Effects of oxygen plasma treatment on domestic aramid fiber III reinforced bismaleimide composite interfacial properties

NASA Astrophysics Data System (ADS)

Shi, Chen; Wang, Jing; Chen, Ping; Feng, Jiayue; Cui, Jinyuan; Yang, Faze

2017-12-01

Domestic Aramid Fiber III (DAF III) was modified by oxygen plasma treatment. The fiber surface characteristics was observed by Scanning Electron Microscopy. The results showed that oxygen plasma treatment changed surface morphologies. The effects of oxygen plasma treatment on DAF III reinforced bismaleimides (BMI) composite bending and interfacial properties were investigated, respectively. The ILSS value increased from 49.3 MPa to 56.0 MPa (by 13.5%) after oxygen plasma treatment. The bending strength changed a little. Furthermore, the composite rupture mode changed from interfacial rupture to fiber or resin bulk rupture.

Influence of Surface Modification on the Microstructure and Thermo-Mechanical Properties of Bamboo Fibers

PubMed Central

Zhang, Xiaoping; Wang, Fang; Keer, Leon M.

2015-01-01

The objective of this study is to investigate the effect of surface treatment on the morphology and thermo-mechanical properties of bamboo fibers. The fibers are subjected to an alkali treatment using 4 wt % sodium hydroxide (NaOH) for 1 h. Mechanical measurements show that the present concentration has an insignificant effect on the fiber tensile strength. In addition, systematic experimental results characterizing the morphological aspects and thermal properties of the bamboo fibers are analyzed by scanning electron microscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis, and differential scanning calorimetry. It is found that an alkali treatment may increase the effective surface area, which is in turn available for superior bonding with the matrix. Fourier transform infrared spectroscopy analysis reveals that the alkali treatment leads to a gradual removal of binding materials, such as hemicellulose and lignin from the bamboo fiber. A comparison of the curve of thermogravimetric analysis and differential scanning calorimetry for the treated and untreated samples is presented to demonstrate that the presence of treatment contributes to a better thermal stability for bamboo fibers. PMID:28793585

Surface roughness analysis of fiber post conditioning processes.

PubMed

Mazzitelli, C; Ferrari, M; Toledano, M; Osorio, E; Monticelli, F; Osorio, R

2008-02-01

The chemo-mechanical surface treatment of fiber posts increases their bonding properties. The combined use of atomic force and confocal microscopy allows for the assessment and quantification of the changes on surface roughness that justify this behavior. Quartz fiber posts were conditioned with different chemicals, as well as by sandblasting, and by an industrial silicate/silane coating. We analyzed post surfaces by atomic force microscopy, recording average roughness (R(a)) measurements of fibers and resin matrix. A confocal image profiler allowed for the quantitative assessment of the average superficial roughness (R(a)). Hydrofluoric acid, potassium permanganate, sodium ethoxide, and sandblasting increased post surface roughness. Modifications of the epoxy resin matrix occurred after the surface pre-treatments. Hydrofluoric acid affected the superficial texture of quartz fibers. Surface-conditioning procedures that selectively react with the epoxy-resin matrix of the fiber post enhance roughness and improve the surface area available for adhesion by creating micro-retentive spaces without affecting the post's inner structure.

Surface characterization in composite and titanium bonding: Carbon fiber surface treatments for improved adhesion to thermoplastic polymers

NASA Technical Reports Server (NTRS)

Devilbiss, T. A.; Wightman, J. P.

1987-01-01

The effect of anodization in NaOH, H2SO4, and amine salts on the surface chemistry of carbon fibers was examined by X-ray photoelectron spectroscopy (XPS). The surfaces of carbon fibers after anodization in NaOH and H2SO4 were examined by scanning transmission electron microscopy (STEM), angular dependent XPS, UV absorption spectroscopy of the anodization bath, secondary ion mass spectrometry, and polar/dispersive surface energy analysis. Hercules AS-4, Dexter Hysol XAS, and Union Carbide T-300 fibers were examined by STEM, angular dependent XPS, and breaking strength measurement before and after commercial surface treatment. Oxygen and nitrogen were added to the fiber surfaces by anodization in amine salts. Analysis of the plasmon peak in the carbon 1s signal indicated that H2SO4 anodization affected the morphological structure of the carbon fiber surface. The work of adhesion of carbon fibers to thermoplastic resins was calculated using the geometric mean relationship. A correlation was observed between the dispersive component of the work of adhesion and the interfacial adhesion.

Basic analytical investigation of plasma-chemically modified carbon fibers1

NASA Astrophysics Data System (ADS)

Bubert, H.; Ai, X.; Haiber, S.; Heintze, M.; Brüser, V.; Pasch, E.; Brandl, W.; Marginean, G.

2002-10-01

The background of the present investigation is to enhance the overall adherence of vapor grown carbon fibers (VGCF) to the surrounding polymer matrix in different applications by forming polar groups at their surfaces and by modifying the surface morphology. This has been done by plasma treatments using a low-pressure plasma with different gases, flow rates, pressures and powers. Two different types of carbon fibers were investigated: carbon microfibers and carbon nanofibers. The characterization of fiber surfaces was achieved by photoelectron spectroscopy (XPS), contact angle measurements and titration. These investigations were accompanied by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The oxygen plasma treatment of the fibers changes the surfaces by forming a layer with a thickness of the order of one nanometer mainly consisting of functional groups like hydroxyl, carbonyl and carboxyl. After functionalization of the complete surface, a further plasma treatment does not enhance the superficial oxygen content but changes slightly the portions of the functional groups. A comparison of the methods applied provides a largely consistent image of the effect of plasma treatment.

Heterogeneous nucleation of a semicrystalline polymer on fiber surfaces

Treesearch

Sangyeob Lee; Todd f. Shupe; Leslie h. Groom; Chung Y. Hse

2006-01-01

Nucleation phenomenon as affected by the surface conditions of six identical wood/non-wood fibers with three levels of fiber treatments were investigated by a combination of complementary techniques. This study was based on results of a preliminary study on the influence of surface characteristics of thermomechanical pulp (TMP) fibers on the transcrystalline layer (TLC...

Surface treatment of CFRP composites using femtosecond laser radiation

NASA Astrophysics Data System (ADS)

Oliveira, V.; Sharma, S. P.; de Moura, M. F. S. F.; Moreira, R. D. F.; Vilar, R.

2017-07-01

In the present work, we investigate the surface treatment of carbon fiber-reinforced polymer (CFRP) composites by laser ablation with femtosecond laser radiation. For this purpose, unidirectional carbon fiber-reinforced epoxy matrix composites were treated with femtosecond laser pulses of 1024 nm wavelength and 550 fs duration. Laser tracks were inscribed on the material surface using pulse energies and scanning speeds in the range 0.1-0.5 mJ and 0.1-5 mm/s, respectively. The morphology of the laser treated surfaces was investigated by field emission scanning electron microscopy. We show that, by using the appropriate processing parameters, a selective removal of the epoxy resin can be achieved, leaving the carbon fibers exposed. In addition, sub-micron laser induced periodic surface structures (LIPSS) are created on the carbon fibers surface, which may be potentially beneficial for the improvement of the fiber to matrix adhesion in adhesive bonds between CFRP parts.

Graphite fiber surface treatment to improve impact strength and fracture resistance in subsequent composites

NASA Technical Reports Server (NTRS)

Paul, J. T., Jr.; Buntin, G. A.

1982-01-01

Graphite (or carbon) fiber composite impact strength improvement was attempted by modifying the fiber surface. Elastomeric particles were made into lattices and deposited ionically on surface treated graphite fiber in an attempt to prepare a surface containing discrete rubber particles. With hard, nonelastomeric polystyrene discrete particle coverage was achieved. All the elastomeric containing lattices resulted in elastomer flow and filament agglomeration during drying.

Influence of airborne-particle abrasion on mechanical properties and bond strength of carbon/epoxy and glass/bis-GMA fiber-reinforced resin posts.

PubMed

Soares, Carlos Jose; Santana, Fernanda Ribeiro; Pereira, Janaina Carla; Araujo, Tatiana Santos; Menezes, Murilo Souza

2008-06-01

Controversy exists concerning the use of fiber-reinforced posts to improve bond strength to resin cement because some precementation treatments can compromise the mechanical properties of the posts. The purpose of this study was to analyze the influence of airborne-particle abrasion on the mechanical properties and microtensile bond strength (MTBS) of carbon/epoxy and glass/bis-GMA fiber-reinforced resin posts. Flexural strength (delta(f)), flexural modulus (E(f)), and stiffness (S) were assessed using a 3-point bending test for glass fiber-reinforced and carbon fiber-reinforced resin posts submitted to airborne-particle abrasion (AB) with 50-microm Al(2)O(3), and for posts without any surface treatment (controls) (n=10). Forty glass fiber (GF) and 40 carbon fiber (CF) posts were submitted to 1 of 4 surface treatments (n=10) prior to MTBS testing: silane (S); silane and adhesive (SA); airborne-particle abrasion with 50-microm Al(2)O(3) and silane (ABS); airborne-particle abrasion, silane, and adhesive (ABSA). Two composite resin restorations (Filtek Z250) with rounded depressions in the lateral face were bilaterally fixed to the post with resin cement (RelyX ARC). Next, the specimen was sectioned with a precision saw running perpendicular to the bonded surface to obtain 10 bonded beam specimens with a cross-sectional area of 1 mm(2). Each beam specimen was tested in a mechanical testing machine (EMIC 2,000 DL), under stress, at a crosshead speed of 0.5 mm/min until failure. Data were analyzed by 2-way ANOVA followed by Tukey HSD test (alpha=.05). Failure patterns of tested specimens were analyzed using scanning electron microscopy (SEM). The 3-point bending test demonstrated significant differences among groups only for the post type factor for flexural strength, flexural modulus, and stiffness. The carbon fiber posts exhibited significantly higher mean flexural strength (P=.001), flexural modulus (P=.003), and stiffness (P=.001) values when compared with glass fiber posts, irrespective of surface treatment. An alteration in the superficial structure of the posts could be observed by SEM after airborne-particle abrasion. MTBS testing showed no significant effect for the surface treatment type; however, significant effects for post system factor and for interaction between the 2 factors were observed. For the carbon fiber post, the ABSA surface treatment resulted in values significantly lower than the S surface treatment. SEM analysis of MTBS-tested specimens demonstrated adhesive and cohesive failures. Airborne-particle abrasion did not influence the mechanical properties of the post; however, it produced undesirable surface changes, which could reduce the bond strength to resin cement. For the surface treatments studied, if silane is applied, the adhesive system and airborne-particle abrasion are not necessary.

Oxidation of carbon fiber surfaces for use as reinforcement in high-temperature cementitious material systems

DOEpatents

Sugama, Toshifumi

1990-01-01

The interfacial bond characteristics between carbon fiber and a cement matrix, in high temperature fiber-reinforced cementitious composite systems, can be improved by the oxidative treatment of the fiber surfaces. Compositions and the process for producing the compositions are disclosed.

Improving degradation resistance of sisal fiber in concrete through fiber surface treatment

NASA Astrophysics Data System (ADS)

Wei, Jianqiang; Meyer, Christian

2014-01-01

As part of an ongoing effort to improve the sustainability of reinforced concrete, recycled concrete aggregate is being considered together with natural fibers such as sisal fiber as replacement of synthetic reinforcement. Since natural fibers are known to undergo potential deterioration in the alkaline cement matrix especially in outdoor erosive environment, they need to be treated to improve their durability. This paper describes two such methods (thermal and Na2CO3 treatment) and evaluates their effects on the degradation resistance of sisal fiber and durability of sisal fiber-reinforced concrete with recycled concrete aggregate. Concrete specimens were subjected to cycles of wetting and drying to accelerate aging. The microstructure, tensile strength and Young's modulus of sisal fiber as well as the weight loss of the composite were evaluated. Of primary interest were the effects on compressive and splitting tensile strength of sisal fiber-reinforced concrete. Thermal treatment and Na2CO3 surface treatment were shown to improve the durability of the composite as measured by splitting tensile strength by 36.5% and 46.2% and the compressive strength by 31.1% and 45.4%, respectively. The mechanisms of these two treatment methods were also analyzed. The thermal treatment achieved improvement of cellulose's crystallization, which ensured the initial strength and improved durability of sisal fiber. A layer consisting of calcium carbonate sediments, which protects the internals of a fiber from the strong alkali solution formed in the cement hydration process, was formed and filled in pits and cavities on the Na2CO3 treated sisal fiber's surface to improve their corrosion resistance and durability and reduced the detrimental effects of Na+ ions on concrete.

Kenaf Bast Fibers—Part II: Inorganic Nanoparticle Impregnation for Polymer Composites

DOE PAGES

Shi, Jinshu; Shi, Sheldon Q.; Barnes, H. Michael; ...

2011-01-01

The objective of this study was to investigate an inorganic nanoparticle impregnation (INI) technique to improve the compatibility between kenaf bast fibers and polyolefin matrices. The Scanning Electron Microscopy (SEM) was used to examine the surface morphology of the INI-treated fibers showing that the CaCO 3 nanoparticle crystals grew onto the fiber surface. Energy-dispersive X-ray spectroscopy (EDS) was used to verify the CaCO 3 nanoparticle deposits on the fiber surface. The tension tests of the individual fiber were conducted, and the results showed that the tensile strength of the fibers increased significantly (more than 20%) after the INI treatments. Polymermore » composites were fabricated using the INI-treated fiber as reinforcement and polypropylene (PP) as the matrix. The results showed that the INI treatments improved the compatibility between kenaf fibers and PP matrix. The tensile modulus and tensile strength of the composites reinforced with INI-treated fibers increased by 25.9% and 10.4%, respectively, compared to those reinforced with untreated kenaf fibers.« less

Oxidation of carbon fiber surfaces for use as reinforcement in high-temperature cementitious material systems

DOEpatents

Sugama, Toshifumi.

1990-05-22

The interfacial bond characteristics between carbon fiber and a cement matrix, in high temperature fiber-reinforced cementitious composite systems, can be improved by the oxidative treatment of the fiber surfaces. Compositions and the process for producing the compositions are disclosed. 2 figs.

The influence of chemical surface modification of kenaf fiber using hydrogen peroxide on the mechanical properties of biodegradable kenaf fiber/poly(lactic acid) composites.

PubMed

Razak, Nur Inani Abdul; Ibrahim, Nor Azowa; Zainuddin, Norhazlin; Rayung, Marwah; Saad, Wan Zuhainis

2014-03-07

Bleaching treatment of kenaf fiber was performed in alkaline medium containing hydrogen peroxide solution maintained at pH 11 and 80 °C for 60 min. The bleached kenaf fiber was analyzed using Fourier Transform Infrared (FTIR) and X-ray Diffraction (XRD) analysis. The bleached kenaf fiber was then compounded with poly-(lactic acid) (PLA) via a melt blending method. The mechanical (tensile, flexural and impact) performance of the product was tested. The fiber treatment improved the mechanical properties of PLA/bleached kenaf fiber composites. Scanning electron micrograph (SEM) morphological analysis showed improvement of the interfacial adhesion between the fiber surface and polymer matrix.

What does nitric acid really do to carbon nanofibers? [What nitric acid really does to carbon nanofibers

DOE PAGES

Sainio, S.; Nordlund, D.; Gandhiraman, R.; ...

2016-09-15

Understanding the chemical nature of the surface of carbon nanofibers (CNF) is critical in assessing their fundamental properties and tailoring them for the right application. To gain such knowledge, we present here a detailed X-ray adsorption spectroscopy (XAS) study accompanied by high resolution transmission electron microscopy (TEM) micrographs of two morphologically different CNF pairs (tetrahedral amorphous carbon (ta-C) grown “open structured” fibers and traditional bamboo-like “closed structured” fibers), where the surface chemical properties and structural features of the fibers are investigated in depth and the effects of nitric acid treatment on the fibers are revealed. The morphology of the fibermore » and/or the original seed- and adhesion layers markedly affect the response of the fibers to the acid treatment. Results also show that the nitric acid treatment increases the observed sp 2 intensity and modifies the two types of fibers to become more-alike both structurally and with respect to their oxygen functionalities. Furthermore, the XAS and HRTEM results confirm that a short nitric acid treatment does not remove the Ni catalyst particle but, instead, oxidizes their surfaces, especially in the case of ta-C grown fibers.« less

What does nitric acid really do to carbon nanofibers? [What nitric acid really does to carbon nanofibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sainio, S.; Nordlund, D.; Gandhiraman, R.

Understanding the chemical nature of the surface of carbon nanofibers (CNF) is critical in assessing their fundamental properties and tailoring them for the right application. To gain such knowledge, we present here a detailed X-ray adsorption spectroscopy (XAS) study accompanied by high resolution transmission electron microscopy (TEM) micrographs of two morphologically different CNF pairs (tetrahedral amorphous carbon (ta-C) grown “open structured” fibers and traditional bamboo-like “closed structured” fibers), where the surface chemical properties and structural features of the fibers are investigated in depth and the effects of nitric acid treatment on the fibers are revealed. The morphology of the fibermore » and/or the original seed- and adhesion layers markedly affect the response of the fibers to the acid treatment. Results also show that the nitric acid treatment increases the observed sp 2 intensity and modifies the two types of fibers to become more-alike both structurally and with respect to their oxygen functionalities. Furthermore, the XAS and HRTEM results confirm that a short nitric acid treatment does not remove the Ni catalyst particle but, instead, oxidizes their surfaces, especially in the case of ta-C grown fibers.« less

Thermo-Oxidative Stability of Graphite/PMR-15 Composites: Effect of Fiber Surface Modification on Composite Shear Properties

NASA Technical Reports Server (NTRS)

Madhukar, Madhu S.; Bowles, Kenneth J.; Papadopolous, Demetrios S.

1994-01-01

Experiments were conducted to establish a correlation between the weight loss of a polyimide (PMR- 15) matrix and graphite fibers and the in-plane shear properties of their unidirectional composites subjected to different isothermal aging times up to 1000 hr at 316 C. The role of fiber surface treatment on the composite degradation during the thermo-oxidative aging was investigated by using A4 graphite fibers with three surface modifications: untreated (AU-4), surface treated (AS-4), and surface treated and sized with an epoxy-compatible sizing (AS-4G). The weight loss of the matrix fibers, and composites was determined during the aging. The effect of thermal aging was seen in all the fiber samples in terms of weight loss and reduction in fiber diameter. Calculated values of weight loss fluxes for different surfaces of rectangular unidirectional composite plates showed that the largest weight loss occurred at those cut surfaces where fibers were perpendicular to the surface. Consequently, the largest amount of damage was also noted on these cut surfaces. Optical observation of the neat matrix and composite plates subjected to different aging times revealed that the degradation (such as matrix microcracking and void growth) occurred in a thin surface layer near the specimen edges. The in-plane shear modulus of the composites was unaffected by the fiber surface treatment and the thermal aging. The shear strength of the composites with the untreated fibers was the lowest and it decreased with aging. A fracture surface examination of the composites with untreated fibers suggested that the weak interface allowed the oxidation reaction to proceed along the interface and thus expose the inner material to further oxidation. The results indicated that the fiber-matrix interface affected the composite degradation process during its thermal aging and that the the weak interface accelerated the composite degradation.

Effects of (Oxy-)Fluorination on Various High-Performance Yarns.

PubMed

Kruppke, Iris; Bartusch, Matthias; Hickmann, Rico; Hund, Rolf-Dieter; Cherif, Chokri

2016-08-26

In this work, typical high-performance yarns are oxy-fluorinated, such as carbon fibers, ultra-high-molecular-weight polyethylene, poly(p-phenylene sulfide) and poly(p-phenylene terephthalamide). The focus is on the property changes of the fiber surface, especially the wetting behavior, structure and chemical composition. Therefore, contact angle, XPS and tensile strength measurements are performed on treated and untreated fibers, while SEM is utilized to evaluate the surface structure. Different results for the fiber materials are observed. While polyethylene exhibits a relevant impact on both surface and bulk properties, polyphenylene terephthalamide and polyphenylene sulfide are only affected slightly by (oxy-)fluorination. The wetting of carbon fiber needs higher treatment intensities, but in contrast to the organic fibers, even its textile-physical properties are enhanced by the treatment. Based on these findings, the capability of (oxy-)fluorination to improve the adhesion of textiles in fiber-reinforced composite materials can be derived.

Effect of alkali treatment on the physical and surface properties of Indian hemp fibers

NASA Astrophysics Data System (ADS)

Sangappa, Rao, B. Lakshmeesha; Asha, S.; Somashekar, R.

2013-02-01

The Plant fibers are rich in cellulose and they are a cheap, easily renewable source of fibers with the potential for polymer reinforcement. The presence of surface impurities and the large amount of hydroxyl groups make plant fibers less attractive for reinforcement of polymeric materials. Hemp (Cannabis Sativa L.) fibers were subjected to alkalization using 1N sodium hydroxide (NaOH). The structural properties and surface morphology of untreated and chemically modified fibers have been studied using X-ray diffraction (WAXS) and Scanning electron microscopy (SEM) respectively.

Effect of surface treatments on the bond strength of CAD/CAM fiberglass posts.

PubMed

Garcia, Paula-Pontes; da Costa, Rogério-Goulart; Garcia, André-Vivan; Gonzaga, Carla-Castiglia; da Cunha, Leonardo-Fernandes; Rezende, Carlos-Eduardo-Edwards; Correr, Gisele-Maria

2018-06-01

There is no ideal protocol for the surface treatment of fiber posts, especially when using a computer-aided design/computer-aided manufacturing (CAD/CAM) experimental fiberglass block. The purpose of this study was to evaluate the bond strength of a CAD/CAM customized glass fiber post and core after applying different surface treatment techniques. Forty premolars were prepared to receive a customized CAD/CAM glass-fiber post and core obtained from an experimental block of glass fiber and epoxy resin. The specimens were randomly distributed in 4 groups (n=10) according to the post and core surface treatment: ETH - 70% ethanol; HP - 24% hydrogen peroxide for 1 minute; ETH/S - 70% ethanol + silane; HP/S - 24% hydrogen peroxide + silane. The universal adhesive containing silane was applied on the posts and prepared post spaces in all groups. The posts were cemented using dual cure resin cement. The specimens were stored in distilled water at 37°C for 24 h, cut (two slices of 1 mm for each root third - coronal, middle, and apical) and subjected to push-out test (0.5 mm/min). Data was subjected to two-way ANOVA (surface treatment and root third) and Tukey's test (α=0,05). There was no significant difference of bond strength values among groups, regardless the surface treatment ( p >0.05). There was significant difference on bond strength values for the different root thirds ( p <0.05) (coronal>middle=apical). The different surface treatment and application of additional silane in the CAD/CAM customized glass-fiber post and core does not interfere on bond strength values. The root dentin third interfered on the bond strength, with higher values for the coronal third. Key words: Post and core technique, cad/cam, shear strength, hydrogen peroxide.

Study on surface adhesion of Plasma modified Polytetrafluoroethylene hollow fiber membrane

NASA Astrophysics Data System (ADS)

Chen, Jiangrong; Zhang, Huifeng; Liu, Guochang; Guo, Chungang; Lv, Jinglie; Zhangb, Yushan

2018-01-01

Polytetrafluoroethylene (PTFE) is popular membrane material because of its excellent thermal stability, chemical stability and mechanical stability. However, the low surface energy and non-sticky property of PTFE present challenges for modification. In the present study, plasma treatment was performed to improve the surface adhesion of PTFE hollow fiber membrane. The effect of discharge voltage, treatment time on the adhesion of PTFE hollow fiber membrane was symmetrically evaluated. Results showed that the plasma treatment method contributed to improve the surface activity and roughness of PTFE hollow fiber membrane, and the adhesion strength depend significantly on discharge voltage, which was beneficial to seepage pressure of PTFE hollow fiber membrane module. The adhesion strength of PTFE membrane by plasma treated at 220V for 3min reached as high as 86.2 N, far surpassing the adhesion strength 12.7 N of pristine membrane. Furthermore, improvement of content of free radical and composition analysis changes of the plasma modified PTFE membrane were investigated. The seepage pressure of PTFE membrane by plasma treated at 220V for 3min was 0.375 MPa, which means that the plasma treatment is an effective technique to improve the adhesion strength of membrane.

Characterization of the interface between cellulosic fibers and a thermoplastic matrix

Treesearch

Feipeng P. Liu; Michael P. Wolcott; Douglas J. Gardner; Timothy G. Rials

1994-01-01

The applicability of the microbond test to evaluate the interfacial properties between cellulosic fibers and thermoplastics was studied. Acetylation and beat treatment were applied to modify the surface of cellulosic fibers (rayon, cotton, and wood). The apparent diameters and surface free energies of the fibers were estimated by dynamic contact angle (DCA) analysis....

Fracture surface analysis in composite and titanium bonding

NASA Technical Reports Server (NTRS)

Devilbiss, T. A.; Wightman, J. P.

1985-01-01

To understand the mechanical properties of fiber-reinforced composite materials, it is necessary to understand the mechanical properties of the matrix materials and of the reinforcing fibers. Another factor that can affect the mechanical properties of a composite material is the interaction between the fiber and the matrix. In general, composites with strong fiber matrix bonding will give higher modulus, lower toughness composites. Composites with weak bonding will have a lower modulus and more ductility. The situation becomes a bit more complex when all possibilities are examined. To be considered are the following: the properties of the surface layer on the fiber, the interactive forces between polymer and matrix, the surface roughness and porosity of the fiber, and the morphology of the matrix polymer at the fiber surface. In practice, the surface of the fibers is treated to enhance the mechanical properties of a composite. These treatments include anodization, acid etching, high temperature oxidation, and plasma oxidation, to name a few. The goal is to be able to predict the surface properties of carbon fibers treated in various ways, and then to relate surface properties to fiber matrix bonding.

A novel Ag catalyzation process using swelling impregnation method for electroless Ni deposition on Kevlar® fiber

NASA Astrophysics Data System (ADS)

Pang, Hongwei; Bai, Ruicheng; Shao, Qinsi; Gao, Yufang; Li, Aijun; Tang, Zhiyong

2015-12-01

A novel Ag catalyzation process using swelling impregnation pretreatment method was developed for electroless nickel (EN) deposition on Kevlar fiber. Firstly, the fiber was immersed into an aqueous dimethylsulfoxide (DMSO) solution of silver nitrate to impart silver nitrate into the inner part of the fiber near the surface. Subsequently silver nitrate was reduced to metal silver nanoparticles on the fiber surface by treatment with aqueous solution of sodium borohydride. After electroless plating, a dense and homogeneous nickel coating was obtained on the fiber surface. The silver nanoparticles formed at the fiber surface functioned as a catalyst for electroless deposition as well as an anchor for the plated layer. The study also revealed that the incorporation of surfactant sodium dodecyl sulfate (SDS) in electroless nickel plating bath can enhance the adhesion strength of EN layer with the fiber surface and minimize the surface roughness of the EN coating. The Ni plated Kevlar fiber possessed excellent corrosion resistance and high tensile strength.

Interfacial enhancement of carbon fiber/nylon 12 composites by grafting nylon 6 to the surface of carbon fiber

NASA Astrophysics Data System (ADS)

Hui, Chen; Qingyu, Cai; Jing, Wu; Xiaohong, Xia; Hongbo, Liu; Zhanjun, Luo

2018-05-01

Nylon 6 (PA6) grafted onto carbon fiber (CF) after chemical oxidation treatment was in an attempt to reinforce the mechanical properties of carbon fiber composites. Scanning electronic microscopy (SEM), Fourier transform infrared analysis (FT-IR), X-ray photoelectron spectroscope (XPS) and thermogravimetric analysis (TG) were selected to characterize carbon fibers with different surface treated. Experimental results showed that PA6 was grafted uniformly on the fiber surface through the anionic polymerization. A large number of functional groups were introduced to the fiber surface and the surface roughness was increased. After grafting PA6 on the oxidized carbon fibers, it played an important role on improving the interfacial adhesion between the fibers and the matrix by improving PA12 wettability, increasing chemical bonding and mechanical interlocking. Compared with the desized CF composites, the tensile strength of PA6-CF/PA12 composites was increased by 30.8% from 53.9 MPa to 70.2 MPa. All results indicated that grafting PA6 onto carbon fiber surface was an effective method to enhance the mechanical strength of carbon fiber/nylon 12 composites.

Effects of various etching protocols on the flexural properties and surface topography of fiber-reinforced composite dental posts.

PubMed

Aksornmuang, Juthatip; Chuenarrom, Chanya; Chittithaworn, Natjira

2017-09-26

The purpose of this study was to evaluate the flexural properties and surface topography of fiber posts surface-treated with various etching protocols. Seventy each of three types of fiber posts: RelyX Fiber Post, Tenax Fiber Trans, and D.T. Light-Post Illusion X-Ro, were randomly divided into 7 groups: no surface treatment, surface treated with hydrofluoric acid (HF) 4.5% for 60 s, HF 4.5% for 120 s, HF 9.6% for 15 s, HF 9.6% for 60 s, HF 9.6% for 120 s, and treated with H 2 O 2 24% for 10 min. The specimens were then subjected to a three-point bending test. Surface topographies of the posts were observed using a SEM. The results indicate that fiber post surface pretreatments had no adverse effects on the flexural properties. However, the fiber posts treated with high HF concentrations or long etching times seemed to have more surface irregularities.

Influence of surface defects on the tensile strength of carbon fibers

NASA Astrophysics Data System (ADS)

Vautard, F.; Dentzer, J.; Nardin, M.; Schultz, J.; Defoort, B.

2014-12-01

The mechanical properties of carbon fibers, especially their tensile properties, are affected by internal and surface defects. In order to asses in what extent the generation of surface defects can result in a loss of the mechanical properties, non-surface treated carbon fibers were oxidized with three different surface treatment processes: electro-chemical oxidation, oxidation in nitric acid, and oxidation in oxygen plasma. Different surface topographies and surface chemistries were obtained, as well as different types and densities of surface defects. The density of surface defects was measured with both a physical approach (Raman spectroscopy) and a chemical approach (Active Surface Area). The tensile properties were evaluated by determining the Weibull modulus and the scale parameter of each reference, after measuring the tensile strength for four different gauge lengths. A relationship between the tensile properties and the nature and density of surface defects was noticed, as large defects largely control the value of the tensile strength. When optimized, some oxidation surface treatment processes can generate surface functional groups as well as an increase of the mechanical properties of the fibers, because of the removal of the contamination layer of pyrolytic carbon generated during the carbonization of the polyacrylonitrile precursor. Oxidation in oxygen plasma revealed to be a promising technology for alternative surface treatment processes, as high levels of functionalization were achieved and a slight improvement of the mechanical properties was obtained too.

PET fiber fabrics modified with bioactive titanium oxide for bone substitutes.

PubMed

Kokubo, Tadashi; Ueda, Takahiro; Kawashita, Masakazu; Ikuhara, Yuichi; Takaoka, Gikan H; Nakamura, Takashi

2008-02-01

A rectangular specimen of polyethylene terephthalate (PET) was soaked in a titania solution composed of titanium isopropoxide, water, ethanol and nitric acid at 25 degrees C for 1 h. An amorphous titanium oxide was formed uniformly on the surface of PET specimen, but did not form an apatite on its surface in a simulated body fluid (SBF) within 3 d. The PET plate formed with the amorphous titanium oxide was subsequently soaked in water or HCl solutions with different concentrations at 80 degrees C for different periods of time. The titanium oxide on PET was transformed into nano-sized anatase by the water treatment and into nano-sized brookite by 0.10 M HCl treatment at 80 degrees C for 8 d. The former did not form the apatite on its surface in SBF within 3 d, whereas the latter formed the apatite uniformly on its surface. Adhesive strength of the titanium oxide and apatite layers to PET plate was increased by pre-treatment of PET with 2 wt% NaOH solution at 40 degrees C for 2 h. A two-dimensional fabric of PET fibers 24 microm in diameter was subjected to the NaOH pre-treatment at 40 degrees C, titania solution treatment at 25 degrees C and subsequent 0.10 M HCl treatment at 80 degrees C. Thus treated PET fabric formed the apatite uniformly on surfaces of individual fibers constituting the fabric in SBF within 3 d. Two or three dimensional PET fabrics modified with the nano-sized brookite on surfaces of the individual fibers constituting the fabric by the present method are believed to be useful as flexible bone substitutes, since they could be integrated with living bone through the apatite formed on their constituent fibers.

Effects of carbon fiber surface characteristics on interfacial bonding of epoxy resin composite subjected to hygrothermal treatments

NASA Astrophysics Data System (ADS)

Li, Min; Liu, Hongxin; Gu, Yizhuo; Li, Yanxia; Zhang, Zuoguang

2014-01-01

The changes of interfacial bonding of three types of carbon fibers/epoxy resin composite as well as their corresponding desized carbon fiber composites subjecting to hygrothermal conditions were investigated by means of single fiber fragmentation test. The interfacial fracture energy was obtained to evaluate the interfacial bonding before and after boiling water aging. The surface characteristics of the studied carbon fiber were characterized using X-ray photoelectron spectroscopy. The effects of activated carbon atoms and silicon element at carbon fiber surface on the interfacial hygrothermal resistance were further discussed. The results show that the three carbon fiber composites with the same resin matrix possess different hygrothermal resistances of interface and the interfacial fracture energy after water aging can not recovery to the level of raw dry sample (irreversible changes) for the carbon fiber composites containing silicon. Furthermore, the activated carbon atoms have little impact on the interfacial hygrothermal resistance. The irreversible variations of interfacial bonding and the differences among different carbon fiber composites are attributed to the silicon element on the carbon fiber bodies, which might result in hydrolyzation in boiling water treatment and degrade interfacial hygrothermal resistance.

Surface decoration of polyimide fiber with carbon nanotubes and its application for mechanical enhancement of phosphoric acid-based geopolymers

NASA Astrophysics Data System (ADS)

Yang, Tao; Han, Enlin; Wang, Xiaodong; Wu, Dezhen

2017-09-01

A new methodology to decorate the surface of polyimide (PI) fiber with carbon nanotubes (CNTs) has been developed in this study. This surface decoration was carried out through a surface alkali treatment, a carboxylation modification, surface functionalization with acyl chloride groups and then with amino groups, and a surface graft of CNTs onto PI fiber. Fourier-transform infrared and X-ray photoelectron spectroscopic characterizations confirmed that CNTs were chemically grafted onto the surface of PI fiber, and scanning electron microscopic observation demonstrated the fiber surface was uniformly and densely covered with CNTs. The surface energy and wettability of PI fiber were improved in the presence of CNTs on the fiber surface, which made a contribution to enhance the interfacial adhesion of PI fiber with other inorganic matrices when used as a reinforcing fiber. The application of CNTs-decorated PI fiber for the reinforcement of phosphoric acid-based geopolymers was investigated, and the results indicated that the geopolymeric composites gained a noticeable reinforcement. Compared to unreinforced geopolymer, the geopolymeric composites achieved a remarkable increase in compressive strength by 120% and in flexural strength by 283%. Fractography investigation demonstrated that the interaction adhesion between the fibers and matrix was enhanced due to the surface decoration of PI fiber with CNTs, which contributed to an improvement in fracture-energy dissipation by fiber pullout and fiber debonding from the matrix. As a result, a significant reinforcement effect on geopolymeric composites was achieved through a fiber-bridging mechanism. This study provided an effective methodology to improve the interracial bonding force for PI fiber and also proves a highly efficient application of CNTs-decorated PI fiber for the mechanical enhancement of geopolymeric composites.

Graphite fiber surface treatment to improve char retention and increase fiber clumping

NASA Technical Reports Server (NTRS)

Paul, J. T., Jr.; Weldy, W. E.

1980-01-01

Composites containing carbon and graphite fibers can release fibers into the atmosphere during a fire. This release can potentially cause failure in some types of electrical equipment. Reduced fiber dispersion during and after combustion will reduce risks. Epoxidized char forming systems were synthesized which will react with commercially available surface treated carbon fiber. Fibers modified with these char formers retained adhesion in a specific epoxy matrix resin. Small scale combustion testing indicates that using these char former modified fibers in laminates will help to reduce the dispersement of fibers resulting from exposure to fire without sacrificing resin to fiber adhesion.

Modification of glass fibers to improve reinforcement: a plasma polymerization technique.

PubMed

Cökeliler, Dilek; Erkut, Selim; Zemek, Josef; Biederman, Hynek; Mutlu, Mehmet

2007-03-01

This study evaluates the effect of plasma treated E-glass fiber to improve the mechanical properties of acrylic resin denture base material, polymethylmethacrlyate (PMMA). Plasma surface treatment of fibers is used as reinforcement in composite materials to modify the chemical and physical properties of their surfaces with tailored fiber-matrix bonding strength. Three different types of monomer 2-hydroxyethyl methacrylate (HEMA), triethyleneglycoldimethylether (TEGDME) and ethylenediamine (EDA) were used in the plasma polymerization modification of glass fibers. A radiofrequency generator was used to sustain plasma in a glass vacuum chamber. Glass fibers were modified at the same glow-discharge power of 25 W and exposure time of 30 min for each monomer. Fibers were incorporated into the acrylic with 1% (w/w) loading except control group. Specimens were prepared using a standard mold of 3 cmx0.5 cmx0.8 cm in dimension with eight specimens in each group. Samples were subjected to a flexural strength test set up at a crosshead speed of 5mm/min. Scanning electron microscopy (SEM) was used to examine the microstructure and X-ray photoelectron spectroscopy (XPS) was used for chemical analysis of the surface. Data were analyzed by means of ANOVA and Duncan's tests. Test results revealed that fiber reinforcement had a significant effect on the flexural strength of the specimens (p<0.05). Among the fiber reinforced groups, plasma treatment with EDA monomer resulted in the most significant increase in flexural strength values (p<0.05). XPS results have shown an increasing number of nitrogenous compounds in EDA treated fibers. The chemical structure of the surface, especially with the increase in nitrogenous compounds could give an idea for the amine film deposition and SEM figures showed an increase in surface roughness. The results showed that plasma treatment with EDA monomer was an effective alternative method of increasing the flexural strength of PMMA based denture base polymers through fiber reinforcement.

Effect of surface treatments on the bond strength of CAD/CAM fiberglass posts

PubMed Central

Garcia, Paula-Pontes; da Costa, Rogério-Goulart; Garcia, André-Vivan; Gonzaga, Carla-Castiglia; da Cunha, Leonardo-Fernandes; Rezende, Carlos-Eduardo-Edwards

2018-01-01

Background There is no ideal protocol for the surface treatment of fiber posts, especially when using a computer-aided design/computer-aided manufacturing (CAD/CAM) experimental fiberglass block. The purpose of this study was to evaluate the bond strength of a CAD/CAM customized glass fiber post and core after applying different surface treatment techniques. Material and Methods Forty premolars were prepared to receive a customized CAD/CAM glass-fiber post and core obtained from an experimental block of glass fiber and epoxy resin. The specimens were randomly distributed in 4 groups (n=10) according to the post and core surface treatment: ETH - 70% ethanol; HP - 24% hydrogen peroxide for 1 minute; ETH/S - 70% ethanol + silane; HP/S - 24% hydrogen peroxide + silane. The universal adhesive containing silane was applied on the posts and prepared post spaces in all groups. The posts were cemented using dual cure resin cement. The specimens were stored in distilled water at 37°C for 24 h, cut (two slices of 1 mm for each root third - coronal, middle, and apical) and subjected to push-out test (0.5 mm/min). Data was subjected to two-way ANOVA (surface treatment and root third) and Tukey’s test (α=0,05). Results There was no significant difference of bond strength values among groups, regardless the surface treatment (p >0.05). There was significant difference on bond strength values for the different root thirds (p<0.05) (coronal>middle=apical). Conclusions The different surface treatment and application of additional silane in the CAD/CAM customized glass-fiber post and core does not interfere on bond strength values. The root dentin third interfered on the bond strength, with higher values for the coronal third. Key words:Post and core technique, cad/cam, shear strength, hydrogen peroxide. PMID:29930778

The effect of oxygen-plasma treatment on Kevlar fibers and the properties of Kevlar fibers/bismaleimide composites

NASA Astrophysics Data System (ADS)

Su, Min; Gu, Aijuan; Liang, Guozheng; Yuan, Li

2011-02-01

The effect of oxygen-plasma treatment for Kevlar fibers on the interfacial adhesion and typical macro-properties of Kevlar fiber/bismaleimide composites was intensively studied. It is found that oxygen-plasma treatment significantly affects the interfacial adhesion by changing the chemistry and morphology of the surfaces of the fibers, and thus leading to improved interlaminar shear strength, water resistance and dielectric properties of the composites. However, the improvement is closely related to the treatment power and time. The best condition for treating Kevlar fiber is 70 W for 5 min. Oxygen-plasma treatment provides an effective technique for overcoming the poor interfacial adhesion of Kevlar fiber based composites, and thus showing great potential in fabricating high performance copper clad laminates.

The Effects of Fiber Surface Modification and Thermal Aging on Composite Toughness And its Measurement

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.; Madhukar, Madhu; Papadopoulos, Demetrios; Inghram, Linda; McCorkle, Linda

1997-01-01

A detailed experimental study was conducted to establish the structure-property relationships between elevated temperature aging and (I) fiber-matrix bonding, (2) Mode II interlaminar fracture toughness, and (3) failure modes of carbon fiber/PMR-15 composites. The fiber-matrix adhesion was varied by using carbon fibers with different surface treatments. Short beam shear tests were used to quantify the interfacial shear strength afforded by the use of the different fiber surface treatments. The results of the short beam shear tests definitely showed that, for aging times up to 1000 hr, the aging process caused no observable changes in the bulk of the three composite materials that---would degrade the shear properties of the material. Comparisons between the interlaminar shear strength (ILSS) measured by the short beam shear tests and the GII c test results, as measured by the ENF test, indicated that the differences in the surface treatments significantly affected the fracture properties while the effect of the aging process was probably limited to changes at the starter crack tip. The fracture properties changed due to a shift in the fracture from an interfacial failure to a failure within the matrix when the fiber was changed from AU-4 to AS-4 or AS-4G. There appears to be an effect of the fiber/matrix bonding on the thermo-oxidative stability of the composites that were tested. The low bonding afforded by the AU-4 fiber resulted in weight losses about twice those experienced by the AS-4 reinforced composites, the ones with the best TOS.

The Effects of Fiber Surface Modification and Thermal Aging on Composite Toughness and Its Measurement

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.; Madhukar, Madhu; Papadopolous, Demetrios S.; Inghram, Linda; Mccorkle, Linda

1995-01-01

A detailed experimental study was conducted to establish the structure-property relationships between elevated temperature aging and fiber-matrix bonding, Mode 2 interlaminar fracture toughness, and failure modes of carbon fiber/PMR-15 composites. The fiber-matrix adhesion was varied by using carbon fibers with different surface treatments. Short beam shear tests were used to quantify the interfacial shear strength afforded by the use of the different fiber surface treatments. The results of the short beam shear tests showed that, for times up to 1000 hr, the aging process caused no changes in the bulk of the three composite materials that would degrade the shear properties of the material. Comparisons between the interlaminar shear strengths (ILSS) measured by the short beam shear tests and the GIIC test results, as measured by the ENF test, indicated that the differences in the surface treatments significantly affected the fracture properties while the effect of the aging process was probably limited to changes at the starter crack tip. The fracture properties changed due to a shift in the fracture from an interfacial failure to a failure within the matrix when the fiber was changed from AU-4 to AS-4 or AS-4G. There appears to be an effect of the fiber/matrix bonding on the thermo-oxidative stability of the composites that were tested. The low bonding afforded by the AU 1 fiber resulted in weight losses about twice those experienced by the AS 1 reinforced composites, the ones with the best TOS.

Interaction between carbon fibers and polymer sizing: Influence of fiber surface chemistry and sizing reactivity

NASA Astrophysics Data System (ADS)

Moosburger-Will, Judith; Bauer, Matthias; Laukmanis, Eva; Horny, Robert; Wetjen, Denise; Manske, Tamara; Schmidt-Stein, Felix; Töpker, Jochen; Horn, Siegfried

2018-05-01

Different aspects of the interaction of carbon fibers and epoxy-based polymer sizings are investigated, e.g. the wetting behavior, the strength of adhesion between fiber and sizing, and the thermal stability of the sizing layer. The influence of carbon fiber surface chemistry and sizing reactivity is investigated using fibers of different degree of anodic oxidation and sizings with different number of reactive epoxy groups per molecule. Wetting of the carbon fibers by the sizing dispersion is found to be specified by both, the degree of fiber activation and the sizing reactivity. In contrast, adhesion strength between fibers and sizing is dominated by the surface chemistry of the carbon fibers. Here, the number of surface oxygen groups seems to be the limiting factor. We also find that the sizing and the additional functionalities induced by anodic oxidation are removed by thermal treatment at 600 °C, leaving the carbon fiber in its original state after carbonization.

Characterization of BN rich layer on ammonia treated Nextel{trademark}312 fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Khasgiwale, N.R.; Butler, E.P.; Tsakalakos, L.

A BN rich layer grown on Nextel{trademark}312 fibers by appropriate ammonia treatments was evaluated using various complimentary techniques including X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Scanning Electron Microscopy (SEM), and Transmission Electron Microscopy (TEM)/Parallel Electron Energy Loss Spectroscopy (PEELS in TEM). Three different ammonia treatments were studied. Ammonia treatment resulted in crystallization of the Nextel{trademark}312 fiber. The BN rich surface layer formed due to ammonia treatment was clearly detected in XPS and PEELS both before and after oxidation. The layer thickness was estimated to be between 5--10 nm. The layer was stable after oxidation treatment at 600 C formore » 100 hours. High resolution TEM observations of the fiber surface revealed a variable BN rich layer thickness. Patches of turbostratic BN were observed under certain conditions, however mostly the layer appeared to be amorphous.« less

Chemical Treatment of Waste Abaca for Natural Fiber-Reinforced Geopolymer Composite

PubMed Central

Malenab, Roy Alvin J.; Ngo, Janne Pauline S.; Promentilla, Michael Angelo B.

2017-01-01

The use of natural fibers in reinforced composites to produce eco-friendly materials is gaining more attention due to their attractive features such as low cost, low density and good mechanical properties, among others. This work thus investigates the potential of waste abaca (Manila hemp) fiber as reinforcing agent in an inorganic aluminosilicate material known as geopolymer. In this study, the waste fibers were subjected to different chemical treatments to modify the surface characteristics and to improve the adhesion with the fly ash-based geopolymer matrix. Definitive screening design of experiment was used to investigate the effect of successive chemical treatment of the fiber on its tensile strength considering the following factors: (1) NaOH pretreatment; (2) soaking time in aluminum salt solution; and (3) final pH of the slurry. The results show that the abaca fiber without alkali pretreatment, soaked for 12 h in Al2(SO4)3 solution and adjusted to pH 6 exhibited the highest tensile strength among the treated fibers. Test results confirmed that the chemical treatment removes the lignin, pectin and hemicellulose, as well as makes the surface rougher with the deposition of aluminum compounds. This improves the interfacial bonding between geopolymer matrix and the abaca fiber, while the geopolymer protects the treated fiber from thermal degradation. PMID:28772936

Corona plasma modification of polyamide 66 for the design of textile delivery systems for cosmetic therapy

NASA Astrophysics Data System (ADS)

Labay, C.; Canal, J. M.; Navarro, A.; Canal, C.

2014-10-01

Cosmetic and medical applications of technical textiles are a research expanding field. One of the added values of these new materials would be that they are suitable to contain and release active ingredients in a controlled manner. The influence of the initial state of the surface of polyamide 6.6 (PA66) fibers on the wetting properties of the fibers as well as on the incorporation of caffeine on the fibers and on its release kinetics from the fibers has been investigated. Comparison between industrially-finished PA66 fabrics and laboratory washed fabrics has been done to carry out this study. Furthermore, surface modification of the PA66 fibers by low temperature plasma has been studied regarding the modification of the physical, chemical and topographical properties of the textile fibers. Corona plasma treatment has been investigated to achieve surface modification in the first nanometers of polymer fibers surface in order to modulate the incorporation and the release of caffeine. It has been demonstrated that both initial state of the PA66 surface and prior plasma treatment of the PA66 fibers before the active principle incorporation condition caffeine release kinetics from the textile fibers. The final release percentage increases linearly with the C-O and Cdbnd O functional groups incorporated by plasma on the surface. It has also been established that the release amounts of caffeine achieved after 8 h from the PA66 fabric are in the same order of magnitude than topical doses of commercial gel-based formulations.

The Challenge of Producing Fiber-Based Organic Electronic Devices

PubMed Central

Könyves-Toth, Tobias; Gassmann, Andrea; von Seggern, Heinz

2014-01-01

The implementation of organic electronic devices on fibers is a challenging task, not yet investigated in detail. As was shown earlier, a direct transition from a flat device structure to a fiber substrate is in principle possible. However, a more detailed investigation of the process reveals additional complexities than just the transition in geometry. It will be shown, that the layer formation of evaporated materials behaves differently due to the multi-angled incidence on the fibers surface. In order to achieve homogenous layers the evaporation process has to be adapted. Additionally, the fiber geometry itself facilitates damaging of its surface due to mechanical impact and leads to a high surface roughness, thereby often hindering commercial fibers to be used as substrates. In this article, a treatment of commercial polymer-coated glass fibers will be demonstrated that allows for the fabrication of rather flexible organic light-emitting diodes (OLEDs) with cylindrical emission characteristics. Since OLEDs rely the most on a smooth substrate, fibers undergoing the proposed treatment are applicable for other organic electronic devices such as transistors and solar cells. Finally, the technique also supports the future fabrication of organic electronics not only in smart textiles and woven electronics but also in bent surfaces, which opens a wide range of applications. PMID:28788128

Apparatus and method for carbon fiber surface treatment

DOEpatents

Paulauskas, Felix L; Sherman, Daniel M

2014-06-03

An apparatus and method for enhancing the surface energy and/or surface chemistry of carbon fibers involves exposing the fibers to direct or indirect contact with atmospheric pressure plasma generated using a background gas containing at least some oxygen or other reactive species. The fiber may be exposed directly to the plasma, provided that the plasma is nonfilamentary, or the fiber may be exposed indirectly through contact with gases exhausting from a plasma discharge maintained in a separate volume. In either case, the process is carried out at or near atmospheric pressure, thereby eliminating the need for vacuum equipment. The process may be further modified by moistening the fibers with selected oxygen-containing liquids before exposure to the plasma.

Apparatus and method for carbon fiber surface treatment

DOEpatents

Paulauskas, Felix L [Knoxville, TN; Sherman, Daniel M [Knoxville, TN

2012-07-24

An apparatus and method for enhancing the surface energy and/or surface chemistry of carbon fibers involves exposing the fibers to direct or indirect contact with atmospheric pressure plasma generated using a background gas containing at least some oxygen or other reactive species. The fiber may be exposed directly to the plasma, provided that the plasma is nonfilamentary, or the fiber may be exposed indirectly through contact with gases exhausting from a plasma discharge maintained in a separate volume. In either case, the process is carried out at or near atmospheric pressure, thereby eliminating the need for vacuum equipment. The process may be further modified by moistening the fibers with selected oxygen-containing liquids before exposure to the plasma.

Fabrication and properties of aluminum silicate fibrous materials with in situ synthesized K2Ti6O13 whiskers

NASA Astrophysics Data System (ADS)

Liu, Hao; Wei, Nan; Wang, Zhou-fu; Wang, Xi-tang; Ma, Yan

2017-11-01

To improve their mechanical and thermal insulation properties, aluminum silicate fibrous materials with in situ synthesized K2Ti6O13 whiskers were prepared by firing a mixture of short aluminum silicate fibers and gel powders obtained from a sol-gel process. During the preparation process, the fiber surface was coated with K2Ti6O13 whiskers after the fibers were subjected to a heat treatment carried out at various temperatures. The effects of process parameters on the microstructure, compressive strength, and thermal conductivity were analyzed systematically. The results show that higher treatment temperatures and longer treatment durations promoted the development of K2Ti6O13 whiskers on the surface of aluminum silicate fibers; in addition, the intersection structure between whiskers modulated the morphology and volume of the multi-aperture structure among fibers, substantially increasing the fibers' compressive strength and reducing their heat conduction and convective heat transfer at high temperatures.

Studies of the Surface Treatment and Sizing of Carbon Fiber Surfaces on the Mechanical Properties of Composites Containing Carbon Fibers

NASA Technical Reports Server (NTRS)

Sherwood, Peter M. A.; Lease, Kevin B.; Locke, James E.; Tomblin, John S.; Wang, Youqi

1996-01-01

Carbon fiber reinforced composites are materials where carbon fibers are used to reinforce a matrix to produce a light and strong material with important applications in the aerospace industry. There are many aspects of the preparation of these materials that would benefit from a study which combines the research of groups involved in the production, testing and analysis of these materials, and studies of the basic surface chemistry involved. This final reports presents the results of a project that has developed a collaboration between groups in all three of the major research universities in the State of Kansas, and promises to lead to a collaborative program that covers the major aspects of composite development and application. Sherwood has provided initial fiber surface treatment and sizing together with fiber and composite surface analysis; Lease, Tomblin and Wang have worked together toward the goal of preparing pre-preg and fabrication of laminated panels; Locke has developed computational models to evaluate the effect of surface treatment (and chemistry) on mechanical properties; Lease, Tomblin and Wang have worked together to perform all necessary mechanical testing. The research has been focused on materials that would benefit the High Speed Civil Transport (HSCT) program. The group has visited Dr. Howard Maars and his colleagues at NASA Langley, and has focused their studies on the NASA requirements discussed in this meeting. An important development, requested by NASA scientists, has been the acquisition and study of K3B as a matrix material for the composites. The project has led to the successful acquisition and surface analysis of K3B, together with the successful deposition of this material onto surface oxidized carbon fibers. Mechanical testing, modelling and the construction of composite preparation equipment has been achieved during the grant period.

Effects of aqueous ammonia treatment on fiber’s surface morphology and enzymatic digestibility of empty fruit bunch fiber (EFBF)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ling, Tang Pei; Hassan, Osman

This study was conducted to investigate the effects of aqueous ammonia reflux and soaked treatment on the fiber’s surface morphology and enzymatic digestibility of empty fruit bunch fiber (EFBF). The surface morphological changes of the fiber after aqueous ammonia treatment was linked to the sugars yield by enzymatic hydrolysis. The effectiveness of 6.25% aqueous ammonia treatment in improving enzymatic digestibility of EFBF was initially studied in reflux system and by soaking. The results showed that soaked treatment was more effective than reflux system. Further study on soaked treatment of EFBF was carried out by increasing the ammonia concentration to 12.50%.more » Soaking in aqueous ammonia was conducted at 30°C and 50°C for 24 hours. The results of enzymatic hydrolysis showed that sugar yield from EFBF soaked in 12.50% aqueous ammonia at 50°C was the highest. Approximately 242.91±15.50 mg/g EFBF of xylose and 320.49±28.31 mg/g EFBF of glucose were produced by the action of enzyme Cellic Ctec 2. Results of scanning electron microscopic showed that aqueous ammonia treatment by soaking had caused a more severe structural distortion on the fiber’s surface and higher removal of silica bodies that embedded on the fiber than those in reflux system. The changes on the fiber’s surface morphology were believed is the contributing factor that improved the enzymatic digestibility of EFBF after aqueous ammonia treatment.« less

Improving engineered wood fiber surfaces for accessible playgrounds.

Treesearch

Theodore Laufenberg; Andrzej Krzysik; Jerrold Winandy

2003-01-01

Some engineered wood fiber surfaces are uneven, tend to shift, and have low density. The goal of our research was to develop a playground surface material that cushions impact and is accessible to people with disabilities. In the initial screening phase, we evaluated a variety of in situ surface treatments and mixtures of wood particles combined with various binders....

Mechanical and interfacial properties of poly(vinyl chloride) based composites reinforced by cassava stillage residue with different surface treatments

NASA Astrophysics Data System (ADS)

Zhang, Yanjuan; Gan, Tao; Li, Qian; Su, Jianmei; Lin, Ye; Wei, Yongzuo; Huang, Zuqiang; Yang, Mei

2014-09-01

Cassava stillage residue (CSR), a kind of agro-industrial plant fiber, was modified by coupling agent (CA), mechanical activation (MA), and MA-assisted CA (MACA) surface treatments, respectively. The untreated and different surface treated CSRs were used to prepare plant fibers/polymer composites (PFPC) with poly(vinyl chloride) (PVC) as polymer matrix, and the properties of these CSR/PVC composites were compared. Surface treated CSR/PVC composites possessed better mechanical properties, water resistance and dimensional stability compared with the untreated CSR/PVC composite, attributing to the improvement of interfacial properties between CSR and PVC matrix. MACA-treated CSR was the best reinforcement among four types of CSRs (untreated, MA-treated, CA-treated, and MACA-treated CSRs) because MACA treatment led to the significant improvement of dispersion, interfacial adhesion and compatibility between CSR and PVC. MACA treatment could be considered as an effective and green method for enhancing reinforcement efficiency of plant fibers and the properties of PFPC.

Cylindrically distributing optical fiber tip for uniform laser illumination of hollow organs

NASA Astrophysics Data System (ADS)

Buonaccorsi, Giovanni A.; Burke, T.; MacRobert, Alexander J.; Hill, P. D.; Essenpreis, Matthias; Mills, Timothy N.

1993-05-01

To predict the outcome of laser therapy it is important to possess, among other things, an accurate knowledge of the intensity and distribution of the laser light incident on the tissue. For irradiation of the internal surfaces of hollow organs, modified fiber tips can be used to shape the light distribution to best suit the treatment geometry. There exist bulb-tipped optical fibers emitting a uniform isotropic distribution of light suitable for the treatment of organs which approximate a spherical geometry--the bladder, for example. For the treatment of organs approximating a cylindrical geometry--e.g. the oesophagus--an optical fiber tip which emits a uniform cylindrical distribution of light is required. We report on the design, development and testing of such a device, the CLD fiber tip. The device was made from a solid polymethylmethacrylate (PMMA) rod, 27 mm in length and 4 mm in diameter. One end was shaped and 'silvered' to form a mirror which reflected the light emitted from the delivery fiber positioned at the other end of the rod. The shape of the mirror was such that the light fell with uniform intensity on the circumferential surface of the rod. This surface was coated with BaSO4 reflectance paint to couple the light out of the rod and onto the surface of the tissue.

Study of the effect of surface treatment of kenaf fibre on mechanical properties of kenaf filled unsaturated polyester composite

NASA Astrophysics Data System (ADS)

Salem, I. A. S.; Rozyanty, A. R.; Betar, B. O.; Adam, T.; Mohammed, M.; Mohammed, A. M.

2017-10-01

In this research, unsaturated polyester/kenaf fiber (UP/KF) composites was prepared by using hand lay-up process. The effect of surface treatment of kenaf fiber on mechanical properties of kenaf filled unsaturated polyester composites were studied. Different concentrationsof stearic acid (SA) were applied, i.e. 0, 0.4, and 0.8 wt%. Tensile strength of untreated UP/KF composites was found to be higher for 40 wt% loading of kenaf fiber. The highest tensile strength value was obtained after treatment with 0.4 wt% concentration of stearic acid at 56 MPa and tensile modulus was at 2409 MPa. From the flexural strength result obtained, it is clearly seen that 40 wt% loading of kenaf fiber and treatment with 0.4 wt% concentration of stearic acid give the highest value at 72 MPa and flexural modulus at 3929 MPa.

The effect of fiber treatment on abrasive wear properties of palm fiber reinforced epoxy composite

NASA Astrophysics Data System (ADS)

Razak, Muhammad Firdaus Abdul; Bakar, Mimi Azlina Abu; Kasolang, Salmiah; Ahmad, Mohamad Ali

2017-12-01

Oil palm industries generate at least 30 million tons of lignocellulosic biomass annually in the form of oil palm trunks (OPT), empty fruit bunches (EFB), oil palm fronds (OPF) and palm pressed fibres (PPF). The palm fiber is one of the natural fibers used as reinforcement in composite materials in order to decrease environmental issues and promotes utilization of renewable resources. This paper presents a study on the effect of alkaline treatment on wear properties of palm fiber reinforced epoxy resin composite. Abrasive wear testing was deployed to investigate the wear profile of the composite surfaces. Testing was carried out which focused on the effect of alkaline treatment to the palm fiber under different amounts of fiber loading i.e. 1 wt%, 3 wt%, 5 wt% and 7 wt%. The palm fibers were soaked into 6 % of alkaline solution or natrium hydroxide (NaOH) for 12 hours. The fiber was treated in order to remove amorphous materials such as hemicelluloses, lignins and pectins of the fiber. The wear test samples were fabricated using hand lay-up technique and cured at room temperature for 24 hours. Surface roughness of the composite material was also measured using the surface measuring instrument. Dry sliding wear test was performed at room temperature at a constant velocity of 1.4 m/s with a constant load of 10 N by using the Abrasion Test Machine. Result shows that 5 wt% and 7 wt% treated palm fiber loadings have better specific wear rate compared to lower fiber loadings. The finding of this study contributes towards material development and utilization in promoting `waste into wealth' which is in line with national aspiration.

Characterization of alkali treated and untreated new cellulosic fiber from Saharan aloe vera cactus leaves.

PubMed

A N, Balaji; K J, Nagarajan

2017-10-15

The aim of this study is to examine the use of new natural fibers, which are extracted from the Saharan aloe vera cactus plant leaves as reinforcement in polymer composites. The physicochemical, mechanical and thermal properties of the Saharan Aloe Vera Cactus Leaves (SACL) fibers are investigated, through the effect of alkali treatment. The contents of α-cellulose, hemicellulose, wax and moisture present in SACL fibers were characterized by standard test methods The mechanical properties of SACL fibers were measured through single fiber tensile test. The interfacial strength between the fiber and matrix was estimated by the fiber pull-out test. These results ensure that the chemical and mechanical properties of the fibers are improved after the alkali treatment. FT-IR spectroscopic analysis confirms that the alkali treatment process has removed certain amount of amorphous materials from the fibers. XRD analysis results show that the alkali treatment has enhanced the Crystallinity Index and Crystalline Size of the fibers. Thermal behavior of the fibers was analyzed by using TGA. The thermal stability and the thermal degradation temperature increases after the alkali treatment of fibers. The morphologies of fibers were analyzed by SEM and prove that the fiber surfaces become rough after alkali treatment. Copyright © 2017 Elsevier Ltd. All rights reserved.

Effect of Surface Treatment on the Properties of Wool Fabric

NASA Astrophysics Data System (ADS)

Kan, C. W.; Yuen, C. W. M.; Chan, C. K.; Lau, M. P.

Wool fiber is commonly used in textile industry, however, it has some technical problems which affect the quality and performance of the finished products such as felting shrinkage, handle, lustre, pilling, and dyeability. These problems may be attributed mainly in the presence of wool scales on the fiber surface. Recently, chemical treatments such as oxidation and reduction are the commonly used descaling methods in the industry. However, as a result of the pollution caused by various chemical treatments, physical treatment such as low temperature plasma (LTP) treatment has been introduced recently because it is similarly capable of achieving a comparable descaling effect. Most of the discussions on the applications of LTP treatment on wool fiber were focused on applying this technique for improving the surface wettability and shrink resistance. Meanwhile, little discussion has been made on the mechanical properties, thermal properties, and the air permeability. In this paper, wool fabric was treated with LTP treatment with the use of a non-polymerizing gas, namely oxygen. After the LTP treatment, the fabrics low-stress mechanical properties, air permeability, and thermal properties were evaluated and discussed.

Thermal stability relationships between PMR-15 resin and its composites

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.; Jayne, Douglas; Leonhardt, Todd A.; Bors, Dennis

1993-01-01

A study was conducted to investigate the relationship between the thermo-oxidative stability of PMR-15 matrix resin and the stability of graphite-fiber-reinforced composites that contain this resin as the matrix material. Three areas were investigated. The first was the effect of fiber/matrix interfacial bond strength on the isothermal aging weight loss of composites. By using type-A graphite fibers produced by Hercules, it was possible to study composites reinforced with fibers that were processed to receive different surface treatments. One of the fibers was untreated, a second fiber was treated by oxidation to enhance fiber/matrix bonding, and the third type of fiber was coated with an epoxy sizing. These treatments produced three significantly different interfacial bond strengths. The epoxy sizing on the third fiber was quickly oxidized from the bare fiber surfaces at 288, 316, and 343 C. The weight loss due to the removal of the sizing was constant at 1.5 percent. This initial weight loss was not observed in thermo-oxidative stability studies of composites. The PMR-15 matrix satisfactorily protected the reinforcemnt at all three temperatures.

Basalt Fiber for Volcanic Slag Lightweight Aggregate Concrete Research on the Impact of Performance

NASA Astrophysics Data System (ADS)

Xiao, Li-guang; Li, Gen-zhuang

2018-03-01

In order to study the effect of basalt fiber on the mechanical properties and durability of volcanic slag lightweight aggregate concrete, the experimental study on the flexural strength, compressive strength and freeze-thaw resistance of volcanic slag concrete with different basalt fiber content were carried out, the basalt fiber was surface treated with NaOH and water glass, the results show that the surface treatment of basalt fiber can significantly improve the mechanical properties, durability and other properties of volcanic slag lightweight aggregate concrete.

Surface modification and characterization of basalt fibers as potential reinforcement of concretes

NASA Astrophysics Data System (ADS)

Iorio, M.; Santarelli, M. L.; González-Gaitano, G.; González-Benito, J.

2018-01-01

Basalt fibers were surface treated with silane coupling agents as a method to enhance the adhesion and durability of fiber-matrix interfaces in concrete based composite materials. In particular, this work has been focused on the study of basalt fibers chemical coatings with aminosilanes and their subsequent characterization. Surface treatments were carried out after removing the original sizing applied by manufacturer and pretreating them with an activation process of surface silanol regeneration. Different samples were considered to make convenient comparisons: as received fibers (commercial), calcinated fibers (without commercial sizing), activated samples (calcinated fibers subjected to an acid process for hydroxyl regeneration), and silanized fibers with γ-aminopropiltriethoxysilane, γ-aminopropilmethyldiethoxysilane and a mixture of 50% by weight of both silanes. A deep characterization was carried out in terms of structure using X-ray diffraction, XRD, and Fourier transform infrared spectroscopy, FTIR, thermal properties by thermogravimetric analysis, TGA, coupled with single differential thermal analysis, SDTA, and morphology by scanning electron microscopy, SEM, and atomic force microscopy, AFM.

Microstructural and strength stability of a developmental CVD SiC fiber

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.; Garg, Anita; Hull, David R.

1995-01-01

The effects of thermal exposure on the room temperature tensile strength and microstructure of a developmental 50 micron CVD SiC fiber have been studied. The fibers were heat treated between 600 and 2000 C in 0.1 MPa argon and air environments for up to 100 hr. In the as-fabricated condition, the fibers showed approximately 6 GPa tensile strength. After argon treatment, the fibers showed strength degradation after 1 hr exposure beyond 1000 C, but those exposed between 1600 and 2000 C retained approximately 2 GPa strength. TEM results showed microstructural changes both in the surface coating and SiC sheath. Flaws created by the rearrangement of carbon in the surface coating and growth of equiaxed SiC grain zone in the SiC sheath are the suggested mechanisms of strength degradation. After air treatment, fibers showed strength degradation after only 2 min exposure at 600 C. Strength retention after 2 min at 1500 C was approximately 2 GPa. Oxidation of the surface coating is the primary reason for strength degradation.

A Comparative Evaluation of Effect of Different Chemical Solvents on the Shear Bond Strength of Glass Fiber reinforced Post to Core Material

PubMed Central

Samadi, Firoza; Jaiswal, JN; Saha, Sonali

2014-01-01

ABSTRACT% Aim: To compare the effect of different chemical solvents on glass fiber reinforced posts and to study the effect of these solvents on the shear bond strength of glass fiber reinforced post to core material. Materials and methods: This study was conducted to evaluate the effect of three chemical solvents, i.e. silane coupling agent, 6% H2O2 and 37% phosphoric acid on the shear bond strength of glass fiber post to a composite resin restorative material. The changes in post surface characteristics after different treatments were also observed, using scanning electron microscopy (SEM) and shear bond strength was analyzed using universal testing machine (UTM). Results: Surface treatment with hydrogen peroxide had greatest impact on the post surface followed by 37% phosphoric acid and silane. On evaluation of the shear bond strength, 6% H2O2 exhibited the maximum shear bond strength followed in descending order by 37% phosphoric acid and silane respectively. Conclusion: The surface treatment of glass fiber post enhances the adhesion between the post and composite resin which is used as core material. Failure of a fiber post and composite resin core often occurs at the junction between the two materials. This failure process requires better characterization. How to cite this article: Sharma A, Samadi F, Jaiswal JN, Saha S. A Comparative Evaluation of Effect of Different Chemical Solvents on the Shear Bond Strength of Glass Fiber Reinforced Post to Core Material. Int J Clin Pediatr Dent 2014;7(3):192-196. PMID:25709300

A Study On the effect of Surface treatment on the Physical and Mechanical properties of date-palm stem liber embedded epoxy composites

NASA Astrophysics Data System (ADS)

Tripathy, Satchidananda; Dehury, Janaki; Mishra, Debasmita

2016-02-01

Natural fiber reinforced polymer composites are being used frequently for variety of engineering applications due to many of their advantages like ease of availability, low density, low production cost and good mechanical properties but natural fibers are more or less hydrophilic in nature. Therefore, an investigation has been carried out to make better utilization of a class of natural fiber that is date palm stem fiber, for making a wide range of products. Attempts have been made in this research work to study the effect of fiber loading on the physical, mechanical and water absorption behaviour of treated and untreated short fiber based epoxy composites. Composites of various compositions of different amounts of fiber loading are fabricated by simple hand lay-up technique. It has been observed that there is a significant effect of surface treatment of fibers on the overall properties of composites. Further enhancement of properties with lower water absorption rate was attained with glass fiber-epoxy based hybrid composites.

Study of the effect of surface treatment of kenaf fiber on chemical structure and water absorption of kenaf filled unsaturated polyester composite

NASA Astrophysics Data System (ADS)

Salem, I. A. S.; Rozyanty, A. R.; Betar, B. O.; Adam, T.; Mohammed, M.; Mohammed, A. M.

2017-10-01

In this research, unsaturated polyester/kenaf fiber (UP/KF) composites was prepared by using hand lay-up process. The effect of surface treatment of kenaf fiber on mechanical properties of kenaf filled unsaturated polyester composites were studied. Different concentrationsof stearic acid (SA) were applied, i.e. 0, 0.4, and 0.8 wt%. The Fourier transform infrared (FT-IR) spectra of kenaf fiber shows high intensity of the peak around 3300-3400 cm-1, which is attributed to the hydrogen bonded O-H stretching. However, the treated kenaf fiber with stearic acid shows the elimination of O-H group and this peak is vanished. This is due to the reaction of (-COOH) group of stearic with (-OH) group of kenaf fiber. The results of water absorption study revealed that increasing the loading of KF in the composite will result is increasing the tendency to absorb water. However, the absorption was significantly decreased after treatment with stearic acid as well as the time to reach to the equilibrium state.

Effect of chemical treatment of Kevlar fibers on mechanical interfacial properties of composites.

PubMed

Park, Soo-Jin; Seo, Min-Kang; Ma, Tae-Jun; Lee, Douk-Rae

2002-08-01

In this work, the effects of chemical treatment on Kevlar 29 fibers have been studied in a composite system. The surface characteristics of Kevlar 29 fibers were characterized by pH, acid-base value, X-ray photoelectron spectroscopy (XPS), and FT-IR. The mechanical interfacial properties of the final composites were studied by interlaminar shear strength (ILSS), critical stress intensity factor (K(IC)), and specific fracture energy (G(IC)). Also, impact properties of the composites were investigated in the context of differentiating between initiation and propagation energies and ductile index (DI) along with maximum force and total energy. As a result, it was found that chemical treatment with phosphoric acid solution significantly affected the degree of adhesion at interfaces between fibers and resin matrix, resulting in improved mechanical interfacial strength in the composites. This was probably due to the presence of chemical polar groups on Kevlar surfaces, leading to an increment of interfacial binding force between fibers and matrix in a composite system.

Effect of different surface treatments on the push-out bond strength of fiber post to root canal dentin.

PubMed

Demiryürek, Ebru Ozsezer; Külünk, Safak; Saraç, Duygu; Yüksel, Gözde; Bulucu, Bilinç

2009-08-01

The purpose of this study was to evaluate the effects of different surface treatments on the bond strength of a fiber post to dentin. Sixty extracted human maxillary incisor teeth were manually shaped with K-files using the step-back technique. ISO size 45 files were used as master apical files. Post spaces were prepared and then the root canals were subjected to one of the following 5 surface treatments: irrigation with 5% sodium hypochlorite (NaOCl); treatment with ethanol, ethyl acetate, and acetone-based cleansing agent (Sikko Tim); irrigation with 17% EDTA; etching with 37% orthophosphoric acid for 15 seconds; and etching with 10% citric acid for 15 seconds. Fiber posts were luted using self-etching/self-priming dual polymerized resin cement. From the coronal part of each root, 3 slides of 0.6-mm thickness were obtained. A push-out bond strength test was performed by a universal testing machine at a crosshead speed of 0.5 mm/min. Dentin surfaces were examined under scanning electron microscopy (SEM) after different surface treatments. Data were analyzed with a one-way analysis of variance (ANOVA) and Tukey HSD test. ANOVA revealed that canal surface treatment affected the bond strength (P < .001). The highest bond strength was obtained in the Sikko Tim group. The results also showed that surface treatment methods increased the bond strength to dentin when compared with the control group. Sikko Tim group was the more effective surface treatment agent compared with EDTA, orthophosphoric acid, citric acid, and control groups; however, it could not remove the smear layer and sealer remnants effectively on radicular dentin surfaces. Removal of the smear layer and opening of dentinal tubules are not recommended when a self-etching/self-priming adhesive system is used.

Influence of surface modified basalt fiber on strength of cinder lightweight aggregate concrete

NASA Astrophysics Data System (ADS)

Xiao, Liguang; Li, Jiheng; Liu, Qingshun

2017-12-01

In order to improve the bonding and bridging effect between volcanic slag lightweight aggregate concrete cement and basalt fiber, The basalt fiber was subjected to etching and roughening treatment by NaOH solution, and the surface of the basalt fiber was treated with a mixture of sodium silicate and micro-silica powder. The influence of modified basalt fiber on the strength of volcanic slag lightweight aggregate concrete was systematically studied. The experimental results show that the modified basalt fiber volcanic slag lightweight aggregate concrete has a flexural strength increased by 47%, the compressive strength is improved by 16% and the toughness is increased by 27% compared with that of the non-fiber.

