fatigue lives. This response was compared to other mechanical properties, in search of correlations. The wide scatter in baseline dwell fatigue life was observed only for material conditions resistant to stress relaxation. For selected materials and conditions, additional tests were then performed with the dwells shifted in part or in total to minimum tensile load. The tests performed with dwells at minimum load exhibited lower fatigue lives than max dwell tests, and also exhibited early crack initiation and a substantial increase in the number of initiation sites. These results could be explained in part by modeling evolution of peak stresses in the notch with continued dwell fatigue cycling. Fatigue-environment interactions were determined to limit life for the fatigue cycles with dwells.

The influence of cyclic shear fatigue on the bracket-adhesive-enamel complex: an in vitro study.

PubMed

Daratsianos, Nikolaos; Musabegovic, Ena; Reimann, Susanne; Grüner, Manfred; Jäger, Andreas; Bourauel, Christoph

2013-05-01

To describe the effect of fatigue on the strength of the bracket-adhesive-enamel complex and characterize the fatigue behavior of the materials tested. Upper central incisor brackets (Discovery(®), Dentaurum) were bonded with a light-curing (Transbond XT™, 3M Unitek) and a chemically-curing adhesive (Concise™, 3M Unitek) on bovine teeth embedded in cylindrical resign bases and stored in water at 37(±2)°C for 24 (±2)h. The first 15 specimens were tested with a universal testing machine ZMART.PRO(®) (Zwick GmbH & Co. KG, Ulm, Germany) for ultimate shear bond strength according to the DIN-13990-2-standard. The remaining three groups of 20 specimens underwent fatigue staircase testing of 100, 1000 and 3000 cycles at 1Hz with a self-made testing machine. The survived specimens were subjected to shear strength testing. The fatigued specimens showed decreased shear strength with both adhesives at all cycle levels. The shear strength after fatigue for 100, 1000 and 3000 cycles was in the Concise™-groups 34.8%, 59.0%, 47.3% and in the Transbond™ XT-groups 33.6%, 23.1%, 27.3% relative to the ultimate shear strength. The fatigue life of the Concise™-groups decreased with increasing stress and Transbond™ XT showed lower fatigue ratio with no obvious trend. The specimens bonded with Transbond™ XT showed typically favorable fracture modes in contrary to Concise™. Fatigue of the bracket-adhesive-enamel complex decreased its shear strength. The staircase method can provide a standardized experimental protocol for fatigue studies, however testing at various cycle numbers is recommended. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Experimental Study on Fatigue Performance of Foamed Lightweight Soil

NASA Astrophysics Data System (ADS)

Qiu, Youqiang; Yang, Ping; Li, Yongliang; Zhang, Liujun

2017-12-01

In order to study fatigue performance of foamed lightweight soil and forecast its fatigue life in the supporting project, on the base of preliminary tests, beam fatigue tests on foamed lightweight soil is conducted by using UTM-100 test system. Based on Weibull distribution and lognormal distribution, using the mathematical statistics method, fatigue equations of foamed lightweight soil are obtained. At the same time, according to the traffic load on real road surface of the supporting project, fatigue life of formed lightweight soil is analyzed and compared with the cumulative equivalent axle loads during the design period of the pavement. The results show that even the fatigue life of foamed lightweight soil has discrete property, the linear relationship between logarithmic fatigue life and stress ratio still performs well. Especially, the fatigue life of Weibull distribution is more close to that derived from the lognormal distribution, in the instance of 50% guarantee ratio. In addition, the results demonstrated that foamed lightweight soil as subgrade filler has good anti-fatigue performance, which can be further adopted by other projects in the similar research domain.

Bithermal fatigue: A simplified alternative to thermomechanical fatigue

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.

1988-01-01

A bithermal fatigue test technique was proposed as a simplified alternative to the thermomechanical fatigue test. Both the thermomechanical cycle and the bithermal technique can be used to study nonisothermal fatigue behavior. The difference between the two cycles is that in a conventional thermomechanical fatigue cycle the temperature is continuously varied concurrently with the applied mechanical strains, but in the bithermal fatigue cycle the specimen is held at zero load during the temperature excursions and all the loads are applied at the two extreme temperatures of the cycle. Experimentally, the bithermal fatigue test technique offers advantages such as ease in synchronizing the temperature and mechanical strain waveforms, in minimizing temperature gradients in the specimen gauge length, and in reducing and interpreting thermal fatigue such as the influence of alternate high and low temperatures on the cyclic stress-strain response characteristics, the effects of thermal state, and the possibility of introducing high- and low-temperature deformation mechanisms within the same cycle. The bithermal technique was used to study nonisothermal fatigue behavior of alloys such as single-crystal PWA 1480, single-crystal Rene N4, cast B1900+Hf, and wrought Haynes 188.

Corrosion fatigue in nitrocarburized quenched and tempered steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Karim Khani, M.; Dengel, D.

1996-05-01

In order to investigate the fatigue strength and fracture mechanism of salt bath nitrocarburized steels, specimens of the steels SAE 4135 and SAE 4140, in a quenched and tempered state, and additionally in a salt bath nitrocarburized and oxidizing cooled state as well as in a polished (after the oxidizing cooling) and renewed oxidized state, were subjected to comparative rotating bending fatigue tests in inert oil and 5 pct NaCl solution. In addition, some of the quenched and tempered specimens of SAE 4135 material were provided with an approximately 50-{mu}m-thick electroless Ni-P layer, in order to compare corrosion fatigue behaviormore » between the Ni-P layer and the nitride layers. Long-life corrosion fatigue tests of SAE 4135 material were carried out under small stresses in the long-life range up to 10{sup 8} cycles with a test frequency of 100 Hz. Fatigue tests of SAE 4140 material were carried out in the range of finite life (low-cycle range) with a test frequency of 13 Hz. The results show that the 5 pct NaCl environment drastically reduced fatigue life, but nitrocarburizing plus oxidation treatment was found to improve the corrosion fatigue life over that of untreated and Ni-P coated specimens. The role of inclusions in initiating fatigue cracks was investigated. It was found that under corrosion fatigue conditions, the fatigue cracks started at cavities along the interfaces of MnS inclusions and matrix in the case of quenched and tempered specimens. The nitrocarburized specimens, however, showed a superposition of pitting corrosion and corrosion fatigue in which pores and nonmetallic inclusions in the compound layer play a predominant role concerning the formation of pits in the substrate.« less

Creep-fatigue of low cobalt superalloys

NASA Technical Reports Server (NTRS)

Halford, G. R.

1982-01-01

Testing for the low cycle fatigue and creep fatigue resistance of superalloys containing reduced amounts of cobalt is described. The test matrix employed involves a single high temperature appropriate for each alloy. A single total strain range, again appropriate to each alloy, is used in conducting strain controlled, low cycle, creep fatigue tests. The total strain range is based upon the level of straining that results in about 10,000 cycles to failure in a high frequency (0.5 Hz) continuous strain-cycling fatigue test. No creep is expected to occur in such a test. To bracket the influence of creep on the cyclic strain resistance, strain hold time tests with ore minute hold periods are introduced. One test per composition is conducted with the hold period in tension only, one in compression only, and one in both tension and compression. The test temperatures, alloys, and their cobalt compositions that are under study are given.

Investigation of fatigue failure in bituminous base mixes.

DOT National Transportation Integrated Search

1980-01-01

A correlation between the results obtained with the fatigue test and those from the indirect tensile test on two base mixes was attempted in anticipation of the possible use of the latter test to design base mixes for maximum fatigue life. Two base m...

Cyclic fatigue damage characteristics observed for simple loadings extended to multiaxial life prediction

NASA Technical Reports Server (NTRS)

Jones, David J.; Kurath, Peter

1988-01-01

Fully reversed uniaxial strain controlled fatigue tests were performed on smooth cylindrical specimens made of 304 stainless steel. Fatigue life data and cracking observations for uniaxial tests were compared with life data and cracking behavior observed in fully reversed torsional tests. It was determined that the product of maximum principle strain amplitude and maximum principle stress provided the best correlation of fatigue lives for these two loading conditions. Implementation of this parameter is in agreement with observed physical damage and it accounts for the variation of stress-strain response, which is unique to specific loading conditions. Biaxial fatigue tests were conducted on tubular specimens employing both in-phase and out-of-phase tension torsion cyclic strain paths. Cracking observations indicated that the physical damage which occurred in the biaxial tests was similar to the damage observed in uniaxial and torsional tests. The Smith, Watson, and Topper parameter was then extended to predict the fatigue lives resulting from the more complex loading conditions.

Test Population Selection from Weibull-Based, Monte Carlo Simulations of Fatigue Life

NASA Technical Reports Server (NTRS)

Vlcek, Brian L.; Zaretsky, Erwin V.; Hendricks, Robert C.

2008-01-01

Fatigue life is probabilistic and not deterministic. Experimentally establishing the fatigue life of materials, components, and systems is both time consuming and costly. As a result, conclusions regarding fatigue life are often inferred from a statistically insufficient number of physical tests. A proposed methodology for comparing life results as a function of variability due to Weibull parameters, variability between successive trials, and variability due to size of the experimental population is presented. Using Monte Carlo simulation of randomly selected lives from a large Weibull distribution, the variation in the L10 fatigue life of aluminum alloy AL6061 rotating rod fatigue tests was determined as a function of population size. These results were compared to the L10 fatigue lives of small (10 each) populations from AL2024, AL7075 and AL6061. For aluminum alloy AL6061, a simple algebraic relationship was established for the upper and lower L10 fatigue life limits as a function of the number of specimens failed. For most engineering applications where less than 30 percent variability can be tolerated in the maximum and minimum values, at least 30 to 35 test samples are necessary. The variability of test results based on small sample sizes can be greater than actual differences, if any, that exists between materials and can result in erroneous conclusions. The fatigue life of AL2024 is statistically longer than AL6061 and AL7075. However, there is no statistical difference between the fatigue lives of AL6061 and AL7075 even though AL7075 had a fatigue life 30 percent greater than AL6061.

Test Population Selection from Weibull-Based, Monte Carlo Simulations of Fatigue Life

NASA Technical Reports Server (NTRS)

Vlcek, Brian L.; Zaretsky, Erwin V.; Hendricks, Robert C.

2012-01-01

Fatigue life is probabilistic and not deterministic. Experimentally establishing the fatigue life of materials, components, and systems is both time consuming and costly. As a result, conclusions regarding fatigue life are often inferred from a statistically insufficient number of physical tests. A proposed methodology for comparing life results as a function of variability due to Weibull parameters, variability between successive trials, and variability due to size of the experimental population is presented. Using Monte Carlo simulation of randomly selected lives from a large Weibull distribution, the variation in the L10 fatigue life of aluminum alloy AL6061 rotating rod fatigue tests was determined as a function of population size. These results were compared to the L10 fatigue lives of small (10 each) populations from AL2024, AL7075 and AL6061. For aluminum alloy AL6061, a simple algebraic relationship was established for the upper and lower L10 fatigue life limits as a function of the number of specimens failed. For most engineering applications where less than 30 percent variability can be tolerated in the maximum and minimum values, at least 30 to 35 test samples are necessary. The variability of test results based on small sample sizes can be greater than actual differences, if any, that exists between materials and can result in erroneous conclusions. The fatigue life of AL2024 is statistically longer than AL6061 and AL7075. However, there is no statistical difference between the fatigue lives of AL6061 and AL7075 even though AL7075 had a fatigue life 30 percent greater than AL6061.

Cognitive and Physical Fatigue Tasks Enhance Pain, Cognitive Fatigue and Physical Fatigue in People with Fibromyalgia

PubMed Central

Dailey, Dana L; Keffala, Valerie J; Sluka, Kathleen A

2014-01-01

Objective Fibromyalgia is a condition characterized by chronic widespread muscle pain and fatigue. The primary objective of this study was to determine if pain, perceived cognitive fatigue, and perceived physical fatigue were enhanced in participants with fibromyalgia compared to healthy controls during a cognitive fatigue task, a physical fatigue task and a dual fatigue task. Methods Twenty four people with fibromyalgia and 33 healthy controls completed pain, fatigue and function measures. A cognitive fatigue task (Controlled Oral Word Association Test) and physical fatigue task (Valpar peg test) were done individually and combined for a dual fatigue task. Resting pain, perceived cognitive fatigue and perceived physical fatigue were assessed during each task using visual analogue scales. Function was assessed with shoulder range of motion and grip. Results People with fibromyalgia had significantly higher increases in pain, cognitive fatigue and physical fatigue when compared to healthy controls after completion of a cognitive fatigue task, a physical fatigue task, or a dual fatigue task (p<0.01). People with fibromyalgia performed equivalently on measures of physical performance and cognitive performance on the physical and cognitive fatigue tasks, respectively. Conclusions These data show that people with fibromyalgia show larger increases in pain, perceived cognitive fatigue and perceived physical fatigue to both cognitive and physical fatigue tasks compared to healthy controls. The increases in pain and fatigue during cognitive and physical fatigue tasks could influence subject participation in daily activities and rehabilitation. PMID:25074583

Laboratory Study on the Fatigue Resistance of Asphaltic Concrete Containing Titanium Dioxide

NASA Astrophysics Data System (ADS)

Buhari, Rosnawati; Ezree Abdullah, Mohd; Khairul Ahmad, Mohd; Azhar Tajudin, Saiful; Khatijah Abu Bakar, Siti

2018-03-01

This study aims to evaluate the fatigue performance of modified asphalt mixture using Indirect Tensile Fatigue Test. Titanium Dioxide (TiO2) powder in a form of rutile was used for producing asphalt concrete with lower mixing and compaction temperature compared to conventional hot mix asphalt without reducing its physical and mechanical also resistance to fatigue. The characteristic of the asphalt and modified asphalt was evaluated using penetration test, softening test and rotational viscosity test. Titanium dioxide of 2%, 4%, 6%, 8% and 10% by weight of asphalt has been incorporated into unaged 80/100 asphalt mix in order to improvise its performance and to fulfill the objectives of this experimental study. As a result, TiO2 as an additive is potential to decrease the penetration and increasing the softening point of the asphalt. In terms of fatigue performance testing, addition TiO2 additive does help in improving the fatigue properties as it shows greater result than the control asphalt. In conclusion, TiO2 is great in improving fatigue properties.

High temperature, low cycle fatigue of copper-base alloys in argon. Part 3: Zirconium-copper; thermal-mechanical strain cycling, hold-time and notch fatigue results

NASA Technical Reports Server (NTRS)

Conway, J. B.; Stentz, R. H.; Berling, J. T.

1973-01-01

The low-cycle fatigue characteristics of smooth bar and notched bar specimens (hourglass shape) of zirconium-copper, 1/2 Hard, material (R-2 Series) were evaluated at room temperature in axial strain control. Over the fatigue life range from about 300 to 3000 cycles the ratio of fatigue life for smooth bar to fatigue life for notched bar remained constant at a value of about 6.0. Some additional hold-time data for the R-2 alloy tested in argon at 538 C are reported. An analysis of the relaxation data obtained in these hold-time tests is also reported and it is shown that these data yield a fairly consistent correlation in terms of instantaneous stress rate divided by instantaneous stress. Two thermal-mechanical strain cycling tests were also performed using a cyclic frequency of 4.5 cycles per hour and a temperature cycling interval from 260 to 538 C. The fatigue life values in these tests were noticeably lower than that observed in isothermal tests at 538 C.

Review of specimen heating in mechanical tests at cryogenic temperatures

NASA Astrophysics Data System (ADS)

Ogata, T.; Yuri, T.; Ono, Y.

2014-01-01

At cryogenic temperatures near 4 K, a discontinuous deformation produces a large amount of specimen temperature rise that might bring significant changes in mechanical properties. The authors measured the specimen heating in tensile tests, fatigue test, and other tests in liquid helium for stainless steels and other materials. In this paper, we have measured the specimen temperature in high-cycle and low-cycle fatigue tests for stainless steels at various frequencies and stress levels and evaluated the testing conditions to keep the specimen at a specified temperature. We proposed maximum frequency in load-controlled fatigue tests for specified loading variables and a maximum strain rate in strain-controlled fatigue tests.

Rolling-element fatigue life with two synthetic cycloaliphatic traction fluids

NASA Technical Reports Server (NTRS)

Loewenthal, S. H.; Parker, R. J.

1976-01-01

The life potential of two synthetic cycloaliphatic hydrocarbon traction fluids in rolling element fatigue was evaluated in a five ball fatigue tester. Life comparisons with a MIL-L-23699 qualified tetraester oil showed that the traction test oils had good fatigue life performance, comparable to that of the tetraester oil. No statistically significant life differences between the traction fluids and the tetraester oil were exhibited under the accelerated fatigue test conditions. Erratic operating behavior was occasionally encountered during tests with the antiwear additive containing traction fluid for reasons thought to be related to excessive chemical activity under high contact pressure. This behavior occasionally resulted in premature test termination due to excessive surface distress and overheating.

Effects of Total SAT® Test Time on Performance and Fatigue. Research Notes. RN-37

ERIC Educational Resources Information Center

Ackerman, Phillip L.; Kanfer, Ruth; Wolman, Stacey D.

2005-01-01

The current study was designed to examine performance effects and fatigue effects associated with different total SAT testing times. In addition, the researchers examined personality, motivation, and other determinants of individual differences in examinee fatigue before, during, and after testing.

Ultrasonic Fatigue Endurance of Thin Carbon Fiber Sheets

NASA Astrophysics Data System (ADS)

Domínguez Almaraz, Gonzalo M.; Ruiz Vilchez, Julio A.; Dominguez, Aymeric; Meyer, Yann

2016-04-01

Ultrasonic fatigue tests were carried out on thin carbon fiber sheets (0.3 mm of thickness) to determine the fatigue endurance under very high-frequency loading (20 kHz). This material, called the gas diffusion layer (GDL), plays a major role in the overall performances of proton exchange membrane fuel cells (PEMFCs). The study of its physical-chemical properties is an on-going subject in the literature; nevertheless, no knowledge is available concerning the high-frequency fatigue endurance. A principal difficulty in carrying out ultrasonic fatigue tests on this material was to determine the dimensions of testing specimen to fit the resonance condition. This aspect was solved by modal numerical simulation: The testing specimen has been a combination of a low-strength steel frame (to facilitate the attachment to the ultrasonic machine and to increase the mass of the specimen), and the carbon fiber hourglass-shape profile. Under resonance condition, a stationary elastic wave is generated along the specimen that induces high stress at the neck section and high displacements at the ends. Results show that fatigue life was close to 3 × 108 cycles when the high Von Misses stress at the neck section was 170 MPa, whereas fatigue life attains the 4.5 × 109 cycles when stress decreases to 117 MPa. Crack initiation and propagation were analyzed, and conclusions were drawn concerning the fatigue endurance of these fiber carbon sheets under ultrasonic fatigue testing.

Fatigue analysis and testing of wind turbine blades

NASA Astrophysics Data System (ADS)

Greaves, Peter Robert

This thesis focuses on fatigue analysis and testing of large, multi MW wind turbine blades. The blades are one of the most expensive components of a wind turbine, and their mass has cost implications for the hub, nacelle, tower and foundations of the turbine so it is important that they are not unnecessarily strong. Fatigue is often an important design driver, but fatigue of composites is poorly understood and so large safety factors are often applied to the loads. This has implications for the weight of the blade. Full scale fatigue testing of blades is required by the design standards, and provides manufacturers with confidence that the blade will be able to survive its service life. This testing is usually performed by resonating the blade in the flapwise and edgewise directions separately, but in service these two loads occur at the same time.. A fatigue testing method developed at Narec (the National Renewable Energy Centre) in the UK in which the flapwise and edgewise directions are excited simultaneously has been evaluated by comparing the Palmgren-Miner damage sum around the blade cross section after testing with the damage distribution caused by the service life. A method to obtain the resonant test configuration that will result in the optimum mode shapes for the flapwise and edgewise directions was then developed, and simulation software was designed to allow the blade test to be simulated so that realistic comparisons between the damage distributions after different test types could be obtained. During the course of this work the shortcomings with conventional fatigue analysis methods became apparent, and a novel method of fatigue analysis based on multi-continuum theory and the kinetic theory of fracture was developed. This method was benchmarked using physical test data from the OPTIDAT database and was applied to the analysis of a complete blade. A full scale fatigue test method based on this new analysis approach is also discussed..

Resistance Spot Welding Characteristics and High Cycle Fatigue Behavior of DP 780 Steel Sheet

NASA Astrophysics Data System (ADS)

Pal, Tapan Kumar; Bhowmick, Kaushik

2012-02-01

Resistance spot welding characteristics of DP 780 steel was investigated using peel test, microhardness test, tensile shear test, and fatigue test. Tensile shear test provides better spot weld quality than conventional peel test and hardness is not a good indicator of the susceptibility to interfacial fracture. The results of high-cycle fatigue behavior of spot welded DP 780 steel under two different parameters show that at high load low cycle range a significant difference in the S- N curve and almost similar fatigue behavior of spot welds at low load high cycle range are obtained. However, when applied load was converted to stress intensity factor, the difference in the fatigue behavior between welds diminished. Furthermore, a transition in fracture mode, i.e., interfacial and plug and hole-type at about 50% of yield load is observed.

Synergistic Effects of Temperature, Oxidation and Stress Level on Fatigue Damage Evolution and Lifetime Prediction of Cross-Ply SiC/CAS Ceramic-Matrix Composites Through Hysteresis-Based Parameters

NASA Astrophysics Data System (ADS)

Li, Longbiao

2017-12-01

The damage development and cyclic fatigue lifetime of cross-ply SiC/CAS ceramic-matrix composites have been investigated at different testing temperatures in air atmosphere. The relationships between the fatigue hysteresis-based damage parameters, i.e., fatigue hysteresis dissipated energy, fatigue hysteresis modulus and fatigue peak strain and the damage mechanisms of matrix multicracking, fiber/matrix interface debonding, interface sliding and fibers failure, have been established. With the increase in the cycle number, the evolution of the fatigue hysteresis modulus, fatigue peak strain and fatigue hysteresis dissipated energy depends upon the fatigue peak stress levels, interface and fibers oxidation and testing temperature. The fatigue life S-N curves of cross-ply SiC/CAS composite at room and elevated temperatures have been predicted, and the fatigue limit stresses at room temperature, 750 and 850 °C, are 50, 36 and 30% of the tensile strength, respectively.

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2014 CFR

2014-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2012 CFR

2012-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2013 CFR

2013-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2011 CFR

2011-01-01

... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be established by tests, or analysis based on tests, for propeller: (1) Hubs. (2) Blades. (3) Blade retention...

Analytical and experimental investigation of fatigue in a sheet specimen with an interference-fit bolt

NASA Technical Reports Server (NTRS)

Crews, J. H., Jr.

1975-01-01

A fatigue analysis, based on finite-element calculations and fatigue tests, was conducted for an aluminum-alloy sheet specimen with a steel interference-fit bolt. The stress analysis of the region near the bolt hole showed that the beneficial effect of an interference-fit bolt can be interpreted as the combined result of two effects: (1) load transfer through the bolt and (2) the compressive interference stresses in the sheet. Results of the fatigue tests show that progressively higher interference levels produced longer fatigue lives. The tests also show that a high level of interference prevents fretting at the bolt-sheet interface and that interferences larger than this level produced little additional improvement in fatigue life.

Corrosion fatigue in nitrocarburized quenched and tempered steels

NASA Astrophysics Data System (ADS)

Khani, M. Karim; Dengel, D.

1996-05-01

In order to investigate the fatigue strength and fracture mechanism of salt bath nitrocarburized steels, specimens of the steels SAE 4135 and SAE 4140, in a quenched and tempered state, and additionally in a salt bath nitrocarburized and oxidizing cooled state as well as in a polished (after the oxidizing cooling) and renewed oxidized state, were subjected to comparative rotating bending fatigue tests in inert oil and 5 pct NaCl solution. In addition, some of the quenched and tempered specimens of SAE 4135 material were provided with an approximately 50-μm-thick electroless Ni-P layer, in order to compare corrosion fatigue behavior between the Ni-P layer and the nitride layers. Long-life corrosion fatigue tests of SAE 4135 material were carried out under small stresses in the long-life range up to 108 cycles with a test frequency of 100 Hz. Fatigue tests of SAE 4140 material were carried out in the range of finite life (low-cycle range) with a test frequency of 13 Hz. The results show that the 5 pct NaCl environment drastically reduced fatigue life, but nitrocarburizing plus oxidation treatment was found to improve the corrosion fatigue life over that of untreated and Ni-P coated specimens. The beneficial effect of nitrocarburizing followed by oxidation treatment on cor-rosion fatigue life results from the protection rendered by the compound layer by means of a well-sealed oxide layer, whereby the pores present in the compound layer fill up with oxides. The role of inclusions in initiating fatigue cracks was investigated. It was found that under corrosion fatigue conditions, the fatigue cracks started at cavities along the interfaces of MnS inclusions and matrix in the case of quenched and tempered specimens. The nitrocarburized specimens, however, showed a superposition of pitting corrosion and corrosion fatigue in which pores and nonmetallic inclusions in the compound layer play a predominant role concerning the formation of pits in the substrate.

Fatigue crack growth in an aluminum alloy-fractographic study

NASA Astrophysics Data System (ADS)

Salam, I.; Muhammad, W.; Ejaz, N.

2016-08-01

A two-fold approach was adopted to understand the fatigue crack growth process in an Aluminum alloy; fatigue crack growth test of samples and analysis of fractured surfaces. Fatigue crack growth tests were conducted on middle tension M(T) samples prepared from an Aluminum alloy cylinder. The tests were conducted under constant amplitude loading at R ratio 0.1. The stress applied was from 20,30 and 40 per cent of the yield stress of the material. The fatigue crack growth data was recorded. After fatigue testing, the samples were subjected to detailed scanning electron microscopic (SEM) analysis. The resulting fracture surfaces were subjected to qualitative and quantitative fractographic examinations. Quantitative fracture analysis included an estimation of crack growth rate (CGR) in different regions. The effect of the microstructural features on fatigue crack growth was examined. It was observed that in stage II (crack growth region), the failure mode changes from intergranular to transgranular as the stress level increases. In the region of intergranular failure the localized brittle failure was observed and fatigue striations are difficult to reveal. However, in the region of transgranular failure the crack path is independent of the microstructural features. In this region, localized ductile failure mode was observed and well defined fatigue striations were present in the wake of fatigue crack. The effect of interaction of growing fatigue crack with microstructural features was not substantial. The final fracture (stage III) was ductile in all the cases.

Statistical characterization of the fatigue behavior of composite lamina

NASA Technical Reports Server (NTRS)

Yang, J. N.; Jones, D. L.

1979-01-01

A theoretical model was developed to predict statistically the effects of constant and variable amplitude fatigue loadings on the residual strength and fatigue life of composite lamina. The parameters in the model were established from the results of a series of static tensile tests and a fatigue scan and a number of verification tests were performed. Abstracts for two other papers on the effect of load sequence on the statistical fatigue of composites are also presented.

The neural effects of positively and negatively re-experiencing mental fatigue sensation: a magnetoencephalography study.

PubMed

Ishii, Akira; Ishizuka, Takuya; Muta, Yuki; Tanaka, Masaaki; Yamano, Emi; Watanabe, Yasuyoshi

2018-06-01

Fatigue sensation is an essential biological alarm that urges us to take rest to avoid disrupting homeostasis and thus plays an important role in maintaining well-being. However, there are situations in which the anticipation of unpleasant fatigue sensation undesirably reduces motivation for activity. The aim of this study was to examine whether thinking positively about the fatigue sensation would increase motivation to accomplish the workload. Fourteen healthy male volunteers participated in this study and performed a two-back test for 30 min to induce mental fatigue sensation. After their subjective level of fatigue had recovered to the baseline level, they re-experienced the fatigue sensation experienced in the two-back test positively, negatively, and without any modification (i.e., re-experienced the fatigue sensation as it was). The level of motivation to perform another two-back test they felt during the re-experiencing was assessed. The neural activity related to the re-experiencing was recorded using magnetoencephalography. The level of the motivation to perform another two-back test was increased by positively re-experiencing the fatigue sensation. The increase in delta band power in Brodmann area 7 was positively associated with the increase in motivation. These results show that positive thinking about fatigue sensation can enhance motivation and suggest that this enhanced motivation may have some effects on visual attention system.

Effects of sour crude oil on fatigue properties of steel plates for shipbuilding

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ouchi, H.; Kobayashi, J.; Ishikawa, T.

1994-12-31

The concentration of diffusible hydrogen introduced into steel was measured, and fatigue crack growth tests and fatigue life tests were carried out in sour crude oil containing a high concentration of hydrogen sulfide and under electrolytic hydrogen-charging conditions in neutral solution, using a high strength steel produced by the thermo-mechanical control process (TMCP) and a mild steel which are steels for hull plates. Comparison of the results demonstrated that a very small amount of hydrogen such as that introduced into steel from sour crude oil under atmospheric pressure accelerated the fatigue crack growth in the high {Delta}K regime and shortenedmore » the fatigue life in the high stress range region, but did not shorten the fatigue life in the low stress region. The electrolytic hydrogen-charging condition appeared to be appropriate as a fatigue-crack-growth test environment to simulate sour crude oil. The deterioration of fatigue characteristics of the TMCP high strength steel was similar with that of the mild steel.« less

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy

PubMed Central

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-01-01

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition. PMID:28774103

Fretting Fatigue Experiment and Analysis of AlSi9Cu2Mg Alloy.

PubMed

Wang, Jun; Xu, Hong; Su, Tiexiong; Zhang, Yi; Guo, Zhen; Mao, Huping; Zhang, Yangang

2016-12-05

An investigation was carried out in order to study the fretting fatigue behavior of an AlSi9Cu2Mg aluminum alloy. The fretting fatigue tests of AlSi9Cu2Mg were performed using a specially designed testing machine. The failure mechanism of fretting fatigue was explored by studying the fracture surfaces, fretting scars, fretting debris, and micro-hardness of fretting fatigue specimens using scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and micro Vickers hardness test techniques. The experimental results show that the fretting fatigue limit (42 MPa) is significantly reduced to approximately 47% of the plain fatigue limit (89 MPa) under 62.5 MPa contact pressure. Furthermore, the fretting fatigue life decreases with increasing alternating stress and increasing contact pressure. The examination results suggest that the stress concentrates induced by oxidation-assisted wear on the contact interface led to the earlier initiation and propagation of crack under the fretting condition.

The fatigue experience for women with human immunodeficiency virus.

PubMed

Lee, K A; Portillo, C J; Miramontes, H

1999-01-01

To examine fatigue as a symptom experienced by women with human immunodeficiency virus (HIV). A convenience sample of 100 women with HIV. Independent sample t-tests were used to test for mean differences in fatigue related to variables in the women's sociocultural and home environment (ethnicity, employment, marital status, and parenting). Pearson product moment correlations were used to examine significant relationships between fatigue and physiologic variables (age, CD4 cell count, and sleep). Lower CD4 cell counts were related to more daytime sleep, higher evening fatigue, and higher morning fatigue. Morning fatigue was related to duration of wake episodes during the night, napping, and perception of sleep disturbance during the past week. The number of awakenings during the first night predicted the severity of fatigue the next evening. To understand the fatigue experienced by women with HIV, researchers and clinicians must focus on the relative contributions of sociocultural, home, and physiologic environments within which these women live. Additional research is ongoing to identify the strategies these women use to manage daily activities such that gender-relevant and culturally relevant interventions for alleviating fatigue can be tested in women with a variety of chronic illnesses, including HIV and acquired immune deficiency syndrome.

Thermomechanical and bithermal fatigue behavior of cast B1900 + Hf and wrought Haynes 188

NASA Technical Reports Server (NTRS)

Halford, G. R.; Verrilli, M. J.; Kalluri, S.; Ritzert, F. J.; Duckert, R. E.; Holland, F. A.

1992-01-01

A thermomechanical fatigue (TMF) high-temperature life prediction method has been evaluated using the experimental data. Bithermal fatigue (BTF), bithermal creep-fatigue (BTC-F), and TMF experiments were performed using two aerospace structural alloys, cast B1900 + Hf and wrought Haynes 188. The method which is based on the total strain version of strain range partitioning and unified cyclic constitutive modeling requires, as an input, information on the flow and failure behavior of the material of interest. Bithermal temperatures of 483 and 871 C were used for the cast B1900 + Hf nickel-base alloy and 316 and 760 C for the wrought Haynes 188 cobalt-base alloy. Maximum and minimum temperatures were also used in both TMF and BTF tests. Comparisons were made between the results of these tests and isothermal tensile and fatigue test data obtained previously. Qualitative correlations were observed between tensile and isothermal fatigue tests.

The direct-stress fatigue strength of 17S-T aluminum alloy throughout the range from 1/2 to 500,000,000 cycles of stress

NASA Technical Reports Server (NTRS)

Hartmann, E C; Stickley, G W

1942-01-01

Fatigue-test were conducted on six specimens made from 3/4-inch-diameter 17S-T rolled-and-drawn rod for the purpose of obtaining additional data on the fatigue life of the material at stresses up to the static strength. The specimens were tested in direct tension using a stress range from zero to a maximum in tension. A static testing machine was used to apply repeated loads in the case of the first three specimens; the other three specimens were tested in a direct tension-compression fatigue machine. The direct-stress fatigue curve obtained for the material indicates that, in the range of stresses above about two-thirds the tensile strength, the fatigue strength is higher than might be expected by simply extrapolating the ordinary curve of stress plotted against the number of cycles determined at lower stresses.

A proposed USAF fatigue evaluation program based upon recent systems experience

NASA Technical Reports Server (NTRS)

Haviland, G. P.; Purkey, G. F.

1972-01-01

The United States Air Force has published a document entitled Aircraft Structural Integrity Program. One phase of the program is concerned with the fatigue life certification of all types of military aircraft. The document describes the criteria, analyses, and tests that are necessary in order to satisfy the USAF fatigue life requirement. Some recent and valid criticism has been directed toward the document, particularly the fatigue-life requirements contained in it. Some changes are proposed based on surveys conducted in the United States and abroad as well as some recent systems' experience. The surveys covered both military and civilian organizations. The fatigue certification case histories of selected military and commercial aircraft are presented. The design development element tests, preproduction design verification tests, and full-scale fatigue tests of each are described. A brief status report on the revisions to the MIL-A-008860 series specifications is included.

Novel Electrochemical Test Bench for Evaluating the Functional Fatigue Life of Biomedical Alloys

NASA Astrophysics Data System (ADS)

Ijaz, M. F.; Dubinskiy, S.; Zhukova, Y.; Korobkova, A.; Pustov, Y.; Brailovski, V.; Prokoshkin, S.

2017-08-01

The aim of the present work was first to develop and validate a test bench that simulates the in vitro conditions to which the biomedical implants will be actually subjected in vivo. For the preliminary application assessments, the strain-controlled fatigue tests of biomedically pure Ti and Ti-Nb-Zr alloy in simulated body fluid were undertaken. The in situ open-circuit potential measurements from the test bench demonstrated a strong dependence on the dynamic cycling and kind of material under testing. The results showed that during fatigue cycling, the passive oxide film formed on the surface of Ti-Nb-Zr alloy was more resistant to fatigue degradation when compared with pure Ti. The Ti-Nb-Zr alloy exhibited prolonged fatigue life when compared with pure Ti. The fractographic features of both materials were also characterized using scanning electron microscopy. The electrochemical results and the fractographic evidence confirmed that the prolonged functional fatigue life of the Ti-Nb-Zr alloy is apparently ascribable to the reversible martensitic phase transformation.

Taltirelin alleviates fatigue-like behavior in mouse models of cancer-related fatigue.

PubMed

Dougherty, John P; Wolff, Brian S; Cullen, Mary J; Saligan, Leorey N; Gershengorn, Marvin C

2017-10-01

Fatigue affects most cancer patients and has numerous potential causes, including cancer itself and cancer treatment. Cancer-related fatigue (CRF) is not relieved by rest, can decrease quality of life, and has no FDA-approved therapy. Thyrotropin-releasing hormone (TRH) has been proposed as a potential novel treatment for CRF, but its efficacy against CRF remains largely untested. Thus, we tested the TRH analog, taltirelin (TAL), in mouse models of CRF. To model fatigue, we used a mouse model of chemotherapy, a mouse model of radiation therapy, and mice bearing colon 26 carcinoma tumors. We used the treadmill fatigue test to assess fatigue-like behavior after treatment with TAL. Additionally, we used wild-type and TRH receptor knockout mice to determine which TRH receptor was necessary for the actions of TAL. Tumor-bearing mice displayed muscle wasting and all models caused fatigue-like behavior, with mice running a shorter distance in the treadmill fatigue test than controls. TAL reversed fatigue-like behavior in all three models and the mouse TRH 1 receptor was necessary for the effects of TAL. These data suggest that TAL may be useful in alleviating fatigue in all cancer patients and provide further support for evaluating TAL as a potential therapy for CRF in humans. Published by Elsevier Ltd.

The effect of matrix mechanical properties on (0)8 unidirectional SiC/Ti composite fatigue resistance

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Gayda, J.; Lerch, B. A.; Halford, G. R.

1991-01-01

The relationship between constituent and MMC properties in fatigue loading is investigated with low-cycle fatigue-resistance testing of an alloy Ti-15-3 matrix reinforced with SiC SCS-6 fibers. The fabrication of the composite is described, and specimens are generated that are weak and ductile (WD), strong and moderately ductile (SM), or strong and brittle (SB). Strain is measured during MMC fatigue tests at a constant load amplitude with a load-controlled waveform and during matrix-alloy fatigue tests at a constant strain amplitude using a strain-controlled waveform. The fatigue resistance of the (0)8 SiC/Ti-15-3 composite is found to be slightly influenced by matrix mechanical properties, and the composite- and matrix-alloy fatigue lives are not correlated. This finding is suggested to relate to the different crack-initiation and -growth processes in MMCs and matrix alloys.

Room Temperature and Elevated Temperature Composite Sandwich Joint Testing

NASA Technical Reports Server (NTRS)

Walker, Sandra P.

1998-01-01

Testing of composite sandwich joint elements has been completed to verify the strength capacity of joints designed to carry specified running loads representative of a high speed civil transport wing. Static tension testing at both room and an elevated temperature of 350 F and fatigue testing at room temperature were conducted to determine strength capacity, fatigue life, and failure modes. Static tension test results yielded failure loads above the design loads for the room temperature tests, confirming the ability of the joint concepts tested to carry their design loads. However, strength reductions as large as 30% were observed at the elevated test temperature, where all failure loads were below the room temperature design loads for the specific joint designs tested. Fatigue testing resulted in lower than predicted fatigue lives.

Fatigue acceptance test limit criterion for larger diameter rolled thread fasteners

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kephart, A.R.

1997-05-01

This document describes a fatigue lifetime acceptance test criterion by which studs having rolled threads, larger than 1.0 inches in diameter, can be assured to meet minimum quality attributes associated with a controlled rolling process. This criterion is derived from a stress dependent, room temperature air fatigue database for test studs having a 0.625 inch diameter threads of Alloys X-750 HTH and direct aged 625. Anticipated fatigue lives of larger threads are based on thread root elastic stress concentration factors which increase with increasing thread diameters. Over the thread size range of interest, a 30% increase in notch stress ismore » equivalent to a factor of five (5X) reduction in fatigue life. The resulting diameter dependent fatigue acceptance criterion is normalized to the aerospace rolled thread acceptance standards for a 1.0 inch diameter, 0.125 inch pitch, Unified National thread with a controlled Root radius (UNR). Testing was conducted at a stress of 50% of the minimum specified material ultimate strength, 80 Ksi, and at a stress ratio (R) of 0.10. Limited test data for fastener diameters of 1.00 to 2.25 inches are compared to the acceptance criterion. Sensitivity of fatigue life of threads to test nut geometry variables was also shown to be dependent on notch stress conditions. Bearing surface concavity of the compression nuts and thread flank contact mismatch conditions can significantly affect the fastener fatigue life. Without improved controls these conditions could potentially provide misleading acceptance data. Alternate test nut geometry features are described and implemented in the rolled thread stud specification, MIL-DTL-24789(SH), to mitigate the potential effects on fatigue acceptance data.« less

Fatigue test results of the rotating steel blades of steam turbine K-25-0.6 GEO with ion-plasma coating

NASA Astrophysics Data System (ADS)

Kachalin, G. V.; Mednikov, A. F.; Tkhabisimov, A. B.; Arkad'ev, D. A.; Temkin, S. G.; Senina, N. A.

2016-12-01

Fatigue test results of the rotating steel blades of the fourth stage of the K-25-0.6 low pressure cylinder Geo steam turbine manufactured in the Kaluga Turbine Plant (hereinafter, KTP) with the ion-plasma coating were presented. Coating formation was carried out at the National Research University (MPEI) on the Gefest vacuum pilot plant by the magnetron sputtering method. Characteristics of the obtained coating were analyzed with the use of the scientific-research equipment of the National Research University (MPEI). Fatigue tests of the rotating blades and determination of the fatigue strength of the material with the ion-plasma coating were carried out on the electrodynamic vibration machines VEDS-400A in the KTP structural laboratory. The following characteristics were obtained after tests: Ti-TiN composition, 10-11 μm thickness, 1200 HV 0.05 microhardness. Fatigue tests showed that destruction, regardless of availability or nonavailability of the coating, took place by cross-section in the root zone both on the leading and trailing edges of the blade, i.e., in the most stressed zones. It was found out that the maximum stresses during tests were revealed in the root section along the trailing edge on the blade pressure side, and the less stresses were on the leading edge. Fatigue strength of the working blades after coating formation increased by 12% minimum. Results of the fatigue tests prove the previously obtained data concerning 10-12% increase of the fatigue strength of the blade steel with the ion-plasma coating and allow claiming that the process of their formation exerts the positive influence on the fatigue characteristics of the blade materials.

Study on Determination Method of Fatigue Testing Load for Wind Turbine Blade

NASA Astrophysics Data System (ADS)

Liao, Gaohua; Wu, Jianzhong

2017-07-01

In this paper, the load calculation method of the fatigue test was studied for the wind turbine blade under uniaxial loading. The characteristics of wind load and blade equivalent load were analyzed. The fatigue property and damage theory of blade material were studied. The fatigue load for 2MW blade was calculated by Bladed, and the stress calculated by ANSYS. Goodman modified exponential function S-N curve and linear cumulative damage rule were used to calculate the fatigue load of wind turbine blades. It lays the foundation for the design and experiment of wind turbine blade fatigue loading system.

Creep-Fatigue Damage Investigation and Modeling of Alloy 617 at High Temperatures

NASA Astrophysics Data System (ADS)

Tahir, Fraaz

The Very High Temperature Reactor (VHTR) is one of six conceptual designs proposed for Generation IV nuclear reactors. Alloy 617, a solid solution strengthened Ni-base superalloy, is currently the primary candidate material for the tubing of the Intermediate Heat Exchanger (IHX) in the VHTR design. Steady-state operation of the nuclear power plant at elevated temperatures leads to creep deformation, whereas loading transients including startup and shutdown generate fatigue. A detailed understanding of the creep-fatigue interaction in Alloy 617 is necessary before it can be considered as a material for nuclear construction in ASME Boiler and Pressure Vessel Code. Current design codes for components undergoing creep-fatigue interaction at elevated temperatures require creep-fatigue testing data covering the entire range from fatigue-dominant to creep-dominant loading. Classical strain-controlled tests, which produce stress relaxation during the hold period, show a saturation in cycle life with increasing hold periods due to the rapid stress-relaxation of Alloy 617 at high temperatures. Therefore, applying longer hold time in these tests cannot generate creep-dominated failure. In this study, uniaxial isothermal creep-fatigue tests with non-traditional loading waveforms were designed and performed at 850 and 950°C, with an objective of generating test data in the creep-dominant regime. The new loading waveforms are hybrid strain-controlled and force-controlled testing which avoid stress relaxation during the creep hold. The experimental data showed varying proportions of creep and fatigue damage, and provided evidence for the inadequacy of the widely-used time fraction rule for estimating creep damage under creep-fatigue conditions. Micro-scale damage features in failed test specimens, such as fatigue cracks and creep voids, were quantified using a Scanning Electron Microscope (SEM) to find a correlation between creep and fatigue damage. Quantitative statistical imaging analysis showed that the microstructural damage features (cracks and voids) are correlated with a new mechanical driving force parameter. The results from this image-based damage analysis were used to develop a phenomenological life-prediction methodology called the effective time fraction approach. Finally, the constitutive creep-fatigue response of the material at 950°C was modeled using a unified viscoplastic model coupled with a damage accumulation model. The simulation results were used to validate an energy-based constitutive life-prediction model, as a mechanistic model for potential component and structure level creep-fatigue analysis.

Multiaxial Fatigue Life Prediction Based on Nonlinear Continuum Damage Mechanics and Critical Plane Method

NASA Astrophysics Data System (ADS)

Wu, Z. R.; Li, X.; Fang, L.; Song, Y. D.

2018-04-01

A new multiaxial fatigue life prediction model has been proposed in this paper. The concepts of nonlinear continuum damage mechanics and critical plane criteria were incorporated in the proposed model. The shear strain-based damage control parameter was chosen to account for multiaxial fatigue damage under constant amplitude loading. Fatigue tests were conducted on nickel-based superalloy GH4169 tubular specimens at the temperature of 400 °C under proportional and nonproportional loading. The proposed method was checked against the multiaxial fatigue test data of GH4169. Most of prediction results are within a factor of two scatter band of the test results.

Study of fatigue behavior of longitudinal welded pipes

NASA Astrophysics Data System (ADS)

Simion, P.; Dia, V.; Istrate, B.; Hrituleac, G.; Hrituleac, I.; Munteanu, C.

2016-08-01

During transport and storage of the various fluids, welded pipes are subjected to cyclic loading due to pressure fluctuations that often exceed the prescribed values for normal operation. These cyclic loading can significantly reduce the life of the pipes; as a result the design should be based on the fatigue strength not only on static resistance. In general the fatigue strength of pipes is dependent by strength, pipe geometry and surface quality. In case of the electric longitudinal welded pipes, the fatigue strength is significantly limited by concentration of residual stress and the size of existing defects in the weld seam. This paper presents the fatigue behaviour of the electric welded pipes by high frequency, under conditions that simulate real operating conditions pipes. Fatigue testing was performed on welded pipes made of micro alloyed carbon steels. Some of these pipes were previously subjected to a heat treatment of normalization, in order to also determine the influence of heat treatment on the fatigue strength of welded pipes. To determine and correlate the different factors affecting the fatigue strength, welded pipes were also subjected to various tests: tensile tests, impact tests, measurement of micro hardness, microstructural analysis by optical microscopy and scanning electron microscopy.

Indentation hardness: A simple test that correlates with the dissipated-energy predictor for fatigue-life in bovine pericardium membranes for bioprosthetic heart valves.

PubMed

Tobaruela, Almudena; Rojo, Francisco Javier; García Paez, José María; Bourges, Jean Yves; Herrero, Eduardo Jorge; Millán, Isabel; Alvarez, Lourdes; Cordon, Ángeles; Guinea, Gustavo V

2016-08-01

The aim of this study was to evaluate the variation of hardness with fatigue in calf pericardium, a biomaterial commonly used in bioprosthetic heart valves, and its relationship with the energy dissipated during the first fatigue cycle that has been shown to be a predictor of fatigue-life (García Páez et al., 2006, 2007; Rojo et al., 2010). Fatigue tests were performed in vitro on 24 pericardium specimens cut in a root-to-apex direction. The specimens were subjected to a maximum stress of 1MPa in blocks of 10, 25, 50, 100, 250, 500, 1000 and 1500 cycles. By means of a modified Shore A hardness test procedure, the hardness of the specimen was measured before and after fatigue tests. Results showed a significant correlation of such hardness with fatigue performance and with the energy dissipated in the first cycle of fatigue, a predictor of pericardium durability. The study showed indentation hardness as a simple and reliable indicator of mechanical performance, one which could be easily implemented in improving tissue selection. Copyright © 2016 Elsevier Ltd. All rights reserved.

Analysis of the Mechanical Behavior, Creep Resistance and Uniaxial Fatigue Strength of Martensitic Steel X46Cr13

PubMed Central

Brnic, Josip; Krscanski, Sanjin; Lanc, Domagoj; Brcic, Marino; Turkalj, Goran; Canadija, Marko; Niu, Jitai

2017-01-01

The article deals with the analysis of the mechanical behavior at different temperatures, uniaxial creep and uniaxial fatigue of martensitic steel X46Cr13 (1.4034, AISI 420). For the purpose of considering the aforementioned mechanical behavior, as well as determining the appropriate resistance to creep and fatigue strength levels, numerous uniaxial tests were carried out. Tests related to mechanical properties performed at different temperatures are presented in the form of engineering stress-strain diagrams. Short-time creep tests performed at different temperatures and different stress levels are presented in the form of creep curves. Fatigue tests carried out at stress ratios R=0.25 and R=−1 are shown in the form of S–N (fatigue) diagrams. The finite fatigue regime for each of the mentioned stress ratios is modeled by an inclined log line, while the infinite fatigue regime is modeled by a horizontal line, which represents the fatigue limit of the material and previously was calculated by the modified staircase method. Finally, the fracture toughness has been calculated based on the Charpy V-notch impact energy. PMID:28772749

Developing measures of fatigue using an alcohol comparison to validate the effects of fatigue on performance.

PubMed

Williamson, A M; Feyer, A M; Mattick, R P; Friswell, R; Finlay-Brown, S

2001-05-01

The effects of 28 h of sleep deprivation were compared with varying doses of alcohol up to 0.1% blood alcohol concentration (BAC) in the same subjects. The study was conducted in the laboratory. Twenty long-haul truck drivers and 19 people not employed as professional drivers acted as subjects. Tests were selected that were likely to be affected by fatigue, including simple reaction time, unstable tracking, dual task, Mackworth clock vigilance test, symbol digit coding, visual search, sequential spatial memory and logical reasoning. While performance effects were seen due to alcohol for all tests, sleep deprivation affected performance on most tests, but had no effect on performance on the visual search and logical reasoning tests. Some tests showed evidence of a circadian rhythm effect on performance, in particular, simple reaction time, dual task, Mackworth clock vigilance, and symbol digit coding, but only for response speed and not response accuracy. Drivers were slower but more accurate than controls on the symbol digit test, suggesting that they took a more conservative approach to performance of this test. This study demonstrated which tests are most sensitive to sleep deprivation and fatigue. The study therefore has established a set of tests that can be used in evaluations of fatigue and fatigue countermeasures.

Evaluating cyclic fatigue of sealants during outdoor testing

Treesearch

R. Sam Williams; Steven Lacher; Corey Halpin; Christopher White

2009-01-01

A computer-controlled test apparatus (CCTA) and other instrumentation for subjecting sealant specimens to cyclic fatigue during outdoor exposure was developed. The CCTA enables us to use weather-induced conditions to cyclic fatigue specimens and to conduct controlled tests in-situ during the outdoor exposure. Thermally induced dimensional changes of an aluminum bar...

A Full-Scale Fatigue Test of 9-m CX-100 Wind Turbine Blades

DTIC Science & Technology

2011-09-01

A Full-Scale Fatigue Test of 9-m CX-100 Wind Turbine Blades G. PARK, K. M. FARINHOLT, S. G. TAYLOR and C. R. FARRAR ABSTRACT This paper...presents the SHM result of a 9m CX-100 wind turbine blade under full- scale fatigue loads. The test was performed at the National Renewable Energy...surface of the blade. The blade underwent fatigue excitation at 1.8 Hz for defined intervals, and data from the sensors were collected between and

Method of Fatigue-Life Prediction for an Asphalt Mixture Based on the Plateau Value of Permanent Deformation Ratio.

PubMed

Sun, Yazhen; Fang, Chenze; Wang, Jinchang; Yuan, Xuezhong; Fan, Dong

2018-05-03

Laboratory predictions for the fatigue life of an asphalt mixture under cyclic loading based on the plateau value (PV) of the permanent deformation ratio (PDR) were carried out by three-point bending fatigue tests. The influence of test conditions on the recovery ratio of elastic deformation (RRED), the permanent deformation (PD) and PDR, and the trends of RRED, PD, and PDR were studied. The damage variable was defined by using PDR, and the relation of the fatigue life to PDR was determined by analyzing the damage evolution process. The fatigue equation was established based on the PV of PDR and the fatigue life was predicted by analyzing the relation of the fatigue life to the PV. The results show that the RRED decreases with the increase of the number of loading cycles, and the elastic recovery ability of the asphalt mixture gradually decreases. The two mathematical models proposed are based on the change laws of the RRED, and the PD can well describe the change laws. The RRED or the PD cannot well predict the fatigue life because they do not change monotonously with the fatigue life, and one part of the deformation causes the damage and the other part causes the viscoelastic deformation. The fatigue life decreases with the increase of the PDR. The average PDR in the second stage is taken as the PV, and the fatigue life decreases in a power law with the increase of the PV. The average relative error of the fatigue life predicted by the fatigue equation to the test fatigue life is 5.77%. The fatigue equation based on PV can well predict the fatigue life.

Linking asphalt binder fatigue to asphalt mixture fatigue performance using viscoelastic continuum damage modeling

NASA Astrophysics Data System (ADS)

Safaei, Farinaz; Castorena, Cassie; Kim, Y. Richard

2016-08-01

Fatigue cracking is a major form of distress in asphalt pavements. Asphalt binder is the weakest asphalt concrete constituent and, thus, plays a critical role in determining the fatigue resistance of pavements. Therefore, the ability to characterize and model the inherent fatigue performance of an asphalt binder is a necessary first step to design mixtures and pavements that are not susceptible to premature fatigue failure. The simplified viscoelastic continuum damage (S-VECD) model has been used successfully by researchers to predict the damage evolution in asphalt mixtures for various traffic and climatic conditions using limited uniaxial test data. In this study, the S-VECD model, developed for asphalt mixtures, is adapted for asphalt binders tested under cyclic torsion in a dynamic shear rheometer. Derivation of the model framework is presented. The model is verified by producing damage characteristic curves that are both temperature- and loading history-independent based on time sweep tests, given that the effects of plasticity and adhesion loss on the material behavior are minimal. The applicability of the S-VECD model to the accelerated loading that is inherent of the linear amplitude sweep test is demonstrated, which reveals reasonable performance predictions, but with some loss in accuracy compared to time sweep tests due to the confounding effects of nonlinearity imposed by the high strain amplitudes included in the test. The asphalt binder S-VECD model is validated through comparisons to asphalt mixture S-VECD model results derived from cyclic direct tension tests and Accelerated Loading Facility performance tests. The results demonstrate good agreement between the asphalt binder and mixture test results and pavement performance, indicating that the developed model framework is able to capture the asphalt binder's contribution to mixture fatigue and pavement fatigue cracking performance.

Advanced Gear Alloys for Ultra High Strength Applications

NASA Technical Reports Server (NTRS)

Shen, Tony; Krantz, Timothy; Sebastian, Jason

2011-01-01

Single tooth bending fatigue (STBF) test data of UHS Ferrium C61 and C64 alloys are presented in comparison with historical test data of conventional gear steels (9310 and Pyrowear 53) with comparable statistical analysis methods. Pitting and scoring tests of C61 and C64 are works in progress. Boeing statistical analysis of STBF test data for the four gear steels (C61, C64, 9310 and Pyrowear 53) indicates that the UHS grades exhibit increases in fatigue strength in the low cycle fatigue (LCF) regime. In the high cycle fatigue (HCF) regime, the UHS steels exhibit better mean fatigue strength endurance limit behavior (particularly as compared to Pyrowear 53). However, due to considerable scatter in the UHS test data, the anticipated overall benefits of the UHS grades in bending fatigue have not been fully demonstrated. Based on all the test data and on Boeing s analysis, C61 has been selected by Boeing as the gear steel for the final ERDS demonstrator test gearboxes. In terms of potential follow-up work, detailed physics-based, micromechanical analysis and modeling of the fatigue data would allow for a better understanding of the causes of the experimental scatter, and of the transition from high-stress LCF (surface-dominated) to low-stress HCF (subsurface-dominated) fatigue failure. Additional STBF test data and failure analysis work, particularly in the HCF regime and around the endurance limit stress, could allow for better statistical confidence and could reduce the observed effects of experimental test scatter. Finally, the need for further optimization of the residual compressive stress profiles of the UHS steels (resulting from carburization and peening) is noted, particularly for the case of the higher hardness C64 material.

Fatigue testing of energy storing prosthetic feet.

PubMed

Toh, S L; Goh, J C; Tan, P H; Tay, T E

1993-12-01

This paper describes a simple approach to the fatigue testing of prosthetic feet. A fatigue testing machine for prosthetic feet was designed as part of the programme to develop an energy storing prosthetic foot (ESPF). The fatigue tester does not simulate the loading pattern on the foot during normal walking. However, cyclic vertical loads are applied to the heel and forefoot during heel-strike and toe-off respectively, for 500,000 cycles. The maximum load applied was chosen to be 1.5 times that applied by the bodyweight of the amputee and the test frequency was chosen to be 2 Hz to shorten the test duration. Four prosthetic feet were tested: two Lambda feet (a newly developed ESPF), a Kingsley SACH foot and a Proteor SACH foot. It was found that the Lambda feet have very good fatigue properties. The Kingsley SACH foot performed better than the Proteor model, with no signs of wear at the heel. The results obtained using the simple approach was found to be comparable to the results from more complex fatigue machines which simulate the load pattern during normal walking. This suggests that simple load simulating machines, which are less costly and require less maintenance, are useful substitutes in studying the fatigue properties of prosthetic feet.

A comparison of fatigue life prediction methodologies for rotorcraft

NASA Technical Reports Server (NTRS)

Everett, R. A., Jr.

1990-01-01

Because of the current U.S. Army requirement that all new rotorcraft be designed to a 'six nines' reliability on fatigue life, this study was undertaken to assess the accuracy of the current safe life philosophy using the nominal stress Palmgrem-Miner linear cumulative damage rule to predict the fatigue life of rotorcraft dynamic components. It has been shown that this methodology can predict fatigue lives that differ from test lives by more than two orders of magnitude. A further objective of this work was to compare the accuracy of this methodology to another safe life method called the local strain approach as well as to a method which predicts fatigue life based solely on crack growth data. Spectrum fatigue tests were run on notched (k(sub t) = 3.2) specimens made of 4340 steel using the Felix/28 tests fairly well, being slightly on the unconservative side of the test data. The crack growth method, which is based on 'small crack' crack growth data and a crack-closure model, also predicted the fatigue lives very well with the predicted lives being slightly longer that the mean test lives but within the experimental scatter band. The crack growth model was also able to predict the change in test lives produced by the rainflow reconstructed spectra.

Ultrasonic fatigue of SiC particle reinforced aluminum in the VHCF-regime

NASA Astrophysics Data System (ADS)

Wolf, M.; Wagner, G.; Eifler, D.

At the WKK ultrasonic testing facilities (UTF) are used to perform fatigue experiments in the VHCF regime with a frequency of 20 kHz. These systems allow an on-line characterization of the actual fatigue state by changes of different process parameters such as generator power, displacement, temperature or frequency-response characteristic. Moreover the experiments can be interrupted at user defined events in order to investigate variations of the surface microstructure or changes in the electrical resistance of the specimens. The fatigue tests were realized as load increase tests as well as constant amplitude tests.

Crack propagation analysis and fatigue life prediction for structural alloy steel based on metal magnetic memory testing

NASA Astrophysics Data System (ADS)

Ni, Chen; Hua, Lin; Wang, Xiaokai

2018-09-01

To monitor the crack propagation and predict the fatigue life of ferromagnetic material, the metal magnetic memory (MMM) testing was carried out to the single edge notched specimen made from structural alloy steel under three-point bending fatigue experiment in this paper. The variation of magnetic memory signal Hp (y) in process of fatigue crack propagation was investigated. The gradient K of Hp (y) was investigated and compared with the stress of specimen obtained by finite element analysis. It indicated that the gradient K can qualitatively reflect the distribution and variation of stress. The maximum gradient Kmax and crack size showed a good linear relationship, which indicated that the crack propagation can be estimated by MMM testing. Furthermore, the damage model represented by magnetic memory characteristic was created and a fatigue life prediction method was developed. The fatigue life can be evaluated by the relationship between damage parameter and normalized life. The method was also verified by another specimen. Because of MMM testing, it provided a new approach for predicting fatigue life.

Preliminary Study on Fatigue Strengths of Fretted Ti-48Al-2Cr-2Nb

NASA Technical Reports Server (NTRS)

Miyoshi, Kazuhisa; Lerch, Bradley A.; Draper, Susan L.

2002-01-01

The fatigue behavior (stress-life curve) of gamma titanium aluminide (Ti-48Al-2Cr-2Nb, atomic percent) was examined by conducting two tests: first, a fretting wear test with a fatigue specimen in contact with a typical nickel-based superalloy contact pad in air at temperatures of 296 and 823 K and second, a high-cycle fatigue test of the prefretted Ti-48Al-2Cr-2Nb fatigue specimen at 923 K. Reference high-cycle fatigue tests were also conducted with unfretted Ti-48Al-2Cr-2Nb specimens at 923 K. All Ti-48Al-2Cr-2Nb fatigue specimens were machined from cast slabs. The results indicate that the stress-life results for the fretted Ti-48Al-2Cr-2Nb specimens exhibited a behavior similar to those of the unfretted Ti-48Al-2Cr-2Nb specimens. The values of maximum stress and life for the fretted specimens were almost the same as those for the unfretted specimens. The resultant stress-life curve for the unfretted fatigue specimens was very flat. The flat appearance in the stress-life curve of the unfretted specimens is attributed to the presence of a high density of casting pores. The fatigue strengths of both the fretted and unfretted specimens can be significantly affected by the presence of this porosity, which can decrease the fatigue life of Ti-48Al-2Cr-2Nb. The presence of the porosity made discerning the effect of fretting damage on fatigue strength and life of the specimens difficult.

