Preliminary study of thermomechanical fatigue of polycrystalline MAR-M 200

NASA Technical Reports Server (NTRS)

Bill, R. C.; Verrilli, M. J.; Mcgaw, M. A.; Halford, G. R.

1984-01-01

Thermomechanical fatigue (TMF) experiments were conducted on polycrystalline MAR-M 200 over a cyclic temperature range of 500 to 1000 C. Inelastic strain ranges of 0.03 to 0.2 percent were imposed on the specimens. The TMF lives were found to be significantly shorter than isothermal low-cycle-fatigue (LCF) life at the maximum cycle temperature, and in-phase cycling was more damaging than out-of-phase cycling. Extensive crack tip oxidation appeared to play a role in promoting the severity of in-phase cycling. Carbide particle - matrix interface cracking was also observed after in-phase TMF cycling. The applicability of various life prediction models to the TMF results obtained was assessed. It was concluded that current life prediction models based on isothermal data as input must be modified to be applicable to the TMF results.

A Predictive Framework for Thermomechanical Fatigue Life of High Silicon Molybdenum Ductile Cast Iron Based on Considerations of Strain Energy Dissipation

NASA Astrophysics Data System (ADS)

Avery, Katherine R.

Isothermal low cycle fatigue (LCF) and anisothermal thermomechanical fatigue (TMF) tests were conducted on a high silicon molybdenum (HiSiMo) cast iron for temperatures up to 1073K. LCF and out-of-phase (OP) TMF lives were significantly reduced when the temperature was near 673K due to an embrittlement phenomenon which decreases the ductility of HiSiMo at this temperature. In this case, intergranular fracture was predominant, and magnesium was observed at the fracture surface. When the thermal cycle did not include 673K, the failure mode was predominantly transgranular, and magnesium was not present on the fracture surface. The in-phase (IP) TMF lives were unaffected when the thermal cycle included 673K, and the predominant failure mode was found to be transgranular fracture, regardless of the temperature. No magnesium was present on the IP TMF fracture surfaces. Thus, the embrittlement phenomenon was found to contribute to fatigue damage only when the temperature was near 673K and a tensile stress was present. To account for the temperature- and stress-dependence of the embrittlement phenomenon on the TMF life of HiSiMo cast iron, an original model based on the cyclic inelastic energy dissipation is proposed which accounts for temperature-dependent differences in the rate of fatigue damage accumulation in tension and compression. The proposed model has few empirical parameters. Despite the simplicity of the model, the predicted fatigue life shows good agreement with more than 130 uniaxial low cycle and thermomechanical fatigue tests, cyclic creep tests, and tests conducted at slow strain rates and with hold times. The proposed model was implemented in a multiaxial formulation and applied to the fatigue life prediction of an exhaust manifold subjected to severe thermal cycles. The simulation results show good agreement with the failure locations and number of cycles to failure observed in a component-level experiment.

Influence of coarsened and rafted microstructures on the thermomechanical fatigue of a Ni-base superalloy

DOE PAGES

Kirka, M. M.; Brindley, K. A.; Neu, R. W.; ...

2015-08-17

The aging of the microstructure of Ni-base superalloys during service is mainly characterized by coarsening and rafting of the γ' precipitates. The influence of these different aged microstructures on thermomechanical fatigue (TMF) under either continuously cycled (CC) and creep-fatigue (CF) was investigated. Three different aged microstructures, generated through accelerated aging and pre-creep treatments, were studied: stress-free coarsened γ', rafted with orientation perpendicular to loading direction (N-raft), and rafted with orientation parallel to loading direction (P-raft). Under most conditions, the aged microstructures were less resistant to TMF than the virgin microstructure; however, there were exceptions. Both stress-free coarsened and N-raft microstructuresmore » resulted in a reduction in TMF life under both CC and CF conditions in comparison to the virgin material. P-raft microstructure also resulted in reduction in TMF life under CC conditions; however, an increase in life over that of the virgin material was observed under CF conditions. Finally, these differences are discussed and hypothesized to be related to the interactions of the dislocations in the γ channels with γ' precipitates.« less

A Critical Assessment of Cyclic Softening and Hardening Behavior in a Near- α Titanium Alloy During Thermomechanical Fatigue

NASA Astrophysics Data System (ADS)

Prasad, Kartik; Sarkar, Rajdeep; Rao, K. Bhanu Sankara; Sundararaman, M.

2016-10-01

Thermomechanical fatigue behavior of Ti-alloy Timetal 834 has been studied at two temperature intervals viz. 573 K to 723 K (300 °C to 450 °C) and 723 K to 873 K (450 °C to 600 °C) under mechanical strain-controlled cycling. Among the temperatures studied, the alloy exhibited initial cyclic softening followed by cyclic hardening at 723 K (450 °C) in the temperature interval of 573 K to 723 K (300 °C to 450 °C). However, continuous cyclic hardening was observed at 723 K (450 °C) in 723 K to 873 K (450 °C to 600 °C). At 573 K (300 °C) and 873 K (600 °C), cyclic softening was observed in the cyclic stress response curves in both the temperature intervals. The dislocation substructure was observed to be planar in both the modes of TMF loading. Based on TEM microstructures and few unconventional fatigue tests, the observed cyclic hardening is attributed to dynamic strain aging. The reduced fatigue life at 723 K to 873 K (450 °C to 600 °C) under OP-TMF loading was attributed to the combined effect of cyclic hardening (leading to early strain localization and crack initiation), oxidation, and development of tensile mean stresses.

Thermal fatigue durability for advanced propulsion materials

NASA Technical Reports Server (NTRS)

Halford, Gary R.

1989-01-01

A review is presented of thermal and thermomechanical fatigue (TMF) crack initiation life prediction and cyclic constitutive modeling efforts sponsored recently by the NASA Lewis Research Center in support of advanced aeronautical propulsion research. A brief description is provided of the more significant material durability models that were created to describe TMF fatigue resistance of both isotropic and anisotropic superalloys, with and without oxidation resistant coatings. The two most significant crack initiation models are the cyclic damage accumulation model and the total strain version of strainrange partitioning. Unified viscoplastic cyclic constitutive models are also described. A troika of industry, university, and government research organizations contributed to the generation of these analytic models. Based upon current capabilities and established requirements, an attempt is made to project which TMF research activities most likely will impact future generation propulsion systems.

Stress analysis, thermomechanical fatique evaluation, and root subcomponent testing of gamma/gamma prime-delta eutectic alloy

NASA Technical Reports Server (NTRS)

Sheffler, K. D.; Jackson, J. J.

1976-01-01

Thermomechanical fatigue (TMF) and root subcomponent tensile, creep, and low cycle fatigue (LCF) tests were conducted to determine the capability of a fully lamellar directionally solidified eutectic alloy to sustain the airfoil thermal fatigue and root attachment loads anticipated in advanced, hollow, high work turbine blades. A three dimensional finite element elastic stress analysis was performed on typical advanced hollow eutectic airfoil and root-platform designs to determine appropriate conditions for these tests. Results of TMF tests conducted on longitudinal specimens (stress axis parallel to the solidification direction) containing a simulated leading edge cooling hole pattern indicated the longitudinal TMF properties to be more than adequate for the particular advanced hollow blade analyzed, with the strain range for a 10,000 cycle life being more than 50% above the maximum strain range calculated for the advanced hollow blade.

Life prediction methodology for thermal-mechanical fatigue and elevated temperature creep design

NASA Astrophysics Data System (ADS)

Annigeri, Ravindra

Nickel-based superalloys are used for hot section components of gas turbine engines. Life prediction techniques are necessary to assess service damage in superalloy components resulting from thermal-mechanical fatigue (TMF) and elevated temperature creep. A new TMF life model based on continuum damage mechanics has been developed and applied to IN 738 LC substrate material with and without coating. The model also characterizes TMF failure in bulk NiCoCrAlY overlay and NiAl aluminide coatings. The inputs to the TMF life model are mechanical strain range, hold time, peak cycle temperatures and maximum stress measured from the stabilized or mid-life hysteresis loops. A viscoplastic model is used to predict the stress-strain hysteresis loops. A flow rule used in the viscoplastic model characterizes the inelastic strain rate as a function of the applied stress and a set of three internal stress variables known as back stress, drag stress and limit stress. Test results show that the viscoplastic model can reasonably predict time-dependent stress-strain response of the coated material and stress relaxation during hold times. In addition to the TMF life prediction methodology, a model has been developed to characterize the uniaxial and multiaxial creep behavior. An effective stress defined as the applied stress minus the back stress is used to characterize the creep recovery and primary creep behavior. The back stress has terms representing strain hardening, dynamic recovery and thermal recovery. Whenever the back stress is greater than the applied stress, the model predicts a negative creep rate observed during multiple stress and multiple temperature cyclic tests. The model also predicted the rupture time and the remaining life that are important for life assessment. The model has been applied to IN 738 LC, Mar-M247, bulk NiCoCrAlY overlay coating and 316 austenitic stainless steel. The proposed model predicts creep response with a reasonable accuracy for wide range of loading cases such as uniaxial tension, tension-torsion and tension-internal pressure loading.

Thermo-Mechanical Fatigue Crack Growth of RR1000

PubMed Central

Pretty, Christopher John; Whitaker, Mark Thomas; Williams, Steve John

2017-01-01

Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechanisms. In the current work, a TMF crack growth testing method has been developed utilising induction heating and direct current potential drop techniques for polycrystalline nickel-based superalloys, such as RR1000. Results have shown that in-phase (IP) testing produces accelerated crack growth rates compared with out-of-phase (OOP) due to increased temperature at peak stress and therefore increased time dependent crack growth. The ordering of the crack growth rates is supported by detailed fractographic analysis which shows intergranular crack growth in IP test specimens, and transgranular crack growth in 90° OOP and 180° OOP tests. Isothermal tests have also been carried out for comparison of crack growth rates at the point of peak stress in the TMF cycles. PMID:28772394

In-phase thermomechanical fatigue mechanisms in an unidirectional SCS-6/Ti 15-3 MMC

NASA Technical Reports Server (NTRS)

Newaz, Golam M.; Majumdar, Bhaskar S.

1995-01-01

The objective of this investigation was to identify the inelastic deformation and damage mechanisms under in-phase (IP) thermomechanical fatigue (TMF) in a unidirectional SCS-6/Ti 15-3 metal matrix composite (MMC). Load-controlled IP TMF tests were conducted at 300-538 C at various stress ranges in high-purity argon. A major emphasis of this work was to identify damage mechanism well before final fracture of specimens, rather than to generate life diagrams, to aid development of a realistic deformation/damage and life model.

Some aspects of thermomechanical fatigue of AISI 304L stainless steel: Part I. creep- fatigue damage

NASA Astrophysics Data System (ADS)

Zauter, R.; Christ, H. J.; Mughrabi, H.

1994-02-01

Thermomechanical fatigue (TMF) tests on the austenitic stainless steel AISI 304L have been conducted under “true≓ plastic-strain control in vacuum. This report considers the damage oc-curring during TMF loading. It is shown how the temperature interval and the phasing (in-phase, out-of-phase) determine the mechanical response and the lifetime of the specimens. If creep-fatigue interaction takes place during in-phase cycling, the damage occurs inside the ma-terial, leading to intergranular cracks which reduce the lifetime considerably. Out-of-phase cy-cling inhibits creep-induced damage, and no lifetime reduction occurs, even if the material is exposed periodically to temperatures in the creep regime. A formula is proposed which allows prediction of the failure mode, depending on whether creep-fatigue damage occurs or not. At a given strain rate, the formula is able to estimate the temperature of transition between pure fatigue and creep-fatigue damage.

Characterization of Damage Progression in SCS-6/timetal 21S (0)4 Under Thermomechanical Fatigue Loadings

NASA Technical Reports Server (NTRS)

Castelli, Michael G.

1994-01-01

A detailed experimental investigation was performed at a single maximum cyclic stress (sigma max) level to physically characterize the progression of thermomechanical fatigue (lW) damage in continuously reinforced (0 deg) SCS-6/Timetal 21S, a titanium matrix composite. In-phase (IP) and out of-phase (OP) loadings were investigated at sigma max = 1000 MPa with a temperature cycle from 150 to 6500 C. Damage progression, in terms of macroscopic property degradation, was experimentally quantified through an advanced TMF test methodology which incorporates explicit measurements of the isothermal static moduli at the TMF temperature extremes and the coefficient of thermal expansion (CTE) as functions of the TMF cycles. Detailed characterization of the physical damage progression at the microstructural level was performed by interrupting multiple TMF tests at various stages of mechanical property degradation and analyzing the microstructure through extensive destructive metallography. Further, the extent of damage was also quantified through residual static strength measurements. Results indicated that damage initiation occurred very early in cyclic life (N less than 0.1Nf) for both the IP and OP TMF loadings. IP TMF damage was found to be dominated by fiber breakage with a physical damage progression in the microstructure which was difficult to quantify. OP TMF loadings produced matrix cracking exclusively associated with surface initiations. Here, damage progression was easily distinguished in terms of both the number of cracks and their relative inward progressions toward the outer fiber rows with increased cycling. The point at which the leading cracks reached the outer fiber rows (when localized fiber/matrix de-bonding and matrix crack bridging occurred) appeared to be reflected in the macroscopic property degradation curves.

Analysis of thermomechanical fatigue of unidirectional titanium metal matrix composites

NASA Technical Reports Server (NTRS)

Mirdamadi, M.; Johnson, W. S.; Bahei-El-din, Y. A.; Castelli, M. G.

1991-01-01

Thermomechanical fatigue (TMF) data was generated for a Ti-15V-3Cr-3Al-3Sn (Ti-15-3) material reinforced with SCS-6 silicon carbide fibers for both in-phase and out-of-phase thermomechanical cycling. Significant differences in failure mechanisms and fatigue life were noted for in-phase and out-of-phase testing. The purpose of the research is to apply a micromechanical model to the analysis of the data. The analysis predicts the stresses in the fiber and the matrix during the thermal and mechanical cycling by calculating both the thermal and mechanical stresses and their rate-dependent behavior. The rate-dependent behavior of the matrix was characterized and was used to calculate the constituent stresses in the composite. The predicted 0 degree fiber stress range was used to explain the composite failure. It was found that for a given condition, temperature, loading frequency, and time at temperature, the 0 degree fiber stress range may control the fatigue life of the unidirectional composite.

Thermal-Mechanical Fatigue Testing of a Titanium-Aluminide Alloy.

DTIC Science & Technology

1987-12-01

DIMSTRIBUTION STA Approved for pubi robing e% dQ *- AFIT/GAB/AA/87D-18 THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS John J...THERMAL-MECHANICAL FATIGUE TESTING OF A TITANIUM - ALUMINIDE ALLOY THESIS Presented to the Faculty of the School of Engineering of the Air Force Institute...develop a Thermal-Mechanical Fatigue (TMF) testing system for titanium - aluminide compact tension specimens. I could not have accomplished this without the

Proposed framework for thermomechanical life modeling of metal matrix composites

NASA Technical Reports Server (NTRS)

Halford, Gary R.; Lerch, Bradley A.; Saltsman, James F.

1993-01-01

The framework of a mechanics of materials model is proposed for thermomechanical fatigue (TMF) life prediction of unidirectional, continuous-fiber metal matrix composites (MMC's). Axially loaded MMC test samples are analyzed as structural components whose fatigue lives are governed by local stress-strain conditions resulting from combined interactions of the matrix, interfacial layer, and fiber constituents. The metallic matrix is identified as the vehicle for tracking fatigue crack initiation and propagation. The proposed framework has three major elements. First, TMF flow and failure characteristics of in situ matrix material are approximated from tests of unreinforced matrix material, and matrix TMF life prediction equations are numerically calibrated. The macrocrack initiation fatigue life of the matrix material is divided into microcrack initiation and microcrack propagation phases. Second, the influencing factors created by the presence of fibers and interfaces are analyzed, characterized, and documented in equation form. Some of the influences act on the microcrack initiation portion of the matrix fatigue life, others on the microcrack propagation life, while some affect both. Influencing factors include coefficient of thermal expansion mismatch strains, residual (mean) stresses, multiaxial stress states, off-axis fibers, internal stress concentrations, multiple initiation sites, nonuniform fiber spacing, fiber debonding, interfacial layers and cracking, fractured fibers, fiber deflections of crack fronts, fiber bridging of matrix cracks, and internal oxidation along internal interfaces. Equations exist for some, but not all, of the currently identified influencing factors. The third element is the inclusion of overriding influences such as maximum tensile strain limits of brittle fibers that could cause local fractures and ensuing catastrophic failure of surrounding matrix material. Some experimental data exist for assessing the plausibility of the proposed framework.

The failure models of Sn-based solder joints under coupling effects of electromigration and thermal cycling

NASA Astrophysics Data System (ADS)

Ma, Limin; Zuo, Yong; Liu, Sihan; Guo, Fu; Wang, Xitao

2013-01-01

Currently, the main concerns of Pb-free solder joints are focusing on electromigration (EM) and thermomechanical fatigue (TMF) problems. Many models have been established to understand the failure mechanisms of the joint under such single test conditions. Based on the fact that almost all microelectronic devices serve in combination conditions of fluctuated temperature and electric current stressing, the coupling effects of EM and TMF on evolution of microstructure and resistance of solder joint had been investigated. The failure models of binary SnBi alloy and ternary SnAgCu (SAC) solder under the coupling stressing were divided into four and three different stages, respectively. The failure mechanisms were dominant by the relationship of phase segregation, polarity effect, phase coarsening, and the coefficient of thermal expansion mismatch. Cracks tend to form and propagate along the interface between intermetallic compound layers and solder matrix in SAC solder. However, grain boundary was considered as the nucleation sites for microcracks in SnBi solder. High current density alleviates the deterioration of solder at the beginning stage of coupling stressing through Joule heating effect. An abrupt jump of resistance could be observed before the failure of the joint. The failure molds were determined by interactions of EM behaviors and TMF damages.

Creep fatigue life prediction for engine hot section materials (isotropic)

NASA Technical Reports Server (NTRS)

Nelson, R. S.; Levan, G. W.; Schoendorf, J. F.

1992-01-01

A series of high temperature strain controlled fatigue tests have been completed to study the effects of thermomechanical fatigue, multiaxial loading, reactive environments, and imposed mean stresses. The baseline alloy used in these tests was cast B1900+Hf (with and without coatings); a small number of tests of wrought INCO 718 are also included. A strong path dependence was demonstrated during the thermomechanical fatigue testing, using in-phase, out-phase, and non-proportional (elliptical and 'dogleg') strain-temperature cycles. The multiaxial tests also demonstrated cycle path to be a significant variable, using both proportional and non-proportional tension-torsion loading. Environmental screening tests were conducted in moderate pressure oxygen and purified argon; the oxygen reduced the specimen lives by two, while the argon testing produced ambiguous data. Both NiCoCrAlY overlay and diffusion aluminide coatings were evaluated under isothermal and TMF conditions; in general, the lives of the coated specimens were higher that those of uncoated specimens. Controlled mean stress TMF tests showed that small mean stress changes could change initiation lives by orders of magnitude; these results are not conservatively predicted using traditional linear damage summation rules. Microstructures were evaluated using optical, SEM and TEM methods.

Thermal-mechanical fatigue test apparatus for metal matrix composites and joint attachments

NASA Technical Reports Server (NTRS)

Westfall, L. J.; Petrasek, D. W.

1985-01-01

Two thermal-mechanical fatigue (TMF) test facilities were designed and developed, one to test tungsten fiber reinforced metal matrix composite specimens at temperature up to 1430C (2600F) and another to test composite/metal attachment bond joints at temperatures up to 760C (1400 F). The TMF facility designed for testing tungsten fiber reinforced metal matrix composites permits test specimen temperature excursions from room temperature to 1430C (2600F) with controlled heating and loading rates. A strain-measuring device measures the strain in the test section of the specimen during each heating and cooling cycle with superimposed loads. Data is collected and recorded by a computer. The second facility is designed to test composite/metal attachment bond joints and to permit heating to a maximum temperature of 760C (1400F) within 10 min and cooling to 150C (300F) within 3 min. A computer controls specimen temperature and load cycling.

Thermal-mechanical fatigue test apparatus for metal matrix composites and joint attachments

NASA Technical Reports Server (NTRS)

Westfall, Leonard J.; Petrasek, Donald W.

1988-01-01

Two thermal-mechanical fatigue (TMF) test facilities were designed and developed, one to test tungsten fiber reinforced metal matrix composite specimens at temperature up to 1430C (2600F) and another to test composite/metal attachment bond joints at temperatures up to 760F (1400F). The TMF facility designed for testing tungsten fiber reinforced metal matrix composites permits test specimen temperature excursions from room temperature to 1430C (2600F) with controlled heating and loading rates. A strain-measuring device measures the strain in the test section of the specimen during each heating and cooling cycle with superimposed loads. Data is collected and recorded by a computer. The second facility is designed to test composite/metal attachment bond joints and to permit heating to a maximum temperature of 760C (1400F) within 10 min and cooling to 150C (300F) within 3 min. A computer controls specimen temperature and load cycling.

TMF design considerations in turbine airfoils of advanced turbine engines

NASA Astrophysics Data System (ADS)

Date, C. G.; Zamrik, S. Y.; Adams, J. H.; Frani, N. E.

A review of thermal-mechanicalfatigue (TMF) in advanced turbine engines is presented. The review includes examples of typical thermal-mechnical loadings encountered in the design of hot section blades and vanes. Specific issues related to TMF behavior are presented and the associated impact on component life analysis and design is discussed.

Constitutive response of Rene 80 under thermal mechanical loads

NASA Technical Reports Server (NTRS)

Kim, K. S.; Cook, T. S.; Mcknight, R. L.

1988-01-01

The applicability of a classical constitutive model for stress-strain analysis of a nickel base superalloy, Rene' 80, in the gas turbine thermomechanical fatigue (TMF) environment is examined. A variety of tests were conducted to generate basic material data and to investigate the material response under cyclic thermomechanical loading. Isothermal stress-strain data were acquired at a variety of strain rates over the TMF temperature range. Creep curves were examined at 2 temperature ranges, 871 to 982 C and 760 to 871 C. The results provide optimism on the ability of the classical constitutive model for high temperature applications.

Multiaxial and Thermomechanical Fatigue of Materials: A Historical Perspective and Some Future Challenges

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh

2013-01-01

Structural materials used in engineering applications routinely subjected to repetitive mechanical loads in multiple directions under non-isothermal conditions. Over past few decades, several multiaxial fatigue life estimation models (stress- and strain-based) developed for isothermal conditions. Historically, numerous fatigue life prediction models also developed for thermomechanical fatigue (TMF) life prediction, predominantly for uniaxial mechanical loading conditions. Realistic structural components encounter multiaxial loads and non-isothermal loading conditions, which increase potential for interaction of damage modes. A need exists for mechanical testing and development verification of life prediction models under such conditions.

Influence of axial self-magnetic field component on arcing behavior of spiral-shaped contacts

DOE Office of Scientific and Technical Information (OSTI.GOV)

Feng, Dingyu; Xiu, Shixin, E-mail: xsx@mail.xjtu.edu.cn; Wang, Yi

2015-10-15

The transverse magnetic field (TMF) contact design is commonly used in vacuum interrupters. When arcing occurs between the TMF contacts, the contact structure can create a self-induced magnetic field that drives the arc to move and rotate on the contact, and thus local overheating and severe erosion can be avoided. However, TMF contacts could also create an axial self-magnetic component, and the influence of this component on the arc behavior has not been considered to date. In this paper, five different types of Cu-Cr spiral-shaped TMF contacts with three different structures are investigated in a demountable vacuum chamber that containsmore » a high-speed charge-coupled device video camera. It was found that the contact structure greatly influenced the arc behavior, especially in terms of arc rotation and the effective contact area, while contacts with the same slot structure but different diameters showed similar arc behavior and arc motion. The magnetic field distribution and the Lorentz force of each of the three different contact structures are simulated, and the axial self-magnetic field was first taken into consideration for investigation of the TMF contact design. It was found that contact designs that have higher axial self-magnetic field components tend to have arc columns with larger diameters and show poorer arc motion and rotation performance in the experiments.« less

Simulation of thermomechanical fatigue in solder joints

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fang, H.E.; Porter, V.L.; Fye, R.M.

1997-12-31

Thermomechanical fatigue (TMF) is a very complex phenomenon in electronic component systems and has been identified as one prominent degradation mechanism for surface mount solder joints in the stockpile. In order to precisely predict the TMF-related effects on the reliability of electronic components in weapons, a multi-level simulation methodology is being developed at Sandia National Laboratories. This methodology links simulation codes of continuum mechanics (JAS3D), microstructural mechanics (GLAD), and microstructural evolution (PARGRAIN) to treat the disparate length scales that exist between the macroscopic response of the component and the microstructural changes occurring in its constituent materials. JAS3D is used tomore » predict strain/temperature distributions in the component due to environmental variable fluctuations. GLAD identifies damage initiation and accumulation in detail based on the spatial information provided by JAS3D. PARGRAIN simulates the changes of material microstructure, such as the heterogeneous coarsening in Sn-Pb solder, when the component`s service environment varies.« less

Food web accumulation of cyclic siloxanes in Lake Mjøsa, Norway.

PubMed

Borgå, Katrine; Fjeld, Eirik; Kierkegaard, Amelie; McLachlan, Michael S

2012-06-05

The biomagnification of the cyclic volatile methyl siloxanes octamethylcyclotetrasiloxane (D4), decamethylcyclopentasiloxane (D5) and dodecamethylcyclohexatetrasiloxane (D6) was analyzed in the Lake Mjøsa food web in Norway from zooplankton and Mysis to planktivorous and piscivorous fish. The trophic magnification factor (TMF) for D5 was determined and compared with TMFs of several legacy contaminants: polychlorinated biphenyl (PCB) congeners 153 and 180, polybrominated diphenyl ether (PBDE) congeners 47 and 99, and p,p'-DDE. D5 showed TMF significantly greater than 1, implying food web biomagnification (TMF = 2.28, CI: 1.22-4.29). This contrasts with two studies that reported TMF < 1, which may reflect variability in TMF between food webs. The Lake Mjøsa D5 TMF was sensitive to the species included at the higher trophic level; whole food web TMF differed from TMF excluding smelt (Osmerus eperlanus) or brown trout (Salmo trutta) (TMF(-SMELT) = 1.62, CI: 0.96-2.72; TMF(-TROUT) = 3.58, CI: 1.82-7.03). For legacy contaminants (e.g., PCB-153 and PCB-180), the TMFs were less sensitive to the food web composition, and a better model fit was obtained compared to D5. The differences in biomagnification behavior between D5 and the legacy contaminants suggest that the biomagnification of D5 is being governed by species-specific properties such as biotransformation rate or tissue distribution that differ from those of legacy contaminants.

Creep-fatigue interaction at high temperature; Proceedings of the Symposium, 112th ASME Winter Annual Meeting, Atlanta, GA, Dec. 1-6, 1991

NASA Astrophysics Data System (ADS)

Haritos, George K.; Ochoa, O. O.

Various papers on creep-fatigue interaction at high temperature are presented. Individual topics addressed include: analysis of elevated temperature fatigue crack growth mechanisms in Alloy 718, physically based microcrack propagation laws for creep-fatigue-environment interaction, in situ SEM observation of short fatigue crack growth in Waspaloy at 700 C under cyclic and dwell conditions, evolution of creep-fatigue life prediction models, TMF design considerations in turbine airfoils of advanced turbine engines. Also discussed are: high temperature fatigue life prediction computer code based on the total strain version of strainrange partitioning, atomic theory of thermodynamics of internal variables, geometrically nonlinear analysis of interlaminar stresses in unsymmetrically laminated plates subjected to uniform thermal loading, experimental investigation of creep crack tip deformation using moire interferometry. (For individual items see A93-31336 to A93-31344)

Determination of Turbine Blade Life from Engine Field Data

NASA Technical Reports Server (NTRS)

Zaretsky, Erwin V.; Litt, Jonathan S.; Hendricks, Robert C.; Soditus, Sherry M.

2013-01-01

It is probable that no two engine companies determine the life of their engines or their components in the same way or apply the same experience and safety factors to their designs. Knowing the failure mode that is most likely to occur minimizes the amount of uncertainty and simplifies failure and life analysis. Available data regarding failure mode for aircraft engine blades, while favoring low-cycle, thermal-mechanical fatigue (TMF) as the controlling mode of failure, are not definitive. Sixteen high-pressure turbine (HPT) T-1 blade sets were removed from commercial aircraft engines that had been commercially flown by a single airline and inspected for damage. Each set contained 82 blades. The damage was cataloged into three categories related to their mode of failure: (1) TMF, (2) Oxidation/erosion (O/E), and (3) Other. From these field data, the turbine blade life was determined as well as the lives related to individual blade failure modes using Johnson-Weibull analysis. A simplified formula for calculating turbine blade life and reliability was formulated. The L10 blade life was calculated to be 2427 cycles (11 077 hr). The resulting blade life attributed to O/E equaled that attributed to TMF. The category that contributed most to blade failure was Other. If there were no blade failures attributed to O/E and TMF, the overall blade L(sub 10) life would increase approximately 11 to 17 percent.

Elevated temperature crack growth

NASA Technical Reports Server (NTRS)

Kim, K. S.; Vanstone, R. H.

1992-01-01

The purpose of this program was to extend the work performed in the base program (CR 182247) into the regime of time-dependent crack growth under isothermal and thermal mechanical fatigue (TMF) loading, where creep deformation also influences the crack growth behavior. The investigation was performed in a two-year, six-task, combined experimental and analytical program. The path-independent integrals for application to time-dependent crack growth were critically reviewed. The crack growth was simulated using a finite element method. The path-independent integrals were computed from the results of finite-element analyses. The ability of these integrals to correlate experimental crack growth data were evaluated under various loading and temperature conditions. The results indicate that some of these integrals are viable parameters for crack growth prediction at elevated temperatures.

Life prediction and constitutive models for engine hot section anisotropic materials program

NASA Technical Reports Server (NTRS)

Nissley, D. M.; Meyer, T. G.

1992-01-01

This report presents the results from a 35 month period of a program designed to develop generic constitutive and life prediction approaches and models for nickel-based single crystal gas turbine airfoils. The program is composed of a base program and an optional program. The base program addresses the high temperature coated single crystal regime above the airfoil root platform. The optional program investigates the low temperature uncoated single crystal regime below the airfoil root platform including the notched conditions of the airfoil attachment. Both base and option programs involve experimental and analytical efforts. Results from uniaxial constitutive and fatigue life experiments of coated and uncoated PWA 1480 single crystal material form the basis for the analytical modeling effort. Four single crystal primary orientations were used in the experiments: (001), (011), (111), and (213). Specific secondary orientations were also selected for the notched experiments in the optional program. Constitutive models for an overlay coating and PWA 1480 single crystal material were developed based on isothermal hysteresis loop data and verified using thermomechanical (TMF) hysteresis loop data. A fatigue life approach and life models were selected for TMF crack initiation of coated PWA 1480. An initial life model used to correlate smooth and notched fatigue data obtained in the option program shows promise. Computer software incorporating the overlay coating and PWA 1480 constitutive models was developed.

Experimental investigation on the initial expansion stage of vacuum arc on cup-shaped TMF contacts

NASA Astrophysics Data System (ADS)

Wang, Ting; Xiu, Shixin; Liu, Zixi; Zhang, Yanzhe; Feng, Dingyu

2018-02-01

Arc behavior and measures to control it directly affect the properties of vacuum circuit breakers. Nowadays, transverse magnetic field (TMF) contacts are widely used for medium voltages. A magnetic field perpendicular to the current direction between the TMF contacts makes the arc move, transmitting its energy to the whole contact and avoiding excessive local ablation. Previous research on TMF arc behavior concentrated mainly on the arc movement and less on the initial stage (from arc ignition to an unstable arc column). A significant amount of experiment results suggest that there is a short period of arc stagnation after ignition. The duration of this arc stagnation and the arc characteristics during this stage affect the subsequent arc motion and even the breaking property of interrupters. The present study is of the arc characteristics in the initial stage. Experiments were carried out in a demountable vacuum chamber with cup-shaped TMF contacts. Using a high-speed camera, both single-point arc ignition mode and multiple-point arc ignition (MPAI) mode were observed. The experimental data show that the probability of MPAI mode occurring is related to the arc current. The influences of arc-ignition mode, arc current, and contact diameter on the initial expansion process were investigated. In addition, simulations were performed to analyze the multiple arc expansion process mechanically. Based on the experimental phenomena and simulation results, the mechanism of the arc expansion motion was analyzed.

Life prediction and constitutive models for engine hot section anisotropic materials program

NASA Technical Reports Server (NTRS)

Nissley, D. M.; Meyer, T. G.; Walker, K. P.

1992-01-01

This report presents a summary of results from a 7 year program designed to develop generic constitutive and life prediction approaches and models for nickel-based single crystal gas turbine airfoils. The program was composed of a base program and an optional program. The base program addressed the high temperature coated single crystal regime above the airfoil root platform. The optional program investigated the low temperature uncoated single crystal regime below the airfoil root platform including the notched conditions of the airfoil attachment. Both base and option programs involved experimental and analytical efforts. Results from uniaxial constitutive and fatigue life experiments of coated and uncoated PWA 1480 single crystal material formed the basis for the analytical modeling effort. Four single crystal primary orientations were used in the experiments: group of zone axes (001), group of zone axes (011), group of zone axes (111), and group of zone axes (213). Specific secondary orientations were also selected for the notched experiments in the optional program. Constitutive models for an overlay coating and PWA 1480 single crystal materials were developed based on isothermal hysteresis loop data and verified using thermomechanical (TMF) hysteresis loop data. A fatigue life approach and life models were developed for TMF crack initiation of coated PWA 1480. A life model was developed for smooth and notched fatigue in the option program. Finally, computer software incorporating the overlay coating and PWA 1480 constitutive and life models was developed.

Thermal Mechanical Fatigue of Coated Blade Materials

DTIC Science & Technology

1989-06-01

temperature and strain greatly affect TMF life. The temperature-strain phase angle may vary from 180 degrees out of phase, for fast transients at...simplified constitutive technique. The life prediction model was specifically not designed to be a constitutive excercise , and therefore the observed test...the actual test. In one case (S/N 25) the actual tensile stresses were larger than the predicted values. This was caused by intermittent problems with

Stress Intensity Solutions of Thermally Induced Cracks in Combustor Liner Hot Spots Using Finite Element Analysis (FEA)

DTIC Science & Technology

2005-12-01

EPFM elastic-plastic fracture mechanics FCG fatigue crack growth FEA finite element analysis FKN ANSYS FEA command for contact pair stiffness FTOLN...current TMF research is too general for thermal gradient applications . Moreover, the nature of a cyclically heated, localized region of higher...when separating this problem into the general engineering issues that are germane to the application , one can find much published research that is

Thermomechanical Fatigue Durability of T650-35/PMR-15 Sheet-Molding Compound Evaluated

NASA Technical Reports Server (NTRS)

Castelli, Michael G.

1999-01-01

High-performance polymer matrix composites (PMC's) continue to be the focus of a number of research efforts aimed at developing cost-effective, lightweight material alternatives for advanced aerospace and aeropropulsion applications. These materials not only offer significant advantages in specific stiffness and strength over their current metal counterparts, but they can be designed and manufactured to eliminate joints and fasteners by combining individual components into integral subassemblies, thus making them extremely attractive for commercial applications. With much emphasis on the low-cost manufacturing aspects of advanced composite structures, there is heightened interest in high-performance sheet-molding compounds (SMC's). Researchers at the NASA Lewis Research Center, in cooperation with the Allison Advanced Development Company, completed an investigation examining the use of T650-35/PMR-15 SMC for a midstage inner-vane endwall application within a gas turbine engine compressor. This component resides in the engine flow path and is subjected not only to high airflow rates, but also to elevated temperatures and pressures. This application is unique in that it represents a very aggressive use of high-performance SMC's, raising obvious concerns related to durability and property retention in the presence of microstructural damage. Therefore, it was necessary to evaluate the fatigue behavior and damage tolerance of this material subjected to a representative thermomechanical fatigue (TMF) mission-cycle loading spectrum.

Materials research for High Speed Civil Transport and generic hypersonics: Adhesive durability

NASA Technical Reports Server (NTRS)

Allen, Mark R.

1995-01-01

This report covers a portion of an ongoing investigation of the durability of adhesives for the High Speed Civil Transport (HSCT) program. Candidate HSCT adhesives need to possess the high-temperature capability required for supersonic flight. This program was designed to initiate an understanding of the behavior of candidate HSCT materials when subjected to combined mechanical and thermal loads. Two adhesives (K3A and FM57) and two adherends (IM7/K3B polymeric composite and the titanium alloy Ti-6Al-4V) were used to fabricate thick adherend lap shear specimens. Due to processing problems, only the FM57/titanium bonds could be fabricated successfully. These are currently undergoing thermomechanical fatigue (TMF) testing. There is an acute need for an adhesive to secondarily bond polymeric composite adherends or, alternately, polymeric composites that remain stable at the processing temperatures of today's adhesives.

Intelligent Life-Extending Controls for Aircraft Engines Studied

NASA Technical Reports Server (NTRS)

Guo, Ten-Huei

2005-01-01

Current aircraft engine controllers are designed and operated to provide desired performance and stability margins. Except for the hard limits for extreme conditions, engine controllers do not usually take engine component life into consideration during the controller design and operation. The end result is that aircraft pilots regularly operate engines under unnecessarily harsh conditions to strive for optimum performance. The NASA Glenn Research Center and its industrial and academic partners have been working together toward an intelligent control concept that will include engine life as part of the controller design criteria. This research includes the study of the relationship between control action and engine component life as well as the design of an intelligent control algorithm to provide proper tradeoffs between performance and engine life. This approach is expected to maintain operating safety while minimizing overall operating costs. In this study, the thermomechanical fatigue (TMF) of a critical component was selected to demonstrate how an intelligent engine control algorithm can significantly extend engine life with only a very small sacrifice in performance. An intelligent engine control scheme based on modifying the high-pressure spool speed (NH) was proposed to reduce TMF damage from ground idle to takeoff. The NH acceleration schedule was optimized to minimize the TMF damage for a given rise-time constraint, which represents the performance requirement. The intelligent engine control scheme was used to simulate a commercial short-haul aircraft engine.

Modeling and life prediction methodology for Titanium Matrix Composites subjected to mission profiles

NASA Technical Reports Server (NTRS)

Mirdamadi, M.; Johnson, W. S.

1994-01-01

Titanium matrix composites (TMC) are being evaluated as structural materials for elevated temperature applications in future generation hypersonic vehicles. In such applications, TMC components are subjected to complex thermomechanical loading profiles at various elevated temperatures. Therefore, thermomechanical fatigue (TMF) testing, using a simulated mission profile, is essential for evaluation and development of life prediction methodologies. The objective of the research presented in this paper was to evaluate the TMF response of the (0/90)2s SCS-6/Timetal-21S subjected to a generic hypersonic flight profile and its portions with a temperature ranging from -130 C to 816 C. It was found that the composite modulus, prior to rapid degradation, had consistent values for all the profiles tested. A micromechanics based analysis was used to predict the stress-strain response of the laminate and of the constituents in each ply during thermomechanical loading conditions by using only constituent properties as input. The fiber was modeled as elastic with transverse orthotropic and temperature dependent properties. The matrix was modeled using a thermoviscoplastic constitutive relation. In the analysis, the composite modulus degradation was assumed to result from matrix cracking and was modeled by reducing the matrix modulus. Fatigue lives of the composite subjected to the complex generic hypersonic flight profile were well correlated using the predicted stress in 0 degree fibers.

Microstructural studies on failure mechanisms in thermo-mechanical fatigue of repaired DS R80 and IN 738 Superalloys

NASA Astrophysics Data System (ADS)

Abrokwah, Emmanuel Otchere

Directionally solidified Rene 80 (DS R80) and polycrystalline Inconel 738(IN 738) Superalloys were tested in thermo-mechanical fatigue (TMF) over the temperature range of 500-900°C and plastic strain range from 0.1 to 0.8% using a DSI Gleeble thermal simulator. Thermo-mechanical testing was carried out on the parent material (baseline) in the conventional solution treated and aged condition (STA), as well as gas tungsten arc welded (GTAW) with an IN-738 filler, followed by solution treatment and ageing. Comparison of the baseline alloy microstructure with that of the welded and heat treated alloy showed that varying crack initiation mechanisms, notably oxidation by stress assisted grain boundary oxidation, grain boundary MC carbides fatigue crack initiation, fatigue crack initiation from sample surfaces, crack initiation from weld defects and creep deformation were operating, leading to different “weakest link” and failure initiation points. The observations from this study show that the repaired samples had extra crack initiation sites not present in the baseline, which accounted for their occasional poor fatigue life. These defects include lack of fusion between the weld and the base metal, fusion zone cracking, and heat affected zone microfissures.

Vacuum arcing behavior between transverse magnetic field contacts subjected to variable axial magnetic field

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ma, Hui; Wang, Jianhua; Liu, Zhiyuan, E-mail: liuzy@mail.xjtu.edu.cn

2016-06-15

The objective of this work is to reveal the effects of an axial magnetic field (AMF) on the vacuum arc characteristics between transverse magnetic field (TMF) contacts. These vacuum arc characteristics include the vacuum arcing behavior and the arc voltage waveform. In the experiments, an external AMF was applied to a pair of TMF contacts. The external AMF flux density B{sub AMF} can be adjusted from 0 to 110 mT. The arc current in the tests varied over a range from 0 to 20 kA rms at 45 Hz. The contact material was CuCr25 (25% Cr). A high-speed charge-coupled device video camera wasmore » used to record the vacuum arc evolution. The experimental results show that the application of the AMF effectively reduces the TMF arc voltage noise component and reduces the formation of liquid metal drops between the contacts. The diffuse arc duration increases linearly with increasing AMF flux density, but it also decreases linearly with increasing arc current under application of the external AMF. The results also indicate that the diffuse arc duration before the current zero is usually more than 1 ms under the condition that the value of the AMF per kiloampere is more than 2.0 mT/kA. Finally, under application of the AMF, the arc column of the TMF contacts may constrict and remain in the center region without transverse rotation. Therefore, the combined TMF–AMF contacts should be designed such that they guarantee that the AMF is not so strong as to oppose transverse rotation of the arc column.« less

Vacuum arc behavior and its voltage characteristics in drawing process controlled by composite magnetic fields along axial and transverse directions

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Lijun, E-mail: lijunwang@mail.xjtu.edu.cn; Deng, Jie; Wang, Haijing

In this research, drawing vacuum arc (VA) experiments were conducted using composite contacts under currents ranging from 5 kA to 20 kA root mean square (rms). The new type of contact comprised an axial magnetic field (AMF) configuration and a transverse magnetic field (TMF) configuration. The TMF plate was in the center, surrounded by the AMF plate. The contact generated both AMFs and TMFs simultaneously. VA appearances and arc voltages were recorded, and the VA was modeled as a conductor for electromagnetic force analysis in ANSYS software. The results showed that the coaxiality of operating mechanisms significantly influenced arc behavior just asmore » the arc was ignited. When arc brightness did not increase after ignition, there was a voltage drop accompanied with diffusion of the VA. As to VA development, when an arc was ignited on an AMF plate, it spread on the plate and rotated. Over time the arc current increased, the constricting arc forms, and the arc column rotated on the TMF plate under the action of Ampere's force. With regard to the influence of a magnetic field on a VA at different stages, in the initial drawing arc stage the TMF was dominant, and the arc started to rotate under the action of Ampere's force. Afterwards, the AMF was dominant, with a steadily burning arc. As for contact melting, in the initial arcing period, a contracted short arc caused severe melting and erosion of the contact plate. When the ignition spot or root was close to the slot of plate, the electromagnetic force pushed the arc toward slot and contact edge, resulting in local erosion of the slot region.« less

Materials research for high-speed civil transport and generic hypersonics: Composites durability

NASA Technical Reports Server (NTRS)

Allen-Lilly, Heather; Cregger, Eric; Hoffman, Daniel; Mccool, Jim

1995-01-01

This report covers a portion of an ongoing investigation of the durability of composites for the High Speed Civil Transport (HSCT) program. Candidate HSCT composites need to possess the high-temperature capability required for supersonic flight. This program was designed to initiate the design, analysis, fabrication, and testing of equipment intended for use in validating the long-term durability of materials for the HSCT. This equipment includes thermally actuated compression and tension fixtures, hydraulic-actuated reversible load fixtures, and thermal chambers. This equipment can be used for the durability evaluation of both composite and adhesive materials. Thermally actuated fixtures are recommended for fatigue cycling when long-term thermomechanical fatigue (TMF) data are required on coupon-sized tension or compression specimens. Long term durability testing plans for polymer matrix composite specimens are included.

SU-G-JeP2-05: Dose Effects of a 1.5T Magnetic Field On Air-Tissue and Lung-Tissue Interfaces in MRI-Guided Radiotherapy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xinfeng; Prior, Phillip; Chen, Guangpei

Purpose: The purpose of the study is to investigate the dose effects of electron-return-effect (ERE) at air-tissue and lung-tissue interfaces under a 1.5T transverse-magnetic-field (TMF). Methods: IMRT and VMAT plans for representative pancreas, lung, breast and head & neck (H&N) cases were generated following clinical dose volume (DV) criteria. The air-cavity walls, as well as the lung wall, were delineated to examine the ERE. In each case, the original plan generated without TMF is compared with the reconstructed plan (generated by recalculating the original plan with the presence of TMF) and the optimized plan (generated by a full optimization withmore » TMF), using a variety of DV parameters, including V100%, D95% and dose heterogeneity index for PTV, Dmax, and D1cc for OARs (organs at risk) and tissue interface. Results: The dose recalculation under TMF showed the presence of the 1.5 T TMF can slightly reduce V100% and D95% for PTV, with the differences being less than 4% for all but lung case studied. The TMF results in considerable increases in Dmax and D1cc on the skin in all cases, mostly between 10-35%. The changes in Dmax and D1cc on air cavity walls are dependent upon site, geometry, and size, with changes ranging up to 15%. In general, the VMAT plans lead to much smaller dose effects from ERE compared to fixed-beam IMRT. When the TMF is considered in the plan optimization, the dose effects of the TMF at tissue interfaces are significantly reduced in most cases. Conclusion: The doses on tissue interfaces can be significantly changed by the presence of a 1.5T TMF during MR-guided RT when the TMF is not included in plan optimization. These changes can be substantially reduced or even removed during VMAT/IMRT optimization that specifically considers the TMF, without deteriorating overall plan quality.« less

Constitutive modeling for isotropic materials (HOST)

NASA Technical Reports Server (NTRS)

Lindholm, U. S.; Chan, K. S.; Bodner, S. R.; Weber, R. M.; Walker, K. P.; Cassenti, B. N.

1985-01-01

This report presents the results of the second year of work on a problem which is part of the NASA HOST Program. Its goals are: (1) to develop and validate unified constitutive models for isotropic materials, and (2) to demonstrate their usefulness for structural analyses of hot section components of gas turbine engines. The unified models selected for development and evaluation are that of Bodner-Partom and Walker. For model evaluation purposes, a large constitutive data base is generated for a B1900 + Hf alloy by performing uniaxial tensile, creep, cyclic, stress relation, and thermomechanical fatigue (TMF) tests as well as biaxial (tension/torsion) tests under proportional and nonproportional loading over a wide range of strain rates and temperatures. Systematic approaches for evaluating material constants from a small subset of the data base are developed. Correlations of the uniaxial and biaxial tests data with the theories of Bodner-Partom and Walker are performed to establish the accuracy, range of applicability, and integability of the models. Both models are implemented in the MARC finite element computer code and used for TMF analyses. Benchmark notch round experiments are conducted and the results compared with finite-element analyses using the MARC code and the Walker model.

Functional involvement of TMF/ARA160 in Rab6-dependent retrograde membrane traffic.

PubMed

Yamane, Junko; Kubo, Akiharu; Nakayama, Kazuhisa; Yuba-Kubo, Akiko; Katsuno, Tatsuya; Tsukita, Shoichiro; Tsukita, Sachiko

2007-10-01

The small GTPase Rab6 regulates retrograde membrane traffic from endosomes to the Golgi apparatus and from the Golgi to the endoplasmic reticulum (ER). We examined the role of a Rab6-binding protein, TMF/ARA160 (TATA element modulatory factor/androgen receptor-coactivator of 160 kDa), in this process. High-resolution immunofluorescence imaging revealed that TMF signal surrounded Rab6-positive Golgi structures and immunoelectron microscopy revealed that TMF is concentrated at the budding structures localized at the tips of cisternae. The knockdown of either TMF or Rab6 by RNA interference blocked retrograde transport of endocytosed Shiga toxin from early/recycling endosomes to the trans-Golgi network, causing missorting of the toxin to late endosomes/lysosomes. However, the TMF knockdown caused Rab6-dependent displacement of N-acetylgalactosaminyltransferase-2 (GalNAc-T2), but not beta1,4-galactosyltransferase (GalT), from the Golgi. Analyses using chimeric proteins, in which the cytoplasmic regions of GalNAc-T2 and GalT were exchanged, revealed that the cytoplasmic region of GalNAc-T2 plays a crucial role in its TMF-dependent Golgi retention. These observations suggest critical roles for TMF in two Rab6-dependent retrograde transport processes: one from endosomes to the Golgi and the other from the Golgi to the ER.

Technical, Managerial and Financial (TMF) Capacity Resources for Small Drinking Water Systems

EPA Pesticide Factsheets

Resources are available to help public water systems build the technical, managerial and financial (TMF) capacity. TMF capacity is necessary to achieve and maintain long-term sustainability and compliance with national safe drinking water regulations.

The Effect of the Traveling Magnetic Field (TMF) on the Buoyancy-Induced Convection in the Vertical Bridgman growth of Germanium

NASA Technical Reports Server (NTRS)

Yesilyurt, S.; Motakef, S.; Grugel, R.; Mazuruk, K.

2003-01-01

A traveling magnetic field (TMF) is created by means of applying out-of-phase currents to a number of coils. When applied to a conducting melt inside a cylindrical container, the TMF induces a Lorentz force that acts in the meridional directions (radial and axial), unlike the application of a rotating magnetic field (RMF), which creates a force in the azimuthal direction. In this work, we present a computational study of the TMF and its application to the Bridgman growth of the Ge. To quantify the effect of the TMF on the solid-melt interface, we use the maximum (magnitude-wise) tangential shear at the interface.

Prognostic indicators for dogs with dilated cardiomyopathy.

PubMed

Borgarelli, Michele; Santilli, Roberto A; Chiavegato, David; D'Agnolo, Gino; Zanatta, Renato; Mannelli, Alessandro; Tarducci, Alberto

2006-01-01

The purpose of this study was to investigate the prognostic value of various clinical, ECG, echocardiographic, and Doppler echocardiographic variables in dogs with dilated cardiomyopathy. The relationship to survival of 11 variables was evaluated in 63 dogs. Studied variables were age at time of diagnosis, class of heart failure (HF), dyspnea, ascites, atrial fibrillation (AF), ejection fraction (EF), E-point septal separation, end-diastolic volume index, end-systolic volume index (ESV-I), and restrictive or nonrestrictive transmitral flow (TMF) pattern. Median survival time was 671 days (lower 95% confidence limit, 350 days). Survival curves showed that severity of HF, ascites, ESV-I greater than 140 mL/m2, EF less than 25%, and restrictive TMF pattern had a significant negative relation to survival time. Thirty-nine dogs with both sinus rhythm and AF presented adequate TMF recordings; in these dogs, after stratification by TMF pattern, the restrictive TMF pattern was the most important negative prognostic indicator. We conclude that in dogs with dilated cardiomyopathy the restrictive TMF pattern appears to represent a useful prognostic indicator. Class of HF, ascites, ESV-I, and EF are also useful indexes if an adequate TMF pattern is not recorded.

Thermomechanical testing of high-temperature composites - Thermomechanical fatigue (TMF) behavior of SiC(SCS-6)/Ti-15-3

NASA Technical Reports Server (NTRS)

Castelli, Michael G.; Bartolotta, Paul; Ellis, John R.

1992-01-01

Thermomechanical testing techniques recently developed for monolithic structural alloys were successfully extended to continuous fiber reinforced composite materials in plate form. The success of this adaptation was verified on a model metal matrix composite (MMC) material, namely SiC(SCS-6)/Ti-15V-3Cr-3Al-3Sn. Effects of heating system type and specimen preparation are also addressed. Cyclic lives determined under full thermomechanical conditions were shown to be significantly reduced from those obtained under comparable isothermal and in-phase bi-thermal conditions. Fractography and metallography from specimens subjected to isothermal, out-of-phase and in-phase conditions reveal distinct differences in damage-failure modes. Isothermal metallography revealed extensive matrix cracking associated with fiber damage throughout the entire cross-section of the specimen. Out-of-phase metallography revealed extensive matrix damage associated with minimal (if any) fiber cracking. However, the damage was located exclusively at surface and near-surface locations. In-phase conditions produced extensive fiber cracking throughout the entire cross-section, associated with minimal (if any) matrix damage.

Quality expectations and tolerance limits of trial master files (TMF) – Developing a risk-based approach for quality assessments of TMFs

PubMed Central

Hecht, Arthur; Busch-Heidger, Barbara; Gertzen, Heiner; Pfister, Heike; Ruhfus, Birgit; Sanden, Per-Holger; Schmidt, Gabriele B.

2015-01-01

This article addresses the question of when a trial master file (TMF) can be considered sufficiently accurate and complete: What attributes does the TMF need to have so that a clinical trial can be adequately reconstructed from documented data and procedures? Clinical trial sponsors face significant challenges in assembling the TMF, especially when dealing with large, international, multicenter studies; despite all newly introduced archiving techniques it is becoming more and more difficult to ensure that the TMF is complete. This is directly reflected in the number of inspection findings reported and published by the EMA in 2014. Based on quality risk management principles in clinical trials the authors defined the quality expectations for the different document types in a TMF and furthermore defined tolerance limits for missing documents. This publication provides guidance on what type of documents and processes are most important, and in consequence, indicates on which documents and processes trial team staff should focus in order to achieve a high-quality TMF. The members of this working group belong to the CQAG Group (Clinical Quality Assurance Germany) and are QA (quality assurance) experts (auditors or compliance functions) with long-term experience in the practical handling of TMFs. PMID:26693218

Quality expectations and tolerance limits of trial master files (TMF) - Developing a risk-based approach for quality assessments of TMFs.

PubMed

Hecht, Arthur; Busch-Heidger, Barbara; Gertzen, Heiner; Pfister, Heike; Ruhfus, Birgit; Sanden, Per-Holger; Schmidt, Gabriele B

2015-01-01

This article addresses the question of when a trial master file (TMF) can be considered sufficiently accurate and complete: What attributes does the TMF need to have so that a clinical trial can be adequately reconstructed from documented data and procedures? Clinical trial sponsors face significant challenges in assembling the TMF, especially when dealing with large, international, multicenter studies; despite all newly introduced archiving techniques it is becoming more and more difficult to ensure that the TMF is complete. This is directly reflected in the number of inspection findings reported and published by the EMA in 2014. Based on quality risk management principles in clinical trials the authors defined the quality expectations for the different document types in a TMF and furthermore defined tolerance limits for missing documents. This publication provides guidance on what type of documents and processes are most important, and in consequence, indicates on which documents and processes trial team staff should focus in order to achieve a high-quality TMF. The members of this working group belong to the CQAG Group (Clinical Quality Assurance Germany) and are QA (quality assurance) experts (auditors or compliance functions) with long-term experience in the practical handling of TMFs.

Sensor Based Engine Life Calculation: A Probabilistic Perspective

NASA Technical Reports Server (NTRS)

Guo, Ten-Huei; Chen, Philip

2003-01-01

It is generally known that an engine component will accumulate damage (life usage) during its lifetime of use in a harsh operating environment. The commonly used cycle count for engine component usage monitoring has an inherent range of uncertainty which can be overly costly or potentially less safe from an operational standpoint. With the advance of computer technology, engine operation modeling, and the understanding of damage accumulation physics, it is possible (and desirable) to use the available sensor information to make a more accurate assessment of engine component usage. This paper describes a probabilistic approach to quantify the effects of engine operating parameter uncertainties on the thermomechanical fatigue (TMF) life of a selected engine part. A closed-loop engine simulation with a TMF life model is used to calculate the life consumption of different mission cycles. A Monte Carlo simulation approach is used to generate the statistical life usage profile for different operating assumptions. The probabilities of failure of different operating conditions are compared to illustrate the importance of the engine component life calculation using sensor information. The results of this study clearly show that a sensor-based life cycle calculation can greatly reduce the risk of component failure as well as extend on-wing component life by avoiding unnecessary maintenance actions.

Tangeretin derivative, 5-acetyloxy-6,7,8,4'-tetramethoxyflavone induces G2/M arrest, apoptosis and autophagy in human non-small cell lung cancer cells in vitro and in vivo.

PubMed

Li, Yi Rong; Li, Shiming; Ho, Chi-Tang; Chang, Ya-Han; Tan, Kok-Tong; Chung, Ting-Wen; Wang, Bing-Yen; Chen, Yu-Kuo; Lin, Chi-Chen

2016-01-01

Tangeretin, a major phytochemicals in tangerine peels--an important Chinese herb, has been found to have anti-carcinogenic properties. To improve bioavailability and increase potency of tangeretin, its derivative, 5-acetyloxy-6,7,8,4'-tetramethoxyflavone (5-AcTMF), has been synthesized and shown potent inhibition of proliferation activity against human breast and leukemia cancer cell lines. In this study, we have further investigated the anticancer effects of 5-AcTMF on CL1-5 non-small cell lung cancer cells (NSCLC) both in vitro and in vivo and demonstrated that 5-AcTMF effectively inhibited cancer cell proliferation, induced G2/M-phase arrest associated with cdc2 and CDC25c and increased in the apoptotic cells associated with caspase activation, down regulation of Bcl-2, XIAP and Survivn, inducing release of cytochrome c into the cytosol and disruption of mitochondrial membrane potential. We also found that 5-AcTMF treatment of CL1-5 activated autophagy, indicated by triggered autophagosome formation and increased LC3-II levels and formation of LC3 puncta. Moreover, we also found that 5-AcTMF lowered phophoatidylinositol 3-kinase/AKT/mTOR signaling pathway. Over-expression of AKT by AKT cDNA transfection decreased 5-AcTMF mediated apoptosis and autophagy, supporting the induction of apoptosis and autophagy by inhibition of AKT pathway. In an animal study, 5-AcTMF effectively delayed tumor growth in a nude mouse model of CL1-5 xenografts without observed adverse effect. Immunohistochemistry Analysis indicated that 5-AcTMF induced CL1-5 cell apoptosis and autophagy in vivo. Taken together, these data demonstrate that 5-AcTMF is a novel small molecule agent that can inhibit NSCLC cell proliferation, and induce G(2)/M phase arrest and via the mitochondrial apoptotic pathway and autophagy.

Investigation of damage mechanisms in a cross-ply metal-matrix composite under thermomechanical loading. Master's thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schubbe, J.J.

1990-12-01

Metal matrix composites (MMCs) are rapidly becoming strong candidates for high temperature and high stiffness structural applications such as the Advanced Tactical Fighter (ATF). This study systematically investigated the failure modes and associated damage in a cross-ply, (0/90)2s SCS6/Ti-15-3 metal matrix composite under in-phase and out-of-phase thermomechanic fatigue. Initiation and progression of fatigue damage were recorded and correlated to changes in Young's Modulus of the composite material. Experimental results show an internal stabilization of reaction zone size but degradation and separation from constituent materials under extended cyclic thermal loading. Critical to damage were transverse cracks initiating in the 90 degreesmore » plies, growing and coalescing from fiber/matrix interfaces internal to the specimen, progressing outward through the 0 degree plies before failure. Maximum mechanical strain at failure was determined to be approximately 0.0075 mm/mm. A correlation was made relating maximum matrix stress to failure life, resulting in a fatigue threshold limit of 280 MPa. An attempt was made to correlate the degradation in Young's Modulus (Damage=1-E/Eo) with the applied life cycles from different TMF tests.« less

Creep fatigue life prediction for engine hot section materials (isotropic)

NASA Technical Reports Server (NTRS)

Nelson, R. S.; Levan, G. W.; Harvey, P. R.

1992-01-01

This Final Report covers the activities completed under the optional program of the NASA HOST Contract, NAS3-23288. The initial effort of the optional program was report-in NASA CR189221, which consisted of high temperature strain controlled fatigue tests to study the effects of thermomechanical fatigue, multiaxial loading, reactive environments, and imposed stresses. The baseline alloy used in the tests included B1900+Hf (with or without coating) and wrought INCO 718. Tests conducted on B1900+Hf included environmental tests using various atmospheres (75 psig oxygen, purified argon, or block exposures) and specimen tests of wrought INCO 718 included tensile, creep, stress rupture, TMF, multiaxial, and mean stress tests. Results of these testings were used to calibrate a CDA model for INCO 718 alloy and to develop modifications or corrections to the CDA model to handle additional failure mechanisms. The Socie parameter was found to provide the best correlation for INCO multiaxial loading. Microstructural evaluations consisting of optical, Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM) techniques, and surface replication techniques to determine crack initiation lives provided data which were used to develop life prediction models.

Mitigating reentry radio blackout by using a traveling magnetic field

NASA Astrophysics Data System (ADS)

Zhou, Hui; Li, Xiaoping; Xie, Kai; Liu, Yanming; Yu, Yuanyuan

2017-10-01

A hypersonic flight or a reentry vehicle is surrounded by a plasma layer that prevents electromagnetic wave transmission, which results in radio blackout. The magnetic-window method is considered a promising means to mitigate reentry communication blackout. However, the real application of this method is limited because of the need for strong magnetic fields. To reduce the required magnetic field strength, a novel method that applies a traveling magnetic field (TMF) is proposed in this study. A mathematical model based on magneto-hydrodynamic theory is adopted to analyze the effect of TMF on plasma. The mitigating effects of the TMF on the blackout of typical frequency bands, including L-, S-, and C-bands, are demonstrated. Results indicate that a significant reduction of plasma density occurs in the magnetic-window region by applying a TMF, and the reduction ratio is positively correlated with the velocity of the TMF. The required traveling velocities for eliminating the blackout of the Global Positioning System (GPS) and the typical telemetry system are also discussed. Compared with the constant magnetic-window method, the TMF method needs lower magnetic field strength and is easier to realize in the engineering field.

Technical Note: Dose effects of 1.5 T transverse magnetic field on tissue interfaces in MRI-guided radiotherapy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xinfeng; Prior, Phil; Chen, Guang-Pei

Purpose: The integration of MRI with a linear accelerator (MR-linac) offers great potential for high-precision delivery of radiation therapy (RT). However, the electron deflection resulting from the presence of a transverse magnetic field (TMF) can affect the dose distribution, particularly the electron return effect (ERE) at tissue interfaces. The purpose of the study is to investigate the dose effects of ERE at air-tissue and lung-tissue interfaces during intensity-modulated radiation therapy (IMRT) planning. Methods: IMRT and volumetric modulated arc therapy (VMAT) plans for representative pancreas, lung, breast, and head and neck (HN) cases were generated following commonly used clinical dose volumemore » (DV) criteria. In each case, three types of plans were generated: (1) the original plan generated without a TMF; (2) the reconstructed plan generated by recalculating the original plan with the presence of a TMF of 1.5 T (no optimization); and (3) the optimized plan generated by a full optimization with TMF = 1.5 T. These plans were compared using a variety of DV parameters, including V{sub 100%}, D{sub 95%}, DHI [dose heterogeneity index: (D{sub 20%}–D{sub 80%})/D{sub prescription}], D{sub max}, and D{sub 1cc} in OARs (organs at risk) and tissue interface. All the optimizations and calculations in this work were performed on static data. Results: The dose recalculation under TMF showed the presence of the 1.5 T TMF can slightly reduce V{sub 100%} and D{sub 95%} for PTV, with the differences being less than 4% for all but one lung case studied. The TMF results in considerable increases in D{sub max} and D{sub 1cc} on the skin in all cases, mostly between 10% and 35%. The changes in D{sub max} and D{sub 1cc} on air cavity walls are dependent upon site, geometry, and size, with changes ranging up to 15%. The VMAT plans lead to much smaller dose effects from ERE compared to fixed-beam IMRT in pancreas case. When the TMF is considered in the plan optimization, the dose effects of the TMF at tissue interfaces (e.g., air-cavity wall, lung-tissue interfaces, skin) are significantly reduced in most cases. Conclusions: The doses on tissue interfaces can be significantly changed by the presence of a TMF during MR-guided RT when the magnetic field is not included in plan optimization. These changes can be substantially reduced or even eliminated during VMAT/IMRT optimization that specifically considers the TMF, without deteriorating overall plan quality.« less

Understanding the Reliability of Solder Joints Used in Advanced Structural and Electronics Applications: Part 2 - Reliability Performance.

DOE PAGES

Vianco, Paul T.

2017-03-01

Whether structural or electronic, all solder joints must provide the necessary level of reliability for the application. The Part 1 report examined the effects of filler metal properties and the soldering process on joint reliability. Filler metal solderability and mechanical properties, as well as the extents of base material dissolution and interface reaction that occur during the soldering process, were shown to affect reliability performance. The continuation of this discussion is presented in this Part 2 report, which highlights those factors that directly affect solder joint reliability. There is the growth of an intermetallic compound (IMC) reaction layer at themore » solder/base material interface by means of solid-state diffusion processes. In terms of mechanical response by the solder joint, fatigue remains as the foremost concern for long-term performance. Thermal mechanical fatigue (TMF), a form of low-cycle fatigue (LCF), occurs when temperature cycling is combined with mismatched values of the coefficient of thermal expansion (CTE) between materials comprising the solder joint “system.” Vibration environments give rise to high-cycle fatigue (HCF) degradation. Although accelerated aging studies provide valuable empirical data, too many variants of filler metals, base materials, joint geometries, and service environments are forcing design engineers to embrace computational modeling to predict the long-term reliability of solder joints.« less

A technique to control cross-field diffusion of plasma across a transverse magnetic field

NASA Astrophysics Data System (ADS)

Hazarika, P.; Chakraborty, M.; Das, B. K.; Bandyopadhyay, M.

2016-12-01

A study to control charged particle transport across a transverse magnetic field (TMF), popularly known as the magnetic filter in a negative ion source, has been carried out in a double plasma device. In the experimental setup, the TMF placed between the two magnetic cages divides the whole plasma chamber into two distinct regions, viz., the source and the target on the basis of the plasma production and the corresponding electron temperature. The plasma produced in the source region by the filament discharge method diffuses into the target region through the TMF. Data are acquired by the Langmuir probe and are compared in different source configurations, in terms of external biasing applied to metallic plates inserted in the TMF plane but in the orthogonal direction. The effect of the direction of current between the two plates in either polarity of bias in the presence of TMF on the plasma parameters and the cross-field transport of charge particles are discussed.

SU-F-BRB-14: Dosimetric Effects at Air- Tissue Boundary Due to Magnetic Field in MR-Guided IMRT/VMAT Delivery for Head and Neck Cancer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Prior, P; Chen, X; Schultz, C

Purpose: The advent of the MR-Linac enables real-time and high soft tissue contrast image guidance in radiation therapy (RT) delivery. Potential hot-spots at air-tissue interfaces, such as the sphenoid sinus, in RT for head and neck cancer (HNC), could potentially occur due to the electron return effect (ERE). In this study, we investigate the dosimetric effects of ERE on the dose distribution at air-tissues interfaces in HNC IMRT treatment planning. Methods: IMRT plans were generated based on planning CT’s acquired for HNC cases (nasopharynx, base of skull and paranasal sinus) using a research planning system (Monaco, v5.09.06, Elekta) employing Montemore » Carlo dose calculations with or without the presence of a transverse magnetic field (TMF). The dose in the air cavity was calculated in a 1 & 2 mm thick tissue layer, while the dose to the skin was calculated in a 1, 3 and 5 mm thick tissue layer. The maximum dose received in 1 cc volume, D1cc, were collected at different TMF strengths. Plan qualities generated with or without TMF or with increasing TMF were compared in terms of commonly-used dose-volume parameters (DVPs). Results: Variations in DVPs between plans with and without a TMF present were found to be within 5% of the planning CT. The presence of a TMF results in <5% changes in sinus air tissue interface. The largest skin dose differences with and without TMF were found within 1 mm of the skin surface Conclusion: The presence of a TMF results in practically insignificant changes in HNC IMRT plan quality, except for skin dose. Planning optimization with skin DV constraints could reduce the skin doses. This research was partially supported by Elekta Inc. (Crowley, U.K.)« less

Comparison of orthorhombic and alpha-two titanium aluminides as matrices for continuous SiC-reinforced composites

NASA Astrophysics Data System (ADS)

Smith, P. R.; Graves, J. A.; Rhodes, Cg.

1994-06-01

The attributes of an orthorhombic Ti aluminide alloy, Ti-21Al-22Nb (at. pct), and an alpha-two Ti aluminide alloy, Ti-24Al-11Nb (at. pct), for use as a matrix with continuous SiC (SCS-6) fiber reinforcement have been compared. Foil-fiber-foil processing was used to produce both unreinforced (“neat”) and unidirectional “SCS-6” reinforced panels. Microstructure of the Ti-24A1-11Nb matrix consisted of ordered Ti3Al ( α 2) + disordered beta (β), while the Ti-21 Al-22Nb matrix contained three phases: α2, ordered beta ( β 0), and ordered orthorhombic (O). Fiber/ matrix interface reaction zone growth kinetics at 982 °C were examined for each composite system. Although both systems exhibited similar interface reaction products (i.e., mixed Ti carbides, silicides, and Ti-Al carbides), growth kinetics in the α 2 + β matrix composite were much more rapid than in the O + β 0 + α 2 matrix composite. Additionally, interfacial reaction in the α 2 + β} composite resulted in a relatively large brittle matrix zone, depleted of beta phase, which was not present in the O + β 0+ α 2 matrix composite. Mechanical property measurements included room and elevated temperature tensile, thermal stability, thermal fatigue, thermo-mechanical fatigue (TMF), and creep. The three-phase orthorhombic-based alloy outperformed the α2+ β alloy in all of these mechanical behavioral areas, on both an absolute and a specific (i.e., density corrected) basis.

Convection Induced by Traveling Magnetic Fields in Semiconductor Melts

NASA Technical Reports Server (NTRS)

Konstantin, Mazuruk

2000-01-01

Axisymmetric traveling magnetic fields (TMF) can be beneficial for crystal growth applications. such as the vertical Bridgman, float zone or traveling heater methods. TMF induces a basic flow in the form of a single roll. This type of flow can enhance mass and heat transfer to the growing crystal. More importantly, the TMF Lorentz body force induced in the system can counterbalance the buoyancy forces, so the resulting convection can be much smaller and even the direction of it can be changed. In this presentation, we display basic features of this novel technique. In particular, numerical calculations of the Lorentz force for arbitrary frequencies will be presented along with induced steady-state fluid flow profiles. Also, numerical modeling of the TMF counter-balancing natural convection in vertical Bridgman systems will be demonstrated.