Interlaminar fracture in carbon fiber/thermoplastic composites

NASA Technical Reports Server (NTRS)

Hinkley, J. A.; Bascom, W. D.; Allred, R. E.

1990-01-01

The surfaces of commercial carbon fibers are generally chemically cleaned or oxidized and then coated with an oligomeric sizing to optimize their adhesion to epoxy matrix resins. Evidence from fractography, from embedded fiber testing and from fracture energies suggests that these standard treatments are relatively ineffective for thermoplastic matrices. This evidence is reviewed and model thermoplastic composites (polyphenylene oxide/high strain carbon fibers) are used to demonstrate how differences in adhesion can lead to a twofold change in interlaminar fracture toughness. The potential for improved adhesion via plasma modification of fiber surfaces is discussed. Finally, a surprising case of fiber-catalyzed resin degradation is described.

Structural and optical properties of antimony-germanate-borate glass and glass fiber co-doped Eu3+ and Ag nanoparticles.

PubMed

Zmojda, Jacek; Kochanowicz, Marcin; Miluski, Piotr; Baranowska, Agata; Pisarski, Wojciech A; Pisarska, Joanna; Jadach, Renata; Sitarz, Maciej; Dorosz, Dominik

2018-08-05

In the paper analysis of structural and luminescent properties of antimony-germanate-borate glasses and glass fiber co-doped with 0.6AgNO 3 /0.2Eu 2 O 3 are presented. Heat treatment of the fabricated glass and optical fiber (400 °C, 12 h) enabled to obtain Ag nanoparticles (NPs) with average size 30-50 nm on their surface. It has been proofed that silver ions migrate to the glass surface, where they are reduced to Ag 0 nanoparticles. Simultaneously, FTIR analysis showed that heat treatment of the glass and optical fiber increases the local symmetry of the Eu 3+ site. Copyright © 2018 Elsevier B.V. All rights reserved.

Nitrogen-Doped Carbon Fiber Paper by Active Screen Plasma Nitriding and Its Microwave Heating Properties.

PubMed

Zhu, Naishu; Ma, Shining; Sun, Xiaofeng

2016-12-28

In this paper, active screen plasma nitriding (ASPN) treatment was performed on polyacrylonitrile carbon fiber papers. Electric resistivity and microwave loss factor of carbon fiber were described to establish the relationship between processing parameters and fiber's ability to absorb microwaves. The surface processing effect of carbon fiber could be characterized by dynamic thermal mechanical analyzer testing on composites made of carbon fiber. When the process temperature was at 175 °C, it was conducive to obtaining good performance of dynamical mechanical properties. The treatment provided a way to change microwave heating properties of carbon fiber paper by performing different treatment conditions, such as temperature and time parameters. Atomic force microscope, scanning electron microscope, and X-ray photoelectron spectroscopy analysis showed that, during the course of ASPN treatment on carbon fiber paper, nitrogen group was introduced and silicon group was removed. The treatment of nitrogen-doped carbon fiber paper represented an alternative promising candidate for microwave curing materials used in repairing and heating technology, furthermore, an efficient dielectric layer material for radar-absorbing structure composite in metamaterial technology.

Effects of high pressure nitrogen on the thermal stability of SiC fibers

NASA Technical Reports Server (NTRS)

Jaskowiak, Martha H.

1991-01-01

Polymer-derived SiC fibers were exposed to nitrogen gas pressures of 7 and 50 atm at temperatures up to 1800 C. The fiber weight loss, chemical composition, and tensile strength were then measured at room temperature in order to understand the effects of nitrogen exposure on fiber stability. High pressure nitrogen treatments limited weight loss to 3 percent or less for temperatures up to 1800 C. The bulk Si-C-O chemical composition of the fiber remained relatively constant up to 1800 C with only a slight increase in nitrogen content after treatment at 50 atm; however, fiber strength retention was significantly improved. To further understand the effects of the nitrogen atmosphere on the fiber stability, the results of previous high pressure argon treatments were compared to those of the high pressure nitrogen treatments. High pressure inert gas can temporarily maintain fiber strength by physically inhibiting the evolution of gaseous species which result from internal reactions. In addition to this physical effect, it would appear that high pressure nitrogen further improved fiber temperature capability by chemically reacting with the fiber surface, thereby reducing the rate of gas evolution. Subsequent low pressure argon treatments following the initial nitrogen treatments resulted in stronger fibers than after argon treatment alone, further supporting the chemical reaction mechanism and its beneficial effects on fiber strength.

Modification of carbon fabrics by radio-frequency capacitive discharge at low pressure to regulate mechanical properties of carbon fiber reinforced plastics based on it

NASA Astrophysics Data System (ADS)

Garifullin, A. R.; Krasina, I. V.; Skidchenko, E. A.; Shaekhov, M. F.; Tikhonova, N. V.

2017-01-01

To increase the values of mechanical properties of carbon fiber (CF) composite materials used in sports equipment production the method of radio-frequency capacitive (RFC) low-pressure plasma treatment in air was proposed. Previously it was found that this type of modification allows to effectively regulate the surface properties of fibers of different nature. This treatment method differs from the traditional ones by efficiency and environmental friendliness as it does not require the use of aggressive, environmentally hazardous chemicals. In this paper it was established that RFC low-pressure air plasma treatment of carbon fabrics enhances the interlaminar shear strength (ILSS) of carbon fiber reinforced plastic (CFRP). As a result of experimental studies of CF by Fourier Transform Infrared (FTIR) spectroscopy method it was proved that after radio-frequency capacitive plasma treatment at low pressure in air the oxygen-containing functional groups is grafted on the surface. These groups improve adhesion at the interface “matrix-fiber”.

The effect of ultrafast fiber laser application on the bond strength of resin cement to titanium.

PubMed

Ates, Sabit Melih; Korkmaz, Fatih Mehmet; Caglar, Ipek Satıroglu; Duymus, Zeynep Yeşil; Turgut, Sedanur; Bagis, Elif Arslan

2017-07-01

The purpose of this study was to investigate the effect of ultrafast fiber laser treatment on the bond strength between titanium and resin cement. A total of 60 pure titanium discs (15 mm × 2 mm) were divided into six test groups (n = 10) according to the surface treatment used: group (1) control, machining; group (2) grinding with a diamond bur; group (3) ultrafast fiber laser application; group (4) resorbable blast media (RBM) application; group (5) electro-erosion with copper; and group (6) sandblasting. After surface treatments, resin cements were applied to the treated titanium surfaces. Shear bond strength testing of the samples was performed with a universal testing machine after storing in distilled water at 37 °C for 24 h. One-way ANOVA and Tukey's HSD post hoc test were used to analyse the data (P < 0.05). The highest bond strength values were observed in the laser application group, while the lowest values were observed in the grinding group. Sandblasting and laser application resulted in significantly higher bond strengths than control treatment (P < 0.05). Ultrafast fiber laser treatment and sandblasting may improve the bond strength between resin cement and titanium.

Effect OF NaOH Treatment on Bending Strength Of The Polyester Composite Reinforce By Sugar Palm Fibers

NASA Astrophysics Data System (ADS)

Arif Irfai, Mochamad; Wulandari, Diah; Sutriyono; Marsyahyo, Eko

2018-04-01

The objective of this research is to investigate the effect of NaOH treatment on bending strength of lamina composite reinforced by sugar palm fiber. To know of mechanism fracture can be done with visual inspection of the fracture surface. The Materials used are random sugar palm fibers that have been in the treatment of NaOH, polyester resin and hardener. Sugar palm fibers after washed and dried then soaked NaOH with a long time soaking 0, 2, 4, 6 and 8 hours. The bending test specimens were produced according to ASTM D 790. All specimens were post cured at 62°C for 4 hours. The Bending test was carried out on a universal testing machine. The SEM analysis has conducted to provide the analysis on interface adhesion between the surfaces of fiber with the matrix. The result shows that polyester composite reinforced by sugar palm fiber has highest bending stress 176.77 N/mm2 for 2 hours of a long time soaking NaOH, the highest flexural strain 0.27 mm for 2 hours of a long time soaking NaOH, elongation 24.05% for 2 hours of a long time soaking NaOH and the highest bending modulus 1.267 GPa for 2 hours of a long time soaking NaOH. Based on the results, it can be concluded that the polyester composite reinforced by sugar palm fiber has the optimum bending properties for a long time soaking 2 hours. The fracture surface shows that the polyester composite reinforced by sugar palm fiber pull out that indicate weakens the bond between fiber and matrix.

Effect of sonication treatment on fibrilating snake fruit (Sallaca) frond fiber

NASA Astrophysics Data System (ADS)

Darmanto, Seno; Rochardjo, Heru S. B.; Jamasri, Widyorini, Ragil

2018-02-01

Aim of this research is to investigate influence of chemical and sonication treatment on fibrillating and mechanical properties of snake fruit frond fiber. The presence of surface impurities and the large amount of hydroxyl groups in natural fibers make less attractive for polymeric materials reinforcement. Effort to remove the impurities can be done by few treatments that consist of physical, chemical and mechanical treatment. Snake fruit frond bundle fiber were firstly subjected to chemical treatments with alkali solution, steaming at 2 bar and steam explosion at 6 bar by 40 times releasing of steam. Advanced treatment is done by flowing ultrasonic wave at 20 kHz by 90 - 210 watt. The output of fibrillation can reach fiber in range 10 - 25 nm compared with 10.72 µm in diameter for sonication and 6 bar in pressure of steam with 40x of rapidly steam release respectively.

The influence of four dual-cure resin cements and surface treatment selection to bond strength of fiber post

PubMed Central

Liu, Chang; Liu, Hong; Qian, Yue-Tong; Zhu, Song; Zhao, Su-Qian

2014-01-01

In this study, we evaluate the influence of post surface pre-treatments on the bond strength of four different cements to glass fiber posts. Eighty extracted human maxillary central incisors and canines were endodontically treated and standardized post spaces were prepared. Four post pre-treatments were tested: (i) no pre-treatment (NS, control), (ii) sandblasting (SA), (iii) silanization (SI) and (iv) sandblasting followed by silanization (SS). Per pre-treatment, four dual-cure resin cements were used for luting posts: DMG LUXACORE Smartmix Dual, Multilink Automix, RelyX Unicem and Panavia F2.0. All the specimens were subjected to micro push-out test. Two-way analysis of variance and Tukey post hoc tests were performed (α=0.05) to analyze the data. Bond strength was significantly affected by the type of resin cement, and bond strengths of RelyX Unicem and Panavia F2.0 to the fiber posts were significantly higher than the other cement groups. Sandblasting significantly increased the bond strength of DMG group to the fiber posts. PMID:24177170

Properties of M40J Carbon/PMR-II-50 Composites Fabricated with Desized and Surface Treated Fibers. Characterization of M40J Desized and Finished Fibers

NASA Technical Reports Server (NTRS)

Allred, Ronald E.; Gosau, Jan M.; Shin, E. Eugene; McCorkle, Linda S.; Sutter, James K.; OMalley, Michelle; Gray, Hugh R. (Technical Monitor)

2002-01-01

To increase performance and durability of high temperature composites for potential rocket engine components, it is necessary to optimize wetting and interfacial bonding between high modulus carbon fibers and high temperature polyimide resins. It has been previously demonstrated that the electro-oxidative shear treatments used by fiber manufacturers are not effective on higher modulus fibers that have fewer edge and defect sites in the surface crystallites. In addition, sizings commercially supplied on most carbon fibers are not compatible with polyimides. This study was an extension of prior work characterizing the surface chemistry and energy of high modulus carbon fibers (M40J and M60J, Torray) with typical fluorinated polyimide resins, such as PMR-II-50. A continuous desizing system which utilizes environmentally friendly chemical- mechanical processes was developed for tow level fiber and the processes were optimized based on weight loss behavior, surface elemental composition (XPS) and morphology (FE-SEM) analyses, and residual tow strength of the fiber, and the similar approaches have been applied on carbon fabrics. Both desized and further treated with a reactive finish were investigated for the composite reinforcement. The effects of desizing and/or subsequent surface retreatment on carbon fiber on composite properties and performance including fiber-matrix interfacial mechanical properties, thermal properties and blistering onset behavior will be discussed in this presentation.

Fabricating and strengthening the carbon nanotube/copper composite fibers with high strength and high electrical conductivity

NASA Astrophysics Data System (ADS)

Han, Baoshuai; Guo, Enyu; Xue, Xiang; Zhao, Zhiyong; Li, Tiejun; Xu, Yanjin; Luo, Liangshun; Hou, Hongliang

2018-05-01

Combining the excellent properties of carbon nanotube (CNT) and copper, CNT/Cu composite fibers were fabricated by physical vapor deposition (PVD) and rolling treatment. Dense and continuous copper film (∼2 μm) was coated on the surface of the CNT fibers by PVD, and rolling treatment was adopt to strengthen the CNT/Cu composite fibers. After the rolling treatment, the defects between the Cu grains and the CNT bundles were eliminated, and the structure of both the copper film and the core CNT fibers were optimized. The rolled CNT/Cu composite fibers possess high tensile effective strength (1.01 ± 0.13 GPa) and high electrical conductivity ((2.6 ± 0.3) × 107 S/m), and thus, this material may become a promising wire material.

Effects of Mechanical and Chemical Pretreatments of Zirconia or Fiber Posts on Resin Cement Bonding

PubMed Central

Li, Rui; Zhou, Hui; Wei, Wei; Wang, Chen; Sun, Ying Chun; Gao, Ping

2015-01-01

The bonding strength between resin cement and posts is important for post and core restorations. An important method of improving the bonding strength is the use of various surface pretreatments of the post. In this study, the surfaces of zirconia (fiber) posts were treated by mechanical and/or chemical methods such as sandblasting and silanization. The bonding strength between the zirconia (fiber) post and the resin cement was measured by a push-out method after thermocycling based on the adhesion to Panavia F 2.0 resin cement. The zirconia and fiber posts exhibited different bonding strengths after sandblasting and/or silanization because of the different strengths and chemical structures. The zirconia post showed a high bonding strength of up to 17.1 MPa after a combined treatment of sandblasting and silanization because of the rough surface and covalent bonds at the interface. This effect was also enhanced by using 1,2-bis(trimethoxysilyl)ethane for the formation of a flexible layer at the interface. In contrast, a high bonding strength of 13.9 MPa was obtained for the fiber post treated by silane agents because the sandblasting treatment resulted in damage to the fiber post, as observed by scanning electron microscopy. The results indicated that the improvement in the bonding strength between the post and the resin cement could be controlled by different chemical and/or mechanical treatments. Enhanced bonding strength depended on covalent bonding and the surface roughness. A zirconia post with high bonding strength could potentially be used for the restoration of teeth in the future. PMID:26066349

A novel surface modification of carbon fiber for high-performance thermoplastic polyurethane composites

NASA Astrophysics Data System (ADS)

Zhang, Yuanyuan; Zhang, Yizhen; Liu, Yuan; Wang, Xinling; Yang, Bin

2016-09-01

Properties of carbon fiber (CF) reinforced composites depend largely on the interfacial bonding strength between fiber and the matrix. In the present work, CF was grafted by 4,4‧-diphenylmethane diisocyanate (MDI) molecules after electrochemical oxidation treatment. The existence of functional groups introduced to the fiber surface and the changes of surface roughness were confirmed by FTIR, AFM, XPS, SEM and Raman spectroscopy. To evaluate the possible applications of this surface modification of carbon fiber, we examined the mechanical properties as well as the friction and wear performance of pristine CF and MDI-CF reinforced thermoplastic polyurethane (TPU) composites with 5-30 wt.% fiber contents, and found that the mechanical properties of TPU composites were all significantly improved. It is remarkable that when fiber content was 30 wt.%, the tensile strength of TPU/MDI-CF was increased by 99.3%, which was greater than TPU/CF (53.2%), and the friction loss of TPU/MDI-CF was decreased by 49.09%. The results of DMA and SEM analysis indicated the positive effects of MDI modification on the interfacial bonding between fibers and matrix. We believed that this simple and effective method could be used to the development of surface modified carbon fiber for high-performance TPU.

Adsorption performance of mixed dyes on alkalization loofah fibers

NASA Astrophysics Data System (ADS)

Wang, Yongli; Liu, Jinyan; Li, Xingxing

2018-02-01

When the polyporous structures of loofah fiber is adequately exposed after alkali treatment,lignin, hemicellulose and pectin are removed. Specific surface area is increased to maximum, which means the efficiency of absorptivity is highest. In this paper, by using alkalization loofah (AL) as adsorbent, the effect of loofah fiber on waste water treatment is studied under the efficiency of loofah fiber which contain acridine yellow, methylene blue, mixed solution of the two dyes. The optimum treatment conditions of loofah fiber were studied from five aspects which include dosage, temperature, mixing time, pH and concentration. The results showed that the optimal conditions are 30°C, pH 8.0, 20mg dosage of loofah fiber in 40ml solution and mixing time 25min. The optimal treatment conditions of mixed dyes were studied from the aspects of mixing time, the dosage of AL and the molar ratio of the two components in the mixed dyes.

Techniques for increasing boron fiber fracture strain

NASA Technical Reports Server (NTRS)

Dicarlo, J. A.

1977-01-01

Improvement in the strain-to-failure of CVD boron fibers is shown possible by contracting the tungsten boride core region and its inherent flaws. The results of three methods are presented in which etching and thermal processing techniques were employed to achieve core flaw contraction by internal stresses available in the boron sheath. After commercially and treatment induced surface flaws were removed from 203 micrometers (8 mil) fibers, the core flaw was observed to be essentially the only source of fiber fracture. Thus, fiber strain-to-failure was found to improve by an amount equal to the treatment induced contraction on the core flaw. Commercial feasibility considerations suggest as the most cost effective technique that method in which as-produced fibers are given a rapid heat treatment above 700 C. Preliminary results concerning the contraction kinetics and fracture behavior observed are presented and discussed both for high vacuum and argon gas heat treatment environments.

Thermomechanical pulp fiber surface modification for enhancing the interfacial adhesion with polypropylene

Treesearch

Sangyeob Lee; Todd F. Shupe; Leslie H. Groom; Chung Y. Hse

2007-01-01

Chemical coupling on the thermomechanical pulp (TMP) fiber improved tensile strength of the TMP fiber handsheet and isotactic polypropylene film laminates (TPL). For the maleic anhydride W) with benzoyl peroxide (BPO)a an initiator, tensile strength increaded 52: with the TMP fiber treatment over untreated laminates. The optimum strength properties were obtained with...

A preliminary characterization of the tensile and fatigue behavior of tungsten-fiber/Waspaloy-matrix composite

NASA Technical Reports Server (NTRS)

Corner, Ralph E.; Lerch, Brad A.

1992-01-01

A microstructural study and a preliminary characterization of the room temperature tensile and fatigue behavior of a continuous, tungsten fiber, Waspaloy-matrix composite was conducted. A heat treatment was chosen that would allow visibility of planar slip if it occurred during deformation, but would not allow growth of the reaction zone. Tensile and fatigue tests showed that the failed specimens contained transverse cracks in the fibers. The cracks that occurred in the tensile specimen were observed at the fracture surface and up to approximately 4.0 mm below the fracture surface. The crack spacing remained constant along the entire length of the cracked fibers. Conversely, the cracks that occurred in the fatigue specimen were only observed in the vicinity of the fracture surface. In instances where two fiber cracks occurred in the same plane, the matrix often necked between the two cracked fibers. Large groups of slip bands were generated in the matrix near the fiber cracks. Slip bands in the matrix of the tensile specimen were also observed in areas where there were no fiber cracks, at distances greater than 4 mm from the fracture surface. This suggests that the matrix plastically flows before fiber cracking occurs.

Alumina fiber strength improvement

NASA Technical Reports Server (NTRS)

Pepper, R. T.; Nelson, D. C.

1982-01-01

The effective fiber strength of alumina fibers in an aluminum composite was increased to 173,000 psi. A high temperature heat treatment, combined with a glassy carbon surface coating, was used to prevent degradation and improve fiber tensile strength. Attempts to achieve chemical strengthening of the alumina fiber by chromium oxide and boron oxide coatings proved unsuccessful. A major problem encountered on the program was the low and inconsistent strength of the Dupont Fiber FP used for the investigation.

UV/O3 treatment as a surface modification of rice husk towards preparation of novel biocomposites

PubMed Central

Rajendran Royan, Nishata Royan; Sulong, Abu Bakar; Yuhana, Nor Yuliana; Ab Ghani, Mohd Hafizuddin; Ahmad, Sahrim

2018-01-01

The use of rice husks (RH) to reinforce polymers in biocomposites are increasing tremendously. However, the incompatibility between the hydrophilic RH fibers and the hydrophobic thermoplastic matrices leads to unsatisfactory biocomposites. Surface modification of the fiber surface was carried out to improve the adhesion between fiber and matrix. In this study, the effect of surface modification of RH via alkali, acid and ultraviolet-ozonolysis (UV/O3) treatments on the properties of composites recycled high density polyethylene (rHDPE) composites was investigated. The untreated and treated RH were characterized by Fourier Transform Infrared (FTIR) and Scanning Electron Microscope (SEM). The composites containing 30 wt% of RH (treated and untreated) were then prepared via extrusion and followed by compression molding. As compared to untreated RH, all surface treated RH exhibited rougher surface and showed improved adhesion with rHDPE matrix. Tensile strength of UV/O3-treated RH composites showed an optimum result at 18.37 MPa which improved about 5% in comparison to the composites filled with untreated RH. UV/O3 treatment promotes shorter processing time and lesser raw material waste during treatment process where this is beneficial for commercialization in the future developments of wood plastic composites (WPCs). Therefore, UV/O3 treatment can be served as an alternative new method to modify RH surface in order to improve the adhesion between hydrophilic RH fibre and hydrophobic rHDPE polymer matrix. PMID:29847568

Carbide coated fibers in graphite-aluminum composites

NASA Technical Reports Server (NTRS)

Imprescia, R. J.; Levinson, L. S.; Reiswig, R. D.; Wallace, T. C.; Williams, J. M.

1975-01-01

The study of protective-coupling layers of refractory metal carbides on the graphite fibers prior to their incorporation into composites is presented. Such layers should be directly wettable by liquid aluminum and should act as diffusion barriers to prevent the formation of aluminum carbide. Chemical vapor deposition was used to uniformly deposit thin, smooth, continuous coats of ZrC on the carbon fibers of tows derived from both rayon and polyacrylonitrile. A wet chemical coating of the fibers, followed by high-temperature treatment, was used, and showed promise as an alternative coating method. Experiments were performed to demonstrate the ability of aluminum alloys to wet carbide surfaces. Titanium carbide, zirconium carbide and carbide-coated graphite surfaces were successfully wetted. Results indicate that initial attempts to wet surfaces of ZrC-coated carbon fibers appear successful.

Preparation and characterization of amphiphilic triblock terpolymer-based nanofibers as antifouling biomaterials.

PubMed

Cho, Youngjin; Cho, Daehwan; Park, Jay Hoon; Frey, Margaret W; Ober, Christopher K; Joo, Yong Lak

2012-05-14

Antifouling surfaces are critical for the good performance of functional materials in various applications including water filtration, medical implants, and biosensors. In this study, we synthesized amphiphilic triblock terpolymers (tri-BCPs, coded as KB) and fabricated amphiphilic nanofibers by electrospinning of solutions prepared by mixing the KB with poly(lactic acid) (PLA) polymer. The resulting fibers with amphiphilic polymer groups exhibited superior antifouling performance to the fibers without such groups. The adsorption of bovine serum albumin (BSA) on the amphiphilic fibers was about 10-fold less than that on the control surfaces from PLA and PET fibers. With the increase of the KB content in the amphiphilic fibers, the resistance to adsorption of BSA was increased. BSA was released more easily from the surface of the amphiphilic fibers than from the surface of hydrophobic PLA or PET fibers. We have also investigated the structural conformation of KB in fibers before and after annealing by contact angle measurements, transmission electron microscopy (TEM), energy-dispersive X-ray spectroscopy (EDX), and coarse-grained molecular dynamics (CGMD) simulation to probe the effect of amphiphilic chain conformation on antifouling. The results reveal that the amphiphilic KB was evenly distributed within as-spun hybrid fibers, while migrated toward the core from the fiber surface during thermal treatment, leading to the reduction in antifouling. This suggests that the antifouling effect of the amphiphilic fibers is greatly influenced by the arrangement of amphiphilic groups in the fibers.

Corrosion control of cement-matrix and aluminum-matrix composites

NASA Astrophysics Data System (ADS)

Hou, Jiangyuan

Corrosion control of composite materials, particularly aluminum-matrix and cement-matrix composites, was addressed by surface treatment, composite formulation and cathodic protection. Surface treatment methods studied include anodization in the case of aluminum-matrix composites and oxidation treatment (using water) in the case of steel rebar for reinforcing concrete. The effects of reinforcement species (aluminum nitride (AIN) versus silicon carbide (SiC) particles) in the aluminum-matrix composites and of admixtures (carbon fibers, silica fume, latex and methylcellulose) in concrete on the corrosion resistance of composites were addressed. Moreover, the effect of admixtures in concrete and of admixtures in mortar overlay (as anode on concrete) on the efficiency of cathodic protection of steel reinforced concrete was studied. For SiC particle filled aluminum, anodization was performed successfully in an acid electrolyte, as for most aluminum alloys. However, for AlN particle filled aluminum, anodization needs to be performed in an alkaline (0.7 N NaOH) electrolyte instead. The concentration of NaOH in the electrolyte was critical. It was found that both silica fume and latex improved the corrosion resistance of rebar in concrete in both Ca(OH)sb2 and NaCl solutions, mainly because these admixtures decreased the water absorptivity. Silica fume was more effective than latex. Methylcellulose improved the corrosion resistance of rebar in concrete a little in Ca(OH)sb2 solution. Carbon fibers decreased the corrosion resistance of rebar in concrete, but this effect could be made up for by either silica fume or latex, such that silica fume was more effective than latex. Surface treatment in the form of water immersion for two days was found to improve the corrosion resistance of rebar in concrete. This treatment resulted in a thin uniform layer of black iron oxide (containing Fesp{2+}) on the entire rebar surface except on the cross-sectional surface. Prior to the treatment, the surface was non-uniform due to rusting. Sand blasting also made the surface uniform, but is an expensive process, compared to the water immersion method. For cathodic protection of steel rebar reinforced concrete, mortar overlay containing carbon fibers and latex needed 11% less driving voltage to protect the rebar in concrete than plain mortar overlay. However, multiple titanium electrical contacts were necessary, whether the overlay contained carbon fibers or not. For the same overlay (containing carbon fibers and latex), admixtures in the concrete also made a significant difference on the effect of cathodic protection; concrete with carbon fibers and silica fume needed 18% less driving voltage than plain concrete and 28% less than concrete containing silica fume.

Influence of Chemical Treatment on Thermal Decomposition and Crystallite Size of Coir Fiber

NASA Astrophysics Data System (ADS)

Manjula, R.; Raju, N. V.; Chakradhar, R. P. S.; Kalkornsurapranee, Ekwipoo; Johns, Jobish

2018-01-01

Coir fibers were treated with sodium hydroxide (NaOH) and glutaraldehyde (GA). The influence of alkali and aldehyde treatment on thermal degradation and crystallinity of coir fiber was studied in detail. Thermogravimetric analysis and X-ray diffraction techniques were mainly used to characterize the coir samples. Activation energy of degradation was calculated from Broido and Horowitz-Metzger equations. NaOH-treated samples showed an increase in thermal stability. Removal of impurities such as waxy and fatty acid residues from the coir fiber by reacting with strong base solution improved the stability of fiber. Crosslinking of cellulose with GA in the fiber enhanced the stability of the material. Scanning electron microscopy was employed to analyze the change in surface morphology upon chemical treatment. Improvement in the properties suggests that NaOH and GA can be effectively used to modify coir fiber with excellent stability.

Toxicology and occupational hazards of new materials and processes in metal surface treatment, powder metallurgy, technical ceramics, and fiber-reinforced plastics.

PubMed

Midtgård, U; Jelnes, J E

1991-12-01

Many new materials and processes are about to find their way from the research laboratory into industry. The present paper describes some of these processes and provides an overview of possible occupational hazards and a list of chemicals used or produced in the processes. The technological areas that are considered are metal surface treatment (ion implantation, physical and chemical vapor deposition, plasma spraying), powder metallurgy, advanced technical ceramics, and fiber-reinforced plastics.

Environmental effects on the tensile strength of chemically vapor deposited silicon carbide fibers

NASA Technical Reports Server (NTRS)

Bhatt, R. T.; Kraitchman, M. D.

1985-01-01

The room temperature and elevated temperature tensile strengths of commercially available chemically vapor-deposited (CVD) silicon carbide fibers were measured after 15 min heat treatment to 1600 C in various environments. These environments included oxygen, air, argon and nitrogen at one atmosphere and vacuum at 10/9 atmosphere. Two types of fibers were examined which differed in the SiC content of their carbon-rich coatings. Threshold temperature for fiber strength degradation was observed to be dependent on the as-received fiber-flaw structure, on the environment and on the coating. Fractographic analyses and flexural strength measurements indicate that tensile strength losses were caused by surface degradation. Oxidation of the surface coating is suggested as one possible degradation mechanism. The SiC fibers containing the higher percentage of SiC near the surface of the carbon-rich coating show better strength retention and higher elevated temperature strength.

Effect of Fiber Esterification on Fundamental Properties of Oil Palm Empty Fruit Bunch Fiber/Poly(butylene adipate-co-terephthalate) Biocomposites

PubMed Central

Siyamak, Samira; Ibrahim, Nor Azowa; Abdolmohammadi, Sanaz; Yunus, Wan Md Zin Wan; Rahman, Mohamad Zaki AB

2012-01-01

A new class of biocomposites based on oil palm empty fruit bunch fiber and poly(butylene adipate-co-terephthalate) (PBAT), which is a biodegradable aliphatic aromatic co-polyester, were prepared using melt blending technique. The composites were prepared at various fiber contents of 10, 20, 30, 40 and 50 wt% and characterized. Chemical treatment of oil palm empty fruit bunch (EFB) fiber was successfully done by grafting succinic anhydride (SAH) onto the EFB fiber surface, and the modified fibers were obtained in two levels of grafting (low and high weight percentage gain, WPG) after 5 and 6 h of grafting. The FTIR characterization showed evidence of successful fiber esterification. The results showed that 40 wt% of fiber loading improved the tensile properties of the biocomposite. The effects of EFB fiber chemical treatments and various organic initiators content on mechanical and thermal properties and water absorption of PBAT/EFB 60/40 wt% biocomposites were also examined. The SAH-g-EFB fiber at low WPG in presence of 1 wt% of dicumyl peroxide (DCP) initiator was found to significantly enhance the tensile and flexural properties as well as water resistance of biocomposite (up to 24%) compared with those of untreated fiber reinforced composites. The thermal behavior of the composites was evaluated from thermogravimetric analysis (TGA)/differential thermogravimetric (DTG) thermograms. It was observed that, the chemical treatment has marginally improved the biocomposites’ thermal stability in presence of 1 wt% of dicumyl peroxide at the low WPG level of grafting. The improved fiber-matrix surface enhancement in the chemically treated biocomposite was confirmed by SEM analysis of the tensile fractured specimens. PMID:22408394

Sapphire reinforced alumina matrix composites

NASA Technical Reports Server (NTRS)

Jaskowiak, Martha H.; Setlock, John A.

1994-01-01

Unidirectionally reinforced A1203 matrix composites have been fabricated by hot pressing. Approximately 30 volume % of either coated or uncoated sapphire fiber was used as reinforcement. Unstabilized ZrO2 was applied as the fiber coating. Composite mechanical behavior was analyzed both after fabrication and after additional heat treatment. The results of composite tensile tests were correlated with fiber-matrix interfacial shear strengths determined from fiber push-out tests. Substantially higher strength and greater fiber pull-out were observed for the coated fiber composites for all processing conditions studied. The coated fiber composites retained up to 95% and 87% of their as-fabricated strength when heat treated at 14000C for 8 or 24 hours, respectively. Electron microscopy analysis of the fracture surfaces revealed extensive fiber pull-out both before and after heat treatment.

Eco-friendly surface modification on polyester fabrics by esterase treatment

NASA Astrophysics Data System (ADS)

Wu, Jindan; Cai, Guoqiang; Liu, Jinqiang; Ge, Huayun; Wang, Jiping

2014-03-01

Currently, traditional alkali deweighting technology is widely used to improve the hydrophilicity of polyester fabrics. However, the wastewater and heavy chemicals in the effluent cause enormous damage to the environment. Esterase treatment, which is feasible in mild conditions with high selectivity, can provide a clean and efficient way for polyester modification. Under the optimum conditions, the polyester fabric hydrolysis process of esterase had a linear kinetics. X-ray photoelectron spectrometry (XPS) results showed that hydroxyl and carboxyl groups were produced only on the surface of modified fiber without changing the chemical composition of the bulk. These fibers exhibited much improved fabric wicking, as well as greatly improved oily stain removal performance. Compared to the harsh alkali hydrolysis, the enzyme treatment led to smaller weight loss and better fiber integrity. The esterase treatment technology is promising to produce higher-quality polyester textiles with an environmental friendly approach.

Hemicellulose and lignin removal on typha fiber by alkali treatment

NASA Astrophysics Data System (ADS)

Ikramullah; Rizal, Samsul; Thalib, Sulaiman; Huzni, Syifaul

2018-05-01

One of the methods commonly utilized to alter the surfaces of natural fibers for improving the interface compatibility among fiber and polymer matrix is by alkali treatment. Several natural fibers have been experimented with alkali treatments such as abaca, borassus and kenaf. There is a relatively few of literature that reports the FTIR investigation of Typha fibers. The purpose of this study is to determine the effect of alkali treatment on Typha fiber. Two of three bundle fibers are immersed in a 5% NaOH solution for one and two hours. The chemical structure of alkali-treated and untreated fibers are both being analyzed by Fourier Transform Infrared Spectroscopy (FTIR) instrument. The emergence of peak at 1155.36 cm-1 in strong intensity denotes the C-O-C asymmetric stretching in cellulose compound. The lignin composition of the fiber is typified by the stretching band of C-O group at 1247 cm-1. Meanwhile, the peak at 1735.03 cm-1 wavenumber is allegedly C=O stretching evidencing the existence of hemicelluloses and pectin. The peaks which are suspected to be hemicellulose, lignin and pectin are no longer visible in alkali treated Typha fiber. Giving alkali treatment to Typha fiber has been successfully removed impurities (hemicelluloses and lignin), as approved by the FTIR analysis. This will lead to a better contact and bonding mechanism between fiber and polymer matrix.

Stem cell responses to plasma surface modified electrospun polyurethane scaffolds.

PubMed

Zandén, Carl; Hellström Erkenstam, Nina; Padel, Thomas; Wittgenstein, Julia; Liu, Johan; Kuhn, H Georg

2014-07-01

The topographical effects from functional materials on stem cell behavior are currently of interest in tissue engineering and regenerative medicine. Here we investigate the influence of argon, oxygen, and hydrogen plasma surface modification of electrospun polyurethane fibers on human embryonic stem cell (hESC) and rat postnatal neural stem cell (NSC) responses. The plasma gases were found to induce three combinations of fiber surface functionalities and roughness textures. On randomly oriented fibers, plasma treatments lead to substantially increased hESC attachment and proliferation as compared to native fibers. Argon plasma was found to induce the most optimal combination of surface functionality and roughness for cell expansion. Contact guided migration of cells and alignment of cell processes were observed on aligned fibers. Neuronal differentiation around 5% was found for all samples and was not significantly affected by the induced variations of surface functional group distribution or individual fiber topography. In this study the influence of argon, oxygen, and hydrogen plasma surface modification of electrospun polyurethane fibers on human embryonic stem cell and rat postnatal neural stem cell (NSC) responses is studied with the goal of clarifying the potential effects of functional materials on stem cell behavior, a topic of substantial interest in tissue engineering and regenerative medicine. Copyright © 2014 Elsevier Inc. All rights reserved.

Effects of Surface Modification on the Mechanical Properties of Flax/β-Polypropylene Composites

PubMed Central

Wu, Chang-Mou; Lai, Wen-You; Wang, Chen-Yu

2016-01-01

The effects of surface treatment of flax fibers featuring vinyltrimethoxy silane (VTMO) and maleic anhydride-polypropylene (MAPP) on the mechanical properties of flax/PP composites were investigated. α-polypropylene (α-PP) and β-polypropylene (β-PP) were used as matrices for measuring the mechanical properties of the flax fiber/polypropylene (flax/PP) composites. Flax/PP composites composed of double-covered uncommingled yarn (DCUY) were prepared using a film-stacking technique. The influence of surface treatment on the tensile, flexural, impact, and water uptake properties of Flax/PP composites were investigated. MAPP treatment was suitable for flax/PP composites in terms of superior tensile and impact properties. VTMO treatment showed superior flexural properties and less influence on the impact properties after moisture absorption. PMID:28773439

The Effect of Adhesion Interaction on the Mechanical Properties of Thermoplastic Basalt Plastics

NASA Astrophysics Data System (ADS)

Bashtannik, P. I.; Kabak, A. I.; Yakovchuk, Yu. Yu.

2003-01-01

The effect of temperature, adhesion time, and surface treatment of a reinforcing filler on the mechanical properties of thermoplastic basalt plastics based on a high-density polyethylene and a copolymer of 1,3,5-trioxane with 1,3-dioxolan is investigated. An extreme dependence for the adhesive strength in a thermoplastic-basalt fiber system is established and its effect on the mechanical properties of basalt plastics and the influence of the adhesion contact time on the adhesive strength in the system are clarified. The surface modification of basalt fibers in acidic and alkaline media intensifies the adhesion of thermoplastics to them owing to a more developed surface of the reinforcing fibers after etching. It is found that the treatment in the acidic medium is more efficient and considerably improves the mechanical properties of basalt plastics.

Effects of fiber density and plasma modification of nanofibrous membranes on the adhesion and growth of HaCaT keratinocytes.

PubMed

Bacakova, Marketa; Lopot, Frantisek; Hadraba, Daniel; Varga, Marian; Zaloudkova, Margit; Stranska, Denisa; Suchy, Tomas; Bacakova, Lucie

2015-01-01

It may be possible to regulate the cell colonization of biodegradable polymer nanofibrous membranes by plasma treatment and by the density of the fibers. To test this hypothesis, nanofibrous membranes of different fiber densities were treated by oxygen plasma with a range of plasma power and exposure times. Scanning electron microscopy and mechanical tests showed significant modification of nanofibers after plasma treatment. The intensity of the fiber modification increased with plasma power and exposure time. The exposure time seemed to have a stronger effect on modifying the fiber. The mechanical behavior of the membranes was influenced by the plasma treatment, the fiber density, and their dry or wet state. Plasma treatment increased the membrane stiffness; however, the membranes became more brittle. Wet membranes displayed significantly lower stiffness than dry membranes. X-ray photoelectron spectroscopy (XPS) analysis showed a slight increase in oxygen-containing groups on the membrane surface after plasma treatment. Plasma treatment enhanced the adhesion and growth of HaCaT keratinocytes on nanofibrous membranes. The cells adhered and grew preferentially on membranes of lower fiber densities, probably due to the larger area of void spaces between the fibers. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

Development of high temperature resistant graphite fiber coupling agents

NASA Technical Reports Server (NTRS)

Griffin, R. N.

1975-01-01

Surface treatments were investigated as potential coupling agents to improve the elevated temperature shear strength retention of polyimide/graphite and polyphenylquinoxaline/graphite composites. The potential coupling agents were evaluated by fiber strand tensile tests, fiber and composite weight losses at 533 and 588K, and by interlaminar shear strength retention at 533 and 588K. The two surface treatments selected for more extensive evaluation were a coating of Ventromer T-1, a complex organometallic reaction product of titanium tetrachloride and trimethyl borate, and a polyphenylquinoxaline (PPQ) sizing which was pyrolyzed in nitrogen to form a carbonaceous layer on the fiber. Pyrolyzed polyphenylquinoxaline is a satisfactory coupling agent for polyimide/Thornel 300 graphite fiber composites. During 1000 hours aging at 588K such composites lose a little over half their transverse tensile strength, and suffer a slight loss in flexural modulus. No degradation of flexural strength or interlaminar shear strength occured during 1000 hours aging at 588K. None of the coupling agents examined had a markedly beneficial effect with polyphenylquinoxaline composites.

The effect of oxyalkylation and application of polymer dispersions on the thermoformability and extensibility of paper.

PubMed

Kouko, Jarmo; Setälä, Harri; Tanaka, Atsushi; Khakalo, Alexey; Ropponen, Jarmo; Retulainen, Elias

2018-04-15

Wood fiber-based packaging materials, as renewable materials, have growing market potential due to their sustainability. A new breakthrough in cellulose-based packaging requires some improvement in the mechanical properties of paper. Bleached softwood kraft pulp was mechanically treated, in two stages, using high- and low-consistency refining, sequentially. Chemical treatment of pulp using the oxyalkylation method was applied to modify a portion of fiber material, especially the fiber surface, and its compatibility with polymer dispersions including one carbohydrate polymer. The results showed that the compatibility of the cellulosic fibers with some polymers could be improved with oxyalkylation. By adjusting mechanical and chemical treatments, and the thermoforming conditions, the formability of paper was improved, but simultaneously the strength and stiffness decreased. The results suggest that the formability of the paper is not a direct function of the extensibility of the applied polymer, but also depends on the fiber network structure and surface energy. Copyright © 2018 The Authors. Published by Elsevier Ltd.. All rights reserved.

The effects of low-temperature plasma treatment on the capillary properties of inorganic fibers

NASA Astrophysics Data System (ADS)

Garifullin, A. R.; Abdullin, I. Sh; Skidchenko, E. A.; Krasina, I. V.; Shaekhov, M. F.

2016-01-01

Solving the problem of achieving high adhesion between the components in the polymeric composite material (PCM) based on carbon fibers (CF) and basalt fibers (BF) is proposed to use the radio-frequency (RF) plasma under lower pressure by virtue of efficiency, environmental friendliness and rationality of the method. The paper gives the results of studies of the properties of CF and BF after RF capacitive discharge plasma treatment. The plasma modification modes of carbon and basalt fiber were investigated. The efficiency of treatment tool in surface properties modification of carbon and basalt fibers was found, namely capillary properties of CF and BF were researched. The optimal treatment modes were selected. It was found that the method of plasma modification in the radio-frequency capacitive discharge under the lower pressure contributes enhancing the capillary properties of inorganic fibers, in particular carbon and basalt ones. It shows the tendency to increase of the adhesive properties in PCM, and, consequently, the increase of the physical and mechanical properties of the products.

Application of non-equilibrium plasmas in treatment of wool fibers and seeds

NASA Astrophysics Data System (ADS)

Petrović, Zoran

2003-10-01

While large effort is under way to achieve stable, large area, non-equilibrium plasma reactors operating at atmospheric pressure we should still consider application of low pressure reactors, which provide well defined, easily controlled reactive plasmas. Therefore, the application of low pressure rf plasmas for the treatment of wool and seed was investigated. The studies were aimed at establishing optimal procedure to achieve better wettability, dyeability and printability of wool. Plasma treatment led to a modification of wool fiber topography and formation of new polar functional groups inducing the increase of wool hydrophylicity. Plasma activation of fiber surface was also used to achieve better binding of biopolymer chitosan to wool in order to increase the content of favorable functional groups and thus improving sorption properties of recycled wool fibers for heavy metal ions and acid dyes. In another study, the increase of germination percentage of seeds induced by plasmas was investigated. We have selected dry (unimbibed) Empress tree seeds (Paulownia tomentosa Steud.). Empress tree seed has been studied extensively and its mechanism of germination is well documented. Germination of these seeds is triggered by light in a limited range of wavelengths. Interaction between activated plasma particles and seed, inside the plasma reactor, leads to changes in its surface topography, modifies the surface layer and increases the active surface area. Consequently, some bioactive nitrogeneous compounds could be bound to the activated surface layer causing the increment of germination percentage.

Effects of endodontic post surface treatment, dentin conditioning, and artificial aging on the retention of glass fiber-reinforced composite resin posts.

PubMed

Albashaireh, Zakereyya S; Ghazal, Muhamad; Kern, Matthias

2010-01-01

Several post surface treatments with or without the application of a bonding agent have been recommended to improve the bond strength of resin cements to posts. A regimen that produces the maximum bond strength of glass fiber-reinforced composite resin posts has not been verified. The purpose of this study was to evaluate the influence of post surface conditioning methods and artificial aging on the retention and microleakage of adhesively luted glass fiber-reinforced composite resin posts. Seventy-two endodontically treated single-rooted teeth were prepared for glass fiber-reinforced composite resin posts. The posts were submitted to 3 different surface treatments (n=24), including no treatment, etching with phosphoric acid, and airborne-particle abrasion. Subgroups of the posts (n=8) were then allocated for 3 different experimental conditions: no artificial aging, no bonding agent; no artificial aging, bonding agent; or artificial aging, bonding agent. The posts were luted with resin cement (Calibra). Post retention was measured in tension at a crosshead speed of 2 mm/min. The posts assigned for microleakage investigation were placed in fuchsin dye for 72 hours. The dislodged posts and the post spaces were examined microscopically to evaluate the mode of failure and explore the microleakage. Data were analyzed by 2-way ANOVA followed by Tukey HSD test (alpha=.05). The mean (SD) retention values for test groups ranged from 269 (63.8) to 349 (52.2) N. The retention values of the airborne-particle-abrasion group were significantly higher than those of the acidic-treatment and no-treatment groups. The application of bonding agent on the post surface produced no significant influence on retention. The mean retention values after artificial aging were significantly higher than without artificial aging. Microscopic evaluation demonstrated that the failure mode was primarily mixed. Treating the surface of the posts with phosphoric acid for 15 seconds before cementation produced no significant improvement in post retention. Airborne-particle abrasion of the surface of the post significantly improved post retention. Copyright 2010 The Editorial Council of the Journal of Prosthetic Dentistry. Published by Mosby, Inc. All rights reserved.

Switchable hydrophobic/hydrophilic surface of electrospun poly (l-lactide) membranes obtained by CF₄microwave plasma treatment

DOE PAGES

Yue, Mengyao; Zhou, Baoming; Jiao, Kunyan; ...

2014-11-29

A switchable surface that promotes either hydrophobic or hydrophilic wettability of poly (L-lactide) (PLLA) microfibrous membranes is obtained by CF₄ microwave plasma treatment in this paper. The results indicated that both etching and grafting process occurred during the CF₄ plasma treatment and these two factors synergistically affected the final surface wettability of PLLA membranes. When plasma treatment was taken under a relatively low power, the surface wettability of PLLA membranes turned from hydrophobic to hydrophilic. Especially when CF₄ plasma treatment was taken under 100 W for 10 min and 150 W for 5 min, the water contact angle sharply decreasedmore » from 116 ± 3.0° to ~0°. According to Field-emission scanning electron microscopy (FESEM) results, the PLLA fibers were notably etched by CF₄ plasma treatment. Combined with the X-ray photoelectron spectroscopy (XPS) measurements, only a few fluorine-containing groups were grafted onto the surface, so the etching effect directly affected the surface wettability of PLLA membranes in low plasma power condition. However, with the plasma power increasing to 200 W, the PLLA membrane surface turned to hydrophobic again. In contrast, the morphology changes of PLLA fiber surfaces were not obvious while a large number of fluorine-containing groups grafted onto the surface. So the grafting effect gradually became the major factor for the final surface wettability.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Yue, Mengyao; Zhou, Baoming; Jiao, Kunyan

A switchable surface that promotes either hydrophobic or hydrophilic wettability of poly (L-lactide) (PLLA) microfibrous membranes is obtained by CF₄ microwave plasma treatment in this paper. The results indicated that both etching and grafting process occurred during the CF₄ plasma treatment and these two factors synergistically affected the final surface wettability of PLLA membranes. When plasma treatment was taken under a relatively low power, the surface wettability of PLLA membranes turned from hydrophobic to hydrophilic. Especially when CF₄ plasma treatment was taken under 100 W for 10 min and 150 W for 5 min, the water contact angle sharply decreasedmore » from 116 ± 3.0° to ~0°. According to Field-emission scanning electron microscopy (FESEM) results, the PLLA fibers were notably etched by CF₄ plasma treatment. Combined with the X-ray photoelectron spectroscopy (XPS) measurements, only a few fluorine-containing groups were grafted onto the surface, so the etching effect directly affected the surface wettability of PLLA membranes in low plasma power condition. However, with the plasma power increasing to 200 W, the PLLA membrane surface turned to hydrophobic again. In contrast, the morphology changes of PLLA fiber surfaces were not obvious while a large number of fluorine-containing groups grafted onto the surface. So the grafting effect gradually became the major factor for the final surface wettability.« less

Mechanical properties of untreated and alkaline treated fibers from zalacca midrib wastes

NASA Astrophysics Data System (ADS)

Raharjo, Wahyu Purwo; Soenoko, Rudy; Purnowidodo, Anindito; Choiron, Mochammad Agus; Triyono

2016-03-01

The environmental concern has been raised due to the abundance of waste from synthetic materials which cannot be biodegraded after their life-time. It provides opportunity to exploit natural resources which are neglected. For example, midrib wastes from zalacca plants after cutting are able to utilize as composite reinforcement. The aim of this research was to characterize the mechanical properties of zalacca midrib fibers. As other ones, zalacca midrib fibers consisted of cellulose, hemicellulose and lignin, which their compositions were 42.54, 34.35 and 28.01 % respectively. To raise their cellulose content, the zalacca fibers were alkaline treated by immersion in the sodium hydroxide for 2 hours and rinsing in the distilled water. The concentration of sodium hydroxide was varied 1 and 5%. To investigate the influence of alkaline treatment, the mechanical testing and morphological analysis was performed. The tensile testing was done to obtain ultimate strength, elastic modulus and strain to fracture. The surface morphology of fibers was observed by SEM. The average ultimate tensile strength of zalacca fibers ranged from 182.12 MPa (untreated) to 417.94 MPa (5%NaOH treated). The diameter measurement showed that the alkaline treatment reduce the average fiber diameters due to the decline of the hemicellulose and lignin content as fiber matrix. This caused the increase of the tensile strength and elastic modulus due to the reduction of diameters as divider meanwhile the cellulose content as structural supporter of the fibers was relatively constant. From the SEM analysis, it was shown that the alkaline treatment reduced the fiber matrix so that its surface morphology became rougher due to the microfibrils appearance.

Oxidation-induced contraction and strengthening of boron fibers

NASA Technical Reports Server (NTRS)

Dicarlo, J. A.; Wagner, T. C.

1981-01-01

An investigation of the physical and mechanical effects of thermal treatment in a controlled oxygen-argon atmosphere on boron fibers is reported, with attention to the optimization of such treatment as a secondary processing method for improvement of fiber strength. The strengthening mechanism is comprised of an oxidation-induced axial contraction of the fiber, accompanied by axial compression of strength-limiting flaws within the fiber's tungsten boride core. It was found that after an oxidation contraction of 0.3% near 900 C, and a slight surface etch near 100 C, the average tensile strength of 203-micron fibers increased from 500 to 800 ksi. Various physical observations are used to develop mechanistic models of oxidation, contraction, and the formation of new flaws in the boron sheath at contractions greater than 0.3%.

New High-Performance SiC Fiber Developed for Ceramic Composites

NASA Technical Reports Server (NTRS)

DiCarlo, James A.; Yun, Hee Mann

2002-01-01

Sylramic-iBN fiber is a new type of small-diameter (10-mm) SiC fiber that was developed at the NASA Glenn Research Center and was recently given an R&D 100 Award for 2001. It is produced by subjecting commercially available Sylramic (Dow Corning, Midland, MI) SiC fibers, fabrics, or preforms to a specially designed high-temperature treatment in a controlled nitrogen environment for a specific time. It can be used in a variety of applications, but it currently has the greatest advantage as a reinforcement for SiC/SiC ceramic composites that are targeted for long-term structural applications at temperatures higher than the capability of metallic superalloys. The commercial Sylramic SiC fiber, which is the precursor for the Sylramic-iBN fiber, is produced by Dow Corning, Midland, Michigan. It is derived from polymers at low temperatures and then pyrolyzed and sintered at high temperatures using boron-containing sintering aids (ref. 1). The sintering process results in very strong fibers (>3 GPa) that are dense, oxygen-free, and nearly stoichiometric. They also display an optimum grain size that is beneficial for high tensile strength, good creep resistance, and good thermal conductivity (ref. 2). The NASA-developed treatment allows the excess boron in the bulk to diffuse to the fiber surface where it reacts with nitrogen to form an in situ boron nitride (BN) coating on the fiber surface (thus the product name of Sylramic-iBN fiber). The removal of boron from the fiber bulk allows the retention of high tensile strength while significantly improving creep resistance and electrical conductivity, and probably thermal conductivity since the grains are slightly larger and the grain boundaries cleaner (ref. 2). Also, as shown in the graph, these improvements allow the fiber to display the best rupture strength at high temperatures in air for any available SiC fiber. In addition, for CMC applications under oxidizing conditions, the formation of an in situ BN surface layer creates a more environmentally durable fiber surface not only because a more oxidation-resistant BN is formed, but also because this layer provides a physical barrier between contacting fibers with oxidation-prone SiC surface layers (refs. 3 and 4). This year, Glenn demonstrated that the in situ BN treatment can be applied simply to Sylramic fibers located within continuous multifiber tows, within woven fabric pieces, or even assembled into complex product shapes (preforms). SiC/SiC ceramic composite panels have been fabricated from Sylramic-iBN fabric and then tested at Glenn within the Ultra-Efficient Engine Technology Program. The test conditions were selected to simulate those experienced by hot-section components in advanced gas turbine engines. The results from testing at Glenn demonstrate all the benefits expected for the Sylramic-iBN fibers. That is, the composites displayed the best thermostructural performance in comparison to composites reinforced by Sylramic fibers and by all other currently available high-performance SiC fiber types (refs. 3 and 5). For these reasons, the Ultra-Efficient Engine Technology Program has selected the Sylramic-iBN fiber for ongoing efforts aimed at SiC/SiC engine component development.

Release of metronidazole from electrospun poly(L-lactide-co-D/L-lactide) fibers for local periodontitis treatment.

PubMed

Reise, Markus; Wyrwa, Ralf; Müller, Ulrike; Zylinski, Matthias; Völpel, Andrea; Schnabelrauch, Matthias; Berg, Albrecht; Jandt, Klaus D; Watts, David C; Sigusch, Bernd W

2012-02-01

We aimed to achieve detailed biomaterials characterization of a drug delivery system for local periodontitis treatment based on electrospun metronidazole-loaded resorbable polylactide (PLA) fibers. PLA fibers loaded with 0.1-40% (w/w) MNA were electrospun and were characterized by SEM and DSC. HPLC techniques were used to analyze the release profiles of metronidazole (MNA) from these fibers. The antibacterial efficacy was determined by measuring inhibition zones of drug-containing aliquots from the same electrospun fiber mats in an agar diffusion test. Three pathogenic periodontal bacterial strains: Fusobacterium nucleatum, Aggregatibacter actinomycetemcomitans and Porphyromonas gingivalis were studied. Cytotoxicity testing was performed with human gingival fibroblasts by: (i) counting viable cells via live/dead staining methods and (ii) by exposing cells directly onto the surface of MNA-loaded fibers. MNA concentration influenced fiber diameters and thus w/w surface areas: diameter being minimal and area maximal at 20% MNA. HPLC showed that these 20% MNA fibers had the fastest initial MNA release. From the third day, MNA release was slower and nearly linear with time. All fiber mats released 32-48% of their total drug content within the first 7 days. Aliquots of media taken from the fiber mats inhibited the growth of all three bacterial strains. MNA released up to the 28th day from fiber mats containing 40% MNA significantly decreased the viability of F. nucleatum and P. gingivalis and up to the 2nd day also for the resistant A. actinomycetemcomitans. All of the investigated fibers and aliquots showed excellent cytocompatibility. This study shows that MNA-loaded electrospun fiber mats represent an interesting class of resorbable drug delivery systems. Sustained drug release properties and cytocompatibility suggest their potential clinical applicability for the treatment of periodontal diseases. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Oil spills abatement: factors affecting oil uptake by cellulosic fibers.

PubMed

Payne, Katharine C; Jackson, Colby D; Aizpurua, Carlos E; Rojas, Orlando J; Hubbe, Martin A

2012-07-17

Wood-derived cellulosic fibers prepared in different ways were successfully employed to absorb simulated crude oil, demonstrating their possible use as absorbents in the case of oil spills. When dry fibers were used, the highest sorption capacity (six parts of oil per unit mass of fiber) was shown by bleached softwood kraft fibers, compared to hardwood bleached kraft and softwood chemithermomechanical pulp(CTMP) fibers. Increased refining of CTMP fibers decreased their oil uptake capacity. When the fibers were soaked in water before exposure to the oil, the ability of the unmodified kraft fibers to sorb oil was markedly reduced, whereas the wet CTMP fibers were generally more effective than the wet kraft fibers. Predeposition of lignin onto the surfaces of the bleached kraft fibers improved their ability to take up oil when wet. Superior ability to sorb oil in the wet state was achieved by pretreating the kraft fibers with a hydrophobic sizing agent, alkenylsuccinic anhydride (ASA). Contact angle tests on a model cellulose surface showed that some of the sorption results onto wetted fibers could be attributed to the more hydrophobic nature of the fibers after treatment with either lignin or ASA.

Modifying Matrix Materials to Increase Wetting and Adhesion

NASA Technical Reports Server (NTRS)

Zhong, Katie

2011-01-01

In an alternative approach to increasing the degrees of wetting and adhesion between the fiber and matrix components of organic-fiber/polymer matrix composite materials, the matrix resins are modified. Heretofore, it has been common practice to modify the fibers rather than the matrices: The fibers are modified by chemical and/or physical surface treatments prior to combining the fibers with matrix resins - an approach that entails considerable expense and usually results in degradation (typically, weakening) of fibers. The alternative approach of modifying the matrix resins does not entail degradation of fibers, and affords opportunities for improving the mechanical properties of the fiber composites. The alternative approach is more cost-effective, not only because it eliminates expensive fiber-surface treatments but also because it does not entail changes in procedures for manufacturing conventional composite-material structures. The alternative approach is best described by citing an example of its application to a composite of ultra-high-molecular- weight polyethylene (UHMWPE) fibers in an epoxy matrix. The epoxy matrix was modified to a chemically reactive, polarized epoxy nano-matrix to increase the degrees of wetting and adhesion between the fibers and the matrix. The modification was effected by incorporating a small proportion (0.3 weight percent) of reactive graphitic nanofibers produced from functionalized nanofibers into the epoxy matrix resin prior to combining the resin with the UHMWPE fibers. The resulting increase in fiber/matrix adhesion manifested itself in several test results, notably including an increase of 25 percent in the maximum fiber pullout force and an increase of 60-65 percent in fiber pullout energy. In addition, it was conjectured that the functionalized nanofibers became involved in the cross linking reaction of the epoxy resin, with resultant enhancement of the mechanical properties and lower viscosity of the matrix.

Effect of liquid epoxidized natural rubber (LENR) on mechanical properties and morphology of natural rubber/high density polyethylene/mengkuang fiber (NR/HDPE/MK) bio-composite

NASA Astrophysics Data System (ADS)

Piah, Mohd Razi Mat; Baharum, Azizah

2016-11-01

The use of mengkuang fiber (MK) fibers in NR/HDPE (40/60) blend was studied via surface modification of fiber. The MK fiber was pre-washed with 5%wt/v sodium hydroxide solution prior to treatment with liquid epoxidized natural rubber (LENR). The concentration of LENR were varied from 5%-20%wt in toluene. The effects of LENR concentrations were studied in terms of mechanical properties and morphology formed. Melt-blending was performed using an internal mixer (Haake Rheomix 600). The processing parameters identified were 135°C temperature, 45 rpm rotor speed, 12 minutes processing time and at 20%wt MK fiber loading. The optimum LENR treatment concentration was obtained at 5%wt with tensile strength, tensile modulus, and impact strength of 10.3 MPa, 414.2 MPa and 14.4 kJ/m2 respectively. The tensile modulus of LENR-treated MK fiber filled NR/HDPE bio-composite has shown enhancement up to 16.7% higher than untreated MK fiber. The tensile and impact strength were decreased with increasing LENR concentration due to the broken of MK fibers to smaller particles and adhered to each other. FESEM micrographs confirmed the formation of fiber-fiber agglomeration in NR/HDPE blends. The optical microscope analysis shows MK fibers is shorter than original fiber lengths after NaOH-LENR surface modification. The internal bonding forces of MK fiber seems to be weaker than external force exerted on it, therefore, the MK fiber has broken to smaller particles and reduced the mechanical properties of NR/HDPE/MK(20%) bio-composite.

Effects of surface treatments and bonding types on the interfacial behavior of fiber metal laminate based on magnesium alloy

NASA Astrophysics Data System (ADS)

Zhang, Xi; Ma, Quanyang; Dai, Yu; Hu, Faping; Liu, Gang; Xu, Zouyuan; Wei, Guobing; Xu, Tiancai; Zeng, Qingwen; Xie, Weidong

2018-01-01

Fiber metal laminates based on magnesium alloys (MgFML) with different surface treatments and different bonding types were tested and analyzed. By using dynamic contact angle measurement and scanning electron microscopy (SEM), it was found that phosphating treatment can significantly improve the surface energy and wettability of magnesium alloy, and the surface energy of phosphated magnesium alloy was approximately 50% higher than that of abraded-only magnesium alloy. The single cantilever beam (SCB) test showed that the interfacial fracture energies of directly bonded MgFMLs based on abraded-only magnesium and abraded + phosphated magnesium were 650 J/m2 and 1030 J/m2, respectively, whereas the interfacial fracture energies of indirectly bonded MgFMLs were 1650 J/m2 and 2260 J/m2, respectively. Phosphating treatment and modified polypropylene interleaf were observed to improve the tensile strength and interfacial fracture toughness of MgFML. In addition, the rougher surface was more conducive to enhance the bonding strength and interfacial fracture toughness of MgFML.

Bioactivity of cellulose acetate/hydroxyapatite nanoparticle composite fiber by an electro-spinning process.

PubMed

Kwak, Dae Hyun; Lee, Eun Ju; Kim, Deug Joong

2014-11-01

Hydroxyapatite/cellulose acetate composite webs were fabricated by an electro-spinning process. This electro-spinning process makes it possible to fabricate complex three-dimensional shapes. Nano fibrous web consisting of cellulose acetate and hydroxyapatite was produced from their mixture solution by using an electro-spinning process under high voltage. The surface of the electro-spun fiber was modified by a plasma and alkaline solution in order to increase its bioactivity. The structure, morphology and properties of the electro-spun fibers were investigated and an in-vitro bioactivity test was evaluated in simulated body fluid (SBF). Bioactivity of the electro-spun web was enhanced with the filler concentration and surface treatment. The surface changes of electro-spun fibers modified by plasma and alkaline solution were investigated by FT-IR (Fourier Transform Infrared Spectroscopy) and XPS (X-ray Photoelectron Spectroscopy).

Effects of Fiber Orientation on the Frictional Properties and Damage of Regenerative Articular Cartilage Surfaces

PubMed Central

Accardi, Mario Alberto; McCullen, Seth D.; Callanan, Anthony; Chung, Sangwon; Cann, Philippa M.

2013-01-01

Articular cartilage provides a low-friction, wear-resistant surface for diarthrodial joints. Due to overloading and overuse, articular cartilage is known to undergo significant wear and degeneration potentially resulting in osteoarthritis (OA). Regenerative medicine strategies offer a promising solution for the treatment of articular cartilage defects and potentially localized early OA. Such strategies rely on the development of materials to restore some aspects of cartilage. In this study, microfibrous poly(ɛ-caprolactone) scaffolds of varying fiber orientations (random and aligned) were cultured with bovine chondrocytes for 4 weeks in vitro, and the mechanical and frictional properties were evaluated. Mechanical properties were quantified using unconfined compression and tensile testing techniques. Frictional properties were investigated at physiological compressive strains occurring in native articular cartilage. Scaffolds were sheared along the fiber direction, perpendicular to the fiber direction and in random orientation. The evolution of damage as a result of shear was evaluated via white light interferometry and scanning electron microscopy. As expected, the fiber orientation strongly affected the tensile properties as well as the compressive modulus of the scaffolds. Fiber orientation did not significantly affect the equilibrium frictional coefficient, but it was, however, a key factor in dictating the evolution of surface damage on the surface. Scaffolds shear tested perpendicular to the fiber orientation displayed the highest surface damage. Our results suggest that the fiber orientation of the scaffold implanted in the joint could strongly affect its resistance to damage due to shear. Scaffold fiber orientation should thus be carefully considered when using microfibrous scaffolds. PMID:23688110

Modification of surface properties of cellulosic substrates by quaternized silicone emulsions.

PubMed

Purohit, Parag S; Somasundaran, P

2014-07-15

The present work describes the effect of quaternization of silicones as well as the relevant treatment parameter pH on the frictional, morphological and relaxation properties of fabric substrates. Due to their unique surface properties, silicone polymers are extensively used to modify surface properties of various materials, although the effects of functionalization of silicones and relevant process conditions on modification of substrates are not well understood. Specifically we show a considerable reduction in fabric friction, roughness and waviness upon treatment with quaternized silicones. The treatment at acidic pH results in better deposition of silicone polymers onto the fabric as confirmed through streaming potential measurements which show charge reversal of the fabric. Interestingly, Raman spectroscopy studies show the band of C-O ring stretching mode at ∼1095 cm(-1) shift towards higher wavenumber indicating lowering of stress in fibers upon appropriate silicone treatment. Thus along with the morphological and frictional properties being altered, silicone treatment can lead to a reduction in fabric strain. It is concluded that the electrostatic interactions play an initial role in modification of the fiber substrate followed by multilayer deposition of polymer. This multi-technique approach to study fiber properties upon treatment by combining macro to molecular level methods has helped in understanding of new functional coating materials. Copyright © 2014 Elsevier Inc. All rights reserved.

A Preliminary Study of the Spreading of AKD in the Presence of Capillary Structures.

PubMed

Shen, Wei; Parker, Ian H.

2001-08-01

There may be several mechanisms at work in the process of migration or redistribution of alkyl ketene dimers (AKD) on cellulose fiber surfaces during paper sizing and curing. This work is the second part of a continuing investigation of the spreading behavior of AKD on the surfaces of hydrophilic substrates. Paper sheets, single cotton, and cotton lint fibers and smooth cellulose film were used as substrates. These represent samples that have pores, V-shaped grooves, and no capillary structure at all. A very simple and effective testing method for studying the AKD migration behavior through these substrates was designed. AFM was used to study the surface capillary structures of cotton and cotton lint fibers. The results of this study provide hard evidence supporting our finding that capillary structures in the form of either interfiber pores in a paper sheet or V-shaped grooves on the surface of single fibers are essential in order for the spreading of molten AKD on a cellulose substrate to occur. Some preliminary results on the existence and the surface diffusion of an autophobic precursor of AKD are also presented. The results support the conclusion we reached in the first part of this investigation; i.e., the molten AKD wets but does not spread on smooth, capillary-free hydrophilic surfaces such as glass and cellulose. The driving force from interfacial energy alone does not cause spontaneous "flow-like" spreading of molten AKD on these surfaces. This is possibly associated with the formation of an autophobic precursor in front of an AKD droplet. The results in this study do not support the perception that molten AKD forms a single molecular layer on the surface of cellulose fibers by spreading during heat treatment, although the autophobic precursor in front of an AKD droplet could theoretically be of a monolayer thickness and the surface diffusion of this precursor may contribute to the sizing development after heat treatment. Copyright 2001 Academic Press.

Hydrothermally tailor-made chitosan fiber for micro-solid phase extraction of petroleum acids in crude oils.

PubMed

Zhu, Gang-Tian; Hu, Xiao-Li; He, Sheng; He, Xiao-Mei; Zhu, Shu-Kui; Feng, Yu-Qi

2018-06-05

Tailor-made chitosan fiber was prepared via hydrothermal treatment to serve as a micro-solid phase extraction (micro-SPE) sorbent for the analysis of petroleum acids (PAs) in crude oils. Chitosan fiber, which is commercial and cheap, has a diameter of about 10 μm and a length of a few centimeters. The fibrous property of the sorbent enables the micro-SPE to deal with viscous crude oil samples because of the low back-pressure during extraction, while the abundant hydroxyl groups and amino groups on the surface of chitosan fiber can provide high density of specific sites for adsorption of PAs. Moreover, it was found that hydrothermal treatment at certain conditions could tune the surface properties of chitosan fiber, leading to significant improvement of the capacity of the fiber in adsorption of PAs. Using hydrothermally treated chitosan fiber as sorbent, the micro-SPE was applied to the determination of PAs in crude oils, with the advantages of easy-operation, rapidness and high sensitivity (the limits of detection range from 0.7 ng/g to 5.4 ng/g). Furthermore, coupled with comprehensive two dimensional gas chromatography-mass spectrometry (GC × GCMS), the treated chitosan fiber packed micro-SPE method showed a great potential for comprehensive profiling of PAs in crude oils. Copyright © 2018 Elsevier B.V. All rights reserved.

Novel approaches for alleviation of electrical hazards of graphite-fiber composites. [aircraft safety

NASA Technical Reports Server (NTRS)

Ramohalli, K.

1979-01-01

Four basically different approaches were considered: gasification of fibers, retention in the matrix, clumping to prevent entrainment, and electrical insulation of fibers. The techniques used to achieve them are described in some detail. These involved surface treatment of fibers to improve the wettability of fibers and coating the fibers with the selected substances before laying them up for composite fabrication. Thermogravimetric analyses were performed on the plain and treated fibers in inert (nitrogen, argon) and reactive (air) atmospheres. The treated fibers embedded in epoxy were ignited in a Bunsen flame to determine the efficiency of these treatments. A simple apparatus was assembled to detect the time for the first short circuit (in a typical electrical circuit) when exposed to the combustion products from a graphite fiber composite fire. The state-of-the-art and treated fibers cast in typical epoxy were burned and ranked for potential success. It was inferred that the gasification schemes appear promising when reduction or oxidation is tried. It was also found that some very promising candidates were available for the clumping and for the electrical insulation of fibers.

Strength advantages of chemically polished boron fibers before and after reaction with aluminum

NASA Technical Reports Server (NTRS)

Dicarlo, J. A.; Smith, R. J.

1982-01-01

In order to determine their strength potential, the fracture properties of different types of commercial boron fibers were measured before and after application of secondary strengthening treatments. The principal treatments employed were a slight chemical polish, which removed low strength surface flaws, and a heat treatment in oxygen, which contracted the fibers and thereby compressed intrinsic bulk flaws. Those fiber types most significantly strengthened were 200 to 400 micrometers (8 to 16 mil) diameter boron on tungsten fibers produced in a single chemical vapor deposition reactor. The slight polish increased average tensile strenghts from 3.4 to 4.4 CN/m2 (500 to 640 ksi) and reduced coefficients of variation from about 15 to 3 percent. The oxygen heat treatment plus slight polish further improved average strengths to 5.5 GN/m2 (800 ksi) with coefficients near 3 percent. To ascertain whether these excellent properties could be retained after fabrication of B/Al composites, as produced and polished 203 micrometers (8 mil) fibers were thinly coated with aluminum, heat treated at B/Al fabrication temperatures, and then tested in tension and flexure at room temperature. The pre-polished fibers were observed to retain their superior strengths to higher temperatures than the as-produced fibers even though both were subjected to the same detrimental reaction with aluminum.

Interfacial adhesion of carbon fibers

NASA Technical Reports Server (NTRS)

Bascom, Willard D.

1987-01-01

Relative adhesion strengths between AS4, AS1, and XAS carbon fibers and thermoplastic polymers were determined using the embedded single filament test. Polymers studied included polycarbonate, polyphenylene oxide, polyetherimide, polysulfone, polyphenylene oxide blends with polystyrene, and polycarbonate blends with a polycarbonate polysiloxane block copolymer. Fiber surface treatments and sizings improved adhesion somewhat, but adhesion remained well below levels obtained with epoxy matrices. An explanation for the differences between the Hercules and Grafil fibers was sought using X ray photon spectroscopy, wetting, scanning electron microscopy and thermal desorption analysis.

Effects of HF Treatments on Tensile Strength of Hi-Nicalon Fibers

NASA Technical Reports Server (NTRS)

Bansal, Narottam P.

1998-01-01

Tensile strengths of as-received Hi-Nicalon fibers and those having a dual BN/SiC surface coating, deposited by chemical vapor deposition, have been measured at room temperature. These fibers were also treated with HF for 24 h followed by tensile strength measurements. Strengths of uncoated and BN/SiC coated Hi-Nicalon fibers extracted from celsian matrix composites, by dissolving away the matrix in HF for 24 h, were also determined. The average tensile strength of uncoated Hi-Nicalon was 3.19 +/- 0.73 GPa with a Weibull modulus of 5.41. The Hi-Nicalon/BN/SiC fibers showed an average strength of 3.04 q 0.53 GPa and Weibull modulus of 6.66. After HF treatments, the average strengths of the uncoated and BN/SiC coated Hi-Nicalon fibers were 2.69 +/- 0.67 GPa and 2.80 +/- 0.53 GPa and the Weibull moduli were 4.93 and 5.96, respectively. The BN/SiC coated fibers extracted from the celsian matrix composite exhibited a strength of 2.38 +/- 0.40 GPa and a Weibull modulus of 7.15. The strength of the uncoated Hi-Nicalon fibers in the composite was so severely degraded that they disintegrated into small fragments during extraction with HF. The uncoated fibers probably undergo mechanical surface damage during hot pressing of the composites. Also, the BN layer on the coated fibers acts as a compliant layer which protects the fibers from mechanical damage during composite processing. The elemental composition and thickness of the fiber coatings were deten-nined using scanning Auger analysis. Microstructural analyses of the fibers and the coatings were done by scanning electron microscopy and transmission electron microscopy. Strengths of fibers calculated using average and measured fiber diameters were in good agreement. Thus, the strength of fibers can be evaluated using an average fiber diameter instead of the measured diameter of each filament.

Laccase/HBT and laccase-CBM/HBT treatment of softwood kraft pulp: impact on pulp bleachability and physical properties.

