fatigued composite samples: Topics by Science.gov

Sample records for fatigued composite samples

Nondestructive monitoring damage in composites using scanning laser acoustic microscopy

NASA Technical Reports Server (NTRS)

Wey, A. C.; Kessler, L. W.; Dos Reis, H. L. M.

1992-01-01

Several Nicalon fiber reinforced LAS (lithium alumino-silicate) glass matrix composites were tested to study the relation between the residual strength and the different amounts of damage. The samples were fatigued by four-point cyclic loading at a 5 Hz rate at 500 C for a different number of cycles. 10 MHz scanning laser acoustic microscope (SLAM) images were taken to monitor damage on the samples. Our SLAM results indicate that there were defects already existing throughout the sample before fatigue, and the resultant damage pattern from fatigue could be related to the initial defect distribution in the sample. Finally, the fatigued samples were fractured and the residual strength data could not be explained by the cyclic fatigue alone. Rather, the damage patterns evident in the SLAM images were needed to explain the scatter in the data. The results show that SLAM is useful in nondestructively monitoring damage and estimating residual strength of fatigued ceramic composites.
Lamb Wave Response of Fatigued Composite Samples

NASA Technical Reports Server (NTRS)

Seale, Michael; Smith, Barry T.; Prosser, William H.; Masters, John E.

1994-01-01

Composite materials are being more widely used today by aerospace, automotive, sports equipment, and a number of other commercial industries because of their advantages over conventional metals. Composites have a high strength-to-weight ratio and can be constructed to meet specific design needs. Composite structures are already in use in secondary parts of the Douglas MD-11 and are planned to be used in the new MD-12X. Plans also exist for their use in primary and secondary structures on the Boeing 777. Douglas proposed MD-XX may also incorporate composite materials into primary structures such as the wings and tail. Use of composites in these structures offers weight savings, corrosion resistance, and improved aerodynamics. Additionally, composites have been used to repair cracks in many B-1Bs where traditional repair techniques were not very effective. Plans have also been made to reinforce all of the remaining B-1s with composite materials. Verification of the structural integrity of composite components is needed to insure safe operation of these aerospace vehicles. One aspect of the use of these composites is their response to fatigue. To track this progression of fatigue in aerospace structures, a convenient method to nondestructively monitor this damage needs to be developed. Traditional NDE techniques used on metals are not easily adaptable to composites due to the inhomogeneous and anisotropic nature of these materials. Finding an effective means of nondestructively monitoring fatigue damage is extremely important to the safety and reliability of such structures. Lamb waves offer one method of evaluating these composite materials. As a material is fatigued, the modulus degrades. Since the Lamb wave velocity can be related to the modulus of the material, an effective tool can be developed to monitor fatigue damage in composites by measuring the velocity of these waves. In this work, preliminary studies have been conducted which monitor fatigue damage in composite samples using strain gage measurements as well as Lamb wave velocity measurements. A description of the test samples is followed by the results of two different measurements of Lamb wave velocity. The first technique is a contact measurement done at a single frequency, while the second involves an immersion study of Lamb waves in which dispersion curves are obtained. The results of the Lamb wave monitoring of fatigue damage is compared to the damage progression measured by strain gages. The final section discusses the results and conclusions.
Flexural Fatigue Behavior of an EBC CMC Composite System In Air and Steam at High Temperature

NASA Technical Reports Server (NTRS)

Jaskowiak, Martha; Bur, Michael; Harder, Bryan; Gorican, Daniel

2017-01-01

Both coated and uncoated SiCSiC ceramic matrix composite (CMC) samples were tested in flexure under sustained peak low cycle fatigue (SPLCF) conditions in air or steam at elevated temperatures. The SiCSiC composites were reinforced with 2-D plies of boron nitride coated Hi-Nicalon Type-S SiC fibers which were woven as 5 harness satin (5HS) cloth. The composites were densified by chemical vapor infiltration (CVI) followed by slurry melt infiltration (SMI). A multilayer barium strontium aluminosilicate (BSAS) coating was applied to the samples by a plasma spray method. Fatigue loading limits were determined from monotonic flexure tests at room temperature and 1200oC. Stress levels under the proportional limit of the composite material were selected for the SPLCF tests. After cyclic testing, the composites were evaluated to determine crack propagation and failure modes in the coated and uncoated composites. Microstructural examination was used to identify coating degradation and failure modes of the EBCCMC system.
In vitro fatigue behavior of restorative composites and glass ionomers.

PubMed

Braem, M J; Lambrechts, P; Gladys, S; Vanherle, G

1995-03-01

This in vitro study was conducted to investigate the fatigue behavior of several dental restoratives, including composites, glass ionomers and a resin-reinforced glass ionomer. Fatigue was imposed under a reverse stress-controlled regimen, following a staircase approach. Samples were stored and tested under both dry and wet conditions. The following parameters were measured and analyzed: Young's modulus, restrained fracture strength, and flexural fatigue limit. As a general trend, all products showed a decrease in Young's modulus following water sorption. For all products except the resin-reinforced glass ionomer, the same trend was seen in the restrained fracture strength. This is, however, no longer valid for the flexural fatigue limit: the trend is steady-state for the glass ionomers, status quo for the resin-reinforced glass ionomer, and all composites tested show a decrease. The diversity in structure of both composites and glass ionomers does not allow findings for one product to be extrapolated to other similar products.
Thermo-elastic nondestructive evaluation of fatigue damage in PMR-15 resin

NASA Astrophysics Data System (ADS)

Welter, J. T.; Sathish, S.; Tandon, G. P.; Schehl, N.; Cherry, M.; Nalladega, V.; Lindgren, E. A.; Hall, R.

2012-05-01

Thermoset polyimide resins are used as the polymer matrix in high temperature composites for aerospace applications such as engine shrouds. At these locations the components have to withstand high temperatures and significant vibration. A number of studies have investigated the effects of thermal exposure on mechanical properties of polyimide resins, and the effects of fatigue on thermoplastics have been discussed at length. However, the effects of fatigue on thermosets, in particular polyimides, have largely been overlooked. In this paper we present studies of nondestructive evaluation of fatigue damage in a thermoset polyimide resin, PMR-15, performed by measuring the changes in the evolution of heat in the samples during cyclic loading. The temperature changes are measured using a high sensitivity IR camera as a function of number of fatigue cycles. Interrupted fatigue tests were performed on four samples. The temperature rise during an increment of fatigue cycling shows two linear regions each with a different slope (region 1 and region 2). Region 1 remains constant for every increment of fatigue, while region 2 increases. The onset of region 2 occurs at the same increase in temperature due to hysteretic heating for all samples. Experimental observations are explained using a phenomenological two phase model based on crosslinking density variations in observed in other thermoset resins at microscopic scales. The results of these experiments are discussed in reference to utilizing this technique for detection and evaluation of fatigue in PMR-15 resin and composites.
The effect of manufacturing conditions on discontinuity population and fatigue fracture behavior in carbon/epoxy composites

NASA Astrophysics Data System (ADS)

Hakim, Issa; Laquai, Rene; Walter, David; Mueller, Bernd; Graja, Paul; Meyendorf, Norbert; Donaldson, Steven

2017-02-01

Carbon fiber composites have been increasingly used in aerospace, military, sports, automotive and other fields due to their excellent properties, including high specific strength, high specific modulus, corrosion resistance, fatigue resistance, and low thermal expansion coefficient. Interlaminar fracture is a serious failure mode leading to a loss in composite stiffness and strength. Discontinuities formed during manufacturing process degrade the fatigue life and interlaminar fracture resistance of the composite. In his study, three approaches were implemented and their results were correlated to quantify discontinuities effecting static and fatigue interlaminar fracture behavior of carbon fiber composites. Samples were fabricated by hand layup vacuum bagging manufacturing process under three different vacuum levels, indicated High (-686 mmHg), Moderate (-330 mmHg) and Poor (0 mmHg). Discontinuity content was quantified through-thickness by destructive and nondestructive techniques. Eight different NDE methods were conducted including imaging NDE methods: X-Ray laminography, ultrasonic, high frequency eddy current, pulse thermography, pulse phase thermography and lock-in-thermography, and averaging NDE techniques: X-Ray refraction and thermal conductivity measurements. Samples were subsequently destructively serial sectioned through-thickness into several layers. Both static and fatigue interlaminar fracture behavior under Mode I were conducted. The results of several imaging NDE methods revealed the trend in percentages of discontinuity. However, the results of averaging NDE methods showed a clear correlation since they gave specific values of discontinuity through-thickness. Serial sectioning exposed the composite's internal structure and provided a very clear idea about the type, shape, size, distribution and location of most discontinuities included. The results of mechanical testing showed that discontinuities lead to a decrease in Mode I static interlaminar fracture toughness and a decrease in Mode I cyclic strain energy release rates fatigue life. Finally, all approaches were correlated: the resulted NDE percentages and parameters were correlated with the features revealed by the destructive test of serial sectioning and static and fatigue values in order to quantify discontinuities such as delamination and voids.
Experimental investigation of fatigue behavior of carbon fiber composites using fully-reversed four-point bending test

NASA Astrophysics Data System (ADS)

Amiri, Ali

Carbon fiber reinforced polymers (CFRP) have become an increasingly notable material for use in structural engineering applications. Some of their advantages include high strength-to-weight ratio, high stiffness-to-weight ratio, and good moldability. Prediction of the fatigue life of composite laminates has been the subject of various studies due to the cyclic loading experienced in many applications. Both theoretical studies and experimental tests have been performed to estimate the endurance limit and fatigue life of composite plates. One of the main methods to predict fatigue life is the four-point bending test. In most previous works, the tests have been done in one direction (load ratio, R, > 0). In the current work, we have designed and manufactured a special fixture to perform a fully reversed bending test (R = -1). Static four-point bending tests were carried out on three (0°/90°)15 and (± 45°)15 samples to measure the mechanical properties of CFRP. Testing was displacement-controlled at the rate of 10 mm/min until failure. In (0°/90°)15 samples, all failed by cracking/buckling on the compressive side of the sample. While in (± 45°)15 all three tests, no visual fracture or failure of the samples was observed. 3.4 times higher stresses were reached during four-point static bending test of (0° /90°)15 samples compared to (± 45°)15. Same trend was seen in literature for similar tests. Four-point bending fatigue tests were carried out on (0° /90°)15 sample with stress ratio, R = -1 and frequency of 5 Hz. Applied maximum stresses were approximately 45%, 56%, 67%, 72% and 76% of the measured yield stress for (0° /90°)15 samples. There was visible cracking through the thickness of the samples. The expected downward trend in fatigue life with increasing maximum applied stress was observed in S-N curves of samples. There appears to be a threshold for ‘infinite’ life, defined as 1.7 million cycles in the current work, at a maximum stress of about 200 MPa. The decay in flexural modulus of the beam as it goes under cyclic loading was calculated and it was seen that flexural modulus shows an exponential decay which can be expressed as: E = E0e AN. Four-point bending fatigue tests were carried out on three (±45°)15 samples with stress ratio, R = -1 and frequency of 5 Hz. Maximum applied stress was 85% of the measured yield stress of (±45°)15 samples. None of the samples failed, nor any sign of crack was seen. Tests were stopped once the number of cycles passed 1.7×106. In general, current study provided additional insight into the fatigue and static behavior of polymer composites and effect of fiber orientation in their mechanical behavior.
Fatigue behavior of a 2XXX series aluminum alloy reinforced with 15 vol Pct SiCp

NASA Astrophysics Data System (ADS)

Bonnen, J. J.; Allison, J. E.; Jones, J. W.

1991-05-01

The fatigue behavior of a naturally aged powder metallurgy 2xxx series aluminum alloy (Alcoa MB85) and a composite made of this alloy with 15 vol pct SiCp, has been investigated. Fatigue lives were determined using load-controlled axial testing of unnotched cylindrical samples. The influence of mean stress was determined at stress ratios of -1, 0.1, and 0.7. Mean stress had a significant influence on fatigue life, and this influence was consistent with that normally observed in metals. At each stress ratio, the incorporation of SiC reinforcement led to an increase in fatigue life at low and intermediate stresses. When considered on a strain-life basis, however, the composite materials had a somewhat inferior resistance to fatigue. Fatigue cracks initiated from several different microstructural features or defect types, but fatigue life did not vary significantly with the specific initiation site. As the fatigue crack advanced away from the fatigue crack initiation site, increasing numbers of SiC particles were fractured, in agreement with crack-tip process zone models.
High-Cycle, Push-Pull Fatigue Fracture Behavior of High-C, Si-Al-Rich Nanostructured Bainite Steel.

PubMed

Zhao, Jing; Ji, Honghong; Wang, Tiansheng

2017-12-29

The high-cycle, push-pull fatigue fracture behavior of high-C, Si-Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push-pull fatigue limits at 10⁷ cycles were estimated as 710-889 MPa, for the samples isothermally transformed at the temperature range of 220-260 °C through data extrapolation, measured under the maximum cycle number of 10⁵. Both the interior inclusion and the sample surface constituted the fatigue crack origins. During the fatigue crack propagation, a high amount of secondary cracks were formed in almost parallel arrangements. The apparent plastic deformation occurred in the fracture surface layer, which induced approximately all retained austenite to transform into martensite.
High-Cycle, Push–Pull Fatigue Fracture Behavior of High-C, Si–Al-Rich Nanostructured Bainite Steel

PubMed Central

Zhao, Jing; Ji, Honghong

2017-01-01

The high-cycle, push–pull fatigue fracture behavior of high-C, Si–Al-rich nanostructured bainitic steel was studied through the measurement of fatigue limits, a morphology examination and phase composition analysis of the fatigue fracture surface, as well as fractography of the fatigue crack propagation. The results demonstrated that the push–pull fatigue limits at 107 cycles were estimated as 710–889 MPa, for the samples isothermally transformed at the temperature range of 220–260 °C through data extrapolation, measured under the maximum cycle number of 105. Both the interior inclusion and the sample surface constituted the fatigue crack origins. During the fatigue crack propagation, a high amount of secondary cracks were formed in almost parallel arrangements. The apparent plastic deformation occurred in the fracture surface layer, which induced approximately all retained austenite to transform into martensite. PMID:29286325
Impact and residual fatigue behavior of ARALL and AS6/5245 composite material

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1989-01-01

The impact sensitivity of aramide fiber-reinforced aluminum laminates (ARALL) was investigated by testing two types of ARALL (7075 aluminum prestrained and 2024 aluminum not prestrained), via static indentation, and the results were compared to those of sheet aluminum alloys 7075-T6 and 2024-T3 and to a state of the art composite AS6/5245. It was found that the impact resistance of the two ARALL samples was inferior to that of monolithic sheet aluminum samples, although the ARALL material made with 2024-T3 aluminum was superior to that made with 7075-T6 aluminum. The impact damage resistance of ARALL materials was at least equal to that of AS6/5245, and the AS6/5245 had higher residual tension-tension fatigue strength after impact than the ARALL samples. It was also found that the prestraining of the ARALL reduced the fatigue growth of impact damage.
Effect of Forging Parameters on Low Cycle Fatigue Behaviour of Al/Basalt Short Fiber Metal Matrix Composites

PubMed Central

Karthigeyan, R.; Ranganath, G.

2013-01-01

This paper deals with metal matrix composites (MMCs) of Al 7075 alloy containing different weight percentage (2.5, 5, 7.5, and 10) basalt short fiber reinforcement and unreinforced matrix alloy. The samples were produced by the permanent stir casting technique. The casting ingots were cut into blanks to be forged in single stage and double stage, using MN press and graphite-based lubricant. The microstructures and fatigue properties of the matrix alloy and MMC samples were investigated in the as cast state and in the single and double stage forging operations. The microstructure results showed that the forged sample had a uniform distribution of the basalt short fiber throughout the specimens. Evaluation of the fatigue properties showed that the forged samples had higher values than those of the as cast counterparts. After forging, the enhancement of the fatigue strength of the matrix alloy was so significant and high in the case of 2.5 and 5.0 wt. percentage basalt short fiber reinforced MMC, and there was no enhancement in 7.5 and 10 weight percentages short fiber reinforced MMCs. The fracture damage was mainly due to decohesion at the matrix-fiber interface. PMID:24298207
Effect of forging parameters on low cycle fatigue behaviour of Al/basalt short fiber metal matrix composites.

PubMed

Karthigeyan, R; Ranganath, G

2013-01-01

This paper deals with metal matrix composites (MMCs) of Al 7075 alloy containing different weight percentage (2.5, 5, 7.5, and 10) basalt short fiber reinforcement and unreinforced matrix alloy. The samples were produced by the permanent stir casting technique. The casting ingots were cut into blanks to be forged in single stage and double stage, using MN press and graphite-based lubricant. The microstructures and fatigue properties of the matrix alloy and MMC samples were investigated in the as cast state and in the single and double stage forging operations. The microstructure results showed that the forged sample had a uniform distribution of the basalt short fiber throughout the specimens. Evaluation of the fatigue properties showed that the forged samples had higher values than those of the as cast counterparts. After forging, the enhancement of the fatigue strength of the matrix alloy was so significant and high in the case of 2.5 and 5.0 wt. percentage basalt short fiber reinforced MMC, and there was no enhancement in 7.5 and 10 weight percentages short fiber reinforced MMCs. The fracture damage was mainly due to decohesion at the matrix-fiber interface.
Scanning and Transmission Electron Microscopy of High Temperature Materials

NASA Technical Reports Server (NTRS)

1994-01-01

Software and hardware updates to further extend the capability of the electron microscope were carried out. A range of materials such as intermetallics, metal-matrix composites, ceramic-matrix composites, ceramics and intermetallic compounds, based on refractory elements were examined under this research. Crystal structure, size, shape and volume fraction distribution of various phases which constitute the microstructures were examined. Deformed materials were studied to understand the effect of interfacial microstructure on the deformation and fracture behavior of these materials. Specimens tested for a range of mechanical property requirements, such as stress rupture, creep, low cycle fatigue, high cycle fatigue, thermomechanical fatigue, etc. were examined. Microstructural and microchemical stability of these materials exposed to simulated operating environments were investigated. The EOIM Shuttle post-flight samples were also examined to understand the influence of low gravity processing on microstructure. In addition, fractographic analyses of Nb-Zr-W, titanium aluminide, molybdenum silicide and silicon carbide samples were carried out. Extensive characterization of sapphire fibers in the fiber-reinforced composites made by powder cloth processing was made. Finally, pressure infiltration casting of metal-matrix composites was carried out.
Lamb Wave Assessment of Fatigue and Thermal Damage in Composites

NASA Technical Reports Server (NTRS)

Seale, Michael D.; Smith, Barry T.; Prosser, W. H.

2004-01-01

Among the various techniques available, ultrasonic Lamb waves offer a convenient method of evaluating composite materials. Since the Lamb wave velocity depends on the elastic properties of a structure, an effective tool exists to monitor damage in composites by measuring the velocity of these waves. Lamb wave measurements can propagate over long distances and are sensitive to the desired in-plane elastic properties of the material. This paper describes two studies which monitor fatigue damage and two studies which monitor thermal damage in composites using Lamb waves. In the fatigue studies, the Lamb wave velocity is compared to modulus measurements obtained using strain gage measurements in the first experiment and the velocity is monitored along with the crack density in the second. In the thermal damage studies, one examines samples which were exposed to varying temperatures for a three minute duration and the second includes rapid thermal damage in composites by intense laser beams. In all studies, the Lamb wave velocity is demonstrated to be an excellent method to monitor damage in composites.
Role of point defects in bipolar fatigue behavior of Bi(Mg{sub 1/2}Ti{sub 1/2})O{sub 3} modified (Bi{sub 1/2}K{sub 1/2})TiO{sub 3}-(Bi{sub 1/2}Na{sub 1/2})TiO{sub 3} relaxor ceramics

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kumar, Nitish, E-mail: nitishkumar.iitk@gmail.com; Ansell, Troy Y.; Cann, David P.

Lead-free Bi(Mg{sub 1/2}Ti{sub 1/2})O{sub 3}-(Bi{sub 1/2}K{sub 1/2})TiO{sub 3}-(Bi{sub 1/2}Na{sub 1/2})TiO{sub 3} (BMT-BKT-BNT) ceramics have been shown to exhibit large electromechanical strains under high electric fields along with negligible fatigue under strong electric fields. To investigate the role of point defects on the fatigue characteristics, the composition 5BMT-40BKT-55BNT was doped to incorporate acceptor and donor defects on the A and B sites by adjusting the Bi/Na and Ti/Mg stoichiometries. All samples had pseudo-cubic symmetries based on x-ray diffraction, typical of relaxors. Dielectric measurements showed that the high and low temperature phase transitions were largely unaffected by doping. Acceptor doping resulted inmore » the observation of a typical ferroelectric-like polarization with a remnant polarization and strain hysteresis loops with significant negative strain. Donor-doped compositions exhibited characteristics that were indicative of an ergodic relaxor phase. Fatigue measurements were carried out on all of the compositions. While the A-site acceptor-doped composition showed a small degradation in maximum strain after 10{sup 6} cycles, the other compositions were essentially fatigue free. Impedance measurements were used to identify the important conduction mechanisms in these compositions. As expected, the presence of defects did not strongly influence the fatigue behavior in donor-doped compositions owing to the nature of their reversible field-induced phase transformation. Even for the acceptor-doped compositions, which had stable domains in the absence of an electric field at room temperature, there was negligible degradation in the maximum strain due to fatigue. This suggests that either the defects introduced through stoichiometric variations do not play a prominent role in fatigue in these systems or it is compensated by factors like decrease in coercive field, an increase in ergodicity, symmetry change, or other factors.« less
Association between poor sleep, fatigue, and safety outcomes in Emergency Medical Services providers

PubMed Central

Patterson, P. Daniel; Weaver, Matthew D.; Frank, Rachel C.; Warner, Charles W.; Martin-Gill, Christian; Guyette, Francis X.; Fairbanks, Rollin J.; Hubble, Michael W.; Songer, Thomas J.; Callaway, Clifton W.; Kelsey, Sheryl F.; Hostler, David

2011-01-01

Objective To determine the association between poor sleep quality, fatigue, and self-reported safety outcomes among Emergency Medical Services (EMS) workers. Methods We used convenience sampling of EMS agencies and a cross-sectional survey design. We administered the 19-item Pittsburgh Sleep Quality Index (PSQI), 11-item Chalder Fatigue Questionnaire (CFQ), and 44-item EMS Safety Inventory (EMS-SI) to measure sleep quality, fatigue, and safety outcomes, respectively. We used a consensus process to develop the EMS-SI, which was designed to capture three composite measurements of EMS worker injury, medical errors and adverse events (AE), and safety compromising behaviors. We used hierarchical logistic regression to test the association between poor sleep quality, fatigue, and three composite measures of EMS worker safety outcomes. Results We received 547 surveys from 30 EMS agencies (a 35.6% mean agency response rate). The mean PSQI score exceeded the benchmark for poor sleep (6.9, 95%CI 6.6, 7.2). Greater than half of respondents were classified as fatigued (55%, 95%CI 50.7, 59.3). Eighteen percent of respondents reported an injury (17.8%, 95%CI 13.5, 22.1), forty-one percent a medical error or AE (41.1%, 95%CI 36.8, 45.4), and 89% (95%CI 87, 92) safety compromising behaviors. After controlling for confounding, we identified 1.9 greater odds of injury (95%CI 1.1, 3.3), 2.2 greater odds of medical error or AE (95%CI 1.4, 3.3), and 3.6 greater odds of safety compromising behavior (95%CI 1.5, 8.3) among fatigued respondents versus non-fatigued respondents. Conclusions In this sample of EMS workers, poor sleep quality and fatigue is common. We provide preliminary evidence of an association between sleep quality, fatigue, and safety outcomes. PMID:22023164
PMMA-hydroxyapatite composite material retards fatigue failure of augmented bone compared to augmentation with plain PMMA: in vivo study using a sheep model.

PubMed

Arabmotlagh, Mohammad; Bachmaier, Samuel; Geiger, Florian; Rauschmann, Michael

2014-11-01

Polymethylmethacrylate (PMMA) is the most commonly used void filler for augmentation of osteoporotic vertebral fracture, but the differing mechanical features of PMMA and osteoporotic bone result in overload and failure of adjacent bone. The aim of this study was to compare fatigue failure of bone after augmentation with PMMA-nanocrystalline hydroxyapatite (HA) composite material or with plain PMMA in a sheep model. After characterization of the mechanical properties of a composite material consisting of PMMA and defined amounts (10, 20, and 30% volume fraction) of HA, the composite material with 30% volume fraction HA was implanted in one distal femur of sheep; plain PMMA was implanted in the other femur. Native non-augmented bone served as control. Three and 6 months after implantation, the augmented bone samples were exposed to cyclic loading and the evolution of damage was investigated. The fatigue life was highest for the ovine native bone and lowest for bone-PMMA specimens. Bone-composite specimens showed significantly higher fatigue life than the respective bone-PMMA specimens in both 3- and 6-month follow-up groups. These results suggest that modification of mechanical properties of PMMA by addition of HA to approximate those of cancellous bone retards fatigue failure of the surrounding bone compared to augmented bone with plain PMMA. © 2014 Wiley Periodicals, Inc.
Nondestructive evaluation of loading and fatigue effects in Haynes(R) 230(R) alloy

NASA Astrophysics Data System (ADS)

Saleh, Tarik Adel

Nondestructive evaluation is a useful method for studying the effects of deformation and fatigue. In this dissertation I employed neutron and X-ray diffraction, nonlinear resonant ultrasound spectroscopy (NRUS), and infrared thermography to study the effects of deformation and fatigue on two different nickel based superalloys. The alloys studied were HAYNES 230, a solid solution strengthened alloy with 4% M6C carbides, and secondarily HASTELLOY C-2000 a similar single phase alloy. Using neutron and X-ray diffraction, the deformation behavior of HAYNES 230 was revealed to be composite-like during compression, but unusual in tension, where the carbides provide strengthening until just after the macroscopic yield strength and then they begin to debond and crack, creating a tension-compression asymmetry that is revealed clearly by in situ diffraction. In fatigue of HAYNES 230, the hkl elastic strains changed very little in tension-tension fatigue. However, in situ tension-compression studies showed large changes over the initial stages of fatigue. The HAYNES 230 samples studies had two distinct starting textures, measured by neutron diffraction. Some samples were texture free initially and deformed in tension and compression to fiber textures. Other samples started with a bimodal texture due to cross-rolling and incomplete annealing. The final texture of these bimodal samples is shown through modeling to be a superposition of the initial texture and typical FCC deformation mechanisms. The texture-free samples deformed significantly more macroscopically and in internal elastic strains than the samples with the cross-rolled texture. In contrast to the relative insensitivity of neutron diffraction to the effects of tension-tension fatigue, NRUS revealed large differences between as-received and progressively fatigued samples. This showed that microcracking and void formation are the primary mechanisms responsible for fatigue damage in tension-tension fatigue. NRUS is shown to be a useful complimentary technique to neutron diffraction to evaluate fatigue damage. Finally, infrared thermography is used to show temperature changes over the course of fatigue in HASTELLOY C-2000. Four stages of temperature are shown over the course of a single fatigue test. Both empirical and theoretical relationships between steady state temperature and fatigue life are developed and presented.
Monitoring the fracture behavior of metal matrix composites by combined NDE methodologies

NASA Astrophysics Data System (ADS)

Kordatos, E. Z.; Exarchos, D. A.; Mpalaskas, A. C.; Matikas, T. E.

2015-03-01

Current work deals with the non-destructive evaluation (NDE) of the fatigue behavior of metal matrix composites (MMCs) materials using Infrared Thermography (IRT) and Acoustic Emission (AE). AE monitoring was employed to record a wide spectrum of cracking events enabling the characterization of the severity of fracture in relation to the applied load. IR thermography as a non-destructive, real-time and non-contact technique, allows the detection of heat waves generated by the thermo-mechanical coupling during mechanical loading of the sample. In this study an IR methodology, based on the monitoring of the intrinsically dissipated energy, was applied for the determination of the fatigue limit of A359/SiCp composites. The thermographic monitoring is in agreement with the AE results enabling the reliable monitoring of the MMCs' fatigue behavior.

Static and Fatigue Strength Evaluations for Bolted Composite/Steel Joints for Heavy Vehicle Chassis Components

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sun, Xin; Stephens, Elizabeth V.; Herling, Darrell R.

2004-09-14

In May 2003, ORNL and PNNL began collaboration on a four year research effort focused on developing joining techniques to overcome the technical issues associated with joining lightweight materials in heavy vehicles. The initial focus of research is the development and validation of joint designs for a composite structural member attached to a metal member that satisfy the structural requirements both economically and reliably. Huck-bolting is a common joining method currently used in heavy truck chassis structures. The initial round of testing was conducted to establish a performance benchmark by evaluating the static and fatigue behavior of an existing steel/steelmore » chassis joint at the single huck-bolt level. Both tension and shear loading conditions were considered, and the resulting static and fatigue strengths will be used to guide the joint design for a replacement composite/steel joint. A commercially available, pultruded composite material was chosen to study the generic issues related to composite/steel joints. Extren is produced by STRONGWELL, and it is a combination of fiberglass reinforcement and thermosetting polyester or vinyl ester resin systems. Extren sheets of 3.2 mm thick were joined to 1.4 mm SAE1008 steel sheets with a standard grade 5 bolt with 6.35 mm diameter. Both tension and shear loading modes were considered for the single hybrid joint under static and fatigue loading conditions. Since fiberglass reinforced thermoset polymer composites are a non-homogenous material, their strengths and behavior are dependent upon the design of the composite and reinforcement. The Extren sheet stock was cut along the longitudinal direction to achieve maximum net-section strength. The effects of various manufacturing factors and operational conditions on the static and fatigue strength of the hybrid joint were modeled and experimentally verified. It was found that loading mode and washer size have significant influence on the static and fatigue strength of the hybrid joint. The effect of different fatigue test frequencies on the sample temperature and the resulting fatigue life was also examined.« less
Simulated Data for High Temperature Composite Design

NASA Technical Reports Server (NTRS)

Chamis, Christos C.; Abumeri, Galib H.

2006-01-01

The paper describes an effective formal method that can be used to simulate design properties for composites that is inclusive of all the effects that influence those properties. This effective simulation method is integrated computer codes that include composite micromechanics, composite macromechanics, laminate theory, structural analysis, and multi-factor interaction model. Demonstration of the method includes sample examples for static, thermal, and fracture reliability for a unidirectional metal matrix composite as well as rupture strength and fatigue strength for a high temperature super alloy. Typical results obtained for a unidirectional composite show that the thermal properties are more sensitive to internal local damage, the longitudinal properties degrade slowly with temperature, the transverse and shear properties degrade rapidly with temperature as do rupture strength and fatigue strength for super alloys.
Fatigue of Self-Healing Nanofiber-based Composites: Static Test and Subcritical Crack Propagation.

PubMed

Lee, Min Wook; Sett, Soumyadip; Yoon, Sam S; Yarin, Alexander L

2016-07-20

Here, we studied the self-healing of composite materials filled with epoxy-containing nanofibers. An initial incision in the middle of a composite sample stretched in a static fatigue test can result in either crack propagation or healing. In this study, crack evolution was observed in real time. A binary epoxy, which acted as a self-healing agent, was encapsulated in two separate types of interwoven nano/microfibers formed by dual-solution blowing, with the core containing either epoxy or hardener and the shell being formed from poly(vinylidene fluoride)/ poly(ethylene oxide) mixture. The core-shell fibers were encased in a poly(dimethylsiloxane) matrix. When the fibers were damaged by a growing crack in this fiber-reinforced composite material because of static stretching in the fatigue test, they broke and released the healing agent into the crack area. The epoxy used in this study was cured and solidified for approximately an hour at room temperature, which then conglutinated and healed the damaged location. The observations were made for at least several hours and in some cases up to several days. It was revealed that the presence of the healing agent (the epoxy) in the fibers successfully prevented the propagation of cracks in stretched samples subjected to the fatigue test. A theoretical analysis of subcritical cracks was performed, and it revealed a jumplike growth of subcritical cracks, which was in qualitative agreement with the experimental results.
Sonic Fatigue Design Techniques for Advanced Composite Aircraft Structures

DTIC Science & Technology

1980-04-01

AFWAL-TR-80.3019 AD A 090553 SONIC FATIGUE DESIGN TECHNIQUES FOR ADVANCED COMPOSITE AIRCRAFT STRUCTURES FINAL REPORT Ian Holehouse Rohr Industries...5 2. General Sonic Fatigue Theory .... ....... 7 3. Composite Laminate Analysis .. ....... ... 10 4. Preliminary Sonic Fatigue...overall sonic fatigue design guides. These existing desiyn methcds have been developed for metal structures. However, recent advanced composite
Microtomography evaluation of dental tissue wear surface induced by in vitro simulated chewing cycles on human and composite teeth.

PubMed

Bedini, Rossella; Pecci, Raffaella; Notarangelo, Gianluca; Zuppante, Francesca; Persico, Salvatore; Di Carlo, Fabio

2012-01-01

In this study a 3D microtomography display of tooth surfaces after in vitro dental wear tests has been obtained. Natural teeth have been compared with prosthetic teeth, manufactured by three different polyceramic composite materials. The prosthetic dental element samples, similar to molars, have been placed in opposition to human teeth extracted by paradontology diseases. After microtomography analysis, samples have been subjected to in vitro fatigue test cycles by servo-hydraulic mechanical testing machine. After the fatigue test, each sample has been subjected again to microtomography analysis to obtain volumetric value changes and dental wear surface images. Wear surface images were obtained by 3D reconstruction software and volumetric value changes were measured by CT analyser software. The aim of this work has been to show the potential of microtomography technique to display very clear and reliable wear surface images. Microtomography analysis methods to evaluate volumetric value changes have been used to quantify dental tissue and composite material wear.
A procedure for utilization of a damage-dependent constitutive model for laminated composites

NASA Technical Reports Server (NTRS)

Lo, David C.; Allen, David H.; Harris, Charles E.

1992-01-01

Described here is the procedure for utilizing a damage constitutive model to predict progressive damage growth in laminated composites. In this model, the effects of the internal damage are represented by strain-like second order tensorial damage variables and enter the analysis through damage dependent ply level and laminate level constitutive equations. The growth of matrix cracks due to fatigue loading is predicted by an experimentally based damage evolutionary relationship. This model is incorporated into a computer code called FLAMSTR. This code is capable of predicting the constitutive response and matrix crack damage accumulation in fatigue loaded laminated composites. The structure and usage of FLAMSTR are presented along with sample input and output files to assist the code user. As an example problem, an analysis of crossply laminates subjected to two stage fatigue loading was conducted and the resulting damage accumulation and stress redistribution were examined to determine the effect of variations in fatigue load amplitude applied during the first stage of the load history. It was found that the model predicts a significant loading history effect on damage evolution.
High temperature tension-compression fatigue behavior of a tungsten copper composite

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Gabb, Timothy P.

1990-01-01

The high temperature fatigue of a (O)12 tungsten fiber reinforced copper matrix composite was investigated. Specimens having fiber volume percentages of 10 and 36 were fatigued under fully-reversed, strain-controlled conditions at both 260 and 560 C. The fatigue life was found to be independent of fiber volume fraction because fatigue damage preferentially occurred in the matrix. Also, the composite fatigue lives were shorter at 560 C as compared to 260 C due to changes in mode of matrix failure. On a total strain basis, the fatigue life of the composite at 560 C was the same as the life of unreinforced copper, indicating that the presence of the fibers did not degrade the fatigue resistance of the copper matrix in this composite system. Comparison of strain-controlled fatigue data to previously-generated load-controlled data revealed that the strain-controlled fatigue lives were longer because of mean strain and mean stress effects.
Effect of phase lag on cyclic durability of laminated composite

NASA Astrophysics Data System (ADS)

Andersons, Janis; Limonov, V.; Tamuzs, Vitants

1992-07-01

Theoretical and experimental results on fatigue of laminated fiber reinforced composites under out-of-phase, biaxial cyclic loading are presented. Experiments were carried out on tubular filament wound samples of epoxy matrix/organic (Kevlar type) fiber composites. Fatigue strength under two different loading modes, namely cyclic torsion combined with axial tension or compression, was investigated for phase lags psi = 0, pi/2, and pi. Durability was shown to decrease with increasing phase shift both for axial tension (R = 0.1) and compression (R = 10). A matrix failure criterion was proposed for a unidirectionally reinforced ply, and the ply discount method was modified to account for phase lag. Calculated S-N curves agree reasonably well with experimental data.
Isothermal life prediction of composite lamina using a damage mechanics approach

NASA Technical Reports Server (NTRS)

Abuelfoutouh, Nader M.; Verrilli, Michael J.; Halford, Gary R.

1989-01-01

A method for predicting isothermal plastic fatigue life of a composite lamina is presented in which both fibers and matrix are isotropic materials. In general, the fatigue resistances of the matrix, fibers, and interfacial material must be known in order to predict composite fatigue life. Composite fatigue life is predicted using only the matrix fatigue resistance due to inelasticity micromechanisms. The effect of the fiber orientation on loading direction is accounted for while predicting composite life. The application is currently limited to isothermal cases where the internal thermal stresses that might arise from thermal strain mismatch between fibers and matrix are negligible. The theory is formulated to predict the fatigue life of a composite lamina under either load or strain control. It is applied currently to predict the life of tungsten-copper composite lamina at 260 C under tension-tension load control. The calculated life of the lamina is in good agreement with available composite low cycle fatigue data.
Open hole and postimpact compressive fatigue of stitched and unstitched carbon-epoxy composites

NASA Technical Reports Server (NTRS)

Portanova, Marc A.; Poe, Clarence C.; Whitcomb, John D.

1992-01-01

The performance is studied of a stitched uniweave fabric composite and that of a toughened tape composite. The effects of stitching on compression fatigue life are addressed. Post impact compression fatigue and open hole fatigue tests were run on an AS4/3501-6 uniweave with stitching and a toughened IM7/8551-7 tape without stitching. Stitching was found to increase the thickness and consequently the weight of the composite material. The two materials were compared on an equal carbon content basis as well as on an equal weight basis. The excess thickness in the stitched uniweave composite was responsible for the lower fatigue life, on an equal carbon basis, compared to the toughened resin tape composite. Comparison of fatigue lives on an equal carbon content basis indicated that puncture or crimp type damage from stitching has very little effect on compression failure. Post impact fatigue test showed that although the damage area in the stitched uniweave composite was twice that of the toughened tape composite, the fatigue lives of the stitched composite were significantly longer than those of the toughened composite. Thus, it appears that the increase in thickness from stitching is much more of a penalty than crimped fibers or puncture type damage from stitching.
Open hole and post-impact compression fatigue of stitched and unstitched carbon/epoxy composites

NASA Technical Reports Server (NTRS)

Portanova, M. A.; Poe, C. C., Jr.; Whitcomb, John D.

1990-01-01

The performance is studied of a stitched uniweave fabric composite and that of a toughened tape composite. The effects of stitching on compression fatigue life are addressed. Post impact compression fatigue and open hole fatigue tests were run on an AS4/3501-6 uniweave with stitching and a toughened IM7/8551-7 tape without stitching. Stitching was found to increase the thickness and consequently the weight of the composite material. The two materials were compared on an equal carbon content basis as well as on an equal weight basis. The excess thickness in the stitched uniweave composite was responsible for the lower fatigue life, on an equal carbon basis, compared to the toughened resin tape composite. Comparison of fatigue lives on an equal carbon content basis indicated that puncture or crimp type damage from stitching has very little effect on compression failure. Post impact fatigue test showed that although the damage area in the stitched uniweave composite was twice that of the toughened tape composite, the fatigue lives of the stitched composite were significantly longer than those of the toughened composite. Thus, it appears that the increase in thickness from stitching is much more of a penalty than crimped fibers or puncture type damage from stitching.
Effect of Spring-in Deviation on Fatigue Life of Composite Elevator Assembly

NASA Astrophysics Data System (ADS)

Wang, Hua

2017-12-01

The spring-in deviation results in the extra stresses around the joints of the composite C-beam and metallic parts when they are assembled together. These extra stresses affect the composite elevator's fatigue life, which should be explored with the fatigue experimentation. The paper presents the experimental investigation on the effect of spring-in deviation on the fatigue life of the composite elevator assembly. The investigation seeks to build the relationship between the spring-in and the fatigue life in order to determine the spring-in threshold during the course of assembling. The phenomenological model of the composite C-beam is constructed to predict the stresses around the joints. Based on the predicted spring-in induced stresses around the joints, pre-stresses are precisely added to the fatigue specimen when conducting the fatigue experiment. At last, the relationship curve of the spring-in on the composite C-beam's fatigue life is obtained from the experimental data. Giving the fatigue life accepting limits, the maximum accepting spring-in deviation during the course of assembling could be obtained from the relationship curve. The reported work will enhance the understanding of assembling the composites with spring-in deviation in the civil aircraft industry.
Fatigue Damage and Lifetime of SiC/SiC Ceramic-Matrix Composite under Cyclic Loading at Elevated Temperatures

PubMed Central

Li, Longbiao

2017-01-01

In this paper, the fatigue damage and lifetime of 2D SiC/SiC ceramic-matrix composites (CMCs) under cyclic fatigue loading at 750, 1000, 1100, 1200 and 1300 °C in air and in steam atmosphere have been investigated. The damage evolution versus applied cycles of 2D SiC/SiC composites were analyzed using fatigue hysteresis dissipated energy, fatigue hysteresis modulus, fatigue peak strain and interface shear stress. The presence of steam accelerated the damage development inside of SiC/SiC composites, which increased the increasing rate of the fatigue hysteresis dissipated energy and the fatigue peak strain, and the decreasing rate of the fatigue hysteresis modulus and the interface shear stress. The fatigue life stress-cycle (S-N) curves and fatigue limit stresses of 2D SiC/SiC composites at different temperatures in air and in steam condition have been predicted. The fatigue limit stresses approach 67%, 28%, 39% 17% and 28% tensile strength at 750, 1000, 1100, 1200 and 1300 °C in air, and 49%, 10%, 9% and 19% tensile strength at 750, 1000, 1200 and 1300 °C in steam conditions, respectively. PMID:28772736
Self-healing fiber-reinforced composite

NASA Astrophysics Data System (ADS)

Lee, Minwook; Yoon, Sam; Yarin, Alexander

In the present work two parts of the healing agent (commercially available epoxy resin and hardener) are encapsulated in separate polymeric nanofibers. The fibers are generated by a single-step dual coaxial solution blowing. The core-shell fibers with the diameters in the 200-2600 nm range are encased in the PDMS (polydimethyl siloxane) matrix to form a self-healing composite material. Under fatigue conditions, the core-shell fibers inside the composite material are ruptured and the healing agents released into the surrounding matrix. Various fatigue conditions including repeated bending and stretching are used to damage the composites and the degree of self-healing is quantified after that. Also, an incision resembling a crack is pre-notched and crack propagation is studied. It is found that the presence of the self-healing agents in the fibers significantly retards crack propagation due to curing by the epoxy at the ruptured site. The stiffness of the composites is also measured for the samples containing self-healing fibers inside them before and after the fatigue tests. A novel theory of crack propagation is proposed, which explains the observed jump-like growth of sub-critical cracks. This work was supported by the International Collaboration Program funded by the Agency for Defense Development.
Fatigue damage accumulation in various metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1987-01-01

The purpose of this paper is to review some of the latest understanding of the fatigue behavior of continuous fiber reinforced metal matrix composites. The emphasis is on the development of an understanding of different fatigue damage mechanisms and why and how they occur. The fatigue failure modes in continuous fiber reinforced metal matrix composites are controlled by the three constituents of the system: fiber, matrix, and fiber/matrix interface. The relative strains to fatigue failure of the fiber and matrix will determine the failure mode. Several examples of matrix, fiber, and self-similar damage growth dominated fatigue damage are given for several metal matrix composite systems. Composite analysis, failure modes, and damage modeling are discussed. Boron/aluminum, silicon-carbide/aluminum, FP/aluminum, and borsic/titanium metal matrix composites are discussed.
Mechanical Properties - Structure Correlation for Commercial Specification of Cast Particulate Metal Matrix Composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Pradeep Rohatgi

2002-12-31

In this research, the effects of casting foundry, testing laboratory, surface conditions, and casting processes on the mechanical properties of A359-SiC composites were identified. To observe the effects, A359-SiC composites with 20 and 305 SiC particles were cast at three different foundries and tested at three different laboratories. The composites were cast in sand and permanent molds and tested as-cast and machined conditions. To identify the effect of the volume fraction and distribution of particles on the properties of the composites, particle distribution was determined using Clemex Image analysis systems, and particle volume fraction was determined using wet chemical analysismore » and Clemex Image analysis systems. The microstructure and fractured surfaces of the samples were analyzed using SEM, and EDX analysis was done to analyze chemical reaction between the particles and the matrix. The results of the tensile strengths exhibited that the tensile strengths depend on the density and porosity of the composites; in general the higher tensile strength is associated with lower porosity and higher density. In some cases, composites with lower density were higher than these with higher density. In the Al-20% SiC samples, the composites with more inclusions exhibited a lower tensile strength than the ones with fewer inclusions. This suggests that macroscopic casting defects such as micro-porosity, shrinkage porosity and inclusions appear to strongly influence the tensile strength more than the microstructure and particle distribution. The fatigue properties of A359/20 vol.% SiC composites were investigated under strain controlled conditions. Hysteresis loops obtained from strain controlled cyclic loading of 20% SiCp reinforced material did not exhibit any measurable softening or hardening. The fatigue life of Al-20% SiC heat treated alloy at a given total strain showed wide variation in fatigue life, which appeared to be related to factors such as inclusions, porosity, and particle distribution. The inclusions and porosity on the fracture surfaces seem to have a more significant influence on the fatigue life of cast Al-20% SiC as compared to other variables, including SiC particle volume percentage and its distribution. Striations were generally not visible on the fracture surface of the composites. In many specimens, SiC particle fracture was also observed. Fracture was more severe around pores and inclusions than in the matrix away from them. Inclusions and porosity seem to have a much stronger influence on fatigue behavior than the particle distribution. The analysis suggests that the enhancement of fatigue behavior of cast MMCs requires a decrease in the size of defects, porosity, and inclusions. The particle volume fraction determined using wet chemical analysis gives values of SiC vol.% which are closer to the nominal Sic % than the values of SiC% obtained by ultrasonic and Clemex Image Analysis system. In view of ALCAN's recommendation one must use wet chemical analysis for determining the volume percent SiC.« less
Cross-cultural differences in the epidemiology of unexplained fatigue syndromes in primary care.

PubMed

Skapinakis, Petros; Lewis, Glyn; Mavreas, Venetsanos

2003-03-01

Unexplained fatigue has been extensively studied but most of the samples used were from Western countries. To present international data on the prevalence of unexplained fatigue and fatigue as a presenting complaint in primary care. Method Secondary analysis of the World Health Organization study of psychological problems in general health care. A total of 5438 primary care attenders from 14 countries were assessed with the Composite International Diagnostic Interview. The prevalence of unexplained fatigue of 1-month duration differed across centres, with a range between 2.26 (95% CI 1.17-4.33) and 15.05 (95% CI 10.85-20.49). Subjects from more-developed countries were more likely to report unexplained fatigue but less likely to present with fatigue to physicians compared with subjects from less developed countries. In less-developed countries fatigue might be an indicator of unmet psychiatric need, but in more-developed countries it is probably a symbol of psychosocial distress.
Study on Fatigue Performance of Composite Bolted Joints with Bolt-Hole Delamination

NASA Astrophysics Data System (ADS)

Liu, M. J.; Yu, S.; Zhao, Q. Y.

2018-03-01

Fatigue performance of composite structure with imperfections is a challenging subject at present. Based on cohesive zone method and multi-continuum theory, delamination evolution response and fatigue life prediction of a 3D composite single-lap joint with a bolt-hole have been investigated through computer codes Abaqus and Fe-safe. Results from the comparison of a perfect composite bolted joint with another defect one indicates that a relatively small delamination damage around the bolt hole brings about significant degradation of local material performance. More notably, fatigue life of stress concentration region of composite bolted joints is highly sensitive to external loads, as an increase of 67% cyclic load amplitude leads to an decrease of 99.5% local fatigue life in this study. However, the numerical strategy for solving composite fatigue problems is meaningful to engineering works.
Fatigue of cord-rubber composites for tires

NASA Astrophysics Data System (ADS)

Song, Jaehoon

Fatigue behaviors of cord-rubber composite materials forming the belt region of radial pneumatic tires have been characterized to assess their dependence on stress, strain and temperature history as well as materials composition and construction . Using actual tires, it was found that interply shear strain is one of the crucial parameters for damage assessment from the result that higher levels of interply shear strain of actual tires reduce the fatigue lifetime. Estimated at various levels of load amplitude were the fatigue life, the extent and rate of resultant strain increase ("dynamic creep"), cyclic strains at failure, and specimen temperature. The interply shear strain of 2-ply 'tire belt' composite laminate under circumferential tension was affected by twisting of specimen due to tension-bending coupling. However, a critical level of interply shear strain, which governs the gross failure of composite laminate due to the delamination, appeared to be independent of different lay-up of 2-ply vs. symmetric 4-ply configuration. Reflecting their matrix-dominated failure modes such as cord-matrix debonding and delamination, composite laminates with different cord reinforcements showed the same S-N relationship as long as they were constructed with the same rubber matrix, the same cord angle, similar cord volume, and the same ply lay-up. Because of much lower values of single cycle strength (in terms of gross fracture load per unit width), the composite laminates with larger cord angle and the 2-ply laminates exhibited exponentially shorter fatigue lifetime, at a given stress amplitude, than the composite laminates with smaller cord angle and 4-ply symmetric laminates, respectively. The increase of interply rubber thickness lengthens their fatigue lifetime at an intermediate level of stress amplitude. However, the increase in the fatigue lifetime of the composite laminate becomes less noticeable at very low stress amplitude. Even with small compressive cyclic stresses, the fatigue life of belt composites is predominantly influenced by the magnitude of maximum stress. Maximum cyclic strain of composite laminates at failure, which measures the total strain accumulation for gross failure, was independent of stress amplitude and close to the level of static failure strain. For all composite laminates under study, a linear correlation could be established between the temperature rise rate and dynamic creep rate which was, in turn, inversely proportional to the fatigue lifetime. Using the acoustic emission (AE) initiation stress value, better prediction of fatigue life was available for the fiber-reinforced composites having fatigue limit. The accumulation rate of AE activities during cyclic loading was linearly proportional to the maximum applied load and to the inverse of the fatigue life of cord-rubber composite laminates. Finally, a modified fatigue modulus model based on combination of power-law and logarithmic relation was proposed to predict the fatigue lifetime profile of cord-rubber composite laminates.
Fatigue-life behavior and matrix fatigue crack spacing in unnotched SCS-6/Timetal 21S metal matrix composites

NASA Technical Reports Server (NTRS)

Ward, G. T.; Herrmann, D. J.; Hillberry, B. M.

1993-01-01

Fatigue tests of the SCS-6/Timetal 21S composite system were performed to characterize the fatigue behavior for unnotched conditions. The stress-life behavior of the unnotched (9/90)2s laminates was investigated for stress ratios of R = 0.1 and R = 0.3. The occurrence of matrix cracking was also examined in these specimens. This revealed multiple matrix crack initiation sites throughout the composite, as well as evenly spaced surface cracks along the length of the specimens. No difference in fatigue lives were observed for stress ratios of R = 0.1 and R = 0.3 when compared on a stress range basis. The unnotched SCS-6/Timetal 21S composites had shorter fatigue lives than the SCS-6/Ti-15-3 composites, however the neat Timetal 21S matrix material had a longer fatigue life than the neat Ti-15-3.

Comparison of Fatigue Life Between C/SiC and SiC/SiC Ceramic-Matrix Composites at Room and Elevated Temperatures

NASA Astrophysics Data System (ADS)

Longbiao, Li

2016-10-01

In this paper, the comparison of fatigue life between C/SiC and SiC/SiC ceramic-matrix composites (CMCs) at room and elevated temperatures has been investigated. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. Under cyclic fatigue loading, the fibers broken fraction was determined by combining the interface wear model and fibers statistical failure model at room temperature, and interface/fibers oxidation model, interface wear model and fibers statistical failure model at elevated temperatures in the oxidative environments. When the broken fibers fraction approaches to the critical value, the composites fatigue fracture. The fatigue life S-N curves and fatigue limits of cross-ply, 2D and 3D C/SiC and SiC/SiC composites at room temperature, 550 °C in air, 750 °C in dry and humid condition, 800 °C in air, 1000 °C in argon and air, 1100 °C, 1300 °C and 1500 °C in vacuum, have been predicted. At room temperature, the fatigue limit of 2D C/SiC composite with ECFL of 20 % lies between 0.78 and 0.8 tensile strength; and the fatigue limit of 2D SiC/SiC composite with ECFL of 20 % lies between 0.75 and 0.85 tensile strength. The fatigue limit of 2D C/SiC composite increases to 0.83 tensile strength with ECFL increasing from 20 to 22.5 %, and the fatigue limit of 3D C/SiC composite is 0.85 tensile strength with ECFL of 37 %. The fatigue performance of 2D SiC/SiC composite is better than that of 2D C/SiC composite at elevated temperatures in oxidative environment.
77 FR 50576 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures; OMB Approval of...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-08-22

... Composite Rotorcraft Structures; OMB Approval of Information Collection AGENCY: Federal Aviation... requirement contained in the FAA's final rule, ``Damage Tolerance and Fatigue Evaluation of Composite... and Fatigue Evaluation of Composite Rotorcraft Structures,'' published in the Federal Register (76 FR...
Fatigue resistance criteria for fiber-reinforced composite structures. Final report, 1 Apr 1971-30 Sep 1974

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dvorak, G.J.

1974-10-01

The research effort was concentrated on metal matrix composites, such as the Al--B, Al--Be, Cu--W, and similar systems. It was found that in as- fabricated composites with soft matrices fatigue failure can be prevented if the composite shakes down during cyclic loading. The fatigue strength of heat- treated composites is affected by residual microstresses, but failure can be prevented if the total microstresses are kept within the respective fatigue limits (at 10 to the 7th power cycles) of the constituents. These criteria for prevention of fatigue failure in metal matrix composite systems were verified by extensive comparisons of theoretical predictionsmore » with available experimental results. (GRA)« less
Multiscale/Multifunctional Probabilistic Composite Fatigue

NASA Technical Reports Server (NTRS)

Chamis, Christos C.

2010-01-01

A multilevel (multiscale/multifunctional) evaluation is demonstrated by applying it to three different sample problems. These problems include the probabilistic evaluation of a space shuttle main engine blade, an engine rotor and an aircraft wing. The results demonstrate that the blade will fail at the highest probability path, the engine two-stage rotor will fail by fracture at the rim and the aircraft wing will fail at 109 fatigue cycles with a probability of 0.9967.
Statistical characterization of the fatigue behavior of composite lamina

NASA Technical Reports Server (NTRS)

Yang, J. N.; Jones, D. L.

1979-01-01

A theoretical model was developed to predict statistically the effects of constant and variable amplitude fatigue loadings on the residual strength and fatigue life of composite lamina. The parameters in the model were established from the results of a series of static tensile tests and a fatigue scan and a number of verification tests were performed. Abstracts for two other papers on the effect of load sequence on the statistical fatigue of composites are also presented.
Monitoring the Damage State of Fiber Reinforced Composites Using an FBG Network for Failure Prediction.

PubMed

Kocaman, Esat Selim; Akay, Erdem; Yilmaz, Cagatay; Turkmen, Halit Suleyman; Misirlioglu, Ibrahim Burc; Suleman, Afzal; Yildiz, Mehmet

2017-01-03

A structural health monitoring (SHM) study of biaxial glass fibre-reinforced epoxy matrix composites under a constant, high strain uniaxial fatigue loading is performed using fibre Bragg grating (FBG) optical sensors embedded in composites at various locations to monitor the evolution of local strains, thereby understanding the damage mechanisms. Concurrently, the temperature changes of the samples during the fatigue test have also been monitored at the same locations. Close to fracture, significant variations in local temperatures and strains are observed, and it is shown that the variations in temperature and strain can be used to predict imminent fracture. It is noted that the latter information cannot be obtained using external strain gages, which underlines the importance of the tracking of local strains internally.
Monitoring the Damage State of Fiber Reinforced Composites Using an FBG Network for Failure Prediction

PubMed Central

Kocaman, Esat Selim; Akay, Erdem; Yilmaz, Cagatay; Turkmen, Halit Suleyman; Misirlioglu, Ibrahim Burc; Suleman, Afzal; Yildiz, Mehmet

2017-01-01

A structural health monitoring (SHM) study of biaxial glass fibre-reinforced epoxy matrix composites under a constant, high strain uniaxial fatigue loading is performed using fibre Bragg grating (FBG) optical sensors embedded in composites at various locations to monitor the evolution of local strains, thereby understanding the damage mechanisms. Concurrently, the temperature changes of the samples during the fatigue test have also been monitored at the same locations. Close to fracture, significant variations in local temperatures and strains are observed, and it is shown that the variations in temperature and strain can be used to predict imminent fracture. It is noted that the latter information cannot be obtained using external strain gages, which underlines the importance of the tracking of local strains internally. PMID:28772393
75 FR 24502 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures; Reopening of Comment...

Federal Register 2010, 2011, 2012, 2013, 2014

2010-05-05

.... FAA-2009-0660; Notice No. 10-09] RIN 2120-AJ52 Damage Tolerance and Fatigue Evaluation of Composite... requirements of normal and transport category rotorcraft. The amendment would address advances in composite... 793) Notice No. 09-12, entitled ``Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft...
77 FR 4890 - Damage Tolerance and Fatigue Evaluation for Composite Rotorcraft Structures, and Damage Tolerance...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-02-01

...-AJ52, 2120-AJ51 Damage Tolerance and Fatigue Evaluation for Composite Rotorcraft Structures, and Damage... Tolerance and Fatigue Evaluation for Composite Rotorcraft Structures'' (76 FR 74655), published December 1... December 2, 2011. In the ``Composite Rotorcraft Structures'' rule, the FAA amended its regulations to...
Fatigue methodology III; Proceedings of the AHS National Technical Specialists' Meeting on Advanced Rotorcraft Structures, Scottsdale, AZ, Oct. 3-5, 1989

DOE Office of Scientific and Technical Information (OSTI.GOV)

Not Available

1989-01-01

Papers on rotorcraft and fatigue methodology are presented, covering topics such as reliability design for rotorcraft, a comparison between theory and fatigue test data on stress concentration factors, the retirement lives of rolling element bearings, hydrogen embrittlement risk analysis for high hardness steel parts, and rotating system load monitoring with minimum fixed system instrumentation. Additional topics include usage data collection to improve structural integrity of operational helicopters, usage monitory of military helicopters, improvements to the fatigue substantiation of the H-60 composite tail rotor blade, helicopter surviellance programs, and potential application of automotive fatigue technology in rotorcraft design. Also, consideration ismore » given to fatigue evaluation of C/MH-53 E main rotor damper threaded joints, SH-2F airframe fatigue test program, a ply termination concept for improving fracture and fatigue strength of composite laminates, the analysis and testing of composite panels subject to muzzle blast effects, the certification plan for an all-composite main rotor flexbeam, and the effects of stacking sequence on the flexural strength of composite beams.« less
Fatigue design curve of a TiNi/Al shape memory alloy composite for aircraft stringer design

NASA Astrophysics Data System (ADS)

Park, Young-Chul; Jo, Young-Jik; Baek, Seok-Heum; Furuya, Yasubumi

2009-05-01

In this study, a TiNi/Al6061 shape memory alloy (SMA) composite was fabricated by the hot press method, and pressed by a roller for its strength improvement using the shape memory fiber shrinkage phenomenon. These two kinds of specimens were fabricated with 0% and 5% volume ratio and 0%, 10 % and 20% reduction ratio of TiNi alloy fiber, respectively. A fatigue test has been performed to evaluate the fatigue life for the fabricated TiNi/Al SMA composite as an S-N curve. The results from the Goodman diagram is able to illustrate the failure criterion and fatigue limit between tensile and bending fatigue strength in the fatigue characterization of TiNi/Al SMA composites.
The isothermal fatigue behavior of a unidirectional SiC/Ti composite and the Ti alloy matrix

NASA Technical Reports Server (NTRS)

Gayda, John, Jr.; Gabb, Timothy P.; Freed, Alan D.

1989-01-01

The high temperature fatigue behavior of a metal matrix composite (MMC) consisting of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) matrix reinforced by 33 vol percent of continuous unidirectional SiC fibers was experimentally and analytically evaluated. Isothermal MMC fatigue tests with constant amplitude loading parallel to the fiber direction were performed at 300 and 550 C. Comparative fatigue tests of the Ti-15-3 matrix alloy were also conducted. Composite fatigue behavior and the in-situ stress state of the fiber and matrix were analyzed with a micromechanical model, the Concentric Cylinder Model (CCM). The cyclic stress-strain response of the composite was stable at 300 C. However, an increase in cyclic mean strain foreshortened MMC fatigue life at high strain ranges at 550 C. Fatigue tests of the matrix alloy and CCM analyses indicated this response was associated with stress relaxation of the matrix in the composite.
Synergistic Effects of Temperature, Oxidation and Stress Level on Fatigue Damage Evolution and Lifetime Prediction of Cross-Ply SiC/CAS Ceramic-Matrix Composites Through Hysteresis-Based Parameters

NASA Astrophysics Data System (ADS)

Li, Longbiao

2017-12-01

The damage development and cyclic fatigue lifetime of cross-ply SiC/CAS ceramic-matrix composites have been investigated at different testing temperatures in air atmosphere. The relationships between the fatigue hysteresis-based damage parameters, i.e., fatigue hysteresis dissipated energy, fatigue hysteresis modulus and fatigue peak strain and the damage mechanisms of matrix multicracking, fiber/matrix interface debonding, interface sliding and fibers failure, have been established. With the increase in the cycle number, the evolution of the fatigue hysteresis modulus, fatigue peak strain and fatigue hysteresis dissipated energy depends upon the fatigue peak stress levels, interface and fibers oxidation and testing temperature. The fatigue life S-N curves of cross-ply SiC/CAS composite at room and elevated temperatures have been predicted, and the fatigue limit stresses at room temperature, 750 and 850 °C, are 50, 36 and 30% of the tensile strength, respectively.
Multi-Scale/Multi-Functional Probabilistic Composite Fatigue

NASA Technical Reports Server (NTRS)

Chamis, Christos C.

2008-01-01

A multi-level (multi-scale/multi-functional) evaluation is demonstrated by applying it to three different sample problems. These problems include the probabilistic evaluation of a space shuttle main engine blade, an engine rotor and an aircraft wing. The results demonstrate that the blade will fail at the highest probability path, the engine two-stage rotor will fail by fracture at the rim and the aircraft wing will fail at 109 fatigue cycles with a probability of 0.9967.
Tensile and fatigue behavior of tungsten/copper composites

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Gabb, Timothy P.; Kim, Y. S.

1989-01-01

Work on W/Cu unidirectional composites was initiated to study the behavior of this ductile-ductile composite system under thermomechanical fatigue and to examine the applicability of fatigue-life prediction methods for thermomechanical fatigue of this metal matrix composite. The first step was to characterize the tensile behavior of four ply, 10 vol. percent W/Cu plates at room and elevated temperatures. Fatigue tests were conducted in load control on 0 degree specimens at 260 C. The maximum cyclic stress was varied but the minimum cyclic stress was kept constant. All tests were performed in vacuum. The strain at failure increased with increasing maximum cyclic stress.
Fatigue Life Methodology for Bonded Composite Skin/Stringer Configurations

NASA Technical Reports Server (NTRS)

Krueger, Ronald; Paris, Isabelle L.; OBrien, T. Kevin

2000-01-01

A methodology is presented for determining the fatigue life of bonded composite skin/stringer structures based on delamination fatigue characterization data and geometric nonlinear finite element analyses. Results were compared to fatigue tests on stringer flange/skin specimens to verify the approach.
Fatigue Life Methodology for Bonded Composite Skin/Stringer Configurations

NASA Technical Reports Server (NTRS)

Krueger, Ronald; Paris, Isabelle L.; OBrien, T. Kevin; Minguet, Pierre J.

2001-01-01

A methodology is presented for determining the fatigue life of composite structures based on fatigue characterization data and geometric nonlinear finite element (FE) analyses. To demonstrate the approach, predicted results were compared to fatigue tests performed on specimens which represented a tapered composite flange bonded onto a composite skin. In a first step, tension tests were performed to evaluate the debonding mechanisms between the flange and the skin. In a second step, a 2D FE model was developed to analyze the tests. To predict matrix cracking onset, the relationship between the tension load and the maximum principal stresses transverse to the fiber direction was determined through FE analysis. Transverse tension fatigue life data were used to -enerate an onset fatigue life P-N curve for matrix cracking. The resulting prediction was in good agreement with data from the fatigue tests. In a third step, a fracture mechanics approach based on FE analysis was used to determine the relationship between the tension load and the critical energy release rate. Mixed mode energy release rate fatigue life data were used to create a fatigue life onset G-N curve for delamination. The resulting prediction was in good agreement with data from the fatigue tests. Further, the prediction curve for cumulative life to failure was generated from the previous onset fatigue life curves. The results showed that the methodology offers a significant potential to Predict cumulative fatigue life of composite structures.
Probabilistic fatigue life prediction of metallic and composite materials

NASA Astrophysics Data System (ADS)

Xiang, Yibing

Fatigue is one of the most common failure modes for engineering structures, such as aircrafts, rotorcrafts and aviation transports. Both metallic materials and composite materials are widely used and affected by fatigue damage. Huge uncertainties arise from material properties, measurement noise, imperfect models, future anticipated loads and environmental conditions. These uncertainties are critical issues for accurate remaining useful life (RUL) prediction for engineering structures in service. Probabilistic fatigue prognosis considering various uncertainties is of great importance for structural safety. The objective of this study is to develop probabilistic fatigue life prediction models for metallic materials and composite materials. A fatigue model based on crack growth analysis and equivalent initial flaw size concept is proposed for metallic materials. Following this, the developed model is extended to include structural geometry effects (notch effect), environmental effects (corroded specimens) and manufacturing effects (shot peening effects). Due to the inhomogeneity and anisotropy, the fatigue model suitable for metallic materials cannot be directly applied to composite materials. A composite fatigue model life prediction is proposed based on a mixed-mode delamination growth model and a stiffness degradation law. After the development of deterministic fatigue models of metallic and composite materials, a general probabilistic life prediction methodology is developed. The proposed methodology combines an efficient Inverse First-Order Reliability Method (IFORM) for the uncertainty propogation in fatigue life prediction. An equivalent stresstransformation has been developed to enhance the computational efficiency under realistic random amplitude loading. A systematical reliability-based maintenance optimization framework is proposed for fatigue risk management and mitigation of engineering structures.
Isothermal fatigue behavior of a (90)(sub 8) SiC/Ti-15-3 composite at 426 C

NASA Technical Reports Server (NTRS)

Gayda, John; Gabb, Timothy P.

1991-01-01

The transverse fatigue behavior of a unidirectional, SiC/Ti-15-3 composite (35 v/o SiC, (90)(sub 8)) was evaluated at 426 C. The fatigue behavior of the composite along the fiber direction (0)(sub 8) and of unreinforced Ti-15-3 alloy were also studied for comparison purposes. The (90)(sub 8) composite fatigue life was much shorter then (0)(sub 8) life. Further, (90)(sub 8) fatigue life was also found to be far lower than that of the unreinforced Ti-15-3 alloys. A simple one-dimensional model for (90)(sub 8) fatigue behavior indicated that the short life of the composite in this orientation resulted, in large part, from weak fiber-matrix bond strength. This conclusion was supported by fractographic evidence showing numerous initiation sites along the fiber-matrix interfaces.
Sonic fatigue testing of an advanced composite aileron

NASA Technical Reports Server (NTRS)

Soovere, J.

1982-01-01

The sonic fatigue test program to verify the design of the composite inboard aileron for the L-1011 airplane is described. The composite aileron is fabricated from graphite/epoxy minisandwich covers which are attached to graphite/epoxy front spar and ribs, and to an aluminum rear spar with fasteners. The program covers the development of random fatigue data by means of coupon testing and modal studies on a representative section of the composite aileron, culminating in the accelerated sonic fatigue proof test. The composite aileron sustained nonlinear panel vibration during the proof test without failure. Viscous damping coefficients as low as 0.4% were measured on the panels. The effects of moisture conditioning and elevated temperature on the random fatigue life of both undamaged and impact damaged coupons were investigated. The combination of impact damage, moisture, and a 180 F temperature could reduce the random fatigue life by 50%.

The effect of matrix mechanical properties on (0)8 unidirectional SiC/Ti composite fatigue resistance

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Gayda, J.; Lerch, B. A.; Halford, G. R.

1991-01-01

The relationship between constituent and MMC properties in fatigue loading is investigated with low-cycle fatigue-resistance testing of an alloy Ti-15-3 matrix reinforced with SiC SCS-6 fibers. The fabrication of the composite is described, and specimens are generated that are weak and ductile (WD), strong and moderately ductile (SM), or strong and brittle (SB). Strain is measured during MMC fatigue tests at a constant load amplitude with a load-controlled waveform and during matrix-alloy fatigue tests at a constant strain amplitude using a strain-controlled waveform. The fatigue resistance of the (0)8 SiC/Ti-15-3 composite is found to be slightly influenced by matrix mechanical properties, and the composite- and matrix-alloy fatigue lives are not correlated. This finding is suggested to relate to the different crack-initiation and -growth processes in MMCs and matrix alloys.
Synergistic Effects of Frequency and Temperature on Damage Evolution and Life Prediction of Cross-Ply Ceramic Matrix Composites under Tension-Tension Fatigue Loading

NASA Astrophysics Data System (ADS)

Longbiao, Li

2017-10-01

In this paper, the synergistic effects of loading frequency and testing temperature on the fatigue damage evolution and life prediction of cross-ply SiC/MAS ceramic-matrix composite have been investigated. The damage parameters of the fatigue hysteresis modulus, fatigue hysteresis dissipated energy and the interface shear stress were used to monitor the damage evolution inside of SiC/MAS composite. The evolution of fatigue hysteresis dissipated energy, the interface shear stress and broken fibers fraction versus cycle number, and the fatigue life S-N curves of SiC/MAS composite under the loading frequency of 1 and 10 Hz at 566 °C and 1093 °C in air condition have been predicted. The synergistic effects of the loading frequency and testing temperature on the degradation rate of fatigue hysteresis dissipated energy and the interface shear stress have been analyzed.
Post-impact fatigue of cross-plied, through-the-thickness reinforced carbon/epoxy composites

NASA Astrophysics Data System (ADS)

Serdinak, Thomas E.