Life prediction and constitutive models for engine hot section anisotropic materials program

NASA Technical Reports Server (NTRS)

Swanson, G. A.; Linask, I.; Nissley, D. M.; Norris, P. P.; Meyer, T. G.; Walker, K. P.

1986-01-01

This report presents the results of the first year of a program designed to develop life prediction and constitutive models for two coated single crystal alloys used in gas turbine airfoils. The two alloys are PWA 1480 and Alloy 185. The two oxidation resistant coatings are PWA 273, an aluminide coating, and PWA 286, an overlay NiCoCrAlY coating. To obtain constitutive and/or fatigue data, tests were conducted on coated and uncoated PWA 1480 specimens tensilely loaded in the 100 , 110 , 111 , and 123 directions. A literature survey of constitutive models was completed for both single crystal alloys and metallic coating materials; candidate models were selected. One constitutive model under consideration for single crystal alloys applies Walker's micromechanical viscoplastic formulation to all slip systems participating in the single crystal deformation. The constitutive models for the overlay coating correlate the viscoplastic data well. For the aluminide coating, a unique test method is under development. LCF and TMF tests are underway. The two coatings caused a significant drop in fatigue life, and each produced a much different failure mechanism.

A comparison of life prediction methodologies for titanium matrix composites subjected to thermomechanical fatigue

DOE Office of Scientific and Technical Information (OSTI.GOV)

Calcaterra, J.R.; Johnson, W.S.; Neu, R.W.

1997-12-31

Several methodologies have been developed to predict the lives of titanium matrix composites (TMCs) subjected to thermomechanical fatigue (TMF). This paper reviews and compares five life prediction models developed at NASA-LaRC. Wright Laboratories, based on a dingle parameter, the fiber stress in the load-carrying, or 0{degree}, direction. The two other models, both developed at Wright Labs. are multi-parameter models. These can account for long-term damage, which is beyond the scope of the single-parameter models, but this benefit is offset by the additional complexity of the methodologies. Each of the methodologies was used to model data generated at NASA-LeRC. Wright Labs.more » and Georgia Tech for the SCS-6/Timetal 21-S material system. VISCOPLY, a micromechanical stress analysis code, was used to determine the constituent stress state for each test and was used for each model to maintain consistency. The predictive capabilities of the models are compared, and the ability of each model to accurately predict the responses of tests dominated by differing damage mechanisms is addressed.« less

Traveling Magnetic Field Applications for Materials Processing in Space

NASA Technical Reports Server (NTRS)

Grugel, R. N.; Mazuruk, K.; Curreri, Peter A. (Technical Monitor)

2001-01-01

Including the capability to induce a controlled fluid flow in the melt can significantly enrich research on solidification phenomena in a microgravity environment. The traveling magnetic field (TMF) is a promising technique to achieve this goal and is the aim of our ground-based project. In this presentation we will discuss new theoretical as well as experimental results recently obtained by our group. In particular, we experimentally demonstrated efficient mixing of metal alloys in long tubes subjected to TMF during processing. Application of this technique can provide an elegant solution to ensure melt homogenization prior to solidification in a microgravity environment where natural convection is generally absent. Results of our experimental work of applying the TMF technique to alloy melts will be presented. Possible applications of TMF on board the International Space Station will also be discussed.

Traditional Masculinity and Femininity: Validation of a New Scale Assessing Gender Roles.

PubMed

Kachel, Sven; Steffens, Melanie C; Niedlich, Claudia

2016-01-01

Gender stereotype theory suggests that men are generally perceived as more masculine than women, whereas women are generally perceived as more feminine than men. Several scales have been developed to measure fundamental aspects of gender stereotypes (e.g., agency and communion, competence and warmth, or instrumentality and expressivity). Although omitted in later version, Bem's original Sex Role Inventory included the items "masculine" and "feminine" in addition to more specific gender-stereotypical attributes. We argue that it is useful to be able to measure these two core concepts in a reliable, valid, and parsimonious way. We introduce a new and brief scale, the Traditional Masculinity-Femininity (TMF) scale, designed to assess central facets of self-ascribed masculinity-femininity. Studies 1-2 used known-groups approaches (participants differing in gender and sexual orientation) to validate the scale and provide evidence of its convergent validity. As expected the TMF reliably measured a one-dimensional masculinity-femininity construct. Moreover, the TMF correlated moderately with other gender-related measures. Demonstrating incremental validity, the TMF predicted gender and sexual orientation in a superior way than established adjective-based measures. Furthermore, the TMF was connected to criterion characteristics, such as judgments as straight by laypersons for the whole sample, voice pitch characteristics for the female subsample, and contact to gay men for the male subsample, and outperformed other gender-related scales. Taken together, as long as gender differences continue to exist, we suggest that the TMF provides a valuable methodological addition for research into gender stereotypes.

Fluid flow analysis and vertical gradient freeze crystal growth in a travelling magnetic field

NASA Astrophysics Data System (ADS)

Lantzsch, R.; Grants, I.; Galindo, V.; Patzold, O.; Gerbeth, G.; Stelter, M.; Croll, A.

2006-12-01

In bulk crystal growth of semiconductors the concept of remote flow control by means of alternating magnetic fields has attracted considerable interest (see, e.g., te{1,2,3,4,5,6}). In this way the melt flow can be tailored for growth under optimised conditions to improve the crystal properties and/or the growth yield. A promising option is to apply an axially travelling magnetic wave to the melt (Travelling Magnetic Field - TMF). It introduces a mainly axial Lorentz force, which leads to meridional flow patterns. In recent numerical studies te{3}, te{6} the TMF has been recognised to be a versatile and efficient tool to control the heat and mass transport in the melt. For the Vertical Bridgman/Vertical Gradient Freeze (VB/VGF) growth, the beneficial effect of an adequately adjusted TMF-induced flow was clearly demonstrated in te{6} in terms of the reduction of thermal shear stress at the solid-liquid interface. In this paper, we present experimental and numerical results on the TMF driven convection in an isothermal model fluid as well as first VGF-TMF crystal growth experiments. The model investigations are focused on the transition from laminar to instationary flow conditions that should be avoided in crystal growth applications. The VGF experiments were aimed at growing Ga doped germanium single crystals under the influence of the travelling field in a newly developed VGF-TMF equipment. Figs 4, Refs 10.

CLONING AND EXPRESSING TRYPSIN MODULATING OOSTATIC FACTOR IN Chlorella desiccata TO CONTROL MOSQUITO LARVAE.

PubMed

Borovsky, Dov; Sterner, Andeas; Powell, Charles A

2016-01-01

The insect peptide hormone trypsin modulating oostatic factor (TMOF), a decapeptide that is synthesized by the mosquito ovary and controls the translation of the gut's trypsin mRNA was cloned and expressed in the marine alga Chlorella desiccata. To express Aedes aegypti TMOF gene (tmfA) in C. desiccata cells, two plasmids (pYES2/TMOF and pYDB4-tmfA) were engineered with pKYLX71 DNA (5 Kb) carrying the cauliflower mosaic virus (CaMV) promoter 35S(2) and the kanamycin resistant gene (neo), as well as, a 8 Kb nitrate reductase gene (nit) from Chlorella vulgaris. Transforming C. desiccata with pYES2/TMOF and pYDB4-tmfA show that the engineered algal cells express TMOF (20 ± 4 μg ± SEM and 17 ± 3 μg ± SEM, respectively in 3 × 10(8) cells) and feeding the cells to mosquito larvae kill 75 and 60% of Ae. aegypti larvae in 4 days, respectively. Southern and Northern blots analyses show that tmfA integrated into the genome of C. desiccata by homologous recombination using the yeast 2 μ circle of replication and the nit in pYES2/TMOF and pYDB4-tmfA, respectively, and the transformed algal cells express tmfA transcript. Using these algal cells it will be possible in the future to control mosquito larvae in the marsh. © 2015 Wiley Periodicals, Inc.

Comparison of diagnostic classification systems for delirium with new research criteria that incorporate the three core domains.

PubMed

Trzepacz, Paula T; Meagher, David J; Franco, José G

2016-05-01

Diagnostic classification systems do not incorporate phenomenological research findings about the three core symptom domains of delirium (Attentional/Cognitive, Circadian, Higher Level Thinking). We evaluated classification performances of novel Trzepacz, Meagher, and Franco research diagnostic criteria (TMF) that incorporate those domains and ICD-10, DSM-III-R, DSM-IV, and DSM-5. Primary data analysis of 641 patients with mixed neuropsychiatric profiles. Delirium (n=429) and nondelirium (n=212) reference standard groups were identified using cluster analysis of symptoms assessed using the Delirium Rating Scale-Revised-98. Accuracy, sensitivity, specificity, positive and negative predictive values (PPV, NPV), and likelihood ratios (LR+, LR-) are reported. TMF criteria had high sensitivity and specificity (87.4% and 89.2%), more balanced than DSM-III-R (100% and 31.6%), DSM-IV (97.7% and 74.1%), DSM-5 (97.7% and 72.6%), and ICD-10 (66.2% and 100%). PPV of DSM-III-R, DSM-IV, and DSM-5 were <90.0%, while PPV for ICD-10 and TMF were >90%. ICD-10 had the lowest NPV (59.4%). TMF had the highest LR+ (8.06) and DSM-III-R the lowest LR- (0.0). Overall, values for DSM-IV and DSM-5 were similar, whereas for ICD-10 and DSM-III-R were inverse of each other. In the pre-existing cognitive impairment/dementia subsample (n=128), TMF retained its highest LR+ though specificity (58.3%) became less well balanced with sensitivity (87.9%), which still exceeded that of DSM. TMF research diagnostic criteria performed well, with more balanced sensitivity and specificity and the highest likelihood ratio for delirium identification. Reflecting the three core domains of delirium, TMF criteria may have advantages in biological research where delineation of this syndrome is important. Copyright © 2016. Published by Elsevier Inc.

Traveling Magnetic Field Applications for Materials Processing in Space

NASA Technical Reports Server (NTRS)

Motakef, S.; Grugel, R. N.; Mazuruk, K.; Whitaker, Ann F. (Technical Monitor)

2001-01-01

Including the capability to induce a controlled fluid flow in the melt can significantly enrich research on solidification phenomena in a microgravity environment. The traveling magnetic field (TMF) is a promising technique to achieve this goal and is the aim of our ground-based project. In this presentation we will discuss new theoretical as well as experimental results recently obtained by our group. In particular, we experimentally demonstrated efficient mixing of metal alloys in long tubes subjected to TMF during processing. Application of this technique can be an elegant solution to ensure melt homogenization prior to solidification in a microgravity environment where natural convection is generally absent. Results of our theoretical work on TMF induced flows, such as convection control in Bridgman as well as in the Traveling Heater method, will be presented. Possible applications of TMF on board the ISS will also be discussed.

Traditional Masculinity and Femininity: Validation of a New Scale Assessing Gender Roles

PubMed Central

Kachel, Sven; Steffens, Melanie C.; Niedlich, Claudia

2016-01-01

Gender stereotype theory suggests that men are generally perceived as more masculine than women, whereas women are generally perceived as more feminine than men. Several scales have been developed to measure fundamental aspects of gender stereotypes (e.g., agency and communion, competence and warmth, or instrumentality and expressivity). Although omitted in later version, Bem's original Sex Role Inventory included the items “masculine” and “feminine” in addition to more specific gender-stereotypical attributes. We argue that it is useful to be able to measure these two core concepts in a reliable, valid, and parsimonious way. We introduce a new and brief scale, the Traditional Masculinity-Femininity (TMF) scale, designed to assess central facets of self-ascribed masculinity-femininity. Studies 1–2 used known-groups approaches (participants differing in gender and sexual orientation) to validate the scale and provide evidence of its convergent validity. As expected the TMF reliably measured a one-dimensional masculinity-femininity construct. Moreover, the TMF correlated moderately with other gender-related measures. Demonstrating incremental validity, the TMF predicted gender and sexual orientation in a superior way than established adjective-based measures. Furthermore, the TMF was connected to criterion characteristics, such as judgments as straight by laypersons for the whole sample, voice pitch characteristics for the female subsample, and contact to gay men for the male subsample, and outperformed other gender-related scales. Taken together, as long as gender differences continue to exist, we suggest that the TMF provides a valuable methodological addition for research into gender stereotypes. PMID:27458394

Objective Evaluation Tool for Texture-Modified Food (OET-TMF): Development of the Tool and Validation.

PubMed

Calleja-Fernández, Alicia; Pintor-de-la-Maza, Begoña; Vidal-Casariego, Alfonso; Cano-Rodríguez, Isidoro; Ballesteros-Pomar, María D

2016-06-01

Texture-modified diets (TMDs) should fulfil nutritional goals, guarantee homogenous texture, and meet food safety regulations. The food industry has created texture-modified food (TMF) that meets the TMD requirements of quality and safety for inpatients. To design and develop a tool that allows the objective selection of foodstuffs for TMDs that ensures nutritional requirements and swallowing safety of inpatients in order to improve their quality of life, especially regarding their food satisfaction. An evaluation tool was designed to objectively determine the adequacy of food included in the TMD menus of a hospital. The "Objective Evaluation Tool for Texture-Modified Food" (OET-TMF) consists of seven items that evaluate the food's nutritional quality (energy and protein input), presence of allergens, texture and viscosity, cooking, storage type, useful life, and patient acceptance. The total score ranged from 0 to 64 and was divided into four categories: high quality, good quality, medium quality, and low quality. Studying four different commercial TMFs contributed to the validation of the tool. All the evaluated products scored between high and good regarding quality. There was a tendency (p = 0.077) towards higher consumption and a higher overall quality of the product obtained with the OET-TMF. The product that scored highest with the tool was the best accepted; the product with the lowest score had the highest rate of refusal. The OET-TMF allows for the objective discrimination of the quality of TMF. In addition, it shows a certain relationship between the observed and assessed quality intake.

Effects of Traveling Magnetic Field on Dynamics of Solidification

NASA Technical Reports Server (NTRS)

2003-01-01

The Lorentz body force induced in electrically conducting fluids can be utilized for a number of materials processing technologies. An application of strong static magnetic fields can be beneficial for damping convection present during solidification. On the other hand, alternating magnetic fields can be used to reduce as well as to enhance convection. However, only special types of time dependent magnetic fields can induce a non-zero time averaged Lorentz force needed for convection control. One example is the rotating magnetic field. This field configuration induces a swirling flow in circular containers. Another example of a magnetic field configuration is the traveling magnetic field (TMF). It utilizes axisymmetric magnetostatic waves. This type of field induces an axial recirculating flow that can be advantageous for controlling axial mass transport, such as during solidification in long cylindrical tubes. Incidentally, this is the common geometry for crystal growth research. The Lorentz force induced by TMF can potentially counter-balance the buoyancy force, diminishing natural convection, or even setting up the flow in reverse direction. Crystal growth process in presence of TMF can be then significantly modified. Such properties as the growth rate, interface shape and macro segregation can be affected and optimized. Melt homogenization is the other potential application of TMF. It is a necessary step prior to solidification. TMF can be attractive for this purpose, as it induces a basic flow along the axis of the ampoule. TMF can be a practical alloy mixing method especially suited for solidification research in space. In the theoretical part of this work, calculations of the induced Lorentz force in the whole frequency range have been completed. The basic flow characteristics for the finite cylinder geometry are completed and first results on stability analysis for higher Reynolds numbers are obtained. A theoretical model for TMF mixing is also developed. In the experimental part, measurements of flow induced by TMF in a column of mercury (Hg) are presented. Also, an alloy mixing of Bi-Sn of the eutectic composition is demonstrated. A traveling magnetic field of 4mT at 3kHz applied for 120 minutes is found to be sufficient to homogenize an alloy enclosed in a 1cm diameter and 12 cm long tube.

Inducing Lift on Spherical Particles by Traveling Magnetic Fields

NASA Technical Reports Server (NTRS)

Mazuruk, Konstantin; Grugel, Richard N.; Rose, M. Franklin (Technical Monitor)

2001-01-01

Gravity induced sedimentation of suspensions is a serious drawback to many materials and biotechnology processes, a factor that can, in principle, be overcome by utilizing an opposing Lorentz body force. In this work we demonstrate the utility of employing a traveling magnetic field (TMF) to induce a lifting force on particles dispersed in the fluid. Theoretically, a model has been developed to ascertain the net force, induced by TMF, acting on a spherical body as a function of the fluid medium's electrical conductivity and other parameters. Experimentally, the model is compared to optical observations of particle motion in the presence of TMF.

Inducing Lift on Spherical Particles by Traveling Magnetic Fields

NASA Technical Reports Server (NTRS)

Mazuruk, Konstantin; Grugel, Richard N.; Rose, M. Franklin (Technical Monitor)

2000-01-01

Gravity induced sedimentation of suspensions is a serious drawback to many materials and biotechnology processes, a factor that can, in principle, be overcome by utilizing an opposing Lorentz body force. In this work we demonstrate the utility of employing a traveling magnetic field (TMF) to induce a lifting force on particles dispersed in the fluid. Theoretically, a model has been developed to ascertain the net force, induced by TMF, acting on a spherical body as a function of the fluid medium's electrical conductivity and other parameters. Experimentally, the model is compared to optical observations of particle motion in the presence of TMF.

The Transportable Measurements Facility (TMF) System Description.

DTIC Science & Technology

1980-05-23

sites using different antennas, antenna/site characterization, ATCRBS-mode and DABS-mode processor evaluation, and DABS-based ATC and ATARS system...conditions met. 34 TABLE 3 TMF DATA RECORDED DURING EXPERIMENTS By Word Type 1) By Parameter Word No. of Bits Experiment Number 8 Physical Location Number of

75 FR 61788 - Triangle Capital Corporation, et al.; Notice of Application

Federal Register 2010, 2011, 2012, 2013, 2014

2010-10-06

... to the issuers of such securities. 2. TMF, a North Carolina limited liability limited partnership, is... same investment objectives and strategies as Triangle. Triangle owns a 99.9% limited partnership... persons who are interested persons of TMF. 3. SBIC II, a Delaware limited partnership, is an SBIC licensed...

Effects of Traveling Magnetic Field on Dynamics of Solidification

NASA Technical Reports Server (NTRS)

Mazuruk, Konstantin; Grugel, Richard; Motakef, Shariar

2001-01-01

TMF is based on imposing a controlled phase-shift in a train of electromagnets, forming a stack. Thus, the induced magnetic field can be considered to be travelling along the axis of the stack. The coupling of this traveling wave with an electrically conducting fluid results in a basic flow in a form of a single axisymmetric roll. The magnitude and direction of this flow can be remotely controlled. Furthermore, it is possible to localize the effect of this force field though activating only a number of the magnets. This force field generated in the fluid can, in principle, be used to control and modify convection in the molten material. For example, it can be used to enhance convective mixing in the melt, and thereby modify the interface shape, and macrosegregation. Alternatively, it can be used to counteract thermal and/or solutal buoyancy forces. High frequency TMF can be used in containerless processing techniques, such as float zoning, to affect the very edge of the fluid so that Marangoni flow can be counter balanced. The proposed program consists of basic fundamentals and applications. Our goal in conducting the following experiments and analyses is to establish the validity of TMF as a new tool for solidification processes. Due to its low power consumption and simplicity of design, this tool may find wide spread use in a variety of space experiments. The proposed ground based experiments are intended to establish the advantages and limitations of employing this technique. In the fundamentals component of the proposed program, we will use theoretical tools and experiments with mercury to establish the fundamental aspects of TMF-induced convection through a detailed comparison of theoretical predictions and experimental measurements of flow field. In this work, we will conduct a detailed parametric study involving the effects of magnetic field strength, frequency, wave vector, and the fluid geometry. The applications component of this work will be focused on investigating the effect of TMF on the following solidification and pre-directional solidification processes: (1) Bridgman growth of Ga:Ge with the goal of counteracting the buoyancy-driven convection; (2) Mixing of Pb-Ga and Pb-Sn alloys with the aim of initiating and maintaining a uniform melt prior to solidification processing; and (3) Float Zone growth with the aim of identifying, through simulations and model experiments, conditions needed to counteract Marangoni flow in a microgravity environment. The proposed research has strong relevance to microgravity research and the objectives of the NRA. TMF can provide a unique and accurate mechanism for generation and control of desirable flow patterns for microgravity research. These attributes have significant relevance to 1) Alloy mixing prior to solidification in a microgravity environment. TMF can provide this mixing with a low level of power consumption; (2) TMF can offset the deleterious effects of Marangoni convection in microgravity containerless processing. Thus, TMF can be instrumental in further understanding this phenomena; (3) Generation of controlled flows will allow the investigation of the effect of these flows on growth morphology and growth kinetics; and (4) On Earth, TMF has the potential to significantly counter-balance thermosolutal convection, thereby creating conditions similar to those obtained in microgravity. Once demonstrated, this new tool for use in solidification has the strong potential to find applications in a host of microgravity material research projects.

Using laser ablation-inductively coupled plasma-mass spectrometry (LA-ICP-MS) to explore geochemical taphonomy of vertebrate fossils in the upper cretaceous two medicine and Judith River formations of Montana

USGS Publications Warehouse

Rogers, R.R.; Fricke, H.C.; Addona, V.; Canavan, R.R.; Dwyer, C.N.; Harwood, C.L.; Koenig, A.E.; Murray, R.; Thole, J.T.; Williams, J.

2010-01-01

Laser ablation-inductively coupled plasma-mass spectrometry (LA-ICP-MS) was used to determine rare earth element (REE) content of 76 fossil bones collected from the Upper Cretaceous (Campanian) Two Medicine (TMF) and Judith River (JRF) Formations of Montana. REE content is distinctive at the formation scale, with TMF samples exhibiting generally higher overall REE content and greater variability in REE enrichment than JRF samples. Moreover, JRF bones exhibit relative enrichment in heavy REE, whereas TMF bones span heavy and light enrichment fields in roughly equal proportions. TMF bones are also characterized by more negative Ce anomalies and greater U enrichment than JRF bones, which is consistent with more oxidizing diagenetic conditions in the TMF. Bonebeds in both formations show general consistency in REE content, with no indication of spatial or temporal mixing within sites. Previous studies, however, suggest that the bonebeds in question are attritional assemblages that accumulated over considerable time spans. The absence of geochemical evidence for mixing is consistent with diagenesis transpiring in settings that remained chemically and hydrologically stable during recrystallization. Lithology-related patterns in REE content were also compared, and TMF bones recovered from fluvial sandstones show relative enrichment in heavy REE when compared with bones recovered from fine-grained floodplain deposits. In contrast, JRF bones, regardless of lithologic context (sandstone versus mudstone), exhibit similar patterns of REE uptake. This result is consistent with previous reconstructions that suggest that channel-hosted microfossil bonebeds of the JRF developed via the reworking of preexisting concentrations embedded in the interfluve. Geochemical data further indicate that reworked elements were potentially delivered to channels in a recrystallized condition, which is consistent with rapid adsorption of REE postmortem. Copyright ?? 2010, SEPM (Society for Sedimentary Geology).

Tangeretin and its metabolite 4'-hydroxytetramethoxyflavone attenuate EGF-stimulated cell cycle progression in hepatocytes; role of inhibition at the level of mTOR/p70S6K.

PubMed

Cheng, Z; Surichan, S; Ruparelia, K; Arroo, R; Boarder, M R

2011-04-01

The mechanisms by which the dietary compound tangeretin has anticancer effects may include acting as a prodrug, forming an antiproliferative product in cancer cells. Here we show that tangeretin also inhibits cell cycle progression in hepatocytes and investigate the role of its primary metabolite 4'-hydroxy-5,6,7,8-tetramethoxyflavone (4'-OH-TMF) in this effect. We used epidermal growth factor (EGF)-stimulated rat hepatocytes, with [(3)H]-thymidine incorporation into DNA as an index of progression to S-phase of the cell cycle, and Western blots for phospho-proteins involved in the cell signalling cascade. Incubation of tangeretin with microsomes expressing CYP1A, or with hepatocytes, generated a primary product we identified as 4'-OH-TMF. Low micromolar concentrations of tangeretin or 4'-OH-TMF gave a concentration-dependent inhibition of EGF-stimulated progression to S-phase while having little effect on cell viability. To determine whether time for conversion of tangeretin to an active metabolite would enhance the inhibitory effect we used long pre-incubations; this reduced the inhibitory effect, in parallel with a reduction in the concentration of tangeretin. The EGF-stimulation of hepatocyte cell cycle progression requires signalling through Akt/mTOR/p70S6K kinase cascades. The tangeretin metabolite 4'-OH-TMF selectively inhibited S6K phosphorylation in the absence of significant inhibition of upstream Akt activity, suggesting an effect at the level of mTOR. Tangeretin and 4'-OH-TMF both inhibit cell cycle progression in primary hepatocytes. The inhibition of p70S6K phosphorylation by 4'-OH-TMF raises the possibility that inhibition of the mTOR pathway may contribute to the anticancer influence of a flavonoid-rich diet. © 2011 The Authors. British Journal of Pharmacology © 2011 The British Pharmacological Society.

MRI-based IMRT planning for MR-linac: comparison between CT- and MRI-based plans for pancreatic and prostate cancers

NASA Astrophysics Data System (ADS)

Prior, Phil; Chen, Xinfeng; Botros, Maikel; Paulson, Eric S.; Lawton, Colleen; Erickson, Beth; Li, X. Allen

2016-05-01

The treatment planning in radiation therapy (RT) can be arranged to combine benefits of computed tomography (CT) and magnetic resonance imaging (MRI) together to maintain dose calculation accuracy and improved target delineation. Our aim is study the dosimetric impact of uniform relative electron density assignment on IMRT treatment planning with additional consideration given to the effect of a 1.5 T transverse magnetic field (TMF) in MR-Linac. A series of intensity modulated RT (IMRT) plans were generated for two representative tumor sites, pancreas and prostate, using CT and MRI datasets. Representative CT-based IMRT plans were generated to assess the impact of different electron density (ED) assignment on plan quality using CT without the presence of a 1.5 T TMF. The relative ED (rED) values used were taken from the ICRU report 46. Four types of rED assignment in the organs at risk (OARs), the planning target volumes (PTV) and in the non-specified tissue (NST) were considered. Dose was recalculated (no optimization) using a Monaco 5.09.07a research planning system employing Monte Carlo calculations with an option to include TMF. To investigate the dosimetric effect of different rED assignment, the dose-volume parameters (DVPs) obtained from these specific rED plans were compared to those obtained from the original plans based on CT. Overall, we found that uniform rED assignment results in differences in DVPs within 3% for the PTV and 5% for OAR. The presence of 1.5 T TMF on IMRT DVPs resulted in differences that were generally within 3% of the Gold St for both the pancreas and prostate. The combination of uniform rED assignment and TMF produced differences in DVPs that were within 4-5% of the Gold St. Larger differences in DVPs were observed for OARs on T2-based plans. The effects of using different rED assignments and the presence of 1.5 T TMF for pancreas and prostate IMRT plans are generally within 3% and 5% of PTV and OAR Gold St values. There are noticeable dosimetric differences between the CT- and MRI-based IMRT plans caused by a combination of anatomical changes between the two image acquisition times, uniform rED assignment and 1.5 T TMF. This work was present in part at the 2014 ASTRO annual meeting.

Care staff perspective on use of texture modified food in care home residents with dysphagia and dementia.

PubMed

Austbø Holteng, Lise Birgitte; Frøiland, Christina Tølbøl; Corbett, Anne; Testad, Ingelin

2017-10-01

Dysphagia and dementia are conditions, which combined, can lead to complications for the person and require good nutritional care. There is very little evidence-based literature regarding nutritional care for people with dysphagia and dementia. It is clear that care staff plays a vital role, and that communication and informed decision-making are critical to the process, yet little is known regarding the use of available interventions such as texture modified food (TMF), and their acceptability and feasibility for care staff and residents. Therefore the aim of this study was to investigate the experiences of care staff when providing nutritional care for people with dysphagia and dementia, and their impressions and experience of using TMF as a new intervention for nutrition. This was a qualitative study with an inductive approach, which aimed to explore the experience of care staff using TMF in a care home setting. Data were collected using focus group interviews, an approach which is validated as a means of supporting and developing the understanding of a phenomenon, through interactions and discussions in the group. Participants were care staff working in a care home setting in Norway. Twelve participants were recruited to this study across two focus groups. The cohort included four nurses, six practical nurses, one nurse assistants and one student nurse. Four main categories emerged from the focus group discussions regarding the use of TMF. These were: (I) emotional strain; (II) deficient nutritional care; (III) increased self-efficacy with use of TMF; (IV) better nutritional care with TMF. Use of TMF to improve nutritional care for people with dysphagia appears to have merit for both residents and care staff, and should be considered as a means of improving nutritional care for people with dementia in care homes. Minimizing feeding difficulties and increasing nutritional intake is an important goal when caring for this vulnerable group of people, and there is a need to provide better training and support for care staff to ensure they feel confident and empowered to provide high quality nutritional care. The existing Norwegian Directorate of Health checklist for nutritional care may provide a helpful basis for improvements to guidance that accounts for the needs of staff and institutions. Further research and evaluation of an intervention for tailored nutritional care is warranted to improve this critical aspect of dementia care.

Evidence for submarine landslides and continental slope erosion related to fault reactivation during the last glaciation offshore eastern Canada

NASA Astrophysics Data System (ADS)

Saint-Ange, F.; Campbell, C.; MacKillop, K.; Mosher, D. C.; Piper, D. J.; Roger, J.

2012-12-01

Many studies have proposed that reactivation of dormant faults during deglaciation is a source of neotectonic activity in glaciated regions, but few have demonstrated the relationship to submarine landslides. In this study, seabed morphology and shallow geology of the outer continental margin adjacent to the Charlie Gibbs Fracture Zone off Newfoundland, Canada was investigated for evidence of this relationship. The glacial history and morphology of the margin suggest that the entire continental shelf in the area, coincident with major continental crustal lineaments, was ice-covered during the Last glacial cycle, and transverse troughs delineate the paleo-icestream drainage patterns. A recent investigation of Notre Dame Trough revealed the existence of large sediment failures on the shelf. The current study investigates complex seafloor erosion and widespread mass transport deposition (MTD) on the continental slope seaward of Notre Dame Trough, using recently-acquired high resolution seismic reflection data and piston cores. The new data reveal that a trough mouth fan (TMF) is present on the slope seaward of Notre Dame Trough. The Notre Dame TMF is characterized by a succession of stacked debris flows, but does not show a lobate shape in plan view like other classic TMFs. Instead, the Notre Dame TMF has abruptly-truncated margins suggesting post-depositional failure and erosion of the fan deposits. Seismic reflection data show that the locations of the failures along the TMF margin are coincident with a set of shallow faults; however the current dataset does not image the deeper portion of the faults. On the upper slope immediately south of the TMF, a narrow and deeply incised canyon is located along-trend with the Notre Dame Trough. The location of this canyon appears to be controlled by a fault. Downslope from this canyon, along the southern margin of the TMF, a 25 km wide, flat-floored, U-shaped valley was eroded into a succession of stacked MTD-filled channels. Seismic stratigraphic analysis shows that the valley developed around the same time as the adjacent TMF, however, the valley morphology and evidence for repeated slope failure suggests that the processes responsible for its formation were different than the processes that formed the nearby TMF. Age control provided from piston cores suggest that the last major slope failure that contributed to valley formation probably occurred at ~29 ka. Geotechnical measurements from piston cores show slightly underconsolidated sediments. The results indicate that this part of the margin is more unstable than Orphan Basin and Labrador slope regions. Given the low factor of safety and the complex fault system, low energy earthquake from the surrounding area could be enough to potentially trigger landslides.

Mountain-Top-to-Mountain-Top Optical Link Demonstration. Part 1

NASA Technical Reports Server (NTRS)

Biswas, A.; Wright, M. W.

2002-01-01

A mountain-top-to-mountain-top optical link was demonstrated between JPL's Table Mountain Facility (TMF), Wrightwood, California, and Strawberry Peak (SP), Lake Arrowhead, California, during the months of June, August, and September of 2000. The bidirectional laser link was nearly horizontal at an altitude of 2 km and spanned a range of 46.8 km. The 780-nm beacon laser transmitted from TMF comprised eight co-propagating mutually incoherent laser beams. The normalized variance or scintillation index (SI) of the individual beacon lasers measured by recording the signal received through 8.50-cm-diameter spotting telescopes on three different nights (June 28-30, 2000) was 1.05 +/- 0.2, 1.76 +/- 0.6, and 0.96 +/- 0.24, respectively. These measurements agreed with values predicted by a heuristic model. The SI of the signal received at SP was found to decrease progressively with an increasing number of beams, and a factor of 3 to 3.5 reduction was achieved for all eight beams. The beam divergence determined by mapping out the point spread function of a few of the individual laser footprints received at SP was 85 to 150 microrad, compared to a design goal of 120 microrad. The 852-nm communications laser beam received at TMF through a 60-cm-diameter telescope on the nights of August 4 and September 14 and 15, 2000, yielded SI values of 0.23 +/- 0.04, 0.32 +/- 0.01, and 0.49 +/- 0.18, respectively, where the reduction was attributed to aperture averaging. The probability distribution functions of the received signal at either end, mitigated by multi-beam averaging in one direction and by aperture averaging in the other direction, displayed lognormal behavior. Consequently, the measured fade statistics showed good agreement with a lognormal model.

From hopping to ballistic transport in graphene-based electronic devices

NASA Astrophysics Data System (ADS)

Taychatanapat, Thiti

This thesis describes electronic transport experiments in graphene from the hopping to the ballistic regime. The first experiment studies dual-gated bilayer graphene devices. By applying an electric field with these dual gates, we can open a band gap in bilayer graphene and observe an increase in resistance of over six orders of magnitude as well as a strongly non-linear behavior in the transport characteristics. A temperature-dependence study of resistance at large electric field at the charge neutrality point shows the change in the transport mechanism from a hopping dominated regime at low temperature to a diffusive regime at high temperature. The second experiment examines electronic properties of Bernal-stacked trilayer graphene. Due to the low mobility of trilayer graphene on SiO 2substrates, we employ hexagonal boron nitride as a local substrate to improve its mobility. This led us to observe a quantum Hall effect with multiple Landau level crossings, proving the coexistence of massless and massive Dirac fermions in Bernal-stacked trilayer graphene. From the position of these crossing points in magnetic field and electron density, we can deduce the band parameters used to model its band structure. At high magnetic field, we observe broken symmetry states via Landau level splittings as well as crossings among these broken-symmetry states. In the third experiment, we investigate transverse magnetic focusing (TMF) in mono-, bi-, and tri-layer graphene. The ability to tune density allows us to electronically modify focal points and investigate TMF continuously from hole to electron regimes. This also allows us to observe the change in band structure of trilayer graphene as a function of applied electric field. Finally, we also observe TMF at room temperature in monolayer graphene which unambiguously proves the existence of ballistic transport at room temperature.

High-performance Thin-layer Chromatography Method Development, Validation, and Simultaneous Quantification of Four Compounds Identified in Standardized Extracts of Orthosiphon stamineus.

PubMed

Hashim, Suzana; Beh, Hooi Kheng; Hamil, Mohamad Shahrul Ridzuan; Ismail, Zhari; Majid, Amin Malik Shah Abdul

2016-01-01

Orthosiphon stamineus is a medicinal herb widely grown in Southeast Asia and tropical countries. It has been used traditionally as a diuretic, abdominal pain, kidney and bladder inflammation, gout, and hypertension. This study aims to develop and validate the high-performance thin layer chromatography (HPTLC) method for quantification of rosmarinic acid (RA), 3'-hydroxy-5,6,7,4'-tetramethoxyflavone (TMF), sinensitin (SIN) and eupatorin (EUP) found in ethanol, 50% ethanol and water extract of O. stamineus leaves. HPTLC method was conducted using an HPTLC system with a developed mobile phase system of toluene: ethyl acetate: formic acid (3:7:0.1) performed on precoated silica gel 60 F254 TLC plates. The method was validated based on linearity, accuracy, precision, limit of detection, limit of quantification (LOQ), and specificity, respectively. The detection of spots was observed at ultraviolet 254 nm and 366 nm. The linearity of RA, TMF, SIN, and EUP were obtained between 10 and 100 ng/spot with high correlation coefficient value (R 2 ) of more than 0.986. The limit of detection was found to be 122.47 ± 3.95 (RA), 43.38 ± 0.79 (SIN), 17.26 ± 1.16 (TMF), and 46.80 ± 1.33 ng/spot (EUP), respectively. Whereas the LOQ was found to be 376.44 ± 6.70 (RA), 131.45 ± 2.39 (SIN), 52.30 ± 2.01 (TMF), and 141.82 ± 1.58 ng/spot (EUP), respectively. The proposed method showed good linearity, precision, accuracy, and high sensitivity. Hence, it may be applied in a routine quantification of RA, SIN, TMF, and EUP found in ethanol, 50% of ethanol and water extract of O. stamineus leaves. HPTLC method provides rapid estimation of the marker compound for routine quality control analysis.The established HPTLC method is rapid for qualitative and quantitative fingerprinting of Orthosiphon stamineus extract used for commercial product.Four identified markers (RA, SIN, EUP and TMF) found in three a different type of O. stamineus extracts specifically ethanol, 50% ethanol and water extract were successfully quantified using HPTLC method. Abbreviations Used : HPTLC: High-performance thin layer chromatography; RA: Rosmarinic acid; TMF: 3'-hydroxy-5,6,7,4'-tetramethoxyflavone; SIN: Sinensitin; EUP: Eupatorin; E: Ethanol; EW: 50% ethanol; W: Water; BK: Batu Kurau; KB: Kepala Batas; S: Sik; CJ: Changkat Jering; SB: Sungai Buloh.

Morphobiochemical diagnosis of acute trabecular microfractures using gamma correction Tc-99m HDP pinhole bone scan with histopathological verification.

PubMed

Bahk, Yong-Whee; Hwang, Seok-Ha; Lee, U-Young; Chung, Yong-An; Jung, Joo-Young; Jeong, Hyeonseok S

2017-11-01

We prospectively performed gamma correction pinhole bone scan (GCPBS) and histopathologic verification study to make simultaneous morphobiochemical diagnosis of trabecular microfractures (TMF) occurred in the femoral head as a part of femoral neck fracture.Materials consisted of surgical specimens of the femoral head in 6 consecutive patients. The specimens were imaged using Tc-99m hydroxymethylene diphosphonate (HDP) pinhole scan and processed by the gamma correction. After cleansing with 10% formalin solution, injured specimen surface was observed using a surgical microscope to record TMF. Morphological findings shown in the photograph, naive pinhole bone scan, GCPBS, and hematoxylin-eosin (H&E) stain of the specimen were reciprocally correlated for histological verification and the usefulness of suppression and enhancement of Tc-99m HDP uptake was biochemically investigated in TMF and edema and hemorrhage using gamma correction.On the one hand, GCPBS was able to depict the calcifying calluses in TMF with enhanced Tc-99m HDP uptake. They were pinpointed, speckled, round, ovoid, rod-like, geographic, and crushed in shape. The smallest callus measured was 0.23 mm in this series. On the other hand, GCPBS biochemically was able to discern the calluses with enhanced high Tc-99m HDP uptake from the normal and edema dipped and hemorrhage irritated trabeculae with washed out uptake.Morphobiochemically, GCPBS can clearly depict microfractures in the femoral head produced by femoral neck fracture. It discerns the microcalluses with enhanced Tc-99m HDP uptake from the intact and edema dipped and hemorrhage irritated trabeculae with suppressed washed out Tc-99m HDP uptake. Both conventional pinhole bone scan and gamma correction are useful imaging means to specifically diagnose the microcalluses naturally formed in TMF.

Magnetic Field Applications in Semiconductor Crystal Growth and Metallurgy

NASA Technical Reports Server (NTRS)

Mazuruk, Konstantin; Ramachandran, Narayanan; Grugel, Richard; Curreri, Peter A. (Technical Monitor)

2002-01-01

The Traveling Magnetic Field (TMF) technique, recently proposed to control meridional flow in electrically conducting melts, is reviewed. In particular, the natural convection damping capability of this technique has been numerically demonstrated with the implication of significantly improving crystal quality. Advantages of the traveling magnetic field, in comparison to the more mature rotating magnetic field method, are discussed. Finally, results of experiments with mixing metallic alloys in long ampoules using TMF is presented

Transverse magnetic field effect on the giant Goos–Hänchen shifts based on a degenerate two-level system

NASA Astrophysics Data System (ADS)

Nasehi, R.

2018-06-01

We study the effect of the Goos–Hänchen (GH) shifts through a cavity with degenerate two-level systems in the line of . For this purpose, we focus on the transverse magnetic field (TMF) in a Floquet frame to obtain the giant GH shifts. Physically, the collisional effects of TMF lead to increasing the population trapping in the ground state. However, we demonstrate that the population trapping generates the large negative or positive GH shifts and simultaneously switches from superluminal to subluminal (or vice versa). Also, we investigate the other optical properties such as the longitudinal magnetic field (LMF), which plays an important role in the control of the GH shifts and leads to the generation of new subsystems. In the next step, we evaluate the GH shifts beyond the multi-photon resonance condition by the control of TMF. Moreover, we compute the appearance of negative and positive GH shifts by setting the width of the incident Gaussian beams in the presence of a multi-photon resonance condition. Our results show that superluminal or subluminal light propagation can be simultaneously controlled by adjusting the rates of the TMF and LMF. The significant effects of these factors on the degenerate two-level systems provide different applications such as slow light, optical switches and quantum information storage.

Predicting arsenic concentrations in porewaters of buried uranium mill tailings

DOE Office of Scientific and Technical Information (OSTI.GOV)

Langmuir, D.; Mahoney, J.; MacDonald, A.

The proposed JEB Tailings Management Facility (TMF) to be emplaced below the groundwater table in northern Saskatchewan, Canada, will contain uranium mill tailings from McClean Lake, Midwest and Cigar Lake ore bodies, which are high in arsenic (up to 10%) and nickel (up to 5%). A serious concern is the possibility that high arsenic and nickel concentrations may be released from the buried tailings, contaminating adjacent groundwaters and a nearby lake. Laboratory tests and geochemical modeling were performed to examine ways to reduce the arsenic and nickel concentrations in TMF porewaters so as to minimize such contamination from tailings buriedmore » for 50 years and longer. The tests were designed to mimic conditions in the mill neutralization circuit (3 hr tests at 25 C), and in the TMF after burial (5--49 day aging tests). The aging tests were run at 50, 25 and 4 C (the temperature in the TMF). In order to optimize the removal of arsenic by adsorption and precipitation, ferric sulfate was added to tailings raffinates having Fe/As ratios of less than 3--5. The acid raffinates were then neutralized by addition of slaked lime to nominal pH values of 7, 8, or 9. Analysis and modeling of the test results showed that with slaked lime addition to acid tailings raffinates, relatively amorphous scorodite (ferric arsenate) precipitates near pH 1, and is the dominant form of arsenate in slake limed tailings solids except those high in Ni and As and low in Fe, in which cabrerite-annabergite (Ni, Mg, Fe(II) arsenate) may also precipitate near pH 5--6. In addition to the arsenate precipitates, smaller amounts of arsenate are also adsorbed onto tailings solids. The aging tests showed that after burial of the tailings, arsenic concentrations may increase with time from the breakdown of the arsenate phases (chiefly scorodite). However, the tests indicate that the rate of change decreases and approaches zero after 72 hrs at 25 C, and may equal zero at all times in the TMF at 4 C. Consistent with a kinetic model that describes the rate of breakdown of scorodite to form hydrous ferric oxide, the rate of release of dissolved arsenate to tailings porewaters from slake limed tailings: (1) is proportional to pH above pH 6--7; (2) decreases exponentially as the total molar Fe/As ratio of tailings raffinates is increased from 1/1 to greater than 5/1; and (3) is proportional to temperature with an average Arrhenius activation energy of 13.4 {+-} 4.2 kcal/mol. Study results suggest that if ferric sulfate and slaked lime are added in the tailings neutralization circuit to give a raffinate Fe/As molar ratio of at least 3--5 and a nominal (initial) pH of 8 (final pH of 7--8), arsenic and nickel concentrations of 2 mg/L or less, are probable in porewaters of individual tailings in the TMF for 50 to 10,000 yrs after tailings disposal. However, the tailings will be mixed in the TMF, which will contain about 35% tailings with Fe/As = 3.0, and 65% tailings with Fe/As = 5.0--7.7. Thus, it seems likely that average arsenic pore water concentrations in the TMF may not exceed 1 mg/L.« less

Interdependence of right ventricular systolic function and left ventricular filling and its association with outcome for patients with pulmonary hypertension.

PubMed

Motoji, Yoshiki; Tanaka, Hidekazu; Fukuda, Yuko; Sano, Hiroyuki; Ryo, Keiko; Imanishi, Junichi; Miyoshi, Tatsuya; Sawa, Takuma; Mochizuki, Yasuhide; Matsumoto, Kensuke; Emoto, Noriaki; Hirata, Ken-ichi

2015-04-01

Although impaired right ventricular (RV) performance has been associated with adverse outcomes for pulmonary hypertension (PH) patients, the relationship between bi-ventricular interdependence and outcomes is not yet fully understood. We studied 96 PH patients. RV systolic function was assessed by means of RV free-wall longitudinal speckle-tracking strain (RV-free), and left ventricular (LV) filling as early diastolic transmitral flow velocity (TMF-E). RV-free ≤19 % and TMF-E <60 cm/s were adopted as pre-defined cut-offs for RV systolic dysfunction and LV under-filling, respectively, associated with worse outcomes. Long-term outcome was tracked over 2.2 years. RV-free correlated significantly with TMF-E (r = 0.57, p < 0.001).TMF-E and RV-free were significantly lower in patients with than in those without cardiac events. RV systolic dysfunction and LV under-filling was observed in 35 patients. These features were associated with worse long-term survival compared to other sub-groups (log-rank p = 0.012). A sequential Cox model based on clinical variables including world health organization functional class IV and brain natriuretic peptide >150 pg/dl (χ(2) = 1.2) was improved by the addition of RV-free (χ(2) = 5.5, p = 0.04) as well as of TMF-E (χ(2) = 11.5, p = 0.01). In conclusions, RV systolic function was shown to correlate significantly with LV filling in PH patients. In addition, not only assessment of RV systolic function, but also of a combined bi-ventricular parameter comprising RV systolic function and LV filling may well have clinical implications for more successful management of PH patients.

Intelligent Life-Extending Controls for Aircraft Engines

NASA Technical Reports Server (NTRS)

Guo, Ten-Huei; Chen, Philip; Jaw, Link

2005-01-01

Aircraft engine controllers are designed and operated to provide desired performance and stability margins. The purpose of life-extending-control (LEC) is to study the relationship between control action and engine component life usage, and to design an intelligent control algorithm to provide proper trade-offs between performance and engine life usage. The benefit of this approach is that it is expected to maintain safety while minimizing the overall operating costs. With the advances of computer technology, engine operation models, and damage physics, it is necessary to reevaluate the control strategy fro overall operating cost consideration. This paper uses the thermo-mechanical fatigue (TMF) of a critical component to demonstrate how an intelligent engine control algorithm can drastically reduce the engine life usage with minimum sacrifice in performance. A Monte Carlo simulation is also performed to evaluate the likely engine damage accumulation under various operating conditions. The simulation results show that an optimized acceleration schedule can provide a significant life saving in selected engine components.

Seismic stratigraphic architecture of the Disko Bay trough-mouth fan system, West Greenland

NASA Astrophysics Data System (ADS)

Hofmann, Julia C.; Knutz, Paul C.

2015-04-01

Spatial and temporal changes of the Greenland Ice Sheet on the continental shelf bordering Baffin Bay remain poorly constrained. Then as now, fast-flowing ice streams and outlet glaciers have played a key role for the mass balance and stability of polar ice sheets. Despite their significance for Greenland Ice Sheet dynamics and evolution, our understanding of their long-term behaviour is limited. The central West Greenland margin is characterized by a broad continental shelf where a series of troughs extend from fjords to the shelf margin, acting as focal points for trough-mouth fan (TMF) accummulations. The sea-ward bulging morphology and abrupt shelf-break of these major depositional systems is generated by prograding depocentres that formed during glacial maxima when ice streams reached the shelf edge, delivering large amounts of subglacial sediment onto the continental slope (Ó Cofaigh et al., 2013). The aim of this study is to unravel the seismic stratigraphic architecture and depositional processes of the Disko Bay TMF, aerially the largest single sedimentary system in West Greenland, using 2D and 3D seismic reflection data, seabed bathymetry and stratigraphic information from exploration well Hellefisk-1. The south-west Disko Bay is intersected by a deep, narrow trough, Egedesminde Dyb, which extends towards the southwest and links to the shallower and broader cross-shelf Disko Trough (maximum water depths of > 1000 m and a trough length of c. 370 km). Another trough-like depression (trough length of c. 120 km) in the northern part of the TMF, indicating a previous position of the ice stream, can be distinguished on the seabed topographic map and the seismic images. The Disko Bay TMF itself extends from the shelf edge down to the abyssal plain (abyssal floor depths of 2000 m) of the southern Baffin Bay. Based on seismic stratigraphic configurations relating to reflection terminations, erosive patterns and seismic facies (Mitchum et al., 1977), the TMF succession has been divided into five seismic units, each representing different stages in the progradational accumulation of the TMF system. This poster and ongoing study will discuss how the ice-stream flow switching is linked to changes in depocentres of sedimentary sequences and further investigate the major controls, e.g. ice-sheet dynamics, ocean-climate changes, tectonic forcing and subglacial geology, that determined the evolution of the Disko Bay TMF. Essencial bibliography Mitchum, R.M. Jr., Vail, P.R., Sangree, J.B., 1977. Seismic stratigraphy and global changes of sea level, Part 6: Stratigraphic interpretation of seismic reflection patterns in depositional sequences. AAPG Memoir 26, 117-133. Ó Cofaigh, C., Andrews, J.T., Jennings, A.E., Dowdeswell, J.A., Hogan, K.A., Kilfeather, A.A., Sheldon, C., 2013. Glacimarine lithofacies, provenance and depositional processes on a West Greenland trough-mouth fan. Journal of Quaternary Science, 28(1), 13-26.

Effect of Heat Treatment Process on Microstructure and Fatigue Behavior of a Nickel-Base Superalloy

PubMed Central

Zhang, Peng; Zhu, Qiang; Chen, Gang; Qin, Heyong; Wang, Chuanjie

2015-01-01

The study of fatigue behaviors for nickel-base superalloys is very significant because fatigue damage results in serious consequences. In this paper, two kinds of heat treatment procedures (Pro.I and Pro.II) were taken to investigate the effect of heat treatment on microstructures and fatigue behaviors of a nickel-base superalloy. Fatigue behaviors were studied through total strain controlled mode at 650 °C. Manson-Coffin relationship and three-parameter power function were used to predict fatigue life. A good link between the cyclic/fatigue behavior and microscopic studies was established. The cyclic deformation mechanism and fatigue mechanism were discussed. The results show that the fatigue resistance significantly drops with the increase of total strain amplitudes. Manson-Coffin relationship can well predict the fatigue life for total strain amplitude from 0.5% to 0.8%. The fatigue resistance is related with heat treatment procedures. The fatigue resistance performance of Pro.I is better than that of Pro.II. The cyclic stress response behaviors are closely related to the changes of the strain amplitudes. The peak stress of the alloy gradually increases with the increase of total strain amplitudes. The main fracture mechanism is inhomogeneous deformation and the different interactions between dislocations and γ′ precipitates. PMID:28793559

Reviews on factors affecting fatigue behavior of high-Mn steels

NASA Astrophysics Data System (ADS)

Kim, Sangshik; Jeong, Daeho; Sung, Hyokyung

2018-01-01

A variety of factors affect the fatigue behavior of high-Mn steels, which include both extrinsic (i.e., loading type, R ratio, specimen type, surface condition, temperature, and environment) and intrinsic (i.e., chemical composition, grain size, microstructure, stacking fault energy) factors. Very often, the influence of extrinsic factors on the fatigue behavior is even greater than that of intrinsic factors, misleading the interpretation of fatigue data. The metallurgical factors influence the initiation and propagation behaviors of fatigue by altering the characteristics of slip that is prerequisite for fatigue damage accumulation. It is however not easy to separate the effect of each factor since they affect the fatigue behavior of high-Mn steels in complex and synergistic way. In this review, the fatigue data of high-Mn steels are summarized and the factors complicating the interpretation are discussed.

Biaxial Fatigue Behavior of Niti Shape Memory Alloy

DTIC Science & Technology

2005-03-01

BIAXIAL FATIGUE BEHAVIOR OF NiTi SHAPE MEMORY ALLOY THESIS Daniel M. Jensen, 1st Lieutenant...BIAXIAL FATIGUE BEHAVIOR OF NiTi SHAPE MEMORY ALLOY THESIS Presented to the Faculty Department of Aeronautics and Astronautics Graduate School of...FOR PUBLIC RELEASE; DISTRIBUTION UNLIMITED AFIT/GA/ENY/05-M06 BIAXIAL FATIGUE BEHAVIOR OF NiTi SHAPE MEMORY ALLOY Daniel M. Jensen

Environmental Effects on Fatigue Behavior of Metals.

DTIC Science & Technology

1981-04-09

Growth Rate Behavior Above and Below KISCC in Steels ," Journal of Materials, Vol. 6, No. 4, 1971, pp. 941-964. 3. Barsom, J. M., " Corrosion -Fatigue...T., and Inoue, K., " Corrosion Fatigue Behavior of 13 Cr Stainless Steel in Sodium-Chloride Aqueous Solution and Steam Environment," Corrosion -Fatigue...34Effect of Environment on the Fatigue Behavior of a Medium Carbon Steel ," Corrosion , Vol. 30, 1974, pp. 280-284. 98. Karpenko, G. V., Romaniv, A. N., and

Review of Corrosion Fatigue.

DTIC Science & Technology

1981-11-16

other is not always well defined. 3.0 CORROSIM FATIGUE VARIABLES AND THEIR EFFECTS Corrosion fatigue behavior is pverned, y Ir of variables- environmental...on near threshold fatigue crack growth behavior is primarily a function of environmental reaction in this steel . 3.2 Mechanical Effects Among the...Gallagher""’ and Pao studied the corrosion fatigue behavior of 4340 steel at various * Ifrequencies in distilled water and water vapor, respectively

Simultaneous lidar observations of the water vapor and ozone signatures of a stratospheric intrusion during the MOHAVE-2009 campaign

NASA Astrophysics Data System (ADS)

Leblanc, T.; McDermid, I. S.; Pérot, K.

2010-12-01

Ozone and water vapor signatures of a stratospheric intrusion were simultaneously observed by the Jet Propulsion Laboratory lidars located at Table Mountain Facility, California (TMF, 34.4N, 117.7W) during the Measurements of Humidity in the Atmosphere and Validation Experiments (MOHAVE-2009) campaign in October 2009. These observations are placed in the context of the meridional displacement and folding of the tropopause, and resulting contrast in the properties of the air masses sampled by lidar. The lidar observations are supported by model data, specifically potential vorticity fields advected by the high-resolution transport model MIMOSA, and by 10-day backward isentropic trajectories. The ozone and water vapor anomalies measured by lidar were largely anti-correlated, and consistent with the assumption of a wet and ozone-poor subtropical upper troposphere, and a dry and ozone-rich extra-tropical lowermost stratosphere. However, it is shown that this anti-correlation relation collapsed just after the stratospheric intrusion event of October 20, suggesting mixed air embedded along the subtropical jet stream and sampled by lidar during its displacement south of TMF (tropopause fold). The ozone-PV expected positive correlation relation held strongly throughout the measurement period, including when a lower polar stratospheric filament passed over TMF just after the stratospheric intrusion. The numerous highly-correlated signatures observed during this event demonstrate the strong capability of the water vapor and ozone lidars at TMF, and provide new confidence in the future detection by lidar of long-term variability of water vapor and ozone in the Upper Troposphere-Lower Stratosphere (UTLS).

Stratospheric Ozone Climatology from Lidar Measurements at Table Mountain (34.0 deg N, 117.7 deg W) and Mauna Loa (19.5 deg N, 155.6 deg W)

NASA Technical Reports Server (NTRS)

Leblanc, T.; McDermid, I. S.

2000-01-01

Using more than 1600 nighttime profiles obtained by the JPL differential absorption lidars (DIAL) located at Table Mountain Facility (TMF, 34.4 N) and Mauna Loa Observatory (MLO, 19.5 N) is presented in this paper. These two systems have been providing high-resolution vertical profiles of ozone number density between 15-50 km, several nights a week since 1989 (TMF) and 1993 (MLO). The climatology presented here is typical of early night ozone values with only a small influence of the Pinatubo aerosols and the 11-year solar cycle. The observed seasonal and vertical structure of the ozone concentration at TMF is consistent with that typical of mid- to subtropical latitudes. A clear annual cycle in opposite phase below and above the ozone concentration peak is observed. The observed winter maximum below the ozone peak is associated with a maximum day-to-day variability, typical of a dynamically driven lower stratosphere. The maximum concentration observed in summer above the ozone peak emphasizes the more dominant role of photochemistry. Unlike TMF, the ozone concentration observed at MLO tends to be higher during the summer months and lower during the winter months throughout the entire stratospheric ozone layer. Only a weak signature of the extra-tropical latitudes is observed near 19-20 km, with a secondary maximum in late winter. The only large variability observed at MLO is associated with the natural variability of the tropical tropopause.

Fatigue Self-Management Behaviors in Patients With Advanced Cancer: A Prospective Longitudinal Survey.

PubMed

Chan, Raymond; Yates, Patsy; McCarthy, Alexandra L

2016-11-01

To explore the fatigue self-management behaviors and factors associated with effectiveness of these behaviors in patients with advanced cancer.
. Prospective longitudinal interviewer-administered survey.
. Royal Brisbane and Women's Hospital in Queensland, Australia.
. 152 outpatients with metastatic breast, lung, colorectal, and prostate cancer experiencing fatigue were recruited.
. Patients were surveyed on three occasions. Fatigue self-management behavior (perceived effectiveness, self-efficacy, and frequency), medical and demographic characteristics (sites of primary cancer and metastasis, comorbidity, performance status), social support, depression, anxiety, and other symptoms were assessed.
. The participants reported moderate levels of fatigue at baseline and maintained moderate levels at four and eight weeks. On average, participants consistently used about nine behaviors at each time point. Factors significantly associated with higher levels of perceived effectiveness of fatigue self-management behaviors were higher self-efficacy, higher education level, and lower levels of depressive symptoms. 
. The findings of this study demonstrate that patients with cancer, even those with advanced disease, still want and are able to use a number of behaviors to control their fatigue. Self-management interventions that aim to enhance self-efficacy and address any concurrent depressive symptoms have the potential to reduce fatigue severity.
. Nurses are well positioned to play a key role in supporting patients in their fatigue self-management.

Simulation of Fatigue Behavior of High Temperature Metal Matrix Composites

NASA Technical Reports Server (NTRS)

Tong, Mike T.; Singhal, Suren N.; Chamis, Christos C.; Murthy, Pappu L. N.

1996-01-01

A generalized relatively new approach is described for the computational simulation of fatigue behavior of high temperature metal matrix composites (HT-MMCs). This theory is embedded in a specialty-purpose computer code. The effectiveness of the computer code to predict the fatigue behavior of HT-MMCs is demonstrated by applying it to a silicon-fiber/titanium-matrix HT-MMC. Comparative results are shown for mechanical fatigue, thermal fatigue, thermomechanical (in-phase and out-of-phase) fatigue, as well as the effects of oxidizing environments on fatigue life. These results show that the new approach reproduces available experimental data remarkably well.

The relationships among health promotion behaviors, compassion fatigue, burnout, and compassion satisfaction in nurses practicing in a community medical center.

PubMed

Neville, Kathleen; Cole, Donna A

2013-06-01

The objective of this study was to examine the relationships among health promotion behaviors, compassion fatigue, burnout, and compassion satisfaction among nurses practicing in a community medical center. Compassion fatigue and burnout are significant nursing stressors. Programs are available to offset the negative consequence of compassion fatigue and burnout and enhance compassion satisfaction, yet there remains a paucity of literature examining the relationships between health promotion behaviors, compassion fatigue, burnout, and compassion satisfaction. A nonexperimental design using a convenience sample of nurses completed the Health Promoting Lifestyle Profile II, the Professional Quality of Life Scale, and a demographic data sheet. Statistically significant relationships among health promotional behaviors and compassion fatigue, compassion satisfaction, and burnout were identified. Compassion fatigue, burnout, and compassion satisfaction are outcomes associated with nursing practice. Support for engagement in health promotional behaviors may contribute to nurses' well-being in counteracting compassion fatigue and burnout and enhancing compassion satisfaction.

Fatigue and work safety behavior in men during early fatherhood.

PubMed

Mellor, Gary; St John, Winsome

2012-01-01

This study investigated the relationship between fatigue and work safety behavior of fathers with new babies. A total of 241 fathers completed a questionnaire at 6 and 12 weeks postpartum with items on fatigue and safety behavior at work. Results revealed that fathers worked long hours, reported a moderate-to-high physical intensity of work, and experienced interrupted sleep averaging less than 6 hours. Fathers also reported moderate fatigue at both 6 and 12 weeks postbirth, which was inversely related to safety behavior. Both fatigue and sleep history made a small but statistically significant contribution to safety behavior results at 6 and 12 weeks postbirth. Findings suggest that working fathers with babies experience fatigue during early fatherhood and are unable to recover due to interrupted and poor sleep patterns. Managers should consider the potential for fatigue to compromise work safety and develop risk management strategies that target new fathers.

Strain-cycling fatigue behavior of ten structural metals tested in liquid helium (4 K), in liquid nitrogen (78 K), and in ambient air (300 K)

NASA Technical Reports Server (NTRS)

Nachtigall, A. J.

1974-01-01

Strain-cycling fatigue behavior of 10 different structural alloys and metals was investigated in liquid helium (4 K), in liquid nitrogen (78 K), and in ambient air (300 K). At high cyclic lives, fatigue resistance increased with decreasing temperature for all the materials investigated. At low cyclic lives, fatigue resistance generally decreased with decreasing temperature for the materials investigated. Only for Inconel 718 did fatigue resistance increase with decreasing temperature over the entire life range investigated. Comparison of the experimental fatigue behavior with that predicted by the Manson method of universal slopes showed that the fatigue behavior of these materials can be predicted for cryogenic temperatures by using material tensile properties obtained at those same temperatures.

Association of fatigue with emotional-eating behavior and the response to mental stress in food intake in a young adult population.

PubMed

Yoshikawa, Takahiro; Tanaka, Masaaki; Ishii, Akira; Watanabe, Yasuyoshi

2014-01-01

Fatigue is a common complaint among young adults. We investigated whether eating behaviors are associated with fatigue in this population. The participants consisted of 117 healthy students attending Osaka City University. They completed questionnaires assessing fatigue and eating behaviors. To identify the factors associated with the prevalence of fatigue, multivariate logistic regression analysis adjusted for gender was performed. The Emotional Eating subscale score of the Japanese version of Three-Factor Eating Questionnaire Revised 21-item and stress response in food intake (large decrease vs. no change) were positively associated with the prevalence of fatigue assessed by the Japanese version of the Chalder Fatigue Scale. The finding suggests that emotional eating and decrease in amount of food intake under mental stress were associated with fatigue in healthy young adults. Our findings may help to clarify the mechanisms underlying fatigue-eating coupling as well as the etiology of diseases related to abnormal eating behavior.

Polarization recovery in lead zirconate titanate thin films deposited on nanosheets-buffered Si (001)

NASA Astrophysics Data System (ADS)

Chopra, Anuj; Bayraktar, Muharrem; Nijland, Maarten; ten Elshof, Johan E.; Bijkerk, Fred; Rijnders, Guus

2016-12-01

Fatigue behavior of Pb(Zr,Ti)O3 (PZT) films is one of the deterrent factors that limits the use of these films in technological applications. Thus, understanding and minimization of the fatigue behavior is highly beneficial for fabricating reliable devices using PZT films. We have investigated the fatigue behavior of preferentially oriented PZT films deposited on nanosheets-buffered Si substrates using LaNiO3 bottom and top electrodes. The films show fatigue of up to 10% at 100 kHz, whereas no fatigue has been observed at 1 MHz. This frequency dependence of the fatigue behavior is found to be in accordance with Dawber-Scott fatigue model that explains the origin of the fatigue as migration of oxygen vacancies. Interestingly, a partial recovery of remnant polarization up to ˜97% of the maximum value is observed after 4×109 cycles which can be further extended to full recovery by increasing the applied electric field. This full recovery is qualitatively explained using kinetic approach as a manifestation of depinning of domains walls. The understanding of the fatigue behavior and polarization recovery that is explained in this paper can be highly useful in developing more reliable PZT devices.

Fatigue Behavior of Steel Fiber Reinforced High-Strength Concrete under Different Stress Levels

NASA Astrophysics Data System (ADS)

Zhang, Chong; Gao, Danying; Gu, Zhiqiang

2017-12-01

The investigation was conducted to study the fatigue behavior of steel fiber reinforced high-strength concrete (SFRHSC) beams. A series of 5 SFRHSC beams was conducted flexural fatigue tests at different stress level S of 0.5, 0.55, 0.6, 0.7 and 0.8 respectively. Static test was conducted to determine the ultimate static capacity prior to fatigue tests. Fatigue modes and S-N curves were analyzed. Besides, two fatige life prediction model were analyzed and compared. It was found that stress level S significantly influenced the fatigue life of SFRHSC beams and the fatigue behavior of SFRHSC beams was mainly determined by the tensile reinforcement.

Cumulative fatigue damage behavior of MAR M-247

NASA Technical Reports Server (NTRS)

Mcgaw, Michael A.; Halford, Gary R.; Kalluri, Sreeramesh

1991-01-01

The objective was to examine the room temperature fatigue and nonlinear cumulative fatigue damage behavior of the cast nickel-based superalloy, MAR M-247. The fatigue test matrix consisted of single-level, fully reversed fatigue experiments. Two series of tests were performed: one of the two baseline fatigue LCF (Low-Cycle Fatigue) life levels was used in the first loading block, and the HCF (High-Cycle Fatigue) baseline loading level was used in the second block in each series. For each series, duplicate tests were performed at each applied LCF life fraction.

Influence of shear cutting parameters on the fatigue behavior of a dual-phase steel

NASA Astrophysics Data System (ADS)

Paetzold, I.; Dittmann, F.; Feistle, M.; Golle, R.; Haefele, P.; Hoffmann, H.; Volk, W.

2017-09-01

The influence of the edge condition of car body and chassis components made of steel sheet on fatigue behavior under dynamic loading presents a major challenge for automotive manufacturers and suppliers. The calculated lifetime is based on material data determined by the fatigue testing of specimens with polished edges. Prototype components are often manufactured by milling or laser cutting, whereby in practice, the series components are produced by shear cutting due to its cost-efficiency. Since the fatigue crack in such components usually starts from a shear cut edge, the calculated and experimental determined lifetime will vary due to the different conditions at the shear cut edges. Therefore, the material data determined with polished edges can result in a non-conservative component design. The aim of this study is to understand the relationship between the shear cutting process and the fatigue behavior of a dual-phase steel sheet. The geometry of the shear cut edge as well as the depth and degree of work hardening in the shear affected zone can be adjusted by using specific shear cutting parameters, such as die clearance and cutting edge radius. Stress-controlled fatigue tests of unnotched specimens were carried out to compare the fatigue behavior of different edge conditions. By evaluating the results of the fatigue experiments, influential shear cutting parameters on fatigue behavior were identified. It was possible to assess investigated shear cutting strategies regarding the fatigue behavior of a high-strength steel DP800.

An overview of the Galileo Optical Experiment (GOPEX)

NASA Technical Reports Server (NTRS)

Wilson, K. E.; Lesh, J. R.

1993-01-01

Uplink optical communication to a deep-space vehicle was demonstrated. In the Galileo Optical Experiment (GOPEX), optical transmissions were beamed to the Galileo spacecraft by Earth-based transmitters at the Table Mountain Facility (TMF), California, and Starfire Optical Range (SOR), New Mexico. The demonstration took place over an eight-day period (9 Dec. through 16 Dec. 1992) as Galileo receded from Earth on its way to Jupiter, and covered ranges from 1-6 million km. At 6 million km (15 times the Earth-Moon distance), the laser beam transmitted from TMF eight days after Earth flyby covered the longest known range for transmission and detection.

Lorentz Body Force Induced by Traveling Magnetic Fields

NASA Technical Reports Server (NTRS)

Volz, M. P.; Mazuruk, K.

2003-01-01

The Lorentz force induced by a traveling magnetic field (TMF) in a cylindrical container has been calculated. The force can be used to control flow in dectrically conducting melts and the direction of the magnetic field and resulting flow can be reversed. A TMF can be used to partially cancel flow driven by buoyancy. The penetration of the field into the cylinder decreases as the frequency increases, and there exists an optimal value of frequency for which the resulting force is a maximum. Expressions for the Lorentz force in the limiting cases of low frequency and infinite cylinder are also given and compared to the numerical calculations.

Investigating the Geochemical Model for Molybdenum Mineralization in the JEB Tailings Management Facility at McClean Lake, Saskatchewan: An X-ray Absorption Spectroscopy Study.

PubMed

Blanchard, Peter E R; Hayes, John R; Grosvenor, Andrew P; Rowson, John; Hughes, Kebbi; Brown, Caitlin

2015-06-02

The geochemical model for Mo mineralization in the JEB Tailings Management Facility (JEB TMF), operated by AREVA Resources Canada at McClean Lake, Saskatchewan, was investigated using X-ray Absorption Near-Edge Spectroscopy (XANES), an elemental-specific technique that is sensitive to low elemental concentrations. Twenty five samples collected during the 2013 sampling campaign from various locations and depths in the TMF were analyzed by XANES. Mo K-edge XANES analysis indicated that the tailings consisted primarily of Mo(6+) species: powellite (CaMoO4), ferrimolybdite (Fe2(MoO4)3·8H2O), and molybdate adsorbed on ferrihydrite (Fe(OH)3 - MoO4). A minor concentration of a Mo(4+) species in the form of molybdenite (MoS2) was also present. Changes in the Mo mineralization over time were inferred by comparing the relative amounts of the Mo species in the tailings to the independently measured aqueous Mo pore water concentration. It was found that ferrimolybdite and molybdate adsorbed on ferrihydrite initially dissolves in the TMF and precipitates as powellite.

Causes and consequences of fatigue in rheumatoid arthritis.