PubMed

Ravalason, Holy; Bertaud, Frédérique; Herpoël-Gimbert, Isabelle; Meyer, Valérie; Ruel, Katia; Joseleau, Jean-Paul; Grisel, Sacha; Olivé, Caroline; Sigoillot, Jean-Claude; Petit-Conil, Michel

2012-10-01

Pycnoporus cinnabarinus laccase and a chimeric laccase-CBM were applied in softwood kraft pulp biobleaching in the presence of 1-hydroxybenzotriazole (HBT). The presence of CBM could enhance the laccase biobleaching potential as a decrease in the enzymatic charge and chlorine dioxide consumption, as well as an increase in pulp brightness were observed. Laccase/HBT treatment could be improved by increasing oxygen pressure from 1 to 3bar and pulp consistency from 5% to 10%. Conversely, under the same conditions, no improvement of laccase-CBM/HBT treatment was observed, indicating a different behavior of both systems. However, laccase-CBM/HBT treatment led to a better preservation of pulp properties. This effect was probably due to fiber surface modifications involving the action of the CBM. Transmission electron microscopy examination of pulp fibers indicated a retention of laccase-CBM inside the pulp fibers due to CBM binding and an increased external microfibrillation of the fibers due to enzymatic treatments. Copyright © 2012 Elsevier Ltd. All rights reserved.

A Novel Method for Depositing Precious Metal Films on Difficult Surfaces

NASA Technical Reports Server (NTRS)

Veitch, L. C.; Phillip, W. H.

1994-01-01

A guanidine-based vehicle was developed to deposit precious metal coatings on surfaces known to be difficult to coat. To demonstrate this method, a platinum coating was deposited on alumina fibers using a guanidine-platinum solution. X-ray diffraction confirmed that the only species present in the coating was platinum and that all of the carbon species had been removed upon heat treatment. SEM results showed that some porosity was present but that the coatings uniformly covered the fiber surface and adhered well to the finer.

Evaluation of ionic liquid treated sisal (agave sisalana) fiber as sorbent in biodiesel spill

NASA Astrophysics Data System (ADS)

Costa, E.; Silva, A.; Mattedi, S.

2018-04-01

The global economic development continually demands the use of energy resources, among which various types of oils are widely used. Despite their undeniable economic importance, environmental accidents with these occur frequently. Thus, the search for efficient and low-cost mitigating measures is recurrent. In this context, techniques that use natural adsorbents, such as vegetable fibers, have been studied, since they combine efficiency, selectivity, low cost and sustainability. Studies have been carried out using various types of fibers, natural or chemically treated. The interest in treating the fiber lies in the fact that, changing the chemical structure of the fiber, its oil sorption capacity is increased. Due to the offered advantages, an alternative and promising type of surface treatment using ionic liquids was performed, to the detriment of traditional treatments. Thus, the technical feasibility of the use of sisal fiber treated with ionic liquid for adsorption of biodiesel was studied.

Hydrogen bonds, interfacial stiffness moduli, and the interlaminar shear strength of carbon fiber-epoxy matrix composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Cantrell, John H., E-mail: john.h.cantrell@nasa.gov

2015-03-15

The chemical treatment of carbon fibers used in carbon fiber-epoxy matrix composites greatly affects the fraction of hydrogen bonds (H-bonds) formed at the fiber-matrix interface. The H-bonds are major contributors to the fiber-matrix interfacial shear strength and play a direct role in the interlaminar shear strength (ILSS) of the composite. The H-bond contributions τ to the ILSS and magnitudes K{sub N} of the fiber-matrix interfacial stiffness moduli of seven carbon fiber-epoxy matrix composites, subjected to different fiber surface treatments, are calculated from the Morse potential for the interactions of hydroxyl and carboxyl acid groups formed on the carbon fiber surfacesmore » with epoxy receptors. The τ calculations range from 7.7 MPa to 18.4 MPa in magnitude, depending on fiber treatment. The K{sub N} calculations fall in the range (2.01 – 4.67) ×10{sup 17} N m{sup −3}. The average ratio K{sub N}/|τ| is calculated to be (2.59 ± 0.043) × 10{sup 10} m{sup −1} for the seven composites, suggesting a nearly linear connection between ILSS and H-bonding at the fiber-matrix interfaces. The linear connection indicates that τ may be assessable nondestructively from measurements of K{sub N} via a technique such as angle beam ultrasonic spectroscopy.« less

Fiber post etching with hydrogen peroxide: effect of concentration and application time.

PubMed

de Sousa Menezes, Murilo; Queiroz, Ellyne Cavalcanti; Soares, Paulo Vinícius; Faria-e-Silva, André Luis; Soares, Carlos José; Martins, Luis Roberto Marcondes

2011-03-01

Etching is necessary to expose the fibers and enable both mechanical and chemical bonding of the resin core to the fiber post. This study evaluated the effect of concentration and application time of hydrogen peroxide on the surface topography and bond strength of glass fiber posts to resin cores. Fiber posts were etched with 24% or 50% hydrogen peroxide for 1, 5, or 10 min (n = 10). Posts without any treatment were used as a control. After etching, the posts were silanated and adhesive resin was applied. The posts were positioned into a mold to allow a self-cured resin core to be inserted. The post/resin assembly was serially sectioned into five beams that were subjected to a tensile bond strength test. Data were subjected to two-way ANOVA and Tukey test (α = 0.05). The surface topography was analyzed using scanning electronic microscopy. Non-etched post presents a relatively smooth surface without fiber exposure. Application of hydrogen peroxide increased the surface roughness and exposed the fibers. All experimental conditions yielded similar bond strength values that were higher than those obtained in the control group. Both 24% and 50% hydrogen peroxide exposure increased the bond strength of resin to the posts, irrespective of the application time. Copyright © 2011 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

Comparison of analytical protein separation characteristics for three amine-based capillary-channeled polymer (C-CP) stationary phases.

PubMed

Jiang, Liuwei; Marcus, R Kenneth

2016-02-01

Capillary-channeled polymer (C-CP) fiber stationary phases are finding utility in the realms of protein analytics as well as downstream processing. We have recently described the modification of poly(ethylene terephthalate) (PET) C-CP fibers to affect amine-rich phases for the weak anion-exchange (WAX) separation of proteins. Polyethylenimine (PEI) is covalently coupled to the PET surface, with subsequent cross-linking imparted by treatment with 1,4-butanediol diglycidyl ether (BUDGE). These modifications yield vastly improved dynamic binding capacities over the unmodified fibers. We have also previously employed native (unmodified) nylon 6 C-CP fibers as weak anion/cation-exchange (mixed-mode) and hydrophobic interaction chromatography (HIC) phases for protein separations. Polyamide, nylon 6, consists of amide groups along the polymer backbone, with primary amines and carboxylic acid end groups. The analytical separation characteristics of these three amine-based C-CP fiber phases are compared here. Each of the C-CP fiber columns in this study was shown to be able to separate a bovine serum albumin/hemoglobin/lysozyme mixture at high mobile phase linear velocity (∼70 mm s(-1)) but with different elution characteristics. These differences reflect the types of protein-surface interactions that are occurring, based on the active group composition of the fiber surfaces. This study provides important fundamental understanding for the development of surface-modified C-CP fiber columns for protein separation.

Use of green chemistry methods in the extraction of dietary fibers from cactus rackets (Opuntia ficus indica): Structural and microstructural studies.

PubMed

Cheikh Rouhou, Marwa; Abdelmoumen, Souhir; Thomas, Sabu; Attia, Hamadi; Ghorbel, Dorra

2018-05-23

This work aims to compare the development of three green chemistry methods in the extraction of cactus (Opuntia ficus indica) dietary fibers. The influence of extraction conditions (solvent nature: water, lemon juice and ethanol; extraction process: maceration and steam explosion; extraction time: 30 min, 1 h, 3 h, 5 h) on the chemical and structural composition was studied. Fourier Transform Infrared (FTIR) spectroscopy proved that all treatments do not affect the cellulose structure and could induce the reduction of hemicelluloses and lignin content. The steam treatment with lemon juice was the best treatment in term of quality of the fibers extracted. Through X-ray Diffraction (XRD) analysis, it was demonstrated that this treatment contributed to the destruction of the amorphous phase with preservation of the crystalline phase. Scanning electron microscopy (SEM) showed that the microstructure of the sample surface was uniform and contains arranged fibers. Atomic Force Microscopy (AFM) revealed fibers with 80 nm of diameter. Copyright © 2018. Published by Elsevier B.V.

Transverse flexural tests as a tool for assessing damage to PMR-15 composites from isothermal aging in air at elevated temperatures

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.

1992-01-01

To date, the effect of thermo-oxidative aging on unidirectional composite mechanical properties has been monitored by the measurement of interlaminar shear strength (ILSS) and either three or four point longitudinal flexural strength (LFS) of the composites being tested. Both results are affected by the fiber-to-matrix bonding, the former being dependent on the shear resistance of the interface and the latter on the degree of load sharing by the fibers through the fiber/matrix interface. Recently, fiber/matrix interfacial bond strengths have been monitored using a transverse flexural strength (TFS) test method. This test method was used to evaluate the effect of fiber surface treatment on the fiber/matrix bond. The interface bonding was varied in these tests using Hercules A-fibers with three-types of surfaces that produce bonds of poor, better, and good quality. The TFS was found not only to be sensitive to the bonding, but also to the aging time of unidirectional A-fiber/PMR-15 composites. This relationship reflects the mechanism by which the PMR-15 degrades during thermal aging.

Corrosion Inhibition of Cold-rolled Low Carbon Steel with Pulse Fiber Laser Ablation in Water

NASA Astrophysics Data System (ADS)

Chan, Sze Ney; Wong, Wai Yin; Walvekar, Rashmi; Kadhum, Abdul Amir H.; Khalid, Mohammad; Lim, Kean Long

2018-04-01

This study aims at the use of a fiber laser for modifying the surface properties of cold-rolled low carbon steel via a pulse laser ablation technique in water. The effect on the corrosion behavior of the fiber laser-treated metal surface was investigated in NaCl and HCl environments. Electrochemical tests showed significant improvement in the corrosion resistance of the laser-treated sample in NaCl, with an increase in open-circuit potential (OCP) from - 0.65 to - 0.60 V and an inhibition efficiency of 89.22% as obtained from the impedance study. Such improvement was less significant in an acidic environment. Lower corrosion rates of 20.9 mpy and 5.819 × 103 mpy were obtained for the laser-treated samples in neutral and acidic electrolytes, respectively, than the corrosion rates obtained for the as-received samples (33.2 mpy and 11.98 × 103 mpy). Morphological analysis indicated a passive film built by spherical grains of regular size on the metal surface after laser treatment. The corrosion inhibition effects in NaCl were evident by the nonexistence of the common corrosion products of lepidocrocite and crystalline structures that were seen on as-received samples; only polyhedral crystals with micrograins grown on them were seen covering the laser-treated surface. Therefore, the laser treatment using a fiber laser source improved the corrosion resistance of cold-rolled low carbon steel.

The effects of corn zein protein coupling agent on mechanical properties of flax fiber reinforced composites

NASA Astrophysics Data System (ADS)

Whitacre, Ryan John

In the field of renewable materials, natural fiber composites demonstrate the capacity to be a viable structural material. When normalized by density, flax fiber mechanical properties are competitive with E-glass fibers. However, the hydrophilic nature of flax fibers reduces the interfacial bond strength with polymer thermosets, limiting composite mechanical properties. Corn zein protein was selected as a natural bio-based coupling agent because of its combination of hydrophobic and hydrophilic properties. Zein was deposited on the surface of flax, which was then processed into unidirectional composite. The mechanical properties of zein treated samples where measured and compared against commonly utilized synthetic treatments sodium hydroxide and silane which incorporate harsh chemicals. Fourier transform infrared spectroscopy, chemical analysis, and scanning electron microscopy were also used to determine analyze zein treatments. Results demonstrate the environmentally friendly zein treatment successfully increased tensile strength 8%, flexural strength 17%, and shear strength 30% compared to untreated samples.

Surface modification of polyester fabrics by atmospheric-pressure air/He plasma for color strength and adhesion enhancement

NASA Astrophysics Data System (ADS)

Zhang, Chunming; Zhao, Meihua; Wang, Libing; Qu, Lijun; Men, Yajing

2017-04-01

Surface properties of water-based pigmented inks for ink-jet printed polyester fabrics were modified with atmospheric-pressure air/He plasma to improve the color strength and pigment adhesion of the treated surfaces. The influence of various parameters, including the surface morphology, chemical compositions, surface energy and dynamic contact angles of the control and plasma treated samples was studied. Color strength and edge definition were used to evaluate the ink-jet printing performance of fabrics. The change in pigment adhesion to polyester fibers was analyzed by SEM (scanning electron microscopy). AFM (Atomic force microscope) and XPS (X-ray photoelectron spectroscopy) analyses indicated the increase in surface roughness and the oxygen-containing polar groups(Cdbnd O, Csbnd OH and COOH) reinforced the fixation of pigments on the fiber surface. The result from this study suggested that the improved pigment color yield was clearly affected by alteration of pigment adhesion enhanced by plasma surface modification. Polyester fabrics exhibited better surface property and ink-jet printing performance after the air/He mixture plasma treatment comparing with those after air plasma treatment.

The effect of modified ijuk fibers to crystallinity of polypropylene composite

NASA Astrophysics Data System (ADS)

Prabowo, I.; Nur Pratama, J.; Chalid, M.

2017-07-01

Nowadays, plastics becomes concern associated with its degradation and environmental issues. It has led studies to develop an environmental-friendly material. To minimize the impact of those problems, recently the usage of natural fibers as a filler are introduced because of biodegradability and availability. The promising natural fiber is “ijuk” fiber from Arenga pinnata plant as a filler and polypropylene (PP) polymer as a matrix. Unfortunately, the natural fibers and polymers have the different properties on which polymers are polar while natural fibers are non-polar so that reducing the compatibility and resulting the poor crystallinity. To enhance the compatibility and crystallinity, ijuk fibers were prepared by multistage treatments including alkalinization with 5 and 10% sodium hydroxide (NaOH), oxidation with 3 and 6% sodium hypochlorite (NaClO) and hydrolysis with 20% sulphuric acid (H2SO4) in sequences. The purposes of multistage treatments are to remove the components such as lignin, wax, hemicellulose, to cause an oxidative fragmentation of remaining lignin and to annihilate the amorphous parts respectively. Fourier-Transform Infrared (FTIR) confirms the compatibility meanwhile Differential Scanning Calorimetry (DSC) reveals the crystallinity and Scanning Electron Microscope (SEM) displays surface morphology of polypropylene. The experiments were revealing that the effects of “ijuk” fibers by the multistage treatments of 5 and 10% NaOH resulting the crystallinity of polypropylene around 31.2 and 27.64% respectively compared to the crystallinity before adding the “ijuk” fibers for 16.8%. It indicates that the entire treatments increasing the compatibility and crystallinity of polypropylene. In addition, the use of 5% NaOH offers the better crystallinity than non-treated polypropylene. The experiments conclude that by adding alkalinized “ijuk” fibers of multistage treatments can increase the compatibility and crystallinity of polypropylene.

Optimization of ultrasonic-assisted preparation of dietary fiber from corn pericarp using response surface methodology.

PubMed

Wang, Anna; Wu, Ligen; Li, Xiulin

2013-09-01

Corn pericarp, which is an industrial waste of corn starch production, is an important source of dietary fiber in cereals, with claimed health benefits. However, they used to be discarded or utilized as animal feed. The application of pre-ultrasound treatment is critical for achieving rapid preparation of desired components from plant materials and for preserving structural and molecular properties of these compounds. Ultrasonic-assisted preparation was used to produce dietary fiber from corn pericarp using response surface methodology. The optimal particle size of corn pericarp (mesh size 40), the ratio of liquid to solid (25 mL g⁻¹), ultrasonic power (180 W) and ultrasonic time (80 min) were determined based on response surface methodology analysis. The interaction effects of particle size of corn pericarp and ultrasonic time had a highlysignificant effect on the yield of dietary fiber, and a significant effect was shown by ultrasonic power and ultrasonic time. The maximum yield of dietary fiber was 86.84%, which agreed closely with the predicted value. Using ultrasonic-assisted preparation, it may be possible to enhance the yield of dietary fiber from corn pericarp. © 2013 Society of Chemical Industry.

Adhesion of nitrile rubber to UV-assisted surface chemical modified PET fabric, part II: Interfacial characterization of MDI grafted PET

NASA Astrophysics Data System (ADS)

Razavizadeh, Mahmoud; Jamshidi, Masoud

2016-08-01

Fiber to rubber adhesion is an important subject in rubber industry. It is well known that surface treatment (i.e. physical, mechanical and chemical) is an effective method to improve interfacial bonding of fibers and/or fabrics to rubbers. UV irradiation is an effective method which has been used to increase fabric-rubber interfacial interactions. In this research UV assisted chemical modification of PET fabrics was used to increase PET to nitrile rubber (NBR) adhesion. Nitrile rubber is a perfect selection as fuel and oil resistant rubber. However it has weak bonding to PET fabric. For this purpose PET fabric was carboxylated under UV irradiation and then methylenediphenyl diisocyanate (MDI) was grafted on carboxylated PET. The chemical composition of the fabric before and after surface treatment was investigated by X-ray photoelectron spectroscopy (XPS). The sectional morphology of the experimental PET fibers and the interface between rubber compound and PET fabric was studied using scanning electron microscope (SEM). The morphology and structure of the product were analyzed by an energy dispersive X-ray spectrometer (EDX). FTIR-ATR and H NMR analysis were used to assess surface modifications on the PET irradiated fabrics.

High temperature heat source generation with a very low power level quasi-cw(continuous wave) semiconductor laser for medical use

NASA Astrophysics Data System (ADS)

Fujimoto, Takahiro; Imai, Yusuke; Tei, Kazuyoku; Fujioka, Tomoo; Yamaguchi, Shigeru

2013-03-01

In most of medical and dental laser treatments, high power pulsed laser have been used as desirable light sources employing with an optical fiber delivery system. The treatment process involves high temperature thermal effect associated with direct laser absorption of the materials such as hard and soft tissues, tooth, bones and so on. Such treatments sometimes face technical difficulties suffering from their optical absorption properties. We investigate a new technology to create high temperature heat source on the tip surface of the glass fiber proposed for the medical surgery applications. Using a low power level (4 6W) semiconductor laser at a wavelength of 980nm, a laser coupled fiber tip was pre-processed to contain certain amount of TiO2 powder with a depth of 400μm from the tip surface so that the irradiated low laser energy could be perfectly absorbed to be transferred to thermal energy. Thus the laser treatment can be performed without suffering from any optical characteristic of the material. Semiconductor laser was operated quasi-CW mode pulse time duration of 180ms and more than 95% of the laser energy was converted to thermal energy in the fiber tip. by Based on twocolor thermometry by using a gated optical multichannel analyzer with 0.25m spectrometer in visible wavelength region, the temperature of the fiber tip was analyzed. The temperature of the heat source was measured to be approximately 3000K. Demonstration of laser processing employing this system was successfully carried out drilling through holes in ceramic materials simulating bone surgery.

The structure and mechanical properties of AlMg5Si2Mn alloy after surface alloying by the use of fiber laser

NASA Astrophysics Data System (ADS)

Pakieła, Wojciech; Tanski, Tomasz; Pawlyta, Mirosława; Pakieła, Katarzyna; Brytan, Zbigniew; Sroka, Marek

2018-03-01

Laser surface treatment is successfully applied to increase hardness as well as corrosion and wear resistance in light alloys such as aluminum or magnesium. The laser surface remelting also can be used to repair superficial cracks, voids or porosity caused by the mechanical impact, metallurgical process as well as the corrosive environment on the surface of the aluminum alloy. The purpose of this paper was to investigate the influence of a fiber laser surface treatment on the structure and properties of the EN AC AlMg5Si2Mn alloy. The goal of this investigation was to increase the hardness and improve tribological properties of the aluminum alloy surface as a result of the conducted laser surface treatment. During laser processing, the top surface of the aluminum alloy was enriched with Cr and Ni particles. The grain size of the applied particles was approximately about 60-130 m. The Cr-Ni powder has been introduced in the molten pool using vacuum feeder at a constant rate of 4.5 g/min. For surface remelting we used square laser beam at a size 3 × 3 mm and with the power of 3.0 kW. The linear laser scan rate of the beam was set at 0.5 m/min. Argon was used to protect the liquid metal alloy during surface treatment. Application of the laser treatment on aluminum alloy has enabled to obtain much harder as well as better wear resistant material compared to the untreated EN AC AlMg5Si2Mn.

Experimental removal of subgingival calculus with the Er:YAG laser

NASA Astrophysics Data System (ADS)

Keller, Ulrich; Hibst, Raimund

1996-01-01

The purpose of this study was to evaluate the effects of the Er:YAG laser removal of subgingival calculi in periodontal treatment and to describe laser-induced cementum surface alterations. Freshly extracted human teeth with adherent plaques and mineralized calculi were laser treated using modified quartz fiber tips in direct contact to the root surface. For the fiber tip tested, the ablation threshold was 6.5 mJ. An effective removal of calculi was possible with 50 mJ resp. 150 mJ for a triple fiber. For the latter, a mass loss with a mean of about 5.1. mg/min was achieved. Histologic examinations of the cementum surface showed smoothed appearance alternately with rough depressions of the fiber tips, which can be discussed as a good precondition for periodontal tissue regeneration. Maximum temperature increase of 1.4 K was reached in the pulp, if an additional water irrigation was applied to the root surface. From these results it can be concluded that with the Er:YAG laser an effective removal of subgingival calculi can be performed without thermal risk for the pulp.

Pre-treatment of multi-walled carbon nanotubes for polyetherimide mixed matrix hollow fiber membranes.

PubMed

Goh, P S; Ng, B C; Ismail, A F; Aziz, M; Hayashi, Y

2012-11-15

Mixed matrix hollow fibers composed of multi-walled carbon nanotubes (MWCNTs) and polyetherimide (PEI) were fabricated. Pre-treatment of MWCNTs was carried out prior to the incorporation into the polymer matrix using a simple and feasible two stages approach that involved dry air oxidation and surfactant dispersion. The characterizations of the surface treated MWCNTs using TEM and Raman spectroscopy have evidenced the effectiveness of dry air oxidation in eliminating undesired amorphous carbon and metal catalyst while surfactant dispersion using Triton X100 has suppressed the agglomeration of MWCNTs. The resultant mixed matrix hollow fibers were applied for O(2)/N(2) pure gas separation. Interestingly, it was found that removal of disordered amorphous carbons and metal particles has allowed the hollow structures to be more accessible for the fast and smooth transport of gas molecules, hence resulted in noticeable improvement in the gas separation properties. The composite hollow fibers embedded with the surface modified MWCNTs showed increase in permeability as much as 60% while maintaining the selectivity of the O(2)/N(2) gas pair. This study highlights the necessity to establish an appropriate pre-treatment approach for MWCNTs in order to fully utilize the beneficial transport properties of this material in mixed matrix polymer nanocomposite for gas separation. Copyright © 2012 Elsevier Inc. All rights reserved.

Click chemistry modification of natural keratin fibers for sustained shrink-resist performance.

PubMed

Yu, Dan; Cai, Jackie Y; Church, Jeffrey S; Wang, Lijing

2015-01-01

This paper introduces a novel chemical treatment for achieving sustained shrink-resist performance on natural keratin fibers. The new treatment involves the controlled reduction of keratin in the cuticle region of the fiber, and the application of a water soluble diacrylate, namely glycerol 1,3-diglycerolate diacrylate (GDA), on the reduced keratin substrate. The acrylate groups of the GDA react with cysteine residues in the reduced keratin through thiol-ene click reactions at room temperature, leading to GDA grafting and the formation of GDA crosslinks in the keratin structure. The modified substrates were characterized by infrared spectroscopy and scanning electron microscopy, and assessed for its shrink-resistance and wet burst strength. This chemical modification has shown to alter the fiber surface morphology and hydrophilicity, resulting in substantially improved shrink-resistance with good fiber strength retention. Possible shrink-resistance mechanisms were also discussed. Crown Copyright © 2015. Published by Elsevier B.V. All rights reserved.

Effect of Plasma Treatment on Air and Water-Vapor Permeability of Bamboo Knitted Fabric

NASA Astrophysics Data System (ADS)

Prakash, C.; Ramakrishnan, G.; Chinnadurai, S.; Vignesh, S.; Senthilkumar, M.

2013-11-01

In this paper, the effects of oxygen and atmospheric plasma on air and water-vapor permeability properties of single jersey bamboo fabric have been investigated. The changes in these properties are believed to be related closely to the inter-fiber and inter-yarn friction force induced by the plasma treatments. The outcomes showed that the water-vapor permeability increased, although the air permeability decreased along with the plasma treatments. The SEM images clearly showed that the plasma modified the fiber surface outwardly. The results showed that the atmospheric plasma has an etching effect and increases the functionality of a bamboo surface, which is evident from SEM and FTIR-ATR analysis. These results reveal that atmospheric pressure plasma treatment is an effective method to improve the performance of bamboo fabric. Statistical analysis also indicates that the results are significant for air permeability and water-vapor permeability of the plasma-treated bamboo fabric.

Development of Al2O3 electrospun fibers prepared by conventional sintering method or plasma assisted surface calcination

NASA Astrophysics Data System (ADS)

Mudra, E.; Streckova, M.; Pavlinak, D.; Medvecka, V.; Kovacik, D.; Kovalcikova, A.; Zubko, P.; Girman, V.; Dankova, Z.; Koval, V.; Duzsa, J.

2017-09-01

In this paper, the electrospinning method was used for preparation of α-Al2O3 microfibers from PAN/Al(NO3)3 precursor solution. The precursor fibers were thermally treated by conventional method in furnace or low-temperature plasma induced surface sintering method in ambient air. The four different temperatures of PAN/Al(NO3)3 precursors were chosen for formation of α-Al2O3 phase by conventional sintering way according to the transition features observed in the TG/DSC analysis. In comparison, the low-temperature plasma treatment at atmospheric pressure was used as an alternative sintering method at the exposure times of 5, 10 and 30 min. FTIR analysis was used for evaluation of residual polymer after plasma induced calcination and for studying the mechanism of polymer degradation. The polycrystalline alumina fibers arranged with the nanoparticles was created continuously throughout the whole volume of the sample. On the other side the low temperature approach, high density of reactive species and high power density of plasma generated at atmospheric pressure by used plasma source allowed rapid removal of polymer in preference from the surface of fibers leading to the formation of composite ceramic/polymer fibers. This plasma induced sintering of PAN/Al(NO3)3 can have obvious importance in industrial applications where the ceramic character of surface with higher toughness of the fibers are required.

Compact light-emitting diode optical fiber immobilized TiO2 reactor for photocatalytic water treatment.

PubMed

O'Neal Tugaoen, Heather; Garcia-Segura, Sergi; Hristovski, Kiril; Westerhoff, Paul

2018-02-01

A key barrier to implementing photocatalysis is delivering light to photocatalysts that are in contact with aqueous pollutants. Slurry photocatalyst systems suffer from poor light penetration and require post-treatment to separate the catalyst. The alternative is to deposit photocatalysts on fixed films and deliver light onto the surface or the backside of the attached catalysts. In this study, TiO 2 -coated quartz optical fibers were coupled to light emitting diodes (OF/LED) to improve in situ light delivery. Design factors and mechanisms studied for OF/LEDs in a flow-through reactor included: (i) the influence of number of LED sources coupled to fibers and (ii) the use of multiple optical fibers bundled to a single LED. The light delivery mechanism from the optical fibers into the TiO 2 coatings is thoroughly discussed. To demonstrate influence of design variables, experiments were conducted in the reactor using the chlorinated pollutant para-chlorobenzoic acid (pCBA). From the degradation kinetics of pCBA, the quantum efficiencies (Φ) of oxidation and electrical energies per order (E EO ) were determined. The use of TiO 2 coated optical fiber bundles reduced the energy requirements to deliver photons and increased available surface area, which improved Φ and enhanced oxidative pollutant removal performance (E EO ). Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of atmospheric oxidative plasma treatments on polypropylenic fibers surface: Characterization and reaction mechanisms

NASA Astrophysics Data System (ADS)

Nisticò, Roberto; Magnacca, Giuliana; Faga, Maria Giulia; Gautier, Giovanna; D'Angelo, Domenico; Ciancio, Emanuele; Lamberti, Roberta; Martorana, Selanna

2013-08-01

Atmospheric pressure plasma-dielectric barrier discharge (APP-DBD, open chamber configuration) was used to functionalize polypropylene (PP) fibers surface in order to generate oxidized-reactive groups such as hydroperoxides, alcohols and carbonyl species (i.e. ketones and others). Such a species increased the surface polarity, without causing material degradation. Three different types of plasma mixture (He, He/O2, He/O2/H2O) under three different values of applied power (750, 1050, 1400 W) were investigated. The formed plasma species (O2+, O single atom and OH radical) and their distribution were monitored via optical emission spectrometry (OES) measurements, and the plasma effects on PP surface species formation were followed by X-ray photoemission spectroscopy (XPS). Results allowed to better understand the reaction pathways between plasma phase and PP fibers. In fact, two reaction mechanisms were proposed, the first one concerning the plasma phase reactions and the second one involving material surface modifications.

Improvement of interfacial adhesion and nondestructive damage evaluation for plasma-treated PBO and Kevlar fibers/epoxy composites using micromechanical techniques and surface wettability.

PubMed

Park, Joung-Man; Kim, Dae-Sik; Kim, Sung-Ryong

2003-08-15

Comparison of interfacial properties and microfailure mechanisms of oxygen-plasma treated poly(p-phenylene-2,6-benzobisoxazole (PBO, Zylon) and poly(p-phenylene terephthalamide) (PPTA, Kevlar) fibers/epoxy composites were investigated using a micromechanical technique and nondestructive acoustic emission (AE). The interfacial shear strength (IFSS) and work of adhesion, Wa, of PBO or Kevlar fiber/epoxy composites increased with oxygen-plasma treatment, due to induced hydrogen and covalent bondings at their interface. Plasma-treated Kevlar fiber showed the maximum critical surface tension and polar term, whereas the untreated PBO fiber showed the minimum values. The work of adhesion and the polar term were proportional to the IFSS directly for both PBO and Kevlar fibers. The microfibril fracture pattern of two plasma-treated fibers appeared obviously. Unlike in slow cooling, in rapid cooling, case kink band and kicking in PBO fiber appeared, whereas buckling in the Kevlar fiber was observed mainly due to compressive and residual stresses. Based on the propagation of microfibril failure toward the core region, the number of AE events for plasma-treated PBO and Kevlar fibers increased significantly compared to the untreated case. The results of nondestructive AE were consistent with microfailure modes.

Self-healable interfaces based on thermo-reversible Diels-Alder reactions in carbon fiber reinforced composites.

PubMed

Zhang, W; Duchet, J; Gérard, J F

2014-09-15

Thermo-reversible Diels-Alder (DA) bonds formed between maleimide and furan groups have been used to generate an interphase between carbon fiber surface and an epoxy matrix leading to the ability of interfacial self-healing in carbon:epoxy composite materials. The maleimide groups were grafted on an untreated T700 carbon fiber from a three step surface treatment: (i) nitric acid oxidization, (ii) tetraethylenepentamine amination, and (iii) bismaleimide grafting. The furan groups were introduced in the reactive epoxy system from furfuryl glycidyl ether. The interface between untreated carbon fiber and epoxy matrix was considered as a reference. The interfacial shear strength (IFSS) was evaluated by single fiber micro-debonding test. The debonding force was shown to have a linear dependence with embedded length. The highest healing efficiency calculated from the debonding force was found to be about 82% more compared to the value for the reference interface. All the interphases designed with reversible DA bonds have a repeatable self-healing ability. As after the fourth healing, they can recover a relatively high healing efficiency (58% for the interphase formed by T700-BMI which is oxidized for 60 min during the first treatment step). Copyright © 2014 Elsevier Inc. All rights reserved.

Argon-oxygen atmospheric pressure plasma treatment on carbon fiber reinforced polymer for improved bonding

NASA Astrophysics Data System (ADS)

Chartosias, Marios

Acceptance of Carbon Fiber Reinforced Polymer (CFRP) structures requires a robust surface preparation method with improved process controls capable of ensuring high bond quality. Surface preparation in a production clean room environment prior to applying adhesive for bonding would minimize risk of contamination and reduce cost. Plasma treatment is a robust surface preparation process capable of being applied in a production clean room environment with process parameters that are easily controlled and documented. Repeatable and consistent processing is enabled through the development of a process parameter window utilizing techniques such as Design of Experiments (DOE) tailored to specific adhesive and substrate bonding applications. Insight from respective plasma treatment Original Equipment Manufacturers (OEMs) and screening tests determined critical process factors from non-factors and set the associated factor levels prior to execution of the DOE. Results from mode I Double Cantilever Beam (DCB) testing per ASTM D 5528 [1] standard and DOE statistical analysis software are used to produce a regression model and determine appropriate optimum settings for each factor.

Laboratory evaluation of airborne particulate control treatments for simulated aircraft crash recovery operations involving carbon fiber composite materials.

PubMed

Ferreri, Matthew; Slagley, Jeremy; Felker, Daniel

2015-01-01

This study compared four treatment protocols to reduce airborne composite fiber particulates during simulated aircraft crash recovery operations. Four different treatments were applied to determine effectiveness in reducing airborne composite fiber particulates as compared to a "no treatment" protocol. Both "gold standard" gravimetric methods and real-time instruments were used to describe mass per volume concentration, particle size distribution, and surface area. The treatment protocols were applying water, wetted water, wax, or aqueous film-forming foam (AFFF) to both burnt and intact tickets of aircraft composite skin panels. The tickets were then cut using a small high-speed rotary tool to simulate crash recovery operations. Aerosol test chamber. None. Airborne particulate control treatments. Measures included concentration units of milligrams per cubic meter of air, particle size distribution as described by both count median diameter and mass median diameter and geometric standard deviation of particles in micrometers, and surface area concentration in units of square micrometers per cubic centimeter. Finally, a Monte Carlo simulation was run on the particle size distribution results. Comparison was made via one-way analysis of variance. A significant difference (p < 0.0001) in idealized particle size distribution was found between the water and wetted water treatments as compared to the other treatments for burnt tickets. Emergency crash recovery operations should include a treatment of the debris with water or wetted water. The resulting increase in particle size will make respiratory protection more effective in protecting the response crews.

Laboratory evaluation of airborne particulate control treatments for simulated aircraft crash recovery operations involving carbon fiber composite materials.

PubMed

Ferreri, Matthew; Slagley, Jeremy; Felker, Daniel

2015-01-01

This study compared four treatment protocols to reduce airborne composite fiber particulates during simulated aircraft crash recovery operations. Four different treatments were applied to determine effectiveness in reducing airborne composite fiber particulates as compared to a "no treatment" protocol. Both "gold standard" gravimetric methods and real-time instruments were used to describe mass per volume concentration, particle size distribution, and surface area. The treatment protocols were applying water, wetted water, wax, or aqueous film-forming foam (AFFF) to both burnt and intact tickets of aircraft composite skin panels. The tickets were then cut using a small high-speed rotary tool to simulate crash recovery operations. Aerosol test chamber. None. Airborne particulate control treatments. Measures included concentration units of milligrams per cubic meter of air, particle size distribution as described by both count median diameter and mass median diameter and geometric standard deviation of particles in micrometers, and surface area concentration in units of square micrometers per cubic centimeter. Finally, a Monte Carlo simulation was run on the particle size distribution results. Comparison was made via one-way analysis of variance. A significant difference (p<0.0001) in idealized particle size distribution was found between the water and wetted water treatments as compared to the other treatments for burnt tickets. Emergency crash recovery operations should include a treatment of the debris with water or wetted water. The resulting increase in particle size will make respiratory protection more effective in protecting the response crews.

Laser Surface Preparation of Epoxy Composites for Secondary Bonding: Optimization of Ablation Depth

NASA Technical Reports Server (NTRS)

Palmieri, Frank L.; Hopkins, John; Wohl, Christopher J.; Lin, Yi; Connell, John W.; Belcher, Marcus A.; Blohowiak, Kay Y.

2015-01-01

Surface preparation has been identified as one of the most critical aspects of attaining predictable and reliable adhesive bonds. Energetic processes such as laser ablation or plasma treatment are amenable to automation and are easily monitored and adjusted for controlled surface preparation. A laser ablation process was developed to accurately remove a targeted depth of resin, approximately 0.1 to 20 micrometers, from a carbon fiber reinforced epoxy composite surface while simultaneously changing surface chemistry and creating micro-roughness. This work demonstrates the application of this process to prepare composite surfaces for bonding without exposing or damaging fibers on the surface. Composite panels were prepared in an autoclave and had a resin layer approximately 10 micrometers thick above the fiber reinforcement. These composite panels were laser surface treated using several conditions, fabricated into bonded panels and hygrothermally aged. Bond performance of aged, experimental specimens was compared with grit blast surface treated specimens using a modified double cantilever beam test that enabled accelerated saturation of the specimen with water. Comparison of bonded specimens will be used to determine how ablation depth may affect average fracture energies and failure modes.

Use of polypropylene fibers coated with nano-silica particles into a cementitious mortar

DOE Office of Scientific and Technical Information (OSTI.GOV)

Coppola, B., E-mail: bcoppola@unisa.it; Di Maio, L.; Scarfato, P.

Fiber reinforced cementitious composite (FRCC) materials have been widely used during last decades in order to overcome some of traditional cementitious materials issues: brittle behaviour, fire resistance, cover spalling, impact strength. For composite materials, fiber/matrix bond plays an important role because by increasing fiber/matrix interactions is possible to increase the behaviour of the entire material. In this study, in order to improve fiber to matrix adhesion, two chemical treatments of polypropylene fibers were investigated: alkaline hydrolysis and nano-silica sol-gel particles deposition. Treatmtents effect on fibers morphology and mechanical properties was investigated by scanning electron microscopy (SEM) and tensile tests. SEMmore » investigations report the presence of spherical nano-silica particles on fiber surface, in the case of sol-gel process, while alkaline hydrolysis leads to an increase of fibers roughness. Both treatments have negligible influence on fibers mechanical properties confirming the possibility of their use in a cementitious mortar. Pullout tests were carried out considering three embedded length of fibers in mortar samples (10, 20 and 30 mm, respectively) showing an increase of pullout energy for treated fibers. The influence on fiber reinforced mortar mechanical properties was investigated by three-point flexural tests on prismatic specimens considering two fibers length (15 and 30 mm) and two fibers volume fractions (0.50 and 1.00 %). A general increase of flexural strength over the reference mix was achieved and an overall better behaviour is recognizable for mortars containing treated fibers.« less

Novel laser contact probe for periodontal treatment

NASA Astrophysics Data System (ADS)

Watanabe, Hisashi; Kataoka, Kenzo; Ishikawa, Isao

2001-04-01

Application of the erbium: YAG laser to periodontal treatment has been attempted and preferable results have been reported for calculus removal, vaporization of granulation tissue, periodontal pocket sterilization and so on. However, it has been difficult to reach and treat some conditions involving complex root morphology and furcated rots with conventional probes. The new broom probe was designed and tested to overcome these obstacles. The probe was made of 20 super-fine optical fibers bound into a broom shape. The experiments were carried out to evaluate the destructive power of a single fiber and to examine the morphology of tissue destruction and the accessibility to a bifurcated root of a human tooth using the broom probe. The Er:YAG laser prototype was used. A flat specimen plate was made by cutting the root of a cow tooth and then attached to an electrically operated table and irradiated under various conditions. The specimens were examined with both an optical and scanning electron microscope. The irradiated surfaces were also examined with a roughness meter. An irradiation applied with a single fiber with an energy level of 1 to 1.5 mJ at its tip results in a destruction depth of 3 to 24 micrometers . The optimum conditions for the fibers of this probe was 1.0 mJ at 10 pps and a scanning speed of 100 mm/min. No part of the tooth surface remained un-irradiated after using the broom probe to cover the surface 5 times parallel to the tooth axis and then five times at a 30 degree angle to the previous irradiation at a power of 20 mJ at 10 pps. Also curved and irregular surface were destroyed to a maximum depth of 19 micrometers . In conclusion, these results suggest that the broom probe would be applicable for periodontal laser treatments even if the tooth surface has a complex and irregular shape.

Fracture toughness testing of polymer matrix composites

NASA Technical Reports Server (NTRS)

Grady, Joseph E.

1992-01-01

A review of the interlaminar fracture indicates that a standard specimen geometry is needed to obtain consistent fracture toughness measurements in polymer matrix composites. In general, the variability of measured toughness values increases as the toughness of the material increases. This variability could be caused by incorrect sizing of test specimens and/or inconsistent data reduction procedures. A standard data reduction procedure is therefore needed as well, particularly for the tougher materials. Little work has been reported on the effects of fiber orientation, fiber architecture, fiber surface treatment or interlaminar fracture toughness, and the mechanisms by which the fibers increase fracture toughness are not well understood. The little data that is available indicates that woven fiber reinforcement and fiber sizings can significantly increase interlaminar fracture toughness.

Picosecond Pulsed Laser Ablation for the Surface Preparation of Epoxy Composites

NASA Technical Reports Server (NTRS)

Palmieri, Frank; Ledesma, Rodolfo; Fulton, Tayler; Arthur, Alexandria; Eldridge, Keishara; Thibeault, Sheila; Lin, Yi; Wohl, Chris; Connell, John

2017-01-01

As part of a technical challenge under the Advanced Composites Program, methods for improving pre-bond process control for aerospace composite surface treatments and inspections, in conjunction with Federal Aviation Administration guidelines, are under investigation. The overall goal is to demonstrate high fidelity, rapid and reproducible surface treatment and surface characterization methods to reduce uncertainty associated with the bonding process. The desired outcomes are reliable bonded airframe structure, and reduced timeline to certification. In this work, laser ablation was conducted using a q-switched Nd:YVO4 laser capable of nominal pulse durations of 8 picoseconds (ps). Aerospace structural carbon fiber reinforced composites with an epoxy resin matrix were laser treated, characterized, processed into bonded assemblies and mechanically tested. The characterization of ablated surfaces were conducted using scanning electron microscopy (SEM), water contact angle (WCA) goniometry, micro laser induced breakdown spectroscopy (uLIBS), and electron spin resonance (ESR). The bond performance was assessed using a double cantilever beam (DCB) test with an epoxy adhesive. The surface characteristics and bond performance obtained from picosecond ablated carbon fiber reinforced plastics (CFRPs) are presented herein.

Effect of micronization on the physicochemical properties of insoluble dietary fiber from citrus (Citrus junos Sieb. ex Tanaka) pomace.

PubMed

Ye, Fayin; Tao, Bingbing; Liu, Jia; Zou, Yan; Zhao, Guohua

2016-04-01

The aim of this work was to study the effect of micronization (mechanical and jet grindings) on the physicochemical properties of the insoluble dietary fiber from citrus pomace in comparison with ordinary grinding. The results showed that micronization treatment effectively pulverized the IDF-CP powders to micron scale and significantly increased the soluble dietary fiber content (p < 0.05). Compared with mechanical grinding, jet grinding was more effective in size reduction and resulted in IDF-CP powders with narrower particle size distributions. Micronized IDF-CP powders had smaller particle size, smoother surface, higher fluidity, cation-exchange capacity, and metal cation binding capacity values, but lower water holding capacity, oil holding capacity, and swelling capacity values. These functional properties were significantly dependent on surface area and particle size (D0.5). The present study suggested that micronization treatments could modify functional properties of IDF-CP powders, which promotes their use in food applications. © The Author(s) 2015.

Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene

PubMed Central

Shepelev, Olga; Kenig, Samuel

2017-01-01

Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called “stacked” graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior. PMID:29046838

Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene.

PubMed

Naveh, Naum; Shepelev, Olga; Kenig, Samuel

2017-01-01

Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called "stacked" graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior.

Nonwoven production from agricultural okra wastes and investigation of their thermal conductivities

NASA Astrophysics Data System (ADS)

Duman, M. N.; Kocak, E. D.; Merdan, N.; Mistik, I.

2017-10-01

Nowadays bio-based composite materials have been used in rising amounts and demanded widely in industrial uses, as they provide cost reduction and weight loss in the end use products. Agricultural cellulose based wastes can be a good alternative to synthetic fibers and can be used in natural fiber reinforced composite production, as there is a huge (more than 40 million tons) potential for natural cellulose production from agricultural wastes. Okra is one of the most grown vegetables around the world with stems left on the fields after harvest. When the similarity of mechanical properties of okra fibers with traditional bast fibers (flax, kenaf, hemp) are considered, from an economical and an environmental point of view this research emphasizes the potential of agricultural biomass for natural fiber production. In this study, okra stem wastes used for natural cellulosic fiber production and treated with 10% NaOH at 60°C for 10, 20, 30 and 40 minutes. By alkali treatment, decrease in fiber diameter and weight, and increase in tensile strength and elongation % have been observed. Nonwoven production has been done from both the fibers with and without surface treatments. Thermal conductivity properties of both nonwovens have been investigated.

Measurement of contact-line dissipation in a nanometer-thin soap film

NASA Astrophysics Data System (ADS)

Guo, Shuo; Lee, Chun Huen; Sheng, Ping; Tong, Penger

2015-01-01

We report a direct measurement of the friction coefficient ξc of two fluctuating contact lines formed on a fiber surface when a long glass fiber intersects the two water-air interfaces of a thin soap film. The glass fiber of diameter d in the range of 0.4-4 μ m and length 100-300 μ m is glued onto the front end of a rectangular cantilever used for atomic force microscopy. As a sensitive mechanical resonator, the hanging fiber probe can accurately measure a minute change of its viscous damping caused by the soap film. By measuring the broadening of the resonant peak of the hanging fiber probe with varying viscosity η of the soap film and different surface treatments of the glass fiber, we confirm that the contact line dissipation obeys a universal scaling law, ξc=α π d η , where the coefficient α =1.1 ±0.3 is insensitive to the change of liquid-solid contact angle. The experimental result is in good agreement with the numerical result based on the phase field model under the generalized Navier boundary conditions.

Measurement of contact-line dissipation in a nanometer-thin soap film.

PubMed

Guo, Shuo; Lee, Chun Huen; Sheng, Ping; Tong, Penger

2015-01-01

We report a direct measurement of the friction coefficient ξ(c) of two fluctuating contact lines formed on a fiber surface when a long glass fiber intersects the two water-air interfaces of a thin soap film. The glass fiber of diameter d in the range of 0.4-4 μm and length 100-300 μm is glued onto the front end of a rectangular cantilever used for atomic force microscopy. As a sensitive mechanical resonator, the hanging fiber probe can accurately measure a minute change of its viscous damping caused by the soap film. By measuring the broadening of the resonant peak of the hanging fiber probe with varying viscosity η of the soap film and different surface treatments of the glass fiber, we confirm that the contact line dissipation obeys a universal scaling law, ξ(c)=απdη, where the coefficient α=1.1±0.3 is insensitive to the change of liquid-solid contact angle. The experimental result is in good agreement with the numerical result based on the phase field model under the generalized Navier boundary conditions.

Recycling polyethylene terephthalate wastes as short fibers in Strain-Hardening Cementitious Composites (SHCC).

PubMed

Lin, Xiuyi; Yu, Jing; Li, Hedong; Lam, Jeffery Y K; Shih, Kaimin; Sham, Ivan M L; Leung, Christopher K Y

2018-05-26

As an important portion of the total plastic waste bulk but lack of reuse and recycling, the enormous amounts of polyethylene terephthalate (PET) solid wastes have led to serious environmental issues. This study explores the feasibility of recycling PET solid wastes as short fibers in Strain-Hardening Cementitious Composites (SHCCs), which exhibit strain-hardening and multiple cracking under tension, and therefore have clear advantages over conventional concrete for many construction applications. Based on micromechanical modeling, fiber dispersion and alkali resistance, the size of recycled PET fibers was first determined. Then the hydrophobic PET surface was treated with NaOH solution followed by a silane coupling agent to achieve the dual purpose of improving the fiber/matrix interfacial frictional bond (from 0.64 MPa to 0.80 MPa) and enhancing the alkali resistance for applications in alkaline cementitious environment. With surface treatment, recycling PET wastes as fibers in SHCCs is a promising approach to significantly reduce the material cost of SHCCs while disposing hazardous PET wastes in construction industry. Copyright © 2018 Elsevier B.V. All rights reserved.

Assessment of the mechanical properties of sisal fiber-reinforced silty clay using triaxial shear tests.

PubMed

Wu, Yankai; Li, Yanbin; Niu, Bin

2014-01-01

Fiber reinforcement is widely used in construction engineering to improve the mechanical properties of soil because it increases the soil's strength and improves the soil's mechanical properties. However, the mechanical properties of fiber-reinforced soils remain controversial. The present study investigated the mechanical properties of silty clay reinforced with discrete, randomly distributed sisal fibers using triaxial shear tests. The sisal fibers were cut to different lengths, randomly mixed with silty clay in varying percentages, and compacted to the maximum dry density at the optimum moisture content. The results indicate that with a fiber length of 10 mm and content of 1.0%, sisal fiber-reinforced silty clay is 20% stronger than nonreinforced silty clay. The fiber-reinforced silty clay exhibited crack fracture and surface shear fracture failure modes, implying that sisal fiber is a good earth reinforcement material with potential applications in civil engineering, dam foundation, roadbed engineering, and ground treatment.

[Fiber reinforced composite posts: literature review].

PubMed

Frydman, G; Levatovsky, S; Pilo, R

2013-07-01

FRC (Fiber-reinforced composite) posts have been used since the beginning of the 90s with the introduction of carbon fiber posts. Fiber posts are widely used to restore endodontically treated teeth that have insufficient coronal tooth structure. Many in vitro and in vivo studies have shown the advantage of using FRC over prefabricated and cast metal post especially indicated in narrow root canals which are prone to vertically root fracture. The most frequent failure of FRC is debonding of a post at the resin cement/dentin interface. Bonding to dentin may be achieved by using etch-and-rinse and self-etch adhesives. The bond strength formed by self-adhesive cements is noticeably lower in comparison to the bond strength formed with resin cements applied in combination with etch-and-rinse adhesives. In an attempt to maximize resin bonding to fiber posts, several surface treatments have been suggested. Sandblasting with alumina particles results in an increased surface roughness and surface area without affecting the integrity of the post as long as it is applied by 50 microm alumina particles at 2.5 bars for maximally 5 seconds at a distance of 30 mm. The efficiency of post salinization is controversial and its contribution to the retention is of minor importance. Hydrofluoric acid has recently been proposed for etching glass fiber posts but this technique produced substantial damage to the glass fibers and affected the integrity of the post. Delayed cementation of fiber post (at least 24h post endodontic treatment) resulted in higher retentive strengths in comparison to immediate cementation and the best results were obtained when the luting agent was brought into the post space with lentulo spirals or specific syringes. The resin cement film thickness also influences the pullout strengths of fiber-reinforced posts .The highest bond strength values were obtained when the cement layer oversized the post spaces but not larger than 0.3 mm. The use of core build-up materials as post luting cements is not recommended. The use of FRC post, combined with proper adhesive cementation technique can give an excellent solution when restoring endodontically treated teeth that are prone to fracture.

Photocatalytic quartz fiber felts with carbon-connected TiO2 nanoparticles for capillarity-driven continuous-flow water treatment

NASA Astrophysics Data System (ADS)

Zhang, Xiaofei; Su, Xiaowen; Gao, Wenqiang; Wang, Fulei; Liu, Zhihe; Zhan, Jie; Liu, Baishan; Wang, Ruosong; Liu, Hong; Sang, Yuanhua

2018-06-01

Immobility of photocatalysts on substrates is a vital factor for the practical application of photocatalysis in polluted water/air treatment. In this study, TiO2 homogenously loaded quartz fiber felt was prepared by assembling of carboxyl-contained organic molecules functionalized TiO2 nanoparticles on the surface of amino group-modified quartz fiber by electrostatic adsorption between them and followed by an anneal process. The immobilization of TiO2 nanoparticles overcomes one main obstacle of the photocatalysts recycling in photocatalysis application. In addition, a plasma treatment endowed the hybrid photocatalyst a high hydrophilic property. Due to the homogeneous distribution of TiO2, charge carriers' separation by carbon, and full contact between water and the photocatalyst derived from the high hydrophilia, the TiO2/quartz fiber felt shows excellent photocatalytic performance. Based on the stable loading and the capillarity effect of the contacted fibers photocatalyst, a demo capillarity-driven continuous-flow water treatment photocatalysis reactor was designed and built up. The TiO2 nanoparticle/quartz fiber hybrid photocatalyst can disposal organic contaminants in actual industrial waste water from a dyeing factory in the continuous-flow reactor. The chemical oxygen demand (COD) of the industrial waste water was decreased from 104 to 45 mg/L, overcoming the problem of deep water treatment which is difficult to solve by other methods. This study provides a new photocatalyst and reaction mode for the continuous-flow photocatalysis application.

Transformation of the released asbestos, carbon fibers and carbon nanotubes from composite materials and the changes of their potential health impacts.

PubMed

Wang, Jing; Schlagenhauf, Lukas; Setyan, Ari

2017-02-20

Composite materials with fibrous reinforcement often provide superior mechanical, thermal, electrical and optical properties than the matrix. Asbestos, carbon fibers and carbon nanotubes (CNTs) have been widely used in composites with profound impacts not only on technology and economy but also on human health and environment. A large number of studies have been dedicated to the release of fibrous particles from composites. Here we focus on the transformation of the fibrous fillers after their release, especially the change of the properties essential for the health impacts. Asbestos fibers exist in a large number of products and the end-of-the-life treatment of asbestos-containing materials poses potential risks. Thermal treatment can transform asbestos to non-hazardous phase which provides opportunities of safe disposal of asbestos-containing materials by incineration, but challenges still exist. Carbon fibers with diameters in the range of 5-10 μm are not considered to be respirable, however, during the release process from composites, the carbon fibers may be split along the fiber axis, generating smaller and respirable fibers. CNTs may be exposed on the surface of the composites or released as free standing fibers, which have lengths shorter than the original ones. CNTs have high thermal stability and may be exposed after thermal treatment of the composites and still keep their structural integrity. Due to the transformation of the fibrous fillers during the release process, their toxicity may be significantly different from the virgin fibers, which should be taken into account in the risk assessment of fiber-containing composites.

Effect of Atmospheric Pressure Plasma Treatment on Surface Characteristics and Adhesive Bond Quality of Peel Ply Prepared Composites

NASA Astrophysics Data System (ADS)

Tracey, Ashley C.

The purpose of this research was to investigate if atmospheric pressure plasma treatment could modify peel ply prepared composite surfaces to create strong adhesive bonds. Two peel ply surface preparation composite systems previously shown to create weak bonds (low fracture energy and adhesion failure) that were potential candidates for plasma treatment were Toray T800/3900-2 carbon fiber reinforced polymer (CFRP) prepared with Precision Fabrics Group, Inc. (PFG) 52006 nylon peel ply and Hexcel T300/F155 CFRP prepared with PFG 60001 polyester peel ply. It was hypothesized that atmospheric pressure plasma treatment could functionalize and/or remove peel ply remnants left on the CFRP surfaces upon peel ply removal. Surface characterization measurements and double cantilever beam (DCB) testing were used to determine the effects of atmospheric pressure plasma treatment on surface characteristics and bond quality of peel ply prepared CFRP composites. Previous research showed that Toray T800/3900-2 carbon fiber reinforced epoxy composites prepared with PFG 52006 peel ply and bonded with Cytec MetlBond 1515-3M structural film adhesive failed in adhesion at low fracture energies when tested in the DCB configuration. Previous research also showed that DCB samples made of Hexcel T300/F155 carbon fiber reinforced epoxy composites prepared with PFG 60001 peel ply and bonded with Henkel Hysol EA 9696 structural film adhesive failed in adhesion at low fracture energies. Recent research suggested that plasma treatment could be able to activate these "un-bondable" surfaces and result in good adhesive bonds. Nylon peel ply prepared 177 °C cure and polyester peel ply prepared 127 °C cure CFRP laminates were treated with atmospheric pressure plasma after peel ply removal prior to bonding. Atmospheric pressure plasma treatment was capable of significantly increasing fracture energies and changing failure modes. For Toray T800/3900-2 laminates prepared with PFG 52006 and bonded with MetlBond 1515-3M, plasma treatment increased fracture energies from 460 J/m 2. Atmospheric pressure plasma treatment also increased fracture energies of Hexcel T300/F155 laminates prepared with PFG 60001 and bonded with EA 9696 from 1500 J/m2. It was demonstrated that atmospheric pressure plasma treatment was able to transform poor bonding surfaces into acceptable ones by reversing the negative effects of incorrect peel ply usage. To determine if the primary reason for adhesion was functionalization or removal, a number of experiments were performed. Surface characteristics of peel ply only and plasma treated samples were determined using contact angle (CA) measurements, FTIR spectroscopy, X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). CA was used to assess solid surface energy that was useful to determine wetting of the adhesive on the adherend, one requirement of adhesion. FTIR and XPS were used to analyze composite surface chemistry, including the identification of functional groups that were a product of atmospheric pressure plasma treatment, as well as contaminants that can inhibit adhesive bonding. SEM was used to capture surface morphology to identify peel ply remnants and whether these remnants were physically removed or modified due to plasma treatment. This research supported that atmospheric pressure plasma treatment resulted in adhesion primarily due to functionalization of peel ply remnants, though a removal mechanism was not disproven. It was also shown that surface energy exhibited potential for predicting adhesion. Lastly, this research indicated that plasma treatment is a robust surface preparation, as strong bonds were observed up to 30 days after treatment.

Thermal Stability of Hi-Nicalon SiC Fiber in Nitrogen and Silicon Environments

NASA Technical Reports Server (NTRS)

Bhatt, R. T.; Garg, A.

1995-01-01

The room temperature tensile strength of uncoated and two types of pyrolytic boron nitride coated (PBN and Si-rich PBN) Hi-Nicalon SiC fibers was determined after 1 to 400 hr heat treatments to 1800 C under N2 pressures of 0.1, 2, and 4 MPa, and under 0.1 Mpa argon and vacuum environments. In addition, strength stability of both uncoated and coated fibers embedded in silicon powder and exposed to 0.1 MPa N2 for 24 hrs at temperatures to 1400 C was investigated. The uncoated and both types of BN coated fibers exposed to N2 for 1 hr showed noticeable strength degradation above 1400 C and 1600 C, respectively. The strength degradation appeared independent of nitrogen pressure, time of heat treatment, and surface coatings. TEM microstructural analysis suggests that flaws created due to SiC grain growth are responsible for the strength degradation. In contact with silicon powder, the uncoated and both types of PBN coated fibers degrade rapidly above 1350 C.

Effect of heat treatment of wood on the morphology, surface roughness and penetration of simulated and human blood.

PubMed

Rekola, J; Lassila, L V J; Nganga, S; Ylä-Soininmäki, A; Fleming, G J P; Grenman, R; Aho, A J; Vallittu, P K

2014-01-01

Wood has been used as a model material for the development of novel fiber-reinforced composite bone substitute biomaterials. In previous studies heat treatment of wood was perceived to significantly increase the osteoconductivity of implanted wood material. The objective of this study was to examine some of the changing attributes of wood materials that may contribute to improved biological responses gained with heat treatment. Untreated and 140°C and 200°C heat-treated downy birch (Betula pubescens Ehrh.) were used as the wood materials. Surface roughness and the effect of pre-measurement grinding were measured with contact and non-contact profilometry. Liquid interaction was assessed with a dipping test using two manufactured liquids (simulated blood) as well as human blood. SEM was used to visualize possible heat treatment-induced changes in the hierarchical structure of wood. The surface roughness was observed to significantly decrease with heat treatment. Grinding methods had more influence on the surface contour and roughness than heat treatment. The penetration of the human blood in the 200°C heat-treated exceeded that in the untreated and 140°C heat-treated materials. SEM showed no significant change due to heat treatment in the dry-state morphology of the wood. The results of the liquid penetration test support previous findings in literature concerning the effects of heat treatment on the biological response to implanted wood. Heat-treatment has only a marginal effect on the surface contour of wood. The highly specialized liquid conveyance system of wood may serve as a biomimetic model for the further development of tailored fiber-composite materials.

Preparation of robust braid-reinforced poly(vinyl chloride) ultrafiltration hollow fiber membrane with antifouling surface and application to filtration of activated sludge solution.

PubMed

Zhou, Zhuang; Rajabzadeh, Saeid; Fang, Lifeng; Miyoshi, Taro; Kakihana, Yuriko; Matsuyama, Hideto

2017-08-01

Braid-reinforced hollow fiber membranes with high mechanical properties and considerable antifouling surface were prepared by blending poly(vinyl chloride) (PVC) with poly(vinyl chloride-co-poly(ethylene glycol) methyl ether methacrylate) (poly(VC-co-PEGMA)) copolymer via non-solvent induced phase separation (NIPS). The tensile strength of the braid-reinforced PVC hollow fiber membranes were significantly larger than those of previously reported various types of PVC hollow fiber membranes. The high interfacial bonding strength indicated the good compatibility between the coating materials and the surface of polyethylene terephthalate (PET)-braid. Owing to the surface segregation phenomena, the membrane surface PEGMA coverage increased upon increasing the poly(VC-co-PEGMA)/PVC blending ratio, resulting in higher hydrophilicities and bovine serum albumin (BSA) repulsion. To compare the fouling properties, membranes with similar PWPs were prepared by adjusting the dope solution composition to eliminate the effect of hydrodynamic conditions on the membrane fouling performance. The blend membranes surface exhibited considerable fouling resistance to the molecular adsorption from both BSA solution and activated sludge solution. In both cases, the flux recovered to almost 80% of the initial flux using only water backflush. Considering their great mechanical properties and antifouling resistance to activated sludge solution, these novel membranes show good potential for application in wastewater treatment. Copyright © 2017 Elsevier B.V. All rights reserved.

Carbon fiber manufacturing via plasma technology

DOEpatents

Paulauskas, Felix L.; Yarborough, Kenneth D.; Meek, Thomas T.

2002-01-01

The disclosed invention introduces a novel method of manufacturing carbon and/or graphite fibers that avoids the high costs associated with conventional carbonization processes. The method of the present invention avoids these costs by utilizing plasma technology in connection with electromagnetic radiation to produce carbon and/or graphite fibers from fully or partially stabilized carbon fiber precursors. In general, the stabilized or partially stabilized carbon fiber precursors are placed under slight tension, in an oxygen-free atmosphere, and carbonized using a plasma and electromagnetic radiation having a power input which is increased as the fibers become more carbonized and progress towards a final carbon or graphite product. In an additional step, the final carbon or graphite product may be surface treated with an oxygen-plasma treatment to enhance adhesion to matrix materials.

Study on the Effect of Straw Fiber on the Performance of Volcanic Slag Concrete

NASA Astrophysics Data System (ADS)

Xiao, Li-guang; Liu, Xi-xu

2018-03-01

In this paper, the effects of straw fiber on the working performance, mechanical properties and frost resistance of volcanic slag lightweight aggregate concrete were studied. The experimental results show that the straw fiber is subjected to surface carbonization treatment and mixed into the volcanic slag light aggregate concrete. The flexural strength and fracture pressure ratio of volcanic slag lightweight aggregate concrete are improved obviously Improved volcanic slag lightweight aggregate concrete brittleness improves toughness. Carbonized straw fiber greatly improves the frost resistance of volcanic slag lightweight aggregate concrete. So that the volcanic slag light aggregate concrete freeze-thaw cycle can reach 300 times.

Microstructural and strength stability of CVD SiC fibers in argon environment

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.; Hull, David R.

1991-01-01

The room temperature tensile strength and microstructure of three types of commercially available chemically vapor deposited silicon carbide fibers were measured after 1, 10, and 100 hour heat treatments under argon pressures of 0.1 to 310 MPa at temperatures to 2100 C. Two types of fiber had carbon-rich surface coatings and the other contained no coating. All three fiber types showed strength degradation beyond 1400 C. Time and temperature of exposure had greater influence on strength degradation than argon pressure. Recrystallization and growth of near stoichiometric SiC grains appears to be the dominant mechanism for the strength degradation.

Microstructural and strength stability of CVD SiC fibers in argon environments

NASA Technical Reports Server (NTRS)

Bhatt, Ramakrishna T.; Hull, David R.

1991-01-01

The room temperature tensile strength and microstructure of three types of commercially available chemically vapor deposited silicon carbide fibers were measured after 1, 10, and 100 hour heat treatments under argon pressures of 0.1 to 310 MPa at temperatures to 2100 C. Two types of fiber had carbon-rich surface coatings and the other contained no coating. All three fiber types showed strength degradation beyond 1400 C. Time and temperature of exposure had greater influence on strength degradation than argon pressure. Recrystallization and growth of near stoichiometric SiC grains appears to be the dominant mechanism for the strength degradation.

DAS Microseismic and Strain Monitoring During Hydraulic Fracturing

NASA Astrophysics Data System (ADS)

Kahn, D.; Karrenbach, M. H.; Cole, S.; Boone, K.; Ridge, A.; Rich, J.; Langton, D.; Silver, K.

2017-12-01

Hydraulic fracturing operations in unconventional subsurface reservoirs are typically monitored using geophones located either at the surface or in adjacent wellbores. A novel approach to record hydraulic stimulations utilizes fiber-optic Distributed Acoustic Sensing (DAS). A fiber-optic cable was installed in a treatment well in a subsurface reservoir (Meramec formation). DAS data were recorded during fluid injection of same fibered well and also during injection into a nearby treatment well at a distance of 350m. For both scenarios the DAS sensing array consisted of approximately 1000 channels at a fine spatial and temporal sampling and with a large sensing aperture. Thus, the full strain wave field is measured along the borehole over its entire length. A variety of physical effects, such as temperature, low-frequency strain and microseismicity were measured and correlated with the treatment program during hydraulic fracturing of the wells. These physical effects occur at various frequency scales and produce complementary measurements. Microseismic events in the magnitude range of -0.5 and -2.0 at a maximum distance of 500m were observed and analyzed for recordings from the fiber-equipped treatment well and also neighboring treatment well. The analysis of this DAS data set demonstrates that current fiber-optic sensing technology can provide enough sensitivity to detect a significant number of microseismic events and that these events can be integrated with temperature and strain measurements for an improved subsurface reservoir description.

Laser anti-corrosion treatment of metal surfaces

NASA Astrophysics Data System (ADS)

Iakovlev, Alexey; Ruzankina, Julia; Kascheev, Sergey; Vasilyev, Oleg; Parfenov, V.; Grishkanich, Alexsandr

2017-02-01

Metal corrosion is the main problem of all metal constructions and buildings. Annual losses resulting from corrosion in industrialized countries are estimated in the range from 2% to 4 % of gross national product. We used a CW fiber laser with the wavelength of 1064 nm and a power up to 18,4 W for laser irradiation of metal surfaces. We report on the optimal treatment of the metal corrosion with laser power density in the range of 93,3÷ 95,5 W/cm2. After the process of laser treatment of steel surface we observe decreased roughness of steel and a small change in its chemical composition. There was an active research of new ways to improve the surface properties of metals and to increase the corrosion resistance. One of the breakthrough methods to protect the material against corrosion is laser treatment. We used a CW fiber laser operating at 1064 nm with up to 18,4 W output power. Experimentally, the samples (steel plates) were irradiated by laser for 35 seconds. Surface treatment of metal was provided at a room temperature and a relative air humidity of 55%. The impact of laser radiation on the surface has contributed to a small change of its chemical composition. It forms protective fluoride coating on the metal surface. The laser radiation significantly increased the concentration of fluorine in the metal from 0.01 atom. % to 5.24 atom. %. The surface roughness of steel has changed from 3.66 μ to 2.66 μ. Protective coatings with best resistance to corrosion were obtained with laser power density in a range of 93.3 W/cm2 to 95.5 W/cm2.

Basic failure mechanisms in advanced composites

NASA Technical Reports Server (NTRS)

Mullin, J. V.; Mazzio, V. F.; Mehan, R. L.

1972-01-01

Failure mechanisms in carbon-epoxy composites are identified as a basis for more reliable prediction of the performance of these materials. The approach involves both the study of local fracture events in model specimens containing small groups of filaments and fractographic examination of high fiber content engineering composites. Emphasis is placed on the correlation of model specimen observations with gross fracture modes. The effects of fiber surface treatment, resin modification and fiber content are studied and acoustic emission methods are applied. Some effort is devoted to analysis of the failure process in composite/metal specimens.

Use of lignocellulose materials as sorption media for phosphorus removal

Treesearch

K.G. Karthikeyan; Mandla A. Tshabalala; Dongmei Wang

2002-01-01

The suitability of modified bark or wood fiber derived from southern yellow pine to function as P sorbents was investigated. Sorbent preparation process included grinding, size fractionation] extraction for surface activation] and treatment with polyallylamine hydrochloride (PAA HCI) or 3-chloro-2-hydroxypropyltrimethlyammonium chloride. SEM images revealed surface...

Effect of the chemical treatments on the characteristics of natural cellulose

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sosiati, H., E-mail: hsosiati@ugm.ac.id; Muhaimin, M.; Abdilah, P.

2014-09-25

In order to characterize the morphology and size distribution of the cellulose fibers, natural cellulose from kenaf bast fibers was extracted using two chemical treatments; (1) alkali-bleaching-ultrasonic treatment and (2) alkali-bleaching-hydrolysis. Solutions of NaOH, H{sub 2}O{sub 2} and H{sub 2}SO{sub 4} were used for alkalization, bleaching and hydrolysis, respectively. The hydrolyzed fibers were centrifuged at a rotation speed of 10000 rpm for 10 min to separate the nanofibers from the microfibers. The separation was repeated in 7 steps by controlling pH of the solution in each step until neutrality was reached. Fourier transform infrared (FTIR) spectroscopy was performed on themore » fibers at the final step of each treatment: i.e. either ultrasonic treated- or hydrolyzed microfibers. Their FTIR spectra were compared with FTIR spectrum of a reference commercial α-cellulose. Changes in morphology and size distribution of the treated fibers were examined by scanning electron microscopy (SEM). FTIR spectra of ultrasonic treated- and hydrolyzed microfibers nearly coincided with the FTIR spectrum of commercial α-cellulose, suggesting successful extraction of cellulose. Ultrasonic treatment for 6 h resulted in a specific morphology in which cellulose nanofibers (≥100 nm) were distributed across the entire surface of cellulose microfibers (∼5 μm). Constant magnetic stirring combined with acid hydrolysis resulted in an inhomogeneous size distribution of both cellulose rods (500 nm-3 μm length, 100–200 nm diameter) and particles 100–200 nm in size. Changes in morphology of the cellulose fibers depended upon the stirring time; longer stirring time resulted in shorter fiber lengths.« less

Phospholipid Nonwoven Electrospun Membranes

NASA Astrophysics Data System (ADS)

McKee, Matthew G.; Layman, John M.; Cashion, Matthew P.; Long, Timothy E.

2006-01-01

Nonwoven fibrous membranes were formed from electrospinning lecithin solutions in a single processing step. As the concentration of lecithin increased, the micellar morphology evolved from spherical to cylindrical, and at higher concentrations the cylindrical micelles overlapped and entangled in a fashion similar to polymers in semi-dilute or concentrated solutions. At concentrations above the onset of entanglements of the wormlike micelles, electrospun fibers were fabricated with diameters on the order of 1 to 5 micrometers. The electrospun phospholipid fibers offer the potential for direct fabrication of biologically based, high-surface-area membranes without the use of multiple synthetic steps, complicated electrospinning designs, or postprocessing surface treatments.

Flexural properties, morphology and bond strength of fiber-reinforced posts: influence of post pretreatment.

PubMed

Braga, Neilor Mateus Antunes; Souza-Gabriel, Aline Evangelista; Messias, Danielle Cristine Furtado; Rached-Junior, Fuad Jacob Abi; Oliveira, Camila Fávero; Silva, Ricardo Gariba; Silva-Sousa, Yara T Corrêa

2012-01-01

The aim of this study was to assess the influence of surface pretreatments of fiber-reinforced posts on flexural strength (FS), modulus of elasticity (ME) and morphology of these posts, as well as the bond strength (BS) between posts and core material. Fifty-two fiber posts (smooth and serrated) were assigned to 4 groups (n=13): no treatment (control), 10% hydrogen peroxide (HP) for 10 min (HP-10), 24% HP for 1 min (HP-24) and airborne-particle abrasion (Al(2)O(3)). To evaluate FS and ME, a 3-point bending test was performed. Three posts of each group were examined by scanning electron microscopy. Composite resin was used as the core build-up and samples were sectioned to obtain microtensile sticks. Data were analyzed by ANOVA and Tukey's test (α=0.05). For FS, significant differences were observed between posts type and surface pretreatment (p<0.05), with the highest means for the smooth posts. Al2O3 provided higher FS than HP-24. Al(2)O(3) promoted higher ME than HP-24 and control. SEM images revealed partial dissolution of the resin matrix in all treated groups. The smooth posts had higher BS and FS than serrated posts (p<0.05). Mechanical properties of the glass fiber posts and the bond strength between posts and composite material were not altered by the surface treatments, except for airborne-particle abrasion that increased the post elastic modulus.

Study of properties of modified silicones at solid-liquid interface: fabric-silicone interactions.

PubMed

Purohit, P; Somasundaran, P; Kulkarni, R

2006-06-15

Silicones are special reagents that impart desired surface properties such as softness, bounciness and antiwrinkle properties to fabrics and related materials. Although these finishing processes have been practiced routinely, very little is known about the mechanisms involved in modification so that they could be improved. The current study was undertaken to develop basic understanding of the mechanisms responsible for surface modification of fibers using silicones. PDMS based amino silicone emulsions, quaternized to various degrees using dimethyl sulphate, were used in the present study. The electrokinetic properties of the modified silicones were studied as a function of pH. It was expected that the silicone emulsions would show a steady positive zeta potential throughout the pH range due to the quaternization by dimethyl sulphate. Surprisingly, a sudden drop in the zeta potential was observed around pH 8 with the samples turning hazy in the pH range of 8-10. Turbidimetric studies also showed a sudden increase in the turbidity in the pH range 8-10 where commercial processes also encounter problems. It was concluded that the emulsions were destabilized at pH 8-10 thus rendering them ineffective for surface treatment. In order to identify reason for the improvement in fabric properties, fiber structure was monitored using atomic force microscopy. It was observed that the treated fibers were far smoother, relaxed and uniform as compared to the untreated fibers. Thus the morphology of the fabric is modified in a specific way by treatment with specialty silicones.

Integrating qPLM and biomechanical test data with an anisotropic fiber distribution model and predictions of TGF-β1 and IGF-1 regulation of articular cartilage fiber modulus

PubMed Central

Stender, Michael E.; Raub, Christopher B.; Yamauchi, Kevin A.; Shirazi, Reza; Vena, Pasquale; Sah, Robert L.; Hazelwood, Scott J.; Klisch, Stephen M.