1994-05-01

An experimental investigation of the post-impact fatigue response of integrally woven carbon/epoxy composites was conducted. Five different through-the-thickness (TTT) reinforcing fibers were used in an experimental textile process that produced an integrally woven (0/90/0/90/0/90/0/90/0)(sub T) ply layup with 21K AS4 carbon tow fiber. The resin was Hercules 3501-6, and the five TTT reinforcing fibers were Kevlar, Toray carbon, AS4 carbon, glass, and IM6 carbon. The purpose of this investigation was to study the post-impact fatigue response of these material systems and to identify the optimum TTT fiber. Samples were impacted with one half inch diameter aluminum balls with an average velocity of 543 ft/sec. Post-impact static compression and constant amplitude tension-compression fatigue tests were conducted. Fatigue tests were conducted with a loading ratio of R=-5, and frequency of 4 Hz. Damage growth was monitored using x-radiographic and sectioning techniques and by examining the stress-strain response (across the impact site) throughout the fatigue tests. The static compressive stress versus far-field strain response was nearly linear for all material groups. All the samples had a transverse shear failure mode. The average compressive modulus (from far-field strain) was about 10 Msi. The average post-impact static compressive strength was about 35.5 Ksi. The IM6 carbon sample had a strength of over 40 Ksi, more than 16 percent stronger than average. There was considerable scatter in the S-N data. However, the IM6 carbon samples clearly had the best fatigue response. The response of the other materials, while worse than IM6 carbon, could not be ranked definitively. The initial damage zones caused by the impact loading and damage growth from fatigue loading were similar for all five TTT reinforcing materials. The initial damage zones were circular and consisted of delaminations, matrix cracks and ply cracks.
Post-impact fatigue of cross-plied, through-the-thickness reinforced carbon/epoxy composites. M.S. Thesis - Clemson Univ.

NASA Technical Reports Server (NTRS)

Serdinak, Thomas E.

1994-01-01

An experimental investigation of the post-impact fatigue response of integrally woven carbon/epoxy composites was conducted. Five different through-the-thickness (TTT) reinforcing fibers were used in an experimental textile process that produced an integrally woven (0/90/0/90/0/90/0/90/0)(sub T) ply layup with 21K AS4 carbon tow fiber. The resin was Hercules 3501-6, and the five TTT reinforcing fibers were Kevlar, Toray carbon, AS4 carbon, glass, and IM6 carbon. The purpose of this investigation was to study the post-impact fatigue response of these material systems and to identify the optimum TTT fiber. Samples were impacted with one half inch diameter aluminum balls with an average velocity of 543 ft/sec. Post-impact static compression and constant amplitude tension-compression fatigue tests were conducted. Fatigue tests were conducted with a loading ratio of R=-5, and frequency of 4 Hz. Damage growth was monitored using x-radiographic and sectioning techniques and by examining the stress-strain response (across the impact site) throughout the fatigue tests. The static compressive stress versus far-field strain response was nearly linear for all material groups. All the samples had a transverse shear failure mode. The average compressive modulus (from far-field strain) was about 10 Msi. The average post-impact static compressive strength was about 35.5 Ksi. The IM6 carbon sample had a strength of over 40 Ksi, more than 16 percent stronger than average. There was considerable scatter in the S-N data. However, the IM6 carbon samples clearly had the best fatigue response. The response of the other materials, while worse than IM6 carbon, could not be ranked definitively. The initial damage zones caused by the impact loading and damage growth from fatigue loading were similar for all five TTT reinforcing materials. The initial damage zones were circular and consisted of delaminations, matrix cracks and ply cracks. Post-impact fatigue loading caused delamination growth, ply cracking and fiber bundle failures, typically 45 deg from impact load direction. During the initial 97 percent of fatigue life, delaminations, ply cracks and fiber bundle failures primarily grew at and near the impact site. During the final 3 percent of life, damage grew rapidly transverse to the loading direction as a through-the-thickness transverse shear failure. The stress-strain response was typically linear during the initial 50 percent of life, and stiffness dropped about 20 percent during this period. During the next 47 percent of life, stiffness dropped about 34 percent, and the stress-strain response was no longer linear. The stiffness decreased about 23 percent during the final 3 percent of life. These trends were typical of all the materials tested. Therefore, by monitoring stiffness loss, fatigue failure could be accurately anticipated.
Predicting Fatigue Lives Of Metal-Matrix/Fiber Composites

NASA Technical Reports Server (NTRS)

Bartolotta, Paul A.

1994-01-01

Method of prediction of fatigue lives of intermetallic-matrix/fiber composite parts at high temperatures styled after method of universal slopes. It suffices to perform relatively small numbers of fatigue tests. Data from fatigue tests correlated with tensile-test data by fitting universal-slopes equation to both sets of data. Thereafter, universal-slopes equation used to predict fatigue lives from tensile properties.
77 FR 42547 - Agency Information Collection Activities: Requests for Comments; Clearance of Renewed Approval of...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-07-19

... and Fatigue Evaluation of Composite Rotorcraft Structures AGENCY: Federal Aviation Administration (FAA... Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures. Form Numbers: There are no FAA forms... ``Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures'' final rule (76 FR 74655...
Composite materials: Fatigue and fracture. Vol. 3

NASA Technical Reports Server (NTRS)

O'Brien, T. K. (Editor)

1991-01-01

The present volume discusses topics in the fields of matrix cracking and delamination, interlaminar fracture toughness, delamination analysis, strength and impact characteristics, and fatigue and fracture behavior. Attention is given to cooling rate effects in carbon-reinforced PEEK, the effect of porosity on flange-web corner strength, mode II delamination in toughened composites, the combined effect of matrix cracking and free edge delamination, and a 3D stress analysis of plain weave composites. Also discussed are the compression behavior of composites, damage-based notched-strength modeling, fatigue failure processes in aligned carbon-epoxy laminates, and the thermomechanical fatigue of a quasi-isotropic metal-matrix composite.
High-Performance Acousto-Ultrasonic Scan System Being Developed

NASA Technical Reports Server (NTRS)

Roth, Don J.; Martin, Richard E.; Cosgriff, Laura M.; Gyekenyesi, Andrew L.; Kautz, Harold E.

2003-01-01

Acousto-ultrasonic (AU) interrogation is a single-sided nondestructive evaluation (NDE) technique employing separated sending and receiving transducers. It is used for assessing the microstructural condition and distributed damage state of the material between the transducers. AU is complementary to more traditional NDE methods, such as ultrasonic cscan, x-ray radiography, and thermographic inspection, which tend to be used primarily for discrete flaw detection. Throughout its history, AU has been used to inspect polymer matrix composites, metal matrix composites, ceramic matrix composites, and even monolithic metallic materials. The development of a high-performance automated AU scan system for characterizing within-sample microstructural and property homogeneity is currently in a prototype stage at NASA. This year, essential AU technology was reviewed. In addition, the basic hardware and software configuration for the scanner was developed, and preliminary results with the system were described. Mechanical and environmental loads applied to composite materials can cause distributed damage (as well as discrete defects) that plays a significant role in the degradation of physical properties. Such damage includes fiber/matrix debonding (interface failure), matrix microcracking, and fiber fracture and buckling. Investigations at the NASA Glenn Research Center have shown that traditional NDE scan inspection methods such as ultrasonic c-scan, x-ray imaging, and thermographic imaging tend to be more suited to discrete defect detection rather than the characterization of accumulated distributed micro-damage in composites. Since AU is focused on assessing the distributed micro-damage state of the material in between the sending and receiving transducers, it has proven to be quite suitable for assessing the relative composite material state. One major success story at Glenn with AU measurements has been the correlation between the ultrasonic decay rate obtained during AU inspection and the mechanical modulus (stiffness) seen during fatigue experiments with silicon carbide/silicon carbide (SiC/SiC) ceramic matrix composite samples. As shown in the figure, ultrasonic decay increased as the modulus decreased for the ceramic matrix composite tensile fatigue samples. The likely microstructural reason for the decrease in modulus (and increase in ultrasonic decay) is the matrix microcracking that commonly occurs during fatigue testing of these materials. Ultrasonic decay has shown the capability to track the pattern of transverse cracking and fiber breakage in these composites.
High-Performance Acousto-Ultrasonic Scan System Being Developed

NASA Technical Reports Server (NTRS)

Roth, Don J.; Martin, Richard E.; Cosgriff, Laura M.; Gyekenyesi, Andrew L.; Kautz, Harold E.

2003-01-01

Acousto-ultrasonic (AU) interrogation is a single-sided nondestructive evaluation (NDE) technique employing separated sending and receiving transducers. It is used for assessing the microstructural condition and distributed damage state of the material between the transducers. AU is complementary to more traditional NDE methods, such as ultrasonic cscan, x-ray radiography, and thermographic inspection, which tend to be used primarily for discrete flaw detection. Throughout its history, AU has been used to inspect polymer matrix composites, metal matrix composites, ceramic matrix composites, and even monolithic metallic materials. The development of a high-performance automated AU scan system for characterizing within-sample microstructural and property homogeneity is currently in a prototype stage at NASA. This year, essential AU technology was reviewed. In addition, the basic hardware and software configuration for the scanner was developed, and preliminary results with the system were described. Mechanical and environmental loads applied to composite materials can cause distributed damage (as well as discrete defects) that plays a significant role in the degradation of physical properties. Such damage includes fiber/matrix debonding (interface failure), matrix microcracking, and fiber fracture and buckling. Investigations at the NASA Glenn Research Center have shown that traditional NDE scan inspection methods such as ultrasonic c-scan, x-ray imaging, and thermographic imaging tend to be more suited to discrete defect detection rather than the characterization of accumulated distributed microdamage in composites. Since AU is focused on assessing the distributed microdamage state of the material in between the sending and receiving transducers, it has proven to be quite suitable for assessing the relative composite material state. One major success story at Glenn with AU measurements has been the correlation between the ultrasonic decay rate obtained during AU inspection and the mechanical modulus (stiffness) seen during fatigue experiments with silicon carbide/silicon carbide (SiC/SiC) ceramic matrix composite samples. As shown in the figure, ultrasonic decay increased as the modulus decreased for the ceramic matrix composite tensile fatigue samples. The likely microstructural reason for the decrease in modulus (and increase in ultrasonic decay) is the matrix microcracking that commonly occurs during fatigue testing of these materials. Ultrasonic decay has shown the capability to track the pattern of transverse cracking and fiber breakage in these composites.
Fatigue behavior of SiC reinforced titanium composites

NASA Technical Reports Server (NTRS)

Bhatt, R. T.; Grimes, H. H.

1979-01-01

The low cycle axial fatigue properties of 25 and 44 fiber volume percent SiC/Ti(6Al-4V) composites were measured at room temperature and at 650 deg C. The S-N curves for the composites showed no anticipated improvement over bulk matrix behavior at room temperature. Although axial and transverse tensile strength results suggest a degradation in SiC fiber strength during composite fabrication, it appears that the poor fatigue life of the composites was caused by a reduced fatigue resistance of the reinforced Ti(6Al-4V) matrix. The reduced matrix behavior was due, to the presence of flawed and fractured fibers created near the specimen surfaces by preparation techniques and to the large residual tensile stresses that can exist in fiber reinforced matrices. The effects of fatigue testing at high temperature are discussed.
Effect of Environment on Fatigue Behavior of a Nicalon(TM)/Si-N-C Ceramic Matrix Composite

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Ojard, Greg C.; Verrilli, Michael J.; Kiraly, Louis J. (Technical Monitor)

2002-01-01

The effect of environmental exposure on the fatigue life of Nicalon(TM) /Si-N-C composite was investigated in this study. Test specimens with arrays of 1.8 mm diameter holes and two different open areas, 25 and 35%, were machined. Three environmental conditions were studied: 1) continuous fatigue cycling in air, 2) fatigue cycling in air alternating with humidity exposure, and 3) fatigue cycling in air alternating with exposure to a salt-fog environment. All fatigue testing on specimens with holes was performed with a load ratio, R = 0.05, and at a temperature of 910 C. In general, fatigue lives were shortest for specimens subjected to salt-fog exposure and longest for specimens subjected to continuous fatigue cycling in air. The fatigue data generated on the specimens with holes were compared with fatigue data generated in air on specimens with no holes. Fatigue strength reduction factors for different environmental conditions and open areas investigated in the study were calculated for the Nicalon(TM) /Si-N-C composite.
Fatigue In Continuous-Fiber/Metal-Matrix Composites

NASA Technical Reports Server (NTRS)

Johnson, William S.

1992-01-01

Report describes experimental approaches to quantification of fatigue damage in metal-matrix composites (MMC's). Discusses number of examples of development of damage and failure along with associated analytical models of behavior of MMC. Objectives of report are twofold. First, present experimental procedures and techniques for conducting meaningful fatigue tests to detect and quantify fatigue damage in MMC's. Second, present examples of how fatigue damage initiated and grows in various MMC's. Report furnishes some insight into what type of fatigue damage occurs and how damage quantified.
Considerations concerning fatigue life of metal matrix composites

NASA Technical Reports Server (NTRS)

Radhakrishnan, V. M.; Bartolotta, Paul A.

1993-01-01

Since metal matrix composites (MMC) are composed from two very distinct materials each having their own physical and mechanical properties, it is feasible that the fatigue resistance depends on the strength of the weaker constituent. Based on this assumption, isothermal fatigue lives of several MMC's were analyzed utilizing a fatigue life diagram approach. For each MMC, the fatigue life diagram was quantified using the mechanical properties of its constituents. The fatigue life regions controlled by fiber fracture and matrix were also quantitatively defined.
Cyclic fatigue-crack propagation, stress-corrosion, and fracture-toughness behavior in pyrolytic carbon-coated graphite for prosthetic heart valve applications.

PubMed

Ritchie, R O; Dauskardt, R H; Yu, W K; Brendzel, A M

1990-02-01

Fracture-mechanics tests were performed to characterize the cyclic fatigue, stress-corrosion cracking, and fracture-toughness behavior of a pyrolytic carbon-coated graphite composite material used in the manufacture of cardiac valve prostheses. Testing was carried out using compact tension C(T) samples containing "atomically" sharp precracks, both in room-temperature air and principally in a simulated physiological environment of 37 degrees C Ringer's lactate solution. Under sustained (monotonic) loads, the composite exhibited resistance-curve behavior, with a fracture toughness (KIc) between 1.1 and 1.9 MPa square root of m, and subcritical stress-corrosion crack velocities (da/dt) which were a function of the stress intensity K raised to the 74th power (over the range approximately 10(-9) to over 10(-5) m/s). More importantly, contrary to common perception, under cyclic loading conditions the composite was found to display true (cyclic) fatigue failure in both environments; fatigue-crack growth rates (da/dN) were seen to be a function of the 19th power of the stress-intensity range delta K (over the range approximately 10(-11) to over 10(-8) m/cycle). As subcritical crack velocities under cyclic loading were found to be many orders of magnitude faster than those measured under equivalent monotonic loads and to occur at typically 45% lower stress-intensity levels, cyclic fatigue in pyrolytic carbon-coated graphite is reasoned to be a vital consideration in the design and life-prediction procedures of prosthetic devices manufactured from this material.
Proceedings of the Annual Mechanics of Composites Review (8th) Held at Wright-Patterson AFB, Ohio on 5-7 October 1982.

DTIC Science & Technology

1983-04-01

Spectrum Fatigue Behavior of Postbuckled Shear Panels; PO01 246 Development of Analysis for Predicting Compression Fatigt Life and Residual Strength in...Lazyup and Frequency Effects on Fatigue Life of Composites, POOl 256 Effect of Stress Ratio on Fatigue Life of Composites,’ POOl 257 High-Load Transfer...L. Agerwall, Northrop Corporation 0950-1020 BREAK 1020-1100 DEVELOPMENT OF ANALYSIS FOR PREDICTING COMPRESSION 34 FATIGUE LIFE AND RESIDUAL STRENGTH
Fatigue evaluation of composite-reinforced, integrally stiffened metal panels

NASA Technical Reports Server (NTRS)

Dumesnil, C. E.

1973-01-01

The fatigue behavior of composite-reinforced, integrally stiffened metal panels was investigated in combined metal and composite materials subjected to fatigue loading. The systems investigated were aluminum-graphite/epoxy, and aluminum-S glass/epoxy. It was found that the composite material would support the total load at limit stress after the metal had completely failed, and the weight of the composite-metal system would be equal to that of an all metal system which would carry the same total load at limit stress.
Composite structural materials

NASA Technical Reports Server (NTRS)

Ansell, G. S.; Loewy, R. G.; Wiberley, S. E.

1984-01-01

Progress is reported in studies of constituent materials composite materials, generic structural elements, processing science technology, and maintaining long-term structural integrity. Topics discussed include: mechanical properties of high performance carbon fibers; fatigue in composite materials; experimental and theoretical studies of moisture and temperature effects on the mechanical properties of graphite-epoxy laminates and neat resins; numerical investigations of the micromechanics of composite fracture; delamination failures of composite laminates; effect of notch size on composite laminates; improved beam theory for anisotropic materials; variation of resin properties through the thickness of cured samples; numerical analysis composite processing; heat treatment of metal matrix composites, and the RP-1 and RP2 gliders of the sailplane project.
Investigation of a ceramic matrix composite under strain controlled fatigue condition

DOE Office of Scientific and Technical Information (OSTI.GOV)

Gudaitis, J.J.; Mall, S.

The fatigue behavior along with damage mechanisms and failure modes of a fiber reinforced ceramic matrix composite with a cross-ply lay-up was investigated under strain controlled mode. Two fatigue conditions involving tension-tension and tension-compression cycling were employed. The strain range versus fatigue life curves for both fatigue conditions were in agreement with each other. However, damage mechanisms and failure modes were different for both cases.
Simulation of Fatigue Behavior of High Temperature Metal Matrix Composites

NASA Technical Reports Server (NTRS)

Tong, Mike T.; Singhal, Suren N.; Chamis, Christos C.; Murthy, Pappu L. N.

1996-01-01

A generalized relatively new approach is described for the computational simulation of fatigue behavior of high temperature metal matrix composites (HT-MMCs). This theory is embedded in a specialty-purpose computer code. The effectiveness of the computer code to predict the fatigue behavior of HT-MMCs is demonstrated by applying it to a silicon-fiber/titanium-matrix HT-MMC. Comparative results are shown for mechanical fatigue, thermal fatigue, thermomechanical (in-phase and out-of-phase) fatigue, as well as the effects of oxidizing environments on fatigue life. These results show that the new approach reproduces available experimental data remarkably well.
The mechanical behaviour of NBR/FEF under compressive cyclic stress strain

NASA Astrophysics Data System (ADS)

Mahmoud, W. E.; El-Eraki, M. H. I.; El-Lawindy, A. M. Y.; Hassan, H. H.

2006-06-01

Acrylonitrile butadiene rubber compounds filled with different concentrations of fast extrusion furnace (FEF) carbon black were experimentally investigated. The stress-strain curves of the composites were studied, which suggest good filler-matrix adhesion. The large reinforcement effect of the filler followed the Guth model for non-spherical particles. The effect of FEF carbon black on the cyclic fatigue and hysteresis was also examined. The loading and unloading stress-strain relationships for any cycle were described by applying Ogden's model for rubber samples. The dissipation energy that indicates the vibration damping capacity for all samples was determined. A simple model was proposed, to investigate the relation between maximum stress and the number of cyclic fatigue.

Effect of stress ratio on the fatigue behaviour of glass/epoxy composite

NASA Astrophysics Data System (ADS)

Syayuthi, A. R. A.; Majid, M. S. Abdul; Ridzuan, M. J. M.; Basaruddin, K. S.; Peng, T. L.

2017-10-01

The effect of stress ratio on the fatigue behaviour of the GFRE composite has been investigated. The glass fibre reinforced epoxy (GFRE) composite plates were fabricated using vacuum infusion method. Static tensile was performed in accordance with the ASTM D5766 standard, and the cyclic test was conducted according to ASTM D3479 with three different stress ratio, R = 0, 0.5, -1. Static tensile tests were carried out to determine the ultimate strength of this composite. Subsequently, fatigue tests loads ranging from 30% to 90% of the ultimate load were applied to each specimen. The S-N curve of different stress ratio loading of fibreglass/epoxy composites was then established. The results show that the number of cycles to failure increases as the loading is decreased. The specimens for fatigue tests loads 30% at R = 0 and -1 recorded the highest number of cycles at 2 million cycles. The results obtained from this test indicated a significant life reduction for R = -1 compared with the tension-tension loading, with the life reduction for R = -1 being greatest. The fatigue behaviour of the GFRE composite materials is not only influenced by the percentage of fatigue tests load but with different of stress ratio.
Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a “sandwich structure” as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50–55% of ultimate tensile strength). The dynamic modulus (E⁎) was found to stay almost constant at 47 GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials.
Biomechanical fatigue analysis of an advanced new carbon fiber/flax/epoxy plate for bone fracture repair using conventional fatigue tests and thermography.

PubMed

Bagheri, Zahra S; El Sawi, Ihab; Bougherara, Habiba; Zdero, Radovan

2014-07-01

The current study is part of an ongoing research program to develop an advanced new carbon fiber/flax/epoxy (CF/flax/epoxy) hybrid composite with a "sandwich structure" as a substitute for metallic materials for orthopedic long bone fracture plate applications. The purpose of this study was to assess the fatigue properties of this composite, since cyclic loading is one of the main types of loads carried by a femur fracture plate during normal daily activities. Conventional fatigue testing, thermographic analysis, and scanning electron microscopy (SEM) were used to analyze the damage progress that occurred during fatigue loading. Fatigue strength obtained using thermography analysis (51% of ultimate tensile strength) was confirmed using the conventional fatigue test (50-55% of ultimate tensile strength). The dynamic modulus (E(⁎)) was found to stay almost constant at 47GPa versus the number of cycles, which can be related to the contribution of both flax/epoxy and CF/epoxy laminae to the stiffness of the composite. SEM images showed solid bonding at the CF/epoxy and flax/epoxy laminae, with a crack density of only 0.48% for the plate loaded for 2 million cycles. The current composite plate showed much higher fatigue strength than the main loads experienced by a typical patient during cyclic activities; thus, it may be a potential candidate for bone fracture plate applications. Moreover, the fatigue strength from thermographic analysis was the same as that obtained by the conventional fatigue tests, thus demonstrating its potential use as an alternate tool to rapidly evaluate fatigue strength of composite biomaterials. Copyright © 2014 Elsevier Ltd. All rights reserved.
The influence of loading frequency on the high-temperature fatigue behavior of a Nicalon-fabric-reinforced polymer-derived ceramic-matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vanswijgenhoven, E.; Holmes, J.; Wevers, M.

Fiber-reinforced ceramic-matrix composites are under development for high-temperature structural applications. These applications involve fatigue loading under a wide range of frequencies. To date, high-temperature fatigue experiments have typically been performed at loading frequencies of 10 Hz or lower. At higher frequencies, a strong effect of loading frequency on fatigue life has been demonstrated for certain CMC`s tested at room temperature. The fatigue life of CMC`s with weak fiber-matrix interfaces typically decreases as the loading frequency increases. This decrease is attributed to frictional heating and frequency dependent interface and fiber damage. More recently, it has been shown that the room temperaturemore » fatigue life of a Nicalon-fabric-reinforced composite with a strong interface (SYLRAMIC{trademark}) appears to be independent of loading frequency. The high-temperature low-frequency fatigue behavior of the SYLRAMIC composite has also been investigated. For a fatigue peak stress {sigma}{sub peak} above a proportional limit stress of 70 MPa, the number of cycles to failure N{sub f} decreased with an increase in {sigma}{sub peak}. The material endured more than 10{sup 6} cycles for {sigma}{sub peak} below 70 MPa. In this paper, the influence of loading frequency on the high-temperature fatigue behavior of the SYLRAMIC composite is reported. It will be shown that the fatigue limit is unaffected by the loading frequency, that the number of fatigue cycles to failure N{sub f} increases with an increase in frequency, and that the time to failure t{sub f} decreases with an increase in frequency.« less
Influence of dental restorations and mastication loadings on dentine fatigue behaviour: Image-based modelling approach.

PubMed

Vukicevic, Arso M; Zelic, Ksenija; Jovicic, Gordana; Djuric, Marija; Filipovic, Nenad

2015-05-01

The aim of this study was to use Finite Element Analysis (FEA) to estimate the influence of various mastication loads and different tooth treatments (composite restoration and endodontic treatment) on dentine fatigue. The analysis of fatigue behaviour of human dentine in intact and composite restored teeth with root-canal-treatment using FEA and fatigue theory was performed. Dentine fatigue behaviour was analysed in three virtual models: intact, composite-restored and endodontically-treated tooth. Volumetric change during the polymerization of composite was modelled by thermal expansion in a heat transfer analysis. Low and high shrinkage stresses were obtained by varying the linear shrinkage of composite. Mastication forces were applied occlusally with the load of 100, 150 and 200N. Assuming one million cycles, Fatigue Failure Index (FFI) was determined using Goodman's criterion while residual fatigue lifetime assessment was performed using Paris-power law. The analysis of the Goodman diagram gave both maximal allowed crack size and maximal number of cycles for the given stress ratio. The size of cracks was measured on virtual models. For the given conditions, fatigue-failure is not likely to happen neither in the intact tooth nor in treated teeth with low shrinkage stress. In the cases of high shrinkage stress, crack length was much larger than the maximal allowed crack and failure occurred with 150 and 200N loads. The maximal allowed crack size was slightly lower in the tooth with root canal treatment which induced somewhat higher FFI than in the case of tooth with only composite restoration. Main factors that lead to dentine fatigue are levels of occlusal load and polymerization stress. However, root canal treatment has small influence on dentine fatigue. The methodology proposed in this study provides a new insight into the fatigue behaviour of teeth after dental treatments. Furthermore, it estimates maximal allowed crack size and maximal number of cycles for a specific case. Copyright © 2015 Elsevier Ltd. All rights reserved.
Comparison of dynamic fatigue behavior between SiC whisker-reinforced composite and monolithic silicon nitrides

NASA Technical Reports Server (NTRS)

Choi, Sung R.; Salem, Jonathan A.

1991-01-01

The dynamic fatigue behavior of 30 vol percent silicon nitride whisker-reinforced composite and monolithic silicon nitrides were determined as a function of temperature from 1100 to 1300 C in ambient air. The fatigue susceptibility parameter, n, decreased from 88.1 to 20.1 for the composite material, and from 50.8 to 40.4 for the monolithic, with increasing temperature from 1100 to 1300 C. A transition in the dynamic fatigue curve occurred for the composite material at a low stressing rate of 2 MPa/min at 1300 C, resulting in a very low value of n equals 5.8. Fractographic analysis showed that glassy phases in the slow crack growth region were more pronounced in the composite compared to the monolithic material, implying that SiC whisker addition promotes the formation of glass rich phases at the grain boundaries, thereby enhancing fatigue. These results indicate that SiC whisker addition to Si3 N4 matrix substantially deteriorates fatigue resistance inherent to the matrix base material for this selected material system.
Effect of mission cycling on the fatigue performance of SiC-coated carbon-carbon composites

NASA Technical Reports Server (NTRS)

Mahfuz, H.; Das, P. S.; Jeelani, S.; Baker, D. M.; Johnson, S. A.

1993-01-01

The effects of thermal and pressure cycling on the fatigue performance of carbon-carbon composites, and the influence of mission cycling on these effects, were investigated by subjecting both virgin and mission-cycled two-dimensional specimens of SiC-coated carbon-carbon composites to fatigue tests, conducted at room temperature in three-point bending, with a stress ratio of 0.2 and a frequency of 1 Hz. It was found that the fatigue strength of C-C composites is high (about 90 percent of the ultimate flexural strength), but decreased with the mission cycling. The lowering of the fatigue strength with mission cycling is attributed to the increase in interfacial bond strength due to thermal and pressure cycling of the material. The already high sensitivity of C-C composites to stress during cyclic loading increases further with the amount of mission cycling. Results of NDE suggest that the damage growth in virgin C-C, in the high-cycle range, is slow at the initial stage of the cyclic life, but propagates rapidly after certain threshold cycles of the fatigue life.
Comparisons of Damage Evolution between 2D C/SiC and SiC/SiC Ceramic-Matrix Composites under Tension-Tension Cyclic Fatigue Loading at Room and Elevated Temperatures

PubMed Central

Li, Longbiao

2016-01-01

In this paper, comparisons of damage evolution between 2D C/SiC and SiC/SiC ceramic-matrix composites (CMCs) under tension–tension cyclic fatigue loading at room and elevated temperatures have been investigated. Fatigue hysteresis loops models considering multiple matrix cracking modes in 2D CMCs have been developed based on the damage mechanism of fiber sliding relative to the matrix in the interface debonded region. The relationships between the fatigue hysteresis loops, fatigue hysteresis dissipated energy, fatigue peak stress, matrix multiple cracking modes, and interface shear stress have been established. The effects of fiber volume fraction, fatigue peak stress and matrix cracking mode proportion on fatigue hysteresis dissipated energy and interface debonding and sliding have been analyzed. The experimental fatigue hysteresis dissipated energy of 2D C/SiC and SiC/SiC composites at room temperature, 550 °C, 800 °C, and 1100 °C in air, and 1200 °C in vacuum corresponding to different fatigue peak stresses and cycle numbers have been analyzed. The interface shear stress degradation rate has been obtained through comparing the experimental fatigue hysteresis dissipated energy with theoretical values. Fatigue damage evolution in C/SiC and SiC/SiC composites has been compared using damage parameters of fatigue hysteresis dissipated energy and interface shear stress degradation rate. It was found that the interface shear stress degradation rate increases at elevated temperature in air compared with that at room temperature, decreases with increasing loading frequency at room temperature, and increases with increasing fatigue peak stress at room and elevated temperatures. PMID:28773966
Tensile and compressive failure modes of laminated composites loaded by fatigue with different mean stress

NASA Technical Reports Server (NTRS)

Rotem, Assa

1990-01-01

Laminated composite materials tend to fail differently under tensile or compressive load. Under tension, the material accumulates cracks and fiber fractures, while under compression, the material delaminates and buckles. Tensile-compressive fatigue may cause either of these failure modes depending on the specific damage occurring in the laminate. This damage depends on the stress ratio of the fatigue loading. Analysis of the fatigue behavior of the composite laminate under tension-tension, compression-compression, and tension-compression had led to the development of a fatigue envelope presentation of the failure behavior. This envelope indicates the specific failure mode for any stress ratio and number of loading cycles. The construction of the fatigue envelope is based on the applied stress-cycles to failure (S-N) curves of both tensile-tensile and compressive-compressive fatigue. Test results are presented to verify the theoretical analysis.
Tension-Tension Fatigue Behavior of Unidirectional C/Sic Ceramic-Matrix Composite at Room Temperature and 800 °C in Air Atmosphere

PubMed Central

Li, Longbiao

2015-01-01

The tension-tension fatigue behavior of unidirectional C/SiC ceramic-matrix composite at room temperature and 800 °C under air has been investigated. The fatigue hysteresis modulus and fatigue hysteresis loss energy corresponding to different number of applied cycles have been analyzed. The fatigue hysteresis loops models for different interface slip cases have been derived based on the fatigue damage mechanism of fiber slipping relative to matrix in the interface debonded region upon unloading and subsequent reloading. The fiber/matrix interface shear stress has been estimated for different numbers of applied cycles. By combining the interface shear stress degradation model and fibers strength degradation model with fibers failure model, the tension-tension fatigue life S-N curves of unidirectional C/SiC composite at room temperature and 800 °C under air have been predicted.
Prediction of composite fatigue life under variable amplitude loading using artificial neural network trained by genetic algorithm

NASA Astrophysics Data System (ADS)

Rohman, Muhamad Nur; Hidayat, Mas Irfan P.; Purniawan, Agung

2018-04-01

Neural networks (NN) have been widely used in application of fatigue life prediction. In the use of fatigue life prediction for polymeric-base composite, development of NN model is necessary with respect to the limited fatigue data and applicable to be used to predict the fatigue life under varying stress amplitudes in the different stress ratios. In the present paper, Multilayer-Perceptrons (MLP) model of neural network is developed, and Genetic Algorithm was employed to optimize the respective weights of NN for prediction of polymeric-base composite materials under variable amplitude loading. From the simulation result obtained with two different composite systems, named E-glass fabrics/epoxy (layups [(±45)/(0)2]S), and E-glass/polyester (layups [90/0/±45/0]S), NN model were trained with fatigue data from two different stress ratios, which represent limited fatigue data, can be used to predict another four and seven stress ratios respectively, with high accuracy of fatigue life prediction. The accuracy of NN prediction were quantified with the small value of mean square error (MSE). When using 33% from the total fatigue data for training, the NN model able to produce high accuracy for all stress ratios. When using less fatigue data during training (22% from the total fatigue data), the NN model still able to produce high coefficient of determination between the prediction result compared with obtained by experiment.
Damage development in titanium metal matrix composites subjected to cyclic loading

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1992-01-01

Several layups of SCS-6/Ti-15-3 composites were investigated. Fatigue tests were conducted and analyzed for both notched and unnotched specimens at room temperature and elevated temperatures. Thermo-mechanical fatigue results were analyzed. Test results indicated that the stress in the 0 degree fibers is the controlling factor in fatigue life. The static and fatigue strength of these materials is shown to be strongly dependent on the level of residual stresses and the fiber/matrix interfacial strength. Fatigue tests of notched specimens showed that cracks can initiate and grow many fiber spacings in the matrix materials without breaking fibers. Fiber bridging models were applied to characterize the crack growth behavior. The matrix cracks are shown to significantly reduce the residual strength of notched composites. The notch strength of these composites was accurately predicted using a micromechanics based methodology.
Damage development in titanium metal-matrix composites subjected to cyclic loading

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1993-01-01

Several layups of SCS-6/Ti-15-3 composites were investigated. Fatigue tests were conducted and analyzed for both notched and unnotched specimens at room temperature and elevated temperatures. Thermo-mechanical fatigue results were analyzed. Test results indicated that the stress in the 0 degree fibers is the controlling factor in fatigue life. The static and fatigue strength of these materials is shown to be strongly dependent on the level of residual stresses and the fiber/matrix interfacial strength. Fatigue tests of notched specimens showed that cracks can initiate and grow many fiber spacings in the matrix materials without breaking fibers. Fiber bridging models were applied to characterize the crack growth behavior. The matrix cracks are shown to significantly reduce the residual strength of notched composites. The notch strength of these composites was accurately predicted using a micromechanics based methodology.
The fatigue life study of polyphenylene sulfide composites filled with continuous glass fibers

NASA Astrophysics Data System (ADS)

Ye, Junjie; Hong, Yun; Wang, Yongkun; Zhai, Zhi; Shi, Baoquan; Chen, Xuefeng

2018-04-01

In this study, an effective microscopic model is proposed to investigate the fatigue life of composites containing continuous glass fibers, which is surrounded by polyphenylene sulfide (PPS) matrix materials. The representative volume element is discretized by parametric elements. Moreover, the microscopic model is established by employing the relation between average surface displacements and average surface tractions. Based on the experimental data, the required fatigue failure parameters of the PPS are determined. Two different fiber arrangements are considered for comparisons. Numerical analyses indicated that the square edge packing provides a more accuracy. In addition, microscopic structural parameters (fiber volume fraction, fiber off-axis angle) effect on the fatigue life of Glass/PPS composites is further discussed. It is revealed that fiber strength degradation effects on the fatigue life of continuous fiber-reinforced composites can be ignored.
Computational simulation of acoustic fatigue for hot composite structures

NASA Technical Reports Server (NTRS)

Singhal, S. N.; Nagpal, V. K.; Murthy, P. L. N.; Chamis, C. C.

1991-01-01

This paper presents predictive methods/codes for computational simulation of acoustic fatigue resistance of hot composite structures subjected to acoustic excitation emanating from an adjacent vibrating component. Select codes developed over the past two decades at the NASA Lewis Research Center are used. The codes include computation of (1) acoustic noise generated from a vibrating component, (2) degradation in material properties of the composite laminate at use temperature, (3) dynamic response of acoustically excited hot multilayered composite structure, (4) degradation in the first-ply strength of the excited structure due to acoustic loading, and (5) acoustic fatigue resistance of the excited structure, including propulsion environment. Effects of the laminate lay-up and environment on the acoustic fatigue life are evaluated. The results show that, by keeping the angled plies on the outer surface of the laminate, a substantial increase in the acoustic fatigue life is obtained. The effect of environment (temperature and moisure) is to relieve the residual stresses leading to an increase in the acoustic fatigue life of the excited panel.
Computational simulation of acoustic fatigue for hot composite structures

NASA Technical Reports Server (NTRS)

Singhal, Surendra N.; Murthy, Pappu L. N.; Chamis, Christos C.; Nagpal, Vinod K.; Sutjahjo, Edhi

1991-01-01

Predictive methods/computer codes for the computational simulation of acoustic fatigue resistance of hot composite structures subjected to acoustic excitation emanating from an adjacent vibrating component are discussed. Select codes developed over the past two decades at the NASA Lewis Research Center are used. The codes include computation of acoustic noise generated from a vibrating component, degradation in material properties of a composite laminate at use temperature, dynamic response of acoustically excited hot multilayered composite structure, degradation in the first ply strength of the excited structure due to acoustic loading, and acoustic fatigue resistance of the excited structure, including the propulsion environment. Effects of the laminate lay-up and environment on the acoustic fatigue life are evaluated. The results show that, by keeping the angled plies on the outer surface of the laminate, a substantial increase in the acoustic fatigue life is obtained. The effect of environment (temperature and moisture) is to relieve the residual stresses leading to an increase in the acoustic fatigue life of the excited panel.
Fatigue behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP)

Treesearch

Jinghao Li; John F. Hunt; Shaoqin Gong; Zhiyong Cai

2015-01-01

The static and fatigue bending behavior of wood-fiber-based tri-axial engineered sandwich composite panels (ESCP) has been investigated by four-point bending tests. Fatigue panels and weakened panels (wESCP) with an initial interface defect were manufactured for the fatigue tests. Stress Ï vs. number of cycles curves (S-N) were recorded under the different stress...
Behavior of a Quasi-Isotropic Ply Metal Matrix Composite under Thermo-Mechanical and Isothermal Fatigue Loading

DTIC Science & Technology

1992-12-01

tensile strength of the composite (20:14). After the heat treatment was accomplished, polishing was performed. Using an automated MAXIMET polishing machine ...AD-A258 902 AFIT/GAE/.ENY/92D-05 Behavior of a Quasi-Isotropic Ply Metal Matrix Composite Under Thermo- Mechanical and Isothermal Fatigue Loading...115 AFIT/GAE/ENY/92D-05 Behavior of a Quasi-Isotropic Ply Metal Matrix Composite Under Thermo- Mechanical and Isothermal Fatigue Loading THESIS
A model for predicting high-temperature fatigue failure of a W/Cu composite

NASA Technical Reports Server (NTRS)

Verrilli, M. J.; Kim, Y.-S.; Gabb, T. P.

1991-01-01

The material studied, a tungsten-fiber-reinforced, copper-matrix composite, is a candidate material for rocket nozzle liner applications. It was shown that at high temperatures, fatigue cracks initiate and propagate inside the copper matrix through a process of initiation, growth, and coalescence of grain boundary cavities. The ductile tungsten fibers neck and rupture locally after the surrounding matrix fails, and complete failure of the composite then ensues. A simple fatigue life prediction model is presented for the tungsten/copper composite system.
Fatigue damage characterization of braided and woven fiber reinforced polymer matrix composites at room and elevated temperatures

NASA Astrophysics Data System (ADS)

Montesano, John

The use of polymer matrix composites (PMC) for manufacturing primary load-bearing structural components has significantly increased in many industrial applications. Specifically in the aerospace industry, PMCs are also being considered for elevated temperature applications. Current aerospace-grade composite components subjected to fatigue loading are over-designed due to insufficient understanding of the material failure processes, and due to the lack of available generic fatigue prediction models. A comprehensive literature survey reveals that there are few fatigue studies conducted on woven and braided fabric reinforced PMC materials, and even fewer at elevated temperatures. It is therefore the objective of this study to characterize and subsequently model the elevated temperature fatigue behaviour of a triaxial braided PMC, and to investigate the elevated temperature fatigue properties of two additional woven PMCs. An extensive experimental program is conducted using a unique test protocol on the braided and woven composites, which consists of static and fatigue testing at various test temperatures. The development of mechanically-induced damage is monitored using a combination of non-destructive techniques which included infrared thermography, fiber optic sensors and edge replication. The observed microscopic damage development is quantified and correlated to the exhibited macroscopic material behaviour at all test temperatures. The fiber-dominated PMC materials considered in this study did not exhibit notable time- or temperature-dependent static properties. However, fatigue tests reveal that the local damage development is in fact notably influenced by temperature. The elevated temperature environment increases the toughness of the thermosetting polymers, which results in consistently slower fatigue crack propagation rates for the respective composite materials. This has a direct impact on the stiffness degradation rate and the fatigue lives for the braided and woven composites under investigation. The developed analytical fatigue damage prediction model, which is based on actual observed damage mechanisms, accurately predicted the development of damage and the corresponding stiffness degradation for the braided PMC, for all test temperatures. An excellent correlation was found between the experimental and the predicted results to within a 2% accuracy. The prediction model adequately captured the local temperature-induced phenomenon exhibited by the braided PMC material. The results presented in this study are novel for a braided composite material subjected to elevated temperature fatigue.

Development of a realistic stress analysis for fatigue analysis of notched composite laminates

NASA Technical Reports Server (NTRS)

Humphreys, E. A.; Rosen, B. W.

1979-01-01

A finite element stress analysis which consists of a membrane and interlaminar shear spring analysis was developed. This approach was utilized in order to model physically realistic failure mechanisms while maintaining a high degree of computational economy. The accuracy of the stress analysis predictions is verified through comparisons with other solutions to the composite laminate edge effect problem. The stress analysis model was incorporated into an existing fatigue analysis methodology and the entire procedure computerized. A fatigue analysis is performed upon a square laminated composite plate with a circular central hole. A complete description and users guide for the computer code FLAC (Fatigue of Laminated Composites) is included as an appendix.
Tensile strength of composite sheets with unidirectional stringers and crack-like damage

NASA Technical Reports Server (NTRS)

Poe, C. C., Jr.

1984-01-01

The damage tolerance characteristics of metal tension panels with riveted and bonded stringers are well known. The stringers arrest unstable cracks and retard propagation of fatigue cracks. Residual strengths and fatigue lives are considerably greater than those of unstiffened or integrally stiffened sheets. The damage tolerance of composite sheets with bonded composite stringers loaded in tension was determined. Cracks in composites do not readily propagate in fatigue, at least not through fibers. Moreover, the residual strength of notched composites is sometimes even increased by fatigue loading. Therefore, the residual strength aspect of damage tolerance, and not fatigue crack propagation, was investigated. About 50 graphite/epoxy composite panels were made with two sheet layups and several stringer configurations. Crack-like slots were cut in the middle of the panels to simulate damage. The panels were instrumented and monotonically loaded in tension to failure. The tests indicate that the composite panels have considerable damage tolerance, much like metal panels. The stringers arrested cracks that ran from the crack-like slots, and the residual strengths were considerably greater than those of unstiffened composite sheets. A stress intensity factor analysis was developed to predict the failing strains of the stiffened panels. Using the analysis, a single design curve was produced for composite sheets with bonded stringers of any configuration.
An evaluation of fatigue limit of notched specimen of a C/C composite

NASA Astrophysics Data System (ADS)

Makabe, C.; Fujikawa, M.; Ferdous, M. S.

2018-06-01

The fatigue strengths in notched specimens of carbon fiber reinforced carbon composites (C/C composites) were investigated. The fatigue limit was measured by S-N curves and load increase tests. The value of fatigue limit obtained by those methods was almost the same. Slits of several sizes were cut on both sides of a test section, and different sizes of slit length were chosen. Also, specimens with blunt-notches were used to compare the fatigue strength. The weakest fatigue limit was obtained in the case of specimens with blunt-notches. However, the stress concentration factor of those is smaller than that of slit specimens. The relationships between fatigue strengths and specimen shapes were analyzed by stress distribution. The effect of slit configuration on fatigue strength was then discussed regarding the experimental consequences. Consequently, it was discussed that the fatigue strength of the present specimens was determined depending on the damage conditions in the vicinity of the notch and on the crack initiation behavior. It is expected that the tendency of the S-N curve and fatigue limit was related to the shear damage and shear mode of the crack growth.
Research on graphite reinforced glass matrix composites

NASA Technical Reports Server (NTRS)

Prewo, K. M.; Thompson, E. R.

1981-01-01

A broad group of fibers and matrices were combined to create a wide range of composite properties. Primary material fabrication procedures were developed which readily permit the fabrication of flat plate and shaped composites. Composite mechanical properties were measured under a wide range of test conditions. Tensile, flexure mechanical fatigue, thermal fatigue, fracture toughness, and fatigue crack growth resistance were evaluated. Selected fiber-matrix combinations were shown to maintain their strength at up to 1300 K when tested in an inert atmosphere. Composite high temperature mechanical properties were shown to be limited primarily by the oxidation resistance of the graphite fibers. Composite thermal dimensional stability was measured and found to be excellent.
Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under strain controlled mode. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Dennis, L.B.

1994-12-01

This research extends the existing knowledge of cross-ply metal matrix composites (MMC) to include fatigue behavior under strain-controlled fully reversed loading. This study investigated fatigue life, failure modes and damage mechanisms of the SCS-6/Ti-15-3, (O/9O)2s, MMC. The laminate was subjected to fully reversed fatigue at elevated temperature (427 deg C) at various strain levels. Stress, strain and modulus data were analyzed to characterize the macro-mechanical behavior of the composite. Microscopy and fractography were accomplished to identify and characterize the damage mechanisms at the microscopic level. Failure modes varied according to the maximum applied strain level showing either mixed mode (i.e.more » combination of both fiber and matrix dominated modes) or matrix dominated fatigue failures. As expected, higher strain loadings resulted in more ductility of the matrix at failure, evidenced by fracture surface features. For testing of the same composite laminate, the fatigue life under strain controlled mode slightly increased, compared to its load-controlled mode counterpart, using the effective strain range comparison basis. However, the respective fatigue life curves converged in the high cycle region, suggesting that the matrix dominated failure mode produces equivalent predicted fatigue lives for both control modes.« less
Advanced composite stabilizer for Boeing 737 aircraft

NASA Technical Reports Server (NTRS)

1978-01-01

Activities related to development of an advanced composites stabilizer for the Boeing 737 commercial transport are reported. Activities include discussion of criteria and objectives, design loads, the fatigue spectrum definition to be used for all spectrum fatigue testing, fatigue analysis, manufacturing producibility studies, the ancillary test program, quality assurance, and manufacturing development.
A differential CDM model for fatigue of unidirectional metal matrix composites

NASA Technical Reports Server (NTRS)

Arnold, S. M.; Kruch, S.

1992-01-01

A multiaxial, isothermal, continuum damage mechanics (CDM) model for fatigue of a unidirectional metal matrix composite volume element is presented. The model is phenomenological, stress based, and assumes a single scalar internal damage variable, the evolution of which is anisotropic. The development of the fatigue damage model, (i.e., evolutionary law) is based on the definition of an initially transversely isotropic fatigue limit surface, a static fracture surface, and a normalized stress amplitude function. The anisotropy of these surfaces and function, and therefore the model, is defined through physically meaningful invariants reflecting the local stress and material orientation. This transversely isotropic model is shown, when taken to it's isotropic limit, to directly simplify to a previously developed and validated isotropic fatigue continuum damage model. Results of a nondimensional parametric study illustrate (1) the flexibility of the present formulation in attempting to characterize a class of composite materials, and (2) the capability of the formulation in predicting anticipated qualitative trends in the fatigue behavior of unidirectional metal matrix composites. Also, specific material parameters representing an initial characterization of the composite system SiC/Ti 15-3 and the matrix material (Ti 15-3) are reported.
Monitoring Poisson's Ratio Degradation of FRP Composites under Fatigue Loading Using Biaxially Embedded FBG Sensors.

PubMed

Akay, Erdem; Yilmaz, Cagatay; Kocaman, Esat S; Turkmen, Halit S; Yildiz, Mehmet

2016-09-19

The significance of strain measurement is obvious for the analysis of Fiber-Reinforced Polymer (FRP) composites. Conventional strain measurement methods are sufficient for static testing in general. Nevertheless, if the requirements exceed the capabilities of these conventional methods, more sophisticated techniques are necessary to obtain strain data. Fiber Bragg Grating (FBG) sensors have many advantages for strain measurement over conventional ones. Thus, the present paper suggests a novel method for biaxial strain measurement using embedded FBG sensors during the fatigue testing of FRP composites. Poisson's ratio and its reduction were monitored for each cyclic loading by using embedded FBG sensors for a given specimen and correlated with the fatigue stages determined based on the variations of the applied fatigue loading and temperature due to the autogenous heating to predict an oncoming failure of the continuous fiber-reinforced epoxy matrix composite specimens under fatigue loading. The results show that FBG sensor technology has a remarkable potential for monitoring the evolution of Poisson's ratio on a cycle-by-cycle basis, which can reliably be used towards tracking the fatigue stages of composite for structural health monitoring purposes.
Monitoring Poisson’s Ratio Degradation of FRP Composites under Fatigue Loading Using Biaxially Embedded FBG Sensors

PubMed Central

Akay, Erdem; Yilmaz, Cagatay; Kocaman, Esat S.; Turkmen, Halit S.; Yildiz, Mehmet

2016-01-01

The significance of strain measurement is obvious for the analysis of Fiber-Reinforced Polymer (FRP) composites. Conventional strain measurement methods are sufficient for static testing in general. Nevertheless, if the requirements exceed the capabilities of these conventional methods, more sophisticated techniques are necessary to obtain strain data. Fiber Bragg Grating (FBG) sensors have many advantages for strain measurement over conventional ones. Thus, the present paper suggests a novel method for biaxial strain measurement using embedded FBG sensors during the fatigue testing of FRP composites. Poisson’s ratio and its reduction were monitored for each cyclic loading by using embedded FBG sensors for a given specimen and correlated with the fatigue stages determined based on the variations of the applied fatigue loading and temperature due to the autogenous heating to predict an oncoming failure of the continuous fiber-reinforced epoxy matrix composite specimens under fatigue loading. The results show that FBG sensor technology has a remarkable potential for monitoring the evolution of Poisson’s ratio on a cycle-by-cycle basis, which can reliably be used towards tracking the fatigue stages of composite for structural health monitoring purposes. PMID:28773901
Nonlinear Acoustic and Ultrasonic NDT of Aeronautical Components

NASA Astrophysics Data System (ADS)

Van Den Abeele, Koen; Katkowski, Tomasz; Mattei, Christophe

2006-05-01

In response to the demand for innovative microdamage inspection systems, with high sensitivity and undoubted accuracy, we are currently investigating the use and robustness of several acoustic and ultrasonic NDT techniques based on Nonlinear Elastic Wave Spectroscopy (NEWS) for the characterization of microdamage in aeronautical components. In this report, we illustrate the results of an amplitude dependent analysis of the resonance behaviour, both in time (signal reverberation) and in frequency (sweep) domain. The technique is applied to intact and damaged samples of Carbon Fiber Reinforced Plastics (CFRP) composites after thermal loading or mechanical fatigue. The method shows a considerable gain in sensitivity and an incontestable interpretation of the results for nonlinear signatures in comparison with the linear characteristics. For highly fatigued samples, slow dynamical effects are observed.
Fatigue resistance and crack propensity of large MOD composite resin restorations: direct versus CAD/CAM inlays.

PubMed

Batalha-Silva, Silvana; de Andrada, Mauro Amaral Caldeira; Maia, Hamilton Pires; Magne, Pascal

2013-03-01

To assess the influence of material/technique selection (direct vs. CAD/CAM inlays) for large MOD composite adhesive restorations and its effect on the crack propensity and in vitro accelerated fatigue resistance. A standardized MOD slot-type tooth preparation was applied to 32 extracted maxillary molars (5mm depth and 5mm bucco-palatal width) including immediately sealed dentin for the inlay group. Fifteen teeth were restored with direct composite resin restoration (Miris2) and 17 teeth received milled inlays using Paradigm MZ100 block in the CEREC machine. All inlays were adhesively luted with a light curing composite resin (Filtek Z100). Enamel shrinkage-induced cracks were tracked with photography and transillumination. Cyclic isometric chewing (5 Hz) was simulated, starting with a load of 200 N (5000 cycles), followed by stages of 400, 600, 800, 1000, 1200 and 1400 N at a maximum of 30,000 cycles each. Samples were loaded until fracture or to a maximum of 185,000 cycles. Teeth restored with the direct technique fractured at an average load of 1213 N and two of them withstood all loading cycles (survival=13%); with inlays, the survival rate was 100%. Most failures with Miris2 occurred above the CEJ and were re-restorable (67%), but generated more shrinkage-induced cracks (47% of the specimen vs. 7% for inlays). CAD/CAM MZ100 inlays increased the accelerated fatigue resistance and decreased the crack propensity of large MOD restorations when compared to direct restorations. While both restorative techniques yielded excellent fatigue results at physiological masticatory loads, CAD/CAM inlays seem more indicated for high-load patients. Copyright © 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Composite structural materials

NASA Technical Reports Server (NTRS)

Ansell, G. S.; Loewy, R. G.; Wiberley, S. E.

1983-01-01

Progress and plans are reported for investigations of: (1) the mechanical properties of high performance carbon fibers; (2) fatigue in composite materials; (3) moisture and temperature effects on the mechanical properties of graphite-epoxy laminates; (4) the theory of inhomogeneous swelling in epoxy resin; (5) numerical studies of the micromechanics of composite fracture; (6) free edge failures of composite laminates; (7) analysis of unbalanced laminates; (8) compact lug design; (9) quantification of Saint-Venant's principles for a general prismatic member; (10) variation of resin properties through the thickness of cured samples; and (11) the wing fuselage ensemble of the RP-1 and RP-2 sailplanes.
Frequency dependence of fatigue life and internal heating of a fiber-reinforced/ceramic-matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Holmes, J.W.; Wu, X.; Sorensen, B.F.

The influence of loading frequency on the fatigue life and internal (frictional) heating of unidirectional SiC-fiber/calcium aluminosilicate-matrix composites was investigated at room temperature. Specimens were subjected to tension-tension fatigue at sinusoidal loading frequencies from 25 to 350 Hz and maximum fatigue stresses of 180 to 240 MPa. The key findings of the study were that (1) fatigue life decreased sharply as the loading frequency was increased, (2) for all loading frequencies, fatigue failures occurred at stress levels that were significantly below the monotonic proportional limit stress if [approximately]285 MPa, and (3) pronounced internal heating occurred during fatigue, with the surfacemore » temperature of the fatigue specimens increasing by 160 K during 350-Hz fatigue at a peak stress of 240 MPa.« less
Fatigue testing and damage development in continuous fiber reinforced metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1988-01-01

A general overview of the fatigue behavior of metal matrix composites (MMC) is presented. The first objective is to present experimental procedures and techniques for conducting a meaningful fatigue test to detect and quantify fatigue damage in MMC. These techniques include interpretation of stress-strain responses, acid etching of the matrix, edge replicas of the specimen under load, radiography, and micrographs of the failure surfaces. In addition, the paper will show how stiffness loss in continuous fiber reinforced metal matrix composites can be a useful parameter for detecting fatigue damage initiation and accumulation. Second, numerous examples of how fatigue damage can initiate and grow in various MMC are given. Depending on the relative fatigue behavior of the fiber and matrix, and the interface properties, the failure modes of MMC can be grouped into four categories: (1) matrix dominated, (2) fiber dominated, (3) self-similar damage growth, and (4) fiber/matrix interfacial failures. These four types of damage will be discussed and illustrated by examples with the emphasis on the fatigue of unnotched laminates.
Fatigue testing and damage development in continuous fiber reinforced metal matrix composites

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1989-01-01

A general overview of the fatigue behavior of metal matrix composites (MMC) is presented. The first objective is to present experimental procedures and techniques for conducting a meaningful fatigue test to detect and quantify fatigue damage in MMC. These techniques include interpretation of stress-strain responses, acid etching of the matrix, edge replicas of the specimen under load, radiography, and micrographs of the failure surfaces. In addition, the paper will show how stiffness loss in continuous fiber reinforced metal matrix composites can be a useful parameter for detecting fatigue damage initiation and accumulation. Second, numerous examples of how fatigue damage can initiate and grow in various MMC are given. Depending on the relative fatigue behavior of the fiber and matrix, and the interface properties, the failure modes of MMC can be grouped into four categories: (1) matrix dominated, (2) fiber dominated, (3) self-similar damage growth, and (4) fiber/matrix interfacial failures. These four types of damage will be discussed and illustrated by examples with the emphasis on the fatigue of unnotched laminates.
A Fatigue Model for Discontinuous Particulate-Reinforced Aluminum Alloy Composite: Influence of Microstructure

NASA Astrophysics Data System (ADS)

McCullough, R. R.; Jordon, J. B.; Brammer, A. T.; Manigandan, K.; Srivatsan, T. S.; Allison, P. G.; Rushing, T. W.

2014-01-01

In this paper, the use of a microstructure-sensitive fatigue model is put forth for the analysis of discontinuously reinforced aluminum alloy metal matrix composite. The fatigue model was used for a ceramic particle-reinforced aluminum alloy deformed under conditions of fully reversed strain control. Experimental results revealed the aluminum alloy to be strongly influenced by volume fraction of the particulate reinforcement phase under conditions of strain-controlled fatigue. The model safely characterizes the evolution of fatigue damage in this aluminum alloy composite into the distinct stages of crack initiation and crack growth culminating in failure. The model is able to capture the specific influence of particle volume fraction, particle size, and nearest neighbor distance in quantifying fatigue life. The model yields good results for correlation of the predicted results with the experimental test results on the fatigue behavior of the chosen aluminum alloy for two different percentages of the ceramic particle reinforcement. Further, the model illustrates that both particle size and volume fraction are key factors that govern fatigue lifetime. This conclusion is well supported by fractographic observations of the cyclically deformed and failed specimens.
Multiscale Fatigue Life Prediction for Composite Panels

NASA Technical Reports Server (NTRS)

Bednarcyk, Brett A.; Yarrington, Phillip W.; Arnold, Steven M.

2012-01-01

Fatigue life prediction capabilities have been incorporated into the HyperSizer Composite Analysis and Structural Sizing Software. The fatigue damage model is introduced at the fiber/matrix constituent scale through HyperSizer s coupling with NASA s MAC/GMC micromechanics software. This enables prediction of the micro scale damage progression throughout stiffened and sandwich panels as a function of cycles leading ultimately to simulated panel failure. The fatigue model implementation uses a cycle jumping technique such that, rather than applying a specified number of additional cycles, a specified local damage increment is specified and the number of additional cycles to reach this damage increment is calculated. In this way, the effect of stress redistribution due to damage-induced stiffness change is captured, but the fatigue simulations remain computationally efficient. The model is compared to experimental fatigue life data for two composite facesheet/foam core sandwich panels, demonstrating very good agreement.
Characterization of failure processes in tungsten copper composites under fatigue loading conditions

NASA Technical Reports Server (NTRS)

Kim, Yong-Suk; Verrilli, Michael J.; Gabb, Timothy P.

1989-01-01

A fractographic and metallographic investigation was performed on specimens of a tungsten fiber reinforced copper matrix composite (9 vol percent), which had experienced fatigue failures at elevated temperatures. Major failure modes and possible failure mechanisms, with an emphasis placed on characterizing fatigue damage accumulation, were determined. Metallography of specimens fatigued under isothermal cyclic loading suggested that fatigue damage initiates in the matrix. Cracks nucleated within the copper matrix at grain boundaries, and they propagated through cavity coalescence. The growing cracks subsequently interacted with the reinforcing tungsten fibers, producing a localized ductile fiber failure. Examinations of interrupted tests before final failure confirmed the suggested fatigue damage processes.
The Role of Viscoelasticity on the Fatigue of Angle-ply Polymer Matrix Composites at High and Room Temperatures- A Micromechanical Approach

NASA Astrophysics Data System (ADS)

Sayyidmousavi, Alireza; Bougherara, Habiba; Fawaz, Zouheir

2015-06-01

A micromechanical approach is adopted to study the role of viscoelasticity on the fatigue behavior of polymer matrix composites. In particular, the study examines the interaction of fatigue and creep in angle ply carbon/epoxy at 25 and 114 °C. The matrix phase is modeled as a vicoelastic material using Schapery's single integral constitutive equation. Taking viscoelsticity into account allows the study of creep strain evolution during the fatigue loading. The fatigue failure criterion is expressed in terms of the fatigue failure functions of the constituent materials. The micromechanical model is also used to calculate these fatigue failure functions from the knowledge of the S-N diagrams of the composite material in longitudinal, transverse and shear loadings thus eliminating the need for any further experimentation. Unlike the previous works, the present study can distinguish between the strain evolution due to fatigue and creep. The results can clearly show the contribution made by the effect of viscoelasticity to the total strain evolution during the fatigue life of the specimen. Although the effect of viscoelsticity is found to increase with temperature, its contribution to strain development during fatigue is compromised by the shorter life of the specimen when compared to lower temperatures.
Fatigue of a 3D Orthogonal Non-crimp Woven Polymer Matrix Composite at Elevated Temperature

NASA Astrophysics Data System (ADS)

Wilkinson, M. P.; Ruggles-Wrenn, M. B.

2017-12-01

Tension-tension fatigue behavior of two polymer matrix composites (PMCs) was studied at elevated temperature. The two PMCs consist of the NRPE polyimide matrix reinforced with carbon fibers, but have different fiber architectures: the 3D PMC is a singly-ply non-crimp 3D orthogonal weave composite and the 2D PMC, a laminated composite reinforced with 15 plies of an eight harness satin weave (8HSW) fabric. In order to assess the performance and suitability of the two composites for use in aerospace components designed to contain high-temperature environments, mechanical tests were performed under temperature conditions simulating the actual operating conditions. In all elevated temperature tests performed in this work, one side of the test specimen was at 329 °C while the other side was open to ambient laboratory air. The tensile stress-strain behavior of the two composites was investigated and the tensile properties measured for both on-axis (0/90) and off-axis (±45) fiber orientations. Elevated temperature had little effect on the on-axis tensile properties of the two composites. The off-axis tensile strength of both PMCs decreased slightly at elevated temperature. Tension-tension fatigue tests were conducted at elevated temperature at a frequency of 1.0 Hz with a ratio of minimum stress to maximum stress of R = 0.05. Fatigue run-out was defined as 2 × 105 cycles. Both strain accumulation and modulus evolution during cycling were analyzed for each fatigue test. The laminated 2D PMC exhibited better fatigue resistance than the 3D composite. Specimens that achieved fatigue run-out were subjected to tensile tests to failure to characterize the retained tensile properties. Post-test examination under optical microscope revealed severe delamination in the laminated 2D PMC. The non-crimp 3D orthogonal weave composite offered improved delamination resistance.

Impact and residual fatigue behavior of ARALL and AS6/5245 composite materials

NASA Technical Reports Server (NTRS)

Johnson, W. S.

1986-01-01

Aramide fiber reinforced aluminum laminates (ARALL) represent a cross between resin matrix composites and metals. The purpose of this study was to evaluate the impact sensitivity of this concept. Two types of ARALL (7075 aluminum prestrained and 2024 aluminum not prestrained) were tested through static indentation and the results compared to sheet 2024-T3 and 7075-T6 aluminum alloys. A state-of-the-art composite (AS6/5245) was also tested and compared to the ARALL. Further, the two types of ARALL material and the composite were dynamically impacted at two energy levels and fatigue tested to determine residual fatigue strength. Both forms of the ARALL material had worse impact resistance than monolithic sheet aluminum. The ARALL material made with 2024-T3 aluminum had better impact resistance than did the laminates made with 7075-T6 aluminum. The ARALL materials are at least equal to the composite material in impact damage resistance and are better for impact detection. The composite material has higher residual fatigue strength after impact than the ARALL material and is 25 percent lighter. The prestraining of the ARALL greatly reduces the fatigue growth of impact damage.
A creep cavity growth model for creep-fatigue life prediction of a unidirectional W/Cu composite

NASA Astrophysics Data System (ADS)

Kim, Young-Suk; Verrilli, Michael J.; Halford, Gary R.

1992-05-01

A microstructural model was developed to predict creep-fatigue life in a (0)(sub 4), 9 volume percent tungsten fiber-reinforced copper matrix composite at the temperature of 833 K. The mechanism of failure of the composite is assumed to be governed by the growth of quasi-equilibrium cavities in the copper matrix of the composite, based on the microscopically observed failure mechanisms. The methodology uses a cavity growth model developed for prediction of creep fracture. Instantaneous values of strain rate and stress in the copper matrix during fatigue cycles were calculated and incorporated in the model to predict cyclic life. The stress in the copper matrix was determined by use of a simple two-bar model for the fiber and matrix during cyclic loading. The model successfully predicted the composite creep-fatigue life under tension-tension cyclic loading through the use of this instantaneous matrix stress level. Inclusion of additional mechanisms such as cavity nucleation, grain boundary sliding, and the effect of fibers on matrix-stress level would result in more generalized predictions of creep-fatigue life.
Analytical and experimental investigation of aircraft metal structures reinforced with filamentary composites. Phase 2: Structural fatigue, thermal cycling, creep, and residual strength

NASA Technical Reports Server (NTRS)

Blichfeldt, B.; Mccarty, J. E.

1972-01-01

Specimens representative of metal aircraft structural components reinforced with boron filamentary composites were manufactured and tested under cyclic loading, cyclic temperature, or continuously applied loading to evaluate some of the factors that affect structural integrity under cyclic conditions. Bonded, stepped joints were used throughout to provide composite-to-metal transition regions at load introduction points. Honeycomb panels with titanium or aluminum faces reinforced with unidirectional boron composite were fatigue tested at constant amplitude under completely reversed loading. Results indicated that the matrix material was the most fatigue-sensitive part of the design, with debonding initiating in the stepped joints. However, comparisons with equal weight all-metal specimens show a 10 to 50 times improved fatigue life. Fatigue crack propagation and residual strength were studied for several different stiffened panel concepts, and were found to vary considerably depending on the configuration. Composite-reinforced metal specimens were also subjected to creep and thermal cycling tests. Thermal cycling of stepped joint tensile specimens resulted in a ten percent decrease in residual strength after 4000 cycles.
A creep cavity growth model for creep-fatigue life prediction of a unidirectional W/Cu composite

NASA Technical Reports Server (NTRS)

Kim, Young-Suk; Verrilli, Michael J.; Halford, Gary R.

1992-01-01

A microstructural model was developed to predict creep-fatigue life in a (0)(sub 4), 9 volume percent tungsten fiber-reinforced copper matrix composite at the temperature of 833 K. The mechanism of failure of the composite is assumed to be governed by the growth of quasi-equilibrium cavities in the copper matrix of the composite, based on the microscopically observed failure mechanisms. The methodology uses a cavity growth model developed for prediction of creep fracture. Instantaneous values of strain rate and stress in the copper matrix during fatigue cycles were calculated and incorporated in the model to predict cyclic life. The stress in the copper matrix was determined by use of a simple two-bar model for the fiber and matrix during cyclic loading. The model successfully predicted the composite creep-fatigue life under tension-tension cyclic loading through the use of this instantaneous matrix stress level. Inclusion of additional mechanisms such as cavity nucleation, grain boundary sliding, and the effect of fibers on matrix-stress level would result in more generalized predictions of creep-fatigue life.
Comparison of Elevated Temperature Tensile Properties and Fatigue Behavior of Two Variants of a Woven SiC/SiC Composite

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Brewer, David N.; Sreeramesh, Kalluri

2005-01-01

Tensile properties (elastic modulus, proportional limit strength, in-plane tensile strength, and strain at failure) of two variants of a woven SiC/SiC composite, manufactured during two separate time periods (9/99 and 1/01), were determined at 1038 and 1204 C by conducting tensile tests on specimens machined from plates. Continuous cycling fatigue tests (R = 0.05) and 20 cpm) were also conducted at the same two temperatures on specimens from both composites. In this study, average tensile properties, 95% confidence intervals associated with the tensile properties, and geometric mean fatigue lives of both composite materials are compared. The observed similarities and differences in the tensile properties are highlighted and an attempt is made to understand the relationship, if any, between the tensile properties and the fatigue behaviors of the two woven composites.
Thermomechanical Fatigue Behavior of a Silicon Carbide Fiber-Reinforced Calcium Aluminosilicate Glass-Ceramic Matrix Composite.

DTIC Science & Technology

1992-08-01

space applications. Prior to being used to replace current metal superalloys and monolithic ceramics, the mechanical and thermal properties of CMCs...many investigations of the general mechanical properties of ceramic composites have been performed (see sources 2-10 for a briej sampling), the room...Review of Materials Science, Vol. 17, 1987, pp. 341-383. 7 Thouless, M.D., and Evans, A.G., "Effects of Pull-Out on the Mechanical Properties of
Failure of a laminated composite under tension-compression fatigue loading

NASA Technical Reports Server (NTRS)

Rotem, A.; Nelson, H. G.

1989-01-01

The fatigue behavior of composite laminates under tension-compression loading is analyzed and compared with behavior under tension-tension and compression-compression loading. It is shown that for meaningful fatigue conditions, the tension-compression case is the dominant one. Both tension and compression failure modes can occur under the reversed loading, and failure is dependent on the specific lay-up of the laminate and the difference between the tensile static strength and the absolute value of the compressive static strength. The use of a fatigue failure envelope for determining the fatigue life and mode of failure is proposed and demonstrated.
Occupation-specific screening for future sickness absence: criterion validity of the trucker strain monitor (TSM).