Analysis of the binder yield energy test as an indicator of fatigue behaviour of asphalt mixes

NASA Astrophysics Data System (ADS)

O'Connell, Johan; Mturi, Georges A. J.; Komba, Julius; Du Plessis, Louw

2017-09-01

Empirical binder testing has increasingly failed to predict pavement performance in South Africa, with fatigue cracking being one of the major forms of premature pavement distress. In response, it has become a national aspiration to incorporate a performance related fatigue test into the binder specifications for South Africa. The Binder Yield Energy Test (BYET) was the first in a series of tests analysed for its potential to predict the fatigue performance of the binder. The test is performed with the dynamic shear rheometer, giving two key parameters, namely, yield energy and shear strain at maximum shear stress (γτmax). The objective of the investigation was to perform a rudimentary evaluation of the BYET; followed by a more in-depth investigation should the initial BYET results prove promising. The paper discusses the results generated from the BYET under eight different conditions, using six different binders. The results are then correlated with four point bending beam fatigue test results obtained from asphalt mix samples that were manufactured from the same binders. Final results indicate that the BYET is not ideal as an indicator of fatigue performance.

Low-cycle thermal fatigue

NASA Technical Reports Server (NTRS)

Halford, G. R.

1986-01-01

A state-of-the-art review is presented of the field of thermal fatigue. Following a brief historical review, the concept is developed that thermal fatigue can be viewed as processes of unbalanced deformation and cracking. The unbalances refer to dissimilar mechanisms occurring in opposing halves of thermal fatigue loading and unloading cycles. Extensive data summaries are presented and results are interpreted in terms of the unbalanced processes involved. Both crack initiation and crack propagation results are summarized. Testing techniques are reviewed, and considerable discussion is given to a technique for thermal fatigue simulation, known as the bithermal fatigue test. Attention is given to the use of isothermal life prediction methods for the prediction of thermal fatigue lives. Shortcomings of isothermally-based life prediction methods are pointed out. Several examples of analyses and thermal fatigue life predictions of high technology structural components are presented. Finally, numerous dos and don'ts relative to design against thermal fatigue are presented.

Removal Torque and Biofilm Accumulation at Two Dental Implant-Abutment Joints After Fatigue.

PubMed

Pereira, Jorge; Morsch, Carolina S; Henriques, Bruno; Nascimento, Rubens M; Benfatti, Cesar Am; Silva, Filipe S; López-López, José; Souza, Júlio Cm

2016-01-01

The aim of this study was to evaluate the removal torque and in vitro biofilm penetration at Morse taper and hexagonal implant-abutment joints after fatigue tests. Sixty dental implants were divided into two groups: (1) Morse taper and (2) external hexagon implant-abutment systems. Fatigue tests on the implant-abutment assemblies were performed at a normal force (FN) of 50 N at 1.2 Hz for 500,000 cycles in growth medium containing human saliva for 72 hours. Removal torque mean values (n = 10) were measured after fatigue tests. Abutments were then immersed in 1% protease solution in order to detach the biofilms for optical density and colony-forming unit (CFU/cm²) analyses. Groups of implant-abutment assemblies (n = 8) were cross-sectioned at 90 degrees relative to the plane of the implant-abutment joints for the microgap measurement by field-emission guns scanning electron microscopy. Mean values of removal torque on abutments were significantly lower for both Morse taper (22.1 ± 0.5 μm) and external hexagon (21.1 ± 0.7 μm) abutments after fatigue tests than those recorded without fatigue tests (respectively, 24 ± 0.5 μm and 24.8 ± 0.6 μm) in biofilm medium for 72 hours (P = .04). Mean values of microgap size for the Morse taper joints were statistically signicantly lower without fatigue tests (1.7 ± 0.4 μm) than those recorded after fatigue tests (3.2 ± 0.8 μm). Also, mean values of microgap size for external hexagon joints free of fatigue were statistically signicantly lower (1.5 ± 0.4 μm) than those recorded after fatigue tests (8.1 ± 1.7 μm) (P < .05). The optical density of biofilms and CFU mean values were lower on Morse taper abutments (Abs630nm at 0.06 and 2.9 × 10⁴ CFU/cm²) than that on external hexagon abutments (Abs630nm at 0.08 and 4.5 × 10⁴ CFU/cm²) (P = .01). The mean values of removal torque, microgap size, and biofilm density recorded at Morse taper joints were lower in comparison to those recorded at external hexagon implant-abutment joints after fatigue tests in a simulated oral environment for 72 hours.

Low cycle fatigue behavior of polycrystalline NiAl at 300 and 1000 K

NASA Technical Reports Server (NTRS)

Lerch, Bradley A.; Noebe, Ronald D.

1993-01-01

The low cycle fatigue behavior of polycrystalline NiAl was determined at 300 and 1000 K - temperatures below and above the brittle- to-ductile transition temperature (BDTT). Fully reversed, plastic strain-controlled fatigue tests were conducted on two differently fabricated alloy samples: hot isostatically pressed (HIP'ed) prealloyed powder and hot extruded castings. HIP'ed powder (HP) samples were tested only at 1000 K, whereas the more ductile cast-and-extruded (C+E) NiAl samples were tested at both 1000 and 300 K. Plastic strain ranges of 0.06 to 0.2 percent were used. The C+E NiAl cyclically hardened until fracture, reaching stress levels approximately 60 percent greater than the ultimate tensile strength of the alloy. Compared on a strain basis, NiAl had a much longer fatigue life than other B2 ordered compounds in which fracture initiated at processing-related defects. These defects controlled fatigue life at 300 K, with fracture occurring rapidly once a critical stress level was reached. At 1000 K, above the BDTT, both the C+E and HP samples cyclically softened during most of the fatigue tests in air and were insensitive to processing defects. The processing method did not have a major effect on fatigue life; the lives of the HP samples were about a factor of three shorter than the C+E NiAl, but this was attributed to the lower stress response of the C+E material. The C+E NiAl underwent dynamic grain growth, whereas the HP material maintained a constant grain size during testing. In both materials, fatigue life was controlled by intergranular cavitation and creep processes, which led to fatigue crack growth that was primarily intergranular in nature. Final fracture by overload was transgranular in nature. Also, HP samples tested in vacuum had a life three times longer than their counterparts tested in air and, in contrast to those tested in air, hardened continuously over half of the sample life, thereby indicating an environmentally assisted fatigue damage mechanism. The C+E samples were tested only in air. At 1000 K, NiAl exhibited a superior fatigue life when compared to most superalloys on a plastic strain basis, but was inferior to most superalloys on a stress basis.

Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP)

Treesearch

Jinghao Li; John F. Hunt; Shaoqin Gong; Zhiyong Cai

2015-01-01

The static and fatigue bending behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP) has been investigated by four-point bending tests. Fatigue panels and weakened panels (wESCP) with an initial interface defect were manufactured for the fatigue tests. Stress σ vs. number of cycles curves (S-N) were recorded under the different stress...

Fatigue in people with localized colorectal cancer who do and do not receive chemotherapy: a longitudinal prospective study

PubMed Central

Vardy, J. L.; Dhillon, H. M.; Pond, G. R.; Renton, C.; Dodd, A.; Zhang, H.; Clarke, S. J.; Tannock, I. F.

2016-01-01

Background Fatigue is associated with cancer and chemotherapy and may be sustained. Here, we describe a prospective longitudinal study evaluating fatigue and putative mechanisms in people with colorectal cancer (CRC). Patients and methods People with localized CRC completed the Functional Assessment of Cancer Treatment-Fatigue (FACT-F) questionnaire at baseline (before chemotherapy, if given), 6, 12, and 24 months. Healthy controls (HCs) were assessed at the first three time points. Fatigue was defined by standardized FACT-F scores ≤68/100. Quality-of-life (QoL, assessed by the FACT-G questionnaire), affective, and cognitive symptoms were evaluated. Associations were sought between fatigue, baseline factors, and blood tests (including hemoglobin, cytokines, and sex hormones). Regression analyses, Fisher's exact tests, and Wilcoxon rank-sum tests assessed levels of fatigue at each time point and change in fatigue from baseline. A repeated-measures analysis investigated prognostic factors of fatigue across all time points. Results A total of 289 subjects with localized CRC (173 received chemotherapy) and 72 HCs were assessed. More CRC patients had fatigue than HCs at baseline (52% versus 26%, P < 0.001). Fatigue was increased in the chemotherapy (CTh) group at 6 months [CTh+ 70% versus CTh− 31% (P < 0.001), HCs 22%] and remained more common at 12 [CTh+ 44% versus CTh− 31% (P = 0.079)] and 24 months [CTh+ 39% versus CTh− 24% (P = 0.047)]. There was no significant difference between those not receiving chemotherapy and HCs at follow-up assessments. Fatigue was associated with poor QoL, affective and cognitive symptoms, but not consistently with cytokine levels. Predictors for sustained fatigue were baseline fatigue, treatment group, cognitive and affective symptoms, poorer QoL, and comorbidities. Conclusions CRC patients have more fatigue than HCs at baseline. Fatigue peaks immediately after adjuvant chemotherapy, but remains common for 2 years in those who receive chemotherapy. Cognitive and affective symptoms, QoL, comorbidities, chemotherapy, and baseline fatigue predict for longer term fatigue. PMID:27443634

Cyclic fatigue behavior of nickel-titanium dental rotary files in clinical simulated root canals.

PubMed

Chi, Chih-Wen; Li, Chun-Chieh; Lin, Chun-Pin; Shin, Chow-Shing

2017-04-01

Dental rotary instruments can be applied in multiple conditions of canals, but unpredictable fatigue fracture may happen. This study evaluated the fatigue lives of two batches of nickel-titanium (NiTi) dental rotary files operating in clinically simulated root canals. Single-step cyclic fatigue tests were carried out to assess the performance of two batches of NiTi files (ProTaper and ProFile) in nine combinations of simulated canals (cylinder radii 5 mm, 7.5 mm, and 10 mm, and insertion angles 20°, 40°, and 60°). Two-step cyclic fatigue tests were carried out in simulated root canals with the same radius by using the following two sets of insertion angles: (20°, 40°), (20°, 60°), (40°, 20°), and (60°, 20°). Fracture surfaces were observed by scanning electron microscopy. The single-step cyclic fatigue results showed that cyclic fatigue lives of the files decreased with increasing insertion angles or decreasing cylinder radius. The ProFile #25 .04 file was more fatigue resistant than the ProTaper F2 file. In two-step cyclic fatigue tests, the total fatigue lives were usually more than 100% when the files operated at a lower strain and then at a higher strain. By scanning electron microscopy, a larger area of fatigue striation corresponded to a longer fatigue life. Cyclic fatigue life can be influenced by the strains and geometries of files. The fatigue life was prolonged when the files operated at a lower strain and then at a higher strain. However, the fatigue life was shortened if the loading sequence was reversed. Copyright © 2016. Published by Elsevier B.V.

Evaluation of materials during outdoor testing using a computer-controlled test apparatus

Treesearch

R. Sam Williams; Steven Lacher; Corey Halpin; Christopher White

2006-01-01

Ultraviolet radiation, moisture, heat, and cyclic fatigue are some of the stressors that cause materials to degrade outdoors. Considerable research has addressed the effects of ultraviolet radiation and moisture on the rate of this degradation. An often overlooked stressor on materials, during outdoor testing, is the cyclic fatigue. Cyclic fatigue is caused by self-...

75 FR 8479 - Airworthiness Directives; Airbus Model A340-541 and -642 Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2010-02-25

... A340-600 full scale fatigue test, cracks were found on left and right sides of the rear spar vertical... scale fatigue test, cracks were found on left and right sides of the rear spar vertical cruciform at... this full scale fatigue test completion, it has been determined that the current inspections values...

Crack Initiation and Growth Behavior at Corrosion Pit in 2024-T3 Aluminum Alloy

DTIC Science & Technology

2014-09-01

63 Figure B.1: The crack length vs. number of cycles during fatigue testing for the 2AI-01 specimen...number of cycles during fatigue testing for the the 2AI- 02 specimen...64 Figure B.3: The crack length vs. number of cycles during fatigue testing for the 2Sl-01 specimen

[The effects of foot reflexology on fatigue and insomnia in patients suffering from coal workers' pneumoconiosis].

PubMed

Lee, Young-Mee; Sohng, Kyeong-Yae

2005-12-01

The purpose of this study was to determine the effects of foot reflexology on fatigue and insomnia in patients suffering from coal workers' pneumoconiosis. This study was a quasi-experimental study of pre-test and post-test design in a non-equivalent control group. The subjects of this study consisted of both the experimental group of twenty-nine and the control group of thirty coal workers' pneumoconiosis patients. Data was collected from December 10, 2002 to February 15, 2003. Foot reflexology was performed for 60 minutes twice a week through five weeks in the experimental group, but none in the control group. To evaluate the effects of foot reflexology, the scores of fatigue and insomnia were measured before and after the experiment in both groups. Fatigue was evaluated by Fatigue Symptoms Inventory. Insomnia was measured with the visual analogue scale (VAS). Data of this experiment was analyzed by Chi-square test, t-test, unpaired t-test and Repeated Measures ANOVA with the SAS Program. The scores of fatigue and insomnia decreased in the experimental group but not in the control group. There was a significant difference of fatigue and insomnia between the two groups. It is suggested that foot reflexology might have beneficial effects on reducing fatigue and insomnia in patients suffering from coal workers' pneumoconiosis, and can be recommended as a nursing intervention program for patients with coal workers' pneumoconiosis.

Effect of Creep and Oxidation on Reduced Creep-Fatigue life of Ni-based Alloy 617 at 850 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xiang; Yang, Zhiqing; Sokolov, Mikhail A

Low cycle fatigue (LCF) and creep fatigue testing of Ni-based alloy 617 was carried out at 850 C. Compared with its LCF life, the material s creep fatigue life decreases to different extents depending on test conditions. To elucidate the microstructure-fatigue property relationship for alloy 617 and the effect of creep and oxidation on its fatigue life, systematic microstructural investigations were carried out using scanning electron microscopy, energy-dispersive X-ray spectroscopy, and electron backscatter diffraction (EBSD). In LCF tests, as the total strain range increased, deformations concentrated near high angle grain boundaries (HAGBs). The strain hold period in the creep fatiguemore » tests introduced additional creep damage to the material, which revealed the detrimental effect of the strain hold time on the material fatigue life in two ways. First, the strain hold time enhanced the localized deformation near HAGBs, resulting in the promotion of intergranular cracking of alloy 617. Second, the strain hold time encouraged grain boundary sliding, which resulted in interior intergranular cracking of the material. Oxidation accelerated the initiation of intergranular cracking in alloy 617. In the crack propagation stage, if oxidation was promoted and the cyclic oxidation damage was greater than the fatigue damage, oxidation-assisted intergranular crack growth resulted in a significant reduction in the material s fatigue life.« less

Effect of welding structure and δ-ferrite on fatigue properties for TIG welded austenitic stainless steels at cryogenic temperatures

NASA Astrophysics Data System (ADS)

Yuri, Tetsumi; Ogata, Toshio; Saito, Masahiro; Hirayama, Yoshiaki

2000-04-01

High-cycle and low-cycle fatigue properties of base and weld metals for SUS304L and SUS316L and the effects of welding structure and δ-ferrite on fatigue properties were investigated at cryogenic temperatures in order to evaluate the long-life reliability of the structural materials to be used in liquid hydrogen supertankers and storage tanks and to develop a welding process for these applications. The S-N curves of the base and weld metals shifted towards higher levels, i.e., the longer life side, with decreasing test temperatures. High-cycle fatigue tests demonstrated the ratios of fatigue strength at 10 6 cycles to tensile strength of the weld metals to be 0.35-0.7, falling below those of base metals with decreasing test temperatures. Fatigue crack initiation sites in SUS304L weld metals were mostly at blowholes with diameters of 200-700 μm, and those of SUS316L weld metals were at weld pass interface boundaries. Low-cycle fatigue tests revealed the fatigue lives of the weld metals to be somewhat lower than those of the base metals. Although δ-ferrite reduces the toughness of austenitic stainless steels at cryogenic temperatures, the effects of δ-ferrite on high-cycle and low-cycle fatigue properties are not clear or significant.

Investigation of fatigue by Australian general practice registrars: a cross-sectional study.

PubMed

Morgan, Simon; Henderson, Kim M; Tapley, Amanda; Thomson, Allison; Wilson, Jessica; Scott, John; Spike, Neil A; McArthur, Lawrie; van Driel, Mieke L; Magin, Parker J

2015-06-01

Fatigue is the most common undifferentiated problem presenting in general practice. Previous studies have shown that this presentation leads to multiple investigations. There is no published literature describing the management of patients with fatigue by general practice (GP) registrars. To document the investigation-ordering behaviour of GP registrars in managing patients with a new diagnosis of unexplained fatigue. This was a cross-sectional analysis of data from Registrar Clinical Encounters in Training (ReCEnT), an ongoing cohort study of GP registrars' consultations. We established the prevalence of new diagnoses of unexplained fatigue and associations with that diagnosis, the rate of test ordering and the number and types of investigations ordered. 644 registrars contributed data from 68 986 encounters. In 0.78% of patient encounters, a new diagnosis of unexplained fatigue was made. Pathology was ordered in 78.4% of these problems (versus 18.1% in non-fatigue problems), at a rate of 488 tests per 100 new fatigue problems. Our study suggests that unexplained fatigue elicits a non-rational approach to test ordering by registrars. These findings contribute to the understanding of GP registrar management of fatigue, and undifferentiated presentations more broadly, and suggest educational approaches to improve practice, including dealing with uncertainty.

Accelerated fatigue durability of a high performance composite

NASA Technical Reports Server (NTRS)

Rotem, A.

1982-01-01

The fatigue behavior of multidirectional graphite-epoxy laminates was analyzed theoretically and experimentally in an effort to establish an accelerated testing methodology. Analysis of the failure mechanism in fatigue of the laminates led to the determination of the failure mode governing fracture. The nonlinear, cyclic-dependent shear modulus was used to calculate the changing stress field in the laminate during the fatigue loading. Fatigue tests were performed at three different temperatures: 25 C, 74 C, and 114 C. The prediction of the S-N curves was made based on the artificial static strength artificial static strength at a reference temperature and the fatigue functions associated with them. The prediction of an S-N curve at other temperatures was performed using shifting factors determined for the specific failure mode. For multidirectional laminates, different S-N curves at different temperatures could be predicted using these shifting factors. Different S-N curves at different temperatures occur only when the fatigue failure mode is matrix dominated. It was found that whenever the fatigue failure mode is fiber dominated, temperature, over the range investigated, had no influence on the fatigue life. These results permit the prediction of long-time, low temperature fatigue behavior from data obtained in short time, high temperature testing, for laminates governed by a matrix failure mode.

Four-point-bending-fatigue behavior of the Zr-based Vitreloy 105 bulk metallic glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morrison, M. L.; Buchanan, R. A.; Liaw, Peter K

The purpose of this study was to make a direct comparison between four-point-bending and uniaxial fatigue tests with the Zr{sub 52.5}Cu{sub 17.9}Ni{sub 14.6}Al{sub 10.0}Ti{sub 5.0} (at.%) BMG alloy (Vitreloy 105). The fatigue lifetimes in four-point bending were found to be greater than those reported in uniaxial testing. However, the fatigue-endurance limit found in four-point bending was slightly less than that reported for uniaxial fatigue. Thus, the significant differences between fatigue studies in the literature are not likely due to this difference in testing geometry. On the contrary, the fatigue lifetimes were found to be highly dependent upon surface defects andmore » material quality. The four-point-bending-fatigue performance of the Vit 105 alloy was found to be greater than most BMGs and similar to the 300 M high-strength steel and other crystalline alloys in spite of not being 'perfectly amorphous.' Due to the detrimental effects of these inhomogeneities and wear at the supporting pins, this fatigue behavior can be assumed to be a conservative estimate of the potential fatigue performance of a perfectly amorphous and homogeneous BMG.« less

The effects of mental fatigue on cricket-relevant performance among elite players.

PubMed

Veness, Darren; Patterson, Stephen David; Jeffries, Owen; Waldron, Mark

2017-12-01

This study investigated the effects of a mentally fatiguing test on physical tasks among elite cricketers. In a cross-over design, 10 elite male cricket players from a professional club performed a cricket run-two test, a Batak Lite reaction time test and a Yo-Yo-Intermittent Recovery Level 1 (Yo-Yo-IR1) test, providing a rating of perceived exertion (RPE) after completing a 30-min Stroop test (mental fatigue condition) or 30-min control condition. Perceived fatigue was assessed before and after the two conditions and motivation was measured before testing. There were post-treatment differences in the perception of mental fatigue (P < 0.001; d = -7.82, 95% CIs = -9.05-6.66; most likely). Cricket run-two (P = 0.002; d = -0.51, 95% CIs = -0.72-0.30; very likely), Yo-Yo-IR1 distance (P = 0.023; d = 0.39, 95% CIs = 0.14-0.64; likely) and RPE (P = 0.001; d = -1.82, 95% CIs = -2.49-1.14; most likely) were negatively affected by mental fatigue. The Batak Lite test was not affected (P = 0.137), yet a moderate (d = 0.41, 95% CIs = -0.05-0.87) change was likely. Mental fatigue, induced by an app-based Stroop test, negatively affected cricket-relevant performance.

A novel evaluation strategy for fatigue reliability of flexible nanoscale films

NASA Astrophysics Data System (ADS)

Zheng, Si-Xue; Luo, Xue-Mei; Wang, Dong; Zhang, Guang-Ping

2018-03-01

In order to evaluate fatigue reliability of nanoscale metal films on flexible substrates, here we proposed an effective evaluation way to obtain critical fatigue cracking strain based on the direct observation of fatigue damage sites through conventional dynamic bending testing technique. By this method, fatigue properties and damage behaviors of 930 nm-thick Au films and 600 nm-thick Mo-W multilayers with individual layer thickness 100 nm on flexible polyimide substrates were investigated. Coffin-Manson relationship between the fatigue life and the applied strain range was obtained for the Au films and Mo-W multilayers. The characterization of fatigue damage behaviors verifies the feasibility of this method, which seems easier and more effective comparing with the other testing methods.

Evaluation of Giga-cycle Fatigue Properties of Austenitic Stainless Steels Using Ultrasonic Fatigue Test

NASA Astrophysics Data System (ADS)

Takahashi, Kyouhei; Ogawa, Takeshi

Ultrasonic fatigue tests have been performed in austenitic stainless steel, SUS316NG, in order to investigate giga-cycle fatigue strength of pre-strained materials, i.e. 5, 10 and 20% tensile pre-strains and -20% compressive pre-strain. The pre-strains were applied before specimen machining. The austenitic stainless steels are known to exhibit remarkable self-heating during the fatigue experiment. Therefore, heat radiation method was established by setting fatigue specimens in a low temperature chamber at about -100°C. The self-heating was controlled by intermittent loading condition, which enabled us to maintain the test section of the specimens at about room temperature. The results revealed that the fatigue strength increased with increasing pre-strain levels. Fish-eye fracture was observed for -20% pre-strained specimen fractured at 4.11×107 cycles, while the other specimens exhibited ordinary fatigue fracture surface originated from stage I facet on the specimen surface. The increase in fatigue limit was predicted by Vickers hardness, HV, which depended on the size of indented region. The prediction was successful using HV values obtained by the size of the indented region similar to those of the stage I facets.

a Study on the Fretting Fatigue Life of Zircaloy Alloys

NASA Astrophysics Data System (ADS)

Kwon, Jae-Do; Park, Dae-Kyu; Woo, Seung-Wan; Chai, Young-Suck

Studies on the strength and fatigue life of machines and structures have been conducted in accordance with the development of modern industries. In particular, fine and repetitive cyclic damage occurring in contact regions has been known to have an impact on fretting fatigue fractures. The main component of zircaloy alloy is Zr, and it possesses good mechanical characteristics at high temperatures. This alloy is used in the fuel rod material of nuclear power plants because of its excellent resistance. In this paper, the effect of the fretting damage on the fatigue behavior of the zircaloy alloy is studied. Further, various types of mechanical tests such as tension and plain fatigue tests are performed. Fretting fatigue tests are performed with a flat-flat contact configuration using a bridge-type contact pad and plate-type specimen. Through these experiments, it is found that the fretting fatigue strength decreases by about 80% as compared to the plain fatigue strength. Oblique cracks are observed in the initial stage of the fretting fatigue, in which damaged areas are found. These results can be used as the basic data for the structural integrity evaluation of corrosion-resisting alloys considering the fretting damages.

Effect of mental fatigue on the central nervous system: an electroencephalography study

PubMed Central

2012-01-01

Background Fatigue can be classified as mental and physical depending on its cause, and each type of fatigue has a multi-factorial nature. We examined the effect of mental fatigue on the central nervous system using electroencephalography (EEG) in eighteen healthy male volunteers. Methods After enrollment, subjects were randomly assigned to two groups in a single-blinded, crossover fashion to perform two types of mental fatigue-inducing experiments. Each experiment consisted of four 30-min fatigue-inducing 0- or 2-back test sessions and two evaluation sessions performed just before and after the fatigue-inducing sessions. During the evaluation session, the participants were assessed using EEG. Eleven electrodes were attached to the head skin, from positions F3, Fz, F4, C3, Cz, C4, P3, Pz, P4, O1, and O2. Results In the 2-back test, the beta power density on the Pz electrode and the alpha power densities on the P3 and O2 electrodes were decreased, and the theta power density on the Cz electrode was increased after the fatigue-inducing mental task sessions. In the 0-back test, no electrodes were altered after the fatigue-inducing sessions. Conclusions Different types of mental fatigue produced different kinds of alterations of the spontaneous EEG variables. Our findings provide new perspectives on the neural mechanisms underlying mental fatigue. PMID:22954020

Modelling and Laboratory Studies on the Adhesion Fatigue Performance for Thin-Film Asphalt and Aggregate System

PubMed Central

Wang, Dongsheng; Feng, Decheng

2014-01-01

Adhesion between asphalt and aggregate plays an important role in the performance of asphalt mixtures. A low-frequency adhesion fatigue test was proposed in this paper to study the effect of environment on the asphalt-aggregate adhesion system. The stress-based fatigue model had been utilized to describe the fatigue behavior of thin-film asphalt and aggregate system. The factors influencing the adhesion fatigue performance were also investigated. Experiment results show that asphalt has more important effect on the adhesion performance comparing with aggregate. Basalt, which is regarded as hydrophobic aggregates with low silica content, has better adhesion performance to asphalt binder when compared with granite. The effects of aging on the adhesion fatigue performance are different for PG64-22 and rubber asphalt. Long-term aging is found to reduce the adhesion fatigue lives for rubber asphalt and aggregate system, while the effect of long-term aging for aggregate and PG64-22 binder system is positive. Generally the increased stress amplitude and test temperature could induce greater damage and lead to less fatigue lives for adhesion test system. PMID:25054187

Modelling and laboratory studies on the adhesion fatigue performance for thin-film asphalt and aggregate system.

PubMed

Wang, Dongsheng; Yi, Junyan; Feng, Decheng

2014-01-01

Adhesion between asphalt and aggregate plays an important role in the performance of asphalt mixtures. A low-frequency adhesion fatigue test was proposed in this paper to study the effect of environment on the asphalt-aggregate adhesion system. The stress-based fatigue model had been utilized to describe the fatigue behavior of thin-film asphalt and aggregate system. The factors influencing the adhesion fatigue performance were also investigated. Experiment results show that asphalt has more important effect on the adhesion performance comparing with aggregate. Basalt, which is regarded as hydrophobic aggregates with low silica content, has better adhesion performance to asphalt binder when compared with granite. The effects of aging on the adhesion fatigue performance are different for PG64-22 and rubber asphalt. Long-term aging is found to reduce the adhesion fatigue lives for rubber asphalt and aggregate system, while the effect of long-term aging for aggregate and PG64-22 binder system is positive. Generally the increased stress amplitude and test temperature could induce greater damage and lead to less fatigue lives for adhesion test system.

Fatigue methodology III; Proceedings of the AHS National Technical Specialists' Meeting on Advanced Rotorcraft Structures, Scottsdale, AZ, Oct. 3-5, 1989

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1989-01-01

Papers on rotorcraft and fatigue methodology are presented, covering topics such as reliability design for rotorcraft, a comparison between theory and fatigue test data on stress concentration factors, the retirement lives of rolling element bearings, hydrogen embrittlement risk analysis for high hardness steel parts, and rotating system load monitoring with minimum fixed system instrumentation. Additional topics include usage data collection to improve structural integrity of operational helicopters, usage monitory of military helicopters, improvements to the fatigue substantiation of the H-60 composite tail rotor blade, helicopter surviellance programs, and potential application of automotive fatigue technology in rotorcraft design. Also, consideration ismore » given to fatigue evaluation of C/MH-53 E main rotor damper threaded joints, SH-2F airframe fatigue test program, a ply termination concept for improving fracture and fatigue strength of composite laminates, the analysis and testing of composite panels subject to muzzle blast effects, the certification plan for an all-composite main rotor flexbeam, and the effects of stacking sequence on the flexural strength of composite beams.« less

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

NASA Astrophysics Data System (ADS)

Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

2014-12-01

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 108 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong; Lee, Sung Min; Wang, James L.

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10^8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and themore » fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Assessment of physical fatigability and fatigue perception in myasthenia gravis.

PubMed

Jordan, Berit; Mehl, Theresa; Schweden, Tabea L K; Menge, Uwe; Zierz, Stephan

2017-05-01

Fatigue includes both performance fatigability and fatigue perception. In 32 stable patients with generalized myasthenia gravis (MG) and 17 controls, time-dependent physical performance was assessed by the arm movement test (AMT) and 6-minute walk test (6MWT). MG patients presented with low quantitative MG scores (mean 0.5, SD 0.5) and without pathologic decrement. Fatigability was based on calculation of linear trend (LT) reflecting dynamic performance within subsequent constant time intervals. Perception of physical fatigue was analyzed using fatigue questionnaires. MG patients showed a negative LT in both AMT and 6MWT, significantly differing from stable performance in controls. LT inversely correlated with elevation of acetylcholine receptor antibodies (r = -0.59, P < 0.005) but not with quantitative MG score and fatigue perception. LT allows quantification of fatigability as an objective measurement of decline in individual performance, even in patients without obvious neuromuscular deficits in routine testing. The missing correlation of experienced fatigue supports the multidimensional fatigue model. Muscle Nerve 55: 657-663, 2017. © 2016 Wiley Periodicals, Inc.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE PAGES

Wang, Hong; Lee, Sung Min; Wang, James L.; ...

2014-12-19

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10^8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and themore » fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Fatigue of notched fiber composite laminates. Part 2: Analytical and experimental evaluation

NASA Technical Reports Server (NTRS)

Kulkarni, S. V.; Mclaughlin, P. V., Jr.; Pipes, R. B.

1976-01-01

The analytical/experimental correlation study was performed to develop an understanding of the behavior of notched Boron/epoxy laminates subjected to tension/tension fatigue loading. It is postulated that the fatigue induced property changes (stiffness as well as strength) of the laminate can be obtained from the lamina fatigue properties. To that end, the Boron/epoxy lamina static and fatigue data (lifetime, residual stiffness and strength) were obtained initially. The longitudinal and transverse tension data were determined from the (0) and (90) laminate tests while the in-plane shear data were obtained from the (+ or - 45) sub s laminates. The static tests obtained the notched strength and mode of failure while the fatigue tests determined lifetime, damage propagation and residual strength. The failure in static tension occurred in a transverse crack propagation mode.

Fatigue Behavior of AM60B Subjected to Variable Amplitude Loading

NASA Astrophysics Data System (ADS)

Kang, H.; Kari, K.; Khosrovaneh, A. K.; Nayaki, R.; Su, X.; Zhang, L.; Lee, Y.-L.

Magnesium alloys are considered as an alternative material to reduce vehicle weight due to their weight which are 33% lighter than aluminum alloys. There has been a significant expansion in the applications of magnesium alloys in automotives components in an effort to improve fuel efficiency through vehicle mass reduction. In this project, a simple front shock tower of passenger vehicle is constructed with various magnesium alloys. To predict the fatigue behavior of the structure, fatigue properties of the magnesium alloy (AM60B) were determined from strain controlled fatigue tests. Notched specimens were also tested with three different variable amplitude loading profiles obtained from the shock tower of the similar size of vehicle. The test results were compared with various fatigue prediction results. The effect of mean stress and fatigue prediction method were discussed.

Hydrogen accelerated fatigue crack growth of friction stir welded X52 steel pipe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ronevich, Joseph Allen; Somerday, Brian P.; Feng, Zhili

Friction stir welded steel pipelines were tested in high pressure hydrogen gas to examine the effects of hydrogen accelerated fatigue crack growth. Fatigue crack growth rate (da/dN) vs. stress-intensity factor range (ΔK) relationships were measured for an X52 friction stir welded pipe tested in 21 MPa hydrogen gas at a frequency of 1 Hz and R = 0.5. Tests were performed on three regions: base metal (BM), center of friction stir weld (FSW), and 15 mm off-center of the weld. For all three material regions, tests in hydrogen exhibited accelerated fatigue crack growth rates that exceeded an order of magnitudemore » compared to companion tests in air. Among tests in hydrogen, fatigue crack growth rates were modestly higher in the FSW than the BM and 15 mm off-center tests. Select regions of the fracture surfaces associated with specified ΔK levels were examined which revealed intergranular fracture in the BM and 15 mm off-center specimens but an absence of intergranular features in the FSW specimens. In conclusion, the X52 friction stir weld and base metal tested in hydrogen exhibited fatigue crack growth rate relationships that are comparable to those for conventional arc welded steel pipeline of similar strength found in the literature.« less

Hydrogen accelerated fatigue crack growth of friction stir welded X52 steel pipe

DOE PAGES

Ronevich, Joseph Allen; Somerday, Brian P.; Feng, Zhili

2016-11-17

Friction stir welded steel pipelines were tested in high pressure hydrogen gas to examine the effects of hydrogen accelerated fatigue crack growth. Fatigue crack growth rate (da/dN) vs. stress-intensity factor range (ΔK) relationships were measured for an X52 friction stir welded pipe tested in 21 MPa hydrogen gas at a frequency of 1 Hz and R = 0.5. Tests were performed on three regions: base metal (BM), center of friction stir weld (FSW), and 15 mm off-center of the weld. For all three material regions, tests in hydrogen exhibited accelerated fatigue crack growth rates that exceeded an order of magnitudemore » compared to companion tests in air. Among tests in hydrogen, fatigue crack growth rates were modestly higher in the FSW than the BM and 15 mm off-center tests. Select regions of the fracture surfaces associated with specified ΔK levels were examined which revealed intergranular fracture in the BM and 15 mm off-center specimens but an absence of intergranular features in the FSW specimens. In conclusion, the X52 friction stir weld and base metal tested in hydrogen exhibited fatigue crack growth rate relationships that are comparable to those for conventional arc welded steel pipeline of similar strength found in the literature.« less

Fatigue Crack Growth Behavior and Microstructural Mechanisms in Ti-6Al-4V Manufactured by Laser Engineered Net Shaping

DTIC Science & Technology

2015-12-01

hardening heat treatment were the controlling factors of the fatigue resistance, while testing directions have the least impact. Leuders et al. [16...radius. The microstructurally-small fatigue crack growth test was run under load control at constant stress ratio R=0.1 and a cyclic frequency of 20 Hz...not been thoroughly investigated. In this study, long fatigue crack growth tests were conducted at two stress ratios (R=0.1 and 0.8), using Ti-6Al

Several submaximal exercise tests are reliable, valid and acceptable in people with chronic pain, fibromyalgia or chronic fatigue: a systematic review.

PubMed

Ratter, Julia; Radlinger, Lorenz; Lucas, Cees

2014-09-01

Are submaximal and maximal exercise tests reliable, valid and acceptable in people with chronic pain, fibromyalgia and fatigue disorders? Systematic review of studies of the psychometric properties of exercise tests. People older than 18 years with chronic pain, fibromyalgia and chronic fatigue disorders. Studies of the measurement properties of tests of physical capacity in people with chronic pain, fibromyalgia or chronic fatigue disorders were included. Studies were required to report: reliability coefficients (intraclass correlation coefficient, alpha reliability coefficient, limits of agreements and Bland-Altman plots); validity coefficients (intraclass correlation coefficient, Spearman's correlation, Kendal T coefficient, Pearson's correlation); or dropout rates. Fourteen studies were eligible: none had low risk of bias, 10 had unclear risk of bias and four had high risk of bias. The included studies evaluated: Åstrand test; modified Åstrand test; Lean body mass-based Åstrand test; submaximal bicycle ergometer test following another protocol other than Åstrand test; 2-km walk test; 5-minute, 6-minute and 10-minute walk tests; shuttle walk test; and modified symptom-limited Bruce treadmill test. None of the studies assessed maximal exercise tests. Where they had been tested, reliability and validity were generally high. Dropout rates were generally acceptable. The 2-km walk test was not recommended in fibromyalgia. Moderate evidence was found for reliability, validity and acceptability of submaximal exercise tests in patients with chronic pain, fibromyalgia or chronic fatigue. There is no evidence about maximal exercise tests in patients with chronic pain, fibromyalgia and chronic fatigue. Copyright © 2014. Published by Elsevier B.V.

An Axial-Torsional, Thermomechanical Fatigue Testing Technique

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Bonacuse, Peter J.

1995-01-01

A technique for conducting strain-controlled, thermomechanical, axial-torsional fatigue tests on thin-walled tubular specimens was developed. Three waveforms of loading, namely, the axial strain waveform, the engineering shear strain waveform, and the temperature waveform were required in these tests. The phasing relationships between the mechanical strain waveforms and the temperature and axial strain waveforms were used to define a set of four axial-torsional, thermomechanical fatigue (AT-TMF) tests. Real-time test control (3 channels) and data acquisition (a minimum of 7 channels) were performed with a software program written in C language and executed on a personal computer. The AT-TMF testing technique was used to investigate the axial-torsional thermomechanical fatigue behavior of a cobalt-base superalloy, Haynes 188. The maximum and minimum temperatures selected for the AT-TMF tests were 760 and 316 C, respectively. Details of the testing system, calibration of the dynamic temperature profile of the thin-walled tubular specimen, thermal strain compensation technique, and test control and data acquisition schemes, are reported. The isothermal, axial, torsional, and in- and out-of-phase axial-torsional fatigue behaviors of Haynes 188 at 316 and 760 C were characterized in previous investigations. The cyclic deformation and fatigue behaviors of Haynes 188 in AT-TMF tests are compared to the previously reported isothermal axial-torsional behavior of this superalloy at the maximum and minimum temperatures.

Relationship of fatigue to the tensile stiffness of asphaltic concrete : final report on phase 1, laboratory investigation.

DOT National Transportation Integrated Search

1972-01-01

The correlation between asphaltic concrete tensile stiffness and fatigue life was determined in the laboratory. Constant strain fatigue tests were utilized and indirect tensile tests were selected because of their simplicity and applicability. Four a...

PZT Active Frequency Based Wind Blade Fatigue to Failure Testing Results for Various Blade Designs

DTIC Science & Technology

2011-09-01

PZT Active Frequency Based Wind Blade Fatigue to Failure Testing Results for Various Blade Designs R. J. WERLINK...number. 1. REPORT DATE SEP 2011 2. REPORT TYPE N/A 3. DATES COVERED - 4. TITLE AND SUBTITLE PZT Active Frequency Based Wind Blade Fatigue ...18 Abstract: This paper summarizes NASA PZT Health Monitoring System results previously reported for 9 meter blade Fatigue loading to failure

Nanosecond pulsed laser micromachining for experimental fatigue life study of Ti-3Al-2.5V tubes

NASA Astrophysics Data System (ADS)

Lin, Yaomin; Gupta, Mool C.; Taylor, Robert E.; Lei, Charles; Stone, William; Spidel, Tom; Yu, Michael; Williams, Reanne

2009-01-01

Defects on external surface of in-service hydraulic tubes can reduce total life cycles for operation. Evaluation of fatigue life of the tubes with damage is thus critical for safety reasons. A methodology of generating defects in the Ti-3Al-2.5V tube—a widely used pipeline in hydraulic systems of aircrafts—using nanosecond pulsed laser for experimental fatigue life study is described in this paper. Straight tubes of five different sizes were laser micromachined to generate notches of given length and depths on the outside surface. Approaches were developed to precisely control the notch dimensions. The laser-notched tubes were tested with cyclic internal impulse pressure and fatigue life was measured. The laser notches and fatigue cracks were characterized after the test. It is concluded that laser micromachining generated consistent notches, and the influence of notch depth on fatigue life of the tube is significant. Based on the experimental test results, the relationship between the fatigue life of the Ti-3Al-2.5V tube and the notch depth was revealed. The research demonstrated that laser micromachining is applicable for experimental fatigue life study of titanium tubes. The presented test data are useful for estimating the damage limits of the titanium tubes in service environment and for further theoretical studies.

Effect of Environment on Fatigue Behavior of a Nicalon(TM)/Si-N-C Ceramic Matrix Composite

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Ojard, Greg C.; Verrilli, Michael J.; Kiraly, Louis J. (Technical Monitor)

2002-01-01

The effect of environmental exposure on the fatigue life of Nicalon(TM) /Si-N-C composite was investigated in this study. Test specimens with arrays of 1.8 mm diameter holes and two different open areas, 25 and 35%, were machined. Three environmental conditions were studied: 1) continuous fatigue cycling in air, 2) fatigue cycling in air alternating with humidity exposure, and 3) fatigue cycling in air alternating with exposure to a salt-fog environment. All fatigue testing on specimens with holes was performed with a load ratio, R = 0.05, and at a temperature of 910 C. In general, fatigue lives were shortest for specimens subjected to salt-fog exposure and longest for specimens subjected to continuous fatigue cycling in air. The fatigue data generated on the specimens with holes were compared with fatigue data generated in air on specimens with no holes. Fatigue strength reduction factors for different environmental conditions and open areas investigated in the study were calculated for the Nicalon(TM) /Si-N-C composite.

Estimating the Contact Endurance of the AISI 321 Stainless Steel Under Contact Gigacycle Fatigue Tests

NASA Astrophysics Data System (ADS)

Savrai, R. A.; Makarov, A. V.; Osintseva, A. L.; Malygina, I. Yu.

2018-02-01

Mechanical testing of the AISI 321 corrosion resistant austenitic steel for contact gigacycle fatigue has been conducted with the application of a new method of contact fatigue testing with ultrasonic frequency of loading according to a pulsing impact "plane-to-plane" contact scheme. It has been found that the contact endurance (the ability to resist the fatigue spalling) of the AISI 321 steel under contact gigacycle fatigue loading is determined by its plasticity margin and the possibility of additional hardening under contact loading. It is demonstrated that the appearance of localized deep and long areas of spalling on a material surface can serve as a qualitative characteristic for the loss of the fatigue strength of the AISI 321 steel under impact contact fatigue loading. The value of surface microhardness measured within contact spots and the maximum depth of contact damages in the peripheral zone of contact spots can serve as quantitative criteria for that purpose.

The isothermal fatigue behavior of a unidirectional SiC/Ti composite and the Ti alloy matrix

NASA Technical Reports Server (NTRS)

Gayda, John, Jr.; Gabb, Timothy P.; Freed, Alan D.

1989-01-01

The high temperature fatigue behavior of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) matrix reinforced by 33 vol percent of continuous unidirectional SiC fibers was experimentally and analytically evaluated. Isothermal MMC fatigue tests with constant amplitude loading parallel to the fiber direction were performed at 300 and 550 C. Comparative fatigue tests of the Ti-15-3 matrix alloy were also conducted. Composite fatigue behavior and the in-situ stress state of the fiber and matrix were analyzed with a micromechanical model, the Concentric Cylinder Model (CCM). The cyclic stress-strain response of the composite was stable at 300 C. However, an increase in cyclic mean strain foreshortened MMC fatigue life at high strain ranges at 550 C. Fatigue tests of the matrix alloy and CCM analyses indicated this response was associated with stress relaxation of the matrix in the composite.

Bending fatigue tests on SiC-Al tapes under alternating stress at room temperature

NASA Technical Reports Server (NTRS)

Herzog, J. A.

1981-01-01

The development of a testing method for fatigue tests on SiC-Al tapes containing a small amount of SiC filaments under alternating stress is reported. The fatigue strength curves resulting for this composite are discussed. They permit an estimate of its behavior under continuous stress and in combination with various other matrices, especially metal matrices.

Experiments of thermomechanical fatigue of SMAs

NASA Astrophysics Data System (ADS)

Lagoudas, Dimitris C.; Miller, David A.

1999-07-01

As SMA wires are gaining in popularity for use as actuators, one constitutive parameter that remain unknown is the thermomechanical fatigue life. Even though the effect of thermal cycles on the transformation characteristics of SMAs has been studied, these teste have not been extended to high number of cycles. In this study, a novel test frame developed to study the thermomechanical fatigue life of SMAs is described. Additionally, a testing protocol is discussed necessary to fully establish the fatigue characteristics of SMAs under various conditions. Initial results of the initial test show a substantial increase in the number of cycles to failure as the applied stress level reduces to approximately 100 MPa.

The effect of weld porosity on the cryogenic fatigue strength of ELI grade Ti-5Al-2.5Sn

NASA Technical Reports Server (NTRS)

Rogers, P. R.; Lambdin, R. C.; Fox, D. E.

1992-01-01

The effect of weld porosity on the fatigue strength of ELI grade Ti-5Al-2.5Sn at cryogenic temperature was determined. A series of high cycle fatigue (HCF) and tensile tests were performed at -320 F on specimens made from welded sheets of the material. All specimens were tested with weld beads intact and some amount of weld offset. Specimens containing porosity and control specimens containing no porosity were tested. Results indicate that for the weld configuration tested, the fatigue life of the material is not affected by the presence of spherical embedded pores.

Psychosocial correlates of fatigue in multiple sclerosis.

PubMed

Schwartz, C E; Coulthard-Morris, L; Zeng, Q

1996-02-01

To explore: (1) the interrelation among the neuropsychological, psychological, and psychosocial factors and fatigue as measured by the Multidimensional Assessment of Fatigue scale, and (2) the impact of fatigue on role performance. Clinical interview with neuropsychological testing and cross-sectional study by mail. Multiple sclerosis (MS) clinic registry of a large Boston teaching hospital. 139 MS patients representing a broad range of disability. The Multidimensional Assessment of Fatigue (MAF) scale, the Extended Disability Status Scale, the Sickness Impact Profile, Rao cognitive battery, the Trailmaking Test, depression, anxiety, and social activity limitations subscales from the Arthritis Impact Measurement Scales, and the Ryff Happiness Scale. Stepwise multiple regression analyses revealed that having a low sense of environmental mastery was the best psychosocial predictor of both global fatigue and fatigue-related distress, after adjusting for sociodemographic and medical factors. Further, people who reported being more depressed tended to report more severe fatigue. Neuropsychological performance was not associated with fatigue. Fatigue was found to limit social, work, and overall role performance, but not physical role performance. People who feel that they can choose or create environments suitable to their psychic or physical conditions report less global fatigue and less fatigue-related distress, and fatigue can have an important impact on role performance. The implications of these findings for designing fatigue management interventions are discussed.

Effect of stress ratio on the fatigue behaviour of glass/epoxy composite

NASA Astrophysics Data System (ADS)

Syayuthi, A. R. A.; Majid, M. S. Abdul; Ridzuan, M. J. M.; Basaruddin, K. S.; Peng, T. L.

2017-10-01

The effect of stress ratio on the fatigue behaviour of the GFRE composite has been investigated. The glass fibre reinforced epoxy (GFRE) composite plates were fabricated using vacuum infusion method. Static tensile was performed in accordance with the ASTM D5766 standard, and the cyclic test was conducted according to ASTM D3479 with three different stress ratio, R = 0, 0.5, -1. Static tensile tests were carried out to determine the ultimate strength of this composite. Subsequently, fatigue tests loads ranging from 30% to 90% of the ultimate load were applied to each specimen. The S-N curve of different stress ratio loading of fibreglass/epoxy composites was then established. The results show that the number of cycles to failure increases as the loading is decreased. The specimens for fatigue tests loads 30% at R = 0 and -1 recorded the highest number of cycles at 2 million cycles. The results obtained from this test indicated a significant life reduction for R = -1 compared with the tension-tension loading, with the life reduction for R = -1 being greatest. The fatigue behaviour of the GFRE composite materials is not only influenced by the percentage of fatigue tests load but with different of stress ratio.

Surface fatigue life and failure characteristics of EX-53, CBS 1000M, and AISI 9310 gear materials

NASA Technical Reports Server (NTRS)

Townsend, D. P.

1985-01-01

Spur gear endurance tests and rolling-element surface fatigue tests are conducted to investigate EX-53 and CBS 1000M steels for use as advanced application gear materials, to determine their endurance characteristics, and to compare the results with the standard AISI 9310 gear material. The gear pitch diameter is 8.89 cm (3.50 in). Gear test conditions are an oil inlet temperature of 320 K (116 F), an oil outlet temperature of 350 K (170 F), a maximum Hertz stress of 1.71 GPa (248 ksi), and a speed of 10,000 rpm. Bench-type rolling-element fatigue tests are conducted at ambient temperature with a bar specimen speed of 12,500 rpm and a maximum Hertz stress of 4.83 GPa (700 ksi). The EX-53 test gears have a surface fatigue life of twice that of the AISI 9310 spur gears. The CBS 1000M test gears have a surface fatigue life of more than twice that of the AISI 9310 spur gears. However, the CBS 1000M gears experience a 30-percent tooth fracture failure which limits its use as a gear material. The rolling-contact fatigue lines of RC bar specimens of EX-53 and ASISI 9310 are approximately equal. However, the CBS 1000M RC specimens have a surface fatigue life of about 50 percent that of the AISI 9310.

Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a “sandwich structure” as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50–55% of ultimate tensile strength). The dynamic modulus (E⁎) was found to stay almost constant at 47 GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials.

Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a "sandwich structure" as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50-55% of ultimate tensile strength). The dynamic modulus (E(⁎)) was found to stay almost constant at 47GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials. Copyright © 2014 Elsevier Ltd. All rights reserved.

Pitting and Bending Fatigue Evaluations of a New Case-Carburized Gear Steel

NASA Technical Reports Server (NTRS)

Krantz, Timothy; Tufts, Brian

2007-01-01

The power density of a gearbox is an important consideration for many applications and is especially important for gearboxes used on aircraft. One approach to improving power density of gearing is to improve the steel properties by design of the alloy. The alloy tested in this work was designed to be case-carburized with surface hardness of Rockwell C66 after hardening. Test gear performance was evaluated using surface fatigue tests and single-tooth bending fatigue tests. The performance of gears made from the new alloy was compared to the performance of gears made from two alloys currently used for aviation gearing. The new alloy exhibited significantly better performance in surface fatigue testing, demonstrating the value of the improved properties in the case layer. However, the alloy exhibited lesser performance in single-tooth bending fatigue testing. The fracture toughness of the tested gears was insufficient for use in aircraft applications as judged by the behavior exhibited during the single tooth bending tests. This study quantified the performance of the new alloy and has provided guidance for the design and development of next generation gear steels.

Cognitive fatigue in patients with myasthenia gravis.

PubMed

Jordan, Berit; Schweden, Tabea L K; Mehl, Theresa; Menge, Uwe; Zierz, Stephan

2017-09-01

Cognitive fatigue has frequently been reported in myasthenia gravis (MG). However, objective assessment of cognitive fatigability has never been evaluated. Thirty-three MG patients with stable generalized disease and 17 healthy controls underwent a test battery including repeated testing of attention and concentration (d2-R) and Paced Auditory Serial Addition Test. Fatigability was based on calculation of linear trend (LT) reflecting dynamic performance within subsequent constant time intervals. Additionally, fatigue questionnaires were used. MG patients showed a negative LT in second d2-R testing, indicating cognitive fatigability. This finding significantly differed from stable cognitive performance in controls (P < 0.05). Results of Paced Auditory Serial Addition Test testing did not differ between groups. Self-assessed fatigue was significantly higher in MG patients compared with controls (P < 0.001), but did not correlate with LT. LT quantifies cognitive fatigability as an objective measurement of performance decline in MG patients. Self-assessed cognitive fatigue is not correlated with objective findings. Muscle Nerve 56: 449-457, 2017. © 2016 Wiley Periodicals, Inc.

The effect of hold-times on the fatigue behavior of type AISI 316L stainless steel under deuteron irradiation

NASA Astrophysics Data System (ADS)

Scholz, R.; Mueller, R.

1998-10-01

Strain controlled fatigue tests have been performed in torsion at 400°C on type 316L stainless steel samples in both 20% cold worked and annealed conditions during an irradiation with 19 MeV deuterons. A hold-time was imposed in the loading cycle. For the cold worked (cw) material, at shear strain ranges of 1.13% and 1.3%, irradiation creep induced stress relaxation led to the built up of a mean stress. The fatigue life was significantly reduced in comparison to thermal control tests. For the annealed (ann) material, tested under similar experimental conditions, irradiation creep effects were negligibly small compared to cyclic and irradiation hardening. The fatigue life was only slightly reduced. Continuous cycling tests conducted under irradiation conditions lay in the scatter band of the thermal control tests. The difference in fatigue life between continuous cycling and hold-time tests is attributed mainly to the observed difference in irradiation hardening.

Microstructural and Material Quality Effects on Rolling Contact Fatigue of Highly Elastic Intermetallic Ball Bearings

NASA Technical Reports Server (NTRS)

DellaCorte, Christopher; Howard, S. Adam; Thomas, Fransua; Stanford, Malcolm K.

2016-01-01

Rolling element bearings made from highly-elastic intermetallic materials (HIM)s, such as 60NiTi, are under development for applications that require superior corrosion and shock resistance. Compared to steel, intermetallics have been shown to have much lower rolling contact fatigue (RCF) stress capability in simplified 3-ball on rod (ASTM STP 771) fatigue tests. In the 3-ball tests, poor material quality and microstructural flaws negatively affect fatigue life but such relationships have not been established for full-scale 60NiTi bearings. In this paper, 3-ball-on-rod fatigue behavior of two quality grades of 60NiTi are compared to the fatigue life of full-scale 50mm bore ball bearings made from the same materials. 60NiTi RCF rods with material or microstructural flaws suffered from infant mortality failures at all tested stress levels while high quality 60NiTi rods exhibited no failures at lower stress levels. Similarly, tests of full-scale bearings made from flawed materials exhibited early surface fatigue and through crack type failures while bearings made from high quality material did not fail even in long-term tests. Though the full-scale bearing test data is yet preliminary, the results suggest that the simplified RCF test is a good qualitative predictor of bearing performance. These results provide guidance for materials development and to establish minimum quality levels required for successful bearing operation and life.

Microstructural and Material Quality Effects on Rolling Contact Fatigue of Highly Elastic Intermetallic NiTi Ball Bearings

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Howard, S. Adam; Thomas, Fransua; Stanford, Malcolm K.

2017-01-01

Rolling element bearings made from highly-elastic intermetallic materials (HIM)s, such as 60NiTi, are under development for applications that require superior corrosion and shock resistance. Compared to steel, intermetallics have been shown to have much lower rolling contact fatigue (RCF) stress capability in simplified 3-ball on rod (ASTM STP 771) fatigue tests. In the 3-ball tests, poor material quality and microstructural flaws negatively affect fatigue life but such relationships have not been established for full-scale 60NiTi bearings. In this paper, 3-ball-on-rod fatigue behavior of two quality grades of 60NiTi are compared to the fatigue life of full-scale 50mm bore ball bearings made from the same materials. 60NiTi RCF rods with material or microstructural flaws suffered from infant mortality failures at all tested stress levels while high quality 60NiTi rods exhibited no failures at lower stress levels. Similarly, tests of full-scale bearings made from flawed materials exhibited early surface fatigue and through crack type failures while bearings made from high quality material did not fail even in long-term tests. Though the full-scale bearing test data is yet preliminary, the results suggest that the simplified RCF test is a good qualitative predictor of bearing performance. These results provide guidance for materials development and to establish minimum quality levels required for successful bearing operation and life.

Evaluation of tilting disc valves after fatigue life testing: preliminary results within a comparison program.

PubMed

Barbaro, V; Boccanera, G; Daniele, C; Grigioni, M; Palombo, A

1995-09-01

A fatigue life test, by accelerating the beat rate, simulates several years of virtual life of a prosthetic heart valve in a short period of time. The correlation between the in vivo life of a valve and in vitro testing expectations is as yet not well established, but reproducible test conditions yield precious information about wear and failure. The paper reports a qualitative analysis of mechanical valve wear as part of a comparison program designed to investigate the significance of fatigue testing with the ultimate aim of defining standard guidelines for these type of tests. Two tilting disc valves (29 mm) were subjected to 16 years of fatigue life simulated by means of a Rowan Ash fatigue tester (accelerated rate of 1,200 bpm). Fatigue-induced effects on valve disc and ring surfaces were observed under a monitor microscope to identify wear sites and patterns. A high speed cinematographic system was used to investigate the mechanisms responsible for the wear (wear modes). Valve closure was inspected at a 6,000 frame/s rate. Because of disc rotation during the tilting movement, the points of contact between disc and ring are distributed all around the disc edge but focally on the ring. On both sides of the disc, the surfaces present ring-like concentric grooves. After 16 years of fatigue life the valves showed neither severe wear nor alteration of their fluidodynamic behavior in the pulsatile flow test.

Fatigue crack monitoring with coupled piezoelectric film acoustic emission sensors

NASA Astrophysics Data System (ADS)

Zhou, Changjiang

Fatigue-induced cracking is a commonly seen problem in civil infrastructures reaching their original design life. A number of high-profile accidents have been reported in the past that involved fatigue damage in structures. Such incidences often happen without prior warnings due to lack of proper crack monitoring technique. In order to detect and monitor the fatigue crack, acoustic emission (AE) technique, has been receiving growing interests recently. AE can provide continuous and real-time monitoring data on damage progression in structures. Piezoelectric film AE sensor measures stress-wave induced strain in ultrasonic frequency range and its feasibility for AE signal monitoring has been demonstrated recently. However, extensive work in AE monitoring system development based on piezoelectric film AE sensor and sensor characterization on full-scale structures with fatigue cracks, have not been done. A lack of theoretical formulations for understanding the AE signals also hinders the use of piezoelectric film AE sensors. Additionally, crack detection and source localization with AE signals is a very important area yet to be explored for this new type of AE sensor. This dissertation presents the results of both analytical and experimental study on the signal characteristics of surface stress-wave induced AE strain signals measured by piezoelectric film AE sensors in near-field and an AE source localization method based on sensor couple theory. Based on moment tensor theory, generalized expression for AE strain signal is formulated. A special case involving the response of piezoelectric film AE sensor to surface load is also studied, which could potentially be used for sensor calibration of this type of sensor. A new concept of sensor couple theory based AE source localization technique is proposed and validated with both simulated and experimental data from fatigue test and field monitoring. Two series of fatigue tests were conducted to perform fatigue crack monitoring on large-scale steel test specimens using piezoelectric film AE sensors. Continuous monitoring of fatigue crack growth in steel structures is demonstrated in these fatigue test specimens. The use of piezoelectric film AE sensor for field monitoring of existing fatigue crack is also demonstrated in a real steel I-girder bridge located in Maryland. The sensor couple theory based AE source localization is validated using a limited number of piezoelectric film AE sensor data from both fatigue test specimens and field monitoring bridge. Through both laboratory fatigue test and field monitoring of steel structures with active fatigue cracks, the signal characteristics of piezoelectric film AE sensor have been studied in real-world environment.

Effects of environment and frequency on the fatigue behavior of the spallation neutron source (SNS) target container material - 316 LN stainless steel

NASA Astrophysics Data System (ADS)

Tian, Hongbo

As the candidate target container material of the new Spallation Neutron Source (SNS) being designed and constructed at the Oak Ridge National Laboratory (ORNL), Type 316 low-carbon nitrogen-added (LN) stainless steel (SS) will operate in an aggressive environment, subjected to intense fluxes of high-energy protons and neutrons while exposed to liquid mercury. The current project is oriented toward materials studies regarding the effects of test environment and frequency on the fatigue behavior of 316 LN SS. In order to study the structural applications of this material and improve the fundamental understanding of the fatigue damage mechanisms, fatigue tests were performed in air and mercury environments at various frequencies and R ratios (R = sigma min/sigmamax, sigmamin and sigmamax are the applied minimum and maximum stresses, respectively). Fatigue data were developed for the structural design and engineering applications of this material. Specifically, high-cycle fatigue tests, fatigue crack-propagation tests, and ultrahigh cycle fatigue tests up to 10 9 cycles were conducted in air and mercury with test frequencies from 10 Hz to 700 Hz. Microstructure characterizations were performed using optical microscopy (OM), scanning-electron microscopy (SEM), and transmission-electron microscopy (TEM). It was found that mercury doesn't seem to have a large impact on the crack-initiation behavior of 316 LN SS. However, the crack-propagation mechanisms in air and mercury are different in some test conditions. Transgranular cracks seem to be the main mechanism in air, and intergranular in mercury. A significant specimen self-heating effect was found during high-cycle faituge. Theoretical calculation was performed to predict temperature responses of the material subjected to cyclic deformation. The predicted cyclic temperature evolution seems to be in good agreement with the experimental results.