2013-01-01

A continuum mixture model with distinct collagen (COL) and glycosaminoglycan (GAG) elastic constituents was developed for the solid matrix of immature bovine articular cartilage. A continuous COL fiber volume fraction distribution function and a true COL fiber elastic modulus (Ef) were used. Quantitative polarized light microscopy (qPLM) methods were developed to account for the relatively high cell density of immature articular cartilage and used with a novel algorithm that constructs a 3D distribution function from 2D qPLM data. For specimens untreated and cultured in vitro, most model parameters were specified from qPLM analysis and biochemical assay results; consequently, Ef was predicted using an optimization to measured mechanical properties in uniaxial tension and unconfined compression. Analysis of qPLM data revealed a highly anisotropic fiber distribution, with principal fiber orientation parallel to the surface layer. For untreated samples, predicted Ef values were 175 and 422 MPa for superficial (S) and middle (M) zone layers, respectively. TGF-β1 treatment was predicted to increase and decrease Ef values for the S and M layers to 281 and 309 MPa, respectively. IGF-1 treatment was predicted to decrease Ef values for the S and M layers to 22 and 26 MPa, respectively. A novel finding was that distinct native depth-dependent fiber modulus properties were modulated to nearly homogeneous values by TGF-β1 and IGF-1 treatments, with modulated values strongly dependent on treatment. PMID:23266906

Performance and efficiency of old newspaper deinking by combining cellulase/hemicellulase with laccase-violuric acid system

DOE Office of Scientific and Technical Information (OSTI.GOV)

Xu Qinghua; Fu Yingjuan; Gao Yang

2009-05-15

Performance and efficiency of old newspaper (ONP) deinking by combining cellulase/hemicellulase with laccase-violuric acid system (LVS) were investigated in this study. Brightness, effective residual ink concentration (ERIC) and physical properties were evaluated for the deinked pulp. Fiber length, coarseness, specific surface area and specific volume were also tested. The changes of dissolved lignin during the deinking processes were measured with UV spectroscopy. The fiber morphology was observed with environmental scanning electronic microscopy (ESEM). Experimental results showed that, compared to the pulp deinked with each individual enzyme, ERIC was lower for the cellulase/hemicellulase-LVS-deinked pulp. This indicated that a synergy existed inmore » ONP deinking using a combination of enzymes. After being bleached by H{sub 2}O{sub 2}, enzyme-combining deinked pulp gave higher brightness and better strength properties. Compared with individual enzyme deinked pulp, average fiber length and coarseness decreased a little for the enzyme-combining deinked pulps. A higher specific surface area and specific volume of the pulp fibers were achieved. UV analysis proved that more lignin was released during the enzyme-combining deinking process. ESEM images showed that more fibrillation was observed on the fiber surface due to synergistic treatment.« less

The Influence of Green Surface Modification of Oil Palm Mesocarp Fiber by Superheated Steam on the Mechanical Properties and Dimensional Stability of Oil Palm Mesocarp Fiber/Poly(butylene succinate) Biocomposite

PubMed Central

Then, Yoon Yee; Ibrahim, Nor Azowa; Zainuddin, Norhazlin; Ariffin, Hidayah; Yunus, Wan Md Zin Wan; Chieng, Buong Woei

2014-01-01

In this paper, superheated steam (SHS) was used as cost effective and green processing technique to modify oil palm mesocarp fiber (OPMF) for biocomposite applications. The purpose of this modification was to promote the adhesion between fiber and thermoplastic. The modification was carried out in a SHS oven at various temperature (200–230 °C) and time (30–120 min) under normal atmospheric pressure. The biocomposites from SHS-treated OPMFs and poly(butylene succinate) (PBS) at a weight ratio of 70:30 were prepared by melt blending technique. The mechanical properties and dimensional stability of the biocomposites were evaluated. This study showed that the SHS treatment increased the roughness of the fiber surface due to the removal of surface impurities and hemicellulose. The tensile, flexural and impact properties, as well as dimensional stability of the biocomposites were markedly enhanced by the presence of SHS-treated OPMF. Scanning electron microscopy analysis showed improvement of interfacial adhesion between PBS and SHS-treated OPMF. This work demonstrated that SHS could be used as an eco-friendly and sustainable processing method for modification of OPMF in biocomposite fabrication. PMID:25177865

DOE Office of Scientific and Technical Information (OSTI.GOV)

Li Hong.

A new technique was developed and demonstrated for combining carbon fibers with aromatic thermoplastic matrices to form a high-quality towpreg. The developed technique utilizes an in-situ electrochemical process (Electrochemical polymerization - ECP) to create the entire polymer matrix surrounding the fiber array by direct polymerization of monomer. Poly-paraxylylene (PPX) and derivatives are successfully polymerized in-situ on carbon fiber surfaces through ECP. A PPX/carbon-fiber towpreg with 40 vol % of matrix is achieved in a fairly short reaction time with a high polymer-coating efficiency. Vapor deposition polymerization (VDP) was also studied. PPX and carbon-fiber towpreg were made successfully by this process.more » A comparison between ECP and VDP was conducted. A study on electrochemical oxidation (ECO) of carbon fibers was also performed. The ECO treatment may be suitable for carbon fibers incorporated in composites with high-temperature curing resins and thermoplastic matrices.« less

Assessment of the Mechanical Properties of Sisal Fiber-Reinforced Silty Clay Using Triaxial Shear Tests

PubMed Central

Wu, Yankai; Li, Yanbin; Niu, Bin

2014-01-01

Fiber reinforcement is widely used in construction engineering to improve the mechanical properties of soil because it increases the soil's strength and improves the soil's mechanical properties. However, the mechanical properties of fiber-reinforced soils remain controversial. The present study investigated the mechanical properties of silty clay reinforced with discrete, randomly distributed sisal fibers using triaxial shear tests. The sisal fibers were cut to different lengths, randomly mixed with silty clay in varying percentages, and compacted to the maximum dry density at the optimum moisture content. The results indicate that with a fiber length of 10 mm and content of 1.0%, sisal fiber-reinforced silty clay is 20% stronger than nonreinforced silty clay. The fiber-reinforced silty clay exhibited crack fracture and surface shear fracture failure modes, implying that sisal fiber is a good earth reinforcement material with potential applications in civil engineering, dam foundation, roadbed engineering, and ground treatment. PMID:24982951

Accelerated aging of adhesive-mediated fiber post-resin composite bonds: A modeling approach.

PubMed

Radovic, Ivana; Monticelli, Francesca; Papacchini, Federica; Magni, Elisa; Cury, Alvaro Hafiz; Vulicevic, Zoran R; Ferrari, Marco

2007-08-01

Although fiber posts luted in root canals are not directly exposed to oral fluids, water storage is considered as in vitro accelerated aging test for bonded interfaces. The aim of the study was to evaluate the influence of accelerated water aging on fiber post-resin composite adhesion. Forty fiber posts (DT Light Post, RTD) were randomly divided into two main groups, according to the surface treatment performed. Group I: XPBond adhesive (Dentsply Caulk); Group II: sandblasting (Rocatec-Pre, 3M ESPE) and XPBond. Dual-cured resin cement (Calibra, Dentsply Caulk) and flowable composite (X-Flow, Dentsply Caulk) were applied on the posts to produce cylindrical specimens. The bond strength at the interface between post and cement/composite was measured with the microtensile test according to the non-trimming technique. Half of the sticks were tested immediately for bond strength, while in the other half testing was performed after 1 month of water storage at 37 degrees C. Post-cement/composite interfaces were evaluated under SEM prior and after water aging. Statistical analysis was performed using the Kruskal-Wallis ANOVA followed by Dunn's multiple range test (p<0.05). Immediate bond strength was higher on sandblasted posts. After water aging the two post surface treatments resulted comparable in bond strength. Resin cement achieved higher bond strength to fiber posts than flowable composite. Water aging significantly reduced bond strength. Sandblasting followed by adhesive coating may improve immediate post-resin bond strength in comparison to adhesive alone. However, fiber post-resin bond strength mediated by hydrophilic adhesive tends to decrease after water aging.

Modification of Wood Fiber for Use in Cement Board

NASA Astrophysics Data System (ADS)

Han, F. Q.; Tan, X.; Zhao, F. Q.

2017-12-01

When ordinary Portland cement is used for wood fiber cement (WFC) board, the setting time is too long, even hard to solidify. Three methods can be used for wood fiber modification, i.e., soaking in water, treated with alkali solution and coated with some substances on the fiber surface. The results show that the proper water-cement ratio of WFC paste is 1:1.3 in the case of wood cement ratio being 1:1. The WFC board from modified wood fiber and cement is better than the control samples, in which the combined treatment, i.e. soaking in hot water and then coating with alkali-BFS-EVA slurry, behaves best. It is proved that ordinary Portland cement can be used to produce WFC board, with the modified wood fiber, which can greatly reduce production costs.

An applied investigation of kenaf-based fiber/polymer composites as potential lightweight materials for automotive components

NASA Astrophysics Data System (ADS)

Du, Yicheng

Natural fibers have the potential to replace glass fibers in fiber-reinforced composite applications. However, the natural fibers' intrinsic properties cause these issues: (1) the mechanical property variation; (2) moisture uptake by natural fibers and their composites; (3) lack of sound, cost-effective, environment-friendly fiber-matrix compounding processes; (4) incompatibility between natural fibers and polymer matrices; and (5) low heat-resistance of natural fibers and their composites. This dissertation systematically studied the use of kenaf bast fiber bundles, obtained via a mechanical retting method, as a light-weight reinforcement material for fiber-reinforced thermoset polymer composites for automotive applications. Kenaf bast fiber bundle tensile properties were tested, and the effects of locations in the kenaf plant, loading rates, retting methods, and high temperature treatments and their durations on kenaf bast fiber bundle tensile properties were evaluated. A process has been developed for fabricating high fiber loading kenaf bast fiber bundle-reinforced unsaturated polyester composites. The generated composites possessed high elastic moduli and their tensile strengths were close to specification requirements for glass fiber-reinforced sheet molding compounds. Effects of fiber loadings and lengths on resultant composite's tensile properties were evaluated. Fiber loadings were very important for composite tensile modulus. Both fiber loadings and fiber lengths were important for composite tensile strengths. The distributions of composite tensile, flexural and impact strengths were analyzed. The 2-parameter Weibull model was found to be the most appropriate for describing the composite strength distributions and provided the most conservative design values. Kenaf-reinforced unsaturated polyester composites were also proved to be more cost-effective than glass fiber-reinforced SMCs at high fiber loadings. Kenaf bast fiber bundle-reinforced composite's water absorption properties were tested. Surface-coating and edge-sealing significantly reduced composite water resistance properties. Encapsulation was a practical method to improve composite water resistance properties. The molding pressure and styrene concentrations on composite and matrix properties were evaluated. Laser and plasma treatment improved fiber-to-matrix adhesion.

A simple method for the preparation of activated carbon fibers coated with graphite nanofibers.

PubMed

Kim, Byung-Joo; Park, Soo-Jin

2007-11-15

A simple method is described for the preparation of activated carbon fibers (ACFs) coated with graphite nanofibers (GNFs). Low-pressure-plasma mixed-gas (Ar/O2) treatment of the ACFs led to the growth of GNFs on their surface. The growth was greater at higher power inputs, and from TEM observations the GNFs were seen to be of herringbone type. It was found that the N2 adsorption capacity of the ACFs did not sharply decrease, and that volume resistivity of the ACFs enhanced as a result of this treatment.

Surface Properties of a Hooked Steel Fiber and their Effects on the Fiber Pullout and Composite Cracking 1. Experimental Study

NASA Astrophysics Data System (ADS)

Zesers, A.; Krūmiņš, J.

2014-09-01

Concrete as a material is brittle, but adding short steel fibers to the matrix can significantly improve its mechanical properties. The chemical adhesion between concrete and steel is weak, and the fiber pullout properties are based on fiber geometry and frictional forces. Single-fiber pullout tests of steel fibers with toothed and smooth surfaces were performed in order to characterize the effects of fiber surface facture. The influence of fiber form, surface facture, and fiber orientation (relative to the pullout direction) on the fiber withdrawal resistance and the maximum pullout force were studied.

Electron beam surface modifications in reinforcing and recycling of polymers

NASA Astrophysics Data System (ADS)

Czvikovszky, T.; Hargitai, H.

1997-08-01

Thermoplastic polymers can be fiber-reinforced in the recycling step through a reactive modification of the interface between the polymer matrix and fiber. Recollected automobile bumpers made of polypropylene copolymers have been reinforced during the reprocessing with eight different types of high-strength fibers, with waste cord-yarns of the tire industry. A thin layer reactive interface of acrylic oligomers has been applied and activated through low energy (175 keV) electron beam (EB). The upcycling (upgrading recycling) resulted in a series of extrudable and injection-mouldable, fiber-reinforced thermoplastic of enhanced bending strength, increased modulus of elasticity and acceptable impact strength. EB treatment has been compared with conventional methods.

Oriented and ordered mesoporous ZrO{sub 2}/TiO{sub 2} fibers with well-organized linear and spring structure

DOE Office of Scientific and Technical Information (OSTI.GOV)

Zhu, Luyi, E-mail: zhuly@sdu.edu.cn; Liu, Benxue; Qin, Weiwei, E-mail: jiuyuan.1001@163.com

Graphical abstract: The ultra-stable order mesoporous ZrO{sub 2}/TiO{sub 2} fibers with well-organized linear and spring structure and large surface area under higher temperatures were prepared by a simple EISA process. - Highlights: • The ZrO{sub 2}/TiO{sub 2} fibers were prepared by EISA process combined with steam heat-treatment. • The mesoporous ZrO{sub 2}/TiO{sub 2} fibers have well-organized linear and spring structure. • The fibers were composed of oval rod nanocrystals of ZrTiO{sub 4}. - Abstract: The ultra-stable order mesoporous ZrO{sub 2}/TiO{sub 2} fibers with well-organized linear and spring structure and large surface areas under higher temperatures were prepared by a (simplemore » evaporation-induced assembly) EISA process. The preparation, microstructures and formation processes were characterized by Fourier transformation infrared (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and N{sub 2} adsorption–absorption measurements. The fibers take on pinstripe configuration which is very orderly along or perpendicular to the axial direction of the fibers. The diameters of the pinstripe are in the region of 200–400 nm and arranges regularly, which are composed of oval rod nanocrystals of ZrTiO{sub 4}.« less

Hydroxyapatite growth on cotton fibers modified chemically

NASA Astrophysics Data System (ADS)

Varela Caselis, J. L.; Reyes Cervantes, E.; Landeta Cortés, G.; Agustín Serrano, R.; Rubio Rosas, E.

2014-09-01

We have prepared carboxymethyl cellulose fibers (CMC) by chemically modifying cotton cellulose with monochloroacetic acid and calcium chloride solution. This modification favored the growth of hydroxyapatite (HAP) on the surface of the CMC fibers in contact with simulated body fluid solutions (SBF). After soaking in SBF for periods of 7, 14 and 21 days, formation of HAP was observed. Analysis by scanning electron microscopy and X-ray diffraction showed that crystallinity, crystallite size, and growth of HAP increased with the soaking time. The amount of HAP deposited on CMC fibers increased greatly after 21 days of immersion in the SBF, while the substrate surface was totally covered with hemispherical aggregates with the size of the order of 2 microns. Elemental analysis showed the presence of calcium and phosphate, with calcium/phosphate atomic ratio of 1.54. Fourier transform infrared spectroscopy bands confirmed the presence of HAP. The results suggest that cotton modified by calcium treatment has a nucleating ability and can accelerate the nucleation of HAP crystals.

Electrospun Nanofibers Made of Silver Nanoparticles, Cellulose Nanocrystals, and Polyacrylonitrile as Substrates for Surface-Enhanced Raman Scattering

PubMed Central

Ren, Suxia; Dong, Lili; Zhang, Xiuqiang; Lei, Tingzhou; Ehrenhauser, Franz; Song, Kunlin; Li, Meichun; Sun, Xiuxuan; Wu, Qinglin

2017-01-01

Nanofibers with excellent activities in surface-enhanced Raman scattering (SERS) were developed through electrospinning precursor suspensions consisting of polyacrylonitrile (PAN), silver nanoparticles (AgNPs), silicon nanoparticles (SiNPs), and cellulose nanocrystals (CNCs). Rheology of the precursor suspensions, and morphology, thermal properties, chemical structures, and SERS sensitivity of the nanofibers were investigated. The electrospun nanofibers showed uniform diameters with a smooth surface. Hydrofluoric (HF) acid treatment of the PAN/CNC/Ag composite nanofibers (defined as p-PAN/CNC/Ag) led to rougher fiber surfaces with certain pores and increased mean fiber diameters. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) results confirmed the existence of AgNPs that were formed during heat and HF acid treatment processes. In addition, thermal stability of the electrospun nanofibers increased due to the incorporation of CNCs and AgNPs. The p-PAN/CNC/Ag nanofibers were used as a SERS substrate to detect p-aminothiophenol (p-ATP) probe molecule. The results show that this substrate exhibited high sensitivity for the p-ATP probe detection. PMID:28772428

Controllable preparation of a nano-hydroxyapatite coating on carbon fibers by electrochemical deposition and chemical treatment.

PubMed

Wang, Xudong; Zhao, Xueni; Wang, Wanying; Zhang, Jing; Zhang, Li; He, Fuzhen; Yang, Jianjun

2016-06-01

A nano-hydroxyapatite (HA) coating with appropriate thickness and morphology similar to that of human bone tissue was directly prepared onto the surfaces of carbon fibers (CFs). A mixed solution of nitric acid, hydrochloric acid, sulfuric acid, and hydrogen peroxide (NHSH) was used in the preparation process. The coating was fabricated by combining NHSH treatment and electrochemical deposition (ECD). NHSH treatment is easy to operate, produces rapid reaction, and highly effective. This method was first used to induce the nucleation and growth of HA crystals on the CF surfaces. Numerous O-containing functional groups, such as hydroxyl (-OH) and carboxyl (-COOH) groups, were grafted onto the CF surfaces by NHSH treatment (NHSH-CFs); as such, the amounts of these groups on the functionalized CFs increased by nearly 8- and 12-fold, respectively, compared with those on untreated CFs. After treatment, the NHSH-CFs not only acquired larger specific surface areas but retained surfaces free from serious corrosion or breakage. Hence, NHSH-CFs are ideal depositional substrates of HA coating during ECD. ECD was successfully used to prepare a nano-rod-like HA coating on the NHSH-CF surfaces. The elemental composition, structure, and morphology of the HA coating were effectively controlled by adjusting various technological parameters, such as the current density, deposition time, and temperature. The average central diameter of HA crystals and the coating density increased with increasing deposition time. The average central diameter of most HA crystals on the NHSH-CFs varied from approximately 60 nm to 210 nm as the deposition time increased from 60 min to 180 min. Further studies on a possible deposition mechanism revealed that numerous O-containing functional groups on the NHSH-CF surfaces could associate with electrolyte ions (Ca(2+)) to form special chemical bonds. These bonds can induce HA coating deposition and improve the interfacial bonding strength between the HA coating and NHCH-CFs. The results of this study and the proposed preparation of uniform and dense nano-HA coating provide theoretical and practical guidance for future investigations of active HA coatings on fiber materials for medical products and implants. This work also lays the foundation for the wider use of HA-coated CFs/HA composite implants in clinical application. Copyright © 2016 Elsevier B.V. All rights reserved.

Plasma treatment of polymers for improved adhesion

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kelber, J.A.

1988-01-01

A variety of plasma treatments of polymer surfaces for improved adhesion are reviewed: noble and reactive gas treatment of fluoropolymers; noble and reactive treatment of polyolefins, and plasma-induced amination of polymer fibers. The plasma induced surface chemical and morphological changes are discussed, as are the mechanisms of adhesion to polymeric adhesives, particularly epoxy. Noble gas plasma etching of flouropolymers produces a partially defluorinated, textured surface. The mechanical interlocking of this textured surface is the primary cause of improved adhesion to epoxy. Reactive gas plasmas also induce defluorination, but oxygen containing gases cause continual ablation of the fluoropolymer surface. Noble andmore » reactive gas (exept for hydrogen) etching of polyolefins results in surface oxidation and improved adhesion via hydrogen bonding of these oxygen containing groups across the interface. The introduction of amine groups to a polymer surface by amonia or amine plasma treatment generally results in improved adhesion to epoxy. However, amine-epoxy ring interactions can be severely effected by steric factors due to chemical groups surrounding the amine. 41 refs.« less

Plasma treatment of polypropylene fabric for improved dyeability with soluble textile dyestuff

NASA Astrophysics Data System (ADS)

Yaman, Necla; Özdoğan, Esen; Seventekin, Necdet; Ayhan, Hakan

2009-05-01

The impact of plasma treatment parameters on the surface morphology, physical-chemical, and dyeing properties of polypropylene (PP) using anionic and cationic dyestuffs were investigated in this study. Argon plasma treatment was used to activate PP fabric surfaces. Activated surfaces were grafted different compounds: 6-aminohexanoic acid (6-AHA), acrylic acid (AA), ethylendiamine (EDA), acryl amide (AAMID) and hexamethyldisiloxane (HMDS). Compounds were applied after the plasma treatment and the acid and basic dyeing result that was then observed, were quite encouraging in certain conditions. The possible formed oxidizing groups were emphasized by FTIR and ATR and the surface morphology of plasma treated PP fibers was also investigated with scanning electron microscopy (SEM). PP fabric could be dyed with acid and basic dyestuffs after only plasma treatment and plasma induced grafting, and fastnesses of the dyed samples were satisfactory.

Surface properties and graphitization of polyacrylonitrile based fiber electrodes affecting the negative half-cell reaction in vanadium redox flow batteries

NASA Astrophysics Data System (ADS)

Langner, J.; Bruns, M.; Dixon, D.; Nefedov, A.; Wöll, Ch.; Scheiba, F.; Ehrenberg, H.; Roth, C.; Melke, J.

2016-07-01

Carbon felt electrodes for vanadium redox flow batteries are obtained by the graphitization of polyacrylonitrile based felts at different temperatures. Subsequently, the surface of the felts is modified via thermal oxidation at various temperatures. A single-cell experiment shows that the voltage efficiency is increased by this treatment. Electrode potentials measured with reference electrode setup show that this voltage efficiency increase is caused mainly by a reduction of the overpotential of the negative half-cell reaction. Consequently, this reaction is investigated further by cyclic voltammetry and the electrode activity is correlated with structural and surface chemical properties of the carbon fibers. By Raman, X-ray photoelectron and near edge X-ray absorption fine structure spectroscopy the role of edge sites and oxygen containing functional groups (OCFs) for the electrochemical activity are elucidated. A significant activity increase is observed in correlation with these two characteristics. The amount of OCFs is correlated with structural defects (e.g. edge sites) of the carbon fibers and therefore decreases with an increasing graphitization degree. Thus, for the same thermal oxidation temperature carbon fibers graphitized at a lower temperature show higher activities than those graphitized at a higher temperature.

The effect of surface modification of glass fiber on the performance of poly(lactic acid) composites: Graphene oxide vs. silane coupling agents

NASA Astrophysics Data System (ADS)

Jing, Mengfan; Che, Junjin; Xu, Shuman; Liu, Zhenwei; Fu, Qiang

2018-03-01

In this work, a comparison study was carried out to investigate the efficacy of glass fiber (GF) in reinforcing poly(lactic acid) (PLA) by using traditional silane coupling agents (GF-S) and novel graphene oxide (GF-GO) as surface modifiers. The crystallization behavior of the PLA matrix was investigated by differential scanning calorimetry. The mechanical performances and the thermomechanical properties of the composites were evaluated by uniaxial tensile testing and dynamic mechanical analysis, respectively. For neat GF without any treatment, the poor interfacial adhesion and the sharp shortening of the GF length result in the relatively poor mechanical performances of PLA/GF composites. However, the incorporation of GF-S significantly improves the mechanical strength and keeps relatively good toughness of the composites, while GF-GO exhibits excellent nucleation ability for PLA and could moderately increase the modulus of the composites. The thermomechanical properties of the composites are improved markedly resulting from the crystallinity increase. The different surface modification of glass fiber influences the crystallinity of matrix, the interfacial interaction and the length of fiber, which altogether affect the mechanical performances of the prepared PLA/GF composites.

Influence of pretreatment on the surface characteristics of PLLA fibers and subsequent hydroxyapatite coating.

PubMed

Peng, F; Olson, J R; Shaw, M T; Wei, M

2009-01-01

A fibrous precursor for bone repair composites was made by coating poly(L-lactide) (PLLA) fibers with hydroxyapatite (HA) using a biomimetic method. To enhance the bonding between the HA coating and the PLLA fiber, PLLA fibers were etched with either sodium hydroxide or sodium hypochlorite to generate carboxyl groups on fiber surfaces. The experiments were designed to determine the influence of etching on the fiber surface morphology and chemistry as well as the subsequent HA coating on the etched fiber surfaces. It was found that the etching pretreatment increased the roughness as well as the hydrophilicity of fibers, indicating that hydrolysis of PLLA chains had taken place on fiber surfaces. The etching pretreatment also promoted HA coating formation by introducing thicker coating on the surface of fibers with a longer etching time, a higher etching concentration, or with NaOCl as the etching agent. A mechanism of surface hydrolysis and oxidation of PLLA was proposed. (c) 2008 Wiley Periodicals, Inc.

Plasma treatments of wool fiber surface for microfluidic applications

DOE Office of Scientific and Technical Information (OSTI.GOV)

Jeon, So-Hyoun; Hwang, Ki-Hwan; Lee, Jin Su

Highlights: • We used atmospheric plasma for tuning the wettability of wool fibers. • The wicking rates of the wool fibers increased with increasing treatment time. • The increasing of wettability results in removement of fatty acid on the wool surface. - Abstract: Recent progress in health diagnostics has led to the development of simple and inexpensive systems. Thread-based microfluidic devices allow for portable and inexpensive field-based technologies enabling medical diagnostics, environmental monitoring, and food safety analysis. However, controlling the flow rate of wool thread, which is a very important part of thread-based microfluidic devices, is quite difficult. For thismore » reason, we focused on thread-based microfluidics in the study. We developed a method of changing the wettability of hydrophobic thread, including wool thread. Thus, using natural wool thread as a channel, we demonstrate herein that the manipulation of the liquid flow, such as micro selecting and micro mixing, can be achieved by applying plasma treatment to wool thread. In addition to enabling the flow control of the treated wool channels consisting of all natural substances, this procedure will also be beneficial for biological sensing devices. We found that wools treated with various gases have different flow rates. We used an atmospheric plasma with O{sub 2}, N{sub 2} and Ar gases.« less

Carbonic anhydrase immobilized on hollow fiber membranes using glutaraldehyde activated chitosan for artificial lung applications

PubMed Central

Kimmel, J. D.; Arazawa, D. T.; Ye, S.-H.; Shankarraman, V.; Wagner, W. R.

2013-01-01

Extracorporeal CO2 removal from circulating blood is a promising therapeutic modality for the treatment of acute respiratory failure. The enzyme carbonic anhydrase accelerates CO2 removal within gas exchange devices by locally catalyzing HCO3− into gaseous CO2 within the blood. In this work, we covalently immobilized carbonic anhydrase on the surface of polypropylene hollow fiber membranes using glutaraldehyde activated chitosan tethering to amplify the density of reactive amine functional groups for enzyme immobilization. XPS and a colorimetric amine assay confirmed higher amine densities on the chitosan coated fiber compared to control fiber. Chitosan/CA coated fibers exhibited accelerated CO2 removal in scaled-down gas exchange devices in buffer and blood (115 % enhancement vs. control, 37 % enhancement vs. control, respectively). Carbonic anhydrase immobilized directly on hollow fiber membranes without chitosan tethering resulted in no enhancement in CO2 removal. Additionally, fibers coated with chitosan/carbonic anhydrase demonstrated reduced platelet adhesion when exposed to blood compared to control and heparin coated fibers. PMID:23888352

High-Temperature Hot Air/Silane Coupling Modification of Wood Fiber and Its Effect on Properties of Wood Fiber/HDPE Composites.

PubMed

Chen, Feng; Han, Guangping; Li, Qingde; Gao, Xun; Cheng, Wanli

2017-03-13

The surfaces of poplar wood fibers were modified using high-temperature hot air (HTHA) treatment and silane coupling agent. The single factor test was then used to investigate the performances (e.g., the change of functional groups, polarity, cellulose crystallinity, and thermal stability) of modified poplar wood fibers (mPWF) through Fourier transform infrared spectrometry, X-ray diffraction and thermo-gravimetric analysis for the subsequent preparation of wood-plastic composites (WPCs). The effect of HTHA treatment conditions-such as temperature, inlet air velocity, and feed rate-on the performances of WPCs was also investigated by scanning electron microscopy and dynamic mechanical analysis. The main findings indicated that HTHA treatment could promote the hydration of mPWF and improve the mechanical properties of WPCs. Treatment temperature strongly affected the mechanical properties and moisture adsorption characteristics of the prepared composites. With the increase of treated temperature and feed rate, the number of hydroxyl groups, holocellulose content, and the pH of mPWF decreased. The degree of crystallinity and thermal stability and the storage modulus of the prepared composites of mPWF increased. However, dimensional stability and water absorption of WPCs significantly reduced. The best mechanical properties enhancement was observed with treatment temperature at 220 °C. This study demonstrated the feasibility for the application of an HTHA treatment in the WPC production industry.

High-Temperature Hot Air/Silane Coupling Modification of Wood Fiber and Its Effect on Properties of Wood Fiber/HDPE Composites

PubMed Central

Chen, Feng; Han, Guangping; Li, Qingde; Gao, Xun; Cheng, Wanli

2017-01-01

The surfaces of poplar wood fibers were modified using high-temperature hot air (HTHA) treatment and silane coupling agent. The single factor test was then used to investigate the performances (e.g., the change of functional groups, polarity, cellulose crystallinity, and thermal stability) of modified poplar wood fibers (mPWF) through Fourier transform infrared spectrometry, X-ray diffraction and thermo-gravimetric analysis for the subsequent preparation of wood-plastic composites (WPCs). The effect of HTHA treatment conditions—such as temperature, inlet air velocity, and feed rate—on the performances of WPCs was also investigated by scanning electron microscopy and dynamic mechanical analysis. The main findings indicated that HTHA treatment could promote the hydration of mPWF and improve the mechanical properties of WPCs. Treatment temperature strongly affected the mechanical properties and moisture adsorption characteristics of the prepared composites. With the increase of treated temperature and feed rate, the number of hydroxyl groups, holocellulose content, and the pH of mPWF decreased. The degree of crystallinity and thermal stability and the storage modulus of the prepared composites of mPWF increased. However, dimensional stability and water absorption of WPCs significantly reduced. The best mechanical properties enhancement was observed with treatment temperature at 220 °C. This study demonstrated the feasibility for the application of an HTHA treatment in the WPC production industry. PMID:28772646

Risk Assessment of Carbon Fiber Composite in Surface Transportation

NASA Technical Reports Server (NTRS)

Hathaway, W. T.; Hergenrother, K. M.

1980-01-01

The vulnerability of surface transportation to airborne carbon fibers and the national risk associated with the potential use of carbon fibers in the surface transportation system were evaluated. Results show airborne carbon fibers may cause failure rates in surface transportation of less than one per year by 1995. The national risk resulting from the use of carbon fibers in the surface transportation system is discussed.

Time Effects on Morphology and Bonding Ability in Mercerized Natural Fibers for Composite Reinforcement

DTIC Science & Technology

2011-01-01

such as lignin , are not favored for interaction with most hydrophilic resins. Lignin , being mostly hydrophobic, shows poor adhe- sion between the...cellulose, hemicelluloses, and lignin , are shown in Figures 1, 2, 3, and 4, respectively. Chemical treatment has been a well-known method em- ployed...to clean the surfaces of fibers and remove unwanted components, such as waxes, pectin, hemicellulose, and lignin . The removal of these materials has

Optical coherence tomography guided dental drill

DOEpatents

DaSilva, Luiz B.; Colston, Jr., Bill W.; James, Dale L.

2002-01-01

A dental drill that has one or multiple single mode fibers that can be used to image in the vicinity of the drill tip. It is valuable to image below the surface being drilled to minimize damage to vital or normal tissue. Identifying the boundary between decayed and normal enamel (or dentine) would reduce the removal of viable tissue, and identifying the nerve before getting too close with the drill could prevent nerve damage. By surrounding a drill with several optical fibers that can be used by an optical coherence domain reflectometry (OCDR) to image several millimeters ahead of the ablation surface will lead to a new and improved dental treatment device.

Flame-resistant textiles

NASA Technical Reports Server (NTRS)

Fogg, L. C.; Stringham, R. S.; Toy, M. S.

1980-01-01

Flame resistance treatment for acid resistant polyamide fibers involving photoaddition of fluorocarbons to surface has been scaled up to treat 10 yards of commercial width (41 in.) fabric. Process may be applicable to other low cost polyamides, polyesters, and textiles.

Effect of components and surface treatments of fiber-reinforced composite posts on bond strength to composite resin.

PubMed

Asakawa, Yuya; Takahashi, Hidekazu; Kobayashi, Masahiro; Iwasaki, Naohiko

2013-10-01

The aim of this study was to clarify the effect of the components and surface treatments of fiber-reinforced composite (FRC) posts on the durable bonding to core build-up resin evaluated using the pull-out and microtensile tests. Four types of experimental FRC posts, combinations of two types of matrix resins (polymethyl methacrylate and urethane dimethacrylate) and two types of fiberglass (E-glass and zirconia-containing glass) were examined. The FRC posts were subjected to one of three surface treatments (cleaned with ethanol, dichloromethane, or sandblasting). The bond strength between the FRC posts and core build-up resin were measured using the pull-out and microtensile tests before and after thermal cycling. The bond strengths obtained by each test before and after thermal cycling were statistically analyzed by three-way ANOVA and Tukey's multiple comparisons test (p<0.05). The bond strengths except for UDMA by the pull-out test decreased after thermal cycling. Regardless the test method and thermal cycling, matrix resins, the surface treatment and their interaction were statistically significant, but fiberglass did not. Dichloromethane treatment was effective for the PMMA-based FRC posts by the pull-out test, but not by the microtensile test. Sandblasting was effective for both PMMA- and UDMA-based FRC posts, regardless of the test method. The bond strengths were influenced by the matrix resin of the FRC post and the surface treatment. The bond strengths of the pull-out test showed a similar tendency of those of the microtensile test, but the value obtained by these test were different. Copyright © 2013 Elsevier Ltd. All rights reserved.

A new fiber optic sensor for inner surface roughness measurement

NASA Astrophysics Data System (ADS)

Xu, Xiaomei; Liu, Shoubin; Hu, Hong

2009-11-01

In order to measure inner surface roughness of small holes nondestructively, a new fiber optic sensor is researched and developed. Firstly, a new model for surface roughness measurement is proposed, which is based on intensity-modulated fiber optic sensors and scattering modeling of rough surfaces. Secondly, a fiber optical measurement system is designed and set up. Under the help of new techniques, the fiber optic sensor can be miniaturized. Furthermore, the use of micro prism makes the light turn 90 degree, so the inner side surface roughness of small holes can be measured. Thirdly, the fiber optic sensor is gauged by standard surface roughness specimens, and a series of measurement experiments have been done. The measurement results are compared with those obtained by TR220 Surface Roughness Instrument and Form Talysurf Laser 635, and validity of the developed fiber optic sensor is verified. Finally, precision and influence factors of the fiber optic sensor are analyzed.

The Design and Testing of a Dual Fiber Textile Matrix for Accelerating Surface Hemostasis

PubMed Central

Fischer, Thomas H.; Vournakis, John N.; Manning, James E.; McCurdy, Shane L.; Rich, Preston B.; Nichols, Timothy C.; Scull, Christopher M.; McCord, Marian G.; Decorta, Joseph A.; Johnson, Peter C.; Smith, Carr J.

2011-01-01

The standard treatment for severe traumatic injury is frequently compression and application of gauze dressing to the site of hemorrhage. However, while able to rapidly absorb pools of shed blood, gauze fails to provide strong surface (topical) hemostasis. The result can be excess hemorrhage-related morbidity and mortality. We hypothesized that cost-effective materials (based on widespread availability of bulk fibers for other commercial uses) could be designed based on fundamental hemostatic principles to partially emulate the wicking properties of gauze while concurrently stimulating superior hemostasis. A panel of readily available textile fibers was screened for the ability to activate platelets and the intrinsic coagulation cascade in vitro. Type E continuous filament glass and a specialty rayon fiber were identified from the material panel as accelerators of hemostatic reactions and were custom woven to produce a dual fiber textile bandage. The glass component strongly activated platelets while the specialty rayon agglutinated red blood cells. In comparison with gauze in vitro, the dual fiber textile significantly enhanced the rate of thrombin generation, clot generation as measured by thromboelastography, adhesive protein adsorption and cellular attachment and activation. These results indicate that hemostatic textiles can be designed that mimic gauze in form but surpass gauze in ability to accelerate hemostatic reactions. PMID:19489008

High-quality fiber fabrication in buffered hydrofluoric acid solution with ultrasonic agitation.

PubMed

Zhong, Nianbing; Liao, Qiang; Zhu, Xun; Wang, Yongzhong; Chen, Rong

2013-03-01

An etching method for preparing high-quality fiber-optic sensors using a buffered etchant with ultrasonic agitation is proposed. The effects of etching conditions on the etch rate and surface morphology of the etched fibers are investigated. The effect of surface roughness is discussed on the fibers' optical properties. Linear etching behavior and a smooth fiber surface can be repeatedly obtained by adjusting the ultrasonic power and etchant pH. The fibers' spectral quality is improved as the ratio of the pit depth to size decreases, and the fibers with smooth surfaces are more sensitive to a bacterial suspension than those with rough surfaces.

Adsorption Properties of Lignin-derived Activated Carbon Fibers (LACF)

DOE Office of Scientific and Technical Information (OSTI.GOV)

Contescu, Cristian I.; Gallego, Nidia C.; Thibaud-Erkey, Catherine

The object of this CRADA project between Oak Ridge National Laboratory (ORNL) and United Technologies Research Center (UTRC) is the characterization of lignin-derived activated carbon fibers (LACF) and determination of their adsorption properties for volatile organic compounds (VOC). Carbon fibers from lignin raw materials were manufactured at Oak Ridge National Laboratory (ORNL) using the technology previously developed at ORNL. These fibers were physically activated at ORNL using various activation conditions, and their surface area and pore-size distribution were characterized by gas adsorption. Based on these properties, ORNL did down-select five differently activated LACF materials that were delivered to UTRC formore » measurement of VOC adsorption properties. UTRC used standard techniques based on breakthrough curves to measure and determine the adsorption properties of indoor air pollutants (IAP) - namely formaldehyde and carbon dioxide - and to verify the extent of saturated fiber regenerability by thermal treatments. The results are summarized as follows: (1) ORNL demonstrated that physical activation of lignin-derived carbon fibers can be tailored to obtain LACF with surface areas and pore size distributions matching the properties of activated carbon fibers obtained from more expensive, fossil-fuel precursors; (2) UTRC investigated the LACF potential for use in air cleaning applications currently pursued by UTRC, such as building ventilation, and demonstrated their regenerability for CO2 and formaldehyde, (3) Both partners agree that LACF have potential for possible use in air cleaning applications.« less

The surface properties of carbon fibers and their adhesion to organic polymers

NASA Technical Reports Server (NTRS)

Bascom, W. D.; Drzal, L. T.

1987-01-01

The state of knowledge of the surface properties of carbon fibers is reviewed, with emphasis on fiber/matrix adhesion in carbon fiber reinforced plastics. Subjects treated include carbon fiber structure and chemistry, techniques for the study of the fiber surface, polymer/fiber bond strength and its measurement, variations in polymer properties in the interphase, and the influence of fiber matrix adhesion on composite mechanical properties. Critical issues are summarized and search recommendations are made.

Surface monofunctionalized polymethyl pentene hollow fiber membranes by plasma treatment and hemocompatibility modification for membrane oxygenators

NASA Astrophysics Data System (ADS)

Huang, Xin; Wang, Weiping; Zheng, Zhi; Fan, Wenling; Mao, Chun; Shi, Jialiang; Li, Lei

2016-01-01

The hemocompatibility of polymethyl pentene (PMP) hollow fiber membranes (HFMs) was improved through surface modification for membrane oxygenator applications. The modification was performed stepwise with the following: (1) oxygen plasma treatment, (2) functionalization of monosort hydroxyl groups through NaBH4 reduction, and (3) grafting 2-methacryloyloxyethyl phosphorylcholine (MPC) or heparin. SEM, ATR-FTIR, and XPS analyses were conducted to confirm successful grafting during the modification. The hemocompatibility of PMP HFMs was analyzed and compared through protein adsorption, platelet adhesion, and coagulation tests. Pure CO2 and O2 permeation rates, as well as in vitro gas exchange rates, were determined to evaluate the mass transfer properties of PMP HFMs. SEM results showed that different nanofibril topographies were introduced on the HFM surface. ATR-FTIR and XPS spectra indicated the presence of functionalization of monosort hydroxyl group and the grafting of MPC and heparin. Hemocompatibility evaluation results showed that the modified PMP HFMs presented optimal hemocompatibility compared with pristine HFMs. Gas permeation results revealed that gas permeation flux increased in the modified HFMs because of dense surface etching during the plasma treatment. The results of in vitro gas exchange rates showed that all modified PMP HFMs presented decreased gas exchange rates because of potential surface fluid wetting. The proposed strategy exhibits a potential for fabricating membrane oxygenators for biomedical applications to prevent coagulation formation and alter plasma-induced surface topology and composition.

Sensing surface morphology of biofibers by decorating spider silk and cellulosic filaments with nematic microdroplets.

PubMed

Aguirre, Luis E; de Oliveira, Alexandre; Seč, David; Čopar, Simon; Almeida, Pedro L; Ravnik, Miha; Godinho, Maria Helena; Žumer, Slobodan

2016-02-02

Probing the surface morphology of microthin fibers such as naturally occurring biofibers is essential for understanding their structural properties, biological function, and mechanical performance. The state-of-the-art methods for studying the surfaces of biofibers are atomic force microscopy imaging and scanning electron microscopy, which well characterize surface geometry of the fibers but provide little information on the local interaction potential of the fibers with the surrounding material. In contrast, complex nematic fluids respond very well to external fields and change their optical properties upon such stimuli. Here we demonstrate that liquid crystal droplets deposited on microthin biofibers--including spider silk and cellulosic fibers--reveal characteristics of the fibers' surface, performing as simple but sensitive surface sensors. By combining experiments and numerical modeling, different types of fibers are identified through the fiber-to-nematic droplet interactions, including perpendicular and axial or helicoidal planar molecular alignment. Spider silks align nematic molecules parallel to fibers or perpendicular to them, whereas cellulose aligns the molecules unidirectionally or helicoidally along the fibers, indicating notably different surface interactions. The nematic droplets as sensors thus directly reveal chirality of cellulosic fibers. Different fiber entanglements can be identified by depositing droplets exactly at the fiber crossings. More generally, the presented method can be used as a simple but powerful approach for probing the surface properties of small-size bioobjects, opening a route to their precise characterization.

Tensile strength of glass fiber posts submitted to different surface treatments.

PubMed

Faria, Maria Isabel A; Gomes, Érica Alves; Messias, Danielle Cristine; Silva Filho, João Manoel; Souza Filho, Celso Bernardo; Paulino, Silvana Maria

2013-01-01

The aim of this in vitro study was to evaluate the tensile strength of glass fiber posts submitted to different surface treatments. Forty-eight maxillary canines had their crowns sectioned and root canals endodontically treated. The roots were embedded in acrylic resin and distributed into 3 groups according to the surface treatment: Group I: the posts were treated with silane agent for 30 s and adhesive; Group II: the posts were cleaned with alcohol before treatment with silane agent and adhesive; Group III: the posts were submitted to conditioning with 37% phosphoric acid for 30 s before treatment with silane agent and adhesive. Each group was divided into 2 subgroups for adhesive polymerization or not before insertion into the canal: A - adhesive was not light cured and B - adhesive was light cured. All posts were cemented with Panavia F and the samples were subjected to tensile strength test in a universal testing machine at crosshead speed of 1 mm/min. Data were submitted to one-way ANOVA and Tukey's test at 5% significance level. There was statistically significant difference (p<0.01) only between group GIII-B and groups GI-A and GI-B. No significant difference was found among the other groups (p>0.05). It was concluded that the products used for cleaning the posts influenced the retention regardless of adhesive light curing.

Synthesis of porous inorganic hollow fibers without harmful solvents.

PubMed

Shukla, Sushumna; de Wit, Patrick; Luiten-Olieman, Mieke W J; Kappert, Emiel J; Nijmeijer, Arian; Benes, Nieck E

2015-01-01

A route for the fabrication of porous inorganic hollow fibers with high surface-area-to-volume ratio that avoids harmful solvents is presented. The approach is based on bio-ionic gelation of an aqueous mixture of inorganic particles and sodium alginate during wet spinning. In a subsequent thermal treatment, the bio-organic material is removed and the inorganic particles are sintered. The method is applicable to the fabrication of various inorganic fibers, including metals and ceramics. The route completely avoids the use of organic solvents, such as N-methyl-2-pyrrolidone, and additives associated with the currently used fiber fabrication methods. In addition, it inherently avoids the manifestation of so-called macro voids and allows the facile incorporation of additional metal oxides in the inorganic hollow fibers. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Carbide coated fibers in graphite-aluminum composites

NASA Technical Reports Server (NTRS)

Imprescia, R. J.; Levinson, L. S.; Reiswig, R. D.; Wallace, T. C.; Williams, J. M.

1975-01-01

The NASA-supported program at the Los Alamos Scientific Laboratory (LASL) to develop carbon fiber-aluminum matrix composites is described. Chemical vapor deposition (CVD) was used to uniformly deposit thin, smooth, continuous coats of TiC on the fibers of graphite tows. Wet chemical coating of fibers, followed by high-temperature treatment, was also used, but showed little promise as an alternative coating method. Strength measurements on CVD coated fiber tows showed that thin carbide coats can add to fiber strength. The ability of aluminum alloys to wet TiC was successfully demonstrated using TiC-coated graphite surfaces. Pressure-infiltration of TiC- and ZrC-coated fiber tows with aluminum alloys was only partially successful. Experiments were performed to evaluate the effectiveness of carbide coats on carbon as barriers to prevent reaction between alluminum alloys and carbon. Initial results indicate that composites of aluminum and carbide-coated graphite are stable for long periods of time at temperatures near the alloy solidus.

Improving the mechanical performance of wood fiber reinforced bio-based polyurethane foam

NASA Astrophysics Data System (ADS)

Chang, Li-Chi

Because of the environmental impact of fossil fuel consumption, soybean-based polyurethane (PU) foam has been developed as an alternative to be used as the core in structural insulated panels (SIPs). Wood fibers can be added to enhance the resistance of foam against bending and buckling in compression. The goal of this work is to study the effect of three modifications: fiber surface treatment, catalyst choice, and mixing method on the compression performance of wood fiber-reinforced PU foam. Foams were made with a free-rising process. The compression performance of the foams was measured and the foams were characterized using Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and X-ray computed tomography (CT). The foam reinforced with alkali-treated fibers had improved compression performance. The foams made with various catalysts shared similar performance. The foam made using a mechanical stirrer contained well-dispersed fibers but the reinforcing capability of the fibers was reduced.

Carbon nanotubes/carbon fiber hybrid material: a super support material for sludge biofilms.

PubMed

Liu, Qijie; Dai, Guangze; Bao, Yanling

2017-07-16

Carbon fiber (CF) is widely used as a sludge biofilm support material for wastewater treatment. Carbon nanotubes/carbon fiber (CNTs/CF) hybrid material was prepared by ultrasonically assisted electrophoretic deposition (EPD). CF supports (CF without handling, CF oxidized by nitric acid, CNTs/CF hybrid material) were evaluated by sludge immobilization tests, bacterial cell adsorption tests and Derjaguin -Landau -Verwey -Overbeek (DLVO) theory. We found that the CNTs/CF hybrid material has a high capacity for adsorbing activated sludge, nitrifying bacterial sludge and pure strains (Escherichia coli and Staphylococcus aureus). CNTs deposited on CF surface easily wound around the curved surface of bacterial cell which resulted in capturing more bacterial cells. DLVO theory indicated the lowest total interaction energy of CNTs/CF hybrid material, which resulted in the highest bacteria cell adsorption velocity. Experiments and DLVO theory results proved that CNTs/CF hybrid material is a super support material for sludge biofilms.

Coatings for Graphite Fibers

NASA Technical Reports Server (NTRS)

Galasso, F. S.; Scola, D. A.; Veltri, R. D.

1980-01-01

Several approaches for applying high resistance coatings continuously to graphite yarn were investigated. Two of the most promising approaches involved (1) chemically vapor depositing (CVD) SiC coatings on the surface of the fiber followed by oxidation, and (2) drawing the graphite yarn through an organo-silicone solution followed by heat treatments. In both methods, coated fibers were obtained which exhibited increased electrical resistances over untreated fibers and which were not degraded. This work was conducted in a previous program. In this program, the continuous CVD SiC coating process used on HTS fiber was extended to the coating of HMS, Celion 6000, Celion 12000 and T-300 graphite fiber. Electrical resistances three order of magnitude greater than the uncoated fiber were measured with no significant degradation of the fiber strength. Graphite fibers coated with CVD Si3N4 and BN had resistances greater than 10(exp 6) ohm/cm. Lower pyrolysis temperatures were used in preparing the silica-like coatings also resulting in resistances as high as three orders of magnitude higher than the uncoated fiber. The epoxy matrix composites prepared using these coated fibers had low shear strengths indicating that the coatings were weak.

Composites with improved fiber-resin interfacial adhesion

NASA Technical Reports Server (NTRS)

Cizmecioglu, Muzaffer (Inventor)

1989-01-01

The adhesion of fiber reinforcement such as high modulus graphite to a matrix resin such as polycarbonate is greatly enhanced by applying a very thin layer, suitably from 50 Angstroms to below 1000 Angstroms, to the surface of the fiber such as by immersing the fiber in a dilute solution of the matrix resin in a volatile solvent followed by draining to remove excess solution and air drying to remove the solvent. The thin layer wets the fiber surface. The very dilute solution of matrix resin is able to impregnate multifilament fibers and the solution evenly flows onto the surface of the fibers. A thin uniform layer is formed on the surface of the fiber after removal of the solvent. The matrix resin coated fiber is completely wetted by the matrix resin during formation of the composite. Increased adhesion of the resin to the fibers is observed at fracture. At least 65 percent of the surface of the graphite fiber is covered with polycarbonate resin at fracture whereas uncoated fibers have very little matrix resin adhering to their surfaces at fracture and epoxy sized graphite fibers exhibit only slightly higher coverage with matrix resin at fracture. Flexural modulus of the composite containing matrix resin coated fibers is increased by 50 percent and flexural strength by 37 percent as compared to composites made with unsized fibers.

Surface modification and characterization of aramid fibers with hybrid coating

NASA Astrophysics Data System (ADS)

Chen, Jianrui; Zhu, Yaofeng; Ni, Qingqing; Fu, Yaqin; Fu, Xiang

2014-12-01

Aramid fibers were modified through solution dip-coating and interfacial in situ polymerization using a newly synthesized SiO2/shape memory polyurethane (SiO2/SMPU) hybrid. Fourier transform infrared and X-ray photoelectron spectroscopy indicated that the synthesized SiO2/SMPU hybrid successfully coated the fiber surface. The surface morphology of the aramid fibers and the single fiber tensile strength and interfacial shear strength (IFSS) of the composites were determined. The IFSS of the fiber coated with the hybrid improved by 45%, which benefited from a special "pizza-like" structure on the fiber surface.

Modification of carbon fiber surfaces via grafting with Meldrum's acid

NASA Astrophysics Data System (ADS)

Cuiqin, Fang; Jinxian, Wu; Julin, Wang; Tao, Zhang

2015-11-01

The mechanism of Meldrum's acid modifying carbon fiber surfaces was investigated in this work. The existing carbonyl groups of carbon fibers were grafted with Meldrum's acid to create carboxylic functionalized surfaces. The surface functionalization effect was detected with X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), atomic force microscopy (AFM), and thermogravimetric analysis (TGA). The XPS results showed that the relative content of carboxylic groups on carbon fiber surfaces was increased from initial 1.41% to 7.84%, however, that of carbonyl groups was decreased from 23.11% to 13.28% after grafting reaction. The SEM, AFM and TGA results indicated that the surfaces of carbon fibers neither etched nor generated coating. The tensile strength of carbon fibers was preserved after grafting reaction according to single fiber tensile strength tests. The fibers were well combined with matrix and the maximal interlaminar shear strength (ILSS) of carbon fiber/epoxy resin composites was sharply increased approximately 74% after functionalization. The effects of acetic acid and sonication on the degree of the surface functionalization were also studied.

Surface modification of aramid fibers by bio-inspired poly(dopamine) and epoxy functionalized silane grafting.

PubMed

Sa, Rina; Yan, Yan; Wei, Zhenhai; Zhang, Liqun; Wang, Wencai; Tian, Ming

2014-12-10

A novel biomimetic surface modification method for meta-aramid (MPIA) fibers and the improvement on adhesion with rubber matrix was demonstrated. Inspired by the composition of adhesive proteins in mussels, we used dopamine (DOPA) self-polymerization to form thin, surface-adherent poly(dopamine) (PDA) films onto the surface of MPIA fibers simply by immersing MPIA fibers in a dopamine solution at room temperature. An epoxy functionalized silane (KH560) grafting was then carried out on the surface of the poly(dopamine)-coated MPIA, either by a "one-step" or "two-step" method, to introduce an epoxy group onto the MPIA fiber surface. The surface composition and microstructure of the modified MPIA was characterized by X-ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), scanning electron microscopy (SEM), and thermogravimetric analysis (TGA). The results indicated successful grafting of KH560 on the PDA-coated MPIA surface. A single-fiber pull-out test was applied to evaluate the adhesion of MPIA fibers with the rubber matrix. Compared with the untreated MPIA fibers, the adhesion strength between the modified MPIA fibers by "one step" method with rubber matrix has an increase of 62.5%.

Novel procedure to enhance PLA surface properties by chitosan irreversible immobilization

NASA Astrophysics Data System (ADS)

Stoleru, Elena; Dumitriu, Raluca Petronela; Munteanu, Bogdanel Silvestru; Zaharescu, Traian; Tănase, Elisabeta Elena; Mitelut, Amalia; Ailiesei, Gabriela-Liliana; Vasile, Cornelia

2016-03-01

A novel two step procedure was applied for poly(lactic acid) (PLA) functionalization consisting in the exposure to cold radiofrequency plasma in nitrogen atmosphere or to gamma irradiation followed by ;grafting to; of a chitosan layer using carbodiimide chemistry. The adhesion and stability of the deposited surface layer was assured by plasma/gamma irradiation treatment while the chitosan layer offers antifungal/antibacterial/antioxidant activities. Chitosan with different viscosities/deacetylation degree was deposited by electrospinning or immersion methods. Correlations between rheological behavior of chitosan solutions and chitosan layer deposition conditions are made. The PLA surface properties were investigated by water contact angle measurements, ATR-FTIR spectroscopy, AFM, chemiluminiscence, etc. It has been established that the surface roughness increases direct proportional with cold plasma duration and gamma irradiation dose and further increases by chitosan coating which at its turn depends on chitosan characteristics (viscosity and deacetylation degree) and method of deposition. Nano-fibers with relatively homogeneous and reproducible features are obtained by electrospinning of highly viscous chitosan while with the other two types of chitosan both microparticles and nano-fibers are formed. The chitosan coating obtained by immersion is more homogenous and compact and has a better antibacterial activity than the electrospun layer as fiber meshes.

Surface chemical analysis and ab initio investigations of CsI coated C fiber cathodes for high power microwave sources

NASA Astrophysics Data System (ADS)

Vlahos, Vasilios; Morgan, Dane; LaCour, Matthew; Golby, Ken; Shiffler, Don; Booske, John H.

2010-02-01

CsI coated C fiber cathodes are promising electron emitters utilized in field emission applications. Ab initio calculations, in conjunction with experimental investigations on CsI-spray coated C fiber cathodes, were performed in order to better understand the origin of the low turn-on E-field obtained, as compared to uncoated C fibers. One possible mechanism for lowering the turn-on E-field is surface dipole layers reducing the work function. Ab initio modeling revealed that surface monolayers of Cs, CsI, Cs2O, and CsO are all capable of producing low work function C fiber cathodes (1 eV<Φ<1.5 eV), yielding a reduction in the turn-on E-field by as much as ten times, when compared to the bare fiber. Although a CsI-containing aqueous solution is spray deposited on the C fiber surface, energy dispersive x-ray spectroscopy and scanning auger microscopy measurements show coabsorption of Cs and I into the fiber interior and Cs and O on the fiber surface, with no surface I. It is therefore proposed that a cesium oxide (CsxOy) surface coating is responsible, at least in part, for the low turn E-field and superior emission characteristics of this type of fiber cathode. This CsxOy layer could be formed during preconditioning heating. CsxOy surface layers cannot only lower the fiber work function by the formation of surface dipoles (if they are thin enough) but may also enhance surface emission through their ability to emit secondary electrons due to a process of grazing electron impact. These multiple electron emission processes may explain the reported 10-100 fold reduction in the turn-on E-field of coated C fibers.

Surface modifications induced by pulsed-laser texturing—Influence of laser impact on the surface properties

NASA Astrophysics Data System (ADS)

Costil, S.; Lamraoui, A.; Langlade, C.; Heintz, O.; Oltra, R.

2014-01-01

Laser cleaning technology provides a safe, environmentally friendly and very cost effective way to improve cleaning and surface preparation of metallic materials. Compared with efficient cleaning processes, it can avoid the disadvantages of ductile materials prepared by conventional technologies (cracks induced by sand-blasting for example) and treat only some selected areas (due to the optical fibers). By this way, laser technology could have several advantages and expand the range of thermal spraying. Moreover, new generations of lasers (fiber laser, disc laser) allow the development of new methods. Besides a significant bulk reduction, no maintenance, low operating cost, laser fibers can introduce alternative treatments. Combining a short-pulse laser with a scanner allows new applications in terms of surface preparation. By multiplying impacts using scanning laser, it is possible to shape the substrate surface to improve the coating adhesion as well as the mechanical behaviour. In addition, during the interactions of the laser beam with metallic surfaces, several modifications can be induced and particularly thermal effects. Indeed, under ambient conditions, a limited oxidation of the clean surface can occur. This phenomenon has been investigated in detail for silicon but few works have been reported concerning metallic materials. This paper aims at studying the surface modifications induced on aluminium alloy substrates after laser texturing. After morphological observations (SEM), a deeper surface analysis will be performed using XPS (X-ray photoelectron spectroscopy) measures and microhardness testing.

Effect of post-space treatment on retention of fiber posts in different root regions using two self-etching systems.

PubMed

Zhang, Ling; Huang, Li; Xiong, Yu; Fang, Ming; Chen, Ji-Hua; Ferrari, Marco

2008-06-01

The effect of post-space treatment on the retention of fiber posts in different root regions was evaluated using two self-etching systems. Post spaces were prepared in extracted premolars and then the root canals were subjected to one of the following post-space treatments: (i) water irrigation (control); (ii) etching with 35% phosphoric acid for 30 s; (iii) irrigation with 17% EDTA followed by 5.25% sodium hypochlorite (NaOCl); and (iv) ultrasonic agitation associated with 17% EDTA and 5.25% NaOCl irrigating solutions. The dentin surfaces were examined under scanning electron microscopy (SEM) after different post-space treatments. Fiber posts were then luted in the treated roots using resin cement with either Clearfil SE Bond or Clearfil DC Bond, and the thin-slice push-out test was performed. Scanning electron microscopy showed that all the post-space treatments tested were effective in removal of the smear layer of debris, or sealer/gutta-percha remnants, on the root canal. The apical push-out strength was affected by post-space treatment. Both 35% phosphoric acid etching and ultrasonic agitation in combination with EDTA/NaOCl irrigation improved the apical push-out strength of the fiber post, regardless of the type of self-etching system. A solo irrigation with an EDTA/NaOCl solution resulted in a lower apical push-out strength compared with the other two experimental groups.

Immobilized enzymes in blood plasma exchangers via radiation grafting

NASA Astrophysics Data System (ADS)

Gombotz, Wayne; Hoffman, Allan; Schmer, Gottfried; Uenoyama, Satoshi

The enzyme asparaginase was immobilized onto a porous hollow polypropylene (PP) fiber blood plasma exchange device for the treatment of acute lymphocytic leukemia. The devices were first radiation grafted with polymethacrylic acid (poly(MAAc)). This introduces carboxyl groups onto the surface of the fibers. Several variables were studied in the grafting reaction including the effects of solvent type and monomer concentration. The carboxyl groups were activated with N-hydroxy succinimide (NHS) using carbodiimide chemistry. Asparaginase was then covalently immobilized on the activated surfaces. Quantitative relationships were found relating the percent graft to the amount of immobilized enzyme which was active. The enzyme reactor was tested both in vitro and in vivo using a sheep as an animal model.

Durability of Cement Composites Reinforced with Sisal Fiber

NASA Astrophysics Data System (ADS)

Wei, Jianqiang

This dissertation focuses mainly on investigating the aging mechanisms and degradation kinetics of sisal fiber, as well as the approaches to mitigate its degradation in the matrix of cement composites. In contrast to previous works reported in the literature, a novel approach is proposed in this study to directly determine the fiber's degradation rate by separately studying the composition changes, mechanical and physical properties of the embedded sisal fibers. Cement hydration is presented to be a crucial factor in understanding fiber degradation behavior. The degradation mechanisms of natural fiber consist of mineralization of cell walls, alkali hydrolysis of lignin and hemicellulose, as well as the cellulose decomposition which includes stripping of cellulose microfibrils and alkaline hydrolysis of amorphous regions in cellulose chains. Two mineralization mechanisms, CH-mineralization and self-mineralization, are proposed. The degradation kinetics of sisal fiber in the cement matrix are also analyzed and a model to predict the degradation rate of cellulose for natural fiber embedded in cement is outlined. The results indicate that the time needed to completely degrade the cellulose in the matrix with cement replacement by 30wt.% metakaolin is 13 times longer than that in pure cement. A novel and scientific method is presented to determine accelerated aging conditions, and to evaluating sisal fiber's degradation rate and durability of natural fiber-reinforced cement composites. Among the static aggressive environments, the most effective approach for accelerating the degradation of natural fiber in cement composites is to soak the samples or change the humidity at 70 °C and higher temperature. However, the dynamic wetting and drying cycling treatment has a more accelerating effect on the alkali hydrolysis of fiber's amorphous components evidenced by the highest crystallinity indices, minimum content of holocellulose, and lowest tensile strength. Based on the understanding of degradation mechanisms, two approaches are proposed to mitigate the degradation of sisal fiber in the cement matrix. In order to relieve the aggressive environment of hydrated cement, cement substitution by a combination of metakaolin and nanoclay, and a combination of rice husk ash and limestone are studied. Both metakaolin and nanoclay significantly optimize the cement hydration, while the combination of these two supplementary cementitious materials validates their complementary and synergistic effect at different stages of aging. The presented approaches effectively reduce the calcium hydroxide content and the alkalinity of the pore solution, thereby mitigating the fiber degradation and improving both the initial mechanical properties and durability of the fiber-cement composites. The role of rice husk ash in cement modification is mainly as the active cementitious supplementary material. In order to improve the degradation resistance of sisal fiber itself, two novel, simple, and economical pretreatments of the fibers (thermal and sodium carbonate treatment) are investigated. Both thermal treatment and Na 2CO3 treatment effectively improve the durability of sisal fiber-reinforced concrete. The thermal treatment achieves improvement of cellulose's crystallization, which ensures the initial strength and improved durability of sisal fiber. A layer consisting of calcium carbonate sediments, which protects the internals of a fiber from the strong alkali pore solution, is formed and filled in pits and cavities on the Na2CO3 treated sisal fiber's surface.

High temperature heat source generation with quasi-continuous wave semiconductor lasers at power levels of 6 W for medical use.

PubMed

Fujimoto, Takahiro; Imai, Yusuke; Tei, Kazuyoku; Ito, Shinobu; Kanazawa, Hideko; Yamaguchi, Shigeru

2014-01-01

We investigate a technology to create a high temperature heat source on the tip surface of the glass fiber proposed for medical surgery applications. Using 4 to 6 W power level semiconductor lasers at a wavelength of 980 nm, a laser coupled fiber tip was preprocessed to contain a certain amount of titanium oxide powder with a depth of 100 μm from the tip surface so that the irradiated low laser energy could be perfectly absorbed to be transferred to thermal energy. Thus, the laser treatment can be performed without suffering from any optical characteristic of the material. A semiconductor laser was operated quasi-continuous wave mode pulse time duration of 180 ms and >95% of the laser energy was converted to thermal energy in the fiber tip. Based on two-color thermometry, by using a gated optical multichannel analyzer with a 0.25 m spectrometer in visible wavelength region, the temperature of the fiber tip was analyzed. The temperature of the heat source was measured to be in excess 3100 K.

Evaluation of Additive Manufacturing for Composite Part Molds

DOE Office of Scientific and Technical Information (OSTI.GOV)

Duty, Chad E.; Springfield, Robert M.

2015-02-01

The ORNL Manufacturing Demonstration Facility (MDF) collaborated with Tru-Design to test the quality and durability of molds used for making fiber reinforced composites using additive manufacturing. The partners developed surface treatment techniques including epoxy coatings and machining to improve the quality of the surface finish. Test samples made using the printed and surface finished molds demonstrated life spans suitable for one-of-a-kind and low-volume applications, meeting the project objective.

Surface decoration of short-cut polyimide fibers with multi-walled carbon nanotubes and their application for reinforcement of lightweight PC/ABS composites

NASA Astrophysics Data System (ADS)

Zhang, Le; Han, Enlin; Wu, Yulun; Wang, Xiaodong; Wu, Dezhen

2018-06-01

The surface decoration of short-cut polyimide (PI) fibers with multi-walled carbon nanotubes (MWCNTs) was performed by fabricating a polydopamine (PDA) coating layer on the fiber surface and then immobilizing MWCNTs onto the coating layer via covalent bonding. This successful surface decoration was confirmed by scanning electron microscopy, X-ray photoelectron spectroscopy, Fourier-transform infrared microscopy and static water contact angle. The application of the surface-decorated PI fibers as reinforcing fibers for reinforcement of polycarbonate (PC)/acrylonitrile-butadiene-styrene copolymer (ABS) alloy was investigated, which indicated that the MWCNTs-decorated PI fibers not only could effectively reinforce the PC/ABS alloy but also generated a significant lightweighting effect on the resulting composites. The maximum mechanical properties were achieved for the composites at a fiber content of 20 wt.% and a fiber length of 3 mm. This significant reinforcement effect is attributed to the enhancement of interaction bonding strength between the fibers and matrix as a result of the surface decoration of PI fibers with MWCNTs. The morphological investigation suggested that fiber rupture was the major energy dissipation mechanism in the tensile and impact failures, whereas fiber debonding and pullout were partly involved in the fracture energy dissipation. In addition, the presence of surface-decorated PI fibers slightly enhanced the thermal stability and load bearing capability of composites. This work can provide a type of high-performance lightweight composite material for automobile and aviation industries.

Conductive cable fibers with insulating surface prepared by co-axial electrospinning of multi-walled nanotubes and cellulose

PubMed Central

Miyauchi, Minoru; Miao, Jianjun; Simmons, Trevor J.; Lee, Jong-Won; Doherty, Thomas V.; Dordick, Jonathan S.; Linhardt, Robert J.

2010-01-01

A core-sheath of multi-walled carbon nanotube (MWNT)-cellulose fibers of diameters from several hundreds nm to several µm were prepared by co-axial electrospinning from a non-valatile, non-flammable ionic liquid (IL) solvent, 1-methyl-3-methylimidazolium acetate ([EMIM][Ac]). MWNTs were dispersed in IL to form a gel solution. This gel core solution was electrospun surrounded by a sheath solution of cellulose disolved in the same IL. Electrospun fibers were collected in a coagulation bath containing ethanol-water to completely remove the IL and dried to form a core-sheath MWNT-cellulose fibers having a cable structure with a conductive core and insulating sheath. Enzymatic treatment of a portion of a mat of these fibers with cellulase selectively removed the cellulose sheath exposing the MWNT core for connection to an electrode. These MWNT-cellulose fiber mats demonstrated excellent conductivity due to a conductive pathway of bundleled MWNTs. Fiber mat conductivity increased with increasing ratio of MWNT in the fibers with a maximum conductivity of 10.7 S/m obtained at 45 wt% MWNT loading. PMID:20690644

Conductive cable fibers with insulating surface prepared by coaxial electrospinning of multiwalled nanotubes and cellulose.

PubMed

Miyauchi, Minoru; Miao, Jianjun; Simmons, Trevor J; Lee, Jong-Won; Doherty, Thomas V; Dordick, Jonathan S; Linhardt, Robert J

2010-09-13

Core-sheath multiwalled carbon nanotube (MWNT)-cellulose fibers of diameters from several hundreds of nanometers to several micrometers were prepared by coaxial electrospinning from a nonvolatile, nonflammable ionic liquid (IL) solvent, 1-methyl-3-methylimidazolium acetate ([EMIM][Ac]). MWNTs were dispersed in IL to form a gel solution. This gel core solution was electrospun surrounded by a sheath solution of cellulose dissolved in the same IL. Electrospun fibers were collected in a coagulation bath containing ethanol-water to remove the IL completely and dried to form core-sheath MWNT-cellulose fibers having a cable structure with a conductive core and insulating sheath. Enzymatic treatment of a portion of a mat of these fibers with cellulase selectively removed the cellulose sheath exposing the MWNT core for connection to an electrode. These MWNT-cellulose fiber mats demonstrated excellent conductivity because of a conductive pathway of bundled MWNTs. Fiber mat conductivity increased with increasing ratio of MWNT in the fibers with a maximum conductivity of 10.7 S/m obtained at 45 wt % MWNT loading.

Electrospinning and electrospraying of silicon oxycarbide-derived nanoporous carbon for supercapacitor electrodes

NASA Astrophysics Data System (ADS)

Tolosa, Aura; Krüner, Benjamin; Jäckel, Nicolas; Aslan, Mesut; Vakifahmetoglu, Cekdar; Presser, Volker

2016-05-01

In this study, carbide-derived carbon fibers from silicon oxycarbide precursor were synthesized by electrospinning of a commercially available silicone resin without adding a carrier polymer for the electrospinning process. The electrospun fibers were pyrolyzed yielding SiOC. Modifying the synthesis procedure, we were also able to obtain electrosprayed SiOC beads instead of fibers. After chlorine treatment, nanoporous carbon with a specific surface area of up to 2394 m2 g-1 was obtained (3089 m2 g-1 BET). Electrochemical characterization of the SiOC-CDC either as free-standing fiber mat electrodes or polymer-bound bead films was performed in 1 M tetraethylammonium tetrafluoroborate in acetonitrile (TEA-BF4 in ACN). The electrospun fibers presented a high gravimetric capacitance of 135 F g-1 at 10 mV s-1 and a very high power handling, maintaining 63% of the capacitance at 100 A g-1. Comparative data of SiOC-CDC beads and fibers show enhanced power handling for fiber mats only when the fiber network is intact, that is, a lowered performance was observed when using crushed mats that employ polymer binder.

Effect of addition of plants-derived polyamide 11 elastomer on the mechanical and tribological properties of hemp fiber reinforced polyamide 1010 composites

NASA Astrophysics Data System (ADS)

Mukaida, Jun; Nishitani, Yosuke; Kitano, Takeshi

2015-05-01

For the purpose of developing the new engineering materials such as structural materials and tribomaterials based on all plants-derived materials, the effect of the addition of plant-derived polyamide 11 Elastomer (PA11E) on the mechanical and tribological properties of hemp fiber(HF) reinforced polyamide 1010 (HF/PA1010) composites was investigated. PA1010 and PA11E (except the polyether groups used as soft segment) were made from plant-derived castor oil. Hemp fiber was surface-treated by two types of treatment: alkali treatment by NaOH solution and surface treatment by ureido silane coupling agent. HF/PA1010/PA11E ternary composites were extruded by a twin screw extruder and injection-molded. Their mechanical properties such as tensile, bending, Izod impact and tribological properties by ring-on-plate type sliding wear testing were evaluated. The effect of the addition of PA11E on the mechanical and tribological properties of HF/PA1010 composite differed for each property. Izod impact strength and specific wear rate improved with the addition of PA11E although tensile strength, modulus, and friction coefficient decreased with PA11E. It follows from these results that it may be possible to develop the new engineering materials with sufficient balance between mechanical and tribological properties.

Influence of additional coupling agent on the mechanical properties of polyester–agave cantala roxb based composites

DOE Office of Scientific and Technical Information (OSTI.GOV)

Ubaidillah, E-mail: ubaidillah@uns.ac.id; Malaysia-Japan International Institute of Technology, Universiti Teknologi Malaysia, Jalan Sultan Yahya Petra, Kuala Lumpur; Raharjo, Wijang W.

The mechanical and morphological properties of the unsaturated polyester resins (UPRs)-agave cantala roxb based composite are investigated in this paper. The cantala fiber woven in 3D angle interlock was utilized as the composite reinforcement. Surface grafting of the cantala fiber through chemical treatment was performed by introducing silane coupling agent to improving the compatibility with the polymer matrix. The fabrication of the composite specimens was conducted using vacuum bagging technique. The effect of additional coupling agent to the morphological appearance of surface fracture was observed using scanning electron microscopy. Meanwhile, the influence of additional silane to the mechanical properties wasmore » examined using tensile, bending and impact test. The photograph of surface fracture on the treated specimens showed the residual matrix left on the fibers in which the phenomenon was not found in the untreated specimens. Based on mechanical tests, the treated specimens were successfully increased their mechanical properties by 55%, 9.67%, and 92.4% for tensile strength, flexural strength, and impact strength, respectively, at 1.5% silane coupling agent.« less

Sealing Penetrating Eye Injuries With Photoactivated Bonding

DTIC Science & Technology

2013-09-01

penetrating eye injuries. Scope: To establish, in ex vitro and in vivo animal models, the treatment parameters for sealing corneal and scleral...cornea surface was compared to that produced by our conventional, bare fiber system using ex vivo rabbit eyes and the standard treatment protocol...Identified the PTB treatment parameters that produce strong bonding of an amnion patch over corneal wounds in ex vivo rabbit eyes . • Determined that a

Improvement of the mode II interface fracture toughness of glass fiber reinforced plastics/aluminum laminates through vapor grown carbon fiber interleaves.