PubMed

Katz, Patricia

2017-05-01

To review current information on the causes, treatments, and consequences of fatigue in rheumatoid arthritis. Disease activity (inflammation, pain, joint symptoms) is associated with greater fatigue. However, disease activity per se accounts for only a small portion of fatigue, and rheumatoid arthritis medications that reduce disease activity have small effects on fatigue. Instead, factors outside the direct effects of rheumatoid arthritis, such as obesity, physical inactivity, sleep disturbance, and depression, explain the majority of variation in fatigue. Some of these factors may be indirect effects of disease (e.g. pain can lead to sleep disturbance). Rheumatoid arthritis has significant effects on the quality of life of individuals with rheumatoid arthritis. The most effective approaches to reducing rheumatoid arthritis fatigue appear to be behavioral, such as increasing physical activity, or cognitive, such as cognitive behavioral interventions. Fatigue in rheumatoid arthritis appears to be largely because of factors outside the direct effects of the disease, such as behavioral and psychological factors. In spite of the tremendous impact of fatigue on patient health and quality of life, effective treatments remain elusive, but existing data show that behavioral and cognitive approaches may be most effective.

Effect of biomimetic non-smooth unit morphology on thermal fatigue behavior of H13 hot-work tool steel

NASA Astrophysics Data System (ADS)

Meng, Chao; Zhou, Hong; Cong, Dalong; Wang, Chuanwei; Zhang, Peng; Zhang, Zhihui; Ren, Luquan

2012-06-01

The thermal fatigue behavior of hot-work tool steel processed by a biomimetic coupled laser remelting process gets a remarkable improvement compared to untreated sample. The 'dowel pin effect', the 'dam effect' and the 'fence effect' of non-smooth units are the main reason of the conspicuous improvement of the thermal fatigue behavior. In order to get a further enhancement of the 'dowel pin effect', the 'dam effect' and the 'fence effect', this study investigated the effect of different unit morphologies (including 'prolate', 'U' and 'V' morphology) and the same unit morphology in different sizes on the thermal fatigue behavior of H13 hot-work tool steel. The results showed that the 'U' morphology unit had the optimum thermal fatigue behavior, then the 'V' morphology which was better than the 'prolate' morphology unit; when the unit morphology was identical, the thermal fatigue behavior of the sample with large unit sizes was better than that of the small sizes.

A literature review and inventory of the effects of environment on the fatigue behavior of metals

NASA Technical Reports Server (NTRS)

Hudson, C. M.; Seward, S. K.

1976-01-01

The current state of knowledge of the effects of gas environments (at atmospheric pressure and below) on the fatigue behavior of metals is reviewed. Among the topics considered are the mechanisms proposed to explain the differences observed in the fatigue behavior of vacuum- and air-tested specimens, the effects of environment on the surface topography of fatigue cycled specimens, the effect of environment on the various phases of the fatigue phenomenon, the effect of prolonged exposure to vacuum on fatigue life, the variation of fatigue life with decreasing gas pressure, and gas evolution during fatigue cycling. Analysis of the findings of this review indicates that hydrogen embrittlement is primarily responsible for decreased fatigue resistance in humid environments, and that dislocations move more easily during tests in vacuum than during test in air. It was found that fatigue cracks generally initiated and propagated more rapidly in air than in vacuum. Prolonged exposure to vacuum does not adversely affect fatigue resistance. The variation of fatigue life with decreasing gas pressure is sometimes stepped and sometimes continuous.

Structure-property relations and modeling of small crack fatigue behavior of various magnesium alloys

NASA Astrophysics Data System (ADS)

Bernard, Jairus Daniel

Lightweight structural components are important to the automotive and aerospace industries so that better fuel economy can be realized. Magnesium alloys in particular are being examined to fulfill this need due to their attractive stiffness- and strength-to-weight ratios when compared to other materials. However, when introducing a material into new roles, one needs to properly characterize its mechanical properties. Fatigue behavior is especially important considering aerospace and automotive component applications. Therefore, quantifying the structure-property relationships and accurately predicting the fatigue behavior for these materials are vital. This study has two purposes. The first is to quantify the structure-property relationships for the fatigue behavior in an AM30 magnesium alloy. The second is to use the microstructural-based MultiStage Fatigue (MSF) model in order to accurately predict the fatigue behavior of three magnesium alloys: AM30, Elektron 21, and AZ61. While some studies have previously quantified the MSF material constants for several magnesium alloys, detailed research into the fatigue regimes, notably the microstructurally small crack (MSC) region, is lacking. Hence, the contribution of this work is the first of its kind to experimentally quantify the fatigue crack incubation and MSC regimes that are used for the MultiStage Fatigue model. Using a multi-faceted experimental approach, these regimes were explored with a replica method that used a dual-stage silicone based compound along with previously published in situ fatigue tests. These observations were used in calibrating the MultiStage Fatigue model.

Taltirelin alleviates fatigue-like behavior in mouse models of cancer-related fatigue.

PubMed

Dougherty, John P; Wolff, Brian S; Cullen, Mary J; Saligan, Leorey N; Gershengorn, Marvin C

2017-10-01

Fatigue affects most cancer patients and has numerous potential causes, including cancer itself and cancer treatment. Cancer-related fatigue (CRF) is not relieved by rest, can decrease quality of life, and has no FDA-approved therapy. Thyrotropin-releasing hormone (TRH) has been proposed as a potential novel treatment for CRF, but its efficacy against CRF remains largely untested. Thus, we tested the TRH analog, taltirelin (TAL), in mouse models of CRF. To model fatigue, we used a mouse model of chemotherapy, a mouse model of radiation therapy, and mice bearing colon 26 carcinoma tumors. We used the treadmill fatigue test to assess fatigue-like behavior after treatment with TAL. Additionally, we used wild-type and TRH receptor knockout mice to determine which TRH receptor was necessary for the actions of TAL. Tumor-bearing mice displayed muscle wasting and all models caused fatigue-like behavior, with mice running a shorter distance in the treadmill fatigue test than controls. TAL reversed fatigue-like behavior in all three models and the mouse TRH 1 receptor was necessary for the effects of TAL. These data suggest that TAL may be useful in alleviating fatigue in all cancer patients and provide further support for evaluating TAL as a potential therapy for CRF in humans. Published by Elsevier Ltd.

Fluoxetine prevents the development of depressive-like behavior in a mouse model of cancer related fatigue.

PubMed

Norden, Diana M; Devine, Raymond; Bicer, Sabahattin; Jing, Runfeng; Reiser, Peter J; Wold, Loren E; Godbout, Jonathan P; McCarthy, Donna O

2015-03-01

Cancer patients frequently suffer from fatigue, a complex syndrome associated with tiredness and depressed mood. Cancer-related fatigue (CRF) can be present at the time of diagnosis, escalates during treatment, and can persist for years after treatment. CRF negatively influences quality of life, limits functional independence, and is associated with decreased survival in patients with incurable disease. We have previously shown that increased pro-inflammatory cytokine expression in the brain contributes to depressive- and fatigue-like behaviors in a mouse model of CRF. Inflammatory cytokines increase the activity of indoleamine 2,3-dioxygenase (IDO) and kynurenine 3-monooxygenase (KMO), which competitively reduce serotonin synthesis. Reduced serotonin availability in the brain and increased production of alternative neuroactive metabolites of tryptophan are thought to contribute to the development of depression and fatigue. The purpose of this study was to determine the effects of fluoxetine, a selective serotonin reuptake inhibitor (SSRI), on brain cytokines and behavioral measures of fatigue and depression in tumor-bearing mice. Here we show that tumor growth increased brain expression of pro-inflammatory cytokines and KMO. Treatment with fluoxetine had no effect on tumor growth, muscle wasting, fatigue behavior, or cytokine expression in the brain. Fluoxetine, however, reduced depressive-like behaviors in tumor bearing mice. In conclusion, our data confirm that increased brain expression of pro-inflammatory cytokines is associated with tumor-induced fatigue- and depressive-like behaviors. However, it is possible to separate the effects of tumor growth on mood and fatigue-like behaviors using SSRIs such as fluoxetine. Copyright © 2014 Elsevier Inc. All rights reserved.

Happy Now, Tired Later? Extraverted and Conscientious Behavior Are Related to Immediate Mood Gains, but to Later Fatigue.

PubMed

Leikas, Sointu; Ilmarinen, Ville-Juhani

2017-10-01

Experience sampling studies on Big Five-related behavior show that people display the whole spectrum of each trait in their daily behavior, and that desirable Big Five states-especially state Extraversion-are related to positive mood. However, other research lines suggest that extraverted and conscientious behavior may be mentally depleting. The present research examined this possibility by extending the time frame of the measured personality processes. A 12-day experience sampling study (N = 48; observations = 2,328) measured Big Five states, mood, stress, and fatigue five times a day. Extraverted and conscientious behavior were concurrently related to positive mood and lower fatigue, but to higher fatigue after a 3-hour delay. These relations were not moderated by personality traits. The relation between extraverted behavior and delayed fatigue was mediated by the number of people the person had encountered. Whether the person had a goal mediated the relation between conscientious behavior and delayed fatigue. Extraverted and conscientious behavior predict mental depletion after a 3-hour delay. The results help reconcile previous findings regarding the consequences of state Extraversion and provide novel information about the consequences of state Conscientiousness. © 2016 Wiley Periodicals, Inc.

Analysis of methods for determining high cycle fatigue strength of a material with investigation of titanium-aluminum-vanadium gigacycle fatigue behavior

NASA Astrophysics Data System (ADS)

Pollak, Randall D.

Today, aerospace engineers still grapple with the qualitative and quantitative understanding of fatigue behavior in the design and testing of turbine-driven jet engines. The Department of Defense has taken a very active role in addressing this problem with the formation of the National High Cycle Fatigue Science & Technology Program in 1994. The primary goal of this program is to further the understanding of high cycle fatigue (HCF) behavior and develop methods in order to mitigate the negative impact of HCF on aerospace operations. This research supports this program by addressing the fatigue strength testing guidance currently provided by the DoD to engine manufacturers, with the primary goal to investigate current methods and recommend a test strategy to characterize the fatigue strength of a material at a specified number of cycles, such as the 109 design goal specified by MIL-HDBK-1783B, or range of cycles. The research utilized the benefits of numerical simulation to initially investigate the staircase method for use in fatigue strength testing. The staircase method is a commonly used fatigue strength test, but its ability to characterize fatigue strength variability is extremely suspect. A modified staircase approach was developed and shown to significantly reduce bias and scatter in estimates for fatigue strength variance. Experimental validation of this proposed test strategy was accomplished using a dual-phase Ti-6Al-4V alloy. The HCF behavior of a second material with a very different microstructure (beta annealed Ti-6Al-4V) was also investigated. The random fatigue limit (RFL) model, a recently developed analysis tool, was investigated to characterize stress-life behavior but found to have difficulty representing fatigue life curves with sharp transitions. Two alternative models (bilinear and hyperbolic) were developed based on maximum likelihood methods to better characterize the Ti-6Al-4V fatigue life behavior. These models provided a good fit to the experimental data for the dual-phase Ti-6Al-4V and were applied to the beta annealed variant in order to estimate stress-life behavior using a small-sample approach. Based on this research, designers should be better able to make reliable estimates of fatigue strength parameters using small-sample testing.

Fatigue Behavior and the Relationship Between Crack Propagation and the Slit Configuration of C/c Composites

NASA Astrophysics Data System (ADS)

Ferdous, Md. Shafiul; Setyabudi, Sofyan Arief; Makabe, Chobin; Fujikawa, Masaki

2013-05-01

The fatigue and fracture behavior of C/C composites fabricated using fine-woven carbon fiber laminates with α = 0/90° direction were investigated. Also, the phenomenon of crack growth behavior and the shear damage in the fiber bundle was discussed. Slits of several sizes were cut on both sides of a test section and different sizes of slit length were chosen. The effect of the slit configuration on crack initiation and growth behavior was observed. Specimens with blunt-notches and center-holes were also used to compare the fatigue strength and crack growth behavior. Non-propagating cracks were observed and fatigue limit was defined as the maximum stress at which specimen did not break for N = 107 cycles stress application. The longest fatigue life was obtained in the case of specimens with shorter slits. The relationships between fatigue strengths and specimen shapes were analyzed by stress concentration, Kt, and stress intensity factor, KI. The effect of slit configuration on fatigue strength was then discussed regarding both the experimental and calculated consequences.

Effects of fine porosity on the fatigue behavior of a powder metallurgy superalloy

NASA Technical Reports Server (NTRS)

Miner, R. V.; Dreshfield, R. L.

1980-01-01

Hot-isostatically-pressed powder-metallurgy Astroloy was obtained which contained 1.4 percent porosity at the grain boundaries produced by argon entering the powder container during pressing. This material was tested at 650 C in fatigue, creep-fatigue, tension, and stress-rupture and the results compared with data on sound Astroloy. They influenced fatigue crack initiation and produced a more intergranular mode of propagation but fatigue life was not drastically reduced. Fatigue behavior of the porous material showed typical correlation with tensile behavior. The plastic strain range-life relation was reduced proportionately with the reduction in tensile ductility, but the elastic strain range-life relation was changed little.

The fatigue life prediction of aluminium alloy using genetic algorithm and neural network

NASA Astrophysics Data System (ADS)

Susmikanti, Mike

2013-09-01

The behavior of the fatigue life of the industrial materials is very important. In many cases, the material with experiencing fatigue life cannot be avoided, however, there are many ways to control their behavior. Many investigations of the fatigue life phenomena of alloys have been done, but it is high cost and times consuming computation. This paper report the modeling and simulation approaches to predict the fatigue life behavior of Aluminum Alloys and resolves some problems of computation. First, the simulation using genetic algorithm was utilized to optimize the load to obtain the stress values. These results can be used to provide N-cycle fatigue life of the material. Furthermore, the experimental data was applied as input data in the neural network learning, while the samples data were applied for testing of the training data. Finally, the multilayer perceptron algorithm is applied to predict whether the given data sets in accordance with the fatigue life of the alloy. To achieve rapid convergence, the Levenberg-Marquardt algorithm was also employed. The simulations results shows that the fatigue behaviors of aluminum under pressure can be predicted. In addition, implementation of neural networks successfully identified a model for material fatigue life.

Thermal Fatigue and Fracture Behavior of Ceramic Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Zhu, Dong-Ming; Choi, Sung R.; Miller, Robert A.

2001-01-01

Thermal fatigue and fracture behavior of plasma-sprayed ceramic thermal barrier coatings has been investigated under high heat flux and thermal cyclic conditions. The coating crack propagation is studied under laser heat flux cyclic thermal loading, and is correlated with dynamic fatigue and strength test results. The coating stress response and inelasticity, fatigue and creep interactions, and interface damage mechanisms during dynamic thermal fatigue processes are emphasized.

Fatigue Assessment of Nickel-Titanium Peripheral Stents: Comparison of Multi-Axial Fatigue Models

NASA Astrophysics Data System (ADS)

Allegretti, Dario; Berti, Francesca; Migliavacca, Francesco; Pennati, Giancarlo; Petrini, Lorenza

2018-03-01

Peripheral Nickel-Titanium (NiTi) stents exploit super-elasticity to treat femoropopliteal artery atherosclerosis. The stent is subject to cyclic loads, which may lead to fatigue fracture and treatment failure. The complexity of the loading conditions and device geometry, coupled with the nonlinear material behavior, may induce multi-axial and non-proportional deformation. Finite element analysis can assess the fatigue risk, by comparing the device state of stress with the material fatigue limit. The most suitable fatigue model is not fully understood for NiTi devices, due to its complex thermo-mechanical behavior. This paper assesses the fatigue behavior of NiTi stents through computational models and experimental validation. Four different strain-based models are considered: the von Mises criterion and three critical plane models (Fatemi-Socie, Brown-Miller, and Smith-Watson-Topper models). Two stents, made of the same material with different cell geometries are manufactured, and their fatigue behavior is experimentally characterized. The comparison between experimental and numerical results highlights an overestimation of the failure risk by the von Mises criterion. On the contrary, the selected critical plane models, even if based on different damage mechanisms, give a better fatigue life estimation. Further investigations on crack propagation mechanisms of NiTi stents are required to properly select the most reliable fatigue model.

Fatigue Assessment of Nickel-Titanium Peripheral Stents: Comparison of Multi-Axial Fatigue Models

NASA Astrophysics Data System (ADS)

Allegretti, Dario; Berti, Francesca; Migliavacca, Francesco; Pennati, Giancarlo; Petrini, Lorenza

2018-02-01

Peripheral Nickel-Titanium (NiTi) stents exploit super-elasticity to treat femoropopliteal artery atherosclerosis. The stent is subject to cyclic loads, which may lead to fatigue fracture and treatment failure. The complexity of the loading conditions and device geometry, coupled with the nonlinear material behavior, may induce multi-axial and non-proportional deformation. Finite element analysis can assess the fatigue risk, by comparing the device state of stress with the material fatigue limit. The most suitable fatigue model is not fully understood for NiTi devices, due to its complex thermo-mechanical behavior. This paper assesses the fatigue behavior of NiTi stents through computational models and experimental validation. Four different strain-based models are considered: the von Mises criterion and three critical plane models (Fatemi-Socie, Brown-Miller, and Smith-Watson-Topper models). Two stents, made of the same material with different cell geometries are manufactured, and their fatigue behavior is experimentally characterized. The comparison between experimental and numerical results highlights an overestimation of the failure risk by the von Mises criterion. On the contrary, the selected critical plane models, even if based on different damage mechanisms, give a better fatigue life estimation. Further investigations on crack propagation mechanisms of NiTi stents are required to properly select the most reliable fatigue model.

Fatigue Crack Growth Behavior of Gas Metal Arc Welded AISI 409 Grade Ferritic Stainless Steel Joints

NASA Astrophysics Data System (ADS)

Lakshminarayanan, A. K.; Shanmugam, K.; Balasubramanian, V.

2009-10-01

The effect of filler metals such as austenitic stainless steel, ferritic stainless steel, and duplex stainless steel on fatigue crack growth behavior of the gas metal arc welded ferritic stainless steel joints was investigated. Rolled plates of 4 mm thickness were used as the base material for preparing single ‘V’ butt welded joints. Center cracked tensile specimens were prepared to evaluate fatigue crack growth behavior. Servo hydraulic controlled fatigue testing machine with a capacity of 100 kN was used to evaluate the fatigue crack growth behavior of the welded joints. From this investigation, it was found that the joints fabricated by duplex stainless steel filler metal showed superior fatigue crack growth resistance compared to the joints fabricated by austenitic and ferritic stainless steel filler metals. Higher yield strength and relatively higher toughness may be the reasons for superior fatigue performance of the joints fabricated by duplex stainless steel filler metal.

Experimental Investigation and Finite Element Analysis on Fatigue Behavior of Aluminum Alloy 7050 Single-Lap Joints

NASA Astrophysics Data System (ADS)

Zhou, Bing; Cui, Hao; Liu, Haibo; Li, Yang; Liu, Gaofeng; Li, Shujun; Zhang, Shangzhou

2018-03-01

The fatigue behavior of single-lap four-riveted aluminum alloy 7050 joints was investigated by using high-frequency fatigue test and scanning electron microscope (SEM). Stress distributions obtained by finite element (FE) analysis help explain the fatigue performance. The fatigue test results showed that the fatigue lives of the joints depend on cold expansion and applied cyclic loads. FE analysis and fractography indicated that the improved fatigue lives can be attributed to the reduction in maximum stress and evolution of fatigue damage at the critical location. The beneficial effects of strengthening techniques result in tearing ridges or lamellar structure on fracture surface, decrease in fatigue striations spacing, delay of fatigue crack initiation, crack deflection in fatigue crack propagation and plasticity-induced crack closure.

Fatigue Behavior of Inconel 718 TIG Welds

NASA Astrophysics Data System (ADS)

Alexopoulos, Nikolaos D.; Argyriou, Nikolaos; Stergiou, Vasillis; Kourkoulis, Stavros K.

2014-08-01

Mechanical behavior of reference and TIG-welded Inconel 718 specimens was examined in the present work. Tensile, constant amplitude fatigue, and fracture toughness tests were performed in ambient temperature for both, reference and welded specimens. Microstructure revealed the presence of coarse and fine-grained heat-affected zones. It has been shown that without any post-weld heat treatment, welded specimens maintained their tensile strength properties while their ductility decreased by more than 40%. It was found that the welded specimens had lower fatigue life and this decrease was a function of the applied fatigue maximum stress. A 30% fatigue life decrease was noticed in the high cycle fatigue regime for the welded specimens while this decrease exceeded 50% in the low cycle fatigue regime. Cyclic stress-strain curves showed that Inconel 718 experiences a short period of hardening followed by softening for all fatigue lives. Cyclic fatigue response of welded specimens' exhibited cyclically stable behavior. Finally, a marginal decrease was noticed in the Mode I fracture toughness of the welded specimens.

Life-Extending Control for Aircraft Engines Studied

NASA Technical Reports Server (NTRS)

Guo, Te-Huei

2002-01-01

Current aircraft engine controllers are designed and operated to provide both performance and stability margins. However, the standard method of operation results in significant wear and tear on the engine and negatively affects the on-wing life--the time between cycles when the engine must be physically removed from the aircraft for maintenance. The NASA Glenn Research Center and its industrial and academic partners have been working together toward a new control concept that will include engine life usage as part of the control function. The resulting controller will be able to significantly extend the engine's on-wing life with little or no impact on engine performance and operability. The new controller design will utilize damage models to estimate and mitigate the rate and overall accumulation of damage to critical engine parts. The control methods will also provide a means to assess tradeoffs between performance and structural durability on the basis of mission requirements and remaining engine life. Two life-extending control methodologies were studied to reduce the overall life-cycle cost of aircraft engines. The first methodology is to modify the baseline control logic to reduce the thermomechanical fatigue (TMF) damage of cooled stators during acceleration. To accomplish this, an innovative algorithm limits the low-speed rotor acceleration command when the engine has reached a threshold close to the requested thrust. This algorithm allows a significant reduction in TMF damage with only a very small increase in the rise time to reach the commanded rotor speed. The second methodology is to reduce stress rupture/creep damage to turbine blades and uncooled stators by incorporating an engine damage model into the flight mission. Overall operation cost is reduced by an optimization among the flight time, fuel consumption, and component damages. Recent efforts have focused on applying life-extending control technology to an existing commercial turbine engine, and doing so without modifying the hardware or adding sensors. This approach makes it possible to retrofit existing engines with life-extending control technology by changing only the control software in the full-authority digital engine controller (FADEC). The significant results include demonstrating a 20- to 30-percent reduction in TMF damage to the hot section by developing and implementing smart acceleration logic during takeoff. The tradeoff is an increase, from 5.0 to 5.2 sec, in the time required to reach maximum power from ground idle. On a typical flight profile of a cruise at Mach 0.8 at an altitude of 41,000 ft, and cruise time of 104 min, the optimized system showed that a reduction in cruise speed from Mach 0.8 to 0.79 can achieve an estimated 25-to 35-percent creep/rupture damage reduction in the engine's hot section and a fuel savings of 2.1 percent. The tradeoff is an increase in flight time of 1.3 percent (1.4 min).

Isothermal fatigue behavior of a (90)(sub 8) SiC/Ti-15-3 composite at 426 C

NASA Technical Reports Server (NTRS)

Gayda, John; Gabb, Timothy P.

1991-01-01

The transverse fatigue behavior of a unidirectional, SiC/Ti-15-3 composite (35 v/o SiC, (90)(sub 8)) was evaluated at 426 C. The fatigue behavior of the composite along the fiber direction (0)(sub 8) and of unreinforced Ti-15-3 alloy were also studied for comparison purposes. The (90)(sub 8) composite fatigue life was much shorter then (0)(sub 8) life. Further, (90)(sub 8) fatigue life was also found to be far lower than that of the unreinforced Ti-15-3 alloys. A simple one-dimensional model for (90)(sub 8) fatigue behavior indicated that the short life of the composite in this orientation resulted, in large part, from weak fiber-matrix bond strength. This conclusion was supported by fractographic evidence showing numerous initiation sites along the fiber-matrix interfaces.

Effect of Pre-Strain on the Fatigue Behavior of Extruded AZ31 Alloys

NASA Astrophysics Data System (ADS)

Wu, Yanjun

2017-09-01

An attempt is made to rationalize the effect of pre-strain history on fatigue behaviors of AZ31 magnesium alloy. Axial fatigue tests were conducted in the extruded and pre-compressioned AZ31 alloy under low cycle total strain control fatigue conditions. The pre-strain process influences the plastic deformation mechanism activated during fatigue deformation, especially during tensile loading, by enhancing the activity of detwinning mechanism. The low-cycle fatigue lifetime of extruded AZ31 alloy can be enhanced by the pre-compression process. And the hysteresis energy was successfully used to predict the low-cycle fatigue lifetime.

Fatigue crack growth and low cycle fatigue of two nickel base superalloys

NASA Technical Reports Server (NTRS)

Stoloff, N. S.; Duquette, D. J.; Choe, S. J.; Golwalkar, S.

1983-01-01

The fatigue crack growth and low cycle fatigue behavior of two P/M superalloys, Rene 95 and Astroloy, in the hot isostatically pressed (HIP) condition, was determined. Test variables included frequency, temperature, environment, and hold times at peak tensile loads (or strains). Crack initiation sites were identified in both alloys. Crack growth rates were shown to increase in argon with decreasing frequency or with the imposition of hold times. This behavior was attributed to the effect of oxygen in the argon. Auger analyses were performed on oxide films formed in argon. Low cycle fatigue lives also were degraded by tensile hold, contrary to previous reports in the literature. The role of environment in low cycle fatigue behavior is discussed.

The compensatory interaction between motor unit firing behavior and muscle force during fatigue

PubMed Central

De Luca, Carlo J.; Kline, Joshua C.

2016-01-01

Throughout the literature, different observations of motor unit firing behavior during muscle fatigue have been reported and explained with varieties of conjectures. The disagreement amongst previous studies has resulted, in part, from the limited number of available motor units and from the misleading practice of grouping motor unit data across different subjects, contractions, and force levels. To establish a more clear understanding of motor unit control during fatigue, we investigated the firing behavior of motor units from the vastus lateralis muscle of individual subjects during a fatigue protocol of repeated voluntary constant force isometric contractions. Surface electromyographic decomposition technology provided the firings of 1,890 motor unit firing trains. These data revealed that to sustain the contraction force as the muscle fatigued, the following occurred: 1) motor unit firing rates increased; 2) new motor units were recruited; and 3) motor unit recruitment thresholds decreased. Although the degree of these adaptations was subject specific, the behavior was consistent in all subjects. When we compared our empirical observations with those obtained from simulation, we found that the fatigue-induced changes in motor unit firing behavior can be explained by increasing excitation to the motoneuron pool that compensates for the fatigue-induced decrease in muscle force twitch reported in empirical studies. Yet, the fundamental motor unit control scheme remains invariant throughout the development of fatigue. These findings indicate that the central nervous system regulates motor unit firing behavior by adjusting the operating point of the excitation to the motoneuron pool to sustain the contraction force as the muscle fatigues. PMID:27385798

The compensatory interaction between motor unit firing behavior and muscle force during fatigue.

PubMed

Contessa, Paola; De Luca, Carlo J; Kline, Joshua C

2016-10-01

Throughout the literature, different observations of motor unit firing behavior during muscle fatigue have been reported and explained with varieties of conjectures. The disagreement amongst previous studies has resulted, in part, from the limited number of available motor units and from the misleading practice of grouping motor unit data across different subjects, contractions, and force levels. To establish a more clear understanding of motor unit control during fatigue, we investigated the firing behavior of motor units from the vastus lateralis muscle of individual subjects during a fatigue protocol of repeated voluntary constant force isometric contractions. Surface electromyographic decomposition technology provided the firings of 1,890 motor unit firing trains. These data revealed that to sustain the contraction force as the muscle fatigued, the following occurred: 1) motor unit firing rates increased; 2) new motor units were recruited; and 3) motor unit recruitment thresholds decreased. Although the degree of these adaptations was subject specific, the behavior was consistent in all subjects. When we compared our empirical observations with those obtained from simulation, we found that the fatigue-induced changes in motor unit firing behavior can be explained by increasing excitation to the motoneuron pool that compensates for the fatigue-induced decrease in muscle force twitch reported in empirical studies. Yet, the fundamental motor unit control scheme remains invariant throughout the development of fatigue. These findings indicate that the central nervous system regulates motor unit firing behavior by adjusting the operating point of the excitation to the motoneuron pool to sustain the contraction force as the muscle fatigues. Copyright © 2016 the American Physiological Society.

Effect of some aggregate characteristics on the fatigue behavior of an asphaltic concrete mixture.

DOT National Transportation Integrated Search

1970-01-01

The effect of aggregate characteristics on the fatigue behavior of asphaltic mixtures was investigated by utilizing a laboratory constant deflection, flexural fatigue test. Coarse aggregate characteristics such as surface texture, rugosity, and flaki...

General planar transverse domain walls realized by optimized transverse magnetic field pulses in magnetic biaxial nanowires

NASA Astrophysics Data System (ADS)

Li, Mei; Wang, Jianbo; Lu, Jie

2017-02-01

The statics and field-driven dynamics of transverse domain walls (TDWs) in magnetic nanowires (NWs) have attracted continuous interests because of their theoretical significance and application potential in future magnetic logic and memory devices. Recent results demonstrate that uniform transverse magnetic fields (TMFs) can greatly enhance the wall velocity, meantime leave a twisting in the TDW azimuthal distribution. For application in high-density NW devices, it is preferable to erase the twisting so as to minimize magnetization frustrations. Here we report the realization of a completely planar TDW with arbitrary tilting attitude in a magnetic biaxial NW under a TMF pulse with fixed strength and well-designed orientation profile. We smooth any twisting in the TDW azimuthal plane thus completely decouple the polar and azimuthal degrees of freedom. The analytical differential equation describing the polar angle distribution is derived and the resulting solution is not the Walker-ansatz form. With this TMF pulse comoving, the field-driven dynamics of the planar TDW is investigated with the help of the asymptotic expansion method. It turns out the comoving TMF pulse increases the wall velocity under the same axial driving field. These results will help to design a series of modern magnetic devices based on planar TDWs.

Characterisation of case depth in induction-hardened medium carbon steels based on magnetic minor hysteresis loop measurement technique

NASA Astrophysics Data System (ADS)

He, Cunfu; Yang, Meng; Liu, Xiucheng; Wang, Xueqian; Wu, Bin

2017-11-01

The magnetic hysteresis behaviours of ferromagnetic materials vary with the heat treatment-induced micro-structural changes. In the study, the minor hysteresis loop measurement technique was used to quantitatively characterise the case depth in two types of medium carbon steels. Firstly, high-frequency induction quenching was applied in rod samples to increase the volume fraction of hard martensite to the soft ferrite/pearlite (or sorbite) in the sample surface. In order to determine the effective and total case depth, a complementary error function was employed to fit the measured hardness-depth profiles of induction-hardened samples. The cluster of minor hysteresis loops together with the tangential magnetic field (TMF) were recorded from all the samples and the comparative study was conducted among three kinds of magnetic parameters, which were sensitive to the variation of case depth. Compared to the parameters extracted from an individual minor loop and the distortion factor of the TMF, the magnitude of three-order harmonic of TMF was more suitable to indicate the variation in case depth. Two new minor-loop coefficients were introduced by combining two magnetic parameters with cumulative statistics of the cluster of minor-loops. The experimental results showed that the two coefficients monotonically linearly varied with the case depth within the carefully selected magnetisation region.

Tensile and fatigue behavior of tungsten/copper composites

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Gabb, Timothy P.; Kim, Y. S.

1989-01-01

Work on W/Cu unidirectional composites was initiated to study the behavior of this ductile-ductile composite system under thermomechanical fatigue and to examine the applicability of fatigue-life prediction methods for thermomechanical fatigue of this metal matrix composite. The first step was to characterize the tensile behavior of four ply, 10 vol. percent W/Cu plates at room and elevated temperatures. Fatigue tests were conducted in load control on 0 degree specimens at 260 C. The maximum cyclic stress was varied but the minimum cyclic stress was kept constant. All tests were performed in vacuum. The strain at failure increased with increasing maximum cyclic stress.

Characterization of fatigue behavior of 2-D woven fabric reinforced ceramic matrix composite at elevated temperature. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Groner, D.J.

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced SiC/SiC ceramic matrix composite specimens at 1100 deg C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle/low stress fatigue tests, far less fiber/matrix interface debond was evident than in low cycle/high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.

Ground-to-Ground Optical Communications Demonstration

NASA Technical Reports Server (NTRS)

Biswas, A.; Lee, S.

2000-01-01

A bidirectional horizontal-path optical link was demonstrated between Strawberry Peak (SP), Lake Arrowhead, California, and the JPL Table Mountain Facility (TMF), Wrightwood, California, during June and November of 1998. The 0.6-m telescope at TMF was used to broadcast a 4-beam 780-nm beacon to SP. The JPL-patented Optical Communications Demonstrator (OCD) at SP received the beacon, performed ne tracking to compensate for the atmosphere-induced beacon motion and retransmitted a 844-nm communications laser beam modulated at 40 to 500 Mb/s back to TMF. Characteristics of the horizontal-path atmospheric channel as well as performance of the optical communications link were evaluated. The normalized variance of the irradiance fluctuations or scintillation index delta2/I at either end was determined. At TMF where a single 844-nm beam was received by a 0.6-m aperture, the measured delta2/I covered a wide range from 0.07 to 1.08. A single 780-nm beam delta2/I measured at SP using a 0.09-m aperture yielded values ranging from 0.66 to 1.03, while a combination of four beams reduced the scintillation index due to incoherent averaging to 0.22 to 0.40. This reduction reduced the dynamic range of the fluctuations from 17 to 21 dB to 13 to 14 dB as compared with the OCD tracking sensor dynamic range of 10 dB. Predictions of these values also were made based on existing theories and are compared. Generally speaking, the theoretical bounds were reasonable. Discussions on the probability density function (PDF) of the intensity fluctuations are presented and compared with the measurements made. The lognormal PDF was found to agree for the weak scintillation regime as expected. The present measurements support evidence presented by earlier measurements made using the same horizontal path, which suggests that the aperture averaging effect is better than theoretically predicted.

Interference-Fit-Fastener Investigation

DTIC Science & Technology

1975-09-01

Crack Initiation . .*. . . .* e . . .*. . . .*. 20 Figure 9. Actual and Predicted Fatigue Life Behavior of Notched Open Hole Plates for 2024 - T351 ... Aluminum (Reference 19) * .. . . . . . . . .. . 22 Figure 10. Gage I Strain Response With Cycles . . . . . . . . 24 Figure 11. Fatigue Damage - Life ... Fatigue Behavior", Effect of Environment and Complex Load History on Fatigue Life , ASTM STP 462, pp 74-91 (1970). (7) Grosskreutz, J. C., and Shaw, G. G

Depositional evolution of the Melville Bay trough-mouth fan, NW Greenland

NASA Astrophysics Data System (ADS)

Knutz, Paul; Gregersen, Ulrik

2015-04-01

The continental margin of NW Greenland bordering northern Baffin Bay is characterized by major sediment accumulations, known as Trough-Mouth Fans (TMF). The fan depocentres represent intense sediment dispersal at the terminus of ice streams that during cold climate periods provided major drainage routes of the northern Greenland Ice Sheet into Baffin Bay. The imprint of paleo-icestreams is seen by erosional troughs crossing a >250 km broad shelf region, which caps a series of sedimentary basins containing thick Mesozoic-Tertiary strata packages. This presentation provides an overview of the seismic stratigraphic division, depositional architecture and examples of seismic facies of the Melville Bay TMF using a 5-10 km grid of industry-quality 2D seismic data (TGS). The focus will primarily be on the inception and early stage of glacial fan development. Comparing the present-day topography with the regional geology shows that the paleo-icestreams exploited the Cenozoic infill of former rift basins that are more conducive to erosion than the adjoining ridges and structural highs. The TMF sequence is constructed by a series of progradational seismic units that represent successive steps in location of ice stream terminus and associated depocenters. The slope fronts of the prograding units show abundant signatures of sediment instability and mass-wasting but evidence of along-slope current-driven processes is also recognized presumably linked to interglacial sea level high-stands. The topset of each unit is characterized by planar erosion that merges landward into hummocky positive geometries with low internal reflectivity. These features are generally interpreted as subglacial landforms, e.g. terminal moraines and ice-contact deposits, associated with grounding zone wedges. Unlike the most recent TMF units deposited in front of the present trough, the oldest glacigenic units have built out from a Neogene sediment prism that forms the core of modern shallow-water banks. These topographic highs probably formed anchoring points facilitating the initial expansion of inland ice onto the shelf. The pre-glacial Neogene package displays typical contourite features concentrated along the mid-shelf region, while further basinward it is marked by intensive erosion and down-slope mass transport in the form of mega-slides. Our results suggests that shelf glaciation in these parts could have been facilitated by tectonic adjustments (e.g. relative fall in sea level) related to phases of tectonic uplift during latest Miocene and Pliocene/early Pleistocene. The present work contributes to a better understanding of the internal complexity of TMF systems as well as the underlying long-term mechanisms that evoked the Late Cenozoic development of the Greenland Ice Sheet.

Fatigue-life behavior and matrix fatigue crack spacing in unnotched SCS-6/Timetal 21S metal matrix composites

NASA Technical Reports Server (NTRS)

Ward, G. T.; Herrmann, D. J.; Hillberry, B. M.

1993-01-01

Fatigue tests of the SCS-6/Timetal 21S composite system were performed to characterize the fatigue behavior for unnotched conditions. The stress-life behavior of the unnotched (9/90)2s laminates was investigated for stress ratios of R = 0.1 and R = 0.3. The occurrence of matrix cracking was also examined in these specimens. This revealed multiple matrix crack initiation sites throughout the composite, as well as evenly spaced surface cracks along the length of the specimens. No difference in fatigue lives were observed for stress ratios of R = 0.1 and R = 0.3 when compared on a stress range basis. The unnotched SCS-6/Timetal 21S composites had shorter fatigue lives than the SCS-6/Ti-15-3 composites, however the neat Timetal 21S matrix material had a longer fatigue life than the neat Ti-15-3.

An Abnormal Increase of Fatigue Life with Dwell Time during Creep-Fatigue Deformation for Directionally Solidified Ni-Based Superalloy DZ445

NASA Astrophysics Data System (ADS)

Ding, Biao; Ren, Weili; Deng, Kang; Li, Haitao; Liang, Yongchun

2018-03-01

The paper investigated the creep-fatigue behavior for directionally solidified nickel-based superalloy DZ445 at 900 °C. It is found that the fatigue life shows an abnormal increase when the dwell time exceeds a critical value during creep-fatigue deformation. The area of hysteresis loop and fractograph explain the phenomenon quite well. The shortest life corresponds to the maximal area of hysteresis loop, i. e. the maximum energy to be consumed during the creep-fatigue cycle. The fractographic observation of failed samples further supports the abnormal behavior of fatigue life.

The effect of matrix microstructure on cyclic response and fatigue behavior of particle- reinforced 2219 aluminum: Part I. room temperature behavior

NASA Astrophysics Data System (ADS)

Vyletel, G. M.; Allison, J. E.; van Aken, D. C.

1995-12-01

The low-cycle and high-cycle fatigue behavior and cyclic response of naturally aged and overaged 2219/TiC/15p and unreinforced 2219 Al were investigated using plastic strain-controlled and stress-controlled testing. In addition, the influence of grain size on the particle-reinforced materials was examined. In both reinforced and unreinforced materials, the naturally aged conditions were cyclically unstable, exhibiting an initial hardening behavior followed by an extended region of cyclic stability and ultimately a softening region. The overaged reinforced material was cyclically stable for the plastic strains examined, while the overaged unreinforced material exhibited cyclic hardening at plastic strains greater than 2.5 × 10-4. Decreasing grain size of particle-reinforced materials modestly increased the cyclic flow stress of both naturally aged and overaged materials. Reinforced and unreinforced materials exhibited similar fatigue life behaviors; however, the reinforced and unreinforced naturally aged materials had superior fatigue lives in comparison to the overaged materials. Grain size had no effect on the fatigue life behavior of the particle-reinforced materials. The fatigue lives were strongly influenced by the presence of clusters of TiC particles and exogenous Al3Ti intermetallics.

Fatigue Behavior of a Third Generation PM Disk Superalloy

NASA Technical Reports Server (NTRS)

Gayda, John; Gabb, Timothy P.

2008-01-01

The fatigue behavior of a 3rd generation PM disk alloy, LSHR, was studied at 1300 F. Tensile, creep, and fatigue tests were run on smooth and notched (Kt = 2) bars under a variety of conditions. Analysis of smooth bar fatigue data, run under strain and load control with R ratios of 0 and -1, showed that a stress based Smith-Watson-Topper approach could collapse the data set. While the tensile and creep data showed substantial notch strengthening at 1300 F, the fatigue data showed a life deficit for the notch specimens. A viscoplastic finite element model, which accounted for stress relaxation at the notch tip, provided the best correlation between the notched and smooth bar behavior, although the fatigue data was not fully rationalized based on this simplified viscoplastic model of the stresses at the notch tip.Inclusion of a 90 sec dwell at peak load was found to dramatically decrease notch fatigue life. This result was shown to be consistent with a simple linear creep-fatigue damage rule, where creep damage dominated at low stresses and fatigue damage was more prevalent at higher stresses.

Development of Fatigue and Crack Propagation Design and Analysis Methodology in a Corrosive Environment for Typical Mechanically-Fastened Joints. Volume 2. State-of-the-Art Assessment.

DTIC Science & Technology

1983-03-01

120] hypothesized a linear summation model to predict the corrosion -fatigue behavior above Kjscc for a high-strength steel . The model considers the...120] could satisfactorily predict the rates of corrosion -fatigue-crack growth for 18-Ni Maraging steels tested in several gaseous and aqueous...NADC-83126-60 Vol. II 6. The corrosion fatigue behavior of titanium alloys is very complex. Therefore, a better understanding of corrosion fatigue

Influence of Prior Fatigue Cycling on Creep Behavior of Reduced Activation Ferritic-Martensitic Steel

NASA Astrophysics Data System (ADS)

Sarkar, Aritra; Vijayanand, V. D.; Parameswaran, P.; Shankar, Vani; Sandhya, R.; Laha, K.; Mathew, M. D.; Jayakumar, T.; Rajendra Kumar, E.

2014-06-01

Creep tests were carried out at 823 K (550 °C) and 210 MPa on Reduced Activation Ferritic-Martensitic (RAFM) steel which was subjected to different extents of prior fatigue exposure at 823 K at a strain amplitude of ±0.6 pct to assess the effect of prior fatigue exposure on creep behavior. Extensive cyclic softening that characterized the fatigue damage was found to be immensely deleterious for creep strength of the tempered martensitic steel. Creep rupture life was reduced to 60 pct of that of the virgin steel when the steel was exposed to as low as 1 pct of fatigue life. However, creep life saturated after fatigue exposure of 40 pct. Increase in minimum creep rate and decrease in creep rupture ductility with a saturating trend were observed with prior fatigue exposures. To substantiate these findings, detailed transmission electron microscopy studies were carried out on the steel. With fatigue exposures, extensive recovery of martensitic-lath structure was distinctly observed which supported the cyclic softening behavior that was introduced due to prior fatigue. Consequently, prior fatigue exposures were considered responsible for decrease in creep ductility and associated reduction in the creep rupture strength.

Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP)

Treesearch

Jinghao Li; John F. Hunt; Shaoqin Gong; Zhiyong Cai

2015-01-01

The static and fatigue bending behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP) has been investigated by four-point bending tests. Fatigue panels and weakened panels (wESCP) with an initial interface defect were manufactured for the fatigue tests. Stress σ vs. number of cycles curves (S-N) were recorded under the different stress...

Resistance Spot Welding Characteristics and High Cycle Fatigue Behavior of DP 780 Steel Sheet

NASA Astrophysics Data System (ADS)

Pal, Tapan Kumar; Bhowmick, Kaushik

2012-02-01

Resistance spot welding characteristics of DP 780 steel was investigated using peel test, microhardness test, tensile shear test, and fatigue test. Tensile shear test provides better spot weld quality than conventional peel test and hardness is not a good indicator of the susceptibility to interfacial fracture. The results of high-cycle fatigue behavior of spot welded DP 780 steel under two different parameters show that at high load low cycle range a significant difference in the S- N curve and almost similar fatigue behavior of spot welds at low load high cycle range are obtained. However, when applied load was converted to stress intensity factor, the difference in the fatigue behavior between welds diminished. Furthermore, a transition in fracture mode, i.e., interfacial and plug and hole-type at about 50% of yield load is observed.

Mechanical Behavior of Additive Manufactured Layered Materials, Part 2: Stainless Steels

DTIC Science & Technology

2015-04-30

and/or excellent cyclic fatigue behavior: stainless - steel 316L and 17-4PH. Additive materials were fabricated at a leading-edge facility using their...Tensile deformation Representative engineering stress- strain data from measurements obtained with our stainless steel specimens are shown in... fatigue behavior Cyclic fatigue strengths demonstrated by the DMLS stainless steels fabricated in the horizontal orientation were almost equal to

Quality of Life and Its Predictors Among Children and Adolescents With Cancer.

PubMed

Pan, Hsien-Ting; Wu, Li-Min; Wen, Shu-Hui

Quality of life (QoL) increasingly is being assessed in pediatric patients with cancer. However, only a few studies focused on QoL predictors during and after treatment for pediatric patients with cancer. The aims of this study were to (1) assess differences of QoL, distress behavior, and fatigue among children and adolescents; (2) examine the relationship of distress behaviors, fatigue, and a variety of demographic factors to QoL; and (3) identify QoL predictors. A cross-sectional descriptive study involving 150 participants treated between 2012 and 2014 was conducted. All participants were given a diagnosis of cancer, ranged in age from 7 to 18 years, and had no developmental delay or mental illness. Three instruments including Pediatric Quality of Life, Distress Behaviors, and Multidimensional Fatigue Scale were administered. Adolescents aged 16 to 18 years reported lower school functioning and experienced more general and sleep/rest fatigue. Fatigue and distress behaviors were associated with a poorer QoL. Diagnosis at a younger age, greater time since diagnosis, and family structure were associated with a better QoL. General fatigue, relationship distress, family structure, and time since diagnosis were significant predictors of QoL, accounting for 64% of the total variance. Factors associated with a poorer QoL included fatigue, distress behaviors, and diagnosis at an older age. Less general fatigue and relationship distress, greater time since diagnosis, and living in nuclear family predicted a better QoL. Routinely evaluating fatigue and school functioning in pediatric patients with cancer is warranted, as well as developing educational programs to enhance the management of fatigue and relationship issues, especially for those who were given a diagnosis recently or for late adolescents.

Severe fatigue after treatment of ductal carcinoma in situ: A comparison with age-matched breast cancer survivors and healthy controls.

PubMed

Abrahams, H J G; Smits, L; Lugt, M de; Roos, W K de; Kamm, Y; Heins, M J; Verhagen, C A H H V M; Gielissen, M F M; Knoop, H

2017-02-01

Severe fatigue after treatment of ductal carcinoma in situ (DCIS) has not been studied before. The current study examined (i) the prevalence of severe fatigue in DCIS patients versus breast cancer survivors (BCS) and healthy controls (HC), (ii) quality of life and functioning of severely versus non-severely fatigued DCIS patients and BCS, and (iii) the association of fatigue with psychosocial and behavioral factors in DCIS patients. 89 patients treated for DCIS were matched on age and gender to 67 BCS and 178 HC (ratio 1:1:2). Fatigue was measured with the Fatigue Severity subscale of the Checklist Individual Strength. 23% of DCIS patients, 25% of BCS, and 6% of HC were severely fatigued (DCIS versus HC: p < 0.001). Severely fatigued DCIS patients had a lower quality of life and were more impaired in all domains of functioning than non-severely fatigued DCIS patients. Sleep problems, dysfunctional cognitions regarding fatigue, avoidance of activities, all-or-nothing behavior, perceived lack of social support, DCIS-related coping problems, and fear of future cancer occurrence were related to fatigue. The prevalence of severe fatigue in DCIS patients was similar to BCS, but higher than in HC. Severely fatigued DCIS patients had a lower quality of life and more functional impairments. The psychosocial and behavioral fatigue-related factors in DCIS patients are known to perpetuate fatigue in BCS. These factors can be targeted in interventions for cancer-related fatigue. Our findings suggest that the same treatment elements might be applicable to severely fatigued DCIS patients. Copyright © 2016 Elsevier Ltd. All rights reserved.

Tension and fatigue behavior of 316LVM 1x7 multi-strand cables used as implantable electrodes.

PubMed

Lewandowski, John J; Varadarajan, Ravikumar; Smith, Brian; Tuma, Chris; Shazly, Mostafa; Vatamanu, Luciano O

2008-07-15

The mechanical behavior of 316LVM 1x7 cables were evaluated in uniaxial tension, and in cyclic strain-controlled fatigue with the use of a Flex tester operated to provide fully reversed bending fatigue. The magnitude of cyclic strains imparted to each cable tested was controlled via the use of different diameter mandrels. Smaller diameter mandrels produced higher values of cyclic strain and lower fatigue life. Multiple samples were tested and analyzed via scanning electron microscopy. The fatigue results were analyzed via a Coffin-Manson-Basquin approach and compared to fatigue data obtained from the literature where testing was conducted on similar materials, but under rotating bending fatigue conditions.

Fatigue crack growth behavior of railroad tank car steel TC-128B subjected to various environments. Volume 2 : appendices

DOT National Transportation Integrated Search

2006-12-01

This is Volume II-Appendices of Fatigue Crack Growth Behavior of Railroad Tank Car Steel TC-128B Subjected to Various Environments. This document contains miscellaneous supporting documentation, fatigue crack growth laboratory data, and analyses.

Fatigue and fracture mechanical behavior for Chinese A508-3 steel at room temperature

NASA Astrophysics Data System (ADS)

Shi, K. K.; Xie, H.; Zheng, B.; Fu, X. L.

2018-06-01

Material, A508-3 steel, has been used in nuclear reactor vessels. In the present study, fatigue and fracture mechanical behavior of Chinese A5083 steel at room temperature are studied by mechanical material testing machine (MTS). Test data of material’s mechanical behavior including uniaxial tension, low cycle fatigue (LCF), threshold value of stress intensity factor (SIF) range, fatigue crack growth (FCG), and fracture toughness is generated and given for further study. It is worth noting that the model in predicting FCG of material from LCF parameters is verified and discussed.

Speech-Processing Fatigue in Children: Auditory Event-Related Potential and Behavioral Measures

PubMed Central

Gustafson, Samantha J.; Rentmeester, Lindsey; Hornsby, Benjamin W. Y.; Bess, Fred H.

2017-01-01

Purpose Fatigue related to speech processing is an understudied area that may have significant negative effects, especially in children who spend the majority of their school days listening to classroom instruction. Method This study examined the feasibility of using auditory P300 responses and behavioral indices (lapses of attention and self-report) to measure fatigue resulting from sustained listening demands in 27 children (M = 9.28 years). Results Consistent with predictions, increased lapses of attention, longer reaction times, reduced P300 amplitudes to infrequent target stimuli, and self-report of greater fatigue were observed after the completion of a series of demanding listening tasks compared with the baseline values. The event-related potential responses correlated with the behavioral measures of performance. Conclusion These findings suggest that neural and behavioral responses indexing attention and processing resources show promise as effective markers of fatigue in children. PMID:28595261

Dynamic and static fatigue behavior of sintered silicon nitrides

NASA Technical Reports Server (NTRS)

Chang, J.; Khandelwal, P.; Heitman, P. W.

1987-01-01

The dynamic and static fatigue behavior of Kyocera SN220M sintered silicon nitride at 1000 C was studied. Fractographic analysis of the material failing in dynamic fatigue revealed the presence of slow crack growth (SCG) at stressing rates below 41 MPa/min. Under conditions of static fatigue this material also displayed SCG at stresses below 345 MPa. SCG appears to be controlled by microcracking of the grain boundaries. The crack velocity exponent (n) determined from both dynamic and static fatigue tests ranged from 11 to 16.

Fatigue Behavior of an Advanced SiC/SiC Composite with an Oxidation Inhibited Matrix at 1200 deg C in Air and in Steam

DTIC Science & Technology

2010-03-01

eight-harness-satin (8HS) weave plies. Tensile stress -strain behavior and tensile properties were evaluated at 1200˚C. Tension-tension fatigue tests...ratio of minimum stress to maximum stress of R = 0.05, with maximum stresses ranging from 100 to 140 MPa in air and in steam. Fatigue run-out was...Hz, the presence of steam appeared to have little influence on the fatigue resistance for the fatigue stress levels < 140 MPa. The presence of steam

Fatigue Behavior and Modeling of Additively Manufactured Ti-6Al-4V Including Interlayer Time Interval Effects

NASA Astrophysics Data System (ADS)

Torries, Brian; Shamsaei, Nima

2017-12-01

The effects of different cooling rates, as achieved by varying the interlayer time interval, on the fatigue behavior of additively manufactured Ti-6Al-4V specimens were investigated and modeled via a microstructure-sensitive fatigue model. Comparisons are made between two sets of specimens fabricated via Laser Engineered Net Shaping (LENS™), with variance in interlayer time interval accomplished by depositing either one or two specimens per print operation. Fully reversed, strain-controlled fatigue tests were conducted, with fractography following specimen failure. A microstructure-sensitive fatigue model was calibrated to model the fatigue behavior of both sets of specimens and was found to be capable of correctly predicting the longer fatigue lives of the single-built specimens and the reduced scatter of the double-built specimens; all data points fell within the predicted upper and lower bounds of fatigue life. The time interval effects and the ability to be modeled are important to consider when producing test specimens that are smaller than the production part (i.e., property-performance relationships).

Compression fatigue behavior and failure mechanism of porous titanium for biomedical applications.

PubMed

Li, Fuping; Li, Jinshan; Huang, Tingting; Kou, Hongchao; Zhou, Lian

2017-01-01

Porous titanium and its alloys are believed to be one of the most attractive biomaterials for orthopedic implant applications. In the present work, porous pure titanium with 50-70% porosity and different pore size was fabricated by diffusion bonding. Compression fatigue behavior was systematically studied along the out-of-plane direction. It resulted that porous pure titanium has anisotropic pore structure and the microstructure is fine-grained equiaxed α phase with a few twins in some α grains. Porosity and pore size have some effect on the S-N curve but this effect is negligible when the fatigue strength is normalized by the yield stress. The relationship between normalized fatigue strength and fatigue life conforms to a power law. The compression fatigue behavior is characteristic of strain accumulation. Porous titanium experiences uniform deformation throughout the entire sample when fatigue cycle is lower than a critical value (N T ). When fatigue cycles exceed N T , strain accumulates rapidly and a single collapse band forms with a certain angle to the loading direction, leading to the sudden failure of testing sample. Both cyclic ratcheting and fatigue crack growth contribute to the fatigue failure mechanism, while the cyclic ratcheting is the dominant one. Porous titanium possesses higher normalized fatigue strength which is in the range of 0.5-0.55 at 10 6 cycles. The reasons for the higher normalized fatigue strength were analyzed based on the microstructure and fatigue failure mechanism. Copyright © 2016 Elsevier Ltd. All rights reserved.

The impact of fatigue on latent print examinations as revealed by behavioral and eye gaze testing.

PubMed

Busey, Thomas; Swofford, Henry J; Vanderkolk, John; Emerick, Brandi

2015-06-01

Eye tracking and behavioral methods were used to assess the effects of fatigue on performance in latent print examiners. Eye gaze was measured both before and after a fatiguing exercise involving fine-grained examination decisions. The eye tracking tasks used similar images, often laterally reversed versions of previously viewed prints, which holds image detail constant while minimizing prior recognition. These methods, as well as a within-subject design with fine grained analyses of the eye gaze data, allow fairly strong conclusions despite a relatively small subject population. Consistent with the effects of fatigue on practitioners in other fields such as radiology, behavioral performance declined with fatigue, and the eye gaze statistics suggested a smaller working memory capacity. Participants also terminated the search/examination process sooner when fatigued. However, fatigue did not produce changes in inter-examiner consistency as measured by the Earth Mover Metric. Implications for practice are discussed. Copyright © 2015 Elsevier Ireland Ltd. All rights reserved.

The isothermal fatigue behavior of a unidirectional SiC/Ti composite and the Ti alloy matrix

NASA Technical Reports Server (NTRS)

Gayda, John, Jr.; Gabb, Timothy P.; Freed, Alan D.

1989-01-01

The high temperature fatigue behavior of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) matrix reinforced by 33 vol percent of continuous unidirectional SiC fibers was experimentally and analytically evaluated. Isothermal MMC fatigue tests with constant amplitude loading parallel to the fiber direction were performed at 300 and 550 C. Comparative fatigue tests of the Ti-15-3 matrix alloy were also conducted. Composite fatigue behavior and the in-situ stress state of the fiber and matrix were analyzed with a micromechanical model, the Concentric Cylinder Model (CCM). The cyclic stress-strain response of the composite was stable at 300 C. However, an increase in cyclic mean strain foreshortened MMC fatigue life at high strain ranges at 550 C. Fatigue tests of the matrix alloy and CCM analyses indicated this response was associated with stress relaxation of the matrix in the composite.

Ae Behavior of Smart Stress Memory Patch after Variable Amplitude Loading

NASA Astrophysics Data System (ADS)

Fujino, Y.; Nambu, S.; Enoki, M.

Recently, the structural health monitoring becomes increasingly great important to assure the ease and safety of our life, and it is required significantly to develop non-destructive evaluation for structures such as bridges and tunnels. Some sacrificed specimens have been developed to evaluate the fatigue damage of structures such as fatigue cycles and residual lifetime, but it can be applied only when the stress history is known beforehand. These fatigue sensors need no cable and can be used at low cost in contrast to strain gage. In previous study, a smart stress memory patch was developed as a new fatigue sensor. The patch can measure simultaneously the maximum stress, stress amplitude and the number of fatigue cycles by crack length measurement and Kaiser effect of Acoustic Emission (AE). The crack growth behavior under constant amplitude (CA) loading has been investigated, and AE behavior also has been evaluated only after CA loading. However, AE characteristics after variable amplitude (VA) loading in service are extremely important. Moreover, it is very important to control AE behavior of the smart patch in order to evaluate the applied stress using Kaiser effect. In this study, fatigue test with single overload was investigated to evaluate its influence. Moreover, effect of crack length and heat treatment on AE behavior was also investigated. Finally, AE behavior of the patch was evaluated after fatigue CA loading with overload or VA loading with log-normal distribution and overload.

Water-Vapor Raman Lidar System Reaches Higher Altitude

NASA Technical Reports Server (NTRS)

Leblanc, Thierry; McDermid, I. Stewart

2010-01-01

A Raman lidar system for measuring the vertical distribution of water vapor in the atmosphere is located at the Table Mountain Facility (TMF) in California. Raman lidar systems for obtaining vertical water-vapor profiles in the troposphere have been in use for some time. The TMF system incorporates a number of improvements over prior such systems that enable extension of the altitude range of measurements through the tropopause into the lower stratosphere. One major obstacle to extension of the altitude range is the fact that the mixing ratio of water vapor in the tropopause and the lower stratosphere is so low that Raman lidar measurements in this region are limited by noise. Therefore, the design of the TMF system incorporates several features intended to maximize the signal-to-noise ratio. These features include (1) the use of 355-nm-wavelength laser pulses having an energy (0.9 J per pulse) that is high relative to the laser-pulse energy levels of prior such systems, (2) a telescope having a large aperture (91 cm in diameter) and a narrow field of view (angular width .0.6 mrad), and (3) narrow-bandpass (wavelength bandwidth 0.6 nm) filters for the water-vapor Raman spectral channels. In addition to the large-aperture telescope, three telescopes having apertures 7.5 cm in diameter are used to collect returns from low altitudes.

A Constitutive Relationship between Fatigue Limit and Microstructure in Nanostructured Bainitic Steels

PubMed Central

Mueller, Inga; Rementeria, Rosalia; Caballero, Francisca G.; Kuntz, Matthias; Sourmail, Thomas; Kerscher, Eberhard

2016-01-01

The recently developed nanobainitic steels show high strength as well as high ductility. Although this combination seems to be promising for fatigue design, fatigue properties of nanostructured bainitic steels are often surprisingly low. To improve the fatigue behavior, an understanding of the correlation between the nanobainitic microstructure and the fatigue limit is fundamental. Therefore, our hypothesis to predict the fatigue limit was that the main function of the microstructure is not necessarily totally avoiding the initiation of a fatigue crack, but the microstructure has to increase the ability to decelerate or to stop a growing fatigue crack. Thus, the key to understanding the fatigue behavior of nanostructured bainite is to understand the role of the microstructural features that could act as barriers for growing fatigue cracks. To prove this hypothesis, we carried out fatigue tests, crack growth experiments, and correlated these results to the size of microstructural features gained from microstructural analysis by light optical microscope and EBSD-measurements. Finally, we were able to identify microstructural features that influence the fatigue crack growth and the fatigue limit of nanostructured bainitic steels. PMID:28773953

Severe fatigue in type 1 diabetes: Exploring its course, predictors and relationship with HbA1c in a prospective study.

PubMed

Menting, Juliane; Nikolaus, Stephanie; van der Veld, William M; Goedendorp, Martine M; Tack, Cees J; Knoop, Hans

2016-11-01

To prospectively identify the course of severe fatigue, its predictors and the relationship with HbA 1c in patients with type 1 diabetes. 214 adult patients completed questionnaires on fatigue severity and fatigue-related factors at baseline. HbA 1c was retrieved from medical records. After 43months, fatigue severity and HbA 1c were reassessed in 194 patients. A logistic regression analysis was used to determine predictors of severe fatigue at follow-up with various cognitive-behavioral and clinical factors as potential predictors. The relationship between fatigue and HbA 1c was investigated in a sub-analysis by differentiating between patients with suboptimal glucose control [HbA 1c >7% (53mmol/mol)] and optimal glucose control [HbA 1c ⩽7% (53mmol/mol)]. The prevalence of severe fatigue was 40% at baseline and 42% at follow-up. In three out of four severely fatigued patients at baseline (76%), severe fatigue persisted over time. More depressive symptoms, more pain, sleep disturbances, lower self-efficacy concerning fatigue, less confidence in diabetes self-care, more fatigue severity at baseline and more diabetes complications predicted severe fatigue at follow-up. Over time, HbA 1c at baseline was positively associated with fatigue severity at follow-up in both groups (suboptimal glucose control: r=.18, p<.05; optimal glucose control: r=.09, p<.05). About three quarters of fatigued[corrected] patients with type 1 diabetes suffer from persistent fatigue. Aside from the number of diabetes complications, no clinical factors explained the persistence of fatigue. HbA 1c and fatigue were weakly associated in a sub-analysis. Since the strongest predictors of severe fatigue were cognitive-behavioral factors, behavioral interventions might be effective in decreasing fatigue. Copyright © 2016 Elsevier Ireland Ltd. All rights reserved.

Design Analysis and Thermo-Mechanical Fatigue of a Polyimide Composite for Combustion Chamber Support

NASA Technical Reports Server (NTRS)

Thesken, J. C.; Melis, M.; Shin, E.; Sutter, J.; Burke, Chris

2004-01-01

Polyimide composites are being evaluated for use in lightweight support structures designed to preserve the ideal flow geometry within thin shell combustion chambers of future space launch propulsion systems. Principles of lightweight design and innovative manufacturing techniques have yielded a sandwich structure with an outer face sheet of carbon fiber polyimide matrix composite. While the continuous carbon fiber enables laminated skin of high specific stiffness; the polyimide matrix materials ensure that the rigidity and durability is maintained at operation temperatures of 316 C. Significant weight savings over all metal support structures are expected. The protypical structure is the result of ongoing collaboration, between Boeing and NASA-GRC seeking to introduce polyimide composites to the harsh environmental and loads familiar to space launch propulsion systems. Design trade analyses were carried out using relevant closed form solutions, approximations for sandwich beams/panels and finite element analysis. Analyses confirm the significant thermal stresses exist when combining materials whose coefficients of thermal expansion (CTEs) differ by a factor of about 10 for materials such as a polymer composite and metallic structures. The ramifications on design and manufacturing alternatives are reviewed and discussed. Due to stringent durability and safety requirements, serious consideration is being given to the synergistic effects of temperature and mechanical loads. The candidate structure operates at 316 C, about 80% of the glass transition temperature T(sub g). Earlier thermomechanical fatigue (TMF) investigations of chopped fiber polyimide composites made this near to T(sub g), showed that cyclic temperature and stress promoted excessive creep damage and strain accumulation. Here it is important to verify that such response is limited in continuous fiber laminates.

A novel evaluation strategy for fatigue reliability of flexible nanoscale films

NASA Astrophysics Data System (ADS)

Zheng, Si-Xue; Luo, Xue-Mei; Wang, Dong; Zhang, Guang-Ping

2018-03-01

In order to evaluate fatigue reliability of nanoscale metal films on flexible substrates, here we proposed an effective evaluation way to obtain critical fatigue cracking strain based on the direct observation of fatigue damage sites through conventional dynamic bending testing technique. By this method, fatigue properties and damage behaviors of 930 nm-thick Au films and 600 nm-thick Mo-W multilayers with individual layer thickness 100 nm on flexible polyimide substrates were investigated. Coffin-Manson relationship between the fatigue life and the applied strain range was obtained for the Au films and Mo-W multilayers. The characterization of fatigue damage behaviors verifies the feasibility of this method, which seems easier and more effective comparing with the other testing methods.

Total strain version of strainrange partitioning for thermomechanical fatigue at low strains

NASA Technical Reports Server (NTRS)

Halford, G. R.; Saltsman, J. F.

1987-01-01

A new method is proposed for characterizing and predicting the thermal fatigue behavior of materials. The method is based on three innovations in characterizing high temperature material behavior: (1) the bithermal concept of fatigue testing; (2) advanced, nonlinear, cyclic constitutive models; and (3) the total strain version of traditional strainrange partitioning.

Cognitive Behavior Therapy for Relatively Active and for Passive Chronic Fatigue Syndrome Patients

ERIC Educational Resources Information Center

Bazelmans, Ellen; Prins, Judith; Bleijenberg, Gijs

2006-01-01

In chronic fatigue syndrome (CFS), facilitating, initiating, and perpetuating factors are distinguished. Although somatic factors might have initiated symptoms in CFS, they do not explain the persistence of fatigue. Cognitive behavior therapy (CBT) for CFS focuses on factors that perpetuate and prolong symptoms. Recently it has been shown that,…

The concept of a plasma centrifuge with a high frequency rotating magnetic field and axial circulation

NASA Astrophysics Data System (ADS)

Borisevich, V. D.; Potanin, E. P.

2017-07-01

The possibility of using a rotating magnetic field (RMF) in a plasma centrifuge (PC), with axial circulation to multiply the radial separation effect in an axial direction, is considered. For the first time, a traveling magnetic field (TMF) is proposed to drive an axial circulation flow in a PC. The longitudinal separation effect is calculated for a notional model, using specified operational parameters and the properties of a plasma, comprising an isotopic mixture of 20Ne-22Ne and generated by a high frequency discharge. The optimal intensity of a circulation flow, in which the longitudinal separation effect reaches its maximum value, is studied. The optimal parameters of the RMF and TMF for effective separation, as well as the centrifuge performance, are calculated.

Investigation of the effect of vacuum environment on the fatigue and fracture behavior of 7075-T6.

NASA Technical Reports Server (NTRS)

Hudson, C. M.

1972-01-01

Axial-load fatigue-life, fatigue-crack propagation, and fracture-toughness experiments were conducted on sheet specimens made of 7075-T6 aluminum alloy. These experiments were conducted at air pressures ranging from 101 kN/sq m to 7 micronewtons/sq m to determine the effect of air pressure on fatigue behavior. Analysis of the results from the fatigue-life experiments indicated that for a given stress level, the lower the air pressure was the longer the fatigue life. At a pressure of 7 micronewtons/sq m, fatigue lives were 15 to 30 times longer than at 101 kN/sq m. Analysis of the results from the fatigue-crack-growth experiments indicates that at low values of stress-intensity range, the fatigue-crack-growth rates were approximately twice as high at atmospheric pressure as in vacuum. However, at higher values of stress-intensity range, the fatigue-crack-growth rates were nominally the same in vacuum and at atmospheric pressure.

Failure of a laminated composite under tension-compression fatigue loading

NASA Technical Reports Server (NTRS)

Rotem, A.; Nelson, H. G.

1989-01-01

The fatigue behavior of composite laminates under tension-compression loading is analyzed and compared with behavior under tension-tension and compression-compression loading. It is shown that for meaningful fatigue conditions, the tension-compression case is the dominant one. Both tension and compression failure modes can occur under the reversed loading, and failure is dependent on the specific lay-up of the laminate and the difference between the tensile static strength and the absolute value of the compressive static strength. The use of a fatigue failure envelope for determining the fatigue life and mode of failure is proposed and demonstrated.

Charge Weld Effects on High Cycle Fatigue Behavior of a Hollow Extruded AA6082 Profile

NASA Astrophysics Data System (ADS)

Nanninga, N.; White, C.; Dickson, R.

2011-10-01

Fatigue properties of specimens taken from different locations along the length of a hollow AA6082 extrusion, where charge weld (interface between successive billets in multi-billet extrusions) properties and the degree of coring (accumulation of highly sheared billet surface material at back end of billet) are expected to vary, have been evaluated. The fatigue strength of transverse specimens containing charge welds is lower near the front of the extrusion where the charge weld separation is relatively large. The relationship between fatigue failure and charge weld separation appears to be directly related to charge weld properties. The lower fatigue properties of the specimens are likely associated with early overload fatigue failure along the charge weld interface. Coring does not appear to have significantly affected fatigue behavior.

An engineering approach to the prediction of fatigue behavior of unnotched/notched fiber reinforced composite laminates

NASA Technical Reports Server (NTRS)

Kulkarni, S. V.; Mclaughlin, P. V., Jr.

1978-01-01

An engineering approach is proposed for predicting unnotched/notched laminate fatigue behavior from basic lamina fatigue data. The fatigue analysis procedure was used to determine the laminate property (strength/stiffness) degradation as a function of fatigue cycles in uniaxial tension and in plane shear. These properties were then introduced into the failure model for a notched laminate to obtain damage growth, residual strength, and failure mode. The approach is thus essentially a combination of the cumulative damage accumulation (akin to the Miner-Palmgren hypothesis and its derivatives) and the damage growth rate (similar to the fracture mechanics approach) philosophies. An analysis/experiment correlation appears to confirm the basic postulates of material wearout and the predictability of laminate fatigue properties from lamina fatigue data.

Numerical simulation of the fatigue behavior of additive manufactured titanium porous lattice structures.

PubMed

Zargarian, A; Esfahanian, M; Kadkhodapour, J; Ziaei-Rad, S

2016-03-01

In this paper, the effects of cell geometry and relative density on the high-cycle fatigue behavior of Titanium scaffolds produced by selective laser melting and electron beam melting techniques were numerically investigated by finite element analysis. The regular titanium lattice samples with three different unit cell geometries, namely, diamond, rhombic dodecahedron and truncated cuboctahedron, and the relative density range of 0.1-0.3 were analyzed under uniaxial cyclic compressive loading. A failure event based algorithm was employed to simulate fatigue failure in the cellular material. Stress-life approach was used to model fatigue failure of both bulk (struts) and cellular material. The predicted fatigue life and the damage pattern of all three structures were found to be in good agreement with the experimental fatigue investigations published in the literature. The results also showed that the relationship between fatigue strength and cycles to failure obeyed the power law. The coefficient of power function was shown to depend on relative density, geometry and fatigue properties of the bulk material while the exponent was only dependent on the fatigue behavior of the bulk material. The results also indicated the failure surface at an angle of 45° to the loading direction. Copyright © 2015 Elsevier B.V. All rights reserved.