The effects of Nitinol phases on corrosion and fatigue behavior

NASA Astrophysics Data System (ADS)

Denton, Melissa

The purpose of these studies was to provide a detailed understanding of Nitinol phases and their effects on corrosion and fatigue life. The two primary phases, austenite and martensite, were carefully evaluated with respect to material geometry, corrosion behavior, wear, and fatigue life. Material characterization was performed using several techniques that include metallography, scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), x-ray photoelectron spectrum (XPS), and Auger electron spectroscopy (AES). Uniaxial tensile tests were conducted to determine the mechanical properties such as elongation, ultimate tensile strength, modulus, transformation strain, and plateau stress. In addition, accelerated wear testing and four point bend fatigue testing were completed to study the fatigue life and durability of the material. The corrosion of Nitinol was found to be dependent on various surface conditions. Electrochemical corrosion behavior of each phase was investigated using cyclic potentiodyamic polarization testing. The corrosion response of electropolished Nitinol was found to be acceptable, even after durability testing. Stress-induced martensite had a lower breakdown potential due to a rougher surface morphology, while thermally induced martensite and austenite performed similarly well. The surface conditioning also had a significant effect on Nitinol mechanical properties. Electropolishing provided a smooth mirror finish that reduced localized texture and enhanced the ductility of the material. Quasi-static mechanical properties can be good indicators of fatigue life, but further fatigue testing revealed that phase transformations had an important role as well. The governing mechanisms for the fatigue life of Nitinol were determined to be both martesitic phase transformations and surface defects. A new ultimate dislocation strain model was proposed based on specific accelerated step-strain testing.

Near-threshold fatigue behavior of copper alloys in air and aqueous environments: A high cyclic frequency study

NASA Astrophysics Data System (ADS)

Ahmed, Tawfik M.

The near-threshold fatigue crack propagation behavior of alpha-phase copper alloys in desiccated air and several aqueous environments has been investigated. Three commercial alloys of nominal composition Cu-30Ni (Cu-Ni), Cu-30Zn (Cu-Zn) and 90Cu-7Al-3Fe (Cu-Al) were tested. Fatigue tests were conducted using standard prefatigued single edged notched (SEN) specimens loaded in tension at a high frequency of ˜100 Hz. Different R-ratios were employed, mostly at R-ratios of 0.5. Low loading levels were used that corresponded to the threshold and near-threshold regions where Delta Kth ≤ DeltaK ≤ 11 MPa√m. Fatigue tests in the aqueous solutions showed that the effect of different corrosive environments during high frequency testing (˜100 Hz) was not as pronounced as was expected when compared relative to air. Further testing revealed that environmental effects were present and fatigue crack growth rates were influenced by the fluid-induced closure effects which are generally reported in the fatigue literature to be operative only in viscous liquids, not in aqueous solutions. It was concluded that high frequency testing in aqueous environments consistently decreased crack growth rates in a manner similar to crack retardation effects in viscous fluids. Several theoretical models reported in the literature have underestimated, if not failed, to adequately predict the fluid induced closure in aqueous solutions. Results from the desiccated air tests confirmed that, under closure-free conditions (high R-ratios), both threshold values and fatigue crack growth rate of stage II can be related to Young's modulus, in agreement with results from the literature. The role of different mechanical and environmental variables on fatigue behavior becomes most visible in the low R -ratio regime, and contribute to various closure processes.

All Fatigue is Not Created Equal: The Association of Fatigue and Its Subtypes on Pain Interference in Orofacial Pain.

PubMed

Boggero, Ian A; Rojas-Ramirez, Marcia V; Carlson, Charles R

2017-03-01

Fatigue is known to be a pathway through which depression, psychological distress, pain intensity, and sleep disturbance influence pain interference, but the independent effects of fatigue on pain interference after controlling for these variables remains unknown. In addition, no study to date has tested whether fatigue subtypes of general fatigue, mental fatigue, emotional fatigue, physical fatigue, or vigor differentially predict pain interference. The current study tested these associations using archival medical data of 2133 chronic orofacial pain patients, who completed a battery of psychological questionnaires at the time of their first appointment at an orofacial pain clinic. Hierarchical linear regression analysis revealed that after controlling for depression, psychological distress, sleep disturbance, pain intensity, and demographic variables, fatigue predicted higher pain interference (B=0.70, SE=0.17, P<0.001, η=0.01). Physical fatigue (B=1.70, SE=0.48, P<0.001, η=0.01) and vigor (B=-3.24, SE=0.47, P<0.001, η=0.03) were independently associated with pain interference after controlling for the aforementioned variables. The findings suggest that fatigue is an important independent predictor of pain interference and not merely a mediator. These findings also suggest that not all fatigue is created equal. Interventions aimed at reducing pain interference should target specific fatigue symptoms of physical fatigue and vigor. Future research investigating the independent associations of fatigue subtypes on pain outcomes may help clarify the nature of the interrelationships between pain and fatigue.

The reliability and validity of fatigue measures during short-duration maximal-intensity intermittent cycling.

PubMed

Glaister, Mark; Stone, Michael H; Stewart, Andrew M; Hughes, Michael; Moir, Gavin L

2004-08-01

The purpose of the present study was to assess the reliability and validity of fatigue measures, as derived from 4 separate formulae, during tests of repeat sprint ability. On separate days over a 3-week period, 2 groups of 7 recreationally active men completed 6 trials of 1 of 2 maximal (20 x 5 seconds) intermittent cycling tests with contrasting recovery periods (10 or 30 seconds). All trials were conducted on a friction-braked cycle ergometer, and fatigue scores were derived from measures of mean power output for each sprint. Apart from formula 1, which calculated fatigue from the percentage difference in mean power output between the first and last sprint, all remaining formulae produced fatigue scores that showed a reasonably good level of test-retest reliability in both intermittent test protocols (intraclass correlation range: 0.78-0.86; 95% likely range of true values: 0.54-0.97). Although between-protocol differences in the magnitude of the fatigue scores suggested good construct validity, within-protocol differences highlighted limitations with each formula. Overall, the results support the use of the percentage decrement score as the most valid and reliable measure of fatigue during brief maximal intermittent work.

Sensitivity, reliability and the effects of diurnal variation on a test battery of field usable upper limb fatigue measures.

PubMed

Yung, Marcus; Wells, Richard P

2017-07-01

Fatigue has been linked to deficits in production quality and productivity and, if of long duration, work-related musculoskeletal disorders. It may thus be a useful risk indicator and design and evaluation tool. However, there is limited information on the test-retest reliability, the sensitivity and the effects of diurnal fluctuation on field usable fatigue measures. This study reports on an evaluation of 11 measurement tools and their 14 parameters. Eight measures were found to have test-retest ICC values greater than 0.8. Four measures were particularly responsive during an intermittent fatiguing condition. However, two responsive measures demonstrated rhythmic behaviour, with significant time effects from 08:00 to mid-afternoon and early evening. Action tremor, muscle mechanomyography and perceived fatigue were found to be most reliable and most responsive; but additional analytical considerations might be required when interpreting daylong responses of MMG and action tremor. Practitioner Summary: This paper presents findings from test-retest and daylong reliability and responsiveness evaluations of 11 fatigue measures. This paper suggests that action tremor, muscle mechanomyography and perceived fatigue were most reliable and most responsive. However, mechanomyography and action tremor may be susceptible to diurnal changes.

Fatigue of restorative materials.

PubMed

Baran, G; Boberick, K; McCool, J

2001-01-01

Failure due to fatigue manifests itself in dental prostheses and restorations as wear, fractured margins, delaminated coatings, and bulk fracture. Mechanisms responsible for fatigue-induced failure depend on material ductility: Brittle materials are susceptible to catastrophic failure, while ductile materials utilize their plasticity to reduce stress concentrations at the crack tip. Because of the expense associated with the replacement of failed restorations, there is a strong desire on the part of basic scientists and clinicians to evaluate the resistance of materials to fatigue in laboratory tests. Test variables include fatigue-loading mode and test environment, such as soaking in water. The outcome variable is typically fracture strength, and these data typically fit the Weibull distribution. Analysis of fatigue data permits predictive inferences to be made concerning the survival of structures fabricated from restorative materials under specified loading conditions. Although many dental-restorative materials are routinely evaluated, only limited use has been made of fatigue data collected in vitro: Wear of materials and the survival of porcelain restorations has been modeled by both fracture mechanics and probabilistic approaches. A need still exists for a clinical failure database and for the development of valid test methods for the evaluation of composite materials.

Microstructural examination of fatigue crack tip in high strength steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuoka, C.; Yoshizawa, H.; Nakagawa, Y.G.

1993-10-01

Fatigue tests were performed to examine how microstructural conditioning influences crack initiation and propagation in SA508 class 3 low-carbon steel. A 3-mm-long crack was introduced in compact tension (CT) fatigue test specimens under four different loads in order to obtain crack tip plastic zones at different stress intensity factor ranges, [Delta]K = 18, 36, 54, and 72 MPa[radical]m. The microstructure of the plastic zones around the crack tip were examined by transmission electron microscopy (TEM) and selected area electron diffraction (SAD). Micro-orientation of the dislocation cells in the plastic zones of all of the CT samples increased to 4 degmore » from the level of an as-received sample. Four-point bending fatigue tests were performed for plate shape samples with a large cyclic strain range. The SAD value of the bending samples was also 4 deg in the damaged area where cracks already initiated at an early stage of the fatigue process. These test results indicate that the microstructural conditioning is a prerequisite for the fatigue crack initiation and propagation in SA508. These observations may lead to better understanding of how fatigue initiation processes transit to cracks.« less

Environmental Effects on Graphite-Epoxy Fatigue Properties

NASA Technical Reports Server (NTRS)

Sumsion, H. T.

1976-01-01

Effects of torsional and flexural fatigue on the long-time Integrity of advanced graphite-epoxy structural composites have been investigated. Torsional fatigue tests were run at stress ratios of R = 0 (zero to maximum, repeated) and R = -1 (zero mean stress) on unidirectional, angleply, and woven graphite fiber materials in air and water at room temperature and at 74 C. Flexural fatigue tests (four-point bending) with R = -1 were run in air and water at room temperature, and with R = 0 in air. Results show that, in torsional cycling, both water environment and higher test temperature contribute to significant degradation of torsional stiffness. The degradation of stiffness from torsional stress cycling was observed to be much greater with R = -1 than with simple R = 0 cycling. The effect of environment also is greater in the fully reversed cycling. Flexural fatigue results on +/- 30 deg material show a large fatigue effect, with fatigue limits of less than 50% and 30% of the static failure strength for specimens tested under stress ratios of R = 0 and R = -1, respectively. Compliance measurements indicate that the final failures are preceded by damage initiation and accumulation, which begins at about 1% of the specimen life.

Elevated temperature biaxial fatigue

NASA Technical Reports Server (NTRS)

Jordan, E. H.

1984-01-01

A three year experimental program for studying elevated temperature biaxial fatigue of a nickel based alloy Hastelloy-X has been completed. A new high temperature fatigue test facility with unique capabilities has been developed. Effort was directed toward understanding multiaxial fatigue and correlating the experimental data to the existing theories of fatigue failure. The difficult task of predicting fatigue lives for non-proportional loading was used as an ultimate test for various life prediction methods being considered. The primary means of reaching improved undertanding were through several critical non-proportional loading experiments. It was discovered that the cracking mode switched from primarily cracking on the maximum shear planes at room temperature to cracking on the maximum normal strain planes at 649 C.

Characterization of wear debris generated in accelerated rolling-element fatigue tests

NASA Technical Reports Server (NTRS)

Jones, W. R., Jr.; Parker, R. J.

1978-01-01

A ferrographic analysis was used to determine the types and quantities of wear debris generated during accelerated rolling contact fatigue tests. The five-ball rolling contact fatigue tester was used. Ball specimens were made of a corrosion resistant, high-temperature bearing steel. The lubricant was a superrefined naphthenic mineral oil. Conditions included a maximum Hertz stress of 5.52 10 to the 9th power Pa and a shaft speed of 10,000 rpm. Four types of wear debris were observed: (1) normal rubbing wear particles, (2) fatigue microspall particles, (3) spheres, and (4) friction polymer deposits. The characterization of wear debris as a function of time was of limited use in predicting fatigue failures in these accelerated tests.

Fatigue of immature baboon cortical bone.

PubMed

Keller, T S; Lovin, J D; Spengler, D M; Carter, D R

1985-01-01

Strain-controlled uniaxial fatigue and monotonic tensile tests were conducted on turned femoral cortical bone specimens obtained from baboons at various ages of maturity. Fatigue loading produced a progressive loss in stiffness and an increase in hysteresis prior to failure, indicating that immature primate cortical bone responds to repeated loading in a fashion similar to that previously observed for adult human cortical bone. Bone fatigue resistance under this strain controlled testing decreased during maturation. Maturation was also associated with an increase in bone dry density, ash fraction and elastic modulus. The higher elastic modulus of more mature bone meant that these specimens were subjected to higher stress levels during testing than more immature bone specimens. Anatomical regions along the femoral shaft exhibited differences in strength and fatigue resistance.

Influence of neutron irradiation at 430$deg;C on the fatigue properties of SA 316L steel

NASA Astrophysics Data System (ADS)

Vandermeulen, W.; Hendrix, W.; Massaut, V.; Van de Velde, J.

1988-07-01

Fatigue tests have been carried out at 430°C on hour-glass shaped specimens of the CEC reference heat of SA 316L stainless steel. The tests were performed under constant total axial strain control with a triangular fully reversed wave shape at frequencies of 0.5, 0.05 and 0.005 Hz. Specimens irradiated at 430°C to doses of 9-12 dpa and helium contents of 80 to 145 appm showed a fatigue life reduction by about a factor of two, compared to unirradiated specimens. The cyclic stress is found to be strongly increased by the irradiation. The test frequency influences the fatigue hardening slightly but it does not affect the fatigue life.

Machining of Aircraft Titanium with Abrasive-Waterjets for Fatigue Critical Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, H. T.; Hovanski, Yuri; Dahl, Michael E.

2010-10-04

Laboratory tests were conducted to determine the fatigue performance of AWJ-machined aircraft titanium. Dog-bone specimens machined with AWJs were prepared and tested with and without sanding and dry-grit blasting with Al2O3 as secondary processes. The secondary processes were applied to remove the visual appearance of AWJ-generated striations and to clean up the garnet embedment. The fatigue performance of AWJ-machined specimens was compared with baseline specimens machined with CNC milling. Fatigue test results not only confirmed the findings of the aluminum dog-bone specimens but also further enhance the fatigue performance. In addition, titanium is known to be notoriously difficult to cutmore » with contact tools while AWJs cut it 34% faster than stainless steel. AWJ cutting and dry-grit blasting are shown to be a preferred combination for processing aircraft titanium that is fatigue critical.« less

A systems approach to solder joint fatigue in spacecraft electronic packaging

NASA Technical Reports Server (NTRS)

Ross, R. G., Jr.

1991-01-01

Differential expansion induced fatigue resulting from temperature cycling is a leading cause of solder joint failures in spacecraft. Achieving high reliability flight hardware requires that each element of the fatigue issue be addressed carefully. This includes defining the complete thermal-cycle environment to be experienced by the hardware, developing electronic packaging concepts that are consistent with the defined environments, and validating the completed designs with a thorough qualification and acceptance test program. This paper describes a useful systems approach to solder fatigue based principally on the fundamental log-strain versus log-cycles-to-failure behavior of fatigue. This fundamental behavior has been useful to integrate diverse ground test and flight operational thermal-cycle environments into a unified electronics design approach. Each element of the approach reflects both the mechanism physics that control solder fatigue, as well as the practical realities of the hardware build, test, delivery, and application cycle.

Effect of Surface Impulsive Thermal Loads on Fatigue Behavior of Constant Volume Propulsion Engine Combustor Materials

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Fox, Dennis S.; Miller, Robert A.; Ghosn, Louis J.; Kalluri, Sreeramesh

2004-01-01

The development of advanced high performance constant-volume-combustion-cycle engines (CVCCE) requires robust design of the engine components that are capable of enduring harsh combustion environments under high frequency thermal and mechanical fatigue conditions. In this study, a simulated engine test rig has been established to evaluate thermal fatigue behavior of a candidate engine combustor material, Haynes 188, under superimposed CO2 laser surface impulsive thermal loads (30 to 100 Hz) in conjunction with the mechanical fatigue loads (10 Hz). The mechanical high cycle fatigue (HCF) testing of some laser pre-exposed specimens has also been conducted under a frequency of 100 Hz to determine the laser surface damage effect. The test results have indicated that material surface oxidation and creep-enhanced fatigue is an important mechanism for the surface crack initiation and propagation under the simulated CVCCE engine conditions.

High temperature fatigue behavior of Haynes 188

NASA Technical Reports Server (NTRS)

Halford, Gary R.; Saltsman, James F.; Kalluri, Sreeramesh

1988-01-01

The high temperature, creep-fatigue behavior of Haynes 188 was investigated as an element in a broader thermomechanical fatigue life prediction model development program at the NASA-Lewis. The models are still in the development stage, but the data that were generated possess intrinsic value on their own. Results generated to date is reported. Data were generated to characterize isothermal low cycle fatigue resistance at temperatures of 316, 704, and 927 C with cyclic failure lives ranging from 10 to more than 20,000. These results follow trends that would be predicted from a knowledge of tensile properties, i.e., as the tensile ductility varies with temperature, so varies the cyclic inelastic straining capacity. Likewise, as the tensile strength decreases, so does the high cyclic fatigue resistance. A few two-minute hold-time cycles at peak compressive strain were included in tests at 760 C. These results were obtained in support of a redesign effort for the Orbital Maneuverable System engine. No detrimental effects on cyclic life were noted despite the added exposure time for creep and oxidation. Finally, a series of simulated thermal fatigue tests, referred to as bithermal fatigue tests, were conducted using 316 C as the minimum and 760 C as the maximum temperature. Only out-of-phase bithermal tests were conducted to date. These test results are intended for use as input to a more general thermomechanical fatigue life prediction model based on the concepts of the total strain version of Strainrange Partitioning.

Rolling-Element Fatigue Testing and Data Analysis - A Tutorial

NASA Technical Reports Server (NTRS)

Vlcek, Brian L.; Zaretsky, Erwin V.

2011-01-01

In order to rank bearing materials, lubricants and other design variables using rolling-element bench type fatigue testing of bearing components and full-scale rolling-element bearing tests, the investigator needs to be cognizant of the variables that affect rolling-element fatigue life and be able to maintain and control them within an acceptable experimental tolerance. Once these variables are controlled, the number of tests and the test conditions must be specified to assure reasonable statistical certainty of the final results. There is a reasonable correlation between the results from elemental test rigs with those results obtained with full-scale bearings. Using the statistical methods of W. Weibull and L. Johnson, the minimum number of tests required can be determined. This paper brings together and discusses the technical aspects of rolling-element fatigue testing and data analysis as well as making recommendations to assure quality and reliable testing of rolling-element specimens and full-scale rolling-element bearings.

Advanced composite stabilizer for Boeing 737 aircraft

NASA Technical Reports Server (NTRS)

1978-01-01

Activities related to development of an advanced composites stabilizer for the Boeing 737 commercial transport are reported. Activities include discussion of criteria and objectives, design loads, the fatigue spectrum definition to be used for all spectrum fatigue testing, fatigue analysis, manufacturing producibility studies, the ancillary test program, quality assurance, and manufacturing development.

A study of fatigue and fracture in 7075-T6 aluminum alloy in vacuum and air environments

NASA Technical Reports Server (NTRS)

Hudson, C. M.

1973-01-01

Axial load fatigue life, fatigue-crack propagation, and fracture toughness experiments were conducted on sheet specimens made of 7075-T6 aluminum alloy. These experiments were conducted at pressures ranging from atmospheric to 5 x 10 to the minus 8th torr. Analysis of the results from the fatigue life experiments indicated that for a given stress level, lower air pressures produced longer fatigue lives. At a pressure of 5 x 10 to the minus 8th torr fatigue lives were 15 or more times as long as at atmospheric pressure. Analysis of the results from the fatigue crack propagation experiments indicated that for small stress intensity factor ranges the fatigue crack propagation rates were up to twice as high at atmospheric pressure as in vacuum. The fracture toughness of 7075-T6 was unaffected by the vacuum environment. Fractographic examination showed that specimens tested in both vacuum and air developed fatigue striations. Considerably more striations developed on specimens tested at atmospheric pressure, however.

Endurance and fatigue characteristics in the neck muscles during sub-maximal isometric test in patients with cervical radiculopathy.

PubMed

Halvorsen, Marie; Abbott, Allan; Peolsson, Anneli; Dedering, Åsa

2014-03-01

The aim of the study was to compare myoelectric manifestation in neck muscle endurance and fatigue characteristics during sub-maximal isometric endurance test in patients with cervical radiculopathy and asymptomatic subjects. An additional aim was to explore associations between primary neck muscle endurance, myoelectric fatigability, and self-rated levels of fatigue, pain and subjective health measurements in patients with cervical radiculopathy. Muscle fatigue in the ventral and dorsal neck muscles was assessed in patients with cervical radiculopathy and in an asymptomatic group during an isometric neck muscle endurance test in prone and supine. 46 patients and 34 asymptomatic subjects participated. Surface electromyography signals were recorded from the sternocleidomastoid, cervical paraspinal muscles and upper and middle trapezius bilaterally during the endurance test. Subjective health measurements were assessed with questionnaires. The results showed altered neck muscle endurance in several of the muscles investigated with greater negative median frequency slope, greater variability, side imbalance, lower endurance time and higher experience of fatigue among the cervical radiculopathy patients compared with healthy subjects. Endurance times were significantly lower in both prone and in supine positions between the patients compared to asymptomatic subjects. During the neck muscle endurance test, fatigues in the upper trapezius muscles during the prone test and in the sternocleidomastoid muscles during the supine test were of more importance than self-perceived pain, fatigue, disability and kinesiophobia in predicting neck muscle endurance (NME). NME testing in the primary neck muscles seems to be an important factor to take into consideration in rehabilitation.

Transverse Tension Fatigue Life Characterization Through Flexure Testing of Composite Materials

NASA Technical Reports Server (NTRS)

OBrien, T. Kevin; Chawan, Arun D.; Krueger, Ronald; Paris, Isabelle

2001-01-01

The transverse tension fatigue life of S2/8552 glass-epoxy and IM7/8552 carbon-epoxy was characterized using flexure tests of 90-degree laminates loaded in 3-point and 4-point bending. The influence of specimen polishing and specimen configuration on transverse tension fatigue life was examined using the glass-epoxy laminates. Results showed that 90-degree bend specimens with polished machined edges and polished tension-side surfaces, where bending failures where observed, had lower fatigue lives than unpolished specimens when cyclically loaded at equal stress levels. The influence of specimen thickness and the utility of a Weibull scaling law was examined using the carbon-epoxy laminates. The influence of test frequency on fatigue results was also documented for the 4-point bending configuration. A Weibull scaling law was used to predict the 4-point bending fatigue lives from the 3-point bending curve fit and vice-versa. Scaling was performed based on maximum cyclic stress level as well as fatigue life. The scaling laws based on stress level shifted the curve fit S-N characterizations in the desired direction, however, the magnitude of the shift was not adequate to accurately predict the fatigue lives. Furthermore, the scaling law based on fatigue life shifted the curve fit S-N characterizations in the opposite direction from measured values. Therefore, these scaling laws were not adequate for obtaining accurate predictions of the transverse tension fatigue lives.

Muscle contractile characteristics: relationship to high-intensity exercise.

PubMed

Morris, Martyn G; Dawes, Helen; Howells, Ken; Scott, Oona M; Cramp, Mary; Izadi, Hooshang

2010-09-01

We investigated the relationship between muscle contractile characteristics, collected using percutaneous electrical stimulation, and high-intensity exercise performance. Seventeen participants performed a muscle performance test for the calculation of rate of torque development (RTD), rate of relaxation (RR(1/2)), rate of fatigue and fatigue resistance. On a second visit the participants completed a Wingate cycle ergometer test with peak power, mean power, fatigue index and fatigue rate calculated. The muscle fatigue index related significantly to the WAnT fatigue index and fatigue rate (p < 0.01). The change in rate of torque development (%DeltaRTD) was also related significantly to the fatigue rate (W/s) during the WAnT. Subjects displaying the greatest reduction in RTD had the greatest fatigue rate during the WAnT and greater fatigue during the electrical stimulation protocol. There were no significant relationships between peak (r 0.36; p > 0.01) or mean power (r -0.11, p > 0.01) with any of the muscle performance measures. These findings demonstrate that muscle contractile characteristics, elicited during standardised in vivo electrical stimulation, relate to performance during a Wingate anaerobic test. They suggest that muscle contraction characteristics play an important role in high-intensity exercise performance and indicate that electrical stimulation protocols can be a useful additional tool to explore muscle contraction characteristics in relation to exercise performance and trainability.

Fatigue and durability of Nitinol stents.

PubMed

Pelton, A R; Schroeder, V; Mitchell, M R; Gong, Xiao-Yan; Barney, M; Robertson, S W

2008-04-01

Nitinol self-expanding stents are effective in treating peripheral artery disease, including the superficial femoral, carotid, and renal arteries. However, fracture occurrences of up to 50% have been reported in some stents after one year. These stent fractures are likely due to in vivo cyclic displacements. As such, the cyclic fatigue and durability properties of Nitinol-based endovascular stents are discussed in terms of an engineering-based experimental testing program. In this paper, the combined effects of cardiac pulsatile fatigue and stent-vessel oversizing are evaluated for application to both stents and stent subcomponents. In particular, displacement-controlled fatigue tests were performed on stent-like specimens processed from Nitinol microtubing. Fatigue data were collected with combinations of simulated oversizing conditions and pulsatile cycles that were identified by computer modeling of the stent that mimic in vivo deformation conditions. These data are analyzed with non-linear finite element computations and are illustrated with strain-life and strain-based constant-life diagrams. The utility of this approach is demonstrated in conjunction with 10 million cycle pulsatile fatigue tests of Cordis SMART Control((R)) Nitinol self-expanding stents to calculate fatigue safety factors and thereby predict in vivo fatigue resistance. These results demonstrate the non-linear constant fatigue-life response of Nitinol stents, whereby, contrary to conventional engineering materials, the fatigue life of Nitinol is observed to increase with increasing mean strain.

Use of atomic force microscopy for characterizing damage evolution during fatigue

NASA Astrophysics Data System (ADS)

Cretegny, Laurent

2000-10-01

A study of the development of surface fatigue damage in PH 13-8 Mo stainless steel and copper by atomic force microscopy (AFM) was performed. AFM observations allow highly automated, quantitative characterization of surface deformation with a resolution of 5 nm or better, which is ideal for understanding fatigue damage evolution. A secondary objective was to establish a correlation between fatigue life exhausted and impedance spectroscopy. Strain controlled fatigue tests were conducted both in high and low cycle fatigue regimes, and interruptions of the fatigue tests allowed characterizing the evolution of the surface upset at various life-fractions. In the low strain amplitude tests on stainless steel (Deltaepsilonpl/2 = 0.0026%), surface damage occurred in the shape of narrow streaks at the interface between martensite laths where reverted austenite was present. The streaks eventually coalesced to form crack nuclei. In high strain amplitude tests (Deltaepsilon pl/2 = 0.049%), fatigue surface damage was essentially dominated by the formation of extrusions. In copper, both low (Deltaepsilonpl/2 = 0.061%) and high (Deltaepsilonpl/2 = 0.134%) strain amplitude tests showed the formation of slip bands (mainly extrusions) across entire grains. Protrusions were present only in copper specimens tested at the high strain amplitude. Crack nucleation in the low strain amplitude tests occurred in both materials at the interface between a region that sustained a high level of deformation and one with little evidence of surface upset. This commonality between these two materials that are otherwise very dissimilar in nature suggests a universal scheme for location of fatigue crack nucleation sites during HCF. A procedure was developed in this study to quantitatively characterize the amount of irreversible surface strain. The proposed formalism is applicable to any material, independently of the type of surface damage, and leads to a criterion for crack nucleation based on physical evidence of surface damage. A correlation between fatigue damage and impedance spectroscopy measurements was shown in copper, in particular during the primary cyclic hardening stage. The measurements were however less sensitive to the development of surface upset that occurred beyond that stage.

Reference values for fatigued versus non-fatigued limb symmetry index measured by a newly designed single-leg hop test battery in healthy subjects: a pilot study.

PubMed

Leister, Iris; Mattiassich, Georg; Kindermann, Harald; Ortmaier, Reinhold; Barthofer, Jürgen; Vasvary, Imre; Katzensteiner, Klaus; Stelzhammer, Christine; Kulnik, Stefan Tino

2018-01-01

There is sparse evidence for return to sport criteria after knee injury. Functional performance deficits, particularly in fatigued muscular condition, should be verified prior to the attempt to return to high-risk pivoting sports. The purpose of this study was to generate reference values for the limb symmetry index (LSI) of healthy subjects in fatigued and non-fatigued muscular condition in a newly designed test battery. Forty-two healthy subjects [22 females, 20 males; mean (SD) age 30.4 (6.6) years] were evaluated using a test battery consisting of an isometric strength test, a series of five single-leg hop tests and an integrated fatigue protocol. Subjective physical activity was assessed with the Tegner Activity Scale (TAS). The cut-off values for healthy subjects were calculated considering the fifth percentile as the minimum reference value for the LSI and single-leg hop distance. The mean (SD) overall LSI was 98.8% (4.6). No significant gender or age specific differences in limb symmetry were observed. The comparison of the non-fatigued LSI with the overall LSI revealed no clinically relevant change due to muscular fatigue. Repeated measures ANOVA revealed a significant within effect on fatigue/non-fatigue condition ( F (1,38)  = 18.000; p  < 0.001, η 2  = 0.321) on absolute single-leg hop distance. Moreover, a significant between effect on the TAS-parameter ( F (1,38)  = 5.928; p  = 0.020, η 2  = 0.135 between: TAS ≤ 5/TAS > 5) and on gender ( F (1,38)  = 23.956; p  < 0.001, η 2  = 0.387) could be detected. The absolute jumping distance in the single-leg hop for distance was significantly reduced due to fatigue. No clinically relevant effect of muscular fatigue was observed on limb symmetry in our study sample. Gender and physical activity are important factors to be considered when interpreting reference values.

The Relationships Between Microstructure, Tensile Properties and Fatigue Life in Ti-5Al-5V-5Mo-3Cr-0.4Fe (Ti-5553)

NASA Astrophysics Data System (ADS)

Foltz, John W., IV

beta-titanium alloys are being increasingly used in airframes as a way to decrease the weight of the aircraft. As a result of this movement, Ti-5Al-5V-5Mo-3Cr-0.4Fe (Timetal 555), a high-strength beta titanium alloy, is being used on the current generation of landing gear. This alloy features good combinations of strength, ductility, toughness and fatigue life in alpha+beta processed conditions, but little is known about beta-processed conditions. Recent work by the Center for the Accelerated Maturation of Materials (CAMM) research group at The Ohio State University has improved the tensile property knowledge base for beta-processed conditions in this alloy, and this thesis augments the aforementioned development with description of how microstructure affects fatigue life. In this work, beta-processed microstructures have been produced in a Gleeble(TM) thermomechanical simulator and subsequently characterized with a combination of electron and optical microscopy techniques. Four-point bending fatigue tests have been carried out on the material to characterize fatigue life. All the microstructural conditions have been fatigue tested with the maximum test stress equal to 90% of the measured yield strength. The subsequent results from tensile tests, fatigue tests, and microstructural quantification have been analyzed using Bayesian neural networks in an attempt to predict fatigue life using microstructural and tensile inputs. Good correlation has been developed between lifetime predictions and experimental results using microstructure and tensile inputs. Trained Bayesian neural networks have also been used in a predictive fashion to explore functional dependencies between these inputs and fatigue life. In this work, one section discusses the thermal treatments that led to the observed microstructures, and the possible sequence of precipitation that led to these microstructures. The thesis then describes the implications of microstructure on fatigue life and implications of tensile properties on fatigue life. Several additional experiments are then described that highlight possible causes for the observed dependence of microstructure on fatigue life, including fractographic evidence to provide support of microstructural dependencies.

Effect of lubricant extreme-pressure additives on surface fatigue life of AISI 9310 spur gears

NASA Technical Reports Server (NTRS)

Scibbe, H. W.; Townsend, D. P.; Aron, P. R.

1984-01-01

Surface fatigue tests were conducted with AISI 9310 spur gears using a formulated synthetic tetraester oil (conforming to MIL-L-23699 specifications) as the lubricant containing either sulfur or phosphorus as the EP additive. Four groups of gears were tested. One group of gears tested without an additive in the lubricant acted as the reference oil. In the other three groups either a 0.1 wt % sulfur or phosphorus additive was added to the tetraester oil to enhance gear surface fatigue life. Test conditions included a gear temperature of 334 K (160 F), a maximum Hertz stress of 1.71 GPa (248 000 psi), and a speed of 10,000 rpm. The gears tested with a 0.1 wt % phosphorus additive showed pitting fatigue life 2.6 times the life of gears tested with the reference tetraester based oil. Although fatigue lives of two groups of gears tested with the sulfur additive in the oil showed improvement over the control group gear life, the results, unlike those obtained with the phosphorus oil, were not considered to be statistically significant.

Effect of interlaminar normal stresses on the uniaxial zero-to-tension fatigue behavior of graphite/epoxy tubes

NASA Technical Reports Server (NTRS)

Krempl, Erhard; An, Deukman

1991-01-01

Fatigue tests conducted with and without internal pressure have been found to possess approximately the same fatigue life as (+/-45)s graphite/epoxy tubes for zero-to-tension axial load-controlled conditions on an axial torsion servohydraulic apparatus. These tests therefore cannot be considered as confirmations of the suspected detrimental effect of interlaminar tensile stresses on the fatigue performance of thin-walled tubes. The addition of 90-deg plies on both the inside and the outside is found to significantly improve the tubes' static and fatigue strengths.

Reliability improvement of wire bonds subjected to fatigue stresses.

NASA Technical Reports Server (NTRS)

Ravi, K. V.; Philofsky, E. M.

1972-01-01

The failure of wire bonds due to repeated flexure when semiconductor devices are operated in an on-off mode has been investigated. An accelerated fatigue testing apparatus was constructed and the major fatigue variables, aluminum alloy composition, and bonding mechanism, were tested. The data showed Al-1% Mg wires to exhibit superior fatigue characteristics compared to Al-1% Cu or Al-1% Si and ultrasonic bonding to be better than thermocompression bonding for fatigue resistance. Based on these results highly reliable devices were fabricated using Al-1% Mg wire with ultrasonic bonding which withstood 120,000 power cycles with no failures.

Damage mechanisms in bithermal and thermomechanical fatigue of Haynes 188

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Halford, Gary R.

1992-01-01

Post failure fractographic and metallographic studies were conducted on Haynes 188 specimens fatigued under bithermal and thermomechanical loading conditions between 316 and 760 C. Bithermal fatigue specimens examined included those tested under high strain rate in-phase and out-phase, tensile creep in-phase, and compressive creep out-of-phase loading conditions. Specimens tested under in-phase and out-of-phase thermomechanical fatigue were also examined. The nature of failure mode (transgrandular versus intergranular), the topography of the fracture surface, and the roles of oxidation and metallurgical changes were studied for each type of bithermal and thermomechanical test.

Fatigue damage characterization of braided and woven fiber reinforced polymer matrix composites at room and elevated temperatures

NASA Astrophysics Data System (ADS)

Montesano, John

The use of polymer matrix composites (PMC) for manufacturing primary load-bearing structural components has significantly increased in many industrial applications. Specifically in the aerospace industry, PMCs are also being considered for elevated temperature applications. Current aerospace-grade composite components subjected to fatigue loading are over-designed due to insufficient understanding of the material failure processes, and due to the lack of available generic fatigue prediction models. A comprehensive literature survey reveals that there are few fatigue studies conducted on woven and braided fabric reinforced PMC materials, and even fewer at elevated temperatures. It is therefore the objective of this study to characterize and subsequently model the elevated temperature fatigue behaviour of a triaxial braided PMC, and to investigate the elevated temperature fatigue properties of two additional woven PMCs. An extensive experimental program is conducted using a unique test protocol on the braided and woven composites, which consists of static and fatigue testing at various test temperatures. The development of mechanically-induced damage is monitored using a combination of non-destructive techniques which included infrared thermography, fiber optic sensors and edge replication. The observed microscopic damage development is quantified and correlated to the exhibited macroscopic material behaviour at all test temperatures. The fiber-dominated PMC materials considered in this study did not exhibit notable time- or temperature-dependent static properties. However, fatigue tests reveal that the local damage development is in fact notably influenced by temperature. The elevated temperature environment increases the toughness of the thermosetting polymers, which results in consistently slower fatigue crack propagation rates for the respective composite materials. This has a direct impact on the stiffness degradation rate and the fatigue lives for the braided and woven composites under investigation. The developed analytical fatigue damage prediction model, which is based on actual observed damage mechanisms, accurately predicted the development of damage and the corresponding stiffness degradation for the braided PMC, for all test temperatures. An excellent correlation was found between the experimental and the predicted results to within a 2% accuracy. The prediction model adequately captured the local temperature-induced phenomenon exhibited by the braided PMC material. The results presented in this study are novel for a braided composite material subjected to elevated temperature fatigue.

Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 Under Biaxial and Uniaxial Fatigue

DTIC Science & Technology

2014-06-19

al. examined the effect of biaxial loading on the fatigue crack growth [52]. They conducted their fatigue tests on SUS 304 stainless steel using a...specimens. Their experiments were carried out on cruciform test coupons using a digitally controlled four actuator biaxial testing system. Steel ...as shown in Figure 3.7. The test specimen was placed between two stainless steel chambers. These chambers were connected together using screws, and

Overload and Underload Effects on the Fatigue Crack Growth Behavior of the 2024-T3 Aluminum Alloy

NASA Technical Reports Server (NTRS)

Dawicke, David S.

1997-01-01

Fatigue crack growth tests were conducted on 0.09 inch thick, 3.0 inch wide middle-crack tension specimens cut from sheets of 2024-T3 aluminum alloy. The tests were conducted using a load sequence that consisted of a single block of 2,500 cycles of constant amplitude loading followed by an overload/underload combination. The largest fatigue crack growth life occurred for the tests with the overload stress equal to 2 times the constant amplitude stress and the underload stress equal to the constant amplitude minimum stress. For the tests with compressive underloads, the fatigue crack growth life decreased with increasing compressive underload stress.

New method of determination of spot welding-adhesive joint fatigue life using full field strain evolution

NASA Astrophysics Data System (ADS)

Sadowski, T.; Kneć, M.

2016-04-01

Fatigue tests were conducted since more than two hundred years ago. Despite this long period, as fatigue phenomena are very complex, assessment of fatigue response of standard materials or composites still requires a long time. Quite precise way to estimate fatigue parameters is to test at least 30 standardized specimens for the analysed material and further statistical post processing is required. In case of structural elements analysis like hybrid joints (Figure 1), the situation is much more complex as more factors influence the fatigue load capacity due to much more complicated structure of the joint in comparison to standard materials specimen, i.e. occurrence of: welded hot spots or rivets, adhesive layers, local notches creating the stress concentrations, etc. In order to shorten testing time some rapid methods are known: Locati's method [1] - step by step load increments up to failure, Prot's method [2] - constant increase of the load amplitude up to failure; Lehr's method [2] - seeking for the point during regular fatigue loading when an increase of temperature or strains become non-linear. The present article proposes new method of the fatigue response assessment - combination of the Locati's and Lehr's method.

Elevated temperature biaxial fatigue

NASA Technical Reports Server (NTRS)

Jordan, E. H.

1985-01-01

A 3 year experimental program for studying elevated temperature biaxial fatigue of a nickel based alloy Hastelloy-X has been completed. A new high temperature fatigue test facility with unique capabilities has been developed. Effort was directed toward understanding multiaxial fatigue and correlating the experimental data to the existing theories of fatigue failure. The difficult task of predicting fatigue lives for nonproportional loading was used as an ultimate test for various life prediction methods being considered. The primary means of reaching improved understanding were through several critical nonproportional loading experiments. The direction of cracking observed on failed specimens was also recorded and used to guide the development of the theory. Cyclic deformation responses were permanently recorded digitally during each test. It was discovered that the cracking mode switched from primarily cracking on the maximum shear planes at room temperature to cracking on the maximum normal strain planes at 649 C. In contrast to some other metals, loading path in nonproportional loading had little effect on fatigue lives. Strain rate had a small effect on fatigue lives at 649 C. Of the various correlating parameters the modified plastic work and octahedral shear stress were the most successful.

Exercise capacity, muscle strength and fatigue in sarcoidosis.

PubMed

Marcellis, R G J; Lenssen, A F; Elfferich, M D P; De Vries, J; Kassim, S; Foerster, K; Drent, M

2011-09-01

The aim of this case-control study was to investigate the prevalence of exercise intolerance, muscle weakness and fatigue in sarcoidosis patients. Additionally, we evaluated whether fatigue can be explained by exercise capacity, muscle strength or other clinical characteristics (lung function tests, radiographic stages, prednisone usage and inflammatory markers). 124 sarcoidosis patients (80 males) referred to the Maastricht University Medical Centre (Maastricht, the Netherlands) were included (mean age 46.6±10.2 yrs). Patients performed a 6-min walk test (6MWT) and handgrip force (HGF), elbow flexor muscle strength (EFMS), quadriceps peak torque (QPT) and hamstring peak torque (HPT) tests. Maximal inspiratory pressure (P(I,max)) was recorded. All patients completed the Fatigue Assessment Scale (FAS) questionnaire. The 6MWT was reduced in 45% of the population, while HGF, EFMS, QPT and HPT muscle strength were reduced in 15, 12, 27 and 18%, respectively. P(I,max) was reduced in 43% of the population. The majority of the patients (81%) reported fatigue (FAS ≥22). Patients with reduced peripheral muscle strength of the upper and/or lower extremities were more fatigued and demonstrated impaired lung functions, fat-free mass, P(I,max), 6MWT and quality of life. Fatigue was neither predicted by exercise capacity, nor by muscle strength. Besides fatigue, exercise intolerance and muscle weakness are frequent problems in sarcoidosis. We therefore recommend physical tests in the multidisciplinary management of sarcoidosis patients, even in nonfatigued patients.

Influence of Training Load and Altitude on HRV Fatigue Patterns in Elite Nordic Skiers.

PubMed

Schmitt, Laurent; Regnard, Jacques; Coulmy, Nicolas; Millet, Gregoire P

2018-06-14

We aimed to analyse the relationship between training load/intensity and different heart rate variability (HRV) fatigue patterns in 57 elite Nordic-skiers. 1063 HRV tests were performed during 5 years. R-R intervals were recorded in resting supine (SU) and standing (ST) positions. Heart rate, low (LF), high (HF) frequency powers of HRV were determined. Training volume, training load (TL, a.u.) according to ventilatory threshold 1 (VT1) and VT2 were measured in zones I≤VT1; VT1VT2, IV for strength. TL was performed at 81.6±3.5% in zone I, 0.9±0.9% in zone II, 5.0±3.6% in zone III, 11.6±6.3% in zone IV. 172 HRV tests matched a fatigue state and four HRV fatigue patterns (F) were statistically characterized as F(HF-LF-)SU_ST for 121 tests, F(LF+SULF-ST) for 18 tests, F(HF-SUHF+ST) for 26 tests and F(HF+SU) for 7 tests. The occurrence of fatigue states increased substantially with the part of altitude training time (r2=0.52, p<0.001). This study evidenced that there is no causal relationship between training load/intensity and HRV fatigue patterns. Four fatigue-shifted HRV patterns were sorted. Altitude training periods appeared critical as they are likely to increase the overreaching risks. © Georg Thieme Verlag KG Stuttgart · New York.

Low cycle fatigue

NASA Technical Reports Server (NTRS)

Solomon, H. D. (Editor); Kaisand, L. R. (Editor); Halford, G. R. (Editor); Leis, B. N. (Editor)

1988-01-01

The papers contained in this volume focus on various aspects of low cycle fatigue, including cyclic deformation, crack propagation, high-temperature low cycle fatigue, microstructural defects, multiaxial and variable amplitude loading, and life prediction. Papers are presented on the low cycle fatigue of some aluminum alloys, prediction of crack growth under creep-fatigue loading conditions, high-temperature low cycle fatigue behavior and lifetime prediction of a nickel-base ODS alloy, and an integrated approach to creep-fatigue life prediction. Other topics discussed include thermal fatigue testing of coated monocrystalline superalloys, low cycle fatigue of Al-Mg-Si alloys, and the effect of superimposed stresses at high frequency on low cycle fatigue.

Rotating Beam Fatigue Testing and Hybrid Ceramic Bearings.

DTIC Science & Technology

1994-07-01

Runout and Fast Fracture ......... 20 FIG.7 Stress-life Plots of Rotating Beam Fatigue Testing ............. 23 FIG.8 Fractograph of Rotating Beam...Chand-Kare Engineering Ceramics, Worcester, MA. Diamond wheels of 600 grits were used with longitudinal grinding applied for the final finishing of...stress in the range of 600-850 MPa. Three test completion modes were encountered, i.e. fast fracture at setup, fatigue fracture and runout (no failure

Predicting Fatigue and Psychophysiological Test Performance from Speech for Safety-Critical Environments.

PubMed

Baykaner, Khan Richard; Huckvale, Mark; Whiteley, Iya; Andreeva, Svetlana; Ryumin, Oleg

2015-01-01

Automatic systems for estimating operator fatigue have application in safety-critical environments. A system which could estimate level of fatigue from speech would have application in domains where operators engage in regular verbal communication as part of their duties. Previous studies on the prediction of fatigue from speech have been limited because of their reliance on subjective ratings and because they lack comparison to other methods for assessing fatigue. In this paper, we present an analysis of voice recordings and psychophysiological test scores collected from seven aerospace personnel during a training task in which they remained awake for 60 h. We show that voice features and test scores are affected by both the total time spent awake and the time position within each subject's circadian cycle. However, we show that time spent awake and time-of-day information are poor predictors of the test results, while voice features can give good predictions of the psychophysiological test scores and sleep latency. Mean absolute errors of prediction are possible within about 17.5% for sleep latency and 5-12% for test scores. We discuss the implications for the use of voice as a means to monitor the effects of fatigue on cognitive performance in practical applications.

Predicting Fatigue and Psychophysiological Test Performance from Speech for Safety-Critical Environments

PubMed Central

Baykaner, Khan Richard; Huckvale, Mark; Whiteley, Iya; Andreeva, Svetlana; Ryumin, Oleg

2015-01-01

Automatic systems for estimating operator fatigue have application in safety-critical environments. A system which could estimate level of fatigue from speech would have application in domains where operators engage in regular verbal communication as part of their duties. Previous studies on the prediction of fatigue from speech have been limited because of their reliance on subjective ratings and because they lack comparison to other methods for assessing fatigue. In this paper, we present an analysis of voice recordings and psychophysiological test scores collected from seven aerospace personnel during a training task in which they remained awake for 60 h. We show that voice features and test scores are affected by both the total time spent awake and the time position within each subject’s circadian cycle. However, we show that time spent awake and time-of-day information are poor predictors of the test results, while voice features can give good predictions of the psychophysiological test scores and sleep latency. Mean absolute errors of prediction are possible within about 17.5% for sleep latency and 5–12% for test scores. We discuss the implications for the use of voice as a means to monitor the effects of fatigue on cognitive performance in practical applications. PMID:26380259

New Equipment for Testing the Fatigue Strength of Riveted and Welded Joints

NASA Technical Reports Server (NTRS)

Muller, W

1940-01-01

The mechanical and electrical construction of a new experimental instrument for fatigue testing riveted and welded joints is described. This experimental device has the advantage of being able to stress, even with comparatively low magnetic exciter force, structural components in alternate bending by resonance vibrations up to incipient fatigue failure.

A microstructurally based model of solder joints under conditions of thermomechanical fatigue

NASA Astrophysics Data System (ADS)

Frear, D. R.; Burchett, S. N.; Rashid, M. M.

The thermomechanical fatigue failure of solder joints is increasingly becoming an important reliability issue. We present two computational methodologies that have been developed to predict the behavior of near eutectic Sn-Pb solder joints under fatigue conditions that are based on metallurgical tests as fundamental input for constitutive relations. The two-phase model mathematically predicts the heterogeneous coarsening behavior of near eutectic Sn-Pb solder. The finite element simulations from this model agree well with experimental thermomechanical fatigue tests. The simulations show that the presence of an initial heterogeneity in the solder microstructure could significantly degrade the fatigue lifetime. The single phase model is a computational technique that was developed to predict solder joint behavior using materials data for constitutive relation constants that could be determined through straightforward metallurgical experiments. A shear/torsion test sample was developed to impose strain in two different orientations. Materials constants were derived from these tests and the results showed an adequate fit to experimental results. The single-phase model could be very useful for conditions where microstructural evolution is not a dominant factor in fatigue.

Experimental Evaluation of Fatigue Crack Initiation from Corroded Hemispherical Notches in Aerospace Structural Materials

NASA Technical Reports Server (NTRS)

Garcia, Daniel B.; Forman, Royce; Shindo, David

2010-01-01

A test program was developed and executed to evaluate the influence of corroded hemispherical notches on the fatigue crack initiation and propagation in aluminum 7075-T7351, 4340 steel, and D6AC steel. Surface enhancements such as shot peening and laser shock peening were also incorporated as part of the test effort with the intent of improving fatigue performance. In addition to the testing, fracture mechanics and endurance limit based analysis methods were evaluated to characterize the results with the objective of challenging typical assumptions used in modeling fatigue cracks from corrosion pits. The results specifically demonstrate that the aluminum and steel alloys behave differently with respect to fatigue crack initiation from hemispherical corrosion pits. The aluminum test results were bounded by the fracture mechanics and endurance limit models while exhibiting a general insensitivity to the residual stress field generated by shot peening. The steel specimens were better characterized by the endurance limit fatigue properties and did exhibit sensitivities to residual stresses from the shot peening and laser shock peening

Effects of High Temperature Exposures on Fatigue Life of Disk Superalloys

NASA Technical Reports Server (NTRS)

Gabb, Tim P.; Telesman, Jack; Kantzos, Pete T.; Smith, James W.; Browning, Paul F.

2004-01-01

The effects on fatigue life of high temperature exposures simulating service conditions were considered for two disk superalloys. Powder metallurgy processed, supersolvus heat treated Udimet (trademark) 720 and ME3 fatigue specimens were exposed in air at temperatures of 650 to 704 C, for times of 100 h to over 1000 h. They were then tested using conventional fatigue tests at 650 and 704 C, to determine the effects of exposure on fatigue resistance. Cyclic dwell verification tests were also performed to contrast the effects of intermixed exposures and fatigue cycles. The prior exposures reduced life by up to 70% and increased the scatter in life, compared to unexposed levels. Cyclic dwell tests reduced lives even more. Fractographic evaluations indicated the failure mode was shifted by the exposures and cyclic dwells from predominantly internal to often surface crack initiations. The increased scatter in life was related to the competition between internal crack initiations at inclusions or large grains producing longer lives, and surface crack initiations at an environmentally affected surface layer producing shorter lives.

Microstructural examination of

NASA Astrophysics Data System (ADS)

Fukuoka, C.; Yoshizawa, H.; Nakagawa, Y. G.; Lapides, M. E.

1993-10-01

Fatigue tests were performed to examine how microstructural conditioning influences crack initiation and propagation in SA508 class 3 low-carbon steel. A 3-mm-long crack was introduced in compact tension (CT) fatigue test specimens under four different loads in order to obtain crack tip plastic zones at different stress intensity factor ranges, ΔK = 18, 36, 54, and 72 MPa√m. The microstructure of the plastic zones around the crack tip were examined by trans- mission electron microscopy (TEM) and selected area electron diffraction (SAD). Micro- orientation of the dislocation cells in the plastic zones of all of the CT samples increased to 4 deg from the level of an as-received sample. Four-point bending fatigue tests were performed for plate shape samples with a large cyclic strain range. The SAD value of the bending samples was also 4 deg in the damaged area where cracks already initiated at an early stage of the fatigue process. These test results indicate that the microstructural conditioning is a prerequisite for the fatigue crack initiation and propagation in SA508. These observations may lead to better under- standing of how fatigue initiation processes transit to cracks.

Effects of exercise-induced fatigue on postural balance: a comparison of treadmill versus cycle fatiguing protocols.

PubMed

Wright, Katherine E; Lyons, Thomas S; Navalta, James W

2013-05-01

The authors of this study examined the effects of muscle fatigue on balance indices and recovery time in recreationally trained individuals after incremental tests on a treadmill and a cycle ergometer. Sixteen participants (male N = 11, female N = 5) (mean age = 21.2 ± 2 years) completed this study. Balance measures were performed on a Biodex Balance System via the Dynamic Balance Test. Balance was measured pre-exercise, immediately post-exercise, and at 3-, 6-, 9-, 12-, 15-, 18-, and 21-min post-exercise. Immediately following the fatiguing treadmill test, balance increased significantly in the overall stability index (SI) (from 4.38 ± 2.48 to 6.09 ± 1.80) and the anterior/posterior index (API) (from 3.49 ± 2.18 to 5.28 ± 1.81) (p < 0.01). Immediately following the fatiguing cycle test, balance was not altered significantly in SI or API. Balance was not altered significantly for the medial/lateral index for either exercise test at any time point. Additionally, there were no significant differences in time to recovery. At 12-min post-exercise, all indices were below pre-exercise values, indicating that fatiguing exercise has a positive effect on balance over time. These results are consistent with previous research, suggesting that any effects of fatigue on balance are seen immediately and are diminished as time after exercise increases.

Temperature dependence of liquid metal embrittlement susceptibility of a modified 9Cr-1Mo steel under low cycle fatigue in lead-bismuth eutectic at 160-450 °C

NASA Astrophysics Data System (ADS)

Gong, Xing; Marmy, Pierre; Qin, Ling; Verlinden, Bert; Wevers, Martine; Seefeldt, Marc

2016-01-01

Low cycle fatigue properties of a 9Cr-1Mo ferritic-martensitic steel (T91) have been tested in a low oxygen concentration (LOC) lead-bismuth eutectic (LBE) environment and in vacuum at 160-450 °C. The results show a clear fatigue endurance "trough" in LOC LBE, while no such a strong temperature dependence of the fatigue endurance is observed when the steel is tested in vacuum. The fractographic observations by means of scanning electron microscopy (SEM) show that ductile microdimples are prevalent on the fracture surfaces of the specimens tested in vacuum, whereas the fracture surfaces produced in LOC LBE at all the temperatures are characterized by quasi-cleavage. Interestingly, using electron backscatter diffraction (EBSD), martensitic laths close to the fatigue crack walls or to the fracture surfaces of the specimens tested in vacuum are found to have transformed into very fine equiaxed subgrains. Nevertheless, such microstructural modifications do not happen to the specimens tested in LOC LBE at 160-450 °C. These interesting microstructural distinctions indicate that liquid metal embrittlement (LME) is able to occur throughout the fatigue crack propagation phase in the full range of the temperatures investigated, i.e. LME is not very sensitive to temperature during the fatigue crack propagation.

Evaluation of Orientation Dependence of Fracture Toughness and Fatigue Crack Propagation Behavior of As-Deposited ARCAM EBM Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Seifi, Mohsen; Dahar, Matthew; Aman, Ron; Harrysson, Ola; Beuth, Jack; Lewandowski, John J.

2015-03-01

This preliminary work documents the effects of test orientation with respect to build and beam raster directions on the fracture toughness and fatigue crack growth behavior of as-deposited EBM Ti-6Al-4V. Although ASTM/ISO standards exist for determining the orientation dependence of various mechanical properties in both cast and wrought materials, these standards are evolving for materials produced via additive manufacturing (AM) techniques. The current work was conducted as part of a larger America Makes funded project to begin to examine the effects of process variables on the microstructure and fracture and fatigue behavior of AM Ti-6Al-4V. In the fatigue crack growth tests, the fatigue threshold, Paris law slope, and overload toughness were determined at different load ratios, R, whereas fatigue precracked samples were tested to determine the fracture toughness. The as-deposited material exhibited a fine-scale basket-weave microstructure throughout the build, and although fracture surface examination revealed the presence of unmelted powders, disbonded regions, and isolated porosity, the resulting mechanical properties were in the range of those reported for cast and wrought Ti-6Al-4V. Remote access and control of testing was also developed at Case Western Reserve University to improve efficiency of fatigue crack growth testing.

Spectrum fatigue testing of T-shaped tension clips

NASA Astrophysics Data System (ADS)

Palmberg, Bjoern; Wallstenius, Bengt

1992-12-01

An investigation of strain distributions during static loading and crack propagation and fatigue lives under spectrum loading of T-shaped tension clips was carried out. Three slightly different, with respect to geometry, T shaped tension clips made of aluminum alloy 7010-T73651 were studied. The type 1 and 4 test specimens were different only with respect to the web thickness of the clamping end. The type 1 and 2 test specimens were different with repect to milled flat circular countersink around the holes in the type 2 specimens and with respect to the radius between the web and foot. The spectrum fatigue loading consisted of a load sequence representative for the wing root, lower side, of a fighter aircraft. Tests were made at two different load levels for each specimen type. The strain measurements show that the countersink in the type 2 specimens increases the stresses in the fatigue critical region. This is also manifested in the spectrum fatigue life results, where type 2 specimens show the shortest fatigue lives. The strain measurements show that the torque used for the bolts in joining two test specimens or one test specimen and a dummy has a rather large impact on the strain in the fatigue region. The strains decrease with increasing torque. The spectrum fatigue loading resulted in approximately an equal number of flights to obtain a 10.0 mm crack for specimens of type 1 and 4. This suggests that the type 1 configuration is superior since the web thickness is smaller for this type as compared to the type 4 specimens. In other words, the type 4 specimens have an unnecessary oversize of the clamping end web thickness.

A comparison of reliability and conventional estimation of safe fatigue life and safe inspection intervals

NASA Technical Reports Server (NTRS)

Hooke, F. H.

1972-01-01

Both the conventional and reliability analyses for determining safe fatigue life are predicted on a population having a specified (usually log normal) distribution of life to collapse under a fatigue test load. Under a random service load spectrum, random occurrences of load larger than the fatigue test load may confront and cause collapse of structures which are weakened, though not yet to the fatigue test load. These collapses are included in reliability but excluded in conventional analysis. The theory of risk determination by each method is given, and several reasonably typical examples have been worked out, in which it transpires that if one excludes collapse through exceedance of the uncracked strength, the reliability and conventional analyses gave virtually identical probabilities of failure or survival.

Fatigue crack growth in 2024-T3 aluminum under tensile and transverse shear stresses

NASA Technical Reports Server (NTRS)

Viz, Mark J.; Zehnder, Alan T.

1994-01-01

The influence of transverse shear stresses on the fatigue crack growth rate in thin 2024-T3 aluminum alloy sheets is investigated experimentally. The tests are performed on double-edge cracked sheets in cyclic tensile and torsional loading. This loading generates crack tip stress intensity factors in the same ratio as the values computed for a crack lying along a lap joint in a pressurized aircraft fuselage. The relevant fracture mechanics of cracks in thin plates along with the details of the geometrically nonlinear finite element analyses used for the test specimen calibration are developed and discussed. Preliminary fatigue crack growth data correlated using the fully coupled stress intensity factor calibration are presented and compared with fatigue crack growth data from pure delta K(sub I)fatigue tests.

Elevated Temperature Fatigue Endurance of Three Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Verrilli, Michael J.

2007-01-01

High-cycle fatigue endurance of three candidate materials for the acoustic liners of the Enabling Propulsion Materials Nozzle Program was investigated. The ceramic matrix composite materials investigated were N720/AS (Nextel 720, 3M Corporation), Sylramic S200 (Dow Corning), and UT 22. High-cycle fatigue tests were conducted in air at 910 C on as-machined specimens and on specimens subjected to tensile cyclic load excursions every 160 hr followed by thermal exposure at 910 C in a furnace up to total exposure times of 2066 and 4000 hr. All the fatigue tests were conducted in air at 100 Hz with a servohydraulic test machine. In the as-machined condition, among the three materials investigated only the Sylramic S200 exhibited a deterministic type of high-cycle fatigue behavior. Both the N720/AS and UT-22 exhibited significant scatter in the experimentally observed high-cycle fatigue lives. Among the thermally exposed specimens, N720/AS and Sylramic S200 materials exhibited a reduction in the high-cycle fatigue lives, particularly at the exposure time of 4000 hr.

Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Hong, E-mail: wangh@ornl.gov; Lee, Sung-Min; Wang, James L.

Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10{sup 8} cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatiguemore » index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.« less

Measurement of fatigue in industries.

PubMed

Saito, K

1999-04-01

Fatigue of workers is a complex phenomenon resulting from various factors in technically innovated modern industries, and it appears as a feeling of exhaustion, lowering of physiological functions, breakdown of autonomic nervous balance, and decrease in work efficiency. On the other hand industrial fatigue is caused by excessive workload, remarkable alteration in working posture and diurnal and nocturnal rhythms in daily life. Working modes in modern industries have changed from work with the whole body into that with the hands, arms, legs and/or eyes which are parts of the body, and from physical work to mental work. Visual display terminal (VDT) work is one of the most characteristic jobs in the various kinds of workplaces. A large number of fatigue tests have already been adopted, but it is still hard to draw a generalized conclusion as to the method of selecting the most appropriate test battery for a given work load. As apparatus for fatigue measurement of VDT work we have developed VRT (Visual Reaction Test) and the Portable Fatigue Meter. Furthermore, we have presented immune parameters of peripheral blood and splenic T cells for physical fatigue.

Clinical, laboratory, and neuroimaging characteristics of fatigue in HIV-infected individuals.