PubMed

De Croon, Einar M; Blonk, Roland W B; Sluiter, Judith K; Frings-Dresen, Monique H W

2005-02-01

Monitoring psychological job strain may help occupational physicians to take preventive action at the appropriate time. For this purpose, the 10-item trucker strain monitor (TSM) assessing work-related fatigue and sleeping problems in truck drivers was developed. This study examined (1) test-retest reliability, (2) criterion validity of the TSM with respect to future sickness absence due to psychological health complaints and (3) usefulness of the TSM two-scales structure. The TSM and self-administered questionnaires, providing information about stressful working conditions (job control and job demands) and sickness absence, were sent to a random sample of 2000 drivers in 1998. Of the 1123 responders, 820 returned a completed questionnaire 2 years later (response: 72%). The TSM work-related fatigue scale, the TSM sleeping problems scale and the TSM composite scale showed satisfactory 2-year test-retest reliability (coefficient r=0.62, 0.66 and 0.67, respectively). The work-related fatigue, sleeping problems scale and composite scale had sensitivities of 61, 65 and 61%, respectively in identifying drivers with future sickness absence due to psychological health complaints. The specificity and positive predictive value of the TSM composite scale were 77 and 11%, respectively. The work-related fatigue scale and the sleeping problems scale were moderately strong correlated (r=0.62). However, stressful working conditions were differentially associated with the two scales. The results support the test-retest reliability, criterion validity and two-factor structure of the TSM. In general, the results suggest that the use of occupation-specific psychological job strain questionnaires is fruitful.
Damage Evolution and Life Prediction of Cross-Ply C/SiC Ceramic-Matrix Composite under Cyclic Fatigue Loading at Room Temperature and 800 °C in Air

PubMed Central

Li, Longbiao

2015-01-01

The damage evolution and life prediction of cross-ply C/SiC ceramic-matrix composite (CMC) under cyclic-fatigue loading at room temperature and 800 °C in air have been investigated using damage parameters derived from fatigue hysteresis loops, i.e., fatigue hysteresis modulus and fatigue hysteresis loss energy. The experimental fatigue hysteresis modulus and fatigue hysteresis loss energy degrade with increasing applied cycles attributed to transverse cracks in the 90° plies, matrix cracks and fiber/matrix interface debonding in the 0° plies, interface wear at room temperature, and interface and carbon fibers oxidation at 800 °C in air. The relationships between fatigue hysteresis loops, fatigue hysteresis modulus and fatigue hysteresis loss energy have been established. Comparing experimental fatigue hysteresis loss energy with theoretical computational values, the fiber/matrix interface shear stress corresponding to different cycle numbers has been estimated. It was found that the degradation rate at 800 °C in air is much faster than that at room temperature due to serious oxidation in the pyrolytic carbon (PyC) interphase and carbon fibers. Combining the fiber fracture model with the interface shear stress degradation model and the fibers strength degradation model, the fraction of broken fibers versus the cycle number can be determined for different fatigue peak stresses. The fatigue life S-N curves of cross-ply C/SiC composite at room temperature and 800 °C in air have been predicted. PMID:28793728
Damage Evolution and Life Prediction of Cross-Ply C/SiC Ceramic-Matrix Composite under Cyclic Fatigue Loading at Room Temperature and 800 °C in Air.

PubMed

Li, Longbiao

2015-12-09

The damage evolution and life prediction of cross-ply C/SiC ceramic-matrix composite (CMC) under cyclic-fatigue loading at room temperature and 800 °C in air have been investigated using damage parameters derived from fatigue hysteresis loops, i.e. , fatigue hysteresis modulus and fatigue hysteresis loss energy. The experimental fatigue hysteresis modulus and fatigue hysteresis loss energy degrade with increasing applied cycles attributed to transverse cracks in the 90° plies, matrix cracks and fiber/matrix interface debonding in the 0° plies, interface wear at room temperature, and interface and carbon fibers oxidation at 800 °C in air. The relationships between fatigue hysteresis loops, fatigue hysteresis modulus and fatigue hysteresis loss energy have been established. Comparing experimental fatigue hysteresis loss energy with theoretical computational values, the fiber/matrix interface shear stress corresponding to different cycle numbers has been estimated. It was found that the degradation rate at 800 °C in air is much faster than that at room temperature due to serious oxidation in the pyrolytic carbon (PyC) interphase and carbon fibers. Combining the fiber fracture model with the interface shear stress degradation model and the fibers strength degradation model, the fraction of broken fibers versus the cycle number can be determined for different fatigue peak stresses. The fatigue life S-N curves of cross-ply C/SiC composite at room temperature and 800 °C in air have been predicted.
Fracture and fatigue of discontinuously reinforced copper/tungsten composites

NASA Technical Reports Server (NTRS)

Harris, B.; Ramani, S. V.

1975-01-01

The strength, toughness and resistance to cyclic crack propagation of composites consisting of copper reinforced with short tungsten wires of various lengths have been studied and the results compared with the behavior of continuously reinforced composites manufactured by the same method, i.e., by vacuum hot-pressing. It has been found that whereas the resistance to fatigue crack growth of continuously reinforced composites is very similar to that of continuous Al/stainless steel composites reported elsewhere, the addition of short fibers completely changes the mode of fracture, and no direct comparisons are possible. In effect, short fibers inhibit single crack growth by causing plastic flow to be distributed rather than localized, and although these composites are much less strong than continuous fiber composites, they nevertheless have much greater fatigue resistance.
Failure models for textile composites

NASA Technical Reports Server (NTRS)

Cox, Brian

1995-01-01

The goals of this investigation were to: (1) identify mechanisms of failure and determine how the architecture of reinforcing fibers in 3D woven composites controlled stiffness, strength, strain to failure, work of fracture, notch sensitivity, and fatigue life; and (2) to model composite stiffness, strength, and fatigue life. A total of 11 different angle and orthogonal interlock woven composites were examined. Composite properties depended on the weave architecture, the tow size, and the spatial distributions and strength of geometrical flaws. Simple models were developed for elastic properties, strength, and fatigue life. A more complicated stochastic model, called the 'Binary Model,' was developed for damage tolerance and ultimate failure. These 3D woven composites possessed an extraordinary combination of strength, damage tolerance, and notch insensitivity.
14 CFR 29.573 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures.

Code of Federal Regulations, 2012 CFR

2012-01-01

... Composite Rotorcraft Structures. 29.573 Section 29.573 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION... Structures. (a) Each applicant must evaluate the composite rotorcraft structure under the damage tolerance..., types, and sizes of damage, considering fatigue, environmental effects, intrinsic and discrete flaws...
14 CFR 27.573 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures.

Code of Federal Regulations, 2012 CFR

2012-01-01

... Composite Rotorcraft Structures. 27.573 Section 27.573 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION... Structures. (a) Each applicant must evaluate the composite rotorcraft structure under the damage tolerance..., types, and sizes of damage, considering fatigue, environmental effects, intrinsic and discrete flaws...
14 CFR 27.573 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures.

Code of Federal Regulations, 2013 CFR

2013-01-01

... Composite Rotorcraft Structures. 27.573 Section 27.573 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION... Structures. (a) Each applicant must evaluate the composite rotorcraft structure under the damage tolerance..., types, and sizes of damage, considering fatigue, environmental effects, intrinsic and discrete flaws...
14 CFR 29.573 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures.

Code of Federal Regulations, 2013 CFR

2013-01-01

... Composite Rotorcraft Structures. 29.573 Section 29.573 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION... Structures. (a) Each applicant must evaluate the composite rotorcraft structure under the damage tolerance..., types, and sizes of damage, considering fatigue, environmental effects, intrinsic and discrete flaws...
14 CFR 27.573 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures.

Code of Federal Regulations, 2014 CFR

2014-01-01

... Composite Rotorcraft Structures. 27.573 Section 27.573 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION... Structures. (a) Each applicant must evaluate the composite rotorcraft structure under the damage tolerance..., types, and sizes of damage, considering fatigue, environmental effects, intrinsic and discrete flaws...
14 CFR 29.573 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures.

Code of Federal Regulations, 2014 CFR

2014-01-01

... Composite Rotorcraft Structures. 29.573 Section 29.573 Aeronautics and Space FEDERAL AVIATION ADMINISTRATION... Structures. (a) Each applicant must evaluate the composite rotorcraft structure under the damage tolerance..., types, and sizes of damage, considering fatigue, environmental effects, intrinsic and discrete flaws...
77 FR 60167 - Agency Information Collection Activities: Requests for Comments; Clearance of Renewed Approval of...

Federal Register 2010, 2011, 2012, 2013, 2014

2012-10-02

... and Fatigue Evaluation of Composite Rotorcraft Structures AGENCY: Federal Aviation Administration (FAA... Control Number: 2120-0753. Title: Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft... technology for composite rotorcraft structures. In order to show compliance and obtain type certification...
A Coupled/Uncoupled Computational Scheme for Deformation and Fatigue Damage Analysis of Unidirectional Metal-Matrix Composites

NASA Technical Reports Server (NTRS)

Wilt, Thomas E.; Arnold, Steven M.; Saleeb, Atef F.

1997-01-01

A fatigue damage computational algorithm utilizing a multiaxial, isothermal, continuum-based fatigue damage model for unidirectional metal-matrix composites has been implemented into the commercial finite element code MARC using MARC user subroutines. Damage is introduced into the finite element solution through the concept of effective stress that fully couples the fatigue damage calculations with the finite element deformation solution. Two applications using the fatigue damage algorithm are presented. First, an axisymmetric stress analysis of a circumferentially reinforced ring, wherein both the matrix cladding and the composite core were assumed to behave elastic-perfectly plastic. Second, a micromechanics analysis of a fiber/matrix unit cell using both the finite element method and the generalized method of cells (GMC). Results are presented in the form of S-N curves and damage distribution plots.

Compressive Strength of Notched Poly(Phenylene Sulfide) Aerospace Composite: Influence of Fatigue and Environment

NASA Astrophysics Data System (ADS)

Niitsu, G. T.; Lopes, C. M. A.

2013-08-01

The purpose of this work is to evaluate the influences of fatigue and environmental conditions (-55 °C, 23 °C, and 82 °C/Wet) on the ultimate compression strength of notched carbon-fiber-reinforced poly(phenylene sulfide) composites by performing open-hole compression (OHC) tests. Analysis of the fatigue effect showed that at temperatures of -55 and 23 °C, the ultimate OHC strengths were higher for fatigued than for not-fatigued specimens; this could be attributed to fiber splitting and delamination during fatigue cycling, which reduces the stress concentration at the hole edge, thus increasing the composite strength. This effect of increasing strength for fatigued specimens was not observed under the 82 °C/Wet conditions, since the test temperature near the matrix glass transition temperature ( T g) together with moisture content resulted in matrix softening, suggesting a reduction in fiber splitting during cycling; similar OHC strengths were verified for fatigued and not-fatigued specimens tested at 82 °C/Wet. Analysis of the temperature effect showed that the ultimate OHC strengths decreased with increasing temperature. A high temperature together with moisture content (82 °C/Wet condition) reduced the composite compressive strengths, since a temperature close to the matrix T g resulted in matrix softening, which reduced the lateral support provided by the resin to the 0° fibers, leading to fiber instability failure at reduced applied loads. On the other hand, a low temperature (-55 °C) improved the compressive strength because of possible fiber-matrix interfacial strengthening, increasing the fiber contribution to compressive strength.
A method for evaluating the fatigue crack growth in spiral notch torsion fracture toughness test

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wang, Jy -An John; Tan, Ting

The spiral notch torsion test (SNTT) has been a recent breakthrough in measuring fracture toughness for different materials, including metals, ceramics, concrete, and polymers composites. Due to its high geometry constraint and unique loading condition, SNTT can be used to measure the fracture toughness with smaller specimens without concern of size effects. The application of SNTT to brittle materials has been proved to be successful. The micro-cracks induced by original notches in brittle materials could ensure crack growth in SNTT samples. Therefore, no fatigue pre-cracks are needed. The application of SNTT to the ductile material to generate valid toughness datamore » will require a test sample with sufficient crack length. Fatigue pre-crack growth techniques are employed to introduce sharp crack front into the sample. Previously, only rough calculations were applied to estimate the compliance evolution in the SNTT crack growth process, while accurate quantitative descriptions have never been attempted. This generates an urgent need to understand the crack evolution during the SNTT fracture testing process of ductile materials. Here, the newly developed governing equations for SNTT crack growth estimate are discussed in the paper.« less
A method for evaluating the fatigue crack growth in spiral notch torsion fracture toughness test

DOE PAGES

Wang, Jy -An John; Tan, Ting

2018-05-21

The spiral notch torsion test (SNTT) has been a recent breakthrough in measuring fracture toughness for different materials, including metals, ceramics, concrete, and polymers composites. Due to its high geometry constraint and unique loading condition, SNTT can be used to measure the fracture toughness with smaller specimens without concern of size effects. The application of SNTT to brittle materials has been proved to be successful. The micro-cracks induced by original notches in brittle materials could ensure crack growth in SNTT samples. Therefore, no fatigue pre-cracks are needed. The application of SNTT to the ductile material to generate valid toughness datamore » will require a test sample with sufficient crack length. Fatigue pre-crack growth techniques are employed to introduce sharp crack front into the sample. Previously, only rough calculations were applied to estimate the compliance evolution in the SNTT crack growth process, while accurate quantitative descriptions have never been attempted. This generates an urgent need to understand the crack evolution during the SNTT fracture testing process of ductile materials. Here, the newly developed governing equations for SNTT crack growth estimate are discussed in the paper.« less
Response of SiC{sub f}/Si{sub 3}N{sub 4} composites under static and cyclic loading -- An experimental and statistical analysis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahfuz, H.; Maniruzzaman, M.; Vaidya, U.

1997-04-01

Monotonic tensile and fatigue response of continuous silicon carbide fiber reinforced silicon nitride (SiC{sub f}/Si{sub 3}N{sub 4}) composites has been investigated. The monotonic tensile tests have been performed at room and elevated temperatures. Fatigue tests have been conducted at room temperature (RT), at a stress ratio, R = 0.1 and a frequency of 5 Hz. It is observed during the monotonic tests that the composites retain only 30% of its room temperature strength at 1,600 C suggesting a substantial chemical degradation of the matrix at that temperature. The softening of the matrix at elevated temperature also causes reduction in tensilemore » modulus, and the total reduction in modulus is around 45%. Fatigue data have been generated at three load levels and the fatigue strength of the composite has been found to be considerably high; about 75% of its ultimate room temperature strength. Extensive statistical analysis has been performed to understand the degree of scatter in the fatigue as well as in the static test data. Weibull shape factors and characteristic values have been determined for each set of tests and their relationship with the response of the composites has been discussed. A statistical fatigue life prediction method developed from the Weibull distribution is also presented. Maximum Likelihood Estimator with censoring techniques and data pooling schemes has been employed to determine the distribution parameters for the statistical analysis. These parameters have been used to generate the S-N diagram with desired level of reliability. Details of the statistical analysis and the discussion of the static and fatigue behavior of the composites are presented in this paper.« less
Fatigue Life Prediction of 2D Woven Ceramic-Matrix Composites at Room and Elevated Temperatures

NASA Astrophysics Data System (ADS)

Longbiao, Li

2017-03-01

In this paper, the fatigue life of 2D woven ceramic-matrix composites, i.e., SiC/SiC, SiC/Si-N-C, SiC/Si-B4C, and Nextel 610™/Aluminosilicate, at room and elevated temperatures has been predicted using the micromechanics approach. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. The Budiansky-Hutchinson-Evans shear-lag model was used to describe the microstress field of the damaged composite considering fibers failure. The statistical matrix multicracking model and fracture mechanics interface debonding criterion were used to determine the matrix crack spacing and interface debonded length. The interface shear stress and fibers strength degradation model and oxidation region propagation model have been adopted to analyze the fatigue and oxidation effects on fatigue life of the composite, which is controlled by interface frictional slip and diffusion of oxygen gas through matrix multicrackings. Under cyclic fatigue loading, the fibers broken fraction was determined by combining the interface/fiber oxidation model, interface wear model and fibers statistical failure model at elevated temperatures, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfy the Global Load Sharing (GLS) criterion. When the broken fibers fraction approaches to the critical value, the composites fatigue fractures. The fatigue life S- N curves of 2D SiC/SiC, SiC/Si-N-C, SiC/Si-B4C, and Nextel 610™/Aluminosilicate composites at room temperature and 800, 1000 and 1200 °C in air and steam have been predicted.
Matrix fatigue crack development in a notched continuous fiber SCS-6/Ti-15-3 composite

NASA Technical Reports Server (NTRS)

Hillberry, B. M.; Johnson, W. S.

1990-01-01

In this study the extensive matrix fatigue cracking that has been observed in notched SCS-6/Ti-15-3 composites is investigated. Away from the notch uniform spacing of the fatigue cracks develops. Closer to the notch, fiber-matrix debonding which occurs increases the crack spacing. Crack spacing and debond length determined from shear-lag cylinder models compare favorably with experimental observations. Scanning electron microscope (SEM) fractography showed that the principal fatigue crack initiation occurred around the zero degree fibers. Interface failure in the 90 degree plies does not lead to the development of the primary fatigue cracking.
Matrix fatigue crack development in a notched continuous fiber SCS-6/Ti-15-3 composite

NASA Technical Reports Server (NTRS)

Hillberry, B. M.; Johnson, W. S.

1990-01-01

In this study the extensive matrix fatigue cracking that has been observed in notched SCS-6/Ti-15-3 composites is investigated. Away from the notch a uniform spacing of the fatigue cracks develops. Closer to the notch, fiber-matrix debonding which occurs increases the crack spacing. Crack spacing and debond length determined from shear-lag cylinder models compare favorably with experimental observations. Scanning electron microscope (SEM) fractography showed that the principal fatigue crack initiation occurred around the zero degree fibers. Interface failure in the 90 degree plies does not lead to the development of the primary fatigue cracking.
Characterization of fatigue behavior of 2-D woven fabric reinforced ceramic matrix composite at elevated temperature. Final report

DOE Office of Scientific and Technical Information (OSTI.GOV)

Groner, D.J.

This study investigated the fatigue behavior and associated damage mechanisms in notched and unnotched enhanced SiC/SiC ceramic matrix composite specimens at 1100 deg C. Stiffness degradation, strain variation, and hysteresis were evaluated to characterize material behavior. Microscopic examination was performed to characterize damage mechanisms. During high cycle/low stress fatigue tests, far less fiber/matrix interface debond was evident than in low cycle/high stress fatigue tests. Notched specimens exhibited minimal stress concentration during monotonic tensile testing and minimal notch sensitivity during fatigue testing. Damage mechanisms were also similar to unnotched.
Analysis of Fracture Mechanism for Al-Mg/SiCp Composite Materials

NASA Astrophysics Data System (ADS)

Maleque, M. A.; Adebisi, A. A.; Izzati, N.

2017-03-01

The present study aims to examine the fracture mechnism of silicon carbide particle (SiCp) reinforced aluminium matrix composite (AMC) material with 1 wt% addition of magnesium is fabricated using the stir casting process. The aluminium composite (Al-Mg/SiCp) is investigated for fatigue life and impact strength considering reinforcement weight fraction and influence of temperature on fracture toughness. The fabricated composite was tested using fatigue testing machine and charpy impact tester. Fractographic observations were evaluated with the scanning electron microscopy (SEM) on the fracture surface. It was found that increasing the SiCp weight fraction increased the fatigue life of the composite. Moreover, the 20 wt% SiCp Al-Mg composite attained the highest number of cycle and fatigue life compared to other variations. The mechanism responsible for the phenomena includes load transfer from the Al matrix alloy phase to the high strength and stiffness of the incorporated SiCp. The temperature variation influenced the impact strength of the composite and improved fracture toughness is achieved at 150 °C. It can be concluded from this study that reinforcement weight fraction and temperature affects the fracture behavior of the composites.
Mechanical fatigue degradation of ceramics versus resin composites for dental restorations.

PubMed

Belli, Renan; Geinzer, Eva; Muschweck, Anna; Petschelt, Anselm; Lohbauer, Ulrich

2014-04-01

For posterior partial restorations an overlap of indication exists where either ceramic or resin-based composite materials can be successfully applied. The aim of this study was to compare the fatigue resistance of modern dental ceramic materials versus dental resin composites in order to address such conflicts. Bar specimens of five ceramic materials and resin composites were produced according to ISO 4049 and stored for 14 days in distilled water at 37°C. The following ceramic materials were selected for testing: a high-strength zirconium dioxide (e.max ZirCAD, Ivoclar), a machinable lithium disilicate (e.max CAD, Ivoclar), a pressable lithium disilicate ceramic (e-max Press, Ivoclar), a fluorapatite-based glass-ceramic (e.max Ceram, Ivoclar), and a machinable color-graded feldspathic porcelain (Trilux Forte, Vita). The composite materials selected were: an indirect machinable composite (Lava Ultimate, 3M ESPE) and four direct composites with varying filler nature (Clearfil Majesty Posterior, Kuraray; GrandioSO, Voco; Tetric EvoCeram, Ivoclar-Vivadent; and CeramX Duo, Dentsply). Fifteen specimens were tested in water for initial strength (σin) in 4-point bending. Using the same test set-up, the residual flexural fatigue strength (σff) was determined using the staircase approach after 10(4) cycles at 0.5 Hz (n=25). Weibull parameters σ0 and m were calculated for the σin specimens, whereas the σff and strength loss in percentage were obtained from the fatigue experiment. The zirconium oxide ceramic showed the highest σin and σff (768 and 440 MPa, respectively). Although both lithium disilicate ceramics were similar in the static test, the pressable version showed a significantly higher fatigue resistance after cyclic loading. Both the fluorapatite-based and the feldspathic porcelain showed equivalent initial and cyclic fatigue properties. From the composites, the highest filled direct material Clearfil Majesty Posterior showed superior fatigue performance. From all materials, e.max Press and Clearfil Majesty Posterior showed the lowest strength loss (29.6% and 32%, respectively), whereas the other materials lost between 41% and 62% of their flexural strength after cyclic loading. Dental ceramics and resin composite materials show equivalent fatigue strength degradation at loads around 0.5σin values. Apart from the zirconium oxide and the lithium disilicate ceramics, resin composites generally showed better σff after 10,000 cycles than the fluorapatite glass-ceramic and the feldspathic porcelain. Resin composite restorations may be used as an equivalent alternative to glass-rich-ceramic inlays regarding mechanical performance. Copyright © 2014 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
The effect of a virtual reality exercise program on physical fitness, body composition, and fatigue in hemodialysis patients.

PubMed

Cho, Hyeyoung; Sohng, Kyeong-Yae

2014-10-01

[Purpose] The aim of the present study was to investigate the effects of a virtual reality exercise program (VREP) on physical fitness, body composition, and fatigue in hemodialysis (HD) patients with end-stage renal failure. [Subjects and Methods] A nonequivalent control group pretest-posttest design was used. Forty-six HD patients were divided into exercise (n=23) and control groups (n=23); while waiting for their dialyses, the exercise group followed a VREP, and the control group received only their usual care. The VREP was accomplished using Nintendo's Wii Fit Plus for 40 minutes, 3 times a week for 8 weeks during the period of May 27 to July 19, 2013. Physical fitness (muscle strength, balance, flexibility), body composition (skeletal muscle mass, body fat rate, arm and leg muscle mass), and fatigue were measured at baseline and after the intervention. [Results] After the VREP, physical fitness and body composition significantly increased, and the level of fatigue significantly decreased in the exercise group. [Conclusion] These results suggest that a VREP improves physical fitness, body composition, and fatigue in HD patients. Based on the findings, VREPs should be used as a health promotion programs for HD patients.
Tension-Compression Fatigue of a Nextel™720/alumina Composite at 1200 °C in Air and in Steam

NASA Astrophysics Data System (ADS)

Lanser, R. L.; Ruggles-Wrenn, M. B.

2016-08-01

Tension-compression fatigue behavior of an oxide-oxide ceramic-matrix composite was investigated at 1200 °C in air and in steam. The composite is comprised of an alumina matrix reinforced with Nextel™720 alumina-mullite fibers woven in an eight harness satin weave (8HSW). The composite has no interface between the fiber and matrix, and relies on the porous matrix for flaw tolerance. Tension-compression fatigue behavior was studied for cyclical stresses ranging from 60 to 120 MPa at a frequency of 1.0 Hz. The R ratio (minimum stress to maximum stress) was -1.0. Fatigue run-out was defined as 105 cycles and was achieved at 80 MPa in air and at 70 MPa in steam. Steam reduced cyclic lives by an order of magnitude. Specimens that achieved fatigue run-out were subjected to tensile tests to failure to characterize the retained tensile properties. Specimens subjected to prior cyclic loading in air retained 100 % of their tensile strength. The steam environment severely degraded tensile properties. Tension-compression cyclic loading was considerably more damaging than tension-tension cyclic loading. Composite microstructure, as well as damage and failure mechanisms were investigated.
Which Measures of Obesity Are Related to Depressive Symptoms and in Whom?

PubMed Central

Lim, Weonjeong; Thomas, Kamala S.; Bardwell, Wayne A.; Dimsdale, Joel E.

2009-01-01

The authors asked which obesity measurements were associated with depressive symptoms, whether this relationship differed by gender, and whether controlling for fatigue and response bias affected the relationship. A sample of 129 subjects (66 men, 63 women), with a mean age of 36.9 years and a mean Body Mass Index (BMI) of 26.4 participated in the study. Depressive symptoms, levels of fatigue, response bias, and anthropometrics were assessed. In women, but not men, BMI and percent of ideal body weight were related to depression. However, percent of body fat did not show a relationship with depression after controlling for fatigue and response bias. These findings suggest that women’s depressive symptoms are more influenced by body size than body fat composition, whereas men’s depressive symptoms seem to be unrelated to obesity. PMID:18212172
Experimental studies on fatigue behavior of macro fiber composite (MFC) under mechanical loading

NASA Astrophysics Data System (ADS)

Pandey, Akash; Arockiarajan, A.

2016-04-01

Macro fiber Composite (MFC) finds its application in active control, vibration control and sensing elements. MFC can be laminated to surfaces or embedded in the structures to be used as an actuator and sensors. Due to its attractive properties and applications, it may be subjected to continuous loading, which leads to the deterioration of the properties. This study is focused on the fatigue lifetime of MFC under tensile and compressive loading at room temperature. Experiments were performed using 4 point bending setup, with MFC pasted at the center of the mild steel beam, to maintain constant bending stress along MFC. MFC is pasted using vacuum bagging technique. Sinusoidal loading is given to sample while maintaining R=0.13 (for tensile testing) and R=10 (for compressive testing). For d31 and d33 type of MFC, test was conducted for the strain values of 727 μ strain, 1400 μ strain, 1700 μ strain and 1900 μ strain for fatigue under tensile loading. For fatigue under compressive loading, both d33 and d31, was subjected to minimum strain of -2000 μ strain. Decrease in the slope of dielectric displacement vs. strain is the measure for the degradation. 10 percent decrease in the slope is set as the failure criteria. Experimental results show that MFC is very reliable below 1700 μ strain (R=0.13) at the room temperature.
The Role of Microstructural Variability on the Very High-Cycle Fatigue Behavior of Discontinuously-Reinforced Aluminum Metal Matrix Composites using Ultrasonic Fatigue (Preprint)

DTIC Science & Technology

2008-05-01

controlled processing. Bhanu-Prasad et al .37 conducted a systematic study of PM-processed 2124/SiC/30p aluminum composites 4 5 in which matrix alloy...Mater., 27, 173-178. [5] Wang A, Rack HJ (1991). Transition wear behavior of SiC-particulate- and SiC- whisker-reinforced 7091 Al metal matrix...modeling of particle distribution effects on fatigue in Al -SiCp composites. Mater. Sci. Eng. A, Struct. Mater. Prop. Microstruct. Process., 300, 113-124
European Scientific Notes. Volume 34, Number 7,

DTIC Science & Technology

1980-07-31

fatigue , the effect of patient during the fitting, but which moisture on mechanical properties, could still be bent 900 without delamin- and creep...behavior. In the fatigue ating the composite or debonding the work; different reinforcing fibers composite from the aluminum . Once (including glass-carbon... fatigue work sulting structure has better properties Sturgeon has under way includes the than steel and weighs a good deal less, effect of
Improved lifetime of new fibrous carbon/ceramic composites

NASA Astrophysics Data System (ADS)

Gumula, Teresa

2018-03-01

New carbon/ceramic composites have been synthesized from low-cost phenol-formaldehyde resin and polysiloxane preceram. A reference carbon composite reinforced with carbon fibre (CC composite) is obtained in first place from a carbon fibre roving impregnated with a solution of phenol-formaldehyde resin in isopropyl alcohol. To obtain fibrous carbon/ceramic composites the CC perform is impregnated with polymethylphenylsiloxane polymer and then a thermal treatment in an inert atmosphere is applied. Depending on the temperature of this process, the resulting ceramics can be silicon carbide (SiC) or silicon oxycarbide (SiCO). Three representative samples, named CC/SiCO( a) (obtained at 1000 °C), CC/SiCO( b) (1500 °C) and CC/SiC (1700 °C), have been tested for fatigue behaviour and oxidation resistance. The value of the Young's modulus remains constant in fatigue tests done in flexion mode for the three new composites during a high number of cycles until sudden degradation begins. This is an unusual and advantageous characteristic for this type of materials and results in the absence of delamination during the measurements. In contrast, the CC reference composite shows a progressive degradation of the Young's modulus accompanied by delamination. SEM micrographs revealed that the formation of filaments of submicrometer diameter during the heat treatment can be responsible for the improved behaviour of these composites. The CC/SiC composite shows the best oxidation resistance among the three types of composites, with a 44% mass loss after 100 h of oxidation.
Evaluation of flawed composite structural components under static and cyclic loading. [fatigue life of graphite-epoxy composite materials

NASA Technical Reports Server (NTRS)

Porter, T. R.

1979-01-01

The effects of initial defects on the fatigue and fracture response of graphite-epoxy composite laminates are presented. The structural laminates investigated were a typical angle ply laminate, a polar/hoop wound pressure vessel laminate, and a typical engine fan blade laminate. Defects investigated were full and half penetration circular holes, full and half penetration slits, and countersink holes. The effects of the defect size and type on the static fracture strength, fatigue performance, and residual static strength are shown as well as the results of loadings on damage propagation in composite laminates. The data obtained were used to define proof test levels as a qualification procedure in composite structure subjected to cyclic loading.
Tensile and fatigue behavior of polymer composites reinforced with superelastic SMA strands

NASA Astrophysics Data System (ADS)

Daghash, Sherif M.; Ozbulut, Osman E.

2018-06-01

This study explores the use of superelastic shape memory alloy (SMA) strands, which consist of seven individual small-diameter wires, in an epoxy matrix and characterizes the tensile and fatigue responses of the developed SMA/epoxy composites. Using a vacuum assisted hand lay-up technique, twelve SMA fiber reinforced polymer (FRP) specimens were fabricated. The developed SMA-FRP composites had a fiber volume ratio of 50%. Tensile response of SMA-FRP specimens were characterized under both monotonic loading and increasing amplitude loading and unloading cycles. The degradation in superelastic properties of the developed SMA-FRP composites during fatigue loading at different strain amplitudes was investigated. The effect of loading rate on the fatigue response of SMA-FRP composites was also explored. In addition, fractured specimens were examined using the scanning electron microscopy (SEM) technique to study the failure mechanisms of the tested specimens. A good interfacial bonding between the SMA strands and epoxy matrix was observed. The developed SMA-FRP composites exhibited good superelastic behavior at different strain amplitudes up to at least 800 cycle after which significant degradation occurred.
Synergistic Effects of Temperature, Oxidation and Multicracking Modes on Damage Evolution and Life Prediction of 2D Woven Ceramic-Matrix Composites under Tension-Tension Fatigue Loading

NASA Astrophysics Data System (ADS)

Longbiao, Li

2017-08-01

In this paper, the synergistic effects of temperature, oxidation and multicracking modes on damage evolution and life prediction in 2D woven ceramic-matrix composites (CMCs) have been investigated. The damage parameter of fatigue hysteresis dissipated energy and the interface shear stress were used to monitor the damage evolution inside of CMCs. Under cyclic fatigue loading, the fibers broken fraction was determined by combining the interface/fiber oxidation model, interface wear model and fibers statistical failure model at elevated temperature, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfy the Global Load Sharing (GLS) criterion. When the broken fibers fraction approaches to the critical value, the composite fatigue fractures. The evolution of fatigue hysteresis dissipated energy, the interface shear stress and broken fibers fraction versus cycle number, and the fatigue life S-N curves of SiC/SiC at 1000, 1200 and 1300 °C in air and steam condition have been predicted. The synergistic effects of temperature, oxidation, fatigue peak stress, and multicracking modes on the evolution of interface shear stress and fatigue hysteresis dissipated energy versus cycle numbers curves have been analyzed.

ON THE DURABILITY OF RESIN-DENTIN BONDS: IDENTIFYING THE WEAKEST LINKS

PubMed Central

Zhang, Zihou; Beitzel, Dylan; Mutluay, Mustafa; Tay, Franklin R.; Pashley, David H.; Arola, Dwayne

2015-01-01

Fatigue of resin-dentin adhesive bonds is critical to the longevity of resin composite restorations. Objectives The objectives were to characterize the fatigue and fatigue crack growth resistance of resin-dentin bonds achieved using two different commercial adhesives and to identify apparent “weak-links”. Methods Bonded interface specimens were prepared using Adper Single Bond Plus (SB) or Adper Scotchbond Multi-Purpose (SBMP) adhesives and 3M Z100 resin composite according to the manufacturers instructions. The stress-life fatigue behavior was evaluated using the twin bonded interface approach and the fatigue crack growth resistance was examined using bonded interface Compact Tension (CT) specimens. Fatigue properties of the interfaces were compared to those of the resin-adhesive, resin composite and coronal dentin. Results The fatigue strength of the SBMP interface was significantly greater than that achieved by SB (p≤0.01). Both bonded interfaces exhibited significantly lower fatigue strength than that of the Z100 and dentin. Regarding the fatigue crack growth resistance, the stress intensity threshold (ΔKth) of the SB interface was significantly greater (p≤0.01) than that of the SBMP, whereas the ΔKth of the interfaces was more than twice that of the parent adhesives. Significance Collagen fibril reinforcement of the resin adhesive is essential to the fatigue crack growth resistance of resin-dentin bonds. Resin tags that are not well hybridized into the surrounding intertubular dentin and/or poor collagen integrity are detrimental to the bonded interface durability. PMID:26169318
Can Meditation Influence Quality of Life, Depression, and Disease Outcome in Multiple Sclerosis? Findings from a Large International Web-Based Study

PubMed Central

Levin, Adam B.; Hadgkiss, Emily J.; Weiland, Tracey J.; Marck, Claudia H.; van der Meer, Dania M.; Pereira, Naresh G.; Jelinek, George A.

2014-01-01

Objectives. To explore the association between meditation and health related quality of life (HRQOL), depression, fatigue, disability level, relapse rates, and disease activity in a large international sample of people with multiple sclerosis (MS). Methods. Participants were invited to take part in an online survey and answer questions relating to HRQOL, depression, fatigue, disability, relapse rates, and their involvement in meditation practices. Results. Statistically and potentially clinically significant differences between those who meditated once a week or more and participants who never meditated were present for mean mental health composite (MHC) scores, cognitive function scale, and health perception scale. The MHC results remained statistically significant on multivariate regression modelling when covariates were accounted for. Physical health composite (PHC) scores were higher in those that meditated; however, the differences were probably not clinically significant. Among those who meditated, fewer screened positive for depression, but there was no relationship with fatigue or relapse rate. Those with worsened disability levels were more likely to meditate. Discussion. The study reveals a significant association between meditation, lower risk of depression, and improved HRQOL in people with MS. PMID:25477709
Comparison of Mode II and III Monotonic and Fatigue Delamination Onset Behavior for Carbon/Toughened Epoxy Composites

NASA Technical Reports Server (NTRS)

Li, Jian; OBrien, T. Kevin; Lee, Shaw Ming

1997-01-01

Monotonic and fatigue tests were performed to compare the Mode II and III interlaminar fracture toughness and fatigue delamination onset for Tenax-HTA/R6376 carbon/toughened epoxy composites. The Mode II interlaminar fracture toughness and fatigue delamination onset were characterized using the end-notched flexure (ENF) test while the Mode III interlaminar fracture toughness and fatigue delamination onset were characterized by using the edge crack torsion (ECT) test. Monotonic tests show that the Mode III fracture toughness is higher than the Mode II fracture toughness. Both Mode II and III cyclic loading greatly increases the tendency for a delamination to grow relative to a single monotonically increasing load. Under fatigue loading, the Mode III specimen also has a longer life than the Mode II specimen.
Fatigue damage in cross-ply titanium metal matrix composites containing center holes

NASA Technical Reports Server (NTRS)

Bakuckas, J. G., Jr.; Johnson, W. S.; Bigelow, C. A.

1992-01-01

The development of fatigue damage in (0/90) sub SCS-6/TI-15-3 laminates containing center holes was studied. Stress levels required for crack initiation in the matrix were predicted using an effective strain parameter and compared to experimental results. Damage progression was monitored at various stages of fatigue loading. In general, a saturated state of damage consisting of matrix cracks and fiber matrix debonding was obtained which reduced the composite modulus. Matrix cracks were bridged by the 0 deg fibers. The fatigue limit (stress causing catastrophic fracture of the laminates) was also determined. The static and post fatigue residual strengths were accurately predicted using a three dimensional elastic-plastic finite element analysis. The matrix damage that occurred during fatigue loading significantly reduced the notched strength.
Fatigue damage mechanisms in boron-aluminium composite laminates

NASA Technical Reports Server (NTRS)

Dvorak, G. J.; Johnson, W. S.

1980-01-01

The relationship between fatigue and shakedown in metal matrix composites is investigated theoretically and experimentally for unidirectional and laminated 6061 Al-B materials. It is shown that no fatigue damage takes place if the applied stress range is such that the material remains elastic, or shakes down, i.e., resumes elastic cyclic straining after a small number of plastic strain cycles. Fatigue damage occurs only in specimens subjected to stress ranges which cause sustained cyclic plastic straining in the aluminum matrix. If the applied stress range is smaller than that required for fatigue failure, after about 10 to the 6th cycles a saturation damage state is reached which remains essentially unchanged with increasing number of cycles.
Fatigue-Induced Damage in Zr-Based Bulk Metallic Glasses

PubMed Central

Chuang, Chih-Pin; Yuan, Tao; Dmowski, Wojciech; Wang, Gong-Yao; Freels, Matt; Liaw, Peter K.; Li, Ran; Zhang, Tao

2013-01-01

In the present work, we investigate the effect of “fatigue” on the fatigue behavior and atomic structure of Zr-based BMGs. Fatigue experiments on the failed-by-fatigue samples indicate that the remnants generally have similar or longer fatigue life than the as-cast samples. Meanwhile, the pair-distribution-function (PDF) analysis of the as-cast and post-fatigue samples showed very small changes of local atomic structures. These observations suggest that the fatigue life of the 6-mm in-diameter Zr-based BMG is dominated by the number of pre-existing crack-initiation sites in the sample. Once the crack initiates in the specimen, the fatigue-induced damage is accumulated locally on these initiated sites, while the rest of the region deforms elastically. The results suggest that the fatigue failure of BMGs under compression-compression fatigue experiments is a defect-controlled process. The present work indicates the significance of the improved fatigue resistance with decreasing the sample size. PMID:23999496
Characterization of Degradation Progressive in Composite Laminates Subjected to Thermal Fatigue and Moisture Diffusion by Lamb Waves.

PubMed

Li, Weibin; Xu, Chunguang; Cho, Younho

2016-02-19

Laminate composites which are widely used in the aeronautical industry, are usually subjected to frequency variation of environmental temperature and excessive humidity in the in-service environment. The thermal fatigue and moisture absorption in composites may induce material degradation. There is a demand to investigate the coupling damages mechanism and characterize the degradation evolution of composite laminates for the particular application. In this paper, the degradation evolution in unidirectional carbon/epoxy composite laminates subjected to thermal fatigue and moisture absorption is characterized by Lamb waves. The decrease rate of Lamb wave velocity is used to track the degradation evolution in the specimens. The results show that there are two stages for the progressive degradation of composites under the coupling effect of thermal cyclic loading and moisture diffusion. The present work provides an alternative to monitoring the degradation evolution of in-service aircraft composite Laminates.
Prolonged fatigue in Ukraine and the United States: Prevalence and risk factors

PubMed Central

Friedberg, Fred; Tintle, Nathan; Clark, Jake; Bromet, Evelyn J.

2015-01-01

Background Prolonged, severe, unalleviated fatigue may be disabling whether it occurs on its own or in conjunction with medical or psychiatric conditions. This paper compares the prevalence and correlates of prolonged fatigue in general population samples in Ukraine versus the U.S. Methods Population surveys were conducted in 2002 in both Ukraine (Ukraine World Mental Health [WMH] Survey) and the U.S. (National Comorbidity Survey-Replication; NCS-R). Both surveys administered the Composite International Diagnostic Interview (CIDI 3.0), which contained modules assessing: neurasthenia (prolonged fatigue); mood, anxiety, and alcohol/drug use disorders; chronic medical conditions; and demographic characteristics. Multivariable logistic regression was used to examine risk factors in each country. Results The lifetime prevalence of prolonged fatigue was higher in Ukraine (5.2%) than the U.S. (3.7%). In both countries, one-fifth of individuals with prolonged fatigue had no medical or DSM-IV psychiatric condition. Also in both settings, fatigue was significantly associated with sociodemographic characteristics (being female, not working, and married before) as well as early onset and adult episodes of mood/anxiety disorder. Fatigue prevalence in Ukraine increased with age, but decreased in the U.S. at age 70. Unique risk factors for fatigue in Ukraine included lower socio-economic status, Ukrainian vs Russian ethnicity, and cardiovascular disease. Unique risk factors in the U.S. were parental depression/anxiety, adult episodes of alcohol/drugs, pain conditions, and other health problems. Conclusions The lifetime prevalence of prolonged fatigue in Ukraine was 40% higher than that found in U.S. data. In addition, fatigue prevalence increased sharply with age in Ukraine perhaps due to limited social and medical resources and greater comorbidity. PMID:26807341
Progressive Failure And Life Prediction of Ceramic and Textile Composites

NASA Technical Reports Server (NTRS)

Xue, David Y.; Shi, Yucheng; Katikala, Madhu; Johnston, William M., Jr.; Card, Michael F.

1998-01-01

An engineering approach to predict the fatigue life and progressive failure of multilayered composite and textile laminates is presented. Analytical models which account for matrix cracking, statistical fiber failures and nonlinear stress-strain behavior have been developed for both composites and textiles. The analysis method is based on a combined micromechanics, fracture mechanics and failure statistics analysis. Experimentally derived empirical coefficients are used to account for the interface of fiber and matrix, fiber strength, and fiber-matrix stiffness reductions. Similar approaches were applied to textiles using Repeating Unit Cells. In composite fatigue analysis, Walker's equation is applied for matrix fatigue cracking and Heywood's formulation is used for fiber strength fatigue degradation. The analysis has been compared with experiment with good agreement. Comparisons were made with Graphite-Epoxy, C/SiC and Nicalon/CAS composite materials. For textile materials, comparisons were made with triaxial braided and plain weave materials under biaxial or uniaxial tension. Fatigue predictions were compared with test data obtained from plain weave C/SiC materials tested at AS&M. Computer codes were developed to perform the analysis. Composite Progressive Failure Analysis for Laminates is contained in the code CPFail. Micromechanics Analysis for Textile Composites is contained in the code MicroTex. Both codes were adapted to run as subroutines for the finite element code ABAQUS and CPFail-ABAQUS and MicroTex-ABAQUS. Graphic user interface (GUI) was developed to connect CPFail and MicroTex with ABAQUS.
Piezoelectric and mechanical properties of fatigue resistant, self-healing PZT-ionomer composites

NASA Astrophysics Data System (ADS)

James, N. K.; Lafont, U.; van der Zwaag, S.; Groen, W. A.

2014-05-01

Piezoelectric ceramic-polymer composites with 0-3 connectivity were fabricated using lead zirconium titanate (PZT) powder dispersed in an ionomer (Zn ionomer) and its reference ethylene methacrylic acid copolymer (EMAA) polymer matrix. The PZT-Zn ionomer and PZT-EMAA composites were prepared by melt extrusion followed by hot pressing. The effects of poling conditions such as temperature, time and electric field on the piezoelectric properties of the composites were investigated. The experimentally observed piezoelectric charge coefficient and dielectric constant of the composites were compared with theoretical models. The results show that PZT-Zn ionomer composites have better piezoelectric properties compared to PZT-EMAA composites. The static and fatigue properties of the composites were investigated. The PZT-Zn ionomer composites were found to have excellent fatigue resistance even at strain levels of 4%. Due to the self-healing capabilities of the ionomer matrix, the loss of piezoelectric properties after high strain tensile cyclic loading could be partially recovered by thermal healing.
Metal Matrix Composites: Fatigue and Fracture Testing. (Latest citations from the Aerospace Database)

NASA Technical Reports Server (NTRS)

1996-01-01

The bibliography contains citations concerning techniques and results of testing metal matrix composites for fatigue and fracture. Methods include non-destructive testing techniques, and static and cyclic techniques for assessing compression, tensile, bending, and impact characteristics.
Nonlinear analyses of composite aerospace structures in sonic fatigue

NASA Technical Reports Server (NTRS)

Mei, Chuh

1993-01-01

This report summarizes the semiannual research progress, accomplishments, and future plans performed under the NASA Langley Research Center Grant No. NAG-1-1358. The primary research effort of this project is the development of analytical methods for the prediction of nonlinear random response of composite aerospace structures subjected to combined acoustic and thermal loads. The progress, accomplishments, and future plates on four sonic fatigue research topics are described. The sonic fatigue design and passive control of random response of shape memory alloy hybrid composites presented in section 4, which is suited especially for HSCT, is a new initiative.
Nonlinear analyses of composite aerospace structures in sonic fatigue

NASA Astrophysics Data System (ADS)

Mei, Chuh

1993-06-01

This report summarizes the semiannual research progress, accomplishments, and future plans performed under the NASA Langley Research Center Grant No. NAG-1-1358. The primary research effort of this project is the development of analytical methods for the prediction of nonlinear random response of composite aerospace structures subjected to combined acoustic and thermal loads. The progress, accomplishments, and future plates on four sonic fatigue research topics are described. The sonic fatigue design and passive control of random response of shape memory alloy hybrid composites presented in section 4, which is suited especially for HSCT, is a new initiative.
Fiberglass epoxy laminate fatigue properties at 300 and 20 K

NASA Technical Reports Server (NTRS)

Toth, J. M., Jr.; Bailey, W. J.; Boyce, D. A.

1985-01-01

A subcritical liquid hydrogen orbital storage and supply experiment is being designed for flight in the Space Shuttle cargo bay. The Cryogenic Fluid Management Experiment (CFME) includes a liquid hydrogen tank supported in a vacuum jacket by two fiberglass epoxy composite trunnion mounts. The ability of the CFME to last for the required seven missions depends primarily on the fatigue life of the composite trunnions at cryogenic temperatures. To verify the trunnion design and test the performance of the composite material, fatigue property data at 300 and 20 K were obtained for the specific E-glass fabric/S-glass unidirectional laminate that will be used for the CFME trunnions. The fatigue life of this laminate was greater at 20 K than at 300 K, and was satisfactory for the intended application.
A coupled/uncoupled deformation and fatigue damage algorithm utilizing the finite element method

NASA Technical Reports Server (NTRS)

Wilt, Thomas E.; Arnold, Steven M.

1994-01-01

A fatigue damage computational algorithm utilizing a multiaxial, isothermal, continuum based fatigue damage model for unidirectional metal matrix composites has been implemented into the commercial finite element code MARC using MARC user subroutines. Damage is introduced into the finite element solution through the concept of effective stress which fully couples the fatigue damage calculations with the finite element deformation solution. An axisymmetric stress analysis was performed on a circumferentially reinforced ring, wherein both the matrix cladding and the composite core were assumed to behave elastic-perfectly plastic. The composite core behavior was represented using Hill's anisotropic continuum based plasticity model, and similarly, the matrix cladding was represented by an isotropic plasticity model. Results are presented in the form of S-N curves and damage distribution plots.
Accceleration of Fatigue Tests of Polymer Composite Materials by Using High-Frequency Loadings

NASA Astrophysics Data System (ADS)

Apinis, R.

2004-03-01

The possibility of using high-frequency loading in fatigue tests of polymer composite materials is discussed. A review of studies on the use of high-frequency loading of organic-, carbon-, and glass-fiber-reinforced plastics is presented. The results obtained are compared with those found in conventional low-frequency loadings. A rig for fatigue tests of rigid materials at loading frequencies to 500 Hz is described, and results for an LM-L1 unidirectional glass-fiber plastic in loadings with frequencies of 17 and 400 Hz are given. These results confirm that it is possible to accelerate the fatigue testing of polymer composite materials by considerably increasing the loading frequency. The necessary condition for using this method is an intense cooling of specimens to prevent them from vibration heating.
Fatigue crack growth in unidirectional and cross-ply SCS-6/Timetal 21S titanium matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Herrmann, D.J.

1994-01-01

Fatigue crack growth in unidirectional and cross-ply SCS-6/ Timetal(R) 21S titanium matrix composite was investigated. Fatigue crack growth tests were performed on (0){sub 4}, (90){sub 4}, and (0/90){sub s} center notch specimens. The (0){sub 4} and (0/90){sub s} fatigue crack growth rates decreased initially. Specimens removed prior to failure were polished to the first row of fibers and intact fibers in the wake of the matrix crack were observed. These bridging fibers reduced the stress intensity range that the matrix material was subjected to, thus reducing the crack growth rate. The crack growth rate eventually increased as fibers failed inmore » the crack wake but the fatigue crack growth rate was still much slower than that of unreinforced Timetal(R) 21S. A model was developed to study the mechanics of a cracked unidirectional composite with any combination of intact and broken fibers in the wake of a matrix crack. The model was correlated to fatigue crack growth rate tests. The model was verified by comparing predicted displacements near the crack surface with Elber gage (1.5 mm gage length extensometer) measurements. The fatigue crack growth rate for the (90){sub 4} specimens was faster than that of unreinforced Timetal(registered trademark) 21S. Elber gage displacement measurements were in agreement with linear elastic fracture mechanics predictions, suggesting that linear elastic fracture mechanics may be applicable to transversely loaded titanium matrix composites.« less
Differential continuum damage mechanics models for creep and fatigue of unidirectional metal matrix composites

NASA Technical Reports Server (NTRS)

Arnold, S. M.; Kruch, S.

1991-01-01

Three multiaxial isothermal continuum damage mechanics models for creep, fatigue, and creep/fatigue interaction of a unidirectional metal matrix composite volume element are presented, only one of which will be discussed in depth. Each model is phenomenological and stress based, with varying degrees of complexity to accurately predict the initiation and propagation of intergranular and transgranular defects over a wide range of loading conditions. The development of these models is founded on the definition of an initially transversely isotropic fatigue limit surface, static fracture surface, normalized stress amplitude function and isochronous creep damage failure surface, from which both fatigue and creep damage evolutionary laws can be obtained. The anisotropy of each model is defined through physically meaningful invariants reflecting the local stress and material orientation. All three transversely isotropic models have been shown, when taken to their isotropic limit, to directly simplify to previously developed and validated creep and fatigue continuum damage theories. Results of a nondimensional parametric study illustrate (1) the flexibility of the present formulation when attempting to characterize a large class of composite materials, and (2) its ability to predict anticipated qualitative trends in the fatigue behavior of unidirectional metal matrix composites. Additionally, the potential for the inclusion of various micromechanical effects (e.g., fiber/matrix bond strength, fiber volume fraction, etc.), into the phenomenological anisotropic parameters is noted, as well as a detailed discussion regarding the necessary exploratory and characterization experiments needed to utilize the featured damage theories.
Weibull models of fracture strengths and fatigue behavior of dental resins in flexure and shear.

PubMed

Baran, G R; McCool, J I; Paul, D; Boberick, K; Wunder, S

1998-01-01

In estimating lifetimes of dental restorative materials, it is useful to have available data on the fatigue behavior of these materials. Current efforts at estimation include several untested assumptions related to the equivalence of flaw distributions sampled by shear, tensile, and compressive stresses. Environmental influences on material properties are not accounted for, and it is unclear if fatigue limits exist. In this study, the shear and flexural strengths of three resins used as matrices in dental restorative composite materials were characterized by Weibull parameters. It was found that shear strengths were lower than flexural strengths, liquid sorption had a profound effect on characteristic strengths, and the Weibull shape parameter obtained from shear data differed for some materials from that obtained in flexure. In shear and flexural fatigue, a power law relationship applied for up to 250,000 cycles; no fatigue limits were found, and the data thus imply only one flaw population is responsible for failure. Again, liquid sorption adversely affected strength levels in most materials (decreasing shear strengths and flexural strengths by factors of 2-3) and to a greater extent than did the degree of cure or material chemistry.
Preliminary Investigation to Determine the Suitable Mixture Composition for Corn Starch Matrix

NASA Astrophysics Data System (ADS)

Huzaimi Zakaria, Nazri; Ngali, Zamani; Zulkefli Selamat, Mohd

2017-01-01

The use of natural fiber as reinforcement in polymeric composites has been seen a dramatically increase over the last decades. The surge in the interest of natural fiber composite or biodegradable composite is mainly due to the attractive cost of production, improved of hardness, better fatigue endurance and good thermal and mechanical resistivity. In this work, corn starch in the form of powder is utilized as the matrix of the composite. However, starch is brittle and has low strength make it inappropriate candidate for matrix binder. The main objective of this study is to modify the mechanical properties of pure corn starch by mixing it with water, glycerol and vinegar. The composition ratio of water is 60~80%, corn starch 10~35%, glycerol is 5~15% and vinegar is 0~5%, ten samples (A-J) have been manufactured and the best mixture composition is selected based on few selection criteria. The selection criteria are visual impaction, hardness and density. From the results, the samples without vinegar are not suitable to be used because of the fungus availability on the surface. Meanwhile the results from the samples with 5 ml vinegar have no fungus on their surface even has been exposed to the ambient air. While the sample C has shown the best sample based on the visual, hardness and density test.

Micromechanics Fatigue Damage Analysis Modeling for Fabric Reinforced Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Min, J. B.; Xue, D.; Shi, Y.

2013-01-01

A micromechanics analysis modeling method was developed to analyze the damage progression and fatigue failure of fabric reinforced composite structures, especially for the brittle ceramic matrix material composites. A repeating unit cell concept of fabric reinforced composites was used to represent the global composite structure. The thermal and mechanical properties of the repeating unit cell were considered as the same as those of the global composite structure. The three-phase micromechanics, the shear-lag, and the continuum fracture mechanics models were integrated with a statistical model in the repeating unit cell to predict the progressive damages and fatigue life of the composite structures. The global structure failure was defined as the loss of loading capability of the repeating unit cell, which depends on the stiffness reduction due to material slice failures and nonlinear material properties in the repeating unit cell. The present methodology is demonstrated with the analysis results evaluated through the experimental test performed with carbon fiber reinforced silicon carbide matrix plain weave composite specimens.
Effects of Meridian Acupressure Massage on Body Composition, Edema, Stress, and Fatigue in Postpartum Women.

PubMed

Jung, Geum-Sook; Choi, In-Ryoung; Kang, Hee-Young; Choi, Eun-Young

2017-10-01

This study aims to investigate the effects of meridian acupressure massage on body composition, edema, stress, and fatigue in postpartum women. A quasi-experimental design with a nonequivalent control group was utilized. The Postpartum Care Center of Women's Hospital in Gwangju City, Republic of Korea. The study group consisted of 39 postpartum women, 19 in the experimental group and 20 in the control group, recruited from the postpartum care center of Women's Hospital in Gwangju city, South Korea. The experimental group was provided with meridian acupressure massage for 90 min daily over 5 days as an experimental therapy. Body composition (body weight, BMI, total body water, ECW ratio, LBM, and body fat) Edema (subjective edema, average girth of the upper limbs, and average girth of the lower limbs), Stress (psychological stress and physical stress), and Fatigue. The experimental group demonstrated a significantly larger decrease compared with the control group in measures of body composition, edema, total subjective stress, psychological stress, and subjective fatigue. Meridian acupressure massage can hasten the return to original body composition after childbirth.
Computational Fatigue Life Analysis of Carbon Fiber Laminate

NASA Astrophysics Data System (ADS)

Shastry, Shrimukhi G.; Chandrashekara, C. V., Dr.

2018-02-01

In the present scenario, many traditional materials are being replaced by composite materials for its light weight and high strength properties. Industries like automotive industry, aerospace industry etc., are some of the examples which uses composite materials for most of its components. Replacing of components which are subjected to static load or impact load are less challenging compared to components which are subjected to dynamic loading. Replacing the components made up of composite materials demands many stages of parametric study. One such parametric study is the fatigue analysis of composite material. This paper focuses on the fatigue life analysis of the composite material by using computational techniques. A composite plate is considered for the study which has a hole at the center. The analysis is carried on (0°/90°/90°/90°/90°)s laminate sequence and (45°/-45°)2s laminate sequence by using a computer script. The life cycles for both the lay-up sequence are compared with each other. It is observed that, for the same material and geometry of the component, cross ply laminates show better fatigue life than that of angled ply laminates.
Fatigue Resistance of CAD/CAM Resin Composite Molar Crowns

PubMed Central

Shembish, Fatma A.; Tong, Hui; Kaizer, Marina; Janal, Malvin N.; Thompson, Van P.; Opdam, Niek J.; Zhang, Yu

2016-01-01

Objective To demonstrate the fatigue behavior of CAD/CAM resin composite molar crowns using a mouth-motion step-stress fatigue test. Monolithic leucite-reinforced glass-ceramic crowns were used as a reference. Methods Fully anatomically shaped monolithic resin composite molar crowns (Lava Ultimate, n = 24) and leucite reinforced glass-ceramic crowns (IPS Empress CAD, n = 24) were fabricated using CAD/CAM systems. Crowns were cemented on aged dentin-like resin composite tooth replicas (Filtek Z100) with resin-based cements (RelyX Ultimate for Lava Ultimate or Multilink Automix for IPS Empress). Three step-stress profiles (aggressive, moderate and mild) were employed for the accelerated sliding-contact mouth-motion fatigue test. Twenty one crowns from each group were randomly distributed among these three profiles (1:2:4). Failure was designated as chip-off or bulk fracture. Optical and electronic microscopes were used to examine the occlusal surface and subsurface damages, as well as the material microstructures. Results The resin composite crowns showed only minor occlusal damage during mouth-motion step-stress fatigue loading up to 1700 N. Cross-sectional views revealed contact-induced cone cracks in all specimens, and flexural radial cracks in 2 crowns. Both cone and radial cracks were relatively small compared to the crown thickness. Extending these cracks to the threshold for catastrophic failure would require much higher indentation loads or more loading cycles. In contrast, all of the glass-ceramic crowns fractured, starting at loads of approximately 450 N. Significance Monolithic CAD/CAM resin composite crowns endure, with only superficial damage, fatigue loads 3 – 4 times higher than those causing catastrophic failure in glass-ceramic CAD crowns. PMID:26777092
Perspective for Fibre-Hybrid Composites in Wind Energy Applications

PubMed Central

2017-01-01

Increasing the efficiency of wind turbines will be vital for the wind energy sector to continue growing. The drive for increased efficiency is pushing turbine manufacturers to shift from glass fibre composite blades towards carbon/glass fibre-hybrid composite blades. This shift brings significant challenges in terms of optimising the design and understanding the failure of these new blade materials. This review therefore surveys the literature on fibre-hybrid composites, with an emphasis on aspects that are relevant for turbine blade materials. The literature on tensile, flexural, compressive, and fatigue performance is critically assessed and areas for future research are identified. Numerical simulations of fibre-hybrid composites have reached a reasonable maturity for tensile failure, but significant progress is required for flexural, compressive, and fatigue failure. Fatigue failure of fibre-hybrid composites in particular, requires more careful attention from both a modelling and experimental point of view. PMID:29117126
Perspective for Fibre-Hybrid Composites in Wind Energy Applications.

PubMed

Swolfs, Yentl

2017-11-08

Increasing the efficiency of wind turbines will be vital for the wind energy sector to continue growing. The drive for increased efficiency is pushing turbine manufacturers to shift from glass fibre composite blades towards carbon/glass fibre-hybrid composite blades. This shift brings significant challenges in terms of optimising the design and understanding the failure of these new blade materials. This review therefore surveys the literature on fibre-hybrid composites, with an emphasis on aspects that are relevant for turbine blade materials. The literature on tensile, flexural, compressive, and fatigue performance is critically assessed and areas for future research are identified. Numerical simulations of fibre-hybrid composites have reached a reasonable maturity for tensile failure, but significant progress is required for flexural, compressive, and fatigue failure. Fatigue failure of fibre-hybrid composites in particular, requires more careful attention from both a modelling and experimental point of view.
The monitoring and fatigue behavior of CFCCs at ambient temperature and 1000{degrees}C

DOE Office of Scientific and Technical Information (OSTI.GOV)

Miriyala, N.; Liaw, P.K.; McHargue, C.J.

1997-04-01

Metallographically polished flexure bars of Nicalon/SiC and Nicalon/alumina composites were subjected to monotonic and cycle-fatigue loadings, with loading either parallel or normal to the fabric plies. The fabric orientation did not significantly affect the mechanical behavior of the Nicalon/SiC composite at ambient temperature. However, the mechanical behavior of the Nicalon/alumina composite was significantly affected by the fabric orientation at ambient temperature in air and at 1000{degrees}C in argon atmosphere. In addition, there was a significant degradation in the fatigue performance of the alumina matrix composite at the elevated temperature, owing to creep in the material and degradation in the fibermore » strength.« less
Fatigue testing of low-cost fiberglass composite wind turbine blade materials

NASA Technical Reports Server (NTRS)

Hofer, K. E.; Bennett, L. C.

1981-01-01

The static and fatigue behavior of transverse filament tape (TFT) fiberglass/epoxy and TFT/polyester composites was established by the testing of specimens cut from panels fabricated by a filament winding process used for the construction of large experimental wind turbine blades.
High-performance fiber/epoxy composite pressure vessels

NASA Technical Reports Server (NTRS)

Chiao, T. T.; Hamstad, M. A.; Jessop, E. S.; Toland, R. H.

1978-01-01

Activities described include: (1) determining the applicability of an ultrahigh-strength graphite fiber to composite pressure vessels; (2) defining the fatigue performance of thin-titanium-lined, high-strength graphite/epoxy pressure vessel; (3) selecting epoxy resin systems suitable for filament winding; (4) studying the fatigue life potential of Kevlar 49/epoxy pressure vessels; and (5) developing polymer liners for composite pressure vessels. Kevlar 49/epoxy and graphite fiber/epoxy pressure vessels, 10.2 cm in diameter, some with aluminum liners and some with alternation layers of rubber and polymer were fabricated. To determine liner performance, vessels were subjected to gas permeation tests, fatigue cycling, and burst tests, measuring composite performance, fatigue life, and leak rates. Both the metal and the rubber/polymer liner performed well. Proportionately larger pressure vessels (20.3 and 38 cm in diameter) were made and subjected to the same tests. In these larger vessels, line leakage problems with both liners developed the causes of the leaks were identified and some solutions to such liner problems are recommended.
Analysis of thermomechanical fatigue of unidirectional titanium metal matrix composites

NASA Technical Reports Server (NTRS)

Mirdamadi, M.; Johnson, W. S.; Bahei-El-din, Y. A.; Castelli, M. G.

1991-01-01

Thermomechanical fatigue (TMF) data was generated for a Ti-15V-3Cr-3Al-3Sn (Ti-15-3) material reinforced with SCS-6 silicon carbide fibers for both in-phase and out-of-phase thermomechanical cycling. Significant differences in failure mechanisms and fatigue life were noted for in-phase and out-of-phase testing. The purpose of the research is to apply a micromechanical model to the analysis of the data. The analysis predicts the stresses in the fiber and the matrix during the thermal and mechanical cycling by calculating both the thermal and mechanical stresses and their rate-dependent behavior. The rate-dependent behavior of the matrix was characterized and was used to calculate the constituent stresses in the composite. The predicted 0 degree fiber stress range was used to explain the composite failure. It was found that for a given condition, temperature, loading frequency, and time at temperature, the 0 degree fiber stress range may control the fatigue life of the unidirectional composite.
Fatigue of notched fiber composite laminates. Part 1: Analytical model

NASA Technical Reports Server (NTRS)

Mclaughlin, P. V., Jr.; Kulkarni, S. V.; Huang, S. N.; Rosen, B. W.

1975-01-01

A description is given of a semi-empirical, deterministic analysis for prediction and correlation of fatigue crack growth, residual strength, and fatigue lifetime for fiber composite laminates containing notches (holes). The failure model used for the analysis is based upon composite heterogeneous behavior and experimentally observed failure modes under both static and fatigue loading. The analysis is consistent with the wearout philosophy. Axial cracking and transverse cracking failure modes are treated together in the analysis. Cracking off-axis is handled by making a modification to the axial cracking analysis. The analysis predicts notched laminate failure from unidirectional material fatique properties using constant strain laminate analysis techniques. For multidirectional laminates, it is necessary to know lamina fatique behavior under axial normal stress, transverse normal stress and axial shear stress. Examples of the analysis method are given.
Proposed framework for thermomechanical life modeling of metal matrix composites

NASA Technical Reports Server (NTRS)

Halford, Gary R.; Lerch, Bradley A.; Saltsman, James F.

1993-01-01

The framework of a mechanics of materials model is proposed for thermomechanical fatigue (TMF) life prediction of unidirectional, continuous-fiber metal matrix composites (MMC's). Axially loaded MMC test samples are analyzed as structural components whose fatigue lives are governed by local stress-strain conditions resulting from combined interactions of the matrix, interfacial layer, and fiber constituents. The metallic matrix is identified as the vehicle for tracking fatigue crack initiation and propagation. The proposed framework has three major elements. First, TMF flow and failure characteristics of in situ matrix material are approximated from tests of unreinforced matrix material, and matrix TMF life prediction equations are numerically calibrated. The macrocrack initiation fatigue life of the matrix material is divided into microcrack initiation and microcrack propagation phases. Second, the influencing factors created by the presence of fibers and interfaces are analyzed, characterized, and documented in equation form. Some of the influences act on the microcrack initiation portion of the matrix fatigue life, others on the microcrack propagation life, while some affect both. Influencing factors include coefficient of thermal expansion mismatch strains, residual (mean) stresses, multiaxial stress states, off-axis fibers, internal stress concentrations, multiple initiation sites, nonuniform fiber spacing, fiber debonding, interfacial layers and cracking, fractured fibers, fiber deflections of crack fronts, fiber bridging of matrix cracks, and internal oxidation along internal interfaces. Equations exist for some, but not all, of the currently identified influencing factors. The third element is the inclusion of overriding influences such as maximum tensile strain limits of brittle fibers that could cause local fractures and ensuing catastrophic failure of surrounding matrix material. Some experimental data exist for assessing the plausibility of the proposed framework.
Fatigue Behavior of a Cross-Ply Metal Matrix Composite at Elevated Temperature Under Strain Controlled Mode.

DTIC Science & Technology

1994-12-01

1991. 114 22. Nimmer, R. P. et al. "Fiber Array Geometry Effects Upon Composite Transverse Tensile Behavior," Titanium Aluminide Composites. February... Titanium , Silicon Carbide, Strain Control Mode 17. SECURITY CLASSIFICATION I18. SECURITY CLASSIFICATION 19. SECURITY CLASSIFIKATION 20. LIMITATION OF...ends. Boyum was the first to examine fully reversed (R=-l) fatigue of a titanium composite under the load control mode, at both room and elevated
Thermo-Mechanical Fatigue of a Fiber Reinforced Titanium Aluminide Composite

DTIC Science & Technology

1991-03-01

Puiitr]on Air Foic. Base, Oiio 91 10 25 038 DTIC 4E L L E C :i<. THERMO- MECHAN I CAL FAT I GUE OF A FIBER REINFORCED TITANIUM ALUMINIDE COMPOSITE Thesis...reinforced titanium aluminide composite was investigated. Three test specimens were subjected to in-phase thermo- mechanical cycling and four to out-of...Unclassified UL ............................... AFIT/GAE/ENY/91S-1 THERMO- MECHANICAL FATIGUE OF A FIBER REINFORCED TITANIUM ALUMINIDE COMPOSITE THESIS
High temperature fatigue behavior of tungsten copper composites

NASA Technical Reports Server (NTRS)

Verrilli, Michael J.; Kim, Yong-Suk; Gabb, Timothy P.

1989-01-01

The high temperature fatigue behavior of a 9 vol percent, tungsten fiber reinforced copper matrix composite was investigated. Load-controlled isothermal fatigue experiments at 260 and 560 C and thermomechanical fatigue (TMF) experiments, both in phase and out of phase between 260 and 560 C, were performed. The stress-strain response displayed considerable inelasticity under all conditions. Also, strain ratcheting was observed during all the fatigue experiments. For the isothermal fatigue and in-phase TMF tests, the ratcheting was always in a tensile direction, continuing until failure. The ratcheting during the out-of-phase TMF test shifted from a tensile direction to a compressive direction. This behavior was thought to be associated with the observed bulging and the extensive cracking of the out-of-phase specimen. For all cases, the fatigue lives were found to be controlled by damage to the copper matrix. Grain boundary cavitation was the dominant damage mechanism of the matrix. On a stress basis, TMF loading reduced lives substantially, relative to isothermal cycling. In-phase cycling resulted in the shortest lives, and isothermal fatigue at 260 C, the longest.
[Evaluation of mechanical properties of four kinds of composite resins for inlay].