PubMed

Ning, Huiming; Li, Yuan; Hu, Ning; Cao, Yanping; Yan, Cheng; Azuma, Takesi; Peng, Xianghe; Wu, Liangke; Li, Jinhua; Li, Leilei

2014-06-01

The effects of acid treatment, vapor grown carbon fiber (VGCF) interlayer and the angle, i.e., 0° and 90°, between the rolling stripes of an aluminum (Al) plate and the fiber direction of glass fiber reinforced plastics (GFRP) on the mode II interlaminar mechanical properties of GFRP/Al laminates were investigated. The experimental results of an end notched flexure test demonstrate that the acid treatment and the proper addition of VGCF can effectively improve the critical load and mode II fracture toughness of GFRP/Al laminates. The specimens with acid treatment and 10 g m -2 VGCF addition possess the highest mode II fracture toughness, i.e., 269% and 385% increases in the 0° and 90° specimens, respectively compared to those corresponding pristine ones. Due to the induced anisotropy by the rolling stripes on the aluminum plate, the 90° specimens possess 15.3%-73.6% higher mode II fracture toughness compared to the 0° specimens. The improvement mechanisms were explored by the observation of crack propagation path and fracture surface with optical, laser scanning and scanning electron microscopies. Moreover, finite element analyses were carried out based on the cohesive zone model to verify the experimental fracture toughness and to predict the interface shear strength between the aluminum plates and GFRP laminates.

Improvement of the mode II interface fracture toughness of glass fiber reinforced plastics/aluminum laminates through vapor grown carbon fiber interleaves

PubMed Central

Ning, Huiming; Li, Yuan; Hu, Ning; Cao, Yanping; Yan, Cheng; Azuma, Takesi; Peng, Xianghe; Wu, Liangke; Li, Jinhua; Li, Leilei

2014-01-01

The effects of acid treatment, vapor grown carbon fiber (VGCF) interlayer and the angle, i.e., 0° and 90°, between the rolling stripes of an aluminum (Al) plate and the fiber direction of glass fiber reinforced plastics (GFRP) on the mode II interlaminar mechanical properties of GFRP/Al laminates were investigated. The experimental results of an end notched flexure test demonstrate that the acid treatment and the proper addition of VGCF can effectively improve the critical load and mode II fracture toughness of GFRP/Al laminates. The specimens with acid treatment and 10 g m−2 VGCF addition possess the highest mode II fracture toughness, i.e., 269% and 385% increases in the 0° and 90° specimens, respectively compared to those corresponding pristine ones. Due to the induced anisotropy by the rolling stripes on the aluminum plate, the 90° specimens possess 15.3%–73.6% higher mode II fracture toughness compared to the 0° specimens. The improvement mechanisms were explored by the observation of crack propagation path and fracture surface with optical, laser scanning and scanning electron microscopies. Moreover, finite element analyses were carried out based on the cohesive zone model to verify the experimental fracture toughness and to predict the interface shear strength between the aluminum plates and GFRP laminates. PMID:27877680

Active constrained layer damping of geometrically nonlinear vibrations of functionally graded plates using piezoelectric fiber-reinforced composites

NASA Astrophysics Data System (ADS)

Panda, Satyajit; Ray, M. C.

2008-04-01

In this paper, a geometrically nonlinear dynamic analysis has been presented for functionally graded (FG) plates integrated with a patch of active constrained layer damping (ACLD) treatment and subjected to a temperature field. The constraining layer of the ACLD treatment is considered to be made of the piezoelectric fiber-reinforced composite (PFRC) material. The temperature field is assumed to be spatially uniform over the substrate plate surfaces and varied through the thickness of the host FG plates. The temperature-dependent material properties of the FG substrate plates are assumed to be graded in the thickness direction of the plates according to a power-law distribution while the Poisson's ratio is assumed to be a constant over the domain of the plate. The constrained viscoelastic layer of the ACLD treatment is modeled using the Golla-Hughes-McTavish (GHM) method. Based on the first-order shear deformation theory, a three-dimensional finite element model has been developed to model the open-loop and closed-loop nonlinear dynamics of the overall FG substrate plates under the thermal environment. The analysis suggests the potential use of the ACLD treatment with its constraining layer made of the PFRC material for active control of geometrically nonlinear vibrations of FG plates in the absence or the presence of the temperature gradient across the thickness of the plates. It is found that the ACLD treatment is more effective in controlling the geometrically nonlinear vibrations of FG plates than in controlling their linear vibrations. The analysis also reveals that the ACLD patch is more effective for controlling the nonlinear vibrations of FG plates when it is attached to the softest surface of the FG plates than when it is bonded to the stiffest surface of the plates. The effect of piezoelectric fiber orientation in the active constraining PFRC layer on the damping characteristics of the overall FG plates is also discussed.

Effects of bond primers on bending strength and bonding of glass fibers in fiber-embedded maxillofacial silicone prostheses.

PubMed

Hatamleh, Muhanad M; Watts, David C

2011-02-01

To evaluate the effect of three commonly used bond primers on the bending strength of glass fibers and their bond strength to maxillofacial silicone elastomer after 360 hours of accelerated daylight aging. Eighty specimens were fabricated by embedding resin-impregnated fiber bundles (1.5-mm diameter, 20-mm long) into maxillofacial silicone elastomer M511 (Cosmesil). Twenty fiber bundles served as control and did not receive surface treatment with primers, whereas the remaining 60 fibers were treated with three primers (n = 20): G611 (Principality Medical), A-304 (Factor II), and A-330-Gold (Factor II). Forty specimens were dry stored at room temperature (23 ± 1°C) for 24 hours, and the remaining specimens were aged using an environmental chamber under accelerated exposure to artificial daylight for 360 hours. The aging cycle included continuous exposure to quartz-filtered visible daylight (irradiance 760 W/m(2) ) under an alternating weathering cycle (wet for 18 minutes, dry for 102 minutes). Pull-out tests were performed to evaluate bond strength between fiber bundles and silicone using a universal testing machine at 1 mm/min crosshead speed. A 3-point bending test was performed to evaluate the bending strength of the fiber bundles. One-way Analysis of Variance (ANOVA), Bonferroni post hoc test, and an independent t-test were carried out to detect statistical significances (p < 0.05). Mean (SD) values of maximum pull-out forces (N) before aging for groups: no primer, G611, A-304, A-330-G were: 13.63 (7.45), 20.44 (2.99), 22.06 (6.69), and 57.91 (10.15), respectively. All primers increased bond strength in comparison to control specimens (p < 0.05). Primer A-330-G showed the greatest increase among all primers (p < 0.05); however, bonding degraded after aging (p < 0.05), and pull-out forces were 13.58 (2.61), 6.17 (2.89), 6.95 (2.61), and 11.72 (3.03). Maximum bending strengths of fiber bundles at baseline increased after treatment with primers and light aging in comparison with control specimens (p < 0.05), and were in the range of 917.72 to 1095.25 and 1124.06 to 1596.68 MPa at both baseline and after 360 hours aging (p < 0.05). The use of A-330-G primer in conjunction with silicone Cosmesil M511 produced the greatest bond strength for silicone-glass fiber surfaces at baseline; however, bond strength was significantly degraded after accelerated daylight aging. Treatment with primer and accelerated daylight aging increased bending strength of glass fibers. © 2011 by The American College of Prosthodontists.

Fiber Optic Temperature Sensor Insert for High Temperature Environments

NASA Technical Reports Server (NTRS)

Black, Richard James (Inventor); Costa, Joannes M. (Inventor); Moslehi, Behzad (Inventor); Zarnescu, Livia (Inventor)

2017-01-01

A thermal protection system (TPS) test plug has optical fibers with FBGs embedded in the optical fiber arranged in a helix, an axial fiber, and a combination of the two. Optionally, one of the optical fibers is a sapphire FBG for measurement of the highest temperatures in the TPS plug. The test plug may include an ablating surface and a non-ablating surface, with an engagement surface with threads formed, the threads having a groove for placement of the optical fiber. The test plug may also include an optical connector positioned at the non-ablating surface for protection of the optical fiber during insertion and removal.

Water-wettable polypropylene fibers by facile surface treatment based on soy proteins.

PubMed

Salas, Carlos; Genzer, Jan; Lucia, Lucian A; Hubbe, Martin A; Rojas, Orlando J

2013-07-24

Modification of the wetting behavior of hydrophobic surfaces is essential in a variety of materials, including textiles and membranes that require control of fluid interactions, adhesion, transport processes, sensing, etc. This investigation examines the enhancement of wettability of an important class of textile materials, viz., polypropylene (PP) fibers, by surface adsorption of different proteins from soybeans, including soy flour, isolate,glycinin, and β-conglycinin. Detailed investigations of soy adsorption from aqueous solution (pH 7.4, 25 °C) on polypropylene thin films is carried out using quartz crystal microbalance (QCM) and surface plasmon resonance (SPR). A significant amount of protein adsorbs onto the PP surfaces primarily due to hydrophobic interactions. We establish that adsorption of a cationic surfactant, dioctadecyldimethylammonium bromide (DODA) onto PP surfaces prior to the protein deposition dramatically enhances its adsorption. The adsorption of proteins from native (PBS buffer, pH 7.4, 25 °C) and denatured conditions (PBS buffer, pH 7.4, 95 °C) onto DODA-treated PP leads to a high coverage of the proteins on the PP surface as confirmed by a significant improvement in water wettability. A shift in the contact angle from 128° to completely wettable surfaces (≈0°) is observed and confirmed by imaging experiments conducted with fluorescence tags. Furthermore, the results from wicking tests indicate that hydrophobic PP nonwovens absorb a significant amount of water after protein treatment, i.e., the PP-modified surfaces become completely hydrophilic.

Thermal degradation of the tensile strength of unidirectional boron/aluminum composites

NASA Technical Reports Server (NTRS)

Grimes, H. H.; Lad, R. A.; Maisel, J. E.

1977-01-01

The variation of ultimate tensile strength with thermal treatment of B-Al composite materials and of boron fibers chemically removed from these composites in an attempt to determine the mechanism of the resulting strength degradation was studied. Findings indicate that thermally cycling B-Al represents a more severe condition than equivalent time at temperature. Degradation of composite tensile strength from about 1.3 GN/m squared to as low as 0.34 GN/m squared was observed after 3,000 cycles to 420 C for 203 micrometers B-1100 Al composite. In general, the 1100 Al matrix composites degraded somewhat more than the 6061 matrix material studied. Measurement of fiber strengths confirmed a composite strength loss due to the degradation of fiber strength. Microscopy indicated a highly flawed fiber surface.

Joint Prediction of Longitudinal Development of Cortical Surfaces and White Matter Fibers from Neonatal MRI

PubMed Central

Rekik, Islem; Li, Gang; Yap, Pew-Thian; Chen, Geng; Lin, Weili; Shen, Dinggang

2017-01-01

The human brain can be modeled as multiple interrelated shapes (or a multishape), each for characterizing one aspect of the brain, such as the cortex and white matter pathways. Predicting the developing multishape is a very challenging task due to the contrasting nature of the developmental trajectories of the constituent shapes: smooth for the cortical surface and non-smooth for white matter tracts due to changes such as bifurcation. We recently addressed this problem and proposed an approach for predicting the multishape developmental spatiotemporal trajectories of infant brains based only on neonatal MRI data using a set of geometric, dynamic, and fiber-to-surface connectivity features. In this paper, we propose two key innovations to further improve the prediction of multishape evolution. First, for a more accurate cortical surface prediction, instead of simply relying on one neonatal atlas to guide the prediction of the multishape, we propose to use multiple neonatal atlases to build a spatially heterogeneous atlas using the multidirectional varifold representation. This individualizes the atlas by locally maximizing its similarity to the testing baseline cortical shape for each cortical region, thereby better representing the baseline testing cortical surface, which founds the multishape prediction process. Second, for temporally consistent fiber prediction, we propose to reliably estimate spatiotemporal connectivity features using low-rank tensor completion, thereby capturing the variability and richness of the temporal development of fibers. Experimental results confirm that the proposed variants significantly improve the prediction performance of our original multishape prediction framework for both cortical surfaces and fiber tracts shape at 3, 6, and 9 months of age. Our pioneering model will pave the way for learning how to predict the evolution of anatomical shapes with abnormal changes. Ultimately, devising accurate shape evolution prediction models that can help quantify and predict the severity of a brain disorder as it progresses will be of great aid in individualized treatment planning. PMID:28284800

Joint prediction of longitudinal development of cortical surfaces and white matter fibers from neonatal MRI.

PubMed

Rekik, Islem; Li, Gang; Yap, Pew-Thian; Chen, Geng; Lin, Weili; Shen, Dinggang

2017-05-15

The human brain can be modeled as multiple interrelated shapes (or a multishape), each for characterizing one aspect of the brain, such as the cortex and white matter pathways. Predicting the developing multishape is a very challenging task due to the contrasting nature of the developmental trajectories of the constituent shapes: smooth for the cortical surface and non-smooth for white matter tracts due to changes such as bifurcation. We recently addressed this problem and proposed an approach for predicting the multishape developmental spatiotemporal trajectories of infant brains based only on neonatal MRI data using a set of geometric, dynamic, and fiber-to-surface connectivity features. In this paper, we propose two key innovations to further improve the prediction of multishape evolution. First, for a more accurate cortical surface prediction, instead of simply relying on one neonatal atlas to guide the prediction of the multishape, we propose to use multiple neonatal atlases to build a spatially heterogeneous atlas using the multidirectional varifold representation. This individualizes the atlas by locally maximizing its similarity to the testing baseline cortical shape for each cortical region, thereby better representing the baseline testing cortical surface, which founds the multishape prediction process. Second, for temporally consistent fiber prediction, we propose to reliably estimate spatiotemporal connectivity features using low-rank tensor completion, thereby capturing the variability and richness of the temporal development of fibers. Experimental results confirm that the proposed variants significantly improve the prediction performance of our original multishape prediction framework for both cortical surfaces and fiber tracts shape at 3, 6, and 9 months of age. Our pioneering model will pave the way for learning how to predict the evolution of anatomical shapes with abnormal changes. Ultimately, devising accurate shape evolution prediction models that can help quantify and predict the severity of a brain disorder as it progresses will be of great aid in individualized treatment planning. Copyright © 2017 Elsevier Inc. All rights reserved.

Plasma treatment of fiber facets for increased (de)mating endurance in physical contact fiber connectors

NASA Astrophysics Data System (ADS)

Van Erps, Jürgen; Voss, Kevin; De Witte, Martijn; Radulescu, Radu; Beri, Stefano; Watté, Jan; Thienpont, Hugo

2016-04-01

It is known that cleaving an optical fiber introduces a number of irregularities and defects to the fiber's end-face, such as hackles and shockwaves. These defects can act as failure initiators when stress is applied to the end-face. Given the fiber's small diameter of 125 ffm, a large amount of mechanical stress can be expected to be applied on its end-face during the mating-demating cycle. In addition, a connector in a fiber-to-the-home (FTTH) network can be expected to be mated and demated more than 30 times during its lifetime for purposes such as testing, churning, or provisioning. For this reason, the performance of a connector that displays low optical loss when first installed can dramatically degrade after few mating-demating cycles and catastrophic connector failure due to end-face breakage is likely. We present plasma discharge shaping of cleaved fiber tips to strongly improve the endurance of the fibers to repeated mating-demating cycles. We quantify the dependency of the plasma-induced surface curvature of the fiber tip on the plasma duration and on the position of the fiber tip within the plasma cloud. Finally we present data showing the improved endurance of fibers that are exposed to plasma compared to conventional as-cleaved fibers.

Sensing surface morphology of biofibers by decorating spider silk and cellulosic filaments with nematic microdroplets

PubMed Central

Aguirre, Luis E.; de Oliveira, Alexandre; Seč, David; Čopar, Simon; Almeida, Pedro L.; Ravnik, Miha; Godinho, Maria Helena; Žumer, Slobodan

2016-01-01

Probing the surface morphology of microthin fibers such as naturally occurring biofibers is essential for understanding their structural properties, biological function, and mechanical performance. The state-of-the-art methods for studying the surfaces of biofibers are atomic force microscopy imaging and scanning electron microscopy, which well characterize surface geometry of the fibers but provide little information on the local interaction potential of the fibers with the surrounding material. In contrast, complex nematic fluids respond very well to external fields and change their optical properties upon such stimuli. Here we demonstrate that liquid crystal droplets deposited on microthin biofibers—including spider silk and cellulosic fibers—reveal characteristics of the fibers’ surface, performing as simple but sensitive surface sensors. By combining experiments and numerical modeling, different types of fibers are identified through the fiber-to-nematic droplet interactions, including perpendicular and axial or helicoidal planar molecular alignment. Spider silks align nematic molecules parallel to fibers or perpendicular to them, whereas cellulose aligns the molecules unidirectionally or helicoidally along the fibers, indicating notably different surface interactions. The nematic droplets as sensors thus directly reveal chirality of cellulosic fibers. Different fiber entanglements can be identified by depositing droplets exactly at the fiber crossings. More generally, the presented method can be used as a simple but powerful approach for probing the surface properties of small-size bioobjects, opening a route to their precise characterization. PMID:26768844

Addition of alkali to the hydrothermal-mechanochemical treatment of Eucalyptus enhances its enzymatic saccharification.

PubMed

Ishiguro, Maki; Endo, Takashi

2014-02-01

The effects of alkali on hydrothermal-mechanochemical treatment (hydrothermal treatment combined with wet-milling) were examined with the aim of improving pretreatment of lignocellulosic biomass before enzymatic saccharification. After enzymatic saccharification, the highest glucose yield was obtained by autoclaving at 170°C in the presence of 20% NaOH per substrate weight. The wood fiber was unraveled into finer nanofibers by hydrothermal-mechanochemical treatment, thus increasing the specific surface area of the substrate from 11 to 132m(2)/g. Adding 20% NaOH to the treatment further increased the specific surface area of the already fibrillated substrate by 76% (232m(2)/g) due to lignin removal and ester bond cleavage between lignin and hemicellulose. This increase in specific surface area was closely related to the increase in enzymatic digestibility; therefore, NaOH addition may have enhanced the effect of hydrothermal-mechanochemical treatment. Copyright © 2013 Elsevier Ltd. All rights reserved.

Electron-beam-induced post-grafting polymerization of acrylic acid onto the surface of Kevlar fibers

NASA Astrophysics Data System (ADS)

Xu, Lu; Hu, Jiangtao; Ma, Hongjuan; Wu, Guozhong

2018-04-01

The surface of Kevlar fibers was successfully modified by electron beam (EB)-induced post-grafting of acrylic acid (AA). The generation of radicals in the fibers was confirmed by electron spin resonance (ESR) measurements, and the concentration of radicals was shown to increase as the absorbed dose increased, but decrease with increasing temperature. The influence of the synthesis conditions on the degree of grafting was also investigated. The surface microstructure and chemical composition of the modified Kevlar fibers were characterized by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The SEM images revealed that the surface of the grafted fibers was rougher than those of the pristine and irradiated fibers. XPS analysis confirmed an increase in C(O)OH groups on the surface of the Kevlar fibers, suggesting successful grafting of AA. These results indicate that EB-induced post-grafting polymerization is effective for modifying the surface properties of Kevlar fibers.

Effect of polymer properties and adherend surfaces on adhesion. [titanium, aluminum

NASA Technical Reports Server (NTRS)

Dwight, D. W.; Counts, M. E.; Wightman, J. P.

1975-01-01

The surface properties associated with good adhesive joints were evaluated in terms of application of adhesive bonding in aerospace technology. The physical and chemical nature was determined of Ti and Al adherend surfaces after various surface treatments, and the effects on fracture surfaces of high temperature aging, and variations in amide, anhydride, and solvent during polymer synthesis. The effects were characterized of (1) high temperature during shear strength testing, (2) fiber-reinforced composites as adherends, (3) acid/base nature of adherends, (4) aluminum powder adhesive filler, and (5) bonding pressure.

Processing and characterization of powdered silk micro- and nanofibers by ultrasonication.

PubMed

Wang, Hai-Yan; Chen, Yun-Yun; Zhang, Yu-Qing

2015-03-01

Silk derived from Bombyx mori silkworm cocoons was degummed in an aqueous sodium carbonate solution, and the resulting silk fibroin fibers were placed in an acidic aqueous solution and were treated with ultrasonication to obtain powdered micro- and nanofibers. The morphologies and spectral characteristics of these powdered silk fibers were investigated in detail. The shape, surface and structural features of the powdered fibers were affected by the ultrasonic power and media. Increasing the acidity of the ultrasonic solution and increasing the ultrasonic power increased the fiber breakage speed, resulting in shorter fiber lengths. Powdered microfibers could not be obtained in a formic acid solution, while powdered nanofibers whose diameter below 1μm were obtained in a combined formic acid and hydrochloric acid ultrasonication solution. Observation via SEM and optical microscopy revealed that the microfiber diameters were approximately 5-10μm, and those of the nanofibers were approximately 30-120nm. The analysis of laser sizer showed that the microfiber sizes ranged mainly from 20 to 100μm. FT-IR and XRD spectra demonstrated that the relative amount of β-sheets increased after the ultrasonic treatment. The ε-amino group content on the surface of the micro- and nanofibers increased significantly. These studies provide reliable methods for the preparation of nano-scale silk fibroin fibers by ultrasonication and open new avenues for the development of powdered silk fibers as advanced functional biomaterials. Copyright © 2014 Elsevier B.V. All rights reserved.

SU-E-T-777: Use of Tennis Racket and Air Gap Between the Body and Carbon Fiber Couch for Skin Sparing in Radiation Therapy of Prone Breast

DOE Office of Scientific and Technical Information (OSTI.GOV)

Lief, E

2015-06-15

Purpose: To reduce the skin dose from the carbon fiber couch scatter in radiation treatment of breast cancer in the prone position. If this issue is not addressed, the prone breast touching the solid carbon fiber couch can absorb significant dose to the skin and cause the skin reaction. Methods: 1. Use of “tennis racket” instead of the solid couch. To check this hypothesis, we measured the dose at the depth of 5 mm in solid water phantom placed on the couch, using a Farmer chamber. A plan for a patient with 6MV beams, gantry angles of 113 and 286more » degrees Varian scale was used. It was found that treatment with “tennis racket” instead of the solid carbon fiber couch reduces the surface dose by 5–7%, depending on the beam direction. 2. Use of the air gap between the couch and the body was analyzed using radiochromic film on the surface of the solid water phantom 10 cm thick. Initially the phantom was placed on the couch with the film sandwiched in between. Two fields at the angles of 135 and 315 degrees were used. The measurements were repeated for the air gap of 2 and 5 cm and 6 and 15 MV beams. Results: It was found that a 2-cm gap decreased the surface dose by 3% for a 6 MV beam and by 5.5% for a 15 MV beam. A 5-cm gap reduced the dose by 9% for 6 MV and 13.5% for 15 MV. Conclusion: Use of both methods (combined if possible) can significantly reduce the surface dose in radiation therapy of the prone breast and possible skin reaction. We plan to explore dependence of the dose reduction upon the angle of incidence.« less

Immediate Repair Bond Strength of Fiber-reinforced Composite after Saliva or Water Contamination.

PubMed

Bijelic-Donova, Jasmina; Flett, Andrew; Lassila, Lippo V J; Vallittu, Pekka K

2018-05-31

This in vitro study aimed to evaluate the shear bond strength (SBS) of particulate filler composite (PFC) to saliva- or water-contaminated fiber-reinforced composite (FRC). One type of FRC substrate with semi-interpenetrating polymer matrix (semi-IPN) (everStick C&B) was used in this investigation. A microhybrid PFC (Filtek Z250) substrate served as control. Freshly cured PFC and FRC substrates were first subjected to different contamination and surface cleaning treatments, then the microhybrid PFC restorative material (Filtek Z250) was built up on the substrates in 2-mm increments and light cured. Uncontaminated and saliva- or water-contaminated substrate surfaces were either left untreated or were cleaned via phosphoric acid etching or water spray accompanied with or without adhesive composite application prior applying the adherent PFC material. SBS was evaluated after thermocycling the specimens (6000 cycles, 5°C and 55°C). Three-way ANOVA showed that both the surface contamination and the surface treatment signficantly affected the bond strength (p < 0.05). Saliva contamination reduced the SBS more than did the water contamination. SBS loss after saliva contamination was 73.7% and 31.3% for PFC and FRC, respectively. After water contamination, SBS loss was 17.2% and 13.3% for PFC and FRC, respectively. The type of surface treatment was significant for PFC (p < 0.05), but not for FRC (p = 0.572). Upon contamination of freshly cured PFC or semi-IPN FRC, surfaces should be re-prepared via phosphoric acid etching, water cleaning, drying, and application of adhesive composite in order to recover optimal bond strength.

Polishing parameter optimization for end-surface of chalcogenide glass fiber connector

NASA Astrophysics Data System (ADS)

Guo, Fangxia; Dai, Shixun; Tang, Junzhou; Wang, Xunsi; Li, Xing; Xu, Yinsheng; Wu, Yuehao; Liu, Zijun

2017-11-01

We have investigated the optimization parameters for polishing end-surface of chalcogenide glass fiber connector in the paper. Six SiC abrasive particles of different sizes were used to polish the fiber in order of size from large to small. We analyzed the effects of polishing parameters such as particle sizes, grinding speeds and polishing durations on the quality of the fiber end surface and determined the optimized polishing parameters. We found that, high-quality fiber end surface can be achieved using only three different SiC abrasives. The surface roughness of the final ChG fiber end surface is about 48 nm without any scratches, spots and cracks. Such polishing processes could reduce the average insertion loss of the connector to about 3.4 dB.

Effect of dialyzer geometry on granulocyte and complement activation.

PubMed

Schaefer, R M; Heidland, A; Hörl, W H

1987-01-01

During hemodialysis with cuprophan membranes, the complement system as well as leukocytes become activated. In order to clarify the role of dialyzer geometry, the effect of hollow-fiber versus flat-sheet dialyzers and of different surface areas on C3a generation and leukocyte degranulation was investigated. Plasma levels of leukocyte elastase in complex with alpha 1-proteinase inhibitor were significantly increased after 1 h (+55%) and 3 h (+62%) of hemodialysis with flat-sheet dialyzers as compared to hollow-fiber devices. In addition, plasma levels of lactoferrin, released from the specific granules of leukocytes during activation, were significantly higher (+42%) 3 h after the onset of dialysis treatment with flat-sheet than with hollow-fiber dialyzers. With respect to surface area, larger dialyzers tended to cause more release of leukocyte elastase as compared to dialyzers with smaller surface areas, irrespectively of the configuration of the dialyzer used. On the other hand, activation of the complement system, as measured by the generation of C3a-desarg, did not differ with both types of configurations. The same held true for leukopenia, which was almost identical for hollow-fiber and flat-sheet dialyzers. From these findings two lines of evidence emerge: First, not only the type of membrane material used in a dialyzer may influence its biocompatibility, but the geometry of the extracorporeal device also determines the degree of compatibility. Hence, the extent of leukocyte activation correlated with both configuration of the dialyzer and surface area of the membrane.(ABSTRACT TRUNCATED AT 250 WORDS)

Bending energy penalty enhances the adhesive strength of functional amyloid curli to surfaces

NASA Astrophysics Data System (ADS)

Zhang, Yao; Wang, Ao; DeBenedictis, Elizabeth P.; Keten, Sinan

2017-11-01

The functional amyloid curli fiber, a major proteinaceous component of biofilm extracellular matrices, plays an important role in biofilm formation and enterobacteriaceae adhesion. Curli nanofibers exhibit exceptional underwater adhesion to various surfaces, have high rigidity and strong tensile mechanical properties, and thus hold great promise in biomaterials. The mechanisms of how curli fibers strongly attach to surfaces and detach under force remain elusive. To investigate curli fiber adhesion to surfaces, we developed a coarse-grained curli fiber model, in which the protein subunit CsgA (curli specific gene A) self-assembles into the fiber. The coarse-grained model yields physiologically relevant and tunable bending rigidity and persistence length. The force-induced desorption of a single curli fiber is examined using coarse-grained modeling and theoretical analysis. We find that the bending energy penalty arising from high persistence length enhances the resistance of the curli fiber against desorption and thus strengthens the adhesion of the curli fiber to surfaces. The CsgA-surface adhesion energy and the curli fiber bending rigidity both play crucial roles in the resistance of curli fiber against desorption from surfaces. To enable the desorption process, the applied peeling force must overcome both the interfacial adhesion energy and the energy barrier for bending the curli fiber at the peeling front. We show that the energy barrier to desorption increases with the interfacial adhesion energy, however, the bending induced failure of a single curli fiber limits the work of adhesion if the proportion of the CsgA-surface adhesion energy to the CsgA-CsgA cohesive energy becomes large. These results illustrate that the optimal adhesion performance of nanofibers is dictated by the interplay between bending, surface energy and cohesive energy. Our model provides timely insight into enterobacteriaceae adhesion mechanisms as well as future designs of engineered curli fiber based adhesives.

Electrospun fiber surface nanotopography influences astrocyte-mediated neurite outgrowth.

PubMed

Johnson, Christopher D; D'Amato, Anthony R; Puhl, Devan L; Wich, Douglas M; Vespermann, Amanda; Gilbert, Ryan J

2018-05-15

Aligned, electrospun fiber scaffolds provide topographical guidance for regenerating neurons and glia after central nervous system injury. To date, no study has explored how fiber surface nanotopography affects astrocyte response to fibrous scaffolds. Astrocytes play important roles in the glial scar, the blood brain barrier, and in maintaining homeostasis in the central nervous system. In this study, electrospun poly L-lactic acid fibers were engineered with smooth, pitted, or divoted surface nanotopography. Cortical or spinal cord primary rat astrocytes were cultured on the surfaces for either 1 or 3 days to examine the astrocyte response over time. The results showed that cortical astrocytes were significantly shorter and broader on the pitted and divoted fibers compared to those on smooth fibers. However, spinal cord astrocyte morphology was not significantly altered by the surface features. These findings indicate that astrocytes from unique anatomical locations respond differently to the presence of nanotopography. Western Blot results show that the differences in morphology were not associated with significant changes in GFAP or vinculin in either astrocyte population, suggesting that surface pits and divots do not induce a reactive phenotype in either cortical or spinal cord astrocytes. Finally, astrocytes were co-cultured with dorsal root ganglia to determine how the surfaces affected astrocyte-mediated neurite outgrowth. Astrocytes cultured on the fibers for shorter periods of time (1 day) generally supported longer neurite outgrowth. Pitted and divoted fibers restricted spinal cord astrocyte-mediated neurite outgrowth, while smooth fibers increased 3 day spinal cord astrocyte-mediated neurite outgrowth. In total, fiber surface nanotopography can influence astrocyte elongation and influence the capability of astrocytes to direct neurites. Therefore, fiber surface characteristics should be carefully controlled to optimize astrocyte-mediated axonal regeneration. . © 2018 IOP Publishing Ltd.

Fiber-coupled three-micron pulsed laser source for CFRP laser treatment

NASA Astrophysics Data System (ADS)

Nyga, Sebastian; Blass, David; Katzy, Veronika; Westphalen, Thomas; Jungbluth, Bernd; Hoffmann, Hans-Dieter

2018-02-01

We present a laser source providing up to 18 W and 1.5 mJ at a wavelength of 3 μm. The output is generated by frequency conversion of randomly polarized multimode radiation at 1064 nm of an Nd:YAG laser in a two-stage conversion setup. The frequency converter comprises an optical parametric oscillator and a subsequent optical parametric amplifier using PPLN as nonlinear medium in both stages. To implement fiber-based beam delivery for materials processing, we coupled the output at 3 μm to a multimode ZrF4-fiber. This source was then used to remove epoxy resin from the surface of CFRP samples.

Research, development and application of noncombustible Beta fiber structures. [for Apollo

NASA Technical Reports Server (NTRS)

Dillon, J. J.; Cobb, E. S.

1975-01-01

Beta fiber was selected as the primary material for flexible fibrous structures used in spacecraft and crew systems applications in the Apollo program because it was noncombustible in a 100 percent oxygen atmosphere up to 16.5 psia. It met NASA criteria for outgassing, toxicity, odor, and crew comfort, and possessed sufficient durability to last through the mission. Topics discussed include: study of spacecraft applications; design of Beta fiber textile structures to meet the requirements; selection of surface treatments (finishes, coatings, and printing systems) to impart the required durability and special functional use to the textile structures; development of sewing and fabrication techniques; and testing and evaluation programs, and development of production sources.

Conversion and characterization of activated carbon fiber derived from palm empty fruit bunch waste and its kinetic study on urea adsorption.

PubMed

Ooi, Chee-Heong; Cheah, Wee-Keat; Sim, Yoke-Leng; Pung, Swee-Yong; Yeoh, Fei-Yee

2017-07-15

Urea removal is an important process in household wastewater purification and hemodialysis treatment. The efficiency of the urea removal can be improved by utilizing activated carbon fiber (ACF) for effective urea adsorption. In this study, ACF was prepared from oil palm empty fruit bunch (EFB) fiber via physicochemical activation using sulfuric acid as an activating reagent. Based on the FESEM result, ACF obtained after the carbonization and activation processes demonstrated uniform macropores with thick channel wall. ACF was found better prepared in 1.5:1 acid-to-EFB fiber ratio; where the pore size of ACF was analyzed as 1.2 nm in diameter with a predominant micropore volume of 0.39 cm 3  g -1 and a BET surface area of 869 m 2  g -1 . The reaction kinetics of urea adsorption by the ACF was found to follow a pseudo-second order kinetic model. The equilibrium amount of urea adsorbed on ACF decreased from 877.907 to 134.098 mg g -1 as the acid-to-fiber ratio increased from 0.75 to 4. During the adsorption process, the hydroxyl (OH) groups on ACF surface were ionized and became electronegatively charged due to the weak alkalinity of urea solution, causing ionic repulsion towards partially anionic urea. The ionic repulsion force between the electronegatively charged ACF surface and urea molecules became stronger when more OH functional groups appeared on ACF prepared at higher acid impregnation ratio. The results implied that EFB fiber based ACF can be used as an efficient adsorbent for the urea removal process. Copyright © 2017 Elsevier Ltd. All rights reserved.

Adhesion properties in systems of laminated pigmented polymers, carbon-graphite fiber composite framework and titanium surfaces in implant suprastructures.

PubMed

Segerström, Susanna; Ruyter, I Eystein

2009-09-01

For long-term stability the adhering interfaces of an implant-retained supraconstruction of titanium/carbon-graphite fiber-reinforced (CGFR) polymer/opaquer layer/denture base polymer/denture teeth must function as a unity. The aim was to evaluate adhesion of CGFR polymer to a titanium surface or CGFR polymer to two different opaquer layers/with two denture base polymers. Titanium plates were surface-treated and silanized and combined with a bolt of CGFR polymer or denture base polymer (Probase Hot). Heat-polymerized plates of CGFR polymer (47 wt% fiber) based on poly(methyl methacrylate) and a copolymer matrix were treated with an opaquer (Sinfony or Ropak) before a denture base polymer bolt was attached (Probase Hot or Lucitone 199). All specimens were heat-polymerized, water saturated (200 days) and thermally cycled (5000 cycles, 5/55 degrees C) before shear bond testing. Silicatized titanium surfaces gave higher bond strength to CGFR polymer (16.2+/-2.34 and 18.6+/-1.32) MPa and cohesive fracture than a sandblasted surface (5.9+/-2.11) MPa where the fracture was adhesive. The opaquer Sinfony gave higher adhesion values and mainly cohesive fractures than the opaquer Ropak. Different surface treatments (roughened or polished) of the CGFR polymer had no effect on bond strength. The fracture surfaces of silicatized titanium/CGFR polymer/opaquer layer (Sinfony)/denture base polymers were mainly cohesive. A combination of these materials in an implant-retained supraconstruction is promising for in vivo evaluation.

Laser surface treatment of polyamide and NiTi alloy and the effects on mesenchymal stem cell response

NASA Astrophysics Data System (ADS)

Waugh, D. G.; Lawrence, J.; Shukla, P.; Chan, C.; Hussain, I.; Man, H. C.; Smith, G. C.

2015-07-01

Mesenchymal stem cells (MSCs) are known to play important roles in development, post-natal growth, repair, and regeneration of mesenchymal tissues. What is more, surface treatments are widely reported to affect the biomimetic nature of materials. This paper will detail, discuss and compare laser surface treatment of polyamide (Polyamide 6,6), using a 60 W CO2 laser, and NiTi alloy, using a 100 W fiber laser, and the effects of these treatments on mesenchymal stem cell response. The surface morphology and composition of the polyamide and NiTi alloy were studied by scanning electron microscopy (SEM) and X-ray photoemission spectroscopy (XPS), respectively. MSC cell morphology cell counting and viability measurements were done by employing a haemocytometer and MTT colorimetric assay. The success of enhanced adhesion and spreading of the MSCs on each of the laser surface treated samples, when compared to as-received samples, is evidenced in this work.

Oxygen inhibition layer of composite resins: effects of layer thickness and surface layer treatment on the interlayer bond strength.

PubMed

Bijelic-Donova, Jasmina; Garoushi, Sufyan; Lassila, Lippo V J; Vallittu, Pekka K

2015-02-01

An oxygen inhibition layer develops on surfaces exposed to air during polymerization of particulate filling composite. This study assessed the thickness of the oxygen inhibition layer of short-fiber-reinforced composite in comparison with conventional particulate filling composites. The effect of an oxygen inhibition layer on the shear bond strength of incrementally placed particulate filling composite layers was also evaluated. Four different restorative composites were selected: everX Posterior (a short-fiber-reinforced composite), Z250, SupremeXT, and Silorane. All composites were evaluated regarding the thickness of the oxygen inhibition layer and for shear bond strength. An equal amount of each composite was polymerized in air between two glass plates and the thickness of the oxygen inhibition layer was measured using a stereomicroscope. Cylindrical-shaped specimens were prepared for measurement of shear bond strength by placing incrementally two layers of the same composite material. Before applying the second composite layer, the first increment's bonding site was treated as follows: grinding with 1,000-grit silicon-carbide (SiC) abrasive paper, or treatment with ethanol or with water-spray. The inhibition depth was lowest (11.6 μm) for water-sprayed Silorane and greatest (22.9 μm) for the water-sprayed short-fiber-reinforced composite. The shear bond strength ranged from 5.8 MPa (ground Silorane) to 36.4 MPa (water-sprayed SupremeXT). The presence of an oxygen inhibition layer enhanced the interlayer shear bond strength of all investigated materials, but its absence resulted in cohesive and mixed failures only with the short-fiber-reinforced composite. Thus, more durable adhesion with short-fiber-reinforced composite is expected. © 2014 Eur J Oral Sci.

Fiber Surface Modification Technology for Fiber-Optic Localized Surface Plasmon Resonance Biosensors

PubMed Central

Zhang, Qiang; Xue, Chenyang; Yuan, Yanling; Lee, Junyang; Sun, Dong; Xiong, Jijun

2012-01-01

Considerable studies have been performed on the development of optical fiber sensors modified by gold nanoparticles based on the localized surface plasmon resonance (LSPR) technique. The current paper presents a new approach in fiber surface modification technology for biosensors. Star-shaped gold nanoparticles obtained through the seed-mediated solution growth method were found to self-assemble on the surface of tapered optical fibers via amino- and mercapto-silane coupling agents. Transmitted power spectra of 3-aminopropyltrimethoxy silane (APTMS)-modified fiber were obtained, which can verify that the silane coupling agent surface modification method is successful. Transmission spectra are characterized in different concentrations of ethanol and gentian violet solutions to validate the sensitivity of the modified fiber. Assembly using star-shaped gold nanoparticles and amino/mercapto silane coupling agent are analyzed and compared. The transmission spectra of the gold nanoparticles show that the nanoparticles are sensitive to the dielectric properties of the surrounding medium. After the fibers are treated in t-dodecylmercaptan to obtain their transmission spectra, APTMS-modified fiber becomes less sensitive to different media, except that modified by 3-mercaptopropyltrimethoxy silane (MPTMS). Experimental results of the transmission spectra show that the surface modified by the gold nanoparticles using MPTMS is firmer compared to that obtained using APTMS. PMID:22736974

Fiber optic temperature sensor

NASA Technical Reports Server (NTRS)

Sawatari, Takeo (Inventor); Gaubis, Philip A. (Inventor)

2000-01-01

A fiber optic temperature sensor uses a light source which transmits light through an optical fiber to a sensor head at the opposite end of the optical fiber from the light source. The sensor head has a housing coupled to the end of the optical fiber. A metallic reflective surface is coupled to the housing adjacent the end of the optical fiber to form a gap having a predetermined length between the reflective surface and the optical fiber. A detection system is also coupled to the optical fiber which determines the temperature at the sensor head from an interference pattern of light which is reflected from the reflective surface.

Fiber optic temperature sensor

NASA Technical Reports Server (NTRS)

Sawatari, Takeo (Inventor); Gaubis, Philip A. (Inventor); Mattes, Brenton L. (Inventor); Charnetski, Clark J. (Inventor)

1999-01-01

A fiber optic temperature sensor uses a light source which transmits light through an optical fiber to a sensor head at the opposite end of the optical fiber from the light source. The sensor head has a housing coupled to the end of the optical fiber. A metallic reflective surface is coupled to the housing adjacent the end of the optical fiber to form a gap having a predetermined length between the reflective surface and the optical fiber. A detection system is also coupled to the optical fiber which determines the temperature at the sensor head from an interference pattern of light which is reflected from the reflective surface.

Electrospinning of gelatin with tunable fiber morphology from round to flat/ribbon.

PubMed

Topuz, Fuat; Uyar, Tamer

2017-11-01

The electrospinning of gelatin with tunable fiber morphology from round to flat/ribbon was shown, and the detailed studies were conducted to correlate the fiber morphology with electrospinning process parameters and gelatin concentration in electrospinning solution. Particularly, variations in the applied voltage and the concentration of gelatin led to the transition of fiber shape from round to flat/ribbon. The formation of flat-shaped fibers was attributed to rapid evaporation of the solvent (formic acid) from the fiber matrix with increasing the applied voltage and gelatin concentration. On the other hand, round fibers were due to the steady evaporation of formic acid throughout the cross-section of fibers. WAXS analysis revealed that the loss of triple-helical crystalline structure in gelatin after the electrospinning process. The gelatin fibers were cross-linked through treatment with toluene 2,4-diisocyanate (TDI) in a mixed solution of acetone and pyridine, and XPS confirmed the cross-linking of the fibers over an increased carbon content on the elemental composition of the fiber surface due to the incorporated TDI moieties. Overall, this study focuses on morphological tuning of gelatin electrospun fibers towards a flat/ribbon-like structure by variation of electrospinning parameters and polymer concentration, and thus, the proposed concept can be adapted towards flattened/ribbon-like fibers of other protein-based systems by electrospinning. Copyright © 2017 Elsevier B.V. All rights reserved.

Numerical modelling on stimulated Brillouin scattering characterization for Graphene-clad tapered silica fiber

NASA Astrophysics Data System (ADS)

Lee, Hui Jing; Abdullah, Fairuz; Ismail, Aiman

2017-11-01

This paper presents finite numerical modelling on the cross-sectional region of tapered single mode fiber and graphene-clad tapered fiber. Surface acoustic wave propagation across the tapered surface region on tapered single mode fiber has a high threshold power at 61.87 W which is challenging to overcome by the incident pump wave. Surface acoustic wave propagation of fiber surface however made tapered wave plausible in the optical sensor application. This research introduces graphene as the cladding layer on tapered fiber, acoustic confinement occurs due to the graphene cladding which lowers the threshold power from 61.87 W to 2.17 W.

Off-axis reflective optical apparatus

NASA Technical Reports Server (NTRS)

Ames, Lawrence L. (Inventor); Leary, David F. (Inventor); Mammini, Paul V. (Inventor)

2005-01-01

Embodiments of the present invention are directed to a simple apparatus and a convenient and accurate method of mounting the components to form an off-axis reflective optical apparatus such as a collimator. In one embodiment, an off-axis reflective optical apparatus comprises a mounting block having a ferrule holder support surface and an off-axis reflector support surface which is generally perpendicular to the ferrule holder support surface. An optical reflector is mounted on the off-axis reflector support surface and has a reflected beam centerline. The optical reflector has a conic reflective surface and a conic center. A ferrule holder is mounted on the ferrule holder support surface. The ferrule holder provides a ferrule for coupling to an optical fiber and orienting a fiber tip of the optical fiber along a fiber axis toward the optical reflector. The fiber axis is nonparallel to the reflected beam centerline. Prior to mounting the optical reflector to the off-axis reflector support surface and prior to mounting the ferrule holder to the ferrule holder support surface, the optical reflector is movable on the off-axis reflector surface and the ferrule holder is movable on the ferrule holder support surface to align the conic center of the optical reflector with respect to the fiber tip of the optical fiber, and the apparatus has at least one of the following features: (1) the optical reflector is movable on the off-axis reflector support surface to adjust a focus of the fiber tip with respect to the optical reflector, and (2) the ferrule holder is movable on the ferrule holder support surface to adjust the focus of the fiber tip with respect to the optical reflector.

Similar hyaline-like cartilage repair of osteochondral defects in rabbits using isotropic and anisotropic collagen scaffolds.

PubMed

de Mulder, Eric L W; Hannink, Gerjon; van Kuppevelt, Toin H; Daamen, Willeke F; Buma, Pieter

2014-02-01

Lesions in knee joint articular cartilage (AC) have limited repair capacity. Many clinically available treatments induce a fibrous-like cartilage repair instead of hyaline cartilage. To induce hyaline cartilage repair, we hypothesized that type I collagen scaffolds with fibers aligned perpendicular to the AC surface would result in qualitatively better tissue repair due to a guided cellular influx from the subchondral bone. By specific freezing protocols, type I collagen scaffolds with isotropic and anisotropic fiber architectures were produced. Rabbits were operated on bilaterally and two full thickness defects were created in each knee joint. The defects were filled with (1) an isotropic scaffold, (2) an anisotropic scaffold with pores parallel to the cartilage surface, and (3) an anisotropic scaffold with pores perpendicular to the cartilage surface. Empty defects served as controls. After 4 (n=13) and 12 (n=13) weeks, regeneration was scored qualitatively and quantitatively using histological analysis and a modified O'Driscoll score. After 4 weeks, all defects were completely filled with partially differentiated hyaline cartilage tissue. No differences in O'Driscoll scores were measured between empty defects and scaffold types. After 12 weeks, all treatments led to hyaline cartilage repair visualized by increased glycosaminoglycan staining. Total scores were significantly increased for parallel anisotropic and empty defects over time (p<0.05). The results indicate that collagen scaffolds allow the formation of hyaline-like cartilage repair. Fiber architecture had no effect on cartilage repair.

Effect of core diameter and surface treatment on the retention of resin composite cores to prefabricated endodontic posts.

PubMed

Artopoulou, Ioli-Ioanna; O'Keefe, Kathy L; Powers, John M

2006-01-01

With advances in adhesive dentistry and current emphasis on esthetic restorations, dowel systems have been developed to take advantage of these new techniques. Of interest when using these systems is the interaction between core materials and post materials. This investigation compared the tensile retentive force of two resin composite core materials to two metallic and one non-metallic prefabricated endodontic posts. Two dimensions of core build-up and two post-surface treatments were tested. One hundred twenty posts (stainless steel, titanium alloy, and glass fiber-impregnated resin) were secured in a jig with 4 mm of the post extending into a cylindrical matrix. The matrix formed cylinders with diameters of 3 and 5 mm into which resin composite was inserted. The posts were treated or not treated with a bonding agent. After storage for 24 hours at 100% humidity, five specimens per condition were tested in an Instron testing machine at a crosshead speed of 0.5 mm/min. Failure loads were recorded in kilograms and failure modes were observed under light microscopy (40 x). Four-way analysis of variance and multiple comparison testing were used to compare means at the 0.05 level of significance. The means and standard deviations of tensile loads were calculated. All variables were significant in either main effects or interactions ( p<0.05). Fisher's PLSD intervals for post, core, treatment, and diameter were 2.0, 1.6, 1.6, and 1.6 kg, respectively. In most cases, the retentive force recorded for metallic posts was higher than that of glass fiber posts. Titanium posts had higher retentive forces than did the stainless steel posts. For metallic posts, 5-mm cores provided higher forces than 3-mm cores. In the glass fiber group, core diameter was not significant. For core materials, Build-It gave higher results with stainless steel posts, and FluoroCore gave higher results with the titanium ones. The surface treatment results were mixed. In the metallic post groups the adhesive failure data ranged between 80% and 100%, whereas in the glass fiber post groups, adhesive failures ranged between 60% and 70%. Within the limitations of this study, the metallic post groups always provided higher tensile retentive forces, with the titanium post groups showing higher retentive forces than the stainless steel ones. In the glass fiber post groups, different core diameters did not affect retention values.

Bacterial reduction and dentin microhardness after treatment by a pulsed fiber optic delivered Nd:YAG laser

NASA Astrophysics Data System (ADS)

Goodis, Harold E.; White, Joel M.; Marshall, Sally J.; Marshall, Grayson W.

1994-09-01

The purpose of this study was to determine the microhardness and extent of bacterial reduction of contaminated dentin following pulsed fiber optic delivered Nd:YAG laser exposure. Knoop hardness was determined before and after laser exposures from 0.3 to 3.0 W and repetition rates of 10 to 30 Hz. Half the sections were covered with an organic black pigment before laser exposure to evaluate the use of the pigment as an initiator to increase laser absorbance on the surface. Repeated measures design was employed to determine the microhardness of cut and polished dentin sections. Additional dentin sections were sterilized by gamma irradiation and then inoculated with B. subtilis, E. coli or B. stearothermophilus. The contaminated sections were exposed to contact delivered Nd:YAG laser. Cultures were obtained from the dentin surfaces and the colony forming units counted. Increased microhardness was found for all laser treatments above the physical modification. Bacterial reduction was obtained but complete sterilization was not.

An oral absorbent, surface-deacetylated chitin nano-fiber ameliorates renal injury and oxidative stress in 5/6 nephrectomized rats.

PubMed

Anraku, Makoto; Tabuchi, Ryo; Ifuku, Shinsuke; Nagae, Tomone; Iohara, Daisuke; Tomida, Hisao; Uekama, Kaneto; Maruyama, Toru; Miyamura, Shigeyuki; Hirayama, Fumitoshi; Otagiri, Masaki

2017-04-01

In this study, we report that surface-deacetylated chitin nano-fibers (SDACNFs) are more effective in decreasing renal injury and oxidative stress than deacetylated chitin powder (DAC) in 5/6 nephrectomized rats. An oral administration of low doses of SDACNFs (40mg/kg/day) over a 4 week period resulted in a significant decrease in serum indoxyl sulfate, creatinine and urea nitrogen levels, compared with a similar treatment with DAC or AST-120. The SDACNFs treatment also resulted in an increase in antioxidant potential, compared with that for DAC or AST-120. Immunohistochemical analyses also demonstrated that SDACNFs treated CRF rats showed a decrease in the amount of accumulated 8-OHdG compared with the CRF group. These results suggest that the ingestion of SDCH-NF results in a significant reduction in the levels of pro-oxidants, such as uremic toxins, in the gastrointestinal tract, thereby inhibiting the subsequent development of oxidative stress in the systemic circulation. Copyright © 2016. Published by Elsevier Ltd.

Light emitting fabric for photodynamic treatment of actinic keratosis

NASA Astrophysics Data System (ADS)

Thecua, E.; Vicentini, C.; Vignion, A.-S.; Lecomte, F.; Deleporte, P.; Mortier, L.; Szeimies, R.-M.; Mordon, S.

2017-02-01

The integration of optical fibers into flexible textile structures, by using knitting or weaving processes can allow the development of flexible light sources. The paper aims to present a new technology: Light Emitting Fabrics (LEF), which can be used for example for PDT of Actinic Keratosis in Dermatology. The predetermined macro-bending of optical fibers, led to a homogeneous side emission of light over the entire surface of the fabric. Tests showed that additional curvatures when applying the LEF on non-planar surfaces had no impact on light delivery and proved that LEF can adapt to the human morphology. The ability of the LEF, coupled with a 635nm LASER source, to deliver a homogeneous light to lesions is currently assessed in a clinical trial for the treatment of AK of the scalp by PDT. The low irradiance and progressive activation of the photosensitizer ensure a pain reduction, compared to discomfort levels experienced by patients during a conventional PDT session.

Development and Mechanical Behavior of FML/Aluminium Foam Sandwiches

NASA Astrophysics Data System (ADS)

Baştürk, S. B.; Tanoğlu, M.

2013-10-01

In this study, the Fiber-Metal Laminates (FMLs) containing glass fiber reinforced polypropylene (GFPP) and aluminum (Al) sheet were consolidated with Al foam cores for preparing the sandwich panels. The aim of this article is the comparison of the flexural properties of FML/Al foam sandwich panels bonded with various surface modification approaches (silane treatment and combination of silane treatment with polypropylene (PP) based film addition). The FML/foam sandwich systems were fabricated by laminating the components in a mould at 200 °C under 1.5 MPa pressure. The energy absorbtion capacities and flexural mechanical properties of the prepared sandwich systems were evaluated by mechanical tests. Experiments were performed on samples of varying foam thicknesses (8, 20 and 30 mm). The bonding among the sandwich components were achieved by various surface modification techniques. The Al sheet/Al foam sandwiches were also consolidated by bonding the components with an epoxy adhesive to reveal the effect of GFPP on the flexural performance of the sandwich structures.

Organic colloids and their influence on low-pressure membrane filtration.

PubMed

Laabs, C; Amy, G; Jekel, M

2004-01-01

Wastewater treatment by low-pressure membrane filtration (MF and UF) is affected to a large extent by macromolecules and colloids. In order to investigate the influence of organic colloids on the membrane filtration process, colloids were isolated from a wastewater treatment plant effluent using a rotary-evaporation pre-concentration step followed by dialysis. Stirred cell tests were carried out using redissolved colloids, with and without additional glass fiber filtration. After constant pressure membrane filtration of 190 L/m2, the initial flux had declined by 50% for colloids > 6-8 kD (glass fiber filtered) with a hydrophilic MF membrane and for colloids > 12-14 kD (glass fiber filtered) with a hydrophobic MF membrane. For the non-filtered colloidal solutions, the flux decline was even steeper with the flux being below 10% of the initial flux after 190 L/m2 were passed through the membranes. As with larger particles, colloids form a filtration cake layer on top of the membrane surface when used as isolates without prior filtration. This filtration cake is easily removed during backwashing. However, polysaccharides as a macromolecular component of the colloid isolate cause severe fouling by the formation of a gel layer on the membrane surface that is difficult to remove completely.

Fiber optic sensor and method for making

DOEpatents

Vartuli, James Scott; Bousman, Kenneth Sherwood; Deng, Kung-Li; McEvoy, Kevin Paul; Xia, Hua

2010-05-18

A fiber optic sensor including a fiber having a modified surface integral with the fiber wherein the modified surface includes an open pore network with optical agents dispersed within the open pores of the open pore network. Methods for preparing the fiber optic sensor are also provided. The fiber optic sensors can withstand high temperatures and harsh environments.

Photochemical properties and sensor applications of modified yellow fluorescent protein (YFP) covalently attached to the surfaces of etched optical fibers (EOFs).

PubMed

Veselov, Alexey A; Abraham, Bobin George; Lemmetyinen, Helge; Karp, Matti T; Tkachenko, Nikolai V

2012-01-01

Fluorescent proteins have the inherent ability to act as sensing components which function both in vitro and inside living cells. We describe here a novel study on a covalent site-specific bonding of fluorescent proteins to form self-assembled monolayers (SAMs) on the surface of etched optical fibers (EOFs). Deposition of fluorescent proteins on EOFs gives the opportunity to increase the interaction of guided light with deposited molecules relative to plane glass surfaces. The EOF modification is carried out by surface activation using 3-aminopropylthrimethoxysilane (APTMS) and bifunctional crosslinker sulfosuccinimidyl 4-[N-maleimidomethyl]cyclohexane-1-carboxylate (sulfo-SMCC) which exposes sulfhydryl-reactive maleimide groups followed by covalent site-specific coupling of modified yellow fluorescent protein (YFP). Steady-state and fluorescence lifetime measurements confirm the formation of SAM. The sensor applications of YPF SAMs on EOF are demonstrated by the gradual increase of emission intensity upon addition of Ca(2+) ions in the concentration range from a few tens of micromolars up to a few tens of millimolars. The studies on the effect of pH, divalent cations, denaturing agents, and proteases reveal the stability of YFP on EOFs at normal physiological conditions. However, treatments with 0.5% SDS at pH 8.5 and protease trypsin are found to denaturate or cleave the YFP from fiber surfaces.

Acid leaching of natural chrysotile asbestos to mesoporous silica fibers

NASA Astrophysics Data System (ADS)

Maletaškić, Jelena; Stanković, Nadežda; Daneu, Nina; Babić, Biljana; Stoiljković, Milovan; Yoshida, Katsumi; Matović, Branko

2018-04-01

Nanofibrous silica with a high surface area was produced from chrysotile by the acid-leaching method. Natural mineral chrysotile asbestos from Stragari, Korlace in Serbia was used as the starting material. The fibers were modified by chemical treatment with 1 M HCl and the mineral dissolution was monitored by transmission electron microscopy, X-ray powder diffraction, inductively coupled plasma spectrometry and low-temperature nitrogen adsorption techniques to highlight the effects of the leaching process. The results showed that the applied concentration of acid solution and processing time of 4 h were sufficient to effectively remove the magnesium hydroxide layer and transform the crystal structure of the hazardous starting chrysotile to porous SiO2 nanofibers. With prolonged acid leaching, the specific surface area, S BET, calculated by BET equation, was increased from 147 up to 435 m2 g- 1, with micropores representing a significant part of the specific surface.

Effect of ultraviolet light irradiation on bond strength of fiber post: Evaluation of surface characteristic and bonded area of fiber post with resin cement.

PubMed

Reza, Fazal; Ibrahim, Nur Sukainah

2015-01-01

Fiber post is cemented to a root canal to restore coronal tooth structure. This research aims to evaluate the effect of ultraviolet (UV) irradiation on bond strength of fiber post with resin cement. A total of 40 of the two types of fiber posts, namely, FRC Prostec (FRC) and Fiber KOR (KOR), were used for the experiment. UV irradiation was applied on top of the fiber post surface for 0, 15, 20, and 30 min. The irradiated surface of the fiber posts (n = 5) were immediately bonded with resin cement (Rely X U200) after UV irradiation. Shear bond strength (SBS) MPa was measured, and the dislodged area of post surfaces was examined with scanning electron microscopes. Changes in surface roughness (Ra) of the FRC group after UV irradiation were observed (n = 3) using atomic force microscopy. Data of SBS were statistically analyzed using one-way analysis of variance, followed by multiple comparisons (P < 0.05). SBS was significantly higher for 20 min of UV irradiation of the FRC group while significantly higher SBS was observed with 15 min of UV irradiation of the KOR group. Resin cement was more evident (cohesive failure) on the dislodged post surface of the UV treated groups compared with the control. The surface roughness of the FRC post was Ra = 175.1 nm and Ra = 929.2 nm for the control and the 20 min group, respectively. Higher surface roughness of the UV irradiated group indicated formation of mechanical retention on the fiber post surface. Evidence of cohesive failure was observed which indicated higher SBS of fiber post with the UV irradiated group.

Effect of ultraviolet light irradiation on bond strength of fiber post: Evaluation of surface characteristic and bonded area of fiber post with resin cement

PubMed Central

Reza, Fazal; Ibrahim, Nur Sukainah

2015-01-01

Objective: Fiber post is cemented to a root canal to restore coronal tooth structure. This research aims to evaluate the effect of ultraviolet (UV) irradiation on bond strength of fiber post with resin cement. Materials and Methods: A total of 40 of the two types of fiber posts, namely, FRC Prostec (FRC) and Fiber KOR (KOR), were used for the experiment. UV irradiation was applied on top of the fiber post surface for 0, 15, 20, and 30 min. The irradiated surface of the fiber posts (n = 5) were immediately bonded with resin cement (Rely X U200) after UV irradiation. Shear bond strength (SBS) MPa was measured, and the dislodged area of post surfaces was examined with scanning electron microscopes. Changes in surface roughness (Ra) of the FRC group after UV irradiation were observed (n = 3) using atomic force microscopy. Data of SBS were statistically analyzed using one-way analysis of variance, followed by multiple comparisons (P < 0.05). Results: SBS was significantly higher for 20 min of UV irradiation of the FRC group while significantly higher SBS was observed with 15 min of UV irradiation of the KOR group. Resin cement was more evident (cohesive failure) on the dislodged post surface of the UV treated groups compared with the control. The surface roughness of the FRC post was Ra = 175.1 nm and Ra = 929.2 nm for the control and the 20 min group, respectively. Conclusions: Higher surface roughness of the UV irradiated group indicated formation of mechanical retention on the fiber post surface. Evidence of cohesive failure was observed which indicated higher SBS of fiber post with the UV irradiated group. PMID:25713488

Flexible all-fiber electrospun supercapacitor

NASA Astrophysics Data System (ADS)

Liu, Xinhua; Naylor Marlow, Max; Cooper, Samuel J.; Song, Bowen; Chen, Xiaolong; Brandon, Nigel P.; Wu, Billy

2018-04-01

We present an all-fiber flexible supercapacitor with composite nanofiber electrodes made via electrospinning and an electrospun separator. With the addition of manganese acetylacetonate (MnACAC) to polyacrylonitrile (PAN) as a precursor for the electrospinning process and subsequent heat treatment, the performance of pure PAN supercapacitors was improved from 90 F g-1 to 200 F g-1 (2.5 mV s-1) with possible mass loadings of MnACAC demonstrated as high as 40 wt%. X-ray diffraction measurements showed that after thermal treatment, the MnACAC was converted to MnO, meanwile, the thermal decomposition of MnACAC increased the graphitic degree of the carbonised PAN. Scanning electron microscopy and image processing showed that static electrospinning of pure PAN and PAN-Mn resulted in fiber diameters of 460 nm and 480 nm respectively after carbonisation. Further analysis showed that the fiber orientation exhibited a slight bias which was amplified with the addition of MnACAC. Use of focused ion beam scanning electron microscopy tomography also showed that MnO particles were evenly distributed through the fiber at low MnACAC concentrations, while at a 40 wt% loading the MnO particles were also visible on the surface. Comparison of the electrospun separators showed improved performance relative to a commercial Celgard separator (200 F g-1 vs 141 F g-1).

Preparation of a non-woven poly(ε-caprolactone) fabric with partially embedded apatite surface for bone tissue engineering applications by partial surface melting of poly(ε-caprolactone) fibers.

PubMed

Kim, In Ae; Rhee, Sang-Hoon

2017-07-01

This article describes a novel method for the preparation of a biodegradable non-woven poly(ε-caprolactone) fabric with a partially embedded apatite surface designed for application as a scaffold material for bone tissue engineering. The non-woven poly(ε-caprolactone) fabric was generated by the electro-spinning technique and then apatite was coated in simulated body fluid after coating the PVA solution containing CaCl 2 ·2H 2 O. The apatite crystals were partially embedded or fully embedded into the thermoplastic poly(ε-caprolactone) fibers by controlling the degree of poly(ε-caprolactone) fiber surface melting in a convection oven. Identical apatite-coated poly(ε-caprolactone) fabric that did not undergo heat-treatment was used as a control. The features of the embedded apatite crystals were evaluated by FE-SEM, AFM, EDS, and XRD. The adhesion strengths of the coated apatite layers and the tensile strengths of the apatite coated fabrics with and without heat-treatment were assessed by the tape-test and a universal testing machine, respectively. The degree of water absorbance was assessed by adding a DMEM droplet onto the fabrics. Moreover, cell penetrability was assessed by seeding preosteoblastic MC3T3-E1 cells onto the fabrics and observing the degrees of cell penetration after 1 and 4 weeks by staining nuclei with DAPI. The non-woven poly(ε-caprolactone) fabric with a partially embedded apatite surface showed good water absorbance, cell penetrability, higher apatite adhesion strength, and higher tensile strength compared with the control fabric. These results show that the non-woven poly(ε-caprolactone) fabric with a partially embedded apatite surface is a potential candidate scaffold for bone tissue engineering due to its strong apatite adhesion strength and excellent cell penetrability. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1973-1983, 2017. © 2017 Wiley Periodicals, Inc.

SU-F-T-515: Increased Skin Dose in Supine Craniospinal Irradiation Due to Carbon Fiber Couch and Vacuum Bag Immobilization Device

DOE Office of Scientific and Technical Information (OSTI.GOV)

Robertson, D; Zhao, Z; Wang, X

2016-06-15

Purpose: To measure the surface dose for supine craniospinal irradiation employing posterior beams, treating through an imaging couch and BlueBag immobilization device. Methods: The percentage depth dose (PDD) in the buildup region of a clinical 6 MV photon beam was measured using an Advanced Markus parallel plate ionization chamber in a solid water phantom. The PDD from a 10×10 cm{sup 2} anterior beam was measured at 100 cm SSD, simulating a traditional prone craniospinal technique. The measurements were compared to commissioning and treatment planning system data. The PDD was also measured in a posterior setup with the phantom surface layingmore » directly on the Brainlab carbon fiber imaging couch, with the phantom surface 100 cm from the source, simulating a supine craniospinal setup. The posterior measurements were repeated with a BlueBag vacuum immobilization device between the couch and phantom, with thicknesses of 1.7 cm and 5 cm. The PDD from a 10×10 cm{sup 2} field and a typical 6×30 cm{sup 2} craniospinal field were also compared. The PDDs were normalized at 5 cm to reflect typical craniospinal prescription dose normalization. Results: The measured PDD curve from the anterior setup agreed well with commissioning and treatment planning data, with surface doses of 19.9%, 28.8% and 27.7%, respectively. The surface doses of the 10×10 cm{sup 2} and 6×30 cm{sup 2} fields delivered through the imaging couch were both 122.4%. The supine setup yielded surface doses of 122.4%, 121.6%, and 119.6% for the couch only, 1.7 cm bag, and 5 cm bag setups, respectively. Conclusion: Delivering craniospinal irradiation through a carbon fiber couch removes the majority of skin sparing. The addition of a vacuum bag immobilization device restores some skin sparing, but the magnitude of this effect is negligible.« less

Technique development for photoacoustic imaging guided interventions

NASA Astrophysics Data System (ADS)

Cheng, Qian; Zhang, Haonan; Yuan, Jie; Feng, Ting; Xu, Guan; Wang, Xueding

2015-03-01

Laser-induced thermotherapy (LITT), i.e. tissue destruction induced by a local increase of temperature by means of laser light energy transmission, has been frequently used for minimally invasive treatments of various diseases such as benign thyroid nodules and liver cancer. The emerging photoacoustic (PA) imaging, when integrated with ultrasound (US), could contribute to LITT procedure. PA can enable a good visualization of percutaneous apparatus deep inside tissue and, therefore, can offer accurate guidance of the optical fibers to the target tissue. Our initial experiment demonstrated that, by picking the strong photoacoustic signals generated at the tips of optical fibers as a needle, the trajectory and position of the fibers could be visualized clearly using a commercial available US unit. When working the conventional US Bscan mode, the fibers disappeared when the angle between the fibers and the probe surface was larger than 60 degree; while working on the new PA mode, the fibers could be visualized without any problem even when the angle between the fibers and the probe surface was larger than 75 degree. Moreover, with PA imaging function integrated, the optical fibers positioned into the target tissue, besides delivering optical energy for thermotherapy, can also be used to generate PA signals for on-line evaluation of LITT. Powered by our recently developed PA physio-chemical analysis, PA measurements from the tissue can provide a direct and accurate feedback of the tissue responses to laser ablation, including the changes in not only chemical compositions but also histological microstructures. The initial experiment on the rat liver model has demonstrated the excellent sensitivity of PA imaging to the changes in tissue temperature rise and tissue status (from native to coagulated) when the tissue is treated in vivo with LITT.

Holmium:YAG (lambda=2120nm) vs. Thulium fiber (lambda=1908nm) laser for high-power vaporization of canine prostate tissue

NASA Astrophysics Data System (ADS)

Casperson, Andrew L.; Barton, Robert A.; Scott, Nicholas J.; Fried, Nathaniel M.

2008-02-01

Direct studies comparing different lasers for treatment of BPH are lacking. This preliminary study compares continuous-wave (CW) vs. pulsed prostate tissue vaporization for the Thulium fiber laser and Holmium:YAG laser, both operating near the 1940 nm water absorption peak in tissue. A 50-W Thulium fiber laser (λ= 1908 nm) delivered CW laser radiation through a 600-μm silica fiber in non-contact mode with a 5-mm-diameter spot at the tissue surface. A Holmium:YAG laser (λ= 2120 nm) operated with an energy of 2 J, pulse rate of 25 Hz, and average power of 50 W, and delivered pulsed laser radiation through a 600-μm silica fiber with a 5-mm-diameter laser spot to achieve similar irradiances at the tissue surface. Tissue vaporization was performed in air with the prostate kept hydrated in saline. Tissue vaporization efficiency of both lasers was compared (n = 10 canine prostates for each laser group). Mean vaporization efficiency measured 5.30 +/- 0.48 kJ/g vs. 4.13 +/- 0.46 kJ/g for Thulium fiber and Holmium lasers (P < 0.05). Tissue vaporization rates measured 0.57 +/- 0.05 g/min vs. 0.73 +/- 0.07 g/min (P < 0.05). The Holmium:YAG laser vaporizes prostate tissue at a higher rate than the Thulium fiber laser, for the same average power delivered to the tissue. Both the Thulium fiber laser and Holmium:YAG lasers are capable of vaporizing prostate tissue at a rate > 1 g/min if operated at the high powers (100-W) typically used in the clinic.

Preparation of thick silica coatings on carbon fibers with fine-structured silica nanotubes induced by a self-assembly process.

PubMed

Baumgärtner, Benjamin; Möller, Hendrik; Neumann, Thomas; Volkmer, Dirk

2017-01-01

A facile method to coat carbon fibers with a silica shell is presented in this work. By immobilizing linear polyamines on the carbon fiber surface, the high catalytic activity of polyamines in the sol-gel-processing of silica precursors is used to deposit a silica coating directly on the fiber's surface. The surface localization of the catalyst is achieved either by attaching short-chain polyamines (e.g., tetraethylenepentamine) via covalent bonds to the carbon fiber surface or by depositing long-chain polyamines (e.g., linear poly(ethylenimine)) on the carbon fiber by weak non-covalent bonding. The long-chain polyamine self-assembles onto the carbon fiber substrate in the form of nanoscopic crystallites, which serve as a template for the subsequent silica deposition. The silicification at close to neutral pH is spatially restricted to the localized polyamine and consequently to the fiber surface. In case of the linear poly(ethylenimine), silica shells of several micrometers in thickness can be obtained and their morphology is easily controlled by a considerable number of synthesis parameters. A unique feature is the hierarchical biomimetic structure of the silica coating which surrounds the embedded carbon fiber by fibrillar and interconnected silica fine-structures. The high surface area of the nanostructured composite fiber may be exploited for catalytic applications and adsorption purposes.

Assessing the Increase in Specific Surface Area for Electrospun Fibrous Network due to Pore Induction.

PubMed

Katsogiannis, Konstantinos Alexandros G; Vladisavljević, Goran T; Georgiadou, Stella; Rahmani, Ramin

2016-10-26

The effect of pore induction on increasing electrospun fibrous network specific surface area was investigated in this study. Theoretical models based on the available surface area of the fibrous network and exclusion of the surface area lost due to fiber-to-fiber contacts were developed. The models for calculation of the excluded area are based on Hertzian, Derjaguin-Muller-Toporov (DMT), and Johnson-Kendall-Roberts (JKR) contact models. Overall, the theoretical models correlated the network specific surface area to the material properties including density, surface tension, Young's modulus, Poisson's ratio, as well as network physical properties, such as density and geometrical characteristics including fiber radius, fiber aspect ratio and network thickness. Pore induction proved to increase the network specific surface area up to 52%, compared to the maximum surface area that could be achieved by nonporous fiber network with the same physical properties and geometrical characteristics. The model based on Johnson-Kendall-Roberts contact model describes accurately the fiber-to-fiber contact area under the experimental conditions used for pore generation. The experimental results and the theoretical model based on Johnson-Kendall-Roberts contact model show that the increase in network surface area due to pore induction can reach to up to 58%.

Multifunctional Textured Surfaces with Enhanced Friction and Hydrophobic Behaviors Produced by Fiber Debonding and Pullout.

PubMed

Rizvi, Reza; Anwer, Ali; Fernie, Geoff; Dutta, Tilak; Naguib, Hani

2016-11-02

Fiber debonding and pullout are well-understood processes that occur during damage and failure events in composite materials. In this study, we show how these mechanisms, under controlled conditions, can be used to produce multifunctional textured surfaces. A two-step process consisting of (1) achieving longitudinal fiber alignment followed by (2) cutting, rearranging, and joining is used to produce the textured surfaces. This process employs common composite manufacturing techniques and uses no reactive chemicals or wet handling, making it suitable for scalability. This uniform textured surface is due to the fiber debonding and pullout occurring during the cutting process. Using well-established fracture mechanics principles for composite materials, we demonstrate how different material parameters such as fiber geometry, fiber and matrix stiffness and strength, and interface behavior can be used to achieve multifunctional textured surfaces. The resulting textured surfaces show very high friction coefficients on wet ice (9× improvement), indicating their promising potential as materials for ice traction/tribology. Furthermore, the texturing enhances the surface's hydrophobicity as indicated by an increase in the contact angle of water by 30%. The substantial improvements to surface tribology and hydrophobicity make fiber debonding and pullout an effective, simple, and scalable method of producing multifunctional textured surfaces.

Surface topography, hardness, and frictional properties of GFRP for esthetic orthodontic wires.