PubMed

Schifitto, Giovanni; Deng, Lijuan; Yeh, Tzu-Min; Evans, Scott R; Ernst, Thomas; Zhong, Jianhui; Clifford, David

2011-02-01

Fatigue is among the most common symptoms reported by HIV-infected individuals. Previous reports suggest that the prevalence of fatigue varies by disease status with rates close to 80% in patients with AIDS. However, most studies have not been conducted in the setting of a controlled trial and have not assessed the association of fatigue with cellular markers of brain activity. Data for this study were derived from baseline and longitudinal evaluations in ACTG A5090, a randomized, double-blind, placebo-controlled trial of the Selegiline Transdermal System for the treatment of HIV-associated cognitive impairment. Fatigue was assessed using the Fatigue Severity Scale with scores of >4 considered "fatigued". Participants in a substudy underwent brain magnetic resonance spectroscopy (MRS) imaging, an in vivo method for assessing brain metabolites associated with neuronal and glia activity. Differences between fatigued and non-fatigued participants were evaluated with respect to demographics and clinical characteristics, plasma and CSF HIV-1 RNA concentration, CD4 counts, and brain metabolites. One hundred and twenty-eight participants were enrolled (88% male, median age = 45 years) and 82 participants (64%, 95% confidence interval 55%, 72%) were fatigued at baseline. MRS was conducted in 62 of the 128 participants. Fatigued participants were significantly younger (p = 0.011), had lower Karnofsky scores (p = 0.032), and had higher levels of depressive symptoms on the Center for Epidemiologic Studies Depression (CES-D) scale (p < 0.001) than non-fatigued participants. Statistically significant differences between fatigued and non-fatigued groups were not detected for plasma and CSF HIV-1RNA concentration, CD4 counts, or on neuropsychological tests. MRS revealed significantly lower levels of the cellular energy marker total creatine (p = 0.002) in the basal ganglia of fatigued participants. Statistically significant differences in other brain metabolites were not detected. Longitudinal data showed that fatigue persisted and worse fatigue at baseline was predictor of future fatigue. Among the cognitive tests, baseline Stroop score was associated with future fatigue. Fatigue was present in 64% of A5090 study participants and persisted during the 24 weeks of follow-up. Fatigue was associated with worse functional performance and depressive mood. Lower cellular energy levels in the basal ganglia, as measured by MRS total creatine concentration, suggest energy dysmetabolism in this brain region. This observation, taken together with the association between fatigue and neuropsychological tests of frontal lobe performance is consistent with the hypothesis of a striatal-cortical circuitry involvement in the symptoms of fatigue.

The Psychometric Properties of an Arabic version of the PedsQL Multidimensional Fatigue Scale Tested for Children with Cancer.

PubMed

Al-Gamal, Ekhlas; Long, Tony

2017-09-01

Fatigue is considered to be one of the most reported symptoms experienced by children with cancer. A major aim of this study was to develop an Arabic version of the Pediatric Quality of Life (PedsQL) Multidimensional Fatigue Scale (child report) and to test its psychometric proprieties for the assessment of fatigue in Arabic children with cancer. The PedsQL Multidimensional Fatigue Scale (Arabic version) and the PedsQL TM 4.0 Generic Core scale (existing Arabic version) were completed by 70 Jordanian children with cancer. Cronbach's alpha coefficients were found to be 0.90 for the total PedsQL Multidimensional Fatigue Scale (Arabic version), 0.94 for the general fatigue subscale, 0.67 for the sleep/rest fatigue subscale, and 0.87 for the cognitive fatigue subscale. The PedsQL Multidimensional Fatigue Scale scores correlated significantly with the PedsQL TM 4.0 Generic Core scale and demonstrated good construct validity. The results demonstrate excellent reliability and good validity of the PedsQL Multidimensional Fatigue Scale (Arabic version) for children with cancer. This is the first validated scale that assesses fatigue in Arabic children with cancer. The English scale has been used with several pediatric clinical populations, so this Arabic version may be equally useful beyond the field of cancer.

Biomechanical Study of the Fixation Strength of Anteromedial Plating for Humeral Shaft Fractures.

PubMed

Zheng, Yin-Feng; Zhou, Jun-Lin; Wang, Xiao-Hong; Shan, Lei; Liu, Yang

2016-08-05

Open reduction and internal fixation with plate and screws are the gold standard for the surgical treatment of humeral shaft fractures, this study was to compare the mechanical properties of anteromedial, anterolateral, and posterior plating for humeral shaft fractures. A distal third humeral shaft fracture model was constructed using fourth-generation sawbones (#3404, composite bone). A total of 24 sawbones with a distal third humeral shaft fracture was randomly divided into three Groups: A, B, and C (n = 8 in each group) for anteromedial, anterolateral, and posterior plating, respectively. All sawbones were subjected to horizontal torsional fatigue tests, horizontal torsional and axial compressive fatigue tests, four-point bending fatigue tests in anteroposterior (AP) and mediolateral (ML) directions and horizontal torsional destructive tests. In the horizontal torsional fatigue tests, the mean torsional angle amplitude in Groups A, B, and C were 6.12°, 6.53°, and 6.81°. In horizontal torsional and axial compressive fatigue tests, the mean torsional angle amplitude in Groups A, B, and C were 5.66°, 5.67°, and 6.36°. The mean plate displacement amplitude was 0.05 mm, 0.08 mm, and 0.10 mm. Group A was smaller than Group C (P < 0.05). In AP four-point bending fatigue tests, the mean plate displacement amplitude was 0.16 mm, 0.13 mm, and 0.20 mm. Group B was smaller than Group C (P < 0.05). In ML four-point bending fatigue tests, the mean plate displacement amplitude were 0.16 mm, 0.19 mm, and 0.17 mm. In horizontal torsional destructive tests, the mean torsional rigidity in Groups A, B, and C was 0.82, 0.75, and 0.76 N·m/deg. The yielding torsional angle was 24.50°, 25.70°, and 23.86°. The mean yielding torque was 18.46, 18.05, and 16.83 N·m, respectively. Anteromedial plating was superior to anterolateral or posterior plating in all mechanical tests except in AP four-point bending fatigue tests compared to the anterolateral plating group. We can suggest that anteromedial plating is a clinically safe and effective way for humeral shaft fractures.

Fatigue life characterization of Superpave mixtures at the Virginia Smart Road.

DOT National Transportation Integrated Search

2005-01-01

Laboratory fatigue testing was performed on six Superpave HMA mixtures in use at the Virginia Smart Road. Evaluation of the applied strain and resulting fatigue life was performed to fit regressions to predict the fatigue performance of each mixture....

Fatigue Life Methodology for Bonded Composite Skin/Stringer Configurations

NASA Technical Reports Server (NTRS)

Krueger, Ronald; Paris, Isabelle L.; OBrien, T. Kevin

2000-01-01

A methodology is presented for determining the fatigue life of bonded composite skin/stringer structures based on delamination fatigue characterization data and geometric nonlinear finite element analyses. Results were compared to fatigue tests on stringer flange/skin specimens to verify the approach.

Effect of carbide distribution on rolling-element fatigue life of AMS 5749

NASA Technical Reports Server (NTRS)

Parker, R. J.; Bamberger, E. N.

1983-01-01

Endurance tests with ball bearings made of corrosion resistant bearing steel which resulted in fatigue lives much lower than were predicted are discussed. Metallurgical analysis revealed an undesirable carbide distribution in the races. It was shown in accelerated fatigue tests in the RC rig that large, banded carbides can reduce rolling element fatigue life by a factor of approximately four. The early spalling failures on the bearing raceways are attributed to the large carbide size and banded distribution.

Corrosion fatigue of 2219-T87 aluminum alloy

NASA Technical Reports Server (NTRS)

Mcmillan, V. C.

1986-01-01

Corrosion fatigue studies were conducted on bare, chemical conversion coated, and anodized 2219-T87 aluminum alloy. These tests were performed using a rotating beam machine running at a velocity of 2500 rpm. The corrosive environments tested were distilled water, 100 ppm NaCl, and 3.5 percent NaCl. Results were compared to the endurance limit in air. An evaluation of the effect of protective coatings on corrosion fatigue was made by comparing the fatigue properties of specimens with coatings to those without.

Characterization and Modeling of Asphalt Binder Fatigue

NASA Astrophysics Data System (ADS)

Safaei, Farinaz

Fatigue cracking is a primary distress in asphalt pavements caused by the accumulation of damage under repeated traffic loading. Many factors influence fatigue damage in pavements, including pavement structure, environmental conditions, and asphalt mixture volumetric properties. Asphalt binder is the weakest asphalt concrete constituent and, thus, plays a critical role in determining the fatigue resistance of pavements. Therefore, the ability to characterize and model the inherent fatigue performance of an asphalt binder is a necessary first step to design. A comprehensive understanding and prediction of asphalt binder fatigue performance require a suitable experiment coupled with a model to predict how the binder will perform under various traffic, temperature, and structural conditions encountered in the field. The simplified viscoelastic continuum damage (S-VECD) model has been used successfully by researchers to predict the damage evolution in asphalt mixtures for various traffic and climatic conditions using limited uniaxial test data. Although the literature shows promise for applying VECD modeling to asphalt binder fatigue, the past efforts have several shortcomings. It has been demonstrated that flow and adhesion loss can impede DSR fatigue test results. Thus, definition of test conditions (e.g., temperature) where cyclic DSR tests are appropriate for fatigue characterization of binders is necessary. In addition, the applicability of the model to predict fatigue performance under varying loading and thermal history has not been rigorously evaluated. Furthermore, the effects of material nonlinearity have been largely neglected in past modeling efforts for simplicity. In addition, past efforts have employed the parallel plate DSR geometry for the fatigue characterization of asphalt binders. In the parallel plate geometry, the strain depends on the radial distance from the specimen center. Therefore, the material will fail at different rates as a function of radial location. Past efforts have neglected the radial strain gradient, using the apparent shear stress at the sample edge to infer fatigue damage and derive S-VECD model parameters. Apparent edge stress is calculated using linear mapping to the total torque, which is erroneous in the presence of material or geometric nonlinearities (such as cracking). This study seeks to overcome the aforementioned shortcomings of past efforts to improve the ability to characterize and predict asphalt binder fatigue.

Fatigue Life of Titanium Alloys Fabricated by Additive Layer Manufacturing Techniques for Dental Implants

NASA Astrophysics Data System (ADS)

Chan, Kwai S.; Koike, Marie; Mason, Robert L.; Okabe, Toru

2013-02-01

Additive layer deposition techniques such as electron beam melting (EBM) and laser beam melting (LBM) have been utilized to fabricate rectangular plates of Ti-6Al-4V with extra low interstitial (ELI) contents. The layer-by-layer deposition techniques resulted in plates that have different surface finishes which can impact significantly on the fatigue life by providing potential sites for fatigue cracks to initiate. The fatigue life of Ti-6Al-4V ELI alloys fabricated by EBM and LBM deposition techniques was investigated by three-point testing of rectangular beams of as-fabricated and electro-discharge machined surfaces under stress-controlled conditions at 10 Hz until complete fracture. Fatigue life tests were also performed on rolled plates of Ti-6Al-4V ELI, regular Ti-6Al-4V, and CP Ti as controls. Fatigue surfaces were characterized by scanning electron microscopy to identify the crack initiation site in the various types of specimen surfaces. The fatigue life data were analyzed statistically using both analysis of variance techniques and the Kaplan-Meier survival analysis method with the Gehan-Breslow test. The results indicate that the LBM Ti-6Al-4V ELI material exhibits a longer fatigue life than the EBM counterpart and CP Ti, but a shorter fatigue life compared to rolled Ti-6Al-4V ELI. The difference in the fatigue life behavior may be largely attributed to the presence of rough surface features that act as fatigue crack initiation sites in the EBM material.

Physical fitness and physical activity in fatigued and non-fatigued inflammatory bowel disease patients.

PubMed

Vogelaar, Lauran; van den Berg-Emons, Rita; Bussmann, Hans; Rozenberg, Robert; Timman, Reinier; van der Woude, Christien J

2015-01-01

To assess physical fitness and physical activity in inflammatory bowel disease (IBD) patients and whether fatigue is associated with impaired physical fitness and impaired physical activity. Ten patients with quiescent IBD and fatigue (fatigue group [FG]) based on the Checklist Individual Strength-Fatigue score of ≥35 were matched for age (±5 years) and sex with a non-fatigue group (NFG) with IBD. Physical fitness was measured with a cyclo-ergometric-based maximal exercise test, a submaximal 6-min walk test, and a dynamometer test to quantify the isokinetic muscle strength of the knee extensors and flexors. Level of physical activity was measured with an accelerometer-based activity monitor. The patients in both groups did not differ in regard to medication use, clinical characteristics, and body composition. However, medium-to-large effect sizes for impaired physical fitness (both cardiorespiratory fitness and muscle strength) and physical activity were seen between the patients in the FG and the NFG. Especially, intensity of physical activity was significantly lower in the FG patients compared with the NFG patients (effect size: 1.02; p = 0.037). Similar results were seen when outcomes of the FG and NFG were compared with reference values of the normal population. Fatigued IBD patients show an impaired physical fitness and physical activity compared with non-fatigued IBD patients. This gives directions for a physical component in fatigue in IBD patients. Therefore, these new insights into fatigue indicate that these patients might benefit from an exercise program to improve physical fitness and physical activity.

The role of insomnia in the treatment of chronic fatigue.

PubMed

Kallestad, Håvard; Jacobsen, Henrik B; Landrø, Nils Inge; Borchgrevink, Petter C; Stiles, Tore C

2015-05-01

The definition of Chronic Fatigue Syndrome (CFS) overlaps with definitions of insomnia, but there is limited knowledge about the role of insomnia in the treatment of chronic fatigue. To test if improvement of insomnia during treatment of chronic fatigue was associated with improved outcomes on 1) fatigue and 2) cortisol recovery span during a standardized stress exposure. Patients (n = 122) with chronic fatigue received a 3.5-week inpatient return-to-work rehabilitation program based on Acceptance and Commitment Therapy, and had been on paid sick leave>8 weeks due their condition. A physician and a psychologist examined the patients, assessed medication use, and SCID-I diagnoses. Patients completed self-report questionnaires measuring fatigue, pain, depression, anxiety, and insomnia before and after treatment. A subgroup (n = 25) also completed the Trier Social Stress Test for Groups (TSST-G) before and after treatment. Seven cortisol samples were collected during each test and cortisol spans for the TSST-G were calculated. A hierarchical regression analysis in nine steps showed that insomnia improvement predicted improvement in fatigue, independently of age, gender, improvement in pain intensity, depression and anxiety. A second hierarchical regression analysis showed that improvement in insomnia significantly predicted the cortisol recovery span after the TSST-G independently of improvement in fatigue. Improvement in insomnia severity had a significant impact on both improvement in fatigue and the ability to recover from a stressful situation. Insomnia severity may be a maintaining factor in chronic fatigue and specifically targeting this in treatment could increase treatment response. Copyright © 2014. Published by Elsevier Inc.

The Effect of Hole Quality on the Fatigue Life of 2024-T3 Aluminum Alloy Sheet

NASA Technical Reports Server (NTRS)

Everett, Richard A., Jr.

2004-01-01

This paper presents the results of a study whose main objective was to determine which type of fabrication process would least affect the fatigue life of an open-hole structural detail. Since the open-hole detail is often the fundamental building block for determining the stress concentration of built-up structural parts, it is important to understand any factor that can affect the fatigue life of an open hole. A test program of constant-amplitude fatigue tests was conducted on five different sets of test specimens each made using a different hole fabrication process. Three of the sets used different mechanical drilling procedures while a fourth and fifth set were mechanically drilled and then chemically polished. Two sets of specimens were also tested under spectrum loading to aid in understanding the effects of residual compressive stresses on fatigue life. Three conclusions were made from this study. One, the residual compressive stresses caused by the hole-drilling process increased the fatigue life by two to three times over specimens that were chemically polished after the holes were drilled. Second, the chemical polishing process does not appear to adversely affect the fatigue life. Third, the chemical polishing process will produce a stress-state adjacent to the hole that has insignificant machining residual stresses.

Mental Fatigue and Physical and Cognitive Performance During a 2-Bout Exercise Test.

PubMed

Vrijkotte, Susan; Meeusen, Romain; Vandervaeren, Cloe; Buyse, Luk; Cutsem, Jeroen van; Pattyn, Nathalie; Roelands, Bart

2018-04-01

The 2-bout exercise protocol has been developed to diagnose nonfunctional overreaching and the "overtraining syndrome." It consists of 2 maximal exercise bouts separated by 4 hours. Mental fatigue negatively influences performance, but the effects of its occurrence during the 2-bout exercise protocol have never been investigated. The aim of this study was to examine whether mental fatigue (induced during the rest period) influences physical and cognitive performance during/after the second exercise bout of the 2-bout exercise protocol. Nine healthy, well-trained male cyclists participated in a single-blind, randomized, placebo-controlled crossover study. The intervention consisted of either 1.5-hour rest (control) or performing a computer-based Stroop task to induce mental fatigue. Cognitive (Eriksen Flanker task), physiological (lactate, maximum heart rate, and maximum wattage), and subjective data (mental fatigue-visual analog scale, Profile of Mood States, and rating of perceived exertion) were gathered. Ratings of fatigue, tension, and mental fatigue were affected in the mental fatigue condition (P < .05). Neither physiological nor cognitive differences were found between conditions. Ratings of mental fatigue were already affected after the first maximum exercise test (P < .05). Neither physical nor cognitive performance was affected by mental fatigue, but subjective ratings did reveal significant differences. It is recommended to exclude mentally challenging tasks during the 2-bout exercise protocol rest period to ascertain unaffected subjective test results. This study should be repeated in athletes diagnosed with nonfunctional overreaching/overtraining syndrome.

Literature review : an analysis of laboratory fatigue tests.

DOT National Transportation Integrated Search

1975-01-01

This report discusses the various types of fatigue tests, grouped by the type of specimen (beam, plate, Marshall, etc.) used. The discussion under each type of specimen covers the test, and the analytical methods used in evaluating the data. The test...

Clinical, laboratory, and neuroimaging characteristics of fatigue in HIV-infected individuals

PubMed Central

Schifitto, Giovanni; Deng, Lijuan; Yeh, Tzu-min; Evans, Scott R.; Ernst, Thomas; Zhong, Jianhui; Clifford, David

2011-01-01

Fatigue is among the most common symptoms reported by HIV-infected individuals. Previous reports suggest that the prevalence of fatigue varies by disease status with rates close to 80% in patients with AIDS. However, most studies have not been conducted in the setting of a controlled trial and have not assessed the association of fatigue with cellular markers of brain activity. Data for this study were derived from baseline and longitudinal evaluations in ACTG A5090, a randomized, double-blind, placebo-controlled trial of the Selegiline Transdermal System for the treatment of HIV-associated cognitive impairment. Fatigue was assessed using the Fatigue Severity Scale with scores of >4 considered “fatigued”. Participants in a substudy underwent brain magnetic resonance spectroscopy (MRS) imaging, an in vivo method for assessing brain metabolites associated with neuronal and glia activity. Differences between fatigued and non-fatigued participants were evaluated with respect to demographics and clinical characteristics, plasma and CSF HIV-1 RNA concentration, CD4 counts, and brain metabolites. One hundred and twenty-eight participants were enrolled (88% male, median age=45 years) and 82 participants (64%, 95% confidence interval 55%, 72%) were fatigued at baseline. MRS was conducted in 62 of the 128 participants. Fatigued participants were significantly younger (p=0.011), had lower Karnofsky scores (p=0.032), and had higher levels of depressive symptoms on the Center for Epidemiologic Studies Depression (CES-D) scale (p<0.001) than non-fatigued participants. Statistically significant differences between fatigued and non-fatigued groups were not detected for plasma and CSF HIV-1RNA concentration, CD4 counts, or on neuropsychological tests. MRS revealed significantly lower levels of the cellular energy marker total creatine (p=0.002) in the basal ganglia of fatigued participants. Statistically significant differences in other brain metabolites were not detected. Longitudinal data showed that fatigue persisted and worse fatigue at baseline was predictor of future fatigue. Among the cognitive tests, baseline Stroop score was associated with future fatigue. Fatigue was present in 64% of A5090 study participants and persisted during the 24 weeks of follow-up. Fatigue was associated with worse functional performance and depressive mood. Lower cellular energy levels in the basal ganglia, as measured by MRS total creatine concentration, suggest energy dysmetabolism in this brain region. This observation, taken together with the association between fatigue and neuropsychological tests of frontal lobe performance is consistent with the hypothesis of a striatal–cortical circuitry involvement in the symptoms of fatigue. PMID:21181521

Preliminary metallographic studies of ball fatigue under rolling-contact conditions

NASA Technical Reports Server (NTRS)

Bear, H Robert; Butler, Robert H

1957-01-01

The metallurgical results produced on balls tested in the rolling-contact fatigue spin rig were studied by metallographic examination. Origin and progression of fatigue failures were observed. These evaluations were made on SAE 52100 and AISI M-1 balls fatigue tested at room temperature (80 F) and 200 to 250 F. Most failures originated subsurface in shear; inclusions, structure changes, and directionalism adversely affected ball fatigue life. Structures in the maximum-shear-stress region of the balls of both materials were stable at room temperature and unstable at 200 to 250 F. Failures were of the same type as those found in full-scale bearings.

Fatigue of DIN 1.4914 martensitic stainless steel in a hydrogen environment

NASA Astrophysics Data System (ADS)

Shakib, J. I.; Ullmaier, H.; Little, E. A.; Faulkner, R. G.; Schmilz, W.; Chung, T. E.

1994-09-01

Fatigue tests at room temperature in vacuum, air and hydrogen have been carried out on specimens of DIN 1.4914 martensitic stainless steel in load-controlled, push-pull type experiments. Fatigue lifetimes in hydrogen are significantly lower than in both vacuum and air and the degradation is enhanced by lowering the test frequency or introducing hold times into the tension half-cycle. Fractographic examinations reveal hydrogen embrittlement effects in the form of internal cracking between fatigue striations together with surface modifications, particularly at low stress amplitudes. It is suggested that gaseous hydrogen can influence both fatigue crack initiation and propagation events in martensitic steels.

Tensile and fatigue behavior of tungsten/copper composites

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Gabb, Timothy P.; Kim, Y. S.

1989-01-01

Work on W/Cu unidirectional composites was initiated to study the behavior of this ductile-ductile composite system under thermomechanical fatigue and to examine the applicability of fatigue-life prediction methods for thermomechanical fatigue of this metal matrix composite. The first step was to characterize the tensile behavior of four ply, 10 vol. percent W/Cu plates at room and elevated temperatures. Fatigue tests were conducted in load control on 0 degree specimens at 260 C. The maximum cyclic stress was varied but the minimum cyclic stress was kept constant. All tests were performed in vacuum. The strain at failure increased with increasing maximum cyclic stress.

The Effect of Moderate and High-Intensity Fatigue on Groundstroke Accuracy in Expert and Non-Expert Tennis Players

PubMed Central

Lyons, Mark; Al-Nakeeb, Yahya; Hankey, Joanne; Nevill, Alan

2013-01-01

Exploring the effects of fatigue on skilled performance in tennis presents a significant challenge to the researcher with respect to ecological validity. This study examined the effects of moderate and high-intensity fatigue on groundstroke accuracy in expert and non-expert tennis players. The research also explored whether the effects of fatigue are the same regardless of gender and player’s achievement motivation characteristics. 13 expert (7 male, 6 female) and 17 non-expert (13 male, 4 female) tennis players participated in the study. Groundstroke accuracy was assessed using the modified Loughborough Tennis Skills Test. Fatigue was induced using the Loughborough Intermittent Tennis Test with moderate (70%) and high-intensities (90%) set as a percentage of peak heart rate (attained during a tennis-specific maximal hitting sprint test). Ratings of perceived exertion were used as an adjunct to the monitoring of heart rate. Achievement goal indicators for each player were assessed using the 2 x 2 Achievement Goals Questionnaire for Sport in an effort to examine if this personality characteristic provides insight into how players perform under moderate and high-intensity fatigue conditions. A series of mixed ANOVA’s revealed significant fatigue effects on groundstroke accuracy regardless of expertise. The expert players however, maintained better groundstroke accuracy across all conditions compared to the novice players. Nevertheless, in both groups, performance following high-intensity fatigue deteriorated compared to performance at rest and performance while moderately fatigued. Groundstroke accuracy under moderate levels of fatigue was equivalent to that at rest. Fatigue effects were also similar regardless of gender. No fatigue by expertise, or fatigue by gender interactions were found. Fatigue effects were also equivalent regardless of player’s achievement goal indicators. Future research is required to explore the effects of fatigue on performance in tennis using ecologically valid designs that mimic more closely the demands of match play. Key Points Groundstroke accuracy under moderate-intensity fatigue is equivalent to performance at rest. Groundstroke accuracy declines significantly in both expert (40.3% decline) and non-expert (49.6%) tennis players following high-intensity fatigue. Expert players are more consistent, hit more accurate shots and fewer out shots across all fatigue intensities. The effects of fatigue on groundstroke accuracy are the same regardless of gender and player’s achievement goal indicators. PMID:24149809

Increased Surface Fatigue Lives of Spur Gears by Application of a Coating

NASA Technical Reports Server (NTRS)

Krantz, Timothy L.; Cooper, Clark V.; Townsend, Dennis P.; Hansen, Bruce D.

2003-01-01

Hard coatings have potential for increasing gear surface fatigue lives. Experiments were conducted using gears both with and without a metal-containing, carbonbased coating. The gears were case-carburized AISI 9310 steel spur gears. Some gears were provided with the coating by magnetron sputtering. Lives were evaluated by accelerated life tests. For uncoated gears, all of fifteen tests resulted in fatigue failure before completing 275 million revolutions. For coated gears, eleven of the fourteen tests were suspended with no fatigue failure after 275 million revolutions. The improved life owing to the coating, approximately a six-fold increase, was a statistically significant result.

Structural Area Inspection Frequency Evaluation (SAIFE). Volume III. Demonstration Input, Inspection Survey, and MRR Data

DTIC Science & Technology

1978-04-01

3 1.7 Production Rate Change Time . . . . 3 1.8 Time of Fatigue Test Start . ..... 3 1.9 Fatigue Test Acceleration Factor . 3 1.10 Corrosion...simulation logic. SAIFE accounts for the following factors : (1) aircraft design analysis; (2) component and full-scale fatigue testing; (3) production ...reliability; production , servi ce,Information Service, Springfield, and corrosion defects; crack or corrosi on Virginia 22151 detection probability; crack

Mode 2 fatigue crack growth specimen development

NASA Technical Reports Server (NTRS)

Buzzard, R. J.; Gross, B.; Srawley, J. E.

1983-01-01

A Mode II test specimen was developed which has potential application in understanding phemonena associated with mixed mode fatigue failures in high performance aircraft engine bearing races. The attributes of the specimen are: it contains one single ended notch, which simplifiers data gathering and reduction; the fatigue crack grous in-line with the direction of load application; a single axis test machine is sufficient to perform testing; and the Mode I component is vanishingly small.

Fatigue Testing of Maglev-Hybrid Box Beam

DTIC Science & Technology

2009-03-02

04142009 3. DATES COVERED: (From - To) 23052006-14092008 4. TITLE AND SUBTITLE Fatigue Testing of Maglev -Hybrid Box Beam 5a. CONTRACT NUMBER NA...was previously built under collaboration between Maglev Inc. and Lehigh University. The girder was instrumented with strain gages and LVDT’s to monitor...report March 2,2009 Contract N00014-06-1-0872 Project: Fatigue Testing of Maglev -Hybrid Box Beam Prepared by Dr. J.L. Grenestedt and Dr. R. Sause

Experimental and theoretical investigation of fatigue life in reusable rocket thrust chambers

NASA Technical Reports Server (NTRS)

Hannum, N. P.; Kasper, H. J.; Pavli, A. J.

1976-01-01

During a test program to investigate low-cycle thermal fatigue, 13 rocket combustion chambers were fabricated and cyclically test fired to failure. Six oxygen-free, high-conductivity (OFHC) copper and seven Amzirc chambers were tested. The failures in the OFHC copper chambers were not typical fatigue failures but are described as creep rupture enhanced by ratcheting. The coolant channels bulged toward the chamber centerline, resulting in progressive thinning of the wall during each cycle. The failures in the Amzirc alloy chambers were caused by low-cycle thermal fatigue. The zirconium in this alloy was not evenly distributed in the chamber materials. The life that was achieved was nominally the same as would have been predicted from OFHC copper isothermal test data.

Reliability aspects of a composite bolted scarf joint. [in wing skin splice

NASA Technical Reports Server (NTRS)

Reed, D. L.; Eisenmann, J. R.

1975-01-01

The design, fabrication, static test, and fatigue test of both tension and compression graphite-epoxy candidates for a wing splice representative of a next-generation transport aircraft was the objective of the reported research program. A single-scarf bolted joint was selected as the design concept. Test specimens were designed and fabricated to represent an upper-surface and a lower-surface panel containing the splice. The load spectrum was a flight-by-flight random-load history including ground-air-ground loads. The results of the fatigue testing indicate that, for this type of joint, the inherent fatigue resistance of the laminate is reflected in the joint behavior and, consequently, the rate of damage accumulation is very slow under realistic fatigue loadings.

Cyclic Fatigue Resistance of Novel Rotary Files Manufactured from Different Thermal Treated Nickel-Titanium Wires in Artificial Canals.

PubMed

Karataşlıoglu, E; Aydın, U; Yıldırım, C

2018-02-01

The aim of this in vitro study was to compare the static cyclic fatigue resistance of thermal treated rotary files with a conventional nickel-titanium (NiTi) rotary file. Four groups of 60 rotary files with similar file dimensions, geometries, and motion were selected. Groups were set as HyFlex Group [controlled memory wire (CM-Wire)], ProfileVortex Group (M-Wire), Twisted File Group (R-Phase Wire), and OneShape Group (conventional NiTi wire)] and tested using a custom-made static cyclic fatigue testing apparatus. The fracture time and fragment length of the each file was also recorded. Statistical analysis was performed using one-way analysis of variance and Tukey's test at the 95% confidence level (P = 0.05). The HyFlex group had a significantly higher mean cyclic fatigue resistance than the other three groups (P < 0.001). The OneShape groups had the least fatigue resistance. CM-Wire alloy represented the best performance in cyclic fatigue resistance, and NiTi alloy in R-Phase had the second highest fatigue resistance. CM and R-Phase manufacturing technology processed to the conventional NiTi alloy enhance the cyclic fatigue resistance of files that have similar design and size. M-wire alloy did not show any superiority in cyclic fatigue resistance when compared with conventional NiTi wire.

Mechanical degradation of fuel cell membranes under fatigue fracture tests

NASA Astrophysics Data System (ADS)

Khorasany, Ramin M. H.; Sadeghi Alavijeh, Alireza; Kjeang, Erik; Wang, G. G.; Rajapakse, R. K. N. D.

2015-01-01

The effects of cyclic stresses on the fatigue and mechanical stability of perfluorosulfonic acid (PFSA) membranes are experimentally investigated under standard fuel cell conditions. The experiments are conducted ex-situ by subjecting membrane specimens to cyclic uniaxial tension at controlled temperature and relative humidity. The fatigue lifetime is measured in terms of the number of cycles until ultimate fracture. The results indicate that the membrane fatigue lifetime is a strong function of the applied stress, temperature, and relative humidity. The fatigue life increases exponentially with reduced stresses in all cases. The effect of temperature is found to be more significant than that of humidity, with reduced fatigue life at high temperatures. The maximum membrane strain at fracture is determined to decrease exponentially with increasing membrane lifetime. At a given fatigue life, a membrane exposed to fuel cell conditions is shown to accommodate more plastic strain before fracture than one exposed to room conditions. Overall, the proposed ex-situ membrane fatigue experiment can be utilized to benchmark the fatigue lifetime of new materials in a fraction of the time and cost associated with conventional in-situ accelerated stress testing methods.

Reproducibility of the spectral components of the electroencephalogram during driver fatigue.

PubMed

Lal, Saroj K L; Craig, Ashley

2005-02-01

To date, no study has tested the reproducibility of EEG changes that occur during driver fatigue. For the EEG changes to be useful in the development of a fatigue countermeasure device the EEG response during each onset period of fatigue in individuals needs to be reproducible. It should be noted that fatigue during driving is not a continuous process but consists of successive episodes of 'microsleeps' where the subject may go in and out of a fatigue state. The aim of the present study was to investigate the reproducibility of fatigue during driving in both professional and non-professional drivers. Thirty five non-professional drivers and twenty professional drivers were tested during two separate sessions of a driver simulator task. EEG, EOG and behavioural measurements of fatigue were obtained during the driving task. The results showed high reproducibility for the delta and theta bands (r>0.95) in both groups of drivers. The results are discussed in light of implications for future studies and for the development of an EEG based fatigue countermeasure device.

Synergistic Effects of Frequency and Temperature on Damage Evolution and Life Prediction of Cross-Ply Ceramic Matrix Composites under Tension-Tension Fatigue Loading

NASA Astrophysics Data System (ADS)

Longbiao, Li

2017-10-01

In this paper, the synergistic effects of loading frequency and testing temperature on the fatigue damage evolution and life prediction of cross-ply SiC/MAS ceramic-matrix composite have been investigated. The damage parameters of the fatigue hysteresis modulus, fatigue hysteresis dissipated energy and the interface shear stress were used to monitor the damage evolution inside of SiC/MAS composite. The evolution of fatigue hysteresis dissipated energy, the interface shear stress and broken fibers fraction versus cycle number, and the fatigue life S-N curves of SiC/MAS composite under the loading frequency of 1 and 10 Hz at 566 °C and 1093 °C in air condition have been predicted. The synergistic effects of the loading frequency and testing temperature on the degradation rate of fatigue hysteresis dissipated energy and the interface shear stress have been analyzed.

Machining of Aircraft Titanium with Abrasive-Waterjets for Fatigue Critical Applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liu, H. T.; Hovanski, Yuri; Dahl, Michael E.

2012-02-01

Laboratory tests were conducted to determine the fatigue performance of abrasive-waterjet- (AWJ-) machined aircraft titanium. Dog-bone specimens machined with AWJs were prepared and tested with and without sanding and dry-grit blasting with Al2O3 as secondary processes. The secondary processes were applied to remove the visual appearance of AWJ-generated striations and to clean up the garnet embedment. The fatigue performance of AWJ-machined specimens was compared with baseline specimens machined with CNC milling. Fatigue test results of the titanium specimens not only confirmed our previous findings in aluminum dog-bone specimens but in comparison also further enhanced the fatigue performance of the titanium.more » In addition, titanium is known to be difficult to cut, particularly for thick parts, however AWJs cut the material 34% faster han stainless steel. AWJ cutting and dry-grit blasting are shown to be a preferred ombination for processing aircraft titanium that is fatigue critical.« less

The characterization of widespread fatigue damage in fuselage structure

NASA Technical Reports Server (NTRS)

Piascik, Robert S.; Willard, Scott A.; Miller, Matthew

1994-01-01

The characteristics of widespread fatigue damage (WSFD) in fuselage riveted structure were established by detailed nondestructive and destructive examinations of fatigue damage contained in a full size fuselage test article. The objectives of this were to establish an experimental data base for validating emerging WSFD analytical prediction methodology and to identify first order effects that contribute to fatigue crack initiation and growth. Detailed examinations were performed on a test panel containing four bays of a riveted lap splice joint. The panel was removed from a full scale fuselage test article after receiving 60,000 full pressurization cycles. The results of in situ examinations document the progression of fuselage skin fatigue crack growth through crack linkup. Detailed tear down examinations and fractography of the lap splice joint region revealed fatigue crack initiation sites, crack morphology, and crack linkup geometry. From this large data base, distributions of crack size and locations are presented and discussions of operative damage mechanisms are offered.

The characterization of widespread fatigue damage in fuselage structure

NASA Technical Reports Server (NTRS)

Piascik, Robert S.; Willard, Scott A.; Miller, Matthew

1994-01-01

The characteristics of widespread fatigue damage (WSFD) in fuselage riveted structure were established by detailed nondestructive and destructive examinations of fatigue damage contained in a full size fuselage test article. The objectives of this work were to establish an experimental data base for validating emerging WSFD analytical prediction methodology and to identify first order effects that contribute to fatigue crack initiation and growth. Detailed examinations were performed on a test panel containing four bays of a riveted lap splice joint. The panel was removed from a full scale fuselage test article after receiving 60,000 full pressurization cycles. The results of in situ examinations document the progression of fuselage skin fatigue crack growth through crack linkup. Detailed tear down examinations and fractography of the lap splice joint region revealed fatigue crack initiation sites, crack morphology and crack linkup geometry. From this large data base, distributions of crack size and locations are presented and discussions of operative damage mechanisms are offered.

Fatigue after stroke: the development and evaluation of a case definition.

PubMed

Lynch, Joanna; Mead, Gillian; Greig, Carolyn; Young, Archie; Lewis, Susan; Sharpe, Michael

2007-11-01

While fatigue after stroke is a common problem, it has no generally accepted definition. Our aim was to develop a case definition for post-stroke fatigue and to test its psychometric properties. A case definition with face validity and an associated structured interview was constructed. After initial piloting, the feasibility, reliability (test-retest and inter-rater) and concurrent validity (in relation to four fatigue severity scales) were determined in 55 patients with stroke. All participating patients provided satisfactory answers to all the case definition probe questions demonstrating its feasibility For test-retest reliability, kappa was 0.78 (95% CI, 0.57-0.94, P<.01) and for inter-rater reliability kappa was 0.80 (95% CI, 0.62-0.99, P<.01). Patients fulfilling the case definition also had substantially higher fatigue scores on four fatigue severity scales (P<.001) indicating concurrent validity. The proposed case definition is feasible to administer and reliable in practice, and there is evidence of concurrent validity. It requires further evaluation in different settings.

A comparison of cognitive performance decreases during acute, progressive fatigue arising from different concurrent stressors.

PubMed

Fogt, Donovan L; Kalns, John E; Michael, Darren J

2010-12-01

Fatigue is known to impair cognitive performance, but it remains unclear whether concurrent common stressors affect cognitive performance similarly. We used the Stroop Color-Word Conflict Test to assess cognitive performance over 24 hours for four groups: control, sleep-deprived (SD), SD + energy deficit, and SD + energy deficit + fluid restricted. Fatigue levels were quantified using the Profile of Mood States (POMS) survey. Linear mixed-effects (LME) models allowed for testing of group-specific differences in cognitive performance while accounting for subject-level variation. Starting fatigue levels were similar among all groups, while 24-hour fatigue levels differed significantly. For each cognitive performance test, results were modeled separately. The simplest LME model contained a significant fixed-effects term for slope and intercept. Moreover, the simplest LME model used a single slope coefficient to fit data from all four groups, suggesting that loss in cognitive performance over a 24-hour duty cycle with respect to fatigue level is similar regardless of the cause.

Effects of the Electron Beam Welding Process on the Microstructure, Tensile, Fatigue and Fracture Properties of Nickel Alloy Nimonic 80A

NASA Astrophysics Data System (ADS)

Zhang, H.; Huang, Chongxiang; Guan, Zhongwei; Li, Jiukai; Liu, Yongjie; Chen, Ronghua; Wang, Qingyuan

2018-01-01

The purpose of this study was to evaluate rotary bending high-cycle fatigue properties and crack growth of Nimonic 80A-based metal and electron beam-welded joints. All the tests were performed at room temperature. Fracture surfaces under high-cycle fatigue and fatigue crack growth were observed by scanning electron microscopy. Microstructure, hardness and tensile properties were also evaluated in order to understand the effects on the fatigue results obtained. It was found that the tensile properties, hardness and high-cycle fatigue properties of the welded joint are lower than the base metal. The fracture surface of the high-cycle fatigue shows that fatigue crack initiated from the surface under the high stress amplitude and from the subsurface under the low stress amplitude. The effect of the welding process on the statistical fatigue data was studied with a special focus on probabilistic life prediction and probabilistic lifetime limits. The fatigue crack growth rate versus stress intensity factor range data were obtained from the fatigue crack growth tests. From the results, it was evident that the fatigue crack growth rates of the welded are higher than the base metal. The mechanisms and fracture modes of fatigue crack growth of welded specimens were found to be related to the stress intensity factor range ΔK. In addition, the effective fatigue crack propagation thresholds and mismatch of welded joints were described and discussed.

Performance Demands in Softball Pitching: A Comprehensive Muscle Fatigue Study.

PubMed

Corben, Jeffrey S; Cerrone, Sara A; Soviero, Julie E; Kwiecien, Susan Y; Nicholas, Stephen J; McHugh, Malachy P

2015-08-01

Monitoring pitch count is standard practice in minor league baseball but not in softball because of the perception that fast-pitch softball pitching is a less stressful motion. To examine muscle fatigue after fast-pitch softball performances to provide an assessment of performance demand. Descriptive laboratory study. Bilateral strength measurements (handheld dynamometer) were made on 19 female softball pitchers (mean age [±SD], 15.2 ± 1.2 years) before and after pitching a game (mean number of pitches, 99 ± 21; mean innings pitched, 5 ± 1). A total of 20 tests were performed on the dominant and nondominant sides: forearm (grip, wrist flexion/extension, pronation/supination, elbow flexion/extension), shoulder (flexion, abduction/adduction, external/internal rotation, empty can test), scapula (middle/lower trapezius, rhomboid), and hip (hip flexion/extension, abduction/adduction). Fatigue (percentage strength loss) was categorized based on bilateral versus unilateral presentation using paired t tests: bilateral symmetric (significant on dominant and nondominant and not different between sides), bilateral asymmetric (significant on dominant and nondominant but significantly greater on dominant), unilateral asymmetric (significant on dominant only and significantly greater than nondominant), or unilateral equivocal (significant on dominant only but not different from nondominant). Bilateral symmetric fatigue was evident for all hip (dominant, 19.3%; nondominant, 15.2%) and scapular tests (dominant, 19.2%; nondominant, 19.3%). In general, shoulder tests exhibited bilateral asymmetric fatigue (dominant, 16.9%; nondominant, 11.6%). Forearm tests were more variable, with bilateral symmetric fatigue in the elbow flexors (dominant, 22.5%; nondominant, 19.2%), and wrist flexors (dominant, 21.6%; nondominant, 19.0%), bilateral asymmetric fatigue in the supinators (dominant, 21.8%; nondominant, 15.5%), unilateral asymmetric fatigue in the elbow extensors (dominant, 22.1%; nondominant, 11.3%), and unilateral equivocal fatigue in the pronators (dominant, 18.8%; nondominant, 15.2%) and grip (dominant, 11.4%; nondominant, 6.6%). The mean (±SD) pitch velocity was 49 ± 4 mph, with a small loss of velocity from the first to last inning pitched (3.4% ± 5.0%, P < .01). Fast-pitch softball pitching resulted in profound bilateral fatigue in the hip and scapular muscles, with more selective fatigue in the shoulder and arm muscles. These findings emphasize the importance of strength in the proximal musculature to provide a stable platform for the arm to propel the ball. © 2015 The Author(s).

Evaluation of fatigue properties of EN31 steel heat treated using biodegradable gingili oil

NASA Astrophysics Data System (ADS)

Harichandra, B. P.; Prashanth, Mrudula; Prakash, S. V.

2016-09-01

Rotating bending fatigue is the most commonly encountered loading in most machines and machine tools. At the same time, modern literature in this area is very little. EN31 steel is a steel which is commonly used in load bearing applications which encounters fatigue loading. Further, studies on heat treated EN31 steel to improve fatigue strength is hardly reported. This paper takes this rare issue further ahead by using bio-degradable gingili oil to heat treat EN31 steel for fatigue applications. This paper reports the results of rotating bending fatigue study of EN31 steel. Fatigue tests were conducted for three conditions a) Untreated, b) Heat treated with water, and c) Heat treated with gingili oil, with cantilever loads ranging from 30% to 90% using double sided rotating bending fatigue testing machine. It is seen that EN31 steel heat treated using gingili oil has far superior fatigue properties than water treated and untreated ones, with gingili oil quenched specimen have ∼10 times more fatigue life than water quenched specimen and ∼100 times more than unquenched specimens when lower bending stresses are involved.

An evaluation of fatigue limit of notched specimen of a C/C composite

NASA Astrophysics Data System (ADS)

Makabe, C.; Fujikawa, M.; Ferdous, M. S.

2018-06-01

The fatigue strengths in notched specimens of carbon fiber reinforced carbon composites (C/C composites) were investigated. The fatigue limit was measured by S-N curves and load increase tests. The value of fatigue limit obtained by those methods was almost the same. Slits of several sizes were cut on both sides of a test section, and different sizes of slit length were chosen. Also, specimens with blunt-notches were used to compare the fatigue strength. The weakest fatigue limit was obtained in the case of specimens with blunt-notches. However, the stress concentration factor of those is smaller than that of slit specimens. The relationships between fatigue strengths and specimen shapes were analyzed by stress distribution. The effect of slit configuration on fatigue strength was then discussed regarding the experimental consequences. Consequently, it was discussed that the fatigue strength of the present specimens was determined depending on the damage conditions in the vicinity of the notch and on the crack initiation behavior. It is expected that the tendency of the S-N curve and fatigue limit was related to the shear damage and shear mode of the crack growth.

Acoustic emission characteristics of copper alloys under low-cycle fatigue conditions

NASA Technical Reports Server (NTRS)

Krampfner, Y.; Kawamoto, A.; Ono, K.; Green, A.

1975-01-01

The acoustic emission (AE) characteristics of pure copper, zirconium-copper, and several copper alloys were determined to develop nondestructive evaluation schemes of thrust chambers through AE techniques. The AE counts rms voltages, frequency spectrum, and amplitude distribution analysis evaluated AE behavior under fatigue loading conditions. The results were interpreted with the evaluation of wave forms, crack propagation characteristics, as well as scanning electron fractographs of fatigue-tested samples. AE signals at the beginning of a fatigue test were produced by a sample of annealed alloys. A sample of zirconium-containing alloys annealed repeatedly after each fatigue loading cycle showed numerous surface cracks during the subsequent fatigue cycle, emitting strong-burst AE signals. Amplitude distribution analysis exhibits responses that are characteristic of certain types of AE signals.

In vitro fatigue tests and in silico finite element analysis of dental implants with different fixture/abutment joint types using computer-aided design models.

PubMed

Yamaguchi, Satoshi; Yamanishi, Yasufumi; Machado, Lucas S; Matsumoto, Shuji; Tovar, Nick; Coelho, Paulo G; Thompson, Van P; Imazato, Satoshi

2018-01-01

The aim of this study was to evaluate fatigue resistance of dental fixtures with two different fixture-abutment connections by in vitro fatigue testing and in silico three-dimensional finite element analysis (3D FEA) using original computer-aided design (CAD) models. Dental implant fixtures with external connection (EX) or internal connection (IN) abutments were fabricated from original CAD models using grade IV titanium and step-stress accelerated life testing was performed. Fatigue cycles and loads were assessed by Weibull analysis, and fatigue cracking was observed by micro-computed tomography and a stereomicroscope with high dynamic range software. Using the same CAD models, displacement vectors of implant components were also analyzed by 3D FEA. Angles of the fractured line occurring at fixture platforms in vitro and of displacement vectors corresponding to the fractured line in silico were compared by two-way ANOVA. Fatigue testing showed significantly greater reliability for IN than EX (p<0.001). Fatigue crack initiation was primarily observed at implant fixture platforms. FEA demonstrated that crack lines of both implant systems in vitro were observed in the same direction as displacement vectors of the implant fixtures in silico. In silico displacement vectors in the implant fixture are insightful for geometric development of dental implants to reduce complex interactions leading to fatigue failure. Copyright © 2017 Japan Prosthodontic Society. Published by Elsevier Ltd. All rights reserved.

Fracture loads of all-ceramic crowns under wet and dry fatigue conditions.

PubMed

Borges, Gilberto A; Caldas, Danilo; Taskonak, Burak; Yan, Jiahau; Sobrinho, Lourenco Correr; de Oliveira, Wildomar José

2009-12-01

The aim of this study was to test the hypothesis that fracture loads of fatigued dental ceramic crowns are affected by testing environment and luting cement. One hundred and eighty crowns were prepared from bovine teeth using a lathe. Ceramic crowns were prepared from three types of ceramic systems: an alumina-infiltrated ceramic, a lithia-disilicate-based glass ceramic, and a leucite-reinforced ceramic. For each ceramic system, 30 crowns were cemented with a composite resin cement, and the remaining 30 with a resin-modified glass ionomer cement. For each ceramic system and cement, ten specimens were loaded to fracture without fatiguing. A second group (n = 10) was subjected to cyclic fatigue and fracture tested in a dry environment, and a third group (n = 10) was fatigued and fractured in distilled water. The results were statistically analyzed using one-way ANOVA and Tukey HSD test. The fracture loads of ceramic crowns decreased significantly after cyclic fatigue loading (p

Damage development in titanium metal matrix composites subjected to cyclic loading

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1992-01-01

Several layups of SCS-6/Ti-15-3 composites were investigated. Fatigue tests were conducted and analyzed for both notched and unnotched specimens at room temperature and elevated temperatures. Thermo-mechanical fatigue results were analyzed. Test results indicated that the stress in the 0 degree fibers is the controlling factor in fatigue life. The static and fatigue strength of these materials is shown to be strongly dependent on the level of residual stresses and the fiber/matrix interfacial strength. Fatigue tests of notched specimens showed that cracks can initiate and grow many fiber spacings in the matrix materials without breaking fibers. Fiber bridging models were applied to characterize the crack growth behavior. The matrix cracks are shown to significantly reduce the residual strength of notched composites. The notch strength of these composites was accurately predicted using a micromechanics based methodology.

Damage development in titanium metal-matrix composites subjected to cyclic loading

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1993-01-01

Several layups of SCS-6/Ti-15-3 composites were investigated. Fatigue tests were conducted and analyzed for both notched and unnotched specimens at room temperature and elevated temperatures. Thermo-mechanical fatigue results were analyzed. Test results indicated that the stress in the 0 degree fibers is the controlling factor in fatigue life. The static and fatigue strength of these materials is shown to be strongly dependent on the level of residual stresses and the fiber/matrix interfacial strength. Fatigue tests of notched specimens showed that cracks can initiate and grow many fiber spacings in the matrix materials without breaking fibers. Fiber bridging models were applied to characterize the crack growth behavior. The matrix cracks are shown to significantly reduce the residual strength of notched composites. The notch strength of these composites was accurately predicted using a micromechanics based methodology.

Experimental and numerical evaluation of the fatigue behaviour in a welded joint

NASA Astrophysics Data System (ADS)

Almaguer, P.; Estrada, R.

2014-07-01

Welded joints are an important part in structures. For this reason, it is always necessary to know the behaviour of them under cyclic loads. In this paper a S - N curve of a butt welded joint of the AISI 1015 steel and Cuban manufacturing E6013 electrode is showed. Fatigue tests were made in an universal testing machine MTS810. The stress ratio used in the test was 0,1. Flaws in the fatigue specimens were characterized by means of optical and scanning electron microscopy. SolidWorks 2013 software was used to modeling the specimens geometry, while to simulate the fatigue behaviour Simulation was used. The joint fatigue limit is 178 MPa, and a cut point at 2 039 093 cycles. Some points of the simulations are inside of the 95% confidence band.

Fatigue crack growth rates in a pressure vessel steel under various conditions of loading and the environment

NASA Astrophysics Data System (ADS)

Hicks, P. D.; Robinson, F. P. A.

1986-10-01

Corrosion fatigue (CF) tests have been carried out on SA508 Cl 3 pressure vessel steel, in simulated P.W.R. environments. The test variables investigated included air and P.W.R. water environments, frequency variation over the range 1 Hz to 10 Hz, transverse and longitudinal crack growth directions, temperatures of 20 °C and 50 °C, and R-ratios of 0.2 and 0.7. It was found that decreasing the test frequency increased fatigue crack growth rates (FCGR) in P.W.R. environments, P.W.R. environment testing gave enhanced crack growth (vs air tests), FCGRs were greater for cracks growing in the longitudinal direction, slight increases in temperature gave noticeable accelerations in FCGR, and several air tests gave FCGR greater than those predicted by the existing ASME codes. Fractographic evidence indicates that FCGRs were accelerated by a hydrogen embrittlement mechanism. The presence of elongated MnS inclusions aided both mechanical fatigue and hydrogen embrittlement processes, thus producing synergistically fast FCGRs. Both anodic dissolution and hydrogen embrittlement mechanisms have been proposed for the environmental enhancement of crack growth rates. Electrochemical potential measurements and potentiostatic tests have shown that sample isolation of the test specimens from the clevises in the apparatus is not essential during low temperature corrosion fatigue testing.

Real-time monitoring of acoustic linear and nonlinear behavior of titanium alloys during low-cycle fatigue and high-cycle fatigue

NASA Astrophysics Data System (ADS)

Frouin, Jerome; Sathish, Shamachary; Na, Jeong K.

2000-05-01

An in-situ technique to measure sound velocity, ultrasonic attenuation and acoustic nonlinear property has been developed for characterization and early detection of fatigue damage in aerospace materials. For this purpose we have developed a computer software and measurement technique including hardware for the automation of the measurement. New transducer holder and special grips are designed. The automation has allowed us to test the long-term stability of the electronics over a period of time and so proof of the linearity of the system. Real-time monitoring of the material nonlinearity has been performed on dog-bone specimens from zero fatigue all the way to the final fracture under low-cycle fatigue test condition (LCF) and high-cycle test condition (HCF). Real-time health monitoring of the material can greatly contribute to the understanding of material behavior under cyclic loading. Interpretation of the results show that correlation exist between the slope of the curve described by the material nonlinearity and the life of the component. This new methodology was developed with an objective to predict the initiation of fatigue microcracks, and to detect, in-situ fatigue crack initiation as well as to quantify early stages of fatigue damage.

Fatigue in industry.

PubMed Central

Grandjean, E

1979-01-01

Physical fatigue is a painful phenomenon which is localised in overstressed muscles. Mental fatigue is a diffuse sensation of weariness; it is a functional state, one of several intermediate conditions between the two extremes of alarm and sleep. A neurophysiological model of fatigue, involving an activating and inhibitory system has been developed. Fatigue in industrial practice has clinical symptoms: psychic instability, fits of depression and increased liability to illness. Indicators of fatigue are work of performance, subjective feelings of fatigue, electroencephalography, flicker-fusion frequency and various psychomotor and mental tests. Several field studies do, to some extent, confirm the above-mentioned concept of fatigue. PMID:40999

Structural fatigue test results for large wind turbine blade sections

NASA Technical Reports Server (NTRS)

Faddoul, J. R.; Sullivan, T. L.

1982-01-01

In order to provide quantitative information on the operating life capabilities of wind turbine rotor blade concepts for root-end load transfer, a series of cantilever beam fatigue tests was conducted. Fatigue tests were conducted on a laminated wood blade with bonded steel studs, a low cost steel spar (utility pole) with a welded flange, a utility pole with additional root-end thickness provided by a swaged collar, fiberglass spars with both bonded and nonbonded fittings, and, finally, an aluminum blade with a bolted steel fitting (Lockheed Mod-0 blade). Photographs, data, and conclusions for each of these tests are presented. In addition, the aluminum blade test results are compared to field failure information; these results provide evidence that the cantilever beam type of fatigue test is a satisfactory method for obtaining qualitative data on blade life expectancy and for identifying structurally underdesigned areas (hot spots).

Residual strength and crack propagation tests on C-130 airplane center wings with service-imposed fatigue damage

NASA Technical Reports Server (NTRS)

Snider, H. L.; Reeder, F. L.; Dirkin, W. J.

1972-01-01

Fourteen C-130 airplane center wings, each containing service-imposed fatigue damage resulting from 4000 to 13,000 accumulated flight hours, were tested to determine their fatigue crack propagation and static residual strength characteristics. Eight wings were subjected to a two-step constant amplitude fatigue test prior to static testing. Cracks up to 30 inches long were generated in these tests. Residual static strengths of these wings ranged from 56 to 87 percent of limit load. The remaining six wings containing cracks up to 4 inches long were statically tested as received from field service. Residual static strengths of these wings ranged from 98 to 117 percent of limit load. Damage-tolerant structural design features such as fastener holes, stringers, doublers around door cutouts, and spanwise panel splices proved to be effective in retarding crack propagation.

Fracture mechanics data for 2024-T861 and 2124-T851 aluminum

NASA Technical Reports Server (NTRS)

Pionke, L. J.; Linback, R. K.

1974-01-01

The fracture toughness and fatigue flaw growth characteristics of 2024-T861 and 2124-T851 aluminum were evaluated under plane stress conditions. Center cracked tension specimens were employed to evaluate these properties under a number of different test conditions which included variations in specimen thickness, specimen orientation, test environment, and initial flaw size. The effect of buckling was also investigated for all tests of thin gage specimens, and the effect of frequency and stress ratio was evaluated for the cyclic tests. Fracture toughness test results were analyzed and presented in terms of fracture resistance curves; fatigue flaw growth data was analyzed using empirical rate models. The results of the study indicate that both fracture toughness and resistance to fatigue crack growth improve with increasing temperature and decreasing thickness. The presence of buckling during testing of thin gage panels was found to degrade the resistance to fatigue flaw growth only at elevated temperatures.

Piezoelectric Bolt Breakers and Bolt Fatigue Testers

NASA Technical Reports Server (NTRS)

Sherrit, Stewart; Badescu, Mircea; Bar-Cohen, Yoseph; Barengoltz, Jack; Heckman, Vanessa

2008-01-01

A proposed family of devices for inducing fatigue in bolts in order to break the bolts would incorporate piezoelectric actuators into resonant fixtures as in ultrasonic/ sonic drills/corers and similar devices described in numerous prior NASA Tech Briefs articles. These devices were originally intended primarily for use as safer, more-reliable, more-versatile alternatives to explosive bolts heretofore used to fasten spacecraft structures that must subsequently be separated from each other quickly on command during flight. On Earth, these devices could be used for accelerated fatigue testing of bolts. Fatigue theory suggests that a bolt subjected to both a constant-amplitude dynamic (that is, oscillatory) stress and a static tensile stress below the ultimate strength of the bolt material will fail faster than will a bolt subjected to only the dynamic stress. This suggestion would be applied in a device of the proposed type. The device would be designed so that the device and the bolt to be fatigue-tested or broken would be integral parts of an assembly (see figure). The static tension in the tightened bolt would apply not only the clamping force to hold the joined structures (if any) together but also the compression necessary for proper operation of the piezoelectric actuators as parts of a resonant structural assembly. The constant-amplitude dynamic stress would be applied to the bolt by driving the piezoelectric actuators with a sinusoidal voltage at the resonance frequency of longitudinal vibration of the assembly. The amplitude of the excitation would be made large enough so that the vibration would induce fatigue in the bolt within an acceptably short time. In the spacecraft applications or in similar terrestrial structural-separation applications, devices of the proposed type would offer several advantages over explosive bolts: Unlike explosive bolts, the proposed devices would be reusable, could be tested before final use, and would not be subject to catastrophic misfire. In fatigue-testing applications, devices of the proposed type would offer advantages of compactness and low cost, relative to conventional fatigue- testing apparatuses. In both structural- separation and fatigue-testing applications, bolts to be broken or tested could be instrumented with additional ultrasonic transducers for monitoring of pertinent physical properties and of fatigue failure processes.

Gamma Radiation Sterilization Reduces the High-cycle Fatigue Life of Allograft Bone.

PubMed

Islam, Anowarul; Chapin, Katherine; Moore, Emily; Ford, Joel; Rimnac, Clare; Akkus, Ozan

2016-03-01

Sterilization by gamma radiation impairs the mechanical properties of bone allografts. Previous work related to radiation-induced embrittlement of bone tissue has been limited mostly to monotonic testing which does not necessarily predict the high-cycle fatigue life of allografts in vivo. We designed a custom rotating-bending fatigue device to answer the following questions: (1) Does gamma radiation sterilization affect the high-cycle fatigue behavior of cortical bone; and (2) how does the fatigue life change with cyclic stress level? The high-cycle fatigue behavior of human cortical bone specimens was examined at stress levels related to physiologic levels using a custom-designed rotating-bending fatigue device. Test specimens were distributed among two treatment groups (n = 6/group); control and irradiated. Samples were tested until failure at stress levels of 25, 35, and 45 MPa. At 25 MPa, 83% of control samples survived 30 million cycles (run-out) whereas 83% of irradiated samples survived only 0.5 million cycles. At 35 MPa, irradiated samples showed an approximately 19-fold reduction in fatigue life compared with control samples (12.2 × 10(6) ± 12.3 × 10(6) versus 6.38 × 10(5) ± 6.81 × 10(5); p = 0.046), and in the case of 45 MPa, this reduction was approximately 17.5-fold (7.31 × 10(5) ± 6.39 × 10(5) versus 4.17 × 10(4) ± 1.91 × 10(4); p = 0.025). Equations to estimate high-cycle fatigue life of irradiated and control cortical bone allograft at a certain stress level were derived. Gamma radiation sterilization severely impairs the high cycle fatigue life of structural allograft bone tissues, more so than the decline that has been reported for monotonic mechanical properties. Therefore, clinicians need to be conservative in the expectation of the fatigue life of structural allograft bone tissues. Methods to preserve the fatigue strength of nonirradiated allograft bone tissue are needed. As opposed to what monotonic tests might suggest, the cyclic fatigue life of radiation-sterilized structural allografts is likely severely compromised relative to the nonirradiated condition and therefore should be taken into consideration. Methods to reduce the effect of irradiation or to recover structural allograft bone tissue fatigue strength are important to pursue.

Biomechanical evaluation of an integrated fixation cage during fatigue loading: a human cadaver study.