Analysis of the Mechanical Behavior, Creep Resistance and Uniaxial Fatigue Strength of Martensitic Steel X46Cr13

PubMed Central

Brnic, Josip; Krscanski, Sanjin; Lanc, Domagoj; Brcic, Marino; Turkalj, Goran; Canadija, Marko; Niu, Jitai

2017-01-01

The article deals with the analysis of the mechanical behavior at different temperatures, uniaxial creep and uniaxial fatigue of martensitic steel X46Cr13 (1.4034, AISI 420). For the purpose of considering the aforementioned mechanical behavior, as well as determining the appropriate resistance to creep and fatigue strength levels, numerous uniaxial tests were carried out. Tests related to mechanical properties performed at different temperatures are presented in the form of engineering stress-strain diagrams. Short-time creep tests performed at different temperatures and different stress levels are presented in the form of creep curves. Fatigue tests carried out at stress ratios R=0.25 and R=−1 are shown in the form of S–N (fatigue) diagrams. The finite fatigue regime for each of the mentioned stress ratios is modeled by an inclined log line, while the infinite fatigue regime is modeled by a horizontal line, which represents the fatigue limit of the material and previously was calculated by the modified staircase method. Finally, the fracture toughness has been calculated based on the Charpy V-notch impact energy. PMID:28772749

New optomechanical approach to quantitative characterization of fatigue behavior of dynamically loaded structures

NASA Astrophysics Data System (ADS)

Furlong, Cosme; Pryputniewicz, Ryszard J.

1995-06-01

The basic relationships between stress and strain under cyclic conditions of loading are not at present well understood. It would seem that information of this type is vital for a fundamental approach to understand the fatigue behavior of dynamically loaded structures. In this paper, experimental and computational methods are utilized to study the fatigue behavior of a thin aluminum cantilever plate subjected to dynamic loading. The studies are performed by combining optomechanical and finite element methods. The cantilever plate is loaded periodically by excitation set at a fixed amplitude and at a specific resonance frequency of the plate. By continuously applying this type of loading and using holographic interferometry, the behavior of the plate during a specific period of time is investigated. Quantitative information is obtained from laser vibrometry data which are utilized by a finite element program to calculate strains and stresses assuming a homogeneous and isotropic material and constant strain elements. It is shown that the use of experimental and computational hybrid methodologies allows identification of different zones of the plate that are fatigue critical. This optomechanical approach proves to be a viable tool for understanding of fatigue behavior of mechanical components and for performing optimization of structures subjected to fatigue conditions.

45 Km Horizontal Path Optical Link Experiment

NASA Technical Reports Server (NTRS)

Biswas, A.; Ceniceros, J.; Novak, M.; Jeganathan, M.; Portillo, A.; Erickson, D.; Depew, J.; Sanii, B.; Lesh, J. R.

2000-01-01

Mountain-top to mountain-top optical link experiments have been initiated at JPL, in order to perform a systems level evaluation of optical communications. Progress made so far is reported. ne NASA, JPL developed optical communications demonstrator (OCD) is used to transmit a laser signal from Strawberry Peak (SP), located in the San Bernadino mountains of California. This laser beam is received by a 0.6 m aperture telescope at JPL's Table Mountain Facility (TMF), located in Wrightwood, California. The optical link is bi-directional with the TMF telescope transmitting a continuous 4-wave (cw) 780 run beacon and the OCD sending back a 840 nm, 100 - 500 Mbps pseudo noise (PN) modulated, laser beam. The optical link path is at an average altitude of 2 km above sea level, covers a range of 46.8 km and provides an atmospheric channel equivalent to approx. 4 air masses. Average received power measured at either end fall well within the uncertainties predicted by link analysis. The reduction in normalized intensity variance (sigma(sup 2, sub I)) for the 4-beam beacon, compared to each individual beam, at SP, was from approx. 0.68 to 0.22. With some allowance for intra-beam mis-alignment, this is consistent with incoherent averaging. The sigma(sup2, sub I) measured at TMF approx. 0.43 +/- 0.22 exceeded the expected aperture averaged value of less than 0.1, probably because of beam wander. The focused spot sizes of approx. 162 +/- 6 microns at the TMF Coude and approx. 64 +/- 3 microns on the OCD compare to the predicted size range of 52 - 172 microns and 57 - 93 microns, respectively. This is consistent with 4 - 5 arcsec of atmospheric "seeing". The preliminary evaluation of OCD's fine tracking indicates that the uncompensated tracking error is approx. 3.3 micro rad compared to approx. 1.7 micro rad observed in the laboratory. Fine tracking performance was intermittent, primarily due to beacon fades on the OCD tracking sensor. The best bit error rates observed while tracking worked were 1E-5 to 1E-6.

Stratospheric Ozone Intercomparison Campaign (STOIC) 1989: Overview

NASA Technical Reports Server (NTRS)

Margitan, J. J.; Barnes, R. A.; Brothers, G. B.; Butler, J.; Burris, J.; Connor, B. J.; Ferrare, R. A.; Kerr, J. B.; Komhyr, W. D.; McCormick, M. P.;

High-Cycle, Push-Pull Fatigue Fracture Behavior of High-C, Si-Al-Rich Nanostructured Bainite Steel.

PubMed

Zhao, Jing; Ji, Honghong; Wang, Tiansheng

2017-12-29

The high-cycle, push-pull fatigue fracture behavior of high-C, Si-Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push-pull fatigue limits at 10⁷ cycles were estimated as 710-889 MPa, for the samples isothermally transformed at the temperature range of 220-260 °C through data extrapolation, measured under the maximum cycle number of 10⁵. Both the interior inclusion and the sample surface constituted the fatigue crack origins. During the fatigue crack propagation, a high amount of secondary cracks were formed in almost parallel arrangements. The apparent plastic deformation occurred in the fracture surface layer, which induced approximately all retained austenite to transform into martensite.

High-Cycle, Push–Pull Fatigue Fracture Behavior of High-C, Si–Al-Rich Nanostructured Bainite Steel

PubMed Central

Zhao, Jing; Ji, Honghong

2017-01-01

The high-cycle, push–pull fatigue fracture behavior of high-C, Si–Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push–pull fatigue limits at 107 cycles were estimated as 710–889 MPa, for the samples isothermally transformed at the temperature range of 220–260 °C through data extrapolation, measured under the maximum cycle number of 105. Both the interior inclusion and the sample surface constituted the fatigue crack origins. During the fatigue crack propagation, a high amount of secondary cracks were formed in almost parallel arrangements. The apparent plastic deformation occurred in the fracture surface layer, which induced approximately all retained austenite to transform into martensite. PMID:29286325

Is there a cognitive signature for MS-related fatigue?

PubMed

Hanken, Katrin; Eling, Paul; Hildebrandt, Helmut

2015-04-01

The compensatory approach of fatigue argues that it is a state caused by task load. The neuropsychiatric approach argues that fatigue is a trait (like depression), unrelated to environmental challenges. We propose that fatigue is an internal state that can be measured behaviorally only by applying specific cognitive tasks. PubMed was searched for articles concerning the relation between fatigue and cognitive performance or brain atrophy or functional MRI, distinguishing between the following cognitive domains: learning/memory, cognitive speed/selective attention, language, visuospatial processing, working memory, alerting/vigilance. Only tasks assessing alerting/vigilance are strongly related to fatigue. Areas with brain atrophy in fatigue patients overlap with brain regions activated in healthy controls performing alerting/vigilance tasks. Fatigue is not a compensatory state, nor a psychogenic trait. It is a feeling with behavioral effects that seems to be caused by brain atrophy or a neurochemical dysfunction of the alerting/vigilance system. © The Author(s), 2014.

Fatigue Life Estimation under Cumulative Cyclic Loading Conditions

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; McGaw, Michael A; Halford, Gary R.

1999-01-01

The cumulative fatigue behavior of a cobalt-base superalloy, Haynes 188 was investigated at 760 C in air. Initially strain-controlled tests were conducted on solid cylindrical gauge section specimens of Haynes 188 under fully-reversed, tensile and compressive mean strain-controlled fatigue tests. Fatigue data from these tests were used to establish the baseline fatigue behavior of the alloy with 1) a total strain range type fatigue life relation and 2) the Smith-Wastson-Topper (SWT) parameter. Subsequently, two load-level multi-block fatigue tests were conducted on similar specimens of Haynes 188 at the same temperature. Fatigue lives of the multi-block tests were estimated with 1) the Linear Damage Rule (LDR) and 2) the nonlinear Damage Curve Approach (DCA) both with and without the consideration of mean stresses generated during the cumulative fatigue tests. Fatigue life predictions by the nonlinear DCA were much closer to the experimentally observed lives than those obtained by the LDR. In the presence of mean stresses, the SWT parameter estimated the fatigue lives more accurately under tensile conditions than under compressive conditions.

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds

PubMed Central

Liu, Xuesong; Berto, Filippo

2018-01-01

The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2–1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them. PMID:29695140

Low-Cycle Fatigue Behavior of 10CrNi3MoV High Strength Steel and Its Undermatched Welds.

PubMed

Song, Wei; Liu, Xuesong; Berto, Filippo; Razavi, S M J

2018-04-24

The use of high strength steel allows the design of lighter, more slender and simpler structures due to high strength and favorable ductility. Nevertheless, the increase of yield strength does not guarantee the corresponding improvement of fatigue resistance, which becomes a major concern for engineering structure design, especially for the welded joints. The paper presents a comparison of the low cycle fatigue behaviors between 10CrNi3MoV high strength steel and its undermatched weldments. Uniaxial tension tests, Push-pull, strain-controlled fatigue tests were conducted on base metal and weldments in the strain range of 0.2⁻1.2%. The monotonic and cyclic stress-strain curves, stress-life, strain-life and energy-life in terms of these materials were analyzed for fatigue assessment of materials discrepancy. The stress-life results of base metal and undermatched weld metal exhibit cyclic softening behaviors. Furthermore, the shapes of 10CrNi3MoV steel hysteresis loops show a satisfactory Masing-type behavior, while the weld metal shows a non-Masing type behavior. Strain, plastic and total strain energy density amplitudes against the number of reversals to failure results demonstrate that the undermatched weld metal presents a higher resistance to fatigue crack initiation than 10CrNi3MoV high strength steel. Finally, fatigue fracture surfaces of specimens were compared by scanning electron microscopy to identify the differences of crack initiation and the propagation between them.

Behavior of a Quasi-Isotropic Ply Metal Matrix Composite under Thermo-Mechanical and Isothermal Fatigue Loading

DTIC Science & Technology

1992-12-01

tensile strength of the composite (20:14). After the heat treatment was accomplished, polishing was performed. Using an automated MAXIMET polishing machine ...AD-A258 902 AFIT/GAE/.ENY/92D-05 Behavior of a Quasi-Isotropic Ply Metal Matrix Composite Under Thermo- Mechanical and Isothermal Fatigue Loading...115 AFIT/GAE/ENY/92D-05 Behavior of a Quasi-Isotropic Ply Metal Matrix Composite Under Thermo- Mechanical and Isothermal Fatigue Loading THESIS

Fatigue Technology Assessment and Strategies for Fatigue Avoidance in Marine Structures

DTIC Science & Technology

1992-06-01

time history. xii MODELING ERROR (Xme) : Typically defined as the ratio of actual behavior of the structure to the one predicted by the model. It is...and temperature changes may be important to fatigue in a local component, these loadings are not a major concern in the global behavior of typical...Reference 3.1) to assess fracture behavior in a low toughness HAZ indicated that a small low- toughness area in the HAZ can be masked by the higher

Fatigue behavior of a cross-ply ceramic matrix composite at elevated temperature under tension-tension loading. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Steiner, C.D.

This study investigated the fatigue behavior and damage mechanisms of a (0/90)4s SiC/MAS ceramic matrix composite under tension-tension loading at two elevated temperatures and two frequencies. Stress and strain hystereses, maximum and minimum strain, and modulus of elasticity were evaluated to characterize the material behavior. Microscopy and fractography were used to evaluate damage progression and mechanisms. Fatigue life was independent of frequency at both temperatures.

Microstructure-fatigue crack propagation relationship in TiB{sub 2} particulate reinforced Zn (ZA-8) alloy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Hua, W.; Zhang, J.; Wang, Z.

1995-10-01

The relationship between microstructure and propagation behavior of fatigue crack in TiB{sub 2} particulate reinforced ZA-8 Zn alloy and in the corresponding constituent matrix material was studied in three point bending fatigue tests with well-polished and pre-etched specimens. Special attention was paid to the observation of microstructure along the crack path as well as on the fracture surface. Mechanism for the difference in fatigue crack growth behavior of the two materials was investigated. The present results indicate that the addition of reinforcement modified the solidification process of the matrix material leading to a considerable change in the matrix microstructure. Thismore » change in the matrix microstructure and the presence of reinforcing particles considerably affected the fatigue crack propagation behavior in the material.« less

Fatigue behavior of SiC reinforced titanium composites

NASA Technical Reports Server (NTRS)

Bhatt, R. T.; Grimes, H. H.

1979-01-01

The low cycle axial fatigue properties of 25 and 44 fiber volume percent SiC/Ti(6Al-4V) composites were measured at room temperature and at 650 deg C. The S-N curves for the composites showed no anticipated improvement over bulk matrix behavior at room temperature. Although axial and transverse tensile strength results suggest a degradation in SiC fiber strength during composite fabrication, it appears that the poor fatigue life of the composites was caused by a reduced fatigue resistance of the reinforced Ti(6Al-4V) matrix. The reduced matrix behavior was due, to the presence of flawed and fractured fibers created near the specimen surfaces by preparation techniques and to the large residual tensile stresses that can exist in fiber reinforced matrices. The effects of fatigue testing at high temperature are discussed.

Fracture Toughness and Fatigue Crack Growth Behavior of As-Cast High-Entropy Alloys

NASA Astrophysics Data System (ADS)

Seifi, Mohsen; Li, Dongyue; Yong, Zhang; Liaw, Peter K.; Lewandowski, John J.

2015-08-01

The fracture toughness and fatigue crack growth behavior of two as-vacuum arc cast high-entropy alloys (HEAs) (Al0.2CrFeNiTi0.2 and AlCrFeNi2Cu) were determined. A microstructure examination of both HEA alloys revealed a two-phase structure consisting of body-centered cubic (bcc) and face-centered cubic (fcc) phases. The notched and fatigue precracked toughness values were in the range of those reported in the literature for two-phase alloys but significantly less than recent reports on a single phase fcc-HEA that was deformation processed. Fatigue crack growth experiments revealed high fatigue thresholds that decreased significantly with an increase in load ratio, while Paris law slopes exhibited metallic-like behavior at low R with significant increases at high R. Fracture surface examinations revealed combinations of brittle and ductile/dimpled regions at overload, with some evidence of fatigue striations in the Paris law regime.

Effects of fine porosity on the fatigue behavior of a powder metallurgy superalloy

NASA Technical Reports Server (NTRS)

Miner, R. V., Jr.; Dreshfield, R. L.

1980-01-01

Hot isostatically pressed powder metallurgy Astroloy was obtained which contained 1.4 percent fine porosity at the grain boundaries produced by argon entering the powder container during pressing. This material was tested at 650 C in fatigue, creep fatigue, tension, and stress-rupture and the results compared with previous data on sound Astroloy. The pores averaged about 2 micrometers diameter and 20 micrometers spacing. They did influence fatigue crack initiation and produced a more intergranular mode of propagation. However, fatigue life was not drastically reduced. A large 25 micrometers pore in one specimen resulting from a hollow particle did not reduce life by 60 percent. Fatigue behavior of the porous material showed typical correlation with tensile behavior. The plastic strain range life relation was reduced proportionately with the reduction in tensile ductility, but the elastic strain range-life relation was little changed reflecting the small reduction in sigma sub u/E for the porous material.

Uniaxial low cycle fatigue behavior for pre-corroded 16MND5 bainitic steel in simulated pressurized water reactor environment

NASA Astrophysics Data System (ADS)

Chen, Xu; Ren, Bin; Yu, Dunji; Xu, Bin; Zhang, Zhe; Chen, Gang

2018-06-01

The effects of uniaxial tension properties and low cycle fatigue behavior of 16MND5 bainitic steel cylinder pre-corroded in simulated pressurized water reactor (PWR) were investigated by fatigue at room temperature in air and immersion test system, scanning electron microscopy (SEM), energy disperse spectroscopy (EDS). The experimental results indicated that the corrosion fatigue lives of 16MND5 specimen were significantly affected by the strain amplitude and simulated PWR environments. The compositions of corrosion products were complexly formed in simulated PWR environments. The porous corrosion surface of pre-corroded materials tended to generate pits as a result of promoting contact area to the fresh metal, which promoted crack initiation. For original materials, the fatigue cracks initiated at inclusions imbedded in the micro-cracks. Moreover, the simulated PWR environments degraded the mechanical properties and low cycle fatigue behavior of 16MND5 specimens remarkably. Pre-corrosion of 16MND5 specimen mainly affected the plastic term of the Coffin-Manson equation.

Atomistic origin of size effects in fatigue behavior of metallic glasses

NASA Astrophysics Data System (ADS)

Sha, Zhendong; Wong, Wei Hin; Pei, Qingxiang; Branicio, Paulo Sergio; Liu, Zishun; Wang, Tiejun; Guo, Tianfu; Gao, Huajian

2017-07-01

While many experiments and simulations on metallic glasses (MGs) have focused on their tensile ductility under monotonic loading, the fatigue mechanisms of MGs under cyclic loading still remain largely elusive. Here we perform molecular dynamics (MD) and finite element simulations of tension-compression fatigue tests in MGs to elucidate their fatigue mechanisms with focus on the sample size effect. Shear band (SB) thickening is found to be the inherent fatigue mechanism for nanoscale MGs. The difference in fatigue mechanisms between macroscopic and nanoscale MGs originates from whether the SB forms partially or fully through the cross-section of the specimen. Furthermore, a qualitative investigation of the sample size effect suggests that small sample size increases the fatigue life while large sample size promotes cyclic softening and necking. Our observations on the size-dependent fatigue behavior can be rationalized by the Gurson model and the concept of surface tension of the nanovoids. The present study sheds light on the fatigue mechanisms of MGs and can be useful in interpreting previous experimental results.

Mixing Dynamics Induced by Traveling Magnetic Fields

NASA Technical Reports Server (NTRS)

Grugel, Richard N.; Mazuruk, Konstantin

2000-01-01

Microstructural and compositional homogeneity in metals and alloys can only be achieved if the initial melt is homogeneous prior to the onset of solidification processing. Naturally induced convection may initially facilitate this requirement but upon the onset of solidification significant compositional variations generally arise leading to undesired segregation. Application of alternating magnetic fields to promote a uniform bulk liquid concentration during solidification processing has been suggested. To investigate such possibilities an initial study of using traveling magnetic fields (TMF) to promote melt homogenization is reported in this work. Theoretically, the effect of TMF-induced convection on mixing phenomena is studied in the laminar regime of flow. Experimentally, with and without applied fields, both: mixing dynamics by optically monitoring the spreading of an initially localized dye in transparent fluids and, compositional variations in metal alloys have been investigated.

Mixing Dynamics Induced by Traveling Magnetic Fields

NASA Technical Reports Server (NTRS)

Grugel, Richard N.; Mazuruk, Konstantin; Rose, M. Franklin (Technical Monitor)

2001-01-01

Microstructural and compositional homogeneity in metals and alloys can only be achieved if the initial melt is homogeneous prior to the onset of solidification processing. Naturally induced convection may initially facilitate this requirement but upon the onset of solidification significant compositional variations generally arise leading to undesired segregation. Application of alternating magnetic fields to promote a uniform bulk liquid concentration during solidification processing has been suggested. To investigate such possibilities an initial study of using traveling magnetic fields (TMF) to promote melt homogenization is reported in this work. Theoretically, the effect of TMF-induced convection on mixing phenomena is studied in the laminar regime of flow. Experimentally, with and without applied fields, both 1) mixing dynamics by optically monitoring the spreading of an initially localized dye in transparent fluids and, 2) compositional variations in metal alloys have been investigated.

Dual-LP11 mode 4×4 MIMO-OFDM transmission over a two-mode fiber.

PubMed

Al Amin, Abdullah; Li, An; Chen, Simin; Chen, Xi; Gao, Guanjun; Shieh, William

2011-08-15

We report successful transmission of dual-LP(11) mode (LP(11a) and LP(11b)), dual polarization coherent optical orthogonal frequency-division multiplexing (CO-OFDM) signals over two-mode fibers (TMF) using all-fiber mode converters. Mode converters based on mechanically induced long-period grating with better than 20 dB extinction ratios are realized and used for interfacing single-mode fiber transmitter and receivers to the TMF. We demonstrate that by using 4×4 MIMO-OFDM processing, the random coupling of the two LP(11) spatial modes can be successfully tracked and equalized with a one-tap frequency-domain equalizer. We achieve successful transmission of 35.3 Gb/s over 26-km two-mode fiber with less than 3 dB penalty. © 2011 Optical Society of America

Effects of Polymethoxyflavonoids on Bone Loss Induced by Estrogen Deficiency and by LPS-Dependent Inflammation in Mice.

PubMed

Matsumoto, Shigeru; Tominari, Tsukasa; Matsumoto, Chiho; Yoshinouchi, Shosei; Ichimaru, Ryota; Watanabe, Kenta; Hirata, Michiko; Grundler, Florian M W; Miyaura, Chisato; Inada, Masaki

2018-01-20

Polymethoxyflavonoids (PMFs) are a family of the natural compounds that mainly compise nobiletin, tangeretin, heptamethoxyflavone (HMF), and tetramethoxyflavone (TMF) in citrus fruits. PMFs have shown various biological functions, including anti-oxidative effects. We previously showed that nobiletin, tangeretin, and HMF all inhibited interleukin (IL)-1-mediated osteoclast differentiation via the inhibition of prostaglandin E2 synthesis. In this study, we created an original mixture of PMFs (nobiletin, tangeretin, HMF, and TMF) and examined whether or not PMFs exhibit co-operative inhibitory effects on osteoclastogenesis and bone resorption. In a coculture of bone marrow cells and osteoblasts, PMFs dose-dependently inhibited IL-1-induced osteoclast differentiation and bone resorption. The optimum concentration of PMFs was lower than that of nobiletin alone in the suppression of osteoclast differentiation, suggesting that the potency of PMFs was stronger than that of nobiletin in vitro. The oral administration of PMFs recovered the femoral bone loss induced by estrogen deficiency in ovariectomized mice. We further tested the effects of PMFs on lipopolysaccharide-induced bone resorption in mouse alveolar bone. In an ex vivo experimental model for periodontitis, PMFs significantly suppressed the bone-resorbing activity in organ cultures of mouse alveolar bone. These results indicate that a mixture of purified nobiletin, tangeretin, HMF, and TMF exhibits a co-operative inhibitory effect for the protection against bone loss in a mouse model of bone disease, suggesting that PMFs may be potential candidates for the prevention of bone resorption diseases, such as osteoporosis and periodontitis.

Fatigue behavior of a 2XXX series aluminum alloy reinforced with 15 vol Pct SiCp

NASA Astrophysics Data System (ADS)

Bonnen, J. J.; Allison, J. E.; Jones, J. W.

1991-05-01

The fatigue behavior of a naturally aged powder metallurgy 2xxx series aluminum alloy (Alcoa MB85) and a composite made of this alloy with 15 vol pct SiCp, has been investigated. Fatigue lives were determined using load-controlled axial testing of unnotched cylindrical samples. The influence of mean stress was determined at stress ratios of -1, 0.1, and 0.7. Mean stress had a significant influence on fatigue life, and this influence was consistent with that normally observed in metals. At each stress ratio, the incorporation of SiC reinforcement led to an increase in fatigue life at low and intermediate stresses. When considered on a strain-life basis, however, the composite materials had a somewhat inferior resistance to fatigue. Fatigue cracks initiated from several different microstructural features or defect types, but fatigue life did not vary significantly with the specific initiation site. As the fatigue crack advanced away from the fatigue crack initiation site, increasing numbers of SiC particles were fractured, in agreement with crack-tip process zone models.

Bithermal fatigue: A simplified alternative to thermomechanical fatigue

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.

1988-01-01

A bithermal fatigue test technique was proposed as a simplified alternative to the thermomechanical fatigue test. Both the thermomechanical cycle and the bithermal technique can be used to study nonisothermal fatigue behavior. The difference between the two cycles is that in a conventional thermomechanical fatigue cycle the temperature is continuously varied concurrently with the applied mechanical strains, but in the bithermal fatigue cycle the specimen is held at zero load during the temperature excursions and all the loads are applied at the two extreme temperatures of the cycle. Experimentally, the bithermal fatigue test technique offers advantages such as ease in synchronizing the temperature and mechanical strain waveforms, in minimizing temperature gradients in the specimen gauge length, and in reducing and interpreting thermal fatigue such as the influence of alternate high and low temperatures on the cyclic stress-strain response characteristics, the effects of thermal state, and the possibility of introducing high- and low-temperature deformation mechanisms within the same cycle. The bithermal technique was used to study nonisothermal fatigue behavior of alloys such as single-crystal PWA 1480, single-crystal Rene N4, cast B1900+Hf, and wrought Haynes 188.

An assessment of cold work effects on strain-controlled low-cycle fatigue behavior of type 304 stainless steel

NASA Astrophysics Data System (ADS)

Rao, K. Bhanu Sankara; Valsan, M.; Sandhya, R.; Mannan, S. L.; Rodriguez, P.

1993-04-01

The influence of prior cold work (PCW) on low-cycle fatigue (LCF) behavior of type 304 stainless steel has been studied at 300, 823, 923, and 1023 K by conducting total axial strain-controlled tests in solution annealed (SA, 0 pct PCW) condition and on specimens having three levels of PCW, namely, 10, 20, and 30 pct. A triangular waveform with a constant frequency of 0.1 Hz was employed for all of the tests performed over strain amplitudes in the range of ±0.25 to ± 1.25 pct. These studies have revealed that fatigue life is strongly dependent on PCW, temperature, and strain amplitude employed in testing. The SA material generally displayed better endurance in terms of total and plastic strain amplitudes than the material in 10, 20, and 30 pct PCW conditions at all of the temperatures. However, at 300 K at very low strain amplitudes, PCW material exhibited better total strain fatigue resistance. At 823 K, LCF life decreased with increasing PCW, whereas at 923 K, 10 pct PCW displayed the lowest life. An improvement in life occurred for prior deformations exceeding 10 pct at all strain amplitudes at 923 K. Fatigue life showed a noticeable decrease with increasing temperature up to 1023 K in PCW state. On the other hand, SA material displayed a minimum in fatigue life at 923 K. The fatigue life results of SA as well as all of the PCW conditions obeyed the Basquin and Coffin-Manson relationships at 300, 823, and 923 K. The constants and exponents in these equations were found to depend on the test temperature and prior metallurgical state of the material. A study is made of cyclic stress-strain behavior in SA and PCW states and the relationship between the cyclic strain-hardening exponent and fatigue behavior at different temperatures has been explored. The influence of environment on fatigue crack initiation and propagation behavior has been examined.

A New Ductility Exhaustion Model for High Temperature Low Cycle Fatigue Life Prediction of Turbine Disk Alloys

NASA Astrophysics Data System (ADS)

Zhu, Shun-Peng; Huang, Hong-Zhong; Li, Haiqing; Sun, Rui; Zuo, Ming J.

2011-06-01

Based on ductility exhaustion theory and the generalized energy-based damage parameter, a new viscosity-based life prediction model is introduced to account for the mean strain/stress effects in the low cycle fatigue regime. The loading waveform parameters and cyclic hardening effects are also incorporated within this model. It is assumed that damage accrues by means of viscous flow and ductility consumption is only related to plastic strain and creep strain under high temperature low cycle fatigue conditions. In the developed model, dynamic viscosity is used to describe the flow behavior. This model provides a better prediction of Superalloy GH4133's fatigue behavior when compared to Goswami's ductility model and the generalized damage parameter. Under non-zero mean strain conditions, moreover, the proposed model provides more accurate predictions of Superalloy GH4133's fatigue behavior than that with zero mean strains.

Low-Cycle Fatigue Behavior of Die-Cast Mg Alloy AZ91

NASA Astrophysics Data System (ADS)

Rettberg, Luke; Anderson, Warwick; Jones, J. Wayne

An investigation has been conducted on the influence of microstructure and artificial aging response (T6) on the low-cycle fatigue behavior of super vacuum die-cast (SVDC) AZ91. Fatigue lifetimes were determined from total strain-controlled fatigue tests for strain amplitudes of 0.2%, 0.4% and 0.6%, under fully reversed loading at a frequency of 5 Hz. Cyclic stress-strain behavior was determined using incremental step test (IST) methods. Two locations in a prototype casting with different thicknesses and, therefore, solidification rates, microstructure and porosity, were examined. In general., at all total strain amplitudes fatigue life was unaffected by microstructure refinement and was attributed to significant levels of porosity. Cyclic softening and a subsequent increased cyclic hardening rate, compared to monotonic tests, were observed, independent of microstructure. These results, fractography and damage accumulation processes, determined from metallographic sectioning, are discussed.

The Merging of Fatigue and Fracture Mechanics Concepts: A Historical Perspective

NASA Technical Reports Server (NTRS)

Newman, James C., Jr.

1997-01-01

The seventh Jerry L. Swedlow Memorial Lecture presents a review of some of the technical developments, that have occurred during the past 40 years, which have led to the merger of fatigue and fracture mechanics concepts. This review is made from the viewpoint of 'crack propagation.' As methods to observe the 'fatigue' process have improved, the formation of fatigue micro-cracks have been observed earlier in life and the measured crack sizes have become smaller. These observations suggest that fatigue damage can now be characterized by 'crack size.' In parallel, the crack-growth analysis methods, using stress-intensity factors, have also improved. But the effects of material inhomogeneities, crack-fracture mechanisms, and nonlinear behavior must now be included in these analyses. The discovery of crack-closure mechanisms, such as plasticity, roughness, and oxide/corrosion/fretting product debris, and the use of the effective stress-intensity factor range, has provided an engineering tool to predict small- and large-crack-growth rate behavior under service loading, conditions. These mechanisms have also provided a rationale for developing, new, damage-tolerant materials. This review suggests that small-crack growth behavior should be viewed as typical behavior, whereas large-crack threshold behavior should be viewed as the anomaly. Small-crack theory has unified 'fatigue' and 'fracture mechanics' concepts; and has bridged the cap between safe-life and durability/damage-tolerance design concepts.

Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under strain controlled mode. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dennis, L.B.

1994-12-01

This research extends the existing knowledge of cross-ply metal matrix composites (MMC) to include fatigue behavior under strain-controlled fully reversed loading. This study investigated fatigue life, failure modes and damage mechanisms of the SCS-6/Ti-15-3, (O/9O)2s, MMC. The laminate was subjected to fully reversed fatigue at elevated temperature (427 deg C) at various strain levels. Stress, strain and modulus data were analyzed to characterize the macro-mechanical behavior of the composite. Microscopy and fractography were accomplished to identify and characterize the damage mechanisms at the microscopic level. Failure modes varied according to the maximum applied strain level showing either mixed mode (i.e.more » combination of both fiber and matrix dominated modes) or matrix dominated fatigue failures. As expected, higher strain loadings resulted in more ductility of the matrix at failure, evidenced by fracture surface features. For testing of the same composite laminate, the fatigue life under strain controlled mode slightly increased, compared to its load-controlled mode counterpart, using the effective strain range comparison basis. However, the respective fatigue life curves converged in the high cycle region, suggesting that the matrix dominated failure mode produces equivalent predicted fatigue lives for both control modes.« less

Systemic lupus erythematosus in three ethnic groups. VI: Factors associated with fatigue within 5 years of criteria diagnosis. LUMINA Study Group. LUpus in MInority populations: NAture vs Nurture.

PubMed

Zonana-Nacach, A; Roseman, J M; McGwin, G; Friedman, A W; Baethge, B A; Reveille, J D; Alarcón, G S

2000-01-01

To determine the frequency, degree and associated features of fatigue among Hispanic (H), African American (AA) and Caucasian (C) patients with recent onset (< or = 5 yr) systemic lupus erythematosus (SLE) at their baseline evaluation. H (n = 69), AA (n = 83) and C (n = 71) patients from the LUMINA (LUpus in MInority populations: NAture vs Nurture) cohort were studied. Fatigue [Fatigue Severity Scale (FSS)] was defined as present if FSS score > or = 3.0. Variables from functional, clinical, sociodemographic, health behaviors, behavioral and psychological and immunogenetics domains were ascertained at study entry. Associations were examined using regression models. Eighty-six percent (85.7%) of patients reported having fatigue (82.6% H; 85.5% AA; 88.7% C); median FSS score, 5.3. Factors from the psychological and clinical domains were primarily associated with FSS; immunogenetic (HLA Class II phenotypes) features were not. Increased fatigue was strongly associated with decreasing function, both physical and mental. Variables associated with significantly greater degree of fatigue at baseline in the multivariable stepwise model in order of decreasing additional partial R2 explained included: abnormal illness-related behaviors, older age, higher self-reported pain, greater degree of helplessness, greater disease activity, Caucasian race, and lacking health insurance (model R2 = 37%). Fatigue is one of the most prevalent clinical manifestations of SLE across all ethnic groups. The perception of fatigue severity in SLE may be multifactorial in origin, including psychosocial factors and disease activity. If these prove causal, knowledge of their contribution may suggest therapeutic and/or behavioral interventions, which could ameliorate this pervasive and often incapacitating symptom of SLE.

Fatigue of Austempered Ductile Iron with Two Strength Grades in Very High Cycle Regime

NASA Astrophysics Data System (ADS)

Zhang, Jiwang; Li, Wei; Song, Qingpeng; Zhang, Ning; Lu, Liantao

2016-03-01

In this study, Austempered ductile irons (ADIs) with two different strength grades were produced and the fatigue properties were measured at 109 cycles. The results show that the S-N curves give a typical step-wise shape and there is no fatigue limit in the very high cycle fatigue regime. The two grades ADI have the similar fracture behaviors and fatigue failure can initiate from defects at specimen surface and subsurface zone. On the fracture surfaces of some specimens, the `granular-bright-facet' area with rich carbon distribution is observed in the vicinity of the defect. The microstructure affects the crack behaviors at the early propagation stage. The ADI with upper and lower bainite shows higher fatigue strength compared with the ADI with coarse upper bainite.

Tensile and compressive failure modes of laminated composites loaded by fatigue with different mean stress

NASA Technical Reports Server (NTRS)

Rotem, Assa

1990-01-01

Laminated composite materials tend to fail differently under tensile or compressive load. Under tension, the material accumulates cracks and fiber fractures, while under compression, the material delaminates and buckles. Tensile-compressive fatigue may cause either of these failure modes depending on the specific damage occurring in the laminate. This damage depends on the stress ratio of the fatigue loading. Analysis of the fatigue behavior of the composite laminate under tension-tension, compression-compression, and tension-compression had led to the development of a fatigue envelope presentation of the failure behavior. This envelope indicates the specific failure mode for any stress ratio and number of loading cycles. The construction of the fatigue envelope is based on the applied stress-cycles to failure (S-N) curves of both tensile-tensile and compressive-compressive fatigue. Test results are presented to verify the theoretical analysis.

Small fatigue cracks; Proceedings of the Second International Conference/Workshop, Santa Barbara, CA, Jan. 5-10, 1986

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ritchie, R.O.; Lankford, J.

Topics discussed in this volume include crack initiation and stage I growth, microstructure effects, crack closure, environment effects, the role of notches, analytical modeling, fracture mechanics characterization, experimental techniques, and engineering applications. Papers are presented on fatigue crack initiation along slip bands, the effect of microplastic surface deformation on the growth of small cracks, short fatigue crack behavior in relation to three-dimensional aspects and the crack closure effect, the influence of crack depth on crack electrochemistry and fatigue crack growth, and nondamaging notches in fatigue. Consideration is also given to models of small fatigue cracks, short crack theory, assessment ofmore » the growth of small flaws from residual strength data, the relevance of short crack behavior to the integrity of major rotating aero engine components, and the relevance of short fatigue crack growth data to the durability and damage tolerance analyses of aircraft.« less

Tension-Tension Fatigue Behavior of Unidirectional C/Sic Ceramic-Matrix Composite at Room Temperature and 800 °C in Air Atmosphere

PubMed Central

Li, Longbiao

2015-01-01

The tension-tension fatigue behavior of unidirectional C/SiC ceramic-matrix composite at room temperature and 800 °C under air has been investigated. The fatigue hysteresis modulus and fatigue hysteresis loss energy corresponding to different number of applied cycles have been analyzed. The fatigue hysteresis loops models for different interface slip cases have been derived based on the fatigue damage mechanism of fiber slipping relative to matrix in the interface debonded region upon unloading and subsequent reloading. The fiber/matrix interface shear stress has been estimated for different numbers of applied cycles. By combining the interface shear stress degradation model and fibers strength degradation model with fibers failure model, the tension-tension fatigue life S-N curves of unidirectional C/SiC composite at room temperature and 800 °C under air have been predicted.

Behavior of Fatigue Crack Tip Opening in Air and Corrosive Atmosphere

NASA Astrophysics Data System (ADS)

Hayashi, Morihito; Toeda, Kazunori

In the study, a formula for predicting fatigue crack tip opening displacement is deduced firstly. And then, due to comparing actual crack growth rate with the deduced formula, the crack tip configuration factor is defined to figure out the crack tip opening configuration that is useful to clarify the behavior of fatigue crack tip formation apparently. Applying the concept, the crack growth of 7/3 brass and 6/4 brass is predicted from the formula, by replacing material properties such as plastic flow resistance, Young modulus, the Poisson ratio, and fatigue toughness, and fatigue test conditions such as the stress intensity factor range, the load ratio, and cycle frequency. Furthermore, the theoretically expected results are verified with the fatigue tests which were carried out on CT specimens under different load conditions of load ratio, cycle frequency, and cyclic peak load, in different environments of air or corrosive ammonia atmosphere, for various brasses. And by comparing and discussing the calculated crack growth rate with attained experimental results, the apparent configuration factor at the crack tip is determined. And through the attained factor which changes along with crack growth, the behaviors of fatigue crack tip formation under different test conditions have been found out.

High-temperature, low-cycle fatigue behavior of an Al-Mg-Si based heat-resistant aluminum alloy

NASA Astrophysics Data System (ADS)

Kim, Kyu-Sik; Sung, Si-Young; Han, Bum-Suck; Park, Joong-Cheol; Lee, Kee-Ahn

2015-11-01

High-temperature, low-cycle fatigue behavior of the new heat-resistant aluminum alloy was investigated in this study. The aluminum alloy consists of aluminum matrix and small amount of precipitated Mg2Si and (Co, Ni)3Al4 strengthening particles. At room temperature and 523 K, the yield and tensile strengths of Al-Mg-Si-(Co, Ni) the aluminum alloy were maintained with no significant decrease, and elongation increased slightly. Low-cycle fatigue tests controlled by total strain were performed with strain ratio (R) = -1, strain rate = 2×10-3 s-1 at 523 K. The fatigue limit of the low-cycle fatigue of this alloy showed plastic strain amplitude (Δ ɛ pa) of 0.22% at 103 cycles. This value was superior to that of conventional aluminum alloy such as A319. The results of the fractographical observation showed that second phases, especially (Co, Ni)3Al4 particles, affected fatigue behavior. This study also attempted to clarify the mechanism of high-temperature, low-cycle fatigue deformation of Al-Mg-Si-(Co, Ni) alloy in relation to its microstructure and energy dissipation analysis.

The fatigue behavior of composite laminates under various mean stresses

NASA Technical Reports Server (NTRS)

Rotem, A.

1991-01-01

A method is developed for predicting the S-N curve of a composite laminate which is subjected to an arbitrary stress ratio, R (minimum stress/maximum stress). The method is based on the measuring of the S-N behavior of two distinct cases, tension-tension and compression-compression fatigue loadings. Using these parameters, expressions are formulated that estimate the fatigue behavior under any stress ratio loading. Experimental results from the testing of graphite/epoxy laminates, with various structures, are compared with the predictions and show good agreement.

Fatigue behavior of 5Ni-Cr-Mo-V steel weldments containing fabrication discontinuities

NASA Technical Reports Server (NTRS)

Gill, Steven J.; Hauser, Joseph A., II; Crooker, Thomas W.; Kruse, Brian J.; Menon, Ravi

1988-01-01

The applicability of linear elastic fracture mechanics to characterize the fatigue behavior of high-strength steel weldments containing lack-of-penetration (LOP) and slag/lack-of-fusion (S/LOF) discontinuities is explored. Full penetration, double-V butt welds with reinforcements removed were tested under zero-to-tension axial loading. Various filler metals and welding techniques were used. Both sound welds and welds containing discontinuities were cycled to failure. Where possible, cycles to crack initiation were estimated by strain gage measurements. The fracture mechanics approach was successful in correlating the fatigue lifetimes of specimens containing single LOP discontinuities of varying size. However, the fatigue behavior of specimens containing multiple S/LOF discontinuities proved to be much more complex and difficult to analyze.

Rolling-element fatigue life with two synthetic cycloaliphatic traction fluids

NASA Technical Reports Server (NTRS)

Loewenthal, S. H.; Parker, R. J.

1976-01-01

The life potential of two synthetic cycloaliphatic hydrocarbon traction fluids in rolling element fatigue was evaluated in a five ball fatigue tester. Life comparisons with a MIL-L-23699 qualified tetraester oil showed that the traction test oils had good fatigue life performance, comparable to that of the tetraester oil. No statistically significant life differences between the traction fluids and the tetraester oil were exhibited under the accelerated fatigue test conditions. Erratic operating behavior was occasionally encountered during tests with the antiwear additive containing traction fluid for reasons thought to be related to excessive chemical activity under high contact pressure. This behavior occasionally resulted in premature test termination due to excessive surface distress and overheating.

Long-term efficacy of cognitive-behavioral therapy by general practitioners for fatigue: a 4-year follow-up study.

PubMed

Leone, Stephanie S; Huibers, Marcus J H; Kant, Ijmert; van Amelsvoort, Ludovic G P M; van Schayck, Constant P; Bleijenberg, Gijs; Knottnerus, J André

2006-11-01

In an earlier study, we found that cognitive-behavioral therapy (CBT) delivered by general practitioners (GPs) for fatigue among employees on sick leave was not effective after 12 months. In this study we aim to assess the long-term efficacy of CBT by GPs for fatigue. It was hypothesized that the intervention could prevent deterioration as well as relapse of fatigue complaints and relapse into absenteeism in the long term. Patients who participated in the original randomized controlled trial were followed up 4 years later. Fatigue and absenteeism were the main outcomes. Fatigue and absenteeism were high in the intervention and control groups at the 4-year follow-up. There was no significant difference between the intervention group and the control group on fatigue and absenteeism. The intervention group however tended toward less-favorable outcomes as compared with the control group. Like that of chronic fatigue syndrome, the prognosis of less-advanced fatigue is rather poor. CBT delivered by GPs is not effective in the long term.

A microstructurally based model of solder joints under conditions of thermomechanical fatigue

NASA Astrophysics Data System (ADS)

Frear, D. R.; Burchett, S. N.; Rashid, M. M.

The thermomechanical fatigue failure of solder joints is increasingly becoming an important reliability issue. We present two computational methodologies that have been developed to predict the behavior of near eutectic Sn-Pb solder joints under fatigue conditions that are based on metallurgical tests as fundamental input for constitutive relations. The two-phase model mathematically predicts the heterogeneous coarsening behavior of near eutectic Sn-Pb solder. The finite element simulations from this model agree well with experimental thermomechanical fatigue tests. The simulations show that the presence of an initial heterogeneity in the solder microstructure could significantly degrade the fatigue lifetime. The single phase model is a computational technique that was developed to predict solder joint behavior using materials data for constitutive relation constants that could be determined through straightforward metallurgical experiments. A shear/torsion test sample was developed to impose strain in two different orientations. Materials constants were derived from these tests and the results showed an adequate fit to experimental results. The single-phase model could be very useful for conditions where microstructural evolution is not a dominant factor in fatigue.

The fatigue damage behavior of a single crystal superalloy

NASA Technical Reports Server (NTRS)

Mcgaw, Michael A.

1988-01-01

The uniaxial fatigue behavior of a single crystal superalloy, PWA 1480, is described. Both monotonic tensile and constant amplitude fatigue tests were conducted at room temperature, in an effort to assess the applicability of polycrystalline-based fatigue life prediction methods to a single crystal superalloy. The observed constant amplitude behavior correlated best using a stress-based life criterion. Nearly all specimens failed at surface or slightly subsurface microporosity; this is thought to be responsible for the unusually large amount of scatter in the test results. An additional term is developed in the stress-life equation for the purpose of accounting for the effect of microporosity on fatigue life. The form chosen is a function of the effective area of the failure-producing microporosity projected on a plane perpendicular to the loading axis, as well as the applied stress. This additional term correlated the data to within factors of two on life. Although speculative, extrapolation of the microporosity relation to zero micropore area indicates that approximately an order of magnitude improvement in fatigue life should result.

Self-Regulatory Fatigue, Quality of Life, Health Behaviors, and Coping in Patients with Hematologic Malignancies

PubMed Central

Ehlers, Shawna L.; Patten, Christi A.; Gastineau, Dennis A.

2015-01-01

Background Self-regulatory fatigue may play an important role in a complex medical illness. Purpose Examine associations between self-regulatory fatigue, quality of life, and health behaviors in patients pre- (N=213) and 1-year post-hematopoietic stem cell transplantation (HSCT; N=140). Associations between self-regulatory fatigue and coping strategies pre-HSCT were also examined. Method Pre- and 1-year post-HSCT data collection. Hierarchical linear regression modeling. Results Higher self-regulatory fatigue pre-HSCT associated with lower overall, physical, social, emotional, and functional quality of life pre- (p’s<.001) and 1-year post-HSCT (p’s<.01); lower physical activity pre-HSCT (p<.02) and post-HSCT (p<.03) and less healthy nutritional intake post-HSCT (p<.01); changes (i.e., decrease) in quality of life and healthy nutrition over the follow-up year; and use of avoidance coping strategies pre-HSCT (p’s<.001). Conclusion This is the first study to show self-regulatory fatigue pre-HSCT relating to decreased quality of life and health behaviors, and predicting changes in these variables 1-year post-HSCT. PMID:24802991

Data related to cyclic deformation and fatigue behavior of direct laser deposited Ti-6Al-4V with and without heat treatment.

PubMed

Sterling, Amanda J; Torries, Brian; Shamsaei, Nima; Thompson, Scott M

2016-03-01

Data is presented describing the strain-controlled, fully-reversed uniaxial cyclic deformation and fatigue behavior of Ti-6Al-4V specimens additively manufactured via Laser Engineered Net Shaping (LENS) - a Direct Laser Deposition (DLD) process. The data was collected by performing multiple fatigue tests on specimens with various microstructural states/conditions, i.e. in their 'as-built', annealed (below the beta transus temperature), or heat treated (above the beta transus temperature) condition. Such data aids in characterizing the mechanical integrity and fatigue resistance of DLD parts. Data presented herein also allows for elucidating the strong microstructure coupling of the fatigue behavior of DLD Ti-6Al-4V, as the data trends were found to vary with material condition (i.e. as-built, annealed or heat treated) [1]. This data is of interest to the additive manufacturing and fatigue scientific communities, as well as the aerospace and biomedical industries, since additively-manufactured parts cannot be reliably deployed for public use, until their mechanical properties are understood with high certainty.

Data related to cyclic deformation and fatigue behavior of direct laser deposited Ti–6Al–4V with and without heat treatment

PubMed Central

Sterling, Amanda J.; Torries, Brian; Shamsaei, Nima; Thompson, Scott M.

2016-01-01

Data is presented describing the strain-controlled, fully-reversed uniaxial cyclic deformation and fatigue behavior of Ti–6Al–4V specimens additively manufactured via Laser Engineered Net Shaping (LENS) – a Direct Laser Deposition (DLD) process. The data was collected by performing multiple fatigue tests on specimens with various microstructural states/conditions, i.e. in their ‘as-built’, annealed (below the beta transus temperature), or heat treated (above the beta transus temperature) condition. Such data aids in characterizing the mechanical integrity and fatigue resistance of DLD parts. Data presented herein also allows for elucidating the strong microstructure coupling of the fatigue behavior of DLD Ti–6Al–4V, as the data trends were found to vary with material condition (i.e. as-built, annealed or heat treated) [1]. This data is of interest to the additive manufacturing and fatigue scientific communities, as well as the aerospace and biomedical industries, since additively-manufactured parts cannot be reliably deployed for public use, until their mechanical properties are understood with high certainty. PMID:26949728

In-situ neutron diffraction study on the tension-compression fatigue behavior of a twinning induced plasticity steel

DOE PAGES

Xie, Qingge; Liang, Jiangtao; Stoica, Alexandru Dan; ...

2017-05-17

Grain orientation dependent behavior during tension-compression type of fatigue loading in a TWIP steel was studied using in-situ neutron diffraction. Orientation zones with dominant behavior of (1) twinning-de-twinning, (2) twinning-re-twinning followed by twinning-de-twinning, (3) twinning followed by dislocation slip and (4) dislocation slip were identified. Jumps of the orientation density were evidenced in neutron diffraction peaks which explains the macroscopic asymmetric behavior. The asymmetric behavior in early stage of fatigue loading is mainly due to small volume fraction of twins in comparison with that at later stage. As a result, easy activation of the de-twin makes the macroscopically unloading behaviormore » nonlinear.« less

In-situ neutron diffraction study on the tension-compression fatigue behavior of a twinning induced plasticity steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xie, Qingge; Liang, Jiangtao; Stoica, Alexandru Dan

Grain orientation dependent behavior during tension-compression type of fatigue loading in a TWIP steel was studied using in-situ neutron diffraction. Orientation zones with dominant behavior of (1) twinning-de-twinning, (2) twinning-re-twinning followed by twinning-de-twinning, (3) twinning followed by dislocation slip and (4) dislocation slip were identified. Jumps of the orientation density were evidenced in neutron diffraction peaks which explains the macroscopic asymmetric behavior. The asymmetric behavior in early stage of fatigue loading is mainly due to small volume fraction of twins in comparison with that at later stage. As a result, easy activation of the de-twin makes the macroscopically unloading behaviormore » nonlinear.« less

Sedimentary response to ice stream advance and retreat on the Storfjorden Trough Mouth Fan (NW Barents Sea), during Late Weichselian

NASA Astrophysics Data System (ADS)

Pedrosa, Mayte; Camerlengui, Angelo; de Mol, Ben; Lucchi, Renata. G.; Úrgeles, Roger; Rebesco, Michele; Winsborrow, Monica; Laberg, Jan. S.; Andreassen, Karin; Accettella, Daniela

2010-05-01

This seafloor morphological study of the Storfjorden Trough Mouth Fan (TMF) (offshore Svalbard, NW Barents Sea) is based on new multibeam bathymetry and chirp sub-bottom profiler data acquired in 2007 during the BIO Hespérides cruise SVAIS that provides an unprecedented image of the sedimentary processes that accompanied the last advance and retreat of the Storfjorden Ice Stream. Compared to other glacial-marine sedimentary systems (such as the adjacent Bjørnøyrenna TMF), the Storfjorden TMF system is small and associated to a relatively small terrestrial ice sheet, approximately 40.000 km2, with local provenance from Svalbard and the Spitsbergen Bank. Due to this short distance from the ice source to the calving areas and the resulting short residence time of ice in the ice sheet, therefore the glacio -marine system of the Storfjorden reacts rapidly to climatic changes. The Storfjorden continental slope is characterized by three depositional lobes, produced by focused sedimentation at the terminus of ice streams that have changed their location with time. The superficial morphology features associated to the two northernmost lobes are straight gullies in the upper slope, and debris lobes starting from the midslope onwards. The seafloor expression of the southernmost lobe, adjacent to the much smaller Kveithola TMF, demonstrate almost no gully incisions and is dominated by the widespread occurrence of small-scale submarine landslides. The subbottom profiles illustrate that sediment failures occurred throughout the Late Neogene evolution of the southern Storfjorden and Kveithola margin, including large-scale mass transport deposits of up to 200 m thick. Seismic facies of the Neogene sequence shows an alternation of glacigenic debris flows and laminated sediment drape inferred to be plumites. Gullies incising glacigenic debris flows at the surface and subsurface and are filled by an interglacial drape sequence. The gullies are formed during each deglaciation phase, most likely by the erosive action of short-lived high density currents originated by sediment-loaded subglacial melt water discharge.At the outer continental shelf of the southernmost lobe a striking fresh linear straight, which has a width of 1, 5 kilometres and cut the morainal deposits. These features are interpreted as mega-scale glacial lineations, which are tentatively attributed to mega-iceberg scours. These lineations are witness the latest advances of the Storfjorden ice streams before the final retreat which was located at the southernmost lobe. One of the main pre-conditioning factors to slope instability on the southern part of the Storfjorden TMF is identified as high sedimentation rate plumites deposited on the middle-upper continental slope by glacial melt water plumes. This study is part of the SVAIS project (funded by the Spanish IPY), that has a main objective to improve the understanding and the relationship between sedimentation and ice sheet dynamics under natural climatic changes.

Genetics Home Reference: COG5-congenital disorder of glycosylation

MedlinePlus

... in my area? Other Names for This Condition carbohydrate deficient glycoprotein syndrome type IIi CDG IIi CDG2I ... the Golgi by the conserved oligomeric Golgi (COG) complex and the golgin TATA element modulatory factor (TMF). ...

Results from the Galileo Laser Uplink: A JPL Demonstration of Deep-Space Optical Communications

NASA Technical Reports Server (NTRS)

Wilson, K. E.; Lesh, J. R.

1993-01-01

The successful completion of the Galileo Optical Experiment (GOPEX), represented the accomplishment of a significant milestone in JPL's optical communication plan. The experiment demonstrated the first transmission of a narrow laser beam to a deep-space vehicle. Laser pulses were beamed to the Galileo spacecraft by Earth-based transmitters at the Table Mountain Facility (TMF), California, and Starfire Optical Range (SOR), New Mexico. The experiment took place over an eight-day period (December 9 through December 16, 1992) as Galileo receded from Earth on its way to Jupiter, and covered ranges from 1 to 6 million kilometers (15 times the Earth-Moon distance), the laser uplink from TMF covered the longest known range for laser beam transmission and detection. This demonstration is the latest in a series of accomplishments by JPL in the development of deep-space optical communications technology.

The Corrosion and Corrosion Fatigue Behavior of Nickel Based Alloy Weld Overlay and Coextruded Claddings

NASA Astrophysics Data System (ADS)

Stockdale, Andrew

The use of low NOx boilers in coal fired power plants has resulted in sulfidizing corrosive conditions within the boilers and a reduction in the service lifetime of the waterwall tubes. As a solution to this problem, Ni-based weld overlays are used to provide the necessary corrosion resistance however; they are susceptible to corrosion fatigue. There are several metallurgical factors which give rise to corrosion fatigue that are associated with the localized melting and solidification of the weld overlay process. Coextruded coatings offer the potential for improved corrosion fatigue resistance since coextrusion is a solid state coating process. The corrosion and corrosion fatigue behavior of alloy 622 weld overlays and coextruded claddings was investigated using a Gleeble thermo-mechanical simulator retrofitted with a retort. The experiments were conducted at a constant temperature of 600°C using a simulated combustion gas of N2-10%CO-5%CO2-0.12%H 2S. An alternating stress profile was used with a minimum tensile stress of 0 MPa and a maximum tensile stress of 300 MPa (ten minute fatigue cycles). The results have demonstrated that the Gleeble can be used to successfully simulate the known corrosion fatigue cracking mechanism of Ni-based weld overlays in service. Multilayer corrosion scales developed on each of the claddings that consisted of inner and outer corrosion layers. The scales formed by the outward diffusion of cations and the inward diffusion of sulfur and oxygen anions. The corrosion fatigue behavior was influenced by the surface finish and the crack interactions. The initiation of a large number of corrosion fatigue cracks was not necessarily detrimental to the corrosion fatigue resistance. Finally, the as-received coextruded cladding exhibited the best corrosion fatigue resistance.

The influence of loading frequency on the high-temperature fatigue behavior of a Nicalon-fabric-reinforced polymer-derived ceramic-matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vanswijgenhoven, E.; Holmes, J.; Wevers, M.

Fiber-reinforced ceramic-matrix composites are under development for high-temperature structural applications. These applications involve fatigue loading under a wide range of frequencies. To date, high-temperature fatigue experiments have typically been performed at loading frequencies of 10 Hz or lower. At higher frequencies, a strong effect of loading frequency on fatigue life has been demonstrated for certain CMC`s tested at room temperature. The fatigue life of CMC`s with weak fiber-matrix interfaces typically decreases as the loading frequency increases. This decrease is attributed to frictional heating and frequency dependent interface and fiber damage. More recently, it has been shown that the room temperaturemore » fatigue life of a Nicalon-fabric-reinforced composite with a strong interface (SYLRAMIC{trademark}) appears to be independent of loading frequency. The high-temperature low-frequency fatigue behavior of the SYLRAMIC composite has also been investigated. For a fatigue peak stress {sigma}{sub peak} above a proportional limit stress of 70 MPa, the number of cycles to failure N{sub f} decreased with an increase in {sigma}{sub peak}. The material endured more than 10{sup 6} cycles for {sigma}{sub peak} below 70 MPa. In this paper, the influence of loading frequency on the high-temperature fatigue behavior of the SYLRAMIC composite is reported. It will be shown that the fatigue limit is unaffected by the loading frequency, that the number of fatigue cycles to failure N{sub f} increases with an increase in frequency, and that the time to failure t{sub f} decreases with an increase in frequency.« less

Fatigue Behavior of AM60B Subjected to Variable Amplitude Loading

NASA Astrophysics Data System (ADS)

Kang, H.; Kari, K.; Khosrovaneh, A. K.; Nayaki, R.; Su, X.; Zhang, L.; Lee, Y.-L.

Magnesium alloys are considered as an alternative material to reduce vehicle weight due to their weight which are 33% lighter than aluminum alloys. There has been a significant expansion in the applications of magnesium alloys in automotives components in an effort to improve fuel efficiency through vehicle mass reduction. In this project, a simple front shock tower of passenger vehicle is constructed with various magnesium alloys. To predict the fatigue behavior of the structure, fatigue properties of the magnesium alloy (AM60B) were determined from strain controlled fatigue tests. Notched specimens were also tested with three different variable amplitude loading profiles obtained from the shock tower of the similar size of vehicle. The test results were compared with various fatigue prediction results. The effect of mean stress and fatigue prediction method were discussed.

Contribution from motor unit firing adaptations and muscle co-activation during fatigue.

PubMed

Contessa, Paola; Letizi, John; De Luca, Gianluca; Kline, Joshua C

2018-03-14

The control of motor unit firing behavior during fatigue is still debated in the literature. Most studies agree that the central nervous system increases the excitation to the motoneuron pool to compensate for decreased force contributions of individual motor units and sustain muscle force output during fatigue. However, some studies claim that motor units may decrease their firing rates despite increased excitation, contradicting the direct relationship between firing rates and excitation that governs the voluntary control of motor units. To investigate whether the control of motor units in fact changes with fatigue, we measured motor unit firing behavior during repeated contractions of the first dorsal interosseous (FDI) muscle while concurrently monitoring the activation of surrounding muscles - including the flexor carpi radialis, extensor carpi radialis, and pronator teres. Across all subjects, we observed an overall increase in FDI activation and motor unit firing rates by the end of the fatigue task. However, in some subjects we observed increases in FDI activation and motor unit firing rates only during the initial phase of the fatigue task, followed by subsequent decreases during the late phase of the fatigue task while the co-activation of surrounding muscles increased. These findings indicate that the strategy for sustaining force output may occasionally change leading to increases in the relative activation of surrounding muscles while the excitation to the fatiguing muscle decreases. Importantly, irrespective of changes in the strategy for sustaining force output, the control properties regulating motor unit firing behavior remain unchanged during fatigue.

A study of microstructure, quasi-static response, fatigue, deformation and fracture behavior of high strength alloy steels

NASA Astrophysics Data System (ADS)

Kannan, Manigandan

The history of steel dates back to the 17th century and has been instrumental in the betterment of every aspect of our lives ever since, from the pin that holds the paper together to the Automobile that takes us to our destination steel touches everyone every day. Path breaking improvements in manufacturing techniques, access to advanced machinery and understanding of factors like heat treatment, corrosion resistance have aided in the advancement in the properties of steel in the last few years. In this dissertation document, the results of a study aimed at the influence of alloy chemistry, processing and influence of the quasi static and fatigue behavior of seven alloy steels is discussed. The microstructure of the as-received steel was examined and characterized for the nature and morphology of the grains and the presence of other intrinsic features in the microstructure. The tensile, cyclic fatigue and bending fatigue tests were done on a fully automated closed-loop servo-hydraulic test machine at room temperature. The failed samples of high strength steels were examined in a scanning electron microscope for understanding the fracture behavior, especially the nature of loading be it quasi static, cyclic fatigue or bending fatigue . The quasi static and cyclic fatigue fracture behavior of the steels examined coupled with various factors contributing to failure are briefly discussed in light of the conjoint and mutually interactive influences of intrinsic microstructural effects, nature of loading, and stress (load)-deformation-microstructural interactions.

Neuroprotective mechanism of losartan and its interaction with nimesulide against chronic fatigue stress.

PubMed

Kumar, Anil; Singh, Barinder; Mishra, Jitendriya; Sah, Sangeeta Pilkhwal; Pottabathini, Raghavender

2015-12-01

Potential role of angiotensin-II and cyclooxygenase have been suggested in the pathophysiology of chronic fatigue stress. The present study has been designed to evaluate the neuroprotective effect of losartan and its interaction with nimesulide against chronic fatigue stress and related complications in mice. In the present study, male Laca mice (20-30 g) were subjected to running wheel activity test session (RWATS) for 6 min daily for 21 days. Losartan, nimesulide and their combinations were administered daily for 21 days, 45 min before being subjected to RWATS. Various behavioral and biochemical and neuroinflammatory mediators were assessed subsequently. 21 days RWATS treatment significantly decreased number of wheel rotations/6 min indicating fatigue stress like behaviors as compared to naive group. 21 days treatment with losartan (10 and 20 mg/kg, ip), nimesulide (5 and 10 mg/kg, po) and their combinations significantly improved behavior [increased number of wheel rotations, reversal of post-exercise fatigue, locomotor activity, antianxiety-like behavior (number of entries, latency to enter and time spent in mirror chamber), and memory performance (transfer latency in plus-maze performance task)], biochemical parameters (reduced serum corticosterone, brain lipid peroxidation, nitrite concentration, acetylcholinesterase activity, restored reduced glutathione levels and catalase activity) as compared to RWATS control. Besides, TNF-α, CRP levels were significantly attenuated by these drugs and their combinations as compared to control. The present study highlights the role of cyclooxygenase modulation in the neuroprotective effect of losartan against chronic fatigue stress-induced behavioral, biochemical and cellular alterations in mice.

Exposure to bullying behaviors as a predictor of mental health problems among Norwegian nurses: results from the prospective SUSSH-survey.

PubMed

Reknes, Iselin; Pallesen, Ståle; Magerøy, Nils; Moen, Bente Elisabeth; Bjorvatn, Bjørn; Einarsen, Ståle

2014-03-01

The relationship between workplace bullying and mental health problems are well documented in previous cross-sectional studies, but knowledge on how this relationship develops over time is still scarce. The aim of this study was to explore the prospective relationship between exposure to bullying behaviors at baseline, and increased symptoms of mental health problems (anxiety, depression, fatigue) one year later. Furthermore, the reverse relationship was investigated. This is a prospective longitudinal study, where members of the Norwegian Nurses Organization answered identical questions regarding workplace bullying and mental health problems, at baseline (2008-2009) and follow-up (2010). Altogether, 1582 nurses completed both questionnaires. Hierarchical regression analyses indicated that exposure to bullying behaviors at baseline predicted subsequent increased symptoms of anxiety and fatigue, after adjusting for baseline symptoms of anxiety and fatigue respectively, age, gender, night work and job demands. Moreover, symptoms of anxiety, depression and fatigue at baseline predicted increased exposure to bullying behaviors one year later, after adjusting for exposure to bullying behaviors at baseline, age, gender, night work and job demands. In this study we find support for a reciprocal relationship between exposure to bullying behaviors and symptoms of anxiety and fatigue, respectively. Thus, the results may indicate a vicious circle where workplace bullying and mental health problems mutually affect each other negatively. Copyright © 2013 Elsevier Ltd. All rights reserved.

Fatique crack growth behavior of a single crystal alloy as observed through an in situ fatigue loading stage

NASA Technical Reports Server (NTRS)

Telesman, Jack; Kantzos, Peter

1988-01-01

An in situ fatigue loading stage inside a scanning electron microscope (SEM) was used to determine the fatigue crack growth behavior of a PWA 1480 single-crystal nickel-based superalloy. The loading stage permits real-time viewing of the fatigue damage processes at high magnification. The PWA 1480 single-crystal, single-edge notch specimens were tested with the load axis parallel to the (100) orientation. Two distinct fatigue failure mechanisms were identified. The crack growth rate differed substantially when the failure occurred on a single slip system in comparison to multislip system failure. Two processes by which crack branching is produced were identified and are discussed. Also discussed are the observed crack closure mechanisms.

High temperature low-cycle fatigue mechanisms in single crystals of nickel-based superalloy Mar-M 200

NASA Technical Reports Server (NTRS)

Milligan, W. W.; Jayaraman, N.

1984-01-01

Twenty three high temperature low-cycle fatigue tests were conducted on single crystals of the nickel-based superalloy Mar-M 200. Tests were conducted at 760 and 870 C. SEM fractography and transmission electron microscopy were used to determine mechanisms responsible for the observed orientation dependent fatigue behavior. It has been concluded that the plastic characteristics of the alloy lead to orientation-dependent strain hardening and fatigue lives at 760 C. At 870 C, the elastic characteristics of the alloy dominated the behavior, even though the plastic strain ranges were about the same as they were at 760 C. This led to orientation-dependent fatigue lives, but the trends were not the same as they were at 760 C.

Low cycle fatigue

NASA Technical Reports Server (NTRS)

Solomon, H. D. (Editor); Kaisand, L. R. (Editor); Halford, G. R. (Editor); Leis, B. N. (Editor)

1988-01-01

The papers contained in this volume focus on various aspects of low cycle fatigue, including cyclic deformation, crack propagation, high-temperature low cycle fatigue, microstructural defects, multiaxial and variable amplitude loading, and life prediction. Papers are presented on the low cycle fatigue of some aluminum alloys, prediction of crack growth under creep-fatigue loading conditions, high-temperature low cycle fatigue behavior and lifetime prediction of a nickel-base ODS alloy, and an integrated approach to creep-fatigue life prediction. Other topics discussed include thermal fatigue testing of coated monocrystalline superalloys, low cycle fatigue of Al-Mg-Si alloys, and the effect of superimposed stresses at high frequency on low cycle fatigue.

Low Cycle Fatigue Behavior of 316LN Stainless Steel Alloyed with Varying Nitrogen Content. Part II: Fatigue Life and Fracture Behavior

NASA Astrophysics Data System (ADS)

Prasad Reddy, G. V.; Sandhya, R.; Sankaran, S.; Mathew, M. D.

2014-10-01

Influence of nitrogen content on low cycle fatigue life and fracture behavior of 316LN stainless steel (SS) alloyed with 0.07 to 0.22 wt pct nitrogen is presented in this paper over a range of total strain amplitudes ( ±0.25 to 1.0 pct) in the temperature range from 773 K to 873 K (500 °C to 600 °C). The combined effect of nitrogen and strain amplitude on fatigue life is observed to be complex i.e., fatigue life either decreases/increases with increase in nitrogen content or saturates/peaks at 0.14 wt pct N depending on strain amplitude and temperature. Coffin-Manson plots (CMPs) revealed both single-slope and dual-slope strain-life curves depending on the test temperature and nitrogen content. 316LN SS containing 0.07 and 0.22 wt pct N showed nearly single-slope CMP at all test temperatures, while 316LN SS with 0.11 and 0.14 wt pct N exhibited marked dual-slope behavior at 773 K (500 °C) that changes to single-slope behavior at 873 K (600 °C). The changes in slope of CMP are found to be in good correlation with deformation substructural changes.

Cognitive Behavioral Training and Education for Spaceflight Operations

NASA Technical Reports Server (NTRS)

Moonmaw, Ronald

2011-01-01

Cognitive behavioral-training (CBT) is an evidence-based practice commonly used to help treat insomnia, and is part of NASA's countermeasure regimen for Fatigue Management. CBT addresses the life style and habits of individuals that are maladaptive to managing stress and fatigue. This includes addressing learned behavioral responses that may cause stress and lead to an increased sense of fatigue. While the initial cause of onset of fatigue in the individual may be no longer present, the perception and engrained anticipation of fatigue persist and cause an exaggerated state of tension. CBT combined with relaxation training allows the individual to unlearn the maladaptive beliefs and behaviors and replace them with routines and techniques that allow cognitive restructuring and resultant relief from stress. CBT allows for elimination in individuals of unwanted ruminating thoughts and anticipatory anxiety by, for example, training the individuals to practice stressful situations in a relaxed state. As a result of CBT, relaxation can be accomplished in many ways, such as progressive muscle relaxation, meditation and guided imagery. CBT is not therapy, but rather the synthesis of behavioral countermeasures. CBT utilizes progressive relaxation as a means of reinforcing educational and cognitive countermeasures. These countermeasures include: masking, elimination of distracting thoughts, anxiety control, split attention, cognitive restructuring and other advanced psychological techniques.

Addressing reverse osmosis fouling within water reclamation--a side-by-side comparison of low-pressure membrane pretreatments.

PubMed

Kent, Fraser C; Farahbakhsh, Khosrow

2011-06-01

A tertiary membrane filtration (TMF) pilot operating on secondary effluent and a membrane bioreactor (MBR) were setup in a side-by-side study as pretreatments for two identical reverse osmosis pilot systems. The water quality of the permeate from both low-pressure membrane pretreatment systems and the fouling rate of the reverse osmosis systems were compared to assess the capabilities of the two low-pressure membrane pretreatments to prevent organic fouling of the reverse osmosis systems. Both pretreatment pilots were setup using typical operating conditions (i.e., solids retention time and mixed-liquor suspended solids). A consistent difference in water quality and reverse osmosis performance was demonstrated during the 12-month study. The MBR permeate consistently had significantly lower total organic carbon (TOC) and chemical oxygen demand concentrations, but higher color and specific UV absorbance compared with the permeate from the TMF pretreatment. The pretreatment with the MBR gave an average reverse osmosis fouling rate over the entire study (0.27 Lmh/bar.month) that was less than half of the value found for the reverse osmosis with TMF pretreatment (0.60 Lmh/bar.month). A correlation of reverse osmosis feed TOC concentration with average reverse osmosis fouling rate also was established, independent of the pretreatment method used. Results from a cleaning analysis, energy dispersive spectroscopy, and fourier transformed infrared reflectometry confirmed that the foulants were primarily organic in nature. It is concluded that, for this type of application and setup, MBR systems present an advantage over tertiary membrane polishing of secondary effluent for reverse osmosis pretreatment.