PubMed

Jiang, Ling-ling; Liu, Hong; Wang, Jin-rui

2011-04-01

To evaluate the compressive strength, wear resistance, hardness, and soaking fatigue of four composite resins for inlay, which were Ceramage, Surefil, Solitaire 2, and Filtek(TM) Z350. Scanning electron microscope (SEM) was used to analyze the microstructures of the wear surface of the samples. The samples for the compression test, hardness test and wear were prepared. The samples were respectively immersed in the artificial saliva for 2 months for immersed test. The electronic universal testing machine was used to test the compression strength. Hardness was quantified by micro-Vickers hardness test. The wear tester was used for the wear test. SEM was used to analyze the microstructures of the wear surface of samples. All the data was analyzed by using SPSS17.0 software package. The compressive strength of Surefil was the biggest which was significantly higher than the other three resins before soaking (P<0.05). After soaking, there was no significant difference between the composite resins (P>0.05). The hardness of Surefil was the best, and significant difference was found between the hardness of the materials before soaking (P<0.05). After soaking, no significant difference was obtained between the hardness of Surefil and Filtek(TM) Z350 (P>0.05).The compressive strength and hardness of 4 materials decreased after soaking in artificial saliva. But only the compressive strength of Filtek(TM) Z350 had no significant change after immersion (P>0.05). Except Filtek(TM) Z350, there was significant difference between the other three materials (P<0.05). Significant relationship was observed between wear and hardness of three materials (P<0.05). According to SEM observation, abrasive wear occurred in four materials. In addition to Ceramage, other composite resins had adhesive wear. The mechanical property of Surefil is the best, and it is suitable for fabrication of posterior inlay. Filtek(TM) Z350's ability to resist fatigue is the best.
Fatigue damage prognosis of internal delamination in composite plates under cyclic compression loadings using affine arithmetic as uncertainty propagation tool

NASA Astrophysics Data System (ADS)

Gbaguidi, Audrey J.-M.

Structural health monitoring (SHM) has become indispensable for reducing maintenance costs and increasing the in-service capacity of a structure. The increased use of lightweight composite materials in aircraft structures drastically increased the effects of fatigue induced damage on their critical structural components and thus the necessity to predict the remaining life of those components. Damage prognosis, one of the least investigated fields in SHM, uses the current damage state of the system to forecast its future performance by estimating the expected loading environments. A successful damage prediction model requires the integration of technologies in areas like measurements, materials science, mechanics of materials, and probability theories, but most importantly the quantification of uncertainty in all these areas. In this study, Affine Arithmetic is used as a method for incorporating the uncertainties due to the material properties into the fatigue life prognosis of composite plates subjected to cyclic compressive loadings. When loadings are compressive in nature, the composite plates undergo repeated buckling-unloading of the delaminated layer which induces mixed modes I and II states of stress at the tip of the delamination in the plates. The Kardomateas model-based prediction law is used to predict the growth of the delamination, while the integration of the effects of the uncertainties for modes I and II coefficients in the fatigue life prediction model is handled using Affine arithmetic. The Mode I and Mode II interlaminar fracture toughness and fatigue characterization of the composite plates are first experimentally studied to obtain the material coefficients and fracture toughness, respectively. Next, these obtained coefficients are used in the Kardomateas law to predict the delamination lengths in the composite plates while using Affine Arithmetic to handle their uncertainties. At last, the fatigue characterization of the composite plates during compressive-buckling loadings is experimentally studied, and the delamination lengths obtained are compared with the predicted values to check the performance of Affine Arithmetic as an uncertainty propagation tool.
Bioimpedance analysis and HIV-related fatigue.

PubMed

Meynell, Janet; Barroso, Julie

2005-01-01

Although various physiological and psychological causes of fatigue in HIV-positive persons have been proposed, it is still not well understood. Bioimpedance analysis has proved to be an easily used, non-invasive measurement of body composition and cellular integrity. This study, looking at whether body composition as measured by bioimpedance analysis is associated with fatigue, is part of a pilot study looking for physiological and psychological biomarkers that could be factors in the fatigue experienced by HIV-positive people. Twenty-nine men and eleven women were measured for height, weight, and bioimpedance analysis. Correlations were examined between fatigue intensity and weight, body mass index, body cell mass, fat-free mass, extracellular mass, and phase angle. Because of the fat redistribution that has occurred with some people taking protease inhibitors, we also examined differences in weight, body mass index, body cell mass, fat-free mass, and fatigue intensity between those taking and those not taking protease inhibitors. There was no association between fatigue intensity and weight, body mass index, body cell mass, fat-free mass, or phase angle, nor were there differences between those taking and those not taking protease inhibitors. However, it was noted that both the phase angle and the ratio of extracellular mass to body cell mass (extracellular mass:body cell mass) were below their respective normal ranges, indicating that the participants were somewhat compromised nutritionally and with regard to cell membrane integrity. Although fatigue was not shown to be related to body composition measurement in this study, further work is needed on the causes of fatigue, because its effects on the lives of HIV-positive people can be devastating.
Prediction of Fatigue Crack Growth of Repaired Al-alloy Structures with Double Sides

NASA Astrophysics Data System (ADS)

Benachour, M.; Benachour, N.; Benguediab, M.; Seriari, F. Z.

During navigation, aircrafts are subject to fatigue damage. In order to rehabilitate damaged structures some techniques are often used to resolve this problem. Efficient repair technique, called composite patch repair, was used to reinforce the damaged structures and stop cracks. In this paper, effect of composite patch repair (Boron/Epoxy) on fatigue crack growth (FCG) was investigated on 2219 T62 Al-alloy. Effects of double patch repair in single notch tensile specimen (SENT) on FCG were studied and compared to single patch repair. Results show beneficial effect of patch repair on fatigue life and FCGR in comparison with the un-patched specimen. In addition, effect of mean stress characterized by stress ratio was highlighted. Fatigue behavior of investigated Al-alloy was compared.
Development of composite carrythrough bulkhead

NASA Technical Reports Server (NTRS)

Ehlen, R. J.; Libeskind, M.

1992-01-01

A structural development program was recently completed in which the weight and fatigue advantages of an all composite major load carrying bulkhead was successfully demonstrated. Fabrication of a full scale article, including static and fatigue testing of the carry-through beam portion verified the producibility, strength and durability of this design, thereby presenting the opportunity for use on aircraft upgrades and new aircraft. A 15% weight saving is achievable and, more importantly, the fatigue problems that normally plague metal bulkheads are virtually eliminated.

Hygrothermal Effects in Continuous Fibre Reinforced Composites. Part 4. Mechanical Properties 2 - Fatigue and Time-Dependent Properties (Effets Hygrothermiques dans les Composites a Renfort de Fibre Continu. Partie 4. Proprietes Mecaniques 2 - Fatigue et Proprietes Dependant du Temps)

DTIC Science & Technology

1983-09-01

reduction of stress intensity at a crack tip due to Lreep was responsible for increasing the fatigue life during the "slow- fast " L .sts. As creep is clearly...Aeronautical Establishment Structures and Materials Laboratory SPONSORING AGENCY/AGENCE DE SUBVENTION 8 DATE FILE/DOSSIER LAB. ORDER PAGES FIGS/ DIAGRAMMES
Fatigue behavior of a cross-ply ceramic matrix composite at elevated temperature under tension-tension loading. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Steiner, C.D.

This study investigated the fatigue behavior and damage mechanisms of a (0/90)4s SiC/MAS ceramic matrix composite under tension-tension loading at two elevated temperatures and two frequencies. Stress and strain hystereses, maximum and minimum strain, and modulus of elasticity were evaluated to characterize the material behavior. Microscopy and fractography were used to evaluate damage progression and mechanisms. Fatigue life was independent of frequency at both temperatures.
Effects of Frequency and Environment on Fatigue Behavior of an Oxide-Oxide Ceramic Matrix Composite at 1200 Deg. C

DTIC Science & Technology

2006-06-01

Mehrman investigated the effects of prior fatigue on creep behavior, and concluded that a history of prior fatigue loading increases creep life of...as reduced susceptibility to oxidation [4]. Nextel™ 720/Alumina composite (N720/A), combines the strength and creep resistance of a di- phase...studied the response to creep and cyclic loading, respectively, and showed that the presence of steam severely degrades performance at 1200ºC [35
Fatigue qualification of high thickness composite rotor components

NASA Astrophysics Data System (ADS)

Raggi, M.; Mariani, U.; Zaffaroni, G.

Fatigue qualification aspects of composite rotor components are presented according with the safe life procedure usually applied by helicopter manufacturers. Test activities are identified at three levels of specimen complexity: coupon, structural element and full scale component. Particular attention is given to high thickness laminates qualification as far as environmental exposure is concerned. A practical approach for an accelerated conditioning procedure is described. The application to a main rotor tension link is presented showing the negligible effect of the moisture absorption on its fatigue strength.
Fracture loads of all-ceramic crowns under wet and dry fatigue conditions.

PubMed

Borges, Gilberto A; Caldas, Danilo; Taskonak, Burak; Yan, Jiahau; Sobrinho, Lourenco Correr; de Oliveira, Wildomar José

2009-12-01

The aim of this study was to test the hypothesis that fracture loads of fatigued dental ceramic crowns are affected by testing environment and luting cement. One hundred and eighty crowns were prepared from bovine teeth using a lathe. Ceramic crowns were prepared from three types of ceramic systems: an alumina-infiltrated ceramic, a lithia-disilicate-based glass ceramic, and a leucite-reinforced ceramic. For each ceramic system, 30 crowns were cemented with a composite resin cement, and the remaining 30 with a resin-modified glass ionomer cement. For each ceramic system and cement, ten specimens were loaded to fracture without fatiguing. A second group (n = 10) was subjected to cyclic fatigue and fracture tested in a dry environment, and a third group (n = 10) was fatigued and fractured in distilled water. The results were statistically analyzed using one-way ANOVA and Tukey HSD test. The fracture loads of ceramic crowns decreased significantly after cyclic fatigue loading (p
An optical motion measuring system for laterally oscillated fatigue tests

NASA Technical Reports Server (NTRS)

Tripp, John S.; Tcheng, Ping; Murri, Gretchen B.; Sharpe, Scott

1993-01-01

This paper describes an optical system developed for materials testing laboratories at NASA Langley Research Center (LaRC) for high resolution monitoring of the transverse displacement and angular rotation of a test specimen installed in an axial-tension bending machine (ATB) during fatigue tests. It consists of a small laser, optics, a motorized mirror, three photodiodes, electronic detection and counting circuits, a data acquisition system, and a personal computer. A 3-inch by 5-inch rectangular plate attached to the upper grip of the test machine serves as a target base for the optical system. The personal computer automates the fatigue test procedure, controls data acquisition, performs data reduction, and provides user displays. The data acquisition system also monitors signals from up to 16 strain gages mounted on the test specimen. The motion measuring system is designed to continuously monitor and correlate the amplitude of the oscillatory motion with the strain gage signals in order to detect the onset of failure of the composite test specimen. A prototype system has been developed and tested which exceeds the design specifications of +/- 0.01 inch displacement accuracy, and +/- 0.25 deg angular accuracy at a sampling rate of 100 samples per second.
Combining Passive Thermography and Acoustic Emission for Large Area Fatigue Damage Growth Assessment of a Composite Structure

NASA Technical Reports Server (NTRS)

Zalameda, Joseph N.; Horne, Michael R.; Madaras, Eric I.; Burke, Eric R.

2016-01-01

Passive thermography and acoustic emission data were obtained for improved real time damage detection during fatigue loading. A strong positive correlation was demonstrated between acoustic energy event location and thermal heating, especially if the structure under load was nearing ultimate failure. An image processing routine was developed to map the acoustic emission data onto the thermal imagery. This required removing optical barrel distortion and angular rotation from the thermal data. The acoustic emission data were then mapped onto thermal data, revealing the cluster of acoustic emission event locations around the thermal signatures of interest. By combining both techniques, progression of damage growth is confirmed and areas of failure are identified. This technology provides improved real time inspections of advanced composite structures during fatigue testing.Keywords: Thermal nondestructive evaluation, fatigue damage detection, aerospace composite inspection, acoustic emission, passive thermography
Deformation, Failure, and Fatigue Life of SiC/Ti-15-3 Laminates Accurately Predicted by MAC/GMC

NASA Technical Reports Server (NTRS)

Bednarcyk, Brett A.; Arnold, Steven M.

2002-01-01

NASA Glenn Research Center's Micromechanics Analysis Code with Generalized Method of Cells (MAC/GMC) (ref.1) has been extended to enable fully coupled macro-micro deformation, failure, and fatigue life predictions for advanced metal matrix, ceramic matrix, and polymer matrix composites. Because of the multiaxial nature of the code's underlying micromechanics model, GMC--which allows the incorporation of complex local inelastic constitutive models--MAC/GMC finds its most important application in metal matrix composites, like the SiC/Ti-15-3 composite examined here. Furthermore, since GMC predicts the microscale fields within each constituent of the composite material, submodels for local effects such as fiber breakage, interfacial debonding, and matrix fatigue damage can and have been built into MAC/GMC. The present application of MAC/GMC highlights the combination of these features, which has enabled the accurate modeling of the deformation, failure, and life of titanium matrix composites.
Fatigue Damage Monitoring of a Composite Step Lap Joint Using Distributed Optical Fibre Sensors

PubMed Central

Wong, Leslie; Chowdhury, Nabil; Wang, John; Chiu, Wing Kong; Kodikara, Jayantha

2016-01-01

Over the past few decades, there has been a considerable interest in the use of distributed optical fibre sensors (DOFS) for structural health monitoring of composite structures. In aerospace-related work, health monitoring of the adhesive joints of composites has become more significant, as they can suffer from cracking and delamination, which can have a significant impact on the integrity of the joint. In this paper, a swept-wavelength interferometry (SWI) based DOFS technique is used to monitor the fatigue in a flush step lap joint composite structure. The presented results will show the potential application of distributed optical fibre sensor for damage detection, as well as monitoring the fatigue crack growth along the bondline of a step lap joint composite structure. The results confirmed that a distributed optical fibre sensor is able to enhance the detection of localised damage in a structure. PMID:28773496
Muscle Fiber Type Composition and Knee Extension Isometric Strength Fatigue Patterns in Power- and Endurance-Trained Males.

ERIC Educational Resources Information Center

Kroll, Walter; And Others

1980-01-01

There is a degree of uniqueness in fatigue patterns, particularly between different levels of absolute maximum strength. Caution should be used when analyzing fatigue curves among subjects with unspecified strength levels. (CJ)
Fatigue Behavior of an Advanced SiC/SiC Composite at Elevated Temperature in Air and in Steam

DTIC Science & Technology

2009-12-01

specimens tested in salt fog achieved fatigue run-out. However, a significant decrease in fatigue life was observed for fatigue stresses ≥ 100 MPa...fatigue stress level approached the proportional limit. The reduction is fatigue life was attributed to the increased matrix cracking near the...oxidation of any free silicon remaining after production using methods such as melt infiltration, and the SiC itself as temperatures near 1000 ºC. These
Real Time Fatigue Damage Growth Assessment of a Composite Three-Stringer Panel Using Passive Thermography

NASA Technical Reports Server (NTRS)

Zalameda, Joseph N.; Burke, Eric R.; Horne, Michael R.; Bly, James B.

2015-01-01

Fatigue testing of advanced composite structures is critical to validate both structural designs and damage prediction models. In-situ inspection methods are necessary to track damage onset and growth as a function of load cycles. Passive thermography is a large area, noncontact inspection technique that is used to detect composite damage onset and growth in real time as a function of fatigue cycles. The thermal images are acquired in synchronicity to the applied compressive load using a dual infrared camera acquisition system for full (front and back) coverage. Image processing algorithms are investigated to increase defect contrast areas. The thermal results are compared to non-immersion ultrasound inspections and acoustic emission data.
Fatigue failure of dentin-composite disks subjected to cyclic diametral compression

PubMed Central

Li, Yuping; Carrera, Carola; Chen, Ruoqiong; Li, Jianying; Chen, Yungchung; Lenton, Patricia; Rudney, Joel. D.; Jones, Robert S.; Aparicio, Conrado; Fok, Alex

2015-01-01

Objective Our aim was to establish the relationship between cyclic loading and fatigue life of the dentin-composite interface using the newly developed disk in diametral compression tests. The results were then used to estimate the fatigue life of restored teeth under occlusal loading. Methods Disk specimens (5mm dia. × 2mm thick) were prepared using bovine incisors and restored with either a methacrylate-based composite Z100™ with Adper Single Bond Plus (Z100) or silorane-based composite Filtek ™ LS with LS System adhesive (LS). The dentin-composite disks were tested under cyclic diametral compression to determine the number of cycles to failure (Nf) at three load levels (n = 3 per group). Finite element analysis (FEA) was used to calculate the interfacial stresses (σ) within the specimen, to establish the σ vs. Nf curves, and those within a restored tooth under normal chewing forces (15N maximum). These were then used to estimate the lifetime of the restored tooth for the two restorative systems. Results The disks restored with LS had a higher fatigue resistance than those restored with Z100. The maximum interfacial stress in the restored tooth determined by FEA was ∼0.5MPa. Based on the estimate of 300,000 cycles of chewing per year, the predicted lifetime under occlusal loading for teeth restored with LS and Z100 was 33 and 10 years, respectively. Significance The disk in cyclic diametral compression has been used successfully to provide fatigue data which allows the lifetime of composite-restored teeth under occlusal loading to be predicted using numerical simulation. PMID:25958269
Life prediction of l6 steel using strain-life curve and cyclic stress-strain curve by means of low cycle fatigue testing

NASA Astrophysics Data System (ADS)

Inamdar, Sanket; Ukhande, Manoj; Date, Prashant; Lomate, Dattaprasad; Takale, Shyam; Singh, RKP

2017-05-01

L6 Steel is used as die material in closed die hot forging process. This material is having some unique properties. These properties are due to its composition. Strain softening is the noticeable property of this material. Due to this in spite of cracking at high stress this material gets plastically deformed and encounters loss in time as well as money. Studies of these properties are necessary to nurture this material at fullest extent. In this paper, numerous experiments have been carried on L6 material to evaluate cyclic Stress - strain behavior as swell as strain-life behavior of the material. Low cycle fatigue test is carried out on MTS fatigue test machine at fully reverse loading condition R=-1. Also strain softening effect on forging metal forming process is explained in detail. The failed samples during low cycle fatigue test further investigated metallurgically on scanning electron microscopy. Based on this study, life estimation of hot forging die is carried out and it’s correlation with actual shop floor data is found out. This work also concludes about effect of pre-treatments like nitro-carburizing and surface coating on L6 steel material, to enhance its fatigue life to certain extent.
Differences and similarities in fatigue behaviour and its influences on critical current and residual strength between Ti-Nb and Nb3Al superconducting composite wires

NASA Astrophysics Data System (ADS)

Ochiai, Shojiro; Oki, Yuichiro; Sekino, Fumiaki; Ohno, Hiroaki; Hojo, Masaki; Moriai, Hidezumi; Sakai, Shuji; Koganeya, Masanobu; Hayashi, Kazuhiko; Yamada, Yuichi; Ayai, Naoki; Watanabe, Kazuo

2000-04-01

The influences of fatigue damage introduced at room temperature on critical current at 4.2 K and residual strength at room temperature of Ti-Nb superconducting composite wire with a low copper ratio (1.04) were studied. The experimental results were compared with those of Nb3 Al composite. The following differences between the composites were found: the fracture surface of the Ti-Nb filaments in the composite varies from a ductile pattern under static loading to a brittle one under cyclic loading, while the Nb3 Al compound always shows a brittle pattern under both loadings; the fracture strength of the Ti-Nb composite is given by the net stress criterion but that of Nb3 Al by the stress intensity factor criterion; in the Ti-Nb composite the critical current Ic decreases with increasing number of stress cycles simultaneously with the residual strength icons/Journals/Common/sigma" ALT="sigma" ALIGN="TOP"/> c ,r , while in the Nb3 Al composite Ic decreases later than icons/Journals/Common/sigma" ALT="sigma" ALIGN="TOP"/> c ,r . On the other hand, both composites have the following similarities: the filaments are fractured due to the propagation of the fatigue crack nucleated in the copper; with increasing number of stress cycles, the damage progresses in the order of stage I (formation of cracks in the clad copper), stage II (stable propagation of the fatigue crack into the inner core) and stage III (overall fracture), among which stage II occurs in the late stage beyond 85 to 90% of the fatigue life; at intermediate maximum stress, many large cracks grow into the core portion at different cross sections but not at high and low maximum stresses; accordingly, the critical current and residual strength of the portion apart from the main crack are low for the intermediate maximum stress but not for low and high maximum stresses.
Low-cycle fatigue of Fe-20%Cr alloy processed by equal- channel angular pressing

NASA Astrophysics Data System (ADS)

Kaneko, Yoshihisa; Tomita, Ryuji; Vinogradov, Alexei

2014-08-01

Low-cycle fatigue properties were investigated on Fe-20%Cr ferritic stainless steel processed by equal channel angular pressing (ECAP). The Fe-20%Cr alloy bullets were processed for one to four passes via Route-Bc. The ECAPed samples were cyclically deformed at the constant plastic strain amplitude ɛpl of 5x10-4 at room temperature in air. After the 1-pass ECAP, low-angle grain boundaries were dominantly formed. During the low-cycle fatigue test, the 1-pass sample revealed the rapid softening which continued until fatigue fracture. Fatigue life of the 1-pass sample was shorter than that of a coarse-grained sample. After the 4-pass ECAP, the average grain size reduced down to about 1.5 μm. At initial stage of the low-cycle fatigue tests, the stress amplitude increased with increasing ECAP passes. At the samples processed for more than 2 passes, the cyclic softening was relatively moderate. It was found that fatigue life of the ECAPed Fe-20%Cr alloy excepting the 1-pass sample was improved as compared to the coarse-grained sample, even under the strain controlled fatigue condition.
Fatigue Analysis of Notched Laminates: A Time-Efficient Macro-Mechanical Approach

NASA Technical Reports Server (NTRS)

Naghipour, P.; Pineda, E. J.; Bednarcyk, B. A.; Arnold, S. M.; Waas, A. M.

2016-01-01

A coupled transversely isotropic deformation and damage fatigue model is implemented within the finite element method and was utilized along with a static progressive damage model to predict the fatigue life, stiffness degradation as a function of number of cycles, and post-fatigue tension and compression response of notched, multidirectional laminates. Initially, the material parameters for the fatigue model were obtained utilizing micromechanics simulations and the provided [0], [90] and [plus or minus 45] experimental composite laminate S-N (stress-cycle) data. Within the fatigue damage model, the transverse and shear properties of the plies were degraded with an isotropic scalar damage variable. The damage in the longitudinal (fiber) ply direction was suppressed, and only the strength of the fiber was degraded as a function of fatigue cycles. A maximum strain criterion was used to capture the failure in each element, and once this criterion was satisfied, the longitudinal stiffness of the element was decreased by a factor of 10 (sup 4). The resulting, degraded properties were then used to calculate the new stress state. This procedure was repeated until final failure of the composite laminate was achieved or a specified number of cycles reached. For post-fatigue tension and compression behavior, four internal state variables were used to control the damage and failure. The predictive capability of the above-mentioned approach was assessed by performing blind predictions of the notched multidirectional IM7/977-3 composite laminates response under fatigue and post-fatigue tensile and compressive loading, followed by a recalibration phase. Although three different multidirectional laminates were analyzed in the course of this study, only detailed results (i.e., stiffness degradation and post-fatigue stress-train curves as well as damage evolution states for a single laminate ([30/60/90/minus 30/minus 60] (sub 2s)) are discussed in detail here.
Fatigue behavior and life prediction of a SiC/Ti-24Al-11Nb composite under isothermal conditions. Ph.D. Thesis

NASA Technical Reports Server (NTRS)

Bartolotta, Paul A.

1991-01-01

Metal Matrix Composites (MMC) and Intermetallic Matrix Composites (IMC) were identified as potential material candidates for advanced aerospace applications. They are especially attractive for high temperature applications which require a low density material that maintains its structural integrity at elevated temperatures. High temperature fatigue resistance plays an important role in determining the structural integrity of the material. This study attempts to examine the relevance of test techniques, failure criterion, and life prediction as they pertain to an IMC material, specifically, unidirectional SiC fiber reinforced titanium aluminide. A series of strain and load controlled fatigue tests were conducted on unidirectional SiC/Ti-24Al-11Nb composite at 425 and 815 C. Several damage mechanism regimes were identified by using a strain-based representation of the data, Talreja's fatigue life diagram concept. Results of these tests were then used to address issues of test control modes, definition of failure, and testing techniques. Finally, a strain-based life prediction method was proposed for an IMC under tensile cyclic loadings at elevated temperatures.
Prediction of Contact Fatigue Life of Alloy Cast Steel Rolls Using Back-Propagation Neural Network

NASA Astrophysics Data System (ADS)

Jin, Huijin; Wu, Sujun; Peng, Yuncheng

2013-12-01

In this study, an artificial neural network (ANN) was employed to predict the contact fatigue life of alloy cast steel rolls (ACSRs) as a function of alloy composition, heat treatment parameters, and contact stress by utilizing the back-propagation algorithm. The ANN was trained and tested using experimental data and a very good performance of the neural network was achieved. The well-trained neural network was then adopted to predict the contact fatigue life of chromium alloyed cast steel rolls with different alloy compositions and heat treatment processes. The prediction results showed that the maximum value of contact fatigue life was obtained with quenching at 960 °C, tempering at 520 °C, and under the contact stress of 2355 MPa. The optimal alloy composition was C-0.54, Si-0.66, Mn-0.67, Cr-4.74, Mo-0.46, V-0.13, Ni-0.34, and Fe-balance (wt.%). Some explanations of the predicted results from the metallurgical viewpoints are given. A convenient and powerful method of optimizing alloy composition and heat treatment parameters of ACSRs has been developed.
Delamination onset in polymeric composite laminates under thermal and mechanical loads

NASA Technical Reports Server (NTRS)

Martin, Roderick H.

1991-01-01

A fracture mechanics damage methodology to predict edge delamination is described. The methodology accounts for residual thermal stresses, cyclic thermal stresses, and cyclic mechanical stresses. The modeling is based on the classical lamination theory and a sublaminate theory. The prediction methodology determines the strain energy release rate, G, at the edge of a laminate and compares it with the fatigue and fracture toughness of the composite. To verify the methodology, isothermal static tests at 23, 125, and 175 C and tension-tension fatigue tests at 23 and 175 C were conducted on laminates. The material system used was a carbon/bismaleimide, IM7/5260. Two quasi-isotropic layups were used. Also, 24 ply unidirectional double cantilever beam specimens were tested to determine the fatigue and fracture toughness of the composite at different temperatures. Raising the temperature had the effect of increasing the value of G at the edge for these layups and also to lower the fatigue and fracture toughness of the composite. The static stress to edge delamination was not affected by temperature but the number of cycles to edge delamination decreased.

Fatigue crack growth in fiber reinforced plastics

NASA Technical Reports Server (NTRS)

Mandell, J. F.

1979-01-01

Fatigue crack growth in fiber composites occurs by such complex modes as to frustrate efforts at developing comprehensive theories and models. Under certain loading conditions and with certain types of reinforcement, simpler modes of fatigue crack growth are observed. These modes are more amenable to modeling efforts, and the fatigue crack growth rate can be predicted in some cases. Thus, a formula for prediction of ligamented mode fatigue crack growth rate is available.
Atomistic origin of size effects in fatigue behavior of metallic glasses

NASA Astrophysics Data System (ADS)

Sha, Zhendong; Wong, Wei Hin; Pei, Qingxiang; Branicio, Paulo Sergio; Liu, Zishun; Wang, Tiejun; Guo, Tianfu; Gao, Huajian

2017-07-01

While many experiments and simulations on metallic glasses (MGs) have focused on their tensile ductility under monotonic loading, the fatigue mechanisms of MGs under cyclic loading still remain largely elusive. Here we perform molecular dynamics (MD) and finite element simulations of tension-compression fatigue tests in MGs to elucidate their fatigue mechanisms with focus on the sample size effect. Shear band (SB) thickening is found to be the inherent fatigue mechanism for nanoscale MGs. The difference in fatigue mechanisms between macroscopic and nanoscale MGs originates from whether the SB forms partially or fully through the cross-section of the specimen. Furthermore, a qualitative investigation of the sample size effect suggests that small sample size increases the fatigue life while large sample size promotes cyclic softening and necking. Our observations on the size-dependent fatigue behavior can be rationalized by the Gurson model and the concept of surface tension of the nanovoids. The present study sheds light on the fatigue mechanisms of MGs and can be useful in interpreting previous experimental results.
Effect of alloy composition on high-temperature bending fatigue strength of ferritic stainless steels

NASA Astrophysics Data System (ADS)

Ahn, Yong-Sik; Song, Jeon-Young

2011-12-01

Exhaust manifolds are subjected to an environment in which heating and cooling cycles occur due to the running pattern of automotive engines. This temperature profile results in the repeated bending stress of exhaust pipes. Therefore, among high-temperature characteristics, the bending fatigue strength is an important factor that affects the lifespan of exhaust manifolds. Here, we report on the effect of the alloy composition, namely the weight fraction of the elements Cr, Mo, Nb, and Ti, on the high-temperature bending fatigue strength of the ferritic stainless steel used in exhaust manifolds. Little difference in the tensile strength and bending fatigue strength of the different composition steels was observed below 600 °C, with the exception of the low-Cr steel. However, steels with high Cr, Mo, or Nb fractions showed considerably larger bending fatigue strength at temperatures of 800 °C. After heating, the precipitates from the specimens were extracted electrolytically and analyzed using scanning electron microscopy energy dispersive spectrometry and transmission electron microscopy. Alloying with Cr and Mo was found to increase the bending fatigue strength due to the substitutional solid solution effect, while alloying with Nb enhanced the strength by forming fine intermetallic compounds, including NbC and Fe2Nb.
The influence of matrix microstructure

NASA Astrophysics Data System (ADS)

Vyletel, G. M.; Allison, J. E.; Aken, D. C.

1993-11-01

The low-cycle and high-cycle fatigue behavior and cyclic response of naturally aged and artificially aged 2219/TiC/15p and unreinforced 2219 Al were investigated utilizing plastic strain-controlled and stress-controlled testing. The cyclic response of both the reinforced and un-reinforced materials was similar for all plastic strain amplitudes tested except that the saturation stress level for the composite was always greater than that of the unreinforced material. The cyclic response of the naturally aged materials exhibited cyclic hardening and, in some cases, cyclic softening, while the cyclic response for the artificially aged materials showed no evidence of either cyclic hardening or softening. The higher ductility of the unreinforced material made it more resistant to fatigue failure at high strains, and thus, at a given plastic strain, it had longer fatigue life. It should be noted that the tensile ductilities of the 2219/TiC/15p were significantly higher than those previously reported for 2XXX-series composites. During stress-controlled test-ing at stresses below 220 MPa, the presence of TiC particles lead to an improvement in fatigue life. Above 220 MPa, no influence of TiC reinforcement on fatigue life could be detected. In both the composite and unreinforced materials, the low-cycle and high-cycle fatigue lives were found to be virtually independent of matrix microstructure.
Elevated Temperature Fatigue Endurance of Three Ceramic Matrix Composites

NASA Technical Reports Server (NTRS)

Kalluri, Sreeramesh; Verrilli, Michael J.

2007-01-01

High-cycle fatigue endurance of three candidate materials for the acoustic liners of the Enabling Propulsion Materials Nozzle Program was investigated. The ceramic matrix composite materials investigated were N720/AS (Nextel 720, 3M Corporation), Sylramic S200 (Dow Corning), and UT 22. High-cycle fatigue tests were conducted in air at 910 C on as-machined specimens and on specimens subjected to tensile cyclic load excursions every 160 hr followed by thermal exposure at 910 C in a furnace up to total exposure times of 2066 and 4000 hr. All the fatigue tests were conducted in air at 100 Hz with a servohydraulic test machine. In the as-machined condition, among the three materials investigated only the Sylramic S200 exhibited a deterministic type of high-cycle fatigue behavior. Both the N720/AS and UT-22 exhibited significant scatter in the experimentally observed high-cycle fatigue lives. Among the thermally exposed specimens, N720/AS and Sylramic S200 materials exhibited a reduction in the high-cycle fatigue lives, particularly at the exposure time of 4000 hr.
Fatigue Behavior and the Relationship Between Crack Propagation and the Slit Configuration of C/c Composites

NASA Astrophysics Data System (ADS)

Ferdous, Md. Shafiul; Setyabudi, Sofyan Arief; Makabe, Chobin; Fujikawa, Masaki

2013-05-01

The fatigue and fracture behavior of C/C composites fabricated using fine-woven carbon fiber laminates with α = 0/90° direction were investigated. Also, the phenomenon of crack growth behavior and the shear damage in the fiber bundle was discussed. Slits of several sizes were cut on both sides of a test section and different sizes of slit length were chosen. The effect of the slit configuration on crack initiation and growth behavior was observed. Specimens with blunt-notches and center-holes were also used to compare the fatigue strength and crack growth behavior. Non-propagating cracks were observed and fatigue limit was defined as the maximum stress at which specimen did not break for N = 107 cycles stress application. The longest fatigue life was obtained in the case of specimens with shorter slits. The relationships between fatigue strengths and specimen shapes were analyzed by stress concentration, Kt, and stress intensity factor, KI. The effect of slit configuration on fatigue strength was then discussed regarding both the experimental and calculated consequences.
Tension and compression fatigue response of unnotched 3D braided composites

NASA Technical Reports Server (NTRS)

Portanova, M. A.

1992-01-01

The unnotched compression and tension fatigue response of a 3-D braided composite was measured. Both gross compressive stress and tensile stress were plotted against cycles to failure to evaluate the fatigue life of these materials. Damage initiation and growth was monitored visually and by tracking compliance change during cycle loading. The intent was to establish by what means the strength of a 3-D architecture will start to degrade, at what point will it degrade beyond an acceptable level, and how this material will typically fail.
Quiet Clean Short-haul Experimental Engine (QCSEE) under-the-wing engine composite fan blade design report

NASA Technical Reports Server (NTRS)

Ravenhall, R.; Salemme, C. T.

1977-01-01

A total of 38 quiet clean short haul experimental engine under the wing composite fan blades were manufactured for various component tests, process and tooling, checkout, and use in the QCSEE UTW engine. The component tests included frequency characterization, strain distribution, bench fatigue, platform static load, whirligig high cycle fatigue, whirligig low cycle fatigue, whirligig strain distribution, and whirligig over-speed. All tests were successfully completed. All blades planned for use in the engine were subjected to and passed a whirligig proof spin test.
The fatigue behavior of composite laminates under various mean stresses

NASA Technical Reports Server (NTRS)

Rotem, A.

1991-01-01

A method is developed for predicting the S-N curve of a composite laminate which is subjected to an arbitrary stress ratio, R (minimum stress/maximum stress). The method is based on the measuring of the S-N behavior of two distinct cases, tension-tension and compression-compression fatigue loadings. Using these parameters, expressions are formulated that estimate the fatigue behavior under any stress ratio loading. Experimental results from the testing of graphite/epoxy laminates, with various structures, are compared with the predictions and show good agreement.
Effect of fatigue loading on critical current in stainless steel-laminated DI-BSCCO superconducting composite tape

NASA Astrophysics Data System (ADS)

Hojo, M.; Osawa, K.; Adachi, T.; Inoue, Y.; Osamura, K.; Ochiai, S.; Ayai, N.; Hayashi, K.

2010-11-01

Tensile strain tolerance of the critical current in (Bi,Pb)2Sr2Ca2Cu3Ox (Bi2223) composite superconductor is dramatically improved when the tape is laminated with stainless steel. For practical applications, it is important to understand whether this reinforcement by lamination is effective under fatigue loading. In the present study, we carried out fatigue tests in LN2 and measured the critical current at the specific fatigue cycles to clarify the strain tolerance of the critical current in stainless steel-laminated drastically innovative Bi2223 (DI-BSCCO®) tapes. The fatigue tests were carried out using a computer-controlled 10 kN servo-hydraulic fatigue testing machine with a load cell capacity of 2.5 kN. Tests under static loading showed that the irreversible stress at which the critical current is reduced by 1% from the original value (tensile stress at Ic/Ic0 = 0.99) was 315 MPa when measured at unloading state. The present fatigue tests results indicated that the critical current was maintained at over 98% of the original value at unloading state after stress cycles of 106 when the static irreversible stress was selected as the maximum stress under fatigue loading. Thus, laminated DI-BSCCO tapes showed excellent mechanical properties even under fatigue loading.
Certification Testing Methodology for Composite Structure. Volume 2. Methodology Development

DTIC Science & Technology

1986-10-01

parameter, sample size and fa- tigue test duration. The required input are 1. Residual strength Weibull shape parameter ( ALPR ) 2. Fatigue life Weibull shape...INPUT STRENGTH ALPHA’) READ(*,*) ALPR ALPRI = 1.O/ ALPR WRITE(*, 2) 2 FORMAT( 2X, ’PLEASE INPUT LIFE ALPHA’) READ(*,*) ALPL ALPLI - 1.0/ALPL WRITE(*, 3...3 FORMAT(2X,’PLEASE INPUT SAMPLE SIZE’) READ(*,*) N AN - N WRITE(*,4) 4 FORMAT(2X,’PLEASE INPUT TEST DURATION’) READ(*,*) T RALP - ALPL/ ALPR ARGR - 1
Nonlinear acoustic measurements ahead of a notch during fatigue

NASA Astrophysics Data System (ADS)

Martin, R. W.; Mooers, R. D.; Hutson, A. L.; Sathish, S.; Blodgett, M. P.

2013-01-01

This paper presents measurements of relative nonlinear acoustic parameter (βrel), ahead of a notch in Al 7075-T651 dog bone samples, subjected to fatigue. It is compared with crack growth measurements on the same samples. Measurements performed on two samples subjected to identical fatigue conditions that failed at vastly different number of fatigue cycles are described. The βrel measurement for both samples as a function of fatigue cycles was fit a Boltzmann curve. The role of changing βrel ahead of a notch is explored as a possible approach for remain life evaluation.
Carbide factor predicts rolling-element bearing fatigue life

NASA Technical Reports Server (NTRS)

Chevalier, J. L.; Zaretsky, E. V.

1973-01-01

Analysis was made to determine correlation between number and size of carbide particles and rolling-element fatigue. Correlation was established, and carbide factor was derived that can be used to predict fatigue life more effectively than such variables as heat treatment, chemical composition, and hardening mechanism.
Effects of a pulsed electromagnetic therapy on multiple sclerosis fatigue and quality of life: a double-blind, placebo controlled trial.

PubMed

Lappin, Martha S; Lawrie, Fraser Wilson; Richards, Todd L; Kramer, Eric D

2003-01-01

There is a growing literature on the biological and clinical effects of pulsed electromagnetic fields. Some studies suggest that electromagnetic therapies may be useful in the treatment of chronic illnesses. This study is a follow-up to a placebo controlled pilot study in which multiple sclerosis (MS) patients exposed to weak, extremely low frequency pulsed electromagnetic fields showed significant improvements on a composite symptom measure. To evaluate the effects of a pulsed electromagnetic therapy on MS related fatigue, spasticity, bladder control, and overall quality of life. A multi-site, double-blind, placebo controlled, crossover trial. Each subject received 4 weeks of the active and placebo treatments separated by a 2-week washout period. The University of Washington Medical Center in Seattle Wash, the Neurology Center of Fairfax in Fairfax, Va, and the headquarters of the Multiple Sclerosis Association of America in Cherry Hill, NJ. 117 patients with clinically definite MS. Daily exposure to a small, portable pulsing electromagnetic field generator. The MS Quality of Life Inventory (MSQLI) was used to assess changes in fatigue, bladder control, spasticity, and a quality of life composite. Paired t-tests were used to assess treatment differences in the 117 subjects (81% of the initial sample) who completed both treatment sessions. Improvements in fatigue and overall quality of life were significantly greater on the active device. There were no treatment effects for bladder control and a disability composite, and mixed results for spasticity. Evidence from this randomized, double-bind, placebo controlled trial is consistent with results from smaller studies suggesting that exposure to pulsing, weak electromagnetic fields can alleviate symptoms of MS. The clinical effects were small, however, and need to be replicated. Additional research is also needed to examine the possibility that ambulatory patients and patients taking interferons for their MS may be most responsive to this kind of treatment.
Static and Fatigue Analysis of Wind Turbine Blades Subject to Cold Weather Conditions Using Finite Element Analysis

NASA Astrophysics Data System (ADS)

Lillo Gallardo, Patricio Andres

Canada has aggressive targets for introducing wind energy across the country, but also faces challenges in achieving these goals due to the harsh Canadian climate. One issue which has received little attention in other countries not experiencing these extremes is the behaviour of composite blades in winter conditions. The scope of the work presented is to analyze the static stresses and fatigue response in cold climates using finite element models of the blade. The work opens with a quantification of the extremes of cold experienced in candidate Canadian wind turbine deployment locations. The thesis then narrows its focus to a consideration of the stresses in the root of the composite blades, specifically two common blade-hub connection methods: embedded root carrots and T-bolts. Finite element models of the root are proposed to properly simulate boundary conditions, applied loading and thermal stresses for a 1.5 MW wind turbine. It is shown that the blade root is strongly affected by the thermal stresses caused by the mismatch and orthotrophy of the coefficients of thermal expansion of the blade root constituents. Fatigue analysis of a blade is then presented using temperature dependent material properties including estimated fatigue coefficients.It was found that the natural frequencies of a 1.5 MW wind turbine blade are not significantly altered at cold temperatures. Additionally, cold temperatures slightly increase stresses in the composite blade skin when the blade is loaded, due to an increase in stiffness. Cold temperatures also lead to higher cyclic flapwise bending moments acting on the blade. However, this increase was found not to affect the lifetime fatigue damage. Finally, it was found that the cold climate as seen in Canada improves the fatigue strength of the saturated composite materials used in the blade. The predicted fatigue damage of the triaxial fabric and the spar cap layers in cold climates was therefore predicted to be half that of the fatigue damage at room temperature. This is caused solely by the temperature dependence of the fatigue coefficient b which requires further experimental verification to validate the numerical results of the current study.
A Simulation of Low and High Cycle Fatigue Failure Effects for Metal Matrix Composites Based on Innovative J2-Flow Elastoplasticity Model

PubMed Central

Wang, Zhaoling; Xiao, Heng

2017-01-01

New elastoplastic J2-flow constitutive equations at finite deformations are proposed for the purpose of simulating the fatigue failure behavior for metal matrix composites. A new, direct approach is established in a two-fold sense of unification. Namely, both low and high cycle fatigue failure effects of metal matrix composites may be simultaneously simulated for various cases of the weight percentage of reinforcing particles. Novel results are presented in four respects. First, both the yield condition and the loading–unloading conditions in a usual sense need not be involved but may be automatically incorporated into inherent features of the proposed constitutive equations; second, low-to-high cycle fatigue failure effects may be directly represented by a simple condition for asymptotic loss of the material strength, without involving any additional damage-like variables; third, both high and low cycle fatigue failure effects need not be separately treated but may be automatically derived as model predictions with a unified criterion for critical failure states, without assuming any ad hoc failure criteria; and, finally, explicit expressions for each incorporated model parameter changing with the weight percentage of reinforcing particles may be obtainable directly from appropriate test data. Numerical examples are presented for medium-to-high cycle fatigue failure effects and for complicated duplex effects from low to high cycle fatigue failure effects. Simulation results are in good agreement with experimental data. PMID:28946637
The ultimate state of polymeric materials and laminated and fibrous composites under asymmetric high-cycle loading

NASA Astrophysics Data System (ADS)

Golub, V. P.; Pogrebniak, A. D.; Kochetkova, E. S.

2008-01-01

The prediction of the high-cycle fatigue strength of polymeric and composite materials in asymmetric loading is considered. The problem is solved on the basis of a nonlinear model of ultimate state allowing us to describe all typical forms of the diagrams of ultimate stresses. The material constants of the model are determined from the results of fatigue tests in symmetric reversed cycling, in a single fatigue test with the minimum stress equal to zero, and in a short-term strength test. The fatigue strength characteristics of some polymers, glass-fiber laminates, glass-fiber-reinforced plastics, organic-fiber-reinforced plastics, and wood laminates in asymmetric tension-compression, bending, and torsion have been calculated and approved experimentally.
Creep-fatigue of low cobalt superalloys

NASA Technical Reports Server (NTRS)

Halford, G. R.

1982-01-01

Testing for the low cycle fatigue and creep fatigue resistance of superalloys containing reduced amounts of cobalt is described. The test matrix employed involves a single high temperature appropriate for each alloy. A single total strain range, again appropriate to each alloy, is used in conducting strain controlled, low cycle, creep fatigue tests. The total strain range is based upon the level of straining that results in about 10,000 cycles to failure in a high frequency (0.5 Hz) continuous strain-cycling fatigue test. No creep is expected to occur in such a test. To bracket the influence of creep on the cyclic strain resistance, strain hold time tests with ore minute hold periods are introduced. One test per composition is conducted with the hold period in tension only, one in compression only, and one in both tension and compression. The test temperatures, alloys, and their cobalt compositions that are under study are given.
Ecological momentary assessment of fatigue, sleepiness, and exhaustion in ESKD.

PubMed

Abdel-Kader, Khaled; Jhamb, Manisha; Mandich, Lee Anne; Yabes, Jonathan; Keene, Robert M; Beach, Scott; Buysse, Daniel J; Unruh, Mark L

2014-02-06

Many patients on maintenance dialysis experience significant sleepiness and fatigue. However, the influence of the hemodialysis (HD) day and circadian rhythms on patients' symptoms have not been well characterized. We sought to use ecological momentary assessment to evaluate day-to-day and diurnal variability of fatigue, sleepiness, exhaustion and related symptoms in thrice-weekly maintenance HD patients. Subjects used a modified cellular phone to access an interactive voice response system that administered the Daytime Insomnia Symptom Scale (DISS). The DISS assessed subjective vitality, mood, and alertness through 19 questions using 7- point Likert scales. Subjects completed the DISS 4 times daily for 7 consecutive days. Factor analysis was conducted and a mean composite score of fatigue-sleepiness-exhaustion was created. Linear mixed regression models (LMM) were used to examine the association of time of day, dialysis day and fatigue, sleepiness, and exhaustion composite scores. The 55 participants completed 1,252 of 1,540 (81%) possible assessments over the 7 day period. Multiple symptoms related to mood (e.g., feeling sad, feeling tense), cognition (e.g., difficulty concentrating), and fatigue (e.g., exhaustion, feeling sleepy) demonstrated significant daily and diurnal variation, with higher overall symptom scores noted on hemodialysis days and later in the day. In factor analysis, 4 factors explained the majority of the observed variance for DISS symptoms. Fatigue, sleepiness, and exhaustion loaded onto the same factor and were highly intercorrelated. In LMM, mean composite fatigue-sleepiness-exhaustion scores were associated with dialysis day (coefficient and 95% confidence interval [CI] 0.21 [0.02 - 0.39]) and time of day (coefficient and 95% CI 0.33 [0.25 - 0.41]. Observed associations were minimally affected by adjustment for demographics and common confounders. Maintenance HD patients experience fatigue-sleepiness-exhaustion symptoms that demonstrate significant daily and diurnal variation. The variability in symptoms may contribute to poor symptom awareness by providers and greater misclassification bias of fatigue related symptoms in clinical studies.
A Continuum Damage Mechanics Model for the Static and Cyclic Fatigue of Cellular Composites

PubMed Central

Huber, Otto

2017-01-01

The fatigue behavior of a cellular composite with an epoxy matrix and glass foam granules is analyzed and modeled by means of continuum damage mechanics. The investigated cellular composite is a particular type of composite foam, and is very similar to syntactic foams. In contrast to conventional syntactic foams constituted by hollow spherical particles (balloons), cellular glass, mineral, or metal place holders are combined with the matrix material (metal or polymer) in the case of cellular composites. A microstructural investigation of the damage behavior is performed using scanning electron microscopy. For the modeling of the fatigue behavior, the damage is separated into pure static and pure cyclic damage and described in terms of the stiffness loss of the material using damage models for cyclic and creep damage. Both models incorporate nonlinear accumulation and interaction of damage. A cycle jumping procedure is developed, which allows for a fast and accurate calculation of the damage evolution for constant load frequencies. The damage model is applied to examine the mean stress effect for cyclic fatigue and to investigate the frequency effect and the influence of the signal form in the case of static and cyclic damage interaction. The calculated lifetimes are in very good agreement with experimental results. PMID:28809806

Modeling of crack bridging in a unidirectional metal matrix composite

NASA Technical Reports Server (NTRS)

Ghosn, Louis J.; Kantzos, Pete; Telesman, Jack

1991-01-01

The effective fatigue crack driving force and crack opening profiles were determined analytically for fatigue tested unidirectional composite specimens exhibiting fiber bridging. The crack closure pressure due to bridging was modeled using two approaches; the fiber pressure model and the shear lag model. For both closure models, the Bueckner weight function method and the finite element method were used to calculate crack opening displacements and the crack driving force. The predicted near crack tip opening profile agreed well with the experimentally measured profiles for single edge notch SCS-6/Ti-15-3 metal matrix composite specimens. The numerically determined effective crack driving force, Delta K(sup eff), was calculated using both models to correlate the measure crack growth rate in the composite. The calculated Delta K(sup eff) from both models accounted for the crack bridging by showing a good agreement between the measured fatigue crack growth rates of the bridged composite and that of unreinforced, unbridged titanium matrix alloy specimens.
Modeling of crack bridging in a unidirectional metal matrix composite

NASA Technical Reports Server (NTRS)

Ghosn, Louis J.; Kantzos, Pete; Telesman, Jack

1992-01-01

The effective fatigue crack driving force and crack opening profiles were determined analytically for fatigue tested unidirectional composite specimens exhibiting fiber bridging. The crack closure pressure due to bridging was modeled using two approaches: the fiber pressure model and the shear lag model. For both closure models, the Bueckner weight function method and the finite element method were used to calculate crack opening displacements and the crack driving force. The predicted near crack tip opening profile agreed well with the experimentally measured profiles for single edge notch SCS-6/Ti-15-3 metal matrix composite specimens. The numerically determined effective crack driving force, Delta K(eff), was calculated using both models to correlate the measure crack growth rate in the composite. The calculated Delta K(eff) from both models accounted for the crack bridging by showing a good agreement between the measured fatigue crack growth rates of the bridged composite and that of unreinforced, unbridged titanium matrix alloy specimens.
Fatigue Behavior Degradation due to the Interlaminar Conditions in Lightweight Piezoelectric Composite Actuator (lipca)

NASA Astrophysics Data System (ADS)

Kim, Cheol-Woong; Yoon, Kwang-Joon

The advanced piezoelectric ceramic composite actuator, which is called LIPCA (LIghtweight Piezoelectric Composite Actuator), replaced the Al foil and stainless steel in THUNDER with the FRP and the optimization of the laminate configuration was performed to maximize the stress transfer and the fiber bridging effect. This study evaluated the fatigue characteristics in LIPCA under the resonance frequency, and the changes of its interlaminar phase were also evaluated. Beside, the residual stress distribution was estimated. In conclusions, firstly, comparing with the fatigue life of LIPCA without the artificial delamination (intact LIPCA), the fatigue life of LIPCA embedded by the artificial delamination was decreased up to 50%. Secondly, the micro void growth and the coalescence of epoxy were actively made at the interlaminar phase subject to the large tensile stress. Finally, it was known that the harmonic configuration between the compressive residuals stress and the tensile one was made. The requirement of the performance displacement increment was satisfied.
Central activation, metabolites, and calcium handling during fatigue with repeated maximal isometric contractions in human muscle.

PubMed

Cairns, Simeon P; Inman, Luke A G; MacManus, Caroline P; van de Port, Ingrid G L; Ruell, Patricia A; Thom, Jeanette M; Thompson, Martin W

2017-08-01

To determine the roles of calcium (Ca 2+ ) handling by sarcoplasmic reticulum (SR) and central activation impairment (i.e., central fatigue) during fatigue with repeated maximal voluntary isometric contractions (MVC) in human muscles. Contractile performance was assessed during 3 min of repeated MVCs (7-s contraction, 3-s rest, n = 17). In ten participants, in vitro SR Ca 2+ -handling, metabolites, and fibre-type composition were quantified in biopsy samples from quadriceps muscle, along with plasma venous [K + ]. In 11 participants, central fatigue was compared using tetanic stimulation superimposed on MVC in quadriceps and adductor pollicis muscles. The decline of peak MVC force with fatigue was similar for both muscles. Fatigue resistance correlated directly with % type I fibre area in quadriceps (r = 0.77, P = 0.009). The maximal rate of ryanodine-induced Ca 2+ -release and Ca 2+ -uptake fell by 31 ± 26 and 28 ± 13%, respectively. The tetanic force depression was correlated with the combined reduction of ATP and PCr, and increase of lactate (r = 0.77, P = 0.009). Plasma venous [K + ] increased from 4.0 ± 0.3 to 5.4 ± 0.8 mM over 1-3-min exercise. Central fatigue occurred during the early contractions in the quadriceps in 7 out of 17 participants (central activation ratio fell from 0.98 ± 0.05 to 0.86 ± 0.11 at 1 min), but dwindled at exercise cessation. Central fatigue was seldom apparent in adductor pollicis. Fatigue with repeated MVC in human limb muscles mainly involves peripheral aspects which include impaired SR Ca 2+ -handling and we speculate that anaerobic metabolite changes are involved. A faster early force loss in quadriceps muscle with some participants is attributed to central fatigue.
The Effect of Hydrofluoric Acid Surface Treatment on the Cyclic Fatigue Resistance of K3 NiTi Instruments

PubMed Central

2017-01-01

The aim of this study was to investigate the effect of 50% hydrofluoric acid (HF) surface treatment on the cyclic fatigue resistance (CFR) of K3 NiTi instruments. Twenty as-received and twenty HF-treated K3 NiTi instruments were compared in CFR. The surface texture and fracture surface of two instrument groups were examined with a scanning electron microscope (SEM). Additionally, any change of Ni and Ti composition from both instrument groups was investigated using energy dispersive spectrometry. The results were analyzed with t-test. The HF-treated K3 group showed statistically higher cyclic fatigue resistance than as-received K3 group (P < 0.05). HF-treated K3 instruments showed smoother and rounded surface compared to as-received K3 under SEM observation. The fracture surfaces of both groups showed typical patterns of cyclic fatigue fracture. There was no difference in surface Ni and Ti composition between two groups. HF treatment of K3 instruments smoothed the file surface and increased the cyclic fatigue resistance, while it had no effect on surface ion composition and the file fracture pattern. PMID:28539854
Effects of two grading techniques of zirconia material on the fatigue limit of full-contour 3-unit fixed dental prostheses

PubMed Central

Villefort, Regina Furbino; Amaral, Marina; Pereira, Gabriel Kalil Rocha; Campos, Tiago Moreira Bastos; Zhang, Yu; Bottino, Marco Antonio; Valandro, Luiz Felipe; de Melo, Renata Marques

2017-01-01

Objective This study evaluated the effects of two grading zirconia techniques on the fatigue limit of 3-unit fixed dental prostheses (FDPs). Methods Presintered blocks of 3Y-TZP were milled to obtain sixty-nine 3-unit FDPs, which were divided into three groups (n = 23). The control group (CTL) was sintered and glazed following manufacturer’s instructuctions. The two experimental groups presintered FDPs received a surface silica/glass infiltration treatment before the sintering process. Silica sol-gel group (SSG) was graded by the sol-gel processing route, while the glass-zirconia-glass group (GZG) was graded by an enameling technique. Graded groups did not receive a glaze layer after sintering. All FDPs were then luted with a dual-curing resin cement on composite abutments, embedded in polyurethane and stored in water for five days. The initial load of the fatigue test was calculated based on the results of the monotonic testing applied on three specimens of each group. To determine the fatigue limit, 20 samples of each group were subjected to staircase testing (100,000 cycles/5 Hz). Results The fatigue limits (in Newtons) were CTL = 1607.27, SSG = 1824.31, and GZG = 2006.57, and the Dixon and Mood test indicated statistically significant differences among groups (95% confidence interval). Significance The infiltration of silica and glass on bulk zirconia, by two different grading methods, increased the fatigue limits of monolithic zirconia FDPs. PMID:28118929
Effects of Control Mode and R-Ratio on the Fatigue Behavior of a Metal Matrix Composite

NASA Technical Reports Server (NTRS)

2005-01-01

Composite Because of their high specific stiffness and strength at elevated temperatures, continuously reinforced metal matrix composites (MMC's) are under consideration for a future generation of aeropropulsion systems. Since components in aeropropulsion systems experience substantial cyclic thermal and mechanical loads, the fatigue behavior of MMC's is of great interest. Almost without exception, previous investigations of the fatigue behavior of MMC's have been conducted in a tension-tension, load-controlled mode. This has been due to the fact that available material is typically less than 2.5-mm thick and, therefore, unable to withstand high compressive loads without buckling. Since one possible use of MMC's is in aircraft skins, this type of testing mode may be appropriate. However, unlike aircraft skins, most engine components are thick. In addition, the transient thermal gradients experienced in an aircraft engine will impose tension-compression loading on engine components, requiring designers to understand how the MMC will behave under fully reversed loading conditions. The increased thickness of the MMC may also affect the fatigue life. Traditionally, low-cycle fatigue (LCF) tests on MMC's have been performed in load control. For monolithic alloys, low-cycle fatigue tests are more typically performed in strain control. Two reasons justify this choice: (1) the critical volume from which cracks initiate and grow is generally small and elastically constrained by the larger surrounding volume of material, and (2) load-controlled, low-cycle fatigue tests of monolithics invariably lead to unconstrained ratcheting and localized necking--an undesired material response because the failure mechanism is far more severe than, and unrelated to, the fatigue mechanism being studied. It is unknown if this is the proper approach to composite testing. However, there is a lack of strain-controlled data on which to base any decisions. Consequently, this study addresses the isothermal, LCF behavior of a [0]_32 MMC tested under strain- and load-controlled conditions for both zero-tension and tension-compression loading conditions. These tests were run at 427 C on thick specimens of SiC-reinforced Ti-15-3. For the fully-reversed tests, no difference was observed in the lives between the load- and strain-controlled tests. However, for the zero-tension tests, the strain-controlled tests had longer lives by a factor of 3 in comparison to the load-controlled tests. This was due to the fact that under strain-control the specimens cyclically softened, reducing the cracking potential. In contrast, the load-controlled tests ratcheted toward larger tensile strains leading to an eventual overload of the fibers. Fatigue tests revealed that specimens tested under fully-reversed conditions had lives approximately an order of magnitude longer than for those specimens tested under zero tension. When examined on a strain-range basis, the fully reversed specimens had similar, but still shorter lives than those of the unreinforced matrix material. However, the composite had a strain limitation at short lives because of the limited strain capacity of the brittle ceramic fiber. The composite also suffered at very high lives because of the lack of an apparent fatigue limit in comparison to the unreinforced matrix. The value of adding fibers to the matrix is apparent when the fatigue lives are plotted as a function of stress range. Here, the composite is far superior to the unreinforced matrix because of the additional load-carrying capacity of the fibers.
Fatigue Crack Growth and Retardation Due to Overloads in Metal-matrix Composites Volume I. Fatigue Crack Growth In Boron-Aluminum Metal-Matrix Composites

DTIC Science & Technology

1986-08-01

respectively ...... ......................... . 61 3.4 Fatigue specimen design curves for 90, 45, and 15 degree orientations in (a), (b), and (c... 61 0.n.500’~~~ .’ 0 * IN lo .00. is 7I=. 2000. Figure 2.12 Strain history from gages along a line 90 degrees to the loading. Notice the high...remover (# SKD -NF/ZC-7B). A developer (# SKD -NF/ZP-9B) was then sprayed on to draw the remaining dye out of the crack, leaving behind a bright red mark where
Fatigue failure processes in aligned carbon-epoxy laminates

NASA Astrophysics Data System (ADS)

Piggott, Michael R.; Lam, Patrick W. K.

The failure mechanism involved in the tensile-tensile fatigue of carbon fiber-reinforced polymer matrices may be initiated by the fiber curvature that can be present in the composite. The varying stresses encountered in fatigue begin to damage the composite at the antinodes of the fiber profiles, perhaps in the form of fiber debonds that generate matrix cracks and result in comminution of the polymer; eventually, as the process proceeds, the flexural stresses in the fiber are sufficiently great to cause early fiber failure in wavy regions. The breaks are connected by splits in the polymer.
Electrical Stimulation Frequency and Skeletal Muscle Characteristics: Effects on Force and Fatigue.

PubMed

Vromans, Maria; Faghri, Pouran

2017-12-05

This investigation aimed to determine the force and muscle surface electromyography (EMG) responses to different frequencies of electrical stimulation (ES) in two groups of muscles with different size and fiber composition (fast- and slow-twitch fiber proportions) during a fatigue-inducing protocol. Progression towards fatigue was evaluated in the abductor pollicis brevis (APB) and vastus lateralis (VL) when activated by ES at three frequencies (10, 35, and 50Hz). Ten healthy adults (mean age: 23.2 ± 3.0 years) were recruited; participants signed an IRB approved consent form prior to participation. Protocols were developed to 1) identify initial ES current intensity required to generate the 25% maximal voluntary contraction (MVC) at each ES frequency and 2) evaluate changes in force and EMG activity during ES-induced contraction at each frequency while progressing towards fatigue. For both muscles, stimulation at 10Hz required higher current intensity of ES to generate the initial force. There was a significant decline in force in response to ES-induced fatigue for all frequencies and for both muscles (p<0.05). However, the EMG response was not consistent between muscles. During the progression towards fatigue, the APB displayed an initial drop in force followed by an increase in EMG activity and the VL displayed a decrease in EMG activity for all frequencies. Overall, it appeared that there were some significant interactions between muscle size and fiber composition during progression towards fatigue for different ES frequencies. It could be postulated that muscle characteristics (size and fiber composition) should be considered when evaluating progression towards fatigue as EMG and force responses are not consistent between muscles.
Influence of frequency on shear fatigue strength of resin composite to enamel bonds using self-etch adhesives.

PubMed

Takamizawa, Toshiki; Scheidel, Donal D; Barkmeier, Wayne W; Erickson, Robert L; Tsujimoto, Akimasa; Latta, Mark A; Miyazaki, Masashi

2016-09-01

The purpose of this study was to determine the influence of different frequency rates on of bond durability of self-etch adhesives to enamel using shear fatigue strength (SFS) testing. A two-step self-etch adhesive (OX, OptiBond XTR), and two single step self-etch adhesives (GB, G-ӕnial Bond and SU, Scotchbond Universal) were used in this study. The shear fatigue strength (SFS) to enamel was obtained. A staircase method was used to determine the SFS values with 50,000 cycles or until failure occurred. Fatigue testing was performed at frequencies of 5Hz, 10Hz, and 20Hz. For each test condition, 30 specimens were prepared for the SFS testing. Regardless of the bond strength test method, OX showed significantly higher SFS values than the two single-step self-etch adhesives. For each of the three individual self-etch adhesives, there was no significant difference in SFS depending on the frequency rate, although 20Hz results tended to be higher. Regardless of the self-etch adhesive system, frequencies of 5Hz, 10Hz, and 20Hz produced similar results in fatigue strength of resin composite bonded to enamel using 50,000 cycles or until bond failure. Accelerated fatigue testing provides valuable information regarding the long term durability of resin composite to enamel bonding using self-etch adhesive system. Copyright © 2016 Elsevier Ltd. All rights reserved.
High temperature fatigue behavior of a SiC/Ti-24Al-11Nb composite

NASA Technical Reports Server (NTRS)

Bartolotta, P. A.; Brindley, P. K.

1990-01-01

A series of tension-tension strain- and load-controlled tests were conducted on unidirectional SiC/Ti-24Al-11Nb (at percent) composites at 425 and 815 C. Several regimes of damage were identified using Talrega's concept of fatigue life diagrams. Issues of test technique, test control mode, and definition of failure were also addressed.
Damage accumulation in titanium matrix composites under generic hypersonic vehicle flight simulation and sustained loads

DOE Office of Scientific and Technical Information (OSTI.GOV)

Johnson, W.S.; Mirdamadi, M.; Bakuckas, J.G. Jr.

1996-12-31

Titanium matrix composites (TMC), such as Ti-15V-3Cr-3Al-3Sn (Ti-15-3) reinforced with continuous silicon-carbide fibers (SCS-6), are being evaluated for use in hypersonic vehicles and advanced gas turbine engines where high strength-to-weight and high stiffness-to-weight ratios at elevated temperatures are critical. Such applications expose the composite to mechanical fatigue loading as well as thermally induced cycles. The damage accumulation behavior of a [0/90]2s laminate made of Ti-15V-3Cr-3Al-3Sn (Ti-15-3) reinforced with continuous silicon-carbide fibers (SCS-6) subjected to a simulated generic hypersonic flight profile, portions of the flight profile, and sustained loads was evaluated experimentally. Portions of the flight profile were used separately tomore » isolate combinations of load and time at temperature that influenced the fatigue behavior of the composite. Sustained load tests were also conducted and the results were compared with the fatigue results under the flight profile and its portions. The test results indicated that the fatigue strength of this materials system is considerably reduced by a combination of load and time at temperature.« less
Investigation of tension-compression fatigue behavior of a cross-ply metal matrix composite at room and elevated temperatures. Master's thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Boyum, E.A.

1993-12-01

This research, the first load-controlled tension-compression fatigue testing to be performed on a MMC, extends the existing knowledge of MMC fatigue damage mechanisms to include the tension compression loading condition. To accomplish this, a (0/90)2, SCS-6/Ti-15-3 laminate was subjected to tension-tension fatigue at room temperature, and tension-compression fatigue at both room temperature and 427 deg C. Stress and strain data was taken to evaluate the macro-mechanic behavior of the material. Microscopy and fractography were performed to characterize the damage on a micro-mechanic level. On a maximum applied stress basis, the room temperature tension-tension specimens had longer fatigue lives than themore » room temperature tension-compression specimens. The room and high temperature tension-compression fatigue lives were nearly identical in the fiber-dominated high stress region of the SN curve. However, the increased ductility and diffused plasticity of the titanium matrix at 427 deg C delayed the onset and severity of matrix cracking, and thus increased the elevated temperature fatigue lives in the matrix dominated region of the SN curve. In all cases, matrix damage initiated at reaction zone cracks which nucleated both matrix plasticity and matrix cracking. Metal matrix composite, Elevated temperature, Fatigue testing, Compression, Fully-reversed, Titanium, Silicon carbide.« less
Strength gradient enhances fatigue resistance of steels

NASA Astrophysics Data System (ADS)

Ma, Zhiwei; Liu, Jiabin; Wang, Gang; Wang, Hongtao; Wei, Yujie; Gao, Huajian

2016-02-01

Steels are heavily used in infrastructure and the transportation industry, and enhancing their fatigue resistance is a major challenge in materials engineering. In this study, by introducing a gradient microstructure into 304 austenitic steel, which is one of the most widely used types of stainless steel, we show that a strength gradient substantially enhances the fatigue life of the material. Pre-notched samples with negative strength gradients in front of the notch’s tip endure many more fatigue cycles than do samples with positive strength gradients during the crack initiation stage, and samples with either type of gradient perform better than do gradient-free samples with the same average yield strength. However, as a crack grows, samples with positive strength gradients exhibit better resistance to fatigue crack propagation than do samples with negative gradients or no gradient. This study demonstrates a simple and promising strategy for using gradient structures to enhance the fatigue resistance of materials and complements related studies of strength and ductility.
Strength gradient enhances fatigue resistance of steels

PubMed Central

Ma, Zhiwei; Liu, Jiabin; Wang, Gang; Wang, Hongtao; Wei, Yujie; Gao, Huajian

2016-01-01

Steels are heavily used in infrastructure and the transportation industry, and enhancing their fatigue resistance is a major challenge in materials engineering. In this study, by introducing a gradient microstructure into 304 austenitic steel, which is one of the most widely used types of stainless steel, we show that a strength gradient substantially enhances the fatigue life of the material. Pre-notched samples with negative strength gradients in front of the notch’s tip endure many more fatigue cycles than do samples with positive strength gradients during the crack initiation stage, and samples with either type of gradient perform better than do gradient-free samples with the same average yield strength. However, as a crack grows, samples with positive strength gradients exhibit better resistance to fatigue crack propagation than do samples with negative gradients or no gradient. This study demonstrates a simple and promising strategy for using gradient structures to enhance the fatigue resistance of materials and complements related studies of strength and ductility. PMID:26907708
Room Temperature and Elevated Temperature Composite Sandwich Joint Testing

NASA Technical Reports Server (NTRS)

Walker, Sandra P.

1998-01-01

Testing of composite sandwich joint elements has been completed to verify the strength capacity of joints designed to carry specified running loads representative of a high speed civil transport wing. Static tension testing at both room and an elevated temperature of 350 F and fatigue testing at room temperature were conducted to determine strength capacity, fatigue life, and failure modes. Static tension test results yielded failure loads above the design loads for the room temperature tests, confirming the ability of the joint concepts tested to carry their design loads. However, strength reductions as large as 30% were observed at the elevated test temperature, where all failure loads were below the room temperature design loads for the specific joint designs tested. Fatigue testing resulted in lower than predicted fatigue lives.
Design for cyclic loading endurance of composites

NASA Technical Reports Server (NTRS)

Shiao, Michael C.; Murthy, Pappu L. N.; Chamis, Christos C.; Liaw, Leslie D. G.

1993-01-01

The application of the computer code IPACS (Integrated Probabilistic Assessment of Composite Structures) to aircraft wing type structures is described. The code performs a complete probabilistic analysis for composites taking into account the uncertainties in geometry, boundary conditions, material properties, laminate lay-ups, and loads. Results of the analysis are presented in terms of cumulative distribution functions (CDF) and probability density function (PDF) of the fatigue life of a wing type composite structure under different hygrothermal environments subjected to the random pressure. The sensitivity of the fatigue life to a number of critical structural/material variables is also computed from the analysis.
Thin-metal lined PRD 49-III composite vessels. [evaluation of pressure vessels for burst strength and fatigue performance

NASA Technical Reports Server (NTRS)

Hoggatt, J. T.

1974-01-01

Filament wound pressure vessels of various configurations were evaluated for burst strength and fatigue performance. The dimensions and characteristics of the vessels are described. The types of tests conducted are explained. It was determined that all vessels leaked in a relatively few cycles (20 to 60 cycles) with failure occurring in all cases in the metallic liner. The thin liner would de-bond from the composite and buckling took place during depressurization. No composite failures or indications of impeding composite failures were obtained in the metal-lined vessels.
Quantifying voids effecting delamination in carbon/epoxy composites: static and fatigue fracture behavior

NASA Astrophysics Data System (ADS)

Hakim, I.; May, D.; Abo Ras, M.; Meyendorf, N.; Donaldson, S.