PubMed

Palepu, Vivek; Peck, Jonathan H; Simon, David D; Helgeson, Melvin D; Nagaraja, Srinidhi

2017-04-01

OBJECTIVE Lumbar cages with integrated fixation screws offer a low-profile alternative to a standard cage with anterior supplemental fixation. However, the mechanical stability of integrated fixation cages (IFCs) compared with a cage with anterior plate fixation under fatigue loading has not been investigated. The purpose of this study was to compare the biomechanical stability of a screw-based IFC with a standard cage coupled with that of an anterior plate under fatigue loading. METHODS Eighteen functional spinal units were implanted with either a 4-screw IFC or an anterior plate and cage (AP+C) without integrated fixation. Flexibility testing was conducted in flexion-extension (FE), lateral bending (LB), and axial rotation (AR) on intact spines, immediately after device implantation, and post-fatigue up to 20,000 cycles of FE loading. Stability parameters such as range of motion (ROM) and lax zone (LZ) for each loading mode were compared between the 2 constructs at multiple stages of testing. In addition, construct loosening was quantified by subtracting post-instrumentation ROM from post-fatigue ROM. RESULTS IFC and AP+C configurations exhibited similar stability (ROM and LZ) at every stage of testing in FE (p ≥ 0.33) and LB (p ≥ 0.23) motions. In AR, however, IFCs had decreased ROM compared with AP+C constructs at pre-fatigue (p = 0.07) and at all post-fatigue time points (p ≤ 0.05). LZ followed a trend similar to that of ROM in AR. ROM increased toward intact motion during fatigue cycling for AP+C and IFC implants. IFC specimens remained significantly (p < 0.01) more rigid than specimens in the intact condition during fatigue for each loading mode, whereas AP+C construct motion did not differ significantly (p ≥ 0.37) in FE and LB and was significantly greater (p < 0.01) in AR motion compared with intact specimens after fatigue. Weak to moderate correlations (R 2 ≤ 56%) were observed between T-scores and construct loosening, with lower T-scores leading to decreased stability after fatigue testing. CONCLUSIONS These data indicate that a 4-screw IFC design provides fixation similar to that provided by an AP+C construct in FE and LB during fatigue testing and better stability in AR motion.

Tensile and Fatigue Testing and Material Hardening Model Development for 508 LAS Base Metal and 316 SS Similar Metal Weld under In-air and PWR Primary Loop Water Conditions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mohanty, Subhasish; Soppet, William; Majumdar, Saurin

This report provides an update on an assessment of environmentally assisted fatigue for light water reactor components under extended service conditions. This report is a deliverable in September 2015 under the work package for environmentally assisted fatigue under DOE’s Light Water Reactor Sustainability program. In an April 2015 report we presented a baseline mechanistic finite element model of a two-loop pressurized water reactor (PWR) for systemlevel heat transfer analysis and subsequent thermal-mechanical stress analysis and fatigue life estimation under reactor thermal-mechanical cycles. In the present report, we provide tensile and fatigue test data for 508 low-alloy steel (LAS) base metal,more » 508 LAS heat-affected zone metal in 508 LAS–316 stainless steel (SS) dissimilar metal welds, and 316 SS-316 SS similar metal welds. The test was conducted under different conditions such as in air at room temperature, in air at 300 oC, and under PWR primary loop water conditions. Data are provided on materials properties related to time-independent tensile tests and time-dependent cyclic tests, such as elastic modulus, elastic and offset strain yield limit stress, and linear and nonlinear kinematic hardening model parameters. The overall objective of this report is to provide guidance to estimate tensile/fatigue hardening parameters from test data. Also, the material models and parameters reported here can directly be used in commercially available finite element codes for fatigue and ratcheting evaluation of reactor components under in-air and PWR water conditions.« less

Stiffness reductions during tensile fatigue testing of graphite/epoxy angle-ply laminates

NASA Technical Reports Server (NTRS)

Odom, E. M.; Adams, D. F.

1982-01-01

Tensile fatigue data was generated under carefully controlled test conditions. A computerized data acquisition system was used to permit the measurement of dynamic modulus without interrupting the fatigue cycling. Two different 8-ply laminate configurations, viz, + or - 45 (2s) and + or - 67.5 (2s), of a T300/5208 graphite/epoxy composite were tested. The + or - 45 (2s) laminate did exhibit some modulus decay, although there was no well-defined correlation with applied stress level or number of cycles. The + or - 67.5 (2s) laminate did not exhibit any measurable modulus decay. Secondary effects observed included a small but distinct difference between modulus as measured statically and dynamically, a slight recovery of the modulus decay after a test interruption, and a significant viscoelastic (creep) response of the + or - 45 (2s) laminate during fatigue testing.

Effect of tooth whitening strips on fatigue resistance and flexural strength of bovine dentin in vitro

PubMed Central

Kim, Namhee; De Souza, Grace M.

2017-01-01

Objective To determine the effects of whitening strips on bovine dentin fatigue resistance and flexural strength in vitro. Materials and methods A total of eighty bovine dentin specimens (2x2x17mm) were treated with either: control glycerine gel on plastic film wrap or whitening strips containing 9.5% hydrogen peroxide. Treatment was applied for 30 minutes, twice a day, for 1- or 4-weeks. After the last treatment, ten specimens per group were randomly selected to undergo fatigue testing (106 cycles, 3Hz, 20N) while the other ten were subjected to flexural strength testing after ten days of storage in artificial saliva. Kaplan-Meier method with a log rank test, Wilcoxon test and Cox regression were used to assess fatigue test results (p<0.05). One-way ANOVA and Tukey’s tests were used to compare the flexural strength results (p<0.05). Results There were significant differences in survival during the fatigue test among the groups (p<0.001). Treatment (control or bleach) was a significant factor for specimen survival (p<0.001, Exp(B) = 33.45). There were significant differences in mean flexural strength (p<0.001). No significant difference was found between “1-wk control” and “4-wk control”. The mean flexural strength and fatigue resistance of the “4-wk bleach” were significantly lower than all the other groups. Conclusions The use of whitening strips reduced the fatigue resistance and flexural strength of bovine dentin in vitro. Until the effect of whitening strips on mechanical properties of human dentin is fully elucidated, it remains prudent to advise patients to avoid excessive direct use of whitening strips on dentin. PMID:28278191

The Neural Mechanisms of Re-Experiencing Mental Fatigue Sensation: A Magnetoencephalography Study

PubMed Central

Ishii, Akira; Karasuyama, Takuma; Kikuchi, Taiki; Tanaka, Masaaki; Yamano, Emi; Watanabe, Yasuyoshi

2015-01-01

There have been several studies which have tried to clarify the neural mechanisms of fatigue sensation; however fatigue sensation has multiple aspects. We hypothesized that past experience related to fatigue sensation is an important factor which contributes to future formation of fatigue sensation through the transfer to memories that are located within specific brain structures. Therefore, we aimed to investigate the neural mechanisms of fatigue sensation related to memory. In the present study, we investigated the neural activity caused by re-experiencing the fatigue sensation that had been experienced during a fatigue-inducing session. Thirteen healthy volunteers participated in fatigue and non-fatigue experiments in a crossover fashion. In the fatigue experiment, they performed a 2-back test session for 40 min to induce fatigue sensation, a rest session for 15 min to recover from fatigue, and a magnetoencephalography (MEG) session in which they were asked to re-experience the state of their body with fatigue that they had experienced in the 2-back test session. In the non-fatigue experiment, the participants performed a free session for 15 min, a rest session for 15 min, and an MEG session in which they were asked to re-experience the state of their body without fatigue that they had experienced in the free session. Spatial filtering analyses of oscillatory brain activity showed that the delta band power in the left Brodmann’s area (BA) 39, alpha band power in the right pulvinar nucleus and the left BA 40, and beta band power in the left BA 40 were lower when they re-experienced the fatigue sensation than when they re-experienced the fatigue-free sensation, indicating that these brain regions are related to re-experiencing the fatigue sensation. Our findings may help clarify the neural mechanisms underlying fatigue sensation. PMID:25826300

Validation of an Arabic version of Fatigue Severity Scale

PubMed Central

Al-Sobayel, Hana I.; Al-Hugail, Hind A.; AlSaif, Ranyah M.; Albawardi, Nada M.; Alnahdi, Ali H.; Daif, Abdulkader M.; Al-Arfaj, Hussein F.

2016-01-01

Objectives: To develop and test the psychometric properties of an Arabic version of Fatigue Severity Scale (FSS-Ar) that can be used to measure fatigue in Arabic patients with disorders where fatigue is a major symptom. Methods: Forward and backward translations of FSS were undertaken to develop an Arabic version. The validity and reliability of the FSS-Ar was then tested on 28 patients with systemic lupus erythematosus (SLE), 24 patients with multiple sclerosis (MS), and 31 healthy subjects. Exploratory factor analysis and hypothesis testing methods were used to examine construct validity. The correlation between FSS-Ar and the vitality domain of the RAND 36-Item Health was examined to test construct validity. The study was conducted at the King Khalid University Hospital, Riyadh, Kingdom of Saudi Arabia between February and June 2012. Results: Using a score of ≥4.05 to define fatigue, 39 of 52 (75%) participants were fatigued compared with 10 out of 31 (32%) healthy participants. The correlation between the FSS-Ar and the vitality domain of the RAND-36 was acceptable (r = -0.46). Factor analysis showed that items of the FSS-Ar measured one underlying construct, namely, fatigue. Test-retest reliability and internal consistency of the FSS-Ar was acceptable (intraclass correlation coefficient model 2,1 = 0.80; Cronbach’s alpha = 0.84). Conclusion: The Arabic version of the FSS demonstrated acceptable psychometric properties and was able to differentiate between patients with SLE or MS, and healthy subjects. PMID:26739978

Corrosion fatigue behaviors of two biomedical Mg alloys - AZ91D and WE43 - In simulated body fluid.

PubMed

Gu, X N; Zhou, W R; Zheng, Y F; Cheng, Y; Wei, S C; Zhong, S P; Xi, T F; Chen, L J

2010-12-01

Magnesium alloys have been recently developed as biodegradable implant materials, yet there has been no study concerning their corrosion fatigue properties under cyclic loading. In this study the die-cast AZ91D (A for aluminum 9%, Z for zinc 1% and D for a fourth phase) and extruded WE43 (W for yttrium 4%, E for rare earth mischmetal 3%) alloys were chosen to evaluate their fatigue and corrosion fatigue behaviors in simulated body fluid (SBF). The die-cast AZ91D alloy indicated a fatigue limit of 50MPa at 10⁷ cycles in air compared to 20MPa at 10⁶ cycles tested in SBF at 37°C. A fatigue limit of 110MPa at 10⁷ cycles in air was observed for extruded WE43 alloy compared to 40MPa at 10⁷ cycles tested in SBF at 37°C. The fatigue cracks initiated from the micropores when tested in air and from corrosion pits when tested in SBF, respectively. The overload zone of the extruded WE43 alloy exhibited a ductile fracture mode with deep dimples, in comparison to a brittle fracture mode for the die-cast AZ91D. The corrosion rate of the two experimental alloys increased under cyclic loading compared to that in the static immersion test. Copyright © 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of initial delamination on Mode 1 and Mode 2 interlaminar fracture toughness and fatigue fracture threshold

NASA Technical Reports Server (NTRS)

Murri, Gretchen Bostaph; Martin, Roderick H.

1991-01-01

Static and fatigue double-cantilever beam (DCB) and end-notch flexure (ENF) tests were conducted to determine the effect of the simulated initial delamination in interlaminar fracture toughness, G(sub c), and fatigue fracture threshold, G(sub th). Unidirectional, 24-ply specimens of S2/SP250 glass/epoxy were tested using Kapton inserts of four different thickness - 13, 25, 75, and 130 microns, at the midplane at one end, or with tension or shear precracks, to simulate an initial delamination. To determine G(sub c), the fatigue fracture threshold below which no delamination growth would occur in less than 1 x 10(exp 6) cycles, fatigue tests were conducted by cyclically loading specimens until delamination growth was detected. Consistent values of model 1 fracture toughness, G(sub Ic), were measured from DCB specimens with inserts of thickness 75 microns or thinner, or with shear precracks. The fatigue DCB tests gave similar values of G(sub Ith) for the 13, 25, and 75 microns specimens. Results for the shear precracked specimens were significantly lower that for specimens without precracks. Results for both the static and fatigue ENF tests showed that measured G(IIc) and G(IIth) values decreased with decreasing insert thickness, so that no limiting thickness could be determined. Results for specimens with inserts of 75 microns or thicker were significantly higher than the results for precracked specimens or specimens with 13 or 25 microns inserts.

Surface fatigue life of M50NiL and AISI 9310 spur gears and R C bars

NASA Technical Reports Server (NTRS)

Townsend, Dennis P.; Bamberger, Eric N.

1991-01-01

Spur gear endurance tests and rolling element surface fatigue tests were conducted to study vacuum induction melted, vacuum arc remelted (VIM-VAR) M50NiL steel for use as a gear steel in advanced aircraft applications, to determine its endurance characteristics, and to compare the results with those for standard VAR and VIM-VAR AISI 9310 gear material. Tests were conducted with spur gears and rolling contact bars manufactured from VIM-VAR M50NiL and VAR and VIM-VAR AISI 9310. The gear pitch diameter was 8.9 cm. Gear test conditions were an inlet oil temperature of 320 K, and outlet oil temperature of 350 K, a maximum Hertz stress of 1.71 GPa, and a speed of 10000 rpm. Bench rolling element fatigue tests were conducted at ambient temperatures with a bar speed of 12,500 rpm and a maximum Hertz stress of 4.83 GPa. The VIM-VAR M50NiL gears had a surface fatigue life that was 4.5 and 11.5 times that for VIM-VAR and VAR AISI 9310 gears, respectively. The surface fatigue life of the VIM-VAR M50NiL rolling contact bars was 13.2 and 21.6 times that for the VIM-VAR and VAR AISI 9310, respectively. The VIM-VAR M50NiL material was shown to have good resistance to fracture through a fatigue spall and superior fatigue life to both other gears.

Fatigue in the Presence of Corrosion (Fatigue sous corrosion)

DTIC Science & Technology

1999-03-01

Fatigue Crack Growth Propagation of Aluminum Lithium cycle managers to safely delay repairs to a more appropriate Alloys " described the effect of... effects of service corrosion on fatigue lab tests with 2024 -T3, because 7178 life , if any, can be established in this was not available. However, we did not... life and the fatigue crack growth behavior of the cases where a structural member is the 2024 alloy was studied as well. stressed or fatigued

High-Cycle Fatigue of High-Strength Low Alloy Steel Q345 Subjected to Immersion Corrosion for Mining Wheel Applications

NASA Astrophysics Data System (ADS)

Dicecco, Sante; Altenhof, William; Hu, Henry; Banting, Richard

2017-04-01

In an effort to better understand the impact of material degradation on the fatigue life of mining wheels made of a high-strength low alloy carbon steel (Q345), this study seeks to evaluate the effect of surface corrosion on the high-cycle fatigue behavior of the Q345 alloy. The fatigue behavior of the polished and corroded alloy was investigated. Following exposure to a 3.5 wt.% NaCl saltwater solution, polished and corroded fatigue specimens were tested using an R.R. Moore rotating-bending fatigue apparatus. Microstructural analyses via both optical microscopy and scanning electron microscopy (SEM) revealed that one major phase, α-iron phase, ferrite, and one minor phase, colony pearlite, existed in the extracted Q345 alloy. The results of the fatigue testing showed that the polished and corroded specimens had an endurance strength of approximately 295 and 222 MPa, respectively, at 5,000,000 cycles. The corroded surface condition resulted in a decrease in the fatigue strength of the Q345 alloy by 24.6%. Scanning electron microscope fractography indicated that failure modes for polished and corroded fatigue specimens were consistent in the high-cycle low loading fatigue regime. Conversely, SEM fractography of low-cycle high-loading fatigue specimens found considerable differences in fracture surfaces between the corroded and polished fatigue specimens.

Fatigue Properties of the Ultra-High Strength Steel TM210A

PubMed Central

Kang, Xia; Zhao, Gui-ping

2017-01-01

This paper presents the results of an experiment to investigate the high cycle fatigue properties of the ultra-high strength steel TM210A. A constant amplitude rotating bending fatigue experiment was performed at room temperature at stress ratio R = −1. In order to evaluate the notch effect, the fatigue experiment was carried out upon two sets of specimens, smooth and notched, respectively. In the experiment, the rotating bending fatigue life was tested using the group method, and the rotating bending fatigue limit was tested using the staircase method at 1 × 107 cycles. A double weighted least square method was then used to fit the stress-life (S–N) curve. The S–N curves of the two sets of specimens were obtained and the morphologies of the fractures of the two sets of specimens were observed with scanning electron microscopy (SEM). The results showed that the fatigue limit of the smooth specimen for rotating bending fatigue was 615 MPa; the ratio of the fatigue limit to tensile strength was 0.29, and the cracks initiated at the surface of the smooth specimen; while the fatigue limit of the notched specimen for rotating bending fatigue was 363 MPa, and the cracks initiated at the edge of the notch. The fatigue notch sensitivity index of the ultra-high strength maraging steel TM210A was 0.69. PMID:28891934

SLM processing-microstructure-mechanical property correlation in an aluminum alloy produced by additive manufacturing

NASA Astrophysics Data System (ADS)

Alejos, Martin Fernando

Additive manufacturing has become a highly researched topic in recent years all over the world. The current research evaluates the merits of additive manufacturing based on the mechanical, microstructural, and fracture properties of additive manufactured AlSi10Mg test specimens. The additive manufactured build plates consisted of tensile and fatigue test specimens. They were printed in the 0°, 30°, 60°, and 90° orientations relative to the build platform. Tensile and dynamic fatigue tests were conducted followed by microstructural characterization and fracture analysis. A wrought 6061 T6 aluminum alloy was also tested for comparison. Tensile tests revealed similar ultimate tensile strengths for all aluminum tensile specimens (350-380 MPa). Fatigue strength was greatest for wrought 6061 T6 aluminum (175 MPa). The fatigue behavior was a strong function of build orientation for the additive manufactured specimens. The 0°, 30°, and 60° orientations had fatigue strengths close to 104 MPa while the 90° orientation had a fatigue strength of 125 MPa. All test specimens failed primarily in a ductile manner. The effect of laser power, hatch spacing, and scan speed were also studied using microstructural analysis. Increasing laser power decreased grain size and void size. Increasing scan speed led to the formation of columnar grains. Increasing hatch spacing decreased grain size and the amount of voids present in the microstructure.

Influence of frequency on shear fatigue strength of resin composite to enamel bonds using self-etch adhesives.

PubMed

Takamizawa, Toshiki; Scheidel, Donal D; Barkmeier, Wayne W; Erickson, Robert L; Tsujimoto, Akimasa; Latta, Mark A; Miyazaki, Masashi

2016-09-01

The purpose of this study was to determine the influence of different frequency rates on of bond durability of self-etch adhesives to enamel using shear fatigue strength (SFS) testing. A two-step self-etch adhesive (OX, OptiBond XTR), and two single step self-etch adhesives (GB, G-ӕnial Bond and SU, Scotchbond Universal) were used in this study. The shear fatigue strength (SFS) to enamel was obtained. A staircase method was used to determine the SFS values with 50,000 cycles or until failure occurred. Fatigue testing was performed at frequencies of 5Hz, 10Hz, and 20Hz. For each test condition, 30 specimens were prepared for the SFS testing. Regardless of the bond strength test method, OX showed significantly higher SFS values than the two single-step self-etch adhesives. For each of the three individual self-etch adhesives, there was no significant difference in SFS depending on the frequency rate, although 20Hz results tended to be higher. Regardless of the self-etch adhesive system, frequencies of 5Hz, 10Hz, and 20Hz produced similar results in fatigue strength of resin composite bonded to enamel using 50,000 cycles or until bond failure. Accelerated fatigue testing provides valuable information regarding the long term durability of resin composite to enamel bonding using self-etch adhesive system. Copyright © 2016 Elsevier Ltd. All rights reserved.

Thermomechanical Multiaxial Fatigue Testing Capability Developed

NASA Technical Reports Server (NTRS)

1996-01-01

Structural components in aeronautical gas turbine engines typically experience multiaxial states of stress under nonisothermal conditions. To estimate the durability of the various components in the engine, one must characterize the cyclic deformation and fatigue behavior of the materials used under thermal and complex mechanical loading conditions. To this end, a testing protocol and associated test control software were developed at the NASA Lewis Research Center for thermomechanical axial-torsional fatigue tests. These tests are to be performed on thin-walled, tubular specimens fabricated from the cobalt-based superalloy Haynes 188. The software is written in C and runs on an MS-DOS based microcomputer.

14 CFR 35.37 - Fatigue limits and evaluation.

Code of Federal Regulations, 2010 CFR

2010-01-01

... 14 Aeronautics and Space 1 2010-01-01 2010-01-01 false Fatigue limits and evaluation. 35.37... AIRWORTHINESS STANDARDS: PROPELLERS Tests and Inspections § 35.37 Fatigue limits and evaluation. This section does not apply to fixed-pitch wood propellers of conventional design. (a) Fatigue limits must be...

Differences in fatigue severity in a sample of adult cancer patients.

PubMed

Gonzalez, Velda J; Tofthagen, Cindy S; Chen, Xusheng; Pedro, Elsa; Saligan, Leorey N

2017-04-05

To describe differences in fatigue severity in a sample of adult Puerto Rican patients during and postcancer treatments. Hispanics, including Puerto Ricans, are an understudied population who are under-represented in clinical trials, especially in symptom research. Although symptom management is a clinical priority in oncology care, treatment-related differences in Puerto Rican cancer patients' report of fatigue severity have not been well described. A cross-sectional survey was conducted from data of self-report of 138 Puerto Rican patients during and postcancer treatments at two ambulatory facilities located in San Juan, Puerto Rico. Fatigue severity was assessed using the Fatigue subscale from the Functional Assessment of Cancer Therapy-Fatigue quality of life questionnaire Spanish version. Differences in fatigue severity across type of treatment (radiation therapy, chemotherapy, combined radiation chemotherapy and post-treatment) were evaluated using nonparametric (Kruskal-Wallis and Mann-Whitney test) statistical tests. The majority of the participants had prostate (33%) and breast (32%) cancers and were receiving radiation therapy (43%) or chemotherapy (28%). The Kruskal-Wallis test showed that there was a statistically significant difference in fatigue scores between the different four treatment conditions, χ 2 (3) = 39.1, p = .001 with patients on combined radiation chemotherapy or chemotherapy alone experiencing more severe fatigue. Findings from the current study suggest that type of treatment is a key component of the symptom burden of fatigue among the Puerto Rican oncology population. Specially, patients receiving combined therapy or chemotherapy alone were at increased risk for experiencing severe fatigue, compared to radiation therapy and post-treatment patients. With the worldwide increase in migration of Puerto Rican families, nurses need to recognise that type of treatment is a key component of the symptom burden of fatigue among the Puerto Rican population. The results of this study will improve understanding of treatment-related fatigue to identify therapeutic targets and improve quality of life of patients. © 2017 John Wiley & Sons Ltd.

Experimental and theoretical investigation of fatigue life in reusable rocket thrust chambers

NASA Technical Reports Server (NTRS)

Hannum, N. P.; Kasper, H. J.; Pavli, A. J.

1976-01-01

During a test program to investigate low-cycle thermal fatigue, 13 rocket combustion chambers were fabricated and cyclically test fired to failure. Six oxygen-free, high-conductivity (OFHC) copper and seven Amzirc chambers were tested. The chamber liners were fabricated of copper or copper alloy and contained milled coolant channels. The chambers were completed by means of an electroformed nickel closeout. The oxidant/fuel ratio for the liquid oxygen and gaseous hydrogen propellants was 6.0. The failures in the OFHC copper chambers were not typical fatigue failures but are described as creep rupture enhanced by ratcheting. The coolant channels bulged toward the chamber centerline, resulting in progressive thinning of the wall during each cycle. The failures in the Amzirc alloy chambers were caused by low-cycle thermal fatigue. The lives were much shorter than were predicted by an analytical structural analysis computer program used in conjunction with fatigue life data from isothermal test specimens, due to the uneven distribution of Zr in the chamber material.

Immediate Effects of Kinesiology Taping of Quadriceps on Motor Performance after Muscle Fatigued Induction.

PubMed

Ahn, Ick Keun; Kim, You Lim; Bae, Young-Hyeon; Lee, Suk Min

2015-01-01

Objectives. The purpose of this cross-sectional single-blind study was to investigate the immediate effects of Kinesiology taping of quadriceps on motor performance after muscle fatigued induction. Design. Randomized controlled cross-sectional design. Subjects. Forty-five subjects participated in this study. Participants were divided into three groups: Kinesiology taping group, placebo taping group, and nontaping group. Methods. Subjects performed short-term exercise for muscle fatigued induction, followed by the application of each intervention. Peak torque test, one-leg single hop test, active joint position sense test, and one-leg static balance test were carried out before and after the intervention. Results. Peak torque and single-leg hopping distance were significantly increased when Kinesiology taping was applied (p < 0.05). But there were no significant effects on active joint position sense and single-leg static balance. Conclusions. We proved that Kinesiology taping is effective in restoring muscle power reduced after muscle fatigued induction. Therefore, we suggest that Kinesiology taping is beneficial for fatigued muscles.

Ultrasonic fatigue of a high strength steel

NASA Astrophysics Data System (ADS)

Koster, M.; Wagner, G.; Eifler, D.

2010-07-01

At the Institute of Materials Science and Engineering at the University of Kaiserslautern an ultrasonic testing system for the fatigue assessment of metallic materials in the very high cycle fatigue (VHCF) regime was developed. The ultrasonic testing system allows to control the test and to measure detailed fatigue data. The achieved results can be used to describe the cyclic deformation behaviour of wheel steels at ultrasonic frequencies. In load increase tests (LIT), the critical stress amplitude can be determined, which leads to a defined change of process parameters like generator power, dissipated energy and specimen temperature. With SEM investigations it was proved that the change of the process parameters correlates with irreversible changes in the microstructure. It can be shown that the stress amplitude, leading to first irreversible changes in the microstructure, strongly depends on the depth position within the original wheel rim. New and basic results on the fatigue mechanisms of high strength steels in the VHCF-regime can be achieved.

Quiet Clean Short-haul Experimental Engine (QCSEE) under-the-wing engine composite fan blade design report

NASA Technical Reports Server (NTRS)

Ravenhall, R.; Salemme, C. T.

1977-01-01

A total of 38 quiet clean short haul experimental engine under the wing composite fan blades were manufactured for various component tests, process and tooling, checkout, and use in the QCSEE UTW engine. The component tests included frequency characterization, strain distribution, bench fatigue, platform static load, whirligig high cycle fatigue, whirligig low cycle fatigue, whirligig strain distribution, and whirligig over-speed. All tests were successfully completed. All blades planned for use in the engine were subjected to and passed a whirligig proof spin test.

Objective assessment of motor fatigue in multiple sclerosis using kinematic gait analysis: a pilot study

PubMed Central

2011-01-01

Background Fatigue is a frequent and serious symptom in patients with Multiple Sclerosis (MS). However, to date there are only few methods for the objective assessment of fatigue. The aim of this study was to develop a method for the objective assessment of motor fatigue using kinematic gait analysis based on treadmill walking and an infrared-guided system. Patients and methods Fourteen patients with clinically definite MS participated in this study. Fatigue was defined according to the Fatigue Scale for Motor and Cognition (FSMC). Patients underwent a physical exertion test involving walking at their pre-determined patient-specific preferred walking speed until they reached complete exhaustion. Gait was recorded using a video camera, a three line-scanning camera system with 11 infrared sensors. Step length, width and height, maximum circumduction with the right and left leg, maximum knee flexion angle of the right and left leg, and trunk sway were measured and compared using paired t-tests (α = 0.005). In addition, variability in these parameters during one-minute intervals was examined. The fatigue index was defined as the number of significant mean and SD changes from the beginning to the end of the exertion test relative to the total number of gait kinematic parameters. Results Clearly, for some patients the mean gait parameters were more affected than the variability of their movements while other patients had smaller differences in mean gait parameters with greater increases in variability. Finally, for other patients gait changes with physical exertion manifested both in changes in mean gait parameters and in altered variability. The variability and fatigue indices correlated significantly with the motoric but not with the cognitive dimension of the FSMC score (R = -0.602 and R = -0.592, respectively; P < 0.026). Conclusions Changes in gait patterns following a physical exertion test in patients with MS suffering from motor fatigue can be measured objectively. These changes in gait patterns can be described using the motor fatigue index and represent an objective measure to assess motor fatigue in MS patients. The results of this study have important implications for the assessments and treatment evaluations of fatigue in MS. PMID:22029427

Damage mechanisms in alloy 800H under creep-fatigue conditions

NASA Astrophysics Data System (ADS)

Mu, Z.; Bothe, K.; Gerold, V.

1994-05-01

The interaction between fatigue damage (i.e., fatigue crack propagation) and internal grain boundary damage (i.e., cavity formation at grain boundaries) has been studied for the Alloy 800H at 750 C for constant plastic strain ranges but different experimental conditions. Most experiments were performed at constant ranges of alternating tensile/compression stresses. Symmetrical as well as asymmetrical tests (with larger compression stresses) were performed. In comparison to the former tests, asymmetrical tests led to shorter cyclic lifetimes mainly due to cavity formation which was not observed for symmetrical tests. It could be shown that a fast compressive and a slow tensile half cycle (at large compressive and low tensile stresses) are ideal conditions for the nucleation and growth of cavities. Based on quantitative measurements of the cavity density from interrupted fatigue tests, a physical model is presented which can predict the number of cycles to failure. This cycle number is determined only by fatigue crack growth which is controlled by (1) athermal plastic deformation, (2) creep deformation and (3) rate enhancement by cavitation.

Thermal-Fatigue Crack-Growth Characteristics and Mechanical Strain Cycling Behavior of A-286 Discaloy, and 16-25-6 Austenitic Steels

NASA Technical Reports Server (NTRS)

Smith, Robert W.; Smith, Gordon T.

1960-01-01

Thermal-fatigue crack-growth characteristics of notched- and unnotched-disk specimens of A-286, Discaloy, hot-cold worked 16-25-6, and overaged 16-25-6 were experimentally studied. Separately controlled variables were total strain range (0.0043 to 0.0079 in./in.), maximum cycle temperature (1300 and 1100 F), and hold time at maximum temperature (O and 5 min). A limited number of mechanical, push-pull, constant-strain cycle tests at room temperature were made using notched and un-notched bars of the same materials. In these tests the number of cycles to failure as well as the variation of load change with accumulated cycles was measured, and the effects of mean stress were observed. Constant-strain-range mechanical-fatigue tests at room temperature revealed notched-bar fatigue life to be strongly influenced by mean stress. For a specific strain range, the longest fatigue life was always found to be associated with the least-tensile (or most compressive) mean stress. By defining thermal-fatigue life as the number of cycles required to produce a crack area of 6000 square mils, the relative thermal-fatigue resistances of the test materials were established. Notched-disk specimens of A-286 and Discaloy steels exhibited longer fatigue lives than either hot-cold worked or overaged 16-25-6. On the other hand, unnotched-disk specimens of Discaloy and hot-cold worked 16-25-6 had longer lives than A-286 and overaged 16-25-6. Separation of the crack-growth data into microstage and macrostage periods revealed that the macrostage period accounted for the greatest part of the difference among materials when tested in the notched configuration, while the microstage was largely responsible for the differences encountered in unnotched disks.

Reduced Electromyographic Fatigue Threshold after Performing a Cognitive Fatiguing Task.

PubMed

Ferris, Justine R; Tomlinson, Mary A; Ward, Tayler N; Pepin, Marie E; Malek, Moh H

2018-02-22

Cognitive fatigue tasks performed prior to exercise may reduce exercise capacity. The electromyographic fatigue threshold (EMGFT) is the highest exercise intensity that can be maintained without significant increase in the EMG amplitude versus time relationship. To date, no studies have examined the effect of cognitive fatigue on the estimation of the EMGFT. The purpose of this study, therefore, was to determine whether or not cognitive fatigue prior to performing exercise reduces the estimated EMGFT. Eight healthy college-aged men were recruited from a university student population and visited the laboratory on multiple occasions. In a randomized order, subjects performed either the cognitive fatigue task (AX Continuous Performance Test; AX-CPT) for 60 min on one visit (experimental condition) or watched a video on trains for 60 min on the other visit (control condition). After each condition, subjects performed the incremental single-leg knee-extensor ergometry test while the EMG amplitude was recorded from the rectus femoris muscle and heart rate was monitored throughout. Thereafter, the EMGFT was calculated for each participant for each visit and compared using paired samples t-test. For exercise outcomes, there were no significant mean differences for maximal power output between the two conditions (control: 51 ± 5 vs. fatigue: 50 ± 3 W), but a significant decrease in EMGFT between the two conditions (control: 31 ± 3 vs. fatigue: 24 ± 2 W; p = 0.013). Moreover, maximal heart rate was significantly different between the two conditions (control: 151 ± 5 vs. fatigue: 132 ± 6; p = 0.027). These results suggest that performing the cognitive fatiguing task reduces the EMGFT with a corresponding reduction in maximal heart rate response.

Effects of Control Mode and R-Ratio on the Fatigue Behavior of a Metal Matrix Composite

NASA Technical Reports Server (NTRS)

2005-01-01

Composite Because of their high specific stiffness and strength at elevated temperatures, continuously reinforced metal matrix composites (MMC's) are under consideration for a future generation of aeropropulsion systems. Since components in aeropropulsion systems experience substantial cyclic thermal and mechanical loads, the fatigue behavior of MMC's is of great interest. Almost without exception, previous investigations of the fatigue behavior of MMC's have been conducted in a tension-tension, load-controlled mode. This has been due to the fact that available material is typically less than 2.5-mm thick and, therefore, unable to withstand high compressive loads without buckling. Since one possible use of MMC's is in aircraft skins, this type of testing mode may be appropriate. However, unlike aircraft skins, most engine components are thick. In addition, the transient thermal gradients experienced in an aircraft engine will impose tension-compression loading on engine components, requiring designers to understand how the MMC will behave under fully reversed loading conditions. The increased thickness of the MMC may also affect the fatigue life. Traditionally, low-cycle fatigue (LCF) tests on MMC's have been performed in load control. For monolithic alloys, low-cycle fatigue tests are more typically performed in strain control. Two reasons justify this choice: (1) the critical volume from which cracks initiate and grow is generally small and elastically constrained by the larger surrounding volume of material, and (2) load-controlled, low-cycle fatigue tests of monolithics invariably lead to unconstrained ratcheting and localized necking--an undesired material response because the failure mechanism is far more severe than, and unrelated to, the fatigue mechanism being studied. It is unknown if this is the proper approach to composite testing. However, there is a lack of strain-controlled data on which to base any decisions. Consequently, this study addresses the isothermal, LCF behavior of a [0]_32 MMC tested under strain- and load-controlled conditions for both zero-tension and tension-compression loading conditions. These tests were run at 427 C on thick specimens of SiC-reinforced Ti-15-3. For the fully-reversed tests, no difference was observed in the lives between the load- and strain-controlled tests. However, for the zero-tension tests, the strain-controlled tests had longer lives by a factor of 3 in comparison to the load-controlled tests. This was due to the fact that under strain-control the specimens cyclically softened, reducing the cracking potential. In contrast, the load-controlled tests ratcheted toward larger tensile strains leading to an eventual overload of the fibers. Fatigue tests revealed that specimens tested under fully-reversed conditions had lives approximately an order of magnitude longer than for those specimens tested under zero tension. When examined on a strain-range basis, the fully reversed specimens had similar, but still shorter lives than those of the unreinforced matrix material. However, the composite had a strain limitation at short lives because of the limited strain capacity of the brittle ceramic fiber. The composite also suffered at very high lives because of the lack of an apparent fatigue limit in comparison to the unreinforced matrix. The value of adding fibers to the matrix is apparent when the fatigue lives are plotted as a function of stress range. Here, the composite is far superior to the unreinforced matrix because of the additional load-carrying capacity of the fibers.

Repeatability of testing procedures for resilient modulus and fatigue.

DOT National Transportation Integrated Search

1989-04-01

Extensive use of diametral resilient modulus and fatigue testing is made by the Oregon State Highway Division to evaluate asphaltic concrete materials. Test results on similar materials (e.g., adjacent field cores), however, often indicate a poor lev...

A microstructurally based model of solder joints under conditions of thermomechanical fatigue

DOE Office of Scientific and Technical Information (OSTI.GOV)

Frear, D.R.; Burchett, S.N.; Rashid, M.M.

The thermomechanical fatigue failure of solder joints in increasingly becoming an important reliability issue. In this paper we present two computational methodologies that have been developed to predict the behavior of near eutectic Sn-Pb solder joints under fatigue conditions that are based on metallurgical tests as fundamental input for constitutive relations. The two-phase model mathematically predicts the heterogeneous coarsening behavior of near eutectic Sn-Pb solder. The finite element simulations from this model agree well with experimental thermomechanical fatigue tests. The simulations show that the presence of an initial heterogeneity in the solder microstructure could significantly degrade the fatigue lifetime. Themore » single phase model is a computational technique that was developed to predict solder joint behavior using materials data for constitutive relation constants that could be determined through straightforward metallurgical experiments. A shear/torsion test sample was developed to impose strain in two different orientations. Materials constants were derived from these tests and the results showed an adequate fit to experimental results. The single-phase model could be very useful for conditions where microstructural evolution is not a dominant factor in fatigue.« less

Effect of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate. [for aerospace applications

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1984-01-01

The effects of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate at frequencies of 1 Hz and 10 Hz were investigated. Twenty-five mm thick compact specimens were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Fatigue crack growth rates were calculated from effective crack lengths determined using a compliance method. Tests were conducted in hard vacuum and at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. Fatigue crack growth rates were frequency insensitive under all environment conditions tested. For constant stress intensity factor ranges crack growth rate transitions occurred at low and high water vapor pressures. Crack growth rates at intermediate pressures were relatively constant and showed reasonable agreement with published data for two Al-Cu-Mg alloys. The existence of two crack growth rate transitions suggests either a change in rate controlling kinetics or a change in corrosion fatigue mechanism as a function of water vapor pressure. Reduced residual deformation and transverse cracking specimens tested in water vapor versus vacuum may be evidence of embrittlement within the plastic zone due to environmental interaction.

The effect of water vapor on fatigue crack Growth in 7475-t651 aluminum alloy plate. [for aerospace applications

NASA Technical Reports Server (NTRS)

Dicus, D. L.

1982-01-01

The effects of water vapor on fatigue crack growth in 7475-T651 aluminum alloy plate at frequencies of 1 Hz and 10 Hz were investigated. Twenty-five mm thick compact specimens were subjected to constant amplitude fatigue testing at a load ratio of 0.2. Fatigue crack growth rates were calculated from effective crack lengths determined using a compliance method. Tests were conducted in hard vacuum and at water vapor partial pressures ranging from 94 Pa to 3.8 kPa. Fatigue crack growth rates were frequency insensitive under all environment conditions tested. For constant stress intensity factor ranges crack growth rate transitions occurred at low and high water vapor pressures. Crack growth rates at intermediate pressures were relatively constant and showed reasonable agreement with published data for two Al-Cu-Mg alloys. The existence of two crack growth rate transitions suggests either a change in rate controlling kinetics or a change in corrosion fatigue mechanism as a function of water vapor pressure. Reduced residual deformation and transverse cracking specimens tested in water vapor versus vacuum may be evidence of embrittlement within the plastic zone due to environmental interaction.

Sensing sheets based on large area electronics for fatigue crack detection

NASA Astrophysics Data System (ADS)

Yao, Yao; Glisic, Branko

2015-03-01

Reliable early-stage damage detection requires continuous structural health monitoring (SHM) over large areas of structure, and with high spatial resolution of sensors. This paper presents the development stage of prototype strain sensing sheets based on Large Area Electronics (LAE), in which thin-film strain gauges and control circuits are integrated on the flexible electronics and deposited on a polyimide sheet that can cover large areas. These sensing sheets were applied for fatigue crack detection on small-scale steel plates. Two types of sensing-sheet interconnects were designed and manufactured, and dense arrays of strain gauge sensors were assembled onto the interconnects. In total, four (two for each design type) strain sensing sheets were created and tested, which were sensitive to strain at virtually every point over the whole sensing sheet area. The sensing sheets were bonded to small-scale steel plates, which had a notch on the boundary so that fatigue cracks could be generated under cyclic loading. The fatigue tests were carried out at the Carleton Laboratory of Columbia University, and the steel plates were attached through a fixture to the loading machine that applied cyclic fatigue load. Fatigue cracks then occurred and propagated across the steel plates, leading to the failure of these test samples. The strain sensor that was close to the notch successfully detected the initialization of fatigue crack and localized the damage on the plate. The strain sensor that was away from the crack successfully detected the propagation of fatigue crack based on the time history of measured strain. Overall, the results of the fatigue tests validated general principles of the strain sensing sheets for crack detection.

Temporal profile of prolonged, night-time driving performance: breaks from driving temporarily reduce time-on-task fatigue but not sleepiness.

PubMed

Phipps-Nelson, Jo; Redman, Jennifer R; Rajaratnam, Shantha M W

2011-09-01

Breaks are often used by drivers to counteract sleepiness and time-on-task fatigue during prolonged driving. We examined the temporal profile of changes in driving performance, electroencephalogram (EEG) activity and subjective measures of sleepiness and fatigue during prolonged nocturnal driving in a car simulator. In addition, the study examined the impact of regular breaks from driving on performance, sleepiness and fatigue. Healthy volunteers (n=12, 23-45 years) maintained a regular sleep-wake pattern for 14 days and were then in a laboratory from 21:00 to 08:30 hours. The driving simulator scene was designed to simulate monotonous night-time rural driving. Participants drove 4 × 2-h test sessions, with a break from driving of 1 h between each session. During the break participants performed tests assessing sleepiness and fatigue, and psychomotor performance (~30 mins), and then were permitted to sit quietly. They were monitored for wakefulness, and not permitted to nap or ingest caffeine. EEG was recorded during the driving task, and subjective assessments of sleepiness and fatigue were obtained at the start and completion of each session. We found that driving performance deteriorated (2.5-fold), EEG delta, theta and alpha activity increased, and subjective sleepiness and fatigue ratings increased across the testing period. Driving performance and fatigue ratings improved following the scheduled breaks from driving, while the breaks did not affect EEG activity and subjective sleepiness. Time-on-task effects increased through the testing period, indicating that these effects are exacerbated by increasing sleepiness. Breaks from driving without sleep temporarily ameliorate time-on-task fatigue, but provide little benefit to the sleepy driver. © 2010 European Sleep Research Society.

A study on setting of the fatigue limit of temporary dental implants.

PubMed

Kim, M H; Cho, E J; Lee, J W; Kim, E K; Yoo, S H; Park, C W

2017-07-01

A temporary dental implant is a medical device which is temporarily used to support a prosthesis such as an artificial tooth used for restoring patient's masticatory function during implant treatment. It is implanted in the oral cavity to substitute for the role of tooth. Due to the aging and westernization of current Korean society, the number of tooth extraction and implantation procedures is increasing, leading to an increase in the use and development of temporary dental implants. Because an implant performs a masticatory function in place of a tooth, a dynamic load is repeatedly put on the implant. Thus, the fatigue of implants is reported to be the most common causes of the fracture thereof. According to the investigation and analysis of the current domestic and international standards, the standard for fatigue of implant fixtures is not separately specified. Although a test method for measuring the fatigue is suggested in an ISO standard, it is a standard for permanent dental implants. Most of the test standards for Korean manufacturers and importers apply 250 N or more based on the guidance for the safety and performance evaluation of dental implants. Therefore, this study is intended to figure out the fatigue standard which can be applied to temporary dental implants when measuring the fatigue according to the test method suggested in the permanent dental implant standard. The results determined that suitable fatigue standards of temporary dental implants should be provided by each manufacturer rather than applying 250 N. This study will be useful for the establishment of the fatigue standards and fatigue test methods of the manufacturers and importers of temporary dental implants.

Behavior of Fatigue Crack Tip Opening in Air and Corrosive Atmosphere

NASA Astrophysics Data System (ADS)

Hayashi, Morihito; Toeda, Kazunori

In the study, a formula for predicting fatigue crack tip opening displacement is deduced firstly. And then, due to comparing actual crack growth rate with the deduced formula, the crack tip configuration factor is defined to figure out the crack tip opening configuration that is useful to clarify the behavior of fatigue crack tip formation apparently. Applying the concept, the crack growth of 7/3 brass and 6/4 brass is predicted from the formula, by replacing material properties such as plastic flow resistance, Young modulus, the Poisson ratio, and fatigue toughness, and fatigue test conditions such as the stress intensity factor range, the load ratio, and cycle frequency. Furthermore, the theoretically expected results are verified with the fatigue tests which were carried out on CT specimens under different load conditions of load ratio, cycle frequency, and cyclic peak load, in different environments of air or corrosive ammonia atmosphere, for various brasses. And by comparing and discussing the calculated crack growth rate with attained experimental results, the apparent configuration factor at the crack tip is determined. And through the attained factor which changes along with crack growth, the behaviors of fatigue crack tip formation under different test conditions have been found out.

A Study on Fretting Behavior in Room Temperature for Inconel Alloy 690

NASA Astrophysics Data System (ADS)

Kwon, Jae Do; Chai, Young Suck; Bae, Yong Tak; Choi, Sung Jong

The initial crack under fretting condition occurs at lower stress amplitude and lower cycles of cyclic loading than that under plain fatigue condition. The fretting damage, for example, can be observed in fossil and nuclear power plant, aircraft, automobile and petroleum chemical plants etc. INCONEL alloy 690 is a high-chromium nickel alloy having excellent resistance to many corrosive aqueous media and high-temperature atmospheres. This alloy is used extensively in the industries of nuclear power, chemicals, heat-treatment and electronics. In this paper, the effect of fretting damage on fatigue behavior for INCONEL alloy 690 was studied. Also, various kinds of tests on mechanical properties such as hardness, tension and plain fatigue tests are performed. Fretting fatigue tests were carried out with flat-flat contact configuration using a bridge type contact pad and plate type specimen. Through these experiments, it is found that the fretting fatigue strength decreased about 43% compared to the plain fatigue strength. In fretting fatigue, the wear debris is observed on the contact surface, and the oblique micro-cracks are initiated at an earlier stage. These results can be used as the basic data in a structural integrity evaluation of heat and corrosion resistant alloy considering fretting damages.

Ferrographic analysis of wear debris generated in accelerated rolling element fatigue tests

NASA Technical Reports Server (NTRS)

Jones, W. R., Jr.; Parker, R. J.

1977-01-01

Ferrographic analysis was used to determine the types and quantities of wear particles generated during accelerated rolling contact fatigue tests. The NASA five-ball rolling contact fatigue tester was used. Ball specimens were made of AMS 5749, a corrosion-resistant high-temperature bearing steel. The lubricant was a super-refined naphthenic mineral oil. Conditions included a maximum Hertz stress of 5.52 billion Pa and a shaft speed of 10,000 rpm. Four types of wear particles were observed: normal rubbing wear particles, fatigue spall particles, spheres, and friction polymer.

Visualization of Lamb Wave Interaction with a 5 mm Fatigue Crack using 1D Ultra High Frequency Laser Doppler Vibrometry

DTIC Science & Technology

2011-09-01

detection of a fatigue crack via 3D LDV measurements, both in aluminum plates. All the referenced LDV/guided wave studies made use of PZT or similar...Figure 1a). (b) (a) (c) Figure 1: (a) Test specimen in MTS fatigue test machine, (b) hole with 5 mm crack, (c) PZT placement with...mm thick aluminum plates with a small (1.59 mm) center hole added to facilitate growth of a fatigue crack. One plate was left undamaged while the

Cyclic fatigue analysis of rocket thrust chambers. Volume 1: OFHC copper chamber low cycle fatigue

NASA Technical Reports Server (NTRS)

Miller, R. W.

1974-01-01

A three-dimensional finite element elasto-plastic strain analysis was performed for the throat section of a regeneratively cooled rocket combustion chamber. The analysis employed the RETSCP finite element computer program. The analysis included thermal and pressure loads, and the effects of temperature dependent material properties, to determine the strain range corresponding to the chamber operating cycle. The analysis was performed for chamber configuration and operating conditions corresponding to a hydrogen-oxygen combustion chamber which was fatigue tested to failure. The computed strain range at typical chamber operating conditions was used in conjunction with oxygen-free, high-conductivity (OHFC) copper isothermal fatigue test data to predict chamber low-cycle fatigue life.

The effect of residual stresses induced by prestraining on fatigue life of notched specimens

NASA Astrophysics Data System (ADS)

Sadeler, R.; Ozel, A.; Kaymaz, I.; Totik, Y.

2005-06-01

The effect of tensile prestraining-induced residual stress on the fatigue life of notched steel parts was investigated. The study was performed on AISI 4140 steel. Rotating bending fatigue tests were carried out on semicircular notched specimens with different notch radii in the as-quenched and tempered conditions. Metallography of the specimens was performed by means of light optical microscopy. The finite-element method was used to evaluate the residual stress distribution near the notch region. Fatigue tests revealed fatigue life improvement for notched specimens, which changes depending on the notch radii and applied stress. Scanning electron microscopy was used to examine the fracture surfaces of the specimens.

The application of probabilistic design theory to high temperature low cycle fatigue

NASA Technical Reports Server (NTRS)

Wirsching, P. H.

1981-01-01

Metal fatigue under stress and thermal cycling is a principal mode of failure in gas turbine engine hot section components such as turbine blades and disks and combustor liners. Designing for fatigue is subject to considerable uncertainty, e.g., scatter in cycles to failure, available fatigue test data and operating environment data, uncertainties in the models used to predict stresses, etc. Methods of analyzing fatigue test data for probabilistic design purposes are summarized. The general strain life as well as homo- and hetero-scedastic models are considered. Modern probabilistic design theory is reviewed and examples are presented which illustrate application to reliability analysis of gas turbine engine components.

Electromyographic fatigue of orbicular oris muscles during exercises in mouth and nasal breathing children.

PubMed

Busanello-Stella, Angela Ruviaro; Blanco-Dutra, Ana Paula; Corrêa, Eliane Castilhos Rodrigues; Silva, Ana Maria Toniolo da

2015-01-01

To investigate the process of fatigue in orbicularis oris muscles by analyzing the median frequency of electromyographic signal and the referred fatigue time, according to the breathing mode and the facial pattern. The participants were 70 children, aged 6 to 12 years, who matched the established criteria. To be classified as 36 nasal-breathing and 34 mouth-breathing children, they underwent speech-language, otorhinolaryngologic, and cephalometric evaluation. For the electromyographic assessment, the children had to sustain lip dumbbells weighing 40, 60, and 100 g and a lip exerciser, until the feeling of fatigue. Median frequency was analyzed in 5, 10, 15, and 20 seconds of activity. The referred time of the feeling of fatigue was also recorded. Data were analyzed through the analysis of variance--repeated measures (post hoc Tukey's test), Kruskal-Wallis test, and Mann-Whitney U-test. A significant decrease in the median frequency from 5 seconds of activity was observed, independently from the comparison between the groups. On comparison, the muscles did not show significant decrease. The reported time for the feeling of fatigue was shorter for mouth-breathing individuals. This feeling occurred after the significant decrease in the median frequency. There were signals that indicated myoelectric fatigue for the orbicularis oris muscles, in both groups analyzed, from the first 5 seconds of activity. Myoelectric fatigue in the orbicularis oris muscles preceded the reported feeling of fatigue in all groups. The account for fatigue time was influenced by only the breathing pattern, occurring more precociously in mouth-breathing children.

Scatter of fatigue data owing to material microscopic effects

NASA Astrophysics Data System (ADS)

Tang, XueSong

2014-01-01

A common phenomenon of fatigue test data reported in the open literature such as S-N curves exhibits the scatter of points for a group of same specimens under the same loading condition. The reason is well known that the microstructure is different from specimen to specimen even in the same group. Specifically, a fatigue failure process is a multi-scale problem so that a fatigue failure model should have the ability to take the microscopic effect into account. A physically-based trans-scale crack model is established and the analytical solution is obtained by coupling the micro- and macro-scale. Obtained is the trans-scale stress intensity factor as well as the trans-scale strain energy density (SED) factor. By taking this trans-scale SEDF as a key controlling parameter for the fatigue crack propagation from micro- to macro-scale, a trans-scale fatigue crack growth model is proposed in this work which can reflect the microscopic effect and scale transition in a fatigue process. The fatigue test data of aluminum alloy LY12 plate specimens is chosen to check the model. Two S-N experimental curves for cyclic stress ratio R=0.02 and R=0.6 are selected. The scattering test data points and two S-N curves for both R=0.02 and R=0.6 are exactly re-produced by application of the proposed model. It is demonstrated that the proposed model is able to reflect the multiscaling effect in a fatigue process. The result also shows that the microscopic effect has a pronounced influence on the fatigue life of specimens.

Electrophysiological and behavioral effects of frontal transcranial direct current stimulation on cognitive fatigue in multiple sclerosis.

PubMed

Fiene, Marina; Rufener, Katharina S; Kuehne, Maria; Matzke, Mike; Heinze, Hans-Jochen; Zaehle, Tino

2018-03-01

Fatigue is one of the most common and debilitating symptoms affecting patients with multiple sclerosis (MS). Sustained cognitive effort induces cognitive fatigue, operationalized as subjective exhaustion and fatigue-related objective alertness decrements with time-on-task. During prolonged cognitive testing, MS patients show increased simple reaction times (RT) accompanied by lower amplitudes and prolonged latencies of the P300 event-related potential. Previous studies suggested a major role of structural and functional abnormalities in the frontal cortex including a frontal hypo-activation in fatigue pathogenesis. In the present study we investigated the neuromodulatory effect of transcranial direct current stimulation (tDCS) over the left dorsolateral prefrontal cortex (DLPFC) on objective measures of fatigue-related decrements in cognitive performance in MS patients. P300 during an auditory oddball task and simple reaction times in an alertness test were recorded at baseline, during and after stimulation. Compared to sham, anodal tDCS caused an increase in P300 amplitude that persisted after the end of stimulation and eliminated the fatigue-related increase in RT over the course of a testing session. Our findings demonstrate that anodal tDCS over the left DLPFC can counteract performance decrements associated with fatigue thereby leading to an improvement in the patient's ability to cope with sustained cognitive demands. This provides causal evidence for the functional relevance of the left DLPFC in fatigue pathophysiology. The results indicate that tDCS-induced modulations of frontal activity can be an effective therapeutic option for the treatment of fatigue-related declines in cognitive performance in MS patients.

Accceleration of Fatigue Tests of Polymer Composite Materials by Using High-Frequency Loadings

NASA Astrophysics Data System (ADS)

Apinis, R.

2004-03-01

The possibility of using high-frequency loading in fatigue tests of polymer composite materials is discussed. A review of studies on the use of high-frequency loading of organic-, carbon-, and glass-fiber-reinforced plastics is presented. The results obtained are compared with those found in conventional low-frequency loadings. A rig for fatigue tests of rigid materials at loading frequencies to 500 Hz is described, and results for an LM-L1 unidirectional glass-fiber plastic in loadings with frequencies of 17 and 400 Hz are given. These results confirm that it is possible to accelerate the fatigue testing of polymer composite materials by considerably increasing the loading frequency. The necessary condition for using this method is an intense cooling of specimens to prevent them from vibration heating.

Rolling-element fatigue life with traction fluids and automatic transmission fluid in a high-speed rolling-contact rig

NASA Technical Reports Server (NTRS)

Parker, R. J.; Nahm, A. H.; Loewenthal, S. H.

1982-01-01

Rolling-element fatigue tests were run in standard and high-speed rolling-contact rigs at bar speeds from 5000 to 50,000 rpm to determine the effects of speed and lubricant film parameter on rolling-element fatigue life. AISI 52100 test bars were tested at a maximum Hertz stress of 4.83 GPa (700,000 psi) with three traction fluids and an automatic transmission fluid. Rolling-element fatigue life increased with speed, with the greatest increases occurring from 10,000 to 50,000 rpm. The life data tended to follow published life-versus-lubricant-film-parameter data up to a film parameter of approximately 3.

The effect of fatigue on the corrosion resistance of common medical alloys.

PubMed

Di Prima, Matthew; Gutierrez, Erick; Weaver, Jason D

2017-10-01

The effect of mechanical fatigue on the corrosion resistance of medical devices has been a concern for devices that experience significant fatigue during their lifespan and devices made from metallic alloys. The Food and Drug Administration had recommended in some instances for corrosion testing to be performed on post-fatigued devices [Non-clinical tests and recommended labeling for intravascular stents and associated delivery systems: guidance for industry and FDA staff. 2005: Food and Drug Administration, Center for Devices and Radiological Health], although the need for this has been debated [Nagaraja S, et al., J Biomed Mater Res Part B: Appl Biomater 2016, 8.] This study seeks to evaluate the effect of fatigue on the corrosion resistance of 5 different materials commonly used in medical devices: 316 LVM stainless steel, MP35N cobalt chromium, electropolished nitinol, mechanically polished nitinol, and black oxide nitinol. Prior to corrosion testing per ASTM F2129, wires of each alloy were split into subgroups and subjected to either nothing (that is, as received); high strain fatigue for less than 8 min; short-term phosphate buffered saline (PBS) soak for less than 8 min; low strain fatigue for 8 days; or long-term PBS soak for 8 days. Results from corrosion testing showed that the rest potential trended to an equilibrium potential with increasing time in PBS and that there was no statistical (p > 0.05) difference in breakdown potential between the fatigued and matching PBS soak groups for 9 out of 10 test conditions. Our results suggest that under these nonfretting conditions, corrosion susceptibility as measured by breakdown potential per ASTM F2129 was unaffected by the fatigue condition. 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 2019-2026, 2017. Published 2016. This article is a U.S. Government work and is in the public domain in the USA.

Development of a plasma sprayed ceramic gas path seal for high pressure turbine applications

NASA Technical Reports Server (NTRS)

Shiembob, L. T.

1977-01-01

The plasma sprayed graded layered yittria stabilized zirconia (ZrO2)/metal(CoCrAlY) seal system for gas turbine blade tip applications up to 1589 K (2400 F) seal temperatures was studied. Abradability, erosion, and thermal fatigue characteristics of the graded layered system were evaluated by rig tests. Satisfactory abradability and erosion resistance was demonstrated. Encouraging thermal fatigue tolerance was shown. Initial properties for the plasma sprayed materials in the graded, layered seal system was obtained, and thermal stress analyses were performed. Sprayed residual stresses were determined. Thermal stability of the sprayed layer materials was evaluated at estimated maximum operating temperatures in each layer. Anisotropic behavior in the layer thickness direction was demonstrated by all layers. Residual stresses and thermal stability effects were not included in the analyses. Analytical results correlated reasonably well with results of the thermal fatigue tests. Analytical application of the seal system to a typical gas turbine engine application predicted performance similar to rig specimen thermal fatigue performance. A model for predicting crack propagation in the sprayed ZrO2/CoCrAlY seal system was proposed, and recommendations for improving thermal fatigue resistance were made. Seal system layer thicknesses were analytically optimized to minimize thermal stresses in the abradability specimen during thermal fatigue testing. Rig tests on the optimized seal configuration demonstrated some improvement in thermal fatigue characteristics.

In-phase and out-of-phase axial-torsional fatigue behavior of Haynes 188 at 760 C

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Bonacuse, Peter J.

1991-01-01

Isothermal, in-phase and out-of-phase axial-torsional fatigue experiments have been conducted at 760 C on uniform gage section, thin-walled tubular specimens of a wrought cobalt-base superalloy, Haynes 188. Test-control and data acquisition were accomplished with a minicomputer. Fatigue lives of the in- and out-of-phase axial-torsional fatigue tests have been estimated with four different multiaxial fatigue life prediction models that were developed primarly for predicting axial-torsional fatigue lives at room temperature. The models investigated were: (1) the von Mises equivalent strain range; (2) the Modified Multiaxiality Factor Approach; (3) the Modified Smith-Watson-Topper Parameter; and (4) the critical shear plane method of Fatemi, Socie, and Kurath. In general, life predictions by the von Mises equivalent strain range model were within a factor of 2 for a majority of the tests and the predictions by the Modified Multiaxiality Factor Approach were within a factor of 2, while predictions of the Modified Smith-Watson-Topper Parameter and of the critical shear plane method of Fatemi, Socie, and Kurath were unconservative and conservative, respectively, by up to factors of 4. In some of the specimens tested under combined axial-torsional loading conditions, fatigue cracks initiated near extensometer indentations. Two design modifications have been proposed to the thin-walled tubular specimen to overcome this problem.

Viscoelastic and fatigue properties of model methacrylate-based dentin adhesives

PubMed Central

Singh, Viraj; Misra, Anil; Marangos, Orestes; Park, Jonggu; Ye, Qiang; Kieweg, Sarah L.; Spencer, Paulette

2013-01-01

The objective of the current study is to characterize the viscoelastic and fatigue properties of model methacrylate-based dentin adhesives under dry and wet conditions. Static, creep, and fatigue tests were performed on cylindrical samples in a 3-point bending clamp. Static results showed that the apparent elastic modulus of the model adhesive varied from 2.56 to 3.53 GPa in the dry condition, and from 1.04 to 1.62 GPa in the wet condition, depending upon the rate of loading. Significant differences were also found for the creep behavior of the model adhesive under dry and wet conditions. A linear viscoelastic model was developed by fitting the adhesive creep behavior. The developed model with 5 Kelvin Voigt elements predicted the apparent elastic moduli measured in the static tests. The model was then utilized to interpret the fatigue test results. It was found that the failure under cyclic loading can be due to creep or fatigue, which has implications for the failure criterion that are applied for these types of tests. Finally, it was found that the adhesive samples tested under dry conditions were more durable than those tested under wet conditions. PMID:20848661

The detection of tightly closed flaws by nondestructive testing (NDT) methods. [fatigue crack formation in aluminum alloy test specimens

NASA Technical Reports Server (NTRS)

Rummel, W. D.; Rathke, R. A.; Todd, P. H., Jr.; Mullen, S. J.