Review on stress corrosion and corrosion fatigue failure of centrifugal compressor impeller

NASA Astrophysics Data System (ADS)

Sun, Jiao; Chen, Songying; Qu, Yanpeng; Li, Jianfeng

2015-03-01

Corrosion failure, especially stress corrosion cracking and corrosion fatigue, is the main cause of centrifugal compressor impeller failure. And it is concealed and destructive. This paper summarizes the main theories of stress corrosion cracking and corrosion fatigue and its latest developments, and it also points out that existing stress corrosion cracking theories can be reduced to the anodic dissolution (AD), the hydrogen-induced cracking (HIC), and the combined AD and HIC mechanisms. The corrosion behavior and the mechanism of corrosion fatigue in the crack propagation stage are similar to stress corrosion cracking. The effects of stress ratio, loading frequency, and corrosive medium on the corrosion fatigue crack propagation rate are analyzed and summarized. The corrosion behavior and the mechanism of stress corrosion cracking and corrosion fatigue in corrosive environments, which contain sulfide, chlorides, and carbonate, are analyzed. The working environments of the centrifugal compressor impeller show the behavior and the mechanism of stress corrosion cracking and corrosion fatigue in different corrosive environments. The current research methods for centrifugal compressor impeller corrosion failure are analyzed. Physical analysis, numerical simulation, and the fluid-structure interaction method play an increasingly important role in the research on impeller deformation and stress distribution caused by the joint action of aerodynamic load and centrifugal load.

The Cyclic Mechanical and Fatigue Properties of Ferroanelastic Beta Prime Gold Cadmium. Ph.D. Thesis. Final Report

NASA Technical Reports Server (NTRS)

Karz, R. S.

1973-01-01

The fatigue behavior of beta prime Au1.05Cd0.95 alloy was investigated and found to be exceptional for certain orientations with lives of 10,000 to 1,000,000 cycles at total strain amplitudes above 0.05 not uncommon. Fatigue lives were influenced principally by the stress level which controlled the amount of plastic deformation, and stress fatigue resistance was low compared with most metals. Failure always exhibited brittle characteristics. An algorithm was devised to predict mechanical behavior from the twin system orientations and was found in good agreement with experiment for longitudinal strains above 0.04. The cyclic mechanical properties were examined, and a model for the behavior was proposed utilizing previous theories of the restoring force and the Peierls-Nabarro stress for twinning and new concepts. Gold-cadmium was found to have certain strain fatigue resistant applications, particularly in electronics where the alloy's high electrical conductivity is utilized.

Mobile phone text messaging intervention to improve alertness and reduce sleepiness and fatigue during shiftwork among emergency medicine clinicians: study protocol for the SleepTrackTXT pilot randomized controlled trial.

PubMed

Patterson, Paul Daniel; Moore, Charity G; Weaver, Matthew D; Buysse, Daniel J; Suffoletto, Brian P; Callaway, Clifton W; Yealy, Donald M

2014-06-21

Mental and physical fatigue while at work is common among emergency medical services (EMS) shift workers. Extended shifts (for example 24 hours) and excessive amounts of overtime work increase the likelihood of negative safety outcomes and pose a challenge for EMS fatigue-risk management. Text message-based interventions are a potentially high-impact, low-cost platform for sleep and fatigue assessment and distributing information to workers at risk of negative safety outcomes related to sleep behaviors and fatigue. We will conduct a pilot randomized trial with a convenience sample of adult EMS workers recruited from across the United States using a single study website. Participants will be allocated to one of two possible arms for a 90-day study period. The intervention arm will involve text message assessments of sleepiness, fatigue, and difficulty with concentration at the beginning, during, and end of scheduled shifts. Intervention subjects reporting high levels of sleepiness or fatigue will receive one of four randomly selected intervention messages promoting behavior change during shiftwork. Control subjects will receive assessment only text messages. We aim to determine the performance characteristics of a text messaging tool for the delivery of a sleep and fatigue intervention. We seek to determine if a text messaging program with tailored intervention messages is effective at reducing perceived sleepiness and/or fatigue among emergency medicine clinician shift workers. Additional aims include testing whether a theory-based behavioral intervention, delivered by text message, changes 'alertness behaviors'. The SleepTrackTXT pilot trial could provide evidence of compliance and effectiveness that would support rapid widespread expansion in one of two forms: 1) a stand-alone program in the form of a tailored/individualized sleep monitoring and fatigue reduction support service for EMS workers; or 2) an add-on to a multi-component fatigue risk management program led and maintained by employers or by safety and risk management services. Clinicaltrials.gov NCT02063737, Registered on 10 January 2014.

Stress-related psychosocial factors at work, fatigue, and risky driving behavior in bus rapid transport (BRT) drivers.

PubMed

Useche, Sergio A; Ortiz, Viviola Gómez; Cendales, Boris E

2017-07-01

There is consistent scientific evidence that professional drivers constitute an occupational group that is highly exposed to work related stressors. Furthermore, several recent studies associate work stress and fatigue with unsafe and counterproductive work behaviors. This study examines the association between stress-related work conditions of Bus Rapid Transport (BRT) drivers and risky driving behaviors; and examines whether fatigue is a mechanism that mediates the association between the two. A sample of 524 male Bus Rapid Transit (BRT) operators were drawn from four transport companies in Bogotá, Colombia. The participants answered a survey which included an adapted version of the Driver Behavior Questionnaire (DBQ) for BRT operators, as well as the Effort-Reward Imbalance and Job Content Questionnaires, the Subjective Fatigue subscale of the Checklist Individual Strength (CIS) and the Need for Recovery after Work Scale (NFR). Utilizing Structural Equation Models (SEM) it was found that risky driving behaviors in BRT operators could be predicted through job strain, effort-reward imbalance and social support at work. It was also found that fatigue and need for recovery fully mediate the associations between job strain and risky driving, and between social support and risky driving, but not the association between effort/reward imbalance (ERI) and risky driving. The results of this study suggest that a) stress related working conditions (Job Strain, Social Support and ERI) are relevant predictors of risky driving in BRT operators, and b) that fatigue is the mechanism which links another kind of stress related to working conditions (job strain and low social support) with risky driving. The mechanism by which ERI increases risky driving in BRT operators remains unexplained. This research suggests that in addition to the individual centered stress-reduction occupational programs, fatigue management interventions aimed to changing some working conditions may reduce risky driving behaviors and promote safety in the professional drivers' jobs and on the road. Copyright © 2017 Elsevier Ltd. All rights reserved.

Flux and stable C and N isotope composition of sinking particles in the Ulleung Basin of the East/Japan Sea

NASA Astrophysics Data System (ADS)

Hyun Kwak, Jung; Han, Eunah; Hwang, Jeomshik; Kim, Young, II; Lee, Chung Il; Kang, Chang-Keun

2017-09-01

Seasonal variability of sinking fluxes of total mass (TMF), particulate organic carbon and nitrogen (POC and PON) was examined using sinking particles collected from sediment traps during July 2011 to December 2011, and December 2012 to June 2013 at an offshore channel site; and from November 2013 to August 2014 at a nearshore slope site of the Ulleung Basin in the East/Japan Sea. δ13C and δ15N values of sinking particles were measured to elucidate the major export processes of POC and PON. Annual TMF (112-638 g m-2 yr-1) and fluxes of POC and PON (9.6-32.1 g C m-2 yr-1 and 1.2-4.5 g N m-2 yr-1, respectively) in the Ulleung Basin corresponded to the upper limit of values reported for other open seas and oceans in the world. No great seasonal variability in both quantitative (TMF, and fluxes and contents of POC and PON) and qualitative (C/N ratios, and δ13C and δ15N values) estimates of vertical fluxes was observed, reflecting a steady standing stock of chlorophyll a in the upper part of water column. Furthermore, high contents of POC and PON and nearly constant δ13C and δ15N values in sinking particles collected in the sediment traps, indicate that primary production in the euphotic zone may be a good predictor of TMF and export flux of organic matter. In this regard, our pilot study points out the importance of high annual primary production and low water temperature (<1 °C) beneath the 200-m water depth, which would enable more sinking particles to be preserved during export process by limiting microbial decomposition activity in the water column, in determining the high annual flux of sinking particles in the Ulleung Basin (UB). A simple stable isotope mixing model of sinking particles indicates that despite a slight seasonal variation, the contribution of intact phytoplankton to sinking organic flux is significant to the POC and PON flux in the UB. Further continuous time series sediment trap experiments are proposed to estimate the contribution of allochthonus sources such as lateral advection through resuspended clay mineral, and aeolian and terrestrial inputs to the sedimentary flux.

An experimental method to quantify the impact fatigue behavior of rocks

NASA Astrophysics Data System (ADS)

Wu, Bangbiao; Kanopoulos, Patrick; Luo, Xuedong; Xia, Kaiwen

2014-07-01

Fatigue failure is an important failure mode of engineering materials. The fatigue behavior of both ductile and brittle materials has been under investigation for many years. While the fatigue failure of ductile materials is well established, only a few studies have been carried out on brittle materials. In addition, most fatigue studies on rocks are conducted under quasi-static loading conditions. To address engineering applications involving repeated blasting, this paper proposes a method to quantify the impact fatigue properties of rocks. In this method, a split Hopkinson pressure bar system is adopted to exert impact load on the sample, which is placed in a specially designed steel sleeve to limit the displacement of the sample and thus to enable the recovery of the rock after each impact. The method is then applied to Laurentian granite, which is fine-grained and isotropic material. The results demonstrate that this is a practicable means to conduct impact fatigue tests on rocks and other brittle solids.

Effect of solution treatment on the fatigue behavior of an as-forged Mg-Zn-Y-Zr alloy

NASA Astrophysics Data System (ADS)

Wang, S. D.; Xu, D. K.; Wang, B. J.; Han, E. H.; Dong, C.

2016-04-01

Through investigating and comparing the fatigue behavior of an as-forged Mg-6.7Zn-1.3Y-0.6Zr (wt.%) alloy before and after solid solution treatment (T4) in laboratory air, the effect of T4 treatment on fatigue crack initiation was disclosed. S-N curves illustrated that the fatigue strength of as-forged samples was 110 MPa, whereas the fatigue strength of T4 samples was only 80 MPa. Observations to fracture surfaces demonstrated that for as-forged samples, fatigue crack initiation sites were covered with a layer of oxide film. However, due to the coarse grain structure and the dissolution of MgZn2 precipitates, the activation and accumulation of {10-12} twins in T4 samples were much easier, resulting in the preferential fatigue crack initiation at cracked twin boundaries (TBs). Surface characterization demonstrated that TB cracking was mainly ascribed to the incompatible plastic deformation in the twinned area and nearby α-Mg matrix.

Prediction of corrosion fatigue crack initiation behavior of A7N01P-T4 aluminum alloy welded joints

NASA Astrophysics Data System (ADS)

An, J.; Chen, J.; Gou, G.; Chen, H.; Wang, W.

2017-07-01

Through investigating the corrosion fatigue crack initiation behavior of A7N01P-T4 aluminum alloy welded joints in 3.5 wt.% NaCl solution, corrosion fatigue crack initiation life is formulated as Ni = 6.97 × 1012[Δσeqv1.739 - 491.739]-2 and the mechanism of corrosion fatigue crack initiation is proposed. SEM and TEM tests revealed that several corrosion fatigue cracks formed asynchronously and the first crack does not necessarily develop into the leading crack. The uneven reticular dislocations produced by fatigue loading are prone to piling up and tangling near the grain boundaries or the second phases and form the “high dislocation-density region” (HDDR), which acts as an anode in microbatteries and dissolved to form small crack. Thus the etching pits, HDDR near the grain boundaries and second phases are confirmed as the main causes inducing the initiation of fatigue crack.

Fatigue in the Presence of Corrosion (Fatigue sous corrosion)

DTIC Science & Technology

1999-03-01

Fatigue Crack Growth Propagation of Aluminum Lithium cycle managers to safely delay repairs to a more appropriate Alloys " described the effect of... effects of service corrosion on fatigue lab tests with 2024 -T3, because 7178 life , if any, can be established in this was not available. However, we did not... life and the fatigue crack growth behavior of the cases where a structural member is the 2024 alloy was studied as well. stressed or fatigued

Is the notion of central fatigue based on a solid foundation?

PubMed

Contessa, Paola; Puleo, Alessio; De Luca, Carlo J

2016-02-01

Exercise-induced muscle fatigue has been shown to be the consequence of peripheral factors that impair muscle fiber contractile mechanisms. Central factors arising within the central nervous system have also been hypothesized to induce muscle fatigue, but no direct empirical evidence that is causally associated to reduction of muscle force-generating capability has yet been reported. We developed a simulation model to investigate whether peripheral factors of muscle fatigue are sufficient to explain the muscle force behavior observed during empirical studies of fatiguing voluntary contractions, which is commonly attributed to central factors. Peripheral factors of muscle fatigue were included in the model as a time-dependent decrease in the amplitude of the motor unit force twitches. Our simulation study indicated that the force behavior commonly attributed to central fatigue could be explained solely by peripheral factors during simulated fatiguing submaximal voluntary contractions. It also revealed important flaws regarding the use of the interpolated twitch response from electrical stimulation of the muscle as a means for assessing central fatigue. Our analysis does not directly refute the concept of central fatigue. However, it raises important concerns about the manner in which it is measured and about the interpretation of the commonly accepted causes of central fatigue and questions the very need for the existence of central fatigue. Copyright © 2016 the American Physiological Society.

High-Cycle Fatigue of High-Strength Low Alloy Steel Q345 Subjected to Immersion Corrosion for Mining Wheel Applications

NASA Astrophysics Data System (ADS)

Dicecco, Sante; Altenhof, William; Hu, Henry; Banting, Richard

2017-04-01

In an effort to better understand the impact of material degradation on the fatigue life of mining wheels made of a high-strength low alloy carbon steel (Q345), this study seeks to evaluate the effect of surface corrosion on the high-cycle fatigue behavior of the Q345 alloy. The fatigue behavior of the polished and corroded alloy was investigated. Following exposure to a 3.5 wt.% NaCl saltwater solution, polished and corroded fatigue specimens were tested using an R.R. Moore rotating-bending fatigue apparatus. Microstructural analyses via both optical microscopy and scanning electron microscopy (SEM) revealed that one major phase, α-iron phase, ferrite, and one minor phase, colony pearlite, existed in the extracted Q345 alloy. The results of the fatigue testing showed that the polished and corroded specimens had an endurance strength of approximately 295 and 222 MPa, respectively, at 5,000,000 cycles. The corroded surface condition resulted in a decrease in the fatigue strength of the Q345 alloy by 24.6%. Scanning electron microscope fractography indicated that failure modes for polished and corroded fatigue specimens were consistent in the high-cycle low loading fatigue regime. Conversely, SEM fractography of low-cycle high-loading fatigue specimens found considerable differences in fracture surfaces between the corroded and polished fatigue specimens.

Influence of stress systems and physical activity on different dimensions of fatigue in female fibromyalgia patients.

PubMed

Doerr, Johanna M; Fischer, Susanne; Nater, Urs M; Strahler, Jana

2017-02-01

Fatigue is a defining characteristic and one of the most debilitating features of fibromyalgia syndrome (FMS). The mechanisms underlying different dimensions of fatigue in FMS remain unclear. The aim of the current study was to test whether stress-related biological processes and physical activity modulate fatigue experience. Using an ambulatory assessment design, 26 female FMS patients reported general, mental, and physical fatigue levels at six time points per day for 14 consecutive days. Salivary cortisol and alpha-amylase were analyzed as markers of neuroendocrine functioning. Participants wore wrist actigraphs for the assessment of physical activity. Lower increases in cortisol after awakening predicted higher mean daily general and physical fatigue levels. Additionally, mean daily physical activity positively predicted next-day mean general fatigue. Levels of physical fatigue at a specific time point were positively associated with momentary cortisol levels. The increase in cortisol after awakening did not mediate the physical activity - fatigue relationship. There were no associations between alpha-amylase and fatigue. Our findings imply that both changes in hypothalamic-pituitary-adrenal axis activity and physical activity contribute to variance in fatigue in the daily lives of patients with FMS. This study helps to paint a clearer picture of the biological and behavioral underpinnings of fatigue in FMS and highlight the necessity of interdisciplinary treatment approaches targeting biological, behavioral and psychological aspects of FMS. Copyright © 2016 Elsevier Inc. All rights reserved.

Effects of applied stress ratio on the fatigue behavior of additively manufactured porous biomaterials under compressive loading.

PubMed

de Krijger, Joep; Rans, Calvin; Van Hooreweder, Brecht; Lietaert, Karel; Pouran, Behdad; Zadpoor, Amir A

2017-06-01

Additively manufactured (AM) porous metallic biomaterials are considered promising candidates for bone substitution. In particular, AM porous titanium can be designed to exhibit mechanical properties similar to bone. There is some experimental data available in the literature regarding the fatigue behavior of AM porous titanium, but the effect of stress ratio on the fatigue behavior of those materials has not been studied before. In this paper, we study the effect of applied stress ratio on the compression-compression fatigue behavior of selective laser melted porous titanium (Ti-6Al-4V) based on the diamond unit cell. The porous titanium biomaterial is treated as a meta-material in the context of this work, meaning that R-ratios are calculated based on the applied stresses acting on a homogenized volume. After morphological characterization using micro computed tomography and quasi-static mechanical testing, the porous structures were tested under cyclic loading using five different stress ratios, i.e. R = 0.1, 0.3, 0.5, 0.7 and 0.8, to determine their S-N curves. Feature tracking algorithms were used for full-field deformation measurements during the fatigue tests. It was observed that the S-N curves of the porous structures shift upwards as the stress ratio increases. The stress amplitude was the most important factor determining the fatigue life. Constant fatigue life diagrams were constructed and compared with similar diagrams for bulk Ti-6Al-4V. Contrary to the bulk material, there was limited dependency of the constant life diagrams to mean stress. The notches present in the AM biomaterials were the sites of crack initiation. This observation and other evidence suggest that the notches created by the AM process cause the insensitivity of the fatigue life diagrams to mean stress. Feature tracking algorithms visualized the deformation during fatigue tests and demonstrated the root cause of inclined (45°) planes of specimen failure. In conclusion, the R-ratio behavior of AM porous biomaterials is both quantitatively and qualitatively different from that of bulk materials. Copyright © 2016 Elsevier Ltd. All rights reserved.

Estimation of Axial Fretting Fatigue Life at Elevated Temperatures Using Critical Distance Theory

NASA Astrophysics Data System (ADS)

Majzoobi, G. H.; Azhdarzadeh, P.

Fretting fatigue life is traditionally estimated by experiment. The objective of this work is to introduce a special approach for estimation of axial fretting fatigue life at elevated temperatures from plain fatigue test based on the critical distance theory. The method uses Fatemi-Socie parameter as a multiaxial criterion to compute the stress multiaxiality on focus path. This method considers only elastic behavior for materials, and two characteristic diagrams are obtained from plain fatigue tests on two U-shaped and V-shaped notched specimens. The results showed reasonable agreement between the predictions by the proposed method and the experiments for ambient temperature. For elevated temperatures, the results indicated that the predicted fretting fatigue life was considerably overestimated in the low cycle fatigue (LCF) regime and underestimated in the high cycle fatigue (HCF) region with respect to experimental measurements. The reason for such discrepancy is believed to be due to the complex behavior of AL 7075-T6, which exhibits at elevated temperatures because of the problems such as aging, oxidation and reduction of strength.

Fatigue testing and damage development in continuous fiber reinforced metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1988-01-01

A general overview of the fatigue behavior of metal matrix composites (MMC) is presented. The first objective is to present experimental procedures and techniques for conducting a meaningful fatigue test to detect and quantify fatigue damage in MMC. These techniques include interpretation of stress-strain responses, acid etching of the matrix, edge replicas of the specimen under load, radiography, and micrographs of the failure surfaces. In addition, the paper will show how stiffness loss in continuous fiber reinforced metal matrix composites can be a useful parameter for detecting fatigue damage initiation and accumulation. Second, numerous examples of how fatigue damage can initiate and grow in various MMC are given. Depending on the relative fatigue behavior of the fiber and matrix, and the interface properties, the failure modes of MMC can be grouped into four categories: (1) matrix dominated, (2) fiber dominated, (3) self-similar damage growth, and (4) fiber/matrix interfacial failures. These four types of damage will be discussed and illustrated by examples with the emphasis on the fatigue of unnotched laminates.

Fatigue testing and damage development in continuous fiber reinforced metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1989-01-01

A general overview of the fatigue behavior of metal matrix composites (MMC) is presented. The first objective is to present experimental procedures and techniques for conducting a meaningful fatigue test to detect and quantify fatigue damage in MMC. These techniques include interpretation of stress-strain responses, acid etching of the matrix, edge replicas of the specimen under load, radiography, and micrographs of the failure surfaces. In addition, the paper will show how stiffness loss in continuous fiber reinforced metal matrix composites can be a useful parameter for detecting fatigue damage initiation and accumulation. Second, numerous examples of how fatigue damage can initiate and grow in various MMC are given. Depending on the relative fatigue behavior of the fiber and matrix, and the interface properties, the failure modes of MMC can be grouped into four categories: (1) matrix dominated, (2) fiber dominated, (3) self-similar damage growth, and (4) fiber/matrix interfacial failures. These four types of damage will be discussed and illustrated by examples with the emphasis on the fatigue of unnotched laminates.

Effects of load and thermal histories on mechanical behavior of materials; Proceedings of the Symposium, Denver, CO, Feb. 25, 26, 1987

DOE Office of Scientific and Technical Information (OSTI.GOV)

Liaw, P.K.; Nicholas, T.

This volume includes topics on fatigue crack propagation; isothermal and thermal-mechanical fatigue; and microstructure, fracture, and damage. Papers are presented on transients in fatigue crack growth, elevated-temperature fatigue crack propagation, the role of crack closure in crack retardation in P/M and I/M aluminum alloys, the acoustic interrogation of fatigue overload effects, and the effects of frequency and environment on crack growth in Inconel 718. Special attention is given to isothermal fatigue failure mechanisms in low-tin lead-based solder, the stress and strain controlled low-cycle fatigue of Pb-Sn solder for electronic packaging applications, load sequence effects on the deformation of isolated microplasticmore » grains, and thermal fatigue of stainless steel. Other papers are on the influence of thermal aging on the creep crack growth behavior of a Cr-Mo steel, the effect of cyclic loading on the fracture toughness of a modified 4340 steel, and the effects of hot rolling condition and boron microalloying on phase transformation and microstructure in niobium-bearing interstitial free steel.« less

A systems approach to solder joint fatigue in spacecraft electronic packaging

NASA Technical Reports Server (NTRS)

Ross, R. G., Jr.

1991-01-01

Differential expansion induced fatigue resulting from temperature cycling is a leading cause of solder joint failures in spacecraft. Achieving high reliability flight hardware requires that each element of the fatigue issue be addressed carefully. This includes defining the complete thermal-cycle environment to be experienced by the hardware, developing electronic packaging concepts that are consistent with the defined environments, and validating the completed designs with a thorough qualification and acceptance test program. This paper describes a useful systems approach to solder fatigue based principally on the fundamental log-strain versus log-cycles-to-failure behavior of fatigue. This fundamental behavior has been useful to integrate diverse ground test and flight operational thermal-cycle environments into a unified electronics design approach. Each element of the approach reflects both the mechanism physics that control solder fatigue, as well as the practical realities of the hardware build, test, delivery, and application cycle.

Effect of Surface Impulsive Thermal Loads on Fatigue Behavior of Constant Volume Propulsion Engine Combustor Materials

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Fox, Dennis S.; Miller, Robert A.; Ghosn, Louis J.; Kalluri, Sreeramesh

2004-01-01

The development of advanced high performance constant-volume-combustion-cycle engines (CVCCE) requires robust design of the engine components that are capable of enduring harsh combustion environments under high frequency thermal and mechanical fatigue conditions. In this study, a simulated engine test rig has been established to evaluate thermal fatigue behavior of a candidate engine combustor material, Haynes 188, under superimposed CO2 laser surface impulsive thermal loads (30 to 100 Hz) in conjunction with the mechanical fatigue loads (10 Hz). The mechanical high cycle fatigue (HCF) testing of some laser pre-exposed specimens has also been conducted under a frequency of 100 Hz to determine the laser surface damage effect. The test results have indicated that material surface oxidation and creep-enhanced fatigue is an important mechanism for the surface crack initiation and propagation under the simulated CVCCE engine conditions.

The effect of erosion on the fatigue limit of metallic materials for aerospace applications

NASA Astrophysics Data System (ADS)

Kordatos, E. Z.; Exarchos, D. A.; Matikas, T. E.

2018-03-01

This work deals with the study of the fatigue behavior of metallic materials for aerospace applications which have undergone erosion. Particularly, an innovative non-destructive methodology based on infrared lock-in thermography was applied on aluminum samples for the rapid determination of their fatigue limit. The effect of erosion on the structural integrity of materials can lead to a catastrophic failure and therefore an efficient assessment of the fatigue behavior is of high importance. Infrared thermography (IRT) as a non-destructive, non-contact, real time and full field method can be employed in order the fatigue limit to be rapidly determined. The basic principle of this method is the detection and monitoring of the intrinsically dissipated energy due to the cyclic fatigue loading. This methodology was successfully applied on both eroded and non-eroded aluminum specimens in order the severity of erosion to be evaluated.

Effect of Various Heat Treatment Processes on Fatigue Behavior of Tool Steel for Cold Forging Die

NASA Astrophysics Data System (ADS)

Jin, S. U.; Kim, S. S.; Lee, Y. S.; Kwon, Y. N.; Lee, J. H.

Effects of various heat treatment processes, including "Q/T (quenching and tempering)", "Q/CT/T (Quenching, cryogenic treatment and tempering)", "Q/T (quenching and tempering) + Ti-nitriding" and "Q/CT/T (Cryogenic treatment and tempering) + Ti-nitriding", on S-N fatigue behavior of AISI D2 tool steel were investigated. The optical micrographs and Vicker's hardness values at near surface and core area were examined for each specimen. Uniaxial fatigue tests were performed by using an electro-magnetic resonance fatigue testing machine at a frequency of 80 Hz and an R ratio of -1. The overall resistance to fatigue tends to decrease significantly with Ti-nitriding treatment compared to those for the general Q/T and Q/CT/T specimens. The reduced resistance to fatigue with Ti-nitriding is discussed based on the microstructural and fractographic analyses.

Evaluation of an mHealth intervention aiming to improve health-related behavior and sleep and reduce fatigue among airline pilots.

PubMed

van Drongelen, Alwin; Boot, Cécile Rl; Hlobil, Hynek; Twisk, Jos Wr; Smid, Tjabe; van der Beek, Allard J

2014-11-01

The aim of this study was to evaluate the effects of an mHealth intervention (intervention using mobile technology) consisting of tailored advice regarding exposure to daylight, sleep, physical activity, and nutrition, and aiming to improve health-related behavior, thereby reducing sleep problems and fatigue and improving health perception of airline pilots. A randomized controlled trial was conducted among 502 airline pilots. The intervention group was given access to both the MORE Energy mobile application (app) with tailored advice and a website with background information. The control group was directed to a website with standard information about fatigue. Health-related behavior, fatigue, sleep, and health perception outcomes were measured through online questionnaires at baseline and at three and six months after baseline. The effectiveness of the intervention was determined using linear and Poisson mixed model analyses. After six months, compared to the control group, the intervention group showed a significant improvement on fatigue (β= -3.76, P<0.001), sleep quality (β= -0.59, P=0.007), strenuous physical activity (β=0.17, P=0.028), and snacking behavior (β= -0.81, P<0.001). No significant effects were found for other outcome measures. The MORE Energy mHealth intervention reduced self-reported fatigue compared to a minimal intervention. Some aspects of health-related behavior (physical activity and snacking behavior) and sleep (sleep quality) improved as well, but most did not. The results show offering tailored advice through an mHealth intervention is an effective means to support employees who have to cope with irregular flight schedules and circadian disruption. This kind of intervention might therefore also be beneficial for other working populations with irregular working hours.

Deformation history and load sequence effects on cumulative fatigue damage and life predictions

NASA Astrophysics Data System (ADS)

Colin, Julie

Fatigue loading seldom involves constant amplitude loading. This is especially true in the cooling systems of nuclear power plants, typically made of stainless steel, where thermal fluctuations and water turbulent flow create variable amplitude loads, with presence of mean stresses and overloads. These complex loading sequences lead to the formation of networks of microcracks (crazing) that can propagate. As stainless steel is a material with strong deformation history effects and phase transformation resulting from plastic straining, such load sequence and variable amplitude loading effects are significant to its fatigue behavior and life predictions. The goal of this study was to investigate the effects of cyclic deformation on fatigue behavior of stainless steel 304L as a deformation history sensitive material and determine how to quantify and accumulate fatigue damage to enable life predictions under variable amplitude loading conditions for such materials. A comprehensive experimental program including testing under fully-reversed, as well as mean stress and/or mean strain conditions, with initial or periodic overloads, along with step testing and random loading histories was conducted on two grades of stainless steel 304L, under both strain-controlled and load-controlled conditions. To facilitate comparisons with a material without deformation history effects, similar tests were also carried out on aluminum 7075-T6. Experimental results are discussed, including peculiarities observed with stainless steel behavior, such as a phenomenon, referred to as secondary hardening characterized by a continuous increase in the stress response in a strain-controlled test and often leading to runout fatigue life. Possible mechanisms for secondary hardening observed in some tests are also discussed. The behavior of aluminum is shown not to be affected by preloading, whereas the behavior of stainless steel is greatly influenced by prior loading. Mean stress relaxation in strain control and ratcheting in load control and their influence on fatigue life are discussed. Some unusual mean strain test results are presented for stainless steel 304L, where in spite of mean stress relaxation fatigue lives were significantly longer than fully-reversed tests. Prestraining indicated no effect on either deformation or fatigue behavior of aluminum, while it induced considerable hardening in stainless steel 304L and led to different results on fatigue life, depending on the test control mode. In step tests for stainless steel 304L, strong hardening induced by the first step of a high-low sequence significantly affects the fatigue behavior, depending on the test control mode used. For periodic overload tests of stainless steel 340L, hardening due to the overloads was progressive throughout life and more significant than in high-low step tests. For aluminum, no effect on deformation behavior was observed due to periodic overloads. However, the direction of the overloads was found to affect fatigue life, as tensile overloads led to longer lives, while compressive overloads led to shorter lives. Deformation and fatigue behaviors under random loading conditions are also presented and discussed for the two materials. The applicability of a common cumulative damage rule, the linear damage rule, is assessed for the two types of material, and for various loading conditions. While the linear damage rule associated with a strain-life or stress-life curve is shown to be fairly accurate for life predictions for aluminum, it is shown to poorly represent the behavior of stainless steel, especially in prestrained and high-low step tests, in load control. In order to account for prior deformation effects and achieve accurate fatigue life predictions for stainless steel, parameters including both stress and strain terms are required. The Smith-Watson-Topper and Fatemi-Socie approaches, as such parameters, are shown to correlate most test data fairly accurately. For damage accumulation under variable amplitude loading, the linear damage rule associated with strain-life or stress-life curves can lead to inaccurate fatigue life predictions, especially for materials presenting strong deformation memory effect, such as stainless steel 304L. The inadequacy of this method is typically attributed to the linear damage rule itself. On the contrary, this study demonstrates that damage accumulation using the linear damage rule can be accurate, provided that the linear damage rule is used in conjunction with parameters including both stress and strain terms. By including both loading history and response of the material in damage quantification, shortcomings of the commonly used linear damage rule approach can be circumvented in an effective manner. In addition, cracking behavior was also analyzed under various loading conditions. Results on microcrack initiation and propagation are presented in relation to deformation and fatigue behaviors of the materials. Microcracks were observed to form during the first few percent of life, indicating that most of the fatigue life of smooth specimens is spent in microcrack formation and growth. Analyses of fractured specimens showed that microcrack formation and growth is dependent on the loading history, and less important in aluminum than stainless steel 304L, due to the higher toughness of this latter material.

Fatigue-Crack-Growth Behavior of Two Pipeline Steels

DOE PAGES

Chen, Bilin; Wang, Gongyao; Chen, Shuying; ...

2016-10-17

This paper focuses on studying the fatigue-crack-growth behavior of two types of pipeline steels, and investigating their microstructural differences, which could influence the fatigue behavior. For fatigue experiments, compact-tension (CT) specimens are employed. These two kinds of base pipeline steels are Alloy B [Fe-0.05C-1.52Mn-0.12Si-0.092Nb, weight percent (wt.%)] and Alloy C [(Fe- 0.04C-1.61Mn-0.14Si-0.096Nb, wt.%)]. They have been tested at various frequencies (10 Hz, 1 Hz, and 0.1 Hz) and different R ratios (0.1 and 0.5, R = P min./P max. where P min. is the minimum applied load, and P max. is the maximum applied load) in air. The effects ofmore » frequencies and R ratios on crackpropagation behavior are compared. The microstructures of fracture surfaces are investigated, using both scanning-electron microscopy (SEM) and transmission-electron microscopy (TEM). It is concluded that higher R ratios lead to faster crack-growth rates, while frequency does not have much influence on the fatigue-crack-growth rates. Moreover, Alloy B (Fe-0.05C-1.52Mn-0.12Si-0.092Nb, wt.%) tends to have better fatigue resistance than Alloy C (Fe-0.04C-1.61Mn-0.14Si-0.096Nb, wt.%) under various test conditions in air.« less

Fatigue-Crack-Growth Behavior of Two Pipeline Steels

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Bilin; Wang, Gongyao; Chen, Shuying

This paper focuses on studying the fatigue-crack-growth behavior of two types of pipeline steels, and investigating their microstructural differences, which could influence the fatigue behavior. For fatigue experiments, compact-tension (CT) specimens are employed. These two kinds of base pipeline steels are Alloy B [Fe-0.05C-1.52Mn-0.12Si-0.092Nb, weight percent (wt.%)] and Alloy C [(Fe- 0.04C-1.61Mn-0.14Si-0.096Nb, wt.%)]. They have been tested at various frequencies (10 Hz, 1 Hz, and 0.1 Hz) and different R ratios (0.1 and 0.5, R = P min./P max. where P min. is the minimum applied load, and P max. is the maximum applied load) in air. The effects ofmore » frequencies and R ratios on crackpropagation behavior are compared. The microstructures of fracture surfaces are investigated, using both scanning-electron microscopy (SEM) and transmission-electron microscopy (TEM). It is concluded that higher R ratios lead to faster crack-growth rates, while frequency does not have much influence on the fatigue-crack-growth rates. Moreover, Alloy B (Fe-0.05C-1.52Mn-0.12Si-0.092Nb, wt.%) tends to have better fatigue resistance than Alloy C (Fe-0.04C-1.61Mn-0.14Si-0.096Nb, wt.%) under various test conditions in air.« less

Fatigue during breast cancer radiotherapy: an initial randomized study of cognitive-behavioral therapy plus hypnosis.

PubMed

Montgomery, Guy H; Kangas, Maria; David, Daniel; Hallquist, Michael N; Green, Sheryl; Bovbjerg, Dana H; Schnur, Julie B

2009-05-01

The study purpose was to test the effectiveness of a psychological intervention combining cognitive-behavioral therapy and hypnosis (CBTH) to treat radiotherapy-related fatigue. Women (n = 42) scheduled for breast cancer radiotherapy were randomly assigned to receive standard medical care (SMC) (n = 20) or a CBTH intervention (n = 22) in addition to SMC. Participants assigned to receive CBTH met individually with a clinical psychologist. CBTH participants received training in hypnosis and CBT. Participants assigned to the SMC control condition did not meet with a study psychologist. Fatigue was measured on a weekly basis by using the fatigue subscale of the Functional Assessment of Chronic Illness Therapy (FACIT) and daily using visual analogue scales. Multilevel modeling indicated that for weekly FACIT fatigue data, there was a significant effect of the CBTH intervention on the rate of change in fatigue (p < .05), such that on average, CBTH participants' fatigue did not increase over the course of treatment, whereas control group participants' fatigue increased linearly. Daily data corroborated the analyses of weekly data. The results suggest that CBTH is an effective means for controlling and potentially preventing fatigue in breast cancer radiotherapy patients.

Very High Cycle Fatigue Behavior of a Directionally Solidified Ni-Base Superalloy DZ4

PubMed Central

Nie, Baohua; Zhao, Zihua; Liu, Shu; Chen, Dongchu; Ouyang, Yongzhong; Hu, Zhudong; Fan, Touwen; Sun, Haibo

2018-01-01

The effect of casting pores on the very high cycle fatigue (VHCF) behavior of a directionally solidified (DS) Ni-base superalloy DZ4 is investigated. Casting and hot isostatic pressing (HIP) specimens were subjected to very high cycle fatigue loading in an ambient atmosphere. The results demonstrated that the continuously descending S-N curves were exhibited for both the casting and HIP specimens. Due to the elimination of the casting pores, the HIP samples had better fatigue properties than the casting samples. The subsurface crack initiated from the casting pore in the casting specimens at low stress amplitudes, whereas fatigue crack initiated from crystallographic facet decohesion for the HIP specimens. When considering the casting pores as initial cracks, there exists a critical stress intensity threshold ranged from 1.1 to 1.3 MPam, below which fatigue cracks may not initiate from the casting pores. Furthermore, the effect of the casting pores on the fatigue limit is estimated based on a modified El Haddad model, which is in good agreement with the experimental results. Fatigue life for both the casting and HIP specimens is well predicted using the Fatigue Indicator Parameter (FIP) model. PMID:29320429

Fatigue properties of type 316LN stainless steel in air and mercury

NASA Astrophysics Data System (ADS)

Strizak, J. P.; Tian, H.; Liaw, P. K.; Mansur, L. K.

2005-08-01

An extensive fatigue testing program on 316LN stainless steel was recently carried out to support the design of the mercury target container for the spallation neutron source (SNS) that is currently under construction at the Oak Ridge National Laboratory in the United States. The major objective was to determine the effects of mercury on fatigue behavior. The S- N fatigue behavior of 316LN stainless steel is characterized by a family of bilinear fatigue curves which are dependent on frequency, environment, mean stress and cold work. Generally, fatigue life increases with decreasing stress and levels off in the high cycle region to an endurance limit below which the material will not fail. For fully reversed loading as well as tensile mean stress loading conditions mercury had no effect on endurance limit. However, at higher stresses a synergistic relationship between mercury and cyclic loading frequency was observed at low frequencies. As expected, fatigue life decreased with decreasing frequency, but the response was more pronounced in mercury compared with air. As a result of liquid metal embrittlement (LME), fracture surfaces of specimens tested in mercury showed widespread brittle intergranular cracking as opposed to typical transgranular cracking for specimens tested in air. For fully reversed loading (zero mean stress) the effect of mercury disappeared as frequency increased to 10 Hz. For mean stress conditions with R-ratios of 0.1 and 0.3, LME was still evident at 10 Hz, but at 700 Hz the effect of mercury had disappeared ( R = 0.1). Further, for higher R-ratios (0.5 and 0.75) fatigue curves for 10 Hz showed no environmental effect. Finally, cold working (20%) increased tensile strength and hardness, and improved fatigue resistance. Fatigue behavior at 10 and 700 Hz was similar and no environmental effect was observed.

Association between poor sleep, fatigue, and safety outcomes in Emergency Medical Services providers

PubMed Central

Patterson, P. Daniel; Weaver, Matthew D.; Frank, Rachel C.; Warner, Charles W.; Martin-Gill, Christian; Guyette, Francis X.; Fairbanks, Rollin J.; Hubble, Michael W.; Songer, Thomas J.; Callaway, Clifton W.; Kelsey, Sheryl F.; Hostler, David

2011-01-01

Objective To determine the association between poor sleep quality, fatigue, and self-reported safety outcomes among Emergency Medical Services (EMS) workers. Methods We used convenience sampling of EMS agencies and a cross-sectional survey design. We administered the 19-item Pittsburgh Sleep Quality Index (PSQI), 11-item Chalder Fatigue Questionnaire (CFQ), and 44-item EMS Safety Inventory (EMS-SI) to measure sleep quality, fatigue, and safety outcomes, respectively. We used a consensus process to develop the EMS-SI, which was designed to capture three composite measurements of EMS worker injury, medical errors and adverse events (AE), and safety compromising behaviors. We used hierarchical logistic regression to test the association between poor sleep quality, fatigue, and three composite measures of EMS worker safety outcomes. Results We received 547 surveys from 30 EMS agencies (a 35.6% mean agency response rate). The mean PSQI score exceeded the benchmark for poor sleep (6.9, 95%CI 6.6, 7.2). Greater than half of respondents were classified as fatigued (55%, 95%CI 50.7, 59.3). Eighteen percent of respondents reported an injury (17.8%, 95%CI 13.5, 22.1), forty-one percent a medical error or AE (41.1%, 95%CI 36.8, 45.4), and 89% (95%CI 87, 92) safety compromising behaviors. After controlling for confounding, we identified 1.9 greater odds of injury (95%CI 1.1, 3.3), 2.2 greater odds of medical error or AE (95%CI 1.4, 3.3), and 3.6 greater odds of safety compromising behavior (95%CI 1.5, 8.3) among fatigued respondents versus non-fatigued respondents. Conclusions In this sample of EMS workers, poor sleep quality and fatigue is common. We provide preliminary evidence of an association between sleep quality, fatigue, and safety outcomes. PMID:22023164

Associations between heavy-vehicle driver compensation methods, fatigue-related driving behavior, and sleepiness.

PubMed

Thompson, Jason; Stevenson, Mark

2014-01-01

There has been growing recognition that broader economic and organizational factors play a role in creating work environments that facilitate high-risk driving behavior. This study investigates the association between compensation methods for drivers, fatigue-related driving behavior, and sleepiness among Australian heavy-vehicle drivers. Specifically, we hypothesized that piece-rate compensation methods linked to performance outcomes would be associated with greater levels of fatigue-related driving behaviors and sleepiness. We examined data from a random sample of 346 long-haul heavy-vehicle drivers who had not been involved in a crash. A 40-min interview was conducted that elicited information regarding driver demographics, truck characteristics, and compensation arrangements. Specific details about drivers' behavior on their most recent trip including load(s) carried, distances driven, hours driven, rest breaks, and hours of sleep on the previous night were taken. The interview also included a standardized assessment of sleepiness using the Epworth Sleepiness Scale (ESS). A multivariate analysis of covariance demonstrated a significant multivariate effect for compensation methods across the combined, fatigue-related driving behavior dependent variables, F (10, 676)=2.80, p<.01. Between-subject effects demonstrated significant association between compensation methods and 4 of 5 fatigue-related variables under study, including kilometers driven per day, F (2, 340)=7.75, p<.001, hours driven per day, F (2, 341)=2.64, p<.05, total hours worked per week, F (2, 340)=5.27, p<.01, and mean driving time between breaks, F (2, 341)=4.45, p<.05. Post hoc tests revealed that piece-rate compensation methods were associated with higher levels of fatigue-related driving than non-piece-rate methods. Follow-up analysis also revealed higher caffeine and amphetamines use among piece-rate drivers for the purpose of staying awake while driving. Despite this, no association between compensation methods and sleepiness were revealed. RESULTS confirmed that performance-based compensation methods are associated with work practices that may exacerbate driving behaviors associated with fatigue. Despite this finding, however, performance-based compensation methods were not associated with higher levels of sleepiness. This highlights the presence of potential differences in self-selection, operational, or fatigue management practices that may be common to drivers paid under various methods. Implications of these results for safety policy and future safety research within the heavy-vehicle industry are discussed.

Decision fatigue: A conceptual analysis.

PubMed

Pignatiello, Grant A; Martin, Richard J; Hickman, Ronald L

2018-03-01

Decision fatigue is an applicable concept to healthcare psychology. Due to a lack of conceptual clarity, we present a concept analysis of decision fatigue. A search of the term "decision fatigue" was conducted across seven research databases, which yielded 17 relevant articles. The authors identified three antecedent themes (decisional, self-regulatory, and situational) and three attributional themes (behavioral, cognitive, and physiological) of decision fatigue. However, the extant literature failed to adequately describe consequences of decision fatigue. This concept analysis provides needed conceptual clarity for decision fatigue, a concept possessing relevance to nursing and allied health sciences.

Strain-controlled fatigue behaviors of porous PLA-based scaffolds by 3D-printing technology.

PubMed

Gong, Baoming; Cui, Shaohua; Zhao, Yun; Sun, Yongtao; Ding, Qian

2017-12-01

In the study, the low-cycle fatigue behaviors of 3D-printed poly lactic acid (PLA) scaffolds with 60% porosity and two kinds of geometrical pores were investigated under strain-controlled loading. The obtained Δε a -N f curves were fitted by Coffin-Manson relation. The mechanical stability of the porous structure under cyclic loading was studied. Both kinds of specimens undergo the strain softening after the initial cyclic hardening. The scaffold with circular pore exhibits stable resistance to the fatigue damage which is desirable for bone repairing. Regarding to the accumulation of inelastic deformation, the triangular-scaffold is more sensitive to the cyclic load. The superior fatigue behaviors of the scaffold with circular pore is attributed to homogeneous distribution of the applied mechanical stress and diminishing stress concentration by the introduction of circular pore.

Composite materials: Fatigue and fracture. Vol. 3

NASA Technical Reports Server (NTRS)

O'Brien, T. K. (Editor)

1991-01-01

The present volume discusses topics in the fields of matrix cracking and delamination, interlaminar fracture toughness, delamination analysis, strength and impact characteristics, and fatigue and fracture behavior. Attention is given to cooling rate effects in carbon-reinforced PEEK, the effect of porosity on flange-web corner strength, mode II delamination in toughened composites, the combined effect of matrix cracking and free edge delamination, and a 3D stress analysis of plain weave composites. Also discussed are the compression behavior of composites, damage-based notched-strength modeling, fatigue failure processes in aligned carbon-epoxy laminates, and the thermomechanical fatigue of a quasi-isotropic metal-matrix composite.

A microstructurally based model of solder joints under conditions of thermomechanical fatigue

DOE Office of Scientific and Technical Information (OSTI.GOV)

Frear, D.R.; Burchett, S.N.; Rashid, M.M.

The thermomechanical fatigue failure of solder joints in increasingly becoming an important reliability issue. In this paper we present two computational methodologies that have been developed to predict the behavior of near eutectic Sn-Pb solder joints under fatigue conditions that are based on metallurgical tests as fundamental input for constitutive relations. The two-phase model mathematically predicts the heterogeneous coarsening behavior of near eutectic Sn-Pb solder. The finite element simulations from this model agree well with experimental thermomechanical fatigue tests. The simulations show that the presence of an initial heterogeneity in the solder microstructure could significantly degrade the fatigue lifetime. Themore » single phase model is a computational technique that was developed to predict solder joint behavior using materials data for constitutive relation constants that could be determined through straightforward metallurgical experiments. A shear/torsion test sample was developed to impose strain in two different orientations. Materials constants were derived from these tests and the results showed an adequate fit to experimental results. The single-phase model could be very useful for conditions where microstructural evolution is not a dominant factor in fatigue.« less

Corrosion Fatigue of Metals in Marine Environments

DTIC Science & Technology

1981-07-01

Fatigue of Alloys 2014-T6 and 2024 -T4 in Air and Artificial Seawater I62 Fatigue Life of 2024 -T4 Aluminum Alloy Specimens... life was still considerably reduced. The effect of prior corrosion pitting on the fatigue life of Alloy 2024 -T4 was investigated by Harmsworth.215...Harmsworth, C. L, " Effect of Corrosion on the Fatigue Behavior of 2024 -T4 Aluminum Alloy ",

Improved High-Cycle Fatigue (HCF) Life Prediction

DTIC Science & Technology

2001-01-01

fatigue in 2024 - T351 aluminum alloy ’, Wear 221, 24-36. Appendix 6C CHARACTERIZATION OF FRETTING FATIGUE INITIATED CRACKS P.J. Golden A.F...0.8. To evaluate the effects of surface residual stresses on notch fatigue life , shot peened specimens were tested at R = -1.0 and 0.1. Data in...Behavior - Response • The undamaged fatigue test program demonstrates the sensitivity of surface effects (for different

Accelerated fatigue durability of a high performance composite

NASA Technical Reports Server (NTRS)

Rotem, A.

1982-01-01

The fatigue behavior of multidirectional graphite-epoxy laminates was analyzed theoretically and experimentally in an effort to establish an accelerated testing methodology. Analysis of the failure mechanism in fatigue of the laminates led to the determination of the failure mode governing fracture. The nonlinear, cyclic-dependent shear modulus was used to calculate the changing stress field in the laminate during the fatigue loading. Fatigue tests were performed at three different temperatures: 25 C, 74 C, and 114 C. The prediction of the S-N curves was made based on the artificial static strength artificial static strength at a reference temperature and the fatigue functions associated with them. The prediction of an S-N curve at other temperatures was performed using shifting factors determined for the specific failure mode. For multidirectional laminates, different S-N curves at different temperatures could be predicted using these shifting factors. Different S-N curves at different temperatures occur only when the fatigue failure mode is matrix dominated. It was found that whenever the fatigue failure mode is fiber dominated, temperature, over the range investigated, had no influence on the fatigue life. These results permit the prediction of long-time, low temperature fatigue behavior from data obtained in short time, high temperature testing, for laminates governed by a matrix failure mode.

Four-point-bending-fatigue behavior of the Zr-based Vitreloy 105 bulk metallic glass

DOE Office of Scientific and Technical Information (OSTI.GOV)

Morrison, M. L.; Buchanan, R. A.; Liaw, Peter K

The purpose of this study was to make a direct comparison between four-point-bending and uniaxial fatigue tests with the Zr{sub 52.5}Cu{sub 17.9}Ni{sub 14.6}Al{sub 10.0}Ti{sub 5.0} (at.%) BMG alloy (Vitreloy 105). The fatigue lifetimes in four-point bending were found to be greater than those reported in uniaxial testing. However, the fatigue-endurance limit found in four-point bending was slightly less than that reported for uniaxial fatigue. Thus, the significant differences between fatigue studies in the literature are not likely due to this difference in testing geometry. On the contrary, the fatigue lifetimes were found to be highly dependent upon surface defects andmore » material quality. The four-point-bending-fatigue performance of the Vit 105 alloy was found to be greater than most BMGs and similar to the 300 M high-strength steel and other crystalline alloys in spite of not being 'perfectly amorphous.' Due to the detrimental effects of these inhomogeneities and wear at the supporting pins, this fatigue behavior can be assumed to be a conservative estimate of the potential fatigue performance of a perfectly amorphous and homogeneous BMG.« less

Intrinsically higher fatigue cracking resistance of the penetrable and movable incoherent twin boundary

NASA Astrophysics Data System (ADS)

Li, L. L.; Zhang, P.; Zhang, Z. J.; Zhang, Z. F.

2014-01-01

Incoherent twin boundaries (ITBs) are widespread and play a crucial role in unidirectional deformation behavior of materials, however, the intrinsic role of individual ITB under cyclic loading remains elusive. Here we show the fatigue cracking behavior of Cu bicrystal with an ITB as its sole interface for the first time. The slip bands (SBs) could transfer through the ITB; meanwhile, the ITB could migrate with the motion of partial dislocations. Both the penetrability and mobility contribute to the higher fatigue cracking resistance of the ITB and hence the fatigue crack nucleates along the SBs preferentially. These new findings not only shed light on the fatigue cracking mechanisms of a penetrable boundary with direct evidence but also could provide important implications for future interfacial optimization of metallic materials.

Fatigue In Continuous-Fiber/Metal-Matrix Composites

NASA Technical Reports Server (NTRS)

Johnson, William S.

1992-01-01

Report describes experimental approaches to quantification of fatigue damage in metal-matrix composites (MMC's). Discusses number of examples of development of damage and failure along with associated analytical models of behavior of MMC. Objectives of report are twofold. First, present experimental procedures and techniques for conducting meaningful fatigue tests to detect and quantify fatigue damage in MMC's. Second, present examples of how fatigue damage initiated and grows in various MMC's. Report furnishes some insight into what type of fatigue damage occurs and how damage quantified.

Fatigue Behavior of an Advanced SiC/SiC Composite at Elevated Temperature in Air and in Steam

DTIC Science & Technology

2009-12-01

specimens tested in salt fog achieved fatigue run-out. However, a significant decrease in fatigue life was observed for fatigue stresses ≥ 100 MPa...fatigue stress level approached the proportional limit. The reduction is fatigue life was attributed to the increased matrix cracking near the...oxidation of any free silicon remaining after production using methods such as melt infiltration, and the SiC itself as temperatures near 1000 ºC. These

Differences in the Microstructure and Fatigue Properties of Dentin Between Residents of North and South America

PubMed Central

Ivancik, J.; Naranjo, M.; Correa, S.; Ossa, A.; Tay, F.R.; Pashley, D.H.; Arola, D.

2014-01-01

Spatial variations in the microstructure of dentin contribute to its mechanical behavior. Objective The objective of this investigation was to compare the microstructure and fatigue behavior of dentin from donors of two different countries. Methods Caries-free third molars were obtained from dental practices in Colombia, South America and the US to assemble two age-matched samples. The microstructure of the coronal dentin was evaluated at three characteristic depths (i.e. deep, middle and superficial dentin) using scanning electron microscopy and image processing techniques. The mechanical behavior of dentin in these three regions was evaluated by the fatigue crack growth resistance. Cyclic crack growth was achieved in-plane with the dentin tubules and the fatigue crack growth behavior was characterized in terms of the stress intensity threshold and the Paris Law parameters. Results There was no difference in the tubule density between the dentin of patients from the two countries. However, there were significant differences (p≤0.05) in the tubule lumen diameters between the two groups in the deep and peripheral regions. In regards to the fatigue resistance, there was a significant increase (p≤0.05) in threshold stress intensity range, and a significant decrease in fatigue crack growth coefficient with increasing distance from the pulp in teeth from the US donors. In contrast, these properties were independent of location for the dentin of teeth from the Colombian donors. Conclusions The microstructure of dentin and its mechanical behavior appear to be a function of patient background, which may include environmental factors and/or ethnicity. PMID:24960115

Computer simulation of solder joint failure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Burchett, S.N.; Frear, D.R.; Rashid, M.M.

The thermomechanical fatigue failure of solder joints is increasingly becoming an important reliability issue for electronic packages. The purpose of this Laboratory Directed Research and Development (LDRD) project was to develop computational tools for simulating the behavior of solder joints under strain and temperature cycling, taking into account the microstructural heterogeneities that exist in as-solidified near eutectic Sn-Pb joints, as well as subsequent microstructural evolution. The authors present two computational constitutive models, a two-phase model and a single-phase model, that were developed to predict the behavior of near eutectic Sn-Pb solder joints under fatigue conditions. Unique metallurgical tests provide themore » fundamental input for the constitutive relations. The two-phase model mathematically predicts the heterogeneous coarsening behavior of near eutectic Sn-Pb solder. The finite element simulations with this model agree qualitatively with experimental thermomechanical fatigue tests. The simulations show that the presence of an initial heterogeneity in the solder microstructure could significantly degrade the fatigue lifetime. The single-phase model was developed to predict solder joint behavior using materials data for constitutive relation constants that could be determined through straightforward metallurgical experiments. Special thermomechanical fatigue tests were developed to give fundamental materials input to the models, and an in situ SEM thermomechanical fatigue test system was developed to characterize microstructural evolution and the mechanical behavior of solder joints during the test. A shear/torsion test sample was developed to impose strain in two different orientations. Materials constants were derived from these tests. The simulation results from the two-phase model showed good fit to the experimental test results.« less

Cognitive Behavior Therapy to Treat Sleep Disturbance and Fatigue After Traumatic Brain Injury: A Pilot Randomized Controlled Trial.

PubMed

Nguyen, Sylvia; McKay, Adam; Wong, Dana; Rajaratnam, Shantha M; Spitz, Gershon; Williams, Gavin; Mansfield, Darren; Ponsford, Jennie L

2017-08-01

To evaluate the efficacy of adapted cognitive behavioral therapy (CBT) for sleep disturbance and fatigue in individuals with traumatic brain injury (TBI). Parallel 2-group randomized controlled trial. Outpatient therapy. Adults (N=24) with history of TBI and clinically significant sleep and/or fatigue complaints were randomly allocated to an 8-session adapted CBT intervention or a treatment as usual (TAU) condition. Cognitive behavior therapy. The primary outcome was the Pittsburgh Sleep Quality Index (PSQI) posttreatment and at 2-month follow-up. Secondary measures included the Insomnia Severity Index, Fatigue Severity Scale, Brief Fatigue Inventory (BFI), Epworth Sleepiness Scale, and Hospital Anxiety and Depression Scale. At follow-up, CBT recipients reported better sleep quality than those receiving TAU (PSQI mean difference, 4.85; 95% confidence interval [CI], 2.56-7.14). Daily fatigue levels were significantly reduced in the CBT group (BFI difference, 1.54; 95% CI, 0.66-2.42). Secondary improvements were significant for depression. Large within-group effect sizes were evident across measures (Hedges g=1.14-1.93), with maintenance of gains 2 months after therapy cessation. Adapted CBT produced greater and sustained improvements in sleep, daily fatigue levels, and depression compared with TAU. These pilot findings suggest that CBT is a promising treatment for sleep disturbance and fatigue after TBI. Copyright © 2017 American Congress of Rehabilitation Medicine. Published by Elsevier Inc. All rights reserved.

Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under the strain controlled mode

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sanders, B.P.; Mall, S.; Dennis, L.B.

1997-10-01

A study was conducted to investigate the fatigue behavior of a cross-ply metal matrix composite subjected to fully-reversed, strain-controlled fatigue cycling at elevated temperature. The stress-strain response, maximum and minimum stresses, and modulus during cycling were analyzed to characterize the macro-mechanical behavior. Additionally, microscopy and fractography were conducted to identify damage mechanisms. Damage always initiated in the 90 deg plies, but the governing factor in the fatigue life was damage in the 0 deg plies. The dominant failure mode was fracturing of fibers in the 0 deg plies when the maximum strain was greater than 0.55%, but the dominant failuremore » mode was matrix cracking when the maximum strain was less than 0.55%. Combining the fatigue life data with the macro-mechanical and microscopic observations, a fatigue life diagram was developed and partitioned into three regions. These regions showed relationships between the maximum applied strain and the dominant damage mechanisms. Also, on a strain range basis, the fatigue lives of the specimens tested under the strain-controlled mode in this study were compared with its counterpart under the load-controlled mode of the previous study. It was found that the fatigue lives for these two conditions were the same within the experimental scatter. The MMC tested in this investigation was the Ti-15V-3Cr-3Al-3Sn titanium alloy reinforced with 36 volume percent of silicon carbide fibers (SCS-6).« less

Fatigue Analysis of Magnesium Alloys Components for Car Industry

NASA Astrophysics Data System (ADS)

Marsavina, Liviu; Rusu, Lucian; Șerban, Dan Andrei; Negru, Radu Marcel; Cernescu, Anghel

2017-12-01

The use of magnesium alloys in the automotive industry increased in the last decade because of their low weight and relative good mechanical properties. However, the variable loading conditions require a good fatigue behavior. This paper summaries the fatigue properties of magnesium alloys and presents new fatigue curve results for die cast AM50 magnesium alloy.

Crack tip field and fatigue crack growth in general yielding and low cycle fatigue

NASA Technical Reports Server (NTRS)

Minzhong, Z.; Liu, H. W.

1984-01-01

Fatigue life consists of crack nucleation and crack propagation periods. Fatigue crack nucleation period is shorter relative to the propagation period at higher stresses. Crack nucleation period of low cycle fatigue might even be shortened by material and fabrication defects and by environmental attack. In these cases, fatigue life is largely crack propagation period. The characteristic crack tip field was studied by the finite element method, and the crack tip field is related to the far field parameters: the deformation work density, and the product of applied stress and applied strain. The cyclic carck growth rates in specimens in general yielding as measured by Solomon are analyzed in terms of J-integral. A generalized crack behavior in terms of delta is developed. The relations between J and the far field parameters and the relation for the general cyclic crack growth behavior are used to analyze fatigue lives of specimens under general-yielding cyclic-load. Fatigue life is related to the applied stress and strain ranges, the deformation work density, crack nucleus size, fracture toughness, fatigue crack growth threshold, Young's modulus, and the cyclic yield stress and strain. The fatigue lives of two aluminum alloys correlate well with the deformation work density as depicted by the derived theory. The general relation is reduced to Coffin-Manson low cycle fatigue law in the high strain region.

Fatigue and shear behavior of HPC bulb-tee girders: final report.

DOT National Transportation Integrated Search

2005-02-01

Five 96-ft. (29.3-m) long, 72-in. (1.83-m) deep, precast, pretensioned bulb-tee girders were tested to evaluate their behavior under flexural fatigue. Three of the girders were also tested to measure their static shear strength. One girder was tested...

Fatigue and shear behavior of HPC bulb-tee girders : interim report.

DOT National Transportation Integrated Search

2003-10-01

Three 96-ft (29.3-m) long, 72-in. (1.83-m) deep, precast, pretensioned bulb-tee girders were tested to evaluate behavior under flexural fatigue and static shear loadings. The three girders had a design concrete compressive strength of 10,000 psi (69....

Effects of Frequency and Environment on Fatigue Behavior of an Oxide-Oxide Ceramic Matrix Composite at 1200 Deg. C

DTIC Science & Technology

2006-06-01

Mehrman investigated the effects of prior fatigue on creep behavior, and concluded that a history of prior fatigue loading increases creep life of...as reduced susceptibility to oxidation [4]. Nextel™ 720/Alumina composite (N720/A), combines the strength and creep resistance of a di- phase...studied the response to creep and cyclic loading, respectively, and showed that the presence of steam severely degrades performance at 1200ºC [35

Feasibility of a Patient-Controlled Cognitive Behavioral Intervention for Pain, Fatigue, and Sleep Disturbance in Cancer

PubMed Central

Kwekkeboom, Kristine L.; Abbott-Anderson, Kristen; Wanta, Britt

2009-01-01

Purpose To evaluate the feasibility of a patient-controlled cognitive-behavioral intervention for pain, fatigue, and sleep disturbance during treatment for advanced cancer, and to assess initial efficacy of the intervention in controlling symptoms. Design One-group pretest-posttest design. Setting Outpatient oncology clinics at a Comprehensive Cancer Center in the Midwestern United States. Sample 30 adults with advanced (recurrent or metastatic) colorectal, lung, prostate, or GYN cancer receiving chemotherapy or radiotherapy. Methods Participants completed baseline measures (demographics, symptom inventory) and received education and training to use an MP3 player loaded with 12 cognitive-behavioral strategies (e.g., relaxation exercises, guided imagery, nature sound recordings). Participants used the strategies as needed for symptom management over the following 2-weeks, keeping a log of symptom ratings with each use. Following the two-week intervention, participants completed a second symptom inventory and an evaluation of the intervention. Main Research Variables Feasibility, patient-controlled cognitive-behavioral intervention, pain, fatigue, sleep disturbance. Findings 73% of the 43 eligible patients agreed to participate (N=30) and of these, 90% (n=27) completed the study. The majority of participants reported that they enjoyed the intervention, had learned useful skills, and perceived improvement in their symptoms. Symptom scores at 2-weeks did not differ significantly from baseline, however significant reductions in pain, fatigue, and sleep disturbance severity were found in ratings made immediately before and after use of a cognitive-behavioral strategy. Conclusions The patient-controlled cognitive-behavioral intervention appears feasible for further study and could reduce day-to-day severity of co-occurring pain, fatigue, and sleep disturbance. Implications for Nursing A randomized controlled trial is necessary to test efficacy of the intervention for co-occurring pain, fatigue, and sleep disturbance. In the mean time, based on previous efficacy studies, cognitive-behavioral strategies can be recommended for certain individual symptoms. PMID:20439200

Bithermal Low-Cycle Fatigue Evaluation of Automotive Exhaust System Alloy SS409

NASA Technical Reports Server (NTRS)

Lu, Gui-Ying; Behling, Mike B.; Halford, Gary R.

2000-01-01

This investigation provides, for the first time, cyclic strainrange-controlled, thermomechanical fatigue results for the ferritic stainless steel alloy SS409. The alloy has seen extensive application for automotive exhaust system components. The data were generated to calibrate the Total Strain Version of the Strainrange Partitioning (TS-SRP) method for eventual application to the design and durability assessment of automotive exhaust systems. The thermomechanical cyclic lifetime and cyclic stress-strain constitutive behavior for alloy SS409 were measured using bithermal tests cycling between isothermal extremes of 400 and 800 C. Lives ranged up to 10,000 cycles to failure with hold-times of 0.33 to 2.0 minutes. The bithermal fatigue behavior is compared to isothermal, strain-controlled fatigue behavior at both 400 and 800 C. Thermomechanical cycling was found to have a profound detrimental influence on the fatigue failure resistance of SS409 compared to isothermal cycling. Supplementary bithermal cyclic stress-strain constitutive tests with hold-times ranging from 40 seconds up to 1.5 hours were conducted to calibrate the TS-SRP equation for extrapolation to longer lifetime predictions. Observed thermomechanical (bithermal) fatigue lives correlated well with lives calculated using the calibrated TS-SRP equations: 70% of the bithermal fatigue data fall within a factor of 1.2 of calculated life; 85% within a factor of 1.4; and 100% within a factor of 1.8.

Evaluation of Orientation Dependence of Fracture Toughness and Fatigue Crack Propagation Behavior of As-Deposited ARCAM EBM Ti-6Al-4V

NASA Astrophysics Data System (ADS)

Seifi, Mohsen; Dahar, Matthew; Aman, Ron; Harrysson, Ola; Beuth, Jack; Lewandowski, John J.

2015-03-01

This preliminary work documents the effects of test orientation with respect to build and beam raster directions on the fracture toughness and fatigue crack growth behavior of as-deposited EBM Ti-6Al-4V. Although ASTM/ISO standards exist for determining the orientation dependence of various mechanical properties in both cast and wrought materials, these standards are evolving for materials produced via additive manufacturing (AM) techniques. The current work was conducted as part of a larger America Makes funded project to begin to examine the effects of process variables on the microstructure and fracture and fatigue behavior of AM Ti-6Al-4V. In the fatigue crack growth tests, the fatigue threshold, Paris law slope, and overload toughness were determined at different load ratios, R, whereas fatigue precracked samples were tested to determine the fracture toughness. The as-deposited material exhibited a fine-scale basket-weave microstructure throughout the build, and although fracture surface examination revealed the presence of unmelted powders, disbonded regions, and isolated porosity, the resulting mechanical properties were in the range of those reported for cast and wrought Ti-6Al-4V. Remote access and control of testing was also developed at Case Western Reserve University to improve efficiency of fatigue crack growth testing.

Resistance to Fracture, Fatigue and Stress-Corrosion of Al-Cu-Li-Zr Alloys

DTIC Science & Technology

1985-02-19

alloys , in both smooth and notch fatigue conditions, are compared in Figure 15 giving a summary of Mg- effect on S-N fatigue behavior. Several ...crack initiation of conventional aluminum alloys and reported that fatigue cracks were associated with cracked constituent particles in 2024 -T3... fatigue cracks. Kung & Fine (14) investigated surface crack initiation in a 2024 -T4 alloy . They observed that at high stresses most cracks formed

Investigation of a ceramic matrix composite under strain controlled fatigue condition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gudaitis, J.J.; Mall, S.

The fatigue behavior along with damage mechanisms and failure modes of a fiber reinforced ceramic matrix composite with a cross-ply lay-up was investigated under strain controlled mode. Two fatigue conditions involving tension-tension and tension-compression cycling were employed. The strain range versus fatigue life curves for both fatigue conditions were in agreement with each other. However, damage mechanisms and failure modes were different for both cases.

Mediators of the effects on fatigue of pragmatic rehabilitation for chronic fatigue syndrome.

PubMed

Wearden, Alison J; Emsley, Richard

2013-10-01

To examine potential mediators of the effect of pragmatic rehabilitation on improvements in fatigue following a randomized controlled trial for patients with chronic fatigue syndrome (CFS/ME) in primary care (IRCTN 74156610). Patients fulfilled the Oxford criteria for CFS. Ninety-five patients were randomized to pragmatic rehabilitation and 100 to general practitioner (GP) treatment as usual. The outcome was the Chalder fatigue scale score (0123 scoring) at end of treatment (20 weeks) and 1-year follow up (70 weeks). First, the effect of treatment on potential mediators was assessed. Then fatigue was regressed on significant mediators, treatment allocation, and baseline measures of fatigue and significant mediators. Reduction in limiting activities at 20 weeks mediated the positive effect of pragmatic rehabilitation on fatigue at 70 weeks (mediated effect size = -2.64, SE = 0.81, p = .001, proportion of effect mediated = 82.0%). Reduction in catastrophizing at 20 weeks mediated the positive effect of pragmatic rehabilitation on fatigue at 70 weeks (mediated effect size = -1.39, SE = 0.61, p = .023, proportion of effect mediated = 43.2%). Reductions in 70-week measures of fear avoidance, embarrassment avoidance, limiting activities, and all-or-nothing behavior all mediated improvement in fatigue at 70 weeks, although the causal direction of these cross-sectional effects cannot be determined. There were no between-group differences on measures of exercise capacity (a timed step test). Improvements in fatigue following pragmatic rehabilitation are related to changes in behavioral responses to and beliefs about fatigue.

The effect of fatigue driving on injury severity considering the endogeneity.

PubMed

Li, Yanyan; Yamamoto, Toshiyuki; Zhang, Guangnan

2018-02-01

Fatigue driving is one of the most risky driving-related behaviors and represented a significant social and economic cost to the community. Several studies have already examined the relationship between fatigue driving behavior and traffic injury severity from different aspects. However, fatigue driving and injury severity in traffic crash may share some common influential factors. Ignoring the impact of these common factors will lead to endogeneity problem and result in biased parameter estimation. Based on 38,564 crash records during 2006-2011 in Guangdong province, China, we apply a bivariate endogenous binary-ordered probit model to examine the relationship between fatigue driving and injury severity considering endogeneity of fatigue driving. We also explore the difference of influential factors between commercial and non-commercial vehicle drivers. This study identifies several common observed influential factors of fatigue driving propensity and fatal injury propensity and reveals a substantial and significant negative correlation of unobserved factors between them. The influence of fatigue driving on injury severity is significantly underestimated if the endogeneity of fatigue driving on fatal injury propensity is ignored. Factors such as vehicle insurance and road types not only affect fatal injury propensity, but also fatigue driving propensity. The findings in this study can help better understand how those factors affect fatigue driving and injury severity, and contributes to more efficient policy for preventing the harmfulness of fatigue-related crashes. Copyright © 2017 National Safety Council and Elsevier Ltd. All rights reserved.