2016-04-01

On the present work, samples of carbon fiber/epoxy composites with different void levels were fabricated using hand layup vacuum bagging process by varying the pressure. Thermal nondestructive methods: thermal conductivity measurement, pulse thermography, pulse phase thermography and lock-in-thermography, and mechanical testing: modes I and II interlaminar fracture toughness were conducted. Comparing the parameters resulted from the thermal nondestructive testing revealed that voids lead to reductions in thermal properties in all directions of composites. The results of mode I and mode II interlaminar fracture toughness showed that voids lead to reductions in interlaminar fracture toughness. The parameters resulted from thermal nondestructive testing were correlated to the results of mode I and mode II interlaminar fracture toughness and voids were quantified.

A Mechanistic Study of Failure of Concrete Subjected to Cyclic Thermal Loads

DTIC Science & Technology

1991-07-01

After Cooling due to Shrinkage ............... 27 ix LIST OF TABLES TABLE I. Cleavage Strength of Composite Samples Prepared with Different Kinds of...microcracking - a possible fatigue mechanism - due to heating and cooling . Therefore the first part of the experimental program concentrated on obtaining...propagation of cracks (7). For temperatures up to 662F cracking happens during the cooling phase, for temperatures above 842F the majority of cracking takes
Design procedures for fiber composite structural components - Rods, beams, and beam columns

NASA Technical Reports Server (NTRS)

Chamis, C. C.

1984-01-01

Step by step procedures are described which are used to design structural components (rods, columns, and beam columns) subjected to steady state mechanical loads and hydrothermal environments. Illustrative examples are presented for structural components designed for static tensile and compressive loads, and fatigue as well as for moisture and temperature effects. Each example is set up as a sample design illustrating the detailed steps that are used to design similar components.
Design procedures for fiber composite structural components: Rods, columns and beam columns

NASA Technical Reports Server (NTRS)

Chamis, C. C.

1983-01-01

Step by step procedures are described which are used to design structural components (rods, columns, and beam columns) subjected to steady state mechanical loads and hydrothermal environments. Illustrative examples are presented for structural components designed for static tensile and compressive loads, and fatigue as well as for moisture and temperature effects. Each example is set up as a sample design illustrating the detailed steps that are used to design similar components.
Fatigue damage evaluation of short fiber CFRP based on phase information of thermoelastic temperature change

NASA Astrophysics Data System (ADS)

Sakagami, Takahide; Shiozawa, Daiki; Nakamura, Yu; Nonaka, Shinichi; Hamada, Kenichi

2017-05-01

Carbon fiber-reinforced plastic (CFRP) is widely used for structural members of transportation vehicles such as automobile, aircraft or spacecraft, utilizing its excellent specific strength and specific rigidity in contrast with the metal. Short carbon fiber composite materials are receiving a lot of attentions because of their excellent moldability and productivity, however they show complicated behaviors in fatigue fracture due to the random fibers orientation. In this study, thermoelastic stress analysis (TSA) using an infrared thermography was applied to the evaluation of fatigue damage in short carbon fiber composites. The distributions of the thermoelastic temperature change was measured during the fatigue test, as well as the phase difference between the thermoelastic temperature change and applied loading signal. Evolution of fatigue damages was detected from distributions of thermoelastic temperature change according to the thermoelastic damage analysis (TDA) procedure. It was also found that fatigue damage evolution was clearly detected than ever by the newly developed thermoelastic phase damage analysis (TPDA) in which damaged area was emphasized in the differential phase delay images utilizing the nature that carbon fiber show opposite phase thermoelastic temperature change.
Response of resin transfer molded (RTM) composites under reversed cyclic loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Mahfuz, H.; Haque, A.; Yu, D.

1996-01-01

Compressive behavior and the tension-compression fatigue response of resin transfer molded IM7 PW/PR 500 composite laminate with a circular notch have been studied. Fatigue damage characteristics have been investigated through the changes in the laminate strength and stiffness by gradually incrementing the fatigue cycles at a preselected load level. Progressive damage in the surface of the laminate during fatigue has been investigated using cellulose replicas. Failure mechanisms during static and cyclic tests have been identified and presented in detail. Extensive debonding of filaments and complete fiber bundle fracture accompanied by delamination were found to be responsible for fatigue failures, whilemore » fiber buckling, partial fiber fracture and delamination were characterized as the failure modes during static tests. Weibull analysis of the static, cyclic and residual tests have been performed and described in detail. Fractured as well as untested specimens were C-scanned, and the progressive damage growth during fatigue is presented. Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) for the fractured specimen were also performed and the analysis of the failure behavior is presented.« less
Hierarchical Simulation of Hot Composite Structures

NASA Technical Reports Server (NTRS)

Chamis, C. C.; Murthy, P. L. N.; Singhal, S. N.

1993-01-01

Computational procedures are described to simulate the thermal and mechanical behavior of high temperature metal matrix composites (HT-MMC) in the following three broad areas: (1) Behavior of HT-MMC's from micromechanics to laminate via Metal Matrix Composite Analyzer (METCAN), (2) tailoring of HT-MMC behavior for optimum specific performance via Metal Matrix Laminate Tailoring (MMLT), and (3) HT-MMC structural response for hot structural components via High Temperature Composite Analyzer (HITCAN). Representative results from each area are presented to illustrate the effectiveness of computational simulation procedures. The sample case results show that METCAN can be used to simulate material behavior such as strength, stress-strain response, and cyclic life in HTMMC's; MMLT can be used to tailor the fabrication process for optimum performance such as that for in-service load carrying capacity of HT-MMC's; and HITCAN can be used to evaluate static fracture and fatigue life of hot pressurized metal matrix composite rings.
Accelerated Insertion of Materials - Composites

DTIC Science & Technology

2001-08-28

Details • Damage Tolerance • Repair • Validation of Analysis Methodology • Fatigue • Static • Acoustic • Configuration Details • Damage Tolerance...Sensitivity – Fatigue – Adhesion – Damage Tolerance – All critical modes and environments Products: Material Specifications, B-Basis Design Allowables...Demonstrate damage tolerance AIM-C DARPA DARPA Workshop, Annapolis, August 27-28, 2001 Requalification of Polymer / Composite Parts • Material Changes – Raw
Fatigue Behavior of an Advanced SiC/SiC Composite with an Oxidation Inhibited Matrix at 1200 deg C in Air and in Steam

DTIC Science & Technology

2010-03-01

eight-harness-satin (8HS) weave plies. Tensile stress -strain behavior and tensile properties were evaluated at 1200˚C. Tension-tension fatigue tests...ratio of minimum stress to maximum stress of R = 0.05, with maximum stresses ranging from 100 to 140 MPa in air and in steam. Fatigue run-out was...Hz, the presence of steam appeared to have little influence on the fatigue resistance for the fatigue stress levels < 140 MPa. The presence of steam
Effect of solution treatment on the fatigue behavior of an as-forged Mg-Zn-Y-Zr alloy

NASA Astrophysics Data System (ADS)

Wang, S. D.; Xu, D. K.; Wang, B. J.; Han, E. H.; Dong, C.

2016-04-01

Through investigating and comparing the fatigue behavior of an as-forged Mg-6.7Zn-1.3Y-0.6Zr (wt.%) alloy before and after solid solution treatment (T4) in laboratory air, the effect of T4 treatment on fatigue crack initiation was disclosed. S-N curves illustrated that the fatigue strength of as-forged samples was 110 MPa, whereas the fatigue strength of T4 samples was only 80 MPa. Observations to fracture surfaces demonstrated that for as-forged samples, fatigue crack initiation sites were covered with a layer of oxide film. However, due to the coarse grain structure and the dissolution of MgZn2 precipitates, the activation and accumulation of {10-12} twins in T4 samples were much easier, resulting in the preferential fatigue crack initiation at cracked twin boundaries (TBs). Surface characterization demonstrated that TB cracking was mainly ascribed to the incompatible plastic deformation in the twinned area and nearby α-Mg matrix.
Phase-contrast x-ray imaging of microstructure and fatigue-crack propagation in single-crystal nickel-base superalloys

NASA Astrophysics Data System (ADS)

Husseini, Naji Sami

Single-crystal nickel-base superalloys are ubiquitous in demanding turbine-blade applications, and they owe their remarkable resilience to their dendritic, hierarchical microstructure and complex composition. During normal operations, they endure rapid low-stress vibrations that may initiate fatigue cracks. This failure mode in the very high-cycle regime is poorly understood, in part due to inadequate testing and diagnostic equipment. Phase-contrast imaging with coherent synchrotron x rays, however, is an emergent technique ideally suited for dynamic processes such as crack initiation and propagation. A specially designed portable ultrasonic-fatigue apparatus, coupled with x-ray radiography, allows real-time, in situ imaging while simulating service conditions. Three contrast mechanisms - absorption, diffraction, and phase contrast - span the immense breadth of microstructural features in superalloys. Absorption contrast is sensitive to composition and crack displacements, and diffraction contrast illuminates dislocation aggregates and crystallographic misorientations. Phase contrast enhances electron-density gradients and is particularly useful for fatigue-crack studies, sensitive to internal crack tips and openings less than one micrometer. Superalloy samples were imaged without external stresses to study microstructure and mosaicity. Maps of rhenium and tungsten concentrations revealed strong segregation to the center of dendrites, as manifested by absorption contrast. Though nominally single crystals, dendrites were misoriented from the bulk by a few degrees, as revealed by diffraction contrast. For dynamic studies of cyclic fatigue, superalloys were mounted in the portable ultrasonic-fatigue apparatus, subjected to a mean tensile stress of ˜50-150 MPa, and cycled in tension to initiate and propagate fatigue cracks. Radiographs were recorded every thousand cycles over the multimillion-cycle lifetime to measure micron-scale crack growth. Crack openings were very small, as determined by absorption and phase contrast, and suggested multiple fracture modes for propagation along {111} planes at room temperature, which was verified by finite element analysis. With increasing temperature, cracks became Mode I (perpendicular to the loading axis) in character and more sensitive to the microstructure. Advancing plastic zones ahead of crack tips altered the crystallographic quality, from which diffraction contrast anticipated initiation and propagation. These studies demonstrate the extreme sensitivity of x-ray radiography for detailed studies of superalloys and crack growth processes.
Thermal shock behavior of W-ZrC/Sc2O3 composites under two different transient events by electron and laser irradiation

NASA Astrophysics Data System (ADS)

Chen, Hong-Yu; Luo, Lai-Ma; Zan, Xiang; Xu, Qiu; Tokunaga, Kazutoshi; Liu, Jia-Qin; Zhu, Xiao-Yong; Cheng, Ji-Gui; Wu, Yu-Cheng

2018-02-01

The transient thermal shock behaviors of W-ZrC/Sc2O3 composites with different ZrC contents were evaluated using transient thermal shock test by electron and laser beams. The effects of different ZrC doping contents on the surface morphology and thermal shock resistance of W-ZrC/Sc2O3 composites were then investigated. Similarity and difference between effects of electron and laser beam transient heat loading were also discussed in this study. Repeated heat loading resulted in thermal fatigue of the irradiated W-ZrC/Sc2O3 samples by thermal stress, leading to the rough surface morphologies with cracks. After different transient thermal tests, significant surface roughening, cracks, surface melting, and droplet ejection occurred. W-2vol.%Sc2O3 sample has superior thermal properties and greater resistance to surface modifications under transient thermal shock, and with the increasing ZrC content in W alloys, thermal shock resistance of W-Zr/Sc2O3 sample tends to be unsatisfied.
A population-based study of associations between current posttraumatic stress symptoms and current fatigue.

PubMed

Lerdal, Anners; Lee, Kathryn A; Rokne, Berit; Knudsen, Øistein; Wahl, Astrid K; Dahl, Alv A

2010-10-01

This study explores current experience with posttraumatic stress disorder (PTSD) symptoms and other variables (sociodemographic, mental distress, somatic morbidity, self-rated health, and quality of life [QoL]) in relation to fatigue. A representative sample of the Norwegian population (N = 3,944) was invited to participate in a mailed survey, and 1,857 (47%) returned valid responses on the questionnaire that included the Fatigue Severity Scale and the Posttraumatic Symptom Scale-10. Posttraumatic stress disorder symptoms showed a strong association with fatigue in univariate (β = .41) and multivariate analyses (β = .33). Associations between psychosocial health variables, QoL, and fatigue were confirmed. However, PTSD symptoms showed the strongest association with fatigue in the analyses. Findings need to be replicated in other population samples and in clinical samples with PTSD and fatigue.
A Review on Strengthening Steel Beams Using FRP under Fatigue

PubMed Central

Jumaat, Mohd Zamin; Ramli Sulong, N. H.

2014-01-01

In recent decades, the application of fibre-reinforced polymer (FRP) composites for strengthening structural elements has become an efficient option to meet the increased cyclic loads or repair due to corrosion or fatigue cracking. Hence, the objective of this study is to explore the existing FRP reinforcing techniques to care for fatigue damaged structural steel elements. This study covers the surface treatment techniques, adhesive curing, and support conditions under cyclic loading including fatigue performance, crack propagation, and failure modes with finite element (FE) simulation of the steel bridge girders and structural elements. FRP strengthening composites delay initial cracking, reduce the crack growth rate, extend the fatigue life, and decrease the stiffness decay with residual deflection. Prestressed carbon fibre-reinforced polymer (CFRP) is the best strengthening option. End anchorage prevents debonding of the CRRP strips at the beam ends by reducing the local interfacial shear and peel stresses. Hybrid-joint, nanoadhesive, and carbon-flex can also be attractive for strengthening systems. PMID:25243221
Simplification of Fatigue Test Requirements for Damage Tolerance of Composite Interstage Launch Vehicle Hardware

NASA Technical Reports Server (NTRS)

Nettles, A. T.; Hodge, A. J.; Jackson, J. R.

2010-01-01

The issue of fatigue loading of structures composed of composite materials is considered in a requirements document that is currently in place for manned launch vehicles. By taking into account the short life of these parts, coupled with design considerations, it is demonstrated that the necessary coupon level fatigue data collapse to a static case. Data from a literature review of past studies that examined compressive fatigue loading after impact and data generated from this experimental study are presented to support this finding. Damage growth, in the form of infrared thermography, was difficult to detect due to rapid degradation of compressive properties once damage growth initiated. Unrealistically high fatigue amplitudes were needed to fail 5 of 15 specimens before 10,000 cycles were reached. Since a typical vehicle structure, such as the Ares I interstage, only experiences a few cycles near limit load, it is concluded that static compression after impact (CAI) strength data will suffice for most launch vehicle structures.
Fatigue degradation in compressively loaded composite laminates. [graphite-epoxy composites

NASA Technical Reports Server (NTRS)

Ramkumar, R. L.

1981-01-01

The effect of imbedded delaminations on the compression fatigue behavior of quasi-isotropic, T300/5208, graphite/epoxy laminates was investigated. Teflon imbedments were introduced during panel layup to create delaminations. Static and constant amplitude (R=10, omega = 10 Hz) fatigue tests were conducted. S-N data and half life residual strength data were obtained. During static compression loading, the maximum deflection of the buckled delaminated region was recorded. Under compression fatigue, growth of the imbedded delamination was identified as the predominant failure mode in most of the test cases. Specimens that exhibited others failures had a single low stiffness ply above the Teflon imbedment. Delamination growth during fatigue was monitored using DIB enhanced radiography. In specimens with buried delaminations, the dye penetrant (DIB) was introduced into the delaminated region through a minute laser drilled hole, using a hypodermic needle. A low kV, microfocus, X-ray unit was mounted near the test equipment to efficiently record the cyclic growth of buried delaminations on Polaroid film.
A review on strengthening steel beams using FRP under fatigue.

PubMed

Kamruzzaman, Mohamed; Jumaat, Mohd Zamin; Sulong, N H Ramli; Islam, A B M Saiful

2014-01-01

In recent decades, the application of fibre-reinforced polymer (FRP) composites for strengthening structural elements has become an efficient option to meet the increased cyclic loads or repair due to corrosion or fatigue cracking. Hence, the objective of this study is to explore the existing FRP reinforcing techniques to care for fatigue damaged structural steel elements. This study covers the surface treatment techniques, adhesive curing, and support conditions under cyclic loading including fatigue performance, crack propagation, and failure modes with finite element (FE) simulation of the steel bridge girders and structural elements. FRP strengthening composites delay initial cracking, reduce the crack growth rate, extend the fatigue life, and decrease the stiffness decay with residual deflection. Prestressed carbon fibre-reinforced polymer (CFRP) is the best strengthening option. End anchorage prevents debonding of the CRRP strips at the beam ends by reducing the local interfacial shear and peel stresses. Hybrid-joint, nanoadhesive, and carbon-flex can also be attractive for strengthening systems.
An investigation of the effects of interfacial microstructure on the fatigue behavior of a four-ply [75]{sub 4} continuous silicon carbide (SCS-6) fiber-reinforced titanium matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jin, O.; Li, Y.; Rabeeh, B.M.

1997-12-01

The effects of interfacial microstructure/thickness on the strength and fatigue behavior of a model four-ply [75]{sub 4} Ti-15V-3Al-3Cr-3Sn/SiC (SCS-6) composite are examined in this article. Interfacial microstructure was controlled by annealing at 815 C for 10, 50, or 100 hours. The reaction layer and coating thickness were observed to increase with increasing annealing duration. Damage initiation/propagation mechanisms were examined in as-received material and composites annealed at 815 C for 10 and 100 hours. Fatigue behavior was observed to be dependent upon the stress amplitude. At high stress amplitudes, the failure was dominated by overload phenomena. However, at all stress levels,more » fatigue crack initiation occurred by early debonding and matrix deformation by stress-induced precipitation. This was followed by matrix crack growth and fiber fracture prior to the onset of catastrophic failure. Matrix shear failure modes were also observed on the fracture surfaces in addition to fatigue striations in the matrix. Correlations were also established between the observed damage modes and acoustic emission signals that were detected under monotonic and cyclic loading conditions.« less
Improved cognitive functioning in obese adolescents after a 30-week inpatient weight loss program.

PubMed

Vantieghem, Stijn; Bautmans, Ivan; Guchtenaere, Ann De; Tanghe, Ann; Provyn, Steven

2018-06-15

Studies linked obesity with a large number of medical conditions including decreased cognitive functioning. The relation between BMI and cognition was proven in adults, but in adolescents the results are conflicting. Further, limited data are available on the impact of weight loss on cognition. This study analyzed the impact of a 30-week lasting weight loss program on cognition and determined the impact of changes in body composition and self-perceived fatigue on changes in cognition. Sixty-two obese adolescents were evaluated at baseline and after 30 weeks. Stroop test (ST; selective attention), Continuous Performance Test (CPT; sustained attention) and Ray Auditory verbal learning test (RAVLT; short-term memory) were assessed. Additionally, body composition parameters and fatigue (MFI-20) were evaluated. Improved reaction times were found for ST and CPT after the intervention, but were independent for reductions in BMI, fat mass, fat%, and fatigue. Short memory also improved with decreased fatigue as an influencing parameter. Accuracy of ST and CPT showed no significant changes. A 30-week lasting inpatient weight loss program improved selective attention, sustained attention, and short-term memory. Changes in body composition did not explain the improvements in cognitive functioning. Decreased fatigue resulted in improved aspects of cognition.
Surface integrity and fatigue behaviour of electric discharged machined and milled austenitic stainless steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lundberg, Mattias, E-mail: mattias.lundberg@liu.se

Machining of austenitic stainless steels can result in different surface integrities and different machining process parameters will have a great impact on the component fatigue life. Understanding how machining processes affect the cyclic behaviour and microstructure are of outmost importance in order to improve existing and new life estimation models. Milling and electrical discharge machining (EDM) have been used to manufacture rectangular four-point bend fatigue test samples; subjected to high cycle fatigue. Before fatigue testing, surface integrity characterisation of the two surface conditions was conducted using scanning electron microscopy, surface roughness, residual stress profiles, and hardness profiles. Differences in cyclicmore » behaviour were observed between the two surface conditions by the fatigue testing. The milled samples exhibited a fatigue limit. EDM samples did not show the same behaviour due to ratcheting. Recrystallized nano sized grains were identified at the severely plastically deformed surface of the milled samples. Large amounts of bent mechanical twins were observed ~ 5 μm below the surface. Grain shearing and subsequent grain rotation from milling bent the mechanical twins. EDM samples showed much less plastic deformation at the surface. Surface tensile residual stresses of ~ 500 MPa and ~ 200 MPa for the milled and EDM samples respectively were measured. - Highlights: •Milled samples exhibit fatigue behaviour, but not EDM samples. •Four-point bending is not suitable for materials exhibiting pronounced ratcheting. •LAGB density can be used to quantitatively measure plastic deformation. •Grain shearing and rotation result in bent mechanical twins. •Nano sized grains evolve due to the heat of the operation.« less
Monitoring fatigue damage in carbon fiber composites using an acoustic impact technique

DOE Office of Scientific and Technical Information (OSTI.GOV)

Haque, A.; Raju, P.K.

1998-06-01

The acoustic impact technique (AIT) of nondestructive testing (NDT) has been used to identify the damage that results from the compressive and tension-compression cycle loading around a circular notch of quasiisotropic carbon-fiber composites. This method involves applying a low velocity impact to the test specimen and evaluating the resulting localized acoustic response. Results indicate that AIT can be applied for identification of both compressive and fatigue damage in composite laminates. The gross area of compressive and fatigue damage is detected through an increase in the pulse width, and a decrease in the amplitude, of the force-time signal. The response obtainedmore » in AIT is sensitive to the frequency of the impactor and the amplitude of the impact force and requires careful monitoring of these values to achieve repeatability of results.« less

Immediate versus one-month wet storage fatigue of restorative materials.

PubMed

Gladys, S; Braem, M; Van Meerbeek, B; Lambrechts, P; Vanherle, G

1998-03-01

Immediate finishing is a highly desirable property of restorative materials. In general, the resin composites, the polyacid-modified resin composites and resin-modified glass-ionomers are finished immediately after light-curing. For the conventional glass-ionomers a waiting period of 24 h is recommended. Therefore, the objective of this study was to investigate whether immediate finishing and application of cyclic loading under water spray on resin-modified glass-ionomers, a conventional glass-ionomer, a polyacid-modified resin composite and a resin composite are reflected in their Young's modulus and fatigue resistance after 1-month wet storage compared with a control group that could mature untroubled for 1 month. From this study, it could be concluded that there is a material-dependent response on immediate finishing. For the conventional glass-ionomer, the waiting period of 24 h is highly advisable. The resin composite suffered more than the other test materials. A second statement is that one must be cautious by the extrapolation of findings obtained on quasi static tests (Young's modulus) towards dynamic properties (flexural fatigue limit).
Fatigue Life Prediction of Fiber-Reinforced Ceramic-Matrix Composites with Different Fiber Preforms at Room and Elevated Temperatures

PubMed Central

Li, Longbiao

2016-01-01

In this paper, the fatigue life of fiber-reinforced ceramic-matrix composites (CMCs) with different fiber preforms, i.e., unidirectional, cross-ply, 2D (two dimensional), 2.5D and 3D CMCs at room and elevated temperatures in air and oxidative environments, has been predicted using the micromechanics approach. An effective coefficient of the fiber volume fraction along the loading direction (ECFL) was introduced to describe the fiber architecture of preforms. The statistical matrix multicracking model and fracture mechanics interface debonding criterion were used to determine the matrix crack spacing and interface debonded length. Under cyclic fatigue loading, the fiber broken fraction was determined by combining the interface wear model and fiber statistical failure model at room temperature, and interface/fiber oxidation model, interface wear model and fiber statistical failure model at elevated temperatures, based on the assumption that the fiber strength is subjected to two-parameter Weibull distribution and the load carried by broken and intact fibers satisfies the Global Load Sharing (GLS) criterion. When the broken fiber fraction approaches the critical value, the composites fatigue fracture. PMID:28773332
Fatigue crack growth in unidirectional metal matrix composite

NASA Technical Reports Server (NTRS)

Ghosn, Louis J.; Telesman, Jack; Kantzos, Peter

1990-01-01

The weight function method was used to determine the effective stress intensity factor and the crack opening profile for a fatigue tested composite which exhibited fiber bridging. The bridging mechanism was modeled using two approaches; the crack closure approach and the shear lag approach. The numerically determined stress intensity factor values from both methods were compared and correlated with the experimentally obtained crack growth rates for SiC/Ti-15-3 (0)(sub 8) oriented composites. The near crack tip opening profile was also determined for both methods and compared with the experimentally obtained measurements.
Perception and predictability of travel fatigue after long-haul flights: a retrospective study.

PubMed

Flower, David J C; Irvine, David; Folkard, Simon

2003-02-01

The impact of travel fatigue and jet lag varies between individuals and may significantly affect the ability of some to perform their occupational role following a transmeridian flight. It would be advantageous in an occupational setting to be able to predict prior to travel those who may suffer most. A Traveler Profile Questionnaire was developed to assess the perceived severity of travel fatigue in 100 subjects making transmeridian flights. The questionnaire provided an internally consistent measure of fatigue and confirmed that subjects experienced greater symptoms of travel fatigue following east/west flights when compared with north/south. Easterly travel was rated marginally worse than travel in a westerly direction. The respondents scores as measured by the Circadian Type Inventory (Folkard 1987) and Composite Morningness Questionnaire (Smith 1989) were used to identify whether such tools could be used as indicators of susceptibility to the effects of travel fatigue. After allowing for a gender difference, increased rigidity in sleeping habits as shown by a decrease in the Flexibility/Rigidity score on the Circadian Type Inventory was associated with an increase in the composite 'severity' score for travel fatigue derived from ratings of specific physiological symptoms. The Traveler Profile Questionnaire, while internally consistent was nonetheless insufficient to be used in a predictive capacity to identify those individuals who would suffer most from the effects of travel fatigue.
An overview of elevated temperature damage mechanisms and fatigue behavior of a unidirectional SCS-6/Ti-15-3 composite

NASA Technical Reports Server (NTRS)

Castelli, Michael G.; Gayda, John

1993-01-01

The fatigue behavior of a unidirectionally reinforced titanium matrix composite (TMC), SiC/Ti-15-3, was thoroughly characterized to support life prediction modeling of advanced TMC disks designed for gas turbine engine applications. The results of this coupon-level experimental investigation are reviewed. On a stress basis, the isothermal fatigue behavior of the (0 deg) TMC revealed significant improvements over the unreinforced matrix. In contrast, the (90 deg) TMC exhibited degraded properties and lives for similar comparisons. This was attributed to the weak fiber/matrix interfacial bond. Encasing the (0 deg) TMC with a Ti-15-3 case did not affect isothermal fatigue lives at higher strain levels. However, at lower strain levels, rapid initiation and propagation of large fatigue cracks in the case degraded the fatigue lives. Thermomechanical fatigue (TMF) lives were significantly reduced for the (0 deg) TMC when compared to isothermal lives. At high strains, in-phase TMF produced extremely short lives. This degradation was attributed to fiber overload failures brought about by stress relaxation in the matrix. At low strains, out-of-phase TMF conditions became life limiting. Environment-assisted surface cracking was found to accelerate fatigue failure. This produced extensive matrix damage with minimal fiber damage. For the (90 deg) TMC, TMF conditions did not promote an additional degradation in cyclic life beyond that observed under isothermal conditions.
Modeling Cyclic Fatigue Hysteresis Loops of 2D Woven Ceramic Matrix Composites at Elevated Temperatures in Steam

PubMed Central

Li, Longbiao

2016-01-01

In this paper, the cyclic fatigue hysteresis loops of 2D woven SiC/SiC ceramic matrix composites (CMCs) at elevated temperatures in steam have been investigated. The interface slip between fibers and the matrix existing in matrix cracking modes 3 and 5, in which matrix cracking and interface debonding occurred in longitudinal yarns, is considered as the major reason for hysteresis loops of 2D woven CMCs. The hysteresis loops of 2D SiC/SiC composites corresponding to different peak stresses, test conditions, and loading frequencies have been predicted using the present analysis. The damage parameter, i.e., the proportion of matrix cracking mode 3 in the entire matrix cracking modes of the composite, and the hysteresis dissipated energy increase with increasing fatigue peak stress. With increasing cycle number, the interface shear stress in the longitudinal yarns decreases, leading to transition of interface slip types of matrix cracking modes 3 and 5. PMID:28773544
Fabrication of aluminum-carbon composites

NASA Technical Reports Server (NTRS)

Novak, R. C.

1973-01-01

A screening, optimization, and evaluation program is reported of unidirectional carbon-aluminum composites. During the screening phase both large diameter monofilament and small diameter multifilament reinforcements were utilized to determine optimum precursor tape making and consolidation techniques. Difficulty was encountered in impregnating and consolidating the multifiber reinforcements. Large diameter monofilament reinforcement was found easier to fabricate into composites and was selected to carry into the optimization phase in which the hot pressing parameters were refined and the size of the fabricated panels was scaled up. After process optimization the mechanical properties of the carbon-aluminum composites were characterized in tension, stress-rupture and creep, mechanical fatigue, thermal fatigue, thermal aging, thermal expansion, and impact.
Thermography Inspection for Early Detection of Composite Damage in Structures During Fatigue Loading

NASA Technical Reports Server (NTRS)

Zalameda, Joseph N.; Burke, Eric R.; Parker, F. Raymond; Seebo, Jeffrey P.; Wright, Christopher W.; Bly, James B.

2012-01-01

Advanced composite structures are commonly tested under controlled loading. Understanding the initiation and progression of composite damage under load is critical for validating design concepts and structural analysis tools. Thermal nondestructive evaluation (NDE) is used to detect and characterize damage in composite structures during fatigue loading. A difference image processing algorithm is demonstrated to enhance damage detection and characterization by removing thermal variations not associated with defects. In addition, a one-dimensional multilayered thermal model is used to characterize damage. Lastly, the thermography results are compared to other inspections such as non-immersion ultrasonic inspections and computed tomography X-ray.
Influence of interface ply orientation on fatigue damage of adhesively bonded composite joints

NASA Technical Reports Server (NTRS)

Johnson, W. S.; Mall, S.

1985-01-01

An experimental study of cracked-lap-shear specimens was conducted to determine the influence of adherend stacking sequence on debond initiation and damage growth in a composite-to-composite bonded joint. Specimens consisted of quasi-isotropic graphite/epoxy adherends bonded together with either FM-300 or EC 3445 adhesives. The stacking sequence of the adherends was varied such that 0 deg, 45 deg, or 90 deg plies were present at the adherend-adhesive interfaces. Fatigue damage initiated in the adhesive layer in those specimens with 0 deg nd 45 deg interface plies. Damage initiated in the form of ply cracking in the strap adherend for the specimens with 90 deg interface plies. The fatigue-damage growth was in the form of delamination within the composite adherends for specimens with the 90 deg and 45 deg plies next to the adhesive, while debonding in the adhesive resulted for the specimens with 0 deg plies next to the adhesive. Those joints with the 0 deg and 45 deg plies next to either adhesive has essentially the same fatigue-damage-initiation stress levels. These stress levels were 13 and 71 percent higher, respectively, than those for specimens with 90 deg plies next to the EC 3445 and FM-300 adhesives.
Fatigue resistance of unnotched and post impact(+/- 30 deg/0 deg) 3-D braided composites

NASA Technical Reports Server (NTRS)

Portanova, Marc A.

1994-01-01

The fatigue resistance of a multiaxial braided (3-D) graphite/expoxy composite in both unnotched and post impacted conditions has been evaluated. The material tested is a (+/- 30/0 deg) multiaxial braid constructed from AS4/12K tow graphite fibers and British Petroleum E905L epoxy resin. These materials were braided as dry preforms and the epoxy was added using a resin transfer molding process (RTM). The unnotched and post-impact specimens were tested in compression-compression fatigue at 10 Hz with a stress ratio of R=10. The unnotched tension-tension fatigue specimens were tested at S Hz with a stress ration of R=0.1. Damage initiation and growth was documented through the application of radiography and ultrasonic through transmission (C-scans). Visible inspection of surface and edge damage was also noted to describe the initiation and progression of damage in these materials. The mechanisms leading to damage initiation were established and failure modes were determined. Stiffness and strength degradation were measured as a function of applied cycles. These 3-D braided composite results were compared to strain levels currently used to design primary structure in commercial aircraft composite components made from prepreg tape and autoclave cured.
Influence of interface ply orientation on fatigue damage of adhesively bonded composite joints

NASA Technical Reports Server (NTRS)

Johnson, W. S.; Mall, S.

1986-01-01

An experimental study of cracked-lap-shear specimens was conducted to determine the influence of adherend stacking sequence on debond initiation and damage growth in a composite-to-composite bonded joint. Specimens consisted of quasi-isotropic graphite/epoxy adherends bonded together with either FM-300 or EC 3445 adhesives. The stacking sequence of the adherends was varied such that 0 deg, 45 deg, or 90 deg plies were present at the adherend-adhesive interfaces. Fatigue damage initiated in the adhesive layer in those specimens with 0 deg and 45 deg interface plies. Damaage initiated in the form of ply cracking in the strap adherend for the specimens with 90 deg interface plies. The fatigue-damage growth was in the form of delamination within the composite adherends for specimens with the 90 deg and 45 deg plies next to the adhesive, while debonding in the adhesive resulted for the specimens with 0 deg plies next to the adhesive. Those joints with the 0 deg and 45 deg plies next to either adhesive has essentially the same fatigue-damage-initiation stress levels. These stress levels were 13 and 71 percent higher, respectively, than those for specimens with 90 deg plies next to the EC 3445 and FM-300 adhesives.
Application of the multidimensional fatigue inventory (MFI-20) in cancer patients receiving radiotherapy.

PubMed Central

Smets, E. M.; Garssen, B.; Cull, A.; de Haes, J. C.

1996-01-01

In this paper the psychometric properties of the multidimensional fatigue inventory (MFI-20) are established further in cancer patients. The MFI is a 20-item self-report instrument designed to measure fatigue. It covers the following dimensions: general fatigue, physical fatigue, reduced activity, reduced motivation and mental fatigue. The instrument was used in a Dutch and Scottish sample of cancer patients receiving radiotherapy. The dimensional structure was assessed using confirmatory factor analyses (Lisrel's unweighted least-squares method). The hypothesised five-factor model appeared to fit the data in both samples (adjusted goodness of fit; AGFI: 0.97 and 0.98). Internal consistency of the separate scales was good in both the Dutch and Scottish samples with Cronbach's alpha coefficients ranging from 0.79 to 0.93. Construct validity was assessed by correlating the MFI-20 to activities of daily living, anxiety and depression. Significant relations were assumed. Convergent validity was investigated by correlating the MFI scales with a visual analogue scale measuring fatigue and with a fatigue-scale derived from the Rotterdam Symptom Checklist. Results support the validity of the MFI-20. The highly similar results in the Dutch and Scottish sample suggest that the portrayal of fatigue using the MFI-20 is quite robust. PMID:8546913
Microstructural Influence on Deformation and Fatigue Life of Composites Using the Generalized Method of Cells

NASA Technical Reports Server (NTRS)

Arnold, S. M.; Murthy, P.; Bednarcyk, B. A.; Pineda, E. J.

2015-01-01

A fully coupled deformation and damage approach to modeling the response of composite materials and composite laminates is presented. It is based on the semi--analytical generalized method of cells (GMC) micromechanics model as well as its higher fidelity counterpart, HFGMC, both of which provide closed-form constitutive equations for composite materials as well as the micro scale stress and strain fields in the composite phases. The provided constitutive equations allow GMC and HFGMC to function within a higher scale structural analysis (e.g., finite element analysis or lamination theory) to represent a composite material point, while the availability of the micro fields allow the incorporation of lower scale sub-models to represent local phenomena in the fiber and matrix. Further, GMC's formulation performs averaging when applying certain governing equations such that some degree of microscale field accuracy is surrendered in favor of extreme computational efficiency, rendering the method quite attractive as the centerpiece in a integrated computational material engineering (ICME) structural analysis; whereas HFGMC retains this microscale field accuracy, but at the price of significantly slower computational speed. Herein, the sensitivity of deformation and the fatigue life of graphite/epoxy PMC composites, with both ordered and disordered microstructures, has been investigated using this coupled deformation and damage micromechanics based approach. The local effects of fiber breakage and fatigue damage are included as sub-models that operate on the microscale for the individual composite phases. For analysis of laminates, classical lamination theory is employed as the global or structural scale model, while GMC/HFGMC is embedded to operate on the microscale to simulate the behavior of the composite material within each laminate layer. A key outcome of this study is the statistical influence of microstructure and micromechanics idealization (GMC or HFGMC) on the overall accuracy of unidirectional and laminated composite deformation and fatigue response.
The Effects of Fiber Orientation and Volume Fraction of Fiber on Mechanical Properties of Additively Manufactured Composite Material

NASA Astrophysics Data System (ADS)

Kuchipudi, Suresh Chandra

Additive manufacturing (AM) also known as 3D printing has tremendous advancements in recent days with a vast number of applications in industrial, automotive, architecture, consumer projects, fashion, toys, food, art, etc. Composite materials are widely used in structures with weight as a critical factor especially in aerospace industry. Recently, additive manufacturing technology, a rapidly growing innovative technology, has gained lot of importance in making composite materials. The properties of composite materials depend upon the properties of constituent's matrix and fiber. There is lot of research on effect of fiber orientation on mechanical properties of composite materials made using conventional manufacturing methods. It will be interesting and relevant to study the relationship between the fiber orientation and fiber volume with mechanical properties of additively manufactured composite materials. This thesis work presents experimental investigation of mechanical behavior like tensile strength and fatigue life with variation in fiber orientation and fiber volume fraction of 3D printed composite materials. The aim is to study the best combination of volume fraction of fiber and fiber orientation that has better fatigue strength for additive manufactured composite materials. Using this study, we can decide the type of orientation and volume percent for desired properties. This study also finds the range of fatigue limits of 3d printed composite materials.
Damage Tolerance Enhancement of Carbon Fiber Reinforced Polymer Composites by Nanoreinforcement of Matrix

NASA Astrophysics Data System (ADS)

Fenner, Joel Stewart

Nanocomposites are a relatively new class of materials which incorporate exotic, engineered nanoparticles to achieve superior material properties. Because of their extremely small size and well-ordered structure, many nanoparticles possess properties that exceed those offered by a wide range of other known materials, making them attractive candidates for novel materials engineering development. Their small size is also an impediment to their practical use, as they typically cannot be employed by themselves to realize those properties in large structures. Furthermore, nanoparticles typically possess strong self-affinity, rendering them difficult to disperse uniformly into a composite. However, contemporary research has shown that, if well-dispersed, nanoparticles have great capacity to improve the mechanical properties of composites, especially damage tolerance, in the form of fracture toughness, fatigue life, and impact damage mitigation. This research focuses on the development, manufacturing, and testing of hybrid micro/nanocomposites comprised of woven carbon fibers with a carbon nanotube reinforced epoxy matrix. Material processing consisted of dispersant-and-sonication based methods to disperse nanotubes into the matrix, and a vacuum-assisted wet lay-up process to prepare the hybrid composite laminates. Various damage tolerance properties of the hybrid composite were examined, including static strength, fracture toughness, fatigue life, fatigue crack growth rate, and impact damage behavior, and compared with similarly-processed reference material produced without nanoreinforcement. Significant improvements were obtained in interlaminar shear strength (15%), Mode-I fracture toughness (180%), shear fatigue life (order of magnitude), Mode-I fatigue crack growth rate (factor of 2), and effective impact damage toughness (40%). Observations by optical microscopy, scanning electron microscopy, and ultrasonic imaging showed significant differences in failure behavior and fracture morphology between the two materials, related to the differences in properties. Altogether these results provided a means for proposing an explanation of the mechanism of reinforcement (and damage tolerance enhancement) provided by carbon nanotubes in hybrid composite materials.
Mechanical and electrical performance characterization of partial mock-up of the ITER PF6 coil tail

NASA Astrophysics Data System (ADS)

Zhang, Z.; Song, Y.; Wu, H.; Zhang, M.; Xie, Y.; Hu, B.; Liu, F.; Shen, G.; Wu, W.; Lu, K.; Wei, J.; Bilbao, M.; Peñate, J.; Readman, P.; Sborchia, C.; Valente, P.; Smith, K.

2017-12-01

International Thermonuclear Experimental Reactor (ITER) is a full superconducting coil tokamak. The tail is an important component of Poloidal Field (PF) coil, of which the main functions are to provide the electrical isolation and transfer the longitudinal load from the last turn to the last-but-one turn. The paper focuses on an optimized mechanical structure of PF6 coil tail, which is made up of two main parts. One was welded to the last turn and the other was welded to the last-but-one turn. Both of them were connected by the mechanical coupling. The electrical isolation between the two parts was maintained by a strap made of insulating composite. In addition, as the PF6 coil is operated under the cyclic electromagnetic load during the tokamak operation, the fatigue property of the tail should be assessed and qualified at low temperature. Moreover, taking into consideration the complexity of the insulation winding process which is performed in a confined space, the wrapping process of the insulation needs to be established. Meanwhile, the high voltage (HV) tests of the tail insulation, including the direct current (DC) and alternating current (AC) tests, need to be assessed before and after the fatigue test. In this paper, a fully bonded PF6 coil tail partial mock-up (not including the weld of the tail to the last conductor turn) was designed and manufactured by simulating the actual manufacturing processes. In addition, the fatigue tests on the sample were carried out at 77 K, and the results showed the sample had good and stable fatigue properties at cryogenic temperature. The HV tests before and after the fatigue test, also including the final 30 kV breakdown DC test after the fatigue test, were carried out. The test results satisfied the requirements of ITER and were discussed in depth. Finally, the sample was destructively inspected to validate the integrity of the insulation by mechanical cross sectioning, and no voids and cracks were observed. Therefore it can be verified from the test results that the designed PF6 coil tail has good comprehensive properties, which can be applied to the formal production of the PF6 coil.
Acoustic emission characteristics of copper alloys under low-cycle fatigue conditions

NASA Technical Reports Server (NTRS)

Krampfner, Y.; Kawamoto, A.; Ono, K.; Green, A.

1975-01-01

The acoustic emission (AE) characteristics of pure copper, zirconium-copper, and several copper alloys were determined to develop nondestructive evaluation schemes of thrust chambers through AE techniques. The AE counts rms voltages, frequency spectrum, and amplitude distribution analysis evaluated AE behavior under fatigue loading conditions. The results were interpreted with the evaluation of wave forms, crack propagation characteristics, as well as scanning electron fractographs of fatigue-tested samples. AE signals at the beginning of a fatigue test were produced by a sample of annealed alloys. A sample of zirconium-containing alloys annealed repeatedly after each fatigue loading cycle showed numerous surface cracks during the subsequent fatigue cycle, emitting strong-burst AE signals. Amplitude distribution analysis exhibits responses that are characteristic of certain types of AE signals.
Self-sealing of thermal fatigue and mechanical damage in fiber-reinforced composite materials

NASA Astrophysics Data System (ADS)

Moll, Jericho L.

Fiber reinforced composite tanks provide a promising method of storage for liquid oxygen and hydrogen for aerospace applications. The inherent thermal fatigue of these vessels leads to the formation of microcracks, which allow gas phase leakage across the tank walls. In this dissertation, self-healing functionality is imparted to a structural composite to effectively seal microcracks induced by both mechanical and thermal loading cycles. Two different microencapsulated healing chemistries are investigated in woven glass fiber/epoxy and uni-weave carbon fiber/epoxy composites. Self-healing of mechanically induced damage was first studied in a room temperature cured plain weave E-glass/epoxy composite with encapsulated dicyclopentadiene (DCPD) monomer and wax protected Grubbs' catalyst healing components. A controlled amount of microcracking was introduced through cyclic indentation of opposing surfaces of the composite. The resulting damage zone was proportional to the indentation load. Healing was assessed through the use of a pressure cell apparatus to detect nitrogen flow through the thickness direction of the damaged composite. Successful healing resulted in a perfect seal, with no measurable gas flow. The effect of DCPD microcapsule size (51 microm and 18 microm) and concentration (0--12.2 wt%) on the self-sealing ability was investigated. Composite specimens with 6.5 wt% 51 microm capsules sealed 67% of the time, compared to 13% for the control panels without healing components. A thermally stable, dual microcapsule healing chemistry comprised of silanol terminated poly(dimethyl siloxane) plus a crosslinking agent and a tin catalyst was employed to allow higher composite processing temperatures. The microcapsules were incorporated into a satin weave E-glass fiber/epoxy composite processed at 120°C to yield a glass transition temperature of 127°C. Self-sealing ability after mechanical damage was assessed for different microcapsule sizees (25 microm and 42 microm) and concentrations (0--11 vol%). Incorporating 9 vol% 42 microm capsules or 11 vol% 25 microm capsules into the composite matrix leads to 100% of the samples sealing. The effect of microcapsule concentration on the short beam strength, storage modulus, and glass transition temperature of the composite specimens was also investigated. The thermally stable tin catalyzed poly(dimethyl siloxane) healing chemistry was then integrated into a [0/90]s uniweave carbon fiber/epoxy composite. Thermal cycling (-196°C to 35°C) of these specimens lead to the formation of microcracks, over time, formed a percolating crack network from one side of the composite to the other, resulting in a gas permeable specimen. Crack damage accumulation and sample permeability was monitored with number of cycles for both self-healing and traditional non-healing composites. Crack accumulation occurred at a similar rate for all sample types tested. A 63% increase in lifetime extension was achieved for the self-healing specimens over traditional non-healing composites.
Bending fatigue tests on SiC-Al tapes under alternating stress at room temperature

NASA Technical Reports Server (NTRS)

Herzog, J. A.

1981-01-01

The development of a testing method for fatigue tests on SiC-Al tapes containing a small amount of SiC filaments under alternating stress is reported. The fatigue strength curves resulting for this composite are discussed. They permit an estimate of its behavior under continuous stress and in combination with various other matrices, especially metal matrices.
Reliability improvement of wire bonds subjected to fatigue stresses.

NASA Technical Reports Server (NTRS)

Ravi, K. V.; Philofsky, E. M.

1972-01-01

The failure of wire bonds due to repeated flexure when semiconductor devices are operated in an on-off mode has been investigated. An accelerated fatigue testing apparatus was constructed and the major fatigue variables, aluminum alloy composition, and bonding mechanism, were tested. The data showed Al-1% Mg wires to exhibit superior fatigue characteristics compared to Al-1% Cu or Al-1% Si and ultrasonic bonding to be better than thermocompression bonding for fatigue resistance. Based on these results highly reliable devices were fabricated using Al-1% Mg wire with ultrasonic bonding which withstood 120,000 power cycles with no failures.

Fatigue Damage Evaluation of Short Carbon Fiber Reinforced Plastics Based on Phase Information of Thermoelastic Temperature Change.

PubMed

Shiozawa, Daiki; Sakagami, Takahide; Nakamura, Yu; Nonaka, Shinichi; Hamada, Kenichi

2017-12-06

Carbon fiber-reinforced plastic (CFRP) is widely used for structural members of transportation vehicles such as automobile, aircraft, or spacecraft, utilizing its excellent specific strength and specific rigidity in contrast with the metal. Short carbon fiber composite materials are receiving a lot of attentions because of their excellent moldability and productivity, however they show complicated behaviors in fatigue fracture due to the random fibers orientation. In this study, thermoelastic stress analysis (TSA) using an infrared thermography was applied to evaluate fatigue damage in short carbon fiber composites. The distribution of the thermoelastic temperature change was measured during the fatigue test, as well as the phase difference between the thermoelastic temperature change and applied loading signal. Evolution of fatigue damage was detected from the distribution of thermoelastic temperature change according to the thermoelastic damage analysis (TDA) procedure. It was also found that fatigue damage evolution was more clearly detected than before by the newly developed thermoelastic phase damage analysis (TPDA) in which damaged area was emphasized in the differential phase delay images utilizing the property that carbon fiber shows opposite phase thermoelastic temperature change.
Modeling Delamination in Postbuckled Composite Structures Under Static and Fatigue Loads

NASA Technical Reports Server (NTRS)

Bisagni, Chiara; Brambilla, Pietro; Bavila, Carlos G.

2013-01-01

The ability of the Abaqus progressive Virtual Crack Closure Technique (VCCT) to model delamination in composite structures was investigated for static, postbuckling, and fatigue loads. Preliminary evaluations were performed using simple Double Cantilever Beam (DCB) and Mixed-Mode Bending (MMB) specimens. The nodal release sequences that describe the propagation of the delamination front were investigated. The effect of using a sudden or a gradual nodal release was evaluated by considering meshes aligned with the crack front as well as misaligned meshes. Fatigue simulations were then performed using the Direct Cyclic Fatigue (DCF) algorithm. It was found that in specimens such as the DCB, which are characterized by a nearly linear response and a pure fracture mode, the algorithm correctly predicts the Paris Law rate of propagation. However, the Abaqus DCF algorithm does not consider different fatigue propagation laws in different fracture modes. Finally, skin/stiffener debonding was studied in an aircraft fuselage subcomponent in which debonding occurs deep into post-buckling deformation. VCCT was shown to be a robust tool for estimating the onset propagation. However, difficulties were found with the ability of the current implementation of the Abaqus progressive VCCT to predict delamination propagation within structures subjected to postbuckling deformations or fatigue loads.
Fatigue and environmental behavior of long fiber thermoplastic (LFT) composites

NASA Astrophysics Data System (ADS)

Goel, Ashutosh

In the present work we have characterized the mechanical behavior of long fiber thermoplastic (LFT) composites (21% E-glass fiber/polypropylene) under different conditions. We start by comparing the elastic modulus of LFT predicted by a microstructure-based approach called Object Oriented Finite (OOF) element method, and compare the result with prediction from various models commonly used in the literature and the experimental value. The predictions from the models used currently in the literature did not agree well with the experimental value due to the assumptions inherent in the models. The prediction by OOF was the closest to the experimental value because of the microstructure based approach which takes into account the fiber distribution and orientation during the finite element calculation. This was followed by characterization of fatigue behavior of LFT. Samples tested along longitudinal direction showed a higher fatigue life than the transverse samples because of the preferred orientation of the fibers along the longitudinal direction developed during the processing of LFT by extrusion-compression molding process. Fatigue life decreased with increase in frequency. Hysteretic energy loss and temperature rise were measured; they depended on the stress amplitude as well as the cyclic frequency. LFT composite showed a lower temperature rise compared to neat PP because LFT has higher thermal conductivity than neat PP and thus faster heat dissipation to the surroundings occur. The hysteretic heating also led to decrease in the modulus of LFT as a function of number of cycles. The last part of the work was to study the effect of ultraviolet (UV) exposure on the microstructure and mechanical properties of LFT. Microscopic observations revealed that the damage due to UV was confined only to the surface region in the form of surface cracking and exposure of fibers to the surface in the case of LFT. FTIR and nanoindentation results showed that there was a large increase in the crystallinity and local modulus of the surface layer due to UV exposure. The change in crystallinity and modulus of the surface layer occurs by chemicrystallization wherein the broken, smaller chains due to UV radiation rearrange into more crystalline form. This increase in crystallinity causes increase in the modulus of surface layer and results in cracking of the surface because tensile residual stresses are generated in the surface layer due to the change in crystallinity. The overall modulus of the LFT, however, decreased with increasing UV exposure time due to the formation of surface cracks.
Effect of bipolar electric fatigue on polarization switching in lead-zirconate-titanate ceramics

NASA Astrophysics Data System (ADS)

Zhukov, Sergey; Fedosov, Sergey; Glaum, Julia; Granzow, Torsten; Genenko, Yuri A.; von Seggern, Heinz

2010-07-01

From comparison of experimental results on polarization switching in fresh and electrically fatigued lead-zirconate-titanate (PZT) over a wide range of applied fields and switching times it is concluded that fatigue alters the local field distribution inside the sample due to the generation of discrete defects, such as voids and cracks. Such defects have a strong influence on the overall electric field distribution by their shape and dielectric permittivity. On this hypothesis, a new phenomenological model of polarization switching in fatigued PZT is proposed. The model assumes that the fatigued sample can be composed of different local regions which exhibit different field strengths but otherwise can be considered as unfatigued. Consequently the temporal response of a fatigued sample is assumed to be the superposition of the field-dependent temporal responses of unfatigued samples weighted by their respective volume fraction. A certain part of the volume is excluded from the overall switching process due to the domain pinning even at earlier stages of fatigue, which can be recovered by annealing. Suitability of the proposed model is demonstrated by a good correlation between experimental and calculated data for differently fatigued samples. Plausible cause of the formation of such regions is the generation of defects such as microcracks and the change in electrical properties at imperfections such as pores or voids.
[Epidemiology of fatigue in general practice].

PubMed

Fuhrer, R

1994-11-01

The epidemiology of fatigue is not well known in France, and this study reports on factors associated with fatigue in a sample of 3,784 general practice patients. Prevalence rates according to several definitions of fatigue are presented and factors are examined that have been reported to be associated with fatigue. Although 41.2% of the sample report having experienced symptoms of fatigue for at least three days, only 7.6% declare fatigue as a reason for consulting a doctor. Women report more symptoms of fatigue, but they do not consult more often than men for this reason. Age is strongly correlated with fatigue, but this is found only for men. Socioprofessional category bears no relationship to fatigue as a reason for consultation, however, the diagnosis of fatigue is more often attributed to professionals and upper management than it is to office staff or skilled and unskilled workers. We do find a strong relationship between depressive symptomatology as measured by the Center for Epidemiologic Studies (CES-D) and fatigue; nonetheless, fatigue is neither sensitive nor specific to the diagnosis of depression.
Structural optimization procedure of a composite wind turbine blade for reducing both material cost and blade weight

NASA Astrophysics Data System (ADS)

Hu, Weifei; Park, Dohyun; Choi, DongHoon

2013-12-01

A composite blade structure for a 2 MW horizontal axis wind turbine is optimally designed. Design requirements are simultaneously minimizing material cost and blade weight while satisfying the constraints on stress ratio, tip deflection, fatigue life and laminate layup requirements. The stress ratio and tip deflection under extreme gust loads and the fatigue life under a stochastic normal wind load are evaluated. A blade element wind load model is proposed to explain the wind pressure difference due to blade height change during rotor rotation. For fatigue life evaluation, the stress result of an implicit nonlinear dynamic analysis under a time-varying fluctuating wind is converted to the histograms of mean and amplitude of maximum stress ratio using the rainflow counting algorithm Miner's rule is employed to predict the fatigue life. After integrating and automating the whole analysis procedure an evolutionary algorithm is used to solve the discrete optimization problem.
Towards a Delamination Fatigue Methodology for Composite Materials

NASA Technical Reports Server (NTRS)

OBrien, Thomas K.

2007-01-01

A methodology that accounts for both delaminaton onset and growth in composite structural components is proposed for improved fatigue life prediction to reduce life cycle costs and improve accept/reject criteria for manufacturing flaws. The benefits of using a Delamination Onset Threshold (DOT) approach in combination with a Modified Damage Tolerance (MDT) approach is highlighted. The use of this combined approach to establish accept/reject criteria, requiring less conservative initial manufacturing flaw sizes, is illustrated.
Wavelet Spectral Finite Elements for Wave Propagation in Composite Plates

DTIC Science & Technology

2012-02-21

aerospace structures is increasing rapidly due to several advantages such as lighter weight, fewer joints, improved fatigue life, and higher...breakage, and matrix cracking. These damages often occur below the surface due to fatigue , foreign object impact, etc., and may not be visible. The...ply [0/90]2s. A piezoelectric ( PZT ) actuator (diameter 13.5 mm and thickness 0.22 mm) is affixed onto the composite plate using epoxy. A National
Biaxial tests of flat graphite/epoxy laminates

NASA Technical Reports Server (NTRS)

Liebowitz, H.; Jones, D. L.

1981-01-01

The influence of biaxially applied loads on the strength of composite materials containing holes was analyzed. The analysis was performed through the development of a three dimensional, finite element computer program that is capable of evaluating fiber breakage, delamination, and matrix failure. Realistic failure criteria were established for each of the failure modes, and the influence of biaxial loading on damage accumulation under monotonically increasing loading was examined in detail. Both static and fatigue testing of specially designed biaxial specimens containing central holes were performed. Static tests were performed to obtain an understanding of the influence of biaxial loads on the fracture strength of composite materials and to provide correlation with the analytical predictions. The predicted distributions and types of damage are in reasonable agreement with the experimental results. A number of fatigue tests were performed to determine the influence of cyclic biaxial loads on the fatigue life and residual strength of several composite laminates.
Fatigue Lifetime of Ceramic Matrix Composites at Intermediate Temperature by Acoustic Emission

PubMed Central

Racle, Elie; Godin, Nathalie; Reynaud, Pascal; Fantozzi, Gilbert

2017-01-01

The fatigue behavior of a Ceramic Matrix Composite (CMC) at intermediate temperature under air is investigated. Because of the low density and the high tensile strength of CMC, they offer a good technical solution to design aeronautical structural components. The aim of the present study is to compare the behavior of this composite under static and cyclic loading. Comparison between incremental static and cyclic tests shows that cyclic loading with an amplitude higher than 30% of the ultimate tensile strength has significant effects on damage and material lifetimes. In order to evaluate the remaining lifetime, several damage indicators, mainly based on the investigation of the liberated energy, are introduced. These indicators highlight critical times or characteristic times, allowing an evaluation of the remaining lifetime. A link is established with the characteristic time around 25% of the total test duration and the beginning of the matrix cracking during cyclic fatigue. PMID:28773019
Reviews on factors affecting fatigue behavior of high-Mn steels

NASA Astrophysics Data System (ADS)

Kim, Sangshik; Jeong, Daeho; Sung, Hyokyung

2018-01-01

A variety of factors affect the fatigue behavior of high-Mn steels, which include both extrinsic (i.e., loading type, R ratio, specimen type, surface condition, temperature, and environment) and intrinsic (i.e., chemical composition, grain size, microstructure, stacking fault energy) factors. Very often, the influence of extrinsic factors on the fatigue behavior is even greater than that of intrinsic factors, misleading the interpretation of fatigue data. The metallurgical factors influence the initiation and propagation behaviors of fatigue by altering the characteristics of slip that is prerequisite for fatigue damage accumulation. It is however not easy to separate the effect of each factor since they affect the fatigue behavior of high-Mn steels in complex and synergistic way. In this review, the fatigue data of high-Mn steels are summarized and the factors complicating the interpretation are discussed.
Advanced Environmental Barrier Coating and SA Tyrannohex SiC Composites Integration for Improved Thermomechanical and Environmental Durability

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Halbig, Michael; Singh, Mrityunjay

2018-01-01

The development of 2700 degF capable environmental barrier coating (EBC) systems, particularly, the Rare Earth "Hafnium" Silicon bond coat systems, have significantly improved the temperature capability and environmental stability of SiC/SiC Ceramic Matrix Composite Systems. We have specifically developed the advanced 2700 degF EBC systems, integrating the EBC to the high temperature SA Tyrannohex SiC fiber composites, for comprehensive performance and durability evaluations for potential turbine engine airfoil component applications. The fundamental mechanical properties, environmental stability and thermal gradient cyclic durability performance of the EBC - SA Tyrannohex composites were investigated. The paper will particularly emphasize the high pressure combustion rig recession, cyclic thermal stress resistance and thermomechanical low cycle fatigue testing of uncoated and environmental barrier coated Tyrannohex SiC SA composites in these simulated turbine engine combustion water vapor, thermal gradients, and mechanical loading conditions. We have also investigated high heat flux and flexural fatigue degradation mechanisms, determined the upper limits of operating temperature conditions for the coated SA composite material systems in thermomechanical fatigue conditions. Recent progress has also been made by using the self-healing rare earth-silicon based EBCs, thus enhancing the SA composite hexagonal fiber columns bonding for improved thermomechanical and environmental durability in turbine engine operation environments. More advanced EBC- composite systems based on the new EBC-Fiber Interphases will also be discussed.
Accelerated Fatigue Resistance of Thick CAD/CAM Composite Resin Overlays Bonded with Light- and Dual-polymerizing Luting Resins.

PubMed

Goldberg, Jack; Güth, Jan-Frederik; Magne, Pascal

To evaluate the accelerated fatigue resistance of thick CAD/CAM composite resin overlays luted with three different bonding methods. Forty-five sound human second mandibular molars were organized and distributed into three experimental groups. All teeth were restored with a 5-mm-thick CAD/CAM composite resin overlay. Group A: immediate dentin sealing (IDS) with Optibond FL and luted with light-polymerizing composite (Herculite XRV). Group B: IDS with Optibond FL and luted with dual-polymerizing composite (Nexus 3). Group C: direct luting with Optibond FL and dual-polymerizing composite (Nexus 3). Masticatory forces at a frequency of 5 Hz were simulated using closed-loop servo-hydraulics and forces starting with a load of 200 N for 5000 cycles, followed by steps of 400, 600, 800, 1000, 1200 and 1400 N for a maximum of 30,000 cycles. Each step was applied through a flat steel cylinder at a 45-degree angle under submerged conditions. The fatigue test generated one failure in group A, three failures in group B, and no failures in group C. The survival table analysis for the fatigue test did not demonstrate any significant difference between the groups (p = 0.154). The specimens that survived the fatigue test were set up for the load-to-failure test with a limit of 4600 N. The survival table analysis for the load-to-failure test demonstrates an average failure load of 3495.20 N with survival of four specimens in group A, an average failure load of 4103.60 N with survival of six specimens in group B, and an average failure load of 4075.33 N with survival of nine specimens in group C. Pairwise comparisons revealed no significant differences (p < 0.016 after Bonferroni correction). Within the limitations of this in vitro study, it can be concluded that although the dual-polymerizing luting material seems to provide better results under extreme conditions, light-polymerizing luting composites in combination with IDS are not contraindicated with thick restorations.
Fatigue Behavior of Porous Ti-6Al-4V Made by Laser-Engineered Net Shaping.

PubMed

Razavi, Seyed Mohammad Javad; Bordonaro, Giancarlo G; Ferro, Paolo; Torgersen, Jan; Berto, Filippo

2018-02-12

The fatigue behavior and fracture mechanisms of additively manufactured Ti-6Al-4V specimens are investigated in this study. Three sets of testing samples were fabricated for the assessment of fatigue life. The first batch of samples was built by using Laser-Engineered Net Shaping (LENS) technology, a Direct Energy Deposition (DED) method. Internal voids and defects were induced in a second batch of samples by changing LENS machine processing parameters. Fatigue performance of these samples is compared to the wrought Ti-6Al-4V samples. The effects of machine-induced porosity are assessed on mechanical properties and results are presented in the form of SN curves for the three sets of samples. Fracture mechanisms are examined by using Scanning Electron Microscopy (SEM) to characterize the morphological characteristics of the failure surface. Different fracture surface morphologies are observed for porous and non-porous specimens due to the combination of head write speed and laser power. Formation of defects such as pores, unmelted regions, and gas entrapments affect the failure mechanisms in porous specimens. Non-porous specimens exhibit fatigue properties comparable with that of the wrought specimens, but porous specimens are found to show a tremendous reduced fatigue strength.
Composite structural materials

NASA Technical Reports Server (NTRS)

Ansell, G. S.; Loewy, R. G.; Wiberley, S. E.

1983-01-01

Transverse properties of fiber constituents in composites, fatigue in composite materials, matrix dominated properties of high performance composites, numerical investigation of moisture effects, numerical investigation of the micromechanics of composite fracture, advanced analysis methods, compact lug design, and the RP-1 and RP-2 sailplanes projects are discussed.
Simultaneous life extension and crack monitoring of fatigue-damaged steel members using multifunctional carbon nanotube based composites

NASA Astrophysics Data System (ADS)

Ahmed, Shafique; Schumacher, Thomas; Thostenson, Erik T.; McConnell, Jennifer

2017-04-01

Steel structures including bridges are susceptible to cracking, particularly due to fatigue-sensitive details found in older designs. Therefore, one of the major challenges to keep those steel bridges in service is to rehabilitate existing and potential fatigue damage. There are several conventional approaches to extend the fatigue-life of damaged steel members, e.g., drilling a crack stop-hole to reduce the stress concentration at the crack tip as well as welding and bolting of steel plates or adhesive-bonding of fiber-reinforced polymers (FRP) to reduce the overall stresses. Improvement in material properties of FRP and adhesives make them a viable candidate to apply for extending the fatigue-life of steel members. However, drawbacks include the potential for debonding of the adhesive layer and/or interfaces between adhesive and adherents as well as difficulty in monitoring fatigue crack growth after rehabilitation. In this research, a holistic approach is proposed and evaluated for simultaneous extension of fatigue-life and monitoring by integrating a carbon nanotube (CNT)-based sensing layer with an adhesively-bonded FRP reinforcement. CNT-based sensing layers have a nerve-like electric resistance network, which enables distributed sensing capabilities to monitor stress levels, crack growth, and damage progression. Using laboratory-scale experiments, the simultaneous fatigue-life extension and crack monitoring capability of multifunctional CNT-based composites was evaluated. This paper introduces the fundamental concept of integrated fatigue-rehabilitation and monitoring of steel members, presents a laboratory-scale experiment to demonstrate the feasibility and effectiveness, and discusses challenges for implementation in real structures.
Property Evaluation and Damage Evolution of Environmental Barrier Coatings and Environmental Barrier Coated SiC/SiC Ceramic Matrix Composite Sub-Elements

NASA Technical Reports Server (NTRS)

Zhu, Dongming; Halbig, Michael; Jaskowiak, Martha; Hurst, Janet; Bhatt, Ram; Fox, Dennis S.

2014-01-01

This paper describes recent development of environmental barrier coatings on SiC/SiC ceramic matrix composites. The creep and fatigue behavior at aggressive long-term high temperature conditions have been evaluated and highlighted. Thermal conductivity and high thermal gradient cyclic durability of environmental barrier coatings have been evaluated. The damage accumulation and complex stress-strain behavior environmental barrier coatings on SiCSiC ceramic matrix composite turbine airfoil subelements during the thermal cyclic and fatigue testing of have been also reported.
Fatigue behavior of a cross-ply metal matrix composite at elevated temperature under the strain controlled mode

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sanders, B.P.; Mall, S.; Dennis, L.B.

1997-10-01

A study was conducted to investigate the fatigue behavior of a cross-ply metal matrix composite subjected to fully-reversed, strain-controlled fatigue cycling at elevated temperature. The stress-strain response, maximum and minimum stresses, and modulus during cycling were analyzed to characterize the macro-mechanical behavior. Additionally, microscopy and fractography were conducted to identify damage mechanisms. Damage always initiated in the 90 deg plies, but the governing factor in the fatigue life was damage in the 0 deg plies. The dominant failure mode was fracturing of fibers in the 0 deg plies when the maximum strain was greater than 0.55%, but the dominant failuremore » mode was matrix cracking when the maximum strain was less than 0.55%. Combining the fatigue life data with the macro-mechanical and microscopic observations, a fatigue life diagram was developed and partitioned into three regions. These regions showed relationships between the maximum applied strain and the dominant damage mechanisms. Also, on a strain range basis, the fatigue lives of the specimens tested under the strain-controlled mode in this study were compared with its counterpart under the load-controlled mode of the previous study. It was found that the fatigue lives for these two conditions were the same within the experimental scatter. The MMC tested in this investigation was the Ti-15V-3Cr-3Al-3Sn titanium alloy reinforced with 36 volume percent of silicon carbide fibers (SCS-6).« less
Low cycle fatigue behavior of polycrystalline NiAl at 300 and 1000 K

NASA Technical Reports Server (NTRS)

Lerch, Bradley A.; Noebe, Ronald D.

1993-01-01

The low cycle fatigue behavior of polycrystalline NiAl was determined at 300 and 1000 K - temperatures below and above the brittle- to-ductile transition temperature (BDTT). Fully reversed, plastic strain-controlled fatigue tests were conducted on two differently fabricated alloy samples: hot isostatically pressed (HIP'ed) prealloyed powder and hot extruded castings. HIP'ed powder (HP) samples were tested only at 1000 K, whereas the more ductile cast-and-extruded (C+E) NiAl samples were tested at both 1000 and 300 K. Plastic strain ranges of 0.06 to 0.2 percent were used. The C+E NiAl cyclically hardened until fracture, reaching stress levels approximately 60 percent greater than the ultimate tensile strength of the alloy. Compared on a strain basis, NiAl had a much longer fatigue life than other B2 ordered compounds in which fracture initiated at processing-related defects. These defects controlled fatigue life at 300 K, with fracture occurring rapidly once a critical stress level was reached. At 1000 K, above the BDTT, both the C+E and HP samples cyclically softened during most of the fatigue tests in air and were insensitive to processing defects. The processing method did not have a major effect on fatigue life; the lives of the HP samples were about a factor of three shorter than the C+E NiAl, but this was attributed to the lower stress response of the C+E material. The C+E NiAl underwent dynamic grain growth, whereas the HP material maintained a constant grain size during testing. In both materials, fatigue life was controlled by intergranular cavitation and creep processes, which led to fatigue crack growth that was primarily intergranular in nature. Final fracture by overload was transgranular in nature. Also, HP samples tested in vacuum had a life three times longer than their counterparts tested in air and, in contrast to those tested in air, hardened continuously over half of the sample life, thereby indicating an environmentally assisted fatigue damage mechanism. The C+E samples were tested only in air. At 1000 K, NiAl exhibited a superior fatigue life when compared to most superalloys on a plastic strain basis, but was inferior to most superalloys on a stress basis.
An engineering approach to the prediction of fatigue behavior of unnotched/notched fiber reinforced composite laminates

NASA Technical Reports Server (NTRS)

Kulkarni, S. V.; Mclaughlin, P. V., Jr.

1978-01-01

An engineering approach is proposed for predicting unnotched/notched laminate fatigue behavior from basic lamina fatigue data. The fatigue analysis procedure was used to determine the laminate property (strength/stiffness) degradation as a function of fatigue cycles in uniaxial tension and in plane shear. These properties were then introduced into the failure model for a notched laminate to obtain damage growth, residual strength, and failure mode. The approach is thus essentially a combination of the cumulative damage accumulation (akin to the Miner-Palmgren hypothesis and its derivatives) and the damage growth rate (similar to the fracture mechanics approach) philosophies. An analysis/experiment correlation appears to confirm the basic postulates of material wearout and the predictability of laminate fatigue properties from lamina fatigue data.