PubMed

Inami, Toshihiro; Tanimoto, Yasuhiro; Yamaguchi, Masaru; Shibata, Yo; Nishiyama, Norihiro; Kasai, Kazutaka

2016-01-01

In our previous study, glass-fiber-reinforced plastics (GFRPs) made from polycarbonate and glass fiber for esthetic orthodontic wires were prepared by using pultrusion. The purpose of the present study was to investigate the surface topography, hardness, and frictional properties of GFRPs. To investigate how fiber diameter affects surface properties, GFRP round wires with a diameter of 0.45 mm (0.018 in.) were prepared incorporating either 13 μm (GFRP-13) or 7 μm (GFRP-7) glass fibers. As controls, stainless steel (SS), cobalt-chromium-nickel alloy, β-titanium (β-Ti) alloy, and nickel-titanium (Ni-Ti) alloy were also evaluated. Under scanning electron microscopy and scanning probe microscopy, the β-Ti samples exhibited greater surface roughness than the other metallic wires and the GFRP wires. The dynamic hardness and elastic modulus of GFRP wires obtained by the dynamic micro-indentation method were much lower than those of metallic wires (p < 0.05). Frictional forces against the polymeric composite brackets of GFRP-13 and GFRP-7 were 3.45 ± 0.49 and 3.60 ± 0.38 N, respectively; frictional forces against the ceramic brackets of GFRP-13 and GFRP-7 were 3.39 ± 0.58 and 3.87 ± 0.48 N, respectively. For both bracket types, frictional forces of GFRP wires and Ni-Ti wire were nearly half as low as those of SS, Co-Cr, and β-Ti wires. In conclusion, there was no significant difference in surface properties between GFRP-13 and GFRP-7; presumably because both share the same polycarbonate matrix. We expect that GFRP wires will deliver superior sliding mechanics with low frictional resistance between the wire and bracket during orthodontic treatment. © 2015 Wiley Periodicals, Inc.

Effect of surface treatment on retention of glass-fiber endodontic posts.

PubMed

Balbosh, Ali; Kern, Matthias

2006-03-01

The effects of surface treatment on the retention of prefabricated fiber-reinforced epoxy resin posts are not well understood because most studies measure retention shortly after cementation, without artificial aging. The purpose of this study was to evaluate the effect of surface treatment on the retention of glass-fiber endodontic posts luted with resin cement and subjected to artificial aging. Thirty-two single-rooted teeth were selected, the coronal aspect of each tooth was removed, and the remaining root received endodontic therapy. Specimens were then divided into 4 groups (n = 8). Post spaces were prepared to a depth of 10 mm by using ISO 90 rotary instruments. The tapered posts received 1 of 4 surface treatments: cleaning with alcohol (Alc), cleaning with alcohol and conditioning with ED-Primer material (Alc-ED), airborne-particle abrasion (Air), or airborne-particle abrasion and conditioning with ED-Primer material (Air-ED). All posts were luted with a composite resin luting agent (Panavia F) after conditioning the canal dentin with autopolymerizing dentin primer (ED-Primer) and without acid etching of the canal dentin. After cementation, the specimens were stored in water at 37 degrees C for 30 days and subjected to simulated aging conditions consisting of 7500 thermal cycles (5 degrees C/55 degrees C) and 300,000 mechanical loading cycles with 30 N. Retention (N) of the posts was measured with a universal testing machine with a crosshead speed of 2 mm/min. The data were analyzed using 1-way ANOVA and the Tukey HSD test (alpha = .05). The dislodged posts were also examined microscopically at x8 and x20 magnification to evaluate the mode of failure. The mean retentive values (N) and SDs of the test groups were as follows: Alc, 375.9 +/- 85.0; Alc-ED, 421.2 +/- 46.8; Air, 534.8 +/- 65.8; and Air-ED, 555.8 +/- 86.9. Airborne-particle-abraded posts had significantly higher retention compared with nonabraded posts (P < .001). Treating the post's surface with ED-Primer material prior to cementation had no significant effect on retention. The failure mode was purely adhesive at the resin cement-post interface for all nonabraded posts. A mixed failure mode, adhesive at the resin cement-dentin interface, at the resin cement-post interface, and cohesive in the resin cement, was observed for airborne-particle-abraded posts. Treating the surface of the posts with ED-Primer material before cementation with Panavia F cement produced no significant improvement in the retention of the posts. Airborne-particle abrasion of the surface of the post significantly improved the retention.

Non-Contact Evaluation for Articular Cartilage Using Ultrasound

NASA Astrophysics Data System (ADS)

Mori, Koji; Nakagawa, Yasuaki; Kuroki, Hiroshi; Nakashima, Keisuke; Ikeuchi, Ken; Mine, Takatomo; Nakamura, Takashi; Kawai, Shinya; Saito, Takashi

In orthopedic field, various new treatments of articular cartilage defect, for example autogenous osteochondral grafts, have been developed. With the spread of these treatments, orthopedists began to focus on the mechanical properties of recovered articular cartilage. The quantitative evaluation of articular cartilage before and after these treatments gives orthopedists the important information to improve these treatments and develop new treatments. We have been investigating the non-contact ultrasonic evaluation for articular cartilage under arthroscopy. In this paper, it was hypothesized that the ultrasonic evaluation depended on the collagen fiber in cartilage. The enzymatically degradation of collagen fiber in cartilage surface was performed. The effect of the degradation on sound velocity, attenuation coefficient and signal intensity, which is the index of cartilage stiffness calculated from the proposed method, was measured. The numerical analysis was performed to clear the relation between the cartilage character and ultrasonic parameters. Experimental and numerical results suggest that the present method can be expanded the sensitive evaluation for cartilage disease in clinical field.

Plasmonic structure: fiber grating formed by gold nanorods on a tapered fiber.

PubMed

Trevisanutto, J O; Linhananta, A; Das, G

2016-12-15

The authors demonstrated the fabrication of a fiber Bragg grating-like plasmonic nanostructure on the surface of a tapered optical fiber using gold nanorods (GNRs). A multimode optical fiber with core and cladding diameters of 105 and 125 μm, respectively, was used to make a tapered fiber using a dynamic etching process. The tip diameter was ∼100  nm. Light from a laser was coupled to the untapered end of the fiber, which produced a strong evanescent field around the tapered section of the fiber. The gradient force due to the evanescent field trapped the GNRs on the surface of the tapered fiber. The authors explored possible causes of the GNR distribution. The plasmonic structure will be a good candidate for sensing based on surface enhanced Raman scattering.

The development and mechanical characterization of aluminium copper-carbon fiber metal matrix hybrid composite

NASA Astrophysics Data System (ADS)

Manzoor, M. U.; Feroze, M.; Ahmad, T.; Kamran, M.; Butt, M. T. Z.

2018-04-01

Metal matrix composites (MMCs) come under advanced materials that can be used for a wide range of industrial applications. MMCs contain a non-metallic reinforcement incorporated into a metallic matrix which can enhance properties over base metal alloys. Copper-Carbon fiber reinforced aluminium based hybrid composites were prepared by compo casting method. 4 weight % copper was used as alloying element with Al because of its precipitation hardened properties. Different weight compositions of composites were developed and characterized by mechanical testing. A significant improvement in tensile strength and micro hardness were found, before and after heat treatment of the composite. The SEM analysis of the fractured surfaces showed dispersed and embedded Carbon fibers within the network leading to the enhanced strength.

UV irradiation improves the bond strength of resin cement to fiber posts.

PubMed

Zhong, Bo; Zhang, Yong; Zhou, Jianfeng; Chen, Li; Li, Deli; Tan, Jianguo

2011-01-01

The purpose is to evaluate the effect of UV irradiation on the bond strength between epoxy-based glass fiber posts and resin cement. Twelve epoxy-based glass fiber posts were randomly divided into three groups. Group 1 (Cont.): No surface treatment. Group 2 (Low-UV): UV irradiation was conducted from a distance of 10 cm for 10 min. Group 3 (High-UV): UV irradiation was conducted from a distance of 1 cm for 3 min. A resin cement (CLEARFIL SA LUTING) was used for the post cementation to form resin slabs which contained fiber posts in the center. Microtensile bond strengths were tested and the mean bond strengths (MPa) were 18.81 for Cont. group, 23.65 for Low-UV group, 34.75 for High-UV group. UV irradiation had a significant effect on the bond strength (p<0.05). UV irradiation demonstrates its capability to improve the bond strength between epoxy-based glass fiber posts and resin cement.

Laser-treated electrospun fibers loaded with nano-hydroxyapatite for bone tissue engineering.

PubMed

Aragon, Javier; Navascues, Nuria; Mendoza, Gracia; Irusta, Silvia

2017-06-15

Core-shell polycaprolactone/polycaprolactone (PCL/PCL) and polycaprolactone/polyvinyl acetate (PCL/PVAc) electrospun fibers loaded with synthesized nanohydroxyapatite (HAn) were lased treated to create microporosity. The prepared materials were characterized by XRD, FTIR, TEM and SEM. Uniform and randomly oriented beadless fibrous structures were obtained in all cases. Fibers diameters were in the 150-300nm range. Needle-like HAn nanoparticles with mean diameters of 20nm and length of approximately 150nm were mostly encase inside the fibers. Laser treated materials present micropores with diameters in the range 70-120μm for PCL-HAn/PCL fibers and in the 50-90μm range for PCL-HAn/PVAC material. Only samples containing HAn presented bioactivity after incubation during 30days in simulated body fluid. All scaffolds presented high viability, very low mortality, and human osteoblast proliferation. Biocompatibility was increased by laser treatment due to the surface and porosity modification. Copyright © 2017 Elsevier B.V. All rights reserved.

Sources and dispersive modes of micro-fibers in the environment.

PubMed

Carr, Steve A

2017-05-01

Understanding the sources and distribution of microfibers (MFs) in the environment is critical if control and remediation measures are to be effective. Microfibers comprise an overwhelming fraction (>85%) of microplastic debris found on shorelines around the world. Although primary sources have not been fully vetted, until recently it was widely believed that domestic laundry discharges were the major source. It was also thought that synthetic fibers and particles having dimensions <5 mm easily bypassed filtration and other solid separation processes at wastewater treatment plants (WWTPs) and entered oceans and surface waters. A more thorough assessment of WWTP effluent discharges indicates, however, that fiber and particulate counts do not support the belief that plants are the primary vectors for fibers entering the environment. This finding may bolster concerns that active and pervasive shedding of fibers from common fabrics and textiles could be contributing significantly, via direct pathways, to burgeoning environmental loads. Integr Environ Assess Manag 2017;13:466-469. © 2017 SETAC. © 2017 SETAC.

Effect of fiber reinforcement on thermo-oxidative stability and mechanical properties of polymer matrix composites

NASA Technical Reports Server (NTRS)

Bowles, K. J.

1992-01-01

A number of studies have investigated the thermooxidative behavior of polymer matrix composites. Two significant observations have been made from these research efforts: (1) fiber reinforcement has a significant effect on composite thermal stability; and (2) geometric effects must be considered when evaluating thermal aging data. The polyimide PMR-15 was the matrix material used in these studies. The control composite material was reinforced with Celion 6000 graphite fiber. T-4OR graphite fibers, along with some very stable ceramic fibers were selected as reinforcing fibers because of their high thermal stability. The ceramic fibers were Nicalon (silicon carbide) and Nextel 312 (alumina-silica-boron oxide). The mechanical properties of the two graphite fiber composites were significantly different, probably owing to variations in interfacial bonding between the fibers and the polyimide matrix. Three oxidation mechanisms were observed: (1) the preferential oxidation of the Celion 6000 fiber ends at cut surfaces, leaving a surface of matrix material with holes where the fiber ends were originally situated; (2) preferential oxidation of the composite matrix; and (3) interfacial degradation by oxidation. The latter two mechanisms were also observed on fiber end cut surfaces. The fiber and interface attacks appeared to initiate interfiber cracking along these surfaces.

Surface and Bulk Characteristics of Cesium Iodide (CsI) coated Carbon (C) Fibers for High Power Microwave (HPM) Field Emission Cathodes

NASA Astrophysics Data System (ADS)

Vlahos, Vasilios; Morgan, Dane; Booske, John H.; Shiffler, Don

2008-11-01

CsI coated C fibers [1] are promising field emission cathodes for HPM applications. Ab initio computational modeling has shown that atomically-thin CsI coatings reduce the work function of C substrates by a surface dipole mechanism [2]. Characterization measurements of the composition and morphology of the CsI-coated C fibers are underway for determining the properties and characteristics of the following important regions of the fiber: (i) the surface on the tip of the fiber where the majority of electron emission is believed to occur, (ii) the surface covering the body of the fiber and its role on the emission properties of the system, and (iii) the interior volume of the fiber and its effects on the CsI surface re-supply process and rate. The results will be interpreted in terms of surface electronic properties and theoretical electron emission models. [1]D. Shiffler, et al., Phys. Plasmas 11 (2004) 1680. [2]V.Vlahos et al., Appl. Phys. Lett. 91 (2007) 144102.

Fog Collection on Polyethylene Terephthalate (PET) Fibers: Influence of Cross Section and Surface Structure.

PubMed

Azad, M A K; Krause, Tobias; Danter, Leon; Baars, Albert; Koch, Kerstin; Barthlott, Wilhelm

2017-06-06

Fog-collecting meshes show a great potential in ensuring the availability of a supply of sustainable freshwater in certain arid regions. In most cases, the meshes are made of hydrophilic smooth fibers. Based on the study of plant surfaces, we analyzed the fog collection using various polyethylene terephthalate (PET) fibers with different cross sections and surface structures with the aim of developing optimized biomimetic fog collectors. Water droplet movement and the onset of dripping from fiber samples were compared. Fibers with round, oval, and rectangular cross sections with round edges showed higher fog-collection performance than those with other cross sections. However, other parameters, for example, width, surface structure, wettability, and so forth, also influenced the performance. The directional delivery of the collected fog droplets by wavy/v-shaped microgrooves on the surface of the fibers enhances the formation of a water film and their fog collection. A numerical simulation of the water droplet spreading behavior strongly supports these findings. Therefore, our study suggests the use of fibers with a round cross section, a microgrooved surface, and an optimized width for an efficient fog collection.

Fiber-based adsorbents having high adsorption capacities for recovering dissolved metals and methods thereof

DOEpatents

Janke, Christopher J.; Dai, Sheng; Oyola, Yatsandra

2016-09-06

A fiber-based adsorbent and a related method of manufacture are provided. The fiber-based adsorbent includes polymer fibers with grafted side chains and an increased surface area per unit weight over known fibers to increase the adsorption of dissolved metals, for example uranium, from aqueous solutions. The polymer fibers include a circular morphology in some embodiments, having a mean diameter of less than 15 microns, optionally less than about 1 micron. In other embodiments, the polymer fibers include a non-circular morphology, optionally defining multiple gear-shaped, winged-shaped or lobe-shaped projections along the length of the polymer fibers. A method for forming the fiber-based adsorbents includes irradiating high surface area polymer fibers, grafting with polymerizable reactive monomers, reacting the grafted fibers with hydroxylamine, and conditioning with an alkaline solution. High surface area fiber-based adsorbents formed according to the present method demonstrated a significantly improved uranium adsorption capacity per unit weight over existing adsorbents.

Fiber-based adsorbents having high adsorption capacities for recovering dissolved metals and methods thereof

DOEpatents

Janke, Christopher J; Dai, Sheng; Oyola, Yatsandra

2014-05-13

A fiber-based adsorbent and a related method of manufacture are provided. The fiber-based adsorbent includes polymer fibers with grafted side chains and an increased surface area per unit weight over known fibers to increase the adsorption of dissolved metals, for example uranium, from aqueous solutions. The polymer fibers include a circular morphology in some embodiments, having a mean diameter of less than 15 microns, optionally less than about 1 micron. In other embodiments, the polymer fibers include a non-circular morphology, optionally defining multiple gear-shaped, winged-shaped or lobe-shaped projections along the length of the polymer fibers. A method for forming the fiber-based adsorbents includes irradiating high surface area polymer fibers, grafting with polymerizable reactive monomers, reacting the grafted fibers with hydroxylamine, and conditioning with an alkaline solution. High surface area fiber-based adsorbents formed according to the present method demonstrated a significantly improved uranium adsorption capacity per unit weight over existing adsorbents.

The effects of heat treatment on physical properties and surface roughness of red-bud maple (Acer trautvetteri Medw.) wood.

PubMed

Korkut, Derya Sevim; Guller, Bilgin

2008-05-01

Heat treatment is often used to improve the dimensional stability of wood. In this study, the effects of heat treatment on physical properties and surface roughness of red-bud maple (Acer trautvetteri Medw.) wood were examined. Samples obtained from Düzce Forest Enterprises, Turkey, were subjected to heat treatment at varying temperatures and durations. The physical properties of heat-treated samples were compared against controls in order to determine their; oven-dry density, air-dry density, and swelling properties. A stylus method was employed to evaluate the surface characteristics of the samples. Roughness measurements, using the stylus method, were made in the direction perpendicular to the fiber. Three main roughness parameters; mean arithmetic deviation of profile (Ra), mean peak-to-valley height (Rz), and maximum roughness (Rmax) obtained from the surface of wood, were used to evaluate the effect of heat treatment on the surface characteristics of the specimens. Significant differences were determined (p>0.05) between surface roughness parameters (Ra, Rz, Rmax) at three different temperatures and three periods of heat treatment. The results showed that the values of density, swelling and surface roughness decreased with increasing temperature treatment and treatment times. Red-bud maple wood could be utilized successfully by applying proper heat treatment techniques without any losses in investigated parameters. This is vital in areas, such as window frames, where working stability and surface smoothness are important factors.

Fiber composite flywheel rim

DOEpatents

Davis, D.E.; Ingham, K.T.

1987-04-28

A flywheel comprising a hub having at least one radially projecting disc, an annular rim secured to said disc and providing a surface circumferential to said hub, a first plurality of resin-impregnated fibers wound about said rim congruent to said surface, and a shell enclosing said first plurality of fibers and formed by a second plurality of resin-impregnated fibers wound about said rim tangentially to said surface. 2 figs.

FIBER ROLLS AS A TOOL FOR RE-VEGETATION OF OIL-BRINE CONTAMINATED WATERSHEDS

EPA Science Inventory

We found that fibrijute burlap cylinders filled with organic matter and inoculated with salt tolerant plants and mycorrhizal fungi promoted remediation of an historic brine scar devoid of vegetation since the 1960's. Soils in plots that received a surface treatment of hay, org...

Caries selective ablation: the handpiece

NASA Astrophysics Data System (ADS)

Hennig, Thomas; Rechmann, Peter; Holtermann, Andreas

1995-05-01

Caries selective ablation is fixed to a window of fluences predicted by the ablation thresholds of carious and healthy dentin, respectively. The aim of the study was to develop a dental handpiece which guarantees homogeneous fluence at the irradiated tooth surface. Furthermore the point of treatment should be cooled down without energy losses due to the cooling system. We suggest the direct coupling of the laser radiation into a laminar stream of liquid, which acts in turn as a lengthened beam guide. The impacts of the laser radiation and of the cooling medium fall exactly into the same point. Hot ablation debris is removed out of the crater by the flush of the water jet. Fluences are constant if the handpiece is used in contact mode or at a distance. Normally the surface of a bare fiber working in contact mode is destroyed after a few shots. Coupling the laser radiation into a stream of liquid prevents this destruction. Putting together the benefits of this special handpiece short overall treatment times seem to be possible. High average power can be applied to the tooth without the threat of thermal damage. Furthermore no time consuming cutting of the fiber prolongs the treatment time.

Improved performance of selective ablation using a specially designed handpiece

NASA Astrophysics Data System (ADS)

Hennig, Thomas; Rechmann, Peter

1996-01-01

Selective ablation is fixed to a range of fluences predicted by the ablation thresholds of infected and healthy tooth structures respectively. The aim of the study was to develop a dental handpiece, which guarantees homogeneous fluence at the irradiated tooth surface. Furthermore the point of treatment should be cooled down without energy losses due to the cooling system. We suggest the direct coupling of the laser radiation into a laminar stream of liquid, which may act in turn as a lengthened beam guide. The impacts of the laser radiation and of the cooling medium hit exactly the same point. Hot ablation debris is removed out of the crater by the flush of the water jet. While the surface of a bare fiber working on contact mode is destroyed after a few shots, it was shown that coupling the laser radiation into a stream of liquid prevents this destruction. Putting together the benefits of this special handpiece short overall treatment times seem to be possible. High average power can be applied to the tooth without the threat of thermal damage. Furthermore no time consuming cutting of the fiber prolongs the treatment time.

[INVITED] Porphyrin-nanoassembled fiber-optic gas sensor fabrication: Optimization of parameters for sensitive ammonia gas detection

NASA Astrophysics Data System (ADS)

Korposh, Sergiy; Kodaira, Suguru; Selyanchyn, Roman; Ledezma, Francisco H.; James, Stephen W.; Lee, Seung-Woo

2018-05-01

Highly sensitive fiber-optic ammonia gas sensors were fabricated via layer-by-layer deposition of poly(diallyldimethylammonium chloride) (PDDA) and tetrakis(4-sulfophenyl)porphine (TSPP) onto the surface of the core of a hard-clad multimode fiber that was stripped of its polymer cladding. The effects of film thickness, length of sensing area, and depth of evanescent wave penetration were investigated to clearly understand the sensor performance. The sensitivity of the fiber-optic sensor to ammonia was linear in the concentration range of 0.5-50 ppm and the response and recovery times were less than 3 min, with a limit of detection of 0.5 ppm, when a ten-cycle PDDA/TSPP film was assembled on the surface of the core along a 1 cm-long stripped section of the fiber. The sensor's response towards ammonia was also checked under different relative humidity conditions and a simple statistical data treatment approach, principal component analysis, demonstrated the feasibility of ammonia sensing in environmental relative humidity ranging from dry 7% to highly saturated 80%. Penetration depths of the evanescent wave for the optimal sensor configuration were estimated to be 30 and 33 nm at wavelengths of 420 and 706 nm, which are in a good agreement with the thickness of the 10-cycle deposited film (ca. 30 nm).

Excimer laser in arthroscopic surgery

NASA Astrophysics Data System (ADS)

Koort, Hans J.

1991-05-01

The development of efficient high-power lasersystems for use in surgery, especially in arthroscopic fields, leads to a new push for all endoscopic techniques. Both techniques, laser and endoscope, complete each other in an ideal way and allow applications which could not be reached with conventional techniques. One of the newer laser types is the excimer laser, which will be a good choice for surface treatment because of its very considerate interaction with tissue. One example is the ablation or smoothing of articular cartilage and meniscal shaving in orthopaedics. On the other hand, the power of this laser system is high enough to cut tissue, for instance in the lateral release, and offers therefore an alternative to the mechanical and electrical instruments. All lasers can only work fine with effective delivery systems. Sometimes there is only a single fiber, which becomes very stiff at diameters of more than 800 micrometers . This fiber often allows only the tangential treatment of tissue, most of the laser power is lost in the background. New fiber systems with many, sometimes hundreds of very thin single fibers, could offer a solution. Special handpieces and fibersystems offer distinct advantages in small joint arthroscopy, especially those for use with excimer lasers will be discussed.

Application of atmospheric pressure plasma in polymer and composite adhesion

NASA Astrophysics Data System (ADS)

Yu, Hang

An atmospheric pressure helium and oxygen plasma was used to investigate surface activation and bonding in polymer composites. This device was operated by passing 1.0-3.0 vol% of oxygen in helium through a pair of parallel plate metal electrodes powered by 13.56 or 27.12 MHz radio frequency power. The gases were partially ionized between the capacitors where plasma was generated. The reactive species in the plasma were carried downstream by the gas flow to treat the substrate surface. The temperature of the plasm gas reaching the surface of the substrate did not exceed 150 °C, which makes it suitable for polymer processing. The reactive species in the plasma downstream includes ~ 1016-1017 cm-3 atomic oxygen, ~ 1015 cm-3 ozone molecule, and ~ 10 16 cm-3 metastable oxygen molecule (O2 1Deltag). The substrates were treated at 2-5 mm distance from the exit of the plasma. Surface properties of the substrates were characterized using water contact angle (WCA), atomic force microscopy (AFM), infrared spectroscopy (IR), and X-ray photoelectron spectroscopy (XPS). Subsequently, the plasma treated samples were bonded adhesively or fabricated into composites. The increase in mechanical strength was correlated to changes in the material composition and structure after plasma treatment. The work presented hereafter establishes atmospheric pressure plasma as an effective method to activate and to clean the surfaces of polymers and composites for bonding. This application can be further expanded to the activation of carbon fibers for better fiber-resin interactions during the fabrication of composites. Treating electronic grade FR-4 and polyimide with the He/O2 plasma for a few seconds changed the substrate surface from hydrophobic to hydrophilic, which allowed complete wetting of the surface by epoxy in underfill applications. Characterization of the surface by X-ray photoelectron spectroscopy shows formation of oxygenated functional groups, including hydroxyl, carbonyl, and carboxyl groups, on the polymer surface after plasma treatment. The resulting strength of the bond based on lap-shear and T-peel tests correlates well with the concentration of oxygen on the polymer surface. The failure modes observed for lap-shear and T-peel tests changed from interfacial to cohesive after the plasma activation. Treating carbon-fiber-reinforced epoxy composites with the atmospheric plasma resulted in the removal of fluorinated contaminants in shallow surface layers. For contaminants that diffused deeply into the composite surface, mechanical abrasion was needed in addition to the plasma treatment to remove the impurities. While cleaning the composite, plasma also generated active oxygen groups on the substrate surface. The presence of these groups improved the adhesive bonding strength of the composite even in the presence of residual fluorine contaminants. Thus, it was speculated that plasma treatment can promote better polymer adhesion with or without fluorine contamination. Carbon nanotube sheets were also treated by the helium oxygen plasma, and the CNT surface turn from super hydrophobic to hydrophilic after a few seconds of exposure. The nanotube surface contained 15% of oxygen in the form of hydroxyl groups. Chemical coupling agents were added to the plasma activated CNT surfaces in order to crosslink the CNTs and to create bonding sites for the resin matrix. Stretched, activated and functionalized CNT was cured with dicyclopentadiene (DCPD) to produce a sheet composite with a tensile strength of 636 MPa, a modulus of 28 GPa, and a density of 1.4 g/cm 3. This may be compared to aerospace-grade aluminum with tensile strength of 572 MPa, modulus of 72 GPa, and density of 2.7 g/cm3. This work demonstrates that new high-strength composite can be produced with the use of atmospheric plasma activation and chemical crosslinking of the fiber matrix.

The critical size of focal articular cartilage defects is associated with strains in the collagen fibers.

PubMed

Heuijerjans, A; Wilson, W; Ito, K; van Donkelaar, C C

2017-12-01

The size of full-thickness focal cartilage defect is accepted to be predictive of its fate, but at which size threshold treatment is required is unclear. Clarification of the mechanism behind this threshold effect will help determining when treatment is required. The objective was to investigate the effect of defect size on strains in the collagen fibers and the non-fibrillar matrix of surrounding cartilage. These strains may indicate matrix disruption. Tissue deformation into the defect was expected, stretching adjacent superficial collagen fibers, while an osteochondral implant was expected to prevent these deformations. Finite element simulations of cartilage/cartilage contact for intact, 0.5 to 8mm wide defects and 8mm implant cases were performed. Impact, a load increase to 2MPa in 1ms, and creep loading, a constant load of 0.5MPa for 900s, scenarios were simulated. A composition-based material model for articular cartilage was employed. Impact loading caused low strain levels for all models. Creep loading increased deviatoric strains and collagen strains in the surrounding cartilage. Deviatoric strains increased gradually with defect size, but the surface area at which collagen fiber strains exceeded failure thresholds, abruptly increased for small increases of defect size. This was caused by a narrow distribution of collagen fiber strains resulting from the non-linear stiffness of the fibers. We postulate this might be the mechanism behind the existence of a critical defect size. Filling of the defect with an implant reduced deviatoric and collagen fiber strains towards values for intact cartilage. Copyright © 2017 Elsevier Ltd. All rights reserved.

Cell proliferation on PVA/sodium alginate and PVA/poly(γ-glutamic acid) electrospun fiber.

PubMed

Yang, Jen Ming; Yang, Jhe Hao; Tsou, Shu Chun; Ding, Chian Hua; Hsu, Chih Chin; Yang, Kai Chiang; Yang, Chun Chen; Chen, Ko Shao; Chen, Szi Wen; Wang, Jong Shyan

2016-09-01

To overcome the obstacles of easy dissolution of PVA nanofibers without crosslinking treatment and the poor electrospinnability of the PVA cross-linked nanofibers via electrospinning process, the PVA based electrospun hydrogel nanofibers are prepared with post-crosslinking method. To expect the electrospun hydrogel fibers might be a promising scaffold for cell culture and tissue engineering applications, the evaluation of cell proliferation on the post-crosslinking electrospun fibers is conducted in this study. At beginning, poly(vinyl alcohol) (PVA), PVA/sodium alginate (PVASA) and PVA/poly(γ-glutamic acid) (PVAPGA) electrospun fibers were prepared by electrospinning method. The electrospun PVA, PVASA and PVAPGA nanofibers were treated with post-cross-linking method with glutaraldehyde (Glu) as crosslinking agent. These electrospun fibers were characterized with thermogravimetry analysis (TGA) and their morphologies were observed with a scanning electron microscope (SEM). To support the evaluation and explanation of cell growth on the fiber, the study of 3T3 mouse fibroblast cell growth on the surface of pure PVA, SA, and PGA thin films is conducted. The proliferation of 3T3 on the electrospun fiber surface of PVA, PVASA, and PVAPGA was evaluated by seeding 3T3 fibroblast cells on these crosslinked electrospun fibers. The cell viability on electrospun fibers was conducted with water-soluble tetrazolium salt-1 assay (Cell Proliferation Reagent WST-1). The morphology of the cells on the fibers was also observed with SEM. The results of WST-1 assay revealed that 3T3 cells cultured on different electrospun fibers had similar viability, and the cell viability increased with time for all electrospun fibers. From the morphology of the cells on electrospun fibers, it is found that 3T3 cells attached on all electrospun fiber after 1day seeded. Cell-cell communication was noticed on day 3 for all electrospun fibers. Extracellular matrix (ECM) productions were found and cell-ECM adhesion was shown on day 7. The cell number was also increased on all of the crosslinked electrospun fibers. It seems that the PVA based electrospun hydrogel nanofibers prepared with post-crosslinking method can be used as scaffold for tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

Mechanical interlocking of cotton fibers on slightly textured surfaces of metallic cylinders

PubMed Central

Zhang, Youqiang; Tian, Yu; Meng, Yonggang

2016-01-01

Mechanical interlocking is widely applied in industry and general lives of human beings. In this work, we realized the control of locking or sliding states of cotton fibers on the metal surfaces with slightly different textures through traditional machining. Three types of sliding states, i.e., locking, one-way sliding, and two-way sliding have been achieved. It is found that the locking or sliding of the cotton fibers on the metallic cylinder depends on the friction coefficient and the ratio of cotton fiber diameter, 2r, to the height of the rough peaks, h, of metal surfaces. When the critical ratio h/r exceeds 1, the cotton fibers could tightly attach to the metallic surface through mechanical interlocking. This work provided a convenient and universal method for the control of interlocking or sliding of fiber-based materials on textured surfaces. PMID:27156720

Influence on proliferation and adhesion of human gingival fibroblasts from different titanium surface decontamination treatments: An in vitro study.

PubMed

Cao, Jie; Wang, Tong; Pu, Yinfei; Tang, Zhihui; Meng, Huanxin

2018-03-01

To investigate the effects of different decontamination treatments on microstructure of titanium (Ti) surface as well as proliferation and adhesion of human gingival fibroblasts (HGFs). Ti discs with machined (M) and sand blasted, acid etched (SAE) surfaces were treated with five different decontamination treatments: (1) stainless steel curette (SSC), ultrasonic system with (2) straight carbon fiber tip (UCF) or (3) metal tip (UM), (4) rotating Ti brush (RTB), and (5) Er:YAG laser (30 mJ/pulse at 30 Hz). Surface roughness was analyzed under optical interferometry. HGFs were cultured on each disc. Proliferation and adhesive strength were analyzed. qRT-PCR and ELISA were performed to detect the RNA and protein expression of FAK, ITGB1, COL1A1, and FN1 respectively from different Ti surfaces. Surface roughness increased on M surface. Proliferation, adhesive strength and gene expression were higher on M surface than SAE surface. Decontamination treatments affected surface parameters significantly (P < 0.001), making M surface less smooth while SAE surface became less rough. SSC, UCF, UM and RTB decreased proliferation on M surfaces significantly (P < 0.05). UCF, RTB and laser increased proliferation on SAE surface significantly (P < 0.05). UM decreased adhesive strength on M surface significantly and laser increased adhesive strength on SAE surface significantly (P < 0.05). Gene expression increased with time and was altered by decontamination treatments significantly (P < 0.001). Decontamination treatments influence surface roughness and cell behavior of HGFs. Laser might be an optimal decontamination treatment which has the least negative effect on M surface and the most positive effect on SAE surface. Copyright © 2017 Elsevier Ltd. All rights reserved.

Surface characterization of carbon fiber polymer composites and aluminum alloys after laser interference structuring

DOE PAGES

Sabau, Adrian S.; Greer, Clayton M.; Chen, Jian; ...

2016-05-03

Here, the increasing use of Carbon Fiber-reinforced Polymer matrix Composites (CFPC) and aluminum alloys as lightweight materials in the automotive and aerospace industries demands enhanced surface preparation and control of surface morphology prior to joining. In this study, surfaces of both composite and aluminum were prepared for joining using an Nd:YAG laser in a two-beam interference setup, enabling the (a) structuring of the AL 5182 surface, (b) removal of the resin layer on top of carbon fibers, and (c) structuring of the carbon fibers. CFPC specimens of T700S carbon fiber, Prepreg - T8 3 epoxy, 5 ply thick, 0/90o plaquesmore » were used. The effect of laser fluence, scanning speed, and number of shots-per-spot was investigated on the removal rate of the resin without an excessive damage of the fibers. Optical micrographs, 3D imaging, and scanning electron microscope (SEM) imaging were used to study the effect of the laser processing on surface morphology.« less

Preparation of thick silica coatings on carbon fibers with fine-structured silica nanotubes induced by a self-assembly process

PubMed Central

Baumgärtner, Benjamin; Möller, Hendrik; Neumann, Thomas

2017-01-01

A facile method to coat carbon fibers with a silica shell is presented in this work. By immobilizing linear polyamines on the carbon fiber surface, the high catalytic activity of polyamines in the sol–gel-processing of silica precursors is used to deposit a silica coating directly on the fiber’s surface. The surface localization of the catalyst is achieved either by attaching short-chain polyamines (e.g., tetraethylenepentamine) via covalent bonds to the carbon fiber surface or by depositing long-chain polyamines (e.g., linear poly(ethylenimine)) on the carbon fiber by weak non-covalent bonding. The long-chain polyamine self-assembles onto the carbon fiber substrate in the form of nanoscopic crystallites, which serve as a template for the subsequent silica deposition. The silicification at close to neutral pH is spatially restricted to the localized polyamine and consequently to the fiber surface. In case of the linear poly(ethylenimine), silica shells of several micrometers in thickness can be obtained and their morphology is easily controlled by a considerable number of synthesis parameters. A unique feature is the hierarchical biomimetic structure of the silica coating which surrounds the embedded carbon fiber by fibrillar and interconnected silica fine-structures. The high surface area of the nanostructured composite fiber may be exploited for catalytic applications and adsorption purposes. PMID:28685115

Optoacoustic imaging of tissue blanching during photodynamic therapy of esophageal cancer

NASA Astrophysics Data System (ADS)

Jacques, Steven L.; Viator, John A.; Paltauf, Guenther

2000-05-01

Esophageal cancer patients often present a highly inflamed esophagus at the time of treatment by photodynamic therapy. Immediately after treatment, the inflamed vessels have been shut down and the esophagus presents a white surface. Optoacoustic imaging via an optical fiber device can provide a depth profile of the blanching of inflammation. Such a profile may be an indicator of the depth of treatment achieved by the PDT. Our progress toward developing this diagnostic for use in our clinical PDT treatments of esophageal cancer patients is presented.

Design, construction and operation of a new filter approach for treatment of surface waters in Southeast Asia

NASA Astrophysics Data System (ADS)

Frankel, R. J.

1981-05-01

A simple, inexpensive, and efficient method of water treatment for rural communities in Southeast Asia was developed using local materials as filter media. The filter utilizes coconut fiber and burnt rice husks in a two-stage filtering process designed as a gravityfed system without the need for backwashing, and eliminates in most cases the need of any chemicals. The first-stage filter with coconut fiber acts essentially as a substitute for the coagulation and sedimentation phases of conventional water-treatment plants. The second-stage filter, using burnt rice husks, is similar to slow sand filtration with the additional benefits of taste, color and odor removals through the absorption properties of the activated carbon in the medium. This paper reports on the design, construction costs, and operating results of several village size units in Thailand and in the Philippines.

Optical fiber head for providing lateral viewing

DOEpatents

Everett, Matthew J.; Colston, Billy W.; James, Dale L.; Brown, Steve; Da Silva, Luiz

2002-01-01

The head of an optical fiber comprising the sensing probe of an optical heterodyne sensing device includes a planar surface that intersects the perpendicular to axial centerline of the fiber at a polishing angle .theta.. The planar surface is coated with a reflective material so that light traveling axially through the fiber is reflected transverse to the fiber's axial centerline, and is emitted laterally through the side of the fiber. Alternatively, the planar surface can be left uncoated. The polishing angle .theta. must be no greater than 39.degree. or must be at least 51.degree.. The emitted light is reflected from adjacent biological tissue, collected by the head, and then processed to provide real-time images of the tissue. The method for forming the planar surface includes shearing the end of the optical fiber and applying the reflective material before removing the buffer that circumscribes the cladding and the core.

Surface characterization and chemical analysis of bamboo substrates pretreated by alkali hydrogen peroxide.

PubMed

Song, Xueping; Jiang, Yan; Rong, Xianjian; Wei, Wei; Wang, Shuangfei; Nie, Shuangxi

2016-09-01

The surface characterization and chemical analysis of bamboo substrates by alkali hydrogen peroxide pretreatment (AHPP) were investigated in this study. The results tended to manifest that AHPP prior to enzymatic and chemical treatment was potential for improving accessibility and reactivity of bamboo substrates. The inorganic components, organic solvent extractives and acid-soluble lignin were effectively removed by AHPP. X-ray photoelectron spectroscopy (XPS) analysis indicated that the surface of bamboo chips had less lignin but more carbohydrate after pre-treatment. Fiber surfaces became etched and collapsed, and more pores and debris on the substrate surface were observed with Scanning Electron Microscopy (SEM). Brenauer-Emmett-Teller (BET) results showed that both of pore volume and surface area were increased after AHPP. Although XRD analysis showed that AHPP led to relatively higher crystallinity, pre-extraction could overall enhance the accessibility of enzymes and chemicals into the bamboo structure. Copyright © 2016. Published by Elsevier Ltd.

Micro-LiDAR velocity, temperature, density, concentration sensor

NASA Technical Reports Server (NTRS)

Dorrington, Adrian A. (Inventor); Danehy, Paul M. (Inventor)

2010-01-01

A light scatter sensor includes a sensor body in which are positioned a plurality of optical fibers. The sensor body includes a surface, in one end of each of the optical fibers terminates at the surface of the sensor body. One of the optical fibers is an illumination fiber for emitting light. A plurality of second optical fibers are collection fibers for collecting scattered light signals. A light sensor processor is connected to the collection fibers to detect the scattered light signals.

High-temperature effects on the light transmission through sapphire optical fiber

DOE PAGES

Wilson, Brandon A.; Petrie, Christian M.; Blue, Thomas E.

2018-03-13

Single crystal sapphire optical fiber was tested at high temperatures (1500°C) to determine its suitability for optical instrumentation in high-temperature environments. Broadband light transmission (450-2300 nm) through sapphire fiber was measured as a function of temperature as a test of the fiber's ability to survive and operate in high-temperature environments. Upon heating sapphire fiber to 1400°C, large amounts of light attenuation were measured across the entire range of light wavelengths that were tested. SEM and TEM images of the heated sapphire fiber indicated that a layer had formed at the surface of the fiber, most likely due to a chemicalmore » change at high temperatures. The microscopy results suggest that the surface layer may be in the form of aluminum hydroxide. Subsequent tests of sapphire fiber in an inert atmosphere showed minimal light attenuation at high temperatures along with the elimination of any surface layers on the fiber, indicating that the air atmosphere is indeed responsible for the increased attenuation and surface layer formation at high temperatures.« less

High-temperature effects on the light transmission through sapphire optical fiber

DOE Office of Scientific and Technical Information (OSTI.GOV)

Wilson, Brandon A.; Petrie, Christian M.; Blue, Thomas E.

Single crystal sapphire optical fiber was tested at high temperatures (1500°C) to determine its suitability for optical instrumentation in high-temperature environments. Broadband light transmission (450-2300 nm) through sapphire fiber was measured as a function of temperature as a test of the fiber's ability to survive and operate in high-temperature environments. Upon heating sapphire fiber to 1400°C, large amounts of light attenuation were measured across the entire range of light wavelengths that were tested. SEM and TEM images of the heated sapphire fiber indicated that a layer had formed at the surface of the fiber, most likely due to a chemicalmore » change at high temperatures. The microscopy results suggest that the surface layer may be in the form of aluminum hydroxide. Subsequent tests of sapphire fiber in an inert atmosphere showed minimal light attenuation at high temperatures along with the elimination of any surface layers on the fiber, indicating that the air atmosphere is indeed responsible for the increased attenuation and surface layer formation at high temperatures.« less

An interferometer having fused optical fibers, and apparatus and method using the interferometer

NASA Technical Reports Server (NTRS)

Hellbaum, Richard F. (Inventor); Claus, Richard O. (Inventor); Murphy, Kent A. (Inventor); Gunther, Michael F. (Inventor)

1992-01-01

An interferometer includes a first optical fiber coupled to a second optical fiber by fusing. At a fused portion, the first and second optical fibers are cut to expose respective cores. The cut or fused end of the first and second optical fibers is arranged to oppose a diaphragm or surface against which a physical phenomenon such as pressure or stress, is applied. In a first embodiment, a source light which is generally single-mode monochromatic, coherent light, is input to the first optical fiber and by evanescence, effectively crosses to the second optical fiber at the fused portion. Source light from the second optical fiber is reflected by the diaphragm or surface, and received at the second optical fiber to generate an output light which has an intensity which depends upon interference of reference light based on the source light, and the reflected light reflected from the diaphragm or surface. The intensity of the output light represents a positional relationship or displacement between the interferometer and the diaphragm or surface.

Evaluation of Mechanical Properties of Glass Fiber Posts Subjected to Laser Surface Treatments.

PubMed

Barbosa Siqueira, Carolina; Spadini de Faria, Natália; Raucci-Neto, Walter; Colucci, Vivian; Alves Gomes, Erica

2016-10-01

The aim of this study was to evaluate the influence of laser irradiation on flexural strength, elastic modulus, and surface roughness and morphology of glass fiber posts (GFPs). Laser treatment of GFPs has been introduced to improve its adhesion properties. A total of 40 GFPs were divided into 4 groups according to the irradiation protocol: GC-no irradiation, GYAG-irradiation with erbium:yttrium-aluminum-garnet [Er:YAG], GCR-irradiation with erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG), and GDI-irradiation with diode laser. The GFP roughness and morphology were evaluated through laser confocal microscopy before and after surface treatment. Three-point bending flexural test measured flexural strength and elastic modulus. Data about elastic modulus and flexural strength were subjected to one-way ANOVA and Bonferroni test (p < 0.05). The effect of roughness was evaluated using the linear mixed effects model and Bonferroni test (p < 0.05). Laser treatment changed surface roughness in the groups GCR (p = 0.000) and GDI (p = 0.007). The mean flexural strength in GYAG (995.22 MPa) was similar to that in GC (980.48 MPa) (p = 1.000) but different from that in GCR (746.83 MPa) and that in GDI (691.34 MPa) (p = 0.000). No difference was found between the groups GCR and GDI (p = 0.86). For elastic modulus: GYAG (24.47 GPa) was similar to GC (25.92 GPa) (p = 1.000) but different from GCR (19.88 GPa) (p = 0.002) and GDI (17.20 GPa) (p = 0.000). The different types of lasers, especially Er,Cr:YSGG and 980 ηm diode, influenced the mechanical properties of GFPs.

Laser surface treatment of porous ceramic substrate for application in solid oxide fuel cells

NASA Astrophysics Data System (ADS)

Mahmod, D. S. A.; Khan, A. A.; Munot, M. A.; Glandut, N.; Labbe, J. C.

2016-08-01

Laser has offered a large number of benefits for surface treatment of ceramics due to possibility of localized heating, very high heating/cooling rates and possibility of growth of structural configurations only produced under non-equilibrium high temperature conditions. The present work investigates oxidation of porous ZrB2-SiC sintered ceramic substrates through treatment by a 1072 ± 10 nm ytterbium fiber laser. A multi-layer structure is hence produced showing successively oxygen rich distinct layers. The porous bulk beneath these layers remained unaffected as this laser-formed oxide scale and protected the substrate from oxidation. A glassy SiO2 structure thus obtained on the surface of the substrate becomes subject of interest for further research, specifically for its utilization as solid protonic conductor in Solid Oxide Fuel Cells (SOFCs).

Measuring the wetting angle and perimeter of single wood pulp fibers : a modified method

Treesearch

John H. Klungness

1981-01-01

In pulp processing development it is often necessary to measure the effect of a process variable on individual pulp fiber wettability. Such processes would include drying of market pulps, recycling of secondary fibers, and surface modification of fibers as in sizing. However, if wettability is measured on a fiber sheet surface, the results are confounded by...

Influence of heating procedures on the surface structure of stabilized polyacrylonitrile fibers

NASA Astrophysics Data System (ADS)

Zhao, Rui-Xue; Sun, Peng-fei; Liu, Rui-jian; Ding, Zhan-hui; Li, Xiang-shan; Liu, Xiao-yang; Zhao, Xu-dong; Gao, Zhong-min

2018-03-01

The stabilized polyacrylonitrile (PAN) fibers were obtained after heating the precursor PAN fibers under air atmosphere by different procedures. The surface structures and compositions of as-prepared stabilized PAN fibers have been investigated by SEM, SSNMR, XPS and Raman spectroscopy. The results show that 200 °C, 220 °C, 250 °C, and 280 °C are key temperatures for the preparation of stabilized PAN fibers. The effect of heating gradient on the structure of stabilized PAN fibers has been studied. The possible chemical structural formulas for the PAN fibers is provided, which include the stable and unstable structure. The stable structure (α-type) could endure the strong chemical reactions and the unstable structure (β- or γ-type) could mitigate the drastic oxidation reactions. The inferences of chemical formula of stabilized PAN fibers are benefit to the design of appropriate surface structure for the production for high quality carbon fibers.

Analytical thermal resistance model for high power double-clad fiber on rectangular plate with convective cooling at upper and lower surfaces

NASA Astrophysics Data System (ADS)

Lv, Yi; Zheng, Huai; Liu, Sheng

2018-07-01

Whether convective heat transfer on the upper surface of the substrate is used or not, the thermal resistance network models of optical fiber embedded in the substrate are established in this research. These models are applied to calculate the heat dissipation in a high power ytterbium doped double-clad fiber (YDCF) power amplifier. Firstly, the temperature values of two points on the fiber are tested when there is no convective heat transfer on the upper surface. Then, the numerical simulation is used to verify the temperature change of the fiber with the effective convective heat transfer coefficient of the lower surface heff increasing when the upper surface is subjected to three loading conditions with hu as 1, 5 and 15 W/(m2 K), respectively. The axial temperature distribution of the optical fiber is also presented at four different values for hu when heff is 30 W/(m2 K). Absolute values of the relative errors are less than 7.08%. The results show that the analytical models can accurately calculate the temperature distribution of the optical fiber when the fiber is encapsulated into the substrate. The corresponding relationship is helpful to further optimize packaging design of the fiber cooling system.

Dispersion of cellulose nanofibers in biopolymer based nanocomposites

NASA Astrophysics Data System (ADS)

Wang, Bei

The focus of this work was to understand the fundamental dispersion mechanism of cellulose based nanofibers in bionanocomposites. The cellulose nanofibers were extracted from soybean pod and hemp fibers by chemo-mechanical treatments. These are bundles of cellulose nanofibers with a diameter ranging between 50 to 100 nm and lengths of thousands of nanometers which results in very high aspect ratio. In combination with a suitable matrix polymer, cellulose nanofiber networks show considerable potential as an effective reinforcement for high quality specialty applications of bio-based nanocomposites. Cellulose fibrils have a high density of --OH groups on the surface, which have a tendency to form hydrogen bonds with adjacent fibrils, reducing interaction with the surrounding matrix. The use of nanofibers has been mostly restricted to water soluble polymers. This thesis is focused on synthesizing the nanocomposite using a solid phase matrix polypropylene (PP) or polyethylene (PE) by hot compression and poly (vinyl alcohol) (PVA) in an aqueous phase by film casting. The mechanical properties of nanofiber reinforced PVA film demonstrated a 4-5 fold increase in tensile strength, as compared to the untreated fiber-blend-PVA film. It is necessary to reduce the entanglement of the fibrils and improve their dispersion in the matrix by surface modification of fibers without deteriorating their reinforcing capability. Inverse gas chromatography (IGC) was used to explore how various surface treatments would change the dispersion component of surface energy and acid-base character of cellulose nanofibers and the effect of the incorporation of these modified nanofibers into a biopolymer matrix on the properties of their nano-composites. Poly (lactic acid) (PLA) and polyhydroxybutyrate (PHB) based nanocomposites using cellulose nanofibers were prepared by extrusion, injection molding and hot compression. The IGC results indicated that styrene maleic anhydride coated and ethylene-acrylic acid coated fibers improved their potential to interact with both acidic and basic resins. From transmission electron micrograph, it was shown that the nanofibers were partially dispersed in the polymer matrix. The mechanical properties of the nanocomposites were lower than those predicted by theoretical calculations for both nanofiber reinforced biopolymers.

[INVITED] Recent advances in surface plasmon resonance based fiber optic chemical and biosensors utilizing bulk and nanostructures

NASA Astrophysics Data System (ADS)

Gupta, Banshi D.; Kant, Ravi

2018-05-01

Surface plasmon resonance has established itself as an immensely acclaimed and influential optical sensing tool with quintessential applications in life sciences, environmental monitoring, clinical diagnostics, pharmaceutical developments and ensuring food safety. The implementation of sensing principle of surface plasmon resonance employing an optical fiber as a substrate has concomitantly resulted in the evolution of fiber optic surface plasmon resonance as an exceptionally lucrative scaffold for chemical and biosensing applications. This perspective article outlines the contemporary studies on fiber optic sensors founded on the sensing architecture of propagating as well as localized surface plasmon resonance. An in-depth review of the prevalent analytical and surface chemical tactics involved in configuring the sensing layer over an optical fiber for the detection of various chemical and biological entities is presented. The involvement of nanomaterials as a strategic approach to enhance the sensor sensitivity is furnished concurrently providing an insight into the diverse geometrical blueprints for designing fiber optic sensing probes. Representative examples from the literature are discussed to appreciate the latest advancements in this potentially valuable research avenue. The article concludes by identifying some of the key challenges and exploring the opportunities for expanding the scope and impact of surface plasmon resonance based fiber optic sensors.

Optical fiber sensor based on surface plasmon resonance for rapid detection of avian influenza virus subtype H6: Initial studies.

PubMed

Zhao, Xihong; Tsao, Yu-Chia; Lee, Fu-Jung; Tsai, Woo-Hu; Wang, Ching-Ho; Chuang, Tsung-Liang; Wu, Mu-Shiang; Lin, Chii-Wann

2016-07-01

A side-polished fiber optic surface plasmon resonance (SPR) sensor was fabricated to expose the core surface and then deposited with a 40 nm thin gold film for the near surface sensing of effective refractive index changes with surface concentration or thickness of captured avian influenza virus subtype H6. The detection surface of the SPR optical fiber sensor was prepared through the plasma modification method for binding a self-assembled monolayer of isopropanol chemically on the gold surface of the optical fiber. Subsequently, N-(3-dimethylaminopropyl)-N'-ethylcarbodiimide/N-hydroxysuccinimide was activated to enable EB2-B3 monoclonal antibodies to capture A/chicken/Taiwan/2838V/00 (H6N1) through a flow injection system. The detection limit of the fabricated optical fiber sensor for A/chicken/Taiwan/2838V/00 was 5.14 × 10(5) EID50/0.1 mL, and the response time was 10 min on average. Moreover, the fiber optic sensor has the advantages of a compact size and low cost, thus rendering it suitable for online and remote sensing. The results indicated that the optical fiber sensor can be used for epidemiological surveillance and diagnosing of avian influenza subtype H6 rapidly. Copyright © 2016 Elsevier B.V. All rights reserved.

The Effects of Fiber Inclusion on Pet Food Sensory Characteristics and Palatability.

PubMed

Koppel, Kadri; Monti, Mariana; Gibson, Michael; Alavi, Sajid; Donfrancesco, Brizio Di; Carciofi, Aulus Cavalieri

2015-02-16

The objectives of this study were to determine (a) the influence of fiber on the sensory characteristics of dry dog foods; (b) differences of coated and uncoated kibbles for aroma and flavor characteristics; (c) palatability of these dry dog foods; and (d) potential associations between palatability and sensory attributes. A total of eight fiber treatments were manufactured: a control (no fiber addition), guava fiber (3%, 6%, and 12%), sugar cane fiber (9%; large and small particle size), and wheat bran fiber (32%; large and small particle size). The results indicated significant effects of fibers on both flavor and texture properties of the samples. Bitter taste and iron and stale aftertaste were examples of flavor attributes that differed with treatment, with highest intensity observed for 12% guava fiber and small particle size sugar cane fiber treatments. Fracturability and initial crispness attributes were lowest for the sugar cane fiber treatments. Flavor of all treatments changed after coating with a palatant, increasing in toasted, brothy, and grainy attributes. The coating also had a masking effect on aroma attributes such as stale, flavor attributes such as iron and bitter taste, and appearance attributes such as porosity. Palatability testing results indicated that the control treatment was preferred over the sugar cane or the wheat bran treatment. The treatment with large sugarcane fiber particles was preferred over the treatment with small particles, while both of the wheat bran treatments were eaten at a similar level. Descriptive sensory analysis data, especially textural attributes, were useful in pinpointing the underlying characteristics and were considered to be reasons that may influence palatability of dog foods manufactured with inclusion of different fibers.

Surface Properties of PEMFC Gas Diffusion Layers

DOE Office of Scientific and Technical Information (OSTI.GOV)

WoodIII, David L; Rulison, Christopher; Borup, Rodney

2010-01-01

The wetting properties of PEMFC Gas Diffusion Layers (GDLs) were quantified by surface characterization measurements and modeling of material properties. Single-fiber contact-angle and surface energy (both Zisman and Owens-Wendt) data of a wide spectrum of GDL types is presented to delineate the effects of hydrophobic post-processing treatments. Modeling of the basic sessile-drop contact angle demonstrates that this value only gives a fraction of the total picture of interfacial wetting physics. Polar forces are shown to contribute 10-20 less than dispersive forces to the composite wetting of GDLs. Internal water contact angles obtained from Owens-Wendt analysis were measured at 13-19 highermore » than their single-fiber counterparts. An inverse relationship was found between internal contact angle and both Owens-Wendt surface energy and % polarity of the GDL. The most sophisticated PEMFC mathematical models use either experimentally measured capillary pressures or the standard Young-Laplace capillary-pressure equation. Based on the results of the Owens-Wendt analysis, an advancement to the Young-Laplace equation is proposed for use in these mathematical models, which utilizes only solid surface energies and fractional surface coverage of fluoropolymer. Capillary constants for the spectrum of analyzed GDLs are presented for the same purpose.« less

Plasma Modification of Graphite Fibers and Its Effect on Composite Properties.

DTIC Science & Technology

1983-08-01

liquids have been difficult to measure with adequate accuracy. As a result, critical surface energy data are not readily available. A flotation method...tension of the fiber surface. However, the fiber density must always exceed the density of the flotation liquid. Although this is a very useful...technioue, it is inanplicable to graphite fiber due to its irregular surface structure, small filament diameter and small difference in density with flotation

Apparatus and process for the surface treatment of carbon fibers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Paulauskas, Felix Leonard; Ozcan, Soydan; Naskar, Amit K.

A method for surface treating a carbon-containing material in which carbon-containing material is reacted with decomposing ozone in a reactor (e.g., a hollow tube reactor), wherein a concentration of ozone is maintained throughout the reactor by appropriate selection of at least processing temperature, gas stream flow rate, reactor dimensions, ozone concentration entering the reactor, and position of one or more ozone inlets (ports) in the reactor, wherein the method produces a surface-oxidized carbon or carbon-containing material, preferably having a surface atomic oxygen content of at least 15%. The resulting surface-oxidized carbon material and solid composites made therefrom are also described.

Multipoint photonic doppler velocimetry using optical lens elements

DOEpatents

Frogget, Brent Copely; Romero, Vincent Todd

2014-04-29

A probe including a fisheye lens is disclosed to measure the velocity distribution of a moving surface along many lines of sight. Laser light, directed to the surface and then reflected back from the surface, is Doppler shifted by the moving surface, collected into fisheye lens, and then directed to detection equipment through optic fibers. The received light is mixed with reference laser light and using photonic Doppler velocimetry, a continuous time record of the surface movement is obtained. An array of single-mode optical fibers provides an optic signal to an index-matching lens and eventually to a fisheye lens. The fiber array flat polished and coupled to the index-matching lens using index-matching gel. Numerous fibers in a fiber array project numerous rays through the fisheye lens which in turn project many measurement points at numerous different locations to establish surface coverage over a hemispherical shape with very little crosstalk.

Enzyme-enhanced fluorescence detection of DNA on etched optical fibers.

PubMed

Niu, Shu-yan; Li, Quan-yi; Ren, Rui; Zhang, Shu-sheng

2009-05-15

A novel DNA biosensor based on enzyme-enhanced fluorescence detection on etched optical fibers was developed. The hybridization complex of DNA probe and biotinylated target was formed on the etched optical fiber, and was then bound with streptavidin labeled horseradish peroxidase (streptavidin-HRP). The target DNA was quantified through the fluorescent detection of bi-p,p'-4-hydroxyphenylacetic acid (DBDA) generated from the substrate 4-hydroxyphenylacetic acid (p-HPA) under the catalysis of HRP, with a detection limit of 1 pM and a linear range from 1.69 pM to 169 pM. It is facile to regenerate this sensor through surface treatment with concentrated urea solution. It was discovered that the sensor can retain 70% of its original activity after three detection-regeneration cycles.

Evaluating the effect of some mechanical properties for chemically treated various natural fibers reinforced polyester composite

NASA Astrophysics Data System (ADS)

Salih, Wafaa Mahdi; Abdulkader, Niveen Jamal; Salih, Sana Mahdi

2018-05-01

This research were studied the effect of some mechanical properties for composite materials reinforced fiber and prepared from material (polyester with various natural fibers) then studied the effect of chemical treatment on the same fiber immerse in 10% NaOH solution for half an hour and then compared, the results of the same test of composite materials without and with chemical treatment and the results proved that there is a clear effect when treat the fiber compared to non-chemical treatment of the fibers also noted that hemp fibers loaded the stress higher than other fibers for both cases to distinguish them that the hemp fiber has continuous fibers either the other fibers are characterized by the type of cross linking or chopped types in tensile test, and the results of the same test of composite materials without and with chemical treatment and the results proved that the hardness of the fiber composite while the treated fiber composite samples better than the untreated fiber, and from the figures the palm leaf has the highest value than lufa fiber, hemp fiber and the smallest value is in sisal fiber because of the nature of formation fibers materials.

Development of a TiO2 modified optical fiber electrode and its incorporation into a photoelectrochemical reactor for wastewater treatment.

PubMed

Esquivel, K; Arriaga, L G; Rodríguez, F J; Martínez, L; Godínez, Luis A

2009-08-01

Electrochemical advanced oxidation processes (EAOPs) are used to chemically burn non biodegradable complex organic compounds that are present in polluted effluents. A common approach involves the use of TiO2 semiconductor substrates as either photocatalytic or photoelectrocatalytic materials in reactors that produce a powerful oxidant (hydroxyl radical) that reacts with pollutant species. In this context, the purpose of this work is to develop a new TiO2 based photoanode using an optic fiber support. The novel arrangement of a TiO2 layer positioned on top of a surface modified optical fiber substrate, allowed the construction of a photoelectrochemical reactor that works on the basis of an internally illuminated approach. In this way, a semi-conductive optical fiber modified surface was prepared using 30 microm thickness SnO2:Sb films on which the photoactive TiO2 layer was electrophoretically deposited. UV light transmission experiments were conducted to evaluate the transmittance along the optical fiber covered with SnO2:Sb and TiO2 showing that 43% of UV light reached the optical fiber tip. With different illumination configurations (external or internal), it was possible to get an increase in the amount of photo-generated H(2)O(2) close to 50% as compared to different types of TiO2 films. Finally, the electro-Fenton photoelectrocatalytic Oxidation process studied in this work was able to achieve total color removal of Azo orange II dye (15 mg L(-1)) and a 57% removal of total organic carbon (TOC) within 60 min of degradation time.

Fast and Exact Fiber Surfaces for Tetrahedral Meshes.

PubMed

Klacansky, Pavol; Tierny, Julien; Carr, Hamish; Zhao Geng

2017-07-01

Isosurfaces are fundamental geometrical objects for the analysis and visualization of volumetric scalar fields. Recent work has generalized them to bivariate volumetric fields with fiber surfaces, the pre-image of polygons in range space. However, the existing algorithm for their computation is approximate, and is limited to closed polygons. Moreover, its runtime performance does not allow instantaneous updates of the fiber surfaces upon user edits of the polygons. Overall, these limitations prevent a reliable and interactive exploration of the space of fiber surfaces. This paper introduces the first algorithm for the exact computation of fiber surfaces in tetrahedral meshes. It assumes no restriction on the topology of the input polygon, handles degenerate cases and better captures sharp features induced by polygon bends. The algorithm also allows visualization of individual fibers on the output surface, better illustrating their relationship with data features in range space. To enable truly interactive exploration sessions, we further improve the runtime performance of this algorithm. In particular, we show that it is trivially parallelizable and that it scales nearly linearly with the number of cores. Further, we study acceleration data-structures both in geometrical domain and range space and we show how to generalize interval trees used in isosurface extraction to fiber surface extraction. Experiments demonstrate the superiority of our algorithm over previous work, both in terms of accuracy and running time, with up to two orders of magnitude speedups. This improvement enables interactive edits of range polygons with instantaneous updates of the fiber surface for exploration purpose. A VTK-based reference implementation is provided as additional material to reproduce our results.

Effect of fiber-matrix adhesion on the creep behavior of CF/PPS composites: temperature and physical aging characterization

NASA Astrophysics Data System (ADS)

Motta Dias, M. H.; Jansen, K. M. B.; Luinge, J. W.; Bersee, H. E. N.; Benedictus, R.

2016-06-01

The influence of fiber-matrix adhesion on the linear viscoelastic creep behavior of `as received' and `surface modified' carbon fibers (AR-CF and SM-CF, respectively) reinforced polyphenylene sulfide (PPS) composite materials was investigated. Short-term tensile creep tests were performed on ±45° specimens under six different isothermal conditions, 40, 50, 60, 65, 70 and 75 °C. Physical aging effects were evaluated on both systems using the short-term test method established by Struik. The results showed that the shapes of the curves were affected neither by physical aging nor by the test temperature, allowing then superposition to be made. A unified model was proposed with a single physical aging and temperature-dependent shift factor, a_{T,te}. It was suggested that the surface treatment carried out in SM-CF/PPS had two major effects on the creep response of CF/PPS composites at a reference temperature of 40 °C: a lowering of the initial compliance of about 25 % and a slowing down of the creep response of about 1.1 decade.

Effects of alkali treatment on the mechanical and thermal properties of Sansevieria trifasciata fiber

NASA Astrophysics Data System (ADS)

Mardiyati, Steven, Rizkiansyah, Raden Reza; Senoaji, A.; Suratman, R.

2016-04-01

In this study, Sansevieria trifasciata fibers were treated by NaOH with concentration 1%,3%, and 5wt% at 100°C for 2 hours. Chesson-Datta methods was used to determine the lignocellulose content of raw sansevieria fibers and to investigate effect of alkali treatment on lignin content of the fiber. Mechanical properties and thermal properties of treated and untreated fibers were measured by means of tensile testing machine and thermogravimetric analysis (TGA).The cellulose and lignin contents of raw sansevieria fiber obtained from Chesson-Datta method were 56% and 6% respectively. Mechanical testing of fibers showed the increase of tensile strength from 647 MPa for raw fibers to 902 MPa for 5wt% NaOH treated fibers. TGA result showed the alkali treatment increase the thermal resistance of fibers from 288°C for raw fibers to 307°C for 5% NaOH treated fiber. It was found that alkali treatment affect the mechanical properties and thermal properties of sansevieria fibers.

Microwave and plasma-assisted modification of composite fiber surface topography

DOEpatents

Paulauskas, Felix L [Knoxville, TN; White, Terry L [Knoxville, TN; Bigelow, Timothy S [Knoxville, TN

2003-02-04

The present invention introduces a novel method for producing an undulated surface on composite fibers using plasma technology and microwave radiation. The undulated surface improves the mechanical interlocking of the fibers to composite resins and enhances the mechanical strength and interfacial sheer strength of the composites in which they are introduced.

Application of Diffuse Reflectance FT-IR Spectroscopy for the Surface Study of Kevlar Fibers

NASA Astrophysics Data System (ADS)

Chatzi, E. G.; Ishida, H.; Koenig, J. L.

1985-12-01

The surfaces of Kevlar-49 aramid fibers, being used in high-performance composite materials, have been characterized by diffuse reflectance Fourier transform infrared (FT-IR) spectroscopy. Enhancement of the surface selectivity of the technique has been achieved using KBr overlayers. The water absorbed by both the skin and the core of the fibers has been characterized by using this technique and the accessibility of the fiber functional groups has been evaluated.

Theoretical Studies of Low-Loss Optical Fibers.

DTIC Science & Technology

1980-09-15

on the fiber surface. Single-mode fiber operation is of interest in communications. Marcuse has shown that surface imperfections are a strong source...0.01 very small value of a : 8A at X = 1 vim Marcuse single mode 2.7 typical value of a = 1 jim, A : 10.6 vm, af = 37 Pim surface imperfections 55...Braunstein, "Scattering Losses in Single and Polycrystalline Materials for Infrared Fiber Applications," unpublished. 5. D. Marcuse , "Mode Conversion

The Effects of Fiber Inclusion on Pet Food Sensory Characteristics and Palatability

PubMed Central

Koppel, Kadri; Monti, Mariana; Gibson, Michael; Alavi, Sajid; Donfrancesco, Brizio Di; Carciofi, Aulus Cavalieri

2015-01-01

Simple Summary The results from this research indicate that fibers have an effect on extruded pet food texture and palatability. These results may help pet food companies select ingredients for successful product formulations. Abstract The objectives of this study were to determine (a) the influence of fiber on the sensory characteristics of dry dog foods; (b) differences of coated and uncoated kibbles for aroma and flavor characteristics; (c) palatability of these dry dog foods; and (d) potential associations between palatability and sensory attributes. A total of eight fiber treatments were manufactured: a control (no fiber addition), guava fiber (3%, 6%, and 12%), sugar cane fiber (9%; large and small particle size), and wheat bran fiber (32%; large and small particle size). The results indicated significant effects of fibers on both flavor and texture properties of the samples. Bitter taste and iron and stale aftertaste were examples of flavor attributes that differed with treatment, with highest intensity observed for 12% guava fiber and small particle size sugar cane fiber treatments. Fracturability and initial crispness attributes were lowest for the sugar cane fiber treatments. Flavor of all treatments changed after coating with a palatant, increasing in toasted, brothy, and grainy attributes. The coating also had a masking effect on aroma attributes such as stale, flavor attributes such as iron and bitter taste, and appearance attributes such as porosity. Palatability testing results indicated that the control treatment was preferred over the sugar cane or the wheat bran treatment. The treatment with large sugarcane fiber particles was preferred over the treatment with small particles, while both of the wheat bran treatments were eaten at a similar level. Descriptive sensory analysis data, especially textural attributes, were useful in pinpointing the underlying characteristics and were considered to be reasons that may influence palatability of dog foods manufactured with inclusion of different fibers. PMID:26479141

DOE Office of Scientific and Technical Information (OSTI.GOV)

Kim, M; Finlay, J; Zhu, T

Purpose: Photosensitizer concentration during photodynamic therapy (PDT) is an important parameter for accurate dosimetry. Fluorescence signal can be used as a measure of photosensitizer concentration. Two methods of data acquisition were compared to an ex vivo study both for in vivo and phantom models. Methods: Fluorescence signal of commonly used photosensitizer benzoporphyrin derivative monoacid ring A (BPD) was obtained in phantoms and mouse tumors using an excitation light of 405 nm. Interstitial fluorescence signal was obtained using a side-cut fiber inserted into the tumor tissue of interest. Using a previously developed multi-fiber probe, tumor surface fluorescence measurements were also collected.more » Signals were calibrated according to optical phantoms with known sensitizer fluorescence. Optical properties for each sample were determined and the influence of different absorption and scattering properties on the fluorescence signals was investigated. Using single value decomposition of the spectra, the sensitizer concentration was determined using the two different measurement geometries. An ex vivo analysis was also performed for tumor samples to determine the sensitizer concentration. Results: The two fluorescence signals obtained from the surface multi-fiber probe and the interstitial measurements were compared and were corresponding for both phantoms and mouse models. The values obtained were comparable to the ex vivo measurements as well. Despite the difference in geometry, the surface probe measurements can still be used as a metric for determining the presence of sensitizer in small volume tumors. Conclusion: The multi-fiber contact probe can be used as a tool to measure fluorescence at the surface of the treatment area for PDT and predict sensitizer concentration throughout the tumor. This is advantageous in that the measurement does not damage any tissue. Future work will include investigating the dependence of these results on intratumor sensitizer distribution.« less

The Effect of CFRP Surface Treatment on the Splat Morphology and Coating Adhesion Strength

NASA Astrophysics Data System (ADS)

Ganesan, Amirthan; Yamada, Motohiro; Fukumoto, Masahiro

2014-01-01

Metallization of Carbon Fiber-Reinforced Polymer (CFRP) composites aggrandized their application to aircraft, automobile, and wind power industries. Recently, the metallization of CFRP surface using thermal spray technique, especially the cold spray, a solid state deposition technique, is a topic of research. However, a direct cold spray deposition on the CFRP substrate often imposes severe erosion on the surface owing to the high-impact energy of the sprayed particles. This urges the requirement of an interlayer on the CFRP surface. In the present study, the effect of surface treatment on the interlayer adhesion strength is evaluated. The CFRP samples were initially treated mechanically, chemically, and thermally and then an interlayer was developed by atmospheric plasma spray system. The quality of the coating is highly dependent on the splat taxonomy; therefore the present work also devoted to study the splat formation behavior using the splat-collection experiments, where the molten Cu particles impinged on the treated CFRP substrates. These results were correlated with the coating adhesion strength. The coating adhesion strength was measured by pull-out test. The results showed that the surface treatment, particularly the chemical treatment, was fairly successful in improving the adhesion strength.

Single mode fibers with antireflective surface structures for high power laser applications

NASA Astrophysics Data System (ADS)

Busse, Lynda E.; Florea, Catalin M.; Shaw, L. Brandon; Aggarwal, Ishwar D.; Sanghera, Jasbinder S.

2014-03-01

We present results for increased transmission of ~99.5% in the near-IR through the end faces of silica single mode fibers by creating a random antireflective microstructure etched into the end face of the fiber. We demonstrate high laser damage thresholds for these fibers with AR structured surfaces.

Control of interfaces in Al-C fibre composites

NASA Technical Reports Server (NTRS)

Warrier, S. G.; Blue, C. A.; Lin, R. Y.

1993-01-01

The interface of Al-C fiber composite was modified by coating a silver layer on the surface of carbon fibres prior to making composites, in an attempt to improve the wettability between molten aluminum and carbon fibers during infiltration. An electroless plating technique was adopted and perfected to provide a homogeneous silver coating on the carbon fiber surface. Al-C fiber composites were prepared using a liquid infiltration technique in a vacuum. It was found that silver coating promoted the wetting between aluminum and carbon fibers, particularly with polyacrylonitrile-base carbon fibers. However, due to rapid dissolution of silver in molten aluminum, it was believed that the improved infiltration was not due to the wetting behavior between molten aluminum and silver. The cleaning of the fiber surface and the preservation of the cleaned carbon surface with silver coating was considered to be the prime reason for the improved wettability. Interfacial reactions between aluminum and carbon fibers were observed. Amorphous carbon was found to react more with aluminum than graphitic carbon. This is believed to be because of the inertness of the graphitic basal planes.

Effects of heat treatment on the mechanical properties of kenaf fiber

NASA Astrophysics Data System (ADS)

Carada, Paulo Teodoro D. L.; Fujii, Toru; Okubo, Kazuya

2016-05-01

Natural fibers are utilized in various ways. One specific application of it, is in the field natural fiber composite (NFC). Considerable amount of researches are conducted in this field due to rising concerns in the harmful effects of synthetic materials to the environment. Additionally, these researches are done in order to overcome the drawbacks which limit the wide use of natural fiber. A way to improve NFC is to look into the reinforcing component (natural fiber). Treatments, which are classified as mechanical or chemical in nature, can be done in order to improve the performance of the natural fiber. The aim of this study is to assess the effects of heat treatment in the mechanical properties of kenaf fiber. In addition, the response of mechanical properties after exposure to high moisture environment of heat-treated kenaf fibers was observed. Heat treatment was done for one hour with the following heating temperatures: 140, 160, 180, and 200 °C. X-ray diffraction analysis was done to calculate the crystallinity index of kenaf fibers after heat treatment. The results showed that increase in tensile strength can be attained when kenaf fibers are heat treated at 140 °C. However, the tensile modulus showed inconsistency with respect to heat treatment temperature. The computed crystallinity index of the fiber matched the tensile strength observed in non-treated and heat-treated kenaf fibers. The results obtained in this study can be used for applications where heat treatment on kenaf fibers is needed.

Effects of heat treatment on the mechanical properties of kenaf fiber

DOE Office of Scientific and Technical Information (OSTI.GOV)

Carada, Paulo Teodoro D. L.; Fujii, Toru; Okubo, Kazuya

Natural fibers are utilized in various ways. One specific application of it, is in the field natural fiber composite (NFC). Considerable amount of researches are conducted in this field due to rising concerns in the harmful effects of synthetic materials to the environment. Additionally, these researches are done in order to overcome the drawbacks which limit the wide use of natural fiber. A way to improve NFC is to look into the reinforcing component (natural fiber). Treatments, which are classified as mechanical or chemical in nature, can be done in order to improve the performance of the natural fiber. Themore » aim of this study is to assess the effects of heat treatment in the mechanical properties of kenaf fiber. In addition, the response of mechanical properties after exposure to high moisture environment of heat-treated kenaf fibers was observed. Heat treatment was done for one hour with the following heating temperatures: 140, 160, 180, and 200 °C. X-ray diffraction analysis was done to calculate the crystallinity index of kenaf fibers after heat treatment. The results showed that increase in tensile strength can be attained when kenaf fibers are heat treated at 140 °C. However, the tensile modulus showed inconsistency with respect to heat treatment temperature. The computed crystallinity index of the fiber matched the tensile strength observed in non-treated and heat-treated kenaf fibers. The results obtained in this study can be used for applications where heat treatment on kenaf fibers is needed.« less

Relative sliding durability of two candidate high temperature oxide fiber seal materials

NASA Technical Reports Server (NTRS)

Dellacorte, Christopher; Steinetz, Bruce M.