1975-01-01

Liquid penetrant, ultrasonic, eddy current and X-radiographic techniques were optimized and applied to the evaluation of 2219-T87 aluminum alloy test specimens in integrally stiffened panel, and weld panel configurations. Fatigue cracks in integrally stiffened panels, lack-of-fusion in weld panels, and fatigue cracks in weld panels were the flaw types used for evaluation. A 2319 aluminum alloy weld filler rod was used for all welding to produce the test specimens. Forty seven integrally stiffened panels containing a total of 146 fatigue cracks, ninety three lack-of-penetration (LOP) specimens containing a total of 239 LOP flaws, and one-hundred seventeen welded specimens containing a total of 293 fatigue cracks were evaluated. Nondestructive test detection reliability enhancement was evaluated during separate inspection sequences in the specimens in the 'as-machined or as-welded', post etched and post proof loaded conditions. Results of the nondestructive test evaluations were compared to the actual flaw size obtained by measurement of the fracture specimens after completing all inspection sequences. Inspection data were then analyzed to provide a statistical basis for determining the flaw detection reliability.

Implementation of a Biaxial Resonant Fatigue Test Method on a Large Wind Turbine Blade

DOE Office of Scientific and Technical Information (OSTI.GOV)

Snowberg, D.; Dana, S.; Hughes, S.

2014-09-01

A biaxial resonant test method was utilized to simultaneously fatigue test a wind turbine blade in the flap and edge (lead-lag) direction. Biaxial resonant blade fatigue testing is an accelerated life test method utilizing oscillating masses on the blade; each mass is independently oscillated at the respective flap and edge blade resonant frequency. The flap and edge resonant frequency were not controlled, nor were they constant for this demonstrated test method. This biaxial resonant test method presented surmountable challenges in test setup simulation, control and data processing. Biaxial resonant testing has the potential to complete test projects faster than single-axismore » testing. The load modulation during a biaxial resonant test may necessitate periodic load application above targets or higher applied test cycles.« less

Fatigue In Continuous-Fiber/Metal-Matrix Composites

NASA Technical Reports Server (NTRS)

Johnson, William S.

1992-01-01

Report describes experimental approaches to quantification of fatigue damage in metal-matrix composites (MMC's). Discusses number of examples of development of damage and failure along with associated analytical models of behavior of MMC. Objectives of report are twofold. First, present experimental procedures and techniques for conducting meaningful fatigue tests to detect and quantify fatigue damage in MMC's. Second, present examples of how fatigue damage initiated and grows in various MMC's. Report furnishes some insight into what type of fatigue damage occurs and how damage quantified.

Fatigue Behavior of an Advanced SiC/SiC Composite at Elevated Temperature in Air and in Steam

DTIC Science & Technology

2009-12-01

specimens tested in salt fog achieved fatigue run-out. However, a significant decrease in fatigue life was observed for fatigue stresses ≥ 100 MPa...fatigue stress level approached the proportional limit. The reduction is fatigue life was attributed to the increased matrix cracking near the...oxidation of any free silicon remaining after production using methods such as melt infiltration, and the SiC itself as temperatures near 1000 ºC. These

Fatigue testing of galvanized and ungalvanized socket connections.

DOT National Transportation Integrated Search

2014-09-01

The fatigue resistance of welded traffic signal support structure details is an ongoing research topic being : addressed at multiple universities primarily through state funding mechanisms. Fatigue problems with these : structures have plagued multip...

Low-Cycle Fatigue Behavior of Die-Cast Mg Alloy AZ91

NASA Astrophysics Data System (ADS)

Rettberg, Luke; Anderson, Warwick; Jones, J. Wayne

An investigation has been conducted on the influence of microstructure and artificial aging response (T6) on the low-cycle fatigue behavior of super vacuum die-cast (SVDC) AZ91. Fatigue lifetimes were determined from total strain-controlled fatigue tests for strain amplitudes of 0.2%, 0.4% and 0.6%, under fully reversed loading at a frequency of 5 Hz. Cyclic stress-strain behavior was determined using incremental step test (IST) methods. Two locations in a prototype casting with different thicknesses and, therefore, solidification rates, microstructure and porosity, were examined. In general., at all total strain amplitudes fatigue life was unaffected by microstructure refinement and was attributed to significant levels of porosity. Cyclic softening and a subsequent increased cyclic hardening rate, compared to monotonic tests, were observed, independent of microstructure. These results, fractography and damage accumulation processes, determined from metallographic sectioning, are discussed.

Fatigue Crack Closure Analysis Using Digital Image Correlation

NASA Technical Reports Server (NTRS)

Leser, William P.; Newman, John A.; Johnston, William M.

2010-01-01

Fatigue crack closure during crack growth testing is analyzed in order to evaluate the critieria of ASTM Standard E647 for measurement of fatigue crack growth rates. Of specific concern is remote closure, which occurs away from the crack tip and is a product of the load history during crack-driving-force-reduction fatigue crack growth testing. Crack closure behavior is characterized using relative displacements determined from a series of high-magnification digital images acquired as the crack is loaded. Changes in the relative displacements of features on opposite sides of the crack are used to generate crack closure data as a function of crack wake position. For the results presented in this paper, remote closure did not affect fatigue crack growth rate measurements when ASTM Standard E647 was strictly followed and only became a problem when testing parameters (e.g., load shed rate, initial crack driving force, etc.) greatly exceeded the guidelines of the accepted standard.

Is the impact of fatigue related to walking capacity and perceived ability in persons with multiple sclerosis? A multicenter study.

PubMed

Dalgas, U; Langeskov-Christensen, M; Skjerbæk, A; Jensen, E; Baert, I; Romberg, A; Santoyo Medina, C; Gebara, B; Maertens de Noordhout, B; Knuts, K; Béthoux, F; Rasova, K; Severijns, D; Bibby, B M; Kalron, A; Norman, B; Van Geel, F; Wens, I; Feys, P

2018-04-15

The relationship between fatigue impact and walking capacity and perceived ability in patients with multiple sclerosis (MS) is inconclusive in the existing literature. A better understanding might guide new treatment avenues for fatigue and/or walking capacity in patients with MS. To investigate the relationship between the subjective impact of fatigue and objective walking capacity as well as subjective walking ability in MS patients. A cross-sectional multicenter study design was applied. Ambulatory MS patients (n = 189, age: 47.6 ± 10.5 years; gender: 115/74 women/men; Expanded Disability Status Scale (EDSS): 4.1 ± 1.8 [range: 0-6.5]) were tested at 11 sites. Objective tests of walking capacity included short walking tests (Timed 25-Foot Walk (T25FW), 10-Metre Walk Test (10mWT) at usual and fastest speed and the timed up and go (TUG)), and long walking tests (2- and 6-Minute Walk Tests (MWT). Subjective walking ability was tested applying the Multiple Sclerosis Walking Scale-12 (MSWS-12). Fatigue impact was measured by the self-reported modified fatigue impact scale (MFIS) consisting of a total score (MFIS total ) and three subscales (MFIS physical , MFIS cognitive and MFIS psychosocial ). Uni- and multivariate regression analysis were performed to evaluate the relation between walking and fatigue impact. MFIS total was negatively related with long (6MWT, r = -0.14, p = 0.05) and short composite (TUG, r = -0.22, p = 0.003) walking measures. MFIS physical showed a significant albeit weak relationship to walking speed in all walking capacity tests (r = -0.22 to -0.33, p < .0001), which persisted in the multivariate linear regression analysis. Subjective walking ability (MSWS-12) was related to MFIS total (r = 0.49, p < 0.0001), as well as to all other subscales of MFIS (r = 0.24-0.63, p < 0.001), showing stronger relationships than objective measures of walking. The physical impact of fatigue is weakly related to objective walking capacity, while general, physical, cognitive and psychosocial fatigue impact are weakly to moderately related to subjective walking ability, when analysed in a large heterogeneous sample of MS patients. Copyright © 2018 Elsevier B.V. All rights reserved.

Metal Matrix Composites: Fatigue and Fracture Testing. (Latest citations from the Aerospace Database)

NASA Technical Reports Server (NTRS)

1996-01-01

The bibliography contains citations concerning techniques and results of testing metal matrix composites for fatigue and fracture. Methods include non-destructive testing techniques, and static and cyclic techniques for assessing compression, tensile, bending, and impact characteristics.

Bearingless helicopter main rotor development. Volume 2: Combined load fatigue evaluation of weathered graphite/epoxy composite

NASA Technical Reports Server (NTRS)

Rackiewicz, J. J.

1977-01-01

Small scale combined load fatigue tests were conducted on six artificially and six naturally weathered test specimens. The test specimen material was unidirectionally oriented A-S graphite - woven glass scrim epoxy resin laminate.

Fatigue Testing of Vampire Wings,

DTIC Science & Technology

1979-06-01

Fork End Upper (Threaded) Lug 2 Lower Root End Filling (R.E.F.) Through Inboard 8 mm (?4 in.) Dia . Bolt Holes. STA.747 (Fig.15) 3 Main Spar Assembl’ at...AD-AOA9 402 AERONAUTICAL RESEARCH LABS MELBOURNE (AUSTRALIA) F/G 1/ 3 FATIGUE TESTING OF VAMPIRE WINGS.(U) JUN 79 R A BRUTON. C A PATCHING...Number: (c) Summary in Isolation: ARL-Struc.-Report-378 Unclassified 3 . Title: FATIGUE TESTING OF VAMPIRE WINGS 4. Personal Author(s): 5. Document Date

Fatigue Testing of Wing Beam by the Resonance Method

NASA Technical Reports Server (NTRS)

Bleakney, William M

1938-01-01

Preliminary fatigue tests on two aluminum-alloy wing-beam specimens subjected to reversed axial loading are described. The motion used consists in incorporating one or two reciprocating motors in a resonance system of which the specimen is the spring element. A description is given of the reciprocating motors, and of the method of assembling and adjusting the vibrating system. The results indicate that the method is well adapted to fatigue tests of not only uniform wing beams but also wing beams with asymmetrical local reinforcements.

Elasto-Plastic 3D Finite Element Contact Analysis of a Hole Containing a Circular Insert in a Fatigue Test Coupon

DTIC Science & Technology

2015-08-01

primarily concerned with the results of a three-dimensional elasto– plastic finite element contact analysis of a typical aluminium fatigue test coupon...determine the nonlinear three-dimensional elasto–plastic contact stress distributions around a circular hole in an aluminium plate that is fitted...Australian Air Force (RAAF) airframes. An aluminium -alloy fatigue test coupon (see Figure 1) has been designed and applied in support of the validation of

Nonlinear Fatigue Damage Model Based on the Residual Strength Degradation Law

NASA Astrophysics Data System (ADS)

Yongyi, Gao; Zhixiao, Su

In this paper, a logarithmic expression to describe the residual strength degradation process is developed in order to fatigue test results for normalized carbon steel. The definition and expression of fatigue damage due to symmetrical stress with a constant amplitude are also given. The expression of fatigue damage can also explain the nonlinear properties of fatigue damage. Furthermore, the fatigue damage of structures under random stress is analyzed, and an iterative formula to describe the fatigue damage process is deduced. Finally, an approximate method for evaluating the fatigue life of structures under repeated random stress blocking is presented through various calculation examples.

Biomechanical Study of the Fixation Strength of Anteromedial Plating for Humeral Shaft Fractures

PubMed Central

Zheng, Yin-Feng; Zhou, Jun-Lin; Wang, Xiao-Hong; Shan, Lei; Liu, Yang

2016-01-01

Background: Open reduction and internal fixation with plate and screws are the gold standard for the surgical treatment of humeral shaft fractures, this study was to compare the mechanical properties of anteromedial, anterolateral, and posterior plating for humeral shaft fractures. Methods: A distal third humeral shaft fracture model was constructed using fourth-generation sawbones (#3404, composite bone). A total of 24 sawbones with a distal third humeral shaft fracture was randomly divided into three Groups: A, B, and C (n = 8 in each group) for anteromedial, anterolateral, and posterior plating, respectively. All sawbones were subjected to horizontal torsional fatigue tests, horizontal torsional and axial compressive fatigue tests, four-point bending fatigue tests in anteroposterior (AP) and mediolateral (ML) directions and horizontal torsional destructive tests. Results: In the horizontal torsional fatigue tests, the mean torsional angle amplitude in Groups A, B, and C were 6.12°, 6.53°, and 6.81°. In horizontal torsional and axial compressive fatigue tests, the mean torsional angle amplitude in Groups A, B, and C were 5.66°, 5.67°, and 6.36°. The mean plate displacement amplitude was 0.05 mm, 0.08 mm, and 0.10 mm. Group A was smaller than Group C (P < 0.05). In AP four-point bending fatigue tests, the mean plate displacement amplitude was 0.16 mm, 0.13 mm, and 0.20 mm. Group B was smaller than Group C (P < 0.05). In ML four-point bending fatigue tests, the mean plate displacement amplitude were 0.16 mm, 0.19 mm, and 0.17 mm. In horizontal torsional destructive tests, the mean torsional rigidity in Groups A, B, and C was 0.82, 0.75, and 0.76 N·m/deg. The yielding torsional angle was 24.50°, 25.70°, and 23.86°. The mean yielding torque was 18.46, 18.05, and 16.83 N·m, respectively. Conclusions: Anteromedial plating was superior to anterolateral or posterior plating in all mechanical tests except in AP four-point bending fatigue tests compared to the anterolateral plating group. We can suggest that anteromedial plating is a clinically safe and effective way for humeral shaft fractures. PMID:27453236

Failure and fatigue characteristics of adhesive athletic tape.

PubMed

Bragg, Richard W; Macmahon, John M; Overom, Erin K; Yerby, Scott A; Matheson, Gordon O; Carter, Dennis R; Andriacchi, Thomas P

2002-03-01

Athletic tape has been commonly reported to lose much of its structural support after 20 min of exercise. Although many studies have addressed the functional performance characteristics of athletic tape, its mechanical properties are poorly understood. This study examines the failure and fatigue properties of several commonly used athletic tapes. A Web-based survey of professional sports trainers was used to select the following three tapes for the study: Zonas (Johnson & Johnson), Leukotape (Beiersdorf), and Jaylastic (Jaybird & Mais). Using a hydraulic material testing system (MTS), eight samples of each tape were compared in three different mechanical tests: load-to-failure, fatigue testing under load control, and fatigue testing under displacement control. Differences in tape microstructure were used to interpret the results of the mechanical tests. Significant differences (P < 0.001) in failure load, elongation at failure, and stiffness were found from failure tests. Significant differences were also found (P < 0.001) in fatigue behavior under both modes of control. As a representative example, in one normalized displacement control fatigue test after 20 min of cycling, 21% (Zonas), 29% (Leukotape), and 57% (Jaylastic) of the mechanical support was lost. After cycling, all tapes loaded to failure showed increased stiffness (P < 0.001), indicating significant energy absorption during cycling. Observed differences in the tapes' microstructure were qualitatively consistent with the measured differences in their mechanical properties. In understanding the shortcomings of currently available tapes, the results of these tests can now be used as benchmarks with which to compare and develop future tape designs. Ultimately, these improved tapes should reduce ankle injuries among athletes.

Cognition, depression, fatigue, and quality of life in primary Sjögren's syndrome: correlations.

PubMed

Koçer, Belgin; Tezcan, Mehmet Engin; Batur, Hale Zeynep; Haznedaroğlu, Şeminur; Göker, Berna; İrkeç, Ceyla; Çetinkaya, Rümeysa

2016-12-01

The aim of the present study was to investigate the prevalence and pattern of cognitive dysfunction observed in primary Sjögren's syndrome (PSS) and to examine the relationships between cognitive abilities, depression, fatigue, and quality of life. Thirty-two subjects with PSS were compared with 19 healthy controls on comprehensive neuropsychological, depression, fatigue, health state, and daily-life activities tests. There was low performance in Clock Drawing, COWAT, Paced Auditory Serial Addition Test (PASAT), Colorless Word Reading (Stroop1) and Recognizing Colors (Stroop2) Patterns of STROOP test, SDLT, Auditory-Verbal Learning Test (AVLT), immediate and long-term verbal memory, Benton Judgment of Line Orientation Test (BJLOT), and in all the patterns of RCFT in PSS patients compared to the healthy control group ( p  < .05). It was observed an increased depression frequency and fatigue severity, impairment in health condition, and a decreased quality of life in PSS cases compared to the healthy controls ( p  < .05). All the depression, fatigue severity, and quality of life tests showed a significant positive correlation with each other ( p  < .05). A significant negative correlation between Clock Drawing and SF-36-BP ( p  = .031, r  = -.382) and SF-36-GH ( p  = .027, r  = -.392) was observed. Clock Drawing, PASAT, and AVLT are very useful tests to determine the subclinical and clinical cognitive dysfunction to evaluate attention, information processing speed, executive functions, and short-term and long-term verbal memory in PSS patients. Depression and fatigue may not affect the neuropsychological tests performance.

Computer simulation of solder joint failure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burchett, S.N.; Frear, D.R.; Rashid, M.M.

The thermomechanical fatigue failure of solder joints is increasingly becoming an important reliability issue for electronic packages. The purpose of this Laboratory Directed Research and Development (LDRD) project was to develop computational tools for simulating the behavior of solder joints under strain and temperature cycling, taking into account the microstructural heterogeneities that exist in as-solidified near eutectic Sn-Pb joints, as well as subsequent microstructural evolution. The authors present two computational constitutive models, a two-phase model and a single-phase model, that were developed to predict the behavior of near eutectic Sn-Pb solder joints under fatigue conditions. Unique metallurgical tests provide themore » fundamental input for the constitutive relations. The two-phase model mathematically predicts the heterogeneous coarsening behavior of near eutectic Sn-Pb solder. The finite element simulations with this model agree qualitatively with experimental thermomechanical fatigue tests. The simulations show that the presence of an initial heterogeneity in the solder microstructure could significantly degrade the fatigue lifetime. The single-phase model was developed to predict solder joint behavior using materials data for constitutive relation constants that could be determined through straightforward metallurgical experiments. Special thermomechanical fatigue tests were developed to give fundamental materials input to the models, and an in situ SEM thermomechanical fatigue test system was developed to characterize microstructural evolution and the mechanical behavior of solder joints during the test. A shear/torsion test sample was developed to impose strain in two different orientations. Materials constants were derived from these tests. The simulation results from the two-phase model showed good fit to the experimental test results.« less

10 CFR 26.211 - Fatigue assessments.

Code of Federal Regulations, 2010 CFR

2010-01-01

... 10 Energy 1 2010-01-01 2010-01-01 false Fatigue assessments. 26.211 Section 26.211 Energy NUCLEAR REGULATORY COMMISSION FITNESS FOR DUTY PROGRAMS Managing Fatigue § 26.211 Fatigue assessments. (a) Licensees... addition to any other test or determination of fitness that may be required under §§ 26.31(c) and 26.77, a...

10 CFR 26.211 - Fatigue assessments.

Code of Federal Regulations, 2011 CFR

2011-01-01

... 10 Energy 1 2011-01-01 2011-01-01 false Fatigue assessments. 26.211 Section 26.211 Energy NUCLEAR REGULATORY COMMISSION FITNESS FOR DUTY PROGRAMS Managing Fatigue § 26.211 Fatigue assessments. (a) Licensees... addition to any other test or determination of fitness that may be required under §§ 26.31(c) and 26.77, a...

75 FR 30284 - Airworthiness Directives; Empresa Brasileira de Aeronautica S.A. (EMBRAER) Model ERJ 170 Airplanes

Federal Register 2010, 2011, 2012, 2013, 2014

2010-06-01

... condition as: During ERJ 170 airplane full scale fatigue test, cracks were found in some structural... intervals, could prevent a timely detection of fatigue cracks. Undetected fatigue cracks in these areas... unsafe condition for the specified products. The MCAI states: During ERJ 170 airplane full scale fatigue...

Thermal Fatigue and Fracture Behavior of Ceramic Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Choi, Sung R.; Miller, Robert A.

2001-01-01

Thermal fatigue and fracture behavior of plasma-sprayed ceramic thermal barrier coatings has been investigated under high heat flux and thermal cyclic conditions. The coating crack propagation is studied under laser heat flux cyclic thermal loading, and is correlated with dynamic fatigue and strength test results. The coating stress response and inelasticity, fatigue and creep interactions, and interface damage mechanisms during dynamic thermal fatigue processes are emphasized.

Fatigue Life Assessment of 65Si7 Leaf Springs: A Comparative Study

PubMed Central

Arora, Vinkel Kumar; Bhushan, Gian; Aggarwal, M. L.

2014-01-01

The experimental fatigue life prediction of leaf springs is a time consuming process. The engineers working in the field of leaf springs always face a challenge to formulate alternate methods of fatigue life assessment. The work presented in this paper provides alternate methods for fatigue life assessment of leaf springs. A 65Si7 light commercial vehicle leaf spring is chosen for this study. The experimental fatigue life and load rate are determined on a full scale leaf spring testing machine. Four alternate methods of fatigue life assessment have been depicted. Firstly by SAE spring design manual approach the fatigue test stroke is established and by the intersection of maximum and initial stress the fatigue life is predicted. The second method constitutes a graphical method based on modified Goodman's criteria. In the third method codes are written in FORTRAN for fatigue life assessment based on analytical technique. The fourth method consists of computer aided engineering tools. The CAD model of the leaf spring has been prepared in solid works and analyzed using ANSYS. Using CAE tools, ideal type of contact and meshing elements have been proposed. The method which provides fatigue life closer to experimental value and consumes less time is suggested. PMID:27379327

The role of helplessness as mediator between neurological disability, emotional instability, experienced fatigue and depression in patients with multiple sclerosis.

PubMed

van der Werf, S P; Evers, A; Jongen, P J H; Bleijenberg, G

2003-02-01

The aim of this study was to test, in patients with multiple sclerosis (MS), whether the concept of helplessness might improve the understanding of the relationship between disease severity (neurological impairment) and personality characteristics (emotional instability) on one hand, and depressive mood and fatigue severity on the other hand. Data pertain to 89 patients with a definite diagnosis of MS (Expanded Disability Status Scale [EDSS] ratings: 1-8). Helplessness, fatigue severity, depressive mood and emotional instability were rated with validated questionnaires. Model testing revealed that more neurological impairment and more emotional instability were associated with more helplessness, while higher levels of helplessness were associated with more fatigue and depressive mood. The initially observed direct relationship between EDSS and fatigue disappeared. Emotional instability also had a direct significant relationship with depressive mood, and depressive mood had only a small relationship with fatigue severity. The results indicated that helplessness affected both depressive mood and fatigue severity and that fatigue was not merely a symptom of depressive mood. The correlation between neurological impairment and fatigue severity was largely explained by the mediating effect of helplessness. These findings suggest that MS patients troubled by disabling fatigue might benefit from a psychological intervention targeting unfavourable illness cognitions.

Estimation of Axial Fretting Fatigue Life at Elevated Temperatures Using Critical Distance Theory

NASA Astrophysics Data System (ADS)

Majzoobi, G. H.; Azhdarzadeh, P.

Fretting fatigue life is traditionally estimated by experiment. The objective of this work is to introduce a special approach for estimation of axial fretting fatigue life at elevated temperatures from plain fatigue test based on the critical distance theory. The method uses Fatemi-Socie parameter as a multiaxial criterion to compute the stress multiaxiality on focus path. This method considers only elastic behavior for materials, and two characteristic diagrams are obtained from plain fatigue tests on two U-shaped and V-shaped notched specimens. The results showed reasonable agreement between the predictions by the proposed method and the experiments for ambient temperature. For elevated temperatures, the results indicated that the predicted fretting fatigue life was considerably overestimated in the low cycle fatigue (LCF) regime and underestimated in the high cycle fatigue (HCF) region with respect to experimental measurements. The reason for such discrepancy is believed to be due to the complex behavior of AL 7075-T6, which exhibits at elevated temperatures because of the problems such as aging, oxidation and reduction of strength.

Fatigue testing and damage development in continuous fiber reinforced metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1988-01-01

A general overview of the fatigue behavior of metal matrix composites (MMC) is presented. The first objective is to present experimental procedures and techniques for conducting a meaningful fatigue test to detect and quantify fatigue damage in MMC. These techniques include interpretation of stress-strain responses, acid etching of the matrix, edge replicas of the specimen under load, radiography, and micrographs of the failure surfaces. In addition, the paper will show how stiffness loss in continuous fiber reinforced metal matrix composites can be a useful parameter for detecting fatigue damage initiation and accumulation. Second, numerous examples of how fatigue damage can initiate and grow in various MMC are given. Depending on the relative fatigue behavior of the fiber and matrix, and the interface properties, the failure modes of MMC can be grouped into four categories: (1) matrix dominated, (2) fiber dominated, (3) self-similar damage growth, and (4) fiber/matrix interfacial failures. These four types of damage will be discussed and illustrated by examples with the emphasis on the fatigue of unnotched laminates.

Fatigue testing and damage development in continuous fiber reinforced metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1989-01-01

A general overview of the fatigue behavior of metal matrix composites (MMC) is presented. The first objective is to present experimental procedures and techniques for conducting a meaningful fatigue test to detect and quantify fatigue damage in MMC. These techniques include interpretation of stress-strain responses, acid etching of the matrix, edge replicas of the specimen under load, radiography, and micrographs of the failure surfaces. In addition, the paper will show how stiffness loss in continuous fiber reinforced metal matrix composites can be a useful parameter for detecting fatigue damage initiation and accumulation. Second, numerous examples of how fatigue damage can initiate and grow in various MMC are given. Depending on the relative fatigue behavior of the fiber and matrix, and the interface properties, the failure modes of MMC can be grouped into four categories: (1) matrix dominated, (2) fiber dominated, (3) self-similar damage growth, and (4) fiber/matrix interfacial failures. These four types of damage will be discussed and illustrated by examples with the emphasis on the fatigue of unnotched laminates.

High temperature fatigue behavior of tungsten copper composites

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Kim, Yong-Suk; Gabb, Timothy P.

1989-01-01

The high temperature fatigue behavior of a 9 vol percent, tungsten fiber reinforced copper matrix composite was investigated. Load-controlled isothermal fatigue experiments at 260 and 560 C and thermomechanical fatigue (TMF) experiments, both in phase and out of phase between 260 and 560 C, were performed. The stress-strain response displayed considerable inelasticity under all conditions. Also, strain ratcheting was observed during all the fatigue experiments. For the isothermal fatigue and in-phase TMF tests, the ratcheting was always in a tensile direction, continuing until failure. The ratcheting during the out-of-phase TMF test shifted from a tensile direction to a compressive direction. This behavior was thought to be associated with the observed bulging and the extensive cracking of the out-of-phase specimen. For all cases, the fatigue lives were found to be controlled by damage to the copper matrix. Grain boundary cavitation was the dominant damage mechanism of the matrix. On a stress basis, TMF loading reduced lives substantially, relative to isothermal cycling. In-phase cycling resulted in the shortest lives, and isothermal fatigue at 260 C, the longest.

Influence of the number of cycles on shear fatigue strength of resin composite bonded to enamel and dentin using dental adhesives in self-etching mode.

PubMed

Tsujimoto, Akimasa; Barkmeier, Wayne W; Erickson, Robert L; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

2018-01-30

The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to enamel and dentin using the adhesive in self-etch mode were determined. Fatigue testing was used with 20 Hz frequency and cycling periods of 50,000, 100,000 and 1,000,000 cycles, or until failure occurred. For each of the cycling periods, there was no significant difference in shear fatigue strength across the cycling periods for the individual adhesives. Differences in shear fatigue strength were found between the adhesives within the cycling periods. Regardless of the adhesive used in self-etch mode for bonding to enamel or dentin, shear fatigue strength was not influenced by the number of cycles used for shear fatigue strength testing.

Fatigue Behavior and Modeling of Additively Manufactured Ti-6Al-4V Including Interlayer Time Interval Effects

NASA Astrophysics Data System (ADS)

Torries, Brian; Shamsaei, Nima

2017-12-01

The effects of different cooling rates, as achieved by varying the interlayer time interval, on the fatigue behavior of additively manufactured Ti-6Al-4V specimens were investigated and modeled via a microstructure-sensitive fatigue model. Comparisons are made between two sets of specimens fabricated via Laser Engineered Net Shaping (LENS™), with variance in interlayer time interval accomplished by depositing either one or two specimens per print operation. Fully reversed, strain-controlled fatigue tests were conducted, with fractography following specimen failure. A microstructure-sensitive fatigue model was calibrated to model the fatigue behavior of both sets of specimens and was found to be capable of correctly predicting the longer fatigue lives of the single-built specimens and the reduced scatter of the double-built specimens; all data points fell within the predicted upper and lower bounds of fatigue life. The time interval effects and the ability to be modeled are important to consider when producing test specimens that are smaller than the production part (i.e., property-performance relationships).

The assessment of fatigue: Psychometric qualities and norms for the Checklist individual strength.

PubMed

Worm-Smeitink, M; Gielissen, M; Bloot, L; van Laarhoven, H W M; van Engelen, B G M; van Riel, P; Bleijenberg, G; Nikolaus, S; Knoop, H

2017-07-01

The Checklist Individual Strength (CIS) measures four dimensions of fatigue: Fatigue severity, concentration problems, reduced motivation and activity. On the fatigue severity subscale, a cut-off score of 35 is used. This study 1) investigated the psychometric qualities of the CIS; 2) validated the cut-off score for severe fatigue and 3) provided norms. Representatives of the Dutch general population (n=2288) completed the CIS. The factor structure was investigated using an exploratory factor analysis. Internal consistency and test-retest reliability were determined. Concurrent validity was assessed in two additional samples by correlating the CIS with other fatigue scales (Chalder Fatigue Questionnaire, MOS Short form-36 Vitality subscale, EORTC QLQ-C30 fatigue subscale). To validate the fatigue severity cut-off score, a Receiver Operating Characteristics analysis was performed with patients referred to a chronic fatigue treatment centre (n=5243) and a healthy group (n=1906). Norm scores for CIS subscales were calculated for the general population, patients with chronic fatigue syndrome (CFS; n=1407) and eight groups with other medical conditions (n=1411). The original four-factor structure of the CIS was replicated. Internal consistency (α=0.84-0.95) and test-retest reliability (r=0.74-0.86) of the subscales were high. Correlations with other fatigue scales were moderate to high. The 35 points cut-off score for severe fatigue is appropriate, but, given the 17% false positive rate, should be adjusted to 40 for research in CFS. The CIS is a valid and reliable tool for the assessment of fatigue, with a validated cut-off score for severe fatigue that can be used in clinical practice. Copyright © 2017. Published by Elsevier Inc.

The effect of notches and pits on corrosion fatigue strength

NASA Astrophysics Data System (ADS)

Tatner, Ian

An investigation has been undertaken to examine the fatigue behaviour of two martensitic steels in air and aggressive environments. The steels studied are, 18% Ni marageing steel and FV520B, the later being a stainless steel turbine blade material and the former being a marageing steel that suffers general corrosion in mild environments. Both steels were heat treated to give similar tensile strength.The design and manufacture of an autoclave allowed push-pull fatigue tests to be conducted in aggressive environments at elevated temperatures.Corrosion potential was monitored using a three electrode cell and was controlled during testing. Base-line fatigue tests were conducted with a range of constant corrosion potentials, using both notched and plain FV520B specimens. In addition fatigue tests with pulsed corrosion potential were performed to asses the effect of transient corrosion conditions on the corrosion fatigue strength. The pulsed tests were designed to simulate service transients in the oxygen content and general chemical hostility in the condensing steam environment during start-up and shut down of the steam turbine.Post test examination of fractured samples was performed using Scanning Electron Microscopy (SEM) and optical microscope techniques. The fractography results were used to quantify microstructural and fracture features of the steels.A model based on the size and geometry of the initial corrosion pitting has been proposed to asses the fatigue life of FV520B in an aggressive environment.The effect of pitting on the corrosion fatigue strength of FV520B has been modelled using linear elastic fracture mechanics (LEFM) type approach. The model has shown a good correlation between predicted fatigue lives with experimental results.The results suggest that the fatigue life is governed by the mechanical stress concentrating effect of the pits rather than the electrochemical damage caused by the environment.Finite Element Analysis (FEA) of the notch allowed calculation of the elastic stress intensity factor (K[t]) for the specimen geometry used. The experimental results together with numerical results of FEA were used to calculate of the notch strength reduction factor (K[f]) for the material. This has been used to derive the notch sensitivity factors (q) for both materials.The results of fatigue tests in air showed that although both materials have similar tensile strength their plain fatigue strengths are different. The sensitivity of the fatigue strength to notches was also found to be significantly different. The marageing steel showed a higher sensitivity to a notch than the FV520B.An empirical model has been proposed to quantify the notch sensitivity and the effects of various microstructural features on the fatigue strength. A model has been developed to predict the serviceable life of a peak hardened FV520B turbine blade subjected to aggressive low load conditions during start-up and non-aggressive high load conditions during continual running. The model is based on the conclusions suggested in the work of a threshold stress intensity factor being reached where a fatigue crack will grow from a corrosion pit at the root of a notch. The model is then used to highlight the life reduction caused to steam turbine blades due to increased numbers of start-up cycles.

The impact of subjective cognitive fatigue and depression on cognitive function in patients with multiple sclerosis.

PubMed

Golan, Daniel; Doniger, Glen M; Wissemann, Karl; Zarif, Myassar; Bumstead, Barbara; Buhse, Marijean; Fafard, Lori; Lavi, Idit; Wilken, Jeffrey; Gudesblatt, Mark

2018-02-01

The association between subjective cognitive fatigue and objective cognitive dysfunction in patients with multiple sclerosis (PwMS) has been studied, with conflicting results. To explore the impact of fatigue on cognitive function, while controlling for the influence of depression, disability, comorbidities, and psychotropic medications. PwMS completed a computerized cognitive testing battery with age- and education-adjusted cognitive domain scores. Disability (Expanded Disability Status Scale (EDSS)), cognitive fatigue, and depression were concurrently evaluated. In all, 699 PwMS were included. Both cognitive fatigue and depression were significantly and negatively correlated with the same cognitive domains: information processing speed, executive function, attention, motor function, and memory (-0.15 ⩽ r ⩽ -0.14 for cognitive fatigue; -0.24 ⩽ r ⩽ -0.19 for depression). Multivariate analysis revealed significant but small independent correlations only between depression and neuropsychological test results, while cognitive fatigue had no independent correlation with objective cognitive function except for a trend toward impaired motor function in highly fatigued PwMS. Depression and cognitive fatigue accounted for no more than 6% of the variance in objective cognitive domain scores. Cognitive fatigue is not independently related to objective cognitive impairment. Depression may influence cognitive function of PwMS primarily when it is severe. Cognitive impairment in PwMS should not be ascribed to fatigue or mild depression.

Does fatigue have any impact on satisfaction of search?

NASA Astrophysics Data System (ADS)

Krupinski, Elizabeth A.; Schartz, Kevin; Caldwell, Robert; Madsen, Mark; Berbaum, Kevin S.

2017-03-01

Previous studies have demonstrated that fatigue impacts diagnostic accuracy, especially for those in training. We continued this line of investigation to determine if fatigue has any impact on a common source of errors - satisfaction of search (SOS). SOS requires subjects to participate in 2 sessions (SOS and non-SOS) and so does fatigue (fatigued and not fatigued) so we ran subjets in only the fatigued condition and used a previous non-fatigued study as the comparison. We used 64 chest computed radiographs half demonstrating various ``test'' abnormalities were read twice by 20 radiologists, once with and once without the addition of a simulated pulmonary nodule. Receiver-operating characteristic detection accuracy and decision thresholds were analyzed to study the effects of adding the nodule on detecting the test abnormalities. Adding nodules did not influence detection accuracy (ROC AUC SOS = 0.667; non-SOS = 0.679), but did induce a reluctance to report them. Adding nodules did not affect inspection time so the reluctance to report was not associated with reduced search. Fatigue did not appear to exacerbate the SOS effect. A second study with fractures revealed the same shift in performance but did reduce viewing times when fatigued. The results of these two studies suggest that the impact of fatigue on SOS is more complicated than expected and thus may require more investigation to fully understand its impact in the clinic.

Examination of ceramic restorative material interfacial debonding using acoustic emission and optical coherence tomography.

PubMed

Lin, Chun-Li; Kuo, Wen-Chuan; Yu, Jin-Jie; Huang, Shao-Fu

2013-04-01

CAD/CAM ceramic restorative material is routinely bonded to tooth substrates using adhesive cement. This study investigates micro-crack growth and damage in the ceramic/dentin adhesive interface under fatigue shear testing monitored using the acoustic emission (AE) technique with optical coherence tomography (OCT). Ceramic/dentin adhesive samples were prepared to measure the shear bond strength (SBS) under static load. Fatigue shear testing was performed using a modified ISO14801 method. Loads in the fatigue tests were applied at 80%, 70%, and 60% of the SBS to monitor interface debonding. The AE technique was used to detect micro-crack signals in static and fatigue shear bond tests. The results showed that the average SBS value in the static tests was 10.61±2.23MPa (mean±standard deviation). The average number of fatigue cycles in which ceramic/dentin interface damage was detected in 80%, 70% and 60% of the SBS were 152, 1962 and 9646, respectively. The acoustic behavior varied according to the applied load level. Events were emitted during 60% and 70% fatigue tests. A good correlation was observed between crack location in OCT images and the number of AE signal hits. The AE technique and OCT images employed in this study could potentially be used as a pre-clinical assessment tool to determine the integrity of cemented load bearing restored ceramic material. Sustainable cyclic load stresses in ceramic/dentin-bonded specimens were substantially lower than the measured SBS. Predicted S-N curve showed that the maximum endured load was 4.18MPa passing 10(6) fatigue cyclic. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

A novel anatomical short glass fiber reinforced post in an endodontically treated premolar mechanical resistance evaluation using acoustic emission under fatigue testing.

PubMed

Wang, Hsuan-Wen; Chang, Yen-Hsiang; Lin, Chun-Li

2017-01-01

This study evaluates the fracture resistance in an endodontically treated tooth using circular fiber-reinforced composite (FRC) and innovated anatomical short glass fiber reinforced (SGFR) posts under fatigue testing, monitored using the acoustic emission (AE) technique. An anatomical SGFR fiber post with an oval shape and slot/notch design was manufactured using an injection-molding machine. Crown/core maxillary second premolar restorations were executed using the anatomical SGFR and commercial cylindrical fiber posts under fatigue test to understand the mechanical resistances. The load versus AE signals in the fracture and fatigue tests were recorded to evaluate the restored tooth failure resistance. The static fracture resistance results showed that teeth restored using the anatomical SGFR post presented higher resistance than teeth restored using the commercial FRC post. The fatigue test endurance limitation (1.2×10 6 cycles) was 207.1N for the anatomical SGFR fiber post, higher than the 185.3N found with the commercial FRC post. The average accumulated number of AE signals and corresponding micro cracks for the anatomical SGFR fiber post (153.0 hits and 2.44 cracks) were significantly lower than those for the commercial FRC post (194.7 hits and 4.78 cracks) under 40% of the static maximum resistance fatigue test load (pass 1.2×10 6 cycles). This study concluded that the anatomical SGFR fiber post with surface slot/notch design made using precise injection molding presented superior static fracture resistance and fatigue endurance limitation than those for the commercial FRC post in an endodontically treated premolar. Copyright © 2016 Elsevier Ltd. All rights reserved.

DETERMINATION OF THE CREEP–FATIGUE INTERACTION DIAGRAM FOR ALLOY 617

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wright, J. K.; Carroll, L. J.; Sham, T. -L.

Alloy 617 is the leading candidate material for an intermediate heat exchanger for the very high temperature reactor. To evaluate the behavior of this material in the expected service conditions, creep-fatigue testing was performed. Testing has been performed primarily on a single heat of material at 850 and 950°C for total strain ranges of 0.3 to 1% and tensile hold times as long as 240 minutes. At 850°C, increases in the tensile hold duration degraded the creep fatigue resistance, at least to the investigated strain-controlled hold time of up to 60 minutes at the 0.3% strain range and 240 minutesmore » at the 1.0% strain range. At 950°C, the creep-fatigue cycles to failure becomes constant with increasing hold times, indicating saturation occurs at relatively short hold times. The creep and fatigue damage fractions have been calculated and plotted on a creep-fatigue interaction D-diagram. Results from earlier creep-fatigue tests at 800 and 1000°C on an additional heat of Alloy 617 are also plotted on the D-diagram. The methodology for calculating the damage fractions will be presented, and the effects of strain rate, strain range, temperature, hold time, and strain profile (i.e. holds in tension, compression or both) on the creep-fatigue damage will be explored.« less

Relations Between Self-Reported Daily-Life Fatigue, Hearing Status, and Pupil Dilation During a Speech Perception in Noise Task.

PubMed

Wang, Yang; Naylor, Graham; Kramer, Sophia E; Zekveld, Adriana A; Wendt, Dorothea; Ohlenforst, Barbara; Lunner, Thomas

People with hearing impairment are likely to experience higher levels of fatigue because of effortful listening in daily communication. This hearing-related fatigue might not only constrain their work performance but also result in withdrawal from major social roles. Therefore, it is important to understand the relationships between fatigue, listening effort, and hearing impairment by examining the evidence from both subjective and objective measurements. The aim of the present study was to investigate these relationships by assessing subjectively measured daily-life fatigue (self-report questionnaires) and objectively measured listening effort (pupillometry) in both normally hearing and hearing-impaired participants. Twenty-seven normally hearing and 19 age-matched participants with hearing impairment were included in this study. Two self-report fatigue questionnaires Need For Recovery and Checklist Individual Strength were given to the participants before the test session to evaluate the subjectively measured daily fatigue. Participants were asked to perform a speech reception threshold test with single-talker masker targeting a 50% correct response criterion. The pupil diameter was recorded during the speech processing, and we used peak pupil dilation (PPD) as the main outcome measure of the pupillometry. No correlation was found between subjectively measured fatigue and hearing acuity, nor was a group difference found between the normally hearing and the hearing-impaired participants on the fatigue scores. A significant negative correlation was found between self-reported fatigue and PPD. A similar correlation was also found between Speech Intelligibility Index required for 50% correct and PPD. Multiple regression analysis showed that factors representing "hearing acuity" and "self-reported fatigue" had equal and independent associations with the PPD during the speech in noise test. Less fatigue and better hearing acuity were associated with a larger pupil dilation. To the best of our knowledge, this is the first study to investigate the relationship between a subjective measure of daily-life fatigue and an objective measure of pupil dilation, as an indicator of listening effort. These findings help to provide an empirical link between pupil responses, as observed in the laboratory, and daily-life fatigue.

Creep and fatigue characteristics of Superpave mixtures.

DOT National Transportation Integrated Search

2005-01-01

Laboratory creep and fatigue testing was performed on five Superpave surface hot-mix asphalt mixtures placed at the Virginia Smart Road. Differences in creep and fatigue response attributable to production and compaction methods were investigated. In...

Fatigue life of laser cut metals

NASA Technical Reports Server (NTRS)

Martin, M. R.

1986-01-01

Fatigue tests were conducted to determine the actual reduction in fatigue life due to weight removal for balancing by: hand grinding, low power (20 watt) Nd:glass laser, and high power (400 watt) Nd:YAG laser.

A two-parameter model to predict fatigue life of high-strength steels in a very high cycle fatigue regime

NASA Astrophysics Data System (ADS)

Sun, Chengqi; Liu, Xiaolong; Hong, Youshi

2015-06-01

In this paper, ultrasonic (20 kHz) fatigue tests were performed on specimens of a high-strength steel in very high cycle fatigue (VHCF) regime. Experimental results showed that for most tested specimens failed in a VHCF regime, a fatigue crack originated from the interior of specimen with a fish-eye pattern, which contained a fine granular area (FGA) centered by an inclusion as the crack origin. Then, a two-parameter model is proposed to predict the fatigue life of high-strength steels with fish-eye mode failure in a VHCF regime, which takes into account the inclusion size and the FGA size. The model was verified by the data of present experiments and those in the literature. Furthermore, an analytic formula was obtained for estimating the equivalent crack growth rate within the FGA. The results also indicated that the stress intensity factor range at the front of the FGA varies within a small range, which is irrespective of stress amplitude and fatigue life.

Effect of Pre-Strain on the Fatigue Behavior of Extruded AZ31 Alloys

NASA Astrophysics Data System (ADS)

Wu, Yanjun

2017-09-01

An attempt is made to rationalize the effect of pre-strain history on fatigue behaviors of AZ31 magnesium alloy. Axial fatigue tests were conducted in the extruded and pre-compressioned AZ31 alloy under low cycle total strain control fatigue conditions. The pre-strain process influences the plastic deformation mechanism activated during fatigue deformation, especially during tensile loading, by enhancing the activity of detwinning mechanism. The low-cycle fatigue lifetime of extruded AZ31 alloy can be enhanced by the pre-compression process. And the hysteresis energy was successfully used to predict the low-cycle fatigue lifetime.

A method for predicting the fatigue life of pre-corroded 2024-T3 aluminum from breaking load tests

NASA Astrophysics Data System (ADS)

Gruenberg, Karl Martin

Characterization of material properties is necessary for design purposes and has been a topic of research for many years. Over the last several decades, much progress has been made in identifying metrics to describe fracture mechanics properties and developing procedures to measure the appropriate values. However, in the context of design, there has not been as much success in quantifying the susceptibility of a material to corrosion damage and its subsequent impact on material behavior in the framework of fracture mechanics. A natural next step in understanding the effects of corrosion damage was to develop a link between standard material test procedures and fatigue life in the presence of corrosion. Simply stated, the goal of this investigation was to formulate a cheaper and quicker method for assessing the consequences of corrosion on remaining fatigue life. For this study, breaking load specimens and fatigue specimens of a single nominal gage (0.063″) of aluminum alloy 2024-T3 were exposed to three levels of corrosion. The breaking load specimens were taken from three different material lots, and the fatigue tests were carried out at three stress levels. All failed specimens, both breaking load and fatigue specimens, were examined to characterize the damage state(s) and failure mechanism(s). Correlations between breaking load results and fatigue life results in the presence of corrosion damage were developed using a fracture mechanics foundation and the observed mechanisms of failure. Where breaking load tests showed a decrease in strength due to increased corrosion exposure, the corresponding set of fatigue tests showed a decrease in life. And where breaking load tests from different specimen orientations exhibited similar levels of strength, the corresponding set of fatigue specimens showed similar lives. The spread from shortest to longest fatigue lives among the different corrosion conditions decreased at the higher stress levels. Life predictions based on breaking load data were generally shorter than the experimental lives by an average of 20%. The life prediction methodology developed from this investigation is a very valuable tool for the purpose of assessing material substitution for aircraft designers, alloy differentiation for manufacturers, or inspection intervals and aircraft retirement schedules for aircraft in service.

Parametric study and characterization of the isobaric thermomechanical transformation fatigue of nickel-rich NiTi SMA actuators

NASA Astrophysics Data System (ADS)

Bertacchini, Olivier W.; Schick, Justin; Lagoudas, Dimitris C.

2009-03-01

The recent development of various aerospace applications utilizing Ni-rich NiTi Shape memory Alloys (SMAs) as actuators motivated the need to characterize the cyclic response and the transformation fatigue behavior of such alloys. The fatigue life validation and certification of new designs is required in order to be implemented and used in future applications. For that purpose, a custom built fatigue test frame was designed to perform isobaric thermally induced transformation cycles on small dogbones SMA actuators (test gauge cross-section up to: 1.270 x 0.508 mm2). A parametric study on the cyclic response and transformation fatigue behavior of Ni-rich NiTi SMAs led to the optimization of several material/process and test parameters, namely: the applied stress range, the heat treatment, the heat treatment environment and the specimen thickness. However, fatigue testing was performed in a chilled waterless glycol environment maintained at a temperature of 5°C that showed evidence of corrosion-assisted transformation fatigue failure. Therefore, it was necessary to build a fatigue test frame that would employ a dry and inert cooling methodology to get away from any detrimental interactions between the specimens and the cooling medium (corrosion). The selected cooling method was gaseous nitrogen, sprayed into a thermally insulated chamber, maintaining a temperature of -20°C. The design of the gaseous nitrogen cooling was done in such a way that the actuation frequency is similar to the one obtained using the original design (~ 0.1 Hz). For both cooling methods, Joule resistive heating was used to heat the specimens. In addition and motivated by the difference in surface quality resulting from different material processing such as EDM wire cutting and heat treatments, EDM recast layer and oxide layer were removed. The removal was followed by an ultra-fine polish (0.05 μm) that was performed on a subset of the fatigue specimens. Experimental results are presented for full actuation of the SMA actuators and are given in terms of applied stress, accumulated plastic strain and number of cycles to failure. In addition, the assessment of the influence of the surface quality is supported by fatigue tests results and post-failure microstructure analysis.

Validation of the Fatigue Impact Scale in Hungarian patients with multiple sclerosis.

PubMed

Losonczi, Erika; Bencsik, Krisztina; Rajda, Cecília; Lencsés, Gyula; Török, Margit; Vécsei, László

2011-03-01

Fatigue is one of the most frequent complaints of patients with multiple sclerosis (MS). The Fatigue Impact Scale (FIS), one of the 30 available fatigue questionnaires, is commonly applied because it evaluates multidimensional aspects of fatigue. The main purposes of this study were to test the validity, test-retest reliability, and internal consistency of the Hungarian version of the FIS. One hundred and eleven MS patients and 85 healthy control (HC) subjects completed the FIS and the Beck Depression Inventory, a large majority of them on two occasions, 3 months apart. The total FIS score and subscale scores differed statistically between the MS patients and the HC subjects in both FIS sessions. In the test-retest reliability assessment, statistically, the intraclass correlation coefficients were high in both the MS and HC groups. Cronbach's alpha values were also notably high. The results of this study indicate that the FIS can be regarded as a valid and reliable scale with which to improve our understanding of the impact of fatigue on the health-related quality of life in MS patients without severe disability.

A fatigue test method for Pb(Zr,Ti)O3 thin films by using MEMS-based self-sensitive piezoelectric microcantilevers

NASA Astrophysics Data System (ADS)

Kobayashi, T.; Maeda, R.; Itoh, T.

2008-11-01

In the present study, we propose a new method for the fatigue test of lead zirconate titanate (PZT) thin films for MEMS devices by using self-sensitive piezoelectric microcantilevers developed in our previous study. We have deposited PZT thin films on SOI wafers and fabricated the microcantilevers through the MEMS microfabrication process. In the self-sensitive piezoelectric microcantilevers, the PZT thin films are separated in order to act as an actuator and a sensor. The fatigue characteristic of the PZT thin films can be evaluated by measuring the output voltage of the sensor as a function of time. When a sine wave of 20 Vpp and a dc bias of 10 V were applied to the PZT thin films for an actuator, the output voltage of the sensor fell down after 107 fatigue cycles. We have also investigated the influence of amplitude of the actuation sine wave and dc bias on the fatigue of the PZT thin films by using the proposed fatigue test method.

Response of resin transfer molded (RTM) composites under reversed cyclic loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahfuz, H.; Haque, A.; Yu, D.

1996-01-01

Compressive behavior and the tension-compression fatigue response of resin transfer molded IM7 PW/PR 500 composite laminate with a circular notch have been studied. Fatigue damage characteristics have been investigated through the changes in the laminate strength and stiffness by gradually incrementing the fatigue cycles at a preselected load level. Progressive damage in the surface of the laminate during fatigue has been investigated using cellulose replicas. Failure mechanisms during static and cyclic tests have been identified and presented in detail. Extensive debonding of filaments and complete fiber bundle fracture accompanied by delamination were found to be responsible for fatigue failures, whilemore » fiber buckling, partial fiber fracture and delamination were characterized as the failure modes during static tests. Weibull analysis of the static, cyclic and residual tests have been performed and described in detail. Fractured as well as untested specimens were C-scanned, and the progressive damage growth during fatigue is presented. Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) for the fractured specimen were also performed and the analysis of the failure behavior is presented.« less

Validity and reliability of the Traditional Chinese version of the Multidimensional Fatigue Inventory in general population.

PubMed

Chuang, Li-Ling; Chuang, Yu-Fen; Hsu, Miao-Ju; Huang, Ying-Zu; Wong, Alice M K; Chang, Ya-Ju

2018-01-01

Fatigue is a common symptom in the general population and has a substantial effect on individuals' quality of life. The Multidimensional Fatigue Inventory (MFI) has been widely used to quantify the impact of fatigue, but no Traditional Chinese translation has yet been validated. The goal of this study was to translate the MFI from English into Traditional Chinese ('the MFI-TC') and subsequently to examine its validity and reliability. The study recruited a convenience sample of 123 people from various age groups in Taiwan. The MFI was examined using a two-step process: (1) translation and back-translation of the instrument; and (2) examination of construct validity, convergent validity, internal consistency, test-retest reliability, and measurement error. The validity and reliability of the MFI-TC were assessed by factor analysis, Spearman rho correlation coefficient, Cronbach's alpha coefficient, intraclass correlation coefficient (ICC), minimal detectable change (MDC), and Bland-Altman analysis. All participants completed the Short-Form-36 Health Survey Taiwan Form (SF-36-T) and the Chinese version of the Pittsburgh Sleep Quality Index (PSQI) concurrently to test the convergent validity of the MFI-TC. Test-retest reliability was assessed by readministration of the MFI-TC after a 1-week interval. Factor analysis confirmed the four dimensions of fatigue: general/physical fatigue, reduced activity, reduced motivation, and mental fatigue. A four-factor model was extracted, combining general fatigue and physical fatigue as one factor. The results demonstrated moderate convergent validity when correlating fatigue (MFI-TC) with quality of life (SF-36-T) and sleep disturbances (PSQI) (Spearman's rho = 0.68 and 0.47, respectively). Cronbach's alpha for the MFI-TC total scale and subscales ranged from 0.73 (mental fatigue subscale) to 0.92 (MFI-TC total scale). ICCs ranged from 0.85 (reduced motivation) to 0.94 (MFI-TC total scale), and the MDC ranged from 2.33 points (mental fatigue) to 9.5 points (MFI-TC total scale). The Bland-Altman analyses showed no significant systematic bias between the repeated assessments. The results support the use of the Traditional Chinese version of the MFI as a comprehensive instrument for measuring specific aspects of fatigue. Clinicians and researchers should consider interpreting general fatigue and physical fatigue as one subscale when measuring fatigue in Traditional Chinese-speaking populations.

Validity and reliability of the Traditional Chinese version of the Multidimensional Fatigue Inventory in general population

PubMed Central

Chuang, Li-Ling; Chuang, Yu-Fen; Hsu, Miao-Ju; Huang, Ying-Zu; Wong, Alice M. K.

2018-01-01

Background Fatigue is a common symptom in the general population and has a substantial effect on individuals’ quality of life. The Multidimensional Fatigue Inventory (MFI) has been widely used to quantify the impact of fatigue, but no Traditional Chinese translation has yet been validated. The goal of this study was to translate the MFI from English into Traditional Chinese (‘the MFI-TC’) and subsequently to examine its validity and reliability. Methods The study recruited a convenience sample of 123 people from various age groups in Taiwan. The MFI was examined using a two-step process: (1) translation and back-translation of the instrument; and (2) examination of construct validity, convergent validity, internal consistency, test-retest reliability, and measurement error. The validity and reliability of the MFI-TC were assessed by factor analysis, Spearman rho correlation coefficient, Cronbach’s alpha coefficient, intraclass correlation coefficient (ICC), minimal detectable change (MDC), and Bland-Altman analysis. All participants completed the Short-Form-36 Health Survey Taiwan Form (SF-36-T) and the Chinese version of the Pittsburgh Sleep Quality Index (PSQI) concurrently to test the convergent validity of the MFI-TC. Test-retest reliability was assessed by readministration of the MFI-TC after a 1-week interval. Results Factor analysis confirmed the four dimensions of fatigue: general/physical fatigue, reduced activity, reduced motivation, and mental fatigue. A four-factor model was extracted, combining general fatigue and physical fatigue as one factor. The results demonstrated moderate convergent validity when correlating fatigue (MFI-TC) with quality of life (SF-36-T) and sleep disturbances (PSQI) (Spearman's rho = 0.68 and 0.47, respectively). Cronbach’s alpha for the MFI-TC total scale and subscales ranged from 0.73 (mental fatigue subscale) to 0.92 (MFI-TC total scale). ICCs ranged from 0.85 (reduced motivation) to 0.94 (MFI-TC total scale), and the MDC ranged from 2.33 points (mental fatigue) to 9.5 points (MFI-TC total scale). The Bland-Altman analyses showed no significant systematic bias between the repeated assessments. Conclusions The results support the use of the Traditional Chinese version of the MFI as a comprehensive instrument for measuring specific aspects of fatigue. Clinicians and researchers should consider interpreting general fatigue and physical fatigue as one subscale when measuring fatigue in Traditional Chinese-speaking populations. PMID:29746466

A study on fatigue strength reduction factor for small diameter socket welded pipe joints

DOE Office of Scientific and Technical Information (OSTI.GOV)

Higuchi, Makoto; Nakagawa, Akira; Hayashi, Makoto

1996-12-01

Factors that may exert influence on the fatigue strength of small diameter socket welded joints of nominal diameter in the 20--50 mm range have been investigated by the fully reversed four-point bending fatigue test with the material, diameter, pipe schedule, throat depth, bead shape, slip-on gap, and root defect as the testing parameters. The fatigue strength of socket joints depended acutely on the diameter. When the diameter is large, the fatigue strength tended to be low and the fracture is of the root-failure mode; when it is small, on the other hand, the fatigue strength is high and the fracturemore » is of the toe-failure mode. Stainless steel proved to be superior to carbon steel; it gave rise to 1.37 times the fatigue strength of the latter for socket joints of nominal diameter 50 mm; the fatigue strength reduction factor determined at 10{sup 7} cycles with respect to the fatigue strength of smooth base metal in the fully reversed fatigue was about 4 for stainless steel and about 5 for carbon steel. The fatigue strength was higher, the larger the Sche number (i.e., the thicker the pipe wall); it was improved markedly by placing one final refinement pass on the toe or by eliminating the slip-on gap. An empirical formula relating the size of the root defect to the fatigue strength reduction has been proposed.« less

The Effects of Shot and Laser Peening on Fatigue Life and Crack Growth in 2024 Aluminum Alloy and 4340 Steel

NASA Technical Reports Server (NTRS)

Everett, R. A., Jr.; Matthews, W. T.; Prabhakaran, R.; Newman, J. C., Jr.; Dubberly, M. J.

2001-01-01

Fatigue and crack growth tests have been conducted on 4340 steel and 2024-T3 aluminum alloy, respectively, to assess the effects of shot peening on fatigue life and the effects of shot and laser peening on crack growth. Two current programs involving fixed and rotary-wing aircraft will not be using shot peened structures. Since the shot peening compressive residual stress depth is usually less than the 0.05-inch initial damage tolerance crack size, it is believed by some that shot peening should have no beneficial effects toward retarding crack growth. In this study cracks were initiated from an electronic-discharged machining flaw which was cycled to produce a fatigue crack of approximately 0.05-inches in length and then the specimens were peened. Test results showed that after peening the crack growth rates were noticeably slower when the cracks were fairly short for both the shot and laser peened specimens resulting in a crack growth life that was a factor of 2 to 4 times greater than the results of the average unpeened test. Once the cracks reached a length of approximately 0.1-inches the growth rates were about the same for the peened and unpeened specimens. Fatigue tests on 4340 steel showed that the endurance limit of a test specimen with a 0.002-inch-deep machining-like scratch was reduced by approximately 40 percent. However, if the "scratched" specimen was shot peened after inserting the scratch, the fatigue life returned to almost 100 percent of the unflawed specimens original fatigue life.

Experimental evaluation of cyclic fatigue resistance of four different nickel-titanium instruments after immersion in sodium hypochlorite and/or sterilization

PubMed Central

BULEM, Üreyen Kaya; KECECI, Ayse Diljin; GULDAS, Hilmi Egemen

2013-01-01

NiTi instruments have a high risk of separation due to torsional or flexural fatigue (cyclic fatigue). Chemomechanical preparation, cleaning procedures, chemical disinfection and sterilization cause the corrosion of endodontic instruments that may weaken the fracture resistance of the instruments. Objective To assess the effects of NaOCl immersion and autoclave sterilization on the cyclic fatigue resistance of ProFile, FlexMaster, Mtwo and TwistedFiles NiTi instruments (tip size 25, 0.06 taper, n=160). Material and Methods The instruments (n=10 for each subgroup) were dynamically immersed in NaOCl; immersed in NaOCl and sterilized in one autoclave cycle; 5 cycles immersed in NaOCl and sterilized in autoclave and not immersed in NaOCl and not sterilized (control group). Dynamic cyclic fatigue resistance was tested. The number of cycles to failure (NCF) were statistically analyzed (P<0.05). Results Kruskall-Wallis test indicated significant differences among the tested instruments in terms of NCF (P=0.000). The mean NCF of Mtwo (556.75) was higher than that of the Twisted File, Flexmaster and ProFile, 483.1, 376.12, 365.25, respectively. NaOCl immersion and autoclave sterilization have no effect on the NCF values of the tested instruments (P>.05). Conclusions Cyclic fatigue resistance of the tested NiTi instruments cannot be adversely affected by NaOCl immersion and autoclave sterilization. Production process (TwistedFiles) or design (Twisted Files, FlexMaster, Mtwo and ProFile) of the instruments can influence their cyclic fatigue resistance. PMID:24473715

A fatigue resistance test for elderly persons based on grip strength: reliability and comparison with healthy young subjects.