3D-seismic observations of Late Pleistocene glacial dynamics on the central West Greenland margin

NASA Astrophysics Data System (ADS)

Hofmann, Julia; Knutz, Paul; Cofaigh, Colm Ó.

2016-04-01

Fast-flowing ice streams and outlet glaciers exert a major control on glacial discharge from contemporary and palaeo ice sheets. Improving our understanding of the extent and dynamic behaviour of these palaeo-ice streams is therefore crucial for predictions of the response of ice sheets to present and future climate warming and the associated implications for global sea level. This poster presents results from two 3D-seismic surveys located on the shelf adjoining the Disko Bay trough-mouth fan (TMF), one of the largest glacial outlet systems in Greenland. Located at the seaward terminus of the c. 370 km long cross-shelf Disko Trough, the Disko Bay TMF was generated by highly efficient subglacial sediment delivery onto the continental slopes during repeated ice-stream advances. A variety of submarine glacial landform assemblages are recognised on the seabed reflecting past ice-stream activity presumably related to glacial-interglacial cycles. The 3D-seismic volumes cover the shallow banks located north and south of the Disko Trough. The focus of this study is the seabed and the uppermost stratigraphic interval associated with the Late Stage of TMF development, presumably covering the late Pleistocene (Hofmann et al., submitted). Seabed morphologies include multiple sets of ridges up to 20 m high that extend in NW-SE direction for c. 30 km, and cross-cutting curvilinear furrows with maximum lengths of c. 9 km and average depths of c. 4.5 m. Back-stepping, arcuate scarps facing NW define the shelf break on the northern survey, comprising average widths of c. 4.5 km and incision depths of c. 27.5 m. The large transverse ridge features on the southern survey are likely ice-marginal and are interpreted as terminal moraine ridges recording the existence of a shelf-edge terminating, grounded Late Weichselian ice sheet. The furrows, most prominent on the outer shelf adjoining the shallow banks and partly incising the moraine ridges, are interpreted as iceberg ploughmarks suggesting the transition between grounded ice and a glacimarine setting. The back-stepping scarps are suggestive of slide scars that were created as a result of mass movement induced by instabilities along the NW slope. The buried section contains morphologies indicating an asymmetric feature with a steeper side facing south. It comprises a thickness of c. 100 m and a length of c. 28 km. The detailed surface observations and seismic geometries suggest that the northern area represents a relict grounding-zone wedge (GZW). The wedge is covered by stratified deposits suggesting that it was at least occasionally submarine after its formation and may have served as pinning-point for floating ice shelves during periods of the Late TMF Stage. Important implications of the study are the intermittent development of floating ice shelves during the course of the Late Stage of TMF development and the presence of shelf-edge terminating grounded Late Weichselian ice outside of the troughs. Hofmann, J.C., Knutz, P.C., Nielsen, T., Kuijpers, A., submitted. Seismic architecture and evolution of the Disko Bay trough-mouth fan, central West Greenland margin. Quaternary Science Reviews.

Fatigue behavior of ULTIMETRTM alloy: Experiment and theoretical modeling

NASA Astrophysics Data System (ADS)

Jiang, Liang

ULTIMETRTM alloy is a commercial Co-26Cr-9Ni (weight percent) superalloy, which possesses excellent resistance to both wear and corrosion. In order to extend the structural applications of this alloy and improve the fundamental understanding of the fatigue damage mechanisms, stress- and strain-controlled fatigue tests were performed at various temperatures and in different environments. The stress- and strain-life data were developed for the structural design and engineering applications of this material. Fractographic studies characterized the crack-initiation and propagation behavior of the alloy. Microstructure evolution during fatigue was revealed by x-ray diffraction, scanning electron microscopy, and transmission electron microscopy. Specifically, it was found that the metastable face-centered-cubic structure of this alloy in the as-received condition could be transformed into a hexagonal-close-packed structure either under the action of plastic deformation at room temperature, or due to the aging and cyclic deformation at intermediate temperatures. This interesting observation constructed a sound basis for the alloy development. The dominant mechanisms, which control the fatigue behavior of ULTIMET alloy, were characterized. High-speed, high-resolution infrared (IR) thermography, as a non-contact, full-field, and nondestructive technique, was used to characterize the damage during fatigue. The temperature variations during each fatigue cycle, which were due to the thermal-elastic-plastic effect, were observed and related to stress-strain analyses. The temperature evolution during fatigue manifested the cumulative fatigue damage process. A constitutive model was developed to predict thermal and mechanical responses of ULTIMET alloy subjected to cyclic deformation. The predicted cyclic stress-strain responses and temperature variations were found to be in good agreement with the experimental results. In addition, a fatigue life prediction model was developed based on the strain-energy consideration, and the measured temperature could be utilized as an index for fatigue-life prediction.

Mobile Technology Use by People Experiencing Multiple Sclerosis Fatigue: Survey Methodology.

PubMed

Van Kessel, Kirsten; Babbage, Duncan R; Reay, Nicholas; Miner-Williams, Warren M; Kersten, Paula

2017-02-28

Fatigue is one of the most commonly reported symptoms of multiple sclerosis (MS). It has a profound impact on all spheres of life, for people with MS and their relatives. It is one of the key precipitants of early retirement. Individual, group, and Internet cognitive behavioral therapy-based approaches to supporting people with MS to manage their fatigue have been shown to be effective. The aim of this project was to (1) survey the types of mobile devices and level of Internet access people with MS use or would consider using for a health intervention and (2) characterize the levels of fatigue severity and their impact experienced by the people in our sample to provide an estimate of fatigue severity of people with MS in New Zealand. The ultimate goal of this work was to support the future development of a mobile intervention for the management of fatigue for people with MS. Survey methodology using an online questionnaire was used to assess people with MS. A total of 51 people with MS participated. The average age was 48.5 years, and the large majority of the sample (77%) was female. Participants reported significant levels of fatigue as measured with the summary score of the Neurological Fatigue Index (mean 31.4 [SD 5.3]). Most (84%) respondents scored on average more than 3 on the fatigue severity questions, reflecting significant fatigue. Mobile phone usage was high with 86% of respondents reporting having a mobile phone; apps were used by 75% of respondents. Most participants (92%) accessed the Internet from home. New Zealand respondents with MS experienced high levels of both fatigue severity and fatigue impact. The majority of participants have a mobile device and access to the Internet. These findings, along with limited access to face-to-face cognitive behavioral therapy-based interventions, create an opportunity to develop a mobile technology platform for delivering a cognitive behavioral therapy-based intervention to decrease the severity and impact of fatigue in people with MS. ©Kirsten Van Kessel, Duncan R Babbage, Nicholas Reay, Warren M Miner-Williams, Paula Kersten. Originally published in JMIR Mhealth and Uhealth (http://mhealth.jmir.org), 28.02.2017.

Mobile Technology Use by People Experiencing Multiple Sclerosis Fatigue: Survey Methodology

PubMed Central

Reay, Nicholas

2017-01-01

Background Fatigue is one of the most commonly reported symptoms of multiple sclerosis (MS). It has a profound impact on all spheres of life, for people with MS and their relatives. It is one of the key precipitants of early retirement. Individual, group, and Internet cognitive behavioral therapy–based approaches to supporting people with MS to manage their fatigue have been shown to be effective. Objective The aim of this project was to (1) survey the types of mobile devices and level of Internet access people with MS use or would consider using for a health intervention and (2) characterize the levels of fatigue severity and their impact experienced by the people in our sample to provide an estimate of fatigue severity of people with MS in New Zealand. The ultimate goal of this work was to support the future development of a mobile intervention for the management of fatigue for people with MS. Methods Survey methodology using an online questionnaire was used to assess people with MS. A total of 51 people with MS participated. The average age was 48.5 years, and the large majority of the sample (77%) was female. Results Participants reported significant levels of fatigue as measured with the summary score of the Neurological Fatigue Index (mean 31.4 [SD 5.3]). Most (84%) respondents scored on average more than 3 on the fatigue severity questions, reflecting significant fatigue. Mobile phone usage was high with 86% of respondents reporting having a mobile phone; apps were used by 75% of respondents. Most participants (92%) accessed the Internet from home. Conclusions New Zealand respondents with MS experienced high levels of both fatigue severity and fatigue impact. The majority of participants have a mobile device and access to the Internet. These findings, along with limited access to face-to-face cognitive behavioral therapy–based interventions, create an opportunity to develop a mobile technology platform for delivering a cognitive behavioral therapy–based intervention to decrease the severity and impact of fatigue in people with MS. PMID:28246073

Fatigue in neuromuscular disorders: focus on Guillain-Barré syndrome and Pompe disease.

PubMed

de Vries, J M; Hagemans, M L C; Bussmann, J B J; van der Ploeg, A T; van Doorn, P A

2010-03-01

Fatigue accounts for an important part of the burden experienced by patients with neuromuscular disorders. Substantial high prevalence rates of fatigue are reported in a wide range of neuromuscular disorders, such as Guillain-Barré syndrome and Pompe disease. Fatigue can be subdivided into experienced fatigue and physiological fatigue. Physiological fatigue in turn can be of central or peripheral origin. Peripheral fatigue is an important contributor to fatigue in neuromuscular disorders, but in reaction to neuromuscular disease fatigue of central origin can be an important protective mechanism to restrict further damage. In most cases, severity of fatigue seems to be related with disease severity, possibly with the exception of fatigue occurring in a monophasic disorder like Guillain-Barré syndrome. Treatment of fatigue in neuromuscular disease starts with symptomatic treatment of the underlying disease. When symptoms of fatigue persist, non-pharmacological interventions, such as exercise and cognitive behavioral therapy, can be initiated.

FATIGUE OF BIOMATERIALS: HARD TISSUES

PubMed Central

Arola, D.; Bajaj, D.; Ivancik, J.; Majd, H.; Zhang, D.

2009-01-01

The fatigue and fracture behavior of hard tissues are topics of considerable interest today. This special group of organic materials comprises the highly mineralized and load-bearing tissues of the human body, and includes bone, cementum, dentin and enamel. An understanding of their fatigue behavior and the influence of loading conditions and physiological factors (e.g. aging and disease) on the mechanisms of degradation are essential for achieving lifelong health. But there is much more to this topic than the immediate medical issues. There are many challenges to characterizing the fatigue behavior of hard tissues, much of which is attributed to size constraints and the complexity of their microstructure. The relative importance of the constituents on the type and distribution of defects, rate of coalescence, and their contributions to the initiation and growth of cracks, are formidable topics that have not reached maturity. Hard tissues also provide a medium for learning and a source of inspiration in the design of new microstructures for engineering materials. This article briefly reviews fatigue of hard tissues with shared emphasis on current understanding, the challenges and the unanswered questions. PMID:20563239

Study of Near-Threshold Fatigue Crack Propagation in Pipeline Steels in High Pressure Environments

NASA Technical Reports Server (NTRS)

Mitchell, M.

1981-01-01

Near threshold fatigue crack propagation in pipeline steels in high pressure environments was studied. The objective was to determine the level of threshold stress intensity for fatigue crack growth rate behavior in a high strength low alloy X60 pipeline-type steel. Complete results have been generated for gaseous hydrogen at ambient pressure, laboratory air at ambient pressure and approximately 60% relative humidity as well as vacuum of 0.000067 Pa ( 0.0000005 torr) at R-ratios = K(min)/K(max) of 0.1, 0.5, and 0.8. Fatigue crack growth rate behavior in gaseous hydrogen, methane, and methane plus 10 percent hydrogen at 6.89 MPa (100 psi) was determined.

Effect of Phosphate-Buffered Solution Corrosion on the Ratcheting Fatigue Behavior of a Duplex Mg-Li-Al Alloy

NASA Astrophysics Data System (ADS)

Yuan, Xin; Yu, Dunji; Gao, Li-Lan; Gao, Hong

2016-05-01

This work reports the uniaxial ratcheting and fatigue behavior of a duplex Mg-Li-Al alloy under the influence of phosphate-buffered solution corrosion. Microstructural observations reveal pitting and filament corrosion defects, which impair the load-bearing capacity of the alloy and cause stress concentration, thus leading to an accelerated accumulation of ratcheting strain and shortened fatigue life under the same nominal loading conditions. Comparing Smith model, Smith-Watson-Topper model, and Paul-Sivaprasad-Dhar model, a ratcheting fatigue life prediction model based on the Broberg damage rule and the Paul-Sivaprasad-Dhar model was proposed, and the model yielded a superior prediction for the studied magnesium alloy.

Fatigue Crack Growth Behavior Evaluation of Grainex Mar-M 247 for NASA's High Temperature, High Speed Turbine Seal Test Rig

NASA Technical Reports Server (NTRS)

Delgado, Irebert R.; Steinetz, Bruce M.; Rimnac, Clare M.; Lewandowski, John J.

2008-01-01

The fatigue crack growth behavior of Grainex Mar-M 247 is evaluated for NASA s Turbine Seal Test Facility. The facility is used to test air-to-air seals primarily for use in advanced jet engine applications. Because of extreme seal test conditions of temperature, pressure, and surface speeds, surface cracks may develop over time in the disk bolt holes. An inspection interval is developed to preclude catastrophic disk failure by using experimental fatigue crack growth data. By combining current fatigue crack growth results with previous fatigue strain-life experimental work, an inspection interval is determined for the test disk. The fatigue crack growth life of the NASA disk bolt holes is found to be 367 cycles at a crack depth of 0.501 mm using a factor of 2 on life at maximum operating conditions. Combining this result with previous fatigue strain-life experimental work gives a total fatigue life of 1032 cycles at a crack depth of 0.501 mm. Eddy-current inspections are suggested starting at 665 cycles since eddy current detection thresholds are currently at 0.381 mm. Inspection intervals are recommended every 50 cycles when operated at maximum operating conditions.

Effects of microstructural inclusions on fatigue life of polyether ether ketone (PEEK).

PubMed

Simsiriwong, Jutima; Shrestha, Rakish; Shamsaei, Nima; Lugo, Marcos; Moser, Robert D

2015-11-01

In this study, the effects of microstructural inclusions on fatigue life of polyether ether ketone (PEEK) was investigated. Due to the versatility of its material properties, the semi-crystralline PEEK polymer has been increasingly adopted in a wide range of applications particularly as a biomaterial for orthopedic, trauma, and spinal implants. To obtain the cyclic behavior of PEEK, uniaxial fully-reversed strain-controlled fatigue tests were conducted at ambient temperature and at 0.02 mm/mm to 0.04 mm/mm strain amplitudes. The microstructure of PEEK was obtained using the optical and the scanning electron microscope (SEM) to determine the microstructural inclusion properties in PEEK specimen such as inclusion size, type, and nearest neighbor distance. SEM analysis was also conducted on the fracture surface of fatigue specimens to observe microstructural inclusions that served as the crack incubation sites. Based on the experimental strain-life results and the observed microstructure of fatigue specimens, a microstructure-sensitive fatigue model was used to predict the fatigue life of PEEK that includes both crack incubation and small crack growth regimes. Results show that the employed model is applicable to capture microstructural effects on fatigue behavior of PEEK. Copyright © 2015 Elsevier Ltd. All rights reserved.

The reciprocal relationship between daily fatigue and catastrophizing following cancer treatment: Affect and physical activity as potential mediators.

PubMed

Müller, Fabiola; Stephenson, Ellen; DeLongis, Anita; Smink, Ans; Van Ginkel, Robert J; Tuinman, Marrit A; Hagedoorn, Mariët

2018-03-01

Fatigue is a distressing symptom many cancer patients experience even after completion of treatment. Although theory and empirical evidence indicate that negative cognitions perpetuate fatigue after completion of treatment, insight into how this process unfolds in daily life is limited. This study used an intensive longitudinal design to investigate the reciprocal relationship between catastrophizing and fatigue in daily life and whether affective and behavioral processes mediate these relationships. Post-treatment colorectal cancer patients (n = 101) completed daily diaries (14 days, 3 times daily) regarding their fatigue, catastrophizing, positive and negative affect, and physical activity. Multilevel modeling was applied to investigate within-person associations within days. Analyses revealed a positive reciprocal relationship between fatigue and catastrophizing throughout the day. That is, high levels of catastrophizing were associated with increases in fatigue within patients. In turn, but to a lesser extent, high levels of fatigue predicted increases in catastrophizing at the next assessment. Low positive affect and high negative affect mediated the effect of catastrophizing on increases in fatigue. Only negative affect mediated the reverse relationship. Physical activity did not mediate either relationship. This study provides evidence for a mutually reinforcing relationship between catastrophizing and fatigue in daily life, which might explain the perpetuation of fatigue after completion of cancer treatment. Fatigue-specific cognitive behavior therapy could be improved by educating patients about this daily reciprocal relationship, train them to quickly replace catastrophizing thoughts in daily life, and help them to cope with affective changes induced by fatigue. Copyright © 2017 John Wiley & Sons, Ltd.

Strain differences in fatigue and depression after experimental stroke.

PubMed

Kunze, Allison; Zierath, Dannielle; Drogomiretskiy, Olga; Becker, Kyra

2014-10-01

Fatigue and depression are common symptoms after stroke. Animal models of poststroke fatigue (PSF) and poststroke depression (PSD) would facilitate the study of these symptoms. Spontaneous locomotor activity is as an objective measure of fatigue and learned helplessness an accepted correlate of depression. We used different rat strains to evaluate stroke-induced changes in behavior in hopes that interstrain differences would provide insights into the biological basis of these symptoms. Male Lewis, Wistar, and Sprague-Dawley (SD) rats underwent experimental stroke. Spontaneous activity was assessed continually after stroke (for up to 50 days). In a subset of animals, the forced swim test was performed prior to and 1 month after stroke to assess learned helplessness; blood was obtained at sacrifice for cytokine assay. Stroke induced strain-related differences in activity; Lewis rats increased spontaneous activity during the dark cycle, while Wistar and SD rats increased activity during the light cycle. The velocity of movement decreased during the dark cycle in Wistar and SD rats and during the light cycle in Lewis rats. Stroke also led to an increase in learned helplessness in Lewis rats. In summary, different patterns of behaviors emerge in different rat strains after stroke. Lewis rats displayed behavior consistent with depression but not fatigue, while Wistar and SD rats displayed behavior consistent with fatigue but not depression. These data argue that PSF and PSD are different biological constructs and suggest that analysis of strain-related differences may provide insight into symptom pathophysiology.

Fatigue behavior of porous biomaterials manufactured using selective laser melting.

PubMed

Yavari, S Amin; Wauthle, R; van der Stok, J; Riemslag, A C; Janssen, M; Mulier, M; Kruth, J P; Schrooten, J; Weinans, H; Zadpoor, A A

2013-12-01

Porous titanium alloys are considered promising bone-mimicking biomaterials. Additive manufacturing techniques such as selective laser melting allow for manufacturing of porous titanium structures with a precise design of micro-architecture. The mechanical properties of selective laser melted porous titanium alloys with different designs of micro-architecture have been already studied and are shown to be in the range of mechanical properties of bone. However, the fatigue behavior of this biomaterial is not yet well understood. We studied the fatigue behavior of porous structures made of Ti6Al4V ELI powder using selective laser melting. Four different porous structures were manufactured with porosities between 68 and 84% and the fatigue S-N curves of these four porous structures were determined. The three-stage mechanism of fatigue failure of these porous structures is described and studied in detail. It was found that the absolute S-N curves of these four porous structures are very different. In general, given the same absolute stress level, the fatigue life is much shorter for more porous structures. However, the normalized fatigue S-N curves of these four structures were found to be very similar. A power law was fitted to all data points of the normalized S-N curves. It is shown that the measured data points conform to the fitted power law very well, R(2)=0.94. This power law may therefore help in estimating the fatigue life of porous structures for which no fatigue test data is available. It is also observed that the normalized endurance limit of all tested porous structures (<0.2) is lower than that of corresponding solid material (c.a. 0.4). © 2013.

Fatigue damage behavior of a surface-mount electronic package under different cyclic applied loads

NASA Astrophysics Data System (ADS)

Ren, Huai-Hui; Wang, Xi-Shu

2014-04-01

This paper studies and compares the effects of pull-pull and 3-point bending cyclic loadings on the mechanical fatigue damage behaviors of a solder joint in a surface-mount electronic package. The comparisons are based on experimental investigations using scanning electron microscopy (SEM) in-situ technology and nonlinear finite element modeling, respectively. The compared results indicate that there are different threshold levels of plastic strain for the initial damage of solder joints under two cyclic applied loads; meanwhile, fatigue crack initiation occurs at different locations, and the accumulation of equivalent plastic strain determines the trend and direction of fatigue crack propagation. In addition, simulation results of the fatigue damage process of solder joints considering a constitutive model of damage initiation criteria for ductile materials and damage evolution based on accumulating inelastic hysteresis energy are identical to the experimental results. The actual fatigue life of the solder joint is almost the same and demonstrates that the FE modeling used in this study can provide an accurate prediction of solder joint fatigue failure.

Metabolism of Kaempferia parviflora polymethoxyflavones by human intestinal bacterium Bautia sp. MRG-PMF1.

PubMed

Kim, Mihyang; Kim, Nayoung; Han, Jaehong

2014-12-24

Poylmethoxyflavones (PMFs) are major bioactive flavonoids, which exhibit various biological activities, such as anticancer effects. The biotransformation of PMFs and characterization of a PMF-metabolizing human intestinal bacterium were studied herein for the first time. Hydrolysis of aryl methyl ether functional groups by human fecal samples was observed from the bioconversion of various PMFs. Activity-guided screening for PMF-metabolizing intestinal bacteria under anaerobic conditions resulted in the isolation of a strict anaerobic bacterium, which was identified as Blautia sp. MRG-PMF1. The isolated MRG-PMF1 was able to metabolize various PMFs to the corresponding demethylated flavones. The microbial conversion of bioactive 5,7-dimethoxyflavone (5,7-DMF) and 5,7,4'-trimethoxyflavone (5,7,4'-TMF) was studied in detail. 5,7-DMF and 5,7,4'-TMF were completely metabolized to 5,7-dihydroxyflavone (chrysin) and 5,7,4'-trihydroxyflavone (apigenin), respectively. From a kinetics study, the methoxy group on the flavone C-7 position was found to be preferentially hydrolyzed. 5-Methoxychrysin, the intermediate of 5,7-DMF metabolism by Blautia sp. MRG-PMF1, was isolated and characterized by nuclear magnetic resonance spectroscopy. Apigenin was produced from the sequential demethylation of 5,7,4'-TMF, via 5,4'-dimethoxy-7-hydroxyflavone and 7,4'-dihydroxy-5-methoxyflavone (thevetiaflavone). Not only demethylation activity but also deglycosylation activity was exhibited by Blautia sp. MRG-PMF1, and various flavonoids, including isoflavones, flavones, and flavanones, were found to be metabolized to the corresponding aglycones. The unprecedented PMF demethylation activity of Blautia sp. MRG-PMF1 will expand our understanding of flavonoid metabolism in the human intestine and lead to novel bioactive compounds.

Fatigue crack growth behaviour of semi-elliptical surface cracks for an API 5L X65 gas pipeline under tension

NASA Astrophysics Data System (ADS)

Shaari, M. S.; Akramin, M. R. M.; Ariffin, A. K.; Abdullah, S.; Kikuchi, M.

2018-02-01

The paper is presenting the fatigue crack growth (FCG) behavior of semi-elliptical surface cracks for API X65 gas pipeline using S-version FEM. A method known as global-local overlay technique was used in this study to predict the fatigue behavior that involve of two separate meshes each specifically for global (geometry) and local (crack). The pre-post program was used to model the global geometry (coarser mesh) known as FAST including the material and boundary conditions. Hence, the local crack (finer mesh) will be defined the exact location and the mesh control accordingly. The local mesh was overlaid along with the global before the numerical computation taken place to solve the engineering problem. The stress intensity factors were computed using the virtual crack closure-integral method (VCCM). The most important results is the behavior of the fatigue crack growth, which contains the crack depth (a), crack length (c) and stress intensity factors (SIF). The correlation between the fatigue crack growth and the SIF shows a good growth for the crack depth (a) and dissimilar for the crack length (c) where stunned behavior was resulted. The S-version FEM will benefiting the user due to the overlay technique where it will shorten the computation process.

Review on fatigue behavior of high-strength concrete after high temperature

NASA Astrophysics Data System (ADS)

Zhao, Dongfu; Jia, Penghe; Gao, Haijing

2017-06-01

The fatigue of high-strength concrete after high temperature has begun to attract attention. But so far the researches work about the fatigue of high-strength concrete after high temperature have not been reported. This article based on a large number of literature. The research work about the fatigue of high-strength concrete after high temperature are reviewed, analysed and expected, which can provide some reference for the experimental study of fatigue damage analysis.

Technical evaluation report of the Specialists Meeting on Characterization of Low Cycle High Temperature Fatigue by the Strainrange Partitioning Method

NASA Technical Reports Server (NTRS)

Drapier, J. M.; Hirschberg, M. H.

1979-01-01

The ability of the Strainrange Partitioning Method SRP was evaluated to correlate the creep-fatigue behavior of gas turbine materials and to predict the creep fatigue life of laboratory specimens subjected to complex cycling conditions. A reference body of high temperature creep fatigue data which can be used in the evaluation of other SRP and low cycle high temperature fatigue predictive techniques was provided.

Statistical characterization of the fatigue behavior of composite lamina

NASA Technical Reports Server (NTRS)

Yang, J. N.; Jones, D. L.

1979-01-01

A theoretical model was developed to predict statistically the effects of constant and variable amplitude fatigue loadings on the residual strength and fatigue life of composite lamina. The parameters in the model were established from the results of a series of static tensile tests and a fatigue scan and a number of verification tests were performed. Abstracts for two other papers on the effect of load sequence on the statistical fatigue of composites are also presented.

Tumor Growth Increases Neuroinflammation, Fatigue and Depressive-like Behavior Prior to Alterations in Muscle Function

PubMed Central

Norden, Diana M.; Bicer, Sabahattin; Clark, Yvonne; Jing, Runfeng; Henry, Christopher J.; Wold, Loren E.; Reiser, Peter J.; Godbout, Jonathan P.; McCarthy, Donna O.

2014-01-01

Cancer patients frequently suffer from fatigue, a complex syndrome associated with loss of muscle mass, weakness, and depressed mood. Cancer-related fatigue (CRF) can be present at the time of diagnosis, during treatment, and persists for years after treatment. CRF negatively influences quality of life, limits functional independence, and is associated with decreased survival in patients with incurable disease. Currently there are no effective treatments to reduce CRF. The aim of this study was to use a mouse model of tumor growth and discriminate between two main components of fatigue: loss of muscle mass/function and altered mood/motivation. Here we show that tumor growth increased fatigue- and depressive-like behaviors, and reduced body and muscle mass. Decreased voluntary wheel running activity (VWRA) and increased depressive-like behavior in the forced swim and sucrose preference tests were evident in tumor-bearing mice within the first two weeks of tumor growth and preceded the loss of body and muscle mass. At three weeks, tumor-bearing mice had reduced grip strength but this was not associated with altered expression of myosin isoforms or impaired contractile properties of muscles. These increases in fatigue and depressive-like behaviors were paralleled by increased expression of IL-1β mRNA in the cortex and hippocampus. Minocycline administration reduced tumor-induced expression of IL-1β in the brain, reduced depressive-like behavior, and improved grip strength without altering muscle mass. Taken together, these results indicate that neuroinflammation and depressed mood, rather than muscle wasting, contribute to decreased voluntary activity and precede major changes in muscle contractile properties with tumor growth. PMID:25102452

Tumor growth increases neuroinflammation, fatigue and depressive-like behavior prior to alterations in muscle function.

PubMed

Norden, Diana M; Bicer, Sabahattin; Clark, Yvonne; Jing, Runfeng; Henry, Christopher J; Wold, Loren E; Reiser, Peter J; Godbout, Jonathan P; McCarthy, Donna O

2015-01-01

Cancer patients frequently suffer from fatigue, a complex syndrome associated with loss of muscle mass, weakness, and depressed mood. Cancer-related fatigue (CRF) can be present at the time of diagnosis, during treatment, and persists for years after treatment. CRF negatively influences quality of life, limits functional independence, and is associated with decreased survival in patients with incurable disease. Currently there are no effective treatments to reduce CRF. The aim of this study was to use a mouse model of tumor growth and discriminate between two main components of fatigue: loss of muscle mass/function and altered mood/motivation. Here we show that tumor growth increased fatigue- and depressive-like behaviors, and reduced body and muscle mass. Decreased voluntary wheel running activity (VWRA) and increased depressive-like behavior in the forced swim and sucrose preference tests were evident in tumor-bearing mice within the first two weeks of tumor growth and preceded the loss of body and muscle mass. At three weeks, tumor-bearing mice had reduced grip strength but this was not associated with altered expression of myosin isoforms or impaired contractile properties of muscles. These increases in fatigue and depressive-like behaviors were paralleled by increased expression of IL-1β mRNA in the cortex and hippocampus. Minocycline administration reduced tumor-induced expression of IL-1β in the brain, reduced depressive-like behavior, and improved grip strength without altering muscle mass. Taken together, these results indicate that neuroinflammation and depressed mood, rather than muscle wasting, contribute to decreased voluntary activity and precede major changes in muscle contractile properties with tumor growth. Copyright © 2014 Elsevier Inc. All rights reserved.

Potential role of licofelone, minocycline and their combination against chronic fatigue stress induced behavioral, biochemical and mitochondrial alterations in mice.

PubMed

Kumar, Anil; Vashist, Aditi; Kumar, Puneet; Kalonia, Harikesh; Mishra, Jitendriya

2012-01-01

Chronic fatigue stress (CFS) is a common complaint among general population. Persistent and debilitating fatigue severely impairs daily functioning and is usually accompanied by combination of several physical and psychiatric problems. It is now well established fact that oxidative stress and neuroinflammation are involved in the pathophysiology of chronic fatigue and related disorders. Targeting both COX (cyclooxygenase) and 5-LOX (lipoxygenase) pathways have been proposed to be involved in neuroprotective effect. In the present study, mice were put on the running wheel apparatus for 6 min test session daily for 21 days, what produced fatigue like condition. The locomotor activity and anxiety like behavior were measured on 0, 8(th), 15(th) and 22(nd) day. The brains were isolated on 22(nd) day immediately after the behavioral assessments for the estimation of oxidative stress parameters and mitochondrial enzyme complexes activity. Pre-treatment with licofelone (2.5, 5 and 10 mg/kg, po) and minocycline (50 and 100 mg/kg, po) for 21 days, significantly attenuated fatigue like behavior as compared to the control (rotating wheel activity test session, RWATS) group. Further, licofelone (5 and 10 mg/kg, po) and minocycline (50 and 100 mg/kg, po) drug treatments for 21 days significantly attenuated behavioral alterations, oxidative damage and restored mitochondrial enzyme complex activities (I, II, III and IV) as compared to control, whereas combination of licofelone (5 mg/kg) with minocycline (50 mg/kg) significantly potentiated their protective effect which was significant as compared to their effect per se. The present study highlights the therapeutic potential of licofelone, minocycline and their combination against CFS in mice.

The Effect of O2, H2O, and N2 on the Fatigue Crack Growth Behavior of an Alpha + Beta Titanium Alloy at 24 C and 177 C

NASA Technical Reports Server (NTRS)

Smith, Stephen W.; Piascik, Robert S.

2001-01-01

To study the effects of atmospheric species on the fatigue crack growth behavior of an a+B titanium alloy (Ti 6-2-2-2-2) at room temperature and 177 C, fatigue tests were performed in laboratory air, ultrahigh vacuum, and high purity water vapor, oxygen, nitrogen and helium at various partial pressures. Accelerated fatigue crack growth rates in laboratory air compared to ultrahigh vacuum are linked to the damaging effects of both water vapor and oxygen. Observations of the fatigue crack growth behavior in ultrahigh purity environments, along with surface film analysis using X-ray photoelectron spectroscopy (XPS), suggest that multiple crack-tip processes govern the damaging effects of air. Three possible mechanisms are proposed: 1) at low pressure (less than 10(exp -1) Pa), accelerated da/dN is likely due to monolayer adsorption on crack-tip surfaces presumably resulting in decreased bond strengths at the fatigue crack tip, 2) for pressures greater than 10(exp -1) Pa, accelerated da/dN in oxygen may result from oxidation at the crack tip limiting reversible slip, and 3) in water vapor, absorption of atomic hydrogen at the reactive crack tip resulting in process zone embrittlement.

Ibuprofen Ameliorates Fatigue- and Depressive-like Behavior in Tumor-bearing Mice

PubMed Central

Norden, Diana M.; McCarthy, Donna O.; Bicer, Sabahattin; Devine, Raymond; Reiser, Peter J.; Godbout, Jonathan P.; Wold, Loren E.

2015-01-01

Aims Cancer-related fatigue (CRF) is often accompanied by depressed mood, both of which reduce functional status and quality of life. Research suggests that increased expression of pro-inflammatory cytokines are associated with skeletal muscle wasting and depressive- and fatigue- like behaviors in rodents and cancer patients. We have previously shown that treatment with ibuprofen, a nonsteroidal anti-inflammatory drug, preserved muscle mass in tumor-bearing mice. Therefore, the purpose of the present study was to determine the behavioral effects of ibuprofen in a mouse model of CRF. Main Methods Mice were injected with colon-26 adenocarcinoma cells and treated with ibuprofen (10mg/kg) in the drinking water. Depressive-like behavior was determined using the forced swim test (FST). Fatigue-like behaviors were determined using voluntary wheel running activity (VWRA) and grip strength. The hippocampus, gastrocnemius muscle, and serum were collected for cytokine analysis. Key Findings Tumor-bearing mice showed depressive-like behavior in the FST, which was not observed in mice treated with ibuprofen. VWRA and grip strength declined in tumor-bearing mice, and ibuprofen attenuated this decline. Tumor-bearing mice had decreased gastrocnemius muscle mass and increased expression of IL-6, MAFBx and MuRF mRNA, biomarkers of protein degradation, in the muscle. Expression of IL-1β and IL-6 was also increased in the hippocampus. Treatment with ibuprofen improved muscle mass and reduced cytokine expression in both the muscle and hippocampus of tumor-bearing mice. Significance Ibuprofen treatment reduced skeletal muscle wasting, inflammation in the brain, and fatigue- and depressive-like behavior in tumor-bearing mice. Therefore, ibuprofen warrants evaluation as an adjuvant treatment for CRF. PMID:26498217

Mechanical and Fatigue Properties of Additively Manufactured Metallic Materials

NASA Astrophysics Data System (ADS)

Yadollahi, Aref

This study aims to investigate the mechanical and fatigue behavior of additively manufactured metallic materials. Several challenges associated with different metal additive manufacturing (AM) techniques (i.e. laser-powder bed fusion and direct laser deposition) have been addressed experimentally and numerically. Experiments have been carried out to study the effects of process inter-layer time interval--i.e. either building the samples one-at-a-time or multi-at-a-time (in-parallel)--on the microstructural features and mechanical properties of 316L stainless steel samples, fabricated via a direct laser deposition (DLD). Next, the effect of building orientation--i.e. the orientation in which AM parts are built--on microstructure, tensile, and fatigue behaviors of 17-4 PH stainless steel, fabricated via a laser-powder bed fusion (L-PBF) method was investigated. Afterwards, the effect of surface finishing--here, as-built versus machined--on uniaxial fatigue behavior and failure mechanisms of Inconel 718 fabricated via a laser-powder bed fusion technique was sought. The numerical studies, as part of this dissertation, aimed to model the mechanical behavior of AM materials, under monotonic and cyclic loading, based on the observations and findings from the experiments. Despite significant research efforts for optimizing process parameters, achieving a homogenous, defect-free AM product--immediately after fabrication--has not yet been fully demonstrated. Thus, one solution for ensuring the adoption of AM materials for application should center on predicting the variations in mechanical behavior of AM parts based on their resultant microstructure. In this regard, an internal state variable (ISV) plasticity-damage model was employed to quantify the damage evolution in DLD 316L SS, under tensile loading, using the microstructural features associated with the manufacturing process. Finally, fatigue behavior of AM parts has been modeled based on the crack-growth concept. Using the FASTRAN code, the fatigue-life of L-PBF Inconel 718 was accurately calculated using the size and shape of process-induced voids in the material. In addition, the maximum valley depth of the surface profile was found to be an appropriate representative of the initial surface flaw for fatigue-life prediction of AM materials in an as-built surface condition.

Development of a 1-m Class Telescope at TMF to Support Optical Communications Demonstrations

NASA Technical Reports Server (NTRS)

Wilson, K. E.; Sandusky, J.

1998-01-01

With the impetus towards high data rate communications in inter-satellite and space-to-ground links, the small size, low-mass, and low-power consumption of optical communications is seen as a viable alternative to radio frequency links.

Influence of the North American monsoon on Southern California tropospheric ozone levels during summer in 2013 and 2014

NASA Astrophysics Data System (ADS)

Granados-Muñoz, Maria Jose; Johnson, Matthew S.; Leblanc, Thierry

2017-06-01

The impact of the North American (NA) monsoon on tropospheric ozone variability in Southern California is investigated using lidar measurements at Jet Propulsion Laboratory-Table Mountain Facility, California, and the chemical-transport model GEOS-Chem. Routine lidar observations obtained in July-August 2013-2014 reveal a consistent ozone enhancement of 23 ppbv in the free troposphere (6-9 km), when ozone-rich air is transported along the western edge of the upper level anticyclone associated with the NA monsoon from regions where maximum lightning-induced NOx production occurs. When the high-pressure system shifts to the southeast, a zonal westerly flow of the air parcels reaching the Table Mountain Facility (TMF) occurs, prohibiting the lightning-induced ozone enhanced air to reach TMF. This modulation of tropospheric ozone by the position of the NA monsoon anticyclone could have implications on long-term ozone trends associated with our changing climate, due to the expected widening of the tropical belt affecting the strength and position of the anticyclone.

Continuously varying of critical exponents with the bismuth doped in the La0.8Na0.2Mn1-xBixO3 (0 ≤ x ≤ 0.06) manganites

NASA Astrophysics Data System (ADS)

Laouyenne, M. R.; Baazaoui, M.; Mahjoub, Sa.; Cheikhrouhou-Koubaa, W.; Farah, Kh.; Oumezzine, M.

2018-04-01

A comprehensive analysis of the critical phenomena for the nominal compositions La0.8Na0.2Mn1-xBixO3 (0 ≤ x ≤ 0.06) was carried out. The critical exponents values were calculated by various techniques such as Modified Arrott plot (MAP), Kouvel Fisher (KF) method and critical isotherm (CI). Comparison of the experimental data with the above theoretical models showed that the critical exponents β, γ and δ for the undoped sample are quite well described by the tricritical mean-field model (TMF). Furthermore, the substitution of Mn by Bi ions led to the increase of γ which approached the 3D-Heisenberg model (γ = 1 325 and β took similar values to those predicted by the TMF model. The validity of the exponents values was confirmed with the scaling hypothesis; the M (T, ε) curves collapse onto two independent universal branches below and above Tc.

Speech-Processing Fatigue in Children: Auditory Event-Related Potential and Behavioral Measures

ERIC Educational Resources Information Center

Key, Alexandra P.; Gustafson, Samantha J.; Rentmeester, Lindsey; Hornsby, Benjamin W. Y.; Bess, Fred H.

2017-01-01

Purpose: Fatigue related to speech processing is an understudied area that may have significant negative effects, especially in children who spend the majority of their school days listening to classroom instruction. Method: This study examined the feasibility of using auditory P300 responses and behavioral indices (lapses of attention and…

Implementing Cognitive Behavioral Therapy for Chronic Fatigue Syndrome in a Mental Health Center: A Benchmarking Evaluation

ERIC Educational Resources Information Center

Scheeres, Korine; Wensing, Michel; Knoop, Hans; Bleijenberg, Gijs

2008-01-01

Objective: This study evaluated the success of implementing cognitive behavioral therapy (CBT) for chronic fatigue syndrome (CFS) in a representative clinical practice setting and compared the patient outcomes with those of previously published randomized controlled trials (RCTs) of CBT for CFS. Method: The implementation interventions were the…

Fatigue crack growth behavior of railroad tank car steel TC-128B subjected to various environments. Volume 1

DOT National Transportation Integrated Search

2006-12-01

As part of an effort to apply damage tolerance concepts to railroad tank cars, the fatigue crack growth (FCG) behavior of two lots of TC-128B steel was investigated. In addition to the material lot difference, variables assessed include: load ratio, ...

The Role of Microstructural Variability on the Very High-Cycle Fatigue Behavior of Discontinuously-Reinforced Aluminum Metal Matrix Composites using Ultrasonic Fatigue (Preprint)

DTIC Science & Technology

2008-05-01

controlled processing. Bhanu-Prasad et al .37 conducted a systematic study of PM-processed 2124/SiC/30p aluminum composites 4 5 in which matrix alloy...Mater., 27, 173-178. [5] Wang A, Rack HJ (1991). Transition wear behavior of SiC-particulate- and SiC- whisker-reinforced 7091 Al metal matrix...modeling of particle distribution effects on fatigue in Al -SiCp composites. Mater. Sci. Eng. A, Struct. Mater. Prop. Microstruct. Process., 300, 113-124

Fatigue behavior of welded connections enhanced with ultrasonic impact treatment (UIT) and bolting.

DOT National Transportation Integrated Search

2008-11-01

A common problem in bridges employing welded steel girders is development of fatigue cracks at the ends of girder coverplates. Fatigue cracks tend to form at the toes of the transverse welds connecting a coverplate to a girder flange since this detai...

Rapid Assessment of the Role of Microstructural Variability in the Fatigue Behavior of Structural Alloys using Ultrasonic Fatigue

DTIC Science & Technology

2007-06-23

6 %AI-2%Sn- 4 %Zr- 6 %Mo in the very high cycle regime. The microstructure is a two-phase structure with primary a grains (ap grains) in a transformed [3...aluminum [2], magnesium [3], nickel-based [ 4 ], and titanium [5,6] alloy systems. Fatigue crack initiation is known to consume the majority of fatigue...microstructural neighborhood affects this process. In fatigue studies of alpha + beta titanium alloys, [ 6 -9] cyclic deformation localization is first observed in

Creep and Fatigue Interaction in the PWA 1484 Single Crystal Nickel-Base Alloy (Preprint)

DTIC Science & Technology

2011-07-01

work by Zhang et al . has shown that during the early part of fatigue cycling dislocations are formed primarily in the γ matrix with the number of...dislocations increasing with the number of applied cycles [11]. Ott and Mughrabi showed that during fatigue of single crystal nickel base superalloys... al . and their research determined that the fatigue behavior of PWA1484 could be well represented by a Walker type fatigue model that also included

High-temperature low cycle fatigue behavior of a gray cast iron

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fan, K.L., E-mail: 12klfan@tongji.edu.cn; He, G.Q.; She, M.

The strain controlled low cycle fatigue properties of the studied gray cast iron for engine cylinder blocks were investigated. At the same total strain amplitude, the low cycle fatigue life of the studied material at 523 K was higher than that at 423 K. The fatigue behavior of the studied material was characterized as cyclic softening at any given total strain amplitude (0.12%–0.24%), which was attributed to fatigue crack initiation and propagation. Moreover, this material exhibited asymmetric hysteresis loops due to the presence of the graphite lamellas. Transmission electron microscopy analysis suggested that cyclic softening was also caused by themore » interactions of dislocations at 423 K, such as cell structure in ferrite, whereas cyclic softening was related to subgrain boundaries and dislocation climbing at 523 K. Micro-analysis of specimen fracture appearance was conducted in order to obtain the fracture characteristics and crack paths for different strain amplitudes. It showed that the higher the temperature, the rougher the crack face of the examined gray cast iron at the same total strain amplitude. Additionally, the microcracks were readily blunted during growth inside the pearlite matrix at 423 K, whereas the microcracks could easily pass through pearlite matrix along with deflection at 523 K. The results of fatigue experiments consistently showed that fatigue damage for the studied material at 423 K was lower than that at 523 K under any given total strain amplitude. - Highlights: • The low cycle fatigue behavior of the HT250 for engine cylinder blocks was investigated. • TEM investigations were conducted to explain the cyclic deformation response. • The low cycle fatigue cracks of HT250 GCI were studied by SEM. • The fatigue life of the examined material at 523 K is higher than that at 423 K.« less

The Effect of Ultrasonic Peening on Service Life of the Butt-Welded High-Temperature Steel Pipes

NASA Astrophysics Data System (ADS)

Daavari, Morteza; Vanini, Seyed Ali Sadough

2015-09-01

Residual stresses introduced by manufacturing processes such as casting, forming, machining, and welding have harmful effects on the mechanical behavior of the structures. In addition to the residual stresses, weld toe stress concentration can play a determining effect. There are several methods to improve the mechanical properties such as fatigue behavior of the welded structures. In this paper, the effects of ultrasonic peening on the fatigue life of the high-temperature seamless steel pipes, used in the petrochemical environment, have been investigated. These welded pipes are fatigued due to thermal and mechanical loads caused by the cycle of cooling, heating, and internal pressure fluctuations. Residual stress measurements, weld geometry estimation, electrochemical evaluations, and metallography investigations were done as supplementary examinations. Results showed that application of ultrasonic impact treatment has led to increased fatigue life, fatigue strength, and corrosion resistance of A106-B welded steel pipes in petrochemical corrosive environment.

Fatigue of Nitinol: The state-of-the-art and ongoing challenges.

PubMed

Mahtabi, M J; Shamsaei, Nima; Mitchell, M R

2015-10-01

Nitinol, a nearly equiatomic alloy of nickel and titanium, has been considered for a wide range of applications including medical and dental devices and implants as well as aerospace and automotive components and structures. The realistic loading condition in many of these applications is cyclic; therefore, fatigue is often the main failure mode for such components and structures. The fatigue behavior of Nitinol involves many more complexities compared with traditional metal alloys arising from its uniqueness in material properties such as superelasticity and shape memory effects. In this paper, a review of the present state-of-the-art on the fatigue behavior of superelastic Nitinol is presented. Various aspects of fatigue of Nitinol are discussed and microstructural effects are explained. Effects of material preparation and testing conditions are also reviewed. Finally, several conclusions are made and recommendations for future works are offered. Copyright © 2015 Elsevier Ltd. All rights reserved.

A study of elevated temperature testing techniques for the fatigue behavior of PMCS: Application to T650-35/AMB21

NASA Technical Reports Server (NTRS)

Gyekenyesi, Andrew L.; Gastelli, Michael G.; Ellis, John R.; Burke, Christopher S.

1995-01-01

An experimental study was conducted to investigate the mechanical behavior of a T650-35/AMB21 eight-harness satin weave polymer composite system. Emphasis was placed on the development and refinement of techniques used in elevated temperature uniaxial PMC testing. Issues such as specimen design, gripping, strain measurement, and temperature control and measurement were addressed. Quasi-static tensile and fatigue properties (R(sub sigma) = 0.1) were examined at room and elevated temperatures. Stiffness degradation and strain accumulation during fatigue cycling were recorded to monitor damage progression and provide insight for future analytical modeling efforts. Accomplishments included an untabbed dog-bone specimen design which consistently failed in the gage section, accurate temperature control and assessment, and continuous in-situ strain measurement capability during fatigue loading at elevated temperatures. Finally, strain accumulation and stiffness degradation during fatigue cycling appeared to be good indicators of damage progression.

Fracture and fatigue behavior of shot-blasted titanium dental implants.

PubMed

Gil, F J; Planell, J A; Padrós, A

2002-01-01

This investigation studies the effect of the shot-blasting treatment on the cyclic deformation behavior of a commercially pure titanium, with two microstructures: equiaxed and acicular. The fatigue tests were carried out in artificial saliva medium at 37 degrees C. Cyclic deformation tests have been carried out up to fracture, and the fatigue crack nucleation and propagation have been analyzed. The results show that the shot-blasting treatment improves the fatigue life in the microstructures studied, and that the equiaxed was better in mechanical properties than the acicular. The cause of this improvement in the mechanical properties is due to the compressive stress on the material surface for the shot-blasted specimens. Hardness tests were carried out to determine the value of these internal stresses.

Assessment of microalloying effects on the high temperature fatigue behavior of NiAl

NASA Technical Reports Server (NTRS)

Noebe, R. D.; Lerch, B. A.; Rao, K. B. S.

1995-01-01

Binary NiAl suffers from a lack of strength and poor creep properties at and above 1000 K. Poor creep resistance in turn affects low cycle fatigue (LCF) lives at low strain ranges due to the additional interactions of creep damage. One approach for improving these properties involved microalloying with either Zr or N. As an integral part of a much larger alloying program the low cycle fatigue behavior of Zr and N doped nickel aluminides produced by extrusion of prealloyed powders has been investigated. Strain controlled LCF tests were performed in air at 1000 K. The influence of these microalloying additions on the fatigue life and cyclic stress response of polycrystalline NiAl are discussed.

Longitudinal risk factors for persistent fatigue in adolescents.

PubMed

Viner, Russell M; Clark, Charlotte; Taylor, Stephanie J C; Bhui, Kam; Klineberg, Emily; Head, Jenny; Booy, Robert; Stansfeld, Stephen A

2008-05-01

To examine whether sedentary behavior, obesity, smoking, and depression are risk factors for persistent fatigue in adolescents. Longitudinal population-based survey. Twenty-eight randomly selected schools in east London, England, in 2001 and 2003. A total of 1880 adolescents (49% male; 81% nonwhite British) aged 11 to 12 years and 13 to 14 years in 2000. Confidential questionnaires completed in class. Persistent fatigue (extreme tiredness twice weekly or more often in the previous month at both surveys), sedentary behavior, physical activity, depressive symptoms, body mass index, and smoking. Severe fatigue was reported in 11% of participants aged 11 to 14 years and 17% of participants aged 13 to 16 years. Eighty-four participants (4%) reported persistent fatigue. Across both surveys, only 3 pupils reported chronic fatigue syndrome. In multivariate logistic regression, risk of persistent fatigue was independently associated with being sedentary for more than 4 hours per day (odds ratio = 1.6; 95% confidence interval, 1.1-2.3; P = .01), being physically active (odds ratio = 1.5; 95% confidence interval, 1.1-2.3; P = .004), and depressive symptoms (odds ratio = 2.0; 95% confidence interval, 1.5-2.7; P < .001) in the first survey, after adjustment for age, sex, and socioeconomic status. Obesity and smoking were not associated with fatigue. Persistent fatigue is common. Being highly sedentary or highly active independently increased the risk of persistent fatigue, suggesting that divergence in either direction from healthy levels of activity increases the risk for persistent fatigue. Mental health is important in the etiology of persistent fatigue. To help define effective preventive strategies, further work is needed on the mechanisms by which these factors contribute to fatigue.

Low cycle fatigue and creep fatigue interaction behavior of 9Cr-0.5Mo-1.8W-V-Nb heat-resistant steel at high temperature

NASA Astrophysics Data System (ADS)

Wang, Xiaowei; Zhang, Wei; Gong, Jianming; Wahab, Magd Abdel

2018-07-01

In this paper, Low Cycle Fatigue (LCF) and Creep-Fatigue Interaction (CFI) behavior of 9Cr-0.5Mo-1.8 W-V-Nb heat-resistant steel (ASME Grade P92 steel) at elevated temperature of 600 °C are investigated. Strain controlled LCF tests are conducted in fully reversed triangular waveform at different strain amplitudes ranging from 0.2% to 0.8%. CFI tests are conducted at 0.4% strain amplitude in trapezoid waveform with tensile hold time varying from 1 min to 60 min and compressive hold time varying from 1 min to 10 min. During LCF and CFI loadings, the evolution of cyclic stress, mean stress and stress relaxation behavior are investigated. It turns out that the softening behavior and lifetime degradation are dependent on strain amplitude, hold time and hold direction. In addition, the microstructure evolution and fracture behavior are characterized by optical, scanning and transmission electron microscope. The initial rapid softening behavior is attributed to the quick elimination of low angle boundaries, whereas no obvious microstructure alteration appears in the stable stage. Fracture behavior analysis reveals creep voids in long-term CFI tests facilitates the initiation and propagation of secondary cracks. The different responses of outer surface oxidation layer during cycling provides an explanation for severer damage of compressive hold and also accounts for the observed various fracture behavior of failed samples.

Efficacy of an Emotion-Focused Treatment for Prolonged Fatigue

ERIC Educational Resources Information Center

Schutte, Nicola S.; Malouff, John M.; Brown, Rhonda F.

2008-01-01

Previous research findings have suggested a relationship between less adaptive emotional functioning and fatigue. The present study used a research design involving multiple baselines across participants to evaluate the efficacy of a new emotion-focused treatment for prolonged fatigue delivered in a cognitive behavioral therapy framework. The 13…

Disease Activity and Damage are not Associated with Increased Levels of Fatigue in Systemic Lupus Erythematosus Patients from LUMINA LXVII, a Multiethnic Cohort

PubMed Central

Burgos, Paula I.; Alarcón, Graciela S.; McGwin, Gerald; Crews, Kendra Q.; Reveille, John D.; Vilá, Luis M.

2009-01-01

Objective To determine the factors associated with increased levels of fatigue over the course of the disease in systemic lupus erythematosus (SLE) patients from LUMINA (Lupus in Minorities: Nature versus Nurture), a longitudinal multiethnic cohort. Methods Patients with SLE (American College of Rheumatology revised and updated criteria), age ≥16 years, disease duration ≤ 5 years at entry into the cohort (T0), of Hispanic (Texan or Puerto Rican), African America or Caucasian ethnicity, were studied. The association between socioeconomic-demographic, health behaviors, behavioral and psychological, functional and clinical characteristics and fatigue was examined using generalized estimating equations to account for the longitudinal nature of the data. Results Five-hundred and fifteen patients (~91% female) contributed 2,609 visits to these analyses; there were: 93 (18.1%) Texan Hispanics, 101 (19.6%) Puerto Rican Hispanics, 169 (32.8%) African Americans, and 152 (29.5%) Caucasians; the patients mean (SD) age and follow up time were 37.2 (12.0) and 4.7 (3.2) years, respectively. Variables associated with increased levels of fatigue in the multivariable analyses were Caucasian ethnicity, the presence of constitutional symptoms(fever, weight loss), higher levels of pain, of abnormal illness-related behaviors and of helplessness (p’s between 0.0018 and <0.0001). Conclusions The presence of pain, abnormal illness-related behaviors, helplessness and constitutional manifestations were associated with increased levels of fatigue; however, lupus specific measures, such as disease activity and damage were not. Interventions aimed at decreasing fatigue need to take into account these findings. PMID:19714612

Effect of NaCl Solution Spraying on Fatigue Lives of Smooth and Slit Specimens of 0.37% Carbon Steel

NASA Astrophysics Data System (ADS)

Makabe, Chobin; Ferdous, Md. Shafiul; Shimabukuro, Akimichi; Murdani, Anggit

2017-07-01

The fatigue crack initiation life and growth rate are affected by experimental conditions. A corrosive environment can be created in a laboratory by means of dropping salt water onto the specimen surface, spraying chloride mist into the experimental chamber, etc. In the case of smooth specimens of some metals, fatigue life is shortened and the fatigue limit disappears under such corrosive experimental conditions. In this study, the effects of intermittent spraying of 3% NaCl solution-mist on corrosion fatigue behavior were investigated. The material used was 0.37% carbon steel. This is called JIS S35C in Japan. Spraying of 3% NaCl solution-mist attacked the surface layer of the specimen. It is well known that the pitting, oxidation-reduction reaction, etc. affect the fatigue strength of metals in a corrosive environment. We carried out corrosion fatigue tests with smooth specimens, holed specimens and slit specimens. Then the effects of such specimen geometry on the fatigue strength were investigated when the NaCl solution-mist was sprayed onto the specimen surface. In the case of lower stress amplitude application in slit specimens, the fatigue life in a corrosive atmosphere was longer than that in the open air. It is discussed that the behavior is related to the crack closure which happens when the oxide builds up and clogs the crack or slit.

Investigation of tension-compression fatigue behavior of a cross-ply metal matrix composite at room and elevated temperatures. Master's thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Boyum, E.A.

1993-12-01

This research, the first load-controlled tension-compression fatigue testing to be performed on a MMC, extends the existing knowledge of MMC fatigue damage mechanisms to include the tension compression loading condition. To accomplish this, a (0/90)2, SCS-6/Ti-15-3 laminate was subjected to tension-tension fatigue at room temperature, and tension-compression fatigue at both room temperature and 427 deg C. Stress and strain data was taken to evaluate the macro-mechanic behavior of the material. Microscopy and fractography were performed to characterize the damage on a micro-mechanic level. On a maximum applied stress basis, the room temperature tension-tension specimens had longer fatigue lives than themore » room temperature tension-compression specimens. The room and high temperature tension-compression fatigue lives were nearly identical in the fiber-dominated high stress region of the SN curve. However, the increased ductility and diffused plasticity of the titanium matrix at 427 deg C delayed the onset and severity of matrix cracking, and thus increased the elevated temperature fatigue lives in the matrix dominated region of the SN curve. In all cases, matrix damage initiated at reaction zone cracks which nucleated both matrix plasticity and matrix cracking. Metal matrix composite, Elevated temperature, Fatigue testing, Compression, Fully-reversed, Titanium, Silicon carbide.« less

Fatigue life of additively manufactured Ti6Al4V scaffolds under tension-tension, tension-compression and compression-compression fatigue load.

PubMed

Lietaert, Karel; Cutolo, Antonio; Boey, Dries; Van Hooreweder, Brecht

2018-03-21

Mechanical performance of additively manufactured (AM) Ti6Al4V scaffolds has mostly been studied in uniaxial compression. However, in real-life applications, more complex load conditions occur. To address this, a novel sample geometry was designed, tested and analyzed in this work. The new scaffold geometry, with porosity gradient between the solid ends and scaffold middle, was successfully used for quasi-static tension, tension-tension (R = 0.1), tension-compression (R = -1) and compression-compression (R = 10) fatigue tests. Results show that global loading in tension-tension leads to a decreased fatigue performance compared to global loading in compression-compression. This difference in fatigue life can be understood fairly well by approximating the local tensile stress amplitudes in the struts near the nodes. Local stress based Haigh diagrams were constructed to provide more insight in the fatigue behavior. When fatigue life is interpreted in terms of local stresses, the behavior of single struts is shown to be qualitatively the same as bulk Ti6Al4V. Compression-compression and tension-tension fatigue regimes lead to a shorter fatigue life than fully reversed loading due to the presence of a mean local tensile stress. Fractographic analysis showed that most fracture sites were located close to the nodes, where the highest tensile stresses are located.

Real-time monitoring of acoustic linear and nonlinear behavior of titanium alloys during low-cycle fatigue and high-cycle fatigue

NASA Astrophysics Data System (ADS)

Frouin, Jerome; Sathish, Shamachary; Na, Jeong K.

2000-05-01

An in-situ technique to measure sound velocity, ultrasonic attenuation and acoustic nonlinear property has been developed for characterization and early detection of fatigue damage in aerospace materials. For this purpose we have developed a computer software and measurement technique including hardware for the automation of the measurement. New transducer holder and special grips are designed. The automation has allowed us to test the long-term stability of the electronics over a period of time and so proof of the linearity of the system. Real-time monitoring of the material nonlinearity has been performed on dog-bone specimens from zero fatigue all the way to the final fracture under low-cycle fatigue test condition (LCF) and high-cycle test condition (HCF). Real-time health monitoring of the material can greatly contribute to the understanding of material behavior under cyclic loading. Interpretation of the results show that correlation exist between the slope of the curve described by the material nonlinearity and the life of the component. This new methodology was developed with an objective to predict the initiation of fatigue microcracks, and to detect, in-situ fatigue crack initiation as well as to quantify early stages of fatigue damage.

Low Cycle Fatigue and Creep-Fatigue Behavior of Alloy 617 at High Temperature

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cabet, Celine; Carroll, Laura; Wright, Richard

Alloy 617 is the leading candidate material for an intermediate heat exchanger (IHX) application of the Very High Temperature Nuclear Reactor (VHTR), expected to have an outlet temperature as high as 950 degrees C. Acceptance of Alloy 617 in Section III of the ASME Code for nuclear construction requires a detailed understanding of the creep-fatigue behavior. Initial creep-fatigue work on Alloy 617 suggests a more dominant role of environment with increasing temperature and/or hold times evidenced through changes in creep-fatigue crack growth mechanism/s and failure life. Continuous cycle fatigue and creep-fatigue testing of Alloy 617 was conducted at 950 degreesmore » C and 0.3% and 0.6% total strain in air to simulate damage modes expected in a VHTR application. Continuous cycle specimens exhibited transgranular cracking. Intergranular cracking was observed in the creep-fatigue specimens, although evidence of grain boundary cavitation was not observed. Despite the absence of grain boundary cavitation to accelerate crack propagation, the addition of a hold time at peak tensile strain was detrimental to cycle life. This suggests that creepfatigue interaction may occur by a different mechanism or that the environment may be partially responsible for accelerating failure.« less

The revised HSE fatigue guidance

DOE Office of Scientific and Technical Information (OSTI.GOV)

Stacey, A.; Sharp, J.V.

1995-12-31

Fatigue cracking has been a principal cause of damage to North Sea structures and consequently considerable attention has been given to the development of guidance for the prediction of fatigue performance. The fatigue guidance of the Offshore Safety Division of the Health and Safety Executive (HSE) was recently revised and published, following a significant offshore industry review in the period 1987 to 1990, and is based on the results of a considerable amount of research and development work on the fatigue behavior of welded tubular and plated joints. As a result of this review, the revised fatigue guidance incorporates severalmore » new clauses and recommendations. The revised recommendations apply to joint classification, basic design S-N curves for welded joints and cast or forged steel components, the thickness effect, the effects of environment and the treatment of low and high stress ranges. Additionally, a new appendix on the derivation of stress concentration factors is included. The new clauses cover high strength steels, bolts and threaded connectors, moorings, repaired joints and the use of fracture mechanics analysis. This paper presents an overview of the revisions to the fatigue guidance, the associated background technical information and aspects of the fatigue behavior of offshore structures which are considered to require further investigation. 67 refs., 7 figs., 8 tabs.« less

Comparative Study on Prediction Effects of Short Fatigue Crack Propagation Rate by Two Different Calculation Methods

NASA Astrophysics Data System (ADS)

Yang, Bing; Liao, Zhen; Qin, Yahang; Wu, Yayun; Liang, Sai; Xiao, Shoune; Yang, Guangwu; Zhu, Tao

2017-05-01

To describe the complicated nonlinear process of the fatigue short crack evolution behavior, especially the change of the crack propagation rate, two different calculation methods are applied. The dominant effective short fatigue crack propagation rates are calculated based on the replica fatigue short crack test with nine smooth funnel-shaped specimens and the observation of the replica films according to the effective short fatigue cracks principle. Due to the fast decay and the nonlinear approximation ability of wavelet analysis, the self-learning ability of neural network, and the macroscopic searching and global optimization of genetic algorithm, the genetic wavelet neural network can reflect the implicit complex nonlinear relationship when considering multi-influencing factors synthetically. The effective short fatigue cracks and the dominant effective short fatigue crack are simulated and compared by the Genetic Wavelet Neural Network. The simulation results show that Genetic Wavelet Neural Network is a rational and available method for studying the evolution behavior of fatigue short crack propagation rate. Meanwhile, a traditional data fitting method for a short crack growth model is also utilized for fitting the test data. It is reasonable and applicable for predicting the growth rate. Finally, the reason for the difference between the prediction effects by these two methods is interpreted.

Low-cycle fatigue testing methods

NASA Technical Reports Server (NTRS)

Lieurade, H. P.

1978-01-01

The good design of highly stressed mechanical components requires accurate knowledge of the service behavior of materials. The main methods for solving the problems of designers are: determination of the mechanical properties of the material after cyclic stabilization; plotting of resistance to plastic deformation curves; effect of temperature on the life on low cycle fatigue; and simulation of notched parts behavior.

The monitoring and fatigue behavior of CFCCs at ambient temperature and 1000{degrees}C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Miriyala, N.; Liaw, P.K.; McHargue, C.J.

1997-04-01

Metallographically polished flexure bars of Nicalon/SiC and Nicalon/alumina composites were subjected to monotonic and cycle-fatigue loadings, with loading either parallel or normal to the fabric plies. The fabric orientation did not significantly affect the mechanical behavior of the Nicalon/SiC composite at ambient temperature. However, the mechanical behavior of the Nicalon/alumina composite was significantly affected by the fabric orientation at ambient temperature in air and at 1000{degrees}C in argon atmosphere. In addition, there was a significant degradation in the fatigue performance of the alumina matrix composite at the elevated temperature, owing to creep in the material and degradation in the fibermore » strength.« less

Associations of fatigue to work-related stress, mental and physical health in an employed community sample.

PubMed

Rose, D M; Seidler, A; Nübling, M; Latza, U; Brähler, E; Klein, E M; Wiltink, J; Michal, M; Nickels, S; Wild, P S; König, J; Claus, M; Letzel, S; Beutel, M E

2017-05-05

While work-related fatigue has become an issue of concern among European employees, the relationship between fatigue, depression and work-related stressors is far from clear. The purposes of this study were (1) to determine the associations of fatigue with work-related stressors, severe medical disease, health behavior and depression in the working population and (2) to determine the unique impact of work-related stressors on fatigue. We used cross-sectional data of N = 7,930 working participants enrolled in the Gutenberg Health Study (GHS) from 2007 to 2012 filled out the Personal Burnout Scale (PBS) of the Copenhagen Psychosocial Questionnaire (COPSOQ), the PHQ-9, and a list of work-related stressors. A total of 27.5% reported increased fatigue, esp. women, younger persons with a lower social status and income, smokers, severely medically ill, previously and currently depressed participants. Fatigue was consistently associated with severe medical disease, health behavior and depression, which need to be taken into account as potential confounders when analyzing its relationship to work-related strains. Depression was consistently associated with work-related stressors. However, after statistically partialling out depression, fatigue was still significantly associated with work-related stress. Fatigue as an indicator of allostatic load is consistently associated with work-related stressors such as work overload after controlling for depression. The brief Personal Burn-out Scale is suitable for assessing work-related fatigue in the general population.

The influence of cell morphology on the compressive fatigue behavior of Ti-6Al-4V meshes fabricated by electron beam melting.

PubMed

Zhao, S; Li, S J; Hou, W T; Hao, Y L; Yang, R; Misra, R D K

2016-06-01

Additive manufacturing technique is a promising approach for fabricating cellular bone substitutes such as trabecular and cortical bones because of the ability to adjust process parameters to fabricate different shapes and inner structures. Considering the long term safe application in human body, the metallic cellular implants are expected to exhibit superior fatigue property. The objective of the study was to study the influence of cell shape on the compressive fatigue behavior of Ti-6Al-4V mesh arrays fabricated by electron beam melting. The results indicated that the underlying fatigue mechanism for the three kinds of meshes (cubic, G7 and rhombic dodecahedron) is the interaction of cyclic ratcheting and fatigue crack growth on the struts, which is closely related to cumulative effect of buckling and bending deformation of the strut. By increasing the buckling deformation on the struts through cell shape design, the cyclic ratcheting rate of the meshes during cyclic deformation was decreased and accordingly, the compressive fatigue strength was increased. With increasing bending deformation of struts, fatigue crack growth in struts contributed more to the fatigue damage of meshes. Rough surface and pores contained in the struts significantly deteriorated the compressive fatigue strength of the struts. By optimizing the buckling and bending deformation through cell shape design, Ti-6Al-4V alloy cellular solids with high fatigue strength and low modulus can be fabricated by the EBM technique. Copyright © 2016 Elsevier Ltd. All rights reserved.

Effect of tensile mean stress on fatigue behavior of single-crystal and directionally solidified superalloys

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Mcgaw, Michael A.

1992-01-01

Two nickel base superalloys, single crystal PWA 1480 and directionally solidified MAR-M 246 + Hf, were studied in view of the potential usage of the former and usage of the latter as blade materials for the turbomachinery of the Space Shuttle main engine. The baseline zero mean stress (ZMS) fatigue life (FL) behavior of these superalloys was established, and then the effect of tensile mean stress (TMS) on their FL behavior was characterized. A stress range based FL prediction approach was used to characterize both the ZMS and TMS fatigue data. In the past, several researchers have developed methods to account for the detrimental effect of tensile mean stress on the FL for polycrystalline engineering alloys. These methods were applied to characterize the TMS fatigue data of single crystal PWA 1480 and directionally solidified MAR-M 246 + Hf and were found to be unsatisfactory. Therefore, a method of accounting for the TMS effect on FL, that is based on a technique proposed by Heidmann and Manson was developed to characterize the TMS fatigue data of these superalloys. Details of this method and its relationship to the conventionally used mean stress methods in FL prediction are discussed.

Effects of environment and frequency on the fatigue behavior of the spallation neutron source (SNS) target container material - 316 LN stainless steel

NASA Astrophysics Data System (ADS)

Tian, Hongbo

As the candidate target container material of the new Spallation Neutron Source (SNS) being designed and constructed at the Oak Ridge National Laboratory (ORNL), Type 316 low-carbon nitrogen-added (LN) stainless steel (SS) will operate in an aggressive environment, subjected to intense fluxes of high-energy protons and neutrons while exposed to liquid mercury. The current project is oriented toward materials studies regarding the effects of test environment and frequency on the fatigue behavior of 316 LN SS. In order to study the structural applications of this material and improve the fundamental understanding of the fatigue damage mechanisms, fatigue tests were performed in air and mercury environments at various frequencies and R ratios (R = sigma min/sigmamax, sigmamin and sigmamax are the applied minimum and maximum stresses, respectively). Fatigue data were developed for the structural design and engineering applications of this material. Specifically, high-cycle fatigue tests, fatigue crack-propagation tests, and ultrahigh cycle fatigue tests up to 10 9 cycles were conducted in air and mercury with test frequencies from 10 Hz to 700 Hz. Microstructure characterizations were performed using optical microscopy (OM), scanning-electron microscopy (SEM), and transmission-electron microscopy (TEM). It was found that mercury doesn't seem to have a large impact on the crack-initiation behavior of 316 LN SS. However, the crack-propagation mechanisms in air and mercury are different in some test conditions. Transgranular cracks seem to be the main mechanism in air, and intergranular in mercury. A significant specimen self-heating effect was found during high-cycle faituge. Theoretical calculation was performed to predict temperature responses of the material subjected to cyclic deformation. The predicted cyclic temperature evolution seems to be in good agreement with the experimental results.