1991-01-01

A test program to determine the relative sliding durability of two candidate ceramic fibers for high temperature sliding seal applications is described. Pin on disk tests were used to evaluate potential seal materials. Friction during the tests and fiber wear, indicated by the extent of fibers broken in a test bundle or yarn, was measured at the end of a test. In general, friction and wear increase with test temperature. This may be due to a reduction in fiber strength, a change in the surface chemistry at the fiber/counterface interface due to oxidation, adsorption and/or desorption of surface species and, to a lesser extent, an increase in counterface surface roughness due to oxidation at elevated temperatures. The relative fiber durability correlates with tensile strength indicating that tensile data, which is more readily available than sliding durability data, may be useful in predicting fiber wear behavior under various conditions. A simple model developed using dimensional analysis shows that the fiber durability is related to a dimensionless parameter which represents the ratio of the fiber strength to the fiber stresses imposed by sliding.

Biological natural retting for determining the hierarchical structuration of banana fibers.

PubMed

Gañán, Piedad; Zuluaga, Robin; Velez, Juan Manuel; Mondragon, Iñaki

2004-10-20

Extraction processes of natural fibers can be performed by different procedures that include mechanical, chemical and biological methods. Each method presents different advantages or drawbacks according to the amount of fiber produced or the quality and properties of fiber bundles obtained. In this study, biological natural retting was satisfactorily used for obtaining banana fibers from plant bunches. However, the most important contribution of this work refers to the description of the hierarchical microstructural ordering present in banana fiber bundles in both bundle surface and inner region. The chemical composition of banana fiber bundles has been evaluated by FTIR spectroscopy. Through exposure time, the fiber bundle configuration presents small variations in composition. The main changes are related to hemicellulose and pectins as they conform the outer walls of the bundle. Hierarchical helicoidal ordering in the bundle surface as well as orientation on the longitudinal axis of the bundle were observed by optical microscopy (OM) and scanning electron microscopy (SEM) for 3-4 microm surface fibers and 10-15 microm inner elementary fibers, respectively. With increasing exposure time, fiber bundle walls lose integrity, as reflected in their mechanical behavior.

Improvement of Interaction in a Composite Structure by Using a Sol-Gel Functional Coating on Carbon Fibers.

PubMed

Szczurek, Anna; Barcikowski, Michał; Leluk, Karol; Babiarczuk, Bartosz; Kaleta, Jerzy; Krzak, Justyna

2017-08-25

The modification of carbon fibers for improving adhesion between fibers and an epoxy resin in composite materials has become the focus of attention. In this work the carbon fiber coating process has been devised in a way preventing the stiffening and clumping of fibers. To improve interactions between coated fibers and a resin in composites, four types of silica coatings with different organic functional groups (3-aminopropyl-coating 1, 3-mercaptopropyl-coating 2, 2-(3,4-epoxycyclohexyl) ethyl-coating 3, methyl-coating 4) were obtained. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to distinguish the changes of a carbon fibers surface after coating deposition. The thickness of the obtained coatings, including the diversity of thickness, was determined by transmission electron microscopy (TEM). The increase in surface free energy (SFE) of modified fibers, including the distinction between the polar and dispersive parts, was examined by wettability measurements using a tensometric test. The developed coating preparation process allowed to cover fibers separately with nanoscale silica layers, which changed their morphology. The introduction of organic functional groups resulted in surface free energy changes, especially an increase in specific polar surface energy components.

Improvement of Interaction in a Composite Structure by Using a Sol-Gel Functional Coating on Carbon Fibers

PubMed Central

Barcikowski, Michał; Leluk, Karol; Babiarczuk, Bartosz; Kaleta, Jerzy

2017-01-01

The modification of carbon fibers for improving adhesion between fibers and an epoxy resin in composite materials has become the focus of attention. In this work the carbon fiber coating process has been devised in a way preventing the stiffening and clumping of fibers. To improve interactions between coated fibers and a resin in composites, four types of silica coatings with different organic functional groups (3-aminopropyl–coating 1, 3-mercaptopropyl–coating 2, 2-(3,4-epoxycyclohexyl) ethyl–coating 3, methyl–coating 4) were obtained. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) were used to distinguish the changes of a carbon fibers surface after coating deposition. The thickness of the obtained coatings, including the diversity of thickness, was determined by transmission electron microscopy (TEM). The increase in surface free energy (SFE) of modified fibers, including the distinction between the polar and dispersive parts, was examined by wettability measurements using a tensometric test. The developed coating preparation process allowed to cover fibers separately with nanoscale silica layers, which changed their morphology. The introduction of organic functional groups resulted in surface free energy changes, especially an increase in specific polar surface energy components. PMID:28841187

Surface modification of polypropylene mesh devices with cyclodextrin via cold plasma for hernia repair: Characterization and antibacterial properties

NASA Astrophysics Data System (ADS)

Sanbhal, Noor; Mao, Ying; Sun, Gang; Xu, Rui Fang; Zhang, Qian; Wang, Lu

2018-05-01

Light weight polypropylene (PP) mesh is the most widely used implant among all other synthetic meshes for hernia repair. However, infection is the complication associated to all synthetic meshes after hernia repair. Thus, to manage mesh related infection; antibacterial drug is generally loaded to surgical implants to supply drug locally in mesh implanted site. Nevertheless, PP mesh restricts the loading of antibacterial drug at operated area due to its low wettability. The aim of this study was to introduce a novel antimicrobial PP mesh modified with β-cyclodextrine (CD) and loaded with antimicrobial agent for infection prevention. A cold oxygen plasma treatment was able to activate the surfaces of polypropylene fibers, and then CD was incorporated onto the surfaces of PP fibers. Afterward, triclosan, as a model antibacterial agent, was loaded into CD cavity to provide desired antibacterial functions. The modified polypropylene mesh samples CD-Tric-1, CD-Tric-3 exhibited excellent inhibition zone and continuous antibacterial efficacy against E. coli and S. aureus up to 6 and 7 days respectively. Results of AFM, SEM, FTIR and antibacterial tests evidenced that oxygen plasma process is necessary to increase chemical connection between CD molecules and PP fibers. The samples were also characterized by using EDX, XRD, TGA, DSC and water contact angle.

Femtosecond laser-induced surface structures on carbon fibers.

PubMed

Sajzew, Roman; Schröder, Jan; Kunz, Clemens; Engel, Sebastian; Müller, Frank A; Gräf, Stephan

2015-12-15

The influence of different polarization states during the generation of periodic nanostructures on the surface of carbon fibers was investigated using a femtosecond laser with a pulse duration τ=300  fs, a wavelength λ=1025  nm, and a peak fluence F=4  J/cm². It was shown that linear polarization results in a well-aligned periodic pattern with different orders of magnitude concerning their period and an alignment parallel and perpendicular to fiber direction, respectively. For circular polarization, both types of uniform laser-induced periodic surface structures (LIPSS) patterns appear simultaneously with different dominance in dependence on the position at the fiber surface. Their orientation was explained by the polarization-dependent absorptivity and the geometrical anisotropy of the carbon fibers.

Regenerated collagen fibers with grooved surface texture: Physicochemical characterization and cytocompatibility.

PubMed

Wang, Xiang; Wu, Tong; Wang, Wei; Huang, Chen; Jin, Xiangyu

2016-01-01

A novel type of protein fibers, regenerated collagen fibers (RC) from cattle skin, was prepared through wet-spinning. Due to the combined effect of solvent exchange and subsequent drawing process, the fibers were found to have a grooved surface texture. The grooves provided not only ordered topographical cues, but also increased surface area. Protein content of the RC fibers was confirmed by Fourier Transform infrared spectroscopy (FTIR) and ninhydrin color reaction. The fibers could be readily fabricated into nonwovens or other textiles, owning to their comparable physical properties to other commercialized fibers. Cell growth behavior on RC nonwovens suggested both early adhesion and prompt proliferation. The high moisture regain, good processability, along with the excellent cytocompatibility indicated that the RC fibers and nonwovens developed in this study might offer a good candidate for biomedical and healthcare applications. Copyright © 2015 Elsevier B.V. All rights reserved.

Infrared light sensor applied to early detection of tooth decay

NASA Astrophysics Data System (ADS)

Benjumea, Eberto; Espitia, José; Díaz, Leonardo; Torres, Cesar

2017-08-01

The approach dentistry to dental care is gradually shifting to a model focused on early detection and oral-disease prevention; one of the most important methods of prevention of tooth decay is opportune diagnosis of decay and reconstruction. The present study aimed to introduce a procedure for early diagnosis of tooth decay and to compare result of experiment of this method with other common treatments. In this setup, a laser emitting infrared light is injected in core of one bifurcated fiber-optic and conduced to tooth surface and with the same bifurcated fiber the radiation reflected for the same tooth is collected and them conduced to surface of sensor that measures thermal and light frequencies to detect early signs of decay below a tooth surface, where demineralization is difficult to spot with x-ray technology. This device will can be used to diagnose tooth decay without any chemicals and rays such as high power lasers or X-rays.

Surface free energy analysis of oil palm empty fruit bunches fiber reinforced biocomposites

NASA Astrophysics Data System (ADS)

Suryadi, G. S.; Nikmatin, S.; Sudaryanto; Irmansyah; Sukaryo, S. G.

2017-05-01

Study of the size effect of natural fiber from oil palm empty fruit bunches (OPEFB) as filler, onto the contact angle and surface free energy of fiber reinforced biocomposites has been done. The OPEFB fibers were prepared by mechanical milling and sieving to obtain various sizes of fiber (long-fiber, medium-fiber, short-fiber, and microparticle). The biocomposites has been produced by extrusion using single-screw extruder with EFB fiber as filler, recycled Acrylonitrile Butadiene Styrene (ABS) polymer as matrix, and primary antioxidant, acid scavanger, and coupling agent as additives. The obtained biocomposites in form of granular, were made into test piece by injection molding method. Contact angles of water, methanol, and hexane on the surface of biocomposites at room temperature were measured using Phoenix 300 Contact Angle Analyzer. The surface free energy (SFE) and their components were calculated using three previous known methods (Girifalco-Good-Fowkes-Young (GGFY), Owens-Wendt, and van Oss-Chaudhury-Good (vOCG)). The results showed that total SFE of Recycled ABS as control was about 24.38 mJ/m2, and SFE of biocomposites was lower than control, decreased with decreasing of EFB fiber size as biocomposites filler. The statistical analysis proved that there are no statistically significant differences in the value of the SFE calculated with the three different methods.

Effect of interactions between Co(2+) and surface goethite layer on the performance of α-FeOOH coated hollow fiber ceramic ultrafiltration membranes.

PubMed

Zhu, Zhiwen; Zhu, Li; Li, Jianrong; Tang, Jianfeng; Li, Gang; Hsieh, Yi-Kong; Wang, TsingHai; Wang, Chu-Fang

2016-03-15

The consideration of water energy nexus inspires the environmental engineering community to pursue a more sustainable strategy in the wastewater treatment. One potential response would be to enhance the performance of the low-pressure driven filtration system. To reach this objective, it is essential to have a better understanding regarding the surface interaction between the target substance and the surface of membrane. In this study, the hollow fiber ceramic membranes were coated with a goethite layer in order to enhance the Co(2+) rejection. Experimental results indicate that higher Co(2+) rejections are always accompanied with the significant reduction in the permeability. Based on the consideration of electroviscous effect, the surface interactions including the induced changes in viscosity, pore radius and Donnan effect in the goethite layer are likely responsible for the pH dependent behaviors in the rejection and permeability. These results could be valuable references to develop the filtration system with high rejection along with acceptable degree of permeability in the future. Copyright © 2015 Elsevier Inc. All rights reserved.

Mineralogic correlates of fibrosis in chrysotile miners and millers

DOE Office of Scientific and Technical Information (OSTI.GOV)

Churg, A.; Wright, J.L.; DePaoli, L.

1989-04-01

To determine which mineral parameters relate to the degree of interstitial fibrosis (asbestosis) in the lungs of chrysotile miners and millers, we graded fibrosis histologically and correlated fibrosis grades with fiber concentration and mean size, surface area, and mass, and with total sample fiber length, surface area, and mass in 21 cases. A positive correlation of fibrosis grade with tremolite concentration and a lesser correlation with chrysotile concentration was found for whole lungs, specific sites within lungs, and, for tremolite, single microscopic fields. No correlations were found for measures of chrysotile fiber size, surface area, or mass, but tremolite meanmore » fiber length, aspect ratio, and surface area were, surprisingly, negatively correlated with fibrosis grade. Measures based on total rather than on mean case or site parameters failed to show correlations with fibrosis. We conclude that: (1) degree of pulmonary fibrosis reflects fiber concentration at both a bulk and a microscopic level; (2) mean fiber length and parameters related to mean fiber length also correlate with fibrosis grade, but, contrary to predictions from animal studies, this correlation is negative, suggesting that short fibers may be more important in the genesis of pulmonary fibrosis than is commonly believed; (3) there is no evidence that parameters such as total fiber length, surface area, or mass provide predictors of degree of fibrosis.« less

Effect of fiber reinforcements on thermo-oxidative stability and mechanical properties of polymer matrix composites

NASA Technical Reports Server (NTRS)

Bowles, Kenneth J.

1991-01-01

A number of studies have investigated the thermo-oxidative behavior of polymer matrix composites. Two significant observations have been made from these research efforts: (1) fiber reinforcement has a significant effect on composite thermal stability; and (2) geometric effects must be considered when evaluating thermal aging data. A compilation of some results from these studies is presented, and this information shows the influence of the reinforcement fibers on the oxidative degradation of various polymer matrix composites. The polyimide PMR-15 was the matrix material that was used in these studies. The control composite material was reinforced with Celion 6000 graphite fiber. T-40R graphite fibers, along with some very stable ceramic fibers were selected as reinforcing fibers because of their high thermal stability. The ceramic fibers were Nicalon (silicon carbide) and Nextel 312 (alumina-silica-boron oxide). The mechanical properties of the two graphite fiber composites were significantly different, probably owing to variations in interfacial bonding between the fibers and the polyimide matrix. The Celion 6000/PMR-15 bond is very tight but the T-40/PMR-15 bond is less tight. Three oxidation mechanisms were observed: (1) the preferential oxidation of the Celion 6000 fiber ends at cut surfaces, leaving a surface of matrix material with holes where the fiber ends were originally situated; (2) preferential oxidation of the composite matrix; and (3) interfacial degradation by oxidation. The latter two mechanisms were also observed on fiber end cut surfaces. The fiber and interface attacks appeared to initiate interfiber cracking along these surfaces.

Thermo-mechanical characterization of siliconized E-glass fiber/hematite particles reinforced epoxy resin hybrid composite

NASA Astrophysics Data System (ADS)

V. R., Arun prakash; Rajadurai, A.

2016-10-01

In this present work hybrid polymer (epoxy) matrix composite has been strengthened with surface modified E-glass fiber and iron(III) oxide particles with varying size. The particle sizes of 200 nm and <100 nm has been prepared by high energy ball milling and sol-gel methods respectively. To enhance better dispersion of particles and improve adhesion of fibers and fillers with epoxy matrix surface modification process has been done on both fiber and filler by an amino functional silane 3-Aminopropyltrimethoxysilane (APTMS). Crystalline and functional groups of siliconized iron(III) oxide particles were characterized by XRD and FTIR spectroscopy analysis. Fixed quantity of surface treated 15 vol% E-glass fiber was laid along with 0.5 and 1.0 vol% of iron(III) oxide particles into the matrix to fabricate hybrid composites. The composites were cured by an aliphatic hardener Triethylenetetramine (TETA). Effectiveness of surface modified particles and fibers addition into the resin matrix were revealed by mechanical testing like tensile testing, flexural testing, impact testing, inter laminar shear strength and hardness. Thermal behavior of composites was evaluated by TGA, DSC and thermal conductivity (Lee's disc). The scanning electron microscopy was employed to found shape and size of iron(III) oxide particles adhesion quality of fiber with epoxy matrix. Good dispersion of fillers in matrix was achieved with surface modifier APTMS. Tensile, flexural, impact and inter laminar shear strength of composites was improved by reinforcing surface modified fiber and filler. Thermal stability of epoxy resin was improved when surface modified fiber was reinforced along with hard hematite particles. Thermal conductivity of epoxy increased with increase of hematite content in epoxy matrix.

Surface Characterization of Carbon Fiber Polymer Composites and Aluminum Alloys After Laser Interference Structuring

NASA Astrophysics Data System (ADS)

Sabau, Adrian S.; Greer, Clayton M.; Chen, Jian; Warren, Charles D.; Daniel, Claus

2016-07-01

The increasing use of carbon fiber-reinforced polymer matrix composites (CFPC) and aluminum alloys as lightweight materials in the automotive and aerospace industries demands enhanced surface preparation and control of surface morphology prior to joining. In this study, surfaces of both composite and aluminum were prepared for joining using an Nd:YAG laser in a two-beam interference setup, enabling the (1) structuring of the AL 5182 surface, (2) removal of the resin layer on top of carbon fibers, and (3) structuring of the carbon fibers. CFPC specimens of T700S carbon fiber, Prepreg—T83 epoxy, 5 ply thick, 0°/90° plaques were used. The effects of laser fluence, scanning speed, and number of shots-per-spot were investigated on the removal rate of the resin without an excessive damage of the fibers. Optical micrographs, 3D imaging, and scanning electron microscope imaging were used to study the effect of the laser processing on the surface morphology. It was found that an effective resin ablation and a low density of broken fibers for CFPC specimens was attained using laser fluences of 1-2 J/cm2 and number of 2-4 pulses per spot. A relatively large area of periodic line structures due to energy interference were formed on the aluminum surface at laser fluences of 12 J/cm2 and number of 4-6 pulses per spot.

Surface functionalization of polyamide fiber via dopamine polymerization

NASA Astrophysics Data System (ADS)

Kuang, Xiao-Hui; Guan, Jin-Ping; Tang, Ren-Cheng; Chen, Guo-Qiang

2017-09-01

The oxidative polymerization of dopamine for the functional surface modification of textile fibers has drawn great attention. In this work, the functionalization of polyamide fiber via dopamine polymerization was studied with the aim of the fabrication of hydrophilic and antistatic surface. The conditions of dopamine application were first discussed in the absence of specific oxidants in terms of the apparent color depth of polyamide fiber. Dopamine concentration, pH and time were found to exert great impact on color depth. The highest color depth was achieved at pH 8.5. In the process of modification, polydopamine was deposited onto the surface of polyamide fiber. The modified polyamide fiber displayed a yellowish brown color with excellent wash and light color fastness, and exhibited good hydrophilic, UV protection and antistatic effects. A disadvantage of the present approach was the slow rate of dopamine polymerization and functionalization.

Creep-induced residual stress strengthening in a Nicalon-fiber-reinforced BMAS-glass-ceramic-matrix composite

DOE Office of Scientific and Technical Information (OSTI.GOV)

Widjaja, S.; Jakus, K.; Ritter, J.E.

The feasibility of inducing a compressive residual stress in the matrix of a Nicalon-fiber-reinforced BMAS-glass-ceramic-matrix composite through a creep-load transfer treatment was studied. Specimens were crept at 1100 C under constant tensile load to cause load transfer from the matrix to the fibers, then cooled under load. Upon removal of the load at room temperature, the matrix was put into compression by the elastic recovery of the fibers. This compressive residual stress in the matrix increased the room-temperature proportional limit stress of the composite. The increase in the proportional limit stress was found to be dependent upon the applied creepmore » stress, with an increase in creep stress resulting in an increase in the proportional limit stress. Acoustic emission results showed that the onset of significant matrix cracking correlated closely to the proportional limit stress. Changes in the state of residual stress in the matrix were supported by X-ray diffraction results. Fracture surfaces of all specimens exhibited fiber pullout behavior, indicating that the creep-load transfer process did not embrittle the fiber/matrix interface.« less

Surface modification of lignocellulosic fibers using high-frequency ultrasound

Treesearch

Jayant B. Gadhe; Ram B. Gupta; Thomas Elder

2005-01-01

Enzymatic and chemical oxidation of fiber surfaces has been reported in the literature as a method for producing medium density fiberboards without using synthetic adhesives. This work focuses on modifying the surface properties of wood fibers by the generation of free radicals using high-frequency ultrasound. A sonochemical reactor operating at 610 kHz is used to...

Characterizing the surface roughness of thermomechanical pulp fibers with atomic force microscopy

Treesearch

Rebecca Snell; Leslie H. Groom; Timothy G. Rials

2001-01-01

Loblolly pine, separated into mature and juvenile portions, was refined at various pressures (4, 8 and 12 bar). Fiber surfaces were investigated using a Scanning Electron Microscope (SEM) and an Atomic Force Microscope (AFM). Refiner pressure had a significant effect on the fiber surefaces. SEM images showed an apparent increase in surface roughness with increased...

Controlling Structure and Properties of High Surface Area Nonwoven Materials via Hydroentangling

NASA Astrophysics Data System (ADS)

Luzius, Dennis

Hydroentangling describes a technique using a series of high-velocity water jets to mechanically interlock and entangle fibers. Over the last decades researchers worked on a fundamental understanding of the process and the factors influencing the properties of the final nonwoven material. Recent studies discovered hydroentangling to be capable to create unique, knot-like structures characterized by high- and low density regions, which are believed to have interesting properties for filtration applications. However, just little is known about the impact of hydroentangling parameters on the properties of filtration media to this day. In this study we report on the effect of various hydroentangling parameters, such as jet spacing, manifold pressure, number of manifolds but also specific energy on the structure and properties of high surface area nonwoven materials. Latter was achieved by different bicomponent fiber technologies and subsequent treatments removing the sacrificial compound from the structure. The highest BET surface area was measured to be 3.5 m2 g-1 and the smallest mean fiber size about 0.5 mum. Hydroentangling with large jet spacing was found to be a parameter significantly enhancing the filtration properties of caustic-treated island-in-the-sea nonwoven materials. Moreover, improved capture efficiencies and reduced pressure drops were achieved by reducing the manifold pressure and therefore specific energy during hydroentangling. Jet spacing but not island count was found to be the dominant factor influencing the structure and properties of island-in-the-sea nonwovens. Contrary to our initial expectations increasing the island count and thus decreasing the fiber size did not result in better filtration properties. Mixed media nonwoven structures made from homocomponent and island-in-the-sea fibers were found to have lower densities, higher air permeabilities and better quality factors compared to island-in-the-sea structures hydroentangled under the exact same conditions. Study showed the specific energy to not be an adequate measure for describing the process-structure relationship in hydroentangling. Hydroentangling with same specific energy but different manifold pressures revealed the structure and properties to be different and the peak manifold pressure to be the dominant parameter. It was further shown that hydroentangling with multiple manifolds but same water pressure influences the structure and properties of mono- and bicomponent nonwoven materials. Hydroentangling with three manifolds having the same water pressure resulted in stronger, less permeable fabrics compared to two manifolds or one manifold with the same water pressure. Necessary hydroentangling intensity for winged and island-in-the-sea nonwoven materials was found to be different. Winged fiber nonwovens required higher manifold pressures and a different energy ratio than island-in-in-the-sea nonwovens. Hydroentangling winged fiber webs with jet spacing larger than 600 mum resulted in materials too weak to withstand the caustic-treatment. Study indicated the charging potential of winged fiber nonwovens to be superior compared to island-in-the-sea-structures. In contrast to winged fiber nonwovens, island-in-the-sea structures showed higher pressure drops after corona discharge. Loading winged fiber nonwovens with potassium chloride revealed caustic-treated, IPA discharged materials to show the highest loading capacity.

[Biliary calculi resistant to dissolution with bile acids: their heterogeneous composition and diversity of treatment response].

PubMed

Ruíz de Aguiar, A; Medina, J A; Garrido, G; Villacorta, J; Berenguer, J

1992-05-01

We have studied thirteen biliary stones resistant to biliary acids, using technical methods of stereomicroscopy, scanning electronic microscopy and EDX analyses. We have investigated changes on surface. Three biliary stones did not change and were considered resistant. Seven biliary stones appear partially dissolved and we observed many irregularities on surface and/or concentric dips in relation with cholesterol dissolution. In six cases, biliary pigment alternates with cholesterol. In three cases we observed a calcium carbonate coat on surface. One case included organic fibers. One biliary stone showed cholesterol with spherical bodies of calcium carbonate and pigment. It was a relapsed case of combined treatment. Three stones are composed of small black portions of polymerized calcium bilirubinate, rich in copper and iron. Our results demonstrate that biliary stones previously selected for treatment are a heterogeneous group. Because of this fact we get variable and unpredictable results.

Studies in fiber guided excimer laser surgery for cutting and drilling bone and meniscus.

PubMed

Dressel, M; Jahn, R; Neu, W; Jungbluth, K H

1991-01-01

Our experiments on transmitting high-power excimer laser pulses through optical fibers and our investigations on excimer laser ablation of hard tissue show the feasibility of using the excimer laser as an additional instrument in general and accident surgery involving minimal invasive surgery. By combining XeCl-excimer lasers and tapered fused silica fibers we obtained output fluences up to 32 J/cm2 and ablation rates of 3 microns/pulse of hard tissue. This enables us to cut bone and cartilage in a period of time which is suitable for clinical operations. Various experiments were carried out on cadavers in order to optimize the parameters of the excimer laser and fibers: e.g., wavelength, pulse duration, energy, repetition rate, fiber core diameter. The surfaces of the cut tissue are comparable to cuts with conventional instruments. No carbonisation was observed. The temperature increase is below 40 degrees C in the tissue surrounding the laser spot. The healing rate of an excimer laser cut is not slower than mechanical treatments; the quality is comparable.

Is in vivo analysis of urinary stone composition feasible? Evaluation of an experimental setup of a Raman system coupled to commercial lithotripsy laser fibers.

PubMed

Miernik, Arkadiusz; Eilers, Yvan; Nuese, Christoph; Bolwien, Carsten; Lambrecht, Armin; Hesse, Albrecht; Rassweiler, Jens J; Schlager, Daniel; Wilhelm, Konrad; Wetterauer, Ulrich; Schoenthaler, Martin

2015-10-01

Raman spectroscopy allows immediate analysis of stone composition. In vivo stone analysis during endoscopic treatment may offer advantages concerning surgical strategy and metaphylaxis. Urinary stone components were evaluated utilizing an experimental setup of a Raman system coupled to commercial laser fibers. Samples of paracetamol (acetaminophen) and human urinary stones with known Raman spectra were analyzed using an experimental Raman system coupled to common commercial lithotripsy laser fibers (200 and 940 µm). Two different excitation lasers were used at wavelengths of 532 and 785 nm. Numerical aperture of the fibers, proportion of reflected light reaching the CCD chip, and integration times were calculated. Mathematical signal correction was performed. Both the laser beam profile and the quality of light reflected by the specimens were impaired significantly when used with commercial fibers. Acquired spectra could no longer be assigned to a specific stone composition. Subsequent measurements revealed a strong intrinsic fluorescence of the fibers and poor light acquisition properties leading to a significant decrease in the Raman signal in comparison with a free-beam setup. This was true for both investigated fiber diameters and both wavelengths. Microscopic examination showed highly irregular fiber tip surfaces (both new and used fibers). Our results propose that laser excitation and light acquisition properties of commercial lithotripsy fibers impair detectable Raman signals significantly in a fiber-coupled setting. This study provides essential physical and technological information for the development of an advanced fiber-coupled system able to be used for immediate stone analysis during endoscopic stone therapy.

Dynamic mechanical analysis, surface chemistry and morphology of alkali and enzymatic retted kenaf fibers

USDA-ARS?s Scientific Manuscript database

Bast fibers grow in the bark layer of many plants, and have been used for textiles and cordage for over 6000 years. Bast fibers of kenaf (Hibiscus cannabinus L.) are retted by three methods and a comparative assessment of available reactive groups on the fiber surface and mechanical properties are ...

The effect of fiber bleaching treatment on the properties of poly(lactic acid)/oil palm empty fruit bunch fiber composites.

PubMed

Rayung, Marwah; Ibrahim, Nor Azowa; Zainuddin, Norhazlin; Saad, Wan Zuhainis; Razak, Nur Inani Abdul; Chieng, Buong Woei

2014-08-22

In this work, biodegradable composites from poly(lactic acid) (PLA) and oil palm empty fruit bunch (OPEFB) fiber were prepared by melt blending method. Prior to mixing, the fiber was modified through bleaching treatment using hydrogen peroxide. Bleached fiber composite showed an improvement in mechanical properties as compared to untreated fiber composite due to the enhanced fiber/matrix interfacial adhesion. Interestingly, fiber bleaching treatment also improved the physical appearance of the composite. The study was extended by blending the composites with commercially available masterbatch colorant.

The Effect of Fiber Bleaching Treatment on the Properties of Poly(lactic acid)/Oil Palm Empty Fruit Bunch Fiber Composites

PubMed Central

Rayung, Marwah; Ibrahim, Nor Azowa; Zainuddin, Norhazlin; Saad, Wan Zuhainis; Razak, Nur Inani Abdul; Chieng, Buong Woei

2014-01-01

In this work, biodegradable composites from poly(lactic acid) (PLA) and oil palm empty fruit bunch (OPEFB) fiber were prepared by melt blending method. Prior to mixing, the fiber was modified through bleaching treatment using hydrogen peroxide. Bleached fiber composite showed an improvement in mechanical properties as compared to untreated fiber composite due to the enhanced fiber/matrix interfacial adhesion. Interestingly, fiber bleaching treatment also improved the physical appearance of the composite. The study was extended by blending the composites with commercially available masterbatch colorant. PMID:25153628

Contamination and Surface Preparation Effects on Composite Bonding

NASA Technical Reports Server (NTRS)

Kutscha, Eileen O.; Vahey, Paul G.; Belcher, Marcus A.; VanVoast, Peter J.; Grace, William B.; Blohowiak, Kay Y.; Palmieri, Frank L.; Connell, John W.

2017-01-01

Results presented here demonstrate the effect of several prebond surface contaminants (hydrocarbon, machining fluid, latex, silicone, peel ply residue, release film) on bond quality, as measured by fracture toughness and failure modes of carbon fiber reinforced epoxy substrates bonded in secondary and co-bond configurations with paste and film adhesives. Additionally, the capability of various prebond surface property measurement tools to detect contaminants and potentially predict subsequent bond performance of three different adhesives is also shown. Surface measurement methods included water contact angle, Dyne solution wettability, optically stimulated electron emission spectroscopy, surface free energy, inverse gas chromatography, and Fourier transform infrared spectroscopy with chemometrics analysis. Information will also be provided on the effectiveness of mechanical and energetic surface treatments to recover a bondable surface after contamination. The benefits and drawbacks of the various surface analysis tools to detect contaminants and evaluate prebond surfaces after surface treatment were assessed as well as their ability to correlate to bond performance. Surface analysis tools were also evaluated for their potential use as in-line quality control of adhesive bonding parameters in the manufacturing environment.

DOE Office of Scientific and Technical Information (OSTI.GOV)

Sabau, Adrian S.; Greer, Clayton M.; Chen, Jian

Here, the increasing use of Carbon Fiber-reinforced Polymer matrix Composites (CFPC) and aluminum alloys as lightweight materials in the automotive and aerospace industries demands enhanced surface preparation and control of surface morphology prior to joining. In this study, surfaces of both composite and aluminum were prepared for joining using an Nd:YAG laser in a two-beam interference setup, enabling the (a) structuring of the AL 5182 surface, (b) removal of the resin layer on top of carbon fibers, and (c) structuring of the carbon fibers. CFPC specimens of T700S carbon fiber, Prepreg - T8 3 epoxy, 5 ply thick, 0/90o plaquesmore » were used. The effect of laser fluence, scanning speed, and number of shots-per-spot was investigated on the removal rate of the resin without an excessive damage of the fibers. Optical micrographs, 3D imaging, and scanning electron microscope (SEM) imaging were used to study the effect of the laser processing on surface morphology.« less

A novel method for preparing microfibrillated cellulose from bamboo fibers

NASA Astrophysics Data System (ADS)

Dat Nguyen, Huu; Thanh Thuy Mai, Thi; Bich Nguyen, Ngoc; Duy Dang, Thanh; Loan Phung Le, My; Dang, Tan Tai; Tran, Van Man

2013-03-01

The bamboo fiber is a potential candidate for biomass and power source application. In this study, microfibrillated cellulose (MFC) is prepared from raw fibers of bamboo tree (Bambusa Blumeana J A & J H Schultes) by an alkali treatment at room temperature in association with a bleaching treatment followed by a sulfuric acid hydrolysis. Field-emission scanning electron microscopy (FESEM) images indicated that final products ranged from 20 to 40 nm in diameter. The chemical composition measurement and Fourier transform infrared (FTIR) spectroscopy showed that both hemicellulose and lignin are mostly removed in the MFC. The x-ray diffraction (XRD) results also show that MFC has crystallinity of more than 70%. The thermogravimetric analysis (TGA) curves revealed that cellulose microfibers have a two-step thermal decomposition behavior owing to the attachment of sulfated groups onto the cellulose surface in the hydrolysis process with sulfuric acid. The obtained MFCs may have potential applications in alternative power sources as biomass, in pharmaceutical and optical industries as additives, as well as in composite fields as a reinforcement phase.

Tunable optofluidic microring laser based on a tapered hollow core microstructured optical fiber.

PubMed

Li, Zhi-Li; Zhou, Wen-Yuan; Luo, Ming-Ming; Liu, Yan-Ge; Tian, Jian-Guo

2015-04-20

A tunable optofluidic microring dye laser within a tapered hollow core microstructured optical fiber was demonstrated. The fiber core was filled with a microfluidic gain medium plug and axially pumped by a nanosecond pulse laser at 532 nm. Strong radial emission and low-threshold lasing (16 nJ/pulse) were achieved. Lasing was achieved around the surface of the microfluidic plug. Laser emission was tuned by changing the liquid surface location along the tapered fiber. The possibility of developing a tunable laser within the tapered simplified hollow core microstructured optical fiber presents opportunities for developing liquid surface position sensors and biomedical analysis.

Method and apparatus for monitoring and measuring the surface tension of a fluid using fiber optics

DOEpatents

Abraham, Bernard M.; Ketterson, John B.; Bohanon, Thomas M.; Mikrut, John M.

1994-01-01

A non-contact method and apparatus for measuring and monitoring the surface of a fluid using fiber optics and interferometric detection to permit measurement mechanical characteristics' fluid surfaces. The apparatus employs an alternating electric field gradient for generating a capillary wave on the surface of the fluid. A fiber optic coupler and optical fiber directs a portion of a laser beam onto the surface of the fluid, another portion of the laser beam onto the photo sensor, and directs light reflected from the surface of the fluid onto the photo sensor. The output of the photo sensor is processed and coupled to a phase sensitive detector to permit measurement of phase shift between the drive signal creating the capillary wave and the detected signal. This phase shift information is then used to determine mechanical properties of the fluid surface such as surface tension, surface elasticity, and surface inhomogeneity. The resulting test structure is easily made compact, portable, and easy to align and use.

Robust, easily shaped, and epoxy-free carbon-fiber-aluminum cathodes for generating high-current electron beams.

PubMed

Liu, Lie; Li, Limin; Wen, Jianchun; Wan, Hong

2009-02-01

This paper presents the construction of carbon-fiber-aluminum (CFA) cathode by squeezing casting and its applications for generating high-current electron beams to drive high-power microwave sources. The fabrication process avoided using epoxy, a volatile deteriorating the vacuum system. These cathodes had a higher hardness than conventional aluminum, facilitating machining. After surface treatment, carbon fibers became the dominator determining emission property. A multineedle CFA cathode was utilized in a triode virtual cathode oscillator (vircator), powered by a approximately 450 kV, approximately 400 ns pulse. It was found that 300-400 MW, approximately 250 ns microwave was radiated at a dominant frequency of 2.6 GHz. Further, this cathode can endure high-current-density emission without detectable degradation in performance as the pulse shot proceeded, showing the robust nature of carbon fibers as explosive emitters. Overall, this new class of cold cathodes offers a potential prospect of developing high-current electron beam sources.

Spectral fiber sensors for cancer diagnostics in vitro

NASA Astrophysics Data System (ADS)

Artyushenko, V.; Schulte, F.; Zabarylo, U.; Berlien, H.-P.; Usenov, I.; Saeb Gilani, T.; Eichler, H.; Pieszczek, Ł.; Bogomolov, A.; Krause, H.; Minet, O.

2015-07-01

Cancer is one of the leading causes for morbidity and mortality worldwide. Therefore, efforts are concentrated on cancer detection in an early stage to enhance survival rates for cancer patients. A certain intraoperative navigation in the tumor border zone is also an essential task to lower the mortality rate after surgical treatment. Molecular spectroscopy methods proved to be powerful tools to differentiate cancerous and healthy tissue. Within our project comparison of different vibration spectroscopy methods were tested to select the better one or to reach synergy from their combination. One key aspect was in special fiber probe development for each technique. Using fiber optic probes in Raman, MIR and NIR spectroscopy is a very powerful method for non-invasive in vivo applications. Miniaturization of Raman probes was achieved by deposition of dielectric filters directly onto the silica fiber end surfaces. Raman, NIR and MIR spectroscopy were used to analyze samples from kidney tumors. The differentiation between cancer and healthy samples was successfully obtained by multivariate data analysis.

Nanofiber Orientation and Surface Functionalization Modulate Human Mesenchymal Stem Cell Behavior In Vitro

PubMed Central

Kolambkar, Yash M.; Bajin, Mehmet; Wojtowicz, Abigail; Hutmacher, Dietmar W.; García, Andrés J.

2014-01-01

Electrospun nanofiber meshes have emerged as a new generation of scaffold membranes possessing a number of features suitable for tissue regeneration. One of these features is the flexibility to modify their structure and composition to orchestrate specific cellular responses. In this study, we investigated the effects of nanofiber orientation and surface functionalization on human mesenchymal stem cell (hMSC) migration and osteogenic differentiation. We used an in vitro model to examine hMSC migration into a cell-free zone on nanofiber meshes and mitomycin C treatment to assess the contribution of proliferation to the observed migration. Poly (ɛ-caprolactone) meshes with oriented topography were created by electrospinning aligned nanofibers on a rotating mandrel, while randomly oriented controls were collected on a stationary collector. Both aligned and random meshes were coated with a triple-helical, type I collagen-mimetic peptide, containing the glycine-phenylalanine-hydroxyproline-glycine-glutamate-arginine (GFOGER) motif. Our results indicate that nanofiber GFOGER peptide functionalization and orientation modulate cellular behavior, individually, and in combination. GFOGER significantly enhanced the migration, proliferation, and osteogenic differentiation of hMSCs on nanofiber meshes. Aligned nanofiber meshes displayed increased cell migration along the direction of fiber orientation compared to random meshes; however, fiber alignment did not influence osteogenic differentiation. Compared to each other, GFOGER coating resulted in a higher proliferation-driven cell migration, whereas fiber orientation appeared to generate a larger direct migratory effect. This study demonstrates that peptide surface modification and topographical cues associated with fiber alignment can be used to direct cellular behavior on nanofiber mesh scaffolds, which may be exploited for tissue regeneration. PMID:24020454

Fiber Tracts of the Medial and Inferior Surfaces of the Cerebrum.

PubMed

Baydin, Serhat; Gungor, Abuzer; Tanriover, Necmettin; Baran, Oguz; Middlebrooks, Erik H; Rhoton, Albert L

2017-02-01

Fiber dissection studies of the cerebrum have focused on the lateral surface. No comparable detailed studies have been done on the medial and inferior surfaces. The object of this study was to examine the fiber tracts, cortical, and subcortical structures of the medial and inferior aspects of the brain important in planning operative approaches along the interhemispheric fissure, parafalcine area, and basal surfaces of the cerebrum. Twenty formalin-fixed human hemispheres (10 brains) were examined by fiber dissection technique under ×6-×40 magnifications. The superior longitudinal fasciculus I, cingulum, inferior longitudinal fasciculus, uncinate fasciculus, optic radiations, tapetum, and callosal fibers were dissected step by step from medial to lateral, exposing the nucleus accumbens, subthalamic nucleus, red nucleus, and central midline structures (fornix, stria medullaris, and stria terminalis). Finally, the central core structures were dissected from medial to lateral. Understanding the fiber network underlying the medial and inferior aspects of the brain is important in surgical planning for approaches along the interhemispheric fissure, parafalcine area, and basal surfaces of the cerebrum. Copyright © 2016. Published by Elsevier Inc.

Improved adhesion performances of aramid fibers with vinyl epoxy via supercritical carbon dioxide modification

NASA Astrophysics Data System (ADS)

Qin, M. L.; Kong, H. J.; Yu, M. H.; Teng, C. Q.

2017-06-01

In this paper, aramid fibers were treated under supercritical carbon dioxide (SCCO2) with isocyanate terminated liquid nitrile rubber to improve the adhesion performances of vinyl epoxy composites. The interfacial shear strength (IFSS) of vinyl epoxy composites was investigated by micro-bond test. The results indicate that the surface modification of aramid fibers in SCCO2 was an efficient method to increase the adhesion performances between fibers and vinyl epoxy. Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) were adopted to investigate the surface structure and composition of aramid fibers. The flexural strength and interlaminar shear strength (ILSS) of treated aramid fibers/vinyl epoxy composites was improved by 18.1% and 28.9% compared with untreated aramid fibers, respectively. Furthermore, the fractured surfaces of the composites were observed by SEM, which showed that the interfacial adhesion of composites has been remarkably changed.

Characterization and Effects of Fiber Pull-Outs in Hole Quality of Carbon Fiber Reinforced Plastics Composite.

PubMed

Alizadeh Ashrafi, Sina; Miller, Peter W; Wandro, Kevin M; Kim, Dave

2016-10-13

Hole quality plays a crucial role in the production of close-tolerance holes utilized in aircraft assembly. Through drilling experiments of carbon fiber-reinforced plastic composites (CFRP), this study investigates the impact of varying drilling feed and speed conditions on fiber pull-out geometries and resulting hole quality parameters. For this study, hole quality parameters include hole size variance, hole roundness, and surface roughness. Fiber pull-out geometries are quantified by using scanning electron microscope (SEM) images of the mechanically-sectioned CFRP-machined holes, to measure pull-out length and depth. Fiber pull-out geometries and the hole quality parameter results are dependent on the drilling feed and spindle speed condition, which determines the forces and undeformed chip thickness during the process. Fiber pull-out geometries influence surface roughness parameters from a surface profilometer, while their effect on other hole quality parameters obtained from a coordinate measuring machine is minimal.

Recycling and characterization of carbon fibers from carbon fiber reinforced epoxy matrix composites by a novel super-heated-steam method.

PubMed

Kim, Kwan-Woo; Lee, Hye-Min; An, Jeong-Hun; Chung, Dong-Chul; An, Kay-Hyeok; Kim, Byung-Joo

2017-12-01

In order to manufacture high quality recycled carbon fibers (R-CFs), carbon fiber-reinforced composite wastes were pyrolysed with super-heated steam at 550 °C in a fixed bed reactor for varying reaction times. The mechanical and surface properties of the R-CFs were characterized with a single fiber tensile test, interface shear strength (IFSS), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). The surface analysis showed that there was no matrix char residue on the fiber surfaces. The tensile strength and IFSS values of the R-CFs were 90% and 115% compared to those of virgin carbon fibers (V-CFs), respectively. The recycling efficiency of the R-CFs from the composites were strongly dependent on the pyrolysis temperature, reaction time, and super-heated steam feeding rate. Copyright © 2017 Elsevier Ltd. All rights reserved.

Adhesion of cellulose fibers in paper.

PubMed

Persson, Bo N J; Ganser, Christian; Schmied, Franz; Teichert, Christian; Schennach, Robert; Gilli, Eduard; Hirn, Ulrich

2013-01-30

The surface topography of paper fibers is studied using atomic force microscopy (AFM), and thus the surface roughness power spectrum is obtained. Using AFM we have performed indentation experiments and measured the effective elastic modulus and the penetration hardness as a function of humidity. The influence of water capillary adhesion on the fiber-fiber binding strength is studied. Cellulose fibers can absorb a significant amount of water, resulting in swelling and a strong reduction in the elastic modulus and the penetration hardness. This will lead to closer contact between the fibers during the drying process (the capillary bridges pull the fibers into closer contact without storing up a lot of elastic energy at the contacting interface). In order for the contact to remain good in the dry state, plastic flow must occur (in the wet state) so that the dry surface profiles conform to each other (forming a key-and-lock type of contact).

Investigation of Structural Properties of Carbon-Epoxy Composites Using Fiber-Bragg Gratings

NASA Technical Reports Server (NTRS)

Grant, J.; Kaul, R.; Taylor, S.; Jackson, K.; Sharma, A.; Burdine, Robert V. (Technical Monitor)

2002-01-01

Fiber Bragg-gratings are embedded in carbon-epoxy laminates as well as bonded on the surface of cylindrical structures fabricated out of such composites. Structural properties of such composites is investigated. The measurements include stress-strain relation in laminates and Poisson's ratio in several specimens with varying orientation of the optical fiber Bragg-sensor with respect to the carbon fiber in an epoxy matrix. Additionally, Bragg gratings are bonded on the surface of cylinders fabricated out of carbon-epoxy composites and longitudinal and hoop strain on the surface is measured.

Surface grafting of styrene on polypropylene fibers by argon plasma and its adsorption-regeneration of BTX

NASA Astrophysics Data System (ADS)

Xu, J. J.; Guo, M. L.; Chen, Q. G.; Lian, Z. Y.; Wei, W. J.; Luo, Z. W.; Xie, G.; Chen, H. N.; Dong, K.

2017-08-01

Active macromolecular free radicals were generated on polypropylene (PP) fibers surfaces by argon (Ar) plasma irradiation, then, PP surface modified fibers (PP-g-St fibers) were prepared by in-situ grafting reaction of styrene monomers (St). Effects of reaction parameters on grafting percentage were studied and adsorption capacities of PP-g-St fibers for benzene, toluene and xylene (BTX) were evaluated. Afterwards, regeneration adsorption efficiencies after maximum adsorption were explored. The results indicated that the optimum input power, irradiation time and grafting reaction time are 90 W, 3 min and 3 h respectively and the grafting percentage of St reached 5.7 %. The adsorption capacities of PP-g-St fibers towards toluene and xylene emulsions and solutions in water increased by 336.89 % and 344.57 % respectively, compared to pristine PP fibers. In addition, regeneration adsorption efficiencies of modified fibers remained > 90 % after six cycles of regeneration-adsorption experiments, which showed excellent regeneration ability.

Laser beam uniformity and stability using homogenizer-based fiber optic launch method: square core fiber delivery

NASA Astrophysics Data System (ADS)

Lizotte, Todd E.

2011-03-01

Over the years, technological achievements within the laser medical diagnostic, treatment, and therapy markets have led to ever increasing requirements for greater control of critical laser beam parameters. Increased laser power/energy stabilization, temporal and spatial beam shaping and flexible laser beam delivery systems with ergonomic focusing or imaging lens systems are sought by leading medical laser system producers. With medical procedures that utilize laser energy, there is a constant emphasis on reducing adverse effects that come about by the laser itself or its optical system, but even when these variables are well controlled the medical professional will still need to deal with the multivariate nature of the human body. Focusing on the variables that can be controlled, such as accurate placement of the laser beam where it will expose a surface being treated as well as laser beam shape and uniformity is critical to minimizing adverse conditions. This paper covers the use of fiber optic beam delivery as a means of defining the beam shape (intensity/power distribution uniformity) at the target plane as well as the use of fiber delivery as a means to allow more flexible articulation of the laser beam over the surface being treated. The paper will present a new concept of using a square core fiber beam delivery design utilizing a unique micro lens array (MLA) launch method that improves the overall stability of the system, by minimizing the impact of the laser instability. The resulting performance of the prototype is presented to demonstrate its stability in comparison to simple lens launch techniques, with an emphasis on homogenization and articulated fiber delivery.

Differential-Integral method in polymer processing: Taking melt electrospinning technique for example

NASA Astrophysics Data System (ADS)

Haoyi, Li; Weimin, Yang; Hongbo, Chen; Jing, Tan; Pengcheng, Xie

2016-03-01

A concept of Differential-Integral (DI) method applied in polymer processing and molding was proposed, which included melt DI injection molding, DI nano-composites extrusion molding and melt differential electrospinning principle and equipment. Taking the melt differential electrospinning for example to introduce the innovation research progress, two methods preparing polymer ultrafine fiber have been developed: solution electro-spinning and melt electro-spinning, between which solution electro-spinning is much simpler to realize in lab. More than 100 institutions have endeavored to conduct research on it and more than 30 thousand papers have been published. However, its industrialization was restricted to some extend because of the existence of toxic solvent during spinning process and poor mechanical strength of resultant fibers caused by small pores on fiber surface. Solvent-free melt electrospinning is environmentally friendly and highly productive. However, problems such as the high melt viscosity, thick fiber diameter and complex equipment makes it relatively under researched compared with solution electrospinning. With the purpose of solving the shortage of traditional electro-spinning equipment with needles or capillaries, a melt differential electro-spinning method without needles or capillaries was firstly proposed. Nearly 50 related patents have been applied since 2005, and systematic method innovations and experimental studies have also been conducted. The prepared fiber by this method had exhibited small diameter and smooth surface. The average fiber diameter can reach 200-800 nm, and the single nozzle can yield two orders of magnitude more than the capillaries. Based on the above principle, complete commercial techniques and equipment have been developed to produce ultra-fine non-woven fabrics for the applications in air filtration, oil spill recovery and water treatment, etc.

Transurethral light delivery for prostate photoacoustic imaging

NASA Astrophysics Data System (ADS)

Lediju Bell, Muyinatu A.; Guo, Xiaoyu; Song, Danny Y.; Boctor, Emad M.

2015-03-01

Photoacoustic imaging has broad clinical potential to enhance prostate cancer detection and treatment, yet it is challenged by the lack of minimally invasive, deeply penetrating light delivery methods that provide sufficient visualization of targets (e.g., tumors, contrast agents, brachytherapy seeds). We constructed a side-firing fiber prototype for transurethral photoacoustic imaging of prostates with a dual-array (linear and curvilinear) transrectal ultrasound probe. A method to calculate the surface area and, thereby, estimate the laser fluence at this fiber tip was derived, validated, applied to various design parameters, and used as an input to three-dimensional Monte Carlo simulations. Brachytherapy seeds implanted in phantom, ex vivo, and in vivo canine prostates at radial distances of 5 to 30 mm from the urethra were imaged with the fiber prototype transmitting 1064 nm wavelength light with 2 to 8 mJ pulse energy. Prebeamformed images were displayed in real time at a rate of 3 to 5 frames per second to guide fiber placement and beamformed offline. A conventional delay-and-sum beamformer provided decreasing seed contrast (23 to 9 dB) with increasing urethra-to-target distance, while the short-lag spatial coherence beamformer provided improved and relatively constant seed contrast (28 to 32 dB) regardless of distance, thus improving multitarget visualization in single and combined curvilinear images acquired with the fiber rotating and the probe fixed. The proposed light delivery and beamforming methods promise to improve key prostate cancer detection and treatment strategies.

Optic probe for multiple angle image capture and optional stereo imaging

DOEpatents

Malone, Robert M.; Kaufman, Morris I.

2016-11-29

A probe including a multiple lens array is disclosed to measure velocity distribution of a moving surface along many lines of sight. Laser light, directed to the moving surface is reflected back from the surface and is Doppler shifted, collected into the array, and then directed to detection equipment through optic fibers. The received light is mixed with reference laser light and using photonic Doppler velocimetry, a continuous time record of the surface movement is obtained. An array of single-mode optical fibers provides an optic signal to the multiple lens array. Numerous fibers in a fiber array project numerous rays to establish many measurement points at numerous different locations. One or more lens groups may be replaced with imaging lenses so a stereo image of the moving surface can be recorded. Imaging a portion of the surface during initial travel can determine whether the surface is breaking up.

Photonic Doppler velocimetry lens array probe incorporating stereo imaging

DOEpatents

Malone, Robert M.; Kaufman, Morris I.

2015-09-01

A probe including a multiple lens array is disclosed to measure velocity distribution of a moving surface along many lines of sight. Laser light, directed to the moving surface is reflected back from the surface and is Doppler shifted, collected into the array, and then directed to detection equipment through optic fibers. The received light is mixed with reference laser light and using photonic Doppler velocimetry, a continuous time record of the surface movement is obtained. An array of single-mode optical fibers provides an optic signal to the multiple lens array. Numerous fibers in a fiber array project numerous rays to establish many measurement points at numerous different locations. One or more lens groups may be replaced with imaging lenses so a stereo image of the moving surface can be recorded. Imaging a portion of the surface during initial travel can determine whether the surface is breaking up.

Solution and interfacial behavior of modified silicone polymers and their interactions with solid substrates

NASA Astrophysics Data System (ADS)

Purohit, Parag

Surface treatment is very important step in many applications such as fabric finishing, coatings, cosmetics and personal care. Silicone polymers are a class of organic/inorganic materials that show unique properties such as weak intermolecular forces and high flexibility enabling even a very high molecular weight chain to achieve optimal orientation on surfaces. Material properties such as softness, repellency, bounciness and friction can therefore be tailored by using appropriately modified silicone polymers. Despite wide applications, the underlying mechanisms of material modification are unknown and tailoring silicones for applications remains mostly empirical. Thus the objective of this research is to understand the solution and interfacial behavior of functionalized silicone polymers, which govern their performance in material modification. Modified silicones are simultaneously hydrophobic and oleophobic in nature and due to this nearly universal non-compatibility, the studies of these polymers present unusual challenges. Due to this incompatible nature, the functionalized silicone polymers were emulsified into O/W emulsions to study their solution and interfacial properties. The colloidal properties such as electrokinetic and droplet distribution of these emulsions are assumed to play an important role in the observed surface and physical properties of solid substrates (in present study, cellulosic substrates) as well the stability of emulsions itself. To understand the effects of modified silicones on cellulosic substrates a variety of techniques such as frictional analysis, scanning electron microscopy and atomic force microscopy that can probe from macro to nano level were used. It is hypothesized that the size distribution and charge of silicone emulsions as well as the physiochemical conditions such as pH, control silicone conformation which in turn affect the modification of the substrate properties. With bimodal droplet distribution of silicone emulsions, the nano-sized droplets can penetrate deeper into the substrate to provide bounciness, whereas macro-sized droplets can coat the top layer leading to friction reduction. It was observed that at pH 5.5 the silicone treatment resulted in charge reversal of fibers as opposed to treatment at pH 9.5. On a macroscopic scale 20% reduction in frictional coefficient of the fabric was observed after treatment with quaternized (cationically modified) silicones as compared to untreated fibers. It was also observed using AFM that the fibrils treated with quaternized silicones are uniform, well stacked and smoother than the untreated fibers. Spectroscopic analysis of treated fibers using Raman spectroscopy indicated a decrease in fiber stress as a function of modification of silicone polymer and the interaction pH. It is concluded that the protonated amine functional silicone (below pH 7) as well as the quaternized silicone interacts with the negatively charged cellulose fibers primarily through electrostatic interactions. It is proposed that this initial surface coating is a uniform thin film which allows further deposition of polymer from the emulsion. It was observed that at high pH the zetapotential of silicone emulsions decreases drastically and the nano emulsions turn turbid. It is proposed that the observed electrophoretic and nephelometric behavior at high pH is due to flocculation of nanosized droplets to micron size, which eventually leads to droplets coalescing and emulsion destabilization. It is also postulated that the nano emulsion possess a critical dilution concentration (CDC), above which dilution leads to rapid coalescence. This critical dilution phase was further confirmed through polarity parameter and excimer formation studies which show significantly different polymer and surfactant microstructures near the CDC. Hence it is concluded that the observed surface properties of the substrate obtained above the CDC are significantly different than those below the CDC. The results reveal the vital role of physiochemical parameters such as pH, droplet size, and concentration on the emulsion stability as well as the observed physical/chemical properties of the substrates.

Pulsed Nd-YAG laser in endodontics

NASA Astrophysics Data System (ADS)

Ragot-Roy, Brigitte; Severin, Claude; Maquin, Michel

1994-12-01

The purpose of this study was to establish an operative method in endodontics. The effect of a pulsed Nd:YAG laser on root canal dentin has been examined with a scanning electron microscope. Our first experimentation was to observe the impacts carried out perpendicularly to root canal surface with a 200 micrometers fiber optic in the presence of dye. Secondarily, the optical fiber was used as an endodontic instrument with black dye. The irradiation was performed after root canal preparation (15/100 file or 40/100 file) or directly into the canal. Adverse effects are observed. The results show that laser irradiation on root canal dentin surfaces induces a nonhomogeneous modified dentin layer, melted and resolidified dentin closed partially dentinal tubules. The removal of debris is not efficient enough. The laser treatment seems to be indicated only for endodontic and periapical spaces sterilization after conventional root canal preparation.

Subcritical water liquefaction of oil palm fruit press fiber in the presence of sodium hydroxide: an optimisation study using response surface methodology.

PubMed

Mazaheri, Hossein; Lee, Keat Teong; Bhatia, Subhash; Mohamed, Abdul Rahman

2010-12-01

Thermal decomposition of oil palm fruit press fiber (FPF) into a liquid product (LP) was achieved using subcritical water treatment in the presence of sodium hydroxide in a high pressure batch reactor. This study uses experimental design and process optimisation tools to maximise the LP yield using response surface methodology (RSM) with central composite rotatable design (CCRD). The independent variables were temperature, residence time, particle size, specimen loading, and additive loading. The mathematical model that was developed fit the experimental results well for all of the response variables that were studied. The optimal conditions were found to be a temperature of 551 K, a residence time of 40 min, a particle size of 710-1000 microm, a specimen loading of 5 g, and a additive loading of 9 wt.% to achieve a LP yield of 76.16%. 2010 Elsevier Ltd. All rights reserved.

Optimization Of Fluoride Glass Fiber Drawing With Respect To Mechanical Strength

NASA Astrophysics Data System (ADS)

Schneider, H. W.; Schoberth, A.; Staudt, A.; Gerndt, Ch.

1987-08-01

Heavy metal fluoride fibers have attracted considerable attention recently as lightguides for infrared optical devices. Besides the optical loss mechanical performance of the fiber is of major interest. At present fiber strength suffers from surface crystallization prior to or during fiber drawing. We developed an etching method for the preparation of preforms with clean surface. Drawing these preforms under optimized conditions in a dry atmosphere results in fibers with improved strength. So far, mean value of 400 N/mm2 tensile strength have been achieved. Maximum values of 800 N/mm2 measured on etched fibers indicate an even higher strength potential for the material itself.

Activated carbon fiber composite as a new material for electrical and electrochemical applications

NASA Astrophysics Data System (ADS)

Nasr, Mohamed Fathy

Activated carbon fiber (ACF) is a microporous material consisting of three-dimensional network of micrographitic layers. The micrographitic edges have a considerable amount of active functional groups (such as -COOH, -OH, -CO-, -O-) and dangling bonds. The huge specific surface area (up to 3000 m2/g) is another important property of ACF. Exploitation of the high surface area and the reactivity of the functional groups of ACF, through incorporating or doping ACF with transition metal salts (M) and/or binder (B), was used to enhance the electrical properties of ACF. Such treatments created new interfaces such as (ACF/M, ACF/M/B, and ACF/B/M) through which an extra charge can be localized, transferred, or stored. This process can be of great benefit in energy storage devices such as supercapacitors for computer memory backup. In this work, activated carbon fiber nonwoven fabrics have been impregnated with different concentrations of organometallic Cu and Zn salts, a carbonaceous sot binder, or mixtures of both, followed by thermal treatment over a temperature range 300°C--900°C under an inert atmosphere. The use of carbonaceous sot as a binder has used in the study, is novel. Electrical measurements, current-voltage characterization, current-time relationship, as well as the relative permittivity and impedance of ACF composites, have been conducted. The electric double-layer capacitance of the as-received and the ACF composites were also evaluated.

Comparison of flat cleaved and cylindrical diffusing fibers as treatment sources for interstitial photodynamic therapy.

PubMed

Baran, Timothy M; Foster, Thomas H

2014-02-01

For interstitial photodynamic therapy (iPDT) of bulky tumors, careful treatment planning is required in order to ensure that a therapeutic dose is delivered to the tumor, while minimizing damage to surrounding normal tissue. In clinical contexts, iPDT has typically been performed with either flat cleaved or cylindrical diffusing optical fibers as light sources. Here, the authors directly compare these two source geometries in terms of the number of fibers and duration of treatment required to deliver a prescribed light dose to a tumor volume. Treatment planning software for iPDT was developed based on graphics processing unit enhanced Monte Carlo simulations. This software was used to optimize the number of fibers, total energy delivered by each fiber, and the position of individual fibers in order to deliver a target light dose (D90) to 90% of the tumor volume. Treatment plans were developed using both flat cleaved and cylindrical diffusing fibers, based on tissue volumes derived from CT data from a head and neck cancer patient. Plans were created for four cases: fixed energy per fiber, fixed number of fibers, and in cases where both or neither of these factors were fixed. When the number of source fibers was fixed at eight, treatment plans based on flat cleaved fibers required each to deliver 7180-8080 J in order to deposit 90 J/cm(2) in 90% of the tumor volume. For diffusers, each fiber was required to deliver 2270-2350 J (333-1178 J/cm) in order to achieve this same result. For the case of fibers delivering a fixed 900 J, 13 diffusers or 19 flat cleaved fibers at a spacing of 1 cm were required to deliver the desired dose. With energy per fiber fixed at 2400 J and the number of fibers fixed at eight, diffuser fibers delivered the desired dose to 93% of the tumor volume, while flat cleaved fibers delivered this dose to 79%. With both energy and number of fibers allowed to vary, six diffusers delivering 3485-3600 J were required, compared to ten flat cleaved fibers delivering 2780-3600 J. For the same number of fibers, cylindrical diffusers allow for a shorter treatment duration compared to flat cleaved fibers. For the same energy delivered per fiber, diffusers allow for the insertion of fewer fibers in order to deliver the same light dose to a target volume.

Comparison of flat cleaved and cylindrical diffusing fibers as treatment sources for interstitial photodynamic therapy

DOE Office of Scientific and Technical Information (OSTI.GOV)

Baran, Timothy M., E-mail: timothy.baran@rochester.edu; Foster, Thomas H.

Purpose: For interstitial photodynamic therapy (iPDT) of bulky tumors, careful treatment planning is required in order to ensure that a therapeutic dose is delivered to the tumor, while minimizing damage to surrounding normal tissue. In clinical contexts, iPDT has typically been performed with either flat cleaved or cylindrical diffusing optical fibers as light sources. Here, the authors directly compare these two source geometries in terms of the number of fibers and duration of treatment required to deliver a prescribed light dose to a tumor volume. Methods: Treatment planning software for iPDT was developed based on graphics processing unit enhanced Montemore » Carlo simulations. This software was used to optimize the number of fibers, total energy delivered by each fiber, and the position of individual fibers in order to deliver a target light dose (D{sub 90}) to 90% of the tumor volume. Treatment plans were developed using both flat cleaved and cylindrical diffusing fibers, based on tissue volumes derived from CT data from a head and neck cancer patient. Plans were created for four cases: fixed energy per fiber, fixed number of fibers, and in cases where both or neither of these factors were fixed. Results: When the number of source fibers was fixed at eight, treatment plans based on flat cleaved fibers required each to deliver 7180–8080 J in order to deposit 90 J/cm{sup 2} in 90% of the tumor volume. For diffusers, each fiber was required to deliver 2270–2350 J (333–1178 J/cm) in order to achieve this same result. For the case of fibers delivering a fixed 900 J, 13 diffusers or 19 flat cleaved fibers at a spacing of 1 cm were required to deliver the desired dose. With energy per fiber fixed at 2400 J and the number of fibers fixed at eight, diffuser fibers delivered the desired dose to 93% of the tumor volume, while flat cleaved fibers delivered this dose to 79%. With both energy and number of fibers allowed to vary, six diffusers delivering 3485–3600 J were required, compared to ten flat cleaved fibers delivering 2780–3600 J. Conclusions: For the same number of fibers, cylindrical diffusers allow for a shorter treatment duration compared to flat cleaved fibers. For the same energy delivered per fiber, diffusers allow for the insertion of fewer fibers in order to deliver the same light dose to a target volume.« less

DOE Office of Scientific and Technical Information (OSTI.GOV)

Addleman, Raymond S; Atkinson, David A; Bays, John T

An enhanced swipe sampler and method of making are described. The swipe sampler is made of a fabric containing selected glass, metal oxide, and/or oxide-coated glass or metal fibers. Fibers are modified with silane ligands that are directly attached to the surface of the fibers to functionalize the sampling surface of the fabric. The swipe sampler collects various target analytes including explosives and other threat agents on the surface of the sampler.

Large-scale and highly efficient synthesis of micro- and nano-fibers with controlled fiber morphology by centrifugal jet spinning for tissue regeneration

NASA Astrophysics Data System (ADS)

Ren, Liyun; Pandit, Vaibhav; Elkin, Joshua; Denman, Tyler; Cooper, James A.; Kotha, Shiva P.

2013-02-01

PLLA fibrous tissue scaffolds with controlled fiber nanoscale surface roughness are fabricated with a novel centrifugal jet spinning process. The centrifugal jet spinning technique is a highly efficient synthesis method for micron- to nano-sized fibers with a production rate up to 0.5 g min-1. During the centrifugal jet spinning process, a polymer solution jet is stretched by the centrifugal force of a rotating chamber. By engineering the rheological properties of the polymer solution, solvent evaporation rate and centrifugal force that are applied on the solution jet, polyvinylpyrrolidone (PVP) and poly(l-lactic acid) (PLLA) composite fibers with various diameters are fabricated. Viscosity measurements of polymer solutions allowed us to determine critical polymer chain entanglement limits that allow the generation of continuous fiber as opposed to beads or beaded fibers. Above a critical concentration at which polymer chains are partially or fully entangled, lower polymer concentrations and higher centrifugal forces resulted in thinner fibers. Etching of PVP from the PLLA-PVP composite fibers doped with increasing PVP concentrations yielded PLLA fibers with increasing nano-scale surface roughness and porosity, which increased the fiber hydrophilicity dramatically. Scanning electron micrographs of the etched composite fibers suggest that PVP and PLLA were co-contiguously phase separated within the composite fibers during spinning and nano-scale roughness features were created after the partial etching of PVP. To study the tissue regeneration efficacy of the engineered PLLA fiber matrix, human dermal fibroblasts are used to simulate partial skin graft. Fibers with increased PLLA surface roughness and porosity demonstrated a trend towards higher cell attachment and proliferation.PLLA fibrous tissue scaffolds with controlled fiber nanoscale surface roughness are fabricated with a novel centrifugal jet spinning process. The centrifugal jet spinning technique is a highly efficient synthesis method for micron- to nano-sized fibers with a production rate up to 0.5 g min-1. During the centrifugal jet spinning process, a polymer solution jet is stretched by the centrifugal force of a rotating chamber. By engineering the rheological properties of the polymer solution, solvent evaporation rate and centrifugal force that are applied on the solution jet, polyvinylpyrrolidone (PVP) and poly(l-lactic acid) (PLLA) composite fibers with various diameters are fabricated. Viscosity measurements of polymer solutions allowed us to determine critical polymer chain entanglement limits that allow the generation of continuous fiber as opposed to beads or beaded fibers. Above a critical concentration at which polymer chains are partially or fully entangled, lower polymer concentrations and higher centrifugal forces resulted in thinner fibers. Etching of PVP from the PLLA-PVP composite fibers doped with increasing PVP concentrations yielded PLLA fibers with increasing nano-scale surface roughness and porosity, which increased the fiber hydrophilicity dramatically. Scanning electron micrographs of the etched composite fibers suggest that PVP and PLLA were co-contiguously phase separated within the composite fibers during spinning and nano-scale roughness features were created after the partial etching of PVP. To study the tissue regeneration efficacy of the engineered PLLA fiber matrix, human dermal fibroblasts are used to simulate partial skin graft. Fibers with increased PLLA surface roughness and porosity demonstrated a trend towards higher cell attachment and proliferation. Electronic supplementary information (ESI) available. See DOI: 10.1039/c3nr33423f

The effect of SiO 2-doped boron nitride multiple coatings on mechanical properties of quartz fibers

NASA Astrophysics Data System (ADS)

Zheng, Yu; Wang, Shubin

2012-01-01

SiO2-doped boron nitride multiple coatings (SiO2/BN multiple coatings) were prepared on quartz fibers surface at 700 °C. Single fiber tensile test was employed to evaluate fiber tensile strength; Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) were employed to evaluate morphology and structure of the fibers. Fiber tensile test results indicated that the strength of quartz fibers with SiO2/BN multiple coatings was about twice of the fibers with BN coatings and original fibers which were heated at 700 °C for 10 h. The SiO2/BN multiple coatings would provide compressive stress on quartz fibers, which would help to seal the defects on fiber surface. Furthermore, TEM images showed that the nano-SiO2 powders crystallized in advance of quartz fibers, which would suppress crystallization of quartz fibers and reduce damage from crystallization. Thus, nano-SiO2 powders would help to keep mechanical properties of quartz fibers.

A high selective methanol gas sensor based on molecular imprinted Ag-LaFeO3 fibers.

PubMed

Rong, Qian; Zhang, Yumin; Wang, Chao; Zhu, Zhongqi; Zhang, Jin; Liu, Qingju

2017-09-21

Ag-LaFeO 3 molecularly imprinted polymers (ALMIPs) were fabricated, which provided special recognition sites to methanol. Then ALMIPs fiber 1, fiber 2 and fiber 3 were prepared using filter paper, silk and carbon fibers template, respectively. Based on the observation of X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), and Nitrogen adsorption surface area analyzer (BET), the structure, morphology and surface area of the fibers were characterized. The ALMIPs fibers (fiber 1, fiber 2 and fiber 3) show excellent selectivity and good response to methanol. The responses to 5 ppm methanol and the optimal operating temperature of ALMIPs fibers are 23.5 and 175 °C (fiber 1), 19.67 and 125 °C (fiber 2), 17.59 and 125 °C (fiber 3), and a lower response (≤10, 3, 2) to other test gases including formaldehyde, acetone, ethanol, ammonia, gasoline and benzene was measured, respectively.

Nd:YAG-laser-based time-domain reflectometry measurements of the intrinsic reflection signature from PMMA fiber splices

NASA Astrophysics Data System (ADS)

Lawson, Christopher M.; Michael, Robert R., Jr.; Dressel, Earl M.; Harmony, David W.

1991-12-01

Optical time domain reflectometry (OTDR) measurements have been performed on polished polymethylmethacrylate (PMMA) plastic fiber splices. After the dominant splice reflection sources due to surface roughness, inexact index matching, and fiber core misalignment were eliminated, an intrinsic OTDR signature 3 - 8 dB above the Rayleigh backscatter floor remained with all tested fibers. This minimum splice reflectivity exhibits characteristics that are consistent with sub-surface polymer damage and can be used for detection of PMMA fiber splices.

Interlaminar and ductile characteristics of carbon fibers-reinforced plastics produced by nanoscaled electroless nickel plating on carbon fiber surfaces.

PubMed

Park, Soo-Jin; Jang, Yu-Sin; Rhee, Kyong-Yop

2002-01-15

In this work, a new method based on nanoscaled Ni-P alloy coating on carbon fiber surfaces is proposed for the improvement of interfacial properties between fibers and epoxy matrix in a composite system. Fiber surfaces and the mechanical interfacial properties of composites were characterized by atomic absorption spectrophotometer (AAS), scanning electron microscopy (SEM), X-ray photoelectron spectrometry (XPS), interlaminar shear strength (ILSS), and impact strength. Experimental results showed that the O(1s)/C(1s) ratio or Ni and P amounts had been increased as the electroless nickel plating proceeded; the ILSS had also been slightly improved. The impact properties were significantly improved in the presence of Ni-P alloy on carbon fiber surfaces, increasing the ductility of the composites. This was probably due to the effect of substituted Ni-P alloy, leading to an increase of the resistance to the deformation and the crack initiation of the epoxy system.

Use of the short-term inflammatory response in the mouse peritoneal cavity to assess the biological activity of leached vitreous fibers.

PubMed Central

Donaldson, K; Addison, J; Miller, B G; Cullen, R T; Davis, J M

1994-01-01

We used a special-purpose glass microfiber sample, Johns-Manville Code 100/475, to study the effects of various acid and alkali treatments on biological activity as assessed by inflammation in the mouse peritoneal cavity, the leaching of Si, and the phase contrast optical microscopy (PCOM) fiber number. We used mild and medium treatments with oxalic acid and Tris buffer and harsh treatment with concentrated HCl and NaOH. Mild oxalic acid and Tris treatment for 2 weeks had no effect on any of the end-points, but prolonging the mild oxalic acid treatment time to 2 months reduced the biological activity and the fiber number. Medium oxalic acid treatment reduced the biological activity and the fiber number and caused a loss of Si. Medium Tris alkali treatment reduced the PCOM-countable fibers and the biological activity but did not cause a substantial loss of Si. Harsh treatment with strong HCl did not affect the fiber number or cause leaching but the biological activity was reduced; strong NaOH reduced the fiber number and biological activity, and caused marked leaching of Si. The medium oxalic acid conditions (pH 1.4) were more acid than those found in lung cells but produced the same effects (reduction in fiber number and biological activity) as the more physiological mild treatment (pH 4.0), when prolonged. This study suggests that medium oxalic acid treatment can be used as a short-term assay to compare loss of Si, reduction in fiber number, and change in biological activity of vitreous fibers.(ABSTRACT TRUNCATED AT 250 WORDS) PMID:7882922

Hemocompatibility Assessment of Carbonic Anhydrase Modified Hollow Fiber Membranes for Artificial Lungs

PubMed Central

Oh, Heung-Il; Ye, Sang-Ho; Johnson, Carl A.; Woolley, Joshua R.; Federspiel, William J.; Wagner, William R.