PubMed

Bautmans, Ivan; Mets, Tony

2005-06-01

Although a wide variety of protocols are available for evaluating skeletal muscle fatigue resistance, they often necessitate important technological resources or are too complicated for elderly subjects. We present here a new test, designed for elderly persons, based on maintaining maximal voluntary grip strength as long as possible. The aim of the study was to determine the reliability of this test procedure in hospitalized geriatric patients and in young healthy persons. Fatigue resistance was considered as the time in which grip strength decreases to 50% of its maximum value. Twenty geriatric, hospitalized patients (age 83 +/- 6 yrs) and thirty-nine young, healthy persons (age 23 +/- 4 yrs) were evaluated for fatigue resistance by two different observers. Height, weight and body mass index were determined for each participant and the current amount of sports activity was recorded in the young subjects. All participants were able to perform the test. Inter- and intra-rater reliability in both subgroups was good to excellent, with ICC(3,1) values ranging from 0.77 to 0.94. No significant differences in inter- and intra-rater measurements were found, except for inter-observer evaluations of the dominant hand in hospitalized geriatric patients. No significant relationships were found between fatigue resistance and maximal grip strength, anthropometrics or gender. The proposed fatigue resistance test is a reliable tool to evaluate geriatric hospitalized patients as well as young, active and healthy persons. Fatigue resistance scores are not related to gender, maximal strength or anthropometrics within the observed subgroups.

Examination of ceramic restoration adhesive coverage in cusp-replacement premolar using acoustic emission under fatigue testing.

PubMed

Chang, Yen-Hsiang; Yu, Jin-Jie; Lin, Chun-Li

2014-12-13

This study investigates CAD/CAM ceramic cusp-replacing restoration resistance with and without buccal cusp replacement under static and dynamic cyclic loads, monitored using the acoustic emission (AE) technique. The cavity was designed in a typical MODP (mesial-occlusal-distal-palatal) restoration failure shape when the palatal cusp has been lost. Two ceramic restorations [without coverage (WOC) and with (WC) buccal cuspal coverage with 2.0 mm reduction in cuspal height] were prepared to perform the fracture and fatigue tests with normal (200 N) and high (600 N) occlusal forces. The load versus AE signals in the fracture and fatigue tests were recorded to evaluate the restored tooth failure resistance. The results showed that non-significant differences in load value in the fracture test and the accumulated number of AE signals under normal occlusal force (200 N) in the fatigue test were found between with and without buccal cuspal coverage restorations. The first AE activity occurring for the WOC restoration was lower than that for the WC restoration in the fracture test. The number of AE signals increased with the cyclic load number. The accumulated number of AE signals for the WOC restoration was 187, higher than that (85) for the WC restoration under 600 N in the fatigue test. The AE technique and fatigue tests employed in this study were used as an assessment tool to evaluate the resistances in large CAD/CAM ceramic restorations. Non-significant differences in the tested fracture loads and accumulated number of AE signals under normal occlusal force (200 N) between different restorations indicated that aggressive treatment (with coverage preparation) in palatal cusp-replacing ceramic premolars require more attention for preserving and protecting the remaining tooth.

High temperature low-cycle fatigue mechanisms in single crystals of nickel-based superalloy Mar-M 200

NASA Technical Reports Server (NTRS)

Milligan, W. W.; Jayaraman, N.

1984-01-01

Twenty three high temperature low-cycle fatigue tests were conducted on single crystals of the nickel-based superalloy Mar-M 200. Tests were conducted at 760 and 870 C. SEM fractography and transmission electron microscopy were used to determine mechanisms responsible for the observed orientation dependent fatigue behavior. It has been concluded that the plastic characteristics of the alloy lead to orientation-dependent strain hardening and fatigue lives at 760 C. At 870 C, the elastic characteristics of the alloy dominated the behavior, even though the plastic strain ranges were about the same as they were at 760 C. This led to orientation-dependent fatigue lives, but the trends were not the same as they were at 760 C.

A Model of BGA Thermal Fatigue Life Prediction Considering Load Sequence Effects

PubMed Central

Hu, Weiwei; Li, Yaqiu; Sun, Yufeng; Mosleh, Ali

2016-01-01

Accurate testing history data is necessary for all fatigue life prediction approaches, but such data is always deficient especially for the microelectronic devices. Additionally, the sequence of the individual load cycle plays an important role in physical fatigue damage. However, most of the existing models based on the linear damage accumulation rule ignore the sequence effects. This paper proposes a thermal fatigue life prediction model for ball grid array (BGA) packages to take into consideration the load sequence effects. For the purpose of improving the availability and accessibility of testing data, a new failure criterion is discussed and verified by simulation and experimentation. The consequences for the fatigue underlying sequence load conditions are shown. PMID:28773980

Fatigue and failure responses of lead zirconate titanate multilayer actuator under unipolar high-field electric cycling

NASA Astrophysics Data System (ADS)

Zeng, Fan Wen; Wang, Hong; Lin, Hua-Tay

2013-07-01

Lead zirconate titanate (PZT) multilayer actuators with an interdigital electrode design were studied under high electric fields (3 and 6 kV/mm) in a unipolar cycling mode. A 100 Hz sine wave was used in cycling. Five specimens tested under 6 kV/mm failed from 3.8 × 105 to 7 × 105 cycles, whereas three other specimens tested under 3 kV/mm were found to be still functional after 108 cycles. Variations in piezoelectric and dielectric responses of the tested specimens were observed during the fatigue test, depending on the measuring and cycling conditions. Selected fatigued and damaged actuators were characterized using an impedance analyzer or small signal measurement. Furthermore, involved fatigue and failure mechanisms were investigated using scanning acoustic microscope and scanning electron microscope. The extensive cracks and porous regions were revealed across the PZT layers on the cross sections of a failed actuator. The results from this study have demonstrated that the high-field cycling can accelerate the fatigue of PZT stacks as long as the partial discharge is controlled. The small signal measurement can also be integrated into the large signal measurement to characterize the fatigue response of PZT stacks in a more comprehensive basis. The former can further serve as an experimental method to test and monitor the behavior of PZT stacks.

A novel method of strain - bending moment calibration for blade testing

NASA Astrophysics Data System (ADS)

Greaves, P.; Prieto, R.; Gaffing, J.; van Beveren, C.; Dominy, R.; Ingram, G.

2016-09-01

A new method of interpreting strain data in full scale static and fatigue tests has been implemented as part of the Offshore Renewable Energy Catapult's ongoing development of biaxial fatigue testing of wind turbine blades. During bi-axial fatigue tests, it is necessary to be able to distinguish strains arising from the flapwise motion of the blade from strains arising from the edgewise motion. The method exploits the beam-like structure of blades and is derived using the equations of beam theory. It offers several advantages over the current state of the art method of calibrating strain gauges.

Effect of five lubricants on life of AISI 9310 spur gears

NASA Technical Reports Server (NTRS)

Townsend, D. P.; Zaretsky, E. V.

1985-01-01

Spur-gear surface fatigue tests were conducted with five lubricants using a single lot of consumable-electrode vacuum melted (CVM) AISI 9310 spur gears. The lot of gears was divided into five groups, each of which was tested with a different lubricant. The test lubricants are classified as either a synthetic hydrocarbon, mineral oil, or ester-based lubricant. All five lubricants have imilar viscosity and pressure-viscosity coefficients. A pentaerythritol base stock without sufficient antiwear additives produced a surface fatigue life pproximately 22 percent that of the same base stock with chlorine and phosphorus type additives. The presence of sulfur type antiwear additives in the lubricant did not appear to affect the surface fatigue life of the gears tested. No statistical difference in the 10-percent surface fatigue life was produced with four of the five lubricants.

Cyclic fatigue resistance of XP-endo Shaper compared with different nickel-titanium alloy instruments.

PubMed

Elnaghy, Amr; Elsaka, Shaymaa

2018-04-01

The aims of this study were to assess and compare the resistance to cyclic fatigue of XP-endo Shaper (XPS; FKG Dentaire, La Chaux-de-Fonds, Switzerland) instruments with TRUShape (TRS; Dentsply Tulsa Dental Specialties, Tulsa, OK, USA), HyFlex CM (HCM; Coltene, Cuyahoga Falls, OH, USA), Vortex Blue (VB; Dentsply Tulsa Dental Specialties), and iRace (iR; FKG Dentaire) nickel-titanium rotary instruments at body temperature. Size 30, 0.01 taper of XPS, size 30, 0.04 taper of HCM, VB, iR, and size 30, 0.06 taper of TRS instruments were immersed in saline at 37 ± 1 °C during cyclic fatigue testing. The instruments were tested with 60° angle of curvature and a 3-mm radius of curvature. The number of cycles to failure (NCF) was calculated and the length of the fractured segment was measured. Fractographic examination of the fractured surface was performed using a scanning electron microscope. The data were analyzed statistically using Kruskal-Wallis H test and Mann-Whitney U tests. Statistical significance was set at P < 0.05. XPS had a significantly greater NCF compared with the other instruments (P < 0.001). The topographic appearance of the fracture surfaces of tested instruments revealed ductile fracture of cyclic fatigue failure. XPS instruments exhibited greater cyclic fatigue resistance compared with the other tested instruments. XP-endo Shaper instruments could be used more safely in curved canals due to their higher fatigue resistance.

Bidirectional Relationships Between Fatigue and Everyday Experiences in Persons Living With HIV.

PubMed

Cook, Paul F; Hartson, Kimberly R; Schmiege, Sarah J; Jankowski, Catherine; Starr, Whitney; Meek, Paula

2016-06-01

Fatigue symptoms are very common among persons living with HIV (PLWH). Fatigue is related to functional and psychological problems and to treatment nonadherence. Using secondary data from ecological momentary assessment, we examined fatigue as a predictor of PLWH everyday experiences. In bidirectional analyses based on the shape shifters model, we also examined these experiences as predictors of fatigue. Data were examined from 67 PLWH who completed daily surveys on a handheld computer. Brief validated scales were used to assess participants' control beliefs, mood, stress, coping, social support, experience of stigma, and motivation. At the beginning and end of the study, fatigue was measured with two CES-D items that have been used in past HIV symptom research. Multilevel models and logistic regression were used to test reciprocal predictive relationships between variables. Moderate to severe fatigue affected 45% of PLWH in the study. Initial fatigue predicted PLWH subsequent overall level of control beliefs, mood, stress, coping, and social support, all p < .05. These state variables remained relatively constant over time, regardless of participants' initial fatigue. In tests for reciprocal relationships with 33 PLWH, average daily stress, OR = 4.74, and stigma, OR = 4.86, also predicted later fatigue. Fatigue predicted several daily survey variables including stress and social support. Stress and support in turn predicted fatigue at a later time, suggesting a self-perpetuating cycle but also a possible avenue for intervention. Future studies should examine daily variation in fatigue among PLWH and its relation to other everyday experiences and behaviors. © 2016 Wiley Periodicals, Inc. © 2016 Wiley Periodicals, Inc.

Rolling-element fatigue life of silicon nitride balls: Preliminary test results

NASA Technical Reports Server (NTRS)

Parker, R. J.; Zaretsky, E. V.

1972-01-01

Hot pressed silicon nitride was evaluated as a rolling element bearing material. The five-ball fatigue tester was used to test 12.7 mm (0.500 in.) diameter balls at a maximum Hertz stress of 800,000 psi at a race temperature of 130 F. The fatigue spalls in the silicon nitride resembled those in typical bearing steels. The ten-percent fatigue life of the silicon nitride balls was approximately one-eighth to one-fifth that of typical bearing steels (52100 and M-50). The load capacity of the silicon nitride was approximately one-third that of typical bearing steels. The load capacity of the silicon nitride was significantly higher than previously tested ceramic materials for rolling element bearings.

Fracture and fatigue behavior of shot-blasted titanium dental implants.

PubMed

Gil, F J; Planell, J A; Padrós, A

2002-01-01

This investigation studies the effect of the shot-blasting treatment on the cyclic deformation behavior of a commercially pure titanium, with two microstructures: equiaxed and acicular. The fatigue tests were carried out in artificial saliva medium at 37 degrees C. Cyclic deformation tests have been carried out up to fracture, and the fatigue crack nucleation and propagation have been analyzed. The results show that the shot-blasting treatment improves the fatigue life in the microstructures studied, and that the equiaxed was better in mechanical properties than the acicular. The cause of this improvement in the mechanical properties is due to the compressive stress on the material surface for the shot-blasted specimens. Hardness tests were carried out to determine the value of these internal stresses.

The ultimate state of polymeric materials and laminated and fibrous composites under asymmetric high-cycle loading

NASA Astrophysics Data System (ADS)

Golub, V. P.; Pogrebniak, A. D.; Kochetkova, E. S.

2008-01-01

The prediction of the high-cycle fatigue strength of polymeric and composite materials in asymmetric loading is considered. The problem is solved on the basis of a nonlinear model of ultimate state allowing us to describe all typical forms of the diagrams of ultimate stresses. The material constants of the model are determined from the results of fatigue tests in symmetric reversed cycling, in a single fatigue test with the minimum stress equal to zero, and in a short-term strength test. The fatigue strength characteristics of some polymers, glass-fiber laminates, glass-fiber-reinforced plastics, organic-fiber-reinforced plastics, and wood laminates in asymmetric tension-compression, bending, and torsion have been calculated and approved experimentally.

Locomotor Muscle Fatigue Does Not Alter Oxygen Uptake Kinetics during High-Intensity Exercise.

PubMed

Hopker, James G; Caporaso, Giuseppe; Azzalin, Andrea; Carpenter, Roger; Marcora, Samuele M

2016-01-01

The [Formula: see text] slow component ([Formula: see text]) that develops during high-intensity aerobic exercise is thought to be strongly associated with locomotor muscle fatigue. We sought to experimentally test this hypothesis by pre-fatiguing the locomotor muscles used during subsequent high-intensity cycling exercise. Over two separate visits, eight healthy male participants were asked to either perform a non-metabolically stressful 100 intermittent drop-jumps protocol (pre-fatigue condition) or rest for 33 min (control condition) according to a random and counterbalanced order. Locomotor muscle fatigue was quantified with 6-s maximal sprints at a fixed pedaling cadence of 90 rev·min -1 . Oxygen kinetics and other responses (heart rate, capillary blood lactate concentration and rating of perceived exertion, RPE) were measured during two subsequent bouts of 6 min cycling exercise at 50% of the delta between the lactate threshold and [Formula: see text] determined during a preliminary incremental exercise test. All tests were performed on the same cycle ergometer. Despite significant locomotor muscle fatigue ( P = 0.03), the [Formula: see text] was not significantly different between the pre-fatigue (464 ± 301 mL·min -1 ) and the control (556 ± 223 mL·min -1 ) condition ( P = 0.50). Blood lactate response was not significantly different between conditions ( P = 0.48) but RPE was significantly higher following the pre-fatiguing exercise protocol compared with the control condition ( P < 0.01) suggesting higher muscle recruitment. These results demonstrate experimentally that locomotor muscle fatigue does not significantly alter the [Formula: see text] kinetic response to high intensity aerobic exercise, and challenge the hypothesis that the [Formula: see text] is strongly associated with locomotor muscle fatigue.

Fatigue properties of type 316LN stainless steel in air and mercury

NASA Astrophysics Data System (ADS)

Strizak, J. P.; Tian, H.; Liaw, P. K.; Mansur, L. K.

2005-08-01

An extensive fatigue testing program on 316LN stainless steel was recently carried out to support the design of the mercury target container for the spallation neutron source (SNS) that is currently under construction at the Oak Ridge National Laboratory in the United States. The major objective was to determine the effects of mercury on fatigue behavior. The S- N fatigue behavior of 316LN stainless steel is characterized by a family of bilinear fatigue curves which are dependent on frequency, environment, mean stress and cold work. Generally, fatigue life increases with decreasing stress and levels off in the high cycle region to an endurance limit below which the material will not fail. For fully reversed loading as well as tensile mean stress loading conditions mercury had no effect on endurance limit. However, at higher stresses a synergistic relationship between mercury and cyclic loading frequency was observed at low frequencies. As expected, fatigue life decreased with decreasing frequency, but the response was more pronounced in mercury compared with air. As a result of liquid metal embrittlement (LME), fracture surfaces of specimens tested in mercury showed widespread brittle intergranular cracking as opposed to typical transgranular cracking for specimens tested in air. For fully reversed loading (zero mean stress) the effect of mercury disappeared as frequency increased to 10 Hz. For mean stress conditions with R-ratios of 0.1 and 0.3, LME was still evident at 10 Hz, but at 700 Hz the effect of mercury had disappeared ( R = 0.1). Further, for higher R-ratios (0.5 and 0.75) fatigue curves for 10 Hz showed no environmental effect. Finally, cold working (20%) increased tensile strength and hardness, and improved fatigue resistance. Fatigue behavior at 10 and 700 Hz was similar and no environmental effect was observed.

Mental Fatigue Impairs Soccer-Specific Physical and Technical Performance.

PubMed

Smith, Mitchell R; Coutts, Aaron J; Merlini, Michele; Deprez, Dieter; Lenoir, Matthieu; Marcora, Samuele M

2016-02-01

To investigate the effects of mental fatigue on soccer-specific physical and technical performance. This investigation consisted of two separate studies. Study 1 assessed the soccer-specific physical performance of 12 moderately trained soccer players using the Yo-Yo Intermittent Recovery Test, Level 1 (Yo-Yo IR1). Study 2 assessed the soccer-specific technical performance of 14 experienced soccer players using the Loughborough Soccer Passing and Shooting Tests (LSPT, LSST). Each test was performed on two occasions and preceded, in a randomized, counterbalanced order, by 30 min of the Stroop task (mentally fatiguing treatment) or 30 min of reading magazines (control treatment). Subjective ratings of mental fatigue were measured before and after treatment, and mental effort and motivation were measured after treatment. Distance run, heart rate, and ratings of perceived exertion were recorded during the Yo-Yo IR1. LSPT performance time was calculated as original time plus penalty time. LSST performance was assessed using shot speed, shot accuracy, and shot sequence time. Subjective ratings of mental fatigue and effort were higher after the Stroop task in both studies (P < 0.001), whereas motivation was similar between conditions. This mental fatigue significantly reduced running distance in the Yo-Yo IR1 (P < 0.001). No difference in heart rate existed between conditions, whereas ratings of perceived exertion were significantly higher at iso-time in the mental fatigue condition (P < 0.01). LSPT original time and performance time were not different between conditions; however, penalty time significantly increased in the mental fatigue condition (P = 0.015). Mental fatigue also impaired shot speed (P = 0.024) and accuracy (P < 0.01), whereas shot sequence time was similar between conditions. Mental fatigue impairs soccer-specific running, passing, and shooting performance.

Locomotor Muscle Fatigue Does Not Alter Oxygen Uptake Kinetics during High-Intensity Exercise

PubMed Central

Hopker, James G.; Caporaso, Giuseppe; Azzalin, Andrea; Carpenter, Roger; Marcora, Samuele M.

2016-01-01

The V˙O2 slow component (V˙O2sc) that develops during high-intensity aerobic exercise is thought to be strongly associated with locomotor muscle fatigue. We sought to experimentally test this hypothesis by pre-fatiguing the locomotor muscles used during subsequent high-intensity cycling exercise. Over two separate visits, eight healthy male participants were asked to either perform a non-metabolically stressful 100 intermittent drop-jumps protocol (pre-fatigue condition) or rest for 33 min (control condition) according to a random and counterbalanced order. Locomotor muscle fatigue was quantified with 6-s maximal sprints at a fixed pedaling cadence of 90 rev·min−1. Oxygen kinetics and other responses (heart rate, capillary blood lactate concentration and rating of perceived exertion, RPE) were measured during two subsequent bouts of 6 min cycling exercise at 50% of the delta between the lactate threshold and V˙O2max determined during a preliminary incremental exercise test. All tests were performed on the same cycle ergometer. Despite significant locomotor muscle fatigue (P = 0.03), the V˙O2sc was not significantly different between the pre-fatigue (464 ± 301 mL·min−1) and the control (556 ± 223 mL·min−1) condition (P = 0.50). Blood lactate response was not significantly different between conditions (P = 0.48) but RPE was significantly higher following the pre-fatiguing exercise protocol compared with the control condition (P < 0.01) suggesting higher muscle recruitment. These results demonstrate experimentally that locomotor muscle fatigue does not significantly alter the V˙O2 kinetic response to high intensity aerobic exercise, and challenge the hypothesis that the V˙O2sc is strongly associated with locomotor muscle fatigue. PMID:27790156

Psychometric Properties of the Chinese Version of the Occupational Fatigue Exhaustion/Recovery Scale: A Test in a Nursing Population.

PubMed

Fang, Jin-Bo; Zhou, Chun-Fen; Huang, Jing; Qiu, Chang-Jian

2018-06-01

The Occupational Fatigue Exhaustion/Recovery Scale (OFER) was designed to assess occupational fatigue in nurses. Although the original English version of this instrument has shown high degrees of reliability and validity, a Chinese version of this scale has yet to be verified. The aim of this study was to evaluate the psychometric properties of the OFER in a population of Chinese nurses. The scale was translated using translation and back-translation. The validities and reliabilities were evaluated on 923 qualified participants using content validity index, concurrent validity, factorial validity, internal consistency reliability, and test-retest reliability. The content validity index for the OFER was .92. The correlation coefficients between the scores of the OFER subscales and the criteria in this study (varying from -.498 to .705) verified that the OFER has acceptable concurrent validity. Principal component analysis and confirmatory factor analysis revealed that three factors correspond to the structure of the original instrument and that recovery mediates the relationship between acute and chronic fatigue. The Cronbach's alpha for the chronic fatigue, acute fatigue, and intershift recovery subscales were .83, .85, and .86, respectively. Test-retest reliabilities with correlation coefficients from .61 to .78 were found in the three subscales. OFER is a reliable and valid instrument for assessing work-related fatigue in Chinese nurses. However, further improvement of the acute fatigue subscale is recommended. The OFER has the potential to elicit information that is useful for assessing fatigue in nurses in China. Furthermore, as it differentiates between acute and chronic fatigue, OFER may be an effective tool for guiding the development and implementation of various, related intervention measures.

Low-cycle fatigue analysis of a cooled copper combustion chamber

NASA Technical Reports Server (NTRS)

Miller, R. W.

1974-01-01

A three-dimensional finite element elastoplastic strain analysis was performed for the throat section of regeneratively cooled rocket engine combustion chamber. The analysis included thermal and pressure loads, and the effects of temperature dependent material properties, to determine the strain range corresponding to the engine operating cycle. The strain range was used in conjunction with OFHC copper isothermal fatigue test data to predict engine low-cycle fatigue life. The analysis was performed for chamber configuration and operating conditions corresponding to a hydrogen-oxygen chamber which was fatigue tested to failure at the NASA Lewis Research Center.

Fatigue and fracture mechanical behavior for Chinese A508-3 steel at room temperature

NASA Astrophysics Data System (ADS)

Shi, K. K.; Xie, H.; Zheng, B.; Fu, X. L.

2018-06-01

Material, A508-3 steel, has been used in nuclear reactor vessels. In the present study, fatigue and fracture mechanical behavior of Chinese A5083 steel at room temperature are studied by mechanical material testing machine (MTS). Test data of material’s mechanical behavior including uniaxial tension, low cycle fatigue (LCF), threshold value of stress intensity factor (SIF) range, fatigue crack growth (FCG), and fracture toughness is generated and given for further study. It is worth noting that the model in predicting FCG of material from LCF parameters is verified and discussed.

Finite element fatigue analysis of rectangular clutch spring of automatic slack adjuster

NASA Astrophysics Data System (ADS)

Xu, Chen-jie; Luo, Zai; Hu, Xiao-feng; Jiang, Wen-song

2015-02-01

The failure of rectangular clutch spring of automatic slack adjuster directly affects the work of automatic slack adjuster. We establish the structural mechanics model of automatic slack adjuster rectangular clutch spring based on its working principle and mechanical structure. In addition, we upload such structural mechanics model to ANSYS Workbench FEA system to predict the fatigue life of rectangular clutch spring. FEA results show that the fatigue life of rectangular clutch spring is 2.0403×105 cycle under the effect of braking loads. In the meantime, fatigue tests of 20 automatic slack adjusters are carried out on the fatigue test bench to verify the conclusion of the structural mechanics model. The experimental results show that the mean fatigue life of rectangular clutch spring is 1.9101×105, which meets the results based on the finite element analysis using ANSYS Workbench FEA system.

Nonlinear ultrasonic fatigue crack detection using a single piezoelectric transducer

NASA Astrophysics Data System (ADS)

An, Yun-Kyu; Lee, Dong Jun

2016-04-01

This paper proposes a new nonlinear ultrasonic technique for fatigue crack detection using a single piezoelectric transducer (PZT). The proposed technique identifies a fatigue crack using linear (α) and nonlinear (β) parameters obtained from only a single PZT mounted on a target structure. Based on the different physical characteristics of α and β, a fatigue crack-induced feature is able to be effectively isolated from the inherent nonlinearity of a target structure and data acquisition system. The proposed technique requires much simpler test setup and less processing costs than the existing nonlinear ultrasonic techniques, but fast and powerful. To validate the proposed technique, a real fatigue crack is created in an aluminum plate, and then false positive and negative tests are carried out under varying temperature conditions. The experimental results reveal that the fatigue crack is successfully detected, and no positive false alarm is indicated.

Effect of Various Heat Treatment Processes on Fatigue Behavior of Tool Steel for Cold Forging Die

NASA Astrophysics Data System (ADS)

Jin, S. U.; Kim, S. S.; Lee, Y. S.; Kwon, Y. N.; Lee, J. H.

Effects of various heat treatment processes, including "Q/T (quenching and tempering)", "Q/CT/T (Quenching, cryogenic treatment and tempering)", "Q/T (quenching and tempering) + Ti-nitriding" and "Q/CT/T (Cryogenic treatment and tempering) + Ti-nitriding", on S-N fatigue behavior of AISI D2 tool steel were investigated. The optical micrographs and Vicker's hardness values at near surface and core area were examined for each specimen. Uniaxial fatigue tests were performed by using an electro-magnetic resonance fatigue testing machine at a frequency of 80 Hz and an R ratio of -1. The overall resistance to fatigue tends to decrease significantly with Ti-nitriding treatment compared to those for the general Q/T and Q/CT/T specimens. The reduced resistance to fatigue with Ti-nitriding is discussed based on the microstructural and fractographic analyses.

Electronics Reliability Fracture Mechanics, Volume 2. Fracture Mechanics

DTIC Science & Technology

1992-05-01

alloy or strength level. Aluminum alloy 2024 - T351 was selected as being representative of the aluminum wire, and the fatigue ...to bracket the bond wire fatigue tests. 3-41 Also shown for comparison are two curves, which are the crack growth rates for 2024 aluminum alloy (Ref...is very similar to that for 2024 aluminum alloy . 3.2.6 Discussion of Loop Vibration Fatigue Testing Results This experimental and

Monotonic, Creep-Rupture, and Fatigue Behavior of Carbon Fiber Reinforced Silicon Carbide (C/SiC) at an Elevated Temperature

DTIC Science & Technology

2004-03-01

elevated temperature of 550 C. Cyclic loading of C/SiC was investigated at frequencies of 375 Hz , 10 Hz, 1 Hz, and 0.1 Hz. Creep-Rupture tests and tests that...is reduced when frequency of fatigue is increased. At high frequency fatigue (10Hz to 375 Hz ), C/SiC composites have longer cycle lives and time lives

Low cycle fatigue behaviour of a plasma-sprayed coating material

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Miner, R. V.

1986-01-01

Single crystal nickel-base superalloys employed in turbine blade applications are often used with a plasma spray coating for oxidation and hot corrosion resistance. These coatings may also affect fatigue life of the superalloy substrate. As part of a large program to understand the fatigue behavior of coated single crystals, fully reversed, total strain controlled fatigue tests were run on a free standing NiCoCrAlY coating alloy, PWA 276, at 0.1 Hz. Fatigue tests were conducted at 650 C, where the NiCoCrAlY alloy has modest ductility, and at 1050 C, where it is extremely ductile, showing tensile elongation in excess of 100 percent. At the lower test temperature, deformation induced disordering softened the NiCoCrAlY alloy, while at the higher test temperature cyclic hardening was observed which was linked to gradual coarsening of the two phase microstructure. Fatigue life of the NiCoCrAlY alloy was significantly longer at the higher temperature. Further, the life of the NiCoCrAlY alloy exceeds that of coated, /001/-oriented PWA 1480 single crystals at 1050 C but at 650 C the life of the coated crystal is greater than that of the NiCoCrAlY alloy on a total strain basis.

An index for breathlessness and leg fatigue.

PubMed

Borg, E; Borg, G; Larsson, K; Letzter, M; Sundblad, B-M

2010-08-01

The features of perceived symptoms causing discontinuation of strenuous exercise have been scarcely studied. The aim was to characterize the two main symptoms causing the discontinuation of heavy work in healthy persons as well as describe the growth of symptoms during exercise. Breathlessness (b) and leg fatigue (l) were assessed using the Borg CR10 Scale and the Borg CR100 (centiMax) Scale, during a standardized exercise test in 38 healthy subjects (24-71 years). The b/l-relationships were calculated for terminal perceptions (ERI(b/l)), and the growth of symptoms determined by power functions for the whole test, as well as by growth response indexes (GRI). This latter index was constructed as a ratio between power levels corresponding to a very strong and a moderate perception. In the majority (71%) of the test subjects, leg fatigue was the dominant symptom at the conclusion of exercise (P<0.001) and the b/l ratio was 0.77 (CR10) and 0.75 (CR100), respectively. The GRI for breathlessness and leg fatigue was similar, with good correlations between GRI and the power function exponent (P<0.005). In healthy subjects, leg fatigue is the most common cause for discontinuing an incremental exercise test. The growth functions for breathlessness and leg fatigue during work are, however, almost parallel.

The influence of matrix microstructure

NASA Astrophysics Data System (ADS)

Vyletel, G. M.; Allison, J. E.; Aken, D. C.

1993-11-01

The low-cycle and high-cycle fatigue behavior and cyclic response of naturally aged and artificially aged 2219/TiC/15p and unreinforced 2219 Al were investigated utilizing plastic strain-controlled and stress-controlled testing. The cyclic response of both the reinforced and un-reinforced materials was similar for all plastic strain amplitudes tested except that the saturation stress level for the composite was always greater than that of the unreinforced material. The cyclic response of the naturally aged materials exhibited cyclic hardening and, in some cases, cyclic softening, while the cyclic response for the artificially aged materials showed no evidence of either cyclic hardening or softening. The higher ductility of the unreinforced material made it more resistant to fatigue failure at high strains, and thus, at a given plastic strain, it had longer fatigue life. It should be noted that the tensile ductilities of the 2219/TiC/15p were significantly higher than those previously reported for 2XXX-series composites. During stress-controlled test-ing at stresses below 220 MPa, the presence of TiC particles lead to an improvement in fatigue life. Above 220 MPa, no influence of TiC reinforcement on fatigue life could be detected. In both the composite and unreinforced materials, the low-cycle and high-cycle fatigue lives were found to be virtually independent of matrix microstructure.

The low cycle fatigue behavior of a plasma-sprayed coating material

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Miner, R. V., Jr.

1986-01-01

Single crystal nickel-base superalloys employed in turbine blade applications are often used with a plasma spray coating for oxidation and hot corrosion resistance. These coatings may also affect fatigue life of the superalloy substrate. As part of a large program to understand the fatigue behavior of coated single crystals, fully reversed, total strain controlled fatigue tests were run on a free standing NiCoCrAlY coating alloy, PWA 276, at 0.1 Hz. Fatigue tests were conducted at 650 C, where the NiCoCrAlY alloy has modest ductility, and at 1050 C, where it is extremely ductile, showing tensile elongation in excess of 100 percent. At the lower test temperature, deformation induced disordering softened the NiCoCrAlY alloy, while at the higher test temperature cyclic hardening was observed which was linked to gradual coarsening of the two phase microstructure. Fatigue life of the NiCoCrAlY alloy was significantly longer at the higher temperature. Further, the life of the NiCoCrAlY alloy exceeds that of coated, /001/-oriented PWA 1480 single crystals at 1050 C, but at 650 C the life of the coated crystal is greater than that of the NiCoCrAlY alloy on a total strain basis.

Dynamic MEMS devices for multi-axial fatigue and elastic modulus measurement

NASA Astrophysics Data System (ADS)

White, Carolyn D.; Xu, Rui; Sun, Xiaotian; Komvopoulos, Kyriakos

2003-01-01

For reliable MEMS device fabrication and operation, there is a continued demand for precise characterization of materials at the micron scale. This paper presents a novel material characterization device for fatigue lifetime testing. The fatigue specimen is subjected to multi-axial loading, which is typical of most MEMS devices. Polycrystalline silicon (polysilicon) fatigue devices were fabricated using the MUMPS process with a three layer mask process ground plane, anchor, and structural layer of polysilicon. A fatigue device consists of two or three beams, attached to a rotating ring and anchored to the substrate on each end. In order to generate a sufficiently large stress, the fatigue devices were tested in resonance to produce a von Mises equivalent stress as high as 1 GPa, which is in the fracture strength range reported for polysilicon. A further increase of the stress in the beam specimens was obtained by introducing a notch with a focused ion beam. The notch resulted into a stress concentration factor of about 3.8, thereby producing maximum von Mises equivalent stress in the range of 1 through 4 GPa. This study provides insight into multi-axial fatigue testing under typical MEMS conditions and additional information about micron-scale polysilicon mechanical behavior, which is the current basic building material for MEMS devices.

Crack initiation and propagation in 50.9 at. pct Ni-Ti pseudoelastic shape-memory wires in bending-rotation fatigue

NASA Astrophysics Data System (ADS)

Sawaguchi, Tak Ahiro; Kausträter, Gregor; Yawny, Alejandro; Wagner, Martin; Eggeler, Gunther

2003-12-01

The structural fatigue of pseudoelastic Ni-Ti wires (50.9 at. pct Ni) was investigated using bending-rotation fatigue (BRF) tests, where a bent and otherwise unconstrained wire was forced to rotate at different rotational speeds. The number of cycles to failure ( N f ) was measured for different bending radii and wire thicknesses (1.0, 1.2, and 1.4 mm). The wires consisted of an alloy with a 50-nm grain size, no precipitates, and some TiC inclusions. In BRF tests, the surface of the wire is subjected to tension-compression cycles, and fatigue lives can be related to the maximum tension and compression strain amplitudes ( ɛ a ) in the wire surface. The resulting ɛ a - N f curves can be subdivided into three regimes. At ɛ a > 1 pct rupture occurs early (low N f ) and the fatigue-rupture characteristics were strongly dependent on ɛ a and the rotational speed (regime 1). For 0.75 pct < ɛ a < 1 pct, fatigue lives strongly increase and are characterized by a significant statistical scatter (regime 2). For ɛ a < 0.75 pct, no fatigue rupture occurs up to cycle numbers of 106 (regime 3). Using scanning electron microscopy (SEM), it was shown that surface cracks formed in regions with local stress raisers (such as inclusions and/or scratches). The growth of surface cracks during fatigue loading produced striations on the rupture surface; during final rupture, ductile voids form. The microstructural details of fatigue-damage accumulation during BRF testing are described and discussed.

Compressive Strength of Notched Poly(Phenylene Sulfide) Aerospace Composite: Influence of Fatigue and Environment

NASA Astrophysics Data System (ADS)

Niitsu, G. T.; Lopes, C. M. A.

2013-08-01

The purpose of this work is to evaluate the influences of fatigue and environmental conditions (-55 °C, 23 °C, and 82 °C/Wet) on the ultimate compression strength of notched carbon-fiber-reinforced poly(phenylene sulfide) composites by performing open-hole compression (OHC) tests. Analysis of the fatigue effect showed that at temperatures of -55 and 23 °C, the ultimate OHC strengths were higher for fatigued than for not-fatigued specimens; this could be attributed to fiber splitting and delamination during fatigue cycling, which reduces the stress concentration at the hole edge, thus increasing the composite strength. This effect of increasing strength for fatigued specimens was not observed under the 82 °C/Wet conditions, since the test temperature near the matrix glass transition temperature ( T g) together with moisture content resulted in matrix softening, suggesting a reduction in fiber splitting during cycling; similar OHC strengths were verified for fatigued and not-fatigued specimens tested at 82 °C/Wet. Analysis of the temperature effect showed that the ultimate OHC strengths decreased with increasing temperature. A high temperature together with moisture content (82 °C/Wet condition) reduced the composite compressive strengths, since a temperature close to the matrix T g resulted in matrix softening, which reduced the lateral support provided by the resin to the 0° fibers, leading to fiber instability failure at reduced applied loads. On the other hand, a low temperature (-55 °C) improved the compressive strength because of possible fiber-matrix interfacial strengthening, increasing the fiber contribution to compressive strength.

FY 2016 Status Report: CIRFT Testing on Spent Nuclear Fuels and Hydride Reorientation Study

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy-An John; Wang, Hong; Yan, Yong

This report provides a detailed description of the Cyclic Integrated Reversible-Bending Fatigue Tester (CIRFT) testing conducted on spent nuclear fuel (SNF) rods in FY 2016, including hydride reorientation test results. Contact-based measurement, or three-LVDT-based curvature measurement, of SNF rods has proven to be quite reliable in CIRFT testing. However, how the linear variable differential transformer (LVDT) head contacts the SNF rod may have a significant effect on the curvature measurement, depending on the magnitude and direction of rod curvature. To correct such contact/curvature issues, sensor spacing, defined as the amount of separation between the three LVDT probes, is a criticalmore » measurement that can be used to calculate rod curvature once the deflections are obtained. Recently developed CIRFT data analyses procedures were integrated into FY 2016 CIRFT testing results for the curvature measurements. The variations in fatigue life are provided in terms of moment, equivalent stress, curvature, and equivalent strain for the tested SNFs. The equivalent stress plot collapsed the data points from all of the SNFs into a single zone. A detailed examination revealed that, at same stress level, fatigue lives display a descending order as follows: H. B. Robinson Nuclear Power Station (HBR), Limerick Nuclear Power Station (LMK), mixed uranium-plutonium oxide (MOX). If looking at the strain, then LMK fuel has a slightly longer fatigue life than HBR fuel, but the difference is subtle. The knee point of endurance limit in the curve of moment and curvature or equivalent quantities is more clearly defined for LMK and HBR fuels. The treatment affects the fatigue life of specimens. Both a drop of 12 in. and radial hydride treatment (RHT) have a negative impact on fatigue life. The effect of thermal annealing on MOX fuel rods was relatively small at higher amplitude but became significant at low amplitude of moment. Thermal annealing tended to extend the fatigue life of MOX fuel rod specimens. However, for HR4 testing, the thermal annealing treatment showed a negative impact on the fatigue life of the HBR rod.« less

Computational Modeling Develops Ultra-Hard Steel

NASA Technical Reports Server (NTRS)

2007-01-01

Glenn Research Center's Mechanical Components Branch developed a spiral bevel or face gear test rig for testing thermal behavior, surface fatigue, strain, vibration, and noise; a full-scale, 500-horsepower helicopter main-rotor transmission testing stand; a gear rig that allows fundamental studies of the dynamic behavior of gear systems and gear noise; and a high-speed helical gear test for analyzing thermal behavior for rotorcraft. The test rig provides accelerated fatigue life testing for standard spur gears at speeds of up to 10,000 rotations per minute. The test rig enables engineers to investigate the effects of materials, heat treat, shot peen, lubricants, and other factors on the gear's performance. QuesTek Innovations LLC, based in Evanston, Illinois, recently developed a carburized, martensitic gear steel with an ultra-hard case using its computational design methodology, but needed to verify surface fatigue, lifecycle performance, and overall reliability. The Battelle Memorial Institute introduced the company to researchers at Glenn's Mechanical Components Branch and facilitated a partnership allowing researchers at the NASA Center to conduct spur gear fatigue testing for the company. Testing revealed that QuesTek's gear steel outperforms the current state-of-the-art alloys used for aviation gears in contact fatigue by almost 300 percent. With the confidence and credibility provided by the NASA testing, QuesTek is commercializing two new steel alloys. Uses for this new class of steel are limitless in areas that demand exceptional strength for high throughput applications.

Effect of some aggregate characteristics on the fatigue behavior of an asphaltic concrete mixture.

DOT National Transportation Integrated Search

1970-01-01

The effect of aggregate characteristics on the fatigue behavior of asphaltic mixtures was investigated by utilizing a laboratory constant deflection, flexural fatigue test. Coarse aggregate characteristics such as surface texture, rugosity, and flaki...

A literature review on fatigue and creep interaction

NASA Technical Reports Server (NTRS)

Chen, W. C.

1978-01-01

Life-time prediction methods, which are based on a number of empirical and phenomenological relationships, are presented. Three aspects are reviewed: effects of testing parameters on high temperature fatigue, life-time prediction, and high temperature fatigue crack growth.

Deformation history and load sequence effects on cumulative fatigue damage and life predictions

NASA Astrophysics Data System (ADS)

Colin, Julie

Fatigue loading seldom involves constant amplitude loading. This is especially true in the cooling systems of nuclear power plants, typically made of stainless steel, where thermal fluctuations and water turbulent flow create variable amplitude loads, with presence of mean stresses and overloads. These complex loading sequences lead to the formation of networks of microcracks (crazing) that can propagate. As stainless steel is a material with strong deformation history effects and phase transformation resulting from plastic straining, such load sequence and variable amplitude loading effects are significant to its fatigue behavior and life predictions. The goal of this study was to investigate the effects of cyclic deformation on fatigue behavior of stainless steel 304L as a deformation history sensitive material and determine how to quantify and accumulate fatigue damage to enable life predictions under variable amplitude loading conditions for such materials. A comprehensive experimental program including testing under fully-reversed, as well as mean stress and/or mean strain conditions, with initial or periodic overloads, along with step testing and random loading histories was conducted on two grades of stainless steel 304L, under both strain-controlled and load-controlled conditions. To facilitate comparisons with a material without deformation history effects, similar tests were also carried out on aluminum 7075-T6. Experimental results are discussed, including peculiarities observed with stainless steel behavior, such as a phenomenon, referred to as secondary hardening characterized by a continuous increase in the stress response in a strain-controlled test and often leading to runout fatigue life. Possible mechanisms for secondary hardening observed in some tests are also discussed. The behavior of aluminum is shown not to be affected by preloading, whereas the behavior of stainless steel is greatly influenced by prior loading. Mean stress relaxation in strain control and ratcheting in load control and their influence on fatigue life are discussed. Some unusual mean strain test results are presented for stainless steel 304L, where in spite of mean stress relaxation fatigue lives were significantly longer than fully-reversed tests. Prestraining indicated no effect on either deformation or fatigue behavior of aluminum, while it induced considerable hardening in stainless steel 304L and led to different results on fatigue life, depending on the test control mode. In step tests for stainless steel 304L, strong hardening induced by the first step of a high-low sequence significantly affects the fatigue behavior, depending on the test control mode used. For periodic overload tests of stainless steel 340L, hardening due to the overloads was progressive throughout life and more significant than in high-low step tests. For aluminum, no effect on deformation behavior was observed due to periodic overloads. However, the direction of the overloads was found to affect fatigue life, as tensile overloads led to longer lives, while compressive overloads led to shorter lives. Deformation and fatigue behaviors under random loading conditions are also presented and discussed for the two materials. The applicability of a common cumulative damage rule, the linear damage rule, is assessed for the two types of material, and for various loading conditions. While the linear damage rule associated with a strain-life or stress-life curve is shown to be fairly accurate for life predictions for aluminum, it is shown to poorly represent the behavior of stainless steel, especially in prestrained and high-low step tests, in load control. In order to account for prior deformation effects and achieve accurate fatigue life predictions for stainless steel, parameters including both stress and strain terms are required. The Smith-Watson-Topper and Fatemi-Socie approaches, as such parameters, are shown to correlate most test data fairly accurately. For damage accumulation under variable amplitude loading, the linear damage rule associated with strain-life or stress-life curves can lead to inaccurate fatigue life predictions, especially for materials presenting strong deformation memory effect, such as stainless steel 304L. The inadequacy of this method is typically attributed to the linear damage rule itself. On the contrary, this study demonstrates that damage accumulation using the linear damage rule can be accurate, provided that the linear damage rule is used in conjunction with parameters including both stress and strain terms. By including both loading history and response of the material in damage quantification, shortcomings of the commonly used linear damage rule approach can be circumvented in an effective manner. In addition, cracking behavior was also analyzed under various loading conditions. Results on microcrack initiation and propagation are presented in relation to deformation and fatigue behaviors of the materials. Microcracks were observed to form during the first few percent of life, indicating that most of the fatigue life of smooth specimens is spent in microcrack formation and growth. Analyses of fractured specimens showed that microcrack formation and growth is dependent on the loading history, and less important in aluminum than stainless steel 304L, due to the higher toughness of this latter material.

The effect of alcohol and fatigue on an FAA readiness-to-perform test.

DOT National Transportation Integrated Search

1995-08-01

Readiness to perform (RTP) testing is considered by some to be a broad-based alternative or supplement to biochemical testing for drugs and alcohol. Since it is also thought to detect impairment due to other sources (e.g., fatigue, illness, depressio...

Fatigue and shear behavior of HPC bulb-tee girders: final report.

DOT National Transportation Integrated Search

2005-02-01

Five 96-ft. (29.3-m) long, 72-in. (1.83-m) deep, precast, pretensioned bulb-tee girders were tested to evaluate their behavior under flexural fatigue. Three of the girders were also tested to measure their static shear strength. One girder was tested...

Effect of initial contact surface condition on the friction and wear properties of bearing steel in cyclic reciprocating sliding contact

NASA Astrophysics Data System (ADS)

Tanaka, Y.; Endo, M.; Moriyama, S.

2017-05-01

Delamination failure is one of the most important engineering problems. This failure can frequently be detrimental to rolling contact machine elements such as bearings, gear wheels, etc. This phenomenon, called rolling contact fatigue, has a close relationship not only with opening-mode but also with shear-mode fatigue crack growth. The crack face interference is known to significantly affect the shear-mode fatigue crack propagation and its threshold behavior. Quantitative investigation on friction and wear at fatigue crack faces in the material is essentially impossible. Previously, thus, a novel ring-on-ring test by making use of fatigue testing machine was proposed to simulate a cyclic reciprocating sliding contact of crack surfaces. However, this test procedure had some problems. For instance, in order to achieve the uniform contact at the start of test, the rubbing of specimens must be conducted in advance. By this treatment, the specimen surfaces were already damaged before the test. In this study, an improvement of experimental method was made to perform the test using the damage-free specimens. The friction and wear properties for heat-treated high carbon-chromium bearing steel were investigated with this new method and the results were compared to the results obtained by using the initially damaged specimens.

Ordering blood tests for patients with unexplained fatigue in general practice: what does it yield? Results of the VAMPIRE trial.

PubMed

Koch, Hèlen; van Bokhoven, Marloes A; ter Riet, Gerben; van Alphen-Jager, Jm Tineke; van der Weijden, Trudy; Dinant, Geert-Jan; Bindels, Patrick J E

2009-04-01

Unexplained fatigue is frequently encountered in general practice. Because of the low prior probability of underlying somatic pathology, the positive predictive value of abnormal (blood) test results is limited in such patients. The study objectives were to investigate the relationship between established diagnoses and the occurrence of abnormal blood test results among patients with unexplained fatigue; to survey the effects of the postponement of test ordering on this relationship; and to explore consultation-related determinants of abnormal test results. Cluster randomised trial. General practices of 91 GPs in the Netherlands. GPs were randomised to immediate or postponed blood-test ordering. Patients with new unexplained fatigue were included. Limited and expanded sets of blood tests were ordered either immediately or after 4 weeks. Diagnoses during the 1-year follow-up period were extracted from medical records. Two-by-two tables were generated. To establish independent determinants of abnormal test results, a multivariate logistic regression model was used. Data of 325 patients were analysed (71% women; mean age 41 years). Eight per cent of patients had a somatic illness that was detectable by blood-test ordering. The number of false-positive test results increased in particular in the expanded test set. Patients rarely re-consulted after 4 weeks. Test postponement did not affect the distribution of patients over the two-by-two tables. No independent consultation-related determinants of abnormal test results were found. Results support restricting the number of tests ordered because of the increased risk of false-positive test results from expanded test sets. Although the number of re-consulting patients was small, the data do not refute the advice to postpone blood-test ordering for medical reasons in patients with unexplained fatigue in general practice.

The effect of mental fatigue on sustained attention: an fNIRS study

NASA Astrophysics Data System (ADS)

Zhang, Zhen; Yang, Hanjun; Cao, Yong; Xu, Fenggang; Jiang, Jin; Jiao, Xuejun

2017-01-01

Sustained attention is the ability to keep focused and vigilance for long time in external stimulation, which was crucial in safe-critical human-machine system. While the ability of sustained attention will decline because of mental fatigue, even lead to serious accidents in fatigue state. Therefore, it is of great significance to explore the impact of fatigue on sustained attention. Functional Near-Infrared Spectroscopy (fNIRS) can measure cerebral hemoglobin in order to reflect cognitive function indirectly. In previous related fatigue studies, monotonous and long-time CPT (continuous performance test task) was often used to explore the performance change and brain activity, but the effect of time on task (TOT) was always involved. In this study, in order to avoid the TOT effect, the sustained attention task and fatigue task were separated. It was adopted in the study that the modified continuous performance test (CPT) was chosen as the sustained attention task and verbal 2-back task as the fatigue induced task. The fNIRS signals were extracted from 10 channels in the prefrontal cortex (PFC) from 20 healthy subjects. Studies found that cerebral lateralization increased significantly from alert to fatigue state in sustained attention task. Besides, Average oxyhemoglobin (HBO) of PFC increased significantly from alert to fatigue task, and the spatial pattern of activity of oxyhemoglobin also changed, which c be sensitive features to fatigue detection.

Effect of Cryorolling and Aging on Fatigue Behavior of Ultrafine-grained Al6061

NASA Astrophysics Data System (ADS)

Yadollahpour, M.; Hosseini-Toudeshky, H.; Karimzadeh, F.

2016-05-01

The effects of cryorolling (rolling at liquid nitrogen temperature) and heat treatment on tensile and high-cycle fatigue properties and fatigue crack growth rate of Al6061 alloy have been investigated in the present work. First, the solid solution-treated bulk Al6061 alloy was subjected to cryorolling with 90% total thickness reduction and subsequent short annealing at 205°C for 5 min and peak aging at 148°C for 39 h to achieve grain refinement and simultaneous improvement of the strength and ductility. Then, hardness measurements, tensile tests, fatigue life, and fatigue crack growth rate tests including fractography analyses using scanning electron microscopy were performed on bulk Al6061 alloy, cryorolled (CR), and cryorolled material followed by peak aging (PA). The PA specimen showed improved yield strength by 24%, ultimate tensile strength by 20%, and ductility by 12% as compared with the bulk Al6061 alloy. It is shown that the fatigue strength of both CR and PA specimens under a high-cycle fatigue regime are larger than that of the bulk Al6061 alloy. Also, fatigue crack growth rates of the CR and PA specimens show significant enhancement in fatigue crack growth resistances as compared with the bulk Al6061 alloy, as a result of grain refinement.

Cognitive behavioural therapy for reducing fatigue in post-polio syndrome and in facioscapulohumeral dystrophy: A comparison.

PubMed

Koopman, Fieke S; Brehm, Merel A; Beelen, Anita; Voet, Nicole; Bleijenberg, Gijs; Geurts, Alexander; Nollet, Frans

2017-07-07

Cognitive behavioural therapy does not reduce fatigue in post-polio syndrome, but is effective in facioscapulohumeral dystrophy. This difference in efficacy might be explained by a different role of cognitions in these conditions. To compare fatigue-related cognitions between patients with post-polio syndrome and facio-scapulohumeral dystrophy. Patients with post-polio syndrome (n = 21) and facioscapulohumeral dystrophy (n = 24) allocated to a cognitive behavioural therapy intervention in 2 identical trials. Assessed cognitions included: sense of control over fatigue; catastrophizing; acceptance; focusing on fatigue; and perceived social support. Group differences in cognitions (independent t-tests or Mann-Whitney U tests) and group differences in the association of cognitions with fatigue (linear regression models) were studied. No differences in cognitions were found between the 2 groups (p > 0.18). Furthermore, there were no cognition-by-group interaction effects, except for "perceived social support", for which a different association with fatigue was found between the 2 groups (p = 0.01). However, univariate models revealed no associations per group. Fatigue-related cognitions in severely fatigued patients with post-polio syndrome are not clearly different from that in facioscapulohumeral dystrophy. Thus, the lack of efficacy of cognitive behavioural therapy in post-polio syndrome cannot be attributed to unique cognitive characteristics of this population.

Determination of Failure Point of Asphalt-Mixture Fatigue-Test Results Using the Flow Number Method

NASA Astrophysics Data System (ADS)

Wulan, C. E. P.; Setyawan, A.; Pramesti, F. P.

2018-03-01

The failure point of the results of fatigue tests of asphalt mixtures performed in controlled stress mode is difficult to determine. However, several methods from empirical studies are available to solve this problem. The objectives of this study are to determine the fatigue failure point of the results of indirect tensile fatigue tests using the Flow Number Method and to determine the best Flow Number model for the asphalt mixtures tested. In order to achieve these goals, firstly the best asphalt mixture of three was selected based on their Marshall properties. Next, the Indirect Tensile Fatigue Test was performed on the chosen asphalt mixture. The stress-controlled fatigue tests were conducted at a temperature of 20°C and frequency of 10 Hz, with the application of three loads: 500, 600, and 700 kPa. The last step was the application of the Flow Number methods, namely the Three-Stages Model, FNest Model, Francken Model, and Stepwise Method, to the results of the fatigue tests to determine the failure point of the specimen. The chosen asphalt mixture is EVA (Ethyl Vinyl Acetate) polymer -modified asphalt mixture with 6.5% OBC (Optimum Bitumen Content). Furthermore, the result of this study shows that the failure points of the EVA-modified asphalt mixture under loads of 500, 600, and 700 kPa are 6621, 4841, and 611 for the Three-Stages Model; 4271, 3266, and 537 for the FNest Model; 3401, 2431, and 421 for the Francken Model, and 6901, 6841, and 1291 for the Stepwise Method, respectively. These different results show that the bigger the loading, the smaller the number of cycles to failure. However, the best FN results are shown by the Three-Stages Model and the Stepwise Method, which exhibit extreme increases after the constant development of accumulated strain.

Fatigue of a 3D Orthogonal Non-crimp Woven Polymer Matrix Composite at Elevated Temperature

NASA Astrophysics Data System (ADS)

Wilkinson, M. P.; Ruggles-Wrenn, M. B.

2017-12-01

Tension-tension fatigue behavior of two polymer matrix composites (PMCs) was studied at elevated temperature. The two PMCs consist of the NRPE polyimide matrix reinforced with carbon fibers, but have different fiber architectures: the 3D PMC is a singly-ply non-crimp 3D orthogonal weave composite and the 2D PMC, a laminated composite reinforced with 15 plies of an eight harness satin weave (8HSW) fabric. In order to assess the performance and suitability of the two composites for use in aerospace components designed to contain high-temperature environments, mechanical tests were performed under temperature conditions simulating the actual operating conditions. In all elevated temperature tests performed in this work, one side of the test specimen was at 329 °C while the other side was open to ambient laboratory air. The tensile stress-strain behavior of the two composites was investigated and the tensile properties measured for both on-axis (0/90) and off-axis (±45) fiber orientations. Elevated temperature had little effect on the on-axis tensile properties of the two composites. The off-axis tensile strength of both PMCs decreased slightly at elevated temperature. Tension-tension fatigue tests were conducted at elevated temperature at a frequency of 1.0 Hz with a ratio of minimum stress to maximum stress of R = 0.05. Fatigue run-out was defined as 2 × 105 cycles. Both strain accumulation and modulus evolution during cycling were analyzed for each fatigue test. The laminated 2D PMC exhibited better fatigue resistance than the 3D composite. Specimens that achieved fatigue run-out were subjected to tensile tests to failure to characterize the retained tensile properties. Post-test examination under optical microscope revealed severe delamination in the laminated 2D PMC. The non-crimp 3D orthogonal weave composite offered improved delamination resistance.

Evaluation of multidimensional COPD-related subjective fatigue following a pulmonary rehabilitation programme.

PubMed

Lewko, Agnieszka; Bidgood, Penelope L; Jewell, Andy; Garrod, Rachel

2014-01-01

Subjective fatigue has been recognised as an important, multi-component symptom in COPD. Pulmonary Rehabilitation (PR) improves fatigue component of the Chronic Respiratory Questionnaire, a quality of life (QoL) measure. However, it is not clear if all fatigue dimensions are affected equally. This study aims to evaluate changes in subjective multidimensional fatigue among people with COPD who participated in PR. Thirty seven stable COPD patients were recruited; 23 patients (15 male) mean age 68.5 (range 49-86) yrs, mean (SD) %predicted FEV1 45.3 (19.8); completed 7 weeks of PR. Assessments (pre and post PR) consisted of the Multidimensional Fatigue Inventory (MFI-20), QoL (SGRQ), Anxiety and Depression (HADS), the London Chest Activity of Daily Living Scale (LCADL), muscle strength, incremental (ISWT) and endurance (ESWT) shuttle walk tests. The differences between pre and post PR fatigue were tested using Wilcoxon's test and relationships with other outcomes were examined using Spearman's correlation. There were statistically significant improvements in Reduced Activity (RA) (p = 0.01), General (GF) (p < 0.01) and Physical Fatigue (PF) (p = 0.03) components of MFI-20 after PR, but there were no differences in Motivation or Mental Fatigue (p > 0.05). There were significant improvements in ISWT (p < 0.05), ESWT (p < 0.01) and muscle strength (p = 0.03). Statistically significant correlations (p < 0.05) were found between changes in GF and in both ISWT (r = -0.43) and SGRQ impact (r = 0.46); and between RA and ESWT changes (r = -0.45). Some dimensions of fatigue in COPD are modifiable by a 7-week PR programme. Change in fatigue dimensions in COPD may be associated with a change in maximal or endurance walking distances or QoL. Copyright © 2013 Elsevier Ltd. All rights reserved.

Fatigue Testing of Ring-Stiffened Traffic Signal Structures.

DOT National Transportation Integrated Search

2010-10-09

Based on in-service inspection of poles with traditional designs, the inventory of Wyoming Department of Transportation ?WYDOT? exhibited approximately a one-third cracking rate. A ring-stiffened connection is presently used. Sixteen fatigue tests we...

Influence of De-icers on the Corrosion and Fatigue Behavior of 4140 Steel

NASA Astrophysics Data System (ADS)

Dean, William P.; Sanford, Brittain J.; Wright, Matthew R.; Evans, Jeffrey L.

2012-11-01

The purpose of this test was to evaluate the effects of calcium magnesium acetate (CMA) and sodium chloride (NaCl)—two common substances used to de-ice roadways—on the corrosion and fatigue behavior of annealed AISI 4140 steel. When CMA-corroded, NaCl-corroded, and as-machined samples were tested using R = 0.1, and f = 20 Hz, it was found that, within the scope of this study, samples corroded in both 3.5% CMA solution and 3.5% NaCl solution exhibited a lower fatigue strength than samples tested in the as-machined, uncorroded condition. For the short lives tested in this study, the difference in the effects of CMA and NaCl is minimal. However, at longer lives it is suspected, based on the trends, that the CMA solution would be less detrimental to the fatigue life.

Sleep Quality and Fatigue Among Prehospital Providers

PubMed Central

Patterson, P. Daniel; Suffoletto, Brian P.; Kupas, Douglas F.; Weaver, Matthew D.; Hostler, David

2010-01-01

Background Fatigue is common among medical professionals and has been linked to poor performance and medical error. Objective To characterize sleep quality and its association with severe fatigue in emergency medical services (EMS) providers. Methods We studied a convenience sample of EMS providers who completed three surveys: the Pittsburgh Sleep Quality Index (PSQI), the Chalder Fatigue Questionnaire (CFQ), and a demographic survey. We used established measures to examine survey psychometrics and performed t-tests, analysis of variance (ANOVA), and chi- square tests to identify differences in PSQI and CFQ scores. Results One hundred nineteen surveys were completed. The eight-hour shift was most commonly reported (35.4%). A majority of subjects were overweight (41.9%) or obese (42.7%), and 59.6% had been diagnosed with one or more health conditions (e.g., diabetes). Results from psychometric tests were positive. The mean (± standard deviation) PSQI score was 9.2 (± 3.7). A CFQ score >4, indicating severe mental and physical fatigue, was present in 44.5% of the subjects. The mean PSQI score was higher among those reporting severe fatigue (11.3 ± 3.2) than among those not reporting fatigue (7.5 ± 3.0, p < 0.0001). Conclusions The results from this study suggest that the sleep quality and fatigue status of EMS workers are at unhealthy levels. The health and safety of the EMS worker and patient population should be considered in light of these results. PMID:20199233

Effect of Applied Potential on Fatigue Life of Electropolished Nitinol Wires

NASA Astrophysics Data System (ADS)

Sivan, Shiril; Di Prima, Matthew; Weaver, Jason D.

2017-09-01

Nitinol is used as a metallic biomaterial in medical devices due to its shape memory and pseudoelastic properties. The clinical performance of nitinol depends on factors which include the surface finish, the local environment, and the mechanical loads to which the device is subjected. Preclinical evaluations of device durability are performed with fatigue tests while electrochemical characterization methods such as ASTM F2129 are employed to evaluate corrosion susceptibility by determining the rest potential and breakdown potential. However, it is well established that the rest potential of a metal surface can vary with the local environment. Very little is known regarding the influence of voltage on fatigue life of nitinol. In this study, we developed a fatigue testing method in which an electrochemical system was integrated with a rotary bend wire fatigue tester. Samples were fatigued at various strain levels at electropotentials anodic and cathodic to the rest potential to determine if it could influence fatigue life. Wires at potentials negative to the rest potential had a significantly higher number of cycles to fracture than wires held at potentials above the breakdown potential. For wires for which no potential was applied, they had fatigue life similar to wires at negative potentials.