The effects of Nitinol phases on corrosion and fatigue behavior

NASA Astrophysics Data System (ADS)

Denton, Melissa

The purpose of these studies was to provide a detailed understanding of Nitinol phases and their effects on corrosion and fatigue life. The two primary phases, austenite and martensite, were carefully evaluated with respect to material geometry, corrosion behavior, wear, and fatigue life. Material characterization was performed using several techniques that include metallography, scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), x-ray photoelectron spectrum (XPS), and Auger electron spectroscopy (AES). Uniaxial tensile tests were conducted to determine the mechanical properties such as elongation, ultimate tensile strength, modulus, transformation strain, and plateau stress. In addition, accelerated wear testing and four point bend fatigue testing were completed to study the fatigue life and durability of the material. The corrosion of Nitinol was found to be dependent on various surface conditions. Electrochemical corrosion behavior of each phase was investigated using cyclic potentiodyamic polarization testing. The corrosion response of electropolished Nitinol was found to be acceptable, even after durability testing. Stress-induced martensite had a lower breakdown potential due to a rougher surface morphology, while thermally induced martensite and austenite performed similarly well. The surface conditioning also had a significant effect on Nitinol mechanical properties. Electropolishing provided a smooth mirror finish that reduced localized texture and enhanced the ductility of the material. Quasi-static mechanical properties can be good indicators of fatigue life, but further fatigue testing revealed that phase transformations had an important role as well. The governing mechanisms for the fatigue life of Nitinol were determined to be both martesitic phase transformations and surface defects. A new ultimate dislocation strain model was proposed based on specific accelerated step-strain testing.

Near-threshold fatigue behavior of copper alloys in air and aqueous environments: A high cyclic frequency study

NASA Astrophysics Data System (ADS)

Ahmed, Tawfik M.

The near-threshold fatigue crack propagation behavior of alpha-phase copper alloys in desiccated air and several aqueous environments has been investigated. Three commercial alloys of nominal composition Cu-30Ni (Cu-Ni), Cu-30Zn (Cu-Zn) and 90Cu-7Al-3Fe (Cu-Al) were tested. Fatigue tests were conducted using standard prefatigued single edged notched (SEN) specimens loaded in tension at a high frequency of ˜100 Hz. Different R-ratios were employed, mostly at R-ratios of 0.5. Low loading levels were used that corresponded to the threshold and near-threshold regions where Delta Kth ≤ DeltaK ≤ 11 MPa√m. Fatigue tests in the aqueous solutions showed that the effect of different corrosive environments during high frequency testing (˜100 Hz) was not as pronounced as was expected when compared relative to air. Further testing revealed that environmental effects were present and fatigue crack growth rates were influenced by the fluid-induced closure effects which are generally reported in the fatigue literature to be operative only in viscous liquids, not in aqueous solutions. It was concluded that high frequency testing in aqueous environments consistently decreased crack growth rates in a manner similar to crack retardation effects in viscous fluids. Several theoretical models reported in the literature have underestimated, if not failed, to adequately predict the fluid induced closure in aqueous solutions. Results from the desiccated air tests confirmed that, under closure-free conditions (high R-ratios), both threshold values and fatigue crack growth rate of stage II can be related to Young's modulus, in agreement with results from the literature. The role of different mechanical and environmental variables on fatigue behavior becomes most visible in the low R -ratio regime, and contribute to various closure processes.

A comparison of the fatigue behavior of cast Ti-7.5Mo with c.p. titanium, Ti-6Al-4V and Ti-13Nb-13Zr alloys.

PubMed

Lin, Chia-Wei; Ju, Chien-Ping; Chern Lin, Jiin-Huey

2005-06-01

The purpose of the present study is to compare the high-cycle fatigue behavior of newly developed Ti-7.5Mo alloy with that of c.p. Ti, Ti-13Nb-13Zr and Ti-6Al-4V alloys in their as-cast state. Experimental results indicate that Ti-6Al-4V and c.p. Ti have higher stress-controlled fatigue resistance but lower strain-controlled fatigue resistance than Ti-7.5Mo and Ti-13Nb-13Zr. Among four materials Ti-7.5Mo demonstrates the best strain-controlled fatigue performance. The fracture surfaces of the present materials are comprised of three morphologically distinct zones: crack initiation zone, crack propagation zone, and the final-stage overload zone. The fatigue cracks almost always initiate from casting-induced surface/subsurface pores. A river pattern is observed in the propagation zone. In the overload zone dimples are typically observed. Three factors most significantly affecting the fatigue performance of the present materials are the presence of the casting-induced surface/subsurface pores; the location of the pores; and the inherent mechanical properties of the materials.

A Study on Fretting Behavior in Room Temperature for Inconel Alloy 690

NASA Astrophysics Data System (ADS)

Kwon, Jae Do; Chai, Young Suck; Bae, Yong Tak; Choi, Sung Jong

The initial crack under fretting condition occurs at lower stress amplitude and lower cycles of cyclic loading than that under plain fatigue condition. The fretting damage, for example, can be observed in fossil and nuclear power plant, aircraft, automobile and petroleum chemical plants etc. INCONEL alloy 690 is a high-chromium nickel alloy having excellent resistance to many corrosive aqueous media and high-temperature atmospheres. This alloy is used extensively in the industries of nuclear power, chemicals, heat-treatment and electronics. In this paper, the effect of fretting damage on fatigue behavior for INCONEL alloy 690 was studied. Also, various kinds of tests on mechanical properties such as hardness, tension and plain fatigue tests are performed. Fretting fatigue tests were carried out with flat-flat contact configuration using a bridge type contact pad and plate type specimen. Through these experiments, it is found that the fretting fatigue strength decreased about 43% compared to the plain fatigue strength. In fretting fatigue, the wear debris is observed on the contact surface, and the oblique micro-cracks are initiated at an earlier stage. These results can be used as the basic data in a structural integrity evaluation of heat and corrosion resistant alloy considering fretting damages.

Preliminary Study on Fatigue Strengths of Fretted Ti-48Al-2Cr-2Nb

NASA Technical Reports Server (NTRS)

Miyoshi, Kazuhisa; Lerch, Bradley A.; Draper, Susan L.

2002-01-01

The fatigue behavior (stress-life curve) of gamma titanium aluminide (Ti-48Al-2Cr-2Nb, atomic percent) was examined by conducting two tests: first, a fretting wear test with a fatigue specimen in contact with a typical nickel-based superalloy contact pad in air at temperatures of 296 and 823 K and second, a high-cycle fatigue test of the prefretted Ti-48Al-2Cr-2Nb fatigue specimen at 923 K. Reference high-cycle fatigue tests were also conducted with unfretted Ti-48Al-2Cr-2Nb specimens at 923 K. All Ti-48Al-2Cr-2Nb fatigue specimens were machined from cast slabs. The results indicate that the stress-life results for the fretted Ti-48Al-2Cr-2Nb specimens exhibited a behavior similar to those of the unfretted Ti-48Al-2Cr-2Nb specimens. The values of maximum stress and life for the fretted specimens were almost the same as those for the unfretted specimens. The resultant stress-life curve for the unfretted fatigue specimens was very flat. The flat appearance in the stress-life curve of the unfretted specimens is attributed to the presence of a high density of casting pores. The fatigue strengths of both the fretted and unfretted specimens can be significantly affected by the presence of this porosity, which can decrease the fatigue life of Ti-48Al-2Cr-2Nb. The presence of the porosity made discerning the effect of fretting damage on fatigue strength and life of the specimens difficult.

High Velocity Burner Rig Oxidation and Thermal Fatigue Behavior of Si3N4- and SiC Base Ceramics to 1370 Deg C

NASA Technical Reports Server (NTRS)

Sanders, W. A.; Johnston, J. R.

1978-01-01

One SiC material and three Si3N4 materials including hot-pressed Si3N4 as a baseline were exposed in a Mach-1-gas-velocity burner rig simulating a turbine engine environment. Criteria for the materials selection were: potential for gas-turbine usage, near-net-shape fabricability and commercial/domestic availability. Cyclic exposures of test vanes up to 250 cycles (50 hr at temperature) were at leading-edge temperatures to 1370 C. Materials and batches were compared as to weight change, surface change, fluorescent penetrant inspection, and thermal fatigue behavior. Hot-pressed Si3N4 survived the test to 1370 C with slight weight losses. Two types of reaction-sintered Si3N4 displayed high weight gains and considerable weight-change variability, with one material exhibiting superior thermal fatigue behavior. A siliconized SiC showed slight weight gains, but considerable batch variability in thermal fatigue.

Randomized Evaluation of Cognitive-Behavioral Therapy and Graded Exercise Therapy for Post-Cancer Fatigue.

PubMed

Sandler, Carolina X; Goldstein, David; Horsfield, Sarah; Bennett, Barbara K; Friedlander, Michael; Bastick, Patricia A; Lewis, Craig R; Segelov, Eva; Boyle, Frances M; Chin, Melvin T M; Webber, Kate; Barry, Benjamin K; Lloyd, Andrew R

2017-07-01

Cancer-related fatigue is prevalent and disabling. When persistent and unexplained, it is termed post-cancer fatigue (PCF). Cognitive behavioral therapy (CBT) and graded exercise therapy (GET) may improve symptoms and functional outcomes. To evaluate the outcomes of a randomized controlled trial, which assigned patients with post-cancer fatigue to education, or 12 weeks of integrated cognitive-behavioral therapy (CBT) and graded exercise therapy (GET). Three months after treatment for breast or colon cancer, eligible patients had clinically significant fatigue, no comorbid medical or psychiatric conditions that explained the fatigue, and no evidence of recurrence. The CBT/GET arm included individually tailored consultations at approximately two weekly intervals. The education arm included a single visit with clinicians describing the principles of CBT/GET and a booklet. The primary outcome was clinically significant improvement in self-reported fatigue (Somatic and Psychological HEalth REport 0-12), designated a priori as greater than one SD of improvement in fatigue score. The secondary outcome was associated improvement in function (role limitation due to physical health problems-36-Item Short Form Health Survey 0-100) comparing baseline, end treatment (12 weeks), and follow-up (24 weeks). There were 46 patients enrolled, including 43 women (94%), with a mean age of 51 years. Fatigue severity improved in all subjects from a mean of 5.2 (±3.1) at baseline to 3.9 (±2.8) at 12 weeks, suggesting a natural history of improvement. Clinically significant improvement was observed in 7 of 22 subjects in the intervention group compared with 2 of 24 in the education group (P < 0.05, χ 2 ). These subjects also had improvement in functional status compared with nonresponders (P < 0.01, t-test). Combined CBT/GET improves fatigue and functional outcomes for a subset of patients with post-cancer fatigue. Further studies to improve the response rate and the magnitude of the benefit are warranted. Copyright © 2017 American Academy of Hospice and Palliative Medicine. Published by Elsevier Inc. All rights reserved.

Mobile phone text messaging intervention to improve alertness and reduce sleepiness and fatigue during shiftwork among emergency medicine clinicians: study protocol for the SleepTrackTXT pilot randomized controlled trial

PubMed Central

2014-01-01

Background Mental and physical fatigue while at work is common among emergency medical services (EMS) shift workers. Extended shifts (for example 24 hours) and excessive amounts of overtime work increase the likelihood of negative safety outcomes and pose a challenge for EMS fatigue-risk management. Text message-based interventions are a potentially high-impact, low-cost platform for sleep and fatigue assessment and distributing information to workers at risk of negative safety outcomes related to sleep behaviors and fatigue. Methods/Design We will conduct a pilot randomized trial with a convenience sample of adult EMS workers recruited from across the United States using a single study website. Participants will be allocated to one of two possible arms for a 90-day study period. The intervention arm will involve text message assessments of sleepiness, fatigue, and difficulty with concentration at the beginning, during, and end of scheduled shifts. Intervention subjects reporting high levels of sleepiness or fatigue will receive one of four randomly selected intervention messages promoting behavior change during shiftwork. Control subjects will receive assessment only text messages. We aim to determine the performance characteristics of a text messaging tool for the delivery of a sleep and fatigue intervention. We seek to determine if a text messaging program with tailored intervention messages is effective at reducing perceived sleepiness and/or fatigue among emergency medicine clinician shift workers. Additional aims include testing whether a theory-based behavioral intervention, delivered by text message, changes ‘alertness behaviors’. Discussion The SleepTrackTXT pilot trial could provide evidence of compliance and effectiveness that would support rapid widespread expansion in one of two forms: 1) a stand-alone program in the form of a tailored/individualized sleep monitoring and fatigue reduction support service for EMS workers; or 2) an add-on to a multi-component fatigue risk management program led and maintained by employers or by safety and risk management services. Trial Registration Clinicaltrials.gov NCT02063737, Registered on 10 January 2014 PMID:24952387

Effect of service exposure on fatigue crack propagation of Inconel 718 turbine disc material at elevated temperatures

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jeong, Dae-Ho; Choi, Myung-Je; Goto, Masahiro

In this study, the fatigue crack propagation behavior of Inconel 718 turbine disc with different service times from 0 to 4229 h was investigated at 738 and 823 K. No notable change in microstructural features, other than the increase in grain size, was observed with increasing service time. With increasing service time from 0 to 4229 h, the fatigue crack propagation rates tended to increase, while the ΔK{sub th} value decreased, in low ΔK regime and lower Paris' regime at both testing temperatures. The fractographic observation using a scanning electron microscope suggested that the elevated temperature fatigue crack propagation mechanismmore » of Inconel 718 changed from crystallographic cleavage mechanism to striation mechanism in the low ΔK regime, depending on the grain size. The fatigue crack propagation mechanism is proposed for the crack propagating through small and large grains in the low ΔK regime, and the fatigue crack propagation behavior of Inconel 718 with different service times at elevated temperatures is discussed. - Highlights: • The specimens were prepared from the Inconel 718 turbine disc used for 0 to 4229 h. • FCP rates were measured at 738 and 823 K. • The ΔK{sub th} values decreased with increasing service time. • The FCP behavior showed a strong correlation with the grain size of used turbine disc.« less

Study the Cyclic Plasticity Behavior of 508 LAS under Constant, Variable and Grid-Load-Following Loading Cycles for Fatigue Evaluation of PWR Components

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mohanty, Subhasish; Barua, Bipul; Soppet, William K.

This report provides an update of an earlier assessment of environmentally assisted fatigue for components in light water reactors. This report is a deliverable in September 2016 under the work package for environmentally assisted fatigue under DOE’s Light Water Reactor Sustainability program. In an April 2016 report, we presented a detailed thermal-mechanical stress analysis model for simulating the stress-strain state of a reactor pressure vessel and its nozzles under grid-load-following conditions. In this report, we provide stress-controlled fatigue test data for 508 LAS base metal alloy under different loading amplitudes (constant, variable, and random grid-load-following) and environmental conditions (in airmore » or pressurized water reactor coolant water at 300°C). Also presented is a cyclic plasticity-based analytical model that can simultaneously capture the amplitude and time dependency of the component behavior under fatigue loading. Results related to both amplitude-dependent and amplitude-independent parameters are presented. The validation results for the analytical/mechanistic model are discussed. This report provides guidance for estimating time-dependent, amplitude-independent parameters related to material behavior under different service conditions. The developed mechanistic models and the reported material parameters can be used to conduct more accurate fatigue and ratcheting evaluation of reactor components.« less

Mechanical behavior and fatigue performance of SMA short fiber reinforced MMC

NASA Astrophysics Data System (ADS)

Al-Matar, Basem Jawad

The mechanical behavior and performance of Shape Memory Alloy (SMA) short fiber NiTi reinforced Al was experimentally investigated for monotonic and fatigue test Al 6061 NiTi-SiC T6 was superior to unreinforced materials as well as to the reinforced Al T4. Taya three-dimensional model was performed on the monotonic tensile test at room temperature. It showed good agreement with experimental results. In order to utilize the compressive criterion for SMA, the NiTi reinforced Al composite was cooled at -10°C and prestrained at 1.2%. Beyond this limit composite suffered from damage. The net enhancement of SMA effect was around 10 MPa on composite yield stress. Results showed that the elastic constant for the composite did not change with loading and unloading suggesting that the inelastic behavior is plasticity. Further investigation on the inelastic behavior model as damage and/or plasticity by evaluating Poisson's ratio during loading was carried out by Adaptive Image Correlation Technique for Full-Field Strain Measurement. Poisson's ratio increased from around 0.33 to 0.5 demonstrating that it is plasticity that is responsible for the inelastic behavior. Scanning electron microscopy was also used and confirmed model results. The overall damage-behavior was quantified in terms of the post fatigue failure strength for low-cycle fatigue tests. Power law model was best to fit experimental findings.

The Representation of Inflammatory Signals in the Brain – A Model for Subjective Fatigue in Multiple Sclerosis

PubMed Central

Hanken, Katrin; Eling, Paul; Hildebrandt, Helmut

2014-01-01

In multiple sclerosis (MS) patients, fatigue is rated as one of the most common and disabling symptoms. However, the pathophysiology underlying this fatigue is not yet clear. Several lines of evidence suggest that immunological factors, such as elevated levels of pro-inflammatory cytokines, may contribute to subjective fatigue in MS patients. Pro-inflammatory cytokines represent primary mediators of immune-to-brain-communication, modulating changes in the neurophysiology of the central nervous system. Recently, we proposed a model arguing that fatigue in MS patients is a subjective feeling, which is related to inflammation. Moreover, it implies that fatigue can be measured behaviorally only by applying specific cognitive tasks related to alertness and vigilance. In the present review, we focus on the subjective feeling of MS-related fatigue. We examine the hypothesis that the subjective feeling of MS-related fatigue may be a variant of inflammation-induced sickness behavior, resulting from cytokine-mediated activity changes within brain areas involved in interoception and homeostasis including the insula, the anterior cingulate, and the hypothalamus. We first present studies demonstrating a relationship between pro-inflammatory cytokines and subjective fatigue in healthy individuals, in people with inflammatory disorders, and particularly in MS patients. Subsequently, we discuss studies analyzing the impact of anti-inflammatory treatment on fatigue. In the next part of this review, we present studies on the transmission and neural representation of inflammatory signals, with a special focus on possible neural concomitants of inflammation-induced fatigue. We also present two of our studies on the relationship between local gray and white matter atrophy and fatigue in MS patients. Finally, we discuss some implications of our findings and future perspectives. PMID:25566171

Fracture mechanics and corrosion fatigue.

NASA Technical Reports Server (NTRS)

Mcevily, A. J.; Wei, R. P.

1972-01-01

Review of the current state-of-the-art in fracture mechanics, particularly in relation to the study of problems in environment-enhanced fatigue crack growth. The usefulness of this approach in developing understanding of the mechanisms for environmental embrittlement and its engineering utility are discussed. After a brief review of the evolution of the fracture mechanics approach and the study of environmental effects on the fatigue behavior of materials, a study is made of the response of materials to fatigue and corrosion fatigue, the modeling of the mechanisms of the fatigue process is considered, and the application of knowledge of fatigue crack growth to the prediction of the high cycle life of unnotched specimens is illustrated.

Equity-Directed Instructional Practices: Beyond the Dominant Perspective

ERIC Educational Resources Information Center

Rubel, Laurie H.

2017-01-01

In this article, the author synthesizes four equity-directed instructional practices: standards-based mathematics instruction, complex instruction, culturally relevant pedagogy (CRP), and teaching mathematics for social justice (TMfSJ). The author organizes these practices according to the dominant and critical axes in Gutiérrez's (2007a) equity…

Exploring the Use of Multimedia Fate and Bioaccumulation Models to Calculate Trophic Magnification Factors (TMFs)

EPA Science Inventory

The trophic magnification factor (TMF) is considered to be a key metric for assessing the bioaccumulation potential of organic chemicals in food webs. Fugacity is an equilibrium criterion and thus reflects the relative thermodynamic status of a chemical in the environment and in ...

Growth behavior of surface cracks in the circumferential plane of solid and hollow cylinders

NASA Technical Reports Server (NTRS)

Forman, R. G.; Shivakumar, V.

1986-01-01

Experiments were conducted to study the growth behavior of surface fatigue cracks in the circumferential plane of solid and hollow cylinders. In the solid cylinders, the fatigue cracks were found to have a circular arc crack front with specific upper and lower limits to the arc radius. In the hollow cylinders, the fatigue cracks were found to agree accurately with the shape of a transformed semiellipse. A modification to the usual nondimensionalization expression used for surface flaws in flat plates was found to give correct trends for the hollow cylinder problem.

Fatigue characteristics of carbon nanotube blocks under compression

NASA Astrophysics Data System (ADS)

Suhr, J.; Ci, L.; Victor, P.; Ajayan, P. M.

2008-03-01

In this paper we investigate the mechanical response from repeated high compressive strains on freestanding, long, vertically aligned multiwalled carbon nanotube membranes and show that the arrays of nanotubes under compression behave very similar to soft tissue and exhibit viscoelastic behavior. Under compressive cyclic loading, the mechanical response of nanotube blocks shows initial preconditioning and hysteresis characteristic of viscoeleastic materials. Furthermore, no fatigue failure is observed even at high strain amplitudes up to half million cycles. The outstanding fatigue life and extraordinary soft tissue-like mechanical behavior suggest that properly engineered carbon nanotube structures could mimic artificial muscles.

Data demonstrating the effects of build orientation and heat treatment on fatigue behavior of selective laser melted 17-4 PH stainless steel.

PubMed

Yadollahi, Aref; Simsiriwong, Jutima; Thompson, Scott M; Shamsaei, Nima

2016-06-01

Axial fully-reversed strain-controlled ([Formula: see text]) fatigue experiments were performed to obtain data demonstrating the effects of building orientation (i.e. vertical versus horizontal) and heat treatment on the fatigue behavior of 17-4 PH stainless steel (SS) fabricated via Selective Laser Melting (SLM) (Yadollahi et al., submitted for publication [1]). This data article provides detailed experimental data including cyclic stress-strain responses, variations of peak stresses during cyclic deformation, and fractography of post-mortem specimens for SLM 17-4 PH SS.

Data demonstrating the effects of build orientation and heat treatment on fatigue behavior of selective laser melted 17–4 PH stainless steel

PubMed Central

Yadollahi, Aref; Simsiriwong, Jutima; Thompson, Scott M.; Shamsaei, Nima

2016-01-01

Axial fully-reversed strain-controlled (R=−1) fatigue experiments were performed to obtain data demonstrating the effects of building orientation (i.e. vertical versus horizontal) and heat treatment on the fatigue behavior of 17–4 PH stainless steel (SS) fabricated via Selective Laser Melting (SLM) (Yadollahi et al., submitted for publication [1]). This data article provides detailed experimental data including cyclic stress-strain responses, variations of peak stresses during cyclic deformation, and fractography of post-mortem specimens for SLM 17–4 PH SS. PMID:26955653

Tensile and fatigue behaviors of printed Ag thin films on flexible substrates

NASA Astrophysics Data System (ADS)

Sim, Gi-Dong; Won, Sejeong; Lee, Soon-Bok

2012-11-01

Flexible electronics using nanoparticle (NP) printing has been highlighted as a key technology enabling eco-friendly, low-cost, and large-area fabrication. For NP-based printing to be used as a successive alternative to photolithography and vacuum deposition, stretchability and long term reliability must be considered. This paper reports the stretchability and fatigue behavior of 100 nm thick NP-based silver thin films printed on polyethylene-terephthalate substrate and compares it to films deposited by electron-beam evaporation. NP-based films show stretchability and fatigue life comparable to evaporated films with intergranular fracture as the dominant failure mechanism.

Fatigue behavior of Long and Short Cracks in Aluminum Alloys.

DTIC Science & Technology

1987-05-01

Mughrabi : in ’Strength ,f met als ind 121. S. Suresh. D. M. Parks, and R.0. Ritchie: in allws’. (ed. P. Haasen (,t %i. V I. Fatigue thresholds’, ed. J...RITCHIE ET AL . ft MAY 67 W ASSIFED UC/RP/ /A14 AFOSR-TR-B7- F/O 1.1NML LEhEEINOE2 hohEE ’EhmhELIEEmhEsh EEEmohhhhhhEEEE EEEmhEEEmhhEEI...TASK IWORK UNIT ELEMENT NO. NO. NO. ACCESSION NO. 0,0 61102F 2306 Al 11. TITLE Include Security Clasfication) FATIGUE BEHAVIOR OF LONG AND SHORT

Is Maternal Fatigue Mediating the Relationship between Maternal Depression and Child Outcomes?

ERIC Educational Resources Information Center

White, Carmel Parker; King, Kathleen

2011-01-01

Fatigue, a subjective state that has been defined as a decreased capacity for physical or mental activity, has many behavioral similarities to depression (e.g., weariness, difficulty concentrating, diminished motivation). We hypothesized that fatigue might mediate the relationship between depression and poor child outcomes. A sample of mothers (14…

Comparison of dynamic fatigue behavior between SiC whisker-reinforced composite and monolithic silicon nitrides

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Salem, Jonathan A.

1991-01-01

The dynamic fatigue behavior of 30 vol percent silicon nitride whisker-reinforced composite and monolithic silicon nitrides were determined as a function of temperature from 1100 to 1300 C in ambient air. The fatigue susceptibility parameter, n, decreased from 88.1 to 20.1 for the composite material, and from 50.8 to 40.4 for the monolithic, with increasing temperature from 1100 to 1300 C. A transition in the dynamic fatigue curve occurred for the composite material at a low stressing rate of 2 MPa/min at 1300 C, resulting in a very low value of n equals 5.8. Fractographic analysis showed that glassy phases in the slow crack growth region were more pronounced in the composite compared to the monolithic material, implying that SiC whisker addition promotes the formation of glass rich phases at the grain boundaries, thereby enhancing fatigue. These results indicate that SiC whisker addition to Si3 N4 matrix substantially deteriorates fatigue resistance inherent to the matrix base material for this selected material system.

Response of resin transfer molded (RTM) composites under reversed cyclic loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahfuz, H.; Haque, A.; Yu, D.

1996-01-01

Compressive behavior and the tension-compression fatigue response of resin transfer molded IM7 PW/PR 500 composite laminate with a circular notch have been studied. Fatigue damage characteristics have been investigated through the changes in the laminate strength and stiffness by gradually incrementing the fatigue cycles at a preselected load level. Progressive damage in the surface of the laminate during fatigue has been investigated using cellulose replicas. Failure mechanisms during static and cyclic tests have been identified and presented in detail. Extensive debonding of filaments and complete fiber bundle fracture accompanied by delamination were found to be responsible for fatigue failures, whilemore » fiber buckling, partial fiber fracture and delamination were characterized as the failure modes during static tests. Weibull analysis of the static, cyclic and residual tests have been performed and described in detail. Fractured as well as untested specimens were C-scanned, and the progressive damage growth during fatigue is presented. Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) for the fractured specimen were also performed and the analysis of the failure behavior is presented.« less

Fatigue behavior of a cross-ply ceramic matrix composite subjected to tension-tension cycling with hold time. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grant, S.A.

This study was carried out to investigate the elevated temperature behavior of the SiC-MAS5 cross- ply (O/9O)4S ceramic matrix composite manufactured by Corning Inc. to fatigue with loading waveforms that combine the characteristics of stress rupture and high cycle fatigue. The test results were compiled in the form of S-N (cycles to failure), S-T (exposure time versus cycles to failure), S-S (energy exposure versus cycles to failure), normalized modulus degradation, strain progression, and hysteresis loop progression. From the mechanical behavior demonstrated by these curves, relationships between the effect of the environment and loading waveform were developed. In addition, a post-mortemmore » SEM analysis of the fracture surface was conducted and the results compared to the mechanical behavior.« less

Axial-Load Fatigue Tests on 17-7 PH Stainless Steel Under Constant-Amplitude Loading

NASA Technical Reports Server (NTRS)

Leybold, Herbert A.

1960-01-01

Axial-load fatigue tests were conducted at room temperature on notched and unnotched sheet specimens of 17-7 PH stainless steel in Condition TH 1050. The notched specimens had theoretical stress-concentration factors of 2.32, 4.00, and 5.00. All specimens were tested under completely reversed loading. S-N curves are presented for each specimen configuration and ratios of fatigue strengths of unnotched specimens to those of notched specimens are given. Predictions of the fatigue behavior of notched specimens near the fatigue limit were made.

Effects of Different R ratios on Fatigue Crack Growth in Laser Peened Friction Stir Welds

NASA Technical Reports Server (NTRS)

Hatamleh, Omar; Hackel, Lloyd; Forth, Scott

2007-01-01

The influence of laser peening on the fatigue crack growth behavior of friction stir welded (FSW) Aluminum Alloy (AA) 7075-T7351 sheets was investigated. The surface modification resulting from the peening process on the fatigue crack growth of FSW was assessed for two different R ratios. The investigation indicated a significant decrease in fatigue crack growth rates resulting from using laser shock peening compared with unpeened, welded and unwelded specimens. The slower fatigue crack growth rate was attributed to the compressive residual stresses induced by the peening.

The fatigue strength of riveted joints and lugs

NASA Technical Reports Server (NTRS)

Schijve, J

1956-01-01

This report deals with a number of tests on riveted joints and lugs for the primary purpose of comparing the several types of riveted joints and to study the effect of various factors on the fatigue strength of lugs. A check was made to ascertain whether or not an estimate of the fatigue life at a certain loading could be made from the dimensions of the joint and the fatigue data of the unnotched materials. Recommendations are made on the proportioning of joints to obtain better fatigue behavior.

Fatigue crack layer propagation in silicon-iron

NASA Technical Reports Server (NTRS)

Birol, Y.; Welsch, G.; Chudnovsky, A.

1986-01-01

Fatigue crack propagation in metal is almost always accompanied by plastic deformation unless conditions strongly favor brittle fracture. The analysis of the plastic zone is crucial to the understanding of crack propagation behavior as it governs the crack growth kinetics. This research was undertaken to study the fatigue crack propagation in a silicon iron alloy. Kinetic and plasticity aspects of fatigue crack propagation in the alloy were obtained, including the characterization of damage evolution.

Relationships between parental sleep quality, fatigue, cognitions about infant sleep, and parental depression pre and post-intervention for infant behavioral sleep problems.

PubMed

Hall, Wendy A; Moynihan, Melissa; Bhagat, Radhika; Wooldridge, Joanne

2017-04-04

Maternal and paternal depression has been associated with infants' behavioral sleep problems. Behavioral sleep interventions, which alter parental cognitions about infant sleep, have improved infant sleep problems. This study reports relationships between parental depression, fatigue, sleep quality, and cognitions about infant sleep pre and post-intervention for a behavioral sleep problem. This secondary analysis of data from Canadian parents (n = 455), with healthy infants aged 6-to-8-months exposed to a behavioral sleep intervention, examined baseline data and follow-up data from 18 or 24 weeks post intervention (group teaching or printed material) exposure. Parents reported on sleep quality, fatigue, depression, and cognitions about infant sleep. Data were analyzed using Pearson's r and stepwise regression analysis. Parents' fatigue, sleep quality, sleep cognitions, and depression scores were correlated at baseline and follow-up. At baseline, sleep quality (b = .52, 95% CI .19-.85), fatigue (b = .48, 95% CI .33-.63), doubt about managing infant sleep (b = .44, 95% CI .19-.69), and anger about infant sleep (b = .69, 95% CI .44-.94) were associated with mothers' depression. At baseline, fathers' depression related to sleep quality (b = .42, 95% CI .01-.83), fatigue (b = .47, 95% CI .32-.63), and doubt about managing infant sleep (b = .50, 95% CI .24-.76). At follow-up, mothers' depression was associated with sleep quality (b = .76, 95% CI .41-1.12), fatigue (b = .25, 95% CI .14-.37), doubt about managing infant sleep (b = .44, 95% CI .16-.73), sleep anger (b = .31, 95% CI .02-.59), and setting sleep limits (b = -.22, 95% CI -.41-[-.03]). At follow-up, fathers' depression related to sleep quality (b = .84, 95% CI .46-1.22), fatigue (b = .31, 95% CI .17-.45), sleep doubt (b = .34, 95% CI .05-.62), and setting sleep limits (b = .25, 95% CI .01-.49). Mothers' and fathers' cognitions about infant sleep demonstrate complex relationships with their depression scores. While mothers' setting sleep limit scores are associated with decreased depression scores, fathers' setting limits scores are associated with increased depression scores. Parental doubts about managing infant sleep and difficulties with setting sleep limits require attention in interventions.

High temperature tension-compression fatigue behavior of a tungsten copper composite

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Gabb, Timothy P.

1990-01-01

The high temperature fatigue of a (O)12 tungsten fiber reinforced copper matrix composite was investigated. Specimens having fiber volume percentages of 10 and 36 were fatigued under fully-reversed, strain-controlled conditions at both 260 and 560 C. The fatigue life was found to be independent of fiber volume fraction because fatigue damage preferentially occurred in the matrix. Also, the composite fatigue lives were shorter at 560 C as compared to 260 C due to changes in mode of matrix failure. On a total strain basis, the fatigue life of the composite at 560 C was the same as the life of unreinforced copper, indicating that the presence of the fibers did not degrade the fatigue resistance of the copper matrix in this composite system. Comparison of strain-controlled fatigue data to previously-generated load-controlled data revealed that the strain-controlled fatigue lives were longer because of mean strain and mean stress effects.

Relationship Between Unusual High-Temperature Fatigue Crack Growth Threshold Behavior in Superalloys and Sudden Failure Mode Transitions

NASA Technical Reports Server (NTRS)

Telesman, J.; Smith, T. M.; Gabb, T. P.; Ring, A. J.

2017-01-01

An investigation of high temperature cyclic fatigue crack growth (FCG) threshold behavior of two advanced nickel disk alloys was conducted. The focus of the study was the unusual crossover effect in the near-threshold region of these type of alloys where conditions which produce higher crack growth rates in the Paris regime, produce higher resistance to crack growth in the near threshold regime. It was shown that this crossover effect is associated with a sudden change in the fatigue failure mode from a predominant transgranular mode in the Paris regime to fully intergranular mode in the threshold fatigue crack growth region. This type of a sudden change in the fracture mechanisms has not been previously reported and is surprising considering that intergranular failure is typically associated with faster crack growth rates and not the slow FCG rates of the near-threshold regime. By characterizing this behavior as a function of test temperature, environment and cyclic frequency, it was determined that both the crossover effect and the onset of intergranular failure are caused by environmentally driven mechanisms which have not as yet been fully identified. A plausible explanation for the observed behavior is proposed.

Fatigue crack growth and fracture behavior of bainitic rail steels.

DOT National Transportation Integrated Search

2011-08-01

"The microstructuremechanical properties relationships, fracture toughness, fatigue crack growth and fracture surface morphology of J6 bainitic, manganese, and pearlitic rail steels were studied. Microstructuremechanical properties correlation ...

Fatigue crack growth and fracture behavior of bainitic rail steels.

DOT National Transportation Integrated Search

2011-09-01

"The microstructuremechanical properties relationships, fracture toughness, fatigue crack growth and fracture surface morphology of J6 bainitic, manganese, and pearlitic rail steels were studied. Microstructuremechanical properties correlation ...

Comparison of the Fatigue Behavior of Copper Alloys

NASA Technical Reports Server (NTRS)

Lerch, Brad; Ellis, David

2006-01-01

This presentation is about the development of advanced copper alloys with high thermal conductivity, good creep strength, and adequate fatigue strength for rocket engine applications. It also focuses on the commercial availability of the advanced alloy-GRCop-84 developed at NASA-GRC. The presentation's conclusions are that GRCop-84 has equivalent or better isothermal fatigue lives compared to other commercially available copper alloys, that GRCop-84 can be fabricated in various forms with minimal change in the fatigue lives, that it is equivalent in sothermal, fatigue to AMZIRC at moderate temperatures, and that Narloy-Z is equivalent in fatigue capabilities to GRCop-84 at 400C and below.

Strength, Fracture Toughness, Fatigue, and Standardization Issues of Free-standing Thermal Barrier Coatings

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Zhu, Dong-Ming; Miller, Robert A.

2003-01-01

Strength, fracture toughness and fatigue behavior of free-standing thick thermal barrier coatings of plasma-sprayed ZrO2-8wt % Y2O3 were determined at ambient and elevated temperatures in an attempt to establish a database for design. Strength, in conjunction with deformation (stress-strain behavior), was evaluated in tension (uniaxial and trans-thickness), compression, and uniaxial and biaxial flexure; fracture toughness was determined in various load conditions including mode I, mode II, and mixed modes I and II; fatigue or slow crack growth behavior was estimated in cyclic tension and dynamic flexure loading. Effect of sintering was quantified through approaches using strength, fracture toughness, and modulus (constitutive relations) measurements. Standardization issues on test methodology also was presented with a special regard to material's unique constitutive relations.

Fatigue loading and R-curve behavior of a dental glass-ceramic with multiple flaw distributions.

PubMed

Joshi, Gaurav V; Duan, Yuanyuan; Della Bona, Alvaro; Hill, Thomas J; St John, Kenneth; Griggs, Jason A

2013-11-01

To determine the effects of surface finish and mechanical loading on the rising toughness curve (R-curve) behavior of a fluorapatite glass-ceramic (IPS e.max ZirPress) and to determine a statistical model for fitting fatigue lifetime data with multiple flaw distributions. Rectangular beam specimens were fabricated by pressing. Two groups of specimens (n=30) with polished (15 μm) or air abraded surface were tested under rapid monotonic loading in oil. Additional polished specimens were subjected to cyclic loading at 2 Hz (n=44) and 10 Hz (n=36). All fatigue tests were performed using a fully articulated four-point flexure fixture in 37°C water. Fractography was used to determine the critical flaw size and estimate fracture toughness. To prove the presence of R-curve behavior, non-linear regression was used. Forward stepwise regression was performed to determine the effects on fracture toughness of different variables, such as initial flaw type, critical flaw size, critical flaw eccentricity, cycling frequency, peak load, and number of cycles. Fatigue lifetime data were fit to an exclusive flaw model. There was an increase in fracture toughness values with increasing critical flaw size for both loading methods (rapid monotonic loading and fatigue). The values for the fracture toughness ranged from 0.75 to 1.1 MPam(1/2) reaching a plateau at different critical flaw sizes based on loading method. Cyclic loading had a significant effect on the R-curve behavior. The fatigue lifetime distribution was dependent on the flaw distribution, and it fit well to an exclusive flaw model. Copyright © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Fatigue loading and R-curve behavior of a dental glass-ceramic with multiple flaw distributions

PubMed Central

Joshi, Gaurav V.; Duan, Yuanyuan; Bona, Alvaro Della; Hill, Thomas J.; John, Kenneth St.; Griggs, Jason A.

2013-01-01

Objectives To determine the effects of surface finish and mechanical loading on the rising toughness curve (R-curve) behavior of a fluorapatite glass-ceramic (IPS e.max ZirPress) and to determine a statistical model for fitting fatigue lifetime data with multiple flaw distributions. Materials and Methods Rectangular beam specimens were fabricated by pressing. Two groups of specimens (n=30) with polished (15 μm) or air abraded surface were tested under rapid monotonic loading in oil. Additional polished specimens were subjected to cyclic loading at 2 Hz (n=44) and 10 Hz (n=36). All fatigue tests were performed using a fully articulated four-point flexure fixture in 37°C water. Fractography was used to determine the critical flaw size and estimate fracture toughness. To prove the presence of R-curve behavior, non-linear regression was used. Forward stepwise regression was performed to determine the effects on fracture toughness of different variables, such as initial flaw type, critical flaw size, critical flaw eccentricity, cycling frequency, peak load, and number of cycles. Fatigue lifetime data were fit to an exclusive flaw model. Results There was an increase in fracture toughness values with increasing critical flaw size for both loading methods (rapid monotonic loading and fatigue). The values for the fracture toughness ranged from 0.75 to 1.1 MPa·m1/2 reaching a plateau at different critical flaw sizes based on loading method. Significance Cyclic loading had a significant effect on the R-curve behavior. The fatigue lifetime distribution was dependent on the flaw distribution, and it fit well to an exclusive flaw model. PMID:24034441

Cognitive behavioral therapy positively affects fatigue in patients with multiple sclerosis: Results of a randomized controlled trial.

PubMed

van den Akker, Lizanne E; Beckerman, Heleen; Collette, Emma H; Twisk, Jos Wr; Bleijenberg, Gijs; Dekker, Joost; Knoop, Hans; de Groot, Vincent

2017-10-01

Fatigue is a common symptom in multiple sclerosis (MS) and often restricts societal participation. Cognitive behavioral therapy (CBT) may alleviate MS-related fatigue, but evidence in literature is inconclusive. To evaluate the effectiveness of CBT to improve MS-related fatigue and participation. In a multi-center, assessor-masked, randomized controlled trial, participants with severe MS-related fatigue were assigned to CBT or control treatment. CBT consisted of 12 individual sessions with a psychologist trained in CBT, the control treatment consisted of three consultations with a MS nurse, both delivered over 16 weeks. Assessments were at baseline, 8, 16 (i.e. post-intervention), 26, and 52 weeks post-baseline. Primary outcomes were the Checklist Individual Strength-fatigue subscale (CIS20r fatigue) and the Impact on Participation and Autonomy questionnaire (IPA). Data were analyzed according to the intention-to-treat principle, using mixed-model analysis. Between 2011 and 2014, 91 patients were randomized (CBT: n = 44; control: n = 47). Between-group analysis showed a positive post-intervention effect for CBT on CIS20r fatigue (T16: -6.7 (95% confidence interval (CI) = -10.7; -2.7) points) that diminished during follow-up (T52: 0.5 (95% CI = -3.6; 4.4)). No clinically relevant effects were found on societal participation. Severe MS-related fatigue can be reduced effectively with CBT in the short term. More research is needed on how to maintain this effect over the long term.

Differences in Physical and Psychosocial Characteristics Between CFS and Fatigued Non-CFS Patients, a Case-Control Study.

PubMed

De Gucht, Veronique; Garcia, Franshelis Katerinee; den Engelsman, Marielle; Maes, Stan

2016-10-01

The main research question is: "Do CFS patients differ from fatigued non-CFS patients with respect to physical, cognitive, behavioral, social, and emotional determinants?" In addition, group differences in relevant outcomes were explored. Patients who met the Centers for Disease Control (CDC) criteria for CFS were categorized as CFS; these patients were mainly recruited via a large Dutch patient organization. Primary care patients who were fatigued for at least 1 month and up to 2 years but did not meet the CDC criteria were classified as fatigued non-CFS patients. Both groups were matched by age and gender (N = 192 for each group). CFS patients attributed their fatigue more frequently to external causes, reported a worse physical functioning, more medical visits, and a lower employment rate. The results of a multiple logistic regression analysis showed that patients who believe that their fatigue is associated with more severe consequences, that their fatigue will last longer and is responsible for more additional symptoms are more likely to be classified as CFS, while patients who are more physically active and have higher levels of "all or nothing behavior" are less likely to be classified as having CFS. A longitudinal study should explore the predictive value of the above factors for the transition from medically unexplained fatigue to CFS in order to develop targeted interventions for primary care patients with short-term fatigue complaints.

Impact of sleep, fatigue, and systemic inflammation on neurocognitive and behavioral outcomes in long-term survivors of childhood acute lymphoblastic leukemia.

PubMed

Cheung, Yin Ting; Brinkman, Tara M; Mulrooney, Daniel A; Mzayek, Yasmin; Liu, Wei; Banerjee, Pia; Panoskaltsis-Mortari, Angela; Srivastava, Deokumar; Pui, Ching-Hon; Robison, Leslie L; Hudson, Melissa M; Krull, Kevin R

2017-09-01

Long-term survivors of childhood acute lymphoblastic leukemia (ALL) are at risk for neurocognitive impairment, which may be associated with fatigue, sleep problems, systemic inflammation, and oxidative stress. We examined these associations among survivors of childhood ALL treated with chemotherapy only. Survivors of childhood ALL (male, n = 35 and female, n = 35; mean age, 14.3 years [standard deviation, 4.7 years] and mean years from diagnosis, 7.4 years [standard deviation, 1.9 years]) completed neurocognitive testing, behavioral ratings, and reported sleep quality and fatigue symptoms 5 years after diagnosis. Serum was collected concurrently and assayed for interleukin (IL)-1β and IL-6, tumor necrosis factor α (TNF-α), high-sensitivity C-reactive protein (hsCRP), malondialdehyde, myeloperoxidase, and oxidized low-density lipoprotein. General linear modeling was used to assess associations among biomarkers and functional outcomes, adjusting for age and stratified by sex. Survivors performed worse than population norms on executive function and processing speed and reported more behavioral problems (P < .05 adjusted for multiple comparison). In female survivors, fatigue was associated with poor executive function (r = 0.41; P = .02), processing speed (r = 0.56; P < .001), and attention (r = 0.36-0.55; P < .05). Female survivors with frequent nighttime awakening displayed more inattention (P = .01), hyperactivity (P = .03), and aggression (P = .01). Worse executive function, processing speed, and behavioral symptoms were observed in female survivors with higher levels of IL-6, IL-1β, and hsCRP (P < .05). Male survivors with high levels of TNF-α demonstrated worse organization (P = .03), but no significant associations between neurocognitive outcomes and sleep/fatigue measures were observed. Neurocognitive function in female survivors of childhood ALL appears more susceptible to the effects of sleep disturbance and fatigue. Systemic inflammation may play a role in neurocognitive impairment and behavioral symptoms. Cancer 2017;123:3410-9. © 2017 American Cancer Society. © 2017 American Cancer Society.

Very high-cycle fatigue failure in micron-scale polycrystalline silicon films: Effects of environment and surface oxide thickness

NASA Astrophysics Data System (ADS)

Alsem, D. H.; Timmerman, R.; Boyce, B. L.; Stach, E. A.; De Hosson, J. Th. M.; Ritchie, R. O.

2007-01-01

Fatigue failure in micron-scale polycrystalline silicon structural films, a phenomenon that is not observed in bulk silicon, can severely impact the durability and reliability of microelectromechanical system devices. Despite several studies on the very high-cycle fatigue behavior of these films (up to 1012cycles), there is still an on-going debate on the precise mechanisms involved. We show here that for devices fabricated in the multiuser microelectromechanical system process (MUMPs) foundry and Sandia Ultra-planar, Multi-level MEMS Technology (SUMMiT V™) process and tested under equi-tension/compression loading at ˜40kHz in different environments, stress-lifetime data exhibit similar trends in fatigue behavior in ambient room air, shorter lifetimes in higher relative humidity environments, and no fatigue failure at all in high vacuum. The transmission electron microscopy of the surface oxides in the test samples shows a four- to sixfold thickening of the surface oxide at stress concentrations after fatigue failure, but no thickening after overload fracture in air or after fatigue cycling in vacuo. We find that such oxide thickening and premature fatigue failure (in air) occur in devices with initial oxide thicknesses of ˜4nm (SUMMiT V™) as well as in devices with much thicker initial oxides ˜20nm (MUMPs). Such results are interpreted and explained by a reaction-layer fatigue mechanism. Specifically, moisture-assisted subcritical cracking within a cyclic stress-assisted thickened oxide layer occurs until the crack reaches a critical size to cause catastrophic failure of the entire device. The entirety of the evidence presented here strongly indicates that the reaction-layer fatigue mechanism is the governing mechanism for fatigue failure in micron-scale polycrystalline silicon thin films.

Development and Characterization of Embedded Sensory Particles Using Multi-Scale 3D Digital Image Correlation

NASA Technical Reports Server (NTRS)

Cornell, Stephen R.; Leser, William P.; Hochhalter, Jacob D.; Newman, John A.; Hartl, Darren J.

2014-01-01

A method for detecting fatigue cracks has been explored at NASA Langley Research Center. Microscopic NiTi shape memory alloy (sensory) particles were embedded in a 7050 aluminum alloy matrix to detect the presence of fatigue cracks. Cracks exhibit an elevated stress field near their tip inducing a martensitic phase transformation in nearby sensory particles. Detectable levels of acoustic energy are emitted upon particle phase transformation such that the existence and location of fatigue cracks can be detected. To test this concept, a fatigue crack was grown in a mode-I single-edge notch fatigue crack growth specimen containing sensory particles. As the crack approached the sensory particles, measurements of particle strain, matrix-particle debonding, and phase transformation behavior of the sensory particles were performed. Full-field deformation measurements were performed using a novel multi-scale optical 3D digital image correlation (DIC) system. This information will be used in a finite element-based study to determine optimal sensory material behavior and density.

In vitro fatigue behavior of restorative composites and glass ionomers.

PubMed

Braem, M J; Lambrechts, P; Gladys, S; Vanherle, G

1995-03-01

This in vitro study was conducted to investigate the fatigue behavior of several dental restoratives, including composites, glass ionomers and a resin-reinforced glass ionomer. Fatigue was imposed under a reverse stress-controlled regimen, following a staircase approach. Samples were stored and tested under both dry and wet conditions. The following parameters were measured and analyzed: Young's modulus, restrained fracture strength, and flexural fatigue limit. As a general trend, all products showed a decrease in Young's modulus following water sorption. For all products except the resin-reinforced glass ionomer, the same trend was seen in the restrained fracture strength. This is, however, no longer valid for the flexural fatigue limit: the trend is steady-state for the glass ionomers, status quo for the resin-reinforced glass ionomer, and all composites tested show a decrease. The diversity in structure of both composites and glass ionomers does not allow findings for one product to be extrapolated to other similar products.

Effects of Stress Ratio and Microstructure on Fatigue Failure Behavior of Polycrystalline Nickel Superalloy

NASA Astrophysics Data System (ADS)

Zhang, H.; Guan, Z. W.; Wang, Q. Y.; Liu, Y. J.; Li, J. K.

2018-05-01

The effects of microstructure and stress ratio on high cycle fatigue of nickel superalloy Nimonic 80A were investigated. The stress ratios of 0.1, 0.5 and 0.8 were chosen to perform fatigue tests in a frequency of 110 Hz. Cleavage failure was observed, and three competing failure crack initiation modes were discovered by a scanning electron microscope, which were classified as surface without facets, surface with facets and subsurface with facets. With increasing the stress ratio from 0.1 to 0.8, the occurrence probability of surface and subsurface with facets also increased and reached the maximum value at R = 0.5, meanwhile the probability of surface initiation without facets decreased. The effect of microstructure on the fatigue fracture behavior at different stress ratios was also observed and discussed. Based on the Goodman diagram, it was concluded that the fatigue strength of 50% probability of failure at R = 0.1, 0.5 and 0.8 is lower than the modified Goodman line.

Advances in Fatigue and Fracture Mechanics Analyses for Aircraft Structures

NASA Technical Reports Server (NTRS)

Newman, J. C., Jr.

1999-01-01

This paper reviews some of the advances that have been made in stress analyses of cracked aircraft components, in the understanding of the fatigue and fatigue-crack growth process, and in the prediction of residual strength of complex aircraft structures with widespread fatigue damage. Finite-element analyses of cracked structures are now used to determine accurate stress-intensity factors for cracks at structural details. Observations of small-crack behavior at open and rivet-loaded holes and the development of small-crack theory has lead to the prediction of stress-life behavior for components with stress concentrations under aircraft spectrum loading. Fatigue-crack growth under simulated aircraft spectra can now be predicted with the crack-closure concept. Residual strength of cracked panels with severe out-of-plane deformations (buckling) in the presence of stiffeners and multiple-site damage can be predicted with advanced elastic-plastic finite-element analyses and the critical crack-tip-opening angle (CTOA) fracture criterion. These advances are helping to assure continued safety of aircraft structures.

Advances in Fatigue and Fracture Mechanics Analyses for Metallic Aircraft Structures

NASA Technical Reports Server (NTRS)

Newman, J. C., Jr.

2000-01-01

This paper reviews some of the advances that have been made in stress analyses of cracked aircraft components, in the understanding of the fatigue and fatigue-crack growth process, and in the prediction of residual strength of complex aircraft structures with widespread fatigue damage. Finite-element analyses of cracked metallic structures are now used to determine accurate stress-intensity factors for cracks at structural details. Observations of small-crack behavior at open and rivet-loaded holes and the development of small-crack theory has lead to the prediction of stress-life behavior for components with stress concentrations under aircraft spectrum loading. Fatigue-crack growth under simulated aircraft spectra can now be predicted with the crack-closure concept. Residual strength of cracked panels with severe out-of-plane deformations (buckling) in the presence of stiffeners and multiple-site damage can be predicted with advanced elastic-plastic finite-element analyses and the critical crack-tip-opening angle (CTOA) fracture criterion. These advances are helping to assure continued safety of aircraft structures.

Effect of moisture on the fatigue behavior of graphite/epoxy composite laminates

NASA Technical Reports Server (NTRS)

Ramani, S. V.; Nelson, H. G.

1979-01-01

The form of the moisture distribution in the specimen (gradient and flat profile) was considered to establish the influence of accelerated moisture conditioning on fatigue behavior. For the gradient specimens having an average moisture content of 1.4 percent, fatigue life was reduced by a factor of 8 at all stress levels investigated. Corresponding reduction in fatigue life for the flat moisture profile specimens at the same average moisture content was comparatively smaller, being about a factor of 5 from the value in dry specimens. X-ray radiographic analysis of damage accumulation in compression-compression fatigue revealed interlaminar cracking to be the dominant mode of failure responsible for the observed enhanced cyclic degradation of moisture-conditioned specimens. This finding was corroborated by the observed systematic reduction in interlaminar shear strength as a function of moisture content, which, in turn, increased the propensity for delamination under cyclic compressive loads. Residual strength measurements on cycled specimens indicated significant strength reductions at long lives, particularly in moisture conditioned specimens.

To Be Connected or Not To Be Connected? Mobile Messenger Overload, Fatigue, and Mobile Shunning.

PubMed

Shin, Jaewook; Shin, Mincheol

2016-10-01

With the increased adoption of mobile devices, mobile communication is all around us and we are connected anywhere, anytime. Mobile communication in general and mobile messenger service in particular make interpersonal communication in Korea so frequent and convenient. However, being connected too much anywhere and anytime via mobile messenger service appears to lead an increasing number of people to feel fatigue and to decrease mobile communication under some conditions. Based on a sample of 334 respondents, this study empirically investigated the relationships among commercial, noncommercial mobile messenger overload, mobile messenger fatigue, relational self-concept, and mobile shunning behavior. The findings show that (a) the effect of noncommercial mobile messenger overload is stronger than that of commercial mobile messenger overload in increasing mobile messenger fatigue although both positively affect mobile messenger fatigue, (b) relational self-concept has moderating effects on the relationship between mobile messenger overload and mobile messenger fatigue, and that (c) mobile messenger fatigue triggers mobile communicators' shunning behavior through which the communicators increase their intention to avoid mobile communication, to change their mobile phone numbers, and to subscribe to dual number service on one mobile device. When confronted with mobile messenger fatigue caused by mobile messenger overload, mobile messaging service users are likely to shun their mobile communication. Being constantly and conveniently connected appears to be a blessing in disguise.

Evaluation of Fatigue Behavior and Surface Characteristics of Aluminum Alloy 2024 T6 After Electric Discharge Machining

NASA Astrophysics Data System (ADS)

Mehmood, Shahid; Shah, Masood; Pasha, Riffat Asim; Sultan, Amir

2017-10-01

The effect of electric discharge machining (EDM) on surface quality and consequently on the fatigue performance of Al 2024 T6 is investigated. Five levels of discharge current are analyzed, while all other electrical and nonelectrical parameters are kept constant. At each discharge current level, dog-bone specimens are machined by generating a peripheral notch at the center. The fatigue tests are performed on four-point rotating bending machine at room temperature. For comparison purposes, fatigue tests are also performed on the conventionally machined specimens. Linearized SN curves for 95% failure probability and with four different confidence levels (75, 90, 95 and 99%) are plotted for each discharge current level as well as for conventionally machined specimens. These plots show that the electric discharge machined (EDMed) specimens give inferior fatigue behavior as compared to conventionally machined specimen. Moreover, discharge current inversely affects the fatigue life, and this influence is highly pronounced at lower stresses. The EDMed surfaces are characterized by surface properties that could be responsible for change in fatigue life such as surface morphology, surface roughness, white layer thickness, microhardness and residual stresses. It is found that all these surface properties are affected by changing discharge current level. However, change in fatigue life by discharge current could not be associated independently to any single surface property.

Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 High Strength Aluminum Alloy

DTIC Science & Technology

2013-06-01

Corrosion Fatigue Corrosion fatigue is defined as the failure of metal due to a cyclical load in combination with exposure to a caustic environment...lifetime is spent creating the crack while the actual crack growth makes up a smaller portion of the total lifetime. With corrosion fatigue however

Crack Initiation and Growth Behavior at Corrosion Pit in 2024-T3 Aluminum Alloy

DTIC Science & Technology

2014-09-01

63 Figure B.1: The crack length vs. number of cycles during fatigue testing for the 2AI-01 specimen...number of cycles during fatigue testing for the the 2AI- 02 specimen...64 Figure B.3: The crack length vs. number of cycles during fatigue testing for the 2Sl-01 specimen

Fatigue Behavior of a Box-Type Welded Structure of Hydraulic Support Used in Coal Mine

PubMed Central

Zhao, Xiaohui; Li, Fuyong; Liu, Yu; Fan, Yanjun

2015-01-01

Hydraulic support is the main supporting equipment of the coal mining systems, and they are usually subjected to fatigue failure under the high dynamic load. The fracture positions are generally at welded joints where there is a serious stress concentration. In order to investigate and further improve the fatigue strength of hydraulic support, the present work first located the possible position where fatigue failure occurs through finite element analysis, and then fatigue tests were carried out on the different forms of welded joints for the dangerous parts. Finally, Fatigue strength-life (S-N) curves and fracture mechanism were studied. This research will provide a theoretical reference for the fatigue design of welded structures for hydraulic support. PMID:28793586

The effect of microstructure on the tensile and fatigue behavior of Ti-22Al-23Nb in air and vacuum

NASA Astrophysics Data System (ADS)

Luetjering, Stephanie

Titanium aluminide alloys containing the ordered orthorhombic (O) phase, based on Ti2AlNb, exhibit high specific strengths at elevated temperature along with good room temperature tensile ductility and fracture toughness values. They are thus considered as potential materials for aerospace applications both in their monolithic form and as matrices in metal matrix composites. Microstructure/property relationships have been studied to a great extend with regard to tensile and creep properties. However, only little is known in the key areas of fatigue crack initiation, fatigue crack propagation and fatigue life. The main objective of this work therefore is to get a comprehensive understanding of the effects of microstructural parameters (such as volume fraction of the individual phases, their size and distribution) on the cyclic properties of O-based titanium aluminides. Furthermore, the performance of these alloys in aggressive environments, a critical issue for this alloy class, is being addressed. Tensile, isothermal fatigue, and fatigue crack growth (FCG) tests were conducted at 20°C and 540°C both in lab air and vacuum (pressure ≤ 1 x 10-6 torr) on three microstructural conditions of a representative O-based titanium alloy, Ti-22Al-23Nb. Results indicate a strong effect of microstructure on tensile and FCG properties, whereas only a slight influence of microstructure on the fatigue life is evident. The O phase contributes mainly to the material's yield stress. The tensile elongation is predominantly influenced by the beta phase volume fraction. The observed effect of microstructure on the FCG behavior is attributed to crack closure, crack front geometry and crystallographic texture. Environmental effects on the fatigue life are pronounced at elevated temperature and high applied stress amplitudes only. These conditions lead to premature crack initiation at the specimen's surface for testing in air, whereas testing in vacuum results in subsurface crack nucleation and an extended fatigue life of about two orders of magnitude. The FCG behavior is influenced by the environment at both 20°C and 540°C, proposing fatigue crack growth mechanisms enhanced by hydrogen embrittlement.

S-N Fatigue and Fatigue Crack Propagation Behaviors of X80 Steel at Room and Low Temperatures

NASA Astrophysics Data System (ADS)

Jung, Dae-Ho; Kwon, Jae-Ki; Woo, Nam-Sub; Kim, Young-Ju; Goto, Masahiro; Kim, Sangshik

2014-02-01

In the present study, the S-N fatigue and the fatigue crack propagation (FCP) behaviors of American Petroleum Institute X80 steel were examined in the different locations of the base metal (BM), weld metal (WM), and heat-affected zone (HAZ) at 298 K, 223 K, and 193 K (25 °C, -50 °C, and -80 °C). The resistance to S-N fatigue of X80 BM specimen increased greatly with decreasing temperature from 298 K to 193 K (25 °C to -80 °C) and showed a strong dependency on the flow strength (½(yield strength + tensile strength)). The FCP rates of X80 BM specimen were substantially reduced with decreasing temperature from 298 K to 223 K (25 °C to -50 °C) over the entire ∆ K regime, while further reduction in FCP rates was not significant with temperature from 223 K to 193 K (-50 °C to -80 °C). The FCP rates of the X80 BM and the WM specimens were comparable with each other, while the HAZ specimen showed slightly better FCP resistance than the BM and the WM specimens over the entire ∆K regime at 298 K (25 °C). Despite the varying microstructural characteristics of each weld location, the residual stress appeared to be a controlling factor to determine the FCP behavior. The FCP behaviors of high strength X80 steel were discussed based on the microstructural and the fractographic observations.

Tensile and high cycle fatigue behaviors of high-Mn steels at 298 and 110 K

DOE Office of Scientific and Technical Information (OSTI.GOV)

Seo, Wongyu; Jeong, Daeho; Sung, Hyokyung

Tensile and high cycle fatigue behaviors of high-Mn austenitic steels, including 25Mn, 25Mn0.2Al, 25Mn0.5Cu, 24Mn4Cr, 22Mn3Cr and 16Mn2Al specimens, were investigated at 298 and 110 K. Depending on the alloying elements, tensile ductility of high-Mn steels either increased or decreased with decreasing temperature from 298 to 110 K. Reasonable correlation between the tendency for martensitic tranformation, the critical twinning stress and the percent change in tensile elongation suggested that tensile deformation of high-Mn steels was strongly influenced by SFE determining TRIP and TWIP effects. Tensile strength was the most important parameter in determining the resistance to high cycle fatigue ofmore » high-Mn steels with an exceptional work hardening capability at room and cryogenic temperatures. The fatigue crack nucleation mechanism in high-Mn steels did not vary with decreasing tempertature, except Cr-added specimens with grain boundary cracking at 298 K and slip band cracking at 110 K. The EBSD (electron backscatter diffraction) analyses suggested that the deformation mechanism under fatigue loading was significantly different from tensile deformation which could be affected by TRIP and TWIP effects. - Highlights: •The resistances to HCF of various high-Mn steels were measured. •The variables affecting tensile and HCF behaviors of high-Mn steels were assessed. •The relationship between tensile and the HCF behaviors of high-Mn steels was established.« less

Fatigue-Induced Damage in Zr-Based Bulk Metallic Glasses

PubMed Central

Chuang, Chih-Pin; Yuan, Tao; Dmowski, Wojciech; Wang, Gong-Yao; Freels, Matt; Liaw, Peter K.; Li, Ran; Zhang, Tao

2013-01-01

In the present work, we investigate the effect of “fatigue” on the fatigue behavior and atomic structure of Zr-based BMGs. Fatigue experiments on the failed-by-fatigue samples indicate that the remnants generally have similar or longer fatigue life than the as-cast samples. Meanwhile, the pair-distribution-function (PDF) analysis of the as-cast and post-fatigue samples showed very small changes of local atomic structures. These observations suggest that the fatigue life of the 6-mm in-diameter Zr-based BMG is dominated by the number of pre-existing crack-initiation sites in the sample. Once the crack initiates in the specimen, the fatigue-induced damage is accumulated locally on these initiated sites, while the rest of the region deforms elastically. The results suggest that the fatigue failure of BMGs under compression-compression fatigue experiments is a defect-controlled process. The present work indicates the significance of the improved fatigue resistance with decreasing the sample size. PMID:23999496

Effectiveness of Long-term Doxycycline Treatment and Cognitive-Behavioral Therapy on Fatigue Severity in Patients with Q Fever Fatigue Syndrome (Qure Study): A Randomized Controlled Trial.

PubMed

Keijmel, Stephan P; Delsing, Corine E; Bleijenberg, Gijs; van der Meer, Jos W M; Donders, Rogier T; Leclercq, Monique; Kampschreur, Linda M; van den Berg, Michel; Sprong, Tom; Nabuurs-Franssen, Marrigje H; Knoop, Hans; Bleeker-Rovers, Chantal P

2017-04-15

Approximately 20% of patients with acute Q fever will develop chronic fatigue, referred to as Q fever fatigue syndrome (QFS). The objective of this randomized controlled clinical trial was to assess the efficacy of either long-term treatment with doxycycline or cognitive-behavioral therapy (CBT) in reducing fatigue severity in patients with QFS. Adult patients were included who met the QFS criteria according to the Dutch guideline: a new onset of severe fatigue lasting ≥6 months with significant disabilities, related to an acute Q fever infection, without other somatic or psychiatric comorbidity explaining the fatigue. Using block randomization, patients were randomized between oral study medication and CBT (2:1) for 24 weeks. Second, a double-blind randomization between doxycycline (200 mg/day, once daily) and placebo was performed in the medication group. Primary outcome was fatigue severity at end of treatment (EOT; week 26), assessed with the Checklist Individual Strength subscale Fatigue Severity. Of 155 patients randomized, 154 were included in the intention-to-treat analysis (doxycycline, 52; placebo, 52; CBT, 50). At EOT, fatigue severity was similar between doxycycline (40.8 [95% confidence interval {CI}, 37.3-44.3]) and placebo (37.8 [95% CI, 34.3-41.2]; difference, doxycycline vs placebo, -3.0 [97.5% CI, -8.7 to 2.6]; P = .45). Fatigue severity was significantly lower after CBT (31.6 [95% CI, 28.0-35.1]) than after placebo (difference, CBT vs placebo, 6.2 [97.5% CI, .5-11.9]; P = .03). CBT is effective in reducing fatigue severity in QFS patients. Long-term treatment with doxycycline does not reduce fatigue severity in QFS patients compared to placebo. NCT01318356. © The Author 2017. Published by Oxford University Press for the Infectious Diseases Society of America. All rights reserved. For permissions, e-mail: journals.permissions@oup.com

An investigation of the effects of interfacial microstructure on the fatigue behavior of a four-ply [75]{sub 4} continuous silicon carbide (SCS-6) fiber-reinforced titanium matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jin, O.; Li, Y.; Rabeeh, B.M.

1997-12-01

The effects of interfacial microstructure/thickness on the strength and fatigue behavior of a model four-ply [75]{sub 4} Ti-15V-3Al-3Cr-3Sn/SiC (SCS-6) composite are examined in this article. Interfacial microstructure was controlled by annealing at 815 C for 10, 50, or 100 hours. The reaction layer and coating thickness were observed to increase with increasing annealing duration. Damage initiation/propagation mechanisms were examined in as-received material and composites annealed at 815 C for 10 and 100 hours. Fatigue behavior was observed to be dependent upon the stress amplitude. At high stress amplitudes, the failure was dominated by overload phenomena. However, at all stress levels,more » fatigue crack initiation occurred by early debonding and matrix deformation by stress-induced precipitation. This was followed by matrix crack growth and fiber fracture prior to the onset of catastrophic failure. Matrix shear failure modes were also observed on the fracture surfaces in addition to fatigue striations in the matrix. Correlations were also established between the observed damage modes and acoustic emission signals that were detected under monotonic and cyclic loading conditions.« less

High Speed Research Program Sonic Fatigue

NASA Technical Reports Server (NTRS)

Rizzi, Stephen A. (Technical Monitor); Beier, Theodor H.; Heaton, Paul

2005-01-01

The objective of this sonic fatigue summary is to provide major findings and technical results of studies, initiated in 1994, to assess sonic fatigue behavior of structure that is being considered for the High Speed Civil Transport (HSCT). High Speed Research (HSR) program objectives in the area of sonic fatigue were to predict inlet, exhaust and boundary layer acoustic loads; measure high cycle fatigue data for materials developed during the HSR program; develop advanced sonic fatigue calculation methods to reduce required conservatism in airframe designs; develop damping techniques for sonic fatigue reduction where weight effective; develop wing and fuselage sonic fatigue design requirements; and perform sonic fatigue analyses on HSCT structural concepts to provide guidance to design teams. All goals were partially achieved, but none were completed due to the premature conclusion of the HSR program. A summary of major program findings and recommendations for continued effort are included in the report.

Fatigue of notched fiber composite laminates. Part 1: Analytical model

NASA Technical Reports Server (NTRS)

Mclaughlin, P. V., Jr.; Kulkarni, S. V.; Huang, S. N.; Rosen, B. W.

1975-01-01

A description is given of a semi-empirical, deterministic analysis for prediction and correlation of fatigue crack growth, residual strength, and fatigue lifetime for fiber composite laminates containing notches (holes). The failure model used for the analysis is based upon composite heterogeneous behavior and experimentally observed failure modes under both static and fatigue loading. The analysis is consistent with the wearout philosophy. Axial cracking and transverse cracking failure modes are treated together in the analysis. Cracking off-axis is handled by making a modification to the axial cracking analysis. The analysis predicts notched laminate failure from unidirectional material fatique properties using constant strain laminate analysis techniques. For multidirectional laminates, it is necessary to know lamina fatique behavior under axial normal stress, transverse normal stress and axial shear stress. Examples of the analysis method are given.

Fatigue behavior of a thermally-activated NiTiNb SMA-FRP patch

NASA Astrophysics Data System (ADS)

El-Tahan, M.; Dawood, M.

2016-01-01

This paper presents the details of an experimental study that was conducted to characterize the fatigue behavior of a thermally-activated shape memory alloy (SMA)/carbon fiber reinforced polymer (CFRP) patch that can be used to repair cracked steel members. A total of 14 thermally-activated patches were fabricated and tested to evaluate the stability of the prestress under fatigue loading. The parameters considered in this study are the prestress level in the nickel-titanium-niobium SMA wires and the applied force range. An empirical model to predict the degradation of the prestress is also presented. The results indicate that patches for which the maximum applied loads in a fatigue cycle did not cause debonding of the SMA wires from the CFRP sustained two million loading cycles with less than 20% degradation of the prestress.

Dynamic strain aging behavior of modified 9Cr-1Mo and reduced activation ferritic martensitic steels under low cycle fatigue

NASA Astrophysics Data System (ADS)

Mariappan, K.; Shankar, Vani; Sandhya, R.; Prasad Reddy, G. V.; Mathew, M. D.

2013-04-01

Influence of temperature and strain rate on low cycle fatigue (LCF) behavior of modified 9Cr-1Mo ferritic martensitic steel and 1.4W-0.06Ta reduced activation ferritic martensitic (RAFM) steel in normalized and tempered conditions was studied. Total strain controlled LCF tests between 300 and 873 K on modified 9Cr-1Mo steel and RAFM steel and at various strain rates on modified 9Cr-1Mo steel were performed at total strain amplitude of ±0.6%. Both the steels showed continuous cyclic softening at all temperatures. Whereas manifestations of dynamic strain aging (DSA) were observed in both the steels which decreased fatigue life at intermediate temperatures, at higher temperatures, oxidation played a crucial role in decreasing fatigue life.

NLRP3 inflammasome activation mediates fatigue-like behaviors in mice via neuroinflammation.