2011-01-01

Hollow fiber membrane (HFM)-based artificial lungs can require a large blood-contacting membrane surface area to provide adequate gas exchange. However, such a large surface area presents significant challenges to hemocompatibility. One method to improve carbon dioxide (CO2) transfer efficiency might be to immobilize carbonic anhydrase (CA) onto the surface of conventional HFMs. By catalyzing the dehydration of bicarbonate in blood, CA has been shown to facilitate diffusion of CO2 toward the fiber membranes. This study evaluated the impact of surface modifying a commercially available microporous HFM-based artificial lung on fiber blood biocompatibility. A commercial poly(propylene) Celgard HFM surface was coated with a siloxane, grafted with amine groups, and then attached with CA which has been shown to facilitate diffusion of CO2 toward the fiber membranes. Results following acute ovine blood contact indicated no significant reduction in platelet deposition or activation with the siloxane coating or the siloxane coating with grafted amines relative to base HFMs. However,HFMs with attached CA showed a significant reduction in both platelet deposition and activation compared with all other fiber types. These findings, along with the improved CO2 transfer observed in CA modified fibers, suggest that its incorporation into HFM design may potentiate the design of a smaller, more biocompatible HFM-based artificial lung. PMID:20633159

Multifunctional Carbon Nanotube-Based Sensors for Damage Detection and Self Healing in Structural Composites

DTIC Science & Technology

2010-10-29

established based on the concept of equipotential surface . The effect of nanotube length on the critical charge level is plotted in Fig. 17. Fig...walled carbon nanotubes was used to develop composites with agglomerated regions of nanotubes at the fiber surface [3]. An image of the nanotube...coating on the surface of two E-glass fibers is shown in Fig. 5. Fig. 5. (a) Carbon nanotube agglomerates on the surface of glass fibers in the

Stress transfer in microdroplet tensile test: PVC-coated and uncoated Kevlar-29 single fiber

NASA Astrophysics Data System (ADS)

Zhenkun, Lei; Quan, Wang; Yilan, Kang; Wei, Qiu; Xuemin, Pan

2010-11-01

The single fiber/microdroplet tensile test is applied for evaluating the interfacial mechanics between a fiber and a resin substrate. It is used to investigate the influence of a polymer coating on a Kevlar-29 fiber surface, specifically the stress transfer between the fiber and epoxy resin in a microdroplet. Unlike usual tests, this new test ensures a symmetrical axial stress on the embedded fiber and reduces the stress singularity that appears at the embedded fiber entry. Using a homemade loading device, symmetrical tensile tests are performed on a Kevlar-29 fiber with or without polyvinylchloride (PVC) coating, the surface of which is in contact with two epoxy resin microdroplets during curing. Raman spectra on the embedded fiber are recorded by micro-Raman Spectroscopy under different strain levels. Then they are transformed to the distributions of fiber axis stress based on the relationship between stress and Raman shift. The Raman results reveal that the fiber axial stresses increase with the applied loads, and the antisymmetric interfacial shear stresses, obtained by a straightforward balance of shear-to-axial forces argument, lead to the appearance of shear stress concentrations at a distance to the embedded fiber entry. The load is transferred from the outer fiber to the embedded fiber in the epoxy microdroplet. As is observed by scanning electronic microscopy (SEM), the existence of a flexible polymer coating on the fiber surface reduces the stress transfer efficiency.

Comparison of four lasers (λ = 650, 808, 980, and 1075 nm) for noninvasive creation of deep subsurface lesions in tissue

NASA Astrophysics Data System (ADS)

Chang, Chun-Hung; Wilson, Christopher R.; Fried, Nathaniel M.

2015-07-01

Lasers have been used in combination with applied cooling methods to preserve superficial skin layers (100's μm's) during cosmetic surgery. Preservation of a thicker tissue surface layer (millimeters) may also allow development of other noninvasive laser procedures. We are exploring noninvasive therapeutic laser applications in urology (e.g. laser vasectomy and laser treatment of female stress urinary incontinence), which require surface tissue preservation on the millimeter scale. In this preliminary study, four lasers were compared for noninvasive creation of deep subsurface thermal lesions. Laser energy from three diode lasers (650, 808, and 980 nm) and a Ytterbium fiber laser (1075 nm) was delivered through a custom built, side-firing, laser probe with integrated cooling. An alcohol-based solution at -5 °C was circulated through a flow cell, cooling a sapphire window, which in turn cooled the tissue surface. The probe was placed in contact with porcine liver tissue, ex vivo, kept hydrated in saline and maintained at ~ 35 °C. Incident laser power was 4.2 W, spot diameter was 5.3 mm, and treatment time was 60 s. The optimal laser wavelength tested for creation of deep subsurface thermal lesions during contact cooling of tissues was 1075 nm, which preserved a surface layer of ~ 2 mm. The Ytterbium fiber laser provides a compact, low maintenance, and high power alternative laser source to the Neodymium:YAG laser for noninvasive thermal therapy.

A novel preparation of milk protein/polyethylene terephthalate fabric

NASA Astrophysics Data System (ADS)

Zhou, J. F.; Zheng, D. D.; Zhong, L.; Zhang, F. X.; Zhang, G. X.

2016-07-01

In this work, -NH2 groups were introduced to polyethylene terephthalate (PET) fibers by nitration and reduction method, and then milk protein was grafted on the nitrated and reduced PET (NR PET) fibers by sucrose glycidyl ether crosslinking agent. FTIR suggested the milk protein was successfully grafted on PET fiber surface. SEM images showed a layer of substance covered on the PET fiber surface. DSC demonstrated an excellent thermal stability of milk protein/PET fiber. The moisture regain was improved by milk protein/PET fiber. Moreover, the crease recovery angle and stiffness were retained by the milk protein/PET fabric.

CVD apparatus and process for the preparation of fiber-reinforced ceramic composites

DOEpatents

Caputo, A.J.; Devore, C.E.; Lowden, R.A.; Moeller, H.H.

1990-01-23

An apparatus and process for the chemical vapor deposition of a matrix into a preform having circumferentially wound ceramic fibers, comprises heating one surface of the preform while cooling the other surface thereof. The resulting product may have fibers that are wound on radial planes or at an angle from the radial planes. The fibers can also be precoated with pyrolytic carbon before application of the matrix. The matrix is applied by passing reactant gas through the preform thereof to the other side thereof for the initial deposition of matrix near such other surface of the preform. The matrix fills in the preform from the other side surface thereof to the surface of the side of application thereof until a desired amount of matrix has been deposited. 6 figs.

CVD apparatus and process for the preparation of fiber-reinforced ceramic composites

DOEpatents

Caputo, Anthony J.; Devore, Charles E.; Lowden, Richard A.; Moeller, Helen H.

1990-01-01

An apparatus and process for the chemical vapor deposition of a matrix into a preform having circumferentially wound ceramic fibers, comprises heating one surface of the preform while cooling the other surface thereof. The resulting product may have fibers that are wound on radial planes or at an angle from the radial planes. The fibers can also be precoated with pyrolytic carbon before application of the matrix. The matrix is applied by passing reactant gas through the preform thereof to the other side thereof for the initial deposition of matrix near such other surface of the preform. The matrix fills in the preform from the other side surface thereof to the surface of the side of application thereof until a desired amount of matrix has been deposited.

Lab-on-fiber technology: a new vision for chemical and biological sensing.

PubMed

Ricciardi, Armando; Crescitelli, Alessio; Vaiano, Patrizio; Quero, Giuseppe; Consales, Marco; Pisco, Marco; Esposito, Emanuela; Cusano, Andrea

2015-12-21

The integration of microfluidics and photonic biosensors has allowed achievement of several laboratory functions in a single chip, leading to the development of photonic lab-on-a-chip technology. Although a lot of progress has been made to implement such sensors in small and easy-to-use systems, many applications such as point-of-care diagnostics and in vivo biosensing still require a sensor probe able to perform measurements at precise locations that are often hard to reach. The intrinsic property of optical fibers to conduct light to a remote location makes them an ideal platform to meet this demand. The motivation to combine the good performance of photonic biosensors on chips with the unique advantages of optical fibers has thus led to the development of the so-called lab-on-fiber technology. This emerging technology envisages the integration of functionalized materials on micro- and nano-scales (i.e. the labs) with optical fibers to realize miniaturized and advanced all-in-fiber probes, especially useful for (but not limited to) label-free chemical and biological applications. This review presents a broad overview of lab-on-fiber biosensors, with particular reference to lab-on-tip platforms, where the labs are integrated on the optical fiber facet. Light-matter interaction on the fiber tip is achieved through the integration of thin layers of nanoparticles or nanostructures supporting resonant modes, both plasmonic and photonic, highly sensitive to local modifications of the surrounding environment. According to the physical principle that is exploited, different configurations - such as localized plasmon resonance probes, surface enhanced Raman scattering probes and photonic probes - are classified, while various applications are presented in context throughout. For each device, the surface chemistry and the related functionalization protocols are reviewed. Moreover, the implementation strategies and fabrication processes, either based on bottom-up or top-down approaches, are discussed. In conclusion we highlight some of the further development opportunities, including lab-in-a-needle technology, which could have a direct and disruptive impact in localized cancer treatment applications.

Electrospinning of single wall carbon nanotube reinforced aligned fibrils and yarns

NASA Astrophysics Data System (ADS)

Lam, Hoa Le

Commercial carbon fibers produced from a polyacrylonitrile (PAN) precursor have reached their performance limit. The approach in this study involves the use of single carbon nanotubes (SWNT) with an ultra-high elastic modulus of approximately ˜1 TPa and tensile strength of ˜37 GPa at a breaking strain of ˜6% to reinforce PAN. In order to translate these extraordinary properties to a higher order structure, the need for a media to carry and assemble the SWNT into continuous fibers or yarns is necessary. Effective translation of properties can only be achieved through uniform distribution of SWNT and their alignment in the fiber axis. This has been one of the major challenges since SWNTs tend to agglomerate due to high van der Waals attraction between tubes. It is the goal of this study to develop dispersion technique(s) for the SWNT and process them into aligned fibers utilizing the electrospinning process. The electrospun nanofibers were then characterized by various techniques such as ESEM, Raman microspectroscopy, HRTEM, and tensile testing. Composite nanofibers containing various contents of SWNT up to 10 wt. % with diameter ranging from 40--300 nm were successfully electrospun through varying the polymer concentration and spinning parameters. The inclusion of SWNTs and their alignment in the fiber axis were confirmed by Raman microspectroscopy, polarized Raman and HRETEM. The failure mechanism of the nanofibers was investigated by HRTEM through fiber surface fracture. A two stage rupture mechanism was observed where crazing initiates at a surface defect followed by SWNTs pulling out of the PAN matrix. Such mechanisms consume energy therefore strengthening and toughening the fibers. Mechanical drawing of the fiber prior to heat treatment induced molecular orientation resulting in oriented graphite layers in the carbonized fibers. This study has established a processing base and characterization techniques to support the design and development of SWNT reinforced PAN-derived carbon nanofibers. The encouraging results from this study suggest a promising pathway to produce the next generation of high performance CNT reinforced carbon nanofibers. This would help in translating of the remarkable properties of SWNT to macroscopic applications, thus filling the dimensional and properties gap between nanoscopic and macroscopic structures.

Activated Carbon Fibers "Thickly Overgrown" by Ag Nanohair Through Self-Assembly and Rapid Thermal Annealing

NASA Astrophysics Data System (ADS)

Yan, Xuefeng; Xu, Sijun; Wang, Qiang; Fan, Xuerong

2017-11-01

Anisotropic nanomaterial-modified carbon fibers attract increasing attention because of their superior properties over traditional ones. In this study, activated carbon fibers (ACFs) "thickly overgrown" by Ag nanohair were prepared through self-assembly and rapid thermal annealing. Viscose fibers with well-dispersed silver nanoparticles (AgNPs) on surfaces were first prepared through self-assembly of hyperbranched poly(amino-amine) (HBPAA)-capped AgNPs on viscose surfaces. HBPAA endowed the AgNP surfaces with negative charges and abundant amino groups, allowing AgNPs to monodispersively self-assemble to fiber surfaces. Ag nanohair-grown ACFs were prepared by sequential pre-oxidation and carbonization. Because the carbonization furnace was open-ended, ACFs are immediately transferrable to the outside of the furnace. Therefore, the Ag liquid adsorbed by ACF pores squeezed out to form Ag nanowires through thermal contraction. FESEM characterization indicated that Ag nanohairs stood on ACF surface and grew from ACF caps. XPS and XRD characterization showed that Ag successfully assembled to fiber surfaces and retained its metallic state even after high-temperature carbonization. TG analysis suggested that Ag nanohair-grown ACFs maintained their excellent thermal stabilities. Finally, the fabricated ACFs showed excellent and durable antibacterial activities, and the developed method may provide a potential strategy for preparing metal nanowire-grown ACFs.

A simple way to an ultra-robust superhydrophobic fabric with mechanical stability, UV durability, and UV shielding property.

PubMed

Ren, Guina; Song, Yuanming; Li, Xiangming; Wang, Bo; Zhou, Yanli; Wang, Yuyan; Ge, Bo; Zhu, Xiaotao

2018-07-15

Development of an ultra-robust superhydrophobic fabric with mechanical stability, UV durability, and UV shielding by a simple method is highly desirable, yet it remains a challenge that current technologies have been unable to fully address. Herein, the original fabric is immersed into the solution containing ZnO nanoparticle and PDMS (polydimethylsiloxane), and the fiber surfaces are uniformly covered by a ZnO-PDMS layer after thermal treatment at 110 °C for 30 min. Droplets of water and corrosive liquids including strong acid, strong alkali, and saturated salt solution display sphere shape on the ZnO-PDMS coated fabric surface. The stable binding of ZnO-PDMS layer onto the fibers allows for the fabric coating with robust superhydrophobicity, and the coated fabric still displays superhydrophobicity after hand twisting, knife scratching, finger touching, and even cycles of sandpaper abrasion. The ZnO-PDMS coated fabric can also keep its superhydrophobic property when exposed to long term UV illumination, demonstrating its UV resistance. Moreover, the uniformly distribution of ZnO nanoparticles on fibers allows the ZnO-PDMS coated fabric to display UV shielding property. Copyright © 2018 Elsevier Inc. All rights reserved.

Radiation properties of two types of luminous textile devices containing plastic optical fibers

NASA Astrophysics Data System (ADS)

Selm, Bärbel; Rothmaier, Markus

2007-05-01

Luminous textiles have the potential to satisfy a need for thin and flexible light diffusers for treatment of intraoral cancerous tissue. Plastic optical fibers (POF) with diameters of 250 microns and smaller are used to make the textiles luminous. Usually light is supplied to the optical fiber at both ends. On the textile surface light emission occurs in a woven structure via damaged straight POFs, whereas the embroidered structure radiates the light out of macroscopically bent POFs. We compared the optical properties of these two types of textile diffusers using red light laser for the embroidery and light emitting diode (LED) for the woven structure as light sources, and found efficiencies for the luminous areas of the two samples of 19 % (woven) and 32 % (embroidery), respectively. It was shown that the efficiency can be greatly improved using an aluminium backing. Additional scattering layers lower the fluence rate by around 30 %. To analyse the homogeneity we took a photo of the illuminated surface using a 3CCD camera and found, for both textiles, a slightly skewed distribution of the dark and bright pixels. The interquartile range of brightness distribution of the embroidery is more than double as the woven structure.

Tribological dry sliding behavior of chopped carbon fiber reinforced polyetheretherketone

NASA Astrophysics Data System (ADS)

Chumaevskii, A. V.; Ivanov, A. N.; Filippov, A. V.; Rubtsov, V. E.; Kolubaev, E. A.

2017-12-01

Tribological tests on 3D printed pure polyetheretherketone and carbon fiber reinforced polyetheretherketone samples were carried out. The negative effect of carbon fiber sticking out of the matrix on wear and sliding process stability was revealed. These fibers may be too long and oriented to the worn surface in a manner that prevents their removal by wear so that the worn surface becomes irregular and the sliding process instable.

Method and apparatus for monitoring and measuring the surface tension of a fluid using fiber optics

DOEpatents

Abraham, B.M.; Ketterson, J.B.; Bohanon, T.M.; Mikrut, J.M.

1994-04-12

A non-contact method and apparatus are described for measuring and monitoring the surface of a fluid using fiber optics and interferometric detection to permit measurement of mechanical characteristics of fluid surfaces. The apparatus employs an alternating electric field gradient for generating a capillary wave on the surface of the fluid. A fiber optic coupler and optical fiber directs a portion of a laser beam onto the surface of the fluid, another portion of the laser beam onto the photo sensor, and directs light reflected from the surface of the fluid onto the photo sensor. The output of the photo sensor is processed and coupled to a phase sensitive detector to permit measurement of phase shift between the drive signal creating the capillary wave and the detected signal. This phase shift information is then used to determine mechanical properties of the fluid surface such as surface tension, surface elasticity, and surface inhomogeneity. The resulting test structure is easily made compact, portable, and easy to align and use. 4 figures.

Laser-Based Surface Modification of Microstructure for Carbon Fiber-Reinforced Plastics

NASA Astrophysics Data System (ADS)

Yang, Wenfeng; Sun, Ting; Cao, Yu; Li, Shaolong; Liu, Chang; Tang, Qingru

2018-05-01

Bonding repair is a powerful feature of carbon fiber-reinforced plastics (CFRP). Based on the theory of interface bonding, the interface adhesion strength and reliability of the CFRP structure will be directly affected by the microscopic features of the CFRP surface, including the microstructure, physical, and chemical characteristics. In this paper, laser-based surface modification was compared to Peel-ply, grinding, and polishing to comparatively evaluate the surface microstructure of CFRP. The surface microstructure, morphology, fiber damage, height and space parameters were investigated by scanning electron microscopy (SEM) and laser confocal microscopy (LCM). Relative to the conventional grinding process, laser modification of the CFRP surface can result in more uniform resin removal and better processing control and repeatability. This decreases the adverse impact of surface fiber fractures and secondary damage. The surface properties were significantly optimized, which has been reflected such things as the obvious improvement of surface roughness, microstructure uniformity, and actual area. The improved surface microstructure based on laser modification is more conducive to interface bonding of CFRP structure repair. This can enhance the interfacial adhesion strength and reliability of repair.

Formation of continuous activated carbon fibers for barrier fabrics

NASA Astrophysics Data System (ADS)

Liang, Ying

1997-08-01

Commercial protective suits made of active carbon granules or nonwoven fabrics are heavy, have low moisture vapor transport rate, and are uncomfortable. Inherent problems due to construction of barrier fabrics lead to severe heat stress when worn for even short time in warm environments. One proposed method to eliminate these problems is to facilitate the construction of a fabric made of continuous activated carbon fibers (CACF). This study is directed toward investigating the possibility of developing CAFC from two precursors: aramid and fibrillated PAN fiber. It was shown in this study that Kevlar-29 fibers could be quickly carbonized and activated to CACF with high adsorptivity and relatively low weight loss. CACF with high surface area (>500 msp2/g) and reasonable tenacity (≈1g/denier) were successfully prepared from Kevlar fibers through a three-step process: pretreatment, carbonization, and activation. X-ray diffraction, Fourier Transform Infrared Spectroscopy (FTIR), and thermal analysis were conducted to understand the evolution of physical and chemical properties during pretreatment. The influence of temperature, heating rate, and pyrolysis environment on the thermal behavior was determined by DSC and TGA/DTA and used as an indicator for optimizing the pyrolysis conditions. Surface analysis by nitrogen isotherms indicated that the resultant fibers had micropores and mesopores on the surface of CACF. This was also inferred by studies on the surface morphology through Scanning Electron Microscopy (SEM) and Scanning Tunneling Microscopy (STM). An investigation of the surface chemical structure by X-ray photoelectron spectroscopy (XPS) before and after activation and elemental analysis confirmed that adsorption of Kevlar based CACF mainly arises due to the physisorption instead of chemisorption. A multistep stabilization along with carbonization and activation was used to prepare active carbon fiber from fibrillated PAN fiber. The resultant fiber retained its fibrillar structure and provided a very high surface area, up to 1400 msp2/g, but was brittle. The characterization of the thermal behavior, mechanical properties, and surface structure of the pyrolyzed fiber at each processing step was also carried out by using various techniques, such as DSC and TGA, Instron, and SEM. These studies provide directions for preparation of CACF from novel precursors.

Surface Modification of Carbon Fiber Polymer Composites after Laser Structuring

NASA Astrophysics Data System (ADS)

Sabau, Adrian S.; Chen, Jian; Jones, Jonaaron F.; Hackett, Alexandra; Jellison, Gerald D.; Daniel, Claus; Warren, David; Rehkopf, Jackie D.

The increasing use of Carbon Fiber-reinforced Polymer matrix Composites (CFPC) as a lightweight material in automotive and aerospace industries requires the control of surface morphology. In this study, the composites surface was prepared by ablating the resin on the top fiber layer of the composite using an Nd:YAG laser. The CFPC specimens with T700S carbon fiber and Prepreg — T83 resin (epoxy) were supplied by Plasan Carbon Composites, Inc. as 4 ply thick, 0/90° plaques. The effect of laser fluence, scanning speed, and wavelength was investigated on the removal rate of the resin without an excessive damage of the fibers. In addition, resin ablation due to the power variation created by a laser interference technique is presented. Optical property measurements, optical micrographs, 3D imaging, and high-resolution optical profiler images were used to study the effect of the laser processing on surface morphology.

Characteristics and formation mechanism for stainless steel fiber with periodic micro-fins

NASA Astrophysics Data System (ADS)

Tang, Tao; Wan, Zhenping; Lu, Longsheng; Tang, Yong

2016-05-01

Metal fibers have been widely used in many industrial applications due to their unique advantages. In certain applications, such as catalyst supports or orthopedic implants, a rough surface or tiny outshoots on the surface of metal fibers to increase surface area are needed. However, it has not been concerned about the surface morphologies of metal fiber in the current research of metal fiber manufacturing. In this paper, a special multi-tooth tool composed of a row of triangular tiny teeth is designed. The entire cutting layer of multi-tooth tool bifurcates into several thin cutting layers due to tiny teeth involved in cutting. As a result, several stainless steel fibers with periodic micro-fins are produced simultaneously. Morphology of periodic micro-fins is found to be diverse and can be classified into three categories: unilateral plane, unilateral tapering and bilateral. There are two forming mechanisms for the micro-fins. One is that periodic burrs remained on the free side of cutting layer of a tiny tooth create micro-fins of stainless steel fiber produced by the next neighboring tiny tooth; the other is that the connections between two fibers stuck together come to be micro-fins if the two fibers are finally detached. Influence of cutting conditions on formation of micro-fins is investigated. Experimental results show that cutting depth has no significant effect on micro-fin formation, high cutting speed is conducive to micro-fin formation, and feed should be between 0.12 mm/r and 0.2 mm/r to reliably obtain stainless steel fiber with micro-fins. This research presents a new pattern of stainless steel fiber characterized by periodic micro-fins formed on the edge of fiber and its manufacturing method.

Antimicrobial Approaches for Textiles: From Research to Market

PubMed Central

Morais, Diana Santos; Guedes, Rui Miranda; Lopes, Maria Ascensão

2016-01-01

The large surface area and ability to retain moisture of textile structures enable microorganisms’ growth, which causes a range of undesirable effects, not only on the textile itself, but also on the user. Due to the public health awareness of the pathogenic effects on personal hygiene and associated health risks, over the last few years, intensive research has been promoted in order to minimize microbes’ growth on textiles. Therefore, to impart an antimicrobial ability to textiles, different approaches have been studied, being mainly divided into the inclusion of antimicrobial agents in the textile polymeric fibers or their grafting onto the polymer surface. Regarding the antimicrobial agents, different types have been used, such as quaternary ammonium compounds, triclosan, metal salts, polybiguanides or even natural polymers. Any antimicrobial treatment performed on a textile, besides being efficient against microorganisms, must be non-toxic to the consumer and to the environment. This review mainly intends to provide an overview of antimicrobial agents and treatments that can be performed to produce antimicrobial textiles, using chemical or physical approaches, which are under development or already commercially available in the form of isolated agents or textile fibers or fabrics. PMID:28773619

The wavelength-tunable tapered surface plasmon resonance fiber sensor based on separated input-output channels

NASA Astrophysics Data System (ADS)

Chen, Shimeng; Liu, Yun; Gao, Xiaotong; Liu, Xiuxin; Peng, Wei

2014-11-01

We present a wavelength-tunable tapered optics fiber surface Plasmon resonance (SPR) sensor by polishing the end faces of multimode fibers(MMF).Two hard plastic clad optical fibers joint closely and are used as the light input and output channels. Their end faces are polished to produce two oblique planes, which are coated with gold film to be the sensing surface and the front mirror. The presence of the tapered geometry formed by the two oblique planes in the orthogonal directions makes it possible to adjust incident angle through changing the tilt angles of the two end faces, so as to achieve tuning the SPR coupling wavelength-angle pair. Compared with previous researches based a tapered optic fiber probe, we report the approach theoretically increase the signal noise ratio (SNR) by separating incident and emergent light propagating in the different coordinate fiber. Since fabricating the sensing surface and the front mirror on the two fibers to replace one single fiber tip, there is more incident light can reach the sensing surface and satisfy SPR effective. In addition, this improvement in structure has advantages of large grinding and sensing area, which can lead to high sensitivity and simple manufacture process of the sensor. Experimental measurement demonstrates the sensor has a favorable SPR resonanceabsorption and the ability of measuring refractive index (RI) of aqueous solution. This novel tapered SPR sensor has the potential to be applied to the biological sensing field.

Fiber Attachment Module Experiment (FAME): Using a Multiplexed Miniature Hollow Fiber Membrane Bioreactor Solution for Rapid Process Testing

NASA Astrophysics Data System (ADS)

Lunn, Griffin; Wheeler, Raymond; Hummerick, Mary; Birmele, Michele; Richards, Jeffrey; Coutts, Janelle; Koss, Lawrence; Spencer, Lashelle.; Johnsey, Marissa; Ellis, Ronald

Bioreactor research, even today, is mostly limited to continuous stirred-tank reactors (CSTRs). These are not an option for microgravity applications due to the lack of a gravity gradient to drive aeration as described by the Archimedes principle. This has led to testing of Hollow Fiber Membrane Bioreactors (HFMBs) for microgravity applications, including possible use for wastewater treatment systems for the International Space Station (ISS). Bioreactors and filtration systems for treating wastewater could avoid the need for harsh pretreatment chemicals and improve overall water recovery. However, the construction of these reactors is difficult and commercial off-the-shelf (COTS) versions do not exist in small sizes. We have used 1-L modular HFMBs in the past, but the need to perform rapid testing has led us to consider even smaller systems. To address this, we designed and built 125-mL, rectangular reactors, which we have called the Fiber Attachment Module Experiment (FAME) system. A polycarbonate rack of four square modules was developed with each module containing removable hollow fibers. Each FAME reactor is self-contained and can be easily plumbed with peristaltic and syringe pumps for continuous recycling of fluids and feeding, as well as fitted with sensors for monitoring pH, dissolved oxygen, and gas measurements similar to their larger counterparts. The first application tested in the FAME racks allowed analysis of over a dozen fiber surface treatments and three inoculation sources to achieve rapid reactor startup and biofilm attachment (based on carbon oxidation and nitrification of wastewater). With these miniature FAME reactors, data for this multi-factorial test were collected in duplicate over a six-month period; this greatly compressed time period required for gathering data needed to study and improve bioreactor performance.

Surface modification of cellulose fibers: towards wood composites by biomimetics.

PubMed

Gradwell, Sheila E; Renneckar, Scott; Esker, Alan R; Heinze, Thomas; Gatenholm, Paul; Vaca-Garcia, Carlos; Glasser, Wolfgang

2004-01-01

A biomimetic approach was taken for studying the adsorption of a model copolymer (pullulan abietate, DS 0.027), representing the lignin-carbohydrate complex, to a model surface for cellulose fibers (Langmuir-Blodgett thin films of regenerated cellulose). Adsorption results were assayed using surface plasmon resonance spectroscopy (SPR) and atomic force microscopy (AFM). Rapid, spontaneous, and desorption-resistant surface modification resulted. This effort is viewed as a critical first step towards the permanent surface modification of cellulose fibers with a layer of molecules amenable to either enzymatic crosslinking for improved wood composites or thermoplastic consolidation.

Characterization of raw and alkali treated new natural cellulosic fiber from Coccinia grandis.L.

PubMed

Senthamaraikannan, P; Kathiresan, M

2018-04-15

The physical, chemical, tensile, crystalline, thermal, and surface morphological properties of raw and alkali treated Coccinia Grandis.L Fibers (CGFs) were characterized for the first time in this work. The results of the chemical analysis indicate that, after alkali treatment, the cellulose content of CGFs increased whereas hemicelluloses, lignin and wax contents decreased. This directly influenced the tensile strength, crystallinity index, thermal stability and the roughness of alkali-treated CGFs. The thermal stability and activation energy of the CGFs improved from 213.4 °C to 220.6 °C and 67.02 kJ/mol to 73.43 kJ/mol, respectively, due to alkali treatment. The statistical approach, Weibull distribution was adopted to analyze the tensile properties. The improved properties of the alkali treated CGF indicate that it could be an appropriate material for reinforcement in polymer composites. Copyright © 2018 Elsevier Ltd. All rights reserved.

Oil sorption and retention capacities of thermally-bonded hybrid nonwovens prepared from cotton, kapok, milkweed and polypropylene fibers.

PubMed

Thilagavathi, G; Praba Karan, C; Das, Dipayan

2018-08-01

This work reports on a series of thermally-bonded, hybrid and oil-sorbent nonwovens developed from binary and tertiary mixing of cotton, kapok, and three varieties of milkweed fibers (Asclepias Syriaca, Calotropis Procera and Calotropis Gigantea) and polypropylene fibers. The physical and chemical properties of the fibers were investigated to examine their oleophilic character. It was observed that all the fiber surfaces were covered with natural wax. Further, kapok and milkweed fibers were found to have less cell wall thickness and high void ratio. Oil sorption and retention characteristics of these fibers were studied in loose fibrous form as well as in structured assembly form (thermally-bonded nonwovens) using high density oil and diesel oil. The effects of fiber diameter, fiber cross-sectional shape, fiber surface area and porosity on the oil sorption behavior were discussed. An excellent and a selective oil sorption behavior of milkweed fibers (Calotropis Procera and Calotropis Gigantea) blended with cotton and polypropylene fibers were observed. The maximum oil sorption capacity of the developed thermal bonded nonwoven was 40.16 g/g for high density (HD) oil and 23.00 g/g for diesel oil. Further, a high porosity combined with high surface area played a major role in deciding the oil sorption and retention characteristics. Copyright © 2018 Elsevier Ltd. All rights reserved.

Translating textiles to tissue engineering: Creation and evaluation of microporous, biocompatible, degradable scaffolds using industry relevant manufacturing approaches and human adipose derived stem cells.

PubMed

Haslauer, Carla M; Avery, Matthew R; Pourdeyhimi, Behnam; Loboa, Elizabeth G

2015-07-01

Polymeric scaffolds have emerged as a means of generating three-dimensional tissues, such as for the treatment of bone injuries and nonunions. In this study, a fibrous scaffold was designed using the biocompatible, degradable polymer poly-lactic acid in combination with a water dispersible sacrificial polymer, EastONE. Fibers were generated via industry relevant, facile scale-up melt-spinning techniques with an islands-in-the-sea geometry. Following removal of EastONE, a highly porous fiber remained possessing 12 longitudinal channels and pores throughout all internal and external fiber walls. Weight loss and surface area characterization confirmed the generation of highly porous fibers as observed via focused ion beam/scanning electron microscopy. Porous fibers were then knit into a three-dimensional scaffold and seeded with human adipose-derived stem cells (hASC). Confocal microscopy images confirmed hASC attachment to the fiber walls and proliferation throughout the knit structure. Quantification of cell-mediated calcium accretion following culture in osteogenic differentiation medium confirmed hASC differentiation throughout the porous constructs. These results suggest incorporation of a sacrificial polymer within islands-in-the-sea fibers generates a highly porous scaffold capable of supporting stem cell viability and differentiation with the potential to generate large three-dimensional constructs for bone regeneration and/or other tissue engineering applications. © 2014 Wiley Periodicals, Inc.

Changes in boron fiber strength due to surface removal by chemical etching

NASA Technical Reports Server (NTRS)

Smith, R. J.

1976-01-01

The effects of chemical etching on the tensile strength of commercial boron/tungsten fibers were investigated. Fibers with as-received diameters of 203, 143, and 100 micrometers were etched to diameters as small as 43 micrometers. The etching generally resulted in increasing fiber tensile strength with decreasing fiber diameter. And for the 203 micrometer fibers there was an accompanying significant decrease in the coefficient of variation of the tensile strength for diameters down to 89 micrometers. Heat treating these fibers above 1,173 K in a vacuum caused a marked decrease in the average tensile strength of at least 80 percent. But after the fibers were etched, their strengths exceeded the as-received strengths. The tensile strength behavior is explained in terms of etching effects on surface flaws and the residual stress pattern of the as-received fibers.

Zinc Oxide Nanowire Interphase for Enhanced Lightweight Polymer Fiber Composites

NASA Technical Reports Server (NTRS)

Sodano, Henry A.; Brett, Robert

2011-01-01

The objective of this work was to increase the interfacial strength between aramid fiber and epoxy matrix. This was achieved by functionalizing the aramid fiber followed by growth of a layer of ZnO nanowires on the fiber surface such that when embedded into the polymer, the load transfer and bonding area could be substantially enhanced. The functionalization procedure developed here created functional carboxylic acid surface groups that chemically interact with the ZnO and thus greatly enhance the strength of the interface between the fiber and the ZnO.

Characterization and Effects of Fiber Pull-Outs in Hole Quality of Carbon Fiber Reinforced Plastics Composite

PubMed Central

Alizadeh Ashrafi, Sina; Miller, Peter W.; Wandro, Kevin M.; Kim, Dave

2016-01-01

Hole quality plays a crucial role in the production of close-tolerance holes utilized in aircraft assembly. Through drilling experiments of carbon fiber-reinforced plastic composites (CFRP), this study investigates the impact of varying drilling feed and speed conditions on fiber pull-out geometries and resulting hole quality parameters. For this study, hole quality parameters include hole size variance, hole roundness, and surface roughness. Fiber pull-out geometries are quantified by using scanning electron microscope (SEM) images of the mechanically-sectioned CFRP-machined holes, to measure pull-out length and depth. Fiber pull-out geometries and the hole quality parameter results are dependent on the drilling feed and spindle speed condition, which determines the forces and undeformed chip thickness during the process. Fiber pull-out geometries influence surface roughness parameters from a surface profilometer, while their effect on other hole quality parameters obtained from a coordinate measuring machine is minimal. PMID:28773950

Impact behaviour of auxetic Kevlar®/ epoxy composites

NASA Astrophysics Data System (ADS)

Yang, S.; Chalivendra, V. B.; Kim, Y. K.

2017-10-01

Experimental study was performed to investigate fracture and impact properties of novel Auxetic Kevlar® laminated composites. For comparison, standard Kevlar® woven composites with and without polyurethane surface treatment were also considered in this study. For these three composites, short nylon fibers of two different fiber lengths and three different fiber densities were flocked between laminates. Vacuum infusion process along with optimized compaction was employed to fabricate composites. The double cantilever beam configuration was used to investigate the fracture properties. The Auxetic Kevlar® composites showed a significant improvement of 225% in fracture toughness compared to regular woven Kevlar® composites. Furthermore, the initiation toughness was increased by 577% with the application of flocking in Auxetic Kevlar®. During impact testing, the Auxetic Kevlar® reinforced composites showed a significant reduction in damaged area compared to woven counterpart. On the other hand, the reduction in damaged area influenced the reduction in impact energy absorption.

Electrodeposited polyaniline as a fiber coating for solid-phase microextraction of organochlorine pesticides from water.

PubMed

Li, Xiang; Zhong, Ming; Chen, Jianmin

2008-08-01

The study on the performance of polyaniline as a fiber coating for solid-phase microextraction (SPME) purposes has been reported. Polyaniline coatings were directly electrodeposited on the surface of a stainless steel wire and applied for the extraction of some organochlorine pesticides (OCPs) from water samples. Analyses were performed using GC-electron capture detection (GC-ECD). The results obtained show that polyaniline fiber coating is suitable for the successful extraction of organochlorine compounds. This behavior is most probably due to the porous surface structure of polyaniline film, which provides large surface areas and allowed for high extraction efficiency. Experimental parameters such as adsorption and desorption conditions were studied and optimized. The optimized method has an acceptable linearity, with a concentration range of 1-5000 ng/L. Single fiber repeatability and fiber-to-fiber reproducibility were less than 12 and 17%, respectively. High environmental resistance and lower cost are among the advantages of polyaniline fibers over commercially available SPME fibers. The developed method was applied to the analysis of real water samples from Yangtse River and Tianmu Lake.

Activated Carbon Fibers with Hierarchical Nanostructure Derived from Waste Cotton Gloves as High-Performance Electrodes for Supercapacitors.

PubMed

Wei, Chao; Yu, Jianlin; Yang, Xiaoqing; Zhang, Guoqing

2017-12-01

One of the most challenging issues that restrict the biomass/waste-based nanocarbons in supercapacitor application is the poor structural inheritability during the activating process. Herein, we prepare a class of activated carbon fibers by carefully selecting waste cotton glove (CG) as the precursor, which mainly consists of cellulose fibers that can be transformed to carbon along with good inheritability of their fiber morphology upon activation. As prepared, the CG-based activated carbon fiber (CGACF) demonstrates a surface area of 1435 m 2  g -1 contributed by micropores of 1.3 nm and small mesopores of 2.7 nm, while the fiber morphology can be well inherited from the CG with 3D interconnected frameworks created on the fiber surface. This hierarchically porous structure and well-retained fiber-like skeleton can simultaneously minimize the diffusion/transfer resistance of the electrolyte and electron, respectively, and maximize the surface area utilization for charge accumulation. Consequently, CGACF presents a higher specific capacitance of 218 F g -1 and an excellent high-rate performance as compared to commercial activated carbon.

Plug Repairs of Marine Glass Fiber / Vinyl Ester Laminates Subjected to Uniaxial Tension

DTIC Science & Technology

2009-06-01

Material characteristics of glass fiber / vinyl ester composites used in naval surface ships 1.1.1.2 Construction of surface ship hulls with FRP...Piping - Ventilation ducts - Deck gratings 1.1.1.1 Material characteristics of glass fiber / vinyl ester composites used in naval surface ships The...that polysester-based composites do [15, 24]. Typical processing methods for vinyl ester composites are hand lay-up, Resin Transfer Molding (RTM

Effect of glass fiber surface treatments on mechanical strength of epoxy based composite materials.

PubMed

Iglesias, J G; González-Benito, J; Aznar, A J; Bravo, J; Baselga, J

2002-06-01

Sizing glass fibers with silane coupling agents enhances the adhesion and the durability of the fiber/polymer matrix interface in composite materials. There are several tests to determine the interfacial strength between a fiber and resin, but all of them present difficulties in interpreting the results and/or sample preparation. In this study, we observed the influence of different aminosilanes fiber coatings on the resistance of epoxy-based composite materials using a very easy fractographic test. In addition, we tried a new fluorescence method to get information on a molecular level precisely at the interface. Strength was taken into account from two standpoints: (i) mechanical strength and (ii) the resistance to hydrolysis of the interface in oriented glass-reinforced epoxy-based composites. Three silanes: gamma-aminopropyltriethoxysilane, gamma-Aminopropylmethyldiethoxysilane, and gamma-Aminopropyldimethylethoxysilane were used to obtain different molecular structures at the interface. It was concluded that: (i) the more accessible amine groups are, the higher the interface rigidity is; (ii) an interpenetrating network mechanism seems to be the most important for adhesion and therefore to the interfacial strength; and (iii) the higher the degree of crosslinking in the silane coupling layer is, the higher the hydrolytic damage rate is.

Preparation of electrospun pyrochlore-structure KGdTa2O7:Eu3+ phosphor: the optical and structural properties for white light emitting diode applications.

PubMed

Yim, Chul Jin; Unithrattil, Sanjith; Chung, Woon Jin; Im, Won Bin

2013-12-01

Red emitting nanofibers, KGdTa2O7:Eu3+ were synthesized by electrospinning technique followed by heat treatment. As-prepared uniform fiber precursor with diameter ranging from about 700 nm to about 900 nm were calcined after removing organic species by calcination. The fiber surface become rough and diameter decreased to about 250-340 nm range due to decomposition of organic species and formation of inorganic phase. Morphology, structural and photoluminescent properties of fibers were analyzed using thermogravimetric and differential thermal analysis (TG-DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), and photoluminescence (PL). TG-DTA analysis indicates that KGdTa2O7:Eu3+ began to crystalize at 520 degrees C. Fibers annealed at 900 degrees C formed well crystallized uniform fibers. Under ultraviolet excitation KGdTa2O7:Eu3+ exhibits red emission due to transitions in 4f states of Eu3+. The excitation band is dominated by the Eu(3+)--O2-charge transfer band peaked at 289 nm. The emission peak is in the region that is ideal for red light emission.

Graphene-deposited photonic crystal fibers for continuous refractive index sensing applications.

PubMed

Tan, Y C; Tou, Z Q; Chow, K K; Chan, C C

2015-11-30

We present a pilot demonstration of an optical fiber based refractive index (RI) sensor involving the deposition of graphene onto the surface of a segment of a photonic crystal fiber (PCF) in a fiber-based Mach-Zehnder Interferometer (MZI). The fabrication process is relatively simple and only involves the fusion splicing of a PCF between two single mode fibers. The deposition process relies only on the cold transfer of graphene onto the PCF segment, without the need for further physical or chemical treatment. The graphene overlay modified the sensing scheme of the MZI RI sensor, allowing the sensor to overcome limitations to its detectable RI range due to free spectral range issues. This modification also allows for continuous measurements to be obtained without the need for reference values for the range of RIs studied and brings to light the potential for simultaneous dual parameter sensing. The sensor was able to achieve a RI sensitivity of 9.4 dB/RIU for the RIs of 1.33-1.38 and a sensitivity of 17.5 dB/RIU for the RIs of 1.38-1.43. It also displayed good repeatability and the results obtained were consistent with the modeling.

Carbon Nanotubes Growth on Graphite Fibers

NASA Technical Reports Server (NTRS)

Zhu, Shen; Su, Ching-Hua; Lehoczky, S. L.; Muntele, I.; Ila, D.; Curreri, Peter A. (Technical Monitor)

2002-01-01

Carbon nanotubes (CNT) were synthesized on graphite fibers by thermal Chemical Vapor Deposition (CVD). On the fiber surface, iron nanoparticles are coated and act as catalysts for CNT growth. The growth temperature ranges from 550 to 1000 C at an ambient pressure. Methane and hydrogen gases with methane contents of 10% to 100% are used for the CNT synthesis. At high growth temperatures (greater than 800 C), the rapid inter-diffusion of the transition metal iron on the graphite surface results in a rough fiber surface with no CNT grown on the surface. When the growth temperature is relatively low (650 - 800 C), CNT are fabricated on the graphite surface with catalytic particles on the nanotube top ends. Using micro Raman spectroscopy in the breath mode region, single-walled or multi-walled CNT can be determined, depending on methane concentrations.

Functional electrospun fibers for the treatment of human skin wounds.

PubMed

Wang, Jing; Windbergs, Maike

2017-10-01

Wounds are trauma induced defects of the human skin involving a multitude of endogenous biochemical events and cellular reactions of the immune system. The healing process is extremely complex and affected by the patient's physiological conditions, potential implications like infectious pathogens and inflammation as well as external factors. Due to increasing incidence of chronic wounds and proceeding resistance of infection pathogens, there is a strong need for effective therapeutic wound care. In this context, electrospun fibers with diameters in the nano- to micrometer range gain increasing interest. While resembling the structure of the native human extracellular matrix, such fiber mats provide physical and mechanical protection (including protection against bacterial invasion). At the same time, the fibers allow for gas exchange and prevent occlusion of the wound bed, thus facilitating wound healing. In addition, drugs can be incorporated within such fiber mats and their release can be adjusted by the material and dimensions of the individual fibers. The review gives a comprehensive overview about the current state of electrospun fibers for therapeutic application on skin wounds. Different materials as well as fabrication techniques are introduced including approaches for incorporation of drugs into or drug attachment onto the fiber surface. Against the background of wound pathophysiology and established therapy approaches, the therapeutic potential of electrospun fiber systems is discussed. A specific focus is set on interactions of fibers with skin cells/tissues as well as wound pathogens and strategies to modify and control them as key aspects for developing effective wound therapeutics. Further, advantages and limitations of controlled drug delivery from fiber mats to skin wounds are discussed and a future perspective is provided. Copyright © 2017 Elsevier B.V. All rights reserved.

Surface modification of carbon fibers by a polyether sulfone emulsion sizing for increased interfacial adhesion with polyether sulfone

NASA Astrophysics Data System (ADS)

Yuan, Haojie; Zhang, Shouchun; Lu, Chunxiang

2014-10-01

Interests on carbon fiber-reinforced thermoplastic composites are growing rapidly, but the challenges with poor interfacial adhesion have slowed their adoption. In this work, a polyether sulfone (PES) emulsion sizing was prepared successfully for increased interfacial adhesion of carbon fiber/PES composites. To obtain a high-quality PES emulsion sizing, the key factor, emulsifier concentration, was studied by dynamic light scattering technique. The results demonstrated that the suitable weight ratio of PES to emulsifier was 8:3, and the resulting PES emulsion sizing had an average particle diameter of 117 nm and Zeta potential of -52.6 mV. After sizing, the surface oxygen-containing functional groups, free energy and wettability of carbon fibers increased significantly, which were advantageous to promote molecular-level contact between carbon fiber and PES. Finally, short beam shear tests were performed to evaluate the interfacial adhesion of carbon fiber/PES composites. The results indicated that PES emulsion sizing played a critical role for the enhanced interfacial adhesion in carbon fiber/PES composites, and a 26% increase of interlaminar shear strength was achieved, because of the improved fiber surface wettability and interfacial compatibility between carbon fiber and PES.

Path Planning Based on Ply Orientation Information for Automatic Fiber Placement on Mesh Surface

NASA Astrophysics Data System (ADS)

Pei, Jiazhi; Wang, Xiaoping; Pei, Jingyu; Yang, Yang

2018-03-01

This article introduces an investigation of path planning with ply orientation information for automatic fiber placement (AFP) on open-contoured mesh surface. The new method makes use of the ply orientation information generated by loading characteristics on surface, divides the surface into several zones according to the ply orientation information and then designs different fiber paths in different zones. This article also gives new idea of up-layer design in order to make up for defects between parts and improve product's strength.

Subtle charge balance controls surface-nucleated self-assembly of designed biopolymers.

PubMed

Charbonneau, Céline; Kleijn, J Mieke; Cohen Stuart, Martien A

2014-03-25

We report the surface-nucleated self-assembly into fibrils of a biosynthetic amino acid polymer synthesized by the yeast Pichia pastoris. This polymer has a block-like architecture, with a central silk-like block labeled SH, responsible for the self-assembly into fibrils, and two collagen-like random coil end blocks (C) that colloidally stabilize the fibers in aqueous solution. The silk-like block contains histidine residues (pKa≈6) that are positively charged in the low pH region, which hinders self-assembly. In aqueous solution, CSHC self-assembles into fibers above a pH-dependent critical nucleation concentration Ccb. Below Ccb, where no self-assembly occurs in solution, fibril formation can be induced by a negatively charged surface (silica) in the pH range of 3.5-7. The density of the fibers at the surface and their length are controlled by a subtle balance in charge between the protein polymer and the silica surface, which is evidenced from the dependence on pH. With increasing number density of the fibers at the surface, their average length decreases. The results can be explained on the basis of a nucleation-and-growth mechanism: the surface density of fibers depends on the rate of nucleation, while their growth rate is limited by transport of proteins from solution. Screening of the charges on the surface and histidine units by adding NaCl influences the nucleation-and-growth process in a complicated fashion: at low pH, the growth is improved, while at high pH, the nucleation is limited. Under conditions where nucleation in the bulk solution is not possible, growth of the surface-nucleated fibers into the solution--away from the surface--can still occur.

Removal of phosphorus using AMD-treated lignocellulosic material

Treesearch

James S. Han; Soo-Hong Min; Yeong-Kwan Kim

2005-01-01

Excess nutrients, including phosphorus, can cause eutrophication in surface water and reservoirs. We tested the phosphate removal capacity of juniper fiber through isotherm, kinetic, column, and field tests. Heavy metals from an acid mine drainage (AMD) site were precipitated on the surface ofjuniper fiber. The modified fiber was tested in laboratory- caled batch and...

Investigation of surface properties of pristine and γ-irradiated PAN-based carbon fibers: Effects of fiber instinct structure and radiation medium

NASA Astrophysics Data System (ADS)

Liu, Liangsen; Wu, Fan; Yao, Hongwei; Shi, Jie; Chen, Lei; Xu, Zhiwei; Deng, Hui

2015-05-01

The different rules for γ-ray modifications of carbon fiber (CF) surface were found in previous literature, and the contributing factors were not clear. To investigate the effects of fiber instinct structure and radiation medium on surface modification of CFs in γ-ray irradiation, argon atmosphere (Ar) and epoxy chloropropane (ECP) were chosen as the irradiation media for T300, T400, T700, T800 and T1000, respectively. Based on the Raman spectroscopy and specific surface area results, changes of surface graphitization and roughness depended on the fiber instinct structure after irradiation. The graphitization of T300, T400 and T800 with low graphitization and rough surface was increased after irradiation, while that of T700 and T1000 with high graphite degree and smooth surface was decreased. Specific surface areas of low-graphitization CFs (T300, T400 and T800) were changed clearly, while those of high-graphitization CFs (T700 and T1000) remained almost unchanged after irradiation. X-ray photoelectron spectroscopy provided the evidence that the surface chemistry change after irradiation was determined by the type of the irradiation medium. The oxygen ratio of CFs irradiated in Ar was decreased while that of CFs irradiated in ECP was increased with Cl element detected. Surface free energy of all CFs was improved obviously after irradiation, and CFs irradiated in ECP had higher surface free energy compared with CFs irradiated in Ar.

Radial-firing optical fiber tip containing conical-shaped air-pocket for biomedical applications.

PubMed

Lee, Seung Ho; Ryu, Yong-Tak; Son, Dong Hoon; Jeong, Seongmook; Kim, Youngwoong; Ju, Seongmin; Kim, Bok Hyeon; Han, Won-Taek

2015-08-10

We report a novel radial-firing optical fiber tip containing a conical-shaped air-pocket fabricated by deforming a hollow optical fiber using electric arc-discharge process. The hollow optical fiber was fusion spliced with a conventional optical fiber, simultaneously deforming into the intagliated conical-shaped region along the longitudinal fiber-axis of the fiber due to the gradual collapse of the cavity of the hollow optical fiber. Then the distal-end of the hollow optical fiber was sealed by the additional arc-discharge in order to obstruct the inflow of an external bio-substance or liquid to the inner air surface during the surgical operations, resulting in the formation of encased air-pocket in the silica glass fiber. Due to the total internal reflection of the laser beam at the conical-shaped air surface, the laser beam (λ = 632.8 nm) was deflected to the circumferential direction up to 87 degree with respect to the fiber-axis.

A New Fiber Preform with Nanocarbon Binder for Manufacturing Carbon Fiber Reinforced Composite by Liquid Molding Process.

PubMed

Seong, Dong Gi; Ha, Jong Rok; Lee, Jea Uk; Lee, Wonoh; Kim, Byung Sun

2015-11-01

Carbon fiber reinforced composite has been a good candidate of lightweight structural component in the automotive industry. As fast production speed is essential to apply the composite materials for the mass production area such as automotive components, the high speed liquid composite molding processes have been developed. Fast resin injection through the fiber preform by high pressure is required to improve the production speed, but it often results in undesirable deformations of the fiber preform which causes defectives in size and properties of the final composite products. In order to prevent the undesirable deformation and improve the stability of preform shape, polymer type binder materials are used. More stable fiber preform can be obtained by increasing the amount of binder material, but it disturbs the resin impregnation through the fiber preform. In this study, carbon nanomaterials such as graphene oxide were embedded on the surface of carbon fiber by electrophoretic deposition method in order to improve the shape stability of fiber preform and interfacial bonding between polymer and the reinforcing fiber. Effects of the modified reinforcing fiber were investigated in two respects. One is to increase the binding energy between fiber tows, and the other is to increase the interfacial bonding between polymer matrix and fiber surface. The effects were analyzed by measuring the binding force of fiber preform and interlaminar shear strength of the composite. This study also investigated the high speed liquid molding process of the composite materials composed of polymer matrix and the carbon fiber preforms embedded by carbon nanomaterials. Process parameter such as permeability of fiber preform was measured to investigate the effect of nanoscale surface modification on the macroscale processing condition for composite manufacturing.

Physico-chemical characterization of functionalized polypropylenic fibers for prosthetic applications

NASA Astrophysics Data System (ADS)

Nisticò, Roberto; Faga, Maria Giulia; Gautier, Giovanna; Magnacca, Giuliana; D'Angelo, Domenico; Ciancio, Emanuele; Piacenza, Giacomo; Lamberti, Roberta; Martorana, Selanna

2012-08-01

Polypropylene (PP) fibers can be manufactured to form nets which can find application as prosthesis in hernioplasty. One of the most important problem to deal with when nets are applied in vivo consists in the reproduction of bacteria within the net fibers intersections. This occurs right after the application of the prosthesis, and causes infections, thus it is fundamental to remove bacteria in the very early stage of the nets application. This paper deals with the physico-chemical characterization of such nets, pre-treated by atmospheric pressure plasma dielectric barrier discharge apparatus (APP-DBD) and functionalized with an antibiotic drug such as chitosan. The physico-chemical characterization of sterilized nets, before and after the functionalization with chitosan, was carried out by means of scanning electron microscopy (SEM) coupled with EDS spectroscopy, FTIR spectroscopy, drop shape analysis (DSA), X-ray diffraction and thermal analyses (TGA and DSC). The aim of the work is to individuate a good strategy to characterize this kind of materials, to understand the effects of polypropylene pre-treatment on functionalization efficiency, to follow the materials ageing in order to study the effects of the surface treatment for in vivo applications.

Developing a tissue-engineered neural-electrical relay using encapsulated neuronal constructs on conducting polymer fibers.

PubMed

Cullen, D Kacy; R Patel, Ankur; Doorish, John F; Smith, Douglas H; Pfister, Bryan J

2008-12-01

Neural-electrical interface platforms are being developed to extracellularly monitor neuronal population activity. Polyaniline-based electrically conducting polymer fibers are attractive substrates for sustained functional interfaces with neurons due to their flexibility, tailored geometry and controlled electro-conductive properties. In this study, we addressed the neurobiological considerations of utilizing small diameter (<400 microm) fibers consisting of a blend of electrically conductive polyaniline and polypropylene (PA-PP) as the backbone of encapsulated tissue-engineered neural-electrical relays. We devised new approaches to promote survival, adhesion and neurite outgrowth of primary dorsal root ganglion neurons on PA-PP fibers. We attained a greater than ten-fold increase in the density of viable neurons on fiber surfaces to approximately 700 neurons mm(-2) by manipulating surrounding surface charges to bias settling neuronal suspensions toward fibers coated with cell-adhesive ligands. This stark increase in neuronal density resulted in robust neuritic extension and network formation directly along the fibers. Additionally, we encapsulated these neuronal networks on PA-PP fibers using agarose to form a protective barrier while potentially facilitating network stability. Following encapsulation, the neuronal networks maintained integrity, high viability (>85%) and intimate adhesion to PA-PP fibers. These efforts accomplished key prerequisites for the establishment of functional electrical interfaces with neuronal populations using small diameter PA-PP fibers-specifically, improved neurocompatibility, high-density neuronal adhesion and neuritic network development directly on fiber surfaces.

Preparation of superhydrophobic glass fiber and interfacially reinforced glass fiber/epoxy composites by grafting polysiloxane nanowires

NASA Astrophysics Data System (ADS)

Lv, Junwei; Wang, Bin; Ma, Qi; Li, Mengyao; Wang, Wenjing; Lu, Gaotaihang; Li, Hui; Zhao, Chunxia

2018-04-01

Ethyltrichlorosilane used as precursor reacted with glass fiber (GF) surface. Then polysiloxane was functionalized onto GF surface to improve GF’s hydrophobicity and interfacial properties of GF reinforced composites. Fourier transform infrared spectroscopy (FTIR) confirmed the successful grafting of polysiloxane onto GF’s surface. Energy dispersive spectroscopy (EDS) characterized the variation of chemical composition of GF surface. Scanning electron microscopy (SEM) images showed that the polysiloxane was grafted onto GF’s surface uniformly and the surface roughness of GF was enhanced obviously. Static contact angle analysis (SCA) revealed the significant improvement of surface hydrophobicity. Compared with the original GF composites, the interfacial shear strength (IFSS) increased by 36.52%. Meanwhile, we discovered a facile way to accomplish the experiment.

Intrinsic Fabry-Perot optical fiber sensors and their multiplexing

DOEpatents

Wang, Anbo

2007-12-11

An intrinsic Fabry-Perot optical sensor includes a thin film sandwiched between two fiber ends. When light is launched into the fiber, two reflections are generated at the two fiber/thin film interfaces due to a difference in refractive indices between the fibers and the film, giving rise to the sensor output. In another embodiment, a portion of the cladding of a fiber is removed, creating two parallel surfaces. Part of the evanescent fields of light propagating in the fiber is reflected at each of the surfaces, giving rise to the sensor output. In a third embodiment, the refractive index of a small portion of a fiber is changed through exposure to a laser beam or other radiation. Interference between reflections at the ends of the small portion give rise to the sensor output. Multiple sensors along a single fiber are multiplexed using an optical time domain reflectometry method.

Graphite coated PVA fibers as the reinforcement for cementitious composites

NASA Astrophysics Data System (ADS)

Zhang, Yunhua; Zhang, Zhipeng; Liu, Zhichao

2018-02-01

A new preconditioning method was developed to PVA fibers as the reinforcement in cement-based materials. Virgin PVA fibers exhibits limited adhesion to graphite powders due to the presence of oil spots on the surface. Mixing PVA fibers with a moderately concentrated KMnO4-H2SO4 solution can efficiently remove the oil spots by oxidation without creating extra precipitate (MnO2) associated with the reduction reaction. This enhances the coating of graphite powders onto fiber surface and improves the mechanical properties of PVA fiber reinforced concrete (PVA-FRC). Graphite powders yields better fiber distribution in the matrix and reduces the fiber-matrix bonding, which is beneficial in uniformly distributing the stress among embedded fibers and creating steady generation and propagation of tight microcracks. This is evidenced by the significantly enhanced strain hardening behavior and improved flexural strength and toughness.

Characterization of low thermal conductivity PAN-based carbon fibers

NASA Technical Reports Server (NTRS)

Katzman, Howard A.; Adams, P. M.; Le, T. D.; Hemminger, Carl S.

1992-01-01

The microstructure and surface chemistry of eight low thermal conductivity (LTC) PAN-based carbon fibers were determined and compared with PAN-based fibers heat treated to higher temperatures. Based on wide-angle x ray diffraction, the LTC PAN fibers all appear to have a similar turbostratic structure with large 002 d-spacings, small crystallite sizes, and moderate preferred orientation. Limited small-angle x ray scattering (SAXS) results indicate that, with the exception of LTC fibers made by BASF, the LTC fibers do not have well developed pores. Transmission electron microscopy shows that the texture of the two LTC PAN-based fibers studied (Amoco T350/23X and /25X) consists of multiple sets of parallel, wavy, bent layers that interweave with each other forming a complex three dimensional network oriented randomly around the fiber axis. X ray photoelectron spectroscopy (XPS) analysis finds correlations between heat treated temperatures and the surface composition chemistry of the carbon fiber samples.

Microscopic observations during longitudinal compression loading of single pulp fibers

Treesearch

Irving B. Sachs

1986-01-01

Paperboard components (linerboard adn corrugating medium) fail in edgewise compression because of failure of single fibers, as well as fiber-to-fiber bonds. While fiber-to-fiber-bond failure has been studied extensively, little is known about the longitudinal compression failure of a single fiber. In this study, surface alterations on single loblolly pine kraft pulp...

Engineered plant biomass feedstock particles

DOEpatents

Dooley, James H [Federal Way, WA; Lanning, David N [Federal Way, WA; Broderick, Thomas F [Lake Forest Park, WA

2012-04-17

A new class of plant biomass feedstock particles characterized by consistent piece size and shape uniformity, high skeletal surface area, and good flow properties. The particles of plant biomass material having fibers aligned in a grain are characterized by a length dimension (L) aligned substantially parallel to the grain and defining a substantially uniform distance along the grain, a width dimension (W) normal to L and aligned cross grain, and a height dimension (H) normal to W and L. In particular, the L.times.H dimensions define a pair of substantially parallel side surfaces characterized by substantially intact longitudinally arrayed fibers, the W.times.H dimensions define a pair of substantially parallel end surfaces characterized by crosscut fibers and end checking between fibers, and the L.times.W dimensions define a pair of substantially parallel top and bottom surfaces. The L.times.W surfaces of particles with L/H dimension ratios of 4:1 or less are further elaborated by surface checking between longitudinally arrayed fibers. The length dimension L is preferably aligned within 30.degree. parallel to the grain, and more preferably within 10.degree. parallel to the grain. The plant biomass material is preferably selected from among wood, agricultural crop residues, plantation grasses, hemp, bagasse, and bamboo.

Surface Acoustic Waves Grant Superior Spatial Control of Cells Embedded in Hydrogel Fibers.

PubMed

Lata, James P; Guo, Feng; Guo, Jinshan; Huang, Po-Hsun; Yang, Jian; Huang, Tony Jun

2016-10-01

By exploiting surface acoustic waves and a coupling layer technique, cells are patterned within a photosensitive hydrogel fiber to mimic physiological cell arrangement in tissues. The aligned cell-polymer matrix is polymerized with short exposure to UV light and the fiber is extracted. These patterned cell fibers are manipulated into simple and complex architectures, demonstrating feasibility for tissue-engineering applications. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Controlling the Electrochemically Active Area of Carbon Fiber Microelectrodes by the Electrodeposition and Selective Removal of an Insulating Photoresist

PubMed Central

Lambie, Bradley A.; Orwar, Owe; Weber, Stephen G.

2008-01-01

A new and simple method permits control of the electrochemically active area of a carbon fiber microelectrode. An electrophoretic photoresist insulates the 10 μm diameter carbon fiber microelectrodes. Photolysis of the photoresist followed by immersion of the exposed area into a developing solution reveals electroactive carbon fiber surface. The electroactive surface area exposed can be controlled with a good degree of reproducibility. PMID:16841943

Glue-induced birefringence in surface-attached FBG strain sensors

NASA Astrophysics Data System (ADS)

Helminger, Dominik; Daitche, Alexej; Roths, Johannes

2014-05-01

The influence of the gluing process on the birefringence of surface-glued FBGs that were inscribed in highly birefringence (HiBi) optical fibers of type Panda was studied by monitoring the variation of the birefringence during the gluing procedure. The isothermal curing process at 100°C of the epoxy-based adhesive is characterized by the reduction of birefringence during curing. Significant transversal strain is introduced into the fiber during the cool down period, which is due to different thermal expansion coefficients of the silica and the glue. When the slow axis of the HiBi fiber is oriented parallel to the surface, the glue-induced transversal strain reduces the birefringence of the fiber by ΔB = -6.6 10-5 and when it is perpendicular to the surface, it is increased by ΔB = 1.1 10-5. It can be estimated that for conventional FBGs in single mode fibers a glue-induced birefringence in the order of ΔB = 3.4 10-5 can be expected, which has to be taken into account if in surface-mounted FBG-based strain measurements a high accuracy has to be achieved.

Engineered plant biomass feedstock particles

DOEpatents

Dooley, James H [Federal Way, WA; Lanning, David N [Federal Way, WA; Broderick, Thomas F [Lake Forest Park, WA

2011-10-11

A novel class of flowable biomass feedstock particles with unusually large surface areas that can be manufactured in remarkably uniform sizes using low-energy comminution techniques. The feedstock particles are roughly parallelepiped in shape and characterized by a length dimension (L) aligned substantially with the grain direction and defining a substantially uniform distance along the grain, a width dimension (W) normal to L and aligned cross grain, and a height dimension (H) normal to W and L. The particles exhibit a disrupted grain structure with prominent end and surface checks that greatly enhances their skeletal surface area as compared to their envelope surface area. The L.times.H dimensions define a pair of substantially parallel side surfaces characterized by substantially intact longitudinally arrayed fibers. The W.times.H dimensions define a pair of substantially parallel end surfaces characterized by crosscut fibers and end checking between fibers. The L.times.W dimensions define a pair of substantially parallel top surfaces characterized by some surface checking between longitudinally arrayed fibers. The feedstock particles are manufactured from a variety of plant biomass materials including wood, crop residues, plantation grasses, hemp, bagasse, and bamboo.

Intrapulpal temperatures during pulsed Nd:YAG laser treatment of dentin, in vitro.

PubMed

White, J M; Fagan, M C; Goodis, H E

1994-03-01

Lasers are being used for soft tissue removal, caries removal, and treatment of root surface sensitivity. One concern for laser safety is that the heat produced at the irradiated root surface may diffuse to the pulp causing irreversible pulpal damage. To test this heat diffusion, copper-constantan thermocouples were inserted into the radicular pulp canals of extracted teeth. Simulating direct exposure which might occur during gingival excision, superficial caries removal, and modification of the dentin surface for treatment of root surface sensitivity, a 2 mm2 area of the external root surface was uniformly irradiated with a pulsed Nd:YAG laser using a 320 microns diameter fiber optic contact probe. Power was varied from 0.3 to 3.0 W with frequencies of 10 and 20 Hz. Temperature changes during cavity preparations using a high speed handpiece with air coolant were also recorded. Repeated measures ANOVA (P < or = 0.05) indicated that intrapulpal temperatures increased as a function of power, frequency, and time. Intrapulpal temperatures decreased as remaining dentin thickness (0.2 to 2.0 mm) increased for each laser parameter. Irradiation of dentin using a Nd:YAG pulsed laser, within the treatment times, powers, and frequencies with adequate remaining dentin thickness, as outlined in this paper, should not cause devitalizing intrapulpal temperature rises.

Three-dimensional carbon fibers and method and apparatus for their production

DOEpatents

Muradov, Nazim Z [Melbourne, FL

2012-02-21

This invention relates to novel three-dimensional (3D) carbon fibers which are original (or primary) carbon fibers (OCF) with secondary carbon filaments (SCF) grown thereon, and, if desired, tertiary carbon filaments (TCF) are grown from the surface of SCF forming a filamentous carbon network with high surface area. The methods and apparatus are provided for growing SCF on the OCF by thermal decomposition of carbonaceous gases (CG) over the hot surface of the OCF without use of metal-based catalysts. The thickness and length of SCF can be controlled by varying operational conditions of the process, e.g., the nature of CG, temperature, residence time, etc. The optional activation step enables one to produce 3D activated carbon fibers with high surface area. The method and apparatus are provided for growing TCF on the SCF by thermal decomposition of carbonaceous gases over the hot surface of the SCF using metal catalyst particles.

Influence of atmospheric plasma on physicochemical properties of vapor-grown graphite nanofibers.

PubMed

Seo, Min-Kang; Park, Soo-Jin; Lee, Sang-Kwan

2005-05-01

Vapor-grown graphite nanofibers (GNFs) were modified by plasma treatments using low-pressure plasmas with different gases (Ar gas only and/or Ar/O2 gases), flow rates, pressures, and powers. Surface characterizations and morphologies of the GNFs after plasma treatment were investigated by X-ray photoelectron spectroscopy (XPS), contact angle, titration, and transmission electron microscopy (TEM) measurements. Also, the investigation of thermomechanical behavior and impact strengths of the GNFs/epoxy composites was performed by dynamic-mechanical thermal analysis (DMTA) and Izod impact testing, respectively. The plasma treatment of the fibers changed the surface morphologies by forming a layer with a thickness on the order of 1 nm, mainly consisting of oxygen functional groups such as hydroxyl, carbonyl, and carboxyl groups. After functionalization of the complete surfaces, further plasma treatment did not enhance the superficial oxygen content but slightly changed the portions of the functional groups. Also, the composites with plasma-treated GNFs showed an increase in T(g) and impact strength compared to the composites containing the same amount of plasma-untreated GNFs.

Lasing of surface-polished polycrystalline Ho: YAG (yttrium aluminum garnet) fiber.

PubMed

Kim, Hyunjun; Hay, Randall S; McDaniel, Sean A; Cook, Gary; Usechak, Nicholas G; Urbas, Augustine M; Shugart, Kathleen N; Lee, HeeDong; Kadhim, Ali H; Brown, Dean P; Griffin, Benjamin; Fair, Geoff E; Corns, Randall G; Potticary, Santeri A; Hopkins, Frank K; Averett, Kent L; Zelmon, David E; Parthasarathy, Triplicane A; Keller, Kristin A

2017-03-20

A polycrystalline 1.5% Ho: YAG fiber with a diameter of 31 µm was prepared. Surface roughness from grain boundary grooving was reduced by polishing, which decreased the fiber scattering coefficient from 76 m^-1 to 35 m^-1. Lasing tests were done on this fiber with a SF57 Schott glass cladding. Lasing was confirmed by spectrum narrowing with threshold pump power lower than 500 mW and a slope efficiency of 7%. To our knowledge, this is the first lasing demonstration from a small diameter polycrystalline ceramic fiber.

Time-domain fiber loop ringdown sensor and sensor network

NASA Astrophysics Data System (ADS)

Kaya, Malik

Optical fibers have been mostly used in fiber optic communications, imaging optics, sensing technology, etc. Fiber optic sensors have gained increasing attention for scientific and structural health monitoring (SHM) applications. In this study, fiber loop ringdown (FLRD) sensors were fabricated for scientific, SHM, and sensor networking applications. FLRD biosensors were fabricated for both bulk refractive index (RI)- and surface RI-based DNA sensing and one type of bacteria sensing. Furthermore, the effect of glucose oxidase (GOD) immobilization at the sensor head on sensor performance was evaluated for both glucose and synthetic urine solutions with glucose concentration between 0.1% and 10%. Detection sensitivities of the glucose sensors were achieved as low as 0.05%. For chemical sensing, heavy water, ranging from 97% to 10%, and several elemental solutions were monitored by using the FLRD chemical sensors. Bulk index-based FLRD sensing showed that trace elements can be detected in deionized water. For physical sensing, water and cracking sensors were fabricated and embedded into concrete. A partially-etched single-mode fiber (SMF) was embedded into a concrete bar for water monitoring while a bare SMF without any treatment was directly embedded into another concrete bar for monitoring cracks. Furthermore, detection sensitivities of water and crack sensors were investigated as 10 ml water and 0.5 mm surface crack width, respectively. Additionally fiber loop ringdown-fiber Bragg grating temperature sensors were developed in the laboratory; two sensor units for water, crack, and temperature sensing were deployed into a concrete cube in a US Department of Energy test bed (Miami, FL). Multi-sensor applications in a real concrete structure were accomplished by testing the six FLRD sensors. As a final stage, a sensor network was assembled by multiplexing two or three FLRD sensors in series and parallel. Additionally, two FLRD sensors were combined in series and parallel by using a 2x1 micro-electromechanical system optical switch to control sensors individually. For both configurations, contributions of each sensor to two or three coupled signals were simulated theoretically. Results show that numerous FLRD sensors can be connected in different configurations, and a sensor network can be built up for multi-function sensing applications.

Analysis of the surfaces of wood tissues and pulp fibers using carbohydrate-binding modules specific for crystalline cellulose and mannan.

PubMed

Filonova, Lada; Kallas, Asa M; Greffe, Lionel; Johansson, Gunnar; Teeri, Tuula T; Daniel, Geoffrey

2007-01-01

Carbohydrate binding modules (CBMs) are noncatalytic substrate binding domains of many enzymes involved in carbohydrate metabolism. Here we used fluorescent labeled recombinant CBMs specific for crystalline cellulose (CBM1(HjCel7A)) and mannans (CBM27(TmMan5) and CBM35(CjMan5C)) to analyze the complex surfaces of wood tissues and pulp fibers. The crystalline cellulose CBM1(HjCel7A) was found as a reliable marker of both bacterially produced and plant G-layer cellulose, and labeling of spruce pulp fibers with CBM1(HjCel7A) revealed a signal that increased with degree of fiber damage. The mannan-specific CBM27(TmMan5) and CBM35(CjMan5C) CBMs were found to be more specific reagents than a monoclonal antibody specific for (1-->4)-beta-mannan/galacto-(1-->4)-beta-mannan for mapping carbohydrates on native substrates. We have developed a quantitative fluorometric method for analysis of crystalline cellulose accumulation on fiber surfaces and shown a quantitative difference in crystalline cellulose binding sites in differently processed pulp fibers. Our results indicated that CBMs provide useful, novel tools for monitoring changes in carbohydrate content of nonuniform substrate surfaces, for example, during wood or pulping processes and possibly fiber biosynthesis.

Effect of Surface-Modified TiO2 Nanoparticles on the Anti-Ultraviolet Aging Performance of Foamed Wheat Straw Fiber/Polypropylene Composites

PubMed Central

Xuan, Lihui; Han, Guangping; Wang, Dong; Cheng, Wanli; Gao, Xun; Chen, Feng; Li, Qingde

2017-01-01

Surface modification and characterization of titanium dioxide (TiO2) nanoparticles and their roles in thermal, mechanical, and accelerated aging behavior of foamed wheat straw fiber/polypropylene (PP) composites are investigated. To improve the dispersion of nanoparticles and increase the possible interactions between wheat straw fiber and the PP matrix, the surface of the TiO2 nanoparticles was modified with ethenyltrimethoxy silane (A171), a silane coupling agent. The grafting of A171 on the TiO2 nanoparticles’ surface was characterized by Fourier transform infrared spectroscopy (FTIR). The wheat straw fibers treated with A171 and modified TiO2 nanoparticles were characterized by FTIR and thermogravimetric analysis (TGA). FTIR spectra confirmed that the organic functional groups of A171 were successfully grafted onto the TiO2 nanoparticles and wheat straw fibers, and the modified TiO2 nanoparticles were adsorbed onto the wheat straw fibers. Thermogravimetric analysis showed that a higher thermal stability of the wheat straw fiber was obtained with the modified TiO2 nanoparticles. The flexural, tensile, and impact properties were improved. A higher ultraviolet (UV) stability of the samples treated with modified TiO2 nanoparticles was exhibited by the study of the color change and loss in mechanical properties. PMID:28772816