Cyclic Fatigue Durability of Uncoated and EBC Coated 3D SiC/SiC Composites Under Thermal Gradient Conditions at 2700F in Air

NASA Technical Reports Server (NTRS)

Smith, Craig; Harder, Bryan; Zhu, Dongming; Bhatt, Ramakrishna; Kalluri, Sreeramesh

2017-01-01

Ceramic matrix composites (CMCs) such as SiC/SiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiC/SiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. Issues associated with laser testing will be discussed, along with initial results for coated and uncoated samples.
Lee Fatigue and Energy Scales: Exploring aspects of validity in a sample of women with HIV using an application of a Rasch model

PubMed Central

Lerdal, Anners; Kottorp, Anders; Gay, Caryl L.; Lee, Kathryn A.

2012-01-01

This study examines the psychometric properties of the Lee Fatigue and Energy Scales (visual analog version) using a Rasch model application. The relationship between fatigue and energy is also described for a convenience sample of 102 women with HIV/AIDS who completed the Lee Fatigue and Energy Scales in the morning and evening. Both scales were assessed for internal scale validity, unidimensionality, and uniform differential item functioning in relation to morning and evening ratings. Analyses confirmed that both the Fatigue and Energy Scales demonstrated evidence of internal scale validity and unidimensionality. Mean fatigue measures were also higher in the evening than in the morning and mean energy measures were higher in the morning than in the evening (both p<0.001), indicating that time of day is an important consideration. Fatigue and energy measures were moderately correlated with each other in the morning but not in the evening. The concepts of energy and fatigue were inversely related, but not polar opposites in this sample. Fatigue and energy may therefore be distinct constructs that should not be used interchangeably, either in measurement or when interpreting outcomes for research or clinical purposes. PMID:22985544
Solution to the problem of the poor cyclic fatigue resistance of bulk metallic glasses

PubMed Central

Launey, Maximilien E.; Hofmann, Douglas C.; Johnson, William L.; Ritchie, Robert O.

2009-01-01

The recent development of metallic glass-matrix composites represents a particular milestone in engineering materials for structural applications owing to their remarkable combination of strength and toughness. However, metallic glasses are highly susceptible to cyclic fatigue damage, and previous attempts to solve this problem have been largely disappointing. Here, we propose and demonstrate a microstructural design strategy to overcome this limitation by matching the microstructural length scales (of the second phase) to mechanical crack-length scales. Specifically, semisolid processing is used to optimize the volume fraction, morphology, and size of second-phase dendrites to confine any initial deformation (shear banding) to the glassy regions separating dendrite arms having length scales of ≈2 μm, i.e., to less than the critical crack size for failure. Confinement of the damage to such interdendritic regions results in enhancement of fatigue lifetimes and increases the fatigue limit by an order of magnitude, making these “designed” composites as resistant to fatigue damage as high-strength steels and aluminum alloys. These design strategies can be universally applied to any other metallic glass systems. PMID:19289820
Behavior of a centrally notched cross-ply and unidirectional ceramic matrix composite in tension-compression fatigue. Master's thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Weidenaar, W.A.

1992-12-01

Centrally notched (hole), cross-ply, ((0/90) sub 2) sub s, and unidirectional, (0) sub 8 laminates of Silicon Carbide fiber-reinforced Aluminosilicate glass, SiC/1723, were fatigue tested under tension-compression loading with a load ratio of -1. Damage accumulated continuously for both lay-ups, leading to eventual failure and a reduced fatigue life. Critical damage in the cross-ply consisted of longitudinal cracks in the 90 deg plies growing and combining with transverse cracks to effectively eliminate the 90 deg plies' load carrying capability and allowing the specimen to buckle. Critical damage in the unidirectional lay-up consisted of longitudinal cracks which initiated at the shearmore » stress concentration points on the hole periphery. Reversed cyclic loading caused continued crack growth at maximum stresses below the tension-tension fatigue limit. The cross-ply lay-up appeared insensitive to the hole, while critical damage in the unidirectional lay-up was dependent on the shear stress concentrations at the hole.... Ceramic matrix composite, Tension-compression fatigue, Notched specimen.« less
Fiber reinforced superalloys for rocket engines

NASA Technical Reports Server (NTRS)

Petrasek, Donald W.; Stephens, Joseph R.

1989-01-01

High pressure turbopumps for advanced reusable liquid propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several fold increase in life and over a 200 C increase in temperature capability over the current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.
Fiber reinforced superalloys for rocket engines

NASA Technical Reports Server (NTRS)

Petrasek, Donald W.; Stephens, Joseph R.

1988-01-01

High-pressure turbopumps for advanced reusable liquid-propellant rocket engines such as that for the Space Shuttle Main Engine (SSME) require turbine blade materials that operate under extreme conditions of temperature, hydrogen environment, high-cycle fatigue loading, thermal fatigue and thermal shock. Such requirements tax the capabilities of current blade materials. Based on projections of properties for tungsten fiber reinforced superalloy (FRS) composites, it was concluded that FRS turbine blades offer the potential of a several-fold increase in life and over a 200C increase in temperature capability over current SSME blade material. FRS composites were evaluated with respect to mechanical property requirements for SSME blade applications. Compared to the current blade material, the thermal shock resistance of FRS materials is excellent, two to nine times better, and their thermal fatigue resistance is equal to or higher than the current blade material. FRS materials had excellent low and high-cycle fatigue strengths, and thermal shock-induced surface microcracks had no influence on their fatigue strength. The material also exhibited negligible embrittlement when exposed to a hydrogen environment.
Surface Irregularity Factor as a Parameter to Evaluate the Fatigue Damage State of CFRP

PubMed Central

Zuluaga-Ramírez, Pablo; Frövel, Malte; Belenguer, Tomás; Salazar, Félix

2015-01-01

This work presents an optical non-contact technique to evaluate the fatigue damage state of CFRP structures measuring the irregularity factor of the surface. This factor includes information about surface topology and can be measured easily on field, by techniques such as optical perfilometers. The surface irregularity factor has been correlated with stiffness degradation, which is a well-accepted parameter for the evaluation of the fatigue damage state of composite materials. Constant amplitude fatigue loads (CAL) and realistic variable amplitude loads (VAL), representative of real in- flight conditions, have been applied to “dog bone” shaped tensile specimens. It has been shown that the measurement of the surface irregularity parameters can be applied to evaluate the damage state of a structure, and that it is independent of the type of fatigue load that has caused the damage. As a result, this measurement technique is applicable for a wide range of inspections of composite material structures, from pressurized tanks with constant amplitude loads, to variable amplitude loaded aeronautical structures such as wings and empennages, up to automotive and other industrial applications. PMID:28793655
Microarc Oxidation Coating Combined with Surface Pore-Sealing Treatment Enhances Corrosion Fatigue Performance of 7075-T7351 Al Alloy in Different Media

PubMed Central

Yang, Hui-Hui; Wang, Xi-Shu; Wang, Ya-Ming; Wang, Yan-Ling; Zhang, Zhi-Hao

2017-01-01

Rotating bending fatigue tests have been performed to evaluate the corrosion fatigue performance and its influence factors of 7075-T7351 Al alloy in different media, namely air and a 5.0 wt % NaCl aqueous solution. All samples were coated by microarc oxidation (MAO) coating technology; some samples were followed by an epoxy resin pore-sealing treatment. Microscopic analyses of the surfaces and fracture cross-sections of samples were carried out. The results reveal that the sample with a MAO coating of 10 μm thickness and pore-sealing treatment by epoxy resin possesses optimal corrosion fatigue performance in the different media. The MAO coating with a pore-sealing treatment significantly improves the corrosion fatigue limit of 7075-T7351 Al alloy. PMID:28772970
Psychometric properties and Dutch norm data of the PedsQL Multidimensional Fatigue Scale for Young Adults.

PubMed

Haverman, Lotte; Limperg, Perrine F; van Oers, Hedy A; van Rossum, Marion A J; Maurice-Stam, Heleen; Grootenhuis, Martha A

2014-12-01

The aim of this study was to assess internal consistency and construct validity (known-groups validity) and to provide Dutch norm data for the Dutch Pediatric Quality of Life Inventory Multidimensional Fatigue Scale for Young Adults ages 18-30 years (PedsQL fatigue_YA). A Dutch sample of 649 young adults completed online a sociodemographic questionnaire and the PedsQL fatigue_YA including three subscales: general fatigue, sleep/rest fatigue and cognitive fatigue (0-100: Higher scores indicate less fatigue symptoms). The PedsQL fatigue_YA showed satisfactory to good internal consistency (Cronbach's alpha = .70-.94), except for one scale (.68). The mean scale scores were 68.23 (SD 19.15) for 'general fatigue,' 67.04 (SD 15.54) for 'sleep/rest fatigue' and 74.62 (SD 19.02) for 'cognitive fatigue.' Men reported significantly higher scores on 'general fatigue' and 'sleep/rest fatigue' than women. The PedsQL fatigue_YA distinguished between healthy young adults and young adults with chronic health conditions, with higher scores on all scales in healthy young adults than in those with a chronic health condition. The results demonstrate good psychometric properties of the PedsQL fatigue_YA in a sample of Dutch young adults. With the current norms available, it is possible to evaluate fatigue in the Netherlands from childhood to adulthood with the PedsQL Multidimensional Fatigue Scale.
Eddy-current testing of fatigue degradation upon contact fatigue loading of gas powder laser clad NiCrBSi-Cr3C2 composite coating

NASA Astrophysics Data System (ADS)

Savrai, R. A.; Makarov, A. V.; Gorkunov, E. S.; Soboleva, N. N.; Kogan, L. Kh.; Malygina, I. Yu.; Osintseva, A. L.; Davydova, N. A.

2017-12-01

The possibilities of the eddy-current method for testing the fatigue degradation under contact loading of gas powder laser clad NiCrBSi-Cr3C2 composite coating with 15 wt.% of Cr3C2 additive have been investigated. It is shown that the eddy-current testing of the fatigue degradation under contact loading of the NiCrBSi-15%Cr3C2 composite coating can be performed at high excitation frequencies 72-120 kHz of the eddy-current transducer. At that, the dependences of the eddy-current instrument readings on the number of loading cycles have both downward and upward branches, with the boundary between the branches being 3×105 cycles in the given loading conditions. This is caused, on the one hand, by cracking, and, on the other hand, by cohesive spalling and compaction of the composite coating, which affect oppositely the material resistivity and, correspondingly, the eddy-current instrument readings. The downward branch can be used to monitor the processes of crack formation and growth, the upward branch - to monitor the degree of cohesive spalling, while taking into account in the testing methodology an ambiguous character of the dependences of the eddy-current instrument readings on the number of loading cycles.
Mechanical behavior and fatigue performance of SMA short fiber reinforced MMC

NASA Astrophysics Data System (ADS)

Al-Matar, Basem Jawad

The mechanical behavior and performance of Shape Memory Alloy (SMA) short fiber NiTi reinforced Al was experimentally investigated for monotonic and fatigue test Al 6061 NiTi-SiC T6 was superior to unreinforced materials as well as to the reinforced Al T4. Taya three-dimensional model was performed on the monotonic tensile test at room temperature. It showed good agreement with experimental results. In order to utilize the compressive criterion for SMA, the NiTi reinforced Al composite was cooled at -10°C and prestrained at 1.2%. Beyond this limit composite suffered from damage. The net enhancement of SMA effect was around 10 MPa on composite yield stress. Results showed that the elastic constant for the composite did not change with loading and unloading suggesting that the inelastic behavior is plasticity. Further investigation on the inelastic behavior model as damage and/or plasticity by evaluating Poisson's ratio during loading was carried out by Adaptive Image Correlation Technique for Full-Field Strain Measurement. Poisson's ratio increased from around 0.33 to 0.5 demonstrating that it is plasticity that is responsible for the inelastic behavior. Scanning electron microscopy was also used and confirmed model results. The overall damage-behavior was quantified in terms of the post fatigue failure strength for low-cycle fatigue tests. Power law model was best to fit experimental findings.
Strength and fatigue life evaluation of composite laminate with embedded sensors

NASA Astrophysics Data System (ADS)

Rathod, Vivek T.; Hiremath, S. R.; Roy Mahapatra, D.

2014-04-01

Prognosis regarding durability of composite structures using various Structural Health Monitoring (SHM) techniques is an important and challenging topic of research. Ultrasonic SHM systems with embedded transducers have potential application here due to their instant monitoring capability, compact packaging potential toward unobtrusiveness and noninvasiveness as compared to non-contact ultrasonic and eddy current techniques which require disassembly of the structure. However, embedded sensors pose a risk to the structure by acting as a flaw thereby reducing life. The present paper focuses on the determination of strength and fatigue life of the composite laminate with embedded film sensors like CNT nanocomposite, PVDF thin films and piezoceramic films. First, the techniques of embedding these sensors in composite laminates is described followed by the determination of static strength and fatigue life at coupon level testing in Universal Testing Machine (UTM). Failure mechanisms of the composite laminate with embedded sensors are studied for static and dynamic loading cases. The coupons are monitored for loading and failure using the embedded sensors. A comparison of the performance of these three types of embedded sensors is made to study their suitability in various applications. These three types of embedded sensors cover a wide variety of applications, and prove to be viable in embedded sensor based SHM of composite structures.
Evaluation of the psychometric properties of the PROMIS Cancer Fatigue Short Form with cancer patients.

PubMed

Cessna, Julie M; Jim, Heather S L; Sutton, Steven K; Asvat, Yasmin; Small, Brent J; Salsman, John M; Zachariah, Babu; Fishman, Mayer; Field, Teresa; Fernandez, Hugo; Perez, Lia; Jacobsen, Paul B

2016-02-01

Fatigue is common among cancer patients and adversely impacts quality of life. As such, it is important to measure fatigue accurately in a way that is not burdensome to patients. The 7-item Patient Reported Outcome Measurement Information System (PROMIS) Cancer Fatigue Short Form scale was recently developed using item response theory (IRT). The current study evaluated the psychometric properties of this scale in two samples of cancer patients using classical test theory (CTT). Two samples were used: 121 men with prostate cancer and 136 patients scheduled to undergo hematopoietic cell transplantation (HCT) for hematologic cancer. All participants completed the PROMIS Cancer Fatigue Short Form as well as validated measures of fatigue, vitality, and depression. HCT patients also completed measures of anxiety, perceived stress, and a clinical interview designed to identify cases of cancer-related fatigue. PROMIS Cancer Fatigue Short Form items loaded on a single factor (CFI=0.948) and the scale demonstrated good internal consistency reliability in both samples (Cronbach's alphas>0.86). Correlations with psychosocial measures were significant (p values<.0001) and in the expected direction, offering evidence for convergent and concurrent validity. PROMIS Fatigue scores were significantly higher in patients who met case definition criteria for cancer-related fatigue (p<.0001), demonstrating criterion validity. The current study provides evidence that the PROMIS Cancer Fatigue Short Form is a reliable and valid measure of fatigue in cancer patients. Copyright © 2015 Elsevier Inc. All rights reserved.
Evaluation of the Psychometric Properties of the PROMIS Cancer Fatigue Short Form with Cancer Patients

PubMed Central

Cessna, Julie M.; Jim, Heather S.L.; Sutton, Steven K.; Asvat, Yasmin; Small, Brent J.; Salsman, John M.; Zachariah, Babu; Fishman, Mayer; Field, Teresa; Fernandez, Hugo; Perez, Lia; Jacobsen, Paul B.

2016-01-01

Objective Fatigue is common among cancer patients and adversely impacts quality of life. As such, it is important to measure fatigue accurately in a way that is not burdensome to patients. The 7-item Patient Reported Outcome Measurement Information System (PROMIS) Cancer Fatigue Short Form scale was recently developed using item response theory (IRT). The current study evaluated the psychometric properties of this scale in two samples of cancer patients using classical test theory (CTT). Methods Two samples were used: 121 men with prostate cancer and 136 patients scheduled to undergo hematopoietic cell transplantation (HCT) for hematologic cancer. All participants completed the PROMIS Cancer Fatigue Short Form as well as validated measures of fatigue, vitality, and depression. HCT patients also completed measures of anxiety, perceived stress, and a clinical interview designed to identify cases of cancer -related fatigue. Results PROMIS Cancer Fatigue Short Form items loaded on a single factor (CFI = 0.948) and the scale demonstrated good internal consistency reliability in both samples (Cronbach’s alphas > 0.86). Correlations with psychosocial measures were significant (p-values < .0001) and in the expected direction, offering evidence for convergent and concurrent validity. PROMIS Fatigue scores were significantly higher in patients who met case definition criteria for cancer-related fatigue (p < .0001), demonstrating criterion validity. Conclusion The current study provides evidence that the PROMIS Cancer Fatigue Short Form is a reliable and valid measure of fatigue in cancer patients. PMID:26800633
In situ SEM thermal fatigue of Al/graphite metal matrix composites

NASA Technical Reports Server (NTRS)

Zong, G. S.; Rabenberg, L.; Marcus, H. L.

1990-01-01

Several thermal fatigue-induced failure mechanisms are deduced for unidirectional graphite-reinforced 6061 Al-alloy MMCs subjected to in situ thermal cycling. These thermal cycling conditions are representative of MMC service cycles in aerospace environments, where thermal fatigue is primarily associated with changes in the stress states near the interfaces due to coefficient of thermal expansion mismatch between fiber and matrix. This in situ SEM thermal-cycling study clarified such factors affecting MMCs' thermal fatigue as local fiber content and distribution, void volume, fiber stiffness, thermal excursion magnitude, and number of thermal cycles. MMC microfailure modes in thermal fatigue have been deduced.
An Investigation on the Wear Resistance and Fatigue Behaviour of Ti-6Al-4V Notched Members Coated with Hydroxyapatite Coatings

PubMed Central

Oskouei, Reza H; Fallahnezhad, Khosro; Kuppusami, Sushmitha

2016-01-01

In this study, surface properties of Ti-6Al-4V alloy coated with hydroxyapatite coatings were investigated. Wear resistance and fatigue behaviour of samples with coating thicknesses of 10 and 50 µm as well as uncoated samples were examined. Wear experiments demonstrated that the friction factor of the uncoated titanium decreased from 0.31 to 0.06, through a fluctuating trend, after 50 cycles of wear tests. However, the friction factor of both the coated samples (10 and 50 µm) gradually decreased from 0.20 to 0.12 after 50 cycles. At the end of the 50th cycle, the penetration depth of the 10 and 50 µm coated samples were 7.69 and 6.06 µm, respectively. Fatigue tests showed that hydroxyapatite coatings could improve fatigue life of a notched Ti-6Al-4V member in both low and high cycle fatigue zones. It was understood, from fractography of the fracture surfaces, that the fatigue zone of the uncoated specimens was generally smaller in comparison with that of the coated specimens. No significant difference was observed between the fatigue life of coated specimens with 10 and 50 µm thicknesses. PMID:28787911
Microstructural examination of fatigue crack tip in high strength steel

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuoka, C.; Yoshizawa, H.; Nakagawa, Y.G.

1993-10-01

Fatigue tests were performed to examine how microstructural conditioning influences crack initiation and propagation in SA508 class 3 low-carbon steel. A 3-mm-long crack was introduced in compact tension (CT) fatigue test specimens under four different loads in order to obtain crack tip plastic zones at different stress intensity factor ranges, [Delta]K = 18, 36, 54, and 72 MPa[radical]m. The microstructure of the plastic zones around the crack tip were examined by transmission electron microscopy (TEM) and selected area electron diffraction (SAD). Micro-orientation of the dislocation cells in the plastic zones of all of the CT samples increased to 4 degmore » from the level of an as-received sample. Four-point bending fatigue tests were performed for plate shape samples with a large cyclic strain range. The SAD value of the bending samples was also 4 deg in the damaged area where cracks already initiated at an early stage of the fatigue process. These test results indicate that the microstructural conditioning is a prerequisite for the fatigue crack initiation and propagation in SA508. These observations may lead to better understanding of how fatigue initiation processes transit to cracks.« less
Effects of bionic units on the fatigue wear of gray cast iron surface with different shapes and distributions

NASA Astrophysics Data System (ADS)

Chen, Zhi-kai; Lu, Shu-chao; Song, Xi-bin; Zhang, Haifeng; Yang, Wan-shi; Zhou, Hong

2015-03-01

To improve the fatigue wear resistance of gray cast iron (GCI), GCI samples were modified by a laser to imitate the unique structure of some soil animals alternating between soft and hard phases; the hard phase resists the deformation and the soft phase releases the deformation. Using the self-controlled fatigue wear test method, the fatigue wear behaviors of treated and untreated samples were investigated and compared experimentally. The results show that the bionic non-smooth surface obtains a beneficial effect on improving the fatigue wear resistance of a sample, and the fatigue wear resistance of the bionic sample assembled with reticulate units (60°+0°), whose mass loss was reduced by 62%, was superior to the others. Meanwhile, a finite element (FE) was used to simulate the compression and the distributions of strain and stress on the non-smooth surface was inferred. From these results, we understood that the functions of the bionic unit such as reducing strain and stress, and also obstructing the closure and propagation of cracks were the main reasons for improving the fatigue wear property of GCI.
Elevated body temperature is linked to fatigue in an Italian sample of relapsing-remitting multiple sclerosis patients.

PubMed

Leavitt, V M; De Meo, E; Riccitelli, G; Rocca, M A; Comi, G; Filippi, M; Sumowski, J F

2015-11-01

Elevated body temperature was recently reported for the first time in patients with relapsing-remitting multiple sclerosis (RRMS) relative to healthy controls. In addition, warmer body temperature was associated with worse fatigue. These findings are highly novel, may indicate a novel pathophysiology for MS fatigue, and therefore warrant replication in a geographically separate sample. Here, we investigated body temperature and its association to fatigue in an Italian sample of 44 RRMS patients and 44 age- and sex-matched healthy controls. Consistent with our original report, we found elevated body temperature in the RRMS sample compared to healthy controls. Warmer body temperature was associated with worse fatigue, thereby supporting the notion of endogenous temperature elevations in patients with RRMS as a novel pathophysiological factor underlying fatigue. Our findings highlight a paradigm shift in our understanding of the effect of heat in RRMS, from exogenous (i.e., Uhthoff's phenomenon) to endogenous. Although randomized controlled trials of cooling treatments (i.e., aspirin, cooling garments) to reduce fatigue in RRMS have been successful, consideration of endogenously elevated body temperature as the underlying target will enhance our development of novel treatments.
Bearingless helicopter main rotor development. Volume 2: Combined load fatigue evaluation of weathered graphite/epoxy composite

NASA Technical Reports Server (NTRS)

Rackiewicz, J. J.

1977-01-01

Small scale combined load fatigue tests were conducted on six artificially and six naturally weathered test specimens. The test specimen material was unidirectionally oriented A-S graphite - woven glass scrim epoxy resin laminate.

Fatigue resistance and microleakage of CAD/CAM ceramic and composite molar crowns.

PubMed

Kassem, Amr S; Atta, Osama; El-Mowafy, Omar

2012-01-01

The aim of this study was to determine effect of compressive cyclic loading on fatigue resistance and microleakage of monolithic CAD/CAM molar ceramic and composite crowns. Thirty-two extracted molars were prepared to receive CEREC crowns according to manufacturer's guidelines using a special paralleling device (Parallel-A-Prep). Sixteen feldspathic ceramic crowns (VITABLOCS Mark II) (VMII) and 16 resin-composite crowns (Paradigm-MZ100 blocks) (PMZ) were milled using a CEREC-3D machine. Eight crowns of each group were cemented to their respective teeth using self-etching resin cement (Panavia-F-2.0) (PAN), and eight were cemented using self-adhesive resin cement (RelyX-Unicem-Clicker) (RXU). Following storage for 1 week in water, specimens were subjected to uniaxial compressive cyclic loading in an Instron testing machine at 12 Hz for 1,000,000 cycles. Load was applied at the central fossa, and the cycle range was 60-600 N. Specimens were then subjected to microleakage testing. Data were statistically analyzed using factorial ANOVA and Post Hoc (Tukey HSD) tests. All composite crowns survived compressive cyclic loading without fracture, while three ceramic crowns from the subgroup cemented with RXU developed surface cracks at the center of occlusal surfaces, extending laterally. Microleakage scores of ceramic crowns cemented with PAN were significantly lower than those of the other three subgroups (p < 0.05). After 1,000,000 cycles of compressive cyclic loading, PMZ composite molar crowns were more fatigue-resistant than VMII ceramic crowns. Cement type had a significant effect on fatigue resistance of the ceramic crowns but not the composite ones. Microleakage scores of ceramic crowns cemented with PAN were significantly lower than those of the other subgroups (p < 0.05). © 2011 by The American College of Prosthodontists.
Conditioning monitoring by microstructural evaluation of cumulative fatigue damage

NASA Astrophysics Data System (ADS)

Fukuoka, C.; Nakagawa, Y. G.; Lance, J. J.; Pangborn, R. N.

1996-12-01

The objective of this work is to evaluate the damage induced below and above the fatigue limit (Δ σ t =360 MPa) in pressure vessel steels, such as SA508. Fatigue damage was induced in samples taken from an SA508 steel plate by various loading histories in order to examine the influence of prior cyclic loading below the fatigue limit. Cell-to-cell misorientation differences were measured by the selected area diffraction (SAD) method. Surface cracking was also studied by the replication method. Small cracks were observed after precycling both below and above the fatigue limit. It was, however, found that fatigue test bars had a longer lifetime after precycling below the fatigue limit, while precycling above the fatigue limit caused other specimens to fail even when subsequently cycled below the fatigue limit. Cell-to-cell misorientation usually increases with accumulation of fatigue damage, but it was found that the misorientations measured after precycling below the fatigue limit decreased again at the beginning of the subsequent cycling above the fatigue limit. It should be noted that the misorientation at failure was always about 4 to 5 deg, regardless of loading histories. Misorientation showed good correlation with the fatigue lifetime of the samples.
Flexure fatigue testing of 90 deg graphite/epoxy composites

NASA Technical Reports Server (NTRS)

Peck, Ann Nancy W.

1995-01-01

A great deal of research has been performed characterizing the in-plane fiber-dominated properties, under both static and fatigue loading, of advanced composite materials. To the author's knowledge, no study has been performed to date investigating fatigue characteristics in the transverse direction. This information is important in the design of bonded composite airframe structure where repeated, cyclic out-of-plane bending may occur. Recent tests characterizing skin/stringer debond failures in reinforced composite panels where the dominant loading in the skin is flexure along the edge of the frame indicate failure initiated either in the skin or else the flange, near the flange tip. When failure initiated in the skin, transverse matrix cracks formed in the surface skin ply closest to the flange and either initiated delaminations or created matrix cracks in the next lower ply, which in turn initiated delaminations. When failure initiated in the flanges, transverse cracks formed in the flange angle ply closest to the skin and initiated delamination. In no configuration did failure propagate through the adhesive bond layer. For the examined skin/flange configurations, the maximum transverse tension stress at failure correlates very well with the transverse tension strength of the composites. Transverse tension strength (static) data of graphite epoxy composites have been shown to vary with the volume of material stressed. As the volume of material stressed increased, the strength decreased. A volumetric scaling law based on Weibull statistics can be used to predict the transverse strength measurements. The volume dependence reflects the presence of inherent flaws in the microstructure of the lamina. A similar approach may be taken to determine a volume scale effect on the transverse tension fatigue behavior of graphite/epoxy composites. The objective of this work is to generate transverse tension strength and fatigue S-N characteristics for composite materials using 3-point flexure tests of 90 deg graphite/epoxy specimens. Investigations will include the volume scale effect as well as frequency and span-to-thickness ratio effects. Prior to the start of the experimental study, an analytical study using finite element modeling will be performed to investigate the span-to-thickness effect. The ratio of transverse flexure stress to shear stress will be monitored and its values predicted by the FEM analysis compared with the value obtained using a 'strength of materials' based approach.
Bending strength of delaminated aerospace composites.

PubMed

Kinawy, Moustafa; Butler, Richard; Hunt, Giles W

2012-04-28

Buckling-driven delamination is considered among the most critical failure modes in composite laminates. This paper examines the propagation of delaminations in a beam under pure bending. A pre-developed analytical model to predict the critical buckling moment of a thin sub-laminate is extended to account for propagation prediction, using mixed-mode fracture analysis. Fractography analysis is performed to distinguish between mode I and mode II contributions to the final failure of specimens. Comparison between experimental results and analysis shows agreement to within 5 per cent in static propagation moment for two different materials. It is concluded that static fracture is almost entirely driven by mode II effects. This result was unexpected because it arises from a buckling mode that opens the delamination. For this reason, and because of the excellent repeatability of the experiments, the method of testing may be a promising means of establishing the critical value of mode II fracture toughness, G(IIC), of the material. Fatigue testing on similar samples showed that buckled delamination resulted in a fatigue threshold that was over 80 per cent lower than the static propagation moment. Such an outcome highlights the significance of predicting snap-buckling moment and subsequent propagation for design purposes.
The influence of muscle fiber type composition on the patterns of responses for electromyographic and mechanomyographic amplitude and mean power frequency during a fatiguing submaximal isometric muscle action.

PubMed

Beck, T W; Housh, T J; Fry, A C; Cramer, J T; Weir, J P; Schilling, B K; Falvo, M J; Moore, C A

2007-07-01

The purpose of this investigation was to examine the influence of muscle fiber type composition on the patterns of responses for electromyographic (EMG) and mechanomyographic (MMG) amplitude and mean power frequency (MPF) during a fatiguing submaximal isometric muscle action. Five resistance-trained (mean +/- SD age = 23.2 +/- 3.7 yrs) and five aerobically-trained (mean +/- SD age = 32.6 +/- 5.2 yrs) men volunteered to perform a fatiguing, 30-sec submaximal isometric muscle action of the leg extensors at 50% of the maximum voluntary contraction (MVC). Muscle biopsies from the vastus lateralis revealed that the myosin heavy chain (MHC) composition for the resistance-trained subjects was 59.0 +/- 4.2% Type IIa, 0.1 +/- 0.1% Type IIx, and 40.9 +/- 4.3% Type I. The aerobically-trained subjects had 27.4 +/- 7.8% Type IIa, 0.0 +/- 0.0% Type IIx, and 72.6 +/- 7.8% Type I MHC. The patterns of responses and mean values for absolute and normalized EMG amplitude and MPF during the fatiguing muscle action were similar for the resistance-trained and aerobically-trained subjects. The resistance-trained subjects demonstrated relatively stable levels for absolute and normalized MMG amplitude and MPF across time, but the aerobically-trained subjects showed increases in MMG amplitude and decreases in MMG MPE The absolute MMG amplitude and MPF values for the resistance-trained subjects were also greater than those for the aerobi-cally-trained subjects. These findings suggested that unlike surface EMG, MMG may be a useful noninvasive technique for examining fatigue-related differences in muscle fiber type composition.
Fatigue properties of piezoelectric-electrostrictive Pb(Mg1/3,Nb2/3)O3-PbTiO3 monolithic bilayer composites

NASA Astrophysics Data System (ADS)

Hall, A.; Akdogan, E. K.; Safari, A.

2006-11-01

The fatigue response of monolithic piezoelectric 0.65Pb(Mg1/3Nb2/3)O3-0.35PbTiO3-electrostrictive 0.90Pb(Mg1/3Nb2/3)O3-0.10PbTiO3 bilayer composites was investigated experimentally. The monomorph bilayers were cosintered at 1150°C, and the polarization hysteresis, relative permittivity, displacement, and cyclic fatigue (107cycles) were measured as a function of piezoelectric-electrostrictive volume fraction (PEVF) ratio. The highest tip displacement of bilayers was found in the 3:1 PEVF monolith, reaching 40μm at 5kV/cm applied field strength. By minimizing the electrostrictive layer thickness, tip displacement substantially increased, while maintaining a lower hysteresis than the purely piezoelectric counterpart. Fatigue measurements indicated a 31% decrease in displacement after 107cycles in 3:1 monoliths, whereas the 1:3 PEVF only showed a 12% decrease under the same conditions. There is a 30% increase in polarization after 107cycles for 1:1 PEVF bilayers, which is attributed to self-poling due to a diffuse transition layer in the vicinity of the interface. It was found that partial 90° domain switching occurred prior to poling because of the residual stresses in the composite, imposed by the electrostrictive layer and the spontaneous strain associated with the cubic-tetragonal transition in the ferroelectric layer. The results indicate that the electrostrictive layer, which is electrically in series with the piezoelectric one, enhances the fatigue resistance of the monolithic bilayer composites in addition to the increase in tip displacement.
Gamma Radiation Sterilization Reduces the High-cycle Fatigue Life of Allograft Bone.

PubMed

Islam, Anowarul; Chapin, Katherine; Moore, Emily; Ford, Joel; Rimnac, Clare; Akkus, Ozan

2016-03-01

Sterilization by gamma radiation impairs the mechanical properties of bone allografts. Previous work related to radiation-induced embrittlement of bone tissue has been limited mostly to monotonic testing which does not necessarily predict the high-cycle fatigue life of allografts in vivo. We designed a custom rotating-bending fatigue device to answer the following questions: (1) Does gamma radiation sterilization affect the high-cycle fatigue behavior of cortical bone; and (2) how does the fatigue life change with cyclic stress level? The high-cycle fatigue behavior of human cortical bone specimens was examined at stress levels related to physiologic levels using a custom-designed rotating-bending fatigue device. Test specimens were distributed among two treatment groups (n = 6/group); control and irradiated. Samples were tested until failure at stress levels of 25, 35, and 45 MPa. At 25 MPa, 83% of control samples survived 30 million cycles (run-out) whereas 83% of irradiated samples survived only 0.5 million cycles. At 35 MPa, irradiated samples showed an approximately 19-fold reduction in fatigue life compared with control samples (12.2 × 10(6) ± 12.3 × 10(6) versus 6.38 × 10(5) ± 6.81 × 10(5); p = 0.046), and in the case of 45 MPa, this reduction was approximately 17.5-fold (7.31 × 10(5) ± 6.39 × 10(5) versus 4.17 × 10(4) ± 1.91 × 10(4); p = 0.025). Equations to estimate high-cycle fatigue life of irradiated and control cortical bone allograft at a certain stress level were derived. Gamma radiation sterilization severely impairs the high cycle fatigue life of structural allograft bone tissues, more so than the decline that has been reported for monotonic mechanical properties. Therefore, clinicians need to be conservative in the expectation of the fatigue life of structural allograft bone tissues. Methods to preserve the fatigue strength of nonirradiated allograft bone tissue are needed. As opposed to what monotonic tests might suggest, the cyclic fatigue life of radiation-sterilized structural allografts is likely severely compromised relative to the nonirradiated condition and therefore should be taken into consideration. Methods to reduce the effect of irradiation or to recover structural allograft bone tissue fatigue strength are important to pursue.
Reciprocal relationship between acute stress and acute fatigue in everyday life in a sample of university students.

PubMed

Doerr, Johanna M; Ditzen, Beate; Strahler, Jana; Linnemann, Alexandra; Ziemek, Jannis; Skoluda, Nadine; Hoppmann, Christiane A; Nater, Urs M

2015-09-01

We investigated whether stress may influence fatigue, or vice versa, as well as factors mediating this relationship. Fifty healthy participants (31 females, 23.6±3.2 years) completed up to 5 momentary assessments of stress and fatigue during 5 days of preparation for their final examinations (exam condition) and 5 days of a regular semester week (control condition). Sleep quality was measured by self-report at awakening. A sub-group of participants (n=25) also collected saliva samples. Fatigue was associated with concurrent stress, stress reported at the previous measurement point, and previous-day stress. However, momentary stress was also predicted by concurrent fatigue, fatigue at the previous time point, and previous-day fatigue. Sleep quality mediated the association between stress and next-day fatigue. Cortisol and alpha-amylase did not mediate the stress-fatigue relationship. In conclusion, there is a reciprocal stress-fatigue relationship. Both prevention and intervention programs should comprehensively cover how stress and fatigue might influence one another. Copyright © 2015 Elsevier B.V. All rights reserved.
Pharmaceutical composition and drug effect of synthetic Bacopa monnieri L. health promoting agent from the perspective of resistance fatigue.

PubMed

Chen, Zhidan; Yan, Yanqin

2017-09-01

Bacopa monnieri has effect on the nervous system, digestive system and blood circulation systems. In this paper, the authors conducted pharmacological analysis on Bacopa monniera and its innovative pharmaceutical preparation of promote motor function. The extract of the drug has some effect on relieving the fatigue and providing the movement function. By analyzing the composition and efficacy of Chinese herbal extracts, it can be seen that these drugs have obvious effect on improving immunity. Experimental results show that the agent can increase the liver glycogen energy reserves, reduce Bla and BUN levels, balance and energy metabolism of muscle cells in the environment, it plays a positive role to improve the exercise capacity and exercise fatigue.
Additional thermal fatigue data on nickel- and cobalt-base superalloys, part 1

NASA Technical Reports Server (NTRS)

Howes, M. A. H.

1973-01-01

The fluidized bed technique was used to measure the relative thermal fatigue resistance of twenty-one superalloys. Among the thirty-six variations of composition, solidification method, and surface protection the cycles to cracking differed by two to three orders of magnitude. Some alloys suffered serious weight losses and oxidation. Thermal fatigue data, oxidation, and dimensional changes are reported. The types of superalloys are identified.
Monotonic, Creep-Rupture, and Fatigue Behavior of Carbon Fiber Reinforced Silicon Carbide (C/SiC) at an Elevated Temperature

DTIC Science & Technology

2004-03-01

elevated temperature of 550 C. Cyclic loading of C/SiC was investigated at frequencies of 375 Hz , 10 Hz, 1 Hz, and 0.1 Hz. Creep-Rupture tests and tests that...is reduced when frequency of fatigue is increased. At high frequency fatigue (10Hz to 375 Hz ), C/SiC composites have longer cycle lives and time lives
Fatigue Behavior of Porous Ti-6Al-4V Made by Laser-Engineered Net Shaping

PubMed Central

Bordonaro, Giancarlo G.; Berto, Filippo

2018-01-01

The fatigue behavior and fracture mechanisms of additively manufactured Ti-6Al-4V specimens are investigated in this study. Three sets of testing samples were fabricated for the assessment of fatigue life. The first batch of samples was built by using Laser-Engineered Net Shaping (LENS) technology, a Direct Energy Deposition (DED) method. Internal voids and defects were induced in a second batch of samples by changing LENS machine processing parameters. Fatigue performance of these samples is compared to the wrought Ti-6Al-4V samples. The effects of machine-induced porosity are assessed on mechanical properties and results are presented in the form of SN curves for the three sets of samples. Fracture mechanisms are examined by using Scanning Electron Microscopy (SEM) to characterize the morphological characteristics of the failure surface. Different fracture surface morphologies are observed for porous and non-porous specimens due to the combination of head write speed and laser power. Formation of defects such as pores, unmelted regions, and gas entrapments affect the failure mechanisms in porous specimens. Non-porous specimens exhibit fatigue properties comparable with that of the wrought specimens, but porous specimens are found to show a tremendous reduced fatigue strength. PMID:29439510
Room Temperature Tensile Behavior and Damage Accumulation of Hi-Nicalon Reinforced SiC Matrix Composites

NASA Technical Reports Server (NTRS)

Morscher, G. N.; Gyekenyesi, J. Z.

1998-01-01

Composites consisting of woven Hi-Nicalon fibers, BN interphases, and different SiC matrices were studied in tension at room temperature. Composites with SiC matrices processed by CVI and melt infiltration were compared. Monotonic and load/unload/reload tensile hysteresis experiments were performed. A modal acoustic emission (AE) analyzer was used to monitor damage accumulation during the tensile test. Post test polishing of the tensile gage sections was performed to determine the extent of cracking. The occurrence and location of cracking could easily be determined using modal AE. The loss of modulus could also effectively be determined from the change in the velocity of sound across the sample. Finally, the stresses where cracks appear to intersect the load-bearing fibers correspond with high temperature low cycle fatigue run out stresses for these materials.
Effects of combined plasma chromizing and shot peening on the fatigue properties of a Ti6Al4V alloy

NASA Astrophysics Data System (ADS)

Yu, Shouming; Liu, Daoxin; Zhang, Xiaohua; Du, Dongxing

2015-10-01

A plasma chromizing treatment was conducted on Ti6Al4V samples by employing the recently developed double glow plasma surface alloying technology. The Cr-alloyed layer consisted of four sub-layers, namely the Cr deposition, Cr2Ti, CrTi4, and Cr-Ti solid-solution layers. The local hardness and moduli were determined via nanoindentation. In addition, the fatigue properties of the samples were evaluated by using a rotating-bending fatigue machine under a given load. The results showed that the hardness or elastic moduli of the adjacent sub-layers differed significantly and the fatigue properties of the Ti6Al4V alloy deteriorated with the plasma chromizing treatment. This deterioration stemmed mainly from cracks initiated at the interfaces between the sub-layers and the microstructural changes of the substrate; these changes were induced by the high temperature used in the plasma chromizing process. However, the fatigue life of the plasma-chromized samples was increased by a shot peening post-treatment. The fatigue life of the samples resulting from this combination of treatments was slightly higher than that of the single-shot-peened Ti6Al4V substrate. In fact, the sample retaining only the Cr-Ti solid-solution layer (that is, the first three sub-layers were removed), when shot-peened, exhibited the highest fatigue life among all the tested samples; this was attributed to that sample having the highest residual compressive stress, the significant work hardening, and the good hardness to toughness balance.
Effect of glucose on fatigue-induced changes in the microstructure and mechanical properties of demineralized bovine cortical bone.

PubMed

Trębacz, Hanna; Zdunek, Artur; Wlizło-Dyś, Ewa; Cybulska, Justyna; Pieczywek, Piotr

2015-10-16

The aim of this study was to test a hypothesis that fatigue-induced weakening of cortical bone was intensified in bone incubated in glucose and that this weakening is revealed in the microstructure and mechanical competence of the bone matrix. Cubic specimens of bovine femoral shaft were incubated in glucose solution (G) or in buffer (NG). One half of G samples and one half of NG were axially loaded in 300 cycles (30 mm/min) at constant deformation (F); the other half was a control (C). Samples from each group (GF, NGF, GC, NGC) were completely demineralized. Slices from demineralized samples were used for microscopic image analysis. A combined effect of glycation and fatigue on demineralized bone was tested in compression (10 mm/min). Damage of samples during the test was examined in terms of acoustic emission analysis (AE). During the fatigue procedure, resistance to loading in glycated samples decreased by 14.5% but only by 8.1% in nonglycated samples. In glycated samples fatigue resulted in increased porosity with pores significantly larger than in the other groups. Under compression, strain at failure in demineralized bone was significantly affected by glucose and fatigue. AE from demineralized bone matrix was considerably related to the largest pores in the tissue. The results confirm the hypothesis that the effect of fatigue on cortical bone tissue was intensified after incubation in glucose, both in the terms of the mechanical competence of bone tissue and the structural changes in the collagenous matrix of bone.
Cast iron-base alloy for cylinder/regenerator housing

NASA Technical Reports Server (NTRS)

Witter, Stewart L.; Simmons, Harold E.; Woulds, Michael J.

1985-01-01

NASACC-1 is a castable iron-base alloy designed to replace the costly and strategic cobalt-base X-40 alloy used in the automotive Stirling engine cylinder/generator housing. Over 40 alloy compositions were evaluated using investment cast test bars for stress-rupture testing. Also, hydrogen compatibility and oxygen corrosion resistance tests were used to determine the optimal alloy. NASACC-1 alloy was characterized using elevated and room temperature tensile, creep-rupture, low cycle fatigue, heat capacity, specific heat, and thermal expansion testing. Furthermore, phase analysis was performed on samples with several heat treated conditions. The properties are very encouraging. NASACC-1 alloy shows stress-rupture and low cycle fatigue properties equivalent to X-40. The oxidation resistance surpassed the program goal while maintaining acceptable resistance to hydrogen exposure. The welding, brazing, and casting characteristics are excellent. Finally, the cost of NASACC-1 is significantly lower than that of X-40.
International Conference on Mechanical Fatigue of Advanced Materials Held in Santa Barbara, California on 13-18 January 1991

DTIC Science & Technology

1991-02-15

been published on the basic microstructure of the monolithic alloys, particularly in the case of nickel and titanium aluminides , and several composite...34Initiation and Growth in Iniermetallic Compounds- N.S. Stoloff (invited) "Fatigue of Titanium Aluminides at Ambient and Elevated Ternperaiures" ). Bowen...applications such as life estimation for gas-turbine blades , the relevance of "small-crack" data is not fully appreciated. 3 Metal-Matrix Composites
Fiber-Reinforced Superalloys For Rocket Engines

NASA Technical Reports Server (NTRS)

Lewis, Jack R.; Yuen, Jim L.; Petrasek, Donald W.; Stephens, Joseph R.

1990-01-01

Report discusses experimental studies of fiber-reinforced superalloy (FRS) composite materials for use in turbine blades in rocket engines. Intended to withstand extreme conditions of high temperature, thermal shock, atmospheres containing hydrogen, high cycle fatigue loading, and thermal fatigue, which tax capabilities of even most-advanced current blade material - directionally-solidified, hafnium-modified MAR M-246 {MAR M-246 (Hf) (DS)}. FRS composites attractive combination of properties for use in turbopump blades of advanced rocket engines at temperatures from 870 to 1,100 degrees C.
A life prediction model for laminated composite structural components

NASA Technical Reports Server (NTRS)

Allen, David H.

1990-01-01

A life prediction methodology for laminated continuous fiber composites subjected to fatigue loading conditions was developed. A summary is presented of research completed. A phenomenological damage evolution law was formulated for matrix cracking which is independent of stacking sequence. Mechanistic and physical support was developed for the phenomenological evolution law proposed above. The damage evolution law proposed above was implemented to a finite element computer program. And preliminary predictions were obtained for a structural component undergoing fatigue loading induced damage.
Fatigue Damage-Strength Relationships in Composite Laminates. Volume 1

DTIC Science & Technology

1983-09-01

NUMBER 2. A ES ION N • /NT’S CATALOG NUMBER AFWAL-TR-83-3084, Vol I .A_"_.._ 4. TITLE (ad Subtitle) S. TYPE OF REPORT & PERIOD COVERED 1 June 1981...Fatigue Damage-Strength Relationships in Final: 31 May 1983 Composite Laminates 6. PERFORMING OAG. REPORT NUMBER 7. AUTHOR(e) 6. CONTRACT OR GRANT...I1. CONTROLLING OFFICE NAME AND ADDRESS 12. REPORT DATE September 1983 AFWAL/FIBEC 13. NUMBER OF PAGES Wright Patterson AFB, OH 45433 55 14. MONITORING

Development of a Composite Delamination Fatigue Life Prediction Methodology

NASA Technical Reports Server (NTRS)

OBrien, Thomas K.

2009-01-01

Delamination is one of the most significant and unique failure modes in composite structures. Because of a lack of understanding of the consequences of delamination and the inability to predict delamination onset and growth, many composite parts are unnecessarily rejected upon inspection, both immediately after manufacture and while in service. NASA Langley is leading the efforts in the U.S. to develop a fatigue life prediction methodology for composite delamination using fracture mechanics. Research being performed to this end will be reviewed. Emphasis will be placed on the development of test standards for delamination characterization, incorporation of approaches for modeling delamination in commercial finite element codes, and efforts to mature the technology for use in design handbooks and certification documents.
Microstructural examination of

NASA Astrophysics Data System (ADS)

Fukuoka, C.; Yoshizawa, H.; Nakagawa, Y. G.; Lapides, M. E.

1993-10-01

Fatigue tests were performed to examine how microstructural conditioning influences crack initiation and propagation in SA508 class 3 low-carbon steel. A 3-mm-long crack was introduced in compact tension (CT) fatigue test specimens under four different loads in order to obtain crack tip plastic zones at different stress intensity factor ranges, ΔK = 18, 36, 54, and 72 MPa√m. The microstructure of the plastic zones around the crack tip were examined by trans- mission electron microscopy (TEM) and selected area electron diffraction (SAD). Micro- orientation of the dislocation cells in the plastic zones of all of the CT samples increased to 4 deg from the level of an as-received sample. Four-point bending fatigue tests were performed for plate shape samples with a large cyclic strain range. The SAD value of the bending samples was also 4 deg in the damaged area where cracks already initiated at an early stage of the fatigue process. These test results indicate that the microstructural conditioning is a prerequisite for the fatigue crack initiation and propagation in SA508. These observations may lead to better under- standing of how fatigue initiation processes transit to cracks.
Fatigue crack growth in an aluminum alloy-fractographic study

NASA Astrophysics Data System (ADS)

Salam, I.; Muhammad, W.; Ejaz, N.

2016-08-01

A two-fold approach was adopted to understand the fatigue crack growth process in an Aluminum alloy; fatigue crack growth test of samples and analysis of fractured surfaces. Fatigue crack growth tests were conducted on middle tension M(T) samples prepared from an Aluminum alloy cylinder. The tests were conducted under constant amplitude loading at R ratio 0.1. The stress applied was from 20,30 and 40 per cent of the yield stress of the material. The fatigue crack growth data was recorded. After fatigue testing, the samples were subjected to detailed scanning electron microscopic (SEM) analysis. The resulting fracture surfaces were subjected to qualitative and quantitative fractographic examinations. Quantitative fracture analysis included an estimation of crack growth rate (CGR) in different regions. The effect of the microstructural features on fatigue crack growth was examined. It was observed that in stage II (crack growth region), the failure mode changes from intergranular to transgranular as the stress level increases. In the region of intergranular failure the localized brittle failure was observed and fatigue striations are difficult to reveal. However, in the region of transgranular failure the crack path is independent of the microstructural features. In this region, localized ductile failure mode was observed and well defined fatigue striations were present in the wake of fatigue crack. The effect of interaction of growing fatigue crack with microstructural features was not substantial. The final fracture (stage III) was ductile in all the cases.
Fatigue Resistance of Liquid-assisted Self-repairing Aluminum Alloys Reinforced with Shape Memory Alloys

NASA Technical Reports Server (NTRS)

Wright, M. Clara; Manuel, Michele; Wallace, Terryl

2013-01-01

A self-repairing aluminum-based composite system has been developed using a liquid-assisted healing theory in conjunction with the shape memory effect of wire reinforcements. The metal-metal composite was thermodynamically designed to have a matrix with a relatively even dispersion of a low-melting eutectic phase, allowing for repair of cracks at a predetermined temperature. Additionally, shape memory alloy (SMA) wire reinforcements were used within the composite to provide crack closure. Investigators focused the research on fatigue cracks propagating through the matrix in order to show a proof-of-concept Shape Memory Alloy Self-Healing (SMASH) technology for aeronautical applications.
Hierarchical damage mechanisms in composite materials subjected to fatigue loadings

NASA Astrophysics Data System (ADS)

D'Amore, Alberto; Grassia, Luigi

2018-02-01

The strength degradation of fiber reinforced composites subjected to constant amplitude (CA) fatigue loadings can be described by a two-parameter residual strength model. From the analytical approach it results that under moderate loadings the multiple damage mechanisms develop with different kinetics and manifest their effectiveness at different time scales highlighting the three-Stage hierarchical nature of damage accumulation in composites. The model captures the sequence of damage accumulation mechanisms from diffuse matrix cracking (I), to fiber/matrix interface failure (II) to fiber and ply rupture and delamination (III). Further, by increasing the loading severity it appears that the different mechanisms superpose witnessing their simultaneous co-existence.
Elite synchronized swimmers display decreased energy availability during intensified training.

PubMed

Schaal, K; Tiollier, E; Le Meur, Y; Casazza, G; Hausswirth, C

2017-09-01

Elite synchronized swimmers follow high-volume training regimen that result in elevated rates of exercise energy expenditure (ExEE). While adequate energy intake (EI) is important to optimize recovery, a number of sport-specific constraints may lead to chronically low energy availability (EA = EI-ExEE). This study aimed to quantify changes in EA, endocrine markers of energy conservation, and perceived fatigue in synchronized swimmers, during a week of baseline training followed by 4 weeks of intensified training (IT). EI, ExEE, and body composition were measured in nine swimmers at Baseline, midpoint (IT WK 2 ), and end of IT (IT WK 4 ). Waking saliva samples were obtained to measure [leptin] s , [ghrelin] s , and [cortisol] s . Fatigue ratings were provided daily. ExEE increased by 27% during IT. Swimmers increased EI from Baseline to IT WK 2 , but decreased it significantly from IT WK 2 to IT WK 4 . EA, fat mass, and [leptin] s decreased from Baseline to IT WK 4 , while [ghrelin] s increased significantly. Fatigue at IT WK 4 was inversely correlated with Baseline EI and EA. The significant decrease in EA was accompanied by endocrine signs of energy conservation in elite swimmers. As perceived fatigue was associated with low EA, particular attention should be paid to these athletes' energy intake during phases of heavy training. © 2016 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.
Experimental study of thermodynamics propagation fatigue crack in metals

DOE Office of Scientific and Technical Information (OSTI.GOV)

Vshivkov, A., E-mail: vshivkov.a@icmm.ru; Iziumova, A., E-mail: fedorova@icmm.ru; Plekhov, O., E-mail: poa@icmm.ru

This work is devoted to the development of an experimental method for studying the energy balance during cyclic deformation and fracture. The studies were conducted on 304 stainless steel AISE samples. The investigation of the fatigue crack propagation was carried out on flat samples with stress concentrators. The stress concentrator was three central holes. The heat flux sensor was developed based on the Seebeck effect. This sensor was used for measuring the heat dissipation power in the examined samples during the fatigue tests. The measurements showed that the rate of fatigue crack growth depends on the heat flux at themore » crack tip and there are two propagation mode of fatigue crack with different link between the propagation mode and heat flux from crack tip.« less
Fatigue testing of wood-concrete composite beams.

DOT National Transportation Integrated Search

2013-05-01

Currently, wood-concrete composite structural members are usually applied in building structures. There are a relatively small number (in the low 100s) of known bridge applications involving wood-concrete composites. A problem with using these novel ...
Prevalence of sarcopenia and relevance of body composition, physiological function, fatigue, and health-related quality of life in patients before allogeneic hematopoietic stem cell transplantation.

PubMed

Morishita, Shinichiro; Kaida, Katsuji; Tanaka, Takashi; Itani, Yusuke; Ikegame, Kazuhiro; Okada, Masaya; Ishii, Shinichi; Kodama, Norihiko; Ogawa, Hiroyasu; Domen, Kazuhisa

2012-12-01

Cachexia in patients with hematological malignancies is often related to sarcopenia. We believe that allogeneic hematopoietic stem cell transplant (allo-HSCT) patients often exhibit sarcopenia prior to transplantation. Here, we aimed to investigate the prevalence of sarcopenia and its relationship with body composition, physiological function, nutrition, fatigue, and health-related quality of life (QOL) in patients before allo-HSCT. We further investigated the confounding factors associated with sarcopenia. We included 164 patients with allo-HSCT in this study. Body composition, handgrip, knee extensor strength, and 6-min walk test were evaluated. Furthermore, fatigue, nutritional status, and health-related QOL were also evaluated. Eighty-three patients (50.6 %) enrolled in our study had sarcopenia prior to allo-HSCT. Patients with sarcopenia experienced decreased muscular strength and increased fatigue compared with patients without sarcopenia (p < 0.05). Patients with sarcopenia showed significantly lower scores in physical functioning, bodily pain, and vitality in health-related QOL than those without sarcopenia. Multivariate regression analysis revealed that only gender and body mass index were significantly related to sarcopenia (gender, odds ratio, 3.09; body mass index, odds ratio, 0.70; p < 0.01). Sarcopenia is common in patients before allo-HSCT and related to low muscle strength, fatigue, and health-related QOL. Male patients may be more susceptible to sarcopenia than female patients before allo-HSCT. Further study of rehabilitation with gender insight is warranted for patients receiving allo-HSCT.
Monitoring of fatigue damage in composite lap-joints using guided waves and FBG sensors

NASA Astrophysics Data System (ADS)

Karpenko, Oleksii; Khomenko, Anton; Koricho, Ermias; Haq, Mahmoodul; Udpa, Lalita

2016-02-01

Adhesive bonding is being increasingly employed in many applications as it offers possibility of light-weighting and efficient multi-material joining along with reduction in time and cost of manufacturing. However, failure initiation and progression in critical components like joints, specifically in fatigue loading is not well understood, which necessitates reliable NDE and SHM techniques to ensure structural integrity. In this work, concurrent guided wave (GW) and fiber Bragg grating (FBG) sensor measurements were used to monitor fatigue damage in adhesively bonded composite lap-joints. In the present set-up, one FBG sensor was strategically embedded in the adhesive bond-line of a lap-joint, while two other FBGs were bonded on the surface of the adherends. Full spectral responses of FBG sensors were collected and compared at specific intervals of fatigue loading. In parallel, guided waves were actuated and sensed using PZT wafers mounted on the composite adherends. Experimental results demonstrated that time-of-flight (ToF) of the fundamental modes transmitted through the bond-line and spectral response of FBG sensors were sensitive to fatigue loading and damage. Combination of guided wave and FBG measurements provided the desired redundancy and synergy in the data to evaluate the degradation in bond-line properties. Measurements taken in the presence of continuously applied load replicated the in-situ/service conditions. The approach shows promise in understanding the behavior of bonded joints subjected to complex loading.
Hydraulic Fatigue-Testing Machine

NASA Technical Reports Server (NTRS)

Hodo, James D.; Moore, Dennis R.; Morris, Thomas F.; Tiller, Newton G.

1987-01-01

Fatigue-testing machine applies fluctuating tension to number of specimens at same time. When sample breaks, machine continues to test remaining specimens. Series of tensile tests needed to determine fatigue properties of materials performed more rapidly than in conventional fatigue-testing machine.
Fiber reinforced PMR polyimide composites

NASA Technical Reports Server (NTRS)

Cavano, P. J.; Winters, W. E.

1978-01-01

Commercially obtained PMR-15 polyimide prepregs with S-glass and graphite fiber reinforcements were evaluated along with in-house prepared glass and graphite cloth PMR 2 materials. A novel autoclave approach was conceived and used to demonstrate that both the PMR systems respond to 1.4 MPa (200 psi) autoclave pressures to produce void free composites equivalent to die molded laminates. Isothermal gravimetric analysis and subsequent mechanical property tests indicated that the PMR 2 system was significantly superior in thermo-oxidative stability, and that S-glass reinforcements may contribute to the accelerated degradation of composites at 316 C (600 F) when compared to graphite fiber reinforced composites. Fully reversed bending fatigue experiments were conducted with a type of fixture unused for organic matrix composites. These studies indicated that the graphite fiber composites were clearly superior in fatigue resistance to the glass fiber reinforced material and that PMR matrix composite systems yield performance of the same order as composite materials employing other families of matrices.
Strain energy release rate as a function of temperature and preloading history utilizing the edge delamination fatique test method

NASA Technical Reports Server (NTRS)

Zimmerman, Richard S.; Adams, Donald F.

1989-01-01

Static laminate and tension-tension fatigue tests of IM7/8551-7 composite materials was performed. The Edge Delamination Test (EDT) was utilized to evaluate the temperature and preloading history effect on the critical strain energy release rate. Static and fatigue testing was performed at room temperature and 180 F (82 C). Three preloading schemes were used to precondition fatigue test specimens prior to performing the normal tension-tension fatigue EDT testing. Computer software was written to perform all fatigue testing while monitoring the dynamic modulus to detect the onset of delamination and record the test information for later retrieval and reduction.
Fatigue behavior of AAR Class A railroad wheel steel at ambient and elevated temperatures.

DOT National Transportation Integrated Search

2006-12-01

This report documents a test program to determine the material properties (chemical composition, tensile, and fatigue) at ambient and elevated temperatures of a Class A wheel steel as designated by the Association of American Railroads. The 3 tempera...
Effects of Long Term Exposures on PM Disk Superalloys

NASA Technical Reports Server (NTRS)

Gabb, T. P.; Sudbrack, C. K.; Draper, S. L.; MacKay, R. A.; Telesman, J.

2013-01-01

Turbine disks in some advanced engine applications may be exposed to temperatures above 700 C for extended periods of time, approaching 1,000 h. These exposures could affect the near-surface composition and microstructure through formation of damaged and often embrittled layers. The creation of such damaged layers could significantly affect local mechanical properties. Powder metal disk superalloys LSHR and ME3 were exposed at temperatures of 704, 760, and 815 C for times up to 2,020 h, and the types and depths of environmental attacked were measured. Fatigue tests were performed for selected cases at 704 and 760 C, to determine the impact of these exposures on fatigue life. Fatigue resistance was reduced up to 98% in both superalloys for some exposure conditions. Tensile tests were also performed to help understand fatigue responses, and showed corresponding reductions in ductility. The changes in surface composition and phases, depths of these changed layers, failure responses, and failure initiation modes were compared.
Design and simulation of Macro-Fiber composite based serrated microflap for wind turbine blade fatigue load reduction

NASA Astrophysics Data System (ADS)

Sun, Xiao; Dai, Qingli; Bilgen, Onur

2018-05-01

A Macro-Fiber Composite (MFC) based active serrated microflap is designed in this research for wind turbine blades. Its fatigue load reduction potential is evaluated in normal operating conditions. The force and displacement output of the MFC-based actuator are simulated using a bimorph beam model. The work done by the aerodynamic, centripetal and gravitational forces acting on the microflap were calculated to determine the required capacity of the MFC-based actuator. MFC-based actuators with a lever mechanical linkage are designed to achieve the required force and displacement to activate the microflap. A feedback control scheme is designed to control the microflap during operation. Through an aerodynamic-aeroelastic time marching simulation with the designed control scheme, the time responses of the wind turbine blades are obtained. The fatigue analysis shows that the serrated microflap can reduce the standard deviation of the blade root flapwise bending moment and the fatigue damage equivalent loads.
Development of the Damage Tolerance Criteria for an Aging Fleet

DTIC Science & Technology

2014-10-20

show that it is possible to increase the fatigue life of aluminium alloys (2024 T3) repaired with composite materials doped with MWNT. Also, it is...possible to detect corrosion effects due to galvanic effects between MWNT and aluminium alloys . Motivation Currently it’s possible and it’s not...Objectives General Goal To study the fatigue life of aluminium alloys used in aeronautics and to investigate how to increase the fatigue
Conditioning monitoring by microstructural evaluation of cumulative fatigue damage

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuoka, C.; Nakagawa, Y.G.; Lance, J.J.

1996-12-01

The objective of this work is to evaluate the damage induced below and above the fatigue limit ({Delta}{sigma}{sub t} = 360 MPa) in pressure vessel steels, such as SA508. Fatigue damage was induced in samples taken from an SA508 steel plate by various loading histories in order to examine the influence of prior cyclic loading below the fatigue limit. Cell-to-cell misorientation differences were measured by the selected area diffraction (SAD) method. Surface cracking was also studied by the replication method. Small cracks were observed after precycling both below and above the fatigue limit. It was, however, found that fatigue testmore » bars had a longer lifetime after precycling below the fatigue limit, while precycling above the fatigue limit caused other specimens to fail even when subsequently cycled below the fatigue limit. Cell-to-cell misorientation usually increases with accumulation of fatigue damage, but it was found that the misorientations measured after precycling below the fatigue limit decreased again at the beginning of the subsequent cycling above the fatigue limit. It should be noted that the misorientation at failure was always about 4 to 5 deg, regardless of loading histories. Misorientation showed good correlation with the fatigue lifetime of the samples.« less
Towards a damage tolerance philosophy for composite materials and structures

NASA Technical Reports Server (NTRS)

O'Brien, T. Kevin

1990-01-01

A damage-threshold/fail-safe approach is proposed to ensure that composite structures are both sufficiently durable for economy of operation, as well as adequately fail-safe or damage tolerant for flight safety. Matrix cracks are assumed to exist throughout the off-axis plies. Delamination onset is predicted using a strain energy release rate characterization. Delamination growth is accounted for in one of three ways: either analytically, using delamination growth laws in conjunction with strain energy release rate analyses incorporating delamination resistance curves; experimentally, using measured stiffness loss; or conservatively, assuming delamination onset corresponds to catastrophic delamination growth. Fail-safety is assessed by accounting for the accumulation of delaminations through the thickness. A tension fatigue life prediction for composite laminates is presented as a case study to illustrate how this approach may be implemented. Suggestions are made for applying the damage-threshold/fail-safe approach to compression fatigue, tension/compression fatigue, and compression strength following low velocity impact.
Towards a damage tolerance philosophy for composite materials and structures

NASA Technical Reports Server (NTRS)

Obrien, T. Kevin

1988-01-01

A damage-threshold/fail-safe approach is proposed to ensure that composite structures are both sufficiently durable for economy of operation, as well as adequately fail-safe or damage tolerant for flight safety. Matrix cracks are assumed to exist throughout the off-axis plies. Delamination onset is predicted using a strain energy release rate characterization. Delamination growth is accounted for in one of three ways: either analytically, using delamination growth laws in conjunction with strain energy release rate analyses incorporating delamination resistance curves; experimentally, using measured stiffness loss; or conservatively, assuming delamination onset corresponds to catastrophic delamination growth. Fail-safety is assessed by accounting for the accumulation of delaminations through the thickness. A tension fatigue life prediction for composite laminates is presented as a case study to illustrate how this approach may be implemented. Suggestions are made for applying the damage-threshold/fail-safe approach to compression fatigue, tension/compression fatigue, and compression strength following low velocity impact.

Materials research for high-speed civil transport and generic hypersonics: Composites durability

NASA Technical Reports Server (NTRS)

Allen-Lilly, Heather; Cregger, Eric; Hoffman, Daniel; Mccool, Jim

1995-01-01

This report covers a portion of an ongoing investigation of the durability of composites for the High Speed Civil Transport (HSCT) program. Candidate HSCT composites need to possess the high-temperature capability required for supersonic flight. This program was designed to initiate the design, analysis, fabrication, and testing of equipment intended for use in validating the long-term durability of materials for the HSCT. This equipment includes thermally actuated compression and tension fixtures, hydraulic-actuated reversible load fixtures, and thermal chambers. This equipment can be used for the durability evaluation of both composite and adhesive materials. Thermally actuated fixtures are recommended for fatigue cycling when long-term thermomechanical fatigue (TMF) data are required on coupon-sized tension or compression specimens. Long term durability testing plans for polymer matrix composite specimens are included.
Microtexture Analysis and Modeling of Ambient Fatigue and Creep-Fatigue Damages in Ti-6Al-4V Alloy

NASA Astrophysics Data System (ADS)

Kumar, Jalaj; Singh, A. K.; Raman, S. Ganesh Sundara; Kumar, Vikas

2017-02-01

In the present investigation, microtexture analysis using electron back-scattered diffraction technique has been performed to study fatigue- and creep-fatigue damages and associated deformation structures in Ti-6Al-4V alloy. Special emphasis has been given to low-angle grain boundary configuration and its possible application as a damage indicator. Damage is mostly present in the form of voids as investigated through scanning electron microscopy. Stored deformation energies have been evaluated for the strain-controlled fatigue-, the stress-controlled fatigue-, and the creep-fatigue-tested samples. Stored deformation energies have also been analyzed vis-à-vis total damage energies to quantify the contribution of damages to various samples. A relation between the stored deformation energy and the applied strain amplitude has been proposed in this study.
Effects of physical activity on body composition and fatigue perception in patients on thyrotropin-suppressive therapy for differentiated thyroid carcinoma.

PubMed

Vigário, Patrícia dos Santos; Chachamovitz, Dhiãnah Santini de Oliveira; Cordeiro, Mônica Fabíola Nogueira; Teixeira, Patrícia de Fátima dos Santos; de Castro, Carmen Lúcia Natividade; de Oliveira, Fátima Palha; Vaisman, Mário

2011-07-01

Subclinical thyrotoxicosis (scTox) may be associated with alterations in body composition and fatigue that can be possibly reversed with physical activity. The aim of the present study was to evaluate whether the systematic practice of physical activity improves lower extremity muscle mass and fatigue perception in patients with scTox. We studied 36 patients (2 men) with median age of 48.0 (43.0-51.0) years, body mass index of 27.4 (22.1-30.2) kg/m(2), thyrotropin <0.4 mU/L, and free thyroxine between 0.8 and 1.9 ng/dL and 48 control subjects (C group; 7 men). Patients were randomly divided in two groups according to the adherence to the exercise training: scTox-Tr (n = 19)-patients who adhered to the exercise intervention and scTox-Sed (n = 17)--patients who did not adhere to it. The C group did not participate in the randomization. The exercise training was supervised by a physical education instructor, and it was composed of 60 minutes of aerobic activity and stretching exercises, twice a week, during 12 weeks. In both groups, body composition was assessed (anthropometric method), and the Chalder Fatigue Scale was determined at baseline and after 3 months of intervention (scTox-Tr group) or observation (scTox-Sed group). At baseline, patients with scTox had lower muscle mass and mid-thigh girth and more fatigue on the Chalder Fatigue Scale than euthyroid control subjects. The scTox-Tr group had an increase in muscle mass, reduction in the variables reflecting whole body fat, and lesser perception of fatigue during the exercise training period (p ≤ 0.05 for these parameters at the start and end of the exercise training period). scTox is associated with lower muscle mass and mid-thigh girth and more fatigue. Physical activity training can partially ameliorate these characteristics. More studies are needed to determine what training program would be optimum, both in terms of beneficial effects and for avoiding potential adverse responses.
Characterization and damage evaluation of advanced materials

NASA Astrophysics Data System (ADS)

Mitrovic, Milan

Mechanical characterization of advanced materials, namely magnetostrictive and graphite/epoxy composite materials, is studied in this dissertation, with an emphasis on damage evaluation of composite materials. Consequently, the work in this dissertation is divided into two parts, with the first part focusing on characterization of the magneto-elastic response of magnetostrictlve materials, while the second part of this dissertation describes methods for evaluating the fatigue damage in composite materials. The objective of the first part of this dissertation is to evaluate a nonlinear constitutive relation which more closely depict the magneto-elastic response of magnetostrictive materials. Correlation between experimental and theoretical values indicate that the model adequately predicts the nonlinear strain/field relations in specific regimes, and that the currently employed linear approaches are inappropriate for modeling the response of this material in a structure. The objective of the second part of this dissertation is to unravel the complexities associated with damage events associated with polymeric composite materials. The intent is to characterize and understand the influence of impact and fatigue induced damage on the residual thermo-mechanical properties and compressive strength of composite systems. The influence of fatigue generated matrix cracking and micro-delaminations on thermal expansion coefficient (TEC) and compressive strength is investigated for woven graphite/epoxy composite system. Experimental results indicate that a strong correlation exists between TEC and compressive strength measurements, indicating that TEC measurements can be used as a damage metric for this material systems. The influence of delaminations on the natural frequencies and mode shapes of a composite laminate is also investigated. Based on the changes of these parameters as a function of damage, a methodology for determining the size and location of damage is suggested. Finally, the influence of loading parameters on impact damage growth is investigated experimentally though constant amplitude and spectrum loading fatigue tests. Based on observed impact damage growth during these tests it is suggested that the low load levels can be deleted from the standardized test sequence without significant influence on impact damage propagation.
Effects of temperature, thermal exposure, and fatigue on an alumina/aluminum composite

NASA Technical Reports Server (NTRS)

Olsen, G. C.