PubMed

Zhang, Ziteng; Ma, Xiujuan; Xia, Zhenna; Chen, Jikuai; Liu, Yangang; Chen, Yongchun; Zhu, Jiangbo; Li, Jinfeng; Yu, Huaiyu; Zong, Ying; Lu, Guocai

2017-09-01

Numerous experimental and clinical studies have suggested that the interaction between the immune system and the brain plays an important role in the pathophysiology of chronic fatigue syndrome (CFS). The NLRP3 inflammasome is an important part of the innate immune system. This complex regulates proinflammatory cytokine interleukin-1β (IL-1β) maturation, which triggers different kinds of immune-inflammatory reactions. We employed repeated forced swims to establish a model of CFS in mice. NLRP3 knockout (KO) mice were also used to explore NLRP3 inflammasome activation in the mechanisms of CFS, using the same treatment. After completing repeated swim tests, the mice displayed fatigue-like behaviors, including locomotor activity and reduced fall-off time on the rota-rod test, which was accompanied by significantly higher mature IL-1β level in the prefrontal cortex (PFC) and malondialdehyde (MDA) level in serum. We also found increased NLRP3 protein expression, NLRP3 inflammasome formation and increased mature IL-1β production in the PFC, relative to untreated mice. The NLRP3 KO mice displayed significantly moderated fatigue behaviors along with decreased PFC and serum IL-1β levels under the same treatment. These findings demonstrated the involvement of NLRP3 inflammasome activation in the mechanism of swimming-induced fatigue. Future therapies targeting the NLRP3/IL-1β pathway may have significant potential for fatigue prevention and treatment. Copyright © 2017. Published by Elsevier Ltd.

Effect of tensile mean stress on fatigue behavior of single-crystal and directionally solidified superalloys

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Mcgaw, Michael A.

1990-01-01

Two nickel base superalloys, single crystal PWA 1480 and directionally solidified MAR-M 246 + Hf, were studied in view of the potential usage of the former and usage of the latter as blade materials for the turbomachinery of the space shuttle main engine. The baseline zero mean stress (ZMS) fatigue life (FL) behavior of these superalloys was established, and then the effect of tensile mean stress (TMS) on their FL behavior was characterized. At room temperature these superalloys have lower ductilities and higher strengths than most polycrystalline engineering alloys. The cycle stress-strain response was thus nominally elastic in most of the fatigue tests. Therefore, a stress range based FL prediction approach was used to characterize both the ZMS and TMS fatigue data. In the past, several researchers have developed methods to account for the detrimental effect of tensile mean stress on the FL for polycrystalline engineering alloys. However, the applicability of these methods to single crystal and directionally solidified superalloys has not been established. In this study, these methods were applied to characterize the TMS fatigue data of single crystal PWA 1480 and directionally solidified MAR-M 246 + Hf and were found to be unsatisfactory. Therefore, a method of accounting for the TMS effect on FL, that is based on a technique proposed by Heidmann and Manson was developed to characterize the TMS fatigue data of these superalloys. Details of this method and its relationship to the conventionally used mean stress methods in FL prediction are discussed.

Fatigue Behavior of Ultrafine-Grained 5052 Al Alloy Processed Through Different Rolling Methods

NASA Astrophysics Data System (ADS)

Yogesha, K. K.; Joshi, Amit; Jayaganthan, R.

2017-05-01

In the present study, 5052 Al alloy was processed through different rolling methods to obtain ultrafine grains and its high-cycle fatigue behavior were investigated. The solution-treated Al-Mg alloys (AA 5052) were deformed through different methods such as cryorolling (CR), cryo groove rolling (CGR) and cryo groove rolling followed by warm rolling (CGW), up to 75% thickness reduction. The deformed samples were subjected to mechanical testing such as hardness, tensile and high-cycle fatigue (HCF) test at stress control mode. The CGW samples exhibit better HCF strength when compared to other conditions. The microstructure of the tested samples was characterized by optical microscopy, SEM fractography and TEM to understand the deformation behavior of deformed Al alloy. The improvement in fatigue life of CR and CGR samples is due to effective grain refinement, subgrain formations, and high dislocation density observed in the heavily deformed samples at cryogenic condition as observed from SEM and TEM analysis. However, in case of CGW samples, formation of nanoshear bands accommodates the applied strain during cyclic loading, thereby facilitating dislocation accumulation along with subgrain formations, leading to the high fatigue life. The deformed or broken impurity phase particles found in the deformed samples along with the precipitates that were formed during warm rolling also play a prominent role in enhancing the fatigue strength. These tiny particles hindered the dislocation movement by effectively pinning it at grain boundaries, thereby improving the resistance of crack propagation under cyclic load.

Effect of interlaminar normal stresses on the uniaxial zero-to-tension fatigue behavior of graphite/epoxy tubes

NASA Technical Reports Server (NTRS)

Krempl, Erhard; An, Deukman

1991-01-01

Fatigue tests conducted with and without internal pressure have been found to possess approximately the same fatigue life as (+/-45)s graphite/epoxy tubes for zero-to-tension axial load-controlled conditions on an axial torsion servohydraulic apparatus. These tests therefore cannot be considered as confirmations of the suspected detrimental effect of interlaminar tensile stresses on the fatigue performance of thin-walled tubes. The addition of 90-deg plies on both the inside and the outside is found to significantly improve the tubes' static and fatigue strengths.

The effect of porosity and gamma-gamma' eutectic content on the low cycle fatigue behavior of hydrogen-charged PWA-1480

NASA Technical Reports Server (NTRS)

Gayda, John; Dreshfield, Robert L.; Gabb, Timothy P.

1991-01-01

Single crystal superalloys such as PWA 1480 are considered for turbopump blades in the main engines of the space shuttle. As fatigue resistance in a hydrogen environment is a key issue in this application, a study of the effect of porosity and gamma-gamma' eutectic content on the fatigue life of a hydrogen-charged PWA 1480 was performed. Porosity and eutectic were linked to fatigue initiation, and therefore reduction of either of both may be one means to improve fatigue life of PWA 1480 when hydrogen is present.

Atmospheric Turbulence Statistics from GOLD Experiments

NASA Technical Reports Server (NTRS)

Jeganathan, Muthu; Wilson, Keith; Lesh, Jim

1996-01-01

Ground-Orbiter Lasercomm Demonstration (GOLD) includes the following: (1) Optical communication experiments between Table Mountain Observatory (TMF) and Japanese Engineering Test Satellite (ETS-VI); (2) International cooperative effort between NASA, NASDA, CRL and JPL; and (3) Phase 1 transmissions from October 1995 to January 1996 and Phase 2 transmissions from March 1996 to May 1996.

Production of enzymes by a newly isolated Bacillus sp. TMF-1 in solid state fermentation on agricultural by-products: The evaluation of substrate pretreatment methods.

PubMed

Salim, Abdalla Ali; Grbavčić, Sanja; Šekuljica, Nataša; Stefanović, Andrea; Jakovetić Tanasković, Sonja; Luković, Nevena; Knežević-Jugović, Zorica

2017-03-01

Study on potential of different agro-industrial waste residues for supporting the growth of newly isolated Bacillus sp. TMF-1 strain under solid-state fermentation (SSF) was conducted aiming to produce several industrially valuable enzymes. Since the feasibility of the initial study was confirmed, further objectives included evaluation of several pretreatments of the studied agricultural by-products (soybean meal, sunflower meal, maize bran, maize pericarp, olive oil cake and wheat bran) on the microbial productivity as means of enhancing the yields of produced proteases, α-amylases, cellulases and pectinases. Among acid/alkaline treatment, ultrasound and microwave assisted methods, chemical treatments superiorly affected most of the studied substrates. Highest yields of produced proteases (50.5IUg -1 ) and α-amylases (50.75IUg -1 ) were achieved on alkaline treated corn pericarp. Alkaline treatment also promoted the secretion of cellulases on maize bran (1.19IUg -1 ). Highest yield of pectinases was obtained on untreated soybean meal (64.90IUg -1 ). Copyright © 2016 Elsevier Ltd. All rights reserved.

Progress in Design and Construction of the Optical Communications Laser Laboratory

NASA Technical Reports Server (NTRS)

Wilson, K. E.; Britcliffe, M.; Golshan, N.

1999-01-01

The deployment of advanced hyperspectral imaging and other Earth sensing instruments on board Earth observing satellites is driving the demand for high-data-rate communications. Optical communications meet the required data rates with small, low mass, and low-power communications packages. JPL, as NASA's lead center in optical communications, plans to construct a 1-m Optical Communications Telescope Laboratory (OCTL) at its Table Mountain Facility (TMF) complex in the San Gabriel Mountains of Southern California. The design of the building has been completed, and the construction contractor has been selected. Ground breaking is expected to start at the beginning of the 1999 TMF construction season. A request for proposal (RFP) has been issued for the procurement of the telescope system. Prior to letting the RFP we conducted a request for information with industry for the telescope system. Several vendors responded favorably and provided information on key elements of the proposed design. These inputs were considered in developing the final requirements in the RFP. Keywords: Free space optical communications, lasercom, telescopes, ground stations, adaptive optics, astrometry, Table Mountain Facility

The merging of fatigue and fracture mechanics concepts: a historical perspective

NASA Astrophysics Data System (ADS)

Newman, J. C.

1998-07-01

In this review, some of the technical developments that have occurred during the past 40 years are presented which have led to the merger of fatigue and fracture mechanics concepts. This review is made from the viewpoint of “crack propagation”. As methods to observe the “fatigue” process have improved, the formation of fatigue micro-cracks have been observed earlier in life and the measured crack sizes have become smaller. These observations suggest that fatigue damage can now be characterized by “crack size”. In parallel, the crack-growth analysis methods, using stress-intensity factors, have also improved. But the effects of material inhomogeneities, crack-fracture mechanisms, and nonlinear behavior must now be included in these analyses. The discovery of crack-closure mechanisms, such as plasticity, roughness, and oxide/corrosion/fretting product debris, and the use of the effective stress-intensity factor range, has provided an engineering tool to predict small- and large-crack-growth rate behavior under service loading conditions. These mechanisms have also provided a rationale for developing new, damage-tolerant materials. This review suggests that small-crack growth behavior should be viewed as typical behavior, whereas large-crack threshold behavior should be viewed as the anomaly. Small-crack theory has unified “fatigue” and “fracture mechanics” concepts; and has bridged the gap between safe-life and durability/damage-tolerance design concepts.

Ascending caudal medullary catecholamine pathways drive sickness-induced deficits in exploratory behavior: brain substrates for fatigue?

PubMed

Gaykema, Ronald P A; Goehler, Lisa E

2011-03-01

Immune challenges can lead to marked behavioral changes, including fatigue, reduced social interest, anorexia, and somnolence, but the precise neuronal mechanisms that underlie sickness behavior remain elusive. Part of the neurocircuitry influencing behavior associated with illness likely includes viscerosensory nuclei located in the caudal brainstem, based on findings that inactivation of the dorsal vagal complex (DVC) can prevent social withdrawal. These brainstem nuclei contribute multiple neuronal projections that target different components of autonomic and stress-related neurocircuitry. In particular, catecholaminergic neurons in the ventrolateral medulla (VLM) and DVC target the hypothalamus and drive neuroendocrine responses to immune challenge, but their particular role in sickness behavior is not known. To test whether this catecholamine pathway also mediates sickness behavior, we compared effects of DVC inactivation with targeted lesion of the catecholamine pathway on exploratory behavior, which provides an index of motivation and fatigue, and associated patterns of brain activation assessed by immunohistochemical detection of c-Fos protein. LPS treatment dramatically reduced exploratory behavior, and produced a pattern of increased c-Fos expression in brain regions associated with stress and autonomic adjustments paraventricular hypothalamus (PVN), bed nucleus of the stria terminalis (BST), central amygdala (CEA), whereas activation was reduced in regions involved in exploratory behavior (hippocampus, dorsal striatum, ventral tuberomammillary nucleus, and ventral tegmental area). Both DVC inactivation and catecholamine lesion prevented reductions in exploratory behavior and completely blocked the inhibitory LPS effects on c-Fos expression in the behavior-associated regions. In contrast, LPS-induced activation in the CEA and BST was inhibited by DVC inactivation but not by catecholamine lesion. The findings support the idea that parallel pathways from immune-sensory caudal brainstem sources target distinct populations of forebrain neurons that likely mediate different aspects of sickness. The caudal medullary catecholaminergic projections to the hypothalamus may significantly contribute to brain mechanisms that induce behavioral "fatigue" in the context of physiological stressors. Copyright © 2010 Elsevier Inc. All rights reserved.

Comparative muscle study fatigue with sEMG signals during the isotonic and isometric tasks for diagnostics purposes.

PubMed

Sarmiento, Jhon F; Benevides, Alessandro B; Moreira, Marcelo H; Elias, Arlindo; Bastos, Teodiano F; Silva, Ian V; Pelegrina, Claudinei C

2011-01-01

The study of fatigue is an important tool for diagnostics of disease, sports, ergonomics and robotics areas. This work deals with the analysis of sEMG most important fatigue muscle indicators with use of signal processing in isometric and isotonic tasks with the propose of standardizing fatigue protocol to select the data acquisition and processing with diagnostic proposes. As a result, the slope of the RMS, ARV and MNF indicators were successful to describe the fatigue behavior expected. Whereas that, MDF and AIF indicators failed in the description of fatigue. Similarly, the use of a constant load for sEMG data acquisition was the best strategy in both tasks.

Procedures for characterizing an alloy and predicting cyclic life with the total strain version of Strainrange Partitioning

NASA Technical Reports Server (NTRS)

Saltsman, James F.; Halford, Gary R.

1989-01-01

Procedures are presented for characterizing an alloy and predicting cyclic life for isothermal and thermomechanical fatigue conditions by using the total strain version of strainrange partitioning (TS-SRP). Numerical examples are given. Two independent alloy characteristics are deemed important: failure behavior, as reflected by the inelastic strainrange versus cyclic life relations; and flow behavior, as indicated by the cyclic stress-strain-time response (i.e., the constitutive behavior). Failure behavior is characterized by conducting creep-fatigue tests in the strain regime, wherein the testing times are reasonably short and the inelastic strains are large enough to be determined accurately. At large strainranges, stress-hold, strain-limited tests are preferred because a high rate of creep damage per cycle is inherent in this type of test. At small strainranges, strain-hold cycles are more appropriate. Flow behavior is characterized by conducting tests wherein the specimen is usually cycled far short of failure and the wave shape is appropriate for the duty cycle of interest. In characterizing an alloy pure fatigue, or PP, failure tests are conducted first. Then depending on the needs of the analyst a series of creep-fatigue tests are conducted. As many of the three generic SRP cycles are featured as are required to characterize the influence of creep on fatigue life (i.e., CP, PC, and CC cycles, respectively, for tensile creep only, compressive creep only, and both tensile and compressive creep). Any mean stress effects on life also must be determined and accounted for when determining the SRP inelastic strainrange versus life relations for cycles featuring creep. This is particularly true for small strainranges. The life relations thus are established for a theoretical zero mean stress condition.

Fatigue failure of hydrogen embrittled high strength steels

NASA Technical Reports Server (NTRS)

Kim, Y. G.; Aleszka, J.

1975-01-01

Results of an experimental investigation are presented concerning the fracture behavior of cathodically charged, quenched and tempered martensitic steels under cyclic load conditions. Introduction of H2 by cathodic charging reduced fatigue life by as much as 60%. It is proposed that subsurface transverse fatigue cracks nucleate simultaneously at multiple sites, such as at microcracks, voids, or inclusions. Fatigue crack growth then occurs on planes perpendicular to the major applied stress axis in the presence of the critical combination of applied external stress and hydrogen.

Effect of Fatigue-Stressing Short of Failure on Some Typical Aircraft Metals

DTIC Science & Technology

1945-10-01

of the fractures .. .,. . ....:,:..;.-.,: ,: TTqm c,on~~~’~rktion of such resultb it seemed worth while ~“~arn+ning the effects of repeated strese:on...fatigue-stz’~$sed short 015:: fracture . ; Tli~ impact behavior of normalized SAE X 4130 staal was studied[’YoTlotiing” fatigue-stressing .under”a...conduc&ed in the conventional manner on a group of notched specimens t-o determine the S-N curve and the fatigue limit (tests to fracture ). Four

Effects of crack tip plastic zone on corrosion fatigue cracking of alloy 690(TT) in pressurized water reactor environments

NASA Astrophysics Data System (ADS)

Xiao, J.; Qiu, S. Y.; Chen, Y.; Fu, Z. H.; Lin, Z. X.; Xu, Q.

2015-01-01

Alloy 690(TT) is widely used for steam generator tubes in pressurized water reactor (PWR), where it is susceptible to corrosion fatigue. In this study, the corrosion fatigue behavior of Alloy 690(TT) in simulated PWR environments was investigated. The microstructure of the plastic zone near the crack tip was investigated and labyrinth structures were observed. The relationship between the crack tip plastic zone and fatigue crack growth rates and the environment factor Fen was illuminated.

Proceedings of the Annual Mechanics of Composites Review (8th) Held at Wright-Patterson AFB, Ohio on 5-7 October 1982.

DTIC Science & Technology

1983-04-01

Spectrum Fatigue Behavior of Postbuckled Shear Panels; PO01 246 Development of Analysis for Predicting Compression Fatigt Life and Residual Strength in...Lazyup and Frequency Effects on Fatigue Life of Composites, POOl 256 Effect of Stress Ratio on Fatigue Life of Composites,’ POOl 257 High-Load Transfer...L. Agerwall, Northrop Corporation 0950-1020 BREAK 1020-1100 DEVELOPMENT OF ANALYSIS FOR PREDICTING COMPRESSION 34 FATIGUE LIFE AND RESIDUAL STRENGTH

On the Use of Equivalent Linearization for High-Cycle Fatigue Analysis of Geometrically Nonlinear Structures

NASA Technical Reports Server (NTRS)

Rizzi, Stephen A.

2003-01-01

The use of stress predictions from equivalent linearization analyses in the computation of high-cycle fatigue life is examined. Stresses so obtained differ in behavior from the fully nonlinear analysis in both spectral shape and amplitude. Consequently, fatigue life predictions made using this data will be affected. Comparisons of fatigue life predictions based upon the stress response obtained from equivalent linear and numerical simulation analyses are made to determine the range over which the equivalent linear analysis is applicable.

Effectiveness of cognitive behavioral therapy for the treatment of fatigue in patients with multiple sclerosis: A systematic review and meta-analysis.

PubMed

van den Akker, Lizanne Eva; Beckerman, Heleen; Collette, Emma Hubertine; Eijssen, Isaline Catharine Josephine Maria; Dekker, Joost; de Groot, Vincent

2016-11-01

Fatigue is a frequently occurring symptom of multiple sclerosis (MS) that limits social participation. To systematically determine the short and long-term effects of cognitive behavioral therapy (CBT) for the treatment of MS-related fatigue. Pubmed, Cochrane, EMBASE, Psychology and Behavioral Sciences Collection, ERIC, PsychINFO, Cinahl, PsycARTICLES, and relevant trial registers were searched up to February 2016. In addition, references from retrieved articles were examined. Studies were included if participants had MS, fatigue was a primary outcome measure, the intervention was CBT, and the design was a randomized controlled trial. The search was performed by two independent reviewers, three CBT experts determined whether interventions were CBT. Data on patient and study characteristics and fatigue were systematically extracted using a standardized data extraction form. Two independent reviewers assessed risk of bias using the Cochrane Collaboration risk of bias tool. In the event of disagreement, a third reviewer was consulted. Of the 994 identified studies, 4 studies were included in the meta-analysis, comprising 193 CBT-treated patients and 210 patients who underwent a control treatment. Meta-analyses of these studies showed that CBT treatment had a positive short-term effect on fatigue (standardized mean difference [SMD]=-0.47; 95% confidence interval [CI]=-0.88; -0.06; I 2 =73%). In addition, three studies showed a long-term positive effect of CBT (SMD=-0.30; CI -0.51; -0.08; I 2 =0%). This review found that the use of CBT for the treatment of fatigue in patients with MS has a moderately positive short-term effect. However, this effect decreases with cessation of treatment. Copyright © 2016 Elsevier Inc. All rights reserved.

Molecular Signatures of Peripheral Blood Mononuclear Cells during Chronic Interferon-alpha Treatment: Relationship with Depression and Fatigue

PubMed Central

Felger, Jennifer C.; Cole, Steve W.; Pace, Thaddeus W. W.; Hu, Fang; Woolwine, Bobbi J.; Doho, Gregory H.; Raison, Charles L.; Miller, Andrew H.

2012-01-01

Background Interferon (IFN)-alpha treatment for infectious disease and cancer causes high rates of depression and fatigue, and has been used to investigate the impact of inflammatory cytokines on brain and behavior. However, little is known about the transcriptional impact of chronic IFN-alpha on immune cells in vivo and its relationship to IFN-alpha-induced behavioral changes. Methods Genome-wide transcriptional profiling was performed on peripheral blood mononuclear cells from 21 patients with chronic hepatitis C either awaiting IFN-alpha therapy (n=10) or at 12 weeks of IFN-alpha treatment (n=11). Results Significance analysis of microarray data identified 252 up-regulated and 116 down-regulated gene transcripts. Of up-regulated genes, 2'-5'-oligoadenylate synthetase 2 (OAS2), a gene linked to chronic fatigue syndrome (CFS), was the only gene that was differentially expressed in patients with IFN-alpha-induced depression/fatigue, and correlated with depression and fatigue scores at 12 weeks (r=0.80, p=0.003 and r=0.70, p=0.017, respectively). Promoter-based bioinformatic analyses linked IFN-alpha-related transcriptional alterations to transcription factors involved in myeloid differentiation, IFN-alpha signaling, AP1 and CREB/ATF pathways, which were derived primarily from monocytes and plasmacytoid dendritic cells. IFN-alpha-treated patients with high depression/fatigue scores demonstrated up-regulation of genes bearing promoter motifs for transcription factors involved in myeloid differentiation, IFN-alpha and AP1 signaling, and reduced prevalence of motifs for CREB/ATF, which has been implicated in major depression. Conclusions Depression and fatigue during chronic IFN-alpha administration were associated with alterations in the expression (OAS2) and transcriptional control (CREB/ATF) of genes linked to behavioral disorders including CFS and major depression, further supporting an immune contribution to these diseases. PMID:22152193

Characterization of fatigue crack growth behavior in LENS fabricated Ti-6Al-4V using high-energy synchrotron x-ray microtomography

DOE PAGES

Sandgren, Hayley R.; Zhai, Yuwei; Lados, Diana A.; ...

2016-09-28

Laser Engineered Net Shaping (LENS) is an additive manufacturing technique that belongs to the ASTM standardized directed energy deposition category. To date, very limited work has been conducted towards understanding the fatigue crack growth behavior of LENS fabricated materials, which hinders the widespread adoption of this technology for high-integrity structural applications. In this study, the propagation of a 20 μm initial crack in LENS fabricated Ti-6Al-4V was captured in-situ, using high-energy synchrotron x-ray microtomography. Fatigue crack growth (FCG) data were then determined from 2D and 3D tomography reconstructions, as well as from fracture surface striation measurements using SEM. The generatedmore » data were compared to those obtained from conventional FCG tests that used compliance and direct current potential drop (DCPD) techniques to measure long and small crack growth. In conclusion, the observed agreement demonstrates that x-ray microtomography and fractographic analysis using SEM can be successfully combined to study the propagation behavior of fatigue cracks.« less

Characterization of fatigue crack growth behavior in LENS fabricated Ti-6Al-4V using high-energy synchrotron x-ray microtomography

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sandgren, Hayley R.; Zhai, Yuwei; Lados, Diana A.

Laser Engineered Net Shaping (LENS) is an additive manufacturing technique that belongs to the ASTM standardized directed energy deposition category. To date, very limited work has been conducted towards understanding the fatigue crack growth behavior of LENS fabricated materials, which hinders the widespread adoption of this technology for high-integrity structural applications. In this study, the propagation of a 20 μm initial crack in LENS fabricated Ti-6Al-4V was captured in-situ, using high-energy synchrotron x-ray microtomography. Fatigue crack growth (FCG) data were then determined from 2D and 3D tomography reconstructions, as well as from fracture surface striation measurements using SEM. The generatedmore » data were compared to those obtained from conventional FCG tests that used compliance and direct current potential drop (DCPD) techniques to measure long and small crack growth. In conclusion, the observed agreement demonstrates that x-ray microtomography and fractographic analysis using SEM can be successfully combined to study the propagation behavior of fatigue cracks.« less

High Cycle Fatigue (HCF) Science and Technology Program 2000 Annual Report

DTIC Science & Technology

2000-01-01

in an area of deep compressive stress. • Results of industry and government testing have indicated the ability to stop crack initiation and...fatigue crack nucleation process with the cyclic deformation behavior of the alloy for different microstructures and crystallographic texture ... texture combinations investigated, bimodal fine uni-rolled and lamellar cross-rolled displayed superior fatigue properties to the remaining four

An Experimental Evaluation of the Effect of Hole Fabrication/Treatment Techniques on Residual Strength and Fatigue Life of Polycarbonate Specimens with Holes

DTIC Science & Technology

1993-08-01

34The Effect of Dimpling on the Fatigue Strength of Loaded Holes in a Corrosive Environment," Experimental Techniques, Vol. 9, September 1985, 33-36. 34...Expansion on the Fatigue Behavior of 7079-T652 Alluminium [sic] Alloy," NLR TR 74016 U, National Aerospace Laboratory (NLR), Amsterdam, The

Acoustic fatigue life prediction for nonlinear structures with multiple resonant modes

NASA Technical Reports Server (NTRS)

Miles, R. N.

1992-01-01

This report documents an effort to develop practical and accurate methods for estimating the fatigue lives of complex aerospace structures subjected to intense random excitations. The emphasis of the current program is to construct analytical schemes for performing fatigue life estimates for structures that exhibit nonlinear vibration behavior and that have numerous resonant modes contributing to the response.

Bending fatigue tests on SiC-Al tapes under alternating stress at room temperature

NASA Technical Reports Server (NTRS)

Herzog, J. A.

1981-01-01

The development of a testing method for fatigue tests on SiC-Al tapes containing a small amount of SiC filaments under alternating stress is reported. The fatigue strength curves resulting for this composite are discussed. They permit an estimate of its behavior under continuous stress and in combination with various other matrices, especially metal matrices.

Fatigue Behavior of Porous Ti-6Al-4V Made by Laser-Engineered Net Shaping.

PubMed

Razavi, Seyed Mohammad Javad; Bordonaro, Giancarlo G; Ferro, Paolo; Torgersen, Jan; Berto, Filippo

2018-02-12

The fatigue behavior and fracture mechanisms of additively manufactured Ti-6Al-4V specimens are investigated in this study. Three sets of testing samples were fabricated for the assessment of fatigue life. The first batch of samples was built by using Laser-Engineered Net Shaping (LENS) technology, a Direct Energy Deposition (DED) method. Internal voids and defects were induced in a second batch of samples by changing LENS machine processing parameters. Fatigue performance of these samples is compared to the wrought Ti-6Al-4V samples. The effects of machine-induced porosity are assessed on mechanical properties and results are presented in the form of SN curves for the three sets of samples. Fracture mechanisms are examined by using Scanning Electron Microscopy (SEM) to characterize the morphological characteristics of the failure surface. Different fracture surface morphologies are observed for porous and non-porous specimens due to the combination of head write speed and laser power. Formation of defects such as pores, unmelted regions, and gas entrapments affect the failure mechanisms in porous specimens. Non-porous specimens exhibit fatigue properties comparable with that of the wrought specimens, but porous specimens are found to show a tremendous reduced fatigue strength.

Crystal viscoplasticity model for the creep-fatigue interactions in single-crystal Ni-base superalloy CMSX-8

DOE Office of Scientific and Technical Information (OSTI.GOV)

Estrada Rodas, Ernesto A.; Neu, Richard W.

A crystal viscoplasticity (CVP) model for the creep-fatigue interactions of nickel-base superalloy CMSX-8 is proposed. At the microstructure scale of relevance, the superalloys are a composite material comprised of a γ phase and a γ' strengthening phase with unique deformation mechanisms that are highly dependent on temperature. Considering the differences in the deformation of the individual material phases is paramount to predicting the deformation behavior of superalloys at a wide range of temperatures. In this work, we account for the relevant deformation mechanisms that take place in both material phases by utilizing two additive strain rates to model the deformationmore » on each material phase. The model is capable of representing the creep-fatigue interactions in single-crystal superalloys for realistic 3-dimensional components in an Abaqus User Material Subroutine (UMAT). Using a set of material parameters calibrated to superalloy CMSX-8, the model predicts creep-fatigue, fatigue and thermomechanical fatigue behavior of this single-crystal superalloy. In conclusion, a sensitivity study of the material parameters is done to explore the effect on the deformation due to changes in the material parameters relevant to the microstructure.« less

Crystal viscoplasticity model for the creep-fatigue interactions in single-crystal Ni-base superalloy CMSX-8

DOE PAGES

Estrada Rodas, Ernesto A.; Neu, Richard W.

2017-09-11

A crystal viscoplasticity (CVP) model for the creep-fatigue interactions of nickel-base superalloy CMSX-8 is proposed. At the microstructure scale of relevance, the superalloys are a composite material comprised of a γ phase and a γ' strengthening phase with unique deformation mechanisms that are highly dependent on temperature. Considering the differences in the deformation of the individual material phases is paramount to predicting the deformation behavior of superalloys at a wide range of temperatures. In this work, we account for the relevant deformation mechanisms that take place in both material phases by utilizing two additive strain rates to model the deformationmore » on each material phase. The model is capable of representing the creep-fatigue interactions in single-crystal superalloys for realistic 3-dimensional components in an Abaqus User Material Subroutine (UMAT). Using a set of material parameters calibrated to superalloy CMSX-8, the model predicts creep-fatigue, fatigue and thermomechanical fatigue behavior of this single-crystal superalloy. In conclusion, a sensitivity study of the material parameters is done to explore the effect on the deformation due to changes in the material parameters relevant to the microstructure.« less

"Well, I'm tired of tryin'!" Organizational citizenship behavior and citizenship fatigue.

PubMed

Bolino, Mark C; Hsiung, Hsin-Hua; Harvey, Jaron; LePine, Jeffery A

2015-01-01

This study seeks to identify workplace conditions that influence the degree to which employees feel worn out, tired, or on edge attributed to engaging in organizational citizenship behavior (OCB) and also how this phenomenon, which we refer to as citizenship fatigue, is associated with future occurrences of OCB. Using data collected from 273 employees and their peers at multiple points in time, we found that the relationship between OCB and citizenship fatigue depends on levels of perceived organizational support, quality of team-member exchange relationships, and pressure to engage in OCB. Specifically, the relationship between OCB and citizenship fatigue is significantly stronger and positive when perceived organizational support is low, and it is significantly stronger and negative when the quality of team-member exchange is high and pressure to engage in OCB is low. Our results also indicate that citizenship fatigue is negatively related to subsequent acts of OCB. Finally, supplemental analyses reveal that the relationship between OCB and citizenship fatigue may vary as a function of the specific facet of OCB. We conclude with a discussion of the key theoretical and practical implications of our findings. (c) 2015 APA, all rights reserved.

Monitoring the fracture behavior of metal matrix composites by combined NDE methodologies

NASA Astrophysics Data System (ADS)

Kordatos, E. Z.; Exarchos, D. A.; Mpalaskas, A. C.; Matikas, T. E.

2015-03-01

Current work deals with the non-destructive evaluation (NDE) of the fatigue behavior of metal matrix composites (MMCs) materials using Infrared Thermography (IRT) and Acoustic Emission (AE). AE monitoring was employed to record a wide spectrum of cracking events enabling the characterization of the severity of fracture in relation to the applied load. IR thermography as a non-destructive, real-time and non-contact technique, allows the detection of heat waves generated by the thermo-mechanical coupling during mechanical loading of the sample. In this study an IR methodology, based on the monitoring of the intrinsically dissipated energy, was applied for the determination of the fatigue limit of A359/SiCp composites. The thermographic monitoring is in agreement with the AE results enabling the reliable monitoring of the MMCs' fatigue behavior.

Low cycle fatigue and creep-fatigue behavior of Ni-based alloy 230 at 850 C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, Xiang; Yang, Zhiqing; Sokolov, Mikhail A

Strain-controlled low cycle fatigue (LCF) and creep-fatigue testing of Ni-based alloy 230 were carried out at 850 C. The material creep-fatigue life decreased compared with its low cycle fatigue life at the same total strain range. Longer hold time at peak tensile strain further reduced the material creep-fatigue life. Based on the electron backscatter diffraction, a novel material deformation characterization method was applied, which revealed that in low cycle fatigue testing as the total strain range increased, the deformation was segregated to grain boundaries since the test temperature was higher than the material equicohesive temperature and grain boundaries became weakermore » regions compared with grains. Creep-fatigue tests enhanced the localized deformation, resulting in material interior intergranular cracking, and accelerated material damage. Precipitation in alloy 230 helped slip dispersion, favorable for fatigue property, but grain boundary cellular precipitates formed after material exposure to the elevated temperature had a deleterious effect on the material low cycle fatigue and creep-fatigue property.« less

Late Weichselian ice-sheet dynamics and deglaciation history of the northern Svalbard margin

NASA Astrophysics Data System (ADS)

Fransner, O.; Noormets, R. R. N. N.; Flink, A.; Hogan, K.; Dowdeswell, J. A.; O'Regan, M.; Jakobsson, M.

2016-12-01

The glacial evolution of the northern Svalbard margin is poorly known compared with the western margin. Gravity cores, swath bathymetric, sub-bottom acoustic and 2D airgun data are used to investigate the Late Weichselian Svalbard-Barents Ice Sheet history on the northern Svalbard margin. Prograding sequences in Kvitøya and Albertini trough mouths (TMs) indicate ice streaming to the shelf edge multiple times during the Quaternary. While Kvitøya Trough has an associated trough-mouth fan (TMF), Albertini TM is cut back into the shelf edge. Down-faulted bedrock below Albertini TM suggests larger sediment accommodation space there, explaining the absence of a TMF. The bathymetry indicates that ice flow in Albertini Trough was sourced from Duvefjorden and Albertinibukta. Exposed crystalline bedrock likely kept the two ice flows separated before merging north of Karl XII-Øya. Subglacial landforms in Rijpfjorden and Duvefjorden indicate that both fjords accommodated northward-flowing ice streams during the LGM. The deeper fjord basin and higher elongation ratios of landforms in Duvefjorden suggest a more focused and/or larger ice flow there. Easily erodible sedimentary rocks are common in Duvefjorden, which may explain different ice flow dynamics in these fjords. Kvitøya TMF is flanked by gullies, probably formed through erosive downslope gravity flows triggered by sediment-laden meltwater during early deglaciation. Glacial landforms in Albertini Trough comprise retreat-related landforms indicating slow deglaciation. Iceberg scours in Albertini Trough suggest the importance of calving for mass-loss. Sets of De Geer moraines in Rijpfjorden imply that slow, grounded retreat continued in <210 m water depth. Lack of retreat-related landforms in deeper areas of Rijpfjorden and in Duvefjorden indicates floating glacier fronts influenced by calving. 14C ages suggest that deglaciation of inner Rijpfjorden and central Duvefjorden were complete before 10,434 cal a BP and 10,779 cal a BP respectively.

SU-E-P-14: Dosimetric Effects of Magnetic Field in MRI-Guided Radiation Therapy Delivery for Breast Cancer

DOE Office of Scientific and Technical Information (OSTI.GOV)

Chen, G; Currey, A; Li, X

2015-06-15

Purpose: MRI-guided radiation therapy (RT) delivery would be beneficial for breast irradiation. The electron return effect due to the presence of a transverse magnetic field (TMF) may cause dosimetric issues on dose on skin and at the lung-tissue interface. The purpose of this study is to investigate these issues. Methods: IMRT plans with tangential beams and VMAT plans with 200 degree arcs to cover ipsilateral breast were generated for 10 randomly selected breast cancer cases using a research planning system (Monaco, Elekta) utilizing Monte Carlo dose calculation with or without a TMF of 1.5 T. Plans were optimized to delivermore » uniform dose to the whole breast with an exclusion of 5 mm tissue under the skin (PTV-EVAL). All four plans for each patient were re-scaled to have the same PTV-EVAL volume to receive the same prescription dose. The skin is defined as the first 5 mm of ipsilateral-breast tissue, plus extensions in the surrounding region. Results: The presence of 1.5 T TMF resulted in (1)increased skin dose, with the mean and maximum skin dose increase of 5% and 9%, respectively; (2) similar dose homogeneity within the PTV-EVAL; (3) the slightly improved (3%) dose homogeneity in the whole breast; (4) Averages of 9 and 16% increases in V5 and V20, respectively, for ipsilateral lung; and (5) increased the mean heart dose by 34%. VMAT plans don’t improve whole breast dose uniformity as compared that to the tangential plans. Conclusion: The presence of transverse magnetic field in MRI-guided RT delivery for whole breast irradiation can Result in slightly improved dose homogeneity in the whole breast, increased dose to the ipsilateral lung, heart, and skin. Plan optimization with additional specific dose volume constraints may eliminate/reduce these dose increases. This work is partially supported by Elekta Inc.« less

Flavonoids-Rich Orthosiphon stamineus Extract as New Candidate for Angiotensin I-Converting Enzyme Inhibition: A Molecular Docking Study.

PubMed

Shafaei, Armaghan; Sultan Khan, Md Shamsuddin; F A Aisha, Abdalrahim; Abdul Majid, Amin Malik Shah; Hamdan, Mohammad Razak; Mordi, Mohd Nizam; Ismail, Zhari

2016-11-09

This study aims to evaluate the in vitro angiotensin-converting enzyme (ACE) inhibition activity of different extracts of Orthosiphon stamineus (OS) leaves and their main flavonoids, namely rosmarinic acid (RA), sinensetin (SIN), eupatorin (EUP) and 3'-hydroxy-5,6,7,4'-tetramethoxyflavone (TMF). Furthermore, to identify possible mechanisms of action based on structure-activity relationships and molecular docking. The in vitro ACE inhibition activity relied on determining hippuric acid (HA) formation from ACE-specific substrate (hippuryl-histidyl-leucine (HHL)) by the action of ACE enzyme. A High Performance Liquid Chromatography method combined with UV detection was developed and validated for measurement the concentration of produced HA. The chelation ability of OS extract and its reference compounds was evaluated by tetramethylmurexide reagent. Furthermore, molecular docking study was performed by LeadIT-FlexX : BioSolveIT's LeadIT program. OS ethanolic extract (OS-E) exhibited highest inhibition and lowest IC 50 value (45.77 ± 1.17 µg/mL) against ACE compared to the other extracts. Among the tested reference compounds, EUP with IC 50 15.35 ± 4.49 µg/mL had highest inhibition against ACE and binding ability with Zn (II) (56.03% ± 1.26%) compared to RA, TMF and SIN. Molecular docking studies also confirmed that flavonoids inhibit ACE via interaction with the zinc ion and this interaction is stabilized by other interactions with amino acids in the active site. In this study, we have demonstrated that changes in flavonoids active core affect their capacity to inhibit ACE. Moreover, we showed that ACE inhibition activity of flavonoids compounds is directly related to their ability to bind with zinc ion in the active site of ACE enzyme. It was also revealed that OS extract contained high amount of flavonoids other than RA, TMF, SIN and EUP. As such, application of OS extract is useful as inhibitors of ACE.

A Pragmatic Evaluation of the National Cancer Institute Physician Data Query (PDQ)®-Based Brief Counseling on Cancer-Related Fatigue among Patients Undergoing Radiation Therapy

PubMed Central

Bauml, Joshua; Xie, Sharon X; Penn, Courtney; Desai, Krupali; Dong, Kimberly W; Bruner, Deborah Watkins; Vapiwala, Neha; Mao, Jun James

2018-01-01

Purpose Cancer-Related Fatigue (CRF) negatively affects quality of life among cancer patients. This study seeks to evaluate the outcome and patient receptiveness of a brief counseling program based on National Cancer Institute (NCI) PDQ® information to manage CRF when integrated into Radiation Therapy (RT). Methods We conducted a prospective cohort study among patients undergoing non-palliative RT. Patients with stage I–III tumors and with Karnofsky score 60 or better were given a ten-minute behavioral counseling session during the first two weeks of RT. The Brief Fatigue Inventory (BFI) was administered at baseline/end of RT. Results Of 93 patients enrolled, 89% found the counseling useful and practical. By the end of RT, 59% reported increased exercise, 41.6% sought nutrition counseling, 72.7% prioritized daily activities, 74.4% took daytime naps, and 70.5% talked with other cancer patients. Regarding counseling, patients who had received chemotherapy prior to RT had no change in fatigue (−0.2), those who received RT alone had mild increase in fatigue (0.7, p=0.02), and those who received concurrent chemotherapy experienced a substantial increase in fatigue (3.0 to 5.2, p=0.05). Higher baseline fatigue and receipt of chemotherapy were predictive of worsened fatigue in a multivariate model (both p<0.01). Conclusion Our data suggests that brief behavioral counseling based on NCI guidelines is well accepted by patients showing an uptake in many activities to cope with CRF. Those who receive concurrent chemotherapy and with higher baseline fatigue are at risk for worsening fatigue despite of guideline-based therapy. PMID:29479490

Mechanical Behavior and Fatigue Studies of Rubber Components Used in Tracked Vehicles

DTIC Science & Technology

2010-08-17

durability to this elastomers and polybutadiene is rubber , which gives rubber -like properties. SBR has good abrasion resistance and good aging ...SIMULATION, TESTING AND VALIDATION (MSTV) MINI-SYMPOSIUM AUGUST 17-19 DEARBORN, MICHIGAN MECHANICAL BEHAVIOR AND FATIGUE STUDIES OF RUBBER COMPONENTS USED...Analytics Group US Army TARDEC Warren, MI ABSTRACT In this study, a styrene butadiene rubber , which is similar to the rubber used in road wheel

Analysis of Methods for Determining High Cycle Fatigue Strength of a Material With Investigation of Ti-6Al-4V Gigacycle Fatigue Behavior

DTIC Science & Technology

2005-10-01

al [77]). 44 Figure 17. Schematic illustration of bimodal S-N behavior (from Mughrabi [54]). The work of these researchers and others has...62 Braam and van der Zwaag Correction ............................................................ 63 Fang et al Approach...Figure 16. Conceptual S-N curves using the concept of a bimodal model (from Shiozawa et al [77

Influence of different temperatures on the thermal fatigue behavior and thermal stability of hot-work tool steel processed by a biomimetic couple laser technique

NASA Astrophysics Data System (ADS)

Meng, Chao; Zhou, Hong; Zhou, Ying; Gao, Ming; Tong, Xin; Cong, Dalong; Wang, Chuanwei; Chang, Fang; Ren, Luquan

2014-04-01

Three kinds of biomimetic non-smooth shapes (spot-shape, striation-shape and reticulation-shape) were fabricated on the surface of H13 hot-work tool steel by laser. We investigated the thermal fatigue behavior of biomimetic non-smooth samples with three kinds of shapes at different thermal cycle temperature. Moreover, the evolution of microstructure, as well as the variations of hardness of laser affected area and matrix were studied and compared. The results showed that biomimetic non-smooth samples had better thermal fatigue behavior compared to the untreated samples at different thermal cycle temperatures. For a given maximal temperature, the biomimetic non-smooth sample with reticulation-shape had the optimum thermal fatigue behavior, than with striation-shape which was better than that with the spot-shape. The microstructure observations indicated that at different thermal cycle temperatures the coarsening degrees of microstructures of laser affected area were different and the microstructures of laser affected area were still finer than that of the untreated samples. Although the resistance to thermal cycling softening of laser affected area was lower than that of the untreated sample, laser affected area had higher microhardness than the untreated sample at different thermal cycle temperature.

Effect of Hierarchical Microstructures of Lath Martensite on the Transitional Behavior of Fatigue Crack Growth Rate

NASA Astrophysics Data System (ADS)

Yang, Ming; Zhong, Yi; Liang, Yi-long

2018-04-01

In this study, the fatigue-crack growth (FCG) behavior of 20CrMTiH steel with different substructure sizes was investigated. The results showed that coarsen microstructures exhibit excellent growth resistance. Moreover, two transitional behaviors were observed in the FCG curves of all specimens. The first transition point occurs in the near-threshold regime, whereas the second transition point occurs in the Paris regime. A comparison of substructure size to cyclic plastic size showed that the block size is almost equal to cyclic plastic size at ΔKT1, indicating that block size is an effective grain size to control the first transitional behavior of fatigue-crack propagation, whereas the second transitional behavior is related to the packet width or grain size. According to the fracture morphology, the fracture mechanism above and below the transition point responsible for the above phenomenon were distinguished. In addition, two prediction models based on microstructure size were established for lath martensite to evaluate the threshold and stress intensity factor range at the transition point.

Effects of cooling rate and stabilization annealing on fatigue behavior of β-processed Ti-6Al-4V alloys

NASA Astrophysics Data System (ADS)

Seo, Wongyu; Jeong, Daeho; Lee, Dongjun; Sung, Hyokyung; Kwon, Yongnam; Kim, Sangshik

2017-07-01

The effects of stabilization annealing and cooling rate on high cycle fatigue (HCF) and fatigue crack propagation (FCP) behaviors of β-processed Ti64 alloys were examined. After β-process heating above β transus, two different cooling rates of air cooling (β-annealing) and water quenching (β-quenching) were utilized. Selected specimens were then underwent stabilization annealing. The tensile tests, HCF and FCP tests on conducted on the β-processed Ti64 specimens with and without stabilization annealing. No notable microstructural and mechanical changes with stabilization annealing was observed for the β-annealed Ti64 alloys. However, significant effect of stabilization annealing was found on the FCP behavior of β-quenched Ti64 alloys, which appeared to be related to the built-up of residual stress after quenching. The mechanical behavior of β-processed Ti64 alloys with and with stabilization annealing was discussed based on the micrographic examination, including crack growth path and crack nucleation site, and fractographic analysis.

Deformation Behavior of Recycled Concrete Aggregate during Cyclic and Dynamic Loading Laboratory Tests

PubMed Central

Sas, Wojciech; Głuchowski, Andrzej; Gabryś, Katarzyna; Soból, Emil; Szymański, Alojzy

2016-01-01

Recycled concrete aggregate (RCA) is a relatively new construction material, whose applications can replace natural aggregates. To do so, extensive studies on its mechanical behavior and deformation characteristics are still necessary. RCA is currently used as a subbase material in the construction of roads, which are subject to high settlements due to traffic loading. The deformation characteristics of RCA must, therefore, be established to find the possible fatigue and damage behavior for this new material. In this article, a series of triaxial cyclic loading and resonant column tests is used to characterize fatigue in RCA as a function of applied deviator stress after long-term cyclic loading. A description of the shakedown phenomenon occurring in the RCA and calculations of its resilient modulus (Mr) as a function of fatigue are also presented. Test result analysis with the stress-life method on the Wohler S-N diagram shows the RCA behavior in accordance with the Basquin law. PMID:28773905

High temperature fatigue behavior of Haynes 188

NASA Technical Reports Server (NTRS)

Halford, Gary R.; Saltsman, James F.; Kalluri, Sreeramesh

1988-01-01

The high temperature, creep-fatigue behavior of Haynes 188 was investigated as an element in a broader thermomechanical fatigue life prediction model development program at the NASA-Lewis. The models are still in the development stage, but the data that were generated possess intrinsic value on their own. Results generated to date is reported. Data were generated to characterize isothermal low cycle fatigue resistance at temperatures of 316, 704, and 927 C with cyclic failure lives ranging from 10 to more than 20,000. These results follow trends that would be predicted from a knowledge of tensile properties, i.e., as the tensile ductility varies with temperature, so varies the cyclic inelastic straining capacity. Likewise, as the tensile strength decreases, so does the high cyclic fatigue resistance. A few two-minute hold-time cycles at peak compressive strain were included in tests at 760 C. These results were obtained in support of a redesign effort for the Orbital Maneuverable System engine. No detrimental effects on cyclic life were noted despite the added exposure time for creep and oxidation. Finally, a series of simulated thermal fatigue tests, referred to as bithermal fatigue tests, were conducted using 316 C as the minimum and 760 C as the maximum temperature. Only out-of-phase bithermal tests were conducted to date. These test results are intended for use as input to a more general thermomechanical fatigue life prediction model based on the concepts of the total strain version of Strainrange Partitioning.

Comparison of Elevated Temperature Tensile Properties and Fatigue Behavior of Two Variants of a Woven SiC/SiC Composite

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Brewer, David N.; Sreeramesh, Kalluri

2005-01-01

Tensile properties (elastic modulus, proportional limit strength, in-plane tensile strength, and strain at failure) of two variants of a woven SiC/SiC composite, manufactured during two separate time periods (9/99 and 1/01), were determined at 1038 and 1204 C by conducting tensile tests on specimens machined from plates. Continuous cycling fatigue tests (R = 0.05) and 20 cpm) were also conducted at the same two temperatures on specimens from both composites. In this study, average tensile properties, 95% confidence intervals associated with the tensile properties, and geometric mean fatigue lives of both composite materials are compared. The observed similarities and differences in the tensile properties are highlighted and an attempt is made to understand the relationship, if any, between the tensile properties and the fatigue behaviors of the two woven composites.

Influence of De-icers on the Corrosion and Fatigue Behavior of 4140 Steel

NASA Astrophysics Data System (ADS)

Dean, William P.; Sanford, Brittain J.; Wright, Matthew R.; Evans, Jeffrey L.

2012-11-01

The purpose of this test was to evaluate the effects of calcium magnesium acetate (CMA) and sodium chloride (NaCl)—two common substances used to de-ice roadways—on the corrosion and fatigue behavior of annealed AISI 4140 steel. When CMA-corroded, NaCl-corroded, and as-machined samples were tested using R = 0.1, and f = 20 Hz, it was found that, within the scope of this study, samples corroded in both 3.5% CMA solution and 3.5% NaCl solution exhibited a lower fatigue strength than samples tested in the as-machined, uncorroded condition. For the short lives tested in this study, the difference in the effects of CMA and NaCl is minimal. However, at longer lives it is suspected, based on the trends, that the CMA solution would be less detrimental to the fatigue life.

Improvement of fatigue resistance for multilayer lead zirconate titanate (PZT)-based ceramic actuators by external mechanical loads

NASA Astrophysics Data System (ADS)

Yang, Gang; Yue, Zhenxing; Ji, Ye; Chu, Xiangcheng; Li, Longtu

2008-12-01

The influence of external compressive loads, applied along a direction perpendicular to polarization, on fatigue behaviors of multilayer lead zirconate titanate (PZT)-based ceramic actuators was investigated. Under no external mechanical load, a normal fatigue behavior was observed, demonstrating that both switching polarization (Pswitching) and remnant polarization (Pr) progressively decreased with increasing switching cycles due to domain pinning by charge point defects. However, an anomalous enhancement in both switching and remnant polarizations was observed upon application of the external compressive loads. After 5×106 cycles of polarization switching, Pswitching and Pr increase by about 13% and 6% at 40 MPa, respectively, while Pswitching and Pr increase by about 11% and 21% at 60 MPa, respectively. The improvement of fatigue resistance can be attributed to non-180° domain switching and suppression of microcracking, triggered by external mechanical loads.

Creep-Fatigue Behavior of Alloy 617 at 850 and 950°C, Revision 2

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carroll, L.; Carroll, M.

Alloy 617 is the leading candidate material for an Intermediate Heat Exchanger (IHX) of the Very High Temperature Reactor (VHTR). To evaluate the behavior of this material in the expected service conditions, strain-controlled cyclic tests including hold times up to 9000 s at maximum tensile strain were conducted at 850 and 950 degrees C. At both temperatures, the fatigue resistance decreased when a hold time was added at peak tensile strain. The magnitude of this effect depended on the specific mechanisms and whether they resulted in a change in fracture mode from transgranular in pure fatigue to intergranular in creep-fatiguemore » for a particular temperature and strain range combination. Increases in the tensile hold duration beyond an initial value were not detrimental to the creep-fatigue resistance at 950 degrees C but did continue to degrade the lifetimes at 850 degrees C.« less

Gigacycle fatigue behavior by ultrasonic nanocrystalline surface modification.

PubMed

Ahn, D G; Amanov, A; Cho, I S; Shin, K S; Pyoun, Y S; Lee, C S; Park, I G

2012-07-01

Nanocrystalline surface layer up to 84 microm in thick is produced on a specimen made of Al6061-T6 alloy by means of surface treatment called ultrasonic nanocrystalline surface modification (UNSM) technique. The refined grain size is produced in the top-layer and it is increased with increasing depth from the top surface. Vickers microhardness measurement for each nanocrystalline surface layer is performed and measurement results showed that the microhardness is increased from 116 HV up to 150 HV, respectively. In this study, fatigue behavior of Al6061-T6 alloy was studied up to 10(7)-10(9) cycles by using a newly developed ultrasonic fatigue testing (UFT) rig. The fatigue results of the UNSM-treated Al6061-T6 alloy specimens were compared with those of the untreated specimens. The microstructure of the untreated and UNSM-treated specimens was characterized by means of scanning electron microscopey (SEM) and transmission electron microscopey (TEM).

Ultrasonic Corrosion Fatigue Behavior of High Strength Austenitic Stainless Steels

NASA Astrophysics Data System (ADS)

Ebara, R.; Yamaguchi, Y.; Kanei, D.; Yamamoto, Y.

Ultrasonic corrosion fatigue tests were conducted for high strength austenitic stainless steels such as YUS270 and SUS304N2 in 3%NaCl aqueous solution. The reduction of giga-cycle corrosion fatigue strength of YUS270 and SUS304N2 was not observed at all, while the reduction of corrosion fatigue life was observed at higher stress amplitude. Corrosion pit was observed on corrosion fatigue crack initiation area. Striation was predominantly observed on crack propagation area in air and in 3% NaCl aqueous solution. The reduction of corrosion fatigue strength of high strength austenitic stainless steels such as YUS270 and SUS304N2 is due to the corrosion pit formation at corrosion fatigue crack initiation area. It can be concluded that the higher the ultimate tensile strength of austenitic stainless steels the higher the giga-cycle corrosion fatigue strength in 3%NaCl aqueous solution is.

A narrative review on the similarities and dissimilarities between myalgic encephalomyelitis/chronic fatigue syndrome (ME/CFS) and sickness behavior.

PubMed

Morris, Gerwyn; Anderson, George; Galecki, Piotr; Berk, Michael; Maes, Michael

2013-03-08

It is of importance whether myalgic encephalomyelitis/chronic fatigue syndrome (ME/CFS) is a variant of sickness behavior. The latter is induced by acute infections/injury being principally mediated through proinflammatory cytokines. Sickness is a beneficial behavioral response that serves to enhance recovery, conserves energy and plays a role in the resolution of inflammation. There are behavioral/symptomatic similarities (for example, fatigue, malaise, hyperalgesia) and dissimilarities (gastrointestinal symptoms, anorexia and weight loss) between sickness and ME/CFS. While sickness is an adaptive response induced by proinflammatory cytokines, ME/CFS is a chronic, disabling disorder, where the pathophysiology is related to activation of immunoinflammatory and oxidative pathways and autoimmune responses. While sickness behavior is a state of energy conservation, which plays a role in combating pathogens, ME/CFS is a chronic disease underpinned by a state of energy depletion. While sickness is an acute response to infection/injury, the trigger factors in ME/CFS are less well defined and encompass acute and chronic infections, as well as inflammatory or autoimmune diseases. It is concluded that sickness behavior and ME/CFS are two different conditions.

A narrative review on the similarities and dissimilarities between myalgic encephalomyelitis/chronic fatigue syndrome (ME/CFS) and sickness behavior

PubMed Central

2013-01-01

It is of importance whether myalgic encephalomyelitis/chronic fatigue syndrome (ME/CFS) is a variant of sickness behavior. The latter is induced by acute infections/injury being principally mediated through proinflammatory cytokines. Sickness is a beneficial behavioral response that serves to enhance recovery, conserves energy and plays a role in the resolution of inflammation. There are behavioral/symptomatic similarities (for example, fatigue, malaise, hyperalgesia) and dissimilarities (gastrointestinal symptoms, anorexia and weight loss) between sickness and ME/CFS. While sickness is an adaptive response induced by proinflammatory cytokines, ME/CFS is a chronic, disabling disorder, where the pathophysiology is related to activation of immunoinflammatory and oxidative pathways and autoimmune responses. While sickness behavior is a state of energy conservation, which plays a role in combating pathogens, ME/CFS is a chronic disease underpinned by a state of energy depletion. While sickness is an acute response to infection/injury, the trigger factors in ME/CFS are less well defined and encompass acute and chronic infections, as well as inflammatory or autoimmune diseases. It is concluded that sickness behavior and ME/CFS are two different conditions. PMID:23497361

European Scientific Notes. Volume 34, Number 7,

DTIC Science & Technology

1980-07-31

fatigue , the effect of patient during the fitting, but which moisture on mechanical properties, could still be bent 900 without delamin- and creep...behavior. In the fatigue ating the composite or debonding the work; different reinforcing fibers composite from the aluminum . Once (including glass-carbon... fatigue work sulting structure has better properties Sturgeon has under way includes the than steel and weighs a good deal less, effect of

Evidence that abnormal grain growth precedes fatigue crack initiation in nanocrystalline Ni-Fe

DOE Office of Scientific and Technical Information (OSTI.GOV)

Furnish, Timothy A.; Bufford, Daniel C.; Ren, Fang

Prior studies on the high-cycle fatigue behavior of nanocrystalline metals have shown that fatigue fracture is associated with abnormal grain growth (AGG). However, those previous studies have been unable to determine if AGG precedes fatigue crack initiation, or vice-versa. The present study shows that AGG indeed occurs prior to crack formation in nanocrystalline Ni-Fe by using a recently developed synchrotron X-ray diffraction modality that has been adapted for in-situ analysis. The technique allows fatigue tests to be interrupted at the initial signs of the AGG process, and subsequent microscopy reveals the precursor damage state preceding crack initiation.

Domain switching of fatigued ferroelectric thin films

NASA Astrophysics Data System (ADS)

Tak Lim, Yun; Yeog Son, Jong; Shin, Young-Han

2014-05-01

We investigate the domain wall speed of a ferroelectric PbZr0.48Ti0.52O3 (PZT) thin film using an atomic force microscope incorporated with a mercury-probe system to control the degree of electrical fatigue. The depolarization field in the PZT thin film decreases with increasing the degree of electrical fatigue. We find that the wide-range activation field previously reported in ferroelectric domains result from the change of the depolarization field caused by the electrical fatigue. Domain wall speed exhibits universal behavior to the effective electric field (defined by an applied electric field minus the depolarization field), regardless of the degree of the electrical fatigue.

Evidence that abnormal grain growth precedes fatigue crack initiation in nanocrystalline Ni-Fe

DOE PAGES

Furnish, Timothy A.; Bufford, Daniel C.; Ren, Fang; ...

2018-09-06

Prior studies on the high-cycle fatigue behavior of nanocrystalline metals have shown that fatigue fracture is associated with abnormal grain growth (AGG). However, those previous studies have been unable to determine if AGG precedes fatigue crack initiation, or vice-versa. The present study shows that AGG indeed occurs prior to crack formation in nanocrystalline Ni-Fe by using a recently developed synchrotron X-ray diffraction modality that has been adapted for in-situ analysis. The technique allows fatigue tests to be interrupted at the initial signs of the AGG process, and subsequent microscopy reveals the precursor damage state preceding crack initiation.

Effects of a One-to-One Fatigue Management Course for People With Chronic Conditions and Fatigue.

PubMed

Van Heest, Katy N L; Mogush, Ashley R; Mathiowetz, Virgil G

We assessed the impact of a one-to-one fatigue management course on participants' fatigue, self-efficacy, quality of life, and energy conservation behaviors. This observational study used a one-group, pretest-posttest, follow-up design. Forty-nine people with chronic conditions and fatigue participated in the one-to-one fatigue management course in outpatient and community-based settings. The Functional Assessment of Chronic Illness Therapy-Fatigue Scale was used to measure fatigue; the Functional Assessment of Cancer Therapy-General measured quality of life; and the Self-Efficacy for Performing Energy Conservation Strategies Assessment was used to measure self-efficacy. Participants showed significant reductions in fatigue and significant increases in self-efficacy and quality of life at posttest. These beneficial effects were maintained at follow-up. The Social Well-Being subscale was the only measure on which outcomes did not change significantly. The one-to-one fatigue management course is a beneficial intervention for people with chronic conditions and fatigue. Copyright © 2017 by the American Occupational Therapy Association, Inc.

Effect of Environment on Fatigue Behavior of a Nicalon(TM)/Si-N-C Ceramic Matrix Composite

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Ojard, Greg C.; Verrilli, Michael J.; Kiraly, Louis J. (Technical Monitor)

2002-01-01

The effect of environmental exposure on the fatigue life of Nicalon(TM) /Si-N-C composite was investigated in this study. Test specimens with arrays of 1.8 mm diameter holes and two different open areas, 25 and 35%, were machined. Three environmental conditions were studied: 1) continuous fatigue cycling in air, 2) fatigue cycling in air alternating with humidity exposure, and 3) fatigue cycling in air alternating with exposure to a salt-fog environment. All fatigue testing on specimens with holes was performed with a load ratio, R = 0.05, and at a temperature of 910 C. In general, fatigue lives were shortest for specimens subjected to salt-fog exposure and longest for specimens subjected to continuous fatigue cycling in air. The fatigue data generated on the specimens with holes were compared with fatigue data generated in air on specimens with no holes. Fatigue strength reduction factors for different environmental conditions and open areas investigated in the study were calculated for the Nicalon(TM) /Si-N-C composite.

Fatigue Behavior under Multiaxial Stress States Including Notch Effects and Variable Amplitude Loading

NASA Astrophysics Data System (ADS)

Gates, Nicholas R.

The central objective of the research performed in this study was to be able to better understand and predict fatigue crack initiation and growth from stress concentrations subjected to complex service loading histories. As such, major areas of focus were related to the understanding and modeling of material deformation behavior, fatigue damage quantification, notch effects, cycle counting, damage accumulation, and crack growth behavior under multiaxial nominal loading conditions. To support the analytical work, a wide variety of deformation and fatigue tests were also performed using tubular and plate specimens made from 2024-T3 aluminum alloy, with and without the inclusion of a circular through-thickness hole. However, the analysis procedures implemented were meant to be general in nature, and applicable to a wide variety of materials and component geometries. As a result, experimental data from literature were also used, when appropriate, to supplement the findings of various analyses. Popular approaches currently used for multiaxial fatigue life analysis are based on the idea of computing an equivalent stress/strain quantity through the extension of static yield criteria. This equivalent stress/strain is then considered to be equal, in terms of fatigue damage, to a uniaxial loading of the same magnitude. However, it has often been shown, and was shown again in this study, that although equivalent stress- and strain-based analysis approaches may work well in certain situations, they lack a general robustness and offer little room for improvement. More advanced analysis techniques, on the other hand, provide an opportunity to more accurately account for various aspects of the fatigue failure process under both constant and variable amplitude loading conditions. As a result, such techniques were of primary interest in the investigations performed. By implementing more advanced life prediction methodologies, both the overall accuracy and the correlation of fatigue life predictions were found to improve for all loading conditions considered in this study. The quantification of multiaxial fatigue damage was identified as being a key area of improvement, where the shear-based Fatemi-Socie (FS) critical plane damage parameter was shown to correlate all fully-reversed constant amplitude fatigue data relatively well. Additionally, a proposed modification to the FS parameter was found to result in improved life predictions in the presence of high tensile mean stress and for different ratios of nominal shear to axial stress. For notched specimens, improvements were also gained through the use of more robust notch deformation and stress gradient models. Theory of Critical Distances (TCD) approaches, together with pseudo stress-based plasticity modeling techniques for local stress-strain estimation, resulted in better correlation of multiaxial fatigue data when compared to traditional approaches such as Neuber's rule with fatigue notch factor. Since damage parameters containing both stress and strain terms, such as the FS parameter, are able to reflect changes in fatigue damage due to transient material hardening behavior, this issue was also investigated with respect to its impact on variable amplitude life predictions. In order to ensure that material deformation behavior was properly accounted for, stress-strain predictions based on an Armstrong-Frederick-Chaboche style cyclic plasticity model were first compared to results from deformation tests performed under a variety of complex multiaxial loading conditions. The model was simplified based on the assumption of Masing material behavior, and a new transient hardening formulation was proposed so that all modeling parameters could be determined from a relatively limited amount of experimental data. Overall, model predictions were found to agree fairly well with experimental results for all loading histories considered. Finally, in order to evaluate life prediction procedures under realistic loading conditions, variable amplitude fatigue tests were performed using axial, torsion, and combined axial-torsion loading histories derived from recorded flight test data on the lower wing skin area of a military patrol aircraft (tension-dominated). While negligible improvements in life predictions were obtained through the consideration of transient material deformation behavior for these histories, crack initiation definition was found to have a slightly larger impact on prediction accuracy. As a result, when performing analyses using the modified FS damage parameter, transient stress-strain response, and a 0.2 mm crack initiation definition, nearly all variable amplitude fatigue lives, for un-notched and notched specimens, were predicted within a factor of 3 of experimental results. However, variable amplitude life predictions were still more non-conservative than those observed for constant amplitude loading conditions.

Fatigued and drowsy driving: a survey of attitudes, opinions and behaviors.

PubMed

Vanlaar, Ward; Simpson, Herb; Mayhew, Dan; Robertson, Robyn

2008-01-01

There is evidence suggesting that the problem of fatigued or drowsy driving is an important contributor to road crashes. However, not much is known about public perceptions of the issue. The purpose of this study was to obtain information on attitudes, opinions, and professed practices related to fatigued or drowsy driving. The data were gathered by means of a public opinion poll among a representative sample of 750 Ontario drivers. A majority of drivers (58.6%) admitted that they occasionally drive while fatigued or drowsy. Of greater importance, 14.5% of respondents admitted that they had fallen asleep or "nodded off" while driving during the past year. Nearly 2% were involved in a fatigue or drowsy driving related crash in the past year. Respondents were also asked about measures they take to overcome fatigue or drowsiness. Results indicate that relatively ineffective measures such as opening the window or playing music are the most popular; the most effective preventive measure--taking a rest--is the least popular. The prevalence of the behavior, coupled with the ineffective prevention measures favored by the public suggest there is a need for increasing their level of awareness and knowledge about the problem. Results from this study further emphasize the importance of increasing the fatigued and drowsy driving knowledge base and the need to educate the public about it.

Microstructure, Fatigue Behavior, and Failure Mechanisms of Direct Laser-Deposited Inconel 718

NASA Astrophysics Data System (ADS)

Johnson, Alex S.; Shao, Shuai; Shamsaei, Nima; Thompson, Scott M.; Bian, Linkan

2017-03-01

Inconel 718 is considered to be a superalloy with a series of superior properties such as high strength, creep resistance, and corrosion resistance at room and elevated temperatures. Additive manufacturing (AM) is particularly appealing to Inconel 718 because of its near-net-shape production capability for circumventing the poor machinability of this superalloy. Nevertheless, AM parts are prone to porosity, which is detrimental to their fatigue resistance. Thus, further understanding of their fatigue behavior is required before their widespread use in load-bearing applications. In this work, the microstructure and fatigue properties of AM Inconel 718, produced in a Laser Engineered Net Shaping (LENS™) system and heat treated with a standard heat treatment schedule, are evaluated at room temperature. Fully reversed strain controlled fatigue tests were performed on cylindrical specimens with straight gage sections at strain amplitudes ranging from 0.001 mm/mm to 0.01 mm/mm. The fracture surfaces of fatigue specimens were inspected with a scanning electron microscope. The results indicate that the employed heat treatment allowed the large, elongated grains and dendritic structure of the as-built material to break down into smaller, equiaxed grains, with some dendritic structures remaining between layers. The AM specimens were found to possess lower fatigue resistance than wrought Inconel 718, and this is primarily attributed to the presence of brittle metal-carbide/oxide inclusions or pores near their surface.

Perceived Fatigue Interference and Depressed Mood: Comparison of Chronic Fatigue Syndrome/Myalgic Encephalomyelitis Patients with Fatigued Breast Cancer Survivors.

PubMed

Hall, Daniel L; Antoni, Michael H; Lattie, Emily G; Jutagir, Devika R; Czaja, Sara J; Perdomo, Dolores; Lechner, Suzanne C; Stagl, Jamie M; Bouchard, Laura C; Gudenkauf, Lisa M; Traeger, Lara; Fletcher, MaryAnn; Klimas, Nancy G

Persistent fatigue and depressive symptoms are both highly prevalent among patients with Chronic Fatigue Syndrome/Myalgic Encephalomyelitis (CFS/ME) as well as breast cancer survivors. This study aimed to assess and directly compare perceptions of fatigue as highly interfering in one's daily functioning in both patient populations to better understand their relationships with depressed mood. Participants were 95 female CFS/ME patients and 67 females who were approximately 5 years post-treatment for stage 0-III breast cancer presenting with clinically elevated fatigue severity. Self-report measures were obtained on participants' fatigue-related interference in daily functioning and fatigue severity as well as depressed mood. Hierarchical regression was used to test effects controlling for relevant demographic, psychosocial, and medical covariates. CFS/ME patients endorsed greater depressed mood and fatigue interference than did fatigued breast cancer survivors, p's <.001. These factors were significantly positively correlated among CFS/ME patients (β=.36, p <.001), but not the fatigued breast cancer survivors (β=.18, p =.19). CFS/ME patients reported elevated fatigue symptoms and depression relative to fatigued breast cancer survivors. In the former group, greater depressed mood was highly and significantly associated with greater fatigue-related inference in daily activities. Potential targets for cognitive behavioral interventions are discussed.

The Development and Preliminary Testing of an Instrument for Assessing Fatigue Self-management Outcomes in Patients With Advanced Cancer.

PubMed

Chan, Raymond Javan; Yates, Patsy; McCarthy, Alexandra L

Fatigue is one of the most distressing and commonly experienced symptoms in patients with advanced cancer. Although the self-management (SM) of cancer-related symptoms has received increasing attention, no research instrument assessing fatigue SM outcomes for patients with advanced cancer is available. The aim of this study was to describe the development and preliminary testing of an interviewer-administered instrument for assessing the frequency and perceived levels of effectiveness and self-efficacy associated with fatigue SM behaviors in patients with advanced cancer. The development and testing of the Self-efficacy in Managing Symptoms Scale-Fatigue Subscale for Patients With Advanced Cancer (SMSFS-A) involved a number of procedures: item generation using a comprehensive literature review and semistructured interviews, content validity evaluation using expert panel reviews, and face validity and test-retest reliability evaluation using pilot testing. Initially, 23 items (22 specific behaviors with 1 global item) were generated from the literature review and semistructured interviews. After 2 rounds of expert panel review, the final scale was reduced to 17 items (16 behaviors with 1 global item). Participants in the pilot test (n = 10) confirmed that the questions in this scale were clear and easy to understand. Bland-Altman analysis showed agreement of results over a 1-week interval. The SMSFS-A items were generated using multiple sources. This tool demonstrated preliminary validity and reliability. The SMSFS-A has the potential to be used for clinical and research purposes. Nurses can use this instrument for collecting data to inform the initiation of appropriate fatigue SM support for this population.