Low-cycle fatigue of Fe-20%Cr alloy processed by equal- channel angular pressing

NASA Astrophysics Data System (ADS)

Kaneko, Yoshihisa; Tomita, Ryuji; Vinogradov, Alexei

2014-08-01

Low-cycle fatigue properties were investigated on Fe-20%Cr ferritic stainless steel processed by equal channel angular pressing (ECAP). The Fe-20%Cr alloy bullets were processed for one to four passes via Route-Bc. The ECAPed samples were cyclically deformed at the constant plastic strain amplitude ɛpl of 5x10-4 at room temperature in air. After the 1-pass ECAP, low-angle grain boundaries were dominantly formed. During the low-cycle fatigue test, the 1-pass sample revealed the rapid softening which continued until fatigue fracture. Fatigue life of the 1-pass sample was shorter than that of a coarse-grained sample. After the 4-pass ECAP, the average grain size reduced down to about 1.5 μm. At initial stage of the low-cycle fatigue tests, the stress amplitude increased with increasing ECAP passes. At the samples processed for more than 2 passes, the cyclic softening was relatively moderate. It was found that fatigue life of the ECAPed Fe-20%Cr alloy excepting the 1-pass sample was improved as compared to the coarse-grained sample, even under the strain controlled fatigue condition.

A test procedure for determining the influence of stress ratio on fatigue crack growth

NASA Technical Reports Server (NTRS)

Fitzgerald, J. H.; Wei, R. P.

1974-01-01

A test procedure is outlined by which the rate of fatigue crack growth over a range of stress ratios and stress intensities can be determined expeditiously using a small number of specimens. This procedure was developed to avoid or circumvent the effects of load interactions on fatigue crack growth, and was used to develop data on a mill annealed Ti-6Al-4V alloy plate. Experimental data suggest that the rates of fatigue crack growth among the various stress ratios may be correlated in terms of an effective stress intensity range at given values of K max. This procedure is not to be used, however, for determining the corrosion fatigue crack growth characteristics of alloys when nonsteady-state effects are significant.

Flexibility and fatigue evaluation of oblique as compared with anterior lumbar interbody cages with integrated endplate fixation.

PubMed

Freeman, Andrew L; Camisa, William J; Buttermann, Glenn R; Malcolm, James R

2016-01-01

This study was undertaken to quantify the in vitro range of motion (ROM) of oblique as compared with anterior lumbar interbody devices, pullout resistance, and subsidence in fatigue. Anterior and oblique cages with integrated plate fixation (IPF) were tested using lumbar motion segments. Flexibility tests were conducted on the intact segments, cage, cage + IPF, and cage + IPF + pedicle screws (6 anterior, 7 oblique). Pullout tests were then performed on the cage + IPF. Fatigue testing was conducted on the cage + IPF specimens for 30,000 cycles. No ROM differences were observed in any test group between anterior and oblique cage constructs. The greatest reduction in ROM was with supplemental pedicle screw fixation. Peak pullout forces were 637 ± 192 N and 651 ± 127 N for the anterior and oblique implants, respectively. The median cage subsidence was 0.8 mm and 1.4 mm for the anterior and oblique cages, respectively. Anterior and oblique cages similarly reduced ROM in flexibility testing, and the integrated fixation prevented device displacement. Subsidence was minimal during fatigue testing, most of which occurred in the first 2500 cycles.

An Ultrasonic Guided Wave Method to Estimate Applied Biaxial Loads (Preprint)

DTIC Science & Technology

2011-11-01

VALIDATION A fatigue test was performed with an array of six surface-bonded PZT transducers on a 6061 aluminum plate as shown in Figure 4. The specimen...direct paths of propagation are oriented at different angles. This method is applied to experimental sparse array data recorded during a fatigue test...and the additional complication of the resulting fatigue cracks interfering with some of the direct arrivals is addressed via proper selection of

Experimental Plan for the Development of Equivalent Crack Size Distributions and a Monte Carlo Model of Fatigue in Low and High-kt Specimens of Corroded AA7050-T7451

DTIC Science & Technology

2012-03-01

18 3.3.7 Fractography ... Fractography : The fracture surfaces of the fractured fatigue specimens will be examined optically and in the scanning electron microscope to measure the size...scanned and added to the report containing the results from these fatigue tests. 3.3.7 Fractography Once a specimen has been tested, and assuming

Major Effects of Nonmetallic Inclusions on the Fatigue Life of Disk Superalloy Demonstrated

NASA Technical Reports Server (NTRS)

Gabb, Timothy P.; Telesman, Jack; Kantzos, Peter T.; Bonacuse, Peter J.; Barrie, Robert L.

2002-01-01

The fatigue properties of modern powder metallurgy disk alloys can vary because of the different steps of materials and component processing and machining. Among these variables, the effects of nonmetallic inclusions introduced during the powder atomization and handling processes have been shown to significantly degrade low-cycle fatigue life. The levels of inclusion contamination have, therefore, been reduced to less than 1 part per million in state-of-the-art nickel disk powder-processing facilities. Yet the large quantities of compressor and turbine disks weighing from 100 to over 1000 lb have enough total volume and surface area for these rare inclusions to still be present and limit fatigue life. The objective of this study was to investigate the effects on fatigue life of these inclusions, as part of the Crack Resistant Disk Materials task within the Ultra Safe Propulsion Project. Inclusions were carefully introduced at elevated levels in a nickel-base disk superalloy, U720, produced using powder metallurgy processing. Multiple strain-controlled fatigue tests were then performed on extracted test specimens at 650 C. Analyses were performed to compare the low-cycle fatigue lives and failure initiation sites as functions of inclusion content and fatigue conditions. Powder of the nickel-base superalloy U720 was atomized in argon at Special Metals Corporation, Inc., using production-scale high-cleanliness powder-processing facilities and handling practices. The powder was then passed through a 270-mesh screen. One portion of this powder was set aside for subsequent consolidation without introduced inclusions. Two other portions of this powder were seeded with alumina inclusions. Small, polycrystalline soft (Type 2) inclusions of about 50 mm diameter were carefully prepared and blended into one powder lot, and larger hard (Type 1) inclusions of about 150 mm mean diameter were introduced into the other seeded portion of powder. All three portions of powder were then sealed in separate containers, hot isostatically pressurized, extruded, forged into subscale disks, and heat treated. Low-cycle-fatigue specimens were then extracted, machined, and tested. Fatigue tests were performed at 650 C in closed-loop servohydraulic testing machines using induction heating and axial extensometers. All tests were continued to failure, and fractographic evaluations were performed on all specimens to determine the crack initiation sites. A large majority of the failures in specimens with introduced inclusions occurred at cracks initiating from inclusions at the specimen surface, as shown for each type of inclusion in the following bar chart. The inclusions significantly reduced fatigue life from unseeded material levels, as shown in the bar chart. These effects were found to depend on the strain range, strain ratio, and inclusion size. Tests at lower strain ranges and higher strain ratios resulted in larger effects of inclusions on life. Inclusion effects on life were thereby maximized in tests at the lowest strain range of 0.6 percent and the most positive strain ratio of 0.5. Under these conditions, small Type 2 inclusions reduced life substantially-- about 20 times, whereas large Type 1 inclusions dramatically reduced life 100 times. These results clearly demonstrate that it is essential to include the effects of inclusions for realistic predictions of disk fatigue life. Important issues, including temperature dependence, crack initiation versus propagation, surface treatments, realistic disk features and machining, and realistic disk spin testing will be addressed to accurately model inclusion effects on disk fatigue life. Fatigue life varied from well over 105 cycles for no inclusions to a little over 103 cycles for 100-micrometer inclusions. A single crack initiating at a surface-connected seeded inclusion caused failure in each case.

Comparison of cyclic fatigue resistance of novel nickel-titanium rotary instruments.

PubMed

Capar, Ismail Davut; Ertas, Huseyin; Arslan, Hakan

2015-04-01

New files (ProTaper Next/HyFlex/OneShape) are made from novel nickel-titanium (NiTi) alloys/treatments. The purpose of this study was to compare the cyclic fatigue resistance of these new instruments with that of Revo-S instruments. Four groups of 20 NiTi endodontic instruments were tested in steel canals with a 3 mm radius and a 60° angle of curvature. The cyclic fatigue of the following NiTi instruments with a tip size 25 and 0.06 taper that were manufactured with different alloys was tested: ProTaper Next X2 (M-Wire), OneShape (conventional NiTi), Revo-S Shaping Universal (conventional NiTi) and HyFlex 25/0.6 (controlled memory NiTi wire). A one-way anova and post-hoc Tukey's test (α = 0.05) revealed that the HyFlex files had the highest fatigue resistance and the Revo-S had the least fatigue resistance among the groups (P < 0.001). © 2014 Australian Society of Endodontology.

A novel in situ device based on a bionic piezoelectric actuator to study tensile and fatigue properties of bulk materials.

PubMed

Wang, Shupeng; Zhang, Zhihui; Ren, Luquan; Zhao, Hongwei; Liang, Yunhong; Zhu, Bing

2014-06-01

In this work, a miniaturized device based on a bionic piezoelectric actuator was developed to investigate the static tensile and dynamic fatigue properties of bulk materials. The device mainly consists of a bionic stepping piezoelectric actuator based on wedge block clamping, a pair of grippers, and a set of precise signal test system. Tensile and fatigue examinations share a set of driving system and a set of signal test system. In situ tensile and fatigue examinations under scanning electron microscope or metallographic microscope could be carried out due to the miniaturized dimensions of the device. The structure and working principle of the device were discussed and the effects of output difference between two piezoelectric stacks on the device were theoretically analyzed. The tensile and fatigue examinations on ordinary copper were carried out using this device and its feasibility was verified through the comparison tests with a commercial tensile examination instrument.

A psychometric study of the multidimensional fatigue inventory to assess fatigue in patients with schizophrenia spectrum disorders.

PubMed

Hedlund, Lena; Gyllensten, Amanda Lundvik; Hansson, Lars

2015-04-01

Fatigue is frequently reported by patients with mental illness. The multidimensional fatigue inventory (MFI-20) is a self-assessment instrument with 20 items including five dimensions of fatigue. The purpose of this study was to examine the test-retest reliability, internal consistency, convergent construct validity and feasibility of using MFI-20 in patients with schizophrenia spectrum disorders. Patients completed two self-assessment instruments, MFI-20 (n = 93) and Visual Analogue Scale (n = 79), twice within 1 week ± 2 days. Fifty-three patients also rated the feasibility of responding to the MFI-20 with a Likert scale. The test-retest reliability and validity were analysed by using Spearman's correlations and internal consistency by calculating Cronbach's α. The test-retest showed a correlation between .66 and .91 for all subscales of MFI. The internal consistency was .92. The analysis of convergent construct validity showed a correlation of .68 (time 1) and .77 (time 2). No item was systematically identified as being difficult to answer.

Fatigue degradation in compressively loaded composite laminates. [graphite-epoxy composites

NASA Technical Reports Server (NTRS)

Ramkumar, R. L.

1981-01-01

The effect of imbedded delaminations on the compression fatigue behavior of quasi-isotropic, T300/5208, graphite/epoxy laminates was investigated. Teflon imbedments were introduced during panel layup to create delaminations. Static and constant amplitude (R=10, omega = 10 Hz) fatigue tests were conducted. S-N data and half life residual strength data were obtained. During static compression loading, the maximum deflection of the buckled delaminated region was recorded. Under compression fatigue, growth of the imbedded delamination was identified as the predominant failure mode in most of the test cases. Specimens that exhibited others failures had a single low stiffness ply above the Teflon imbedment. Delamination growth during fatigue was monitored using DIB enhanced radiography. In specimens with buried delaminations, the dye penetrant (DIB) was introduced into the delaminated region through a minute laser drilled hole, using a hypodermic needle. A low kV, microfocus, X-ray unit was mounted near the test equipment to efficiently record the cyclic growth of buried delaminations on Polaroid film.

A novel in situ device based on a bionic piezoelectric actuator to study tensile and fatigue properties of bulk materials

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Shupeng; Zhang, Zhihui, E-mail: zhzh@jlu.edu.cn; Ren, Luquan

2014-06-15

In this work, a miniaturized device based on a bionic piezoelectric actuator was developed to investigate the static tensile and dynamic fatigue properties of bulk materials. The device mainly consists of a bionic stepping piezoelectric actuator based on wedge block clamping, a pair of grippers, and a set of precise signal test system. Tensile and fatigue examinations share a set of driving system and a set of signal test system. In situ tensile and fatigue examinations under scanning electron microscope or metallographic microscope could be carried out due to the miniaturized dimensions of the device. The structure and working principlemore » of the device were discussed and the effects of output difference between two piezoelectric stacks on the device were theoretically analyzed. The tensile and fatigue examinations on ordinary copper were carried out using this device and its feasibility was verified through the comparison tests with a commercial tensile examination instrument.« less

Effect of helium to dpa ratio on fatigue behavior of austenitic stainless steel irradiated to 2 dpa

NASA Astrophysics Data System (ADS)

Ioka, I.; Yonekawa, M.; Miwa, Y.; Mimura, H.; Tsuji, H.; Hoshiya, T.

2000-12-01

The effect of helium due to nuclear transmutation reactions during neutron irradiation on low cycle fatigue life of type 304 stainless steel was investigated. The specimens were irradiated in spectrally tailored capsules in the Japan Materials Testing Reactor (JMTR) at a temperature of 823 K to a neutron fluence of approximately 1×1025 n/m2 (E>1 MeV) and helium levels of 0.8, 2.5 and 8.1 appm. The low cycle fatigue tests were performed in total axial strain ranges of 0.8-1.6% at 823 K. A laser extensometer was used for controlling the axial strain of a specimen under cyclic testing. The difference between unirradiated and irradiated specimens is quite clear and appears to be a reduction by a factor of 2-5 in fatigue life. The helium concentration of the specimen is not the main factor to shorten fatigue life in the present experimental condition.

Influence of Mixed Mode I-Mode II Loading on Fatigue Delamination Growth Characteristics of a Graphite Epoxy Tape Laminate

NASA Technical Reports Server (NTRS)

Ratcliffe, James G.; Johnston, William M., Jr.

2014-01-01

Mixed mode I-mode II interlaminar tests were conducted on IM7/8552 tape laminates using the mixed-mode bending test. Three mixed mode ratios, G(sub II)/G(sub T) = 0.2, 0.5, and 0.8, were considered. Tests were performed at all three mixed-mode ratios under quasi-static and cyclic loading conditions, where the former static tests were used to determine initial loading levels for the latter fatigue tests. Fatigue tests at each mixed-mode ratio were performed at four loading levels, Gmax, equal to 0.5G(sub c), 0.4G(sub c), 0.3G(sub c), and 0.2G(sub c), where G(sub c) is the interlaminar fracture toughness of the corresponding mixed-mode ratio at which a test was performed. All fatigue tests were performed using constant-amplitude load control and delamination growth was automatically documented using compliance solutions obtained from the corresponding quasi-static tests. Static fracture toughness data yielded a mixed-mode delamination criterion that exhibited monotonic increase in Gc with mixed-mode ratio, G(sub II)/G(sub T). Fatigue delamination onset parameters varied monotonically with G(sub II)/G(sub T), which was expected based on the fracture toughness data. Analysis of non-normalized data yielded a monotonic change in Paris law exponent with mode ratio. This was not the case when normalized data were analyzed. Fatigue data normalized by the static R-curve were most affected in specimens tested at G(sub II)/G(sub T)=0.2 (this process has little influence on the other data). In this case, the normalized data yielded a higher delamination growth rate compared to the raw data for a given loading level. Overall, fiber bridging appeared to be the dominant mechanism, affecting delamination growth rates in specimens tested at different load levels and differing mixed-mode ratios.

Response of SiC{sub f}/Si{sub 3}N{sub 4} composites under static and cyclic loading -- An experimental and statistical analysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahfuz, H.; Maniruzzaman, M.; Vaidya, U.

1997-04-01

Monotonic tensile and fatigue response of continuous silicon carbide fiber reinforced silicon nitride (SiC{sub f}/Si{sub 3}N{sub 4}) composites has been investigated. The monotonic tensile tests have been performed at room and elevated temperatures. Fatigue tests have been conducted at room temperature (RT), at a stress ratio, R = 0.1 and a frequency of 5 Hz. It is observed during the monotonic tests that the composites retain only 30% of its room temperature strength at 1,600 C suggesting a substantial chemical degradation of the matrix at that temperature. The softening of the matrix at elevated temperature also causes reduction in tensilemore » modulus, and the total reduction in modulus is around 45%. Fatigue data have been generated at three load levels and the fatigue strength of the composite has been found to be considerably high; about 75% of its ultimate room temperature strength. Extensive statistical analysis has been performed to understand the degree of scatter in the fatigue as well as in the static test data. Weibull shape factors and characteristic values have been determined for each set of tests and their relationship with the response of the composites has been discussed. A statistical fatigue life prediction method developed from the Weibull distribution is also presented. Maximum Likelihood Estimator with censoring techniques and data pooling schemes has been employed to determine the distribution parameters for the statistical analysis. These parameters have been used to generate the S-N diagram with desired level of reliability. Details of the statistical analysis and the discussion of the static and fatigue behavior of the composites are presented in this paper.« less

In-air and pressurized water reactor environment fatigue experiments of 316 stainless steel to study the effect of environment on cyclic hardening

NASA Astrophysics Data System (ADS)

Mohanty, Subhasish; Soppet, William K.; Majumdar, Saurindranath; Natesan, Krishnamurti

2016-05-01

Argonne National Laboratory (ANL), under the sponsorship of Department of Energy's Light Water Reactor Sustainability (LWRS) program, is trying to develop a mechanistic approach for more accurate life estimation of LWR components. In this context, ANL has conducted many fatigue experiments under different test and environment conditions on type 316 stainless steel (316 SS) material which is widely used in the US reactors. Contrary to the conventional S ∼ N curve based empirical fatigue life estimation approach, the aim of the present DOE sponsored work is to develop an understanding of the material ageing issues more mechanistically (e.g. time dependent hardening and softening) under different test and environmental conditions. Better mechanistic understanding will help develop computer-based advanced modeling tools to better extrapolate stress-strain evolution of reactor components under multi-axial stress states and hence help predict their fatigue life more accurately. Mechanics-based modeling of fatigue such as by using finite element (FE) tools requires the time/cycle dependent material hardening properties. Presently such time-dependent material hardening properties are hardly available in fatigue modeling literature even under in-air conditions. Getting those material properties under PWR environment, are even harder. Through this work we made preliminary attempt to generate time/cycle dependent stress-strain data both under in-air and PWR water conditions for further study such as for possible development of material models and constitutive relations for FE model implementation. Although, there are open-ended possibility to further improve the discussed test methods and related material estimation techniques we anticipate that the data presented in this paper will help the metal fatigue research community particularly, the researchers who are dealing with mechanistic modeling of metal fatigue such as using FE tools. In this paper the fatigue experiments under different test and environment conditions and related stress-strain results for 316 SS are discussed.

An assessment of cold work effects on strain-controlled low-cycle fatigue behavior of type 304 stainless steel

NASA Astrophysics Data System (ADS)

Rao, K. Bhanu Sankara; Valsan, M.; Sandhya, R.; Mannan, S. L.; Rodriguez, P.

1993-04-01

The influence of prior cold work (PCW) on low-cycle fatigue (LCF) behavior of type 304 stainless steel has been studied at 300, 823, 923, and 1023 K by conducting total axial strain-controlled tests in solution annealed (SA, 0 pct PCW) condition and on specimens having three levels of PCW, namely, 10, 20, and 30 pct. A triangular waveform with a constant frequency of 0.1 Hz was employed for all of the tests performed over strain amplitudes in the range of ±0.25 to ± 1.25 pct. These studies have revealed that fatigue life is strongly dependent on PCW, temperature, and strain amplitude employed in testing. The SA material generally displayed better endurance in terms of total and plastic strain amplitudes than the material in 10, 20, and 30 pct PCW conditions at all of the temperatures. However, at 300 K at very low strain amplitudes, PCW material exhibited better total strain fatigue resistance. At 823 K, LCF life decreased with increasing PCW, whereas at 923 K, 10 pct PCW displayed the lowest life. An improvement in life occurred for prior deformations exceeding 10 pct at all strain amplitudes at 923 K. Fatigue life showed a noticeable decrease with increasing temperature up to 1023 K in PCW state. On the other hand, SA material displayed a minimum in fatigue life at 923 K. The fatigue life results of SA as well as all of the PCW conditions obeyed the Basquin and Coffin-Manson relationships at 300, 823, and 923 K. The constants and exponents in these equations were found to depend on the test temperature and prior metallurgical state of the material. A study is made of cyclic stress-strain behavior in SA and PCW states and the relationship between the cyclic strain-hardening exponent and fatigue behavior at different temperatures has been explored. The influence of environment on fatigue crack initiation and propagation behavior has been examined.

Endurance and failure characteristics of modified Vasco X-2, CBS 600 and AISI 9310 spur gears. [aircraft construction materials

NASA Technical Reports Server (NTRS)

Townsend, D. P.; Zaretsky, E. V.

1980-01-01

Gear endurance tests and rolling-element fatigue tests were conducted to compare the performance of spur gears made from AISI 9310, CBS 600 and modified Vasco X-2 and to compare the pitting fatigue lives of these three materials. Gears manufactured from CBS 600 exhibited lives longer than those manufactured from AISI 9310. However, rolling-element fatigue tests resulted in statistically equivalent lives. Modified Vasco X-2 exhibited statistically equivalent lives to AISI 9310. CBS 600 and modified Vasco X-2 gears exhibited the potential of tooth fracture occurring at a tooth surface fatigue pit. Case carburization of all gear surfaces for the modified Vasco X-2 gears results in fracture at the tips of the gears.

A Review of Fatigue Crack Growth in Metallics at Low Stress Intensities.

DTIC Science & Technology

1983-01-01

received R 0,35 * 257 C 2i 0*C b -sT 625C 0 0 10 0 ~1O90 co 0 C 2 2,5 3 4 5 67 8 910C12 15 20 A K MN rfiV2 Figure 31 The influence of test temperature...34 L.2. 11111 L25I MICROCOPY RESOLUTION TEST CHART NATIONAL. BUREAU OF STANDARDS 1963-A A 44-7 F 49620-82-C-0088 A REVIEW OF FATIGUE CRACK GROWTH IN...relation to the following variables, mean stress, yield stress, test temperature, test frequency, fatigue crack closure, microstructure, environment and

Development of an algorithm for an EEG-based driver fatigue countermeasure.

PubMed

Lal, Saroj K L; Craig, Ashley; Boord, Peter; Kirkup, Les; Nguyen, Hung

2003-01-01

Fatigue affects a driver's ability to proceed safely. Driver-related fatigue and/or sleepiness are a significant cause of traffic accidents, which makes this an area of great socioeconomic concern. Monitoring physiological signals while driving provides the possibility of detecting and warning of fatigue. The aim of this paper is to describe an EEG-based fatigue countermeasure algorithm and to report its reliability. Changes in all major EEG bands during fatigue were used to develop the algorithm for detecting different levels of fatigue. The software was shown to be capable of detecting fatigue accurately in 10 subjects tested. The percentage of time the subjects were detected to be in a fatigue state was significantly different than the alert phase (P<.01). This is the first countermeasure software described that has shown to detect fatigue based on EEG changes in all frequency bands. Field research is required to evaluate the fatigue software in order to produce a robust and reliable fatigue countermeasure system. The development of the fatigue countermeasure algorithm forms the basis of a future fatigue countermeasure device. Implementation of electronic devices for fatigue detection is crucial for reducing fatigue-related road accidents and their associated costs.

The Development and Preliminary Testing of an Instrument for Assessing Fatigue Self-management Outcomes in Patients With Advanced Cancer.

PubMed

Chan, Raymond Javan; Yates, Patsy; McCarthy, Alexandra L

Fatigue is one of the most distressing and commonly experienced symptoms in patients with advanced cancer. Although the self-management (SM) of cancer-related symptoms has received increasing attention, no research instrument assessing fatigue SM outcomes for patients with advanced cancer is available. The aim of this study was to describe the development and preliminary testing of an interviewer-administered instrument for assessing the frequency and perceived levels of effectiveness and self-efficacy associated with fatigue SM behaviors in patients with advanced cancer. The development and testing of the Self-efficacy in Managing Symptoms Scale-Fatigue Subscale for Patients With Advanced Cancer (SMSFS-A) involved a number of procedures: item generation using a comprehensive literature review and semistructured interviews, content validity evaluation using expert panel reviews, and face validity and test-retest reliability evaluation using pilot testing. Initially, 23 items (22 specific behaviors with 1 global item) were generated from the literature review and semistructured interviews. After 2 rounds of expert panel review, the final scale was reduced to 17 items (16 behaviors with 1 global item). Participants in the pilot test (n = 10) confirmed that the questions in this scale were clear and easy to understand. Bland-Altman analysis showed agreement of results over a 1-week interval. The SMSFS-A items were generated using multiple sources. This tool demonstrated preliminary validity and reliability. The SMSFS-A has the potential to be used for clinical and research purposes. Nurses can use this instrument for collecting data to inform the initiation of appropriate fatigue SM support for this population.

Effect of load ratio on fatigue crack propagation behavior of solid-solution-strengthened Ni-based superalloys at elevated temperature

NASA Astrophysics Data System (ADS)

Ma, Longzhou; Roy, Shawoon K.

2013-04-01

The fatigue crack propagation (FCP) behavior of two solid-solution-strengthened Ni-based superalloys, INCONEL 617 and HAYNES 230, were studied simultaneously in laboratory air using a constant stress intensity factor (K)-controlled mode with different load ratios (R-ratio) at 700 °C. The FCP tests were performed in both cycle and time-dependent FCP domains to examine the effect of R-ratio on the FCP rate, da/dn. For cycle-dependent FCP test, a 1-s sinusoidal fatigue was applied for a compact tension (CT) specimen of INCONEL 617 and HAYNES 230 to measure their FCP rates. For time-dependent FCP test, a 3-s sinusoidal fatigue with a hold time of 300 s at maximum load was applied. Both cycle/time-dependent FCP behaviors were characterized and analyzed. The results showed that increasing R-ratio would introduce the fatigue incubation and decrease the FCP rates at cycle-dependent FCP tests. On the contrary, fatigue incubation was not observed at time-dependent FCP tests for both INCONEL 617 and HAYNES 230 at each tested R-ratio, suggesting that association of maximum load (Kmax) with crack tip open displacement (CTOD) and environmental factor governed the FCP process. Also, for time-dependent FCP, HAYNES 230 showed lower FCP rates than INCONEL 617 regardless of R-ratio. However, for cycle-dependent FCP, HAYNES 230 showed the lower FCP rates only at high R-ratios. Fracture surface of specimens were examined using SEM to investigate the cracking mechanism under cycle/time-dependent FCP condition with various R-ratios.

Load-bearing capacity of all-ceramic posterior inlay-retained fixed dental prostheses.

PubMed

Puschmann, Djamila; Wolfart, Stefan; Ludwig, Klaus; Kern, Matthias

2009-06-01

The purpose of this in vitro study was to compare the quasi-static load-bearing capacity of all-ceramic resin-bonded three-unit inlay-retained fixed dental prostheses (IRFDPs) made from computer-aided design/computer-aided manufacturing (CAD/CAM)-manufactured yttria-stabilized tetragonal zirconia polycrystals (Y-TZP) frameworks with two different connector dimensions, with and without fatigue loading. Twelve IRFDPs each were made with connector dimensions 3 x 3 mm(2) (width x height) (control group) and 3 x 2 mm(2) (test group). Inlay-retained fixed dental prostheses were adhesively cemented on identical metal-models using composite resin cement. Subgroups of six specimens each were fatigued with maximal 1,200,000 loading cycles in a chewing simulator with a weight load of 25 kg and a load frequency of 1.5 Hz. The load-bearing capacity was tested in a universal testing machine for IRFDPs without fatigue loading and for IRFDPs that had not already fractured during fatigue loading. During fatigue testing one IRFDP (17%) of the test group failed. Under both loading conditions, IRFDPs of the control group exhibited statistically significantly higher load-bearing capacities than the test group. Fatigue loading reduced the load-bearing capacity in both groups. Considering the maximum chewing forces in the molar region, it seems possible to use zirconia ceramic as a core material for IRFDPs with a minimum connector dimension of 9 mm(2). A further reduction of the connector dimensions to 6 mm(2) results in a significant reduction of the load-bearing capacity.

Heat pipe fatigue test specimen: Metallurgical evaluation

NASA Technical Reports Server (NTRS)

Walak, Steven E.; Cronin, Michael J.; Grobstein, Toni

1992-01-01

An innovative creep/fatigue test was run to simulate the temperature, mechanical load, and sodium corrosion conditions expected in a heat pipe designed to supply thermal energy to a Stirling cycle power converter. A sodium-charged Inconel 718 heat pipe with a Nickel 200 screen wick was operated for 1090 hr at temperatures between 950 K (1250 F) and 1050 K (1430 F) while being subjected to creep and fatigue loads in a servo-hydraulic testing machine. After testing, the heat pipe was sectioned and examined using optical microscopy, scanning electron microscopy, and electron microprobe analysis with wavelength dispersive x-ray spectroscopy. The analysis concentrated on evaluating topographic, microstructural, and chemical changes in the sodium exposed surfaces of the heat pipe wall and wick. Surface changes in the evaporator, condenser, and adiabatic sections of the heat pipe were examined in an effort to correlate the changes with the expected sodium environment in the heat pipe. This report describes the setup, operating conditions, and analytical results of the sodium heat pipe fatigue test.

Effectiveness of Shot Peening In Suppressing Fatigue Cracking At Non-Metallic Inclusions In Udimet(Registered Trademark)720

NASA Technical Reports Server (NTRS)

Barrie, Robert L.; Gabb, Timothy P.; Telesman, Jack; Kantzos, Peter T.; Prescenzi, Anthony; Biles, T.; Bonacuse, P. J.

2006-01-01

The fatigue lives of modern powder metallurgy disk alloys can be reduced over an order of magnitude by cracking at inherent non-metallic inclusions. The objective of this work was to study the effectiveness of shot peening in suppressing LCF crack initiation and growth at surface nonmetallic inclusions. Inclusions were carefully introduced at elevated levels during powder metallurgy processing of the nickel-base disk superalloy Udimet 720. Multiple strain-controlled fatigue tests were then performed on machined specimens with and without shot peened test sections at 427 C and 650 C. The low cycle fatigue lives and failure initiation sites varied as functions of inclusion content, shot peening, and fatigue conditions. A large majority of the failures in as-machined specimens with the introduced inclusions occurred at cracks initiating from inclusions intersecting the specimen surface. These inclusions reduced fatigue life by up to 100X, when compared to lives of material without inclusions residing at specimen surface. Large inclusions produced the greatest reductions in life for tests at low strain ranges and high strain ratios. Shot peening improved life in many cases by reducing the most severe effects of inclusions.

Results of inphase axial-torsional fatigue experiments on 304 stainless steel

NASA Technical Reports Server (NTRS)

Bonacuse, Peter J.; Kalluri, Sreeramesh

1989-01-01

A series of axial-torsional, inphase, strain-controlled, low-cycle fatigue tests were performed at room temperature on tubular specimens of 304 stainless steel. The program was conducted in cooperation with the task group on multiaxial fatigue research of ASTM committee E-09. The objective was to quantify the variability in multiaxial test results among several laboratories. Only included is data which was generated at the NASA Lewis Research Center's High Temperature Fatigue and Structures Laboratory. The experimental equipment and procedures used are described. The tubular specimens were polished on the outer surface to aid in the use of a cellulose film surface replication technique for crack detection. However, cracking initiated predominantly on the internal surface for all specimens. Honing of the bore of the tubular specimens lessened but did not entirely eliminate this problem. The observed fatigue lives are compared with lives calculated from three multiaxial life models. Constants for the life prediction models were obtained from uniaxial and torsional tests performed on the same heat of material. The observed fatigue lives agreed with calculated lives to within a factor of two for all but one of the life prediction models.

Construction and validation of the fatigue impact and severity self-assessment for youth and young adults with cerebral palsy.

PubMed

Brunton, Laura K; Bartlett, Doreen J

2017-07-01

The Fatigue Impact and Severity Self-Assessment (FISSA) was created to assess the impact, severity, and self-management of fatigue for individuals with cerebral palsy (CP) aged 14-31 years. Items were generated from a review of measures and interviews with individuals with CP. Focus groups with health-care professionals were used for item reduction. A mailed survey was conducted (n=163/367) to assess the factor structure, known-groups validity, and test-retest reliability. The final measure contained 31 items in two factors and discriminated between individuals expected to have different levels of fatigue. Individuals with more functional abilities reported less fatigue (p < 0.002) and those with higher pain reported higher fatigue (p < 0.001). The FISSA was shown to have adequate test-retest reliability, intraclass correlation coefficient (ICC)(3,1)=0.74 (95% confidence interval [CI] 0.53-0.87). The FISSA valid and reliable for individuals with CP. It allows for identification of the activities that may be compromised by fatigue to enhance collaborative goal setting and intervention planning.

Interim Report on Fatigue Characteristics of a Typical Metal Wing

NASA Technical Reports Server (NTRS)

Kepert, J L; Payne, A O

1956-01-01

Constant amplitude fatigue tests of seventy-two P-51D "Mustang" wings are reported. The tests were performed by a vibrational loading system and by an hydraulic loading device for conditions with and without varying amounts of pre-load. The results indicate that: (a) the frequency of occurrence of fatigue at any one location is related to the range of the loads applied, (b) the rate of propagation of visible cracks is more or less constant for a large portion of the life of the specimen, (c) the fatigue strength of the structure is similar to that of notched material having a theoretical stress concentration factor of more than 3.0, (d) the frequency distribution of fatigue life is approximately logarithmic normal, (e) the relative increase in fatigue life for a given pre-load depends on the maximum load of the loading cycle only, while the optimum pre-load value is approximately 85 percent of the ultimate failing load, and (f) that normal design procedure will not permit the determination of local stress levels with sufficient accuracy to determine the fatigue strength of an element of a redundant structure.

The Influence of Work-Related Fatigue, Work Conditions, and Personal Characteristics on Intent to Leave Among New Nurses.

PubMed

Liu, Yi; Wu, Li-Min; Chou, Pi-Ling; Chen, Mei-Hsin; Yang, Li-Chien; Hsu, Hsin-Tien

2016-01-01

This study aimed to (a) test the fit of the hypothesized model for new nurses' intent to leave and (b) determine the extent to which personal characteristics, work conditions, and work-related fatigue predict intent to leave among new nurses. This study was a cross-sectional survey study. A total of 162 new nurses were recruited. A hypothesized model was proposed for model testing. Structural equation modelling was used for data analysis. Work conditions only had an effect through work-related fatigue on new nurses' intent to leave. Personal characteristics did not have a significant effect on new nurses' intent to leave. The final model showed a good fit. Work-related fatigue, work conditions, and health explained 65% of the variance in new nurses' intent to leave. Work-related fatigue was a major determinant of new nurses' intent to leave. More attention should be paid to fatigue reduction strategies among new nurses. Work-related fatigue should be monitored, particularly for new nurses who work more than 10 hr per day and who have greater workloads. © 2015 Sigma Theta Tau International.

Sustained Attention is Associated with Error Processing Impairment: Evidence from Mental Fatigue Study in Four-Choice Reaction Time Task

PubMed Central

Xiao, Yi; Ma, Feng; Lv, Yixuan; Cai, Gui; Teng, Peng; Xu, FengGang; Chen, Shanguang

2015-01-01

Attention is important in error processing. Few studies have examined the link between sustained attention and error processing. In this study, we examined how error-related negativity (ERN) of a four-choice reaction time task was reduced in the mental fatigue condition and investigated the role of sustained attention in error processing. Forty-one recruited participants were divided into two groups. In the fatigue experiment group, 20 subjects performed a fatigue experiment and an additional continuous psychomotor vigilance test (PVT) for 1 h. In the normal experiment group, 21 subjects only performed the normal experimental procedures without the PVT test. Fatigue and sustained attention states were assessed with a questionnaire. Event-related potential results showed that ERN (p < 0.005) and peak (p < 0.05) mean amplitudes decreased in the fatigue experiment. ERN amplitudes were significantly associated with the attention and fatigue states in electrodes Fz, FC1, Cz, and FC2. These findings indicated that sustained attention was related to error processing and that decreased attention is likely the cause of error processing impairment. PMID:25756780

High-temperature acoustic test facilities and methods

NASA Astrophysics Data System (ADS)

Pearson, Jerome

1994-09-01

The Wright Laboratory is the Air Force center for air vehicles, responsible for developing advanced technology and incorporating it into new flight vehicles and for continuous technological improvement of operational air vehicles. Part of that responsibility is the problem of acoustic fatigue. With the advent of jet aircraft in the 1950's, acoustic fatigue of aircraft structure became a significant problem. In the 1960's the Wright Laboratory constructed the first large acoustic fatigue test facilities in the United States, and the laboratory has been a dominant factor in high-intensity acoustic testing since that time. This paper discusses some of the intense environments encountered by new and planned Air Force flight vehicles, and describes three new acoustic test facilities of the Wright Laboratory designed for testing structures in these dynamic environments. These new test facilities represent the state of the art in high-temperature, high-intensity acoustic testing and random fatigue testing. They will allow the laboratory scientists and engineers to test the new structures and materials required to withstand the severe environments of captive-carry missiles, augmented lift wings and flaps, exhaust structures of stealth aircraft, and hypersonic vehicle structures well into the twenty-first century.

Fatigue-Arrestor Bolts

NASA Technical Reports Server (NTRS)

Onstott, Joseph W.; Gilster, Mark; Rodriguez, Sergio; Larson, John E.; Wickham, Mark D.; Schoonover, Kevin E.

1995-01-01

Bolts that arrest (or, more precisely, retard) onset of fatigue cracking caused by inelastic strains developed. Specifically developed to be installed in flange holes of unrestrained rocket engine nozzle. Fanges sometimes used to bolt nozzle to test stand; however, when rocket engine operated without this restraint, region around bolt holes experience severe inelastic strains causing fatigue cracking. Interference fits introduce compressive preloads that retard fatigue by reducing ranges of strains. Principle of these fatigue-arrestor bolts also applicable to holes in plates made of other materials and/or used for different purposes.

Development of Fatigue and Crack Propagation Design and Analysis Methodology in a Corrosive Environment for Typical Mechanically-Fastened Joints. Volume 2. State-of-the-Art Assessment.

DTIC Science & Technology

1983-03-01

120] hypothesized a linear summation model to predict the corrosion -fatigue behavior above Kjscc for a high-strength steel . The model considers the...120] could satisfactorily predict the rates of corrosion -fatigue-crack growth for 18-Ni Maraging steels tested in several gaseous and aqueous...NADC-83126-60 Vol. II 6. The corrosion fatigue behavior of titanium alloys is very complex. Therefore, a better understanding of corrosion fatigue

Effects on fatigue life of gate valves due to higher torque switch settings during operability testing

DOE Office of Scientific and Technical Information (OSTI.GOV)

Richins, W.D.; Snow, S.D.; Miller, G.K.

1995-12-01

Some motor operated valves now have higher torque switch settings due to regulatory requirements to ensure valve operability with appropriate margins at design basis conditions. Verifying operability with these settings imposes higher stem loads during periodic inservice testing. These higher test loads increase stresses in the various valve internal parts which may in turn increase the fatigue usage factors. This increased fatigue is judged to be a concern primarily in the valve disks, seats, yokes, stems, and stem nuts. Although the motor operators may also have significantly increased loading, they are being evaluated by the manufacturers and are beyond themore » scope of this study. Two gate valves representative of both relatively weak and strong valves commonly used in commercial nuclear applications were selected for fatigue analyses. Detailed dimensional and test data were available for both valves from previous studies at the Idaho National Engineering Laboratory. Finite element models were developed to estimate maximum stresses in the internal parts of the valves and to identity the critical areas within the valves where fatigue may be a concern. Loads were estimated using industry standard equations for calculating torque switch settings prior and subsequent to the testing requirements of USNRC Generic Letter 89--10. Test data were used to determine both; (1) the overshoot load between torque switch trip and final seating of the disk during valve closing and (2) the stem thrust required to open the valves. The ranges of peak stresses thus determined were then used to estimate the increase in the fatigue usage factors due to the higher stem thrust loads. The usages that would be accumulated by 100 base cycles plus one or eight test cycles per year over 40 and 60 years of operation were calculated.« less

Effect of aromatherapy via inhalation on the sleep quality and fatigue level in people undergoing hemodialysis.

PubMed

Muz, Gamze; Taşcı, Sultan

2017-10-01

The most common problems in hemodialysis patients are sleep disorders and fatigue. This randomized-controlled experimental study was conducted to determine the effect of aromatherapy applied by inhalation on sleep quality and fatigue level in hemodialysis patients. The study was completed in five hemodialysis centers settled in two provinces with 27 intervention group patients and 35 controls, being totally 62 patients, recruited with simple randomization. Ethical approval, informed consent from the individuals and institutional permission were obtained. Data were collected with a questionnaire form and Visual Analogue Scale (VAS) for fatigue, Piper fatigue scale, Pittsburgh Sleep Quality Index (PSQI), and follow-up forms for the patient and the researcher. Aromatherapy inhalation (sweet orange and lavender oil) was performed before going to bed every day for one month to the intervention group patients. No other application has been made to the control group patients except for standard hemodialysis treatment. All of the forms were performed at baseline and at follow-up at the end of the four weeks (baseline and last follow-up), VAS and Piper fatigue scale were performed during follow-ups at the end of every week (the first, second and third follow-ups). Data were statistically analyzed with Independent Samples t-test, one way analysis of variance, Pearson correlation analysis, chi-square test, Friedman and Mann Whitney U tests and Bonferroni test. p<0.05 was set as statistically significant in comparisons. Mean total and sub-dimension scores of VAS, Piper fatigue scale and PSQI (except for daytime sleepiness dysfunction sub-dimension) of the intervention and control groups at baseline were not significantly different (p>0.05). It was found that mean total and sub-dimension scores of VAS, Piper fatigue scale and PSQI of the intervention group significantly decreased in other follow-ups compared to the control group (p<0.05). Consequently, it was determined that aromatherapy applied by inhalation improved sleep quality, decreased fatigue level and severity in hemodialysis patients. Accordingly, aromatherapy prepared with sweet orange and lavender oil may be recommended to increase sleep quality and to decrease fatigue level of the hemodialysis patients. Copyright © 2017 Elsevier Inc. All rights reserved.

Durability Assessment of Gamma Tial

NASA Technical Reports Server (NTRS)

Draper, Susan L.; Lerch, Bradley A.; Pereira, J. Michael; Miyoshi, Kazuhisa; Arya, Vinod K.; Zhuang, Wyman

2004-01-01

Gamma TiAl was evaluated as a candidate alloy for low-pressure turbine blades in aeroengines. The durability of g-TiAl was studied by examining the effects of impact or fretting on its fatigue strength. Cast-to-size Ti-48Al-2Cr-2Nb was studied in impact testing with different size projectiles at various impact energies as the reference alloy and subsequently fatigue tested. Impacting degraded the residual fatigue life. However, under the ballistic impact conditions studied, it was concluded that the impacts expected in an aeroengine would not result in catastrophic damage, nor would the damage be severe enough to result in a fatigue failure under the anticipated design loads. In addition, other gamma alloys were investigated including another cast-to-size alloy, several cast and machined specimens, and a forged alloy. Within this Ti-48-2-2 family of alloys aluminum content was also varied. The cracking patterns as a result of impacting were documented and correlated with impact variables. The cracking type and severity was reasonably predicted using finite element models. Mean stress affects were also studied on impact-damaged fatigue samples. The fatigue strength was accurately predicted based on the flaw size using a threshold-based, fracture mechanics approach. To study the effects of wear due to potential applications in a blade-disk dovetail arrangement, the machined Ti-47-2-2 alloy was fretted against In-718 using pin-on-disk experiments. Wear mechanisms were documented and compared to those of Ti-6Al-4V. A few fatigue samples were also fretted and subsequently fatigue tested. It was found that under the conditions studied, the fretting was not severe enough to affect the fatigue strength of g-TiAl.

Cyclic fatigue resistance of D-RaCe, ProTaper, and Mtwo nickel-titanium retreatment instruments after immersion in sodium hypochlorite.

PubMed

Topçuoğlu, Hüseyin Sinan; Pala, Kanşad; Aktı, Ahmet; Düzgün, Salih; Topçuoğlu, Gamze

2016-07-01

The aim of this study was to investigate the effect of immersion in sodium hypochlorite (NaOCl) on cyclic fatigue resistance of three different rotary nickel-titanium (NiTi) retreatment files. A total of 90 new ProTaper, D-RaCe, and Mtwo retreatment files were tested. Thirty files of the same brand were randomly assigned to two groups (n = 15). Group 1 was no immersion (control group) and 16 mm of group 2 instruments were immersed in 5 % NaOCl at 37 °C for 5 min. All instruments were then tested for cyclic fatigue. Resistance to cyclic fatigue was determined by counting the numbers of cycles to failure in a 60° curve with a 5-mm radius, recording the time in seconds to fracture. Data were analyzed by two-way analysis of variance. Resistance to cyclic fatigue decreased significantly for D-RaCe retreatment files after immersion in NaOCl. ProTaper and Mtwo retreatment files were not affected from immersion to NaOCl. D-RaCe retreatment instruments showed better cyclic fatigue resistance than ProTaper and Mtwo retreatment instruments, and the difference was statistically significant (p < 0.05). There was no significant difference between ProTaper and Mtwo retreatment instrument groups (p > 0.05). D-RaCe retreatment instruments had the highest cyclic fatigue resistance among retreatment files tested in this study, but immersion to NaOCl decreased the cyclic fatigue resistance of D-RaCe retreatment instrument. It should be considered that cyclic fatigue resistance of D-RaCe can decrease in contact with NaOCl during the removal of canal filling material.

Mind-body treatments for the pain-fatigue-sleep disturbance symptom cluster in persons with cancer.

PubMed

Kwekkeboom, Kristine L; Cherwin, Catherine H; Lee, Jun W; Wanta, Britt

2010-01-01

Co-occurring pain, fatigue, and sleep disturbance comprise a common symptom cluster in patients with cancer. Treatment approaches that target the cluster of symptoms rather than just a single symptom need to be identified and tested. To synthesize evidence regarding mind-body interventions that have shown efficacy in treating two or more symptoms in the pain-fatigue-sleep disturbance cancer symptom cluster. A literature search was conducted using CINAHL, Medline, and PsychInfo databases through March 2009. Studies were categorized based on the type of mind-body intervention (relaxation, imagery/hypnosis, cognitive-behavioral therapy/coping skills training [CBT/CST], meditation, music, and virtual reality), and a preliminary review was conducted with respect to efficacy for pain, fatigue, and sleep disturbance. Mind-body interventions were selected for review if there was evidence of efficacy for at least two of the three symptoms. Forty-three studies addressing five types of mind-body interventions met criteria and are summarized in this review. Imagery/hypnosis and CBT/CST interventions have produced improvement in all the three cancer-related symptoms individually: pain, fatigue, and sleep disturbance. Relaxation has resulted in improvements in pain and sleep disturbance. Meditation interventions have demonstrated beneficial effects on fatigue and sleep disturbance. Music interventions have demonstrated efficacy for pain and fatigue. No trials were found that tested the mind-body interventions specifically for the pain-fatigue-sleep disturbance symptom cluster. Efficacy studies are needed to test the impact of relaxation, imagery/hypnosis, CBT/CST, meditation, and music interventions in persons with cancer experiencing concurrent pain, fatigue, and sleep disturbance. These mind-body interventions could help patients manage all the symptoms in the cluster with a single treatment strategy. Copyright 2010 U.S. Cancer Pain Relief Committee. Published by Elsevier Inc. All rights reserved.

Corrosion fatigue of high strength fastener materials in seawater

NASA Technical Reports Server (NTRS)

Tipton, D. G.

1983-01-01

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Corrosion fatigue of high strength fastener materials in seawater

NASA Astrophysics Data System (ADS)

Tipton, D. G.

1983-12-01

Environmental effects which significantly reduce the fatigue life of metals are discussed. Corrosion fatigue is a major concern in the engineering application of high strength fasteners in marine environments. The corrosion fatigue failure of an AISI 41L4O high strength steel blade to hub attachment bolt at the MOD-OA 200 kW wind turbine generator was investigated. The reduction of fatigue strength of AISI 41L4O in marine environments and to obtain similar corrosion fatigue data for candidate replacement materials was studied. The AISI 4140, PH 13-8Mo stainless steel, alloy 718 and alloy MP-35N were tested in axial fatigue at a frequency of 20 Hz in dry air and natural seawater. The fatigue data are fitted by regression equations to allow determination of fatigue strength for a given number of cycles to failure.

Research on fatigue cracking growth parameters in asphaltic mixtures using computed tomography

NASA Astrophysics Data System (ADS)

Braz, D.; Lopes, R. T.; Motta, L. M. G.

2004-01-01

Distress of asphalt concrete pavement due to repeated bending from traffic loads has been a well-recognized problem in Brazil. If it is assumed that fatigue cracking growth is governed by the conditions at the crack tip, and that the crack tip conditions can be characterized by the stress intensity factor, then fatigue cracking growth as a function of stress intensity range Δ K can be determined. Computed tomography technique is used to detect crack evolution in asphaltic mixtures which were submitted to fatigue tests. Fatigue tests under conditions of controlled stress were carried out using diametral compression equipment and repeat loading. The aim of this work is imaging several specimens at different stages of the fatigue tests. In preliminary studies it was noted that the trajectory of a crack was influenced by the existence of voids in the originally unloaded specimens. Cracks would first be observed in the central region of a specimen, propagating in the direction of the extremities. Analyzing the graphics, that represent the fatigue cracking growth (d c/d N) as a function of stress intensity factor (Δ K), it is noticed that the curve has practically shown the same behavior for all specimens at the same level of the static tension rupture stress. The experimental values obtained for the constants A and n (of the Paris-Erdogan Law) present good agreement with the results obtained by Liang and Zhou.

Development of a fatigue testing setup for dielectric elastomer membrane actuators

NASA Astrophysics Data System (ADS)

Hill, M.; Rizzello, G.; Seelecke, S.

2017-04-01

Dielectric elastomers (DE's) represent a transduction technology with high potential in many fields, including industries, due to their low weight, flexibility, and small energy consumption. For industrial applications, it is of fundamental importance to quantify the lifetime of DE technology, in terms of electrical and mechanical fatigue, when operating in realistic environmental conditions. This work contributes toward this direction, by presenting the development of an experimental setup which permits systematic fatigue testing of DE membranes. The setup permits to apply both mechanical and electrical stimuli to several membranes simultaneously, while measuring at the same time their mechanical (force, deformation) and electrical response (capacitance, resistance). In its final state, the setup will allow to test up to 15 DE membranes at the same time for several thousands of cycles. Control of the modules, monitoring of the actuators, and data acquisition are realized on a cRio FPGA-system running with LabVIEW. The setup is located in a climate chamber, in order to investigate the fatigue mechanisms at different environmental conditions, i.e., in terms of temperature and humidity. The setup consists of two main parts, namely a fatigue group and a measurement group. The fatigue group stays permanently in the climate chamber, while the measurement group is assembled to the fatigue group and allows to perform measurements at 20°C.

The effects of autoclave sterilization on the cyclic fatigue resistance of ProTaper Universal, ProTaper Next, and ProTaper Gold nickel-titanium instruments.

PubMed

Özyürek, Taha; Yılmaz, Koray; Uslu, Gülşah

2017-11-01

It was aimed to compare the cyclic fatigue resistances of ProTaper Universal (PTU), ProTaper Next (PTN), and ProTaper Gold (PTG) and the effects of sterilization by autoclave on the cyclic fatigue life of nickel-titanium (NiTi) instruments. Eighty PTU, 80 PTN, and 80 PTG were included to the present study. Files were tested in a simulated canal. Each brand of the NiTi files were divided into 4 subgroups: group 1, as received condition; group 2, pre-sterilized instruments exposed to 10 times sterilization by autoclave; group 3, instruments tested were sterilized after being exposed to 25%, 50%, and 75% of the mean cycles to failure, then cycled fatigue test was performed; group 4, instruments exposed to the same experiment with group 3 without sterilization. The number of cycles to failure (NCF) was calculated. The data was statistically analyzed by using one-way analysis of variance and post hoc Tukey tests. PTG showed significantly higher NCF than PTU and PTN in group 1 ( p < 0.05). Sterilization significantly increased the NCF of PTN and PTG ( p < 0.05) in group 2. PTN in group 3 had significantly higher cyclic fatigue resistance than PTN group 4 ( p < 0.05). Also, significantly higher NCF was observed for PTG in group 2 than in groups 3 and 4 ( p < 0.05). PTG instrument made of new gold alloy was more resistant to fatigue failure than PTN and PTU. Autoclaving increased the cyclic fatigue resistances of PTN and PTG.

Statistical complex fatigue data for SAE 4340 steel and its use in design by reliability

NASA Technical Reports Server (NTRS)

Kececioglu, D.; Smith, J. L.

1970-01-01

A brief description of the complex fatigue machines used in the test program is presented. The data generated from these machines are given and discussed. Two methods of obtaining strength distributions from the data are also discussed. Then follows a discussion of the construction of statistical fatigue diagrams and their use in designing by reliability. Finally, some of the problems encountered in the test equipment and a corrective modification are presented.

Orbital fatigue tester for use in Skylab experiment T032

NASA Technical Reports Server (NTRS)

Sandorff, P. E.

1973-01-01

A prototype fatigue test machine is described which is suitable for use by an astronaut in conducting constant amplitude materials fatigue tests aboard a Skylab or space shuttle vehicle. The machine is comparised of a mechanical tester, which would be passed through a small (7.6-inch square) airlock to be supported in the space environment on an extendible boom, and a control console, which would provide remote control from within the space vehicle.

Thermal Fatigue Testing of ZrO2-Y2O3 Thermal Barrier Coating Systems using a High Power CO2 Laser

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Miller, Robert A.

1997-01-01

In the present study, the mechanisms of fatigue crack initiation and propagation, and of coating failure, under thermal loads that simulate diesel engine conditions, are investigated. The surface cracks initiate early and grow continuously under thermal Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF) stresses. It is found that, in the absence of interfacial oxidation, the failure associated with LCF is closely related to coating sintering and creep at high temperatures. Significant LCF and HCF interactions have been observed in the thermal fatigue tests. The fatigue crack growth rate in the ceramic coating strongly depends on the characteristic HCF cycle number, N*(sub NCF), which is defined as the number of HCF cycles per LCF cycle. The crack growth rate is increased from 0.36 microns/LCF cycle for a pure LCF test to 2.8 microns/LCF cycle for a combined LCF and HCF test at N*(sub NCF) about 20,000. A surface wedging model has been proposed to account for the HCF crack growth in the coating systems. This mechanism predicts that HCF damage effect increases with increasing surface temperature swing, the thermal expansion coefficient and the elastic modulus of the ceramic coating, as well as with the HCF interacting depth. A good agreement has been found between the analysis and experimental evidence.

Learning and cognitive fatigue trajectories in multiple sclerosis defined using a burst measurement design.

PubMed

Holtzer, Roee; Foley, Frederick; D'Orio, Vanessa; Spat, Jessica; Shuman, Melissa; Wang, Cuiling

2013-10-01

Compromised learning and cognitive fatigue are critical clinical features in multiple sclerosis. This study was designed to determine the effect of repeated exposures within and across study visits on performance measures of learning and cognitive fatigue in relapsing-remitting multiple sclerosis (RRMS). Thirty patients with RRMS and 30 controls were recruited. Using a burst measurement design (i.e. repeated assessments within and across study visits) the oral version of the Symbol Digit Modalities Test (SDMT) was administered three times during the baseline and two consecutive monthly follow-up visits for a total of nine test administrations. Learning was assessed within and across study visits whereas cognitive fatigue was assessed during the course of each test administration that was divided into three 30-second intervals. Linear mixed-effect models revealed compromised learning within (95% CI: 2.6355 to 3.9867) and across (95% CI: 1.3250 to 3.1861) visits and worse cognitive fatigue (95% CI: -2.1761 to -0.1720) in patients with RRMS compared with controls. Among patients with RRMS, worse self-rated cognitive dysfunction predicted poor learning within (95% CI: -0.1112 to -0.0020) and across (95% CI: -0.0724 to -0.0106) visits. Burst design is optimal to study learning and cognitive fatigue. This methodology, using the SDMT or other time-efficient tests as outcome measures, can be successfully implemented in longitudinal studies and clinical trials.

A Constitutive Relationship between Fatigue Limit and Microstructure in Nanostructured Bainitic Steels

PubMed Central

Mueller, Inga; Rementeria, Rosalia; Caballero, Francisca G.; Kuntz, Matthias; Sourmail, Thomas; Kerscher, Eberhard

2016-01-01

The recently developed nanobainitic steels show high strength as well as high ductility. Although this combination seems to be promising for fatigue design, fatigue properties of nanostructured bainitic steels are often surprisingly low. To improve the fatigue behavior, an understanding of the correlation between the nanobainitic microstructure and the fatigue limit is fundamental. Therefore, our hypothesis to predict the fatigue limit was that the main function of the microstructure is not necessarily totally avoiding the initiation of a fatigue crack, but the microstructure has to increase the ability to decelerate or to stop a growing fatigue crack. Thus, the key to understanding the fatigue behavior of nanostructured bainite is to understand the role of the microstructural features that could act as barriers for growing fatigue cracks. To prove this hypothesis, we carried out fatigue tests, crack growth experiments, and correlated these results to the size of microstructural features gained from microstructural analysis by light optical microscope and EBSD-measurements. Finally, we were able to identify microstructural features that influence the fatigue crack growth and the fatigue limit of nanostructured bainitic steels. PMID:28773953

The role of cognitive, emotional and personality factors in the experience of fatigue in a university and community sample.

PubMed

Kangas, Maria; Montgomery, Guy H

2011-05-01

The aim of this study was to investigate the contribution of cognitive, emotional and personality factors to the experience of fatigue severity in healthy adult individuals. Specifically, the study examined whether fatigue catastrophising and emotional distress mediated the relationships between neuroticism, general irrational and rational thoughts to fatigue severity. One hundred and eighty nine university students and community volunteers completed self-report questionnaires assessing fatigue catastrophising and symptom severity, neuroticism, general rational and irrational thoughts and emotional distress. A series of correlational and path analyses were conducted to test the study hypotheses. Neuroticism and more general negative, irrational cognitions were associated with elevated fatigue catastrophising and fatigue severity, whereas more adaptive, rational cognitions were related to lower fatigue catastrophising and fatigue severity. Both elevated fatigue catastrophising and emotional distress uniquely and simultaneously mediated the relationships between irrational and rational cognitions and neuroticism to fatigue severity. These findings demonstrate that cognitions play a role in fatigue severity. The results have implications in the assessment and treatment of fatigue disturbances in the general community.

Gear Performance Improved by Coating

NASA Technical Reports Server (NTRS)

Krantz, Timothy L.

2004-01-01

Gears, bearings, and other mechanical elements transmit loads through contacting surfaces. Even if properly designed, manufactured, installed, and maintained, gears and bearings will eventually fail because of the fatigue of the working surfaces. Economical means for extending the fatigue lives of gears and bearings are highly desired, and coatings offer the opportunity to engineer surfaces to extend the fatigue lives of mechanical components. A tungsten-containing diamondlike-carbon coating exhibiting high hardness, low friction, and good toughness was evaluated for application to spur gears. Fatigue testing was done at the NASA Glenn Research Center on both uncoated and coated spur gears. The results showed that the coating extended the surface fatigue lives of the gears by a factor of about 5 relative to the uncoated gears. For the experiments, a lot of spur test gears made from AISI 9310 gear steel were case-carburized and ground to aerospace specifications. The geometries of the 28-tooth, 8-pitch gears were verified as meeting American Gear Manufacturing Association (AGMA) quality class 12. One-half of the gears were randomly selected for coating. The method of coating was selected to achieve desired adherence, toughness, hardness, and low-friction characteristics. First the gears to be coated were prepared by blasting (vapor honing) with Al2O3 particles and cleaning. Then, the gears were provided with a thin adhesion layer of elemental chromium followed by magnetron sputtering of the outer coating consisting of carbon (70 at.%), hydrogen (15 at.%), tungsten (12 at.%), and nickel (3 at.%) (atomic percent at the surface). In total, the coating thickness was about 2.5 to 3 microns. As compared with the steel substrate, the coated surface was harder by a factor of about 2 and had a smaller elastic modulus. All gears were tested using a 5-centistoke synthetic oil, a 10,000-rpm rotation speed, and a hertzian contact stress of at least 1.7 GPa (250 ksi). Tests were run until either surface fatigue occurred or 300 million stress cycles were completed. Tests were run using either a pair of uncoated gears or a pair of coated gears (coated gears mated with uncoated gears were not evaluated). The fatigue test results, shown on Weibull coordinates in the graph, demonstrate that the coating provided substantially longer fatigue lives even though some of the coated gears endured larger stresses. The increase in fatigue life was a factor of about 5 and the statistical confidence for the improvement is high (greater than 99 percent). Examination of the tested gears revealed substantial reductions of total wear for coated gears in comparison to uncoated gears. The coated gear surface topography changed with running, with localized areas of the tooth surface becoming smoother with running. Theories explaining how coatings can extend gear fatigue lives are research topics for coating, tribology, and fatigue specialists. This work was done as a partnership between NASA, the U.S. Army Research Laboratory, United Technologies Research Corporation, and Sikorsky Aircraft.