1980-01-01

An experimental investigation of the mechanical properties and microstructure of an aluminum matrix/polycrystalline alumina fiber composite material is discussed. The effects of fabrication, isothermal exposure (up to 10,000 hours at 590 K), thermal cycling (6000 cycles between 200 K and 590 K), fatigue (1,000,000 tension-tension cycles) were determined by mechanical testing and metallurgical analysis. The fabrication process severely degraded the fiber strength by reducing the alumina to a nonstoichiometric form and quenching in the resultant vacancies and stress fields. However, isothermal exposure, thermal cycling, and fatigue cycling all restored the fiber strength by enhancing vacancy annihilation. Comparison of the as-fabricated material with other aerospace materials shows that it is an attractive candidate for select applications. Long duration isothermal exposure weakened the matrix by overaging and through the diffusional loss of lithium to a surface reaction forming lithium carbonate. Thermal cycling initiated cracks in the matrix and fibers. Tension-tension fatigue cycling caused no apparent damage to the as-fabricated material but in fact, strengthened it to the rule-of-mixtures value. Fatigue cycling after thermal exposure did have a cumulative damage effect.
Study on the Effect of Secondary Banded Structure on the Fatigue Property of Non-Quenched and Tempered Micro Alloyed Steel

NASA Astrophysics Data System (ADS)

Yajie, Cheng; Qingliang, Liao; Yue, Zhang

Due to composition segregation and cooling speed, streamline or banded structure were often obtained in the thermal forming parts along the direction of parts forming. Generally speaking, banded structure doesn't decrease the longitudinal mechanical properties, so the secondary banded structure can't get enough attention. The effect of secondary banded structure on the fatigue properties of micro alloyed DG20Mn and 35CrMo steel was investigated using the axial tensile fatigue test of stress ratio of 0.1. The result shows that secondary banded structure was obtained in the center of the steel parts, because of the composition segregation and the lower cooling rate in center part of steel. Secondary banded structure has no significant effect on axial tensile properties of both DG20Mn and 35CrMo, but decreases the axial tensile fatigue performance of DG20Mn steel. This study suggests that under the high cyclic tensile stress, multi-source damage cracks in steel initiated by large strain of pearlite of secondary banded structure, which is larger than damage strain, is the major factor of the decrease of fatigue life of steel.
Fatigue behavior of thin-walled grade 2 titanium samples processed by selective laser melting. Application to life prediction of porous titanium implants.

PubMed

Lipinski, P; Barbas, A; Bonnet, A-S

2013-12-01

Because of its biocompatibility and high mechanical properties, the commercially pure grade 2 titanium (CPG2Ti) is largely used for fabrication of patient specific implants or hard tissue substitutes with complex shape. To avoid the stress-shielding and help their colonization by bone, prostheses with a controlled porosity are designed. The selective laser melting (SLM) is well adapted to manufacture such geometrically complicated structures constituted by struts with rough surfaces and relatively small diameters. Few studies were dedicated to characterize the fatigue properties of SLM processed samples and bulk parts. They followed conventional or standard protocols. The fatigue behavior of standard samples is very different from the one of porous raw structures. In this study, the SLM made "as built" (AB) and "heat treated" (HT) tubular samples were tested in fatigue. Wöhler curves were determined in both cases. The obtained endurance limits were equal to σD(AB)=74.5MPa and σD(HT)=65.7MPa, respectively. The heat treatment worsened the endurance limit by relaxation of negative residual stresses measured on the external surface of the samples. Modified Goodman diagram was established for raw specimens. Porous samples, based on the pattern developed by Barbas et al. (2012), were manufactured by SLM. Fatigue tests and finite element simulations performed on these samples enabled the determination of a simple rule of fatigue assessment. The method based on the stress gradient appeared as the best approach to take into account the notch influence on the fatigue life of CPG2Ti structures with a controlled porosity. The direction dependent apparent fatigue strength was found. A criterion based on the effective, or global, nominal stress was proposed taking into account the anisotropy of the porous structures. Thanks to this criterion, the usual calculation methods can be used to design bone substitutes, without a precise modelling of their internal fine porosity. © 2013 Elsevier Ltd. All rights reserved.
Cyclic Fatigue Durability of Uncoated and EBC Coated 3D SiC/SiC Composites Under Thermal Gradient Conditions at 2700F in Air

NASA Technical Reports Server (NTRS)

Smith, Craig; Harder, Bryan; Zhu, Dongming; Bhatt, Ramakrishna; Kalluri, Sreeramesh

2017-01-01

Ceramic matrix composites (CMCs) such as SiCSiC are currently being designed and implemented in high temperature sections of aerospace turbine engines. Such components will be subject to through-thickness thermal gradients, which may affect the durability. In this study, SiCSiC CMCs with a hybrid chemical vapor infiltrated (CVI) and polymer infiltration and pyrolysis (PIP) matrix were loaded in tension while one surface was heated with a laser and the opposite surface was cooled. The samples were each coated with an environmental barrier coating (EBC), which was produced by electron beam physical deposition (EBPVD). Results for CMCs tested with and without the EBC be discussed.
Release of TEGDMA from composite during the chewing situation.

PubMed

Durner, J; Glasl, B; Zaspel, J; Kunzelmann, K H; Hickel, R; Reichl, F X

2010-07-01

The aim of this study was to investigate the triethylene glycol (TEGDMA) elution kinetics from light-cured composite with and without chewing simulation over a time period of 86 h. An experimental composite with TEGDMA labeled with a tracer dose of 14C-TEGDMA was used. The material parameters were in the range of commercially available composites. The mastification was simulated with the Fatigue-machine and the MUC-3 chewing simulator. 14C was eluted to 2.55% of the applied 14C-TEGDMA dose within 86 h after chewing simulation with the Fatigue-machine and to 2.60% after chewing simulation with the MUC-3. Similar 14C-kinetic data were found for 14C-elution with and without chewing simulation with the Fatigue-machine and with MUC-3. During the first 26 h after the beginning of the experiments a linear 14C-elution kinetic was observed, followed by a second linear 14C-elution kinetic with a lower slope up to 86 h in both apparatus. It could be shown that chewing simulation has no significant (p<0.05) effect on the release of 14C-TEGDMA (and/or 14C-degradation products) from polymerized composites. Copyright 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
The Effect of the More Active MuMs in Stirling Trial on Body Composition and Psychological Well-Being among Postnatal Women.

PubMed

Lee, Alyssa S; McInnes, Rhona J; Hughes, Adrienne R; Guthrie, Wendy; Jepson, Ruth

2016-01-01

Introduction. Physical activity is important for health and well-being; however, rates of postnatal physical activity can be low. This paper reports the secondary outcomes of a trial aimed at increasing physical activity among postnatal women. Methods. More Active MuMs in Stirling (MAMMiS) was a randomised controlled trial testing the effect of physical activity consultation and pram walking group intervention among inactive postnatal women. Data were collected on postnatal weight, body composition, general well-being, and fatigue. Participants were also interviewed regarding motivations and perceived benefits of participating in the trial. Results. There was no significant effect of the intervention on any weight/body composition outcome or on general well-being at three or six months of follow-up. There was a significant but inconsistent difference in fatigue between groups. Qualitative data highlighted a number of perceived benefits to weight, body composition, and particularly well-being (including improved fatigue) which were not borne out by objective data. Discussion. The MAMMiS study found no impact of the physical activity intervention on body composition and psychological well-being and indicates that further research is required to identify successful approaches to increase physical activity and improve health and well-being among postnatal women.
Accelerated fatigue testing of dentin-composite bond with continuously increasing load.

PubMed

Li, Kai; Guo, Jiawen; Li, Yuping; Heo, Young Cheul; Chen, Jihua; Xin, Haitao; Fok, Alex

2017-06-01

The aim of this study was to evaluate an accelerated fatigue test method that used a continuously increasing load for testing the dentin-composite bond strength. Dentin-composite disks (ϕ5mm×2mm) made from bovine incisor roots were subjected to cyclic diametral compression with a continuously increasingly load amplitude. Two different load profiles, linear and nonlinear with respect to the number of cycles, were considered. The data were then analyzed by using a probabilistic failure model based on the Weakest-Link Theory and the classical stress-life function, before being transformed to simulate clinical data of direct restorations. All the experimental data could be well fitted with a 2-parameter Weibull function. However, a calibration was required for the effective stress amplitude to account for the difference between static and cyclic loading. Good agreement was then obtained between theory and experiments for both load profiles. The in vitro model also successfully simulated the clinical data. The method presented will allow tooth-composite interfacial fatigue parameters to be determined more efficiently. With suitable calibration, the in vitro model can also be used to assess composite systems in a more clinically relevant manner. Copyright © 2017 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Model Determined for Predicting Fatigue Lives of Metal Matrix Composites Under Mean Stresses

NASA Technical Reports Server (NTRS)

Lerch, Bradley

1997-01-01

Aircraft engine components invariably are subjected to mean stresses over and above the cyclic loads. In monolithic materials, it has been observed that tensile mean stresses are detrimental and compressive mean stresses are beneficial to fatigue life in comparison to a base of zero mean stress. Several mean stress models exist for monolithic metals, but each differ quantitatively in the extent to which detrimental or beneficial effects are ascribed. There have been limited attempts to apply these models to metal matrix composites. At the NASA Lewis Research Center, several mean stress models--the Smith-Watson- Topper, Walker, Normalized Goodman, and Soderberg models--were examined for applicability to this class of composite materials. The Soderberg approach, which normalizes the mean stress to a 0.02-percent yield strength, was shown to best represent the effect of mean stresses over the range covered. The other models varied significantly in their predictability and often failed to predict the composite behavior at very high tensile mean stresses. This work is the first to systematically demonstrate the influence of mean stresses on metal matrix composites and model their effects. Attention also was given to fatigue-cracking mechanisms in the Ti-15-3 matrix and to micromechanics analyses of mean stress effects.
Prediction of thermal cycling induced matrix cracking

NASA Technical Reports Server (NTRS)

Mcmanus, Hugh L.

1992-01-01

Thermal fatigue has been observed to cause matrix cracking in laminated composite materials. A method is presented to predict transverse matrix cracks in composite laminates subjected to cyclic thermal load. Shear lag stress approximations and a simple energy-based fracture criteria are used to predict crack densities as a function of temperature. Prediction of crack densities as a function of thermal cycling is accomplished by assuming that fatigue degrades the material's inherent resistance to cracking. The method is implemented as a computer program. A simple experiment provides data on progressive cracking of a laminate with decreasing temperature. Existing data on thermal fatigue is also used. Correlations of the analytical predictions to the data are very good. A parametric study using the analytical method is presented which provides insight into material behavior under cyclical thermal loads.
Isothermal Damage and Fatigue Behavior of SCS-6/Timetal 21S [0/90](Sub S) Composite at 650 Deg C

NASA Technical Reports Server (NTRS)

Castelli, Michael G.

1994-01-01

The isothermal fatigue damage and life behaviors of SCS-6/Timetal 21S (0/90)s were investigated at 650 C. Strain ratcheting and degradation of the composite's static elastic modulus were carefully monitored as functions of cycles to indicate damage progression. Extensive fractographic and metallographic analyses were conducted to determine damage/failure mechanisms. Resulting fatigue lives show considerable reductions in comparison to (0) reinforced titanium matrix composites subjected to comparable conditions. Notable stiffness degradations were found to occur after the first cycle of loading, even at relatively low maximum stress levels, where cyclic lives are greater than 25,000 cycles. This was attributed to the extremely weak fiber/matrix bond which fails under relatively low transverse loads. Stiffness degradations incurred on first cycle loadings and degradations thereafter were found to increase with increasing maximum stress. Environmental effects associated with oxidation of the (90) fiber interfaces clearly played a role in the damage mechanisms as fracture surfaces revealed environment assisted matrix cracking along the (90) fibers. Metallographic analysis indicated that all observable matrix fatigue cracks initiated at the (90) fiber/matrix interfaces. Global de-bonding in the loading direction was found along the (90) fibers. No surface initiated cracks were evident and minimal if any (0) fiber cracking was visible.
Cancer-Related Fatigue and Its Associations with Depression and Anxiety: A Systematic Review

PubMed Central

Brown, Linda F.; Kroenke, Kurt

2010-01-01

Background Fatigue is an important symptom in cancer and has been shown to be associated with psychological distress. Objectives This review assesses evidence regarding associations of CRF with depression and anxiety. Methods Database searches yielded 59 studies reporting correlation coefficients or odds ratios. Results Combined sample size was 12,103. Average correlation of fatigue with depression, weighted by sample size, was 0.56 and for anxiety, 0.46. Thirty-one instruments were used to assess fatigue, suggesting a lack of consensus on measurement. Conclusion This review confirms the association of fatigue with depression and anxiety. Directionality needs to be better delineated in longitudinal studies. PMID:19855028
Composite structural materials

NASA Technical Reports Server (NTRS)

Loewy, R. G.; Wiberley, S. E.

1985-01-01

Various topics relating to composite structural materials for use in aircraft structures are discussed. The mechanical properties of high performance carbon fibers, carbon fiber-epoxy interface bonds, composite fractures, residual stress in high modulus and high strength carbon fibers, fatigue in composite materials, and the mechanical properties of polymeric matrix composite laminates are among the topics discussed.
Assessment of fatigue in rheumatoid arthritis: a psychometric comparison of single-item, multiitem, and multidimensional measures.

PubMed

Oude Voshaar, Martijn A H; Ten Klooster, Peter M; Bode, Christina; Vonkeman, Harald E; Glas, Cees A W; Jansen, Tim; van Albada-Kuipers, Iet; van Riel, Piet L C M; van de Laar, Mart A F J

2015-03-01

To compare the psychometric functioning of multidimensional disease-specific, multiitem generic, and single-item measures of fatigue in patients with rheumatoid arthritis (RA). Confirmatory factor analysis (CFA) and longitudinal item response theory (IRT) modeling were used to evaluate the measurement structure and local reliability of the Bristol RA Fatigue Multi-Dimensional Questionnaire (BRAF-MDQ), the Medical Outcomes Study Short Form-36 (SF-36) vitality scale, and the BRAF Numerical Rating Scales (BRAF-NRS) in a sample of 588 patients with RA. A 1-factor CFA model yielded a similar fit to a 5-factor model with subscale-specific dimensions, and the items from the different instruments adequately fit the IRT model, suggesting essential unidimensionality in measurement. The SF-36 vitality scale outperformed the BRAF-MDQ at lower levels of fatigue, but was less precise at moderate to higher levels of fatigue. At these levels of fatigue, the living, cognition, and emotion subscales of the BRAF-MDQ provide additional precision. The BRAF-NRS showed a limited measurement range with its highest precision centered on average levels of fatigue. The different instruments appear to access a common underlying domain of fatigue severity, but differ considerably in their measurement precision along the continuum. The SF-36 vitality scale can be used to measure fatigue severity in samples with relatively mild fatigue. For samples expected to have higher levels of fatigue, the multidimensional BRAF-MDQ appears to be a better choice. The BRAF-NRS are not recommended if precise assessment is required, for instance in longitudinal settings.
Metallurgical characterization of M-Wire nickel-titanium shape memory alloy used for endodontic rotary instruments during low-cycle fatigue.

PubMed

Ye, Jia; Gao, Yong

2012-01-01

Rotary instruments made of a new nickel-titanium (NiTi) alloy (M-Wire) have shown improved cyclic fatigue resistance and mechanical properties compared with those made of conventional superelastic NiTi wires. The objective of this study was to characterize microstructural changes of M-Wire throughout the cyclic fatigue process under controlled strain amplitude. The average fatigue life was calculated from 30 M-Wire samples that were subjected to a strain-controlled (≈ 4%) rotating bend fatigue test at room temperature and rotational speed of 300 rpm. Microstructural evolution of M-Wire has been investigated by different metallurgical characterization techniques, including differential scanning calorimetry, Vickers microhardness, and transmission electron microscopy at 4 different stages (as-received state, 30%, 60%, and 90% of average fatigue life). During rotating bend fatigue test, no statistically significant difference (P > .05) was found on austenite finish temperatures between as-received M-Wire and fatigued samples. However, significant differences (P < .05) were observed on Vickers microhardness for samples with 60% and 90% fatigue life compared with as-received and 30% fatigue life. Coincidentally, substantial growth of martensite grains and martensite twins was observed in microstructure under transmission electron microscopy after 60% fatigue life. The results of the present study suggested that endodontic instruments manufactured with M-Wire are expected to have higher strength and wear resistance than similar instruments made of conventional superelastic NiTi wires because of its unique nano-crystalline martensitic microstructure. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.
Effects of Coatings on the High-Cycle Fatigue Life of Threaded Steel Samples

NASA Astrophysics Data System (ADS)

Eder, M. A.; Haselbach, P. U.; Mishin, O. V.

2018-05-01

In this work, high-cycle fatigue is studied for threaded cylindrical high-strength steel samples coated using three different industrial processes: black oxidation, normal-temperature galvanization and high-temperature galvanization. The fatigue performance in air is compared with that of uncoated samples. Microstructural characterization revealed the abundant presence of small cracks in the zinc coating partially penetrating into the steel. This is consistent with the observation of multiple crack initiation sites along the thread in the galvanized samples, which led to crescent type fracture surfaces governed by circumferential growth. In contrast, the black oxidized and uncoated samples exhibited a semicircular segment type fracture surface governed by single-sided growth with a significantly longer fatigue life. Numerical fatigue life prediction based on an extended Paris-law formulation has been conducted on two different fracture cases: 2D axisymmetric multisided crack growth and 3D single-sided crack growth. The results of this upper-bound and lower-bound approach are in good agreement with experimental data and can potentially be used to predict the lifetime of bolted components.
Influence of the creep ageing process on the fatigue properties of components from V95pchT2 (analog 7175T76) and V95ochT2 (analog 7475) aluminium alloys

NASA Astrophysics Data System (ADS)

Larichkin, A.; Zakharchenko, K.; Gorev, B.; Kapustin, V.; Maksimovskiy, E.

2017-10-01

Influence of conditions of technological process of forming thick panels of a given geometry on fatigue limit of flat specimens from the V95ochT2 and V95pchT2 (analogues 7475 and 7175T76) alloys (Al-Mg-Cu-Zn) has been analysed. The process has been simulated experimentally on flat samples for temperatures 20, 165 and 420°C. The process includes: non-elastic strain in the range 10-5 - 10-2 s-1 up to 2% of total strain, followed by heat treatment according to T2 mode (quenching and aging). Fatigue life tests were carried out both on solid samples and on samples with a hole. It has been shown that resistance to fatigue of the observed alloys after forming at the annealing temperature (420°C) is comparable to the basic material resistance to fatigue. Meso-structure analysis showed absence of stress in grains. It is established that, on average, the shape of the grains is the same for a series of samples for different temperatures and loading rates. The results of testing samples with a hole showed that fatigue limit slightly decreases in samples which were previously deformed at (420°C), with respect to the durability of samples from the material in basic state. With an increase in rate of pre-strain, the relative number of cycles before destruction occurs increased.

Fatigue Behavior of Ultrafine-Grained 5052 Al Alloy Processed Through Different Rolling Methods

NASA Astrophysics Data System (ADS)

Yogesha, K. K.; Joshi, Amit; Jayaganthan, R.

2017-05-01

In the present study, 5052 Al alloy was processed through different rolling methods to obtain ultrafine grains and its high-cycle fatigue behavior were investigated. The solution-treated Al-Mg alloys (AA 5052) were deformed through different methods such as cryorolling (CR), cryo groove rolling (CGR) and cryo groove rolling followed by warm rolling (CGW), up to 75% thickness reduction. The deformed samples were subjected to mechanical testing such as hardness, tensile and high-cycle fatigue (HCF) test at stress control mode. The CGW samples exhibit better HCF strength when compared to other conditions. The microstructure of the tested samples was characterized by optical microscopy, SEM fractography and TEM to understand the deformation behavior of deformed Al alloy. The improvement in fatigue life of CR and CGR samples is due to effective grain refinement, subgrain formations, and high dislocation density observed in the heavily deformed samples at cryogenic condition as observed from SEM and TEM analysis. However, in case of CGW samples, formation of nanoshear bands accommodates the applied strain during cyclic loading, thereby facilitating dislocation accumulation along with subgrain formations, leading to the high fatigue life. The deformed or broken impurity phase particles found in the deformed samples along with the precipitates that were formed during warm rolling also play a prominent role in enhancing the fatigue strength. These tiny particles hindered the dislocation movement by effectively pinning it at grain boundaries, thereby improving the resistance of crack propagation under cyclic load.
Validity of the Multidimensional Fatigue Symptom Inventory-Short Form in an African American Community-Based Sample

PubMed Central

Asvat, Yasmin; Malcarne, Vanessa L.; Sadler, Georgia R.; Jacobsen, Paul B.

2014-01-01

Objectives This study examined the psychometric properties of the Multidimensional Fatigue Symptom Inventory-Short Form (MFSI-SF) in a community-based sample of African Americans. Design. A sample of 340 African Americans (116 men, 224 women) ranging in age from 18–81 years were recruited from the community (e.g., churches, health fairs, beauty salons). Participants completed a brief demographic survey, the MFSI-SF and the Positive and Negative Affect Schedule. Results The structural validity of the MFSI-SF for a community-based sample of African Americans was not supported. The five dimensions of fatigue (General, Emotional, Physical, Mental, Vigor) found for Whites in prior research were not found for African Americans in this study. Instead, fatigue, while multidimensional for African Americans, was best represented by a unique four-four profile in which general and emotional fatigue are collapsed into a single dimension and physical fatigue, mental fatigue, and vigor are relatively distinct. Hence, in the absence of modifications, the MFSI-SF cannot be considered to be structurally invariant across ethnic groups. A modified four-factor version of the MFSI-SF exhibited excellent internal consistency reliability and evidence supports its convergent validity. Using the modified four-factor version, gender and age were not meaningfully associated with MFSI-SF scores. Conclusion Future research should further examine whether modifications to the MFSI-SF would, as the findings suggest, improve its validity as a measure of multidimensional fatigue in African Americans. PMID:24527980
Research on graphite reinforced glass matrix composites

NASA Technical Reports Server (NTRS)

Prewo, K. M.; Thompson, E. R.

1980-01-01

High levels of mechanical performance in tension, flexure, fatigue, and creep loading situations of graphite fiber reinforced glass matrix composites are discussed. At test temperatures of up to 813 K it was found that the major limiting factor was the oxidative instability of the reinforcing graphite fibers. Particular points to note include the following: (1) a wide variety of graphite fibers were found to be comparable with the glass matrix composite fabrication process; (2) choice of fiber, to a large extent, controlled resultant composite performance; (3) composite fatigue performance was found to be excellent at both 300 K and 703 K; (4) composite creep and stress rupture at temperatures of up to 813 K was limited by the oxidative stability of the fiber; (5) exceptionally low values of composite thermal expansion coefficient were attributable to the dimensional stability of both matrix and fiber; and (6) component fabricability was demonstrated through the hot pressing of hot sections and brazing using glass and metal joining phases.
In-situ thermal cycling in SEM of a graphite-aluminum composite

NASA Technical Reports Server (NTRS)

Cheong, Y. M.; Marcus, H. L.

1987-01-01

In situ SEM observations of a graphite-aluminum composite (unidirectional P100 graphite-fiber-reinforced 6061 aluminum MMC plates) were used to measure displacements within the graphite fiber relative to the interface between the graphite fiber and the aluminum matrix during thermal cycling. Specimens were thermally cycled from room temperature to 300 C or 500 C in a SEM chamber and then cooled to room temperature. The obtained shear strains within the fiber were then related to anomalous values of measured residual stresses and to the impact on the composite coefficient of expansion and potential damage under thermal fatigue loading. The shear mechanism was proposed as a source of temperature limits on the low coefficient of expansion of these composites, as well as a potential source of thermal fatigue degradation.
Accelerated Aging Experiments for Prognostics of Damage Growth in Composite Materials

DTIC Science & Technology

2011-09-01

possible resource to collect such data is an accelerated aging platform. To that end this paper describes a fatigue cycling experiment with the goal to...possible resource to collect such data is an accelerated aging platform. To that end this paper describes a fatigue cycling experiment with the goal to...suffer from two damage types: matrix micro-cracks and inter- laminar delamination. When subject to fatigue loading matrix micro-cracks develop in the
Probabilistic Simulation of Combined Thermo-Mechanical Cyclic Fatigue in Composites

NASA Technical Reports Server (NTRS)

Chamis, Christos C.

2011-01-01

A methodology to compute probabilistically-combined thermo-mechanical fatigue life of polymer matrix laminated composites has been developed and is demonstrated. Matrix degradation effects caused by long-term environmental exposure and mechanical/thermal cyclic loads are accounted for in the simulation process. A unified time-temperature-stress-dependent multifactor-interaction relationship developed at NASA Glenn Research Center has been used to model the degradation/aging of material properties due to cyclic loads. The fast probability-integration method is used to compute probabilistic distribution of response. Sensitivities of fatigue life reliability to uncertainties in the primitive random variables (e.g., constituent properties, fiber volume ratio, void volume ratio, ply thickness, etc.) computed and their significance in the reliability-based design for maximum life is discussed. The effect of variation in the thermal cyclic loads on the fatigue reliability for a (0/+/-45/90)s graphite/epoxy laminate with a ply thickness of 0.127 mm, with respect to impending failure modes has been studied. The results show that, at low mechanical-cyclic loads and low thermal-cyclic amplitudes, fatigue life for 0.999 reliability is most sensitive to matrix compressive strength, matrix modulus, thermal expansion coefficient, and ply thickness. Whereas at high mechanical-cyclic loads and high thermal-cyclic amplitudes, fatigue life at 0.999 reliability is more sensitive to the shear strength of matrix, longitudinal fiber modulus, matrix modulus, and ply thickness.
Comparison between universal adhesives and two-step self-etch adhesives in terms of dentin bond fatigue durability in self-etch mode.

PubMed

Tsujimoto, Akimasa; Barkmeier, Wayne W; Takamizawa, Toshiki; Watanabe, Hidehiko; Johnson, William W; Latta, Mark A; Miyazaki, Masashi

2017-06-01

This aim of this study was to compare universal adhesives and two-step self-etch adhesives in terms of dentin bond fatigue durability in self-etch mode. Three universal adhesives - Clearfil Universal, G-Premio Bond, and Scotchbond Universal Adhesive - and three-two-step self-etch adhesives - Clearfil SE Bond, Clearfil SE Bond 2, and OptiBond XTR - were used. The initial shear bond strength and shear fatigue strength of resin composite bonded to adhesive on dentin in self-etch mode were determined. Scanning electron microscopy observations of fracture surfaces after bond strength tests were also made. The initial shear bond strength of universal adhesives was material dependent, unlike that of two-step self-etch adhesives. The shear fatigue strength of Scotchbond Universal Adhesive was not significantly different from that of two-step self-etch adhesives, unlike the other universal adhesives. The shear fatigue strength of universal adhesives differed depending on the type of adhesive, unlike those of two-step self-etch adhesives. The results of this study encourage the continued use of two-step self-etch adhesive over some universal adhesives but suggest that changes to the composition of universal adhesives may lead to a dentin bond fatigue durability similar to that of two-step self-etch adhesives. © 2017 Eur J Oral Sci.
Probabilistic Simulation for Combined Cycle Fatigue in Composites

NASA Technical Reports Server (NTRS)

Chamis, Christos C.

2010-01-01

A methodology to compute probabilistic fatigue life of polymer matrix laminated composites has been developed and demonstrated. Matrix degradation effects caused by long term environmental exposure and mechanical/thermal cyclic loads are accounted for in the simulation process. A unified time-temperature-stress dependent multifactor interaction relationship developed at NASA Glenn Research Center has been used to model the degradation/aging of material properties due to cyclic loads. The fast probability integration method is used to compute probabilistic distribution of response. Sensitivities of fatigue life reliability to uncertainties in the primitive random variables (e.g., constituent properties, fiber volume ratio, void volume ratio, ply thickness, etc.) computed and their significance in the reliability-based design for maximum life is discussed. The effect of variation in the thermal cyclic loads on the fatigue reliability for a (0/+/- 45/90)s graphite/epoxy laminate with a ply thickness of 0.127 mm, with respect to impending failure modes has been studied. The results show that, at low mechanical cyclic loads and low thermal cyclic amplitudes, fatigue life for 0.999 reliability is most sensitive to matrix compressive strength, matrix modulus, thermal expansion coefficient, and ply thickness. Whereas at high mechanical cyclic loads and high thermal cyclic amplitudes, fatigue life at 0.999 reliability is more sensitive to the shear strength of matrix, longitudinal fiber modulus, matrix modulus, and ply thickness.
Thermomechanical and isothermal fatigue behavior of a (90)sub 8 titanium matrix composite

NASA Technical Reports Server (NTRS)

Castelli, Michael G.

1993-01-01

An experimental investigation was conducted to analyze the fatigue damage mechanisms operative in a 35 fiber volume percent (90 deg) titanium matrix composite (TMC) under 427 C isothermal and thermomechanical loading conditions. The thermomechanical fatigue (TMF) tests were performed with a temperature cycle from 200 to 427 C under closely controlled conditions to define both the deformation and fatigue life behavior. Degradation of the TMC's isothermal elastic moduli and coefficient of thermal expansion were monitored throughout the TMF tests. The results indicated TMF life trends which contrasted those established in a comparable (0 deg) system, as TMF loading of the (90 deg) TMC was not found to be 'life-limiting' in comparison to maximum temperature isothermal conditions. In-phase lives were very similar to those established under 427 C isothermal conditions. High stress isothermal fatigue at 427 C produced increased strain ratchetting and stiffness degradation relative to TMF conditions. Out-of-phase loadings produced TMF lives approximately an order of magnitude greater than the lives determined under isothermal and in-phase conditions. Extensive fractography and metallography were also performed. Two key issues were identified and appeared to dominate the fatigue damage and life of the (90 deg) TMC, namely, the weak fiber/matrix interface and environmental attack of the fiber/matrix interface via the exposed (90 deg) fiber ends.
Probabilistic Simulation of Combined Thermo-Mechanical Cyclic Fatigue in Composites

NASA Technical Reports Server (NTRS)

Chamis, Christos C.

2010-01-01

A methodology to compute probabilistically-combined thermo-mechanical fatigue life of polymer matrix laminated composites has been developed and is demonstrated. Matrix degradation effects caused by long-term environmental exposure and mechanical/thermal cyclic loads are accounted for in the simulation process. A unified time-temperature-stress-dependent multifactor-interaction relationship developed at NASA Glenn Research Center has been used to model the degradation/aging of material properties due to cyclic loads. The fast probability-integration method is used to compute probabilistic distribution of response. Sensitivities of fatigue life reliability to uncertainties in the primitive random variables (e.g., constituent properties, fiber volume ratio, void volume ratio, ply thickness, etc.) computed and their significance in the reliability-based design for maximum life is discussed. The effect of variation in the thermal cyclic loads on the fatigue reliability for a (0/+/-45/90)s graphite/epoxy laminate with a ply thickness of 0.127 mm, with respect to impending failure modes has been studied. The results show that, at low mechanical-cyclic loads and low thermal-cyclic amplitudes, fatigue life for 0.999 reliability is most sensitive to matrix compressive strength, matrix modulus, thermal expansion coefficient, and ply thickness. Whereas at high mechanical-cyclic loads and high thermal-cyclic amplitudes, fatigue life at 0.999 reliability is more sensitive to the shear strength of matrix, longitudinal fiber modulus, matrix modulus, and ply thickness.
Effect of Cyclic Thermo-Mechanical Loads on Fatigue Reliability in Polymer Matrix Composites

NASA Technical Reports Server (NTRS)

Shah, A. R.; Murthy, P. L. N.; Chamis, C. C.

1996-01-01

A methodology to compute probabilistic fatigue life of polymer matrix laminated composites has been developed and demonstrated. Matrix degradation effects caused by long term environmental exposure and mechanical/thermal cyclic loads are accounted for in the simulation process. A unified time-temperature-stress dependent multi-factor interaction relationship developed at NASA Lewis Research Center has been used to model the degradation/aging of material properties due to cyclic loads. The fast probability integration method is used to compute probabilistic distribution of response. Sensitivities of fatigue life reliability to uncertainties in the primitive random variables (e.g., constituent properties, fiber volume ratio, void volume ratio, ply thickness, etc.) computed and their significance in the reliability- based design for maximum life is discussed. The effect of variation in the thermal cyclic loads on the fatigue reliability for a (0/+/- 45/90)(sub s) graphite/epoxy laminate with a ply thickness of 0.127 mm, with respect to impending failure modes has been studied. The results show that, at low mechanical cyclic loads and low thermal cyclic amplitudes, fatigue life for 0.999 reliability is most sensitive to matrix compressive strength, matrix modulus, thermal expansion coefficient, and ply thickness. Whereas at high mechanical cyclic loads and high thermal cyclic amplitudes, fatigue life at 0.999 reliability is more sensitive to the shear strength of matrix, longitudinal fiber modulus, matrix modulus, and ply thickness.
Chronicity and remission of fatigue in patients with established HIV infection.

PubMed

Pence, Brian Wells; Barroso, Julie; Harmon, James L; Leserman, Jane; Salahuddin, Naima; Hammill, Bradley G

2009-04-01

Fatigue is one of the most common and debilitating complaints of HIV-positive individuals, potentially leading to important functional limitations. We recruited 128 HIV-positive individuals (fatigued and nonfatigued) between March 2005 and May 2006; 66% were male, 66% were African American, 45% had greater than a high school education, 67% were unemployed, and ages ranged from 26-66 (median, 44). Every 3 months for 15 months, participants completed a 56-item self-report fatigue scale developed and validated by the authors. Participants were classified as fatigued or not fatigued at each assessment and received scores for fatigue intensity and impact of fatigue on functioning. We used linear mixed-effects models to assess longitudinal variation in fatigue scores and generalized estimating equations for binary outcomes to model predictors of fatigue remission among those fatigued at baseline. At baseline, 88% of the sample was fatigued. Fatigue measures were highly correlated across time points (rho 0.63-0.85 [intensity], 0.63-0.80 [functioning]) and showed no evidence of overall improvement, deterioration, or convergence over time. Predictors of lower fatigue scores included higher income, employment, longer time since HIV diagnosis, and antiretroviral therapy use. Those employed at baseline were likely to show improvements in fatigue while those unemployed were not. Of those fatigued at baseline, 11% experienced remission during follow-up; remission was associated with Caucasian race and employment. In summary, fatigue intensity and related functional limitations were persistent, stable, and unlikely to remit over 15 months of follow-up in this sample of patients with established HIV infection.
Investigation of damage mechanisms in a cross-ply metal-matrix composite under thermomechanical loading. Master's thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Schubbe, J.J.

1990-12-01

Metal matrix composites (MMCs) are rapidly becoming strong candidates for high temperature and high stiffness structural applications such as the Advanced Tactical Fighter (ATF). This study systematically investigated the failure modes and associated damage in a cross-ply, (0/90)2s SCS6/Ti-15-3 metal matrix composite under in-phase and out-of-phase thermomechanic fatigue. Initiation and progression of fatigue damage were recorded and correlated to changes in Young's Modulus of the composite material. Experimental results show an internal stabilization of reaction zone size but degradation and separation from constituent materials under extended cyclic thermal loading. Critical to damage were transverse cracks initiating in the 90 degreesmore » plies, growing and coalescing from fiber/matrix interfaces internal to the specimen, progressing outward through the 0 degree plies before failure. Maximum mechanical strain at failure was determined to be approximately 0.0075 mm/mm. A correlation was made relating maximum matrix stress to failure life, resulting in a fatigue threshold limit of 280 MPa. An attempt was made to correlate the degradation in Young's Modulus (Damage=1-E/Eo) with the applied life cycles from different TMF tests.« less
Microstructural evaluation of cumulative fatigue damage in a plant component sample

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuoka, C.; Nakagawa, Y.G.; Yoshida, K.

1996-12-31

Fatigue damage accumulated in a real plant was evaluated in terms of microstructural conditioning. Microstructural damage induced in laboratory by cyclic deformation near and below the fatigue limit was also examined. A Transmission Electron Microscopy (TEM) technique called the Selected Area Diffraction (SAD) method was employed in this study. In earlier studies, it was found that the SAD value indicating a magnitude of crystallographic misorientation in the substructure (dislocation cells) was increasing with the increase of fatigue damage accumulation. Small samples removed from PWR feed water nozzle welds were examined by the SAD. It was found that the damage statemore » measured by the SAD well agreed with the morphological evidence. Cyclic stresses near or below the fatigue limit were applied to samples taken from a SA508 steel plate at various stresses. The SAD value increased even below the fatigue limit, but there was no sign of microstructural conditioning below the stresses of 50% of the fatigue limit. These results suggested that at stresses below the current design curve (below half the fatigue limit) no microstructural conditioning proceeded. It was concluded that the microstructural method was effective to evaluate damage accumulation in real plant components, and also that the current design curve was adequate in terms of microstructural conditioning state.« less
Fast prediction of the fatigue behavior of short-fiber-reinforced thermoplastics based on heat build-up measurements: application to heterogeneous cases

NASA Astrophysics Data System (ADS)

Serrano, Leonell; Marco, Yann; Le Saux, Vincent; Robert, Gilles; Charrier, Pierre

2017-09-01

Short-fiber-reinforced thermoplastics components for structural applications are usually very complex parts as stiffeners, ribs and thickness variations are used to compensate the quite low material intrinsic stiffness. These complex geometries induce complex local mechanical fields but also complex microstructures due to the injection process. Accounting for these two aspects is crucial for the design in regard to fatigue of these parts, especially for automotive industry. The aim of this paper is to challenge an energetic approach, defined to evaluate quickly the fatigue lifetime, on three different heterogeneous cases: a classic dog-bone sample with a skin-core microstructure and two structural samples representative of the thickness variations observed for industrial components. First, a method to evaluate dissipated energy fields from thermal measurements is described and is applied to the three samples in order to relate the cyclic loading amplitude to the fields of cyclic dissipated energy. Then, a local analysis is detailed in order to link the energy dissipated at the failure location to the fatigue lifetime and to predict the fatigue curve from the thermomechanical response of one single sample. The predictions obtained for the three cases are compared successfully to the Wöhler curves obtained with classic fatigue tests. Finally, a discussion is proposed to compare results for the three samples in terms of dissipation fields and fatigue lifetime. This comparison illustrates that, if the approach is leading to a very relevant diagnosis on each case, the dissipated energy field is not giving a straightforward access to the lifetime cartography as the relation between fatigue failure and dissipated energy seems to be dependent on the local mechanical and microstructural state.
Relation between the fracture laws and the fatigue life of a surface-hardened pseudo-α titanium alloy

NASA Astrophysics Data System (ADS)

Bagmutov, V. P.; Vodop'yanov, V. I.; Zakharov, I. N.; Denisevich, D. S.

2016-07-01

The laws of fracture and fatigue life of the PT-3V pseudo-α titanium alloy subjected to surface hardening using electromechanical, ultrasonic, and combined treatment are studied. Fracture mechanisms and the structures of crack nucleation and growth zones are described using the results of metallographic and fractographic analysis of samples after fatigue tests. It is shown that the existence of a thin hardened layer on the sample surface changes the crack nucleation time and the state of fracture surface in the crack nucleation zone. This surface is characterized by signs of brittle or ductile fracture, which substantially affects the fatigue life of the sample.
Cyclic debonding of adhesively bonded composites

NASA Technical Reports Server (NTRS)

Mall, S.; Johnson, W. S.; Everett, R. A., Jr.

1982-01-01

The fatigue behavior of a simple composite to composite bonded joint was analyzed. The cracked lap shear specimen subjected to constant amplitude cyclic loading was studied. Two specimen geometries were tested for each bonded system: (1) a strap adherend of 16 plies bonded to a lap adherend of 8 plies; and (2) a strap adherend of 8 plies bonded to a lap adherend of 16 plies. In all specimens the fatigue failure was in the form of cyclic debonding with some 0 deg fiber pull off from the strap adherend. The debond always grew in the region of adhesive that had the highest mode (peel) loading and that region was close to the adhesive strap interface.
Self-Repairing Fatigue Damage in Metallic Structures for Aerospace Vehicles Using Shape Memory Alloy Self-healing (SMASH) Technology

NASA Technical Reports Server (NTRS)

Wright, M. Clara; Manuel, Michele; Wallace, Terryl; Newman, Andy; Brinson, Kate

2015-01-01

This DAA is for the Phase II webinar presentation of the ARMD-funded SMASH technology. A self-repairing aluminum-based composite system has been developed using liquid-assisted healing theory in conjunction with the shape memory effect of wire reinforcements. The metal matrix composite was thermodynamically designed to have a matrix with a relatively even dispersion of low-melting phase, allowing for repair of cracks at a pre-determined temperature. Shape memory alloy wire reinforcements were used within the composite to provide crack closure. Investigators focused the research on fatigue cracks propagating through the matrix in order to optimize and computer model the SMASH technology for aeronautical applications.
Fatigue of notched fiber composite laminates. Part 2: Analytical and experimental evaluation

NASA Technical Reports Server (NTRS)

Kulkarni, S. V.; Mclaughlin, P. V., Jr.; Pipes, R. B.

1976-01-01

The analytical/experimental correlation study was performed to develop an understanding of the behavior of notched Boron/epoxy laminates subjected to tension/tension fatigue loading. It is postulated that the fatigue induced property changes (stiffness as well as strength) of the laminate can be obtained from the lamina fatigue properties. To that end, the Boron/epoxy lamina static and fatigue data (lifetime, residual stiffness and strength) were obtained initially. The longitudinal and transverse tension data were determined from the (0) and (90) laminate tests while the in-plane shear data were obtained from the (+ or - 45) sub s laminates. The static tests obtained the notched strength and mode of failure while the fatigue tests determined lifetime, damage propagation and residual strength. The failure in static tension occurred in a transverse crack propagation mode.
A randomised controlled trial testing the feasibility and efficacy of a physical activity behavioural change intervention in managing fatigue with gynaecological cancer survivors.

PubMed

Donnelly, C M; Blaney, J M; Lowe-Strong, A; Rankin, J P; Campbell, A; McCrum-Gardner, E; Gracey, J H

2011-09-01

To determine the feasibility and efficacy of a physical activity behavioural change intervention in managing cancer-related fatigue among gynaecological cancer survivors during and post anti-cancer treatments. A two arm, single blind, randomised controlled trial was conducted within the Northern Ireland regional Cancer Centre. Thirty three sedentary gynaecological cancer survivors (stage I-III; ≤3 years post diagnosis), experiencing cancer-related fatigue (mild-severe) took part. Participants were randomly assigned to a behavioural change, moderate intensity physical activity intervention (n=16) or a Contact Control group (n=17). The primary outcome was fatigue (Multidimensional Fatigue Symptom Inventory-Short Form and Functional Assessment in Chronic Illness Therapy-Fatigue subscale). Secondary outcomes included quality of life, physical functioning, positive and negative affect, depression, body composition, sleep dysfunction and self-reported physical activity. Feasibility was assessed based on the recruitment rate, programme and physical activity adherence and participants' programme evaluation, including optional focus groups (n=16). Twenty five percent of eligible women took part (33/134). Participants were 8.7 (SD=9.1) months post diagnosis, with a mean age of 53 (SD=10.3) years. The majority of the sample had a diagnosis of ovarian (n=12) or endometrial cancer (n=11). Significant differences favouring the intervention group were observed for fatigue at 12 weeks and 6 months follow-up (12 week: mean difference=-11.06; 95% confidence interval (CI)=-21.89 to -0.23; effect size (d)=0.13; p=0.046; 6 month: mean difference=-19.48; 95% CI=-19.67 to -19.15; effect size (d)=0.20; p=0.01). A mean of 10 calls (SD=1.2 calls) were delivered to the Physical Activity Group, and 10 (SD=1.6 calls) to the CC group. The intervention was positively perceived based on exit questionnaire and focus group findings. A physical activity behavioural change intervention for gynaecological cancer survivors is feasible in terms of participants' programme adherence and evaluation, and the intervention demonstrates improvements in fatigue. However, confirmation in the form of a larger fully powered RCT is warranted. Copyright © 2011 Elsevier Inc. All rights reserved.

LH2 on-orbit storage tank support trunnion design and verification

NASA Technical Reports Server (NTRS)

Bailey, W. J.; Fester, D. A.; Toth, J. M., Jr.

1985-01-01

A detailed fatigue analysis was conducted to provide verification of the trunnion design in the reusable Cryogenic Fluid Management Facility for Shuttle flights and to assess the performance capability of the trunnion E-glass/S-glass epoxy composite material. Basic material property data at ambient and liquid hydrogen temperatures support the adequacy of the epoxy composite for seven-mission requirement. Testing of trunnions fabricated to the flight design has verified adequate strength and fatigue properties of the design to meet the requirements of seven Shuttle flights.
Design and fabrication of composite wing panels containing a production splice

NASA Technical Reports Server (NTRS)

Reed, D. L.

1975-01-01

Bolted specimens representative of both upper and lower wing surface splices of a transport aircraft were designed and manufactured for static and random load tension and compression fatigue testing including ground-air-ground load reversals. The specimens were fabricated with graphite-epoxy composite material. Multiple tests were conducted at various load levels and the results were used as input to a statistical wearout model. The statically designed specimens performed very well under highly magnified fatigue loadings. Two large panels, one tension and compression, were fabricated for testing by NASA-LRC.
Design solutions for the solar cell interconnect fatigue fracture problem

NASA Technical Reports Server (NTRS)

Mon, G. R.; Ross, R. G., Jr.

1982-01-01

Mechanical fatigue of solar cell interconnects is a major failure mechanism in photovoltaic arrays. A comprehensive approach to the reliability design of interconnects, together with extensive design data for the fatigue properties of copper interconnects, has been published. This paper extends the previous work, developing failure prediction (fatigue) data for additional interconnect material choices, including aluminum and a variety of copper-Invar and copper-steel claddings. An improved global fatigue function is used to model the probability-of-failure statistics of each material as a function of level and number of cycles of applied strain. Life-cycle economic analyses are used to evaluate the relative merits of each material choce. The copper-Invar clad composites demonstrate superior performance over pure copper. Aluminum results are disappointing.
Graphene nano-devices and nano-composites for structural, thermal and sensing applications

NASA Astrophysics Data System (ADS)

Yavari, Fazel

In this dissertation we have developed graphene-based nano-devices for applications in integrated circuits and gas sensors; as well as graphene-based nano-composites for applications in structures and thermal management. First, we have studied the bandgap of graphene for semiconductor applications. Graphene as a zero-bandgap material cannot be used in the semiconductor industry unless an effective method is developed to open the bandgap in this material. We have demonstrated that a bandgap of 0.206 eV can be opened in graphene by adsorption of water vapor molecules on its surface. Water molecules break the molecular symmetries of graphene resulting in a significant bandgap opening. We also illustrate that the lack of bandgap in graphene can be used to our advantage by making sensors that are able to detect low concentrations of gas molecules mixed in air. We have shown that 1-2 layers of graphene synthesized by chemical vapor deposition enables detection of trace amounts of NO 2 and NH3 in air at room temperature and atmospheric pressure. The gas species are detected by monitoring changes in electrical resistance of the graphene film due to gas adsorption. The sensor response time is inversely proportional to the gas concentration. Heating the film expels chemisorbed molecules from the graphene surface enabling reversible operation. The detection limits of ~100 parts-per-billion (ppb) for NO2 and ~500 ppb for NH3 obtained using this device are markedly superior to commercially available NO2 and NH3 detectors. This sensor is fabricated using individual graphene sheets that are exquisitely sensitive to the chemical environment. However, the fabrication and operation of devices that use individual nanostructures for sensing is complex, expensive and suffers from poor reliability due to contamination and large variability from sample-to-sample. To overcome these problems we have developed a gas sensor based on a porous 3D network of graphene sheets called graphene foam that is macroscopic and easy to mass produce. The walls of the foam are comprised of a few layers of graphene sheets resulting in high sensitivity. We demonstrate parts-per-million (ppm) level detection of NH3 and NO2 in air at room-temperature using this sensor. Further, the foam is a mechanically robust and flexible macro-scale network that is easy to contact (without lithography) and can rival the durability and affordability of traditional sensors. Moreover, Joule-heating expels chemisorbed molecules from the foam’s surface leading to fully-reversible and low-power operation. In the second part of this dissertation the focus is on graphene platelets and their incorporation into polymer matrices to improve their mechanical and thermal properties. We demonstrate the synthesis and fatigue characterization of fiberglass/epoxy composites with various weight fractions of graphene platelets infiltrated into the epoxy resin as well as directly spray-coated on to the glass micro-fibers. Remarkably, only ~0.2wt.% of graphene additives enhances the fatigue life of the composite in the flexural bending mode by up to 1200-fold. By contrast, under uniaxial tensile fatigue conditions, the graphene fillers resulted in ~3 to 5-fold increase in fatigue life. In-situ ultrasound analysis of the nanocomposite during the cyclic fatigue test suggests that the graphene network toughens the fiberglass/epoxy-matrix interface and prevents the delamination/buckling of the glass micro-fibers under compressive stress. Such fatigue-resistant hierarchical materials show potential to improve the safety, reliability, and cost-effectiveness of fiber-reinforced composites that are increasingly the material of choice in the aerospace, automotive, marine, sports, bio-medical and wind energy industries. We also investigated the effect of graphene platelets on thermal properties of Graphene/1-Octadecanol composite as a nano-structured phase change material (PCM) for energy storage applications. The liquid-solid phase change enthalpy, crystallization, and thermal conductivity of this composite were studied as a function of graphene content. The thermal conductivity (κ) of the nanocomposite increased by nearly 2.5-fold (~140% increase) upon ~4wt. % graphene addition while the drop in the heat of fusion (i.e. storage capacity) was only ~15.4%. The enhancement in thermal properties of 1-Octadecanol obtained with the addition of graphene is markedly superior to the effect of other nanofillers such as silver nanowires and carbon nanotubes reported previously in the literature. Boosting the thermal conductivity of organic PCMs without incurring a significant loss in the heat of fusion is one of the key issues in enabling their practical application as latent heat storage/release units for thermal management and thermal protection.
Unprecedented simultaneous enhancement in damage tolerance and fatigue resistance of zirconia/Ta composites

NASA Astrophysics Data System (ADS)

Smirnov, A.; Beltrán, J. I.; Rodriguez-Suarez, T.; Pecharromán, C.; Muñoz, M. C.; Moya, J. S.; Bartolomé, J. F.

2017-03-01

Dense (>98 th%) and homogeneous ceramic/metal composites were obtained by spark plasma sintering (SPS) using ZrO2 and lamellar metallic powders of tantalum or niobium (20 vol.%) as starting materials. The present study has demonstrated the unique and unpredicted simultaneous enhancement in toughness and strength with very high flaw tolerance of zirconia/Ta composites. In addition to their excellent static mechanical properties, these composites also have exceptional resistance to fatigue loading. It has been shown that the major contributions to toughening are the resulting crack bridging and plastic deformation of the metallic particles, together with crack deflection and interfacial debonding, which is compatible with the coexistence in the composite of both, strong and weak ceramic/metal interfaces, in agreement with predictions of ab-initio calculations. Therefore, these materials are promising candidates for designing damage tolerance components for aerospace industry, cutting and drilling tools, biomedical implants, among many others.
Thermal-mechanical fatigue test apparatus for metal matrix composites and joint attachments

NASA Technical Reports Server (NTRS)

Westfall, L. J.; Petrasek, D. W.

1985-01-01

Two thermal-mechanical fatigue (TMF) test facilities were designed and developed, one to test tungsten fiber reinforced metal matrix composite specimens at temperature up to 1430C (2600F) and another to test composite/metal attachment bond joints at temperatures up to 760C (1400 F). The TMF facility designed for testing tungsten fiber reinforced metal matrix composites permits test specimen temperature excursions from room temperature to 1430C (2600F) with controlled heating and loading rates. A strain-measuring device measures the strain in the test section of the specimen during each heating and cooling cycle with superimposed loads. Data is collected and recorded by a computer. The second facility is designed to test composite/metal attachment bond joints and to permit heating to a maximum temperature of 760C (1400F) within 10 min and cooling to 150C (300F) within 3 min. A computer controls specimen temperature and load cycling.
Unprecedented simultaneous enhancement in damage tolerance and fatigue resistance of zirconia/Ta composites

PubMed Central

Smirnov, A.; Beltrán, J. I.; Rodriguez-Suarez, T.; Pecharromán, C.; Muñoz, M. C.; Moya, J. S.; Bartolomé, J. F.

2017-01-01

Dense (>98 th%) and homogeneous ceramic/metal composites were obtained by spark plasma sintering (SPS) using ZrO2 and lamellar metallic powders of tantalum or niobium (20 vol.%) as starting materials. The present study has demonstrated the unique and unpredicted simultaneous enhancement in toughness and strength with very high flaw tolerance of zirconia/Ta composites. In addition to their excellent static mechanical properties, these composites also have exceptional resistance to fatigue loading. It has been shown that the major contributions to toughening are the resulting crack bridging and plastic deformation of the metallic particles, together with crack deflection and interfacial debonding, which is compatible with the coexistence in the composite of both, strong and weak ceramic/metal interfaces, in agreement with predictions of ab-initio calculations. Therefore, these materials are promising candidates for designing damage tolerance components for aerospace industry, cutting and drilling tools, biomedical implants, among many others. PMID:28322343
Thermal-mechanical fatigue test apparatus for metal matrix composites and joint attachments

NASA Technical Reports Server (NTRS)

Westfall, Leonard J.; Petrasek, Donald W.

1988-01-01

Two thermal-mechanical fatigue (TMF) test facilities were designed and developed, one to test tungsten fiber reinforced metal matrix composite specimens at temperature up to 1430C (2600F) and another to test composite/metal attachment bond joints at temperatures up to 760F (1400F). The TMF facility designed for testing tungsten fiber reinforced metal matrix composites permits test specimen temperature excursions from room temperature to 1430C (2600F) with controlled heating and loading rates. A strain-measuring device measures the strain in the test section of the specimen during each heating and cooling cycle with superimposed loads. Data is collected and recorded by a computer. The second facility is designed to test composite/metal attachment bond joints and to permit heating to a maximum temperature of 760C (1400F) within 10 min and cooling to 150C (300F) within 3 min. A computer controls specimen temperature and load cycling.
The effects of embedded piezoelectric fiber composite sensors on the structural integrity of glass-fiber-epoxy composite laminate

NASA Astrophysics Data System (ADS)

Konka, Hari P.; Wahab, M. A.; Lian, K.

2012-01-01

Piezoelectric fiber composite sensors (PFCSs) made from micro-sized lead zirconate titanate (PZT) fibers have many advantages over the traditional bulk PZT sensors for embedded sensor applications. PFCSs as embedded sensors will be an ideal choice to continuously monitor the stress/strain levels and health conditions of composite structures. PFCSs are highly flexible, easily embeddable, have high compatibility with composite structures, and also provides manufacturing flexibility. This research is focused on examining the effects of embedding PFCS sensors (macro-fiber composite (MFC) and piezoelectric fiber composite (PFC)) on the structural integrity of glass-fiber-epoxy composite laminates. The strengths of composite materials with embedded PFCSs and conventional PZT sensors were compared, and the advantages of PFCS sensors over PZTs were demonstrated. Initially a numerical simulation study is performed to understand the local stress/strain field near the embedded sensor region inside a composite specimen. High stress concentration regions were observed near the embedded sensor corner edge. Using PFCS leads to a reduction of 56% in longitudinal stress concentration and 38% in transverse stress concentration, when compared to using the conventional PZTs as embedded sensors. In-plane tensile, in-plane tension-tension fatigue, and short beam strength tests are performed to evaluate the strengths/behavior of the composite specimens containing embedded PFCS. From the tensile test it is observed that embedding PFCS and PZT sensors in the composite structures leads to a reduction in ultimate strength by 3 and 6% respectively. From the fatigue test results it is concluded that both embedded PFCS and PZT sensors do not have a significant effect on the fatigue behavior of the composite specimens. From the short beam strength test it is found that embedding PFCS and PZT sensors leads to a reduction in shear strength by 7 and 15% respectively. Overall the pure PZT sensors seem to have low compatibility with composites when compared to PFCSs.
The fatigue experience for women with human immunodeficiency virus.

PubMed

Lee, K A; Portillo, C J; Miramontes, H

1999-01-01

To examine fatigue as a symptom experienced by women with human immunodeficiency virus (HIV). A convenience sample of 100 women with HIV. Independent sample t-tests were used to test for mean differences in fatigue related to variables in the women's sociocultural and home environment (ethnicity, employment, marital status, and parenting). Pearson product moment correlations were used to examine significant relationships between fatigue and physiologic variables (age, CD4 cell count, and sleep). Lower CD4 cell counts were related to more daytime sleep, higher evening fatigue, and higher morning fatigue. Morning fatigue was related to duration of wake episodes during the night, napping, and perception of sleep disturbance during the past week. The number of awakenings during the first night predicted the severity of fatigue the next evening. To understand the fatigue experienced by women with HIV, researchers and clinicians must focus on the relative contributions of sociocultural, home, and physiologic environments within which these women live. Additional research is ongoing to identify the strategies these women use to manage daily activities such that gender-relevant and culturally relevant interventions for alleviating fatigue can be tested in women with a variety of chronic illnesses, including HIV and acquired immune deficiency syndrome.
Fatigue in HIV-Infected People: A Three-Year Observational Study

PubMed Central

Barroso, Julie; Leserman, Jane; Harmon, James L.; Hammill, Bradley; Pence, Brian W.

2015-01-01

Context HIV-related fatigue remains the most frequent complaint of seropositive patients. Objectives To describe the natural course of fatigue in HIV infection, in a sample (n=128) followed for a three-year period. Methods A longitudinal prospective design was used to determine what factors influenced changes in fatigue intensity and fatigue-related impairment of functioning in a community-dwelling sample of HIV-infected individuals. Participants were followed every six months for a three-year period. At each study visit, we collected data on a large number of physiological and psychosocial markers that have been shown to be related to fatigue in HIV-infected people. At three-month intervals between study visits, we collected data on fatigue via mailed questionnaires. Results Fatigue in HIV infection is largely a result of stressful life events, and is closely tied to the anxiety and depression that accompany such events. Fatigue did not remit spontaneously over the course of the study, indicating the need for interventions to ameliorate this debilitating symptom. Conclusion Intervening to help people who are suffering from HIV-related fatigue to deal with stressful life events may help to ameliorate this debilitating symptom. PMID:25701691
Fatigue Moderates the Relationship Between Perceived Stress and Suicidal Ideation: Evidence From Two High-Resolution Studies.

PubMed

Kleiman, Evan M; Turner, Brianna J; Chapman, Alexander L; Nock, Matthew K

2018-01-01

Theoretical models of self-harm suggest that high perceived stress and high fatigue (which might affect the ability to cope with stress) may interact to predict the short-term occurrence of suicidal ideation and nonsuicidal self-injury (NSSI). We tested 3 approaches to examining this interaction, each of which provided a different understanding of the specific nature of these associations: comparing each individual's daily stress/fatigue to the entire sample's overall average (i.e., grand-mean centering), comparing each individual's daily perceived stress/fatigue to his or her overall average (i.e., group- or participant-mean centering), and comparing each individual's average perceived stress/fatigue to the sample's overall average (i.e., centering participant means on overall grand mean). In 2 studies, adolescents (n = 30; 574 daily reports, M age = 17.3 years, range = 12-19; 87.6% female) and young adults (n = 60; 698 daily reports; M age = 23.25 years, range = 18-35; 85% female) completed daily measures of perceived stress, fatigue, suicidal ideation, and NSSI. In both samples, the interaction between high daily perceived stress and high daily fatigue predicted greater odds of daily suicidal ideation (but not NSSI). Only the model comparing each individual's daily stress/fatigue to the entire sample's overall average was consistently significant across the two studies. Participants were most likely to experience suicidal ideation on days when both perceived stress and fatigue were elevated relative to the average level experienced across people and time points. Studies should build upon these findings with more in-depth examination of the temporal nature of stability and change in these factors as they relate to sustained suicidal ideation.
Subjective Fatigue in Children With Hearing Loss: Some Preliminary Findings

PubMed Central

Hornsby, Benjamin W. Y.; Werfel, Krystal; Camarata, Stephen; Bess, Fred H.

2014-01-01

Purpose In this study, the authors examined the effect of hearing loss on subjective reports of fatigue in school-age children using a standardized measure. Methods As part of a larger ongoing study, the authors obtained subjective ratings of fatigue using the Pediatric Quality of Life Inventory (PedsQL) Multidimensional Fatigue Scale (Varni, Burwinkle, Katz, Meeske, & Dickinson, 2002). This standardized scale provides a measure of general fatigue, sleep/rest fatigue, cognitive fatigue, and an overall composite measure of fatigue. To date, data from 10 children with hearing loss (CHL) and 10 age-matched children with normal hearing (CNH) have been analyzed. Results These preliminary results show that subjective fatigue is increased in school-age children with hearing loss (Cohen's d = 0.78–1.90). In addition, the impact of hearing loss on fatigue in school-age children appears pervasive across multiple domains (general, sleep/rest, and cognitive fatigue). Conclusion School-age CHL reported significantly more fatigue than did CNH. These preliminary data are important given the negative academic and psychosocial consequences associated with fatigue. Further research is needed to determine the underlying mechanisms responsible for this increased fatigue in school-age children with hearing loss, and to identify factors that may modulate (e.g., degree of loss) and mediate (e.g., hearing aid or cochlear implant use) its impact. PMID:23824428
Detection of Fatigue Crack in Basalt FRP Laminate Composite Pipe using Electrical Potential Change Method

NASA Astrophysics Data System (ADS)

Altabey, Wael A.; Noori, Mohammed

2017-05-01

Novel modulation electrical potential change (EPC) method for fatigue crack detection in a basalt fibre reinforced polymer (FRP) laminate composite pipe is carried out in this paper. The technique is applied to a laminate pipe with an embedded crack in three layers [0º/90º/0º]s. EPC is applied for evaluating the dielectric properties of basalt FRP pipe by using an electrical capacitance sensor (ECS) to discern damages in the pipe. Twelve electrodes are mounted on the outer surface of the pipe and the changes in the modulation dielectric properties of the piping system are analyzed to detect damages in the pipe. An embedded crack is created by a fatigue internal pressure test. The capacitance values, capacitance change and node potential distribution of ECS electrodes are calculated before and after crack initiates using a finite element method (FEM) by ANSYS and MATLAB, which are combined to simulate sensor characteristics and fatigue behaviour. The crack lengths of the basalt FRP are investigated for various number of cycles to failure for determining crack growth rate. Response surfaces are adopted as a tool for solving inverse problems to estimate crack lengths from the measured electric potential differences of all segments between electrodes to validate the FEM results. The results show that, the good convergence between the FEM and estimated results. Also the results of this study show that the electrical potential difference of the basalt FRP laminate increases during cyclic loading, caused by matrix cracking. The results indicate that the proposed method successfully provides fatigue crack detection for basalt FRP laminate composite pipes.
Effects of once weekly NMES training on knee extensors fatigue and body composition in a person with spinal cord injury.

PubMed

Gorgey, Ashraf S; Caudill, Caelb; Khalil, Refka E

2016-01-01

Single-subject case (male, 33 years of age, T6 SCI AIS A). To determine the effect of surface neuromuscular electrical stimulation (NMES) training conducted once weekly on improving fatigue resistance as well as regional and whole body composition in an individual with spinal cord injury (SCI). Laboratory setting within a SCI Center. Surface NMES resistance training (RT) of the paralyzed knee extensors was conducted once weekly for 12 weeks using ankle weights. Knee extensor fatigue index was determined by the number of repetitions (reps) achieved out of 30 reps. Total and regional body composition including percentage body fat (%BF), fat mass (FM), lean mass (LM) were conducted before the first session and one week after the last training session using whole-body dual-energy X-ray absorptiometry. The participant had a compliance rate of 83% and he was able to lift 6 and 2 lbs on the right and left legs, respectively. Right knee extensors showed greater fatigue resistance compared to the left one. Leg LM increased by 6% accompanied with decrease in arm, trunk and total body LM by -4.7%, -13%, -5%, respectively. The %BF increased by 8%, 7.3%, 15.5%, 11.5% for arm, legs, trunk and total body. Once weekly of NMES RT evokes local positive changes in leg LM without reciprocating the continuous loss in LM or gain in FM in other regions and total body. Training was effective in increasing strength as well as fatigue resistance of the trained knee extensors.
Calculation of trajectories and the rate of growth of curvilinear fatigue cracks in isotropic and composite plates

NASA Astrophysics Data System (ADS)

Pokhmurska, H.; Maksymovych, O.; Dzyubyk, A.; Dzyubyk, L.

2018-06-01

The methods of calculating the trajectories and the rate of growth of curvilinear fatigue cracks in isotropic and composite plate structure elements during cyclic loading along straight or curvilinear trajectories are developed. For isotropic and anisotropic materials, the methodes are developed on the basis of the force criterion of destruction with the additional application of the fatigue fracture diagrams. To find the change in the shape of the cracks in the loading process, the step-by-step method was used. At each stage, the direction of the growth of all vertices of cracks and the lengths of their arcs was found on the basis of determining the intensity coefficients of stresses by the method of singular integral equations. The results of calculations of the cracks system growth process are presented.
Nondestructive damage evaluation in ceramic matrix composites for aerospace applications.

PubMed

Dassios, Konstantinos G; Kordatos, Evangelos Z; Aggelis, Dimitrios G; Matikas, Theodore E

2013-01-01

Infrared thermography (IRT) and acoustic emission (AE) are the two major nondestructive methodologies for evaluating damage in ceramic matrix composites (CMCs) for aerospace applications. The two techniques are applied herein to assess and monitor damage formation and evolution in a SiC-fiber reinforced CMC loaded under cyclic and fatigue loading. The paper explains how IRT and AE can be used for the assessment of the material's performance under fatigue. IRT and AE parameters are specifically used for the characterization of the complex damage mechanisms that occur during CMC fracture, and they enable the identification of the micromechanical processes that control material failure, mainly crack formation and propagation. Additionally, these nondestructive parameters help in early prediction of the residual life of the material and in establishing the fatigue limit of materials rapidly and accurately.
Fabric strain sensor integrated with CNPECs for repeated large deformation

NASA Astrophysics Data System (ADS)

Yi, Weijing

Flexible and soft strain sensors that can be used in smart textiles for wearable applications are much desired. They should meet the requirements of low modulus, large working range and good fatigue resistance as well as good sensing performances. However, there were no commercial products available and the objective of the thesis is to investigate fabric strain sensors based on carbon nanoparticle (CNP) filled elastomer composites (CNPECs) for potential wearing applications. Conductive CNPECs were fabricated and investigated. The introduction of silicone oil (SO) significantly decreased modulus of the composites to less than 1 MPa without affecting their deformability and they showed good stability after heat treatment. With increase of CNP concentration, a percolation appeared in electrical resistivity and the composites can be divided into three ranges. I-V curves and impedance spectra together with electro-mechanical studies demonstrated a balance between sensitivity and working range for the composites with CNP concentrations in post percolation range, and were preferred for sensing applications only if the fatigue life was improved. Due to the good elasticity and failure resist property of knitted fabric under repeated extension, it was adopted as substrate to increase the fatigue life of the conductive composites. After optimization of processing parameters, the conductive fabric with CNP concentration of 9.0CNP showed linear I-V curves when voltage is in the range of -1 V/mm and 1 V/mm and negligible capacitive behavior when frequency below 103 Hz even with strain of 60%. It showed higher sensitivity due to the combination of nonlinear resistance-strain behavior of the CNPECs and non-even strain distribution of knitted fabric under extension. The fatigue life of the conductive fabric was greatly improved. Extended on the studies of CNPECs and the coated conductive fabrics, a fabric strain sensor was designed, fabricated and packaged. The Young's modulus of the packaged fabric strain sensor was less than 1 MPa; the strain gauge factor was 4.76 within the strain range of 0-40% and the hysteresis was 5.5%; the resistance relaxation was 5.56% with a constant strain of 40%; the fatigue life of the sensor was more than 100,000 cycles.
Influence of Microstructure and Shot Peening Treatment on Corrosion Resistance of AISI F55-UNS S32760 Super Duplex Stainless Steel.

PubMed

Ciuffini, Andrea Francesco; Barella, Silvia; Peral Martínez, Luis Borja; Mapelli, Carlo; Fernández Pariente, Inés

2018-06-19

Shot peening is a surface process commonly used in the aeronautic and automotive industries to improve fatigue resistance. Shot peening is proven to be beneficial in the fatigue behavior of components, but rarely has its influence on wear and pitting corrosion resistance been evaluated. In this work, shot peening was performed on AISI F55-UNS S32760 super-duplex stainless steel samples previously submitted to various thermal treatments, to obtain different initial microstructures and properties. Samples have been characterized in terms of microstructure morphology, local chemical composition, microhardness of each constituent phase, and energy dissipation modes. The enhanced properties provided by shot peening has been evaluated through residual stress depth profiles and Full Width at Half Maximum (FWHM) using X-ray diffraction (XRD), surface hardness, surface roughness, and corrosion resistance through salt spray fog tests. The 1400 °C solution thermal treatment was identified as the optimum initial condition, which maximizes the advantages of the shot peening treatment, even pitting corrosion resistance. These results are related to the uniformity of austenite and ferrite in terms of microstructure morphology, micromechanical properties, and alloying elements distribution.
75 FR 793 - Damage Tolerance and Fatigue Evaluation of Composite Rotorcraft Structures

Federal Register 2010, 2011, 2012, 2013, 2014

2010-01-06

... there are six U.S. part 27 helicopter manufacturers that produce composite helicopters. MD Helicopters... and is not expected to produce composite heliopters in the future.. 8/10/2009 Part 29 Helicopter... helicopter inspection time for a composite part will be the same as or less than for a metallic part...

An in vitro study of the effect of different restorative materials on the reliability of a veneering porcelain.

PubMed

Anderson, Matthew R; Chung, Kwok-Hung; Flinn, Brian D; Raigrodski, Ariel J

2013-12-01

Implant-supported, porcelain veneered restorations experience a greater rate of porcelain fracture than tooth-supported restorations. For completely edentulous patients, one approach to minimizing porcelain fracture is to use acrylic resin in the mandible, although its efficacy is unknown. The purpose of this study was to evaluate the reliability of a veneering porcelain fatigued with different restorative materials in vitro. Fifty-nine veneering porcelain disk specimens were fabricated by layering veneering porcelain on nickel-chromium base metal alloy disks. Four groups of different indenter materials fatigued the porcelain specimens: group WC, tungsten carbide served as a control; group FC, pressed leucite glass ceramic; group NHC, nanohybrid composite resin denture tooth; and group AR, unfilled acrylic resin denture tooth. Porcelain specimens were randomly divided into 4 groups (n=14). A step-stress accelerated life-testing model was used. Use-level probability Weibull plots were generated, and the reliability of each group was estimated for a theoretical completion of 50 000 cycles at 150 N. Nanohybrid composite resin and unfilled acrylic resin denture tooth groups had higher reliability than tungsten carbide and leucite glass ceramic groups. No significant differences existed between the reliability of the tungsten carbide and leucite glass ceramic groups and the nanohybrid composite resin and acrylic resin denture tooth groups. Veneering porcelain disk specimens fatigued with the unfilled acrylic resin and nanohybrid composite resin denture tooth indenters exhibited higher reliability than the specimens fatigued with either the tungsten carbide or leucite glass ceramic indenters. All of the veneering porcelain disk specimens failed with the same mode of fracture, although the surface posttest exhibited different fracture characteristics among specimens fatigued with the 4 different materials. Copyright © 2013 Editorial Council for the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.
Multiscale Modeling of Novel Carbon Nanotube/Copper-Composite Material Used in Microelectronics

NASA Astrophysics Data System (ADS)

Awad, Ibrahim; Ladani, Leila

2016-06-01

Current carrying capacity is one of the elements that hinders further miniaturization of Copper (Cu) interconnects. Therefore, there is a need to propose new materials with higher ampacity (current carrying capacity) that have the potential to replace Cu. Experimental observations have shown that Carbon Nanotube (CNT)/Cu-composite material has a hundredfold ampacity of Cu, which makes it a good candidate to replace Cu. However, sufficient information about the mechanical behavior of the novel CNT/Cu-composite is not available. In the current paper, the CNT/Cu-composite is utilized to construct Through Silicon Via (TSV). The mechanical behavior, specifically the fatigue life, of the CNT/Cu-TSV is evaluated by applying a multiscale modeling approach. Molecular Dynamics (MD) simulations are conducted to evaluate the tensile strength and the coefficient of thermal expansion of CNTs. MD simulation is also used to determine the interface behavior between CNTs and Cu. MD simulation results are integrated into Finite Element analysis at the micro-level to estimate the fatigue life of the CNT/Cu-TSV. A comparison is made with base material; Cu. CNTs addition has redistributed the plastic deformation in Cu to occur at two different locations (Si/Cu interface and Cu/CNT interface) instead of only one location (Si/Cu interface) in the case of Cu-only-TSV. Thus, the maximum equivalent plastic strain has been alleviated in the CNT/Cu-TSV. Accordingly, CNT/Cu-TSV has shown a threefold increase in the fatigue life. This is a solid indication of the improvement in the fatigue life that is attributed to the addition of CNTs.
Effect of Prior Aging on Fatigue Behavior of IM7/BMI 5250-4 Composite at 191 C

DTIC Science & Technology

2007-06-01

6 Figure 4. Three stages of fatigue life cycle for general material ....................................... 9 Figure 5...calibration ........ 24 vii Figure 17. Omega thermocouple reader setup .................................................................. 26 Figure...cost and fleet readiness. To assure long- term durability and structural integrity of HTPMC components, reliable experimentally- based life -prediction
Ultrasonic Characterization of Fatigue Cracks in Composite Materials

NASA Technical Reports Server (NTRS)

Workman, Gary L.; Watson, Jason; Johnson, Devin; Walker, James; Russell, Sam; Thom, Robert (Technical Monitor)

2002-01-01

Microcracking in composite structures due to combined fatigue and cryogenic loading can cause leakage and failure of the structure and can be difficult to detect in-service. In aerospace systems, these leaks may lead to loss of pressure/propellant, increased risk of explosion and possible cryo-pumping. The success of nondestructive evaluation to detect intra-ply microcracking in unlined pressure vessels fabricated from composite materials is critical to the use of composite structures in future space systems. The work presented herein characterizes measurements of intraply fatigue cracking through the thickness of laminated composite material by means of correlation with ultrasonic resonance. Resonant ultrasound spectroscopy provides measurements which are sensitive to both the microscopic and macroscopic properties of the test article. Elastic moduli, acoustic attenuation, and geometry can all be probed. The approach is based on the premise of half-wavelength resonance. The method injects a broadband ultrasonic wave into the test structure using a swept frequency technique. This method provides dramatically increased energy input into the test article, as compared to conventional pulsed ultrasonics. This relative energy increase improves the ability to measure finer details in the materials characterization, such as microcracking and porosity. As the microcrack density increases, more interactions occur with the higher frequency (small wavelength) components of the signal train causing the spectrum to shift toward lower frequencies. Several methods are under investigation to correlate the degree of microcracking from resonance ultrasound measurements on composite test articles including self organizing neural networks, chemometric techniques used in optical spectroscopy and other clustering algorithms.
Electromechanical fatigue in IPMC under dynamic energy harvesting conditions

NASA Astrophysics Data System (ADS)

Krishnaswamy, Arvind; Roy Mahapatra, D.

2011-04-01

Ionic polymer-metal composites (IPMCs) are an interesting subset of smart, multi-functional materials that have shown promises in energy conversion technologies. Being electromechanically coupled, IPMCs can function as dynamic actuators and sensors, transducers for energy conversion and harvesting, as well as artificial muscles for medical and industrial applications. Like all natural materials, even IPMCs undergo fatigue under dynamic load conditions. Here, we investigate the electromechanical fatigue induced in the IPMCs due to the application of cyclic mechanical bending deformation under hydrodynamic energy harvesting condition. Considering the viscoelastic nature of the IPMC, we employ an analytical approach to modeling electromechanical fatigue primarily under the cyclic stresses induced in the membrane. The polymer-metal composite undergoes cyclic softening throughout the fatigue life without attaining a saturated state of charge migration. However, it results in (1) degradation of electromechanical performance; (2) nucleation and growth of microscopic cracks in the metal electrodes; (3) delamination of metal electrodes at the polymer-electrode interface. To understand these processes, we employ a phenomenological approach based on experimentally measured relaxation properties of the IPMC membrane. Electromechanical performance improves significantly with self-healing like properties for a certain range of relaxation time. This is due to reorientation of the backbone polymer chains which eventually leads to a regenerative process with increased charge transport.
Modeling the Residual Strength of a Fibrous Composite Using the Residual Daniels Function

NASA Astrophysics Data System (ADS)

Paramonov, Yu.; Cimanis, V.; Varickis, S.; Kleinhofs, M.

2016-09-01

The concept of a residual Daniels function (RDF) is introduced. Together with the concept of Daniels sequence, the RDF is used for estimating the residual (after some preliminary fatigue loading) static strength of a unidirectional fibrous composite (UFC) and its S-N curve on the bases of test data. Usually, the residual strength is analyzed on the basis of a known S-N curve. In our work, an inverse approach is used: the S-N curve is derived from an analysis of the residual strength. This approach gives a good qualitive description of the process of decreasing residual strength and explanes the existence of the fatigue limit. The estimates of parameters of the corresponding regression model can be interpreted as estimates of parameters of the local strength of components of the UFC. In order to approach the quantitative experimental estimates of the fatigue life, some ideas based on the mathematics of the semiMarkovian process are employed. Satisfactory results in processing experimental data on the fatigue life and residual strength of glass/epoxy laminates are obtained.
DOE Office of Scientific and Technical Information (OSTI.GOV)

MANDELL, JOHN F.; SAMBORSKY, DANIEL D.; CAIRNS, DOUGLAS

This report presents the major findings of the Montana State University Composite Materials Fatigue Program from 1997 to 2001, and is intended to be used in conjunction with the DOE/MSU Composite Materials Fatigue Database. Additions of greatest interest to the database in this time period include environmental and time under load effects for various resin systems; large tow carbon fiber laminates and glass/carbon hybrids; new reinforcement architectures varying from large strands to prepreg with well-dispersed fibers; spectrum loading and cumulative damage laws; giga-cycle testing of strands; tough resins for improved structural integrity; static and fatigue data for interply delamination; andmore » design knockdown factors due to flaws and structural details as well as time under load and environmental conditions. The origins of a transition to increased tensile fatigue sensitivity with increasing fiber content are explored in detail for typical stranded reinforcing fabrics. The second focus of the report is on structural details which are prone to delamination failure, including ply terminations, skin-stiffener intersections, and sandwich panel terminations. Finite element based methodologies for predicting delamination initiation and growth in structural details are developed and validated, and simplified design recommendations are presented.« less
Modeling Fatigue Damage Onset and Progression in Composites Using an Element-Based Virtual Crack Closure Technique Combined With the Floating Node Method

NASA Technical Reports Server (NTRS)

De Carvalho, Nelson V.; Krueger, Ronald

2016-01-01

A new methodology is proposed to model the onset and propagation of matrix cracks and delaminations in carbon-epoxy composites subject to fatigue loading. An extended interface element, based on the Floating Node Method, is developed to represent delaminations and matrix cracks explicitly in a mesh independent fashion. Crack propagation is determined using an element-based Virtual Crack Closure Technique approach to determine mixed-mode energy release rates, and the Paris-Law relationship to obtain crack growth rate. Crack onset is determined using a stressbased onset criterion coupled with a stress vs. cycle curve and Palmgren-Miner rule to account for fatigue damage accumulation. The approach is implemented in Abaqus/Standard® via the user subroutine functionality. Verification exercises are performed to assess the accuracy and correct implementation of the approach. Finally, it was demonstrated that this approach captured the differences in failure morphology in fatigue for two laminates of identical stiffness, but with layups containing ?deg plies that were either stacked in a single group, or distributed through the laminate thickness.
A Fatigue Measuring Protocol for Wireless Body Area Sensor Networks.

PubMed

Akram, Sana; Javaid, Nadeem; Ahmad, Ashfaq; Khan, Zahoor Ali; Imran, Muhammad; Guizani, Mohsen; Hayat, Amir; Ilahi, Manzoor

2015-12-01

As players and soldiers preform strenuous exercises and do difficult and tiring duties, they are usually the common victims of muscular fatigue. Keeping this in mind, we propose FAtigue MEasurement (FAME) protocol for soccer players and soldiers using in-vivo sensors for Wireless Body Area Sensor Networks (WBASNs). In FAME, we introduce a composite parameter for fatigue measurement by setting a threshold level for each sensor. Whenever, any sensed data exceeds its threshold level, the players or soldiers are declared to be in a state of fatigue. Moreover, we use a vibration pad for the relaxation of fatigued muscles, and then utilize the vibrational energy by means of vibration detection circuit to recharge the in-vivo sensors. The induction circuit achieves about 68 % link efficiency. Simulation results show better performance of the proposed FAME protocol, in the chosen scenarios, as compared to an existing Wireless Soccer Team Monitoring (WSTM) protocol in terms of the selected metrics.
Fatigue-environment interactions in a SiC/Ti-15-3 composite

NASA Technical Reports Server (NTRS)

Gayda, J.; Gabb, T. P.; Lerch, B. A.

1993-01-01

Load-controlled isothermal and nonisothermal fatigue lives of a (0-deg)s SiC/Ti-15-3 were evaluated at temperatures between 150 and 550 C and a target strain range of about 0.45 percent. In nonisothermal fatigue tests, load was first cycled at minimum temperature and then temperature was cycled at zero load. For fatigue tests with peak temperatures at or above 300 C, fatigue life was dramatically reduced compared to that at 150 C. The shortest life was produced by the nonisothermal test with the greatest temperature range (Delta T = 400 C) and highest peak temperature (T(max) = 550 C). Vacuum testing showed that much of the life reduction under isothermal and nonisothermal conditions was related to environmental effects, although the nature of the fatigue-environment interaction was decidedly different for the isothermal and nonisothermal test cycles which were studied.
Circadian type, chronic fatigue, and serum IgM in the shift workers of an industrial organization

PubMed Central

Khaleghipour, Shahnaz; Masjedi, Mohsen; Kelishadi, Roya

2015-01-01

Background: Night shift workers are more vulnerable to immune-related diseases. Immunoglobulin M (IgM) is a potent activator of complement, and complement has a crucial role in defense against bacterial infections. Circadian type is known as an effective agent on vulnerability and adaptation with shift work due to non-compliance with shift stress. The objective of this study was to investigate the correlation of circadian type and chronic fatigue with the serum concentration of IgM in a group of shift workers. Materials and Methods: This cross-sectional study was performed in an industrial organization in Isfahan, Iran. The study population consisted of 221 male employees working at night shifts who were selected by random cluster sampling. The following questionnaires were used: composite morningness (Torsvall and Akerstedt), circadian type (Folkard), and chronic fatigue (Barton and colleagues). The serum concentration of IgM was measured by the nephelometric method. The data were analyzed with the Pearson coefficient correlation and the path analysis for finding the pattern of the structural equations to evaluate the direct and indirect relationships between variables, using the SPSS 15 and LISREL 8.5 statistical software. Results: Significant correlation was documented between morningness, flexibility, languidness, and chronic fatigue with the serum concentration of IgM (P < 0.01). Conclusion: The results showed that the shift workers with morningness and languidness experienced more problems during the working hours due to more tiredness, and had decreased serum concentration of IgM. Correct management of shift work may attenuate fatigue in workers and also improve many health issues experienced by the shift workers. PMID:25802830
Compression fatigue behavior and failure mechanism of porous titanium for biomedical applications.

PubMed

Li, Fuping; Li, Jinshan; Huang, Tingting; Kou, Hongchao; Zhou, Lian

2017-01-01

Porous titanium and its alloys are believed to be one of the most attractive biomaterials for orthopedic implant applications. In the present work, porous pure titanium with 50-70% porosity and different pore size was fabricated by diffusion bonding. Compression fatigue behavior was systematically studied along the out-of-plane direction. It resulted that porous pure titanium has anisotropic pore structure and the microstructure is fine-grained equiaxed α phase with a few twins in some α grains. Porosity and pore size have some effect on the S-N curve but this effect is negligible when the fatigue strength is normalized by the yield stress. The relationship between normalized fatigue strength and fatigue life conforms to a power law. The compression fatigue behavior is characteristic of strain accumulation. Porous titanium experiences uniform deformation throughout the entire sample when fatigue cycle is lower than a critical value (N T ). When fatigue cycles exceed N T , strain accumulates rapidly and a single collapse band forms with a certain angle to the loading direction, leading to the sudden failure of testing sample. Both cyclic ratcheting and fatigue crack growth contribute to the fatigue failure mechanism, while the cyclic ratcheting is the dominant one. Porous titanium possesses higher normalized fatigue strength which is in the range of 0.5-0.55 at 10 6 cycles. The reasons for the higher normalized fatigue strength were analyzed based on the microstructure and fatigue failure mechanism. Copyright © 2016 Elsevier Ltd. All rights reserved.
Development and characterization of fatigue resistant Aramid reinforced aluminium laminates (ARALL) for fatigue Critical aircraft components

NASA Astrophysics Data System (ADS)

Qaiser, M. H.; Umar, S.; Nauman, S.

2014-06-01

The structural weight of an aircraft has always been a controlling parameter that governs its fuel efficiency and transport capacity. In pursuit of achieving light-weight aircraft structures, high design stress levels have to be adopted and materials with high specific strength such as Aluminum etc. are to be deployed. However, an extensive spectrum of fatigue load exists at the aircraft wings and other aerodynamic components that may cause initiation and propagation of fatigue cracks and concludes in a catastrophic rupture. Fatigue is therefore the limiting design parameter in such cases and materials with high fatigue resistance are then required. A major improvement in the fatigue behavior was observed by laminating Kevlar fibers with Aluminum using epoxy. ARALL (Aramid Reinforced ALuminum Laminates) is a fatigue resistant hybrid composite that consists of layers of thin high strength aluminum alloy sheets surface bonded with aramid fibers. The intact aramid fibers tie up the fatigue cracks, thus reducing the stress intensity factor at the crack tip as a result of which the fatigue properties of can be enhanced with orders of magnitude as compared to monolithic high strength Aluminum alloy sheets. Significant amount of weight savings can be achieved in fatigue critical components in comparison with the traditional materials used in aircraft.
Is the impact of fatigue related to walking capacity and perceived ability in persons with multiple sclerosis? A multicenter study.

PubMed

Dalgas, U; Langeskov-Christensen, M; Skjerbæk, A; Jensen, E; Baert, I; Romberg, A; Santoyo Medina, C; Gebara, B; Maertens de Noordhout, B; Knuts, K; Béthoux, F; Rasova, K; Severijns, D; Bibby, B M; Kalron, A; Norman, B; Van Geel, F; Wens, I; Feys, P

2018-04-15

The relationship between fatigue impact and walking capacity and perceived ability in patients with multiple sclerosis (MS) is inconclusive in the existing literature. A better understanding might guide new treatment avenues for fatigue and/or walking capacity in patients with MS. To investigate the relationship between the subjective impact of fatigue and objective walking capacity as well as subjective walking ability in MS patients. A cross-sectional multicenter study design was applied. Ambulatory MS patients (n = 189, age: 47.6 ± 10.5 years; gender: 115/74 women/men; Expanded Disability Status Scale (EDSS): 4.1 ± 1.8 [range: 0-6.5]) were tested at 11 sites. Objective tests of walking capacity included short walking tests (Timed 25-Foot Walk (T25FW), 10-Metre Walk Test (10mWT) at usual and fastest speed and the timed up and go (TUG)), and long walking tests (2- and 6-Minute Walk Tests (MWT). Subjective walking ability was tested applying the Multiple Sclerosis Walking Scale-12 (MSWS-12). Fatigue impact was measured by the self-reported modified fatigue impact scale (MFIS) consisting of a total score (MFIS total ) and three subscales (MFIS physical , MFIS cognitive and MFIS psychosocial ). Uni- and multivariate regression analysis were performed to evaluate the relation between walking and fatigue impact. MFIS total was negatively related with long (6MWT, r = -0.14, p = 0.05) and short composite (TUG, r = -0.22, p = 0.003) walking measures. MFIS physical showed a significant albeit weak relationship to walking speed in all walking capacity tests (r = -0.22 to -0.33, p < .0001), which persisted in the multivariate linear regression analysis. Subjective walking ability (MSWS-12) was related to MFIS total (r = 0.49, p < 0.0001), as well as to all other subscales of MFIS (r = 0.24-0.63, p < 0.001), showing stronger relationships than objective measures of walking. The physical impact of fatigue is weakly related to objective walking capacity, while general, physical, cognitive and psychosocial fatigue impact are weakly to moderately related to subjective walking ability, when analysed in a large heterogeneous sample of MS patients. Copyright © 2018 Elsevier B.V. All rights reserved.
Cryogenic Fluid Management Experiment (CFME) trunnion verification testing

NASA Technical Reports Server (NTRS)

Bailey, W. J.; Fester, D. A.

1983-01-01

The Cryogenic Fluid Management Experiment (CFME) was designed to characterize subcritical liquid hydrogen storage and expulsion in the low-g space environment. The CFME has now become the storage and supply tank for the Cryogenic Fluid Management Facility, which includes transfer line and receiver tanks, as well. The liquid hydrogen storage and supply vessel is supported within a vacuum jacket to two fiberglass/epoxy composite trunnions which were analyzed and designed. Analysis using the limited available data indicated the trunnion was the most fatigue critical component in the storage vessel. Before committing the complete storage tank assembly to environmental testing, an experimental assessment was performed to verify the capability of the trunnion design to withstand expected vibration and loading conditions. Three tasks were conducted to evaluate trunnion integrity. The first determined the fatigue properties of the trunnion composite laminate materials. Tests at both ambient and liquid hydrogen temperatures showed composite material fatigue properties far in excess of those expected. Next, an assessment of the adequacy of the trunnion designs was performed (based on the tested material properties).
Interlaminar shear fracture toughness and fatigue thresholds for composite materials

NASA Technical Reports Server (NTRS)

Obrien, T. Kevin; Murri, Gretchen B.; Salpekar, Satish A.

1987-01-01

Static and cyclic end notched flexure tests were conducted on a graphite epoxy, a glass epoxy, and graphite thermoplastic to determine their interlaminar shear fracture toughness and fatigue thresholds for delamination in terms of limiting values of the mode II strain energy release rate, G-II, for delamination growth. The influence of precracking and data reduction schemes are discussed. Finite element analysis indicated that the beam theory calculation for G-II with the transverse shear contribution included was reasonably accurate over the entire range of crack lengths. Cyclic loading significantly reduced the critical G-II for delamination. A threshold value of the maximum cyclic G-II below which no delamination occurred after one million cycles was identified for each material. Also, residual static toughness tests were conducted on glass epoxy specimens that had undergone one million cycles without delamination. A linear mixed-mode delamination criteria was used to characterize the static toughness of several composite materials; however, a total G threshold criterion appears to characterize the fatigue delamination durability of composite materials with a wide range of static toughness.
Mechanical Properties and Fatigue Behavior of Unitized Composite Airframe Structures at Elevated Temperature

DTIC Science & Technology

2016-09-01

investigated. The unitized composite consisted of a polymer matrix composite (PMC) co-cured with a ceramic matrix composite (CMC). The PMC portion...ply non- crimp 3D orthogonal weave composite consisting of a ceramic matrix reinforced with glass fibers. In order to assess the performance and...2.3 Ceramic Matrix Composites ...................................................................................5 2.4 2D vs 3D Reinforcement
Fractographic study of epoxy fractured under mode I loading and mixed mode I/III loading

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ren, Fei; Wang, Jy-An John; Bertelsen, Williams D.

2011-01-01

Fiber reinforced polymeric composite materials are widely used in structural components such as wind turbine blades, which are typically subject to complicated loading conditions. Thus, material response under mixed mode loading is of great significance to the reliability of these structures. Epoxy is a thermosetting polymer that is currently used in manufacturing wind turbine blades. The fracture behavior of epoxy is relevant to the mechanical integrity of the wind turbine composite materials. In this study, a novel fracture testing methodology, the spiral notch torsion test (SNTT), was applied to study the fracture behavior of an epoxy material. SNTT samples weremore » tested using either monotonic loading or cyclic loading, while both mode I and mixed mode I/III loading conditions were used. Fractographic examination indicated the epoxy samples included in this study were prone to mode I failure even when the samples were subject to mixed mode loading. Different fatigue precracks were observed on mode I and mixed mode samples, i.e. precracks appeared as a uniform band under mode I loading, and a semi-ellipse under mixed mode loading. Fracture toughness was also estimated using quantitative fractography.« less
The Effect of Moisture on the Properties of an Aramid/Epoxy Composite

DTIC Science & Technology

1983-05-01

COMPOSITES DEVELOP~ENT DIVISiON...TYPE OF REPORT II PERIOD COV ERED THE EFFECT OF MOISTURE ON THE PROPERTIES OF AN Final Report ARAMID/EPOXY COMPOSITE ’· PERFORMING ORG. REPORT...ConrJnue on reror•ralt •rde ff n~(•.’lsar:,.- .,d ldenrl(y b~ L/odc numbe-r) Composite Materials Fatigue (mechanic s ) Aramid/epoxy composites
The relationship between parental fatigue, parenting self-efficacy and behaviour: implications for supporting parents in the early parenting period.

PubMed

Chau, V; Giallo, R

2015-07-01

Emerging evidence indicates that parental fatigue is associated with low warmth and increased hostility in parent-child interactions. One possible pathway by which fatigue may impact on parenting behaviour is via parental self-efficacy (PSE), whereby high fatigue may undermine PSE, which is often associated with suboptimal parenting behaviour. The current study sought to explore a model of the relationships between parental fatigue, parenting warmth and hostility, where PSE mediates these relationships and whether the nature of these relationships differ by social or family context. The current sample was drawn from a larger Australian community sample survey on parent well-being and parenting. It consisted of 1143 parents (mothers, n = 1003; fathers, n = 140) of children aged 0-4 years. Path analysis revealed that the relationship between fatigue and parenting warmth and hostility was fully mediated by PSE. These results indicate that fatigue has the potential to negatively influence parenting behaviours that are important for their children's well-being and development, and that fatigue plays a mediating role in this relationship. Implications of the study for psycho-education and interventions targeting the management of parental fatigue are discussed. © 2014 John Wiley & Sons Ltd.

Very High Cycle Fatigue Behavior of a Directionally Solidified Ni-Base Superalloy DZ4

PubMed Central

Nie, Baohua; Zhao, Zihua; Liu, Shu; Chen, Dongchu; Ouyang, Yongzhong; Hu, Zhudong; Fan, Touwen; Sun, Haibo

2018-01-01

The effect of casting pores on the very high cycle fatigue (VHCF) behavior of a directionally solidified (DS) Ni-base superalloy DZ4 is investigated. Casting and hot isostatic pressing (HIP) specimens were subjected to very high cycle fatigue loading in an ambient atmosphere. The results demonstrated that the continuously descending S-N curves were exhibited for both the casting and HIP specimens. Due to the elimination of the casting pores, the HIP samples had better fatigue properties than the casting samples. The subsurface crack initiated from the casting pore in the casting specimens at low stress amplitudes, whereas fatigue crack initiated from crystallographic facet decohesion for the HIP specimens. When considering the casting pores as initial cracks, there exists a critical stress intensity threshold ranged from 1.1 to 1.3 MPam, below which fatigue cracks may not initiate from the casting pores. Furthermore, the effect of the casting pores on the fatigue limit is estimated based on a modified El Haddad model, which is in good agreement with the experimental results. Fatigue life for both the casting and HIP specimens is well predicted using the Fatigue Indicator Parameter (FIP) model. PMID:29320429
Influence of the number of cycles on shear fatigue strength of resin composite bonded to enamel and dentin using dental adhesives in self-etching mode.

PubMed

Tsujimoto, Akimasa; Barkmeier, Wayne W; Erickson, Robert L; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

2018-01-30

The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to enamel and dentin using the adhesive in self-etch mode were determined. Fatigue testing was used with 20 Hz frequency and cycling periods of 50,000, 100,000 and 1,000,000 cycles, or until failure occurred. For each of the cycling periods, there was no significant difference in shear fatigue strength across the cycling periods for the individual adhesives. Differences in shear fatigue strength were found between the adhesives within the cycling periods. Regardless of the adhesive used in self-etch mode for bonding to enamel or dentin, shear fatigue strength was not influenced by the number of cycles used for shear fatigue strength testing.
An experimental method to quantify the impact fatigue behavior of rocks

NASA Astrophysics Data System (ADS)

Wu, Bangbiao; Kanopoulos, Patrick; Luo, Xuedong; Xia, Kaiwen

2014-07-01

Fatigue failure is an important failure mode of engineering materials. The fatigue behavior of both ductile and brittle materials has been under investigation for many years. While the fatigue failure of ductile materials is well established, only a few studies have been carried out on brittle materials. In addition, most fatigue studies on rocks are conducted under quasi-static loading conditions. To address engineering applications involving repeated blasting, this paper proposes a method to quantify the impact fatigue properties of rocks. In this method, a split Hopkinson pressure bar system is adopted to exert impact load on the sample, which is placed in a specially designed steel sleeve to limit the displacement of the sample and thus to enable the recovery of the rock after each impact. The method is then applied to Laurentian granite, which is fine-grained and isotropic material. The results demonstrate that this is a practicable means to conduct impact fatigue tests on rocks and other brittle solids.
Fatigue resistance and crack propensity of novel "super-closed" sandwich composite resin restorations in large MOD defects.

PubMed

Magne, Pascal; Silva, Silvana; Andrada, Mauro de; Maia, Hamilton

2016-01-01

To assess the influence of conventional glass ionomer cement (GIC) vs resin-modified GIC (RMGIC) as a base material for novel, super-closed sandwich restorations (SCSR) and its effect on shrinkage-induced crack propensity and in vitro accelerated fatigue resistance. A standardized MOD slottype tooth preparation was applied to 30 extracted maxillary molars (5 mm depth/5 mm buccolingual width). A modified sandwich restoration was used, in which the enamel/dentin bonding agent was applied first (Optibond FL, Kerr), followed by a Ketac Molar (3M ESPE)(group KM, n = 15) or Fuji II LC (GC) (group FJ, n = 15) base, leaving 2 mm for composite resin material (Miris 2, Coltène-Whaledent). Shrinkageinduced enamel cracks were tracked with photography and transillumination. Samples were loaded until fracture or to a maximum of 185,000 cycles under isometric chewing (5 H z), starting with a load of 200 N (5,000 X), followed by stages of 400, 600, 800, 1,000, 1,200, and 1,400 N at a maximum of 30,000 X each. Groups were compared using the life table survival analysis (α = .008, Bonferroni method). Group FJ showed the highest survival rate (40% intact specimens) but did not differ from group KM (20%) or traditional direct restorations (13%, previous data). SCSR generated less shrinkage-induced cracks. Most failures were re-restorable (above the cementoenamel junction [CEJ]). Inclusion of GIC/RMGIC bases under large direct SCSRs does not affect their fatigue strength but tends to decrease the shrinkage-induced crack propensity. The use of GIC/ RMGIC bases and the SCSR is an easy way to minimize polymerization shrinkage stress in large MOD defects without weakening the restoration.
Experimental study of crack initiation and propagation in high- and gigacycle fatigue in titanium alloys

DOE Office of Scientific and Technical Information (OSTI.GOV)

Bannikov, Mikhail, E-mail: mbannikov@icmm.ru, E-mail: oborin@icmm.ru, E-mail: naimark@icmm.ru; Oborin, Vladimir, E-mail: mbannikov@icmm.ru, E-mail: oborin@icmm.ru, E-mail: naimark@icmm.ru; Naimark, Oleg, E-mail: mbannikov@icmm.ru, E-mail: oborin@icmm.ru, E-mail: naimark@icmm.ru

Fatigue (high- and gigacycle) crack initiation and its propagation in titanium alloys with coarse and fine grain structure are studied by fractography analysis of fracture surface. Fractured specimens were analyzed by interferometer microscope and SEM to improve methods of monitoring of damage accumulation during fatigue test and to verify the models for fatigue crack kinetics. Fatigue strength was estimated for high cycle fatigue regime using the Luong method [1] by “in-situ” infrared scanning of the sample surface for the step-wise loading history for different grain size metals. Fine grain alloys demonstrated higher fatigue resistance for both high cycle fatigue andmore » gigacycle fatigue regimes. Fracture surface analysis for plane and cylindrical samples was carried out using optical and electronic microscopy method. High resolution profilometry (interferometer-profiler New View 5010) data of fracture surface roughness allowed us to estimate scale invariance (the Hurst exponent) and to establish the existence of two characteristic areas of damage localization (different values of the Hurst exponent). Area 1 with diameter ∼300 μm has the pronounced roughness and is associated with damage localization hotspot. Area 2 shows less amplitude roughness, occupies the rest fracture surface and considered as the trace of the fatigue crack path corresponding to the Paris kinetics.« less
High Cycle Fatigue Properties Of Electron Beam Melted TI-6AL-4V Samples Without And With Integrated Defects ("Effects Of Defects")

NASA Astrophysics Data System (ADS)

Brandl, Erhard; Greitemeier, Daniel; Maier, Hans Jurgen; Syassen, Freerk

2012-07-01

The understanding of additive manufactured material properties is still at an early stage and mostly not profound. Nowadays, there is only little experience in predicting the effect of defects (e.g. porosity, unmelted spots, insufficient bonding between the layers) on the fatigue behaviour. In this paper, some of these questions are adressed. An electron beam melting process is used to manufacture Ti-6Al-4V high cycle fatigue samples without and with intentionally integrated defects inside of the samples. The samples were annealed or hot isostatically pressed. The defects were analysed by non- destructive methods before and by light/electron microscopy after the tests. In order to predict the high cycle fatigue properties, the crack propagation properties of the material (da/dN - ΔK curve) were tested and AFGROW simulation was used.
Gender differences in fatigue: biopsychosocial factors relating to fatigue in men and women.

PubMed

Bensing, J M; Hulsman, R L; Schreurs, K M

1999-10-01

Fatigue is a common problem, which is found more frequently among women than men. To date, neither the etiology of fatigue nor the factors that explain the gender difference in its incidence are still fully understood. In a sample of men (n = 4,681) and women (n = 4,698) (age range, 15-64 years) in the Dutch National Survey of Morbidity and Interventions in General Practice, the gender differences in the underlying biological, psychological, and social factors of fatigue were analyzed. Both general and gender-specific factors were recognized. Men and women who experience complaints of fatigue appeared to be younger and more highly educated. They had more acute health complaints and more psychosocial problems and also showed a lower level of perceived health. Among women, only gender-specific biological complaints and psychosocial problems were related to fatigue. In addition, relevant sociodemographic variables included taking care of young children and being employed. Among men, fatigue was particularly related to having handicaps and severe chronic complaints. Taking care of young children did not make a difference in the male sample. Fatigue can only be adequately understood in a multicausal model with biomedical and psychosocial factors. Complaints of fatigue are too often ignored in general practice. By adopting a patient-centered style of communication, physicians can acquire a more complete picture of the patients' fatigue.
Hygrothermomechanical evaluation of transverse filament tape epoxy/polyester fiberglass composites

NASA Technical Reports Server (NTRS)

Lark, R. L.; Chamis, C. C.

1983-01-01

The static and cyclic load behavior of transverse filament tape (TFT) fiberglass/epoxy and TFY fiberglass/polyester composites, intended for use in the design of low-cost wind turbine blades, are presented. The data behavior is also evaluated with respect to predicted properties based on an integrated hygrothermomechanical response theory. Experimental TFT composite data were developed by the testing of laminates made by using composite layups typical of those used for the fabrication of TFT fiberglass wind turbine blades. Static properties include tension, compression, and interlaminar shear strengths at ambient conditions and at high humidity/elevated temperature conditions after a 500 hour exposure. Cyclic fatigue data were obtained using similar environmental conditions and a range of cyclic stresses. The environmental (temperature and moisture) and cyclic load effects on composite strength degradation are subsequently compared with the predictions obtained by using the composite life/durability theory. The results obtained show that the predicted hygrothermomechanical environmental effects on TFT composites are in good agreement with measured data for various properties including fatigue at different cyclic stresses.
The PROMIS fatigue item bank has good measurement properties in patients with fibromyalgia and severe fatigue.

PubMed

Yost, Kathleen J; Waller, Niels G; Lee, Minji K; Vincent, Ann

2017-06-01

Efficient management of fibromyalgia (FM) requires precise measurement of FM-specific symptoms. Our objective was to assess the measurement properties of the Patient-Reported Outcome Measurement Information System (PROMIS) fatigue item bank (FIB) in people with FM. We applied classical psychometric and item response theory methods to cross-sectional PROMIS-FIB data from two samples. Data on the clinical FM sample were obtained at a tertiary medical center. Data for the U.S. general population sample were obtained from the PROMIS network. The full 95-item bank was administered to both samples. We investigated dimensionality of the item bank in both samples by separately fitting a bifactor model with two group factors; experience and impact. We assessed measurement invariance between samples, and we explored an alternate factor structure with the normative sample and subsequently confirmed that structure in the clinical sample. Finally, we assessed whether reporting FM subdomain scores added value over reporting a single total score. The item bank was dominated by a general fatigue factor. The fit of the initial bifactor model and evidence of measurement invariance indicated that the same constructs were measured across the samples. An alternative bifactor model with three group factors demonstrated slightly improved fit. Subdomain scores add value over a total score. We demonstrated that the PROMIS-FIB is appropriate for measuring fatigue in clinical samples of FM patients. The construct can be presented by a single score; however, subdomain scores for the three group factors identified in the alternative model may also be reported.
Fatigue behavior of a cross-ply ceramic matrix composite subjected to tension-tension cycling with hold time. Master`s thesis

DOE Office of Scientific and Technical Information (OSTI.GOV)

Grant, S.A.

This study was carried out to investigate the elevated temperature behavior of the SiC-MAS5 cross- ply (O/9O)4S ceramic matrix composite manufactured by Corning Inc. to fatigue with loading waveforms that combine the characteristics of stress rupture and high cycle fatigue. The test results were compiled in the form of S-N (cycles to failure), S-T (exposure time versus cycles to failure), S-S (energy exposure versus cycles to failure), normalized modulus degradation, strain progression, and hysteresis loop progression. From the mechanical behavior demonstrated by these curves, relationships between the effect of the environment and loading waveform were developed. In addition, a post-mortemmore » SEM analysis of the fracture surface was conducted and the results compared to the mechanical behavior.« less
Corrosion fatigue crack propagation in metals

NASA Technical Reports Server (NTRS)

Gangloff, Richard P.

1990-01-01

This review assesses fracture mechanics data and mechanistic models for corrosion fatigue crack propagation in structural alloys exposed to ambient temperature gases and electrolytes. Extensive stress intensity-crack growth rate data exist for ferrous, aluminum and nickel based alloys in a variety of environments. Interactive variables (viz., stress intensity range, mean stress, alloy composition and microstructure, loading frequency, temperature, gas pressure and electrode potential) strongly affect crack growth kinetics and complicate fatigue control. Mechanistic models to predict crack growth rates were formulated by coupling crack tip mechanics with occluded crack chemistry, and from both the hydrogen embrittlement and anodic dissolution/film rupture perspectives. Research is required to better define: (1) environmental effects near threshold and on crack closure; (2) damage tolerant life prediction codes and the validity of similitude; (3) the behavior of microcrack; (4) probes and improved models of crack tip damage; and (5) the cracking performance of advanced alloys and composites.
Effets de l'humidite sur la propagation du delaminage dans un composite carbone/epoxy sollicite en mode mixte I/II

NASA Astrophysics Data System (ADS)

LeBlanc, Luc R.

Les materiaux composites sont de plus en plus utilises dans des domaines tels que l'aerospatiale, les voitures a hautes performances et les equipements sportifs, pour en nommer quelques-uns. Des etudes ont demontre qu'une exposition a l'humidite nuit a la resistance des composites en favorisant l'initiation et la propagation du delaminage. De ces etudes, tres peu traitent de l'effet de l'humidite sur l'initiation du delaminage en mode mixte I/II et aucune ne traite des effets de l'humidite sur le taux de propagation du delaminage en mode mixte I/II dans un composite. La premiere partie de cette these consiste a determiner les effets de l'humidite sur la propagation du delaminage lors d'une sollicitation en mode mixte I/II. Des eprouvettes d'un composite unidirectionnel de carbone/epoxy (G40-800/5276-1) ont ete immergees dans un bain d'eau distillee a 70°C jusqu'a leur saturation. Des essais experimentaux quasi-statiques avec des chargements d'une gamme de mixites des modes I/II (0%, 25%, 50%, 75% et 100%) ont ete executes pour determiner les effets de l'humidite sur la resistance au delaminage du composite. Des essais de fatigue ont ete realises, avec la meme gamme de mixite des modes I/II, pour determiner 1'effet de 1'humidite sur l'initiation et sur le taux de propagation du delaminage. Les resultats des essais en chargement quasi-statique ont demontre que l'humidite reduit la resistance au delaminage d'un composite carbone/epoxy pour toute la gamme des mixites des modes I/II, sauf pour le mode I ou la resistance au delaminage augmente apres une exposition a l'humidite. Pour les chargements en fatigue, l'humidite a pour effet d'accelerer l'initiation du delaminage et d'augmenter le taux de propagation pour toutes les mixites des modes I/II. Les donnees experimentales recueillies ont ete utilisees pour determiner lesquels des criteres de delaminage en statique et des modeles de taux de propagation du delaminage en fatigue en mode mixte I/II proposes dans la litterature representent le mieux le delaminage du composite etudie. Une courbe de regression a ete utilisee pour determiner le meilleur ajustement entre les donnees experimentales et les criteres de delaminage en statique etudies. Une surface de regression a ete utilisee pour determiner le meilleur ajustement entre les donnees experimentales et les modeles de taux de propagation en fatigue etudies. D'apres les ajustements, le meilleur critere de delaminage en statique est le critere B-K et le meilleur modele de propagation en fatigue est le modele de Kenane-Benzeggagh. Afin de predire le delaminage lors de la conception de pieces complexes, des modeles numeriques peuvent etre utilises. La prediction de la longueur de delaminage lors des chargements en fatigue d'une piece est tres importante pour assurer qu'une fissure interlaminaire ne va pas croitre excessivement et causer la rupture de cette piece avant la fin de sa duree de vie de conception. Selon la tendance recente, ces modeles sont souvent bases sur l'approche de zone cohesive avec une formulation par elements finis. Au cours des travaux presentes dans cette these, le modele de progression du delaminage en fatigue de Landry & LaPlante (2012) a ete ameliore en y ajoutant le traitement des chargements en mode mixte I/II et en y modifiant l'algorithme du calcul de la force d'entrainement maximale du delaminage. Une calibration des parametres de zone cohesive a ete faite a partir des essais quasi-statiques experimentaux en mode I et II. Des resultats de simulations numeriques des essais quasi-statiques en mode mixte I/II, avec des eprouvettes seches et humides, ont ete compares avec les essais experimentaux. Des simulations numeriques en fatigue ont aussi ete faites et comparees avec les resultats experimentaux du taux de propagation du delaminage. Les resultats numeriques des essais quasi-statiques et de fatigue ont montre une bonne correlation avec les resultats experimentaux pour toute la gamme des mixites des modes I/II etudiee.
Eukaryotes in the gut microbiota in myalgic encephalomyelitis/chronic fatigue syndrome

PubMed Central

Mandarano, Alexandra H.; Giloteaux, Ludovic; Keller, Betsy A.; Levine, Susan M.

2018-01-01

Patients with myalgic encephalomyelitis/chronic fatigue syndrome (ME/CFS) often suffer from gastrointestinal symptoms and many are diagnosed with irritable bowel syndrome (IBS). Previous studies, including from our laboratory, have demonstrated that the ME/CFS gut bacterial composition is altered and less diverse when compared to healthy individuals. Patients have increased biomarkers of inflammation and leaky gut syndrome. To further investigate dysbiosis in the ME/CFS gut microbiome, we sought to characterize the eukaryotes present in the gut of 49 individuals with ME/CFS and 39 healthy controls. Using 18S rRNA sequencing, we have identified eukaryotes in stool samples of 17 healthy individuals and 17 ME/CFS patients. Our analysis demonstrates a small, nonsignificant decrease in eukaryotic diversity in ME/CFS patients compared to healthy individuals. In addition, ME/CFS patients show a nonsignificant increase in the ratio of fungal phyla Basidiomycota to Ascomycota, which is consistent with ongoing inflammation in ME/CFS. We did not identify specific eukaryotic taxa that are associated with ME/CFS disease status. PMID:29375937
Transient Dynamic Response and Failure of Composite Structure Under Cyclic Loading with Fluid Structure Interaction

DTIC Science & Technology

2014-09-01

TERMS fluid structure interaction, composite structures shipbuilding, fatigue loading 15. NUMBER OF PAGES 85 16. PRICE CODE 17. SECURITY...under the three point bending test. All the composites exhibit an initial nonlinear and inelastic deformation trend and end with a catastrophic abrupt
Fatigue life prediction of bonded primary joints

NASA Technical Reports Server (NTRS)

Knauss, J. F.

1979-01-01

The validation of a proposed fatigue life prediction methodology was sought through the use of aluminum butt and scarf joint and graphite/epoxy butt joint specimens in a constant amplitude fatigue environment. The structural properties of the HYSOL 9313 adhesive system were obtained by mechanical test of molded heat adhesive specimens. Aluminum contoured double cantilever beam specimens were used to generate crack velocity versus stress intensity factor data. The specific objectives were: (1) to ascertain the feasibility of predicting fatigue failure of an adhesive in a primary bonded composite structure by incorporating linear elastic crack growth behavior; and (2) to ascertain if acoustic emission and/or compliance measurement techniques can be used to detect flaws.
Design, development, and testing of a hybrid in situ testing device for building joint sealant

Treesearch

C. White; N. Embree; C. Buch; R.S. Williams

2005-01-01

The testing of sealant samples has been restricted to devices that either focus on fatiguing multiple samples or quantifying the mechanical properties of a single sample. This manuscript describes a device that combines these two instrumental designs: the ability to both fatigue and characterize multiple sealant samples at the same time. This device employs precise...
Accelerated fatigue durability of a high performance composite

NASA Technical Reports Server (NTRS)

Rotem, A.

1982-01-01

The fatigue behavior of multidirectional graphite-epoxy laminates was analyzed theoretically and experimentally in an effort to establish an accelerated testing methodology. Analysis of the failure mechanism in fatigue of the laminates led to the determination of the failure mode governing fracture. The nonlinear, cyclic-dependent shear modulus was used to calculate the changing stress field in the laminate during the fatigue loading. Fatigue tests were performed at three different temperatures: 25 C, 74 C, and 114 C. The prediction of the S-N curves was made based on the artificial static strength artificial static strength at a reference temperature and the fatigue functions associated with them. The prediction of an S-N curve at other temperatures was performed using shifting factors determined for the specific failure mode. For multidirectional laminates, different S-N curves at different temperatures could be predicted using these shifting factors. Different S-N curves at different temperatures occur only when the fatigue failure mode is matrix dominated. It was found that whenever the fatigue failure mode is fiber dominated, temperature, over the range investigated, had no influence on the fatigue life. These results permit the prediction of long-time, low temperature fatigue behavior from data obtained in short time, high temperature testing, for laminates governed by a matrix failure mode.
The mediating role of emotional symptomatology between anticipatory fatigue and the perception of fatigue.

PubMed

Rodríguez Testal, Juan F; Fuentes Márquez, Sandra; Senín Calderón, Cristina; Carrasco, Miguel A

2016-05-01

Clinical research stresses the importance of cognitive variables for predisposition, onset, and especially, perpetuation of perceived fatigue. The aim was to analyze the mediating effects of emotional symptomatology (somatic, depressive and anxiety) between anticipatory fatigue and perception of physical and cognitive fatigue. The sample was composed of 317 participants (29% from a clinical population) aged 18 to 76. Anticipatory fatigue and perception of fatigue were measured by fatigue scales. Emotional symptoms were assessed by the General Health Questionnaire, GHQ-28. Results : Depressive symptomatology mediated the relationship between anticipatory fatigue and cognitive fatigue in both groups, and also somatic symptoms/somatization in patients. The indirect effect of physical fatigue was observed only in the clinical group, with depressive symptoms partially mediating the anticipatory fatigue and cognitive fatigue relationship. Anticipatory fatigue has a partial indirect effect on total physical fatigue, and full indirect effect on cognitive fatigue, mediated by depressive and somatic symptoms. Anticipatory fatigue is a relevant cognitive factor in the design of psychological intervention for improvement of cognitive and physical fatigue.
Fatigue 󈨛. Papers presented at the International Conference on Fatigue and Fatigue Threshold (3rd) Held in Charlottesville, Virginia on June 28-July 3, 1987. Volume 3.

DTIC Science & Technology

1987-10-15

cracks and loss of fiber-matrix bond, leadin, to nonuniform loading (tensile overload) of composite structure. Figures 13 through 15 show the micro...propagation within the matrix, and alon- the interface, leading to a nonuniform load transfer from matrix to fibers, and causing tensile overload failure...long cracks, were attributed to high cyclic strains at crack tips within grains of maximum crystallographic orientation. Ma and Laire (4) studying the
Design, durability and low cost processing technology for composite fan exit guide vanes

NASA Technical Reports Server (NTRS)

Blecherman, S. S.

1979-01-01

A lightweight composite fan exit guide vane for high bypass ratio gas turbine engine application was investigated. Eight candidate material/design combinations were evaluated by NASTRAN finite element analyses. A total of four combinations were selected for further analytical evaluation, part fabrication by two ventors, and fatigue test in dry and wet condition. A core and shell vane design was chosen in which the unidirectional graphite core fiber was the same for all candidates. The shell material, fiber orientation, and ply configuration were varied. Material tests were performed on raw material and composite specimens to establish specification requirements. Pre-test and post-test microstructural examination and nondestructive analyses were conducted to determine the effect of material variations on fatigue durability and failure mode. Relevant data were acquired with respect to design analysis, materials properties, inspection standards, improved durability, weight benefits, and part price of the composite fan exit guide vane.

Acousto-ultrasonic evaluation of ceramic matrix composite materials

NASA Technical Reports Server (NTRS)

Dosreis, Henrique L. M.

1991-01-01

Acousto-ultrasonic nondestructive evaluation of ceramic composite specimens with a lithium-alumino-silicate glass matrix reinforced with unidirectional silicon carbide (NICALON) fibers was conducted to evaluate their reserve of strength. Ceramic composite specimens with different amount of damage were prepared by four-point cyclic fatigue loading of the specimens at 500 C for a different number of cycles. The reserve of strength of the specimens was measured as the maximum bending stress recorded during four-pointed bending test with the load monotonically increased until failure occurs. It was observed that the reserve of strength did not correlate with the number of fatigue cycles. However, it was also observed that higher values of the stress wave factor measurements correspond to higher values of the reserve of strength test data. Therefore, these results show that the acousto-ultrasonic approach has the potential of being used to monitor damage and to estimate the reserve of strength of ceramic composites.
Tungsten wire-nickel base alloy composite development

NASA Technical Reports Server (NTRS)

Brentnall, W. D.; Moracz, D. J.

1976-01-01

Further development and evaluation of refractory wire reinforced nickel-base alloy composites is described. Emphasis was placed on evaluating thermal fatigue resistance as a function of matrix alloy composition, fabrication variables and reinforcement level and distribution. Tests for up to 1,000 cycles were performed and the best system identified in this current work was 50v/o W/NiCrAlY. Improved resistance to thermal fatigue damage would be anticipated for specimens fabricated via optimized processing schedules. Other properties investigated included 1,093 C (2,000 F) stress rupture strength, impact resistance and static air oxidation. A composite consisting of 30v/o W-Hf-C alloy fibers in a NiCrAlY alloy matrix was shown to have a 100-hour stress rupture strength at 1,093 C (2,000 F) of 365 MN/square meters (53 ksi) or a specific strength advantage of about 3:1 over typical D.S. eutectics.
Flight service evaluation of composite helicopter components

NASA Technical Reports Server (NTRS)

Mardoian, G. H.; Ezzo, M. B.

1986-01-01

This report presents an assessment of composite helicopter tail rotor spars and horizontal stabilizers, exposed to the effects of the environment, after up to five and a half years of commercial service. This evaluation is supported by test results of helicopter components and panels which have been exposed to outdoor environmental effects since September 1979. Full scale static and fatigue tests have been conducted on graphite/epoxy and Kevlar/epoxy composite components obtained from Sikorsky Model S-76 helicopters in commercial operations in the Gulf Coast region of Louisiana. Small scale static and fatigue tests are being conducted on coupons obtained from panels under exposure to outdoor conditions in Stratford, Connecticut and West Palm, Florida. The panel layups are representative of the S-76 components. Additionally, this report discusses the results of moisture absorption evaluations and strength tests on the S-76 components and composite panels with up to five years of outdoor exposure.
Monitoring the fracture behavior of SiCp/Al alloy composites using infrared lock-in thermography

NASA Astrophysics Data System (ADS)

Kordatos, E. Z.; Myriounis, D., P.; Hasan, S., T.; Matikas, T. E.

2009-03-01

his work deals with the study of fracture behavior of silicon carbide particle-reinforced (SiCp) A359 aluminum alloy matrix composites using an innovative nondestructive method based on lock-in thermography. The heat wave, generated by the thermo-mechanical coupling and the intrinsic energy dissipated during mechanical cyclic loading of the sample, was detected by an infrared camera. The coefficient of thermo-elasticity allows for the transformation of the temperature profiles into stresses. A new procedure was developed to determine the crack growth rate using thermographic mapping of the material undergoing fatigue: (a) The distribution of temperature and stresses at the surface of the specimen was monitored during the test. To this end, thermal images were obtained as a function of time and saved in the form of a movie. (b) The stresses were evaluated in a post-processing mode, along a series of equally spaced reference lines of the same length, set in front of the crack-starting notch. The idea was that the stress monitored at the location of a line versus time (or fatigue cycles) would exhibit an increase while the crack approaches the line, then attain a maximum when the crack tip was on the line. Due to the fact that the crack growth path could not be predicted and was not expected to follow a straight line in front of the notch, the stresses were monitored along a series of lines of a certain length, instead of a series of equally spaced points in front of the notch. The exact path of the crack could be easily determined by looking at the stress maxima along each of these reference lines. The thermographic results on the crack growth rate of the metal matrix composite (MMC) samples with three different heat treatments were correlated with measurements obtained by the conventional compliance method, and found to be in agreement.
Can the Fatigue Severity Scale 7-item version be used across different patient populations as a generic fatigue measure - a comparative study using a Rasch model approach

PubMed Central

2014-01-01

Background Fatigue is a disabling symptom associated with reduced quality of life in various populations living with chronic illnesses. The transfer of knowledge about fatigue from one group to another is crucial in both research and healthcare. Outcomes should be validly and reliably comparable between groups and should not be unduly influenced by diagnostic variations. The present study evaluates whether the Fatigue Severity Scale 7-item version (FSS-7) demonstrates similar item hierarchy across people with multiple sclerosis, stroke or HIV/AIDS to ensure valid comparisons between groups, and provide further evidence of internal scale validity. Methods A secondary comparative analysis was performed using data from three different studies of three different chronic illnesses: multiple sclerosis, stroke and HIV/AIDS. Each of these studies had previously concluded that the FSS-7 has better psychometric properties than the original FSS for measuring fatigue interference. Data from 224 people with multiple sclerosis, 104 people with stroke and 316 people with HIV/AIDS were examined. Item response theory and a Rasch model were chosen to analyze the similarity of the FSS-7 item hierarchy across the three diagnostic groups Results Cross-sample differences were found for items #3, #5, #6 and #9 for two of the three samples, which raise questions about item validity across groups. However, disease-specific and disease-generic Rasch measures were similar across samples, indicating that individual fatigue interference measures in these three chronic illnesses might still be reliably comparable using the FSS-7. Conclusions Some items performed differently between the three samples but did not bias person measures, thereby indicating that fatigue interference in these illnesses might still be reliably compared using FSS-7 scores. However, caution is warranted when comparing fatigue raw sum scores directly across diagnostic groups using the FSS-7. Further studies of the scale are needed in other types of chronic illnesses. PMID:24559076
Characterizing Fatigue: The Effects of Ethnicity and Acculturation

PubMed Central

Cordero, Elizabeth D.; Loredo, Jose S.; Murray, Kate E.; Dimsdale, Joel E.

2012-01-01

It is unknown if fatigue measures like the Multidimensional Fatigue Symptom Inventory-Short Form (MFSI-SF; Stein, Jacobsen, Blanchard, & Thors, 2004) appropriately describe fatigue in Hispanics or if acculturation plays a role in fatigue. This study compared fatigue in community samples of Hispanics and Anglos. The MFSI-SF and pertinent questionnaires were administered to adults in San Diego County via telephone survey. Some differences in fatigue were observed in initial comparisons between Hispanics and Anglos, including when acculturation was considered. When age and education were controlled, Hispanics reported less general fatigue than Anglos, regardless of acculturation status, p = < .01. Exploratory factor analyses indicate that the MFSI-SF general-fatigue subscale was problematic for Hispanics. Implications, limitations, and future directions are discussed. PMID:22773899
Mean stress and the exhaustion of fatigue-damage resistance

NASA Technical Reports Server (NTRS)

Berkovits, Avraham

1989-01-01

Mean-stress effects on fatigue life are critical in isothermal and thermomechanically loaded materials and composites. Unfortunately, existing mean-stress life-prediction methods do not incorporate physical fatigue damage mechanisms. An objective is to examine the relation between mean-stress induced damage (as measured by acoustic emission) and existing life-prediction methods. Acoustic emission instrumentation has indicated that, as with static yielding, fatigue damage results from dislocation buildup and motion until dislocation saturation is reached, after which void formation and coalescence predominate. Correlation of damage processes with similar mechanisms under monotonic loading led to a reinterpretation of Goodman diagrams for 40 alloys and a modification of Morrow's formulation for life prediction under mean stresses. Further testing, using acoustic emission to monitor dislocation dynamics, can generate data for developing a more general model for fatigue under mean stress.
The theoretical and experimental study of a material structure evolution in gigacyclic fatigue regime

NASA Astrophysics Data System (ADS)

Plekhov, Oleg; Naimark, Oleg; Narykova, Maria; Kadomtsev, Andrey; Betekhtin, Vladimir

2015-10-01

The work is devoted to the study of the metal structure evolution under gigacyclic fatigue (VHCF) regime. The study of the mechanical properties of the samples (Armco iron) with different state of life time existing was carried out on the base of the acoustic resonance method. The damage accumulation (porosity of the samples) was studied by the hydrostatic weighing method. A statistical model of damage accumulation was proposed in order to describe the damage accumulation process. The model describes the influence of the sample surface on the location of fatigue crack initiation.
The Influence of Porosity on Fatigue Crack Initiation in Additively Manufactured Titanium Components.

PubMed

Tammas-Williams, S; Withers, P J; Todd, I; Prangnell, P B

2017-08-04

Without post-manufacture HIPing the fatigue life of electron beam melting (EBM) additively manufactured parts is currently dominated by the presence of porosity, exhibiting large amounts of scatter. Here we have shown that the size and location of these defects is crucial in determining the fatigue life of EBM Ti-6Al-4V samples. X-ray computed tomography has been used to characterise all the pores in fatigue samples prior to testing and to follow the initiation and growth of fatigue cracks. This shows that the initiation stage comprises a large fraction of life (>70%). In these samples the initiating defect was often some way from being the largest (merely within the top 35% of large defects). Using various ranking strategies including a range of parameters, we found that when the proximity to the surface and the pore aspect ratio were included the actual initiating defect was within the top 3% of defects ranked most harmful. This lays the basis for considering how the deposition parameters can be optimised to ensure that the distribution of pores is tailored to the distribution of applied stresses in additively manufactured parts to maximise the fatigue life for a given loading cycle.
A Rasch Analysis of Assessments of Morning and Evening Fatigue in Oncology Patients Using the Lee Fatigue Scale.

PubMed

Lerdal, Anners; Kottorp, Anders; Gay, Caryl; Aouizerat, Bradley E; Lee, Kathryn A; Miaskowski, Christine

2016-06-01

To accurately investigate diurnal variations in fatigue, a measure needs to be psychometrically sound and demonstrate stable item function in relationship to time of day. Rasch analysis is a modern psychometric approach that can be used to evaluate these characteristics. To evaluate, using Rasch analysis, the psychometric properties of the Lee Fatigue Scale (LFS) in a sample of oncology patients. The sample comprised 587 patients (mean age 57.3 ± 11.9 years, 80% women) undergoing chemotherapy for breast, gastrointestinal, gynecological, or lung cancer. Patients completed the 13-item LFS within 30 minutes of awakening (i.e., morning fatigue) and before going to bed (i.e., evening fatigue). Rasch analysis was used to assess validity and reliability. In initial analyses of differential item function, eight of the 13 items functioned differently depending on whether the LFS was completed in the morning or in the evening. Subsequent analyses were conducted separately for the morning and evening fatigue assessments. Nine of the morning fatigue items and 10 of the evening fatigue items demonstrated acceptable goodness-of-fit to the Rasch model. Principal components analyses indicated that both morning and evening assessments demonstrated unidimensionality. Person-separation indices indicated that both morning and evening fatigue scales were able to distinguish four distinct strata of fatigue severity. Excluding four items from the morning fatigue scale and three items from the evening fatigue scale improved the psychometric properties of the LFS for assessing diurnal variations in fatigue severity in oncology patients. Copyright © 2016 American Academy of Hospice and Palliative Medicine. Published by Elsevier Inc. All rights reserved.
Large Area Nondestructive Evaluation of a Fatigue Loaded Composite Structure

NASA Technical Reports Server (NTRS)

Zalameda, Joseph N.; Burke, Eric R.; Horne, Michael R.; Madaras, Eric I.

2016-01-01

Large area nondestructive evaluation (NDE) inspections are required for fatigue testing of composite structures to track damage initiation and growth. Of particular interest is the progression of damage leading to ultimate failure to validate damage progression models. In this work, passive thermography and acoustic emission NDE were used to track damage growth up to failure of a composite three-stringer panel. Fourteen acoustic emission sensors were placed on the composite panel. The signals from the array were acquired simultaneously and allowed for acoustic emission location. In addition, real time thermal data of the composite structure were acquired during loading. Details are presented on the mapping of the acoustic emission locations directly onto the thermal imagery to confirm areas of damage growth leading to ultimate failure. This required synchronizing the acoustic emission and thermal data with the applied loading. In addition, processing of the thermal imagery which included contrast enhancement, removal of optical barrel distortion and correction of angular rotation before mapping the acoustic event locations are discussed.
Microstructural evaluation of cumulative fatigue damage below the fatigue limit

DOE Office of Scientific and Technical Information (OSTI.GOV)

Fukuoka, C.; Nakagawa, Y.G.

1996-05-01

The objective of this work is to evaluate the microstructural changes induced near and below the fatigue limit in a pressure vessel steel plate, SA508. Dislocation cell to cell misorientation differences, {theta}, which increase with fatigue damage accumulation, are measured by the Selected Area Diffraction (SAD) method. The misorientation difference, {theta}, of the sample failed just above the fatigue limit is about 4.0 degrees on the average, which is about the same as that for the failure conditions of low cycle fatigue at higher stresses. The {theta} value increases even below the fatigue limit, but it does not increase atmore » stresses which are lower than 50% of the fatigue limit.« less
Development of a patient reported outcome scale for fatigue in multiple sclerosis: The Neurological Fatigue Index (NFI-MS)

PubMed Central

2010-01-01

Background Fatigue is a common and debilitating symptom in multiple sclerosis (MS). Best-practice guidelines suggest that health services should repeatedly assess fatigue in persons with MS. Several fatigue scales are available but concern has been expressed about their validity. The objective of this study was to examine the reliability and validity of a new scale for MS fatigue, the Neurological Fatigue Index (NFI-MS). Methods Qualitative analysis of 40 MS patient interviews had previously contributed to a coherent definition of fatigue, and a potential 52 item set representing the salient themes. A draft questionnaire was mailed out to 1223 people with MS, and the resulting data subjected to both factor and Rasch analysis. Results Data from 635 (51.9% response) respondents were split randomly into an 'evaluation' and 'validation' sample. Exploratory factor analysis identified four potential subscales: 'physical', 'cognitive', 'relief by diurnal sleep or rest' and 'abnormal nocturnal sleep and sleepiness'. Rasch analysis led to further item reduction and the generation of a Summary scale comprising items from the Physical and Cognitive subscales. The scales were shown to fit Rasch model expectations, across both the evaluation and validation samples. Conclusion A simple 10-item Summary scale, together with scales measuring the physical and cognitive components of fatigue, were validated for MS fatigue. PMID:20152031
Chronic fatigue in developing countries: population based survey of women in India.

PubMed

Patel, Vikram; Kirkwood, Betty R; Weiss, Helen; Pednekar, Sulochana; Fernandes, Janice; Pereira, Bernadette; Upadhye, Medha; Mabey, David

2005-05-21

To describe the prevalence of and risk factors for chronic fatigue in a developing country; in particular, to determine the association of anaemia, mental health, and gender disadvantage factors with chronic fatigue. Community survey. Primary health centre catchment area in Goa, India. 3000 randomly sampled women aged 18 to 50 years. Data on the primary outcome (reporting of fatigue for at least six months) and psychosocial exposures elicited by structured interview; presence of anaemia determined from a blood sample. 2494 (83%) women consented to participate; 12.1% (95% confidence interval 10.8 to 13.4%) complained of chronic fatigue. In multivariate analyses, older women (P = 0.03) and those experiencing socioeconomic deprivation-less education (P < 0.001), families in debt (P = 0.09), or hunger in the past three months (P = 0.03)-were more likely to report chronic fatigue. After adjustment for these factors, factors indicating gender disadvantage (notably sexual violence by the husband; P < 0.001) and poor mental health (P < 0.001) were strongly associated with chronic fatigue. Although women with a high body mass index had a reduced risk, suggesting an influence of poor nutrition, no association was found between chronic fatigue and haemoglobin concentrations. Chronic fatigue was commonly reported by women in this community study from India. The strongest associations with chronic fatigue were for psychosocial factors indicative of poor mental health and gender disadvantage.
Psychometric Evaluation of the Multidimensional Assessment of Fatigue Scale for Use with Pregnant and Postpartum Women

ERIC Educational Resources Information Center

Fairbrother, Nichole; Hutton, Eileen K.; Stoll, Kathrin; Hall, Wendy; Kluka, Sandy

2008-01-01

Although fatigue is a common experience for pregnant women and new mothers, few measures of fatigue have been validated for use with this population. To address this gap, the authors assessed psychometric properties of the Multidimensional Assessment of Fatigue (MAF) scale, which was used in 2 independent samples of pregnant women. Results…
Guidelines for VCCT-Based Interlaminar Fatigue and Progressive Failure Finite Element Analysis

NASA Technical Reports Server (NTRS)

Deobald, Lyle R.; Mabson, Gerald E.; Engelstad, Steve; Prabhakar, M.; Gurvich, Mark; Seneviratne, Waruna; Perera, Shenal; O'Brien, T. Kevin; Murri, Gretchen; Ratcliffe, James;

2017-01-01

This document is intended to detail the theoretical basis, equations, references and data that are necessary to enhance the functionality of commercially available Finite Element codes, with the objective of having functionality better suited for the aerospace industry in the area of composite structural analysis. The specific area of focus will be improvements to composite interlaminar fatigue and progressive interlaminar failure. Suggestions are biased towards codes that perform interlaminar Linear Elastic Fracture Mechanics (LEFM) using Virtual Crack Closure Technique (VCCT)-based algorithms [1,2]. All aspects of the science associated with composite interlaminar crack growth are not fully developed and the codes developed to predict this mode of failure must be programmed with sufficient flexibility to accommodate new functional relationships as the science matures.

Structural design significance of tension-tension fatigue data on composites

NASA Technical Reports Server (NTRS)

Grimes, G. C.

1977-01-01

Constant cycle tension-tension fatigue and related static tension data have been generated on six single composite material/orientation combinations and twenty-one hybrid composite material/orientation combinations. Anomalies are related to the temperature rise and stopped interval creep, whereas endurance limit stresses (runouts) are associated with static proportional limit values, when they occur, and internal damage. The significance of these room temperature-dry data on the design allowables and weight of aerodynamic structueres is discussed. Such structures are helicopter rotor blades and wing and horizontal stabilizer lower surfaces. Typical criteria for turning these data into preliminary allowables are shown, as are examples of such allowables developed from the data. These values are then compared to those that might be used if the structures were made of metal.
Durability and Damage Tolerance of High Temperature Polymeric Composites

NASA Technical Reports Server (NTRS)

Case, Scott W.; Reifsnider, Kenneth L.

1996-01-01

Modern durability and damage tolerance predictions for composite material systems rely on accurate estimates of the local stress and material states for each of the constituents, as well as the manner in which the constituents interact. In this work, an number of approaches to estimating the stress states and interactions are developed. First, an elasticity solution is presented for the problem of a penny-shaped crack in an N-phase composite material system opened by a prescribed normal pressure. The stress state around such a crack is then used to estimate the stress concentrations due to adjacent fiber fractures in composite materials. The resulting stress concentrations are then used to estimate the tensile strength of the composite. The predicted results are compared with experimental values. In addition, a cumulative damage model for fatigue is presented. Modifications to the model are made to include the effects of variable amplitude loading. These modifications are based upon the use of remaining strength as a damage metric and the definition of an equivalent generalized time. The model is initially validated using results from the literature. Also, experimental data from APC-2 laminates and IM7/K3B laminates are used in the model. The use of such data for notched laminates requires the use of an effective hole size, which is calculated based upon strain distribution measurements. Measured remaining strengths after fatigue loading are compared with the predicted values for specimens fatigued at room temperature and 350 F (177 C).
An Abnormal Increase of Fatigue Life with Dwell Time during Creep-Fatigue Deformation for Directionally Solidified Ni-Based Superalloy DZ445

NASA Astrophysics Data System (ADS)

Ding, Biao; Ren, Weili; Deng, Kang; Li, Haitao; Liang, Yongchun

2018-03-01

The paper investigated the creep-fatigue behavior for directionally solidified nickel-based superalloy DZ445 at 900 °C. It is found that the fatigue life shows an abnormal increase when the dwell time exceeds a critical value during creep-fatigue deformation. The area of hysteresis loop and fractograph explain the phenomenon quite well. The shortest life corresponds to the maximal area of hysteresis loop, i. e. the maximum energy to be consumed during the creep-fatigue cycle. The fractographic observation of failed samples further supports the abnormal behavior of fatigue life.
New method of determination of spot welding-adhesive joint fatigue life using full field strain evolution

NASA Astrophysics Data System (ADS)

Sadowski, T.; Kneć, M.

2016-04-01

Fatigue tests were conducted since more than two hundred years ago. Despite this long period, as fatigue phenomena are very complex, assessment of fatigue response of standard materials or composites still requires a long time. Quite precise way to estimate fatigue parameters is to test at least 30 standardized specimens for the analysed material and further statistical post processing is required. In case of structural elements analysis like hybrid joints (Figure 1), the situation is much more complex as more factors influence the fatigue load capacity due to much more complicated structure of the joint in comparison to standard materials specimen, i.e. occurrence of: welded hot spots or rivets, adhesive layers, local notches creating the stress concentrations, etc. In order to shorten testing time some rapid methods are known: Locati's method [1] - step by step load increments up to failure, Prot's method [2] - constant increase of the load amplitude up to failure; Lehr's method [2] - seeking for the point during regular fatigue loading when an increase of temperature or strains become non-linear. The present article proposes new method of the fatigue response assessment - combination of the Locati's and Lehr's method.

Some links on this page may take you to non-federal websites. Their policies may differ from this site.